LACTONE MODIFIED, ESTERIFIED OR AMINATED ADDITIVES USEFUL IN OLEAGINOUS COMPOSITIONS

Abstract: C₅-C₉ lactone derived materials are made by simultaneously reacting (a) a C₅-C₉ lactone with (b) a polyamine, a polyol or an amino alcohol and (c) a hydrocarbyl substituted C₄-C₁₀ monounsaturated dicarboxylic acid producing material, e.g., a poly­ isobutenyl succinimide, which preferably was made by reacting a polymer of a C₂ to C₁₀ monoolefin, preferably polyisobutylene, having a molecular weight of about 300 to 10,000 with a C₄ to C₁₀ mono­ unsaturated acid, anhydride or ester, preferably maleic anhydride, such that there are 0.7 to 2.0 di­ carboxylic acid producing moieties per molecule of said olefin polymer used in the reaction mixture. The resulting lactone derived materials, which may be post-treated, for example, with a boron compound, are useful, per se, as oil soluble dispersant additives, and are useful in fuel and lubricating oil compositions including concentrates containing the additives.

Description: This invention relates to oil soluble dispersant additives useful in fuel and lubricating oil compositions, including concentrates containing said additives, and methods for their manufacture and use. The dispersant additives are poly (C₅-C₉ lactone) adducts which have been prepared by simultaneously reacting a (1) C₅-C₉ lactone with (2) a polyamine, a polyol or an amino alcohol and (3) and with a dicarboxylic acid material which has been substituted with a high molecular weight hydrocarbon group. The high molecular weight hydrocarbon group has a number average molecular weight (M n ) of about 300 to about 10,000. The additives will have a ratio (functionally) of about .70 to about 2.0 dicarboxylic acid producing moieties for each equivalent weight of the high molecular weight hydrocarbon therein. Polyalkylene substituted C₄-C₁₀ dicarboxylic acid and anhydride adducts with polyols and polyamines are well known lubricating additives. These agents act to keep sludge and varnish dispersed in engine oils and have been very successful commercially. It is also known that polymers of 6 to 10 membered lactones such as valerolactone or epsiloncaprolactone (hereinafter caprolactone or E-caprolactone), can be prepared by reacting the lactone monomer with a hydroxyl or amine initiator. When reacting E-caprolactone, for example, the polymerization reaction may be illustrated by the following equations: The reactions are known to be catalyzed by various esterification catalysts such as stannous octanoate, and a variety of different molecular weight products are feasible depending upon the ratio of lactone to initiator. Molecular weights on the order of from a few hundred up to about 5,000 are reproducably achievable. Caprolactone can also be polymerized to a very high molecular weight, e.g., on the order of 100,000 or more. Thypically such high molecular weight polymers do not employ initiators and preservation of functionality is not a requirement. It is also known to react a lactone such as E-caprolactone with a polyol to form polyesters having terminal hydroxyl groups which are useful as plasticizers. It has now been found that improved oil soluble dispersant additives, useful in fuel and lubricating oil compositions, including concentrates containing the additives, can be prepared by first reacting a 6 to 10 membered lactone with either a polyamine, a polyol or an amino alcohol to form an intermediate adduct, and then reacting the intermediate adduct with a known class of oil soluble dispersants, namely: dicarboxylic acids, anhydrides, esters, etc. that have been substituted with a high molecular weiight hydrocarbon group. A typical example of one such known oil soluble dispersant is a polyalkylene succinic anhydride, wherein the polyalkylene moiety has a number average molecular weight of about 300 to about 10,000 and wherein the ratio (functionality) of succinic acid producing moieties to each equivalent weight of the polyalkylene moiety is from about 0.70 to about 2.0. While there are a number of prior art disclosures relating to adducts of lactones and polyols and/or amino alcohols, to polyalkenyl succinic acid or anhydride type dispersants, and to lactone polymerization reactions, in general, little or no prior art of direct pertinence appears to have surfaced in regard to the present dispersants. Exemplary of the patent literature which relates to lactone polymerization processes and/or to oil soluble dispersant additives are following U.S. Patents: U.S. 4,362,635 discloses synthetic ester oils which are esterification products of monoalcohols and dicarboxylic acids or of polyhydric alcohols and monocarboxylic acids respectively, containing 5 to 45% by weight of units of hydroxycarboxylic acids obtained from aliphatic alcohols, aliphatic, cycloaliphatic or aromatic carboxylic acids, and lactones of aliphatic C₅-C₁₂ hydrocarobxylic acids. The synthetic ester oils are suitable for the preparation of lubricants and lubricant compositions. U.S. Patent 4,234,435 discloses as oil additives, polyalkylene substituted dicarboxylic acids derived from polyalkylenes having a M n of 1,300 to 5,000 and containing at least 1.3 dicarboxylic acid groups per polyalkylene. In Example 34 of this patent, a polyisobutene-substituted succinic acylating agent is reacted with caprolactone in the presence of mineral oil and sodium hydroxide. U.S. Patent 4,532,058 discloses as a motor oil dispersant, a spirodilactone condensation product formed by heating alkenyl succinic anhydrides in the presence of a basic catalyst, and then heating the resulting bicyclic spirodilactone condensation product with a polyamine or polyamine alcohol. It should be emphasized that this patent describes the intermolecular decarboxylation of an alkenyl succinic anhydride at elevated temperatures to form a condensation product and carbon dioxide as a by-product. This prior art is not concerned with polymerizable lactones which are the subject of the instant invention. SUMMARY OF THE INVENTION Despite the efficacy of prior art dispersant and oleaginous compositions, there is a need for more efficient and less costly dispersants which can either perform better, or perform well at lower dispersant levels. Accordingly, it is a principal object of this invention to provide novel lactone adduct based dispersants which are effective, and readily prepared under typical dispersant manufacturing conditions. Another object is to provide a novel class of poly (C₅-C₉ lactone) adduct dispersants. Another object is to provide a process for preparing efficient dispersants by simultaneously reacting a hydrocarbyl substituted dicarboxylic acid, anhydride, etc. with a C₅-C₉ lactone and with a polyamine, a polyol, an amino alcohol or a mixture thereof. A further object is to provide lubricant compositions and concentrates containing the novel C₅-C₉ lactone based dispersants of this invention. Yet another object is to provide a novel class of oil soluble dispersants from polyalkylene substituted acylating agents which have at least one group in their structure which is reactive with C₅-C₉ lactone and/or a polyamine, a polyol, an amino alcohol, or a mixture thereof. Still another object is to provide metal complexes and other post-treatment derivatives, e.g. borated derivatives, of the novel C₅-C₉ lactone based dispersants of this invention. Still another object is to provide metal complexes and other post-treated derivatives, e.g., borated derivatives, of the novel poly (C₅-C₉) lactone adduct dispersants of this invention, as well as lubricant compositions and concentrates containing such post-treated derivatives. The manner in which these and other objects can be achieved will be apparent from the detailed description of the invention which appears hereinbelow. In one aspect of this invention, one or more of the above objects can be achieved by simultaneously reacting a C₅-C₉ lactone with a polyamine and with a polyolefin substituted dicarboxylic acylating agent, wherein the polyolefin has a number average molecular weight of about 300 to about 10,000, and wherein the acylating agent contains from about 0.70 to about 2.0 dicarboxylic acid producing moieties, preferably acid anhydride moieties, per equivalent weight of polyolefin. In another aspect, one or more of the objects of this invention can be achieved by heating a C₅-C₉ lactone such as E-caprolactone at a temperature of at least about 30°C, and preferably from about 75°C to about 180°C with a mixture of a polyamine and a polyalkylene