FLUIDITY CONTROLLING AGENT FOR HEAT CURING PAINTS

Abstract: A fluidity controlling agent for paints is a reaction product between paratoluidine and hexamethylene diisocyanate with a particular mol ratio (NH₂/NCO) and gives thixotropic properties to the paint without sagging at a thicker thickness of coating film.

Description: This invention relates to a fluidity controlling agent for paints which gives thixotoropic properties to a coating film when it is applied to the paint and hardly produces sagging even in the formation of thick coating film, and more particularly to a fluidity controlling agent useful for heat curing paints. Heretofore, calcium carbonate, organic bentonite, hydrophobic silica, organic polyamide wax, polyethylene wax and the like have been used as a fluidity controlling agent for paints. Recently, compounds having urea bond in molecule are included in the above known fluidity controlling agents. For example, Japanese Patent laid open No. 49-99,131 discloses a fluidity controlling agent consisting of a urea adduct obtained by reacting (a) a diisocyanate compound, (b) primary and/or secondary polyamine and, if necessary, (c) monofunctional alcohol, oxime, amine and/or alkanol amine at such a ratio that the amount of primary and/or secondary amino group does not stoichiometrically exceed the amount of isocyanate group. Furthermore, US Patent No 4,311,622 discloses a fluidity controlling agent consisting of a reaction product of a diisocyanate and a monoamine or hydroxymonoamine of an aliphatic hydrocarbon having a carbon number of 1∼5. The fluidity controlling agent having such a urea bond has an advantage that the effect of preventing the sagging is large even in paints containing a large amount of a high polarity solvent such as alcohol, ketone or the like because the intermolecular force acting to the urea bond is generally strong, and the effect of preventing the sagging is hardly lost even during the temperature rising in the curing when it is applied to the heat curing paint. However, when such a fluidity controlling agent as disclosed in Japanese Patent laid open No. 49-99,131 is applied to a transparent clear paint containing no pigment, the sagging prevention effect is lowered with the lapse of time, and the gloss of coating film is undesirably degraded if the curing is performed at a temperature below 140°C even after the production of the paint. On the other hand, the fluidity controlling agent made from monoamine or hydroxymonoamine of aliphatic hydrocarbon having a carbon number of 1∼5 and diisocyanate, for example, benzylamine and hexamethylene diisocyanate as disclosed in U.S. Patent No. 4,311,622 is high in the melting point in the coating film and has a drawback that when it is applied to a transparent clear paint containing no pigment, if the curing temperature is lower than 140°C of usual baking temperature, the gloss of the coating film is degraded. Under the above circumstances, the inventors have made studies with respect to a means for solving the above problems and found that very high thixotropic properties are obtained by using a reaction product between a primary monoamine directly bonding amino group to aromatic ring and aliphatic diisocyanate as a fluidity controlling agent, and consequently proposed a fluidity controlling agent containing a component obtained by reacting aniline and aliphatic diisocyanate and a component obtained by reacting oxygen-containing primary monoamine and aliphatic diisocyanate at a particular mixing ratio (Japanese Patent laid open No. 61-97,375). In this case, however, the oxygen-containing primary monoamine is used, so that when the molecular weight of a resin used as an organic binder is small, the water resistance of the coating film undesirably lowers. The invention is based on the unexpectedly discovery that when a novel product obtained by reacting paratoluidine with hexamethylene diisocyanate at a particular ratio is used as a fluidity controlling agent for paints, the high sagging prevention effect is obtained in an amount smaller than the amount of the fluidity controlling agent used in U.S. Patent No. 4,311,622 and also the gloss is good after the curing at a relatively low temperature below 140°C without using the component of reaction product between oxygen-containing primary monoamine and