PHOTOENGRAVING ARTICLES AND METHODS OF PRODUCING SUCH ARTICLES

Abstract: An alloy, a photoengraving article, a photoengraved article, and a method of forming a photoengraved article. The photoengraving article is formed of a magnesium-based alloy which contains from 2 to 4 percent by weight aluminum, an amount of calcium effective to improve the sharpness of an etched pattern on the article, and less than 100 ppm zinc. The method of forming the photoengraved article comprises the steps of etching the photoengraving article with a composition of nitric acid and a stearic acid additive. The article and method do not release zinc into the etching bath. Ultimate release of zinc into the environment is also reduced.

Description: PHOTOENGRAVING ARTICLES AND METHODS OF PRODUCING SUCH ARTICLES The invention relates to photoengraving articles which are adapted to be etched by a powder »less etching process to form photoengraved articles. The invention also relates to photoengraved printing articles and to a method for forming such photoengraved articles. Photoengraving involves the manufacture of photoengraved printing articles. The manufacture of such articles involves coating a metal substrate, e.g., a plate, sheet or cylinder with a light-sensitive material. The light-sensitive material is then transformed in selected areas by the action of light, with or without the assistance of heat, into an etch resistant pattern. This pattern is known in the art as a photo resist pattern. This photo resist pattern comprises portions which can be selectively removed from the metal substrate by dissolving those portions to thereby expose the underlying metal substrate. Accordingly, the metal substrate has a photo resist pattern thereon and portions of the coating which have been removed by etching to expose the underlying bare metal. The bare metal pattern is then etched, i.e., metal is removed therefrom, to a depth sufficient to permit a printing process to take place or for the preparation of mats. Typical etching depths range from about 0.1 mm, e.g., for half tones, to about 1 mm for letter press work and up to about 3-8 mm for flexographic masters. Typically, a plate having both the image (resist protected) and non-image (bare metal) areas is placed in a commercial etcher for etching. Various types of etchers are used and these are generally of such character that droplets of an etching liquid are directed against the surface of the plate to be etched by a rotating paddle which extends-part way into an etching bath. The etching solution removes a portion of the bare metal to produce an etched pattern on the metal substrate. A disadvantage of prior art photoengraving articles formed of conventional photoengraving alloys relates to the presence of zinc in such alloys. When such alloys are etched in a bath which contains an etchant solution, a large amount of zinc is released into the etching effluent. However, the presence of zinc in the effluent is a great cause of concern since zinc is highly toxic to the environment and thus constitutes a serious pollutant. Prior art photoengraving alloys contain zinc as a means for regulating the etching process, e.g., as a means for regulating the etching speed and also as a means for providing a clean, clear etched pattern in the printing plate, or the like. Particularly with the use of early etchant compositions, if the photoengraving article was formed of an alloy which did not contain zinc, the resulting pattern on the etched article was defective and therefor of a quality which was commercially not acceptable. Typically, the etched pattern would include pimples, undercut portions () resulting from lateral etching, and rough edges. As 0 used herein, lateral etching refers to undesirable etching of metal protected by the photo resist pattern and extending underneath the photo resist pattern. Significant advancement has occurred in the 5 field of etchant compositions. Thus, etchant compositions which include an isostearic acid additive have become available and are exemplified in U.S. .Patent No's. 3,935,118; 4,032,379; 3,992,234; 0 3,922,229; 3,736, 197,3,730,899; ' 3,728, 180; 3,728,180; 3,725,158 and 3,725,159. As used herein, "etching bath" refers