RAPIDLY PROCESSABLE SILVER HALIDE PHOTOGRAPHIC LIGHT-SENSITIVE MATERIAL

Abstract: A rapidly processable silver halide photographic light-sensitive material is disclosed, which comprises a support having thereon at least one silver halide emulsion layer comprising, (a) silver halide grains comprising not less than 80 mol% of silver chloride, (b) at least one optical sensitizing dye represented by the following general formula [I] and (c) at least one compound represented by the following general formula [II]. The photographic material has a high sensitivity, lowered fog and excellent storage stability.

Description: The present invention relates to a silver halide photographic light-sensitive material, and, in particular, to a silver halide photographic light-sensitive material having silver halide emulsion layers containing silver halide grains substantially composed of silver chloride which is capable of being rapidly treated, and or giving a high quality image even under conditions of rapid processing. There is demand for shorter developing times for silver halide photographic light-sensitive materials, and consequently there is a need for the development of light-sensitive materials which are capable of being rapidly treated. It is known that a light-sensitive material comprising silver halide grains with a high silver chloride content is suitable for use in rapid processing, and that such a material shows high developing speed under specific conditions, for example when no bromide is present in the material. However, though a light-sensitive material having silver halide grains with a high silver chloride content is suitable for rapid treatment, its sensitivity is low. This is because one characteristic of silver chloride is that it absorbs very little, if any, visible light. To remedy this, a means of sensitizing is required. However, the chemical sensitization of grains with a high silver chloride content readily results in fogging, and when raw samples (raw samples prior to exposure) are stored for long periods, fogging may increase, thus reducing the sensitivity. An anti-fogging agent may be added to a silver halide emulsion to prevent fogging. However, the presence of anti-fogging agents usually lowers the sensitivity of the emulsion; therefore, there would be little benefit in incorporating an anti-fogging agent, into an emulsion possessing a high silver chloride content, which is already low in sensitivity. Therefore, when using an anti-fogging agent, it is necessary to provide the emulsion with an effective sensitization means. However, it is known that the incorporation of an anti-fogging agent into an emulsion possessing a high silver chloride content renders the sensitization means less effective. For example, when a conventionally known fogging restrainer such as a tetrazaindene or a mercapto compound is used, which is readily adsorbed onto silver halide grains, the sensitizing dye is desorbed by such a compound, lessening the sensitization effect, even when the grains have been sensitized with a sensitizing dye. This tendency is very likely in an emulsion with a high silver chloride content. In theory, it should be possible to develop either a sensitizing agent which is capable of exerting an effective sensitizing power upon an emulsion possessing a high silver chloride content, the sensitizing effect of which is not lost by any fogging restrainer, or to develop a fogging restrainer which is capable of exerting an effective anti-fogging effect upon an emulsion possessing a high silver chloride content, but which has no adverse effects upon any sensitizing function. In reality, however, it is extremely difficult to develop such a sensitizing agent or fogging restrainer. Accordingly, the purpose of this invention is to provide both a sensitizing agent and a fogging restrainer each of which is capable of carrying out its own function without adversely affecting the other. It has now been unexpectedly found that satisfactory sensitization may be achieved by incorporating a certain spectral sensitizing dye into an emulsion having a high silver chloride content, while at the same time using a certain mercapto compound as a fogging restrainer; the result is that fogging is satisfactorily inhibited without reducing sensitization. The present invention provides a silver halide photographic light-sensitive material comprising a support having thereon at least one silver halide emulsion layer comprising (a) Silver halide grains comprising not less than 80 mol% of silver chloride, (b) at least one optical sensitizing dye represented by the following general formula [I], (c) at least one compound represented by the following general formula [II]: wherein X₁, X₂, X₃ and X₄ are each independently a hydrogen atom, a halogen atom, an alkyl group, an alkoxy group, an aryl group or a hydroxy group; R₁ and R₂ are each independently an optionally substituted alkyl group; X is a counter anion and n is 0 or 1, wherein Q is an atomic group necessary to complete a five-membered heterocyclic ring, a five-membered heterocyclic ring condensed with a benzene ring or a 1,3,5-triazine ring and M is a hydrogen atom, an alkali metal atom or an ammonium group, and (d) a gold sensitizer. In the prior art DE-A-2909190 describes a photographic material having a silver halide emulsion comprising any type of silver halide grains containing a sensitizing dye of formula (I) and a mercapto compound of general formula (II). EP-A-0082649 discloses a silver halide emulsion comprising 80 mol% silver chloride and a sensitizing dye of formula (I). The silver halide photographic light-sensitive material of the present invention is suitable for rapid treatment, has high sensitivity, and seldom develops fogging. In addition, as increases in fogging and losses in sensitivity are inhibited (even when a raw sample is stored for a long period prior to exposure) the light-sensitive material has an excellent shelf-life. Although very effective as a sensitizing agent, the spectral sensitizing dye of formula [I] causes an increase in fogging when it is incorporated into an emulsion with a high silver chloride content, particularly, when the light-sensitive material is stored over a long period. In contrast, if such a dye is used in combination with a compound of formula [II], the fogging problem is overcome, and, in addition, the compound of formula [II] does not affect sensitization. The compounds of formula [II] are a type of mercapto compound. Some mercapto compounds cause problems: their addition to inhibit fogging reduces sensitivity; although effective as fogging inhibitors immediately after the emulsion is applied, show no anti-fogging effects after prolonged storage; and the sensitivity is decreased in emulsions having a high silver chloride content. In contrast, mercapto compounds of general formula [II] give excellent fogging inhibition even when the light-sensitive material has been stored for a prolonged period, and furthermore, these compounds do not reduce the sensitivity of emulsions having a high silver chloride content which contain a sensitizing dye of general formula [I]. A gold-sulfur sensitization is additionally incorporated in the photographic material of the present invention. Although this gives high sensitization, gold-sulfur sensitization usually results in an increase in