CATALYSTS

Abstract: A CO shift catalyst comprises the calcined form of a pre­ cursor of the approximate formula, the precursor having a layer structure, (Cu+Zn)₆Al x R y (CO₃)OH 12+2(x + y) nH₂O where R is lanthanum, cerium or zirconium x is not les than 1 and not greater than 4; y is not less than 0.01 and not greater than 1.5 n is approximately 4

Description: The invention relates to catalysts, and in particular to CO shift catalysts useful in reactions of the type A typical application for the conversion of carbon monoxide to carbon dioxide and water by the water gas shift reaction is in the production of hydrogen or synthesis gas for ammonia production. The reaction is exothermic and hence the lower the operating temperature of the catalyst, the lower the CO content in the product gas. The reaction is facilitated in the presence of a catalyst. It is usual to carry out the conversion in two stages, one at high temperature, typically 330°C to 540°C, the other at low temperature, typically 190° to 260°. Each stage requires a catalyst: for high temperature shift it is usual to use a catalyst comprising iron oxide and chromium oxide and for low temperature it is usual to use a catalyst comprising copper, zinc oxide and alumina. While the iron oxide/chromium oxide catalyst will last for several years, the low temperature shift catalysts have a more limited life. A catalyst may be prepared by making a precursor and subjecting that to calcination/reduction prior to use. It is convenient and more meaningful to those skilled in the art to define that catalyst in terms of the formula of the precursor prior to calcination or reduction and that convention will be adopted in this specification. In EP-A-0155868 there is discloses a catalyst precursor comprising copper, aluminium and lanthanum or cerium, the atomic ratio of (Cu + Zn): Al being in the range of 1.5 to 6: 1 and the ratio of (Cu + Zn): La or Ce is 600 to 4: 1. A catalyst made from such a precursor does not have sufficient thermal stability and hydrothermal stability. It has now been discovered that by modifying the ratios of the elements so that the precursor has a layer structure comprising positively charged brucite like layers alternating with negatively charged interlayers, the catalysts formed can be of increased stability, in particular thermal stability and hydrothermal stability. The activity of the catalyst is maintained or improved. In one aspect the invention provides a catalyst comprising the calcined form of a precursor, the precursor comprising copper, zinc, aluminium and lanthanum or cerium, the atomic ratio of (Cu + Zn): Al being the range of 1.5 to 6: 1 and the ratio of (Cu + Zn): La or Ce is 600 to 4: 1, characterised in that the precursor is of the formula Where R is lanthanum, cerium or zirconium x is not less that 1 and not greater than 4 y is not less than 0.01 and not greater than 1.5 n is approximately 4 the atomic ratio of (Cu + Zn): Al is 1.5 to 4: 1 and the element R is present in a ratio of (Cu + Zn): R of 600 to 40: 1, and the precursor has a hydrotalcite layer structure comprising positively charged brucite like layers alternating with negatively charged interlayers. Preferably Cu: Zn is 1: 1; R is lanthanum, and x and y are in the range of 1.5 to 3 and 0.01 and 0.1 respectively. It is further preferred that the atomic ratio of Cu + Zn: Al is 3: 1 and that the ratio of Cu + Zn: La is 600 to 40.1, preferably about 150: 1. It will be noted that the precursor has a hydrotalcite layer structure. By this we mean that there are positively charged brucite like layers e.g [(Cu.Zn)₆.Al₂. La(OH)₁₆] alternating with negatively charged interlayers e.g (CO₃ 4H₂O)²⁻. The number and disposition of the hydrotalcite layers will depend on the ratio of (Cu + Zn): Al. At the atomic ratio of (Cu + Zn): Al of about 3: 1 the precursor will be almost pure hydrotalcite layer compound whereas at higher or lower ratios phases of copper and zinc containing compounds are present. At lower ratios discrete phases free of alumina are formed. Such a precursor when subjected to calcination gives catalysts of desirable surface area, copper crystallite size and pore volume. These lead in turn to high thermal stability and hydrothermal stability. The proportion of element R should be selected to be the minimum for a beneficial effect, and a maximum below the concentration at which in addition to being present in the precursor the additive forms a discrete layer or phase. Where the lanthanum is used the lanthanum component may be derived from pure lanthanum salts or mixtures of rare earth salts particularly lanthanum and cerium mixtures in which lanthanum is the major component. In the formula anions other than the carbonate may be present, examples being nitrate, phosphate. The precursor may be made in a variety of ways. In one technique, the precursor is made by co-precipitation under controlled conditions of pH and temperature by the addition of alkalis such as sodium carbonate, sodium hydroxide, ammonium bicarbonate or ammonium hydroxide. After precipitation, the