NOVEL SILOXANYL ACRYLIC MONOMER AND GAS-PERMEABLE CONTACT LENSES MADE THEREFROM

Abstract: A novel monomer, and oxygen-permeable copolymers made therefrom, as well as contact lenses made from said copolymers, wherein the novel monomer has formula (3).

Description: -I- NOVEL SILOXANYL ACRYLIC MONOMER AND GAS-PERMEABLE CONTACT LENSES MADE THEREFROM The present invention relates to a novel siloxane- acrylic monomer, to polymers made therefrom, and to contact lenses made from said polymers. U.S. Patent No. 4,314,068 discloses oxygen- permeable contact lenses made from a copolymer including a first comonomer with the following general formula (1) : wherein R is selected from the group consisting of lower alkyl groups and hydrogen; n is an integer from about 1-3; X and Y are selected from the class consisting of lower alkyl groups, cycloalkyl groups, phenyl groups (substituted or unsubstituted) , polysiloxanyl groups, fluorine and Z groups, Z is a group of the structure - O-Si(OSi(A) _) _; and wherein A is selected from the group consiting of lower alkyl " groups and phenyl groups; a second comonomer which is an alkyl or' cycloalkyl acrylate or methacrylate; a wetting component which can be acrylic or methacrylic acid, N-vinyl 2-pyrrolidone, or a hydroxyalkyl ester of acrylic or methacrylic acid; and a cross-linking agent such as an alk lene glycol dimethacrylate. U.S. Patent No. 4,152,508 discloses a silicone- containing hard contact lens material containing a first monomer having the formula (2) : A I R - ( O ) d- CH 2 (2) ( 0-Si^- c R 3 A wherein R 1 is hydrogen or methyl, a is an integer from 1-3, b and c are integers from 0-2, d is 0 or 1, A is methyl or phenyl, R 2 is methyl or phenyl, and R_ and R. represent either no group or methyl or phenyl groups; a second comonomer comprising an itaconate ester; a fracture strength adding material which is an ester of a C.-C_ n monohydric or polyhydric alkanol, or phenol, and acrylic or methacrylic acid; a hydrophilic neutral, cationic or anionic monomer or ester thereof; and a cross-linking agent. The present invention is characterized by a Si-O-C linkage which is expressly discouraged in U.S. Patent No. 4,259,467, column 2, in the context of siloxanyl-di-acrylic compounds. This teaching in the '467 patent confirms that the superiority of the present invention is unexpected. The present invention relates to a novel compound having the following formula (3) : wherein each X is independently a straight or branched chain C.-C, alkyl or phenyl group, a is an integer from 1-6, and R is hydrogen or methyl. The present invention further comprises copolymers of a compound (a) according to formula (3); a CJ..-C n 1 0 o-alkyl, cyclo-C 3 -C -alkyl, phenyl or benzyl acrylate or methacrylate; a fluorinated C 1. -C c b alkyl methacrylate or acrylate substituted with at least 3 fluorine atoms; and a cross- linking agent. The present invention further comprises contact lenses made from the above-mentioned copolymer. Another novel aspect of the present invention comprises an ultraviolet-absorbing compound which is a copolymer of 3-(2-benzotriazolyl)-2-hydroxy-5-tert-octyl- benzyl methacrylamide with the monomer of the formula (3) and one or more of the other comonomers described herein. Also, the present invention relates to a compound , useful as an ultraviolet absorber and comprising an addition polymer which is the reaction product of a composition comprising (a) 3-(2-benzotriazolyl)-2-hydroxy-5-tert- octylbenzyl methacrylamide; (b) a compound having the formula: (R)-C(0)-O-(CH2„)a-O-Si-[O-Si(X) 3]3 wherein each X is independently a straight or branched alkyl group containing 1-6 carbon atoms, or phenyl; a is an integer from 1-6; and R is hydrogen or methyl; and (c) a fluorinated C.-C fi alkyl acrylate or methacrylate substituted with at least 3 fluorine atoms, and optionally (d) a C..-C., alkyl or C_-C 0 cycloalkyl acrylate or methacrylate. 