succinic acid or anhydride wherein the polyalkylene is characterized by a number average molecular weight of about 300-10,000, and wherein the polyalkylene succinic acid or anhydride is characterized by the presence within its structure of from about 0.7 to about 2.0 succinic acid or succinic acid derivative moieties for each equivalent weight of polyalkylene; and, in a further aspect, one or more objects of this invention are achieved by providing the C₅-C₉ lactone reaction products produced by such a process. One or more objects of this invention can be illustrated in connection with the simultaneous reaction between a C₅-C₉ lactone such as E-caprolactone, a polyamine such as tetraethylene pentamine (TEPA) and a polyisobutenyl succinimide-amide dispersant. Still other objects can be illustrated in connection with the simultaneous reaction between E-caprolactone, a polyol such as pentaerythritol,and a PIBSA to form a PIBSA-polyol-caprolactone dispersant. Still other objects can be illsutrated in connection with the simultaneous reaction between E-caprolactone, an amino alcohol such as 2-amino-2-(hydroxymethyl)-1,3-propanediol (THAM) and a PIBSA to form a PIBSA-bis ester oxazoline dispersant. The novel products of this invention are useful per se as an additive, e.g., a dispersant additive, for example, in the same manner as disclosed in U.S. Patent 3,219,666 where prior art derivatives of polyalkenyl succinic acids and nitrogen compounds are used as dispersant/detergents in lubricants, especially lubricants intended for use in the crankcase of internal combustion engines, gears, and power transmitting units. Accordingly, one or more objects of this invention are achieved by providing lubricating oil compositions, e.g., automatic transmission fluids, heeavy duty oils suitable for use in the crankcases of gasoline and diesel engines, etc. containing the novel C₅-C₉ lactone based products of this invention. Such lubricating oil compositions may contain additional additives such as viscosity index improves, antioxidants, corrosion inhibitors, detergents, pour depressants, antiwear agents, etc. Still further objects are achieved by providing concentrate compositions comprising from about 20 to about 80 weight % of a normally liquid, substantially inert, organic solvent/diluent, e.g., mineral lubricating oil, or other suitable solvent/diluent and from about 20° to about 80 weight % of a C₅-C₉ lactone based dispersant, as mentioned above and described in more detail hereinafter. DESCRIPTION OF THE PREFERRED EMBODIMENTS THE LACTONE MATERIAL Lactone compound which may be used to prepare the dispersants of this invention include polymerizable lactones having at least five carbon atoms in the lactone ring, e.g., 5 to 9 carbon atoms. The lactone may be substituted or unsubstituted and the substitutents, if any may comprise, for example, alkyl, aryl, aralkyl, cycloalkyl, alkoxy or other groups which would not interfere with the ring opening reaction and adduct formation. The preferred lactones have no more than two substituent groups, and the more preferred lactones are unsubstituted. Non-limiting examples of the useful lactones include delta-valerolactone, methyl-delta-valero-lactone, E-caprolactone, methyl-E-caprolactone, dimethyl-E-caprolactone, methoxy-E-caprolactone, cyclohexyl-E-caprolactone, methylbenzyl-E- caprolactone, caprylolactone, methyl-caprylolactone, and the like, with E-caprolactone being particularly preferred. THE POLYAMINE MATERIAL Useful amine compounds for reaction with the lactone material and with the hydrocarbyl substituted dicarboxylic acid material include polyamines of about 2 to 60, e.g. 3 to 20, most preferably 3 to 10, total carbon atoms in the molecule. These amines may be hydrocarbyl amines or may be hydrocarbyl amines including other noninterfering groups, e.g., alkoxy groups, amide groups, nitrile groups, imidazoline groups, and the like. Preferred amines are aliphatic saturated amines, including those of the general formula: wherein R and R′ are independently selected from the group consisting of hydrogen: C₁ to C₂₅ straight or branched chain alkyl radicals, C₁ to C₁₂ alkoxy C₂ to C₆ alkylene radicals, and C₁ to C₁₂ alkylamino C₂ to C⁶ alkylene radicals, each s is the same or a different number of from 2 to 6, preferably 2 to 4; and t is a number of from 0 to 10, preferable 2 to 7. If t=0, then at least one of R or R′ must be H such that there are at least two of either primary or secondary amino groups. Non-limiting examples of suitable amine compounds include: 1,2-diaminoethane, 1,3-diaminopropane, 1,4-diaminobutane, 1,6-diaminohexane, polyethylene amines such as diethylene triamine, triethylene tetramine, tetraethylene pentamine, polypropylene amines such as 1,2-propylene diamine, di-(1,2 propylene) triamine, di-(1,3-propylene)triamine, N,N-dimethyl-1-1,3-diaminopropane, N,N-di-(2-aminoethyl)ethylene diamine, N-dodecyl-1-1,3-propane diamine, di-,and tri-tallow amines, amino morpholines such as N-(3-aminopropyl morpholine, etc. Other useful amine compounds include: alicylic diamines such as 1,4-di(aminomethyl) cyclohexane, and heterocyclic compounds such as imidazolines, morpholines and N-aminolakyl piperazines of the general formula: wherein G is independently selected from the group consisting of hydrogen and omega (non-tertiary)aminoalkylene radicals of from 1 to 3 carbon atoms, and p is a number of from 1 to 4. Non-limiting examples of such amines include 2-pentadecyl imidazoline, N-(2-aminoethyl) piperazine, etc. Commercial mixtures of amine compounds advantageously may be used. For example, one process for preparing alkylene amines involves the reaction of an alkylene dihalide (such as ethylene dichloride or propylene dichloride) with ammonia, which results in a complex mixture of alkylene amines wherein pairs of nitrogens are joined by alkylene groups, forming such compounds as diethylene triamine, triethylenetetramine, tetraethylene pentamine and isomeric piperazines. A low cost mixture of poly(ethyleneamine) compounds averging about 5 to 7 nitrogen atoms per molecule are available commercially under trade names as "Polyamine H", "Polyamine 400", "Dow Polyamine E-100", etc. Useful amines also include polyoxalkylene polyamines such as those of the formulas: where m has a value of about 3 to 70 and preferably 10 to 35; and where n has a value of about 1 to 40 with the provision that the sum of all the n's is from about 3 to about 70 and preferably from about 6 to 35, R is a substituted saturated hydrocarbon radical of up to 10 carbon atoms, wherein the number of substituents on the R group is represented by the value of "a", which is a number from 3 to 6. The alkylene groups in either formula III or IV may be straight or branched chain containing about 2 to 7, and preferably about 2 to 4 carbon atoms. The above polyoxyalkylene polyamines, preferably polyoxyalkylene diamines and polyoxyalkylene triamines, may have average molecular weights ranging from about 200 to about 4,000 and preferably from about 400 to about 2,000. The preferred polyoxyalkylene polyamines include the polyoxyethylene and polyoxypropylene diamines and the polyoxypropylene triamines having average molecular weight ranging from about 200 to 2,000. The polyoxyalkylene polyamines are commercially available and may be obtained, for example, from the Jefferson Chemical Company, Inc. under the trace name "Jeffamines D-230, D-400, D-1000, D-2000, T-403", etc. The polyamine is readily reacted with the lactone, with or without a catalyst, simply by heating a mixture of the lactone and polyamine in a reaction vessel in the absence of a solvent at a temperature of about 30°C to about 200°C, more preferably to a temperature of about 75°C to about 180°C, and most preferably at about 90°C to about 160°C, for a sufficient period of time to effect reaction. Optionally, a solvent for the lactone, polyamine and/or adduct can be employed to control viscosity and or reaction rates. In one preferred embodiment of the invention, a polyamine such as tetraethylene pentamine is employed in a ratio of about 10:1 to 0.1:1 based on the amount of lactone used in the reaction. However, it will be appreciated that the mole ratio of lactone to polyamine can be varied widely as a means for controlling the length of the sequence of lactone units in the adduct. In this latter regard, the mole ratio of lactone to polyamine may vary from about 10:1 to about 0.1:1, more preferably from about 4:1 to about 0.2:1, and most preferably from about 2:1 to