CERAMICS

Abstract: Aqueous dispersions of binders may be used to make a slurry of a ceramic material. The slurry may then be shaped to a green part by conventional techniques such as tape casting. The tensile strength of the green part may be increased by subjecting the green part to an energy treatment such as irradiation, e.g. ultraviolet (UV), X-­ rays and electron beams.

Description: This is a divisional application of European Patent Application 87301918.6-2111 which is laid open as EP-A 237.273. There are a number of fields of application for ceramics including traditional ceramics such as pottery and fine china; refractories; industrial ceramics such as abrasives and grinding wheels and technical ceramics. Technical ceramics are ceramics having a high purity. They are used in a number of applications including substrates for electrical circuits and mechanical parts. There are several major processes currently used in manufacturing ceramics. In several of these processes, a liquid based ceramic composition containing a binder is dried. The dried composition is then subjected to a compaction step such as dry pressing, roll compaction or injection molding. In fluid compositions which are to be dried, the liquid phase has generally been water if a water soluble binder has been used or a volatile organic solvent for water insoluble binders. These organic solvents are relatively expensive; should not be released to the environment and may present a fire hazard. Polyvinylbutyral in a solvent is typical of such systems and is used in tape casting. Polyvinylalcohol has been used in aqueous based binder systems for dry pressing. Unfortunately, polyvinylalcohol is hygroscopic and spray dried ceramic particles coated with polyvinylalcohol tend to pick up moisture from the environment, thus reducing the free flowing nature of the ceramic powder. United States Patent 3,472,803 issued October 14, 1969 assigned to Corning Glass Works discloses a ceramic composition for slip casting which comprises 70 to 83 percent of a ceramic material; 4 to 12 percent of a binder which is a copolymer of styrene and butadiene. Preferably the compound contains a sodium salt of a polyacrylic acid optionally in combination with triethanol amine. United States Patent 3,991,029 issued November 9, 1976 assigned to E.I. DuPont de Nemours and Company discloses a ceramic compound for tape casting comprising an internally plasticized thermosetting resin. The polymers contain a self crosslinking monomer selected from glycidyl methacrylate and the n-methylol amides of acrylic or methacrylic acid. Chemical Abstract 102:11330h of Japanese Kokai 59,121,152 [84,121,152] discloses the use of an aqueous based ceramic slip containing from 5 to 20 parts by weight of a copolymer of one or more of acrylic and methacrylic acid and one or more of C₁₋₁₈ mono or polyhydric alcohol esters of (meth)acrylic acid in a weight ratio of 50:50 to 99:1. The esters have a molecular weight of from 20,000 to 500,000 and are used in conjunction with an organic plasticizer, such as di-butyl phthalate. U.S. Patent 4,329,271 issued May 11, 1982 to GTE Products Corporation disclosed a process for tape casting using water soluble polymers. The present invention contemplates the use of polymer emulsions in water. Derwent Accession No. 85-192624/32, an abstract of Japanese Kokai 60/118676 discloses a hot isostatic pressing of a uniform mixture of from 5 to 300 parts by volume of a thermoplastic material such as wax or polyethylene and 100 parts by volume of a ceramic. The soft binder permits the deformation of the ceramic mixture under a fluid pressure medium for the shaping of complex parts. The references do not describe the use of an aqueous emulsion of a polymeric binder nor do they describe the type of treatment contemplated in the present invention. The present invention seeks to provide a process for improving the green fracture strength of ceramic parts. The present invention provides a process for increasing the green fracture strength of a ceramic part, characterised by: i) forming an aqueous based ceramic composition having at least 50 weight percent of solids comprising at least 65 weight percent of a mixture of from 100 to 85 weight percent of ceramic particles, and 0 to 15 weight percent of a flux material; a sufficient amount of an aqueous emulsion of a polymeric binder which has a Tg of from -100 to 120°C, to provide from 0.5 to 35 weight percent of said binder and optionally up to 5 weight percent of a dispersing agent; ii) tape or slip casting a green ceramic part from said slurry; and drying said part under such conditions that the vapour pressure of water in said ceramic composition does not exceed the total ambient presssure; and iii) subjecting said green part to one or more energy treatments selected from electron beam irradiation, x-ray irradiation, ultraviolet irradiation for a period of time sufficient to increase the green fracture strength of said green ceramic part. The present invention is applicable to liquid casting methods such as tape casting or slip molding. In tape casting the liquid ceramic composition