A MAGNETIC RECORDING MEDIUM

Abstract: A magnetic recording medium is formed by depositing a layer of a cobalt-platinum magnetic alloy (which may also contain chromium) on a non-magnetic underlayer consisting of tungsten, molybdenum, niobium or vanadium. The magnetic alloy has a higher coercivity than when deposited on a chromium underlayer. The coercivity of the magnetic alloy becomes even higher when the substrate is maintained within such a temperature range during deposition of the magnetic alloy that an intermetallic compound of cobalt and the metal of the underlayer is formed at the interface between the magnetic alloy layer and the underlayer.

Description: This invention relates to a magnetic recording medium. Various alloys of cobalt and platinum have been used as the magnetic material in thin film magnetic recording disks for horizontal recording. In such disks, the hexagonal close packed (HCP) crystalline structure of the cobalt-platinum (CoPt) alloy is formed on the substrate, or on an intermediate underlayer, so that the C-axis, i.e. the [002] axis, of the CoPt film is either in the plane of the film or has a component in the plane of the film. The coercivity (H c ) of CoPt films is dependent upon the composition of the alloy, with the maximum H c occurring at approximately 20 atomic percent (at.%) platinum. See J. A. Aboaf, et al., "Magnetic Properties and Structure of Co-Pt Thin Films", IEEE Trans on Magnetics, MAG-19, 1514 (1983), and M. Kitada, et al., "Magnetic Properties of Sputtered Co-Pt Thin Films", J. Appl. Phys. 54 (12), December 1983, pp. 7089-7094. The coercivity and other properties of cobalt-platinum films have been reported by Opfer, et al. in an article entitled "Thin-Film Memory Disc Development," Hewlett-Packard Journal , November 1985, pp. 4-10. A thin film disk with a cobalt-platinum-chromium (CoPtCr) magnetic layer, wherein Cr is added to improve the corrosion resistance of the magnetic layer, is described in Japanese published patent application 198568. The CoPtCr magnetic layer is deposited onto a nickel-phosphorus (NiP) film formed on a suitable substrate. In order to improve the coercivity of the CoPt magnetic film in certain types of disks, a chromium (Cr) underlayer is often formed between the substrate and the CoPt magnetic layer. The use of a chromium underlayer in a CoPt thin film disk is described in the above referenced article by Opfer, et al. and in EP -A- 145157. The use of tungsten (W) as an enhancement layer in certain types of thin film disks for horizontal recording has been suggested in an article by Dubin, et al. in "Degradation of Co-based Thin-film Recording Materials in Selected Corrosive Environments," J. Appl. Phys. 53(3), March 1982, pp. 2579-2581. The Dubin, et al. article states that a 100 nm thick underlayer of tungsten is used to promote epitaxial crystal growth in magnetic layers of cobalt-nickel-tungsten (CoNiW) and cobalt-nickel (CoNi). In Japanese unexamined published patent application 59-227107, a magnetic recording medium is described in which the magnetic film contains cobalt, platinum and tungsten, with platinum comprising between 4 and 15 at.% and tungsten comprising between 0.5 and 8 at.% of the CoPtW alloy. This Japanese document indicates that greatly improved coercivity is obtained by adding tungsten to the cobalt-platinum alloy. EP -A- 140513 suggest various combinations of underlayers and magnetic layers as structures for horizontal magnetic recording, including a CoPt magnetic layer formed on a nonmagnetic layer of a WCo alloy. According to one aspect, the invention provides a magnetic recording medium comprising a layer of a cobalt-platinum magnetic alloy formed on a non-magnetic underlayer on a substrate, characterised by: an intermetallic compound interface between the magnetic alloy layer and the underlayer, the underlayer consisting of tungsten, molybdenum, niobium or vanadium, and the intermetallic compound being a compound of cobalt and the metal of the underlayer. According to another aspect, the invention provides a method of making a magnetic recording medium comprising the steps of sputter depositing a non-magnetic underlayer on a suitable substrate and sputter depositing a layer of a cobalt-platinum magnetic alloy on the underlayer, characterised in that: the underlayer consists of tungsten, molybdenum, niobium or vanadium; and the substrate is maintained within such a temperature range while the magnetic alloy is deposited that an intermetallic compound consisting of cobalt and the metal of the underlayer is formed at the interface of the underlayer and the layer of magnetic alloy. With the use of a tungsten underlayer and the deposition of the underlayer and magnetic layers in a manner so as to form an intermetallic compound of cobalt and the metal of the underlayer in the interface region, the coercivity of CoPt or CoPtCr layers can be increased, or alternatively, the same coercivity can be achieved with less platinum. How the invention can be carried out will now be described by way of example, with reference to the accompanying drawings, in which:- Fig. 1 represents M-H hysteresis loops of a CoPt film formed on a tungsten underlayer and a