COATED SUBSTRATES

Abstract: A consolidated web may be produced by impregnating it with a compound of latex of a polymer comprising from 10 to 45 weight percent of a C 3-6 alkenyl nitrile; from 36 to 85 weight percent of a C 4-6 conjugated diolefin; from 5 to 20 weight percent of a monomer mixture comprising from 100 to 60 percent of a C 8-12 vinyl aromatic monomer which may be unsubstituted or substituted by a C 1-4 alkenyl radical or a chlorine or bromine atom; from 0 to 40 weight percent of a C 1-2 alkyl ester of acrylic or methacrylic acid; from 0.5 to 10 weight percent of at least one, C 3-6 ethylenically unsaturated carboxylic acid; and from 0.1 to 5 weight percent of an N-C 1-4 alkylol derivative of an amide of a C 3-6 ethylenically unsaturated carboxylic acid; per 100 parts by dry weight of said polymer from 40-100 parts by weight of a filler, an effective amount of a gelling agent and optionally a cure paste.

Description: This invention relates to the manufacture of a consolidated web. More particularly the present invention relates to the manufacture of a consolidated web by impregnating a web with a heat sensitive latex and heating the impregnated web to gel the latex. The resulting webs are useful in a number of applications including the manufacture of synthetic leather and relatively strong sheet material. It is known to manufacture consolidated sheet material by impregnating a non woven web with a compound of a latex. The compound is gelled and then the consolidated web is dried and cured. Representative of such art are British Patent 1,502,827 published August 9, 1978 in the name of the B. F. Goodrich Company, Canadian Patent 668,788 issued August 20, 1963 to Farbenfabriken Bayer A.G. and United States Patent 4,143,198 issued March 6, 1979 to Bayer A.G. These patents are restricted to the impregnation of a fibrous web with a latex compound which contains a curing agent. The compound does not contain any filler. For the manufacture of impregnated webs these drawbacks are undesirable as they require the compounding of a vulcanizing agent and at best an extremely limited use of filler. Synthetic leather prepared with latices which are currently available suffer a decrease in abrasion resistance with increasing filler levels. The present invention seeks to overcome these limitations. The latices of the present invention are self curing and accept from 40 to 100, preferably from 50 to 70 parts by weight of a filler without a significant reduction in properties, even in the absence of cure paste. Accordingly, the present invention provides a latex characterised by 45 to 60 weight percent of a polymer comprising: - from 10 to 45 weight percent of a C 3-6 alkenyl nitrile; - from 36 to 85 weight percent of a C 4-6 conjugated diolefin; - from 5 to 20 weight percent of a monomer mixture comprising from 100 to 60 percent of a C 8-12 vinyl aromatic monomer which may be unsubstituted or substituted by a C 1-4 alkenyl radical or a chlorine or bromine atom; from 0 to 40 weight percent of a C 1-2 alkyl ester of acrylic or methacrylic acid; from 0.5 to 10 weight percent of at least one, C 3-6 ethylenically unsaturated carboxylic acid and from 0.1 to 5 weight percent of an N-C 1-4 alkylol derivative of an amide of a C 3-6 ethylenically unsaturated carboxylic acid; and a 0.2 to 0.3 mm thick film of matter consisting essentially of 60 parts by weight of a particulate mineral filler and 100 parts by weight of said polymer has a tensile strength of not less than 65 kg/cm². The present invention also provides a method for the manufacture of a consolidated sheet material characterised by impregnating a non woven fibrous web with from 30 to 150 weight percent of the web of compound of a latex of a synthetic polymer and gelling and curing the compound; said latex containing from 50 to 65 weight percent of a polymer of: - from 10 to 45 weight percent of a C 3-6 alkenyl nitrile; - from 36 to 85 weight percent of a C 4-6 conjugated diolefin; - from 5 to 20 weight percent of a monomer mixture comprising 100 to 60 percent of a C 8-12 vinyl aromatic monomer which may be unsubstituted or substituted by a C 1-4 