Lubricating oil containing dispersant viscosity index improver

Abstract: Lubricating oils of improved properties contain a terpolymer of maleic anhydride, lauryl methacrylate, and stearyl methacrylate which has been functionalized or coupled with phenothiazine and with N-methyl piperazine.

Description: FIELD OF THE INVENTION This invention relates to lubricating oils. More particularly, it relates to lubricating compositions characterized by improved properties of antioxidation, dispersancy and viscosity index. BACKGROUND OF THE INVENTION As is well known to those skilled in the art, it is possible to improve the properties of a lubricating oil by addition of various components. The viscosity index may be improved, as well as the dispersancy and antioxidant activity. From GB-A-1 025 795 lubricating oil compositions are known comprising a mineral lubricating oil and an oil-soluble copolymer of an α-β unsaturated carboxylic acid or acid anhydride, vinyl acetate and a C₆-C₂₄ alkyl fumarate, which copolymer has been reacted with a primary or secondary amine, or an aliphatic diamine which contains one tertiary amine group. Continued efforts are being made to attain improvement in said and other properties, and to attain these improvements at reduced cost. Thus, it is an object of this invention to provide an improved lubricating composition. Other objects will be apparent to those skilled in the art. STATEMENT OF THE INVENTION This invention is directed to a lubricating oil composition comprising lubricating oil and an effective amount about 0.2 to 15 weight%, based on the total composition, of one or more functionalized polymers as multifunctional additives obtained by copolymerizing first monomer(s) and second monomer(s) in a mole ratio of 1:2 bis 1:12, under free radical polymerization conditions, (i) said first monomer is maleic anhydride, and (ii) said second monomer is an acrylate having the formula wherein R is the stearyl- and/or lauryl group, and R' is hydrogen or methyl, thereby forming a copolymer backbone of molecular weight M n from about 10,000 to about 1,000,000 bearing at least two pendant side chains containing anhydride moities, the monomers being employed in pure form or in commercially available form, reacting said chains containing dicarboxylic acid anhydride moieties with a mixture of (substituted) phenothazine as first agent and N-methyl piperazine and/or 3-(N,N-dimethylamino)propylamine as second agent; thereby forming the functionalized polymers; and recovering said functionalized polymers. THE FIRST MONOMER The first monomer is maleic anhydride. THE SECOND MONOMER The second monomer is an acrylate having the formula wherein R is the stearyl group and/or the lauryl group. R' is hydrogen or more preferably is methyl. When R' is hydrogen or methyl, it is apparent that the compositions may be acrylates or methacrylates. Typical acrylates and methacrylates may include those listed below in Table 1. lauryl acrylate lauryl methacrylate stearyl acrylate stearyl methacrylate The preferred second monomer may be lauryl methacrylate. It is a feature of this invention that the copolymer may be formed from more than one second monomer. For example, it may be possible to form copolymer from (i) maleic anhydride as first monomer, (ii) lauryl methacrylate as second monomer and (iii) stearyl methacrylate as auxiliary second monomer. In one preferred embodiment, the polymer may be formed from (i) maleic anhydride as first monomer, (ii) stearyl methacrylate as second monomer, and (iii) lauryl methacrylate as auxiliary second monomer. When two second monomers are employed, they may for example be both acrylates or both methacrylates. In the preferred embodiment, they may both be methacrylates wherein the alcohol-derived portions of the esters may be characterized as higher and lower moieties in the higher and lower second and auxiliary second monomers. The preferred higher second monomer may be stearyl (C₁₈) methacrylate. The preferred lower second monomer may be lauryl (C₁₂) methacrylate. The monomers may be employed in pure form or in commercially available