PROCESS FOR CATIONIC COATING COMPOSITIONS

Abstract: This invention provides a process for the preparation of water-thinnable, hydrolytically stable, thermosetting, cationic coating composition, which comprises blending: 1) 5-35 %w of a crosslinking compound, and 2) 65-95 %w of a carboxylated amide group-containing amino binder being the reaction product of an amino group-­ containing resin binder and not more than 0.1 mol of a cyclic anhydride per amino group equivalent of said amino group-containing resin binder, which amino group-containing binder comprises the reaction product of a) ammonia, and b) a blend of b₁) a polyglycidyl ether having n epoxy groups per molecule, wherein 1<n<1.9, said polyglycidyl ether being the reaction product of a multifunctional polyglycidyl ether having x epoxy groups per molecule, wherein x>2, and (x-n) mol of a mono­ functional phenol per mol of the multifunctional polyglycidyl ether, and b₂) a diglycidyl ether, having an EGC in the range of from 1000 to 5500 mmol/kg, the average molar epoxy functionality of the glycidyl ethers present in the blend of polyglycidyl ehter and diglycidyl ether being <1.75. and wherein 1) and 2) are blended before or after neutralization of 2). The thus prepared coating compositions when used for coating the interior of food and beverage cans, result in coatings which combine very good taste performance properties with a high level of mechanical and chemical resistance properties.

Description: This invention relates to a process for the preparation of hydrolytically stable cationic coating compositions, to the coating compositions prepared by said process and to the use thereof, particularly to their use as aqueous thermosetting coating compositions for application via electrodeposition. Water-thinnable, hydrolytically stable, thermosetting cationic coating compositions, comprising a blend of a carboxylated crosslinking compound and an amine group-containing resin binder, being the reaction product of ammonia and at least a specific type of polyglycidyl ether, are suitable for coating the interior of beer and beverage cans, especially for such applications where the taste performance requirements were very critical. A disadvantage associated with the use of carboxylated crosslinking compounds, such as the carboxylated melamine formaldehyde resin, is that they are not widely available and certainly not as well established at their non-carboxylated counterparts, and thus restrict the applicability of these amino group-containing binders. Thus, the formulation of cationic coating compositions for the applications referred to hereinbefore leaves room for further improvement. Therefore, the problem underlying the present invention is to develop cationic coating compositions which do not have the disadvantages inherent to the use of the carboxylated crosslinking compounds but having the same high level of performance properties as the cationic coating composition described hereinbefore. The invention provides a process for the preparation of a water-thinnable, hydrolytically stable, thermosetting, cationic coating composition, which comprises blending: 1) 5-35 %w of a crosslinking compound, and 2) 65-95 %w of a carboxylated amide group-containing amino binder being the reaction product of an amino group-containing resin binder and not more than 0.1 mol of a cyclic anhydride per amino group equivalent of said amino group containing resin binder, which amino group-containing binder comprises the reaction product of a) ammonia, and b) a blend of b₁) a polyglycidyl ether having n epoxy groups per molecule, wherein the 1<n<1.9, said polyglycidyl ether being the reaction product of a multifunctional polyglycidyl ether having x epoxy group per molecule, wherein x>2, and (x-n) mol of a monofunctional phenol per mol of the multifunctional polygycidyl ether, and b₂) a diglycidyl ether, having an epoxy group concentration (EGC) in the range of from 1.0 to 5.5 eq.kg⁻¹ the average molar epoxy functionality of the glycidyl ethers present in the blend of polyglycidyl ether and diglycidyl ether being <1.75. and wherein 1) and 2) are blended before or after neutralization of 2). The carboxylated amide group-containing amino binders present in the coating composition prepared by a process according to the present invention, and wherein the carboxylated amide groups are only present in a relatively low concentration vis a vis the amino groups, can be made water thinnable by neutralizing the amino groups with an acid. These carboxylated amide group-containing binders and the cationic coating compositions based thereon, thus differ from the anionic coating compositions based on carboxylated amide group-containing binders, wherein the carboxylated amide group content is sufficiently high to make said binder water reducible after neutralization with a base. Such anionic coating compositions have been described in Patent Application GB-A 2.037291. The multifunctional polyglycidyl ether from which the polyglycidyl ether having n epoxy groups per molecule is derived, may conveniently be a polyglycidyl ether prepared by reaction of a polyhydric phenol having a phenolic hydroxyl functionality greater than 2, with an epihalodrin, preferably epichlorohydrin, in the