alkyl radical or a bromine or chlorine atom; from 0 to 40 weight percent of a C 1-2 alkyl ester of acrylic or methacrylic acid; - from 0.5 to 10 weight percent of at least one C 3-6 ethylenically unsaturated carboxylic acid; and - from 0.1 to 5 weight percent of an N-C 1-4 alkylol derivative of an amide of a C 3-6 ethylenically unsaturated carboxylic acid; per 100 parts by dry weight of said polymer from 40 to 100 parts by weight of a particulate mineral filler, an effective amount of a gelling agent, and optionally a cure paste. The present invention also provides a consolidated sheet material prepared by the above process. The latices useful in accordance with the present invention are characterized as nitrile rubber latices. They are particularly useful where the consolidated substrate may be exposed to oil or chemicals. The nitrile polymers in accordance with the present invention preferably comprise from 10 to 45, preferably from 30 to 40, weight percent of a C 3-6 alkenyl nitrile; from 36 to 85, preferably from 40 to 55, weight percent of a C 4-6 conjugated diolefin; from 5 to 20, preferably from about 5 to 15, weight percent of a monomer mixture comprising from 100 to 60, preferably more than 80 percent and most preferably 100 percent, of a C 8-12 vinyl aromatic monomer which may be unsubstituted or substituted by a C 1-4 alkyl radical or a chlorine or bromine atom, and the balance a C 1-2 alkyl ester of acrylic or methacrylic acid; from 0.5 to 10, preferably from 2 to 6, weight percent of a C 3-6 ethylenically unsaturated carboxylic acid; and from 0.1 to 5, preferably from 0.5 to 2, weight percent of an N-C 1-4 alkylol derivative of an amide of a C 3-6 ethylenically unsaturated carboxylic acid. Some C 3-6 alkenyl nitriles are acrylonitrile and methacrylonitrile. Some C 4-6 conjugated diolefins are acyclic diolefins e.g. butadiene and isoprene. Some C 8-12 vinyl aromatic monomers are styrene which may be substituted by methyl, ethyl, propyl, and butyl radicals, e.g. alpha methyl styrene. The styrene monomer may optionally be substituted by a bromine or chlorine atom. When present, the acrylate monomers may be selected from methyl acrylate, methyl methacrylate, ethyl acrylate and ethyl methacrylate. Carboxylic acid monomers which may be used in accordance with the present invention are e.g. acrylic acid, methacrylic acid, maleic acid and itaconic acid. The most commonly available N-alkylol derivatives of an amide of a C 3-6 ethylenically unsaturated carboxylic acid which may be used in accordance with the present invention are N-methylol acrylamide and N-ethylol acrylamide. Processes for preparing latices of these polymers are well known in the art. A batch polymerization process is disclosed in U.S. Patent 3,344,103 issued September 26, 1967 to B. F. Goodrich. A semi continuous process for preparing such latices is disclosed in Chemical Abstracts CA 96:124630g and CA 98:162209g. These are abstracts of East German Patents 151,456 and 157,193 published October 21, 1981 and October 20, 1982 in the name of VEB Chemische Werke Buna. As the latex is to be gelled the emulsifier should be capable of being gelled under the condition of use. Long chain fatty acid soaps are suitable with amine-divalent metal oxide type gelling systems, e.g. ammonium acetate zinc oxide. Sulphonate surfactants are particularly useful with silicone polyether gelling agents. Some sulphonate surfactants and silicone ethers are disclosed in U.S. Patent 3,702,315 issued November 7, 1972 to B. F. Goodrich. Other types of sulphonate surfactant e.g. C 10-20 alkyl sulfonates are also suitable. Generally the emulsifier level should be less than 2 percent. The monomeric ingredients are polymerized to provide a latex with a polymeric solids content from 40 to 55 percent by weight. Through conventional procedures e.g. agglomeration and concentration the solids level may be raised up to 65 percent by weight. The latex is then compounded. The filler is added in an amount from 40 to 100, preferably 50 to 70 parts by weight per 100 parts by weight of polymer in the latex. The filler should be added to the latex in accordance with good