MODIFICATION OF ALGINATES OR OTHER URONIC ACID COMPOUNDS BY TREATMENT WITH CO2

Abstract: A method for modification of alginates or other uronic acid containing compounds to give improved physical properties, wherein the alginates in solid form are treated with CO2 at near-supercritical or supercritical conditions. The method may be used for the epimerisation of mono, oligo or polyuronides such as heparin and chondroitin sulphate, or other uronate containing polymers.

Description: Modification of alginates or other uro.nic acid compounds by treatment with CO The present invention relates to a method for modification of alginates and other uronic acid substances to obtain changes in the functional properties, in particular with respect to the ability of forming gels with inorganic or organic polyvalent ions . Alginates are manufactured from brown sea-weed and are utilized in several applications where their polyelectrolytic nature forms the basis for e.g. gelation, thickening as well as water- and ion-binding. Chemically spςaking, alginates constitute a group of linear, binary copolymers built up of salts of β-p-mannuronic acid (M) and its C-5 epimer, α-]_,-guluronic acid (G) . The M and G units are found in three types of sequences; G-rich sequences called G-blocks, M-rich sequences called M-blocks, and alternating sequences ^ found in MG-blocks, symbolized as MGMG. The fractional content of these monomer units as well as their sequencial distribution varies with the algal source. The ioii binding and' gelforming properties depend on the monomer fractions, but in particular on the distribution of G-units along the chain. A high content of G-blocks leads to the technically important gel-forming properties. The object of the present invention is to convert M-units to G-units in oligomers or polymers, in order to change their physical properties. This type of endo-epimerisation of the intact polymer may be performed by treating alginate with mannuronan C-5 epimerase, an enzyme participating in the in vivo biosynthesis of alginate (cf. NO application 845059) . According to the present invention such epimerisation, well known as an enzymatic process from several polysaccharide producing organisms, may also be performed without enzymes. This kind of process has previously not been possible on a polymer level, as an alkali catalyzed abstraction of H-5, resulting in a carbanion (charge at C-5) , will lead to hydrolysis of the polymer chain in the presence of water. Furthermore, most polyuronides (.e.g. alginate) are insoluble in non-polar solvents, reactions in aprotic solvents will therefore be difficult to perform. The present invention is based on a completely new principle that eliminates the problem mentioned above by treating alginate in the solid state with carbon dioxide under supercritical conditions, where the density is like in a liquid, but the diffusion rate is as in the gas state. CO2 may then act both as an aprotic solvent and as a catalyst in the alkaline removal of H-5, resulting in a C-5 carbanion. The high pressure will contribute energetically to the epimerisation, as the diaxially linked G-units give a more compact chain structure, and hence, a lower partial molar volume as compared to the diequatorially linked M-units. Furthermore, in aprotic solvents the anomeric effect renders axial substitution in C-l more favorable, as in α-^-guluronate in alginate. As starting material alginate from algal or bacterial sources may be chosen, either as salts (alkali or alkaline earth metal forms) , esters or other acid derivatives. Applications of supercritical carbon dioxide are hitherto found mainly within extraction of e.g. aroma compounds, using the supercritical fluid as an inert solvent (see H. Coenen and E. Kriegel, "Uses of Supercritical Gas Extraction in the Food Industry", J. Chem. Ing. Tech. 55 (1983) 890) . The invention forming the basis for the present invention is the first known example of a non—enzymatic, chemical epimerization of poly- saccharides, and the first application of a supercritical fluid as both catalyst and solvent in a chemical reaction. The present invention also differs from enzymatic and most other known chemical modification processes of this kind in being applicable to a solid state material. The known processes mentioned require dilute solutions (<1%) , and the product must be precipitated, purified and dried in a costly process. We have treated alginate with CO2 under supercritical conditions using varying pressures (150-500 bar) , and the experimental conditions were reflected in a varying, but significant epimerisation, a corresponding increase in gel strength also accompanied the epimerisation. Thus, the result suggests that C-5 epimerisation of glycuronans or corresponding oligosaccharides by supercritical carbon dioxide treatment provides a completely new method for chemical modification of carbohydrates. The chemical process being, the object of the present invention has a great economic potential due to the following: A) It may be performed on solid state material. B) No toxic or hazardous chemicals are needed, and hence, no purification of the product is required. C) The process may conveniently be