SPARE PARTS FOR, AND A METHOD OF, REPAIRING TURBINE BLADES

Abstract: A spare part for, and a method of, repairing a high velocity fluid flow machine part, for example a turbine blade (10) comprises an insert (20) which may be made from a piece of material the same as the turbine blade (10) and prior to attachment to the blade has an edge region (21) hardened by any suitable means, for example induction hardening, or with a first part made from a durable material and a second part of a material compatible with the blade material, the insert (20) then being secured to the blade (10) by welding or brazing, the weld or braze material being of a relatively soft nature to provide a cushion between the insert and the blade so as to minimise the occurrence of stress corrosion cracking.

Description: The present invention relates to methods of repairing machines and is primarily but not exclusively concerned with high velocity fluid flow machinery such as turbines, and in particular turbine blades, nozzles, buckets and similar parts all hereinafter referred to for convenience as turbine blades. Turbine blades in particular are subjected to wear during use and particularly in the case of steam turbines, the outer end of the turbine blades in a rotor assembly is the part which has the greatest linear speed in use and it is the outer leading end that is most prone to erosion. Erosion generally occurs because of contact between the turbine blades and particles carried by the steam and also with the steam itself. The high pressure end of a steam turbine, for example, is subjected to relatively hot steam and damage to the turbine blades is generally caused due to contact with particles of solid matter carried by the steam. At the low pressure end of the turbine the steam is at a lower temperature and hence the water condenses more readily and considerable erosion occurs because of impact between the turbine blades and droplets of water. Because of the known phenomenon of erosion, particularly at the leading outer edge of a turbine blade, it is quite usual to make that part of the blade as an insert made from a suitable hardened steel or from another hard material such as Stellite. Such an insert may be secured to the blade by brazing or welding for example. Sometimes turbine blades are formed without such an insert and after some use when repair is necessary such an insert may be secured to the blades by cutting away the damaged part of the blade and securing, for example by brazing, a Stellite insert in position. Whereas such inserts are very satisfactory and can prolong the life of the blade considerably, problems do occur in the securing of such inserts to the blade itself, such problems have at least partially been overcome in respect of certain types of blade by methods of repair proposed by the applicants and described in British patent specification Nos. 2, 091,139; 2,114,921; 2,124,126 and 2,144,361. The document GB-A-2091139 discloses a method of repairing a turbine blade in which a damaged or eroded part has been removed from the leading edge of a turbine blade and an insert made from Stellite or a suitable hardened steel has been secured to the remainder of the turbine blade by a welding process, the blade end being subsequently machined to restore it to its original form. Problems occur during the securing of, for example, a Stellite shield to the blade because of the different nature of the materials to be joined together. A turbine blade is commonly made from a chrome steel, for example 12% chrome steel, and the securing by brazing or welding of the Stellite shield to such a blade involves the application of considerable thermal energy to the blade itself for which some compensation can be made by pre-heating the blade before the welding or brazing operation, controlled selective heating during the welding or brazing operation and post welding stress relief heating. If such repairs can be carried out under controlled conditions then the chances of subsequent failure occurring are reduced. However, such careful control may require the complete dismantling of the turbine so that the blade to be repaired can be separated therefrom so as to be repaired in a gas chamber for example. The cost of dismantling turbine blades is not only considerable from the labour cost involved but also the "down time" of the turbine is increased which can render such operations commercially unacceptable. The cost of repairing a turbine blade which has not been provided with a Stellite shield and which is merely repaired by brazing or welding a new piece of chrome steel to the blade is relatively modest and a rather more simple operation. Unfortunately, the long term wear characteristics of a Stellite shield are not provided and hence such a repaired blade will, in a relatively short space of time, require further repair. It is an object of the present invention to provide a method of repair that overcomes or reduces the abovementioned problems. According to one aspect of the present invention, we provide a method of repairing a damaged part of the leading edge of a turbine blade, said method being characterised in the steps of:- (a) removing the damaged part from the leading edge to leave a cut-out in the turbine blade; (b) preparing an insert from a material compatible with the material from which the turbine blade is made, the dimensions of said insert being substantially the same as the dimensions of said cut-out; (c) hardening that part of the insert which will present the leading edge part of the turbine blade when secured to the turbine blade, said hardening