aliphatic diisocyanate as disclosed in Japanese Patent laid open No. 61-97,375. According to the invention, there is the provision of a fluidity controlling agent for paints, consisting of a reaction product between paratoluidine and hexamethylene diisocyanate with a mol ratio of NH₂/NCO of 0.8∼1.2. In the fluidity controlling agent according to the invention, paratoluidine wherein amino group and methyl group are bonded to aromatic ring at symmetrical positions is used as a primary monoamine. When using orthotoluidine and metatoluidine, wherein the bonding positions of amino group and methyl group are unsymmetry, and other primary monoamines wherein amino group and aliphatic hydrocarbon residue are bonded to aromatic ring such as 2,3-xylidine, 3,4-xylidine and the like, the high sagging prevention effect is not obtained. On the other hand, hexamethylene diisocyanate. is used as an organic polyisocyanate in the fluidity controlling agent according to the invention. The use of other diisocyanate such as tolylene diisocyanate or the like does not provide the high sagging prevention effect and lowers the gloss of the coating film. According to the invention, it is necessary that the ratio of paratoluidine to hexamethylene diisocyanate is within a range of 0.8∼1.2 as a mol ratio of NH₂/NCO. When the mol ratio of NH₂/NCO is less than 0.8, excessive isocyanate groups react with each other to produce high molecular weight substance, resulting in the lowering of film gloss, or excessive isocyanate groups may react with a solvent or an active hydrogen atom of a resin so as not to provide high thixotropic properties. On the contrary, when the mol ratio of NH₂/NCO exceeds 1.2, the color of the coating film changes into yellow or the curing is poor. In the production of the fluidity controlling agent according to the invention, a solution of paratoluidine in an organic solvent is stirred at a temperature of not higher that 60°C, preferably 0∼40°C in an inert gas atmosphere, to which is slowly added hexamethylene diisocyanate. As the organic solvent for dissolving paratoluidine, the use of an aromatic solvent such as benzene, toluene, xylene or the like is preferable. If necessary, there may be included an ester series solvent such as ethyl acetate, butyl acetate, amyl acetate or the like, a ketone series solvent such as acetone, methyl ethyl ketone, methyl isobutyl ketone, cyclohexanone or the like, an alcohol such as methanol, ethanol, isopropanol, n-butanol or the like, and so on. Moreover, the production of the fluidity controlling agent according to the invention may be carried out in a resin used as an organic binder component for the paint. As the resin, mention may be made of polyester resins, acrylic resins, vinyl resins, polyurethane resins, polyether resins, petroleum resins and so on. For example, the use of the polyester resin or acrylic resin is preferable when using for applications requiring the weather resistance as a top coat. When the fluidity controlling agent for paint is produced in the resin, it is preferable that the solution of paratoluidine in the organic solvent is mixed with the resin and the resulting mixture is held at a temperature of 0∼40°C, during which hexamethylene diisocyanate is slowly added while stirring at high speed. The concentration of the fluidity controlling agent can be properly selected by the kind of the solvent used or the kind and viscosity of the resin, but it is preferable within a range of 1∼10% by weight in case of producing in the solvent or 0.1∼3% by weight in case of producing in the resin. When a paint is produced by using the fluidity controlling agent produced according to the method of the invention, a curing agent (for example, polyisocyanate compounds such as hexamethylene diisocyanate, isophorone diisocyanate and the like; blocked isocyanate compounds hindering a whole or a part of isocyanate groups contained in the polyisocyanate compound with a blocking agent such as lower alcohol, ε-caprolactam, methyl ethyl ketoxime or the like; amino resins such as melamine resin, urea resin and the like; epoxy resins and so on); a pigment such as organic pigment, inorganic pigment, extender pigment and the like; an additive such as surface adjustor, anti-settling agent, heat and light deterioration preventing agents, pigment dispersing agent and the