DEINKING COMPOSITION FOR RECLAMATION OF WASTE PAPER

Abstract: A deinking composition and a process for preparing it for the reclamation of waste paper comprises (a) an alkylene oxide adduct to a mixture of a natural oil or fat and a polyhyd­ ric alcohol and (b-1) an alkylene oxide adduct of a higher alcohol, and/or (b-2) a sulfate of (b-1) and/or (b-3) a higher fatty acid.

Description: The present invention relates to a deinking agent used for the reclamation of waste paper such as newspapers or magazines. More particularly, the invention relates to a deinking agent for the reclamation of waste paper such as newspapers or magazines by the flotation method to obtain deinked pulp having a high degree of whiteness and low residual ink droplet number. Newspapers and magazines have been reclaimed for reuse from old times and, recently, their reclamation becomes more important and extensive use of deinked pulp is highly demanded. On the other hand, the deinking of recent waste paper is quite different because of changes in the printing techniques, printing system and printing ink composition. Under these circumstances, deinking devices have also been improved variously to enhance the efficiency. Chemicals used for separating and removing ink and other impurities from waste paper in the prior art include alkalis such as sodium hydroxide, silicate and phosphate; bleaching agents such as hydrogen peroxide, hyposulfites and hypochlorites; and sequestering agents such as DTPA and EDTA. In combination with these chemicals, deinking agents are used, which include anionic surfactants such as alkylbenzenesulfonates, higher alcohol sulfate salts, α-olefinsulfonates and dialkyl sulfosuccinates; and nonionic surfactants such as, ethylene oxide adducts of higher alcohols, alkylphenols and fatty acids, ethylene oxide/propylene oxide adducts and alkanolamides. These agents are used either alone or in the form of a mixture of two or more of them. Examples of such deinking solutions are disclosed in US-A-4 162 186 and JP-A-239 585/85 of which the latter discloses a deinking agent a) obtained by reacting an alkylene oxide with a fat/polyol mixture. However, when these deinking agents are used in the flotation method, the capacities of them for separating and removing the ink are poor. Thus, the development of a deinking agent having a high ink coagulating power has been demanded. Deinking agents including fatty acids, as disclosed in JP-A-239 586/85 and JP-A-239 587/85 are also known. However, although fatty acids (which form fatty acid soaps with sodium hydroxide used in the waste paper disinteration step) have been know as deinking agents having the highest deinking capacity in the flotation step, they have defects that (1) when they are used in the treatment of waste newspapers and magazines, the ink released from the waste paper deposits on the surface of the device to cause troubles, (2) the foamability of them in the flotation step is very low and, therefore, suspending coagulated ink cannot be removed sufficiently and ink spots remaining in the obtained pulp cause troubles in the subsequent steps and (3) the fatty acids are required in an amount far larger than those of anionic surfactants and nonionic surfactants for obtaining the intended effects and, therefore, the chemical costs are high. Summary of the Invention A purpose of the invention is to present a deinking agent and overcome the above shown defects. The deinking composition according to the invention has a high capacity of releasing the ink from waste paper and can remove the released ink from the pulp fibers by adsorption on foams in the flotation treatment step to form deinked pulp having a high degree of whiteness and a low residual ink droplet number and unreleased ink droplet number. A deinking composition of the invention is useful for reclamation of waste paper and comprises (a) a reaction product obtained by adding an alkylene oxide to a mixture of a natural oil or fat and a polyhydric alcohol, characterised by also comprising (b) a compound selected from the group consisting of (b1) an alkylene oxide adduct of a higher alcohol having the formula (1): in which R is an alkyl or alkenyl having 12 to 18 carbon atoms, A is an alkylene having 2 to 4 carbon atoms and n is 5 or more on the average, (b2) a sulfate of an alkylene oxide adduct of a higher alcohol having the formula (2): in which R′ is an alkyl or alkenyl having 10 to 18 carbon atoms, A′ is an alkylene, m is from 0.3 to 5 on the average an M is hydrogen, an alkali metal or ammonium, and (b3) a higher fatty acid having 8 to 22 carbon atoms or a salt thereof. The weight ratio of (a) to (b) ranges from 99/1 to 30/70. It is preferred that said reaction product (a) is a product obtained by adding 5 moles or more of an alkylene oxide to 1 mole in total of a mixture of a natural oil or fat and a polyhydric alcohol, a weight ratio of the natural oil or fat to the polyhydric alcohol ranging from 1/0.1 to 1/3. The invention