COMPOSITE RESIN PARTICLES AND PREPARATION THEREOF

Abstract: Composite resin particles each comprising a particulate crosslinked polymer to which a number of substantiary linear, metal-containing polymer chains are chemically bonded. The invention also provide methods for the preparation of said composite resin particles. The present composite resin particles have the self-film forming properties, can give a stable dispersion in an organic solvent or a resinous varnish and are specifically useful in paint industries. The particles are further characterized by having the desired properties of the metal element contained, as, for example, self-catalytic function in crosslinking, excellent biological activities and the like.

Description: The present invention relates to novel crosslinked composite resin particles and preparation thereof. More particularly, the invention concerns composite resin particles which are specifically useful in coating compositions and preparation of such resin particles. Granular resins are supplied in the forms of emulsions, microgels, non-aqueous dispersion resins (NAP resins), powder resins and the like, and have been watched with keen interest in paint industries, especially in aqueous paints, high solid paints and powder paints, because of measuring up to the social requirements of economization of natural resources, energy saving and conservation of good surroundings. However, such a resin is usually crosslinked so that the characteristics of the resin particles can be fully developed, and therefore, when the granular resin is used alone, it is unable to get a uniform or excellent film and the resulted film has a serious drawback of deficient film appearance. Even when the granular resin is combined with a soluble type resin, there is a case that the viscosity of the mixture is unduly increased as compared with that of said soluble type resin alone, due to the considerable interaction between the surfaces of said granules and the soluble type resin. Therefore, great care is often required in the actual use of such combination of resins. Furthermore, since the characteristics of crosslinked resins are greatly influenced by the nature of surfactant used, crosslinking degree and combination of constituting monomers and the like, heretofore proposed crosslinked resin particles are hardly dispersible in such media as aliphatic hydrocarbons, high boiling aromatic hydrocarbons, high polar solvents or the like and, once they make agglomerates, the primary particles hardly become loose. Thus, considerable difficulties are always encountered in the actual application thereof. An acrylic resin for film use is prepared by the two step process in US-A-4,115,480. However, the citation employs only one crosslinking monomer in the first step of the preparation of crosslinked elastomer (description and examples), whereas in the present invention particular polyfunctional monomer (A) and other crosslinking monomer (B) are essential in the preparation of crosslinked polymer particles which bear 1,2-di-substituted, 1,1,2-tri-substituted or 1,1,2,2-tetra-substituted ethylenic groups. In the second step of the preparation of graft polymer chain, the citation merely uses polymerizable monomers, whereas in the present invention polymerizable aromatic compound (D) having selective reactivity towards 1,2-di-substituted. 1,1,2-tri-substituted or 1,1,2,2-tetra-substituted ethylenic groups is included in the employed monomers. In the present invention, a particular emulsifier is used in an emulsion polymerization which is not stated in the citation. Furthermore, the metal elements stated in the citation, i.e. Na, K and Ca, are excluded from the metal elements used in the present invention. GB-A-1,269,297 (citation 4) merely describes a process wherein a synthetic polymer or wood is contacted with a trialkylacryloxystannane and ionizing radiation is applied to graft polymerize the trialkylacryloxystannane onto the polymer or wood. FR-A-2,401,207 discloses chlorinated natural rubber, chlorinated polybutadiene and the like, grafted with linear Sn-containing monomer, prepared by radical polymerization in solution. The said rubber and said polybutadiene are not crosslinked particles. GB-A-1,450,175 discloses a process of forming graft polymer latex particles comprising a first-stage, rubbery crosslinked polymer and a second stage thermoplastic polymerr. In that invention, the first-stage reaction is carried out by an emulsion polymerization of a monomer mixture of (a) a principal monomer system mainly of alkyl acrylate, which may include a minor amount of one or more co-polymerizable monoethylenically unsaturated monomers (b) a