like, and further a reaction catalyst for promoting reaction may be compounded in addition to the resin used as the aforementioned organic binder component. The amount of the fluidity controlling agent according to the invention to be compounded in the paint is within a range of 0.05∼2% by weight per total weight of the paint, which provides high thixotropic properties and makes possible to perform thick coating film. In order to compound the fluidity controlling agent according to the invention into the paint, when the fluidity controlling agent is produced in the organic solvent and is a mixture with the organic solvent, it is mixed with the resin used as the organic binder in a mixing and kneading apparatus such as dissolver, ball mill, sand grind mill or the like and then the resulting mixture is compounded into the paint. On the other hand, when the fluidity controlling agent is produced in the resin used as the organic binder component, it may be compounded into the paint as it is. The fluidity controlling agent for paint according to the invention is a product obtained by using paratoluidine, wherein amino group and methyl group are bonded to aromatic ring at symmetrical positions, as an organic monoamine and hexamethylene diisocyanate as an organic diisocyanate and reacting them at a particular mol ratio of NH₂/NCO of 0.8∼1.2, so that the steric configuration of the molecule is symmetry and the crystallinity is good. Therefore, it has excellent effects that the high sagging prevention effect is obtained at a smaller amount as compared with the same type of the conventional fluidity controlling agent, and the hardness, water resistance and solvent resistance are excellent, and the gloss is not degraded and the discoloration is not caused in the curing at a lower temperature even when being applied to a transparent clear paint. The following examples are given in illustration of the invention and are not intended as limitations thereof. Unless otherwise specified, part and percentage are by weight. Production Example 1 Production of acrylic resin varnish Into a reactor provided with an agitator, a thermometer, a reflux condenser and a monomer dropping device was charged 35.0 parts of xylene, which was refluxed by heating at a temperature of 135∼140°C with stirring. Then, a mixture of the following monomers was placed in the monomer dropping device and added dropwise at an equal speed over 3 hours. stylene 12.5 parts methyl methacrylate 12.5 parts butyl methacrylate 10.0 parts 2-ethylhexyl acrylate 13.5 parts 2-hydroxyethyl methacrylate 10.0 parts methacrylic acid 2.5 parts Perbutyl Z (trade name of polymerization initiator, made by Nippon Oils & Fats Co., Ltd.) 4.0 parts After the completion of the addition of the monomer mixture, the stirring was further continued under reflux state for 2 hours, whereby an acrylic resin varnish having a solid content of 65% and a viscosity of Y-Z as measured at a temperature of 25°C by means of a foam viscometer (according to JIS K5400 4.2.2). Production Example 2 Production of 20% paratoluidine solution Paratoluidine was dissolved by warming at a temperature of 40∼50°C, which was made into a 20% solution according to the following recipe: xylene 80.0 parts paratoluidine 20.0 parts Example 1 acrylic resin varnish of Production Example 1 92.5 parts 20% paratoluidine solution of Production Example 2 5.7 parts The mixture of the above components was charged into a reactor provided with an agitator, a thermometer and a dropping funnel and then cooled to a temperature of 10°C with stirring. Thereafter, 0.9 part of hexamethylene diisocyanate and 0.9 part of xylene were placed into the dropping funnel, which were added dropwise at an equal speed over 30 minutes. After the completion of the addition, the stirring was further continued at a temperature of 10∼15°C for 30 minutes, whereby an opaque acrylic resin varnish containing 2% per total weight of a fluidity controlling agent with a mol ratio of NH₂/NCO of 1.0 as a ratio of paratoluidine to hexamethylene diisocyanate and having thixotropic properties was obtained. The acrylic resin varnish containing the fluidity controlling agent was used according to the following compounding recipe to prepare a paint: acrylic resin varnish containing fluidity controlling agent 10.0 parts acrylic resin varnish