LIGHT-SENSITIVE SILVER HALIDE PHOTOGRAPHIC MATERIAL

Abstract: A light-sensitive silver halide photographic material, which is suitably adapted for rapid process and comprises a support and, provided thereon, at least one silver halide emulsion layer, wherein at least one silver halide emulsion layer of said silver halide emulsion layer contains silver halide grains containing not less than 80 mol % of silver chloride, a magenta dye-forming coupler represented by formula [M-I] and a compound represented by formula [AO]; wherein Z represents a group of non-metal atoms necessary for the formation of a nitrogen-containing heterocyclic ring, said ring formed including Z may have a substituent; X represents a hydrogen atom or a group capable of being split off upon reaction with the oxidized product of a color developing agent; and R represents a hydrogen atom or a substituent; wherein A is a group of non-metal atoms necessary to complete a 5-member to 8-member nitrogen-containing ring and R⁰ represents an aryl group or a heterocyclic group.

Description: FIELD OF THE INVENTION The present invention relates to a light-sensitive silver halide photographic material feasible for the rapid processing and improved in the color reproducibility and light-fastness of dye images. BACKGROUND OF THE INVENTION Recent years, desired in the prent industrial field are light-sensitive silver halide photgraphic materials (hereinafter referred to often as "light-­ sensitive material(s)") having a high image quality and capable of being rapidly processed. As for the image quality of the dye images obtained from a light-sensitive material, what is required is that there can be achieved a good color reproducibility and good light-fastness. Both the feasibility for rapid processing and the color reproducibility can be satisfied by the combination of a silver halide emulsion of the composition rich in silver chloride and a magenta coupler of the pyrazoloazole type, but the light-fastness may become poor. Techniques for improving the light-fastness of a magenta dye image by use of a piperazine type antioxidant or hindered amine type antioxidant are disclosed in Japanese Patent Publication Open to Public Inspections (hereinafter referred to as "Japanese Unexamined Patent Publication(s)") No. 72246/1986, No. 73152/1986, No. 189539/1986, No. 180367/1987, etc. However, these methods, although can attain a great effect of improving the light-fastness, are accompanied with disadvantages such that the rapid processing feasibility becomes lower and there occurs an increase in the white area yellowing caused by light. Also, a phenol type antioxidant may not impair the rapid processing feasibility (as disclosed in Japanese Patent O.P.I. Publications No. 125732/1984, No. 262159/1985, No. 184543/1986, No. 186960/1986, No. 194444/1986, No. 241753/1986, etc.), but can have only a small effect of improving the light-fastness. Accordingly, it is demanded to bring forth a color light-sensitive material that can be excellent in the color reproducibility, light-fastness and rapid processing feasibility, and also may suffer less yellowing of the white area. SUMMARY OF THE INVENTION An object of the present invention is to provide a color light-sensitive material improved in the color reproducibility, light-fastness of dye images and color-­ forming performance, feasible for the rapid processing, and also suffering less yellowing of the white area. The above object of the present invention can be achieved by a light-sensitive material comprising a support and at least one silver halide emulsion layer provided thereon, wherein at least one layer of said silver halide emulsion layer contains silver halide grains containing 80 mol % or more of silver chloride, a magenta coupler represented by Formula (M-I) shown below, and a compound represented by Formula (A-0) shown below. wherein Z represents a group of non-metallic atoms necessary for the formation of a nitrogen containing heterocyclic ring, which ring formed by Z may have a substituent; X represents a hydrogen atom or a group capable of being split off through the reaction with an oxidized product of a color developing agent; and R represents a hydrogen atom or a substituent. wherein A is a group of non-metal atoms necessary to complete a 5-member to 8-member nitrogen-containing ring, and R⁰ represents an aryl group or a heterocyclic group DETAILED DESCRIPTION OF THE INVENTION The present invention will be described below in detail. In the magenta coupler represented by the above Formula (M-1) according to the present invention, Z represents a group of non-metal atoms necessary for the formation of