crosslinking monomer for said (a) monomer, and (c) a graft-linking monomer, in the presence of an emulsifier such as dioctyl sodium sulfosuccinate, and the second stage reaction is carried out by an emulsion polymerization, in the presence of said first stage polymer particles, with a monomer mixture of (d) a hard alkyl ester of methacrylic acid (80 to 100%) and (e) copolymerizable monoethylenically unsatured monomer (0 to 20%), in the presence of an emulsifier such as dioctyl sodium sulfosuccinate. Therefore, the present invention aims to provide composite resin particles which are free from the drawbacks of the abovementioned resin particles. Thus, a principal aim of the invention is to provide composite resin particles which can be used either singularly or in combination form with any other resins customarily used in the paint industry to give excellent coating compositions with good application characteristics and storage stability and capable of obtaining a uniform coating with excellent appearance. An additional aim of the invention is to provide composite resin particles having self catalytic function in crosslinking or having excellent biological activities. The inventors have now found that composite resin particles each of which comprises a particulate crosslinked polymer to which a number of substantially linear metal-containing polymer chains are chemically bonded are quite useful in the paint industry because of having comparatively lower solution viscosities, being able to give a uniform coating even when used alone, and having excellent compatability with other resins and solvents, and that the abovesaid composite resin particles have a self-catalytic function in crosslinking or useful biological activities depending on the type of metallic element contained, and on the basis of these findings, the present invention has been accomplished. The present invention provides a process for preparing composite resin particles each comprising a particulate crosslinked polymer to which substantially linear, metal-containing polymer chains are chemically bonded, which comprises first effecting an emulsion polymerization of a monomer mixture of (A) a polyfunctional monomer having one or more mono-substituted or 1, 1-di-substituted ethylenic groups and one or more 1,2-di-substituted, 1,1,2-tri-substituted or 1,1,2,2-tetra-substituted ethylenic groups, (B) a crosslinking monomer having two or more mono-substituted or 1,1-di-substituted ethylenic groups or a combination of two monomers each having one or more mono-substituted or 1,1-di-substituted ethylenic groups and a mutually reactive functional group, and (C) polymerizable monomers other than said (A) and (B) and excluding polymerizable aromatic compounds, in the presence of an acrylic, polyester, alkyd or epoxy resin having in its molecule an amphoionic group of the formula: wherein R represents C₁ to C₆ alkylene or phenylene and Y⁻ represents COO⁻ or SO₃, as an emulsifier, to obtain an emulsion of crosslinked polymer particles still having 1,2-di-substituted, 1,1,2-tri-substituted or 1,1,2,2-tetra-substituted ethylenic groups in free state in the polymer, and subsequently effecting a graft-polymerization of said crosslinked polymer particles with a monomer mixture of (D) a polymerizable aromatic compound, to which 1,2-di-substituted, 1,1,2-tri-substituted or 1,1,2,2-tetra-substituted ethylenic groups have selective reactivity, (E) a metal-containing monomer, the metal excluding alkali metals and alkaline earth metals, and (F) other polymerizable mono-functional monomers, thereby forming substantially linear metal-containing polymer chains chemically bonded to said crosslinked polymer particles. The present composite resin particles have a core-shell structure, the core portion being composed of crosslinked polymer and having a mean diameter of 0.01 to 10µ and the shell portion being composed of substantially linear metal-containing polymer, one end of the respective polymer chain being chemically bonded to said core polymer. In the present specification and claims, the term "metallic element" or "metal" shall mean the element being in the left side of the line linking B with Si, As, Te and At, in the long form of the Periodic Table, excluding the members on said line. The term "polymer" shall include polymerization type polymer such as acrylic resin, vinyl resin and the like. Since the linear polymer chain may include a certain degree of branching or crosslinking, depending on the intended application, the term "substantially linear" shall mean the polymer chain which is essentially a linear polymer admitting the presence of a degree of branching or crosslinking