Catalyst for purifying exhaust gas and method for its production

Abstract: A catalyst for purifying exhaust gas comprises a honeycomb carrier of monolithic structure and a coating layer deposited on the honeycomb carrier and formed with a catalyst composition containing a refractory inorganic oxide in the form of particles possessing an average particle diameter in the range of 0.5 to 20 microns, which refractory inorganic oxide has platinum and/or palladium and rhodium deposited thereon in high concentrations. This catalyst is produced by coating the honeycomb carrier with an aqueous slurry containing the catalyst composition and calcining the coated carrier.

Description: This invention relates to a catalyst for purifying exhaust gas. More particularly, it relates to a catalyst for purifying the exhaust gas from the internal combustion engine such as of an automobile for simultaneous removal from the exhaust gas of noxious components such as hydrocarbon (HC), carbon monoxide (CO), and nitrogen oxides (NOx), which catalyst especially exhibits outstanding durability even when it is used under harsh conditions such as under a high-temperature oxidative atmosphere and manifests a high purifying ability to the aforementioned noxious components at low temperatures. In conventional noble metal-containing catalysts for purifying the exhaust gas, for the purpose of ensuring effective use of the noble metal contained in a very minute amount in the catalyst, efforts have been made to allow the noble metal to be deposited in as high a degree of dispersion as possible on a refractory inorganic oxide of a large surface area such as activated alumina. The catalyst having the noble metal carried in a high degree of dispersion enjoys a high initial activity. When it is exposed to such harsh conditions as involved under a high-temperature oxidative atmosphere, however, the noble metal gains gradually in particle size, undergoes a chemical conversion into a less active state, and tends to induce a reaction with the carrier substance and cerium oxide. Because the noble metal is deposited in the high degree of dispersion, there tends to ensue a disadvantage that the degradation of catalytic activity is rather heavy. In this field, zirconia is used more often than not as incorporated chiefly in a carrier substrate for the purpose of stabilizing the physical properties of the catalyst such as specific surface area. To cite a case using zirconia as a carrier substrate for a noble metal, Japanese Patent Publication SHO 57(1982)-29,215 and Japanese Patent Laid-Open SHO57(1982)-153,737 disclose a method which comprises forming on a carrier a coating layer containing alumina and zirconia and subsequently depositing a noble metal thereon. The catalyst produced by the method of this principle, however, suffers from the degradation of catalytic activity due to the same cause as mentioned above because the greater part of the noble metal is substantially dispersed in a high ratio in the alumina. As carrier substances incapable of interacting noble metals, particularly rhodium, zirconia (U.S.P. No. 4,233,189) and alpha alumina (U.S.P. No. 4,172,047) have been known in the art. Zirconia and alpha alumina generally possess small surface areas. It has been pointed out, however, that the catalysts having rhodium carried on these substances have a disadvantage that exhibit poor initial activity and possess no satisfactorily high ability to purify the exhaust gas at low temperatures after long term using. An object of this invention, therefore, is to provide a novel catalyst for purifying the exhaust gas and a method for the production thereof. Another object of this invention is to provide a catalyst for purifying the exhaust gas which may exhibit outstanding durability even when it is used under harsh conditions and possesses a notable ability to purify thoroughly the exhaust gas of the noxious components thereof even at low temperatures and a method for the production thereof. The objects of the invention described above are accomplished by a catalyst for purifying exhaust gas comprising a honeycomb carrier of monolithic structure and a coating layer applied on the honeycomb carrier and formed with a catalyst composition comprising: A catalyst for purifying exhaust gas comprising a honeycomb carrier of monolithic structure and a coating layer applied on the honeycomb carrier and formed with a catalyst composition comprising: zirconia, a platinum group metal, a refractory inorganic oxide, and a rare earth metal oxide; characterised in that the platinum group metal is deposited on zirconia powder to produce a zirconia-supported platinum group metal; the platinum group metal comprises at least one member selected from (a) rhodium, (b) a combination of rhodium and platinum, (c) a combination of rhodium and palladium and (d) a combination of rhodium, platinum and palladium, the platinum