PROCESS FOR THE PREPARATION OF A MODIFIED ELASTOMERIC POLYMER

Abstract: Process for introducing a conjugated diolefin linkage in an elastomeric polymer by (a) reacting the polymer having an active group containing an alkali metal atom with a 2,3-ethylenically unsaturated aldehyde or ketone to produce an alkali metal salt, (b) converting this salt into the corresponding alcohol, and (c) dehydrating this alcohol.

Description: The invention relates to a process for the preparation of a modified elastomeric homopolymer or modified elastomeric copolymer. Elastomeric homopolymers and copolymer of various monomers are, of course, well known in the prior art. Moreover, polymers of this type having at least one active group comprising an alkali metal atom are also well known. In general, polymers comprising at least one alkali metal atom are prepared by polymerizing the monomers, either alone or in combination with other monomers, in the presence of an organometallic catalyst, wherein the metal is an alkali metal, particularly lithium, at a temperature within the range of from -150°C to 300°C. Copolymers prepared in this manner may be block, tapered or random. Polymers of this type are described in a large number of references including, for example, U.S. patent specifications Nos. 3,135,716; 3,150,209; 3,265,765; 3,231,635; 3,322,856; 3,496,154; 3,498,960; 4,145,298 and 4,298,202. It is also known in the prior art, that the reactive group or groups containing the alkali metal atom, particularly a lithium atom, may be reacted with various reagents to replace the alkali metal atom with a more stable reactive group. Such conversion is taught, for example, in U.S. patent specification Nos. 3,135,716 and 3,150,209. The reactive groups thus incorporated are said to facilitate curing through crosslinking or coupling. It is also known in the prior art to incorporate one or more carboxyl groups into an elastomeric polymer and then using the thus modified copolymer in various applications, such as a modifier for thermosetting polyester resin compositions and in various other applications requiring polymers with adhesive properties. Incorporation of the carboxylic containing copolymer into polyester resin compositions may be via physical admixture as taught in the background sections of U.S. patent specifications Nos. 4,439,438 and 4,400,478 as well as U.S. patent specification No. 4,329,438 or via chemical incorporation of the carboxyl containing polymer into the polyester as is taught in U.S. patent specification No. 3,892,819. In general, elastomeric homopolymers of conjugated diolefins and/or elastomeric copolymers of at least one conjugated diolefin and at least one other vinyl monomer, particularly an alkenyl substituted aromatic monomer, have, heretofore, been incorporated into thermosetting unsaturated polyester resin compositions in an effort to improve both the surface characteristics and the impact resistance of cured moulded products. Physical incorporation of such thermoplastic modifiers has, however, heretofore frequently resulted in destructive phase separation of the components in the polyester resin composition and the properties of the cured products are frequently inferior to rather than superior to those obtained with a conventional polyester resin composition. The use of polymers comprising pendant carboxyl groups apparently reduces the negative results heretofore realized when a thermoplastic polymer was incorporated into an otherwise conventional thermosetting polyester resin composition but as indicated in the background section of U.S. patent specification 4,329,438 none of these approaches has been completely successful. The need, then, for an improved elastomeric modifier suitable for polyester resin compositions is believed to be readily apparent. It has now been discovered that the foregoing and other disadvantages of the prior art elastomeric polymers useful as modifiers can be overcome or at least significantly reduced with the modified elastomeric polymer prepared according to the present invention. It is, therefore, an object of the present invention to provide a process for the preparation of said improved modified elastomeric polymer. It is another object of this invention to provide such an elastomeric polymer which is useful to impart impact resistance to a thermosetting unsaturated polyester resin composition. It is still another object of this invention to provide such an improved elastomeric polymer which is particularly effective in imparting impact resistance when used in sheet and bulk