fogging, especially on prolonged storage. However, in the present invention, any increase in fogging is inhibited, thus enabling gold-sulfur sensitization to be effective. Gold-sulfur sensitization is particularly useful in rapid treatment. The silver halide emulsion layer used in the present invention contains silver halide grains comprising not less than 80% silver chloride, a spectral sensitizing dye of general formula [I] and a compound of general formula [II]. When a light-sensitive material of the invention comprises only one silver halide emulsion layer, this layer contains all of the above-mentioned compounds. When the light-sensitive material of the invention has a plurality of silver halide emulsion layers, it is sufficient that at least one of the layers is a silver halide emulsion layer as described above. It is preferred to use a blue-sensitive emulsion layer, which is formed as the bottom layer (a layer closest to the support), as the silver halide emulsion layer used in the invention. If the light-sensitive material has a plurality of silver halide emulsion layers, not all emulsion layers need have the constitution of the silver halide emulsion layer used in the invention. The spectral sensitizing dye of general formula [I] which is incorporated into the silver halide emulsion layer used in the invention is described below. where X₁, X₂, X₃ and X₄ are each independently a hydrogen atom, a halogen atom, an alkyl group, an alkoxy group, an aryl group or a hydroxy group. Typically the halogen atom is the chlorine, alkyl group contains from 1 to 6 carbon atoms, e.g. methyl or ethyl and the alkoxy group contains from 1 to 6 carbon atoms, e.g. methoxy or ethoxy. Preferably, at least one of X₁, X₂, X₃ and X₄ is a chlorine atom, more preferably, two are chlorine atoms. R₁ and R₂ are, independently, optionally substituted alkyl. Preferably R₁ and R₂ are independently an unsubstituted alkyl group or carboxyl- or sulfo-substituted alkyl group, more preferably carboxyl- or sulfo-substituted alkyl groups, and most preferably sulfoalkyl groups and carboxylalkyl groups each having one to four carbon atoms. R₁ and R₂ may be either identical or different, preferably at least one of them is a carboxyl-substituted alkyl group having one to four carbon atoms. X⁻ is a counter anion, for example halogen ions (such as Br⁻ and I⁻). n is 0 or 1. Spectral sensitizing dyes of general formula [I], may be synthesized, for example as described in British Patent No. 660408, U.S. Patent No. 3149105, Japanese Patent Publication Open to Public Inspection No. 4127/1975 (hereinafter referred to as Japanese Patent O.P.I. Publication) or "The Cyanine Dyes and Related Compounds" by F.M. Hamer, (Interscience Publisher, New York, 1969), paragraphs 32 - 76. Typical examples of spectral sensitizing dyes of general formula [I] which may used in the present invention are listed in Table - 1. In Table - 1, above, NEt₃ represents the following; The preferred amount of spectral sensitizing dye to be used is in the range of from 5 x 10⁻⁶ to 5 x 10⁻² mol/AgX, more preferably 1 x 10⁻⁵ to 1 x 10⁻³ mol/AgX, and most preferably 1 x 10⁻⁴ to 9 x 10⁻⁴ mol/AgX. Known methods may be used to add the spectral sensitizing dye to the emulsion. For example, the sensitizing dye may be dispersed directly in the emulsion, the dye may be added to the emulsion in the form of an aqueous solution, or the dye may be dissolved in a water-soluble solvent, which may be diluted with water if necessary, such as pyridine, methyl alcohol, ethyl alcohol, methyl cellosolve or acetone (or a mixture of these solvents). The use of ultrasonic vibration is effective in dissolving the dyes. Other methods include dissolving the sensitizing dye in a volatile organic solvent, dispersing the resulting solution in a hydrophilic colloid and then adding the dispersion to the emulsion; such a method is described in U.S. Patent No. 3,469,987. Another method involves dispersing a water-insoluble dye in a water soluble solvent and then adding this dispersion to the emulsion; such a method is described in Japanese Patent Examined Publication No. 24185/1971. In addition, the spectral sensitizing dye may be added to the emulsion in the form of a dispersion, obtained from an acid dissolution-dispersion process. The dye may also be added to the emulsion as described in U.S. Patents No. 2,912,345, No. 3,342,605, No. 2,996,287 and No. 3,425,835. The spectral sensitizing dyes of formula [I] may be used independently or in combination. When two or more dyes are used in combination they may be blended into the emulsion at the same time, or on a step-by-step basis. When the dyes are added step by step, the sequence, timing and intervals of addition may be arbitrarily determined. According to the invention, the joint use of a dye of formula I together with other dyes is not restricted. The spectral sensitizing dye contained in the silver halide emulsion layer of the invention may be added at any time during the preparation of the silver halide photographic emulsion. Usually, the spectral sensitizing dye is added after the completion of the first ripening and before the completion of the second ripening. The silver halide grains used in the silver halide emulsion layer may comprise any of silver chloro-bromide, silver iodo-chloride, silver chloro-iodo-bromide, or silver chloride, but the silver halide emulsion layer must have a high silver chloride content containing not less than 80 mol % silver chloride. A silver chloride content of 95 - 100% is preferable. The emulsion may contain silver iodide; however, the preferred content is less than one mol%, more preferably less than 0.5 mol%, and most preferably zero mol %. The preferred content of silver bromide is less than five mol%, more preferably zero mol%. According to the invention, it is preferable that the silver halide grains containing not less than 80 mol% silver chloride form at least 80 weight %, more preferably, 100 weight % of the total silver halide grains contained in the silver halide emulsion layers as a whole. In addition, it is preferred that silver chloride content of each of the emulsion layers containing such silver halide grains is, on average, greater than 80 mol%, more preferably more than 85 mol %. That the silver halide grains contained in the silver halide emulsion layers preferably contain, on average, more than 80 mol % of silver chloride means that it is satisfactory that the silver chloride mole percentage is, on average, more than 80% for the emulsion layers as a whole. Naturally, it is possible some of the layers may have a composition other than the above composition, and that some of the layers may contain silver halide grains (such as pure silver bromide) which do not have the above mole percentage. As mentioned previously, the light-sensitive material of the present invention, which has a plurality of silver halide emulsion layers, may have emulsion layers having a constitution other than that of the silver halide emulsion layers described above for use in the invention. The layers other than those for use in the invention may not necessarily have a high silver chloride content. However, it is preferred that the average silver chloride content for the emulsion layers, as a whole, is more than 80 mol%, and more preferred that every emulsion layer constituting the