includes two preferable embodiments. One embodiment comprises (a) and (b) selected from the group consisting of (b1) and (b2), a weight ratio of (a) to (b) ranging from 99/1 to 50/50. The other comprises (a) and (b3), a weight ratio of (a) to (b3) ranging from 95/5 to 30/70. The invention will be explained in detail below first in respect to the first embodiment comprising (a) and (b1) or (b2). The present invention provides a deinking agent for reclamation of waste paper comprising: (a) a reaction product obtained by adding an alkylene oxide to a mixture of a natural oil or fat and a polyhydric alcohol, characterised by also comprising (b) a compound of the general formula (1) and/or a compound of the general formula (2): wherein R represents an alkyl or alkenyl group having 12 to 18 carbon atoms, AO represents two or more kinds of hydroxyalkylene groups having 2 to 4 carbon atoms and n represents a number of at least 5 on average, and wherein R′ represents an alkyl or alkenyl group having 10 to 18 carbon atoms, A′O represents a hydroxyalkylene group having 2 to 4 carbon atoms, m represents a number of 0.3 to 5 on average and M represents H, an alkali metal or ammonium, in a weight ratio of (a)/(b) of 99/1 to 50/50. The natural oils and fats used in the present invention include vegetable oils such as coconut oil, palm oil, olive oil, soybean oil, rapeseed oil and linseed oil; animal oils such as lard, beef tallow and bone oils; fish oils; and hardened and semi-hardened oils derived from them as well as recovered oils obtained in the steps of purification of these oils and fats. The polyhydric alcohols used in the present invention include ethylene glycol, propylene glycol, trimethylene glycol, butylene glycol, glycerol, trimethylolpropane, trimethylolethane, 1,2,4-butanetriol, 1,2,6-hexanetriol, 1,1,1-trimethylolhexane, pentaerythritol, tetramethylolcyclohexanol and diglycerol. The alkylene oxides to be added to the mixture of said natural oil or fat and polyhydric alcohol include, for example, ethylene oxide, propylene oxide and butylene oxide. The alkylene oxide adducts can be prepared by mixing the alkylene oxide with said mixture (random addition) or by the successive addition (block addition). The random addition or block addition of ethylene oxide and an alkylene oxide other than ethylene oxide are preferred. The mixing molar ratio of the natural oil or fat to the polyhydric alcohol is 1/0.1 to 1/3, preferably 1/0.3 to 1/2. The alkylene oxide is used in an amount of preferably at least 5 mol, particularly, 20 to 100 mol, per mol of the total of the natural oil or fat and polyhydric alcohol. When the amount of the alkylene oxide is less than 5 mol, the power of releasing the ink from the waste paper, ink-scavenging capacity and foamability in the flotation step are reduced and the intended deinked pulp having a high quality cannot be obtained. The compounds of the above general formula (1) used in the present invention are prepared by adding an alkylene oxide to an alcohol. When the alkyl or alkenyl group R in the above general formula has a carbon number outside the range of 12 to 18, the ink-releasing power, ink-scavenging capacity and foamability are reduced unfavorably. The alkylene oxide addition is preferably the random addition or block addition of ethylene oxide and an alkylene oxide other than ethylene oxide, i.e. propylene oxide or butylene oxide. The molar ratio of ethylene oxide to propylene oxide or butylene oxide is preferably 1/1 to 3/1. The number n in the above formula is at least 5 on average, preferably in the range of 20 to 100. The compounds of the above general formula (2) used in the present invention are prepared by adding said alkylene oxide to said alcohol and sulfating the obtained adduct. When the alkyl or alkenyl group R′ in the above general formula has a carbon number outside the range of 10 to 18, the foamability and ink-scavenging capacity in the flotation step are reduced. The same applies to a case wherein m exceeds 5. It is important in the deinking agent of the present invention that the weight ratio of the component (a) to the component (b1) or (b2) is 99/1 to 50/50. When said ratio is outside said range, the balance of the ink-releasing power, ink-scavenging power and foamability is broken and, therefore, any deinked pulp having a high quality cannot be obtained and the stable operation becomes difficult. When the component (b) is particularly a compound of the above general formula (1), the ratio of (a)/(b) is preferably 80/20 to 60/40. When the component (b) is a compound of the above general formula (2), the ratio of (a)/(b) is preferably 95/5 to 80/20. The invention will be illustrated below in respect to the second embodiment comprising (a) and (b3). The above shown (a) can be used here. The composition comprises (a) and (b3) a higher fatty acid having 8 to 22 carbon atoms or a salt thereof, a weight ration to (a) to (b3) ranging from 30/70 to 95/5, preferably from 40/60 to 70/30. When