AROMATIC DICARBOXYLIC ACID DIALLYL ESTER DERIVATIVE, PREPOLYMER DERIVED FROM THE DERIVATIVE AND CURABLE RESIN COMPOSITION CONTAINING THE DERIVATIVE

Abstract: A diallyl aromatic dicarboxylate derivative of the formula wherein Y is a hydrogen atom or a perfluoroalkenyl group having 6 to 14 carbon atoms, is a novel compound. The compound (1) is a starting material for a prepolymer containing a repeating unit derived from diallyl aromatic fluorine-containing dicarboxylate and represented by the formula wherein X is a perfluoroalkenyl group having 6 to 14 carbon atoms. Further, the present invention provides a curable resin composition which comprises a prepolymer having at least one carbon-carbon double bond in the molecule and diallyl aromatic fluorine-containing dicarboxylate represented by the formula

Description: The present invention relates to an aromatic dicarboxylic acid diallyl ester derivative, prepolymer derived from the derivative and curable resin composition containing the derivative. It is known that a hexafluoropropene oligomer is reacted with 4-hydroxyphthalic acid or 5-hydroxyisophthalic acid to obtain a corresponding [perfluoroalkenyloxy](iso)phthalic acid (Japanese Unexamined Patent Publication Nos. 140,951/1981 and 51,146/1985). Further, also is known a dialkyl ester of 4-perfluoroalkenyloxyphthalic acid (Japanese Unexamined Patent publication No. 24,547/1986). However, these compounds have no double bond in the molecule and cannot polymerize alone or with other compounds having a double bond. Diallyl aromatic dicarboxylate such as diallyl phthalate is a monomer having two polymerizable functional groups and is used for preparing a thermosetting resin. In a molding process for obtaining a desired molded article by polymerizing such a monomer having at least two polymerizable functional groups to a polymer, it is usually conducted to suspend the polymerization reaction to obtain a polymer having a solubility in solvent or thermoplasticity. The polymer is molded in the form of a solution or a thermoplastic resin and then polymerized after molding or with molding at the same time to a cured resin which is neither soluble in solvent nor molten. In the above, the polymer having a solubility or thermoplasticity is called a prepolymer. A cured article of a conventional prepolymer such as diallyl phthalate is useful as a socket, connector and like electric parts, laminates, decorative sheets, etc., but has a defect of being poor in water-resistance. Further, various curable resin compositions are conventionally known and are used for ink, varnish, coating composition, adhesive, FRP, molded article and the like. An epoxy acrylate resin is excellent in adhesion to various kinds of substrates but is inferior in water-resistance. Further, an unsaturated polyester has a defect of being insufficient in water-resistance. An object of the invention is to provide a novel aromatic dicarboxylic acid diallyl ester derivative and process for preparing the same; the derivative has a double bond and can polymerize by itself or with other compounds having a double bond. Another object of the invention is to provide a novel prepolymer derived from diallyl aromatic dicarboxylate which affords a cured product having an excellent water-resistance. Still another object of the invention is to obviate the above-mentioned defects and to provide a curable resin composition which hardens by heating or irradiation of active energy rays to give a cured article having an excellent water-resistance. The present invention provides a diallyl aromatic dicarboxylate derivative of the formula wherein Y is a hydrogen atom or a perfluoroalkenyl group having 6 to 14 carbon atoms. The above diallyl aromatic dicarboxylate derivative includes all isomers in which one 2-propenyloxycarbonyl group is bonded to ortho, meta or para position of the other 2-propenyloxycarbonyl group. Examples of perfluoroalkenyl groups Y having 6 to 14 carbon atoms of the invention are the following groups of the formulae wherein R¹, R² and R³ are each a perfluoroalkyl group having 1 to 6 carbon atoms, or one of them is a fluorine atom and the others are each a perfluoroalkyl group having 1 to 6 carbon atoms, R⁴ is a perfluoroalkyl group having 1 to 5 carbon atoms. Especially preferable are groups formed by eliminating one fluorine atom from a dimer or trimer of hexafluoropropene, or tetramer, pentamer, hexamer or heptamer of tetrafluoroethylene. These groups are shown below by the formulae. In the invention, the compound (3) of the formula is novel and is prepared, for example, by reacting a perfluoroalkene XF with a hydroxy aromatic dicarboxylic acid derivative of the formula In the above, X is perfluoroalkenyl group having 6 to 14 carbon atoms. The above compound (2) is novel and is obtained, for example, by esterifying hydroxyphthalic acid with allyl alcohol in the presence of a catalyst. In the reaction, allyl alcohol is used preferably in an amount of about 2 to 40moles per mole of hydroxyphthalic acid. As a catalyst concentrated sulfuric acid, p-toluenesulfonic acid, boron trifluoride ethyl etherate, etc. are used. The reaction temperature is preferably about 50 to 200°C, the reaction time is suitably determined and is generally about 30 minutes to 20 hours. The reaction pressure is not particularly limited. The reaction is conducted