Process for producing novel block copolymers

Abstract: The present invention is a novel class of block copolymers and a process of making the same. An alkylene oxide is reacted with CO₂ in an organic solvent in the presence of an organometallic catalyst to form a polyalkylene carbonate. A second alkylene oxide is subsequently added without the addition of catalyst. The resulting product is a block copolymer comprising distinct, covalently linked, alkylene carbonate blocks.

Description: TECHNICAL FIELD OF THE INVENTION The present invention relates to the production of block copolymers comprising covalently linked alkylene carbonate blocks. BACKGROUND OF THE INVENTION Inoue, U.S. Patent 3,585,168 teaches a process for producing a high molecular weight polycarbonate by copolymerizing an epoxide, such as propylene oxide, ethylene oxide, styrene oxide, isobutylene oxide or epichlorohydrin with carbon dioxide. The process is carried out under carbon dioxide gas pressure in the presence of an organometallic compound catalyst. The polycarbonates formed by this process are made of substantially the same mole ratio of carbon dioxide and epoxide and have a molecular weight between 10,000 and 200,000. U.S. Patent 3,900,424 discloses a catalyst composition, and method of preparing said composition, for use in preparing copolymers of epoxy compounds with carbon dioxide. The catalyst composition comprises the reaction product of an organometallic compound, a co-catalyst component which is sulfur or a compound containing active hydrogen atoms and carbon dioxide. U.S. Patent 3,953,383 teaches a process for producing a copolymer of an epoxy compound with carbon dioxide by carrying out the polymerization reaction in the presence of a catalyst composition as described in U.S. Patent 3,900,424. The copolymerization is carried out at a temperature within the range of from about 0°C to about 150°C. U.S. Patent 3,248,415 discloses a process for copolymerizing carbon dioxide and a 1,2 epoxide, such as ethylene oxide, to yield polycarbonates of 700 to 5,000 molecular weight. The process is carried out in the presence of a small controlled concentration of an organic compound having at least 2, usually 2 to 4, active hydrogens such as a polyhydric alcohol at elevated temperature, superatmospheric pressure and preferably under conditions of base catalyst. In Introduction to Polymer Chemistry by Raymond B. Seymour, (1971) at page 204 it is disclosed that "homopolymers with reactive end groups may be converted to block copolymers by reactions with the active end groups, such as hydroxyl, carboxyl, and amine groups. Poly (ethylene oxides) with hydroxyl terminal groups may react with propylene oxide to product chains with different blocks of alkylene oxides." In Textbook of Polymer Science by Fred W. Billmeyer, Jr. at page 351, it is taught that block copolymers can be synthesized by producing "living" polymers by unterminated anionic polymerization. A second monomer can be added to the still active polymer, leading to a block copolymer uncontaminated with homopolymer and having blocks of accurately known and controlled length. BRIEF SUMMARY OF THE INVENTION The present invention is a novel class of block copolymers and a process for producing the same. The block copolymers have at least two distinct, covalently linked alkylene carbonate blocks, and have the structural formula: wherein R₁ is H, CH₃, C₂H₅, or C₆H₅; R₂ and R₃ are independently H, CH₃, C₂H₅ or R₂ and R₃ together form a six member ring; and x and y are both integers from 50 to 10,000. The process for producing block copolymers as described above comprises initially copolymerizing an alkylene oxide with carbon dioxide to form the corresponding polyalkylene carbonate. The process is carried out in a reaction vessel containing an organic solvent and in the presence of an organometallic catalyst. After the copolymerization reaches completion or equilibrium, a second alkylene oxide is added to the reaction vessel. The addition of the second alkylene oxide can take place without the addition of catalyst although additional catalyst may be added if desired. The second alkylene oxide reacts with the polyalkylene carbonate to form the block copolymer. DETAILED DESCRIPTION OF THE INVENTION A novel class of block copolymers are synthesized by initially reacting an alkylene oxide with CO₂ in an organic solvent in the presence of an organometallic catalyst to form a polyalkylene carbonate. The polyalkylene carbonate is subsequently reacted with a second alkylene oxide to form a block copolymer comprising distinct, covalently linked, alkylene carbonate blocks. The block copolymers of the present invention have the general structural formula: wherein R₁ is H, CH₃, C₂H₅ or C₆H₅; R₂ and R₃ are independently H, CH₃, C₂H₅ or R₂ and R₃ together form a six member ring; and x and y are both integers from 50 to 10,000. The block copolymer has a molecular weight between about 5,000 and 2 million with a range between 5000 and 1,000,000 being preferred and a range between 20,000 and 100,000 weight average being more preferred. Initially, an alkylene oxide is reacted with CO₂ to form the corresponding polyalkylene carbonate. The alkylene oxide can be any compound which will polymerize with CO₂, and preferably are selected from the class of 1,2 epoxides. Specific examples of suitable alkylene oxides are described by S. Inoue and N. Yamazaki in Organic and Bio-organic