group metal is present on the zirconia powder in a proportion in the range of 0.5 to 30% by weight based on the zirconia powder; and the refractory inorganic oxide is present in the range of 1 to 20g deposited per litre of the carrier. A convenient method for the production of such a catalyst comprises coating a honeycomb carrier of monolithic structure with an aqueous slurry containing the zirconia-supported platinum group metal, the refractory inorganic oxide, and the rare earth metal oxide, and calcining the resultant coated carrier. We have found, as a result of a diligent study, that directly contrary to the conventional theory that the noble metal which must be used in a very minute amount ought to be deposited in a small ratio on the refractory inorganic oxide of a large surface area so as to heighten the degree of dispersion of the noble metal to the highest possible extent, a noble metal-containing refractory inorganic oxide produced by depositing the noble metal in a high ratio on a small amount of refractory inorganic oxide gives rise to a catalyst of surprisingly high durability. The present invention has been made as the result. Preferred embodiments of the invention will now be described. A catalyst composition in accordance with this invention comprises a zirconia having deposited thereon a platinum group preferably rhodium or rhodium-containing, a refractory inorganic oxide, and a rare earth metal oxide. The zirconia to be used in this invention may possess a specific surface area exceeding 10 m²/g, preferably falling in the range of 60 to 100 m²/g. The primary particles of this zirconia possess an average particle diameter of not more than 2,000 Å, preferably not more than 500 Å. A commercially available zirconia may be used on condition that it satisfies these requirements. Otherwise the zirconia may be prepared, for example, by a method which comprises neutralizing an aqueous solution of zirconium salt as with ammonia, washing the product of neutralization, drying and calcining the washed product. The amount of the zirconia to be used generally is in the range of 0.5 to 50% by weight, based on the amount of the catalyst composition. Even when it is used in an amount falling in the range of 0.5 to 10% by weight, so produced catalyst compositions are capable of fully manifesting the effect contemplated by the invention. If the amount of the zirconia exceeds 50% by weight, the individual particles of zirconia may gain in growth of particle diameter at an accelerated rate possibly to impair the catalytic activity of the composition. The platinum group metal deposited on the zirconia may be or incorporate rhodium. Further incorporation of platinum or palladium is observed to bring about an improvement further in the low-temperature activity of the catalyst after long term use at elevated temperatures. The total amount of platinum and palladium to be incorporated in addition to rhodium desirably falls in the range of 1/5 to 5 in gravimetric ratio, based on the amount of rhodium. The noble metal-carrying zirconia may contain such noble metals in a total concentration falling in the range of 0.5 to 30% by weight, preferably 1 to 20% by weight. The platinum group metal except for rhodium is not required to be wholly deposited on the zirconia. It may be deposited on a refractory inorganic oxide such as alumina or on a rare earth metal oxide. The deposition of the noble metal on the zirconia may be effected by any of the conventional methods and need not be carried out by any specific method. Rhodium chloride, rhodium nitrate, and rhodium sulfate can be used as rhodium sources and platinic chloride, dinitrodiammine platinum, palladium chloride, and palladium nitrate as platinum or paladium sources, all in the form of an aqueous solution or an alcoholic solution. Where two or more platinum group metals are to be deposited on the zirconia, this deposition may be effected by impregnating the metals either separately or collectively in the solution. Then, by drying and calcining the impregnated zirconia, the noble metals are deposited fast on the zirconia. Examples of suitable refractory inorganic oxides include alumina, silica, titania, magnesia, and zirconia. It is desirable to use alumina, particularly activated alumina among other refractory inorganic oxides cited above. This alumina may be used in any of possible crystalline forms such as γ, δ , ϑ , α , ζ , κ , and η . Though the refractory inorganic oxide may be directly incorporated in the unmodified form in the catalyst composition, it is enabled to contribute to further enhancing the catalyst composition's purifying ability by incorporating therein rare earth metals and such base metal elements as chromium, manganese, iron, cobalt, nickel, and zirconium in the form of oxides in a total amount falling in the range of 0.1 to 30% by weight, preferably 2 to 20% by weight, based on the amount