to the etching composition which is applied to a c photoengraving article provided with a photo resist coating to conduct the etching process. Because zinc- free, magnesium-based alloys for printing articles functioned unacceptably with present etching compositions, it was expected that they would also 0 function unacceptably with recently developed etching compositions. As used herein, the term "photoengraving article" is intended to embrace, inter alia, printing plates, pattern plates or mold masters, embossing dies, debossing dies, foil stamping dies, hot stamping dies, thermal cutting dies, and the like. As used herein, the term "pimples" refers to unetched portions of metal having a conical shape found in the non-imaged area of an engraved article. The term "seediness" refers to the presence of small pimples found at the base of the image shoulder, 0 and are usually found in reverses. Seediness is particularly damaging to printing plates. The term "rough shoulders" refers to image shoulders which slope away from the image in a very C - irregular manner, rather than a smooth, continuous taper. U.S. Patent No. 1,028,216 discloses the melting and casting of magnesium in the presence of a small Q amount of calcium. The calcium is added to the magnesium or an alloy thereof. Zinc is not a component of the alloys of the examples The alloys are not disclosed as being useful as printing articles in photoengraved printing processes. 5 U.S. Patent No. 1,698,647 discloses a process for the manufacture of a similar magnesium alloy containing from 0.05 to 0.3 percent by weight calcium which is used in the process to lower the melting point 0 of the magnesium. Published British patent application No. 661,759 discloses a magnesium-based alloy containing from 1 to 12 percent by weight aluminum, from 0.05 to 1 5 percent by weight manganese and from 0.005 to 0.7 percent by weight zirconium. Up to 5 percent by weight zinc may also be present. The alloy is formulated with or without the zinc. The alloys are not disclosed as being useful as printing articles in photoengraved printing processes. U.S. Patent Nos. 2,185,452 and 2,185,453 disclose magnesium alloys containing from 1 to 12 percent by weight aluminum, from 0.3 to 5 percent by weight zinc, from 0.05 to 0.3 percent by weight manganese, and from 0.03 to 0.3 percent by weight calcium, the balance being magnesium. The alloys are not disclosed as being useful for photoengraved printing articles in printing processes. U.S. Patent No. 3,475,140 discloses a composite printing plate formed of a magnesium alloy layer bonded to an aluminum layer. The magnesium alloy in the layer are standard alloys known 'as PE (photoengraving) • • alloys, which do not con-tain calcium. Canadian Patent No. 594,432; and British Patent No. 661,759 disclose magnesium-based photoengraving alloy compositions containing both calcium and zinc. The present invention particularly resides in a photoengraving article formed of a magnesium alloy containing from 2 to 4 percent by weight aluminum, an amount of calcium effective to improve the resolution of the etched pattern, and less than 100 ppm zinc. More particularly, the alloy is a ternary alloy comprising a major proportion of magnesium; from 2 to 4 percent by weight aluminum; from 0.01 to 0.04 percent by weight calcium, and less than 0.01 percent by weight zinc. The present invention also resides in a ternary alloy comprising a major proportion of magnesium, from 2 to 4 percent by weight of aluminum, from 0.01 to 0.04 percent by weight of calcium, and less than 100 ppm 5 zinc The photoengraving article made from the specified alloy is subjected to powderless etching of a pattern in a surface of the article with an etchant 10 solution to produce a photoengraved article. The presence of calcium in the photoengraving article is effective to improve the resolution of the etched pattern in the photoengraved article. 