performed on a large scale as technology for extraction with supercritical fluids is already developed for other purposes. D) The process is not limited to epimerisation of β-D- mannuronate residues in alginate, but may as well be utilized for epimerisation of other polyuronides as e.g. C-6 oxidized cellulose, where D-glucuronic acid is converted to its C-5 epi er L-iduronic acid. Corresponding reactions may be utilized in treatment of ucopolysaccharides , e.g. chondroitin sulfate and hyaluronic acid. ' Example 1: Sodium alginate (50 g) isolated from Laminaria hyperborea was packed in a steel column and treated with CO2 under supercritical conditions. The pressure was varied between 150 and 500 bar. The gas flow was 0.5-10 ml/min, the temperature 45°C and the treatment lasted for 12 hours. Loss of material was <1% in all experiments. The polymer composition was determined by high-field (400 MHz) 1 NMR spectroscopy (cf. Figure 1) (H. Grasdalen "High-field 1 H-NMR Spectroscopy of Alginate: Sequential Structure and Linkage Conformation." Carbohydr. Res. 118 (1983) 255-260) and is expressed in Table I as the molar fractions of the two monomer units, M and G, as FM and FG , respectively, where FM + FG = 1, and as the sequence parameters or fractions of the four "Nearest neighbour" sequences, MM, GG , MG and GM, where F + FS S + 2FMG = 1. The results in table I show that CO2 treatment has resulted in a significant increase in the guluronate content by three different pressure conditions. The content, as expressed by FG , changed from 0.52 (i.e. 52%) in the untreated material to 0.60, 0.64 and 0.66 after the treatment. The highest pressure (500 bar) gave the greatest change in composition. This increase in G content resulted in alginates with an increased ability to form gels with polyvalent ions. Table II shows some physical properties of the CO2 treated polymers. Viscosities were determined in a Brookfield visco eter and intrinsic viscosities [i-,] were determined in a Cannon-Ubbelohde capillary viscosimeter. Gel strengths of 1% calcium alginate gels were determined in a FIRA gel strength apparatus , and the modulus of rigidity in 2% homogenous calcium gels were determined in a Stevens Texture Analyser (G. Skjak-Brak, B. Larsen and 0. Smidsrød "Tailoring of Alginate By Enzymatic Modification in vitro." Int. J. Biol. Macromol. 8 (1986) 330-336) . The CO2 treatment resulted in a decrease in the intrinsic viscosity, supposedly caused by hydrolytic cleavage of glycosidic bonds. However, the limited degradation has r no influence on the gel forming properties of alginates. The gel strength, in terms of both the FIRA values and the modulus of rigidity, showed a pronounced increase and led to values comparable to those found for the most strongly gel-forming alginates obtained from the stipe of Laminaria hyperborea. Table I MONOMER COMPOSITION AND SEQUENCE PARAMETERS FOR CO2 -TREATED ALGINATE. Untreated sample 0.52 0.48 0.34 0.13 0.30 150 bar 0.60 0.40 0.50 0.10 0.30 250 bar 0.64 0.36 0.55 0.09 0.27 500 bar 0.66 0.34 0.53 0.13 0.21 Table II PHYSICAL PORPERTIES OF C0 2 -TREATED ALGINATE Viscosity Intrinsic vis- Gel strength in water (1%) cosity [Γ, ] FIRA Modulus of (mPa.s) (dl/g) (ml) rigidity (N/cm 2 ) 1% calcium 2% calcium gel gel Untreated sample 205 8.8 40 6,2 150 bar 80.6 6.9 63 250 bar 86.2 6.8 63.5 500 bar 80.7 6.9 63.5 9.0 Example " 2 The sodium salt of poly-mannuronic acid isolated from Ascophyllum nodosum was treated for 12 hours with supercritical CO2 at 200 bar and 45°C. The loss was <0.5%. The guluronate content in the polymer increased from <5% to 16% (cf. Figure 2) . The result clearly suggests that D-mannuronate of the intact polymer is C-5 epi erised under the given conditions. Figure 1. 400 MHz l H n.m.r. spectra of Na-alginate from L. hyperborea fronds. A: Na-alginate from L . . hyperborea fronds, treated with CO2 under supercritical conditions for 12 hours at 500 bar and 45°C. B: Untreated alginate. The change in G content of the modified polymer is demonstrated by the relative intensity increase in "G signals" (I and III) compared to "M signals" (II) Figure 2. 400 MHz 1 H n. .r. spectra of sodium polymannuronate isolated from A. nodosum. A) Treated with supercritical CO2 for 12 hours at 200 bar. (Fs = 0.16) B) Untreated poly-M (FG <0.05) . Signal I in the spectrum corresponds to tije L-guluronate content.

Claims: CLAIMS 1. A method for modification of alginates or other uronic acid containing compounds to give improved physical properties, wherein the alginates in solid form, either as salts, acid, esters or other alginic acid derivatives, are treated with CO2 , either batchwise or by continuous flushing, at near-supercritical or supercritical conditions. 2. Application of the method of claim 1 for modification of other mono, oligo or polyuronides (e.g. heparin and chondroitin sulfate, or other uronate containing polymers) .

Inventors: EKLUND TRYGVE, KVAM BJARNE JOHANNES, SKJAAK-BRAEK GUDMUND, SMIDSROED OLAV, VON HUSBY KURT OVE, EKLUND, TRYGVE, KVAM, BJARNE, JOHANNES, SKJAAK-BRAEK, GUDMUND, SMIDSROED, OLAV, VON HUSBY, KURT, OVE
Applicants: PROTAN AS, PROTAN A/S
Application year: 1987
Main classification: C08B37
IPC codes: C08B1, C08B37