Particles containing Fe7C3 and process for preparing them

Abstract: Particles containing FeC are prepared by mixing (a) a boron compound or alkaline earth metal compound with (b) iron oxyhydroxide or iron oxide particles, or coating the former compound (a) to the latter particles (b), and then carburizing the mixture or coated particles with a carburizing agent.

Description: The present invention relates to particles containing an iron carbide, particularly Fe₇C₃, and a process for preparing them. As magnetic materials for magnetic recording, there are conventionally used γ-iron oxide, cobalt-containing γ-iron oxide, chromium dioxide, etc. However, attention is recently drawn to particles containing an iron carbide in view of excellence in coercive force, electroconductivity and hardness thereof. The particles containing an iron carbide are known to contain Fe₅C₂ as a main component of iron carbides, and further Fe₃O₄ and free carbon. Although, various kinds of iron carbides are known, those containing Fe₅C₂ or Fe₃C as a main component are only useful as a magnetic recording material. Particles containing other iron carbides as a main component are not known to be useful as a magnetic recording material. EP-A-179490 describes a process for producing particles containing iron carbide which involves contacting acicular iron oxide or oxyhydroxide with a carbonising and reducing agent. The starting iron compound may be coated with a sintering-preventing agent, e.g. a boron compound, in an amount of from 0.01 to 0.5% by weight. JACS Vol. 72, pp. 1042/3 and JACS Vol. 79, pp. 5899-5902 refer to the use of catalysts comprising an iron carbide in hydrocarbon synthesis. An object of the present invention is to provide particles containing an iron carbide mainly composed of Fe₇C₃ which particles are useful as magnetic recording materials. A further object is to provide a process for preparing these particles. In accordance with the present invention, these and other objects are achieved by means of the subject matter claimed in the appendant claims. The present invention provides particles containing Fe₇C₃. These particles are prepared, for example, by mixing (a) a boron compound or alkaline earth metal compound with (b) iron oxyhydroxide or iron oxide particles, or coating the former compound (a) to the latter particles (b), and then carburizing the mixture or coated particles with a carburizing agent. Examples of preferred iron oxyhydroxides are α-FeOOH (goethite), β-FeOOH (akaganite) and γ-FeOOH (lepidocrosite). Examples of preferred iron oxides are α-Fe₂O₃ (hematite), γ-Fe₂O₃ (maghemite) and Fe₃O₄ (magnetite). α-Fe₂O₃ is, for example, any of one prepared by heating α-FeOOH, β-FeOOH or γ-FeOOH at about 200 to about 350°C, followed by dehydration, α-Fe₂O₃ prepared by heating the resulting product further at about 350 to about 900°C to compact the crystals, and others. Further, γ-Fe₂O₃ is, for example, any of one prepared by reducing iron oxyhydroxide or α-Fe₂O₃ in a hydrogen atmosphere at 300 to 400°C and reoxidizing the resulting Fe₃O₄ in air at 150 to 250°C. β-FeOOH is preferably treated with an aqueous solution of alkaline compound. In the present invention, examples of boron compounds are boric acid aid borates such as sodium borate, ammonium borate, etc. Alkaline earth metal compounds include Ca(OH)₂, CaCO₃ and like calcium salts, Ba(OH)₂, BaCO₃ and like barium salts, etc. The proportion of the boron compound or alkaline earth metal compound to iron oxyhydroxide or iron oxide is preferably 0.1 to 20 atom% and more preferably 0.1 to 5 atom% of boron or alkaline earth metal based on iron. The boron compound or alkaline earth metal compound is mixed or coated by a conventional mixing or coating method. For example, these compounds are mixed using a ball mill, mixer, etc. Alternately, a slurry of the starting iron compound and boron compound or alkaline earth metal compound is, for example, dried with or without filtration. When the boron compound or alkaline earth metal compound is dissolved in water, an aqueous solution of alkaline compound is added dropwise to the slurry, if required, stirred for 30 minutes to one hour, and the resulting precipitate is filtered off and dried. In the present invention, as the carburizing agents are used the following reducing-and-carburizing agents containing carbon atoms. 