LIGHT SENSITIVE MATERIAL CONTAINING SILVER HALIDE, REDUCING AGENT AND POLYMERIZABLE COMPOUND

Abstract: A light-sensitive material comprising a light-sensitive layer which contains silver halide, a reducing agent and a polymerizable compound provided on a support, charac­ terized in that the silver halide and the polymerizable compound are together contained in microcapsules which are dispersed in the light-sensitive layer, and the light-­ sensitive layer further contains dispersed grains of a hyd­ rophobic organic base compound and/or base precursor having a melting point of from 80 to 180°C which are arranged outside of the microcapsules.

Description: BACKGROUND OF THE INVENTION Field of the invention This invention relates to a light-sensitive material comprising a light-sensitive layer containing silver halide, a reducing agent and a polymerizable compound provided on a support. Description of prior arts Light-sensitive materials comprising a light-sensitive layer containing silver halide, a reducing agent and a polymerizable compound provided on a support can be used in an image forming method in which a latent image of silver halide is formed, and then the polymerizable compound is polymerised to form the corresponding image. Examples of said image forming methods are described in Japanese Patent Publication Nos. 45(1970)-11149 (corresponding to U.S. Patent No. 3,697,275), 47(1972)-20741 (corresponding to U.S. Patent No. 3,657,667) and 49(1974) -10697, and Japanese Patent Provisional Publication Nos. 57(1982)-138632, 57(1982)-142638, 57(1982)-176033, 57(1982)-211146 (corresponding to U.S. Patent No. 4,557,997), 58(1983)-107529 (corresponding to U.S. Patent No. 4,560,637), 58(1983)-121031 (corresponding to U.S. Patent No. 4,547,450) and 58(1983)-169143. In these image forming methods, when the exposed silver halide is developed using a developing solution, the polymerizable compound is induced to polymerize in the presence of a reducing agent (which is oxidized) to form a polymer image. Thus, these methods need a wet development process employing a developing solution. Therefore the process takes a relatively long time. An improved image forming method employing a dry process is described in Japanese Patent Provisional Publication Nos. 61(1986)-69062 and 61(1986)-73145 (the contents of both publications are described in U.S. Patent No. 4,629,676 and European Patent Provisional Publication No. 0174634A2). In this image forming method, a recording material (i.e., light-sensitive material) comprising a light-sensitive layer containing a light-sensitive silver salt (i.e., silver halide), a reducing agent, a cross -linkable compound (i.e., polymerizable compound) and a binder provided on a support is imagewise exposed to form a latent image, and then the material is heated to polymerize within the area where the latent image of the silver halide has been formed. The above method employing the dry process and the light-sensitive material employable for such method are also described in Japanese Patent Provisional Publication Nos. 61(1986)-183640, 61(1986)-188535 and 61(1986)-228441. The above-mentioned image forming methods are based on the principle in which the polymerizable compound is polymerized within the area where a latent image of the silver halide has been formed. Further, Japanese Patent Provisional Publication No. 61(1986)-260241 describes another image forming method in which the polymerizable compound in a portion where a latent image of the silver halide has not been formed is polymerized. In this method, when the material is heated, the reducing agent functions as polymerization inhibitor in the portion where a latent image of the silver halide has been formed, and the polymerizable compound in the other portion is polymerized. In the light-sensitive material employed in these image forming method, the silver halide and the polymerizable compound can be contained in a microcapsule. The light-sensitive material employing the microcapsule is described in Japanese Patent Application No. 60(1985)-261888. The light-sensitive material containing such microcapsules has an adventage in that the reaction to accelerate (or inhibit) the polymerization in the area where a latent image of silver halide has been formed can smoothly progress. SUMMARY OF THE INVENTION An object of the present invention is to provide a light-sensitive material which is improved both in the preservability and in the sensitivity. There is provided by the present invention a light-sensitive material comprising a light-sensitive layer which contains silver halide, a reducing agent and a polymerizable compound provided on a support, characterized in that the silver halide and the polymerizable compound are together contained in microcapsules which are dispersed in the light-sensitive layer, and the light-sensitive layer further contains dispersed grains of a hydrophobic organic base compound and/or base precursor having a melting point of from 80 to 180°C which are arranged outside of the microcapsules. Preferably, the silver halide, the polymerizable compound and the reducing agent are together contained in the microcapsules. The light-sensitive layer preferably further contains a hot-melt solvent. The hydrophobic organic base compound or base precursor preferably is a guanidine derivative, more preferably is a guanidine derivative having a pKa of not less than 8, or one being insoluble in water. In the light-sensitive layer of the material of the present invention, a hydrophobic organic base compound or base precursor having a melting point of from 80 to 180°C which functions as an image-formation accelerator is contained in the form of dispersion of the solid grains thereof. Therefore, the base compound or base precursor is not deteriorated even if the light-sensitive material has been preserved for a long term after the preparation, because the base compound or base precursor in the above form is not susceptible to influences from the outside, such as moisture. Further, these grains are arranged outside of the microcapsules in the light-sensitive layer. The other compornents contained in the microcapsules, the silver halide, the polymerizable compound and preferably the reducing agent are not influenced by the base compound or base precursor. As a result, the light-sensitive material can maintain the high sensitivity over a long time of period. In a heat development process, the organic base compound or the base released from the base precursor can easily permeate the microcapsule containing the silver halide, the polymerizable compound and preferably the reducing agent, because the organic base compound of the invention melts to be fluid in the vicinity of the heating temperature in the development process. Therefore, the base compound or base precursor can effectively accelerate the polymerization of the polymerizable compound. Further, in the case that the light-sensitive layer further contains a hot-melt solvent, the hot-melt solvent functions for plasticizing the shell material of the microcapsule when the hot-melt solvent is brought in contact with the microcapsule in a development process. Therefore, in the light-sensitive layer containing the hot-melt solvent, the organic base or the other components arranged outside of the microcapsule can more easily permeat the microcapsule. DETAILED DESCRIPTION OF THE INVENTION The light-sensitive layer of the light-sensitive material of the present invention contains dispersed grains of a hydrophobic organic base compound and/or base precursor having a melting point of from 80 to 180°C which are arranged outside of the microcapsules. The hydrophobic organic base compound or base precursor has a function of accelerating the oxidation-reduction reaction between the silver halide (and/or an organic silver salt) and the reducing agent. Preferred examples of the hydrophobic