4,4-BIS(4-HYDROXYPHENYL)CYCLOHEXANECARBOXYLIC ACID DERIVATIVES AND PROCESS FOR PREPARING SAME

Abstract: Novel 4,4-bis(4-hydroxyphenyl)cyclohexane­ carboxylic acid derivatives. These compounds can be prepared by reacting a cyclohexanone-4-carboxylic acid with a phenol, e.g.

Description: This invention relates to novel 4,4-bis(4-­ hydroxyphenyl)cyclohexanecarboxylic acid derivatives and a process for preparing the same. l,l-Bis(4-hydroxyphenyl)cyclohexane and its derlvative having one or more alkyl groups on the cyclohexane ring, such as 4-methyl-l,l-bis(4-­ hydroxyphenyl)cyclohexane, are well known. For example, l,l-bis(4-hydroxyphenyl)cyclohexane is a crystalline substance having a melting point of l84°C, while 4-­ methyl-l,l-bis(4-hydroxyphenyl)cyclohexane and 3,5-­ dimethyl-l,l-bis(4-hydroxyphenyl)cyclohexane are crystalline substances having melting points of l80°C and l74°C, respectively (Methoden der organischen Chemie, Vol. 6, No. 2, l028). It is an object of the present invention to provide novel 4,4-bis(4-hydroxyphenyl)cyclohexane­ carboxylic acid derivatives. It is another object of the present invention to provide a process for preparing novel 4,4-bis(4-­ hydroxyphenyl)cyclohexanecarboxylic acid derivatives. The 4,4-bis(4-hydroxyphenyl)cyclohexane­ carboxylic acid derivatives of the present invention can be represented by the formula where R is a hydrogen atom or a lower alkyl group, R₁ and R₂ are lower alkyl groups, and m and n are whole numbers of 0 to 4. The compounds of the present invention are useful as precursors of 4-hydroxybiphenyl-4′-carboxylic acids which are very useful as starting materials for the synthesis of polymers and the like. The conversion of these compounds into 4-hydroxybiphenyl-4′-carboxylic acids is described in our copending Japanese Patent Applications No. 76684/l986 filed April 4, l986; No. l58707/l986 filed July 8, l986; and No. 223889/l986 filed September 24, l986. The compounds represented by the formula (I) can be prepared by reacting a cyclohexanone-4-carboxylic acid of the formula where R, R₁ and m are as defined for formula (I), with a phenol of the formula where R₂ and n are as defined for formula (I). Some embodiments of the invention will now be described in greater detail with reference to the accompanying drawing in which: Fig. l is the infrared spectrum of 4,4-bis(4-­ hydroxyphenyl)cyclohexanecarboxylic acid obtained in Example l; and Fig. 2 is the infrared spectrum of 4,4-­ bis(4-hydroxypheny)cyclohexanecarboxylic acid methyl ester obtained in Example 2. Specific examples of the compounds of formula (I) include 4,4-bis(4-hydroxyphenyl)cyclohexanecarboxylic acid, the methyl, ethyl and butyl esters of 4,4-bis(4-­ hydroxyphenyl)cyclohexanecarboxylic acid, 4,4-bis(3,5-­ dimethyl-4-hydroxyphenyl)cyclohexanecarboxylic acid methyl ester, 4,4-bis(3-tert-butyl-4-hydroxyphenyl)­ cyclohexanecarboxylic acid and 4,4-bis(4-hydroxyphenyl)-­ 2-methylcyclohexanecarboxylic acid methyl ester. Preferably, the lower alkyl groups represented by R, R₁ and R₂ in the above formula (I) are alkyl groups having l to 4 carbon atoms. The reaction of a cyclohexanone-4-carboxylic acid of formula (II) with a phenol of formula (III) is preferably carried out in the presence of an acid catalyst. Examples of the acid catalyst used for this purpose include hydrogen chloride gas, hydrochloric acid, sulfuric acid, phosphoric acid, toluenesulfonic acid, BF₃, ZnCl₂, AlCl₃, SnCl₄, cation exchange resins having movable acid groups, and the like. These catalysts may be used in an amount of 0.l to 30 parts by weight per l00 parts by weight of the cyclohexanone-­ 4-carboxylic acid of formula (II). Moreover, the reaction rate can further be enhanced by the additon of a co-catalyst. Active co­ catalysts include alkyl mercaptans such as methyl mercaptan, ethyl mercaptan, n-propyl mercaptan, isopropyl mercaptan, n-butyl mercaptan, isobutyl mercaptan, tert-butyl mercaptan, etc., as well as high-molecular-weight alkyl mercaptans. It is also possible to use other sulfur compounds such as hydrogen sulfide, thiophenol, thioalcohols, thio acids, polymeric thioacetone, dialkyl sulfides, etc., as well as analogous selenium compounds. The aforesaid reaction may be carried out in a solvent which exerts no adverse influence on the reaction, and usable solvents include aromatic hydro­ carbons, chlorinated aliphatic hydrocarbons, glacial acetic acid and the like. However, in order to enhance the yield of the product