METHOD OF MANUFACTURING A SEMICONDUCTOR DEVICE OF THE "SEMICONDUCTOR ON INSULATOR" TYPE

Abstract: In a method of manufacturing a semiconductor device of the "semiconductor on insulator" type comprising at least one carrier body and a monocrystalline semi­ conductor body, in a major surface (2) of a monocrystalline semiconductor body (1) grooves (3) are provided having a predetermined depth. The surface provided with grooves is coated with a layer (4) of material resistant to polishing; this layer is coated with a layer (5) of a chemomechanically polishable material having a layer thickness exceeding the groove depth, the latter layer (5) being polished to flatness and smoothness. The polished surface of the semiconductor body (1) is con­ nected to a smooth flat major surface of a carrier body (6). Subsequently, the semiconductor body (1) is made thin, at least the last part of this operation consisting of a polishing step, which terminates on the layer (4) of material resistant to polishing so that mutually insulated "semiconductor on insulator" regions are obtained, the thickness of the semiconductor regions being equal to the depth of the grooves.

Description: The invention relates to a method of manufacturing a semiconductor device of the "semiconductor on insulator" type comprising at least one carrier body and a monocrystalline semiconductor body, both bodies being provided with at least one flat optically smooth surface, the flat surfaces of the said two bodies being brought into contact with each other and being interconnected, while at least one of the interconnected surfaces has an electrically insulating layer, after which the semiconductor body is made thin by removing material to a predetermined value. Such a method is known from "Applied Physics Letters", Vol. 43, No. 3, August 1983, p. 263-265. In this known method, the semiconductor body is made thin by means of electrochemical thin-etching. The etchants used for this purpose generally comprise hydrofluoride as one of the constituents. These HF-containing etchants attack not only the silicon frequently used as semiconductor material, but also the silicon dioxide frequently used as insulator. Moreover, parts of the semiconductor body subjected to mechanical stress can be preferentially attacked by such etchants. Furthermore, chemical etchants must be treated with great care in order to avoid environmental pollution. If further insulated regions should be obtained in the thin-etched semiconductor layer, a number of further processing steps must be carried out in the known method. The invention has for its object to provide a method of the kind mentioned in the opening paragraph, in which disadvantages inherent in electrochemical etching are avoided, in which the layer thickness of the thin-etched semiconductor body is controlled accurately and in which simultaneously mutually insulated regions can be obtained in the thin semiconductor layer without further complicated processing steps being required. In order to achieve this end, in the method according to the invention, grooves having a depth equal to the desired value of the layer to be made thin are provided in a surface of the monocrystalline semiconductor body, the surface provided with grooves is coated with a layer of material resistant to polishing, the latter layer is coated with a layer of a material which can be polished chemo-mechanically and has a layer thickness exceeding the groove depth, the said layer being polished to smoothness and flatness, after which the polished surface of the semiconductor body is connected to the smooth flat surface of the carrier body, and the semiconductor body is then made thin, at least the last part of this operation consisting of a polishing operation terminating on the layer of material resistant to polishing. Thus, a "semiconductor on insulator" is obtained, in which very reproducible and a thin semiconductor layer is obtained, which is subdivided into a plurality of insulated regions. In a preferred embodiment of a method according to the invention, the operation of polishing to flatness the chemomechanically polishable material applied to the surface provided with grooves of the semiconductor body is continued down to the layer of material resistant to polishing. The thickness of the semiconductor layer on the insulator is then determined exactly because both before and after the semiconductor body is connected to the carrier body a polishing operation is carried out, which terminates on the layer resistant to polishing, which is formed in the surface provided with grooves. The layer resistant to polishing may preferably consist of silicon nitride (Si₃N₄) or of a densified silicon dioxide (SiO₂). The chemomechanically polishable material can consist according to the invention of an undensified silicon dioxide. Other materials, such as polycrystalline silicon, are also suitable. In the latter case, a layer resistant to polishing of a denisfied silicon dioxide may be provided between the layer of polycrystalline silicon and the layer resistant to polishing of a densified silicon dioxide may be provided between the layer of polycrystalline silicon and the layer resistant to polishing of silicon nitride. An insulating layer of very high quality is then obtained. The semiconductor device obtained by means of the method according to the invention is particularly suitable for forming a tridimensional IC structure. For