presence of a hydrogen halide acceptor, e.g. an alkali metal hydroxide. Examples of suitable such polyhydric phenols are novolac resins of general formula wherein R represents an alkylene, e.g. CH₂ group, R¹ represents an alkyl group, e.g. a methyl, p -t-butyl, octyl or nonyl group, q and p are numbers having average values 0<q<6 and 0<p<2, or of general formula wherein R² represents an alkylene, e.g. CH₂ group, R³ represents an alkylene, e.g. CH₂ or C(CH₃)₂ group, a carbonyl group, an oxygen or sulphur atom and q′ is a number having an average value in the range of from 0 to 2. Other examples of suitable polyhydric polynuclear phenols are 1,1,2,2-tetra(4-hydroxyphenyl)ethane and the tetraphenol derives from diphenolic acid having the general formula wherein R⁴ represents the residue of a diol. Polyglycidyl ethers derived from polyhydric phenols of formulae I, II and III are known and are described, together with processes for their preparation, in for example, US-A 2,844,553, NL-A 8100830, DE-A 2,656,867 and GB-A 2 001 991. Preferably the multifunctional polyglycidyl ether is an epoxy novolac resin wherein x is in the range from 2.5 to 3.5. The monofunctional phenol may be a single phenol or a mixture of phenols. For example the phenol may conveniently be phenol optionally substituted by one or more of one or more substituents selected from C 1-16 alkyl, C 3-16 alkenyl, C 1-4 hydroxylalkyl, C 2-13 alkoxycarbonyl and C 1-16 alkoxy groups. Examples of such compounds include phenol, the cresols, salicyl alcohol, 2-allyl phenol, 2,4,6-triallyl phenol, dimethyl phenol, 4-hydroxymethyl-2,6-dimethyl phenol, 2-hydroxyphenethyl alcohol, 4-hydroxybenzyl alcohol and ethyl 4-hydroxybenzoate. Preferably the monofunctional phenol is phenol substituted in the para-position by a C 4-12 alkyl substituent. Examples of such alkyl substituents include n-, iso- and t-butyl, n- and iso-octyl, n-and iso-nonyl and n-and iso-dodecyl groups. Branched alkyl substituents are particularly suitable. P-iso-octyl phenol has been found to be a very suitable monofunctional phenol. The diglycidyl ether will generally be a diglycidyl ether of a dihydric phenol such as 2,2-bis(4-hydroxyphenyl)-propane. Examples of diglycidyl ethers based on such a dihydric phenol are "EPIKOTE 1001" (registered trade mark) (EGC 2.0 to 2.2) and "EPIKOTE 3003" (registered trade mark) (EGC 1.2 to 1.38). Preferred diglycidyl ethers have a EGC in the range of from 1.8 to 2.4 eq.kg⁻¹. The reaction between ammonia and epoxy groups is known. From GB-A 1221906, wherein reaction products of ammonia and diglycidyl ethers have been described, it can be concluded that the content of secondary and tertiary amino groups present in the reaction product, is related to the excess of ammonia over epoxy used. A smaller excess will increase the content of secondary and tertiary amino groups as well as the molecular weight of the reaction product and the risk of gelation. It can be expected that the presence of such higher molecular weight polyaddition products will contribute positively towards the performance of the ultimate coating. Although it might be possible to prepare such higher molecular weight reaction products by carefully controlled process conditions, in the process of the present invention it has been found advantageous to reduce the omnipresent risk of gelation by restricting the average number of epoxy groups per molecule of glycidyl ether. For the polyglycidyl ether the average molar epoxy functionality is restricted to 1<n<1.9 preferably 1.3<n<1.6, while the average molar epoxy functionality for the glycidyl ethers present in the blend of polyglycidyl ethers and diglycidyl ether is set at <1.75. It is preferred that the polyglycidyl ether and diglycidyl ethers are present in said blend in a weight ratio in the range of from 75:25 to 45:55. In the preparation of the hereinbefore mentioned amino group-containing binders, it is preferred that on average 0.45 to 0.6 of ammonia is reacted per equivalent of epoxy, for which at least 4.5 equivalents of amino-hydrogen per equivalent of epoxy is generally employed. In the preparation of the amino group-containing binders, the blend of the polyglycidyl ether and diglycidyl ether may conveniently be contacted with ammonia while dissolved in an organic solvent. Preferably said solvent is a water-miscible solvent and includes mono C 1-6 alkyl ethers of mono- or polyethylene glycol or mono- or poly propylene glycol, and cyclic ethers such as tetrahydrofuran (THF) or dioxane. A preferred water-miscible solvent is 2-n-butoxyethanol. The glycidyl ether content of these solutions may conveniently be in the range of from 50 to 90 %w and preferably in the range of from 60 to 70 %w. Ammonia may be introduced into the reactor as supplied e.g. as a 25 %w aqueous solution. The resulting mixture will generally be inhomogeneous and may as such be used for preparing the amino group-containing binder. It has however proven to be advantageous to carry out the reaction with ammonia in the presence of one or more solvents, which when present in a sufficient concentration will convert the reactor contents into a more or less homogeneous mixture. Suitable such solvents include lower alcohols such as methanol and ethanol as well as