FLUORINE-CONTAINING COPOLYMER AND OIL AND WATER REPELLENT COMPOSITION CONTAINING THE SAME

Abstract: A copolymer comprising 50 to 90% by weight of the constituting unit derived from (a) a polymerizable compound having a perfluoralkyl group of 4 to 20 carbon atoms, 10 to 50% by weight of the constituting unit derived from (b) cyclohexyl or benzyl ester of acrylic acid or methacrylic acid and 0.1 to 10% by weight of the constituting unit derived from (c) at least one selected from the group consisting of polyethylene glycol diacrylate of the formula CH₂=CRCOO(CH₂CH₂O)rCOCR=CH₂ wherein R is hydrogen atom or methyl, r is an integer of 1 to 50, and N-methylolacrylamide. The copolymer is useful as an oil and water repellent composition.

Description: The present invention relates to a fluorine-containing copolymer having solubility in organic solvents, which can afford an oil and water repellent composition, and to an oil and water repellent composition containing the copolymer. Conventionally, an oil and water repellent composition was known which comprises a polymer of a compound having perfluoroalkyl group. Oil and water repellent compositions are classified, for example, into a latex type in which the copolymer is emulsified in an aqueous medium with use of a surfactant, solution type in which the copolymer is dissolved in an organic solvent, aerosol type. In order to use the composition in commercially wide fields or to afford various other properties, it is proposed to copolymerize the compound having perfluoroalkyl group with other polymerizable compound such as alkyl acrylate, maleic anhydride, chloroprene, butadiene, methyl vinyl ketone, styrene. For example, it is known that the compound having perfluoroalkyl group is copolymerized with methyl acrylate, butyl methacrylate to render the resulting copolymer soluble in an organic solvent to prepare a solution type oil and water repellent composition. Although, the copolymer obtained by the copolymerization of the compound having perfluoroalkyl group with methyl acrylate or butyl methacrylate has an improved solubility in an organic solvent, the copolymer has a defect of being lowered in oil and water repellency, particularly in water repellency. Further, vinyl acetate or vinyl chloride does not lower water repellency of the resulting copolymer, but they render the copolymer insoluble in an organic solvent. JP-B-3759/1978 discloses a copolymer of a compound having a perfluoroalkyl group and benzyl acrylate or methacrylate, which copolymer has solubility in organic solvents without reducing water repellency. EP-A-198252 discloses a water and oil repellent composition containing a copolymer derived from a perfluoroalkyl (meth)acrylate and a methacrylate the homopolymer of which has a glass transition temperature of not lower than 115°C and, optionally, other comonomers, such as benzyl acrylate or N-methylolacrylamide. With the trend towards increasing needs for high and varied quality of oil and water repellent compositions, it is required to further improve the properties thereof, but the oil and water repellent compositions containing the above copolymers have the problem of being inferior, particularly in oil and water repellency after dry-cleaning. An object of the present invention is to provide an oil and water repellent composition which has excellent solubility in an organic solvent, is extremely improved in oil and water repellency and in lasting of the repellency, and further has excellent durability to dry-cleaning, and to provide a fluorine-containing copolymer constituting the composition. The present invention provides a copolymer comprising 50 to 90% by weight of the constituting units derived from (a) a polymerizable compound having a perfluoroalkyl group of 4 to 20 carbon atoms, 10 to 50% by weight of the constituting units derived from (b) cyclohexyl or benzyl ester of acrylic acid or methacrylic acid and 0.1 to 10% by weight of the constituting units derived from (c) polyethylene glycol diacrylate of the formula CH₂=CRCOO(CH₂CH₂O)rCOCR=CH₂ wherein R is hydrogen or methyl, r is an integer of 1 to 50, and, optionally, N-methylolacrylamide. The compound having a perfluoroalkyl group of 4 to 20 carbon atoms of the present invention (hereinafter referred to as "(a) monomer") includes the following acrylates and methacrylates. In the above, Rf is perfluoroalkyl group of 4 to 20 carbon atoms, R¹ is hydrogen atom or alkyl group of 1 to 10 carbon atoms, R² is alkylene group of 1 to 10 carbon atoms, R³ is hydrogen atom or methyl group, R⁴ is alkyl group of 1 to 17 carbon atoms, n is 1 to 10, m is 0 to 10. The amount of (a) monomer is 50 to 90% by weight. Amounts less than 50% render the copolymer lower oil and water repellency. The content of cyclohexyl or benzyl ester of acrylic acid or methacrylic acid of the present invention (hereinafter referred to as "(b) monomer") is 10 to 50% by weight. Amounts less than 10% render the copolymer less soluble in an organic solvent. Amounts more than 50% render oil and water repellency of the copolymer lower. Among polyethylene glycol diacrylate of the