therein. The composite resin particles may be prepared by a method wherein addition polymerizable unsaturation bonds are introduced to the particulate crosslinked polymer, during or after formation thereof, and a metal-containing addition polymerizable ethylenic compound and other optional polymerizable ethylenic compounds are then reacted with the said particulate polymer, thereby forming the desired linear polymer chains chemically bonded to the same. However, in the present invention, the most important composite resin particles are, from the standpoint of application range and ease of preparation, composite acrylic resin particles each comprising a particulate crosslinked acrylic polymer, to which a number of substantially linear, metal-containing acrylic polymer chains are chemically bonded. Such particles may be advantageously prepared by the following method. That is, a monomer mixture of a polyfunctional monomer containing two or more polymerizable ethylenic groups each having different co-reactivity, and polymerizable monomers including a crosslinking monomer which are reactive with one ethylenic group of said polyfunctional monomer is subjected to an emulsion polymerization to obtain an emulsion of particulate materials of crosslinked polymer still having the other ethylenic group of said polyfunctional monomer in free state in the polymer, and after adding a polymerizable monomer reactive with the other ethylenic groups still remaining in the aforesaid particulate materials, a metal-containing monomer and other optional polymerizable monomers, a graft polymerization is effected to form substantially linear, metal-containing acrylic polymer chains. The term "polymerizable ethylenic groups each having different co-reactivity" shall mean the combination of ethylenic groups, one being of selective nature towards the type of employable comonomers as in 1,2-di-, 1,1,2-tri- or 1,1,2,2-tetra-substituted ethylene and the other having no such properties as in mono- or 1,1-di-substituted ethylene group, the combination of ethylenic groups, one being able to give homopolymer and the other being not, and the combination of ethylenic groups each having different reactivity. In this invention, any polyfunctional monomer having in its molecule two or more of the abovementioned ethylenic groups may be advantageously used in the preparation of the present composite resin particles. Examples of such monomers are allyl (meth) acrylate, addition product or allyl glycidyl ether and acrylic or methacrylic acid, addition product of monoallyl amine or diallyl amine and glycidyl (meth) acrylate or (meth) acryloyl bearing isocyanate, addition product of allyl alcohol and (meth) acryloyl bearing isocyanate, addition product of maleic acid or fumaric acid and glycidyl (meth) acrylate, addition product of maleic or fumaric monoester and glycidyl (meth) acrylate, and addition product of unsaturated fatty acid and glycidyl (meth) acrylate. Among the various ethylenic groups, the unsaturation bonds included in maleic or fumaric acid, or derivatives thereof, i.e. 1,1-di-, 1,1,2-tri-, or 1,1,2,2-tetra-substituted ethylenic groups, are selectively reactive with polymerizable aromatic compounds, whereas the unsaturation bonds included in acryloyl or methacryloyl groups, i.e. mono- or 1,1-di-substituted ethylenic groups are non-selective in the type of employable comonomers. Therefore, in a most preferable embodiment, the former is used for the preparation of linear polymer chains and the latter is for the preparation of crosslinked core polymer. Examples of such particularly useful monomers having in its molecule one or more radically polymerizable mono- or 1,1-di-substituted ethylenic unsaturation bonds and one or more radically polymerizable 1,2-di-, 1,1,2-tri- or 1,1,2,2-tetra-substituted ethylenic unsaturation bonds, are addition product of maleic acid and glycidyl acrylate, addition product of maleic acid and glycidyl methacrylate, addition product of fumaric acid and glycidyl acrylate, addition product of fumaric acid and glycidyl methacrylate, addition product of maleic acid monoester and glycidyl acrylate, maleic acid monoester and glycidyl methacrylate, addition product of fumaric acid monoester and glycidyl acrylate, addition product of fumaric acid monoester and glycidyl methacrylate, addition product of substituted maleic acid and glycidyl (meth) acrylate, addition product of substituted maleic acid monoester and glycidyl (meth) acrylate, addition product of substituted fumaric acid and glycidyl (meth) acrylate, and addition product of subsituted fumaric acid monoester and glycidyl (meth) acrylate. The abovesaid polyfunctional monomer is combined