15 The invention further resides in a powderless etching process for forming a photoengraved article, comprising the steps of forming a photoengraving article from a magnesium-based alloy containing from 2 to 4 percent by weight aluminum, an amount of calcium 20 effective to improve the resolution of an etched pattern in the photoengraved article, and less than about 100 ppm zinc, and etching a pattern on said article with an acid etching solution. The etching 2c solution preferably comprises a nitric acid solution containing an isostearic acid based etching additive. The photoengraving articles of this invention are formed of a magnesium-based, essentially zinc-free • 3Q alloy. The term "essentially zinc-free" means that the alloy does not contain any zinc except for trace amounts that may be present as an impurity in the magnesium alloy. For example, zinc can be present in the alloy in trace amounts, but should not exceed an 35 amount of greater than 100 ppm (parts per million). An amount of less than 50ppm is preferred, with less than 10 ppm being most preferred. The photoengraving articles are produced by coating the surface of the article (alloy plate or sheet) with a light sensitive coating or enamel. The coated surface of the ar ' ticle is then exposed to light through a negative having an image thereon so as to produce an image on the coating. The exposed coating is then developed to form an acid- resistant coating on the article corresponding to the image produced by exposure to the light. This coating 0 may be further hardened by heating. The final acid- resistant image is known in the art as a "resist coating". Subsequently, the image-bearing, coated surface of the photoengraving article is subjected to C - acid etching in an etching bath, to remove the metal which is not protected by the photo resist coating and to .thus produce the image in relief. Since the alloy of the invention is essentially zinc-free, very low ' - amounts of zinc are transferred to the etching bath and consequently, very low amounts of zinc are released into the environment upon disposal of the etching bath. Presently used alloys contain zinc as a means for regulating and controlling the rate of etching by the etching solution. The presence of zinc is presently required (usually on the order of about 1.2 percent by weight of the alloy) in order to provide an etched pattern in the photoengraved article which is clean, of high resolution, and which does not contain aberrations in the surfaces of the etched pattern, e.g., pimples, rough shoulders or seediness (fine pimples in revere images). Although the rate of etching can be controlled by adjusting the concentration of acid in the etching bath, the degree of control afforded thereby is not sufficient to compensate for the absence of zinc In the etching bath. It has now been discovered that the presence of calcium in the magnesium alloy compensates for the lack of zinc. Thus, when the photoengraving article of this invention is formed of a magnesium alloy which contains calcium, it is possible to control the rate and other parameters of the etching process by adjusting, e.g., the acid concentration of the etching bath, while at the same time allowing the use of an essentially zinc- free alloy. An example of an optimum etching recipe for a Master DM-35 is: 18 percent by volume of a 42 Be° nitric acid, a paddle speed of 500 RPM, a bath temperature of 35C, and an etchant additive of 69 percent Hunt X-FLEX™. The use of- calcium in the alloy results in a photoengraving article which is ' of superior quality having a substantially reduced formation of pimples and seediness and having a clean, clear etched pattern. The calcium in this alloy should be uniformly dispersed throughout the alloy and, preferably, should be added at a late stage in the formation of the alloy. The calcium should not be present in the alloy in segregate form, e.g., as stated above, it should be present in uniform concentrations throughout the alloy. As used herein, the term "segregate" refers to agglomerations of calcium, or regions of Increased calcium concentration in the alloy which causes a slower rate of etch. These agglomorations shoulα not be present in sizes of from 15 to 40 microns. Photoengraving articles of the present invention are formed of alloys containing from 0.01 to 0.4 percent by weight and preferably from 0.02 to 0.03 percent by weight calcium. It is believed that the presence of calcium in the alloy controls the etching process by controlling the film-forming