PROCESS FOR FORMING CMOS STRUCTURES

Abstract: In a process for forming CMOS devices, polysilicon gate structures (16N, 16P) having overlying overhang masks (17N, 18N; 17P, 18P) are provided on a substrate and oxidized to form relatively thick sidewall oxide (21N, 21P). Next, n<+> source/drain regions (27N, 28N) are implanted, whereafter the sidewall oxide (21N) of the NMOS device is partially etched. Then the NMOS overhang mask (17N, 18N) is removed and a low energy implant effected to form LDD regions (31N, 32N). Next, the p<+> source and drain regions (27P, 28P) are implanted, the PMOS sidewall oxide (21P) is partially etched, the PMOS overhang mask (17P, 18P) is removed and an n<+> PMOS guard band diffusion (33P, 34P) is formed around the PMOS LDD regions. Finally, a blanket p-type implant is effected to simultaneously form a guard band diffusion (33N, 34N) around the NMOS LDD region and form the PMOS LDD diffusion (31P, 32P).

Description: PROCESS FOR FORMING CMOS STRUCTURES Technical Field This invention relates to processes for forming complementary PMOS and NMOS integrated circuit structures. Background Art One of the constant aims of the microelectronics industry has been to achieve ever small device and component dimensions and spacings to provide increased packing densities. However, as the technology has progressed through LSI and VLSI toward future technologies, it has become increasingly difficult to provide the ever smaller, more dense integrated circuit structures and the associated spacings and diffusion depths. Various problems associated with decreased feature size contribute to decreased yields which can offset the savings occasioned by increased packing density and circuit performance. Perhaps chief among these problems are the so-called short channel effects, which include hot carrier injection into the gate oxide and/or substrate, source-to-drain punch through, threshold voltage reduction with channel length and drain/source operating voltage, subthreshold leakage, and impact ionization. For example, in hot carrier injection, electrons are injected into the gate oxide by the high electric field created by the narrow channel region and adjacent the drain and, as a consequence, alter the threshold voltage of the device. In addition to the short channel effects, overlap between the gate electrode and the source and drain diffusions results in parasitic capacitance between the diffusion region and the gate, known as Miller capacitance, which decrease the device operational speeds. The above-mentioned hot electron carrier injection, low voltage breakdown and impact ionization problems are alleviated using lightly doped drain- source (LDD) regions. The LDD structure is comprised 5 of a shallow, gate-aligned n " or p~ region formed between the MOSFET channel and the respective n + or p + source and drain diffusions. This structure increases breakdown voltage and reduces impact ionization and hot electron emission by spreading the high electric Q field at the drain pinchoff region into the n~ region. One method of fabricating LDD structures involves the use of sidewall spacers in conjunction with etching techniques such as anisotrophic and reactive ion etching (RIE). Tsang et al., 5. "Fabrication of High Performance LDDFET'S with Oxide Sidewall-Spacer ' echnology", IEEE Transactions on Electron Devices, .Vol. ED-29, No. 4, April, 1982, pp 590-596 j teaches a method for forming an LDD NMOSFET. According to Tsang et al., after forming the 2.0 polysilicon gate structure consisting of the gate oxide, the polysilicon gate and an oxide etch mask, n- type ions are implanted to form the n~ LDD regions. A layer of chemical vapor deposited (CVD) silicon dioxide of a desired thickness is then conformally 5 deposited and, using directional RIE, the planar portion of the CVD oxide is removed to leave the vertical oxide sidewall spacer on the polysilicon gate structure. The sidewall spacer is used as a mask during arsenic ion implantation of the n + source and Q drain regions. Liu, U.S. Patent No. 4,330,931 issued May 25, 1982, discloses a process for forming a self-aligned, silicon gate NMOS FET having n~ source and drain extensions. In this process, after forming a 5 polysilicon gate having a nitride overhang mask, arsenic ions are implanted to form the n + source and drain. During the implant step, lightly doped source and drain extensions are also formed due to the blocking of some ions by the nitride overhangs. The structure is then subjected to a high temperature