CATIONIC ASPHALT EMULSIONS

Abstract: The setting time of a cationic emulsion of bitumen, asphalt, coal tar or a mixture thereof is shortened by incorporating into such emulsion at least 0.001 parts by weight per 100 parts by dry weight of said emulsion of a polycarboxylic acid.

Description: The present invention relates to the modification of cationic emulsions of asphalt, bitumen, coal tar or a mixture thereof. As used in this specification, asphalt is intended to include naturally occurring asphalts such as Trinidad Lake asphalts and synthetic asphalts produced from the refining of crude oil. Emulsions of asphalt, bitumen, coal tar or a mixture thereof have a wide numbers of applications, including but not limited to the production of aggregate pavement. One of the problems encountered with emulsions of asphalt, bitumen, coal tar or a mixture thereof is the length of time it takes for the emulsion to start to set and the time for the emulsion to dry in admixture with an aggregate material suitable for the production of aggregate pavement. This is extremely expensive when traffic must be kept off a lane of a highway for a lengthy period of time. The properties of asphalt, bitumen, coal tar or a mixture thereof may be improved by the incorporation of a polymer. This improves adhesion, ductility, tensile strength, and cold temperature properties of the asphalt, bitumen, coal tar or a mixture thereof. This may be done by melting the asphalt bitumen, coal tar or mixture thereof and adding the polymer. This process is energy intensive. The addition of polymer to asphalt, bitumen, coal tar or a mixture thereof may be accomplished by mixing emulsions of such material with a latex of the polymer. While this process is less energy intensive, it further accentuates the delay in setting times and drying times of emulsions of asphalt, bitumen, coal tar or a mixture thereof in admixture with an aggregate material suitable for the production of aggregate pavement. One approach to enhance the drying time of anionic asphalt emulsions has been to include a silicofluoride gelling agent into the system. Examples of this approach include CA 96: 163961k of E.P. 45,619 published Feb. 10, 1982 in the name of the British Petroleum Co. Ltd.; CA 83: 196173g of Belgium Patent 821,210 published Feb. 17, 1975 in the name of Kamenouhelve Poly Oborove Rzeditelstvi; and CA 81:171549n of German Offen. 2,363,085 published July 4, 1974 in the name of Rambelli Giacinto. Silicofluorides are time dependent gelling agents. Thus, the silicofluoride is mixed with the asphalt emulsion shortly before the asphalt emulsion is to set. This necessitates a two component application system or use of the system immediately after adding the gelling agent. One approach is to add one or more thickening agents to asphalt emulsions. This approach is taught by U.S. Patent 4,492,781 to Duzak et al. (Hercules Inc.) which discloses a composition of an cationic emulsion of asphalt/rubber/acrylic copolymer (100-10:0-90:0-70), a water soluble polymer, reinforcing component, aggregate, a curing and thickening agent and a rosin ester. The acrylic polymer disclosed in the Hercules patent is a copolymer of ethylene and acrylic acid. The water soluble polymer described as RETEN is an acrylamide copolymer. Neither of these polymer types is the poly C₃₋₄ ethylenically unsaturated carboxylic acid required in the present invention. Additionally, such polymer types do not improve the setting or drying time of emulsions of asphalt, bitumen, coal tar or a mixture thereof which have been modified with an aqueous emulsion of a polymer in admixture with an aggregate material suitable for the production of aggregate pavement. None of the prior art teaches that a cationic emulsion of asphalt, bitumen, coal tar, or a mixture thereof may in admixture with an aggregate material suitable for the production of aggregate pavement be set and dried at a faster rate by including relatively minor amounts of an acidic solution of a cationic emulsifier and a polymer consisting of acrylic acid or methacrylic acid a mixture thereof or salts thereof. As used in this specification the term set means the point at which aggregate in contact with an aqueous emulsion of bitumen, asphalt, coal tar or a mixture thereof is first resistant to movement. Setting time means the time it takes from initial contact with aggregate for an emulsion of asphalt, bitumen, coal tar or a mixture thereof to set. The present invention provides a method to reduce the setting time of a cationic emulsion of bitumen, asphalt, coal