MAGNETIC RECORDING MATERIAL

Abstract: Process for preparing magnetic recording material by depositing ferromagnetic material in particulate form into an aluminum substrate. The aluminum substrate is prepared by cleaning an aluminum or aluminum metal containing substrate; anodizing the cleaned metal substrate, to produce a suitably pitted or porous oxide substrate surface; and rinsing the anodized substrate,substantially to remove therefrom acid residues remaining from the anodizing step. The substrate in contact with a liquid solution of a salt of at least one ferromagnetic metal is then subjected to electrolysis with alternating current, to deposit the metal into the pores of the oxide in small-particle, ferromagnetic form while adjusting and controlling the frequency of the alternating current to obtain discrete particles in the pores assembled in an anisotropic configuration. Excess liquid solution is subsequently removed from the so-treated substrate. The material is then preferably coated with a suitable resin or polymer to seal the pores and then polished to generate a suitable surface for reading or writing by magnetic heads.

Description: Title: "Magnetic Recording Material" This invention relates to magnetic recording material and methods for preparation thereof. More particularly, it relates to a form of magnetic recording material which comprise a pitted or porous aluminum oxide film having ferromagnetic particles deposited in the pits and pores therein, and processe for preparation of such magnetic recording materials. State-of-the-art magnetic recording disks are moulded from mixes of fine particles of oxides of iron, cobalt or other ferromagnetic substances and plastic composites. It is very difficult to achieve correct anisotropy of the particles by mea of such a process. This limits the coercivity of these magneti recording disks, which limits the information density which can be recorded by the disk. Coercivity is the magnetic field required to invert t magnetic moment of the magnetic material and hence make a magnetic record. It is desirable to have high coercivity, so that the information density which can be recorded by the magnetic particles can be increased, without their inverting and erasing adjacent information through interactions. To obtain the highest possible coercivity it is necessary to obtain magnetic elements with small individual magnetic domains and the smallest number of domains possible. Single domain particles are ideal. The term "domain" pertains to the concept of individua magnets within a single piece of ferromagnetic material. For example, a lump of iron consists of many domains, each of which is itself a magnet, all these magnets having random polarity so that they cancel out. When a magnetic field is applied, the domains which are aligned with the field grow larger, and those not oriented with the field grow smaller. Eventually one obtain a critical field at which the material is all one single aligned domain. The magnetic mpment of the material is then at its maximum. If one has a collection of single domain particles, the sizes of the domains cannot change, so that the particles sit dormant until a critical field is applied, and then all the domains suddenly invert their polarity. On attaining critical field, the polarities are inverted very suddenly, so that a very square hysteresis loop is obtained from single domain particles. In other words, the material has a large coercive force, a highly desirable property in magentic recording material. Thus to keep a sharp magnetic inversion, it is desirable to have magnetic particles of small and uniform size. Such are not found in state-of-the-art recording disks. The term "anisotropy" refers to the property of being more readily magnetized in one specific direction. If a unit magnetic element having such a property is magnetized, it is relatively difficult to erase. In respect of magnetic tape, it is preferred that the more readily magnetizable direction be along the tape. In respect of a magnetic disk, it is preferred that the more readily magnetizable direction be perpendicular to the plane of the surface of the disk. To enhance or improve anisotropy it is necessary to have particles with a larger dimension perpendicular to rather than parallel to the plane of the surface of the disk. • Such combined small particle size and anisotropy are not found in state-of-the-art recording disks. The problems of obtaining both particles of high coercivity and anisotropy are addressed in U.K. patent number 1,418,933 to Pilot Man-Nen-Hitsu Kabashiki Kaisha. This patent discloses a magnetic recording material comprising aluminum on the surface of which a porous film is deposited by anodic oxidation treatment. Each of the pores