CATALYTIC PRODUCTION OF OPTICALLY ACTIVE CARBOXYLIC ACID

Abstract: A carboxylic acid having optically active C atom, of formula: wherein R¹, R² and R³ each represents hydrogen, alkyl, alkenyl, or phenyl or naphthyl which may have a substituent, provided that all of R¹ to R³ are not simultaneously hydrogen; when R¹ and R² are both hydrogen then R³ is not methyl and when R³ is hydrogen, R¹ and R² are each other than hydrogen, is produced by dissolving an α,β-unsaturated carboxylic acid represented by the formula: in an aprotic solvent, optionally adding equimolar tertiary amine and adding a ruthenium-optically active phosphine complex as a catalyst, hydrogenating under pressure of 4-135 kg/cm², and distilling off the solvent. Three classes of such catalyst, containing a 'BINAP' group, are shown, and syntheses thereof. The carboxylic acids produced can be used as raw materials for syntheses, e.g. of physiologically active substances of natural materials, and also as liquid crystal materials.

Description: This invention relates to a process for producing an optically active carboxylic acid by asymmetric synthesis. More particularly, the invention relates to a process for producing an optically active carboxylic acid represented by formula (I): wherein R¹, R², and R³ each represents a hydrogen atom, an alkyl group, an alkenyl group, or a phenyl or naphthyl group which may have a substituent, provided that all of R¹, R² and R³ are not simultaneously a hydrogen atom; when R¹ and R² are simultaneously a hydrogen atom, then R³ is not a methyl group; and that when R³ is a hydrogen atom, then R¹ and R² are each a group other than a hydrogen atom. The optically active carboxylic acids shown by formula (I) have been considered with keen interest as raw materials for synthesizing various useful materials, for example, as intermediates for synthesizing physiolosically active substances of natural materials and also as liquid crystal materials. Several methods of asymmetric synthesis have been available for producing such optically active carboxylic acids, for example, (1) a method starting with naturally occurring optically active isomers; (2) a method utilizing microbial asymmetric hydrogenation; and (3) a method involving asymmetric hydrogenation in the presence of a specified catalyst. In particular, as the process for producing the optically active carboxylic acid of formula (I) from the α,β-unsaturated carboxylic acid of formula (II) by asymmetric synthesis, a process in which the α,β-unsaturated carboxylic acid is asymmetrically hydrogenated in the presence of a rhodium-optically active phosphine complex as a catalyst is reported. That is, C. Fisher et al report in Tetrahedron Letters , No. 29, pp. 2487 to 2490 (1977) that 2-methylphenylacetic acid is obtained in an optical yield of 27.5 %ee by asymmetric hydrogenation of atropic acid (2-methylenephenylacetic acid). Also, P. Aviron-Violet et al report asymmetric hydrogenation of atropic acid in an optical yield of 70 %ee in J. Mol. Cat. , 5 , pp. 41 to 50 (1979). Furthermore, M. Yamashita et al report in Bull. Chem. Soc. Jpn. , 55 , pp. 2917 to 2921 (1982) that 2-methylbutyric acid is obtained by asymmetric hydrogenation of tiglic acid ((E) 2-methyl-2-butenoic acid) in an optical yield of 62 %ee. Among these methods of asymmetric synthesis, according to the method (1) starting with naturally occurring optically active isomers or method (2) utilizing microbial asymmetric hydrogenation, though desired carboxylic acids with high optical purities can be obtained, not only the absolute configuration of the resulting optically active carboxylic acids is limited to a specific one, but also it is difficult to synthesize their enantiomers. Further, in accordance with the asymmetric hydrogenation of α,β-unsaturated carboxylic acid derivatives using a rhodium-optically active phosphine catalyst, not only the optical purities of the resulting carboxylic acids are not yet satisfactory, but also since metallic rhodium to be used is expensive due to limitations in place and quantity of production when used as a catalyst component, it forms a large proportion in cost of the catalyst, ultimately resulting in an increase in cost of the final commercial products. In order to solve the aforesaid problems, the present inventors have conducted intensive studies and eventually found that when asymmetric hydrogenation is carried out using, as a catalyst, a relatively cheap ruthenium-optically