of Production Example 1 56.0 parts Super Beckamin L-116-70 (trade name of butylated melamine resin, made by Dainippon Ink Chemicals Industries, Ltd.) 27.0 parts xylene 4.0 parts n-butyl alcohol 3.0 parts The resulting paint was diluted with a mixed solvent of xylene and n-butyl alcohol of 90:30 (parts) to a viscosity of 30 seconds as measured at a temperature of 20°C through Ford Cup No. 4, which was applied by spraying to a vertically stood test plate (Bonderite #3004, trade name of phosphated steel sheet, made by Nippon Perkalizing Co., Ltd.) and cured at a temperature of 120°C for 30 minutes. As a result, the sagging was not caused and the gloss was good when the thickness of coating film reached up to 49 µm. Example 2 An acrylic resin varnish containing 2% of a fluidity controlling agent with a mol ratio of NH₂/NCO of 0.8 was produced according to the following compounding recipe in the same manner as in Example 1: acrylic resin varnish of Production Example 1 92.5 parts 20% paratoluidine solution of Production Example 2 5.0 parts hexamethylene diisocyanate 1.0 part xylene 1.5 parts This acrylic resin varnish containing the fluidity controlling agent was used to prepare a paint in the same manner as in Example 1, which was then applied in the same manner as in Example 1. As a result, when the thickness of coating film reached up to 47 µm, the sagging was not caused and the gloss of the film was good. Example 3 An acrylic resin varnish containing 2% of a fluidity controlling agent with a mol ratio of NH₂/NCO of 1.2 was produced according to the following compounding recipe in the same manner as in Example 1: acrylic resin varnish of Production Example 1 92.5 parts 20% paratoluidine solution of Production Example 2 6.0 parts hexamethylene diisocyanate 0.8 part xylene 0.7 part This acrylic resin varnish containing the fluidity controlling agent was used to prepare a paint in the same manner as in Example 1, which was then applied in the same manner as in Example 1. As a result, when the thickness of coating film reached up to 48 µm, the sagging was not caused and the gloss of the film was good. Production Example 3 Production of polyester resin varnish Into a reactor provided with an agitator, a reflux condenser attached with a distilled water separating device, a thermometer and an inert gas supply tube were charged the following components: neopentyl glycol 25.3 parts trimethylol propane 6.0 parts adipic acid 25.9 parts isophthalic acid 14.3 parts These components were heated to a temperature of 120°C, stirred and then heated to a temperature of 200°C to further conduct the reaction, during which a small amount of the content was sometimes taken out to measure an acid value. When the acid value reached to 15, the reaction product was cooled and then diluted with the following components: xylene 18.0 parts Solveso 150 (trade name of high boiling aromatic solvent, made by Esso Chemicals Co., Ltd.) 10.5 parts The amount of distilled water in the reaction was 18 parts. Thus, there was obtained a polyester resin varnish having a solid content of 65% and a viscosity of X-Y as measured at a temperature of 25°C by means of a foam viscometer (according to JIS K5400 4.2.2). Example 4 (1) Production of polyester resin varnish containing fluidity controlling agent (1) polyester resin varnish of Production Example 3 98.2 parts 20% paratoluidine solution of Production Example 2 1.4 parts The mixture of the above components was charged into a reactor provided with an agitator, a thermometer and a dropping funnel and then cooled to a temperature of 10°C with stirring. Thereafter, 0.2 part of hexamethylene diisocyanate and 0.2 part of xylene were placed in the dropping funnel and added dropwise at an equal speed over 30 minutes. After the completion of the addition, the stirring was further continued at a temperature of 10.