CoPt film formed on a chromium underlayer; Fig. 2 is a graphical representation of the coercivity of CoPt films of various thicknesses deposited on tungsten and chromium underlayers at various substrate deposition temperatures; Fig. 3 is an X-ray diffraction curve for a CoPt film deposited on a tungsten underlayer wherein the interfacial region between the tungsten and the CoPt layer is an intermetallic compound of Co₃W; and Fig. 4 is an X-ray diffraction curve for a CoPtCr film deposited on a tungsten underlayer wherein the interfacial region between the tungsten and the CoPtCr layer is an intermetallic compound of Co₃W. In order to illustrate the improved coercivity of a CoPt disk embodying the present invention, a CoPt disk was first made with a chromium underlayer between the substrate and the CoPt magnetic layer. A chromium underlayer 100 nm thick was deposited by DC magnetron sputtering onto a silicon substrate at an Argon pressure of 0.43 Pa (3.2 × 10⁻³ Torr) and a substrate temperature of 128°C. Thereafter, a 40 nm thick cobalt-platinum alloy film with 20 at.% platinum (Co₈₀Pt₂₀) was sputter deposited onto the chromium underlayer without breaking vacuum in the sputtering chamber. Curve A in Fig. 1 is an M-H hysteresis loop for this film which has a coercivity H c of 105 kA.m⁻¹ (1320 Oersteds (Oe)) and a squareness S of .887. Curve B is an M-H loop for a cobalt-platinum film of similar thickness deposited onto a tungsten underlayer. A 100 nm thick tungsten underlayer was deposited by DC magnetron sputtering onto a silicon substrate with the substrate maintained at a temperature of 38°C. Thereafter, without breaking vacuum in the sputtering chamber, a 42.5 nm, thick Co₈₀Pt₂₀ film was sputter deposited onto the tungsten underlayer. The resulting M-H hysteresis loop (Curve B of Fig. 1) for this film has a coercivity of 171 kA.m⁻¹ (2145 Oe) and a squareness S of .864. The same Co₈₀Pt₂₀ sputtering target was used for the two disks whose data is depicted in Fig. 1. Cobalt-platinum films of various thicknesses were formed on tungsten underlayers at various substrate deposition temperatures, and the magnetic properties of these films were compared with cobalt-platinum films formed on chromium underlayers. As shown by Curve A in Fig. 2, the various experimental samples had Co₈₀Pt₂₀ thicknesses ranging between approximately 24 and 64 nm and were sputter deposited onto 100 nm thick tungsten underlayers while the silicon substrate temperature was maintained between approximately 30 and 40°C. The coercivity values for such films were substantially greater than the coercivity of Co₈₀Pt₂₀ films deposited onto 100 nm thick chromium underlayers while the silicon substrate temperature was maintained at approximately 128°C, as shown by Curve C in Fig. 2. (The coercivity of the Si/100 nm, Cr/40 nm Co₈₀Pt₂₀ disk of Fig. 1 is significantly less than the corresponding disk in Curve C of Fig. 2 because the latter was made with a different Co₈₀Pt₂₀ sputtering target, which may have had slight variations in composition). When the temperature of the silicon substrate was increased from approximately 30 to 40°C to 128°C and Co₈₀Pt₂₀ films of the same thickness range were deposited onto the 100 nm thick tungsten underlayers, the resulting coercivities were substantially reduced, but still substantially higher than for the CoPt samples formed on chromium underlayers. (See Curve B in Fig. 2.) In order to understand the difference in coercivity of the Co₈₀Pt₂₀ films depicted by Curves A and B in Fig. 2, an X-ray diffraction analysis was performed on the silicon disks with the Co₈₀Pt₂₀ film deposited onto the tungsten underlayers. The X-ray diffraction curve of Fig. 3 is for a silicon disk with a 100 nm thick W underlayer and a 62.5 nm thick Co₈₀Pt₂₀ magnetic layer deposited at a silicon substrate temperature of 38°C. Fig. 3 depicts a peak intensity at 2ϑ equal to 42.62 degrees, which corresponds to the (002) plane of the HCP Co₈₀Pt₂₀ magnetic film and a peak intensity at 2ϑ equal to 39.7 degrees, which corresponds to the (110) plane of the body-centred-cubic (BCC) tungsten underlayer. In addition, a peak intensity at 2ϑ equal to 35.25 degrees corresponds to the (110) plane of the HCP Co₃W intermetallic compound. This peak in Fig. 3 confirms that an intermetallic compound phase of cobalt and tungsten is present at the interfacial region between the Co₈₀Pt₂₀ and W layers. The (110) reflection for the HCP Co₃W implies that a component of the C-axis [002] of the Co₃W is in the plane of the film. The (110) reflection for Co₃W was not detected in an X-ray diffraction analysis of Co₈₀Pt₂₀ films on tungsten underlayers deposited at 128°C (i.e. those disks whose data is shown by Curve B in Fig. 2). Thus, the results shown in Fig. 3 indicate that the relatively low temperature deposition of Co₈₀Pt₂₀ on a tungsten underlayer causes an interfacial reaction between Co and W, which results in a highly oriented hexagonal Co₃W phase at the interface. This interface enhances the C-axis orientation of the Co₈₀Pt₂₀ film in the plane of the film. A thin film disk with a 62.5 nm thick (Co₉₀Pt₁₀)₈₀Cr₂₀ magnetic layer deposited onto a 100 nm thick W underlayer on a silicon substrate