ANTI-REFLECTION PLATE FOR DISPLAY DEVICE

Abstract: An anti-reflection plate for a display device, which plate comprises a transparent substrate wherein, on one or both surfaces of the substrate, a flat first layer consisting of a transparent hardening agent containing a silicon-containing organic compound has been applied and dried and, on the first layer, a second layer consisting of a transparent hardening agent containing a silicon-containing compound has been spray coated and hardened to form an uneven surface having projections each having a height of 0.1 to 2.0 µm in height, a diameter of 10 to 100 µm and a height/diameter ratio of 1/30 to 1/500 can effectively prevents reflection of external light on a screen of a display device without deteriorating resolution of an image on the screen.

Description: The present invention relates to an anti-reflection plate for a display device such as a CRT (cathode-ray tube), a light emitting diode and the like. More particularly, it relates to an anti-reflection plate which is installed in or placed on a screen of the display device to prevent or decrease reflection of external light on the screen and has good abrasion resistance, moisture resistance and chemical resistance. When the display device such as the CRT, the light emitting diode, a liquid crystal and a plasma display (e.g., a TV set, a watch or clock or an electronic calculator) is used in daylight or under artificial light, external light reflects on the surface of the screen of the display device or a surface of a transparent plate covering the screen so that the screen becomes glare, contrast of the displayed image is deteriorated or the image on the screen becomes less visible. To overcome such problems caused by the reflection of the external light, various anti-reflection plates have been proposed. (1) A transparent plate such as a methacrylic resin or glass plate a surface of which is physically or chemically roughened. Such anti-reflection plate has greatly decreased light transmission so that the image on the screen becomes too dark to read even under the normal conditions since unevenness of the screen surface is too deep or a shape of each projection is too sharp. In addition, although the anti-reflection plate can suppress glaring of the screen since it randomly reflects the external light, it cannot decrease the amount of the reflected light so that the surface of the anti-reflection plate becomes light and in turn the image on the screen becomes less visible. (2) A transparent synthetic resin plate onto which surface, unevenness is transferred by means of a physically or chemically roughened glass plate or a roughened roll. This anti-reflection plate has the same disadvantages as that of the anti-reflection plate (1). Further, it is easily damaged and has poor chemical resistance. (3) An anti-reflection plate consisting of a mechanically roughened transparent substrate coated with a transparent material to form unevenness on the surface. Since the mechanically formed unevenness of the substrate is too deep or the shape of each projection is too sharp as described in the above (1), the unevenness of the coated material is still deep so that it is very difficult to read the image on the screen of the display device. Further, it is difficult to control the thickness of the coating of the transparent material which reflects the external light. (4) An anti-reflection plate consisting of a transparent substrate and a coating of a transparent material containing a delustering agent. This anti-reflection plate has several drawbacks such as whitening of the coating due to a difference of the refractive indexes between the coating material and the delustering agent, irregularity or scattering of the unevenness due to sedimentation or agglomeration of the delustering agent. In addition, any of the conventional anti-reflection plates tends to be easily damaged on its surface, and the damage or flaw on the surface decreases the properties and commercial value of the anti-reflection plate. As described in the above, the anti-reflection plate should have both the glare shield effect which is achieved by scattering the external light by suitable unevenness of the surface and resolution of the image displayed on the screen of the display device. However, the conventional methods for roughening the surface of the anti-reflection plate are not satisfactory, and the anti-reflection plates are not sufficient in view of preventing flaw on the surface. One object of the present invention is to provide an anti-reflection plate for a display device, which does not suppress scattering of the light from the display device and can maintain good readability of the image on the screen of the display device. Another object of the present invention is to provide an anti-reflection plate for a display device, which can prevent glare caused by external light by scattering it. Further object of the present invention is to provide a flaw-free anti-reflection plate having good mechanical and chemical properties such as abrasion resistance and chemical