tar or a mixture thereof in admixture with an aggregate material suitable for the production of aggregate pavement which comprises incorporating into said emulsion an effective amount of an acidic solution of a cationic emulsifier and a sufficient amount of a polymer consisting of acrylic acid or methacrylic acid or a mixture thereof or salts thereof. Preferably the polymer consisting of acrylic acid or methacrylic acid or a mixture thereof or salts thereof is used in an amount sufficient to provide at least about 0.001 parts by dry weight of said polymer per 100 parts by dry weight of said cationic emulsion of bitumen, asphalt, coal tar or a mixtures thereof. The present invention also provides a composition comprising: 100 parts by dry weight of a cationic emulsion of bitumen, asphalt, coal tar or a mixtures thereof; and an acidic solution of a cationic emulsifier and a polymer consisting of acrylic acid or methacrylic acid or a mixture thereof or salts thereof, in an amount of from 0,001 to 1.0 part by dry weight of said polymer. The cationic emulsions of asphalt, bitumen, coal tar or a mixture thereof may be purchased commercially or prepared in a high shear colloid mill. The preparation of such emulsions per se is not intended to form part of the present invention. The setting time should be less than about 40, preferably less than 30 minutes. If the cationic emulsion of asphalt, bitumen, coal tar or a mixture thereof is not modified with a latex the setting time may be as low as 5 minutes. If the emulsion is modified with a latex of a polymer being different from a polymer consisting of acrylic acid or methacrylic acid or a mixture thereof or salts thereof the setting time may range about 15 to about 40 minutes. In accordance with the present invention, 100 parts by dry weight of such cationic emulsions of asphalt, bitumen, coal tar or a mixture thereof are modified with an acidic solution of a cationic emulsifier and a polymer consisting of acrylic acid or methacrylic acid or a mixture thereof or salts thereof, in an amount of at least 0.001, preferably up to about 1, most preferably 0.001 to 0.5 parts by dry weight of said polymer. Such acidic solutions may be made using conventional techniques known by the industry. A cationic emulsifier is added to the anionic solution of the polycarboxlyic acid salt and then thee pH is adjusted to from about 1 to about 5, preferably from about 2 to about 4, e.g. about 3 to about 3.5. The pH of the solution is adjusted with an acid. Some suitable inorganic acids are hydrochloric acid, sulfuric acid and phosphoric acid. Some suitable organic acids are lower alkyl (C₁₋₄) acids, e.g. acetic acid, formic acid and oxalic acid. The surfactant may contain a nitrogen, sulphur or phosphorus atom. The surfactants may be "onium" compounds. Surfactants containing a nitrogen atom may be a primary, secondary or tertiary amine. A particularly useful class of surfactants are tertiary amines of the formula wherein R is a C₁₀₋₁₈ alkenyl radical and x and y integers and the sum of x + y is from 2 to 20. Some surfactants may be amphoteric surfactants which contain both a carboxyl group and a nitrogen atom , e.g. ampholytes and betaines. The surfactant may be an amine oxide. Generally, the surfactant is used in an amount up to about 10 percent by weight of the total polymer consisting of acrylic acid or methacrylic acid or a mixture thereof or salts thereof added to the cationic emulsion. Preferably, the surfactant is used as about 5 to about 10 percent by weight based on the total polymer consisting of acrylic acid or methacrylic acid or a mixture thereof or salts thereof added to the cationic emulsion of asphalt, bitumen, coal tar or a mixture thereof. Preferably the polymer consisting of acrylic acid or methacrylic acid, or a mixture thereof or salts thereof is mixed with a latex of a polymer selected from the following group. The latex polymers may comprise about 20 to about 60, e.g. 20 to 40 weight percent of a C₈₋₁₂ vinyl aromatic monomer which may be unsubstituted or substituted by a C₁₋₄ alkyl radical or a chlorine or bromine atom; and about 80 to about 40, preferably 80 to 60, weight percent of a C₄₋₆ conjugated diolefin. SBR polymers are typical of this class. Preferably the SBR is a latex prepared by a cold emulsion polymerization process. Some vinyl aromatic monomers may be styrene, alpha methyl styrene, t-butyl styrene, chlorostyrene and bromostyrene. Some conjugated diolefins may be 1,3 butadiene or isoprene. The above polymers may contain functional monomer(s) e.g. copolymerizable