USE OF A COATING

Abstract: A coating composition comprising a film forming binder and at least one of 3,3,4,4-tetrachlorotetrahydrothiophene-1,1-­ dioxide and 3,3,4-trichlorotetrahydrothiophene-1,1-dioxide as an effective ingredient is highly useful as an underwater antifouling agent.

Description: This invention relates to the use of a coating composition. More particularly, this invention relates to a low-toxic antifouling coating composition for inhibiting the adhesion and growth of underwater organisms on the surface of ships, port facilities, buoys, pipelines, bridges, submarine bases, excavators for submarine oil fields, raceways in power plants, culture nets, fixed shore nets etc. (hereinafter referred to briefly as underwater structures). JP-A-59/175406 describes a composition comprising a compound of the formula (wherein R¹ is H, a lower alkyl or aryl, R² is H or a hydroxy-substituted lower alkyl, and X is a halogen) and 3,3,4,4-tetrachlorotetrahydrothiophene-1,1-dioxide. In the same way, JP-A-59/193808 and US-A-3 822 351 describe a combination agent between 3,3,4,4-tetrachlorotetrahydrothiophene-1,1-dioxide and a second active compound. In the sea, rivers, lakes and marshes, many underwater organisms such as acorn barnacles, sea squirts, serpula, Mytilus edulis , fresh-water mussels, Bugula neritina , green laver or sea lettuce present fouling problems with respect to the above underwater structures and the adhesion and growth of these organisms on the surface or on the splashed parts of the underwater structures cause considerable damages. For example, when organisms adhere to ships' hulls, the frictional resistance increases and the sailing speed decreases, and thereby maintaining a fixed speed results in increased fuel consumption. This gives rise to economical disadvantage. In the case where underwater organisms adhere to port facilities, the materials thereof are often eroded. Where the organisms adhere to culture nets or fixed shore nets, the mesh of these nets become blocked. Hitherto, for the purpose of inhibiting the adhesion and growth of underwater organisms, antifouling coating compositions containing a highly toxic antifouling agent, such as organotin or cuprous oxide have been coated to the surface of underwater structures, so that the adhesion and growth of underwater organisms could be inhibited. However, the highly toxic antifouling agents are harmful to environmental safety and hygiene when these coating compositions are produced or actually used. Moreover, these highly toxic antifouling agents gradually dissolve out of the coating composition film formed on the surface of the underwater structures, thereby causing water pollution and unfavorable effects on desirable underwater life such as fish, shellfish etc. Accordingly, the development of antifouling coating compositions which exert excellent antifouling effects over a prolonged period, and are of low toxicity to humans and desirable underwater life have been strongly demanded. The present inventors have conducted studies to obtain coating compositions which are of low toxicity to humans and desirable underwater life, yet exhibit strong antifouling activity against underwater organisms. As a result, the present inventors have found that two compounds as explained hereinafter are very safe, yet exhibit excellent antifouling effects. These findings were followed by continued studies, which have culminated in the present invention. The present invention provides the use of a composition which comprises a film forming binder, selected from vinyl chloride-vinyl acetate copolymers, vinyl chloride-vinyl isobutyl ether copolymers, styrene-butadiene copolymers, chlorinated rubber resins, chlorinated polypropyrene resins, petroleum resins, alkyd resins, acryl resins, phenolic resins, synthetic rubbers, epoxy resins, silicon rubbers, silicon resins, teflon resins or rosin resins and at least one of 3,3,4,4-tetrachlorotetrahydrothiophene-1,1-dioxide and 3,3,4-trichlorotetrahydrothiophene-1,1-dioxide as effective ingredient in the film forming binder as an underwater antifouling agent. The effective ingredients are at least one of 3,3,4,4-tetrachlorotetrahydrothiophene-1,1-dioxide, i.e. a compound of the formula: and 3,3,4-trichlorotetrahydrothiophene-1,1-dioxide, i.e. a compound of the formula: 3,3,4,4-tetrachlorotetrahydrothiophene-1,1-dioxide and 3,3,4-trichlorotetrahydrothiophene-1,1-dioxide (hereinafter these will be referred to simply as low-toxic antifouling agents) are known (see U.S.P.2,957,887, U.S.P.3,821,396, U.S.P.3,822,351), but the