Method for production of ceramic circuit board

Abstract: A method for producing a ceramic circuit board comprising the steps of (i) forming a conductor portion of the ceramic circuit board by printing a conductive paste composition on a ceramic base plate for the circuit board and then (ii) firing the ceramic base plate and the conductive paste composition together, wherein a copper-base composition comprising a copper powder and 0.5 to 5 parts by weight, based on 100 parts by weight of copper powder, of at least one organo metallic compound capable of forming an inorganic compound or compounds, respectively, when fired in an inert atmosphere, is used as the conductive paste composition. The combined use of isopropyl tridodecylbenzene sulfonyl titanate and isopropyl triisostearoyl titanate greatly improve the flowability of the copper-base conductive paste composition.

Description: The present invention relates to a method for producing a ceramic circuit board. Glass ceramic composite multilayer circuit boards having superior electrical characteristics can include a copper conductive layer, since the boards can be fired or baked at a relatively low temperature (e.g. 1000°C or less) to greatly improve the conductivity of the boards. However, known copper-base pastes used to form conductors have been developed mainly for use with alumina circuit boards and, therefore, have not been directly applied to multilayer glass-ceramic circuit boards. Nevertheless, the development of glass-ceramic circuit boards having good electrical characteristics is progressing and, therefore, there is a need to develop conductive copper paste compositions suitable for use in glass-ceramic composite circuit boards in the form of a green sheet before firing, having good printing properties, excellent adhesion properties and, furthermore, capable of entirely filling through holes in the boards. Various conductive paste compositions are known and used in the art. For example, paste compositions containing a conductor component of a noble metal such as gold, silver, and palladium dispersed in organic vehicles, paste compositions containing a conductor component of a high-melting point metal such as tungsten and molybdenum dispersed in organic vehicles, and paste compositions containing a conductor component of copper dispersed in organic vehicles. Of the above-mentioned conductive paste compositions, the conventional copper paste compositions which can be fired at a relatively low temperature generally contain copper powder, glass powder, and an organic vehicle. That is, generally 1% to 5% by weight, based on the weight of the copper powder (i.e. conductor component), of the glass powder is included, to provide the required adhesion strength with the binder and the substrate, and the organic vehicle is included so that the glass powder can be made into a paste by mixing therewith. For example, JP-A-59-155988 (Kokai) discloses a method for producing a conductive paste composition for coating a thicker film or layer containing gold, silver, copper, platinum, palladium, nickel, and/or aluminum powder and an organic vehicle by mixing in the presence of a titanate coupling agent. However, this paste is used only for alumina substrates and the titanate coupling agent is used to prevent the formation of metal flakes. JP-A-58-74759 (Kokai) discloses a conductive copper paste composition containing copper powder, a thermosetting resin binder, an unsaturated fatty acid, and an organic titanium compound. The organic titanium compound is used, together with the unsaturated fatty acid, to ensure a fine dispersion of the copper powder and to provide a stable and good conductivity. U.S. Patent No. 4 503 090 discloses a thick film resistor circuit formed from a paste containing copper, silver and aluminum, a binder, ethyl cellulose, and a solvent. When the above known conductive paste compositions are used to form conductors, however, the following disadvantages arise:- (1) The paste compositions containing a noble metal as a conductor component are expensive and, therefore, are not preferable in practice; (2) The paste compositions containing a metal having a high melting point cannot be fired at a relatively low temperature and, since the resistivity of the conductor component is high, the conductor has a poor quality; (3) Although the development of paste compositions having copper as the conductor component is very desirable, the properties when printed on a green sheet of glass-ceramic composite substrate are poor and the adhesion strength after the integral firing is low. Furthermore, although it has been proposed that a small amount of glass having a low melting point be added, to improve the adhesion strength, this is not very effective for glass-ceramic composite substances. Furthermore, when a small amount of glass powder having a low melting point is added, the copper powder has little or no flowability, and during printing, the copper-base paste composition does not easily fill through-holes in a glass-ceramic green sheet. Accordingly, it is desirable to solve the above mentioned problems of the prior art and to provide a method for producing a ceramic circuit board with a copper-base conductive paste having improved printing and adhesion properties, and having other