PROCESS FOR THE PREPARATION OF POLYMERS

Abstract: Process for the preparation of polymers characterized in that a mixture of carbon monoxide and ethene is polymerized at an overall pressure of between 75 and 250 bar and an ethene/carbon monoxide partial pressure ratio of between 0.75 and 3 by using a catalyst composition based upon a) a palladium compound, b) an anion of an acid with a pKa of less than 2, provided that the acid is not a hydrohalogenic acid, and c) a bidentate ligand of the general formula R¹R²-M-R-M-R³R⁴, wherein M represents phosphorus, arsenic or antimony, R¹, R², R³ and R⁴ represent hydrocarbyl groups which may or may not be substituted with polar groups and R represents a bivalent organic bridging group which contains at least two carbon atoms in the bridge.

Description: The invention relates to a process for the preparation of polymers of carbon monoxide and ethene. It is known from EP-A-121965 that high molecular weight linear polymers of carbon monoxide and ethene in which the monomer units occur in an alternating order and therefore consist of units of the formula -CO-(C₂H₄)-, can be prepared by copolymerizing a mixture of carbon monoxide and ethene at a temperature of between 20 and 200 °C and at elevated pressure, by using a catalyst composition based upon a) a palladium salt of a carboxylic acid , b) an anion of an acid with a pKa of less than 2, provided that the acid is not a hydrohalogenic acid, and c) a bidentate ligand of the general formula R¹R²-M-R-M-R³R⁴ wherein M represents phosphorus, arsenic or antimony, R¹, R², R³ and R⁴ represent hydrocarbyl groups which may or may not be substituted with polar groups and R represents a bivalent organic bridging group which contains at least two carbon atoms in the bridge. In the above-mentioned polymer preparation both reaction rates and molecular weights of the polymers obtained play a major role. On the one hand the highest possible reaction rate should be aimed at in the polymer preparation, while on the other hand the polymers are more valuable with a view to their uses according as they have higher molecular weights. Both reaction rates and molecular weights can be influenced by the temperatures and overall pressures applied during the polymerization. Higher reaction rates and lower molecular weights will be obtained according as higher reaction temperatures are chosen. Higher reaction rates and higher molecular weights will be obtained according as higher overall pressures are chosen. The effect which a rise in reaction temperature and overall pressure has on reaction rates is greatest at reaction temperatures below 85 °C and overall pressures below 75 bar. Above these values increased reaction temperatures and overall pressures will still lead to higher reaction rates but the increase will become increasingly smaller. In view of the above, the polymers used to be hitherto prepared mainly at a reaction temperature in the range of from 60 to 70 °C and at an overall pressure in the range of from 50 to 60 bar. A correct choice of reaction temperatures and overall pressures within the said ranges allowed polymers of sufficiently high molecular weights for the relevant application to be produced at acceptable reaction rates. Attempts to achieve an increase in reaction rate by varying the ratio between the ethene partial pressure and the carbon monoxide partial pressure remained unsuccessful. It was found that at overall pressures below 75 bar variations in the ratios between ethene partial pressure and carbon monoxide partial pressure ranging from 0.3 to 3 did not lead to any significant change in the reaction rate. Neither were variations of the partial pressure ratios within the same range seen to have any significant influence on the molecular weights of the polymers obtained. The Applicant has carried out an investigation into the execution of the polymerization at overall pressures between 75 and 250 bar while using ethene/carbon monoxide partial pressure ratios between 0.3 and 3. As could be expected from the results of low pressure polymerization found earlier, variation of the ethene/carbon monoxide partial pressure ratio within a given high overall pressure proved to produce no significant change in the reaction rate. Surprisingly and in sharp contrast with the expectations based on earlier results of low pressure polymerization