CURABLE LINEAR POLYPHENYLENE ETHER INTERPENETRATING POLYMER NETWORK COMPOSITIONS AND PROCESS

Abstract: Curable compositions comprising a polyphenylene ether resin free of substitutents which inhibit free radicals are combined with liquid polymerizable monomers, such as styrene, and the vinyl monomers cured with an optional catalyst to produce interpolymers more rapidly than in the prior art. Before curing, the compositions can be combined with flame retardants, reinforcing fillers and/or impact modifiers.

Description: This application is related to EP-A-87113543.0. The present invention relates to curable polymer compositions and to methods to make shaped articles using them. More particularly it relates to interpolymerizable compositions of a polyphenylene ether resin, free of groups which inhibit free radicals, at least one liquid vinyl unsaturated monomer in combination with at least one monovinyl unsaturated compound copolymerizable with and different from previous liquid vinyl unsaturated monomer and an optional catalyst as well as optional reinforcing agents, flame retardant agents and/or impact modifying agents. Articles are produced by shaping the novel compositions below normal decomposition temperatures and allowing the vinyl component of the composition to cure into a polymer network. In U.S.-A- 3,356,761, are disclosed compositions comprising hydroxy-terminated polyphenylene ethers, liquid vinyl monomers, such as styrene and vinyl pyridine, alone, or in further combination with free radical-generating catalysts, such as peroxides. It is taught that a primary advantage is to form products containing polyphenylene ethers at low temperatures, e.g., well below 300°C., to avoid thermal degradation of the polyphenylene ethers at such high temperatures, as might otherwise be required. Although this patent teaches the production of linear polyphenylene ether containing interpenetrating polymer networks by curing the liquid styrene monomer, it does not suggest that additives which are normally thermally degradable at 300°C. can be included in such composition. Moreover the compositions of this patent cure rather slowly and this is a major drawback. In U.S.-A- U.S 3,637,578, compositions are disclosed comprising hydroxy-terminated polyphenylene ethers, liquid vinyl monomers, and a reactive-type polyester resin in combination with a free radical catalyst. In general, interpolymers are produced by curing, but, again, recommended curing times are very slow, e.g., 20 minutes at 150°C., or the use of a highly reactive liquid vinyl monomer, such as diallyl phthalate is required to cure in 5 minutes at a higher temperature, 160°C., and these are major drawbacks. From U.S.-A- 3,375,228, it is known to modify polyphenylene ethers to improve their stability to oxidation, by reacting them with a so-called end-capping agent, which functionalizes the terminal hydroxyl groups of the polymers, rendering them less subject to interaction with oxygen. Suitable end-capping agents are, for example, acid halides, anhydrides and ketenes. There is no suggestion in this patent, however, that such end-capped polyphenylene ether resins can be used to make rapidly curing interpenetrating polymer networks with monomers, such as styrene. In U.S.-A- 4,287,321, there is disclosed the production of interpolymers by subjecting solutions of polyphenylene ethers in liquid styrene to polymerization. Among the techniques disclosed is the reaction of the terminal hydroxyl groups of the polyphenylene ethers with an unsaturated anhydride, such as maleic anhydride. This is done to provide a reactive site for grafting styrene monomer off the end of the modified polyphenylene ether. There is no suggestion in this patent that such a modification will give an increased rate of cure when making interpolymers. US-A-4148843 is directed toward a process for the preparation of a composition which comprises : (a) a capped polyphenylene oxide resin ; and (b) an alkenyl aromatic resin. The process comprises a first step of forming a mixture of a capped polyphenylene oxide in an alkenyl aromatic monomer and a second step of heating this mixture for at least 2 hours to form the final composition.The alkenyl aromatic polymer in the final composition is said to have a higher molecular weight as compared with a composition prepared under similar conditions with an uncapped polyphenylene oxide. In the present state of the art, therefore, it is known to use polyphenylene ether with a plasticizing monomer, such as styrene, to achieve low processing temperatures. However, slow curing is a major drawback and, if curing rates can be accelerated, then such compositions should become widely useful. For example, numerous additives could then be employed which cannot take normal polyphenylene ether processing temperatures. Among these can be mentioned the excellent, low cost flame retardant, aluminum trihydrate, and inexpensive forms of polyester fibers which can not now be used. In addition block copolymers of styrene-butadiene-styrene and acrylate core-styrene shell polymers which are very efficient impact modifiers can be used. It has now been discovered that a polyphenylene ether resin substantially free of groups which interfere with free radicals is necessary to provide rapid curing when interpolymerized with a liquid, plasticizing monomer. It is believed that the hydroxyl terminal groups and any ether groups normally present and easily convertible to hydroxyl groups, i.e., incipient hydroxyl groups, must be removed or converted to inert functional groups prior to forming the interpenetrating polymer networks. Although numerous methods suggest themselves to so modify the polyphenylene ethers prior to use, especially convenient