GLASS/POLY(CARBOXYLIC ACID) CEMENT COMPOSITIONS

Abstract: A process for producing a radiopaque cement comprises reacting a polymer containing free carboxyl groups (generally a homo or copolymer of acrylic acid) with a particulate acid-leachable source of polyvalent metal ions (such as an acid-leachable glass) in the presence of water and strontium fluoride.

Description: This invention is concerned with improvements in and relating to glass/poly(carboxylic acid) compositions. Glass/poly(carboxylic acid) cement compositions are well known and established. Such compositions basically comprise (i) a polymer containing free carboxylic acid groups (typically a homo- or co-polymer of acrylic acid) and (ii) an acid leachable source of polyvalent metal ions (e.g. an acid leachable glass such as a calcium aluminofluorosilicate glass). In the presence of water, the polyacid leaches polyvalent metal ions from the source thereof and these serve to cross-link the polymer chains to give a solid material (a cement). Such compositions are discussed authoritatively in, for example, "Organolithic Macromolecular Materials" by A.D. Wilson and S. Crisp. Applied Science Publishers, 1977 (see especially Chapter 4). Glass/poly(carboxylic acid) cement compositions have been found to have particular application as dental restorative materials but suffer from one practical disadvantage in that they are radiolucent, that is they are essentially transparent to X-rays. As a result, it it is not possible, for example, to examine a dental restoration, carried out using such a composition, by means of an X-ray technique and, further, it is not possible to locate any portion of a dental restoration which may become dislodged and ingested by a person, using an X-ray technique. US-A-4215033 describes a composite dental material comprising inorganic glass particles combined with an organic resin. The glass may include strontium oxide. However, there is no disclosure of the use of strontium fluoride as a radioopacifying agent, nor that the inorganic glass may constitute a source of fluoride ions. FR-A-2246589 describes a dental restoration composition which comprises a mixture of inorganic glasses and an acrylic resin. One of the inorganic glasses is transparent to X-rays and the other is a radioopaque barium glass. There is no disclosure of the use of strontium fluoride as a radioopacifying agent in a dental composition. US-A-4492777 describes the heat treatment of acid-washed barium or strontium glass powders for use in dental composite materials. The document contains no details of the strontium glass powders except that they contain strontium oxide. In particular, there is no disclosure of the use of strontium fluoride as a radioopacifying agent in a dental cement. The radioopacity of tooth substances (i.e. the degree to which they absorb X-rays) may conveniently be defined in terms of the thickness (in mm) of aluminium having the same radioopacity as 1 mm of the substance. Typical values for enamel are 1.3-2.7 mm aluminium per mm enamel and for dentine, 0.6-2.0 mm aluminium per mm dentine. It has now been found, in accordance with the present invention, that a radioopaque cement may be formed from a composition comprising a polymer containing free carboxyl groups, an acid leachable source of polyvalent metal ions and water, and also containing strontium fluoride. In the compositions of the invention, strontium fluoride provides substantially all the radioopaque properties even in the presence of other materials having some radioopacifying properties. It has further been found that the use of strontium fluoride gives an optically transparent set cement (similar to the set cement obtained in the absence of strontium fluoride), which renders the set cement of the invention of value in dental restoration. Expressed in terms of the C 0.70 value, the translucency is suitably less than 0.7, preferably less than 0.6 and most preferably less than 0.5. According to the invention, therefore, there is provided a method of producing a cross-linked cement which comprises reacting a polymer containing free carboxyl groups with a particulate acid- or alkali-leachable source of polyvalent metal ions in the presence of water and strontium fluoride, where strontium provides substantially all radioopaque properties in the set cement. In order to achieve acceptable radioopacity in use, the strontium fluoride is suitably present in an amount of from 7.5 to 50%, preferably 15 to 33%, and more preferably 19 to 23%, by weight, based on the total weight of the polymer containing free carboxyl groups, the acid leachable source of polyvalent metal ions and the strontium fluoride. The source of polyvalent metal ions may, for example, be an acid-leachable glass such as a calcium aluminofluorosilicate glass, preferably comprising; calcium (calculated as CaO) 9 to 25% by