is cast as a thin tape. Depending on the application this may be from 30 microns to 0.1 inch (0.254 cm), e.g. 1 to 20 mils (0.00254 to 0.051 cm). Since the films are thin the treatment may be carried out by irradiation such as electron beam, x-ray or ultraviolet light. The utility of ultraviolet irradiation will depend on the ability of the light to pass through the film and the reactivity of the polymeric binder under ultraviolet light. Where ultraviolet irradiation will not pass through the green part, and a short process time is desired the treatment may be selected from electron beam or x-ray irradiation. The ceramic materials useful in the present invention include those known in the industry and not susceptible to derogatory chemical reaction, under the process conditions of this invention. Such ceramics are e.g. non reactive oxides, nitrides and carbides. Examples of such ceramics are alumina, silicon carbide, silicon nitride, zirconia, silica, barium titanate; and mixtures thereof. Silicates are e.g. glass silicates and aluminum silicates. Preferably the ceramic material has a small particle size in the range from 0.5 to 12 microns. Depending on the end use of the ceramic up to 10 percent preferably 0.001 to 5 percent, preferably 0.05 to 1 percent, of the ceramic may be replaced with a flux material or another ceramic such as borides or oxides of lead, iron or tin, or another ceramic such as magnesium oxide. In preparing the fluid ceramic composition the ceramic may be set or dry milled for a period of time sufficient to break up and separate agglomerated material but not further reduce particle size. The length of the milling will depend upon the time it takes to get to the desired particle size. Some times for wet milling are up to 24 hours, preferably from 4 to 18 hours. Wet milling provides a uniform dispersion. In some cases excessive milling may be detrimental to the final ceramic composition. The ceramic is dispersed in water in an amount to provide a ceramic content of not less than 50 weight percent in the final composition. Generally 75 to 85 parts by weight of ceramic are dispersed in from 25 to 15 parts by weight of water. If the ceramic is dry milled an aqueous dispersion of the ceramic is formulated to give the solids content described above. A dispersing agent may be added to the ceramic/water slurry to prevent a reagglomeration of ceramic particles and to form a uniform dispersion. The type of level of dispersing agent should be selected so as not to have a negative impact on the process. Anionic or non ionic dispersing agents may be used with anionic aqueous emulsions of polymeric binder. Similarly nonionic or cationic dispersing agents may be used with cationic aqueous emulsions of polymeric binder. Amphoteric surfactants may be used with both anionic and cationic emulsions. Many useful dispersing agents are listed in McCutcheons' Functional Materials published annually by McCutcheon Division of MC Publishing Co. A particularly useful class of dispersing agents are the poly electrolytes such as Darvan 7 (Trademark of R. T. Vanderbilt Co.). In the preparation of ceramics for use in electronic applications it is believed to be desirable to use a dispersing agent which does not contain high amounts of metallic ions; such dispersing agents include styrene maleic anhydride; Daxad 32 an ammonium salt of a carboxylated polyelectrolyte (Trademark of W. R. Grace and Co.) and Darvan C (a trademark of R. T. Vanderbilt Co.). If present, the dispersing agent is preferably used in the minimum amount to be effective. Generally the dispersant may be used in amounts up to 5 weight percent based on the total weight of the final ceramic compound. Preferably the dispersant is used in amounts of less than 2 weight percent based on the final ceramic composition. After the formation of the ceramic and water dispersion the aqueous emulsions of the polymeric binder is added to it. Preferably the binder is added as a medium solids emulsion containing from 30 to 60 percent polymer. The binder is added in an amount so that the solids level of the resulting composition is not less than 50 percent, preferably in the range 65 to 85 percent. The binders of the present invention are added in the form of an emulsion in water. In selecting a binder the isoelectric point and the surface charge of the ceramic material should be considered. The aqueous emulsion of polymeric binder should not coagulate to any appreciable extent under the conditions of use. In some cases it may be necessary to buffer the ceramic slurry. If a buffer is necessary care should be taken to avoid agents which will contribute undesirable ions to the ceramic slurry. The binder is generally present in the ceramic compound in an amount not greater than 50, preferably less than 35, percent by weight calculated as dry parts of polymer on dry parts of ceramic material. In dry pressing the binder is usually present in an amount of less than 6 weight percent of the dried ceramic composition, preferably from 1 to 3 weight percent. For other applications such as injection molding or roll compaction, the