Method and apparatus for continuous compression forging of continuously cast steel

Abstract: A segregation preventive or eliminative operation is performed in under the following conditions: solidified/unsolidified ratio of the solidifying block (1) is in a range of 0.5:1 to 0.9:1; ratio between the overall compression δ (mm) versus thickness of unsolidified area in the block (d mm) is greater than or equal to 0.5 or the thickness (d mm) of the unsolidified layer in the solidifying block is: 1.2 × D - 80 < d < 10.0 × D - 80 where D is the thickness of the block before compression. Casting speed may be controlled according to thickness of the solidifying shell (1a) at a crater end or near the crater end. Preferably, electromagnetic stirring (3) is performed before performing compression forging (4,5).

Description: BACKGROUND OF THE INVENTION Field of the Invention The present invention relates generally to a continuous casting technic. More specifically, the invention relates to a method and apparatus for continuously performing compressive forging for cast steel derived from a continuous casting process in order to prevent segregations in a cast block drawn from a mold according to the preambles of claims 1 and 20. Description of the Background Art In the conventional art, it has been regarded in inevitable to form central segregation in a continuously cast steel. This segregation is caused by condensation of carbon (C), sufur (S) and phosphorus (P) in the molten metal near the central axis of the cast steel during the cooling and solidifying process. Such segregation degrades the cast blocks. Particularly, in case of thick steel plate, such segregation in the cast steel may degrade the mechanical propertys by causing stratification or layering lamination. Segregation in casted steel is caused at the final stage of solidification due to the solidification shrinkage or bulging of the solidifying shell which draw the condensed molten metal to the solidifying end and result the central segregation. In order to eliminate central segregation in the casted steel, various techniques have been attempted. For example, one technique attempted to electromagnetically stir the metal in the secondary cooling zone. However, such attempts failed to completely eliminate segregation at the semi-micron level and therefor are not yet satisfactory. On the other hand, in-line reduction methods, in which the solidifying end is compressed during the solidification period by means such as a pair of rollers or opposed reciprocating forging tools have been proposed in "Iron and Steel" Vol. 7, 1974, pages 875 to 884, and US-A- 4519439, upon which the preambles of claims 1 and 20 are based. In these in-line reduction methods, it is also required to compress the solidifying block during the stage where the solidifying block contains a relatively large proportion of unsolidified steel. If the force of this compression is not sufficiently great, cracks can form at the interface between the solidified steel and the still molten portion. On the other hand, when compression at the aforementioned solidifying stage is excessive, inversely segregated areas in which certain components of the desired alloy are missing can be created at the center of the cast steel during the compression process. In order to avoid the aforementioned defects, the Japanese Patent First (unexamined) Publication 49-12738 discloses a method for compensating for reduction of volume of the solidifying cast steel by reducing gaps between pairs of rolls. On the other hand, the Japanese Patent First Publication 53-40633 discloses a method for performing heavy compression by means of a casting die at the end stage of solidification. The improvement for the method of publication 53-40633 has been proposed in the Japanese Patent First Publication 60-148651, in which electromagnetic stirring is performed, or ultra-sonic waves are applied to the solidifying steel during the solidification. This process along with substantial compression by means of the casting die during the solidification stage helps to reduce segregation. However, in the former case as disclosed in publication 49-12738, bulging and other defects cannot be completely avoided even when pairs of rolls are provided to reduce the gaps between them as several mm/m. In addition, in this case, when the position of the rollers is not appropriate, the light compression process may actually degrade the cast steel by creating worse segregation around the center. On the other hand, in the later case, heavy compression by means of the casting