RUBBER COMPOSITIONS CONTAINING AMINE DERIVATIVES OF 1,3,4,-THIADIAZOLE

Abstract: A process is disclosed for stabilization of natural rubber against oxidative degradation in the presence of copper by incorporating therein diarylamine derivatives of 3-hydroxymethyl-5-hydroxymethylthio-1,3-4-thiadiazoli­ dine-2-thione and stabilized rubber compositions thereof.

Description: This invention relates to bifunctional additives for rubber compositions and their use in the stabilization of said compositions. More particularly, the invention relates to rubber compositions that possess a high degree of resistance to the detrimental effects of oxidative aging and metal corrosion over prolonged periods of time. Essentially all types of rubber are known to be susceptible to deterioration resulting from prolonged exposure to atmospheric oxygen. The major cause of deterioration is the attack of oxygen on the olefinic unsaturation bonds contained in rubber. There is a general agreement that the presence of metals, particularly copper has an overall enhancing effect on the oxidizability of rubber. Although antioxidants have a beneficial effect on the rate of oxidative deterioration, the protective effect is relatively less if metal impurities are present in the rubber composition or the rubber is in contact with metals as, for example, in wire and cable applications. Depending on the grade and type of rubber, antioxidants are generally selected with regard to the severity of processing and service of the finished article. For added protection, a copper inhibitor is incorporated into the composition. Among the known antioxidants, arylamines are widely used to protect rubber against oxidative effects. However, arylamine-type antioxidants impart staining and discoloration of the vulcanized rubber. The demand for light colored heavy-duty rubber articles such as white wall tires, fixtures and wires has led to a search for nonstaining, nondiscoloring antioxidants with greater control over metal corrosion. It has been now discovered that certain diarylamine derivatives of 1,3,4-thiadiazole prevent the detrimental effect of both oxygen and copper on the rubber composition. Furthermore, the bifunctional additives are nonstaining and may be used in black as well as light colored rubber articles. An aspect of the invention is a rubber composition having incorporated therein a 1,3,4-thiadiazole compound selected from the group consisting of compounds of the structural formula wherein R represents 2,2,4-trimethyl-2,3-dihydroquinolinyl, N-phenothiazinyl,diphenylamino and dialkylphenylamino group having 4 to 9 carbons in the alkyl chain. Another aspect of the invention is a method of protecting rubber compositions against oxidative deterioration and copper corrosion by incorporating therein the above described 1,3,4-thiadiazole compounds. DETAILED DESCRIPTION OF THE INVENTION The additives of the invention may be prepared by reacting a diarylamine with 3-hydroxymethyl-5-hydroxymethylthio-1,3,4-thiadiazolidine-2-thione according to the following reaction scheme. The R′ groups represent alkyl and aryl groups which together with the amine nitrogen form R groups defined herein above. Alternately, the compounds may be prepared by reacting the arylamine with 2,5-dimercapto-1,3,4-thiadiazole and formaldehyde in the presence of an acid and hydrochloric acid. The additive of the invention may be incorporated into rubber in the amount of 0.2 to 5 parts per hundred parts rubber (PHR). The effective amount will depend to some extent on the type and grade of rubber used and on the severity of the deteriorating conditions to which the finished article will be exposed. Rubber that can be protected with the bifunctional additive includes natural rubber such as balata and gutta percha in various forms. The rubber may be of the black variety containing carbon black fillers and of light variety containing inorganic and mineral fillers such as, among others, titanium dioxide, calcium carbonate, silicate minerals, particularly kaolin clay, whiting, talc and wollastonite. Other compounding ingredients may be