active phosphine catalyst, the desired carboxylic acid with a high optical purity can be obtained. An object of the present invention is, therefore, to provide a process for producing an optically active carboxylic acid represented by formula (I) above which comprises asymmetrically hydrogenating an α,β-unsaturated carboxylic acid represented by formula (II): wherein R¹, R², and R³ are the same as defined above, in the presence of a catalyst a complex α defined under (1) and (2) below. The process of this invention is performed as follows. That is, an α,β-unsaturated carboxylic acid of formula (II) is dissolved in a protic solvent such as methol, ethanol or 2-methoxy ethanol. Depending upon the type of substrate used, an equimolar amount of a tertiary amine such as triethylamine, dicyclohexylmethylamine, and tri-n-butylamine is appropriately selected and added thereto, and the mixture is placed in an autoclave. Thereafter, a ruthenium-optically active phosphine complex is added to the mixture in an amount of from 1/100 to 1/3000 mole per mole of the α,β-unsaturated carboxylic acid, and hydrogenation is performed for from one to 100 hours at a hydrogenation temperature of from 0°C to 80°C under a hydrogen pressure of from 4 kg/cm² to 135 kg/cm². After completion of the reaction, the solvent is distilled off and, then, the residue is distilled under reduced pressure to provide the desired optically active carboxylic acid of formula (I) in an almost quantitative yield. In formula (II) which represents the α,β-unsaturated carboxylic acid used as a raw material in this invention, R¹, R², and R³ each represents a hydrogen atom, an alkyl group (e.g., those having from 1 to 7 carbon atoms), an alkenyl group (e.g., those having from 3 to 6 carbon atoms), or a phenyl or naphthyl group which may have a substituent (e.g., a hydroxyl group, a methoxy group, an amino group, a dimethylamino group, a chlorine atom, and a bromine atom), or an aryl group which may have a substituent, provided that all of R¹, R², and R³ are not simultaneously a hydrogen atom; when R¹ and R² are simultaneously a hydrogen atom, then R³ is not a methyl group; and that when R³ is a hydrogen atom, then R¹ and R² are a group other than a hydrogen atom. The above-described condition is to be provided such that the carbon atom at the α-position or β-position of the carboxylic acid of formula (I) obtained by the process of this invention is an asymmetric carbon atom to exhibit optical activity. Examples of the α,β-unsaturated carboxylic acid of formula (II) are tiglic acid, angelic acid ((Z)-2-methyl-2-butenoic acid), 2-methyl-2-pentenoic acid, atropic acid (2-methylenephenylacetic acid), p-hydroxy atropic acid, p-methoxy atropic acid, p-chloro atropic acid, p-bromo atropic acid, p-amino atropic acid, p-dimethylamino atropic acid, 3-methyl-2,5-hexadienoic acid, geranic acid, 2-methylenenonanoic acid, 2-methylcinnamic acid, 3-methylcinnamic acid, 2-phenylcinnamic acid and 6-methyoxy-α-methylene-2-naphthaleneacetic acid. Examples of the ruthenium-optically active phosphine complex which can be used as the catalyst in the present invention are those as described below. In the following examples, the abbreviations designated below are used. Et: Ethyl group Bu: Butyl group t-Bu: t-Butyl group i-Pr: Isopropyl group Ph: Phenyl group BINAP: 2,2′-Bis(diphenylphosphino)-1,1′-binaphthyl T-BINAP: 2,2′-Bis(di-p-tolylphosphino)-1,1′-binaphthyl t-BuBINAP: 2,2′-Bis(di-p-t-butylphenylphosphino)-1,1′-binaphthyl sulfonated BINAP: 2,2′-Bis(diphenylphosphino)-5,5′-bis-(sodium sulfonate)-1,1′-binaphthyl amino BINAP: 2,2′-Bis(diphenylphosphino)-5,5′-bis(amino)-1,1′-binaphthyl acetylamino BINAP: 2,2'-Bis(diphenylphosphino)-5,5'-bis-(acetylamino)-1,1'-binaphthyl wherein X-R⁵-BINAP signifies a tertiary phosphine of formula (VI): in which X represents a hydrogen atom, an amino group, an acetylamino group or a sulfo group; R⁵ represents a hydrogen atom or a lower alkyl group (e.g., those having from 1 to 4 carbon atoms); R⁶ and R⁷ each represents an alkyl group (e.g., those having from 1 to 9 carbon atoms), a halogenated lower alkyl group (e.g., those having from 1 to 4 carbon atoms; examples of the halogen include fluorine, chlorine and bromine), a phenyl group, a phenyl group substituted with a lower alkyl group (e.g., those having from 1 to 4 carbon atoms), an α-aminoalkyl group (e.g., those having from 1 to 4 carbon atoms), or an α-aminophenylalkyl group (e.g., those having