∼15°C for 30 minutes. Thus, there was obtained a slightly opaque polyester resin varnish containing 0.5% per total weight of a fluidity controlling agent with a mol ratio of NH₂/NCO of 1.0 as a ratio of paratoluidine to hexamethylene diisocyanate and having thixotropic properties. (2) Production and application of white paint containing fluidity controlling agent polyester resin varnish of Production Example 3 13.4 parts titanium dioxide (JR-602, trade name, made by Teikoku Kako Co., Ltd.) 29.0 parts xylene 4.4 parts ethylene glycol monoethyl ether acetate 4.4 parts The mixture of the above components was dispersed by means of a glass bead mill for 1 hour. After the removal of glass beads by filtration, the following components were added with stirring: polyester resin varnish of Production Example 3 7.2 parts polyester resin varnish containing the fluidity controlling agent (1) 20.0 parts Super Beckamin L-116-70 16.0 parts BYK-300 (trade name of silicon resin additive, made by BYK Chemie Gmbh) 0.1 part Solveso 150 2.5 parts n-butyl alcohol 3.0 parts This paint was diluted and applied by spraying in the same manner as in Example 1. As a result, when the thickness of coating film reached up to 60 µm, the sagging was not caused and the gloss was good. Example 5 (1) Production of polyester resin varnish containing fluidity controlling agent (2) A polyester resin varnish containing 3.0% of fluidity controlling agent with a mol ratio of NH₂/NCO of 1.0 was produced according to the following compounding recipe in the same manner as in the item (1) of Example 4: polyester resin varnish of Production Example 3 88.9 parts 20% paratoluidine solution of Production Example 2 8.5 parts hexamethylene diisocyanate 1.3 parts xylene 1.3 parts (2) Production and application of white paint containing fluidity controlling agent polyester resin varnish of Production Example 3 13.4 parts titanium dioxide 29.0 parts xylene 4.4 parts ethylene glycol monoethyl ether acetate 4.4 parts The mixture of the above components was dispersed and filtered in the same manner as in the item (2) of Example 4, to which were added the following components: polyester resin varnish of Production Example 3 21.0 parts polyester resin varnish containing the fluidity controlling agent (2) 6.5 parts Super Beckamin L-116-70 15.7 parts BYK-300 0.1 part Solveso 150 2.5 Parts n-butyl alcohol 3.0 parts This paint was diluted and applied by spraying in the same manner as in Example 1. As a result, when the thickness of coating film reached up to 65 µm, the sagging was not caused and the gloss was good. Example 6 The following components were mixed: acrylic resin varnish of Production Example 1 50.0 parts acrylic resin varnish containing the fluidity controlling agent of Example 1 25.0 parts ethylene glycol momoethyl ether acetate 5.0 parts butyl acetate 7.5 parts The resulting mixture was added with 12.5 parts of polyisocyanate (Desmodule N-75, trade name, made by Bayer AG, heating residue: 75%) as a curing agent. The thus produced paint capable of curing with polyisocyanate was diluted with a mixed solvent of butyl acetate and cyclohexanone of 70:30 to a viscosity of 30 seconds as measured at a temperature of 20°C through Ford Cup No. 4 and then applied by spraying in the same manner as in Example 1. As a result, when the thickness of coating film reached up to 50 µm, the sagging was not caused and the gloss was good. Example 7 (1) Production of fluidity controlling agent in solvent xylene 81.6 parts 20% paratoluidine solution 14.0 parts The mixture of the above components was charged into a reactor provided with an agitator, a thermometer and a dropping device, to which was added dropwise a mixture of 2.2 parts of hexamethylene diisocyanate and 2.2 parts of xylene from the dropping device with stirring over 2 hours. In this case, the temperature was maintained so as not to exceed 40°C. After the completion of the addition, the stirring was further continued for 1 hour. Thus, there was obtained a white waxy mixture of fluidity controlling agent and xylene containing 5% of the fluidity controlling agent with a mol ratio of NH₂/NCO of 1.0 as a ratio of paratoluidine to hexamethylene diisocyanate. (2) Production of paint The mixture containing 5% of the fluidity controlling agent was mixed with the acrylic resin varnish of Production Example 1 at the following mixing ratio and dispersed in a ball mill for 24 hours: mixture containing 5% of fluidity controlling agent 20.0 parts acrylic resin varnish of Production Example 1 20.0 parts After the dispersion, balls were removed by filtering through a wire net, and then the following components were mixed to obtain a paint containing 1% per total weight of the fluidity controlling agent: acrylic resin varnish of Production Example 1 33.6 parts Super Beckamin L-116-70 