light-sensitive material has more than 80 mol% silver chloride. In fact, both on an average for all the layers as a whole, and for every individual layer, the silver chloride content is preferably more than 95 mol%. The size of silver halide grains used for the silver halide emulsion layers used in the invention, and for other emulsion layers is represented by the length of an edge of a cube, when the silver halide grain is a cube, or is represented by the length of an edge of a cube having the equivalent volume, when the silver halide grain has a shape other than that a cube, such as a sphere. The average grain size F is determined as shown below; Wherein r i is the diameter of each grain and n i is the number of grains having a grain size of r i . The preferred average grain size of the silver halide grains of the invention is, in terms of the above-mentioned average grain size, less than five µm, more preferably less than three µm, and most preferably less than one µm. The grain size distribution of the silver halide grain may be either the multi-dispersed or the mono-dispersed type; however, a mono-dispersed emulsion is preferred. The term "mono-dispersed" means an emulsion having a coefficient of variation of less than 22%, preferably less than 15% in terms of the size distribution of the silver halide grains contained in the emulsion. The coefficient of variation is a coefficient indicating the range of the grain size distribution and is defined as follows: The grain size may be measured by a variety of methods known in the art. Typical methods are described in the following: Analysis Method of Grain Size, A.S.T.M. Symposium on Light Microscopy, 1955, pp. 94 - 122; The Theory of the Photographic Process by Mees and James, 3rd edition, Chapter 2, published by MacMillan Company (1966). The silver halide grains used may be prepared by, for example, the acid process, the neutra process or the ammonia process The grains may be grown at once, or may be grown after forming seed grains. The method used to form seed grains may be identical to or different from the method used to grow the grains. To prepare the silver halide grains, both halide ions and silver ions may be simultaneously blended together, or to a solution containing one type of ion, the other type of ion may be incorporated. To conform with the critical growth rate of silver halide crystals, silver halide grains may be formed by adding in combination, halide ions and silver ions step by step into a mixing vessel while controlling the pH and pAg. Using this method, mono-dispersed silver halide grains having a regular crystal configuration and substantially identical grain size can be obtained. The halogen composition of grains may be modified by using the conversion method after the grains have been satisfactorily grown up. Any type of silver halide emulsion manufacturing equipment known in the photographic art may be used. In particular, the preferred equipment uses any one of the following methods: a method to introduce both aqueous silver halide solution and aqueous halide salt solution into a hydrophilic colloid, contained in a mixing vessel, via a nozzle immersed in the colloid; a method to continuously vary the concentration of the solution being added to the emulsion; a method, such as ultrafiltration, to remove excess water soluble salts and water in the hydrophilic colloid contained in the mixing vessel, so as to prevent inter-grain distances becoming too large. During the course of preparation of the silver halide emulsion, the grain size, grain configuration, grain size distribution and growth rate of the silver halide grains may be regulated by using a solvent capable of dissolving silver halide. Metal atoms, in the form of metallic ions, may be integrated into the interior and/or onto the surface of each of the silver halide grains used in the silver halide emulsion, by using at least one type of salt, in order to form and/or grow the grains. The type of salt may be selected from cadmium salts, zinc salts, lead salts, thallium salts, iridium salts (or complex salts containing them), rhodium salts (or complex salts containing them), and iron salts (or complex salts containing them), for example. In addition, by subjecting the grains to an adequate reducing atmosphere, the reduction-sensitization nucleus may be integrated into the interior and/or onto the surface of every grain. Excess soluble salts may be either removed from or left in the silver halide emulsion after the silver halide grains have satisfactorily grown. Such salts may be removed as described in Research Disclosure No. 17643. Each silver halide grain used in the silver halide emulsion may have a uniformly distributed silver halide composition, or may be a core/shell grain where the interior and surface of each grain have different silver halide compositions. Cubic-shaped silver halide grains with a high silver chloride content in the silver halide emulsion are readily available. However, by introducing various types of compounds during the formation of the grains, or by an other procedure, grains may be formed which have irregular crystal configurations such as octahedron or tetradecahedron, or regular crystal configurations such as spherical or tabular shape. With these grains, the ratio between the (100) face and the (111) face may be arbitrarily selected. Each grain may have a composite configuration with any of the above configurations, and the emulsion may contain various crystal-configurations of grains. However it is preferred to use cubic grains. The silver halide emulsion described above for use in the invention may be prepared by blending two or more independently prepared types of silver halide emulsion. The silver halide emulsion layers of the present invention contain an auric sensitizer. Suitable auric compounds are, for example, chloroauric acid, sodium chloroaurate and gold potassium thiosulfate. The preferred amount of auric compound to be integrated into the emulsion layer is in the range of from 5 x 10⁻⁷ to 5 x 10⁻³ mol, more preferably 2 x 10⁻⁶ to 1 x 10⁻⁶ mol, even more preferably 2.6 x 10⁻⁶ to 4 x 10⁻⁵ mol, and most preferably 2.6 x 10⁻⁶ to 9 x 10⁻⁶ mol per mol silver halide. Although the time of addition of the auric compound to the silver halide emulsion may be at any stage in the preparation of the emulsion, the preferred time is between the completion of the formation of the silver halide grains and the completion of chemical sensitization. In addition, the auric compound may be added to the emulsion, following the completion of chemical ripening, any time after the addition of a compound known as an anti-fogging agent or a stabilizer, but before the silver halide emulsion is actually applied to form the photographic light-sensitive material. It is preferred that the silver halide emulsion layers contains sulfur sensitizers. Examples of suitable sulfur sensitizers include sodium thiosulfate and thiourea derivatives (such as, diphenylthiourea and allylthiourea). The amount of sulfur sensitizer used is enough to sensitize the silver halide. For example, the preferred amount of sodium thiosulfate to be added is in the range of from 1 x 10⁻⁷ to 1 x 10⁻⁵ mol, more preferably from 2 x 10⁻⁶ to 8 x 10⁻⁶ mol per mol silver halide. Compounds of general formula [II] for use in the silver halide emulsion layers