Fertilizer-containing compositions

Abstract: A fertilizer-containing composition comprises of water-soluble central mass of plant food compound containing reactive functional groups amounting to at least 10 percent, and a base component, surrounding and chemically bonded to the central mass, formed by reacting a molecular excess of a polyfunctional monomeric-type compound with the reactive functional group of the central mass, the base component having residual reactive functionality. This fertilizer-containing composition can be used as an intermediate in the preparation of fertilizer particles.

Description: This invention relates to fertilizer-containing compositions. More particularly this invention relates to fertilizer-containing compositions e.g. for use in obtaining coated fertilizer compositions. Rapid release of water-soluble plant food in soils containing plants may cause phytotoxicity to the plants, and/or the early depletion of the plant food by leaching. Plant food researchers for a long time have attempted to develop plant food particles which release nutrients at a rate about equal to their uptake by plants to minimize phytotoxicity and maximize plant food use efficiency. Improved release control has been achieved primarily with nitrogen in the form of urea, by substantially reacting it with aldehydes to form insoluble products such as ureaform, which must chemically decompose in the soil before the nitrogen becomes available for utilization by plants. Another method consists of physically coating fertilizer granules with solidified water-insoluble melts. Various materials have been used as coatings, including sulfur, paraffin waxes, and plastics. These coatings must be broken down by erosion, internal vapor pressure, microbes, or attrition before the contained nutrients become available. Unfortunately, attrition in producing, storing, handling, and applying the coated products prematurely breaks down the coatings causing substantial loss of release control, phytotoxic problems, and excessive nutrient leaching. Related problems and disadvantages associated with these coated products are that as a result of the coating the nitrogen, depending on the type of coating used, is not available for plant uptake in a reasonable time period, or the nitrogen release rate is still sufficiently high so as to cause phytotoxic problems when substantial amounts of the fertilizers are applied. Additionally, since there is no direct chemical bonding between the plant food and the coating material, the release rate of the plant food is not rigidly controlled as a result of cracking of the coatings or the like, leading to the uncontrolled release of the plant food. Australian Patent Specification 528086 discloses insecticide coated fertilizers. Particles are coated with a polymeric type coating which acts to provide a matrix in which an insecticide is dispersed. Japanese Patent Specification 73042673 describes fertilizer particles which have a durable, and hence unreactive, surface coating. It is disclosed that such a coating may be formed from urea treated with an organic isocyanate. According to the present invention there is provided a fertilizer-containing composition which comprises fertiliser particles consisting of a water-soluble central mass of plant food compound containing reactive functional groups and the central mass of each particle being surrounded by a coating of a monomer-type component having reactive functionality, characterised in that the plant food compound contains reactive functional groups to an extent of at least 10% and the monomer-type component having reactive functionality being present in an amount so as to have sufficient functionality to react with all the reactive groups available at the surface of the central mass while leaving the coating with residual reactive functionality. The fertilizer-containing composition according to the present invention can be used as an intermediate in the preparation of an attrition-resistant, controlled release fertilizer particle composition as described and claimed in European Patent Application 87905544.0 (WO 88/01132) from which this application is divided. The fertilizer-containing composition according to the invention can also be used as a means of providing fertilizer i.e., the water-soluble central mass, containing an auxiliary agricultural component such as a herbicide, a fungicide, an insecticide, or the like through reaction of the intermediate with the agricultural component. Additionally, the intermediate offers a convenient means for providing a fortified fertilizer particle through reaction of the intermediate composition with, for example, melamine to provide increased fertilizer value and increased control of the release of a plant