binder content may be as high as 50 weight percent, typically 25 to 40, preferably less than 35, weight percent, for injection molding and isostatic pressing and 5 to 15 weight percent for roll compaction. Preferably the polymers of the present invention are polymers which are film forming at or below 40°C, preferably below room temperature. The polymers should be capable of deformation under pressure and capable of crosslinking or reacting with a crosslinking agent if present upon further energy inputting treatment such as heating, electron beam, ultraviolet light, x-ray, irradiation, etc. Some polymers in accordance with the present invention may be generally characterized as polymers of esters including acrylates, SBR type polymers, ethylene vinyl acetates, NBR's, conjugated diolefins and copolymers or homopolymers of vinyl chloride and vinylidene chloride copolymers of ethylene and vinylidene chloride, copolymers of ethylene and vinyl chloride and homopolymers of vinyl aromatics polymers. The polymers may be in the form of an aqueous emulsion containing up to 70 percent by weight of polymer. Commercially available emulsions of polymers in water generally have a polymeric content from 45 to 60 percent. The polymers may have a Tg from -100 to +120, preferably from -20 to +40°C. For polymers with a relatively high Tg it may be necessary to include a conventional external plasticizer. Some esters are polymers comprising: at least about 50, preferably at least 90, weight percent of one or more C₁₋₆ alkyl or hydroxy alkyl esters of a C₃₋₆ ethylenically unsaturated monocarboxylic acid or a half ester of a C₃₋₆ ethylenically unsaturated dicarboxylic acid; up to 45 weight percent of one or more monomers selected from C₈₋₁₂ vinyl aromatic monomers which may be unsubstituted or substituted by a C₁₋₄ alkyl radical; C₃₋₆ alkenyl nitriles and C₃₋₈ alkenyl or hydroxy alkenyl esters of a C₁₋₈ saturated carboxylic acid; and optionally up to a total of 20 preferably less than 10 weight percent of one or more monomers selected from C₃₋₆ ethylenically unsaturated carboxylic acids; C₃₋₆ ethylenically unsaturated aldehydes; and amides of C₃₋₆ ethylenically unsaturated carboxylic acids which amides may be unsubstituted or substituted at the nitrogen atom by up to two radicals selected from C₁₋₄ alkyl radicals and C₁₋₄ hydroxy alkyl radicals. The amount of ethylenically unsaturated acid should be chosen to give the required rheology properties in the ceramic dispersion. At high pH's highly carboxylated latices tend to swell and are subject to an upward drift in viscosity. A method for controlling this type of viscosity drift by incorporating from 0.1 to 10 percent by weight based on the weight of the polymer of a low molecular weight (100 to 5000) C₂₋₄ alkylene glycol is disclosed in U.S. Patent 4,474,919 issued October 2, 1985 to Polysar Limited. Preferred C₃₋₆ ethylenically unsaturated acids are acrylic acid, methacrylic acid and itaconic acid. Some esters of acrylic and methacrylic acid include methyl acrylate, ethyl acrylate, propyl acrylate, butyl acrylate, pentyl acrylate, hexyl acrylate, hydroxyethyl acrylate, methyl methacrylate, ethyl methacrylate, propyl methacrylate, butyl methacrylate, pentyl methacrylate, hexyl methacrylate, hydroxyethyl methacrylate, and other hydroxy alkyl homologues of the foregoing esters. Homologues of other C₃₋₆ ethylenically unsaturated non carboxylic acids or half esters of dicarboxylic acids are also useful. Some amides are acrylamide, methacrylamide, N-methylol acrylamide, N-methylol methacrylamide. Preferably the polymer contains from about 0.5 to 2.5 weight percent of these amides if they are present. Some vinyl aromatic polymers are styrene, and alpha methyl styrene. Preferably the ester polymers have a Tg from -30 to +30°C, most preferably from -10 to 25°C. Some alkenyl and hydroxy alkenyl esters of C₁₋₈ saturated carboxylic acids are the vinyl esters such as vinyl acetate. These esters may also be referred to as esters of non addition polymerizable carboxylic acids. A particular useful class of acrylate polymers comprises: from 95 to 50, preferably 60 to 80, weight percent of one or more C₁₋₈ alkyl or hydroxyl alkyl esters of acrylic or methacrylic acid; from 1 to 45 preferably 5 to 40 weight percent of a monomer selected from C₈₋₁₂ vinyl aromatic monomers which may be unsubstituted or substituted by a C₁₋₄ alkyl radical and a C₃₋₆ alkenyl nitrile; from 0.5 to 5 weight percent of one or more C₃₋₆ ethylenically unsaturated carboxylic acids; and optionally up to 10, preferably 5, weight percent of one or more amides of a C₃₋₆ ethylenically unsaturated carboxylic acid, which amide may be unsubstituted or substituted at the carbon atom by up to two radicals selected from C₁₋₄ alkyl radicals and C₁₋₄ hydroxy alkyl radicals. Some esters of acrylic and methacrylic have been listed above under the description of acrylic polymers. Vinyl aromatics are preferred monomers in this polymers group. The vinyl aromatic monomers have been discussed above. Some alkenyl nitriles are acrylonitrile, methacrylonitrile and nitriles of higher ethylenically unsaturated