preferably in a solvent. A prefered solvent is one which forms an azeotrope with water and is substantially immiscible with water. Examples thereof are benzene, toluene, xylene, diallyl ether, etc. The obtained compound (2) can be pyrified by a known method such as concentration, extraction, distillation, chromatography, etc. but can be reacted without purification with the perfluoroalkene XF in a next process. Examples of perfluoroalkenes XF are the following compound of the formula wherein R¹, R² and R³ are each perfluoroalkyl group having 1 to 6 carbon atoms, or one of them is fluorine atom and the others are each perfluoroalkyl group having 1 to 6 carbon atoms. Especially preferable are a dimer or trimer of hexafluoropropene, or tetramer, pentamer, hexamer or heptamer of tetrafluoeroethylene. These are shown below by the formulae. The reaction is conducted preferably in a solvent in the presence of a base. Examples of bases are triethylamine, trimethylamine, tripropylamine or like amines, alkali metal or hydroxides thereof, etc. A prefered solvent is an aprotic polar solvent such as acetonitrile, dimethyl formamide, dimethyl sulfoxide, etc. The perfluoroalkene is used preferably in an amount of about 1 to 10moles per mole of the compound (2). The reaction temperature is suitable selected but is usually about 0 to 40°C, preferably about 0 to 20°C. The base is used preferably in an amount of about 2 to 20moles per mole of the compound (2). The desired compound (3) can be separated and recovered by known methods used in the separation of a mixture of organic compounds containing solid dissolved in liquid. For example, the reaction mixture is added to a large amount of diluted hydrochloric acid and the resulting precipitates are collected and is distilled at a reduced pressure to obtain the desired compound. The compounds XF of the formula (5) include compounds represented by the formulae below. From the above compounds, the following groups are produced respectively. More specifically, from the compound the following group is formed. Further, the compound (1) can also be prepared by reacting an allyl alcohol with an aromatic dicarboxylic acid of the formula wherein Y is hydrogen atom or perfluoroalkenyl group having 6 to 14 carbon atoms. The compound (4) is a known compound. The reaction is conducted preferably in a solvent. As a solvent is preferably used one which make an azeotrope with water and is substantially immiscible with water. Examples thereof are benzene, toluene, xylene, diallyl ether, etc. Allyl alcohol is used preferably in an amount of about 2 to 10moles per mole of the compound (4). The reaction temperature is suitably selected but is usually about 50 to 200°C, preferably about 70 to 160°C. The desired compound (1) can be separated and recovered by known methods used in the separation of a mixture of organic compounds containing solid dissolved in liquid. For example, the desires compound (1) can be recovered by concentration, distillation, gas chromatography, etc. The compound (1) can be polymerized by heating in the presence of a peroxide such as benzoyl peroxide, thereby a polymer (prepolymer) having a double bond is prepared. The prepolymer can be cured to resin by heating or with irradiation of light, electron rays or like active energy rays and the cured product is excellent in water-resistance. Thus, the present invention provides a prepolymer containing a repeating unit derived from diallyl aromatic fluorine-containing dicarboxylate and represented by the formula wherein X is prefluoroalkenyl group having 6 to 14 carbon atoms. Examples of X are same as described above. In the invention, the repeating unit of the formula (6) is derived from diallyl fluorine-containing dicarboxylate which is a monomer of the above prepolymer and is represented by the formula The compound (3) may convert, in some case, into a repeating unit of the formula In the present invention, it is probable that a small amount of the above repeating unit(s) be present. The present prepolymer includes a copolymer having the repeating unit of the formula (6) and an other repeating unit. Examples of other repeating units are those derived from cleavage of double bond of various compounds such as ethylene, vinyl acetate, vinyl fluoride, vinyl chloride, acrylamide, methacrylamide, styrene, α-methylstyrene, p-methylstyrene, alkyl ester of acrylic acid or methacrylic acid, benzyl (meth)acrylate, vinyl alkyl ether, halogenated alkyl vinyl ether, vinyl alkyl ketone, cyclohexyl (meth) acrylate, maleic anhydride, butadiene, isoprene, chloroprene, diallyl phthalate, diallyl isophthalate, diallyl terephthalate, etc. The prepolymer has a molecular weight ( M n) preferably of about 1000 to 50000, more preferably about 3000 to 10000 and an iodine value (gram of iodine which adducts to 100g of sample) preferably of about 10 to 95, more preferably about 25 to 80. With a too high molecular weight, the gelled polymer is hard to process. With a too small molecular weight, the cured product does not have practical strength. The prepolymer having too small iodine value cannot afford a cured product having practical strength. A cured product having inferior impact-resistance is obtained from the prepolymer having a too large iodine value. The prepolymer is prepared by polymerizing the compound (3) or copolymerizing it with a