oxidization step to grow a 100 nanometer thick oxide over the sides of the polysilicon gate and the substrate corresponding to the source and drain regions. The oxide thus formed over the n + source and drain regions is then damaged by argon ion implantation. During this oxide damaging step, the oxide over the n~ source and drain extensions regions at the sidewalls of the gate is protected by the nitride overhang mask. The damaged oxide and the nitride mask are then removed and a tungsten layer is selectively deposited over the exposed n + source and drain regions and the gate. The oxide damaging step of the Liu '931 process is not only an extra process step but also requires very careful control. Furthermore, any variation in undercutting the polysilicon may cause damage to the sidewall oxide during the argon ion bombardment step. The Liu '931 process also appears to be limited to forming a very thin, 100 nanometers thick, polysilicon gate sidewall oxide. Jecmen, U.S. Patent No. 4,198,250 issued April 15, 1980, also used an overhang mask on the polycrystalline silicon gate electrode to effect the implanting of an LDD structure. In this case, the mask is silicon dioxide. The overhang mask is provided by wet chemical overetching of the supporting poly gate, then the n + source and drain regions are implanted. During implantation, the mask overhang absorbs a large percentage, but not all, of the incident implant species. As a consequence, the n + source and drain implant also forms shallow, lightly doped LDD regions beneath the mask overhang between the channel and the n + source and drain regions. As mentioned, overlap between the gate electrode and the source and drain results in parasitic capacitance between the impurity region and the gate, known as Miller capacitance, which decreases 5 high frequency response and operational speeds. Increased depth can also cause increased susceptibility to punch through. The Jecmen '250 patent states that its LDD regions do not diffuse (laterally or vertically) significantly during the Iff subsequent high temperature processing. As a consequence, the LDD regions do not significantly overlap the gate and rstain their shallow junction depth. The initial shallow aligned LDD regions and the subsequent dimensional stability provide reduced 15. Miller capacitance. Chiao, U.S. Patent No. 4,503,601, issued March 12, 1985, which is assigned to the assignee of the present application, is directed t©_ a reproducible manufacturing process for forming NMOS devices which Z incorporate both LDD structures and sidewall oxide spacers. Initially, after forming the gate oxide, and forming a doped polysilicon layer, a silicon oxide layer, and a silicon nitride layer and patterning the poly-oxide-nitride into the configuration of the gate 25: electrode, n~ LDD regions are formed in sel -alignment with the gate by ion implantation. Then, a low temperature selective oxidation process is applied to form a much thicker layer of oxide on the vertical sidewalls of the highly doped polysilicon gate than _ Q > over the lightly doped exposed substrate. The thin • source/drain oxide is then readily removed, leaving thick sidewall oxide spacers which self-align the n + source and drain implants with the LDD regions and also prevent shorting of the gate to the source/drain 5 diffusion during subsequent metallization. An article in IBM Technical Disclosure Bulletin, Vol. 26 No. 12, May 1984, pages 6584-6586: Cordelia: "Sub icron IGFET Device with Double Implanted Lightly Doped Drain/Source Structure", discloses a device wherein p-pockets are disposed under narrow self-aligned n-regions between n+ source and drain regions. The application to CMOS devices is mentioned, although no process for forming such CMOS structures is disclosed. Disclosure of the Invention It is an object of the present invention to provide a process for forming complementary PMOS and NMOS integrated circuit structures, which is suitable for producing small geometry, high density structures, yet which is simple, reproducible and conducive to high yields. Therefore, according to the present invention, there is provided a process for forming a complementary PMOS and NMOS integrated circuit structure, characterized by the steps of: forming a gate structure for each device having an overlying overhang mask defining underlying regions adjacent the gate structure as source and drain regions; doping the NMOS source and drain regions with n-type dopant in the presence of the NMOS overhang mask