are described below. Examples of five-membered heterocycles formed by Q in general formula [II] include: an imidazole ring, tetrazole ring, thiazole ring, oxazole ring, selenazole ring, benzimidazole ring, naphthoimidazole ring, benzoselenazole ring, naphthoselenazole ring, benzoxazole ring, 1, 3, 4-oxadiazole ring, 1, 3, 4-thiadiazole ring or 1, 3, 4-triazole ring. Preferred compounds of general formula [II] are those of formulae [II a] to [II f]. where R₁₁ is a hydrogen atom, an alkyl group, an aryl group, a halogen atom, a carboxyl group, a sulfo group, and salts thereof, an amino group and an alkoxy group, and Z is -NH-, -O- or -S-. where Ar is a phenyl group, a naphthyl group or a cyclohexyl group, and R₁₂ is a hydrogen atom, an alkyl group, an alkoxy group, a carboxyl group and a sulfo group, each of which may be substituted with Ar, or salts thereof, as well as a hydroxy group, amino group, acylamino group, carbamoyl group and sulfamide group. Where R₁₃ is hydrogen, alkyl, aryl, alkenyl, cycloalkyl, -SR₁₄, or or -NHSO₂R₁₇ or heterocyclic group; R₁₄ and R₁₅ are independently hydrogen, alkyl or aryl; R₁₆ and R₁₇ are independently alkyl or aryl. Examples of alkyl groups represented by any of R₁₃, R₁₄, R₁₅, R₁₆, and R₁₇ in general formulae [II c] and [II d] include a methyl group, benzyl group, ethyl group or propyl group. Examples of aryl groups represented by any of the similar symbols include a phenyl group or naphthyl group. Examples of alkenyl groups represented by R₁₃ include propenyl group. Examples of cycloalkenyl groups represented by R₁₃ include cyclohexyl group. Examples of heterocyclic groups represented by R₁₃ include a furyl group or a pyridinyl group. An alkyl group and aryl group independently represented by any of R₁₃, R₁₄, R₁₅, R₁₆ and R₁₇ may have a substituent. Also, an alkenyl group, cycloalkyl group and heterocyclic group respectively represented by R₁₃ may have a substituent. M is a hydrogen atom, alkali metal atom or ammonium group. where R₁₈ is a hydrogen atom, alkyl group, cycloalkyl group, alkenyl group, aryl group, -COR₁₉ and -SOR₂₀, and R₁₉ and R₂₀ are independently an alkyl group, aryl group, cycloalkyl group or alkenyl group. Where, R₂₁ and R₂₂ are independently a group identical to that represented by R₁₄ or R₁₅ in general formulae [II a] and [II b]. Typical compounds of general formulae [II a] to [II f] are listed below. The above compounds may generally be synthesized by referring to the following: Journal of Chemical Society 49, 1748, 1927; Journal of Organic Chemistry 39, 2469, 1965; Japanese Patent O.P.I. Publication 89034/1975; Annalen Chimie, 44-3, 1954; Japanese Patent Examined Publication No, 28496/1965; Chemical Berichte 20, 231, 1887; and U.S. Patent No. 3,259,976. In addition, the compounds of general formula [II] may include those compounds described in, for example, Chemical and Pharmaceutical Bulletine, Tokyo, Vol. 26. pp 314 (1978); Japanese Patent O.P.I. Publication No. 79436/1980; Berichte der Deutchen Chemischen Gesellschaft, 82, pp. 121 (1948); U.S. Patents No. 2,843,491 and No. 3,017,270; British Patent No. 940,169; Japanese Patent O.P.I. Publications No. 102639/1981 and No. 59463/1980; Journal of American Chemical Society, 44, pp. 1502 - 1510. To incorporate a compound of general formula [II] into the silver halide emulsion layers, the compound may firstly be dissolved in water or an organic solvent (such as methanol or ethanol), which is miscible with water, and then the solution is incorporated into the emulsion. The compounds of formula [II] may be used either independently or in combination with other compounds of formula [II], or with a stabilizer or a fogging restrainer not of formula [II]. The various stabilizers and fogging restrainers to be used in the invention are described later. Compound [II] may be present while the silver halide grains are forming or may be added after their formation, it is preferred that compound [II] is added on completion of the formation of the silver halide grains. The timing of addition may be at or during any of the following times: from completion of formation of the silver halide grain nuclei up to the initiation of chemical ripening; during chemical ripening; on completion of chemical ripening; after completion of chemical ripening up to application of the emulsion. Preferably, the compound [II] is added to the emulsion during or on completion of chemical ripening, or from completion of chemical ripening up to application of the emulsion. In adding compound [II], the required amount may be added to the emulsion all at once or on a step-by-step basis. Compound [II] may be added directly to the silver halide emulsion (or to the silver halide emulsion coating solution) or may firstly be added to the coating solution for the non-photosensitive hydrophilic colloidal layers adjacent to the silver halide emulsion layer and then allowed to diffuse into the silver halide emulsion layer. Usually, the amount of compound (II) to be added is in the range of from 1 x 10⁻⁶ to 1 x 10⁻¹ mol, preferably from, 1 x 10⁻⁵ to 1 x 10⁻² mol, and more preferably from 10 x 10⁻⁴ to 1 x 10⁻³ per mol silver halide. Some compounds of formula [II], known as stabilizing agents or fog-restrainers, are described, for example, in British Patent No. 1,273,030, Japanese Patent Examined Publications No. 9936/1983 and No. 27010/1985 and Japanese Patent O.P.I. Publications No. 102639/1976, No. 22416/1978, No. 59463/1980, No. 79436/1980 and No. 232342/1984. When using the light-sensitive material of the invention as a color photographic light-sensitive material, a dye-forming coupler which is capable of coupling with the oxidized product of a primary aromatic amine developing agent (for example, a derivative of p-phenylenediamine, or a aminophenol) and of forming a dye in the color developing may be used. Each emulsion layer making up the light-sensitive material may have a coupler. However, as mentioned previously, a yellow coupler is preferably contained in the silver halide emulsion layer. Examples of a yellow coupler which may be used in the invention include those described in U.S. Patent No. 2,186,849, No. 2,322,027, No. 2,728,658, No. 2,875,057, No. 3,265,506, No. 3,277,155, No. 3,408,194, No. 3,415,652, No. 3,447,928, No. 3,664,841, No. 3,770,446, No. 3,778,277, No. 3,849,140 and No. 3,894,875, British Patent No. 778,089, No. 808,276, No. 875,476, No. 1,402,511, No. 1,421,126 and No. 1,513,832, Japanese Patent Examined Publication No. 13576/1974, Japanese Patent O.P.I. Publications No. 29432/1973, No. 66834/1973, No. 10736/1974, No. 122335/1974, No. 28834/1975, No. 132926/1975, No. 138832/1975, No. 3631/1976, No. 17438/1976, No. 26038/1976, No. 26039/1976, No. 50734/1976, No. 53825/1976, No. 755211976, No. 89728/1976, No. 102636/1976, No. 107137/1976, No. 117031/1976, No. 122439/1976, No. 143319/1976, No. 9529/1978, No. 82332/1978, No. 135625/1978, No. 145619/1978, No. 23528/1979, No. 48541/1979, No. 655035/1979, No. 133329/1979, and No. 598/1980. Suitable magenta couplers include those described in U.S. Patent No. 1,969,479, No. 2,213,986, No. 2,294,909, No. 2,338,677, No. 2,340,703, No. 2,359,332, No. 2,411,951, No. 2,435,550, No. 2,592,303, No. 2,600,788, No. 2,618,641, No. 2,619,419, No. 2,673,801, No. 2,691,659, No. 2,803,554, No. 2,829,975, No. 2,866,706, No. 2,881,167, No. 2,895,826, No. 