Uniform polymer particles

Abstract: Uniform polymer particles in a spherical form, having a three dimensional network structure, wherein not less than 80 % by volume of the whole particles have a particle size within the range of ±20 % of the volume average particle size of said uniform polymer particles, and said uniform polymer particles do not include particles having a particle size of not more than 5 % of the volume average particle size, a process for preparing the uniform polymer particles, an apparatus suitable for use in the process, and uniform polymer particles in a spherical form suitable for use in a direct extracorporeal hemo-perfusion treatment. The uniform polymer particles of the present invention can be also used in various uses such as a parent material for an ion exchange resin, an adsorbent, and a packing material for a chromatography.

Description: The present invention relates to uniform polymer particles which in particular are suitable for use in a direct extracorporeal hemo-perfusion treatment, a process for preparing these uniform polymer particles, and an apparatus suitable for use in this process. More particularly, the present invention relates to uniform polymer particles having a narrow particle size distribution which can be widely used, for instance, as a parent material for an ion exchange resin, as a packing for a chromatography, as a support onto which an enzyme is immobilized, as a support for an affinity chromatography, as a material for a foamed article, and in a direct extracorporeal hemo-perfusion treatment; to a process for preparing these uniform polymer particles; and to an apparatus for forming uniform liquid droplets by jetting a liquid with a high viscosity containing a natural high molecular substance or a synthetic high molecular substance from an orifice at a constant flow rate with applying cyclic turbulences having a constant frequency thereto. As methods for preparing polymer particles in a spherical form, there have been hitherto known dispersion methods and spray methods. According to a dispersion method, polymer particles are obtained by coagulating a dilute polymer solution containing a pore-forming agent being dispersed in the form of droplet in a dispersion medium containing a surface active agent, through volatilizing the solvent thereof [cf. Japanese Unexamined Patent Publication (Tokkyo Kokai) No. 24430/1981], or through gradually adding a coagulating agent for the droplets [cf. Japanese Unexamined Patent Publication (Tokkyo Kokai) No. 159801/1982]. However, in the dispersion method, no polymer particles other than polymer particles with a broad particle size distribution can be obtained. Also, in the dispersion method, in order to remove the solvent, the dispersion medium and the surface active agent from the coagulated particles, it is necessary to wash the coagulated particles not only with water but also with an organic solvent. There is known another dispersion method in which polymer particles are obtained by polymerizing polymerizable monomers after dispersing the monomers in a dispersion medium, the polymer particles thereby obtained also has a broad particle size distribution. In observing the particles by an electron microscope, there can be found that minute spherical particles aggregate to form a particle. When a suspension of the above-obtained particles is stirred by a magnetic stirrer, minute polymer chips occur in a large amount, which is presumed to be due to the above-described structure of the particles. Further, the particles obtained by the above method have pores with a broad pore size distribution. Especially, on the particle surface, the particles have various size of openings. According to a spray method, polymer particles is obtained by spraying a polymer solution into a coagulating liquid. Thus obtained polymer particles also have a broad particle size distribution and the particles have relatively large particle size [cf. Japanese Unexamined Patent Publication (Tokkyo Kokai) No. 129788/1977]. Polymer particles with a broad particle size distribution require a further process of classification. As generally known, by a classifying process, for instance, a sieving process, it is possible to make not less than 80 % by volume of the whole particles have a particle size within the range of ±20 % of the volume average particle size. In the sieving process, it is also possible to remove particles with a particle size of not less than the size of sieve opening by the sieve. However, in order to pass all of the particles with a particle size of less than the size of sieve opening, a long time sieving is necessary. Further, taking the sieving process results in a very low yeild. Therefore, it is not industrially practical to take such a process. Particularly, it is practically very difficult or virtually impossible to remove all of particles having a particle size of not more than 5 % of the volume average particle size. When very small particles or very large particles are included in the polymer particles, various problems arise in uses of the particles. For instance, when the particles are used as a packing for chromatography or an adsorbent, the very small particles are mixed in the liquid to be treated, or cause a large pressure drop, and the very large particles cause a lowering the separation efficiency or the adsorption rate. When particles having pores with a broad pore size distribution, particularly openings on the particle surface with a broad opening size distribution are used as an adsorbent, such particles cause an inferior physical selectivity. Recently, there has been found a technique for forming uniform liquid droplets, in which cyclic turbulences are applied to a liquid jetted at a constant flow rate (hereinafter such technique referred to as "vibration method"). There has been already reported that uniform particles are obtained by applying the above technique to the dispersion method using polymerizable monomers [cf. Japanese Unexamined Patent Publication (Tokkyo Kokai) 102905/1982]. However, the particles thus obtained have the above-stated structure, i.e. minute particles coagulate to form a particle, and therefore the particles have defects that polymer chips easily occur and that the particles have pores with a broad pore size distribution. There are reported some examples of that polymer particles or capsules are prepared by applying the vibration method [cf. Japanese Unexamined Patent Publication (Tokkyo Kokai) No. 129686/1977 and Japanese Unexamined Patent Publication (Tokkyo Kokai) No. 112833/1964]. However, in an example disclosed in Japanese Unexamined Patent Publication No. 129686/1977, a very dilute polymer solution, i.e. a solution with a very low viscosity are employed and micro-capsules are prepared in another example disclosed in Japanese Unexamined Patent Publication No. 112833/1984, and particles with a large particle size are prepared since nozzles themselves are directly vibrated and therefore the vibration frequency is restricted to a low frequency. In both examples, it is necessary that a multiple tubular nozzle is employed and more than one kinds of solutions are simultaneously jetted with keeping a delicate balance. Also, in Japanese Examined Patent Publication (Tokkyo Kokoku) No. 33134/1981, there is disclosed that the vibration method is applied to a process for preparing uniform particles of an inorganic compound. In this or other publications, cyclic turbulences of flow rate of the liquid jetted from an orifice of a nozzle are applied by applying vibrational energy to the whole nozzle part. Generally, the force F [10 -5 N (dyn)] required to vibrate an object with a mass M (g) at a frequency f (Hz) with an amplitude 2D (cm) is calculated by the following equation: F = M·(2πf) 2 ·D For instance, when the total vibrating mass of nozzle and vibration transmission part is 1,000 g, the frequency is 10,000 Hz and the amplitude is 10 µm, F is about 2·10 4 N (2 x 10 9 dyn). In order to stably generate the above vibration by an electromagnetic coil vibrator, there is required an electric power as enormous as several decades KVA. Therefore, it is not economical to directly vibrate the nozzles, particularly when a high frequency of vibration is required. In EP-A-0 173 518 which corresponds to Japanese Unexamined Patent Publication (Tokkyo Kokai) No. 83202/1986, it is disclosed that the vibration method is applied to form uniform liquid droplets of polymerizable monomers. In this case, such enormous energy as in the previous case is not required since the vibration is directly transmitted to polymerizable monomers by piezoelectric vibrator which itself constitutes a part of vessel containing the monomers which are jetted through the orifices. However, when employing a high viscosity liquid such as a polymer solution, not a low viscosity liquid such as a polymerizable monomer, it is supposed that a high pressure is imposed on the piezoelectric vibrator and therefore the vibrator is destroyed or the vibrator does not generated a stable vibration. Also, there is the possibility that the vibrator does not vibrate a stable vibration when the liquid is heated in order to reduce the viscosity. US-A-4 485 055 discloses a process for producing shaped particles, that process comprising centrifugally expelling a liquid form product from a rotating member in the form of particles, and introducing that particles in a radially outward direction. However, no uniform polymer particles having a narrow particle size distribution can be obtained according to this process. US-A-3 702 748 discoses an apparatus wherein a vertically reciprocating needle is used for formation of particles (pellets). The pellet bodies are formed by utilizing not frequency of movement but valve function of the above mentioned needle. Also in this process uniform polymer particles having a narrow particle size distribution cannot be obtained. W.E. Yates and his co-worker developed an apparatus for preparing uniform liquid droplets using a magnetostrictive vibrator as a vibration