to form the heavily doped n-type source and drain regions in self- alignment with the NMOS overhang mask; removing the NMOS overhang mask; relatively lightly doping the NMOS active areas adjacent the gate structure with n-type dopant to form LDD regions in self-alignment with the NMOS gate between the gate and highly doped source and drain regions; selectively doping the PMOS source and drain regions with p-type dopant in the presence of the PMOS overhang mask to form the heavily doped p- type source and drain regions in self-alignment with the PMOS overhang mask; removing the PMOS overhang mask; and relatively lightly doping the PMOS active areas adjacent the gate structure with p-type dopant to form LDD structures in self-alignment with the PMOS gate between the gate and the highly doped source and drain regions. It will be appreciated that a process according to the invention is adapted to provide a reproducible process for forming a short channel, graded source and drain doping profile for controlling hot carrier effects. According to a preferred feature, guard band : diffusions are provided for the CMOS LDD structures. The guard band diffusions can be implemented in a minimum number of process steps. According to another preferred feature, sidewall oxide is formed on the sidewalls of the gate structures. This has the advantage of enabling a metal layer, such as tungsten, to be selectively deposited over polysilicon gate electrodes and on source and drain substrate regions with a low risk of shorting between the gate and source/drain metal deposited layers. In brief summary of a preferred embodiment of the invention, there is disclosed hereinafter a process for forming a complementary set of PMOS and NMOS integrated circuit devices incorporating LDD, : guard band and oxide sidewall structures and comprises: (1) forming a gate structure for the PMOS and NMOS devices having an overlying overhang mask defining underlying regions adjacent the gate structure as source and drain regions. In step (2), the structure is placed in an oxidizing ambient at a relatively low temperature to preferentially form a relatively thick sidewall oxide on the highly doped NMOS and PMOS gate structures. Next, (3), the NMOS n + source and drain are implanted in self-alignment with the overhang mask or with the overhang mask and sidewall oxide. In step (4), the thickness of the NMOS sidewall oxide is selectively partially etched. leaving a remnant thickness for the purpose of providing insulation between the gate and source/drain connections. Next, (5), the overhang mask is removed and (6) n-type ions are selectively implanted in the 5 NMOS active area at a relatively low energy and dose to form LDD regions in self-alignment with the NMOS gate between the gate and the n + regions. Step (7) involves selectively implanting p-type species at relatively high energy and dose to a relatively deep 1.0 junction depth in self-alignment with the PMOS overhang mask. Step (8) involves selectively partially etching the thickness of the PMOS sidewall oxide leaving a remnant insulating thickness at the sidewall followed by (9) removal of the PMOS overhang 15 mask. In step (10), a PMOS guard band diffusion is formed about the associated LDD region by selectively implanting (in the PMOS active area) n-type species to a relatively shallow junction depth in self-alignment with the PMOS gate and between that gate and the p + 20 source and drain regions. Finally, (11) the CMOS structure in blanket implanted with p-type species to simultaneously provide the guard band diffusion about the NMOS LDD region and form the PMOS LDD diffusion in the associated diffusion region. 5 Thus, the combined LDD, sidewall oxide and guard band structures are provided in a CMOS fabrication sequence which requires only two more processing masks than the Chiao NMOS process, i.e., the same additional number necessary for conventional 0 CMOS integrated circuits. The two additional masks are, first, for the PMOS active region during the NMOS source/drain processing, and, second, for the NMOS active region during the PMOS source/drain processing. Furthermore, the described process is readily 5 tailored to delete the above individual features in response to the needs of a particular circuit. This permits tailoring the process to the lowest possible level of complexity consistent with the density and operational requirements of the circuit. In short, where one or more of the features is/is not needed it is readily included/deleted from the