molding applications. It is yet another object of this invention to provide such an improved elastomeric polymer which when used in a thermosetting resin composition will impart improved surface characteristics. It is an even further object of this invention to provide such an improved elastomeric polymer which can be incorporated into a thermosetting unsaturated polyester resin composition without resulting in destructive phase separation. The foregoing and other objects and advantages will become apparent from the description set forth hereinafter. Accordingly, the invention provides a process for the preparation of a modified elastomeric homopolymer or modified elastomeric copolymer, which process comprises introducing at least one conjugated diolefin linkage in said elastomeric homopolymer or copolymer with the aid of a process comprising the steps of: a) reacting an elastomeric homopolymer or elastomeric copolymer having at least one active group containing an alkali metal atom with a 2,3-ethylenically unsaturated aldehyde or 2,3-ethylenically unsaturated ketone to produce an alkali metal salt; b) converting the alkali metal salt from step (a) to the corresponding alcohol; and c) dehydrating the alcohol from step (b). As indicated hereinbefore, the present invention deals with an elastomeric homopolymer or copolymer which has been chemically treated to incorporate a conjugated diolefin linkage therein. In general, any of the elastomeric homopolymers or copolymers known in the prior art may be chemically treated to incorporate a conjugated diolefin linkage in accordance with the present invention. Useful elastomeric polymers, then, include those prepared in bulk, suspension, solution and emulsion processes. As is well known, polymerization of monomers to produce an elastomer may be accomplished with free-radical, cationic and anionic initiators or polymerization catalyst. As indicated more fully hereinafter, however, it is important, in the process of this invention, that the elastomeric polymer comprise at least one active group containing an alkali metal atom when it is treated to incorporate the conjugated diolefin linkage. As a result, elastomeric polymers prepared with free-radical or cationic initiators, as well as those prepared with an anionic initiator and then deactivated, must be metallated to incorporate at least one active site comprising an alkali metal atom prior to treatment thereof to incorporate the conjugated diolefin linkage by the process according to the invention. Metallization may, of course, be accomplished using techniques well known in the prior art such as the method taught in U.S. patent specification No. 4,145,298. Notwithstanding that any elastomeric polymer may be modified by the process of the present invention, the process of this invention is simplified when the treated polymer is prepared via anionic initiation using an organo alkali metal compound initiator and then treated in accordance with the process of this invention prior to deactivation of the alkali metal active site. The invention will, then, be described in greater detail by reference to the treatment of such polymers. Any elastomeric polymer metallated to incorporate at least one active site containing an alkali metal atom could, however, be substituted for the preferred elastomers referred to in the description. The process of the present invention is, then, particularly effective with diene homopolymers and copolymers which are prepared via anionic polymerization with an organo metallic catalyst, wherein said metal is an alkali metal, particularly lithium, since the active groups comprising the alkali metal atom may be readily treated to incorporate a conjugated diolefin linkage. Diene homopolymers and copolymers prepared via other techniques, as well as other elastomers, may, however, be metallated so as to comprise at least one active site containing an alkali metal atom, using methods well known in the prior art, and then treated to incorporate a conjugated diolefin linkage in accordance with the present invention. Diene homopolymers and copolymers comprising at least one terminal active group containing an alkali metal atom and prepared via anionic polymerization techniques, which polymers are particularly useful in the present invention, may be prepared in accordance with techniques well known in the prior art. In general, such polymers are prepared by contacting the monomer or monomers to be polymerized with an organo alkali metal compound in a suitable solvent at a temperature within the range from -150°C