1 ○ CO 2 ○ aliphatic, linear or cyclic, saturated or unsaturated hydrocarbons such as methane, propane, butane, cyclohexane, methylcyclohexane, acetylene, ethylene, propylene, butadiene, isoprene, town gas, etc. 3 ○ aromatic hydrocarbons such as benzene, toluene, xylene, alkylated or alkenylated derivatives thereof having a boiling point up to 150°C. 4 ○ aliphatic alcohols such as methanol, ethanol, propanol, cyclohexanol, etc. 5 ○ esters such as methyl formate, ethyl acetate and like esters having a boiling point up to 150°C 6 ○ ethers such as lower alkyl ether, vinyl ether and like ether having a boiling point up to 150°C 7 ○ aldehydes such as formaldehyde, acetaldehyde and like aldehydes having a boiling point up to 150°C 8 ○ ketones such as acetone, methyl ethyl ketone, methyl isobutyl ketone and like ketone having a boiling point up to 150°C Particularly preferable reducing-and-carburizing agents containing a carbon atom are CO, CH₃OH, HCOOCH₃, saturated or unsaturated aliphatic hydrocarbons having 1 to 5 carbon atoms. In the carburization of the present invention, the mixture or coated particles are contacted with a carburizing agent. The carburizing agent can be used together with a carbon-free reducing gas such as hydrogen gas. The carbon-free reducing gas no is preferably used in an amount of up to 5 times the volume of the carburizing agent in the vapor phase. In the present invention, the carburizing agent can be used as it is or in diluted form. Examples of diluents are N₂, argon, helium, etc. The dilution ratio is suitably selected but is preferably up to about 10 times (by volume). The contacting temperature, contacting time, gas flow rate and other conditions depend, for example, on the preparation history, average axial ratio, average particle size and specific surface area of the iron oxyhydroxide or iron oxide. The preferred contacting temperature is about 250 to about 400°C, preferably about 300 to about 400°C. The preferred contacting time is about 0.5 to about 12 hours. The preferred gas flow rate (excluding diluent) is about 1 to about 1000 ml S.T.P./min per gram of the starting iron compound. The contacting pressure inclusive of that of the diluent is usually 1 to 2 atm. although not particularly limited. Before carburizing in the process of the invention, the mixture or coated particles may be contacted with a carbon-free reducing gas such as hydrogen gas. In the above, the carbon-free reducing gas can be used alone or diluted. Examples of diluents are N₂, CO₂, argon, helium, etc. The dilution ratio is suitably selected and is preferably up to about 10 times (by volume). The contacting temperature, contacting time, gas flow rate and other conditions depend, for example, on the preparation history, average axial ratio, average particle size and specific surface area of the iron compound. The preferred contacting temperature is about 200 to about 700°C, preferably about 300 to about 400°C. The preferred contacting time is about 0.5 to about 6 hours. The preferred gas flow rate (excluding diluent) is about 1 to about 1000 ml S.T.P./min per gram of the starting iron compound. The contacting pressure inclusive of that of the diluent is usually 1 to 2 atm. although not particularly limited. The particles obtained by the present process are in the form of generally uniform particles when observed under an electron microscope. The particles are present as primary particles and have the same particulate form as the starting particles of iron oxyhydroxide or iron oxide. The particles obtained by the process are found to contain carbon by elementary analysis and to contain an iron carbide by its X -ray diffraction pattern, which exhibits plane spacings at 0,201nm (2.01Å), 0,211nm (2.11Å) and 0,225nm (2.25Å). Such a pattern corresponds to Fe₇C₃. The iron carbide component of the present material chiefly comprises Fe₇C₃. In the case of incomplete carburization, the particles obtained by the present process further contain an iron oxide component which is chiefly Fe₃O₄. With respect to iron oxides, FeO, Fe₃O₄ and γ-Fe₂O₃ are generally related to one another in structure. The oxygen atoms in these three oxides are packed in a three-dimensional structure to the highest possible density, and the number of oxygen atoms in Fe₃O₄ actually present varies in an overall range covering the numbers of oxygen atoms in these oxides, so that it is suitable to represent the iron oxide in the particles by FeOy (1<y≦1.5). While the particles prepared by the present process contain iron oxide in addition to the iron carbide component in most cases, the elementary analysis values of C, H and N indicate that the amount of carbon is usually excess of that calculated from the chemical formula of the iron carbide identified by the X-ray diffraction pattern. It is not clear whether the excess of carbon is present as combined with iron or as free carbon. In this sense, it is probable that the particles obtained by the present process contain elemental carbon. The particles obtained by the present process are then composed substantially of iron carbide alone or iron carbide and iron oxide and/or elemental