CHELATE LIGANDS FOR LOW PRESSURE HYDROFORMYLATION CATALYST AND PROCESS EMPLOYING SAME

Abstract: Hydroformylation reactions wherein at least one olefin having from 2 to 20 carbon atoms is contacted in a reaction zone at a temperature of from about 20 DEG C to about 250 DEG C and a pressure of from about 15 psig to about 800 psig with hydrogen, carbon monoxide, and a catalyst containing rhodium, at least one ligand having formula (I), wherein each Ar is independently selected from aromatic ring compounds having 6 up to 14 carbon atoms, e.g., phenyl, naphthyl, phenanthryl and anthracenyl; the x bonds and the y bonds are attached to adjacent carbon atoms on the ring structures; each R, when present as a substituent, is independently selected from alkyl, alkoxy, aryloxy, aryl, aralkyl, alkanyl, alkoxyalkyl, cycloaliphatic, halogen (except Cl, Br or I in the ortho position), alkanoyl, alkanoyloxy, alkoxycarbonyl, or formyl; n is a whole number in the range of 0-4 where Ar is phenyl; 0-6 where Ar is naphthyl; and 0-8 where Ar is phenanthryl or anthracenyl; each R1 and R2 is independently selected from alkyl, aryl, aralkyl, alkaryl or cycloaliphatic; each R3 and R4 is independently selected from hydrogen and the R1 substituents; each of the above alkyl groups or moieties is straight or branched chain of 1-20 carbons, preferably 1-8 carbons; each aryl group contains 6-10 ring carbons; each cycloaliphatic group contains from 4-8 ring carbons; and each Y is independently selected from the elements N, P, As, Sb and Bi. Also disclosed are novel ligands wherein one or both of the Ar moieties are phenyl rings.

Description: CHELATE LIGANDS FOR LOW PRESSURE HYDROFORMYLATION CATALYST AND PROCESS EMPLOYING SAME This invention concerns novel chelate ligands and hydroformylation catalysts and processes employing the same wherein one or more olefins and/or non-conjugated diolefins andlor other unsaturated organic compounds, all hereinafter referred to as hydroformylation stock, may be converted to aldehydes for use as such or for conversion by known methods, to products such as alcohols and acids. More particularly, the invention concerns ligands especially useful for oxo or hydroformylation processes designed for relatively low pressure operation for the preparation of unusually high proportions of normal er unbranched aldehydes from a-olefins, particularly n-butyraldehyde from propylene. The chelate ligands contemplated by the present invention are compounds of the general formula EMI1.1 wherein: each Ar is independently selected from aromatic ring compounds having 6 up to 14 carbon atoms, e.g., phenyl, naphthyl, phenanthryl and anthracenyl; the x bonds and the y bonds are attached to adjacent carbon atoms on the ring structures; each R, when present as a substituent, is independently selected from alkyl, alkoxy, aryloxy, aryl, aralkyl, alkaryl, alkoxyalkyl, cycloaliphatic, halogen (except C1, Br or I in the ortho-position), alkanoyl, alkanoyloxy, alkoxycarbonyl or formyl; n is a whole number in the range of 0-4 were Ar is phenyl; 0-6 where Ar is naphthyl; and 0-8 where Ar is phenanthryl or anthracenyl; each R1 and R2 is independently selected from alkyl, aryl, aralkyl, alkaryl or cycloaliphatic; each R3 and R4 is independently selected from hydrogen and the R1 substituents; each of the above alkyl groups or moieties is straight or branched chain of 1-20 carbons, preferably 1-8 carbons; each aryl group contains 6-10 ring carbons; each cycloaliphatic group contains from 4-8 ring carbons; and each Y is independently selected from the elements N, P, As, Sb and Bi, with P being preferried. In a particular embodiment of the present invention, the ligands employed in the practice of the present invention are compounds of the formula EMI2.1 wherein: n is 0-4; each R is independently selected from alkyl, alkoxy, aryloxy, aryl, aralkyl, alkaryl, alkoxyalkyl, cycloaliphatic, halogen (except C1, Br or I in the ortho position), alkanoyl, alkanoyloxy, alkoxycarbonyl, or form; each R1 and R2 is independently selected from alkyl, aryl, aralkyl, alkaryl or cycloaliphatic; each R3 and R4 is independently selected from hydrogen and the R1 substituents; each of the above alkyl groups or moieties is straight or branched chain of 1-20 carbons, each aryl group contains 6-10 ring carbons, and each cycloaliphatic group contains from 4-8 ring carbons; and each Y is independently selected from the elements N, P, As, Sb and Bi, with P being preFerred. In another particular embodiment of the present invention, the ligands contemplated are compounds of the general formula EMI3.1 wherein: the x bonds and the y bonds are attached to adjacent carbon atoms on the ring structures; each R when present as a substituent is independently selected from alkyl, alkoxy, aryloxy, aryl, aralkyl, alkaryl, alkoxyalkyl, cycloaliphatic, halogen (except C1, Br or I in the ortho position), alkanoyl, alkanoyloxy, alkoxycarbonyl, or form; each R1 and R2 is independently selected from alkyl, aryl, aralkyl, alkaryl or cycloaliphatic; each R3 and R4 is independently selected from hydrogen and the R1 substituents; ; each of the above alkyl groups or moieties is straight or branched chain of 1-20 carbons, preferably 1-8 carbons, each aryl group contains 6-10 ring carbons, and each cycloaliphatic group contains from 4-8 ring carbons; and each Y is independently selected from the elements N, P, As, Sb and Bi, with P being preferred. In yet another particular embodiment of the present invention, the ligands contemplated are compounds of the general formula EMI4.1 wherein: the x bonds and the y bonds are attached to adjacent carbon atoms on the ring structures; each R when present as a substituent is independently selected from alkyl, alkoxy, aryloxy, aryl, aralkyl, alkaryl, alkoxyalkyl, cycloaliphatic, halogen (except C1, Br or I in the ortho position), alkanoyl, alkanoyloxy, alkoxycarbonyl, or form; each R1 and R2 is independently selected from alkyl, aryl, aralkyl, alkaryl or cycloaliphatic; each R3 and R4 is independently selected from hydrogen and the R1 substituents; ; each of the above alkyl groups or moieties is straight or branched chain of 1-20 carbons, preferably 1-8 carbons, each aryl group contains 6-10 ring carbons, and each cycloaliphatic group contains from 4-8 ring carbons; and each Y is independently selected from the elements N, P, As, Sb and Bi, with P being preFerred. Preferred of the present ligands are 2,2'-bis (diphenylphosphinomethyl)-l,l"-biphenyl; 2,2'-bis (dibenzylphosphinomethyl)-l,l'-biphenyl; 2,2'-bis (phenylbenzylphosphinomethyl )-l , 1 '-biphenyl; 2,2'-bis(diisobutylphosphinomethyl)-1,1'-biphenyl; 2-(diphenylphosphinomethyl )-l-[ 2-(diphenylphosphino- methyl)phenyl]naphthalene; and 2,2'-bis(diphenyl phosphinomethyl )-l, 1 '-binaphthyl. The present hydroformylation process in its broad sense comprises contacting at least one olefin having from 2 to 20 carbon atoms in a reaction zone at a temperature of from about 200C to about 2500C and a pressure of from about 15 psig to about 800 psig with syn gas (H2, CO) and a catalyst comprising rhodium in chemical complex with one or more of the above ligands for a sufficient period of time to permit reaction of said olefin with said syn gas to form aldehyde product. Alpha-olefins with heteroatom substitution on the molecule such as allyl alcohol, allyl acetate, 4-hydroxybutene-l, and the like may also be used in this invention. Also, branched olefins such as isobutene and internal olefins such as cis-butene-2 may be used herein as feedstocks for the preparation of aldehyde products. Diolefins such as 1,7-octadiene and the like may also be used to prepare dialdehyde products provided that the two carboncarbon double bonds are not in conjugation. The present ligands, in particular, the 2,2'-bis(phosphinomethyl)-l,l'-biphenyl ligand class (hereinafter BISBI), the 2-(diphenylphosphino methyl)-l-[2-(diphenylphosphinomethyl)phenyl]- naphthalene ligand class (hereinafter, PHENAP), the 2,2'-bis(diphenylphosphinomethyl)-l ,l '-binaphthyl ligand class (hereinafter, NAPHOS) have great utility as bidentate ligand modifiers for the low pressure rhodium hydroformylation of alphaolefins to prepare aldehyde products with unusually high ratios of normal to branched isomers. This invention effects the efficient use of olefinic feedstocks to prepare desirable linear aldehyde products in high yield. Such products from propylene include n-butyraldehyde which is used to prepare the commercial solvent n-butanol. The hydroformylation of l-butene and l-pentene yield intermediate aldehyde products useful for the preparation of the solvents l-pentanol and l-hexanol, respectively. The hydroformylations of l-hexene and l-octene