26.4 parts This paint had thixotropic properties, which was diluted and applied by spraying in the same manner as in Example 1. As a result, when the thickness of coating film reached up to 61 µm, the sagging was not caused and the gloss of the film was good. Example 8 (1) Production of fluidity controlling agent in solvent xylene 63.2 parts 20% paratoluidine solution 28.0 parts The mixture of the above components was charged in the same reactor as in Example 7 and the following mixture was added dropwise thereto from the dropping device over 4 hours with stirring: hexamethylene diisocyanate 4.4 parts xylene 4.4 parts During the addition of the mixture, the temperature was maintained so as not to exceed 40°C. After the completion of the addition, the stirring was further continued for 1 hour. In this way, there was obtained a white waxy mixture of fluidity controlling agent and xylene containing 10% of the fluidity controlling agent with a mol ratio of NH₂/NCO of 1.0 as a ratio of paratoluidine to hexamethylene diisocyanate. (2) Production of paint The above mixture containing 10% of the fluidity controlling agent was mixed with the acrylic resin varnish at the following compounding recipe and dispersed through a ball mill for 24 hours: mixture containing 10% of fluidity controlling agent 20.0 parts acrylic resin varnish of Production Example 1 20.0 parts After the dispersion, balls were removed by filtering through a wire net and then the following components were mixed to obtain a paint containing 2% per total weight of the fluidity controlling agent: acrylic resin varnish of Production Example 1 33.6 parts Super Beckamin L-116-70 26.4 parts This paint had thixotropic properties, which was diluted and applied by spraying in the same manner as in Example 1. As a result, when the thickness of coating film reached up to 60 µm, the sagging was not caused and the gloss of the film was good. Example 9 polyester resin varnish of Production Example 3 12.4 parts mixture containing 5% of fluidity controlling agent in Example 7 1.0 part titanium dioxide 29.0 parts ethylene glycol monoethyl ether acetate 4.4 parts xylene 4.4 parts The mixture of the above components was dispersed through a ball mill for 24 hours and then balls were removed by filtering through a wire net. Thereafter, the following components were mixed with stirring: polyester resin varnish of Production Example 3 27.2 parts Super Beckamin L-116-70 16.0 parts BYK-300 0.1 part Solveso 150 2.5 parts n-butyl alcohol 3.0 parts This paint was diluted and applied by spraying in the same manner as in Example 1. As a result, when the thickness of coating film reached up to 50 µm, the sagging was not caused and the gloss was good. Comparative Example 1 An acrylic resin varnish containing 2% of fluidity controlling agent with a mol ratio of NH₂/NCO of 0.6 was produced according to the following compounding recipe in the same manner as in Example 1: acrylic resin varnish of Production Example 1 92.5 parts 20% paratoluidine solution 4.3 parts hexamethylene diisocyanate 1.1 parts xylene 2.1 parts This acrylic resin varnish containing the fluidity controlling agent was low in the thixotropic properties. This varnish was used to prepare a paint in the same manner as in Example 1. When the thickness of coating film reached 29 µm by applying the resulting paint, the sagging was caused and the gloss of the film was poor. Comparative Example 2 An acrylic resin varnish containing 2% of fluidity controlling agent with a mol ratio of NH₂/NCO of 1.4 was prepared according to the following compounding recipe in the same manner as in Example 1: acrylic resin varnish of Production Example 1 92.5 parts 20% paratoluidine solution 6.4 parts hexamethylene diisocyanate 0.7 part xylene 0.4 part A paint was prepared by using the acrylic resin varnish containing the fluidity controlling agent in the same manner as in Example 1. When the thickness of coating film reached up to 45 µm, the sagging was not caused, but the color of the film was changed into yellow. Further, the water resistance, solvent resistance and hardness were poor as a result of the film performance test as mentioned later. Comparative Example 3 An acrylic resin varnish containing 3% of fluidity controlling agent was produced by using orthotoluidine as a primary monoamine according to the