form. One typical commercially available stearyl methacrylate for example contains the components shown below in Table 2. Component W% Stearyl (C₁₈) 52-64 Cetyl (C₁₆) 30-44 Less than C₁₆ remainder When the esters employed are commercially available esters containing several homologues, then the carbon number to be employed in determining the alcohols which may be employed is the weight average carbon number, as determined for example by quantitative gas chromatographic analysis. The preferred product polymers may be those which use as second and as auxiliary second monomers, those obtained from (i) commercially available lauryl methacrylate and (ii) commercially available stearyl methacrylate. It is preferred to produce the desired product by copolymerization. PREPARATION OF COPOLYMER Copolymerization is typically effected by adding first monomer(s) and second monomer(s) to a reaction operation in mole ratio of 1:2 - 1:12, preferably 1:4 - 1:8, say about 1:6. There is preferably also added to the reaction operation polymerization-solvent in amount of 25 - 75 parts, say 47 parts per 100 parts of total reactants. Typical solvent may include hydrocarbons such as toluene, xylene, gas oil, lubricating oil cuts, etc. A preferred solvent may be the lubricating oil in which the product is to be used. Preferred may be a solvent neutral oil typified by 145 P Pale Turbine Oil. There is added to the reaction mixture 0.018 - 0.35 parts, say 0.05 parts of C₁ - C₂₀ alkyl mercaptan which serves as chain transfer agent (polymer chain length modifier). There is also added to the reaction mixture 0.05 - 0.15 parts, say 0.05 parts of dicumyl peroxide, dibenzoyl peroxide, or azobisisobutyronitrile which serves as polymerization initiator. The reaction system may be purged with inert gas such as nitrogen and heated to 40°C- 150°C, preferably 40°C-100°C, say 83°C for 1 - 10 hours, preferably 1 - 6 hours, say 2.5 hours. Typically heating is continued until two consecutive identical refractive indices are obtained. Then additional azobisisobutyronitrile and solvent may be added. The temperature may be raised to 60°C - 160°C, preferably 80°C - 120°C, say 100°C and maintained at that level for 10 - 120 minutes, say 60 minutes. The product copolymer typically contains the same molar proportions as are present in the reaction mixture i.e. it contains moieties derived from the first reactant in amount of about 8 to about 35 mole %, preferably about 10 to about 20 mole %, say 15 mole % and moieties derived from the second reactant in an amount of about 65 to about 92 mole %, preferably about 80 to about 90 mole %, say 85 mole %. This corresponds to a mole ratio of about 1:2-12, preferably of about 1:4-8, say about 1:6. In the preferred-embodiment in which the first monomer is maleic anhydride and the second monomer is stearyl methacrylate and lauryl methacrylate, the final polymer may contain about 2 to about 15 mole %, say about 8 mole % derived from maleic anhydride, about 60 to about 70 mole %, say 65 mole % derived from lauryl methacrylate and about 15 to about 38 mole %, say about 27 mole % derived from stearyl methacrylate. The molecular weight M n of the copolymer ranges from about 10,000 to about 1,000,000, preferably from about 20,000 to about 180,000, more preferably from about 60,000 to about 100,000, say about 98,000, corresponding to a M w of about 38,000 to about 450,000, preferably from about 200,000 to about 250,000, say about 213,000. Control of the molecular weights to within this desired range is obtained by use of chain transfer agents such as C₁ - C₂₀ alkyl (eg lauryl) mercaptans and by control of the ratio of monomer to initiator. The product polymer is typically obtained as a 25 - 80 wt.%, preferably 30 - 70 wt.%, say 50 wt.