antifouling effects of these compounds against underwater organisms have not been known until now. The present inventors found that these compounds exert excellent antifouling effects against undesirable underwater organisms equal or superior to cuprous oxide-copolymer or tributyltin-copolymer. That is, the above two low-toxic antifouling agents dissolve into water out from the coating composition film formed on the surface of the underwater structures so that they can combat underwater organisms in the neighborhood of the coating composition film. The above mentioned two low-toxic antifouling agents can prevent the adhesion as well as the growth of underwater organisms. Futhermore, the above low-toxic antifouling agents unexpectedly decompose rapidly as soon as the antifouling agents dissolve into water, to lose toxicity against humans, fish and shellfish. It has been experimentally proven that the above low-toxic antifouling agents do not cause any adverse effects, even if they have been absorbed by humans, fish and shellfish. One or both of the low-toxic antifouling agents are desirably used in an amount of about 0.1% to 50%, more preferably about 0.5% to 25% by weight of the total coating composition. The antifouling coating composion of the present invention which contains one or both of the above low-toxic antifouling agents exerts a very strong effect, but may additionally contain one or more of the conventional antifouling agents, such as organotin compounds e.g. triphenyltin hydroxide, triphenyltin chloride, triphenyltin fluoride, triphenyltin acetate, triphenyltin dimethyldithiocarbamate, bis(triphenyltin) oxide, tri(phenyltin) versatic acid, tri(phenyltin) nicotinic acid, triphenyltin α , α '-dibromosuccinate, triphenyltin monochloroacetate, tributyltin fluoride, bis(tibutyltin) α , α '-dibromosuccinate or tributyltin methacrylate-copolymer; organochlorines e.g. DDT or BHC; thiurams e.g. tetraalkylthiuram disulfide; carbamates e.g. zinc dimethyldithiocarbamate; or cuprous oxide. Referring to the antifouling coating composition of the present invention, a film forming binder for coating compositions is employed as one of the vehicles of the composition . As the film forming binder, those film forming materials which are conventionally used in antifouling coating compositions may be employed. The examples of the film forming binder include a polymeric binder such as vinyl chloride-vinyl acetate copolymers, vinyl chloride-vinyl isobutyl ether copolymers, styrene-butadiene copolymers, chlorinated rubber resins, chlorinated polypropyrene resins, petroleum resins, alkyd resins, acryl resins, phenolic resins, synthetic rubbers, epoxy resins, silicon rubbers, silicon resins, teflon resins or rosin resins. Among these, silicon rubbers and silicon resins are preferred to improve the antifouling effect of the present invention. The antifouling coating composition of the present invention may additionally include plasticizers for the purpose of regulating the physical properties of antifouling coating composition film. The examples of the plasticizers include phthalate derivatives such as diethyl phthalate, dibutyl phthalate, diisobutyl phthalate, dioctyl phthalate, butyl benzyl phthalate or glycol acid butyl phthalate; phosphate derivatives such as tricresyl phosphate, triphenyl phosphate or diphenyl cresyl phosphate; epoxy derivaties such as epoxy bean oil; paraffin; and paraffin derivaties such as chlorinated paraffin. In the antifouling coating composition used in the present invention, 3,3,4,4-tetrachlorotetrahydrothiophene-1,1-dioxide or/and 3,3,4-trichlorotetrahydrothiophene-1,1-dioxide may usually be used in an amount of about 1 to 350 weight parts, preferably about 5 to 150 weight parts more preferably 5 to 80 weight parts per 100 weight parts of the film forming binder (solids component) for the coating composition. The above mentioned plasticizers may be incorporated into the composition of the present invention in an amount not more than 20 weight parts per 100 weight parts of the film forming binder for the coating composition. The antifouling composition used in the present invention may additionally include known coloring pigments such as red iron oxide, titanium dioxide, carbon, phthalocyanine blue B or cyanine green or/and filler or body pigments, such as talc, barium oxide or zinc oxide. The composition used in the present invention may additionally contain organic solvents for the purpose of regulating the viscosity of coating composition. The examples of the organic solvents include any solvent