yield aldehyde products used to prepare the commercially valuable carboxylic acids, n-heptanoic acid and n-nonanoic acid. These same aldehyde products may be converted into alcohols useful for the preparation of plasticizers, synthetic lubricants, and detergents. Likewise, the hydroformylation of higher olefins such as l-decene and l-dodecene yield aldehyde precursors to l-undecanol and l-hydroxytridecane useful as fabric softeners and ingredients in plasticizers and detergents. These ligands show improvements in hydroformylation technology in one or more areas such as high normal to iso ratios employing relatively small amounts of ligand effective in low pressure systems, increased catalytic activity and retention thereof over extended periods, and increased catalyst stability. The ligands of the invention are particularly useful in their unique ability to produce the desired high normalliso ratios even at desirable low levels of ligand. As a general statement of the actual chemical composition of the present active catalyst species in the reaction zone, the species preferably comprises rhodium complexed with (a) a ligand defined by the above structural formulae in a molar ratio of ligand/Rh of about 1/1, (b) H in an atomic ratio of H/Rh of about 1/1, and (c) carbon monoxide in a molar ratio of CO/Rh of about 2/1. The present process is carried out preferably in a gas sparged reactor such that the catalyst which is dissolved in a high boiling organic solvent under pressure does not leave the reaction zone with the aldehyde product which is taken overhead by the unreacted gases. The overhead gases are then chilled in a vapor liquid separator to condense out the aldehyde product, the gases being recycled to the reactor'and the liquid product let down to atmospheric pressure for separation and purification by conventional techniques. A side draw from the reactor preferably is provided so that a small amount of the catalyst can be withdrawn at a desirable rate for more complete distillation and/or regeneration and returned to the reactor after the addition of make-up ligand thereto. The metal catalyst components are charged preferably with solvent to the reactor through suitable pressurized pumping means, preferably in their soluble forms, e.g., their carboxylate salts or mineral acid salts or the like well known to the art as disclosed, for example, in U.S. Patent 2,880,241. Charged therewith or separately is one or more of the present modifying ligands in amounts such that the molar ratio of ligand to rhodium in the reactor is from about 1.0 to about 200 or more, preferably from about 2.0 to about 10.0, and most preferably from about 2.3 to about 4.0 The process is particularly effective at pressures from about 15 to about 800 psig with from about 100 to about 400 psig being preferred, and from about 240 to about 280 psig being most preferred. The reaction temperatures can vary from about 20 to about 2500C, but preferably from about 50 to about 1750C and most preferably from about 80 to about l500C. In a highly preferred embodiment, the above process is carried out wherein at steady state hydroformylation conditions in said reaction zone the ratio of Rh(mg.)/solvent (ml) is from about 0.07 to about 0.28, the ratio of (olef in feed in liters (STP)/min]/mg. of Rh is from about 0.03 to about 0.30, the ratio of tCO or H2 feed in liters (STP)/min]/mg. of Rh is from about 0.015 to about 1.5, the temperature is maintained at from about 800C to about 150 C, and the reactor pressure is maintained at from about 240 psig to about 280 psig. The term "STP" refers to standard temperature of 2730K and standard pressure of 760 mm Hg. In the process, the syn gas is introduced into the reactor in a continuous manner by means, for example, of a primary compressor, and the ratio of hydrogen to carbon monoxide in the feed may be selected according to the particular olefin being hydroformylated and the reaction conditions present, as is well known in the art. Generally, the molar ratio of hydrogen to carbon monoxide in the reactor is maintained within the range of about 0.5 to about 4.0, but it has been found in many hydroformylations that the rate of reaction as well as yield of the desired product may be increased by increasing the hydrogen to carbon monoxide molar ratio above 4.0, and up to about 10.0 or more. In the reactor zone the syn gas preferably is present in a molar excess (total moles of H2 + CO) with respect to the olefin and the molar ratio varies typically from about 0.25 to about 20, preferably from about 1.2 to about 6. In a liquid overflow reactor, the above molar ratio may have a lower limit of about 0.02. The olefin is fed to the reactor by means of suitable pumps capable of operating under substantial pressures, and the feed rates of the olefin and syn gas are selected to maintain the above-recited molar ratios of these reactants in the reactor. Typical olefins to which the present invention is applicable include straight or branched chain a-olefins containing from 2 to 20 carbon atoms and preferably from 2 to 10 carbon atoms, and optionally containing groups or substituents'which do not interfere with the hydroformylation process. Illustrative of such a-olefins are ethylene, propylene, l-butene, 2methylpropylene, 2-methyl-l-butene, 1-pentene, l-hexene, l-heptene, l-octene, 2-ethyl-1-hexene, l-dodecene, l-octadecene and allyl alcohol. Also useful with the present invention are the internal olefins such as butene-2 and cyclic olefins such as cyclooctene. If desired, mixtures of olefins, particularly ethylene and propylene, can be fed to the reactor. Any suitable solvent which does not adversely affect the hydroformylation process and which is inert with respect to the catalyst, olefin feed, syn gas and the hydroformylation products may be used. Inert solvents of this nature are well known to those skilled in the art and include benzene, xylene, toluene and their substituted derivatives, pentanes, naphtha, kerosene, mineral oils, cyclohexane, cyclopentane, ethers, esters, etheresters, alcohols, acetals, ketones, and various mixtures thereof. Preferred solvents are those which are sufficiently high boiling to remain for the most part in the gas sparged reactor, and include 2,2,4-trimethyl-1,3pentanediol monoisobutyrate (TMPDMI; available from Eastman Chemicals Division of Eastman Kodak as Texanole solvent), and its isomers, and the by-products such as alcohols, esters, acetals, and hydroxyaldehydes produced in the hydroformylation reaction and retained as high boiling liquids at the bottom of the subsequent distillation columns. Aldehyde product also may be prepared batchwise with the present invention by contacting the olefin, hydrogen, and carbon monoxide with the present catalyst in an autoclave. High boiling aldehyde products such as normal nonanal may be prepared in a continuous manner with the aldehyde product being removed from the reactor zone as a liquid in combination with the catalyst. The aldehyde product may be separated from the catalyst by conventional means such as by distillation, and the catalyst then recycled back to the reactor. It will be apparent to those skilled in-the art that other reactor schemes may be used with this invention. The present process can be carried out with very small amounts of catalyst containing from about 1 x 10 moles of rhodium (calculated as RhO) per mole of olefin in the reactor zone. However, such low catalyst concentrations are not commercially desirable since the reaction tates are low. The upper catalyst concentration is essentially unlimited and appears to be dictated principally by the high cost of rhodium and the fact that no advantage is evident in the use of catalyst containing above about 1 x 10 1 moles of rhodium per mole of olefin in the reactor zone. A concentration of from about 1 x 10 5 moles to about 5 x 10 2 moles of rhodium per mole of olefin is preferred, and from about 1 x 10 to about 1 x 10 is most preferred. This invention will be illustrated further by the following examples although it will be understood that these examples do not limit the invention and are for purposes of illustration only. LIGAND PREPARATION The synthesis of the present chelating diphosphine ligands is straightforward thus making them easily prepared in practical quantities. Below are given some of the synthetic routes available to prepare the ligands, the phosphorylation of 2,2'-bis (bromomethyl)-l,l'-biphenyl by alkali metal "M" phosphine anions being a particularly useful synthesis. Examples are given herein of the synthesis of the bis(diphenylphosphino), bis(phenylbenzylphosphino), and bis(diisobutylphosphino) derivatives using this method (Reaction I). Likewise, the diphosphino chelate ligands may be prepared by the oxyphosphorylation of the above dibromo compound by its reaction with alkali metal salts of the phosphine oxide anion and subsequent reduction to the diphosphine chelating ligand (Reaction II) by any of a number of reducing agents such as lithium aluminum hydride. EMI11.1 Reaction I EMI12.1 Reaction II The above 2,2'-bis(bromomethyl)-1,1'-biphenyl intermediate is prepared in high yield.