compounding procedure. When the filler is added as a slurry or suspension a surfactant compatible with the surfactant in the latex should be used. Preferably the surfactant should be of a type and used amount not to interfere with the gelling systems. Due to cost considerations the filler is generally a particulate inorganic material. Some fillers are calcium carbonate, clay, silicates, and other mineral fillers typically used with latex compounds. These types of systems are preferred as they reduce the tendency of stratification in the web due to premature gellation and to binder migration either to the surface or interior of the web. Heat sensitive gelling agents cause gelling of the latex over a relatively narrow temperature range. It is desirable to use low temperature gelling agents which will cause gellation under relatively mild conditions at temperatures from 40 to 80°C, preferably from 45 to 60°C. There are a number of different heat sensitive gel systems known in the art. The amine-divalent metal oxide gel systems, e.g. amine or ammonium ion releasing compound and zinc oxide. Typically these gelling agents cause gelling in the range of from 25 to 40°C. Usually the amine generating agent should be used to provide ammonia in an amount from 0.1 to 4, preferably 0.3 to 2 parts by weight per 100 parts by weight of polymer in the latex. The divalent metal should be present in a minimum effective amount generally from 0.5 to 20, preferably 2 to 10 parts by weight per 100 parts of polymer. These systems require that the compound have a pH from 10 to 11. Chemicals to broaden the tolerance of the compound to the amine metal oxide system may be added to the compound. Typically these are compounds ammonium or amine sulphamates or ammonium or amine sulphates. These compounds are typically used in amounts up to 30, preferably less than 6 parts by weight per 100 parts by weight of polymer in the latex. A preferred class of heat sensitive gelling agents are the organic siloxane compounds. Some such compounds have the formula [R′ (OC n H 2n ) x OOCNH-A-CH₂CH₂] a (R) b SiO wherein R is an organic radical; R′ is a C 1-7 alkyl radical or an aryl radical; A is a divalent hydrocarbon containing up to 7 hydrocarbons; a is from 0.05 to 1.00 inclusive; b is from 1.12 to 2.25 inclusive; and a+b is from 2.02 to 2.40; n is from 2 to 4 and x is at least 5. A particularly useful starting siloxane has the formula (R₃)SiO [(R)₂SiO]p[(R) (H)SiO]q Si(R)₃ wherein R is as previously defined; p has an average value from 0 to 45, q has a value from 1 to 48 and the sum of p+q is equal to from 3 to 48 and the sum of the silicon bonded R groups and silicon bonded hydrogen is from 2.04 to 2.40 per silicon atom. Preferably R is methyl. These agents are described in above noted U.S. Patent 3,702,315 and in U.S. Patent 3,483,240 issued December 9, 1969 to the General Electric Company. The organo siloxane in an amount from 0.01 to 1.0 preferably from 0.01 to 0.5 parts by weight per 100 parts by weight of polymer. These siloxane compounds will cause the latex compound to gel at a temperature from 45 to 55°C. These compounds are particularly useful with the sulphonate surfactants. Particularly useful are the alkane surfactants containing from 10 to 20 carbon atoms, preferably from 10 to 14 carbon atoms. The gelling system may also comprise an amine or ammonium ion releasing agent in conjunction with a non ionic surfactant. Such non ionic surfactants are the reaction of a long chain fatty alcohol having from 15 to 20 carbonations with the condensation product of a lower alkylene oxide having from 20 to 40, preferably from 20 to 30, alkylene oxide units. Preferably the alkylene oxide is ethylene oxide. The amine compound and the surfactant added to the latex in a total amount of 5 to 10 parts by weight per 100 parts by weight of polymer in the latex. The ratio of amine releasing compound to non ionic surfactant may be 1:1 to 1:3. Some amine release compounds are ammonium salts e.g. ammonium chloride; organic amines, amine sulphates and amine sulphamates. Many non ionic compounds which are the adduct of a long chain fatty alcohol and the