weight; aluminium (calculated as Al₂O₃), 28 to 38%, by weight; silica (calculated as SiO₂) 25 to 30% by weight; and fluorine (calculated as F₂), 0 to 12% by weight; and phosphorus (calculated as P₂O₅), 0 to 9% by weight. For the sake of convenience the source of polyvalent metal ions will hereinafter simply b e referred to as a "glass". As will be appreciated strontium fluoride itself may serve as a source of polyvalent metal ions. The polymer containing free carboxyl groups is preferably a homopolymer of acrylic acid. Copolymers of acrylic acid, may be used but are less suitable (see D.J. Setchell et al, British Dental Journal, 1985, Vol. 158: Vol. page 220). The acrylic acid polymer or copolymer suitably has a molecular weight of 20,000 to 125,000, preferably 35,000 to 70,000, and most preferably preferably 45,000 to 55,000. For the sake of convenience the polymer containing free carboxylic acids will hereinafter simply be referred to as a "polyacrylic acid". The glass should be in particulate form and suitably has a particle size of from 0.5 to 60 µm. The particle size of the glass may vary within these limits depending upon the intended end use of the composition. Thus, for example, where the composition is to be used as a simple dental restorative material (i.e. as a filling or stopping material) the particle size is suitably from 0.5 to 40 µm, preferably 1 to 30 µm, and most preferably 2 to 20 µm; and when intended for use as a sub-filling, base or liner under a so-called "composite" dental restorative material (i.e. a mixture of an ethylenically unsaturated resinous material, an inert particulate filler and a curing agent for the resinous material), the particle size is suitably 2 to 60 µm. preferably 2 to 40 µm and most preferably 5 to 30 µm. The weight ratio of polyacrylic acid to glass is suitably from 0.15:1 to 0.5:1, preferably 0.2:1 to 0.3:1; and the weight ratio of water to glass is suitably from 0.2:1 to 0.5:1, preferably about 0.25:1. The reaction of the polyacrylic acid and glass may be carried out in the presence of other materials serving to alter or modify the working time and/or setting time of the mixture, e.g. a hydroxycarboxylic acid such as tartaric acid which serves to increase the rate of set of the composition without effecting the working time. Compositions for forming a solid cement from glass, polyacrylic acid and strontium fluoride may be put up as two-part packs, one part comprising an aqueous solution of the polyacrylic acid (and optionally working/setting time modifiers) and the other part comprising a particulate glass together with strontium fluoride. Alternatively, a dry blend may be formed of particulate glass and a powdered polymer and strontium fluoride for subsequent addition of water to form a cement-forming composition. Cements formed in accordance with the invention are radioopaque and we have found that they are eminently suitable as base-fillings, bases or liners for use in under the so-called composite filling materials discussed above. A wide variety of such composite filling materials are known or have been proposed. Those in more common use comprise a polyethylenically unsaturated monomer or oligomer (e.g. bis-GMA or a derivative thereof or a urethane diacrylate), an ethylenically unsaturated component (e.g. ethylene glycol dimethacrylate), a filler and a polymerization initiator. Typical fillers are particulate quartz, borosilicate glasses or glass ceramics having a particulate size of from 1 to 80 um, and/or colloidal silica having a particulate size of 0.005 to 0.2 um. The polymerization initiator may be a heat room temperature acting initiator, such as benzoyl peroxide and a tertiary amine, or may be an actinic radiation sensitive initiator such as benzophenone or camphorquinone. In accordance with a further embodiment, the invention includes the use in dental restoration of a radioopaque cross-linked cement formed as a base, liner or sub-filling for an overlying filler formed from a composite dental composition comprising one or more ethylenically unsaturated compounds, a particulate filler and a polymerisation initiator for the ethylenically unsaturated compound(s). Strontium fluoride may be used, in accordance with the invention, as radioopacifying agent in other dental restorative materials, e.g. in composite type materials as discussed above. In particular, strontium fluoride may be used in composite filling materials and in pit and tissue sealants where the caries inhibiting effect of fluoride in ion is particularly desirable and the radioopacifying effects of strontium fluoride may assist in the diagnosis of recurrent caries. In a broader aspect, the invention provides a resinous structure containing strontium as a radioopacifying agent, which provides substantially all the radioopaque properties in the resin. Such a structure, which is preferably