lower ethers, especially cyclic ethers such as THF and dioxane. Very promising results have been obtained with a 4:1 w/w blend of THF and ethanol. The reaction with ammonia is carried out at a temperature in the range of from 20 to 120°C and at atmospheric or slightly above atmospheric pressure. The introduction of the carboxy groups by reacting the amino group-containing resin binder with a cyclic anhydride may be conducted at a temperature in the range of from 30 to 120 °C, preferably at a temperature in the range of from 60 to 90°C. Said reaction is preferably carried out in the presence of a solvent e.g. a glycol ether, such as 2-n-butoxyethanol. Depending on the reaction temperature, the conversion of the amino groups into the corresponding carboxylated amide groups can be accomplished within 30 minutes. The cyclic anhydrides which may be employed in the process of the present invention, are intra molecular anhydrides having from 4 to 12 carbon atoms per molecule and include anhydrides such as succinic anhydride, chlorosuccinic anhydride, maleic anhydride and hexahydrophthalic anhydride. Trimellitic anhydride (TMA) is a preferred anhydride. The crosslinking compounds which may be employed in formulating the cationic coating compositions include water thinnable as well as solvent borne and non-water thinnable melamine-, urea- and phenolformaldehyde resin. The invention is not restricted to the use of the conventional crosslinking compounds mentioned hereinbefore, but is also understood to include modified melamine-, urea- and phenolformaldehyde resins, such as chelating group-containing melamineformaldehyde resins. The crosslinking compounds are preferably used in a ratio of carboxylated amide group-containing resin binder to crosslinking compound of 85:15 to 70:30 w/w. Pigments, fillers, dispersing agents, and other components known in the art of paint formulation may further be added. Addition of small amounts (up to 1 %w) of non-ionic surfactant may be useful for further stabilization of aqueous compositions or improvement of the wetting during application. Co-solvents, such as 2-n-butoxyethanol and, especially, 2-n-hexyloxyethanol, may advantageously be included. The water for use in the aqueous compositions is preferably purified, such as by distillation or demineralization. The water-dilutable compositions may be applied by a variety of methods known in the art, onto a variety of substrates, in particular metals such as bare steel, phosphated steel, chromate-treated steel, zinc, tin plate (for can coating), and aluminium (also e.g. for can coating), to produce cured coatings of desireable thickness, from 2 micrometres upwards up to in general 40 micrometres. Curing of the coating compositions made according to the process of the present invention can be performed by stoving, for example, at temperatures of from 170 to 220°C, with curing times varying from 3 to 20 minutes. The thermosetting coating compositions may generally be applied by electrodeposition and other methods such as spraying or dipping, and are particularly suitable for coating cans by electrodeposition. The invention will be further understood from the following examples, in which parts and percentages are by weight, unless otherwise indicated, and various terms are defined as follows: Polyether I is a multifunctional epoxy diphenylolpropane novolac resin, having an average molecular weight 615 and on average 3.1 epoxy groups per molecule. Polyether II is a multifunctional epoxy novolac resin, having an average molecular weigh 665 and on average 3.5 epoxy groups per molecule. Polyether E-1 is a solid diglycidyl ether of 2,2-bis(4-hydroxyphenyl)propane having an EGC of 2.12. Polyether E-2 is a solid diglycidyl ether of 2,2-bis(4-hydroxyphenyl)propane having an EGC of 2.04. Cymel 1141 (trade mark) is a highly alkylated melamineformaldehyde resin of mixed methyl-isobutyl alkylation having a non-volatile content of 85 %w in isobutanol. The resin contains acid chelating groups in an amount corresponding with 22 mg KOH/g. Cymel 1156 (trade mark) is an approximately 100 % non-volatile, highly viscous, hexabutoxymethylmelamine resin. Cymel 1116 (trade mark) is an approximately 100 % non-volatile highly alkylated monomeric melamine formaldehyde crosslinking agent containing ethoxy and methoxy groups. "Amine value" is expressed in milli-equivalents (amino) nitrogen per gram. in which EE represents the epoxy equivalent weight in g.e q ⁻¹,calculated in accordance with the ISO-standard 3001-1978(E). "Ep f av ": average epoxy functionality. Polyglycidyl ether preparation Two polyglycidyl ethers were prepared by heating a multifunctional polyether and a monofunctional phenol with stirring to 140°C, whereupon tetramethylammonium chloride (TMAC) was added as a 50% solution in water. The reactor contents were maintained at 140°C until the reaction had been completed, i.e. the calculated EGC had been obtained. After a slight cooling 2-n-butoxyethanol was added to arrive at a solution containing 66.7 %w solids. Process details and product characteristics are given in Table 1. Examples I & II Preparation of amino group-containing resin binders The binders were prepared according the following procedure: An amount of a Polyether solution, 