condensation product of a lower alkylene oxide are commercially available. Such products may be Lutensol AT 25 (Trademark of BASF). The gelling agent may also be a compound which has a lower solubility in the latex compound at an elevated temperature than at lower temperatures, e.g. polyethers as described in High Polymer Latices by D. C. Blackley, Maclaren and Sons, London, 1966 at Vol. 1 pages 43 and 44. The polyethers are generally used in an amount from 0.5 to 5 percent by weight based on the weight of the polymer. Polymers of lower alkylene glycols may also be used as a heat sensitive gelling agent. These compounds may be homopolymers or copolymers of C 2-3 alkylene glycols. Preferably the polymers are functional derivatives of such polyglycols e.g. those sold by BASF under the trade mark BASENSOL. These poly alkylene glycols are typically used in an amount from 3 to 6 percent by weight based on the weight of the polymer. The latex compound does not need to contain a vulcanization paste. The latices of the present invention are self curing, when heated to from 120 to 180°C, typically 150°C, for from 5 to 20 minutes, typically 10 minutes. The latex compound may contain other usual ingredients e.g. antioxidants and pigments in amounts generally used in the industry. The web may be web of synthetic or natural fibre or a mixture of both. Generally blends of synthetic fibers polyester, polyamide, or polyolefin with cellulosic fibers either natural or regenerated may be used. The web may be non woven and may have a weight up to 2000 grams per square meter. Generally, the webs have a weight from 800 to 1500 grams per square meter. To obtain the required density, these webs are usually needled and shrunk. Typically the web passes through a bath to saturate it. The pick up of the web may be from 30 to 150 typically from 50 to 120 weight percent preferably from 70 to 100 weight percent, based on the dry weight of the web. The impregnated web is then heated, to the gel temperature, typically by infra red heaters. The gelled web then passes through a dryer or oven at a temperature of from 120 to 180°C for a period of time sufficient to dry and cure the web. Generally the time is from 5 to 20 minutes depending on the air flow in the oven and the base weight of the web. The consolidated web may then be treated in the usual manner. The following examples are intended to illustrate the invention and are not intended to limit it. In the examples parts refers to parts by dry weights unless otherwise specified. The latex was prepared from a total monomer composition consisting of 50 parts of butadiene; 9 parts of styrene; 35 parts of acrylonitrile; 5 parts of a C 3-6 ethylenically unsaturated acid and 1 part of N-methylol acrylamide by a semi continuous method. A film of the latex per se and latex plus 60 parts filler per 100 parts polymer was cast and dried at 70°C for 2 hours and then cured at 130°C for 15 minutes. Films of POLYSAR (Trademark) PL5372 and PL5361 (Trademark) latex used for web impregnation per se, contaning 8.5 parts by weight of a sulphur cure paste per 100 parts of polymer, and containing 8.5 parts of a sulphur cure paste and 60 parts of the same filler, per 100 parts of polymer were also cast and dried and cured under the same conditions. POLYSAR Latex 5372 is competitive with latices sold for web impregnation or saturation in the manufacture of synthetic leather. Competitive latices are PERBUNAN (Trademark) N3415M and PERBUNAN N Latex T. The tensile strength of the film at various degrees of elongation was then measured in kg/cm². The tensile and the percent elongation at break was also recorded. The results are set forth in Table I. These results show that the latices of the present invention are self curing, and give comparable tensile strengths in the absence of a cure paste with the latices currently used. The elimination of the need for a cure paste is an advantage to the user of the latex as it does away with compounding reducing the cost of equipment and labour associated with compounding. The latex of the present invention and comparative latex PL 5372 were compounded as indicated