methods, as will be described, involve reacting them with capping agents, for example, an anhydride or an acid halide, prior to use. The compositions thereafter produced by blending the modified polyphenylene ethers with the liquid plasticizing monomers have been found to be uniquely suitable, in light of their vastly increased cure rates, for shaping and curing into articles having a wide variety of end uses. According to the present invention there are provided curable compositions comprising (i) a thermoplastic polyphenylene ether resin substantially free of substituents which are inhibitors of free radicals; (ii)(a) at least one liquid, mono vinyl unsaturated compound having a general formula selected from or a mixture of said compounds, wherein R is hydrogen or methyl, Z is hydrogen, halogen, alkyl or alkoxy and p is 0 or a whole number of from 1 to 3, in combination with, (ii)(b) at least one monovinyl unsaturated compound copolymerizable with and different from component (ii)(a), said vinyl unsaturated compounds (ii)(a) and (ii)(b) comprising from 1 to 60 percent by weight of (i) and (ii)(a) and (ii)(b) combined; and, optionally, (iii) an effective amount of a catalyst capable of generating free radicals to initiate polymerization of the vinyl unsaturated compounds (ii)(a) and (ii)(b); and at least one of: (iv)(a) an effective amount of a reinforcing agent; (iv)(b) an effective amount of a flame retardant agent; (iv)(c) an effective amount of an impact modifier. Also contemplated by this invention are shaped articles of manufacture formed by melt processing a composition as defined above by (1) blending powder or pellets of component (i), with liquid component (ii)(a), liquid component (ii)(b); optionally, component (iii), and at least one of components (iv)(a); (iv)(b) or (iv)(c). (2) extruding the composition to a desired shape at a temperature below 150°C.; and (3) curing component (ii)(a) and component (ii)(b). Among the preferred features of the invention are curable compositions comprising (i) the reaction product of (A) a polyphenylene ether polymer; and (B) a compound having the general formula (I) ― Z ―(II) which is a compound that contains in its molecule both group (I) which is at least one group having the formula where X is F, Cl, Br, I, OH, OR, or where R is H or an alkyl or aryl radical and group (II) which is at least one carboxylic acid, acid anydride, acid amide, imido, carboxylic acid ester, amino or hydroxyl group; wherein groups (I) and (II) are covalently bonded through linkage Z which is a divalent hydrocarbon radical; (ii)(a) at least one liquid, mono vinyl unsaturated compound having a general formula selected from or a mixture of said compounds, wherein R is hydrogen or methyl, Z is hydrogen, halogen, alkyl or alkoxy and p is 0 or a whole number of from 1 to 3, in combination with, (ii)(b) at least one monovinyl unsaturated compound copolymerizable with and different from component (ii)(a), said vinyl unsaturated compounds (ii)(a) and (ii)(b) comprising from 1 to 60 percent by weight of (i) and (ii)(a) and (ii)(b) combined; and, optionally, (iii) an effective amount of a catalyst capable of generating free radicals to initiate polymerization of the vinyl unsaturated compounds (ii)(a) and (ii)(b). Also contemplated are shaped articles of manufacture formed by melt processing the immediately preceding composition by (1) blending powder or pellets of components (i), with liquid component (ii)(a), component (ii)(b) and, optionally, component (iii); (2) extruding the composition to a desired shape at a temperature below 150°C.; and (3) curing component (ii)(a) and optional component (ii)(b). Preferably the compounds (ii)(a) and (ii)(b) comprise from 15 to 40 percent by weight of (i) and (ii)(a) and (ii)(b) combined. Before modification, the polyphenylene ethers (also known as polyphenylene oxides) used in the present invention are a well known class of polymers which have become very useful commercially as a result of the discovery by Allan S. Hay of an efficient and economical method of production (See, for example, U.S.-A- 3,306,874 and 3,306,875). After modification, they are still characterized as a class by the presence of arylenoxy structural units. The polyphenylene ethers favored for modification and use in the practice of this invention generally contain structural units of the following formula in which each of these units independently each Q¹ is hydrogen, halogen, primary or secondary lower alkyl (i.e., alkyl containing up to 7 carbon atoms), phenyl, haloalkyl or aminoalkyl wherein at least two carbon atoms separate the halogen or nitrogen atom from the benzene ring, hydrocarbonoxy, or halohydrocarbonoxy wherein at least two carbon atoms separate the halogen and oxygen atoms; and each Q² is independently hydrogen, halogen, primary or secondary lower alkyl, phenyl, haloalkyl, hydrocarbonoxy or halohydrocarbonoxy as defined for Q¹. Examples of suitable primary lower alkyl groups are methyl, ethyl, n-propyl, n-butyl, isobutyl, n-amyl, isoamyl, 2-methylbutyl, n-hexyl, 2,3-dimethylbutyl, 2-, 3- or 4-methylpentyl and the corresponding heptyl groups. Examples of secondary lower alkyl groups are isopropyl, sec-butyl and 3-pentyl. Preferably, any alkyl radicals are straight chain rather than branched. Most often, each Q¹ is alkyl or phenyl, especially C 1-4 alkyl, and each Q² is hydrogen. Both homopolymers and copolymers are included. Suitable homopolymers are those containing, for example, 2,6-dimethyl-1,4-phenylene ether units. Suitable copolymers include random copolymers containing such units in combination with, for example, 2,3,6-trimethyl-1,4-phenylene ether units. Many suitable random copolymers, as well as homopolymers, are disclosed in