carboxylic acids, aldehydes, esters, amides or a mixture thereof. The functional monomer(s) may be present in an amount from about 0.5 up to about 10 weight percent. Some carboxylic acid monomers are C₃₋₆ ethylenically unsaturated carboxylic acids, e.g. acrylic acid, methacrylic acid, fumaric acid and itaconic acid. The functional monomer may be a C₃₋₆ ethylenically unsaturated aldehyde e.g. acrolein. The functional monomer may be a C₁₋₄ alkyl or hydroxy alkyl ester of a C₃₋₆ ethylenically unsaturated carboxylic acid. Some ester monomers are methyl acrylate, methyl methacrylate, ethyl acrylate, ethyl methacrylate, butyl acrylate, butyl methacrylate, hydroxy ethyl acrylate and half esters of dicarboxylic acids e.g. the ethyl half ester of itaconic acid and hydroxy ethyl half ester of maleic acid. The functional monomer may be an amide of a C₃₋₆ carboxylic acid , e.g. acrylamide, methacrylamide. The amides may be unsubstituted or substituted at the nitrogen atom by a C₁₋₄ alkyl radical or hydroxy alkyl radical. Some substituted amides are N-methyl acrylamide, N-ethyl acrylamide, N-methylol acrylamide, N-methyl methacrylamide, N-methyl methacrylamide, N-methylol methacrylamide. The polymer may comprise one or more monomers of C₄₋₆ conjugated diolefins which may be unsubstituted or substituted by a chlorine atom. Preferred members of this group are latices of natural rubber or chloroprene. The polymer may be a nitrile polymer. Typically, these polymers comprise up to 40 weight percent of a C₃₋₆ alkenyl nitrile and the balance a C₄₋₆ conjugated diolefin. Preferred nitrile monomers are acrylonitrile and preferred diolefins are butadiene and isoprene. These polymers are particularly useful where the final composite may be subjected to oils, or solvents. This type of emulsion of asphalt, bitumen or coal tar is particularly useful in the construction of refueling aprons at airports. The polymer may be a copolymer of from 90 to 75 weight percent of a C₂₋₃ olefin and from 10 to 25 weight percent of a C₃₋₄ ethylenically unsaturated carboxylic acid. Preferred monomers are ethylene and acrylic or methacrylic acid. The polymer may be a polymer of a C₂₋₃ alpha olefin and an unsaturated ester of a saturated organic acid. Such polymers may optionally contain up to 10, e.g. about 0.5 to about 10, weight percent of a functional monomer. Such monomers have been discussed above. Typically such polymers comprise: about 1 to about 40, e.g. about 5 to about 25, weight percent of a C₂₋₃ alpha olefin monomer, about 99 to about 50, preferably 95 to 65, weight percent of a C₂₋₈ alkenyl or hydroxy alkenyl ester of a C₁₋₁₂ saturated carboxylic acid; and optionally about 0.5 to about 10, preferably about 0.5 to about 5, weight percent of one or more monomers selected from the group consisting of: C₃₋₆ ethylenically unsaturated carboxylic acids; C₃₋₆ ethylenically unsaturated aldehydes; C₁₋₄ alkyl and hydroxy alkyl esters of a C₃₋₆ ethylenically unsaturated carboxylic acids; and amides of C₃₋₆ ethylenically unsaturated carboxylic acids, which amides may be unsubstituted or substituted at the nitrogen atom by up to two radicals selected from the group consisting of C₁₋₄ alkyl and C₁₋₄ hydroxy alkyl radicals. Some alpha olefins and functional monomers have been discussed above. Some C₂₋₈ alkenyl or hydroxy alkenyl ester of C₁₋₁₂ saturated carboxylic acids vinyl esters e.g. vinyl acetate and its homologues; and allyl esters e.g. allyl acetate and its homologues. Typically the solution of the polymer consisting of acrylic acid or methacrylic acid, or a mixture thereof or salts thereof is added to the latex in an amount from about 0.1 to about 2.0, preferably 0.1 to 1.0, most preferably from 0.1 to 0.5 parts by dry weight per 100 parts by dry weight of latex polymer. After the addition of the cationic emulsifier the latex is made cationic by adjusting the pH with an inorganic acid. Preferred polymers consisting of acrylic acid or methacrylic acid or a mixture thereof or salts thereof are soluble in water. Preferably these polymers have a molecular weight of less than 100,000, preferably less than 60,000. These molecular weight limits are practical from the point of view of viscosity problems in blending salts of high molecular weight polymers consisting of acrylic or meth acrylic acids or a mixture thereof or salts thereof with an anionic latex prior to making it cationic. The cationic latex mixture is then added to the cationic emulsion of asphalt, bitumen, coal tar or a mixture thereof. Preferably, the latex polymers are used in an amount