PLATE-LIKE MAGNETOPLUMBITE TYPE FERRITE PARTICLES FOR MAGNETIC RECORDING AND MAGNETIC RECORDING MEDIA USING THE SAME

Abstract: Ba-containing plate-like magnetoplumbite type ferrite particles for magnetic recording have the composition AO·n{(Fe 1-x M x )₂O₃} wherein A represents Ba or Ba and Sr, M represents Zn and Ti or Zn, Co and Ti, n is from 6.5 to 11.0 and x is from 0.05 to 0.25 and exhibit a change of coercive force at a temperature of from 20 to 120°C of from 159 A m⁻¹/°C to +159 A m⁻¹/°C (-2.0 Oe/°C to +2.0 Oe/°C).

Description: The present invention relates to plate-like magnetoplumbite type ferrite particles for magnetic recording, to their preparation and to magnetic recording media which incorporate them. With the advancement of technology for longer recording times and with the smaller size and weight of magnetic video and audio recording and reproducing devices in recent years, the necessity has grown for higher performance of magnetic recording media such as magnetic tapes, magnetic discs, etc. Especially, high-density recording by magnetic recording media is required acutely. Magnetic recording media are generally produced by coating a resin composition containing magnetic particles on a substrate. According to the conventional recording system, the acicular magnetic particles such as acicular γ-Fe₂O₃ particles or Co-coated acicular γ-Fe₂O₃ particles have been oriented in the longitudinal direction on the plane of the magnetic recording medium and recording has been made by making use of the remanent magnetization in the direction. For attaining high-density recording, it is necessary to shorten the recording wavelength. However, according to the conventional recording system, because of the necessity of shortening the major axis of the acicular magnetic particles for short wavelength recording, the influence of the dimagnetizing field between the particles would increase to cause a drop of reproducing output, so that this system was disadvantageous for high-density recording. As a high-density recording system, there has been proposed recently a so-called perpendicular magnetic recording system in which recording is performed by making use of the remanent magnetization in the direction perpendicular to the longitude of the magnetic recording medium, and this system is reaching the stage of practical application. According to this perpendicular magnetic recording system, since the magnetic particles are oriented in the direction perpendicular to the longitude of magnetic recording medium and arranged so that the particles of opposite magnetic polarities adjoin each other, there hardly arises the influence of diamagnetizing field between the particles even when short wavelength recording is conducted. Further, since the adjoining particles strengthen their magnetization each other, the drop of output is lessened. Thus, this system is suited for high-density recording. As mentioned above, the development of perpendicular magnetic recording media capable of high-density recording is most acutely required at present. As such magnetic recording media, there are known ones made by coating on a substrate a resin composition containing the Ba-containing plate-like magnetoplumbite type ferrite particles as for instance disclosed in JP-A-55-86103 (1980). Extensive studies have been conducted in recent years for the development of plate-like magnetoplumbite type ferrite particles and practical use of the recording media coated with such particles, and in accordance with the advancement of such studies, request has mounted not only for the improvement of electro-magnetic performance and durability which are normally required for the recording media but also for the magnetic (especially coercive force) stability to temperature (hereinafter referred to simply as temperature stability). Such request is based on the following fact. Magnetic recording is made by magnetizing the magnetic recording medium with a magnetic field generated by the magnetic head, but it becomes impossible to carry out the best mode of recording if the coercive force of the magnetic recording medium varies due to a rise of temperature caused by an environmental change, even if the magnetic field of the magnetic head and the value of coercive force, which is a magnetization component of the recording media, have been adjusted at room temperature so as to allow the best mode of recording. The properties such as electromagnetic performance of magnetic recording media are closely associated with the properties of the magnetic particles used therefor. Regarding the properties of the Ba-containing magnetoplumbite type ferrite particles, it is usually