leaving an edge region of said insert, adapted to abut the blade, substantially unaffected by said hardening: (d) securing said insert to said turbine blade by welding or brazing and using weld or braze material of a relatively ductile nature so as to provide a cushion between said blade and said insert; and (e) subjecting said insert and at least that part of the blade in the region of said insert to a stress relieving heat treatment process. Preferably, the method of repair is accompanied by heating the turbine blade, which heating may occur during:- (a) a period prior to said welding or brazing operation: (b) the welding or brazing operation: (c) a period after said welding or brazing operation. Preferably, the heating of the machine part is carefully controlled so as to achieve desired temperatures in various parts of the turbine blade. Preferably, said heating is controlled in a manner that tends to counter any distortion of the blade which may occur during the welding or brazing operation. Preferably, said method further includes the method of manufacturing an insert as aforedescribed, testing said insert so that the properties thereof are known, both after manufacture and after securing to material the same as that from which a turbine blade is made, making any alteration to the conditions under which said insert is manufactured to enhance both the life of said insert and its ease of securement to the turbine blade or either one thereof and manufacturing said insert under said enhanced conditions for securement to turbine blades. The insert for securing to a turbine blade may have a first part of a material of high durability and a second part of a material the same as or compatible with the material of the turbine blade to which it is to be secured or is secured. Preferably, said insert may be made from material the same as that of the machine part and said first part may be produced by selectively hardening a part of the insert by any suitable treatment such as heat treatment, or coating said insert with durable material. Said insert may be formed from a hard material to which is affixed, secured or otherwise connected, soft material the same as or compatible with the machine part. Said insert may comprise a combination of material comprising a durable hard leading edge region through one or more different materials leading to a material that may readily be affixed to the turbine blade, said materials further enhancing the life of the machine part provided with such an insert. It is envisaged, for example, that where such an insert is provided in a turbine blade, then material between the hardened edge region and the turbine blade may be adapted to provide a barrier to prevent or minimise cracks due to, for example, the phenomenon of stress corrosion cracking which first may occur in the leading edge of the turbine blade. The weld or brazing material itself is of a relatively ductile nature and may provide further isolation between the "impact region" of the leading edge of the turbine blade, particularly at its outer end, and the remainder of the blade thus providing a cushion to minimise the propagation of cracks which may first appear in the leading edge of the turbine blade. It is further envisaged that an insert as aforedescribed may be attached to the blade by a mechanical connection such as a "dovetail" connection. In the case where the insert has the first part produced by hardening of a part of a material the same as or compatible with that of the material of the turbine blade, then means may be provided to ensure that a part of said insert is not affected by the hardening process. It is also envisaged that, for example, where said insert is treated by the application of heat, for example induction hardening, then a heat sink may be provided so as to minimise the effect of the application of considerable heat to harden the insert, at least over a part thereof that is to be joined to the turbine blade. Inserts as above described may be secured to a new turbine blade to help ensure that they have as long a service life as possible before repair is required. The insert provides significant advantages in the repair of machines in that not only can the insert be made under very carefully controlled conditions so that the properties thereof are well know, but relatively basic materials may be used which are subject to hardening processes while omitting, by masking for example, the hardening of the material in the area where it has to be attached to the machine part such as a turbine blade. It is envisaged that, particularly in the case of repair of a turbine blade, the insert may be made of a size such that the position of the weld or braze to the turbine blade is in an area which is unlikely to receive substantial damage in use of the turbine. Such selective positioning of the join area enables a relatively soft weld material to be used, such as Inconel, providing a ductile barrier required to prevent the propagation of cracks between the insert and the blade. Where it is not possible to provide the join in an area which would not be subject to impact and erosion, then it is envisaged that the weld material may be provided with a cap of very hard weld material such as an alloy containing 0.17 to .22% carbon, 0.2 to 0.3% nickel, 12 to 14% chromium, 0.1% molybdenum and 0.02% vanadium which, even though may be a very thin layer, provides an erosion barrier to the weld material itself whilst still leaving the ductile nature of the soft weld material intact. One method of hardening an insert may comprise chromising involving