CATALYST FOR POLYMERIZING OLEFINS

Abstract: An olefin polymerisation catalyst contains (1) a catalyst component; (2) a silicon cpd. of formula SiRm(OR')4-m (where R is H, alkyl or aryl; R' is alkyl or aryl; m is 0-4); and (3) an organo-aluminium cpd. The catalyst component (1) is obtd. by reacting (a) a dialkoxymagnesium; (b) a diester of an aromatic dicarboxylic acid (pref. a phthalate); (c) an aromatic hydrocarbon (pref. one which is liq. at room temp.); (d) a titanium halide (pref. the tetrachloride, tetrabromide or tetraiodide) in the presence or absence of a solvent to give a solid compsn., then heat-treating. Specifically, the dialkoxymagnesium is diethoxy-, dibutoxy, diphenoxy, dipropoxy, di-sec. butoxy, di-tert-butoxy, or diisopropoxymagnesium. The diester is dimethyl, diethyl, dipropyl, diisopropyl, dibutyl, diisobutyl, diamyl, diisoamyl, ethyl butyl, ethyl isobutyl or ethyl propyl phthalate. The aromatic hydrocarbon is toluene, o-xylene, m-xylene, p-xylene, benzene, ethylbenzene, propylbenzene or trimethylbenzene. The silicon cpd. is a phenylalkoxysilane such as Ph(R'O)3Si (where R' is methyl, ethyl, propyl, isopropyl) or Ph2(R'O)2Si (where R' is methyl or ethyl), or an alkylalkoxysilane such as (MeO)4Si, (MeO)3EtSi, Et(OiPr)3Si, etc.

Description: Technical Field This invention relates to a process for preparing a catalyst for the polymerization of olefins which exhibits a high catalytic activity and is capable of producing a highly stereoregular olefin polymer having regular particle size distribution in a high yield. Background Art A catalyst for the polymerization of olefins formed by combining a solid titanium halide as a catalyst component with an organoaluminum compound is well known and extensively used in the art. However, in the polymerization of olefins by use of the conventional catalyst, the yield of polymer per unit weight of the catalyst component or of titanium moiety in the catalyst component (hereinafter referred to as a polymerization activity per unit weight of the catalyst component or of titanium moiety in the catalyst component) is so low that the so-called deashing process for removing catalyst residues from the produced polymer is indispensable. In the deashing process, alcohols or chelating agents are used in large amounts, so that the deashing process needs an apparatus for recovery or reprocess thereof, and consequently has many problems accompanying therewith relative to resources and energy. Thus. the deashing process raises great problems to be solved urgently in the art. A number of studies and suggestions have been made for enhancing the polymerization activity per unit weight of catalyst component or of titanium moiety in the catalyst component, so that the complicated deashing process may be dispensed with. Especially as a recent tendency, a large number of suggestions have been made such that the polymerization activity per unit weight of titanium in the catalyst component is remarkably enhanced in the polymerization of olefins with a catalyst component prepared by supporting a transition-metal compound as an active ingredient such as a titanium halide on such a carrier material as magnesium chloride. However, the improved process employing magnesium chloride as a carrier has such drawbacks that chlorine moiety contained in the magnesium chloride predominantly used as the carrier as well as a halogen atom contained in the titanium halide gives bad influence on the resultant polymer, resulting in leaving problems to be solved such as requirements for such a high activity as to be substantially free from the adverse effect due to the chlorine moiety, or as requirements for controlling a concentration of the magnesium chloride itself at a sufficiently low level. FR-A-2 516 520 discloses a catalyst component prepared by reacting diethoxymagnesium, 2-ethylhexylalcohol and decane in the presence of hydrogen chloride to obtain a uniform solution to which phthalic anhydride is added. The obtained solution is reacted with titanium tetrachloride to obtain a solid catalyst component, which is combined with a silicon compound and an organoaluminium compound. GB-A-2 143 834 discloses a catalyst component obtained by contacting (a) a fatty acid salt of magnesium and/or (b) dialkoxymagnesium with (c) mono or diester of an aromatic dicarboxylic acid, (d) a halogenated hydrocarbon and (e) a titanium halide TiX 4 . This catalyst component is combined with a silicon compound and an organoaluminium compound to obtain a catalyst for the polymerization of olefins. However, the known catalysts are not completely satisfactory with respect to overall yield of crystalline polymer and bulk density of produced polymer. The present inventors proposed a process for preparing a catalyst component for the polymerization of olefins in Japanese Patent application No. 200454/1982 for an object of reducing a chlorine content in the produced polymer with high polymerization activity and high yield of stereoregular polymer, attaining the aforementioned object. Further, it is essential for a catalyst formed by combining a catalyst component using magnesium chloride