required of such particles that they have an average particle diameter of 0.01 to 0.3 µm and are excellent in dispersibility, that their coercive force can be controlled in the range of 300 to 2,000 Oe, and that the magnetization value is as high as possible. Control of coercive force in the range of 300 to 2,000 Oe is necessary for enabling recording by the currently used ferrite type magnetic heads. For reducing the coercive force of plate-like magnetoplumbite type ferrite particles, it has been proposed to replace part of Fe (III) in the ferrite with Ti (IV) and Co (II), or Co (II) and divalent metal ions M (II) such as Mn, Zn, etc. As to the magnetization value, it is required that such magnetization value is as large as possible. This is mentioned in, for instance, JP-A-56-149328 (1981) which states: "Magnetoplumbite ferrite used as a material for magnetic recording media is required to have as large a degree of saturation magnetization as possible..." The requirement that the plate-like magnetoplumbite type ferrite particles for magnetic recording should be as small in size as possible, especially not greater than 0.3 µm, is also mentioned in many literatures. For instance, JP-A-56-125219 (1981) states: "The utility of perpendicular magnetic recording for longitudinal magnetic recording becomes apparent in the recording wavelength region below 1 µm. For conducting satisfactory recording and reproduction in this wavelength region, it is desirable that the crystal particle size of the ferrite particle is less than about 0.3 µm. However, since no desired ferromagnetism is provided when the crystal particle size becomes smaller than 0.01 µm, a crystal particle size in the range of 0.01 to 0.3 µm is practically required." There is no end to the requirement for the improvement of properties of plate-like magnetoplumbite type ferrite particles for magnetic recording. The strong request for temperature stability in addition to the proper coercive force, large magnetization value and a proper average particle size is explained by the fact that while magnetic recording is made by magnetizing the magnetic particles in the magnetic recording medium with a magnetic field generated by the magnetic head, it becomes impossible to carry out the best mode of recording if the coercive force of the magnetic particles varies due to a rise of tempereature caused by an environmental change, even if the magnetic field of the magnetic head and the value of coercive force, which is a magnetization component of the magnetic particles, have been adjusted at room temperature so as to allow the best mode of recording. The Ba-containing plate-like magnetoplumbite type ferrite particles having a proper coercive force, a large magnetization, a proper average particle size and excellent temperature stability, and the magnetic recording media capable of high-density recording are most strongly required at present. The plate-like magnetoplumbite type ferrite particles and the media coated with such particles are known as the particles and media that satisfy the property requirements, but the Ba-containing plate-like magnetoplumbite type ferrite particles tend to increase in coercive force as the temperature rises, and thus such particles are poor in temperature stability. This phenomenon is evident from the disclosures in the June, 1986, issue of "METALS" (published by Agness) volume 6, 1986, Special Edition "Magnetic Materials" which states on page 10: "The coercive force of barium ferrite particles increases with the rise of temperature...", and on page 12: "The coercive force of magnetic recording media and the change of saturation magnetization by temperature are decided by the magnetic particles used. It has been confirmed that even in the barium ferrite media, the coercive force and saturation magnetization show the same characteristics as the temperature characteristics of magnetic particles shown in Fig. 4." As means for improving the temperature stability of Ba-containing plate-like magnetoplumbite type ferrite particels, there is known, for instance, the method disclosed in JP-A-61-152003 (1986). According to the method of this JP-A-61-152003 (1986), the plate-like barium ferrite particles containing the elements for reducing coercive force, such as Co (II) and Ti (IV), are heat-treated in a reducing atmosphere at 300-700°C, but this method has the problem that the heat-treatment increases the coercive force more than twice that before the treatment, and it is difficult to control the coercive force to a proper level. Therefore, when a magnetic recording media is produced by using the Ba-containing plate-like magnetoplumbite type