generator. [cf. W.E. Yates and N.B. Akesson, Proceedings of the 1st International Conference on Liquid Atomization and Spary Systems (Proc. ICLASS), 181-185 and 459 to 460 (1978)]. In the above apparatus, the vibration transmission part is embedded in a fixing cylinder with a potting agent, and at the end thereof is fixed to a vibrating rod. As well known by a person skilled in the art, the vibration transmission part is precisely designed so as to resonate with the vibration generated by the magnetostrictive vibrator and so as to have a function of amplifying its small amplitude of vibration. The vibrating rod is also precisely designed so that, the amplitude reaches its maximum at the end of rod by resonating with the vibration generated by magnetostrictive vibrator. Therefore, when the vibration-transmission part is heated or subjected to an external force, a constant vibration can not be obtained, since the vibration transmission part or the vibrating rod does not resonate with the magnetostrictive vibrator. In the apparatus of W. E. Yates et al., it is not possible to keep the temperature of the vibration transmission part constant and to restrict external force being applied only to the end of vibrating rod. Therefore, it is presumed that it is not possible to form uniform liquid droplets from a high temperature liquid or a high pressure liquid by the apparatus of W. E. Yates et al. Various conditions for preparing uniform liquid droplets by the vibration method have been studied in detail as disclosed by T. Sakai [cf. T. Sakai, Proc. ICLASS-'82, 37 to 45 (1982)]. It has been found that when uniform liquid droplets are stably formed, parameters including a viscosity and, a surface tension of the liquid, a flow rate of liquid jetted from the orifice, a size of the orifice, and a frequency and a displacement of cyclic turbulences are within a specific range (hereinafter, such specific range referred to as "synchronized condition"). As a general tendency, the higher the liquid viscosity becomes and the smaller the size of the orifice becomes, the higher flow rate and frequency of jetted liquid are required to be synchronized. That is, in order to form liquid droplets with a small diameter from a liquid containing high molecular substances, the aperture diameter of orifice must be small, and the flow rate and frequency of jetted liquid must be high. In addition, in many cases, such liquid has a high temperature and a high pressure. Consequently, it is difficult to form uniform liquid droplets with a small particle size from such liquid by applying the conventional methods. In recent years, there has been tried an extracorporeal hemo-perfusion treatment using an adsorbent, for various obstinate diseases and its effect has been confirmed. As generally known, blood cells are physiologically quite unstable outside of the body, and therefore easily injured, for instance, there occurs a decrease in their number because of their adhesion to the matters with which blood cells contact, hemolysis or coagulation. Therefore, in an extracorporeal hemoperfusion treatment, blood is separated into unstable blood cells and relatively stable blood plasma by a centrifugal separator or by a membrane for the separation of blood plasma, and then the blood plasma containing pathogenic substances is treated by an adsorbent. However, it is as a matter of course that if blood can be treated directly by an adsorbent, not only the extracorporeal hemo-perfusion treatment system can be remarkably simplified but also physiological burden to the patient can be alleviated. As for the relationship between blood compatibility and adsorbent characteristics, in other words, whether an adsorbent injures blood or not, though there are many points not explicated chemically, there has been physically explicated a point that in order not to injure blood, an adsorbent should be smooth on its surface and the pressure drop occured in using it should be small. A granular activated charcoal adsorbent has been employed in a direct extracorporeal hemo-perfusion system since decades ago [cf. T. M. S. Chang et al, Trans Amer. Soc. Artif. Int. Organs 17, 246 (1971)]. At the beginning, an adsorbent covered with a hydrophilic polymer was employed for the purpose of avoiding the effluence of activated charcoal and improving the chemical blood compatibility. Recently, uncovered activated charcoal with smooth surface has been employed [cf. V. Bonomini and T. M. S. Chang, "Hemoperfusion" (1981), ISBN 3-8055-3421-3]. This fact shows that the relationship between blood compatibility and chemical characteristics of adsorbent is hard to estimate since the chemical properties of the surface of the above two adsorbents are quite different. The granular activated charcoal has an relatively large average particle size of 0.5 to 3 mm. The granular activated charcoal adsorbent is employed with the object of adsorbing blood plasma components having a relatively low molecular weight. Such components can be rapidly adsorbed even if the granular activated charcoal has a large particle size. However, pathogenic substances causing obstinate diseases are, in many cases, substances having a high molecular weight of several handreds of thousand to several millions daltons. Since such substances having a high molecular weight diffuse at a low rate, it is required that particles for an adsorbent for such substances have a particle size of not more than about 400 µm, preferably not more than 300 µm so as to attain a practical adsorption rate. However, there has not been hitherto well known an example of carring out a direct extracorporeal hemo-perfusion treatment using granular activated charcoal adsorbent having such a small particle size. Though there is a report in which a direct extracorporeal hemo-perfusion treatment is carried out using a modified polyvinyl alcohol gel having particle sizes of 74 to 210 µm [cf. Ichikawa et al, Jinkozoki 12 (1), 116 (1983)], there are not reported data showing whether a hemolysis occurs or not and data of pressure drop, these data being basic data relating to blood compatibility. EP-A-0 051 210 describes spheroidal polymer beads which are prepared by suspension polymerisation of monomer droplets resulting in uniform polymer particles which have a volume average particle size of 10 to 1000 µm, which include particles having a particle size of more than 5 µm, wherein each particle has a spherical form and a macroporous structure and wherein at least 80 % by volume of the whole particles have a particle size within the range of ± 20 % of the volume average particle size. The US-A-4 302 166 describes a process for preparing uniform polymer particles having a narrow particle size distribution, comprising the following steps: jetting a polymer solution containing an added material, such as a dye, in the form of uniform liquid droplets with electric charges with the same sign from an orifice into a gas atmosphere at a constant flow rate while applying cyclic turbulences having a constant frequency to the solution, letting the droplets fly through the gas atmosphere, and then letting the droplets fall into a coagulating liquid which is a non-solvent of the polymer of the polymer solution, is miscible with the solvent of the polymer solution, and has a surface tension enough to spontaneously wet the liquid droplets, the droplets being in a spherical form at the collision with the coagulating liquid. An apparatus according to the initial part of claim 19 is known from BIOTECHNOLOGY AND BIOENGINEERING, VOL. 27, JUNE 1985, pages 870 - 876. As described above, in prior arts, there are defects that the polymer particles have a broad particle size distribution or that minute polymer chips occur due to the particle structure, and further that in preparing such polymer particles, such a complicated apparatus as a multiple tubular nozzle is necessary and a delicate operation is required. In a conventional apparatus for forming liquid droplets, it is difficult to form uniform liquid droplets having a small particle size from a high viscosity liquid. Further, when the liquid has a high temperature and a high pressure, it is still more difficult to form uniform liquid droplets with a coventional apparatus. As described above, though there has not been explicated what chemical properties an adsorbent should have so that a direct extracorporeal hemo-perfusion treatment can be carried out with employing the adsorbent, at least, the pressure drop occured in using it should be small, and the surface of adsorbent should be smooth. Further, there has not been clear what properties of adsorbent suitable for evaluating blood compatibility therewith since conventional adsorbents have a broad particle size distribution. As described above, there are many points not explicated chemically as to the relationship between blood compatibility and properties of adsorbent. Therefore, it is an object of the present invention to provide uniform particles having a narrow particle size distribution and such a structure which does not cause an occurence of minute polymer chips and which, in particular, are suitable for use in a direct extracorporeal hemo-perfusion treatment with a practical flow rate of blood to be treated without causing problems such as hemolysis and increase in pressure drop, as well as a process for preparing such particles and an apparatus suitable for use in this process which can form uniform liquid droplets from a liquid even if the liquid has not only a high viscosity but also a high temperature and a high pressure. The present inventors have found that uniform polymer particles in a spherical form, having a narrow particle size distribution and a three dimensional network structure which does not cause an occurrence of polymer chips can be prepared without using a complicated apparatus such as a multiple tubular nozzle when a polymer solution is jetted from an orifice into a gas atmosphere in the form of uniform liquid droplets with electric charges with a same sign at a constant flow rate while applying cyclic