comonomer. Examples of useful comonomers are various compound such as ethylene, vinyl acetate, vinyl fluoride, vinyl chloride, acrylamide, methacrylamide, styrene, α-methylstyrene, p-methylstyrene, alkyl ester of acrylic acid or methacrylic acid, benzyl (meth)acrylate, vinyl alkyl ether, halogenated alkyl vinyl ether, vinyl alkyl ketone, cyclohexyl (meth)acrylate, maleic anhydride and like ethylenic compounds, butadiene, isoprene, chloroprene and like conjugated diene compounds, diallyl phthalate, diallyl isophthalate, diallyl terephthalate and like non-conjugated diene compounds, etc. The prepolymer contains the repeating unit (6) in an amount preferably of at least about one percent (weight percent, same as hereinafter), more preferably at least about 10%. With less than about one percent, water-resisitance is not expected. In the polymerization, methods and conditions thereof are suitably selected. For example, as radical polymerization are adopted bulk polymerization, solution polymerization, suspension polymerization, emulsion polymerization, etc. As ionic polymerization are conducted cationic polymerization, etc. As an initiator in radical polymerization is used a compound which produces free radicals. Preferred radical initiators are benzoyl peroxide, tert-butyl perbenzoate, acetyl benzoyl peroxide, succinyl peroxide, diisopropyl peroxydicarbonate, ammonium persulfate and like peroxides, azobisisobutyronitrile and like azonitriles, etc. Further, it is possible to use a chain transfer agent which is disclosed in Japanese Examined Patent Publication No. 16,035/1960 and has the formula wherein Z is Cl, OH or group convertible to OH, R is lower alkyl (1 to 4 carbon atoms), m is 0 to 4, n is 0 to (4-m). The chain transfer agent is used in an amount of preferably about 10 to 25% by weight in order to adjust the molecular weight and to prevent the gelation. For the same purpose are adjusted amount of initiator, polymerization temperature, polymerization time, etc. The radical initiator is used in an amount of 0.1 to 10% by weight based on the weight of monomers. However, the amount of initiator is not limited to the above range and is suitably selected depending on the polymerization degree of the desired polymer, polymerization time, polymerization temperature, etc. The polymerization temperature is usually -80°C to +250°C, depending on the decomposition temperature of the initiator. Generally, the temperature is preferably in the range of -40°C to +150°C. Solvents useful for solution polymerization are benzene, toluene, xylene and like aromatic hydrocarbons, chloroform, methylene chloride, ethylene chloride and like low-basic solvents. These solvents are used singly or in a mixture. The cationic polymerization is preferably conducted in a solvent such as toluene, benzene, etc. at -30°C to +250°C in the presence of boron trifluoride ethyl etherate, aluminum chloride or a like initiator. The polymer is separated from the reaction mixture by a usual method, for example, by adding the mixture to a poor solvent which does not dissolve the polymer such as methanol, diisopropyl ether, dimethyl ether, petroleum ether or n-hexane. The polymer is obtained as it precipitates. The precipitated polymer is purified by dissolving it in a solvent which is capable of dissolving the polymer such as acetone, methyl ethyl ketone, ethyl acetate, dioxane, tetrahydrofuran, ethylene dichloride, chloroform, carbon tetrachloride, trichloroethylene, benzene, toluene, etc. and thereafter re-precipitating the polymer by adding the solution to a poor solvent. The present prepolymer can be cured by itself or in the form of a mixture thereof with a prepolymer of diallyl phthalate, diallyl isophthalate, diallyl terephthalate, etc. The curing is conducted by heating or light in the presence of a thermal polymerization initiator, photopolymerization initiator, etc. or with irradiation of electron rays, gamma-rays or like active energy rays in the absence of the initiator. In case of using the initiator, diallyl phthalate, diallyl isophthalate, diallyl terephthalate or like monomer is used as a carrier for the initiator. The carrier is used preferably up to about 90% by weight of the mixture. Examples of thermal polymerization initiators are methyl ethyl ketone peroxide, cyclohexanone peroxide and like ketone peroxides, t-butyl perbenzoate, t-butyl peroxy-2-ethylhexoate and like peresters, t-butyl hydroperoxide, cumene hydroperoxide and like hydroperoxides, benzoyl peroxide and like diacyl peroxides. The photopolymerization initiators include 2,2-diethoxyacetophenone, 2,2-dimethoxy-2-phenylacetophenone and like benzoin alkyl ethers, diethoxyacetophenone and like acetophenones, benzophenone and like ketones, 2-chlorothioxanthone and like thioxanthones, etc. The initiator is used preferably in an amount of about 0.001 to 20% by weight, more preferably about 0.1 to 10% by weight based on the total amount of the prepolymer and carrier. The curing is conducted usually at a temperature from room temperature to 250°C, preferably from room temperature to 180°C, despite that any of heat, light or active energy rays is used. The compound (3) which is diallyl aromatic fluorine-containing dicarboxylate is mixed with a prepolymer having at least one carbon-carbon double bond in the molecule to form a curable resin composition. The following