from 7 to 10 carbon atoms), or R⁶ and R⁷ are taken together to form an alkylene group (e.g., those having from 1 to 4 carbon atoms); and q represents 1 or 2. The complex of formula (V) can be prepared in accordance with the method as disclosed in Japanese Patent Application No. 108888/1986 corresponding to EP-0245959. That is, Ru₂Cl₄(X-R⁵-BINAP)₂(NEt₃) as a starting material is reacted with a carboxylic acid salt in an alcoholic solvent such as methanol, ethanol or t-butanol at a temperature of from about 20 to 110°C for a period of time of from 3 to 15 hours; after distilling off the solvent, the desired complex is extracted with a solvent such as diethyl ether or ethanol; and the extract is evaporated to dryness to obtain a crude complex which is then recrystallized from a suitable solvent such as ethyl acetate, whereby a purified product can be obtained. Also, a complex having a trifluoroacetate group can be obtained by reacting a diacetate complex, Ru(X-R⁵-BINAP)(O₂CCH₃)₂ obtained by the manner as described above and trifluoroacetic acid using methylene chloride as a solvent for about 12 hours at about 25°C. Furthermore, in the case of producing the complex having two equivalents of ligands coordinated to the ruthenium metal, that is, the complex of formula (V) wherein q is 2, RuHCl(X-R⁵-BINAP)₂ obtained by the above-described manner is reacted with a carboxylate in a solvent such as methylene chloride. If an optically active form of X-R⁵-BINAP is used in the method described above, a ruthenium-phosphine complex of formula (V) having corresponding optically active properties can be obtained. Specific examples of the complex of formula (V) are listed below: Ru(BINAP)(O₂CCH₃)₂; Ru(BINAP)(O₂CCF₃)₂; Ru(T-BINAP)₂(O₂CCF₃)₂; Ru(T-BINAP)₂(O₂CCH₃)₂; Ru(BINAP)(O₂Ct-Bu)₂; Ru(BINAP)(O₂CPh)₂; Ru(T-BINAP)(O₂CCH₃)₂; Ru(T-BINAP)(O₂CCF₃)₂; Ru(t-BuBINAP)(O₂CCH₃)₂; Ru(amino BINAP)(O₂CCH₃)₂; Ru(acetylamino BINAP)(O₂CCH₃)₂; Ru(sulfonated BINAP)(O₂CCH₃)₂; (2) [RuH ℓ (R⁴-BINAP) v ]Y w (VII) wherein R⁴-BINAP signifies a tertiary phosphine of formula (IV) described above; Y is ClO₄, BF₄, or PF₆; when ℓ is 0, then v is 1 and w is 2; and when ℓ is 1, then v is 2 and w is 1. The complex of formula (VII) can be prepared in accordance with the method as disclosed in Japanese Patent Application No. 184651/1986 corresponding to EPA 87305302.9. That is, a complex of formula (VII) wherein ℓ is 0, v is 1, and w is 2 is produced by reacting, as a starting compound, Ru₂Cl₄(R⁴-BINAP)₂(NEt₃) with a salt represented by formula (VIII): MY (VIII) wherein M is a metal selected from Na, K, Li, Mg and Ag; and Y is C10₄, BF₄ or PF₆, in a solvent composed of water and methylene chloride in the presence of, as a phase transfer catalyst, a quaternary ammonium salt or a quaternary phosphonium salt represented by formula (IX): R⁸R⁹R¹⁰R¹¹AB (IX) wherein R⁸, R⁹, R¹⁰ and R¹¹ are each an alkyl group having from 1 to 16 carbon atoms, a phenyl group or a benzyl group; A is nitrogen or phosphorus; and B is a halogen (e.g., chorine, iodine or bromine). The reaction between Ru₂Cl₄(R⁴-BINAP)₂(NEt₃) and the salt of formula (VIII) is carried out by adding these two compounds and the phase transfer catalyst of formula (IX) a mixed solvent of water and methylene chloride and stirring the mixture. The salt of formula (VIII) is used in an amount of from 2 to 10 moles and preferably 5 moles per mole of the ruthenium, and the phase transfer catalyst of formula (IX) is used in an amount of from 1/100 to 1/10 mole per mole of the ruthenium, respectively. It suffices to continue the stirring for a period of time of from 6 to 18 hours and typically 12 hours at a temperature of from 5 to 30°C. Examples of the salt of formula (VIII) include perchlorates, borofluorides and hexafluorophosphates of Na, K, Li, Mg or Ag. Compounds useful as the phase transfer catalyst of formula (IX) are found in suitable publications, such as W. P. Weber and G. W. Gokel, Phase Transfer Catalysis in Organic Synthesis, Springer-Verlag, pp. 6 (1977). After completion of the reaction, the reaction mixture is allowed to stand, and the methylene chloride solution separated from the aqueous layer is washed and stripped of the methylene chloride by evaporation under vacuum so as to obtain the end product. Alternatively, the end compound can be synthesized by reacting Ru(R⁴-BINAP)(O₂CCH₃)₂ with an acid represented by formula (X): HY (X) wherein Y is ClO₄, BF₄ or PF₆, under stirring in a mixed solvent of