and a mixed polyester, polyamide, rayon (40/40/20 by weight) web having a dry weight of 1000 g per square meter was impregnated with the compound. The impregnated web was then gelled, dried, cured and split to 1 mm thickness and the strength and elongation of the web at break was recorded. The results are set forth in Table II. This test shows that the web of the present invention, containing 100 parts of filler per 100 of polymer is comparable to the webs of the prior art with no filler. As soon as filler is added to or the cure paste omitted from the compounds of the prior art the strength of the web deteriorates by 30%. To test abrasion resistance the comparative latex was compounded with 8.5 parts of a cure paste and with 60 parts of filler per 100 parts of polymer. Two different samples of the latex of the invention were compounded in a similar manner with and without filler, in the presence and absence of cure paste. Webs were impregnated with these compounds and the web was then tested for abrasion resistance using the Veslic Test (Swiss association of Leather Industry Chemists) in which higher numbers give a poorer result. Additionally samples of web from Trial V and Trial VIII in Table II were also tested using the Veslic Test. In the test a sample of synthetic leather is placed on the apparatus. A 500 gm weight is placed on a plastic foot having a pedestal extending to the surface of the synthetic leather. The pedestal has a base 15 mm long by 3 mm wide. The foot is rubbed over the leather in the longitudinal direction of the pedestal for 5, 10, 20 and 40 cycles. The results for 40 cycles are reported in Table III. The synthetic leather samples were subjectively compared for the relative extent of abrasion, 5 being the worst and 1 being the best. The results are set forth in Table III below. In industrial applications PL 5372 is always used in conjunction with a cure paste. In the present application, numerical values include their precise values and their "about" values, e.g. "45" includes the precise value "45" and "about 45". The present application includes any embodiment of the present invention, e.g. as indicated above and below, for instance the embodiments: A consolidated web may be produced by impregnating it with a compound of latex of a polymer comprising from 10 to 45 weight percent of a C 3-6 alkenyl nitrile; from 36 to 85 weight percent of a C 4-6 conjugated diolefin; from 5 to 20 weight percent of a monomer mixture comprising from 100 to 60 percent of a C 8-12 vinyl aromatic monomer which may be unsubstituted or substituted by a C 1-4 alkenyl radical or a chlorine or bromine atom; from 0 to 40 weight percent of a C 1-2 alkyl ester of acrylic or methacrylic acid; from 0.5 to 10 weight percent of at least one, C 3-6 ethylenically unsaturated carboxylic acid; and from 0.1 to 5 weight percent of an N-C 1-4 alkylol derivative of an amide of a C 3-6 ethylenically unsaturated carboxylic acid; from 40-100 parts by weight of a filler, an effective amount of a gelling agent and optionally a cure paste.

Claims: 1. A latex characterised by 45 to 60 weight percent of a polymer comprising: - from 10 to 45 weight percent of a C3-6 alkenyl nitrile; - from 36 to 85 weight percent of a C4-6 conjugated diolefin; - from 5 to 20 weight percent of a monomer mixture comprising 100 to 60 percent of a C8-12 vinyl aromatic monomer which may be unsubstituted or substituted by a C1-4 alkenyl radical or a chlorine or bromine atom; from 0 to 40 weight percent of a C1-2 alkyl ester of acrylic or methacrylic acid; from 0.5 to 10 weight percent of at least one, C3-6 ethylenically unsaturated carboxylic acid and from 0.1 to 5 weight percent of an N-C1-4 alkylol derivative of an amide of a C3-6 ethylenically unsaturated carboxylic acid; and a 0.2 to 0.3 mm thick film of matter consisting essentially of 60 parts by weight of a particulate mineral filler and 100 parts by weight of said polymer has a tensile strength of not less than 65 kg/cm². 2. A latex as claimed in claim 1, characterised by said polymer comprises: - from 30 to 40 weight percent of a C3-6 alkenyl nitrile; - from 40 to 55 weight percent of a C4-6 conjugated diolefin; - from 5 to 15 weight percent of a C8-12 vinyl aromatic monomer which may be unsubstituted or substituted by a C1-4 alkyl radical or a chlorine or bromine atom; - from 2 to 6 weight percent of at least one C3-6 ethylenically unsaturated carboxylic acid; and - from 0.5 to 2 weight percent of an N-C1-4 alkylol derivative of acrylamide or meth acrylamide. 