are examples of useful prepolymers having at least one double bond in the molecule, although not limited thereto. (1) Polyester obtained by using an unsaturated polybasic carboxylic acid or polyester using an unsaturated polyol These polyesters are prepared by the condensation of a polybasic carboxylic acid and polyol in which a part or all of at least one component is an unsaturated polybasic carboxylic acid or unsaturated polyol. Polybasic carboxylic acids include an unsaturated polybasic carboxylic acid and saturated polybasic carboxylic acid. Examples of the former are maleic anhydride, fumaric acid, citraconic acid, itaconic acid, etc. The latter includes phthalic anhydride, isophthalic acid, terephthalic acid, adipic acid, azelaic acid, sebacic acid, dodecane dicarboxylic acid, etc. The detail of carboxylic acids are described in "Highpolymer Data Handbook, fundamental edition, p 259∼275 (Dicarboxylic acids)", published by Baihukan, Tokyo, Jan. 30, 1986. Polyols include a saturated polyol and unsaturated polyol. The former includes ethylene glycol, propylene glycol and like alkanediol having 2 to 8 carbon atoms. Examples of the latter are butenediol, 3,4-dihydroxy-1,5-hexadiene, pentaerythritol diallyl ether, etc. The detail of polyols are shown in the above "Highpolymer Data Handbook, fundamental edition, p 283∼322 (Diols and polyols)". Generally, the polyester is a condensation product of an unsaturated polybasic carboxylic acid or a mixture thereof with a saturated polybasic carboxylic acid, and a saturate polyol. (ii) Polyester using an unsaturated monocarboxylic acid The polyester is a condensation product of an unsaturated monocarboxylic acid, polybasic carboxylic acid and polyol. The unsaturated monocarboxylic acids include acrylic acid, methacrylic acid, crotonic acid, cinnamic acid, half-ester of an unsaturated dicarboxylic acid such as monoalkyl (C 1∼8 ) ester of maleic acid, monoalkyl (C 1∼8 ) ester of fumaric acid, monoalkyl (C 1∼8 ) ester of itaconic acid, etc. As a polybasic carboxylic acid and polyol, same compounds are used as mentioned in (i). Generally, the polyester is a condensation product of an unsaturated monocarboxylic acid, saturated polybasic carboxylic acid and saturated polyol. (iii) Adduct of a polyepoxy compound and unsaturated monocarboxylic acid Polyepoxy compounds include polyepoxy-hydrocarbon, polyepoxy-halogenohydrocarbon, polyepoxy-alcohol, polyepoxy-aldehyde, polyepoxy-caboxylic acid, etc. Polyepoxy compounds may be either saturated or unsaturated compounds and include a polymer, i.e., epoxy resin, as long as at least two epoxy groups are contained in the molecule. Examples of polyepoxy compounds are bisphenol A-diglycidyl ether, neopentyl glycol diglycidyl ether, vinylcyclohexene diepoxide, epoxidized soybean oil, etc. As unsaturated monocarboxylic acids, same compounds are used as mentioned in (ii). (iv) Polyetherpolyol unsaturated monocarboxylic acid ester The ester is an ester of an adduct of polyol and alkylene oxide (polyetherpolyol), and unsaturated monocarboxylic acid. Alkylene oxides include ethylene oxide, propylene oxide and like alkylene oxides having 2 to 8 carbon atoms, or those in which part of the hydrogen atoms is substituted with halogen atoms such as a chlorine atom, etc. As polyols and unsaturated monocarboxylic acids, the same compounds are used as mentioned in (i) and (ii). (v) Unsaturated polyurethane The unsaturated polyurethane is an adduct of a partial ester of a polyol and unsaturated monocarboxylic acid, and soluble or meltable compound having a free isocyanate group (containing a linear or branched structure but no network structure). Examples of compounds having a free isocyanate group are a polyisocyanate and adduct of polyisocyanate to polyol and/or polyetherpolyol. Polyisocyanates include tolylenediisocyanate, dimethylenebenzenediisocyanate, diphenylmethanediisocyanate, hexahydrotolylenediisocyanate, dimethylenecyclohexanediisocyanate, dicyclohexylmethanediisocyanate, hexamethylenediisocyanate, isophoronediisocyanate, triphenylmethanetriisocyanate, compounds of the formulae As polyols, the same compounds as mentioned in(i) are used and as polyetherpolyols the same compounds as stated in (iv) are employed. As partial esters of a polyol and unsaturated monocarboxylic acid are listed 2-hydroxyethyl(meth)acrylate, trimethylolpropane di(meth)acrylate, glycerine di(meth)acrylate, etc. These compounds (i)∼(v) can be used singly or in mixture of at least two of them. In the present composition, the compound (3) is used preferably in an amount of about 1 to 99% (weight %, same as hereinafter specified), more preferably about 20 to 60%. In curing the above resin composition of the invention, ethylenically unsaturate compounds can be used, when required, as a reactive diluent. The ethylenically unsaturated compounds include various known compounds and typical examples thereof are styrene, vinyltoluene, chlorostyrene, t-butylstyrene, α-methylstyrene, divinylbenzene, acrylic acid, methacrylic acid, methyl, ethyl, isopropyl, n-butyl, t-butyl, α-ethylhexyl, n-nonyl, n-decyl, lauryl or stearyl ester of acrylic acid or methacrylic acid, n-butoxyethyl, cyclohexyl, phenoxyethyl, tetrahydrofurfuryl, glycidyl, allyl, benzyl, tribromophenyl, 2,3-dichloropropyl, 3-chloro-2-hydroxypropyl ester of acrylic acid or methacrylic acid, ethylene