it has now been found that variation of the ethene/carbon monoxide partial pressure ratio at a given high overall pressure has a substantial effect on the molecular weights of the polymers obtained, in that polymers of considerably higher molecular weights are obtained when the polymerization is carried out at an ethene/carbon monoxide partial pressure ratio between 0.75 and 3 as opposed to polymers prepared at the same temperature and overall pressure but at an ethene/carbon monoxide partial pressure ratio between 0.3 and 0.75. The present find is of interest not only for the preparation of polymers with higher molecular weights but also for the execution of the polymerization at increased reaction rates. For it is possible by increasing the ethene/carbon monoxide partial pressure ratio and simultaneously raising the reaction temperature to realise considerably higher reaction rates while the molecular weights of the polymers remain unchanged. The present patent application therefore relates to a process for the preparation of polymers comprising copolymerizing a mixture of carbon monoxide and ethene at a temperature of between 20 and 200 °C and at elevated pressure, by using a catalyst composition based upon a) a palladium salt of a carboxylic acid, b) an anion of an acid with a pKa of less than 2, provided that the acid is not a hydrohalogenic acid, and c) a bidentate ligand of the general formula R¹R²M-R-MR³R⁴, wherein M represents phosphorus, arsenic or antimony, R¹, R², R³ and R⁴ represent hydrocarbyl groups which may or may not be substituted with polar groups and R represents a bivalent organic bridging group which contains at least two carbon atoms in the bridge, characterized in that the copolymerization is carried out at an overall pressure of between 75 and 250 bar and an ethene/carbon monoxide partial pressure ratio of between 0.75 and 3. The patent application further relates to the polymers thus prepared. The process according to the invention is preferably carried out at an overall pressure between 80 and 200 bar and in particular between 85 and 175 bar. As regards the ethene/carbon monoxide partial pressure ratio used, preference is given to a ratio lying between 0.80 and 2.5 and in particular between 0.85 and 2. The polymerization is preferably carried out at a temperature between 20 and 200 °C and in particular between 30 and 150 °C. Furthermore, the polymerization is preferably carried out in a liquid diluent. Very suitable liquid diluents are lower alcohols such as methanol and ethanol. The quantity of catalyst composition used in the process according to the invention may vary within wide ranges. Per mol of ethene to be polymerized such a quantity of catalyst composition is preferably used as to contain 10⁻⁷-10⁻³ and in particular 10⁻⁶-10⁻⁴ gram atom of palladium. Preferably the palladium compound applied as component a) is a palladium salt of a carboxylic acid and in particular palladium acetate. Examples of suitable acids with a pKa lower than 2 (determined in aqueous solution at 18 °C) are sulphuric acid, perchloric acid, sulphonic acids, such as methanesulphonic acid, trifluoromethanesulphonic acid and para-toluenesulphonic acid and carboxylic acids such as trichloroacetic acid, difluoroacetic acid and trifluoroacetic acid. Preference is given to para-toluenesulphonic acid and trifluoroacetic acid. In the catalyst compositions component b) is preferably present in a quantity of from 0.5 to 200 and in particular of from 1.0 to 100, equivalents per gram atom of palladium. Component b) may be introduced into the catalyst compositions either in the form of an acid or as a salt. Eligible salts are salts of non-noble transition metals and salts of main group metals. Examples of transition metals whose salts are very suitable for use as component b) are the Group 4B metal zirconium, the Group 5B metal vanadium, the Group 6B metal chromium, the Group 8 metals iron and nickel, the Group 1B metal copper, the lanthanide cerium and the actinides thorium and uranium. If in the catalyst compositions component b) is used in the form of an acid or in the form of a salt of a non-noble transition metal, it is preferred also to include a quinone as component d) in the catalyst compositions in order to enhance the activity of the latter. 