Modified acrylic polymers

Abstract: An extrudable acrylic composition including an inter­ polymer produced by the polymerisation of methyl meth­ acrylate monomer, an N-substituted maleimide monomer, an alkyl acrylate monomer and a di-functional reactive mon­ omer.

Description: This invention relates to improved acrylic resins. In one of its more specific aspects, this invention relates to the modification of alkyl methacrylate homo- and copolymers by the introduction thereinto of an interpolymer formed by the polymerization of methyl methacrylate monomer, an N-substituted maleimide monomer, an alkyl acrylate monomer, and a difunctional reactive monomer. Alkyl methacrylate polymers, especially poly(methyl methacrylate), which possess the distinctive property of being transparent, are well known. When alkyl methacrylate polymers are fabricated into cast sheets or extruded rods, the fabricated products while having the ability to transfer light usually possess poor impact and heat resistance. In order to eliminate at least a portion of these difficulties, it is customary to incorporate into an alkyl methacrylate polymer an alkyl acrylate polymeric impact modifier. Numerous patents address the preparation and use of alkyl acrylate polymers as impact modifiers for alkyl methacrylate polymers, for example U.S. Pat. Nos. 3,502,745; 3,661,994 3,676,404; 4,121,016; 4,129,614; 4,217,424; 4,246,374, and 4,473,679. And, U.S. Pat. Nos. 3,655,826 and 3,681,475 teach impact modification of thermoplastic acrylic polymers, specifically poly(methyl methacrylate) with alkyl acrylate polymers. According to this invention, there is provided a composition comprising an interpolymer produced by the polymerization of methyl methacrylate monomer, at least one N-substituted maleimide monomer, at least one alkyl acrylate monomer, and a difunctional reactive monomer. Also, according to this invention, there is provided a method of producing a thermoplastic composition, which comprises incorporating into an alkyl methacrylate polymer matrix an interpolymer comprising the polymerization product of methyl methacrylate monomer, an N-substituted maleimide monomer, an alkyl acrylate monomer, and a difunctional reactive monomer, the interpolymer being present in an amount sufficient to improve at least one property of the extruded alkyl methacrylate polymer. The alkyl methacrylate polymers, in themselves, are well known in the art as are the methods of preparing them. The term "alkyl methacrylate polymer", as used herein means alkyl methacrylate homo- and copolymers. The alkyl methacrylate polymers employable in this invention are produced using any suitable prior art methods and include poly(methyl methacrylate), poly(methyl methacrylate-co-styrene), poly(methyl methacrylate-co-N-substituted maleimide) e.g. poly(methyl methacrylate-co-N-phenylmaleimide), poly(methyl methacrylate-co- α-methyl-styrene), poly(methyl methacrylate-co-maleic anhydride), polyglutarimide, and the like and their mixtures. The interpolymer modifier of this invention is an interpolymer formed by polymerisation of methyl methacrylate monomer, at least one N-substituted maleimide monomer, at least one alkyl acrylate monomer, and a difunctional reactive monomer wherein the reactive groups are either acrylate or methacrylate. The interpolymer modifier can be produced using a suitable method of polymerization ; for example by emulsion polymerization. The polymerization reaction mixture will contain from 15 to 60 weight % methyl methacrylate monomer, from 5 to 20 weight % N-substituted maleimide monomer, from 20 to 80 weight % alkyl acrylate monomer, and from 0.0001 to 1 part per hundred parts of total monomer of a difunctional reactive monomer. Preferably the polymerization reaction mixture will contain from 30 to 45 weight % methyl methacrylate monomer, from 10 to 15 weight % N-substituted maleimide monomer, from 40 to 60 weight % alkyl acrylate monomer and from 0.001 to 0.01 part per hundred parts of total monomer of a difunctional reactive monomer. The N-substituted maleimide monomer is selected from N-alkylmaleimides such as N-methylmaleimide and N-ethylmaleimide