die may cause internal cracks of the solidifying steel and generate inversely segregated areas. However, the improvement in the semi-macro segregation can be achieved, this method requires quite delicate adjustment of the compression conditions. Namely, when the heavy die compression is performed at a stage, in which a relatively large proportion of unsolidified steel exists, it is possible to create cracks at the interface between the solidified section and the unsolidified section. Still worse, if the heavy die compression is performed while a relatively large proportion of unsolidified metal is left, inversely segregated area can be formed. On the other hand, if such compression is performed at a stage when a excessively small proportion of unsolidified metal is left, compression is not so effective in avoiding segregation. By performing electromagnetic stirring or by applying ultra-sonic waves, centerline segregation, can be reduced by increasing uni-directional crystalline. However, it is still not satisfactory avoiding creation of the centerline segregation and so forth for a wide range variety of thicknesses, casting speeds, temperatures and so forth encountered when forming a steel block. SUMMARY OF THE INVENTION Therefore, it is a principle object of the present invention to provide a method and apparatus which can successfully and satisfactorily prevent segregations in the continuously cast steel. In order to accomplish the aforementioned and other objects, segregation prevention or elimination operation, performed in accordance with the invention. is carried out under the following conditions: the solid phase proportion at the center of the solidifying block is in a range of 50 percent to 90 percent: The ratio between the thickness δ (mm) of the unsolidified section at the center of the steel block and the amount d (mm) of reduction in thickness of the steel block during compression forging should be greater than s/d 0.5:1. In another embodiment, the thickness d (mm) of the unsolidified layer in the solidifying block is: 1.2 x √ D - 80 ≦ d ≦ 10.0 x √ D - 80 where D is thickness of the steel block before compression. Preferably, casting speed is to be controlled according to the thickness of the solidified shell at a crater end or near the crater end. Further preferably, electromagnetic stirring is performed before performing compression. The solid phase proportion (f s ) is the ratio of solidified/total material at a given section of the steel block. In the disclosure, the word "interface" refers to that area between the solidified material of the block and the still unsolidified material thereof. According to one aspect of the invention, a method for compression forging on a cast steel block drawn from a casting mold in a continuous casting process comprises the steps disclosed in claim 1. Preferably, the thickness (d) is: 1.2 x √ D-80 ≦ d ≦ 10.0 x √ D-80 where D is overall thickness (mm) of the cast steel block before compression, and the ratio of thickness reduction (δ mm) versus thickness of unsolidified layer (d mm) is held greater than or equal to 1.0. Preferably, the method further comprises a step of exerting stirring force on the cast block in the advance of performing compression forging. On the other hand the method may further comprises the steps of: monitoring thickness of the unsolidified layer in the cast steel block at the crater end or near the crater end; and adjusting casting speed of the continuous caster so that the solid phase proportion at the forging compression stage is kept in the range of 50 to 90 percent. An electromagnetic stirring force is exerted on the cast steel block in the stirring step. The electromagnetic stirring, at a frequency between 0.1 to 20 Hz, magnetic flux density is in the range of 200 to 1600 gauss, while the solid phase proportion is in the range of 0 to 80 percent and/or where the thickness (d) of the unsolidified layer is in the range of: 2.0 x √ D-80 ≦ d ≦ 14.0 x √ D-80. According to a further aspect of the invention, an apparatus for compression forging a cast steel block drawn from a mold in a continuous casting process is disclosed in claim 20. Preferably the thickness of the unsolidified layer (d) is in a range of: 1.2 x √ D-80 ≦ d ≦ 10.0 x √ D-80 where D is overall thickness (mm) of the block before compression, and the ratio of thickness reduction of the block (δ mm) versus thickness of unsolidified layer of the block (d mm) is greater than or equal to 1.0. In the preferred construction, the apparatus, set forth above may further comprise means provided upstream