POLYOLEFIN COMPOSITIONS FOR USE WITH HOT WATER SYSTEMS

Abstract: An olefin polymer composition having improved resist­ ance to deterioration in the presence of chlorinated and non-­ chlorinated water and having improved resistance to tempera­ tures in the range of 0°C to 110°C consisting of a blend of: (a) 93 to 99.5 percent by weight of an isotactic polymer of an alpha olefin having 2-6 carbon atoms; (b) 0.05 to 0.50 percent by weight of a hindered amine U.V. stabilizer; (c) 0.05 to 1.1 by weight of a hindered phenolic thermal stabilizer having a molecular weight above 530; (d) 0 to 0.5 percent by weight of a nucleating agent; (e) 0 to 4 percent by weight of a pigment; and (f) 0 to 3.0 percent by weight of a filler.

Description: The present invention relates to an improved polymeric composition resistant to ultraviolet light deterioration and useful in chlorinated and non-chlorinated, potable and non-potable water systems wherein the water temperatures can range from 0°C to 110°C. Olefin polymer compositions, particularly butene-1 polymer compositions, have been used for many applications. It has been found that for many end uses it is essential to combine the polymer with antioxidants and ultraviolet (UV) stabilizers in order to develop a resin composition capable of withstanding a variety of conditions, such as heat, oxygen, UV radiation, chlorinated water, or water with a temperature higher than room temperature. US-A-4576983 discloses polymer compositions for use with hot water systems comprising a butene-1 homopolymer, sterically hindered phenolic antioxidant, lauryl-stearyl thiodipropionate, nucleating agent, mineral filler coated with acid acceptor and pigment. Plastics and Rubber Processing and Applications, vol. 5, No. 3, 1985, pages 259-265 describes the interactions between antioxidants, including hindered phenols, and hindered piperidine compounds (as light stabilisers) in the thermal and photochemical oxidation of propylene film. A polymer composition has long been needed which is resistant to deterioration when exposed to hot oxygenated water having a temperature of 23°C to 110°C, chlorinated water, and UV radiation. The present invention with an unusual blend of components meets this need and is a significant improvement in the art. The present invention relates to an olefin polymer composition having improved resistance to deterioration when exposed to hot oxygenated water with a temperature of 0°C to 110°C, chlorinated water, and UV radiation. More specifically, the present invention relates to an olefin polymer composition consisting of a blend of: (a) 93 to 99.5, preferably 95.5 to 99.5, percent by weight of an isotactic butene-1 homopolymer or copolymer; (b) 0.05 to 0.50, preferably 0.10 to 0.40, especially 0.15 to 0.3, percent by weight of a hindered amine U.V. stabilizer of formula wherein R₁ is an alkyl group of 1 to 18 carbon atoms, R₂ is an alkyl group of 1 to 8 carbon atoms, m is an integer from 0 to 30, and n is an integer from 1 to 40; (c) 0.05 to 1.1, preferably 0.10 to 0.90, especially 0.4 to 0.75, percent by weight of at least one hindered phenolic thermal stabilizer having a molecular weight above 530; (d) up to 0.5, preferably 0.05 to 0.4, especially 0.1 to 0.2, percent by weight of a nucleating agent; (e) up to 4, preferably 0 to 3, especially 0.2 to 2, percent by weight of a pigment; and (f) up to 3.0, preferably 0 to 2, especially 0.5 to 1.5, percent by weight of a filler. The invention also relates to pipes for carrying water, including hot water at temperatures up to 40°C, fabricated from the olefin polymer composition. The hindered phenolic thermal stabilizer (c) is preferably selected from 1,3,5-trimethyl-2,4,6-tris (3,5-di-tert-butyl-4-hydroxy-benzyl) benzene, octadecyl 3,5-di-tert-butyl-4-hydroxyhydrocinnamate, tetrakis [methylene(3,5-di-tert-butyl-4-hydroxy-hydrocinnamate)] methane, 1,3,5-tris(4-tert-butyl-3-hydroxy-2,6-dimethylbenzyl)-1,3,5-triazine-2,4,6-(1H,3H,5H)-trione, bis-[3,3-bis(4'hydroxy-3'tert.butyl-phenyl)-butanoic acid]-glycolester and