about 0.4:1. Catalysts useful in the promotion of the lactone-polyamine reactions are selected from the group consisting of stannous octanoate, stannous hexanoate, stannous oxalate, tetrabutyl titanate, a variety of metal organic based catalyst acid catalysts and amine catalysts, as described on page 266, and forward in a book chapter authorized by R.D. Lundberg and E. F. Cox entitled, "Kinetics and Mechanisms of Polymerization: Ring Opening Polymerization", edited by Frisch and Reegen, published by Marcel Dekker in 1969, wherein stannous octanoate is an especially preferred catalyst. The catalyst is added to the reaction mixture at a concentration level of about 50 to about 10,000 parts of catalyst per one million parts by weight of the total reaction mixture. THE POLYOL MATERIAL Suitable polyol compounds which can be used to react with the C₅-C₉ lactone and with the hydrocarbyl substituted dicarboxylic acid material include aliphatic polyhydric alcohols containing up to about 100 carbon atoms and about 2 to about 10 hydroxyl groups. These alcohols can be quite diverse in structure and chemical composition, for example, they can be substituted or unsubstituted, hindered or unhindered, branched chain or straight chain, etc. as desired. Typical alcohols are alkylene glycols such as ethylene glycol, propylene glycol, trimethylene glycol, butylene glycol, and polyglycol such as diethylene glycol, triethylene glycol, tetraethylene glycol, dipropylene glycol, tripropylene glycol, dibutylene glycol, tributylene glycol, and other alkylene glycols and polyalkylene glycols in which the alkylene radical contains from two to about eight carbon atoms. Other useful polyhydric alcohols inlcude glycerol, monomethyl ether of glycerol, pentaerythritol, dipentaerythritol,tripentaerythritol, 9,10-dihydroxystearic acid, the ethyl ester of 9,10-dihydroxystearic acid, 3-chloro-1, 2-propanediol, 1,2 butanediol, 1,4-butanediol, 2,3-hexanediol, 2,3-hexanediol, pinacol, tetrahydroxy pentane, erythritol, arabitol, sorbitol, mannitol, 1,2-cyclohexanediol, 1,4-cyclohexanediol, 1,4-(2-hydroxyethyl)-cyclohexane, 1,4-dihydroxy-2-nitrobutane, 1,4-di(2-hydroxyethyl)-benzene, the carbohydates such as a glucose, rhamnose, mannose, glyceraldehyde, and galactose, and the like, amino alcohols such as di(2-hydroxyethyl)amine, tri-(3-hydroxypropyl)amine, N,N′-di-(hydroxyethyl)-ethylenediamine, copolymer of allyl alcohol and styrene, N,N-di-(2-hydroxylethyl) glycine and esters thereof with lower mono-and polyhydric aliphatic alcohols, etc. Included within the group of aliphatic alcohols are those alkane polyols which contain ether groups such as polyethylene oxide repeating units, as well as those polyhydric alcohols containing at least three hydroxyl groups, at least one of which has been esterified with a mono-carboxylic acid having from eight to about 30 carbon atoms such as octanoic acid, oleic acid, stearic acid, linoleic acid, dodecanoic acid, or tall oil acid. Examples of such partially esterified polyhydric alcohols are the mono-oleate of sorbitol, the mono-oleate of glycerol, the mono-stearate of glycerol, the di-stearate of sorbitol, and the di-dodecanoate of erythritol. A preferred class of C₅-C₉ lactone derived dispersants are those prepared from aliphatic alcohols containing up to 20 carbon atoms, and especially those containing three to 15 carbon atoms. This class of alcohols inlcudes glycerol, erythritol, pentaerythritol, dipentaerythritol, tripentaerythritol, gluconic acid, glyceraldehyde, glucose, arabinose, 1,7-heptanediol, 2,4-heptanediol, 1,2,3-hexanetriol, 1,2,4-hexanetriol, 1,2,5-hexanetriol, 2,3,4-hexanetriol, 1,2,3-butanetriol, 1,2,4-butanetriol, quinic acid, 2,2,6,6-tetrakis(hydroxymethyl)-cyclohexanol, 1,10-decanediol, digitalose, and the like. The dispersants prepared from aliphatic alcohols containing at least three hydroxyl groups and up to fifteen carbon atoms are particularly preferred. An especially preferred class of polyhydric alcohols for preparing the lactone derived dispersants of the present invention are the polyhydric alkanols containing three to 15, especially three to six carbon atoms and having at least three hydroxyl groups. Such alcohols are exemplified in the above specifically identified alcohols and are represented by glycerol, erythritol, pentaerythritol, mannitol, sorbitol, 1,2,4-hexanetriol, and tetrahydroxy pentane and the like. In one preferred embodiment of the invention, a polyol, e.g., pentaerythritol is employed in a ratio of about 10:1 to 0.1:1, based on the amount of lactone used in the reaction. In practice, the ratio of lactone to polyol may vary considerable as a means of controlling the length of the sequence of the lactone units in the dispersant product. For example, the mole ratio of lactone to polyol may vary from about 10:1 to about 0.1:1, more preferable from about 5:1 to about 0.2:1, and most preferably from about 2:1, to about 0.4:1. Catalysts useful in the promotion of the lactone-polyol reactions are the same as those which are useful in connection with the lactone-polyamine reactions discussed above. The catalyst may be added to the reaction mixture at a concentration level of from about 50 to about 10,000 parts of catalyst per one million parts by weight of the total reaction mixture. THE AMINO ALCOHOL MATERIAL Suitable amino alcohol compounds which can be reacted with the lactone and hydrocarbyl substituted dicarboxylic acid material include those containing up to about 50 total carbon atoms and preferably up to abut 10 total carbon atoms, from about 1 to 5 nitrogen atoms, preferably from 1 to 3 nitrogen atoms, and from about 1 to about 15 hydroxyl groups, preferably from 1 to about 5 hydroxyl groups. Preferred amino alcohols include the 2,2-disubstituted-2-amino-1-alkanols having from two to three hydroxy groups and containing a total of 4 to 8 carbon atoms. This amino alcohol can be represented by the formula: wherein X is an alkyl or hydroxyalkyl group with the alkyl groups having 1 to 3 carbon atoms wherein at least one, and preferably both, of the X substituent is a hydrxoyalkyl group of the structure -(CH₂) n OH, n being 1 to 3. Examples of such amino alcohols include: 2-amino-2-methyl-1,3 propanediol, 2-amino-2-ethyl-1,3-propanediol, and 2-amino-2-(hydroxymethyl)1,3-propanediol, the latter also being known as THAM or tris (hydroxymethyl) amino methane. THAM is particularly preferred because of its effectiveness, availability and low cost. In one preferred embodiment of the invention, an amino alcohol, e.g., THAM is employed in a mole ratio of about 10:1 to 0.1:1, based on the amount of lactone used in the reaction. It will be appreciated,however, that the mole ratio lactone to amino alcohol may be varied considerably and that the reaction product, in most cases, will comprise a mixture of adducts. In this latter regard, it is contemplated that the mole ratio of lactone to amino alcohol may vary from about 10:1 to about 0.1:1, more preferable from about 5:1 to about 0.5:1, and most preferably from about 2:1 to about 0.6:1. Catalysts useful in the promotion of the lactone-amino alcohol reactions are the same as those which are useful in connection with the lactone-polyamine and lactone-polyol reactions, and corresponding amounts of catalyst may be employed. THE ACYLATING AGENTS The acylating agents which may be reacted simultaneously with the lactone and with the polyamine, polyol and/or amino alcohol materials to form the dispersant additives of the invention are dicarboxylic acid materials, e.g., acid, anhydride or ester materials, which are substituted with a long chain hydrocarbyl group, generally a polyolefin, and which contain 0.7 to 2.0, preferably 1.00 to 1.5, e.g, 1.05 to 1.3 moles, per mole of polyolefin of an alpha or beta unsaturated C₄ to C₁₀ dicarboxylic acid or anhydride or ester thereof, such a fumaric acid, itaconic acid, maleic acid, maleic anhydride, chloromaleic acid, dimethyl fumarate, chloromaleic anhydride, etc. Preferred olefin polymer substituents are polymers comprising a major molar amount of C₂ to C₁₀, e.g., C₂ to C₅ mono-olefin. Such olefins include ethylene, propylene, butylene, isobutylene, pentene, octene-1, styrene, etc. The polymers can be homopolymers such as polyisobutylene, as well as copolymers of two or more of such olefins such as copolymers of: ethylene and propylene; butylene and isobutylene; propylene and isobutylene; etc. Other copolymers include those in which a minor molar amount of the copolymer monomers, e.g., 1 to 10 mole %, is a