carboxylic acids. Some ethylenically unsaturated carboxylic acids are acrylic acid, methacrylic acid, fumaric acid and itaconic acid. Preferably the acids are present in an amount from 0.5 to 3 weight percent of the binder. If present the amide of C₃₋₆ ethylenically unsaturated carboxylic acids is preferably in an amount from 0.5 to 3 weight percent of the binder. Some amides have been discussed above. Preferably the acrylate polymers have a Tg from -20 to 35°C. The polymers of the SBR type have a Tg from -55 to 60°C, preferably from -50 to 40°C. The polymers comprise from 20 to 60, preferably 20 to 40 weight percent of a C₈₋₁₂ vinyl aromatic monomer which may be unsubstituted or substituted by a C₁₋₄ alkyl radical; from 80 to 40, preferably from 80 to 60 weight percent of one or more C₄₋₆ conjugated diolefin which may be unsubstituted or substituted by a chlorine atom; and optionally from 0.5 to 10 preferably from 1.5 to 5 weight percent of one or more C₃₋₆ ethylenically unsaturated carboxylic acids; and optional up to 5 preferably from 0.5 to 3 weight percent of the polymer of an amide of a C₃₋₆ ethylenically unsaturated carboxylic acid which amide may be unsubstituted or substituted at the nitrogen atom by up to two radicals selected from C₁₋₄ alkyl radicals and C₁₋₄ hydroxy alkyl radicals. Some vinyl aromatic monomers have been discussed above. Some C₄₋₆ conjugated diolefins are butadiene and isoprene. Some C₃₋₆ unsaturated carboxylic acids and amide derivatives thereof have been discussed above. The polymer may be a co- or ter-polymer of an alpha olefin and a vinyl ester type monomer or vinyl chloride or vinylidene chloride. Preferably the polymer comprises: from 1 to 25 preferably from 5 to 20 weight percent of one or more C₂₋₃ alpha olefins; from 65 to 99 preferably from 60 to 80 weight percent of one or more monomers selected from a C₃₋₆ ethylenically unsaturated ester of a C₁₋₆ non addition polymerizable carboxylic acid, vinyl chloride and vinylidene chloride; and optionally up to a total of 10 weight percent of one or more monomers selected from C₃₋₆ ethylenically unsaturated carboxylic acids; and C₁₋₄ alkyl or hydroxy alkyl esters of C₃₋₆ ethylenically unsaturated carboxylic acids; amides of a C₃₋₆ ethylenically unsaturated carboxylic acid which amide may be unsubstituted or substituted at the nitrogen atom by up to two radicals selected from C₁₋₄ alkyl radicals and C₁₋₄ hydroxy alkyl radicals; and C₃₋₆ ethylenically unsaturated aldehydes. If present, the acid is used in an amount from 0.5 to 5 weight percent of the polymer. If the amide is present it is also preferred to be used in an amount from 0.5 to 5 weight percent of the polymer. Preferably the polymer will have a Tg from about -20 to 40°C preferably from -20 to 25°C. Some ethylenically unsaturated carboxylic acids and amides thereof have been discussed above. Some olefins are ethylene and propylene. Some unsaturated esters of non addition polymerizable saturated acids are vinyl acetate, vinyl propionate and vinyl formate. The polymer may be nitrile rubber polymer. The polymer may comprise: from 15 to 50, preferably from 20 to 40 weight percent of a C₃₋₆ alkenyl nitrile; from 85 to 50 weight percent of one or more monomers selected from C₈₋₁₂ vinyl aromatic monomers which may be unsubstituted or substituted by a C₁₋₄ alkyl radical; C₄₋₆ conjugated diolefins; and C₁₋₄ alkyl or hydroxy alkyl ester of C₃₋₆ ethylenically unsaturated carboxylic acids; and optionally up to a total of 10 weight percent of one or more monomers selected from C₃₋₆ ethylenically unsaturated carboxylic acids; C₃₋₆ ethylenically unsaturated aldehydes; and amides of C₃₋₆ ethylenically unsaturated carboxylic acids which amides may be unsubstituted or substituted at the nitrogen atom by up to two radicals selected from C₁₋₄ alkyl radicals and C₁₋₄ hydroxy alkyl radicals. Preferably the polymer comprises 20 to 40 weight percent of an alkenyl nitrile from 80 to 60 weight percent of a C₄₋₆ conjugated diolefin and optionally up to 10 percent of styrene or a carboxylic acid monomer. Some monomers have been described above. Generally, the nitriles have a Tg from -50 to +40°C. Preferably the polymers have a Tg from -20°C to +40°C. Some polymers may be homopolymers or copolymers of vinyl chloride or vinylidene chloride. Homopolymers of vinyl chloride are useful. It is also possible to use a copolymer of vinyl chloride and a C₃₋₆ alkylor hydroxy alkyl ester of a C₃₋₆ ethylenically unsaturated carboxylic acid in a weight ratio from 25:75 to 75:25 and optionally up to a total of 10 weight percent of one or more monomers selected from C₃₋₆ ethylenically unsaturated aldehydes; and amides of C₃₋₆ ethylenically unsaturated carboxylic acids which amides may be unsubstituted or substituted at the nitrogen atom by up to two radicals selected from C₁₋₄ alkyl radicals and C₁₋₄ hydroxyalkyl radicals. The homopolymers and copolymers predominantly of the vinyl aromatic monomers are also suitable in the present invention. Some polymers comprise at least 80 percent of a C₈₋₁₂ vinyl aromatic monomer which may be unsubstituted or substituted by a C₁₋₄ alkyl