MAGNETIC RECORDING MEDIUM

Abstract: A magnetic recording medium with improved output characteristics and durability is provided by using magnetic powder comprising iron-containing particles each of which carries a compound containing aluminum and/or a compound containing silicon in such amounts that, in the whole magnetic powder, a weight ratio of aluminum to iron is from 0.010:1 to 0.150:1 and a weight ratio of silicon to iron is from 0.040:1 to 0.150:1.

Description: The present invention relates to a magnetic recording medium such as a magnetic tape and magnetic disc. A coating type magnetic recording medium, which comprises a substrate and a magnetic layer formed on a substrate by applying a magnetic paint on the substrate followed by drying, is widely used since it has good handling property and mass productivity so that it is suitable for production in an industrial scale. For improving recording characteristics of the coating type magnetic recording medium, various proposals have been made to add a larger amount of magnetic powder as a magnetic recording element to the magnetic layer, or to more homogeneously disperse the magnetic powder in the magnetic layer. As the result, output characteristics, particularly electromagnetic conversion characteristics have been improved. During the use of a video tape or a floppy disc, however, the homogeneously contained magnetic powder in a large amount in the magnetic layer is scraped off from the surface by a magnetic head to which the magnetic layer is slidingly contact, whereby the output characteristics and the electromagnetic conversion characteristics are deteriorated. To prevent the scraping of the magnetic powder, abrasion particles having greater hardness than the magnetic head and the magnetic powder are added to the magnetic layer and, if desired, a liquid lubricant is additionally used. Such techniques are disclosed in Japanese Patent Publication Nos. 18572/1973, 15003/1973, 28642/1977, 49961/1977, 15771/1980, 24171/1980 and 51171/1982 and Japanese Patent Kokai Publication (unexamined) Nos. 466/1972, 56404/1973, 115510/1974, 62604/1975, 92101/1975, 93405/1975, 147308/1975, 31201/1976, 45309/1977, 75410/1977, 88307/1977, 97709/1977, 97710/1977, 16605/1978, 47806/1978, 134407/1978, 21805/1979, 103005/1979, 143608/1979, 1638/1980, 17811/1980, 17813/1980, 17814/1980, 17835/1980, 129935/1980, 150131/1982, 159236/1983 and 144036/1984. EP-0 165 536 A2 discloses a magnetic recording medium comprising a substrate and a magnetic layer formed on said substrate, said magnetic layer including iron-containing magnetic powder dispersed in a binder. Furthermore, it is disclosed to use SiO₂ and Al₂O₃ as a sinter-protection. However, the addition of the non-magnetic materials such as the abrasive and the lubricant which do not contribute to magnetic recording to the magnetic layer not only decreases the volume ratio of the contained magnetic powder in the magnetic layer, but also makes it difficult to homogeneously disperse both the magnetic powder and the non-magnetic materials. That is, when the magnetic powder alone is dispersed in a binder resin of the magnetic layer, only the dispersibility of the magnetic powder is taken into consideration. When the non-magnetic materials, for example, the abrasive particles are used, they should be dispersed in the binder resin in addition to the magnetic powder. In such case, when a mixing ratio of the magnetic powder and the non-magnetic materials is not kept constant in the magnetic layer, the magnetic characteristics become ununiform in the magnetic layer and in turn the output characteristics fluctuate. Therefore, recently, it is desired to provide another way to achieve both good output characteristics and durability of the magnetic recording medium at a high level. One object of the present invention is to provide a magnetic recording medium which has good electromagnetic conversion characteristics and simultaneously can solve various problems caused by sliding contact of the magnetic recording medium to a magnetic head. Another object of the present invention is to provide a magnetic recording medium comprising a magnetic layer containing magnetic powder which achieves good electromagnetic conversion characteristics and improves the durability of the medium. These and other objects of the present invention are achieved by a magnetic recording medium according to the independent claim. Further embodiments can be found in the claims being dependent therefrom. Figure is a graph showing the weight ratios of silicon to iron and aluminum to iron of the magnetic powder The magnetic powder consisting of particles surfaces of which are covered with an aluminum-containing compound is disclosed in Japanese Patent Kokai Publication Nos. 122213/1977 and 134858/1977, and the magnetic powder consisting of particles surfaces of which are covered with a silicon-containing compound is disclosed in Japanese Patent Kokai Publication Nos. 30758/1977 and 