with other α,β-ethylenic monomers including a crosslinking monomer and the mixture is subjected to an emulsion polymerization to prepare the particulate crosslinked acrylic polymer. As a crosslinking monomer, any of the known compounds having in its molecule two or more radically polymerizable ethylenic unsaturation bonds may be satisfactorily used, as, for example, a polymerizable unsaturated monocarboxylic acid ester of polyhydric alcohol and a polymerizable unsaturated alcohol ester of polycarboxylic acid. Alternatively, use use can be made a combination of compounds each having a mutually reactive functional group and one or more α,β-ethylenically unsaturation bonds, as, for example, (meth) acrylic acid and glycidyl (meth) acrylate; hydroxy (meth) acrylate and isocyanate alkyl (meth) acrylate (blocked compound); and radically polymerizable silane coupling agents as vinyl trialkoxy silane and (meth) acryloxyalkyl trialkoxy silane and the like. Other α,β-ethylenic monomers may be any type of compounds customarily used in the preparation of acrylic resin. However, in order to leave the maleic type double bonds in free form in the resulted polymer, a polymerizable aromatic compound capable of showing a selective reactivity towards said double bonds should be excluded therefrom. Examples of such monomers are classified in the following groups. (1) carboxyl group containing monomer as, for example, acrylic acid, methacrylic acid, crotonic acid, itaconic acid, maleic acid, fumaric acid and the like, (2) hydroxyl group containing monomer as, for example, 2-hydroxyethyl acrylate, hydroxypropyl acrylate, 2-hydroxyethyl methacrylate, hydroxypropyl methacrylate, hydroxybutyl acrylate, hydroxybutyl methacrylate, allyl alcohol, methallyl alcohol and the like, (3) nitrogen containing alkyl acrylate or methacrylate as, for example, dimethylaminoethyl acrylate, dimethylaminoethyl methacrylate and the like, (4) polymerizable amide as, for example, acryl amide, methacryl amide and the like, (5) polymerizable nitrile as, for example, acrylonitrile, methacrylonitrile and the like, (6) alkyl acrylate or methacrylate as, for example, methyl acrylate, methyl methacrylate, ethyl acrylate, n-butyl acrylate, n-butyl methacrylate, 2-ethyl hexyl acrylate and the like, (7) polymerizable glycidyl compound as, for example, glycidyl acrylate, glycidyl methacrylate and the like, (8) α-olefin as, for example, ethylene, propylene and the like, (9) vinyl compound as, for example, vinyl acetate, vinyl propionate and the like, (10) diene compound as, for example, butadiene, isoprene and the like, reaction compounds of the abovesaid monomers as, for example, reaction compound of hydroxyl containing monomer (2) with isocyanate compound, reaction compound of carboxyl containing monomer (1) with glycidyl containing compound and the like. They may be used each singularly or in combination form. The emulsion polymerization may be carried out in a conventional way, using a polymerization initiator and an appropriate emulsifier. Particularly preferable emulsifiers are acrylic, polyester, alkyd or epoxy resin having in its molecule an amphoionic group of the formula: wherein R represents C₁ to C₆ alkylene or phenylene and Y ⊖ stands for -COO ⊖ or -SO₃ ⊖ , as disclosed in Japanese Patent Application Kokai No. 129066/83. In this first step of polymerization, only mono- or 1,1-di-substituted ethylenic bonds may participate in the reaction, giving crosslinked acrylic polymer particles still having unreacted 1,2-di-, 1,1,2-tri- or 1,1,2,2-tetra-substituted ethylenic unsaturation bonds on the surfaces thereof. Therefore, in the next stage of reaction, a polymerizable aromatic compound is added to the abovesaid emulsion and polymerization is continued to effect a graft polymerization between the remaining ethylenic unsaturation bonds and the polymerizable aromatic compound. Since 1,2-di-, 1,1,2-tri- or 1,1,2,2-tetra-substituted ethylenic bond has a selective reactivity towards polymerizable aromatic compound such as styrene, α-methyl styrene, vinyl toluene, t-butyl styrene and the like, a higher grafting rate can be attained with the aforesaid particulate crosslinked polymer coupled with the polymerizable aromatic compound. It is of course possible to use, besides the required polymerizable aromatic compound, other polymerizable monomers for the preparation of said linear polymer chains as desired. Any of the mono-functional polymerizable monomers hereinbefore stated. Furthermore, since a certain degree of branching or crosslinking is permissible according to circumstances, a limitted amount of crosslinking monomer may be used together, as desired. The invention is characterized