CARRIER LATEX FOR DIAGNOSTIC REAGENT

Abstract: Carrier latex for use in diagnostic reagents consists of a suspension of particles of a copolymer of ethylene and an alpha,beta-ethylenically unsaturated carboxylic acid (or its salt) grafted with an aromatic vinyl cpd., bearing carboxyl groups on the particle surface. Pref. the copolymer contains 65-98% ethylene (by wt.) and 35-2% unsatd. acid, grafted with 1-9 pts. vinyl cpd. per 1 pt. unsatd. acid. The particle size is pref. 0.05-1 microns and the particles pref. bear 0.01-0.3 meq/g carboxyl gps. on their surface. The unsatd. acid is acrylic, methacrylic, itaconic, maleic and/or fumaric acid, or their Na, K, Mg, Ca, Ba or Zn salts. The aromatic vinyl cpd. is styrene, alpha-methylstyrene, vinyltoluene or ethylstyrene. The melt flow rate of the grafted copolymer (190 deg.C/2.16 kg) is 50-700 g/10 min..

Description: This invention relates to a carrier latex for use as a diagnostic reagent which can be used in immuno-serological diagnosis utilizing an antigen-antibody reaction while minimizing nonspecific agglutination. Immuno-serological diagnosis is carried out by sensitizing a carrier latex with a serologically active material such as an antigen or antibody, combining the serum to be tested with the latex, and allowing agglutination to take place in the latex, resulting in the detection of the presence of the corresponding antibody or antigen in the serum. Because of its ease and quickness, the immuno-serological diagnosis is widely applied to reagents in the clinical examination art in order to detect a variety of antigens or antibodies. For this type of diagnostic reagent, carriers to be sensitized with an antigen or antibody are generally formed of resin latices, for example, latices of polystyrene and styrene-butadiene copolymers. These resin latices are required to form a stable emulsion, not to agglutinate during sensitization with an antigen or antibody, and not to agglutinate upon contact with a negative serum when the latices are observed for agglutination by reacting with an antibody or antigen which corresponds to the sensitizing antigen or antibody, that is, to be free of nonspecific agglutination. Presently, not only qualitative, but also quantitative determination of trace amounts of a material such as antigen or antibody are crucial in the field of immuno-serological diagnostic examination. A prior art practice is the qualitative detection of a subject material being tested which is carried out by mixing and reacting a sensitized latex with the subject material to be tested on a glass plate and visually observing the agglutination of the particles in the latex. Numerous attempts have been made to achieve quantitative detection by a measurement using an optical instrument such as a spectrophotometer, turbidimeter, and quasi-elastic scattered light meter instead of the visual observation of agglutination. A method of detecting a reduction in tubidity of supernatant by utilizing the phenomenon that particles agglutinate in the sensitized latex, and a method of measuring a variation of absorbance or scattered light due to agglutination of particles in the sensitized latex, are known. See CROATICA CHEMICAACTA, 42 , 457 (1970), Immunochemistry, 12 , 349 (1975), and Japanese Patent Application Kokai Nos. 53-24015 and 54-109494. These methods achieve quantitative measurement by determining the variation of the optical properties, such as absorbance and scattered light intensity, of a reaction system due to the immuno-serological agglutination of particles in a sensitized latex. However, these methods are not sufficiently accurate and are not capable of consistent reproduction because only a small variation occurs in the optical properties of a reaction system due to the agglutination. Further, quite often the optical properties of a sensitized latex will change with time, which creates a problem for obtaining a practical measurement. A latex may be sensitized with an antigen or antibody either by physical adsorption or by chemical bonding. Because an adsorption-dissociation equilibrium does exist between the latex and the antigen or antibody with which the latex is sensitized, a commonly used sensitization method based on physical adsorption would have the drawback that there is the possibility of the antigen or antibody dissociating from the latex during measurement or storage. It is, therefore, an object of the present invention to provide a carrier latex for use as a diagnostic reagent