A PROCESS FOR THE PHOTOCATALYTIC DECOMPOSITION OF WATER INTO HYDROGEN AND OXYGEN

Abstract: Hydrogen and oxygen are obtained by the photocatalytic decomposition of water by passing light in an inert atmosphere through an aqueous solution of dioxygen complex of rhuthenium and EDTA (ethylene diamine tetra acetic acid) in which is suspended a semiconductor of hexagonal crystal structure loaded with a nobel metal and a transition metal oxide. Hydrogen and oxygen are known to have various uses. Precipitation of the semiconductor material and annealing it at a temperature from 300-350°C result in the semiconductor of hexagonal structure which is suspended in the aqueous solution.

Description: The present invention relates to the photocatlytic decomposition of water into hydrogen and oxygen and to the production of a semiconductor therefor. Hydrogen is one of the products of this invention which is simultaneously produced with oxygen and this has never been achieved before. Uses of these products are very well known. For example, hydrogen is used for the hydrogenation of essential oils, in fuel cells and is also considered to be the fuel of the future on depletion of fossil fuel whereas oxygen, apart from it being an important element for the survival of living beings, has multifarious uses includidng oxidation reactions. At present, hydrogen is produced by the electrolysis of water but this is a slow process and consumes electrical energy. Gratzel et al reported the production of hydrogen from water but the biggest drawback in this system has been that it uses EDTA (Ethylene diamine tetraacetic acid) as a sacrificial electron donor and is consumed in the system. Not only is the photodecomposition system incomplete but it also does not produce oxygen. In this process, the CdS semiconductor is light absorbing species. On illumination it absorbs light and this light energy is utilised to transfer an electron from the valence band of the semiconductor to the conduction band. The transfer of electron from the valence band to the conduction band leaves a positive charge in the valence band. The electron of the conduction band is transferred to water via Pt giving hydrogen. The hole in the valence band receives an electron from EDTA (Ethylene diamine tetra-acetic acid) dissolved in water through RuO₂ filling the gap which was created by jump of the electron to the conduction band. This cycle continues as long as the system is illuminated and the EDTA in solution decomposes. So the EDTA acts as the sacrificial electron donor and hydrogen is produced at the cost of EDTA. Nitrogen is used to create inert atmosphere in the cell. The following are the drawbacks in the known system: (a) It is not a complete cycle for photodecomposition of water and only hydrogen is produced and no oxygen. (b) The hydrogen is generated at the cost of EDTA. (c) Yield of hydrogen is very low. All the aforesaid drawbacks have been overcome by the process according to the present invention which, being the cheapest, not only produces hydrogen but also oxygen using solar energy without, however, consuming fossil fuel, EDTA or electrical energy. The process is a completely free photocatalytic photodecomposition of water where nothing is consumed except water and solar energy. The ideal method which we have developed for obtaining hydrogen from water has to be the simultaneous oxidation and reduction of water in which the water itself acts as an electron donor and gives oxygen on the one hand and on the other it (water) acts as an electron receiver where it gets reduced to give hydrogen and the energy consumed is Solar energy. The main object of the present invention is to provide a process for the photodecomposition of water to get hydrogen and oxygen using solar energy. Another object of the invention is to provide a method for the production of a semi-conductor. It is observed that when colloidal semiconductor loaded with noble metal and the transition metal oxide suspended in aqueous solution of dioxygen complex of Ru-EDTA is subject to solar illumination, the electrons and positive charge are created in the semiconductor. The electron in the conduction band of the semiconductor is received by water through noble metal producing hydrogen and OH⁻ ions according to the following equations: The electron goes to the conduction band and a positive charge is left in the valence band. This valence band receives electrons from the peroxoy species of dioxygen complex and the vacancy created i.e. hole, by electron group by illumination is filled again. The peroxocomplex after giving electron to the positive charge gets converted to superoxo species. The superoxo species of dioxygen complex receives electron from OH⁻ resulting in the process liberating oxygen and gets converted back to