A TOLAN DERIVATIVE AND A LIQUID CRYSTAL MIXTURE CONTAINING THE SAME

Abstract: A novel tolan derivative compound as a liquid crystal substance having a low viscosity and a good compatibility with existing liquid crystals at low temperatures in addition to a large optical anisotropy value and a high clearing point, and a liquid crystal mixture containing the above compound are provided, which compound is expressed by the formula wherein R¹ represents an alkyl group of l to l0 carbon atoms, R² represents an alkyl group or an alkoxy group each of l to l0 carbon atoms, X represents -CH₂CH₂- or a single bond and A represents H atom or F atom provided that A represents F atom in the case where X represents a single bond.

Description: 1. Field of the Invention This invention relates to a tolan derivative as a novel compound and a liquid crystal mixture containing the same. 2. Description of the Related Art Display elements having liquid crystals applied thereto make use of the electrooptical effect exhibited by liquid crystal substances, and the display modes thereof include various ones such as those of TN (Twisted Nematic) type, DS (Dynamic Scattering) type, guest-host type, DAP type, etc. While the properties required for liquid crystal substances used vary depending on these respective modes, the following properties are required in common therewith: a property that liquid crystal phases are exhibited within as broad a temperature range as possible and a property that the liquid crystal substances are stable to moisture, heat, light, air, etc. At present, however, there is no single compound which satisfies all of such requirements; thus there have been used liquid crystal mixtures obtained by mixing several kinds of liquid crystal compounds or mixing similar compound(s) to liquid crystal compounds with a several kinds of liquid crystal compounds. As to tolan derivatives used as a component of liquid crystal materials, compounds expressed by the following formulas (l) to (3) are disclosed in (l) French patent application laid-open No. 2,l4l,438, (2) Japanese patent application laid-open No. Sho 60-l52427/l985 and (3) Japanese patent application laid-open No. Sho 60-20473l/l985, respectively: wherein R³ and R⁴ each represent an alkyl group or an alkoxy group. and R and R′ each represent a linear chain alkyl group. These tolan compounds are liquid crystal materials having specific features of a large optical anisotropy value (hereinafter abbreviated to Δn) and a high clearing point. SUMMARY OF THE INVENTION The object of the present invention is to provide a liquid crystal substance having a low viscosity and a good compatibility with existing liquid crystals at low temperatures in addition to the above-mentioned specific features and also to enhance the degree of freeness of choice of liquid crystal materials. The present invention resides in a tolan derivative compound expressed by the formula wherein R¹ represents an alkyl group of l to l0 carbon atoms, R² represents an alkyl group or an alkoxy group each of l to l0 carbon atoms, X represents -CH₂CH₂- or a single bond and A represents H atom or F atom provided that A represents F atom in the case where X represents a single bond, and a liquid crystal mixture comprising at least two components at least one of which is said tolan derivative compound. DETAILED DESCRIPTION OF PREFERRED EMBODIMENTS The embodiments of the present invention are compounds expressed by the following group of formulas: wherein R¹ and R² are as defined above. These compounds are liquid crystalline compounds having a slightly negative dielectric anisotropy value. Preferred compounds among those expressed by the formula (I-a) are those wherein R¹ represents ethyl, propyl, butyl or pentyl and R² represents methyl, ethyl, propyl, butyl, pentyl, methoxy, ethoxy, propoxy, butoxy or pentyloxy in the formula (I-a). For example, 4-(trans-4-propylcyclohexyl-l-ethyl)-4′-ethyltolan shown in Example described later is a liquid crystal compound having a large Δn value, a very low viscosity and a broad nematic range and it can constitute a nematic liquid crystal material having various specific features well balanced. Preferred compounds among those expressed by the formula (I-b) are those wherein R¹ represents ethyl, propyl, butyl or pentyl and R² represents ethyl, propyl, butyl or pentyl in the formula. The tolan derivatives expressed by the formula (l-a) or (l-b) are characterized in that an ethylene