-from 2,2'bis(hydroxymethyl)-l,l'-biphenyl by its reaction with PBr The diol precursor is easily obtained in known manner by either standard catalytic hydrogenation or by lithium aluminum hydride reduction of diphenic acid. The diol is also easily prepared by reduction of 2,2'-bis(formyl)-l,l-biphenyl, obtained by the high yield ozonolysis of phenanthrene in known manner. The diphosphine ligand 2-(diphenylphosphinomethyl)-1-[2-(diphenylphosphinomethyl)phenyl]naphthalene (PHENAP) was prepared by a reaction sequence shown below. In this sequence 2-methyl- l-(2-methylphenyl)naphthalene (I) was synthesized by the nickel-catalyzed cross-coupling of 2-bromotoluene and the Grignard reagent produced from l-bromo-2methylnaphthalene by the Maigrot/Mazaleyrat procedure published in Synthesis, 317 (1985). The resulting biaryl was brominated using N-bromosuccinimide, with N,N'-azobis(isobutyronitrile) as catalyst, to form 2-bromomethyl-1-[2-bromomethyl)phenyl]naphthalene (II) by the Bestman/Both procedure, Chem. Ber., 107,2926, (1974). The dibromide was then treated with methyl diphenylphospinite by the procedure of Arbuzov/Nikonorov Zhur Obshchei Khim., 18,2008 (1984); Chem; Abstracts, 43,380li (1949) to give the bisphosphine dioxide (III). Reduction of the dioxide with trichlorosilane/triethylamine by the procedure of Fritzsche/Hasserodt Chem. Ber.. 98.171 (1965) produced the desired product PHENAP. Reaction Sequence For PHENAP EMI13.1 EMI14.1 <tb> ioi <SEP> ./\ <SEP> C1SIH <SEP> fizzo <SEP> o <SEP> I\ <tb> <SEP> Ph <SEP> Cl3SiH <SEP> lOiOi <tb> CE3t3iH > <SEP> \ <SEP> / <SEP> \i/ <SEP> \*/ <SEP> 2 <tb> <SEP> I <SEP> Et3N <SEP> > <SEP> I <tb> <SEP> 3 <SEP> / <SEP> .\?Ph <tb> <SEP> I\O/ <SEP> I <SEP> \gPh2 <SEP> 1\O/I <SEP> 2 <tb> <SEP> III <SEP> PHENAP <tb> wherein Ph = phenyl. NAPHOS was synthesized by a sequence of published procedures. The 2,2'-dimethyl-l,l'- binaphthyl was prepared from 1-bromo-2-methylnaphthalene by the method of Maigrot and Mazaleyrat, Synthesis, 317 (1985). Benzylic bromination of 2,2'-dimethyl-1,1'-binaphthyl with N-bromosuccinimide and catalytic N,N'-azobis(isobutyronitrile), by the procedure of Bestmann and Both Chem. Ber., 107, 2926 (1974), afforded 2,2'-bis(bromomethyl)-1,1'- binaphthyl. Using methods outlined by Tamao, et al in Tetrahedron Letters No. 16, pp 1389-1392, 1977, Pergamon Press, Gr. Brit., the dibromide was converted to NAPHOS (1,1) dioxide by reaction with methyl diphenylphosphinite and the dioxide was reduced with trichlorsilane/triethylamine to yield NAPHOS. It is noted that none of these references are concerned in any way with the use of NAPHOS for oxo or hydroformylation reactions. All experimental procedures involving phosphines or organometallic compounds were run under an atmosphere of nitrogen using dry,. deoxygenated solvents. Tetrahydrofuran (THF) was distilled under nitrogen from sodium/benzophenone ketyl. Chemical shifts for nuclear magnetic resonance (NMR) spectra are reported in parts per million (b) downfield from tetramethylsilane for 1 H NMR spectra and relative to aqueous H3PO4 for 31P NMR spectra. Example 1 - 2,2'-Bis(hydroxymethyl)-l,l'-biphenyl Lithium aluminum hydride (12.60 grams, 0.332 mol) and THF (175 ml) were placed in a dry 500 ml three-necked round-bottomed flask fitted with a condenser, addition funnel, nitrogen inlet, and magnetic stirrer. The mixture was cooled with an ice bath and diphenic acid (40.00 grams, 0.165 mol) in THF (100 ml) was added dropwise to the stirring mixture. After the addition was complete, the flask was removed from the ice bath and allowed to warm to room temperature. The reaction mixture was heated at reflux for 2 hours, then stirred overnight at room temperature. After cooling the mixture with an ice bath, water (12.6 ml) was added dropwise, followed by the successive dropwise addition of 155 aqueous sodium hydroxide (12.6 ml) and water (38 ml). The resulting yellow mixture was warmed to room tempera- ture, and the solids were separated by vacuum filtrate tion. The filtrate was placed on a rotary evaporator to remove the solvent. The remaining brownish-yellow solid was recrystallized from toluene-hexane to give 28.60 grams (815 yield) of light brown solid product, melting point 1050 to 1080C. 1H NMR (CDCl3): 6 2.77 (br s, 2H, -OH); 3.95 (s, 4H, 6.50-7.25 (m, 8H, aromatic). ExamPle 2 - 2,2'-Bis(bromomethyl)-l,l'-biphenyl 2,2'-Bis(hydroxymethyl)-l,l'-biphenyl (25.00 grams, 0.117 mol) and methylene chloride (200 ml) were placed in a 500 ml round-bottomed flask equipped with a magnetic stirrer and an addition funnel with a Caul2 drying tube. The stirred mixture was cooled with an ice bath, and phosphorus tribromide (23.1 ml, 66.50 grams, 0.246 mol) was added dropwise from the addition funnel. After the addition was complete, the reaction mixture was removed from the ice bath and stirred overnight at room temperature. The mixture was again cooled with an ice bath, and water (35 ml) was added slowly. After stirring for 1 hour, additional water (75 ml) was added. The layers were separated in a separatory funnel, and the aqueous layer extracted twice with CH2Cl2 - The combined organic layer was washed with saturated aqueous NaHCO3 and water and was then dried with MgSO4. The solvent was removed on a rotary evaporator to give 37.05 grams (935 yield) of light yellow solid which was suitable for use without further purification. The melting point was 850C to 880C. H NMR (CDCl3): 6 4.10 (d, J = 10 Hz, 2H, -cH-Br); 4.22 (d, J = 10 Hz, 2H, -CH-Br); 6.92-7.53 (m, 8H, aromatic) ExamPle 3 - 2,2'-Bis(diphenylphosphinomethyl)-l,l' biphenyl Diphenylphosphine (10.0 ml, 10.70 grams, 0.057 mol) was dissolved in dry THF (115 ml) under nitrogen in a 300-ml three-necked round-bottomed flask equipped with a magnetic stirrer, addition funnel, and condenser with a nitrogen inlet. The solution was cooled to about -700C with a dry ice/acetone bath and n-butyllithium (35.9 ml of a 1.6 M solution in hexane, 0.057 mol) was added dropwise from the addition funnel. The orange solution was stirred 1 hour in the cold bath. A solution of 2,2'-bis(bromomethyl)-l,l'-biphenyl (9.30 grams, 0.027 mol) in THF (50 ml) was added dropwise from the addition funnel over about 20 minutes. The solution was allowed to stir overnight at room temperature and was then heated at reflux for 3 hours. Saturated aqueous NH4C1 (about 50 ml) was added to the stirring solution at room temperature. Diethyl ether (75 ml) was added, and the layers were separated in a separatory funnel. The aqueous layer was extracted twice with diethyl ether. The combined organic solution was washed twice with water. The organic solvent was evaporated on a steam bath under a stream of nitrogen to give a thick, oily residue. The residue was recrystallized from ethanol/diethyl ether to give 10.64 grams (71X yield) of white solid, melting point 840 to 870c. 1H NMR (CDCl3): s 3.15 (s, 4H, -CH2-); 6.60-7.40 (m, 28H, aromatic). 31P NMR (CDCl3): 6 + 9. Example 4 - 2,2'-Bis(diisobutylphosphinomethyl)-l,l'- biphenyl Diisobutylphosphine (1.66 grams, 11.37 mmol) was dissolved in THF (25 ml) under nitrogen and cooled with a dry ice/acetone bath. n-Butyllithium (7.11 ml of a 1.6 M solution in hexane, 11.37 mmol) was added dropwise to the stirring solution which was then allowed to stir for 1 hour in the cold bath. 2,2'-Bis(bromomethyl)-l,l'-biphenyl (1.89 grams, 5.55 mmol) in THF (10 ml) was added dropwise at -700C. The solution was allowed to stir overnight at room temperature and was then heated at reflux for 1 hour. Saturated aqueous NH4C1 was added to the solution at room temperature. Diethyl ether was added and the layers were separated in a separatory funnel. The aqueous layer was extracted twice with diethyl ether, and the combined organic solution was then washed twice with water. The solvent was removed on a steam bath under a stream of nitrogen. The oily residue was then placed on a Kugelrohr distillation apparatus to remove low boiling material at about 170C and 1 mm Hg leaving 1.88 grams (72X yield) of a thick orange glassy product. 1H NMR (CDCl3): 6 0.65-1.67 (complex, 36H, aliphatic); 2.42 (s, 4H, benzylic); 6.67-7.30 (complex, 8H aromatic). 