DEACTIVATION OF PHOSPHONIUM SALT CATALYST

Abstract: A process for deactivating a hydrocarbyl phosphonium salt catalyst in an epoxy resin fusion reaction by contacting with a sulphonic acid, such as p-toluenesulphonic acid or methane sulphonic acid. The process is particularly suited for deactivation of moisture-resistant phosphonium salts such as methylene bis(triphenyl phosphonium halide)s.

Description: This invention relates to deactivation of phosphonium salt catalysts. In a further aspect, the invention relates to terminating an epoxy fusion reaction in which a polyepoxide is reacted with a phenol or other acidic compound in the presence of a phosphonium salt catalyst. It is known e.g. from U.S. patent No. 3,006,891 to prepare epoxy resins by reacting a compound having a 1,2-epoxy group, such as epichlorohydrin, with bisphenol-A in the presence of sodium hydroxide. To prepare linear, high molecular weight epoxy resins, it is common practice to first prepare an epoxy resin having a relatively low epoxy equivalent weight and then react it, in the presence of a catalytic amount of a hydrocarbyl phosphonium halide, with a compound containing phenolic hydroxyl groups. The use of phosphonium halide catalysts for such an epoxy "fusion" or "advancement" reaction results in the formation of linear, high molecular weight epoxy resin. In order to control the molecular weight of this epoxy resin reaction product, it is necessary that the catalyst be deactivated at the desired phase of the reaction. How readily the fusion catalyst is deactivated depends upon the particular catalyst and the conditions under which the reaction is being carried out. For example in the process disclosed in U.S. patent No. 4,438,254, certain phosphonium halide catalysts are applied such as ethyl triphenyl phosphonium iodide, which are subject to attack by hydroxyl ions. Thus, performing the advancement reaction in a reaction mixture which contains water results in deactivation of the catalyst as the reaction proceeds. This rather slow catalyst deactivation can be used to advantage to control the speed of the advancement reaction, preventing too-rapid reaction as the desired molecular weight is approached. Other phosphonium halide deactivating agents mentioned in U.S. patent No. 4,438,254 for deactivating the phosphorium halide catalysts applied in the claimed process are for instance aldehydes, ketones, sulfoxides and sulfones. International patent application No. WO-A-86/01213 discloses a process for deactivating a lithium or cesium catalyst in the presence of ethyltriphenylphosphoniumacetate-acetic acid complex by contacting the catalyst with a sulphonic acid deactivator such as p-toluol-sulphonic acid. The deactivator is used in excess with respect to the Li or Cs compound and thus will also deactivate the ethyltriphenylphosphoniumacetate-acetic acid complex. By contrast, certain hydrocarbyl phosphonium salt advancement catalysts are very stable to hydroxyl ion attack. Such stable catalysts, such as methylene bis(triphenyl phosphonium bromide), for example, are not deactivated to an appreciable extent by residual water in the reaction mixture. If the reactivity of the catalyst is not controlled, the molecular weight of the fusion product will continue to increase. This can result in difficulty controlling the properties of the fusion resin and changes in properties during storage of the resin. It would thus be desirable to provide a means whereby those hydrocarbyl phosphonium salt fusion catalysts which are highly resistant to hydroxyl ions, can be deactivated in the epoxy fusion reaction medium at the desired point of the fusion process. According to the invention, a hydrocarbyl phosphonium salt catalyst represented by the formula I, wherein each R is independently selected from a hydrocarbyl or inertly substituted hydrocarbyl group and X is a compatible anion is deactivated by contacting the catalyst with a sulphonic acid. The contacting can take place in an epoxy resin fusion reaction mixture in which an epoxide is reacted with an acidic hydroxyl group-containing compound in the presence of a catalytic amount of a hydrocarbyl phosphonium salt of the above formula I, to produce a high molecular weight epoxy resin fusion product. The deactivating agent is preferably a substituted or unsubstituted hydrocarbyl sulphonic acid, such as p-toluene-sulphonic acid. The catalyst deactivating agents useful in the invention catalyst deactivation method include compounds which can be described by the formula R-SO₃H, in which R is a substituted or unsubstituted hydrocarbyl moiety. R can be aliphatic or aromatic, monomeric or polymeric. R will generally be substituted or unsubstituted C₁-C₈ aliphatic or C₆-C₂₀ aromatic. Examples of R-SO₃H catalyst deactivation agents include toluene sulphonic acid, methane sulphonic acid, dodecylbenzene sulphonic acid, trifluoromethane