PROSTHETIC LIGAMENT

Abstract: A nonaugmented prosthetic ligament (10) for per­ manently replacing a natural ligament spanning first and second body members, such as the femur and tibia includes a load bearing member (20) formed from a plurality of biocompatible polyolefin fibers (22) positioned at angles of from 0 to 55° relative to the longitudinal axis of the load bearing member. Each fiber is less than 100 microns in diameter and has a tensile strength greater than or equal to about 50,000 psi. The load bearing member may be used alone or may be formed into a hollow braid having a core (30) disposed within the hollow portion of the braid to provide shape for the load bearing member. A sheath (40) may be friction fit or molded onto the exterior of the load bearing member to prevent abrasion of the fibers.

Description: BACKGROUND OF THE INVENTION Field of the Invention The present invention relates generally to prosthetic devices and more particularly to a permanent prosthetic ligament. Description of the Prior Art Attempts to repair or replace damaged ligaments have been varied and generally inadequate for immediately restoring full strength and stability to the involved joint. Workers in the field have transferred natural tissue from other parts of a patient's body to the involved joint. Synthetic materials have also been used to augment natural tissue transfers. A number of techniques employing carbon fiber-type or polypropylene augmentation devices are described in 196 CLINICAL ORTHOPAEDICS AND RELATED RESEARCH, SYNTHETIC LIGAMENTS AND TENDONS, (H. ALexander & A. Weiss eds. June 1985). For example, a flat strap-like braid of polypropylene fibers was used to augment natural tissue grafts in studies conducted on goats. See G. McPherson et al. "Experimental Mechanical and Histologic Evaluation of the Kennedy Ligament Augmentation Device", CLINICAL ORTHOPAEDICS supra at 186. The time required for the recipient to return to normal activity is generally about one year or longer. As an alternative to natural tissue grafts, xenografts, tissue grafts from a species other than the recipient species, have been implanted to replace natural ligaments. Like the natural tissue grafts and the augmentation devices, xenografts have tended to be unpredictable in the long term for restoring full strength and stability to the involved joint. Another type of prosthetic ligament relies on bone ingrowth to aid in the attachment of the ligament to bone. Bone ingrowth strengthens the attachment but requires about six months to complete. In the meantime, the recipient's mobility should be restricted. Dahlen et al. U. S. Patent No. 4,187,558, which issued on February 12, 1980, describes a flexible braid made of polyethylene, encased in silicone rubber. A velour covered collar at one or both ends of the braid aids in attachment to the bone and promotes bone ingrowth to anchor the device. Several permanent, nonaugmented prosthetic ligaments have been developed. Dore U. S. Patent No. 4,301,551, which issued on November 24, 1981 describes a deformable silicone core surrounded by a tensionable wrapping of stainless steel threads wound in a helical angle about the core. The core is the load bearing member and is capable of large elastic deformation in response to compression by the threads when the device is stretched. Two rigid plastic rods, one at each end of the core, connect the device to the bones of a joint. Treace U. S. Patent No. 3,953,896, which issued on May 4, 1976 describes a prosthetic ligament made of a flexible high molecular weight polyethylene rod. Stainless steel sleeves and polyethylene nuts on each end of the flexible rod hold the prosthetic ligament to the bones. A third permanent, nonaugmented prosthetic ligament reported by C. Bolton and W. Bruchman, "The GORE-TEX tm Expanded Polytetrafluoroethylene Prosthetic Ligament", CLINICAL ORTHOPAEDICS supra at 202, is constructed of bundles of Gore-Tex R fibers arranged in a braided configuration. The braid is fixed by bone screws placed through eyelets at each end of the braid. The goal of ligament replacement is to permit the recipient to return to his or her full range of activity as soon as possible. To that end, researchers have attempted by several means to mimic some of the parameters of strength, flexibility, extension and/or recovery found in natural ligaments. Natural ligaments are bands of flexible fibrous connective tissue which join bones or hold organs in place. The mechanical properties of a natural ligament