C₄ to C₁₈ diolefin, e.g., a copolymer of isobutylene and butadiene; or a copolymer of ethylene, propylene and 1,4-hexadiene; etc. In some cases, the olefin polymer may be completely saturated, for example an ethylene-propylene copolymer made by a Ziegler-Natta synthesis using hydrogen as a moderator to control molecular weight. The olefin polymers will usually have number average molecular weights within the rang of about 300 and about 10,000, more usually between 500 and about 7,000. Particularly useful olefin polymers have number average molecular weights within the range of about 500 and 3,000, and more preferable between about 900 and about 2,500, with approximately one terminal double per polymer chain. An especially useful olefin polymer for a highly potent dispersant additive made in accordance with this invention is polyisobutylene. The number average molecular weight for such polymers can be determined by several known techniques. A convenient method for such determination is by gel permeation chromatography (GPC) which additionally provides molecular weight distribution information, wee W.W. Yau, J.J. Kirkland and D.D. Bly, "Modern Size Exclusion Liquid Chromatography", John Wiley and Sons, New York, 1979. Processes for reacting the olefin polymer with the C₄-C₁₀ unsaturated dicarboxylic acid, anhydride or ester to form athe acylating agents to be used in this invention are known in the art. For example, the olefin polymer and the dicarboxylic acid material may be simply heated together as disclosed in U.S. patents 3,361,673 and 3,401,118 to cause a thermal "ene" reaction to take place. Or, the olefin polymer can be first halogenated, for example, chlorinated or brominated to about 1 to 8, preferably 3 to 7 wt. % chlorine, or bromine, based on the weight of polymer, by passing the chlorine or bromine through the polyolefin at a temperature of 100 to 250, e.g., 140 to 225°C for about 0.5 to 10, preferably 1 to 7 hours. The halogenated polymer may then be reacted with sufficient unsaturated acid or anhydride at 100 to 250°C, usually about 140 to 180°C for about 0.5 to 10, e.g., 3 to 8 hours, so the product obtained will contain about 1.0 to 1.5, preferably 1.06 to 1.20, eg., 1.10 moles of the unsaturated acid per mole of the halogenated polymer. Processes of this general type are taught in U.S. Patents 3,087,436; 3,172,892; 3,272,746 and others. Alternatively, the olefin polymer, and the unsaturated acid material are mixed and heated while adding chlorine to the hot material. Processes of this type are disclosed in U.S. patents 3,215,707; 3,231,587; 3,912,764; 4,110,329; 4,234,435; and in U.K. 1,440,219. By the use of halogen, about 65 to 95 wt. % of the polyolefin, e.g., polyisobutylene will normally react with the dicarboxylic acid material. Upon carrying out a thermal reaction usually only about 50 to 75 wt. % of the polyisobutylene will react. Chlorination helps increase the reactivity. For convenience, the aforesaid functionality ratios of dicarboxylic acid producing units to polyolefin of 0.7 to 2.0 are based upon the total amount of polyolefin, that is, the total of both the reacted and unreacted polyolefin, used to make the product. REACTIONS OF THE LACTONE MATERIAL WITH AMINES, ALCOHOLS AND CARBOXYLIC ACIDS In order to form the lactone based dispersants of the present invention, the C₅-C₉ lactone material is reacted simultaneously with the acylating agent and with a polyamine, a polyol, an amino alcohol or a mixture thereof. This will result in a number of simultaneous and competing reactions whereby the lactone material, the acylating agent and the polyamine, polyol and/or amino alcohol react with each other to form a diversity of structures. The simultaneous reaction of the reagent materials may be effected, in the presence or absence of a solvent and in the presence or absence of a catalyst, simply by heating the reaction mixture to about 100°C to about 220°C, preferably from about 140°C to about 190°C, and most preferably from about 160°C to about 180°C, generally for 1 to 10, e.g., 2 to 6 hours until the desired amount of water is removed. Reaction ratios can vary considerably, depending upon the reactants, the amount of excess lactone, if any, the type bonds formed, etc. Generally, the ratio of lactone to acylating agent, or polyamine, or polyol, or amino alcohol is from about 10:1 to about 0.1:1. In general, the chemistry of these competing reactions is known. However, prior to the present invention, there was no published information on the quantitative reaction rates of C₅-C₉ lactone, such as E-caprolactone, with polyamines, polyols, amino alcohols and acylating agents of the type discussed above. These data are very important when practical utilization of this chemistry for preparing dispersants is considered. This is due to the diversity of structures of amino group- and hydroxyl group-containing that are available. In one aspect of the invention, it has been found that the relative rate constants, for example, when reacting E-caprolactone with various amines, alcohols and acids at 140°C using 50 wt.% chlorobenzene as a solvent medium and with stoichiometric quantities of reagents, can be summarized as follows: 1. The rate constant for amino groups is much higher than the rate constant for hydroxyl groups; 2. The rate constant for primary amino or hydroxyl groups is very much higher than for secondary amino or hydroxyl groups; 3. The use of a catalyst, e.g., stannous octanoate increases the rate contant for primary amino groups by a factor of about 3, and increases the rate constant for primary hydroxyl groups of a factor of about 100; and 4. Acids are virtually unreactive with caprolactone. Based on the above findings, it will be appreciated that when a C₅-C₉ lactone, such as E-caprolactone is heated simultaneously with a polyamine, such as 1,2-diaminoethane, and with an acylating agent, such as polyisobutenyl succinic anhydride, the reaction mass will comprise a mixture of dispersants which contain a sequence of methylene units which is derived from the lactone reagents. In the case of E-caprolactone, which is a preferred lactone for use in this invention, the dispersant products will contain a sequence of five methylene units as illustrated schematically by the following equation: (It is to be understood that only one of a mixture of dispersant products is illustrated.) where PIB is polyisobutylene having a molecular weight of 300-10,000 and there are 0.7-2.0 succinic anhydride moieties per polyisobutylene moiety. In an alternative embodiment, the simultaenous reaction between E-caprolactone, a polyisobutenyl succinic anhydride acrylating agent and a polyol, such as pentaerythritol can be illustrated as follows: (It is to be understood that only one of a mixture of dispersant products is illustrated) where PIB is the same as above. In another alternative embodiment, the simultaneous reaction between E-caprolactone, a polyisobutenyl succinic anhydride and an amino alcohol such as tris (hydroxymethyl) amino methane can be illustrated as follows: (it is to be understood that only one of a mixture of dispersant products is illustrated.) Although the chemistry of the lactone-polyamine, lactone-polyol and lactone-amino alcohol reactions are such that primary functional groups are more reactive than the secondary functional groups, it is possible that the secondary functional groups and the hydroxyl gruops in the reaction products can react with additional lactone molecules to form a diversity of structures. In the reactions discussed above, the average degree of polymerization (DP) of the lactone moiety i.e., the sequence of lactone units in a row in the reaction products, may vary depending upon the intended application. At DP's of much greater than about 10 the dispersants which are formed can exhibit crystallinity; a characteristic which is undesirable in an oil soluble dispersant due to the consequent high viscosity, or even solid, oil products which can be obtained. However, at lower DP's oil soluble adducts posessing low viscosity and desirable sludge and varnish inhibition characteristics are obtained. Accordingly, regardless of the identity of the lactone material, the average degree of polymerization (DP) should be between about 0.2 and about 100, more preferably between about 0.2 and about 50, and most preferably between 0.5 and about 20. For optimal dispersant performance sequences of from about 1 to about 5 lactone units in a row are preferred. The degree of polymerization can be