Intrinsically antistatic thermoplastic resin compositions

Abstract: Thermoplastic resin compositions comprising 1 to 40 wt % a polyether ester amide (A) and 99 to 60 wt % of at least one thermoplastic resin (B) selected from styrene based resins, polyphenylene ether resins and polycarbonate resins are dis­ closed.These are permanently antistatic and in preferred forms are excellent in mechanical properties represented by impact resistance, heat resistance, moldability and also in the appear­ ance and gloss of the moldings, and are suitable for housing of optical or magnetic recording media.

Description: Synthetic polymeric materials are being used in extensive areas because of their excellent properties. If provided with antistatic capability in addition to the mechanical properties peculiar to them, these materials can find more areas of application. That is, they can be used for parts of electronic and electric machines such as copiers and television sets which it is desired to keep tree from electrostatic trouble, parts of various dustproof apparatuses, their housings, etc. Synthetic polymeric materials have been generally provided with antistatic property (1) by kneading a water absorbable compound such as a polyalkylene oxide, antistatic agent, etc. with the polymer concerned, or (2) by coating the polymer on the surface with a surfactant, etc. Neither method provides satisfactory antistatic property, nor can it avoid such problems that rinsing or surface wiping decreases the antistatic capability, or that the ingredient contained bleeds out onto the surface, to degrade the quality of the material, and that the antistatic property is degraded by secular change. These problems have not been solved so far. Various prior art documents disclose resin compositions comprising a blend of a polyether ester amide with a styrene based resin or a polyphenylene ether resin or a polycarbonate resin. These include JP-A-61 73 753 (published 15.04.86), JP-A-61 64 747 (published 03.04.86), EP-A-167 824, and EP-A-149 091. An object of the present invention is to provide intrinsically antistatic resins excellent in antistatic property, in mechanical properties represented by impact resistance, weld strength, heat resistance, and moldability and also in the appearance and gloss of moldings. Another object of the present invention is to provide intrinsically antistatic resins excellent in the prevention of layer exfoliation and mold corrosion. A further object of the present invention is to provide resins suitable for housings of optical and magnetic recording media. An intrinsically antistatic thermoplastic resin composition having a satisfactory combination of the qualities referred to in the above objects has now been found. The resin composition of the invention comprises (I) 1 to 40 weight percent of a polyether ester amide and 99 to 60 weight percent of at least one thermoplastic resin, the nature of which will be specified below; and (II) a modified vinyl polymer containing carboxyl groups in an amount of 0.1 to 14.8 weight percent based on the weight of the entire composition. The thermoplastic resin is selected from (i) styrene based resins containing a graft (co)polymer obtained by graft (co)polymerizing 99 to 20 weight % of amonomer or monomer mixture selected from a monomer or monomer mixture consisting of an aromatic vinyl monomer and/or a (meth)acrylic acid ester monomer, and a monomer mixture consisting of 99 to 40 weight % of an aromatic vinyl monomer and/or a (meth)acrylic acid ester monomer and 1 to 60 weight % of a vinyl cyanide monomer to 1 to 80 weight % of a rubbery polymer; (ii) polyphenylene ether resins; and (iii) polycarbonate resins. In the case where the thermoplastic resin consists of a styrene based resin containing the graft (co)polymer, the rubbery polymer must account for 1 to 40 weight % of the whole composition. In the description which follows the polyether ester amide will be referred to under the designation (A), the thermoplastic resin as (B) and the modified vinyl polymer as (D). The polyether ester amide (A) as a component of the present invention can be selected from block or graft copolymers obtained by letting a polyamide forming ingredient react with a poly(alkylene oxide) glycol and a dicarboxylic acid. Components of