134858/1977. When the former is used alone, a magnetic recording medium has poor output characteristics although its durability is good, while when the latter is used alone, a magnetic recording medium has poor durability although its output characteristic is good. According to the study by the present inventors, it was found that, when the aluminum-containing compound or the silicon-containing compound is provided in the form of an abrasive instead of the coating on the magnetic powder iron-containing particles, for example, when a mixture of the magnetic powder consisting of iron-containing particles surfaces of which are covered with the silicon-containing compound and Al₂O₃ powder is used, the produced magnetic recording medium has unsatisfactory output characteristics and durability. When magnetic powder particles covered with both the aluminum-containing compound and the silicon-containing compound as disclosed in Japanese Patent Publication No. 19168/1974 are used alone, a produced recording medium has good output characteristics and durability insofar as the aluminum-containing compound and the silicon-containing compound are used in a certain specific ratio. It has been found that, to produce a magnetic recording medium which satisfies both output characteristics and durability, it is desirable for aluminum and silicon to be present on the surfaces of the magnetic powder particles in a certain ratio in the form of an aluminum-containing compound and a silicon-containing compound rather than they are contained in the magnetic layer as abrasives in the form of Al₂O₃ or SiO₂, independently. The reasons for this have not been known but is supposed to be as follows: (i) When the output characteristics are improved by homogeneously dispersing the magnetic powder in the magnetic layer, the aluminum-containing compound and the silicon-containing compound carried on the surface of the magnetic powder particles are also homogeneously dispersed in the magnetic layer. Therefore, suitable amounts of these compounds can be exposed to the surface of the magnetic layer so that uniform contact between the magnetic recording medium and the magnetic head can be achieved. (ii) In comparison with a case where the Al₂O₃ particles and the SiO₂ particles are used together with the conventional magnetic powder, an abrasion effect is achieved by a smaller volume of aluminum and silicon in the magnetic layer. Therefore, the content of the magnetic powder in the magnetic layer can be increased. (iii) When the abrasives containing aluminum and/or silicon is contained in the magnetic layer together with the conventional magnetic powder with insufficient dispersion of the abrasives, magnetization strength of the magnetic layer becomes ununiform, whereby the output characteristics are considerably deteriorated. In an extreme case, agglomerates of the undispersed abrasive particles are exposed on the surface of the magnetic layer and in turn the surface smoothness of the magnetic layer is greatly deteriorated. However, according to the present invention, such defects are hardly found. (iv) Since both of the aluminum-containing compound and the silicon-containing compound have good affinity with the binder resin, their combination keeps the properties of the magnetic surface uniform. (v) Since the aluminum-containing material such as Al₂O₃ is homogeneously dispersed by a function of silicon which has strong affinity with said material and silicon having good affinity with a material of the magnetic head is homogeneously dispersed in the surface layer of the magnetic layer, the magnetic recording medium is not adversely affected by the sliding contact with the magnetic head. It should be noted that the magnetic recording medium which satisfies both the output characteristics and durability is produced only when the aluminum-containing compound and the silicon-containing compound are contained in a certain specific amount range. If one of them is contained in an amount outside this range, at least one of the output characteristics or durability is deteriorated. For example, Japanese Patent Kokai Publication (unexamined) No. 25901/1981 discloses magnetic powder particles a surface of which is covered with the aluminum-containing compound and the silicon-containing compound. In this magnetic powder particles, aluminum is contained in an Al/Fe weight ratio of 10⁻⁵:1 to 0.02:1 and silicon is contained in a Si/Fe weight ratio of 0.002:1 to 0.05:1. That is, the adhered amounts of the aluminum and silicon components are in the domain D in Figure. It was found that the magnetic recording medium having such magnetic powder particles does not have satisfactory output characteristics and durability. According to the present invention, the Al/Fe weight ratio is in the range of 0.060:1 to 0.130:1, and the Si/Fe weight ratio is in the range of 0.010:1 to 0.090:1 which are in the domain B, B' and C in Figure. When the weight ratio of aluminum to iron is larger than the above