properties of the etching bath as the photoengraving article is coated with the etching bath. Preferably, the alloy also contains from 2 to 4 percent by weight aluminum to impart desirable mechanical characteristics to the alloy and articles formed therefrom. More preferably, the alloy contains from 3 to 4 percent by weight aluminum. Other metals may be present in the alloy in trace amounts (as impurities) such as, for example, copper, nickel, iron, manganese, a.nd silicon. Preferably, the alloys employed in forming the photoengraving article of this invention contain a total of less than about 100 ppm, and more preferably less than 50 ppm of such other metal impurities. For example, the alloy of the invention may contain less than 5 ppm copper; less than 2 ppm nickel; less than 50 ppm iron; and less than 20 ppm manganese. PE (photoengraving) magnesium alloys are standard alloys which are well known in the art. These alloys may be modified to form the essentially zinc- free alloy of the invention which additionally contains calcium. The photoengraved article of this invention is formed by etching with a multi-component, isostearic acid/nitric acid etching solution or additive. Typically, the etching additive is formulated and added to the etching bath. Generally, it will be required to modify the j . concentration of the components of the etching bath to provide optimal results. The particular formulation used will, generally, depend on the particular characteristics of the pattern which is desired to be etjchs.d into the surface of the photoengraving article, 10 and on the composition of the alloy employed. The particular etching bath formulation to be employed is determinable by routine optimization experiments. In the following examples, all temperatures are 15 set forth in degrees centigrade and all parts and percentages are by weight unless otherwise indicated. » Example 1 20 Photoengraving articles were prepared by extrusion of alloys set forth in Table 1A, wherein alloy 1 contains zinc and calcium; alloy 2, an alloy of this invention, is essentially zinc-free and contains calcium; alloy 3 is essentially zinc and calcium free, 25 and alloy 4 is a standard PE magnesium alloy. The articles produced from the alloys were coated with a photo resist coating and then etched to determine the impact of removing the zinc from the alloy, while leaving calcium in the alloy. These samples were 30 etched in an etching bath containing 20 percent by volume 42° B e nitric acid, a 5 percent by volume Hunt X-FLEX™(isostearic acid based etching additive) and the remainder tap water. In the first run (of 4 alloy oj- compositions), the temperature of the bath was maintained at 38°C and in the second run at 35°C. In both runs, the paddle speed was maintained at 480 rpm. The samples were etched simultaneously with a commercial control of Dowetch™ PRC Redtop. The results obtained are set forth in Table 1B. The results show that the magnesium-based, zinc-free alloys used in photoengraving articles provide a "dirty" etch when calcium is not present in the alloy. The term dirty etch when calcium is not present in the alloy designates that the etched pattern is characterized by 10. an appearance of seediness and by the presence of pimples. The alloys which contain zinc provided a clean etched pattern without the formation of a seedy appearance or pimples and without lateral etching which , £ - is evidenced by an undercut. The essentially zinc-free alloy, containing calcium provided a clean etched pattern in one instance without the formation of pimples or a seedy appearance. In another instance the e"tch was clean but was characterized by broad ragged 0 shoulders. The data show that a photoengraving article formed of a magnesium-based alloy which contains calcium can be etched to produce a clean etched pattern in spite of the fact that the alloy is essentially free of zinc. As can be seen, standard alloys containing 5 zinc etch clean, but essentially zinc-free, magnesium based alloys which do not also contain calcium do not perform acceptably. 0 5 TABLE 1A Alloy Zn Ca Al Cu Ni F-e Mn Si R 1 1.4556 0.03% 3.805. 1 ppm 1 ppm 17 ppm 10 ppm — Balance 2* 61 ppm 0.024 . 3.64?. 1.6 ppm 1 ppm . 