a nitrogen-containing heterocyclic ring, and the ring formed by Z may have a substituent. X represents a hydrogen atom or a group capable of being split off through the reaction with an oxidized product of a color developing agent. And, R represents a hydrogen atom or a substituent. There is no particular limitation in the substituent represented by R, but it may typically include the groups such as alkyl, aryl, anilino, acylamino, sulfonamide, alkylthio, arylthio, alkenyl and cycloalkyl. Besides these it may also include a halogen atom, the groups such as cycloalkenyl, alkynyl, a heterocyclic ring, sulfonyl, sulfinyl, phosphonyl, acyl, carbamoyl, sulfamoyl, cyano, alkoxy, aryloxy, heterocyclic oxy, siloxy, acyloxy, carbamoyloxy, amino, alkylamino, imide, ureido, sulfamoylamino, alkoxycarbonylamino, aryloxycarbonylamino, alkoxycarbonyl, aryloxycarbonyl and heterocyclic thio, and a spiro compound residual group, a bridged hydrocarbon compound residual group, etc. The alkyl group represented by R may preferably be an alkyl group having 1 to 32 carbon atoms, which may be of stright-chain or branched-chain types. The aryl group represented by R may preferably be a phenyl group. The acylamino group represented by R may include an alkylcarbonylamino group, an arylcarbonylamino group, etc. The sulfonamide group represented by R may include an alkylsulonylamino group, an arylsulfonylamino group, etc. The alkyl component or aryl component in the alkylthio group or arylthio group represented by R may include the above alkyl group or aryl group represented by R, respectively. The alkenyl group represented by R may preferably be an alkenyl group having 2 to 32 carbon atoms; and the cycloalkyl group, a cycloalkyl group having 3 to 12, particularly 5 to 7, carbon atoms. The alkenyl group may be of straight-chain or branched-chain types. The cycloalkenyl group represented by R may preferably be a cycloalkenyl group having 2 to 12, particularly 5 to 7, carbon atoms. The sulfonyl group represented by R may include an alkylsulfonyl group, an arylsulfonyl group, etc.; the sulfinyl group, an alkylsulfinyl group, an arylsulfinyl group, etc.; the phosphonyl group, an alkylphosphonyl group, an alkoxyphosphonyl group, an aryloxyphosphonyl group, an arylphosphonyl group, etc.; the acyl group, an alkylcarbonyl group, an arylcarbonyl group, etc.; the carbamoyl group, an alkylcarbamoyl group, an arylcarbamoyl group, etc.; the sulfamoyl group, an alkylsulfamoyl group, an arylsulfamoyl group, etc.; the acyloxy group, an alkylcarbonyloxy group, an arylcarbonyloxy group, etc.; the carbamoyloxy group, an alkylcarbamoyloxy group, an arylcarbamoyloxy group, etc.; the ureido group, an alkylureido group, an arylureido group, etc.; the sulfamoylamino group, an alkylsulfamoylamino group, an arylsulfamoylamino group, etc.; the heterocyclic group may preferably be a heterocyclic group of 5 to 7 members, specifically a 2-­ furyl group, a 2-thienyl group, a 2-pyrimidinyl group, a 2-­ benzothiazolyl group, etc.; the heterocyclic oxy group may preferably be a heterocyclic oxy group having a heterocyclic ring of 5 to 7 members, for example, a 3,4,5,6-tetrahydropyranyl-2-oxy group, a 1-phenyltetrazole-5-oxy group, etc.; the heterocyclic thio group may preferably be a heterocyclic thio group of 5 to 7 members, for example, a 2-pyridylthio group, a 2- benzothiazolylthio group, a 2,4-­ diphenoxy-1,3,5-triazole-6-thio group, etc.; the siloxy group, a trimethylsiloxy group, a triethylsiloxy group, a dimethylbutylsiloxy group, etc.; the imide group, a succinimide group, a 3-­ heptadecylsuccinimide group, a phthalimide group, a glutalimide group, etc.; the spiro compound residual group, spiro[3.3]heptan-­ 1-yl, etc.; and the bridged hydrocarbon compound residual group, bicyclo[2.2.1]heptan-1-yl, tricyclo[3.3.1.1 3,7 ]decan-1-yl, 7,7-dimethyl-bicyclo[2.2.1]heptan-1-yl, etc. The group capable of being split off through the reaction with an oxidized product of a color developing agent may include, for example, a halogen atom (such as a chlorine atom, a bromine atom and a fluorine atom) and the groups such as alkoxy, aryloxy, heterocyclic oxy, acyloxy, sulfonyloxy, alkoxycarbonyloxyl, aryloxycarbonyl, alkyloxazyloxy, alkoxyoxazylozy, alkyl thio, arylthio, heterocyclic thio, alkyloxythiocarbonylthio, acylamino, sulfonamide, a nitrogen-containing heterocyclic ring linked with an N atom, alkyloxycarbonylamino, aryloxycarbonylamino, carboxyl and (R₁′ has the same definition as in the above R; Z′ has the same definition as the above Z; and R₂ and R₃ each represents a hydrogen atom, an aryl group, an alkyl group or a heterocyclic group), but preferably includes a