MONOAZO LAKE PIGMENT

Abstract: A monoazo lake pigment of the formula (I): whose X-ray diffraction pattern shows a high diffraction strength at an diffraction angle (2ϑ ± 0.2°; Cu - K α ) of 4.9°, moderate diffraction intensities at 18.4°, 25.9° and 26.8° and relatively low diffraction intensities at 11.1°, 15.3° and 21.2°, and a printing ink, a paint and plastics in which the monoazo lake pigment is contained.

Description: This invention relates to a novel red monoazo lake pigment which is excellent in various properties including brightness, color strength, gloss, fastness to water and fastness to heat and highly useful in, for example, printing inks, paints, plastics and stationery products. A conventional monoazo lake pigment of the following formula (I): may be prepared by, for example, coupling a diazo component, which is obtained by diazotizing an amine of the following formula (II): at a temperature of 5°C or below, with a coupler component, which is obtained by dissolving an acid of the following formula (III): in an aqueous solution of a caustic alkali metal, at a temperature of 5°C or below to thereby give a monoazo dye of the following formula (IV): wherein M + / 2 represents a sodium, potassium or lithium ion; and then laking the resulting monoazo dye (IV) by adding an aqueous solution of a strontium salt to a suspension of said monoazo dye (IV) and then allowing the obtained mixture to react at a temperature of 5°C or below. An X-ray diffraction pattern of the conventional monoazo lake pigment of the formula (I) thus obtained shows a high diffraction intensity at a diffraction angle (2ϑ ± 0.2°; Cu - K α ) of 5.0; moderate diffraction intensities at 6.4° and 26.4°; and relatively low diffraction intensities at 7.8°, 13.9°, 16.5°, 21.1° and 28.5°. However the monoazo lake pigment having a crystal form of the above mentioned X-ray diffraction pattern, which will be referred to as α form hereinafter, has not been marketed yet. This is because that it is inferior to a presently marketed calcium lake pigment known as C.I. Pigment Red 57 : 1 in brightness, color strength and gloss when used in a printing ink or a paint; and in fastness to heat when used in coloring plastics, although the former is superior to the latter in fastness to water. Chemical Abstracts, volume 106 (1987), page 83, abstract no. 51794b discloses the preparation of a pigment of general formula in which the substituents R¹ and R² may represent inter alia methyl or hydrogen groups, and the metal M can represent inter alia strontium. The pigment is prepared by a diazotizing process and then coupling with an alkali salt at 0-25°C in the presence of rosin soap, surfactants and soluble salts of the metal M. FR-A-2 432 538 discloses the preparation of a calcium lake pigment of general formula in which the substituent D may represent one of The pigment is obtained by firstly preparing the corresponding ammonium salt which is then introduced into an aqueous solution of calcium chloride. Chemical Abstracts, volume 80 (1974), page 74, abstract no. 72062w discloses a red azo pigment lake of general formula in which the metal M can represent inter alia strontium. The pigment lakes are prepared by a coupling process in which a sodium rosin soap is added to an aqueous suspension of the stable form of the sodium salt of the above formula prepared by heating to 60°C, before the addition of for example strontium. In order to overcome these disadvantages, we have attempted to convert a monoazo dye of the formula (IV): wherein M + / 2 is as defined above; into a pigment. As a result, we have found that a pigment having a novel crystal form, which is excellent in various properties including brightness, color strength, gloss, fastness to water and fastness to heat and shows an X-ray diffraction pattern different from those of conventional α form pigments, can be obtained by heating said dye and then laking the same, thus completing the present invention. Accordingly, the present invention relates to a monoazo lake pigment of the formula (I): whose X-ray diffraction pattern shows a high diffraction intensity at an diffraction angle (2ϑ ± 0.2°; Cu - K α ) of 4.9°; moderate diffraction intensities at 18.4°, 25.9° and 26.8°; and relatively low