methylene chloride and methanol. The acid of formula (X) is used in an amount of from 2 to 6 moles and preferably 4 moles per mole of the ruthenium. It suffices to continue the stirring for a period of time of from 6 to 18 hours and typically 12 hours at a temperature of from 5 to 30°C. A complex of formula (VII) wherein ℓ is 1, v is 2, and w is 1 can be produced by reaction of, as a starting material, RuHCl(R⁴-BINAP)₂ with the salt of formula (VIII) in a mixed solvent of water and methylene chloride in the presence of the phase transfer catalyst of formula (IX). The salt of formula (VIII) is used in an amount of from 2 to 10 moles and preferably 5 moles per mole of the ruthenium, and the phase transfer catalyst of formula (IX) is used in an amount of from 1/100 to 1/10 mole per mole of the ruthenium. It suffices to continue the stirring for a period of time of from 6 to 18 hours and typically 12 hours at a temperature of from 5 to 30°C. Specific examples of the complex of formula (VII) are listed below: [Ru(T-BINAP)](BF₄)₂; [RuH(T-BINAP)₂]BF₄; [Ru(BINAP)](BF₄)₂; [Ru(BINAP)](ClO₄)₂; [Ru(T-BINAP)](ClO₄)₂; [Ru(T-BINAP)](PF₆)₂; [RuH(BINAP)₂]BF₄; [RuH(T-BINAP)₂]ClO₄; and [RuH(T-BINAP)₂]PF₆. The present invention is hereunder described in greater detail by way of Referential Examples and Examples which, however, should not be taken as limiting. Analyses were conducted in these examples with the following instruments: Gas chromatography: Shimadzu GC-9A (made by Shimadzu Seisakusho, Ltd.) Column: OV-101 silica capillary (0.25 mm ⊘ × 25 m L , made by Gasukuro Kogyo Inc.), with the temperature being increased from 100 to 250°C at a rate of 3°C/min High-performance liquid chromatography: Hitachi Liquid Chromatograph 655A-11 (made by Hitachi, Ltd.) Column: Chemcopack Nucleosil 100-3 (4.6 mm ⊘ × 300 mm L , made by Chemco Co., Ltd.) Solvent: hexane/diethyl ether (7:3 by volume) at a flow rate 1 ml/min Detector: UV Detector 635M (UV-254) (made by Hitachi, Ltd.) ¹H NMR spectrometer: Model JNM-GX400 (400MHz) (made by JEOL Ltd.) Internal standard: tetramethylsilane Polarimeter: Polarimeter DIP-4 (made by Japan Spectroscopic Co., Ltd.) ³¹P NMR spectrometer: Model JNM-GX400 (161 MHZ) (made by JEOL Ltd.), with chemical shifts being determined with 85% phosphoric acid used as an external standard Referential Example 1 Preparation of Ru((-)-BINAP)(O₂CCH₃)₂: In a 250 ml Schlenk's tube were placed 1.43 g (0.9 mmole) of Ru₂Cl₄((-)-BINAP)₂(NEt₃) prepared according to the same manner as in Referential Example 1 except using (-)-BINAP in place of (-)-T-BINAP and 3.06 g (37 mmoles) of sodium acetate. After sufficiently replacing the inside atmosphere of the tube with nitrogen, 100 ml of t-butanol was added thereto, and the resultant mixture was heated under reflux for 12 hours to perform reaction. After completion of the reaction, the t-butanol was distilled off under a reduced pressure of 20 mmHg to dryness, and the residue was extracted twice with 10 ml of diethyl ether. The diethyl ether was distilled off to dryness, and solids thus obtained were further extracted twice with 10 ml of ethanol. The extract was concentrated to dryness to provide 1.5 g of crude Ru((-)-BINAP)(O₂CCH₃)₂. The product was further recrystallized from ethyl acetate to provide 0.79 g of a yellowish brown solid. The yield was 52%. Melting Point: 180-181°C (decomposed) Elemental Analysis for C₄₈H₃₈O₄P₂Ru: Referential Example 2 Preparation of Ru((-)-T-BINAP)(O₂CCF₃)₂ : In a 250 ml Schlenk's tube, the inside atmosphere of which had previously been replaced with nitrogen, was placed 0.74 g (0.82 mmole) of Ru((-)-T-BINAP)(O₂CCH₃)₂ prepared according to the same manner as in Referential Example 3 except using (-)-T-BINAP in place of (-)-BINAP and 10 ml of methylene chloride was added thereto to form a homogeneous solution. Then, 0.14 ml (1.81 mmoles) of trifluoroacetic acid was added to the solution, and the mixture was stirred for 12 hours at room temperature. After completion of the reaction, the reaction mixture was concentrated to dryness to provide 0.7 g of Ru((-)-T-BINAP)(O₂CCF₃)₂ as a brown solid. The yield was 91%. Elemental Analysis for C₅₂H₄₀F₆O₄P₂Ru: Ru C H P Calculated: 10.05% 62.09% 4.01% 6.16% Found: 9.89% 62.27% 4.15% 5.82% ³¹P NMR (CDCl₃) δppm: 59.91 (s) Referential Example 3 Preparation of [Ru((-)-BINAP)](BF₄)₂: In a Schlenk's tube was placed 0.51 g (0.61 mmole) of Ru((-)-BINAP)(O₂CCH₃)₂ obtained in Referential Example 3. After sufficiently replacing the