PROCESS FOR PREPARING STYRENIC POLYMERS

Abstract: This process has been developed for preparing styrenic polymers having isotactic and syndiotactic structures. The catalyst contains as its two major components (a) a solid component contg. titanium and halogen and being insoluble in hydrocarbons and (b) a reaction prod. produced by the reaction of analkylaluminium and water. Component (b) is specified to be the prods. of the contact reaction between trimethylaluminium and water. Typical examples of component (a) are TiCl3, TiBr3, TiL3 cpds. contg. AlCl3, various ethers, esters, ketones, amines, etc. or Titanium halides carried in magnesium cpds. such as MgCl2, Mg(OH)2, Mg(OCOR)2 etc. (where R is an alkyl gp.) The polymerisation reactions are carried out in a hydrocarbon solvent e.g. alipahtic, aromatic, alicyclic hydrocarbons and at a temp. between -30 and 90 deg. C (pref. between 0 and 60 deg. C).

Description: TECHNICAL FIELD The present invention relates to a method for the preparation of a styrene-based polymer and, more particularly, to a method for the preparation of a styrene-based polymer composed, substantially, of an isotactic structure and syndiotactic structure by using a specific catalyst. BACKGROUND ART In general, steric structures of styrene-based polymers such as polystyrene and poly(p-methylstyrene) can be classified as the isotactic structure, syndiotactic structure or atactic structure depending on the steric configuration of the pendant groups relative to the polymeric molecular chain. Styrene-based polymers having the isotactic structure, among them, can be prepared by the polymerization using a so-called Ziegler catalyst and styrene-based polymers having the atactic structure can be prepared by the free-radical polymerization. No prior art method is known, however, for the preparation of a styrene-based polymer having the syndiotactic structure except that the present inventors have recently succeeded in obtaining a styrene-based polymer having a substantially syndiotactic structure (see Japanese Patent Kokai 62-104818). For example, EP-A-0 224 097 (Art 54 (3),(4) EPC) refers to a process for producing styrene polymers having a high syndiotactic structure which comprises polymerizing styrene or styrene derivatives by the use of a catalyst comprising a) a titanium compound, preferably a titanium compound containing halogen, and b) a contact product of an organoaluminum compound and a condensation agent, preferably, a product resulting from modification of trimethylaluminum with water. Such process for polymerizing styrene to a polystyrene having a high syndiotactic structure using a catalyst comprising a) titanium tetrachloride, magnesium chloride and ethylbenzoate and b) methylaluminoxane is also disclosed in EP-A-0 210 615. (Art. 54 (3),(4) EPC) An object of the present invention is to efficiently produce a styrene-based polymer having binary structures of the isotactic structure and syndiotactic structure. DISCLOSURE OF THE INVENTION The present invention provides a method for the preparation of a styrene-based polymer composed, substantially, of the isotactic structure and syndiotactic structure comprises, in carrying out polymerization of a styrene compound in the presence of a catalyst, which contains as the principal ingredients (a) a solid substance containing titanium and a halogen and being insoluble in hydrocarbons, and (b) a reaction product of an alkyl aluminum compound and water, in combination, wherein in the used catalyst the halogen-containing titanium compound is deposited on a magnesium compound selected from the group consisting of MgCl₂, Mg(OR)Cl, Mg(OR)₂, Mg(OH)Cl, Mg(OH)₂ and Mg(OCOR)₂ wherein R is an alkyl group, said magnesium compound containing an electron-donor compound, provided that such electron-donor compound is not ethylbenzoate in the case that the halogen-containing titanium compound is titaniumtetrachloride and the magnesium compound is magnesium chloride. In the method of the present invention, styrenes or styrene derivatives are used as starting materials, and they are polymerized using catalyst composed mainly of the ingredients (a) and (b). The proportion of the ingredients (a) and (b) in the catalyst has influence on the proportion of the isotactic structure and the syndiotactic structure in the resultant styrene-based polymer. BRIEF DESCRIPTION OF THE DRAWING FIGURES 1 to 4 each show a signal assignable to the C₁ carbon of the aromatic ring appearing in the ¹³C-NMR diagram of the polymer obtained in Examples 1 to 4, respectively. FIGURES 5 to 7 each show a signal assignable to the C₁ carbon of the aromatic ring appearing in the ¹³C-NMR diagram of the syndiotactic, isotactic