the patent literature, including various Hay patents. The polyphenylene ether generally has a molecular weight (number average, as determined by gel permeation chromatography, whenever used herein) within the range of 5,000 to 40,000. The intrinsic viscosity of the polymer is usually in the range of 0.4 to 0.6 deciliters per gram (dl./g.), as measured in solution in chloroform at 25°C. The polyphenylene ethers may be prepared by known methods, and typically by the oxidative coupling of at least one corresponding monohydroxyaromatic (e.g., phenolic) compound. A particularly useful and readily available monohydroxyaromatic compound is 2,6-xylenol (in which for the above formula each Q₁ is methyl and each Q² is hydrogen), the corresponding polymer of which may be characterized as a poly(2,6-dimethyl-1,4-phenylene ether). Any of the various catalyst systems known in the art to be useful for the preparation of polyphenylene ethers can be used in preparing those employed in this invention. For the most part, they contain at least one heavy metal compound, such as a copper, manganese or cobalt compound, usually in combination with various other materials. Among the preferred catalyst systems are those containing copper. Such catalysts are disclosed, for example, in the aforementioned U.S-A- 3,306,874 and 3,306,875, and elsewhere. They are usually combinations of cuprous or cupric ions, halide ions (i.e., chloride, bromide or iodide), and at least one amine. Also preferred are catalyst systems containing manganese. They are generally alkaline systems containing divalent managanese and such anions as halide, alkoxide or phenoxide. Most often, the manganese is present as a complex with one or more complexing and/or chelating agents such as dialkylamines, alkanolamines, alkylenediamines, o-hydroxyaromatic aldehydes, o-hydroxyazo compounds, alpha-hydroxyoximes (both monomeric and polymeric), o-hydroxyaryl oximes, and beta-diketones. Also useful are cobalt-containing catalyst systems. Those skilled in the art will be familiar with patents disclosing manganese and cobalt-containing catalyst systems for polyphenylene ether preparation. Especially useful polyphenylene ethers for modification according to this invention are those which comprise molecules having at least one of the end groups of formulas II and III, below, in which Q¹ and Q² are as previously defined, each R¹ is independently hydrogen or alkyl, providing that the total number of carbon atoms in both R¹ radicals is 6 or less, and each R² is independently hydrogen or a C 1-6 primary alkyl radical. Preferably, each R¹ is hydrogen and each R² is alkyl, especially methyl or n-butyl. Polymers containing the aminoalkyl-substituted end groups of formula II may be obtained by incorporating an appropriate primary or secondary monoamine as one of the constitutents of the oxidative coupling reaction mixture, especially when a copper- or manganese-containing catalyst is used. Such amines, especially the dialkylamines and preferably di-n-butylamine and dimethylamine, frequently become chemically bound to the polyphenylene ether, most often by replacing one of the alpha-hydrogen atoms on one or more Q¹ radicals adjacent to the hydroxy group on the terminal unit of the polymer chain. During further processing and/or blending, the aminoalkyl-substituted end groups may undergo various reactions, probably involving a quinone methide-type intermediate of formula IV, below (R¹ is defined as above), with beneficial effects often including an increase in impact strength and compatibilization with other blend components. Polymers with biphenol end groups of formula III are typically obtained from reaction mixtures in which a by-product diphenoquinone of formula V, below, is present, especially in a copper-halide-secondary or tertiary amine system. In this regard, the disclosures of the U.S.-A-4,234,706, 4,477,649 and 4,482,697 are particularly pertinent. In mixtures of this type, the diphenoquinone is ultimately incorporated into the polymer in substantial amounts, chiefly as an end group. In many polyphenylene ethers obtained under the conditions described above, a substantial proportion of the polymer molecules, usually as much as about 90% by weight of the polymer, contain end groups having one or frequently both of formulas II and III. It should be understood, however, that other end groups may be present and that the invention in its broadest sense may not be dependent on the molecular structures of the polyphenylene ether end groups. To modify the foregoing polyphenylene ethers, they are preferably provided with terminal groups selected from the reaction products thereof with an organic acid, an organic acid halide, an organic acid anhydride, a ketene, or a compound having one or more of such functional groups or a mixture of any of foregoing. Many ways are known to those skilled in this art for forming such modified polyphenylene ethers. For example,US-A-3375228. describes heat treatment of the polymer to generate incipient, reactive hydroxyl groups on the polymer chain followed by reaction of generated hydroxyl groups with a material capable of reacting therewith to form the inert substituents. According to the patent, the polyphenylene ethers can be modified using either a one-step or a two-step capping procedure. In the one step process, a solution is prepared by dissolving both the polymer and a capping agent in a mutual solvent such as toluene, benzene, or any other liquid non-reactive with the polymer and capping agent. The solution is heated to an elevated temperature, preferably to temperatures in excess of (250°F) 121°C and most preferably, to temperatures varying between (400) 204 and (650°F) 343°C. Heating may be performed in an