and minimize the occurrence of said reactions, it is desirable to use an excess of the phenol as the solvent. The amount of phenol used is suitably in the range of 2 to l0 parts by weight per part by weight of the cyclohexanone-4-carboxylic acid. In the process of the present invention, the reaction may be carried out at a temperature of 30 to l00°C and preferably 40 to 70°C. If the reaction temperature is too high, the formation of by-products will undesirably increase and, therefore, cause a reduction in the yield of the product. The 4,4-bis(4-hydroxyphenyl)cyclohexane­ carboxylic acid derivative formed as a result of the reaction can be isolated by pouring the reaction mass into a solvent (such as benzene or the like) in which the compounds of the present invention are hardly soluble, and then cooling the resulting mixture to crystallize the product. The phenol used in excess can be recovered and reused by neutralizing the mother liquor and filter­ ing off the crystallized salts, or by distilling the mother liquor under reduced pressure. Cyclohexanone-4-carboxylic acids serving as starting materials in the process of the present invention can be obtained by reacting the corresponding 4-hydroxybenzoic acids (such as 4-hydroxybenzoic acid, methyl 4-hydroxybenzoate, ethyl 4-hydroxybenzoate, propyl 4-hydroxybenzoate and butyl 4-hydroxybenzoate) in a solvent (such as water, acetic acid, alcohols, etc.) under the influence of a catalyst comprising, for example, palladium supported on a carrier. The present invention is further illustrated by the following examples. However, these examples are given merely by way of illustration and are not to be construed to limit the scope of the invention. Example l Preparation of cyclohexanone-4-carboxylic acid: One mole of 4-hydroxybenzoic acid was reacted with two moles of hydrogen in the presence of 5% palladium-carbon catalyst. This reaction was carried out in isopropyl alcohol at a temperature of l30-l40°C and a hydrogen pressure of 20-40 kg/cm² (gauge). After the reaction mixture was filtered to recover the catalyst therefrom, the filtrate was distilled to recover the solvent. The resulting residue was recrystallized from a mixture of benzene and hexane to obtain cyclohexane-4-carboxylic acid. This product had a melting point of 67.0-68.0°C. Preparation of 4,4-bis(4-hydroxyphenyl)cyclohexane­ carboxylic acid: Into a 500-ml reaction flask were charged 35.5 g of cyclohexanone-4-carboxylic acid, 284.0 g of phenol and 30 ml of 36% hydrochloric acid. This reaction mixture was stirred at 40-45°C for 6 hours. After completion of the reaction, hydrogen chloride-­ containing water was removed by means of an evaporator. Thereafter, the greater part of phenol was removed by distillation and the remaining phenol was then removed by sludging with 300 ml of benzene. The precipitate so formed was collected by filtration and then dried to obtain 74.9 g of white crystals. By subjecting these crystals to column chromatography, there was obtained a pure crystalline product which was identified as 4,4-bis(4-hydroxyphenyl)cyclohexanecarboxylic acid on the basis of its ¹H-NMR and infrared spectra. The crude crystals were obtained in a 94% yield and had a purity of 98%. The ¹H-NMR data of 4,4-bis(4-hydroxyphenyl)­ cyclohexanecarboxylic acid are shown in Table l. In addition, its infrared spectrum is shown in Fig. l. Each peak area coincided with the corresponding proton ratio. Example 2 Preparation of cyclohexanone-4-carboxylic acid methyl ester: One mole of methyl 4-hydroxybenzoate was reacted with two moles of hydrogen in the presence of 5% palladium-carbon catalyst. This reaction was carried out in isoproyl alcohol at a temperature of l70-l80°C and a hydrogen pressure of 20-40 kg/cm². After the reaction mixture was filtered to recover the catalyst therefrom, the filtrate was distilled to obtain cyclo­ hexanone-4-carboxylic acid methyl ester as the distil­ late at l40°C/20 mmHg. Preparation of 4,4-bis(4-hydroxyphenyl)cyclohexane­ carboxylic acid methyl ester: Into a 300-ml reaction flask were charged 62.5 g (0.40 mole) of cyclohexanone-4-carboxylic acid methyl ester, l88.2 g (2.0 moles) of phenol and 20 ml of 36% hydrochloric acid. This reaction mixture was stirred at 40-45°C for 5 hours. After completion of the reaction, the reaction mixture was poured into 500 ml of benzene, followed by stirring at 20°C for l hour. The precipitate so formed was collected by filtration and then dried to obtain