were reported by D. Butler et al., "On the Interpretation of Our Anterior Cruciate Ligament Data", CLINICAL ORTHOPAEDICS, supra at 26. Butler et al. measured the stiffness of the anterior cruciate ligament-bone unit. The stiffness measured for young donors was 182 ± 56 kilonewtons per meter and for older donors was 129 ± 39 kilonewtons per meter. The maximum force for tissues obtained from young donors was 1730 ± 66N. An object of the present invention is to provide a permanent nonaugmented prosthetic ligament having parameters of strength, flexibility, extension and recovery that at least approximate those of a natural ligament. A further object of the present invention is to provide such a prosthetic ligament that does not depend solely upon bone ingrowth for strengthening the attachment to the bones of the involved joint, and thus, does not require long periods of recuperation before the recipient can resume a full range of normal activity. In EP-A-0169045, there is disclosed a prosthetic ligament for permanently, flexibly connecting first and second body members comprising a nonaugmented load bearing member having a longitudinal axis for permanently spanning the distance between said first and second body members for providing a prosthetic ligament having parameters of strength, flexibility, extension and recovery that at least approximate those of a natural ligament, said load bearing member comprising a plurality of fibers of less than 100 microns in diameter. In its attempt to reproduce the mechanical properties of a natural ligament, the prosthetic ligament disclosed in EP-A-0169045 utilizes a composite construction of two load bearing elements, the first of which has a low elastic modulus, and the second of which has a higher elastic modulus. The second load bearing element comprises a plurality of filaments attached to the first load bearing element at several points along its length. The lengths of the filaments between their points of attachment to the first load bearing element are chosen to be greater than the unstressed length of the first element between these points, so that the filaments are unstressed until the load on the first element exceeds a pre-determined value. Accordingly, the ligament disclosed in EP-A-0169045 employs a composite construction of two load bearing elements of differing elastic modulae, which elements must be carefully assembled to provide the required non-linear elastic deformation characteristic. In EP-A-0122744 there is disclosed a prosthetic ligament for permanently, flexibly connecting first and second body members, comprising a nonaugmented load bearing member having a longitudinal axis for permanently spanning the distance between first and second body members for providing a prosthetic ligament having parameters of strength, flexibility, extension and recovery that at least approximate those of a natural ligament, said load bearing member comprising a braid of biocompatible polyolefin yarns, each yarn being composed of a plurality of fibers. The load bearing member is formed of three yarns braided triaxially, one yarn being positioned axially and the other two yarns being arranged symmetrically at equal and opposite angles to the axially orientated yarn. The elasticity of the axially orientated yarn is greater than the elasticity of the angled yarns. According to the present invention there is provided a prosthetic ligament for permanently, flexibly connecting first and second body members comprising a nonaugmented load bearing member having a longitudinal axis for permanently spanning the distance between said first and second body members for providing a prosthetic ligament having parameters of strength, flexibility, extension and recovery that at least approximate those of a natural ligament, said load bearing member comprising a braid made of a plurality of biocompatible polyolefin yarns, each yarn being composed of a plurality of fibers, characterised in that all said fibers are of less than 100 microns in diameter, have the same elasticity and have a tensile strength greater than or equal to about 345 MPa (50,000 psi), and that the yarns of the load bearing member are biaxially braided and are positioned at angles of from about 0 to 55° relative to said longitudinal axis. The load bearing member may define a longitudinal bore therethrough. Means may be disposed within the bore to provide shape for the load bearing member. The shape providing means is preferably made of a biocompatible radiopaque