% solution in the solvent. It may be recovered and used as is or preferably it may be formulated into a concentrate containing polymer. Typical polymers which may be utilized in practice of the process of this invention may include the following listed below in Table 3. A. 8 mole % maleic anhydride 64 mole % lauryl methacrylate 28 mole % stearyl methacrylate B. 4 mole % maleic anhydride 70 mole % lauryl methacrylate 26 mole % stearyl methacrylate It is a feature of the polymers of this invention as so prepared that they are characterized by their ability to be utilized as pour depressants in hydrocarbon systems typified by lubricating oils. When used as a pour depressant, the polymer may be present in the system in pour depressant amount. This may typically be 0.05 - 0.3 parts, preferably 0.07 - 0.25 parts, say 0.1 parts per 100 parts of eg. lubricating oil. By the use of quantities of this magnitude it is possible to convert an oil having a pour point of minus 21°C to minus 7°C, say minus 12°C (minus 5°F to 20°F, say 10°F) (as measured by ASTM D-97) to a product having a pour point of minus 23°C to minus 32°C, say minus 29°C (minus 10°F to minus 25°F, say minus 20°F). COUPLING REACTIONS The polymer containing maleic anhydride moieties may be subjected to a coupling reaction in which a portion of the side chains containing anhydride moieties is coupled with a first functionalizing agent (antioxidant) which contains at least one sulfur atom and at least one hetero nitrogen atom and a second functionalizing agent (dispersant amine). It is a feature of the process of this invention that there may be coupled onto these oil-soluble, substantially linear, carbon-carbon, backbone polymers, units derived from a first functionalizing agent which contains at least one sulfur atom and at one hetero nitrogen atom to provide anti-oxidant properties in the product polymer. It is believed that best anti-oxidant activity in the desired polymer product is attained by coupling heterocyclic compounds which exhibit anti-oxidant activity when present in unbonded form. Selected of these latter is phenothiazine. The compounds which may be used as the first functionalizing agent include: phenothiazine and ring or/and N-substituted phenothiazine. Substituents may include hydrocarbon radicals selected from the group consisting of alkyl, alkenyl, cycloalkyl, aryl, alkaryl, or heterocyclic, including such radicals when containing oxygen, nitrogen, sulfur, halide or combinations thereof. Typically, the ring-substituted phenothiazine may include alkyl or alkenyl phenothiazines, alkoxy phenothiazines, hydroxy alkyl phenothiazines, aminophenothiazines, nitrophenothiazines, 3-formyl-10-alkyl-phenothiazine, or 2-amino-4-(2-phenthiazinyl) thiazole. Preferred of the functionalizing agents is phenothiazine. In practice of the process of this invention, 100 parts of charge polymer containing anhydride groups may be added to 100-1000 parts, say 300 parts of diluent-solvent. Typical diluent-solvent may be a hydrocarbon solvent such as mineral oil, n-hexane, n-heptane, or tetrahydrofuran. Preferred solvent may be a commercial mineral oil. Reaction mixture may then be heated to reaction conditions of 60°C-180°C, preferably 150°C-170°C, say 155°C. First functionalizing agent, typically phenothiazine, is admitted in amount of 1-40 parts, say 5 parts, as a solution in 2-20 parts, say 8 parts of diluent-solvent typically synthetic diester base stock oil. Phenothiazine may be added alternatively as a powder or as a slurry in oil or other solvent used as reaction medium. It is a feature of this invention that the first functionalizing agent may impart activity both as a pour-point depressant viscosity index improver and an antioxidant when the product is present in anti-oxidant amounts of 1-20 parts, say 5 parts per 100 parts of eg. a lubricating oil. The polymer containing dicarboxylic acid anhydride moieties is coupled preferably in the polymerization solvent in which it was prepared with a second functionalizing agent. According to the invention the amine is a N-methylpiperazine or 3(N,N-dimethylamino)propylamine. In practice of the process of this invention, 100 parts of charge polymer containing anhydride groups may be added to 100-1000 parts, say 300 parts of diluent-solvent. Typical diluent-solvent may be a hydrocarbon solvent such as mineral oil, n-hexane, n-heptane, or tetrahydrofuran. Preferred solvent may be a commercial mineral oil. Reaction