3,062,653, No. 3,127,269, No. 2,881,167, No. 2,895,826, No. 3,062,653, No. 3,127,269, No. 3,214,437, No. 3,253,924, No. 3,311,476, No. 3,419,391, No. 3,486,894, No. 3,519,429, No. 3,558,318, No. 3,617,291, No. 3,684,514, No. 3,705,896, No. 3,725,067, and No. 3,888,680, British Patent No. 720,284, No. 737,700, No. 813,866, No. 892,886, No. 918,128, No. 1,019,117, No. 1,042,832, No. 1,047,612, No. 1,398,828 and No. 1,398,979, West German Patent Official Gazette No. 814,996 and No. 1,070,030, Belgium Patent No. 724,427, Japanese Patent O.P.I. Publication No. 60479/1971, No. 29639/1974, No. 111631/1974, No. 129538/1974, No. 13041/1975, No. 116471/1975, No. 159336/1975, No. 3232/1976, No. 3233/1976, No. 10935/1976, No. 16924/1976, No. 20826/1976, No. 26541/1976, No. 30228/1976, No. 36938/1976, No. 37230/1976, No. 37646/1976, No. 39039/1976, No. 44927/1976, No. 104344/1976, No. 105820/1976, No. 108842/1976, No. 112341/1976, No. 112342/1976, No. 112343/1976, No. 112344/1976, No. 117032/1976, No. 126831/1976, No. 31738/1977, No. 9122/1978, No. 35122/1978, No. 75930/1978, No. 86214/1978, No. 25835/1978, No. 123129/1978 and No. 56429/1979. Suitable cyan couplers include those described in U.S. Patent No. 2,306,410, No. 2,356,475, No. 2,362,598, No. 2,367,531, No. 2,369,929, No. 2,423,730, No. 2,474,293, No. 2,476,008, No. 2,498,466, No. 2,545,687, No. 2,728,660, No. 2,772,162, No. 2,895,826, No. 2,976,146, No. 3,002,836, No. 3,419,390, No. 3,446,622, No. 3,476,563, No. 3,737,316, No.3,758,308 and No. 3,839,044, British Patent No. 478,991, No. 945,542, No. 1,084,480, No. 1,377,233, No. 1,388,024 and No. 1,543,040, Japanese Patent O.P.I. Publications No. 37425/1972, No. 10135/1975, No. 25228/1975, No. 112038/1975, No. 117422/1975, No. 130441/1975, No. 6551/1976, No. 37647/1976, No. 52828/1976, No. 108841/1976, No. 109630/1978, No. 48237/1979, No. 66129/1979, No. 131931/1979 and No. 32071/1980. Couplers capable of forming a coupling product having a maximum spectral absorption wavelength in the range of from 700 to 854 µm include those described in Japanese Patent Examined Publication No. 24849/1977 and Japanese Patent O.P.I. Publication No. 125836/1978, No. 129036/1978, No. 21094/1980, No. 21095/1980 and No. 21096/1980. The coupler is normally introduced into the silver halide emulsion by using a high boiling organic solvent and a dispersing agent. Into the silver halide photographic light-sensitive matrix of the invention may be incorporated various compounds in addition to the compounds represented by general formula [II], in order to prevent fogging during the manufacture, storage developing of the material, and to stabilize the photographic performance thereof. Suitable anti-fogging agents and stabilizers, include tetrazaindenes; azoles such as benzothiazolium salts, nitroindazoles, nitrobenzimidazoles, chlorobenzimidazoles, bromobenzimidazoles, aminotriazoles, benzotriazoles, nitrobenzotriazoles, benzenethiosulfinic acid; benzenesulfinic acid; amide benzenesulfonate; hydroquinone derivatives; aminophenol derivatives; gallic derivatives; and ascorbic derivatives. The scope of useful hydrophilic colloids for forming hydrophilic colloidal layers which comprise a silver halide photographic light-sensitive material of the invention is not specifically limited. Suitable binders for the light-sensitive and non-light-sensitive layers include gelatin; colloidal albumin, agar-agar, gum arabic, dextran, alginic acid; derivative of cellulose such as cellulose acetate hydrolyzed to have 19 - 26 % acetyl content; polyacrylic amide, imidopolyacrylic amide, casein; vinyl alcohol polymers, containing urethanecarboxylic group or cyanoacetyl group, such as vinyl alcohol-vinyl cyanoacetate copolymer; polyvinyl alcohol-polyvinyl pyrrolidinone, hydrolyzed polyvinyl acetate; and a polymer, obtained by polymerization of protein or saturated acylated protein and a monomer having a vinyl group, such as polyvinyl pyridine, polyvinyl amine, polyamineethylmethacrylate and polyethylene imine. Examples of suitable hardeners are as follows: organic hardeners such as vinyl sulfonic, acryloyl and ethyleneimine hardeners and inorganic hardeners such as chromic alum and potash alum. The hardener may be used, independently or in combination with two or more hardeners. The light-sensitive material of the invention may also contain a surface active agent as a coating auxiliary, anti-static agent, slide-improvement emulsification dispersion or an adhesion inhibitor. Examples of suitable surface active agents include saponin, sodium dodecylbenzenesulfonate, sodium sulfosuccinate, and those disclosed in Japanese Patent O.P.I. Publications No. 46733/1974, No. 10722/1974 and No. 16525/1975. As the ultraviolet absorbent, benzotriazole compounds, thiazolidone compounds, acrylonitrile compounds and benzophenone compounds, for example, may be used. Also, the light-sensitive material may contain fluorescent whitening agents, oxidation inhibitors and anti-stain agents. Typically, to prepare the light-sensitive material of the invention, photographic additives are incorporated into the silver halide emulsions, which are then applied to the support to form the silver halide emulsion layers. When the coats of the similar layers are formed, they may be formed via a subbing layer or intermediate layers. Examples of suitable supports are as follows: supports made of paper, glass, cellulose acetate, cellulose nitrate, polyester, polyamide and polystyrene; and supports made of more than two types of substrates bonded together, such as a lamination of paper and polyolefin (such as polyethylene or polypropylene). To improve adhesion to the silver halide emulsion layer, such a support is usually subjected to various surface improvement treatments, such as electron impact treatment, or subbing treatment to provide a subbing layer. To apply, and then dry the silver halide photographic emulsion to the support, known coating processes such as dip coating, roller coating, bead coating, curtain and flow coating may be used. When the invention is embodied as a color photographic light-sensitive material, developing is carried out using a conventional color developing process. Examples of suitable color developers used for the color developing are as follows: primary aromatic amine compounds, such as N-diethyl-p-phenylenediamine, N-ethyl-N-hydroxyethylparaphenylenediamine, 4-(N-ethyl-N-hydroxyethyl) amino-2-methylaniline, 4-(N-ethyl-N-β-methaneesulfonamidethyl) amino-2-methylaniline, 4-(N,N-diethyl) amino-2-methylaniline, 4-(N-ethyl-N-methoxyethyl) amino-2-methylaniline and sulfates, hydrochlorides, sulfates and p-toluenesulfonates of the above primary aromatic amine compounds. The color developer may also contain, in addition to the above-mentioned color developing agent and N, N-dialkylhydroxylamine salt serving as a preservative, various photographic development additives. Examples of suitable additives are as follows: alkali agents such as sodium hydroxide, potassium hydroxide, sodium carbonate, potassium carbonate, sodium metaborate and potassium tertiary phosphate; pH buffers such as sodium phosphate, potassium dihydrogen phosphate, disodium hydrogen phosphate and potassium bicarbonate; and organic solvents such as methanol, ethylene glycol and triethanolamine. Benzyl alcohol may be present in the color developer solution as