PROCESS FOR PRODUCING COPPER PHTHALOCYANINE PIGMENT

Abstract: A process for preparing a copper phthalocyanine pigment, which comprises reacting, in a hydrophilic solvent in the presence of a catalyst, a compound capable of forming phthalocyanine rings, urea, copper or a compound thereof and at least one compound of formula (1) to (9): (1) an aliphatic tetracarboxylic acid, (2) benzophenone-3,3′,4,4′-tetracarboxylic acid or an anhydride thereof, (3) pyromellitic acid or an anhydride thereof, (4) copper phthalocyanine sulfonic acid, (5) a compound of formula (I): (6) a compound of formula (II): wherein X represents 0, NH,NCH₂0H,N-R, in which R represents an alkyl group ,allyl group or aralkyl group, or a NCH₂Y group in which Y represents a phenyl group or a derivative thereof, a napthalene ring or a derivative thereof or a phthalocyanine ring or derivative thereof, (7) a compound of formula (III): wherein A and B, which may be the same or different, each represents hydrogen, an alkyl group, hydroxyalkyl group, alkoxyalkyl group, cycloalkyl group, allyl group, aralkyl group or a -CH₂Y group in which Y represents a phenyl group or a or a derivative thereof, a naphthalene ring or a derivative thereof or a phthalocyanine ring or a derivative thereof, (8) a compound of formula (IV): wherein M represents hydrogen or an alkali metal, and A and B, which may be the same or different, each represents a carboxyl group or a group derived from a carboxyl group or A and B together form an imide or acid anhydride, or (9) a compound of formula (V): wherein R₁, R₂ and R₃, which may be the same or different each represents hydrogen, a carboxyl group or group derived from a carboxyl group, it being possible for R₁ and R₂ or R₂ and R₃ to form, together with the carbons to which they are attached, an imide or acid anhydride ring, and X, Y and Z, which may be the same or different, each represents a carboxyl group, a group derived from a carboxyl group or a nitrile group, it being possible for X and Y, or Y and Z, to form an imide or an acid anhydride.

Description: The present invention relates to a process for producing a copper phthalocyanine pigment which is generally used as a blue colorant for use in, for example inks, paints and plastics as a particularly effective blue pigment of clear hue and high tinting strength. Copper phthalocyanine pigments have generally been produced by way of a first step of synthesizing crude copper phthalocyanine and a second step of pigmentation as below: (1) Synthesis Step A crude copper phthalocyanine is prepared by heating phthalic acid anhydride or the derivatives thereof, copper or copper compounds, a nitrogen source such as urea and a small amount of a catalyst in an inert high boiling solvent. (2) Pigmentation Step Since the copper phthalocyanine prepared by the synthesis step above is a lump of coarse particles, it does not have a clear hue and has a low tinting strength, and as such its use is not practical. Accordingly, a pigmentation step is necessary to provide tinting strength, clearness and aptitude as a pigment. The step to this pigmentation includes a chemical method and a mechanical method of making finer; in the former, sulfate formed by adding sulfuric acid to the crude compound or dissolving the crude compound in highly concentrated sulfuric acid is poured in a large amount of water, and in the latter, mechanical grinding is applied, for example by a ball mill or a kneader. However, the above-mentioned process of synthesis of the crude copper phthalocyanine and then pigmentation involves the following drawbacks: (1) the steps are lengthy and not economical; (2) in the case of using sulfuric acid in the pigmentation step, there are serious problems such as corrosion of the apparatus and those of public pollutions e.g. a large amount of wasted acid; (3) a large amount of energy is necessary for the mechanical grinding and the treatment is complicated and requires a great amount of energy for a long period of time; an amount per one batch is so small that productivity is extremely small; further after-treatment is needed for high COD wasted water. In order to overcome these drawbacks, development for the direct production process for a copper phthalocyanine pigment requiring no pigmentation step has been expected. The following various methods have been proposed: (1) Japanese Patent Laid-Open No. Sho 48-32919, (2) Japanese Patent Laid-Open Sho 49-131224 and 49-97820, (3) US-A-4135944, (4) US-A-4171309, (5) Japanese Patent Laid-Open Nos. Sho 57-141453 and 149358, (6) Japanese Patent Laid-Open No. Sho 57-168950, (7) Japanese Patent Laid-Open Nos. Sho 61-195166 and 203175 and (8) US-A-4152171. US-A-4171309 uses benzophenone 3,3',4,4' tetracarboxylic acid or a derivative thereof as an additive and US-A-4152171 uses a sulfonated copper phthalocyanine as an additive. In addition, JP-A-57-135866 describes a process using sulfolane as solvent. However, those methods are not quite satisfactory in operation and performance. We have made extensive studies for eliminating the foregoing various drawbacks in the direct production process for copper phthalocyanine pigments and, as a result, have accomplished the present invention based on the findings that copper phthalocyanine fine particles may be used directly as a pigment without a further pigmentation step, when they are obtained by conducting the synthesis step above using a specific organic solvent and specific compound. Accordingly, the present invention provides a process for preparing a copper phthalocyanine pigment, which comprises reacting, in a hydrophilic solvent which is sulfolane, 2-methylsulfolane, 3-methylsulfolane, dimethylsulfoxide, 2,4-dimethylsulfolane, N-methylpyrrolidane or 1,3-dimethyl-2-imidazolidinone, in the presence of a catalyst, a compound capable of forming phthalocyanine rings, urea, copper or a compound thereof and at least one compound of formula (1) to (9): (1) an aliphatic tetracarboxylic acid, (2) benzophenone-3,3',4,4'-tetracarboxylic acid or an anhydride thereof, (3) pyromellitic acid or an anhydride thereof, (4) copper phthalocyanine sulfonic acid, (5) a compound of formula (I) : (6) a compound of formula (II) : wherein X represents O, NH, NCH₂OH, N-R in which R represents an alkyl group, allyl group or aralkyl group, or a NCH₂Y group in which Y represents a phenyl group or a derivative thereof, a naphthalene ring or a derivative thereof, a phthalocyanine ring or derivative thereof, (7) a compound of formula(III): wherein A and B, which may be the same or different, each represents hydrogen, an alkyl group, hydroxyalkyl group, alkoxyalkyl group, cycloalkyl group, allyl group, aralkyl group or a -CH₂Y group in which Y represents a phenyl group or a derivative thereof, a naphthalene ring or a derivative thereof or a phthalocyanine ring or a derivative thereof, (8) a compound of formula (IV) : wherein M represents hydrogen or an alkali metal, and A and B, which may be the same or different, each represent a carboxyl group or a group derived from a