Silicon nitride sintered material for cutting tools and process for making the same

Abstract: A silicon nitride sintered material for cutting tools comprising from about 3 to l0 wt% of partially stablized zirconium oxide, from about l to 5 wt% of aluminum oxide, and from about l to l0 wt% of yttrium oxide, the balance being silicon nitride, and the process for makine the same

Description: This invention relates to a silicon nitride sintered material having a high strength and a high toughness, which is suitable for cutting tools, and a process for making the same. As materials for high speed cutting tools for steel and cast iron, composite materials in which a super hard alloy is coated with ceramics, and alumina sintered materials have been used. However, tools of the composite material of a super hard alloy and ceramics have insufficient heat crack resistance, so that the practical cutting speed is restricted at most 300 m/min. On the other hand, tools of the alumina sintered material have superior heat oxidation resistance in high speed cutting and a low chemical reactivity in comparison to the above-mentioned composite material tools, but they are not satisfactory in toughness and heat impact resistance, and are liable to disadvantageously develop a broken edge during continuous cutting (lathe) as well as discontinuous cutting (fraise) when a material to be cut yields discontinuous scraps upon cutting, such as a cast iron. It is difficult to cut a cast iron material stably at a high speed using conventional cutting tools of the above-mentioned composite material or alumina sintered material. JP-A-59190270 and JP-A-57071871 use fully stabilized and non-stabilized ZrO 2 in similar silicon nitride based sintermaterials. An object of this invention is to provide a silicon nitride sintered material for cutting tools, which can be used for stable cutting at a high speed. Another object of this invention is to provide a silicon nitride sintered material having good wear resistance as well as a high strength and toughness. A further object of this invention is to provide a silicon nitride sintered material which does not undergo edge damage even under cutting conditions involving a violent heat impact, when used in a wet cutting, a high speed lathe or discontinuous cutting, and the like of cast iron. A further object of this invention is to provide a process for making such silicon nitride sintered materials. It has now been found that these objects of this invention can be obtained if the starting powder mixture comprises defined amounts of partially stabilized zirconium oxide powder, aluminum oxide powder, yttrium oxide powder and silicon nitride powder. The silicon nitride sintered material for cutting tools according to this invention is produced by a process comprising the steps of mixing from 3 to l0 wt% of partially stabilized zirconium oxide powder, from l to 5 wt% of aluminum oxide powder, from about l to l0 wt% of yttrium oxide powder, and the balance of silicon nitride powder; and sintering the resulting mixed powder at from about l,600 to l,900°C in an atmosphere of non-oxidative gas. The non-oxidative gas is preferably nitrogen gas. The priod of time for sinterring is preferably from 2 to 5 hours. The silicon nitride powder preferably contains at least about 40 wt%, more preferably from about 40 to 60 wt%, of β-phase cristals (β-Si 3 N 4 ). Such a silicon nitride powder can be obtained, e.g., by subjecting a commercial α-phase crystal powder, preferably an amorphous Si 3 N 4 powder, to heat treatment at from about l,600 to l,900°C in an atmosphere of nitrogen gas at form about l to l0 atm for from about 3 to 6 hours to convert at least a part therof into β-phase crystals. If desired, the entire silicon nitride powder may be β-phase cryltals. The partially stabilized zirconium oxide is a ZrO 2 containing partially stable cubic crystals, and is described in detail, e.g., in R.C. Garvie et al, Nature , vol. 258, pp 703 (l975) and N. Claussen et al, Proc. 4th Int. Meeting on the Modern Cer. Tech. , Elsevier Sci. Pub. Co., Amsterdam, Oxfdord, N.Y., pp 680 (l980). The prtialy stabilized zirconium oxide may be produced, as is known in the art, by heating in an