material to permit radiographic visualization of the prosthetic ligament. The shape providing means preferably has a diameter less than equal to the diameter of the bore and is made form a high strength block copolymer containing silicone oil. The prosthetic ligament may further include a tear resistant sheath encasing the load bearing member for preventing abrasion of the fibers. The sheath may be a tube friction fit to the load bearing member or may be molded onto the load bearing member. The sheath is preferably made of a high strength block copolymer containing silicone oil. The load bearing member may be a hollow polypropylene braid which is formed from sixteen four-ply strands. Each of the four-ply strands may have sixty-eight fibers. The polypropylene braid preferably has a weaver angle of between 40° and 48° relative to the longitudinal axis. Polyethylene may also be used to form the load bearing member. Means, such as eyelets, or looped extensions of the load bearing member, for anchoring the prosthetic ligament to the first and second body members may also be provided. There is thus provided a prosthetic ligament having an appropriate deformation characteristic, yet utilising a comparatively simple construction in which all the fibers have the same elasticity and the yarns of the load bearing member are braided biaxially. This is in contrast to the complicated constructions employed in the prior art documents EP-A-0169045 and EP-A-0122744 in particular. The first and second body members to be permanently connected by the prosthetic ligament may be the femur and the tibia. Such a prosthetis can provide a permanent synthetic replacement for a natural ligament which does not depend solely upon the ingrowth of natural tissue to augment the connection between the two body members. Thus, the recipient of the prosthetic ligament can return to a normal range of activity much more quickly than recipient of a prosthetic ligament requiring augmentation with natural tissue. Furthermore, the mechanical parameters of strength, flexibility, extension and recovery provided by such a prosthetic ligament at least approximate those of a natural ligament to such an extent that recipients may resume normal activities. BRIEF DESCRIPTION OF THE DRAWINGS The present invention can better be understood by reference to the drawings in which: FIG. 1 is a view of the preferred embodiment of the prosthetic ligament of the present invention joining the femur and tibia of a recipient. FIG. 2 is a view of a braided load bearing member of the present invention; FIG. 3 is a view of the load bearing member of Figure 2 with an inner core; FIG. 4 is a view of the load bearing member of Figure 2 with an inner core and an outer sheath; and FIG. 5 is a view of one end of the load bearing member of Figure 2 with a looped extension for anchoring the prosthetic ligament to the recipient. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT Figures 1 through 5 illustrate the preferred embodiments of the prosthetic ligament 10 of the present invention. Although the prosthetic ligament 10 is shown as flexibly connecting the femur and tibia, it should be recognized that the prosthetic ligament 10 can be used to connect other skeletal members and, depending upon the means of attachment employed, to support soft tissue organs in place. For purposes of describing the preferred embodiment of the invention, however, the prosthetic ligament 10 is employed to permanently replace the natural cruciate ligament of the human knee. The prosthetic ligament 10 includes primarily a major load bearing member 20. A core 30 and sheath 40 may also be included. The load bearing member 20 is formed from a plurality of biocompatible polyolefin fibers 22 positioned at angles of from about 0 to 55° relative to the longitudinal axis 18 of the load bearing member 20, a range of about 110° in all. The weave angle provides the load deformation characteristics of the prosthetic ligament 10. A weave angle greater than about 55° relative to the longitudinal axis 18 has been found to elongate or stretch too much when the ligament 10 is under stress. Straight fibers will elongate much less. Angled fibers will elongate more and lower the stiffness in the ligament 10. It has been determined that, depending upon the desired stiffness (a natural cruciate ligament has a stiffness of about 180 N/mm), the anatomical location of the prosthetic ligament 10, and the diameter and length of the prosthesis, the weave angle can vary between