20 ppm 14 ppm — Balance 3 53 ppm 1 ppm 3.665. 1 ppm 1 ppm 26 ppm 9 ppm — Balance 4 .7-1.656 0.0156 4.056 0.00556 0.0055$ O.O85. O.0556 Balance min max max max max max *Alloy of this invention TABLE IB Depth of Relief in Depth of Open (Line) Relief in Etch Area Tone Areas Comments on Alloy Time ( in mm) (in mm) Etchinq 4 8 in 0.84 0.13 Clean 1 8 min 0.89 0.13 Clean Orientation 2* 8 min 0.96 0.13 Clean 3 8 min 1.09 0.10 Dirty 4 20 min 2.01 0.16 Clean 1 20 mi-n 2.03 0-.15 Slight undercut 20 min 2. 34 0.15 Clean, Broad Ragged shoulders 20 min 2. 34 0.15 Dirty , Broad Ragged Shoulders *Alloys of the invention Example 2 Additional photoengraving articles were prepared from the alloys of Table 1A. They were etched using a Master DM 35 (etching machine) of 130 liter capacity. The etchant employed was Freundorfer Mago 20X (etching additive) which was used to prepare an etching bath comprising 5 percent by volume etchant additive and 20 percent by volume nitric acid (42° Be). The bath also contained 15 g magnesium. The articles were etched at a paddle speed of 400 rpm and a bath temperature of 38°C for 6 minutes. The results are set fort in Table 2. TABLE 2 Depth of Re ' lief in Depth of Open (Line) Relief in Area Tone Areas Alloy (in mm) ( in mm) Comments 0.72-0.83 0.15-0.16 Good clean etch, no undercutting 0.72-0.83 0.15-0.18 Low pimpling, rough shoulders, no undercutting 2* 0.77-0.91 0.1-0.15 Good clean etch. Wide shoulders 0.95-0.99 0.15-0.20 Wide shoulders, slight roughness, some small pimpling. *Alloy of the invention Example 3 Additional photoengraving articles were prepared from the alloys of Table 1A. An etching bath similar to that of Example 2 was employed except that the bath contained 280 gm of magnesium. The etching was conducted at 35°C at a paddle speed of 400 rpm for 5 minutes. The results are set forth in Table 3. TABLE 3 Depth of Relief in Open Depth of (Line) Relief in Area Tone Areas Alloy (in mm) (in mm) Comments 4 0.68-0.72 • 0.13-0.16 Good Shoulders, Clean etch 1 0.75-0.89 0.21-0.28 Much smaller, low pimpling, undercut 2* 0.66-0.75 0.13-0.16 No undercutting, but rough shoulders 3 0.68-0.82 0.18-0.21 No undercutting. but very rough shoulders *Alloy of the invention Example 4 Photoengraving articles were prepared from the alloys of Table A1. An etching bath similar to that of Example 2 was prepared except that the bath contained 340 gm of magnesium. The etching was conducted at 40°C and at a paddle speed of 550 rpm for 6 minutes. The results are set forth in Table 4. TABLE 4 Depth of Relief in Open Depth of (Line) Relief in Area Tone Areas Alloy (in mm) ( in mm) • Comments 4 0.99-1.10 0.14-0.24 Clean Shoulders, fairly wide 1.10-1.17 0.20-0.28 Much smaller low pimpling, undercut on reverses 2* 1.07-1.22 0.15-0.21 Clean undercutting,, but rough shoulders 1.21-1.32 0.18-0.29 Some small deep pimples, very rough shoulders, no undercutting *Alloy of the invention Example 5 Photoengraved articles were prepared from the alloys of Table A1. An etching bath was prepared using Hunt X-5K express 5 percent by volume etchant additive and 42° Be nitric acid to make the total nitric acid concentration 15 percent by weight. Etching was conducted at 39°C at a paddle speed of 450 rpm for a prer αd of 8 minutes. The results are set forth in bLe 5. TABLE 5 Depth of Relief in Open Depth of (Line) Relief in Area Tone Areas Alloy (in mm) (in mm) Comments 4 0.89-1.02,' 0.13-0.19 Shoulders somewhat rough, but no undercutting 1 0.89-0.99 0.15-0.20 Many pimples, rough shoulders, but no undercutting 2* 0.89-1.08 0.24-0.36 Many low pimples, rough shoulders, no undercutting. 3 1.08-1.17 0.24-0.36 Many low pimples, Rough shoulders, Undercut *Alloy of the invention Example 6 Photoengraving articles were prepared from the alloys of Table A1. An etching bath similar to that of Example 5 was employed except that 5200 ml of acid was added to raise the concentration of acid to 18 percent by volume in an attempt to avoid the pimpling and rough shoulders evidenced in Example 5. The bath contained 84 gm magnesium and the etching was conducted at 40°C and at a paddle speed of 350 rpm for 7 minutes. The results are summarized in Table 6. TABLE 6 Depth of r Relief in Open Depth of (Line) Relief in Area Tone Areas Alloy (in