BETA2 MICROGLOBULIN ADSORBENT

Abstract: A β₂ microglobulin adsorbent composed of hydroxy­ apatite particles having an average size of 5 to 2,000.µm is disclosed. The adsorbent preferably has a Ca/P ratio of 1.5 to 1.8.

Description: FIELD OF THE INVENTION The present invention relates to an adsorbent or material that is used for an efficient adsorption of β2 microglobulins in blood. BACKGROUND OF THE INVENTION It has been known that proteins whose molecular weights are too low to be rejected by conventional techniques of blood dialysis occur in blood of patients with renal insufficiency who are receiving dialysis treatment. Among these proteins β₂ microglobulins (hereinafter abbreviated as β₂MG) are those which cause amyloidosis that frequently occurs in subjects receiving dialysis over a prolonged period and removal of this substance is important for successful treatment of renal insufficiency. Heretofore, various techniques of blood purification have been employed as the principal means of treating patients with renal insufficiency and they include hemodialysis, blood filtration, blood filtration/dialysis, protein permeating filtration/dialysis, sustained extraneous peritoneum dialysis, blood adsorption therapy with activated carbon, and plasma exchange. However, the clearance or reject ratio of β₂MG that can be attained by each of these methods is less than 50% and no significant drop of blood β₂MG levels can be expected. From CHEMICAL ABSTRACT, vol. 68, 1968, page 7380, abstract no. 765695, the isolation of beta1A/C-globulin from human serum with the aid of hydroxyapatite and DEAE-cellulose column chromatography is known. Furthermore, PATENT ABSTRACTS OF JAPAN, vol. 10, no. 53 (P-433) [2110], corresponding to JP-A-60 198 458 discloses the use of hydroxyapatite as a stationary material for column chromatography. CHEMICAL ABSTRACTS, vol. 72, 1970, page 71 , abstract no. 118300n, discloses the resolving power of hydroxyapatite columns. None of these prior art references discloses or suggests the use of hydroxyapatite as an adsorbent for β₂MG. There is a strong demand in clinical fields to develop a higher-performance β₂MG adsorbent and to establish an efficient means for blood purification by using such an adsorbent in blood adsorption. SUMMARY OF THE INVENTION An object of the present invention is to provide an adsorbent that can be used in blood adsorption for the purpose of efficient removal of β₂MG and other deleterious components from blood. In order to attain this object, the present inventors conducted intensive studies in which they compared the ability of various substances to adsorb β₂MG and as a result, they found that hydroxyapatite had a particularly high capability of adsorbing β₂MG. The present invention has been accomplished on the basis of this finding. The present invention is directed to the use of hydroxy apatite particles having an average size of 5 to 2000 µm as a β₂ microglobulin adsorbent. BRIEF DESCRIPTION OF THE DRAWING The accompanying drawing is a graph showing the relationship between the incubation time of serum containing the adsorbent of the present invention and each of the β₂MG level and the total protein content of the serum. The term "TP" represents "total protein" present in blood. DETAILED DESCRIPTION OF THE INVENTION The hydroxyapatite particles of which the adsorbent of the present invention is made can be synthesized by any of the known methods such as the wet process in which a water-soluble phosphate salt and a water-soluble calcium salt are reacted in an aqueous solution and the dry process in which a phosphoric acid compound is reacted with a calcium compound at high temperatures. Whichever method of synthesis is employed, it is preferable to blend the starting materials in such proportions that the Ca/P ratio of the hydroxyapatite to be finally obtained will be in the range of 1.5 to 1.8. If the Ca/P ratio is less than 1.5, great difficulty will be involved in obtaining the desired product since the crystalline structure of apatite cannot be retained. If the Ca/P ratio exceeds 1.8, products other than apatite will also form, which reduces the ability of the finally obtained product to adsorb β₂MG. The hydroxyapatite particles produced by either one of the methods described above is subsequently granulated by any common technique such as spray granulation with a spray dryer, disk granulation, and crush granulation. In the first method, a slurry of hydroxyapatite particles dispersed in water is spray-dried at a temperature of about 100 to 250°C to form generally spherical granules. In the second method, the hydroxyapatite particles on a disk plate are allowed to agglomerate into granules by rotating the disk. In the third method, blocks of hydroxyapatite particles are crushed into granules. The hydroxyapatite granules may assume a variety of shapes such as spherical, flaky, filamentous and amorphous forms, provided that they will have an average size of 5 to 2,000 µm after firing. If the average size of fired hydroxyapatite granules is less than 5 µm, an increased pressure loss will occur when blood to be treated is allowed to flow. If the average particle size exceeds 2,000 µm, the specific surface area of the hydroxyapatite particles is reduced to cause a corresponding decrease in adsorption capacity. The hydroxyapatite granules are then fired preferably at a temperature between 100 and 1,400°C so as to attain the β₂ MG adsorbent of the present invention. If the firing temperature is less than 100°C, the strength of the fired granules is weak enough to increase the chance of their crumbling into fine particles. If the firing temperature exceeds 1,400°C, the hydroxyapatite will undergo decomposition and its adsorption capacity is decreased. The structure of the hydroxyapatite particles may