the weight ratio falls outside the range, the balance of the ink coagulation and foamability in the flotation step is broken and therefore the pulp having a high degree of whiteness and a low residual ink droplet number cannot be obtained and the stable operation becomes difficult. It is important that the higher fatty acids used in the present invention have 8 to 22, preferably 8 to 18, carbon atoms. When the number of carbon atoms is less than 8, the ink-coagulating effects are reduced, while and when it exceeds 22, the deinking effects are reduced. Examples of the fatty acids having 8 to 22 carbon atoms include caprylic, capric, lauric, myristic, palmitic, stearic and oleic acids. The higher fatty acids include not only those having a given carbon number but also mixtures of these acids having various carbon numbers, such as beef tallow fatty acids or coconut fatty acids. Since sodium hydroxide is used in combination with the higher fatty acids, these acids act as fatty acid soaps in the waste paper disintegration step. Therefore, the higher fatty acids may be used in the form of their salts such as sodium, potassium or ammonium salts. Though the deinking agent of the present invention may be used in either or both of the waste paper disintegration step and the aging tower step, the maximum effects can be obtained by using it in the waste paper disintegration step. The amount of the deinking agent is preferably 0.2 to 1.0 wt.% based on the waste paper to be treated. The deinking agent of the present invention can be used also in combination with known deinking agents conventionally used heretofore. The following examples will further illustrate the present invention, which by no means limit the invention. Example 1 Components (a) having compositions shown in Table 1 (samples 1 to 10) were prepared. Then the component (a) was mixed with the component (b) shown in Table 2 in a weight ratio shown in Table 2 to obtain deiking agents. Waste newspapers recovered in the town were cut into pieces having a size of 2 x 5 cm. A given amount of the pieces was placed in a bench disintegrator, to which were then added water, 1.0% (by weight based on the starting material; the same shall apply hereinafter) of sodium hydroxide, 3.0% of sodium silicate, 3.0% of a 30% aqueous hydrogen peroxide solution and 0.4% of a deinking agent shown in Table 2. After the disintegration carried out at 55°C for 20 min while the pulp concentration was kept at 5%, aging was effected at 50°C for 60 min. Then, the mixture was diluted with water to a pulp concentration of 1.0%, 1.0% of CaCl₂ was added thereto and the flotation treatment was effected at 30°C for 10 min. After completion of the flotation, the pulp slurry was concentrated to 6%. The concentrate was diluted to 1% with water and shaped into pulp sheets with a TAPPI sheet machine. The degrees of whiteness of the obtained pulp sheets were measured with a colorimetric color-difference meter and the residual ink droplet number and unreleased ink droplet number were determined with an image analyzer (x 126). The results are summarized in Table 2. Example 2 Waste newspapers recovered in the town were cut into pieces having a size of 2 x 5 cm. A given amount of the pieces was placed in a bench disintegrator, to which were then added water, 1.0% of sodium hydroxide, 0.5% of sodium silicate No. 3 and 0.4% of a deinking agent shown in Table 3. After carrying out disintegration at 45°C for 20 min while the pulp concentration was kept at 5%, the mixture was dehydrated to a pulp concentration of 18%. 1.5% of sodium hydroxide, 2.5% of sodium silicate No. 3 and 3.0% of a 30% aqueous hydrogen peroxide solution were added thereto. After mixing them, the aging treatment was effected at 55°C for 90 min while the pulp concentration was kept at 15%. Then, water was added thereto to adjust the pulp concentration at 4%. After disintegration on the bench disintegrator for 5 min, the mixture was diluted with water to a pulp concentration of 1.0%. 1.0% of CaCl₂ was added thereto and the flotation treatment was effected at 30°C for 10 min. After completion of the flotation, the pulp slurry was concentrated to 6%. The concentrate was diluted to 1% with water and shaped into pulp sheets with a TAPPI sheet machine. The degrees of whiteness of the obtained pulp sheets were measured with a colorimetric color-difference meter and the residual ink droplet number and unreleased ink droplet number were determined with an image analyzer (x 126). The results are summarized in Table 3. Example 3 The component (a) was prepared to obtain samples 1 to 6 as shown in Table 4. Then, waste newspapers recovered in the town were cut into pieces having a size of 2 x 5 cm. A given amount of the pieces was placed in a bench disintegrator, to which were then added water, 1,0% (by weight based on the starting material; the same shall apply hereinafter) of sodium hydroxide, 3.0% of sodium silicate, 3.0% of a 30% aqueous hydrogen peroxide solution and 