TITANIUM-CLAD STEEL AND METHOD FOR THE MANUFACTURE THEREOF

Abstract: A titanium-clad steel with improved bonding properties and a method for the manufacture thereof are disclosed. The titanium-clad steel is characterized by comprising a Ti-cladding, a base metal steel, and an insert between them, the insert being made of an alloy consisting essentially of, in % by weight, 0.05% or less of carbon, 3 to 20% by weight of at least one of niobium (Nb) and vanadium (V), and a balance of iron.

Description: This invention relates to a titanium-clad steel with a high bonding strength and to a method for its manufacture. Titanium-clad steel has been manufactured by the explosive cladding method, which is advantageous in that the formation of intermetallic compounds is markedly suppressed since the bonding area is not heated to high temperatures, bonding being achieved by heavy working. However, the explosive cladding method has drawbacks regarding noise, productivity, and manufacturing costs. As a method to eliminate these drawbacks, a rolling method for manufacturing a titanium-clad steel has been developed. In carrying out the rolling method, important factors are (i) an insert to be placed between the steel base metal and Ti cladding, (ii) conditions for assembling with welding as well as for evacuating the assembly, and (iii) heating temperatures for rolling. Among these factors, it is most important to select an insert particularly suitable for avoiding the formation of brittle intermetallic compounds in the bonding area. Titanium easily forms intermetallic compounds with various other elements. There are only a few elements such as Mo, Nb, and V that do not form any intermetallic compounds with titanium. However, it is rather difficult to use such materials as an insert, since they are expensive and usually not available in the form of a thin plate. In addition, if they are used as an insert, they are easily broken during rolling. The purpose of using an insert for manufacturing titanium-cladding steel is to prevent the formation of intermetallic compounds as well as a brittle titanium carbide layer caused by diffusion of carbon from the base metal steel to the Ti cladding in the bonding area between the titanium or titanium alloy and the base metal steel. In the prior art, in order to prevent the formation of titanium carbides in the bonding area it has been proposed to use a nickel insert (Japanese Patent application No. 146763/1985), and a pure iron or ultra-low carbon steel insert (Japanese Patent Application Laid-Open Specification No. 122681/1981), and to carry out decarburization of the base metal steel on the titanium-facing side prior to cladding (Japanese Patent Application Laid-Open Specification No. 220292/1984). The diffusion rate of nickel in titanium is large and the transformation of Ti from alpha-phase to beta-phase due to the diffusion of Ni into Ti during heating and rolling, further accelerates the diffusion of nickel into the Ti cladding. Therefore, the temperature range which can be employed is very restricted. Thus, a nickel insert is less desirable than ferrous inserts. However, the formation of intermetallic compounds is unavoidable even if a ferrous insert is used. Once formed, such intermetallic compounds grow during spinning, welding, strain-releasing annealing, and other processes which follow cladding, resulting in a deterioration in bonding properties. Thus, in order to achieve stable and improved bonding properties, it is necessary to develop an insert with which there is no formation of intermetallic compounds in the boundary area between the Ti cladding and the insert, or which can delay the formation and growth of such intermetallic compounds. GB-A-1 042 603 discloses a composite metallic plate consisting of a Ti-cladding bonded to a base metal steel through an intermediate layer of metallic bonding material consisting of an iron-base alloy which comprises niobium or vanadium. EP-A-0 060 083 discloses a titanium-clad steel comprising a Ti-cladding, a base metal steel, an insert between them of niobium or a niobium alloy and a supplemental intermediate layer of nickel or a nickel alloy between said base metal and said insert. As far as an intermediate layer of tantalum or niobium or alloys thereof is concerned, this document describes an explosive cladding method or a diffusion bonding method for making clad steel. The object of this invention