preferable polyether ester amides (A) in the present invention include the following. The polyamide forming ingredient can be selected from amino carboxylic acids with 6 or more carbon atoms, lactams and diamine-dicarboxylates. The aminocarboxylic acids include ω-aminocaproic acid, ω-aminoenanthic acid, ω-aminocaprylic acid, ω-aminopelargonic acid, ω-aminocapric acid, 11-aminoundecanoic acid, 12-aminododecanoic acid, etc. The lactams include caprolactam, enantholactam, capryllactam and laurolactam. The diamine-dicarboxylates include hexamethylenediamine-adipate, hexamethylenediamine-sebacate and bexamethylenediamine-isophthalate. Especially caprolactam, 12-aminododecanoic acid and hexamethylene-diamineadipate can be preferably used. The poly(alkylene oxide) glycol can be selected from polyethylene glycol, poly(1,2-propylene oxide) glycol, poly(1,3-propylene oxide) glycol, poly(tetramethylene oxide) glycol, poly(hexamethylene oxide) glycol, block or random copolymers of ethylene oxide and propylene oxide, block or random copolymers of ethylene oxide and tetrahydrofuran, etc. Among them, especially polyethylene glycol can be preferably used in view of excellent intrinsically antistatic property. The number average molecular weight of the poly(alkylene oxide) glycol should be 200 to 6,000, preferably 250 to 4,000. If the number average molecular weight is less than 200, the mechanical properties of the polyether ester amide obtained are degraded, and if more than 6,000, the antistatic capability deteriorates. The dicarboxylic acid should have 4 to 20 carbon atoms can be selected from aromatic dicarboxylic acids such as terephthalic acid, isophthalic acid, phthalic acid, naphthalene-2,6-dicarboxylic acid, naphthalene-2,7-dicarboxylic acid, diphenyl-4,4'-dicarboxylic acid, diphenoxyethanedicarboxylic acid and sodium 3-sulfoisophthalate alicyclic dicarboxylic acids such as 1,4-cyclohexanedicarboxylic acid, 1,2-cyclohexanedicarboxylic acid and dicyclohexyl-4,4'-dicarboxylic acid; aliphatic dicarboxylic acid such as succinic acid, oxalic acid, adipic acid, sebacic acid and decanedicarboxylic acid, etc. Especially terephthalic acid, isophthalic acid, 1,4-cyclohexanedicarboxylic acid, sebacic acid, adipic acid and decanedicarboxylic acid can be preferably used in view of polymerizability, color tone and physical properties. A poly(alkylene oxide) glycol and a dicarboxylic acid react theoretically at a molar ratio of 1 : 1, but usually, they are supplied at a different ratio, depending on the dicarboxylic acid used. The polyether ester composed of a poly(alkylene oxide) glycol and a dicarboxylic acid with 4 to 20 carbon atoms is a component unit of the polyether ester amide and is used in an amount of 95 to 10 wt %, preferably 80 to 30 wt % based on the weight of the polyether ester amide. A polyether ester content of more than 95 wt % degrades the mechanical properties of the polyether ester amide, and less than 10 wt % degrades the antistatic property of the resin obtained. The thermoplastic resin (B) can be a styrene based resin, which can be selected from rubber modified polystyrene, styrene-rubbery polymer-acrylonitrile copolymers (ABS resin, AES resin, AAS resin) etc. Two or more of styrene based resins can be used. In these resins, the styrene and/or acrylonitrile may be partially substituted by α-methylstyrene, p-methylstyrene, p-t-butylstyrene, (meth)acrylic acid or any of their ester compounds of methyl, ethyl, propyl, n-butyl, etc., unsaturated dicarboxylic acids, unsaturated dicarboxylic anhydrides, maleimide based monomers such as maleimide, N-methylmaleimide and N-phenylmaleimide, and vinyl monomers copolymerizable with styrene such as acrylamide. Especially preferably used styrene based resins are ABS resin, AES resin, AAS resin, MBS resin, etc. The styrene based resin contains a graft (co)polymer which is composed of a rubbery polymer, and an aromatic vinyl monomer and/or a (meth)acrylic acid ester monomer, and optionally a vinyl cyanide monomer. The rubbery polymer should be preferably lower than 0°C in glass transition temperature, and can be selected from diene rubbers such as polybutadiene, polystyrene-butadiene and polyacrylonitrile-butadiene, polyisoprene, polychloroprene, acrylic rubbers such as polybutylacrylate, three-ingredient copolymers