range, not only the electromagnetic conversion characteristics are deteriorated but also the magnetic head is vigorously abrased by the sliding contact between the head and the magnetic recording medium. When it is smaller than the above range, the benefits of the present invention are hardly achieved. When the weight ratio of silicon to iron is larger than the above range, the electromagnetic conversion characteristics are considerably deteriorated. When it is smaller than the above range, the benefits of the present invention are hardly achieved. A weight ratio of aluminum to silicon (Al/Si) is from 2:1 to 15:1. When the content of aluminum is too large in comparison with that of silicon, the magnetic head is extremely abrased by the sliding contact between the head and the magnetic recording medium. When the content of silicon is too large in comparison with that of aluminum, the electromagnetic conversion characteristics are deteriorated. Therefore, more preferably, the contents of aluminum and silicon are below the line corresponding to Al/Si=1, namely in the domains B and C. Therefore, the most preferred contents of aluminum and silicon are in the domain C in Figure. The output characteristics and durability of the magnetic recording medium are improved particularly when the content of the magnetic powder in the magnetic layer is not less than 15 % by volume. Specific examples of the magnetic powder comprising iron are γ-Fe₂O₃, Fe₃O₄, an intermediate iron oxide of γ-Fe₂O₃ and Fe₃O₄, cobalt-containing γ-Fe₂O₃, cobalt-containing Fe₃O₄, a cobalt containing intermediate iron oxide of γ-Fe₂O₃ and Fe₃O₄, iron nitride, an alloy comprising iron, cobalt and nickel, and barium ferrite which may be modified with titanium or cobalt. The present invention is particularly effective when the magnetic powder consists of such metal or alloy that is soft and easily corroded by moisture and/or oxygen in the air. This is because the aluminum or silicon-containing compound on the surfaces of the magnetic powder particles acts as a protective layer against oxidation and the like. The magnetic recording medium containing the metal oxide type magnetic powder is more widely used than the metal type magnetic powder and expected to be used under severer conditions. When the present invention is applied to such magnetic recording medium, it is possible to improve the desirable properties of the metal oxide type magnetic powder so that the magnetic recording medium can be used in wide ranges of temperature and humidity. The magnetic particle to be used according to the present invention may be of any shape such as granule, sphere, acicular shape, plate or ellipsoid. Particularly preferred is magnetic powder having a particle shape which is easily orientated in parallel with the surface of the substrate by shear force during application of the magnetic paint. Examples of such easily orientated magnetic powder are those having an acicular particle shape or a plate-like particle shape. This is because the larger surface area of such particle is in parallel with the surface of the magnetic layer contacting the magnetic head, namely in the running direction of the magnetic recording medium and therefore the aluminum or silicon-containing compound can be effectively placed near the surface of the magnetic layer. Further, the easily orientated magnetic powder can be contained in a higher volume content in the magnetic layer. Preferably, an average major axis of the acicular or granular magnetic powder particle and an average diameter of the plate-like magnetic powder particle is from 0.01 to 1 µm. An average aspect ratio (average major axis/average minor) of the acicular magnetic powder particle is preferably from 3/1 to 20/1. An average plate ratio (average diameter/average thickness) is preferably from 2/1 to 30/1. According to the present invention, the surface smoothness of the magnetic layer is improved. A center line average height of the surface of the magnetic layer can be reduced to 0.01 µm or less according to the present invention. This is partly because the aluminum and silicon-containing compounds are carried on the surface of the magnetic powder particles which are homogeneously dispersed in the magnetic layer instead of placing the abrasive particles on the surface of the magnetic powder particles, so that it is possible to avoid adverse influence of the extruding particles, and partly because the aluminum or silicon-containing compound can be effectively contained in the magnetic layer particularly when the magnetic powder particles have the easily orientated shape. The magnetic particles surfaces of which are covered with the aluminum and silicon-containing compound may be prepared by contacting the magnetic powder particles with gas comprising such compounds, or by dipping the particles in a solution containing such compounds. Further, in case of the metal type magnetic powder prepared by reduction of goethite, treatment with the aluminum