about 0 and ± 55° , inclusive, relative to the longitudinal axis 18. For example, in one embodiment, when the ligament 10 is made of polypropylene and replaces a cruciate ligament of the knee, the weave angle is between 40° and 48° , inclusive. The preferred weave angle varies for different materials. A preferred embodiment is that of a braided member shown in Figure 2. The braided construction allows utilization of the high-strength fibers as individual units while providing negligible bending resistance. Braiding also allows for the selection of a braiding angle which will result in the optimum load deformation characteristics. The fibers must be made of a biocompatible organic polymer, preferably polyolefins such us high strength polypropylene or ultrahigh molecular weight polyethylene. Kavesh et al. U. S. Patent No. 4,413,110 describes a process for the production of ultrahigh molecular weight polypropylene and polyethylene fibers which have a high tenacity and a high tensile modulus. The commercial embodiments of the polyethylene fibers described in the Kavesh patent, have a tensile strength of about 2,587 MPa (375,000 psi) per individual monofilament. The density of each monofilament is between .5 - 1.5 g/cc, preferably about 0.97. Each monofilament is less than 100 microns in diameter. A plurality of such high strength polyolefin fibers, with each fiber having a tensile strength greater than or equal to about 345 MPa (50,000 psi) and being less than about 100 microns in diameter, woven at the desired angle, provides a high strength load bearing member 10. Numerous fibers add to the life of the ligament 10 because there are numerous surfaces to tolerate the stress and to break in the event of excessive stress before the entire ligament 10 can fail. The fibers may be assembled to form a porous surface on at least a portion of the load bearing member 20. Pore sizes from about 0 to 100 microns enhance fibrous ingrowth. Pour sizes greater than 100 microns enhance bony ingrowth. Fibrous or bony ingrowth will not occur, however, in those places where sheath 40 covers the load bearing member 20. For polypropylene, the braided load bearing member 20 is optimally formed from sixteen four-ply strands. Each four-ply strand has sixty-eight high strength polypropylene fibers. Thus, the preferred embodiment of the braided load bearing member 20 of ligament 10 has 4,352 individual fibers. The unit can carry a minimum load of 1350 N (300 lbs). The prosthetic ligament 10 can be placed in the recipient by any suitable surgical technique. If bone tunnels 16 are used, the load bearing member 20 is preferably encased in a tear resistant sheath 40, as shown in Figure 4, to protect the fibers 22 of load bearing member 20 from abrasion at the entrance to the tunnels 16. The sheath 40 may be a tube having an internal diameter equal to or less than the diameter of the load bearing member 20 which is friction fit onto the load bearing member 20. The sheath 40 must be thick enough to withstand the abrasion to which it will be subjected. In the preferred embodiment for use in replacing a cruciate ligament, the sheath 40 is about 1.59 mm (1/16 inch) thick. The thickness may vary depending upon the desired use of the prosthetic ligament 10. The sheath 40 may also be extruded onto the load bearing member 20. Care should be taken, however, to avoid over heating the load bearing member 20. Excessive heat can damage the fibers 22. Regardless of how the sheath 40 is applied to the load bearing member 20, the sheath 40 must be relatively thick. It has been determined that merely thinly coating the load bearing member 20 is insufficient because the coating shreds and peels over time. While the drawings show ligament 10 as having a circular cross-section, those skilled in the art will recognize that the cross-section can be elliptical or any other shape suitable for the intended end use of the prosthesis. For example, sheath 40 may have an elliptical cross section to match the shape of a natural ligament. The ligament 10 may also be more narrow at its midportion than at its end portions. The core 30 is disposed within a longitudinal bore 28 through load bearing member 20 to provide shape for the load bearing member. The core 30 is preferably made of a biocompatible elastomer to which is added a biocompatible radiopaque material which permits radiographic visualization of the prosthetic ligament 10. The material of choice is made of between 5-25%, inclusive, barium sulfate, by weight, in a high