l03.7 g of white crystals. By subjecting these crystals to column chromatography, there was obtained a pure crystalline product which was identified as 4,4-bis(4-hydroxyphenyl)cyclohexane­ carboxylic acid methyl ester on the basis of its ¹H-NMR and infrared spectra. The crude crystals were obtained in a 65% yield and had a purity of 82%, and the greater part of the by-products comprised 4,4-bis(4-hydroxy­ phenyl)cyclohexanecarboxylic acid formed as a result of hydrolysis. The ¹H-NMR data of 4,4-bis(4-hydroxyphenyl)­ cyclohexanecarboxylic acid methyl ester are shown in Table 2. In addition, its infrared spectrum is shown in Fig. 2. Each peak area coincided with the corresponding proton ratio. Example 3 The procedure of Example 2 for the preparation of cyclohexanone-4-carboxylic acid methyl ester was repeated, except that the starting methyl 4-hydroxy­ benzoate was replaced by ethyl 4-hydroxybenzoate. Thus, there was obtained cyclohexanone-4-carboxylic acid ethyl ester (B.P. l50-l52°C/40 mmHg; n D = l.4594). In the same manner as described in Example 2, this compound was reacted with phenol to obtain a white crystalline product. On the basis of its NMR and infrared spectra, this product was identified as 4,4-bis(4-hydroxy­ phenyl)cyclohexanecarboxylic acid ethyl ester. Example 4 Into a reaction flask were charged 62.5 g (0.40 mole) of cyclohexanone-4-carboxylic acid methyl ester, 244.3 g (2.0 moles) of 2,6-xylenol, 6.3 g of n-butyl mercaptan and 200 ml of toluene. While this mixture was kept at 40-45°C, reaction was effected by blowing hydrogen chloride gas therethrough for 8 hours at a rate of 2-l0 ml/min. After completion of the reaction, the reaction mixture was cooled by the addition of 200 ml of toluene and l00 ml of water, and then sludged at room temperature for 30 minutes. The precipitate so formed was collected by filtration, washed with toluene, and then dried to obtain l40.3 g of white crystals. After purification, this product was identified as 4,4-bis(3,5-dimethyl-4-hydroxyphenyl)­ cyclohexanecarboxylic acid methyl ester on the basis of its NMR and infrared spectra. The crude crystals were obtained in a 66% yield and had a purity of 72%. Example 5 Into a reaction flask were charged 56.9 g (0.40 mole) of cyclohexanone-4-carboxylic acid, 480.7 g (3.2 moles) of o-tert-butylphenol and 5.7 g of n-butyl mercaptan. While this mixture was kept at 60°C, reaction was effected by blowing hydrogen chloride gas therethrough for 6 hours at a rate of 2-l0 ml/min. After completion of the reaction, the reaction mixture was poured into a two-layered mixture consisting of 500 ml of toluene and l00 ml of water, followed by sludging at room temperature for 30 minutes. The precipitate so formed was collected by filtration, washed with toluene, and then dried to obtain l59.l g of white crystals. After purification, this product was identified as 4,4-bis(3-tert-butyl-4-hydroxyphenyl)­ cyclohexanecarboxylic acid on the basis of its NMR and infrared spectra. The crude crystals were obtained in an 88% yield and had a purity of 95%. Example 6 : Preparation of 3-methylcyclohexanone-4-carboxylic acid methyl ester: 2-Methyl-4-hydroxybenzoic acid was heated in methanol under the influence of sulfuric acid catalyst to convert it into its methyl ester. One mole of the methyl 2-methyl-4-hydroxybenzoate thus obtained was reacted with two moles of hydrogen in the presence of 5% palladium-carbon catalyst. This reaction was carried out in isopropyl alcohol at a temperature of l50-l70°C and a hydrogen pressure of 20-40 kg/cm². After the reaction mixture was filtered to recover the catalyst therefrom, the filtrate was distilled to obtain 3-­ methylcyclohexanone-4-carboxylic acid methyl ester as the distillate.at ll2-l20°C/5 mmHg. Preparation of 4,4-bis(4-hydroxyphenyl)-2-methylcyclo­ hexanecarboxylic acid methyl ester: Into a 300-ml reaction flask were charged 68.l g of 3-methylcyclohexanone-4-carboxylic acid methyl ester, l87.5 g of phenol and 20 ml of 36% hydrochloric acid. This reaction mixture was stirred at 40-45°C for 6 hours. After completion of the reaction, the reaction mixture was worked up in the same manner as described in Example 2. Thus, there was obtained ll2.9 g of white crystals. After purifi­ cation, this product was identified as 4,4-bis(4-­ hydroxyphenyl)-2-methylcyclohexanecarboxylic acid methyl ester on the basis of its NMR and infrared spectra. The crude crystals were obtained in a 63% yield and had a purity of 76%.