1,4-Benzoquinones have proved very useful for this purpose. Examples of main group metals the salts of which can very suitably be used as component b) are the Group 3A metals aluminium and gallium, the Group 4A metals tin and lead and the Group 5A metal antimony. Salts of Group 1A metals such as lithium, potassium and sodium and salts of Group 2A metals such as magnesium are also eligible for the purpose, provided that the catalyst compositions also contain an ether as component d). It is preferred when a salt of a metal belonging to the main groups 3A-5A is used as component b), that in addition an ether is included in the catalyst compositions as component d) in order to enhance their activity. Crown ethers have proved to be very suitable ethers. Optionally the two components a) and b) can be combined and used in the form of a single compound. An example of such a compound is the complex Pd(CH₃CN)₂(O₃S-C₆H₄-CH₃)₂ which can be prepared by reacting a palladium chloride with the silver salt of para-toluenesulphonic acid in acetonitrile as the solvent. In the bidentate ligand M is preferably phosphorus. The groups R¹, R², R³ and R⁴ present in the bidentate ligand preferably contain 6-14 carbon atoms. Special preference is given to bidentate ligands in which the groups R¹, R², R³ and R⁴ are phenyl groups or substituted phenyl groups. The bivalent organic bridging group R preferably contains three carbon atoms in the bridge. Examples of suitable bidentate ligands are 1,3-bis(di-p-tolylphosphino)propane, 1,3-bis(diphenylphosphino)propane, and 2-methyl-2-(diphenylphosphinomethyl)-1,3-bis(diphenylphosphino)-propane. Preferably one of the latter two bidentate ligands is used. The bidentate ligand is preferably applied in a quantity of 0.1-5 and in particular 0.5-1.5 mol per mol of palladium compound. The carbon monoxide used in the preparation of the polymers need not be pure. It may contain such contaminations as hydrogen, carbon dioxide and nitrogen. The higher the molecular weight of the polymers according to the invention, the higher will be in general the intrinsic viscosity they exhibit. For the determination of the intrinsic viscosity of a polymer according to the invention, four solutions are first of all prepared by dissolving the polymer in four different concentrations at 100 °C in m-cresol. For each of these solutions, the viscosity is measured in a viscometer at 100 °C relative to m-cresol at 100 °C. If T o represents the outflow time of m-cresol and T p the outflow time of the polymer solution, the relative viscosity (η rel ) is obtained from η rel =T p T o . From η rel can be calculated the inherent viscosity (η inh ) according to the formula: where c represents the concentration of the polymer in grams per 100 ml solution. By plotting graphically the η inh found for each of the four polymer solutions against the corresponding concentration (c) and then by extrapolating to c=0, the intrinsic viscosity [η] in dl/g is found. Instead of "intrinsic viscosity", this patent application will henceforth use the term recommended by the International Union of Pure and Applied Chemistry, viz. "Limiting Viscosity Number" (LVN). The polymers according to the invention generally have an LVN of between 0.2 and 5.0 dl/g. Preferred polymers have an LVN of between 0.3 and 4.5 dl/g and in particular an LVN of between 0.4 and 4.0 dl/g. The invention will now be illustrated with the aid of the following examples. EXAMPLE 1 A carbon monoxide/ethene copolymer was prepared as follows. 200 ml of methanol was introduced into a mechanically stirred autoclave with a volume of 300 ml. After the contents of the autoclave had been brought to a temperature of 65 °C, ethene and CO were introduced in amounts equivalent to 18 bar and 36 bar, respectively. A catalyst solution was then introduced into the autoclave, consisting of: 18 ml of methanol, 0.03 mmol of palladium acetate, 0.03 mmol of 2-methyl-2-(diphenylphosphinomethyl)-1,3-bis(diphenylphosphino)propane, and 0.06 mmol of p-toluenesulphonic acid. The pressure was maintained at 55 bar by introduction under pressure of a 1:1 carbon monoxide/ethene mixture. After one hour the polymerization was terminated by releasing the pressure. The polymer was filtered off, washed with methanol and dried at 70 °C. The product was 9.6 g of copolymer, so the polymerization rate was 3200 g of copolymer/g of palladium/hour. The copolymer had an LVN of 1.1 