strength block copolymer containing silicone oil. Zirconium oxide, titanium oxide or any other suitable radiopaque material may be used in place of barium sulfate. A suitable elastomer is described in Sterling U. S. Patent No. 4,386,179, and sold commercially under the trademark C-FLEX R . Sheath 40 is preferably also made of C-FLEX R . Prosthetic ligament 10 includes means, such as the braided eyelets 50 or looped extensions of load bearing member 20, 50 metallic eyelets or surgical staples (not shown), for anchoring the ligament 10 to the skeletal members 12, 14. One braided eyelet 50 is connected to each end 24 and 26 of load bearing member 20. Bone screws 52 connect the braided eyelets 50 to the skeletal members 12, 14. Surgical staples may also be used. Mechanical tests of the prosthetic ligament 10 with and without sheath 40 were conducted. All of the ligaments tested included the core 30. One series of tests were performed using a high strength polypropylene braid composed of sixteen 4-ply yarn, each 4-ply yarn having sixty-eight individual fibers. The fibers were braided around a barium sulfateloaded C-FLEX R core. A C-FLEX R sheath 40 was present in some of the ligaments tested. The tests included tensile strength and stress relaxation. All tensile strength testing was performed on a Model TMS Instron. An extension meter with 1.59 mm (1/16 in.) discrete gradiations was used to measure elongation of each ligament 10 tested. The chart below compares test results of the sheathed and unsheathed polypropylene prosthetic ligament 10 having an eliptical cross-sectioned core, the sheathed and unsheathed prosthetic ligament 10 having a circular cross-sectioned core and test results reported by other reseachers* for human anterior cruciate ligaments. The braided load bearing member 20 was found to have a breaking load of 2088 N (464 lb); an apparent ultimate tensile strength of 501 MPa (72,600 psi), a modulus of elasticity of 2,104 MPa (305,000 psi) and a stiffness of 325 Kg/cm (1836 lb/in). Each fiber of the braid had an average ultimate tensile strength of 711 MPa (103,000 psi) and a modulus of elasticity of 2,594 MPa (376,000 psi). A second series of mechanical tests were conducted (see Table II) using a braided load bearing member 20 made of ultrahigh molecular weight polyethylene. Both sheathed and unsheathed ligaments 10 were tested. MANUFACTURE OF FIBERS The polypropylene yarn from which load bearing member 20 is made is obtained by melt spinning the polypropylene fibers in a screw-type extruder. The yarn used to make the braided ligaments employed in the tests discussed above was extruded from a pilot-plant extruder fitted with a spinning head and metering pump, a forced-air quench zone, a spin-finish applicator, twin tale-up godets and a winder. A spinneret having 68 orifices and a pack assembly filled with 20-30 mesh ottawa sand supported by two 40 and two 400-mesh stainless steel screens are fitted into the lower portion of the head. The feed zone of the extruder is preset to a temperature of 306 ± 5° C. The metering zone - upper head is preset to a temperature of 277 ± 5° C and the metering zone - lower head is preset to a temperature of 275 ± 5° C. Polypropylene pellets (MARLEX tm , Type HGN-020-01, Phillips Tetroleum Co.) are fed into the feed hopper of the extruder which is preferably set at a feed rate of about 675-900 g/hr (1.5 to 2.0 lb/h). The feed pressure is preferably set at about 124 to 193 bar (1800 to 2800 psig). The polypropylene fibers are then oriented on a draw winder to increase the strength of the fibers. The fibers are passed from the feed spools through tensioning guides to a feed godet, and then oriented as they are drawn over a heated plate (120 ± 10°C) by the draw godet, which rotates at a faster speed than the feed godet. The delivery godet speed is set at about 1-2 cm/s (5-10 ft/min) and the draw level is adjusted to about 6:1 - 8:1. The oriented fibers are plied on a draw winder where they are passed from four feed spools through tensioning devices and guides to a godet at room temperature and finally to a spool on a constant-tension winder to produce the four-ply yarn. The four-ply yarn is then placed on each end carrier of a 16 end-carrier braider. The yarn is braided around the radiopaque core 30. When desired, the elastomeric sheath 40 is applied to complete the embodiment of ligament 10 having the sheath. Polyethylene fibers may be manufactured in accordance with the teachings of Karesh U. S. Patent No. 4,413,110.