based on ethylene, propylene and diene, etc. Polybutadiene and butadiene copolymer are preferred. The aromatic vinyl monomer can be selected from styrene, α-methylstyrene, vinyltoluene, o-ethylstyrene, o-p-dichlorostyrene, etc. Styrene is preferred. The (meth)acrylic acid ester monomer can be selected from methyl, ethyl, propyl, n-butyl, i-butyl, etc. of acrylic and methacrylic acids. Methyl methacrylate is preferred. The vinyl cyanide monomer can be selected from acrylonitrile, methacrylonitrile, ethacrylonitrile, etc. Acrylonitrile is preferred. As required, other vinyl monomers, for example, maleimide based monomers such as maleimide, N-methylmaleimide and N-phenylmaleimide, acrylamide, etc. can also be used. The mixture of an aromatic vinyl monomer and/or (meth)acrylic acid ester monomer and a vinyl cyanide monomer used to prepare the graft (co)polymer should consist of 99 to 40 wt %, preferably 90 to 50 wt % of an aromatic vinyl monomer and/or (meth)acrylic acid ester monomer and 1 to 60 wt %, preferably 10 to 50 wt % of a vinyl cyanide monomer. If the amount of the vinyl cyanide monomer is less than 1 wt %, the effect of enhancing impact resistance by adding the vinyl cyanide monomer is minimal. If more than 60 wt %, the thermal stability of the graft copolymer is remarkably lowered, to degrade the moldings in color tone. The graft (co)polymer consisting of a rubbery polymer and a monomer or monomer mixture should consist of 1 to 80 parts by weight, preferably 5 to 70 parts by weight of a rubbery polymer and 99 to 20 parts by weight, preferably 95 to 30 parts by weight of the monomer or monomer mixture-in total 100 parts by weight of the graft (co)polymer. If the amount of the rubbery polymer in the graft (co)polymer is less than 1 part by weight, the impact resistance of the resin composition obtained is poor, and if more than 80 parts by weight, the rubbery polymer is defectively dispersed, to impair the appearance of the moldings. In addition to the graft (co)polymer, the graft-(co)polymer-containing composition can further contain another (co)polymer such as styrene-acrylonitrile copolymer, α-methylstyrene-styrene-acrylonitrile copolymer, α-methylstyrene-methyl methacrylate-acrylonitrile copolymer, α-methylstyrene-acrylonitrile copolymer, styrene-methyl methacrylate-acrylonitrile copolymer, styrene-methyl methacrylate copolymer, styrene-N-phenylmaleimideacrylonitrile copolymer, α-methylstyrene-methyl methacrylate copolymer, polystyrene, polymethyl methacrylate, etc. Preferable are a (co)polymer consisting of an aromatic vinyl monomer and/or a (meth)acrylic acid ester, a (co)polymer consisting of an aromatic vinyl monomer and/or a (meth)acrylic acid ester monomer and a vinyl cyanide monomer, etc. Especially a (co)polymer consisting of 100 to 40 wt %, preferably 100 to 50 wt % of an aromatic vinyl monomer and/or a (meth)acrylic acid ester monomer, and 0 to 60 wt %, preferably 0 to 50 wt % of a vinyl cyanide monomer is most preferable. In the (co)polymer, if the amount of the aromatic vinyl monomer and/or (meth)acrylic acid ester monomer is too small, the affinity with the polyether ester amide becomes poor, and layer exfoliation tends to be caused. Therefore, the amount should preferably be 40 wt % or more. Where the component (B) is a styrene based resin containing said graft (co)polymer, the amount of the rubbery polymer is 1 to 40 wt % in the entire resin composition. If the amount of the rubbery polymer is less than 1 wt %, the impact resistance of the resin composition is degraded, and if more than 40 wt %, the composition becomes undesirably soft. The resin composition of the present invention further contains a modified vinyl polymer (D) containing carboxyl groups (hereinafter abbreviated as "modified vinyl polymer"). It is a polymer or copolymer with a structure obtained by polymerizing or copolymerizing one or more vinyl monomers and containing carboxyl groups in the molecule. The carboxyl groups may be anhydrous carboxyl groups. The carboxyl group content is not especially limited, and can be small or large to such an extent that no degradation is caused in resin performance. Usually, the effect of the present invention can be efficiently displayed if the modified vinyl polymer substantially contains one or more carboxyl groups on