or N-arylmaleimides such as N-phenylmaleimide, N-(2-chloro) phenylmaleimide, N-(4-methyl)phenylmaleimide, N-(4-cyano) phenylmaleimide or N-(2,4,6-tribromo)phenylmaleimide, and their mixtures. The preferred N-substituted maleimide monomer is N-phenylmaleimide. The alkyl acrylate monomer may be selected from, for example methyl acrylate, ethyl acrylate, propyl acrylate, n-butyl acrylate, hexyl acrylate, dodecyl acrylate, 2-ethylhexyl acrylate and 2-(2-ethoxyethoxy)ethyl acrylate, and their mixtures. The preferred alkyl acrylate is n-butyl acrylate. Representative examples of the difunctional reactive monomers suitable for uses to produce the interpolymer of this invention include, but are not limited to, tetraethyleneglycol diacrylate, tetraethyleneglycol dimethacrylate, trimethylolpropane di- or triacrylate, triallyl isocyanurate and their mixtures. Tetraethyleneglycol diacrylate is preferred. The interpolymer modifier of this invention consists of a methyl methacrylate/N-substituted maleimide copolymer and an alkyl acrylate homopolymer which are chemically and/or physically linked as a result of the presence of the difunctional reactive monomer during the free radical polymerization The methyl methacrylate/N-substituted maleimide copolymer of the interpolymer preferably has a number average molecular weight (Mn) as measured by gel permeation chromatography relative to polystyrene standards of from 150,000 to 450,000; preferably from 200,000 to 400,000. The alkyl acrylate homopolymer portion of the interpolymer should have a number average molecular weight (Mn) as measured by gel permeation chromatography relative to polystyrene of from 150,000 to 500,000; preferably from 200,000 to 400,000. The glass transition temperature of the methyl methacrylate/N-substituted maleimide copolymer of the interpolymer as measured by differential scanning calorimetry (DSC) is preferably greater than 120°C and more preferably greater than 140°C. The glass transition temperature of the alkyl acrylate homopolymer as measured by DSC is preferably less than 0°C and more preferably less than -20°C. The alkyl methacrylate homo- and copolymer matrices for which the interpolymer serves as both a heat distortion temperature modifier and an impact modifier are those alkyl methacrylate homo- and copolymers which (1) exhibit thermodynamic miscibility with the methyl methacrylate/N-substituted maleimide copolymer portion of the interpolymer and (2) are immiscible with the alkyl acrylate homopolymer portion of the interpolymer. Thermodynamic miscibility between two polymers exists if a blend of the two polymers results in a single phase characterized by a single glass transition temperature value which is intermediate between the glass transition temperatures of the two respective polymers. Thus, a blend of the interpolymer of this invention with an alkyl methacrylate homo- or copolymer matrix will result in a blend which exhibits two glass transition temperatures , one characteristic of the alkyl acrylate homopolymer of the interpolymer which is immiscible with the alkyl methacrylate homo- or copolymer matrix and the second characteristic of the single phase formed between the methyl methacrylate/N-substituted maleimide copolymer of tile interpolymer and the alkyl methacrylate homo- or copolymer matrix as a result of the thermodynamic miscibility. The modified acrylic polymers according to this invention can be prepared using any suitable conventional method of combining polymers such as melt mixing, as taught in the Examples which follow. The interpolymer will be incorporated into the alkyl methacrylate polymer to provide a polymer blend which contains in weight percent, from 60 to 95, preferrably from about 70 to about 90 alkyl methacrylate polymer and from 5 to 40, preferrably from about 10 to about 30 interpolymer. The interpolymer modifier described above when incorporated into an alkyl methacrylate homo- or copolymer matrix results in a transparent thermoplastic composition useful for glazing applications, lighting applications e.g. automobile taillights and other optical applications requiring toughness, high heat