organic base compound include aliphatic amines (e.g., trialkylamines, hydroxylamines and aliphatic polyamines); aromatic amines (e.g., N-alkyl-substituted aromatic amines, N-hydroxylalkyl-substituted aromatic amines and bis[p-(dialkylamino)phenyl]methanes), heterocyclic amines, amidines, cyclic amidines, guanidines, and cyclic guanidines. Of these organic base compounds, those having a pKa of 8 or more are preferred. The base precursor preferably is a compound which can release the above mentioined organic base compound when it is heated. The base precursor more preferably is a salt comprising the above mentioned organic base compound and an organic acid. Examples of the organic acid include trichloroacetic acid, phenylsulfonylacetic acid, 4-chlorophenylsulfoylacetic acid, 4-methyl-sulfonyl-phenylsulfonylacetic acid and 4-acetylaminomethyl propionic acid. These hydrophobic organic base compounds and/or base precursor are preferably used in an amount of not more than 50 % by weight, and more preferably from 0.01 to 40 % by weight, based on the total solid content of the light-sensitive layer. These hydrophobic organic base compounds can be used singly or in combination. The grains of a hydrophobic organic base compound preferably are despersed in a water-soluble polymer. Examples of the water-soluble polymer include polyvinyl alcohol, polyacrylamide, a cellulose derivative and gelatin. Examples of the guanidine derivative which are preferably used as the hydrophobic organic base compound in the invention will be described hereinafter. in which each of R¹ to R⁹ and R¹¹ to R¹⁴ independently is a monovalent group selected from the group consisting of hydrogen, an alkyl group containing 1 - 18 carbon atoms, a cycloalkyl group, an aralkyl group, amino, an alkylamino, an acylamino, carbamoylamino a heterocyclic group and an aryl group which may be substituted with a monovalent group selected from the group consisting of a lower alkyl group, an alkoxyl group, nitro, an acylamino group, an alkylamino group and a halogen atom; and R¹⁰ is a divalent group selected from the group consisting of a lower alkylene, phenylene, naphthylene and (X is a single bond or a divalent group selected from the group consisting of a lower alkylene, -SO₂-, -S₂-, -S-, -O- and -NH-). Concrete examples of the guanidine derivative will be described hereinafter. In the following formula, is cyclohexyl. These guanidine derivatives can be prepared according to a known method or analogous methods. In the light-sensitive material of the invention, the light-sensitive layer preferably contains a hot-melt solvent. The hot-melt solvent means a compound which is in solid state at room temperature, and melts at heating temperature in the development process to function as a solvent of the base compound. The hot-melt solvent preferably is a compound having a melting point of not lower than about 40°C. Examples of the hot-melt solvent include urea, urethane, amide, polyol (e.g., sorbitol, dulcitol, mannitol, trimethylolpropane, dimethylolurea), sulfonamide, sulfone, sulfoxide, ester, ketone, ether and derivatives of these compound. The hot-melt solvent can be a compound which may be used as a solvent of the reducing agent or that which has high dielectric constant and can accelerate physical development of silver salts. Examples of the above hot-melt solvent include polyethylene glycols, derivatives of polyethylene oxides (e.g., oleate ester), beeswax, monostearin and high dielectric constant compounds having -SO₂- and/or -CO- group described in U.S. Patent No. 3,347,675; polar compounds described in U.S. Patent No. 3,667,959; and 1,10-decanediol, methyl anisate and biphenyl suberic acid described in Research Disclosure 26-28 (November 1976). The hot-melt solvent is preferably used in an amount of from 0.5 to 50 % by weight, and more preferably from 1 to 20 % by weight, based on the total solid content of the light-sensitive layer. The microcapsule containing the silver halide and the polymerizable compound, the reducing agent, and the support which constitute the light-sensitive material of the invention with the hydrophobic organic base compound are described below. Thus composed material is referred hereinafter to as "light-sensitive material". There is no specific limitation with respect to silver halide contained in the light-sensitive layer of the light-sensitive material. Examples of the silver halides include as silver chloride, silver bromide, silver iodide, silver chlorobromide, silver chloroiodide, silver iodobromide, and silver chloroiodobromide in the form of grains. The halogen composition of individual grains may be homogeneous or heterogeneous. The heterogeneous grains having a multilayered structure in which the halogen composition varies from the core to the outer shell (see Japanese Patent Provisional Publication Nos. 57(1982)-154232, 58(1983)-108533, 59(1984)-48755 and 59(1984)-52237, U.S. Patent No. 4,433,048, and European Patent No. 100,984) can be employed. There is no specific limitation on the crystal habit of silver halide grains. Two or more kinds of silver halide grains which differ in halogen composition, crystal habit, grain size, and/or other features from each other can be used in combination. There is no specific limitation on grain size distribution of silver halide grains. The silver halide grains ordinarily have a mean size of 0.001 to 5 µm, more preferably 0.001 to 2 µm. The total silver content (including silver halide and an organic silver salt which is one of optional components) in the light-sensitive layer preferably is in the range of from 0.1 mg/m² to 10 g/m². The silver content of the silver halide in the light-sensitive layer preferably is not more than 1 g/m², more preferably in the range of from 1 mg to 500 mg/m². The reducing agent employed in the light-sensitive material has a function of reducing the silver halide and/or a function of accelerating or restraining a polymerization of the polymerizable compound. Examples of the reducing agents having these functions include various compounds, such as hydroquinones, catechols, p-aminophenols, p-phenylenediamines, 3-pyrazolidones, 3-aminopyrazoles, 4-amino-5-pyrazolones, 5-aminouracils, 4,5-dihydroxy-6-aminopyrimidines, reductones, aminoreductones, o- or p-sulfonamidophenols, o- or p-sulfonamidonaphthols, 2-sulfonamidoindanones, 4-sulfonamido-5-pyrazolones, 3-sulfonamidoindoles, sulfonamidopyrazolobenzimidazoles, sulfonamidopyrazolotriazoles, α-sulfonamidoketones, hydrazines, etc. Depending on the nature or amount of the reducing agent, the polymerizable compound in either a portion where a latent image of the silver halide has been formed or a portion where a latent image of the silver halide has not been formed can be polymerized. In the developing system in which the polymerizable compound in the portion where the latent image has not been formed is polymerized, 1-phenyl-3-pyrazolidone is preferably employed as the reducing agent. The light-sensitive materials employing the reducing agent having these functions (including compounds referred to as developing agent or hydrazine derivative) are described in Japanese Patent Provisional Publication Nos. 61(1986)-183640, 61(1986)-188535 and 61(1986)-228441, and Japanese Patent Application Nos. 60(1985)-210657, 60(1985)-226084, 60(1985)-227527 and 60(1985)-227528. These reducing agents are also described in T. James, "The Theory of the Photographic Process", 4th edition, 291-334 (1977), Research Disclosure No. 17029, 9-15 (June 1978), and Research Disclosure No. 17643, 22-31 (December 1978). The reducing agents described in the these publications and applications can be employed in the light-sensitive material of the present invention. Thus, "the reducing agent(s)" in the present specification means to include all of the reducing agents described in the above mentioned publications and applications. These