carboxyl group or A and B together form an imide or acid anhydride or (9) a compound of formula (V) : wherein R₁, R₂ and R₃ which may be the same or different, each represent a hydrogen atom, a carboxyl group or a group derived from a carboxyl group, it being possible for R₁ and R₂ or R₂ and R₃ to form, together with the carbon to which they are attached, an imide or acid anhydride ring; and X, Y and Z, which may be the same or different, each represesnt a carboxyl group, a group derived from a carboxyl group or a nitrile group, it being possible for X and Y or Y and Z to form an imide or an acid anhydride. Compounds capable of forming phthalocyanine rings usable in the present invention include, for example, phthalic acid salt, phthalic anhydride, phthalimide, phthalamic acid or a salt or ester thereof, a phthalic acid ester and phthalonitrile. Copper or a compound thereof usable in the present invention include, for example, metallic copper, cuprous or cupric halide, copper oxide, copper cyanide, copper sulfate, copper nitrate, copper phosphate, copper acetate, copper sulfide and copper hydroxide. The amount of the copper or copper compound used is generally from 1 to 1.3 mol every 4 mol of the phthalic acid and/or derivative thereof. The amount of urea used in the present invention is typically from 4 to 40 mol every 4 mol of the phthalic acid and/or derivatives thereof. Catalysts usable in the present invention include, for example, molybdenum compounds such as ammonium molybdate, molybdenum oxide and phosphomolybdenic acid, titanium compounds such as titanium tetrachloride and titanic acid ester, zirconium compounds such as zirconium chloride and zirconium carbonate. In the present invention, the compounds (1) - (9) above are used in such an amount, preferably, from 1 to 30 % by weight, and more preferably from 3 to 10 % by weight based on the compound capable of forming the phthalocyanine ring such as phthalic acid. The compounds (1) - (9) above may be added at any time before the formation of the phthalocyanine ring. The temperature is usually within the range of from 150 to 250 °C. The compounds (1) - (9) above are discussed in further detail. Aliphatic tetracarboxylic acids (1) include aliphatic tetracarboxylic acids and aliphatic tetracarboxylic dianhydrides. Compounds of (VI) - (VIII) are preferably used : wherein each X,which may be the same or different, represents O or n represents a number of 2 - 4 and A represents a direct bond or an aliphatic hydrocarbon or aromatic hydrocarbon residue; wherein each X,which may be the same or different, represents O or B represents an aliphatic cyclic residue having 4 to 8 carbon atoms. wherein each X,which may be the same or different, represents O or n represents a number from 2 to 4, K represents an unsubstituted, substituted or ring-condensed aliphatic cyclic residue having 4 to 10 carbon atoms. As examples, the following compounds are mentioned: Copper phthalocyanine sulfonic acid (4) means a compound of formula (IX) : wherein each M,which may be the same or different, represents hydrogen or an alkali metal and n represents a number from 0.2 to 3. As examples, the following compounds are mentioned: As described above, the compound represented by the formula (IX) above includes both individual compounds and mixtures thereof in which n represents a number of the total sulfonic acid groups based on the entire copper phthalocyanine nucleus in the individual compound or a mixture thereof. The present inventors have further found that the compound represented by the formula (IX) in which n is 0.2 - 3, preferably 0.5 - 2, is particularly preferred not only for obtaining the pigment particles without any pigmentation but also for the synthesis of ε-type copper phthalocyanine. That is, it is known that there are a number of crystal forms in copper phthalocyanine, and red-shade α-type and green-shade β-type are usually used as pigments. Further, ε-type which shows clearer hue in red-shade and excellent in the solvent stability than α-type is so expensive that it was not widely used. The present process also provides a process for producing the ε-type copper phthalocyanine having extremely disirable property and is of an industrial value without any pigmentation. The compound of the formula (I) in (5) above is prepared easily by the following method. That is, pyromellitic acid, pyromellitic anhydride or pyromellitic acid diimide is heated in an inert organic solvent with urea, copper or compound thereof, e.g., cuprous chloride, cupric chloride or copper sulfate in the presence of a catalyst, e.g., ammonia molybdate, titanium tetrachloride or antimonium oxide. As an alternative method, tetracyano benzene is heated together with a metal salt and then treated with a strong alkali to obtain a phthalocyanine octacarboxylate which is reacted with, for example ammonia to produce the corresponding imide. The method of synthesizing the compound (I) will be described later in the synthesis example. The compound represented by the formula (II) in the (6) includes the following compounds: wherein R represents an alkyl group, allyl group or aralkyl group wherein Y represents a phenyl group or derivatives thereof or naphthalene ring or derivatives thereof, phthalocyanine ring or the derivative thereof. As the specific examples, the following compounds are exemplified: wherein Cu-Pc represents copper phthalocyanine ring and n = 1 - 4. Compounds represented by the formula (III) in (7) above include the followings: where n and n' represent an integer from 1 to 18. 4 ○ A mixture of No. 1 and No. 2 compounds above wherein R and R' each represents an alkyl group, aralkyl group or cycloalkyl group. Compounds represented by the formula (IV) in (8) include, for example, 4-sulfophthalic acid, 4-sulfophthalimide, 3-sulfophthalimide or alkali metal salts thereof, preferably 4-sulfophthalic acid. Compounds represented by the formula (V) in (9) include, for example, benzene-1,2,3-tricarboxylic acid, benzene hexacarboxylic acid, benzene-1,2,3,4- or 1,2,3,5-tetracarboxylic acid. According to the present invention, the desired copper phthalocyanine pigment is obtained easily by substantially the same reaction procedures as those for producing usual crude copper phthalocyanine. Copper phthalocyanine pigment obtained by the reaction is recovered by distilling off a solvent from a reaction mass under a reduced pressure, washing the product obtained with water or aqueous mineral acid solution and then filtering the same. Alternatively, the reaction mass is mixed with warm water followed by filtration. It is surprising that a copper phthalocyanine usable as it is as a pigment is obtained only by way of the synthesis reaction step using phthalic acids without any pigmentation step as compared with the conventional process for producing copper phthalocyanine pigment. When the thus prepared copper phthalocyanine pigment is dispersed into a medium depending on the purpose, such as resin, varnish, plastic, paints, inks, plastic or colorants are