A METHOD OF PRODUCING A SEMICONDUCTOR DEVICE SHOWING A GOOD OHMIC CONTACT BETWEEN A PLURALITY OF WIRING LAYERS

Abstract: A method for fabricating a semiconductor device, to establish electrical contact between two wiring layers (3, 8) comprises forming a contact hole (5) in an insulating film (4) formed on a first wiring (3) composed of an Al film, covering the surface of the insulating film (4) and the surface of wiring (3) exposed by the contact hole (5) with a second Al film wiring and patterning the Al film to form the second wiring (8). A pulsed laser beam is applied from above to the second Al film (8) and this causes local melting so that it fills the contact hole (5) and displaces any oxide or adsorbed material formed on the upper surface of wiring (3) to provide a good ohmic contact between the first and second wiring (3 and 8).

Description: The present invention relates to a method of fabricating a semiconductor device. More particularly, the present invention relates to a method of establishing a good ohmic contact between a plurality of wiring layers composed of an Al film. "Al film" as used herein refers to a film of aluminium or an aluminium alloy mainly composed of aluminium. Conventionally a method of fabricating a semiconductor device to establish electrical contact between two wiring layers formed of aluminium or an aluminium alloy comprises forming a contact hole in an insulating film formed on a first wiring, covering the surface of the insulating film and the surface of the wiring exposed by the contact hole with a second wiring layer, and patterning the second wiring layer to form second wiring. However, upon exposure to air or an adsorbing material a layer of oxide or adsorbent is formed on the surface of the first wiring exposed by the contact hole. This forms an obstacle to the formation of a good ohmic contact between the two wiring layers. Previous attempts to remove this film have used ion bombardment by an Ar plasma as will be described in detail subsequently but these have not been completely satisfactory. In "Laser Planarization", Solid State Technology, April 1986, pages 129-134, it is disclosed that a non-oxidising metal conductor film, such as of gold, is planarized by irradiation with a dye laser beam. For solving the problem of removal of an oxide or absorded film formed between two wiring layers of Al, sputter-etching of the native oxide or the absorded film prior to planarization is recommended instead. The article "Techniques for Improving Engineering Productivity of VLSI Designs," IBM Journal of Research and Development, vol. 25, May 1981, pages 107-115, discloses connection of two Al layers separated by an insulating layer with the aid of a pulsed dye laser. According to this invention such a fabrication method also includes a step in which laser beam pulses having an energy intensity between 5 and 12 J/cm² and a duration of less than 100 ns are applied to the second Al film wiring layer from above to remove an oxide or an adsorbed material formed on the first wiring and instantaneously to melt the second wiring so that it partially flows into the contact hole. The present invention solves the problem of the conventional technique, and provides a method for fabricating a semiconductor device, in which a good ohmic contact can be obtained in a plurality of wiring layers without damaging an element. A particular embodiment of a method in accordance with this invention will now be described and contrasted with the prior art with reference to the accompanying drawings, in which:- Figure 1 is a sectional view illustrating a method for fabricating a semiconductor device according to one embodiment of the present invention; Figure 2 is a sectional view illustrating the conventional method for fabricating a semiconductor device; and, Figure 3 is a diagram showing experimental data, which illustrates effects attained in the embodiment of the present invention. Figures 2a through 2C are sectional views illustrating the conventional method for fabricating a semiconductor device. As shown in Figure 2a an SiO₂ film 2 and an Al film 3 for a first wiring are formed on an Si substrate 1, and an SiO₂ film is formed as an interlaminar insulating film. A contact hole 5 is also formed. By formation of the contact hole 5, the Al film 3 is exposed and an oxide formed by reaction with O₂ in air or an adsorbed material 6 is deposited on the exposed surface of the Al film 3. The presence of the oxide or adsorbed material 6 is an obstacle to formation of a good ohmic contact. Therefore, according to the conventional technique, as shown in Figure 2b, the oxide or adsorbed material is removed by irradiation with Ar plasma before formation of an upper Al film. Namely, as shown in Figure 2c, an Al film 7 is formed by the sputtering method and a good ohmic contact is obtained between the Al film 3 and the Al film 7. As pointed out above, according to the conventional method, the oxide or adsorbed material 6 on the Al film 3 is removed by irradiation with Ar plasma before formation of the Al film 7. However, according to the conventional method since irradiation with an ion or radical is carried out, the surface of the Al film 3 is roughened and the SiO₂ film 4 is seriously damaged, resulting in formation of a defective element. Especially, in a high-density MOSLSI, since a gate SiO₂ film is broken by the discharge of the electrical charge accumulated, a short circuit is readily formed. Further, where the contact hole 5 has a very small diameter or a very large depth, it is difficult to satisfactorily remove the oxide or adsorbed