reducing agents can be used singly or in combination. In the case that two or more reducing agents are used in combination, certain interactions between these reducing agents may be expected. One of the interactions is for acceleration of reduction of silver halide (and/or an organic silver salt) through so-called super-additivity. Other interaction is for a chain reaction in which an oxidized state of one reducing agent formed by a reduction of silver halide (and/or an organic silver salt) induces or inhibits the polymerization of the polymerizable compound via oxidation-reduction reaction with other reducing agent. Both interactions may occur simultaneously. Thus, it is difficult to determine which of the interactions has occurred in practical use. Examples of these reducing agents include pentadecylhydroquinone, 5-t-butylcatechol, p-(N,N-diethylamino)-phenol, 1-phenyl-4-methyl-4-hydroxymethyl-3-pyrazolidone, 1-phenyl-4-methyl-4-heptadecylcarbonyloxymethyl-3-pyrazolidone, 2-phenylsulfonylamino-4-hexadecyloxy-5-t-octylphenol, 2-phenylsulfonylamino-4-t-butyl-5-hexadecyloxyphenol, 2-(N-butylcarbamoyl)-4-phenylsulfonylaminonaphtol, 2-(N-methyl-N-octadecylcarbamoyl)-4-sulfonylaminonaphthol, 1-acetyl-2-phenylhydrazine, 1-acetyl-2-(p- or o-aminophenyl)hydrazine, 1-formyl-2-(p or o-aminophenyl)hydrazine, 1-acetyl-2-(p- or o-methoxyphenyl)hydrazine, 1-lauroyl-2-(p- or o-aminophenyl)hydrazine, 1-trityl-2-(2,6-dichloro-4-cyanophenyl)hydrazine, 1-trityl-2-phenylhydrazine, 1-phenyl-2-(2,4,6-trichlorophenyl)hydrazine, 1-{2-(2,5-di-tert-pentylphenoxy)butyloyl}-2-(p- or o-aminophenyl)hydrazine, 1-{2-(2,5-di-t-pentylphenoxy)-butyloyl}-2-(p- or o-aminophenyl)hydrazine pentadecylfluorocaprylate salt, 3-indazolinone, 1-(3,5-dichlorobenzoyl)-2-phenylhydrazine, 1-trityl-2-[{(2-N-butyl-N-octylsulfamoyl)-4-methanesulfonyl}phenyl]hydrazine, 1-{4-(2,5-di-tert-pentylphenoxy)butyloyl}-2-(p- or o-methoxyphenyl)hydrazine, 1-(methoxycarbonylbenzohydryl)-2-phenylhydrazine, 1-formyl-2-[4-{2-(2,4-di-tert-pentyl-phenoxy)butylamide}phenyl]hydrazine, 1-acetyl-2-[4-{2-(2,4-di-tert-pentylphenoxy)butylamido}phenyl]hydrazine, 1-trityl-2-[{2,6-dichloro-4-(N,N-di-2-ethylhexyl)carbamoyl}phenyl]hydrazine, 1-(methoxycarbonylbenzohydryl)-2-(2,4-dichlorophenyl)hydrazine and 1-trityl-2-[{2-(N-ethyl -N-octylsulfamoyl)-4-methanesulfonyl}phenyl]hydrazine. The amount of the reducing agent in the light-sensitive layer preferably ranges from 0.1 to 1,500 mole % based on the amount of silver (contained in the silver halide and an organic silver salt). These reducing agents can be contained in the micro-capsule or arranged outside of the microcapsule in the light-sensitive layer. Generally, the reducing agent is preferably contained in the microcapsule, because the reaction can progress smoothly in such case. The reducing agent is more preferably dispersed or dissolved in the core material containing the polymerizable compound. In the case that heat development is utilized in the use of the light-sensitive material, there is no problem in arranging the reducing agent outside of the microcapsule, because the reducing agent can permeate the microcapsule to reach the core material. There is no specific limitation with respect to the polymerizable compound, and any known polymerizable compounds including monomers, oligomers and polymers can be contained in the light-sensitive layer. In the case that heat development (i.e., thermal development) is utilized for developing the light-sensitive material, the polymerizable compounds having a relatively higher boiling point (e.g., 80°C or higher) that are hardly evaporated upon heating are preferably employed. In the case that the light-sensitive layer contains a color image forming substance, the polymerizable compounds are preferably cross-linkable compounds having plural polymerizable groups in the molecule, because such cross-linkable compounds favorably serve for fixing the color image forming substance in the course of polymerization hardening of the polymerizable compounds. The polymerizable compound employable for the light-sensitive material of the invention are described in the above-mentioned and later-mentioned publications and applications concerning the light-sensitive material. Preferred polymerizable compounds employable for the light-sensitive material are compounds which are polymerizable through addition reaction or ring-opening reaction. Preferred examples of the compounds being polymerizable through addition reaction include compounds having an ethylenic unsaturated group. Preferred examples of the compounds being polymerizable through ring-opening reaction include the compounds having an epoxy group. Among them, the compounds having an ethylenic unsaturated group are preferred. Examples of compounds having an ethylenic unsaturated group include acrylic acid, salts of acrylic acid, acrylic esters, acrylamides, methacrylic acid, salts of methacrylic acid, methacrylic esters, methacrylamide, maleic anhydride, maleic esters, itaconic esters, styrene, styrene derivatives, vinyl ethers, vinyl esters, N-vinyl heterocyclic compounds, allyl ethers, allyl esters, and compounds carrying a group or groups corresponding to one or more of these compounds. Concrete examples of the acrylic esters include n-butyl acrylate, cyclohexyl acrylate, 2-ethylhexyl acrylate, benzyl acrylate, furfuryl acrylate, ethoxyethoxy acrylate, dicyclohexyloxyethyl acrylate, nonylphenyloxyethyl acrylate, hexanediol diacrylate, butanediol diacrylate, neopentylglycol diacrylate, trimethylolpropane triacrylate, pentaerythritol tetraacrylate, dipentaerythritol pentaacrylate, diacrylate of polyoxyethylenated bisphenol A, polyacrylate of hydroxypolyether, polyester acrylate, and polyurethane acrylate. Concrete examples of the methacrylic esters include methyl methacrylate, butyl methacrylate, ethylene glycol dimethacrylate, butanediol dimethacrylate, neopentylglycol dimethacrylate, trimethylolpropane trimethacrylate, pentaerythritol trimethacrylate, pentaerythritol tetramethacrylate, and dimethacrylate of polyoxyalkylenated bisphenol A. The polymerizable compounds can be used singly or in combination of two or more compounds. Further, compounds formed by bonding a polymerizable group such as a vinyl group or a vinylidene group to a reducing agent or a color image forming substance are also employed as the polymerizable compounds. The light-sensitive materials employing these compounds which show functions as both the reducing agent and the polymerizable compound, or of the color image forming substance and the polymerizable compound are included in embodiments of the invention. The amount of the polymerizable compound for incorporation into the light-sensitive layer preferably ranges from 5 to 1.2x10⁵ times (by weight) as much as the amount of silver halide, more preferably from 10 to 1x10⁴ times as much as the silver halide. There is no specific limitation on preparation of the microcapsules. There is also no specific limitation with respect to the shell material of the microcapsule, and various known materials such as polymers which are used in the conventional microcapsules can be employed as the shell material. The mean particle size of the microcapsule preferably ranges from 0.5 to 50 µm, more preferably 1 to 25 µm, most preferably 3 to 20 µm. The light-sensitive material of the invention can be prepared by arranging a light-sensitive layer containing the above-mentioned components on a support. There is no limitation with respect to the support. In the case that heat development is utilized in the use of the light-sensitive material, the material of the support preferably is resistant to heat given in the processing stage. Examples of the material employable for the preparation of the support include glass, paper, fine paper, coat paper, synthetic paper, metals and analogues thereof, polyester, acetyl cellulose, cellulose ester, polyvinyl