this purpose, according to the invention, IC structures are provided in a thin semiconductor layer, as a result of which the surface exhibits embossed parts, while chemomechanically polishable material is deposited on the surface, this material being planarized, for example, by means of polishing, until an insulating layer of small thickness is present above the semiconductor structures, this assembly being a first register which forms the carrier body, on which a second semiconductor body is provided in the manner indicated in Claim 1, the thin semiconductor layer of IC structures forming a second register and any further analogous steps being carrier out for forming a tridimensional stack of IC's. It is noted that it is known per se from "IBM TDB, Vol. 16,no. 9, Feb. 1974, p.2869-2870" to form islands of silicon by polishing back a silicon body down to a layer resistant to polishing. The invention will be described more fully with reference to the drawing. In the drawing: Fig. 1 shows a semiconductor body provided with at least one flat and smooth major surface, Fig. 2 shows the semiconductor body provided with grooves, Fig. 3 shows the semiconductor body coated with a layer resistant to polishing, Fig. 4 shows the semiconductor body of Fig. 3, on which a layer of a polishable material is provided, Fig. 5 shows the semiconductor body of Fig. 4, the layer of polishable material being polished to flatness and smoothness, Fig. 6 shows the semiconductor body of Fig. 4, the operation of polishing to flatness and smoothness being continued down to the layer resistant to polishing, Fig. 7 shows the semiconductor body of Fig. 6 connected to a carrier body, Fig. 8 shows the combination of Fig. 7, in which the semiconductor body is made thinner, Fig. 9 shows the combination of Fig. 8, in which the thinning operation is terminated by a stopping polishing down to the layer resistant to polishing, and Fig. 10 shows a tridimensional stack of IC's. The method of obtaining a "semiconductor on insulator" is shown in steps in Figures 1 to 9. Fig. 1 shows a semiconductor body 1, of which at least the major surface 2 is made flat and smooth, Grooves 3 are provided in the semiconductor body, which consists, for example, of silicon, at the area of the major surface 2, for example by means of etching. The depth of these grooves depends upon the desired layer thickness of the ultimate semiconductor layer on the "semiconductor on insulator" to be formed. The grooves 3 are covered by a layer 4 resistant to polishing of an insulating material (cf. Fig. 3). The material of the layer 4 may be silicon nitride (Si₃N₄); other suitable materials may also be used, such as a densified silicon dioxide obtained by deposition from tetra-ethyl orhosilicate (TEOS) and a subsequent annealing treatment. The thickness of the layer 4 is preferably a few hundreds of nanometres. The semiconductor wafer thus prepared is coated on the surface provided with grooves with a chemomechanically polishable material 5 having a layer thickness larger than the depth of the grooves 3. The layer 5 shown in Fig. 4 may consist of polycrystalline silicon, which is applied, for example, by means of LPCVD (Low Pressure Chemical Vapour Deposition). Another suitable material is an undensified silicon dioxide obtained by deposition from tetraethyl orthosilicate (TEOS). This layer 5 is polished to flatness chemomechanically. This operation can be continued until a layer of polishable material is still present on the whole major surface 2 (cf. Fig. 5), or the polishing treatment is continued down to the layer 4 resistant to polishing, indicated by stopping polishing (cf. Fig. 6). This chemomechanical polishing operation is a polishing operation, in which use is made, for example, of colloidal silicon dioxide in an alkaline solution with an oxidant, such as, for example, the polishing agent marketed under the trade-name of Syton W 30 by Monsanto. In order to form a "semiconductor on insulator", the semiconductor body is now secured on a carrier body. Fig. 7 shows the semiconductor body of Fig. 6 connected to a carrier body 6. The carrier body shown is formed from monocrystalline silicon, of which a major surface is provided with an insulating layer 7 of thermally grown silicon dioxide having a thickness of, for example, 1 µm. Another material, for example quartz glass, may also be chosen for the carrier body. Various techniques may be used to connect the carrier body 6 to the semiconductor body 1. Very favourable is a connection established by wringing, i.e. an optimized van der Waals connection (cf. for example EP 137537). A flow glass connection is also possible of the kind described in "Applied Physics Letters" 43, August 1983, p. 263-265. A further possibility is impact diffusion, as described in EP 1219. Somewhat more complicated is the anodic connection step (see Journal of Applied Physics, 58(3), 1 August 1985, p. 1240-1247) The semiconductor body 1 is now made thin, This may be effected in a number of steps. Preferably, all these steps consist, but at any rate the last step consists of a chemomechanical polishing operation and a stopping polishing treatment is carried out down to the layer 4 resistant to polishing. For this purpose, the aforementioned polishing agent may again be used. Figures 8 and 9 show a few steps. Fig. 9 shows the "semiconductor on insulator". Due to the fact that the grooves are provided and stopping