and atactic polystyrenes, respectively, obtained in Comparative Examples 1 to 3, respectively. BEST MODE FOR CARRYING OUT THE INVENTION The ingredient (a) in the catalyst system of the present invention is a solid material containing titanium and a halogen and insoluble in hydrocarbons. The solid material here implied are insoluble in hydrocarbons such as aliphatic, alicyclic and aromatic hydrocarbons at room temperature or at an elevated temperature. Typical examples of such a titanium- and halogen-containing solid material insoluble in such a hydrocarbon solvent include titanium halides such as titanium trichloride TiCl₃, titanium tribromide TiBr₃ and titanium triiodide TiI₃, optionally, containing an aluminum compound such as aluminum chloride AlCl₃ or forming a complex with an electron donor such as ethers, esters, ketones and amines. Further, these titanium halide compounds are supported on magnesium compounds as carriers selected from the group consisting of MgCl₂, Mg(OR)Cl, Mg(OR)₂, Mg(OH)Cl, Mg(OH)₂ and Mg(OCOR)₂, in which R is an alkyl group. The carrier-supported material can be prepared by the treatment of the magnesium compound with a halogen- or alkoxy-containing titanium compound, containing an electron-donor compound such as ethers, esters, ketones and amines. Suitable solid materials can be obtained also by the treatment of a titanium compound such as titanium tetrachloride TiCl₄ with an organic magnesium compound, containing an electron donor compound as mentioned above. The ingredient (b) is a reaction product of an alkyl aluminum and water. Various kinds of alkyl aluminum compounds can be used for the purpose including those represented by the general formula AlR₃, in which R is an alkyl group having 1 to 8 carbon atoms, exemplified by trimethyl aluminum, triethyl aluminum, triisopropyl aluminum and triisobutyl aluminum, of which trimethyl aluminum is preferred. When an alkyl aluminum is reacted with water to give the ingredient (b) of the catalyst system used in the method of the present invention, the resultant product is composed mainly of an alkyl aluminoxane. The reaction of an alkyl aluminum compound and water can be performed in several different ways. For example, the alkyl aluminum compound is dissolved in an organic solvent and the solution is brought into contact with water. Alternatively, the alkyl aluminum compound is added to the polymerization mixture at the start of the polymerization reaction followed by subsequent addition of water to cause the reaction in situ. The water to be reacted with the alkyl aluminum compound may not be free water but water of crystallization contained in a metal salt and the like can be utilized therefor. The reaction product of an alkyl aluminum compound and water can be used alone as the ingredient (b) of the catalyst system used in the inventive method but the ingredient (b) may be a mixture of such a reaction product and the unreacted alkyl aluminum compound without particular drawbacks. The catalyst system used in the inventive method, which is composed mainly of the above described ingredients (a) and (b), may optionally contain other ingredients according to need. Although the optimum proportion of the ingredients (a) and (b) in the catalyst system should adequately be controlled depending on the types of the respective ingredients, kind of the styrene compound to be polymerized, conditions of the polymerization reaction and other factors, the catalyst system should usually contain the ingredients (a) and (b) in such a proportion that the atomic ratio Al/Ti of the aluminum in the ingredient (b) to the titanium in the ingredient (a) is in the range from 1 to 10⁶ or, preferably, from 10 to 10⁴. The atomic ratio Al/Ti in the catalyst system is a determinant factor of the stereospecificity in the styrene-based polymer as the product of the inventive method having influence on the proportion of the isotactic structure and the syndiotactic structure. Namely, the isotactic structure is predominant in the polymer molecules over the syndiotactic structure when the atomic ratio Al/Ti is small in the catalyst system. Increase of the atomic ratio Al/Ti in the catalyst system has an effect to increase the predominance of the syndiotactic structure over the isotactic structure in the polymer. The styrene compound to be polymerized according to the inventive method includes styrene and various kinds of derivatives of styrene exemplified by methyl styrenes, e.g., p-, m- and o-methyl styrenes, dimethyl styrenes, e.g., 2,4-, 2,5-, 3,4- and 3,5-dimethyl styrenes, ethyl styrenes, e.g., p-, m- and o-ethyl styrenes, isopropyl styrenes, e.g., p-, m- and o-isopropyl