acetal, polystyrene, polycarbonate, polyethylene terephthalate, and paper laminated with resin or polymer (e.g., polyethylene). The light-sensitive layer can further contain optional components such as color image forming substances, sensitizing dyes, organic silver salts, various kinds of image formation accelerators, thermal polymerization inhibitors, thermal polymerization initiators, development stopping agents, fluorescent brightening agents, discoloration inhibitors, antihalation dyes or pigments, antiirradiation dyes or pigments, matting agents, anti-smudging agents, plasticizers, water releasers and binders. There is no specific limitation with respect to the color image forming substance, and various kinds of substances can be employed. Thus, examples of the color image forming substance include both colored substance (i.e., dyes and pigments) and non-colored or almost non-colored substance (i.e., color former or dye- or pigment-precursor) which develops to give a color under application of external energy (e.g., heating, pressing, light irradiation, etc.) or by contact with other components (i.e., developer). The light-sensitive material using the color image forming substance is described in Japanese Patent Provisional Publication No. 61(1986)-73145. Examples of the dyes and pigments (i.e., colored substances) employable in the invention include commercially available ones, as well as various known compounds described in the technical publications, e.g., Yuki Gosei Kagaku Kyokai (ed.), Handbook of Dyes (in Japanese, 1970) and Nippon Ganryo Gijutsu Kyokai (ed.), New Handbook of Pigments (in Japanese, 1977). These dyes and pigments can be used in the form of a solution or a dispersion. Examples of the substances which develop to give a color by certain energy includes thermochromic compounds, piezochromic compounds, photochromic compounds and leuco compounds derived from triarylmethane dyes, quinone dyes, indigoid dyes, azine dyes, etc. These compounds are capable of developing a color by heating, application of pressure, light-irradiation or air-oxidation. Examples of the substances which develop to give a color in contact with other components include various compounds capable of developing a color through some reaction between two or more components, such as acid-base reaction, oxidation-reduction reaction, coupling reaction, chelating reaction, and the like. Examples of such color formation systems are described in Hiroyuki Moriga, "Introduction of Chemistry of Speciality Paper" (in Japanese, 1975), 29-58 (pressure-sensitive copying paper), 87-95 (azo-graphy), 118-120 (heat-sensitive color formation by a chemical change) or in MSS. of the seminer promoted by the Society of Kinki Chemical Industry, "The Newest Chemistry of Coloring Matter - Attractive Application and New Development as a Functional Coloring Matter", 26-32 (June, 19, 1980). Examples of the color formation systems specifically include a color formation system used in pressure-sensitive papers, etc., comprising a color former having a partial structure of lactone, lactam, spiropyran, etc., and an acidic substance (developer), e.g., acid clay, phenol, etc.; a system utilizing azo-coupling reaction between an aromatic a diazonium salt, diazotate or diazosulfonate and naphthol, aniline, active methylene, etc.; a system utilizing a chelating reaction, such as a reaction between hexamethylenetetramine and a ferric ion and gallic acid, or a reaction between a phenolphthalein-complexon and an alkaline earth metal ion; a system utilizing oxidation-reduction reaction, such as a reaction between ferric stearate and pyrogallol, or a reaction between silver behenate and 4-methoxy-1-naphthol, etc. The color image forming substance in the light-sensitive material is preferably used in an amount of from 0.5 to 50 parts by weight, and more preferably from 2 to 30 parts by weight, per 100 parts by weight of the polymerizable compound. In the case that the developer is used, it is preferably used in an amount of from about 0.3 to about 80 parts by weight per one part by weight of the color former. There is no specific limitation with respect to the sensitizing dyes, and known sensitizing dyes used in the conventional art of photography may be employed in the light-sensitive material of the invention. Examples of the sensitizing dyes include methine dyes, cyanine dyes, merocyanine dyes, complex cyanine dyes, complex merocyanine dyes, holopolar cyanine dyes, hemicyanine dyes, styryl dyes, and hemioxonol dyes. These sensitizing dyes can be used singly or in combination. Combinations of sensitizing dyes are often used for the purpose of supersensitization. In addition to the sensitizing dyes, a substance which does not per se exhibit spectral sensitization effect or does not substantially absorb visible light but shows supersensitizing activity can be used. The amount of the sensitizing dye to be added generally ranges from about 10⁻⁸ to about 10⁻² mol per 1 mol of silver halide. The sensitizing dye is preferably added during the stage of the preparation of the silver halide emulsion. When the heat development is employed in the use of the light-sensitive material, an organic silver salt is preferably contained in the light-sensitive material. It can be assumed that the organic silver salt takes part in a redox reaction using a silver halide latent image as a catalyst when heated to a temperature of 80°C or higher. In such case, the silver halide and the organic silver salt preferably are located in contact with each other or close together. Examples of organic compounds employable for forming such organic silver salt include aliphatic or aromatic carboxylic acids, thiocarbonyl group-containing compounds having a mercapto group or an α-hydrogen atom, imino group-containing compounds, and the like. Among them, benzotriazoles are most preferable. The organic silver salt is preferably used in an amount of from 0.01 to 10 mol., and preferably from 0.01 to 1 mol., per 1 mol. of the light-sensitive silver halide. Instead of the organic silver salt, an organic compound (e.g., benzotriazole) which can form an organic silver salt in combination with an inoganic silver salt can be added to the light-sensitive layer to obtain the same effect. Various image formation accelerators are employable in the light-sensitive material of the invention. The image formation accelerators have a function to accelerate the oxidation-reduction reaction between a silver halide (and/or an organic silver salt) and a reducing agent, a function to accelerate emigration of an image forming substance from a light-sensitive layer to an image-receiving material or an image-receiving layer, or a similar function. The image formation accelerators can be classified into oils, surface active agents and the like. These groups, however, generally have certain combined functions, i.e., two or more of the above-mentioned effects. Thus, the above classification is for the sake of convenience, and one compound often has a plurality of functions combined. Various examples of these image formation accelerators are shown below. Examples of the oils employable in the invention include high-boiling organic solvents which are used as solvents in emulsifying and dispersing hydrophobic compounds. Examples of the surface active agents employable in the invention include pyridinium salts, ammonium salts and phosphonium salts as described in Japanese Patent Provisional Publication No. 59(1984)-74547; polyalkylene oxides as described in Japanese Patent Provisional Publication No. 59(1984)-57231. The thermal polymerization initiators employable in the light-sensitive material preferably are compounds that are decomposed under heating to generate a polymerization initiating species, particularly a radical, and those commonly employed as initiators of radical polymerization. The thermal polymerization