3. A latex as claimed in claim 2, characterised by said alkenyl nitrile is selected from acrylonitrile and and methacrylonitrile; said C4-6 conjugated diolefin is selected from butadiene and isoprene; said vinyl aromatic monomer is styrene; said C3-6 ethylenically unsaturated carboxylic acid is selected from acrylic acid, methacrylic acid and itaconic acid and said amide is selected from N-methylol acrylamide and N-methylol methacrylamide. 4. In the method for the manufacture of a consolidated sheet material comprising impregnating a non woven fibrous web with from 30 to 150 weight percent of the web of compound of a latex of a synthetic polymer and gelling and curing the compound, characterized by the compound comprises a latex containing from 50 to 65 weight percent of a polymer of: - from 10 to 45 weight percent of a C3-6 alkenyl nitrile; - from 36 to 85 weight percent of a C4-6 conjugated diolefin; - from 5 to 20 weight percent of a monomer mixture comprising 100 to 60 percent of a C8-12 vinyl aromatic monomer which may be unsubstituted or substituted by a C1-4 alkyl radical or a bromine or chlorine atom; and from 0 to 40 weight percent of a C1-2 alkyl ester of acrylic or methacrylic acid; - from 0.5 to 10 weight percent of at least one C3-6 ethylenically unsaturated carboxylic acid; and - from 0.1 to 5 weight percent of an N-C1-4 alkylol derivative of an amide of a C3-6 ethylenically unsaturated carboxylic acid; per 100 parts by dry weight of said polymer from 40 to 100 parts by weight of a particulate mineral filler, an effective amount of a gelling agent and optionally a cure paste. 5. A method as claimed in claim 4, characterised by the polymer comprises: - from 30 to 40 weight percent of a C3-6 alkenyl nitrile; - from 40 to 55 weight percent of C4-6 conjugated diolefin; - from 5 to 15 weight percent of a C 8-12 vinyl aromatic monomer which may be unsubstituted or substituted by a C1-4 radical or a chlorine or bromine atom; - from 2 to 6 weight percent of at least one C3-6 ethylenically unsaturated carboxylic acid; and - from 0.5 to 2 weight percent of an N-C1-4 alkylol derivative of acrylamide or meth acrylamide. 6. A process as claimed in claim 5, characterised by said paste is absent and said particulate mineral filler is present in an amount from 50 to 70 parts by weight per 100 parts by weight of said polymer. 7. A process as claimed in claim 6, characterised by - said alkenyl nitrile is selected from acrylonitrile and methacrylonitrile; - said C4-6 conjugated diolefin is selected from butadiene and isoprene - said vinyl aromatic monomer is styrene - said C3-6 ethylenically unsaturated carboxylic acid is selected from acrylic acid, methacrylic acid, and itaconic acid; and - said amide is selected from N-methylol acrylamide and N-methylol meth acrylamide. 8. A method as claimed in claim 7, characterised by said agent is prepared from a silicone ether of the formula (R₃)SiO[(R)₂SiO]p[(R)(H)SiO]q Si(R)₃ and is present in an amount from 0.05 to 2 parts by weight per 100 parts by weight of polymer. 9. A method as claimed in claim 7, characterised by said agent is present in an amount from 5 to 10 parts by weight per 100 parts by weight of polymer and comprises a mixture of an amine or ammonium generating compound and an emulsifier which is an adduct of a C15-20 saturated alcohol and the condensation product of 20-30 moles of ethylene oxide in a weight ratio of from 1:1 to 1:3. 10. A consolidated sheet material prepared according to a method as claimed in any one of claims 4 to 9.

Inventors: CLAASSEN, PETER JOSEPH MARIA WILHELMUS, DE BEER, LEX
Applicants: BASF AKTIENGESELLSCHAFT
Application year: 1987
Main classification: D04H1
IPC codes: C08L33, B32B27, C08F236, C08L9, C08J5, C08L7, C08L21, D04H1, C08K3, C08L47