radical; and optionally up to a total of 10 weight percent of one or more monomers selected from C₃₋₆ ethylenically unsaturated carboxylic acids; C₃₋₆ ethylenically unsaturated aldehydes; C₁₋₄ alkyl or hydroxy alkyl esters of C₃₋₆ ethylenically unsaturated carboxylic acids; and amides of C₃₋₆ ethylenically unsaturated carboxylic acids which amides may be unsubstituted or substituted at the nitrogen atom by up to two radicals selected from C₁₋₄ alkyl radicals and C₁₋₄ hydroxy alkyl radicals. Some monomers have been identified above. As used in this specification the term polymeric binder is intended to include polymer systems which may contain an external plasticizer. Most of the polymers of the present invention are soft enough not to require the presence of a plasticizer. Some of the higher Tg acrylates, PVC's, and homopolymers of aromatic monomers may require plasticizers. Some plasticizers are esters such as dioctyl phthalate and the aromatic phosphates. It is known that the molecular weight distribution of the polymer will affect its adhesive properties. The binder may be as disclosed in U.S. Patent 4,508,864 issued April 2, 1985 to Polysar Limited with a molecular weight distribution so that from 20 to 55 percent of the binder has a molecular weight greater than 320,000. The methods for controlling the molecular weight of a polymer are well known in the art and do not form part of the teaching of the present application. One suitable method for controlling the molecular weight distribution of acrylate polymers is discussed in U.S. Patent 3,732,139 issued May, 8, 1973 to Johnson and Johnson. From packing theory, it is known that the particle size distribution of polymer particles in a latex will affect the solids content and rheology of the latex and compounds based on the latex. The particle size distribution of the polymer also effects the adhesion and binding power of the polymer. The particle size of the polymer in the latex should be selected on the basis of the particle size of the ceramic material and the required rheology of the ceramic slurry. One useful particle size distribution in high solids compositions is such that from 65 to 85 weight percent of the polymer particles have a size from 1700 to 3000 A (170 to 300 nm), preferably from 1200 to 1800 A (120 to 180 nm), and from 35 to 25 weight percent of the polymer particles have a particle size from 300 to 1000 A (30 to 100 nm), preferably from 450 to 650 A (45 to 65 nm). A process for obtaining such a particle size distribution is disclosed in British Patent Specification 2,138,830 in the same of Polysar Limited. Depending on the green fracture strength required, the fluid ceramic composition of the present invention may include a crosslinking agent. There are many types of these agents available e.g. sulphur and sulphur containing organic compounds such as carbamyls carbamates and sulfenamides; metal oxides such as zinc oxide or lead oxide; diamines or polyamines such as alkylene diamines e.g. ethylene diamine or hexamethylene diamine, epoxides or polyhydric alcohols such as 1,2,3,4 diepoxide butane, and 3,4 epoxy-6-methyl cyclohexyl methyl 3-4 epoxy-6-methyl cyclohexane carboxylate; diisocyanates such as p-phenylene diisocyanate. Functional groups may be combined in one crosslinking agent such as a diamine and a sulphur containing compounds. In selecting a crosslinking agent care must be taken to ensure that the treatments applied to the ceramic composition prior to the formation of the green part will not result in significant crosslinking which will have a negative effect on the adhesion and binding characteristics of the polymer. While metal compounds are inappropriate in circumstances where the purity of the ceramic is important, in other cases metal ions such as zinc oxide or magnesium oxide may serve a dual purpose of doping the ceramic and crosslinking the binder. For liquid forming processes the ceramic slurry is formed by casting or in a mold and dried under conditions so that the vapor pressure of water in the slurry does not exceed the total pressure of the ambient environment, preferably from room temperature up to 100°C at atmospheric pressure. The green part is then subjected to a treatment in accordance with the present invention, and then subjected to conventional firing. In the process of the present invention the green ceramic part is subject to an energy treatment which will improve the green fracture strength of the part. The total energy input into the entire process must be considered in relation to the mass of polymer and its Tg, and the efficiency of the energy input in the last step of the process. The total energy input should be controlled so that only after formation of the green part is the green fracture strength of the part maximized. For irradiation the dosage and type of irradiation will depend on the amount of polymer and the mass of the ceramic. Preferred irradiation techniques include electron beam, and x-ray irradiation. In thin films ultraviolet light may be sufficient to achieve the required green fracture strength. In some cases the ultra violet light will