up to about 20, preferably about 3 to about 15 parts by dry weight per 100 parts by dry weight of asphalt, bitumen, coal tar or a mixture thereof. Typically, such emulsions are applied to a surface, then about 1000 parts by weight of aggregate is laid over about 100 parts by dry weight of the asphalt, bitumen, coal tar or mixture thereof. The aggregate may be a mixture of fine aggregate such as sand and more coarse aggregate such as gravel. In some applications such as surface sealing, the aggregate may be entirely fine aggregate such as sand. The following examples are intended to illustrate the invention and are not intended to restrict its scope. In the following examples unless otherwise specified, parts are parts by dry weight. In the following experiments, a cationic bitumen emulsion under the tradename Actimul RED 65% was obtained from Societe Chimique de la Route (SCR). Example 1 The effect of a salt of polyacrylic acid on the setting time and drying time of the bitumen emulsion in admixture of aggregate material is demonstrated by the following experiment. A sample of a low molecular weight polyacrylic acid salt sold under the tradename Dispex N40 was made cationic by adding to it about 7 parts per 100 parts of polymer of a tertiary amine sold under the trade mark Noramox S11 and adjusting the pH to from 3 to 3.5 wih HCL. A sufficient amount of this cationic polyacrylic acid was added to the cationic bitumen emulsion to provide 0.3 parts by weight of polyacrylic acid per 100 parts by dry weight bitumen. The bitumen emulsion was then spread in a polyester cup and gravelled with washed and dried aggregate with a particle size of 6-10 mm. The time at which the stones were no longer movable and the time at which the emulsion dried was recorded. Bitumen Emulsion Bitumen Emulsion Polyacrylic acid --- 0.3 Starts setting 45 min. 5 min. --- Completely gelled after 10 min. End Drying 120 min. --- This experiment clearly shows the setting of a cationic bitumen emulsion in admixture with aggregate material is reduced by the addition of 0.3 parts by weight of a low molecular weight polyacrylic acid per 100 parts by dry weight of bitumen. A series of various latices was modified with varying amounts of a low molecular weight sodium salt of polyacrylic acid. The modified latex was then made cationic by adding 7 parts per 100 parts of polymer of a tertiary amine sold under the tradename Noramox S-11. The pH of the latex was adjusted to 3-3.5 with HCl. Then 3 parts by dry weight of the resulting cationic latex was added to 100 parts by dry weight of the bitumen emulsion. The setting and drying time for the bitumen emulsion in admixture with aggregate material were determined as described above. The results are recorded in Table 2. A series of modified cationic asphalt emulsion prepared above were tested for their cohesive strength in accordance with Essai d'Adhesion Globale A La Plaque Vialit of the Laboratoire Central des Ponts et Chaussees (sometimes called the French Chip Test). In this test two stainless steel plates 200 mm/200 mm/3 mm are coated with 1.5 kg dry/m² latex modified bitumen emulsion (M.B.E.) 100 stainless steel balls with a diameter of 12 mm are put in the M.B.E. and the plates allowed to dry for 24 h at room temperature. Afterwards, the one plate is dried for 48 h more at room temperature, while the second plate is aged 48 h in an oven at 60°C. Both plates are then brought to 5°C by means of a cooling bath. The plates are then inverted on a four point stand and a steel ball (500 g, 50 mm diam.) is then dropped from a 50 cm height to the back of each plate ten times. The number of balls fallen from the asphalt each time and the number of balls remaining in the asphalt on the plate are recorded. The number of balls fallen in each test is multiplied by a factor ranging from 10 to 1 sequentially for the first to the tenth drop of the 500 g ball. The sum of these factors is substracted from 1000 to give a measure of the cohesive strength of the asphalt. The results are recorded in Table 3. Note: The qualification "about" used in this specification's description and claims so as to qualify numerical values includes the precise values and quantities that are about or substantially the same as the precise values. The present invention also provides a method to reduce the setting time of a cationic emulsion of bitumen, asphalt, coal tar or a mixture thereof characterised by incorporating into said emulsion at least 0.001 parts by weight per 100 parts by dry weight of said emulsion of a polycarboxylic acid.