diffraction intensities at 11.1°, 15.3° and 21.1°. Fig. 1 is an X-ray diffraction pattern (2ϑ ± 0.2°; Cu -K α ) of the β form monoazo lake pigment of the present invention as obtained in Example 1. Fig. 2 is an X-ray diffraction pattern (2ϑ ± 0.2°; Cu - K α ) of the conventional form monoazo lake pigment as obtained in Comparative Example 1. Fig. 3 is an infrared absorption spectrum of the β form monoazo lake pigment of the present invention as obtained in Example 1. Fig. 4 is an infrared absorption spectrum of the conventional α form monoazo lake pigment as obtained in Comparative Example 1. The monoazo lake pigment of the present invention, whose crystal form, which will be referred to as β form hereinafter, shows an X-ray diffraction pattern completely different from those of conventional α form pigments as described above, may be obtained by, for example, heating a suspension of the monoazo dye of the formula (IV), which is obtained in a conventional manner, usually to a temperature of 20 to 100°C, adding an aqueous solution of a strontium salt thereto and allowing the resulting mixture to react usually at a temperature of - 3 to 90°C to thereby laking the same. A particularly preferable process comprises heating said suspension in such a manner as to maintain the same at a temperature of 23 to 40°C for 2 to 20 minutes, then adding an aqueous solution of a strontium salt thereto and allowing the resulting mixture to react at 0 to 40°C, since a β form pigment being excellent in, for example, brightness, color strength and gloss can be efficiently obtained thereby. Examples of the strontium salt to be used in the laking step of the present invention include strontium chloride, strontium nitrate and strontium acetate. Effects of the Invention: When used in, for example, printing inks or paints, the novel β form red monoazo lake pigment of the present invention exhibits an excellent brightness, color strength and gloss and is highly fast to water. Further it is highly fast to heat, when employed in coloring plastics. Example: To further illustrate the present invention, and not by way of limitation, the following Examples will be given, wherein all parts and percentages are expressed by weight. Example 1 20.0 parts of 2-amino-5-methylbenzenesulfonic acid was dispersed in 200 parts of water and 22.0 parts of a 20 % aqueous solution of hydrochloric acid was added thereto. The resulting mixture was diazotizing by adding 25.1 parts of a 30 % aqueous solutin of sodium nitrite dropwise thereto while maintaining the resulting mixture at 0°C to thereby give a diazo solution. Then 20.6 parts of 2-hydroxy-3-naphthoic acid was dispersed in 242 parts of water and 22.0 parts of a 48 % aqueous solution of caustic soda was added thereto to thereby dissolve said acid. The coupler solution thus obtained was cooled to 0°C and the above mentioned diazo solution was added dropwise thereto under stirring. The resulting mixture was stirred at 0°C for 60 minutes to thereby complete the coupling. Subsequently 60 parts of a 10 % aqueous solution of sodium rosinate was added thereto and the obtained mixture was stirred for 60 minutes to thereby give a suspension of a monoazo dye. This dye suspension was heated to 30°C within 15 minutes and then maintained at this temperature for five minutes. Subsequently a solution obtained by dissolving 42.1 parts of strontium chloride hydride in 150 parts of water was added thereto and the resulting mixture was stirred at 30°C for 60 minutes. After adjusting the pH value to 7.6, the mixture was stirred for additional 60 minutes to thereby give a lake product. After the completion of the laking, the reaction mixture was stirred at 80°C for 60 minutes, hot-filtered, washed with water and then dried at 80°C. Thus 56.7 parts of a yellowish red monoazo lake pigment was obtained in the form of a powder. As shown in Fig. 1, an X-ray diffraction pattern of this pigment showed a high diffraction intensity at a diffraction angle (2ϑ ± 0.2°; Cu - K α ) of 4.9°, moderate diffraction intensities at 18.4°, 25.9° and 26.8° and relatively low diffraction intensities at 11.1°, 15.3° and 21.2°. Fig. 3 shows an infrared absorption spectrum of this pigment. Example 2 The procedure of Example 1 was followed