not quickly cause an increase in green fracture strength. In such cases the ceramic composition may include small amounts of catalysts which are activated under UV light such as the benzoin ether. These compounds may be benzoin allyl ether and benzoin C₃₋₅ alkyl ethers. In the formation of the green part the green density of the ceramic material should be at least 50 percent, preferably at least 55 percent of the theoretical density of the ceramic. It should be noted that it is desirable to achieve a green density as high as possible in the ceramic part as the density variation of 1 or 2 percent in the green part may cause a variation in the density and/or the uniformity of the sintered product. Without being bound by theory it is believed that the Tg of the polymer is significant. Higher Tg polymers give higher green strength but are more difficult to deform in the mold. Prolonged irradiation may cause polymer degradation and a loss of green strength. This loss of strength can, to a reasonable extent, be guarded against by incorporating an antioxidant into the fluid ceramic composition. Care should be taken in the amount and type of antioxidant used, if any, as this may increase the heat treatment required to "burn out" the binder and/or interfere with the improvements in green fracture strength. It is best to test the ceramic compositions by spray drying them then pressing pellets from the powder and subjecting them to various irradiation treatments to determine optimum composition and process conditions to be used. The resulting green part is then fired. Firing will affect the final density of the ceramic. Generally firing for a longer time or at higher temperatures tends to produce a ceramic with a final density closer to theoretical density. Firing conditions will vary depending on the ceramic. For alumina typical firing conditions are from 1300 to 1550°C for from 2 to 5 hours, preferably 2 to 3 hours. The following example is intended to illustrate the invention and not to limit it. In the example unless otherwise indicated the parts are parts by weight. Example A master batch slurry was prepared using Reynolds calcined alumina RC-HP DBM alumina (trademark) containing 0.050 wt. percent of magnesium oxide as a fluxing aid. The slurry composition comprised: The master batch was charged to a one gallon milling crock filled to 50 percent of its volume with 1.2 cm ceramic balls, and milled for 18 hours. The milled master batch was a smooth dispersed slurry and was recovered through a 325 mesh screen. The viscosity was 70 Cp and the pH was 9.2. To 96.8 grams of master batch slurry was added a sufficient amount of Polysar Latex AL-608 (acrylate-type, Tg: -9°C) as an emulsion having a 40 percent solids content and Santicizer 160 (trademark of Monsanto Co. for butyl benzyl phthalate) to give a master batch of ceramic slurry comprising by dry weight 50 parts of ceramic material, 2 parts of Polysar Latex AL-608 and 2 parts of Santicizer 160 The binder emulsions are generally commercially available at more than 40 percent solids but are diluted to 40 percent solids for mixing. The resulting composition was placed in a jar, which was then placed on its side and agitated vigorously on a table shaker for 1 hour. The ceramic was cast on a polypropylene film at 0.007 inch (0.018 cm) wet thickness and dried at room temperature for 18 hours. The film was then cut into several strips. The control was not subject to any further treatment. The samples of the material were then subject to UV treatments for various lengths of time at 30 minutes, 1 hour, 4 hours, and 24 hours. The temperature in the UV device was 60°C (140°F). The UV source was provided by three General Electric sun lamps of 275 watts each. The distance from the UV source was 10 inches (25.4 cm). Dumbbell samples were punched from the tape and the tensile strength of the ceramic (using a pull test rather than a crush test) were determined on an Instron. The results are reported in the Table. There is a decline in properties after the initial strength improvement. It is not clear why this occurs. It is speculated that the polymer may be degrading. Per se this is not undesirable as ultimately the polymer must be burned out. This demonstrates the need to control the energy input into the ceramic. With energy inputs which operate in a very narrow range with relative intensity it is important to select an energy input with the best efficiency (i.e. select the appropriate wave length for UV etc.) In the present application, numerical values indicate their precise values and their "about" values, e.g. "50" includes the precise value "50" and "about 50". The present invention includes any embodiment of the present invention, e.g. as indicated above and below, for instance: Aqueous dispersions of binders may be used to make a slurry of a ceramic material. The slurry may then be shaped to a green part by conventional techniques such as tape casting. The tensile strength of the green part may be increased by subjecting the green part to an energy treatment such as irradiation, e.g. ultraviolet (UV), X-rays and electron beams.