contain a magnetic substance deposited therein by electrolytic treatment. However, the coercivities of the materials reported therein do not appear to be any significant improvement over state-of-the-art material. It is an object of the present invention to provide a magnetic recording disk of increased coercivity and improved anisotropy, and processes for their preparation. Accordingly, the invention provides a process for preparing magnetic recording material by depositing ferromagnetic material in particulate form into an aluminum substrate. The aluminum substrate is prepared by cleaning an aluminum or aluminum metal containing substrate; anodizing the cleaned metal substrate, to produce a suitably pitted or porous oxide substrate surface; and rinsing the anodized substrate, substantially to remove therefrom acid residues remaining from the anodizing step. The substrate in contact with a liquid solution of a salt of at least one ferromagnetic metal is then subjected to electrolysis with alternating current, to deposit the metal into the pores of the oxide in small-particle, ferromagnetic form using a frequency of the alternating current adjusted so as to obtain discrete particles in the pores of the oxide substrate surface, assembled in an anisotropic configuration. Excess liquid solution is subsequently removed from the so-treated substrate. The material is then preferably coated with a suitable resin or polymer to seal the pores and then polished to generate a suitable surface for reading or writing by magnetic heads. According to a second aspect of the invention there is provided a magnetic recording material. This material consists of a substrate of aluminum or aluminum alloy containing a high proportion of aluminum; and at least one ferromagnetic metal selected from cobalt, nickel and iron. The at least one metal is present in the pores of the oxide in discrete, micro-particulate form, piled into pits and pores created in the substrate surface in an anisotropic configuration by anodizing thereof. The magnetic recording material has a coercivity in excess of 2000 oersted. With cobalt, coercivities of 2030 oersted have been achieved in the perpendicular direction; while with iron a coercivity of 2220 oersted has been achieved in the perpendicular direction. For the same two materials the parallel coercivities were both 910 oersted indicating the high degree of anisotropy. With mixtures of Co and Fe a perpendicular coercivity of 2570 oersted can be obtained. Coercivities at least as high as 3000 oersted can be achieved according to the invention. With the present invention, when a ferromagnetic metal such as iron, cobalt or nickel or a mixture thereof is chosen as the metal for deposition, and the frequency of applied alternating current for the electro depositions step is correctly controlled and adjusted, magnetic recording materials of very high quality can be obtained. In fact, magnetic recording materials of up to twice the coercivity of such similarly prepared materials disclosed in the aforementioned U.K. patent 1,418,933 can be obtained according to this invention. The preferred process according to the invention uses, in the electrodeposition step, a partially rectified AC current in the range of 75 to 2500 and preferably 200 to 500 Hz; also, the pH of the electrodeposition bath is adjusted to a highly acid value, in the range 2.7 - 3.7 and for Co and Fe preferably in tne range 2.8 - 3.5. The substrate of the magnetic recording material of the present invention is aluminum metal or an alloy or composition thereof, e.g. aluminum-magnesium alloy, containing at least a major proportion of aluminum metal. It is suitable and convenient to use aluminum in the form of thin metal foil, for example the type of foil commonly used in domestic cooking applications. Such a form of substrate lends itself well to continuous handling and treatment, being available in long rolled lengths capable of being rolled and unrolled continuously. However, the invention is not limited to any specific form of aluminum substrate, and is applicable to use with aluminum strips, rods, sheets, plates, films and the like. Thus, the magnetic recording material of the present invention may be made from an aluminum sheet substrate, which is cleaned, anodized and onto which the chosen metal is electrolytically deposited as described herein, following which the sheet may be cut into coupons. Alternatively, the ferromagnetic metal may be deposited, by the techniques described herein, onto aluminum particles, spheres, gauze, wire, chips, flakes or wool. As an early step in the process of the present invention, the substrate is cleaned for the purpose of removing grease from the surface thereof. This is best accomplished with a suitable