following compounding recipe acrylic resin varnish of Production Example 1 92.5 parts orthotoluidine 1.7 parts xylene 3.2 parts That is, the above mixture was charged into the same reactor as in Example 1 and cooled to a temperature of 10°C with stirring. Then, 1.3 parts of hexamethylene diisocyanate and 1.3 parts of xylene were placed in the dropping device and added dropwise at an equal speed over 30 minutes. After the completion of the addition, the stirring was further continued at a temperature of 10∼15°C for 30 minutes. The thus obtained acrylic resin varnish containing 3% of the fluidity controlling agent was used to prepare a paint having the following compounding recipe: acrylic resin varnish containing the fluidity controlling agent 33.3 parts acrylic resin varnish of Production Example 1 32.7 parts Super Beckamin L-116-70 27.0 parts xylene 4.0 parts n-butyl alcohol 3.0 parts When this paint was applied in the same manner as in Example 1, the sagging was caused at a thickness of 22 µm. Comparative Example 4 An acrylic resin varnish containing 3% of fluidity controlling agent was produced by using 3,4-xylidine as a primary monoamine according to the following compounding recipe: acrylic resin varnish of Production Example 1 92.5 parts 3,4-xylidine 1.8 parts xylene 3.3 parts That is, the above mixture was charged into the same reactor as in Example 1 and cooled to a temperature of 10°C with stirring. Then, 1.2 parts of hexamethylene diisocyanate and 1.2 parts of xylene were placed in the dropping device and added dropwise at an equal speed over 30 minutes. After the completion of the addition, the stirring was further continued at a temperature of 10∼15°C for 30 minutes. The thus obtained acrylic resin varnish containing 3% of the fluidity controlling agent was used to prepare a paint according to the following compounding recipe acrylic resin varnish containing fluidity controlling agent 33.3 parts acrylic resin varnish of Production Example 1 32.7 parts Super Beckamin L-116-70 27.0 parts xylene 4.0 parts n-butyl alcohol 3.0 parts When the resulting paint was applied in the same manner as in Example 1, the sagging was caused at a thickness of 25 µm. Comparative Example 5 acrylic resin varnish of Production Example 1 94.4 parts aniline 1.4 parts hexamethylene diisocyanate 1.4 parts xylene 2.8 parts An acrylic resin varnish containing a fluidity controlling agent derived from aniline was produced according to the above compounding recipe in the same manner as in Example 1. Separately, an acrylic resin varnish containing a fluidity controlling agent derived from an oxygen-containing primary monoamine was produced according to the following compounding recipe in the same manner as described above: acrylic resin varnish of Production Example 1 94.4 parts monoethanolamine 1.1 parts hexamethylene diisocyanate 1.7 parts xylene 2.8 parts A paint was prepared by using these two acrylic resin varnishes according to the following compounding recipe: acrylic resin varnish of Production Example 1 40.2 parts acrylic resin varnish containing the fluidity controlling agent derived from aniline 17.9 parts acrylic resin varnish containing the fluidity controlling agent derived from monoethanolamine 17.9 parts Super Beckamin L-116-70 24.0 parts When the resulting paint was applied in the same manner as in Example 1, the sagging was not caused at a thickness up to 42 µm and the gloss of the film was good, but the water resistance was poor. Comparative Example 6 An acrylic resin varnish containing 3% of fluidity controlling agent derived from benzylamine was produced according to the following compounding recipe in the same manner as in Example 1: acrylic resin varnish of Production Example 1 92.5 parts benzylamine 1.7 parts hexamethylene diisocyanate 1.3 parts xylene 4.5 parts A paint was prepared by using the acrylic resin varnish containing the fluidity controlling agent according to the following compounding recipe: acrylic resin varnish of Production Example 1 32.7 parts acrylic resin varnish containing the fluidity controlling agent 33.3 parts Super Beckamin L-116-70 27.0 parts xylene 4.0 parts n-butyl alcohol 3.0 parts When the resulting paint was applied in the same manner as in Example 1, the sagging was caused at a thickness of 32 µm and the gloss of the film was poor. The film performance