in that the aforesaid linear polymer chains to be chemically bonded to the crosslinked polymer particles should contain a metallic element which is in the left side of the line linking B with Si, As, Te and At, in the long form of the Periodic Table, excluding the members on said line. As already stated, such metallic element can be advantageously introduced into the linear polymer chains in two different ways. In one method, a metal containing monomer is present in the abovesaid second stage of reaction together with polymerizable aromatic compound and other optional polymerizable monomers. Examples of metal containing monomers are metal esters or metal salts of polymerizable organic acids as acrylic acid, methacrylic acid, itaconic acid, maleic acid and the like, vinyl metals and styryl metals. The metal may also carry with hydroxyl group, an organic acid residue, an alkyl, a substituted alkyl or the like. More specifically, they may be zinc mono (meth) acrylate, zinc di (meth) acrylate, tributyl tin (meth) acrylate, dibutyl tin di (meth) acrylate, dihydroxy Al (meth) acrylate, hydroxy Al di (meth) acrylate, (meth) acryloyl ferrocene, furyl (meth) acryloyl ferrocene, (meth) acryloxy Zr octate, (meth) acryloxy Zr laurate, isopropyl (meth) acryloyl diisostearoyl titanate, isopropyl di (meth) acryloyl isostearoyl titanate, triethyl Ge (meth) acrylate, styryl triethyl germanium, vinyl triethyl germanium, diphenyl Pb di (meth) acrylate, styryl triethyl Pb, and the monomeric compounds represented by the formulae: (CH₂=CH) x M n R n-x ; (CH₂=CHC₆H₄) x M n R n-x ; and (CH₂=CR′COO) x M n R n-x wherein M stands for metallic element; R is alkyl, substituted alkyl, phenyl, substituted phenyl or hydroxyl; R′ is hydrogen or methyl; n is the valency of said metallic element; x stands for an integer of less than n. It will be appreciated that there are no particular limitation on the kind of radically polymerizable monomers used for the preparation of linear polymer chains. And, hence, the linear polymer chains can be freely designed, and various desired properties may be given to the present composite resin particles by varying the grafting monomers. For example, when the aforesaid monomers (1) or (3) are selected as a part of the monomers to be used for the preparation of linear polymer chains, the composite resin particles having carboxyl or amino containing polymer chains can be obtained, which particles have self-catalytic function in curing, high reactivity with an epoxy compound and are useful in an anionic or cationic electrodeposition. Selection of hydroxyl containing monomer (2) is of great use to give the composite resin particles which are to be compounded with a melamine resin and/or an isocyanate compound and cured to give a tough coating. The aforesaid monomers (4), addition products of hydroxyl containing monomers and monoisocyanate compounds, and addition products of isocyanate containing monomers and monoamide compounds are useful for giving the composite crosslinked resin particles with highly crystalline polymer chains, which are beneficial to the products in giving the structural viscosity and rheology controllable functions, thereto. Various functional groups, thus, may be carried on the linear polymer chains and utilized as reactive sites or made the best of the characteristic properties thereof. It is of course possible to select a particular combination of functional monomers and make the most of the characteristic properties of the respective functional group. The invention has been explained, for understanding easiness, on the composite resin particles prepared by only two stage reactions, and however, it would be appreciated that multi-stage reactions may likewise be used as desired, as for example, linear polymer particles are partly prepared, followed by the formation of crosslinked polymer core, and linear polymer chains are finally prepared. The present composite resin particles are excellent in dispersion stability in various solvents and resinous varnishes and have the characteristical self-film forming properties. Various functional polymers can be chemically bonded on the surface of particulate crosslinked polymer, and the designed metal element can be introduced into the linear polymer chains, thereby exhibiting the desired properties as cure catalytic function, bioactive function and the like. Therefore, the present composite resin particles are quite useful in various technical fields, including paint industries, resin molding and other industries. The invention shall be now more fully explained in the following Examples. Unless otherwise being stated, all parts and percentages are by weight. Reference