glycol mono(meth) acrylate, propylene glycol mono(meth)acrylate, diethylene glycol mono(meth)acrylate, dipropylene glycol mono(meth)acrylate, polyethylene glycol [Molecular weight (MW), 200∼1000] mono(meth)acrylate, polyethylene glycol (MW, 200∼1000) monomethyl ether mono(meth)acrylate, polypropylene glycol (MW, 200∼1000) mono(meth)acrylate, polypropylene glycol (MW, 200∼1000) monomethyl ether mono(meth)acrylate, polyethylene glycol (MW, 200∼1000) monoethyl ether mono(meth)acrylate, polypropylene glycol (MW, 200∼1000) monoethyl ether mono(meth)acrylate, ethylene glycol di(meth)acrylate, propylene glycol di(meth)acrylate, 1,3-propanediol di(meth)acrylate, 1,4-butanediol di(meth)acrylate, neopentyl glycol di(meth)acrylate, 1,6-hexanediol di(meth)acrylate, polyethylene glycol di(meth)acrylate, polypropylene glycol di(meth)acrylate, glycerin di(meth)acrylate, glycerin tri(meth)acrylate, trimethylolethane di(meth)acrylate, trimethylolethane tri(meth)acrylate, trimethylolpropane tri(meth)acrylate, diallyl phthalate, dibutyl fumarate, vinyl acetate, etc. The reactive diluent is used preferably in an amount of about 1 to 95% by weight, more preferably about 5 to 80% by weight based n the total weight of the reactive diluent and the prepolymer. In order to keep the present composition in a stable state, a known polymerization inhibitor can be added thereto. The amount thereof is 0.001 to 2.5% by weight, preferably 0.005 to 1% by weight based on the total weight of the composition. Further, a coloring agent, dispersant and like conventional additives can be, as required, added to the present composition. The present composition can be obtained by mixing the above ingredients by a known method, for example, by use of a mixer, roll mill, ball mill, sand mill, high-speed impeller, etc. The prepolymer of the present invention having at least one double bond in the molecule can be cured by a known method, for example, by heating or with irradiation of ultraviolet rays, electron rays, X-rays, gamma-ray and like active energy rays. When using the above electron rays, X-rays, gamma-rays or like ionizing radioactive rays having high energy and releasing secondary electrons having been absorbed in a substance, it is not necessary to use a polymerization initiator. However, in case the composition is cured by heating or with irradiation of ultraviolet rays, it is preferable to use a thermal polymerization initiator or photopolymerization initiator. Examples of thermal polymerization initiators are methyl ethyl ketone peroxide, cyclohexanone peroxide and like ketone peroxides, t-butyl perbenzoate, t-butyl peroxy-2-ethylhexoate and like peresters, t-butyl hydroperoxide, cumene hydroperoxide and like hydroperoxides, benzoyl peroxide and like diacyl peroxides. The photopolymerization initiators include 2,2-diethoxyacetophenone, 2,2-dimethoxy-2-phenylacetophenone and like benzoin alkyl ethers, diethoxyacetophenone and the like acetophenones, benzophenone and like ketones, 2-chlorothioxanthone and like thioxanthones, etc. The initiator is used preferably in an amount of about 0.001 to 20% by weight, more preferably about 0.1 to 10% by weight based on the total amount of the prepolymer and reactive diluent. The curing is conducted usually at a temperature from room temperature to 250°, preferably from room temperature to 180°C, despite that any of heat, light or active energy rays is used. The compound (1) is useful as a starting material for a prepolymer and cured product. For example, a homoprepolymer or coprepolymer of the compound (1) is employed for the preparation of a fiber reinforced plastic, glass cloth prepreg, etc. The prepolymer contains a side chain which has a carbon-carbon double bond in the terminal, exhibits cross-linking ability and affords a cured product. Further, the prepolymer has a perfluoroalkenyloxy chain as the other side chain which gives an excellent water-resistance to the cured product. The cured product obtained from the present prepolymer has water-resistance which is much superior to that of a cured product prepared from the conventional diallyl phthalate. Even the prepolymer containing about 50% by weight of the repeating unit (6) provides a curing product which is about 1/10 in water absorbency than the conventional product. The invention will be described below with reference to Examples and Comparison Examples in which parts are all by weight, unless otherwise specified. Example 1 Into a reaction vessel equipped with a stirrer, condenser and thermometer was placed 0.2mole of 5-hydroxy-isophthalic acid. Thereto were added 0.6mole of allyl alcohol, 300ml of toluene, 1.3g of sulfuric acid and 0.2g of p-methoxyphenol, and the mixture was refluxed by heating. A mixture of toluene and water was distilled off and cooled with a condenser, and toluene was separated from water and returned continuously to the reaction vessel. The mixture was heated for 8 hours and then allowed to cool. At this point, the total amount of the distilled water was 7mℓ. After the reaction mixture was washed with a saturated aqueous solution of sodium chloride until the aqueous layer did not indicate acidity, toluene was distilled at a reduced pressure. The resulting concentrate was distilled at a reduced pressure to obtain 27g (yield 52%) of diallyl 5-hydroxy-isophthalate. b.p. 202∼205°C/5mmHg. ¹H-NMR (TMS standard, in