except the following points. Namely, a dye suspension, which was obtained through a diazo coupling reaction similar to the one as described in Example 1, was heated to 36°C within 18 minutes and then maintained at this temperature for five minutes. Subsequently it was cooled again to 10°C and a solution of 33.8 parts of strontium acetate in 200 parts of water was added thereto. The resulting mixture was stirred at 10°C for 60 minutes. After adjusting the pH value to 7.6, it was further stirred for additional 60 minutes to thereby complete the laking. Thus 56.4 parts of a yellowish red monoazo lake pigment was obtained in the form of a powder. An X-ray diffraction pattern of this pigment was similar to that of the pigment as prepared in Example 1. Example 3 The procedure of Example 1 was followed except the following points. Namely, a dye suspension, which was obtained through a diazo coupling reaction similar to the one as described in Example 1, was heated to 70°C within 25 minutes. Then a solution of 42.1 parts of strontium chloride hydrate in 150 parts of water was added thereto. The resulting mixture was stirred at 70°C for 60 minutes. After adjusting the pH value to 7.6, it was further stirred for additional 60 minutes to thereby complete the laking. Thus 55.0 parts of a yellowish red monoazo lake pigment was obtained in the form of a powder. An X-ray diffraction pattern of this pigment was similar to that of the pigment as prepared in Example 1. Comparative Example 1 The procedure of Example 1 was followed except the following points. Namely, a dye suspension which was obtained through a diazo coupling reaction similar to the one as described in Example 1 was employed without heating. A solution of 42.1 parts of strontium chloride hydrate in 150 parts of water was added thereto and the resulting mixture was stirred at 0°C for 60 minutes. After adjusting the pH value to 7.6, the mixture was further stirred for additional 60 minutes to thereby complete the laking. Thus 57.0 parts of a yellowish red monoazo lake pigment was obtained in the form of a powder. As shown in Fig. 2, an X-ray diffraction pattern of this pigment showed a high diffraction intensity at a diffraction angle (2ϑ ± 0.2°; Cu - K α ) of 5.0°, moderate diffraction intensities at 6.4° and 26.4° and relatively low diffraction intensities at 7.8°, 13.9°, 16.5°, 21.1° and 28.5°. Fig. 4 shows an infrared absorption spectrum of this pigment. Test Example 1: Print test on litho printing ink 4.0 parts of a pigment obtained in one of Examples 1 to 3 or Comparative Example 1 was milled together with 16.0 parts of ink varnish in a Hoover Automatic muller mixer by repeating three times for 100 revolution mixing to thereby give an ink. The obtained ink was printed on a sheet of coated paper with the use of a small-scale rotary press (RI tester). The chroma (C*), gloss (60°) and density of the paper thus colored were measured with a spectrophotometer, a glossmeter and a Gretag densitometer (reflection densitometer) respectively. Table 1 shows the results. Chroma (C*) Gloss (60°) Gretag density Ex. 1 68.0 68.3 1.69 Ex. 2 66.0 69.0 1.68 Ex. 3 63.1 67.8 1.66 Comp. Ex. 1 44.5 24.0 0.75 The inks comprising the pigments of Examples 1 to 3 showed each a high chroma, an excellent gloss and a high density. Test Example 2: Test on paint 12 parts of a pigment obtained in one of Examples 1 to 3 or Comparative Example 1, 52 parts of a melamine alkyd resin having a weight ratio of melamine resin to alkyd resin of 3 : 7, 52 parts of xylene and 120 parts of glass beads were introduced into a polyethylene bottle. The mixture was dispersed with the use of a paint conditioner for one hour and then additional 50 parts of the melamine alkyd resin was added thereto. The resulting mixture was further dispersed for ten minutes with the paint conditioner. Then the glass beads were filtered off to thereby give a red paint. This paint was spray-baked onto a plate and the gloss of the film was measured with a glossmeter. Table 2 shows the results. Gloss (60°) Ex. 1 90 Ex. 2 93 Ex. 3 87 Comp. Ex. 1 45 The paints comprising the pigments of Examples 1 to 3 showed each an excellent gloss. Test Example 3: Test on fastness to water 12 parts of a pigment as obtained in one of