inert gas (e.g., argon gas) ZrO 2 at elevated temperature (e.g., at l,000 to l,400°C for 2 hours) with a suitable amount (e.g.. 3 to 8 mol%) of an oxide of yttrium, calcium, magnesium and the like. A ZrO 2 partially stablized with Y 2 O 3 is preferred. In the silicon nitride sintered material for cutting tools according to this invention, the most amount, preferably at least about 90%, of Si 3 N 4 is in a β-phase, and the partially stabilized ZrO 2 is dispersed in the Si 3 N 4 matrix, so that the silicon nitride sintered material has a very high toughness in addition to its inherent high hardness and heat stability, and has a high heat conductivity and a small heat expansion coefficient. Therefore, its application for cutting tools provides cutting tools of far longer life than previous tools of alumina sintered materials without edge damage, chipping, etc. when used in lathe processing or wet cutting processing with a violent heat cycle. The partially stabilized zirconium oxide is used to improve the sintering properties of silicon nitride and to increase the toughness of the resulting sintered material. According to this invention, Y 2 O 3 , MgO, or the like, which is in a form of a solid solution in partially stabilized ZrO 2 , contributes the improvement in sintering properties upon sintering, whereas even the addition of Y 2 O 3 itself as a sintering assistant in the use of unstabilized ZrO 2 cannot provide sufficient improvement in sintering properties. Additionally, the process according to this invention gives a mixture of cubic and tetragonal crystals of ZrO 2 in the sintered material resulting in a contribution of a high toughness of the sintered material. The ratio of the cubic and tetragonal crystals is not limited. The content of the partially stabilized ZrO 2 is from about 3 to 10 wt%; when it is less than about 3 wt%, the toughness of the silicon nitride sintered material improves little, and when it is more than about l0 wt%, the strength and hardness of the silicon nitride sintered material decreases to a great extent. Further, the addition of aluminum oxide and yttrium oxide is necessary for the improvement of the sintering property and the compactibility and high strengthening of the silicon nitride powder, which is difficult to be sintered by itself. If less than about 1 wt% of Aℓ 2 O 3 or Y 2 O 3 is used, an insufficient compactability of the sintered material results, and using more than about 5 wt% of Aℓ 2 O 3 or more than about l0 wt% of Y 2 O 3 remarkably decreases the strength and hardness of the sintered material, especially at an elevated temperature. In a preferred embodiment according to the process of this invention, since not only an ordinary α-phase crystal but also at least about 40% of β-phase crystals of Si 3 N 4 powder are used as a starting silicon nitride powder, a remarkable phase change from α-phase to β-phase crystal and growth of crystal particles are minimized upon sintering. Therefore, the resulting silicon nitride sintered material has a high density and strength as well as high hardness and improved wear resistance. To attain such effects, it is preferred to use a Si 3 N 4 powder containing at least about 40% of a β-phase crystal. In order to obtain a sintered material having uniform fine particulate texture, the starting Si 3 N 4 powder is preferably fine and has a narrow particle size distribution. The starting Si 3 N 4 preferably has a mean particle size of about 0.5 µm o r less, more preferably from about 0.l to 0.3 µm. The toughness of the silicon nitride sintered material is remarkably improved by using a hot isostatic press (HIP) under a pressure from about l0 to 2,000 atm in an atmosphere of nitrogen, argon or a mixed gas thereof after the sintering step. The silicon nitride sintered material according to this invention, as mentioned above, containing from about l to 5 wt% of Aℓ 2 O 3 and from about l to l0 wt% of Y 2 O 3 as sintering assistants, can be produced as a sintered material having a sufficiently high density and high strength not only by pressure sintering such as by using a hot press, but also by normal pressure sintering. This is advantageous in the cost of mass production of many kinds of products