ASYMMETRICAL MEMBRANE OF POLYESTERAMIDE AND PROCESS FOR PREPARING IT

Abstract: An asymmetrical membrane of polyester-amide, useful in dialysis processes and in ultra-filtration processes in general, is formed by a polyester-amide with repetitive units (TATE) n (wherein T is the terephthalic acid radical; A is the hexamethylenediamine radical; and E is the hexanediol radical), shows a thickness of from 15 to 190 µm, a water permeability value of up to about 9 litres/m²/hour, for a ΔP of 300 mm Hg and a good permeability for substances having a molecular weight of up to about 17,000. Such an asymmetrical membrane is obtained by means of a process which comprises the following steps, carried out sequentially: - preparation of a solution of polyesteramide (TATE) n in a solvent constituted by formic acid at a concentration higher than about 99%, or constituted by a solution of lithium chloride in dimethylformamide or dimethylacetamide; - spreading of said solution on a flat support, to a layer of from about 20 to about 200 µm of thickness; - dipping of the coated support in an aqueous coagulation bath; washing with water and recovery of the so-obtained asymmetrical membrane.

Description: The present invention relates to an asymmetrical membrane of polyester-amide and to the process for preparing it. In the art asymmetrical membranes are known, which are used in dialysis and ultrafiltration processes, and are obtained by starting from such synthetic polymers as polyvinyl alcohol and acrylic polymers, or from regenerated cellulose or from cellulose derivatives, such as disclosed, e.g., in French patent No. 2,314,215, and U.S. patent No. 3,962,158. In case of synthetic polymers, difficulties exist in controlling the dimensions and the distribution of the pores of the membranes, and sometimes problems exist of haemocompatibility; such reasons have limited, to date, the commercial applications of these membranes, in particular in the haemodialysis field. On the other hand, the asymmetrical membranes obtained from cellulose derivatives display a good permeability for the substances having a relatively low molecular weight, but not completely satisfactory permeability values for the substances having an average or relatively high molecular weight, and this constitutes a drawback in particular in the application in haemodialysis processes. It has been found now that it is possible to obtain an asymmetrical membrane endowed with good characteristics of permeability for substances having a molecular weight comprised within a wide range of values, by means of a simple and convenient process, which uses a particular polyester-amide as the starting material. Said asymmetrical membrane has furthermore a controlled distribution of the pores, it is mechanically strong, and does not give rise to haemocompatibility problems, thus overcoming, or at least greatly reducing, the problems involved by the asymmetrical membranes of the known art. Accordingly, the present invention relates to an asymmetrical membrane of polyester-amide, useful in the processes of dialysis and in general in the ultrafiltration processes, formed by a polyester-amide with repetitive unit (TATE) n (wherein T is the radical of terephthalic acid; A is the radical of hexamethylenediamine; and E is the radical of hexanediol), said asymmetrical membrane having a thickness of from 15 to 190 µm, a water permeability value of up to 9 litres/m²/hour, for a ΔP of 399,9 hPa (300 mm Hg ) and being endowed with a good permeability for substances having a molecular weight of up to about 17,000. According to another aspect thereof, the present invention relates to the process for preparing said asymmetrical membrane, said process comprising the following steps, carried out sequentially: preparation of a solution of polyester-amide (TATE) n in a solvent constituted by formic acid at a concentration higher than 99%, or constituted by a solution of lithium chloride in dimethylformamide or dimethylacetamide; spreading of the polyester-amide solution on a flat support, to a layer having a thickness of from 20 to 200 µm; dipping of the coated support in an aqueous coagulation bath; washing with water and recovery of the so-obtained asymmetrical membrane. By polyester-amide, according to the present invention, a copolymer is meant which comprises the repetitive unit (TATE) n , wherein: T represents the radical of terephthalic acid; A represents the radical of hexamethethylenediamine; and E represents the radical of hexanediol. As regards the preparation and the general characteristics of such a polyester-amide, reference is made to Italian patents No. 908,843 and No. 908,844. To the purposes of the present invention, also those