as a carrier with an organoaluminum compound to carry out on an industrial scale the polymerization of olefins, especially stereoregular polymerization of propylene and 1-butene in the presence of an electron donor compound such as aromatic carboxylic acid esters in the polymerization system. However, the aforementioned aromatic carboxylic acid ester imparts a peculiar estereal odor to the produced polymer, raising a serious problem of deodorizing therefrom in the art. It was substantially impossible for the so-called highly active supported catalyst formed by use of a catalyst component employing the aforementioned magnesium chloride as a carrier to be of practical use, because use of the supported catalyst results in abrupt deactivation thereof in spite of high activity thereof in the beginning of polymerization, and results in raising problems in process operations, particularly in the case where a prolonged polymerization time is required as in block copolymerization and the like. In order to solve the aforementioned problems, Japanese Patent laid-open publication No. 94590/1979 discloses a catalyst for the polymerization of olefins which comprises a catalyst component prepared by use of magnesium dihalide as one of the starting materials, an organoaluminum compound, an aromatic carboxylic acid ester, and a compound having a M-O-R group. However, the catalyst disclosed as above fails to solve the problem of deodorizing from the produced polymer in that organic carboxylic acid esters are used on polymerization, and requires complicated procedures for the preparation thereof as shown in the Examples with practically insufficient catalyst performance and polymerization activity with time. Furthermore, it is required in an apparatus for the polymerization of olefins on an industrial scale to supply a catalyst in a polymerization tank which is kept at a high temperature. In this instance, the conventional supported catalysts exhibit significant decrease in catalytic activity, stereospecific performance, and bulk density. This was a big problem, particularly, in a so-called continuous slurry polymerization process using an organic solvent, and the improvement thereof is strongly demanded in the art. The present invention has been made after extensive research and experimentation for overcoming the foregoing disadvantages of the prior art. The present invention provides a process as defined in claim 1. Polymerization of olefins by use of the catalyst component of the present invention shows such a high catalytic activity that the amount of the catalyst residues in the produced polymer is reduced to a very low level, and chlorine content in the produced polymer is reduced to a trace amount, resulting in that influence of chlorine on the produced polymer is reduced to such an extent that the deashing process may be completely dispensed with. Since chlorine contained in the produced polymer causes corrosion of devices employed in such steps as pelletizing and molding, and further causes deterioration. yellowing, of the produced polymer itself, reduction of chlorine content in the produced polymer as above has an extremely important meaning in the art. Further features of the present invention reside in that the problem of the estereal odor in the produced polymer has been solved without using aromatic carboxylic acid esters on polymerization, and that such a substantial defect of the so-called highly active supported catalyst as mentioned above that catalyst activity per unit time is greatly reduced as polymerization proceeds has been overcome to provide a catalyst practically applicable to copolymerization of olefins as well as homopolymerization thereof. It is of a common practice in the preparation of olefinpolymer on an industrial scale that polymerization is carried out in the presence of hydrogen from the standpoints of controlling the melt index of polymer, and the catalyst formed from the catalyst component prepared by use of magnesium chloride as a carrier in the presence of hydrogen has such a disadvantage that both catalytic activity and stereoregularity of the polymer are greatly reduced. However, polymerization of olefins in the presence of hydrogen using the catalyst of the present invention provides such an effect that little or no decrease in catalytic activity and in stereoregularity of the polymer is observed in spite of very high melt index of the polymer, providing extremely great advantages in the art An additional effect of the present invention is in that the catalyst of the present invention has an excellent property in catalytic activity, stereospecific performance and bulk density of the produced polymer which are significantly decreased when the conventional supported catalyst is supplied into a polymerization tank maintained at a high temperature in a polymerization apparatus on an industrial scale, particularly in ths so-called continuous slurry polymerization process using an organic solvent, for which improvements are strongly demanded in the art. The decrease in the bulk density of the produced polymer causes production capacities of the