such as cutting tools. Further, in the silicon nitride sintered material for cutting tools according to a preferred embodiment of this invention, the most amount of Si 3 N 4 is in a compact a-phase phase, and the partially stabilized ZrO 2 is dispersed in the β-phase Si 3 N 4 matrix, to obtain a sintered material having high density and high strength, and at the same time, having especially high hardness, excellent wear resistance, and extremely high toughness. When the silicon nitride sintered material according to this invention is used to produce cutting tools, the cutting tools obtained have far longer life than those of conventional sintered materials, without damaging and chipping of the edges during fraise processing or wet cutting processing with a violent heat cycle. The silicon nitride sintered material accoriding to this invention may further contain, e.g., a nitride, oxide, oxynitride, carbide, or boride of IVA, VA, or VIA Group metal of Periodic Table; and SiC, SiC whisker, and Si 3 N 4 whisker. The silicon nitride sintered material according to this invention can also be produced by a conventional hot press method. This invention is explained hereinafter in greater detail by reference to the following examples, which are not to be construed as limiting the scope of the present invention. Unless otherwise indicated, all parts, percents, and ratios are by weight. Example l The silicon nitride sintered material according to this invention (silicon nitride containing 3 wt% of partially stabilized zirconium oxide, 3 wt% of aluminum oxide, and 3 wt% of yttrium oxide) and β'-Sialon sintered material (z = 5, a typical example of conventional silicon nitride materials) were prepared by a hot press method in a graphite mold under the condition as follows. Temperature: 1,800°C Time: 2 hours Pressure: 150 kg/cm 2 Atmosphere: N 2 1.5 atm The samples obtained were measured for bending strength according to JIS R1601 (the term "JIS" used herein refers to "Japanese Industrial Standard") and stress intensity factor K IC according to B.R. Law et al, J. Am. Ceram. Soc. , vol. 63 (1980), pp 557. The results obtained are shown in Table 1. Sample Bending Strength (MPa) K IC (MPa√m) This invention 1,100 7.0 β-'Sialon 750 5.6 From the results shown in Table 1, it is apparent that the silicon nitride sintered material according to this invention is particularly improved in bending strength and stress intensity factor K IC . EXAMPLE 2 A commercial α-Si 3 N 4 powder (mean particle size: 0.8 µm), a partially stablized ZrO 2 powder containing 3 mol% of Y 2 O 3 (mean particle size: l µm), an Aℓ 2 O 3 powder (mean particle size: 0.5 µm), and a Y 2 O 3 powder (mean particle size: 0.5 µm) were blended in the ratio as shown in Table 2, ground and mixed in a ball mill, and then hydrauric press-molded at l.5 ton/cm 2 . The molding was sintered in an atmosphere of nitrogen gas at l,750°C for 2 hours under normal pressure and then HIP-treated in an atmosphe re of nitrogen gas at l,800°C under a pressure of l,000 atm. The resulting sintered material was cut to form throw away chips of l2.7 × l2.7 × 4.76 mm according to JIS SNG 433. A cutting test was carried out with the chips under the following conditions and the results are shown in Table 2. Work: FC 25, (Gray cast iron, H B =230) 150 mm wide × 300 mm long Machine: Vertical-Type Fraise machine Cutter: DNF 4080 R (made by Sumitomo Electric Industries, Ltd.) one blade-cutting Cutting conditions: Cutting speed 400m/min Cutting depth 2mm Feed 0.2mm/edge Edge treatment 0.15mm, -25° Life rating: Worn width of edge relief surface, 0.3 mm No. Composition (wt%) Life (min) Si 3 N 4 ZrO 2 Aℓ 2 O 3 Y 2 O 3 1 89 5 3 3 30 2 79 15 3 3 9 3 94 5 0.5 0.5 broken after 5 min 4 77 5 3 15 5 5 77 5 15 3 7 6 Sintered material of commercial Aℓ 2 O 3 matrix broken after 5 min 7 Commercial super hard coating material 5 Note: Nos. 2 to 7 are the comparative samples. As seen from Table 2, the silicon nitride sintered material according to this invention has excellent in the life and damage resistance when it is used as a cutting tool. Example 3 A commercial α-Si 3 N 4 powder (mean particle size: 0.8 µm), a partially stabilized ZrO 2 powder containing 3 mol% of