Chemistry of Carbon Dioxide (1982) p. 173, Table 4.15 and include ethylene oxide, propylene oxide, butylene oxide, isobutylene oxide, cyclohexyl oxide, etc. The alkylene oxide is contacted with an organometallic catalyst in a suitable reaction vessel. The reaction vessel preferably contains an organic solvent capable of dissolving the alkylene oxide; e.g. dioxane, and the catalyst, and also preferably contains an organic diluent such as toluene. The reaction vessel is then pressurized to between 5 and 50 kg/cm² with carbon dioxide and the reaction is allowed to proceed to equilibrium or completion. The carbon dioxide is preferably added in excess, i.e. a CO₂ to alkylene oxide ratio of between 3:1 to 10:1. The reaction is carried out at a temperature between 0° and 150°C. The catalyst employed can be any suitable organometallic catalyst which is capable of catalyzing the reaction. Generally the organometallic catalyst-has the structural formula: R'n M wherein n is an integer, at least one R' is an alkyl group an alicyclic group or halogen or hydroxy or alkoxy radicals, or hydrogen; the remaining R' groups are alkyl groups, alicyclic groups, alkaryl groups, aralkyl group, acyl groups or halogen or hydroxy or alkoxy radicals, and M is a metal of Group I, II or III of the Periodic Table. Specific examples of suitable metal elements include zinc, aluminum, lithium, calcium, magnesium and cadmium, although other metal elements may be equally suitable . A favored catalyst is diethyl zinc. The catalyst may also contain a co-catalyst component such as sulfur or a compound containing active hydrogen atoms;, e.g. water. In some instances, the catalyst/co-catalyst system may be reacted with CO₂ prior to being used to catalyze the polymerization. The catalyst should typically be present in a catalytic amount of from between 0.01 to 10 mole percent. After the initial polymerization between the alkylene oxide and the carbon dioxide is completed or has reached equilbrium, a second alkylene oxide is added to the reaction vessel. The second alkylene oxide may be added with additional CO₂ if necessary, but additional catalyst does not have to be added. Careful steps must be taken to insure that water or other chain terminating compounds are excluded from the reaction vessel. The second alkylene oxide reacts with the carbon dioxide in the reaction vessel to form a second polyalkylene carbonate which covalently bonds to the first polyalkylene carbonate present in the reaction vessel to form the desired block copolymer. The addition of the second alkylene oxide can take place shortly after the addition of CO₂ with the first alkylene oxide, or can be delayed for a significant time thereafter; e.g. in some instances addition of the second alkylene oxide more than 90 hours after initiation of the first reaction resulted in block copolymer product. The fact that the addition of the second alkylene oxides can be delayed for a significant period of time indicates, at least theoretically, that the initial reaction does not undergo a termination step, thus allowing the second alkylene oxide to react with CO₂ and block onto the previously formed polyalkylene carbonate. Additionally, the fact that additional catalyst does not have to be added with the second alkylene oxide further supports the theory that the reaction is still "alive" and is not reinitiated by the addition of more catalyst. Also, the method of reactant addition and product analysis indicates that the block copolymer is formed by covalent step-wise addition, and is not a graft copolymer. The block copolymer produced comprises at least two, distinct, covalently-linked polyalkylene carbonate blocks. The initial polycarbonate block is generally a "pure" block comprised of CO₂ and the first alkylene oxide monomers. The subsequent blocks can also be "pure" blocks or alternatively can be "mixed" blocks comprising CO₂ and monomer units of both the first and subsequent alkylene oxide monomers. This is especially true if the initial polymerization does not proceed to completion and there is unreacted alkylene oxide present when the second alkylene oxide is added. In such instances the product comprises a "pure" block covalently linked to a "mixed" block. The present process allows for the production of block copolymers having a wide range of properties. The properties can be tailored according to desired end product use by selecting both the type and quantity of alkylene oxide monomers for the polymerization process. For example, the properties of polyethylene carbonate can be altered slightly by blocking on a small amount of polypropylene carbonate. Alternatively, a block copolymer can be synthesized which has unique properties, significantly different from the individual polycarbonates, such as one having both thermoplastic and elastomeric properties. A block copolymer of polyethylene carbonate and polycyclohexyl carbonate is one example of such a copolymer. Several examples were carried out in accordance with the present invention and are set out below. These examples are presented to illustrate the invention and are not meant to be limiting. Example 1 A clean dry 5-gallon autoclave was charged 4 kg of p-dioxane, 174 g of diethylzinc, 200 ml of toluene, and 26 g of Al₂ (SO₄) · / 318H₂O. This was pressurized to 450 psi (31 bar) with carbon dioxide and heated at 264°F with stirring for 24 hours. The reactor was cooled and vented and 1583 g of