SILICATE PHOSPHOR

Abstract: A silicate phosphor comprising manganese as an activator, a trivalent element and a pentavalent element, wherein said trivalent element is at least one element selected from the group consisting of boron and indium, said pentavalent element is at least one element selected from the group consisting of arsenic, antimony and bismuth, the content of the trivalent element is from l × l0⁻⁴ to 2 × l0⁻² gram-atom/mol, the content of the pentavalent element is not more than 3 × l0⁻³ gram-atom/mol, and the molar ratio of the trivalent element to the pentavalent element (trivalent element/pentavalent element) is at least l.5.

Description: The present invention relates to a silicate phosphor containing manganese as an activator. More particularly, the present invention relates to a silicate phosphor wherein specific trivalent and pentavalent elements are incorporated in a specific ratio to reduce the initial degradation in luminance and after glow. In recent years, it has been desired to use a cathode ray tube having high resolution for a terminal display unit of a computer system for displaying fine characters and figures, or for a display unit of an aircraft control system. In many cases, a phosphor having a long after-glow characteristic is used for a fluorescent screen of such a high resolution cathode ray tube. In general, it is necessary for the phosphor constituting such a fluorescent screen to exhibit an after-glow period of from a few tens to several tens times longer than the after-glow period of the short after-glow phosphor which constitutes the fluorescent screen of an ordinary cathode ray tube. The term "after-glow period" used in this specification means the period of time required for the emission luminance to decrease to l0% of the emission luminance under excitation after the excitation of the phosphor is stopped, i.e. a "l/l0 after-glow period". As green emitting zink silicate phosphors with long after-glow, there have been known a manganese and arsenic-activated zinc silicate phosphor (P39 phosphor) and a manganese-activated zinc silicate phosphor (Pl phosphor). Particularly, P39 phosphor is used practically in a large amount. However, as the phosphor is used for various applications, many drawbacks have been found, for instance, in the degradation of the luminance or after-glow, or in the coating properties. It has been strongly desired to overcome such drawbacks. Various compositions have been proposed, for instance, in U.S. Patent 4,23l,892, Japanese Unexamined Patent Publication No. l5l322/l983 and U.S. Patent 4,55l,397. However, it is common that a display tube prepared by using a silicate phosphor containing manganese as an activator, is subjected to an initial adjustment such as a linearity adjustment, after the production, whereby the same pattern is displayed on the tube for a period of a few hours to a few tens hours. A fluorescent screen wherein a conventional silicate phosphor is used, has a drawback such that the portion subjected to electron beam irradiation for the above display has a shorter after-glow (initial after-glow degradation) and a lower luminance (initial luminance degradation) than the portion not subjected to electron beam irradiation. This makes the initial adjustment of the display tube cumbersome, and a number of cathode ray tubes have to be subjected to aging for long hours, and yet the subsequent degradation is hardly predictable. Thus, there have been various problems such that circuit setting for such products is difficult, the pattern used for the initial adjustment remains on the image due to the luminance degradation, and flickering is likely to result due to a partial after-glow degradation. It is an object of the present invention to provide a silicate phosphor containing manganese as an activator, wherein the initial after-glow degradation and initial luminance degradation under excitation by electron beams are substantially reduced. The present inventors have conducted various studies on silicate phosphors to accomplish the above object, and as a result, have found that the above-mentioned degradation can be substantially reduced when certain specific trivalent