polyester-amides are useful, which have the above-indicated repetitive unit, and which are endowed with the following characteristics: relative viscosity: from 2 to 2.5 (measured at 25°C, with 1% by weight of polymer in a 1:1 by volume phenoltetrachloroethane solvent mixture); content of free carboxy groups: from 15 to 25 meq/kg; melting point: from 252 to 260°C. To the purposes of the present invention, the polyester-amides are preferred, which have the following characteristics: relative viscosity: about 2.3; content of free carboxy groups: about 22 meq/kg; melting point: about 255°C. According to the process of the present invention, a solution is prepared of the polyester-amide in a solvent selected from: formic acid at a concentration higher than 99%; dimethylformamide containing dissolved lithium chloride; dimethylacetamide containing dissolved lithium chloride. In particular, by means of the solvent consisting of formic acid at a concentration higher than 99%, preparing is possible solutions containing up to 35 parts by weight of polyester-amide, per each 100 part by weight of solvent, by operating at temperatures of up to about 100°C. In case of the other above-mentioned solvents, the amount of dissolved lithium chloride is normally ranging from 2 to 7 parts by weight per each 100 parts by weight of dimethylformamide or of dimethylacetamide. In the typical case of a solvent contaning from 4 to 6 parts by weight of dimethylformamide or of dimethylacetamide, preparing is possible solutions containing up to about 35 parts by weight of polyesteramide per each 100 parts by weight of the same solvent, by operating at a temperature of up to about 100°C. In the preferred form of practical embodiment of the present invention, as the solvent for the polyester-amide a solution is used of from 4 to 6 parts by weight of lithium chloride per each 100 parts by weight of dimethylacetamide, or formic acid at a concentration higher than about 99% is used, and in such solvents the polyester-amide is dissolved in an amount of from 15 to 35 parts by weight per each 100 parts by weight of the same solvent, by operating at a temperature of the order of 100°C. The so-obtained solution is filtered at the same temperature, and is then spread on a flat surface. For the spreading step, any equipment can be used, which allows a layer of polymer solution to be spread on a flat support, e.g., a glass sheet, such as a spreading device equipped with a doctor blade with micrometric adjustment. The temperature of the solution being spread is conveniently maintained at values of from 80 to 100°C, and however at a temperature higher than that which makes polymer precipitate. The spreading operation can be obviously performed on supports of different sizes, as a function of the size of the desired membranes, and it can be furthermore carried out either as a batchwise or as a continuous process. In any case, immediately after the spreading, the coated support is dipped into an aqueous coagulation bath, at room temperature (20-25°C), or at temperatures close to room temperature. The coagulation time, under the above indicated conditions, may range from 1 to 10 minutes, and is preferably of the order of 3-5 minutes. At coagulation end, the membrane is mechanically separated from the support, and is thoroughly washed with running water, e.g., for 24 hours. The washed membrane is then conditioned in a glycerol-water bath (e.g., at 70/30 by volume), containing formaldehyde (e.g., 100 ppm). The so-obtained asymmetrical membrane generally shows a thickness of from 15 to 200 µm and preferably of from 30 to 180 µm. Said membrane is endowed with values of permeability to water which may generally vary within the range of from 3 to 9 litres/m²/hour, for a ΔP of 399,9 hPa (300 mm Hg ) and with good values of permeability for substances having a molecular weight of up to about 17,000, and that as a function of the conditions under which the same membrane was obtained. When examined by the electron microscope, the asymmetrical membrane results constituted, in section, by a thick and compact layer, and by a porous layer, with pores having a uniform size and being evenly distributed. Such an asymmetrical membrane is particularly useful in the dialysis processes, in particular in haemodialysis processes and in Ultrafiltration processes in general. In the following experimental Examples, which are supplied to purely illustrative and not limitative purposes, the membrane is characterized from the viewpoint of its properties of transport of such model substances as: sodium chloride, urea, creatinine, uric acid, vitamin B12, inulin, myoglobin and albumin. To that purpose, a measurement cell is used, such as that shown in