to 300°C. Particularly effective polymerization initiators are organo lithium compounds having the general formula RLi n wherein R is an aliphatic, cycloaliphatic or aromatic hydrocarbon radical having from 1 to 20 carbon atoms and n is an integer of 1 to 4. In general, the polydienes useful in the present invention will have a molecular weight within the range of from 2,000 to 200,000 and when the polydiene is a copolymer of 1 or more diolefins and 1 or more other monomers, the polydiene will comprise from 20 to 99 wt% monomeric diolefin units. In general, the polydiene useful in this invention may be a polymer of one or more dienes, containing from 4 to 12 carbon atoms such as, for example, 1,3-butadiene, isoprene, piperylene, 2- and 3-methyl-pentadiene, phenylbutadiene, 3,4-dimethyl- 1,3-hexadiene and, 4,5-diethyl-1,3-octadiene, preferably conjugated dienes containing 4 to 8 carbon atoms per molecule. Moreover, one or more of the hydrogen atoms in these diolefins may be substituted with a halogen atom. The polydiene may also be a copolymer of one or more of the aforementioned diolefins and one or more other monomers. Other monomers which may be used include vinylaryl compounds such as, for example, styrene, various alkylstyrenes, paramethoxystyrene, vinylnaphthalene and vinyltoluene. Preferably, the block copolymer comprises in the range of from 20 to 99 per cent by weight of said diolefin block and in the range of from 1 to 80 per cent by weight of an alkenyl-substituted aromatic hydrocarbon block. Other monomers which may be used include heterocyclic nitrogen-containing monomers such as pyridine and quinoline derivatives containing at least one vinyl or α-methyl vinyl group such as, for example, 2-vinylpyridine, 3-vinylpyridine and 4-vinylpyridine. Still other useful comonomers include, for example, acrylic and methylacrylic acid esters, vinyl halides, vinylidene halides and various vinyl esters. The diene homopolymers and copolymers useful in the present invention include those terminally reactive homopolymers and copolymers described in U.S. patent specifications Nos. 3,135,716; 3,150,209; 3,496,154; 3,498,960; 4,145,298 and 4,238,202. Those diene homopolymers and copolymers having only one terminal lithium atom, and described in U.S. patent specifications Nos. 3,150,209; 3,496,154; 3,498,960; 4,145,298 and 4,238,202, are particularly useful in the present invention. The copolymer may be either random, block or tapered. Diene copolymers useful in the present invention also include the block copolymers prepared in accordance with the methods described in U.S. patent specifications Nos. 3,231,635; 3,265,765 and 3,322,856, the disclosure of which patent specifications are incorporated herein by reference. Particularly useful block copolymers are those block copolymers having the general formulae B x -(A-B) y and A x -(B-A) y wherein A and B are as defined in the aforementioned U.S. patent specifications Nos. 3,231,635; 3,265,765 and 3,322,856, A being a polymer block of an alkenyl-substituted aromatic hydrocarbon and B a polymer block of a conjugated diene, x is a number equal to 0 or 1 and y is a whole number from 1 to about 15. As indicated supra, it is, at least, desirable in the present invention that the diene homopolymer or copolymer treated comprise at least one active site containing an alkali metal atom, preferably a lithium atom. In the event that the diene homopolymer or copolymer to be treated in the present invention does not contain such an active group, the polymer may first be treated to incorporate such a group. As well known in the prior art, at least one active site containing an alkali metal atom, particularly a lithium atom, may be incorporated into a polymer by contacting said polymer with an organo alkali metal compound in a suitable solvent or diluent at a temperature within the range from about 0 to about 200°C. In general, any of the organo alkali metal compounds known in the prior art to be useful as polymerization initiators may be used in the reaction to create an active site containing an alkali metal atom. As also well known in the prior art, the metallization reaction may be promoted with various amines and alkoxide salts. To produce an elastomeric homopolymer or copolymer comprising at least one conjugated diolefin linkage in accordance with the present invention, one will start with an elastomeric homopolymer or copolymer containing at least one alkali metal atom. For convenience, an elastomeric polymer comprising at least one active group containing an alkali metal atom is