ELECTROPHOTOGRAPHIC PHOTORECEPTOR

Abstract: Disclosed herein is an electrophotographic photoreceptor having high sensitivity and excellent durability. The photoreceptor has a photosensitive layer which contains at least one disazo compound having the 2-phenyl-benzooxazole skeleton.

Description: This invention relates to an electrophotographic photoreceptor, and more specifically to an electrophotographic photoreceptor as claimed in claim 1 containing an azo compound as a charge-generating material in a photosensitive layer on an electrically-conductive base. Inorganic photosensitive materials such as selenium, cadmium sulfide and zinc oxide have heretofore been used widely as photosensitive materials for electrophotographic photoreceptors. However, photoreceptors using these photosensitive materials cannot fully satisfy properties required as electrophotographic photoreceptors such as sensitivity, light stability, moisture proofness and durability. For example, photoreceptors making use of selenium-base materials have excellent sensitivity. They are however accompanied by many drawbacks on the other hand. Namely, they are prone to crystallization under heat or by adhesion of smear, so that their characteristic properties as photoreceptors tend to deteriorate. They are fabricated by vacuum evaporation and their fabrication costs are hence high. Due to lack of flexibility, it is difficult to form them into belt-like configurations. Photoreceptors making use of CdS-base materials have problems in moisture proofness and durability, whereas zinc oxide photoreceptors are insufficient in durability. In order to overcome the above-mentioned drawbacks of photoreceptors which use such inorganic photosensitive materials, various photoreceptors making use of organic photosensitive materials have been studied. As organic photosensitive materials which have already found some commercial utility, there are known, for example, photosensitive materials making combined use of 2,4,7-trinitro-9-fluorenone and poly-N-vinylcarbazole. However, photoreceptors using the above photosensitive materials have low sensitivity and their durability is also dissatisfactory. Among photoreceptors developed to improve the above-mentioned drawbacks, photoreceptors each of which comprises a charge-generating layer and a charge-transporting layer having respective allotted functions (hereinafter called "function-separated photoreceptors) have drawn attention in recent years. In such a function-separated photoreceptor, materials having the above functions separately can be chosen from a wide range of materials and can then be used in combination. It is thus possible to fabricate a high-sensitivity and high-durability photoreceptor. As charge-generating materials useful in such function-separated photoreceptors, many materials have been reported. Of these, photoreceptors making use of organic dyes or organic pigments as charge-generating materials have attracted particular attention in recent years. There have been reported, for example, photoreceptors using disazo pigments having the styryl stilbene skeleton (Japanese Patent Laid-Open No. 133445/1978), photoreceptors using disazo pigments having the carbazole skeleton (Japanese Patent Laid-Open No. 95033/1978), photoreceptors using trisazo pigments having the triphenylamine skeleton (Japanese Patent Laid-Open No. 132347/1978), photoreceptors using disazo pigments having the distyryl carbazole skeleton (Japanese Patent Laid-Open No. 14967/1979), photoreceptors using disazo pigments having the bisstilbene skeleton (Japanese Patent Laid-Open No. 17733/1979), etc. DE 3301453 describes disazo naphthylene compounds suitable for incorporation into electrophotographic materials. EP 0034942 describes disazo compounds containing a divalent heterocyclic group which may be condensed with a benzene ring. These electrophotographic receptors cannot however fully satisfy the performance requirements. It has hence been desired to develop still better photoreceptors. SUMMARY OF THE INVENTION An object of this invention is to provide an electrophotographic photoreceptor having sufficient sensitivity and good durability. Another object of this invention is to provide a charge-generating material useful in the electrophotographic photoreceptor. The present inventors have conducted an investigation with a view toward achieving the above objects. As a result, it