HIGH RATE LASER ETCHING TECHNIQUE

Abstract: A method and means for high-rate etching a material is disclosed including the steps of disposing a gas mixture of a fluorine-containing molecule and H2 over the surface of a material to be etched; and laser dissociating this fluorine-containing molecule in the gas mixture to cause very fast etching of the material surface. In a preferred embodiment, the fluorine-containing molecule is chosen from the group of NF3, SF6, and COF2, and the surface to be etched is unmasked silicon.

Description: Background of the Invention The present invention relates generally to material etching, and more particularly to high-rate etching via energy beam dissociation. Etching is a standard process step used in the fabrication of many of products, most notably semiconductor circuit products for the electronics industry. There are a variety of etching techniques based on the use of either wet chemical etch baths or dry etch plasmas as the etching medium. All of these techniques are characterized by the requirement to initially deposit a mask layer, typically a photoresist layer, over the surface to be etched to thereby define a surface pattern to be etched therein. Such a masking step typically requires the separate steps of depositing the mask layer, properly developing that layer, and after the etching step, removing the mask layer. It would be highly desirable to define the desired etch pattern during the etch step itself, and thereby eliminate the above-described masking steps. However, the etch-rate for such an etch process must be fast enough to provide a clear process advantage over current etch techniques. In this regard, it is known that a surface may be etched by laser-induced dissociation of a molecule to form a radical etchant adjacent to the surface to be etched. For example, Loper and Tabat, Applied Physics Letters 46(7), 1 April 1985, at page 675, disclose the use of an ArF laser to dissociate COF2 to obtain fluorine radicals for etching silicon. Likewise, Chuang, Journal of Chemical Physics, 74(2), 15 January 1981, at page 1453, discloses the use of a CO2 laser to dissociate SF6 to obtain fluorine radicals for etching silicon. Both of these references describe photo dissociation techniques for generating radical etchants from the interaction of radical precursor molecules with photons at or near a gas-substrate interface. The substrate at the interface undergoes an etching reaction with the radicals in the localized regions exposed to the laser light via the formation of volatile compounds containing the substrate elements. By controlling the localized areas exposed to laser light, it is possible to simultaneously pattern and etch the substrate with submicron resolution. However, radical etching via laser-induced dissociation is slow relative to currently available etching processes. Document EP-A-0 209 288 discloses a method of etching a III-V semiconductor by exposing the surface of said semiconductor to a mixture of hydrogen and halogen gas while illuminating said surface with a beam of radiation adapted to dissociate said halogen gas into halogen radicals which subsequently etch said surface. The invention as claimed is intended to eliminate most presently-required substrate masking steps while providing high-rate radical etching of a material via energy-beam dissociation. Summary of the Invention Briefly, the present invention comprises a method for high-rate etching a semiconductor material, including the steps of: disposing a gas mixture of a fluorine-containing molecule consisting of NF3 or SF6 and H2 over the surface of a semiconductor material to be etched in a fluorine-containing molecule/H2 pressure ratio in the range of 2 to 14 for NF3 and a ratio of 1-10 for SF6; directing a beam of energy adjacent to said semiconductor material surface to be etched, with said energy beam having an energy which approximately matches that required for dissociating said molecule and having sufficient energy to cause said molecule to be dissociated into etching components. In another embodiment of the present invention, the disposing step may be replaced by the step of disposing a gas mixture of H2 and COF2 over the surface of a semiconductor material to be etched in a COF2/H2 pressure ratio in the range of 1 to 10. Brief Description of the Drawing The Figure shows one embodiment of an apparatus which may be utilized to implement the present invention. Detailed Description of the Preferred Embodiment It has been discovered that photo dissociating a molecule to obtain a fluorine-atom radical in the presence of H2 yields an extremely high etch rate on an adjacent semiconductor surface to be etched. This very high etch rate is surprising and unexpected in view of prior art teachings in the plasma-etching field that the addition to be of H2 reduces the etch rate of fluorine radicals and is thus to be used as a scavenger gas. In this regard, see U.S. Patent Nos. 4,579,623 and 4,505,949. The method of the present invention will now be described in the context of the device shown in the Figure. It should be noted that the device shown in the Figure was an experimental device utilized in making the present discoveries. The present invention is not limited in any fashion to this particular experimental device shown in the Figure. Referring now to the Figure, there is shown a standard etching chamber 10 for holding a semiconductor wafer of material 12 to be etched. The wafer 12 is disposed with its surface to be etched centered about a center line 11. The chamber 10 includes a line 14 connected to a