propylene oxide and 800 ml of toluene added. The reactor and its contents were pressurized to 600 psi (41.5 bar) and heated 48 hours at 50°C (122°F) with stirring, then 76 bar (1100 psi) for four hours at 50°C (122 °F). A 1530 g quantity of ethylene oxide was added and heating and stirring continued another four hours. The products were isolated by washing with 10% HCl, then with water until neutral, and precipitating in 3-fold excess of methanol. After drying, the clear, tough polymeric products weighed 1858 g and were characterized as follows: Weight - Average molecular weight, GPC - 200,000 Solubility - Soluble in chloroform and methylene chloride; insoluble in tetrahydrofuran, methanol and acetone. Infrared Spectrum - Strong absorption at 1750 and 1210 cm⁻¹, absorption at 1450, 1380, 1060, 1040, 970, 850 and 780 cm⁻¹. NMR - Singlet at delta 4.36, and multiplets at delta 1.32, 4.21 and 4.99. Thermochanical Analysis - Inflection point and glass transition temperature at 27°C. Tensile Strength - The tensile strength of the specimens averages 70.3kg/cm² (1000 psi). By way of contrast, the copolymer of propylene oxide and carbon dioxide; i.e. polypropylene carbonate (PPC), is soluble in tetrahydrofuran, does not show an infrared absorption at 1040 cm⁻¹, shows NMR resonances at deltas 1.32, 4.21 and 4.99, has a glass transition temperature of 27-32°C, and has a tensile strength of 210.9 to 281.2 kg/cm² (3000-4000 psi). Polyethylene carbonate (PEC), by itself is not soluble in tetrahydrofuran, has no infrared absorption at 1060 and 970 cm⁻¹ , has a glass transition temperature of 7-17°C, a tensile strength of 7 - 105.5 kg/cm² (100-1500) psi,) and an NMR singlet at delta 4.35. Additionally, the polymeric product exhibited elastic recovery from up to a six-fold elongation. The polymer product was a block copolymer comprising a "pure" polypropylene carbonate block covalently linked to a second block containing polyethylene carbonate. The polyethylene carbonate block was either a "pure" block or a mixed block of predominantly polyethylene carbonate with minor amounts of propylene carbonate. The weaker polyethylene carbonate linkages dominate the tensile strength and limit solubility in tetrahydrofuran, whereas the infrared, glass transition temperature, and NMR analyses reflect that of polypropylene carbonate structure. Example 2 1530 g of propylene oxide was copolymerized with carbon dioxide using 174 g of diethyl zinc. The reaction was carried out in the presence of dioxane solvent. Visual examination of the products revealed a very thick paste at the end of 48 hours of reaction. The reactor was repressurized at 76 bar (1100 psi) with carbon dioxide and the reaction continued at 50°C for an additional four hours. Subsequently, 1538 g of ethylene oxide was added to the reaction vessel. After approximately two hours the reaction exothermed badly, reaching 132°C before venting of pressure cooled the reactor. Evidently carbon dioxide was consumed rapidly, the pressure being only 27.6 bar (400 psi) at 132°C. At the end of the second monomer addition the percent solids was close to theoretical (46 percent vs 51 percent). The product was collected and purified in much the same manner as described in Example 1. The IR spectrum was that of PPC, although the spectrum of PPC has all the features of PEC, plus some. The glass transition temperature, Tg, was that of PPC. The solubility, density and tensile strength, however, was that of PEC. An NMR analysis revealed about an 1:1.8 ratio of PEC:PPC.. Based upon the above characterization data and the exotherm during the reaction, it can be concluded that the recovered product was a block copolymer of polyethylene carbonate and polypropylene carbonate. Since no additional catalyst was added along with the second monomer, the initial catalyst remained active at the end of the first copolymerization. The weight average molecular weight of the product was about 207,000. Example 3 A block copolymer of cyclohexyl carbonate and ethylene carbonate was prepared in accordance with the general procedures set out in Example 1 above. Polycyclohexyl carbonate (PCHC) was prepared first by copolymerization of cyclohexene oxide and carbon dioxide. After approximately 90 hours, the product was sampled. The PCHC was isolated by methanol precipitation and dried to obtain a clear, brittle film-forming material, consistent with the reported Tg of 130°C for PCHC. Ethylene oxide and carbon dioxide were subsequently added to the reactor and the copolymerization continued. After approximately a nineteen hour reaction period, the product was isolated by methanol precipitation, and compared to the PCHC recovered above. PCHC is soluble in chloroform, methylene chloride, p-dioxane, tetrahydrofuran, toluene and methylethyl ketone. The product was soluble only in p-dioxane, methylene chloride and chloroform. NMR spectrum results for the product showed resonance at delta 4.36, attributable to PEC, and delta 1.54, attributable to PCHC. The ratio of PEC:PCHC was about 40:60. The above results indicate that the product was a copolymer of a polycyclohexyl carbonate block and a second block containing polyethylene carbonate. Additional blocks could be added to form a block copolymer having the properties expected of a thermoplastic elastomer. Having thus described the present invention, what is now deemed appropriate for Letters Patent is set out in the following appended claims.