controlled by controlling the reaction conditions, including the mole ratio of lactone material relative to the other reagents, amount of catalyst employed, and the like. The dispersants of this invention other advantages over those dispersants which are prepared by first reacting the C₅-C₉ lactone with a polyamine, or polyol or amino alcohol to form an intermediate adduct, and then acylating the intermediate adduct. For example, in the case of the simultaneous reaction of the lactone material, a polyamine and an acylating agent, the reaction time is reduced since the post-capping is avoided. In the case of the simultaneous reaction of the lactone, polyol and acylating agent, the advantages are even more evident since the simultaneous reaction can take place at significantly lower temperatures than are required for the more conventional acylating agent/polyol/post-capping process. The simultaneous reaction process also results in less sediment formation than the conventional higher temperature process, and the resulting dispersants are characterized by lower viscosities than the corresponding acylating agent/polyol or acylating agent/polyol/lactone post-capping dispersants. Further aspects of the present invention reside in the formation of metal complexes and other post-treatment derivatives, e.g. borated derivatives, of the novel additives prepared in accordance with this invention. Suitable metal complexes may be formed in accordance with known techniques of employing a reactive metal ion species during or after the simultaneous reaction of the lactone, acylating agent and polyamine, polyol or amino alcohol. Complex-forming metal reactants include the nitrates, thiocyanates, halides, carboxylates, phosphates, thio-phosphates, sulfates, and borates of transition metals such as iron, cobalt, nickel, copper, chromium, manganese, molybdenum, tungsten, ruthenium, palladium, platinum, cadmium, lead, silver, mercury, antimony and the like. Prior art disclosures of these complexing reactions may be found in U.S. Patents 3,306,908 and Re. 26,433. Post-treatment compositions include those formed by reacting the novel additives of the present invention with one or more post-treating reagents, usually selected from the group consisting of boron oxide, boron oxide hydrate, boron halides, boron acids, sulfur chlorides, phophorous sulfides and oxides, carboxylic acid or anhydride acylating agents, epoxides episulfides and acrylonitriles. The reaction of such post-treating agents with the novel C₅-C₉ lactone derived dispersant compounds of this invention is carried out using procedures known in the art. For example, boration may be accomplished in accordance with the teachings of U.S. Patent 3,254,025 by treating a nitrogen-halide, ester or acid to provide about 0.1 to 1 atomic proportions of boron for each atomic proportion of nitrogen in the composition. Treatment may be carried out by adding about 1-3 wt % of the boron compound, preferably boric acid, and heating and stirring the reaction mixture at about 135° C to 165°C for 1 to 5 hours followed by nitrogen stripping and filtration, if desired. Mineral oil or inert organic solvents facilitate the process. THE COMPOSITIONS The lactone derived additives of the present invention have been found to possess very good dispersant properties as measured herein in a wide variety of environments. Accordingly, the lactone derived adducts are used by incorporation and dissolution into an oleaginous material such as fuels and lubricating oils. When the dispersants of this invention are used in normally liquid petroleum fuels such as middle distillates boiling from about 66 to 427°C (150° to 800°F) including kerosene, diesel fuels, home heating fuel oil, jet fuels, etc., a concentration of the additive in the fuel in the range of typically from about 0.001 to about 0.5, and preferably 0.001 to about 0.1 weight percent, based on the total weight of the composition, will usually be employed. The lactone derived dispersants find their primary utility in lubricating oil compositions which employ a base oil in which the additives are dissolved or dispersed. Such base oils may be natural or synthetic although the natural base oils will derive a greater benefit. Thus, base oils suitable for use in preparing lubricating compositions of the present invention include those conventionally employed as crankcase lubricating oils for spark-ignited and compression-ignited internal combustion engines, such as automobile and truck engines, marine and railroad diesel engines, and the like. Advantageous results are also achieved by employing the dispersant additives of the present invention in base oils conventionally employed in and/or adapted for use as power transmitting fluids such as automatic transmission fluids, tractor fluids, universal tractor fluids and hydraulic fluids, heavy duty hydraulic fluids,power steering fluids and the like. Gear lubricants, industrial oils, pump oils and other lubricating oil compositions can also benefit from the incorporation therein of the additives of the present invention. Thus, the additives of the present invention may be suitably incorporated into synthetic base oils such as alkyl esters of dicarboxylic acids, polyglycols and alcohols, polyalphaolefins, alkyl benzenes, organic esters of phosphoric acids, polysilicone oil, etc. Natural base oils include mineral lubricating oils which may vary widely as to their crude source, e.g., whether paraffinic, naphthenic, mixed, paraffinic-naphthenic, and the like; as well as to their formation, e.g., distillation range, straight run or cracked, hydrofined, solvent extracted and the like. More specifically, the natural lubricating oil base stocks which can be used in the compositions of this invention may be straight mineral lubricating oil or distillates derived from paraffinic, naphthenic, asphaltic, or mixed base crudes, or, if desired, various blends oils may be employed as well as residuals, particularly those from which asphaltic constituents have been removed. The oils may be refined by conventional methods using acid, alkali, and/or clay or other agents such as aluminum chloride, or they may be extracted oils produced, for example, by solvent extraction with solvents of the type of phenol, sulfur dioxide, furfural, dichlorodiethyl ether, nitrobenzene, crotonaldehyde, etc. The lubricating oil base stock conveniently has a viscosity of typically about 2.5 to about 12, and preferably about 2.5 to about 9 mm²/sec (cs.) at 100°C. Thus, the lactone derived additives of the present invention can be employed in a lubricating oil composition which comprises a lubricating oil, typically in a major amount, and the dispersant additive, typically in a minor amount, which is effective to impart enhanced dispersancy, relative to the absence of the additive. Additional conventional additives selected to meet the particular requrements of a selected type of lubricating oil composition can be included as desired. The dispersants of this invention are oil-soluble, dissolvable in oil with the aid of a suitable solvent, or are stably dispersible materials. Oil-soluble, dissolvable, or stably dispersible as that terminology is used herein does not necessarily indicate that the materials are soluble, dissolvable, miscible, or capable of being suspended in oil in all proportions. It does mean, however, that the dispersant additives, for instance, are soluble or stably dispersible in oil to an extent sufficient to exert their intended effect in the environment in which the oil is employed. Moreover, the additional incorporation of other additives may also permit incorporation of higher levels of a particular dispersant, if desired. Accordingly, while any effective amount of the dispersant additives can be incorporated into the lubricating oil composition, it is contemplated that such effective amount be sufficient to provide said lube oil composition with an amount of the additive of typically from about 0.01 to about 15 e.g., 0.1 to 10, and preferably from about 0.1 to about 7 wt.%, based on the weight of said composition. The dispersant additives of the present invention can be incorporated into the lubricating oil in any convenient way. Thus, they can be added directly to the oil by dispersing, or dissolving the same in the oil at the desired level of concentration typically with the aid of a suitable solvent such as toluene, or tetrahydrofuran. Such blending can occur at room temperature or elevated temperatures. Alternatively, the dispersant additives may be blended with a suitable oil-soluble solvent and base oil to form a concentrate, and then blending the concentrate with lubricating oil base stock to obtain the final formulation. Concentrates will typically contain from about 20 to about 60 wt.