TITANIUM-ALUMINIUM ALLOY

Abstract: Disclosed are Ti-Al alloys having increased ductility and Ti-Al alloys having increased ductility and lowered melting points, in both of which the main constituent phase is an intermetallic compound, TiAl. The Ti-Al alloys having increased ductility essentially consisting of Al: 28-38%, and B: 0.005-0.3%, the balance being Ti and inevitable impurities. Since the alloys of this type have good proces­ sability, they are suitable as materials for mechanical parts of rotating or reciprocating systems, where high heat-resistance and high specific strength are required. The Ti-Al alloys having increased ductility as well as lowered melting points essentially consisting of Al: 28-38%, one or two of Ni: 0.05-3.0% and Si: 0.05-3.0%, and the balance being Ti and inevitable impurities. Optionally, this alloy further contains B: 0.005-0.3%. The alloy of this type is, in addition to the above use, suitable for producing machine parts made by precision casting technology.

Description: The present invention relates to improvement of Ti-Al alloys, particularly, alloys in which the main constituent phase is the intermetallic compound, TiAl. Machine parts which are used under rotary or reciprocal movement, for example, turbine blades, hot wheels of turbochargers and engine valves, are recently being more and more light-weighted in order to meet the requirements of high performance such as high responce and high output. Heat-resistant materials for the above noted parts are, therefore evaluated by their specific strength (strength/ density) rather than the absolute strength, and efforts are being made to improve the specific strength of these materials. Under the circumstances, Ti-Al alloys, particularly, alloys in which the main constituent phase is intermetallic compound, TiAl, are drawing attention. The maximum usable temperature (a temperature at which the creep rupture life is 1000 hours under stress of 2756.6 bar (28.1 Kgf/mm²) of TiAl is 800°C, which is higher than that of conventional titanium alloy (Ti-6Al-4V), 550°C. Moreover, the specific gravity of Tial. (3.8) is lower than that of the conventional titanium alloy. (4.5) and is closer to that of ceramics (e.g., Si₃N₄ 3.2). TiAl has a ductility which ceramics lack, and its specific strength is higher than that of nickel-based super-alloys (e.g., Inconel 713C). Ti-Al alloys in which the main constituent phase is TiAl, however, have lower ductility when compared with the titanium alloys and nickel-based super-alloys, and have the drawback of poor plastic workability. Efforts are being made to improve this (for example, Japanese Patent Disclosure 56-4344 discloses addition of appropriate amount of V), but have not yet reached practical use. Also, the melting point of the intermetallic compound, TiAl, exceeds 1500°C which is higher than those of the nickel-based super-alloys for casting use (usually, 1250-1400°C), and therefore, it is difficult to obtain defectless cast products having desired shape by conventional lost-wax method using ceramic molds due to chemical reactions between the active molten metal, TiAl, of a high temperature exceeding 1500°C and ceramics forming the molds. US-A-3 203 794 describes a titanium-base alloy containing about 34 to 46% of aluminum and characterized in maintaining substantially its room temperature hardness at temperatures as high as about 1250° C, and in being highly resistant to oxidation at elevated temperatures up to at least 1050° C. Accordingly, the object of this invention is to solve the above described problems, and to provide a light weight heat-resistant alloy with improved workability in plastic working by increasing the ductility of Ti-Al alloys in which the main constituent phase is the intermetallic compound, TiAl. Another object of this invention is to improve the ductility of Ti-Al alloys in which the main constituent phase is the intermetallic compound, TiAl, so as to facilitate the plastic working, and further, to provide a light weight heat-resistant alloy with improved workability in plastic working and mold casting by increasing the ductility and lowering the melting point of the Ti-Al alloys in which the main constituent is the intermetallic compound, TiAl. The present invention provides a Ti-Al alloy consisting of Al: 28-38%, Ni: 0.05-3.0% and Si: 0.05-3.0%, and the balance being Ti and inevitable impurities. The present invention further provides a Ti-Al alloy consisting of Al: 28-38%, one or two of Ni: 0.05-3.0% and Si: 0.05-3.0%, and further, B: 0.005-0.30%, the balance being Ti and inevitable impurities. In the above alloy compositions, if a better ductility at a lower temperature is desired, it is neccessary to chose a low Al-content, and if the ductility at a higher temperature is more important, it is advisable to chose an Al-content of 32% or more. It is preferable that amounts of the impurities are in the following range: C: up to 0.2%, O: up to 0.3% and N: up to 0.3%, whereby O + N: up to 0.4%. As the means for producing desired structural parts with the Ti-Al alloys of this invention, casting as well as forging can be used. Selection of the above described composition of the Ti-Al alloys according to the present invention is based on the following reasons: Al: 28-38% The stoichiometric composition of the intermetallic compound, TiAl (gamma-phase), is Al: 36%, and the range in which single phase TiAl can exist in the binary alloys is Al: 34-42%. However, in case where Al exceeds 38%, the ductility decreases contrary to the object of this invention, and therefore, 38% is selected as the upper limit. On the other hand, in case where the composition is rich of Ti, or Al is less than 34%, Ti₃Al (alpha₂-phase) is formed. This compound enhances the ductility of the alloy at a lower temerature, and therefore, in case where a good cold ductility is desired, the Al-content range of 28-34% is