mixture may then be heated to reaction conditions of 60°C-180°C, preferably 150°C-170°C, say 155°C. Second functionalizing agent, typically N-methylpiperazine is admitted in the amount of 1-40 parts, say 5 parts to the reactor. It is a feature of this invention that the second functionalizing agent may impart activity such as a pour-point depressant, viscosity index improver and a dispersant when the product is present in amounts of 1-20 parts, say 5 parts per 100 parts of a lubricating oil. It is a feature of the process of this invention to effect functionalization with the first functionalizing agent and the second functionalizing agent simultaneously. In practice of the process of this invention, 100 parts of charge polymer bearing anhydride units may be added to 100-1000 parts, say 300 parts of diluent-solvent. Typical diluent-solvent may be a hydrocarbon solvent such as n-hexane, n-heptane, tetrahydrofuran, or mineral oil. Preferred solvent may be a commercial mineral oil of low sulfur content and high content of saturated hydrocarbons. Reaction mixture may then be heated to reaction conditions of 60°C-180°C, preferably 150°C-170°C, say 155°C. Preferably first functionalizing agent, typically phenothiazine, in amount of 1 - 20 parts, say 4 parts may be mixed with 0.5 - 20 parts, say 2 parts of second functionalizing agent, typically N-methyl piperazine, and the mixture may be admitted to the reaction system. Reaction is typically carried out at 60°C-180°C, say 155°C for 0.5 - 20 hours, preferably 2 - 10 hours, say 5 hours during which time coupling of functionalizing agent with anhydride moeties containing polymer. Typically the product may by contain 0.1 - 60, say 3 units derived from first functionalizing agent and 0.1 - 60, say 3 units derived from second functionalizing agent per 1000 carbon atoms of the charge backbone polymer. Typical dually functionalized product polymers which may be used in practice of the process of this invention may include units derived from those listed below in Table 4. E. 8 mole % maleic anhydride 60 mole % lauryl methacrylate 24 mole % stearyl methacrylate 4 mole % phenothiazine 4 mole % N-methyl piperazine F. 6 mole % maleic anhydride 66 mole % lauryl methacrylate 22 mole % stearyl methacrylate 3 mole % phenothiazine 3 mole % N-methyl piperazine It is a feature of this invention that the so-prepared polymer may find use in lubricating oils as multifunctional additive (e.g. viscosity index improvers which provide pour depressant, dispersant, and anti-oxidant properties, etc) when present in effective amount of 0.2-20.0 wt.%, preferably 2.0-10.0 wt.%, say 5.0 wt.%. Lubricating oils in which the multifunctional additives of this invention may find use may include automotive, aircraft, marine, railway, etc. oils; oils used in spark ignition or compression ignition; summer or winter oils; etc. Typically the lubricating oils may be characterized by an ibp of 299°C to 349°C (570°F to 660°F), say 321°C (610°F); an ep of 399°C to 649°C (750°F to 1200°F), say 549°C (1020°F); and an API gravity of 25 to 31, say 29. A typical lubricating oil in which the polymer of this invention may be present may be a standard SAE 5W-30 hydrocarbon motor oil formulation having the composition shown below in Table 5. W% Base Oil 86 -Viscosity Index Improver (product of the invention) 5 -Standard Additive Package: 9 Polyisobutenyl ( M n 1290) succinimide (dispersant); calcium sulfonate (detergent); Zinc dithiophosphate (anti-wear); di-nonyl diphenyl amine (anti-oxidant); 4,4'-methylene-bis (2,6-di-t-butyl phenol) (antioxidant); Use of the additive of this invention makes it possible to readily increase the viscosity index by 25-40 units, say 35 units and to obtain improved ratings on the tests measuring the dispersancy of the system. The viscosity index is determined by ASTM Test D-445. Practice of the process of this invention will be apparent to those skilled in the art from the following examples wherein, as elsewhere in this specification, all parts are parts by weight unless otherwise set forth. Control examples are designated by an asterisk and