A crystalline aromatic polyketone copolymer and a process for producing the same

Abstract: A copolymer which can be employed for various molded particles, particularly for uses which require a high nonflammability which copolymer is a crystalline aromatic polyketone type copolymer which has an 0.40 and has a linear polymer structure comprising structural units (A) represented by the formula (A) structural units (B) represented by the formula (B) structural units (C) represented by the formula (C₁) or by the formula (C₂) the molar ratio of said units (B) to said units (C) being in the range from 30 : 70 to 99 : l, and the unit (A) and either the unit (B) or the unit (C) being linked alter­ nately; and a process producing the same.

Description: FIELD OF THE INVENTION AND RELATED ART STATEMENT FIELD OF THE INVENTION This invention relates to a novel crystalline aromatic etherthioether - aromatic ketone type copolymer and a process for producing the same. More particularly, it relates to a novel crystalline polymer excellent in heat resistance, nonflammability, solvent resistance and mechanical properties which has a chemical structure comprising phenylene groups linked through an ether group, thioether group, and ketone group, and also to an industrially useful process for producing the same. RELATED ART STATEMENT Polymers heretofore known which have a structure comprising phenylene group linked through an ether group and ketone group include those which have the structural formula or the structural formula They are attracting attention as molding materials owing to their excellent heat resistance, molding stability, and mechanical strength. These polymers have a certain extent of nonflammability since they contain aromatic rings. However, they are not fully satisfactory for fields of application which require a high degree of nonflammability. Accordingly, an attempt has been made to enhance the nonflammability of these macromolecular compounds (i.e., polymers) by adding flame retardants thereto [Japanese Patent Application Kokai (Laid-Open) No. 51,743/85]. On the other hand, a known polymer having a structure comprising phenylene groups linked through a thioether group is polyphenylene sulfide having the structural formula The polymer is obtained, for example, by reacting dichlorobenzene with sodium sulfide [Japanese Patent Application Kokoku (Post-Exam. Appln.) No. 12,240/77]. Said polyphenylene sulfide has the advantage of excellent nonflammability. Further, it has excellent characteristics including low moisture absorption, high dimensional stability, and good compatibility with inorganic fillers, which allows incorporation of a high concentration of said fillers. However, since said polyphenylene sulfide has a low glass transition temperature (hereinafter referred to as Tg) of 80°C, it shows a low heat distortion temperature (hereinafter referred to as HDT) and hence has a weakness in heat resistance; further it has a relatively low crystal melting point (hereinafter referred to as Tm) of 281°C. Therefore, its field of application as a heat resistant polymer is inevitably subjected to limitation. Accordingly, development of this type of polymer having a higher crystal melting point has been eagerly awaited. Various attempts have been made for this type of polymer to obtain a product having a higher melting point. For example, it has been proposed to introduce the unit randomly into a polymer chain comprising linkages (U.S. Patent No. 4,286,018). However, polymers thus obtained have a disadvantage in that they show lower crystallinity and lower heat resistance and mechanical properties than those of homopolymer when the content of the unit therein decreases to 90% or less. Further, there are also known macromolecular compounds, formed by introducing ketone groups regularly into polyphenylene sulfide, which have the structural formula or the structural formula However, the macromolecular compound represented by the formula (IV) mentioned above melts at 220° to 230°C (U.S. Patent No. 3,432,468) and hence is unsatisfactory in heat resistance. On the other hand, the macromolecular compounds represented by the above formula (V) has, although it has a high Tm of 352°C, the disadvantage of brittleness of films obtained therefrom. (B.P. No. 1,368,967). Thus, there has not yet been found any polymer of the polyphenylene sulfide type which has an improved heat resistance with increased Tg and Tm while retaining the excellent characteristics of polyphenylene sulfide. In order to obviate the disadvantages described above, the present inventors have previously proposed a linear polymer comprising structural units represented by the formula (Ia) and/or the formula (Ib) and structural units represented by the formula (IIa) linked alternately (EP-A- 185,317). The above-mentioned polymer possesses an excellent heat resistance while retaining excellent characteristics of polyphenylene sulfide including, for example, high nonflammability, low moisture absorption, good molding stability, and good compatibility with inorganic fillers. The polymer comprising structural units of the formula (Ia) and/or (Ib) and those of the formula (IIa) linked alternately is excellent in nonflammability and heat resistance (as judged by the measure of thermal weight loss temperature). It is suitable for film production. However, it has a low crystallization rate although its maximum degree of crystallization is high, so that, in injection molding, such procedures are