LUBRICATING OIL COMPOSITION

Abstract: Properties of paraffinic or naphthenic mineral oil lubricants may be improved by admixing therewith a poly­ alkylene oxide compound having a C₂-C₄ alkylene oxide moiety and a C₆-C₄₀ alkylene oxide moiety.

Description: BACKGROUND OF THE INVENTION This invention relates to lubricating oil compositions containing a mineral base oil and an oil-soluble polyalkylene oxide compound. Mineral oil lubricants, such as paraffinic or naphthenic petroleum oils, have been used for most lubricating purposes. However, they have certain disadvantages such as relatively low viscosity indices over varying temperatures and high susceptibility to oxidation. Synthetic lubricating oils such as those of poly­ alkylene oxide type have been used as substitutes for mineral oil lubricants in certain area because of their relatively high viscosity indices in comparison with mineral oil lubricants. Since both mineral oils and polyalkylene oxide oils have their own advantages, it would be desirable to combine them. However, most of polyalkylene oxides such as poly­ ethylene oxide, polypropylene oxide, copolymers of ethylene oxide and propylene oxide and their ethers or esters have limited solubilities in aliphatic hydrocarbons and thus cannot be mixed with paraffinic or naphthenic lubricating oil bases. We have found that certain polymeric alkylene oxides containing long chain alkylene oxide moieties are substantially freely soluble in aliphatic hydrocarbon liquids and may be mixed with paraffinic or naphthenic lubricating oil bases to improve their properties such as viscosity indices, load-­ carrying capacities, anti-oxidative properties, wear resist­ ances and the like. SUMMARY OF THE INVENTION According to this invention, there is provided a lubricating oil composition consisting essentially of a paraffinic or naphthenic or a mixture of both types of mineral oils, and 5 to 60 % by weight of the composition of a polyalkylene oxide compound of the formula: R-C n H 2n O-C m H 2m O H] Z wherein R is the residue of a compound having l-8 active hydrogen atoms with removal of the active hydrogen atoms, n is 2-4, m is 6-40, x and y are an integer, and Z is l-8; said polyalkylene oxide compound having a molecular weight of 500 to l00,000 and a C₆-C₄₀ alkylene oxide content of l5 to 60 % by weight of the entire molecule. DETAILED DISCUSSION Some of polyalkylene oxide compounds of the above type are disclosed in, for example, U.S. Patent No. 4,302,349 to Kosswig et al, and a co-pending U.S. Patent Application Serial No. 409,262, filed August l8, l982 and assigned to the assignee of this application. The polyalkylene oxide compounds may be prepared by reacting a starting active hydrogen compound R(H) Z in the presence of a basic or acidic catalyst first with a C₂-C₄ alkylene oxide and then with a C₆-C₄₀ alkylene oxide. Examples of starting active hydrogen compounds include monoalcohols such as methanol, ethanol, butanol, lauryl alcohol, oleyl alcohol and stearyl alcohol; glycols such as ethylene glycol, propylene glycol and butylene glycol; polyols such as glycerine, trimethylolpropane, sorbitol and sucrose; phenols such as phenol, bisphenol A and hydroquinone; amines such as ammonia, ethylenediamine, triethylenediamine, n-butylamine, laurylamine, aniline and toluidine; carboxylic acids such as acetic acid, maleic acid and oleic acid. Examples of C₂-C₄ alkylene oxides include ethylene oxide, propylene oxide and butylene oxide. Mixtures of these alkylene oxides may also be used. Propylene oxide alone or mixtures of propylene oxide with ethylene oxide are preferable. Examples of usable C₆-C₄₀ alkylene oxides, namely epoxyalkanes include cyclohexene oxide, nonene oxide and alpha olefin oxides of l2-40 carbon atoms. Usable basic or acidic catalyst include sodium hydr­ oxide, potassium hydroxide, sodium acetate, sodium methoxide, boron tetrafluoride and phosphoric acid. The proportions of C₂-C₄ alkylene oxide and C₆-C₄₀ alkylene oxide relative to the active hydrogen compound are selected so that the resulting adduct has a molecular weight of 500-l00,000 and the C₆-C₄₀ alkylene oxide content of l5 to 60%, preferably 20 to 50% by weight of the entire molecule. The reaction may be carried out at a temperature of l00°C to l50°C at a pressure below 5 kg/cm²G. The resulting polyalkylene oxide adducts are substan­ tially freely soluble in aliphatic hydrocarbon liquids such as paraffinic or naphthenic mineral oil bases. Heretofore, there have not been known polyalkylene oxides which are soluble in both aliphatic and aromatic hydrocarbon liquids while those soluble only in aromatic hydrocarbons are known. Accordingly, the polyalkylene oxide compounds used in the present invention may be intermixed with a paraffinic or naphthenic or a mixture of both types of mineral oils at any proportion. However, the proportions of the polyalkylene oxide compounds ranging from 5 to 60%, preferably from l0 to 50% by weight of the composition have been found advantageous. Within this range, the polyalkylene compounds may improve properties of the base oils including viscosity indices, load-carrying capacities, anti-oxidative properties, wear resistances and the like while retaining inherent beneficial properties of the base oils. The composition may contain conventional additives such as anti-oxidants, rust preventors and the like. The following examples are given to illustrate the present invention. All parts and percents therein are by weight unless otherwise indicated. EXAMPLE l An autoclave having stirring means was charged with 6 parts of propylene glycol and 5 parts of potassium hydroxide and then purged with nitrogen gas. 924 parts of propylene oxide were introduced to the autoclave at a pressure of 3 kg/cm²G and reacted at l30°C. Thereafter, 284 parts of nonene oxide were reacted at l30°C. Total reaction time was 4 hours. After 20 parts of synthetic aluminum silicate powder were added, the reaction mixture was stirred at l20°C for 3 hours and then filtered through a l micron mesh screen to remove aluminum silicate particles. l284 parts of a liquid polyalkylene oxide compound were obtained. This polyalkylene oxide compound has a viscosity of 250 cps at 25°C, a nonene oxide content of 22%, and a molecular weight of l284, and is freely soluble in liquid paraffin. EXAMPLE 2 An autoclave having stirring means was charged with 550 parts of an adduct of l mole of nonylphenol and 7.5 moles of ethylene oxide, and l part of sodium hydroxide. After the interior was purged with nitrogen gas, the content of autoclave was heated to l50°C. Thereafter, 204 parts of alpha-olefin oxide of l6-l8 carbon atoms were introduced at a pressure of 0.2 kg/cm²G and reacted for 3.5 hours. The sodium hydroxide catalyst was neutralized with acetic acid. 754 parts of a liquid polyalkylene oxide compound were obtained. This polyalkylene compound has a viscosity of l70 cps at 25°C, an alpha-olefin content of 27% and a molecular weight of 754, and is freely soluble in liquid paraffin. EXAMPLES 3-8 Analogous to Example l, polyalkylene oxide compounds listed Table l below were prepared. EXAMPLE 9 The polyalkylene oxide compound prepared in Example l was incorporated to a paraffinic mineral oil (l50 neutral), a naphthenic mineral oil (500 neutral) or a commercial motor oil (SAE 30) at a concentration shown in Table 2 below. The resulting compositions and control oils free of the polyalkylene oxide compound were subjected to a load-carrying capacity test using Soda's four-balls tester at 220 rpm. The results are shown in Table 2. As is apparent in Table 2, the polyalkylene oxide compound improved various properties of the base oils signif­ icantly.

