AN ELECTROLYTE FOR ELECTROLYTIC CAPACITOR

Abstract: An electrolyte for electrolytic capacitor containing within an aprotic solvent an alkyl quarternary ammonium salt of enol-form of l,3-cyclodiketone compound as solute. An electrolyte for electrolytic capacitor according to the invention may conveniently be prepared by adding one equiva­ lent amount of enol-form of l,3-cyclodiketone compound to a methylene chloride solution of alkyl ammonium hydrogen­ sulfate for reaction with subsequent addition of two equiva­ lent amounts of alkali hydroxide. A deposit is removed from the reaction product with subsequent vacuum drying to obtain an anhydrous salt and then dissolving said anhydrous salt to an aprotic solvent until a desired conductivity is obtained, for example, as an approximately l0% by weight solution.

Description: This invention relates to an electrolyte for electrolytic capacitor containing within an aprotic solvent an alkyl quarternary ammonium salt of enol-form of l,3-cyclodiketone compound as solute. An electrolytic capacitor is composed by using an anode electrode of the so-called valve metal such as aluminium or tantalum, said metal being caused to form an insulating oxide layer on its surface, said insulating oxide layer acting as a dielectric layer, contacting said insulating oxide layer with an electrolyte layer and arranging a current collector electrode generally referred to as cathode. The electrolyte for the electrolytic capacitor, as above mentioned, contacts directly with the dielectric layer and acts as a true cathode, that is, the electrolyte lies between the dielectric layer of the electrolytic capacitor and the current collector electrode and hence its resistance is inserted in series for the electrolytic capacitor. Therefore, the characteristic of the electrolyte results in an important factor controlling the characteristic of the electrolytic capacitor. For example, if a conductivity of an electrolyte is lower, an equivalent series resistance within an electrolytic capacitor is increased and hence a high-frequency characteristic and a loss characteristic may be lowered. That is the reason of the demand for high conductivity electrolyte and as such a high conductivity electrolyte, a solution of an organic acid or its salt, such as adipic acid in glycols, such as ethylene glycol or alcohols has been used. The latest expansion of demands of electrolytic capacitors having higher electric characteristics has not been satisfied with the conductivity of the present electrolyte. Especially in the case of the present electrolyte, when a desired conductivity is not obtained or a low solubility solute is used, the conductivity has been improved by adding intentionally water. However, in the latest utilizing condition of the electrolytic capacitor required to use at above 100°C and for many hours, the presence of water causes a dielectric layer to be worsened, an internal vapor pressure of the electrolytic capacitor to be increased and hence the life of the electrolytic capacitor is worsened because of a breakage of a seal part or a volatilization of an electrolyte. Therefore, the present electrolytic capacitor has had a drawback unable to hold a stable characteristic over a long term. To solve the matter, it is known that an ammonium or a primary, secondary or tertiary amine salt of an organic acid is used as a solute in an aprotic solvent as disclosed in the Japanese patent publication Nos. 55-3989, 57-56763, 58-32769 and the U.S Patent No. 4,117,531. It has been discovered that an alkyl quaternary ammonium salt of enol-form of l,3-cyclodiketone has a considerable solubility to an aprotic solvent and the solution has an extremely high conductivity, even though an ammonium or a primary, secondary or tertiary amine salt of l,3-cyclodiketone is practically insoluble in an aprotic solvent and hence such a solution has substantially no conductivity. Thus, a principal object of the invention is to provide an electrolyte of substantially non water series high conductivity with use of the aprotic solvent. An electrolyte for electrolytic capacitor according to the invention is characterized by containing an alkyl quaternary ammonium salt of enol-form of l,3-cyclodiketone compound in the aprotic solvent as solute. The enol-form of l,3-cyclodiketone compound according to the invention is the tautomer of the l,3-cyclodiketone compound and can form the alkyl quaternary ammonium salt and these relations are represented by the following general formula, in which R is alkyl group having l to 6 carbon atoms, B is alkylene group having 2 to 5 carbon atoms and two hydrogen atoms of any one methylene of B may be substituted with one or two alkyl groups having l to 6 carbon atoms and A is alkyl ammonium comprising alkyl groups having l to 6 carbon atoms. The l,3-cyclodiketone compound to be preferably used in the invention may be selected from the following but not limited thereto: l,3-cyclopentadione, 2-methyl-l,3-cyclopentadione, l,3-cyclohexadione, 2-methyl-l,3-cyclohexadione, 5,5-dimethyl-l,3-cyclohexadione. The alkyl quaternary ammonium to be preferably used in the invention may be selected from the following but not limited thereto: tetramethylammonium, tetraethylammonium, tetrabutylammonium. The aprotic solvent to be used in the invention may be selected from the following but not limited thereto: (l) Amide system solvent: N-methylformamide, N,N-dimethylformamide, N-ethylformamide, N,N-diethylformamide, N-methylacetoamide, N,N-dimethylacetoamide, N-ethylacetoamide, N,N-diethylacetoamide, hexamethylphosphorinamide (2) Oxide compounds: di-methylsulfoxide (3) Nitrile compounds : acetonitrile (4) Cyclic esters, cyclic amides : γ-butyrolactone, N-methyl-2-pyrrolidone, ethylene carbonate, propylene carbonate. An electrolyte for electrolytic capacitor according to the invention may conveniently be prepared by adding one equivalent amount of enol-form of l,3-cyclodiketone compound to a methylene chloride solution of alkyl ammonium hydrogensulfate for reaction with subsequent addition of two equivalent amounts of alkali hydroxide. A deposit is removed from the reaction product with subsequent vacuum drying to obtain an anhydrous salt and then dissolving said anhydrous salt to an aprotic solvent until a desired conductivity is obtained, for example, as an approximately l0% to 20% by weight solution. (Examples l to 5) An electrolyte for electrolytic capacitor according to the invention will be exemplified in the following with l0% to 20% by weight solution for alkyl ammonium salt of various enol-forms of l,3-cyclodiketone compounds with respect to the conductivity as shown in Table l. Further, as comparative example the conventional standard electrolytes composed of 78% by weight of ethylene glycol, l0% by weight of water and l2% by weight of ammonium adipate are shown also in Table l. As understandable from the result above, the electrolyte of the present invention has higher conductivty than that of the conventional electrolyte. Further, a series of electrolytic capacitors for comparative test are prepared with the electrolytes of examples and each of the capacitor characteristics is compared. The electrolytic capacitor for the test is prepared by rolling three layers superposed a cathode and an anode of aluminium foil and a separator paper between them to form a cylindrical capacitor element. The capacitor element is impregnated with each of electrolytes of the examples and then is introduced into an external case and sealed respectively. Each electrolytic capacitor consists of the same dimentional capacitor element having 16V rated voltage and 180 µF rated capacity. The actual high-temperature load test obtained at 16WV 180 micro F for electrolytes exemplified in examples l to 5 and the comparative example are shown at the mean value of l0 load tests in Table 2. As understandable from the result above, the electrolytic capacitor using the electrolyte of the present invention has lower capacitor losses or tanδ as compared with that of the conventional electrolyte because of the higher conductivity of the electrolyte of the present invention. Furthermore, as the result of the essentially non-aqueous system, the electrolytic capacitor using the electrolyte of the present invention shows no abnormal exterior or decrease of the electrostatic capacity due to the increase of the internal pressure and the extremely few change of the characteristic values in comparison of the initial value with the value after the load test. The electrolyte according to the invention may provide the electrolytic capacitor for the power device such as the switching regulator used at high frequency and requiring high efficiency and for various electrical machineries and apparatuses used at high temperature for a long term because of the maintenances of the lower capacitor losses and the stable characteristic used at high temperature for a long term.