polymerization plant to be seriously deteriorated and invites shutdown of the plant in the worst case. The catalyst of the present invention satisfactorily solves these problems. Best Mode for Carrying out the Invention The dialkoxymagnesium used in the present invention is diethoxymagnesium. The diester of aromatic dicarboxylic acid used in the present invention is dibutylphthalate. The aromatic hydrocarbon used in the present invention is toluene, which is liquid at normal temperature. The titanium halide used in the present invention is TICℓ 4 . Examples of solvent used in the present invention include aliphatic hydrocarbons, aromatic hydrocarbons and hydrocarbon halides which are liquid at normal temperatures. For example. the aromatic hydrocarbons include those having 5 to 15 carbon atoms; the aromatic hydrocarbons include those having 6 to 10 carbon atoms, such as, for example, toluene, o-xylene, m-xylene, p-xylene, benzene, ethylbenzene, propylbenzene and trimethylbenzene; and the hydrocarbon halides include aliphatic hydrocarbon halides having 5 to 15 carbon atoms and aromatic hydrocarbon halides having 6 to 10 carbon atoms. The silicon compound used in the present invention includes phenylalkoxysilanes and alkylalkoxysilanes. Examples of phenylalkoxysilane include phenyltrimethoxysilane, phenyltriethoxysilane, phenyltripropoxysilane, phenyltriisopropoxysilane, diphenyldimethoxysilane and diphenyldiethoxysilane. Examples of alkylalkoxysilane include tetramethoxysilane, tetraethoxysilane, trimethoxyethysilane, trimethoxymethylsilane, triethoxymethylsilane, ethyltriethoxysilane and ethyltriisopropoxysilane. The amount to be used of ingredients, the conditions of contact of the ingredients, and the like for the preparation of the solid composition in the present invention are not specifically limited unless they have adverse effects on the performance of the catalyst component formed therefrom, but diester of aromatic dicarboxylic acid is used normally in an amount of from 0.01 to 2g, preferably from 0.1 to 1g based on 1g of dialkoxymagnesium. The titanium halide is used normally in an amount more than 0.1g, preferably more than 1g based on 1g of dialkoxymagnesium. The aromatic hydrocarbon may be used in an arbitrary amount, preferably in such an amount as to form a suspension. Each of the ingredients used for the formation of the catalyst component of the present invention is brought into contact at a temperature ranging from generally 0°C to a boiling point of the titanium halide used for less than 100 hours, preferably for less than 10 hours. The contacting order and method of the starting materials used for formation of the catalyst component are not specifically limited, and any suitable manner may be used. The solid composition obtained after having been brought into contact may be further brought into contact one or more times with the titanium halide, and also may be washed with an organic solvent such as n-heptane. The solid composition thus obtained is subjected to a heat treatment The heat treatment may be carried out in the presence of an solvent in an amount of more than 0.1g based on 1g of the composition or in the absence of the solvent. The heat treatment may be conducted under a normal pressure or reduced pressure. The catalyst component thus obtained is combined with the silicon compound and an organoaluminum compound to form a catalyst for the polymerization of olefins. The organoaluminum compound is used in a molar ratio of from 1 to 1000 per atom of titanium in the catalyst component, and the silicon compound is used in a molar ratio of less than 1 preferably from 0.005 to 0.5 per mole of the organoaluminum compound. The polymerization of olefins may be performed in the presence of, or in the absence of an organic solvent, and olefin monomers may be used in the gaseous or liquid state. The polymerization temperature is below 200°C, preferably below 100°C, and the polymerisation pressure is below 98.1 bar (100kg/cm 2 ) gauge preferably below 49.1 bar (50 kg/cm 2 ) gauge. Examples of olefins homopolymerized or copolymerised by use of the catalyst prepared according to the method of the present invention include ethylene, propylene and 1-butene. Examples The following examples and comparative example illustrate the present invention more in detail. Example 1 (Preparation of Catalyst Component) To a 200mℓ round flask fitted with a stirrer and thoroughly purged with nitrogen are charged 10g of diethoxy magnesium and 80mℓ of toluene to form a suspension. Then 20mℓ of Ticℓ 4 is injected into the suspension, which is elevated at a temperature of 90°C, and 2,7mℓ of dibutylphthalate is further injected thereto followed by heating up to 115°C for reacting with agitation at that temperature for 2 hours. After the completion of the reaction, a reaction product is washed twice with 100mℓ of toluene at 90°C, and 80mℓ of fresh toluene and 20mℓ of TiCℓ 4 are added thereto for reacting with agitation at 115°C for two hours. After the completion of the reaction, the reaction product is washed 10 times with 200mℓ of n-heptane at 40°C and is dried under a reduced pressure