and transparency. The following examples illustrate the methods involved in the preparation of the interpolymer modifier of the invention and the use of the interpolymer modifier as a dual impact modifier/heat distortion modifier for alkyl methacrylate homo- and copolymers. EXAMPLE I This example demonstrates the preparation of an interpolymer modifier of this invention and its incorporation into a poly(methyl methacrylate) matrix. A 1-liter resin kettle was charged with about 300 grams of water, about 2.6 grams of sodium dodecylbenzene sulfonate, about 100 grams of n-butyl acrylate monomer, about 75 grams of methyl methacrylate monomer, about 25 grams of N-phenylmaleimide, about 0.21 gram of tetraethyleneglycol diacrylate, about 80 milliliters of a 2% aqueous potassium persulfate solution and about 2 milliliters of a 0.1% aqueous sodium bisulfite solution. The emulsion reaction was stirred at about 300 rpm at a reaction temperature of about 63.5°C for about four hours. The resulting interpolymer was recovered as a powder by coagulation of the emulsion with a saturated calcium chloride solution. The interpolymer exhibited two glass transition temperatures by DSC: -32°C and 146°C. The nitrogen content of the interpolymer was measured to he 1.0 weight percent which corresponded to a 12.3 weight percent N-phenylmaleimide content. The yield of interpolymer was 195 grams (97%). The resulting interpolymer was blended with poly(methyl methacrylate) (PMMA) [PLEXIGLAS® V-052, commercially available from Rohm & Haas] as follows. In a Brabender mixing apparatus a PMMA/interpolymer blend (80:20 wt. %) was prepared at 220°C for five minutes at 63 rpm. The resulting blend was removed from the mixing head and test specimens were compression molded to evaluate notched Izod impact strength and deflection temperature under load (in accordance with ASTM procedures D-256 and D-648, respectively). A comparison of the data in Table I demonstrates the enhanced physical properties of the PMMA/interpolymer blend of the invention as compared to the base PMMA resin. PMMA (wt. %) 100 80 Interpolymer of Example 1 (wt. %) 0 20 Tg (C°) 105 112 DTUL °C(°F) 77(171) 82(179) Notched Izod J/M (ft-lbs/in) 26.5(0.5) 137.8(2.6) % Transmittance Visible Light 92 86 EXAMPLE 2 This example also demonstrates the preparation of an interpolymer of this invention and its incorporation into a poly(methyl methacrylate) matrix. A 1-liter resin kettle was charged with about 300 grams of water, about 2.6 grams of sodium dodecylbenzene sulfonate, about 75 grams of n-butyl acrylate monomer, about 25 grams of ethyl acrylate monomer, about 75 grams of methyl methacrylate monomer, about 25 grams of N-phenylmaleimide monomer, about 0.21 gram of tetraethyleneglycol diacrylate, about 80 milliliters of a 2% aqueous potassium persulfate solution and about 2 milliliters of a 0.1% aqueous sodium bisulfite solution. The emulsion reaction was stirred at about 300 rpm at a reaction temperature of 63.5°C for about four hours. The resulting interpolymer was recovered as a powder by coagulation of the emulsion with a saturated calcium chloride solution. The interpolymer exhibits two glass transition temperatures by DSC: -27°C and 147°C. The nitrogen content of the interpolymer was 1.1 weight percent which corresponded to a 13.5 weight percent N-phenylmaleimide content. The yield of interpolymer was 194 grams (96.5%). The resulting interpolymer was blended with PLEXIGLAS® V-052 resin in a Brabender mixing apparatus at 220°C for five minutes at 63 rpm. The resulting PMMA/ interpolymer blend (80:20 wt %) was removed from the mixing head and test specimens were compression molded for physical property evaluation. A comparison of the data in Table 2 demonstrates the enhanced physical properties of the PMMA/ interpolymer blend of the invention as compared to the base PMMA resin. PMMA (wt. %) 100 80 Interpolymer of Example 2 (wt. %) 0 20 Tg (°C) 105 111.5 DTUL °C(°F) 77(171) 82(179) Notched Izod J/M (ft-lbs/in) 26.5(0.5) 121.9(2.3) % Transmittance Visible Light 92 87 EXAMPLE 3 This example also demonstrates the preparation of an interpolymer of this invention and its