halogen atom, particularly a chlorine atom. The nitrogen-containing heterocyclic ring formed by Z or Z′ may include a pyrazole ring, an imidazole ring, a triazole ring or tetrazole ring, etc., and the substituent the above ring may have may include those described for the above R. The magenta coupler represented by Formula (M-I) is more specifically represented by, for example, Formulas (M-­ II) to (M-VII) shown below, respectively. In the above Formulas (M-II) to (M-VII), R₁ to R₈ and X have the same definition as the above R and X, respectively. Most preferred among Formula (M-I) is a compound represented by Formula (M-VIII) shown below. In the formula, R₁, X and Z₁ have the same definition as R, X and Z in Formula (M-I), respectively. Of the magenta couplers represented by Formulas (M-­ II) to (M-VII), particularly preferred is the magenta coupler represented by Formula (M-II). Most preferred as the substituents R and R₁ on the above heterocyclic ring is a substituent represented by Formula (M-IX) shown below. In the formula, R₉, R₁₀ and R₁₁ each have the same definition as the above R. Any two of the above R₉, R₁₀ and R₁₁, for example, R₉ and R₁₀ may be combined to form a saturated or unsaturated ring (for example cycloalkane, cycloalkene or a heterocyclic ring), or R₁₁ may further be combined to said ring to constitute a bridged hydrocarbon compound residual group. Particularly preferred among Formula (M-IX) is (i) an instance in which at least two of R₉ to R₁₁ are each an alkyl group, and (ii) an instance in which any one of R₉ to R₁₁, for example, R₁₁ is a hydrogen atom and the other two of R₉ and R₁₀ are combined to form a cycloalkyl together with a route carbon atom. Further preferred among (i) is an instance in which any two of R₉ to R₁₁ are each an alkyl group and the other one is a hydrogen atom or an alkyl group. The substituent the ring formed by Z in Formula (M-­ 1) or the ring formed by Z₁ in Formula (M-VIII) may have and R₂ to R₈ in Formulas (M-II) to (M-VI) may preferably be a compound represented by Formula (X) shown below. Formula (M-X): -R₁₂-SO₂-R₁₃- In the formula, R₁₂ represents an alkylene group, and R₁₃ represents a cycloalkyl group or an aryl group. The alkylene group represented by R₁₂ may preferably have a carbon atom number of 2 or more, more preferably 3 to 6, at the part of the straight-chain, and may be of either straight-chain or branched-chain types. The cycloalkyl group represented by R₁₃ may preferably be a cycloalkyl group of 5 or 6 members. Typical examples of the above compounds according to the present invention are shown below. In addition to the above typical examples of the compound according to the present invention, examples of the compound according to the present invention may also include the compounds shown as Nos. 1 to 4, 6, 8 to 17, 19 to 24, 26 to 43, 45 to 59, 61 to 104, 106 to 121, 123 to 162 and 164 to 223 among the compounds described in Japanese Patent O.P.I. Publication No. 16339/1987. The above couplers can be also synthesized by making reference to Journal of the Chemical Society, Perkin I (1977), 2047-2052, U.S. Patent No. 3,725,067, Japanese Patent O.P.I. Publications No. 99437/1984, No. 42045/1983, No. 162548/1984, No. 171956/1984, No. 33552/1985, No. 43659/1985, No. 172982/1985, No. 190779/1985, etc. The couplers of the present invention can be used usually in the range of 1 x 10⁻³ mol to 1 mol, preferably 1 x 10⁻² mol to 8 x 10 ⁻¹ mol, per mol of silver halide. The couplers of the present invention can be used in combination with magenta couplers of different kinds. The anti-color-fading agent represented by the above Formula (A0) and is used in combination with the magenta coupler of the present invention will be described below. When the compound represented by the above Formula (A0) (hereinafter referred to also "magenta dye image stabilizing agent of the present invention") contained in the light-sensitive silver halide photographic material of the present invention is used in combination with the magenta coupler of the present invention, there can be obtained not only the effect of preventing the magenta dye image from being color-faded owing to light but also the effect of preventing the white area from being yellowed owing to light. In the present invention, the compound represented by Formula (A0) is more specifically represented by Formula (A) or Formula (B) shown below. wherein R¹ represents an aryl group or a heterocyclic group; and Z¹ and Z² each represent an alkylene group having 1 to 3 carbon atom, provided that the total sum of the carbon atom number of the alkylene group represented by Z¹ and Z² each is 3 to 6; and n represents 