%, by weight dispersant additive, and typically from about 80 to about 20%, preferably form about 60 to about 20% by weight base oil, based on the concentrate weight. The lubricating oil base stock for the dispersant additives of the present invention typically is adapted to perform a selected function by the incorporation of additives therein to form lubricating oil compositions (i.e., formulations). Representative additives typically present in such formulations include viscosity modifiers, corrosion inhibitors, oxidation inhibitors, friction modifiers, other dispersants, anti-foaming agents, anti-wear agents, pour point depressants, detergents, rust inhibitors. Viscosity modifiers impart high and low temperature operability to the lubricating oil and permit it to remain shear stable at elevated temperatures and also exhibit acceptable viscosity or fluidity at low temperatures. Viscosity modifiers are generally high molecular weight hydrocarbon polymers including polyesters. The viscosity modifiers may also be derivatized to include other properties or functions, such as the addition of dispersancy properties. These oil soluble viscosity modifying polymers will generally have number average molecular weights of from 10³ to 10⁶, preferably 10⁴ to 10⁶, e.g., 20,000 to 250,000, as determined by gel permeation chromatography or membrane osmometry. Representative examples of suitable viscosity modifiers are any of the types known to the art including polyisobutylene, copolymers of ethylene and propylene, polymethacrylates, methacrylate copolymers, copolymers of an unsaturated dicarboxylic acid and vinyl compound, interpolymers of styrene and acrylic esters, and styrene/isoprene copolymers. Corrosion inhibitors, also known as anti-corrosive agents, reduce the degradation of the metallic parts contacted by the lubricating oil composition. Illustrative of corrosion inhibitors are phosphosulfurized hydrocarbons and the products obtained by reaction of a phosphosulfurized hydrocarbon with an alkaline earth metal oxide or hydroxide, preferably in the presence of an alkylated phenol or of an alkylphenol thioester, and also preferably in the presence of carbon dioxide. Phosphosulfurized hydrocarbons are prepared by reacting a suitable hydrocarbon such as terpene, a heavy petroleum fraction of a C₂ to C₆ olefin polymer such as polyisobutylene, with from 5 to 30 wt.% of a sulfide of phosphorus for 1/2 to 15 hours, at a temperature in the range of 66 to 316°C (150° to 600°F) Neutralization of the phosphosulfurized hydrocarbon may be effected in the manner taught in U.S. Patent No. 1,969,324. Oxidation inhibitors reduce the tendency of mineral oils to deteriorate in service which deterioration can be evidenced by the products of oxidation such as sludge and varnish-like deposits on the metal surfaces and by viscosity growth. Such oxidation inhibitors include alkaline earth metal salts of alkylphenolthioesters having preferably C₅ to C₁₂ alkyl side chains, e.g., calcium nonylphenol sulfide, barium t-octylphenyl sulfide, dioctylphenylamine, phenylalphanaphthylamine, phosphosulfurized or sulfurized hydrocarbons. Friction modifiers serve to impart the proper friction characteristics to lubricating oil compsoitions such as automatic transmission fluids. Representative examples of suitable friction modifiers are found in U.S. Patent No. 3,933,659 which discloses fatty acid esters and amides; U.S. Patent No. 4,176,074 which describes molybdenum complexes of polyisobutyenyl succinic anhydride-amino alkanols; U.S. Patent No. 4,105,571 which discloses glycerol esters of dimerized fatty acids; U.S. Patent No. 3,779,928 which discloses alkane phosphonic acid salts; U. S. Patent No. 3,778,375 which discloses reaction products of a phosphonate with an oleamide; U. S. Patent No. 3,852,205 which discloses S-carboxyalkylene hydrocarbyl succinimide, S-carboxyalkylene hydrocarbyl succinamic acid and mixtures thereof; U. S. Patent No. 3,879,306 which discloses N-(hydroxyalkyl)alkenyl-succinamic acids or succinimides; U.S. Patent No. 3,932,290 which discloses reaction products of di-(lower alkyl) phosphites and epoxides; and U. S. Patent No. 4,028,258 which discloses the alkylene oxide adduct of phosphosulfurized N-(hydroxyalkyl) alkenyl succinimides. The disclosures of the above references are herein incorporated by reference. The most preferred friction modifiers are succinate esters, or metal salts thereof, of hydrocarbyl substituted succinic acids or anhydrides and thiobis alkanols such as described in U. S. Patent No. 4,344,853. Dispersants maintain oil insolubles, resulting from oxidation during use, in suspension in the fluid thus preventing sludge flocculation and precipitation or deposition on metal parts. Suitable dispersants include high molecular weight alkyl succinates, the reaction product of oil-soluble polyisobutylene succinic anhydride with ethylene amines such as tetraethylene pentamine and borated salts thereof. Pour point depressants lower the temperature at which the fluid will flow or can be poured. Such depressants are well known. Typically of those additives which usefully optimize the low temperature fluidity of the fluid are C₈-C₁₈ dialkylfumarate vinyl acetate copolymers, polymethacrylates, and wax naphthalene. Foam control can be provided by an antifoamant of the polysiloxane type, e.g., silicone oil and polydimethyl siloxane. Anti-wear agents, as their name implies, reduce wear of metal parts. Representatives of conventional anti-wear agents are zinc dialkyldithiophosphate and zinc diaryldithiosphate. Detergents and metal rust inhibitors include the metal salts of sulphonic acids, alkyl phenols, sulfurized alkyl phenols, alkyl salicylates, naphthenates and other oil soluble mono- and di-carboxylic acids. Highly basic (viz, overbased) metal salts, such as highly basic alkaline earth metal sulfonates (especially Ca and Mg salts) are frequently used as detergents. Some of these numerous additives can provide a multiplicity of effects, e.g., a dispersant-oxidation inhibitor. This approach is well known and need not be further elaborated herein. Compositions when containing these conventional additives are typically blended into the base oil in amounts which are effective to provide their normal attendant function. Representative effective amounts of such additives are illustrated as follows: When other additives are employed, it may be desirable, although not necessary, to prepare additive concentrates comprising concentrated solutions or dispersions of the dispersant (in concentrate amounts hereinabove described), together with one or more of said other additives (said concentrate when constituting an additive mixture being referred to herein as an additive-package) whereby several additives can be added simultaneously to the base oil to form the lubricating oil composition. Dissolution of the additive concentrate into the lubricating oil may be facilitated by solvents and by mixing accompanied with mild heating, but this is not essential. The concentrate or additive-package will typically be formulated to contain the dispersant additive and optional additional additives in proper amounts to provide the desired concentration in the final formulation when the additive-package is combined with a predetermined amount of base lubricant. Thus, the dispersant of the present invention can be added to small amounts of base oil or other compatible solvents along with other desirable additives to form additive-packages containing active ingredients in collective amounts of typically from about 2.5 to about 90%, and preferably from about 5 to about 75%, and most preferably from about 8 to about 50% by weight additives in the appropriate proportions with the remainder being base oil. The final formulations may employ typically about 10 wt.