turbulences having a constant frequency to the solution, the droplets are let fly through the gas atmosphere, and then the droplets are let into a coagulating liquid which is a non-solvent of the polymer of the polymer solution, is miscible with the solvent of the polymer solution, and has a surface tension enough to spontaneously wet the liquid droplets, the distance of the gas atmosphere between the orifice and the surface of the coagulating liquid being such that the droplets are not greatly deformed by the collision with the coagulating liquid. The present inventors eagarly studied in order to provide uniform polymer particles suitable for use in direct extracorporeal hemo-perfusion treatment which do not cause problems such as hemolysis and increase in pressure drop even if their particle size is not more than 400 µm, and investigated particle properties required for direct extracorporeal hemo-perfusion treatment, with paying attention only to physical properties. As a result, the present inventors have found that a direct extracorporeal hemo-perfusion treatment can be carried out with a practical flow rate of blood to be treated without problems such as hemolysis and increase in pressure drop by using uniform polymer particles having a volume average particle size of 80 to 400 µm, wherein not less than 80 % by volume of the whole particles have a particle size within the range of ±20 % of the volume average particle size, the content of particles having a particle size of less than 74 µm is not more than 5 % by volume, the content of particles having a particle size of less than 25 µm is not more than 0.1 % by volume, and said uniform polymer particles do not include particles having a particle size of not more than 5 % of the volume average size. It is also found that such particles with a narrow particle size distribution are prepared by a process hitherto unknown. According to a first aspect the present invention relates to uniform polymer particles which have a volume average particle size of 10 to 1000 µm, which include particles having a particle size of more than 5 µm, wherein each particle has a spherical form and a three dimensional network structure, wherein at feast 80 % by volume of the whole particles have a particle size within the range of ± 20 % of the volume average particle size, and wherein the remaining particles have a particle size of more than 5 % of the volume average particle size, obtained by the following steps: jetting a polymer solution consisting of solvent and polymer in the form of uniform liquid droplets with electric charges with the same sign from an orifice into a gas atmosphere at a constant flow rate while applying cyclic turbulences having a constant frequency to the solution, letting the droplets fly through the gas atmosphere, and then letting the droplets fall into a coagulating liquid which is a non-solvent of the polymer of the polymer solution, is miscible with the solvent of the polymer solution, and has a surface tension enough to spontaneously wet the liquid droplets, the distance in the gas atmosphere between the orifice and the surface of the coagulation liquid giving the droplets in a spherical form at the collision with the coagulating liquid. Preferred embodiments of these uniform polymer particles are described in subclaims 2 to 10. According to a second aspect the present invention relates to a process for preparing uniform polymer particles having a narrow particle size distribution as described above which is characterized in that it comprises the following steps: jetting a polymer solution consisting of solvent and polymer, in the form of uniform liquid droplets with electric charges with the same sign from an orifice into a gas atmosphre at a constant flow rate while applying cyclic turbulences having a constant frequency to the solution, letting the droplets fly through the gas atmosphere, and then letting the droplets fall into a coagulating liquid which is a non-solvent of the polymer of the polymer solution, is miscible with the solvent of the polymer solution, and has a surface tension enough to spontaneously wet the liquid droplets, the distance in the gas atmosphere between the orifice and the surface of the coagulating liquid giving the droplets in a spherical form at the collision with the coagulating liquid. Preferred embodiments of the proces of the present invention are described in subclaims 12 to 20. According to a third aspect the present invention relates to an apparatus for forming uniform liquid droplets having a narrow particle size distribution as described above and for carrying out the above process comprising a cylinder (2) having a inlet of a liquid (9) and at least one orifice (12) through which the liquid is sent out, a vibration rod (6) and a vibration generator connected with the vibrating rod (6), characterised by means for electrically charging the formed liquid droplets, by a vibration rod (6) inserted in the cylinder (2) and by an O-ring (7) for sealing the clearance between the cylinder (2) and the vibrating rod (6). Preferred embodiment of the apparatus of the present invention are described in subclaims 22 to 29. According to a particularly preferred embodiment of the present invention there are provided uniform polymer particles in a spherical form which are suitable for use in a direct extracorporeal hemi-perfusion treatment having a volume average particle size of 80 to 400 µm, wherein not less than 80 % by volume of the whole particles have a particle size within the range of ±20 % of the volume average particle size, the content of particles having a particle size of less than 74 µm is not more than 5 % by volume, the content of particles having a particle size of less than 25 µm is not more than 0.1 % by volume, and said uniform polymer particles do not include particles having a particle size of not more than 5 % of the volume average particle size. Fig. 1 is a schematic sectional view showing an apparatus for forming uniform liquid droplets of the present invention. Fig. 2 is a sketch of the photograph of uniform liquid droplets obtained in Example 1. The meanings of some specific terms or mesuring process used in the present specification are explained below. The term "polymer particles in a spherical form" means polymer particles in the form of a spheroid, smooth on the surface, which are applicable to various uses. The term "uniform particles" means particles wherein not less than 80 % by volume of the whole particles have an particle size within the range of ±20 % of, preferably within the range of ±10 % of the volume average particle size. The term "volume average particle size" is the value obtained by classifying particles by means of wet sieve classification, in which water, an alcohol or the like is employed as a dispersion medium, using standard sieves under Japanese Industrial Standards, collecting particles captured in each sieve, measuring each total volume of particles sedimented after allowing them to stand for one day, and caluculating according to the following equation: volume average particle size = Σ DiVi Σ Vi wherein Di is the size of sieve opening, and Vi is each total volume of sedimented particles in particles captured in each sieve having the size of sieve opening of Di. The term "particles with a particle size of less than D µm" means particles pass through a sieve with the size of sieve opening of D µm. The term "particles with a particle size of not less than D µm" means particles do not pass through a sieve with the size of sieve opening of D µm. When not less than 80 % by volume of the whole particles have a particle size within the range of ±20 % of the volume average particle size, such polymer particles can be employed in various uses as they are without a classification process. Further, not less than 90 % by volume of the whole particles have a particle size within the range of ±20 % of the volume average particle size, such polymer particles have advantages not only a classification process is not needed but also, in using as parent material for an ion exchange resin or as a packing for a chromatography, they can be uniformly packed and the pressure drop is small. When uniform polymer particles have a volume average particle size of 10 to 1,000 µm, such uniform polymer particles can be generally used in the above-stated uses. When uniform polymer particles have a volume average particle size of 10 to 500 µm, such uniform polymer particles can be used as parent material for an ion exchange resin with a high ion exchange rate, as an adsorbent with a high adsorption rate and high selectivity, or as a packing for a chromatography for an industrial use. When uniform polymer particles have a volume average particle size of 20 to 250 µm, such uniform polymer particles can be used as an adsorbent or a packing for a chromatography for substances with a high molecular weight with sharp fractions in addition to the uses described above. However, uniform polymer particles having a volume average particle size of less than 10 µm are hard to produce. The presence of very small particles with a particle size of less than 5 µm, which contaminate a treating liquid or cause an increase in pressure drop was examined by a microscope or a Coulter Counter (commercially available under the trade name "Coulter Counter" made by Coulter Electronics Inc.) The term "three dimensional network structure" literally means a structure that fiber or porous sheet is three dimensionally connected with each other, in contrast to particles made by polymerizing polymerizable monomers having a structure that minute particles aggregate. The term "direct extracorporeal hemo-perfusion treatment" means that in an extracorporeal hemo-perfusion treatment, blood is treated by an adsorbent directly without separating the blood into blood cell and blood plasma. In order to obtain firm polymer particles which do not cause an occurrence of minute polymer chips, the polymer concentration of polymer solution, though it is determined depending on the molecular weight