produced. Copper phthalocyanine pigment thus obtained is particularly suitable as color matching pigment for black ink using carbon black. In particular, the present pigment has more desired hue and printability than any conventional Copper phthalocyanine pigments or an Alkali blue used for color matching. Any amount of the present copper phthalocyanine pigment may be used to this effect, as long as red-shade specific to carbon black disappears and the desired performances as black ink becomes to display. Color matching may be conducted by adding the present pigment as well as carbon black to a vehicle or varnish when they are being processed to form dispersion in mixers such as kneaders, three-rolls mills or beads-mills. Alternatively, the present pigment is added to a suitable vehicle or varnish to produce processing pigment or toner before it is added to black ink. In the accompanying drawings, Figures 1-4 are X-ray diffraction spectrum of β-type copper phthalocyanine pigment in Example 6, IR-spectrum of structural formula (I) referred to in Example 14, X-ray diffraction spectrum of β-type copper phthalocyanine in Reference example 1 and X-ray diffraction spectrum of β-type copper phthalocyanine in Referrence example 8, respectively. Examples The present invention will now be described referring to Examples, Comparative Examples, and Reference Examples. In the examples "parts" and "%" are based on the weight and the specific surface area value is determined by N₂ gas adsorption of BET method. Example 1 592 parts of phthalic anhydride, 960 parts of urea, 105 parts of cuprous chloride, 80 parts of titanium tetrachloride and 30 parts of tetracarboxylic acid represented by the following formula : were added to 4,500 parts of sulfolane, the temperature was elevated to 180 - 190°C under stirring and the mixture was heated at that temperature for 5 hours. Then, the mixture was cooled to 100°C and then 5000 parts of warm water (60°C) was added. Then the reaction mass was filtered and, after the completion of the filtration, washed with 5,000 parts of warm water at 80°C. Then, recovered wet cake was added to 10,000 parts of 2 % aqueous hydrochloric acid and then filtered after being stirred at 60°C for one hour. Then, the cake was washed with 10,000 parts of warm water at 80°C and dried to obtain 575 parts of the desired copper phthalocyanine. Specific surface area of the resultant compound was 70 m²/g. Example 2 592 parts of phthalic anhydride, 960 parts of urea, 105 parts of cuprous chloride, 50 parts of titanium tetrachloride and 60 parts of tetracarboxylic acid represented by the following formula : were added to 4,500 parts of sulfolane, the temperature was elevated to 180 - 190°C under stirring and the mixture was heated at that temperature for 5 hours. Then, the mixture was cooled to 100°C and then 5,000 parts of warm water of 60°C was added. Then, the reaction mass was filtered and, after the completion of the filtration, washed with 5,000 parts of warm water at 80°C. Then, recovered wet cake was added to 10,000 parts of 2 % aqueous hydrochloric acid and filtered after being stirred at 60°C for on hour. Then, the cake was washed with 10,000 parts of warm water at 80°C and dried to obtain 575 parts of the desired copper phthalocyanine. Specific surface area of the resultant compound was 75 m²/g. Example 3 592 parts of phthalic anhydride, 960 parts of urea, 140 parts of cuprous chloride, 90 parts of titanium tetrachloride and 60 parts of tetracarboxylic acid represented by the following formula : were added to 6,000 parts of sulfolane, the temperature was elevated to 170 - 180°C under stirring and the mixture was heated at that temperature for 7 hours. Then, the mixture was cooled to 100°C and then 5,000 parts of warm water of 60°C was added. Then, the reaction mass was filtered and, after the completion of the filtration, washed with 5,000 parts of warm water at 80°C. Then, recovered wet cake was added to 10,000 parts of 2 % aqueous hydrochloric acid and filtered after being stirred at 60°C for one hour. Then, the cake was washed with 10,000 parts of warm water at 80°C and dried to obtain 575 parts of the desired copper phthalocyanine. Specific surface area of the resultant compound was 75 m²/g. Example 4 592 parts of phthalic anhydride, 960 parts of urea, 150 parts of cuprous chloride, 10 parts of titanium tetrachloride and 30 parts of tetracarboxylic acid represented by the following formula : were added to 5,000 parts of N-methylpyrrolidone, the temperature was elevated to 180 - 190°C under stirring and the mixture was heated at that temperature for 5 hours. Then, the mixture was cooled to 100°C and then 5,000 parts of warm water of 60°C was added. Then, the reaction mass was filtered and, after the completion of the filtration, washed with 5,000 parts of warm water at 80°C. Then, recovered wet cake was added to 10,000 parts of 2 % aqueous hydrochloric acid and filtered after being stirred at 60°C for one hour. Then, the cake was washed with 10,000 parts of warm water at 80°C and dried to obtain 550 parts of copper phthalocyanine. Specific surface area of the resultant compound was 70 m²/g. Example 5 592 parts of phthalic anhydride, 1,000 parts of urea, 100 parts of cuprous chloride, 6 parts of ammonium molybdate and 30 parts of tetracarboxylic acid represented by the following formula : were added to 4,500 parts of sulfolane, the temperature was elevated to 180 - 190°C under stirring and the mixture was heated at that temperature for 5 hours. Then the mixture was cooled to 100°C and then 5,000 parts of warm water of 60°C was added. Then, the reaction mass was filtered and, after the completion of the filtration, washed with 5,000 parts of warm water at 80°C. Then, recovered wet cake was added to 10,000 parts of 2 % aqueous hydrochloric acid and filtered after being stirred at 60°C for one hour. Then, the cake was washed with 10,000 parts of warm water at 80°C and dried to obtain 565 parts of copper phthalocyanine. Specific surface area of the resultant compound was 70 m²/g. Example 6 592 parts of phthalic anhydride, 960 parts of urea, 105 parts of cuprous chloride, 80 parts of titanium tetrachloride and 30 parts of benzophenone-3,3′,4,4′-tetracarboxylic acid were added to 5,000 parts of sulfolane, the temperature was elevated to 180 - 190°C under stirring and the mixture was heated at that temperature for 5 hours. Then, they were cooled to 100°C and then 5,000 parts of warm water of 60°C was added. Then, the reaction mass was filtered and, after the completion of the filtration, washed with 10,000 parts of warm water at 80°C. Then, recovered wet cake was added to 5,000 parts of 2 % aqueous hydrochloric acid and filtered after being stirred at 60°C for one hour. Then, the cake was washed with 10,000 parts of warm water at 80°C and dried to obtain 575 parts of β-type copper phthalocyanine pigment having X-ray diffraction spectrum shown in Figure 1. The specific surface area of the product was 120 m²/g. Example 7 592 parts of phthalic anhydride, 960 parts of