or silicon-containing compound may be carried out during formation or post-treatment of goethite followed by reduction of the treated goethite to form the magnetic powder. The aluminum or silicon-containing compound is usually an oxide or water-containing oxide of aluminum or silicon, which has best effects among the aluminum or silicon compounds. Alternatively, an organic compound containing aluminum or silicon (e.g. aluminum isopropoxide, tetramethoxysilane, and silicone oil) may be used according to the present invention. When a two-layer coating of the aluminum-containing compound and the silicon-containing compound is formed on the surfaces of the magnetic powder particles, the sequence of two layers is arbitrary. Preferably, the aluminum-containing compound forms the upper layer, whereby the durability of the magnetic recording medium is greatly improved. The reasons for this are that the layer of the silicon-containing compound has good adherence with both the surface of the magnetic powder particle and the layer of the aluminum-containing compound, and that the aluminum-containing compound which is harder than the silicon-containing compound forms the outer surface of the magnetic powder particle so that the surface of the magnetic powder particle becomes harder. The magnetic particles the surfaces of which are covered with the coating having large surface hardness firmly adhered to said surfaces can impart good abrasion effect to the magnetic layer and make the magnetic layer more tough, so that wear or break of the magnetic powder particles due to sliding contact of the magnetic layer to the magnetic head is effectively prevented and removal of the magnetic powder and drop out of the recorded signals are avoided. Thus, the durability of the magnetic recording medium is satisfactorily improved. Since the layer of the aluminum-containing compound formed on the surface of the magnetic particle has good affinity with the binder resin and is firmly bonded to the binder resin through functional groups such as hydroxyl groups, the dispersibility of the magnetic powder in the binder resin is improved and therefore the magnetic recording medium containing such magnetic powder has improved output characteristics. Aluminum atoms and silicon atoms are carried by the whole magnetic powder, namely statistically carried by the magnetic powder. That is, the magnetic powder may retain both the aluminum-containing compound and the silicon-containing compound on the surface of one particle, or the magnetic powder may be a mixture of particles the surfaces of which are covered with the aluminum-containing compound and the particles the surface of which are covered with the silicon-containing compound. When the magnetic recording medium is produced by using the former magnetic powder, ununiformity of the durability over the surface of the magnetic recording medium is decreased since the aluminum-containing compound and the silicon-containing compound are homogeneously present on the surfaces of the magnetic powder particles. Even when the latter mixture type magnetic powder is used, the electromagnetic conversion characteristics of the magnetic recording medium is excellent since the number of steps for coating different kinds of atoms over the surfaces of the magnetic particles can be reduced, preferably to only one step. The aluminum-containing compound and the silicon-containing compound can be formed either by a vapor deposition method or a liquid coating method by a method similar to those disclosed in the above described patent publications. The both compounds may be applied by the same method or the different methods. The magnetic particles the surfaces of which are covered with the aluminum-containing compound and the silicon-containing compound are mixed with and dispersed in a thermoplastic binder resin having a softening point of 140°C or lower, a polymerization degree of about 200 to 2,000 and a number average molecular weight of about 10,000 to 200,000. Specific example of the binder resin are vinyl chloride-vinyl acetate copolymers, vinyl chloride-vinyl acetate-vinyl alcohol copolymers, vinyl chloride-vinylidene chloride copolymers, vinyl chloride-acrylonitrile copolymers, methacrylate-acrylonitrile copolymers, polyurethane resins, nitrocellulose and the like. A magnetic paint containing the magnetic powder and the binder resin may be prepared by a conventional method. For example, the magnetic powder and the binder resin are mixed with an organic solvent in which the binder resin is dissolved to form a paste. Then, a viscosity of the paste is adjusted by dilution with the organic solvent and treated in a suitable mixer such as a ball mill and a sand mill to prepare the magnetic paint. Examples of the organic solvent are methyl ethyl ketone, methyl isobutyl ketone, toluene, ethyl acetate, tetrahydrofuran, dioxane, cyclohexanone and mixtures thereof. The magnetic paint can be applied on the substrate such as a polyester or