nutrient. The fertilizer containing composition according to the present invention may be prepared by a method which comprises surrounding and chemically bonding to particles of a water-soluble central mass of plant food compound containing reactive functional groups amounting to at least 10 percent, a molecular excess of a monomer-type component having reactive functionality by reaction with the reactive functional groups of the central mass. In the fertilizer-containing particles according to the invention the monomer-type component strongly connects itself to the water-soluble central mass to form generally a base coat, with the base coat then being capable of being bonded e.g. to a water-insoluble coating or sealing layer so that the coated fertilizer particle is highly resistant to attrition even under conditions of extreme vibration, impact, and abrasion. The strong connection of the monomer-type compound acting as coupling agent is achieved by the chemical reaction of functional groups on the coupling agent, such as an isocyanate group of a liquid polyfunctional isocyanate, with, in a preferred embodiment, the nucleophilic functional groups such as NH₂ groups at, and near, the surface of the water-soluble central mass, to form a complex such as substituted ureas which are integral parts of the central mass and the base coating. The coupling agent, or base coating, can then be surrounded and chemically bonded to a water-soluble sealing layer which provides a barrier to moisture penetration and the release of the soluble fertilizer from the central mass of the particle. The sealing layer is formed by reacting a material also having reactive functional groups, such as an organic polyol, with the coupling agent, such as the polyfunctional isocyanate, thus chemically bonding the sealing layer with the base coating and, in turn, with the water-soluble central mass. The method for the preparation of the fertilizer-containing composition according to the invention requires surrounding and chemically bonding particles of water-soluble fertilizer compounds containing functional groups, such as nucleophilic groups, with a coupling agent containing functional groups reactive with functionality on the water-soluble central mass and material making up the layer to be subsequently applied. In a preferred embodiment where the water-soluble central mass contains NH₂ functionality, the central mass is reacted with a coupling agent to form a base coating consisting of substituted ureas by applying a molecular excess of liquid polyfunctional isocyanate to a mobile mass of the particles of fertilizer at a temperature between 30°C and 160°C, and holding for a period of time between one and 60 minutes. Then the base coating can be surrounded and chemically bonded with e.g. a water-insoluble sealing layer by reaction and polymerization of the remaining functionality of the polyfunctional isocyanate of the coupling agent with an amount of anhydrous organic polyol. The fertilizer-containing composition of this invention contains a water-soluble central mass of plant food. The plant food is a chemical compound, or compounds, normally used for plant nutrition. This central mass must contain at least about 10 percent reactive functional groups, such as nucleophilic groups, to provide the reaction sites for chemically bonding to a coupling material. The water-soluble central mass of plant food can be any of the various materials having plant food values such as materials containing potassium, phosphorus, nitrogen and sulfur. It is essential, however, that the functionality be available at the surface of the mass for reaction with a monomeric-type coupling agent. Useful materials include compounds containing NH₂ (amino) functionality such as urea, substituted ureas including ureaform and alkylurea; biurets, guanidine, melamine, amino acids, proteins, methylolureas, ethanolamines; compounds having OH (hydroxyl) functionality and plant food value, such as the nitrogen-containing polyols, and the plant food materials monoammonium phosphate, diammonium phosphate, ammonium polyphosphate, monopotassium phosphate, dipotassium phosphate, potassium bicarbonate, ammonium sulfate and potassium bisulfate. Plant food materials containing carboxyl functionalities such as potassium formate, potassium acetate and potassium diacetate and elemental sulfur can also be used. The reactive functionality, such as nucleophilic groups, as above stated must be present in an amount of at least about 10 percent to provide the necessary reaction sites. The percent of nucleophilic functionality preferably is at least 23 percent, and more preferably in the range of 23 to 60 percent. All percents used throughout this disclosure are by weight unless otherwise