inside atmosphere of the tube with nitrogen, 7 ml of methylene chloride, 7 ml of methanol, and 0.52 ml (2.48 mmoles) of an aqueous solution of 42% borofluoric acid were added thereto, and the mixture was stirred for 12 hours at room temperature. Thereafter, the reaction mixture was concentrated under reduced pressure to provide 0.53 g of [Ru((-)-BINAP)](BF₄)₂ as a brown solid. The yield was 97.2%. Elemental Analysis for C₄₄H₃₂B₂F₈P₂Ru: Ru P C H Calculated: 11.26% 6.90% 58.90% 3.59% Found: 10.88% 6.51% 58.62% 3.82% ³¹P NMR (CDCl₃) δppm:10.357 (d, J=48.9Hz), 77.450 (d, J=48.9Hz) Referential Example 4 Preparation of [Ru((+)-T-BINAP)](ClO₄)₂: In a 250 ml Schlenk's tube was placed 0.54 g (0.3 mmole) of Ru₂Cl₄((+)-T-BINAP)₂(NEt₃) prepared according to the same manner as in Referential Example 1 except using (+)-T-BINAP in place of (-)-T-BINAP. After sufficiently replacing the inside atmosphere of the tube with nitrogen, 60 ml of methylene chloride was added thereto. Then, after adding a solution of 0.36 g (3.0 mmoles) of sodium perhydrochloride dissolved in 60 ml of water and a solution of 16 mg (0.06 mmole) of triethylbenzylammonium bromide dissolved in 3 ml of water to the mixture, the resultant mixture was stirred for 12 hours at room temperature to perform reaction. After completion of the reaction, the reaction mixture was allowed to stand, and an aqueous layer thus formed was removed by liquid separation. The methylene chloride was distilled off under reduced pressure, and the residue was dried under reduced pressure to provide 0.59 g of [Ru((+)-T-BINAP)](ClO₄)₂ as a dark brown solid. The yield was 99.6%. Elemental Analysis for C₄₈H₄₀Cl₂O₈P₂Ru: Ru P C H Calculated: 10.32% 6.33% 58.90% 4.12% Found: 10.08% 5.97% 58.61% 4.53% ³¹P NMR (CDCl₃) δppm: 12.920 (d, J=41.1Hz), 61.402 (d, J=41.1Hz) Example 1 Production of (2S)-(+)-2-methylbutyric acid : In a 100 ml stainless steel autoclave, the inside atmosphere of which had previously been replaced with argon, were placed 0.2 g (2 mmoles) of (E)-2-methyl-2-butenoic acid and 20 ml of methanol and then, 6.0 mg (0.007 mmole) of [Ru((-)-BINAP)](BF₄)₂ prepared in Referential Example 5 was added to the mixture to perform hydrogenation for 12 hours at a hydrogen pressure of 4 kg/cm² and at a reaction temperature of 20°C. Thereafter, the solvent was distilled off to provide 0.2 g of 2-methylbutyric acid. The yield thereof was 100%. Boiling Point: 50°C/0.07 mmHg ¹H NMR (CDCl₃) δppm: 0.95 (t, 3H), 1.17 (d, 3H), 1.15-2.00 (m, 2H), 2.4 (m, 1H), 9.76 (s, 1H) Specific Rotation: [α] 25 / D = +18.05° (neat) Then, an amide was synthesized from the carboxylic acid thus obtained and (R)-(+)-(1-naphthyl)ethylamine, and a high-performance liquid chromatographic analysis was performed. As the result, The original carboxylic acid was found to be a mixture of 95.8% of (2S)-(+)-2-methylbutyric acid and 4.2% of (2R)-(-)-2-methylbutyric acid, and the optical yield of (2S)-(+)-2-methylbutyric acid was 91.6 %ee. EXAMPLE 2 Production of (2S)-(+)-2-methylbutyric acid: In a 100 ml autoclave, the inside atmosphere of which had previously been replaced with argon, were placed 0.2 g (2 mmoles) of (Z)-2-methyl-2-butenoic acid, 20 ml of methanol, and 0.39 g (2 mmoles) of dicyclohexylmethylamine to form a solution. Then, 3.4 mg (0.004 mmole) of Ru((+)-BINAP)(O₂CCH₃)₂ prepared according to the same manner as in Referential Example 3 except using (+)-BINAP in place of (-)-BINAP was added to the mixture to perform hydrogenation with stirring for 4 hours at a hydrogen pressure of 125 kg/cm² and at a reaction temperature of 25°C. Thereafter, the solvent was distilled to provide 0.2 g of 2-methylbutyric acid. The yield was 100%. Specific Rotation: [α] 25 / D = +12.25° (neat) An amide was prepared using the aforesaid carboxylic acid and analyzed by the same manner as in Example 1. As the result, the optical yield of (2S)-(+)-2-methylbutyric acid was 57.9 %ee. EXAMPLE 3 Production of (2S)-(+)-2-methylvaleric acid: In a 100 ml autoclave, the inside atmosphere of which had previously been replaced with argon, were placed 0.23 g (2 mmoles) of (E)-2-methyl-2-pentenoic acid and 20 ml of methanol. Then, 8.4 mg (0.01 mmole) of Ru((-)-BINAP)(O₂CCH₃)₂ prepared in Referential Example 3 was added to the mixture to perform hydrogenation for 24 hours at a hydrogen pressure of 4 kg/cm² and at a reaction temperature of 25°C. Thereafter, the solvent was distilled off to provide 0.23 g of 2-methylvaleric acid. The yield was 100%. Boiling