RUBBER COMPOSITION

Abstract: Disclosed is a rubber composition comprising 85 to 55 wt.% of copolymer rubber and 15 to 45 wt.% of chloroprene rubber, wherein the copolymer rubber comprises 10 to 60 mole % of epichlorohydrin, 30 to 90 mole % of propylene oxide or of propylene oxide and ethylene oxide and 0 to 15 mole % of unsaturated epoxide.

Description: The present invention relates to a rubber composition which comprises a blend of epichlorohydrinpropylene oxide type copolymer rubber and chloroprene rubber, and has remarkably improved properties. Among known oil-resistant rubber products, particularly chloroprene rubber (hereinafter referred to as CR) is known to have properties which are advantageously balanced and, as such, has been widely used for such as hose-covers, dust cover boots, belts and so forth in automobiles: CR has been put for use in view of its remarkable properties with respect to such as the oil resistance, the heat resistance, the low-temperature resistance, the ozone resistance, the resistance to bending and so on. However, as the social demand for controlling the pollution of air has of late grown to be greater and, to cope with this, the control of exhaust gas from passenger cars has become more strongly regulated than before, there have been various improvements made in or relating to for example automobile engines. A result of this is that it is now required of CR to have a further improved heat resistance. However, CR can hardly answer such demand for a further improvement in its heat resistance, and since it is prone to undergo a curing-type deterioration and can hardly stand a long use, it is likely to give rise to a serious danger. Also, CR has a crystalline structure and is regarded as being unsuited for use in cold areas, and it in addition involves a problem with respect to the dynamic ozone proof. Then, with epichlorohydrin-ethylene oxide copolymer rubber (hereinafter referred to as CHC), although this has better properties in comparison to CR, with respect to the heat resistance, oil resistance, low-temperature resistance and dynamic ozone resistance, it fails to be satisfactory with respect to the resistance to bending and it is not suitable for use as material which is required to possess high dynamic characteristics. The same is true with the copolymers known from the FR-A-2,567,900 and consisting of 10 to 60 mole % of epichlorohydrin, 30 to 90 mole % of propylene oxide or of propylene oxide and ethylene oxide and 0 to 15 mole % of unsaturated epoxide. With epichlorohydrin-propylene oxide type copolymer rubber, then, while it exceeds CR in respect of the heat resistance, oil resistance, low-temperature resistance and dynamic ozone resistance, it fails to be comparable to CR in respect of the flexibility. Summary Accordingly, it is a primary object of the present invention to provide such a rubber composition which has an oil resistance and a resistance to bending comparable to those of CR and which is improved over CR with respect to the heat resistance, low-temperature resistance and dynamic ozone resistance. The above object is attained according to the present invention by providing a rubber composition characterized by comprising 85 to 60 wt.% of a copolymer rubber and 15 to 40 wt.% of chloroprene rubber, wherein the copolymer rubber comprises 10 to 60 mole % of epichlorohydrin, 30 to 90 mole % of propylene oxide or of propylene oxide and ethylene oxide (providing the molar ratio of propylene oxide to ethylene oxide is 1 or higher) and 0 to 15 mole % of unsaturated epoxide, said rubber composition containing 0,1 to 5 parts by weight of sulfur as curing agent or 0,1 to 10 parts by weight of other sulfur type curing agent, per 100 parts by weight of said blend of copolyme rubber and chloroprene rubber. The Preferred Embodiments In or for the present invention, the copolymer rubber is obtainable by copolymerization of epichlorohydrin with propylene oxide or of propylene oxide with ethylene oxide, further with unsaturated epoxide as needs be. Unsaturated epoxide includes allyl glycidyl ether, glycidyl methacrylate, glycidyl acrylate and butadiene monoxide. With the unsaturated epoxide copolymerized, it is feasible to obtain an improvement with respect to the softening deterioration by heat and the dynamic ozone resistance, but if the molar ratio of the unsaturated epoxide exceeds 15 mole %, then the copolymer rubber