31P NMR (CDCl3): b +31. Example 5 - 2,2'-Bis(dibenzylphosphinomethyl)-l,l' biphenyl Dioxide Dibenzylphosphine oxide (6.93 grams, 30.1 mmol) and THF (100 ml) were placed in a 300-ml three-necked flask and cooled at -400C under nitrogen. n-Butyllithium (18.84 ml of a 1.6 M solution in hexane, 30.1 mmol) was added dropwise from an addition funnel over about 10 minutes and the resulting yellow solution was stirred for 1 hour at -300C to -350C. 2,2'-Bis (bromomethyl)-l,l'-biphenyl (5.00 grams, 14.7 mmol) in THF (20 ml) was added dropwise to the cold solution. -When the addition was complete,.the solution was warmed to room temperature and was then heated at reflux for 1.5 hours. Saturated aqueous NH4C1 was added and the layers were separated. The aqueous layer was extracted twice with diethyl ether. The combined organic solution was washed with saturated aqueous NaCl. The organic solvent was evaporated on a steam bath under a stream of nitrogen to give a light brown solid. The product was recrystallized from acetone to give a first crop of 3.57 grams (385 yield) of white solid, melting point 2030 to 2050C. No attempt was made to recover a second crop. H NMR (CDCl3): 6 2.07-3.08 (complex, 12H, benzylic); 6.57-7.47 (complex, 28H, aromatic). 31p NMR (CDC13): b -43. Example 6 - 2,2'-Bis(dibenzylphosphinomethyl)-l,l' biphenyl Chlorotrimethylsilane (4.1 ml, 32.2 mmol) was added to lithium aluminum hydride (122 grams, 32.2 mmol) in THF (20 ml) at -720C. The mixture was removed from the cold bath, stirred 2 hours, and then cooled again at -350C. A suspension of the above 2,2'-bis(dibenzylphosphinomethyl)-1,1'-biphenyl dioxide (3.40 grams, 5.32 mmol) in THF (45 ml) was added by cannula. The mixture was stirred 0.5 hour at -300C, then overnight at room temperature. The reaction mixture was cooled in an ice bath and quenched by the successive, dropwise addition of water (1.2 ml), 15% aqueous NaOH (1.2 ml) and water (3.6 ml). The resulting mixture was filtered, and the solid was washed with diethyl ether. The filtrate was evaporated on the steam bath under a stream of nitrogen. The residual solid was heated in ethanol, then cooled and filtered to give 2.00 grams (62% yield) of white solid, melting point 1630 to 167 C. 1H MMR (CDCl3): 6 2.43 (s, 12H, benzylic); 6.50-7.17 (complex, 28H, aromatic). 31P NMR (CDCl3): 6 +9.5. ExamPle 7 - 2,2'-Bis(benzylphenylphosphinomethyl) 1 , 1 '-biphenyl Benzyldiphenylphosphine (9.74 grams, 35.3 mmol) was dissolved in THF (100 ml) under nitrogen in a 250 ml three-necked round-bottomed flask equipped with a magnetic stirrer', thermometer, and condenser with a nitrogen inlet. A small amount of naphthalene (0.12 gram) was added followed by the addition of lithium metal (0.49 gram, 70.6 mmol) in small pieces. The mixture quickly became dark reddishbrown and was heated at 400C for 6 hours. t-Butyl chloride (2.29 grams, 24.8 mmol) was added dropwise at room temperature, and the mixture was stirred for 0.5 hour. 2,2'-Bis(bromomethyl)-l,l'-biphenyl (4.71 grams, 13.9 mmol) in THF (20 ml) was added dropwise, whereupon the color changed from dark red-brown to medium orange. The mixture was allowed to stir overnight at room temperature and was then heated at reflux for 1 hour. Water (40 ml) was added and most of the THF was removed on the steam bath under a stream of nitrogen. The aqueous solution was extracted three times with diethyl ether. The combined organic solution was washed with water. The solvent was evaporated to leave an orange oily residue which was placed in a Kugelrohr distillation apparatus and heated at 2200C/1 mm Hg to remove low boiling components, leaving 9.20 grams of an orange glassy solid. 1H NMR (benzene-d6): b 3.28 (br s, 8H benzylic); 6.33-7.33 (complex,, 28H, aromatic). P NMR (benzened6): s +10. ExamPle 8 - Preparation of Compound I, 2Methyl-l- (2Methyl-phenyl )Naphthalene Magnesium turnings (4.00 gr, 0.165 mol) and anhydrous diethyl ether (30 mL) were placed in a 500mL three-neck round bottom flask, fitted with a condenser, addition funnel and nitrogen inlet. A crystal of iodine and 3-4 drops of 1,2-dibromoethane were added and the mixture was stirred magnetically. A solution of l-bromo-2-methylnaphthalene (33.20 gr, 0.150 mol) in a 1:1 mixture of diethyl ether-benzene (120 mL) was added dropwise at a rate such that gentle reflux was maintained. After the addition was complete (about 1.5 hour), the mixture was heated at reflux for an additional hour, then cooled to room temperature. This mixture was then added rapidly under nitrogen to a stirring mixture of 2-bromotoluene (22.90 gr, 0.134 mol) and bis(triphenylphosphine)nickel dichloride (1.0 gr, 1.52 mmol) in diethyl ether (100 mL). The flask which had contained the Grignard reagent was rinsed with additional diethyl ether (60 mL), which was then added to the reaction mixture. The mixture was heated at reflux for 16 hours and then cooled to room temperature. Water (100 mL) was added, followed by the addition of 20 percent hydrochloric acid (100 mL). After stirring about 1 hour, the mixture was transferred to a separatory funnel and the layers were separated. The organic solution was washed twice with water (100 mL each) and then dried (MgSO4). After filtration, the solvent was evaporated from the filtrate and the residue was distilled to give the desired product (I), boiling point 156 -163 /0.5 mm Hg, 23.82 gr (77 percent), as a thick, light yellow liquid. 1H nmr (benzene-d6): S = 1.77 (s, CH3), 1.99 (s, CH3), 6.67-7.60 (complex, aromatic) Example 9 - Preparation of Compound II, 2-Bromo methyl-l-12-(bromomethyl)phenyl]- naphthalene 2-Methyl-l-(2methylphenyl )naphthalene (I) (21.58 gr, 0.093 mol) was dissolved in carbon tetrachloride (70 mL) and placed in a 250-mL round bottom flask fitted with a condenser. N-Bromosuccinimide (34.23 gr, 0.192 mol) and N,N'-azobis (isobutyronitrile) (0.1 gr) were added and the mixture was heated at reflux for 5 hr. After cooling to room temperature, the mixture was filtered. The filtrate was washed with saturated aqueous sodium bicarbonate and then was washed twice with saturated aqueous sodium chloride. The organic solution was dried (MgSO4), filtered and evaporated on the rotary evaporator to give a dark amber, thick liquid. This material was dissolved in toluene and passed through a short column of neutral alumina. The solvent was removed on the rotary evaporator to give a thick, orange liquid, 32.34 gr (89 percent), which was used in the next reaction without further purification. 1H nmr (CDC13): 6 = 4.03 (dd, CH2), 6.75-7.80 (complex, aromatic) Example 10 - Preparation of Compound III, 2-(Diphenyl phosphinomethyl) 2-(diphenylphosphino- methyl )phenyl ]naphthalene Dioxide The dibromide II (15.10 gr, 0.039 mol) was dissolved in toluene (20 mL) in a 100-mL round bottom Flask. A Claisen head, fitted with a short-path distillation head and an addition funnel was attached. The solution of dibromide was heated until toluene began to distill slowly and a solution of methyl diphenylphosphinite (17.56 gr, 0.081 mol) in toluene (23 mL) was added dropwise to the distilling mixture at a rate such that the liquid level in the flask remained approximately constant. After addition was complete, the mixture was heated at reflux an additional 15 minutes. After standing overnight at room temperature, a light brown solid had separated from the solution. The mixture was cooled in an ice bath and then filtered. The solid was washed with cold toluene, followed by diethyl ether to give the dioxide (III) as an off-white powder, 11.12 gr (45 percent). H nmr (CDC13): 6 = 3.17 (br d, CH2), 6.58-7.83 complex, aromatic) 31P nmr (CDCl3): # = -30, -31 ppm ExamPle 11 - Preparation of PHENAP, 2-(Diphenyl phosphinomethyl)-1-[2-(diphenylphosphino methyl)phenyl]naphthalene To a cold (ice bath) mixture of the bisphosphine dioxide (III) (4.00 gr, 6.33 mmol) and triethylamine (3.08 gr, 30.51 mmol) in toluene (50 mL), under nitrogen, was added trichlorosilane (4.14 gr, 30.51 mmol), dropwise by syringe. The mixture was allowed to stir overnight at room temperature, then heated at reflux for 3 hours. The resulting heterogeneous mixture was cooled in an ice bath and 20 percent aqueous potassium hydroxide (60 mL) was added gradually. After stirring about 30 minutes at room temperature, the mixture was transferred to a separatory funnel and the layers were separated. The aqueous layer was washed with toluene (40 mL). The organic layers were combined and washed three times with water (40 mL each). The toluene solution was dried (MgSO4) and filtered. The solvent was then removed under vacuum leaving PHENAP as a glassy, yellow solid, 3.64 gr (96 percent). H nmr (benzene-d6): 6 = 3.42 (br d, CH2), 6.58-7.63 (complex, aromatic) 31P nmr (benzene-d6): b - +9, +12 ppm ExamPle 12 - Preparation of Rhodium 2-Ethylhexanoate Solution in TexanolS Solvent The apparatus consists of a 5-liter three-necked flask equipped with a heating mantle, Teflon bladed mechanical stirrer, reflux condenser, and a thermo- meter. Sodium hydroxide (80 grams) was dissolved in 1,000 ml of water in the flask. 