ferrite particles, the obtained magnetic recording media has an elevated coercive force, and as a result it is difficult to perform recording with a conventional ferrite-made magnetic head. Thus, the establishment of a process for producing the Ba-containing plate-like magnetoplumbite type ferrite particles having a proper level of coercive force and excellent temperature stability has been strongly desired. As a result of extensive studies for obtaining the Ba-containing plate-like magnetoplumbite type ferrite particles having a proper level of coercive force and excellent temperature stability, it has been found that the Ba-containing plate-like magnetoplumbite type ferrite particles having the composition of AO·n{(Fe 1-X M X )₂O₃} (wherein A represents Ba or Ba and Sr, M represents Zn and Ti, or Zn, Co and Ti, n = 6.5-11.0, and x = 0.05-0.25) and the change of coercive force at a temperature of 20-120°C in the range of -2.0 Oe/°C to +2.0 Oe/°C, obtained by mixing Ba material, Fe material and substituting elements, viz. Zn material, Ti material and Co material, in the specified ratios, heating and calcining the mixture at a temperature of from 750 to 950°C in the presence of a flux, crushing the calcined product and washing it with water and an acid, are the plate-like magnetoplumbite type ferrite particles having a proper level of coercive and excellent temperature stability, and magnetic recording media coated with such particles also have a proper level of coercive force and excellent temperature stability. The present invention has been attained on the basis of this finding. In the first aspect of the present invention, there is provided Ba-containing plate-like magnetoplumbite type ferrite particles for use in magnetic recording, which particles have the composition AO·n{(Fe 1-X M X )₂O₃} wherein A represents Ba or Ba and Sr, M represents Zn and Ti, or Zn, Co and Ti, n is from 6.5 to 11.0 and x is from 0.05 to 0.25 and exhibit a change of coercive force at a temperature of from 20 to 120°C of from -159 A m⁻¹/°C to +159 A m⁻¹/°C (-2.0 Oe/°C to +2.0 Oe/°C). In a second aspect of the present invention, there is provided a magnetic recording medium comprising a substrate coated with a resin composition containing, as the magnetic material, the Ba-containing plate-like magnetoplumbite type ferrite particles according to the invention. BRIEF DESCRIPTION OF THE DRAWING FIG. 1 is an electron microphotograph (x 100,000) of the Ba-containing magnetoplumbite type ferrite particles obtained in Example 1. The present invention is concerned with Ba-containing plate-like magnetoplumbite type ferrite particles having the composition AO·n{(Fe 1-X M X )₂O₃} (wherein A represents Ba or Ba and Sr, M represents Zn and Ti, or Zn, Co and Ti, n is from 6.5 to 11.0 and x is from 0.05 to 0.25), and magnetic recording media obtained by coating a resin composition containing said particles on a substrate, which have excellent temperature stability. More specifically, the Ba-containing plate-like magnetoplumbite type ferrite particles according to the present invention show a change of coercive force at a temperature of 20-120°C in the range of -2.0 Oe/°C to +2.0 Oe/°C. Especially, in the case where the Ba-containing plate-like magnetoplumbite type ferrite particles of the present invention contain Co in addition to Zn and Ti, the change of coercive force at a temperature of from 20-120°C is from -119 A m⁻¹/°C to +119 A m⁻¹/°C (-1.5 Oe/°C to +1.5 Oe/°C). Also, the magnetic recording media coated with a resin composition containing the Ba-containing plate-like magnetoplumbite type ferrite particles of the present invention exhibit a change in coercive force of from -2.0 Oe/°C to +2.0 Oe/°C in the temperature range of 20-90°C. In the case of the magentic recording media coated with a resin composition containing the Ba-containing plate-like magnetoplumbite type ferrite particles containing Zn, Co and Ti, the change of coercive force at a temperature of from 20 to 90°C is in the range of from -1.5 Oe/°C to +1.5 Oe/°C. The reason why the Ba-containing plate-like magnetoplumbite type ferrite particles with excellent temperature stability can be obtained by the process of the present invention is not yet definitely known. However in view of the fact that Ba-containing plate-like magnetoplumbite type ferrite particles with excellent temperature stability can not be obtained either in the case of Ba-containing plate-like magnetoplumbite type ferrite particles having the composition AO·n{(Fe 1-X M X )₂O₃} in which n is outside the range of 6.5-11.0 or in the case of particles having the composition AO·n{(Fe 1-X M X )₂O₃} in which n is 6.5-11.0 and M