urea, 105 parts of cuprous chloride, 80 parts of titanium tetrachloride and 50 parts of benzophenone-3,3′,4,4′-tetracarboxylic acid dianhydride were added to 6,000 parts of sulfolane, the temperature was elevated to 180 - 190°C under stirring and the mixture was heated at that temperature for 5 hours. Then, the mixture was cooled to 100°C and then 5,000 parts of warm water of 60°C was added. Then, the reaction mass was filtered and, after the completion of the filtration, washed with 5,000 parts of warm water at 80°C. Then, recovered wet cake was added to 10,000 parts of 2 % aqueous hydrochloric acid and filtered after being stirred at 60°C for one hour. Then, the cake was washed with 10,000 parts of warm water at 80°C and dried to obtain 570 parts of β-type copper phthalocyanine. The specific surface area of the resultant compound was 115 m²/g. Example 8 592 parts of phthalic anhydride, 960 parts of urea, 105 parts of cuprous chloride, 80 parts of titanium tetrachloride and 30 parts of pyromellitic acid were added to 4,500 parts of sulfolane, the temperature was elevated to 180 - 190°C under stirring and the mixture was heated at that temperature for 5 hours. Then, the mixture was cooled to 100°C and then 5,000 parts of warmed water of 60°C was added. Then, the reaction mass was filtered and, after the completion of the filtration, washed with 5,000 parts of warm water at 80°C. Then, recovered wet cake was added to 10,000 parts of 2 % aqueous hydrochloric acid and filtered after being stirred at 60°C for one hour. Then, the cake was washed with 10,000 parts of warm water at 80°C and dried to obtain 575 parts of copper phthalocyanine. The purity of the resultant compound was 95 % and the specific surface area thereof was 120 m²/g. Example 9 592 parts of phthalic anhydride, 960 parts of urea, 105 parts of cuprous chloride, 50 parts of titanium tetrachloride and 59 parts of pyromellitic acid were added to 4,500 parts of sulfolane, the temperature was elevated to 180 - 190°C under stirring and the mixture was heated at that temperature for 5 hours. Then, the mixture was cooled to 100°C and then 5,000 parts of warm water of 60°C was added. Then, the reaction mass was filtered and, after the completion of the filtration, washed with 5,000 parts of warm water at 80°C. Then, recovered wet cake was added to 10,000 parts of 2 % aqueous hydrochloric acid and filtered after being stirred at 60°C for one hour. Then, the cake was washed with 10,000 parts of warm water at 80°C and dried to obtain 575 parts of copper phthalocyanine. The purity of the resultant compound was 96 % and the specific surface area thereof was 105 m²/g. Example 10 592 parts of phthalic anhydride, 1,000 parts of urea, 108 parts of cuprous chloride, 90 parts of titanium tetrachloride and 20 parts of pyromellitic anhydride were added to 5,000 parts of sulfolane, the temperature was elevated to 180 - 190°C under stirring and the mixture was heated at that temperature for 7 hours. Then, the mixture was cooled to 100°C and then 5,000 parts of warm water of 60°C was added. Then, the reaction mass was filtered and, after the completion of the filtration, washed with 5,000 parts of warm water at 80°C. Then, recovered wet cake was added to 10,000 parts of 2 % aqueous hydrochloric acid and filtered after being stirred at 60°C for one hour. Then, the cake was washed with 10,000 parts of warm water at 80°C and dried to obtain 600 parts of copper phthalocyanine. The purity of the resultant compound was 90 % and the specific surface area thereof was 95 m²/g. Example 11 592 parts of phthalic anhydride, 800 parts of urea, 100 parts of cuprous chloride, 4 parts of ammonium molybdate and 40 parts of pyromellitic anhydride were added to 4,500 parts of sulfolane, the temperature was elevated to 180 - 190°C under stirring and the mixture was heated at that temperature for 5 hours. Then, the mixture was cooled to 100°C and then 5,000 parts of warm water of 60°C was added. Then, the reaction mass was filtered and, after the completion of the filtration, washed with 5,000 parts of warm water at 80°C. Then, recovered wet cake was added to 8,000 parts of 2 % aqueous hydrochloric acid and filtered after being stirred at 60°C for one hour. Then, the cake was washed with 10,000 parts of warm water at 80°C and dried to obtain 550 parts of the desired copper phthalocyanine. The purity of the resultant compound was 95 % and the specific surface area thereof was 110 m²/g. Example 12 592 parts of phthalic anhydride, 960 parts of urea, 105 parts of cuprous chloride, 80 parts of titanium tetrachloride and 30 parts of copper phthalocyanine sulfonic acid (n = 0.9 in the formula (IX)) were added to 4,500 parts of sulfolane, the temperature was elevated to 180 - 190°C under stirring and the mixture was heated at that temperature for 5 hours. Then, the mixture was cooled to 100°C and then 5,000 parts of warm water of 60°C was added. Then, the reaction mass was filtered and, after the completion of the filtration, washed with 5,000 parts of warm water at 80°C. Then, recovered wet cake was added to 10,000 parts of 2 % aqueous hydrochloric acid and filtered after being stirred at 60°C for one hour. Then, the cake was washed with 10,000 parts of warm water at 80°C and dried to obtain 590 parts of the desired copper phthalocyanine pigment. Purity of the resultant compound was 95 % and the specific surface area thereof was 65 m²/g. Further, the crystal form was ε-type. Example 13 592 parts of phthalic anhydride, 960 parts of urea, 105 parts of cuprous chloride, 50 parts of titanium tetrachloride and 30 parts of sodium copper phthalocyanine sulfonate (n = 1.9 in the formula (IX)) were added to 4,500 parts of sulfolane, the temperature was elevated to 180 - 190°C under stirring and the mixture was heated at that temperature for 5 hours. Then, the mixture was cooled to 100°C and then 5,000 parts of warm water of 60°C was added. Then, the reaction mass was filtered and, after the completion of the filtration, washed with 5,000 parts of warm water at 80°C. Then, recovered wet cake was added to 10,000 parts of 2 % aqueous hydrochloric acid and filtered after being stirred at 60°C for one hour. Then, the cake was washed with 10,000 parts of warm water at 80°C and dried to obtain 585 parts of copper phthalocyanine pigment. Purity of the resultant compound was 96 % and the specific surface area thereof was 70 m²/g. Further, the crystal form was ε-type. Example 14 (Synthesis Example of the coexistent compound having the formula (I)) 872 parts of pyromellitic anhydride, 960 parts of urea, 105 parts of cuprous chloride and 80 parts of titanium tetrachloride were added to 9,000 parts of sulfolane, the temperature was elevated to 190 - 200°C under stirring and the mixture was heated at that temperature for 10 hours. Then, the mixture was cooled to 100 °C and then, 5,000 parts of warm water of 60°C was added. Then, the reaction mass was filtered and, after the completion of the filtration, washed with 10,000 parts of warm water at 80°C. Then, recovered wet