dl/g. EXAMPLE 2 A carbon monoxide/ethene copolymer was prepared substantially in the same way as the copolymer of Example 1, except that in this case ethene and CO were introduced into the autoclave both in amounts equivalent to 27 bar. The product was 10.5 g of copolymer, so the polymerization rate was 3500 g of copolymer/g of palladium/hour. The copolymer had an LVN of 1.3 dl/g. EXAMPLE 3 A carbon monoxide/ethene copolymer was prepared substantially in the same way as the copolymer of Example 1, except for the following differences a) ethene and CO were introduced into the autoclave in amounts equivalent to 5 bar and 10 bar, respectively, b) the quantity of catalysts was 10/3 of the quantity used in Example 1, c) the pressure was maintained at 16 bar by introduction of a 1:1 carbon monoxide/ethene mixture, and d) the polymerization was terminated after 19 hours. The product was 51 g of copolymer, so the polymerization rate was 270 g of copolymer/g of palladium/hour. The copolymer had an LVN of 0.3 dl/g. EXAMPLE 4 A carbon monoxide/ethene copolymer was prepared substantially in the same way as the copolymer of Example 3, except that in this case ethene and CO were introduced into the autoclave both in amounts equivalent to 7.5 bar. The product was 47 g of copolymer, so the polymerization rate was 250 g of copolymer/g of palladium/hour. The copolymer had an LVN of 0.4 dl/g. EXAMPLE 5 A carbon monoxide/ethene copolymer was prepared substantially in the same way as the copolymer of Example 1, except for the following differences a) ethene and CO were introduced into the autoclave in amounts equivalent to 50 bar and 100 bar, respectively, b) the quantity of catalyst was 5/3 of the quantity used in Example 1, and c) the pressure was maintained at 151 bar by introduction of a 1:1 carbon monoxide/ethene mixture. The product was 20 g of copolymer, so the polymerization rate was 4000 g of copolymer/g of palladium/hour. The copolymer had an LVN of 3.3 dl/g. EXAMPLE 6 A carbon monoxide/ethene copolymer was prepared substantially in the same way as the copolymer of Example 5, except that in this case ethene and CO were introduced into the autoclave both in amounts equivalent to 75 bar. The product was 22 g of copolymer, so the polymerization rate was 4400 g of copolymer/g of palladium/hour. The copolymer had an LVN of 5.1 dl/g. EXAMPLE 7 A carbon monoxide/ethene copolymer was prepared substantially in the same way as the copolymer of Example 5, except for the following differences a) the reaction temperature was 80 °C, and b) the polymerization was terminated after 0.5 hour. The product was 25 g of copolymer, so the polymerization rate was 10,000 g of copolymer/g of palladium/hour. The copolymer had an LVN of 1.1 dl/g. EXAMPLE 8 A carbon monoxide/ethene copolymer was prepared substantially in the same way as the copolymer of Example 7, except that in this case ethene and CO were introduced into the autoclave both in amounts equivalent to 75 bar. The product was 25 g of copolymer, so the polymerization rate was 10,000 g of copolymer/g of palladium/hour. The copolymer had an LVN of 2.4 dl/g. EXAMPLE 9 A carbon monoxide/ethene copolymer was prepared substantially in the same way as the copolymer of Example 1, except for the following differences a) the reaction temperature was 35 °C, b) the quantity of catalyst was 10/3 of the quantity used in Example 1, and c) the polymerization was terminated after 25 hours. The product was 37 g of copolymer, so the polymerization rate was 150 g of copolymer/g of palladium/hour. The copolymer had an LVN of 5.3 dl/g. EXAMPLE 10 A carbon monoxide/ethene copolymer was prepared substantially in the same way as the copolymer of Example 1, except for the following differences a) the reaction temperature was 40 °C, and b) the polymerization was terminated after 20 hours. The product was 18 g of copolymer, so the polymerization rate was 300 g of copolymer/g of palladium/hour. The copolymer had an LVN of 2.2 dl/g. EXAMPLE 11 A carbon monoxide/ethene copolymer was prepared substantially in the same way as the copolymer of Example 1, except that in this case the reaction temperature was 85 °C. The product was 15 g of copolymer, so the polymerization rate was 5000 g of copolymer/g of palladium/hour. The copolymer had an LVN of 0.5 dl/g. EXAMPLE 12 A carbon monoxide/ethene copolymer was prepared substantially