has been found that disazo compounds, each of which is represented by the following general formula (I): wherein A means a coupler residuum, can provide electrophotographic photoreceptors having excellent characteristics such as higher sensitivity and durability compared with conventional disazo compounds, leading to the present invention consisting of an electrophotographic photoreceptor including an electrically-conductive base and a photosensitive layer provided thereon which contains a charge generating material selected from diazo compounds, characterized in that said charge generating material is at least one disazo compound represented by the following general formula (I): wherein A means a coupler residuum. BRIEF DESCRIPTION OF THE DRAWINGS In the accompanying drawings, FIGURE 1 shows an infrared absorption spectrum of Disazo Pigment No. 1 as measured by the KBr method; and FIGURES 2 and 3 are schematic cross-sectional views showing illustrative examples of the construction of an electrophotographic photoreceptor respectively. DETAILED DESCRIPTION OF THE INVENTION AND PREFERRED EMBODIMENTS Among the disazo compounds represented by the general formula (I), those represented by the following general formula (II) or (III) are particularly suitable. The following residua 1) - 4) may be mentioned by way of example as the coupler residuum A in the general formula (I). 1) Coupler residua of the following general formula (IV): wherein X means a substituted or unsubstituted cyclic hydrocarbon ring or a substituted or unsubstituted heterocyclic ring, Y denotes or in which R₁ means a substituted or unsubstituted cyclic hydrocarbon ring or a substituted or unsubstituted heterocyclic ring, R₂ denotes a hydrogen atom, a substituted or unsubstituted alkyl group or a substituted or unsubstituted phenyl group, R₃ is a substituted or unsubstituted cyclic hydrocarbon ring, a substituted or unsubstituted heterocyclic ring or a substituted or unsubstituted styryl group, R₄ means a hydrogen atom, an alkyl group or a substituted or unsubstituted phenyl group, and R₃ and R₄ may optionally form a ring together with the carbon atom to which R₃ and R₄ are bonded. As illustrative specific examples of X in the general formula (IV), may be mentioned hydrocarbon rings such as naphthalene ring and anthracene rings as well as heterocyclic rings such as indole ring, carbazole ring, benzocarbazole ring and dibenzofuran rings, each of which is fused with the benzene ring to which the hydroxyl group and Y are bonded. Where X is substituted, halogen atoms such as chlorine and bromine and hydroxyl group may be mentioned as exemplary substituents. As illustrative examples of the cyclic group represented by R₁ or R₃, may be mentioned cyclic hydrocarbon groups such as phenyl, naphthyl, anthryl and pirenyl; and heterocyclic groups such as pyridyl, thienyl, furyl, indolyl, benzofuranyl, carbazolyl and dibenzofuranyl. As a ring which R₃ and R₄ form as a result of their coupling, the fluorene ring or the like may be mentioned by way of example. Where R₁ or R₃ is a substituted cyclic ring, illustrative examples of the substituent or substituents may include alkyl groups such as methyl, ethyl, propyl and butyl; alkoxy groups such as methoxy, ethoxy, propoxy and butoxy; halogen atoms such as chlorine and bromine atoms; halomethyl groups such as trifluoromethyl; dialkylamino groups such as dimethylamino and diethylamino; nitro group; cyano group; and carboxyl group and its ester groups. Where R₂ is a phenyl group, halogen atoms such as chlorine and bromine atoms may be mentioned as illustrative substituents for the phenyl group. 2) Coupler residua of the following general formula (V) or (VI): wherein R₅ means a substituted or unsubstituted hydrocarbon group. Illustrative specific examples of R₅ may include alkyl groups such as methyl, ethyl, propyl, butyl and octyl; and alkoxyalkyl groups such as methoxyethyl and ethoxyethyl. 3) Coupler residua of the following general formula (VII): wherein R₆ means alkyl, carbamoyl, or carboxyl or an ester group thereof, R₇ denotes a substituted or unsubstituted cyclic hydrocarbon group. As R₇, cyclic hydrocarbon groups such as phenyl and naphthyl may be mentioned specifically by way of example. Where these groups are substituted, illustrative substituents may include alkyl groups such as methyl, ethyl, propyl and butyl; alkoxy groups such as methoxy, ethoxy, propoxy and butoxy; dialkylamino groups such as dimethylamino and diethylamino; halogen atoms such as chlorine and bromine atoms; nitro group; and cyano group. 