required as increasing the temperature of the mold, increasing the cooling time in the mold, or annealing the molded article to increase degree of crystallization. Thus, the polymer cannot be regarded suitable for injection molding. On the other hand, as to the method of preparing a polymer containing thioether groups, there is known a process of producing poly(etherthioether) from an alkali metal salt of hydroxythiophenol and an aromatic dihalide such as dichlorodiphenyl sulfone (B.P. No. 1,295,584). However, since the polymer obtained by the process contains sulfone groups and has an internal structure of irregular arrangement of repeating units, it is amorphous and is not fully satisfactory regarding heat resistance, solvent resistance and mechanical properties. Further, a method has been proposed which produces polyether or polythioether from a compound having two -XH groups (wherein X is an oxygen or sulfur atom) and a dihalobenzenoid compound in the presence of potassium carbonate (B.P. 1,264,900). However, this method uses a low polymerization temperature and, like in the above-mentioned case, cannot give a crystalline polymer. Thus, there has hitherto been known no material which has been imparted a sufficiently improved nonflammability while retaining excellent heat resistance, molding stability and mechanical strength which are inherent to aromatic polyetherketone, in other words no material which has a heat resistance enhanced to the same level as that in prior polyetherketone while retaining excellent nonflammability, low moisture absorption, and excellent dimensional stability which are inherent to polyphenylene sulfide. OBJECT AND SUMMARY OF THE INVENTION The object of this invention is to provide a novel crystalline copolymer which can be produced by a simple means and yet has an excellent nonflammability imparted thereto while retaining excellent heat resistance, molding stability and mechanical strength which are inherent to aromatic polyether ketone. After extensive studies the present inventors have found that the above-mentioned object can be attained by using, as the raw materials, 4,4′-dihaloterephthalophenone, 4-hydroxythiophenol, and hydroquinone or 4,4′-dihydroxybenzophenone, and polymerizing them in a specified molar ratio. The present invention has been accomplished on the basis of the above finding. Thus, according to this invention, there is provided a crystalline aromatic polyketone type copolymer which has an intrinsic viscosity of not less than 0.40 and has a linear polymer structure comprising structural units (A) represented by the formula (A) structural units (B) represented by the formula (B) and structural units (C) represented by the formula (C₁) or the formula (C₂) the molar ratio of said units (B) to said units (C) being in the range from 30 : 70 to 99 : 1, and the unit (A) and either the unit (B) or the unit (C) being linked alternately. The above-mentioned copolymer can be prepared, for example, by polycondensing an active-hydrogen containing component consisting of 30 to 99% by mole of 4-hydroxythiophenol and 70 to 1% by mole of hydroquinone, or an active-hydrogen containing component consisting of 30 to 99% by mole of 4-hydroxythiophenol and 70 to 1% by mole of 4,4′-dihydroxybenzophenone, with an amount of 4,4′-dihaloterephthalophenone substantially equimolar to the said active-hydrogen containing component, in at least one member selected from aromatic sulfones and aromatic ketones used as the solvent at a temperature in the range of 200° to 400°C and in the presence of at least one member selected from alkali metal carbonates and bicarbonates. BRIEF DESCRIPTION OF THE DRAWINGS Figs. 1, 2, 3 and 4 are each a graph showing the X-ray diffraction spectrum or the infrared absorption spectrum of a copolymer obtained according to this invention. The copolymers according to this invention involve two kinds of copolymer, namely (1) a copolymer in which the unit (B) and the unit (C) represented by the formula (C₁) on one hand and the unit (A) on the other hand are linked alternately, and (2) a copolymer in which the unit (B) and the unit (C) represented by the formula (C₂) on one hand and the unit (A) on the other hand are linked alternately, in copolymer (1) the molar ratio of the unit (B) to the unit (C) being in the range from 30 : 70 to 99 : 1 and in copolymer (2) from 30 : 70 to 90 : 10. In these copolymers, the distribution of the units (B) and (C), which link with the unit (A) alternately, is random, block, or alternate. However, irrespective of the distribution, the copolymers show an excellent nonflammability so long as their composition is within the range specified in this invention. The molar ratio of the unit (B) to the unit (C) is preferably in the range from 40 : 60 to 95 : 5, more preferably from 50 : 50 to 90 : 10. The copolymer according to this invention is crystalline over the whole range of composition and in all the kind of linking manners. In general, when monomers which give respectively a crystalline polymer in homopolymerization are copolymerized with each other, it is usual that the resulting copolymer becomes amorphous in a certain range of copolymer composition. However, the copolymer of this invention was found to be crystalline over the whole range of composition specified by this invention. This was quite unanticipated. The copolymer of this invention has a more excellent nonflammability than that of previous aromatic polyetherketone. It shows properties equal or