6 o The novel copolymers including the compound or the present invention are useful in making contact lenses having many desirable attributes including oxygen permeability, machinability, and capability to exhibit good wettability in finished articles. The novel comonomer imparts these properties to the copolymer and articles made therefrom. In the preferred embodiment of the novel comonomer identified above as formula (3) , each radical X is lower alkyl and more preferably methyl. In an even more preferred embodiment, a equals 1-3 and more preferably 2. The monomer most preferred is tris (trimethylsiloxy) siloxyethyl metacrylate. The novel comonomers of the present invention can be prepared for instance by reaction of tris (trialkylsiloxv) chlorosilane or tris (triphenylsiloxy) chlorosilane with hydroxyalkyl acrylate or hydroxyalkyl methacrylate in an inert solvent. A more detailed description of the preparation of the preferred comonomer is given below. Representative second comonomers useful in making the useful copolymers of the present invention include the following: methylmethacrylate (preferred) ; ethylmethacrylate; ethylacrylate; or propyl, isopropyl, butyl, sec-butyl, pentyl, hexyl, heptyl, octyl, 2-ethyl hexyl, nonyl, decyl, undecyl, dodecyl, lauryl, cetyl, octadecyl, benzyl, phenyl or cycloalkyl acrylate or methacrylate. The alkyl substituent preferably has 1 to 6 carbon atoms. Representative cycloalkyl groups include cyclopropyl, cyclobutyl, cyclopentyl, cyclohexyl, cycloheptyl, and cyclooctyl. The third comonomer in the useful compolymers of the present invention is a fluorinated or polyfluorinated (C.-C-.) acrylate or methacrylate, preferably one in which up to 8 hydrogen atoms (preferably 3 to 8) are replaced by fluorine atoms. The preferred example is trifluoro ethyl methacrylate (CF 3 -CH 2 -0-C(O)-C(CH_)=CH 2 ) . Other comonomers which would perform the equivalent function include the following : pentafluoropropyl methacrylate, heptafluoro methylmethacrylate, hexafluoro isopropyl methacrylate and similar compounds. The copolymer of the present invention also contains a cross-linking monomer having difunctional reactive sites, such as ethylene glycol dimethacrylate (preferred); diethylene glycol dimethacrylate; triethylene glycol dimethacrylate; tetraethylene glycol dimethacrylate; and other compounds known to those skilled in the art for use in cross-linking compounds of the type referred to herein. The copolymer of the present invention is prepared by mixing together the four components indicated above, preferably in the following ranges: about 30 to about 60 weight percent of the comonomer of formula (3) ; about 5 to about 25 weight percent of the second comonomer; about 15 to about 35 weight percent of the fluorinated comonomer; and about 5 to about 15 percent of the ethylene glycol dimethacrylate or equivalent cross-linking agent. The preferred concentration of the component of formula (3) is 45 to 60 weight percent, and more preferably about 50 weight percent. The preferred concentration of the second comonomer is about 5 to about 20 weight percent, and more preferably about 15 weight percent. The preferred concentration of the trifluoroethyl methacrylate or equivalent comonomer is about 20 to about 35 weight percent, and more preferably about 25 weight percent. The preferred concentration of the cross-linking agent is about 5 to 15 weight percent, more preferably about 10 weight percent. here it is desired that the copolymer's product have the ability to absorb ultraviolet radiation, a small but effecive amount (typically up to about 5 weight percent) of an ultraviolet absorber is mixed together with the other monomers. The preferred copolymeric ultraviolet absorber is a copolymer made by copolymerizmg a monomeric ultraviolet absorber having polymerizable vinylic unsaturation with the same monomers from which the copolymeric product itself is made, thereby facilitating dissolution of the copolymeric ultraviolet absorber into the monomer mixture from which the copolymeric product is made. For instance, a macromolecular product can be formed by copolymerizing a mixture of 20-40 wt% of a UV absorber such as 3-(2-benzotriazolyl)-2-hydroxy- 5-tert-octylbenzyl methacrylamide, 20-40 wt% of a comonomer of formula (3) such as tris (trimethylsiloxy) siloxyethyl methacrylate, and 20-40 wt% of 2,2, -trifluoroethyl meth¬ acrylate, or other fluorinated comonomer as defined herein, and optionally 20-40 wt% of an alkyl or cycloalkyl acrylate or methacrylate as