insertion of the part into a powdered compound and in which case some masking of the part will be necessary to ensure that the area of the insert to be joined to the machine part is still of a ductile nature. The material of the insert may comprise a cobalt-free alloy steel having approximately 19% nickel, 3% molybdenum and 1.4% titanium. The invention will now be described in more detail, by way of example only, with reference to the accompanying drawings, wherein:- FIGURE 1 is a diagrammatic view of a damaged turbine blade; FIGURE 2 is a view of the blade shown in Figure 1 with the damage part removed and an insert in spaced relation therewith; FIGURE 3 is a sectional view through one embodiment of insert; FIGURE 4 is a sectional view through a second embodiment of insert; FIGURE 5 is a sectional view through a third embodiment of insert; FIGURE 6 is an illustration of a turbine blade being repaired and accompanying heating apparatus; FIGURE 7 is a sectional view through a blade to which an insert has been secured; FIGURE 8 is a view of the repaired blade: FIGURE 9 is a sectional view through an insert indicating a progressive hardness value therethrough. Referring first to Figure 1 there is shown a turbine blade 10 which has an outer end 11 and a root end 12. As aforedescribed, most damage occurs to the leading edge 13 and in particular the outer end of the leading edge 13 in the area generally indicated at 14. Referring now in addition to Figure 2, the damaged area 14 may be removed by cutting a piece out of the turbine blade and securing thereto an insert 15 by welding or brazing operation. Referring now to Figure 3, one embodiment of insert is shown in section, the insert 20 being made from, for example, a piece of chrome steel similar to the material from which turbine blades are made and which has had the leading edge region 21 subjected to a hardening process, for example induction hardening. The induction hardening of the region 21, the extent of which is intended to be shown by the stippling in the illustration shown in Figure 3, does not extend completely throughout the insert 20 and the end region 22 is substantially free of any affect due to induction hardening. It is envisaged that for example the end 22 may be kept substantially free from the affect due to induction hardening by careful positioning of the induction hardening apparatus and providing a heat sink in the region of the end 22 such that the temperature of this part of the insert is not excessively raised. It is further envisaged that whereas the whole insert may be subjected to extreme temperature changes to effect hardening thereof, the region 22 could subsequently be treated in a manner to render it more ductile and so as to return, at least this part of the insert, to its original condition. It will be appreciated that it is not only the region 22 of the insert 15 that has to be relatively free of the effect of the hardening process but also the region 23, as can best be seen in Figure 2, since this additional region has to be secured to the turbine blade 10. Referring now to Figure 4, an alternative form of insert is shown and comprises a part 25 which initially has its leading edge generally indicated at 26 of a profiled somewhat slimmed or reduced from the normal profile of the blade and which is subsequently build up by deposition by any suitable manner of a very hard material 27. The deposition continues until the insert 25 has achieved the desired shape so that it may be joined to a turbine blade such as the turbine blade 10, the profile of the complete article being as intended. It is envisaged that the material 27 may be deposited in any manner which gives a durable effect, for example the material could be laid thereon in a fused state as in a welding operation, or could be secured thereto in a sintering or sputtering operation, the nature of the material 27 being such as to provide a very durable finish to the insert 25. Referring now to Figure 5, a still further embodiment of insert is shown, the insert generally indicated at 30 comprises a first part 31 of very hard material, a second part 32 of a material the same as or compatible with the material of the turbine blade to which it is to be affixed and an intermediate zone 33 of a material capable of being satisfactorily secured to the hard material 31 and the (turbine blade) material 32. It is envisaged that in some circumstances a piece of material 31 may be directly secured to the material 32, for example by a welding or brazing operation, or possibly through a mechanical bond such as a type of dove-tail conenction. However, in some circumstances the permanent bond between the first part 31 and second part 32 may be considerably enhanced by the provision of an intermediate material 33 having properties such as to provide a buffer zone between the hard material 31 and turbine blade material 32. Referring now to Figure 6, there is shown a turbine blade 10 and an insert 15 secured in position by welding, through if preferred the insert could be secured by mechanical means such as co-operating interengaging surfaces one on the insert and one on the turbine blade itself. Figures 6 also shows a plurality of heating means such as electrically energisable heating elements 40, 41, 42, 43, 44, and 45 all selectively connected to a control panel 46. A plurality of temperature sensing means such as thermocouples are shown at 50, 51, 52, 53, 54, 55 and 56 and are connected to a further conrol panel 58 which sends instructions through connection 60 to the heating control means 46. The turbine blade 10 can