specified. The monomeric-type coupling agent reacts at the surface of the water-soluble mass to form what can be considered a base coating which surrounds and chemically bonds to the central mass, and then can react with a second material to form an e.g. water-insoluble coating. The coupling agent can be any monomeric-type material having at least two functional groups available for coupling. In this context, monomer-type component or monomeric-type material includes those materials having the necessary functionality and includes compounds, low molecular weight polymers, and the like. The available functionality must be selected so that it will react with the reactive functionality, such as a nucleophilic group on the water-soluble central mass and also with the functionality of the component providing the intended coating. Materials which can be used, depending upon the functionality on the water-soluble mass and the component forming the intended coating, can be a polyfunctional isocyanate, as illustrated by diphenylmethane diisocyanate; a polycarboxylic acid compound, as illustrated by terephthalic acid, and adipic acid, as well as the amino-substituted carboxyl groups; an anhydride of a polycarboxylic acid, as illustrated by maleic anhydride; an alkylated polycarboxylic acid, as illustrated by methyl terephthalate; and the like. In the event the water-soluble central mass contains amino functionality, and the coupling agent is a polyisocyanate, the base coating consists of substituted ureas formed by reacting a molecular excess of the polyfunctional isocyanate with the NH₂ groups of the central mass. The chemical bond is formed by the penetration of the isocyanate at and near the surface of the central mass to react with the NH₂ groups available there. A molecular excess of the coupling agent such as the isocyanate means that sufficient functionality, such as NCO (isocyanate) groups, are present to react with all the reactive groups available at the surface of the central mass, and to provide sufficient unreacted groups to form a chemical bond with the sealing layer. The water-insoluble sealing layer which can then surround and chemically bond to the base coating is formed by the reaction and polymerization of the excess polyfunctional isocyanate of the coupling agent or base coating with an amount of material sufficient to form a water-insoluble coating or sealing layer. In the event the coupling agent is a polyisocyanate, a preferred sealing material is an anhydrous organic polyol in an amount sufficient to produce a ratio of NCO to OH groups between one and three. Other materials which can be utilized in forming a water-insoluble sealing coating are those materials having sufficient reactive functionality to react with the functionality of the coupling agent. These materials include polyester resins containing hydroxyl and amino groups reactive with the coupling agent illustrated by polyols obtained as distillation bottoms in the recycle recovery of fiber grade glycol in the production of polyethylene terephthalate polyesters, blended with triethanolamine; materials containing formaldehyde or amino-formaldehyde functionality illustrated by monomethylolurea, methylene diurea, and polymethyleneureas; as well as reactive components containing substituted urea linkages. Other materials which are suitable for reacting with the coupling agents to form water-insoluble sealing layers include caprolactam, epichlorohydrin, propylene oxide, ethylene oxide, styrene oxide, hexamethylene tetramine, and natural and synthetic polysaccharides. To achieve the desired chemical bond between the base coating and the central mass of soluble fertilizer, the coupling agent, such as the polyfunctional isocyanate used in the composition, should be fluid at the time of reaction and preferably have a kinematic viscosity lower than 200 centipoise at 25°C and preferably between 60 and 120; and that it be chemically reactive at relatively low termperatures, i.e., at temperatures below about 160°C, and preferably in the range of 30°C to 110°C, and more preferably in the range of 90°C to 100°C. Coupling agents most effective are those having a reactive functional group content between 10 and 60 percent, and preferably between 25 and 45 percent. The amount of coupling agent utilized to form the base coating is generally critical to attrition resistance of a coated particle. It was found that the coupling agent preferably is between .03 and 10 percent of the total fertilizer particle. Lower amounts will not produce a satisfactory bond, while larger amounts are difficult to apply in a practical manner and are costly. A particularly effective fertilizer particle composition of this invention, especially useful in the preparation of a commercial