defined above. Free radical copolymerization of the mixture using the initiator, amounts, and reaction conditions disclosed herein for the novel lens polymer, is preferred. An effective amount, preferably about 0.5 to about 2.0 weight, of the ultraviolet absorbing polymer (or another UV absorber such as or about 0.3 to about 1.0 weight percent of 2,2',4, 4*-tetrahydroxy benzophenone, 2,2'- dihydroxy, 4, '-dimethoxy benzophenone or 2,2'-dihydroxy-4- methoxy benzophenone) can be added to impart ultraviolet absorbing ability to the resulting material. The absorber preferably absorbs some or all of the radiation in the range 350-450 nm, or preferably 300-450 nm. The ultraviolet absorber becomes dispersed in the copolymer and is physically entrapped therein, thereby resisting leaching of the absorber from lenses. In making the copolymers of the present invention, a minor but effective amount such as 0.1-0.75 weight percent of a free radical initiator such as tert-butyl peroxyneodecanoate, tert-butyl peroctoate, or tert-butyl perbenzoate is added to the monomer mixture described above. The resulting mixture is then placed in a waterbath, or in an oven under nitrogen atmosphere. The effective polymerization temperature of from about 35°C to about 110°C is maintained for sufficient time, such as 170 hours, to permit the polymerization to proceed to completion. The resulting clear, hard solid can then be relathed to form a rod, which is cut in the conventional way into buttons which are then machined to form contact lenses using known machining techniques. The resultant lenses exhibit the properties described above to a superior degree not heretofore expected. Another aspect of the present invention is the > treatment of lenses made from a copolymer containing one or more siloxanyl moieties of the formula -0SiD..D_D_ wherein D.. , D 2 and D_ are ' indepedently C.-C. alkoxy, C 1 -C- 0 alkyl, a phenyl ring, or another -510-0 2 0- group, pendant from a polymeric backbone of repeating acrylic or methacrylic units to render the copolymer surface more wettable by water or isotonic saline solution. The lens is treated with an acqueous solution of an agent which is a strong acid, or less preferably is a strong base. The agent cleaves siloxanyl groups from the lens surface and leaves hydroxyl groups in their place, thereby increasing the wettability of the lens surface. Suitable agents for increasing the wettability include sodium, potassium and ammonium bisulfate, sulphuric acid, and arylsulfonic acids, such as toluenesulfonic acid. This process increases the wettability of lenses made from the copolymers of the present invention. It is also useful with lenses containing pendant siloxyanyl moieties derived from any of the siloxyanyl-acrylic compounds disclosed in any of the following U.S. patents: 4,314,068; 4,152,508; 4,259,467; 3,808,178; 4,120,570; 4,139,513 4,139,692; 4,216,303; 4,246,389; 4,330,383; 4,400,333; 4,410,674; 4,414,375; 4,419,505; 4,424,328; 4,433,125; 4,463,149; 4,500,695; 4,507,452; 4,508,884; 4,535,138, 4,581,184; 4,582,884; and 4,602,074. This process comprises reacting the surface of a lens or other material with an aqueous solution of an effective agent, such as one of those defined above, under conditions of time and temperature effective to replace pendant siloxanyl groups with hydroxyl groups on the surface of the article. Typically, times of 1 to 10 hours are satisfactory, with 2 - 6 hours preferred. Temperatures of typically 40°C - 80°C are effective. Within these parameters, one skilled in this art can readily determine the concentration of the agent of choice which is effective to cause the desired degree of improvement in wetability. In general, higher concentrations require shorter reaction times. The following examples are included for purposes of illustration and should not be considered limiting. - EXAMPLE 1 This example illustrates the synthesis of tri(trimethylsiloxy) siloxyethyl methacr late. 2-Hydroxyethyl methacrylate (315 g) and pyridine (286 g) were placed in a three liter round bottom flask equipped with overhead stirrer, dropping funnel, drying tube, and thermometer. After cooling the flask in an ice-water bath to 12-15°C, tris (trimethylsiloxy)chlorosilane (400 g) was added with stirring over a 60 minute period while maintaining a temperature below 15°C. After the addition was over, the content were stirred for 16 hours at room temperature. Pentane (150 ml) was added to the mixture and pyridinium hydrochloride was filtered out and washed with some more pentane. The entire filtrate was extracted successively with water, 10% aq. acetic acid solution, water, 10% aq. sodium bicarbonate solution, and water. After drying the organic layer over anhydrous magnesium sulfate and filtering, the solvent was removed under reduced pressure. The colorless residual liquid was distilled under vacuum with 300 mm Claisen Vigreux distillation head and with 3% cuprous chloride as inhibitor. The fraction boiling at 87-90°C at about 10 m-torr pressure yielded 385 g (75%) of the title monomer. It was refrigerated until used. EXAMPLE 2 This example illustrates the preparation of a copolymer made with the novel siloxanyl ester of Example 1. A polymerization mixture was prepared by mixing 150 parts of tris (trimethylsiloxy) siloxy ethyl methacrylate (monomer of Example 1) , 15 parts methyl methacrylate, 90 parts 2, 2, 2-trifluoroethylmethacrylate, 45 parts ethylene glycol dimethacrylate, 4.27 parts of a copolymeric UV absorber (made from previously copolymerizing 1.5 parts of 3-(2-benzotriazolyl)-2-hydroxy-5-tert-octylbenzyl methacrylamide with 0.64 parts tris (trimethylsiloxy) siloxy-ethyl methacrylate and 2.13 parts of 2, 2, 2-trifluoroethyl methacrylate in toluene solution with tert-butyl peroxyneodecanoate and tert-butyl peroctoate as organic initiators), 0.018 parts D & C green #6, and organic peroxide initiators, 0.45 parts t-butyl peroxyneodecanoate, 0.45 parts t-butyl peroctoate and 0.45 parts t-butyl perbenzoate. Then the mixture was poured into foot-long high density polyethylene tubes (ID 5/8") , and polymerized under nitrogen blanket. The polymerization was effected by initially heating the tubes at 35°C in a waterbath for 48 hours and then at 45°C for 24 hours. Then these tubes were placed in a forced air oven and heating was continued at 85°C for 24 hours, 100°C for 56 hours and finally at 110°C for 12 hours. The resulting polymeric rods were cut into lens blanks. The lenses obtained by lathing the blanks had excellent mechanical properties and oxygen permeability, DK 82 Barrier units at 35°C. EXAMPLE 3 This example illustrates the preparation of another copolymer made with the novel siloxanyl ester of Example 1. A polymerization mixture was prepared by mixing 60 parts of tris(trimethylsiloxy) siloxy-ethyl methacrylate, 5 parts methylmethacrylate, 25 parts 2, 2, 2'-trifluoroethyl methacrylate, 10 parts ethylene glycol dimethacrylate, 1.42 parts of a copolymeric UV absorber (made by previously copolymerizing 3-(2-benzotriazolyl)-2-hydroxy-5-tert-octyl benzyl methacrylamide with tris (trimethylsiloxy) siloxyethyl methacrylate, and 2, 2, 2-trifluoroethylmethacrylate as described in Example 2), 0.003 parts D & C green #6, and organic peroxide initiators, 0.15 parts t-butyl peroxyneodecanoate, 0.15 parts t-butyl peroctoate and 0.15 parts t-butyl perbenzoate. The mixture was polymerized in foot-long high density polyethylene tubes (ID 5/8") and lenses were prepared as described in Example 2. The lenses obtained had excellent mechanical properties and oxygen permeability, DK 125 Barrier units at 35°C. EXAMPLE 4 This example illustrates one of the methods employed to modify the surface of finished articles to enhance their wetability. The finished lenses made from the copolymer of Example 2 were treated with a 66% solution of ammonium bisulfate in water and heated at 50°C for four hours. The lenses were thereafter rinsed in water, 5% solution of sodium bicarbonate and water successively. Then, these lenses were stored in wetting and soaking solution. The wettability was measured by determining the soak state wetting angle of contact lens material. The wetting angle of 65° (+ 4) for untreated and 30° (± 4 ) for treated material was observed. These reported numbers are the average of ten bubbles measured left and right sides for each of the three disks employed. A lower wetting angle value indicates better wetting characteristics.