group is introduced into a core structure having three six-membered rings bonded linearly. It is presumed that by introducing the ethylene group, a relatively low melting point (i.e. the lower limit temperature of a mesomorphic phase) and a low viscosity have been realized in the compounds of (I-a) and (I-b). Further, it is also presumed that as to the compound of the formula (I-b), introduction of a fluorine atom as a lateral substituent into the central phenylene ring of the compound of the formula (I-a) may have realized increase in the nematic range and decrease in the smectic range without increasing the viscosity so much as compared to the compound of the formula (I-a). The compound (I-b) is also a nematic liquid crystal having a large Δn value and a low viscosity as in the case of the compound (I-a). Preferred compounds among those of the formula (I-c) are those wherein R¹ or R² represents ethyl, propyl, butyl or pentyl. Some compounds of the formula (I-c) wherein both R¹ and R² have a long chain alkyl group have a high viscosity so that such compounds are practically not preferred so much. In the compounds of the formula (I-c) the melting point and the clearing point are lowered by a fluorine substitution at a lateral position of the central phenylene ring. Further, as to compounds expressed by the formulas (I-b) and (I-c), a fluorine substitution at a lateral position of the central phenylene ring improves the compatibility of the compound with other liquid crystals at low temperatures The compounds of the present invention can be prepared for example according to the following preparation scheme, R¹, R², X and A therein being as defined above: A substituted benzene expressed by the formula (II) is first reacted with a 4-substituted-phenylacetyl chloride and anhydrous aluminum chloride in carbon disulfide to obtain a ketone derivative of the formula (III), which is then reacted with a reducing agent such as lithium aluminum hydride in an anhydrous solvent such as ether or tetrahydrofuran to obtain a compound of the formula (IV). Successively this alcohol derivative is subjected to dehydration reaction in the presence of a catalyst mentioned later in an inert organic solvent under the atmospheric pressure and at a reflux temperature to obtain an ethylene derivative of the formula (V). As the inert organic solvent, benzene, toluene, chloroform, carbon tetrachloride, methylene chloride, etc. are suitable, and as the catalyst, Lewis acids such as aluminum chloride, tin tetrachloride, titanium tetrachloride, etc., mineral acids such as sulfuric acid, phosphoric acid, etc., toluenesulfonic acid, etc. are usable. Successively bromine is attached onto the ethylene derivative of the formula (V) in a solvent such as methylene chloride, ethylene chloride, carbon tetrachloride, etc. to obtain a compound of the formula (VI), which is reacted with potassium tertiary-butoxide in tetrahydrofuran solvent, followed by a series of generally known purification procedures of extraction, washing, recrystallization, etc. to obtain the objective compound of the formula (I). The reactions of the respective steps are known, but the overall reactions are novel. The substituted benzene of the formula (II) as the starting raw material is obtained by applying a known reaction to an easily commercially available raw material. Namely, a substituted benzene of the formula (II) wherein X represents ethylene group is obtained by reducing a ketone derivative obtained by Friedel-Crafts reaction of a trans-4-alkylcyclohexylacetyl chloride with benzene or by coupling reaction of a trans-4-alkylcyclohexylacetyl chloride with bis(3-fluorophenyl)cadmium, while a substituted benzene of the formula (II) wherein X represents a single bond is obtained by subjecting a substituted cyclohexanol obtained by Grignard reaction of 3-fluorophenylmagnesium bromide with a 4-alkylcyclohexanone, to dehydration reaction and then hydrogenation reaction. Preferred representative examples of liquid crystal compounds used as components of the liquid crystal mixture of the present invention in admixture with the compound expressed by the formula (I) are 4-substituted-phenyl 4′-substituted-benzoates, 4-substituted-phenyl 4′-substituted-cyclohexanecarboxylates, 4′-substituted-biphenyl-4-yl 4″-substituted-cyclohexanecarboxylates, 4-substituted-phenyl 4′-(4-substituted-cyclohexanecarbonyloxy)benzoates, 4-substituted-phenyl 4′-(4-substituted-cyclohexyl)benzoates, 