is to provide a titanium-clad steel which is less expensive and is substantially free from intermetallic compounds in the bonding area between the Ti cladding and the base metal steel and a method for the manufacture thereof. More specifically, the object of this invention is to provide a titanium-clad steel exhibiting a shear strength of 137 N/mm² (14 kgf/mm²) ore more as defined in JIS G 3603 (Ti-clad steels) even after being reheated to high temperatures, and a method for the manufacture thereof. The inventor of this invention has noted that (i) niobium and vanadium do not form intermetallic compounds with titanium, (ii) Fe-V and Fe-Nb alloys can be worked more easily than Fe-Mo alloys and the former alloys can be rolled to form a thin plate, which is useful as an insert, and (iii) these metals are carbide-formers and effective to prevent the formation of Ti-carbides caused by diffusion of carbon from the base metal. With the above in mind, the inventor has conducted a series of experiments and found that a ferrous insert containing Nb and V in an amount of 3% or more markedly inhibits the formation of intermetallic compounds of Ti and Fe and that these intermetallic compounds are not formed when the content of Nb and V is increased. This is because V and Nb are stabilizers for the beta-phase of Ti and broaden the beta-phase range due to a diffusive dissolution of these elements into Ti to suppress the formation of intermetallic compounds between Fe and Ti. Thus, according to this invention a ferrous alloy containing Nb and V is used as an insert. According to this invention, it is possible to provide a titanium-clad steel exhibiting stable and improved bonding properties. However, when it is heated for an extended period of time at a temperature over 600°C or 650°C during working or servicing, carbon from the base metal steel and Nb and V of the insert react to form a layer of carbides such as NbC and VC, which deteriorates the bonding properties. The inventor of this invention has found that the provision of a nickel layer between the insert and the base metal can successfully prevent the diffusion of carbon from the base metal while producing no adverse effects on the insert of the ferrous alloy. Thus, in one aspect, this invention is a titanium-clad steel with improved bonding properties comprising a Ti-cladding, a base metal steel, an insert between them and an intermediate layer between said base metal steel and said insert, the insert being made of a ferrous alloy consisting of, in % by weight, 0.05% or less of carbon, 3 to 20% by weight of at least one of niobium (Nb) and vanadium (V), a balance of iron and normal impurities, and said intermediate layer being made of nickel (Ni) or a nickel alloy. The inventor of this invention has also found that austenitic alloys with a fcc crystal structure such as austenitic stainless steels are very effective to successfully prevent diffusion of carbon from the base metal steel, and that the diffusion of carbon is determined by the crystal structure of the matrix phase, and the diffusion rate of carbon in the closed-packed structure is small, i.e., 0.1 mm for 100 hours at 600°C. Thus, in another aspect, this invention is a titanium-clad steel with improved bonding properties, comprising a Ti-cladding, a base metal steel, an insert between them and an intermediate layer between said base metal steel and said insert, the insert being made of a ferrous alloy consisting of, in % by weight, 0.1% or less of carbon, 1 to 20% by weight of at least one of niobium (Nb) and vanadium (V), a balance of iron and normal impurities, and said intermediate layer being made of a Fe-Ni-Cr austenitic alloy containing the amounts of Ni and Cr as defined by the following formulas, in % by weight; Cr ≦ 18%, Ni ≧ - 0.78Cr% + 26 Cr > 18%, Ni ≧ 1.13(Cr% -18) + 12 wherein, Cr% + Ni% ≦ 100. In a still another aspect, this invention is a method of manufacturing a Ti-clad steel with improved bonding properties as defined above, the method comprising preparing a cladding assembly of the Ti-cladding, the base metal steel, the insert placed between them, and the intermidiate layer placed between said base metal steel and said insert, heating the cladding assembly or the bonding area at a temperature of 680 to 900°C, and preferably 700 to 870°C, and effecting bonding under pressure. The preparation of the cladding assembly comprises sealing the assembly of