organic solvent and then with an alkaline chemical liquid, so as to achieve a degree of surface etching, followed by neutralization of any residual alkali excess with acid. Sodium carbonate solution is a suitable base, followed by nitric acid, but many other chemicals can be chosen and used for this purpose. The preferred cleaning process is ultrasonic cleaning in dichloro ethane, followed by treatment with dilute sodium carbonate and then with dilute nitric acid. It may also be desirable to remove oxide formed during the etching process. Then the treated substrate is electrolytically anodized, for the purpose of depositing on the metal a surface porous layer of oxide. This anodizing is best accomplished by making the metal the anode of an electrolytic cell, using inert (e.g. lead) counter-electrodes, in an acidic bath. Suitably, the bath is a relatively dilute solution of an inorganic acid, such as sulphuric acid or phosphoric acid or an organic acid such as oxalic acid. In practice, a 13.8% sulphuric acid solution has been found to be most satisfactory, in providing pores of suitable diameter. Direct current is passed through the cell between the electrodes, at a current and voltage suitably adjusted to provide the correct film deposition. This operation is suitably conducted at room temperatures. In practice, a current of the order of 15 milliamps per square centimeter, at a voltage of 15 volts, in 13.8% by weight sulphuric acid has been found to provide suitable surface oxide characteristics. For best use in the present invention, the pores in the aluminum oxide surface should be fairly small but not too small. They should be large enough to contain single domain magnetic particles, but not so small as to contain super-paramagnetic particles or so large as to contain multidomain particles. If the pores are too small, the ferromagnetic character of the metal particles therein will be lost. One should avoid pores large enough to hold particles o of smallest diameter greater than 350 A. The height of the pores o o is controllable between 2,000 A and 50 microns (500,000 A). The height of the pores is not controllable at heights less than o 2 r 000 A. It is desirable to keep the pores as shallow as possible as the particles deposit at the bottom of the pores and for the most efficient recording the particles should be as close as possible to the magnetic head of the recorder. There is no o significant difficulty in obtaining pores of depth 2000 A, and with such shallow depths it is preferred to fill them with deposited ferromagnetic metal, as described below. The deposited metal should not protrude beyond the pore opening. After suitable anodizing as described, the substrate is removed from the anodizing bath and rinsed. It is important to rid the surface of the treated substrate of residual acid, and neutralize it at this point. It is, however, undesirable to neutralize the acid chemically,, since this might have the effect of damaging the deposited film. However, if residual acid is left at the subsequent electrolysis step, hydrogen will be generated, which is undesirable. It is preferred to rinse the anodized film with suitable quantities of water, to remove acid and effect sufficient neutralization. After rinsing, the material is not dried, otherwise the pores may seal up. Next, the ferromagnetic metal or metals are deposited electrolytically into the so-prepared substrate. In this process, the substrate is placed in an electrolyte having dissolved therein ions of the metal or metals to be deposited, along with an inert counterelectrode, e.g. graphite, and alternating current is passed between the two electrodes in the electrolyte. Normally the electrolyte will be an aqueous solution of suitable salts of the metals to be deposited, but it can under certain circumstances if desired be a non-aqueous solution. The concentration range of the salt can be from 5% up to saturation. When cobalt is to be deposited, (cobalt sulfate) is suitably dissolved in the electrolyte medium. One should avoid use in the electrolyte bath of salts of metals which contribute to the solution anions which would themselves harm the coating on the aluminum substrate during the process, e.g. by oxidation. An inhibitor, e.g. citric acid or ascorbic acid is preferably added to the electrolyte, especially when using iron, to prevent oxidation of the ferrous material to ferric material. It is believed that the particles should have a size o measured across their smallest diameter of from 30 to 350 A, o optimally about 100 A. The lower critical limit is somewhere in o the range of 30-80 A, at room temperature, depending upon the nature of the material. Concentrations of metal compound and other constituents in the electrolyte have some effect