Claims: A process for increasing the green fracture strength of a ceramic part, characterised by: i) forming an aqueous based ceramic composition having at least 50 weight percent of solids comprising at least 65 weight percent of a mixture of from 100 to 85 weight percent of ceramic particles, and 0 to 15 weight percent of a flux material; a sufficient amount of an aqueous emulsion of a polymeric binder which has a Tg of from -100 to 120°C, to provide from 0.5 to 35 weight percent of said binder and optionally up to 5 weight percent of a dispersing agent; ii) tape or slip casting a green ceramic part from said slurry; and drying said part under conditions such that the vapour pressure of water in said ceramic composition does not exceed the total ambient pressure; and iii) subjecting said green part to one or more energy treatments selected from electron beam irradiation, X-ray or ultraviolet irradiation, for a period of time sufficient to increase the green fracture strength of said green ceramic part. A process according to claim 1, characterised by said binder comprising a polymer selected from: i) polymers comprising at least 60 weight percent of one or more C₁₋₆ alkyl or hydroxy alkyl esters of a C₃₋₆ ethylenically unsaturated monocarboxylic acid or a half esters of a C₃₋₆ ethylenically unsaturated dicarboxylic acid; up to 40 weight percent of one or more monomers selected from C₈₋₁₂ vinyl aromatic monomers which may be unsubstituted or substituted by a C₁₋₄ alkyl radical and C₃₋₆ alkenyl nitriles; and C₃₋₈ alkenyl or hydroxy alkenyl esters of a C₁₋₈ saturated carboxylic acid and optionally up to a total of 10 weight percent of one or more monomers selected from C₃₋₆ ethylenically unsaturated carboxylic acids; C₃₋₆ ethylenically unsaturated aldehydes; and amides of C₃₋₆ ethylenically unsaturated carboxylic acids which amides may be unsubstituted or substituted at the nitrogen atom by up to two radicals selected from C₁₋₄ alkyl radicals and C₁₋₄ hydroxy alkyl radicals; ii) polymers comprising: from 20 to 60 weight percent of a C₈₋₁₂ vinyl aromatic monomer which may be unsubstituted or substituted by a C₁₋₄ alkyl or hydroxy alkyl radical from 80 to 40 weight percent of one or more C₄₋₆ conjugated diolefins which may be unsubstituted or substituted by a chlorine atom; and optionally up to a total of 10 weight percent of one or more monomers selected from C₃₋₆ ethylenically unsaturated carboxylic acids; C₃₋₆ ethylenically unsaturated aldehydes; C₁₋₄ alkyl and hydroxy alkyl esters of C₃₋₆ ethylenically unsaturated carboxylic acids and amides of C₃₋₆ ethylenically unsaturated carboxylic acids with amides may be unsubstituted or substituted at the nitrogen atom by up to two radicals selected from C₁₋₄ alkyl radicals and C₁₋₄ hydroxy alkyl radicals. iii) polymers comprising: i) from about 1 to 25 weight percent of one more C₂₋₃ alpha olefins; from about 65 to 99 weight percent of one or more monomers selected from a C₃₋₆ ethylenically unsaturated ester of a C₁₋₆ non addition polymerizable carboxylic acid, vinyl chloride, and vinylidene chloride; and optionally up to a total of 10 weight percent of one or more monomers selected from C₃₋₆ ethylenically unsaturated carboxylic acids; C₃₋₆ ethylenically unsaturated aldehydes; C₁₋₄ alkyl and hydroxy alkyl esters of C₃₋₆ ethylenically unsaturated carboxylic acids and amides of C₃₋₆ ethylenically unsaturated carboxylic acids which amides may be unsubstituted or substituted at the nitrogen atom by up to two radicals selected from C₁₋₄ alkyl radicals and C₁₋₄ hydroxy alkyl radicals. iv) polymers comprising homopolymers of vinyl chloride and vinylidene chloride; v) polymers comprising: from 15 to 50 weight percent of a C₃₋₆ alkenyl nitrile; from 75 to 50 weight percent of one or more monomers selected from: C₈₋₁₂ vinyl aromatic monomers which may unsubstituted or substituted by a C₁₋₄ alkyl radical; C₄₋₆ conjugated diolefins; and C₁₋₄ alkyl or hydroxy alkyl esters of C₃₋₆ ethylenically unsaturated carboxylic acids; and optionally up to a total of 10 weight percent of one or more monomers selected from C₃₋₆ ethylenically unsaturated carboxylic acids; C₃₋₆ ethylenically unsaturated aldehydes; and amides of C₃₋₆ ethylenically unsaturated carboxylic acids which amides may be unsubstituted or substituted at the nitrogen atom by up to two radicals selected from C₁₋₄ alkyl radicals and C₁₋₄ hydroxyalkyl radicals. vi) polymers of one or more monomers selected from C₄₋₆ conjugated diolefins; and vii) copolymers of from 75 to 25 weight percent vinyl chloride or vinylidene chloride and one or more monomers