initiators are described in "Addition Polymerization and Ring Opening Polymerization", 6-18, edited by the Editorial Committee of High Polymer Experimental Study of the High Polymer Institute, published by Kyoritsu Shuppan (1983). Examples of the thermal polymerization initiators include azo compounds, e.g., azobisisobutyronitrile, 1,1'-azobis(1-cyclohexanecarbonitrile), dimethyl 2,2'-azobisisobutyrate, 2,2'-azobis(2-methylbutyronitrile), and azobisdimethylvaleronitrile; organic peroxides, e.g., benzoyl peroxide, di-tert-butyl peroxide, dicumyl peroxide, tert-butyl hydroperoxide, and cumene hydroperoxide; inorganic peroxides, e.g., hydrogen peroxide, potassium persulfate, and ammonium persulfate; and sodium p-toluenesulfinate. The thermal polymerization initiators are preferably used in an amount of from 0.1 to 120 % by weight, and more preferably from 1 to 10 % by weight, based on amount of the polymerizable compound. In a system in which the polymerizable compound located in a portion where the latent image has not been formed is polymerized, the thermal polymerization initiators are preferably incorporated into the light-sensitive layer. The light-sensitive material employing the thermal polymerization initiators is described in Japanese Patent Provisional Publication No. 61(1986)-260241. The development stopping agents employable in the light-sensitive material are compounds that neutralize a base or react with a base to reduce the base concentration in the layer to thereby stop development, or compounds that mutually react with silver or a silver salt to suppress development. More specifically, examples of the development stopping agents include acid precursors capable of releasing acids upon heating electrophilic compounds capable of undergoing substitution reaction with a coexisting base upon heating, nitrogen-containing heterocyclic compounds, mercapto compounds, and the like. Examples of the acid precursors include oxide esters described in Japanese Patent Provisional Publication Nos. 60(1985)-108837 and 60(1985)-192939 and compounds which release acids through Lossen rearrangement described in Japanese Patent Provisional Publication No. 60(1985)-230133. Examples of the electrophilic compounds which induce substitution reaction with bases upon heating are described in Japanese Patent Provisional Publication No. 60(1985)-230134. The antismudging agents employable in the light-sensitive material preferably are particles which are solid at ambient temperatures. Examples of the antismudging agents include starch particles described in U.K. Patent No. 1,232,347; polymer particles described in U.S. Patent No. 3,625,736; microcapsule particles containing no color former described in U.K. Patent No. 1,235,991; and cellulose particles, and inorganic particles, such as particles of talc, kaolin, bentonite, agalmatolite, zinc oxide, titanium oxide or almina described in U.S. Patent No. 2,711,375. Such particles preferably have a mean size of 3 to 50 µm, more preferably 5 to 40 µm. When the microcapsule is employed in the light-sensitive material, the size of said particle is preferably larger than that of the microcapsule. Binders employable in the light-sensitive material preferably are transparent or semi-transparent hydrophilic binders. Examples of the binders include natural substances, such as gelatin, gelatin derivatives, cellulose derivatives, starch, and gum arabic; and synthetic polymeric substances, such as water-soluble polyvinyl compounds e.g., polyvinyl alcohol, polyvinylpyrrolidone, and acrylamide polymers. In addition to the synthetic polymeric substances, vinyl compounds dispersed in the form of latex, which are particularly effective to increase dimensional stability of photographic materials, can be also used. These binders can be used singly or in combination. The light-sensitive material employing a binder is described in Japanese Patent Provisional Publication No. 61(1986)-69062. Examples and usages of the other optional components which can be contained in the light-sensitive layer are also described in the above-mentioned publications and applications concerning the light-sensitive material, and in Research Disclosure Vol. 170, No. 17029, 9-15 (June 1978). Examples of auxiliary layers which are optionally arranged on the light-sensitive material include an image -receiving layer, a heating layer, an antistatic layer, an anticurl layer and a release layer. Instead of the use of the image-receiving material, the image-receiving layer can be arranged on the light-sensitive material to produce the desired image on the on the image-receiving layer of the light-sensitive material. The image-receiving layer of the light-sensitive material can be constructed in the same manner as the layer of the image-receiving layer. The details of the image-receiving layer will be described later. The light-sensitive material employing the heating layer is described in Japanese Patent Application No. 60(1985)-135568 (corresponding to European Patent Provisional Publication No. 203613A). Examples and usage of the other auxiliary layers are also described in the above-mentioned publications and applications concerning the light-sensitive material. The light-sensitive material of the invention can be prepared, for instance, by the following process. The light-sensitive material is usually prepared by dissolving, emulsifying or dispersing each of the components of the light-sensitive layer in an adequate medium to obtain coating solution, and then coating the obtained coating solution on a support. The coating solution can be prepared by mixing liquid compositions each containing a component of the light-sensitive layer. Liquid composition containing two or more components may be also used in the preparation of the coating solution. Some components of the light-sensitive layer can be directly added to the coating solution or the liquid composition. Further, a secondary composition can be prepared by emulsifying the oily (or aqueous) composition in an aqueous (or oily) medium to obtain the coating solution. The silver halide is preferably prepared in the form of a silver halide emulsion. Various processes for the preparation of the silver halide emulsion are known in the conventional technology for the preparation of photographic materials. The silver halide emulsion can be prepared by the acid process, neutral process or ammonia process. In the stage for the preparation, a soluble silver salt and a halogen salt can be reacted in accordance with the single jet process, double jet process or a combination thereof. A reverse mixing method, in which grains are formed in the presence of excess silver ions, or a controlled double jet process, in which a pAg value is maintained constant, can be also employed. In order to accelerate grain growth, the concentrations or amounts or the silver salt and halogen salt to be added or the rate of their addition can be increased as described in Japanese Patent Provisional Publication Nos. 55(1980)-142329 and 55(1980) -158124, and U.S. Patent No. 3,650,757, etc. The silver halide emulsion may be of a surface latent image type that forms a latent image predominantly on the surface of silver halide grains, or of an inner latent image type that forms a latent image predominantly in the interior of the grains. A direct reversal emulsion comprising an inner latent image type emulsion and a nucleating agent may be employed. The inner latent image type emulsion suitable for this purpose is described in U.S. Patent Nos. 2,592,250 and 3,761,276, Japanese Patent Publication No. 58(1983)-3534 and Japanese Patent Provisional Publication No. 57(1982)-136641, etc. The nucleating agent that is preferably used in combination with the inner latent image type emulsion is described in U.S. Patent Nos. 3,227,552, 4,245,037, 4,255,511, 4,266,013 and 4,276,364, and West German Patent Provisional