resistance. According to the present invention, there is provided an anti-reflection plate for a display device. comprising a transparent substrate having on one or both surface(s) a flat transparent first layer and, on the first layer, a second transparent layer, wherein the first layer is applied as a composition comprising colloidal silica, an alkoxysilane, a mixture of two or more alkoxysilanes, a partially hydrolized alkoxysilane and/or a partially condensed alkoxysilane and, optionally, a polymer; and dried at room temperature or slightly elevated temperature, and the second layer is spray coated as a composition comprising colloidal silica, an alkoxysilane, a mixture of two or more alkoxysilanes, a partially hydrolized alkoxysilane and/or a partially condensed alkoxysilane and, optionally, a polymer and 70 to 90% by weight of a diluent having a boiling point of 110°C to 200°C under atmospheric pressure; and thermally hardened to form an uneven surface having projections each having a height of 0.1 to 2.0 µm, preferably 0.1 to 1.2 µm, a diameter of 10 to 100 µm and a height/diameter ratio of 1/30 to 1/500. The anti-reflection plate according to the present invention is attached on the screen of the display device to prevent reflection of the external light so as to improve the readability of the image on the screen. Therefore, the anti-reflection plate is required to be transparent and to have good resolution, that is, the image being clearly read through the anti-reflection plate without any blur. When the projection of the unevenness formed on the surface of the anti-reflection plate of the present invention has a height lower than 0.1 µm, the anti-reflection plate hardly prevents reflection of the external light. When the projection of the unevenness has a height higher than 20 µm, the anti-reflection plate has poor resolution so that the image on the screen cannot be read clearly. When the diameter of the most of the projections is less than 10 µm, the image on the screen cannot be clearly read irrespective of the height of the projections. When the diameter is larger than 100 µm, the anti-reflection plate has decreased anti-reflection effect. When the height/diameter ratio of the projection is larger than 1/30, the resolution of the anti-reflection plate is deteriorated. When said ratio is smaller than 1/500, the anti-reflection plate has deteriorated anti-reflection effect. The substrate of the anti-reflection plate may be made of any of transparent materials. Preferred examples of the transparent material are methacrylic resins, polycarboname resins, acrylonitrile-styrene copolymer resins, methyl methacrylate-styrene copolymer resins, polyvinyl chloride resins and glass. Among them, the methacrylic resins are more preferable because of their excellent transparency, surface hardness and adhesion. As the composition containing the silicon-containing organic compound, those not containing any material that roughens the surface of the coated layer (e.g. a delustering agent) are preferred. Examples of the composition containing the silicon-containing organic compound are colloidal silica, an alkoxysilane, a mixture of two or more of alkoxysilanes, a partially hydrolized alkoxysilane and a partially condensated alkoxysilane. The composition may optionally contain a polymer such as an acrylic polymer or a vinyl acetate base polymer. Specific examples of the alkoxysilane are tetraalkoxysilanes of the formula: Si-(OR₁)₄ alkyltrialkoxysilanes of the formula: R₂-Si-(OR₁)₃ and dialkyldialkoxysilanes of the formula: wherein R₁, R₂ and R₃ are the same or different and each an alkyl group having 1 to 5 carbon atoms, an acetoxy group, a vinyl group, a (meth)acryloxy group, an allyl group, a phenyl group, a glycidyl group, an alkylthiol group having 1 to 5 carbon atom in the alkyl group or an alkylamino group having 1 to 5 carbon atom in the alkyl group. In addition to the above described colloidal silica and alkoxysilane, the composition containing the silicon-containing organic compound to be used to form the first layer may contain water or an acid which is necessary for hydrolysis, and as a diluent, a solvent such as alcohols (e.g., methanol, ethanol, propanol, butanol), ketones (e.g., acetone, methyl ethyl ketone, methyl isobutyl ketone), esters (e.g., ethyl acetate, methyl acetate, isopropyl acetate, isobutyl acetate), cellosolves (e.g., methylcellosolve, ethylcellosolve, butylcellosolve, cellosolve acetate), carboxylic acids (e.g., formic acid, acetic acid, propionic acid), aromatic hydrocarbons (e.g., benzene, toluene, xylene, mesitylene) and halides. The kinds of such additives depend on several factors such as the kind of the substrate and the evaporation rates of the additives. The mixing ratio of the composition containing the silicon-containing organic compound and the additive(s) may vary in a wide range. Among the solvents, a lower alkyl carboxylic acid such as formic acid and acetic acid is useful since it improves the adhesiveness of the layer to the substrate and stability of the layer. The composition containing the