and pentavalent elements are incorporated in a certain specific molar ratio to a silicate phosphor containing manganese as an activator. The present invention has been accomplished on the basis of this discovery. U.S. Patent 4,23l,892 discloses P39 phosphor containing the trivalent and pentavalent elements in equimolar amounts. The present inventors have found that the above-mentioned problems can be solved with a ratio substantially different from the disclosed ratio. The silicate phosphor of the present invention comprises manganese as an activator, a trivalent element and a pentavalent element, and is characterized in that said trivalent element is at least one element selected from the group consisting of boron and indium, said pentavalent element is at least one element selected from the group consisting of arsenic, antimony and bismuth, the content of the trivalent element is from l × l0⁻⁴ to 2 × l0⁻² gram-atom/mol, the content of the pentavalent element is not more than 3 × l0⁻³ gram-atom/mol, and the molar ratio of the trivalent element to the pentavalent element (trivalent element/pentavalent element) is at least l.5. The most typical silicate phosphor containing manganese as an activator, is a manganese-activated zinc silicate phosphor. However, the silicate phosphor further includes bivalent metal cation silicate phosphors such as a manganese-activated magnesium silicate phosphor and a manganese and lead-activated calcium silicate phosphor. In the accompanying drawings: Figure l is a graph showing the luminance degradation characteristics of the zinc silicate phosphor of the present invention as compared with those of the conventional phosphor. Figure 2 is a graph showing the relation between the initial after-glow degradation characteristics of the zinc silicate phosphor, and the boron content and the molar ratio of the trivalent element to the pentavalent element, when the arsenic content is constant. Figure 3 is a graph showing the relation between the initial after-glow degradation characteristics, and the indium content when the arsenic content or the arsenic and boron contents are constant. Figure 4A is a graph showing the relation between the arsenic content and the molar ratio of the trivalent element to the pentavalent element, and the l/l0 after-glow period and the after-glow degradation characteristics, when the boron and antimony contents are constant. Figure 4B is a graph showing the relation between the arsenic content and the molar ratio of the trivalent element to the pentavalent element, and the l/l0 after-glow period and the after-glow degradation characteristics, when the boron content is constant. Figure 5 is a graph showing the relation between the arsenic content, and the l/l0 after-glow period and the after-glow degradation characteristics, when the indium and antimony contents are constant, and when the indium, boron and antimony contents are constant. Figure 6 is a graph showing the relation between the relative luminance and the boron content, when the trivalent element is boron alone. Figure 7 is a graph showing the relation between the indium content and the relative luminance, when the trivalent element is indium alone. Now, the present invention will be described in detail with reference to a process for producing the most typical manganese-activated zinc silicate phosphor. Firstly, as the phosphor raw material, there may be employed l) zinc oxide (ZnO) or a zinc compound such as a carbonate or oxalate, which is capable of being readily converted to ZnO at a high temperature, ii) silicon dioxide (SiO₂) or a silicon compound such as ethyl silicate or silicic acid, which is capable of being readily converted to SiO₂ at a high temperature, iii) manganese oxide (MnO₂) or a manganese compound such as metal manganese, a carbonate, a halide, a nitrate or a sulfate, which is capable of being converted to manganese oxide at a high temperature, iv) indium and boron oxides, or indium and boron compounds which are capable of being readily converted to indium and boron oxides at a high temperature, v) arsenic, antimony and bismuth oxides, or arsenic, antimony and bismuth or their compounds such as halides, which are