controlled release fertilizer, comprises a central mass of urea containing between 26 and 53 percent NH₂ functional groups; a base coating, surrounding and chemically bonded to the central mass, formed by reacting a molecular excess of polymeric diphenylmethane diisocyanate, amounting to between 0.5 and 1.5 percent to the fertilizer particle and containing between 30 and 33 percent NCO, with the NH₂ functional groups from the cental mass of urea. A water-insoluble sealing layer surrounding and chemically bonded to the base coating, can then be formed by the reaction and polymerization of the excess polymeric diphenylmethane diisocyanate of the base coating, with an amount of polyalkyleneterephthalate polyester polyol to produce an NCO to OH moiety ratio between 1.1 and 1.8, with the polyol containing between 5 and 15 percent trialkanolamine and less than 0.1 percent water, and exhibiting a hydroxyl number between 225 and 350; and between one and five water-insoluble coatings surrounding the sealing layer with each coating amounting to between 0.5 and 1.5 percent of the fertilizer particle, the coatings consisting of layers of polymeric diphenylmethane diisocyanate and polyalkyleneterephthalate polyester polyol applied in alternate layers to produce an NCO to OH moiety ratio in the water-insoluble coatings between 1.0 and 1.5. An effective method by which the particulate fertilizer-containing composition of this invention can be prepared comprises surrounding and chemically bonding particles of water-soluble fertilizer materials, preferably consisting of urea, biuret, guanidine, ureaform, alkylurea and melamine, containing at least 10 percent, and preferably between 26 and 53 percent, NH₂ functional groups, with a base coating consisting of substituted ureas by applying a molecular excess of liquid polyfunctional isocyanate, preferably between 0.5 and 1.5 percent of polymeric diphenylmethane diisocyanate containing between 30 and 33 percent NCO, to a mobile mass of the particles of fertilizer at a temperature between 30°C and 160°C, preferably between 80°C and 120°C and holding for a period of time between one and 60 minutes, preferably between two and ten minutes. It has been found that several practical methods may be used to create the mobile mass of particles of fertilizer for applying the base coating of this invention and that the method may be carried out batchwise or continuously. A rotary drum was found to work satisfactorily. When this apparatus was used in a continuous matter, it was necessary that it be operated so that there was little backmixing as the reactants passed through the rotary drum. It was also found possible to perform the method of this invention in fluid beds. In the aforesaid disclosure it is to be understood that the term "polyfunctional isocyanate" is used to define aliphatic, aromatic, and aliphatic aromatic polyisocyanate compounds generally known as polyisocyanates. These compounds contain two or more NCO groups available for reaction, and are widely used in the production of polyurethane polymers. The term "organic polyol" is used to define organic compounds containing two or more OH groups located on an aliphatic or aromatic carbon skeleton. Because of the nucleophilic nature of the OH groups, these compounds may be readily reacted and polymerized with the electrophilic polyfunctional isocyanates. The organic polyols used in the instant invention must be substantially anhydrous when the coupling agent is a polyisocyanate. Any water present reacts with the isocyanates to produce carbon dioxide gas, thereby blowing perforations through the sealing layer and allowing higher than desired moisture penetration of the sealing layer. It has been found that the use of low molecular weight polyols, such as ethylene or propylene glycols, or blended polyols containing substantial amounts of low molecular weight polyols, also causes the generation of some carbon dioxide and creates less effective sealing layers. The term "substituted urea" is used to define compounds such as RNHCONHR' formed by the reaction of the NCO group in RNCO with the NH₂ group of R'NH₂. The substituted ureas are solids exhibiting limited water solubility. They are generally too soluble to protect the central soluble mass of plant food from dissolution by water. These ureas, however, form a very strong physical and chemical bond between the soluble central mass and the water-insoluble sealing layer. The exact reason for this exceptionally strong bond is unknown, but it is thought to be related to the chemical similarity of the substituted ureas to both the NH₂ groups of the central mass and the isocyanate-based polymers in the sealing layer. The supply of a plant nutrient such as NH₂ in the central water-soluble mass