the Ti-cladding, the insert, the intermediate layer, and the base metal steel, degassing, and evacuating the assembly. The Ti cladding may include pure titanium and titanium alloys. The base metal steel is not restricted to a specific one, but preferably it is selected from carbon steels and low-alloy high-strength steels. The insert may be a powder layer, powder coating layer, or electroplated layer placed on the base metal. The austenitic alloy may contain 0.1% by weight or less of carbon, and it may contain Mn, Si, Mo, Ti, Nb, and other alloying elements in a total amount of 5% by weight or less. Fig. 1 is a diagramatic sectional view of a cladding assembly of this invention; Fig. 2 and Fig. 3 are graphs showing the test results of the working examples of this invention; Fig. 4 and Fig. 5 are graphs showing relationships between the growth of intermetallic compounds and heating time for Nb- and V-bearing inserts, respectively; and Fig. 6 is a graph showing the Ni and Cr content of alloys used as an intermediate member. This invention will now be described in conjunction with the attached drawings. Fig. 1 shows a diagramatic sectional view of a cladding assembly 1 prior to bonding. The assembly 1 comprises Ti cladding 2 and a base metal steel 3, an insert 4 of a ferrous alloy placed between them, and an intermediate member 5 of a nickel or an austenitic alloy. The thickness of the insert is preferably 0.5 mm or more, and usually 1 mm or more. The thickness of the intermediate member is generally greater than 50 µm, and preferably greater than 100 µm, but is thinner than the insert. A cover 6 is disposed over the whole of the assembly, and is seal-welded to the base metal steel. The inside thereof is degassed and evacuated, preferably to 13.3 Pa (10⁻¹ Torr) or less. The evacuation is carried out in order to suppress oxidation of each of the bonding surfaces. When a predetermined level of vacuum is achieved, the whole of the assembly or at least the bonding area thereof is heated to 680 to 900°C, and preferably 700 to 870°C, and is hot rolled to effect cladding. After the rolling, the cover 6 is removed to obtain a Ti-clad steel. Each of the steps mentioned above is known in the art as a rolling method to achieve cladding except for the above-specified heating conditions. The reasons for the restrictions on the composition of the insert employed in this invention will be described in more detail. First, the carbon content is defined as 0.05% or less in order to have V and Nb as active as possible. For this purpose, the lower the carbon content the better. When the carbon content is over 0.05%, Nb and V easily react with carbon to form carbides thereof, causing cracks during cold rolling which is employed to prepare an insert in the form of a thin plate. The upper limit on the carbon content is therefore set at 0.05%, since a satisfactory level of the shear strength can be obtained even when the content of carbon is restricted to 0.05% or less. In case the Fe-Ni-Cr alloy is used as the intermediate member between the insert and the base metal, the upper limit of carbon may be 0.1%. Regarding the content of Nb and V, the total amount thereof is restricted to 3.0% or more. In case the Fe-Ni-Cr alloy is employed in place of the nickel plate as the intermediate member, the lower limit of a total amount of Nb and V may be 1.0%. It is not always necessary to specify an upper limit thereon, but in view of the material costs, the upper limit thereof is restricted to 20%. Preferably, the total amount of Nb and/or V is 5 - 15%. Such a ferrous alloy insert may be placed on the base metal steel in the form of a thin plate or a foil. The insert may be formed by means of powder coating. In this invention, an additional insert, i.e., the intermediate member is employed in order to further improve the bonding properties. The intermediate member may be a nickel plate or nickel alloy plate. The nickel plate may be of industrial-grade pure nickel. The purity and the content of impurities do not have any substantial effects. The nickel alloy may include commercial nickel alloys such as Permalloy (50%Ni - 50%Fe) -- tradename -- and invar alloys (36%Ni - 64%Fe). The nickel intermediate member may be in the form of a foil. This layer may also be formed by means of electroplating or powder coating. Since one of the purposes of providing the intermediate member is to prevent the carbon of the base