recommended. Also, this compound, when the content is small, is useful to improve the high temperature ductility. However, Ti₃Al itself is brittle, the alloy will lose ductility as the amount thereof increases. Thus, in case where a good hot workability is required, the Al-content range of 32-38% is preferable. Also, Al lowers the melting point of the alloy, like boron, nickel and silicon mentioned below. B: 0.005-0.3% Boron increases ductility by strengthening the grain boundary of TiAl compound and also contributes to improvement in the strength by grain refinement. This effect may be obtained by addition of an amount as small as 0.005%. On the other hand, when the amount increases, boron will induce the formation of brittle borides, thus reducing the ductility. Hence, 0.3% is selected as the upper limit. Also, boron is, like nickel and silicon mentioned below, effective for lowering the melting point of the present alloys. Ni: 0.05-3.0%, Si: 0.05-3.0% Both nickel and silicon dissolve in TiAl phase and increase ductility. This effect is appreciable at the contents as low as 0.05%. On the other hand, the amounts of nickel and silicon which can be dissolved in TiAl phase are limited to 3.0%, and excess addition causes decrease in the ductility. Thus, the upper limits of these elements are determined to be 3.0%. Nickel and silicon are effective for lowering the melting temperature of the present alloy. C: up to 0.2% Carbon forms Ti-carbide, TiC, which improves the strength of the alloy, but carbon decreases the ductility of the alloy. Thus, 0.2% is selected as the upper limit. O: up to 0.3%, N: up to 0.3% preferably up to 0.2%, whereby, O + N: up to 0.4% Both oxygen and nitrogen are dissolved in TiAl and strengthen it. They, however, decrease the ductility of the alloy, and the above upper limits are determined from this point of view. If a better strength is desired for the alloy, the impurities are rather useful, and therefore, positive addition in the above noted range is preferable. On the other hand, if the alloy should have a higher ductility, the amounts of these impurities must be as low as possible. According to the present invention, ductility of Ti-Al alloys having high heat-resistant property and a high specific strength is improved and the workability of plastic wroking is thus improved. The lowered melting points of the alloys result in higher castability and facilitate precision casting. Therefore, various mechanical parts of rotating or reciprocating systems such as blades of aircraft jetengines and gasturbines for industrial use, intake and exhaust valves, rocker arms, connecting rods and hot wheels of turbochargers for motorcycle and automobile engines can be easily produced by forging or casting. Easier working also results in reduction of problems in reliability of the products due to difficulties in processing the material. Example Ti-Al alloys of the composition shown in Table 1 were prepared. Melting was carried out under argon gas atmosphere by plasma arc in a skull furnace with a water-cooled copper crucible. Runs Nos. 1-7 are examples according to the present invention, and Runs Nos. 8 and 9 are control examples for comparison. Test-prices cut out from the cast ingots of the alloys were subjected to tensile tests at 900°C and measurement of the melting points (liquidus and solidus) by differential thermal analysis. The results are shown in Table 4. It is understood from Table 4 that the present alloys have increased ductility and lowered melting points. Alloy No. 5 was subjected to 30% and 50% upsetting at 1150°C. No crack appeared on the test-piece even in case of 50% upset. Using the alloys Nos. 5 and 7 and ceramics molds made by lost-wax method, hot wheels for turbochargers were cast. There was observed defects on the blades of the hot wheels cast with control alloy No. 7 due to chemical reaction between the mold and the molten TiAl, and hence, no sound product was obtained. On the other hand, the hot wheels made of alloy No. 5 according to the present invention were sound products without defects. Alloy Composition (wt %, balance Ti) No. Al Si Ni B C O N Present Invention 1 33.34 0.33 0.35 - 0.019 0.122 0.009 2 35.36 0.59 0.36 - 0.018 0.090 0.009 3 27.92 0.32 0.21 0.05 0.023 0.095 0.028 4 35.47 0.35 - 0.08 0.045 0.130 0.007 5 35.28 - 0.27 0.04 0.019 0.075 0.012 6 37.21 - 0.47 0.16 0.037 0.103 0.030 7 35.30 0.36 0.54 0.06 0.020 0.083 0.024 Control 8 35.00 - - - - - - 9 34.90 - - - - - - V : 1.91 No. Tensil Properties Melting Point Tensile Strength bar (Kgf/mm²) Elongation % Reduction of Area % Liquidus °C Solidus °C Present Invention 1 3021.5 (30.8) 15.3 13.6 1499 1433 2 2923.4 (29.8) 34.9 30.9 1478 1421 3 3678.8 (37.5) 8.9 8.0 1506 1437 4 3482.6 (35.5) 36.2 31.9 1482 1427 5 2972.4 (30.3) 53.0 42.1 1492 1433 6 3198.1 (32.6) 25.3 20.3 1462 1407 7 2982.2 (30.4) 57.6 49.3 1463 1405 Control 8 2383.8 (24.3) 6.7 5.0 1503 1451 9 2158.2 (22.0) 0.5 0 1513 1469

Claims: A Ti-Al alloy consisting of Al: 28-38%, Ni: 0.05-3.0% and Si: 0.05-3.0%, and the balance being Ti and inevitable impurities. A Ti-Al alloy consisting of Al: 28-38%, one or two of Ni: 0.05-3.0% and Si: 0.05-3.0%, and further, B: 0.005-0.30%, the balance being Ti and inevitable impurities. A Ti-Al alloy according to one of claims 1-2, wherein the amounts of the impurities are in the ranges below: C: up to 0.2%, O: up to 0.3%, N: up to 0.3%, whereby O + N: up to 0.4%. Articles made from the alloys of one of claims 1-3 comprising one of blades of aircraft jetengines and gasturbines for industrial use, intake and exhaust valves, rocker arms, connecting rods and hot wheels of turbochargers for motorcycle and automobile engines.

Inventors: ISOBE, SUSUMU, MIYASHITA, TAKUYA, NISHIYAMA, YUKIO, NODA, TOSHIHARU
Applicants: DAIDO TOKUSHUKO KABUSHIKI KAISHA, KAWASAKI JUKOGYO KABUSHIKI KAISHA
Application year: 1987
Main classification: C22C14
IPC codes: C22C14