polishing is carried out down to the layer 4, mutually insulated semiconductor regions are obtained, of which the thickness of accurately determined. For example, integrated circuits may be provided in these regions. The thickness of the semiconductor regions may be 0.1 to 3 µm for many applications. For example for power IC's, a larger thickness, for example 5 µm, is preferably chosen. These values are obtained automatically in the method according to the invention by the choice of the groove depth. In a favourable embodiment, in which the layer 4 resistant to polishing consists of silicon nitride (Si₃N₄) and the chemomechanically polishable material consists of polycrystalline silicon, a layer of densified silicon dioxide may be provided between these layers in order to obtain an extraordinarily good electrical and chemical insulation, the silicon nitride acting as a very good chemical insulator and the silicon dioxide acting as a very good electrical insulator. The "semiconductor on insulator" shown in Fig. 9 is particularly suitable to be used for forming a tridimensional stack of IC's. Fig. 10 shows an example thereof. Integrated circuits are provided in the semiconductor layer 1 of the "semiconductor on insulator" formed, which is subdivided into individual regions. As a result, embossed parts are formed in this layer. The whole major surface is now provided with an electrically insulating layer, for example of silicon dioxide, and this layer is planarized. This body now serves as a carrier body, on which a second semiconductor body is placed. The second semiconductor body may be formed in the manner indicated in Fig. 6. After this second semiconductor body has been connected to the "semiconductor on insulator" provided with a planarized layer, the semiconductor layer of the second semiconductor body is made thin. At any rate, the last processing step consists of stopping polishing. Semiconductor structures may also be provided in this second semiconductor layer. If desired, further semiconductor bodies may be provided in order to obtain a tridimensional stack of IC's comprising a desired number of registers.

Claims: A method of manufacturing a semiconductor device of the "semiconductor on insulator" type, in which a monocrystalline semiconductor body (1) and a carrier body (3) are provided with at least one flat, optically smooth surface, at least one of both bodies bearing an electrically insulating layer at its flat surface, both bodies are interconnected with their flat surfaces brought into contact with each other, and the semiconductor body (1) is made thin to a desired thickness by removing material to a predetermined extent, characterized in that grooves (3), having a depth equal to the desired thickness of the semiconductor body (1), are provided at a major surface (2) of the semiconductor body (1), the surface (2) provided with the grooves is coated with a layer (4) resistant to polishing, the layer (4) resistant to polishing is coated with a layer (5) of chemomechanically polishable material having a thickness exceeding the groove depth, the layer (5) of chemomechanically polishable material is polished flat and smooth, the semiconductor body (1) is interconnected with its major surface (2) to the carrier body (3), and the semiconductor body is subsequently made thin by an operation of which at least the last stage consists of a polishing step terminating on the layer (4) resistant to polishing. A method as claimed in claim 1 characterized in that the layer (5) of chemomechanically polishable material is polished down to the layer (4) resistant to polishing. A method as claimed in claim 1 or 2 characterized in that the layer (4) resistant to polishing comprises silicon nitride. A method as claimed in claim 1 or 2 characterized in that the layer (4) resistant to polishing comprises densified silicon oxide. A method as claimed in any one of the preceding claims characterized in that the chemomechanically polishable material consists of undensified silicon oxide. A method as claimed in any of claims 1 to 4 characterized in that the chemomechanically polishable material consists of polycrystalline silicon. A method as claimed in claim 6 in combination with claim 3, characterized in that a layer of densified silicon dioxide is provided between the chemomechanically polishable layer (5) of polycrystalline silicon and the layer (4) resistant to polishing. A method as claimed in any one of the preceding claims, characterized in that IC structures are provided in the semiconductor body (1) at a surface of it, as a result of which the surface exhibits embossed parts, chemomechanically polishable, insulating material is deposited on said surface and is subsequently planarized until only a thin insulating layer is left above the IC structures, the assembly forms a first register and is used as a carrier body on which another semiconductor body is provided in the manner indicated in claim 1, said other semiconductor body is provided with IC structures to form a second register and any further analogous steps are performed in order to form a tridimensional stack of IC's.

Inventors: ALEXANDER, ELIZABETH MARIA LEONTINA, HAISMA, JAN, MICHIELSEN, THEODORUS MARTINUS, VAN DER VELDEN, JOHANNES WILHELMUS ADRIANUS, VERHOEVEN, JOHANNES FRANCISCUS CORNELIS MARIA
Applicants: N.V. PHILIPS' GLOEILAMPENFABRIEKEN
Application year: 1987
Main classification: H01L21
IPC codes: H01L21, H01L27