metal from diffusing and permeating into the ferrous alloy insert when reheating after rolling, the thickness of the intermediate member is expressed in terms of thickness after rolling. If it is expressed in this way, a thickness of 5 µm or more is enough. On the other hand, regarding the intermediate member of Fe-Ni-Cr alloys which may be used in place of the nickel intermediate member between the insert and the base metal steel, the crystal structure is to have an austenitic phase (fcc phase) in order to prevent diffusion of carbon from the base metal steel. As long as it has an austenitic phase, there is no limit regarding the intermediate member. Fe-Ni-Cr alloys which comprise an austenitic phase (fcc phase) are austenitic alloys containing the amounts of Ni and Cr defined by the following formulas, in % by weight; Cr ≦ 18%, Ni ≧ - 0.78Cr% + 26 Cr > 18%, Ni ≧ 1.13(Cr% -18) + 12 wherein, Cr% + Ni% ≦ 100. The austenitic alloy intermediate member may be in the form of a foil. This layer may also be formed by means of electroplating or powder coating. Fig. 6 is a graph showing the Ni and Cr content of alloys used as an intermediate. The hatched area in the graph indicates an austenitic alloy, and the other area indicates ferrite or ferrite + austenite dual-phase alloys. The reference numerals in the graph refer to the alloy numbers of Table 3 to be detailed hereinafter. The presence of Fe does not have any substantial effects on the formation of an austenitic phase, and the Fe content does not have any upper limit. However, the Ni content should be as low as possible because Ni is expensive. The remainder is iron with incidental impurities. Therefore, it is desirable that the Fe content be as high as possible. When the austenitic alloy contains more than 0.1% of carbon, the diffusion of carbon sometimes occurs so much that Ti carbides form, producing a decrease in bonding strength. Thus, it is desirable that the carbon content be restricted to 0.1% or less. In addition, when the total amount of other alloying elements such as Si, Mn, Mo, Ti, and Nb is more than 5% by weight, the austenitic phase becomes unstable. Thus, the total content of these elements, if present, is restricted to 5% by weight or less. There is no specific restriction on the thickness of the intermediate member. The thickness is determined in view of reheating temperatures and reheating time after rolling. In most cases, a thickness of 5 µm or more after cladding by rolling is enough. The upper limit may be determined based on the circumstances. A cladding assembly is heated to a predetermined temperature and then is subjected to bonding under pressure. In the case of this invention, the bonding area or the whole of the cladding assembly is heated to 680 to 900°C, preferably 700 to 870°C, and then is subjected to bonding under pressure. When the assembly is not heated to 680°C or higher, and preferably 700°C or higher, the interdiffusion is not thorough, and a more powerful rolling apparatus is necessary to carry out rolling. In contrast, when the assembly is heated to a temperature higher than 900°C, transformation of the Ti cladding into beta-phase takes place or the formation of beta-phase is accelerated. As a result, the diffusion rate of Ti becomes too great, accelerating the formation of intermetallic compounds, so that the bonding strength does not satisfy specifications. Therefore, in this invention, the upper limit on the heating temperature is defined as 900°C, and preferably 870°C. A typical means of carring out bonding under pressure is rolling. It may also be performed by forging and the like, which are suitable methods for carrying out bonding of small-sized articles. This invention will be further detailed with reference to working examples, which are presented merely for illustrative purposes. Reference Example 1: A plate of low-alloy high-strength steel of 490 N/mm² (50 kgf/mm²) grade, 90 mm thick, was machined to give a flat surface and degreased. This plate was the base metal. A Ti-plate (JIS first grade), 10 mm thick, was used as the Ti cladding. These members were assembled by means of welding to give the cladding assembly shown in Fig. 1. In this example, the intermediate member 5 was deleted. As the insert 4, a lot of materials shown in Table 1 were employed in the form of a sheet 1 mm thick. The inside of the cladding assembly was evacuated to a pressure of 40 Pa (3 x 10⁻¹ Torr), and