on the particle size, pH has a greater effect but the frequency and rectification of the alternating current have the greatest effect. The frequency of the alternating current affects the nature of the deposited metal. The use of alternating current in this electrolysis step is essential in the process of the invention. Alternating current causes the metal ions to become reduced (or in some cases oxidized) and deposited as metals in the porous oxide coating, in the desired small particle form. Typically the alternating current is passed for at least 2-3 minutes. Results indicate that there is an initial surge of metal deposition, the rate of which rapidly declines after the first few minutes. Times of about 10 minutes at 14 volts RMS alternating current have been found suitable when depositing cobalt from (cobalt salt) in a boric acid containing bath. A suitable voltage range for cobalt is 10-20V. Saccharin may be added to the electrolyte as a stress reducer, preferably in the form of a saccharin salt. This has the effect of improving particle size uniformity especially when using cobalt. It was previously found difficult to obtain even, uniform particles when using cobalt. The pH is a factor inside the pore, as the particle grows therein under the influence of the alternating current. The presence of hydrogen ions in the pores will affect the dynamics of particle growth. A certain pH is needed for the metal compound to be reduced to the metal, and each metal has its own preference where pH is concerned. It is preferred to maintain the electrolyte at a substantially constant, strongly acidic pH, in the 2.7 - 3.7 range. For cobalt the pH should be between 2.8 - 3.7, for nickel 3.6 - 3.7, and for iron 2.7 - 3.0. This is suitably done by addition to the bath of appropriate quantities of weak acid such as boric acid, to avoid substantial evolution of gaseous hydrogen during the process. The amount of ferromagnetic metal deposited, as oppose to the nature and structure of the deposit, is controlled by the ferromagnetic salt solution concentration in the electrolytic bath, and the time for which deposition takes place. It is best to arrange these conditions so that the metal deposits in the o pores are at least 2000 A in depth, which in some instances will represent a complete filling of the pores of the substrate, up to a depth representing complete filling of the pores, which could be a depth of 500,000 A. This depth of deposit, which will normally correspond to a partial filling of the pores of the o o substrate, is preferably from about 5000 A to 100,000 A, and is controlled by solution concentration, deposition time and choice of anodizing acid. For example, when phosphoric acid is used in the anodizing bath, it is difficult to obtian pores of size o greater than 20,000 A, hence limiting the metal deposit depth to that maximum. To obtain the optimum coercivity and anisotropy of the magnetic elements, it is necessary initially to adjust the frequency of applied alternating current during deposition, e.g. by using a variable frequency power supply. Any given system of metal salt or metal salt combination, acidity, bath composition, substrate nature, coating nature, etc. is likely to have its own optimum AC frequency, best determined by initial experiments. Invariably, however, the frequency is at least 75 Hz, to obtain good results in this invention, and preferably at least 200 Hz. The optimum alternating current waveform is partially rectified, which when plotted out would show a sine wave form in which the peaks above zero are of a different amplitude from the peaks below zero. This assists in controlling particle growth and hence the particle size. Most preferred among the ferromagnetic materials of use in the present invention is cobalt, which can give materials having twice the coercivity of the prior art. Iron can give improved results over the prior art, but only cobalt can give an improvement in coercivity of up to a factor of two. Following the electrolytic deposition of the metal, the treated metal substrate is suitably rinsed and cleaned, to rid the metal of residual boric acid. It may further be cleaned, e.g. by ultrasonic cleaning in ethanol. In practice these final cleaning steps to remove the residual boric acid are best conducted prior to use of the material since it appears that the residual boric acid may afford some protection against deterioration of the surface quality of the material on storage. Finally, if desired, the magnetic recording material may be coated with a suitable resin, polymer or plastic to seal the pores and then polished to generate a suitable surface for magnetic reading and recording. The invention is further illustrated in the following specific examples. EXAMPLE 1 Magnetic