4-substituted-cyclohexyl 4′-(4-substituted-cyclohexyl)benzoates, 4,4′-substituted-biphenyls, 4,4′-substituted-phenylcyclohexanes, 4,4″-substituted-terphenyls, 4,4″-substituted-biphenyl-4′-yl-cyclohexanes, 2-(4′-substituted-phenyl)-5-substituted-pyrimidines, etc. Compounds having lateral substituent(s) of halogen atom(s) or cyano group(s) on the phenylene ring(s) of the above-mentioned compounds may also be used as components of the liquid crystal mixture of the present invention. As is generally known, in a liquid crystal display element, the product of the cell thickness (d) and the optical anisotropy value (Δn) of the liquid crystal material employed must be set to a specified value in order to prevent an interference fringe on the cell surface which deteriorates the view of the display. In the case of practically used display cells, the value of Δn × d has been set to any one of 0.5, l.0, l.6 or 2.2. Since the value of Δn × d is set to definite values as described above, if a liquid crystal material having a large Δn value is used, it is possible to reduce the d value. When the d value is reduced, the response time is reduced. Thus, liquid crystal materials having a large Δn value are important for preparing a liquid crystal display cell having a high response rate and no interference fringe. Further, in order to reduce the response time, a low viscosity is also necessary. Now, the compound of the formula (I) of the present invention is a novel nematic liquid crystal compound having a large Δn value (ca. 0.26), a high N-I transition point and further a low viscosity (ca. l6 cp at 20°C). Thus, when the compound of the formula (I) of the present invention is mixed with various mother liquid crystals, it is possible to prepare a practical liquid crystal material having a low viscosity, a large Δn value and a high N-I transition point. The present invention will be described in more concretely by way of Examples, but it should not be construed to be limited thereto. In addition, symbols C-S point, C-N point, S-N point and N-I point in Examples refer to crystalline-smectic transition point, crystalline-nematic transition point, smectic-nematic transition point and nematic-isotropic liquid transition point, respectively. Example l 4-(Trans-4-propylcyclohexyl-l-ethyl)-4′-ethyltolan Anhydrous aluminum chloride (27.7 g, 0.2l mol) was added to carbon disulfide (l60 cc), followed by adding 4-ethylphenylacetyl chloride (3l.7 g, 0.l74 mol) under cooling, successively adding trans-4-propylcyclohexylethylbenzene (40 g, 0.l74 mol) over about one hour, thereafter agitating the reaction mixtrue at room temperature for l0 hours, distilling off carbon disulfide, adding the residue to dilute hydrochloric acid aqueous solution, decomposing the resulting aluminum chloride complex with stirring for one hour, extracting the resulting raw crystals with toluene (l00 cc), washing with water, drying, distilling off toluene and recrystallizing the remaining solids from ethyl acetate to obtain the following compound (35.3 g): This compound was dissolved in anhydrous tetrahydrofuran (50 cc), followed by dropwise adding the solution to a solution of lithium aluminum hydride (2.7 g, 0.07 mol) in anhydrous tetrahydrofuran (l00 cc), further agitating the mixture at 0°C for one hour, thereafter adding 20 wt.% sulfuric acid (50 cc) to the reaction mixture to dissolve the inorganic substance, extracting the separated oily substance with toluene (l00 cc), washing the separated toluene solution with l0% sodium hydrogen carbonate aqueous solution, further washing with water till the washing water became neutral, drying the resulting toluene solution with anhydrous sodium sulfate, adding p-toluenesulfonic acid (l.8 g), heating the mixture under reflux, removing the formed water to the outside of the system, allowing the resulting material to cool down to room temperature after completion of the reaction, washing the toluene solution with water till the washing water became neutral, drying the toluene solution with anhydrous sodium sulfate, distilling off toluene and recrystallizing the remaining solids from ethyl acetate to obtain the following compound (25 g): This product exhibited liquid crystal phases and the transition points were as follows: C-S point: l43.9°C, S-N point: l5l.3°C and N-I point: l97.9°C. This compound was dissolved in methylene chloride (l50 cc), followed by dropwise adding bromine (ll.0 g, 0.069 mol) at room temperature to