% of the additive-package with the remainder being base oil. All of said weight percents expressed herein are based on active ingredient (a.i.) content of the additive, and/or upon the total weight of any additive-package, or formulation which will be the sum of the a.i. weight of each additive plus the weight of total oil or diluent. This invention will be further understood by reference to the following examples, wherein all parts are parts by weight and all molecular weights and number average molecular weights unless otherwise noted, and which include preferred embodiments of the invention. Example 1 - Polyisobutenyl Succinic Anhydride-Polyamine Reaction Product (Control) About 324g (0.2 mole) of a 59% a.i. polyisobutenyl succinic anhydride (PIBSA) derived from of polyisobutylene (PIB) having an average molecular weight of 1300 was diluted with 74g of solvent 150 neutral mineral oil (S15ON) and heated to 150°C while under a nitrogen blanket. The PIBSA had an ASTM Saponification Number (SAP) of 103 which calculates to a succinic anhydride (SA) to polyisobutylene (PIB) ratio of 1.31 based upon the starting PIB as follows Thereafter, 19.3g (0.1 mole) of polyamine bottoms (PAM) was added slowly while stirring under a nitrogen blanket. This reaction was kept at 150°C for two yours while stirring and nitrogen sparging to form a polyisobutenyl succinimide (PIBSI). The oil solution was filtered and collected. It analyzed for 1.59 wt.% nitrogen and had a viscosity of 508 SSU. Example 2 - Post Reaction Polyisobutenyl Succinimide To about 413g of the polyisobutenyl succinimide prepared in accordance with Example 1, 4.13g of E-caprolactone was added and the reaction mixture was heated to 150°C for 2 hours. The reaction product analyzed for 1.54 wt% nitrogen and a viscosity of 505 SSU. Example 3 - Simultaneous Reaction About 324g (0.2 mole) of the PIBSA used in Example 1, 19.3g of polyamine bottoms, 74g of S15ON and 4.13g of E-caprolactone were mixed in a reaction flask and heated to 150°C while stirring under nitrogen blanket. The reaction mixture was held at 150°C for 2 hours, and then stripped with a mild nitrogen stream for one half hour. The product was filtered and collected. It analyzed for 1.57 wt.% nitrogen and a viscosity of 523 SSU. Example 4 - Polyisobutenyl Succinic Anhydride Polyol Reaction Product (Control) About 200g (0.1 mole) of a polyisobutenyl succinic anhydride (SAP 59.5, ai 82.2 wt.% active ingredient) derived from a PIB of average M n 1,900 was mixed with 14.3g of a S15ON and 16.5g (0.12 mole) of pentaerythritol (PE) in the presence of 1.7 g of SA 117 (a commercially available alkyl sulfonic acid esterification catalyst). The reaction mixture was slowly heated to 210-220oC and kept at this temperature for 4-5 hours until the esterification was completed as evidenced by infrared analysis. The reaction product was stripped with nitrogen for one half hour, filtered and collected. It had a viscosity of 1485 SSU. Example 5 - Post-Reacted Polyisobutenyl Succinate About 358g of the product prepared in Example 4 was mixed with 3.9g of E-caprolactone and 0.2g of stannous octanoate, and was heated to 150°C for 2 hours. The product was then stripped with nitrogen and collected. It had a viscosity of 1614 SSU. Example 6 - Simultaneous Reaction About 200g (0.1 mole) of the PIBSA employed in Example 4 was mixed with 16.5g of PE, 3.9g of E-caprolactone, and 0.2g of stannous octanoate. The reaction mixture was then slowly heated to 180°C. It was observed that the PE went in solution at about 165°C. The reaction mixture was held at 180°C for 2 hours and nitrogen stripped for one half hour. The reaction mixture was filtered, collected and analyzed for a viscosity of 895 SSU. Samples of the dispersants prepared in accordance with Examples 1-6 were then subjected to a standard sludge inhibition bench test (SIB) and a standard varnisch inhibition bench test (VIB) The SIB and VIB tests forecast the performance of a lubricant in a gasoline engine. These tests are described below. The SIB test employs a used crancase mineral lubricating oil composition having an original viscosity of about 325 SUS at 37.8°C that has been used in a taxicab that is driven generally for short trips only, thereby causing a buildup of a high concentration of sludge precursors. The oil used contains only a refined base mineral oil, a viscosity index improver, a pour point depressant and zinc dialkyldithiophosphate antiwear additives. The oil contains no sludge dispersants. Such oil is acquired by draining and refilling taxicab crankcases at about 1610-3220 km (1,000-2,000 mile) intervals. The SIB test is conducted in the following manner: the used crankcase oil is freed of sludge by centrifuging for one half hour at about 39.000 gravities (gs). The resulting clear bright red oil is then decanted from the insoluble particles. However, the supernatant oil still contains oil-soluble sludge precursors which, under the conditions employed by this test, tend to form additional oil-insoluble deposits of sludge. The sludge inhibiting properties of the additives being tested are determined by adding to portions of the used oil 0.5 wt.% on an active basis, of the particular additive being tested. Ten grams of each one being tested is placed in a stainless steel centrifuge tube and is heated at 140°C for 16 hours in the presence of air. Following the heating, the tube containing the oil being tested is cooled and then centrifuged for 30 minutes at about 39,000 gs. Any deposits of new sludge that form in this step are separated from the decanting supernatant oil and then carefully washed with 15 ml. of pentane to remove all remaining oils from the sludge. The weight, in milligrams, of the new solid sludge that forms in the test is determined by drying the residue and weighing it. The results are reported as milligrams of sludge per ten grams of oil thus measuring differences as small as one part per ten thousand. The less new sludge formed, the more effective is the additive as a dispersant. In other words, if the additive is effective, it will hold at least a portion of the new sludge that forms on heating and oxidation, stably suspended in the oil so that it does not precipitate during the centrifuging period. In the VIB test, a test sample consisting of ten grams of lubricating oil containing 0.5 wt.%, on an active basis, of the additive being evaluated is used. The test oil is a commercial lubricating oil obtained from a taxi after 3220 km (2,000) miles of driving with said lubricating oil. Each sample is heat soaked overnight at about 140°C and thereafter centrifuged to remove the sludge. The supernatant fluid of each sample is subjected to heat cycling from about 150°C to room temperature over a period of 3.5 hours at a frequency of about two cycles per minute. During the heating phase, a gas containing a mixture of 0.7 volume percent SO₂, 1.4 volume percent NO and the balance air is bubbled through the test samples and during the cooling phase, water vapor was bubbled through the test samples. At the end of the test period, which testing cycle can be repeated as necessary to determine the inhibiting effect of any additive, the wall surfaces of the test flasks in which the samples are contained are visually evaluated as to the varnish inhibition. The amount of varnish deposited on the walls is rated at values of from one to eleven with the higher number being the greater amount of varnish. It has been found that this test forecasts the varnish results obtained as a consequence of carrying out the ASTM MS-VD engine tests which is described more fully hereinbelow. Table I, which follows, summarizes the compositions tested and the test results: The data in Table I indicate that the viscosity of the dispersant prepared by reacting PIBSA with PAM (Example 1) is comparable with the viscosity of the dispersants by post-reacting PIBSA-PAM with caprolactone (CL) (Example 2) or by simultaneously reaction PIBSA-PAM and CL (Example 3). However, the data show a marked improvement in sludge inhibition properties when caprolactone-derived moieties are present in the dispersant, particularly in the case of the dispersants formed by simultaneously reacting PIBSA, PAM and CL. The varnish inhibition properties are marginally improved for both CL-containing dispersants, and all of the dispersants are within commercially acceptable standards. For the PIBSA-PE system, the data indicate that the dispersant prepared by simultaneously reacting PIBSA, PE and CL (Example 6) had a much lower viscosity than did either the control (Example 4) which did not contain any CL moieties or the post reacted product (Example 5). The SIB value for the product of this invention (Example 6), although somewhat higher than that of the control (Example 4, which contains no CL) is shown to be much lower than that of the post reacted product. The VIB values are excellent in all cases due to the sensitivity of the VIB test to polyol systems.