recording materials were prepared using the • method of the preferred embodiment of the invention. Anodic films were prepared on aluminum substrates in one of two ways. These two ways respectively used: (a) 1.0 M H 3 P0 4 solution, 5mA/cm 2 against a lead electrode, at 23°C to create a phosphoric acid film; and (b) 1.5 M H 2 S0 4 , 16mA/cm 2 against a lead electrode at 23°C to create a sulphuric acid film. The anodizing voltage was varied from 10 to 20V DC for the various substrates and films were deposited on the substrates. The compositions of the metal deposition baths used were as follows: 1. Cobalt bath 120g/l CoS0 4 .7H 2 0 45g/l H 3 BO 3 1.0 - 1.5g/l saccharin pH 2.8 - 3.7 2. Nickel bath 120g/l NiS0 4 .6H 2 0 45g/l H 3 BO 3 pH 3.6 - 3.7 3. Iron bath I20g/1 FeS0 4 .7H 2 0 45g/l H 3 BO 3 0.5 - 1.5g/l ascorbic acid pH 2.7 - 3.0 4. Iron/Cobalt bath 36g/l FeS0 4 .7H 2 0 84g/l CoS0 4 .7H 2 0 45g/l H 3 BO 3 1.0 - 1.5g/l saccharin 0.5 - 1.5g/l ascorbic acid pH 2.8 - 3.7 Sulfuric films deposited on aluminum were placed in either cobalt, nickel, iron or iron/cobalt baths, and phosphoric films were placed in a nickel bath. Electrodeposition of the metal in the bath into the substrate was done with 14V RMS of AC variable frequency 50 to 500 Hz against graphite electrodes. The results of the deposition were as given in the following tables. Figures 1 to 3 show hysteresis loops for the results in Tables I, IV and V respectively. TABLE (I) Cobalt (in. sulfuric acid films 15V DC) deposition frequency squareness coercivity squareness coercivity time Hz (perpendicular) (perpendicular (parallel) (parallel oersted) oersted) 1) 30 sec 200 0.87 1770 0.14 580 2) 3 min 200 0.90 1730 0.20 885 3) 10 min 200 0.92 1900 0.157 740 4) 20 min 200 0.916 2030 0.186 910 5) 3 min 50 0.87 1720 — — 6) 3 min 500 0.84 1850 0.21 910 These experiments indicate that the time of deposition should be longer than three minutes, and preferably 10-20 minutes for optimum results under these conditions. Indications are that the frequency of 50 Hz is too low for obtaining best results, as evidenced by the relatively low coercivity figure and perpendicular squareness of the experiment 5. That a frequency of 50 Hz is unsatisfactory for obtaining good products with high coercivity has been confirmed in other experimental work, using fixed, preferred times of deposition in the 10-30 minute range. The frequency should not be lower than bout 75 Hz, whatever time of deposition is chosen. The deposition of the correct amount of metal as determined by the deposition time and solution concentration, and the frequency which determines the nature of the deposited metal structure, are normally optimized in combination with one another. For a given substrate, an optimum combination of values giving deposition amounts within the aforementioned ranges can readily be formed by routine experimentation and adjustment, to obtain an optimum product. A typical hysteresis curve is shown in Figure 1, which refers to sample 3 in the, above table. On the basis of the experimental results reported in Table 1, in which the frequency was adjusted to find an optimum range or value, subsequent experiments reported in this example were conducted at a constant frequency of 200 Hz. TABLE (II) Nickel (in sulfuric acid films 15V DC) deposition frequency squareness coercivity squareness coercivity time Hz (perpendicular) (perpendicular (parallel) (parallel oersted) oersted) 1) 3 min 200 0.83 540 0.13 255 2) 20 min 200 0.78 420 0.12 175 TABLE (III) Nickel (in phosphoric acid films) anodizing deposition frequency squareness coercivity squareness coercivit_ voltage time Hz (perpendicular) (perpendicular) (parallel (parallel oersted) oersted) 1) 15 30 sec 200 0.37 540 0.26 185 2) 15 1 min 200 0.43 660 0.20 240 3) 15 2 min 200 0.41 640 0.21 260 4) 15 5 min 200 0.42 600 0.20 260 5) 20 5 min 200 0.44 615 0.19 230 6) 25 5 min 200 0.44 595 0.19 250 TABLE (IV) Iron (in suilfuric acid films) anodizing deposition frequency squareness coercivi ■ty squareness coercivity voltage time Hz (perpendicular) (perpendicular) (parallel (parallel oersted) oersted) 1) 15 30 sec 200 0.75 1220 0.22 970 2) 15 3 min 200 0.84 1850 0.17 770 3) 15 10 min 200 0.91 2220 0.163 910 4) 15 20 min 200 0.90 2180 0.22 1200 The hysteresis curves for iron in sample 3 is shown in Figure 2. TABLE (V) Iron/Cobalt mixtures 0.3/0.7 moles % in deposition bath anodizing deposition frequency squareness coercivity squareness coercivity voltage time Hz (perpendicular) (perpendicular) (parallel (parallel oersted) oersted) 1) 15 15 sec 200 0.92 2570 0.15 910 The hysteresis curve for this mixed metal sample is shown in Figure 3. Materials having high coercivity with hysteresis loops having a high degree of squareness were thereby obtained.