Examples 1 to 3 or Comparative Example 1 or a commercially available calcium lake pigment (C.I. Pigment Red 57 : 1), 84 parts of an urethane resin, 12 parts of methyl ethyl ketone and 150 parts of steel beads were introduced into a polyethylene bottle. The mixture was dispersed with a paint conditioner for one hour. Then the steel beads were filtered off to thereby give a red ink. This red ink was drawn down on a sheet of nylon film with a 0.15 mm bar coater. Then a filter paper was placed onto the colored face of the film and the composite sheet thus formed was sandwiched between two aluminum plates and clipped. After boiling in water for one hour, the filter paper was peeled off and the degree of the migration of the pigment thereto was determined by measuring the density with a Gretag densitometer. Table 3 shows the results. Gretag density Ex. 1 0.02 Ex. 2 0.03 Ex. 3 0.05 Comp. Ex. 1 0.03 C.I. Pigment Red 57 : 1 0.44 The inks comprising the pigments of Examples 1 to 3 and Comaprative Example 1 were superior to the C.I. Pigment Red 57 : 1 in fastness to water. Test Example 4: Test on fastness to heat A dry color comprising six parts of a pigment as obtained in one of Examples 1 to 3 or Comparative Example 1 and two parts of zinc stearate was blended with 1200 parts of polypropylene. With the use of the resulting blend, a lithograph was formed with an in-line screw injection molding machine (three ounces) at a molding temperature of 280°C and at a residence time of 0 or 20 minutes. Then the fastness to heat of each pigment was evaluated by measuring the color difference ( Δ E). Table 4 shows the results. Color difference ( Δ E) Ex. 1 1.0 Ex. 2 0.8 Ex. 3 1.1 Comp. Ex. 1 3.5 The lithographs colored with the pigments as obtained in Examples 1 to 3 showed each a small color difference and a bright red color and was highly fast to heat.

Claims: A monoazo lake pigment of the formula (I): whose X-ray diffraction pattern shows a high diffraction intensity at an diffraction angle (2ϑ ± 0.2° ; Cu - K α ) of 4.9°, moderate diffraction intensities at 18.4°, 25.9° and 26.8° and relatively low diffraction intensities at 11.1°, 15.3° and 21.2°. A monoazo lake pigment according to claim 1, which is obtained by heating a monoazo dye of formula (IV): wherein M₂⁺ represents a sodium, potassium or lithium ion; and adding an aqueous solution of a strontium salt thereto, and allowing the resulting mixture to react, thus laking the same. A monoazo lake pigment according to Claim 2, obtained by adjusting the temperature of an aqueous suspension of the monoazo dye of the formula (IV) to a value of 20 to 100°C, and then reacting a mixture of said monoazo dye suspension and an aqueous solution of a strontium salt at a temperature of -3 to 90°C. A monoazo lake pigment according to Claim 2, obtained by adjusting the temperature of an aqueous suspension of the monoazo dye of the formula (IV) to a value of 23 to 40°C, maintaining the temperature of the aqueous suspension for 2 to 20 minutes, and then reacting a mixture of said monoazo dye and an aqueous solution of a strontium salt at a temperature of 0 to 40°C. A printing ink which comprises a monoazo lake pigment of the formula (I): whose X-ray diffraction pattern shows a high diffraction intensity at an diffraction angle (2ϑ ± 0.2° ; Cu - K α ) of 4.9°, moderate diffraction intensities at 18.4°, 25.9° and 26.8° and relatively low diffraction intensities at 11.1°, 15.3° and 21.2°. A paint which comprises a monoazo lake pigment of the formula (I): whose X-ray diffraction pattern shows a high diffraction intensity at an diffraction angle (2ϑ ± 0.2° ; Cu - K α ) of 4.9°, moderate diffraction intensities at 18.4°, 25.9° and 26.8° and relatively low diffraction intensities at 11.1°, 15.3° and 21.2°. Plastic which comprise a monoazo lake pigment of the formula (I): whose X-ray diffraction pattern shows a high diffraction intensity at an diffraction angle (2ϑ ± 0.2° ; Cu - K α ) of 4.9°, moderate diffraction intensities at 18.4°, 25.9° and 26.8° and relatively low diffraction intensities at 11.1°, 15.3° and 21.2°.

Inventors: ANDO, HIROHITO, KOBAYASHI, NAGATOSHI
Applicants: DAINIPPON INK AND CHEMICALS, INC.
Application year: 1987
Main classification: C09B63
IPC codes: C09B67, C09B63