Figure 1 of the hereto attached drawing table. More particularly, referring to said figure, the cell consists of two compartments A and B, separated by the membrane M under investigation, positioned between the flanges F. To compartment A, through the inlet pipe E, the solution containing the substance under investigation is fed. The same solution exits compartment A, through the outlet U, in such a way that inside A a circulation is maintained of the solution containing the substance to be tested, by means of a suitable recycle pump. In compartment B, distilled water is contained, in which the concentration of the substance diffused from A is measured. A mechanical stirrer C stirs the liquid contained in B. Both compartments A and B are kept at 25°C by a fluid circulating through the temperature-control jacket T. Example 1 15 parts by weight of polyester-amide (TATE) n having the following characteristics: relative viscosity: 2.3; content of free carboxy groups: 22 meq/kg; melting point: 255°C; is dissolved at 100°C in a solution consisting of 80 parts by weight of dimethylacetamide and 5 parts by weight of lithium chloride. When the polymer is completely dissolved, the solution is cooled to 80°C and is used for preparing a flat asymmetrical membrane. To that purpose, a device is used, which is essentially constituted by a doctor blade with micrometric adjustment, which allows the polymer solution to be spread on glass sheets of about 15 cm x 15 cm of dimensions. Immediately after the spreading, the glass sheet is dipped into a coagulation tank, containing 3 litres of water, at room temperature (25°C). After 3-5 minutes, the glass sheet is removed from the coagulation tank, and the membrane is mechanically separated from the glass sheet and is dipped into a wash tray, wherein it is left, inside running water, for 24 hours. The washed membrane is then conditioned with a water/glycerin solution (70/30 by volume) containing 100 ppm of formaldehyde. On the so-obtained asymmetrical membrane, the characteristics are determined, which are reported in following Table 1: The membrane permeability to water is of 6.8 litres/m²/hour, for a ΔP of 399,9 hPa (300 mm Hg ). The thickness of the membrane is of 180 µm. Example 2 20 Parts by weight of the polyester-amide of Example 1 is dissolved in a solution constituted by 75 parts by weight of dimethylacetamide and 5 parts by weight of lithium chloride. The so-obtained polymer solution is spread on a glass sheet and coagulated as disclosed in Example 1 . On the so-obtained asymmetrical membrane, the characteristics are determined, which are reported in following Table 2. The membrane permeability to water is of 6 litres/m²/hour, for a ΔP of 399,9 hPa (300mm Hg ). The thickness of the membrane is of 170 µm. Example 3 25 Parts by weight of the polyester-amide of Example 1 is dissolved in a solution constituted by 70 parts by weight of dimethylacetamide and 5 parts by weight of lithium chloride. On the so-obtained membrane the characteristics are determined, which are reported in following Table 3. The membrane permeability to water is of 3.0 litres/m²/hour, for a ΔP of 399,9 hPa (300 mm Hg ). The thickness of the membrane is of 190 µm. Example 4 15 Parts by weight of the polyester-amide as disclosed in Example 1 is dissolved in a solution constituted by 85 parts by weight of formic acid at a concentration higher than 89%, by operating at the temperature of about 100°C. The obtained solution is filtered on a 29.5 mm opening (500-mesh) steel net and is spread on glass sheets, in a similar way to Example 1, by Operating with the solution at 98-100°C. On the so-obtained membrane the characteristics are ,: c s a r e determined, which are reported in following Table 4. The membrane permeability to water is of 8.7 litres/m²/hour, for a ΔP of 399,9 hPa (300 mm Hg ). The thickness of the membrane is of 70 µm. Example 5 20 Parts by weight of the polyester-amide of Example 1 is dissolved in 80 parts by weight of formic acid at a concentration higher than 99%. By operating as disclosed in Example 4, a membrane is obtained, the characteristics of which are reported in following Table 5. The membrane permeability to water is of 8.0 litres/m²/hour, for a ΔP of 399,9 hPa (300 mm Hg ). The thickness of the membrane is of 70 µm. Example 6 25 Parts by weight of the polyester-amide as disclosed in Example 1 is dissolved in 75 parts by weight of formic acid at a concentration higher than 99%. By operating as disclosed in Example 4, a membrane is obtained, the characteristics of which are reported in following Table 6. The membrane permeability to water is of 7.0 litres/m²/hour,for a ΔP of 399.9 hPa (300 mm Hg ). The thickness of the membrane is of 70 µm.