thus be heated during the securing operation of the insert to the turbine blade both prior to any welding or brazing of the insert to the blade during the welding or brazing operation and after the brazing or welding operation to provide stress relief in a very carefully controlled manner in accordance with known desiderata to minimise any detrimental effect to the turbine blade 10 by the application of considerable thermal energy during the welding or brazing operation. Figure 7 is a section through a turbine blade in which the insert 15 has been secured to the blade 10 by brazing, the braze material being shown at 70 with excess braze material left after the welding operation shown at 71 and 72. Referring now to Figure 8, the excess material 71 and 72 has been removed by grinding, for example, to leave a composite turbine blade having the insert 15 secured thereto, the insert providing a hardened edge region 21. Referring now to Figure 9, there is shown another insert suitable for connection to a turbine blade, nozzle or the like, the insert 90 having a leading edge 91 therein of a width of a few millimetres, for example two or three millimetres, of a first relatively high hardness, for example approximately 500 Hv, a second area 92 of greater width, for example 10mm or 15mm of a hardness value that may be slightly greater than the hardness value of area 91, for example 500/550Hv, a third area 93 of a width similar to or slightly greater than the width of area 92, for example 15mm to 20mm of a hardness value considerably reduced from areas 91 and 92, for example between 300/400Hv. A fourth area 94 may have a width greater than areas 92 and 93, for example 20mm to 30mm and once again of a reduced hardness value, for example in the region 200/225 Hv. If the insert is made of a material the same as that to which it is to be secured, for example if part of a turbine blade, then the material might be 12% chrome steel and the typical hardness value of the blade itself may be about 200 Hv and it is envisaged that the area 95 will have a hardness value a little greater than that of the turbine blade since inevitably there will be some "spill-over" of the hardening of the regions 91 to 94. It is envisaged that the width of area 95 will be greater than the collective width of areas 91 to 94 and thus the edge region 96, 97 the hardness value of the insert 90 should be substantially the same or very slightly greater than the hardness value of the blade material to which it is to be secured. Whereas the above description has had specific application to the leading edge portion thereof at its outer end, it will be appreciated that the insert may be secured to any part of a machine and in particular a high velocity fluid flow machine such as a turbine and the present invention has particularly reference to turbine parts such as turbine blade, rotor, stator or nozzle, where damage has occurred. Although particular embodiments of the invention have been described and illustrated herein, it will be evident that various modifications are possible without departing from the scope of the invention as the same will now be understood by those skilled in the art and as defined in the appended claims.

Claims: A method of repairing a damaged part of the leading edge of a turbine blade, said method being characterised in the steps of:- (a) removing the damaged part (14) from the leading edge to leave a cut-out in the turbine blade (10); (b) preparing an insert (15) from a material compatible with the material from which the turbine blade is made, the dimensions of said insert (15) being substantially the same as the dimensions of said cut-out; (c) hardening that part (21) of the insert (15) which will present the leading edge part of the turbine blade (10) when secured to the turbine blade, said hardening leaving an edge region of said insert, adapted to abut the blade, substantially unaffected by said hardening; (d) securing said insert (15) to said turbine blade (10) by welding or brazing and using weld or braze material (70) of a relatively ductile nature so as to provide a cushion between said blade and said insert; and (e) subjecting said insert (15) and at least that part of the blade (10) in the region of said insert to a stress relieving heat treatment process. A method of repair according to Claim 1 characterised in that said weld or braze material (70) is provided along any external surface thereof with a covering of a hard metallic material (71,72). A method of repair according to Claim 1 and Claim 2 characterised in that said method involves the application of controlled heating to the machine part (10), which heating occurs during:- (a) a period prior to any welding or brazing operation; (b) during the welding or brazing operation; (c) a period after said welding or brazing operation. A method of repairing a turbine blade according to any one of the preceding claims characterised in that the hardening of said insert (15) comprises the step of subjecting said insert to induction heating. A method of repairing a turbine blade according to any one of Claims 1 to 3 characterised in that the hardening of said insert (25) is effected by coating said insert (25) with durable material (27). A method of repairing a turbine blade according to any one of Claims 1 to 4 characterised in that said insert (15; 25) is subjected, prior to securing to said turbine blade to a chemical hardening treatment.

Inventors: FRASER, MICHAEL JAMES
Applicants: REFURBISHED TURBINE COMPONENTS LIMITED
Application year: 1987
Main classification: B23P6
IPC codes: B23P15, B23P6, F01D5