polyacetate film by a conventional method, for example, with a coater. The magnetic paint may contain conventionally used additives such as an organic dispersant, an electrically conductive filler such as carbon black, a solid or liquid lubricant and the like. Further, the magnetic paint may contain the conventional abrasive such as Al₂O₃, SiO₂, TiO₂, Cr₂O₃, α-Fe₂O₃ and the like. The present invention will be explained further in detail by following examples, in which parts are by weight unless otherwise indicated. Table 1 shows the properties of the magnetic powder used in Examples and Comparative Examples. Each magnetic powder was prepared as follows: Magnetic powder No. 1 In a 1 N aqueous solution of sodium hydroxide (300 l), goethite powder (average major axis: 0.3 µm, average aspect ratio (average major axis/average minor axis): 14) (5 kg) was suspended, and a 0.5 M aqueous solution of Al₂(SO₄)₃ (15 l) was added. Then, carbon dioxide gas was bubbled in the mixture with thoroughly stirring to neutralize the mixture. After pH was reduced to less than 8, the powder was filtered, washed with water and well dried. The surface treated goethite powder was reduced in a hydrogen stream at 500°C for 4 hours to produce iron magnetic powder having a coating containing aluminum on the particle surface. Magnetic powder No. 2 In a 1 N aqueous solution of sodium hydroxide (300 l), goethite powder (average major axis: 0.3 µm, average aspect ratio: 14) (5 kg) was suspended, and a 1 M aqueous solution of Na₄SiO₄ (11 l) was added. Then, carbon dioxide gas was bubbled in the mixture with thoroughly stirring to neutralize the mixture. After pH was reduced to less than 8, the powder was filtered, washed with water and well dried. The surface treated goethite powder was reduced in a hydrogen stream at 500°C for 4 hours to produce iron magnetic powder having a coating containing silicon on the particle surface. Magnetic powder No. 3 In a 0.5 N aqueous solution of sodium hydroxide (300 ml), commercially available metal iron magnetic powder having SiO₂ coatings on particle surfaces (average major axis: 0.2 µm, Si content: 2 % by weight based on the weight of iron) (5 g) was suspended, and a 0.5 M aqueous solution of Al₂(SO₄)₃ (13 ml) was added. Then, carbon dioxide gas was bubbled in the mixture with thoroughly stirring to neutralize the mixture. After pH was reduced to less than 8, the metal iron powder was recovered by filtration and washed with water followed by removal of water by a solvent replacing method and drying to produce the metal iron magnetic powder having an under coating containing silicon and an upper coating containing aluminum on the particle surface. Magnetic powder Nos. 4, 9 and 14 In the same manner as in the production of Magnetic powder No. 3 but using commercially available metal iron magnetic powder having SiO₂ coatings on particle surfaces, an average particle size (major axis) and an aspect ratio as shown in Table 1 and changing the concentration and amount of the aqueous solution Al₂(SO₄)₃ so as to adjust the weight ratio of aluminum to iron as shown in Table 1, metal iron magnetic powder having an under coating containing silicon and an upper coating containing aluminum on the particle surface was produced. Magnetic powder No. 5 To a 1 N aqueous solution of sodium hydroxide (300 l), goethite powder (average major axis: 0.3 µm, average aspect ratio: 14) (5 kg) was suspended, and a 1 M aqueous solution of Na₄SiO₄ (5 l) was added. Then, carbon dioxide gas was bubbled in the mixture to neutralize the mixture to produce goethite powder having a coating of silica gel, which was then washed with water (?) and well dried. The dried goethite powder was hated at 400°C for 2 hours to obtain hematite powder. Hematite powder (500 g) was suspended and well dispersed in a 0.5 N aqueous solution of sodium hydroxide (80 l) and then a 0.5 M aqueous solution of Al₂(SO₄)₃ (2 l) was added. Thereafter, carbon dioxide gas was bubbled in the mixture to neutralize the mixture to obtain hematite powder having a coating of aluminum hydroxide gel on a particle surface, which was washed with water and well dried. The produced hematite powder had a coating of SiO₂ on the particle surface and a coating of Al₂O₃ on the SiO₂ coating. The hematite powder was then heated and reduced in a hydrogen stream at 500°C for 4 hours to produce metal iron magnetic powder having an under coating containing silicon and an upper coating containing aluminum on the particle surface. Magnetic powder Nos. 7, 8, 10-13 and 15-19 In the same manner as in the production of Magnetic powder No. 5 but changing the concentrations and amounts of the aqueous solutions of Al₂(SO₄)₃ and Na₄SiO₄ so as to adjust the weight ratios of aluminum and silicon to iron as shown in Table 1, metal iron magnetic powder having an under coating containing silicon and an upper coating containing aluminum on the particle surface was produced. Magnetic powder No. 20 In the same manner as in the production