acetone-d₆, δ ppm) The obtained diallyl 5-hydroxy-isophthalate (26g) was dissolved into 90mℓ of dimethylformamide and thereto was added 31g of triethylamine. To the mixture were added dropwise 45 g of hexafluoropropene trimer with stirring at room temperature in a period of 10 minutes. The mixture was further stirred for 2 hours and then poured into a large amount of a diluted aqueous solution of hydrochloric acid to obtain oily precipitates. The precipitates were separated, washed with water and distilled at a reduced pressure to give 41g (yield 59%) of diallyl 5-(perfluorononenyloxy)isophthalate (Compound A). b.p. 150∼152°C/4mmHg. ¹⁹F-NMR (external standard CF₃COOH, in CDCl₃) Chemical shift (δppm) is shown in which high magnetic field is indicated by a plus value. Example 2 The reaction was conducted in the same manner as in Example 1 except that 4-hydroxy-phthalic acid was used in place of 5-hydroxy-isophthalic acid to obtain diallyl 4-(perfluorononenyloxy)phthalate (Compound B). b.p. 160∼162°C/7mmHg. Example 3 The reaction was conducted in the same manner as in Example 1 except that 30g of hexafluoropropene dimer was used in place of the trimer thereof and the reaction with diallyl 5-hydroxy-isophthalate was conducted at 0 to 4°C to obtain 39g of diallyl 5-(perfluorohexenyloxy)isophthalate (Compound C). b. p. 128∼131°C/5mmHg. ¹⁹F-NMR (external standard CF₃COOH, in CDCl₃, δppm) Example 4 The reaction was conducted in the same manner as in Example 2 except that 50g of tetrafluoroethylene pentamer was used in place of hexafluoropropene trimer to obtain diallyl 4-(perfluorodecenyloxy)phthalate (Compound D). b. p. 165∼167°C/6mmHg. Example 5 Into a vessel equipped with a stirrer and condenser were placed Compound A (250g), diallyl terephthalate (250g), benzoyl peroxide (7g), dibutyltin dilaurate (6g) and water 250g), and the mixture was reacted at 85°C for 5 hours. After completion of the reaction, the mixture was cooled to room temperature and acetone (50g) was added thereto. The organic layer was added dropwise to a large amount of methanol with stirring. The resulting precipitates were filtered, washed with methanol, dried at a reduced pressure and pulverized to obtain 120g of white powder. The powder was 66 in iodine value, 8.6×10³ in number average molecular weight ( M n), 5.3×10⁴ in weight average molecular weight ( M w) in term of polystyrene with use of gel permeation chromatography and 18.5wt% in fluorine content. Accordingly, the above white powder was a prepolymer in which Compound A and diallyl terephthalate were contained in molar ratio of 1 : 4.3. To a solution of the prepolymer (50 parts) and diallyl terephthalate (50 parts) was added benzoyl peroxide (2 parts). The mixture was poured into a Petri dish having internal diameter of 50mm and heated at 90°C for 8 hours to obtain a casting plate which was 50 mm in diameter and 3mm in thickness. Example 6 White powder (102g) was obtained in the same manner as in Example 5 except that Compound B (250g) was used as diallyl aromatic fluorine-containing dicarboxylate and the reaction was conducted for 4 hours. The powder was 70 in iodine value, 7.3×10³ in M n, 4.4×10⁴ in M w and 18.6wt% in fluorine content. Accordingly, the above white powder was a prepolymer in which Compound B and diallyl terephthalate were contained in molar ratio of 1 : 4.3. A casting plate was obtained in the same manner as in Example 5 with use of the prepolymer. Example 7 White powder (148g) was obtained in the same manner as in Example 6 except that Compound B (375g) and diallyl terephthalate (125g) were used. The powder was 49 in iodine value, 1.1×10⁴ in M n, 4.6×10⁵ in M w and 31.4wt% in fluorine content. Accordingly, the above white powder was a prepolymer in which Compound B and diallyl terephthalate were contained in molar ratio of 1 : 1.4. A casting plate was obtained in the same manner as in Example 5 with use of the prepolymer. Example 8 White powder (118g) was obtained in the same manner as in Example 5 except that diallyl phthalate (125g) and diallyl isophthalate (125g) were used in place of diallyl terephthalate. The powder was 65 in iodine value, 7.2×10³ in M n, 4.2×10⁴ in M w and 18.7 wt% in fluorine content. Accordingly, the above white powder was a prepolymer in which Compound A and diallyl esters were contained in molar ratio of 1 : 4.3. A casting plate was obtained in the same manner as in Example 5 with use of the prepolymer. Example 9 White powder (121g) was obtained in the same manner as in Example 5 except that diallyl isophthalate was used in place of diallyl terephthalate. The powder was 72 in iodine value, 5.6×10³ in M n, 6.1×10⁴ in M w and 18.5wt% in fluorine content. Accordingly, the above white powder was a prepolymer in which Compound A and diallyl isophthalate were contained in molar ratio of 1 : 4.3. A casting plate was obtained in the same manner as in Example 5 with use of the prepolymer. Example 10 A prepolymer (87g) of Compound B only was prepared in the same manner as in Example 6 except that Compound B was used as a sole component of aromatic dicarboxylate without use of diallyl terephthalate. The powder was 28 in iodine value, 2.4×10³ in M n, 4.8×10³ in M w and 45.9wt% in fluorine content. The prepolymer (50 parts) and Compound B (50 parts) were mixed homogeneously with heating and benzoyl peroxide (2 parts) was added thereto. The