IMPROVEMENTS IN OR RELATING TO THE MOULDING OF PLASTICS PRODUCTS

Abstract: The invention provides a method of moulding a plastics material comprising the steps of placing the material with a quantity of an appropriate catalyst in granular (including powdered) form into a hollow mould shell (1); suspending the mould in a mounting system enabling rotation in a plurality of directions whereby the powdered material, together with the catalyst, is able to flow over all the interior surfaces; containing the mould and mounting system within an oven (7) and heating the mould therein whilst rotating the same; cooling the mould and subsequently withdrawing the moulded article therefrom.

Description: This invention relates to the production of plastics products. It is well known to mould plastics products, such as polyethylene and its co-polymers, by injection moulding. However, injection moulding suffers from the disadvantage that tooling costs are relatively high and that there is a limited size range capable of injection moulding. It has also been proposed to mould thermoplastic materials by placing powdered or granular material in a hollow metal mould shell which is then suspended in a mounting system enabling rotation in one or two axes causing the powdered material to flow over all the interior surfaces of the mould shell (which have, of course, the appropriate mould impressions). The mounting system and the mould is then contained within an oven which heats the mould to the desired appropriate temperature (above the melting temperature of the plastics polymer concerned) and after a period of rotation with the oven the powdered material melts and creates a relatively even coating over the inside of the mould thus taking the mould impression. The mould is then removed from the oven for cooling and the moulded article then removed from the mould. Such a rotational system does, in certain circumstances, suffer from the drawback that high melt flow (low molecular weight) materials must be used in order to achieve satisfactory mould quality. Such materials, in practice, commonly have poor physical properties unsuitable for certain applications. In addition, materials of low or moderate melt flow give, not only poor moulding quality, but also a porosity which further reduces certain physical properties. It is for this reason that the practice of crosslinking during the rotational moulding process has become common. The production of high quality, tough mouldings can be made possible with crosslinking. There are however associated disadvantages of higher material cost and inability of mouldings, now of a thermoset nature, to be fusion welded, for example. It is an object of the present invention to provide a moulding arrangement which overcomes or at least substantially reduces the above mentioned disadvantages and drawbacks. In accordance with the invention, there is provided a method of moulding a plastics material comprising the steps of placing the material with a quantity of an appropriate catalyst in granular (including powdered) form into a hollow mould shell; suspending the mould in a mounting system enabling rotation in a plurality of directions whereby the powdered material, together with the catalyst, is able to flow over all the interior surfaces; containing the mould and mounting system within an oven and heating the mould therein whilst rotating the same; cooling the mould and subsequently withdrawing the moulded article therefrom. By "an appropriate catalyst" as used herein we mean a catalyst or agent of a kind which will, during the moulding process, bring about a significant controlled increase in molecular weight of the plastics material polymer, but, most importnt, no significant cross-linking effect. This may occur, for example, by process steps involving initially heating the rotating mould at a temperature sufficient to melt the polymer and allow it to flow into the desired moulded shape, but below the activation temperature of the catalyst, and subsequently raising the temperature of the oven, when the initial moulding stage is assessed to be complete, thereby activating the catalyst and creating an increase in molecular weight of the polymer. Depending upon the thickness of the moulding the process may also be carried out at a single moulding temperature whereby melting and activation of catalyst occurs sequentially due to the temperature gradient resulting from the poor heat transfer in the moulding. The selection of the catalyst or agent and its activation properties is, of course, important. We have found that, for example, a free radical initiator such as an organic peroxide is a suitable agent. It is important to stress that no significant cross-linking effect is produced by the method of the present invention is that no thermosetting product, with the severe problems mentioned above, results. In addition, in order to achieve satisfactory results, care must be taken in selecting the polymer utilised as its molecular weight distribution and level of unsaturation will greatly influence the success of the process as will the type and level of heat and ultra-violet light stabilisers. We have found certain polyethylene polymers or co-polymers to be very satisfactory. We have found the process according to the invention to be of particular use in moulding large bore fittings for polyethylene gas and water pipes, large bore pipes, inspection chambers and tanks. To produce large (300mm and greater) fittings by injection moulding, for example, would require equipment hitherto unavailable and, in any event, the tooling costs would be very high and difficult to recover on the low number of mouldings required commercially. In contrast, rotational mouldings of this size are a practical proposition and mould costs commercially reasonable, but such moulding often do not have the performance to match that of pipe extruded from pipe grade materials. Even if crosslinked rotational mouldings are considered they may have the required performance but because they are thermosetting material they cannot be joined by fusion welding. In contrast, mouldings manufactured according to this invention can have their performance tailored to match that of the extruded thermoplastics pipe and also retain the ability to be fusion welded into pipeline systems. By means of the process of the invention there is only an increase in molecular weight of the polymer such that the material benefits from improved physical properties but remains thermoplastic and retains the ability for fusion welding of fittings for example to pipes, the reaction is not taken to such a level that crosslinking takes place which would result in the production of an intractable thermosetting material. The method of the present invention may be used as a precursor or preliminary stage to further processing e.g. subsequent irradiation or heat treatment in order further to enhance physical properties. Thus, for example, a rotationally moulded pipe fitting produced according to the method of the invention, may have short lengths of pipe welded to it, and may subsequently be irradiated using either gamma ray or electron beam radiation, in order to cause cross-linking of the fitting and weld zone. In such a case, the free ends of the pipes may be protected from irradiation by, for example, lead shielding, so that they remain substantially unaffected by the radiation and may be subsequently joined to other pipes or fittings by further welding. Such further processing may be used because it has been found, for example, that products such as pipe components of the method of the present invention can be used with conventional welding techniques for joining to pipe prior to irradiation. We believe this is difficult when not using products of the method of the invention, because rotomoulded goods tend to have a much higher melt flow index than extruded pipes, thereby causing welding difficulties due to different welding temperature requirements. In order that the invention may be more readily understood, one embodiment thereof will now be described by way of example with reference to the accompanying drawing which illustrates schematically rotational moulding equipment for use in the process of the present invention. Referring now to the drawing, it will be seen that a plurality of moulds 1 mounted on spiders 2 are carried on arms 10 rotatable with a crosspiece 9 of a spindle 3 carrying drive motors 4. The spindle arm is pivotal on a support 8 between positions where the moulds are located within a cooling chamber 5, a loading and unloading station6, and an oven 7. Activation of the drive motors 4 causes rotation of the spindle 3 carrying the spiders, and rotation of the spiders themselves on the arms 10 associated therewith. By this means, the moulds are rotated in all three directions so that any polymer material located therein flows freely throughout the moulds to cover the interior mould configuration. By way of an example, a polyethylene homo-polymer or co-polymer of density ranging from 0.870 to 0.970g per cc and preferably 0.93 to 0.95g per cc and a melt flow index ranging from 1.0 to 40.0g per 10min (2.16kg load weight) and preferably 5.0 to 20.0g per 10 mins is blended with heat and ultra-violet light stabilisers, and a free radical initiator (preferably an organic peroxide or azo compound). Alternatively, and preferably, the free radical initiation and the heat and ultra-violet light stabilisers are dispersed into the polymer by a compounding operation prior to rotomoulding, by which is meant, for example, melt processing in either a single screw extruder having a mixing action, or twin screw extruder, or other mixing equipment such that the initiator and other additives are well dispersed in the polymer melt at a temperature below the activation temperature of the initiator, but above the melting point of the polymer. The material is then further processed as necessary to give a powder suitable for rotomoulding. This mixture, in powder form, is then added in the required quantities to each of the moulds in the rotary moulding apparatus. The moulds and the associated spiders are then pivoted into the oven and rotated whilst the oven is heated to between 150 and 500°C preferably between 200 and 400°C, for between 5 and 120 minutes preferably 20-40 minutes, depending upon the quantity of powder added to the moulds and the required section thickness of the moulding and the initial melt flow index of the polyethylene. After this period, the temperature of the melt in the mould within the oven is raised to between 180 and 280°C preferably 220 to 240°C to allow activation of the initiator, and rotary moulding continued for a further 5 to 120 minutes preferably 20-40 minutes depending on the moulding section thickness within the mould. Thereafter, the spindle and spider, with contained moulds, is moved to the cooling chamber and allowed to cool to room temperature. After cooling, the resultant moulding is found to have a melt flow index of between 1.0 and 0.01g per 10 mins (2.16kg load weight) and preferably between 0.4 and 0.1g/10 minutes. The process may also be used to produce other rotary moulded hollow objects that require good physical properties and can undergo fusion welding operations, for example vehicle petrol tanks, marine craft and leisure goods and containers.