4) Coupler residua represented by the following general formula (VIII) or (IX): wherein Z means a substituted or unsubstituted divalent cyclic hydrocarbon group, or a substituted or unsubstituted divalent heterocyclic group. As specific examples of Z, may be mentioned divalent residua of monocyclic aromatic hydrocarbons, such as o-phenylene; divalent residua of fused polycyclic aromatic hydrocarbons, such as o-naphthylene, peri-naphthylene, 1,2-anthraquinonylene and 9,10-phenanthrylene; and divalent residua of heterocyclic rings, such as 3,4-pyrazolediyl, 2,3-pyridinediyl, 4,5-pyrimidinediyl, 6,7-imidazolediyl, 5,6-benzimidazolediyl and 6,7-quinolinediyl. Where these cyclic groups are substituted, exemplary substituents may include alkyl groups such as methyl, ethyl, propyl and butyl; alkoxy groups such as methoxy, ethoxy, propoxy and butoxy; dialkylamino groups such as dimethylamino and diethylamino; halogen atoms such as chlorine and bromine atoms; nitro group; and cyano group. Among the coupler residua exemplified above, the coupler residua represented by the general formula (IV) are most preferable for their high optical sensitivity, easier availability of their intermediate raw materials and their low production costs. Disazo compounds useful in the practice of this invention will next be exemplified more specifically by their structural formulae in Tables 1 and 2. The disazo compounds represented by the general formula (I) can be prepared in a manner known per se in the art. For example, they may be synthesized by the following reaction scheme. Namely, the methyl-substituted derivative of an o-aminophenol such as 6-amino-m-cresol or 2-amino-4-methylphenol and p-toluic acid are subjected to a condensation and ring-closure reaction under heat in polyphosphoric acid, thereby to obtain the compound (a). N-bromosuccinimide is then reacted to bromomethylate, whereby the compound (b) is obtained. After reacting triethyl phosphite to form the compound (c), p-nitrobenzaldehyde is reacted to obtain the compound (d). The compound (d) is thereafter reduced to obtain the diamine compound (e) which is a precursor of the compound of the general formula (I). The disazo compound of the general formula (I) can be prepared easily, for example, by converting the compound (e) into a tetrazo form and then coupling it with a coupler in the presence of an alkali or by isolating the above-mentioned tetrazonium salt of the diamine in the form of a borofluoride and then causing a base to act on the borofluoride in a suitable organic solvent, e.g., N,N-dimethylformamide so as to induce a coupling reaction. The electrophotographic photoreceptor of this invention contains at least one of such disazo compounds, which are represented by the general formula (I), as a charge-generating material in a photo-conductive layer on an electrically-conductive base. Typical constructions of such a photoreceptor are illustrated respectively in FIGURES 2 and 3 by way of example. Namely, the photoreceptor of FIGURE 2 is a dispersion-type photoreceptor, in which a photosensitive layer 4 containing a charge-generating material 2 and a charge-transporting material 3 in a binder is provided on an electrically-conductive base 1. The photoreceptor of FIGURE 3 is a laminated photoreceptor which includes, on an electrically-conductive base 1, a charge-generating layer 6 with a charge-generating material 2 contained in a binder and a charge transporting layer 5 with a charge-transporting material 3 contained in a binder. In the aforementioned laminated photoreceptor, the positions of the charge-generating layer and charge-transporting layer may be opposite. Intermediate layer(s) may be disposed between the photosensitive layer and the electrically-conductive base. In the photoreceptor of FIGURE 3, light which has been obtained subsequent to exposure of a picture or mark transmits through the charge-transporting layer, whereby the charge-generating material generates charges in the charge-generating layer. The thus-produced charges are charged into the charge-transporting layer, so that the charge-transporting material performs their transportation. The electrophotographic photoreceptor of this invention is composed of an electrically-conductive