of the fertilizer-containing composition is critical to the instant invention. Urea, biuret, guanidine, ureaform (methylene urea polymer), and melamine, were found to supply satisfactory amounts of NH₂ groups when used as a simple granule or when combined with other plant nutrients to form a composite granule containing the necessary amounts of NH₂. Other plant nutrients such as potassium, phosphorus, and sulfur can replace part or all of the nitrogen-containing material. The method of preparation is important in securing an effective attrition-resistant, controlled release particle composition. For example, it was not possible to obtain the secure chemical bond between the base coating and the central mass of soluble fertilizer by dissolving a water-insoluble resin such as a polyurethane in an organic solvent, applying that liquid to the particle, and evaporating the solvent. It was also not possible to obtain such a secure bond by applying a molten thermoplastic material such as wax, polyethylene, or polystyrene to the soluble particle and cooling. Further, it was not possible to simply add preformed substituted ureas to the central soluble particle mass to produce the strong base coat. It was necessary that these substituted ureas be formed in situ . The failure of the aforesaid methods is because the central mass is not chemically bonded to the base coating and the base coating is not bonded to the water-insoluble coating. The above description of the invention has been directed in part primarily to the utilization of a water-soluble mass carrying amino groups as the nucleophilic functional group. It will be apparent, however, that the same considerations apply when the water-soluble mass carries different nucleophilic functional groups. The invention has also been described primarily in reference to using a polyisocyanate as the coupling agent. It will again be understood that the same considerations apply when using coupling agents having other or a combination of different functional groups. The invention is further illustrated in the following Examples, including the preferred methods of preparation, method of use and comparative evaluations with prior art compositions. Example 1 A sample of -6 + 14 U.S. Standard Mesh Screen Size granular fertilizer particles was prepared which was composed of water-soluble central masses (granules) of urea containing 53 percent NH₂ functional groups; and a base coating, surrounding and chemically bonded to the central mass, consisting of the substituted ureas resulting from the reaction of 1.3 percent (by weight of the granular fertilizer particles) polymeric diphenylmethane diisocyanate with the NH₂ functional groups at the surfaces of the central masses of the urea particles. The polymeric diphenylmethane diisocyanate, sometimes designated as isocyanic acid, polymethylene polyphenylene ester, was a liquid containing about 65 percent diphenylmethane diisocyanate (commonly abbreviated as MDI) and about 35 percent of higher oligomers of MDI, having a kinematic viscosity at 25°C of 80 centipoise, an average molecular weight of 350, a specific gravity of 1.24, and an isocyanate (NCO) functional group concentration of 31.9 percent. There was sufficient polymeric diphenylmethane diisocyanate so that all of the NCO functional groups were not reacted by the NH₂ groups at the surface of the urea granules while forming the base coating. The sample composition included a water-insoluble sealing layer, surrounding and bonded to the base coating, which layer was formed by the reaction and polymerization of the excess diphenylmethane diisocyanate of the base coating with a polyethylene terephthalate polyester polyol which provided one OH group (moiety) per 1.3 NCO group (moiety) used in preparing the base coating. The polyol used was a by-product recovered as still-bottoms in the recovery of glycols from polyester production from glycols and terephthalic acid. Moisture content was less than 0.1 percent, free diethylene glycol content was 8 percent, and the hydroxyl number of the polyol was 319. The polyol contained 10 percent triethanolamine as reaction-polymerization catalyst. The total weight of the base coating and sealing layer was 3 percent of the granular fertilizer particles. Examination of the individual particles with a 200 power laboratory microscope showed the base coatings and the sealing layers to be continuous, smooth, and completely attached to the central particles, with no visible holes or cracks. Example 2 Microscopic examination was made of two samples of -6 + 14 mesh granules of coated urea. The first was coated with 18 percent elemental sulfur, prepared by applying molten sulfur, cooling, sealing with 0.6 percent polyethylene in bright oil, then conditioned with 