Example 1 Preparation of dispersion stabilizer Into a 2 liters flask fitted with a stirrer, an air inlet tube, a thermoregulator, a condenser and a decanter, were placed 134 parts of bishydroxy ethyl taurine, 130 parts of neopentylglycol, 236 parts of azelaic acid, 186 parts of phthalic anhydride and 27 parts of xylene and the mixture was heated while removing the formed water azeotropically with xylene. The temperature was raised to 190°C in about 2 hours from the commencement of reflux and the reaction was continued under stirring and dehydration until the acid value (based on carboxylic acid group) reached 145. Thereafter, the reaction mixture was allowed to cool to 140°C and to this, 314 parts of Cardura E-10 ( ™ ) (glycidyl versatate, trademark of Shell) were dropwise added in 30 minutes at 140°C. The mixture was stirred at the same temperature for 2 hours and then the reaction was stopped to obtain a polyester resin having an acid value of 59, a hydroxyl value of 90 and a number average molecular weight of 1054. Reference Example 2 Preparation of dispersion stabilizer Into a similar reaction vessel as used in Reference Example 1, were placed 73.5 parts of taurine Na salt, 100 parts of ethyleneglycol, and 200 parts of ethyleneglycol monomethyl ether, and the mixture was heated, under stirring, to 120°C. At the stage when a uniform solution was obtained, a mixture of 470 parts of Epicohto 1001 ( ™ ) (bisphenol A diglycidyl ether type epoxy resin, epoxy equivalent 470, trademark of Shell Chem.) and 400 parts of ethyleneglycol monomethyl ether was dropwise added in 2 hours. After completion of said addition, the combined mixture was heated and stirred for 20 hours. Thus obtained product was then purified and dried to obtain 518 parts of modified epoxy resin, whose acid value (measured by KOH titration method) was 49.4 and sulfur content (measured by fluorescent X ray analysis) was 2.8%. Reference Example 3 Preparation of dispersion stabilizer Into a 1 liter flask fitted with a stirrer, a thermoregulator, dropping funnels, a nitrogen gas inlet tube and a condenser, were placed 140 parts of ethyleneglycol monomethyl ether and 140 parts of xylene, and the mixture was heated to 120°C. To this, a monomer mixture of 74 parts of methyl methacrylate, 70 parts of 2-ethyl hexyl acrylate, 24 parts of 2-hydroxyethyl methacrylate, and 12 parts of methacrylic acid, added with 5 parts of azobisisobutyronitrile and a solution of 20 parts of N-(3-sulfopropyl)-N-methacryloyloxyethyl-N,N-dimethyl ammonium betaine in 150 parts of ethyleneglycol monoethyl ether were simultaneously and dropwise added in 3 hours. After elapsing 30 minutes from the completion of said addition, a solution of 0.4 part of t-butylperoxy-2-ethylhexanoate in 8 parts of ethyleneglycol monomethyl ether was added and the combined mixture was kept at 120°C for 1 hour and thereafter, the solvent was removed off to obtain an amphoionic group containing acrylic resin having a non-volatile content of 92%. Reference Example 4 Preparation of monomer containing two polymerizable ethylenic groups each having different co-reactivity Into a 1 liter flask fitted with a stirrer, an air inlet tube, a thermoregulator, and a condenser, were placed 430 parts of n-butyl maleate and 1.6 parts of hydroquinone and the mixture was heated to 150°C. To this, were dropwise added 373 parts of glycidyl methacrylate in 20 minutes and the combined mixture was maintained at 150°C for 60 minutes. The reaction was stopped at the stage when the resinous acid value reached 3 KOH mg/g. Example 1 Into a 1 litter flask fitted with a stirrer, a thermoregulator, a dropping funnel, a nitrogen gas inlet tube and a condenser, were placed 330 parts of deionized water and the temperature was raised to 80°C. Separately, a pre-emulsion was prepared by providing an aqueous solution of dispersion stabilizer comprising 12 parts of the amphoionic group containing polyester resin obtained in Reference Example 1, 1.2 parts of dimethyl ethanol amine and 104 parts of deionized water, and gradually adding, while stirring in a Disper, a mixture of 66 parts of methyl methacrylate, 60 parts of n-butyl acrylate, 14 parts of allyl methacrylate and 40 parts of ethyleneglycol dimethacrylate thereto. An aqueous initiator solution was also prepared in a separate vessel, by mixing 2 parts of azobiscyanovaleric acid, 1.3 parts of dimethyl ethanol amine and 40 parts of deionized water. To the aforesaid reaction flask, the initiator solution and the pre-emulsion were dropwise added, in 80 minutes and 60 minutes, respectively. However, the addition of said pre-emulsion was started after elapsing 10 minutes from the commencement of