of the compression forging means for exerting stirring force on the cast steel block in advance of performing forging compression. The stirring means performs electromagnetic stirring on the cast steel block in the stirring step. The condition to perform the electromagnetic stirring is that: the frequency is 0.1 to 20 Hz; the magnetic flux density is in the 200 to 1600 gauss range; the solid phase proportion is in the 0 to 80 percent range; and/or the thickness (d) of unsolidified layer is: 2.0 x √ D-80 ≦ d ≦ 14.0 x √ D-80. BRIEF DESCRIPTION OF THE DRAWINGS The present invention will be understood more fully from the detailed description given herebelow and from the accompanying drawings of the preferred embodiment of the invention, which, however, should not be taken to limit the invention to the specific embodiment but are for explanation and understanding only. In the drawings: Fig. 1 is a schematic illustration showing the preferred embodiment of a continuous forging apparatus according to the invention; Fig. 2 is a graph showing relationship between the ratio of compressingly reduced thickness and the thickness of the unsolidified layer and solid phase proportion; Fig. 3 is a graph showing relationship between segregation ratio and the solid phase proportion; Fig. 4 is a graph showing relationship between unsolidified layer in the cast steel block and the thickness of the casted block before compression; Fig. 5 is a graph showing relationship between unsolidified layer in the cast steel block and the thickness of casted block before forging compression; Fig. 6 is a graph showing the variation of segregation ratio in relation to solid phase proportion; Fig. 7 is a graph showing the variation of number of segregated particles and particle sizes thereof, showing the result of an example 1; and Fig. 8 is a graph showing the variation of number of segregated particles and particle sizes thereof, showing the result of an example 2. DESCRIPTION OF THE PREFERRED EMBODIMENT Referring now to the drawings particularly to Fig. 1, the preferred embodiment of a segregation preventive compression forging apparatus according to the present invention, is arranged in series to a continuous caster which includes a mold 7. The apparatus comprises a pairs of guide rollers 2 defining a path for cast steel block 1, such as cast strip, cast slab and so forth. The cast steel block path extends from the end of the casting mold 7 to a forging compression stage, where a pair of forging compression dies 4 are provided. An electromagnetical stirring device 3 is arranged adjacent the cast steel block path at an intermediate position between the end of the casting mold 7 and the compression forging means. Pairs of pinch rollers 6 are provided at downstream of the compression forging stage for drawing the block. The compression forging dies 4 are respectively associated with power cylinders 5 which drive the compression forging dies toward and away from the cast steel block to be compressed. The power cylinders 5 may be adjusted according to the type of cast steel block, temperature of the block and so forth. As will be seen from Fig. 1, the preferred construction of the segregation preventive compression forging apparatus, according to the invention, arranges the forging compression dies 4 at a orientation where the solid phase proportion (f s ) is in a range of 50 to 90 percent, and the ratio of compressive reduction (δ mm) versus the thickness of the unsolidified layer (d mm) is greater than or equal to 0.5. The segregation preventive compression forging apparatus, arranges the forging compression dies 4 at a position where the thickness (d mm) of the unsolidified layer is: 1.2 x √ D-80 ≦ d ≦ 10.0 x √ D-80 where D is overall thickness (mm) of the cast steel block before compression, and the ratio of compressive reduction (δ mm) versus thickness of unsolidified layer (d mm) is greater than or equal to 0.5:1. In order to obtain the aforementioned optimal position of the compression forging stage, experiments were performed at various solid phase proportions (f s ), thickness of the unsolidified layer (d) and thickness reduction amounts (δ). The results of the experiments are shown in Figs. 2 and 3. In Fig. 2, there is shown the variation (δ/d) of block thickness reduction versus thickness of the unsolidified layer, in relation to the solid phase proportion at the central portion of the cast steel block 1. From Fig. 2, it will be appreciated: that, when the thickness (d) of the unsolidified layer is excessively great and thus the ratio (δ/d) is smaller than 