selected from 25 to 75 weight percent of C₃₋₆ alkyl or hydroxyalkyl esters of C₃₋₆ ethylenically unsaturated carboxylic acids; and optionally up to a total of 10 weight percent of one or more monomers selected from C₃₋₆ ethylenically unsaturated carboxylic acids; C₃₋₆ ethylenically unsaturated aldehydes; and amides of C₃₋₆ ethylenically unsaturated carboxylic acids which amides may be unsubstituted or substituted at the nitrogen atom by up to two radicals selected from C₁₋₄ alkyl radicals and C₁₋₄ hydroxyalkyl radicals. viii)a polymer comprising at least about 80 percent of a C₈₋₁₂ vinyl aromatic monomer which may be unsubstituted or substituted by a C₁₋₄ alkyl radical; and optionally up to a total of 10 weight percent of one or more monomers selected from C₃₋₆ ethylenically unsaturated carboxylic acids; C₃₋₆ ethylenically unsaturated aldehydes; C₁₋₄ alkyl or hydroxy alkyl esters of C₃₋₆ ethylenically unsaturated carboxylic acids; and amides of C₃₋₆ ethylenically unsaturated carboxylic acids which amides may be unsubstituted or substituted at the nitrogen atom by up to two radicals selected from C₁₋₄ alkyl radicals and C₁₋₄ hydroxyalkyl radicals. A process according to claim 1 or 2, characterised by ceramic material has a particle size from 0.5 to 12 microns and is selected from alumina, silicon carbide, silicon nitride, zirconia, silica, barium titanate and mixtures thereof. A process according to claims 1 to 3, characterised by latex has a bimodal particle size distribution so that from 65 to 85 weight percent of the particles have a size from 1700 to 3000 A (170 to 300 nm) and 35 to 15 weight percent of the particles have a size from 300 to 1000 A (30 to 100 nm). A process according to claims 1 to 4, characterised by said dispersing agent is present in an amount of less than 2 weight percent based on the ceramic composition and is a carboxylated polyelectrolyte. A process according to claims 1 to 5, characterised by said binder is present in an amount from 0.5 to 6 weight percent based on the dry weight of the ceramic material and is a polymer having a Tg from -20 to +35°C comprising at least 90 percent of one or more monomers selected from C₁₋₆ alkyl or hydroxyalkyl esters of acrylic or methacrylic acid; and optionally up to a total of 10 weight percent of one or more monomers selected from C₃₋₆ ethylenically unsaturated carboxylic acids; C₃₋₆ ethylenically unsaturated aldehydes; and amides of C₃₋₆ ethylenically unsaturated carboxylic acids which amides may be unsubstituted or substituted at the nitrogen atom by up to two radicals selected from C₁₋₄ alkyl radicals and C₁₋₄ hydroxyalkyl radicals. A process according to claims 1 to 6, characterised by said binder is present in an amount from 0.5 to 6 weight percent based on the dry weight of the ceramic material and is a styrene-acrylate polymer comprising: from 50 to 95 weight percent of one or more C₃₋₅ alkyl or hydroxy alkyl ester of acrylic or methacrylic acid; from 5 to 40 weight percent of one or more monomers selected from C₈₋₁₂ vinyl aromatic monomers which may be unsubstituted or substituted by a C₁₋₄ alkyl radical; and optionally up to a total of 10 weight percent of one or more monomers selected from C₃₋₆ ethylenically unsaturated carboxylic acids; C₃₋₆ ethylenically unsaturated aldehydes; and amides of C₃₋₆ ethylenically unsaturated carboxylic acids which amides may be unsubstituted or substituted at the nitrogen atom by up to two radicals selected from C₁₋₄ alkyl radicals and C₁₋₄ hydroxyalkyl radicals. A process according to claims 1 to 7, characterised by said binder is present in an amount from 0.5 to 6 weight percent based on the dry weight of the ceramic material and is a polymer comprising: from 1 to 25 weight percent of one or more C₂₋₃ alpha olefins; from 65 to 99 weight percent of a C₃₋₆ ethylenically unsaturated ester of a C₁₋₆ non addition polymerizable carboxylic acid; and optionally up to a total of 10 weight percent of one or more monomers selected from C₃₋₆ ethylenically unsaturated carboxylic acids; C₃₋₆ ethylenically unsaturated aldehydes; and amides of C₃₋₆ ethylenically unsaturated carboxylic acids which amides may be unsubstituted or substituted at the nitrogen atom by up to two radicals selected from C₁₋₄ alkyl radicals and C₁₋₄ hydroxy alkyl radicals. A green ceramic part produced according to claims 1 to 8.

Inventors: GURAK, NUR RECEP, JOSTY, PETER LYN, RUSSELL, JAMES POWELL, THOMPSON, RONALD JAMES, XANTHOPOULO, VALENTINO GEORGE
Applicants: BASF AKTIENGESELLSCHAFT
Application year: 1987
Main classification: C04B35
IPC codes: C04B35, C09J11