2-Ethylhexanoic acid (196 grams) was added to the flask and dissolved. Rhodium chloride hydrate (46.62 grams containing 20 grams of rhodium metal value) was dissolved in 900 ml of water separately and then added to the stirred sodium 2-ethylhexanoate solution in the Flask. The mixture was heated to 950C and kept vigorously stirred for 1.5 hours. A dark green oil of crude product separated. The mixture was cooled to room temperature and 400 ml of Texanol (2,2,4-trimethyl pentane-1,3diolmonoisobutyrate) solvent was added with stirring. The two phases were separated. The aqueous layer was reextracted with three 400 ml Texanol washes which were combined with the first organic extract. The combined organic phases were washed with 1,000 ml of water. The water wash was combined with the original water wash for rhodium analysis. The combined organic phases were filtered through a 0.5-inch thick bed of celite and made up to 2 liters volume with Texanol that was washed through the celite. The concentration of rhodium in the organic phase was 10,000 ppm and in the combined aqueous phase was 2 ppm. ExamPle 13 - General Bench-Scale Procedure for Low Pressure Hydroformylation of Propylene Using the Invention Catalysts The reactor consists of a vertically held stainless steel 4 foot by 1 inch (inside diameter) tube having a stainless steel filter element welded into its side near the bottom. The bottom of the tube has a drain valve and the top has a side port through which the vaporized products and unreacted gases leave the reactor. The top end of the tube is provided with a screwed plug which can be removed for charging the catalyst and which contains a thermowell whereby the temperature of the catalyst solution (reaction medium) in the reactor is measured accurately. Hydrogen and carbon monoxide are fed to the reactor from cylinders via pressure regulators and flow controllers which use differential pressure cells and air actuated flow control valves to maintain accurate flow. A third feed of nitrogen from a cylinder goes to the reactor via a pressure regulator and rotameter with needle valve. The carbon monoxide passes through a heated commercial "deoxo" unit as marketed by Engelhard Industries, Division, Engelhard Minerals and Chemicals Corp., Newark, N.J., to remove oxygen impurities. The nitrogen admixed with hydrogen pass through a similar "deoxo" unit before entering the reactor. Propylene is fed as a liquid to a preheater section or plenum chamber, where it is vaporized, then combined with the other feed gases prior to entering the reactor via the stainless steel filter element. The propylene feed rate is measured using rate-of-level drop in a tank containing liquid propylene using an armored rotameter with a needle valve to control the liquid propylene feed rate. In operation, the catalyst is contained as a solution in the lower portion of the reactor tube and the reactant gases are sparged up through the solution as bubbles emanating from the filter element. Product butyraldehyde is formed in the catalyst solution where it accumulates and eventually is removed as a vapor by vapor/liquid equilibration with unreacted gases. This type of reactor is known as a vapor take-off or gas sparged reactor. The hot gases are cooled upon leaving the reactor through said side port and the butyraldehyde product, along with some unreacted propylene, collects in a cooled high pressure separator connected by suitable conduit means to said side port. The noncondensed gases are let down to atmospheric pressure via a back pressure regulator which controls the reactor pressure. Additional butyraldehyde is condensed out of the atmospheric pressure gas stream by passing it through a series of three dry ice traps. Once an hour the contents of the high pressure separator and dry ice traps are collected and combined. The weight of butyraldehyde product obtained during the hour and its n/iso ratio are calculated using standard gas/liquid chromatographic techniques in combination with the crude weight of the product collected. In practice, approximately one hour is required for this bench unit to reach steady state production rates where catalyst activity and n/iso product ratio remain substantially constant. Example 14 - Hydroformylation of Propylene with BISBI - Rhodium Catalyst A catalyst charge was prepared using 2,2'-bis (diphenylphosphinomethyl)-l,l"-biphenyl (0.40 gram, 0.729 mmol) and rhodium 2-ethylhexanoate solution in TMPDMI (Texanole) containing 31.25 mg (0.304 mmol) of rhodium as the metal in a total volume of 200 ml of TMPDMI solvent. This preparation was carried out under nitrogen and the catalyst solution charged to the bench unit reactor under argon as described in Example 13. After sealing, the reactor was pressured to 260 psig with hydrogen, carbon monoxide, and nitrogen and heated to 1250C by an external oil bath with said gases purging through the catalyst solution. The gas feed rates at STP were: H2 = CO 2 3.36 liters per minute; and N2 - 0.96 liter per minute. Propylene feed was then started at 1.92 liters per minute as gas at STP. The run was carried out for a total of 5 hours. Reactor catalyst volume was kept at a standard operating level of 223 ml by pumping in TMPDMI solvent if level drop occurred as measured by a liquid level differential pressure cell attached to the reactor. The average butyraldehyde production rate for the last 4 hours of operation was 82.3 grams per hour, equivalent to a catalyst activity of 5.80 pounds of butyraldehyde per gram Rh-hour (lb HBu/g Rh-hr) with a very high n/iso ratio of 25.1/1. ExamPle 15 - Comparison of Propylene Hydroformylation Runs Using Different Organophosphine Ligands in the Presence of Rhodium Table 1 gives data obtained from several runs in the bench unit hydroformylation reactor wherein different organophosphine ligands were used in the presence of rhodium charged as rhodium 2-ethylhexanoate and operated using the same reactor pressure, catalyst volume, and reactant feed rates as described in- Example 16. Table 1 shows the utility of the present ligands, and the exceptional utility of the 2,2'-bis(diphenylphosphinomethyl)-l,l'- biphenyl ligand in producing very high n/iso product ratios in the hydroformylation of propylene. ExamPle 16 - Effect of Hydroformylation Reaction Temperature on Catalyst Activity and n/iso Product Ratios Table 2 shows the effect of reaction temperature on the catalyst activity and butyraldehyde n/iso ratio obtained from a 2.4/1 ligand/rhodium mole ratio of the 2,2'-bis(diphenylphosphinomethyl)-1,l1- biphenyl ligand to rhodium. The reactant feed rates, catalyst volume, and reactor pressure are the same as in Example 16. The data show that the n/iso product ratio increases with lower reaction temperature while the catalyst activity decreases. TABLE 1 Comperison of Different Organophosphine/Rh Catalyst Systems Rh Charge, Ligand Charde, L/Rh Reactor Catalyst Activity, HBu Run No. Ligand mg mmol Mole Ratio Temp. C lb HBu/g Rh-hr M/Iso Ratio 1 BISBI 31.25 0.729 2.4/1 125 5.80 25.1/1 2 BPBMB 31.25 0.458 4.8/1 125 5.10 12.8/1 3 BDBMB 31.25 0.729 2.4/1 125 0.87 3.8/1 4 BIBMB 31.25 0.239 4.1/1 125 1.31 2.00/1 5 TR-DMCB 31.25 0.729 2.4/1 125 5.05 4.36/1 6 TR-DMECB 31.25 0.729 2.4/1 125 4.41 4.23/1 7 TR-DPNOR 31.25 0.729 2.4/1 125 4.07 2.67/1 8 CID-DPNOR 31.25 0.729 2.4/1 125 2.44 0.95/1 9 1,8-DINAP 31.25 0.729 2.4/1 125 0.84 3.56/1 10 FL 31.25 0.729 2.4/1 125 5.00 2.03/1 11 CIS-1, 2DPCH 31.25 0.729 2.4/1 125 5.16 4.02/1 12 DIOP 31.25 0.729 2.4/1 125 1.25 2.45/1 13 1,3-BUT 31.25 0.729 2.4/1 125 0.97 0.84/1 14 1,5-PENT 31.25 0.729 2.4/1 125 2.32 2.28/1 16 1,6-HEX 31.25 0.729 2.4/1 125 4.00 1.51/1 Rh Charge, Ligand Charde, L/Rh Reactor Catalyst Activity, HBu Run No. Ligand mg mmol Mole Ratio Temp. C lb HBu/g Rh-hr M/Iso Ratio 17 O-XYL 31.25 0.729 2.4/1 125 5.80 2.41/1 18 TPP 15.00 18.13 124/1 125 9.41 2.43/1 Above Ligand Identification BISBI = 2,2'-bis(diphenylphosphinomethyl)-1,1'-biphenyl BDBMB = 2,2'-bis(diphenylphosphinomethyl)-1,1'-biphenyl BPBMP = 2,2'-bis(phenylbenzylphosphinomethyl)-1,1'-biphenyl BIBMB = 2,2'-bis(diisobutylphosphinomethyl)-1,1'-biphenyl TR-DMCB = trans-1,2-bis(diphenylphosphinomethyl)-3,3-dimethylcyclobutene TR-DMECB= trans-trans-1,2-bis(diphenylphosphinomethyl)-3-ethoxy-4,4-dimethylcyclobutene TR-DPNOR = trans-2,3-bis(diphenylphosphinomethyl)[2.2.1]bicycloheptane 1,8-DINAP = 1,8-bis(diphenylphosphinomethyl)naphthalene CIS-DPNOR = endo, cis-2,3-bis(diphenylphosphinomethyl)[2.2.1]bicyclohetane FL = 1,1'-bis(diphenylphosphino)ferrocene CIS-1, 2 DPCH = cis-1,2-bis(diphenylphosphinomethyl)cycloghexene DIOP = (-)-2,3-0-isopropylidene-2,3-dihydroxy-1,4-bis(diphenylphosphino)butene 1,4-BUT=1,4-bis(diphenylphosphino)butane 1,3-PROP = 1,3-bis(diphenylphosphino)propane 1,5-PENT = 1,5-bis(diphenylphosphino)pentane 1,6-HEX = 1,6-bis(diphenylphosphino)hexane O-XYL = &alpha;,&alpha; ;'-bis(diphenylphosphino)orthoxylene TPP = triphenylphosphine TABLE 2 Effect of Reaction Temperature of BISBI/Rh Catalyst Rh Charge, Ligand Charge, L/Rh Reactor Catalyst Activity, HBu Run No. mg mmol Mole Ratio Temp. C lb HBu/g Rh-hr N/Iso Ratio 19 31.25 0.729 2.4/1 125 5.80 25.1/1 20 31.25 0.729 2.4/1 115 3.43 27.2/1 21 31.25 0.729 2.4/1 105 2.21 28.7/1 22 31.25 0.729 2.4/1 95 0.86 32.2/1 Example 17 - Hydroformylation of Propylene by Rhodium/ PHENAP Oxo Catalyst at 1050C Using a 3/1 Hydrogen/Carbon Monoxide Mole Ratio and 30 Mole Percent Propylene in the Feed A catalyst solution was prepared by dissolving rhodium (II) 2-ethylhexanoate (containing 33.45 mg of rhodium, 0.325 mmol) in 180 ml of TMPDMI (Texanole) solvent under nitrogen. PHENAP (0.49 gr, 0.813 mmol) was dissolved in toluene (10 ml) under nitrogen. The PHENAP solution was added to the rhodium/TMPDMI solution and mixed under nitrogen until homogeneous. The catalyst solution was charged to a bench-scale continuous gas sparged reactor as described in Example 13 under an argon blanket. The reactor was pressured to 260 psig with hydrogen, carbon monoxide, and nitrogen and heated to 1050C. After reaching 1050C, propylene feed was started and the unit was operated at the feed flows listed below as standard temperature and pressure flow rates. Hydrogen 4.31 Liters/Min Carbon Monoxide 1.44 Liters/Min Propylene 2.88 Liters/Min Nitrogen 0.96 Liter/Min The reactor was run under these conditions for a total of 5 hours with the butyraldehyde product collected, weighed, and analyzed by gas/liquid chromatography hourly. The net weight of butyraldehyde product averaged 100.9 grams per hour in the last 4 hours of operation. The mole ratio of normal butyraldehyde/isobutyraldehyde (n/iso ratio) over this period averaged 54.3/1. The oxo activity of the catalyst is equivalent to 6.65 pounds butyraldehyde per gram Rh-hour. In the following Example 18, several other ligands were used under essentially the same conditions as this Example 17 to hydroformylate propylene. The runs of Examples 17 and 18 are designated (a)-(o) in Table 3 and are compared therein to show the vast improvement in n/iso ratio achieved by the present invention. ExamPle 18 - Hydroformylation of Propylene: Comparison of Ligands For runs (b)-(o), the reactor was maintained at 1250C and 260 psig with the catalyst charges shown in the table. The reactant gases were fed to the reactor at the rates shown below for 5 hours. Hydrogen 3.36 Liters/Min Carbon Monoxide 3.36 Liters/Min Propylene 1.92 Liters/Min Nitrogen 0.96 Liter/Min Butyraldehyde product was collected, weighed, and analyzed as in Example 17. TABLE 3 Comparison of Different Ligan/Rh Catalyst System at 260 psig Rh Charge, Ligand Charge, L/Rh Reactor Catalyst Activity, HBu Run Ligand mg mmol Mole Ratio Temp. C lb HBu/g Rh-hr N/Iso Ratio (a) PHENAP 33.45 0.813 2.5/1 125 6.65 54.3/1 (b) TR-DMCB 31.25 0.729 2.4/1 125 5.05 4.36/1 (c) TR-DMECB 31.25 0.729 2.4/1 125 4.41 4.23/1 (d) TR-DPNOR 31.25 0.729 2.4/1 125 4.07 4.32/1 (e) CIS-DPNOR 31.25 0.729 2.4/1 125 2.44 2.67/1 (f) 1,8-DINAP 31.25 0.729 2.4/1 125 0.84 0.95/1 (g) FL 31.25 0.729 2.4/1 125 5.00 3.56/1 (h) CIS-1, 2DPCH 31.25 0.729 2.4/1 125 1.39 2.03/1 (i) DIOP 31.25 0.729 2.4/1 125 5.16 4.02/1 (j) 1,4-BUT 31.25 0.729 2.4/1 125 1.25 2.45/1 (k) 1,3-PROP 31.25 0.729 2.4/1 125 0.97 0.84/1 (l) 1,5-PENT 31.25 0.729 2.4/1 125 2.32 2.28/1 (m) 1,6-HEX 31.25 0.729 2.4/1 125 4.00 1.51/1 Rh Charge, Ligand Charge, L/Rh Reactor Catalyst Activity, HBu Run Ligand mg mmol Mole Ratio Temp. C lb HBu/g Rh-hr N/Iso Ratio (n) O-XYL 31.25 0.729 2.4/1 125 3.10 2.41/1 (o) TPP 15.00 18.13 124/1 125 9.41 2.43/1 Above Ligand Identifications TR-DMCB = trans-1,2-bis(diphenylphosphinomethyl)-3,3-dimethylcyclobutane TR-DMECB = trans-trans-1,2-bis(diphenylphosphinomethyl)-3-ethoxy-4,4-dimethylcyclobutane TR-DPNOR = trans-2,3-bis(diphenylphosphinomethyl)[2.2.1]bicycloheptane 1,8-DINAP = 1,8-bis(diphenylphosphinomethyl)naphthalene CIS-DPNOR = endo, cis-2,3-bis(diphenylphosphinomethyl)[2.2.1]bicycloheptane FL = 1,1'-bis(diphenylphosphino)ferroce CIS-1,2DPCH = cis-1,2-bis(diphenylphosphinomethyl)cyclohexane DIOP = (-)-2,3-0-isopropylidene-2,3-dihydroxy-1,4-bis(diphenylphosphino)butene 1,4-BUT = 1,4-bis(diphenylphosphino)butane 1,3-PROP = 1,3-bis(diphenylphosphino)propane 1,5-PENT = 1,5-bis(diphenylphosphino)pentane 1,6-HEX = 1,6-bis(diphenylphosphino)hexane O-XYL = &alpha;,&alpha;'-bis(diphenylphosphino)orthoxylene TPP = triphenylphosphine ExamPle 19 - Hydroformylation of Propylene by Rhodium/ NAPHOS Oxo Catalyst at 1050C Using a 3/1 Hydrogen/Carbon Monoxide Mole Ratio and 30 Mol Percent Propylene in the Feed A catalyst solution was prepared by dissolving rhodium (II) 2-ethylhexanoate (containing 33.45 mg of rhodium; 0.325 =ole) in 180 ml of TMPDMI solvent under nitrogen. NAPHOS (0.53 gram; 0.813 =ole) was dissolved in 10 ml of toluene under nitrogen. The NAPHOS solution was added to the rhodium/TMPDMI solution and mixed under nitrogen until homogeneous. The catalyst solution was charged to the bench scale continuous gas-stripped reactor under an argon blanket. The reactor was pressured to 260 psig with hydrogen, carbon monoxide, and nitrogen and heated to 1050C. After reaching 1050C, propylene feed was started and the unit was operated at the feed rates listed below at standard temperature and pressure conditions, in Liters/Minute. Hydrogen 4.31 Liters/Min Carbon Monoxide 1.44 Liters/Min Propylene 2.88 Liters/Min Nitrogen 0.96 Liter/Min The reactor was run under these conditions for a total of 5 hours with the butyraldehyde product collected, weighed, and analyzed by gas/liquid chromatography hourly. The net weight of butyraldehyde product averaged 124.6 grams per hour in the last 4 hours of operation. The mole ratio of normal butyraldehyde/isobutyraldehyde (n/iso ratio) over this period averaged 56.6/1. The oxo activity of the catalyst is equivalent to 8.2 pounds butyraldehyde per gram Rh-hour. In the following Example 20, NAPHOS and several other ligands were used under essentially identical conditions to hydroformylate propylene. The runs are designated (a)-(o) in Table 4 and are given to show the vast improvement in n/Iso ratio achieved by the present invention. ExamPle 20 The catalyst charge from Example 19 employing NAPHOS ligand was left in the reactor under 260 psig of hydrogen and carbon monoxide pressure overnight at room temperature. The reactor was heated to 1250C and run at 260 psig. The reactant gases were fed to the reactor at the rates shown below for 5 hours. Hydrogen 3.36 Liters/Min Carbon Monoxide 3.36 Liters/Min Propylene 1.92 Liters/Min Nitrogen 0.96 Liter/Min Butyraldehyde product was collected, weighed, and analyzed as in Example 19. The net weight of butyraldehyde product averaged 88.9 grams per hour in the last 4 hours of operation with a n/iso ratio of 20.4/1. The oxo activity of the catalyst is equivalent to 5.85 pounds of butyraldehyde per gram Rh-hour. This run is designated (a) in Table 4. Runs (b)-(o) employing different ligands were made at essentially these same reactant feed rates and at the catalyst charges shown in the Table. ExamPle 21 - Hydroformylation of l-Octene by Rhodium/NAPHOS A solution of rhodium (I) dicarbonylacetylacetonate (0.0377 gram; 0.146 =ole), NAPHOS (0.23 gram; 0.35 =ole) and octene-l (31.3 ml, 22.4 grams; 0.2 mole) in toluene (69 ml) was prepared under nitrogen and placed in a nitrogen flushed 300-ml stainless steel autoclave. The autoclave was pressurized to 300 psig with 1/1 H2/CO and heated, with rapid stirring, to 1050C. When the pressure dropped to 250 psig, it was replenished to 300 psig with 1/1, H2/CO. The reaction was maintained at 105 C and 250-300 psig for 2 hours. A total pressure drop of 325 pounds was observed. After cooling to room temperature, the light yellow solution was removed from the autoclave and analyzed by gas chromatography. Results are shown in Table 5 in runs (a)-(j) wherein a variety of other ligands were also used under the same reaction conditions except where the ligandfRh mole ratio is shown to be different. The very large improvement in n/Iso ratio for the product aldehydes as a result of the use of NAPHOS ligand is shown in Table 6, run (j). Example 22 - Hydroformylation of Allyl Alcohol by Rhodium/NAPHOS