also showed excellent magnetic properties. This disk was formed by DC magnetron sputtering using separate Co₉₀Pt₁₀ and Cr targets at a substrate temperature of 28°C. The disk had H c = 77.2 kA.m⁻¹ (970 Oe), coercivity squareness S* = 0.89 and a remanance-thickness product Mr·t = 1.68 x 10⁻² A (1.68 × 10⁻³ emu/cm²). The X-ray diffraction analysis of this disk is shown in Fig. 4 and depicts a strong peak intensity at 2ϑ = 35.16°C, which corresponds to the (110) plane of the Co₃W interface region, thereby confirming the formation of the Co₃W interface between the W underlayer and (Co₉₀Pt₁₀)₈₀Cr₂₀ magnetic layer. As used herein the term "intermetallic compound" refers to those chemical compositions which are more than a simple mixture in the form of an alloy, but in which the constituents are present in a fixed stoichometric ratio so that the composition can be represented by a chemical formula. An intermetallic binary compound of two elements, such as cobalt and tungsten, is an intermediate phase which exists only at the discrete stoichometric ratio of three atoms of cobalt to one atom of tungsten. The Co₃W intermetallic compound is indicated on the published phase diagrams for cobalt and tungsten, such as in Constitution of Binary Alloys , McGraw Hill, 1958, p. 519. In all the experimental examples described herein the substrate was semiconductor grade single-crystal silicon. When a silicon substrate is used, an underlayer is required to cause the C-axis orientation of the magnetic layer to be in the plane of the film. The tungsten underlayer in recording media embodying the present invention serves this purpose. When the substrate is another material, such as a nickel-phosphorus (NiP) film formed on an aluminium alloy disk, however, an underlayer may not be absolutely necessary but only beneficial to improve the in-plane C-axis orientation of the magnetic layer. The tungsten underlayer enhances the in-plane C-axis orientation of the magnetic layer and thereby improves the magnetic properties of the thin film disk when the substrate is a NiP film on an aluminium alloy disk. While the experimental examples described herein were limited to the use of tungsten as the underlayer, other refractory metals such as niobium (Nb), molybdenum (Mo), and vanadium (V) would enhance the orientation of the CoPt and CoPtCr film because such metals are known to form HCP intermetallic compounds with cobalt. These compounds are, respectively, Co₂Nb, Co₃Mo and Co₃V. The above description relates only to the formation of the magnetic layer and underlayer on the substrate and not to the well known aspects of the media and the media fabrication processes. For example, in the fabrication of thin film metal alloy disks it is known to provide a protective overcoat, such as a sputtered, essentially amorphous carbon film, over the magnetic layer and in certain instances to provide an adhesion layer, such as a sputtered film of titanium, between the overcoat and the magnetic layer.

Claims: A magnetic recording medium comprising a layer of a cobalt-platinum magnetic alloy formed on a non-magnetic underlayer consisting of tungsten, molybdenum, niobium or vanadium on a substrate, characterised by: an intermetallic compound interface between the magnetic alloy layer and the underlayer, the intermetallic compound being a compound of cobalt and the metal of the underlayer. A magnetic recording medium as claimed in claim 1, in which the underlayer is of tungsten and the intermetallic compound interface consists of Co₃W. A magnetic recording medium as claimed in claim 1 or claim 2, in which the magnetic alloy also contains chromium. A magnetic recording medium as claimed in any preceding claim, in which the substrate is of silicon. A magnetic recording medium as claimed in any of claims 1 to 3, in which the substrate consists of an aluminium alloy having a nickel-phosphorus film formed thereon beneath the underlayer. A magnetic recording medium as claimed in any preceding claim, further comprising a protective overcoat formed over the layer of magnetic alloy. A method of making a magnetic recording medium comprising the steps of sputter depositing a non-magnetic underlayer consisting of tungsten, molybdenum, niobium or vanadium on a suitable substrate and sputter depositing a layer of a cobalt-platinum magnetic alloy on the underlayer, characterised in that: the substrate is maintained within such a temperature range while the magnetic alloy is deposited that an intermetallic compound consisting of cobalt and the metal of the underlayer is formed at the interface of the underlayer and the layer of magnetic alloy. A method as claimed in claim 7, in which the underlayer is formed by depositing tungsten and the interface consists of the compound Co₃W. A method as claimed in claim 7 or claim 8, further comprising forming a protective overcoat over the later of magnetic alloy. A method as claimed in any of claims 7 to 9, in which the sputter-deposited magnetic alloy also contains chromium.

Inventors: AHLERT, RICHARD HENRY, HOWARD, JAMES KENT, LIM, GRACE SU
Applicants: INTERNATIONAL BUSINESS MACHINES CORPORATION
Application year: 1987
Main classification: G11B5
IPC codes: G11B5