Point: 50°C/0.07 mmHg ¹H NMR (CDCl₃) δppm: 0.92 (t, 3H), 1.18 (d, 3H), 1.3-1.5 (m, 2H), 1.6-1.75 (m, 1H), 2.48 (m, 1H), 11.00 (s, 1H). Specific Rotation: [α] 25 / D = +14.40° (neat) An amide was prepared using the aforesaid carboxylic acid and analyzed by the same manner as in Example 1. As the result, the optical yield of (2S)-(+)-2-methylvaleric acid was 77.9 %ee. EXAMPLE 4 Production of (2R)-(-)-2-methylphenylacetic acid: In a 100 ml autoclave, the inside atmosphere of which had previously been replaced with argon, were placed 0.3 g (2 mmoles) of 2-methylenephenylacetic acid and 20 ml of methanol. Then, 8.4 mg (0.01 mmole) of Ru((+)-BINAP)(O₂CCH₃)₂ prepared according to the same manner as in Referential Example 1 except using (+)-BINAP in place of (-)-BINAP was added to the mixture to perform hydrogenation for 24 hours at a hydrogen pressure of 100 kg/cm² and at a rection temperature of 30°C to provide 0.3 g of 2-methylphenylacetic acid. The yield was 100%. Boiling Point: 120°C/0.07 mmHg. ¹H NMR (CDCl₃) δppm: 1.51 (d, 3H), 3.73 (q, 2H), 7.31-7.33 (m, 5H), 14.05 (s, 1H). Specific Rotation: [α] 25 / D = -68.37° (c=1.72, chloroform) An amide was prepared using the aforesaid carboxylic acid and analyzed by the same manner an in Example 1. As the result, the optical yield of (2R)-(-)-2-methylphenylacetic acid was 91.0 %ee. EXAMPLE 5 Production of (2R)-(-)-2-methylnonanoic acid : In a 200 ml autoclave, the inside atmosphere of which had previously been replaced with argon, were placed 3.0 g (17.6 mmoles) of 2-methylenenonanoic acid and 50 ml of ethanol. Then, 6.9 mg (0.007 mmole) of [Ru((-)-T-BINAP)](ClO₄)₂ prepared according to the same manner as in Referential Example 4 except using (-)-T-BINAP in place of (+)-T-BINAP was added to the mixture to perform hydrogenation for 15 hours at a hydrogen pressure of 30 kg/cm² and at a reaction temperature of 20°C. Thereafter, the solvent was distilled off to provide 3.0 g of 2-methylnonanoic acid. The theoretical yield (hereafter simply referred to as "yield") was 100%. Boiling point: 110-112°C/2 mmHg. ¹H NMR (CDCl₃) δppm: 0.85-1.80 (m, 18H), 2.24-2.75 (m, 1H), 11.90 (s, 1H) Specific Rotation: [α] 20 / D = -5.40° (c=2.11, ethanol) An amide was prepared using the aforesaid carboxylic acid and analyzed by the same manner as in Example 1. As the result, the optical yield of (2R)-(-)-2-methylnonanoic acid was 37 %ee. Example 6 Production of (2R)-(-)-2,3-diphenylpropanoic acid : In a 100 ml autoclave, the inside atmosphere of which had previously been replaced with argon, were placed 0.45 g (2 mmoles) of (E)-2-phenylcinnamic acid and 20 ml of ethanol, then, 11.2 mg (0.013 mmole) of Ru((-)-BINAP)(O₂CCH₃)₂ prepared in Referential Example 1 was added to the mixture to perform hydrogenation for 100 hours at a hydrogen pressure of 4 kg/cm² and at a reaction temperature of 40°C. Thereafter, the solvent was distilled off to provide 0.45 g of 2,3-diphenylpropanoic acid. The yield was 100%. Boiling Point: 230°C/0.07 mmHg. ¹H NMR (CDCl₃) δppm: 3.03 (d of d, 1H), 3.41 (d of d, 1H), 3.86 (d of d, 1H), 7.07-7.40 (m, 10H), 15.2 (s, 1H). Specific Rotation: [α] 25 / D = -54.05° (c=0.52, acetone) An amide was prepared using the aforesaid carboxylic acid and analyzed by the same manner as in Example 1. As the result, the optical yield of (2R)-(-)-2,3-diphenylpropanoic acid was 40.5 %ee. Example 7 Production of (3S)-(-)-citronellic acid : In a 100 ml autoclave, the inside atmosphere of which had previously been replaced with argon, were placed 0.34 g (2 mmoles) of geranic acid, 20 ml of methanol, and 0.39 g (2 mmoles) of dicyclohexylmethylamine. Then, 5.6 mg (0.007 mmole) of Ru((+)-BINAP)(O₂CCH₃)₂ prepared according to the same manner as in Referential Example 1 except using (+)-BINAP in place of (-)-BINAP was added to the mixture to perform hydrogenation for 12 hours at a hydrogen pressure of 100 kg/cm² and at a reaction temperature of 25°C. Thereafter, the solvent was distilled off to provide 0.34 g of citronellic acid. Boiling Point: 100°C/0.07 mmHg. ¹H NMR (CDCl₃) δppm: 0.97 (d, 3H), 1.1-1.5 (m, 2H), 1.60 (s, 3H), 1.67 (s, 3H), 1.73-2.50 (m, 4H), 5.08 (t, 1H), 12.30 (s, 1H). Specific Rotation: [α] 25 / D = -7.82° (c=2.99, methanol) An amide was prepared using the aforesaid carboxylic acid and analyzed by the same manner as in Example 1. As the result, the optical yield of (3S)-(-)-citronellic acid was 87.0 %ee. Example 8 Production of naproxen (6-methoxy-α-methyl-2-naphthaleneacetic