0.5, cracking occurs at the interface between the solidified and unsolidified metals; and that the thickness (d) of the unsolidified layer is small and thus the ratio (δ/d) is substantially great, therefore prevention of segregation becomes difficult. In the former case, it is believed that cracking at the interface between the solid phase and liquid phase occurs due to excessive compression of the cast steel block. On the other hand, in the later case, when the solid phase proportion (f s ) becomes greater than or equal to 70 percent, reduction of segregation occurring around the center of the cast steel block becomes difficult. When the solid phase proportion (f s ) is greater than or equal to 90 percent or in other words the cast steel block is nearly solid, extremely high pressure is required to reduce segregation therein. Fig. 3 shows variation of carbon segregation ratio (C/C₀) in the cast steel block relative to the solid phase proportion (f s ). Here, C represents carbon content in a sample obtained from cast steel block, and C₀ is an average carbon content in the cast steel block. As will be seen from Fig. 3, the ratio C/C₀ become substantially 1.0 at the solid phase proportion (f s ) about 70 percent. Therefore, in view of the carbon segregation ratio (C/C₀), the preferred solid phase proportion becomes about 70 percent. In view of the required quality and properties of the cast products, the carbon segregation ratio (C/C₀) and the reduction ratio (δ/d), the optimum range of the solid phase proportion is 50 to 90 percent. On the other hand, as will be appreciated, in practice it is difficult to control the solid phase proportion (f s ) during continuous casting operation. In order to enable practical control, observation is made of the thickness of the cast steel block obtained, the thickness of the unsolidified layer at the center of the cast steel block and the types of the cast steels to be produced. Fig. 4 shows the variation in the thickness (d mm.) of the unsolidified layer relative to the cast steel block thickness (D mm.) before compression, when thickness reduction is performed at a condition where the ratio δ/d is greater than or equal to 0.5. The graph of Fig. 4 represents carbon segregation distribution relative to the thickness of the unsolidified layer (d) and thickness of the cast steel block (D). As will be seen in Fig. 4, where the unsolidified layer thickness d fall within a range expressed by. 1.2 x √ D-80 ≦ d ≦ 10.0 x √ D-80 the solid phase proportion (f s ) remains within the range of 50 to 90 percent. Therefore, by setting the unsolidified layer thickness (d) relative to the cast steel block thickness (D) in the range set forth above, compression forging can be performed while the solid phase proportion (f s ) is within the range of 50 to 90 percent. In order to effectively perform compression forging for reducing segregation in the cast steel block, it is essential to arrange the forging means at an optimal position. Therefor, it is quite important to control the location of the solification point during continuous casting. Therefore, it is desirable to monitor the thickness of the solified shell 1a of the cast steel block 1 at the crater end or near the crater end and control casting speed so that the solid phase proportion (f s ) and the unsolidified layer thickness d can be maintained within the ranges set forth above. On the other hand, as set forth in the introduction of the disclosure, applying electromagnetic stirring force before compression forging is performed is effective for reducing segregation in the cast steel block. Therefore, as seen in Fig. 1, the preferred embodiment of the segregation preventing compression forging appratus according to the present invention employs the electromagnetic stirring device 3 upstream of the compression forging means where the compression forging dies 4 are provided. In the practical embodiment, electromagnetic stirring is performed at a frequency in the 0.1 to 20 Hz range, and a magnetic flux density B at the surface of the caseted block in the 200 to 1600 gauss range. For this purpose, circumferential horizontal or vertical electromagnetic stirring is performed by means of the device 3. In order to determine the optimum position of the electromagnetically stirring device 3, experiments are performed at positions: in the mold 7 of the continuos caster; at a position where the solid phase proportion (f s ) at the center of the casted block 1 is about 0 to 80 percent and at a position where the thickness of the unsolidified layer thickness is: 2.0 x √ D-80 ≦ d ≦ 14.0 x √ D-80. As a result of the aforementioned experiments the optimal position of the electromagnetic stirring means as shown in Fig. 5 is: 2.0 x √ D-80 ≦ d ≦ 14.0 x √ D-80. Highly uniform fine cristalline structure can be obtained in the cast steel block can be obtained when the above equation is satisfied. It should be noted when the frequency for electromagnetic stirring is less than 0.1 Hz, stirring cannot be performed effectively. On the other hand, frequency over 20 Hz will not penetrate deeply enough into the cast steel block and can not provide the necessary stirring force. When the magnetic flux density is less than 200 Gauss, adequate stirring force can not be obtained, and when the magnetic flux density is in excess of 1600 Gauss, stirring force becomes too great causing flowing of the molten metal in the cast steel block and generating inversely segregated areas. It should be appreciated that, though the shown embodiment provides a single electromagnetic stirring stage, it would be more effective to provide several electromagnetic stirring stages. On the other hand, as seen in Fig. 2, when the high ratio of thickness reduction is performed in the compression forging stage, segregation can be reduced even when the thickness of the unsolidified layer is relatively great. Specifically, as shown in Fig. 6, when the acceptable quality is 0.9 ± 0.1 with regard to the carbon segregation ratio (C/C₀), the desired quality of cast steel block can be obtained by performing compression forging at an δ/d ratio greater than or equal to 1.0 irregardless of the solid phase proportion. Therefore, it should be appreciated that by performing relatively high reduction ratio compression forging, substantial improvement can be obtained irregardless of the position of the compression stage. EXAMPLE 1 Continuous casting of cast block 1 of 270 mm thickness and 2,200 mm width was performed by means of a per se well known type of continuous caster. The cast steel block 1 was processed by means of the preferred embodiment of the segregation preventive compression forging apparatus of Fig. 1. After compression forging, the block (SM 50) was 220 mm. in thickness and 2,240 mm. in width. The composition of the steel block is shown in the appended table 1. Compression forging was performed under the following conditions: solid phase proportion f s = 70 percent reduction ratio δ/d = 0.9. Casting speed was controlled at 0.7 m/min. so that the solid phase proportion (f s ) could be maintained at 70 percent which corresponded to a thickness of about 50 mm of the unsolidified layer. In addition, electromagnetic stirring was performed under the following conditions: solid phase proportion f s = 70 percent and 74 percent unsolidified layer thickness d = 80 mm and 60 mm. 1.2 x √ D-80 ≦ d ≦ 10.0 x √ D-80 Electromagnetic stirring parameters are set out in the appended table 2. Carbon segregation ratio C/C₀ is checked with respect to the resultant cast block. The carbon segregation ratio C/C₀ obtained was 0.98. This demonstrates high potential of the preferred embodiment of the segregation preventive compression forging apparatus of the present invention. The cast steel block obtained from the aforementioned compression process was further checked with respect to particle size and particle number of semi-macro segregation. In order to check the above, the resultant cast steel block is separated into 200 µm mesh blocks. Average phosphrous (P) concentration in respective mesh blocks was measured. In order to compare the results of measurements of the forging compression forged cast steel block, the same measurement was performed for cast block, on which no compression forging process was performed. The result of measurements are shown in Fig. 7. It should be noted that Fig. 7 shows the semi-macro segreation particle size and particle number of the blocks which had a segregation ratio greater than or equal to 3. As will be seen in Fig. 7, segregation can be reduced by performing compression forging. Reduction of the segregation in relatively large particles particularly marked. EXAMPLE 2 Under the same conditions as listed above but without electromagnetic stirring, casting and forging compression was performed. The compression forging means was arranged at a position where the unsolidified layer thickness d was: 1.2 x √ D-80 ≦ d ≦ 10.0 x √ D-80 With respect to the cast steel block, the semi-macro phosphorous segregation was measured in a manner identical to that performed with respect to the former embodiment. As a result, it was found that, though