tris(3,5-di-t-butyl-4-hydroxybenzyl) isocyanurate. The hindered amine (b) is preferably a polymer of N,N'-bis(2,2,6,6-tetramethyl-4-piperidinyl)-1,6-hexane diamine, 2,4,6-trichloro-1,3,5-triazine and 2,4,4-trimethyl-1,2-pentanamine. The nucleating agent (d) is preferably a polyethylene, especially a high density polyethylene. The pigment (e) is preferably at least one of carbon black, iron oxide yellow and titanium dioxide, especially a mixture of carbon black and titanium dioxide. The filler (f) preferably is a magnesium silicate, especially talc, coated with a metal stearate. This invention is directed to the combination of the ingredients and the particular use of the hindered amine light stabilizer as a thermal stabilizer in the blend. A significant aspect of the present invention is the synergism which results from combining the butene-1 polymer with a particular hindered amine, at least one phenolic thermal stabilizer having a molecular weight over 530, and a nucleating agent, such as high density polyethylene, a pigment and a filler as described. The resulting overall polymeric composition has an excellent balance of properties not available in prior art formulations. The polymeric composition of the invention is formulated from an isotactic butene-1 homopolymer or copolymer. The polymer is preferably a crystallizable thermoplastic butene-1 polymer with a number average molecular weight above 15,000, preferably above 20,000, and an isotactic content above 85%, preferably above 90%, and most preferably above 95%, as determined by conventional methods. Suitable isotactic butene-1 homopolymers and copolymers are commercially available from the Shell Oil Company and methods for their preparation are well known in the art (see US-A-3,362,940). Illustrative of butene-1 polymers suitable for use in the present invention are those known in the industry as pipe grades. Particularly preferred are Shell butene-1 homopolymers. Suitable hindered amine ultraviolet (U.V.) stabilizers are disclosed in Japanese Patent No. Sho 60[1985]-124642 and in Japanese Patent No. Sho 60[1985]-130635 and are of the formula given above. A particular hindered amine which can be used within the scope of this invention is a polymer of N,N'-bis(2,2,6,6-tetramethyl-4-piperidinyl)-1,6-hexane diamine, 2,4,6-trichloro-1,3,5-triazine and 2,4,4-trimethyl-2-pentane diamine. The most preferred hindered amine for use is that wherein R₁ represents a methyl group, R₂ represents the 2,4,4-trimethyl-2-pentyl group, n is an integer of at least 4, and m is the integer 6. This preferred hindered amine is commercially known as "Chimassorb" (Registered Trade Mark) 944, and is available from Ciba-Geigy Corporation. Chimassorb is usually used as a light stabilizer. However, in this context, the Chimassorb is being used as a thermal stabilizer. A hindered phenolic stabilizer/antioxidant is used herein. Numerous hindered phenolic stabilizers which would work in the present inventive blend are described in JP-A-59[1984]-221344. Particular high molecular weight hindered phenolic stabilizers which work well within the scope of the present invention include "Ethanox" (Registered Trade Mark) 330 which is 1,3,5-trimethyl-2,4,6-tris (3,5-di-tert-butyl-4-hydroxy-benzyl) benzene, "Irganox" (Registered Trade Mark) 1076 which is octadecyl 3,5-di-tert-butyl-4-hydroxyhydrocinnamate, "Irganox" 1010 which is tetrakis [methylene(3,5-di-tert-butyl-4-hydroxy-hydro-cinnamate)]methane, "Cyanox" (Registered Trade Mark) 1790 which is 1,3,5-tris(4-tert-butyl-3-hydroxy-2,6-dimethylbenzyl)-1,3,5-triazine-2,4,6-(1H,3H,5H)-trione, "Hostanox" (Registered Trade Mark) 03 which is bis-[3,3-bi (4'hydroxy-3'tert.butyl-phenyl)-butanoic acid]-glycolester, and "Goodrite" (Registered Trade Mark) 3114 which is tris(3,5-di-t-butyl-4-hydroxy-benzyl)isocyanurate; "Ethanox" 330 (molecular weight 775) is available from the Ethyl Corporation, "Irganox" 1076 (molecular weight 531) and "Irganox 1010 (molecular weight 1178) are available from Ciba-Geigy Corporation. "Cyanox" 1790 (molecular weight 700) is