acid) : In a 100 ml autoclave, the inside atmosphere of which had previously been replaced with argon, were placed 0.45 g (2 mmoles) of 6-methoxy-α-methylene-2-naphthaleneacetic acid, 20 ml of methanol, and 0.39 g (2 mmoles) of dicyclohexylmethylamine. Then, 9.0 mg (0.010 mmole) of Ru((-)-T-BINAP)(O₂CCH₃)₂ prepared according to the same manner as in Referential Example 1 except using (-)-T-BINAP in place of (-)-BINAP was added to the mixture to perform hydrogenation for 12 hours at a hydrogen pressure of 135 kg/cm² and at a reaction temperature of 17°C. Thereafter, the solvent was distilled off to provide 0.39 g of naproxen. The yield was 84%. Melting Point: 154-155°C ¹H NMR (CDCl₃) δppm: 1.57 (d, 3H), 3.86 (q, 1H), 3.90 (s, 3H), 7.07-7.87 (m, 6H), 10.83 (s, 1H) Specific Rotation: [α] 25 / D = +59.21° (c=1.08, chloroform) An amide was prepared using the the aforesaid carboxylic acid and analyzed by the same manner as in Example 1. As the result, the optical yield of naproxen was 90.4 %ee. EXAMPLE 9 Production of naproxen: In a 100 ml autoclave, the inside atmosphere of which had previously been replaced with argon, were placed 0.45 g (2 mmoles) of 6-methoxy-α-methylene-2-naphthaleneacetic acid and 20 ml of methanol. Then, 2.0 mg (0.002 mmole) of Ru((-)-T-BINAP)(O₂CCF₃)₂ prepared in Referential Example 2 was added to the mixture to perform hydrogenation for 24 hours at a hydrogen pressure of 40 kg/cm² and at a reaction temperature of 20°C. Thereafter, the solvent was distilled off to provide 0.43 g of naproxen. The yield thereof was 93.7%. Melting Point: 154-155°C. ¹H NMR (CDCl₃) δppm: 1.57 (d, 3H), 3.86 (q, 1H), 3.90 (s, 3H), 7.07-7.87 (m, 6H), 10.83 (s, 1H). Specific Rotation: [α] 25 / D = +38.87° (c=0.98, chloroform). An amide was prepared using the aforesaid carboxylic acid and analyzed by the same manner as in Example 1. As the result, the optical yield of naproxen was 58.8 %ee. EXAMPLE 10 Production of (3S)-(+)-3-phenylbutyric acid: In a 100 ml autoclave, the inside atmosphere of which had previously been replaced with argon, were placed 0.32 g (2 mmoles) of (Z)-3-methylcinnamic acid and 20 ml of methanol. Then, 2.9 mg (0.0034 mmole) of Ru((+)-BINAP)(O₂CCH₃)₂ prepared according to the same manner as in Referential Example 1 except using (+)-BINAP in place of (-)-BINAP was added to the mixture to perform hydrogenation for 70 hours at a hydrogen pressure of 104 kg/cm² and at a reaction temperature of 25°C. Thereafter, the solvent was distilled off to provide 0.32 g of 3-phenylbutyric acid. The yield was 100%. Boiling Point: 170°C/0.05 mmHg. ¹H NMR (CDCl₃) δppm: 1.30 (d, 3H), 2.57 (d, 1H), 2.60 (d, 1H), 3.27 (m, 1H), 7.32 (broad s, 5H), 12.20 (s, 1H). Specific Rotation: [α] 25 / D = +0.44° (c=0.94, benzene). An amide was prepared using the aforesaid carboxylic acid and analyzed by the same manner as in Example 1. As the result, the optical yield of (3S)-(+)-3-phenylbutyric acid was 84.8 %ee. EXAMPLE 11 Production of (2R)-(-)-2-(p-methoxyphenyl)propionic acid : In a 100 ml autoclave, the inside atmosphere of which had previously been replaced with argon, were placed 0.36 g (2 mmoles) of p-methoxyatropic acid and 20 ml of methanol. Then, 7.5 mg (0.009 mmole) of Ru((+)-BINAP)(O₂CCH₃)₂ prepared according to the same manner as in Referential Example 1 except using (+)-BINAP in place of (-)-BINAP was added to the mixture to perform hydrogenation for 12 hours at a hydrogen pressure of 100 kg/cm² and at a reaction temperature of 19°C. Thereafter, the solvent was distilled off to provide 0.32 g of (2R)-(-)-2-(p-methoxyphenyl)propionic acid. The yield was 89%. Boiling Point: 220°C/0.05 mmHg. ¹H NMR (CDCl₃) δppm: 1.49 (d, 3H), 3.71 (q, 1H), 3.82 (s, 3H), 6.88 (d, 2H), 7.28 (d, 2H), 11.3 (broad s, 1H). Specific Rotation: [α] 25 / D = -53.91° (c=1.02, ethanol). An amide was prepared using the aforesaid carboxylic acid and analyzed by the same manner as in Example 1. As the result, the optical yield of (2R)-(-)-2-(p-methoxyphenyl)propionic acid was 83.0 %ee. As described above, in this invention, by asymmetrically hydrogenating α,β-unsaturated carboxylic acids using a ruthenium-optically active phosphine complex as a catalyst, optically active carboxylic acids which can be widely used as raw materials for synthesizing various useful compounds, for example, as intermediates for synthesizing physiologically active substances of natural materials and also as liquid crystal materials can be industrially advantageously produced.