the average in the molecule. The method for introducing carboxyl groups into the modified vinyl polymer is not especially limited. The introduction can be executed, for example, (1) by copolymerizing a vinyl monomer containing a carboxyl group or anhydrous carboxyl group such as acrylic acid, methacrylic acid, maleic acid, maleic anhydride, phthalic acid or itaconic acid, with a desired vinyl monomer, or (2) by (co)polymerizing a desired vinyl monomer, using a polymerization initiator with a carboxyl group such as γ,γ'-azobis(γ-cyanovaleric acid), α,α'-(α-cyano)ethyl-p-benzoic acid or succinic acid peroxide and/or a polymerization degree regulating agent such as thioglycollic acid, α-mercaptopropionic acid, β-mercaptopropionic acid, α-mercaptoisobutyric acid or 2,3- or 4-mercaptobenzoic acid, or (3) by saponifying a (co)polymer of a (meth)acrylic acid ester such as methyl methacrylate or butyl acrylate, by an alkali. The vinyl monomer used to prepare the modified vinyl polymer is not especially limited, and can be one or more selected for each purpose, for example, from aromatic vinyl monomers such as styrene and α-methylstyrene, vinyl cyanide monomers such as acrylonitrile and methacrylonitrile, (meth)acrylic acid ester monomers such as methyl methacrylate and butyl acrylate, α,β-unsaturated carboxylic acids (anhydrides) such as maleic acid and maleic anhydride, and vinyl monomers such as vinyl chloride, vinyl acetate and butadiene. Especially aromatic vinyl monomers such as styrene, (meth)acrylic acid ester monomers such as methyl methacrylate, maleimide monomers such as N-phenylmaleimide, and vinyl cyanide monomers such as acrylonitrile can be preferably used, since the resin compositions obtained become excellent in mechanical properties. The amount of the modified vinyl polymer should be 0.1 to 14.8 wt %, preferably 1 to 14.8 wt % based on the weight of the entire composition. If the amount is less than 0.1 wt %, the effect of enhancing impact resistance by the modified vinyl polymer is minimal. The resin composition of the present invention may further contain an organic halogen compound, meaning thereby an organic compound with a halogen atom in the molecule, i.e., being chlorinated or brominated, and generally known as a flame retardant, and can be concretely selected from low molecular weight organic bromine compounds such as hexabromobenzene, pentabromotoluene, hexabromobisphenyl, decabromobisphenyl, hexabromocyclodecane, decabromodiphenyl ether, octabromodiphenyl ether, hexabromodiphenyl ether, bis(pentabromophenoxy)ethane, ethylenebis(tetra-bromophthalimide) and tetrabromobisphenol A, halogenated polymers and oligomers such as brominated polycarbonates (e.g., polycarbonate oligomer prepared from brominated bisphenol A), brominated epoxy compounds (e.g.,a diepoxy compound prepared by the reaction between brominated bisphenol A and epichlorohydrin, a monoepoxy compound prepared by the reaction between brominated phenol and epochlorohydrin), poly(brominated benzylacrylate), brominated polyphenylene ether, brominated bisphenol A, a condensation product of cyanuric chloride and brominated bisphenol, and brominated polystyrene, and their mixtures. Among them, decabromodiphenyl ether, tetrabromobisphenol A, and brominated polycarbonate can be preferably used. The amount of the organic halogen compound should be preferably 1 to 60 wt %, more preferably 5 to 40 wt % based on the weight of the entire composition. If the amount is less than 1 wt %, flame retardancy is insufficient, and if more than 60 wt %, the physical properties of the composition are considerably lowered unpreferably. As desired, the organic halogen compound can be used with an antimony compound such as antimony trioxide. It is also allowed to use zirconium oxide, zinc sulfide, barium sulfate etc. together with antimony trioxide. The thermoplastic resin (B) can be a polyphenylene ether resin, or a mixture of such a resin with a styrene based resin containing the graft (co)polymer, particularly a mixture with 1 to 99 wt % of the styrene based resin containing the graft (co)polymer to 99 to 1 wt % of polyphenylene ether resin. The polyphenylene ether resin is a homopolymer or copolymer with the following formula [I] as the unit. (where Q₁, Q₂, Q₃ and Q₄ respectively independently