Claims: A C₅-C₉ lactone derived material useful as an oil additive and formed by simultaneously reacting a hydrocarbyl substituted C₄-C₁₀ dicarboxylic acid producing materials with a C₅-C₉ lactone and a member selected from the group consisting of (a) a polyamine having from 2 to 60 total carbon atoms and from 2 to 12 nitrogen atoms, (b) an aliphatic polyhydric alcohol containing up to 100 carbon atoms and from 2 to 10 hydroxyl groups, (c) an amino alcohol containing up to 50 total carbon atoms, from 1 to 5 nitrogen atoms and from 1 to 15 hydroxyl groups, or (d) mixtures thereof, said hydrocarbyl substituted acid producing material being formed by reacting an olefin polymer of a C₂-C₁₀ monoolefin having a number average molecular weight of 300 to 10,000 and a C₄-C₁₀ monounsaturated dicarboxylic acid material, wherein there are an average of 0.7 to 2.0 dicarboxylic acid producing moieties per molecule of said olefin polymer used in the reaction. A C₅-C₉ lactone derived material of claim 1, wherein said olefin polymer is polyisobutylene. A C₅-C₉ lactone derived material of claim 1 or claim 2, wherein said lactone is E-caprolactone. A C₅-C₉ lactone derived material of any of claims 1 to 3, wherein said C₄-C₁₀ monounsaturated dicarboxylic acid material is maleic anhydride. The C₅-C₉ lactone derived material of claims 2 and 4, wherein there are 1 to 1.5 succinic anhydride units per polyisobutenyl moiety present in said hydrocarbyl substituted C₄-C₁₀ dicarboxylic acid producing material and wherein the number average molecular weight of said polyisobutylene is from 500 to 3,000. The C₅-C₉ lactone derived material of any of claims 1 to 5, wherein said C₅-C₉ lactone and said hydrocarbyl substituted C₄-C₁₀ dicarboxylic acid producing material are reacted with a polyamine, and wherein said polyamine is an aliphatic saturated amine having the formula: wherein R and R′ independently are selected from the group consisting of hydrogen, C₁ to C₂₅ straight or branched chain alkyl radicals, C₁ to C₁₂ alkoxy C₂ to C₆ alkylene radicals, and C₁ to C₁₂ alkylamino C₂ to C₆ alkylene radicals; each s is the same or a different number of from 2 to 6, and t is a number of from 0 to 10, with the provision that when t=0, at least one of R or R′ must be H such that there are at least two of either primary or secondary amino groups. A C₅-C₉ lactone derived material of claim 6, wherein said amine is 1,2-diaminoethane; 1,3-diaminopropane; 1,4-diaminobutane, 1,6-diaminohexane; diethylene triamine; triethylene tetramine; tetraethylene pentamine; 1,2-propylene diamine; di-(1,2-propylene) triamine; di-(1,3-propylene) triamine; N,N-dimethyl-1,3-diaminopropane; N,N-di-(2-aminoethyl) ethylene diamine; or N-dodecyl-1,3-propane diamine. A C₅-C₉ lactone derived material of any of claims 1 to 5, wherein said amine is selected from the group consisting alicyclic diamines, imidazolines, morpholines and N-aminoalkyl piperazines of the general formula: wherein G is independently selected from the group consisting of hydrogen and omega (nontertiary)-amino-alkylene radicals of from 1 to 3 carbon atoms, and p is a number of from 1 to 4. The C₅-C₉ lactone derived material of any of claims 1 to 5, wherein said amine is a mixture of poly (ethyleneamines) averaging from 5 to 7 nitrogen atoms per molecule. The C₅-C₉ lactone derived material of any of claims 1 to 5, wherein said amine is a polyoxyalkylene polyamine having the formula: NH₂-alkylene-(0-alkylene) m -NH₂ wherein m has a value of from 3 to 70; or R-[alkylene-(0-alkylene) n -NH₂] a wherein n has a value of from 1 to 40 with the provision that the sum of all the n's is from 3 to 70, R is a substituted saturated hydrocarbon radical of up to 10 carbon atoms, wherein the number of substituents on the R group is represented by the value of "a", which is a number from 3 to 6. The C₅-C₉ lactone derived material of any of claims 1 to 10, which has been post-treated with a complex-forming metal or boron reactant. The C₅-C₉ lactone derived material of any of claims 1 to 5, wherein said C₅-C₉ lactone and said hydrocarbyl substituted C₄-C₁₀ dicarboxylic acid producing material are reacted with a polyhydric alcohol comprising erythritol, pentaerythritol, mannitol, sorbitol, 1,2,4-hexanetriol or tetrahydroxy pentane. The C₅-C₉ lactone derived material of any of claims 1 to 5, wherein said C₅-C₉ lactone and said hydrocarbyl substituted C₄-C₁₀ dicarboxylic acid producing material reacted with an amino alcohol comprising a 2,2-disubstituted-2-amino-1-alkanol of the formula: wherein X is alkyl or hydroxyalkyl group with the alkyl groups having from 1 to 3 carbon atoms and at least one of the X substituents is a hydroxyalkyl group of the formula -(CH₂) n OH, and wherein n is 1 to 3. The C₅-C₉ lactone derived material of claim 13, wherein said amino alcohol tris (hydroxymethyl) amino methane. A process for preparing a C₅-C₉ lactone derived material useful as an oil additive, which comprises simultaneously reacting i) a C₅-C₉ lactone with ii) a member selected from the group consisting of a) polyamines having from 2 to 60 total carbon atoms and from 2 to 12 nitrogen atoms, b) aliphatic polyhydric alcohols having containing up to 100 carbon atoms and from 2 to 10 hydroxyl groups, c) or amino alcohols containing up to 50 total carbon atoms, from 1 to 3 nitrogen atoms, and from 1 to 15 hydroxyl groups, or d) mixtures thereof to form a lactone adduct intermediate product; and with iii) a hydrocarbyl substituted C₄-C₁₀ dicarboxylic acid producing material, said hydrocarbyl substituted acid producing material being formed by reacting an olefin polymer of a C₂-C₁₀ monoolefin having a number average molecular weight of from 300 to 10,000 and a C₄-C₁₀ monounsaturated dicarboxylic acid material, wherein there are an average of 0.7 to 2.0 dicarboxylic acid producing moieties per molecule of said olefin polymer used in the reaction. The process of claim 15, wherein said olefin polymer is polyisobutylene and/or said lactone is E-caprolactone and/or said C₄-C₁₀ monounsaturated dicarboxylic acid material is maleic anhydride. An oleaginous composition comprising (I) an oleaginous material selected from the group consisting of fuels and lubricating oil and (II) a C₅-C₉ lactone derived material of any of claims 1 to 14. A lubricating oil composition comprising a lubricating oil and from 0.01 to 15 wt. % of the C₅-C₉ lactone derived material of any of claims 1 to 14.

Inventors: GUTIERREZ, ANTONIO, LUNDBERG, ROBERT DEAN
Applicants: EXXON CHEMICAL PATENTS INC.
Application year: 1987
Main classification: C10M159
IPC codes: C08G63, C10M145, C10M149, C10L1, C10M159, C10L10, C10M133, C10M129, C10N20, C10N40, C08F8, C10N60, C10N30