of polymer, should be not more than 5 % by weight. Such polymer solution is a solution of polymer with relatively high degree of polymerization, having a viscosity,though its viscosity depends on the temperature at which the measurement of viscosity is carried out, of not less than about 10 mPa·s (cP), preferrably not less than about 50 mPa·s (cP). When the solution has a viscosity of more than 2,000 mPa·s (cP) it is hard to form liquid droplets having a particle size of not more than 1,000 µm by a vibration method. Therefore, the viscosity of solution is preferably not more than 2,000 mPa·s (cP). As previously mentioned, in order to form uniform liquid droplets, the viscosity and surface tension of polymer solution, the flow rate of liquid, the size of orifice, and the frequency and displacement of cyclic turbulences, these parameters being mutually related, should be adjusted in a specific range (synchronized condition). When the diameter of liquid droplets to be formed is more than 1,000 µm, the synchronized condition can be also attained by directly vibrating the nozzle [cf. T. Sakai, Proc. ICLASS-1982 37 (1982)]. However, when the particle size of liquid droplets to be formed is small, the frequency to be synchronized is so high that an enomous energy is required to directly vibrate the nozzle. Therefore, in this case it is preferable to apply cyclic turbulences directly to the solution. Especially, when the diameter of liquid droplets to be formed is not more than 250 µm, the frequency to be synchronized reaches 3,000 to 40,000 Hz. In Fig. 1, the cylinder (2) is fixed on the fixing cylinder (1). The nat (4) is tightened up to ensure the fixation between the cylinder (2) and the fixing cylinder (1). The cylinder (2) has an inlet of a liquid and orifices (12). The cylinder (2) is further equipped with the O-ring (7) on the position where the vibrating rod (6) slides, for sealing the clearance between the cylinder (2) and the vibrating rod (6). With the vibrating rod (6) was connected a vibration transmission part (15) in order to transmit vibration generated by a vibration generator (not shown in Fig. 1), for instance, a magnetostrictive vibrator, an electrostrictive vibrator or a electromagnetic coil vibrator to the vibrating rod (6). When a magnetostrictive vibrator or an electrostrictive vibrator is employed as a vibration generator, the vibrator, the vibration transmission part (15) and the vibrating rod (6) are organized so as to form a resonator. When an electromagnetic coil vibrator is employed as a vibration generator, the vibrating rod (6) is directly connected with a vibrator of the vibration generator. In the latter case in order to reduce the weight of the vibrating rod (6), it is preferred that the vibrating rod (6) is thin other than the end (16) of vibrating rod (6) which is thick as shown in Fig. 1. In order to efficiently thansmit the vibrational energy to the vibrating rod (6), it is preferable to employ the O-ring (7) having a small contact resistance for sealing the clearance between the cylinder (2) and the vibrating rod (6). The distance between the nozzle (5) having orifices (12) and the end (16) of vibrating rod (6) can be suitably controlled by a screw (11) of the cylinder (2) and a nat (4) for fixing the cylinder. The nozzle (5) is fixed to an end of the cylinder (2) by a nat (3) for fixing the nozzle (5). The clearance between the nozzle (5) and the cylinder (2) is sealed by the O-ring (8). The liquid solution by a gear pump is introduced into the cylinder (2) through an inlet of a liquid (9) and is jetted from the orifices (12) while applying a cyclic pressure change to the liquid by reciprocating motion of the vibrating rod (6) over the nozzle (5). If necessary, a polymer solution in the cylinder (2) can be heated by a heater (13). The temperature sensor (14) is therefore also used for managing the temperature. Fig. 1 shows a apparatus with a magnetostrictive vibrator as a vibrating generator. The magnetostrictive vibrator is used for the purpose of generating vibration particularly with a high frequency, for instance, supersonic vibration with a frequency of about 20,000 to 40,000 Hz. When the apparatus for forming liquid droplets of the present invention is used and the above-mentioned vibration with a high frequency is applied, uniform liquid droplets with a small particle size are obtained. Herein, the term "uniform liquid droplets" means that the droplets are produced under the synchronized condition, in other words, that the droplets are produced periodically with the same frequency with the vibrating rod (6). The frequency of vibration is preferably 1,000 to 40,000 Hz, more preferably 3,000 to 40,000 Hz. When the frequency is less than 1,000 Hz, it is difficult to form uniform liquid droplets. When the frequency is more than 40,000 Hz, the distance between formed liquid droplets becomes too small and the reconnection frequency of liquid droplets becomes high, and consequently it becomes hard to form uniform liquid droplets. The clearance between the vibrating rod (6) and the cylinder (2) is sealed by the O-ring (7) on a site so-called node, which is well known by a person skilled in the art, where the displacement is zero, and the friction caused by a slide of the vibrating rod (6) on the O-ring (7) can be almost neglected. The distance between the end (16) of the vibrating rod (6) and the nozzle (5) is preferably 2 to 20 mm, more preferably 5 to 15 mm. In case such distance is less than 2 mm, when the frequency is as high as that of supersonic waves, a cavitation occurs and there arises a possibility of an erosion of the end (16) of vibrating rod (6) or the inside of the nozzle (5). In case such distance is more than 20 mm, the turbulences given by the vibrating rod (16) are attenuated before the turbulences reach the inside of nozzle (5), the turbulences are not transmitted to the liquid jetted from the orifice (12), and it becomes difficult to form uniform liquid droplets. The nozzle (5) preferably has one or more than one orifices, and each orifice is preferably a round shape orifice having an aperture of not more than 500 µm, more preferably 10 to 250 µm, still more preferably 20 to 100 µm. When the orifice (12) have an aperture diameter of more than 500 µm, uniform liquid droplets having a diameter of not more than 1,000 µm, cannot be always obtained. As the shape of the orifice (12), there can be exemplified round shape, slit shape, rectangle, multiple tubular shape, and the like. Among them, round shape is preferable since spherical liquid droplets usable in many uses can be obtained. If necessary, the apparatus may be equipped with a heater (13) so that a liquid in the cylinder (2) can be heated. The temperature sensor (14) may be used for managing the temperature of heated liquid. Particularly, when it is necessary to keep the liquid a high temperature, the vibration transmission part (15) should be cooled so that the synchronized condition is maintained. The inlet/outlet of cool water (10) is used for that purpose. When the liquid in the cylinder (2) is heated by the heater (13) in the present invention, it is preferable to cool the vibration transmission part (15) and a part of the vibrating rod (16) from the joint with the vibration transmission part (15) to the position contacting the O-ring (7) by, for instance, letting cool water flow there. The process of forming very small liquid droplets from a high temperature, high pressure, and high viscosity liquid by the apparatus of the present invention is explained below. A liquid sent from a gear pump at a constant flow rate is put into the cylinder (2) from the inlet of the liquid (9) and jetted from orifices (12) while applying a cyclic pressure change to the liquid by the vibrating rod (6). As described above, as the size of orifice (12) becomes small, the synchronized flow rate of the liquid and frequency of the vibration become high and consequently the pressure applied to the liquid becomes high. The apparatus of the present invention have a pressure resistance of not less than several MPa (tens atm) as is presumed from the structure thereof. As the viscosity of the liquid becomes high, the turbulences, i.e. the pressure change applied to the liquid at the orifice (12) by the vibrating rod (6) becomes large. The turbulences and the pressure change can be controlled by adjusting the distance between the nozzle (5) and the end (16) of the vibrating rod (6). However, when the viscosity is more than about 2,000 mPa·s (cP), in case using an orifice having an aperture diameter of not more than 100 µm, uniform liquid droplets cannot be formed even if a large pressure change is applied. In order that the particles, which are obtained by forming uniform liquid droplets, and coagulating the droplets by contacting them with a coagulating liquid, have a mechanical strength enough for using them in the above-stated uses, the concentration of polymer in the polymer solution should be at least about 5 % by weight. Such solution has a viscosity at least about 10 cP, though the viscosity depends on the temperature. Therefore, in using the apparatus of the present invention, a liquid with a viscosity of 10 to 2,000 mPa·s (cP), preferably 50 to 2,000 mPa·s (cP) is mainly employed. Even if the liquid has such high viscosity, uniform liquid droplets can be formed, when the diameter of liquid droplets is more than about 1,000 µm, by a conventional apparatus in which an orifice is directly vibrated. However, when the diameter of liquid droplets is not more than 250 µm, the frequency of turbulences to be synchronized is not less than about 3,000 Hz. And since, as described above, an enomous energy is requied in order to directly vibrate the orifice, it is economical to apply the turbulences to the liquid directly as the apparatus of the present invention. It is possible to confirm whether the diameter of the liquid droplets is uniform or not in an usual manner. That is to say, in case uniform liquid droplets are formed, liquid droplets ranging at regular intervals can be seen by observing the droplets with a magnifying glass or taking a photograph of the droplets while the flashing cycle of the stroboscope is synchronized with the liquid droplets generation cycle. The uniform liquid droplets formed move at random by air resistance with going away from the nozzle (5), and many liquid droplets collide and reconnect each other. As reported by J. M. Schneider et al, the reconnection of the liquid droplets can be prevented for a arelatively long time by electrifying each of the liquid droplets with electric charges with a same sign [cf. Rev. Sci, Instr. 