Claims: A process for producing a block copolymer having at least two distinct, covalently linked alkylene carbonate blocks and having the structural formula: wherein R₁ is H, CH₃, C₂H₅, or C₆H₅; R₂ and R₃ are independently H, CH₃, C₂H₅ or R₂ and R₃ together form a six member ring; and x and y are both integers from 50 to 10,000, said block copolymer having a weight average molecular weight between 5000 and 2 million, said process comprising: (a) copolymerizing an alkylene oxide corresponding to the hydrocarbon moiety in one of the blocks in said formula with excess carbon dioxide in the presence of an organometallic catalyst at a temperature of 0 to 150°C, a pressure of 5 to 50 kg/cm² and a carbon dioxide to alkylene oxide ratio of 3:1 to 10:1 to form the corresponding polyalkylene carbonate; and (b) subsequently copolymerizing a second alkylene oxide, corresponding to the hydrocarbon moiety in the other of said blocks, with carbon dioxide in the presence of said catalyst to form said block copolymer. Process in accordance with claim 1 wherein no additional catalyst is employed in the copolymerization (b). Process in accordance with claim 1 wherein said second alkylene oxide is accompanied by additional carbon dioxide. The process in accordance with Claim 1 wherein the alkylene oxides are selected from the group consisting of ethylene oxide, propylene oxide, isobutylene oxide and cyclohexyl oxide. The process in accordance with Claim 1, wherein the organometallic catalyst having the general formula R'n M wherein n is an integer, at least one R' is an alkyl group, an alicyclic group or halogen or hydroxy or alkoxy radicals, or hydrogen, the remaining R' groups are alkyl groups, alicyclic groups, alkaryl groups, aralkyl groups, aryl groups or halogen or hydroxy or alkoxy radicals, and M is a metal of Group I, II or III of the Periodic Table. The process in accordance with Claim 7 wherein said catalyst is diethyl zinc. The process in accordance with Claim 7 wherein said catalyst also comprises a co-catalyst component which is sulfur or a compound containing active hydrogen atoms. The process in accordance with Claim 9 wherein said catalyst and co-catalyst are also reacted with CO₂ prior to being used to catalyze the copolymerization. The process in accordance with Claim 1 wherein said block copolymer has a molecular weight between 5,000 and 1,000,000. The process in accordance with Claim 1 wherein said process is carried out in the presence of an organic solvent. The process in accordance with Claim 10 wherein said organic solvent comprises dioxane. The process in accordance with Claim 10 wherein an organic diluent is added to the organic solvent. The process in accordance with Claim 12 wherein said organic diluent is toluene. A block copolymer having at least two distinct covalently linked alkylene carbonate blocks with each of the alkylene carbonate units in a first block having the formula (I): with each of the alkylene carbonate units in a second block having the formula (II): wherein R₂ is H,CH₃,C₂H₅ or C₆H₅; and R₂ and R₃ are independently H,CH₃,C₂H₅ or R₂ and R₃ together form a six member ring; each block having from 50 to 10000 alkylene carbonate units; and the molecular weight of said copolymer being between 5000 and 2000000; with the proviso that alkylene carbonate units (I) may also be present in the second block and that alkylene carbonate units (II) may also be present in the first block. The block copolymer in accordance with Claim 14 wherein said copolymer is a thermoplastic elastomer. The block copolymer in accordance with Claim 14 wherein one covalently linked alkylene carbonate block comprises ethylene carbonate. The block copolymer in accordance with Claim 16 wherein the second covalently linked alkylene carbonate block comprises propylene carbonate. The block copolymer in accordance with Claim 16 wherein the second covalently linked alkylene carbonate block comprises cyclohexyl carbonate. The block copolymer in accordance with Claim 14 where in said Copolymer has a molecular weight between 5000 and 1,000,000.

Inventors: SANTANGELO JOSEPH GERMANO, SINCLAIR RICHARD GLENN, WEBER JAMES JOSEPH, SANTANGELO,JOSEPH GERMANO, SINCLAIR, RICHARD GLENN, WEBER, JAMES JOSEPH
Applicants: PAC POLYMERS INC, PAC POLYMERS INC.
Application year: 1987
Main classification: C08G64
IPC codes: C08G64