66.7 %w in 2-n-butoxyethanol, corresponding with 1.5 eq epoxy, an amount of diglycidyl ether E-1 or E-2 corresponding with 1.5 eq epoxy and additional 2-n-butoxyethanol were homogenized by heating to 90°C with stirring. After cooling to 25°C a 25 %w aqueous solution of ammonia was added in an amount as indicated hereinafter together with a sufficient amount of a 4/1 w/w blend of THF/ethanol to arrive at a clear "solution". Thereupon the temperature of the reactor contents was gradually raised to about 60°C in approximately 6 hours during which period virtually all the epoxy groups had reacted. Subsequently the temperature in the reactor was increased to 120°C, in as short a time as was possible, and maintained at that temperature to remove excess ammonia, water, THF, and ethanol by distillation using a nitrogen purge. The ammonia removal was checked with the aid of a wet paper-pH-indicator. Process details and product characteristics are given in Table 2. Examples III-VIII Preparation of carboxylated amide group-containing amino binders Solutions of the amino group-containing resin binders in 2-n butoxyethanol, as prepared following Examples I and II, respectively, were reacted with varying amounts of TMA at 80°C for about 30 minutes, which reaction time appeared to be sufficient to convert the anhydride into the corresponding carboxylated amide groups. Process details and product characteristics are given in Table 3. Examples IX-XI Preparation of aqueous lacquers for electrodeposition The 2-n-butoxyethanol solutions of the carboxylated amide group-containing amino resin binders as prepared in examples IV-VI were blended respectively with the appropriate amounts of crosslinking compound and 2-n-hexyloxyethanol, neutralized with lactic acid and finally diluted with demineralized water to arrive at lacquers having a solids content of 15 %w. The quantities of each of the components used are given in Table 4 together with the characteristics of the lacquers thus prepared. Comparative Example A Preparation of aqueous lacquers for electrodeposition The amino group-containing resin binder solution as prepared following Example I were blended with 2-n-hexyloxyethanol and "Cymel 1141" at ambient temperature (20°C). The resulting homogeneous mixture was neutralized with 90 %w lactic acid in water and thinned with demineralized water. The lacquer composition and the characteristics thereof are given in Table 4. Examples XII-XIV Cathodic electrodeposition The lacquers as prepared in examples IX-XI were used to coat 330 ml tin-plate cans (2-piece DWI cans) by cathodic electrodeposition. The can formed the cathode of an electrodepositon cell, the anode being a stainless steel member inserted within the can at a substantially uniform separation of 2 millimetres from the can. A potential difference of 100-120V, which resulted after baking in a coating weight per can in the range of 200-250 mg, corresponding with an average dry film thickness in the range of 5 to 6 m, was applied between the can and the anode for 1-2 seconds. After removal from the electrodeposition cell, the coated can was vigorously rinsed with demineralized water and the coating was cured by stoving for 5 minutes at 200°C. After curing and measuring the weight of the coating, the porosity was tested by using a WACO ENAMEL RATER (ex Wilkens-Anderson Co. USA). The principle of this method is that when a potential difference (6.2V) is applied between the can filled with an electrolytic solution and an electrode inserted in said electrolytic solution, a current will pass between the electrode and the inner surface of the can only if the coating has insufficient insulating power, i.e. when the film contains pores. Hence the current measured in a yard stick for the film quality. A current < 0.6 mA is considered to correspond with a non porous film. Results are given in Table 5 following, in which solvent resistance is expressed in terms of "MEK rubs", i.e. the number of double rubs with a methylethylketone-moistened cloth necessary to remove the coatings, while the film appearance (flow) is expressed as a numerical rating resulting from a visual assessment (5: smooth surface, excellent flow, no defects, 4: orange-peel type surface, 3: orange-peel type surface and few bubbles and/or pinholes, 2: many bubbles and/or pinholes). The sterilisation resistance of the coatings was determined by exposure to water at 120°C for 90 minutes and rated according to a numerical scale ranging from 5: no blushing to 0: very heavy blushing. The coatings were tested for taste by a taste panel employing mineral water as the taste sensitive beverage. Comparative Example B Cathodic electrodeposition of aqueous lacquer composition from comparative example The aqueous lacquer composition from comparative example A was applied by electrodeposition onto a 330 ml tin-plate can by the same method as described in examples XII-XIV. The results have been incorporated in Table 5. The results in Table 5 indicate that the cationic coating compositions, made according to the process of the present invention, provide coatings of which the performance properties are on the same high level as those of compositions based on the amino binders and the carboxylated crosslinking compounds.