available from American Cyanamid Corporation. "Hostanox" 03 (molecular weight 790) is available from American Hoechst Corporation and "Goodrite" 3114 (molecular weight 785) now known as "Irganox" 3114 is currently available from Ciba-Geigy Corporation. The nucleating agent useful within the scope of the present invention can be a member of the group consisting of: high density polyethylene, graphitic non-turbostatic carbon; fatty acid amides; anthraquinones; and amides. A variety of preferred nucleating agents, preferred pigments and preferred fillers, contemplated for use in this invention are detailed in US-A-4,576,983 which is assigned to the same company as the present invention. Other nucleating agents contemplated for use in this invention include graphitic non-turbostatic carbon nucleating agents, disclosed in US-A-4,321,334 (having common assignee) and fatty acid amide nucleating agents disclosed in US-A-4,322,503 (having common assignee). These fatty acid amides include N,N'ethylene-bis-stearamide. Specific anthraquinones include 1,2-dihydroxy-9,10-anthraquinone; 1,4-dihydroxy-9, 10-anthraquinone; 1,5-dihydroxy-9,10-anthraquinone; 12,5,8-tetrahydroxy-9-10-anthraquinone; 9,10-anthraquinone; and sodium 2-anthraquinone sulfonate. Other amide nucleating agents are disclosed in US-A-4,320,209 (having common assignee). Preferred amides include 1-naphthalene acetamide; N-stearoyl-p-aminophenol; mercapto-N-2-naphthyl-acetamide; malonamide; nicotinamide; isonicotinamide; and 1,8-naphthalimide. The most preferred nucleating agent is high density polyethylene. The high density polyethylene (HDPE) employed in the composition of this invention is characterized by a density above 0.93 g/cm³ and preferably at least 0.95 g/cm³. An HDPE with a melt index of from 0.1 to 20, as measured by ASTM D1238, Condition E, is typically employed; HDPE of higher melt index may also be suitable. The melt index and molecular weight of HDPE are inversely related; the corresponding molecular weight for a polymer with a given melt index may be readily determined by routine experimentation. A particularly suitable HDPE, for example, has a melt index of 0.45 g/10 min., a weight average molecular weight of about 166,000 and a density of 0.950 grams/cm³. A high density polyethylene with a viscosity at mixing temperatures approximating that of the butene-1-homopolymer facilitates intimate mixing in conventional extrusion compounding equipment. A wide variety of suitable high density polyethylenes are commercially available and methods for their preparation are well known in the art. They may be prepared by polymerization processes employing Ziegler-type coordination catalysts or supported chromium oxide catalysts. Commercially available HDPE of either type is suitable. The filler component employed in this invention is preferably a coated mineral filler, in particular a magnesium silicate coated with an acid acceptor. The preferred magnesium silicate is talc. The acid acceptors which are coated on the mineral filler are preferably stearates of weak bases, such as alkaline earth metal stearates. A preferred acid acceptor is zinc stearate. Accordingly, the preferred filler component is zinc stearate-coated talc. Such materials are well known, commercially available fillers. In addition to adding certain strength properties to the composition of the invention, the particular fillers employed herein also unexpectedly improve the long term stability of the blends. Pigments are added as desired to achieve a particular color for the resin. Typical pigments useful within the scope of the invention include carbon black, titanium dioxide and iron oxide. The relative amounts of each of the various ingredients in the polymeric composition of the present invention are listed below in percent by weight (the total for a particular composition adding up to 100 percent): COMPONENT EX1 EX2 EX3 butene-1 homopolymer, or copolymer 93-99.5 93-99.5 95-99.5 hindered amine 0.05-0.5 0.10-0.4 0.15-0.3 at least one hindered phenolic stabilizer 0.05-1.1 0.05-0.9 