process " fabrication sequence. As an example, the sidewall oxide can be eliminated by deleting steps (2), (4) and (8). The guard bands are eliminated by deleting step (10) and by using step (11) to provide only the LDD diffusion. : Also, the PMOS (NMOS) sequence can be deleted to provide an NMOS-only (PMOS-only) process. Brief Description of the Drawings One embodiment of the present invention will now be described in detail in conjunction with the 5 appended drawings, in which-: FIGS, lr-11 are-schematic cross-sectional representations of CMOS FETs taken sequentially during the major processing steps and illustrating the sequence-for forming LDD structures, sidewall spacers ' and guard band structures in the complementary- integrated circuit. Best Mode for Carrying Out the Invention Referring to FIG. 1, the starting structure for the present invention typically is an unpatterned ; bulk <100> silicon substrate or, preferably, a p " type epitaxial layer 10, formed on a substrate, which layer has a resistivity of about 8 to 20 ohm centimeters. The epitaxial layer will then be processed to form n~ well regions 13. ' To reach the stage of fabrication depicted in Fig. 1, a trench dielectric isolation structure 14 is formed to a typical thickness of about 1 to 2 micrometers and a typical depth of 1 to 5 micrometers to define and electrically isolate the active areas of : the CMOS p-channel and n-channel devices. The trench structure 14 can be formed by following the technique disclosed in U.S. Patent No. 4,104,086. Next the n-wells 13 are formed in the epitaxial layer. An implantation mask (not shown) is formed to define or expose the n-wells using conventional ultraviolet photolithographic techniques. The n-well 13 is then formed by depositing impurities in the exposed substrate epitaxial layer in the presence of the mask. Preferably, this is done using ion implantation, although furnace diffusion can be used. A typical ion implantation sequence for forming the n~ phosphorus well 13 in the p~ layer 10 involves ion implantation of phosphorus at about 50 keV and a dose of about 2.5E12 cm "2 . Other n-type impurities such as arsenic and antimony can be used. As the result of this processing, electrically isolated p~ regions 10 and n~ wells 13 are defined for the NMOS and PMOS transistors, respectively. Next, a high quality silicon dioxide layer 15 is formed over- the substrate to serve as the gate insulator of the CMOS transistors. Typically, the gate oxide layer 15 is formed about 20 to 50 nanometers thick. One suitable process is thermal oxidation in an oxidizing ambient at between 900 to 1100°C. An excellent quality oxide, although a slower-growing one, is provided by oxidation of the substrate using an HCI/O2 ambient at a temperature of between about 900 to 1000°C. Referring still further to FIG. 1, a highly doped polycrystalline silicon (poly) layer 16 is next formed to a thickness of about 200 to 500 nanometers on the gate oxide layer 15. The doping level of about 10 20 to 10 21 atoms/cc provides the high conductivity necessary for the electrode and other conductors which are formed from the layer 16 and also aids the formation of a thick oxide sidewall on the gate electrode by preferential oxidation in the event such a step is used. Low pressure chemical vapor deposition (LPCVD) is one suitable process for forming the poly gate layer 16 using SiH4 ambient. The poly can be doped in situ by adding the impurity species to, the gas ambient system, or afterwards. One example of a separate doping step uses phosphorus oxychloride (POCI3) doping at a temperature of about 925 to 975°C for a time of one hour to attain the impurity concentration noted above. The next step is to form the oxide 17 and nitride 18, the composite overhang-mask layers. The PAD oxide layer 17 is formed to a thickness of about 10 to 30 nanometers using thermal oxidation in an oxidizing ambient such as steam at 950 to 1150°C to convert the upper surface of the poly layer 16 to silicon dioxide. Another suitable approach is chemical vapor deposition. The silicon o ide„„layer-17- reduces the stress between the polysilicon layer 16 and the subsequently formed silicon nitride layer 18. Oxide layer 17 also facilitates " the- removal of nitride layer 18 at a later stage in the fabrication cycle. The oxide also is used as an oxidation/dopant mask in conjunction with the silicon nitride layer 18. The silicon nitride layer is formed on the oxide to a thickness of about 100 to 300 nanometers by conventional