Claims: A process for the proparation of a water-thinnable, hydrolytically stable, thermosetting, cationic coating composition, which comprises blending: 1) 5-35 %w of a crosslinking compound, and 2) 65-95 %w of a carboxylated amide group-containing amino binder being the reaction product of an amino group-containing resin binder and not more than 0.1 mol of a cyclic anhydride per amino group equivalent of said amino group-containing resin binder, which amino group-containing binder comprises the reaction product of a) ammonia, and b) a blend of b₁) a polyglycidyl ether having n epoxy groups per molecule, wherein 1<n<1.9, said polyglycidyl ether being the reaction product of a multifunctional polyglycidyl ether having x epoxy groups per molecule, wherein x>2, and (x-n) mol of a monofunctional phenol per mol of the multifunctional polyglycidyl ether, and b₂) a diglycidyl ether, having an EGC in the range of from 1.0 to 5.5 eq.kg⁻¹ the average molar epoxy functionality of the glycidyl ethers present in the blend of polyglycidyl ether and diglycidyl ether being <1.75. and wherein 1) and 2) are blended before or after neutralization of 2). A process according to claim 1, wherein the multifunctional polyglycidyl ether is an epoxy novolac resin wherein 2.5 < x < 3.5. A process according to claim 1 or 2, wherein the monofunctional phenol is a phenol substituted in the para position by a C 4-12 alkyl substituent. A process according to any of claims 1 to 3, wherein 1.3<n<1.6. A process according to any of claims 1 to 4, wherein the diglycidyl ether is a diglycidyl ether of 2,2-bis(4-hydroxyphenyl)propane, having an EGC in the range of from 1.8 to 2.4. A process according to any of claims 1 to 5, wherein the polyglycidyl ether and the diglycidyl ether are present in the blend as mentioned under b) in a weight ratio in the range of from 75:25 to 45:55. A process according to any of claims 1 to 6, wherein the amino group-containing binder is prepared reacting ammonia with a blend as mentioned under b) at a temperature in the range of from 20 to 120°C and at atmospheric or slightly above atmospheric pressure. A process according to claim 7, wherein at least 4.5 eq of amino-hydrogen per equivalent of epoxy is employed. A process according to any of claims 1 to 8, wherein the cyclic anhydride is reacted with the amino group-containing resin binder at a temperature in the range of from 30 to 120°C. A process according to any of claims 1 to 9, wherein the crosslinking compound and the carboxylated amide group-containing amino binder are present in a weight ratio in the range of from 15:85 to 30:70. A process according to any of previous claims, wherein the crosslinking compound is selected from the group of melamine formaldehyde, urea formaldehyde and phenol formaldehyde resins. Food and beverage cans, internally coated with a coating composition comprising a cured binder composition, the latter resulting from a process as claimed in any one of claims 1 to 11.

Inventors: KOOIJMANS, PETRUS GERARDUS, VAN DER MARK, JOHANNES MARIA, VAN IPEREN, ROELAND
Applicants: SHELL INTERNATIONALE RESEARCH MAATSCHAPPIJ B.V.
Application year: 1987
Main classification: C09D163
IPC codes: C09D5, C08G59, C09D163