the range of variation in the data is wider than that obtained in the former embodiment, marked reduction of segregation in the cast steel block could still be obtained. Therefore, the invention fulfills all of the objects and advantages sought thereby. While the present invention has been disclosed in terms of the preferred embodiment in order to facilitate better understanding of the invention, it should be appreciated that the invention can be embodied in various ways without departing from the principle of the invention. Therefore, the invention should be understood to include all possible embodiments and modifications to the shown embodiments which can be embodied without departing from the principle of the invention set out in the appended claims. Thickness of Unsolidified Layer (mm) 80 60 Frequency (Hz) 2 2 Stirring Direction Horizontal Horizontal Magnetic Flux Density 700 700

Claims: A method for preventing segregations in a continuous casting by compression forging a cast block (1) drawn from a mold (7), wherein the compression forging (4,5) is performed at a position where the solid phase proportion at the center of the block (1) is in a predetermined range from 50 percent to 90 percent, characterized in that said compression forging is performed at a thickness reduction as expressed by the following formula : δ/d ≧ 0.5 where δ is overall reduction (mm) in thickness of the cast block during compression forging ; d is thickness (mm) of the unsolidified layer in the cast block at the position where compression forging is performed. A method as set forth in claim 1, which further comprises a step of exerting stirring force (3) on said cast block (1) in advance of performing compression forging. A method as set forth in claim 1, which further comprises steps of : monitoring the thickness of said unsolidified layer in said cast block (1) at a crater end or near the crater end ; and adjusting casting speed of said continuous caster so that the solid phase proportion at said compression forging stage is maintained in said range of 50 percent to 90 percent. A method as set forth in claim 3, which further comprises a step of exerting stirring force on said cast block (1), in advance of performing compression forging. A method as set forth in claim 2, characterized in that electromagnetic stirring force is exerted on said cast block (1), in said stirring step. A method as set forth in claim 5, characterized in that said electromagnetic stirring is performed at a frequency between 0.1 to 20 Hz. A method as set forth in claim 5, characterized in that said electromagnetic stirring is performed with a magnetic flux density is in the range of 200 to 1600 gauss. A method as set forth in claim 5, characterized in that said electromagnetic stirring is performed while said solid phase proportion is in a range of 0 to 80 percent. A method as set forth in claim 5, characterized in that said electromagnetic stirring is performed while the thickness (d) of unsolidified layer is expressed as : 2.0 x √ D - 80 ≦ d ≦ 14.0 x √ D - 80 A method as set forth in claim 1, characterized in that the compression forging is performed at a position where the thickness (d) of unsolidified layer is expressed as : 1.2 x √ D - 80 ≦ d ≦ 10.0 x √ D - 80 where D is overall thickness (mm) of the cast block (1), before compression, and the ratio of thickness reduction δ (mm) versus thickness of unsolidified layer d (mm) is greater than or equal to 1.0. A method as set forth in claim 10, which further comprises a step of exerting stirring force on said cast block (1), in advance of performing compression forging. A method as set forth in claim 10, which further comprises steps of : monitoring the thickness of said unsolidified layer in said cast block (1) at a crater end or near the crater end ; and adjusting casting speed of said continuous caster so that the solid phase proportion at said compression forging stage is maintained in said range. A method as set forth in claim 12, which further comprises a step of exerting stirring force on said cast block in advance of performing compression forging. A method as set forth in claim 11, characterized in that electromagnetic stirring force is exerted on said cast block in said stirring step. A method as set forth in claim 14, characterized in that said electromagnetic stirring is performed at a frequency between 0.1 to 20 Hz. A method as set forth in claim 15, characterized in that magnetic flux density of said electromagnetic stirring is in a range between 200 to 1600 gauss. A method as set forth in claim 14, characterized