0.05-0.75 nucleating agent 0-0.5 0.05-0.4 0.1-0.2 pigment 0-4 0.0-3 0.0-2 filler 0-3 0-2 0.5-1.5 The relative amounts of the hindered amine and hindered phenolic component are significant to stabilize the resulting composition, that is, to provide both heat resistance to temperatures from 0°C to 110°C, and more preferably from 23°C to 100°C, U.V. resistance, chlorine resistance and processing stability due to the synergistic effects of these interacting components. In the preferred embodiment, the various ingredients are blended or intimately mixed in an intensive mixing device, such as a C.W. Brabender Mixer/Measuring Head or a Banbury-type mixer. The resulting blends have particular utility for carrying pressurized hot water in view of the long-term pressure capability of the resin and improved resistance to a loss of polymer properties resulting from heat, oxygenated hot water, aqueous chlorine destabilization and ultraviolet radiation. An importnt feature for a water carrying polymer is that the combination of ingredients that is used must not leach into the water supply. The combination chosen here is very resistant to leaching particularly in the presence of aqueous chlorine and hot water. The invention is further illustrated by reference to the following Example, which is given for the purpose of illustration. EXAMPLE In this Example, eight formulations F1 to F8 were prepared using the following combinations of ingredients in percent by weight: COMPONENT F1 F2 F3 F4 F5 F6 F7 F8 PB (BR-200) 99.03 98.73 98.73 99.03 98.73 96.328 96.328 96.328 Chimassorb 944 0.15 0.25 0.40 0.15 0.23 0.30 0.30 0.30 Ethanox 330 0.30 0.40 0.25 0.30 0.40 0.20 -- -- Irganox 1076 0.15 0.25 0.25 -- -- -- 0.20 -- Irganox 1010 -- -- -- 0.15 0.25 -- -- 0.20 High density polyethylene 0.10 0.10 0.10 0.10 0.10 0.20 0.20 0.20 Titanium dioxide 0:25 0.25 0.25 0.25 0.25 1.70 1.70 1.70 Carbon black 0.008 0.008 0.008 0.008 0.008 0.06 0.06 0.06 Zinc oxide 0.012 0.012 0.012 0.012 0.012 0.012 0.012 0.012 ZSC talc -- -- -- -- -- 1.20 1.20 1.20 The various formulations were prepared by mixing the ingredients in a Brabender-type mixing head at 210°C at 60 RPM for five minutes under nitrogen purge in order to avoid oxidative degradation. Each resin was then compression-molded into 1.5 mm (60 mil) thick plaque. After transformation in at least 10 days to a stable hexagonal crystal form I of polybutylene (PB), the plaques were tested. Water oxidation tests were performed in a stainless steel cylinder that was filled with tap water 2.54 cm (one inch) from the top. The samples were inserted into the cylinder which was then sealed. The temperature of the cylinder was brought up to operation temperature by a silicone oil bath (the cylinder sits in the oil bath). As the cylinder temperature was increasing to the set temperature, 100 cc/min of oxygen was bubbled through the test water at a pressure of 25 psig. When the cylinder reached the set temperature the oxygen was bubbled for three hours at a rate of 300 cc/min. This brought the dissolved oxygen content of the hot water to the desired level for testing. After the three hours the flow of oxygen was turned off and a 170 kPa gauge (25 psig) head pressure was maintained. The samples were visually inspected once a week for signs of plaque failure. The text results follow: EFFECT OF HOT WATER AGING (110°C WITH 25 ppm 0₂) OF 1.5 mm PLAQUES ON THE LIFETIME OF EIGHT EXPERIMENTAL PB RESIN FORMULATIONS SHOWN ABOVE Formulation F1 F2 F3 F4 F5 F6 F7 F8 Days to Fail 53 66 66 40 40 40 32 19 These results show that formulations in accordance with the invention are capable of withstanding hot oxygenated water for prolonged periods. Particularly impressive results are obtained with the formulations that contain Chimassorb 944, Ethanox 330 and Irganox 1076 (F1 to F3). In addition formulations prepared in accordance with the invention show improved chlorine resistance, improved UV resistance, and reduced extraction of stabilizers upon prolonged exposure to hot water (110°C) as compared with prior art formulations.