base, a binder, a charge-transporting material and the like in addition to the disazo compound of the general formula (I). No particular limitation is however imposed on other components or elements of the photoreceptor so long as they have functions as components or elements for photoreceptors. As illustrative examples of the electrically-conductive base useful in the practice of this invention, may be mentioned metal plates such as aluminium, copper and zinc plates, those obtained by depositing an electrically-conductive material such as aluminium or SnO₂ on plastic sheets or films such as polyester sheets or films, and paper rendered electrically conductive. As binders, may be used vinyl polymers such as polystyrene, polyacrylamide and poly-N-vinylcarbazole as well as condensation polymers such as polyamide resins, polyester resins, epoxy resins, phenoxy resins and polycarbonate resins. Any resins may be used as binders, so long as they are electrically insulating and have close adhesion to bases. Charge-transporting materials may generally be classified into two kinds, one being hole-transporting materials and the other electron-transporting materials. In the photoreceptor of this invention, both kinds of charge-transporting materials can be used. In addition to electron-receptive materials having ability to transport electrons such as trinitrofluorenone and tetranitrofluorenone, the following materials may be mentioned as exemplary hole-transporting materials: electron-donative materials having ability to transport holes, such as polymers containing heterocyclic compounds typified by poly-N-vinylcarbazole; triazole derivatives; oxadiazole derivatives; imidazole derivatives; pyrazoline derivatives; polyarylalkane derivatives; phenylenediamine derivatives; hydrazone derivatives; amino-substituted chalcon derivatives; triarylamine derivatives; carbazole derivatives; and stilbene derivatives. There are, for example, 9-ethylcarbazole-3-aldehyde-1-methyl-1-phenylhydrazone, 9-ethylcarbazole-3-aldehyde-1-benzyl-1-phenylhydrazone, 9-ethylcarbazole-3-aldehyde-1,1-diphenylhydrazone, 4-diethylaminostyrene-β-aldehyde-1-methyl-1-phenylhydrazone, 4-methoxynaphthalene-1-aldehyde-1-benzyl-1-phenylhydrazone, 4-methoxybenzaldehyde-1-methyl-1-phenylhydrazone, 2,4-dimethoxybenzaldehyde-1-benzyl-1-phenylhydrazone, 4-diethylaminobenzaldehyde-1,1-diphenylhydrazone, 4-methoxybenzaldehyde-1-benzyl-1-(4-methoxy)phenylhydrazone, 4-diphenylaminobenzaldehyde-1-benzyl-1-phenylhydrazone, 4-dibenzylaminobenzaldehyde-1,1-diphenylhydrazone, 1,1-bis(4-dibenzylaminophenyl)propane, tris(4-diethylaminophenyl)methane, 1,1-bis(4-dibenzylaminophenyl)propane, 2,2′-dimethyl-4,4′-bis(diethylamino)-triphenylmethane, 9-(4-diethylaminostyryl)anthracene, 9-bromo-10-(4-diethylaminostyryl)anthracene, 9-(4-dimethylaminobenzylidene)fluorene, 3-(9-fluorenylidene)-9-ethylcarbazole, 1,2-bis(4-diethylaminostyryl)benzene, 1,2-bis(2,4-dimethoxystyryl)benzene, 3-styryl-9-ethylcarbazole, 3-(4-methoxystyryl)-9-ethylcarbazole, 4-diphenylaminostilbene, 4-dibenzylaminostilbene, 4-ditolylaminostilbene, 1-(4-diphenylaminostyryl)naphthalene, 1-(4-diethylaminostyryl)naphthalene, 4′-diphenylamino-α-phenylstilbene, 4′-methylphenylamino-α-phenylstilbene, 1-phenyl-3-(4-diethylaminostyryl)-5-(4-diethylaminophenyl)pyrazoline, and 1-phenyl-3-(4-dimethylaminostyryl)-5-(4-dimethylaminophenyl)pyrazoline. As other hole-transporting materials, may be mentioned, for example, 2,5-bis(4-diethylaminophenyl)-1,3,4-oxadiazole, 2,5-bis[4-(4-diethylaminostyryl)phenyl]-1,3,4-oxadiazole, 2-(9-ethylcarbazolyl-3-)-5-(4-diethylaminophenyl)-1,3,4-oxadiazole, 2-vinyl-4-(2-chlorophenyl)-5-(4-diethylaminophenyl)oxazole, 2-(4-diethylaminophneyl)-4-phenyloxazole, 9-[3-(4-diethylaminophenyl)-2-propenylidene]-9H-xanthene, poly-N-vinylcarbazole, halogenated poly-N-vinylcarbazoles, polyvinylpyrene, polyvinylanthracene, pyreneformaldehyde resins, and ethylcarbazole-formaldehyde resins. As exemplary electron-transporting materials, may be mentioned chloroanil, bromoanil, tetracyanoethylene, tetracyanoquinodimethane, 2,4,7-trinitro-9-fluorenone, 2,4,5,7-tetranitro-9-fluorenone, 2,4,5,7-tetranitroxanthone, 2,4,8-trinitrothioxanthone, 2,6,8-trinitro-4H-indino[1,2-b]thiophen-4-one and 1,3,7-trinitrodibenzothiophene-5,5-dioxide. These charge-transporting materials may be used either singly or in combination. Between the photosensitive layer