autoclave using pressures exceeding atmospheric. The temperature is held for a period of time sufficient to allow any incipient hydroxyl groups to be generated. This is, of course, dependent upon the temperature used and the reactivity of the materials. In general times varying between 30 seconds and 2 hours have been found suitable. Hydroxyl groups are generated at the elevated temperature and simultaneously react with capping agent to form substituents substantially inert to free radicals. Upon completion of the capping reaction, the solution is cooled and the polymer recovered by precipitation with a polymer non-solvent such as methanol. Alternatively, the one-step capping reaction can be carried out dry by blending polymer in powder form with a capping agent and extruding the blend at the elevated temperatures. The two-step capping procedure is similar to the one-step process and involves a first step of preheating the polymer, either in powder or solution form to generate hydroxyl groups in accordance with the procedure outlined above. The polymer may then be cooled and reacted with the capping agent, at ambient or elevated temperatures to stabilize the polymer. At lower temperatures, it is desirable to use a catalyst such as boron trifluoride etherate, sodium acetate or a tertiary amine. The specific capping agents used are not critical providing they are reactive with hydroxyl groups to form a substituent inert to free radicals. Typical examples of capping agents include acid halides, anhydrides, ketenes, etc. Typical examples of acid halides include, but are not limited to, acetyl chloride, acetyl bromide, benzoyl chloride, cinnamoyl chloride, succinoyl chloride, succinoyl fluoride, adipoyl chloride, stearoyl fluoride, lauroyl chloride, malonoyl chloride, terephthaloyl chloride, isophthaloyl chloride, etc. Typical examples of anhydrides, include for example, maleic anhydride, butyric anhydride, trichloroacetic anhydride, propionic anhydride, pivalic anhydride, phthalic anhydride, succinic anhydride, m-dichlorobenzoic anhydride, 2,3,4,5,6-pentachlorobenzoic anhydride, pentaoic anhydride, palmatoic anhydride, stearic anhydride, etc. Typical ketenes include, for example, diphenyl ketene, unsubstituted ketene, butyl ethylketene, dimethyl ketene, etc. Special mention is made of an especially preferred family of capping agents. These are of the formula: (I)―Z―(II), wherein I and (II) are as defined above. Illustratively, the group (I) portion of the capping agent has been generalized as an acyl-functional group depicted by the following formula: where X is F, Cl, Br, I, OH, OR or etc. and where R is H or an aliphatic or aromatic radical having up to about 10 carbon atoms. Group (I) is covalently bonded to a Group II, e.g., an anhydride group. Examples of suitable materials of general formula (I)―Z―(II) include but are not limited to the following: Chloroethanoylsuccinic anhydride trimellitic anhydride acid chloride (TAAC) chloroformylsuccinic anhydride 1-acetoxyacetyl-3,4-dibenzoic acid anhydride Special mention is made of the most preferred such compound, trimellitic anhydride acid chloride. Its use as a capping agent and the use of the polyphenylene ethers reacted therewith in the compositions of this invention are exemplified hereinafter. With respect to component (ii)(a), the liquid monovinyl unsaturated compound is meant to include a compound or a mixture of compounds liquid at room temperature or at elevated temperatures of up to 100°C. and selected from: or a mixture of the foregoing, where R is hydrogen or methyl; Z is hydrogen, halogen (e.g., chlorine, bromine, iodine and fluorine), alkyl (e.g., methyl, ethyl, propyl, isopropyl, butyl, octyl, etc.) or alkoxy (e.g., methoxy, ethoxy, propoxy, isopropoxy, butoxy, etc); and p is 0 or a whole number equal to from 1 to 3. The preferred vinyl unsaturated material is styrene. With respect to component (ii)(b), this will comprise at least one monovinyl unsaturated compound compolymerizable with and different from (ii)(a). Illustratively, the compounds can be unsaturated esters, e.g., dialkyl fumarates, e.g., diethyl fumarate and dioctyl fumarate, dialkyl itaconates, dialkyl maleates, N-substituted maleimides, e.g., N-phenyl maleimide, acrylates, such as butyl acrylate, vinyl ethers, vinyl esters, such as vinyl acetate, and the like. Preferably, the component (ii)(b) will be diethyl fumarate or N-phenyl maleimide. In those embodiments of the invention which are reinforced, any conventional reinforcing agent can be used, in conventional amounts, so long as it does not inhibit the interpolymerization reaction. Illustratively, these will comprise reinforcing glass fibers, carbon fibers, polyester fibers, titanium whiskers, generally in amounts of from 5 parts to 50 parts by weight, per 100 parts by weight of the total composition. Preferably in component (iv)(a) the reinforcing fibers comprise glass fibers, polyester fibers or a mixture thereof. In those embodiments of the invention which are flame retarded, component (iv)(b) can vary widely in type and amount. For example a halogenated aromatic compound or low polymer can be used, e.g., decabromodiphenyl ether, or brominated polycarbonate oligomer can be used, as well as phosphate esters, and the like, in amounts of from 1 to 40 parts by weight per 100 parts by weight of the total composition. Special mention is made non-halogen, non-phosphorus, polyphenylene ether-containing compositions of this invention rendered flame retardant with aluminum trihydrate, when contacted with flame, these give only water as an off gas, and the flame retardant does not contribute to smoke formation. In those embodiments of the invention which are impact modified, component (iv)(c) the (c)can vary