test was made with respect to the test plates coated with each paint of Examples 1∼9 and Comparative Examples 1∼5 according to the following evaluation methods to obtain results as shown in the following Table 1. Evaluation methods Gloss: measured by means of a Dorigon meter made by Hunter Laboratories, and represented by a gloss value (Rs) reflected at 30°. Discoloration: visual observation. Hardness: according to a pencile scrubbing test of JIS K5400 6.14 Water resistance: discoloration and softening of the film were measured after the immersion in a hot water of 80°C for 3 hours. Solvent resistance: the discoloration and softening of the film were measured after the immersion in a mixture of 90%/10% of petroleum benzine/methyl alcohol at room temperature for 1 hour. Note: (1) acrylic resin varnish containing the fluidity controlling agent produced in each of Examples 1∼3, 6∼8 and Comparative Examples 1∼6 (2) polyester resin varnish containing the fluidity controlling agent produced from each of Examples 4, 5, 9 (3) trade name of butylmelamine resin, made by Dainippon Ink Chemical Industries Ltd., heating residue: 68% (4) trade name of polyisocyanate, made by Bayer AG, heating residue: 75% (5) trade name of titanium dioxide, made by Teikoku Kako Co., Ltd. (6) trade name of silicon resin additive, made by BYK Chemie Gmbh (7) trade name of high boiling aromatic solvent, made by Esso Chemicals Ltd. (8) content of fluidity controlling agent in total paint weight before dilution of paint (9) sagging limit thickness (µm) after the paint diluted to 30 seconds (20°C) through Ford Cup No. 4 was applied by spraying to a vertically stood test plate (Bonderite #3004, made by Nippon Perkalizing Co., Ltd., trade name of phosphated steel sheet) and then cured at a temperature of 120°C at a vertically stood state for 30 minutes As seen from the above results, the paints using the fluidity controlling agent according to the invention in Examples 1∼9 can be applied at a thicker thickness, and exhibit good gloss even after the curing at a temperature of 120°C, and are good in the film performances such as discoloration, hardness, water resistance, solvent resistance and the like. On the other hand, in case of Comparative Example 1 wherein the mol ratio of NH₂/NCO is less than 0.8, the sagging prevention effect is insufficient and the gloss of the film is poor. In case of Comparative Example 2 wherein the mol ratio of NH₂/NCO exceeds 1.2, the color of the film is changed into yellow during the curing, and the curing is poor at the curing temperature of 120°C, and the hardness, water resistance and solvent resistance are also poor. In case of Comparative Examples 3 and 4 wherein orthotoluidine and 3,4-xylidine are used as a primary monoamine, even when the fluidity controlling agent is compounded in an amount of 1% per total weight of the paint, the sagging prevention effect is poor. In case of Comparative Example 5 according to Japanese Patent laid open No. 61-97,375, the hardness and water resistance are poor at the curing temperature of 120°C. In case of Comparative Example 6 according to U.S. Patent No. 4,311,622, even when the fluidity controlling agent is compounded in an amount of 1% per total weight of the paint, the sagging prevention effect is poor, and the gloss of the film cured at a temperature of 120°C is poor, and also the water resistance and solvent resistance are poor.

Claims: A fluidity controlling agent for heat curing paints, consisting of a reaction product between paratoluidine and hexamethylene diisocyanate at a mol ratio of NH₂/NCO of 0.8∼1.2. The fluidity controlling agent according to claim 1, wherein said reaction product is produced in an organic solvent. The fluidity controlling agent according to claim 2, wherein a concentration of said reaction product is within a range of 1∼10% by weight. The fluidity controlling agent according to claim 1, wherein said reaction product is produced in a resin used as an organic binder component. The fluidity controlling agent according to claim 4, wherein a concentration of said reaction product is within a range of 0.1∼3% by weight.

Inventors: INOUE, OSAMU, KAMIKURI, YOSHIMASA, NAGURA, OSAMU, TAKIZUKA, NORIKAZU
Applicants: NIPPON OIL AND FATS COMPANY, LIMITED
Application year: 1987
Main classification: C09D5
IPC codes: C09D5, C09D7