of the refractory inorganic oxide such as, for example, alumina. As examples of the rare earth metal oxide, there can be cited the oxides of cerium, lanthanum, and neodymium. It is particularly desirable to use cerium oxide among other rare earth metal oxides enumerated above. The rare earth metal oxide can be deposited in an amount falling in the range of 0.1 to 30% by weight, preferably 2 to 20% by weight, on the refractory inorganic oxide such as alumina as mentioned above. Otherwise, it can be incorporated directly in the catalyst composition in the form of oxide, carbonate or hydroxide, which may be converted into a corresponding oxide by calcing or in use. In the latter case of incorporation, the oxide can be incorporated in an amount falling in the range of 5 to 80% by weight, preferably 10 to 50 % by weight, in the catalyst composition. Since the platinum group metal, particularly the platinum group metal containing rhodium, may be stably deposited on the zirconia in the form of microfine particles possessing a very large surface area, the possible adverse effects arising from the interaction among the carrier substance, the rare earth metal oxide, and the base metal oxide can be curbed and the catalyst composition is enabled to incorporate therein the rare earth metal oxide and the base metal oxide in larger amounts than heretofore permitted and, as the result, the catalyst composition is allowed to possess notably improved durability and purifying ability. The zirconia having deposited therein the platinum group metal, particularly the platinum group metal containing rhodium, the rare earth group oxide, and the refractory inorganic oxide which have been obtained as described above are preferably ground and stirred as in a ball mill to produce an aqueous slurry. A finished catalyst may then be produced by coating a honeycomb carrier of monolithic structure with the aqueous slurry, and optionally calcining the dried carrier. This calcining can be performed at a temperature in the range of 100°C to 600°C, preferably 130°C to 300°C for a period in the range of 1 to 10 hours, preferably 1 to 3 hours. Attention is drawn to the present Applicants' Application No. EP-A-558159 which is divided from the present application and is generally directed to a catalyst for purifying exhaust gas comprising a honeycomb carrier of monolithic structure and a coating layer applied on the honeycomb carrier formed by a catalyst composition consisting of cerium oxide free of any noble metal deposited thereon, a first refractory inorganic oxide free of any noble metal deposited thereon, and a second refractory inorganic oxide, characterised in that the second refractory, inorganic oxide comprises: a refractory inorganic oxide having deposited thereon 5 to 30% by weight of a noble metal comprising platinum and/or palladium, and/or a refractory inorganic oxide having 1 to 20% by weight of rhodium deposited thereon; or a refractory inorganic oxide having deposited thereon 5 to 30% by weight of a noble metal comprising platinum and/or palladium, and 1 to 20% by weight of rhodium, the second refractory inorganic oxide being in the form of particles possessing an average particle diameter in the range of 0.5 to 20 microns and being dispersed in the coating layer, the second refractory inorganic oxide being present in the range of 1 to 20g deposited per litre of carrier. The honeycomb carrier of monolithic structure to be used in the present invention can be any of honeycomb carriers referred to by the generic term "ceramic honeycomb carrier." The honeycomb carriers formed with such materials as cordierite, mullite, -alumina, zirconia, titania, titanium phosphate, aluminium titanate, petalite, spodumene, alumino silicate, and magnesium silicate prove to be particularly desirable. Those made of cordieritic susbtance are used particularly adavantageously in the catalyst for use in the internal combustion engine among other materials enumerated above. Honeycomb carrier formed in monolithic structure with a metal such as stainless steel or Fe-Cr-Al alloy which is resistant to oxidation and to heat can be used too. The monolithic carrier of the preceding description can be produced, for example, by the extrusion molding method or the method of tightly rolling a sheetlike element. The openings (cells) formed in the monolithic honeycomb carrier for passage of the gas under treatment may be in a hexagonal, tetragonal, trigonal, or corrugated shape. The honeycomb carrier functions very satisfactorily when the cell density (number of cells per unit cross sectional area) is in the range of 150 to 600 cells/square inch (23 to 93 cells per cm²). Now, the present invention will be described more specifically with reference to working examples. Needless to mention, this invention is not limited only to these working examples. Example 1 A 10.0-g portion of zirconia possessing a specific