formula CH₂=CRCOO(CH₂CH₂O)rCOCR=CH₂ wherein R is hydrogen atom, or methyl, r is an integer of 1 to 50 (hereinafter referred to as "(c₁) monomer"), preferable are those having r of 14 to 23. Further, in the present invention, sometimes is used N -methylolacrylamide (hereinafter referred to as "(c₂) monomer"). In case of using the both of (c₁) monomer and (c₂) monomer, the resulting oil and water repellent composition has extremely excellent durability to dry-cleaning, and hence is preferable. In the invention, (c₁) monomer and (c₂) monomer are referred to as (c) monomer. In the present invention, the copolymer comprises optionally as a constituting unit thereof, at least one of various copolymerizable compounds such as ethylene, vinyl acetate, vinyl fluoride, vinyl chloride, acrylic acid amide, methacrylic acid amide, styrene, α-methylstyrene, p -methylstyrene, alkyl(C 1∼20 ) ester of acrylic acid or methacrylic acid, benzyl acrylate or methacrylate, vinyl alkyl(C 1∼20 ) ether, halogenated alkyl(C 1∼20 ) vinyl ether, vinyl alkyl(C 1∼20 ) ketone, maleic anhydride, butadiene, isoprene, chloroprene. In the present invention is prepared a copolymer comprising 50 to 90% (% by weight, the same as hereinafter) of the constituting units derived from (a) monomer, 10 to 50% of the one derived from (b) monomer, 0.1 to 10% of the one derived from (c) monomer which is (c₁) monomer and, optionally, (c₂) monomer and the copolymer is used as an oil and water repellent composition. The copolymer can be prepared by copolymerizing these monomers according to a known method such as bulk polymerization, solution polymerization, suspension polymerization, emulsion polymerization, radiation polymerization or photopolymerization. For example, for solution polymerization, the monomers to be polymerized are dissolved in an organic solvent and copolymerized with stirring. Examples of polymerization initiators are organic peroxides, azo compounds, persulfates and ionized radiation such as γ-ray. For emulsion polymerization are used as a surfactant almost all of emulsifiers which are any of anionic, cationic or nonionic one. In the present invention, the copolymer may be prepared opptionally by copolymerizing the above-mentioned monomer such as ethylene or vinyl acetate. By selecting and copolymerizing the above polymerizable compound with the present monomers, it is possible to improve the characteristics such as soil release property, wear resistance, selective solubility, flexibility or touch-softness in addition to oil and water repellency and durability. The copolymer of the present invention has a molecular weight of preferably 10,000 to 60,000. The oil and water repellent composition comprising the present copolymer can be formulated into an aerosol composition according to a usual manner. For example, it is possible to prepare an aerosol concentrate containing 10 to 40wt.% of the present copolymer which is directly obtained by solution polymerization. Further, the copolymer obtained by emulsion polymerization, suspension polymerization, bulk polymerization or like other polymerization methods is separated from the medium and is dissolved in a solvent to obtain a solution. Preferred examples of solvents used for polymerization are trichlorotrifluoroethane, difluoroethane, acetone, methyl - chloroform, trichloroethylene, tetrachloroethylene. These solvents can be used singly or in mixture of at least two of them. Aerosol formulation can be prepared by dissolving the copolymer in the above solvent into a solution at a concentration of 0.2 to 5wt.% of the copolymer, adding thereto a propellant such as dichlorofluoromethane, monofluorotrichloromethane, dichlorotetrafluoroethane and filling the mixture in an appropriate container. Generally, 40 to 80 parts of the solution and 60 to 20 parts of the propellant are mixed. Further, the oil and water repellent composition of the present invention may be mixed with an other polymer, or with other additives such as other water repellent composition, oil repellent composition, insecticide, flame retarder, antistatic agent, dye fixing agent or flavor. Articles which can be treated with the oil and water repellent composition of this invention are not limited, and can be fibrous fabrics, glass, paper, wood, leather, wool, asbestos, brick, cement, metal, metal oxides, ceramics, plastics, coating surfaces and plaster. Particularly preferable are fiber or fibrous fabric made of polyester, cotton, polyamide, acrylic polymer, silk, wool, and mixtures thereof. The present invention will be explained in more detail by showing examples and comparison examples. In the following, water repellency and oil repellency are measured by the methods below. Water repellency is measured by J I S L-1092 spray method and is evaluated by water repellency rating shown in Table 1. Oil repellency is measured by placing a drop of test solution on the article, observing whether any penetration into the article is noted visually after three minutes, and is evaluated by oil repellency rating given in Table 2. In the water repellency rating, the "+" symbol next to