1 or 2. wherein R¹ represents an alkyl group, a cycloalkyl group, an alkenyl group, an aryl group, a heterocyclic group, an acyl group, a bridged hydrocarbon group, an alkyl sulfonyl group or an aryl sulfonyl group; R² represents a group capable of being substituted on the benzene ring; m represents an integer of 0 to 4, provided that a plurality of R² may be the same or different when m is 2 or more or may form a ring with each other, or R² may form a ring together with -OR¹ (wherein R¹ is as defined above); and A represents a group of non-­ metal atoms necessary for the formation of a 5- to 8- membered ring together with a nitrogen atom. In the above Formula (A), the aryl group represented by R¹ may include, for example, a phenyl group, a 1-­ naphthyl group, etc., and these aryl groups may have a substituent. The substituent may include the substituents such as those set out as the substituents of R in Formula (M-I). The heterocyclic group represented by R¹ may include, for example, a 2-furyl group, a 2-thienyl group, etc., and these heterocyclic groups include those having the substituents such as those set out for R in Formula (M-­ I). Z¹ and Z² each represent an alkylene group having 1 to 3 carbon atoms, provided that the total sum of the carbon atom number of the alkylene group represented by Z¹ and Z² each is 3 to 6. These alkylene groups may have the substituent such as those set out for R in Formula (M-I). The symbol n represents 1 or 2. Particularly preferred in the present invention is the compound wherein, in the above Formula (A), R¹ is a phenyl group, Z¹ and Z² each are an ethylene group, and n is 2. Examples of the magenta dye image stabilizing agent of the present invention are shown below. In addition to the above, there can be included the following compounds. Typical examples for the synthesis of the magenta dye image stabilizing agent of the present invention will be described below. Synthesis Example 1 [Synthesis of compound (A-3)] In 200 ml of ethanol, 27 g of p-dodecyloxyaniline and 15 g of divinyl sulfone were dissolved, and the solution was boiled under reflux for 3 hours, followed by ice-cooling to collect by filtration the crystals precipitated, which were recrystallized from ethanol to obtain 18 g of white scaly crystals. The structure thereof was confirmed by mass spectrum and nucelar magnetic rezonance spectrum. Synthesis Example 2 [Synthesis of compound (A-17)] In 150 ml of dioxane, 20 g of p-benzyloxyaniline and 13 g of divinyl sulfoxide were dissolved, and the solution was boiled under reflux for 5 hours, and thereafter allowed to stand for 24 hours to collect by filtration the crystals precipitated, which were recrystallized from ethanol to obtain 15 g of white powdery crystals. The structure thereof was confirmed by mass spectrum and nuclear magnetic rezonance spectrum. The above magenta dye image stabilizing agent represented by Formula (A) of the present invention may be used preferably in an amount of 5 to 400 mol %, more preferably 10 to 300 mol %, based on the magenta coupler of the present invention. The magenta dye image stabilizing agent represented by the above Formula (B) and is used in another embodiment of the present invention in combination with the magenta coupler of the present invention will be described below. In Formula (B), the alkyl group represented by R¹ may include, for example, an straight-chain or branched-­ chain alkyl group having 1 to 24 carbon atoms; the cycloalkyl group, for example, a cycloalkyl group having 5 to 24 carbon atoms; the alkenyl group, for example, an alkenyl group having 3 to 24 carbon atoms; the aryl group, for example, a phenyl group and a naphthyl group; the heterocyclic group, for example, a pyridyl group, an imidazolyl group and a thiazolyl group; the acyl group, for example, an acetyl group and a benzoyl group; the bridged hydrocarbon group, for example, a bicyclo[2.2.1]heptyl group, and so forth, respectively. These groups represented by by R¹ include those further having a substituent. Preferred as R¹ is an alkyl group. The group represented by R² and capable of being substituted on the benzene ring may typically include a halogen atom and the groups such as alkyl, aryl, alkoxy, aryloxy, alkylthio, arylthio, acyl, alkoxycarbonyl, carbamoyl (for example, alkylcarbamoyl, arylcarbamoyl, etc.), ureido (for example, alkylureido, arylureido, etc.), sulfamoyl (for example, alkylsulfamoyl, arylsulfamoyl, etc.), amino (including substituted amino), alkylsulfonyl, arylsulfonyl, nitro, cyano and carboxy. Of these, preferred as R² are a halogen atom, an alkyl group and an alkylthio group. The groups represented by R² may