mm) ( in mm) . Comme-nts 4 0.80-0.85 0.10-0.13 Shoulders much improved, but a little too wide 1 0.82-0.93 0.11-0.16 Still some pimples, but much cleaner. Shoulders look better but still a little rough and too wide 2* 0.90-0.95 0.10-0.14 Similar appearance to alloy 1 0.99-1.03 0.13-0.18 Rough shoulders, some low pimpling. *Alloy of the invention Example 7 Photoengraving articles were prepared from the alloys of Table A1. An etching bath similar to that of Example 5 was employed except that the bath contained 140 gm of magnesium. Etching was conducted at 38°C, at a paddle speed of 350 rpm for 7.5 minutes. The results are summarized in Table 7. TABLE 7 Depth of Relief in Open Depth of (Line) Relief in Area Tone Areas Alloy (in mm) (in mm) Comments 4 0.80-0.89 0.11-0.15 Good shoulders but ' a little wide 1 0.89-1.00 0.13-0.18 ' Some low pimples, shoulders still a little rough 2* 0.84-0.89 A few low pimples 1 less than alloy 1 above. Some shoulders a little rough and wide 0.99-1.13 0.13-0.24 Some low pimples, rough shoulders *Alloy of the invention Example 8 Photoengraving articles were prepared from the alloys of Table A1. An etching bath was prepared from Freundorfer Mago 14 etchant additive and 42° Be nitric acid: 5 percent by volume etchant additive and 14 percent by volume acid were employed. The bath contained 28 gm of magnesium. The articles were etched at 40°C, and at a paddle speed of 400 rpm for 10 minutes. The results are summarized in Table 8. TABLE 8 Depth of Relief in Open Depth of (Line) Relief in Area Tone Areas Alloy (in mm) (in mm) Comments 1.02-1.09 0.13-0.16 Good shoulders but a little wide. Some random pimples mostly type I 1.02-1.07 0.15-0.22 Much pimpling, almost blank-off but center almost clear. 5 cm wide areas on each side in the machine direction are almost solid wall-to-wall pimples. 2* 1.03-1.14 0.09-0.13 Very wide rough shoulder some random pimples 1.12-1.24 Low pimpling almost wall-to-wall. Very rough shoulders and wide. *Alloy of the invention Example 9 Photoengraving articles were prepared from the alloys of Table A1. An etching bath similar to Example 8 was employed except that the bath contained 1204 gm of magnesium, 16 percent by volume acid and 5 percent by volume etchant additive. Etching was conducted at 40°C, and at a paddle speed of 500 rpm for 10 minutes. The. results; are summarized in Table 9. : TABLE 9 Depth of Relief in Open Depth of (Line) Relief in Area Tone Areas Alloy (in mm) (i mm) Comments 4 ' 1.02-1.13 0.14-0.18 Clean good shoulders 1 1.04-1.19 0.23-0.38 'Severely undercut and many small pimples. 2* 1.18-1.33 0.13-0.16 Shoulder rough but no undercut. Some pimpling 3 1.27-1.37 0.11-0.15 Shoulder very rough with undercutting down deep. A few scattered low pimples. *Alloy of the invention Example 10 Photoengraving articles were prepared from the alloys of Table A1. The articles were etched in an etching bath similar to that of Example 8 except that the bath contained 125 gm of magnesium. The articles were etched at 38°C, and at a paddle speed of 400 rpm for 9 minutes. The results are summarized in Table 10. 101- TABLE 10 Depth of Relief in Open Depth of (Line) Relief in 15 Area Tone Areas Alloy (in mm) (in mm) Comments 4 0.76-0.81 0.14-0.16 • Clean, most shoulders good Reverse is very steep, but no undercutting. 0 0.77-0.84 0.19-0.24 Many small pimples, undercutting. 2* 0.80-0.85 0.13-0.16 Wide shoulders, many pimples in some areas. 0.89-0.99 0.10-0.15 Wide rough shoulders, a 5 few scattered pimples. *Alloy of the invention 30 35 Example 11 Photoengraving articles were prepared from the alloys of Table A1. The articles were etched in an etching bath similar to Example 8 except that the bath contained 2353 gm of magnesium. Etching was conducted at 38°C, at a paddle speed of 400 rpm for 10 minutes. The results are summarized in Table 11. 10. TABLE 11 Depth of Relief in Open Depth of (Line) Relief in 15 Area Tone Areas Alloy (in mm) (in mm) Comments 4 0.63-0.71 0.13-0.14 Good shoulders, clean - etch 2* 0.6£- .71 0.14-0.19 Good shoulders, no under 20 cutting, but many pimples. 0.71-0.79 0.076-0.10 Wide rough shoulders many pimples. *Alloy of the invention 25. 