which is free from the above-mentioned problems of conventional diagnostic reagent carrier latices, and can be used in an immuno-serological diagnostic test utilizing an antigen-antibody reaction while experiencing minimized nonspecific agglutination reaction. Another object is to provide a carrier latex which is suitable for the optical measurement of absorbence and scattered light intensity. According to the invention there is provided a carrier latex comprising a suspension of particles of a copolymer of 65 to 98 wt% ethylene, and 2 to 35 wt% of a C₃ to C₅ α,β-ethylenically unsaturated carboxylic acid and/or a salt thereof, said copolymer containing graft units of, as styrene compound, styrene optionally substituted by a methyl or ethyl group in a proportion of 100 to 900 parts by weight of the styrene compound to 100 parts by weight of the copolymer. The carboxyl group on the surface of the suspended particles preferably ranges from 0.01 to 0.3 meq/g (meg/gram) based on the weight of the particles. The suspended particles preferably have an average particle size of from 0.05 to 1 µm and a specific gravity of at least 1. The latex preferably has a solid content of from 5 to 45% by weight. Preferably, the α,β-ethylenically unsaturated carboxylic acid is at least one of acrylic acid, methacrylic acid, itaconic acid, maleic acid, and fumaric acid and the salt is at least one metal salt selected from a sodium salt, a potassium salt, a magnesium salt, a calcium salt, a barium salt, and a zinc salt of these carboxylic acids. The styrene compound to be grafted is suitably at least one of styrene, α-methylstyrene, vinyltoluene and ethylstyrene, and is grafted in a proportion of from 100 to 900 parts by weight per 100 parts by weight of the copolymer, and the copolymer to which the styrene compound is to be grafted suitably has a melt flow rate of 50 to 700 g(grams)/10 min as measured at 190°C under a load of 2.16 kg. FIG. 1 illustrates the scattered light intensity associated with the agglutination reaction of the carrier latices which are prepared in Example 1 as sample Nos. 1 to 5 and Comparative Example 1 and are sensitized with an anti-AFP antibody, as a function of antigen concentration. The α,β-ethylenically unsaturated carboxylic acids or carboxylates encompass α,β-ethylenically unsaturated carboxylic acids or their salts, or mixtures thereof. Their examples include such α,β-ethylenically unsaturated carboxylic acids as acrylic, methacrylic, itaconic, maleic, and fumaric acid, and metal salts thereof such as sodium, potassium, magnesium, calcium, barium, and zinc salts of these carboxylic acids. Of these acids and salts, methacrylic acid and its salts are preferred. The copolymers may also be fully or partially neutralized products of the copolymer of ethylene and an α,β-ethylenically unsaturated carboxylic acid, a salt of an α,β-ethylenically unsaturated carboxylic acid or a mixture thereof. Prior to grafting the copolymers generally have a melt flow rate of from 50 to 700 g(grams)/10 min, preferably from 100 to 600 g(grams)/10 min as measured at 190°C under a load of 2.16 kg. In the suspension of the copolymer prior to grafting of the styrene compound thereto, the copolymer particles generally have an average particle size of from 0.03 to 1 µm, preferably from 0.04 to 0.8 µm. The proportion of the styrene compound generally ranges from 100 to 900 parts by weight, preferably from 200 to 800 parts by weight per 100 parts by weight of the copolymer. Examples of the styrene compound include styrene, α-methylstyrene, vinyltoluene and ethylstyrene. In the carrier latex for use as a diagnostic reagent, the suspended particles generally have an average particle size of from 0.05 to 1 µm, preferably from 0.1 to 0.3 µm, with a narrower particle size distribution being preferred. The carrier latex for use as a diagnostic reagent generally has a solid content of from 5 to 45% by weight, preferably from 10 to 35% by weight. Since the carrier latex is often subjected to centrifugal separation in a subsequent sensitizing step or sensitized latex separating step, the suspended particles in the carrier latex may generally have a specific gravity of at least 1, preferably from 1.0 to 1.1. The suspended particles of the carrier latex for use as a diagnostic reagent of the present invention have attached on the surface a carboxyl group capable of chemically bonding an immuno-serologically active material such as an antigen or antibody. The amount of carboxyl group