and the electrically-conductive layer, an intermediate layer may be provided as needed. Polyamide, nitrocellulose, casein, polyvinyl alcohol or the like is suitable as its material. The thickness of the intermediate layer may preferably be 1 µm or less. For the fabrication of the photoreceptor, conventionally-known processes may be used. In the case of a laminated photoreceptor, fine particles of a disazo compound is dispersed in a solution in which a binder has been dissolved in advance. The resultant coating formulation is applied onto an electrically-conductive base and is then dried to obtain a charge-generating layer. Thereafter, a solution with a charge-transporting material and a binder dissolved therein is coated and then dried to form a charge-transporting layer. Other methods may also be used to form such a charge-producing layer. For example, a disazo pigment may be applied by vacuum evaporation. Alternatively, a solution of a disazo pigment may be coated and then dried. The former method is however accompanied by a drawback that the fabrication cost is high. The latter method involves drawbacks in operation, because it uses an organic amine which is generally inconvenient to handle, e.g., ethylenediamine or n-butylamine. It is therefore suitable to coat a dispersion of fine particles of a disazo compound. The coating may be effected by a usual method, for example, by the doctor blade method, dipping method or wire bar method. The optimal thickness range of each photo-sensitive layer varies depending on the kind of the associated photoreceptor. For example, the thickness may preferably be 3 - 50 µm with 5 - 30 µm being more preferable in the case of such a photoreceptor as shown in FIGURE 2. In the case of a photoreceptor such as that shown in FIGURE 3, the thickness of the charge-generating layer 6 may preferably be 0.01 - 5 µm with 0.05 - 2 µm being more preferred. If this thickness is less than 0.01 µm, the generation of charges is not sufficient. On the other hand, any thicknesses greater than 5 µm are not preferred from the practical viewpoint since such large thicknesses lead to high residual potentials. Further, the thickness of the charge-transporting layer 5 may preferably be 3 - 50 µm with 5 - 30 µm being more preferred. Any thicknesses smaller than 3 µm cannot achieve any sufficient charge level, whereas any thicknesses greater than 50 µm are not preferable from the practical viewpoint because such large thicknesses lead to high residual potentials. The content of the disazo compound of the general formula (I) in the photosensitive layer varies in accordance with the kind of each photoreceptor. In the case of such a photoreceptor as shown in FIGURE 2, the disazo compound may be contained preferably in an amount of 50 wt.% or less, more preferably, in an amount of 20 wt.% or less in the photosensitive layer 4. Further, a charge-transporting material is also added preferably in a proportion of 10 - 95 wt.%, more preferably, in a proportion of 30 - 90 wt.% to the photosensitive layer 4. In the case of such a photoreceptor as depicted in FIGURE 3, the proportion of the disazo compound in the charge-generating layer 5 may preferably be at least 30 wt.% with at least 50 wt.% being more preferred. In addition, 10 - 95 wt.%, preferably, 30 - 90 wt.% of a charge-transporting material is incorporated in the charge-transporting layer 6. If the content of the charge-transporting material in this layer is less than 10 wt.%, the transportation of charges is not effected substantially. On the other hand, any amounts in excess of 95 wt.% are not preferable from the practical viewpoint because the mechanical strength of the photoreceptor is reduced. Owing to the use of the disazo compound represented by the general formula (I) as a charge-generating material, the electrophotographic photoreceptor of this invention is easy to fabricate and has excellent properties that its sensitivity is high and its performance does not deteriorate through repeated use. The present invention will hereinafter be described specifically by the following Examples. It should however be borne in mind that this invention is not limited to or by the following Examples. Preparation Example 1: In a solution consisting of 600 mℓ of water and 15 mℓ of 35% hydrochloric acid, was suspended 2.2 g of a diamine compound represented by the following structural formula: After allowing