Claims: An olefin polymer composition consisting of a blend of: (a) 93 to 99.5 percent by weight of an isotactic butene-1 homopolymer or copolymer; (b) 0.05 to 0.50 percent by weight of a hindered amine U.V. stabiliser of formula; where R₁ is an alkyl group of 1 to 18 carbon atoms, R₂ is an alkyl group of 1 to 8 carbon atoms, m is an integer from 0 to 30, and n is an integer from 1 to 40; (c) 0.05 to 1.1 percent by weight of at least one hindered phenolic thermal stabiliser having a molecular weight above 530; (d) up to 0.5 percent by weight of a nucleating agent; (e) up to 4 percent by weight of a pigment; and (f) up to 3.0 percent by weight of a filler. A composition according to claim 1 wherein the relative amounts of each component are: (a) 95.5 to 99.5 percent by weight; (b) 0.10 to 0.40 percent by weight; (c) 0.10 to 0.90 percent by weight; (d) 0.05 to 0.4 percent by weight; (e) 0 to 3 percent by weight; and (f) 0 to 2 percent by weight. A composition according to claim 2 wherein the relative amounts of each component are: (a) 95.5 to 99.5 percent by weight; (b) 0.15 to 0.3 percent by weight; (c) 0.4 to 0.75 percent by weight; (d) 0.1 to 0.2 percent by weight; (e) 0.2 to 2 percent by weight; (f) 0.5 to 1.5 percent by weight. A composition according to any one of the preceding claims wherein (b) is a polymer of N,N'-bis(2,2,6,6-tetramethyl -4-piperidinyl)-1,6-hexane diamine, 2,4,6-trichloro-1,3,5-triazine and 2,4,4-trimethyl-2-pentanamine. A composition according to any one of the preceding claims wherein (c) is at least one of 1,3,5-trimethyl-2,4,6-tris(3,5-di-tert-butyl-4-hydroxybenzyl) benzene, octadecyl 3,5-di-tert-butyl-4-hydroxyhydrocinnamate, tetrakis [methylene (3,5-di-tert-butyl-4-hydroxy-hydrocinnamate)] methane, 1,3,5-tris(4-tert-butyl-3-hydroxy-2,6-dimethylbenzyl)-1,3,5-triazine-2,4,6-(1H,3H,5H)-trione, bis-[3,3-bis(4'hydroxy-3'tert.butyl-phenyl)-butanoic acid]-glycolester and tris(3,5-di-t-butyl-4-hydroxybenzyl) isocyanurate. A composition according to any one of the preceding claims wherein (d) is a high density polyethylene. A composition according to any one of the preceding claims wherein (e) is at least one of carbon black, iron oxide yellow and titanium dioxide. A composition according to any one of the preceding claims wherein (f) comprises a magnesium silicate coated with a metal stearate. A composition according to claim 8 wherein (f) is talc coated with zinc stearate. Pipes for carrying water fabricated from a composition as claimed in any one of the preceding claims.

Inventors: HAYDEN, EARL E.
Applicants: MITSUI PETROCHEMICAL INDUSTRIES, LTD., SHELL OIL COMPANY
Application year: 1987
Main classification: C08L23
IPC codes: C08K5, C08L23, C08L21, C08L101, C08L7