properties such that the copper-base conductive paste composition can be easily filled into through holes in a ceramic circuit board, e.g. a glass-ceramic green sheet, before firing. Using organotitanates as additives in copper-base conductive pastes is known from EP-A-0 177 772 or US-A-4 594 181. In accordance with the present invention, there is provided a method for producing a ceramic circuit board comprising the steps of :- (i) forming a conductor portion of the ceramic circuit board by printing a conductive paste composition on at least one ceramic base plate for the ceramic circuit board, and then (ii) firing said ceramic circuit board together with said conductive paste composition printed thereon, wherein said conductive paste composition consists essentially of (a) a copper powder, (b) a vehicle composed of a binder, a thixotropicity-providing agent, and an alcoholic solvent, and (c) 0.5 to 3.5 parts by weight of isopropyl tridodecylbenzene sulfonyl titanate and 0.5 to 3.5 parts by weight of isopropyl triisostearoyl titanate, both based on 100 parts by weight of the copper powder. Reference will now be made, by way of example, to the accompanying drawings, in which:- Fig. 1 shows a typical process block diagram illustrating the basic steps for preparing a copper-base paste of the present invention; Fig. 2 shows a process diagram illustrating the basic steps for manufacturing a multilayer ceramic circuit board with copper conductors employing the present invention; and Fig. 3 shows a typical graph of adhesion strength of the copper conductor pattern to glass ceramic substrate and sheet resistivity of the copper conductor pattern as a function of concentration of coupling agent in the copper-base paste. As mentioned above, in the present invention, a copper-base paste composition uses specifically the organic titanate compounds set forth in claim 1, these being capable of forming inorganic compounds when fired in an inert atmosphere (e.g. an inert gas or nitrogen). The copper powder used in the paste composition may be any copper powder usually used in copper-base conductive paste compositions, such as copper powders having an average particle size of 0.1 to 10 µm. The organic titanate compounds used in the present invention are isopropyl tridodecylbenzene sulfonyl titanate and isopropyl triisostearoyl titanate. Each organic titanate compound is used in an amount of 0.5 to 3.5 parts by weight, based on 100 parts by weight of the copper powder. When the amount of the organic titanate compound is less than 0.5 parts by weight, the desired paste composition is not obtained. This is thought to be because not all of the surface of each copper powder particle is coated by the organic titanate compound. Conversely, when the amount is excessive, an excess amount of the organic compound remains in the paste composition and will cause voids to appear in the conductor. A copper-base conductive paste composition used in the method according to the present invention can be prepared by first dissolving the organic titanate compounds in a solvent such as an alcoholic high boiling-point solvent (e.g. terpineol, 2-butoxyethanol, 2-hexyloxyethanol, 4-methylcyclohexanol, 3-methylcyclohexanol, and/or 2-hexyloxyethanol) and then thoroughly mixing the resultant organic vehicle with the copper powder, while stirring, to produce the desired copper-base conductive paste composition in the form of a dispersion having a viscosity of 10,000 to 200,000 c.p. The copper-base conductive paste composition can be applied to a glass-ceramic substrate such as ceramic composites of borosilicate glass and alumina, zirconia, or magnesia in any conventional manner. In examples of the method of the present invention, since the entire surfaces of the copper powder particles in the copper-base paste composition are covered with the organic titanate having a monoalkoxy group, the flowability between the copper powder particles is good. Furthermore, a green sheet of a glass-ceramic composite substrate to be printed contains a large amount of a solvent, and thus the wetability of the conductive paste composition to the green sheet is increased. Furthermore, since for example isopropyl tridodecylbenzene sulfonyl titanate is converted to rutile type titanium dioxide (TiO₂) when the copper-base paste composition is fired in an inert atmosphere such as nitrogen, the adhesion strength at the interface between the copper conductor and the glass-ceramic substrate is greatly improved. Fig. 1 shows a typical process block diagram illustrating the basic steps for forming a copper-base paste used in the method of the present invention. An example of a process diagram illustrating the basic steps for manufacturing a multilayer ceramic circuit board with copper conductors embodying the present invention, is shown in Fig. 2. It is feasible that a multilayered structure be formed such that the patterns of copper-based conductors and the glass-ceramic paste are alternately printed on a sintered ceramic substrate, the glass-ceramic paste layers having openings to form through-holes therethrough. It is advantageous that the multilayered structure be formed such that a plurality of composite layers is laminated, each layer being produced by printing patterns of copper-based conductors on