addition of said initiator solution. Then, the combined mixture was kept standing at 80°C for 30 minutes, dropwise added with a mixture of 12 parts of styrene, 2 parts of methyl methacrylate, 4 parts of n-butyl methacrylate and 2 parts of zinc monomethacrylate and an aqueous solution of 0.8 part of azobiscyanovaleric acid and 0.6 part of dimethyl ethanol amine in 20 parts of deionized water in 20 minutes. The combined mixture was then kept at the same temperature for 1 hour and the reaction was stopped at this stage. Thus obtained emulsion was then subjected to freeze-drying to obtain zinc containing composite resin particles. The zinc containing composite resin particles could be easily dispersed in xylene and in butyl acetate. Viscosities of said dispersions and mean grain diameter of the particles in the respective dispersion were examined and the dates obtained were shown in the following Table. Incidentally, the mean grain diameter of the particles in an aqueous emulsion was 150 nm. The abovementioned organic solvent dispersions were applied on glass plates by using a doctor blade (20 mils) and dried to obtain clear coatings. Zinc concentration of the xylene dispersion (non-volatile content 30%) was measured by a fluorecent X-ray analyzer and was found to be 4000 ppm to the total solid matters. Example 2 Into a similar reaction vessel as used in Example 1, were placed 330 parts of deionized water and heated to 80°C. Next, a pre-emulsion was prepared by providing an aqueous solution of dispersion stabilizer comprising 40 parts of amphoionic group containing acrylic resin obtained in Reference Example 3, 4 parts of dimethyl ethanol amine and 160 parts of deionized water, and gradually adding, while stirring in a Disper, a monomer mixture of 30 parts of methyl methacrylate, 40 parts of n-butyl acrylate, 14 parts of the monomer of Reference Example 4 and 56 parts of ethyleneglycol dimethacrylate. An aqueous initiator solution was also prepared by mixing 2 parts of azobiscyanovaleric acid, 1.3 parts of dimethyl ethanol amine and 40 parts of deionized water. To the aforesaid reaction vessel, the initiator solution and the pre-emulsion were dropwise added in 65 and 45 minutes, respectively. At that time, the addition of pre-emulsion was started after elapsing 10 minutes from the commencement of said addition of the initiator solution. After completion of said addition, the combined mixture was kept at 80°C for 20 minutes, added dropwise with an aqueous initiator solution comprising 0.8 part of azobiscyanovaleric acid, 0.6 part of dimethyl ethanol amine and 20 parts of deionized water in 40 minutes and with a monomer mixture of 18 parts of styrene, 8 parts of methyl methacrylate, 23 parts of n-butyl methacrylate, 10 parts of 2-hydroxyethyl methacrylate and 1 part of methacryloxy zirconium octate in 20 minutes. At that time, the addition of said monomer mixture was started after elapsing 10 minutes from the commencement of addition of the initiator solution. Thereafter, the combined mixture was reacted at the same temperature for 90 minutes. Thus obtained emulsion was then subjected to freeze-drying to obtain zirconium containing composite resin particles. The resin particles could be easily dispersed in both xylene and butyl acetate. The viscosities of these dispersions and mean grain diameters of the composite resin particles in the dispersions were examined as in Example 1 and shown in the following Table 2. The mean grain diameter of the composite resin particles in the aqueous emulsion was 120 nm. The abovementioned organic solvent dispersions were applied on glass plates by using a doctor blade (20 mils) and dried to obtain clear coatings. Zr content of the xylene dispersion was measured by a fluorecent X-ray analyzer and was found to be 1100 ppm to the total solid matters. Example 3 Using the same reactor and procedures as stated in Example 2, tin containing composite resin particles were prepared, excepting substituting 23 parts of the amphoionic group containing polyester of Reference Example 1 for 40 parts of the amphoionic group containing acrylic resin of Reference Example 3, and 1 part of tributyl tin methacrylate for 1 part of methacryloxy zirconium octate, as metal containing monomer. Thus obtained composite resin particles showed excellent dispersibility towards xylene and butyl acetate. Viscosities of these dispersions and mean grain diameters of the composite resin particles in said dispersions were shown in the following Table 3. Incidentally, the mean grain diameter of aqueous emulsion of the composite resin particles was 90 nm. The tin content of the xylene dispersion was 1400 ppm to the total solid matters.