frequently referred to hereinafter as either an active or living polymer. To incorporate the conjugated diolefin linkage, then, an active or living polymer is treated by reacting the same first with a 2,3-ethylenically unsaturated aldehyde (1) or ketone (2) having, respectively, the general formula I wherein R₁ represents a hydrogen atom or an aliphatic, cycloaliphatic, aryl or alkyl-substituted aryl hydrocarbon group having in the range of from 1 to 10 carbon atoms; and the general formula II wherein R₁ is as defined in general formula I and R₂ is an aliphatic, cycloaliphatic, aryl or alkyl-substituted aryl hydrocarbon group having in the range of from 1 to 10 carbon atoms; and thereafter converting the resulting lithium salt to the corresponding alcohol and then dehydrating the alcohol. As is well known in the prior art, the latter two steps may be accomplished, in effect, simultaneously when an excess of acid is used to convert the lithium salt to the corresponding alcohol at an elevated temperature. In general, reaction of the 2,3-ethylenically unsaturated aldehyde or ketone with the active or living polymer will be accomplished in a suitable solvent at a temperature within the range from 10°C to 200°C. Nominal holding times at reaction conditions will, generally, range from 1 to 120 minutes. Suitable solvents include any of the solvents known in the prior art to be effective for use during preparation of the diene homopolymer or copolymer. These include hydrocarbons such as paraffins, cycloparaffins, alkyl-substituted cycloparaffins, aromatics and alkyl-substituted aromatics containing from about 4 to about 10 carbon atoms per molecule. Suitable solvents include, for example, benzene, toluene, cyclohexane, methylcylohexane, n-butane, n-hexane and n-heptane. In general, the reaction between the living polymer and the 2,3-ethylenically unsaturated aldehyde or ketone proceeds stoichiometrically. It will, then, generally, be sufficient to combine 1 mol of 2,3-ethylenically unsaturated aldehyde or ketone for each mol of active sites to be converted. In this regard, it should be noted that if the living polymer contained, on average, two active groups containing alkali metal atoms per polymer segment, it would take 2 mol of ethylenically unsaturated aldehye or ketone per mol of polymer to convert all of the active sites to the corresponding alkali metal salt. Similarly, if the living polymer contained only, on average, one active site containing an alkali metal atom per polymer segment, it would take only 1 mol of unsaturated aldehyde or ketone per mol of polymer to convert all of the active sites to the corresponding lithium salt. The alkali metal salt produced by reacting the living polymer with a 2,3-ethylenically unsaturated aldehyde or ketone is next converted to the corresponding alcohol. Any of the methods known in the prior art to be effective for such conversions may be used in the present invention. One such method is to simply react the alkali metal salt with an acid. In general, any acid, organic or inorganic, may be used. Suitable acids, then, include the series of aliphatic carboxylic acids starting with formic acid, the series of aromatic carboxylic acids starting with benzoic acid and the various mineral acids such as, for example, hydrochloric acid, nitric acid and sulphuric acid. After the corresponding alcohol has been produced, the same will be dehydrated to yield the desired conjugated diolefin structure. Generally, this may be accomplished simply by heating the alcohol. More expediently, however, this may accomplished by effecting the acid treatment with an excess of acid at an elevated temperature. In a preferred embodiment of the present invention, then, the acid treatment will be accomplished at a temperature within the range from 40°C to 200°C. Generally, nominal holding times within the range from 1 to 120 minutes will be sufficient to permit both conversion of the alkali metal salt to the corresponding alcohol and dehydration of the alcohol. Again, conversion of the alkali metal salt to the alcohol will occur stoichiometrically. Notwithstanding, an excess amount of acid will generally be used during the conversion of the alkali metal salt to the corresponding alcohol since the excess of acid will catalyze the dehydration. The elastomeric homopolymer or copolymer thus produced and containing at least one conjugated diolefin structure may be recovered from solution using conventional technology well known in the prior art or used directly in the preparation of a modified polyester as described