cake was added to 15,000 parts of 2 % aqueous hydrochloric acid and filtered after being stirred at 60°C for 2 hours. Then, the cake was washed with 1,500 parts of warm water at 80°C. Then, the wet cake was taken out and added to 10,000 parts of aqueous 10 % ammonia solution and stirred at 30 - 35°C for one hour. Then, the cake was filtered and washed with 10,000 parts of water at 30°C. Further, the wet cake was taken out, added to 5,000 parts of DMF at 50°C, stirred for 2 hours and then filtered. Similar DMF processing was conducted further twice. Then, the cake was washed with methanol, washed with water and then dried to obtain 650 parts of blue green crystals. The melting point of the compound was higher than 300°C. Elemental analysis found: C = 56.0 %, H = 1.8 %, N = 19.9 % and Cu = 7.3 %. These values well agree to those calculated which are given below, assuming the structural formula (I): C = 56.4 % H = 1.9 % N = 19.7 % Cu = 7.5 % Further, the above-mentioned structural formula was confirmed by IR shown in Figure 2. (Synthesis of copper phthalocyanine pigment) 592 parts of phthalic anhydride, 960 parts of urea, 105 parts of cuprous chloride, 80 parts of titanium tetrachloride and 30 parts of copper phthalocyanine derivative (I) obtanined in the foregoing Synthesis Example were added to 6,000 parts of sulfolane, the temperature was elevated to 180 - 190°C under stirring and the mixture was heated at that temperature for 5 hours. Then, the mixture was cooled to 100°C and then 5,000 parts of warmed water of 60°C was added. Then, the reaction mass was filtered and, after the completion of the filtration, washed with 5,000 parts of warm water at 80°C. Then, recovered wet cake was added to 10,000 parts of 2 % aqueous hydrochloric acid and filtered after being stirred at 60°C for one hour. Then, the cake was washed with 10,000 parts of warm water at 80°C and dried to obtain 580 parts of copper phthalocyanine. The specific surface area of the resultant compound was 90 m²/g. Example 15 592 parts of phthalic anhydride, 960 parts of urea, 140 parts of cuprous bromide, 20 parts of titanium tetrachloride and 30 parts of copper phthalocyanine derivative (I) obtanined in the foregoing Synthesis Example were added to 6,000 parts of sulfolane, the temperature was elevated to 180 - 190°C under stirring and the mixture was heated at that temperature for 5 hours. Then, the mixture was cooled to 100°C and then 5,000 parts of warm water of 60°C was added. Then, the reaction mass was filtered and, after the completion of the filtration, washed with 5,000 parts of warm water at 80°c. Then, recovered wet cake was added to 10,000 parts of 2 % aqueous hydrochloric acid and filtered after being stirred at 60°C for one hour. Then, the cake was washed with 10,000 parts of warm water at 80°C and dried to obtain 576 parts of copper phthalocyanine. The specific surface area of the resultant compound was 80 m²/g. Example 16 592 parts of phthalic anhydride, 960 parts of urea, 105 parts of cuprous chloride, 6 parts of ammonium molybdate and 45 parts of copper phthalocyanine derivative (I) obtained in the foregoing Synthesis Example were added to 6,000 parts of sulfolane, the temperature was elevated to 180 - 190°C under stirring and the mixture was heated at that temperature for 5 hours. Then, they were cooled to 100°C and then, 5,000 parts of warm water of 60°C was added. Then, the reaction mass was filtered and, after the completion of the filtration, washed with 5,000 parts of warm water at 80°C. Then, recovered wet cake was added to 10,000 parts of 2 % aqueous hydrochloric acid and filtered after being stirred at 60°C for one hour. Then, the cake was washed with 10,000 parts of warm water at 80°C and dried to obtain 578 parts of copper phthalocyanine. The specific surface area of the resultant compound was 80 m²/g. Example 17 592 parts of phthalic anhydride, 960 parts of urea, 105 parts of cuprous chloride, 80 parts of titanium tetrachloride and 30 parts of 3,4,5,6-tetrahydrophthalimide were added to 4,500 parts of sulfolane, the temperature was elevated to 180 - 190°C under stirring and the mixture was heated at that temperature for 5 hours. Then the mixture was cooled to 100°C and then 5,000 parts of warm water of 60°C was added. Then, the reaction mass was filtered and, after the completion of the filtration, washed with 5,000 parts of warm water at 80°C. Then, recovered wet cake was added to 10,000 parts of 2 % aqueous hydrochloric acid and filtered after being stirred at 60°C for one hour. Then, the cake was washed with 10,000 parts of warm water at 80°C and dried to obtain 575 parts of the desired copper phthalocyanine. Purity of the resultant compound was 95 % and the specific surface area thereof was 70²m /g. Example 18 592 parts of phthalic anhydride, 960 parts of urea, 105 parts of cuprous chloride, 50 parts of titanium tetrachloride and 35 parts of 3,4,5,6-tetrahydrophthalic anhydride were added to 4,500 parts of sulfolane, temperature was elevated to 180 - 190°C under stirring and the mixture was heated at that temperature for 5 hours. Then, the mixture was cooled to 100°C and then 5,000 parts of warm water of 60°C was added. Then, the reaction mass was filtered and, after the completion of the filtration, washed with 5,000 parts of warm water at 80°C. Then, recovered wet cake was added to 10,000 parts of 2 % aqueous hydrochloric acid and filtered after being stirred at 60°C for one hour. Then, the cake was washed with 10,000 parts of warm water at 80°C and dried to obtain 575 parts of copper phthalocyanine. Purity of the resultant compound was 96 % and the specific surface area thereof was 73 m²/g. Example 19 592 parts of phthalic anhydride, 1,000 parts of urea, 108 parts of cuprous chloride, 90 parts of titanium tetrachloride and 40 parts of N-hydroxymethyl-3,4,5,6-tetrahydrophthalimide were added to 5000 parts of sulfolane, the temperature was elevated to 180 - 190°C under stirring and the mixture was heated at that temperature for 5 hours. Then, the mixture was cooled to 100°C and then, 5,000 parts of warm water of 60°C was added. Then, the reaction mass was filtered and, after the completion of the filtration, washed with 5,000 parts of warm water at 80°C. Then, recovered wet cake was added to 10,000 parts of 2 % aqueous hydrochloric acid and filtered after being stirred at 60°C for one hour. Then, the cake was washed with 10,000 parts of warm water at 80°C and dried to obtain 600 parts of copper phthalocyanine. Purity of the resultant compound was 90 % and the specific surface area thereof was 85²m /g. Example 20 592 parts of phthalic anhydride, 960 parts of urea, 105 parts of cuprous chloride, 80 parts of titanium tetrachloride and 35 parts of benzotriazole derivative of the following structure : were added to 6,000 parts of sulfolane, the temperature was elevated to 180 - 190°C under stirring and the mixture was heated at that temperature for 5 hours. Then, the mixture was cooled to 100°C and then 5,000 parts of warm water of 60°C was added. Then, the