Y 2 O 3 (mean particle size: l µm), an Aℓ 2 O 3 powder (mean particle size: 0.5 µm), and a Y 2 O 3 powder (mean particle size: 0.5 µm) were blended in the ratio shown in Table 3, ground and mixed in a ball mill, CIP-molded (cold isostatic press-molded) under a pressure of l50 MPa, and sintered under the same conditions as in Example 2. No. Composition (wt%) Si 3 N 4 ZrO 2 Aℓ 2 O 3 Y 2 O 3 8 89 5 3 3 9 74 20 3 3 10 72 15 3 10 11 72 15 10 3 12 93 5 1 1 13 75 5 10 10 14 85 5 5 5 15 94 0 3 3 Note: Nos. 9 to 11, 13, and 15 are the comparative samples. Break test pieces of 3 × 3 × 40 mm according to JIS Rl60l were formed by cutting the resulting sintered materials, which were polished and measured for the relative density (%), hardness (Hv), and high temperature hardness at l,200°C (Hv). The test results and the life (min) in the same cutting test as in Example 2 are shown in Table 4. No. Density (%) Hardness (Hv) High temperature hardness (Hv) Life (min) 8 99 1,750 1,100 30 9 95 1,560 1,000 8 10 98 1,690 920 5 11 98 1,700 800 5 12 98 1,720 1,050 18 13 98 1,700 750 3 14 99 1,740 980 7 15 - 1,700 950 3 Note: Nos. 9 to 11, 13, and 15 are comparative samples. As seen from Table 4, the silicon nitride sintered material according to this invention has excellent in hardness, high temperature hardness, and life. Example 4 A commercial α-Si 3 N 4 powder (mean particle size: 0.8 µm) was subjected to the heat treatment in an atmosphere of N 2 gas at l,800°C for 3 hours under a pressure of 9 atm. It was found that the resulting Si 3 N 4 powder contained 60% of β-Si 3 N 4 by means of X-ray diffraction. The resulting Si 3 N 4 powder was blended with a ZrO 2 powder partially stablized with 3 mol% of Y 2 O 3 - (mean particle size: l µm), an Aℓ 2 O 3 powder (mean particle size: 0.5 µm), and a Y 2 O 3 powder (mean particle size: 0.5 µm) in the ratios shown in Table 5, ground and mixed in a ball mill, and press-molded. The molding was sintered in an atmosphere of N 2 gas at l,750°C for 2 hours under normal pressure and then HIP-treated in an atmosphere of N 2 gas at l,800°C under a pressure of l,000 atm. The resulting sintered material was cut to form throw away chips of l2.7 × l2.7 × 4.76 mm according to JIS SNG 433. The cutting test was carried out with the chips under the following conditions, and the results are shown in Table 5. m Work: FC 25, 150 mm wide × 300 mm long Cutter: DNF 4080 R (made by Sumitomo Electric Industries, Ltd.) one blade-cutting Machine: Vertical-Type Fraise machine Cutting conditions: Cutting speed 400m/min Cutting depth 3mm Feed 0.3mm/edge Edge treatment 0.20mm, -25° Life rating: worn width of edge relief surface, 0.3 mm No. Composition (wt%) Life (min) Si 3 N 4 ZrO 2 Aℓ 2 O 3 Y 2 O 3 16 89 5 3 3 25 17 79 15 3 3 7 18 94 5 0.5 0.5 broken after 3 min 19 77 5 3 15 4 20 77 5 15 3 6 21 Sintered material of commercial Aℓ 2 O 3 matrix broken after 0.3 min 22 Commercial super hard coating material 4 Note: Nos. 17 to 22 are the comparative samples. As seen from Table 5, the silicon nitride sintered material according to this invention is excellent, especially in life and damage resistance. Example 5 A commercial α-Si 3 N 4 powder (mean particle size: 0.8 µm) was hea t-treated in an atmosphere of N 2 gas under 5 atm at l,650 to l,800°C for 0.5 to 3 hours. The content of β-phase crystal (β/α ratio) of the resulting Si 3 N 4 powder was determined by means of X-ray diffraction, and the results are shown in Table 6. Samples were prepared by blending 86 wt% of Si 3 N 4 powder having different contents of β-phase crystals with 8 wt% of ZrO 2 powder partially stabilized with 3 mol% of Y 2 O 3 (mean particle size: l µm), 3 wt% of Aℓ 2 O 3 powder (mean particle size: 0.5 µm), and 3 wt% of Y 2 O 3 powder (mean particle size: 0.5 µm), and sintered in the same manner as in Example 2. Throw away chips according to JIS SNG 433 were formed from the resulting sintered materials, and the cutting test was carried out under the following conditions. The results are shown in Table 6. Work: FC 25 200 mm diameter × 300 mm long Machine: NC Type lathe Cutting conditions: Cutting speed 600 m/min Cutting depth 2 mm Feed 0.36 mm/rev. Life rating: V B = 0.3 mm No. β/α of Si 3 N 4 Life (min) 23 