carbon. The particles prepared by the present process generally have an average particle size (long axis) of 0.05 to 5µm, and an average axial ratio (long axis/short axis) of not less than 1. In case the present particles are used as a magnetic material for magnetic recording, the particles have an average axial ratio usually of at least 3, preferably 3 to 20, and an average particle size (long axis) usually of up to 2µm, preferably 0.1 to 2µm, most preferably 0.1 to 1.0µm. The particles of the present invention containing iron carbide are useful as a magnetic material for magnetic recording as is apparent from the foregoing characteristics, etc., while the use thereof is not limited thereto. For example, the particles are usable as a catalyst for preparing lower aliphatic hydrocarbons from CO and H₂. The present invention provides a process for preparing particles containing Fe₇C₃ with use of the starting iron compound which is easily available. The invention will be described below in detail with reference to examples. In the following examples, characteristics, etc. are determined by the methods described below. (1) Magnetic characteristics. Determined by the following method unless otherwise specified. Coercive force (Hc, Oe), saturation magnetization (σs, e.m.u.) and remanent magnetization (σr, e.m.u.) are measured in a magnetic field of 10 kOe, using a vibrating sample magnetometer. Fig. 1 shows the X-ray diffraction pattern of the powder obtained in Example 1. Example 1 Ten grains of goethite particles, 0.7µm in average size (long axis), 10 in average axial ratio and having surface pH of 9, and 0.07g of boric acid (B/Fe=1 atom%) were mixed in a ball mill for 3 hours. After the resulting powder was heated in air at 350°C for one hour, the powder was treated at 340°C for 3 hours while passing CO at a flow rate of 200ml/min. Fig. 1 shows the X -ray diffraction pattern of the product and Table 1 gives comparison between each peak of the product and that of ASTM X-Ray Powder Data File 6-0686 of Fe₇C₃. Example 1 Fe₇C₃ (ASTM) 2ϑ (deg) dnm·10 I/I₁ dnm·10 I/I₁ 40.032 2.250 35 2.255 35 42.736 2.114 50 2.119 45 43.636 2.072 34 44.967 2.014 100 2.016 100 50.633 1.801 21 1.805 30 53.230 1.719 14 1.719 15 From Table 1, it is shown that the product comprises Fe₇C₃ as a main component. Further, a peak at 0.2072nm (2.072Å) is deemed to be that of Fe₅C₂. Magnetic characteristics of the obtained powder are as follows. Coercive force 740 Oe Saturation magnetization 96.9 emu/g Remanent magnetization 42.3 emu/g Example 2 To a slurry containing 10g of goethite particles, 0.7µm in average size (long axis), 10 in average axial ratio and having surface pH of 9, and 0.125g of calcium chloride (Ca/Fe=1 atom%) and adjusted the pH to 3 with addition of hydrochloric acid was added dropwise an aqueous solution of sodium hydroxide to adjust the pH to 13. The slurry was filtered, washed, dried and the resulting lumps were pulverized. After the resulting powder was heated in air at 350°C for one hour, the powder was contacted at 340°C for 3 hours by passing CO at a flow rate of 200ml/min. The X-ray diffraction pattern showed the product comprises Fe₇C₃ as a main component. Magnetic characteristics of the obtained powder are as follows. Coercive force 900 Oe Saturation magnetization 103.5 emu/g Remanent magnetization 51.6 emu/g

Claims: Particles containing Fe₇C₃ and having an average particle size (long axis) of 0.05 to 5 µm and an average axial ratio (long axis/short axis) of not less than 1. Particles containing Fe₇C₃ and having an average particle size of 0.1 to 2 µm and an average axial ratio of 3 to 20. A process for preparing the particles according to claim 1 or 2 which comprises mixing (a) a boron compound or alkaline earth compound with (b) iron oxyhydroxide or iron oxide particles having the same average particle size and average axial ratio as the desired particles, or coating the former compound (a) on the latter particles (b), the proportion of (a) to (b) being 0.1 to 20 atom % boron or alkaline earth metal based on iron, and carburizing the mixture or coated particles with a carburizing agent. The process of claim 3 wherein the boron compound is boric acid, sodium borate or ammonium borate. The process of claim 3 wherein the alkaline earth metal compound is Ca(OH)₂, CaCO₃, Ba(OH)₂ or BaCO₃. The process of any one of claims 3 to 5 wherein the carburizing agent is CO, methanol, methyl formate or a saturated or unsaturated aliphatic hydrocarbon of 1 to 5 carbon atoms.

Inventors: ARASE TAKUYA, DAIMON SHIGEO, TOKUNAGA KATSUSHI, ARASE, TAKUYA, DAIMON, SHIGEO, TOKUNAGA, KATSUSHI
Applicants: DAIKIN IND LTD, DAIKIN INDUSTRIES, LIMITED
Application year: 1987
Main classification: C01B31
IPC codes: B01J23, G11B5, H01F1, C01B31