mixture was heated at 90°C for 8 hours to obtain a casting plate. Example 11 A white powder (108g) was obtained in the same manner as in Example 5 with use of Compound C (300g), diallyl terephathalate (200g), benzoyl peroxide (7 g), dibutyltin dilaurate (6 g) and water (250g). The powder was 71 in iodine value, 9.2×10³ in M n, 5.9×10⁴ in M w and 19.8wt% in fluorine content. Accordingly, the above white powder was a prepolymer in which Compound C and diallyl terephthalate were contained in molar ratio of 1 : 2.1. The prepolymer (60 parts) and diallyl terephthalate (40 parts) were mixed and benzoyl peroxide (2 parts) was added thereto. A casting plate was prepared in the same manner as in Example 5 with use of the mixture. Example 12 In Compound D, perfluoroalkenyloxy group X is derived from pentamer of tetrafluoroethylene. A prepolymer (107g) of Compound D only was prepared in the same manner as in Example 10 except that Compound D (500g) was used and the reaction was conducted for 6 hours. The powder was 26 in iodine value, 3.2×10³ in M n, 6.7×10³ in M w and 48.5wt% in fluorine content. The prepolymer (70 parts) and Compound D (30 parts) were mixed homogeneously with heating and benzoyl peroxide (2 parts) was added thereto. A casting plate was prepared in the same manner as in Example 5 with use of the mixture. Comparison Example 1 Diallyl terephthalate (50 parts) was dissolved in 50 parts of diallyl phthalate prepolymer [ trade name, DAISO DAP A, Osaka Soda Co., Ltd. , M n =6.7X10³, M w=2.6X10⁴, iodine value 61] and benzoyl peroxide (2 parts) was added thereto. A casting plate was prepared in the same manner as in Example 5 with use of the mixture. Comparison Example 2 A casting plate was prepared in the same manner as in Comparison Example 1 except that diallyl terephthalate polymer [trade name, DAPREN, Osaka Soda Co., Ltd. , M n=7.3X10³, M w=2.5X10⁵, iodine value 51] was used in place of DAISO DAP A. Casting plates prepared in Examples 5 to 12 and Comparison Examples 1 and 2 mere checked for water absorbency at 23°C according to JIS K-6911. The results were given in Table 1. Water absorbency (wt%) Water absorbency (wt%) Ex.5 0.03 Ex.10 <0.01 Ex.6 0.03 Ex.11 0.04 Ex.7 0.01 Ex.12 <0.01 Ex.8 0.04 Com.Ex.1 0.33 Ex.9 0.03 Com.Ex.2 0.41 Example 13 A ultraviolet-ray curable resin composition (I) was prepared according to the following formulation. * Oligoester acrylate [trade name, ARONIX M-6420 X, viscosity 4 X10⁴cps/50°C, Toagosei Chemical Industry Co., Ltd.] 50 * Compound (A) 35 * Trimethylolpropane triacrylate 5 * 2-Hydroxyethyl acrylate 3 * Methyl o-benzoylbenzoate 5 * Diethylaminoethyl methacrylate 2 100 parts Composition (I) was applied by a bar coater to a glass plate in a thickness of 20µm and the coating film was cured sufficiently by subjecting the film to pass under a high-voltage mercury lamp (80W/cm) three times, the film being placed on a conveyor moving at 5m /min. Example 14 A ultraviolet-ray curable resin composition (II) was prepared according to the following formulation. * Unsaturated epoxy resin [trade name Diclite UE-8200, Dainippon Ink & Chemicals Inc.] 50 * Compound (B) 30 * 1,6-Hexanediol diacrylate 10 * 2-Hydroxyethylacryloyl phosphate 3 * Methyl o-benzoylbenzoate 5 *Triethanolamine 2 100 parts Composition (II) was applied by a bar coater to a degreased soft steel plate in a thickness of 20µm and the coating film was cured in the same manner as in Example 13. Example 15 A thermosetting resin composition (III) was prepared according to the following formulation. * Maleic acid-propylene glycol type unsaturated polyester resin (acid value 18.5mg KOH/g) 40 * Compound (C) 35 * Styrene 20 * Methyl ethyl ketone peroxide 3 * Dimethylaniline (0.5% solution) 1 * Cobalt naphthenate (Co content 5%) 1 100 parts Composition (III) was applied by a bar coater to a degreased soft steel plate in a thickness of 100µm and the coating film was allowed to stand in a desiccator at 30°C for 10 hours, the air in the desiccator having been previously replaced by nitrogen. Example 16 * Urethane acrylate [trade name, ARONIX M-1100, vicosity 8∼12X10⁴cps/50°C, Toagosei Chemical Industry Co., Ltd.] 45 * Compound (A) 25 * Trimethylolpropane triacrylate 20 * 2-Hydroxyethylacryloyl phosphate 3 * Methyl o-benzoylbenzoate 5 * Triethanolamine 2 100 parts A ultraviolet-ray curable resin composition (IV) was prepared according to the above formulation and a coating film was cured in the same manner as in Example 13. Example 17 * Polyether acrylate [trade name, ARONIX M-220, viscosty 10∿20cps/25°C, Toagosei Chemical Industry Co., Ltd.] 30 * Compound (B) 50 * Trimethylolpropane triacrylate 13 * Methyl o-benzoylbenzoate 5 * Diethylaminoethyl methacrylate 2 100 parts A ultraviolet-ray curable resin composition (V) was prepared according to the above formulation and the composition (V) was applied by a bar coater to a glass plate in a thickness of 20µm, and the coating film was cured in the same manner as in Example 13. Comparison Example 3 The procedure was conducted in the same manner as in Example 13 except that diallyl isophthalate was used in place of Compound (A). Comparison Example 4 The procedure was conducted in the same manner as in Example 14 except that diallyl phthalate was used in place of Compound (B). Comparison Example 5 The procedure was conducted in the same manner as in Example 15 except