in that said electromagnetic stirring is performed while said solid phase proportion is in a range of 0 to 80 percent. A method as set forth in claim 15, characterized in that said electromagnetic stirring is performed while the thickness (d) of the unsolidified layer is expressed as : 2.0 x √ D - 80 ≦ d ≦ 14.0 x √ D - 80 . A method as set forth in claim 10, characterized in that the ratio of compressive reduction δ (mm) versus thickness of unsolidifed layer d (mm) is greater than or equal to 0.5. An apparatus for preventing segregations in a continuous casting, comprising : means (2) for receiving a cast block (1) from a casting mold (7) and compression forging means (4,5) for performing a compression forging at a position where the solid phase proportion at the center of the block (1) is in a predetermined range from 50 percent to 90 percent, characterized in that said compression forging means are arranged to perform a thickness reduction as expressed by the following formula : δ/d ≧ 0.5 where δ is overall reduction (mm) in thickness of the cast block during compression forging ; d is thickness (mm) of unsolidified layer in the cast block at the position where compression forging is performed. An apparatus as set forth in claim 20, which further comprises means (3) provided upstream of said compression forging means for exerting stirring force on said cast block in advance of performing compression forging. An apparatus as set forth in claim 21, characterized in that said stirring means (3) exerts electromagnetic stirring force on said cast block in said stirring step. An apparatus as set forth in claim 22, characterized in that said stirring means performs said electromagnetic stirring at a frequency between 0.1 to 20 Hz. An apparatus as set forth in claim 22, characterized in that said electromagnetic stirring is performed with a magnetic flux density in a range between 200 to 1600 gauss. An apparatus as set forth in claim 22, characterized in that said stirring means (3) performs said electromagnetic stirring while said solid phase proportion is in a range of 0 to 80 percent. An apparatus as set forth in claim 22, characterized in that said stirring means (3) perofrms said electromagnetic stirring while the thickness (d) of unsolidified layer is : 2.0 x √ D - 80 ≦ d ≦ 14.0 x √ D - 80 . An apparatus as set forth in claim 20, characterized in that said compression forging is performed at a position where the thickness (d) of an unsolidified layer is expressed as : 1.2 x √ D - 80 ≦ d ≦ 10.0 x √ D - 80 where D is overall thickness (mm) of the cast block before compression, and the ratio of thickness reduction ( δ mm) versus thickness of unsolidified layer (d mm) is greater than or equal to 1.0. An apparatus as set forth in claim 27, which further comprises means (3) provided upstream of said forging compression means for exerting stirring force on said cast block in advance of performing compression forging. An apparatus as set forth in claim 28, characterized in that said stirring means (3) exerts electromagnetic stirring force on said cast block in said stirring step. An apparatus as set forth in claim 29, characterized in that said stirring means performs said electromagnetic stirring at a frequency between 0.1 to 20 Hz. An apparatus as set forth in claim 29, characterized in that said electromagnetic stirring is performed with a magnetic flux density in a range between 200 to 1600 gauss. An apparatus as set forth in claim 29, characterized in that said stirring means (3) performs said electromagnetic stirring while said solid phase proportion is in a range between 0 to 80 percent. An appartus as set forth in claim 29, characterized in that said stirring means (3) performs said electromagnetic stirring while the thickness (d) of unsolidified layer is : 2.0 x √ D - 80 ≦ d ≦ 14.0 x √ D - 80 . An apparatus as set forth in claim 27, characterized in that said compression forging means ((4,5) performs compression forging of said cast block while ratio of reduction δ (mm) versus thickness of unsolidified layer (d mm) is held greater than or equal to 0.5.

Inventors: FUJIMURA TOSHIO KAWASAKI STEEL, IMAI TAKUO KAWASAKI STEEL CORP, KOJIMA SHINJI KAWASAKI STEEL C, MATSUKAWA TOSHITANE KAWASAKI S, FUJIMURA, TOSHIO KAWASAKI STEEL CORP.MIZUSHIMA WOR, IMAI, TAKUO KAWASAKI STEEL CORP. MIZUSHIMA WORKS, KOJIMA, SHINJI KAWASAKI STEEL CORP.MIZUSHIMA WORKS, MATSUKAWA, TOSHITANE KAWASAKI STEEL CORP.MIZUSHIMA
Applicants: KAWASAKI STEEL CO, KAWASAKI STEEL CORPORATION
Application year: 1987
Main classification: B22D11
IPC codes: B22D11, C21D7