35 ,1349 (1964)]. In the process of the present invention, the liquid droplets thus jetted into a gas atmosphere at a constant flow rate are let into a coaguating liquid which is a non-solvent of the polymer of the polymer solution, is miscible with the solvent of the polymer solution, and has a surface tension enough to spontaneously wet the liquid droplets, after the droplets let fly such a distance that the flying rate of droplets are lowered as low as the droplets are not greatly deformed by the collision with the coagulating liquid. When the surface tension of coagulating liquid is more than that of the solvent of polymer solution and therefore the liquid droplets are not spontaneously wetted, the droplets float on the surface of the coagulating liquid for a long time even if the specific gravily of the liquid droplets is more than that of coagulating liquid, and droplets later reached the surface collide with the floating droplets to form a large reconnected droplets. On the other hand, when the droplets reached the surface of coagulating liquid are wetted with the coagulating liquid, since the reconnection of droplets does not occur even if the droplets collide with the droplets later reached the surface, and the droplets later reached the surface are also wetted with the coagulating liquid, each droplet becomes a separate polymer particle. The coagulating liquid is selected from ones having a surface tension approximate to that of the solvent of the polymer solution or preferably ones having a surface tension of less than that of the solvent of the polymer solution. As disclosed in a preceding patent application by the present inventors [Japanese Unexamined Patent Publication (Tokkyo Kokai) No. 191033/1987], when the viscosity of the polymer solution is high and the diameter of the liquid droplets is small, since the jetting rate of the polymer solution jetted from the orifice, i.e. the initial flying rate of the liquid droplets, reaches several m/sec to decades m/sec, if these droplets are immediately let into the coagulating liquid, the droplets are broken or deformed to be a flat shape by an impact of the collision. In order to avoid such break or deformation, the jetted droplets should be let into the coagulating liquid after reducing flying rate of the droplets. As described above, the reconnection of the liquid droplets can be prevented for a relatively long time by electrifying each of the liquid droplets with a single sign. In addition, the present inventors have found that the flying rate of the jetted liquid droplets is rapidly decreased by electrifying each of the liquid droplets with a single sign. Particularly, when the diameter of the liquid droplets is small, the synchronized initial flying rate is high, and therefore the liquid droplets without electric charges are sometimes deformed to be a flat shape even if letting the droplets fly a distance of 2 m. However, in case such liquid droplets have elecric charges with a same sign, they enter the coagulating liquid without deformation even if letting the droplets fly a distance of 30 cm. It is important to minimize the distance between the orifice and the surface of the coagulating liquid in preventing the reconnection of the liquid droplets. Therefore, the distance between the orifice and the surface of the coagulating liquid should be minimized as far as the droplets are not deformed in such extent that the droplets become not spheroidal. When the liquid droplets have electric charges with a same sign, liquid droplets are scattered from each other because of their mutual repulsion. These droplets are attracted to a matter having the opposite electric charge or a conductors grounded. That is to say, the droplets flown off tend to be attracted to the wall of container for coagulating liquid or the electrodes for providing electric charges. The droplets attracted to such matters cause some obstraction, for instance, ununiform particles are formed, the electric field strength are reduced, or the like. However, the whole liquid droplets can be attracted into the coagulating liquid by using an electric conductive coagulating liquid in a metallic container, and grounding the metallic container. The porosity of the particles is controlled by various methods usually employed in dry-wet spinning processes. It is known that the pore size of pores on the surface of particles prepared by the dry-wet spinning process have a high uniformity whether they have a skin layer or not. Generally, when liquid droplets are coagulated by a coagulating liquid with a high coagulating activity, porous particles with a thin fine surface layer, so-called non-porous skin layer, are obtained. On the contrary, when a coagulating liquid having a low coagulating activity is employed, the particles have a skin layer with a porous structure. When a coagulating agent having a still lower activity is employed, the particles do not have a skin layer and the surface of particles also have a network structure. Through a skin layer, substances having a size of not more than a certain size pass, but substances having a size of more than the certain size do not pass. By controlling the pore size of the skin layer, the molecular weight of substance which pass through, which corresponds to the above-stated certain size, can be varied from decades to hundreds of thousand. Therefore, an adsorbent showing an excellent selectivity to a substance having such molecular weight can be obtained by employing particles with a skin layer. Conventional polymer particles prepared by polymerizing liquid droplets of polymerizable monomers do not have such advantage. Particles which do not have a skin layer and have a network structure over the particle have an excellent selectivity to a substance having a molecular weight of more than the aforementioned, for instance, to a substance having a molecular weight of several millions. Also, even if the particles have such porous structure, minute polymer chips do not occur since the polymer in the particle have a three dimensional network structure formed by fiber or porous sheet. Generally, the size of mesh of the three dimensional network structure decreases as the concentration of a polymer in the polymer solution increases. The porosity of the particles can be also controlled by adding a bad solvent of the polymer to the polymer solution or by adding an additives which can be easily removed by extraction, for instance, a water-soluble polymer such as polyethylene glycol, polyvinyl pirrolidone or dextran to the polymer solution in an amount such that the viscosity of the polymer solution is a viscosity in the range of constituting a synchronized condition, that is, according to the experience of the present inventors, the range of not more than 2,000 mPa·s (cP). A porous particulate polymer in a spherical form of the present invention, is thus obtained. In order to improve the characteristics of the polymers according to their uses, various post-treatment may be conducted. Particularly, heat-treatment in a non-solvent is effective to stabilize the particle structure. In the process of present invention, any polymers being dissoluble in the solvent can be used. Examples of the polymers which are especially useful in the invention are mentioned below. A polystyrene is useful as a packing material used for chromatography, which does not have defects such that when using, a large pressure drop is caused or minute particles contaminate the liquid to be treated, and as an adsorbent causing only a small pressure drop and no occurrance of minute polymer chips, and having excellent selectivity. A polymer which is available for crosslinking and introduction of an ion exchange group, such as a styrene-butadiene copolymer or a styrene-chloromethylated styrene copolymer, is suitably used as a parent material for an ion exchange resin which causes only a small pressure drop, high ion exchange rate and no generation of minute polymer chips. A polyvinyl alcohol or ethylene-vinyl alcohol copolymer is useful in affinity chromatography as a carrier having an active hydroxyl group, having excellent selectivety, and causing only a small pressure drop. Also, various kinds of natural high molecular substances such as cellulose, silk, collagen, and their derivatives are useful as a carrier for chromatography as they are, or as a carrier for affinity chromatography. Further, many other vinyl polymers and condensation polymers can be used for the above-mentioned uses. The solvents of these polymer solutions are found in manuals, e.g. J. Brandrup, "Polymer Handbook 2nd edition", John Wiley and Sons, Inc. (1975), and the like. However, as mentioned later, the preferable coagulating liquid in the invention is an aqueous solution, therefore, a water-miscible solvent is desirable in order that it is miscible with the coagulating liquid. Examples of the solvent which is used in a number of polymer solutions are, for instance, N-methyl-2-pyrrolidone, dimethylformamide, dimethylacetoamide, dimethyl sulfoxide, diacetone alcohol, acetone, tetrahydrofuran, dioxane, and the like. Also, it is possible to use these solvents as an admixture, or mixed solvents of the above solvents with other solvents such as ethanol, methanol, ethylene glycol, propylene glycol and glycerol. Further, there can be added a water soluble polymer such as polyethylene glycol or polyvinyl pyrrolidone as an additive for the purpose of controlling the porosity of the particles, which can