processing such as LPCVD using a silane and ammonia gas ambient (SIH4/NH3) and a typical reaction temperature of about 800°C. As mentioned, the silicon nitride layer 18 provides a barrier to doping and oxidation of the underlying structure during subsequent processing. The primary masking use of the silicon nitride is in the formation of the LDD source and drain regions. Referring to FIGS. 1 and 2, the silicon nitride 18 and silicon dioxide 17 layers are then patterned into an overhang masking structure and the polysilicon layer 16 is formed into gate electrodes which are recessed beneath the oxide-nitride mask. The oxide 17 and nitride 18 can be patterned using conventional photolithographic and etching techniques. These include the above-mentioned ultraviolet photolithographic technique involving the application of a photoresist layer 19 (FIG. 1) about 500 to 1,000 nanometers thick, followed by exposure of the layer to ultraviolet radiation in the presence of a mask, and developing and dissolving of selected areas to leave the gate overhang mask 19N and 19P (the N and P suffixes indicating whether the element relates respectively to the n-channel or p-channel FET) shown in FIG. 2. The nitride layer 18 is then etched into masks 18N and 18P, using the overlying photoresist masks 19N and 19P as an etch mask, by conventional etching techniques such as RIE etching. Similarly, the oxide masking sections 17N and.17P are then formed, for example, by reactive ion etching using- the overlying photoresist-nitride dual layer as an etch mask. The polysilicon layer 16 is then patterned using an isotropic etch to form the NMOS and PMOS gate electrodes 16N and 16P recessed about 100 nanometers from the edge of the composite oxide nitride masks. The photoresist masks 19N and 19P can be removed either before or after the polysilicon gate electrode etch. One suitable polysilicon etching approach which has the desired lateral etch component is plasma etching using SF5 etching gas. The next step shown in FIG. 3 is to form thick oxide sidewall layers 21N and 21P on the vertical sidewalls 22N and 22P of the polysilicon gates 16N and 16P. The sidewall oxide 21N and 21P are used to prevent shorting of the gate and source/drain metallization in the LDD integrated circuit structure. Additionally, the sidewall oxides can be used as a mask during the formation of the LDD source/drain regions. The sidewall oxides are formed by a preferential, blanket steam oxidation of the existing integrated circuit structure. The sidewall oxide growth is preferential in the sense that the growth rate and, therefore, the resulting oxide thicknesses are significantly greater at sidewalls 22N and 22P than that over the substrate source/drain regions or other lightly doped or undoped regions of polycrystalline or monocrystalline silicon. The growth and thickness ratios of the sidewall oxides relative to the oxide growth of the source/drain substrate regions is a function of factors such as the crystallographic orientation of the silicon substrate (the growth rate for <111> silicon is about 10 to 20% higher than for <100>); the relative doping ^ concentrations of the polycrystalline silicon gate and the silicon substrate (10 20 -10 21 atoms per cubic centimeter polysilicon provides an oxide thickness of about 6 to 10 times that of undoped <100> silicon); oxidation temperature (the highly doped/lightly doped " growth rate ratio increases as the oxidation temperature is lowered) , and the oxidation pressure (oxidation rates increase with increasing temperature and, generally, increase faster for highly doped silicon than for lightly or undoped silicon) . Because - " of these factors and the enhancing effect of low temperature on the growth rate ratio, in one preferred embodiment of the present polysilicon sidewall oxidation technique (using <100> silicon substrate p-region 10 and n-wells 13, a polysilicon gate phosphorus dopant concentration of about 10 20 -10 21 atoms per cubic centimeter, and p-region 10 and n-well - 13 arsenic surface concentrations of about lO^-lO 18 atoms per cubic centimeter), the thicknesses of the polysilicon sidewall oxides 21N and 21P and the oxide layer formed over thin oxide layer 15 will be approximately 440 nanometers and 70 nanometers, respectively, when the substrate is subjected to an oxidation step at ambient pressure and temperature of about 750°C for a period of three hours. The thickness of the polysilicon sidewall oxide regions 21N and 21P is approximately six times that of the