EPOXY GROUP CONTAINING DISILAZANE AND METHOD FOR ITS PRODUCTION

Abstract: An epoxy group-containing disilazane having the formula, is described. Also described is a process for producing the epoxy group-containing disilazane. The process comprises reacting a disilazane having the formula, with an epoxy compound selected from a group consisting of allyl glycidyl ether and vinylcyclohexene oxide in the presence of a platinum-type catalyst.

Description: This invention relates to a novel epoxy group-containing disilazane. In addition, this invention relates to a method for producing the epoxy group-containing disilazane. Gamma-glycidoxypropyltrimethoxysilane and beta-(3,4-epoxycyclohexyl)ethyltrimethoxysilane are known in the art as epoxy group-containing organosilanes and are used as epoxy-substituted organosilylating agents. See Dow Corning Product Bulletins for Z-6040 Silane and Z-6076 Silane. However, neither epoxy group-containing disilazanes nor a method for their production are known at present. The object of the present invention is to provide both epoxy group-containing disilazanes and a method for their production. In accordance with the instant invention, there is provided an epoxy group-containing disilazane. What is described, therefore is an epoxy group-containing disilazane having the formula, wherein R is a monovalent hydrocarbon group selected from alkyl, substituted alkyl, aryl and substituted aryl, and A is The monovalent hydrocarbon group, R, is exemplified by alkyl groups such as methyl, ethyl, propyl, and octyl; substituted alkyl groups such as 2-phenylethyl, 2-phenylpropyl, and 3,3,3-trifluoropropyl; aryl groups such as phenyl and tolyl; and substituted aryl groups. The epoxy group-containing disilazane of the invention is concretely exemplified by The epoxy group-containing disilazane of the instant invention finds utility as a silylating agent for various organic compounds and organosilicon compounds, as well as an organosilylating agent for solid substrates. The instant invention also provides for a process for the production of an epoxy group-containing disilazane. What is described, therefore, is process for producing an epoxy group-containing disilazane, said process comprising reacting a disilazane having the formula, with an epoxy compound selected from a group comprising allyl glycidyl ether and vinylcyclohexene oxide in the presence of a platinum-type catalyst; where R is a monovalent hydrocarbon group, as defined above. The disilazane is concretely exemplified by Platinum-type catalysts operative in the present invention are exemplified by finely divided platinum, finely divided platinum adsorbed on a carbon powder support, chloroplatinic acid, alcohol-modified chloroplatinic acid, olefin complexes of chloroplatinic acid, chloroplatinic acid-vinylsiloxane coordination compounds, platinum black, palladium and rhodium. The quantity of use of the platinum-type catalyst will vary with the type of catalyst used, and so cannot be specifically restricted. However, it is preferably in a range from about 0.1 to 1,000 ppm as platinum-type metal proper based on the weight of the disilazane. The reaction temperature is not specifically restricted, but is preferably in a range from about 20°C to 300°C. The atmosphere in the reaction system also is not specifically restricted, and can be air or an inert gas, at ambient pressure or under elevated pressure. The simultaneous use is also permissible of an aromatic hydrocarbon solvent such as benzene, toluene or xylene; a ketone solvent; or a chlorinated hydrocarbon solvent. So that those skilled in the art may better understand and appreciate the instant invention, the following examples are presented. The examples are presented as being illustrative and are not to be construed as limiting the claims as delineated herein. Example 1: 27.4 g (0.24 mole) of allyl glycidyl ether was placed in a 100 ml four-neck flask equipped with a thermometer, stirrer, reflux condenser, and addition funnel. A vinylsiloxane complex of chloroplatinic acid was then added to give 50 ppm as platinum metal proper based on the tetramethyldisilazane whose addition followed. After heating to 140°C, 13.4 g (0.1 mole) of tetramethyldisilazane was gradually dripped in with stirring. The vigorous evolution of heat was observed during this addition. After addition, stirring was continued at 140°C for 30 minutes, followed by distillation in vacuo to afford 32 g of a fraction at 170°C/2 mmHg. The results of elemental analysis, nuclear magnetic resonance analysis, and infrared absorption spectral analysis confirmed the product to be a compound having the formula, Known methods of elemental analysis were used to determine carbon, hydrogen, and nitrogen content of the product. The following is a comparison of the analysis and the calculated content of these elements: The results of nuclear magnetic resonance analysis (δ ppm) were: The results of infrared absorption spectral analysis (cm⁻¹) were: 3300, 3030, 2980, 2940, 2920, 2850, 1340, 1260, 1170, 1095, 930, 835, 790. Example 2: 29.8 g (0.24 mole) of vinylcyclohexene oxide was placed in a 100 ml four-neck flask equipped with a thermometer, stirrer, reflux condenser, and addition funnel. To this was added 2 weight percent isopropanolic chloroplatinic solution sufficient to give 50 ppm as platinum metal proper based on the tetramethyldisilazane whose addition followed. After heating to 140°C, 13.4 g (0.1 mole) of tetramethyldisilazane was gradually dripped in with stirring. The vigorous evolution of heat was observed during this addition. After addition, heating was continued for 30 minutes at 140°C with stirring, followed by distillation in vacuo to obtain 34 g of a fraction at 145°C/0.3 mmHg. The results of elemental analysis, nuclear magnetic resonance analysis, and infrared absorption spectral analysis confirmed the product to be a compound having the formula, Known methods of elemental analysis were used to determine carbon, hydrogen, and nitrogen content of the product. The following is a comparison of the analysis and the calculated content of these elements: The results of nuclear magnetic resonance analysis (δ ppm) were: The results of infrared absorption spectral analysis (cm⁻¹) were: 3300, 3010, 2980, 2920, 2850, 1320, 1260, 1175, 1090, 920, 840.