superior even to those of polyphenylene sulfide, which is known to be excellent in nonflammability. At an equal molar composition of the unit (B) and the unit (C), the above-mentioned copolymer (1) is more excellent in nonflammability than the copolymer (2). As will be shown later in Referential Examples, the copolymer of this invention has a crystallization rate which is higher than that of a homopolymer comprising the unit (A) and the unit (B) linked alternately, and is equal to or higher than that of prior aromatic polyetherketone. Further, the copolymer of this invention has Tm and Tg both higher than those of a homopolymer comprising the unit (A) and the unit (B) linked alternately, and is more excellent in heat resistance than the homopolymer. The polymer of this invention should have an intrinsic viscosity of not less than 0.40, preferably 0.4 to 1.8. Polymers having an intrinsic viscosity of less than 0.4 are brittle and cannot be suitably used as molded articles. Polymers having an intrinsic viscosity of 1.8 or more show too high a viscosity when melted and are difficult to mold. The X-ray diffraction analysis of the polymer of this invention has revealed that the polymer could be classified into two groups based on the pattern of the X-ray diffraction chart. The values of 2ϑ in the diffraction charts for respective groups are shown below in the order of intensity down to the third. Group 1: 23.0 ±0.3, 16.6 ±0.6, 18.5 ±0.3 Group 2: 18.7 ±0.2, 23.0 ±0.1, 20.7 ±0.3 The peak of 16.6 ± 0.6 is characteristic of the group 1, and that of 20.7 ± 0.3 is characteristics of the group 2. The monomers of the raw materials used in this invention are 4-hydroxythiophenol, 4,4′-dihydroxybenzophenone, hydroquinone, and 4,4′-dihaloterephthalophenone represented by the general formula wherein X¹ and X² may be the same or different and each denotes a halogen atom. The ratio of said 4-hydroxythiophenol to hydroquinone or 4,4′-dihydroxybenzophenone to be used is selected from the range of 30 : 70 to 99 : 1 or 30 : 70 to 90 : 10, respectively, by mole. Specific examples of 4,4′-dihaloterephthalophenone include 4,4′-difluoroterephthalophenone, 4,4′-dichloroterephthalophenone, and 4-chloro-4′-fluoroterephthalophenone. These monomers may be used each alone or in a combination of two or more thereof. The ratio of 4,4′-dihaloterephthalophenone used to the total amount of 4-hydroxythiophenol and hydroquinone or to the total amount of 4-hydroxythiophenol and 4,4′-dihydroxybenzophenone should be substantially equimolar, and is selected from the range of 0.95 to 1.05 mole of the former relative to 1 mole of the latter. When the molar ratio is outside the above mentioned range, a high molecular weight polymer cannot be obtained. In order that the polymer terminals may be in the form of stable aromatic halide units, it is particularly preferable to use 1.00 to 1.05 mole of 4,4′-dihaloterephthalophenone relative to 1 mole of the total of 4-hydroxythiophenol and hydroquinone or the total of 4-hydroxythiophenol and 4,4′-dihydroxybenzophenone. In the process according to this invention, aromatic ketones and aromatic sulfones are used as the polymerization solvent. Aromatic ketones may be those represented by the general formula wherein R¹ and R² may be the same or different from each other, and are a hydrogen atom, an alkyl group of 1 to 3 carbon atoms, or a phenyl group, provided that when R¹ and/or R² are (is) a phenyl group, they (it) may be fused with the benzene ring of the benzophenone skeleton. Specific examples of such compounds include benzophenone, 4-methylbenzophenone, 4-phenylbenzophenone, naphthyl phenyl ketone, and 4,4′-dimethylbenzophenone. Of these, benzophenone (m.p.: 48° to 49°C) is particularly preferred because it is thermally stable, easily available, can be treated as liquid near room temperatures as contrasted to solid solvent such as diphenyl sulfone (m.p.: 128 to 129°), allowing easy separation of the product and recovery and purification of the solvent. As another group of aromatic ketones, there may be mentioned the compounds represented by the general formula wherein Y is an oxygen or sulfur atom; and R³ and R⁴ are the same as R¹ and R² defined above. Examples of such xanthone and thioxanthone compounds include xanthone, 2-methylxanthone, 2-phenylxanthone, thioxanthone, 2-methylthioxanthone, and 2-phenylthioxanthone. Particularly preferred of these are xanthone and thioxanthone. As further examples of aromatic ketones, mention may be made of 4-phenoxybenzophenone, terephthalophenone and isophthalophenone. Aromatic sulfones may be those represented by the general formulas wherein R⁵ and R⁶ are the same as R¹ and R² defined above. Specific examples thereof include diphenyl sulfone, ditolyl sulfone, dibenzothiophenone, phenoxathin dioxide and 4-phenylsulfonylbiphenyl, diphenyl sulfone being more preferable of these. Of these solvents, aromatic ketones are thermally more stable than aromatic polysulfones, and give a highly crystalline polymer of high molecular weight more readily. This is considered to be due to their higher capability to dissolve the polymer produced. The amount of the solvent to be used is preferably in the range of 10 to 1,000 parts by weight, more preferably 20 to 500 parts by weight, relative to 100 parts by weight of the total of 4-hydroxythiophenol, hydroquinone or 4,4′-dihydroxybenzophenone, and 4,4′-dihaloterephthalophenone. An amount of solvent larger than the above-mentioned range adversely affects the