to obtain a solid composition. The titanium content in the solid composition is measured to be 2.61% by weight Then, 3g of the solid composition is charged in a 200mℓ round flask fitted with a stirrer and thoroughly purged with nitrogen, and is subjected to a heat treatment at 100°C for 1 hour adding 30mℓ of n-heptane thereby to obtain a catalyst componenL (Polymerization) To a 2.0ℓ autoclave fitted with a stirrer, the air in which is thoroughly replaced with nitrogen, 700mℓ of n-heptane, 301mg of triethylaluminum and, 64mg of phenyltriethoxysilane are charged in an atmosphere of nitrogen. Thereafter, 120mℓ of hydrogen gas and 10.0mg of the catalyst component obtained as above are charged thereinto and the resultant mixture is heated to 70°C and subjected to polymerization under a pressure of 5.88 bar (6kg/cm 2. G) for 4 hours introducing thereinto propylene gas. After the completion of the polymerization reaction, solid polymer thus obtained is collected by filtration and dried by heating at 80°C under reduced pressure. On the other hand, the filtrate is thickened to obtain polymer soluble in a solvent used in polymerization. The amount of the polymer soluble in the solvent used in polymerization is represented by (A) and the amount of the solid polymer obtained as above is represented by (B). The solid polymer is subjected to extraction with boiling n-heptane for 6 hours to obtain polymer insoluble in boiling n-heptane, the amount of which is represented by (C). The polymerization activity (D) per unit weight of the catalyst component is represented by the formula (D) = [(A) + (B)] (g) amount of catalyst component (g) and the yeild (E) of crystalline polymer is represented by the formula (E) = (C) (B) x 100% Further, the overall yield (F) of crystalline polymer is represented by the formula (F) = (C) (A) + (B) x 100% The chlorine content, melt index and bulk density of the produced polymer are represented by (G), (H) and (I), respectively. Results thus obtained are shown in Table 1. Example 2 The procedures of Example 1 are repeated except that polymerization reaction is effected for 6 hours. Results thus obtained are shown in Table 1. Example 3 The procedures of Example 1 are repeated except that a heat treatment is effected at 80°C for 2 hours instead of at 100°C for 1 hour. In the polymerization, the procedures of Example 1 are repeated. Results thus obtained are shown in Table 1. Example 4 The procedures of Example 1 are repeated except that 30mℓ of o-dichlorobenzene is added to a solid composition which is subjected to a heat treatment at 90°C for 2 hours to prepare a catalyst componenL Results thus obtained are shown in Table 1. Example 5 The procedures of Example 1 are repeated except that the polymerization reaction is effected for 6 hours using the catalyst components obtained in Example 1. Results thus obtained are shown in Table 1. Example 6 The procedures of Example 1 are repeated except that a heat treatment is effected at 80°C for 3 hours instead of at 90°C for 2 hours as in Example 4 to prepare a catalyst component. Results thus obtained are shown in Table 1. Example 7 The procedures of Example 1 are repeated except that 30mℓ of toluene is added to a solid composition which is subjected to a heat treatment at 100°C for 1 hour to prepare a catalyst componenL Results thus obtained are shown in Table 1. Example 8 The procedures of Example 1 are repeated except that the polymerization reaction is effected for 6 hours using the catalyst component obtained in Example 1. Results thus obtained are shown in Table 1. Example 9 The procedures of Example 1 are repeated except that a heat treatment is effected at 80°C for 2 hours instead of at 100°C for 1 hour as in Example 7 to prepare a catalyst component. Results thus obtained are shown in Table 1. Example 10 The procedures of Example 1 are repeated except that the solid composition is subjected to a heat treatment at 100°C for 1 hour in the absence of a solvent to prepare a catalyst component. Results thus obtained are shown in Table 1. Example 11 The procedures of Example 1 are repeated except that the polymerization reaction is effected for 6 hours using the catalyst component obtained in Example 10. Results thus obtained are shown in Table 1. Example 12 The procedures of Example 1 are repeated except that a heat treatment is effected at 80°C for 3 hours instead of at 100°C for 1 hour as in Example 10 to prepare a catalyst component. Results thus obtained are shown in Table 1. Comparative Example The solid composition obtained in Example 1 is used as a catalyst component without being subjected to a heat treatment. In polymerization, the procedures of Example 1 are repeated. Results thus obtained are shown in Table 1. As explained hereinabove, the catalyst of the present invention is useful as a catalyst for the polymerization of olefins, such as, ethylene, propylene and 1-butene. In particular, the catalyst of the present invention exhibits a high catalytic activity and is capable of producing stereoregular polymers in a high yield, which is suitable for use for producing olefin polymers on an industrial scale.