be extracted. For example, as a solvent for cellulose, a known solvent, e.g. a mixed solvent of dimethyl sulfoxide and formaldehyde, cuprammonium solution, an aqueous solution of calcium thiocyanate can be used. Generally, the solvents are suitably selected depending on the kinds of the polymers. As mentioned above, it is desirable that the surface tension of the coagulating liquid is approximate to or less than that of the solvent of the polymer solution, and that the coagulating liquid is electric conductive. As the coagulating liquid, water with a surface active agent, an aqueous solution of alcohol and an aqueous solution of the above-mentioned solvent or a mixture thereof are particularly preferable so as to control the fine structure of the obtained polymer particles. Uniform polymer particles in a spherical form suitable for use in the direct extracorporeal hemo-perfusion treatment of the present invention is described hereinafter. The blood compatibility is judged according to the following method. A column having an inner diameter of 7 mm and a length of 100 mm is prepared and filters made of polyester, of which opening diameter is 20 µm, are fixed at both ends of the column in order to prevent the particles from leaking out. Then, the particles are dispersed in water of a volume of five times as much as the volume of the sedimented particles, and the particles are packed into the column by transmitting the dispersion into the column at a rate of 5 mℓ/min as observing so that bubbles of gas are not mixed. The average linear velocity is determined at 1.3 cm/min in consideration that blood is circulated at the flow rate of at least 50mℓ/min in actual treatment system and a column used in practice has a sectional area of about a hundred times of that of the column used in this examination. Bovine blood maintained at the temperature of 37°C is passed through the column at the above-mentioned average linear velocity. After an hour, the difference between the pressure at the inlet and the pressure at the outlet of the column, i.e. the pressure drop is measured, and it is confirmed whether hemolysis occurs or not to judge the blood compatibility. That is, when no hemolysis occurrs and the pressure drop is not more than 100 mmHg, the blood compatibility is judged good. The judgement whether hemolysis occurred or not is conducted by means that the blood run out of the column is subjected to the centrifugation, it is decided that hemolysis occurred when the plasma is extremely colored and hemolysis did not occur when the plasma is not colored. As materials of the particles, cellulose acetate and cellulose are employed for convenience sake since there are a lot of points not explicated in the relation between the blood compatibility and the chemical properties of the particles as mentioned above, and therefore, the materials cannot be defined. Generally available particles, e.g. particles used for chromatography have a broad particle size distribution. By repeating classification, it becomes possible to obtain the particles having a narrow particle size distribution from them. Nevertheless, the yield is low in this case, accordingly, the method is not practical. Therefore, as described later the uniform particles of cellulose acetate are prepared according to the process of the present invention and the particles are compared with the commercially available cellulose particles used for chromatography on the blood compatibility. Herein, when the uniform particles are densely packed into the column, the particle size of the substances which can be passed through between the particles in the column is about 15 % of the particle size of the uniform particles. That is, when the particles having the particle size of about 70 µm are packed into the column, there arises a fear that erythrocyte sticks between the particles. If the volume average particle size is less than 80 µm, the pressure drop becomes too large. Accordingly, it is required that the particles have the volume average particle size of 80 to 400 µm, preferably 80 to 300 µm. When the volume average particle size is less than 80 µm, erythrocyte sticks between particles and the pressure drop is over 100 mmHg, also when the volume average particle size is more than 400 µm, the ability of adsorbing pathogenic substances having a high molecular weight is small, both of which are unpreferable. Further, it is necessary that not less than 80 % by volume of the whole particles have a particle size within the range of ±20 % of the volume average particle size. It is not preferable that the particles have a particle size distribution broader than the above-mentioned, i.e. not less than 80 % by volume of the whole particles do not have a particle size within the range of ±20 % of the volume average particle size in such case, the increase of the pressure drop or the hemolysis occurs when many particles have a particle size of less than -20 % of the volume average particles, or the ability of adsorption is lowered when many particles have a particle size of more than +20 % of the volume average particles. Still more, even though the volume average particle size is not less than 80 µm, the content of the particles having a particle size of less than 74 µm should be limited to not more than 5 % by volume of the whole particles. When the content of them is more than 5 % by volume, the pressure drop is over 13,33 kPa (100 mmHg), which is unpreferable. When a direct extracorporeal hemo-perfusion treatment is carried out, minute particles must not flow into the blood. For the above reason, a filter with openings as small as possible is attached to the outlet for the blood of a column packed with particles. However, it is also desired that the opening diameter of the filter is at least 20 µm so as not to injure erythrocyte which is nearly 10 µm in diameter. Therefore, the content of the particles having a particle size of less than 25 µm must be not more than 0.1 % by volume of the whole particles. When the column is packed with the particles containing more than 0.1 % by volume of the particles of which particle size is less than 25 µm, the opening of the filter is clogged. However, according to the process of the present invention, it can be obtained the uniform polymer particles in a spherical form containing only few particles having a particle size of less than 25 µm, further, it is possible to prepare the uniform polymer not containing the minute particles of the above size at all. The particles of the present invention, as a matter of cource, have a strength so as not to be deformed with the pressure drop of at least 100 mmHg, which is confirmed from a result that the relation of the pressure drop and the flow rate, when passing water through the column packed with the particles, keeps a linear relationship until the pressure drop is increased to 13,33 kPa (100 mmHg). The adsorbent use of the uniform polymer particles of the present invention, having the above-mentioned physical properties makes it possible to promptly remove pathogenic substances having a high molecular weight by a direct extracorporeal hemo-perfusion treatment, which is of great value. The present invention is more specifically described and explained by means of the following Examples in which all percents ant parts are by weight unless otherwise noted. Example 1 Cellulose acetate (degree of acetylation: 55 %) was dissolved in a mixture of N-methyl-2-pyrrolidone and propylene glycol mixed at a weight ratio of 4 : 6 to prepare a polymer solution having a cellulose acetate concentration of 5 %. The polymer solution had a viscosity of 78 mPa·s (cP) at 90°C. The surface tension of the mixed solvent was 38·10 -5 N/cm (38 dyn/cm), which is the arithmetical mean value of the surface tension of the solvent at 25°C. By using the apparatus shown in Fig. 1, the polymer solution was jetted through the nozzle (5) having the orifice (12) of two having a diameter of 50 µm, aligned at an interval of 5 mm. At that time, the parameters were adjusted to attain the synchronized condition, i.e. the distance between the end (16) of the vibrating rod (6) and the nozzle (5) was 15 mm, the temperature of the polymer solution was maintained at 90°C, the frequency of the vibrating rod (6) connected with the magnetostrictive vibrator was 25 KHz and the flow rate of the jetted liquid was 18 m/s, to give uniform liquid droplets. At the position of about 2 mm from the lower face of the nozzle (5), parallel-plate electrodes having a width of 20 mm and a distance between the plates of 10 mm was set parallel to the orifices (12), and a voltage of 500 V was given to the droplets between the cylinder and the parallel-plate electrodes. The cylinder was grounded. A coagulating liquid was put into a grounded cylindrical container made of stainless steel having a diameter of about 40 cm, and the container was put right under the nozzle (5) so as to make the distance between the nozzle and the surface of the coagulating liquid 40 cm. As the coagulating liquid, a 40 % ethanol aqueous solution under room temperature was employed. The surface tension of the coagulating liquid was 32·10 -5 N/cm (32 dyn/cm) at 25°C. The obtained particles were perfectly spherical, and from which any minute polymer chips did not occur even though the particles were stirred with a magnetic stirrer for about 3 hours. The above particles were suspended in water and classified by passing through wet sieves of which opening size were 44 µm, 63 µm, 74 µm, 88 µm, 105 µm, 125 µm and 149 µm, respectively. Particles which gathered on each sieve were suspended in water and the volume of sedimented particles was measured after allowing them to stand for a day. The volume average particle size of the obtained particles was 111 µm and not less than 97 % by volume of the whole particles had a particle size within the range of ±20 % of the volume average particle size. There could not be found a particle with a particle size of less than 44 µm. Further, particle with a particle size of not more than 5 % of the volume