DIRECTIONAL COUPLER

Abstract: A fused tapered optical fibre directional coupler for use in a polarisation-preserving fibre system has a short stub length (4, 8) of non-polarisation-preserving fibre spliced into each fibre (2, 3, 6, 7) from which the coupler is made. The reduced diameter and tapered portions of the coupler are confined to the stub lengths since it is found that low loss coupling is not achieved if these portions are fabricated in fibre with a polarisation-preserving structure.

Description: So-called single mode optical fibre that is circularly symmetric is in fact capable of supporting two degenerate orthogonally polarised modes. Bends, twists and other irregularities are liable to introduce coupling between these modes, with the result that the polarisation state with which light is launched into one end of such fibre is soon changed as the light propagates along the fibre. In many coherent light optical fibre communications systems and sensor systems the resulting indeterminate change of state of polarisation (SOP) is unacceptable, in which case use is made of fibre in which the degeneracy of the two zero-order modes is removed. The two modes are arranged to have sufficiently different propagation constants for the bends, twists and other irregularities encountered by the fibre to introduce substantially no coupling of the modes, and hence the separate identity of the two modes is preserved as light propagates down such fibre. Mode degeneracy is removed by making the fibre deliberately birefringent. For the purposes of this specification single mode optical fibre which is designed to be sufficiently birefringent to inhibit coupling between its zero-order modes will be referred to as polarisation-preserving fibre, also known as high birefringence fibre. Single mode fibre which has not been designed to be birefringent, and which therefore either exhibits no birefringence, or for which residual birefringence is too small to be effective in the prevention of mode coupling, will be referred to as non-polarisation-preserving single mode fibre. Many of the systems that require the use of polarisation preserving fibre in order to avoid the generation of indeterminate changes of SOP also require the use of branching and/or tapping elements in their optical fibre networks. Such elements are conveniently implemented in optical fibre as optical fibre directional couplers. In ordinary, non-polarisation-preserving fibre low insertion loss examples of such elements are advantageously provided by optical fibre directional couplers created by the method described in Patent Specification No. 2150703A. Satisfactory results have however not been obtained when attempting to make such directional couplers of high stress-induced birefringence polarisation-preserving fibre. The present invention is concerned with the provision of adequately low loss single mode fibre directional couplers for use in polarisation-preserving fibre networks. An article by M.S. Yataki et al entitled 'All-Fibre Polarising Beamsplitter', Electronics Letters, 14th March 1985, Vol. 21, No. 6, pp 249-251, to which attention is directed, describes the polarisation beam-splitting properties of fused tapered optical fibre directional couplers made of conventional (non-polarisation-preserving) fibre which have long enough coupling regions. The article observes that this type of polarising beam splitter 'does not have the ability to preserve a polarisation state owing to the use of conventional fibre for the leads', and suggests that this (problem) 'can be overcome by jointing polarisation-maintaining fibre leads close to the coupling region'. In practice there would be difficulties in implementing this suggested procedure. The coupling region of the coupler is particularly fragile and susceptible to strain which would introduce birefringence that would upset the beam-splitting properties of the coupling region. Accordingly the coupling region needs to be held immobile and strain-free between a pair of anchorages, one securing the coupler leads at some point beyond one end of the coupling region, and the other securing the coupler leads at some other point beyond the other end of the coupling region, and thus it would not be practical to cleave the leads of a fused tapered coupler, and then splice on new leads, except at locations beyond the region extending between the two anchorages. Furthermore there are practical difficulties in splicing close to these anchorages because, in order not to strain the coupling region, the leads will be anchored close together in each anchorage, whereas in order to splice either lead it will normally be necessary to have the other lead well clear of the splicing zone. Splicing at some distance from an anchorage eases the problems of mechanical support during cleaving and subsequent splicing, but in the completed device the stretch of lead between the anchorage and the splice will also need to be held immobile and strain-free. The invention provides a method of making a fused tapered optical fibre directional coupler which method is characterised in that a plurality of lengths of single mode fibre are made, each having first and second axes-aligned portions of polarisation-preserving fibre spliced to opposite ends of an associated stub of non-polarisation-preserving fibre, in that said lengths are arranged in side-by-side assembly and, in the region of their non-polarisation-preserving fibre stubs, are drawn down and fused together to form a reduced cross-section portion of the assembly, within which reduced cross-section portion the fibres are mutually optically coupled. The problem associated with trying to fabricate directional couplers directly in high stress-induced birefringence fibre results from the unfavourable refractive index profile that is associated with the provision of the required stress pattern. The usual technique for inducing stress-birefringence into a fibre structure involves the provision of heavily doped regions of the cladding in regions adjacent the optical core. These heavily doped regions having a significantly different thermal expansion from the rest of the fibre, and the stress results from the effects of differential thermal expansion when the fibre is cooled to room temperature from the high temperature at which it was drawn from fibre preform. Associated with the heavy doping to induce the intended differential thermal expansion effect produced by the differential doping, is an unintended differential refractive index effect. When such a fibre is tapered down in size in an attempt to make a directional coupler, too much light is coupled into unwanted modes associated with the stress-inducing structure instead of into the zero-order core modes of the other fibre or fibres of the directional