react the mixture for one hour, thereafter distilling off methylene chloride and recrystallizing the remaining solids from n-heptane to obtain the following compound (24.5 g): This compound was then dissolved in anhydrous tetrahydrofuran (l00 cc), followed by adding potassium tertiary-butoxide (22.5 g, 0.20 mol), agitating the mixture at 40°C for 2 hours, thereafter adding water (200 cc) to the reaction mixture, extracting the separated raw crystals with toluene (l00 cc), washing with water, drying, distilling off toluene and recrystallizing the remaining solids from ethyl acetate to obtain the following compound (l5.0 g): This compound exhibited liquid crystal phases and the transition points were as follows: C-S point: 68.7°C, S-N point: 74.l°C and N-I point: l6l.8°C. Examples 2 to l6 Tolan derivatives obtained in the same manner as in Example l and their phase transition points are shown in Table l together with the results of Example l. In Table l and the succeeding Tables 2 and 3, the symbol ( ) indicates a monotropic transition point. Examples l7 to 25 Compounds shown in Table 2 were obtained from 3-(trans-4-alkylcyclohexylethyl)fluorobenzenes and 4-substituted-phenylacetyl chlorides in the same manner as in Example l. Examples 26 to 32 Compounds shown in Table 3 were obtained from 3-(trans-4-alkylcyclohexyl)fluorobenzenes and 4-substituted-phenylacetyl chlorides in the same manner as in Example l. Example 33 A liquid crystal mixture A consisting of has a N-I point of 52.l°C, a viscosity at 20°C of 22.4 cp and an optical anisotropy value Δn of 0.ll9. When 4-(trans-4-propylcyclohexyl-l-ethyl)-4′-ethyltolan (l5 parts by weight) as a compound of the present invention shown in Example l was added to the liquid crystal mixture A (85 parts by weight), the N-I point of the resulting liquid crystal mixture rose to 68.0°C, the viscosity at 20°C thereof lowered to l9.0 cp and the optical anisotropy value Δn thereof rose to 0.l42. Further, even when this liquid crystal mixture was allowed to stand at -30°C for 30 days, no deposition of crystal occurred. Example 34 When 2-fluoro-4-(trans-4-propylcyclohexyl-l-ethyl)-4′-ethyltolan (l5 parts by weight) as a compound of the present invention shown in Example 20 was added to the liquid crystal mixture A (85 parts by weight) used in Example 33, the N-I point of the resulting liquid crystal mixture rose to 65.0°C, the viscosity at 20°C thereof lowered to 20.8 cp and the optical anisotropy value Δn rose to 0.l40. Further, even when this liquid crystal mixture was allowed to stand at -30°C for 30 days, no deposition of crystal occurred. Example 35 When 2-fluoro-4-(trans-4-propylcyclohexyl)-4′-ethyltolan (l5 parts by weight) as a compound of the present invention shown in Example 27 was added to the liquid crystal mixture A (85 parts by weight) used in Example 33, the N-I point of the resulting liquid crystal mixture rose to 66.7°C, the viscosity at 20°C lowered to 2l.0 cp and the optical anisotropy value Δn rose to 0.l40. Further, even when this liquid crystal mixture was allowed to stand at -30°C for 30 days, no deposition of crystal occurred. It can be seen from these Examples that the compound of the formula (I) of the present invention can raise the N-I point of the mother liquid crystals up to a practically sufficient value, can raise the Δn thereof and yet can reduce the viscosity thereof and also is a liquid crystal material having a superior compatibility at low temperatures. Comparative example l When 4-(trans-4-propylcyclohexyl)-4′-ethyltolan (l5 parts by weight) as one of tolan derivatives shown in the formula (2) as a prior art was added to the liquid crystal mixture A (85 parts by weight) used in Example 33, the N-I point of the resulting liquid crystal mixture rose to 68.3°C, the viscosity at 20°C thereof was 22.8 cp and the optical anisotropy value thereof rose to 0.l4l, but when the mixture was allowed to stand at -30°C, deposition of crystal occurred in only one day. Comparative example 2 When 4-(4-propylphenyl)-4′-ethyltolan (l5 parts by weight) as one of tolan derivatives shown in the formula (2) as a prior art was added to the liquid crystal mixture A (85 parts by weight) used in Example 33, the N-I point of the resulting liquid crystal mixture rose to 70.3°C and the Δn thereof rose to 0.l45, but the viscosity at 20°C thereof also rose to 28.0 cp. When this liquid crystal mixture was allowed to stand -30°C, deposition of crystal occurred in only 5 hours.