average particle size or with a particle size of less than 5 µm was not recognized by using COULTER COUNTER® (made by COULTER ELECTRONICS, INC.) Example 2 The particles obtained in Example 1 were fully washed with methanol and dried under vacuum at room temperature. After vapor deposition of gold on them, the surface and section of the particles were observed with a scanning electron microscope. It was observed that the particles had no skin layer and had a lot of pores of about 0.5 µm on the surface, also on the section, had pores which were nearly as large as and as many as those on the surface, which showed that a three dimensional network structure was extended all over the particle. Example 3 Cellulose acetate (degree of acetylation: 61.5 %) was dissolved in a mixture of dimethyl sulfoxide and propylene glycol mixed at a weight ratio of 6 : 4 to prepare a polymer solution having a concentration of 5 %. Then, uniform polymer particles were obtained in the same manner as in Example 1 except that a 0.2 % aqueous solution of a detergent for home use (commercially available under the trade name "Runa Mild" made by Kao Corporation) was used as the coagulating liquid. The viscosity of the polymer solution was 52 cP at 90°C. The surface tension of the mixture solvent of the polymer solution was 39·10 -5 N/cm (39 dyn/cm), which is the arithmetical mean values of the surface tension of the solvents at 25°C. The surface tension of the coagulating liquid was 20·10 -5 N/cm (20 dyn/cm) at 25°C. The particles was heated at 120°C for 30 minutes with immersing the particles in water. By means of this treatment, the particles were uniformly shrinked about 20 % in diameter. The obtained particles were perfectly spherical, and from which any minute polymer chips did not occur even though the particles were stirred with the magnetic stirrer for about 3 hours. The surface and section of the particles were observed with the scanning electron microscope in the same manner as in Example 2. There was skin layer having a thickness of about 0.1 µm on the surface of the particle, on which no pore was observed even though the observation was carried out at a magnification of 20,000 X. Except the surface, the three dimensional network structure was observed. The classification was carried out with wet sieves in the same manner as in Example 1. As a result of the measurement of the particle size distribution, the obtained particles had the volume average particle size of 103 µm and not less than 97 % by volume of the whole particles had a particle size within the range of ±20 % of the volume average particle size. There could not be found a particle having a particle size of less than 44 µm. Example 4 Polystyrene was dissolved in N-methyl-2-pyrrolidone to prepare a polymer solution having a concentration of 15 %. The polymer solution had a viscosity of 250 cP at 90°C and a surface tension of the solvent of the solution 41·10 -5 N/cm (41 dyn/cm) at 25°C. Uniform polymer particles was obtained from the above solution in the same manner as in Example 3. The obtained particles were perfectly spherical, and from which any minute polymer chips did not occur even though the particles were stirred with the magnetic stirrer for about 3 hours. The classification was carried out with wet sieves in the same manner as in Example 1. As a result of the measurement of the particle size distribution, the obtained particles had a volume average particle size of 116 µm and not less than 97 % by volume of the whole particles had a particle size within the range of ±20 % of the volume average particle size. Particles with the particle size of less than 44 µm could not be found. Example 5 Cellulose was dissolved in a 60 % aqueous solution of calcium thiocyanate to prepare a polymer solution having a cellulose concentration of 4 %. The solution had a viscosity of 550 cP at 100°C and a surface tension of the solvent of the solution 73·10 -5 N/cm (73 dyn/cm) at 25°C. By using the above solution, uniform polymer particles were obtained in the same manner as in Example 1 except that a 50 % ethanol solution was used as the coagulating liquid, and, the apparatus shown in Fig. 1 was set so that the distance between the end (16) of the vibrating rod (6) and the nozzle (5) was 5 mm and the temperature of the polymer solution was 100°C. The surface tension of the coagulating liquid was 30·10 -5 N/cm (30 dyn/cm) at 25°C. The obtained particles were perfectly spherical and from which any minute polymer chips did not occur even though the particles were stirred with the magnetic stirrer for about 3 hours. The classification was carried out with wet sieves in the same manner as in Example 1. As a result of the measurement of the particle size distribution, the obtained particles had the volume average particle size of 112 µm and not less than 97 % by volume of the whole particles had a particle size within the range of ±20 % of the volume average particle size. There could not be found a particle having a particle size of less than 44 µm. In Exmaples 1 to 5, there was used the nozzle which had the orifice (12) with a aperture diameter of 50 µm. However, by changing the aperture diameter and adjusting the parameters to attain the synchronized condition for giving uniform liquid droplets, droplets having a diameter of not more than 1,000 µm, not more than 500 µm or not more than 250 µm, respectively, and having a narrow particle size distribution can be suitably obtained in compliance with the uses of the polymer particles. Example 6 Cellulose acetate (degree of acetylation: 61.5 %) was dissolved in N-methyl-2-pyrrolidone to prepare a polymer solution having a cellulose acetate concentration of 7 %. The solution had a viscosity of 350 mPa·s (cP) at 64°C and a surface tension of the solvent of the solution 41·10 -5 N/cm (41 dyn/cm) at 25°C. By using the apparatus shown in Fig. 1, the polymer solution was jetted through the orifice (12) having a round shape with a diameter of 50 µm at a flow rate of 2500 cm/s. In order to obtain uniform liquid droplets, each parameter was adjusted to attain the synchronized condition, i.e. the distance between the end (16) of the vibrating rod (6) and the nozzle (5) was 15 mm, the temperature of the polymer solution was maintained at 64°C, the frequency of the vibrating rod (6) which was connected with the magnetostrictive vibrator (which was not shown in Fig. 1) via the vibration transmission part (15) were 25 KHz and the amplitude of vibration of the top (16) of the vibrating rod was 5 µm. When the pressure of the polymer solution in the cylinder (2) was 1,56 MPa (15.9 Kg/cm 2 ), uniform liquid droplets were stably formed. It was confirmed that the uniform liquid droplets were formed actually by taking a photograph of the droplets at the position of 5 cm downward from the nozzle with turning on and off a stroboscope ("MSX-1A" type, made by Kabushiki Kaisha Sugawara Kenkyusho). As shown in Fig. 2 which is a sketch of the photograph, it was observed that the droplets (17) having a uniform diameter of about 155 µm were in a line at regular intervals. Example 7 Cellulose acetate (degree of acetylation: 55 %) was dissolved in dimethyl sulfoxide to prepare a polymer solution having a cellulose acetate concentration of 16 %. The solution had a viscosity of 380 mPa·s (cP) at 130°C and a surface tension of the solvent of the solution 43·10 -5 N/cm (43 dyn/cm) at 25°C. By using the apparatus shown in Fig. 1, the polymer solution was jetted from the orifice (12) having a round shape with a diameter of 50 µm at a flow rate of 2,800 cm/s. Uniform liquid droplets having a diameter of about 115 µm were obtained stably when the parameters were adjusted to attain the synchronized condition, i.e. the distance between the end (16) of the vibrating rod (6) and the nozzle (5) was 5 mm, the temperature of the polymer solution was maintained at 130°C, the frequency of the vibrating rod (6) was 25 KHz and the amplitude of vibration of the top (16) of the vibrating rod was 5 µm. At that time, the pressure of the polymer solution in the cylinder (2) was 1,59 MPa (16.2 Kg/cm 2 ). Example 8 Polystyrene was dissolved in N-methyl-2-pyrrolidone to prepare a polymer solution having a polystyrene concentration of 15 %. The viscosity of the solution was 250 mPa·s (cP) at 90°C. By using the apparatus shown in Fig. 1, the polymer solution was jetted from the round shape orifice (12) with an aperture diameter of 35 µm at a flow rate of 2000 cm/s. The parameters were adjusted to attain the synchronized condition, i.e. the distance between the end (16) of the vibrating rod (6) and the nozzle (5) was 15 mm, the temperature of the polymer solution was maintained at 90°C, the frequency of the vibrating rod (6) was 25 KHz and the amplitude of vibration of the end (16) of the vibrating rod was about 5 µm. The pressure of the polymer solution in the cylinder (2) was 2,85 MPa (29 Kg/cm 2 ) at that time, and uniform liquid droplets having a diameter of about 115 µm were obtained stably. From the above-mentioned results, it is recognized that minute uniform liquid droplets can be obtained from a liquid having a high temperature, a high pressure and a high viscosity by using the apparatus of the present invention, which is impossible with an apparatus conventionally used. Example 9 Cellulose acetate (degree of acetylation: 61.5 %) was dissolved in a mixture of dimethyl sulfoxide and propylene glycol mixed in a weight ratio of 6 : 4 to prepare a polymer solution having a cellulose acetate concentration of 5 %. The solution was heated to 90°C and jetted through a nozzle with a orifice having an aperture diameter of 50 µm at a flow rate of 18 m/sec, while applying turbulences with a constant frequency of 25 KHz to give uniform liquid droplets. In order to give electric charge to the liquid droplets, parallel-plate electrodes having a width of 20 mm and a distance between the plates of 10 mm was set at the position of about 2 mm from the lower face of the nozzle and a voltage of 500 V was given to the droplets between the nozzle and the