a glass-ceramic green sheet, which contains the thermally depolymerizable resin, and minute copper balls are filled in a row penetrating or by printing copper-base paste to the opening as through-holes through the glass-ceramic green sheet. It is preferable that the firing process comprises prefiring the multilayer structure in an inert atmosphere containing water vapour, the partial pressure of which is 0.005 to 0.3 atmosphere, at a temperature at which the thermally depolymerizable resin is eliminated; and firing the multilayer structure in an inert atmosphere containing no water vapour at a temperature below the melting point of copper so as to sinter the glass-ceramic. Fig. 3 is a graph of the adhesion strength of the copper conductor pattern to glass-ceramic substrate and the sheet resistivity of the copper conductor pattern, after sintering, as a function of concentration of the coupling agent in the copper-base paste. Sintering was done by prefiring at 870°C for 4 hours in an inert atmosphere containing water vapour, and then firing at 1020°C for 4 hours in an inert atmosphere not containing water vapour. The composition of the copper-base paste used in Fig. 3 was as follows. This composition is not in accordance with the present invention, but is useful for illustrative purposes. Composition of Copper Paste Ingredient Maker Rate (phr) Cu powder (1.25) MITSUI KINZOKU 100.0 PMMA MITSUBISHI 1.5 Castor oil NODA WAX 0.3 Terpineol WAKOH JUNYAKU 10.5 Coupling agent AJINOMOTO 1.0 In a method of the present invention, two types of organic titanate coupling agents, namely 0.5 to 3.5 parts by weight (preferably 0.5 to 1 part by weight) of isopropyl tridodecylbenzene sulfonyl titanate, and 0.5 to 3.5 parts by weight (preferably 0.5 to 1 part by weight) of isopropyl triisostearoyl titanate, both in relation to 100 parts by weight of the copper powder, are contained in the copper-base conductive paste composition, without using a glass frit, which has an adverse affect on the hole filling properties thereof. The isopropyl triisostearoyl titanate contained in the composition improves the flowability of the copper powder during the hole filling, and the isopropyl tridodecylbenzene sulfonyl titanate improves the adhesion properties to the glass-ceramic substrate, as mentioned above. Thus, the flowability between the copper powder particles is improved by the inclusion of the above-mentioned two types of the titanate coupling agents and, therefore, when the conductive paste composition is made to flow into a through-hole in the green sheet during the printing, since the flowability of the copper-base paste composition is improved and, furthermore, the penetration of the organic vehicle into the green sheet is prevented, the copper-base paste composition can easily flow into the through-hole without causing voids. Furthermore, the adhesion strength is remarkably improved by the action of the two types of the titanate coupling agents, compared to paste compositions not containing the titanate coupling agents. In a paste composition, made for use in the method of the present invention, a vehicle containing connectional ingredients such as a binder, thixotropicity-providing agent, solvent, and any other optional ingredient is used. The amount of the vehicle in the composition is preferably 5 to 30 parts by weight based on 100 parts by weight of the copper powder. As mentioned above, and as explained below, in examples of the present invention, the printing of the copper-base paste composition on the glass-ceramic substrate is remarkably improved and the adhesion between the substrate and the conductor is excellent. Furthermore, a conductor without voids can be obtained, without causing a penetration of the solvent and without an adverse affect on the flowability of the powder particles during the filling of the holes in the board. The present invention now will be further illustrated by, but is by no means limited to, the following Example and Comparative Example, wherein all parts and percentages are expressed on a weight basis unless otherwise noted. Comparative Example The copper-base paste compositions having the following formulations listed in TABLE 1, which are not according to the present invention, were prepared. Formulation of Copper-base Paste Component Copper Paste Sample No. 1 2 3 Copper powder (1 µm) 100 parts 100 parts 100 parts Organic vehicle 13 parts 13 parts 13 parts Organic titanate 0.5 parts 1 part 1.5 parts Viscosity (poise) 400-600 400-600 400-600 The copper-base paste composition Sample Nos. 1 to 3 were prepared as follows. That is, the isopropyl tridodecylbenzene sulfonyl titanate was dissolved in a high boiling-point alcoholic solvent (i.e. terpineol) at a temperature of 25°C, followed by adding thereto a thixotropy-providing agent (i.e. castor oil) and an organic depolymerizable binder (PMMA). Thus, the organic vehicle was prepared. The copper powder having a particle size of 1.5 µm was mixed into the organic vehicle and the resultant mixture was mixed by wet ball mill mixing at room temperature for 48 hours, followed by drying and then mixing or kneading in a three-roll mill. The copper-base paste composition Sample Nos. 1 to 3 were evaluated with respect to their characteristics by using a glass-ceramic substrate composed