Publication (OLS) No. 2,635,316. In the preparation of the silver halide emulsions, hydrophilic colloids are advantageously used as protective colloids. Examples of usable hydrophilic colloids include proteins, e.g., gelatin, gelatin derivatives, gelatin grafted with other polymers, albumin, and casein; cellulose derivatives, e.g., hydroxyethyl cellulose, carboxymethyl cellulose, cellulose sulfate, etc.; saccharide derivatives, e.g., sodium alginate and starch derivatives; and a wide variety of synthetic hydrophilic polymers, such as polyvinyl alcohol, polyvinyl alcohol partial acetal, poly-N-vinylpyrrolidone, polyacrylic acid, polymethacrylic acid, polyacrylamide, polyvinylimidazole, and polyvinylpyrazole, and copolymers comprising monomers constituting these homopolymers. Among them, gelatin is most preferred. Examples of employable gelatins include not only lime-processed gelatin, but also acid-processed gelatin and enzyme-processed gelatin. Hydrolysis products or enzymatic decomposition products of gelatin can also be used. In the formation of silver halide grains in the silver halide emulsion, ammonia, an organic thioether derivative as described in Japanese Patent Publication No. 47(1972)-11386 or sulfur-containing compound as described in Japanese Patent Provisional Publication No. 53(1978)-144319 can be used as a silver halide solvent. Further, in the grain formation or physical ripening, a cadmium salt, a zinc salt, a lead salt, a thallium salt, or the like can be introduced into the reaction system. Furthermore, for the purpose of improving high or low intensity reciprocity law failure, a water-soluble iridium salt, e.g., iridium (III) or (IV) chloride, or ammonium hexachloroiridate, or a water-soluble rhodium salt, e.g., rhodium chloride can be used. After the grain formation or physical ripening, soluble salts may be removed from the resulting emulsion by a known noodle washing method or a sedimentation method. The silver halide emulsion may be used in the primitive condition, but is usually subjected to chemical sensitization. Chemical sensitization can be carried out by the sulfur sensitization, reduction sensitization or noble metal sensitization, or a combination thereof that are known for emulsions for the preparation of the conventional light-sensitive materials. When the sensitizing dyes are added to the silver halide emulsion, the sensitizing dye is preferably added during the preparation of the emulsion as described in Japanese Patent Application No. 60(1986)-139746. When the organic silver salts are introduced in the light-sensitive microcapsule, the emulsion of the organic silver salts can be prepared in the same manner as in the preparation of the silver halide emulsion. In preparation of the light-sensitive material, the polymerizable compounds are used as the medium for preparation of the liquid composition containing another component of the light-sensitive layer. For example, the silver halide, including the silver halide emulsion), the reducing agent, or the color image forming substance can be dissolved, emulsified or dispersed in the polymerizable compound to prepare the light-sensitive material. Especially, the color image forming substance is preferably incorporated in the polymerizable compound. Further, the necessary components for preparation of a microcapsule, such as shell material can be incorporated into the polymerizable compound. The light-sensitive composition which is the polymerizable compound containing the silver halide can be prepared using the silver halide emulsion. The light-sensitive composition can be also prepared using silver halide powders which can be prepared by lyophilization. These light-sensitive composition can be obtained by stirring the polymerizable compound and the silver halide using a homogenizer, a blender, a mixer or other conventional stirring device. Polymers having a principal chain consisting essentially of a hydrocarbon chain substituted in part with hydrophilic groups which contain, in their terminal groups, -OH or nitrogen having a lone electron-pair are preferably introduced into the polymerizable compound prior to the preparation of the light-sensitive composition. The polymer has a function of dispersing silver halide or other component in the polymerizable compound very uniformly as well as a function of keeping thus dispered state. Further, the polymer has another function of gathering silver halide along the interface between the polymerizable compound (i.e., light-sensitive composition) and the aqueous medium in preparation of the microcapsule. Therefore, using this polymer, silver halide can be easily introduced into the shell material of the microcapsule. The polymerizable compound (including the light-sensitive composition) are preferably emulsified in an aqueous medium to prepare the coating solution. The necessary components for preparation of the microcapsule, such as shell material can be incorporated into the emulsion. Further, other components such as the reducing agent can be added to the emulsion. The emulsion of the polymerizable compound can be processed for forming shell of the microcapsule. Examples of the process for the preparation of the microcapsules include a process utilizing coacervation of hydrophilic wall-forming materials as described in U.S. Patent Nos. 2,800,457 and 2,800,458; an interfacial polymerization process as described in U.S. Patent No. 3,287,154, U.K. Patent No. 990,443 and Japanese Patent Publication Nos. 38(1963)-19574, 42(1967)-446 and 42(1967)-771; a process utilizing precipitation of polymers as described in U.S. Patent Nos. 3,418,250 and 3,660,304; a process of using isocyanate-polyol wall materials as described in U.S. Patent No. 3,796,669; a process of using isocyanate wall materials as described in U.S. Patent No. 3,914,511; a process of using urea-formaldehyde or urea-formaldehyde-resorcinol wall-forming materials as described in U.S. Patent Nos. 4,001,140, 4,087,376 and 4,089,802; a process of using melamine-formaldehyde resins hydroxypropyl cellulose or like wall-forming materials as described in U.S. Patent No. 4,025,455; an in situ process utilizing polymerization of monomers as described in U.K. Patent No. 867,797 and U.S. Patent No. 4,001,140; an electrolytic dispersion and cooling process as described in U.K. Patent Nos. 952,807 and 965,074; a spray-drying process as described in U.S. Patent No. 3,111,407 and U.K. Patent 930,422; and the like. It is preferable, though not limitative, that the microcapsule is prepared by emulsifying core materials containing the polymerizable compound and forming a polymeric membrane (i.e., shell) over the core materials. The dispersion of the grains of the hydrophobic organic base compound can be added to the obtained dispersion of the microcapsule to preapre the coating solution of the light-sensitive material. The dispersion of the grains of the hydrophobic organic base compound can be prepared by a known dipsersing device. A water-soluble polymer can be previously added to the dispersion of the grains. A light-sensitive material of the invention can be prepared by coating and drying the above-prepared coating solution on a support in the conventional manner. Use of the light-sensitive material is described below. In the use of the light-sensitive material of the invention, a development process is conducted simultaneously with or after an imagewise exposure. Various exposure means can be employed in the imagewise exposure, and in general, the latent image on the silver halide is obtained by imagewise exposure to radiation including visible light. The type of light source and exposure can be selected depending on the light-sensitive wavelengths determined by spectral sensitization or sensitivity of silver halide. Original image can be either monochromatic image or color image. Development of the light-sensitive material can