is Zn or Ti, it is considered that the excellent temperature stability of the particles of the present invention is attributable to a synergistic effect due to substituting part of Fe (III) with both Zn and Ti in the specified range in the ferrite and the magnetoplumbite type ferrite particles. The Ba-containing plate-like magnetoplumbite type ferrite particles according to the present invention have the composition of AO·n{(Fe 1-X M X )₂O₃} wherein n is from 6.5 to 11.0 and x is from 0.05 to 0.25. When n is less than 6.5, the change of coercive force in the temperature range of from 20 to 120°C. becomes greater than +2.0 Oe/°C, and the object of the present invention can not be attained. When n is greater than 11.0, a non-magnetic phase or spinel ferrite phase may be allowed to exist in the composition, resulting in a reduced magnetization value. When x is less than 0.05, the change of coercive force in the temperature range of from 20 to 120°C becomes greater than +2.0 Oe/°C, and the object of the present invention can not be attained. When x is greater than 0.25, there may east a non-magnetic phase or spinel ferrite phase in the composition to reduce the magnetization value. The Ba-containing plate-like magnetoplumbite type ferrite particles of the present invention are prepared by a process which comprises (i) mixing a Ba material such as barium carbonate (optionally, part of the Ba material may be substituted with an Sr material such as strontium carbonate), an Fe material such as hematite, magnetite, maghemite, goethite, etc., and substituting elements, viz. a Zn material such as zinc oxide, zinc carbonate, zinc hydroxide, etc., a Ti material such as titanium oxide and optionally a Co material such as cobalt carbonate, cobalt hydroxide, basic cobalt carbonate (2CoCO₃·3Co(OH)₂·H₂O), etc. in the required proportions; (ii) heating and calcining the thus obtained mixture at a temperature of from 750 to 950°C in the presence of a flux; and (iii) crushing the calcined product and washing it with water and an acid. As the flux used in the present invention, one or more of the halides of alkali metals and alkali earth metals, sulfates, silicates and the like can be used. The amount of such flux is 15 to 100% by weight based on the weight of the Fe material. When the amount of the flux is less than 15% by weight based on the weight of the Fe material, the ferrite-forming reaction is not effected to a satisfactory degree, with the result that the unreacted material may remain and also the particle size distribution of the produced particles is broadened, so that, in this case, the object of the present invention can not be attained. It is possible to obtain the Ba-containing plate-like magnetoplumbite type ferrite particles of the present invention even when the amount of the flux in step (ii) exceeds 100% by weight based on the weight of the Fe material, but it is meaningless to let the flux exist in a greater amount than actually needed. When the calcining temperature is less than 750°C, the ferrite-forming reaction is not effected sufficiently and the unreacted material remains. When the calcining temperature exceeds 950°C, there takes place sintering of the particles and between the particles, so that the produced particles prove unsuited for use as magnetic particles for magnetic recording. A magnetic recording medium according to the present invention is prepared by a method which comprises coating a substrate with a resin composition containing the Ba-containing plate-like magnetoplumbite type ferrite particles of the invention as the magnetic material. The resin composition may further contain one or more additives such as dispersants, lubricants, abrasives, antistatic agents, etc. As the substrate for the magnetic recording media according to the present invention, there can be used the films of synthetic resins such as polyethylene terephthalate, polyethylene, polypropylene, polycarbonate, polyethylene naphthalate, polyamide, polyamide-imide, polyimide, polysulfone, etc., foils and plates of metals such as aluminum, stainless steel, etc., and various types of paper which are commonly used in the production of magnetic recording media. As the resins usable in the present invention, vinyl chloride-vinyl acetate copolymer, vinyl chloride-vinyl acetate-maleic acid urethane elastomer, butadiene-acrylonitrile copolymer, polyvinyl butyral, cellulose derivatives such as nitrocellulose, polyester resin, synthetic rubber resins such as polybutadiene, epoxy resin, polyamide resin, polyisocyanate polymer, radiation cured type acrylic urethane resin, and mixtures thereof, which are generally used in the production of magnetic