silicon-containing organic compound to be used to form the second layer should contain 70 to 90 % by weight of a diluent having a boiling point of 110°C to 200°C to form desired unevenness on the surface. When the prepared composition contains a sufficient amount of the diluent, it can be directly used. However, when the amount of the diluent is not sufficient, an additional amount of the diluent is added to the composition. When the amount of the diluent having a boiling point of 110 to 200°C is less than 70 % by weight, the degree of the unevenness is greatly affected by external factors such as atmospheric temperature so that the uneven surface is not formed reproducibly. In addition, the height/diameter ratio of the projection becomes large so that it is hardly controlled to less than 1/30. When the amount of the diluent is more than 90 % by weight, the height/diameter ratio of the projection becomes small so that it is hardly controlled to a ratio of more than 1/500. Specific examples of the diluent having a boiling point of 110 to 200°C are aromatic hydrocarbons (e.g., toluene, xylene), ketones (e.g., methyl isobutyl ketone, cyclohexanone), cellosolve (methylcellosolve, ethylcellosolve, butylcellosolve) and alcohols (e.g. amyl alcohol, n-butanol). To form the flat first layer, the composition is applied on the surface of the substrate by any of conventional methods such as dip coating, spray coating or flow coating. The applied composition is then dried at room temperature (or slightly elevated temperature). Thereafter, the composition for the second layer is applied on the flat first layer and hardened. To form minute unevenness on the surface, the second layer is applied by spray coating such as air spraying, airless spraying, electrostatic coating, ultrasonic spraying or centrifugal spraying. Other coating method which can uniformly form fine particles of the coating may be used to apply the second layer. The second layer may be coated twice or more to decrease surface gloss and form the uniform particles of the coating. The anti-reflection coating comprising the above first and second layers may be formed directly on at least one surface of the substrate. When the composition of the first layer has insufficient adhesiveness with the surface of the substrate, a suitable primer can be supplied between the substrate and the first layer. Examples of the primer are aromatic hydrocarbons (e.g., toluene, xylene), esters (e.g., ethyl acetate), ketones (e.g., acetone, methyl isobutyl ketone, methyl ethyl ketone), ethers (e.g., tetrahydrofuran, dioxane) or mixture thereof, one or more of them containing a dissolved (meth)acrylic polymer or a silane or titan type coupling agent. The substrate material may contain suitable additives such as a coloring agent, an anti-static agent, a filler, a UV absorber or a heat absorber. On the substrate, a polarizing film or membrane, a metal mesh or a synthetic fiber mesh with metal plating may be laminated or bonded. When the anti-reflection plate of the present invention is used as a cover of any display device such as a CRT installed in a TV set or a terminal of a computer or word processor, a liquid crystal display, a plasma display, a light emitting diode display and an electroluminescence display, reflection of the external light is suppressed without deteriorating the readability of the image on the screen of the display and prevent any adverse effect caused by the display device. Practical and presently preferred embodiments of the present invention are shown in the following Examples wherein parts and % are by weight unless otherwise indicated. In the Examples, one of the following coating compositions was used: Coating Compositions Composition A 100 parts of partial hydrolyzate of organosiloxane prepared by refluxing a mixture of isopropanol (68 g), tetraethoxysilane (38 g), methyltriethoxysilane (72 g) and 0.05N hydrochloric acid (36 g); 20 parts of a copolymer prepared by thermally polymerizing butyl acrylate (40 g) and 2-hydroxyethyl methacrylate (10 g) in the presence of azo-bis-isobutyronitrile (0.5 g) in ethyl alcohol (300 g) and pouring the reaction product in petroleum ether; 0.4 part of sodium acetate; 20 parts of acetic acid; 40 parts of n-butanol Viscosity: 0.01 Pa x s (10 centipoise) (20°C) Content of the diluent: 33.3 % (n-butanol and acetic acid) Composition B 100 parts of Composition A; 25 parts of toluene; 75 parts of methyl isobutyl ketone; 100 parts of butylcellosolve Viscosity: 0.0025 Pa x s (2.5 centipoise) (20°C) Content of the diluent: 77.8 % (n-butanol, acetic acid, toluene, methyl isobutyl ketone and butylcellosolve) Composition C 100 parts of Composition A; 25 parts of toluene; 75 parts of methyl isobutyl ketone; 30 parts of butylcellosolve Viscosity: 0.004 Pa x s (4 centipoise) Content of the diluent: 71.0 % Composition D 100 parts of Composition A; 15 parts of toluene; 55 parts of methyl isobutyl ketone; Viscosity: 0.007 Pa x s (7 centipoise) (20°C) Content of the diluent: 60.7 % Composition E 100 parts of Composition A; 15 parts of toluene; 44 parts of methyl