Claims: 1. A lubricating oil composition consisting essen­ tially of a paraffinic or naphthenic mineral oil or a mixture of both types of mineral oils, and 5 to 60 % by weight of the composition of a polyalkylene oxide compound of the formula: R-CnH2n O-CmH2mO-H]Z wherein R is the residue of a compound having l-8 active hydrogen atoms with removal of the active hydrogen atoms, n is 2-4, m is 6-40, x and y are an integer, and Z is l-8; said polyalkylene oxide compound having a molecular weight of 500 to l00,000 and a C₆-C₄₀ alkylene oxide content of l5 to 60 % by weight of the entire molecule. 2. The lubricating oil composition of Claim l, said compound having l-8 active hydrogen atoms is an aliphatic monoalcohol, a glycol, a polyol, an amine, a phenol or a carboxylic acid. 3. The lubricating oil composition of Claim l, wherein the -CnH2n- moiety is polyoxypropylene or poly(oxypropylene-oxyethylene). 4. The lubricating oil composition of Claim l, wherein the -CmH2m- moiety is derived from cyclohexene oxide, nonene oxide or a C₁₂-C₄₀ alpha-olefin oxide. 5. The lubricating oil composition of Claim l, wherein said C₆-C₄₀ alkylene oxide content is 20 to 50 % by weight of the entire molecule of the polyalkylene oxide compound.

Inventors: ISODA, CHUZO, MORI, SHIGEO, TESHIMA, SATOSHI
Applicants: DAI-ICHI KOGYO SEIYAKU CO., LTD.
Application year: 1987
Main classification: C10M145
IPC codes: C10N30, C07C43, C10M145, C10M129, C07C41, C08G65, C10M111, C10M133, C08L71, C07C67, C10N40, C10M107