and claimed in U.S. patent application Serial No. 948,374, filed on even date. As indicated hereinbefore, the modified elastomeric polymer prepared according to the present invention may be used in various unsaturated polyester resins for the purpose of improving impact resistance in structures moulded therewith. The modified elastomer may be added directly to such thermosetting compositions or the same may first be, in effect, grafted on to the backbone of a polyester used in such compositions as described in the afore-mentioned copending application. In a preferred embodiment of the present invention, a polydiene block copolymer will be treated so a to incorporate a conjugated diolefin group into said block copolymer. The block copolymer may be prepared using the method described in U.S. patent specification 3,231,635 and may comprise a single alkenyl-substituted aromatic hydrocarbon block and a single diolefin block. The block copolymer used in the preferred embodiment may be represented by the general formula A-B wherein A and B are, respectively, polymer blocks of an alkenyl-substituted aromatic hydrocarbon and a diolefin. In the preferred embodiment, the alkenyl-substituted aromatic hydrocarbon block will have a weight average molecular weight within the range of from 1,000 to 100,000 and the diolefin block will have a weight average molecular weight within the range of from 1,000 to 150,000. In a most preferred embodiment, the alkenyl-substituted aromatic hydrocarbon will be styrene and the diolefin will be a conjugated diolefin; viz., either butadiene or isoprene. In the preferred embodiment, the block copolymer will be treated in accordance with this invention before the active site formed during polymerization has been converted or deactivated. In the preferred embodiment, the block copolymer will contain, on average, approximately one active site containing a lithium atom per polymer segment, which active site will be on the diolefin block. In the preferred embodiment, the living block copolymer will first be reacted with acrolein to produce the corresponding lithium salt and then with about a 10 wt.% excess of sulphuric acid at elevated temperature to, in effect, simultaneously form the corresponding alcohol and to dehydrate said alcohol. In the preferred embodiment, treatment of the active polymer will be accomplished in the same solvent as was used for polymerization. The reaction between the living polymer and acrolein will be accomplished at a temperature within the range from 10°C to 200°C and preferably from 25°C to 150°C at a nominal holding time within the range from 1 to 120 minutes. The resulting lithium salt will then be reacted with a monocarboxylic acid at a temperature within the range from 40°C to 200°C at a nominal holding time within the range from 1 to 120 minutes. In a most preferred embodiment of the present invention, the acid will be sulphuric acid. The preferred modified polymers of this invention, which modified polymers are prepared by using the preferred operating conditions, may then be recovered. The following Examples further illustrate the invention. Example 1 Preparation of styrene-butadiene block copolymer The block copolymer was prepared under anhydrous and anaerobic conditions in a closed, glass reaction vessel. Initially, styrene (13.1g) dissolved in cyclohexane (170g) was charged to the reaction vessel along with n-butoxy-t-butoxy ethane (100µl) and a 0.25N solution of s-butyllithium (3ml). The reaction vessel was heated to 50°C and when the polymerization of styrene was substantially complete polymerization grade butadiene monomer (24.1g) was added to the vessel. Polymerization of the diene monomer was allowed to proceed substantially to completion and the resulting styrene-butadiene living block copolymer was quenched by the addition of an excess of methyl alcohol. The nonfunctionalized styrene- butadiene block copolymer was then recovered as crumb by coagulation with and excess of methyl alcohol. Analysis of the recovered product indicated that the block copolymer contained a single block of styrene having a weight average molecular weight of 13,400 and a single butadiene block having a weight average molecular weight of 29,400. Preparation of three styrene-butadiene block copolymers containing a single acrolein end group Three styrene-butadiene block copolymers containing a single acrolein end group were prepared according to steps (a) and (b) of the process according to the present invention. For convenience, these polymer samples have been identified as A, B