invention examples by two asterisks. DESCRIPTION OF THE PREFERRED EMBODIMENTS EXAMPLE 1 In this example which describes the best mode presently known of carrying out the first step, there is charged to a reaction vessel, under nitrogen, 11.08g maleic anhydride first monomer, 161.92g lauryl methacrylate second monomer, 79.75g of stearyl methacrylate auxiliary second monomer, 0.25g of lauryl mercaptan chain transfer agent, and 45.55g of mineral oil as a polymerization solvent. The reaction mixture is heated to 83°C with agitation under nitrogen; and 0.40g of azobisisobutyronitrile (AIBN) polymerization initiator is added. The reaction mixture is stirred for 3 hours, followed by addition of 0.09g of azobisisobutyronitrile and 199.3g of 100E Pale Oil. Heating at 83°C is continued for 1.5 hour and then the temperature is raised to 100°C for an additional hour. The reaction mixture is then cooled to room temperature. EXAMPLE 2 The reaction conditions are the same as in Example 1. Charge included 14.85g of maleic anhydride, 159.39g of lauryl methacrylate, and 78.51g of stearyl methacrylate. All other regent quantities are the same as in Example 1. EXAMPLE 3 Reaction conditions are the same as in Example 1. Charge includes 16.63g of maleic anhydride, 158.20g of lauryl methacrylate, and 83.47g of stearyl methacrylate. All other reagent quantities are the same as in Example 1. EXAMPLE 4 Reaction conditions are the same as in Example 1. Charge includes 16.63g of maleic anhydride, 158.20g of lauryl methacrylate, and 77.92g of stearyl methacrylate. All other reagent quantities are the same as in Example 1. EXAMPLE 5 In this example there is added to the product of Example 1 in the same reaction vessel 45.02g of phenothiazine and 19.33g of undecylamine. The reaction temperature is raised to 160C and maintained for 5 hours. The reaction mixture is then cooled to room temperature. EXAMPLE 6 In this example, there is added to the product of Example 1 in the same reaction vessel a 22.61g of N-methylpiperazine. The reaction conditions are the same as in Example 5. EXAMPLE 7 ** In this example there is added to the product of Example 3 in the same reaction vessel a mixture of 22.5g phenothiazine and 19.33g of N-methylpiperazine. The reaction conditions are the same as in Example 5. EXAMPLE 8 ** In this example there is added to the product of Example 1 in the same reaction vessel a mixture of 22.50g of phenothiazine and 11.54g of 3(N,N-dimethylamino) propylamine. The reaction conditions are the same as in Example 5. EXAMPLE 9 ** In this example there is added to the product of Example 2 in the same reaction vessel a mixture of 30.15g of phenothiazine and 14.85g of 3(N,N-dimethylamino)propylamine. The reaction conditions are the same as in Example 5. EXAMPLE 10 ** In this example there is added to the product of Example 4 in the same reaction vessel a mixture of 33.7g of phenothiazine and 16.63g of 3(N,N-dimethylamino)propylamine. The reaction conditions are the same as in Example 5. EXAMPLES 11-18 In these Examples, a Base Blend is employed as follows: Composition Wt. % Solvent Neutral Oil 130 75.25 Solvent Neutral Oil 335 21.74 Zinc Dithiophosphate 1.12 Dinonyldiphenylamine 0.39 Magnesium Sulfonate 1.50 Poly(siloxane) 150ppm ANALYSES Kinematic Viscosity, cst, 40C 31.50 100C 5.36 Pour Point, D-97 - 15°C (+5°F) Ash, Sulfated % D-874 0.93 Phosphorus, % X-Ray 0.11 Sulfur, % X-Ray Total 0.40 Zinc, % X-Ray 0.12 Magnesium, % 0.33 Cold Cranking Simulator, cP, -18C 1660 The compositions of this invention of Examples 1, 4-10 were blended at a 4.85 wt.