A solution of rhodium (I) dicarbonylacetylacetonate (0.0377 gram; 0.146 mmole), NAPHOS (0.23 gram; 0.35 mmole) and allyl alcohol (13.6 ml; 11.6 grams; 0.2 mole) in toluene (86 ml) was prepared under nitrogen and placed in a nitrogen flushed 300-ml stainless steel autoclave. The autoclave was pressurized to 125 psig with H2/CO (1/1 molar ratio) and heated, with rapid stirring, to 800C. When the pressure dropped to 75 psig, it was replenished to 125 psig with additional (1/1) H2/CO. The reaction was maintained at 800C and 75-12S psig for 30 minutes. A total pressure drop of 305 pounds was observed. After cooling to room temperature, the light yellow solution was removed from the autoclave and analyzed by gas chromatography. Conversion of allyl alcohol: 98.7 percent. Yields (based on allyl) alcohol): 4-hydroxybutyraldehyde - 81.3 percent, 2-methyl-3-hydroxy- propionaldehyde - 13.0 percent, propionaldehyde 4.4 percent. Ratio of linear oxo aldehyde to branched oxo aldehyde - 6.28/1. TABLE 4 Comparison of Different Ligan/Rh Catalyst System at 260 psig Rh Charge, Ligand Charge, L/Rh Reactor Catalyst Activity, HBu Run Ligand mg mmol Mole Ratio Temp. C lb HBu/g Rh-hr N/Iso Ratio (a) NAPHOS 33.45 0.813 2.5/1 125 5.85 20.4/1 (b) TR-DMCB 31.25 0.729 2.4/1 125 5.05 4.36/1 (c) TR-DMECB 31.25 0.729 2.4/1 125 4.41 4.23/1 (d) TR-DPNOR 31.25 0.729 2.4/1 125 4.07 4.32/1 (e) CIS-DPNOR 31.25 0.729 2.4/1 125 2.44 2.67/1 (f) 1,8-DINAP 31.25 0.729 2.4/1 125 0.84 0.95/1 (g) FL 31.25 0.729 2.4/1 125 5.00 3.56/1 (h) CIS-1, 2DPCH 31.25 0.729 2.4/1 125 1.39 2.03/1 (i) DIOP 31.25 0.729 2.4/1 125 5.16 4.02/1 (j) 1,4-BUT 31.25 0.729 2.4/1 125 1.25 2.45/1 (k) 1,3-PROP 31.25 0.729 2.4/1 125 0.97 0.84/1 (l) 1,5-PENT 31.25 0.729 2.4/1 125 2.32 2.28/1 (m) 1,6-HEX 31.25 0.729 2.4/1 125 4.00 1.51/1 Rh Charge, Ligand Charge, L/Rh Reactor Catalyst Activity, HBu Run Ligand mg mmol Mole Ratio Temp. C lb HBu/g Rh-hr N/Iso Ratio (n) O-XYL 31.25 0.729 2.4/1 125 3.10 2.41/1 (o) TPP 15.00 18.13 124/1 125 9.41 2.43/1 Above Ligand Identifications TR-DMCB = trans-1,2-bis(diphenylphosphinomethyl)-3,3-dimethylcyclobutane TR-DMECB = trans-trans-1,2-bis(diphenylphosphinomethyl)-3-ethoxy-4,4-dimethylcyclobutane TR-DPNOR = trans-2,3-bis(diphenylphosphinomethyl)[2.2.1]bicycloheptane 1,8-DINAP = 1,8-bis(diphenylphosphinomethyl)naphthalene CIS-DPNOR = endo, cis-2,3-bis(diphenylphosphinomethyl)[2.2.1]bicycloheptane FL = 1,1'-bis(diphenylphosphino)ferroce CIS-1,2DPCH = cis-1,2-bis(diphenylphosphinomethyl)cyclohexane DIOP = (-)-2,3-0-isopropylidene-2,3-dihydroxy-1,4-bis(diphenylphosphino)butene 1,4-BUT = 1,4-bis(diphenylphosphino)butane 1,3-PROP = 1,3-bis(diphenylphosphino)propane 1,5-PENT = 1,5-bis(diphenylphosphino)pentane 1,6-HEX = 1,6-bis(diphenylphosphino)hexane O-XYL = &alpha;,&alpha; ;'-bis(diphenylphosphino)orthoxylene TPP = triphenylphosphine TABLE 5 Batch Autoclave Hydroformylations of Octene-1 % % % Yield to C9 L/Rh Conversion Yield to Aldehyde of Run Ligand Ratio Octene-1 Isoocteneb Olefin Fed (a) O-XYL 2.4/1 94.3 3.7 90.6 (b) TR-DMCB 2.4/1 97.1 2.8 94.3 (c) FL 2.4/1 93.6 3.1 90.5 (d) TPP 150/1 98.4 3.5 94.9 (e) DIOP 2.4/1 98.1 4.3 93.8 (f) BDPPa 5/1 99.2 2.9 96.3 (g) 1,4-BUT 2.4/1 95.3 2.7 92.6 (h) 1,5-PENT 2.4/1 98.4 2.6 95.8 (i) 1,3-PROP 2.4/1 67.0 1.9 65.1 (j) NAPHOS 2.4/1 98.1 7.2 90.9 aBDPP - n-Butyldiphenylphosphine. bMixture of octene-2 and octene-3 isomers. TABLE 6 % Isomer Distribution of C9 Aldehyde 2-Methyl 2-Ethyl 2-Propyl N/Branched RUN n-Nonanal octanal heptanal hexanal Aldehyde Ratio (a) 77.64 22.32 0.05 0.00 3.47/1 (b) 87.2 12.74 0.06 0.00 6.81/1 (c) 82.8 17.19 0.05 0.00 4.80/1 (d) 77.2 21.49 0.77 0.04 3.46/1 (e) 85.12 14.70 0.189 0.00 5.72/1 (f) 72.82 25.02 1.99 0.164 2.68/1 (g) 75.16 24.75 0.081 0.00 3.03/1 (h) 73.35 26.14 0.507 0.00 2.75/1 (i) 49.10 50.78 0.115 0.00 0.96/1 (j) 97.11 2.73 0.16 0.00 33.60/1 The invention has been described in detail with particular reference to preferred embodiments thereof, but it will be understood that variations and modifications can be effected within the spirit and scope of the invention.

Claims: Claims 1. A hydroformylation process comprising contacting hydroformylation stock in a reaction zone at a temperature of from about 200C to about 2500C and a pressure of from about 15 psig to about 800 psig with hydrogen, carbon monoxide, and a catalyst comprising rhodium in chemical complex with one or more ligands of the formula EMI45.1 wherein each Ar is independently selected from aromatic ring compounds having 6 up to 14 carbon atoms, e.g., phenyl, naphthyl, phenanthryl and anthracenyl; the x bonds and the y bonds are attached to adjacent carbon atoms on the ring structures; each R, when present as a substituent, is independently selected from alkyl, alkoxy, aryloxy, aryl, aralkyl, alkaryl, alkoxyalkyl, cycloaliphatic, halogen (except C1, Br or I in the ortho position), alkanoyl, alkanoyloxy, alkoxycarbonyl, or form; ; n is a whole number in the range of 0-4 were Ar is phenyl; 0-6 where Ar is naphthyl; and 0-8 where Ar is phenanthryl 6r anthracenyl; each R1 and R2 is independently selected from alkyl, aryl, aralkyl, alkaryl or cycloaliphatic; each R3 and R4 is independently selected from hydrogen and the R1 substituents; each of the above alkyl groups or moieties is straight or branched chain of 1-20 carbons, preferably 1-8 carbons; each aryl group contains 6-10 ring carbons; each cycloaliphatic group contains from 4-8 ring carbons; and each Y is independently selected from the elements N, P, As, Sb and Bi, for a sufficient period of time to permit reaction of said olefin with said carbon monoxide and hydrogen to form aldehyde product. 2. The hydroformylation process according to Claim 1 wherein said ligand has the formula: EMI46.1 wherein: n is,O; each R is independently selected from alkyl, alkoxy, aryloxy, aryl, alkyl, alkaryl, alkoxyalkyl, cycloaliphatic, halogen (except C1, Br or I in the ortho position), alkanoyl, alkanoyloxy, alkoxycarbonyl, or form; each R1 and R2 is independently selected from alkyl, aryl, aralkyl, alkaryl or cycloaliphatic; each R3 and R4 is independently selected from hydrogen and the R1 substituents; wherein each alkyl group or moiety is straight or branched chain of 1-20 carbons, each aryl group contains 6-10 ring carbons, and each cycloaliphatic group contains from 4-8 ring carbons; and each Y is independently selected from the elements N, P, As, Sb and Bi. 3. The hydroformylation process according to Claim 1 wherein said ligand has the formula: EMI47.1 wherein: the x bonds and the y bonds are attached to adjacent carbon atoms on the ring structures; each R when present as a substituent is independently selected from alkyl, alkoxy, aryloxy, aryl, aralkyl, alkaryl, alkoxyalkyl, cycloaliphatic, halogen (except C1, Br or I in the ortho position), alkanoyl, alkanoyloxy, alkoxycarbonyl, or formyl; each R1 and R2 is independently selected from alkyl, aryl, aralkyl, alkaryl or cycloaliphatic; each R3 and R4 is independently selected from hydrogen and the R1 substituents; wherein each of the above alkyl groups or moieties is straight or branched chain of 1-20 carbons, each aryl group contains 6-10 ring carbons, and each cycloaliphatic group contains from 4-8 ring carbons; and each Y is independently selected from the elements N, P, As, Sb and Bi. 4. The hydroformylation process according to Claim 1 wherein said ligand has the formula: EMI48.1 wherein: the x bonds and the y bonds are attached to adjacent.carbon atoms on the ring structures; each R when present as a substituent is independently selected from' alkyl, alkoxy, aryloxy, aryl, aralkyl, alkaryl, alkoxyalkyl, cycloaliphatic, halogen (except C1, Br or I in the ortho position), alkanoyl, alkanoyloxy, alkoxycarbonyl, or formyl; each R1 and R2 is independently selected from alkyl, aryl, aralkyl, alkaryl or cyclo aliphatic; each R3 and R4 is independently selected from hydrogen and the R1 substituents; wherein each of the above alkyl groups or moieties is straight or branched chain of 1-20 carbons, each aryl group contains 6-10 ring carbons, and each cycloaliphatic group contains from 4-8 ring carbons; and each Y is independently selected from the elements N, P, As, Sb and Bi. 5. The process of Claim 1 wherein each said alkyl group or moiety is from 1-8 carbons. 6. The hydroformylation process according to Claim 1 wherein said reaction zone is operated at temperatures between about 800C and 1500C and at pressures between about 100 psig and 400 psig, and the molar ratio of ligand to rhodium is from about 0.5 to about 200. 7. The hydroformylation process according to Claim 6 wherein the molar ratio of said hydrogen to carbon monoxide is at least 0.5, and the total moles of hydrogen and carbon monoxide are present in said reaction zone in the ratio range of from about 0.02 to about 20 with respect to moles of said olefin. 