material is filtered, washed and dried at elevated temperatures. It has been found that the removal of impurities such as sodium ions may be facilitated if the material is dried at an elevated temperature prior to washing. The washed and dried material is preferably only partially calcined at a temperature of 220°C to 300°C prior to forming into a suitable shape for process requirements. In another aspect the invention provides a method of forming a catalyst as defined by first forming a catalyst precursor and then calcining the precursor, the precursor being formed by co-precipitating copper, zinc, aluminium and the R element from a solution of their salts by reaction with alkali, and recovering the precipitate characterised in that the pH and temperature of the solution are kept substantially constant throughout the reaction so that the precursor formed comprises a lager structure defined above. The pH of the solution will be about 9, and the temperature about 80°C. The precursor may be calcined or reduced and used as a catalyst or it may be mounted in a porous carrier, in Known manner, the form being chosen to meet the requirements of the particular process. In a much preferred feature of the invention the porous carrier is a preformed low surface area ceramic matrix. In such a case, the catalyst precursor of the invention may be incorporated in a porous ceramic matrix. To achieve this, coprecipitation of the copper, zinc, aluminium and R metals in the porous ceramic matrix may be induced using a homogeneous precipitation technique using a readily hydrolysable material such as urea. In another aspect the invention therefore provides a method of making a catalyst as defined and located in a porous body, comprising introducing a solution of salts of the components within the pores of a preformed low surface area ceramic matrix and decomposing the metal salts to metal oxide or hydroxide form by heating e.g. by calcining, wherein the solution also contains a hydrolysable material and after the solution of salts and hydrolysable material has been introduced into the pores of the ceramic matrix, the body is heated to a temperature suitable for controlled hydrolysis of the hydrolysable material thereby increasing the pH to precipitate the metal components within the pores whereby the metal components are almost exclusively confined to the pores. Preferably the preformed low surface area ceramic matrix has an apparent porosity in the range 15% to 80% and has a mean pore diameter in the range of 0.1 micron to 20 micron. The matrix may be the wall of a hollow shape such as hollow spheres. The preformed low surface area ceramic matrix may be alpha - alumina but other preformed low surface matrices of ceramic materials such as silicon carbide, aluminosilicates, silica etc., may be used. By the use of this type of carrier the supported catalyst has improved refractoriness and useful life. The preformed low surface area ceramic matrix may be pretreated with acid or alkali to modify the interaction of the catalytically active material and the ceramic matrix. The surface of the ceramic matrix may also be modified by the addition of "spacer/support" material e.g. alumina within the pores of the ceramic matrix prior to the addition of the active phase. This may be accomplished by the simple impregnation of the ceramic matrix with a soluble salts of the "spacer/support" material, e.g. aluminium nitrate or by using the homogeneous precipitation technique. In each case the temperature of the calcination of the impregnated preformed low surface area ceramic matrix must be carefully controlled to achieve the required surface properties. Preferably the preformed alpha - alumina matrix is impregnated, under vacuum, with a solution containing nitrate salts of the metal components and also a precipitation agent such as urea. It should be noted that other promoters/spacers such as zirconium may be added, preferably as the nitrate, to further increase the stability and/or improve the selectivity of the catalyst. The zirconium will enter the layer structure or if there is an excess of aluminium will stabilise the alumina structure. After draining of excess solution from the outside of the support the alpha - alumina matrix may be heated to a temperature suitable for the controlled hydrolysis of the urea thus increasing the pH of the absorbed solution and bringing about the deposition of the insoluble hydroxides within the pores. The catalyst is then dried by heating to a suitably elevated temperature. The metal loading of the catalyst may be increased by repetition of the process steps. Prior to re-impregnation of the catalyst the pores must be opened to remove blocking substances such as urea by-products, nitrogen oxides etc. within the mouth of pores. This may be done by heating i.e. thermal decomposition or the precursor is washed with water or weaker alkaline solution and then dried at a suitably elevated temperature. The catalyst of the required metal loading is subjected to a final calcination temperature of about 450°C. The catalyst