sulphonic acid, and benzene sulphonic acid. The catalyst deactivating agent will generally be added as a solution, preferably an aqueous solution, having a sulphonic acid concentration of from 2 to 30 weight per cent, preferably 5 to 25 weight per cent, based on the weight of the liquid medium. The catalyst deactivating agent is used in any amount effective to reduce the activity of the phosphonium salt catalyst, e.g., to reduce the rate at which the fusion reaction proceeds in the presence of the phosphonium salt catalyst. Generally, the catalyst deactivation agent will be added to the fusion reaction mixture in an amount within the range of from 0.2 to 3 equivalents deactivating agent per equivalent of phosphonium salt catalyst, preferably from 0.5 to 2, most preferably from 0.8 to 1.5. Preferred fusion catalysts which are deactivated according to the invention are hydrocarbyl phosphonium salts wherein X is selected from the group consisting of halides, preferably bromide, chloride or iodide; carboxylates such as formate, acetate, oxalate or trifluoroacetate; conjugate bases of weak inorganic acids, including bicarbonate, tetrafluoroborate or biphosphate; and conjugate bases of a phenol, including phenate or an anion derived from bisphenol-A. The R groups can each independently be aliphatic or aromatic, preferably aromatic. The preferred water-resistant catalyst is methylene bis(triphenyl-phosphonium) dibromide (MBTPPB). The above-described phosphonium salts are useful as catalysts of reactions of compounds having a 1.2-epoxy group with acidic compounds such as phenols, thiophenols, carboxylic acids and carboxylic acid anhydrides, for example. An example of such a reaction is an epoxy fusion process in which a low molecular weight epoxy resin is reacted with an acidic fusion compound such as a phenol, thiophenol, carboxylic acid or carboxylic acid anhydride, to produce a high molecular weight fusion product. The low molecular weight epoxy resin starting material will preferably be a liquid polyepoxide having an average of more than one 1,2-epoxy group per molecule and a weight per epoxide less than about 500. Preferred liquid polyepoxides include liquid glycidyl polyethers of polyhydric phenols and polyhydric alcohols. Most preferred are the glycidyl polyethers of 2,2-bis(4-hydroxyphenyl)propane having an average molecular weight between 340 and 900 and an epoxy equivalent weight (ASTM D- 1652) of between 170 and 500. Such liquid epoxy resins are available commercially as EPIKOTE 828, a liquid epoxy resin having a molecular weight of 376 and an epoxy equivalent of 185-192. The low molecular weight epoxide is reacted with an acidic hydroxyl group containing compound such as a phenol, thiophenol, carboxylic acid or carboxylic acid anhydride. The phenols useful in the fusion reaction are those compounds having at least one hydroxyl group attached to an aromatic nucleus. The phenols can be monohydric or polyhydric and can be substituted or unsubstituted. Examples of suitable phenols include phenol, resorcinol, 0-cresol, m-cresol, p-cresol, chlorophenol, nitrophenol, hydroquinone, 2,2-bis(4-hydroxyphenyl)propane, 2,2-bis(4-hydroxyphenyl)pentane, and the like, and polymeric polyhydric phenol obtained by condensing monohydric or polyhydric phenols with formaldehyde. Preferred phenols are polyhydric phenols containing from 2 to 6 hydroxyl groups and up to about 30 carbon atoms, including those represented by the formula V, wherein X is a polyvalent radical and each R′ is independently selected from hydrogen, halogen and hydrocarbyl. The preferred radicals represented by X are oxygen, sulphur, divalent hydrocarbon radicals containing up to about 10 carbon atoms, and oxygen-, silicon-, sulphur- and nitrogen-containing hydrocarbon radicals. The preferred compound according to formula V is 2,2-bis(4-hydroxyphenyl)propane (bisphenol-A), in which each R′ is H and X is propyl. The amount of the phosphonium salt catalyst used in a fusion reaction can vary over a wide range, but the catalyst will generally be present in the fusion reaction mixture in an amount of from 0.001 to 8 weight per cent, preferably from 0.01 to 2 weight per cent, based on the weight of the reactants. The fusion reaction may be carried out in the presence or absence of solvents or diluents. Generally, the reactants will be liquid and the reaction can be carried out without the addition of solvents or diluents. If it is considered desirable to carry out the reaction in a diluent, an inert hydrocarbon such as xylene, toluene or cyclohexane will generally be chosen. The fusion reaction is generally carried out by combining the polyepoxide and fusion compound reactants at a starting temperature of about 100-120 °C and allowing the reaction to exotherm to a temperature of about 160-200 °C, for a time of about 1-2 hours. The relative amounts of the reactants depend upon