peroxo species. The same cycle is repeated and H₂ and O₂ are generated from water. The following are the equations : "M" is a metal which can be Ruthenium and L can be Ethylene diamine tetra-acetic acid (EDTA), Hydroxyl ethyl ethylenediamine tetra-acetic acid (HEDTA), Cyclohexane diamine tetra-acetic acid (CDTA), or 1,2-diaminopropane N,N,N′,N′-tetra-acetic acid (PDTA) The CdS may be replaced by ZnS, Cd Zn x S wherein x is a numeral which can be operated in visible light and TiO₂, BaTiO₃ which can be operated under ultraviolet light. An aqueous solution of dioxygen complex is kept in a pyrex cell. The semiconductor loaded with noble metal and transition metal oxides is suspended in this solution and light is passed through the system under inert atmosphere. The semiconductor employed may be CdS, ZnS, Cd x Zn x S or CdS doped with Ag₂S, TiO₂ or BaTiO₃. The noble metal employed may be Pt, Rh, Ir,. The dioxygen complex may be of the type [{ Ru (L) (OH)₂ } O₂] where L may be EDTA, HEDTA, CDTA or PDTA. The light used is solar light which can be visible if CdS, ZnS, Cd x Zn x S or CdS doped Ag₂S is used and can be ultraviolet if TiO₂ or BaTiO₃ are used. The inert gas employed may be Nitrogen or Argon. The pyrex cell has an inlet to pass inert gas and an outlet from where hydrogen and oxygen are collected. The semiconductor acts as light absorbing species. The noble metal acts as electron transferring catalyst while the RuO₂ acts as the positive charge scavanger where the dioxygen complex acts as electron relay between the OH ions and semiconductor. The system under illumination produces H₂ and O₂ in course of time. The CdS, ZnS or Cd x Zn x S available in the market will not work. Only hexagonal crystal structure of semiconductor is suitable which is obtained by precipitation of the semiconductor eg CdS, and annealing it at temperatures ranging from 300°C - 500°C. The complex [{ Ru (L) (OH)₂} O₂] K is prepared at a specific pH which should not be either highly acidic or basic pH. The addition of noble metal directly to semiconductor is not effective in the production of H₂ and O₂ from water under illumination even if all the other contents are added in the system. Thus, the following procedure is adopted in the production and loading of the semiconductor according to the invention. (1) Preparation of [{Ru (L) (OH)₂} O₂]K This complex is prepared by first preparing Ru (EDTA) Cl K. The complex K₂RuCl₅(H₂O) is dissolved in a minimum amount of HClO₄ (dilute) and added to a hot solution of Na₂(H₂EDTA) dissolved in the requisite volume of HClO₄. The mixture is refluxed for two hours. The light yellow solution is filtered and filtrate is evaporated to a small volume on a water bath and treated with ethanol and cooled overnight. The light yellow complex is washed with a cooled mixture of acetone and water preferably 9:10, till it is free from chloride ion. It is dried in a desicator. This yellow complex is dissolved in water and pH of the solution is adjusted to 6.5 to 8.0 by addition of NaOH. Oxygen gas is passed through this solution for half an hour. The yellow solution turns to green indicating the formation of [{Ru (L) (OH)₂} O₂] K complex. (2) Preparation of Semiconductor 1 litre of concentrated solution of Cd(CH₃COO)₂.2H₂O or Zn(CH₃COO)₂.2H₂O and 1 litre of concentrated solution of (NH₄)₂S are thoroughly mixed together by a magnetic stirrer at room temperature. The stirred suspension is brought to boiling point for about 10 minutes. The suspension is allowed to settle for about 24 hours and is subsequently decanted. The precipitate is collected by filtration and dried. (3) Loading Rh on Semiconductor An aqueous solution of RhCl₃. 3H₂O is added to a suspension of semiconductor and the mixture is stirred for about 30 minutes whereafter the mixture is irradiated in a pyrex cell. The mixture is stored preferably for about 5 hours. The suspended solid becomes yellowish grey during photochemical deposition. The catalyst is centrifuged and dried under vacuum at room temperature. (4) Platinum Loading on Semiconductor Requisite quantity of semiconductor powder is added to a dilute acetic acid solution inferred at pH 4.5 containing 6 gms of H₂PtCl₆.xH₂O and 5 ml of 5% Cd(NO₃)₂.4H₂O solution. After ultrasonic stirring the resultant suspension is introduced into a pyrex cell. At a constant temperature the vigorously stirred suspension is deaerated with argon for about 30 minutes and subsequently irradiated for about 30-60 minutes. The photocatalyst is then filtered and dried at about 60°C. Loading RuO₂ on Semiconductor Loading of RuO₂ on semiconductor/noble metal is carried out by dispersing requisite quantity of loaded semiconductor with noble metal in solution of dilute RuO₄. The dispersion was illuminated with visible light for about 30-60 minutes to