stand for a hydrogen atom, halogen atom, hydrocarbon group, halo hydrocarbon group, hydrocarbon oxy group or halo hydrocarbon oxy group; and n is the repeated number of the monomer unit and stands for an integer of 20 or more). Furthermore, the polyphenylene ether resin (B) can also be selected from the graft polymers obtained by graft-polymerizing an aromatic vinyl monomer to a polyphenylene ether resin. A polyphenylene ether resin can be prepared by letting a phenol react according to the procedure described in the specification of, for example, US Patent No.3 306,874, 3,306,875, 3,257,357 or 3,257,358. The phenol can be selected from 2,6-dimethylphenol, 2,6-diethylphenol, 2,6-dibutylphenol, 2,6-dilaurylphenol, 2,6-dipropylphenol, 2,6-diphenylphenol, 2-methyl-6-ethylphenol, 2-methyl-6-cyclohexylphenol, 2-methyl-6-tolylphenol, 2-methyl-6-methoxyphenol, 2-methyl-6-butylphenol, 2,6-dimethoxyphenol, 2,3,6-trimethylphenol, 2,3,5,6-tetramethylphenol and 2,6-diethoxyphenol, but is not limited to these. Any of these may be polymerized to obtain the corresponding homopolymer or may be copolymerized with another phenol, to prepare the corresponding copolymer with a different unit conforming to the above formula. For example, 2,6-dimethylphenol may be polymerized to make its polymer, i.e., poly(2,6-dimethyl-1,4-phenylene) ether, or 2,6-dimethyl phenol may be copolymerized with another phenol such as 2,3,6-trimethylphenol or 2-methyl-6-butylphenol, etc., to make the corresponding copolymer such as poly(2,6-dimethyl-2-methyl-6-butyl-1,4-phenylene) ether. The thermoplastic resin (B) constituting the present invention composition can be a polycarbonate resin. The polycarbonate resin can be an aromatic polycarbonate, aliphatic polycarbonate, or aliphatic-aromatic polycarbonate, etc. In general, it is a homopolymer or copolymer of a bisphenol such as a 2,2-bis(4-hydroxyphenyl) alkane, bis(4-hydroxyphenyl) ether or bis(4-hydroxyphenyl) sulfone, sulfide or sulfoxide, or also a polymer of a bisphenol substituted by a halogen atom as required for a specific purpose. The present invention composition can further contain a hydrotalcite. It is a compound represented by general formula [M 1-x ²⁺ M x ³⁺ (OH)₂] x+ [A x/n n- ·mH₂O] x- (where M²⁺ stands for a divalent metal such as Mg²⁺, Mn²⁺, Fe²⁺, Co²⁺, Ni²⁺, Cu²⁺ or Zn²⁺; M³⁺, a trivalent metal such as Al³⁺, Cr³⁺, Co³⁺ or In³⁺; A n- , an n-valent anion such as OH⁻, F⁻,Cl⁻ , Br⁻, NO₃⁻, CO₃² ⁻ , SO₄²⁻, Fe(CN)₆³⁻, CH₃COO⁻, oxalate ions or salicylate ion; m, the mole number of hydrate; n, charges on anion(s) A; and x, a number smaller than 1). Above all, preferable is Mg 4.5 Al₂(OH)₁₃CO₃ 3.5H₂O and Mg 4.5 Al₂(OH)₁₃CO₃. Hydrotalcite compounds can be synthesized by various methods as described in US Patent Specification No. 3,539,306. In general, a synthetic hydrotalcite is produced by coprecipitation of a cationic ingredient solution and an anionic ingredient solution. The most easily available hydrotalcite must be magnesium-aluminium hydroxycarbonate hydrate. A preferable hydrotalcite is magnesium aluminium hydroxycarbonate hydrate available under brand DHT-40 expressed as Mg 4.5 Al₂(OH)₁₃CO₃ 3.5H₂O by the manufacturer. The amount of the hydrotalcite used should be preferably 0.01 to 10 wt %, more preferably 0.1 to 5 wt % based on the entire composition. If the amount is less than 0.01 wt %, mold corrosion is only poorly prevented, and if more than 10 wt %, the physical properties of the composition are considerably degraded disadvantageously. The present invention compositions can be molded to prepare housings of optical or magnetic media which can prevent optical or magnetic records from dropping out and sounds and pictures from being disturbed. For example, they can be used for optical disc jackets, video floppies, digital audio casettes, television remote control cases, television game software, video cassettes, video discs and IC cards. A composition of the present invention comprises 1 to 40 wt %, preferably 5 to 30 wt % of a polyether ester amide (A) and 99 to 60 wt %, preferably 95 to 70 wt % of at least one thermoplastic resin (B). If the amount of polyether ester amide (A) is less than 1 wt %, the antistatic property of the composition is insufficient, and if more than 40 wt %, the composition becomes soft and degraded