% polymer level in the above Base Blend; and the resultant composition was tested for Dispersancy by the Bench VC Test. In this test, the dispersancy is measured against three standards (excellent/good/poor) and improved dispersancy is evidenced by the lower ratings provided below in Table 6. Example Polymer of Example BVCT Result Standards 11* 1 98.5 8/29/68 12* 4 98.6 8/29/68 13 5 98.0 9/25/56 14 6 11.4 10/20/55 15** 7 28.4 9/25/56 16** 8 29.0 6 34/61 17** 9 24.5 7/20/53 18** 10 24.2 7/20/53 From the above, it will be apparent to those skilled in the art that the product of Examples 11* and 12* (which were not functionalized at all) and product of Example 13 (which was functionalized with phenothiazine) are not characterized by the desired degree of dispersancy. Examples 14-18 which, in accordance with this invention, contain polymer which is functionalized phenothiazine and amine, are characterized by desired degree of dispersancy. In a further series of tests, the compositions of Examples 1, 5, 8 and 10 were blended at 0.75 w % polymer concentration in SNO-130 oil and evaluated in the Bench Oxidation Test. In this test, a solution containing 1.5 wt.% of test polymer in SNO-130 oil is blown with air while heated and stirred. Samples are withdrawn periodically for analysis by Differencial Infrared Absorption (DIR) to observe changes in the carbonyl vibration band at 1710 CM⁻¹. Higher carbonyl vibrational band intensity indicates a lower thermal-oxidative stability of the sample as shown below in Table 7. Example Polymer of Example Oxidation Index @ 144 hours 19* 1 17.4 20 5 2.2 21** 7 1.7 22** 8 2.2 23** 10 2.9 From the above, it will be apparent to those skilled in the art that the composition of Example 19* fails to exhibit anti-oxidation ability. Note that the compositions of Examples 20-23 of the instant invention exhibit antioxidant characteristics. In a further series of tests, the Thickening Effect is measured. The compositions of Examples 5-10 are blended at 5 w % polymer composition in SNO-100 and the kinematic viscosity at 100°C is measured as shown below in Table 8. Example Polymer of Example Kinematic Viscosity cst @ 100°C Thickening Effect CST 24 5 13.00 4.87 25 6 11.74 3.61 26** 7 11.75 3.60 27** 8 13.16 5.03 28** 9 12.70 4.57 29** 10 12.93 4.80 From the above Table, it is apparent that the products formulated with the additives of this invention provide increased thickening effect. Although this invention has been illustrated by reference to specific embodiments, it will be apparent to those skilled in the art that various changes and modifications may be made which clearly fall within the scope of this invention.

Claims: A lubricating oil composition comprising lubricating oil and an effective amount of 0.2 to 15 weight%, based on the total composition, of one or more functionalized polymers as multifunctional additives obtained by copolymerizing first monomer(s) and second monomer(s) in a mole ratio of 1:2 bis 1:12, under free radical polymerization conditions, (i) said first monomer is maleic anhydride, and (ii) said second monomer is an acrylate having the formula wherein R is the stearyl and/or lauryl group, and R' is hydrogen or methyl, thereby forming a copolymer backbone of molecular weight M n from 10,000 to 1,000,000 bearing at least two pendant side chains containing anhydride moities, the monomers being employed in pure form or in commercially available form, reacting said chains containing dicarboxylic acid anhydride moieties with a mixture of phenothiazine or substituted phenothiazine as first agent and N-methyl piperazine and/or 3-(N,N-dimethylamino)propylamine as second agent; thereby forming the functionalized polymers; and recovering said functionalized polymers. A lubricating oil composition of claim 1 wherein said functionalized polymers are copolymers of molecular weight M n from about 20,000 to about 180,000. A lubricating oil composition of claim 1 or claim 2, wherein the method of obtaining said functionalized polymers comprises copolymerizing and functionalizing in the presence of diluent(s)/solvent(s), preferably in the presence of lubricating oil in which the product is to be used. A lubricating oil composition of any of claims 1 to 3, wherein the effective amount is about 2 to 10 weight%, based on the total composition.

Inventors: HART WILLIAM PIUS, KAPUSCINSKI MARIA MAGDALENA, LIU CHRISTOPHER SOUNDANG, HART, WILLIAM PIUS, KAPUSCINSKI, MARIA MAGDALENA, LIU, CHRISTOPHER SOUNDANG
Applicants: TEXACO DEVELOPMENT CORP, TEXACO DEVELOPMENT CORPORATION
Application year: 1987
Main classification: C08F8
IPC codes: C10M145, C08F220, C08F20, C10M151, C10N30, C10M149, C08F8