tends to undergo a curing-type deterioration, lose the rubber elasticity and become brittle. Whereas the amount of propylene oxide or the total amount of propylene oxide and ethylene oxide may be suitably determined within a range of 30 to 90 mole % in consideration of low-temperature resistance values to be obtained of molded rubber products, if the amount or the total amount in reference is less than 30 mole %, a problem is likely to be posed relating to the low-temperature resistance, while if it exceeds 90 mole % it is likely that the oil resistance is lowered and the degree of swelling is increased. Particularly preferable proportions of the copolymerization components are 15 to 55 mole % for epichlorohydrin, 35 to 85 mole % for propylene oxide or for propylene oxide and ethylene oxide in combination, and 0 to 10 mole % for unsaturated epoxide. Further, if the molar ratio of propylene oxide to ethylene oxide is less than 1, then it is impossible to obtain a satisfactory resistance against bending. For or in the present invention, chloroprene rubber means a homopolymer of 2-chloro-1,3-butadiene or a copolymerized rubber of 2-chloro-1,3-butadiene and a monomer copolymerizable therewith, and includes a sulfur-modified copolymerized rubber. In the blend of the copolymer rubber and the chloroprene rubber according to the invention, the proportion of the copolymer rubber may be appropriately determined within a range of 85 to 60 wt.% in consideration of the required particular properties of molded rubber products. With a proportion exceeding 85 wt.%, it is infeasible to obtain a satisfactory resistance to bending, while with an amount not reaching 60 wt.%, a problem is likely concerning the dynamic ozone resistance. With regard to the curring agent for the blend of copolymer rubber and the chloroprene rubber, now that both components of the blend contain chlorine atoms, use may be made of a polythiol type curing agent and a thiourea type curing agent which cause a curing reaction through the chlorine atoms, and in the cases of a copolymer rubber copolymerized with unsaturated epoxide and a chloroprene rubber containing an unsaturated double bond, it is also feasible to use a sulfur type curing agent. For the polythiol type curing agent, use may be made of such ones as being normally used for CHC, for example such as di- or trithiol-S-triazine compounds (disclosed in for example United States Patent 3,787,376), 2,5-dimercapto-1,3,4-thiadiazole compounds (disclosed in for example United States Patent 4,288,576), 2,3-dimercapto-pyrazine compounds (disclosed in for example Japanese patent publication No. 58-14468), 2,3-dimercapto-quinoxaline compounds (disclosed in for example Japanese patent publication No. 58-14469), and 3,5-dimercapto-1,2,4-triazole compounds (disclosed in for example Japanese patent publication No. 57-46463). Then, the thiourea type curing agent includes 2-mercapto-imidazoline (ethyl thiourea) compounds and 2-mercapto-pyrimidine compounds (both disclosed in for example United States Patent 3,341,490). The sulfur type curing agent may be any of the one normally used for diene type rubber and includes such as sulfur and sulfur donors, for example, morpholine disulfide, thiuram compounds such as tetramethyl thiuram disulfide for example and high molecular polysulfur compounds. The use amount of the curing agent, based on 100 parts by weight of the blend of polymer rubber and chloroprene rubber, is within a range of 0.1 to 5 parts by weight in the case of sulfur, while it is within a range of 0.1 to 10 parts by weight in the cases of other sulfur type curing agent. Further, it is feasible to make a co-use of curing agents of different kinds. The rubber composition according to the present invention can be prepared by blending together a copolymerized rubber of epichlorohydrin and propylene oxide, or of propylene oxide and ethylene oxide, and further with unsaturated epoxide as needs be, and chloroprene rubber, and blending with the resulting mixture a curing agent and, if necessary, a compounding material for rubber such as a vulcanization accelerator, reinforcing agent, filler, plasticizer, antioxidant and so forth in or by an ordinarily employed mixer, for example rollers or a Banbury's mixer (trade mark). The resulting rubber composition will be heated in a mold as desired at a temperature normally of 100 to 250° C to obtain a cured rubber