Claims: An epoxy group-containing disilazane having the formula, wherein each R is independently selected and is a monovalent hydrocarbon group selected from a group consisting of alkyl groups, substituted alkyl groups, aryl groups, and substituted aryl groups, and A is An epoxy group-containing disilazane, according to Claim 1, wherein A is each R is a methyl group, and the epoxy group-containing disilazane has the formula, An epoxy group-containing disilazane, according to Claim 1, wherein A is each R is an ethyl group, and the epoxy group-containing disilazane has the formula, An epoxy group-containing disilazane, according to Claim 1, wherein A is each R is a methyl group or a phenyl group, and the epoxy group-containing disilazane has the formula, An epoxy group-containing disilazane, according to Claim 1, wherein A is each R is a methyl group, and the epoxy group-containing disilazane has the formula, 6. An epoxy group-containing disilazane, according to Claim 1, wherein A is each R is a propyl-group, and the epoxy group-containing disilazane has the formula, An epoxy group-containing disilazane, according to Claim 1, wherein A is each R is a phenyl group, and the epoxy group-containing disilazane has the formula, A process for producing an epoxy group-containing disilazane, said process comprising reacting a disilazane having the formula, with an epoxy compound selected from a group consisting of allyl glycidyl ether and vinylcyclohexene oxide in the presence of a platinum-type catalyst; where each R is independently selected and is a monovalent hydrocarbon group, selected from alkyl groups, substituted alkyl groups, aryl groups and substituted aryl groups. A process according to Claim 8, wherein the platinum-type catalyst is selected from a group consisting of platinum metal, platinum adsorbed on a solid support, chloroplatinic acid, alcohol-modified chloroplatinic acid, olefin complexes of chloroplatinic acid, chloroplatinic acid-vinylsiloxane coordination compounds, platinum black, palladium and rhodium. A process according to Claim 8, wherein the platinum-type catalyst is present in a range from about 0.1 to 1,000 ppm as platinum-type metal proper based on the weight of the disilazane. A process according to Claim 8, wherein the temperature at which the disilazane and the epoxy compound are reacted is in a range from about 20°C to 300°C. A process according to Claim 8. wherein there is also present a solvent. A process according to Claim 12, wherein the solvent is selected from a group consisting of aromatic hydrocarbons, chlorinated hydrocarbons, and ketones.

Inventors: SHIRAHATA, AKIHIKO
Applicants: TORAY SILICONE COMPANY, LTD.
Application year: 1987
Main classification: C07F7
IPC codes: C07B61, C07F7