be porous or solid. In practice, the β₂MG adsorbent of the present invention is packed in a column through which blood to be treated is passed. By this procedure, β₂MG and other deleterious components in the blood are adsorbed on the column to produce a purified effluent. The following examples are provided for the purpose of further illustrating the present invention but are in no sense to be taken as limiting. EXAMPLE 1 A solution of a phosphate salt was reacted with a solution of a calcium salt by a known method and a slurry of hydroxyapatite was formed. This slurry was dried and granulated with a Mobile Minor spray dryer (product of Ashizawaniro) under the following conditions: hot air temperature, 200°C; feed rate, 2.5 ℓ/hr; rotational speed of spray disk, 25,000 rpm. The granulation was fired to produce hydroxyapatite particles having an average diameter of 20.µm. These hydroxyapatite particles and four comparative adsorbents, namely cellulosic adsorbent, PAN (polyacrylonitrile) adsorbent of Mitsubishi Rayon Company Limited, immuno-adsorbent IMP (crosslinked polyvinyl alcohol gel), and a sheet of activated carbon (product of Toyobo Co., Ltd.), were used in adsorption of β₂MG in the sera of patients under dialysis using the following procedures. One gram each of the test adsorbents was distributed among test tubes, washed with distilled water, and centrifuged at 3,000 rpm for 15 minutes, followed by discarding the supernatant. Six mℓ of serum was added to each sample which was shaken several times and left to stand for 60 minutes. Measurement of β₂MG was conducted by the double antibody technique with a β₂MG radio-immunoassay kit of Eiken Chemical Co., Ltd. The results are shown in Table l. Adsorbent β₂MG (mg/ℓ) Hydroxyapatite 3.5 Cellulosic adsorbent 26.3 PAN adsorbent 22.7 Immunoadsorbent 21.1 Sheet of activated carbon 21.6 Control 22.6 As the above data shows, the hydroxyapatite particles had a much higher ability to adsorb β₂MG than the comparative adsorbents which could adsorb little or no β₂MG. EXAMPLE 2 Hydroxyapatite (20µm) particles were prepared as in Example 1, and one-gram portions thereof were put into 9 test tubes, washed with distilled water and centrifuged at 3,000 rpm for 15 minutes, followed by discarding of the supernatant. A 6-mℓ portion of serum was put into each of the test tubes. One of these test tubes was shaken several times after addition of serum and immediately subjected to compositional analysis (Sample No. 1). The other tubes were grouped in twos and given 30 shakes per minute at room temperature for 15 minutes (Sample Nos. 2-a and 2-b), 30 minutes (Sample Nos. 3-a and 3-b), 60 minutes (Sample Nos. 4-a and 4-b) and 120 minutes (Sample Nos. 5-a and 5-b). Thereafter, these 8 samples were subjected to compositional analysis. The compositional analysis was conducted on the supernatant that had been separated from each sample by centrifugation at 3,000 rpm for 10 minutes, and the total protein (TP), alubumin (Alb), total bilirubin (T. bil), direct reacting bilirubin (d), indirect reacting bilirubin (i), and β₂MG present in the supernatant were determined. The results of these measurement are summarized in Table 2, and the relationship between sample shaking time and each of the TP and β₂MG levels is shown in the accompanying drawing. Table 2 and the drawing show that the adsorption of β₂MG is largely independent of the shaking time, with momentary adsorption occurring simply as a result of imparting several shakes. Therefore, the adsorbent of the present invention is highly adapted for continuous blood treatment by such techniques as passage through a column packed with the adsorbent. Sample No. Shaking Time TP (g/dℓ) Alb (g/dℓ) Tibil (mg/dℓ) d/i β₂MG (mg/ℓ) Control 5.2 3.4 19.7 9.0/10.7 28.6 1 0 3.0 1.9 8.2 5.1/3.1 3.4 2-a 15 2.9 1.9 6.9 4.2/2.7 4.3 2-b 15 2.9 1.9 7.2 4.6/2.6 3.3 3-a 30 2.9 1.9 7.6 4.9/2.7 4.3 3-b 30 2.9 2.0 7.5 4.7/2.8 3.1 4-a 60 2.9 1.9 7.6 4.8/2.8 3.5 4-b 60 2.9 1.9 7.4 4.7/2.7 3.2 5-a 120 2.9 2.0 7.3 4.7/2.6 2.9 5-b 120 2.9 1.9 7.1 4.6/2.5 3.2 As described in the foregoing, the adsorbent of the present invention which is composed of hydroxyapatite particles with an average size of 5 to 2,000.µm is highly effective in adsorbing β₂MG in blood so as to produce a purified effluent. The adsorbent can, therefore, be used to eliminate β₂MG from the blood of patients under dialysis treatment so as to prevent the occurrence of amyloidosis and other β₂MG-related disorders of protein metabolism. While the invention has been described in detail and with reference to specific embodiments thereof, it will be apparent to one skilled in the art that various changes and modifications can be made therein without departing from the spirit and scope thereof.

Claims: Use of hydroxy apatite particles having an average size of 5 to 2000 µm as a β₂ microglobulin adsorbent. Use according to claim 1, wherein said hydroxy apatite particles have a Ca/P ratio of 1.5 to 1.8. Use according to claim 1, wherein said hydroxy apatite particles are spherical, flaky, filamentous or amorphous in shape. Use according to claim 2, wherein said hydroxy apatite particles are spherical, flaky, filamentous or amorphous in shape. Use according to claim 3, wherein said hydroxy apatite particles are porous in surface structure. Use according to claim 4, wherein said hydroxy apatite particles are porous in surface structure. Use according to claim 3, wherein said hydroxy apatite particles are non-porous in surface structure. Use according to claim 4, wherein said hydroxy apatite particles are non-porous in surface structure.

Inventors: KOSHIKAWA, SHOZO, NAKABAYASHI, NOBUO, OGAWA, TETSURO C/O ASAHI KOGAKU KYOGO
Applicants: ASAHI KOGAKU KOGYO KABUSHIKI KAISHA
Application year: 1987
Main classification: B01J20
IPC codes: B01J20, A61M1