translucent, suitably has a radiopacity of at least 1.0 mm of aluminium per mm of structure, preferably at least 1.5 mm, most preferably at least 2.0mm of aluminium per mm of structure. Such a structure is suitably used for dental restorative procedures. In order that the invention may be well understood the following Examples are given by way of illustration only. In the Examples all percentages are by weight unless otherwise stated. EXAMPLE 1 A cement-forming powder was prepared from (a) 62.1% by weight of a particulate calcium fluoroaluminosilicate glass (commercially available as Chemfil II) having a Sauter Mean Diameter of 5 µm. (b) 15.1% of a polyacrylic acid powder having a molecular weight of 45,000, (c) 1.3% of tartaric acid, and (d) 21.5% of strontium fluoride. The powder was mixed with water, by hand using a dental spatula and a glass block, at a powder/water ratio of 6.8:1. The resulting cement typically had a working time at 23°C of 2 minutes, a radiopacity of 2.5 mm aluminium per 1 mm cement, a compressive strength of 182 MPa, a diametral strength of 15.3 MPa and a solubility of 0.25%. EXAMPLE 2 A powder was prepared as described in Example 1 except that it contained 69.3% of the powdered glass and 14.3% of strontium fluoride. The powder was evaluated as described in Example 1 and was found to have a typical working time of 2 minutes at 23°C, a compressive strength of 204 MPa, and a radiopacity of 1.4 mm per 1 mm cement. EXAMPLE 3 10 Grams of a resin comprising 5 parts of the urethane adduct of 2 moles of hydroxypropyl methacrylate and tri-methylhexamethylene diisocyanate are dissolved in 10 grams of triethylene glycol dimethacrylate. They are then dissolved in the solution, 0.03 g of camphorquinone and 0.2 g of methyldiethanolamine; and finally, 15 g of strontium fluoride having a particle size less than 10 µm is dispersed in the solution. The resulting composition is polymerized by actinic radiation using a Prismalite (product of L.D. Caulk Division, Dentsply Inc.) using 20 seconds of irradation, to provide a radiopaque composition suitable for sealing pits and fissures.

Claims: A method of producing a radioopaque cross-linked cement which comprises reacting a polymer containing free carboxyl groups with a particulate acid- or alkali-leachable source of polyvalent metal ions in the presence of water and strontium fluoride where strontium provides substantially all radioopaque properties in set cement. A method as claimed in claim 1 in which the strontium fluoride is present in an amount of from 7.5 to 50% by weight, based on the total weight of the polymer containing free carboxyl groups, leachable source of polyvalent ions and strontium fluoride. A method as claimed in claim 1 or claim 2 in which the leachable source of polyvalent metal ions is an acid-leachable glass, preferably a calcium aluminofluorosilicate glass. A method as claimed in any one of the preceding claims in which the polymer containing free carboxyl groups is a homopolymer or copolymer of acrylic acid, preferably having a molecular weight of from 35,000 to 70,000. Use of a radioopaque cross-linked cement formed by the method claimed in any one of the preceding claims for the preparation of a base, liner or subfilling for an overlying filler formed from a composite dental composition comprising one or more ethylenically unsaturated compounds, a particulate filler and a polymerisation initiator for the ethylenically unsaturated compound(s), for dental restoration. A radioopaque dental restorative material comprising a polymerized matrix containing strontium fluoride which provides substantially all radioopaque properties in the matrix. A restorative material as claimed in claim 6 in which the polymerized matrix is formed from a composite composition comprising one or more ethylenically unsaturated compounds, a particulate filler and polymerization initiator. A restorative material as claimed in claim 6 in which the polymerized matrix is a polyacrylate dental cement. A radioopaque resinous structure containing strontium fluoride as a radioopacifying agent. A structure as claimed in claim 9 in which strontium fluoride provides substantially all the radioopaque properties in the resin. A structure as claimed in claim 10, in which strontium fluoride is substantially the only radioopacifying agent. A structure as claimed in any one of claims 9 to 11 having a radioopacity of at least 1.0 mm of aluminium per mm of structure, preferably at least 1.5 aluminium per mm of structure. A structure as claimed in any one of claims 9 to 12 which is substantially translucent.

Inventors: BILLINGTON RICHARD WILLIAM, WILLIAMS JILL ANN, BILLINGTON, RICHARD WILLIAM, WILLIAMS, JILL ANN
Applicants: DENTSPLY LTD, DENTSPLY INTERNATIONAL, INC.
Application year: 1987
Main classification: A61K6
IPC codes: G21F1, A61K6, C08K3, C08F8, C08L33, C04B28, C04B22, C08L101