styrenes, tert-butyl styrenes, e.g., p-, m- and o-tert-butyl styrenes, and other alkyl-substituted styrenes as well as halogen-substituted styrenes, e.g., p-, m- and o-chloro styrenes, p-, m- and o-bromo styrenes and p-, m- and o-fluoro styrenes. The polymerization reaction of the above named styrene compound in the presence of the specific catalyst system according to the inventive method should usually be performed in a hydrocarbon solvent which may be aliphatic, alicyclic or aromatic although the polymerization reaction can proceed even without addition of any solvent. The polymerization temperature is not limited but, from the practical standpoint, it should be in the range from -30 to +90°C, or, preferably, from 0 to +60°C. When the polymerization reaction is performed under the above described conditions, the product is a binary stereo-specific styrene-based polymer composed, substantially, of the isotactic structure and the syndiotactic structure. The relative predominance of the syndiotactic structure to the isotactic structure in the styrene-based polymer obtained according to the inventive method is usually in the range from 95:5 to 5:95 or, mostly, from 90:10 to 10:90 in the pentad determined by analysis of ¹³C-NMR and can be controlled according to desire by adequately selecting the conditions in the polymerization reaction including the atomic ratio Al/Ti in the catalyst system used for the polymerization. In the following, the method of the present invention is illustrated in more detail by way of Examples and Comparative Examples. Preparation Example 1. (1) Preparation of the ingredient (b) The ingredient (b) in the catalyst system was prepared in the following manner. Thus, 47.4 ml (0.492 mole) of trimethyl aluminum and 35.5 g (0.142 mole) of copper sulfate pentahydrate were reacted at 20°C for 24 hours in 200 ml of toluene as the solvent followed by removal of the solid matter to give a toluene solution containing 12.4 g of methyl aluminoxane as a constituent of aluminum compound to serve as the ingredient (b) of the catalyst system. Example 1. (1) Preparation of the ingredient (a) The ingredient (a) in the catalyst system was prepared in the following manner. Thus, 2.0 g (18 m moles) of magnesium diethoxide were dispersed in 100 ml of dehydrated n-heptane contained in a three-necked flask of 200 ml capacity with agitation followed by the addition of 0.53 g (3.5 m moles) of ethyl benzoate at room temperature and then dropwise addition of 34 g (180 m moles) of titanium tetrachloride and the reaction mixture in the flask was heated for 3 hours under reflux to effect the reaction. After completion of the reaction, the supernatant was discarded and the solid matter was repeatedly washed with n-heptane by decantation to give a solid material to serve as the ingredient (a) of the catalyst system. This solid material contained 40 mg of titanium per g of the carrier as determined by the spectrophotometric analysis. (2) Polymerization of styrene Into a reaction vessel of 500 ml capacity were introduced 100 ml of toluene, the above obtained ingredient (a) in an amount of 0.2 m mole calculated as titanium and the methyl aluminoxane as the ingredient (b) prepared in Preparation Example 1 in an amount of 10 m moles calculated as aluminum to form a mixture into which 50 ml of styrene were added at 50°C and the polymerization reaction was performed for 2 hours at this temperature. After completion of the reaction, the product was washed with a mixture of methyl alcohol and hydrochloric acid to decompose and remove the catalyst ingredients followed by drying to give 1.33 g of a polymer. The thus obtained polymer was subjected to extraction with methyl ethyl ketone as the solvent in a Soxhlet extractor to leave 71.6% by weight of the unextracted matter. The table given below summarizes several data relevant to this polymer product. FIGURE 1 in the accompanying drawing shows a signal assignable to the C₁ carbon of the aromatic ring appearing in the ¹³C-NMR diagram of the unextractable fraction of the polymer left after extraction with methyl ethyl ketone. Example 2. Into a reaction vessel of 500 ml capacity were introduced 100 ml of toluene, the ingredient (a) prepared in Example 1 in an amount of 0.02 m mole calculated as titanium and the methyl aluminoxane as the ingredient (b) prepared in Preparation Example 1 in an amount of 10 m moles calculated as aluminum to form a mixture into which 50 ml of styrene were added at 50 °C and the polymerization reaction was performed for 2 hours at this temperature. After completion of the reaction, the product was washed with a mixture of methyl alcohol and hydrochloric acid to decompose and