Claims: A process for preparing composite resin particles each comprising a particulate crosslinked polymer to which substantially linear, metal-containing polymer chains are chemically bonded, which comprises first effecting an emulsion polymerization of a monomer mixture of (A) a polyfunctional monomer having one or more mono-substituted or 1,1-di-substituted ethylenic groups and one or more 1,2-di-substituted, 1,1,2-tri-substituted or 1,1,2,2-tetra-substituted ethylenic groups, (B) a crosslinking monomer having two or more mono-substituted or 1,1-di-substituted ethylenic groups or a combination of two monomers each having one or more mono-substituted or 1,1-di-substituted ethylenic groups and a mutually reactive functional group, and (C) polymerizable monomers other than said (A) and (B) and excluding polymerizable aromatic compounds, in the presence of an acrylic, polyester, alkyd or epoxy resin having in its molecule an amphoionic group of the formula: wherein R represents C₁ to C₆ alkylene or phenylene and Y⁻ represents COO⁻ or SO - / 3, as an emulsifier, to obtain an emulsion of crosslinked polymer particles still having 1,2-di-substituted, 1,1,2-tri-substituted or 1,1,2,2-tetra-substituted ethylenic groups in free state in the polymer, and subsequently effecting a graft-polymerization of said crosslinked polymer particles with a monomer mixture of (D) a polymerizable aromatic compound to which 1,2-di-substituted, 1,1,2-tri-substituted or 1,1,2,2-tetra-substituted ethylenic groups have selective reactivity, (E) a metal-containing monomer, the metal excluding alkali metals and alkaline earth metals, and (F) other polymerizable mono-functional monomers, thereby forming substantially linear metal-containing polymer chains chemically bonded to said crosslinked polymer particles. A process as claimed in claim 1, characterized in that the polyfunctional monomer having one or more mono-substituted or 1,1-di-substituted ethylenic groups and one or more 1,2-disubstituted, 1,1,2-tri-substituted or 1,1,2,2-tetra-substituted ethylenic groups is selected from addition products of maleic acid and glycidyl acrylate, addition products of maleic acid and glycidyl methacrylate, addition products of fumaric acid and glycidyl acrylate, addition products of fumaric acid and glycidyl methacrylate, addition products of maleic acid monoester and glycidyl acrylate, addition products of maleic acid monoester and glycidyl methacrylate, addition products of fumaric acid monoester and glycidyl acrylate, addition products of fumaric acid monoester and glycidyl methacrylate, addition products of substituted maleic acid and glycidyl acrylate, addition products of substituted maleic acid and glycidyl methacrylate, addition products of substituted maleic acid monoester and glycidyl acrylate, addition products of substituted maleic acid monoester and glycidyl methacrylate, addition products of substituted fumaric acid and glycidyl acrylate, addition products of substituted fumaric acid and glycidyl methacrylate, addition products of substituted fumaric acid monoester and glycidyl acrylate and addition products of substituted fumaric acid monoester and glycidyl methacrylate.

Inventors: ISHIKURA, SHINICHI, KASHIHARA, AKIO, MIYAZONO, TADAFUMI
Applicants: NIPPON PAINT CO., LTD.
Application year: 1987
Main classification: C08F291
IPC codes: C09D201, C08F2, C08F291, C08F8, C08F265, C08J3