which can dissolve or disperse the film forming binder or plasticizers as mentioned above, such as hydrocarbons, e.g. xylene or toluene; ketones, e.g. methyl ethyl ketone or methyl isobutyl ketone; esters, e.g. butyl acetate or ethyl acetate. The coating composition used in the present invention is produced by per se known procedures, for example by admixing the above mentioned ingredients. The coating composition used in the present invention may be formulated into a water-insoluble type of matrix in which low toxic antifouling agent comprising 3,3,4,4-tetrachlorotetrahydrothiophene-1,1-dioxide or/and 3,3,4-trichlorotetrahydrothiophene-1,1-dioxide (as well as the conventional antifouling agents if they are incorporated) dissolve in water and a water-soluble type of matrix in which the film forming binder dissolves in water together with the above active ingredients. The new use of the coating composition of the present invention is preferably a marine antifouling coating composition. The coating composition film obtained from the antifouling coating composition of the present invention exhibits particularly good antifouling effects against acorn barnacles. A composition of the above low toxic antifouling agents with the conventional antifouling agent possesses a higher degree of antifouling activity against underwater organisms, in comparison with the composition containing either of the above low toxic antifouling agents. Below are illustrative examples of the preparation of the new use of the coating composition of the present invention. In the examples all parts are parts by weight and all % are % by weight, unless otherwise specified. Example 1 Pliolite S-5 (B) [trade name of a commercial product of Goodyear Co. (U.S.A.), solid component: 100 % styrene-butadiene copolymer] 10 parts rosin 10 parts Adekacizer E 450 [trade name of a commercial product of Adeka Argus Chemical Co., Ltd. (Japan), component: chlorinated n-paraffin] 5 parts The above ingredients were dissolved in 34 parts of xylene, followed by admixing the additional ingredients as described below. 3,3,4,4-tetrachlorotetrahydrothiophene 1,1-dioxide 10 parts red iron oxide 5 parts talc 20 parts Aerosil® [trade name of a comercial product of Degussa Co. (West Germany), component: silicon oxide] 1 part The obtained mixture was further mixed to give a uniform coating composition. Examples 2 to 7 and Comparative Examples 1 to 2 In accordance with formulations of the following Table 1, the coating compositions of Examples 2 to 7 and Comparative Examples 1 to 2 were obtained by the same procedure as in Example 1. Test Example 1 Sandblast boards were coated with an anticorrosive paint made from chlorinated rubbers and dried at room temperature to obtain undercoated sandblast boards. Each of the thus obtained boards was coated with each of the coating compositions of Examples 1 to 7 and Comparative Examples 1 to 2 and the thickness of the dried coating composition film was about 60µm. After drying at room temperature, the boards were submerged by use of a raft in Toba Bay, Mie prefecture, Japan for 6 months or 12 months and then area of surface to which underwater organisms adhered was measured. The results were shown by means of % in Table 2. As for Comparative Example 3, the undercoated sandblast board was used also as a test material. Table 2 clearly shows that the new use of the coating compositions of the present invention exert a much superior antifouling effect than the composition of the Comparative Examples.

Claims: Use of a composition which comprises a film forming binder, selected from vinyl chloride-vinyl acetate copolymers, vinyl chloride-vinyl isobutyl ether copolymers, styrene-butadiene copolymers, chlorinated rubber resins, chlorinated polypropyrene resins, petroleum resins, alkyd resins, acryl resins, phenolic resins, synthetic rubbers, epoxy resins, silicon rubbers, silicon resins, teflon resins or rosin resins and at feast one of 3,3,4,4-tetrachlorotetrahydrothiophene-1,1-dioxide and 3,3,4-trichlorotetrahydrothiophene-1,1-dioxide as effective ingredient in the film forming binder as an underwater antifouling agent. The use as claimed in claim 1, wherein the effective ingredient is 3,3,4,4-tetrachlorotetrahydrothiophene-1,1-dioxide. The use as claimed in claim 1, wherein the amount of effective ingredient is in the range of about 0.1 % to 50 % by weight of the total coating composition.

Inventors: SUMINA, IKUO, WATANABE, TAKASHI
Applicants: TAKEDA CHEMICAL INDUSTRIES, LTD.
Application year: 1987
Main classification: C09D5
IPC codes: C09D5