A PROCESS FOR ENHANCING THE RESISTANCE OF A RESIST IMAGE TO REACTIVE ION ETCHING AND TO THERMAL FLOW

Abstract: The reactive ion etching and thermal flow resistance of a resist image is enhanced by contacting the resist image with an alkyl metal compound of magnesium or aluminium.

Description: The present invention is concerned with a process for enhancing the resistance of a resist image to reactive ion etching and to thermal flow. In the manufacture of microcircuits, it is often desired to have resist images which are resistant to thermal flow and which are also resistant to reactive ion etching. In the past, a large amount of research has been done to achieve either or both of these objectives. Some such work is disclosed, for example, in U.S. -A- 4,201,800, U.S. -A- 4,230,781, U.S. -A-4,259,421 and U.S. -A- 4,439,516. See also CHEMICAL ABSTRACTS, Vol. 96:152832t and CHEMICAL ABSTRACTS, Vol. 97:153930f, both 1982. The previously proposed methods have obtained some success but they still leave much to be desired, particularly in the area of simultaneously enhancing both the resistance to reactive ion etching and to thermal flow. The previous proposals also have not been very successful in the treatment of thick resists, particularly bilayer resists. The present invention provides a process for increasing the reactive ion etching and thermal flow resistance of a resist image, the process being characterised by contacting the resist image after it has been developed with an alkyl metal compound of magnesium or aluminium, the resist comprising a polymer which has a group which reacts with the alkyl metal compound to undergo metallization or salt formation. The process of the present invention is broadly applicable to resist images, particularly including photoresist images. It is applicable to many types of resists, including, for example phenolic resins, novolac resins, poly(para-hydroxy styrene), poly(methyl methacrylate) and other acrylate esters, and also copolymers. The alkyl metal compounds suitable for use in practising the present invention include dialkyl-magnesium compounds and trialkyl-aluminium compounds, and also other compounds wherein at least one alkyl group is linked to the metal. Examples of these include triethyl aluminium, diisobutyl aluminium hydride, diethoxyethyl aluminium, lithium diisobutyl aluminium hydride, diethyl magnesium and Grignard reagents. In the operation of the process of the present invention, the resist should comprise a polymer which has a group which reacts with the alkyl metal compound to undergo metallation or salt formation. The actual contacting of the resist image with the alkyl metal compound may be carried out simply by dissolving the metal alkyl compound in a solvent and dipping the resist image in the solution. Alternatively, the contacting may also be carried out by contacting the resist image with the vapour of the alkyl metal compound. By application of a process embodying the present invention, thermal flow resistance, at least up to 250 degrees C, is obtained without any reticulation in large surface areas, such as is often found in previously known methods of treatment. As a result of application of the present invention, a resist image is given increased resistance to reactive ion etching when the etching is carried out using any halogen-containing gases, such as CF₄, SF₆ and CCl₂F₂, and also oxygen as well. The resist images can be removed in N-methyl-2-pyrrolidinone after these reactive ion etching treatments. It should be emphasised that practice of the process of the present invention results in incorporating magnesium or aluminium deeply inside the resist image, i.e., about 1 µm, as measured from ESCA depth profile and Argon sputtering rates. This deep incorporation of metals permits the use of bilayer resists and is one of the unexpected advantages of the present invention. The following examples are given solely for purposes of illustration and should not be considered as limitations on the present invention, many variations of which will occur to those skilled in the art. Dialkyl-Magnesium: Dibutyl-magnesium solution (0.7M in heptane) and diethyl-magnesium solution (0.7M in ether) were used. Dibutyl-Magnesium Treatment: Images from two types of commercial diazonaphthoquinone novolac matrix resists, with thicknesses of 3.2 µm and 3.7 µm respectively, on silicon wafers were dipped into the magnesium solution either for 15 sec or 50 sec, then, immediately into toluene for rinsing. Afterwards, toluene was flushed away with a nitrogen stream. The whole process was carried out in a nitrogen atmosphere. The incorporation of magnesium into the resist films was confirmed with ESCA measurements. Halogen-Based RIE Measurements: As halogen-containing gases, pure SF₆ and an 1:1 argon/dichlorodifluoromethane mixture were used. The 15-sec treatment provided 13 times enhancement in SF₆ RIE resistance for the diazonapthoquinone-novolac resist. A similar result was obtained with dichlorodifluoromethane RIE; here, the thickness loss of the magnesium-treated resist films was so small that the enhancement ratio was difficult to assess. Thermal Flow Resistance: Resist images were treated exactly in the same way as described above. For comparison purpose, uv-hardened images were heated side-by-side with a non-treated sample on a hot plate having a surface temperature of 175 degrees C. The untreated sample deformed badly at 175 degrees C. The uv-bonded sample, and also the sample treated by a process embodying the present invention, showed no deformation at 250 degrees C. Trialkyl Aluminium Treatments: Solution: The solution treatment of resist images was carried out by dipping a wafer with resist images into a hexane solution of triethyl aluminium (1.0 M solution) for 1 to 4 min at room temperature, followed immediately by rinsing with toluene/heptane, and by nitrogen blowing. The treatment was done in a nitrogen atmosphere. After the nitrogen blowing, the wafer was processed in air. Vapour Phase: For the vapour-phase treatment a wafer with resist images was placed in a vessel with a rubber septum for an injection of trimethyl aluminium. Then, the vessel was evacuated by a mechanical pump to 6.65 Pa (50 micron) pressure, followed by an injection of trimethyl aluminium solution (1 ml of 1 M hexane solution per 500 ml volume). The wafer was kept inside the vessel for one hour at room temperature. Unreacted trimethyl aluminium and hexane were blown off in a nitrogen stream. Argon Sputtering: Argon Ion Sputtering Rates and Depth Profiles: Depth profiles of these metal atoms in resist films were measured with ESCA and argon ion sputtering, while at the same time the sputtering rate was measured with an Alpha Step 200 thickness measurement instrument. Argon sputtering was carried out in a Plasma Therm diode system under following conditions: incident power of 0.24 Watts per sq cm, -220 V bias potential, 20 sccm, 9.58 Pa (72 mTorr), 25 C aluminium substrate surrounded by a poly(methyl methacrylate) ring.

Claims: A process for increasing the reactive ion etching and thermal flow resistance of a resist image, the process being characterised by contacting the resist image after it has been developed with an alkyl metal compound of magnesium or aluminium, the resist comprising a polymer which has a group which reacts with the alk yl metal compound to undergo metallization or salt formation. A process as claimed in claim 1 wherein the resist is a photoresist. A process as claimed in claim 1 or claim 2, wherein the resist is a phenolic resin. A process as claimed in claim 1 or claim 2, wherein the resist is a novolac resist. A process as claimed in claim 1 or wherein the resist is in a bilayer resist. A process as claimed in any preceding claim, wherein the alkyl metal compound is a dialkyl-magnesium compound. A process as claimed in any of claims 1 to 5, wherein the alkyl metal compound is a trialkyl-aluminium compound. A process as claimed in any preceding claim, which the contacting is carried out with the alkyl metal compound in a solution. A process as claimed in any of claims 1 to 7, in which the contacting is carried out with the alkyl metal compound in the vapour state.

Inventors: HIRAOKA, HIROYUKI, LABADIE, JEFFREY WILLIAM, LEE, JAMES HSI-TANG, MACDONALD, SCOTT ARTHUR, WILLSON, CARLTON GRANT
Applicants: INTERNATIONAL BUSINESS MACHINES CORPORATION
Application year: 1987
Main classification: G03F7
IPC codes: G03F7, H01L21