capable of being readily converted to arsenic, antimony and bismuth oxides. The above phosphor raw materials are weighed, and then thoroughly mixed to obtain a phosphor material mixture. The mixing operation can be conducted in a dry system by using a ball mill, a mixer mill or a mortar, or may be conducted in a wet system i.e. in a paste state by using water, an alcohol or a weak acid as the medium. Further, a flux may be incorporated to the phosphor raw material mixture for the purpose of improving the emission luminance and the powdery nature of the resulting phosphor. Further, among the above raw materials, materials iv) and v) tend to evaporate when fired at a high temperature, and they may be incorporated more or less in an excess amount depending on the temperature and time for the firing. Then, the above-mentioned mixture of phosphor raw material is filled in a heat resistant container such as an aluminum crucible or a quartz crucible, and subjected to firing. The firing is usually conducted from one to a few times (i.e. 3 - 4 times) in the air (i.e. in an oxidative atmosphere), in a neutral atmosphere such as a nitrogen gas atmosphere or an argon gas atmosphere, or in a reducing atmosphere such as a nitrogen gas atmosphere containing a small amount of hydrogen gas or a carbon atmosphere, at a temperature of from l000 to l350°C, preferably from l200 to l300°C. Better results are obtainable by subjecting the above phosphor matrix material to preliminary firing at a temperature of from 500 to l300°C so that the matrix material undergoes grain growth. The firing time may be varied depending upon the amount of the mixture of the phosphor raw materials filled in the heat resistant container and the firing temperature employed. However, it is usually from 0.5 to 6 hours, preferably from l to 4 hours, when the firing temperature is within the above-mentioned range. After the firing, the fired product is treated by various operations which are commonly employed for the production of phosphors, such as pulverization, washing (which may be conducted by means of water, a weak mineral acid, a weak alkaline solution or a weak organic acid), drying and sieving, whereby a phosphor of the present invention will be obtained. The phosphor of the present invention thus obtained and the conventional zinc silicate phosphor (P39) are respectively uniformly coated on glass plates by a precipitation coating method to obtain fluorescent screens, and then display tubes were prepared in accordance with a conventional method for the preparation of a display tube. With use of these display tubes, fluorescent degradation characteristics under continuous excitation of the fluorescent screens were measured. The results are shown in Figure l. From the Figure, it is evident that the zinc silicate phosphor of the present invention is substantially superior to the conventional product in the fluorescence degradation characteristics. The following Table l shows the results of the measurement of the after-glow degradation characteristics, from which it is evident that the zinc silicate phosphor of the present invention is superior to the conventional product in the after-glow degradation characteristics. Further, the after-glow tends to be slightly longer. Figure 2 shows the relation between the initial after-glow degradation characteristics and the boron (trivalent) content with respect to a Zn₂SiO₄:Mn,B,As phosphor. It is evident from Figure 2 that from the viewpoint of the initial after-glow degradation characteristics, a substantial degradation is observed when the B/As molar ratio is l, whereas no substantial degradation is observed when the molar ratio is about l.5 or higher. Figure 3 shows the relation between the initial after-glow degradation characteristics and the indium (trivalent) content. In this Figure, curve l represents a Zn₂SiO₄:Mn,In,As phosphor (As = l × l0⁻⁴ gram-atom/mol), and cruve 2 represents a Zn₂SiO₄:Mn,B,In,As phosphor (B = 2 × l0⁻³ gram-atom/mol, As = l × l0⁻⁴ gram-atom/mol). The same comment as in Figure 2 applies to Figure 3. Figure 4A shows the relation between the arsenic (pentavalent) content and the molar ratio of the trivalent element to