some numbers indicates a number slightly higher than the base numbers. Dry-cleaning test was conducted with use of a Launder-o-meter by treating the article with tetrachloroethylene at 30°C for 30 minutes and drying at room temperature, and dry-cleaning property was evaluated by water repellency rating according to J I S L-1092. Shower test was conducted according to J I S L -1092 by showering the article continuously with water and the result is evaluated by water repellency rating after prescribed period. Examples 1 to 13 and Comparison Examples 1 to 7 Five or less kinds of the monomers listed in Table 3 were placed into a 100-cc flask in a prescribed amount (total in 20g). Thereto were added 46g of trichlorotrifluoroethane, 46g of tetrachloroethylene, 3g or tert-butyl alcohol and 3 g of acetone. The flask was provided with a thermometer, nitrogen purge tube, stirrer and condenser and the mixture was copolymerized with addition of 0.3g of Perbutyl PV (catalyst, a product of Nippon Oil & Fats Co., Ltd.) at 60°C for 12 hours with stirring while purging with nitrogen. The resulting copolymer solution was diluted with tetrachloroethylene to obtain a 0.2wt.% solution of the copolymer. A polyester fabric (tropical) was dipped in the above diluted solution, squeezed by a mangle and dried at room temperature for 24 hours. Table 3 shows oil and water repellency and dry-cleaning property of the treated fabric. The copolymer obtained in Example 1 had melting point of 65°C and molecular weight (vapor pressure equilibrium method, solvent : metaxylene hexafluoride) of 40,000. In Table 3, FA : CH₂=CHCOOCH₂CH₂C₈F₁₇ FMA : CH₂=C(CH₃)COOCH₂CH₂C₈F₁₇ NK23G : NK ester 23G produced by Shin-Nakamura Chemical Co., Ltd. and represented by the formula CH₂=C(CH₃)COO(CH₂CH₂O)₂₃COC(CH₃)=CH₂ NKA600 : NK ester A600 produced by Shin-Nakamura Chemical Co., Ltd. and represented by the formula CH₂=CHCOO(CH₂CH₂O)₁₃COCH=CH₂ NMAM : CH₂=CHCONHCH₂OH MA : CH₂=CHCOOCH₃ MMA : CH₂=C(CH₃)COOCH₃ n-BMA : CH₂=C(CH₃)COOCH₂CH₂CH₂CH₃ BenA : CH₂=CHCOOCH₂C₆H₅ BenMA : CH₂=C(CH₃)COOCH₂C₆H₅ StA : CH₂=CHCOOC₁₈H₃₇ * : Lauryl methacrylate WR : Water repellency OR : Oil repellency DC : Dry-cleaning property Examples 14 to 17 and Comparison Examples 8 to 9 Copolymers having a composition listed in Table 4 were prepared in the same manner as in Example 1 and diluted with tetrachloroethylene to obtain a 0.2wt.% solution of the copolymer. A polyester fabric (tropical) was treated in the same manner as in Example 1 and shower test was conducted. The results were given in Table 4. Examples 18 to 24 and Comparison Examples 10 to 12 Five or less kinds of the monomers listed in Table 5 were placed into a 100-cc flask in a prescribed amount (total in 20g). Thereto were added 4g of ethylene glycol, 16g of acetone, 40g of water, 3g of nonionic emulsifier (Nonion HS 220, a product of Nippon Oil & Fats Co., Ltd.) and 3g of cationic emulsifier (Cation AB, a product of Nipoon Oil & Fats Co., Ltd.). The flask was provided with a thermometer, nitrogen purge tube, stirrer and condenser and the mixture was copolymerized with addition of 0.2g of V-50 (catalyst, hydrochloride of azobisisobutyronitrile) at 60°C for 3 hours with stirring while purging with nitrogen. The resulting copolymer latex was diluted with water to obtain a 0.2wt.% solution of the copolymer. A polyester fabric (tropical) was dipped in the above diluted solution, squeezed by a mangle and treated at 120°C for 3 minutes. Table 5 shows oil and water repellency and dry-cleaning property of the treated fabric.

Claims: A copolymer comprising 50 to 90% by weight of the constituting units derived from (a) a polymerizable compound having a perfluoroalkyl group of 4 to 20 carbon atoms, 10 to 50% by weight of the constituting units derived from (b) cyclohexyl or benzyl ester of acrylic acid or methacrylic acid and 0.1 to 10% by weight of the constituting units derived from (c) polyethylene glycol diacrylate of the formula CH₂=CRCOO(CH₂CH₂O)rCOCR=CH₂ wherein R is hydrogen or methyl, r is an integer of 1 to 50, and, optionally, N-methylolacrylamide. A copolymer as defined in claim 1 wherein the polymerizable compound (a) having a perfluoroalkyl group is at least one compound selected from the following compounds: wherein Rf is a perfluoroalkyl group of 4 to 20 carbon atoms, R¹ is a hydrogen atom or alkyl group of 1 to 10 carbon atoms, R² is an alkylene group of 1 to 10 carbon atoms, R³ is a hydrogen atom or methyl group, R⁴ is an alkyl group of 1 to 17 carbon atoms, n is 1 to 10, and m is 0 to 10. An oil and water repellent composition which contains a copolymer of claim 1. An oil and water repellent composition which contains a copolymer of claim 2. An oil and water repellent composition as defined in claims 3 or 4 which further contains an organic solvent. An oil and water repellent composition as defined in any one of claims 3 to 5 which further contains a propellant.

Inventors: AMIMOTO, YOSHIO, ENOMOTO, TAKASHI, HAYASHI, KAZUNORI, SHINJO, MASAYOSHI
Applicants: DAIKIN INDUSTRIES, LIMITED
Application year: 1987
Main classification: C08F220
IPC codes: D06M15, C08F220