Claims: A method of reducing the setting time of a cationic emulsion of bitumen, asphalt, coal tar or a mixture thereof in admixture with an aggregate material suitable for the production of aggregate pavement from said cationic emulsion characterised by incorporating into said emulsion an effective amount of an acidic solution of a cationic emulsifier and a polymer consisting of acrylic acid or methacrylic acid or a mixture thereof or salts thereof. A method as claimed in claim 1, wherein said aggregate material is sand, stone and/or gravel. A method as claimed in claim 1 or 2, wherein said polymer is used in an amount sufficient to provide at least 0.001 part by dry weight per 100 parts by dry weight of said cationic emulsion of bitumen, asphalt, coal tar or a mixture thereof. A method as claimed in claims 1 to 3, wherein said polymer is used in an amount sufficient to provide from 0.001 to 1 part by dry weight per 100 parts by dry weight of said cationic emulsion of bitumen, asphalt, coal tar or a mixture thereof. A method as claimed in claims 1 to 4, wherein said polymer is used in an amount sufficient to provide from 0.001 to 0.5 part by dry weight per 100 parts by dry weight of said cationic emulsion of bitumen, asphalt, coal tar or a mixture thereof. A method as claimed in claims 1 to 5, wherein the molecular weight of said polymer is less than 100,000. A method as claimed in claims 1 to 6, wherein the molecular weight of said polymer is less than 60,000. A method as claimed in claim 1, wherein said cationic emulsion of bitumen, asphalt, coal tar or a mixture thereof is modified with an aqueous polymer latex, said polymer being different from a polymer consisting of acrylic acid, methacrylic acid, a mixture thereof or salts thereof. A method as claimed in claim 8, wherein said cationic emulsion of bitumen, asphalt, coal tar or a mixture thereof is modified with the aqueous polymer latex in an amount of up to 20 parts by dry weight per 100 parts by dry weight bitumen, asphalt, coal tar or a mixture thereof. A method as claimed in claim 8, wherein said cationic emulsion of bitumen, asphalt, coal tar or a mixture thereof is modified with the aqueous polymer latex in an amount of from 3 to 15 parts by dry weight per 100 parts by dry weight of bitumen, asphalt, coal tar or a mixture thereof. A method as claimed in claims 1 to 10 characterised by 1000 parts by weight of an aggregate material per 100 parts by dry weight of bitumen, asphalt, coal tar or a mixture thereof. A composition comprising: 100 parts by dry weight of a cationic emulsion of bitumen, asphalt, coal tar or a mixture thereof; and an acidic solution of a cationic emulsifier and a polymer consisting of acrylic acid or methacrylic acid or a mixture thereof or salts thereof, in an amount of from 0.001 to 1.0 part by dry weight of said polymer. A composition comprising: 100 parts by dry weight of a cationic emulsion of bitumen, asphalt, coal tar or a mixture thereof; an acidic solution of a cationic emulsifier and a polymer consisting of acrylic acid or methacrylic acid or a mixture thereof or salts thereof, in an amount of from 0.001 to 1.0 part by dry weight of said polymer; and up to 20 parts by dry weight of a polymer latex, said polymer being different from a polymer consisting of acrylic acid or methacrylic acid or mixture thereof or salts thereof.

Inventors: BLANPAIN, PETER RONALD JEFFREY, CREAK, JOHN WILLIAM, MORI, GUY FREDERIC, OFFNER, ROLAND FRANCOIS EUGENE
Applicants: BASF AKTIENGESELLSCHAFT
Application year: 1987
Main classification: C10C3
IPC codes: C08L95, E01C7