widely in type and amount, although some are better than others. For example, rubber, synthetic or natural, can be included. However, it is preferred to use polymeric impact modifiers well known to those skilled in this art such as block copolymers and core shell polymers. Preferred block copolymers are styrene-ethylene-butylene-styrene compositions and preferred core shell polymers have a polymerized butyl acrylate core and a polystyrene shell. The method of forming the blend of the vinyl material and other components and the modified polyphenylene ether is not critical, any of the methods well known in the prior art being suitable. For example, the components may be mixed in a blender such as a Waring Blender, a Haake mixing bowl, or in conventional rubber milling equipment. Alternatively, the vinyl material and other components an polymer may be dissolved in a common solvent and recovered therefrom by solvent evaporation or by precipitation with a non-solvent. The quantity of vinyl material and other components combined with the polyphenylene ether may vary within broad limits, but should not be used in an amount that would cause complete dissolution of the polymer. Prefer ably, the mixture of vinyl material and polymer is in the form of free flowing powder or pellets. When an excessive amount of vinyl material is used, a paste or viscous liquid forms. In general, the quantity of vinyl material may vary between 1.0 and 60.0%, by weight, of the total composition, but it should be understood that this is dependent upon the specific materials used and the molecular weight of the polymer. From 15.0 to 40.0% by weight, of vinyl material in the total composition, constitutes a preferred embodiment of this invention. Following combination of the vinyl material with the polyphenylene ether, the composition may be formed into shaped articles by melt processing using conventional procedures. For example, film and fiber of substantial cross section can be formed by extrusion. The temperature of processing is dependent upon the quantity of vinyl material in the composition and the molecular weight of the polymer. For example, with a mixture consisting of styrene and a linear poly-(2,6-dimethyl-1,4-phenylene) ether having an intrinsic viscosity of about 0.50 dl./g., the extrusion temperature through the orifice is about 80°C. The same polymer free of styrene has an extrusion temperature in excess of 275°C. If the composition used to form the shaped article is in the form of free flowing powder or pellets, the so formed shaped article will maintain its structural integrity and can be handled and processed without damage. Curing or polymerization of the vinyl starting material may be initiated by almost any source of free radicals including organic peroxide materials and organic azo compounds, such as benzoyl peroxide, dicumyl peroxide, azobisisobutyronitrile, etc., any of which can be included in the initial formulation. A wide variety of organic peroxides may be used including organic diperoxides. Special mention is made of t-butyl peroxybenzoate. Other means of initiating and carrying out the polymerization include the use of ionizing radiation such as X-radiation, electron beam irradiation, promoted UV radiation, and similar application of ionizing energy. A further alternative is to use heat alone without added catalyst. This approach requires extended cure time, but has the advantage of not requiring catalysts and provides for very extensive shelf life of the pre-mix. Articles formed by the above procedures possess excellent physical properties as will be described in the following examples. As an aid in practicing the present invention the following procedure can be used to provide a polyphenylene ether substantially free of inhibitors of free radicals by capping with trimellitic anhydride acid chloride. PROCEDURE Various polyphenylene ether-trimellitic anhydride acid chloride reaction products were prepared. In one method, a 30% by weight solution of poly(2,6 dimethyl-1,4-phenylene) ether in toluene (obtained directly from the polymerization of 2,6-xylenol in toluene after removal of copper catalyst) was utilized ("PRE CON" PPE). In another method, an "isolated PPE" obtained by methanol precipitation and dissolved in 500 parts toluene was used. In either case, one hundred parts of PPE was reacted with between 1.7 and 2.3 parts of trimellitic anhydride acid chloride (TAAC), and between 4.1 to 5.8 parts of dimethyl-n-butylamine (DMBA) was utilized as an acid acceptor. The reactions were carried out at 95°C. for between 0.5 to 3.0 hours. The TAAC was obtained from Aldrich Chemical at a purity of 99%, molecular weight 210.57 g/mole, and melting point of 66 to 68°C. The reaction products were purified by precipitation in methanol and thereafter dried overnight in a vacuum oven at 60 to 80°C. The formation of PPE-TAAC was verified by infrared analysis which indicated a reduction of a known PPE hydroxyl peak at 2650 to 2900 nm and the appearance of a carbonyl absorption peak at 1730-1740 cm⁻¹. The following examples illustrate the present invention. COMPARATIVE EXAMPLES 1A-2A AND EXAMPLES 1-2 Compositions are prepared comprising PPE-TAAC, styrene, N-phenyl maleimide or diethyl fumarate and t-butyl peroxybenzoate and subjected to cure time testing by differential scanning colorimetry, and the time to achieve 100% cure is noted. For comparison purposes, compositions are also prepared, but using hydroxy-terminated PPE in accordance with the prior art. The compositions used and the results obtained are set forth in Table 1: The foregoing results demonstrate the vastly superior cure rates obtained following the use of capped polyphenylene ethers in comparison to the uncapped polyphenylene