the pentavalent element, and the l/l0 after-glow period and the after-glow degradation characteristics (the ratio of the l/l0 after-glow period after irradiation to the l/l0 after-glow period before irradiation), when the boron (trivalent) and antimony (pentavalent) contents are constant (B = 2.2 × l0⁻³ gram-atom/mol, Sb = l.3 × l0⁻³ gram-atom/mol) in the Zn₂SiO₄:Mn,B,As,Sb phosphor. Figure 4B shows the relation between the antimony and arsenic contents and the molar ratio of the trivalent element to the pentavalent element, and the l/l0 after-glow period and the after-glow degradation characteristics, when the boron content is constant in the same phosphor as in Figure 4A. In the Figure, curves a and b show the relation between the arsenic content and the l/l0 after-glow period, and curves l and 2 show the relation between the arsenic content and the after-glow degradation characteristics. Further, curves l and a represent the case where the antimony content is 2 × l0⁻³ gram-atom/mol, and curves 2 and b represent the case where the antimony content is 0. Figure 5 like Figure 4B, shows the relation between the arsenic content, and the l/l0 after-glow period and the after-glow degradation characteristics when the indium and antimony contents are constant, and when the indium, boron and antimony contents are constant. From the foregoing Figures, it is evident that when the molar ratio of the trivalent element to the pentavalent element is higher than the conventional molar ratio, the after-glow degradation characteristics can be substantially improved. Figure 6 is a graph showing the relation between the boron content and the relative luminance with respect to the silicate phosphor of the present invention containing boron alone as the trivalent element. Figure 7 shows the relation between the indium content and the relative luminance when the trivalent element is indium only. As is evident from Figure 7, when indium is incorporated in a large amount, the relative luminance substantially decreases, such being undesirable. Thus, the indium content is preferably within a range of from l × l0⁻⁴ to l × l0⁻² gram-atom/mol, more preferably from 2 × l0⁻⁴ to 5 × l0⁻³ gram-atom/mol. From the foregoing graphs, it is evident that the content of the trivalent element is preferably from l × l0⁻⁴ to 2 × l0⁻² gram-atom/mol. Especially when the trivalent element is boron only, its content is preferably from 2 × l0⁻⁴ to 2 × l0⁻² gram-atom/mol, the content of the pentavalent element is preferably not higher than 3 × l0⁻³ gram-atom/mol, and the molar ratio of the boron to the pentavalent element (trivalent element/pentavalent element) is preferably at least l.5, more preferably at least l.8. When the trivalent element is indium only, its content is preferably from l × l0⁻⁴ to l × l0⁻² gram-atom/mol, the content of the pentavalent element is preferably not higher than 3 × l0⁻³ gram-atom/mol, and the molar ratio of the trivalent element to the pentavalent element (trivalent element/pentavalent element) is preferably at least l.5, more preferably at least l.8. The upper limit of the molar ratio is usually 500 in the case where the pentavalent element is arsenic only, or 50 in the case where the pentavalent element is at least one of antimony and bismuth. The lower limit of the content of the pentavalent element is usually 7 × l0⁻⁵ gram-atom/mol. From the viewpoints of the effects of the present invention, boron is preferred to indium as the trivalent element, and arsenic is preferred as the pentavalent element. The content of the arsenic is preferably from 5 × l0⁻⁵ to l × l0⁻³ gram-atom/mol, more preferably from 7 × l0⁻⁵ to 8 × l0⁻⁴ gram-atom/mol. Likewise, the content of boron is preferably within a range of from 3 × l0⁻³ to l.2 × l0⁻² gram-atom/mol. When arsenic only or a substantial amount of arsenic is incorporated as the pentavalent element, the molar ratio of the trivalent element to the pentavalent element is preferably at least 5. Further, the amount of manganese used as an activator in the present invention is usually within a range of from l × l0⁻³ to 3 × l0⁻² gram-atom/mol, preferably from 2 × l0⁻³ to l × l0⁻² gram-atom/mol, from the practical viewpoint. The