reaction mass was filtered and, after the completion of the filtration, washed with 5,000 parts of warm water at 80°C. Then, recovered wet cake was added to 10,000 parts of 2 % aqueous hydrochloric acid and filtered after being stirred at 60°C for one hour. Then, the cake was washed with 10,000 parts of warm water at 80°C and dried to obtain 590 parts of copper phthalocyanine. Purity of the resultant compound was 92 % and the specific surface area thereof was 70²m /g. Example 21 592 parts of phthalic anhydride, 960 parts of urea, 105 parts of cuprous chloride, 80 parts of titanium tetrachloride and 40 parts of a mixture of phthalocyanine derivatives of the following structure : wherein n = 1-4 and Cu-Pc represents copper phthalocyanine ring, were added to 5,500 parts of sulfolane, the temperature was elevated to 180 - 190°C under stirring and the mixture was heated at that temperature for 5 hours. Then, the mixture was cooled to 100°C and then 5,000 parts of warm water of 60°C was added. Then, the reaction mass was filtered and, after the completion of the filtration, washed with 5,000 parts of warm water at 80°C. Then, recovered wet cake was added to 8,500 parts of 2 % aqueous hydrochloric acid and filtered after being stirred at 60°C for one hour. Then, the cake was washed with 10,000 parts of warm water at 80°C and dried to obtain 600 parts of copper phthalocyanine. Purity of the resultant compound was 95 % and the specific surface area thereof was 80 m²/g. Example 22 592 parts of phthalic anhydride, 800 parts of urea, 100 parts of cuprous chloride, 4 parts of ammonium molybdate and 30 parts of 3,4,5,6-tetrahydrophthalimide were added to 4,500 parts of sulfolane, the temperature was elevated to 180 - 190°C under stirring and the mixture was heated at that temperature for 5 hours. Then, the mixture was cooled to 100°C and then 5,000 parts of warm water of 60°C was added. Then, the reaction mass was filtered and, after the completion of the filtration, washed with 5,000 parts of warm water at 80°C. Then, recovered wet cake was added to 8,000 parts of 2 % aqueous hydrochloric acid and filtered after being stirred at 60°C for one hour. Then, the cake was washed with 10,000 parts of warm water at 80°C and dried to obtain 550 parts of copper phthalocyanine. Purity of the resultant compound was 95 % and the specific surface area thereof was 70 m²/g. Example 23 592 parts of phthalic anhydride, 720 parts of urea, 200 parts of cuprous iodide, 40 parts of titanium tetrachloride and 12 parts of 3,4,5,6-tetrahydophthalimide were added to 4,500 parts of sulfolane, the temperature was elevated to 180 -190°C under stirring and the mixture was heated at that temperature for 5 hours. Then, the mixture was cooled to 100°C and then 5,000 parts of warm water of 60°C was added. Then, the reaction mass was filtered and, after the completion of the filtration, washed with 5,000 parts of warm water at 80°C. Then, recovered wet cake was added to 10,000 parts of 2 % aqueous hydrochloric acid and filtered after being stirred at 60°C for one hour. Then the cake was washed with 10,000 parts of warm water at 80°C and dried to obtain 530 parts of copper phthalocyanine. Purity of the resultant compound was 95 % and the specific surface area thereof was 73 m²/g. Example 24 592 parts of phthalic anhydride, 960 parts of urea, 105 parts of cuprous chloride, 50 parts of titanium tetrachloride and 30 parts of an imide represented by the following formula : were added to 4,500 parts of sulfolane, the temperature was elevated to 180 - 190°C under stirring and the mixture was heated at that temperature for 5 hours. Then, the mixture was cooled to 100°C and then 5,000 parts of warm water of 60°C was added. Then, the reaction mass was filtered and, after the completion of the filtration, washed with 5,000 parts of warm water at 80°C. Then, recovered wet cake was added to 5,000 parts of 2 % aqueous hydrochloric acid and filtered after being stirred at 60°C for one hour. Then, the cake was washed with 5,000 parts of warm water at 80°C and dried to obtain 575 parts of copper phthalocyanine. The specific surface area of the resultant compound was 90 m²/g. Example 25 592 parts of phthalic anhydride, 960 parts of urea, 105 parts of cuprous chloride, 80 parts of titanium tetrachloride and 45 parts of imide methylol represented by the following formula : were added to 6,000 parts of sulfolane, the temperature was elevated to 180 - 190°C under stirring and the mixture was heated at that temperature for 5 hours. Then, the mixture was cooled to 100°C and 5,000 parts of warm water of 60°C was added. Then, the reaction mass was filtered and, after the completion of the filtration, washed with 5,000 parts of warm water at 80°C. Then, recovered wet cake was added to 5,000 parts of 2 % aqueous hydrochloric acid and filtered after being stirred at 60°C for one hour. Then, the cake was washed with 5,000 parts of warm water at 80°C and dried to obtain 590 parts of copper phthalocyanine. The specific surface area of the resultant compound was 90 m²/g. Example 26 592 parts of phthalic anhydride, 800 parts of urea, 100 parts of cuprous chloride, 4 parts of ammonium molybdate and 40 parts of imide represented by the following formula : were added to 4,500 parts of sulfolane, the temperature was elevated to 180 - 190°C under stirring and the mixture was heated at that temperature for 5 hours. Then, the mixture was cooled to 100°C and then 5,000 parts of warm water of 60°C was added. Then, the reaction mass was filtered and, after the completion of the filtration, washed with 5,000 parts of warm water at 80°C. Then, recovered wet cake was added to 8,000 parts of 2 % aqueous hydrochloric acid and filtered after being stirred at 60°C for one hour. Then, the cake was washed with 10,000 parts of warm water at 80°C and dried to obtain 550 parts of copper phthalocyanine. The specific surface area of the resultant compound was 85 m²/g. Example 27 592 parts of phthalic anhydride, 960 parts of urea, 105 parts of cuprous chloride, 80 parts of titanium tetrachloride and 30 parts of 4-sulfophthalic acid were added to 6,000 parts of sulfolane, the temperature was elevated to 180 - 190°C under stirring and the mixture was heated at that temperature for 5 hours. Then, the mixture was cooled to 100°C and then 5,000 parts of warm water of 60°C was added. Then, the reaction mass was filtered and, after the completion of the filtration, washed with 5,000 parts of warm water at 80°C. Then, recovered wet cake was added to 10,000 parts of 2 % aqueous hydrochloric acid and filtered after being stirred at 60°C for one hour. Then, the cake was washed with 10,000 parts of warm water at 80°C and dried to obtain 578 parts of copper phthalocyanine. The specific surface area of the resultant compound was 102 m²/g. Example 28 592 parts of phthalic anhydride, 960 parts of urea, 105 parts of cuprous chloride, 80 parts of titanium tetrachloride and 30 parts of 4-sulfophthalimide were added to 6,000 parts of sulfolane, the temperature was elevated to 180 - 