ethers when curing styrene and either N-phenyl maleimide or diethyl fumarate (1A* and 2A*). EXAMPLES 3-8 Linear polyphenylene ether interpenetrating network polymers were prepared by melt mixing poly(2,6-dimethyl-1,4-phenylene ether) TAAC (Procedure), styrene monomer and diethyl fumarate in a Haake bowl (set temperature, 75°C.) for 2 minutes at 90 revolutions per minute (rpm). The compositions were subsequently compression molded at 150°C., for 5 minutes, to polymerize the unsaturated components, and the heat distortion temperature of the shaped article measured by ASTM Standard Method D 648. The formulations used and the results obtained are set forth in Table 2: EXAMPLE 9 A glass-reinforced interpolymer according to this invention was prepared. In a Haake mixing bowl with set temperatures at 75°C. polyphenylene ether-TAAC, 54.5 parts was melted, mixed in the presence of 19 parts of styrene monomer, 8.1 parts diethyl fumarate and 0.41 wt-% of t-butyl peroxybenzoate. 18.2 parts of (1/4″) 6.35 mm Owens Corning chopped fibrous reinforcement was added (Fiberglass 405AA). After mixing for 2 minutes at 90 rpm, the mixture was removed and subsequently compression molded at 150°C. for 5 minutes. The resulting shaped article had a heat distortion temperature at 1.82 MPa (264 psi) of 153°C., a flexural strength of 121.76 MPa (17,660 psi), and a flexural modulus of 4550.5 MPa (660,000 psi). EXAMPLES 10-12 Impact modified interpolymers according to this invention were made in a Haake mixing bowl by melt mixing at 75°C. polyphenylene ether-TAAC, 60 parts, 21 parts of styrene, 9 parts of diethyl fumarate and 0.45 parts of t-butylperoxybenzoate as catalyst. The resulting material was formed into a shaped article by compression molding at 150°C. for 5 minutes to polymerize the styrene and the diethyl fumarate. The workpieces were subjected to impact strength testing according to the standard notched Izod Method of ASTM D 256. The composition used and the results obtained are set forth in Table 3: The foregoing results indicate that efficiently impact modified shaped articles can be obtained in accordance with this invention. EXAMPLES 13-21 Compositions according to this invention were made by the general procedure of Examples 1-6, substituting N-phenyl maleimide for the diethyl fumarate. The mixing bowl was carried out at 80°C. in the Haake mixing and the compression molding and curing were conducted at 150°C., for 5 minutes. The compositions used and the results obtained are set forth in Table 4: Shaped articles in accordance with the present invention were obtained. EXAMPLES 22-36 The general procedure of Examples 8-10 was repeated, substituting N-phenyl maleimide and using impact modifiers. Melt mixing was carried out at 80°C. for 3 minutes. Compression molding and curing were carried out at 150°C. for 3 minutes. A falling dart impact tester (Dynatup) using a 10.16 cm (4″) sample and 1.27 cm (1/2″) dart and speed at impact of 3.35 m/s (11 feet/sec.) was used to measure impact strength. The compositions used and the results obtained are set forth in Table 5: In addition to the foregoing tests, articles molded from Examples 25, 29, 33 and 36 were also tested for physical strength with the following results: EXAMPLES 37-44 Reinforced articles were prepared in accordance with this invention by following the general procedure of Examples 13-21, but also including glass fiber reinforcement and poly(ethylene terephthalate) fiber reinforcement. Mixing temperatures were 80°C. for 3 minutes. Molding was carried out at 150°C. for 3 minutes. The formulations used and the results obtained are set forth in Table 6: EXAMPLES 45-50 Reinforced and impact modified articles were prepared in accordance with this invention by following the general procedure of Examples 13-21, but also including glass fibers, and two block copolymers. The formulations used and the results obtained are set forth in Table 7: EXAMPLE 51 A flame retardant composition according to this invention was prepared by mixing 50 parts by weight of poly(2,6-dimethyl-1,4-phenylene ether)TAAC, 20 parts of styrene, 5 parts of diethylfumarate, 0.375 parts t-butylperoxybenzoate and 25 parts of aluminum trihydrate. The composition was compounded in a Haake bowl at 80°C. for 3 minutes, and molded and cured at 150°C. for 6 minutes to give a shaped article having a heat distortion temperature at 1.82 MPa (264 psi) of (310°F) 154°C. When tested for flammability in the Underwriters Laboratories Vertical Burn Test, UL-94, the shaped article self-extinguished in less than ten seconds and did not drip flaming resin (rating V-0). The above-mentioned patents and publications are incorporated herein by reference. Many variations will suggest themselves to those skilled in this art in light of the above, detailed decription. For example, instead of using polyphenylene ether capped with TAAC, polyphenylene ether capped with acetic anhydride, maleic anhydride and benzoyl chloride can be used. Instead of styrene monomer, alpha-methyl styrene, vinyl toluene, and 4-vinyl pyridine can be used. Instead of t-butyl peroxybenzoate, azobisisobutyronitrile can be used. As a flame retardant, aluminum trihydrate and decabromodiphenyl ether can be used. Instead of glass fibers and polyester fibers, fibers comprising polypropylene, cellulosics (rayon, cotton, jute, etc.), nylon, acrylics, wool, and the like can be used. Other additives, such as chlorinated polymers, antioxidants, thermal and ultraviolet stabilizers, lubricants, organic dyes and pigments, anti-static agents and the like can be employed. In general, any additives conventional for use in commodity plastics, e.g., polyethylene, polypropylene, polystyrene and vinyls can now be used in an engineering system.