substrate oxide. The total thickness of the thermal substrate oxide and existing gate oxide 15 was 120 nanometers. The resulting structure is shown in FIG. 3. Next, referring to FIG. 4, a mask 26 is formed over the PMOS active regions using conventional photoresist and photolithographic forming techniques and the heavily doped n + source and drain regions 27N and 28N for the NMOS device are implanted. Arsenic is a preferred dopant, because the relatively heavy mass and relatively small diffusion coefficient of arsenic makes it relatively immobile and forms a shallow junction. One typical example of this step, for forming arsenic-doped source and drain regions 27N and 28N of concentration 10 20 atoms/cc involves an implant of 5E15-5E16 cm "2 at an energy of 80 keV. During implantation, the oxide 17N-nitride 18N composite masking structure masks the underlying channel 30N and LDD regions so that the heavily doped n + regions 27 and 28 are formed spaced away from the channel region adjacent to the LDD region. Referring to FIG. 5, next the sidewall oxide regions 21N are isotropically etched to partially reduce the thickness thereof. A typical process involves a 30°1 HF dip for 30 seconds. The purpose is to decrease the original thickness of the sidewall oxide 21N from about 440 nanometers to about 150 nanometers, to provide adequate electrical separation for the subsequently formed gate and source/drain metallization, and provide a dopant mask for the LDD regions which nonetheless permits light doping thereof. The resulting reduced thickness sidewall oxide regions 29N are shown in FIG. 5. Following sidewall reduction, and referring to FIG. 6, the nitride cap 18N and oxide pad 17N are removed by conventional techniques such as a plasma etch, or a nitride etch using concentrated hot phosphoric acid at about 160°C followed by oxide removal in buffered hydrofluoric acid. During this removal sequence, the NMOS sidewall oxide 29N will also be etched. However, as the residual sidewall oxide thickness is relatively large, the relatively small additional thickness removed does not alter the above characteristics of electric isolation and dopant mask. The etch process also removes the substrate surface oxide 15 outside the PMOS mask 26. With the composite oxide-nitride mask removed as shown in FIG. 6, the structure is subjected to a light dopant step using-n-type ions such as arsenic to deposit the- shallow,-lightly doped n~ source and drain regions 31N and 32N, respectively. Typical arsenic ion dose and energy for forming the n " regions are 1E13-1E14 cm "2 and 160 keV, respectively. The resulting lightly doped source and drain regions 31N and 32N have a very shallow junction depth of about 100-150 nanometers, are self-aligned with the gate electrode 16N and are in electrical contact with the deep n + source and drain contact regions 27N and 28N. Subsequently, the mask 26 is removed. The next step, optional for CMOS, involves a thermal anneal in an inert ambient such as nitrogen or argon to drive in the n + source-drain regions 27N and 28N. An anneal at 900°C for one hour results in n + junction depths of about 200 to 400 nanometers. The lightly doped arsenic regions 31N and 32N have excellent dimensional thermal stability; their junction depth and lateral dimensions are not changed significantly by the n + anneal. The above sequence substantially completes the crucial NMOS process steps except for the formation of the p-type guard bands 33N and 34N, FIG. 10. In the event PMOS devices are not formed, a light p-type boron guard band implant can be made at this point to complete the critical NMOS-only fabrication steps. Preferably, for CMOS processes, these guard bands are formed subsequently during the PMOS LDD formation to save a dopant step. As stated previously, the nitride-oxide composite masking structure is a sufficient mask for the n + source-drain doping step (and the subsequent p + source-drain doping step) . Therefore, the sidewall oxide spacers can be eliminated for the NMOS and/or the PMOS device in the event they are not required for isolation between the gate and source/drain conductors. When the sidewall oxide spacers are present, however, they can be used to reduce the thickness of the oxide 17-nitride 18 mask or of the nitride-only mask. The separate PMOS processing starts at FIG. 7 and is similar to the NMOS process. Initially, a mask 36 is formed over the NMOS active regions. To accomplish this, a photoresist layer may be formed and conventional photolithographic