190°C under stirring and the mixture was heated at that temperature for 5 hours. Then, the mixture was cooled to 100°C and then 5,000 parts of warm water of 60°C was added. Then, the reaction mass was filtered and, after the completion of the filtration, washed with 5,000 parts of warm water at 80°C. Then, recovered wet cake was added to 10,000 parts of 2 % aqueous hydrochloric acid and filtered after being stirred at 60°C for one hour. Then, it was washed with 10,000 pats of warm water at 80°C and dried to obtain 573 parts of copper phthalocyanine. The specific surface area of the resultant compound was 100 m²/g. Example 29 592 parts of phthalic anhydride, 960 parts of urea, 105 parts of cuprous chloride, 50 parts of titanium tetrachloride and 30 parts of 4-sulfophthalic acid were added to 6,000 parts of dimethylsulfoxide, the temperature was elevated to 170 - 180°C under stirring and the mixture was heated at that temperature for 5 hours. Then, the mixture was cooled to 100°C and then 5,000 parts of warm water of 70°C was added. Then, the reaction mass was filtered and, after the completion of the filtration, washed with 5,000 parts of warm water at 80°C. Then, recovered wet cake was added to 10,000 parts of 5 % aqueous hydrochloric acid and filtered after being stirred at 60°C for one hour. Then, the cake was washed with 10,000 parts of warm water at 80°C and dried to obtain 540 parts of copper phthalocyanine. The specific surface area of the resultant compound was 80 m²/g. Example 30 592 parts of phthalic anhydride, 1,000 parts of urea, 100 parts of cuprous chloride, 50 parts of titanium tetrachloride and 60 parts of 4-sulfophthalimide were added to 6,000 parts of sulfolane, the temperature was elevated to 210 - 220°C under stirring and the mixture was heated at that temperature for 3 hours. Then, the mixture was cooled to 100°C and then 5,000 parts of warm water of 60°C was added. Then, the reaction mass was filtered and, after the completion of the filtration, washed with 5,000 parts of warm water at 80°C. Then, recovered wet cake was added to 10,000 parts of 2 % aqueous hydrochloric acid and filtered after being stirred at 60°C for one hour. Then, it was washed with 10,000 parts of warm water at 80°C and dried to obtain 598 parts of copper phthalocyanine. The specific surface area of the resultant compound was 90 m²/g. Example 31 592 parts of phthalic anhydride, 1,000 parts of urea, 100 parts of cuprous chloride, 6 parts of ammonium molybdate and 30 parts of trisodium 4-sulfophthalate were added to 4,500 parts of sulfolane, the temperature was elevated to 180 - 190°C under stirring and the mixture was heated at that temperature for 5 hours. Then, the mixture was cooled to 100°C and then 5,000 parts of warm water of 60°C was added. Then, the reaction mass was filtered and, after the completion of the filtration, washed with 5,000 parts of warm water at 80°C. Then, recovered wet cake was added to 10,000 parts of 2 % aqueous hydrochloric acid and filtered after being stirred at 60°C for one hour. Then, the cake was washed with 10,000 parts of warm water at 80°C and dried to obtain 565 parts of copper phthalocyanine. The specific surface area of the resultant compound was 98 m²/g. Example 32 592 parts of phthalic anhydride, 960 parts of urea, 150 parts of cuprous chloride, 80 parts of titanium tetrachloride and 30 parts of hemimellitic acid (benzene-1,2,3-tricarboxylic acid) were added to 4,500 parts of sulfolane, the temperature was elevated to 180 - 190°C under stirring and the mixture was heated at that temperature for 5 hours. Then, the mixture was cooled to 100°C and then 5,000 parts of warm water of 60°C was added. Then, the reaction mass was filtered and, after the completion of the filtration, washed with 5,000 parts of warm water at 80°C. Then, recovered wet cake was added to 10,000 parts of 2 % aqueous hydrochloric acid and filtered after being stirred at 60°C for one hour. Then, it was washed with 10,000 parts of warm water at 80°C and dried to obtain 575 parts of copper phthalocyanine. The specific surface area of the product was 75 m²/g. Example 33 592 parts of phthalic anhydride, 960 parts of urea, 150 parts of cuprous chloride, 80 parts of titanium tetrachloride and 40 parts of mellitic acid (benzene-hexacarboxylic acid) were added to 4,500 parts of sulfolane, the temperature was elevated to 180 - 190°C under stirring and the mixture was heated at that temperature for 5 hours. Then, the mixture was cooled to 100°C and then 5,000 parts of warm water of 60°C was added. Then, the reaction mass was filtered and, after the completion of the filtration, washed with 5,000 parts of warm water at 80°C. Then, recovered wet cake was added to 10,000 parts of 2 % aqueous hydrochloric acid and filtered after being stirred at 60°C for one hour. Then, the cake was washed with 10,000 parts of warm water at 80°C and dried to obtain 570 parts of copper phthalocyanine. The specific surface area of the product was 73 m²/g. Reference example 1 The same reaction as Example 1 was conducted except that no tetracarboxylic acid derivative was present, until 560 parts of β-type copper phthalocyanine having the X-ray diffraction spectrum shown in Figure 3 was obtained. Purity was 95 % and the specific surface area was 25 m²/g. Reference example 2 Examples 3 was repeated except 4,500 parts of nitrobenzene were used in place of 4,500 parts of sulfolane. Color of the reaction mass was not blue but brown. Then, nitrobenzene was removed under a reduced pressure, the residue was added to 5,000 parts of warm water at 60°C. The mixture was stirred at that temperature, filtered and dried. The resultant compound weighed 300 parts. The compound was brown colored and no formation of copper phthalocyanine was confirmed by FD-Mass spectral measurement. Reference examples 3 - 7 592 parts of phthalic anhydride, 960 parts of urea, 105 parts of cuprous chloride were heated to 190 - 200°C under stirring while varying the catalyst, the solvent and the coexistent compounds, and heated at that temperature for 8 hours. Color of the reaction masses was not blue but brown. Reference example 8 Heating under stirring at 180 - 190°C for 5 hours as in Example 7 was conducted except that 3,500 parts of Hisol P (manufactured by Nippon Petroleum Co.) and 10 parts of ammonium molybdate were used in place of 6,000 parts of sulfolane and 80 parts of titanium tetrachloride, respectively. Then, Hisol P was removed under a reduced pressure, the residue was added to 10,000 parts of aqueous 2 % hydrochloric acid, stirred at 60°C for one hour, filtered, washed and then dried to obtain 570 parts of β-type copper phthalocyanine having X-ray diffraction spectrum as shown in Figure 4. The specific surface area of the resultant compound was 35 m²/g. Reference example 9 592 parts of phthalic anhydride, 960 parts of urea, 105 parts of cuprous chloride, 30 parts of pyromellitic acid and 10 parts of ammonium molybdate were added to 5,000 parts of nitrobenzene, the temperature was elevated to 190 - 200°C under