effects of the present invention are obtainable only with the above-mentioned specific elements, and no such effects have been observed when other trivalent and pentavalent elements are used. As described in the foregoing, according to the present invention, the specific trivalent and pentavalent elements are incorporated in the specific proportions to a silicate phosphor containing manganese as an activator, whereby the initial degradation of luminance and after-glow can substantially be reduced. Now, the present invention will be described in detail with reference to Examples. However, it should be understood that the present invention is by no means restricted to such specific Examples. Firstly, the test method used in the Examples will be described. Measuring method by means of demountable apparatus: (a) Preparation of a test piece A phosphor to be tested is coated on a test piece of 2.5 × 3 cm by a precipitation method to form a fluorescent layer. (b) Electron beam irradiation The above test piece is mounted on a demountable electron beam stimulating apparatus (manufactured by Kasei Optonix, Ltd.), and electron beams are irradiated at an accelerating voltage of 20 kV at a current density of l µA/cm² with a luster size of l × l cm for 20 minutes. (c) Luminance measurement During the above electron beam irradiation, luminance is measured every one minute by means of a luminance meter. (d) After-glow measurement The l/l0 after-glow period is measured before and after the electron beam irradiation under the following conditions. Excitation is conducted by non-deflection defocus beams with a duty of 50% at an accelerating voltage of l5 kV with a pulse width of l02.4 ms. The current density is 0.5 µA/cm². EXAMPLE l Zinc oxide ZnO 370 g Silicon dioxide SiO₂ l50 g Manganese carbonate MnCO₃.0.5H₂O 2.5 g Antimony trioxide Sb₂O₃ l.0 g To the above raw materials, 25 ml of an aqueous solution containing 0.5 mol/liter of B₂O₃, 5 ml of an aqueous solution containing 0.05 mol/liter of As₂O₅ and l.5 liter of purified water were added. The mixture was mixed in a wet system in a ball mill, and then dried and pulverized. The material thus obtained was filled in an alumina crucible, and fired in the air at l300° for 4 hours. The fired product was pulverized, washed and dried to obtain a phosphor of the present invention having a composition of Zn₂SiO₄:Mn 0.008 As 0.0001 B 0.005 ,Sb 0.002 . This phosphor contained 0.005 gram-atom/mol of Zn₂SiO₄, of boron as the trivalent element and 0.002l gram-atom/mol of Zn₂SiO₄, of arsenic and antimony as the pentavalent element, and the molar ratio of the trivalent element to the pentavalent element was 2.38. A fluorescent layer was formed with this phosphor and subjected to the above described accelerated aging test, whereupon the fluorescence-maintaining rate was measured. The fluorescence-maintaining rate was 99%. Whereas, the fluorescence-maintaining rate of a Zn₂SiO₄:Mn 0.008 ,As 0.0001 phosphor prepared in the same manner, was 94%. Further, no after-glow degradation was observed with the fluorescent layer of the phosphor of the present invention. EXAMPLE 2 Zinc oxide ZnO 390 g Silicon dioxide SiO₂ l50 g Manganese carbonate MnCO₃.0.5H₂O l.5 g Boron trioxide B₂O₃ 0.5 g Arsenic trioxide As₂O₃ 0.05 g The above raw materials were thoroughly pulverized and mixed in a dry system ball mill, then filled in an alumina crucible, and fired in the air at l250°C for 4 hours. The material thus obtained was treated in the same manner as in Example l to obtain a phosphor of the present invention having a composition of Zn₂SiO₄:Mn 0.005 ,As 0.0001 ,B 0.006 . This phosphor had a molar ratio of the trivalent element to the pentavalent element of 60 and a fluorescence-maintaining rate of 99%. No after-glow degradation was observed. EXAMPLE 3 Zinc oxide ZnO 370 g Silicon dioxide SiO₂ l50 g Manganese carbonate MnCO₃.0.5H₂O 5 g Antimony trioxide Sb₂O₃ 0.5 g To the above raw materials, a suitable amount of purified water was added, and the mixture was thoroughly mixed to obtain a paste. Then, 5 ml of an aqueous solution containing 0.5 mol/liter of B₂O₃ and 5 ml of an aqueous solution containing 0.05 ml/liter of As₂O₅ were added thereto