polycondensation efficiency. When the amount is smaller than the range, the effect of the solvent cannot be exhibited substantially. Examples of alkali metal carbonates and alkali metal bicarbonates used in the process of this invention include sodium carbonate, potassium carbonate, rubidium carbonate, cesium carbonate, sodium hydrogen carbonate, potassium hydrogen carbonate, rubidium hydrogen carbonate, and cesium hydrogen carbonate. Particularly preferred are sodium carbonate, potassium carbonate, sodium hydrogen carbonate, and potassium hydrogen carbonate. These alkalis may be used each alone or in a combination of two or more thereof. The amount of alkali metals to be used is preferably 0.3 to 2 gram atoms relative to 1/2 mole of the total of 4-hydroxythiophenol and hydroquinone or the total of 4-hydroxythiophenol and 4,4′-dihydroxybenzophenone. The alkali metal salt is preferably used in as small an amount as possible, because an excessive amount of the salt used makes the reaction too vigorous, causing harmful side reactions to take place, and also is disadvantageous in point of cost. However, when the amount of the alkali metal atom is less than 0.3 gram atom, a longer polymerization time is necessary and further the intended high molecular weight polymer can be difficultly obtained. When the solvent is an aromatic sulfone, xanthone compound, and thioxanthone compound, 0.5 to 1 gram atom is particularly preferable. When it is a benzophenone compound, 0.7 to 1.2 gram atoms is particularly preferable. The alkali metal salt is preferably anhydrous. In the case of a hydrous salt, it can be used by distilling water away from the polymerization system together with an azeotropic solvent. The process for production according to this invention is advantageously carried out as follows. A solvent, an alkali metal salt, 4,4′-dihaloterephthalophenone, 4-hydroxythiophenol and hydroquinone or 4,4′-dihydroxybenzophenone are placed in a reactor under an atmosphere of inert gas such as nitrogen or argon. Polymerization is carried out by heating the resulting mixture under an atmosphere of inert gas such as nitrogen or argon at a temperature in the range of 200° to 400°C, preferably in the range of 250°C to 350°C. At a temperature below 200°C, precipitation of polymer takes place during polymerization and a high molecular weight polymer is not obtained, whereas at a temperature exceeding 400°C, a marked discoloration of the polymer formed takes place owing to the degradation of the polymer. Too rapid temperature elevation is unfavorable because it makes polymerization system ununiform, and accelerates side reactions which cause the discoloration and the gellation of polymer. Accordingly, it is necessary that due measures be taken to increase the temperature stepwise or gradually and to keep the temperature of the polymerization system as uniform as possible. In order to obtain a high molecular weight polymer having an intrinsic viscosity of 0.40 or more, polymerization should be carried out at the final stage at a temperature not below 200°C, preferably not below 280°C. Also, prepolymerization may be carried out below said temperature to make the polycondensation proceed smoothly. Water evolved during polymerization is preferably removed out of the polymerization system. Methods used to remove water involve simply replacing the gas phase of the polymerization system with a dry inert gas, or carrying out the polymerization under a dry inert gas stream, or introducing a solvent having a lower boiling point than that of the polymerization solvent into the system to distill water away from the system together with the solvent. Polymerization can be terminated by adding to and making react with the reaction system a suitable terminal stopping agent, for example a monofunctional or polyfunctional halide, more specifically methylene chloride, tert-butyl chloride, 4,4′-dichlorodiphenyl sulfone, 4,4′-difluorobenzophenone, 4,4′-difluoroterephthalophenone or 4-fluorobenzophenone at the above-mentioned polymerization temperature. Also, this makes it possible to change a hydroxyl group of polymer into a thermally stable alkyl group, aromatic halogen group, and aromatic group at the terminal. Examples This invention will be further discribed in detail below with reference to Examples. However, it is in no way limited by these Examples. Since the polymer of this invention is soluble only in concentrated sulfuric acid and insoluble in organic solvents in general, its average molecular weight is difficult to obtain. Accordingly, intrinsic viscosity is used as the measure of molecular weight. The properties of the polymer were determined in the following manner. (1) Intrinsic viscosity By using a concentrated sulfuric acid of a density of 1.84 g/cm³, a solution containing 0.1 g of polymer per 100 cm³ of solution and a solution containing 0.5 g of polymer per 100 cm³ of solution were prepared. The viscosity of the solution was measured at 25°C. Intrinsic viscosity was obtained by using the following equation: Intrinsic viscosity = {(η rel -1)/c} c → 0 , wherein η rel denotes relative viscosity; c denotes concentration (expressed in g/100 ml); and the symbol c → 0 means that the value of (η rel -1)/c is extraporated to a point at which concentration c is 0. (2) Crystal melting point (Tm) and glass transition temperature (Tg) These were determined by using a DSC (differential scanning colorimeter) at a temperature increasing rate of 10°C/min. (3) Crystallinity Crystallinity