a color-forming improvement agent but it preferably is not present. A limited amount of benzyl alcohol may be contained in a color developer. The preferred amount of benzyl alcohol contained in color developer is from zero to five mℓ, more preferably from zero to three mℓ, per ℓ color developer. It is particularly preferred that the color developer contains, in addition to N,N-dialkylhydroxylamine, a combination of sulfites, such as sodium sulfite and potassium sulfite, in order to improve the shelf life of the color developer. The amount of sulfite is preferably from 0.05 to 12 g, more preferably from, 0.1 to 0.3 g, per ℓ color developer. Furthermore, it is preferred that the amount of water soluble bromide, serving as a development inhibitor and contained in the color developer, is as small as possible, more preferably, that no such bromide is contained in the developer. The term "rapid processing" usually refers to color developing where the processing time is less than 90 seconds, and where the temperature of the color developer is from 20 to 50°C, preferably from 30 to 40°C. In rapid processing, after a dye image has been formed by color developing, it is necessary to remove the undeveloped silver halide and developed silver image by means of bleach-fixing. The bleach-fixing time is preferably less than 90 seconds, more preferably less than 60 seconds. The preferred bleaching agent for the developed silver is a metal salt of a multivalent organic salt, which is typified by a ferric salt of an organic acid. Examples of such a salt are the iron salts of the following acids: nitrilotriacetic acid, diethylenetriaminepentaacetic acid, ethylene glycol bis (aminoethyl ether) tetraacetic acid, diaminopropanol tetraacetic acid, N-(2-hydroxyethyl) ethylenediamine triacetic acid, ethyliminodipropionic acid, cyclohexanediaminetetraacetic acid, and ethylenediaminetetraacetic acid. Other useful iron salts include the salts of polycarboxylic acids, disclosed in Japanese Patent O.P.I. Publication No. 107737/1974, such as of oxalic acid, malonic acid, succinic acid, malic acid, tartaric acid, citric acid and salicylic acid. In addition, the salts of multivalent metals such as a cupric salt and a cobalt salt may be used. Furthermore, inorganic multivalent metal salts such as ferric chloride and ferric sulfate may be used. As a suitable fixer, thiosulfate or thiocyanate may be used, and the fixer may contain a water soluble alkali metal salt such as potassium bromide or sodium iodide, or ammonium bromide or iodide as described in Japanese Patent O.P.I Publication No. 101934/1973. Each process of film-prehardening, neutralization, rinsing and stabilizing may also be carried out in combination with color developing and bleach-fixing. EXAMPLES Example 1 A silver halide emulsion, comprising silver chloro-bromide grains with an average grain size of 0.6 µm and containing uniformly distributed three mol% silver bromide, was prepared by the double jet method. Sodium thiosulfate was added to the emulsion at a rate of 3.5 x 10⁻⁶ mol per mol AgX, and, one minute after addition, chloroauric acid was added, at the rate at 2.7 x 10⁻⁶ mol per mol AgX: the emulsion was then subjected to chemical ripening. The emulsion was divided into portions and one spectral sensitizing dye listed in Table - 2 was added to each portion of emulsion at a rate of 3 x 10⁻⁴ mol per mol AgX. Each spectrally sensitized emulsion was then further divided into portions; some of the emulsions were left unchanged as indicated in Table - 2, while a mercapto compound or fogging restrainer listed in Table - 2 was added to each of the remaining emulsions at a rate of 1.2 x 10⁻³ mol per mol AgX. In this way, blue-sensitive silver chloro-bromide emulsions were prepared. Each blue-sensitive silver chloro-bromide emulsion was applied to form a coat, that is one of the photographic structural layers. Using this procedure the samples listed in Table - 2 were prepared. Specifically, each sample was prepared in the following manner; The support was made of paper with a specific gravity of 170 g/m², having a lamination of polyethylene on one face, and a lamination of polyethylene containing 11 weight % of anatase-type titanium dioxide on the other face. The lamination of titanium dioxide-containing polyethylene was subjected to corona discharge and then the following layers were formed thereon by coating. The amount of addition is, unless otherwise specified, the amount per one m² sample. Layer 1 A layer containing 1.2 g gelatin, 0.28 g (silver-converted value) of the blue-sensitive silver chloro-bromide emulsion, as well as 0.50 g dinonyl phthalate (DNP) in which 0.78 g yellow coupler (Y - 1), 0.35 g the image stabilizer STB - 1 and 0.04g antistain agent HQ - 1 had been dissolved. Layer 2 An intermediate layer containing 0.7 g gelatin and 0.05 g di-2-ethylhexyl phthalate (DOP) in which 15 mg anti-irradiation dye (AI - 1), 10 mg anti-irradiation dye (AI - 2) and 0.05 g HQ - 1 had been dissolved. Layer 3 A layer containing 1.25 g gelatin, 0.29 g of green-sensitive silver chloro-bromide emulsion (Note - 1: AgBr, 1.2 mol%; average grain size, 0.40 m) and 0.30 g DOP in which 0.45 g magenta coupler (M - 1), 0.8 g light-stabilizer STB - 2, 0.15 g light-stabilizer STB - 3 and 0.01 g HQ - 1 had been dissolved. Layer 4 An intermediate layer containing 1.2 g gelatin and 0.35 g DOP in which 0.08 g HQ - 1, 0.4 g ultraviolet absorbent (UV - 1) and 0.2 g ultraviolet absorbent (UV - 2) had been dissolved. Layer 5 A layer containing 1.4 g gelatin, 0.20 g red-sensitive silver chloro-bromide emulsion (Note - 2: AgBr, five mol%; average grain size, 0.65m) and 0.20 g DOP in which 0.25 g cyan coupler (C - 1), 0.25 g cyan coupler (C - 2), 0.15 g light-stabilizer STB - 1 and 0.01 g HQ - 1 had been dissolved. Layer 6 A layer containing 1.0 g gelatin and 0.20 g DOP in which 0.30 g UV - 1 and 0.05 g polyvinyl pyrolidone had been dissolved. Layer 7 A layer containing 0.05 g gelatin. In addition, the following hardeners were added to the emulsions for the layers immediately before the coating process; sodium 2,4-dichloro-6-hydroxy-s-triazine for the above-mentioned layer, and a reaction product prepared by allowing (tetrakisvinylsulfonylmethyl) methane and taurine sodium to react at a molar ratio of 4 : 1. (Note-1): Green-sensitive silver chloro-bromide emulsion Sodium thiosulfate was added to the emulsion at a rate of 3.5 x 10⁻⁵ mol per mol silver halide in order to effect chemical sensitization; the optical sensitization was effected with green sensitizing dye (GSD - 1). Also, the stabilising agent 4-hydroxy-6-methyl-1, 3, 3a, 7-tetrazaindene compound was added to the emulsion at a rate of 1.2 g per mol silver halide. (Note-2): Red-sensitive silver chloro-bromide emulsion Sodium thiosulfate was added to the emulsion at a rate of 3.5 x 10⁻³ mol per mol silver halide in order to effect chemical sensitization; the optical sensitization was effected with red sensitizing dye (RSD - 1). Also the stabilizing agent 4-hydroxy-6-methyl-1, 3, 3a, 7-tetrazaindene compound was added to the emulsion at a rate of 1.2 g per mol silver halide. Each of the prepared samples was subjected to stepwise exposure with white light, then treated in the processing steps specified below. Some of the samples were stored at a temperature of 50° and relative humidity of 80% for six