techniques used to pattern the mask. The deep p + source and drain regions 27P and 28P are then formed using boron or other p-type dopant species. A typical boron implant sequence involves a dose of 2E15-1E16 cm "2 and an energy of 20 keV to form a concentration of 2E10 20 atoms/cc. Referring to FIG. 8, the lateral thickness of the PMOS gate sidewall oxide spacers 21P are then reduced using the same etching process which was described relative to the NMOS device, FIG. 5, and with substantially identical results. The oxide 17P- nitride 18P composite mask is then removed as described relative to the NMOS device, FIG. 5 See Fig. 9. Referring further to FIG. 9, shallow, relatively heavy doped n + guard band regions 33P and 5 34P are then formed in the PMOS active region, self- aligned with the gate 16P. Note, the sidewall oxide spacers 29P absorb some of the incident ions, but the dose/energy and implant angle is readily adjusted to compensate for this. This absorption/compensation 1.0. applied to the other LDD and guard band doping steps as well. Preferably, a relatively heavy, immobile n- type dopant species such as phosphorus- is used to provide a shallow junction depth, minimum overlap of the guard bands 33P, 34P with the gate, and minimum 15 lateral and vertical diffusion during the subsequent thermal processing. A typical phosphorus guard band ,„„ implant sequence involves»a dose of 8E12_-cm~ 2 ,an_i__ J an -~» energy of 120 keV. Referring now to FIG. 10, after the PMOS 2.0. guard band formation, the NMOS mask_,36 is removed and the integrated circuit structure is given a shallow - blanket p-type implant to simultaneously form the PMOS LDD regions 31P and 32P along with the NMOS guard band regions 33N and 34N. A suitable boron implant process 53 for this step involves a boron dose of 5E13 cm "2 and implant energy of 20 keV. The implant (and the subsequent diffusion of the mobile boron atoms compared to the relatively immobile n-type atoms) forms the NMOS guard bands 33N and 34N at a junction 0 depth of about 200 nanometers, just slightly deeper than the 150 nanometer junction depth of the associated LDD regions 31N and 32N. This implant simultaneously forms the PMOS LDD regions 31P and 32P to a junction depth of about 200 nanometers which is 5 slightly shallower than the 250 nanometer junction depth of the associated guard band regions 33P and 34P. The representations of the LDD and guard band regions as depicted in the drawings have been exaggerated to accentuate the structural effects. The CMOS structure is annealed as described previously in an inert ambient such as nitrogen or argon to drive in the heavily doped p + and n + regions to the final junction depths of about 200 nanometers for the NMOS source and drain and about 350 nanometers for the PMOS source and drain. The LDD short channel regions and the guard band regions are substantially unaffected by this anneal, because these lightly doped regions do not diffuse substantially at the annealing temperatures used. Next, referring to FIG. 11, a metal such as tungsten is selectively deposited to a thickness of about 100 to 200 nanometers, for example, using chemical vapor deposition and gaseous tungsten hexafluoride (WF5), over all the exposed areas,of the silicon substrate and the polysilicon agates 16N and 16P. During this selective deposition step, no tungsten is formed over the oxide regions such as sidewalls 29N and 29P. The tungsten conducting members 41N, 41P, 42N, 42P, 46N and 46P formed in this manner make electrical contact, respectively, with the source and drain regions 27N, 27P, 28N and 28P and polysilicon gate electrodes 16N and 16P. Other metals that are suitable for substitution for tungsten include refractory metal suicides such as tungsten suicide. The disclosed process of the present invention provides NMOS and CMOS devices having polysilicon- gates and interconnects which are 1-5 micrometers or less in width and having source and drain regions which are 1-3 micrometers or less on a side. The use of gate sidewall oxide spacers prevents short-circuiting between adjacent conductors such as those formed on the gate electrodes and source/drain regions. The minimum spacing between such conductors is determined by photolithographic limitations. Using the disclosed process in conjunction with conventional optical lithography, it is possible to use a conductor spacing of one micrometer. The use of x-ray " lithography or other more precise lithography will reduce the interconductor or interconnect