Claims: An electrolyte for electrolytic capacitor comprising an aprotic solvent and an alkyl quaternary ammonium salt of an enol-form of l,3-cyclodiketone compound of general formula, in which R is alkyl group having l to 6 carbon atoms, B is alkylene group having 2 to 5 carbon atoms and two hydrogen atoms of any one methylene of B may be substituted with one or two alkyl groups having l to 6 carbon atoms and A is alkyl ammonium comprising alkyl groups having l to 6 carbon atoms. An electrolyte for electrolytic capacitor according to claim l, wherein aprotic solvent is selected from the group of N-methylformamide, N,N-dimethylformamide, N-ethylformamide, N,N-diethylformamide, N-methylacetamide, N,N-dimethylacetamide, N-ethylacetamide, N,N-diethylacetamide, γ-butyrolactone, N-methyl-2-pyrrolidone, ethylene carbonate, propylene carbonate, dimethyl sulfoxide, acetonitrile or the mixture thereof. An electrolyte for electrolytic capacitor according to claim l, wherein l,3-cyclodiketone compound is selected from the group of l,3-cyclopentadione, 2-methyl-l,3-cyclopentadione, l,3-cyclohexadione, 2-methyl-l,3-cyclohexadione, 5,5-dimethyl-l,3-cyclohexadione. An electrolyte for electrolytic capacitor according to claim l, wherein alkyl ammonium is selected from the group of tetramethylammonium, tetraethylammonium, tetrabutylammonium.

Inventors: SHINOZAKI, FUMIHIKO C/O NIPPON CHEMI-CON CORP., TSUJI, TATSUNORI C/O NIPPON CHEMI-CON CORP., YOKOYAMA, YUTAKA C/O NIPPON CHEMI-CON CORP.
Applicants: NIPPON CHEMI-CON CORPORATION
Application year: 1987
Main classification: H01G9
IPC codes: H01G9