50/50 11 24 70/30 13 25 90/10 15 26 10/90 8 As seen from Table 6, the silicon nitride sintered material according to this invention, in which a silicon nitride containing at least 40% of β-phase crystals is used, is excellent especially in life and damage resistance. Example 6 Si 3 N 4 powder obtained in the same manner as in Example 5 and each having a different content of β-phase crystals was blended with a ZrO 2 powder partially stablized with 3 mol% of Y 2 O 3 (mean particle size: l µm), an Aℓ 2 O 3 powder (mean particle size: 0.5 µm), and a Y 2 O 3 powder (mean particle size: 0.5 µm) in the ratios shown in Table 7 (the mixing ratios of Nos. 23 to 26 are the same as that in Example 5), HIP-molded under l50 MPa and sintered in the same manner as in Example 4. No. Composition (wt%) Si 3 N 4 (β/α ratio) ZrO 2 Aℓ 2 O 3 Y 2 O 3 23 86 (50/50) 8 3 3 24 86 (70/30) 8 3 3 25 86 (90/10) 8 3 3 26 86 (10/90) 8 3 3 27 79 (70/30) 15 3 3 28 91 (70/30) 8 0.5 0.5 29 79 (70/30) 8 3 10 30 79 (70/30) 8 10 3 Note: Nos. 27, 28, and 30 are comparative samples. Test pieces were cut from the resulting sintered materials and evaluated. The test results for relative density (%), room temperature hardness (Hv), and high temperature hardness at l,200°C (Hv) are shown in Table 8. No. Density (%) Room temperature hardness (Hv) High temperature hardness (Hv) 23 99 1,700 920 24 99 1,730 940 25 99 1,780 950 26 98 1,620 870 27 95 1,590 870 28 93 1,530 820 29 97 1,620 760 30 98 1,630 780 Note: Nos. 27, 28 and 30 are comparative samples. As seen from Table 8, the silicon nitride sintered material according to this invention, in which a silicon nitride powder containing at least 40% of β-phase crystal is used, is excellent especially in the hardness. According to this invention, it is possible to provide a silicon nitride sintered material for cutting tools, which has an extremely high hardness and a high toughness, in addition to the inherent high strength and heat stability of the silicon nitride sintered material. The silicon nitride sintered material for cutting tools according to this invention is excellent in wear resistance and damage resistance and has far longer life than conventional ceramic tools of alumina matrix, even under cutting condition of a violent heat cycle.

Claims: A silicon nitride sintered material for cutting tools obtained by the steps of: (a) mixing from 3 to 10 wt% of partially stabilized zirconium oxide powder, from 1 to 5 wt% of aluminum oxide powder, from 1 to 10 wt% of yttrium oxide powder, and the balance of silicon nitride powder, and (b) sintering the resulting mixed powder in a non-oxidative gas atmosphere at about 1,600 to 1,900°C. A silicon nitride sintered material according to claim 1, wherein said powder mixture has been hot isostatically pressed in an atmosphere of nitrogen, argon, or a combination thereof at a pressure of about 10 to 2,000 atm. A silicon nitride sintered material according to claim 1, wherein said silicon nitride powder contains at least about 40% of β-phase crystals. A silicon nitride sintered material according to claim 1, wherein said partially stabilized zirconium oxide powder is partially stabilized with an oxide of yttrium, calcium, or magnesium. A silicon nitride sintered material according to claim 4, wherein said partially stabilized zirconium oxide powder is partially stabilized with yttrium oxide. A silicon nitride sintered material according to claim 1, wherein the mean particle size of said silicon nitride powder is less than about 0.5 µm. A silicon nitride sintered material according to claim 1, wherein said material comprises cubic and tetragonal crystals of partially stabilized zirconium oxide in a silicon nitride matrix. A process for making a silicon nitride sintered material for cutting tools comprising the method steps as defined in one of claims 1-7.

Inventors: MIYAKE MASAYA, NISHIOKA TAKAO, YAMAKAWA AKIRA, MIYAKE, MASAYA, NISHIOKA, TAKAO, YAMAKAWA, AKIRA, MIYAKE, MASAYA ITAMI WORKS OF SUMITOMO, NISHIOKA, TAKAO ITAMI WORKS OF SUMITOMO, YAMAKAWA, AKIRA ITAMI WORKS OF SUMITOMO
Applicants: SUMITOMO ELECTRIC INDUSTRIES, SUMITOMO ELECTRIC INDUSTRIES LIMITED
Application year: 1987
Main classification: C04B35
IPC codes: C04B35