and C. Each sample was prepared by repeating the polymerization steps summarized in this Example for the preparation of styrene-butadiene block copolymer but before deactivating the lithium atom with methyl alcohol the living diblock copolymer was titrated with acrolein until the pale yellow color of the living anionic polymer had disappeared. The end-capped block copolymer was then contacted with an aliquot of ammonium chloride in methyl alcohol to deactivate the lithium atom. Each of the three samples were recovered by coagulating with an excess of methyl alcohol. After recovery, each sample was analyzed to determine the weight average molecular weight of each block and the amount of coupled products in each sample. These results are shown in the following table: Acrolein Capped Block Copolymers A B C Molecular Weight of Styrene Block (x10⁻³) 14.4 13.3 13.3 Molecular Weight of Butadiene Block (x10⁻³) 29.1 29.1 29.5 Coupled Product (% by weight) 4 5 5 Preparation of styrene-butadiene block copolymer containing a cyclic anhydride moiety The acrolein capped polymers identified as A and B in this Example were combined and dissolved in 600ml cyclohexane. The solution was then divided into two equal sized aliquots and each aliquot treated with an excess of maleic anhydride to produce an elastomer having a cyclic anhydride moiety chemically bonded thereto through a 6-carbon atom cyclic structure containing one carbon-carbon double bond and to dehydrate the alcohol which was produced in this Example, the dehydration being step (c) of the process according to the present invention. The treatment was accomplished by adding maleic anhydride (0.25g) to each aliquot and then heating both to reflux and holding each at this temperature for four hours. The resulting reaction products were then recovered as a crumb by coagulating in excess methyl alcohol. The elastomer thus produced could be substituted for a portion of the unsaturated dicarboxylic acid or anhydride monomer in any of the polyester resin operations hereinbefore discussed. Example 2 Preparation of modified unsaturated polyester The acrolein capped polymer identified as C in Example 1 was dissolved in xylene (215ml) and combined with 10g of a maleate/propylene glyclol unsaturated polyester resins (known under the trade name Koppers 3702-5 unsaturated polyester resin). Three drops of concentrated H₂SO₄ were then added to this solution and the solution heated to reflux temperature and held at this temperature for four hours. The H₂SO₄, inter alia, acted as a catalyst for the Diels Alder reaction. As a result of this treatment, the alcohol produced in Example 1 was dehydrated (step (c) according to the present invention) and the conjugated diolefin group produced then reacted with the maleate/propylene glyclol unsaturated polyester resin. The product was contacted with an excess of methyl alcohol, a good solvent for the polyester resin. As a result of the contacting with methyl alcohol, the reaction product of the end-capped elastomer and the polyester and any unreacted end-capped elastomer were precipitated while any unreacted polyester remained in solution. After separation, the coagulated product was subjected to infra-red (IR) analysis to confirm the presence of grafted polyester therein. This was confirmed by a peak occurring at 1640 cm⁻¹. Signals in the IR spectrum at 690 cm⁻¹ and 920 cm¹ also indicated that the coagulated product contained styrene- butadiene block copolymer. The relative intensities of the IR signals indicated that the modified polyester contained significant amounts of both of the polymeric reactants. Example 3 and Comparative Experiment X A portion of the block copolymer produced in Example 1 and a portion of the acrolein modified block copolymer produced in Example 1 and identified as C were dissolved in styrene monomer at a concentration of 30% by weight of polymer in said solution. A 50g aliquot of each solution was then treated with 3 drops of sulphuric acid and blended with an equal weight of solution (about 70% by weight of unsaturated polyester) containing Koppers 3702-5 unsaturated polyester, the same polyester which was modified in Example 2, in styrene. The blending was accomplished at 500 revolutions per minute (rpm) for 3 minutes using a 2.54cm jiffy blade positioned in a 0.23kg jar. Each of the blends were then set aside and observed to determine whether gross phase separation would occur. The observations are summarized in the following table: Blend Phase Separation Comp. Exp. X with styrene-butadiene block complete after 2 days