Claims: 1 A method of moulding a plastics material comprising the steps of placing the material with a quantity of an appropriate catalyst in granular (including powdered) form into a hollow mould shell; suspending the mould in a mounting system enabling rotation in the plurality of directions whereby the powdered material, together with the catalyst, is able to flow over all the interior surfaces; containing the mould and mounting system within an oven and heating the mould therein whilst rotating the same; cooling the mould and subsequently withdrawing the moulded article therefrom. 2 A method as claimed in claim 1 wherein the catalyst is a free radical initiator. 3 A method as claimed in claim 1 or 2 wherein the catalyst is an organic peroxide. 4 A method as claimed in any one of the preceding claims wherein the plastics material is a polyethylene polymer or co-polymer. 5 A method as claimed in any one of the preceding claims used in the production of a polyethylene pipe fitting. 6 A method as claimed in any one of the preceding claims including the subsequent step of welding the rotationally moulded article to a further plastics material article and subjecting the welded composite product to irradiation. 7 A method as claimed in any one of claims 1 to 5 including the subsequent step of welding the rotationally moulded article to a further plastics material article and subjecting the welded composite to heat treatment.

Inventors: KLIENE, RONALD IAN, WILSON, KEITH ANDREW
Applicants: ROTEC CHEMICALS LIMITED, VICTAULIC PLC
Application year: 1987
Main classification: B29C41
IPC codes: B29C41, B29C71, B29C65