remove the catalyst ingredients followed by drying to give 0.49 g of a polymer. The thus obtained polymer was subjected to extraction with methyl ethyl ketone as the solvent in a Soxhlet extractor to leave 60.0% by weight of the unextracted matter. The table given below summarizes several data relevant to this polymer product. FIGURE 2 in the accompanying drawing shows a signal assignable to the C₁ carbon of the aromatic ring appearing in the ¹³C-NMR diagram of the unextractable fraction of the polymer left after extraction with methyl ethyl ketone. Example 3. Into a reaction vessel of 500 ml capacity were introduced 100 ml of toluene, the ingredient (a) prepared in Example 1 in an amount of 0.02 m mole calculated as titanium and the methyl aluminoxane as the ingredient (b) prepared in Preparation Example 1 in an amount of 20 m moles calculated as aluminum to form a mixture into which 50 ml of styrene were added at 50 °C and the polymerization reaction was performed for 2 hours at this temperature. After completion of the reaction, the product was washed with a mixture of methyl alcohol and hydrochloric acid to decompose and remove the catalyst ingredients followed by drying to give 0.62 g of a polymer. The thus obtained polymer was subjected to extraction with methyl ethyl ketone as the solvent in a Soxhlet extractor to leave 51.9% by weight of the unextracted matter. The table given below summarizes several data relevant to this polymer product. FIGURE 3 in the accompanying drawing shows a signal assignable to the C₁ carbon of the aromatic ring appearing in the ¹³C-NMR diagram of the unextractable fraction of the polymer left after extraction with methyl ethyl ketone. Example 4. (1) Preparation of the ingredient (a) The ingredient (a) of the catalyst system was prepared in the following manner. Thus, 2.0 g (18 m moles) of magnesium diethoxide were dispersed in 30 ml of dehydrated n-heptane contained in a three-necked flask of 200 ml capacity with agitation followed by the addition of 0.42 g (4.4 m moles) of carbon tetrachloride and 0.54 g (1.8 m moles) of titanium tetraisopropoxide at room temperature. The mixture in the flask was heated to 80°C and kept for 2 hours at this temperature to effect the reaction. After completion of the reaction, the supernatant of the reaction mixture was discarded and the solid material was washed twice at room temperature by decantation using 100 ml of dehydrated n-heptane. Thereafter, 30 ml of dehydrated n-heptane and 0.5 g (3.5 m moles) of ethyl benzoate were added to the solid material and the mixture was heated at 98°C for 1 hour to effect the reaction. Further, 34 g (180 m moles) of titanium tetrachloride were added dropwise to the mixture in the flask and the mixture was heated at 98°C for 3 hours. After completion of the reaction, the solid material in the reaction mixture was repeatedly washed with n-heptane by decantation to give a solid material to serve as the ingredient (a) of the catalyst system. This solid material contained 26 mg of titanium per g of the carrier as determined by the spectrophotometric analysis. (2) Polymerization of styrene Into a reaction vessel of 500 ml capacity were introduced 100 ml of toluene, the above obtained ingredient (a) in an amount of 0.02 m mole calculated as titanium and the methyl aluminoxane as the ingredient (b) prepared in Preparation Example 1 in an amount of 10 m moles calculated as aluminum to form a mixture, into which 50 ml of styrene were added at 50°C and the polymerization reaction was performed for 2 hours at this temperature. After completion of the reaction, the product was washed with a mixture of methyl alcohol and hydrochloric acid to decompose and remove the catalyst ingredients followed by drying to give 1.63 g of a polymer. The thus obtained polymer was subjected to extraction with methyl ethyl ketone as the solvent in a Soxhlet extractor to leave 83.8% by weight of the unextracted matter. The table given below summarizes several data relevant to this polymer product. FIGURE 4 in the accompanying drawing shows a signal assignable to the C₁ carbon of the aromatic ring appearing in the ¹³C-NMR diagram of the unextractable fraction of the polymer left after extraction with methyl ethyl ketone. Reference Example 1 (Preparation of a syndiotactic polystyrene) Into a glass vessel of 500 ml capacity equipped with a stirrer were 100 ml of toluene, methyl aluminoxane in an amount of 40 m moles calculated as aluminum atoms and 0.05 m mole of cyclopentadienyl titanium trichloride to form a mixture into which 180 ml of styrene were added at 20°C and the polymerization reaction was performed for 1 hour at this temperature. After then, methyl