Example 3 co-polymer of example 1 with acrolein modified block co-polymer of example 1 no separation after 7 days Example 4 and Comparative Experiment Y Blends were prepared with the polymers described in example 1 under "Preparation of styrene-butadiene block copolymer" and example 2 and Koppers 3702-5 polyester. These resin blend were then used in the preparation of Sheet Moulding Compound pastes. Each of the pastes were prepared according to the following recipe: 100g Block Copolymer in Styrene Monomer (30wt% polymer) 100g Koppers 3702-5 Unsaturated Polyester Resin (70wt% in styrene) 300g Calcium Carbonate 6g Zinc Stearate 0.5g Black pigment 2.6g t-Butyl perbenzoate 0.5g PEP-100 Cure Promoter 7.8g Marinco H Thickening Agent Each paste was blended in an 800ml plastic beaker using a 2.54 cm Jiffy Mixer blade at 500rpm. The fully blended pastes were then transferred to 0.46kg jars, sealed and set aside to age. After 18 days, the paste were inspected to access the homogeneity of the blend. The paste samples were evaluated for (1) the lack of exudate formation, (2) the absence of chalkiness and (3) smoothness. Each criteria was rated on a scale from 1 (worst) to 5 (best) so that a superior paste would get a combined score of 15, and the worst possible score would be 3. The results of each of the paste are summarized in the following table: Paste Numerical Rating Comp. Exp. Y with polymer of example 1 3 Example 4 with polymer of example 2 9

Claims: A process for the preparation of a modified elastomeric homopolymer or modified elastomeric copolymer, which process comprises introducing at least one conjugated diolefin linkage in said elastomeric homopolymer or copolymer with the aid of a process comprising the steps of: a) reacting an elastomeric homopolymer or elastomeric copolymer having at least one active group containing an alkali metal atom with a 2,3-ethylenically unsaturated aldehyde or 2,3-ethylenically unsaturated ketone to produce an alkali metal salt; b) converting the alkali metal salt from step (a) to the corresponding alcohol; and c) dehydrating the alcohol from step (b). A process as claimed in claim 1 in which said 2,3-ethylenically unsaturated aldehyde has the general formula I wherein R₁ represents a hydrogen atom or an aliphatic, cycloaliphatic, aryl or alkyl-substituted aryl hydrocarbon group having in the range of from 1 to 10 carbon atoms. A process as claimed in claim 2 in which the aldehyde is acrolein. A process as claimed in claim 1 in which said ketone has the general formula II wherein R₁ represents a hydrogen atom or an aliphatic, cycloaliphatic, aryl or alkyl-substituted aryl hydrocarbon group having in the range of from 1 to 10 carbon atoms and R₂ represents an aliphatic, cycloaliphatic, aryl or alkyl-substituted aryl hydrocarbon group having in the range of from 1 to 10 carbon atoms. A process as claimed in any one of the preceding claims in which the reaction of step (a) is carried out at a temperature in the range of from 10°C to 200°C. A process as claimed in claim 5 in which the reaction of step (a) is carried out at a temperature in the range of from 25°C to 150°C. A process as claimed in any one of the preceding claims in which steps (b) and (c) are carried out simultaneously by reacting said alkali metal salt with an excess of acid in step (b) at a temperature within the range from 40°C to 200°C. A process as claimed in claim 7 in which said acid is sulphuric acid. A process as claimed in any one of the preceding claims in which said elastomer is a copolymer of at least one diolefin having in the range of from 4 to 12 carbon atoms per molecule and at least one alkenyl-substituted aromatic hydrocarbon. A process as claimed in claim 9 which said copolymer is a block copolymer. A process as claimed in claim 10 in which said block copolymer comprises a single alkenyl-substituted aromatic hydrocarbon block and a single diolefin block. A process as claimed in claim 11 in which said active group comprising an alkali metal is attached to said diolefin block. A process as claimed in claim 12 in which said alkali metal is lithium. A process as claimed in any one of claims 11 to 13 in which said block copolymer comprises in the range of from 20 to 99 per cent by weight of said diolefin block and in the range of from 1 to 80 per cent by weight of said alkenyl-substituted aromatic hydrocarbon block.

Inventors: BROEKHUIS, ANTONIUS AUGUSTINUS
Applicants: SHELL INTERNATIONALE RESEARCH MAATSCHAPPIJ B.V.
Application year: 1987
Main classification: C08F8
IPC codes: C08F8, C08L67, C08C19, C08F299