recording media may be exemplified. Owing to their composition of AO·n{(Fe 1-X M X )₂O₃} (wherein A represents Ba or Ba and Sr, M represents Zn and Ti, or Zn, Co and Ti, n is from 6.5 to 11.0, and x is from 0.05 to 0.25), the Ba-containing plate-like magnetoplumbite type ferrite particles according to the present invention have a proper coercive force and excellent temperature stability, especially a change of coercive force at a temperature of from 20 to 120°C in the range of from -2.0 Oe/°C to +2.0 Oe/°C , so that they are best suited for use as plate-like magnetoplumbite type ferrite particles for magnetic recording which are most keenly required at present. Typically the Ba-containing plate-like magnetoplumbite type ferrite particles of the present invention have an average particle diameter of 0.05 to 0.3 µm, preferably 0.05 to 0.2 µm, a coercive force of 300 to 2,000 Oe, preferably 500 to 1,700 Oe (3.98 x 10⁴ to 1.35 x 10⁵ A m⁻¹), a magnetization of 45 to 60 emu/g, preferably 50 to 60 emu/g (50 to 60 A m²/kg) and a temperature stability (the change of coercive force in the temperature range of 20-120°C) of -2.0 Oe/°C to +2.0 Oe/°C, preferably -1.5 Oe/°C to +1.5 Oe/°C. Further, because of use of the Ba-containing plate-like magnetoplumbite type ferrite particles having a proper coercive force and excellent temperature stability, the magnetic recording media according to the present invention also have a proper coercive force and excellent temperature stability, especially the change of coercive force at a temperature of 20-90°C in the range of -2.0 Oe/°Cto +2.0 Oe/°C, so that these media are best suited for use as magnetic recording media for high-density recording which are most intensely required at present. More specifically, the magnetic recording media according to the present invention are the ones having a coercive force of 300 to 2,000 Oe, preferably 550 to 1,700 Oe, and a temperature stability (the change of coercive force in the temperature range of 20-90°C) of -2.0 Oe/°C + 2.0 Oe/°C , preferably -1.5 Oe/°C + 1.5 Oe/°C . The following Examples illustrate the present invention. In the following Examples and Comparative Examples, the average diameter of the particles was measured by electron microphotographs. The magnetic properties of the Ba-containing magnetoplumbite type ferrite particles were determined under an external magnetic field of 10 KOe by using "Sample Vibrating Type Magnetometer VSM-3S-15" (made by Toei Kogyo KK), and the properties of the magnetic recording media were determined by applying an external magnetic field of 10 KOe vertically to the surface of each magnetic recording medium. The temperature stability of the Ba-containing plate-like magnetoplumbite type ferrite particles and the magnetic recording media was shown by the value (Oe/°C) obtained by dividing the difference between coercive force at 20°C and that at 90°C by the temperature difference (70°C) in the case of the magnetic recording media, and by dividing the difference between coercive force at 20°C and that at 120°C by the temperature difference (100°C) in the case of the Ba-containing magnetoplumbite type ferrite particles. Preparation of Ba-containing plate-like magnetoplumbite type ferrite particles: Example 1 195 g of barium carbonate, 1,070 g of magnetite, 131.8 g of zinc oxide, 116.2 g of titanium oxide and a flux comprising 250 g of NaCl and 250 g of Na₄SiO₄ were supplied into an alumina-made crucible and heated and calcined at 800°C for 1.5 hours by using an electric furnace. The calcined product was crushed in the conventional method and, after removing the flux by washing, filtered and dried to obtain the brown particles. The thus obtained ferromagnetic brown particles had an average diameter of 0.07 µm from an electron microphotograph shown in FIG. 1, and the results of fluorescent X-ray analysis and X-ray diffraction confirmed that these particles were the magnetoplumbite type ferrite particles having the composition of BaO.8.19{(Fe 0.818 Zn 0.096 Ti 0.0860 )₂O₃}. These particles of the composition showed a coercive force Hc of 530 Oe, a magnetization of 53.4 emu/g and a temperature stability of -1.3 Oe/°C. Examples 2-7 and Comparative Examples 1-2 Ba-containing plate-like magnetoplumbite type ferrite particles were obtained in the same process as Example 1 except that the kind and amount of the Fe material, the kind and amount of the Ba or Ba and Sr material, the kind and amount of the Zn material, the kind and amount of the Ti material, the kind and amount of the flux, and the calcining temperature and time were changed. The main preparation conditions used in the Examples and Comparative Examples are