the resultant suspension to stand overnight, a solution of 1.1 g of sodium nitrite in 20 mℓ of water was added dropwise at 0 - 5°C, followed by stirring at the same temperature for 3 hours. After removing insoluble matter, 15 mℓ of 42% borofluoric acid was added. A precipitate, which had crystallized out, was collected by filtration and then dried, thereby obtaining 2.4 g of tetrazonium difluoroborate (yield: 74%). Dissolved next in 200 mℓ of N,N-dimethylformamide were 2.0g of the above-obtained tetrazonium difluoroborate and 1.7 g of 2-hydroxy-3-naphthoic anilide, followed by a dropwise addition of a solution of 1.5 g of sodium acetate and 30 mℓ of water at 0 - 5°C over 30 minutes. After stirring the reaction mixture for 2 hours at the same temperature, the temperature of the reaction mixture was allowed to rise to room temperature and the reaction mixture was stirred overnight. Crystals which had been collected by filtration were repeatedly subjected to dispersion four time into 200 mℓ portions of N,N-dimethylformamide and 5 times into 200 mℓ portions of water. The crystals were then dried to obtain 2.6 g of the disazo compound of the above Compound No.1 (yield: 75.8%). The thus-obtained powder had a bluish black color and did not melt up to 300°C. It was confirmed to be the intended product from its elemental analysis data and infrared absorption spectrum (measured by the KBr method). IR absorption spectrum: Absorption based on >C=O: 1660 cm⁻¹ The IR absorption spectrum (measured by the KBr method) is shown in FIGURE 1. Preparation Examples 2 - 8: Various disazo compounds shown in Table 3 were synthesized in the same manner as in Preparation Example 1 except that the compounds corresponding to disazo compounds shown in Table 3 were used as coupler compounds in lieu of 2-hydroxy-3-naphthoic anilide. Preparation Example 9: The disazo dyestuff of the above Compound No. 47 was synthesized in the same manner as in Preparation Example 1 except that a diamine compound represented by the following structural formula: Preparation Examples 10 - 15: Various disazo compounds shown in Table 3 were synthesized in the same manner as in Preparation Example 9 except that the compounds corresponding to disazo compounds shown in Table 3 were used as coupler compounds in lieu of 2-hydroxy-3-naphthoic anilide. Elemental analysis data, infrared absorption spectra (the KBr method, ν C=0 ) and melting points of the disazo compounds obtained in Preparation Examples 2 - 15 respectively are given in Table 3. Example 1: In a ball mill, 0.5 part of a polyester resin (trade name: "Adhesive 49000", product of E.I. du Pont de Nemours & Co., Inc.), 0.5 part of Disazo Compound No. 1 and 50 parts of tetrahydrofuran were ground and mixed. An aluminium plate was coated with the thus-obtained dispersion by a wire bar, followed by drying at 80°C for 20 minutes to form a charge-generating layer of about 1 µm thick. Coated over the charge-generating layer by means of a wire bar was a solution of 1 part of 9-ethylcarbazole-3-aldehyde-1-methyl-1-phenylhydrazone and 1 part of a polyester resin (trade name: "Vyron 200", product of Toyobo Co., Ltd.) in 10 parts of chloroform. The thus-coated solution was dried at 80°C for 30 minutes to form a charge-transporting layer of about 18 µm thick, thereby fabricating the laminated photoreceptor shown in FIGURE 3. Using a testing apparatus for electrostatic copying paper ("Model EPA-8100", trade name; manufactured by Kawaguchi Denki Seisakusho, Co. Ltd.), the photoreceptor was charged by a corona discharge at an impression voltage of -6 KV. The surface potential V 0 at that time was measured. The receptor was left over for 2 seconds in a dark place and the surface potential V₂ at that time was also measured. Under conditions such that the surface illuminance of the photoreceptor reached 5 lux, the photoreceptor was exposed to light from a halogen lamp (color temperature: 2856°K) and the exposure time required to reduce the surface potential V₂ to one half was measured. A half-value exposure E ½ (lux·sec) was then calculated. In addition, the surface potential V R after exposure to light for 10 seconds, i.e., the residual potential was also measured. Examples 2 - 9: Photoreceptors were separately fabricated in the same manner as in Example 1 except that Disazo Compound Nos. 3, 12, 32, 36, 45, 47, 49 and 69 were respectively used in place of Disazo