electrodes. A grounded container made of stainless steel in which a 40 % ethanol solution was contained was set about 50 cm right under the nozzle. When the minute droplets with electric charge, uniformly jetted one by one were letted into the aqueous solution of ethanol, they were coagulated to be spherical particles. The obtained particles were washed with water and heated at 120°C for 30 minutes with immersing them in water. The particles were suspended in water and classified by using wet sieves having the size of sieve opening 44 µm, 63 µm, 74 µm, 83 µm, 105 µm, 125 µm and 149 µm, respectively. The effluent solution which was passed through the sieve of 44 µm and each particle caught on each sieve was suspended in water. After allowing to stand them for a day, the volume of sedimented particles was measured and the volume average particle size and the particle size distribution were calculated. The volume average particle size was 100 µm, the content of particles having a particle size of less than 74 µm was not more than 1 % by volume, and particles with the particle size of less than 44 µm were not recognized. Further, not less than 97 % by volume of the whole particles had a particle size within the range of ±20 % of the volume average particle size. The particles were suspended in water of a volume of about five times as much as the volume of sedimented particles and the suspension was passed through a column with a inner diameter of 7 mm and a length of 100 mm, equipped with a filter made of polyester, of which opening diameter was 20 µm, at the outlet of it at a flow rate of 5 mℓ/min to pack the particles in the column. When the column was filled with the particles, it was stopped to transmit the suspension and the inlet of the column was also covered with a cap attached with a filter of which opening diameter was 20 µm. Bovine blood containing 1 part by volume of 3.1 % tris buffer solution of sodium citrate as an anticoagulant, based on 9 parts by volume of blood was maintained at the temperature of 37°C, and the blood was sent into the above-mentioned column at a flow rate of 0.5 mℓ/ min. Though the pressure drop was gradually risen with the passage of time, it was 85 mmHg after 1 hour had passed. Also, there occurred no hemolysis. Comparative Example 1 The procedure of Example 1 was repeated except that commercially available hard cellulose particles used in chromatography were classified with sieves of which opening size were 25 µm, 44 µm, 63 µm, 74 µm, 88 µm, 105 µm, 125 µm and 149 µm, respectively. The content of the particles having particle size of less than 25 µm was 0.3 % by volume and the content of the particles having particle size of less than 74 µm was 7.7 % by volume. The volume average particle size of the particles was 95 µm and at most 66 % by volume of the whole particles had a particle size within the range of ±20 % of the volume average particle size. A column was made with the above particles and bovine blood was passed through the column in the same manner as in Example 9. Since the pressure drop reached 172 mmHg after 30 minutes, the hemo-perfusion was stopped. It was confirmed that hemolysis occurred in effluent blood from the column. From the results mentioned above, it was confirmed that when the direct extracorporeal hemo-perfusion was conducted by employing the particles of the present invention, the pressure drop was not increased to more than 100 mmHg even after 1 hour of operation, which showed the particles of the present invention were excellent in blood compatibility. In addition to the ingredients used in the Examples, other ingredients can be used in the Examples as set forth in the specification to obtain substantially the same results.

Claims: Uniform polymer particles which have a volume average particle size of 10 to 1000 µm, which include particles having a particle size of more than 5 µm, wherein each particle has a spherical form and a three dimensional network structure, wherein at least 80 % by volume of the whole particles have a particle size within the range of ± 20 % of the volume average particle size, and wherein the remaining particles have a particle size of more than 5 % of the volume average particle size, obtained by the following steps: jetting a polymer solution consisting of solvent and polymer in the form of uniform liquid droplets with electric charges with the same sign from an orifice into a gas atmosphere at a constant flow rate while applying cyclic turbulences having a constant frequency to the solution, letting the droplets fly through the gas atmosphere, and then letting the droplets fall into a coagulating liquid which is a non-solvent of the polymer of the polymer solution, is miscible with the solvent of the polymer solution, and has a surface tension enough to spontaneously wet the liquid droplets, the distance in the gas atmosphere between the orifice and the surface of the coagulation liquid giving the droplets in a spherical form at the collision with the coagulating liquid. The uniform polymer particles of claim 1, wherein each particle has a skin layer on the surface thereof. The uniform polymer particles of claim 1, wherein each particle does not have a skin layer on the surface thereof. The uniform polymer particles of any of claims 1 to 3, wherein at least 90 % by volume of the whole particles have a particle size within the range of ± 20 % of the volume average particle size, The uniform polymer particles of any of claims 1 to 4, which have a volume average particle size of 10 to 500 µm. The uniform polymer particles of claim 5, which have a volume average particle size of 20 to 250 µm. The uniform polymer particles of any of claims 1 to 6, suitable for use in a direct extracorporeal hemoperfusion treatment having a volume average particle size of 80 to 400 µm, the content of particles having a particle size of less than 74 µm is at most 5 % by volume, the content of particles having a particle size of less than 25 µm is at most 0,1 % by volume, and the remaining uniform polymer particles are particles having a particle size of more than 5 % of the volume average particle size. The uniform polymer particles of claim 7, which have a volume average particle size of 80 to 300 µm. A process for preparing uniform polymer particles having a narrow particle size distribution according to any of claims 1 to 8, characterized in that it comprises the following steps: jetting a polymer solution consisting of solvent and polymer in the form of uniform liquid droplets with electric charges with the same sign from an orifice into a gas atmosphere at a constant flow rate while applying cyclic turbulences having a constant frequency to the solution, letting the droplets fly through the gas atmosphere, and then letting the droplets fall into a coagulating liquid which is a non-solvent of the polymer of the polymer solution, is miscible with the solvent of the polymer solution, and has a surface tension enough to spontaneously wet the liquid droplets, the distance in the gas atmosphere between the orifice and the surface of the coagulating liquid giving the droplets in a spherical form at the collision with the coagulating liquid. The process of claim 9, wherein said polymer solution has a viscosity of 10 to 2000 mPa·s. The process of claim 9 or 10, wherein said turbulences have a frequency of 1000 to 40000 Hz. The process of claim 11, wherein said turbulences have a frequency of 3000 to 40000 Hz. The process of any of claims 9 to 12, wherein the solvent of said polymer solution is miscible with water. The process of any of claims 9 to 13, wherein said liquid droplets have a diameter of at most 1000 µm. The process of claim 14, wherein said liquid droplets have a diameter of at most 250 µm. The process of any of claims 9 to 15, where said coagulating liquid has a surface tension which is at most as high as that of the solvent of the polymer solution. The process of any of claims 9 to 16, wherein said coagulating liquid has an electric conductivity. The process of any of claims 9 to 17, wherein said coagulating liquid is an aqueous solution. An apparatus for forming uniform liquid droplets having a narrow particle size distribution according to any of claims 1 to 8 and for carrying out the process according to any of claims 9 to 18, comprising a cylinder (2) having an inlet of a liquid (9) and at least one orifice (12) through which the liquid is sent out, a vibration rod (6) and a vibration generator connected with the vibrating rod (6), characterised by means for electrically charging the formed liquid droplets, by a vibration rod (6) inserted in the cylinder (2) and by an O-ring (7) for sealing the clearance between the cylinder (2) and the vibrating rod (6). The apparatus of claim 19, wherein said vibration generator is a magnetostrictive vibrator. The apparatus of claim 19, wherein said vibration generator is an electrostrictive vibrator. The apparatus of claim 19, wherein said vibration generator is an electromagnetic coil vibrator. The apparatus of claim 19, which has a means of heating (13) the cylinder (2). The apparatus of any of claims 19 to 23, which has a vibration transmission part (15) for transmitting the vibration generated by the vibration generator to the vibrating rod (6), and a means of cooling (10) the vibration transmission part (15) and a part of the vibrating rod (6) from the joint with the vibration transmission part (15) to the position contacting the O-ring (7). The apparatus of any of claims 19 to 24, which has one or more round shape orifices (12) having an aperture diameter of at most 500 µm. The apparatus of any of claims 19 to 25, wherein said vibrating rod (6) is vibrated at a frequency of 1000 to 40000 Hz. The apparatus of claim 26, wherein said vibrating rod (6) is vibrated at a frequency of 3000 to 40000 Hz.

Inventors: EGUCHI TAMIYUKI, TSUNOMORI MICHITO, EGUCHI, TAMIYUKI, TSUNOMORI, MICHITO
Applicants: KANEGAFUCHI CHEMICAL IND, KANEGAFUCHI KAGAKU KOGYO KABUSHIKI KAISHA
Application year: 1987
Main classification: B29B9
IPC codes: B29B9, C08J3, B01J2