pump for creating a vacuum within the chamber. The chamber further includes a gas input line 16 providing a desired etching gas mixture into the chamber. The chamber 10 also includes a pressure gauge 18 and a pedestal 20 for holding the wafer 12 to be etched. The pedestal 20 is connected in the Figure to a quartz crystal micro balance for detecting changes in mass in the wafer 12. This micro balance operates by generating a frequency which is dependent upon the mass of the wafer 12 and measuring changes in this frequency to thereby measure the etch rate on the surface of the wafer 12. Means 22 is provided in the Figure for dissociating one of the etching gas molecules contained in the chamber in adjacency to the surface of the wafer 12 to be etched. In the embodiment shown in the Figure, this dissociating means 22 may comprise means for directing a beam of energy at the surface of the wafer 12 to be etched, with the energy beam having an energy which approximately matches a strong absorption line of the molecule to be dissociated. In the experimental embodiment shown in the Figure, the means for directing a beam of energy comprises a laser 24 in combination with various optical components to direct the beam from the laser 24 through one or more laser beam transparent windows 26 or 28 in the chamber 10. In the embodiment shown in the Figure, the laser beam optics comprise an iris diaphragm 30, a beam splitter 32, a filter 34, a lens 35, mirrors 36 and 38, a filter 37, and a lens 40. This set of optical components is configured to direct the beam from the laser 24 so that a portion thereof is transmitted through the optical window 28 to impinge orthogonally on the surface of the wafer 12, and also to direct a portion of the laser beam through the optical 26 in the chamber 10 to propagate adjacent to and parallel with the surface of the wafer 12. In operation, the laser beam from the laser 24 is directed through the diaphragm 30 which operates to define the beam size. This defined laser beam is then directed through the beam splitter 32 which transmits a portion of the beam along the path 42, and reflects a portion of the beam along the path 44. The laser beam transmitted along the path 42 propagates through the filter 34 and the lens 35 and through the window 28 into the chamber 10. The filter 34 in path 42 is a power attenuator for controlling the power of the laser beam. The lens 35 is for focussing the laser beam to a point along the center line 11 for the wafer 12, with the focus point either at the wafer surface or in the adjacency thereto. Likewise, the portion of the laser beam reflected along the optical path 44 is reflected by the mirror 36, transmitted through the filter 37, reflected by the mirror 38, and focused by the lense 40 to propagate through the window 26 into the chamber 10. Again, the filter 37 is a power attenuator for controlling the power of the laser beam. The lense 40 is utilized to focus the laser beam at the center line 11 for the wafer 12. The apparatus shown in the Figure further may conveniently include some means for aligning the laser beam in the system. In the embodiment shown, a small He-Ne laser 50 is directed along the same path as the beam from the laser 24 by means of a beam splitter 52. Alignment may be accomplished by utilizing this small laser 50 prior to turning on the dissociating laser 24. The apparatus in the Figure further includes a third window 54 and a power meter/beam stop 56 for measuring the beam power of the dissociating laser 24. As noted previously, the present invention is based on the unexpected discovery that the energy-beam dissociation of a fluorine-containing molecule in the presence of H2 adjacent to the surface of a semiconductor material to be etched causes an extremely fast etching of this material surface. Three examples are now provided for the present invention. In the first example, an NF3 and an H2 gas mixture at room temperature was utilized to verify the present invention. In this experiment, the NF3 (nitrogen trifluoride) gas pressure was varied over a series of runs from 3.3 kPa (25 Torr) to 20 kPa (150 Torr), while the H2 gas was varied from 666 Pa (5 Torr) to 4 kPa (30 Torr). It was found that pressure ratios of NF3/H2 in the range 2 - 14 provided extremely high-rate etching of an underlying silicon material, when the NF3 molecule was dissociated. This dissociation was achieved by utilizing a CO2 laser within an energy range of 100 mJ per pulse up to 600 mJ per pulse. This laser generated a wavenumber of 922 cm-1 which matches a strong absorption line in NF3. The focusing of the CO2 laser beam was accomplished by a zinc selenide lens 40 with a focal length of 15 cm. In a preferred embodiment, 1.33 kPa (10 Torr) of H2 was utilized in combination with 9.33 kPa (70 Torr) of NF3 to provide a resulting pressure of 10.66 kPa (80 Torr). The monitoring of the etching of the silicon by means of the quartz crystal micro balance showed that one pulse from the CO2 laser 24 resulted in an instantaneous etching, followed by a dark etching that continued for several minutes. The final etch rate was found to be in excess of 20 nm/cm2/pulse. In contrast, using the NF3 alone at 9.33 kPa (70 Torr) and using the same laser conditions, an etch rate of only approximately 0.2 nm/cm2/pulse was observed. Accordingly, it can be seen that adding the H2 to the NF3 unexpectedly resulted in an enhancement of over 2 orders of magnitude in the etch rate, relative to the NF3 alone. It is speculated that the above-described unexpected result was caused by the energy beam acting to promote