in mechanical properties. The present invention composition may be mixed with another thermoplastic resin compatible with it, such as a polyamide, polybutylene terephthalate, polyethylene terephthalate, vinyl chloride resin, or an elastomer like styrene-butadiene block copolymer, to be enhanced in moldability. Furthermore, an antistatic agent such as a metal sulfonate or an anionic, cationic or nonionic surfactant can be added to further enhance the antistatic capability. In addition, as required, various stabilizers such as an antioxidant, ultraviolet ray absorbent, etc., pigment, dye, lubricant, plasticizer, glass fibers, metallic filler, etc. can also be added. Examples The present invention is described more concretely below in reference to present invention examples and comparative examples. The finally obtained resin compositions were injection-molded and tested by the following methods, to measure respective physical properties. Izod impact strength: ASTM D256-56A Thermal distortion temperature: ASTM D648 (18.56 kg/cm² load) Flexural elastic modulus: ASTM D790 Combustibility: Vertical burning test was executed using a 1/16" x 1/2" x 5" (0.16 x 1.27 x 12.7 cm) test piece according to UL94 Code. MFR: Measured at 220°C and 10 kg (98.1 N) load, using a 2 mm dia. x 8 mm nozzle. Volume resistivity: Measured at room temperature (23°C) and 50% RH, using a 2 mm t x 40 mm dia. disc. For the measurement, super-insulation resistance meter Model SM-10 made by Toa Electronics Ltd. was used. Prevention of layer exfoliation of molded product: A molded product as a test piece was folded and tensile-tested, and the fracture was observed in reference to the following criterion: o ○ Very good ○ Good × Molded product caused layer exfoliation. Appearance of molded product: Appearance was observed in reference to the following criterion: o ○ Very good ○ Good × Molded product was inferior in surface appearance. In the following examples, "parts" mean "parts by weight" and "%" means "wt %". Reference Example (1) Preparation of polyether ester amides (A) A-1: Forty five parts of caprolactam, 51.6 parts of polyethylene glycol of 2000 in number average molecular weight and 4.5 parts of terephthalic acid were put into a reactor with helical ribbon stirring blades, together with 0.2 part of Irganox 1098 (antioxidant) and 0.1 part of antimony trioxide catalyst. With the atmosphere substituted by nitrogen, the mixture was heated and stirred at 240°C for 60 minuts, to make a transparent homogeneous solution, and polymerization was executed at 260°C and 0.5 mm Hg or less for 4 hours, to obtain a consistent transparent polymer. The polymer was discharged like guts onto a cooling belt and pelletized, to prepare a polyether ester amide (A-1) as pellets. A-2: Operation was executed as done to prepare (A-1), except that 60 parts of nylon 6.6 salt (AH salt), 33.8 parts of polyethylene glycol of 600 in number average molecular weight and 8.7 parts of adipic acid were used for polymerization for 4 hours, to prepare a polyether ester amide (A-2). A-3: Operation was executed as done to prepare (A-1), except that 30 parts of ω-aminodecanoic acid, 14.2 parts of decanedicarboxylic acid and 58.6 parts of polyethylene glycol of 1000 in number average molecular weight were used for polymerization for 3 hours, to prepare a polyether ester amide (A-3). A-4: Operation was executed as done to prepare (A-1), except that 95 parts of ω-aminodecanoic acid, 4.2 parts of polyethylene glycol of 1000 in number average molecular weight and 1.0 part of decanedicarboxylic acid were used, to prepare a polyether ester amide (A-4). (2) Preparation of graft (co)polymers (B) B-1: Forty parts of a monomer mixture consisting of 55% of styrene and 45% of methyl methacrylate were emulsion-polymerized in the presence of 60 parts (in terms of solid content) of a polybutadiene latex (rubber grain size 0.25 µm, gel content 80%). The obtained graft copolymer was coagulated by sulfuric acid, neutralized by caustic soda, washed, filtered and dried, to prepare a powdery graft copolymer (B-1). B-2: Ten parts of Diene NF35A (made by Asahi Kasei Ltd.) were dissolved into 90 parts of styrene, to prepare a graft polymer (B-3) by bulk polymerisation. B-3: Forty parts of a monomer mixture consisting of 70% of styrene and 30% of