Claims: Claims : 1. A process for preparing magnetic recording material comprising the steps of: cleaning an aluminum or aluminum metal containing substrate; anodizing the cleaned metal substrate, to produce a suitably pitted or porous oxide substrate surface; rinsing the anodized substrate, substantially to remov therefrom acid residues remaining from the anodizing step; subjecting the substrate in contact with a liquid solution of a salt of at least one ferromagnetic metal to electrolysis with alternating current, to deposit the metal into the substrate in small-particle, ferromagnetic form at an adjusted and controlled frequency of said alternating current to obtain discrete particles in the pores aggregated in an anisotropic configuration; and removing excess liquid solution from the so-treated substrate. 2. The process of claim 1 wherein said alternating current is partially rectified, and has a frequency in the range 75 to 2500 Hz. 3. The process of claim 2 wherein the AC electrolysis step is conducted in a metal salt solution of pH 2.7 - 3.7. 4. The process of claim 1 wherein said ferromagnetic metal is selected from cobalt, iron, nickel and combinations thereof. 5. The process of claim 1 wherein the substrate is aluminum foil or sheet. 6. The process of claim 5 wherein the process is conducted continuously by passing a continuous long length of aluminum foil or sheet through successive cleaning, anodizing, rinsing, AC-electrolγzing and final cleaning stations, with appropriate residence times in each station. 7. The process of claim 4 wherein said liquid solution of at least one ferromagnetic metal also contains a stress-reducing agent. 8. The process of claim 1 wherein said liquid solution also contains oxidation inhibitors. 9. The process of claim 1 wherein the metal particles deposited into the pores of the substrate are between 30 A and 350 A in diameter. 10. The process of claim 1 further including the step of coating the treated substrate with plastic to seal the pores, and polishing said plastic. 11. A magnetic recording material comprising: a substrate of aluminum or aluminum alloy containing a high proportion of aluminum; at least one ferromagnetic metal; said at least one metal being present near the surface of the substrate in discrete, micro-particulate form, piled into pits and pores created in the substrate surface in an anisotropic configuration; and said magnetic recording material having a coercivity in excess of 2000 oersted in the perpendicular direction. 12. The magnetic recording material of claim 11 wherein said metal is selected from cobalt, nickel and iron or mixtures thereof. 13. The magnetic recording material of claim 11 wherein said metal is in the form of particles between 30 and 350 A in diameter. 14. The magnetic recording material of claim 16 wherein said particles are substantially single domain particles. 15. The magnetic recording material of claim 16 wherein said metal is a mixture of cobalt and iron and said coercivity in excess of 2570 oersted.

Inventors: MOSKOVITS MARTIN, SCHMIDHALTER BEAT, MOSKOVITS, MARTIN, SCHMIDHALTER, BEAT
Applicants: UNIV TORONTO, WALSH PAULINE MARGARET, THE UNIVERSITY OF TORONTO INNOVATIONS FOUNDATION, WALSH, PAULINE, MARGARET
Application year: 1987
Main classification: G11B5
IPC codes: G11B5, H01F1