isobutyl ketone; Viscosity: 0.008 Pa x s (8 centipoise) Content of the diluent: 58.0 % Composition F 100 parts of Composition A 100 parts of toluene 100 parts of methyl isobutyl ketone 100 parts of butylcellosolve Viscosity: 0.002 Pa x s (2 centipoise) Content of the diluent: 83.3 % Examples 1 - 5 On a methacrylic resin plate (Sumipex (trade mark) -000 sold by Sumitomo Chemical Company Ltd.), the composition A was spray coated with an air spray gun having a nozzle of 1.5 mm in diameter from a distance of 20 cm under air pressure of about 3 bar (3 kg/cm²) at a discharging rate of 100 ml/min. and dried at room temperature for 10 minutes to form a flat first layer. Then, the composition B was coated with an air sp ray gun having a nozzle of 1.5 mm in diameter from a distance of 30 cm under conditions shown in Table 1 followed by thermal hardening in an oven kept at 80°C for 2 hours to prepare an anti-reflection plate having a double layered anti-reflection film. Since the anti-reflection plate is required to have little gloss at an angle of 20° (glare shielding) and high transmission of parallel ray (resolution), following tests were carried out on the anti-reflection plate: (1) Gloss Gloss at an angle of 20° of the anti-reflection plate was measured according to JIS Z 8741. (2) Maximum height of the Projections The maximum height of the projections was measured along a standard length of 2.5 mm according to JIS B 0601. (3) Diameter of the Projections By means of a surface roughness meter, Surfcom 30C (Tokyo Seimitsu Kabushikikaisha), surface conditions of the anti-reflection plate were measured and distribution of diameters of the projections was calculated. (4) Transmission of Parallel Ray and Diffused Light Transmission The transmission of parallel ray and diffused light transmission were measured according to JIS K 7105. (5) Pencil Hardness Pencil hardness of the anti-reflection film was measured according to JIS K 5400. The results are shown in Table 2. The anti-reflection plates of Examples 1-5 had gloss at an angle of 20° of less than 100 % and high transmission of parallel ray, which means that they had good anti-reflection property and resolution of transmitted images. Examples 6-7 and Comparative Examples 1-2 In the same manner as in Example 1 but using the composition C (Example 6. Content of the diluent: 71.0 %), the composition F (Example 7. Content of the diluent: 83.3 %), the composition D (Comparative Example 1. Content of the diluent: 60.7 %) or the composition E (Comparative Example 2. Content of the diluent: 58.0 %) in place of the composition B and spraying the second layer composition under following conditions, an anti-reflection plate was prepared: Spraying conditions Air pressure: 3 bar Discharging rate: 25 ml/min. Moving rate of air gun: 30 cm/sec. The properties of the anti-reflection plates are shown in Table 3. The anti-reflection plates of Examples 1, 6 and 7 using the compositions B, C and F, respectively had low diffused light transmission and good resolution of transmitted imaged.

Claims: An anti-reflection plate for a display device comprising a transparent substrate having on one or both surface(s) a flat transparent first layer and, on the first layer, a second transparent layer, wherein the first layer is applied as a composition comprising colloidal silica, an alkoxysilane, a mixture of two or more alkoxysilanes, a partially hydrolized alkoxysilane and/or a partially condensed alkoxysilane and, optionally, a polymer; and dried at room temperature or slightly elevated temperature, and the second layer is spray coated as a composition comprising colloidal silica, an alkoxysilane, a mixture of two or more alkoxysilanes, a partially hydrolized alkoxysilane and/or a partially condensed alkoxysilane and, optionally, a polymer and 70 to 90% by weight of a diluent having a boiling point of 110°C to 200°C under atmospheric pressure; and thermally hardened to form an uneven surface having projections each having a height of 0.1 to 2.0 µm, preferably 0.1 to 1.2 µm, a diameter of 10 to 100 µm and a height/diameter ratio of 1/30 to 1/500. The anti-reflection plate according to claim 1, wherein the diluent is toluene, xylene, methyl isobutyl ketone, cellosolve, methylcellosolve, butyl cellosolve, cellosolve acetate, cyclohexanone, amyl alcohol, n-butanol or a mixture thereof. The anti-reflection plate according to claim 1, wherein the alkoxysilane is a tetraalkoxysilane of the formula: Si-(OR₁)₄ an alkyltrialkoxysilane of the formula: R₂-Si-(OR₁)₃ or a dialkyldialkoxysilane of the formula: wherein R₁, R₂ and R₃ are the same or different and each an alkyl group having 1 to 5 carbon atoms, an acetoxy group, a vinyl group, a (meth)acryloxy group, an allyl group, a phenyl group, a glycidyl group, an alkylthiol group having 1 to 5 carbon atom in the alkyl group or an alkylamino group having 1 to 5 carbon atom in the alkyl group.

Inventors: DOI, TOSHIKI, FUJITA, TAKANORI, YASUNORI, YUKIO
Applicants: SUMITOMO CHEMICAL COMPANY, LIMITED
Application year: 1987
Main classification: G02B1
IPC codes: G09F13, G02B1, G09F9, G02B5