Claims: 1. A prosthetic ligament (10) for permanently, flexibly connecting first and second body members (12,14), comprising a nonaugmented load bearing member (20) having a longitudinal axis (18) for permanently spanning the distance between said first and second body members (12,14) for providing a prosthetic ligament (10) having parameters of strength, flexibility, extension and recovery that at least approximate those of a natural ligament, said load bearing member (20) comprising a braid made of a plurality of biocompatible polyolefin yarns, each yarn being composed of a plurality of fibers (22), characterised in that all said fibers (22) are of less than 100 microns in diameter, have the same elasticity and have a tensile strength greater than or equal to about 345 MPa (50,000 psi), and that the yarns of the load bearing member are biaxially braided and are positioned at angles of from about 0 to 55° relative to said longitudinal axis. 2. A prosthetic ligament as claimed in claim 1, wherein said load bearing member (20) defines a longitudinal bore (28) therethrough and said prosthetic ligament further comprises means (30) disposed within said bore (28) to provide shape for said load bearing member (20). 3. A prosthetic ligament as claimed in Claim 2, wherein said shape providing means (30) is made of a biocompatible radiopaque material to permit radiographic visualization of said prosthetic ligament (10). 4. A prosthetic ligament as claimed in Claim 2 or Claim 3, wherein said shape providing means (30) is a solid core having a diameter less than or equal to the diameter of said bore (28) and is made from a high strength block copolymer containing silicone oil. 5. A prosthetic ligament as claimed in any of the proceeding claims, further comprising a tear resistant sheath (40) encasing said load bearing member (20) for preventing abrasion of said fibers (22). 6. A prosthetic ligament as claimed in Claim 5, wherein said sheath (40) is a tube friction fit to said load bearing member (20). 7. A prosthetic ligament as claimed in Claim 5, wherein said sheath (40) is extruded onto said load bearing member (20). 8. A prosthetic ligament as claimed in Claim 5, wherein said sheath (40) is made of a high strength block copolymer containing silicone oil. 9. A prosthetic ligament as claimed in any of the preceding claims, wherein said braid is formed from high strength polypropylene into sixteen four-ply yarns, each said four-ply yarn having sixty-eight said fibers (22). 10. A prosthetic ligament as claimed in any of the preceding claims, wherein said polyolefin is polyethylene. 11. A prosthetic ligament as claimed in any of Claims 1 to 9, wherein said polyolefin is polypropylene. 12. A prosthetic ligament as claimed in any of the preceding claims, further comprising means (50) for anchoring said prosthetic ligament to said first and second body members (12,14). 13 A prosthetic ligament as claimed in claim 12, wherein said anchoring means (50) are eyelets joined to each end (24,26) of said load bearing member (20). 14. A prosthetic ligament as claimed in claim 13, wherein said eyelets (50) are looped extensions of said load bearing member (20). 15. A prosthetic ligament as claimed in any of the preceding claims having a circular cross-section. 16. A prosthetic ligament as claimed in any of claims 1 to 14 having an eliptical cross-section. 17. A prosthetic ligament as claimed in any of claims 1 to 14 having a cross-section that varies in size such that the size of the midportion of said ligament is less than equal to the size of the ends (24,26) of said ligament. 18. A prosthetic ligament as claimed in any of the preceding claims, wherein at least a portion of said load bearing member (20) forms a porous surface for enhancing fibrous ingrowth. 19. A prosthetic ligament as claimed in any of claims 1 to 17, wherein at least a portion of said load bearing member (20) forms a porous surface for enhancing bony ingrowth.

Inventors: DUNN , RICHARD L., LEWIS , DANNY H., SANDER , THOMAS W., TREHARNE , III, RICHARD W.
Applicants: SMITH & NEPHEW RICHARDS, INC.
Application year: 1987
Main classification: A61F2
IPC codes: A61F2