and mixed. Then, the subsequent operation including firing and washing was conducted in the same manner as in Example l to obtain a phosphor of the present invention having a composition of Zn₂SiO₄:Mn 0.015 ,As 0.0001 ,B 0.002 ,Sb 0.001 . This phosphor had a molar ratio of the trivalent element to the pentavalent element of about l.8 and a fluorescence-maitaining rate of 98%. No after-glow degradation was observed. EXAMPLE 4 Zinc oxide ZnO 390 g Silicon dioxide SiO₂ l50 g Manganese carbonate MnCO₃.0.5H₂O 2.5 g Borax Na₂B₄O₇.l0H₂O 2.0 g Arsenic trioxide As₂O₃ 0.05 g Antimony trioxide Sb₂O₃ 0.5 g The above raw materials were thoroughly mixed in a dry system ball mill, then filled in an alumina crucible, and fired in the air at l250°C for 4 hours. The material was treated in the same manner as in Example l to obtain a phosphor of the present invention having a composition of Zn₂SiO₄:Mn 0.008 ,As 0.0001 ,B 0.006 ,Sb 0.001 . This phosphor had a molar ratio of the trivalent element to the pentavalent element of about 5.5 and a fluorescence-maintaining rate of 98%. No after-glow degradation was observed. Further, a trace amount of Na was detected in the matrix of this phosphor. EXAMPLE 5 Zinc oxide ZnO 370 g Silicon dioxide SiO₂ l50 g Manganese carbonate MnCO₃.0.5H₂O 2.5 g Boron trioxide B₂O₃ 0.5 g Arsenic trioxide As₂O₃ 0.05 g Antimony trioxide Sb₂O₃ l g Barium iodide BaI₂ 2.5 g The above raw materials were thoroughly pulverized and mixed in a dry system ball mill, then filled in an alumina crucible, and fired in the air at l250°C for 4 hours. The material thus obtained was treated in the same manner as in Example l to obtain a phosphor of the present invention having a composition of Zn₂SiO₄:Mn 0.008 ,As 0.0001 ,B 0.006 ,Sb 0.002 . This phosphor had a molar ratio of the trivalent element to the pentavalent element of about 2.9 and a fluorescence-maintaining rate of 99%. No after-glow degradation was observed. Further, 0.l% by weight of Ba was detected in the matrix of this phosphor. EXAMPLE 6 Zinc oxide ZnO 370 g Silicon dioxide SiO₂ l50 g Manganese carbonate MnCO₃.0.5H₂O 2.5 g Boron trioxide B₂O₃ 0.5 g Antimony trioxide Sb₂O₃ l g The above raw materials were thoroughly pulverized and mixed in a dry system ball mill, then filled in an alumina crucible, and fired in the air at l250°C for 4 hours. The material thus obtained was treated in the same manner as in Example l to obtain a phosphor of the present invention having a composition of Zn₂SiO₄:Mn 0.008 ,B 0.006 ,Sb 0.002 . This phosphor had a molar ratio of the trivalent element to the pentavalent element of 3 and a fluorescence-maintaining rate of 99%. No after-glow degradation was observed. EXAMPLE 7 Zinc oxide ZnO 370 g Silicon dioxide SiO₂ l50 g Manganese carbonate MnCO₃.0.5H₂O 2.5 g Indium trioxide In₂O₃ l.9 g Arsenic trioxide As₂O₃ 0.05 g Antimony trioxide Sb₂O₃ l.5 g The above raw materials were thoroughly pulverized and mixed in a dry system ball mill, then filled in a quartz crucible, and fired in the air at l300°C for 4 hours to obtain a phosphor of the present invention having a composition of Zn₂SiO₄:Mn 0.008 ,In 0.003 ,As 0.001 ,Sb 0.001 . This phosphor had a fluorescence-maintaining rate of 99%, and no after-glow degradation was observed. Whereas, the conventional phosphor (Zn₂SiO₄:Mn 0.008 ,As 0.0001 ) had a fluorescence-maintaining rate of 94%. EXAMPLE 8 Zinc oxide ZnO 390 g Silicon dioxide SiO₂ l50 g Manganese carbonate MnCO₃.0.5H₂O l.5 g Indium trioxide In₂O₃ 0.6 g Boron trioxide B₂O₃ 0.25 g Arsenic trioxide As₂O₃ 0.05 g Antimony trioxide Sb₂O₃ l g The above raw materials were thoroughly pulverized and mixed in a dry system ball mill, then filled in a quartz crucible, and fired in the air at l300°C for 4 hours to obtain a phosphor of the present invention having a composition of Zn₂SiO₄:Mn 0.005 ,In 0.001 ,B 0.003 ,As 0.0001 ,Sb 0.002 . The fluorescence-maintaining rate was 99%, and no after-glow degradation was observed. The conventional phosphor had a fluorescence-maintaining rate of 94%. EXAMPLE 9 Zinc oxide ZnO 390 g Silicon dioxide SiO₂ l50 g Manganese carbonate MnCO₃.0.5H₂O 2.5 g Indium trioxide In₂O₃ l.9 g Antimony trioxide Sb₂O₃ 0.5 g The above raw materials were thoroughly