Claims: Claims for the following Contracting States : BE, CH, DE, FR, GB, GR, LI, LU, NL, SE Process for preparing an asymmetrical membrane, characterized in that : a solution is prepared of polyester-amide (TATE) n (wherein T is the radical of terephthalic acid; A is the radical of hexamethylenediamine; and E is the radical of hexanediol) in a solvent constituted by formic acid at a concentration higher than 99%, or constituted by a solution of lithium chloride in dimethylformamide or dimethylacetamide; said solution is spread on a flat support, to a layer having a thickness of from 20 to 200 µm; said coated support is dipped into an aqueous coagulation bath; the asymmetrical membrane is washed with water and is recovered. Process according to claim 1, wherein the polyester-amide has a relative viscosity of from 2 to 2.5, and preferably of about 2.3 (as measured at 25°C, with 1% by weight of polymer in a solvent mixture constituted by 1:1 phenol-tetrachloroethane by volume) a content of free carboxy groups of from 15 to 25 and preferably of about 22 meq/kg, and a melting point of from 252 to 260°C and preferably of about 255°C. Process according to claim 1, wherein the solvent is constituted by a solution of 2-7 parts, and preferably of 4-6 parts by weight of lithium chloride in 100 parts by weight of dimethylformamide or of dimethylacetamide and in said solvent the polyester-amide is dissolved in an amount of from 15 to 35 parts by weight per each 100 parts by weight of solvent. Process according to claim 1, wherein the polyester-amide is dissolved in formic acid at a concentration higher than 99%, up to an amount of from 15 to 35 parts by weight of same formic acid. Process according to claim 1, wherein the solution of polyester-amide is spread at a temperature of from 8 to 100°C. Process according to claim 1, wherein the aqueous s coagulation bath is kept at a temperature value equal to room temperature (20-25°C), or nearly equal to room temperature, and the coagulation time varies within the range of from 1 to 10 minutes, and preferably of from 3 to 5 minutes. Asymmetrical membrane, suitable for processes of dialysis and for ultrafiltration processes, characterized in that it is prepared according to a method of claims 1 and 2, and in that it displays a thickness of from 15 to 190 µm, a water permeability value of from 3 up to 9 litres/m²/hour, for a ΔP of 399,9 hPa (300 mm Hg ) and is endowed with good values of permeability for substances having a molecular weight of up to 17,000. Asymmetrical membrane according to claim 7, having a thickness of from 30 to 180 µm. Claims for the following Contracting States : AT, ES Process for preparing an asymmetrical membrane, characterized in that : a solution is prepared of polyester-amide (TATE) (wherein T is the radical of terephthalic acid; A is the radical of hexamethylenediamine; and E is the radical of hexanediol) in a solvent constituted by formic acid at a concentration higher than 99%, or constituted by a solution of lithium chloride in dimethylformamide or dimethylacetamide; said solution is spread on a flat support, to a layer having a thickness of from 20 to 200 µm; said coated support is dipped into an aqueous coagulation bath; the asymmetrical membrane is washed with water and is recovered. Process according to claim 1, wherein the polyester-amide has a relative viscosity of from 2 to 2.5, and preferably of about 2.3 (as measured at 25°C, with 1% by weight of polymer in a solvent mixture constituted by 1:1 phenol-tetrachloroethane by volume) a content of free carboxy groups of from 15 to 25 and preferably of about 22 meq/kg, and a melting point of from 252 to 260°C and preferably of about 255°C. Process according to claim 1, wherein the solvent is constituted by a solution of 2-7 parts, and preferably of 4-6 parts by weight of lithium chloride in 100 parts by weight of dimethylformamide or of dimethylacetamide and in said solvent the polyester-amide is dissolved in an amount of from 15 to 35 parts by weight per each 100 parts by weight of solvent. Process according to claim 1, wherein the polyester-amide is dissolved in formic acid at a concentration higher than 99%, up to an amount of from 15 to 35 parts by weight of same formic acid. Process according to claim 1, wherein the solution of polyester-amide is spread at a temperature of from 8 to 100°C. Process according to claim 1, wherein the aqueous coagulation bath is kept at a temperature value equal to room temperature (20-25°C), or nearly equal to room temperature, and the coagulation time varies within the range of from 1 to 10 minutes, and preferably of from 3 to 5 minutes.

Inventors: BARTOLI, FRANCESCO, FARIAS, OTELLO, PITTALIS, FRANCESCO
Applicants: ENIRICERCHE S.P.A.
Application year: 1987
Main classification: B01D67
IPC codes: B01D71, B29C41, B05D7, C08J5