shown in Table 1, and the properties of the obtained particles are shown in Table 2. Production of magnetic recording media : Example 8 100 parts by weight of the Ba-containing magnetoplumbite type ferrite particles obtained in Example 1, 14 parts by weight of VAGH (vinyl choloride-vinyl acetate-vinyl alcohol copolymer, made by U.C.C. Ltd., USA), 1 part by weight of myristic acid, 30 parts by weight of toluene, 30 parts by weight of metyl ethyl ketone, 1 part by weight of Al₂O₃ powder and 2 parts by weight of carbon black were kneaded together for 90 minutes by using a kneader. The kneaded material was diluted by adding 45 parts by weignt of toluene and 45 parts by weight of methyl ethyl ketone and then mixed and dispersed for 3 hours by a sand grinder. To the resulting dispersion was added 140 parts by weight of a methyl ethyl ketone solution containing 14 parts by weight of solids of a polyurethane resin (Nipporan 2304, made by Nippon Polyurethane Kogyo KK), followed by 30-minute mixing and filtration, and the filtered material was mixed with 3 parts by weight of coronate L (a trifunctional low-molecular weight isocyanate compound, made by Nippon Polyurethane Kogyo KK) to prepare a magnetic coating print. This magnetic coating print was coated on a 12 µm thick polyester base film and then dried to form a 4 µm thick magnetic coat, and this coated film was calendered and then cut to a width of 3.81 mm to make a magnetic tape. The thus obtained magnetic tape showed the following magnetic properties: coercive force of 570 Oe; saturation flux density Bm of 1,340 Gauss; residual flux density Br of 427 Gauss; squareness ratio Br/Bm of 0.319. It also showed a temperature stability of -1.4 Oe/°C. Examples 9-14 and Comparative Examples 3-4 Magnetic recording media were obtained in the same process as Example 8 except that the type of Ba-containing magnetoplumbite type ferrite particles used was changed. The properties of the obtained magnetic recording media are shown in Table 3.

Claims: Ba-containing plate-like magnetoplumbite type ferrite particles suitable for use in magnetic recording media, which particles have the composition AO.n{(Fe 1-X M X )₂O₃} wherein A represents Ba or Ba and Sr, M represents Zn and Ti, or Zn, Co and Ti, n is from 6.5 to 11.0 and x is from 0.05 to 0.25 and exhibit a change of coercive force at a temperature of from 20 to 120°C of from -159 A m⁻¹/°C to +159 A m⁻¹/°C (-2.0 Oe/°C to + 2.0 Oe/°C). Particles according to claim 1, wherein M represents Zn, Co and Ti and the change of coercive force at from 20 to 120°C is from -119 A m⁻¹/°C to +119 A m⁻¹/°C (-1.5 Oe/°C to +1.5 Oe/°C). Particles according to claim 1 or 2 having an average particle diameter of 5 x 10⁻⁸ to 2 x 10⁻⁷m (0.05 to 0.2 µm), a coercive force of from 3.98 x 10⁴ to 1.35 x 10⁵ A m⁻¹ (500 to 1,700 Oe) and a magnetization of 50 to 60 A m²/kg (50 to 60 emu/g). A process for the preparation of particles as defined in claim 1, which process comprises: (i) mixing a Ba material, optionally a Sr material, a Fe material, a Zn material, a Ti material and, optionally, a Co material in the required proportions; (ii) heating and calcining the thus-obtained mixture at a temperature of from 750 to 950°C in the presence of a flux; and (iii) crushing and washing the calcined product with water and an acid. A process according to claim 4, wherein the Ba material is barium carbonate and the optional Sr material is strontium carbonate. A process according to claim 4 or 5, wherein the Fe material is hematite, magnetite, maghemite or goethite. A process according to any one of claims 4 to 6, wherein the Zn material is zinc oxide, zinc carbonate or zinc hydroxide, the Ti material is titanium oxide and the optional Co material is cobalt carbonate, cobalt hydroxide or basic cobalt carbonate. A magnetic recording medium comprising a substrate coated with a resin composition containing, as the magnetic material, particles as claimed in any one of claims 1 to 3 or which have been prepared by a process as claimed in any one of claims 4 to 7. A medium according to claim 8, wherein the resin compostion further contains one or more additives selected from dispersants, lubricants, abrasives and antistatic agents. A method of preparing a magnetic recording medium, which method comprises coating a substrate with a resin composition containing, as the magnetic material, particles as claimed in any one of claims 1 to 3 or which have bee prepared by a process as claimed in any one of claims 4 to 7.

Inventors: FUJITA, RYUJI, HORIISHI, NANAO, SANADA, KAZUTOSHI, YAMAMOTO, SHIGEHISA
Applicants: TODA KOGYO CORP.
Application year: 1987
Main classification: G11B5
IPC codes: G11B5