0.4% of a deinking agent shown in Table 5. After the disintegration carried out at 55°C for 20 min while the pulp concentration was kept at 5%, aging was effected at 50°C for 60 min. Then, the mixture was diluted with water to a pulp concentration of 1.0%, 1.0% of CaCl₂ was added thereto and the flotation treatment was effected at 30°C for 10 min. After completion of the flotation, the pulp slurry was concentrated to 6%. The concentrate was diluted to 1% with water and shaped into pulp sheets with a TAPPI sheet machine. The degrees of whiteness of the obtained pulp sheets were measured with a colorimetric color-difference meter and the residual ink droplet number was determined with an image analyzer (x 126). The results are summarized in Table 5. Example 4 Waste newspapers recovered in the town were cut into pieces having a size of 2 x 5 cm. A given amount of the pieces was placed in a bench disintegrator, to which were then added water, 1.0% of sodium hydroxide, 0.5% of sodium silicate No. 3 and 0.4% of a deinking agent shown in Table 6. After carrying out disintegration at 45°C for 20 min while the pulp concentration was kept at 5%, the mixture was dehydrated to a pulp concentration of 18%. 1.5% of sodium hydroxide, 2.5% of sodium silicate No. 3 and 3.0% of a 30% aqueous hydrogen peroxide solution were added thereto. After mixing them, the aging treatment was effected at 55°C for 90 min while the pulp concentration was kept at 15%. Then, water was added thereto to adjust the pulp concentration at 4%. After disintegration on the bench disintegrator for 5 min, the mixture was diluted with water to a pulp concentration of 1.0%. 1.0% of CaCl₂ was added thereto and the flotation treatment was effected at 30°C for 10 min. After completion of the flotation, the pulp slurry was concentrated to 6%. The concentrate was diluted to 1% with water and shaped into pulp sheets with a TAPPI sheet machine. The degrees of whiteness of the obtained pulp sheets were measured with a colorimetric color-difference meter and the residual ink droplet number was determined with an image analyzer (x 126). The results are summarized in Table 6.

Claims: 1. A deinking composition for reclamation of waste paper, which comprises (a) a reaction product obtained by adding an alkylene oxide to a mixture of a natural oil or fat and a polyhydric alcohol, characterised by also comprising (b), in which (b) is (b1) an alkylene oxide adduct of a higher alcohol having the formula (1): in which R is an alkyl or alkenyl having 12 to 18 carbon atoms, A is an alkylene having 2 to 4 carbon atoms and n is 5 or more on the average, and/or (b2) a sulfate of an alkylene oxide adduct of a higher alcohol having the formula (2): in which R′ is an alkyl or alkenyl having 10 to 18 carbon atoms, A′ is an alkylene, m is from 0.3 to 5 on the average and M is hydrogen, an alkali metal or ammonium, and/or (b3) a higher fatty acid having 8 to 22 carbon atoms or a salt thereof, wherein the weight ratio of (a) to (b) ranges from 99/1 to 50/50 when (b) is (b1), (b2), or mixtures thereof, and from 95/5 to 30/70 when (b) is (b3). 2. A composition as claimed in Claim 1, in which said reaction product (a) is a product obtained by adding 5 moles or more of an alkylene oxide to 1 mole in total of a mixture of a natural oil or fat and a polyhydric alcohol, the weight ratio of the natural oil or fat to the polyhydric alcohol ranging from 1/0.1 to 1/3. 3. A process for preparing a deinking composition for reclamation of waste paper, which comprises (a) reacting together an alkylene oxide and a mixture comprising a natural oil or fat and a polyhydric alcohol, characterised by also (b) reacting together an alkylene oxide and a higher alcohol to obtain an adduct having the formula (1): in which R is an alkyl or alkenyl having 12 to 18 carbon atoms, A is an alkylene having 2 to 4 carbon atoms and n is 5 or more on the average, and/or sulfating an alkylene oxide adduct of a higher alcohol to obtain a sulfate having the formula (2): in which R′ is an alkyl or alkenyl having 10 to 18 carbon atoms, A′ is an alkylene, m is from 0.3 to 5 on the average and M is hydrogen, an alkali metal or ammonium, and mixing together the product of reaction (a) with adduct (1) and/or sulfate (2) and/or a higher fatty acid having 8 to 22 carbon atoms, or a salt thereof to obtain a weight ratio of (a) to (b) which ranges from 99/1 to 50/50 when (b) is the adduct (1), the sulfate (2), or mixtures thereof and from 95/5 to 30/70 when (b) is a higher fatty acid. 4. A process as claimed in Claim 3, in which said reaction (a) is performed by adding 5 moles or more of an alkylene oxide to 1 mole in total of a mixture of a natural oil or fat and a polyhydric alcohol, the weight ratio of the natural oil or fat to the polyhydric alcohol ranging from 1/0.1 to 1/3.

Inventors: HAMAGUCHI, KOJI, MIYAUCHI, YOSHITAKA, TOGASHI, FUMIHIKO
Applicants: KAO CORPORATION
Application year: 1987
Main classification: D21C5
IPC codes: D21C5, C08L71, C08G65