further have a substituent. The symbol m represents an integer of 0 to 4, but may preferably represent 0 to 2. The 5- to 8-membered ring formed by A may include the rings such as pyrrolidine, piperidine, piperadine, morpholine and pyridine. These rings include those having a substituent. The group -OR¹ can be located at any position with regard to but preferably at the p-position. Typical examples of the magenta dye image stabilizing agent of the present invention, represented by Formula (B) will be shown below, but by no means limited to these. In addition to the above typical compounds of the compound according to the present invention, the compound used in the present invention may also include the compounds described in Japanese Patent Application No. 241743/1986 (unpublished). The magenta dye image stabilizing agent represented by Formula (B) of the present invention may be used preferably in an amount of 5 to 300 mol %, more preferably 10 to 200 mol %, based on the magenta coupler of the present invention. The magenta coupler of the present invention and the magenta dye image stabilizing agent of the present invention may preferably be used in the same layer, but this stabilizing agent may also be used in a layer adjacent to the layer in which said coupler is present. For the purpose of further improving the light-­ fastness of the magenta coupler in the light-sensitive silver halide photographic material of the present invention, a phenol type antioxidant represented by Formula (II) shown below may preferably be used in the silver halide emulsion layer containing the magenta coupler. In the formula, R³ represents a hydrogen atom, an alkyl group, an alkenyl group, an aryl group or a heterocyclic group; R⁴, R⁵, R⁷ and R⁸ each represent a hydrogen atom, a halogen atom, a hydroxyl group, an alkyl group, an alkenyl group, an aryl group, an alkoxy group or an acylamino group; and R⁶ represents an alkyl group, a hydroxy group, an aryl group or an alkoxy group. R³ and R⁴ may be ring-closed each other to form a 5- or 6-­ membered ring, and R⁶ in such an instance represents a hydroxyl group or an alkoxy group. Also, R³ and R⁴ may be ring-closed to form a methylenedioxy ring. Still also, R⁵ and R⁶ may be ring-closed to form a 5-membered hydrocarbon ring, and R³ in such an instance represents an alkyl group, an aryl group or a heterocyclic ring, except, however, the instance in which R³ is a hydrogen atom and R⁶ is a hydroxyl group. Examples of the compound of Formula (II) preferably used in the present invention are shown below. This phenol type compound or phenyl ethyer type compound represented by Formula (II) may be used preferably in the range of 1 x 10⁻² mol to 5 mols, more preferably 1 x 10⁻¹ mol to 2 mols, per mol of the magenta coupler of the present invention. In the present invention, a compound represented by Formula (S) shown below may preferably be used for the purpose of maintaining the effect of the present invention, i.e., the effect of improving the rapid processing feasibility, color reproducibility and light-­ fastness and also for the purpose of suppressing the minimum density of a dye image to a lower level. Formula (S): In the formula, Q represents a group of atoms necessary for the formation of a 5- or 6-membered heterocyclic ring that may be condensed with a benzene ring; and M represents a hydrogen atom, an alkali metal atom or an ammonium group. The heterocyclic ring formed by Q and that may be condensed with a benzene ring may include the rings such as imidazole, tetrazole, thiazole, oxazole, selenazole, benzimidazole, naphthimidazole, benzothiazole, naphtothiazole, benzoselenazole, naphthoselenazole, benzoxazole, pyridine, pyrimidine and quinoline, and these heterocyclic rings include those having a substituent. Typical examples of the compound represented by Formula (S) are shown below. As for the time at which the compound (S) is to be added, the compound may preferably be added in the course of the chemical ripening, at the time of the completion of the chemical ripening, or in the time of after the completion of the chemical ripening and before the coating. The compound may be added in one time in its whole amount, or may be added in plural portions. The compound (S) may be used usually in the range of 1 x 10⁻⁶ to 1 x 10⁻¹ mol, preferably 1 x 10⁻⁵ to 1 x 10⁻² mol, per mol of silver halide. A fast-reactive yellow coupler preferably used in the present invention is a yellow coupler having a relative coupling reaction rate of 0.5 or more. The coupling reaction rate of a coupler can be determined as a relative value by measuring the amount of respective dyes in a color image which