1.1 percent fine diatomaceous earth powder. The second was prepared by spraying on layers of polyurethane polymer dissolved in a volatile hydrocarbon solvent. The total amount of urethane resin applied amounted to 5 percent by weight. The sulfur coated urea was observed to contain a large number of cracks, and areas of lumps or thick sulfur coats. The urethane coated urea particles were found to contain areas where the coating was unattached and not in contact with the central urea particle. The coatings contained a substantial number of bubbles and some holes created by the escaping solvent vapours. Example 3 Samples amounting to 500 grams each of the Example 1 composition and the sulfur and urethane coated urea granules of Example 2 were tested for resistance to attrition and were placed in a 150mm diameter by 200mm long porcelain laboratory ball mill containing 40 steel balls, about one centimetre in diameter, and allowed to roll for twenty minutes at 100 rpm, providing a high degree of abrasion and impact. At the end of the test period, the sample granules were removed and attrition was measured by screening in a vibratory shaker for five minutes. The amount of material passing through a 16-mesh screen from each sample was weighed. No appreciable amount of fines was produced from the composition of Example 1. The fines from the sulfur-coated urea and the urethane-coated urea amounted to 7.2 and 1.8 grams respectively. Example 4 Samples from the attrition resistance test of Example 3, each amounting to 25 grams, were placed in 100 grams of water and stored for 24 hours at 100°C in a quiet closed bottle. The amounts of urea dissolved from the composition of Example 1, the urethane-coated urea and the sulfur-coated urea were 7.1, 43.6 and 78.3 percent respectively. Example 5 To a laboratory rotary drum coater, 600mm in diameter, 250mm long, fitted with fifteen slanted lifts to induce particle rolling, 4000 grams of -4 + 6 mesh granular urea particles containing 52 percent NH₂ groups were added and rotation of the drum at 30 rpm was initiated. A base coating surrounding and bonded to the urea was formed by spraying 1.0 percent of liquid polymeric diphenylmethane diisocyanate containing 30 percent NCO and consisting of 50 percent diphenylmethane diisocyanate (MDI) and 50 percent of higher oligomers of MDI on to the surfaces of the mobile mass of urea granules in the coater at 110°C and allowed to react and produce substituted urea for a period of two minutes. The molecular excess of unreacted NCO groups remaining on the outer surface of the base coating made the particle slightly tacky at this intermediate stage of the method. To produce a sealing layer on the base coating, the rotation of the coating drum was continued and on to the mobile mass of particles in the drum was sprayed 1.5 percent of a polyol which was preheated to 80°C to improve its reactivity and spread rate over the granules. The polyol consisted of scrap terephthalate polyester plastic bottles, ground and dissolved by refluxing in triethylene glycol. This economic polyester polyol had a hydroxyl number of 240 and contained 9 percent triethylene glycol and less than 0.1 percent water, and exhibited a viscosity of 13,800 centipoise at 25°C. Prior to its use, 10 percent triethanolamine was added as a reaction and polymerization catalyst to the polyol. The sealing layer was formed by holding the temperature of coated particles at 112°C for two minutes. About half of the particles were discharged hot from the coating drum and were found to be hard and very resistant to attrition and water dissolution. Example 6 Two kg of the product from Example 5 were retained in the rotary drum and alternate layers of the diisocyanate and polyols of Example 5 were sprayed on to the mass of sealing layer coated urea particles at 120°C. Each two applications were allowed to polymerize for four minutes before another series of sprays was applied. Each series of sprays contained 1.0 percent of the diisocyanate and 1.4 percent of the polyol. Two series of water-insoluble coatings were applied over the sealing layer, giving a total coating of 7.3 percent. Microscopic inspection of the coated granules showed them to be substantially free of holes, bubbles and cracks. Each coating appeared to be substantially a part of the coating which it covered, and there were no voids between the central urea particles and the coatings. Example 7 The product from Example 6 was given the attrition test of Example 3 and less than 0.1 gram of fines were produced. A 2000 gram sample of polyurethane-coated urea was prepared by coating -4 + 6 mesh urea with four layers each amounting to 2 percent polyurethane polymer, by application as a hydrocarbon solution and evaporating the solvent from