Claims: A process for producing an optically active carboxylic acid represented by formula (I): wherein R¹, R², and R³ each represents a hydrogen atom, an alkyl group, an alkenyl group, or a phenyl or naphthyl group which may have a substituent, provided that all of R¹, R² and R³ are not simultaneously a hydrogen atom; when R¹ and R² are simultaneously a hydrogen atom, then R³ is not a methyl group; and that when R³ is a hydrogen atom, then R¹ and R² are each a group other than a hydrogen atom, which process comprises asymmetrically hydrogenating an α,β-unsaturated carboxylic acid represented by formula (II): wherein R¹, R², and R³ are the same as defined above, characterised by the use as a catalyst of a phosphine complex represented by formula (V): wherein X-R⁵-BINAP represents a tertiary phosphine of formula (VI): in which X represents a hydrogen atom, an amino group, an acetylamino group, or a sulfo group; R⁵ represents a hydrogen atom or a lower alkyl group; R⁶ and R⁷ each represents an alkyl group, a halogenated lower alkyl group, a phenyl group, a phenyl group substituted with a lower alkyl group, an α-aminoalkyl group, or an α-aminophenylalkyl group, or R⁶ and R⁷ are taken together to form an alkylene group; and q represents 1 or 2; or by formula (VII): [RuH l (R⁴-BINAP)v]Yw (VII) wherein R⁴-BINAP represents a tertiary phosphine of formula (IV): in which R⁴ is a hydrogen atom or a methyl group; Y is ClO₄, BF₄, or PF₆; when l is 0, then v is 1 and w is 2; and when l is 1, then v is 2 and w is 1. A process as claimed in Claim 1, wherein for R⁵ a lower alkyl group has from 1 to 4 carbon atoms; an alkyl group has from 1 to 9 carbon atoms; the alkyl group in an α-aminoalkyl group has from 1 to 4 carbon atoms; and the alkyl group in an α-aminophenylalkyl group has from 1 to 4 carbon atoms. A process as claimed in Claim 1, wherein said ruthenium-optically active phosphine complex is selected from among the following: Ru(BINAP)(O₂CCH₃)₂; Ru(BINAP)(O₂CCF₃)₂; Ru(T-BINAP)₂(O₂CCF₃)₂; Ru(T-BINAP)₂(O₂CCH₃)₂; Ru(BINAP)(O₂Ct-Bu)₂; Ru(BINAP)(O₂CPh)₂; Ru(T-BINAP)(O₂CCH₃)₂; Ru(T-BINAP)(O₂CCF₃)₂; Ru(t-BuBINAP)(O₂CCH₃)₂; Ru(amino BINAP)(O₂CCH₃)₂; Ru(acetylamino BINAP)(O₂CCH₃)₂; Ru(sulfonated BINAP)(O₂CCH₃)₂; wherein i-Pr represents an isopropyl group; Ph represents a phenyl group; BINAP represents 2,2'-bis(diphenylphosphino)-1,1'-binaphthyl; T-BINAP represents 2,2'-bis(di-p-tolylphosphine)-1,1'-binaphthyl; t-BuBINAP signifies 2,2'-bis(di-p-t-butylphenylphosphino)-1,1'-binaphthyl; sulfonated BINAP represents 2,2'-bis(diphenylphosphine)-5,5'-bis(sodium sulfonate)-1,1'-naphthyl; amino BINAP signifies 2,2'-bis(diphenylphosphino)-5,5'-bis(amino)-1,1'-binaphthyl; and acetylamino BINAP represents 2,2'-bis(diphenylphosphino)-5,5'-bis(acetylamino)-1,1'-binaphthyl. A process as claimed in Claim 1, wherein said ruthenium-optically active phosphine complex is selected from among the following: [Ru(T-BINAP)](BF₄)₂; [RuH(T-BINAP)₂]BF₄; [Ru(BINAP)](BF₄)₂; [Ru(BINAP)](ClO₄)₂; [Ru(T-BINAP)](ClO₄)₂; [Ru(T-BINAP)](PF₆)₂; [RuH(BINAP)₂]BF₄; [RuH(T-BINAP)₂]ClO₄; and [RuH(T-BINAP)₂]PF₆, wherein BINAP represents 2,2'-bis(diphenylphosphino)-1,1'-binaphthyl, and T-BINAP represents 2,2'-bis(di-p-tolylphosphino)-1,1'-binaphthyl. A process as claimed in any preceding claim, wherein in formula (I) the alkyl group has from 1 to 7 carbon atoms; and the alkenyl group has 3 to 6 carbon atoms.

Inventors: AKUTAGAWA, SUSUMU, KUMOBAYASHI, HIDENORI, NOYORI, RYOJI, OHTA, TETSUO, SAYO, NOBORU, TAKAYA, HIDEMASA
Applicants: TAKASAGO INTERNATIONAL CORPORATION
Application year: 1987
Main classification: C07C51
IPC codes: C07C51, C07F15