surface area of 70 m²/g and an average particle diameter of 200 Å (produced by Daiichi Kigenso Kagaku K.K.) was impregnated with an aqueous rhodium chloride solution containing 0.3 g of rhodium and the impregnated zirconia was dried at 120°C for 12 hours. Then, the dried zirconia was calcined in the air at 500°C for 1 hour, to produce zirconia powder containing 2.9% by weight of rhodium. Then, 150 g of activated alumina possessing a specific surface area of 150 m²/g was impregnated with an aqueous platinic chloride solution containing 1.5 g of platinum. The impregnated activated alumina was dried at 150°C for 12 hours and then calcined in the air at 500°C for 1 hour, to afford a platinum-containing alumina powder. In a ball mill, the two powders obtained as described above and 75 g of commercially available cerium oxide powder were wet pulverized for 20 hours, to prepare an aqueous slurry. Monolithic carrier pieces of cordierite 33 mm in outside diameter and 76 mm in length containing about 400 gas flow cells per square inch of cross-sectional area were immersed in the aforementioned slurry, removed from the slurry, then blown with compressed air to remove excess slurry from inside the cells, and dried at 140°C for 3 hours, to produce a catalyst A. This catalyst A, on analysis by the fluorescent X-ray, was found to contain 0.056 g of platinum and 0.011 g of rhodium per catalyst piece. Example 2 A zirconia powder containing 1.8% by weight of rhodium and 8.9% by weight of platinum was prepred by impregnating 15.0 g of the same zirconia powder as used in Example 1 in a mixture of an aqueous rhodium chloride solution containing 0.3 g of rhodium with an aqueous platinic chloride solution containing 1.5 g of plainum, drying the product of impregnation at 120°C for 12 hours, and then calcining the dried powder in the air at 500°C for 1 hour. In a ball mill, the zirconia powder and 145 g of the same activated alumina as used in Example 1 and 75 g of cerium oxide were wet pulverized for 20 hours, to produce an aqueous slurry. A catalyst B was obtained by following the procedure of Example 1 using this aqueous slurry. The catalyst B was found to contain 0.052 g of platinum and 0.010 g of rhodium per catalyst piece. Example 3 A catalyst C was obtained by following the procedure of Example 2, excepting a powder (iron-containing activated alumina) produced by impregnating 140 g of activated alumina with a solution of 25.3 g of ferric nitrate in 100 g of purified water and drying and calcining the product of impregnation was used in the place of the activated alumina of Example 2. The catalyst C was found to contain 0.054 g of platinum and 0.011 g of rhodium per catalyst piece. Control 1 An aqueous slurry was prepared by wet pulverizing 160 g of the same activated alumina and 75 g of the same cerium oxide as used in Example 1 in a ball mill for 20 hours. Then, by following the procedure of Example 1, monolithic carrier pieces of cordierite were wash coated with the aqueous slurry, dried at 140°C for 3 hours, and then calcined in the air at 500°C for 1 hour. The monolithic carrier pieces so treated were immersed in a mixed aqueous solution of platinic chloride and rhodium chloride, dried and calcined in the air at 400°C for 1 hours, to produce a catalyst I. This catalyst I was found to contain 0.055 g of platinum and 0.011 g of rhodium per carrier piece. Control 2 An aqueous slurry was prepared by wet pulverizing 120 g of the same activated alumina as used in Example 1 and 120 g of a commercially available zirconia powder in a ball mill for 20 hours. Then, by following the procedure of Example 1, monolithic carrier pieces of cordierite were wash coated with the aqueous slurry, dried at 140°C for 3 hours, and calcined in the air at 500°C for 1 hour. The monolithic carrier pieces so treated were immersed in a mixed aqueous solution of platinic chloride and rhodium chloride, dried, and calcined in the air at 400°C for 1 hour, to produce as catalyst II. This catalyst II was found to contain 0.056 g of platinum and 0.011 g of rhodium per carrier piece. Example 4 A zirconia powder containing 2.3% by weight of rhodium and 20.3% by weight of palladium was prepared by immersing 12.0 g of zirconia possessing a specific surface area of 90 m²/g and an average particle diameter of 150 Å (produced by Daiichi Kigenso Kagaku K.K.) in a mixture of an aqueous rhodium nitrate solution containing 0.35g of rhodium with an aqueous palladium nitrate solution containing 3.15 g of palladium, drying the product of immersion at 120°C for 12 hours, and then calcining the dried immersion product in the air at 500°C for 1 hour. An alumina powder containing CeO₂ and Fe₂O₃ was obtained by dissolving 56.1g of cerium nitrate and 32.2 g of ferric nitrate in 200 g of purified water, mixing the resultant mixture with 200 g of an activated alumina possessing a specific surface area of 100 m²/g, drying the