Claims: Claims for the following Contracting States : CH, DE, FR, GB, IT, LI, NL A tolan derivative compound expressed by the formula wherein R¹ represents an alkyl group of l to l0 carbon atoms, R² represents an alkyl group or an alkoxy group each of l to l0 carbon atoms, X represents -CH₂CH₂- or a single bond and A represents H atom or F atom provided that A represents F atom in the case where X represents a single bond. A tolan derivative compound according to claim l wherein said X represents -CH₂CH₂- and said A represents H. A tolan derivative compound according to claim l wherein said X represents -CH₂CH₂- and said A represents F. A tolan derivative compound according to claim l wherein said X represents a single bond and said A represents F. A liquid crystal mixture comprising at least two components at least one of which is a tolan derivative compound expressed by the formula wherein R¹ represents an alkyl group of l to l0 carbon atoms, R² represents an alkyl group or an alkoxy group each of l to l0 carbon atoms, X represents -CH₂CH₂- or a single bond and A represents H atom or F atom provided that A represents F atom in the case where X represents a single bond. Claims for the following Contracting State : AT A method to prepare a tolan derivative compound according to formula I wherein R¹ represents an alkyl group of 1 to 10 carbon atoms, R² represents an alkyl group or an alkoxy group each of 1 to 10 carbon atoms, X represents -CH₂CH₂-or a single bond and A represents H atom or F atom, provided that A represents F atom in the case where X represents a single bond, characterized by reacting a substituted benzene according to formula II with a 4-substituted-phenyl acetyl chloride of the following formula the meanings of R₁, R₂, x and A being the same as defined above, to obtain a ketone derivative of the formula III which is then reacted with a reducing agent to obtain a compound of formula IV subjecting the above alcohol derivative to a dehydration reaction to obtain an ethylene derivative of the formula V attaching bromine onto the ethylene derivative of formula V to obtain a compound according to formula VI and reacting the later with potassium-butoxide in a solvent to obtain the compound of formula I. A method according to claim 1 wherein said X represents -CH₂CH₂- and said A represents H. A method according to claim 1 wherein said X represents -CH₂CH₂- and said A represents F. A method according to claim 1 wherein said X represents a single bond and said A represents F. A method for the preparation of a liquid crystal mixture characterized by mixing at least two components at least one of which is a tolan derivative compound expressed by formula I wherein R¹ represents an alkyl group of 1 to 10 carbon atoms, R² represents an alkyl group or an alkoxy group each of 1 to 10 carbon atoms, X represents -CH₂CH₂-or a single bond and A represents H atom or F atom, provided that A represents F atom in the case where x represents a single bond. The use of tolan derivative compounds prepared according to claims 1 to 4 in liquid crystal mixtures for display elements.

Inventors: GOTO, YASUYUKI, OGAWA, TETSUYA
Applicants: CHISSO CORPORATION
Application year: 1987
Main classification: C07C43
IPC codes: C07C13, C07C25, C09K19