added as necessary. The following compounding ingredients, among others, are applicable: accelerators, plasticizers, peptizers, lubricants and processing aids. Unless otherwise stated, all parts and percentages in the specification and claims are by weight EXAMPLE I A reactor was charged with 30g (0.20 moles) of 2,5-dimercapto-1,3,4-thiadiazole, 32.4g (0.40 moles) of formaldehyde (37% aqueous solution) and 250 ml toluene. The mixture was stirred vigorously for 15 minutes. An exothermic reaction occured at 35°C. Then 77.6g (0.40 moles) of diphenylamine were added and the reaction mixture was heated to reflux. About 28.0g water was collected by azeotropic distillation in about 1½ to 2 hours, while the reaction temperature reached 112°C. After cooling, toluene was removed with a rotary evaporator giving a brown hard resin having a softening point of 40°C. EXAMPLE II A reactor was charged with 42.0g (0.20 moles) of 3-hydroxymethyl-5-hydroxymethylthio-1,3,4-thiadiazolidine-2-thione, 77.6g (0.40 moles) diphenylamine and 250 ml toluene. The reaction mixture was heated to reflux with stirring. About 28.0g water was collected by azeotropic distillation in about 1½ to 2 hours. After cooling, toluene was removed with a rotary evaporator. The yield of the product, 3-diphenylaminomethyl-5-diphenylaminomethylthio-1,3,4-thiadiazolidine-2-thione was 102g. EXAMPLE III A 500 ml round bottom flask equipped with a stirrer, thermometer and condenser was charged with 32.0g (0.20 moles) of 2,5-dimercapto-1,3,4-thiadiazole, 32.5g (0.40 moles) of formaldehyde (37% aqueous solution) and 150 ml toluene. After stirring for 15 minutes, 68.8g (0.40 moles) of 2,2,4-trimethyldihydroquinoline were added to the mixture and heated to reflux. About 28.0g water was collected by azeotropic distillation. The reaction mixture was stripped of volatiles with a rotary evaporator. The yield was 69.0g of brittle, dark brown resin, 3-(2,2,4-trimethyldihydroquinolinylmethyl)-5-(2,2,4-trimethyldihydroquinolinylmethylthio)-1,3,4-thiadiazolidine-2-thione. EXAMPLE IV Test specimens were prepared by compounding natural rubber with additives of the invention and other conventional compounding ingredients. The samples were press cured for 15 minutes at 153°C. After 4 day aging in oxygen bomb at 100°C, the elongation and tensile strength were determined according to ASTM D-412 method. The physical data compiled in Table I show that the specimens containing the compounds of the invention retained the desired properties under oxidative conditions. EXAMPLE V Test specimens were prepared by compounding natural rubber with additives of the invention and other conventional compounding ingredients. Copper oleate was added as a controlled impurity. The specimens were cured and after aging at 80°C for four days, tested according to the methods described in Example III. The data compiled in Table II show that the specimens retained the desired physical properties even in the presence of copper under oxidative conditions.

Claims: A stabilized composition comprising natural rubber and 0.2 to 5 parts per hundred parts rubber of a 1,3,4-thiadiazole compound selected from the group consisting of compounds of the structural formula wherein R represents 2,2,4-trimethyl-2,3-dihydroquinolinyl, N-phenothiazinyl, diphenylamino and dialkylphenylamino group having 4 to 9 carbons in the alkyl chain. A composition of claim 1 wherein the 1,3,4-thiadiazole compound is 3-diphenylaminomethyl-5-diphenylaminomethylthio-1,3,4-thiadiazolidine-2-thione. A process for stabilizing rubber against oxidative degradation in the presence of metals which comprises incorporation in the rubber 0.2 to 5 parts per hundred parts rubber of a 1,3,4-thiadiazole compound selected from the group consisting of compounds of the structural formula wherein R represents 2,2,4-trimethyl-2,3-dihydroquinolinyl, N-phenothiazinyl,diphenylamino and dialkylphenylamino groups having 4 to 9 carbons in the alkyl chain.

Inventors: DOE, LESTER A., JR.
Applicants: R.T. VANDERBILT COMPANY, INC.
Application year: 1987
Main classification: C08K5
IPC codes: C08L7, C07D285, C08K5