that diallyl isophthalate was used in place of Compound (C). Comparison Example 6 The procedure was conducted in the same manner as in Example 16 except that diallyl isophthalate was used in place of Compound (A). Comparison Example 7 The procedure was conducted in the same manner as in Example 17 except that diallyl isophthalate was used in place of Compound (B). Example 18 A ultraviolet-ray curable resin composition (VI) was prepared according to the following formulation and a coating film was cured in the same manner as in Example 13. * Polyethylene glycol diacrylate (average molecular weight : 510) 40 * Compound (A) 20 * Trimethylolpropane triacrylate 30 * Methyl o-benzoylbenzoate 6 * Diethylaminoethyl methacrylate 4 100 parts Example 19 A mixture of one mole of maleic anhydride, one mole of phthalic anhydride and 2.16moles of diethylene glycol was heated to 150°C in a period of one hour under nitrogen atmosphere and then was maintained at the same temperature for 2 hours. Then the mixture was heated at 190°C for 3 hours As a residue was obtained an unsaturated polyester having an acid value of 55.7mg KOH/g and hydroxyl value of 84.9mg KOH/g. A thermosetting resin composition (VII) and a cured product thereof were obtained in the same manner as in Example 15 except that the above unsaturated polyester was used in place of the polyester of Example 15. Example 20 A ultraviolet-ray curable resin composition (VIII) was prepared according to the following formulation and a coating film was cured in the same manner as in Example 13. Example 21 A ultraviolet-ray curable resin composition (IX) was prepared in the same manner as in Example 13 except that 50 parts of the oligoester acrylate having the formula below [trade name, Viscoat #3700, Osaka Organic Chemical Ind. Co., Ltd. ] was used in place of the oligoester acrylate of Example 13. A coating film was cured in the same manner as in Example 13. Example 22 A ultraviolet-ray curable resin composition (X) was prepared according to the following formulation and a coating film was cured in the same manner as in Example 14. Adhesion and water-resistance tests Curable resin compositions were checked for adhesiveness to a substrate before boiling in water according to the following cross-cut peeling test and were checked for water-resistance by observing an appearance of a coating after boiling in water. The results were given in Table 2. The present invention showed excellent effects in which the water-resistance was improved by using the compound (3). Adhesion: Adhesiveness was checked by a cross-cut peeling test. The coating was crosscut to the surface of the substrate in 100 pieces, each 1×1mm. A cellophane tape was adhered to the cross-cut portion and then peeled off quickly and the remaining pieces were counted. ( Number of the remaining pieces is shown.) Water-resistance: Appearance of the coating after immersed in boiling water was shown. ○ No change Δ Coating was partially whited and swollen X Coating was peeled off from the substrate Adhesiveness (number of remaining pieces) Water-resistance Ex.13 100 ○ 14 100 ○ 15 100 ○ 16 100 ○ 17 100 ○ 18 100 ○ 19 100 ○ 20 100 ○ 21 100 ○ 22 100 ○ Com.Ex.3 100 ▵ 4 100 ▵ 5 100 ▵ 6 100 ▵ 7 100 X

Claims: A diallyl aromatic dicarboxylate derivative of the formula wherein Y is a hydrogen atom or a perfluoroalkenyl group having 6 to 14 carbon atoms. A process for preparing an aromatic dicarboxylate derivative of the formula which comprises reacting a perfluoroalkene XF with a hydroxy aromatic dicarboxylic acid derivative of the formula wherein X is a perfluoroalkenyl group having 6 to 14 carbon atoms. A process for preparing diallyl aromatic dicarboxylate derivative of the formula (1) which comprises reacting an allyl alcohol with an aromatic dicarboxylic acid of the formula wherein Y is as defined above. A prepolymer containing a repeating unit derived from diallyl aromatic fluorine-containing dicarboxylate and represented by the formula wherein X is as defined above. A prepolymer as defined in claim 4 which contains at least one percent by weight of the repeating unit (6). A prepolymer as defined in claim 5 wherein the prepolymer is a copolymer having the repeating unit of the formula (6) and an other repeating unit, e.g. a repeating unit which is derived from the cleavage of double bond of an ethylenically unsaturated compound. A prepolymer as defined in claim 6 wherein the ethylenically unsaturated compound is diallyl phthalate, diallyl isophthalate or diallyl terephthalate. A curable resin composition which comprises a prepolymer having at least one carbon-carbon-double bond in the molecule and a diallyl aromatic fluorine-containing dicarboxylate represented by the formula (3) of claim 2. A composition as defined in claim 8 wherein the prepolymer is a polyester of unsaturated polybasic carboxylic acid, polyester of unsaturated polyol, polyester of unsaturated monocarboxylic acid, adduct of a polyepoxy compound and an unsaturated monocarboxylic acid, ester of polyether polyol and an unsaturated monocarboxylic acid or unsaturated polyurethane. A composition as defined in one or both of the claims 8-9 which further comprises a reactive diluent.

Inventors: KUBO, MOTONOBU, TAMARU, SINJI
Applicants: DAIKIN INDUSTRIES, LIMITED
Application year: 1987
Main classification: C07C69
IPC codes: C08F291, C08F18, C08F290