wet mixture at 120°C for 12 hours, and then calcining the dried mixture in the air at 700°C for 1 hour. An aqueous slurry was prepared by wet pulverizing the two powders obtained as described above in a ball mill for 20 hours. By following the procedure of Example 1, monolithic carrier pieces of cordierite were wash coated with the aqueous slurry and dried at 140°C for 3 hours, to produce a catalyst D. This catalyst D was found to contain 0.120 g of palladium and 0.013 g of rhodium per carrier piece. Example 5 A zirconia powder containing 2.8% by weight of rhodium and 2.8% by weight of palladium was prepared by immersing 12.0 g of the same zirconia as used in Example 4 in a mixture of an aqueous rhodium nitrate solution containing 0.35 g of rhodium with an aqueous palladium nitrate solution containing 0.35 g of palladium, drying the product of immersion at 120°C for 12 hours, and then calcining the dried product in the air at 500°C for 1 hour. Then, an aqueous solution of 56.1 g of cerium nitrate and 32.2 g of ferric nitrate in 200 g of purified water and an aqueous palladium nitrate solution containing 2.8 g of palladium were mixed. The resultant mixed solution was mixed with 200 g of an activated alumina possessing a specific surface area of 100 m²/g, dried at 120°C for 12 hours, and then calcined in the air at 600°C for 1 hour. In a ball mill, the two powders obtained as described above were wet pulverized for 20 hours, to produce an aqueous slurry. Then, a catalyst E was obtained by following the procedure of Example 1 using the aqueous slurry. This catalyst E was found to contain 0.121 g of palladium and 0.013 g of rhodium per carrier piece. Example 6 An aqueous slurry was prepared by wet pluverizing a zirconia powder containing 2.3.% by weight of rhodium and 20.3% by weight of palladium prepared by following the procedure of Example 4, 150 g of an activated alumina possessing a specific surface area of 90 m²/g, and 80 g of cerium oxide in a ball mill for 20 hours. A catalyst F was obtained by following the procedure of Example 1 using the aqueous slurry. This catalyst F was found to contain 0.115 g of palladium and 0.012 g of rhodium per catalyst piece. Control 3 A solution of 56.1 g of cerium nitrate and 32.2 g of ferric nitrate in 200 g of purified water was mixed with 200 g of an activated alumina possessing a specific surface area of 100 m²/g, dried at 120°C for 12 hours, and then calcined in the air at 700°C for 1 hour. An aqueous slurry was prepared by wet pulverizing the powder obtained as described above in a ball mill for 20 hours. Then, by following the procedure of Example 1, monolithic carrier pieces of cordierite were wash coated with the aqueous slurry, dried at 140°C for 3 hours, and calcined in the air at 500°C for 1 hour. A catalyst III was obtained by immersing the monolithic carrier pieces so treated in a mixed aqueous solution of palladium chloride and rhodium chloride, drying the product of immersion, and then calcining the dry product in the air at 400°C for 1 hour. This catalyst III was found to contain 0.123 g of palladium and 0.013 g of rhodium per carrier piece. Control 4 A powder possessing a specific surface area of 5 m²/g and an average particle diameter of 5,000 Å was obtained by calcining a commerically available zirconia at 1,000°C for 10 hours. A catalyst IV was obtained by following the procedure of Example 4, excepting the zirconia mentioned above was instead. The catalyst IV was found to contain 0.120 g of palladium and 0.013 g of rhodium per carrier piece. Example 7 The catalysts of Examples 1 through 3 and the catalysts of Controls 1 and 2 were tested for catalytic property during initial use and after aging in an electric furnace. The aging in the electric furnace was carried out in a high-temperature oxidative atmosphere of air involving very harsh conditions of 900°C and 20 hours. The evaluation of catalytic property was performed with an electronically controlled engine (4 cylinders 1,800 cc), with the gas temperature at the inlet to a catalyst bed continuously varied from 200°C to 450°C with a heat-exchanger to determine purifying ratios of CO, HC, and NOx. During this evaluation, the engine was operated as vibrated at a rate of 1 Hz, with the space velocity of gas (S.V.) fixed at 90,000 hr⁻¹ and the average air combustion ratio, A/F, at 14.6 ± 0.5. The inlet gas temperatures (T₅₀) at which the purifying ratios of CO, HC, and Nox reached 50% were as shown in Table 1. The catalyst of Examples 1 through 3 and the catalysts of Controls 1 and 2 were also tested for catalytic property after test run of engine. This test was carried out with an electronically controlled engine (8 cylinder 4,400 cc). With this motor operated in a mode of alternating 60 seconds' steady operation and 6 seconds' decelerated operation (during which period the fuel supply was cut and the catalyst was exposed to a high-temperature