was judged from wide angle X-ray diffraction and the crystal melting point (Tm). Example 1 In a 4-necked separable flask equipped with a stirrer, a nitrogen inlet tube and a cooler, which had been replaced by nitrogen, were placed 13.14 g (0.0408 mole) of 4,4′-difluoroterephthalophenone, 2.77 g (0.022 mole) of 4-hydroxythiophenol, 1.98 g (0.018 mole) of hydroquinone, 5.52 g (0.040 mole) of anhydrous potassium carbonate, and 30 g of benzophenone. Heating of the mixture was initiated under a nitrogen gas stream while evolved water being removed from the reaction system. The reaction mixture was brought to 305°C over a period of one hour and 30 minutes, then kept at the temperature for 3 hours and, after addition of 4.0 g of 4,4′-difluorobenzophenone thereto, further kept at the temperature for 30 minutes. The reaction mixture was then cooled, and the solid product obtained was pulverized. It was then washed twice with warm acetone, twice with warm water, and further once with warm acetone to obtain a polymer in 97% yield. The polymer had an intrinsic viscosity of 0.80, Tm of 361°C, and Tg of 154°C. The polymer was insoluble at room temperature in such solvents as methylene chloride, chloroform, N,N'-dimethylformamide, sulfolane, dimethyl sulfoxide, hexamethylphosphorictriamide, hexane and toluene. The X-ray diffraction chart and the IR analysis chart of the polymer are shown in Figs. 1 and 3, respectively. The X-ray diffraction and the IR analysis were conducted by using the powder obtained by polymerisation as it was. The result of the elemental analysis of the polymer was as follows. C H O S Found (%) 77.8 4.0 13.7 4.3 Calculated (%) 77.82 4.02 13.76 4.40 The polymer was found to comprise aromatic etherthioether units, consisting of 55% by mole of units (B) and 45% by mole of units (C) according to the formula (1), and units (A) linked alternately. The polymer was pressed at 400°C for 6 minutes to obtain a film. The film was highly resistant to repeated bending and had a tensile strength of 920 kg/cm² and an elongation at break of 80% (as determined according to ASTM D-882). Example 2 Heating was initiated in the same manner as in Example 1 but by using 13.14 g (0.0408 mole) of 4,4'-difluoroterephthalophenone, 3.53 g (0.028 mole) of 4-hydroxythiophenol, 1.32 g (0.012 mole) of hydroquinone 2.76 g (0.020 mole) of anhydrous potassium carbonate, 2.12 g (0.020 mole) of anhydrous sodium carbonate, and 30 g of benzophenone. The reaction mixture was kept at 305°C for 5 hours, then 3.0 g of 4,4′-dichlorodiphenyl sulfone was added thereto, and the mixture was kept at the temperature for 30 minutes. It was then allowed to cool, and treated in the same manner as in Example 1 to obtain a solid. The polymer thus obtained had an intrinsic viscosity of 1.12 and Tm of 359°C. Example 3 In the same manner as in Example 1, 14.63 g (0.0412 mole) of 4,4′-dichloroterephthalophenone, 4.54 g (0.036 mole) of 4-hydroxythiophenol, 0.44 g (0.004 mole) of hydroquinone, 4.42 g (0.032 mole) of anhydrous potassium carbonate, and 30 g of xanthone were placed in the reaction flask and heating was initiated. The mixture was kept at 300°C for 4 hours, then 4 g of 4,4′-difluorobenzophenone was added thereto, and the resulting mixture was further kept at the temperature for 30 minutes. It was then allowed to cool and treated in the same manner as in Example 1 to obtain a solid. The polymer thus obtained had an intrinsic viscosity of 0.76 and Tm of 356°C. Example 4 In the same manner as in Example 1, 13.14 g (0.0408 mole) of 4,4′-difluoroterephthalophenone, 4.03 g (0.032 mole) of 4-hydroxythiophenol, 0.88 g (0.008 mole) of hydroquinone, 5.52 g (0.040 mole) of anhydrous potassium carbonate, and 30 g of diphenyl sulfone were placed in the reaction flask and heating was initiated. The mixture was kept at 310°C for 3 hours, and then methyl chloride was blown thereinto at the temperature for 30 minutes. The reaction mixture was allowed to cool and treated in the same manner as in Example 1 to obtain a solid. The polymer thus obtained had an intrinsic viscosity of 1.01 and Tm of 357°C. Example 5 In the same manner as in Example 1, 13.14 g (0.0408 mole) of 4,4′-difluoroterephthalophenone, 3.02 g (0.024 mole) of 4-hydroxythiophenol, 1.76 g (0.016 mole) of hydroquinone, 3.86 g (0.028 mole) of anhydrous potassium carbonate, and 30 g of thioxanthone were placed in the reaction flask and heating was initiated. The mixture was kept at 310°C for 4 hours, then 3.0 g of 4,4′-difluoroterephthalophenone was added thereto, and the resulting mixture was allowed to react at the temperature for 30 minutes. It was then allowed to cool, and treated in the same manner as in Example 1 to obtain a solid. The polymer thus obtained had an intrinsic viscosity of 0.92 and Tm of 360°C. Example 6 In the same manner as in Example 1, 13.01 g (0.0404 mole) of 4,4′-difluoroterephthalophenone, 2.67 g (0.0212 mole) of 4-hydroxythiophenol, 2.07 g (0.0188 mole) of hydroquinone, 5.63 g (0.0408 mole) of anhydrous potassium carbonate, and 30 g of benzophenone were placed in the reaction flask and heating was initiated. The mixture was kept at 305°C for 2 hours and 30 minutes, then 3.0 g of 4,4′-difluorobenzophenone was added thereto, and the resulting mixture was kept at the temperature for 30 minutes. It was then allowed to cool, and treated in the same manner as in Example 1 to obtain a solid. The polymer thus obtained had an intrinsic viscosity of 0.89, Tm of 356°C, and Tg of 154°C. The polymer showed a