incorporation into a poly(methyl methacrylate) matrix. A 1-liter resin kettle was charged with about 300 grams of water, about 2.6 grams of sodium dodecylbenzene sulfonate, about 75 grams of n-butyl acrylate monomer, about 25 grams of methyl acrylate monomer, about 75 grams of methyl methacrylate monomer, about 25 grams of N-phenylmaleimide, about 0.21 gram of tetraethyleneglycol diacrylate, about 80 milliliters of a 2% aqueous potassium persulfate solution and about 2 milliliters of a 0.1% aqueous sodium bisulfite solution. The emulsion reaction was stirred at about 300 rpm at a reaction temperature of 63.5°C for four hours. The resulting interpolymer was recovered as a powder by coagulation of the emulsion with a saturated calcium chloride solution. The interpolymer exhibits two glass transition temperatures by DSC: -21°C and 145°C. The nitrogen content of the interpolymer was 1.0 weight percent which corresponded to a 12.3 weight percent N-phenylmaleimide content. The yield of interpolymer was 196 grans (97%). The resulting interpolymer was blended with PLEXIGLAS® V-052 in a Brabender mixing apparatus at 220°C for five minutes at 63 rpm. The resulting PMMA/interpolymer blend (80:20 wt. %) was removed from the mixing head and test specimens were compression molded. The molded specimens exhibited the physical properties shown in Table 3 as compared to the base PMMA resin. PMMA (wt. %) 100 80 Interpolymer of Example 3 (wt. %) 0 20 Tg (°C) 105 112.5 DTUL °C(°F) 77(171) 82(180) Notched Izod J/M(ft-lbs/in) 26.5(0.5) 132.5(2.5) % Transmittance Visible Light 92 89 EXAMPLE 4 This example also demonstrates the preparation of an interpolymer of this invention and its incorporation into a poly(methyl methacrylate) matrix. A 1-liter resin kettle was charged with about 300 grams of water, about 2.6 grams of sodium dodecylbenzene sulfonate, about 75 grams of n-butyl acrylate, about 25 grams of 2-(ethoxy-ethoxy)ethyl acrylate, about 75 grams of methyl methacrylate monomer, about 25 grams of N-phenylmaleimide, about 0.21 grams of tetraethyleneglycol diacrylate, about 80 milliliters of a 2% aqueous potassium persulfate solution and about 2 milliliters of a 0.1% aqueous sodium bisulfite solution. The emulsion reaction was stirred at about 300 rpm at a reaction temperature of about 63.5°C for four hours. The resulting interpolymer was recovered as a powder by coagulation of the emulsion with a saturated calcium chloride solution. The interpolymer exhibits two glass transition temperatures by DSC: of -38°C and 147°C. The nitrogen content of the interpolymer was 1.1 weight percent which corresponded to a 13.5 weight percent N-phenylmaleimide content. The yield of interpolymer was 195 grams (97%). The resulting interpolymer was blended with PLEXIGLAS ® V-052, in a Brabender mixing apparatus at 220°C for five minutes at 63 rpm. The resulting PPMA/ interpolymer (80:20 wt. %) blend was removed from the mixing head and specimens were compression molded to evaluate notched Izod impact strength and deflection temperature under load. A comparison of the data in Table 4 demonstrates the physical properties of the invention as compared to the base PMMA resin. PMMA (wt. %) 100 80 Interpolymer of Example 4 (wt. %) 0 20 Tg (°C) 105 113 DTUL °C(°F) 77(171) 83(181) Notched Izod J/M(ft-lbs/in) 26.5(0.5) 169.6(3.2) % Transmittance Visible Light 92 88 EXAMPLE 5 This example serves to compare the interpolymer modifiers of this invention with a commercially available impact modified poly(methyl methacrylate) resin, PLEXIGLAS® DR resin commercially available from Rohm & Haas. To prepare the compositions of this invention PLEXIGLAS® V-052 and the interpolymers were physically mixed and extruded into pellets. The PLEXIGLAS® DR and the PMMA/interpolymer blends of this invention were separately injection molded into test specimens at a pyromelt temperature of 215°c. Table 5 presents the physical property comparison between the commercially available impact modified PMMA and the PMMA/ interpolymer modifier compositions of this invention. PLEXIGLAS® DR (wt. %) 100 0 0 PLEXIGLAS® V-052 (wt. %) 0 80 80 Interpolymer of Example 1 (wt. %) 0 20 0 