then was closed. After heating, bonding under pressure was carried out to provide a 20-mm thick Ti-clad steel. The thus-manufactured Ti-clad steels were then subjected to the shearing tensile test defined in JIS G 0601 to evaluate the bonding properties. When the heating temperature was within the range of 700 - 800°C, the shear strength was over 137 N/mm² (14 kgf/mm²) for each of the specimens. In order to evaluate a change in the shear strength after reheating, the shear strength after reheating at 850°C for 10 hours was determined. For the steel of this invention, the shear strength was 137 N/mm² (14 kgf/mm²) or more, showing improvement in bonding properties. The test results are summarized in Table 1 and the relationships between the shear strength of the as-rolled specimens and that of the specimens after being reheated are shown in Figs. 2 and 3, respectively. The relationships between the content of Nb and V of the ferrous alloy insert and the growth of intermetallic compounds were evaluated. Figs. 4 and 5 show graphs of the thickness (µm) of intermetallic compounds with iron in the boundary of the base metal steel, which are plotted with respect to the heating time (second) at 850°C when the contents of Nb and V are varied. In these cases, when the content of Nb and V is 3% or more, there is no longer a significant degree of formation of intermetallic compounds, When the content goes over 20%, the effect thereof saturates. Example 2: In this example, Reference Example 1 was repeated except that the intermediate member 5 of industrial-grade pure nickel was used in the form of a foil 100 µm thick. In this example, too, when the heating temperature was within the range of 700 - 800°C, the shear strength was over 137 N/mm² (14 kgf/mm²) for each of the specimens. In order to evaluate a change in the shear strength after reheating, the shear strength after reheating at 850°C for 10 hours, 30 hours, and 100 hours was determined. For steels of this invention, the shear strength was 137 N/mm² (14 kgf/mm²) or more even after being reheated at 850°C for 100 hours, showing a remarkable improvement in bonding properties. The test results are summarized in Table 2. Example 3: In this example, Example 2 was repeated except that a Fe-Ni-Cr alloy in a foil 100 µm thick was used in place of the Ni member as the intermediate member. In order to evaluate the bonding properties after reheating, the test pieces were heated to 850°C for 100 hours, and the change in shearing strength was determined. The alloying compositions of austenitic alloys of the intermediates employed in this example are shown in Table 3. The test results are summarized in Table 4. As is apparent from the test results shown in Table 4, according to this invention, the shear strength of the as-rolled steel was 196 N/mm² (20 kgf/mm²) or more for each of the test samples. In addition, after heating at 850°C for 100 hours, the shear strength defined in JIS specifications is 137 N/mm² (14 kgf/mm²) or higher, e.g., 196 N/mm² (20 kgf/mm²) or higher. Thus, according to this invention bonding properties have been improved remarkably. As is apparent from the foregoing, this invention can provide a Ti-clad steel in which intermetallic compounds are not found in the bonding area, and which exhibits improved properties including a high level of bonding strength even after reheating at high temperatures. Thus, this invention is very advantageous from a practical viewpoint. Table 1 Run No. Ferrous Alloy Insert (% by weight) Heating Temperature (°C) Shear Strength N/mm² (kgf/mm²) Remarks C Nb V As-Rolled Reheated 1 0.02 3.1 - 800 196 (20) 176.4 (18) Reference 2 0.02 3.1 - 650 78.4 (8) 19.6 (2) Comparative 3 0.04 10 - 850 245 (25) 196 (20) Reference 4 0.03 20 - 830 265 (27) 245 (25) " 5 0.03 20 - 950 88.2 (9) 29.4 (3) Comparative 6 0.02 0.5 - 820 176.4 (18) 58.8 (6) " 7 0.03 - 0.3 830 186 (19) 39.2 (4) " 8 0.03 - 3.2 850 216 (22) 176.4 (18) Reference 9 0.01 - 5 800 245 (25) 186 (19) " 10 0.03 - 11 750 274.4 (28) 245 (25) " 11 0.01 - 19 700 245 (25) 235 (24) " 12 0.03 5 10 750 235 (24) 196 (20) " 13 0.02 0.2 0.1 800 186 (19) 58.8 (6) Comparative Run No. Ferrous Alloy Insert (% by weight) Intermediate Member Heating Temperature (°C) Shear Strength (kgf/mm²) N/mm² Remarks C Nb V As-Rolled Time Elapsed After Heating at 850°C (hr) 10 30 100 1 0.02 3.5 - Present 800 216 (22) 196 (20) 196 (20) 176 (18) Invention 2 0.02 3.5 - None* 800 