Claims: 1. A 4,4-bis(4-hydroxyphenyl)cyclohexane­ carboxylic acid derivative of the formula where R is a hydrogen atom or a lower alkyl group, R₁ and R₂ are lower alkyl groups, and m and n are whole numbers of 0 to 4. 2. A 4,4-bis(4-hydroxyphenyl)cyclohexanecarboxylic acid derivative as claimed in claim l which is 4,4-­ bis(4-hydroxyphenyl)cyclohexanecarboxylic acid. 3. A 4,4-bis(4-hydroxyphenyl)cyclohexanecarboxylic acid derivative as claimed in claim l which is 4,4-­ bis(4-hydroxyphenyl)cyclohexanecarboxylic acid methyl ester. 4. A 4,4-bis(4-hydroxyphenyl)cyclohexanecarboxylic acid derivative as claimed in claim l which is 4,4-­ bis(4-hydroxyphenyl)cyclohexanecarboxylic acid ethyl ester. 5. A 4,4-bis(4-hydroxyphenyl)cyclohexanecarboxylic acid derivative as claimed in claim l which is 4,4-bis­ (3,5-dimethyl-4-hydroxyphenyl)cyclohexanecarboxylic acid methyl ester. 6. A 4,4-bis(4-hydroxyphenyl)cyclohexanecarboxylic acid derivative as claimed in claim l which is 4,4-bis­ (3-tert-butyl-4-hydroxyphenyl)cyclohexanecarboxylic acid. 7. A 4,4-bis(4-hydroxyphenyl)cyclohexanecarboxylic acid derivative as claimed in claim l which is 4,4-bis­ (4-hydroxyphenyl)-2-methylcyclohexanecarboxylic acid methyl ester. 8. A process for preparing 4,4-bis(4-hydroxyphenyl)­ cyclohexanecarboxylic acid derivatives which comprises reacting a cyclohexanone-4-carboxylic acid of the formula where R, R₁ and m are as defined for formula (I), with a phenol of the formula where R₂ and n are as defined for formula (I). 9. A process as claimed in claim 8 wherein the reaction is carried out in the presence of an acid catalyst. l0. A process as claimed in claim 9 wherein the acid catalyst is hydrogen chloride, hydrochloric acid, sulfuric acid, phosphoric acid, toluenesulfonic acid, boron trifluorine, zinc chloride, aluminum chloride, stannic chloride or a cationic exchange resin. 11. A process as claimed in claim 9 wherein the acid catalyst is used in an amount of 0.l to 30% by weight based on the cyclohexanone-4-carboxylic acid. 12. A process as claimed in claim 9 wherein a co-catalyst is used in combination with the acid catalyst. 13. A process as claimed in claim 8 wherein the phenol is used in an amount of 2 to l0 parts by weight per part by weight of the cyclohexanone-4-carboxylic acid. 14. A process as claimed in claim 8 wherein the reaction is carried out at a temperature of 30 to l00°C.

Inventors: MIURA, TOHRU, NAGATA, TERUYUKI
Applicants: MITSUI TOATSU CHEMICALS, INC.
Application year: 1987
Main classification: C07C62
IPC codes: C07C67, B01J27, C07C69, C07C51, C07B61, C07C62