a photo-induced chemical reaction between the NF3 and the H2 (or their reaction products) and the silicon that created conditions under which rapid etching of the silicon occurred. It is speculated that the H2 or possibly HF acted to remove an oxide on the semiconductor surface to thereby promote the fast etching of the underlying silicon. It is also speculated that the complexity of standard plasma ion products tends to negate this effect in plasma etching devices. It should be noted that the foregoing experiment with NF3 is significant because NF3 is a fairly inert gas which will not act upon a given substrate such as silicon unless photoactivated by a laser. The laser essentially breaks up the NF3 molecule into its constituent parts including at least one fluorine atom, which is highly reactive. This relative inertness of the NF3 molecule in combination with its very fast etching rate when dissociated in the presence of H2 makes it a prime candidate for implementing a maskless etching process. The impingement of the laser beam on or adjacent to the surface of the wafer being etched could be used to define a predetermined etch pattern on the wafer surface without the use of a mask layer. Such a predetermined pattern could be defined on the surface of the wafer 12 simply by scanning the laser beam in a predetermined pattern, as is well known in the art. Alternatively, the laser beam could be directed along a stationary axis, and the wafer 12 translated by means of standard X-Y servomotors in a well known manner. A step and repeat pulsed laser process could be utilized with either pattern determining technique. It should also be noted that both laser beams, i.e., the beam directed parallel to the surface and the beam directed perpendicular to the surface of the wafer 12 could be utilized simultaneously to obtain a desired etching rate. It should be noted that NF3 is advantageous for maskless etching because it is a relatively small molecule whose dissociated components will not cause undesirable secondary reactions which could, for example, deposit some form of a polymer on the surface being etched. Finally, it should be noted that NF3 is advantageous because it can be dissociated with long wavelengths. It should be noted that there are a number of other strongly absorbing lines in the NF3 molecule which may be utilized for dissociation. For example, an excimer UV laser could be utilized to dissociate the NF3 molecule. As a further example of the present invention, the laser dissociation of SF6 in the presence of H2 could be utilized to obtain the desirable high-rate etching of a substrate such as silicon. In this regard, the general dissociation of SF6 without H2 is described in the previously noted article by T.J. Chuang entitled "Multiple Photon-Excited SF6 Interaction With Silicon Surfaces", Journal of Chemical Physics, 74(2):1453(1981). In this example, a pressure of 0.13 - 1.33 kPa (1-50 Torr) of SF6 may be utilized with a sufficient pressure of H2 to realize a SF6/H2 pressure ratio range of 1-10. The dissociation of the SF6 molecule may be obtained by means of a CO2 infrared laser at a wavelength of 10.6 micrometers and with a pulse energy in the range 100-600 mJ per pulse. As a third example, COF2 may be energy-beam dissociated in the presence of H2 to obtain high-rate etching of a material. COF2 dissociation without H2 is discussed in the previously noted article by G.L. Loper and M.D. Tabat entitled "UV Laser-Generated Fluorine Atom Etching of Polycrystalline Si, Mo, and Ti", Applied Physics Letters 46(7:654(1985). In this example, a COF2 pressure of 6.7 - 66.7 kPa (50-500 Torr) may be utilized in combination with 6.7 kPa (50 Torr) of H2 in order to implement a COF2/H2 ratio range of 1-10. COF2 could be dissociated by means of an argon fluoride UV laser tuned to 0.193 micrometers and using a power of 50-100 mJ per pulse. The above-described invention discloses a method and means for obtaining an extremely high etch rate by energy-beam dissociating a fluorine-containing molecule in the presence of H2. This invention thus makes feasible maskless etching of a surface, thereby eliminating the standard mask formation and mask removal steps.

Claims: A method for etching a semiconductor material, including the steps of: disposing a gas mixture of a fluorine-containing molecule consisting of NF3 or SF6 and H2 over the surface of a semiconductor material to be etched in a fluorine-containing molecule/H2 pressure ratio in the range of 2 to 14 for NF3 and a ratio of 1-10 for SF6; directing a beam of energy adjacent to said semiconductor material surface to be etched, with said energy beam having an energy which approximately matches that required for dissociating said molecule and having sufficient energy to cause said molecule to be dissociated into etching components. A method for etching a semiconductor material, including the steps of: disposing a gas mixture of COF2 and H2 over the surface of a semiconductor material to be etched in a COF2/H2 pressure ratio in the range of 1 to 10; and directing a beam of energy adjacent to said semiconductor material surface to be etched, with said energy beam having an energy which approximately matches that required for dissociating the COF2 molecule and having sufficient energy to cause said molecule to be dissociated into etching components. A method as defined in claims 1 or 2, wherein said material to be etched is silicon.

Inventors: BRANNON, JAMES HAMMOND
Applicants: INTERNATIONAL BUSINESS MACHINES CORPORATION
Application year: 1987
Main classification: H01L21
IPC codes: H01L21