acrylonitrile were emulsion-polymerized in the presence of 60 parts (in terms of solid content) of the polybutadiene latex used in B-1, to prepare a powdery graft copolymer (B-3) as done to prepare (B-1). B-4: Sixty parts of a monomer mixture consisting of 72% of methyl methacrylate, 24% of styrene and 4% of acrylonitrile were emulsion-polymerized in the presence of 40 parts (in terms of solid content) of the polybutadiene latex used in B-1, to prepare a powdery graft copolymer (B-4) as done to prepare (B-1). B-5: Eighty five parts of a monomer mixture consisting of 75% of styrene and 25% of acrylonitrile were emulsion-polymerized in the presence of 15 parts (in terms of solid content) of the polybutadiene used in B-1, to prepare a powdery graft copolymer (B-5) as done to prepare (B-1). B-6: Fifteen parts of a monomer mixture consisting of 70% of styrene and 30% of acrylonitrile were emulsion-polymerized in the presence of 85 parts (in terms of solid content) of the polybutadiene latex used in B-1, to prepare a powdery graft copolymer (B-6) as done to prepare (B-5). B-7: CPX-100L (Mitsubishi Gas Chemical Co., Inc.) was used. B-8: Lexan 121-111 (EPL) was used. (3) Preparation of (co)polymers (C) C-1: Fifty five parts of methyl methacrylate and 45 parts of styrene were suspension-polymerized, to prepare a copolymer (C-1). C-2: Seventy two parts of styrene and 28 parts of acrylonitrile were suspension-polymerized, to prepare a copolymer (C-2). C-3: Seventy two parts of methyl methacrylate, 24 parts of styrene and 4 parts of acrylonitrile were suspension-polymerized, to prepare a copolymer (C-3). C-4: Fifty parts of styrene, 30 parts of N-phenylmaleimide and 20 parts of acrylonitrile were suspension-polymerized, to prepare a copolymer (C-4). (4) Preparation of modified vinyl polymers containing carboxyl groups (D) D-1: Forty five parts of styrene, 50 parts of methyl methacrylate and 5 parts of methacrylic acid were suspension-polymerized, to prepare a modified vinyl polymer (D-1) as beads. D-2: Seventy parts of styrene, 25 parts of acrylonitrile and 5 parts of methacrylic acid were suspension-polymerized, to prepare a modified vinyl polymer (D-2) as beads. D-3: Seventy parts of methyl methacrylate, 24 parts of styrene, 4 parts of acrylonitrile and 2-parts of acrylic acid were suspension-polymerized, to prepare a modified vinyl polymer (D-3) as beads. D-4: Ninety parts of styrene and 10 parts of methacrylic acid were suspension-polymerized, to prepare a modified vinyl polymer (D-4) as beads. D-5: Ninety parts of styrene and 10 parts of maleic anhydride were mixed in a solution, and the solvent was removed, to prepare a modified vinyl polymer (D-5). Examples of the invention and Comparative Examples The polyester ester amides (A), thermoplastic resins (B) and/or modified vinyl polymers (D) prepared in the Reference Example were mixed at ratios listed in Table 1, molten, kneaded and extruded at a resin temperature of 200°C by a vented 40 mm die. extruder, to prepare pellets. For the thermoplastic resins (B) containing a polyphenylene ether resin and a polycarbonate resin, the other ingredients than the polyphenylene ether resin and polycarbonate resin were mixed, and molten, kneaded and extruded at a resin temperature of 200°C, to prepare pellets, and the pellets were mixed with the polyphenylene ether resin and polycarbonate resin. The mixtures were then molten, kneaded and extruded at any resin temperature of 240 to 260°C, to prepare pellets. They were molded to prepare desired test pieces by an injection molding machine. The volume resistivity values were measured using 2 mm thick discs under the following conditions: (1) Immediately after completion of molding, the test piece was sufficiently washed with distilled water, had the water on the surface removed, allowed to stand at 50% RH and 23°C for 24 hours. (2) After completion of molding, the test piece was allowed to stand at 50% RH and 23°C for 200 days, washed sufficiently with distilled water, had the water on the surface removed and allowed to stand at 50% RH and 23°C for 24 hours, and measured. Physical properties of the resin compositions were also measured, and the results are listed in Table 2. Properties as housings of recording media were also evaluated, and the results are listed in Table 3.