present on the particle surface generally ranges from 0.01 to 0.3 meq/g (meq/gram) based on the weight of the particles, preferably from 0.02 to 0.1 meq/g (meg/gram) based on the weight of the particles. The latex tends to give rise to nonspecific agglutination with a lesser carboxyl group content whereas the latex tends to reduce its agglutination reactivity and hence, its sensitivity with a larger carboxyl group content. The amount of carboxyl group present on the surface of suspended particles of the carrier latex may be determined by the measurement method developed by Johnhen. See Journal of Colloid and Interface Science, 49 , 425 (1974). The preparation of the carrier latex for use as a diagnostic reagent according to the present invention will be described. The carrier latex may be prepared, for example, by combining a suspension of a copolymer of ethylene and an α,β-ethylenically unsaturated carboxylic acid, a salt of an α,β-ethylenically unsaturated carboxylic acid or a mixture thereof, a styrene compound in an amount of 100 to 900 parts per 100 parts by weight of the solids of the suspension, and water at a temperature of from 50 to 100°C, adding an aqueous persulfate solution to the mixture, and allowing graft polymerization to proceed for 1 to 6 hours. The persulfates include ammonium persulfate, sodium persulfate, and potassium persulfate, and may be used in an amount of 0.1 to 5% by weight based on the weight of the aromatic vinyl compound. The polymerization temperature preferably ranges from 50 to 100°C, more preferably from 70 to 90°C. At the end of the polymerization, vacuum distillation may be carried out to remove the unreacted monomer and/or the product may be diluted or concentrated to control the concentration. The carrier latex for use as a diagnostic reagent of the present invention may be sensitized or chemically bonded with an immuno-serologically active material such as an antigen or antibody by any known prior art method. Examples of the present invention are given below by way of illustration and not by way of limitation. The following methods were employed to carry out sensitization of a latex with an antibody and measurement of the agglutination sensitivity of the sensitized latex. (1) Latex sensitization Preparation of anti-AFP latex reagent A resin latex is suspended in a phosphate buffer solution to obtain 0.25 ml of a suspension having a solid concentration of 5%. To the suspension are added 1 mg of an IgG fraction prepared from anti-AFP (alpha-fetoprotein) rabbit serum and 5 mg of water-soluble carbodiimide. The mixture is adjusted to pH 5 and stirred for one hour under ice cooling to chemically bond IgG to the latex surface. Then the reaction mixture is combined with glycine, adjusted to pH 8, centrifuged at 20,000 rpm for 30 minutes, removed of the supernatant, and dispersed again in a glycine buffer solution (pH 8.2) containing 3% by weight of human serum albumin, obtaining a sensitized latex having a solid concentration of 0.1%. (2) Measurement of agglutination sensitivity The sensitized latex, 50 µl, is diluted with 150 µl of a glycine buffer solution (pH 8.2) containing 1% by weight of bovine serum albumin, combined with 10 µl of a sample containing a predetermined concentration of AFP, stirred for mixing, and allowed to react for 30 minutes at room temperature. The scattered light intensity of the mixture is measured by a scattered light measuring meter to determine the relation of scattered light intensity to AFP concentration. Example 1 Preparation of ionomer dispersion A solution was prepared by heating 100 grams of an ethylene-methacrylic acid copolymer containing 10% by weight of methacrylic acid in 330 grams of toluene and 220 grams of isopropyl alcohol to 75°C. The solution was added to 250 grams of distilled water containing 0.78 grams of sodium hydroxide in a homomixer and agitated for 10 to 20 minutes. The toluene and isopropyl alcohol were removed from the suspension under vacuum to adjust the solid concentration to 30%. Dispersions having different particle sizes were obtained by varying the polymer concentration of the oily layer and the weight ratio of toluene to isopropyl alcohol as shown in Table 1. Styrene graft polymerization of ionomer dispersion A mixture of the above-prepared ionomer dispersion, styrene, and distilled water in the proportion shown in Table 2 was heated at 80°C, combined with 50 grams of distilled water containing potassium persulfate, and stirred for 2 hours at 80°C for