stirring and the mixture was heated at that temperature for 5 hours. After the reaction was over, the solvent was removed under a reduced pressure, the residue was added to 10,000 parts of aqueous 2 % hydrochloric acid, stirred at 60°C for one hour, filtered, then washed with 10,000 parts of warm water at 80°C and dried to obtain 570 parts of copper phthalocyanine. The resultant compound had specific surface area of 30 m²/g. Reference example 10 The same procedure as in Example 12 was conducted except that 40 parts of a compound represented by the following formula : was used in place of copper phthalocyanine sulfonic acid, to obtain 570 parts of copper phthalocyanine. Purity was 80 % and the specific surface area was 30 m²/g. The crystal from was β-type. Reference example 11 The same procedure as in Example 32 was conducted except that 30 parts of trimellitic acid (benzene-1,2,4-tricarboxylic acid) was used in place of humimellitic acid, to obtain 576 parts of copper phthalocyanine. The resultant compound had specific surface area of 35 m²/g. Comparative example 1 100 parts of commercially available crude copper phthalocyanine, 400 parts of sodium chloride and 100 parts of ethylene glycol were ground for 5 hours by twine-arm kneader while maintaining at a temperature from 80 to 85°C. The mixture was washed with warm water at 80°C and the then dried to obtain 98 parts of copper phthalocyanine pigment. The purity was 96 % and the specific surface area was 70²m /g. Inks were prepared by using 4 parts of various copper phthalocyanine pigments, 80 parts of titanium white and 160 parts of linseed oil. Tinting strength was measured and listed in the table below. Standard (100) : tinting strength of ink where pigment obtained in comparative example 1 was used. Comparative example 2 4 parts of copper phthalocyanine pigment obtained in Comparative Example 1 was placed in a plastic bottle charged with 90 parts of glass beads (3 mm diameter each), to which 12 parts of melamine alkyd paint varnish and 14 parts of xylene were added. After being processed in a paint shaker for one hour, the mixture was further processed for 10 minutes with additional 50 parts of the same melamine alkyd varnish. Then, the glass beads were filtered using a metal gauge to obtain a blue primary color paint. 3 part of the blue primary color paint and 5 parts of the same kind of white paint containing 30 % titanium white were well mixed by a glass rod to prepare a blue paint. Then, copper phthalocyanines obtained in Examples and Reference Examples were similarly prepared into paints. Tinting strengths thereof were listed in the table below.

Claims: A process for preparing a copper phthalocyanine pigment, which comprises reacting, in a hydrophilic solvent which is sulfolane, 2-methylsulfolane, 3-methylsulfolane, dimethylsulfoxide, 2,4-dimethylsulfolane, N-methylpyrrolidone or 1,3-dimethyl-2-imidazolidinone, in the presence of a catalyst, a compound capable of forming phthalocyanine rings, urea, copper or a compound thereof and at least one compound of formula (1) to (9): (1) an aliphatic tetracarboxylic acid, (2) benzophenone-3,3',4,4'-tetracarboxylic acid or an anhydride thereof, (3) pyromellitic acid or an anhydride thereof, (4) copper phthalocyanine sulfonic acid, (5) a compound of formula (I): (6) a compound of formula (II): wherein X represents O, NH, NCH₂OH, N-R, in which R represents an alkyl group, allyl group or aralkyl group, or a NCH₂Y group in which Y represents a phenyl group or a derivative thereof, a napthalene ring or a derivative thereof or a phthalocyanine ring or derivative thereof, (7) a compound of formula (III): wherein A and B, which may be the same or different, each represents hydrogen, an alkyl group, hydroxyalkyl group, alkoxyalkyl group, cycloalkyl group, allyl group, aralkyl group or a -CH₂Y group in which Y represents a phenyl group or a derivative thereof, a naphthalene ring or a derivative thereof or a phthalocyanine ring or a derivative thereof, (8) a compound of formula (IV): wherein M represents hydrogen or an alkali metal, and A and B, which may be the same or different, each represents a carboxyl group or a group derived from a carboxyl group or A and B together form an imide or acid anhydride, or (9) a compound of formula (V): wherein R₁, R₂ and R₃, which may be the same or different, each represents hydrogen, a carboxyl group or group derived from a carboxyl group, it being possible for R₁ and R₂ or R₂ and R₃ to form, together with the carbons to which they are attached, an imide or acid anhydride ring, and X, Y and Z, which may be the same or different, each represents a carboxyl group, a group derived from a carboxyl group or a nitrile group, it being possible for X and Y, or Y and Z, to form an imide or an acid anhydride. A process according to claim 1, wherein the aliphatic tetracarboxylic acid is a compound of formula (VI): wherein each X, which may be the same or different, represents O or n represents a number from 2 to 4 and A represents a direct bond or an aliphatic hydrocarbon or aromatic hydrocarbon residue. A process according to claim 1, wherein the aliphatic tetracarboxylic acid is a compound of formula (VII): wherein each X, which may be the same or different, represents O or and B represents an aliphatic cyclic residue having from 4 to 10 carbon atoms. A process according to claim 1, wherein the aliphatic tetracarboxylic acid is a compound of formula (VIII): wherein each X, which may be the same or different, represents O or n represents a number from 2 to 4 and K represents an unsubstituted, substituted or ring-condensed cycloaliphatic residue having 4 to 10 carbon atoms. A process according to claim 1, wherein the copper phthalocyanine sulfonic acid is a product of formula (IX): wherein each M, which may be identical or different, represents hydrogen or an alkali metal and n represents a number from 0.2 to 3. A process according to any one of claims 1 to 5, wherein the reaction temperature is from 150 to 250°C. A process according to any one of claims 1 to 6, wherein the compound of formula (1) to (9) is present in an amount of from 1 to 30% by weight based on the weight of the compound capable of forming the phthalocyanine ring. A process according to any one of claims 1 to 7, wherein the compound capable of forming phthalocyanine rings is a phthalic acid salt, phthalic anhydride, phthalimide, phthalamic acid or a salt or ester thereof, a phthalic acid ester or phthalonitrile. A process according to any one of claims 1 to 8, wherein the compound of copper is cuprous or cupric halide, copper oxide, copper cyanide, copper sulphate, copper nitrate, copper phosphate, copper acetate, copper sulfide or copper hydroxide. A process according to any one of claims 1 to 9, wherein the catalyst is a molybdenum compound, a titanium compound or a zirconium compound.

Inventors: FUJITA, TAIRA, KISHIMOTO, TOSHIAKI, OKAYASU, HIROSHI
Applicants: SUMITOMO CHEMICAL COMPANY, LIMITED
Application year: 1987
Main classification: C09B47
IPC codes: C09B47, C09B67