Interpolymer of Example 4 (wt. %) 0 0 20 Tg (°C) 104 112 113 DTUL °C(°F) 73(163) 82(179) 83(181) Notched Izod J/M(ft-lbs/in) 121.9(2.3) 201.4(3.8) 238.5(4.5) GFWI Nm(in-lbs) 5.4(48) 9.9(88) 13.3(118) Elongation (%) 31 57 64 Flexural Modulus MPa (lbs/sq.in) 1868(270,900) 2366(343,100) 2389(346,500) The data of Table 5 shows the compositions of the invention to possess enhanced physical properties as compared to a commercially available impact modified PMMA. EXAMPLE 6 This example demonstrates the use of the interpolymers described by this invention as impact modifiers for an alkyl methacrylate copolymer matrix resin. A poly(methyl methacrylate-co-N-phenylmaleimide) copolymer (76/24 wt. %) was blended with the interpolymer prepared according to the procedure described in Example 4 in a Brabender Mixing aparatus at 240°C for five minutes at 63 rpm. Table 6 shows the impact strengths for various MMA/N-PMI:interpolymer compositions. MMA/N-PMI (wt. %) 100 80 60 Interpolymer of Example 4 (wt. %) 0 20 40 Tg (°C) 144 144 145 Notched Izod J/M(ft-lbs/in) 37.1(0.7) 95.4(1.8) 180.2(3.4) % Transmittance Visible Light 86 80 79 The data of Table 6 show the interpolymers of the invention serve to enhance the impact properties of a poly(methyl methacrylate-co-N-phenylmaleimide) copolymer. It will be evident from the foregoing that various modifications can be made to the invention. Such, however, are considered as being within the scope of this invention.

Claims: A composition comprising an interpolymer consisting of a methyl methacrylate/N-substituted maleimide copolymer and an alkyl acrylate homopolymer linked through at least one difunctional reactive monomer and in which said N-substituted maleimide is selected from N-alkylmaleimides and N-arylmaleimides; said interpolymer being obtained from a polymerisable composition comprising in weight percent from 15 to 60 methyl methacrylate, from 5 to 20 of at least one N-substituted maleimide, from 20 to 80 of at least one alkyl acrylate, and from 0.0001 to 1 part per 100 parts of total monomer of said difunctional reactive monomer. A composition as claimed in claim 1 in which said difunctional reactive monomer bears acrylate or methacrylate reactive groups. A composition as claimed in claim 1 or claim 2 in which said methyl methacrylate/N-substituted maleimide copolymer has a number average molecular weight (Mn) as measured by gel permeation chromatography relative to polystyrene standards of from 150,000 to 450,000. A composition as claimed in any one of claims 1 to 3 in which said alkyl acrylate homopolymer has a number average molecular weight (Mn) as measured by gel permeation chromatography relative to polystyrene standards of from 150,000 to 500,000. A composition as claimed in any one of claims 1 to 4 characterised in that said methyl methacrylate/N-substituted maleimide copolymer has a glass transition temperature as measured by differential scanning calorimetry of greater than 120°C. A composition as claimed in any one of claims 1 to 5 characterised in that said alkyl acrylate homopolymer has a glass transition temperature as measured by differential scanning calorimetry of less than 0°C. A composition comprising, in weight percent, 60 to 95 of alkyl methacrylate homo- or copolymer matrix resin and 5 to 40 of interpolymer as specified in any one of claims 1 to 6, and wherein said methyl methacrylate/N-substituted maleimide copolymer and said alkyl methacrylate homo- or copolymer matrix resin are thermodynamically miscible with one another, and said alkyl acrylate homopolymer and said alkyl methacrylate homo- or copolymer matrix resin are immiscible. A method of producing a thermoplastic composition which comprises incorporating into an alkyl methacrylate homo- or copolymer matrix resin an interpolymer as specified in any one of claims 1 to 6, the interpolymer being present in an amount sufficient to improve at least one property of the extruded alkyl methacrylate polymer.

Inventors: DEAN BARRY D, DEAN, BARRY D.
Applicants: ARCO CHEM TECH, ARCO CHEMICAL TECHNOLOGY, L.P.
Application year: 1987
Main classification: C08L33
IPC codes: C08F220, C08L33, C08F22, C08F222