oxidative atmosphere) to effect 50 hours' aging of the catalyst under conditions such that the catalyst temperature would reach 850°C in the steady operation. The evaluation of the catalyst property after the test run of engine was carried out by the same procedure as described above. The results are shown in Table 2. Then the catalyst of Examples 4 through 6 and the catalysts of Controls 3 and 4 were tested for catalytic property during initial use and after 50 hours' test run of engine. An electronically controlled engine (6 cylinders 2,400 cc) was used for the test run of engine mentioned above. The endurance test of engine was performed in a mode of alternating 30 seconds' exposure to an oxygen-lean atmosphere and as long exposure to an oxygen-rich atmosphere, introducing secondary air thereby varying the air combustion ratio A/F, between 14.5 and 17.5. During the test, the catalyst temperature reached the maximum of 950°C. The evaluation of catalytic property was performed with the same engine as used for the endurance test under the conditions of A/F = 14.6 and SV = approximately 140,000 hr⁻¹, to determined the purifying ratios of HC, CO and NO. In the test during the initial use, the evalution was made at an inlet temperature of 500°C. In the test after the engine endurance test, the evalution was made at two inlet temperatures of 500°C and 700°C. The results are shown in Tables 3 and 4. It is clearly noted from the results that the catalysts of Examples 1 through 3 and the catalysts of Examples 4 through 6 having noble metals deposited on zirconia of large surface area and minute particle diameter possessed highly desirable initial properties and exhibited very high durability even after harsh endurance conditions as in a high-temperature oxidative atmosphere. Initial activity After aging in electric furnace 50% conversion temperature (°C) 50% conversion temperature CO HC NOx CO HC NOx Example 1 Catalyst A 265 268 264 391 398 390 2 B 254 259 255 379 383 380 3 C 254 256 249 371 375 367 Control 1 I 260 264 258 436 443 433 2 II 258 262 254 415 423 412 After aging by engine 50% conversion temperature (°C) Purifying ratio at 450°C (%) CO HC NOx CO HC NOx Example 1 Catalyst A 359 365 355 95 93 93 2 B 341 347 337 97 95 94 3 C 340 345 333 97 96 95 Control 1 I 389 397 388 85 88 88 2 II 395 402 391 79 83 85 Initial activity Purifying ratio at 500°C (%) CO HC NOx Example 4 Catalyst D 95 95 93 5 E 96 97 94 6 F 97 98 97 Control 3 III 96 97 94 4 IV 88 90 87 After aging by engine Purifying ratio at 500°C (%) Purifying ratio at 700°C (%) CO HC NO CO HC NO Example 4 Catalyst D 76 85 74 88 93 87 5 E 82 88 78 91 94 89 6 F 80 88 77 92 95 88 Control 3 III 62 71 59 75 82 73 4 IV 61 73 56 81 86 79 From the results given above, it is clear that the catalysts of the present invention incur only slight deterioration and possess outstanding durability under ordinary operating conditions of engine and even under harsh conditions as under a high-temperature oxidative atmosphere.

Claims: A catalyst for purifying exhaust gas comprising a honeycomb carrier of monolithic structure and a coating layer applied on the honeycomb carrier and formed with a catalyst composition comprising: zirconia, a platinum group metal, a refractory inorganic oxide, and a rare earth metal oxide; characterised in that the platinum group metal is deposited on zirconia powder to produce a zirconia-supported platinum group metal; the platinum group metal comprises at least one member selected from (a) rhodium, (b) a combination of rhodium and platinum, (c) a combination of rhodium and palladium and (d) a combination of rhodium, platinum and palladium, the platinum group metal is present on the zirconia powder in a proportion in the range of 0.5 to 30% by weight based on the zirconia powder; and the refractory inorganic oxide is present in the range of 1 to 20g deposited per litre of the carrier. A catalyst as claimed in Claim 1, characterised in that the refractory inorganic oxide is activated alumina. A catalyst as claimed in Claim 1 or Claim 2, characterised in that the refractory inorganic oxide contains one member selected from the oxides of cerium, lanthanum, and neodymium in proportion in the range of 0.1 to 30% by weight based on the refractory inorganic oxide. A method for the production of a catalyst as claimed in any preceding Claim, characterised by coating a honeycomb carrier of monolithic structure with an aqueous slurry containing the zirconia-supported platinum group metal, the refractory inorganic oxide, and the rare earth metal oxide, and calcining the resultant coated carrier.

Inventors: KITAGUCHI SHINYA, OHATA TOMOHISA, SHIRAISHI EIICHI, TSUCHITANI KAZUO, KITAGUCHI, SHINYA, OHATA, TOMOHISA, SHIRAISHI, EIICHI, TSUCHITANI, KAZUO
Applicants: NIPPON CATALYTIC CHEM IND, NIPPON SHOKUBAI CO., LTD.
Application year: 1987
Main classification: B01D53
IPC codes: B01J23, B01D53, B01J37, B01J35