coupler. The consequence is that the resulting coupler does not function properly, but exhibits an unacceptably high insertion loss. According to the teachings of the present invention this problem is circumvented by substituting non-polarisation-preserving fibre for the polarisation preserving fibre over the region where mutual coupling of the fibres is arranged to occur. Although the inserted non-polarisation-preserving fibre contains no structure to ensure that the SOP of light launched into one end propagates to the other end with substantially no change of SOP, nevertheless such a preservation of SOP is found in practice to occur. This is because the distance is relatively short, and over this distance the fibre is restrained against the sorts of bends, twists and irregularities that would otherwise be liable to induce significant changes of SOP. Because the cleaving and splicing is performed prior to the creation of the coupling region, instead of after it, as contemplated by the M.S. Yataki et al article, the operations involved in cleaving, aligning, splicing and mounting of the individual lengths of fibre from which the coupler is constructed are straightforward operations. Moreover the length of non-polarisation-preserving fibre needed to be employed is less because in this instance the splices can be located between the two anchorages. Accordingly fabrication is easier, adequate alignment not so difficult to achieve and maintain, and the completed resulting structure can be appreciably shorter in length. There follows a description of the manufacture of a directional coupler embodying the present inventionin a preferred form. The description refers to the accompanying drawings in which:- Figures 1 to 3 depict successive stages in the manufacture of the directional coupler. A length of polarisation-preserving single mode optical fibre complete with plastics protective coating 1 is cleaved into two pieces 2, 3 to enable a stub length 4 of non-polarisation-preserving single mode fibre to be inserted in between the cleaved ends. Conveniently this insertion is effected by first forming a fusion splice between one of the pieces of polarisation-preserving fibre and a piece of non-polarisation-preserving fibre (not shown), and then re-cleaving the fibre a short distance along the non-polarisation-preserving fibre from the splice, before connecting the second piece of polarisation-preserving fibre by means of a second fusion splice. In making the second fusion splice, care needs to be taken that the axes of the two pieces of polarisation-preserving fibre are aligned with each other. A second length of identical polarisation-preserving fibre complete with plastics protective coating 5 is similarly divided into two pieces 6, 7 for the insertion of its stub length 8 of non-polarisation-preserving fibre. The two lengths of fibre are then assembled for making a directional coupler. For this purpose the fibres need to be in glass-to-glass contact with each other along the region that is to be drawn down to provide the mutual optical coupling. This region of contact is conveniently provided by stranding the fibres, as illustrated in Figure 1, while taking care that the stranding introduces substantially no twist of either fibre about its own axis. Preferably the stranded fibres are clamped between independently driven carriages 9 and 10 for the making of the fused directional coupler by the progressive stretching method substantially as described in Patent Specification No. 2150703A. According to this method the fibres are heated in a flame 11 of a burner 12 to produce local softening of the glass while the fibres are being moved in a longitudinal direction through the flame. To this end the leading carriage, carriage 9 for a rightward traverse, carriage 10 for a leftward traverse, is traversed at a slightly faster rate than the trailing carriage. This stretching process is repeated a number of times until the requisite amount of coupling has been produced. Typically, though not essentially, successive traverses are performed in opposite directions. The extent of the traverses are limited so that the stretching is confined exclusively to the stub lengths 4 and 8 of non-polarisation-preserving fibre. In a typical example these stub lengths are initially about 5 to 6mm long, and the central 1mm is stretched to about 5mm. When the desired coupling has been reached the fibres are mounted upon a substrate. Conveniently this may take the form of a rod 13 (Figure 3), made for instance of fused silica, to which the fibres are secured by the application of quantities of adhesive resin applied at locations 14 and 15 where the fibres emerge from their plastics protective coatings. In this way the portion of the fibres between the two resin attachment points 14 and 15 is held in a substantially strain-free fashion. This ensures that polarisation state is well retained even in regions where the light is propagating in non-polarisation-preserving fibre. This in turn means that the stub lengths 4 and 8 of fibre can, if required, be made significantly longer than is necessary solely to accommodate the stretched region. For further mechanical protection the assembly may be placed in a long slender box (not shown) where its ends are anchored before the interior of the box is filled with a soft potting compound such as silicone rubber. Alternatively, the shape of the substrate to which the fibres are secured may be such that it can be filled with the potting compound after attachment of the fibres to an interior surface thereof. Although the foregoing description has related specifically to the construction of a 4-port directional coupler constructed from two fibres, it is to be clearly understood that the invention is applicable also to directional couplers with more than the 4 ports, particularly 6-port couplers constructed from three fibres.

Claims: A method of making a fused tapered optical fibre directional coupler which method is characterised in that a plurality of lengths of single mode fibre are made, each having first and second axes-aligned portions (2, 3, 6, 7) of polarisation-preserving fibre spliced to opposite ends of an associated stub (4, 8) of non-polarisation-preserving fibre, in that said lengths are arranged in side-by-side assembly and, in the region of their non-polarisation-preserving fibre stubs, are drawn down and fused together to form a reduced cross-section portion of the assembly, within which reduced cross-section portion the fibres are mutually optically coupled. A method as claimed in claim 1, wherein the number of lengths of single mode fibre employed to construct the coupler is two.

Inventors: BRICHENO, TERRY
Applicants: NORTHERN TELECOM LIMITED
Application year: 1987
Main classification: G02B6
IPC codes: G02B6