thermal weight loss temperature (expressed in terms of the temperature at which the weight loss reached 5% when the temperature of the polymer was increased at a rate of 10°C/min) of 555°C, a markedly improved value as compared with the thermal weight loss temperature of 480°C of a polyphenylene sulfide, Ryton V-l. Example 7 In a 4-necked separable flask equipped with a stirrer, a nitrogen inlet tube and a cooler, which had been replaced by nitrogen, were placed 9.76 g (0.0303 mole) of 4,4′-difluoroterephthalophenone, 2.65 g (0.021 mole) of 4-hydroxythiophenol, 1.93 g (0.009 mole) of 4,4′-dihydroxybenzophenone, 4.14 g (0.030 mole) of anhydrous potassium carbonate, and 30 g of diphenyl sulfone. Heating of the mixture was initiated under nitrogen atmosphere. The reaction mixture was brought to 305°C over a period of 2 hours, kept at the temperature for 3 hours, then 6.0 g of 4,4′-difluorobenzophenone was added thereto, and the resulting mixture was kept at the temperature for further 30 minutes. The reaction mixture was cooled, and the solid obtained was pulverized. It was then washed twice with warm acetone, once with warm water, once with an about 5% aqueous hydrochloric acid solution, twice with warm water, and further once with warm acetone, to obtain a polymer in 96% yield. The polymer had an intrinsic viscosity of 0.89, Tm of 356°C, and Tg of 155°C. The polymer was insoluble at room temperature in such solvents as methylene chloride, chloroform, N,N-dimethylformamide, sulfone, dimethyl sulfoxide, hexamethylphosphorictriamide, hexane, and toluene. The X-ray diffraction chart and the IR analysis chart are shown in Figs. 2 and 4, respectively. The X-ray diffraction and the IR analysis were conducted by using the powder obtained by polymerisation as it was. The result of elemental analysis of the polymer was as follows. C H O S Found (%) 77.5 3.9 13.1 5.2 Calculated (%) 77.61 3.99 13.24 5.16 The polymer was found to comprise aromatic etherthioether units, consisting of 70% by mole of units (B) and 30% by mole of units (C) according to the formula (C₂), and units (A) linked alternately. The polymer was pressed at 400°C for 6 minutes to obtain a film. The film was highly resistant to repeated bending. The film had a tensile strength of 930 kg/cm² and an elongation at break of 75% (as determined according to ASTM D-882). Example 8 Heating was initiated in the same manner as in Example 1 but by using 10.86 g (0.0306 mole) of 4,4'-dichloroterephthalophenone, 2.08 g (0.0165 mole) of 4-hydroxythiophenol, 2.89 g (0.0135 mole) of 4,4'-dihydroxybenzophenone, 4.14 g (0.030 mole) of anhydrous potassium carbonate, and 30 g of xanthone. The reaction mixture was kept at 325°C for 5 hours, then 40 g of 4-fluorobenzophenone was added thereto, and the resulting mixture was kept at the temperature for 30 minutes. It was then allowed to cool, and treated in the same manner as in Example 1 to obtain a solid. The polymer thus obtained had an intrinsic viscosity of 0.68, Tm of 360°C, and Tg of 156°C. Example 9 In the same manner as in Example 1, 9.76 g (0.0303 mole) of 4,4′-difluoroterephthalophenone, 3.40 g (0.027 mole) of 4-hydroxythiophenol, 0.64 g (0.003 mole) of 4,4′-dihydroxybenzophenone, 1.59 g (0.015 mole) of anhydrous sodium carbonate, 2.07 g (0.015 mole) of anhydrous potassium carbonate, and 30 g of benzophenone were placed in the reaction flask and heating of the mixture was initiated. The reaction mixture was kept at 305°C for 3 hours and 30 minutes, then 4.0 g of 4,4′-dichlorodiphenyl sulfone was added thereto, and the resulting mixture was kept at the temperature for further 30 minutes. It was then allowed to cool and treated in the same manner as in Example 1 to obtain a solid. The polymer thus obtained had an intrinsic viscosity of 0.92, Tm of 355°C, and Tg of 153°C. Example 10 In the same manner as in Example 1, 9.76 g (0.0301 mole) of 4,4′-difluoroterephthalophenone, 3.02 g (0.024 mole) of 4-hydroxythiophenol, 1.28 g (0.006 mole) of 4,4′-dihydroxybenzophenone, 0.95 (0.009 mole) of anhydrous sodium carbonate, 2.90 g (0.021 mole) of anhydrous potassium carbonate, and 30 g of benzophenone were placed in the reaction flask and heating of the mixture was initiated. The reaction mixture was kept at 305°C for 4 hours and 30 minutes, then 6.0 g of 4,4′-difluoroterephthalophenone was added thereto, and the resulting mixture was further kept at the temperature for 30 minutes. Then, it was allowed to cool, and treated in the same manner as in Example 1 to obtain a solid. The polymer thus obtained had an intrinsic viscosity of 1.15, Tm of 356°C, and Tg of 154°C. Example 11 In the same manner as in Example 1, 10.86 g (0.0306 mole) of 4,4′-dichloroterephthalophenone, 2.27 g (0.018 mole) of 4-hydroxythiophenol, 2.57 g (0.012 mole) of 4,4′-dihydroxybenzophenone, 4.14 g (0.030 mole) of anhydrous potassium carbonate, and 30 g of diphenyl sulfone were placed in the reaction flask and heating of the mixture was initiated. The reaction mixture was kept at 320°C for 4.5 hours, then 6.0 g of 4,4′-difluoroterephthalophenone was added thereto, and the resulting mixture was allowed to react at the temperature for 30 minutes. The reaction mixture was then allowed to cool, and treated in the same manner as in Example 1 to obtain a solid. The polymer thus obtained had an intrinsic viscosity of 0.72, Tm of 357°C, and Tg of 155°C. Example 12 A 1-liter autoclave was used as the reactor. After the interior of the reaction system was replaced with nitrogen, 95.57 g (0.303 