Claims: A curable composition comprising: (i) a thermoplastic polyphenylene ether resin substantially free of substituents which are inhibitors of free radicals; (ii)(a) at least one liquid, monovinyl unsaturated compound having a general formula selected from or a mixture of said compounds, wherein R is hydrogen or methyl, Z is hydrogen, halogen, alkyl or alkoxy and p is 0 or a whole number of from 1 to 3, in combination with, (ii)(b) at least one monovinyl unsaturated compound copolymerizable with and different from component (ii)(a), said vinyl unsaturated compound (ii)(a) and (ii)(b) comprising from 1 to 60 percent by weight of (i) and (ii)(a) and (ii)(b) combined; and, optionally, (iii) an effective amount of a catalyst capable of generating free radicals to initiate polymerization of the vinyl unsaturated compounds (ii)(a) and (ii)(b); and at least one of: (iv)(a) an effective amount of a reinforcing agent; (iv)(b) an effective amount of a flame retardant agent; or (iv)(c) an effective amount of an impact modifier. A composition as defined in Claim 1 wherein the compounds (ii)(a) and (ii)(b) comprise from 15 to 40 percent by weight of (i) and (ii)(a) and (ii)(b) combined. A composition as defined in Claim 1 wherein said polyphenylene ether is a homopolymer or copolymer containing structural units of the formula: in which for each of these units independently each Q¹ is hydrogen, halogen, primary or secondary lower alkyl having up to seven carbon atoms, phenyl, haloalkyl or aminoalkyl wherein at least two carbon atoms separate the halogen or nitrogen atom from the benzene ring, hydrocarbonoxy, or halohydrocarbonoxy wherein at least two carbon atoms separate the halogen and oxygen atoms; and each Q² is independently hydrogen, halogen, primary or secondary lower alkyl, phenyl, haloalkyl, hydrocarbonoxy or halohydrocarbonoxy as defined for Q¹, said polyphenylene ether having terminal groups selected from reaction products of said polyphenylene ether with an organic acid, an organic acid halide, an organic acid anhydride, a ketene, or a compound having more than one of the functional groups or a mixture of any of the foregoing. A composition as defined in Claim 3 wherein said polyphenylene ether is a poly(2,6-dimethyl-1,4-phenylene ether) or a poly(2,6-dimethyl-co-2,3,6-trimethyl-1,4-phenylene ether) end capped with an acid halide, and acid anhydride or compound having both acid halide and acid anhydride functional groups. A composition as defined in Claim 4 wherein said polyphenylene ether is end capped with trimellitic anhydride acid chloride. A composition as defined in Claim 1 wherein component (ii)(a) comprises a vinyl aromatic hydrocarbon and component (ii)(b) comprises a dialkyl fumarate or an N-substituted maleimide. A composition as defined in Claim 6 wherein component (ii)(a) comprises styrene and component (ii)(b) comprises diethyl fumarate or N-phenyl maleimide. A composition as defined in Claim 1 wherein component (iii) comprises an organic peroxide or an organic azo compound. A composition as defined in Claim 8 wherein said organic peroxide comprises t-butylperoxybenzoate. A composition as defined in Claim 1 wherein component (iv)(a) comprises a reinforcing amount of glass fibers, polyester fibers or a mixture thereof. A composition as defined in Claim 1 wherein component (iv)(b) comprises a flame retardant amount of aluminum trihydrate. A composition as defined in Claim 1 wherein component (iv)(c) comprises an impact improving amount of a styrene-ethylene-butylene-styrene block copolymer or a polymer having a polymerized butyl acrylate core and a styrene shell. A shaped article of manufacture formed by melt processing a composition as defined in Claim 1 by (1) blending powder or pellets of component (i), with liquid component (ii)(a), liquid component (ii)(b); optionally, component (iii), and at least one of components (iv)(a); (iv)(b) or (iv)(c); (2) extruding the composition to a desired shape at a temperature below 150°C.; and (3) curing component (ii)(a) and component (ii)(b). A curable composition comprising (i) the reaction product of (A) a polyphenylene ether polymer; and (B) a compound having the general formula (I)―Z―(II) which is a compound that contains in its molecule both group (I) which is at least one group having the formula where X is F, Cl, Br, I, OH, OR, or where R is H or an alkyl or aryl radical and group (II) which is at least one carboxylic acid, acid anhydride, acid amide, imido, carboxylic acid ester, amino or hydroxyl group; wherein groups (I) and (II) are covalently bonded through