composition of the invention will have enhanced thermal stability and hydrothermal stability. The precursor may contain by-products formed as a result of the method of preparation and these can be tolerated so long as they do not affect the activity of the catalyst or the stability thereof. In another aspect the invention provides a method of converting carbon monoxide in the presence of steam to carbon dioxide and hydrogen which method comprises passing the mixture over a catalyst of the invention at an appropriate temperature. The temperature will be of the order of 190 to 260°C in the case of a low temperature shift. Because of the high thermal stability and hydrothermal stability the catalyst can be used at higher temperatures and therefore as a substitute for the more usual high temperature shift catalysts. Copper based catalysts can be used in the low pressure synthesis of methanol, and the invention includes in another aspect a method of converting carbon monoxide and hydrogen into methanol which comprises passing the mixture over a catalyst of the invention at a temperature of the order of about 240°C at a pressure of 5MPa to 10MPa. In order that the invention may be well understood it will now be described by way of example with reference to the Following example. Example An aqueous solution was made of 100 g of cupric nitrate trihydrate, 150 g of zinc nitrate hexahydrate and 110 g of aluminium nitrate nonahydrate. A molar solution was made of sodium carbonate. The nitrate solution was fed at the rate of 16 ml/min into a 5 litre beaker containing 0.5 litres of deionised water at 80°C, and the sodium carbonate solution was added at a rate to maintain the pH constant at a value of 9. The solution was kept at 80°C For one hour after complete precipitation. The precipitate was filtered using a 24 cm diameter Buchner funnel and two paper filters. The precipitate was washed twice by resuspending the precipitate in 2.5 litres of deionised water at 80°C and then filtering. The filtered precipitate was dried in an oven at 267°C overnight. The precipitate was partly calcined as a result and then washed substantially free of sodium ions. The material was dried and calcined at about 357°C. The method was repeated using a nitrate solution containing additionally 5 g of lanthanum nitrate hexahydrate. The total surface area was measured using the B.E.T. method and the following results were obtained total surface area m²/gm of catalyst These results show that the lanthanum containing catalyst was very much more stable than the lanthanum-free product. Analysis showed that the Cu/Zn/Al/La catalyst had a layer structure. When used in CO shift processes, both in the water gas shift reaction and the preparation of methanol, the catalyst displayed great stability.

Claims: 1. A catalyst comprising the calcined form of a precursor, the precursor comprising copper, zinc, aluminium and lanthanum or cerium, the atomic ratio of (Cu + Zn): Al being in the range of 1.5 to 6: 1 and the ratio of (Cu + Zn): La or Ce is 600 to 4: 1, characterised in that the precursor is of the formula where R is lanthanum, cerium or zirconium x is not less than 1 and not greater than 4 ; y is not less than 0.01 and not greater than 1.5 n is approximately 4 the atomic ratio of (Cu + Zn): Al is 1.5 to 4: 1 and the element R is present in a ratio of (Cu + Zn): R of 600 to 40: 1, and the precursor has a hydrotalcite layer structure comprising positively charged brucite like layers alternating with negatively charged interlayers. 2. A catalyst according to Claim 1, characterised in that R is lanthanum, and x and y are in the range of 1.5 to 3 and 0.01 to 0.1 respectively. 3. catalyst according to any preceding Claim, characterised in that the atomic ratio of (Cu + Zn): Al is about 3: 1. 4. A catalyst according to any preceding Claim characterised in that the element R is present in a ratio of Cu + Zn: R of 600 to 40: 1, about 150: 1. 5. A catalyst according to any preceding Claim characterised in that anions other than the carbonate such as nitrate or phosphate, are additionally present. 6. A method of making a catalyst according to any of Claims 1 to 5 by co-precipitation of salts of the Cu, Zn, Al and the R element from solutions thereof at substantially constant pH and temperature by the addition of alkali characterised in that the pH of the solution is maintained at substantially 9. 7. A method of converting carbon monoxide in the presence of steam to carbon dioxide and hydrogen characterised by passing the starting mixture over a catalyst according to any of Claims 1 to 5 at a temperature of the oder of 190 to 260° or about 330°C. 8. A method of converting carbon monoxide and hydrogen into methanol characterised by passing the starting mixture over a catalyst according to any of Claims 1 to 5 at a temperature of the order of 240°C at a pressure of 5MPa to 10Mpa.

Inventors: SAMBROOK, RODNEY MARTIN
Applicants: DYSON REFRACTORIES LIMITED
Application year: 1987
Main classification: B01J23
IPC codes: C07C29, C07C31, B01J23, C01B3, C07C27, B01J27, C07C67