Claims: A process for preparing a catalyst for use in the polymerisation of olefins which comprises A) the preparation of a catalyst component by contacting only (a) diethoxymagnesium, (b) dibutylphthalate as the only electron donor, (c) toluene and (d) titanium tetrachloride, to provide a solid catalyst component, subsequently washing the solid catalyst component with an organic solvent, drying it under reduced pressure, and subsequently subjecting the thus obtained solid catalyst component to a heat treatment at a temperature of at least 80°C for at least 5 minutes in the presence or absence of a solvent; and B) mixing said heat treated catalyst component with a silicon compound represented by a general formula SiR m (OR') 4-m , wherein R is hydrogen, alkyl group or aryl group, R' is alkyl group or aryl group, and m is represented as 0≤m≤4, and an organoaluminium compound. A process as defined in Claim 1, wherein the solvent is aliphatic hydrocarbon which is liquid at normal temperatures. A process as defined in Claim 2, wherein the aliphatic hydrocarbon has 5 to 15 carbon atoms. A process as defined in Claim 1, wherein the solvent is aromatic hydrocarbon which is liquid at normal temperatures. A process as defined in Claim 4, wherein the aromatic hydrocarbon has 6 to 10 carbon atoms. A process as defined in Claim 4 or 5, wherein the aromatic hydrocarbon is selected from the group consisting of toluene, o-xylene, m-xylene, p-xylene, benzene, ethylbenzene, propylbenzene and trimethylbenzene. A process as defined in Claim 1, wherein the solvent is halogenated hydrocarbon which is liquid at normal temperatures. A process as defined in Claim 7, wherein the halogenated hydrocarbon is halogenated aliphatic hydrocarbon having 5 to 15 carbon atoms. A process as defined in Claim 7, wherein the halogenated hydrocarbon is halogenated aromatic hydrocarbon having 6 to 10 carbon atoms. A process as defined in Claim 1, wherein the catalyst component is prepared by contacting the diethoxymagnesium, dibutylphthalate,toluene and titanium tetrachloride to obtain a solid composition, and then subjecting the solid composition to the heat treatment in the absence of a solvent. A process as defined in Claim 1, wherein the silicon compound is phenylalkoxysilane. A process as defined in Claim 11, wherein the phenylalkoxysilane is selected from the group consisting of phenyltrimethoxysilane, phenyltriethoxysilane, phenyltripropoxysilane, phenyttriisopropoxyslane, diphenyldimethoxysilane and diphenyldiethoxysilane. A process as defined in Claim 1, wherein the silicon compound is alkylalkoxysilane. A process as defined in Claim 13, wherein the alkylalkoxysilane is selected from the group consisting of tetramethoxysilane, tetraethoxysilane, trimethoxylethylsilane, trimethoxymethylsilane, triethoxymethylsilane, ethyltriethoxysilane and ethyltriisopropoxysilane. A process as defined in Claim 1, wherein the dibutylphtalate and titanium tetrachloride are used in amounts of 0.01 to 2g and 0.1 g or more based on diethoxymagnesium of 1g, respectively. A process as defined in Claim 1, wherein the diethoxymagnesium, dibutylphthalate and titanium tetrachloride are brought into contact at a temperature of ranging from 0°C to a boiling point of the titanium tetrachloride for less than 100 hours. A process as defined in Claim 1, wherein the solid composition obtained by contacting the diethoxymagnesium, dibutylphthalate and toluene is further brought into contact one or more times with the titanium halide. A process as defined in Claim 2 or 3, wherein the aliphatic hydrocarbon is present in an amount of more than 0.1g based on 1g of the solid composition obtained by contacting the diethoxymagnesium, dibutylphthalate, toluene and titanium tetrachloride. A process as defined in any one of Claims 4 to 6, wherein the aromatic hydrocarbon is present in an amount of more than 0.1 g based on 1g of the solid composition obtained by contacting the diethoxymagnesium, dibutylphthalate, toluene and titanium tetrachloride. A process as defined in any one of Claims 7 to 9, wherein the hydrocarbon halide is present in an amount of more than 0.1g based on 1g of the solid composition obtained by contacting the diethoxymagnesium, dibutylphthalate, toluene and titanium tetrachloride.

Inventors: KIMURA KOHEI, SOGA HIROKAZU, TERANO MINORU, KIMURA, KOHEI, SOGA, HIROKAZU, TERANO, MINORU
Applicants: TOHO TITANIUM CO LTD, TOHO TITANIUM CO. LTD.
Application year: 1987
Main classification: C08F10
IPC codes: C08F10, C08F4