each layer. A 2000 gram sample of the same urea granules was coated with 28 percent elemental sulfur with 0.5 percent sealer and 1.0 percent conditioner. Samples of the sulfur- and urethane-coated urea granules were given the attrition test of Example 3, and attrition amounted to 4.7 and 1.1 grams respectively. Example 8 The samples given the attrition resistance tests of Example 3, after discarding the fines, were given the water dissolution test of Example 4, except in this test the coated granules were allowed to stand for seven days before the amount of urea dissolved out of the granules was measured. Only 7.4 percent of the urea in the granules produced in Example 6 dissolved, compared with 47.7 percent of the urethane-coated urea and 61.1 percent of the sulfur-coated urea of Example 7. Example 9 Example 5 was repeated using, as the central soluble mass, -6 + 14 mesh particles of co-granulated urea and melamine containing 45 percent melamine and 55 percent urea, and the two additional series of water-insoluble coatings were added as in Example 6, producing a total coating of 7.5 percent. Microscopic inspection showed the seal of the coating to be complete and the seven-day water dissolution test of Example 8 showed the total nitrogen dissolved was equivalent to 3.8 percent of the contained urea. In the above examples illustrating the present invention, the water-soluble central mass can be replaced by other plant food containing materials including ureaform, alkylurea, biurets, guanidine, melamine, amino acids, proteins, methanol ureas, ethanolamines, nitrogen-containing polyols, monoammonium phosphate, diammonium phosphate, ammonium polyphosphate, monopotassium phosphate, dipotassium phosphate, potassium bicarbonate, ammonium sulfate, potassium bisulfate, potassium formate, potassium acetate, potassium diacetate, and a material containing elemental sulfur. Additionally, the coupling agent can be replaced by terephthalic acid, adipic acid, maleic anhydride, methyl terephthalic acid, or a prepolymer of a polyisocyanate and polyol. The water-insoluble sealing layer which surrounds and chemically bonds to the base coating can be based on caprolactam, epichlorohydrin, propylene oxide, ethylene oxide, styrene oxide, hexamethylene tetramine, and natural and synthetic polysaccharides; as well as prepolymers containing unreacted epoxy groups, or phenol formaldehyde resins carrying functionality reactive with the selected coupling agent.

Claims: A fertiliser-containing composition which comprises fertiliser particles consisting of a water-soluble central mass of plant food compound containing reactive functional groups and the central mass of each particle being surrounded by a coating of a monomer-type component having reactive functionality, characterised in that the plant food compound contains reactive functional groups to an extent of at least 10% and the monomer-type component having reactive functionality being present in an amount so as to have sufficient functionality to react with all the reactive groups available at the surface of the central mass while leaving the coating with residual reactive functionality. A composition according to Claim 1 wherein the reactive functional groups of the plant food compound are nucleophilic reactive groups. A composition according to Claim 2 wherein the nucleophilic reactive groups of the plant food compound are -NH₂. A composition according to any one of Claims 1 to 3 wherein the water-soluble central mass is a particle of urea, biuret, guanidine, ureaform, or melamine. A composition according to any preceding Claim wherein the monomer-type component having reactive functionality is a polyisocyanate. A composition according to Claim 5 wherein the polyfunctional isocyanate has a viscosity lower than 200 centipoise at 25°C and an NCO content between 20 and 35 percent. A composition according to Claim 5 or 6 wherein the polyfunctional isocyanate amounts to between 0.3 and 2.5 percent by weight of the coated fertiliser particles. A method of preparing the fertiliser-containing composition of any one of Claims 1 to 7, which method comprises surrounding and chemically bonding to the fertiliser particles a monomer-type component having reactive functionality which reacts with their reactive functional groups. A method according to Claim 8 wherein a molar excess of the monomer-type component having reactive functionality is applied to a mobile mass of the particles of fertiliser at a temperature between 30°C and 190°C and holding for a period of time between one minute and 60 minutes.

Inventors: MOORE WILLIAM PERCY, MOORE, WILLIAM PERCY
Applicants: RLC TECHNOLOGIES LLC, RLC TECHNOLOGIES, L.L.C.
Application year: 1987
Main classification: C05G3
IPC codes: C05C9, C05G3, C08G18