days, then subjected to the procedure mentioned above. Processing steps Color developing 35°C 45 sec Bleach-fixing 35°C 50 sec Washing 30 - 24°C 90 sec Drying 50 - 70°C 60 sec The compositions of color developer and bleach-fixer used were as follows. (per one ℓ solution) (Color developer) Pure water 80 mℓ N,N-diethylhydroxylamine 6 mℓ Potassium sulfite 2.0 g N-ethyl-N-β-methanesulfonamidmethyl-3-methyl-4-aminoaniline sulfate 5 g Sodium tetrapolyphosphate 2 g Potassium carbonate 30 g Triethanol amine 8.3 g Pure water was added into the above ingredients to prepare one ℓ solution, and the pH value was adjusted to 10.08. (Bleach-fixer) Pure water 800 mℓ Ammonium ferric (II) ethylenediaminetetraacetate 65 g Bisodium ethylenediaminetetraacetate 5 g Ammonium thiosulfate 85 g Sodium metabisulfite 2 g Sodium chloride 10 g Hydroxylamine sulfate 2 g Pure water was added into the above ingredients to prepare one ℓ solution, and the pH value was adjusted to 6.2 with dilute sulfuric acid. The density of each of the developed samples was measured using monochromatic blue light. Then, the sensitivity was determined using the characteristic curve obtained from the density measurements. In addition, each of the undeveloped samples was developed, using a color developing time of 100 sec, in order to measure the fogging density. The results are listed in Table - 2. Sample No. Sensitizing dye Compound Before storage After 6 days storage at 50°C, 80% RH Remarks Sensitivity Fogging Sensitivity Fogging 1 Comparison A - 100 0.20 50 0.40 Comparison 2 Comparison B - 110 0.25 90 0.45 " 3 I-12 - 130 0.24 110 0.44 " 4 I-1 - 120 0.25 100 0.45 " 5 I-5 - 115 0.25 95 0.45 " 6 I-4 - 120 0.24 100 0.44 " 7 Comparison B E 90 0.20 80 0.25 " 8 " F 90 0.10 80 0.25 " 9 " II a-3 95 0.10 90 0.20 " 10 " II a-4 95 0.10 90 0.20 " 11 " II a-7 95 0.10 90 0.20 " 12 I-12 E 120 0.20 100 0.25 " 13 I-12 II a-2 130 0.03 130 0.03 Invention 14 I-12 II a-4 130 0.03 130 0.03 " 15 I-12 II a-5 130 0.03 130 0.03 " 16 I-1 F 110 0.20 105 0.25 Comparison 17 I-1 II a-1 120 0.02 118 0.02 Invention 18 I-1 II a-6 120 0.02 118 0.02 " 19 I-1 II a-8 120 0.02 118 0.02 " Sensitivity is the relative sensitivity in proportion to the sensitivity, 100, of sample No. 1. The results in Table - 2 illustrate the following. From samples 1 to 6 it is apparent that spectral sensitizing dyes independently having two benzothiazole nuclei are highly sensitive to AgCl, but lead to serious fogging and desensitization, with even more severe fogging forming on extended storage. Results were obtained by comparing sample No. 1, containing a sensitizing dye having benzoselenazole nuclei, with each of samples No. 2 to 6 each containing a sensitizing dye having benzothiazole nuclei. In sample 7 to 19, spectral sensitizing dyes having a benzothiazole nucleus were used and compounds for restraining fog-desensitization were added before and after storage. In samples 9 to 11, in which a comparative spectral sensitizing dye having a benzthiazole nucleus and a naphthothiazole nucleus was used, desensitization caused by storage was a little reduced, and, desensitization before storage and fog increases before and after storage were still caused. In addition, it should be noted that in the comparison samples, pre-storage desensitization is quite significant. Though comparable to samples according to the invention in terms of the degree of desensitization on storage, some of the comparison samples show inferior fog-restraining effects. Also, though comparable to the samples of the invention in terms of fog-restraining effects, some of the comparison samples show worse desensitization. In summary, no comparison sample is more effective than a sample of the invention. Even with samples 12 to 19 containing a spectral sensitizing dye used in the invention, a sample having a compound other than that used in the invention shows a difference between pre-storage and post-storage fogging sensitivities. In contrast, samples 13 to 15 and samples No. 17 to 19, all containing a sensitizing dye and a compound used in the invention, not only maintain their original level of sensitivity obtained with the spectral sensitizing dye and show only low amounts of fogging, but also the effects of the dye and compound are well maintained even after prolonged storage. These results cannot be readily expected from the effects obtained from the independent use of a sensitizing dye or a compound used in the invention. Example - 2 A similar procedure to that described for Example 1 was used except that the rate of addition of compound was 6.0 x 10⁻⁴ mol per mol AgX. The results are given in Table - 3. Sample No. Sensitizing dye Compound Before storage After 6 days storage at 50°C, 80% RH Remarks Sensitivity Fogging Sensitivity Fogging 20 Comparison B II b-2 100 0.10 95 0.20 Comparison 21 " II b-4 100 0.10 95 0.20 " 22 I-12 II b-2 130 0.02 130 0.20 Invention 23 I-12 II b-5 130 0.02 130 0.02 " 24 I-12 II b-6 130 0.02 130 0.02 " 25 I-12 II b-7 125 0.03 123 0.03 " 26 I-12 II b-8 132 0.02 130 0.02 " 27 I-12 II b-9 128 0.02 129 0.03 " 28 I-5 II b-1 113 0.03 113 0.03 " 29 I-5 II b-2 115 0.03 114 0.03 " 30 I-5 II b-4 113 0.03 113 0.03 " 31 I-17 II b-2 118 0.02 115 0.02 " 32 I-17 II b-8 115 0.02 116 0.02 " Example 3 A similar procedure to that described for Example - 1 was used except that the rate of addition of compounds was 5.8 x 10⁻⁴ mol/mol AgX. The results are given in Table - 4. It can be seen that results identical to those obtained in Example 1 were achieved by using a combination of a sensitizing dye used in the invention and a mercapto compound of formula [II c] used in the invention. Sensitivity values are relative to the pre-storage sensitivity of sample 33 which is assumed to be 100. Sample No. Senitizing dye Compound Before storage After 6 day storage at 50°C, 80% RH Remarks Sensitivity Fogging Sensitivity Fogging 33 Comparison B II c-8 100 0.10 95 0.20 Comparison 34 " II c-13 100 0.10 95 0.20 " 35 " II c-16 100 0.10 95 0.20 " 36 I-12 II c-1 130 0.03 130 0.03 Invention 37 I-12 II c-6 130 0.03 130 0.03 " 38 I-12 II c-8 130 0.03 130 0.03 " 39 I-12 II c-13 130 0.03 130 0.03 " 40 I-12 II c-14 130 0.03 130 0.03 " 41 I-2 II c-1 120 0.02 119 0.02 " 42 I-2 II c-8 120 0.02 119 0.02 " 43 I-2 II c-16 120 0.02 119 0.02 " Example 4 A similar procedure to that of Example - 1 was used except that the rate of addition of compounds was 7.0 x 10⁻⁴ mol/mol AgX. The results are given in Table - 5. Results identical to those obtained in Example - 1 were achieved by using a combination of a sensitizing dye used in the invention and a mercapto compound of formula [II d] used in the invention. Sensitivity values are relative to the pre-storage sensitivity of sample 33 which is assumed to be 100. Sample No. Sensitizing dye Compound Before storage After 6 day storage at 50°C, 80% RH Remarks Sensitivity Fogging Sensitivity Fogging 44 Comparison B II d-1 100 0.10 95 0.20 Comparison 45 " II d-4 100 0.10 95 0.20 " 46 I-12 II d-9 130 0.02 130 0.02 Invention 47 I-12 II d-2 130 0.02 130 0.02 " 48 I-12 II d-13 130 0.02 130 0.02 " 49 I-6 II d-9 115 0.03 114 0.03 " 50 I-6 II d-6 113 0.03 111 0.04 " 51 I-6 II d-12 115 0.03 114 0.03 " Example 5 A similar procedure to that of Example - 1 was used except that the amount of compounds used was 8.2 x 10⁻⁵ mol/mol AgX. The results are given in Table - 6. Results identical to