be conducted simultaneously with or after the imagewise exposure. The development can be conducted using a developing solution in the same manner as the image forming method described in Japanese Patent Publication No. 45(1970)-11149. The image forming method described in Japanese Patent Provisional Publication No. 61(1986)-69062 which employs a heat development process has an advantage of simple procedures and short processing time because of the dry process. Thus, the latter method is preferred as the development process of the light-sensitive material. Heating in the heat development process can be conducted in various known manners. The heating layer which is arranged on the light-sensitive material can be used as the heating means. Heating temperatures for the development process usually ranges from 80°C to 200°C, and preferably from 100°C to 160°C. Various heating patterns are applicable. The heating time is usually from 1 second to 5 minutes, and preferably from 5 seconds to 1 minute. During the above development process, a polymerizable compound in a portion where a latent image of the silver halide has been formed or in a portion where a latent image of the silver halide has not been formed is polymerized. In a general system, the polymerizable compound in a portion where the latent image has been formed is polymerized. If a nature or amount of the reducing agent is controlled, the polymerizable compound in a portion where the latent image has not been formed can be polymerized in the same manner as the light-sensitive material described in Japanese Patent Provisional Publication No. 61(1986)-260241. In the above development process, a polymer image can be formed on the light-sensitive layer. A pigment image can be also obtained by fixing pigments to the polymer image. The image can be also formed on the image-receiving material. The image-receiving material is described hereinbelow. The image forming method employing the image-receiving material or the image-receiving layer is described in Japanese Patent Provisional Publication No. 61(1986)-278849. Examples of the material employable as the support of the image-receiving material include baryta paper in addition to various examples which can be employed as the support of the known light-sensitive material. The image-receiving material is usually prepared by providing the image-receiving layer on the support. The image-receiving layer can be constructed according to the color formation system. In the cases that a polymer image is formed on the image-receiving material and that a dye or pigment is employed as the color image forming substance, the image-receiving material be composed of a simple support. For example, when a color formation system using a color former and developer is employed, the developer can be contained in the image-receiving layer. Further, the image-receiving layer can be composed of at least one layer containing a mordant. The mordant can be selected from the compounds known in the art of the conventional photography according to the kind of the color image forming substance. If desired, the image-receiving layer can be composed of two or more layers containing two or more mordants different in the mordanting power from each other. The image-receiving layer preferably contains a polymer as binder. The binder which may be employed in the above-mentioned light-receiving layer is also employable in the image-receiving layer. The image-receiving layer can be composed of two or more layers according to the above-mentioned functions. The thickness of the image-receiving layer preferably ranges from 1 to 100 µm, more preferably from 1 to 20 µm. After the development process, pressing the light-sensitive material in contact with the image-receiving material to transfer the polymerizable compounds which is still polymerizable to the image-receiving material, a polymer image can be obtained in the image-receiving material. The process for pressing can be carried out in various known manners. In the case that the light-sensitive layer contains a color image forming substance, the color image forming substance is fixed by polymerization of the polymerizable compound. Then, pressing the light-sensitive material in contact with the image-receiving material to transfer the color image forming substance in unfixed portion, a color image can be produced on the image-receiving material. The light-sensitive material can be used for monochromatic or color photography, printing, radiography, diagnosis (e.g., photography for CRT of diagnostic device using supersonic wave), copy (e.g., computer-graphic hard copy), etc. The present invention is further described by the following examples without limiting the invention. EXAMPLE 1 Preparation of silver halide emulsion In 3 ℓ of water were dissolved 40 g of gelatin and 23.8 g of potassium bromide, and the resulting gelatin solution was kept at 50°C. To the gelatin solution, 200 mi of an aqueous solution containing 34 g of silver nitrate was added over a period of 10 minutes while stirring. To the solution, 100 mℓ of an aqueous solution containing 3.3 g of potassium iodide was added over a period of 2 minutes to obtain a silver bromoiodide emulsion. After the emulsion was adjusted to a pH for sedimentation, excess salts were removed, and the emulsion was adjusted to a pH of 6.0. The yield of the emulsion was 400 g. Preparation of silver benzotriazole emulsion In 3,000 mℓ of water were dissolved 28 g of gelatin and 13.2 g of benzotriazole, and the solution was kept at 40°C while stirring. To the solution was added 100 mℓ of an aqueous solution of 17 g of silver nitrate over 2 minutes. Excessive salts were sedimented and removed from the resulting emulsion by pH-adjustment. Thereafter, the emulsion was adjusted to pH 6.30 to obtain a silver benzotriazole emulsion. The yield of the emulsion was 400 g. Preparation of light-sensitive composition In 100 g of trimethylolpropane triacrylate were dissolved 0.40 g of the following copolymer and 6.00 g of Pargascript Red I-6-B (tradename, Ciba-Geigy). To 10.8 g of the resulting solution were added 0.22 g of Emulex NP-8 (tradename, produced by Nippon Emulsion Co., Ltd.) and a solution in which 0.65 g of the following reducing agent (I) and 0.73 g of the following reducing agent (II) were dissolved in 2.4 g of methylene chloride. To the solution was further added a mixture of 2.4 g of the silver halide emulsion, 2 g of the silver benzotriazole emulsion and 0.066 g of benzotriazole, and the resulting mixture was stirred at 15,000 r.p.m. for 5 minutes to obtain a light-sensitive composition. Preparation of light-sensitive microcapsule To the light-sensitive composition was dissolved 10 g of an adduct of xylylene diisocyanate and trimethylolpropane (tradename "Takenate D110N", produced by Takeda Chemical Industries, Ltd.). The resulting solution was added to 50 g of 4 % aqueous solution of methyl cellulose (tradename; Metholose, produced by Shinetsu Chemical Industry Co., Ltd.), and the mixture was stirred at 5,000 r.p.m. for 1 minutes to obtain an emulsion. The emulsion was reacted for 2 hours at 60°C while stirring at 1,000 r.p.m. to obtain a dispersion containing light-sensitive microcapsules in which the light-sensitive composition is contained in the microcapsule having a shell material made of polyurea resin. Preparation of dispersion of solid grains of hydrophobic organic base precursor To 10 parts by weight of 10 % aqueous solution of polyvinyl alcohol (tradename PVA-205, produced by Kuraray Co., Ltd.) was added 1.5 part by weight of tricyclohexylguanidine trichloroacetate, and the mixture was coarsely dispersed. The coarse dispersion was then finely dispersed for four times (passing for four times) in horizontal Dynomile to obtain the dispersion of the grains of tricyclohexylguanidine trichloroacetate. Preparation of light-sensitive material To 10.0 g