alcohol was added to the reaction system to stop the polymerization reaction. The product was washed with a mixture of methyl alcohol and hydrochloric acid to decompose and remove the catalyst ingredients followed by drying to give 16.5 g of a polystyrene. This polystyrene had a weight-average molecular weight of 280,000, a number-average molecular weight of 57,000. Further, this polystyrene was subjected to extraction for 4 hours in a Soxhlet extractor with methyl ethyl ketone as the solvent to give 97% by weight of the unextracted matter. This unextracted polystyrene had a melting point of 260°C and a specific gravity of 1.043. Comparative Example 1. FIGURE 5 in the accompanying drawing shows a signal assignable to the C₁ carbon of the aromatic ring appearing in the ¹³C-NMR diagram of this syndiotactic polystyrene prepared in Reference Example 1. Reference Example 2. A hundred ml of styrene was polymerized at 70°C for two hours in a heptane solvent by the use of a catalyst consisting of 1.0 m mole of a titanium catalyst ingredient depositing titanium compound as obtained by reacting 10.0 g of magnesium diethoxide with 50 ml of titanium tetrachloride, and 10 m mole of triethylaluminum, to obtain 48.7 g of isotactic polystyrene having a weight average molecular weight of 1,000,000. This polystyrene was extracted with methyl ethyl ketone in the same manner as in Reference Example 1 to give 96% by weight of the unextracted matter. Comparative Example 2. FIGURE 6 in the accompanying drawing shows a signal assignable to the C₁ carbon of the aromatic ring appearing in the ¹³C-NMR diagram of this isotactic polystyrene prepared in Reference Example 2. Reference Example 3. Atactic polystyrene obtained by radical polymerizing styrene at 0°C by the use of an organic peroxide was extracted with methyl ethyl ketone in the same manner as in Reference Example 1. The whole of the polystyrene was extracted. The polystyrene had a glass transition temperature of 100°C and a specific gravity of 1.05. Comparative Example 3. FIGURE 7 in the accompanying drawing shows a signal assignable to the C₁ carbon of the aromatic ring appearing in the ¹³C-NMR diagram of this atactic polystyrene prepared in Reference Example 3. INDUSTRIAL APPLICABILITY According to the inventive method, a new binary stereo-specific styrene-based polymer composed of the isotactic and syndiotactic structures can be prepared. The styrene-based polymer thus obtained is excellent in heat resistance, moldability and mechanical strength. Polymer mixture obtained by blending a syndiotactic polystyrene and an isotactic polystyrene in the molten state is similar to styrene-based polymer obtained by the inventive method in properties. A great deal of energy is, however, needed to prepare the polymer mixture, and the resultant polymer mixture becomes undesirably degenerate. Therefore, styrene-based polymer obtained by the inventive method has excellent properties which can not result from conventional polystyrenes. The styrene-based polymer is widely and efficiently utilized as a molding material, a structural material and an electric insulation material.

Claims: A method for the preparation of a binary stereospecific styrene-based polymer composed, substantially, of the isotactic structure and the syndiotactic structure by carrying out the polymerization of the styrene compound in the presence of a catalyst, which contains as the principal ingredients (a) a solid substance containing titanium and a halogen and being insoluble in hydrocarbons, and (b) a reaction product of an alkyl aluminum compound and water, in combination, wherein in the used catalyst the halogen-containing titanium compound is deposited on a magnesium compound selected from the group consisting of MgCl₂, Mg(OR)Cl, Mg(OR)₂, Mg(OH)Cl, Mg(OH)₂ and Mg(OCOR)₂ wherein R is an alkyl group, said magnesium compound containing an electron-donor compound, provided that such electron-donor compound is not ethylbenzoate in the case that the halogen-containing titanium compound is titaniumtetrachloride and the magnesium compound is magnesium chloride. The method as claimed in claim 1 wherein the ingredient (b) of the catalyst is a product formed by contacting trimethyl aluminum with water. The method as claimed in claim 1 or 2, wherein the halogen-containing titanium compound is titanium tetrachloride, and the magnesium compound is magnesium diethoxide.

Inventors: ISHIHARA, NOBUHIDE IDEMITSU KOSAN COMPANY LIMITED, KURAMOTO, MASAHIKO IDEMITSU KOSAN COMPANY LIMITED, NAKANO, AKIKAZU IDEMITSU KOSAN COMPANY LIMITED
Applicants: IDEMITSU KOSAN COMPANY LIMITED
Application year: 1987
Main classification: C08F12
IPC codes: C08F4, C08F12