Claims: WHAT IS CLAIMED IS: 1. A compound having the formula: R 0 CH 2 >==CC 1 -- 1CC!--00~- (CH 2 ) a -0-Si- [O-Si (X) 3] 3 wherein each X is independently a straight or branched-chain alkyl group containing 1-6 carbon atoms, or phenyl; a is an integer from 1-6; and R is hydrogen or methyl. 2. A compound in accordance with Claim 1 wherein each X is independently a straight or branched-chain alkyl group containing 1-6 carbon atoms. 3. A compound in accordance with Claim 1 or 2 wherein a is 1, 2 or 3. 4. A compound in accordance with Claim 3 wherein each X is methyl and a is 2. 5. A compound in accordance with Claim 1 wherein the compound is tris (trimethylsiloxy) siloxyethyl methacrylate. 6. A hard, oxygen-permeable copolymer comprising an addition polymer which is the reaction product of a composition comprising: (a) a compound in accordance with any of Claims 1 to 5 (b) a C^-C^g-alkyl, cyclo-C 3 -C 8 -alkyl, phenyl or benzyl acrylate or methacrylate; (c) a fluoriήated C,-C fi alkyl methacrylate or acrylate substituted with at least 3 fluorine atoms; and (d) a cross-linking agent. 7. A copolymer in accordance with Claim 6 wherein component (b) is a C--C 8 alkyl acrylate or methacrylate, and component (c) is trifluoroethyl methacrylate. 8. A copolymer in accordance with Claim 6 or 7 wherein component (a) is present in the amount of about 30 to about 60 weight percent; component (b) is present in the amount of about 5 to about 25 weight percent; component (c) is present in the amount of about 15 to about 35 weight percent; and component (d) is present in the amount of about 5 to about 15 weight percent. 9. A copolymer in accordance with any of Claims 6 to 8 which includes an ultraviolet absorbing addition polymer which is the reaction product of 3- (2-benzotriazolyl) -2-hydroxy-5-tert-octylbenzyl methacrylamide, compound (a) , compound (c) and optionally compound (b) . 10. A copolymer in accordance with Claim 9 wherein the ultraviolet absorbing addition polymer is present in an amount sufficient to absorb ultraviolet radiation in a wavelength range of 300-450 nm. 11. A contact lense made from a composition containing the compound or copolymer of any of Claims 1 to 10. 12. A compound useful as an ultraviolet absorber and comprising an addition polymer which is the reaction product of a composition comprising: (a) 3- (2-benzotriazolyl) -2-hydroxy-5-tert-octylbenz methacrylamide; (b) a comopund having the formula CH =C(R) -C (O) -O- (CH.,) -O-Si- [O-Si (X) ] 2 2 a 3 3 wherein each X is independently a straight or branched alkyl group containing 1-6 carbon atoms, or phenyl; a is an integer from 1-6; and R is hydrogen or methyl; and (c) a fluorinated C.-C fi alkyl acrylate or methacrylate substituted with at least 3 fluorine atoms, and optionally (d) a C.-C, alkyl or C--C_ cycloalkyl acrylate or methacrylate. 13. A compound according to Claim 19 wherein in compound (b) each X is methyl; a is 2; and R is methyl. >* 14. A compound according to Claim 19 wherein compound (c) is trifluoroethyl methacrylate. 15. A compound in accordance with Claim 19 which is the reaction product of a composition in which components (a) , (b) , (c) and (d) each comprise 20-40 wt.%. 16. A process for increasing the wettability of the surface of an object made from a homopolymer or copolymer of at least one acrylate or methacrylate monomer having pendant -0SiD-D D 3 groups, wherein D_, D 2 and D are independently C..-D..- alkyl, C.-C- n alkoxy, phenyl, or another -OSiD-D_D_ group, comprising reacting said pendant groups with an agent capable of cleaving said groups, and replacing the cleaved groups by hydroxyl groups. 17. A process according to Claim 16 wherein the cleaving agent is a strong acid or base. 18. A process according to Claim 17 or 18 wherein the cleaving agent is an aqueous solution of sulphuric acid, toluenesulfonic acid, sodium, potassium or ammonium bisulfate. 19. The process of Claim 16 wherein said object is a contact lens.

Inventors: KULKARNI CHIDAMBAR L, LIM DRAHOSLAV, KULKARNI, CHIDAMBAR, L., LIM, DRAHOSLAV
Applicants: BARNES HIND INC, BARNES-HIND, INC.
Application year: 1987
Main classification: C07F7
IPC codes: C07F7, C08F20, C08F30, G02B1, G02C7