of Magnetic powder No. 19 but changing the sequence of the formations of the SiO₂ coating and the Al₂O₃ coating, metal iron magnetic powder having an under coating containing aluminum and an upper coating containing silicon on the particle surface was produced. Magnetic powder No. 21 In a 1 N aqueous solution of sodium hydroxide (1 l), goethite powder (average major axis: 0.4 µm, average aspect ratio: 15) (24 g) was suspended, and Al₂(SO₄)₃· 16H₂O (400 mg) and Na₂SiO₄ (10 g) were added. Then, carbon dioxide gas was bubbled in the mixture to reduce pH of the mixture to 6-8 so that Al(OH)₃ and silica gel were deposited on the surfaces of the goethite particles. The powder was filtered and dried at 70°C for 5 hours. The surface treated goethite powder (1 g) was reduced in a hydrogen stream at 320°C for 4 hours to produce iron magnetic powder having a coating containing aluminum and silicon on the particle surface. Magnetic powder No. 22 In a 2 N aqueous solution of sodium hydroxide (1 l), goethite powder (average major axis: 0.4 µm, average aspect ratio: 14) (24 g) was suspended, and Al₂(SO₄)₃· 16H₂O (400 mg) was added. Then, carbon dioxide gas was bubbled in the mixture to reduce pH of the mixture to 6-8 so that Al(OH)₃ was deposited on the surfaces of the goethite particles. The powder was filtered and dried at 70°C for 5 hours. The dried powder was mixed with and dispersed in a solution of a silicone oil (dimethylpolysiloxane. KF 96 manufactured by Shinetsu Chemical. 100 CS) (0.48 g) in methyl ethyl ketone (400 ml). After filtration, the powder was dried at 70°C for 3 hours. The surface treated goethite powder (1 g) was reduced in a hydrogen stream at 320°C for 4 hours to produce iron magnetic powder having an under coating containing aluminum and an upper coating containing silicon on the particle surface. Magnetic powder No. 23 Commercially available untreated cobalt-containing γ-Fe₂O₃ magnetic powder (cobalt content: 2.5 % by weight) was used. Magnetic powder No. 24 In a 2 N aqueous solution of sodium hydroxide (1 l), the same cobalt-containing γ-Fe₂O₃ magnetic powder as Magnetic powder No. 23 (24 g) was suspended, and a 1 M aqueous solution of Na₄SiO₄ (25 ml) and 0.5 M aqueous solution of Al₂(SO₄)₃ (40 ml) were added. Then, carbon dioxide gas was bubbled in the mixture with stirring to neutralize the mixture to form a coating comprising the silicon-containing compound and the aluminum-containing compound on the surface of the powder particles. The powder was filtered, washed with water and dried at 60°C under reduced pressure to obtain γ-Fe₂O₃ magnetic powder having a coating containing aluminum and silicon on the particle surface. Magnetic powder No. 25 Commercially available untreated hexagonal system plate-like barium ferrite magnetic powder was used. Magnetic powder No. 26 To a 2 N aqueous solution of sodium hydroxide (1 l), the same hexagonal system plate-like barium ferrite magnetic powder as Magnetic powder No. 25 (20 g) was suspended, and a 1 M aqueous solution of Na₄SiO₄ (20 ml) and 0.5 M aqueous solution of Al₂(SO₄)₃ (35 ml) were added. Then, carbon dioxide gas was bubbled in the mixture with stirring to neutralize the mixture to form a coating comprising the silicon-containing compound and the aluminum-containing compound on the surface of the powder particles. The powder was filtered, washed with water and dried at 60°C under reduced pressure to obtain barium ferrite having a coating containing aluminum and silicon on the particle surface. Examples 1-8 and Comparative Examples 1-19 By using the magnetic powder shown in Table 1, a magnetic recording medium (magnetic tape) was produced according to one of the following production methods: Production methods Method No. 1 In a 3 liters steel-made ball mill, the magnetic powder (100 parts), a vinyl chloride-vinyl acetate-vinyl alcohol copolymer (VAGH®) (10 parts), a polyurethane resin having an average molecular weight of 20,000 to 30,000 (Pandex® T-5201) (6 parts), myristic acid (5 parts), carbon black (HS-500, a trade name of Asahi Denka) (1 part), toluene (85 parts) and methyl isobutyl ketone (85 parts) were charged and stirred for 72 hours to prepare a magnetic paste. With the magnetic paste, toluene (40 parts) and a polyisocyanate compound (Colonate® L) (2 parts) were mixed to prepare a magnetic paint. The magnetic paint was coated on a polyester film having a thickness of 12 µm so that the dried thickness of the coating was 4 µm and dried. The coated film was, then, planished and cut to a width of 1.27 cm (1/2 inch) to produce a magnetic tape. Method No. 2 In the same manner as in Method No. 1 but additionally using n-butyl stearate (1 part), α-Al₂O₃ powder (particle size: 0.4 µm. AKP-30, a trade name of Sumitomo Chemical) (5 parts) and liquid paraffin (1 part) for the preparation of a magnetic paste, a magnetic tape was produced. Method No. 3 In the same manner as in Method No. 1 but additionally using α-Fe₂O₃ powder (particle size: 0.01 µm. R-1107, a trade