in the same way as the copolymer of Example 1, except that in this case the reaction temperature was 110 °C. The product was 18 g of copolymer, so the polymerization rate was 6000 g of copolymer/g of palladium/hour. The copolymer had an LVN of 0.2 dl/g. Of the Examples 1-12 only Examples 6 and 8 are examples according to the invention. In these examples the copolymers were prepared at an overall pressure of between 75 and 250 bar and an ethene/carbon monoxide partial pressure ratio of between 0.75 and 3. Examples 1-5, 7 and 9-12 fall outside the scope of the invention; they have been included in this patent application for comparison. With the aid of ¹³C-NMR analysis it was established that the copolymers prepared according to Examples 1-12 had a linear alternating structure and therefore consisted of units of the formula -CO-(C₂H₄)-. All the copolymers prepared according to Examples 1-12 had a melting point of 257 °C. Comparison of Examples 9, 10, 1, 11 and 12, which were all carried out at the same overall pressure and ethene/carbon monoxide partial pressure ratio but at different reaction temperatures, shows that an increase in reaction temperature of from 35 to 100 °C leads to an increased polymerization rate of from 150 to 6000 g of copolymer/g of palladium/hour, whereas the LVN drops from 5.3 to 0.2 dl/g. It is also seen that according as the temperatures used are higher, the positive influence this has on the polymerization rate decreases whilst the negative influence on the LVN is maintained. Comparison of Examples 3, 1 and 5, which were all carried out at the same temperature and ethene/carbon monoxide partial pressure ratio but at different overall pressures, shows that an increase in the overall pressure of from 16 to 151 bar leads to an increased polymerization rate of from 270 to 4000 g of copolymer/g of palladium/hour while at the same time the LVN increases from 0.3 to 3.3 dl/g. Comparison of Example 1 with Example 2 and of Example 3 with Example 4, which were prepared in pairs at the same temperatures and overall pressures but at different ethene/carbon monoxide partial pressure ratios, shows that an increase in partial pressure ratio from 0.5 to 1 at an overall pressure below 75 bar produces no significant change in either polymerization rate or LVN. Comparison of Example 5 with Example 6 and of Example 7 with Example 8, which were carried out in pairs at the same temperatures and overall pressures but at different ethene/carbon monoxide partial pressure ratios, shows that an increase in partial pressure ratio from 0.5 to 1 at an overall pressure between 75 and 250 bar produces no significant change in the polymerization rate, whereas the LVN increases considerably. Comparison of Example 6 with Example 9 and of Example 8 with Example 10, which produced pairs of copolymers having similar LVN's, shows that by the polymerizations carried out according to the invention polymerization rates are achieved which are 29 and 33 times as high, respectively.

Claims: Process for the preparation of polymers comprising copolymerizing a mixture of carbon monoxide and ethene at a temperature of between 20 and 200 °C and at elevated pressure, by using a catalyst composition based upon a) a palladium salt of a carboxylic acid, b) an anion of an acid with a pKa of less than 2, provided that the acid is not a hydrohalogenic acid, and c) a bidentate ligand of the general formula R¹R²M-R-MR³R⁴, wherein M represents phosphorus, arsenic or antimony, R¹, R², R³ and R⁴ represent hydrocarbyl groups which may or may not be substituted with polar groups and R represents a bivalent organic bridging group which contains at least two carbon atoms in the bridge, characterized in that the copolymerization is carried out at an overall pressure of between 75 and 250 bar and an ethene/carbon monoxide partial pressure ratio of between 0.75 and 3. A process as claimed in claim 1, characterized in that it is carried out at an overall pressure of between 80 and 200 bar. A process as claimed in claim 1 or 2, characterized in that it is carried out at an ethene/carbon monoxide partial pressure ratio of between 0.80 and 2.5.

Inventors: DOYLE, MICHAEL JOHN, VAN BROEKHOVEN, JOHANNES ADRIANUS MARIA
Applicants: SHELL INTERNATIONALE RESEARCH MAATSCHAPPIJ B.V.
Application year: 1987
Main classification: C08G67
IPC codes: B01J31, C08G67