of borosilicate glass and alumina as follows. That is, the above-prepared copper-base paste composition Sample Nos. 1 to 3 were applied to the surfaces of green sheets of borosilicate glass-alumina composite ceramic having a thickness of 300 µm in a conventional manner under the conditions of a size of a screen mask of 300 mesh, a pattern width of 80 µm, and a squeegee hardness of 80. The printed paste composition was then dried in a constant temperature bath at a temperature of 70°C for 30 minutes to evaporate the solvent 1. The printed green sheet was then pressed in a mold under the conditions of 10 MPa x 100°C x 30 min. The resultant laminate having 30 layers was heated from room temperature at a rate of 80 to 100°C/hr and allowed to stand for 5 hours at a maximum temperature of 850°C in a nitrogen atmosphere containing water vapour, followed by allowing the laminate to cool to room temperature. Thereafter, the resultant laminate was heated from room temperature to a maximum temperature of 1000°C at a rate of 80 to 100°C/hr and allowed to stand at the maximum temperature for 4 hours in a nitrogen atmosphere not containing water vapour, followed by allowing it to cool to room temperature. As mentioned above, a typical manufacturing process of the multilayer ceramic board with the copper conductor is shown in Fig. 2. The results are shown in TABLE 2. The evaluation results of the conductor characteristics of Sample Nos. 1 to 6 are shown in TABLE 3. Example The copper-base paste composition Sample Nos. 1 and 2 exemplifying pastes used in the method of the present invention, having the compositions listed in TABLE 4, were prepared. Composition of Copper Paste Ingredient Copper Paste Sample (parts) 1 2 Copper powder (1.5 µm⊘) 100 100 Organic vehicle 13 14 Isopropyl tridodecylbenzene sulfonyl titanate 0.5 0.5 Isopropyl triisostearoyl titanate 0.5 1 These copper paste compositions were prepared as follows. To the organic vehicle containing an organic solvent (i.e. 2-hexyloxy ethanol, and terpineol), an organic thixotropy-providing agent (i.e. castor oil), and a binder (i.e. ethyl cellulose,PMMA), the Ti coupling agent listed in TABLE 5 was added. The mixture was agitated at a temperature of 25°C and the copper powder having a size of 1.5 µm was mixed thereinto. The mixture was mixed by wet ball mill mixing and, after drying, the mixture was mixed or kneaded in a three-roll mill to produce the desired copper-base composition in the form of a paste. The paste compositions thus prepared were applied, in the same manner as in the Comparative Example, to borosilicate glass-alumina composite ceramic substrate. The evaluation was carried out in the same manner as in the Comparative Example. The results of the sheet resistivity, the adhesion strength to the substrate, and hole filling property are shown in TABLES 5 and 6. Characteristics of Copper Paste after Firing Copper Paste Composition Sample No. Sheet Resistivity (mΩ/□) Adhesion Strength to Substrate (kg/mm²) 1 1.0 1.6 2 1.0 1.6 3 1.0 0.5 4 1.5 2.0 5 1.2 0 6 1.0 0 Hole-filling of Copper Paste in Glass-ceramic Green Sheet Copper Paste Sample No. Hole-filling Percentage (100 µm⊘, v = 1000) Hole-filling Conditions 1 99.0% Good 2 99.0% Good 3 90.0% Good 4 60.0% Void in Via 5 99.0% Void in Via 6 90.0% Good Furthermore, when isopropyl tridodecylbenzene sulfonyl titanate and isopropyl triisostearoyl titanate were used together, the improvement in the adhesion strength was obtained when 0.5 parts by weight or more of isopropyl tridodecylbenzene sulfonyl titanate was used. On the other hand, the upper limit of the total amount of the isopropyl tridodecylbenzene sulfonyl titanate and isopropyl triisostearoyl titanate is preferably 4 parts by weight, because, when the total amount is more than 4 parts by weight, the organic content in the paste composition becomes large and the generation of voids around the vias (through holes) is liable to occur after firing the multilayer circuit board.

Claims: A method for producing a ceramic circuit board comprising the steps of:- (i) forming a conductor portion of the ceramic circuit board by printing a conductive paste composition on at least one ceramic base plate for the ceramic circuit board, and then (ii) firing said ceramic circuit board together with said conductive paste composition printed thereon, wherein said conductive paste composition consists essentially of (a) a copper powder, (b) a vehicle composed of a binder, a thixotropicity-providing agent, and an alcoholic solvent, and (c) 0.5 to 3.5 parts by weight of isopropyl tridodecylbenzene sulfonyl titanate and 0.5 to 3.5 parts by weight of isopropyl triisostearoyl titanate, both based on 100 parts by weight of the copper powder. A method as claimed in claim 4, wherein said base plate is a ceramic green sheet. A method as claimed in claim 4 or 5, wherein plural ceramic base plates each having the conductive paste composition printed thereon are laminated before firing.

Inventors: KAMEHARA NOBUO, NIWA KOICHI, OGAWA HIROMI, SUZUKI HITOSHI, TSUKADA MINEHARU, YOKOYAMA HIROMITSU, KAMEHARA, NOBUO, NIWA, KOICHI, OGAWA, HIROMI, SUZUKI, HITOSHI, TSUKADA, MINEHARU, YOKOYAMA, HIROMITSU
Applicants: FUJITSU LTD, FUJITSU LIMITED
Application year: 1987
Main classification: H05K3
IPC codes: H05K1, H01B1, H05K3