pulverized and mixed in a dry system ball mill, then filled in a quartz crucible, and fired in the air at l300°C for 4 hours to obtain a phosphor of the present invention having a composition of Zn₂SiO₄:Mn 0.008 ,In 0.003 ,Sb 0.001 . The fluorescence-maintaining rate was 99%, and no after-glow degradation was observed. The conventional phosphor (Zn₂SiO₄:Mn 0.008 ) had a fluorescence-maintaining rate of 93%. EXAMPLE l0 Zinc oxide ZnO 370 g Silicon dioxide SiO₂ l50 g Manganese carbonate MnCO₃.0.5H₂O 2.5 g Indium trioxide In₂O₃ 0.6 g Borax Na₂B₄O₇.l0H₂O 2.l g Arsenic trioxide As₂O₃ 0.09 g Antimony trioxide Sb₂O₃ 0.5 g The above raw materials were thoroughly pulverized and mixed in a dry system ball mill, then filled in a quartz crucible, and fired in the air at l300°C for 4 hours to obtain a phosphor of the present invention having a composition of Zn₂SiO₄:Mn 0.008 ,In 0.001 ,B 0.006 ,As 0.0002 ,Sb 0.001 . The fluorescence-maintaining rate was 99%, and no after-glow degradation was observed. The conventional phosphor had a fluorescence-maintaining rate of 94%. EXAMPLE ll Zinc oxide ZnO 390 g Silicon dioxide SiO₂ l50 g Manganese carbonate MnCO₃.0.5H₂O 2.5 g Indium trioxide In₂O₃ 0.6 g Arsenic trioxide As₂O₃ 0.05 g The above raw materials were thoroughly pulverized and mixed in a dry system ball mill, and filled in a quartz crucible, and fired in the air at l300°C for 4 hours to obtain a phosphor of the present invention having a composition of Zn₂SiO₄:Mn 0.008 ,In 0.001 ,As 0.0001 . The fluorescence-maintaining rate was 99%, and no after-glow degradation was observed. Whereas, a phosphor having a composition of Zn₂SiO₄:Mn 0.008 ,As 0.0001 had a fluorescence-maintaining rate of 94%.

Claims: 1. A silicate phosphor comprising manganese as an activator, a trivalent element and a pentavalent element, wherein said trivalent element is at least one element selected from the group consisting of boron and indium, said pentavalent element is at least one element selected from the group consisting of arsenic, antimony and bismuth, the content of the trivalent element is from l × l0⁻⁴ to 2 × l0⁻² gram-atom/mol, the content of the pentavalent element is not more than 3 × l0⁻³ gram-atom/mol, and the molar ratio of the trivalent element to the pentavalent element (trivalent element/pentavalent element) is at least l.5. 2. The phosphor according to Claim l, wherein the trivalent element is boron alone, and the content of boron is from 2 × l0⁻⁴ to 2 × l0⁻² gram-atom/mol. 3. The phosphor according to Claim l, wherein the trivalent element is indium only, and the content of indium is from l × l0⁻⁴ to l × l0⁻² gram-atom/mol. 4. The phosphor according to Claim l, wherein the content of arsenic is not more than l × l0⁻³ gram-atom/mol. 5. The phosphor according to Claim l, wherein the content of the trivalent element is from l × l0⁻³ to l × l0⁻² gram-atom/mol in the case of boron alone or a combination of indium and boron, or from 2 × l0⁻⁴ to 5 × l0⁻³ gram-atom/mol in the case of indium alone, and the molar ratio of the trivalent element to the pentavalent element is at least l.8. 6. The phosphor according to Claim l, wherein the molar ratio of the trivalent element to the pentavalent element is at least l.8. 7. The phosphor according to Claim l, wherein the pentavalent element is arsenic alone, and the molar ratio of the trivalent element to the pentavalent element is at least 5. 8. The phosphor according to Claim 7, wherein the content of arsenic is from 7 × l0⁻⁵ to 8 × l0⁻⁴ gram-atom/mol. 9. The phosphor according to Claim l, wherein the content of manganese is from l × l0⁻³ to 3 × l0⁻² gram-atom/mol. l0. The phosphor according to Claim l, wherein the content of manganese is from 2 × l0⁻³ to l × l0⁻² gram-atom/mol. 11. The phosphor according to Claim l, wherein the pentavalent element is arsenic, the trivalent element is boron, and the contents of arsenic and boron are from 5 × l0⁻⁵ to l × l0⁻³ gram-atom/mol and from 3 × l0⁻³ to l.2 × l0⁻² gram-atom/mol, respectively.

Inventors: MIKAMI, TOMOKI, NATSUGARI, MITSUHARU, OOMATOI,SUSUMU, TOKUNAGA, YUKIO, YOKOTA, SHINJI
Applicants: KASEI OPTONIX, LTD.
Application year: 1987
Main classification: C09K11
IPC codes: C09K11