bring out decomposition of RuO₄. RuO₄-----------RuO₂ + O₂ The resultant RuO₂ precipitates as ultrafine layer into loaded semiconductor. The hydrogen and oxygen are produced for 60 hrs when the sytem was illuminated with visible light. The loaded semiconductor and the dioxygen complex is recovered after 60 hrs of operation. According to the present invention there is provided a process for the photocatalytic decomposition of water into hydrogen and oxygen which comprises loading a semiconductor having a hexagonal crystal structure, with a noble metal and a transition metal oxide, suspending the loaded semiconductor in an aqueous solution of dioxygen complex of rhuthenium passing light under inert atmosphere and separating the hydrogen and oxygen so formed. The invention will now be illustrated by the following Examples but are not be construed as a limitation to the scope of the invention. Example -1 50 mg of loaded semiconductor with noble metal and RuO₂ is suspended in 25 ml solution of peroxospecies of dioxygen complex in a pyrex cell. The pH of the solution is maintained at which dioxygen complex is stable. The suspension is magnetically stirred and inert gas like argon or nitrogen is passed for 1/2 an hour. The cell is illuminated by visible light of 505 nm with intensity of 70 mw/cm. The hydrogen and oxygen generated in the course of time is measured using manometer and analysed by gas chromatograph. Example -2 50 mg of CdS/Rh/RuO₂ is suspended in 25 ml solution of [{Ru (EDTA) (OH)₂{O₂] K (0.1m)² in a pyrex cell. The pH of the solution is maintained at 7.6 by addition of 0.1 M NaOH. The suspension is stirred and illuminated after passing N₂ gas for 1/2 an hour. The hydrogen and oxygen generated and the results of H₂ and O₂ are shown in Fig.1(a) and Fig.2(a) of the drawings accompanying this specification. Example -3 50 mg of CdS/Pt/RuO₂ was suspended in 25-30 ml solution of [ { Ru (EDTA) (OH)₂{O₂] K in a pyrex cell at pH 7.6. The suspension was stirred and nitrogen was passed for 1/2 an hour. The cell when illuminated gave hydrogen and Oxygen and the results are shown in Fig.1(b) and Fig.2(b) of the drawings. Example -4 This experiment was done similar to examples 1 and 2 except that CdS was loaded with Ir. 50 mg CdS/Ir/RuO₂ was suspended in solution of dioxygen complex and irradiated at pH 7.6 - 8.00. The results are shown in Fig.1(c) of the drawings.

Claims: A process for the photocatalytic decomposition of water into hydrogen and oxygen which comprises loading a semiconductor with a noble metal and a transition metal oxide, suspending the loaded semiconductor in an aqueous solution of dioxygen complex of rhuthenium, passing light under inert atmosphere and separating the hydrogen and oxygen so formed, said semiconductor having been prepared by precipitating the semiconductor material and annealing it at a temperature ranging from 300-350°C so that it has a hexagonal crystal structure, A process as claimed in claim 1 wherein the dioxygen complex of rhuthenium is of the type [{Ru (L) (OH)₂} O₂] wherein L is selected from EDTA, HEDTA, CDTA and PDTA. A process as claimed in any of the preceding claims wherein the semiconductor material employed is selected from CdS, ZnS, Cd x Zn x S wherein x is a numeral and CdS doped with Ag₂S or Tio₂, BaTiO₃. A process is claimed in any of the preceding claims wherein the noble metal is selected from Pt, Rh, Ir. A process as claimed in any of the preceding claims wherein the transition metal oxide is selected from RuO₂ and osmium tetraoxide. A process as claimed in any of the preceding claims wherein the complex has been prepared by first preparing [{ Ru (L) (OH)₂} O₂] K by dissolving complex K₂ Ru Cl₅ (H₂O) in minimum amount of HClO₄ (dilute) and adding to hot solution of Na₂ (H₂L) dissolved in HClO₄, refluxing the mixture, filtering and heating the filtrate with ethanol and adjusting the pH to 7.5 to 8.0 and passing oxygen. A process as claimed in any of the preceding claims wherein the loading of rhuthenium to the semiconductor is done by stirring the mixture and thereafter irradiating in a pyrex cell. A process as claimed in any of the preceding claims wherein the light used is solar light. A process as claimed in claim 8 wherein the solar light is visible when the semiconductor material CdS, ZnS, Cd x Zn x S and CdS is doped with Ag₂S. A process as claimed in any of claims 1-7 wherein the light is ultraviolet light when the semiconductor material is doped with TiO₂ or BaTiO₃. A process as claimed in any of the preceding claims wherein the inert atmosphere is created by nitrogen or argon.

Inventors: BHARDWAJ, CHHAYA, BHARDWAJ, RAMESH CHANDRA, KHAN, MIZRA MOHAMMAD TAQUI
Applicants: COUNCIL OF SCIENTIFIC AND INDUSTRIAL RESEARCH
Application year: 1987
Main classification: C01B3
IPC codes: C01B3