of the light-sensitive microcapsule dispersion were added 1.0 g of 10 % aqueous solution of Emulex NP-8 (tradename, produced by Nippon Emulsion Co., Ltd.) and 2 g of the dispersion of the grains of tricyclohexylguanidine trichloroacetate to prepare a coating solution for the light-sensitive layer. The coating solution was uniformly coated on a polyethylene terephthalate film (thickness: 100 µm) using a coating rod of # 40 to a wet thickness of 70 µm and dried at about 40°C to obtain a light-sensitive material. EXAMPLE 2 Preparation of dispersion of solid grains of hydrophobic organic base precursor To 10 parts by weight of 10 % aqueous solution of polyvinyl alcohol (tradename PVA-205, produced by Kuraray Co., Ltd.) were added 1.5 part by weight of tricyclohexylguanidine trichloroacetate and 6.0 part by weight of p-benzyloxyphenol (hot-melt solvent), and the mixture was coarsely dispersed. The coarse dispersion was then finely dispersed for four times (passing for four times) in horizontal Dynomile to obtain the dispersion of the grains of tricyclohexylguanidine trichloroacetate and p-benzyloxyphenol. Preparation of light-sensitive material A light-sensitive material was prepared in the same manner as in Example 1 except that the above the dispersion of the grains of tricyclohexylguanidine trichloroacetate and p-benzyloxyphenol was used in place of the dispersion of the grains of tricyclohexylguanidine trichloroacetate. EXAMPLE 3 Preparation of silver halide emulsion In 1,000 mℓ of water were dissolved 20 g of gelatin and 3 g of sodium chloride, and the resulting gelatin solution was kept at 75°C. To the gelatin solution, 600 mℓ of an aqueous solution containing 21 g of sodium chloride and 56 g of potassium bromide and 600 mℓ of an aqueous solution containing 0.59 mole of silver nitrate were added simultaneously at the same feed rate over a period of 40 minutes to obtain a silver chlorobromide emulsion having cubic grains, uniform grain size distribution, a mean grain size of 0.35 µm and a bromide content of 80 mole %. The emulsion was washed for desalting and then subjected to chemical sensitization with 5 mg of sodium thiosulfate and 20 mg of 4-hydroxy-6-methyl-1,3,3a,7-tetraazaindene at 60°C to obtain the silver halide emulsion. The yield of the emulsion was 600 g. Preparation of silver benzotriazole emulsion In 3,000 mℓ of water were dissolved 28 g of gelatin and 13.2 g of benzotriazole, and the solution was kept at 40°C while stirring. To the solution was added 100 mℓ of an aqueous solution of 17 g of silver nitrate over 2 min. An excessive salt was sedimented by pH-adjustment and removed from the resulting emulsion. Thereafter, the emulsion was adjusted to pH 6.30 to obtain a silver benzotriazole emulsion. The yield of the emulsion was 400 g. Preparation of light-sensitive composition In 100 g of trimethylolpropane triacrylate were dissolved 0.40 g of the following copolymer, 6.00 g of Pargascript Red I-6-B (tradename, Ciba-Geigy) and 2 g of Emulex NP-8 (tradename, preduced by Nippon Emulsion Co., Ltd.). In 18.00 g of the resulting solution was dissolved 0.002 g of the following thiol derivative. To the solution was added a solution in which 0.16 g of the following reducing agent (III) and 1.22 g of the following reducing agent (II) were dissolved in 1.80 g of methylene chloride. Further, to the resulting solution were added 3.50 of the silver halide emulsion and 3.35 g of the silver benzotriazole emulsion, and the mixture was stirred at 15,000 r.p.m. for 5 min. using a homogenizer to obtain a light-sensitive composition. Preparation of light-sensitive microcapsule To 10.51 g of 18.6 % aqueous solution of Isobam (tradename, produced by Kuraray Co., Ltd.) was added 48.56 g of 2.89 % aqueous solution of pectin. After the solution was adjusted to pH 4.0 using 10 % solution of sulfuric acid, the light-sensitive composition was added to the resulting solution, and the mixture was stirred at 7,000 r.p.m. for 2 min. using a homogenizer to emulsify the light-sensitive composition in the aqueous medium. To 72.5 g of the aqueous emulsion were added 8.32 g of 40 % aqueous solution of urea, 2.82 g of 11.3 % aqueous solution of resorcinol, 8.56 g of 37 % aqueous solution of formaldehyde, and 3.00 g of 8.00 % aqueous solution of ammonium sulfate in this order, and the mixture was heated at 60°C for 2 hours while stirring. After the mixture was adjusted to a pH of 7.3 using 10 % aqueous solution of sodium hydroxide, 3.62 g of 30.9 % aqueous solution of sodium hydrogen sulfite was added to the mixture to obtain a dispersion containing light-sensitive microcapsules. Preparation of dispersion of solid grains of hydrophobic organic base compound To 10 parts by weight of 10 % aqueous solution of polyvinyl alcohol (tradename PVA-205, produced by Kuraray Co., Ltd.) was added 1.5 part by weight of tricyclohexylguanidine, and the mixture was coarsely dispersed. The coarse dispersion was then finely dispersed for four times (passing for four times) in horizontal Dynomile to obtain the dispersion of the grains of tricyclohexylguanidine. Preparation of light-sensitive material To 10.0 g of the light-sensitive microcapsule dispersion were added 1.0 g of 10 % aqueous solution of Emulex NP-8 (tradename, produced by Nippon Emulsion Co., Ltd.) and 11.5 g of the dispersion of the grains of tricyclohexylguanidine to prepare a coating solution for the light-sensitive layer. The coating solution was uniformly coated on a polyethyleneterephthalate film (thickness: 100 µm) using a coating rod of # 40 to a wet thickness of 70 µm and dried at about 40°C to obtain a light-sensitive material. Evaluation of light-sensitive material Each of the light-sensitive materials prepared in Examples 1, 2 and 3 was imagewise exposed to light using a tungsten lamp at 2,000 lux for 1 second and then heated on a hot plate at 125°C for 60 seconds. As a result, a silver image having high contrast was formed on each of the exposed and heated light-sensitive material.

Claims: In a light-sensitive material comprising a light-sensitive layer which contains silver halide, a reducing agent and a polymerizable compound provided on a support, characterized in that the silver halide and the polymerizable compound are contained in microcapsules which are dispersed in the light-sensitive layer, and the light-sensitive layer further contains dispersed grains of a hydrophobic organic base compound and/or base precursor having a melting point of from 80 to 180°C which are arranged outside of the microcapsules. The light-sensitive material as claimed in claim 1, wherein the silver halide, the polymerizable compound and the reducing agent are contained in microcapsules in the light-sensitive layer. The light-sensitive material as claimed in claim 1, wherein the grains of a hydrophobic organic base compound and/or base precursor is contained in the light-sensitive layer in the form of the despersion of the grains in a water-solble polymer. The light-sensitive material as claimed in claim 1, wherein the hydrophobic organic base compound and/or base precursor is a guanidine derivative. The light-sensitive material as claimed in claim 1, wherein the hydrophobic organic base compound is a guanidine derivative having a pKa value of not lower than 8. The light-sensitive material as claimed in claim 1, wherein the hydrophobic organic base compound is contained in an amount of from 0.01 to 50 weight % based on the total solid content of the light sensitive layer. The light-sensitive material as claimed in claim 1, wherein the light-sensitive layer further contains a color image forming substance. The light-sensitive material as claimed in claim 1, wherein the light-sensitive layer further contains a hot-melt solvent.

Inventors: KAKIMI, FUJIO FUJI PHOTO FILM CO., LTD.
Applicants: FUJI PHOTO FILM CO., LTD.
Application year: 1987
Main classification: G03F7
IPC codes: G03F7, G03C1