mole) of 4,4′-difluoroterephthalophenone, 20.79 g (0.165 mole) of 4-hydroxythiophenol, 14.85 g (0.135 mole) of hydroquinone, 42.23 g (0.306 mole) of anhydrous potassium carbonate, and 300 g of benzophenone were placed in the autoclave, and the temperature of the resulting mixture was increased while evolved water being removed from the system under a nitrogen gas stream. After brought to 300°C, the reaction mixture was kept at the temperature for 1 hour and 30 minutes, then the nitrogen gas stream was stopped, the autoclave was tightly closed, and the mixture was brought to 330°C and kept at the temperature for 3 hours. Then, 80 g of 4,4′-difluoroterephthalophenone was added to the above mixture, and the resulting mixture was kept at the temperature for 20 minutes and then allowed to cool. The solid thus obtained was washed in the same manner as in Example 1 to obtain 116.4 g of a copolymer. The copolymer had an intrinsic viscosity of 0.96. Test pieces of 3.2 mm thickness were prepared by injection molding from the copolymer. The test pieces showed a tensile strength of 1,250 kg/cm², elongation at break of 80%, flexural modulus of 43,500 kg/cm², Izod impact strength of 3.2 kg·cm/cm, and heat distortion temperature (at 18.6 kg/mm²) of 169°C, as determined according to ASTM D-638, D-790, D-256, and D-648, respectively. Example 13 A copolymer was obtained in the same manner as in Example 1 but by using 13.14 g (0.0408 mole) of 4,4′-difluoroterephthalophenone, 2.02 g (0.016 mole) of 4-hydroxythiophenol, 2.64 g (0.024 mole) of hydroquinone, 5.52 g (0.040 mole) of anhydrous potassium carbonate, and 30 g of benzophenone. The copolymer had an intrinsic viscosity of 0.89 and Tm of 362°C. Example 14 A copolymer obtained in the same manner as in Example 1 but by using 9.76 g (0.0303 mole) of 4,4′-difluoroterephthalophenone, 1.13 g (0.009 mole) of 4-hydroxythiophenol, 4.49 g (0.021 mole) of 4,4′-dihydroxybenzophenone, 4.14 g (0.030 mole) of anhydrous potassium carbonate, and 30 g of diphenyl sulfone. The copolymer had an intrinsic viscosity of 0.81, Tm of 367°C, and Tg of 157°C. Comparative Example 1 A solid polymer was obtained in the same manner as in Example 1 but by using 13.14 g (0.0408 mole) of 4,4′-difluoroterephthalophenone, 5.04 g (0.0400 mole) of 4-hydroxythiophenol, 5.63 g (0.0408 mole) of anhydrous potassium carbonate, and 30 g of benzophenone. The polymer had an intrinsic viscosity of 1.08, Tm of 355°C, and Tg of 152°C. Comparative Example 2 A solid polymer was obtained in the same manner as in Example 12 but by using 97.57 g (0.303 mole) of 4,4′-difluoroterephthalophenone, 7.56 g (0.060 mole) of 4-hydroxythiophenol, 26.40 g (0.240 mole) of hydroquinone, 42.23 g (0.306 mole) of anhydrous potassium carbonate, and 300 g of benzophenone in a 1 ℓ autoclave. The polymer had an intrinsic viscosity of 0.87. Comparative Example 3 A solid polymer was obtained in the same manner as in Example 12 but by using 97.57 g (0.303 mole) of 4,4′-difluoroterephthalophenone, 7.56 g (0.060 mole) of 4-hydroxythiophenol, 51.36 g (0.240 mole) of 4,4′-dihydroxybenzophenone, 42.23 g (0.306 mole) of anhydrous potassium carbonate, and 300 g of benzophenone in a 1 ℓ autoclave. The polymer had an intrinsic viscosity of 0.92. Referential Example 1 1) Preparation of copolymer for nonflammability test Sample A: A copolymer was obtained in the same manner as in Example 1 except that a 1-liter autoclave was used and the reagents were used in 10 times the amount. It had an intrinsic viscosity of 0.89, Tm of 361°C and Tg of 154°C. Sample B: A copolymer was obtained in the same manner as in Example 2 except that a 1-liter autoclave was used and the reagents were used in 10 times the amount. It had an intrinsic viscosity of 1.01, Tm of 358°C, and Tg of 153°C. Sample C: A copolymer was obtained in the same manner as in Example 7 except that a 1-liter autoclave was used and the reagents were used in 10 times the amount. It had an intrinsic viscosity of 0.98, Tm of 356°C, and Tg of 155°C. Sample D: A copolymer was obtained in the same manner as in Example 13 except that a 1-litter autoclave was used and the reagents were used in 10 times the amount. It had an intrinsic viscosity of 0.83, Tm of 362°C, and Tg of 155°C. 2) Polymers used for nonflammability test The copolymers obtained in Examples 1, 2, 3, 7, 8, 9, 13 and 14, the copolymers of Samples A, B, C and D, and, for comparison, an aromatic polyetherketone PEEK (mfd. by I.C.I. Ltd., brand name: Victrex 45 P), polyphenylene sulfides (Ryton P-4 and Ryton R-4, mfd. by Phillips Corp.), and the copolymers obtained in Comparative Examples 2 and 3 were used to determined the oxygen index. The determination was made according to JIS-K7201. Film No. B-l or test piece No. A-l was prepared for the determination. Film No. B-l was prepared by pressing and test piece No. A-l was prepared by means of a small injection machine. 