the characteristics, particularly molecular weight, of the product desired. For the preferred high molecular weight phenolic hydroxy ether resin products having an epoxy equivalent weight of between 500 and 7000, 0.4 to 1 mol of bisphenol-A will be reacted with each mol of a liquid diglycidyl ether of bisphenol-A. The fusion reaction can be carried out in the presence or absence of water, depending upon the sensitivity to water of the particular phosphonium salt catalyst employed and the fusion product desired. Satisfactory product is obtained when 0.01 weight per cent or more water is present in the reaction mixture, particularly when the methylene bis-type fusion catalyst is employed. When the fusion reaction has proceeded to an epoxy resin having the desired epoxy equivalent weight, generally 500 or greater, deactivation of the catalyst is conveniently carried out by adding, with stirring, the desired amount of the sulphonic acid deactivating agent to the fusion reaction mixture. The temperature at which deactivation is carried out is not critical, and will generally occur at the temperature of the fusion reaction mixture at the desired point of termination of the fusion reaction, which will generally be 160-195 °C. Reduction of the activity of the catalyst is essentially immediate upon contact by the sulphonic acid. Following deactivation of the catalyst, the advanced epoxy resin is recovered and processed by conventional methods. EXAMPLE 1 This example shows the effectiveness of two different sulphonic acids in deactivating a highly stable phosphonium salt catalyst in an epoxy fusion reaction. 225 g of EPIKOTE 828, was advanced by reaction with 75 g bisphenol-A in the presence of 0.05 weight per cent, based on the initial epoxy plus BPA charge, of methylene bis(triphenyl phosphonium bromide) catalyst at 182 °C for about 2 hours, to yield an epoxy resin having an epoxy equivalent weight (WPE) of about 600. When an additional charge of 30 g bisphenol-A was added, the reaction proceeded to an epoxy product having a WPE of 2200, showing the continued high activity of the phosphonium halide catalyst. In one deactivation trial, 1 mol of p-toluenesulphonic acid per equivalent (0.5 mol) of catalyst was added to the reaction mixture containing 600 WPE resin. The WPE of the fusion resin stayed the same for 3 hours. The WPE did not increase appreciably even after additional BPA was added. The addition of 2 mol of p-toluene sulphonic acid or methane sulphonic acid per mol of the catalyst to the reaction mixture containing 600 WPE resin essentially terminated the fusion reaction. The results of the runs are summarized below in Table 1.

Claims: A process for deactivating a hydrocarbyl phosphonium salt catalyst of the formula I in which each R is selected independently from a hydrocarbyl or inertly substituted hydrocarbyl group and X is a compatible anion, comprising contacting the catalyst with a sulphonic acid. The process of claim 1 in which the sulphonic acid is toluene-sulphonic acid or methane sulphonic acid. The process of claim 1 or 2 in which each R is independently an aromatic group. The process of any one of claims 1 to 3 in which X is an anion selected from the group consisting of halides, carboxylates, conjugate bases of weak inorganic acids and conjugate bases of a phenol. The process of any one of claims 1 to 4 in which the hydrocarbyl phosphonium salt catalyst is a methylene bis(triphenyl phosphonium halide). The process of any one of claims 1 to 5 in which the sulphonic acid is employed in an amount of from about 0.05 to about 2.0 equivalents per equivalent of the hydrocarbyl phosphonium salt catalyst. A process for preparing an advanced epoxy resin, the process comprising: contacting in a reaction mixture a polyepoxide having an average of more than one 1,2-epoxide group per molecule and an epoxy equivalent weight of less than 500 with a fusion compound selected from the group consisting of phenols, thiophenols, carboxylic acids and carboxylic acid anhydrides in the presence of a catalytic amount of a hydrocarbyl phosphonium salt catalyst of the formula I in which each R is selected independently from a hydrocarbyl or inertly substituted hydrocarbyl group and X is a compatible anion, at a temperature in the range of from 100 °C to 200 °C, for a time sufficient to produce an epoxy resin having an epoxy equivalent weight of more than 500; and thereafter, adding to the reaction mixture an amount of a sulphonic acid effective to reduce the activity of the hydrocarbyl phosphonium salt catalyst. The process of claim 7 in which the sulphonic acid is added to the reaction mixture in an amount of from 0.05 to 2.0 mol per mol of the hydrocarbyl phosphonium salt catalyst.

Inventors: FRANK, HARRY
Applicants: SHELL INTERNATIONALE RESEARCH MAATSCHAPPIJ B.V.
Application year: 1987
Main classification: C08G59
IPC codes: C08G59, B01J31