Compound No. 1, followed by measurement of their E ½ values. Results are shown in Table 4. Examples 10 - 18: Photoreceptors were separately fabricated in the same manner as in Example 1 except that 1-phenyl-3-(4-diethylaminostyryl)-5-(4-diethylaminophenyl)pyrazoline was employed as a charge-transporting material in lieu of 9-ethylcarbazole-3-aldehyde-1-methyl-1-phenylhydrazone and disazo compounds shown in Table 5 were used as charge-generating materials respectively, followed by measurement of their E ½ values. Results are shown in Table 5. Examples 19 - 25: Photoreceptors were separately fabricated in the same manner as in Example 1 except that 2,5-bis(4-diethylaminophenyl)-1,3,4-oxadiazole was employed as a charge-transporting material in lieu of 9-ethylcarbazole-3-aldehyde-1-methyl-1-phenylhydrazine and disazo compounds shown in Table 6 were used as charge-generating materials respectively, followed by measurement of their E ½ values. Results are shown in Table 6. Comparative Example 1: A photoreceptor was fabricated in the same manner as in Example 1 except that a disazo compound of the following structural formula: which is disclosed in Japanese Patent Publication No. 42380/1980, was used as a charge-generating material. E ½ was 12.0 (lux·sec). Comparative Example 2: A photoreceptor was fabricated in the same manner as in Example 1 except that a disazo compound of the following structural formula: which is disclosed in Japanese Patent Laid-Open No. 202451/1983, was used as a charge-generating material. E ½ was 11.4 (lux·sec). Example 26: Separately using the photoreceptors fabricated in Examples 1, 8 and 11 respectively, an electrification-exposure operation was repeated 1,000 times to obtain values shown in Table 7. As has been described above, the electrophotographic photoreceptor making use of the disazo compound of this invention has high sensitivity and shows stable performance even when used repeatedly. Accordingly, the electrophotographic photoreceptor of this invention is also considered to be excellent in durability. The electrophotographic photoreceptor of this invention can therefore be used widely not only in electrophotographic copying machines but also in various printers and electrophotographic plate-making systems both of which make use of the principle of electrophotographic copying.

Claims: An electrophotographic photoreceptor comprising an electrically-conductive base and a photosensitive layer provided thereon which contains a charge generating material selected from diazo compounds, characterised in that said charge generating material is at least one disazo compound represented by the following general formula (I): wherein A means a coupler residuum. The electrophotographic photoreceptor as claimed in Claim 1, wherein the disazo compound is represented by the following general formula (II): wherein A means a coupler residuum. The electrophotographic photoreceptor as claimed in Claim 1, wherein the disazo compound is represented by the following general formula (III): wherein A means a coupler residuum. The electrophotographic photoreceptor as claimed in Claim 1, wherein the photosensitive layer contains at least a charge-transporting material and a binder in addition to the disazo compound. The electrophotographic photoreceptor as claimed in Claim 4, wherein the content of the disazo compound in the photosensitive layer is at most 50 wt.%. The electrophotographic photoreceptor as claimed in Claim 4, wherein the content of the charge-transporting material in the photosensitive layer is 10-95 wt.%. The electrophotographic photoreceptor as claimed in Claim 1, wherein the photosensitive layer is a laminate of a charge generating layer which contains the disazo compound, and a charge transporting layer which contains a charge-transporting material. The electrophotographic photoreceptor as claimed in Claim 7, wherein the content of the disazo compound in the charge generating layer is at least 30 wt.%. The electrophotographic photoreceptor as claimed in Claim 7, wherein the content of the charge-transporting material in the charge transporting layer is at least 10-95 wt.%.

Inventors: ITOH, HISATO MITSUI TOATSU APAATO 2-18, NISHIZAWA, TSUTOMU, YAMADA, YASUYUKI MITSUI TOATSU APAATO 2-37, YAMAGUCHI, AKIHIRO
Applicants: MITSUI TOATSU CHEMICALS, INC.
Application year: 1987
Main classification: G03G5
IPC codes: G03G5, C09B56, G03C1