those of Example - 1 were achieved by using a combination of a sensitizing dye used in the invention and a mercapto compound of formula [II e] used in the invention. Sensitivity values are relative to the pre-storage sensitivity of sample 52 which is assumed to be 100. Sample No. Sensitizing dye Compound Before storage After 6 day storage at 50°C, 80% RH Remarks Sensitivity Fogging Sensitivity Fogging 52 Comparison B II e-4 100 0.10 95 0.20 Comparison 53 " II e-6 100 0.10 95 0.20 " 54 I-12 II e-2 125 0.02 124 0.03 Invention 55 I-12 II e-4 125 0.02 125 0.02 " 56 I-12 II e-6 125 0.02 125 0.03 " 57 I-2 II e-1 120 0.03 118 0.04 " 58 I-2 II e-3 120 0.03 118 0.04 " 59 I-2 II e-7 120 0.03 118 0.03 " Example 6 A similar procedure to that of Example - 1 was used except that the amount of compounds used was 3.0 x 10⁻⁵ mol/mol AgX. The results are given in Table - 7. Results identical to those of Example - 1 were achieved by using a combination of a sensitizing dye used in the invention and a mercapto compound of formula [II-f] used in the invention. Sensitivity values are relative to the pre-storage sensitivity of sample 60 which is assumed to be 100. Sample No. Sensitizing dye Compound Before storage After 6 day storage at 50°C, 80% RH Remarks Sensitivity Fogging Sensitivity Fogging 60 Comparison B II f-1 100 0.10 95 0.20 61 " II f-4 100 0.10 95 0.20 62 I-12 II f-1 120 0.02 120 0.02 63 I-12 II f-5 120 0.02 120 0.02 64 I-12 II f-6 120 0.02 120 0.02 65 I-1 II f-1 120 0.03 119 0.03 66 I-1 II f-4 120 0.03 119 0.03 67 I-1 II f-5 120 0.03 119 0.03 Example 7 A similar procedure to that described for Example - 1 was used except that various combinations, as shown in Table - 8, of sensitizing dye and mercapto compound were used, and that some samples were stored for seven days at 50°C and 32 %RH. Sensitivity values are relative to the pre-storage sensitivity of sample 60 which is assumed to be 100. Under high-temperature and low-humidity storage conditions, the increase in both sensitivity and fogging is apparent. Even samples containing a compound used in the invention, for example sample 69, but also containing sensitizing dye not used in the invention shows insufficient inhibition of increases in sensitivity and decreases in fogging. In contrast, samples containing both the sensitizing dye used in the invention and a mercapto compound used in the invention show reduced variation both in sensitivity and fogging. This means that the samples of the invention have improved shelf life. In particular it is apparent that use of a compound of general formula [II b] is especially effective in inhibiting increases in fogging. With each of samples 69, 72 and 80, two types of samples, that is, pre-storage and post-storage samples, were exposed through a color negative film, and subjected to developing as described in Example - 1. Each of the pre-storage samples, samples 72 and 80, provided a satisfactory color print, though sample 69 appeared rather yellowish. In contrast, post-storage sample No. 69 provided a poor color print whose overall area was yellowish. Both sample 72 and 80, whether after or before storage, provided color prints of equal image quality. On thorough examination of the white area of the print prepared with either sample 72 or 80, though both samples were identical to each other in terms of fogging, sample 72 was a little more yellowish. The possible cause of this is that some of the sensitizing dye remains in the developed light-sensitive material. Thus, it can be seem that of the sensitizing dyes of general formula [I], those having alkyl groups represented respectively by R₁ and R₂ one of which is a sulfoalkyl group and the other is a carboxyalkyl group, are especially advantageous in terms of rapid processing.

Claims: A silver halide photographic light-sensitive material comprising a support having thereon at least one silver halide emulsion layer comprising (a) silver halide grains comprising not less than 80 mol% of silver chloride, (b) at least one optical sensitizing dye represented by the following general formula [I], (c) at least one compound represented by the following general formula [II]: wherein X₁, X₂, X₃ and X₄ are each independently a hydrogen atom, a halogen atom, an alkyl group, an alkoxy group, an aryl group or a hydroxy group; R₁ and R₂ are each independently an optionally substituted alkyl group; X⁻ is a counter anion and n is 0 or 1, wherein Q is an atomic group necessary to complete a five-membered heterocyclic ring, a five-membered heterocyclic ring condensed with a benzene ring or a 1, 3, 5- triazine ring and M is a hydrogen atom, an alkali metal atom or an ammonium group, and (d) a gold sensitizer A silver halide photographic light-sensitive material according to claim 1, wherein Q is an atomic group necessary to complete a five-membered heterocyclic ring or a five-membered heterocyclic ring condensed with a benzene ring. A silver halide photographic light-sensitive material according to claim 1, wherein Q is an atomic group necessary to complete a tetrazole ring, 1,3,4-oxadiazole ring, 1,3,4-diazole ring or 1,3,4-triazole ring. A silver halide photographic light-sensitive material according to claim 1, wherein Q is an atomic group necessary to complete a tetrazole ring. A silver halide photographic light-sensitive material according to any one of the preceding claims, wherein said silver halide emulsion layer contains said optical sensitizing dye represented by the general formula [I] in an amount of from 5 x 10⁻⁶ to 5 x 10⁻² mol per mol of silver halide contained in said silver halide emulsion layer. A silver halide photographic light-sensitive material according to any one of the preceding claims, wherein said silver halide emulsion layer contains said compound represented by the general formula [II] in an amount of from 1 x 10⁻⁶ to 1 x 10⁻¹ mol per mol of silver halide contained in said silver halide emulsion layer. A silver halide photographic light-sensitive material according to any one of the preceding claims, wherein said silver halide emulsion layer contains said silver halide grains comprising not less than 80 mol% of silver chloride in an amount of not less than 80% by weight to the total weight of silver halide grains contained said silver halide emulsion layer. A silver halide photographic light-sensitive material according to claim 7, wherein all the silver halide grains contained in said silver halide emulsion layer are said silver halide grains comprising not less than 80 mol% of silver chloride. A silver halide photographic light-sensitive material according to any one of the preceding claims, wherein the average silver chloride content of all the silver halide grains contained in said silver halide emulsion layer is not less than 80 mol%. A silver halide photographic light-sensitive material according to any one of the preceding claims, wherein said silver halide emulsion layer contains a gold compound in an amount of from 5 x 10⁻⁷ to 5 x 10⁻³ mol per mol of silver halide contained in said emulsion layer. A silver halide photographic light-sensitive material according to any one of the preceding claims, wherein said silver halide emulsion layer contains a sulfur sensitizer.

Inventors: KOJIMA, TAKAAKI, OKUMURA, MITSUHIRO
Applicants: KONICA CORPORATION
Application year: 1987
Main classification: G03C1
IPC codes: G03C1