3) Test of nonflammability The determination was made by using a candle-type combustion tester, Type D (mfd. by Toyo Seiki Co.). The results of determination are shown below. As is apparent from the results shown above, the copolymers according to this invention showed excellent nonflammability as compared with prior aromatic polyetherketone (PEEK). Further, they showed equal or superior nonflammability to that of polyphenylene sulfide, which is known to be excellent in nonflammability. Referential Example 2 Determination of crystallization rate The copolymers obtained in Examples 1, 2, and 7 and, for comparison, an aromatic polyetherketone PEEK (mfd. by I.C.I. Ltd., brand name: Victrex 45 P) and the copolymer obtained in Comparative Example 1 were used to determine the crystallization rate. The determination was made by using a DSC. The specimen was brought up to 400°C, then cooled down to a predetermined temperature at a rate of 320°C/min and held at the temperature. The time which elapsed from the beginning of the holding till the appearance of the peak of crystallization was measured. The results of determination are shown below. As is apparent from the results shown above, the copolymers according to this invention showed a high crystallization rate as compared to a homopolymer comprising units (A) and units (B). Further, they showed a crystallization rate equal or superior even to that of prior aromatic polyetherketone. As shown in Referential Examples 1 and 2 above, the copolymer of this invention is a material which has been enhanced in heat resistance (Tm, Tg, and thermal weight loss temperature) while retaining a high nonflammability inherent to polyphenylene sulfide, in other words a material which has been imparted a satisfactory nonflammability without addition of flame retardants while retaining a high heat resistance, molding stability, and mechanical strength which are inherent to aromatic polyetherketone. EFFECT OF THE INVENTION As is clear from the above descriptions including that in Examples, the copolymer of this invention has superior crystallization rate, and good processability for injection molding as compared to a homopolymer comprising units (A) and units (B), and a satisfactory nonflammability similarly to polyphenylene sulfide while retaining excellent heat resistance, molding stability, mechanical strength etc., as compared with prior aromatic polyetherketone. Accordingly, it can be favorably employed under severe conditions of high temperature and particularly for uses which require high nonflammability. The polymer can be used in any desired form including molded articles, coatings, films, and fibers. Further, it can be used after formed into polymer alloys or composite materials by incorporation of various engineering plastics, heat resistant resins, glass fibers, carbon fibers and other inorganic substances.

Claims: A crystalline linear aromatic polyetherthioetherketone copolymer having an intrinsic viscosity of not less than 0.40 wherein structural units (A) represented by the formula alternate with structural units (B) represented by the formula and either structural units (C₁) represented by the formula or structural units (C₂) represented by the formula the molar ratio of said units (B) to said units (C₁) being in the range from 30 : 70 to 99 : 1 the molar ratio of said units (B) to said units (C₂) being in the range from 30 : 70 to 90 :10, and wherein the distribution of the units (B) and (C₁) or (C₂), which are linked with the unit (A), in the copolymer is random, block or alternate. A crystalline copolymer according to claim 1, wherein the intrinsic viscosity is not less than 0.40 and not more than 1.8. A process for producing a copolymer according to claim 1 or 2 which process comprises polycondensing an active-hydrogen containing component consisting of 30 to 99% by mole of 4-hydroxythiophenol and 70 to 1% by mole of hydroquinone, or an active-hydrogen containing component consisting of 30 to 90% by mole of 4-hydroxythiophenol and 70 to 10% by mole of 4,4'-dihydroxybenzophenone, with an amount of 4,4'-dihaloterephthalophenone substantially equimolar to the said active-hydrogen containing component, in at least one member selected from aromatic sulfones and aromatic ketones used as the solvent at a temperature in the range of 200° to 400°C and in the presence of at least one member selected from alkali metal carbonates and bicarbonates. A process according to claim 3, wherein the solvent is a benzophenone compound represented by the general formula wherein R¹ and R² may be the same or different and are each a hydrogen atom, an alkyl group of 1 to 3 carbon atoms, or a phenyl group, provided that when R¹ and/or R² are (is) a phenyl group they (it) may be fused with the benzene ring of the benzophenone skeleton. A process according to claim 4, wherein the solvent is benzophenone. A process according to claim 3, wherein the solvent is a xanthone compound or thioxanthone compound represented by the general formula wherein Y is an oxygen atom or a sulfur atom; R³ and R⁴ may be the same or different from each other and are each a hydrogen atom, an alkyl group of 1 to 3 carbon atoms, or a phenyl group, provided that when R³ and/or R⁴ are (is) a phenyl group, they (it) may be fused with the benzene ring of the xanthone or thioxanthone skeleton. A process according to claim 6, wherein the solvent is xanthone or thioxantone. A process according to claim 3, wherein the solvent is an aromatic sulfone represented by the general formulae wherein R⁵ and R⁶ may be the same or different from each other and are each a hydrogen atom, an alkyl group of 1 to 3 carbon atoms, or a phenyl group, provided that when R⁵ and/or R⁶ are (is) a phenyl group they (it) may be fused with the benzene ring of the aromatic sulfone skeleton. A process according to claim 8, wherein the solvent is diphenyl sulfone.

Inventors: FUKAWA ISABURO, YONEDA HARUYUKI, FUKAWA, ISABURO, YONEDA, HARUYUKI
Applicants: ASAHI CHEMICAL IND, ASAHI KASEI KOGYO KABUSHIKI KAISHA
Application year: 1987
Main classification: C08G75
IPC codes: C08G65, C08G75