material 6 due to the insufficient irradiation of the Ar plasma, or to obtain a good contact between the Al films 3 and 7 due to the insufficient penetration of Al into the hole. Therefore, the development of a means for overcoming these disadvantages is eagerly desired. The method for fabricating a semiconductor device according to the present invention is characterized by the steps of forming a contact hole in an insulating film formed on a first wiring composed of an Al film, covering the insulating film with an Al film for a second wiring, applying laser beam pulses to the Al film for a second wiring from above, and patterning the Al film to form a second wiring. According to the present invention, after formation of the Al film for a second wiring, laser beam pulses are applied to the Al film from above, whereby the oxide or adsorbed material formed on the Al film for a first wiring is removed and a good ohmic contact is obtained between the Al film for a first wiring and the Al film for a second wiring. By irradiation with these pulses, the upper Al film is appropriately instantaneously melted and flows into the contact hole, and therefore, a good coverage with the Al film can be attained at the step portion and disconnection can be prevented. An embodiment of the present invention will now be described with reference to the accompanying drawings. Figures 1a through 1c are diagrams illustrating a method for fabricating a semiconductor device according to the embodiment of the present invention. Note, the same reference numerals as in Figure 2 represent the same members. (1) Referring to Fig. 1a, an SiO₂ film formed on an Si substrate 1. Reference numeral 3 represents an Al film as a first wiring, reference numeral 4 represents an SiO₂ film formed as an interlaminar insulating film on the Al film 3, and reference numeral 5 represents a contact hole. (2) Then, as shown in Fig. 1b, an Al film 8 is covered on the entire surface by, for example, the sputtering method. Since an oxide or adsorbed material 6 is formed on the surface of the Al film 3 exposed by formation of the contact hole, the contact between the Al films 8 and 3 is not always good. Furthermore, the coverage with the Al film 8 at the step portion of the insulating film 4 in the contact hole is not sufficient. (3) Then, as shown in Fig. 1c, excimer laser beam pulses are applied to the Al film 8 from above. For example, ArF excimer laser beam (wavelength = 193 nm) is used as the excimer laser beam, and the irradiation is carried out under conditions of an energy intensity of 10 J/cm² and a pulse width of 15 ns. If the energy intensity is lower than 3 J/cm², a substantial effect is not attained. In contrast, if the energy intensity is higher than 15 J/cm², the Al film is damaged. Accord­ ingly, preferably the energy intensity is 5 to 12 J/cm². Furthermore, if the pulse width is increased (for example, to 1 µs) or continuous waves are applied, the Al film 8 is damaged and good results can not be obtained. Note, the KrF₂ excimer laser beam (wavelength = 248 nm), XeCl excimer laser beam (wavelength = 308 nm) and TEA-CO₂ laser beam (wavelength = 106 nm) can be also used as the laser beam. These laser beams may preferably have a pulse width of not larger than 100 ns. By this irradiation with laser beam, a good ohmic contact can be obtained between the Al film 3 and Al film 8. This is illustrated in Fig. 3, which is a diagram showing experimental data. From Fig. 3, it is seen that, by irradiation with laser beam, a good ohmic contact is obtained between the upper Al film and the lower Al film. Moreover, since by irradiation with laser beam pulses, the Al film 8 is appropriately melted without being damaged and the melt flows into the contact hole 5, the coverage with the Al film 8 at the step portion of the insulating film 4 is greatly improved. As is apparent from the foregoing illustration, by irradiation with laser beam pulses, a good ohmic contact can be obtained in a plurality of wiring layers composed of an Al film without damaging the Al film. Accordingly, a semiconductor device having a high quality and a high integration degree can be provided. Moreover, since the Al film is appropriately melted by irradiation with laser beam and the melt flows into the contact hole, the coverage with the Al film at the step portion can be improved and disconnection can be prevented.

Claims: 1. A method of fabricating a semiconductor device to establish electrical contact between two wiring layers (3, 8) formed of aluminium or an aluminium alloy comprises forming a contact hole (5) in an insulating film (4) formed on a first wiring (3), covering the surface of the insulating film (4) and the surface of the wiring (3) exposed by the contact hole (5) with a second wiring layer (8), and patterning the second wiring layer to form a second wirin, characterised in that laser beam pulses having an energy intensity between 5 and 12 J/cm² and a duration of less than 100 ns are applied to the second wiring layer (8) from above to remove an oxide or an adsorbed material (6) formed on the first wiring (3) and instantaneously to melt the second wiring (8) that it partially flows into the contact hole (5). 2. A method according to claim 1, wherein the pulsed laser beam is selected from ArF excimer laser beam, KrF₂ excimer laser beam, XeCl excimer laser beam and TEA-CO₂ laser beam. 3. A method according to claim 1 or 2, wherein the duration of the laser pulses is substantially 15 ns.

Inventors: MUKAI, RYOICHI
Applicants: FUJITSU LIMITED
Application year: 1987
Main classification: H01L21
IPC codes: H01L23, H01L21