name of Titan Industries) (3 parts) for the preparation of a magnetic paste, a magnetic tape was produced. Method No. 4 In the same manner as in Method No. 1 but additionally using SiO₂ powder (particle size: 0.01 µm. Aerosil® 200) (5 parts) for the preparation of a magnetic paste, a magnetic tape was produced. Properties of the produced magnetic tape were measured as follows. The results are shown in Table 2 together with the number of the used magnetic powder. RF output After recording signals of 5 MHz at a constant level, output during reproducing was measured and the result is shown in Table 2 in terms of a comparative value with the output of the tape of Comparative Example 2 being 0 (zero). In Example 8 and Comparative Examples 10 11 and 12, since the kinds of the magnetic powder were different from that used in other Examples and Comparative Examples, comparative values with Comparative Example 10 or 12 were also shown in brackets. Durability By using a commercially available videotape recording (VTR) device, measured was a time period till the output decreased by 3 dB when a still image was reproduced at -5°C Surface smoothness By using a tracer type surface roughness tester, surface roughness (C.L.A., center line average) of the magnetic tape was measured at a tracer speed of 0.06 cm/sec. with cut off of 0.08 mm. The result is shown in terms of a relative value calculated according to the following equation with using the tape of Comparative Example 2 as a standard: Jitter Jitter was expressed by the maximum value of fluctuation of distance in horizontal synchronizing signals of image signals reproduced by a VTR device, which was measured by a jitter meter (MK-611 A manufactured by Meguro Denpa Co., Ltd.). Erasing characteristic By using a commercially available VTR device, signals of 1 KHz was recorded in a sound track at a constant level. After erasing those signals, residual output of the recorded signals was measured and evaluated according to the following equation: As is clear from the results of Table 2, the magnetic tapes of the present invention (Examples 1-8) have much better output characteristics such as RF output and durability than the magnetic tapes of Comparative Examples. Particularly, the magnetic tapes utilizing the magnetic powder having the coating containing both aluminum and silicon are excellent in jitter. When the Al/Si ratio is in the range between 2 and 15 and the powder particles are of acicular shape (Examples 1-3, 5 and 6), the magnetic tapes have superior RF output to those of Comparative Examples 12-15 and 17-18, and further superior durability and surface smoothness to that of Example 4. The combination of the magnetic powder particles surfaces of which are covered with the silicon-containing compound and Al₂O₃ particles (Comparative Example 9) or the combination of the magnetic powder particles of which are covered with the aluminum-containing compound and the SiO₂ particles (Comparative Example 8) could not provide a magnetic tape having satisfactory output characteristics.

Claims: A magnetic recording medium comprising a substrate and a magnetic layer which is formed on said substrate, said magnetic layer including magnetic powder dispersed in a binder, characterized in that said magnetic powder comprises iron-containing particles the surfaces of which are covered with both a compound containing aluminum and a compound containing silicon in such amounts that the weight ratio of aluminum to silicon is from 2:1 to 15:1 and the weight ratio of aluminum to iron is from 0.060:1 to 0.130:1 and a weight ratio of silicon to iron is from 0.010:1 to 0.090:1. The magnetic recording medium according to claim 1, wherein the magnetic powder is contained in the magnetic layer in a volume not less than 15 % by volume. The magnetic recording medium according to claim 1, wherein the magnetic powder consists of particles having easily orientated shape. The magnetic recording medium according to claim 1, wherein the magnetic powder is metal iron magnetic powder. The magnetic recording medium according to claim 1, which has surface roughness of 0.01 µm in terms of center line average height. The magnetic recording medium according to claim 1, wherein aluminum is present in the form of aluminum oxide or water-containing aluminum oxide. The magnetic recording medium according to claim 1, wherein the magnetic powder consists of magnetic powder particles each having an under coating of the silicon-containing compound and an upper coating of the aluminum-containing compound on the under coating. The magnetic recording medium according to claim 7, wherein the under coating consists of silicon oxide or water-containing silicon oxide, and the upper coating consists of aluminum oxide or water-containing aluminum oxide.

Inventors: AMEMIYA, MASAHIRO, ASADA, SEIICHI, KAWARAI, SEIGI, MIYAKE, AKIRA, SUEYOSHI, TOSHINOBU
Applicants: HITACHI MAXELL LTD.
Application year: 1987
Main classification: G11B5
IPC codes: G11B5