216 (22) 196 (20) 137 (14) 98 (10) Comparative 3 0.02 3.5 - Present 650* 98 (10) 19.6 (2) 29.4 (3) 9.8 (1) " 4 0.04 10 - " 850 245 (25) 245 (25) 196 (20) 176 (18) Invention 5 0.04 10 - None* 850 245 (25) 225 (23) 176 (18) 127 (13) Comparative 6 0.03 20 - Present 830 265 (27) 265 (27) 245 (25) 196 (20) Invention 7 0.03 20 - None* 830 265 (27) 245 (25) 196 (20) 127 (13) Comparative 8 0.03 20 - Present 950* 127 (13) 98 (10) 78.4 (8) 49 (5) " 9 0.02 0.5* - " 820 196 (20) 176 (18) 118 (12) 49 (5) " 10 0.03 - 0.3* " 800 176.4 (18) 147 (15) 49 (5) 19.6 (2) " 11 0.03 - 4.5 " 750 274.4 (28) 245 (25) 196 (20) 157 (16) Invention 12 0.03 - 4.5 None* 750 274.4 (28) 196 (20) 137 (14) 68.6 (7) Comparative 13 0.03 - 4.5 Present 600* 78.4 (8) 49 (5) 19.6 (2) 19.6 (2) " 14 0.03 - 11 " 800 274.4 (28) 24.5 (25) 245 (25) 196 (20) Invention 15 0.03 - 11 None* 800 274.4 (28) 196 (20) 137 (14) 98 (10) Comparative 16 0.03 - 19 Present 700 294 (30) 274 (28) 245 (25) 245 (25) Invention 17 0.01 5 10 " 700 265 (27) 265 (27) 255 (26) 196 (20) " 18 0.02 5 10 None* 750 274.4 (28) 206 (21) 167 (17) 98 (10) Comparative 19 0.02 0.3 0.5 Present 820 196 (20) 176 (18) 127 (13) 78.4 (8) " None : * indicates outside the range of the invention. Alloy No. C Cr Ni Others 1 0.08 5.0 80.0 2 0.04 19.9 55.3 Mn=1.5 3 0.10 40.2 50.2 Si=2.5 4 0.02 20.3 25.7 Mo=1.0 5 * 0.02 39.8 30.4 6 * 0.10 4.8 10.5 7 * 0.08 50.3 0.24 8 * 0.05 35.2 20.2 Note : * indicates outside the range of the invention. Run No. Ferrous Alloy Insert (% by weight) Fe-Ni-Cr Alloy (Alloy No. of Table 3) Shear Strength (kgf/mm²) N/mm² Remarks C Nb V As-Rolled 100 hours After Heating at 850°C 1 0.09 3.5 - 1 (25) 245 (20) 196 Invention 2 0.03 5.2 - 6 * (28) 274 (11) 108 Comparative 3 0.10 10.3 - 2 (30) 294 (23) 225.4 Invention 4 0.09 12.5 - 8 * (31) 304 (10) 98 Comparative 5 0.05 20.0 - 3 (35) 343 (25) 245 Invention 6 0.03 19.5 - 7 * (33) 323.4 (12) 118 Comparative 7 0.10 - 4.5 4 (26) 255 (18) 176 Invention 8 0.02 - 4.6 5 * (26) 255 (7) 68.6 Comparative 9 0.03 - 11.2 1 (30) 294 (20) 196 Invention 10 0.08 - 13.0 6 * (31) 304 (10) 98 Comparative 11 0.03 - 19.0 2 (34) 333 (24) 235 Invention 12 0.09 - 19.5 8 * (35) 343 (11) 108 Comparative 13 0.02 2.0 1.5 3 (24) 235 (18) 176 Invention 14 0.01 2.0 2.0 7 * (25) 245 (6) 58.8 Comparative 15 0.07 10.0 2.0 4 (31) 304 (23) 225.4 Invention 16 0.03 11.0 2.5 5 * (32) 314 (12) 117.6 Comparative Note : * indicates outside the range of the invention.

Claims: A titanium-clad steel with improved bonding properties comprising a Ti-cladding, a base metal steel, an insert between them and an intermediate layer between said base metal steel and said insert, said insert being a ferrous alloy consisting of, in % by weight, 0.05 % or less of carbon, 3 to 20% of at least one of niobium (Nb) and vanadium (V), a balance of iron and normal impurities, and said intermediate layer being of nickel (Ni) or a nickel alloy. A titanium-clad steel with improved bonding properties comprising a Ti-cladding, a base metal steel, an insert between them and an intermediate layer between said base metal steel and said insert, said insert being a ferrous alloy consisting of, in % by weight, 0.1 % or less of carbon, 1 to 20% of at least one of niobium (Nb) and vanadium (V), a balance of iron and normal impurities, and said intermediate layer being an Fe-Ni-Cr austenitic alloy containing the amounts of Ni and Cr as defined by the following formulae, in % by weight: Cr ≦ 18%, Ni ≧ -0.78 Cr % + 26 Cr > 18%, Ni ≧ 1.13 (Cr % - 18) + 12, wherein Cr % + Ni % ≦ 100. A titanium-clad steel as defined in claim 1 or 2, in which the Ti-cladding is selected from pure titanium and titanium alloys. A titanium-clad steel as defined in any one of claims 1 to 3, in which the base metal is selected from carbon steels and low-alloy high-strength steels. A method of manufacturing a Ti-clad steel as defined in claim 1 or 2, the method comprising preparing a cladding assembly of the Ti-cladding, the base metal steel, the insert placed between them and the intermediate layer placed between said base metal steel and said insert, heating the cladding assembly or the bonding area at a temperature of 680 to 900°C, and effecting bonding under pressure. A method as defined in claim 5, in which the bonding is carried out by rolling.

Inventors: HINOTANI, SHIGEHARU
Applicants: SUMITOMO METAL INDUSTRIES, LTD.
Application year: 1987
Main classification: B32B15
IPC codes: B32B15, B23K35