30 5 Example 12 Photoengraving articles were prepared from the alloys of Table A1. The articles were etched in a Tasope D.P. 4.20, 200 liter capacity etching machine. An etching bath comprising Hunt X-FLEX™ 42° Be nitric acid and water was prepared comprising 5 percent by volume etchant additive and 20 percent by volume acid. 310-4 gm of magnesium were present in the bath. Etching was: conducted at a temperature of 40°C and at a paddle speed of 480 rpm for 8 minutes. The results are summarized in Table 12. TABLE 12 Depth of Relief in Open Depth of • (Line) . Relief in Area' Tone Areas * ' Alloy (in mm) (in mm) Comments 4 1.05-1.12 0.11-0.19 Clean etch, steep shoulders, some slight undercutting. 2* 1.09-1.18 0.20-0.28 Rough shoulders, slight undercut. Many small pimples in some areas. 1.07-1.12 0.20-0.25 Steep, rough shoulders but not undercut. Scattered pimples. *Alloy of the invention Collectively, the data in the above examples demonstrate that photoengraved printing articles formed of magnesium-based alloys which contain calcium can be etched to produce a clean etched pattern in spite of the fact that the alloy is essentially free of zinc. As can be seen, standard alloys which also contain zinc also etch clean but essentially zinc-free magnesium- based alloys which do not also contain calcium do not perform acceptably. The preceding examples can be repeated with similar success by substituting the generically or specifically described reactants and/or operating conditions of this invention for those used in the preceding examples. From the foregoing description, one skilled in the art can easily ascertain the essential characteristics of this invention, and without departing from the spirit and scope thereof, can make various changes and modifications of the invention to adapt it to various usages conditions.

Claims: CLAIMS 1. A photoengraving article formed of a magnesium alloy containing from 2 to 4 percent by weight aluminum, an amount of calcium effective to improve the resolution of the etched pattern, and less than 100 ppm zinc. 2. The article of Claim 1, wherein said alloy 5. contains from 0.01 percent to 0.04 percent by weight calcium. 3. The article o.f Claim 1 or 2, wherein said alloy contains from 3 to 4 percent by weight aluminum 10 and less than about 50 ppm zinc. 4. A photoengraved article formed by powderless etching of a pattern in a surface of the photoengraving article of Claim 1. 15 5. The article of Claim 4, wherein the powderless etching of the photoengraving article is conducted with an etching composition of nitric acid and an isostearic acid base etching additive to form a 20 photoengraved article for use as a printing plate, pattern plate, mold master, embossing die, debossing die, foil stamping die, hot stamping die, or thermal casting die. 25 6. A ternary alloy comprising a major proportion of magnesium, from 2 to 4 percent by weight of aluminum, from 0.01 to 0.04 percent by weight of calcium, and less than 100 ppm zinc. 7. The alloy of Claim 6, comprising from 3 to 4 percent by weight aluminum, from 0.02 to 0.03 percent by weight calcium, and less than 50 ppm zinc. 8. The alloy of Claim 6 or 7, containing less than 100 ppm of other metal impurities. 9. A powderless etching process for forming a photoengraved article, comprising the steps of forming a photoengraving article from a magnesium-based alloy containing from 2 to 4 percent by weight aluminum, an amount of calcium effective to improve the resolution of an etched pattern in the photoengraved article, and less than about 100 ppm zinc, and etching a pattern on said article with an acid etching solution. 10. The method of claim 10, wherein the acid etching solution comprises a composition of nitric acid and an isostearic acid based etching additive. 11. The method of Claim 9 or 10, wherein said alloy contains from 0.01 to 0.04 percent by weight calcium. 12. The method of Claim 9 , 10, or 11 , wherein said alloy contains from 0.02 to 0.03 percent by weight calcium, from 3 to 4 percent by weight aluminum, less than about 75 ppm zinc, and less than 100 ppm of any other trace metals.

Inventors: NEWHOUSE GEOFFREY S, NEWHOUSE, GEOFFREY, S.
Applicants: DOW CHEMICAL CO, THE DOW CHEMICAL COMPANY
Application year: 1987
Main classification: C22C23
IPC codes: C22C23, C23F1, G03F7