linkage Z which is a divalent hydrocarbon, radical; (ii)(a) at least one liquid, mono vinyl unsaturated compound having a general formula selected from or a mixture of said compounds, wherein R is hydrogen or methyl, Z is hydrogen, halogen, alkyl or alkoxy and p is 0 or a whole number of from 1 to 3, in combination with, (ii)(b) at least one monovinyl unsaturated compound copolymerizable with and different from component (ii)(a), said vinyl unsaturated compound (ii)(a) and (ii)(b) comprising from 1 to 60 percent by weight of (i) and (ii)(a) and (ii)(b) combined; and, optionally, (iii) an effective amount of a catalyst capable of generating free radicals to initiate polymerization of the vinyl unsaturated compounds (ii)(a) and (ii)(b). A composition as defined in Claim 14 wherein the compounds (ii)(a) and (ii)(b) comprise from 15 to 40 percent by weight of (i) and (ii)(a) and (ii)(b) combined. A composition as defined in Claim 14 wherein said polyphenylene ether is a homopolymer or copolymer containing structural units of the formula: in which for each of these units independently each Q¹ is hydrogen, halogen, primary or secondary lower alkyl having up to seven carbon atoms, phenyl, haloalkyl or aminoalkyl wherein at least two carbon atoms separate the halogen or nitrogen atom from the benzene ring, hydrocarbonoxy, or halohydrocarbonoxy wherein at least two carbon atoms separate the halogen and oxygen atoms; and each Q² is independently hydrogen, halogen, primary or secondary lower alkyl, phenyl, haloalkyl, hydrocarbonoxy or halohydrocarbonoxy as defined for Q¹, said polyphenylene ether having terminal groups selected from reaction products of said polyphenylene ether with an organic acid, an organic acid halide, an organic acid anhydride, a ketene, or a compound having more than one of the functional groups or a mixture of any of the foregoing. A composition as defined in Claim 16 wherein said polyphenylene ether is a poly(2,6-dimethyl-1,4-phenylene ether) or a poly(2,6-dimethyl-co-2,3,6-trimethyl-1,4-phenylene ether). A composition as defined in Claim 16 wherein said polyphenylene ether is end capped with trimellitic anhydride acid chloride. A composition as defined in Claim 14 wherein component (ii)(a) comprises a vinyl aromatic hydrocarbon and component (ii)(b) comprises a dialkyl fumarate or an N-substituted maleimide. A composition as defined in Claim 14 wherein component (ii)(a) comprises styrene and component (ii)(b) comprises diethyl fumarate or N-phenyl maleimide. A composition as defined in Claim 14 wherein component (iii) comprises an organic peroxide or an organic azo compound. A composition as defined in Claim 21 wherein said organic peroxide comprises t-butyl peroxybenzoate. A curable composition as defined in Claim 14 which also includes (iv)(a) an effective amount of a reinforcing agent; (iv)(b) an effective amount of a flame retardant agent; (iv)(c) an effective amount of an impact modifier; or a combination of any of the foregoing. A composition as defined in Claim 23 wherein component (iv)(a) comprises a reinforcing amount of glass fibers, polyester fibers or a mixture thereof. A composition as defined in Claim 23 wherein component (iv)(b) comprises a flame retardant amount of aluminum trihydrate. A composition as defined in Claim 23 wherein component (iv)(c) comprises an impact improving amount of a styrene-ethylene-butylene-styrene block copolymer or a polymer having a polymerized butyl acrylate core and a styrene shell. A shaped article of manufacture formed by melt processing a composition as defined in Claim 14 by (1) blending powder or pellets of components (i), with liquid component (ii)(a), liquid component (ii)(b) and, optionally, component (iii); (2) extruding the composition to a desired shape at a temperature below 150°C.; and (3) curing component (ii)(a) and component (ii)(b). A shaped article of manufacture formed by melt processing a composition as defined in Claim 23 by (1) blending powder or pellets of component (i), with liquid component (ii)(a), liquid component (ii)(b); optionally, component (iii), and at least one of components (iv)(a); (iv)(b) or (iv)(c); or a mixture of any of said components (iv)(a), (iv)(b) or (iv)(c); (2) extruding the composition to a desired shape at a temperature below 150°C.; and (3) curing component (ii)(a) and component (ii)(b).

Inventors: BOOKBINDER, DANA CRAIG, FOX, DANIEL WAYNE, PETERS, EDWARD NORMAN, SMITH, GARY FRANCIS
Applicants: GENERAL ELECTRIC COMPANY
Application year: 1987
Main classification: C08F283
IPC codes: C08L71, C08G65, C08F283, C08K5