8. The hydroformylation process according to Claim 7 wherein said hydroformylation stock is selected from one or more of ethylene, propy lene, 2methylpropylene, 2-butene, l-butene, 2-methyl-l-butene, l-pentene, l-hexene, l-heptene, l-octene, allyl alcohol, allyl acetate, methyl vinyl ether, ethyl vinyl ether, allyl ethyl ether, vinyl acetate and acrolein diethyl acetal. 9. The hydroformylation process according to Claim 1 wherein said rhodium is present in said reaction zone in an amount between about 1 x 10-6 to about 1 x 10-1 moles per mole of said olefin present in said reaction zone. 10. The process of Claim 2 wherein said ligand is selected from: 2,2'-bis(diphenylphosphino methyl)-1,1'-biphenyl; 2,2'-bis-(dibenzylphos phinomethyl)-l,l'-biphenyl; 2,2'-bis(phenyl benzylphosphinometehyl)-1,1'-biphenyl; 2,2'-bis (diisobutylphosphinomethyl )-l , 1 '-biphenyl; or mixtures thereof. 11. The process of Claim 10 wherein the olefin is propylene. 12. The process of Claim 10 wherein the molar-ratio of ligand to rhodium is from about 2 to about 10. 13. The process of Claim 10 wherein the molar ratio of ligand to rhodium is from about 2.3 to about 4. 14. The process of Claim 1 wherein at steady state hydroformylation conditions in said reaction zone the molar ratio of ligand to Rh is from about 2 to about 5, the ratio of Rh(mg.)/solvent (ml) is from about 0.07 to about 0.28, the ratio of [olefin feed in L(STP)/min]/mg. of Rh is from about 0.03 to about 0.30, the ratio of [CO or H2 feed in L(STP)/min]/mg. of Rh is from about 0.015 to about 1.5, the temperature is main tained at from about 800C to about 1500C and the reactor pressure is maintained at from about 240 psig to about 280 psig. 15. The process of any one of Claims 2-9 or 14 wherein the ligand is 2,2'-bis(diphenyl phosphinomethyl)-l,l'-biphenyl. 16. The process of Claim 3 wherein said ligand has the formula EMI51.1 17. The process of Claim 16 wherein the olefin is propylene. 18. The process of Claim 16 wherein the molar ratio of ligand to rhodium is from about 1 to about 10. 19. The process of Claim 16 wherein the molar ratio of ligand to rhodium is from about 2.3 to about 4. 20. The process of Claim 4 wherein said ligand has the formula EMI52.1 21. The process of Claim 20 wherein the olefin is propylene. 22. The process of Claim 20 wherein the molar ratio of ligand to rhodium is from about 1 to about 10 . 23. The process of Claim 20 wherein the molar ratio of ligand to rhodium is from about 2.3 to about 4. 24. A compound of the formula EMI52.2 useful as a ligand in hydroformylation and other reactions, wherein n is 0-4; each R is independently selected from alkyl, alkoxy, aryloxy, aryl, aralkyl, alkaryl, alkoxyalkyl, cycloaliphatic, halogen (except C1, Br or I in the ortho position), alkanoyl, alkanoyloxy, alkoxycarbonyl, or formyl; each R1 and R2 is independently selected from alkyl, aryl, aralkyl, alkaryl or cyclo aliphatic; each R3 and R4 is independently selected from hydrogen and the R1 substituents; each Y is independently selected from the elements N, P, As, Sb and Bi; and each alkyl group or moiety is straight or branched chain of 1-20 carbons, each aryl group contains 6-10 ring carbons, and each cyclo aliphatic group contains from 4-8 ring carbons. 25. The compound of Claim 24 wherein n is zero, R1 and R2 are alkyl or phenyl, and R3 and R4 are hydrogen or phenyl. 26. The compound of Claim 24 selected from: 2,2'-bis(diphenylphosphinomethyl)-1,1' biphenyl; 2,2 '-bis(dibenzylphosphinomethyl )- l,l'-biphenyl; 2,2'-bis(phenylbenzylphosphino methyl)-l,l'-biphenyl; 2,2'-bis(diisobutyl- phosphinomethyl)-1,1'-biphenyl; and mixtures thereof. 27. The compound of Claim 24 designated 2,2'-bis (diphenylphosphinomethyl)-1,1'-biphenyl. 28. A compound of the formula EMI53.1 wherein: the x bonds and the y bond are attached to adjacent carbon atoms on the ring structures; each R when present as a substituent is independently selected from alkyl, alkoxy, aryloxy, aryl, aralkyl, alkaryl, alkoxyalkyl, cycloaliphatic, halogen (except C1, Br or I in the ortho position), alkanoyl, alkanoyloxy, alkoxycarbonyl, or formyl; each R1 and R2 is independently selected from alkyl, aryl, aralkyl, alkaryl or cycloaliphatic; each R3 andR4 is independently selected from hydrogen and the R1 substituents; each Y is independently selected from the elements N, P, As, Sb and Bi; and each of the alkyl groups or moieties is straight or branched chain of 1-20 carbons, each aryl group contains 6-10 ring carbons, and each cycloaliphatic group contains from 4-8 ring carbons. 29. A compound of Claim 28 wherein each said alkyl group or moiety is from 1-8 carbons. 30. A compound of Claim 28 wherein the rings are unsubstituted, R1 and R2 are alkyl or phenyl, and R3 and R4 are hydrogen or phenyl. 31. A compound of Claim 28 of the structure EMI55.1 32. The catalyst comprising rhodium complexed with: (a) a ligand of the formula EMI55.2 wherein: each Ar is independently selected from aromatic ring compounds having 6 up to 14 carbon atoms, e.g., phenyl, naphthyl, phenanthryl and anthracenyl; the x bonds and the y bonds are attached to adjacent carbon atoms on the ring structures; each R, when present as a substituent, is independently selected from alkyl, alkoxy, aryloxy, aryl, aralkyl, alkaryl, alkoxyalkyl, cycloaliphatic, halogen (except C1, Br or I in the ortho position), alkanoyl, alkanoyloxy, alkoxycarbonyl, or form; n is a whole number in the range of 0-4 were Ar is phenyl; 0-6 where Ar is naphthyl; and 0-8 where Ar is phenanthryl or anthracenyl; each R1 and R2 is independently selected from alkyl, aryl, aralkyl, alkaryl or cyclo aliphatic; each R3 and R4 is independently selected from hydrogen and the R1 substituents; each of the above alkyl groups or moieties is straight or branched chain of 1-20 carbons, preferably 1-8 carbons; each aryl group contains 6-10 ring carbons; each cycloaliphatic group contains from 4-8 ring carbons; and each Y is independently selected from the elements N, P, As, Sb and Bi; in a molar ratio of ligand/Rh of about 1/1; (b) H in an atomic ratio of H/Rh of about 1/1; and (c) carbon monoxide in a molar ratio of CO/Rh of about 2/1. 33. The catalyst according to Claim 32 wherein said ligand has the Formula: EMI56.1 wherein n is 0-4; each R is independently selected from alkyl, alkoxy, aryloxy, aryl, aralkyl, alkaryl, alkoxyalkyl, cycloaliphatic, halogen (except C1, Br or I in the ortho position), alkanoyl, alkanoyloxy, alkoxycarbonyl, or formyl; each R1 and R2 is independently selected from alkyl, aryl, aralkyl, alkaryl or cyclo aliphatic; each R3 and R4 is independently selected from hydrogen and the R1 substituents; each Y is independently selected from the elements N, P, As, Sb and Bi; and each alkyl group or moiety is straight or branched chain of 1-20 carbons, each aryl group contains 6-10 ring carbons, and each cyclo aliphatic group contains from 4-8 ring carbons. 34. The catalyst according to Claim 33 wherein the ligand is selected from: 2,2'-bis(diphenyl phosphinomethyl)-l,l'-biphenyl; 2,2 '-bis- (dibenzylphosphinomethyl)-l,l '-biphenyl; 2,2' bis(phenylbenzylphosphinomethyl)-l,l'-biphenyl; 2,2'-bis(diisobutylphosphinomethyl)-1 , 1 '-biphenyl; and mixtures thereof. 35. The catalyst according to Claim 32 wherein said ligand has the formula: EMI57.1 wherein: the x bonds and the y bonds are attached to adjacent carbon atoms on the ring structures; each R when present as a substituent is independently selected from alkyl, alkoxy, aryloxy, aryl, aralkyl, alkaryl, alkoxyalkyl, cycloaliphatic, halogen (except C1, Br or I in the ortho position), alkanoyl, alkanoyloxy, alkoxycarbonyl, or formyl; each R1 and R2 is independently selected from alkyl, aryl, aralkyl, alkaryl or cyclo aliphatic; each R3 and R4 is independently selected from hydrogen and the R1 substituents; wherein each of the above alkyl groups or moieties is straight or branched chain of 1-20 carbons, each aryl group contains 6-10 ring carbons, and each cycloaliphatic group contains from 4-8 ring carbons; and each Y is independently selected from the elements N, P, As, Sb and Bi. 36. The catalyst according to Claim 35 wherein the ligand has the structure EMI58.1

Inventors: DEVON THOMAS JAMES, PHILLIPS GERALD WAYNE, PUCKETTE THOMAS ALLEN, STAVINOHA JEROME LEONARD JR, VANDERBILT JEFFREY JAMES, DEVON, THOMAS, JAMES, PHILLIPS, GERALD, WAYNE, PUCKETTE, THOMAS, ALLEN, STAVINOHA, JEROME, LEONARD, JR., VANDERBILT, JEFFREY, JAMES
Applicants: EASTMAN KODAK CO, EASTMAN KODAK COMPANY
Application year: 1987
Main classification: C07C47
IPC codes: B01J31, C07B61, C07C45, C07C47, C07C67, C07F9, C07F15