Claims: Intrinsically antistatic thermoplastic resin compositions comprising (I) 1 to 40 wt % of a polyether ester amide (A) and 99 to 60 wt % of at least one thermoplastic resin (B) selected from styrene based resins containing a graft (co)polymer obtained by graft (co)polymerizing 99 to 20 wt % of a monomer or monomer mixture selected from a monomer or monomer mixture consisting of an aromatic vinyl monomer and/or a (meth)acrylic acid ester monomer, and a monomer mixture consisting of 99 to 40 wt % of an aromatic vinyl monomer and/or a (meth)acrylic acid ester monomer and 1 to 60 wt % of a vinyl cyanide monomer to 1 to 80 wt % of a rubbery polymer; polyphenylene ether resins; and polycarbonate resins and (II) a modified vinyl polymer (D) containing carboxyl groups in an amount of 0.1 to 14.8 wt % based on the weight of the entire composition, with the proviso that, in the case of using a styrene based resin containing the said graft (co)polymer, the rubbery polymer accounts for 1 to 40 wt % of the entire composition. Compositions according to claim 1, wherein the polyether ester amide (A) is formed from an aminocarboxylic acid with 6 or more carbon atoms or a lactam or a diaminedicarboxylate with 6 or more carbon atoms, a poly(alkylene oxide) glycol of 200 to 6000 in number average molecular weight and a dicarboxylic acid with 4 to 20 carbon atoms, with the polyether ester unit accounting for 95 to 10 wt %. Compositions according to claim 2, wherein the poly(alkylene oxide) glycol is a polyethylene glycol. Compositions according to any one of the preceding claims, wherein the thermoplastic resin (B) is a styrene based resin containing the graft (co)polymer. Compositions according to any preceding claim, using for the thermoplastic resin (B) a graft (co)polymer selected from rubber modified polystyrene, ABS resin, AAS resin, AES resin and MBS resin. Compositions according to any one of claims 1 to 3, wherein the thermoplastic resin (B) is a polyphenylene ether resin. Compositions according to any one of claims 1 to 4, wherein the thermoplastic resin (B) is a mixture consisting of a styrene based resin containing the graft (co)polymer and a polyphenylene ether resin. Compositions according to claim 7, wherein the mixing ratio of the styrene based resin containing the graft (co)polymer and the polyphenylene ether resin is 99-1 wt % : 1 - 99 wt %. Compositions according to any one of claims 1 to 3, wherein the thermoplastic resin (B) is a polycarbonate resin. Compositions according to any one of claims 1 to 4, wherein the thermoplastic resin (B) is a mixture of a styrene based resin containing the graft (co)polymer and a polycarbonate resin. Compositions according to any preceding claim, containing an organic halogen compound in an amount of 1 to 60 wt % based on the weight of the entire composition. Compositions according to any preceding claim, wherein a hydrotalcite is further contained in an amount of 0.01 to 10 wt % based on the weight of the entire composition. Housings of optical or magnetic recording media, prepared by molding from an intrinsically antistatic resin composition according to any preceding claim.

Inventors: FUKUMOTO TADAO, IWAMOTO MASATOSHI, KISHIMOTO AKIHIKO, FUKUMOTO, TADAO, IWAMOTO, MASATOSHI, KISHIMOTO, AKIHIKO
Applicants: TORAY INDUSTRIES, TORAY INDUSTRIES, INC.
Application year: 1987
Main classification: C08L25
IPC codes: C08L69, G11B23, C08L71, C08L25, C08L77, C08L67, C08L51