product. Cured rubber products made with use of the rubber composition according to the present invention are possessed or remarkable characteristics with respect to each of the oil resistance, the bending resistivity, the heat resistance, the low-temperature resistance and the dynamic ozone resistance, therefore they are advantageously useful not only for hose covers but also particularly for such members which are required to possess dynamic characteristics such as dust-cover boots and belts in automobiles. Now, the present invention will be described in greater detail with reference to specific examples and comparative example, and in the following description, the numerical values for the blending recipes and the rubber compositions means parts by weight. Example 1: Epichlorohydrin-propylene oxide-allyl glycidyl ether type copolymer rubber which was prepared with use of an organoaluminum compound type polymerization catalyst and by a solution polymerization process known per se and chloroprene rubber were together blended, with other compounding agents, according to the following blending recipe in a cooling roller, and the resulting blend was heated at 170° C for 15 minutes to obtain cured rubber products. Of the above obtained cured rubber products, the properties were determined according to JISK-6301 to obtain results as entered in the following Table 1. From considering the Table 1, it is clearly seeb that the cured rubber product of Experiment No. 5 (Comparative Example) is poor in the low-temperature resistance and the bending resistivity. Example 2: Copolymer rubber of epichlorohydrin (30 mole %)-propylene oxide (67 mole %)-allyl glycidyl ether (3 mole %) and chloroprene rubber were together blended, with other compounding agents, according to the blending recipe recited in the following Table 2, in a cooling roller, and with use of the resulting blend according to the blending recipe entered in the below Table 3, mixtures were prepared by a cooling roller. A determination of properties of cured rubber products was carried out according to JISK-6301. A grease dipping test was conducted according to JISK-6301 with use for the testing grease of Molilex No. 2 (product of Kyodo Oil & Fats Co., Ltd.). Further, a dynamic ozone deterioration test was operated at an ambient temperature of 40° C, at an ozone concentration of 50 pphm and under a dynamic condition with an elongation of 0 to 30% imparted to test samples, to find generation of cracks. Results of the determinations and tests are shown in the following Table 3. Example 3: Except that the compounding ratio of chloroprene rubber was changed as in the following blending recipe, the above Example 2 was repeated and determinations/tests were conducted as in the Example 2. The results of the determinations/tests are entered in the below Table 4. Example 4: Copolymer rubber of epichlorohydrin (30 mole %)-propylene oxide (67 mole %)-allyl glycidyl ether (3 mole %) and chloroprene rubber were blended according to the blending recipe entered in the following Table 5 and same determinations and tests as in Example 2 were carried out. The results of the determinations and tests are entered in Table 6.

Claims: 1. A rubber composition comprising 85 to 60 weight % of copolymer rubber and 15 to 40 weight % of chloroprene rubber, said copolymer rubber comprising 10 to 60 mole % of epichlorohydrin, 30 to 90 mole % of propylene oxide or of propylene oxide and ethylene oxide (providing the molar ratio fo propylene oxide to ethylene oxide is 1 or more) and 0 to 15 mole % of unsaturated epoxide, said rubber composition containing 0,1 to 5 parts by weight of sulfur as curing agent or 0,1 to 10 parts by weight of other sulfur type curing agent, per 100 parts of said blend of copolymer rubber and chloroprene rubber. 2. A rubber composition as claimed in claim 1, wherein said copolymer rubber comprises 15 to 55 mole % of epichlorohydrin, 35 to 85 mole % of propylene oxide or of propylene oxide and ethylene oxide and 0 to 10 mole % of unsaturated epoxide. 3. A rubber composition as claimed in claim 1, wherein said unsaturated epoxide is allyl glycidyl ether, glycidyl methacrylate, glycidyl acrylate or butadiene monoxide.

Inventors: MAEDA, AKIO NIPPON ZEON K.K., UESHIMA, KEI NIPPON ZEON K.K.
Applicants: NIPPON ZEON CO., LTD., THE YOKOHAMA RUBBER CO., LTD.
Application year: 1987
Main classification: C08L71
IPC codes: C08L71