polymerization. The resulting polymer particle latex was subjected to vacuum distillation to remove the unreacted styrene. The average particle size and surface carboxyl group content of the polymer particles are also shown in Table 2. Sample Nos. of Example 1 1 2 3 4 5 Ionomer dispersion (type) A A A B C (gram) 67 100 133 100 100 Styrene (gram) 80 70 60 70 70 Distilled water (gram) 103 80 57 80 80 Potassium persulfate(gram) 0.4 0.35 0.3 0.35 0.35 Average particle size (µm) 0.19 0.18 0.17 0.12 0.26 Surface carboxyl group content (meq/g) 0.04 0.06 0.08 0.07 0.05 Comparative Example 1 Preparation of styrene-methacrylic acid copolymer particle latex Distilled water, 150 grams, was heated to 80°C with stirring. Then a mixture of 98 grams of styrene and 2 grams of methacrylic acid and 50 grams of distilled water containing 0.5 grams of potassium persulfate were simultaneously and continuously added to the water over a period of 10 hours. At the end of addition, the mixture was stirred for a further 2 hours to complete polymerization. The resulting polymer particle latex was subjected to vacuum distillation to remove the unreacted monomers. The resulting polymer particles had an average particle size of 0.20 µm and a surface carboxyl group content of 0.06 meq/g. The carrier latices prepared in Example 1 and Comparative Example 1 were sensitized with an anti-AFP antibody according to the above-described latex sensitizing procedure (1) to produce sensitized latices, which were measured for agglutination sensitivity according to the above-described agglutination sensitivity measuring procedure (2). The results are shown in FIG. 1. As evident from FIG. 1, the sensitized latices using latex sample Nos. 1 to 5 of Example 1 exhibit a marked change in scattered light intensity with the AFP concentration. In contrast, the sensitized latex using the latex of Comparative Example 1 exhibits a less change in scattered light intensity with the AFP concentration. INDUSTRIAL APPLICABILITY A carrier latex ready for use as diagnostic reagent which is prepared from a diagnostic reagent carrier latex according to the present invention, that is, sensitized latex exhibits minimized nonspecific agglutination and high sensitivity to specific agglutination, and is thus optimum for use in a diagnostic system based on optical measurement.

Claims: A carrier latex comprising a suspension of particles of a copolymer of 65 to 98 wt% ethylene, and 2 to 35 wt% of a C₃ to C₅ α,β-ethylenically unsaturated carboxylic acid and/or a salt thereof, said copolymer containing graft units of, as styrene compound, styrene optionally substituted by a methyl or ethyl group in a proportion of 100 to 900 parts by weight of the styrene compound to 100 parts by weight of the copolymer. A carrier latex according to claim 1, wherein the carboxyl group on the surface of said suspended particles ranges from 0.01 to 0.3 meq/g based on the weight of the particles. A carrier latex according to claim 1 or 2, wherein said suspended particles have an average particle size of from 0.05 to 1 µm. A carrier latex according to claim 1, 2 or 3, wherein said latex has a solid content of from 5 to 45% by weight. A carrier latex according to any one of the preceding claims, wherein the particles suspended in said latex have a specific gravity of at least 1. A carrier latex according to any one of the preceding claims, wherein said carboxylic acid is at least one of acrylic acid, methacrylic acid, itaconic acid, maleic acid and fumaric acid, and said salt is at least one metal salt selected from a sodium salt, a potassium salt, a magnesium salt, a calcium salt, a barium salt and a zinc salt. A carrier latex according to any one of the preceding claims, wherein said copolymer, prior to grafting of the styrene compound, has a melt flow rate of 50 to 700 g/10 min as measured at 190°C under a load of 2.16 kg. A carrier latex according to any one of the preceding claims, wherein the styrene compound to be grafted is at least one of styrene, α-methylstyrene, vinyltoluene and ethylstyrene. A carrier latex according to any one of the preceding claims, wherein the proportion of the styrene compound is 200 to 800 parts by weight per 100 parts by weight of said copolymer. Use of a carrier latex as claimed in any one of the preceding claims as a diagnostic reagent.

Inventors: NISHIKAWA, HIROSHI, OHDAIRA, AKIO
Applicants: MITSUI PETROCHEMICAL INDUSTRIES, LTD.
Application year: 1987
Main classification: G01N33
IPC codes: C08F255, G01N33