spacing to much less than 1 micrometer. The present process also creates shallow diffusions of the same type as the source/drain 0: diffusions, but which are more lightly doped. The shallow LDD diffusions are less subject to redistribution upon anneal and are therefore very closely aligned to the edge of the polysilicon gates and, as a consequence, reduce Miller capacitance and 5 allow faster device operation compared to conventional CMOS processing. The deeper, highly doped source/drain regions 27 and 28 are provided by the ____ process at a distance far enough away from the gate to allow the shallow diffused LDD regions 31N, 32N, 32P ϋ ~ and 33P to determine critical device characteristics, yet still provide low resistance connections. In addition, the process provides shallow guard bands 33N, 34N, 33P and 34P of doped silicon at the junction edges of the LDD diffusion regions. These guard bands : are of the opposite conductivity type as the source/drain diffusions. The guard bands are the same conductivity type as the corresponding bulk substrate, epi layer or well regions. The guard bands are more highly doped than are the bulk regions, however, and ' yield the advantages of using a more highly doped bulk region without increasing the back-gate effect or junction capacitance. Furthermore, the overall process is designed so that in the event any of the above features is not " critical to a particular integrated circuit, it can be deleted. Because of the control which is provided over the degrading effects normally associated with small dimension devices, and because of the associated processing simplicity, which is similar to that of conventional CMOS processes, the present process is amenable to the high yield manufacture of high- quality, short channel integrated circuit devices.

Claims: CLAIMS ; 1. A process for forming a complementary PMOS and NMOS integrated circuit structure, characterized by the steps of: forming a gate structure for each device having an overlying overhang mask (17N, 18N; 17P, 18P) ; defining underlying regions adjacent the gate structure as source and drain regions; doping the NMOS source and drain regions with n-type dopant in the presence of the NMOS overhang mask to form the heavily doped n-type source and drain regions (27N, 28N) in self-alignment with the NMOS overhang mask; removing the NMOS overhang mask; relatively lightly doping the NMOS active areas adjacent the gate structure with n-type dopant to form LDD regions (31N, 32N) in self-alignment with the NMOS gate between the ' gate~aa highly doped source and drain regions_(_27N, -28N-) r r selectively doping the PMOS source and drain regions with p-type dopant in the presence of the PMOS overhang mask to form the heavily doped p-type source and drain regions (27P, 28P) in self-alignment with the PMOS overhang mask;...removing the PMOS overhang mask; and relatively lightly doping the PMOS active areas-adjacent the gate structure with p-type dopant to form LDD structures (31P, 32P) in self-alignment with the PMOS gate between the gate and the highly doped source and drain regions (27P, 28P). 2. A process according to claim 1, characterized in that after removal of the PMOS overhang mask, the structure is selectively doped with n-type impurities to form guard band regions (33P, 34P) for the PMOS LDD structures. 3. A process according to claim 2, characterized in that the PMOS LDD doping step is a blanket doping step for simultaneously forming (a) p- type guard bands (33N, 34N) for the NMOS LDD structures and (b) the p-type LDD structures (31P, 32P) for the PMOS structures. 4. A process according to claim 1, characterized in that after forming the gate structures and the overlying overhang masks, the resulting structure is placed in an oxidizing ambient at a relatively low temperature to preferentially form a layer of oxide (21N, 21P) on the sidewalls of the highly doped NMOS and PMOS gate structures. 5. A process according to claim 4, characterized in that after the doping step for the NMOS heavily doped n-type source and drain, the NMOS sidewall oxide (21N) is etched to reduce the thickness thereof; and in that after the doping step for the PMOS heavily doped p-type source and drain regions, the PMOS sidewall oxide (21P) is etched to reduce the thickness thereof.

Inventors: MILLER GAYLE WILBURN, SZLUK NICHOLAS JOHN, MILLER, GAYLE, WILBURN, SZLUK, NICHOLAS, JOHN
Applicants: NCR CO, NCR CORPORATION
Application year: 1987
Main classification: H01L21
IPC codes: H01L21, H01L27, H01L29