is obtained by mixing two types of couplers M and N capable of giving mutually distinctively separable different dyes, adding them in a silver halide emulsion, and then carrying out color development. This method is described in Japanese Patent O.P.I. Publications No. 178954/1987 and No. 178252/1987, Japanese Patent Applications No. 97513/1986, No. 97154/1986 and No. 135150/1986 (unpublished), etc. In the present invention, it refers to the coupling activity ratio (RM/RN) established when the coupler shown below is used as the above coupler N. Typical examples of the fast-reactive yellow coupler are shown below. The yellow coupler may preferably be added in an amount of from 2 x 10⁻³ to 5 x 10⁻¹ mole, more preferably from 1 x 10⁻² to 5 x 10⁻¹ mol, per mol of silver. The above-described magenta coupler of the present invention may be added in an intended hydrophilic colloid layer after it is dissolved in a high-boiling organic solvent boiling at about 150°C or more, optionally with use of a low-boiling and/or water-soluble organic solvent in combination, and dispersed by emulsification in a hydrophilic binder such as an aqueous gelatin solution with use of a surface active agent. For the above high-boiling organic solvent, there may preferably be used a compound having a dielectric constant of 7.0 or less, preferably 2.0 or more at the minimum, at 30°C. The compound having a dielectric constant of 7.0 or less may include esters such as phthalate and phosphate, organic amides, ketones, hydrocarbon compounds, etc. The high-boiling solvent preferably used may include dibutyl phthalate, dihexyl phthalate, di-2-ethyl-hexyl phthalate, dioctyl phthalate, dinonyl phthalate, didodecyl phthalate, di-i-octadecyl phthalate, tricrezyl phthalate, trioctyl phthalate, tri-i-nonyl phthalate, tri-i-dodecyl phthalate, etc. There is no particular limitation in a cyan coupler to be used together with the magenta coupler of the present invention and the fast-reactive yellow coupler, but there can be preferably used the 2,5-diacylaminophenol type cyan couplers described in Japanese Patent O.P.I. Publications No. 112038/1975, No. 109636/1978, No. 163537/1980, No. 31935/1980, No. 100440/1984, No. 121332/1984, No. 124341/1984, No. 139352/1984, No. 146050/1984 and No. 166956/1984, U.S. Patent No. 2,895,826, etc., and 2-acylaminophenol type cyan couplers described in Japanese patent O.P.I. Publications No. 117249/1985, No. 205447/1985, No. 3142/1986, No. 9652/1986, No. 9653/1986, No. 27540/1986, No. 39045/1986, No. 50136/1986 and No. 105545/1986, U.S. Patent No. 3,772,002, etc. These cyan couplers may be used either alone or in combination, and can be used usually in the range of 1 x 10⁻³ to 1 mole, preferably 1 x 10⁻² to 8 x 10⁻¹ mole, per mol of silver. The silver halide emulsion layer containing the magenta coupler of the present invention contains silver halide grains containing 80 mol % or more of silver chloride. The silver halide grains of the present invention contain 80 mol % or more of silver chloride, and may preferably have a silver chloride content of 90 mol % or more. The content of silver bromide may preferably to 10 mol % or less; and the content of silver iodide, 0.5 mol % or less. More preferably, the content of silver chloride may be 95 mol % or more. The silver halide grains of the present invention may be used alone or may be used by mixing them with other silver halide grains of different compositions. The may be also used by mixing them with silver halide grains having a silver chloride content of 10 mol % or less. In the silver halide emulsion layer containing the silver halide grains of the present invention, having a silver chloride content of 80 mol % or more, the proportion of the silver halide grains having a silver halide content of 80 mol % or more may account for 60 % by weight or more, preferably 80 % by weight or more, of the total silver halide grains contained in said emulsion layer. The silver halide grains of the present invention may have the composition that is uniform from the inside to outside of a grain, or that is different between the inside and outside of a grain. In the instance in which the composition is different between the inside and outside of a grain, the composition may vary either continuously or discontinuously. There is no particular limitation in the grain size of the silver halide grains of the present invention, but it may preferably be in the range of 0.2 to 1.6 µµ, more preferably 0.25 to 1.2 µm, taking account of other photographic performances such as rapid processability and sensitivity. The silver halide grains used in the emulsion of the present invention may preferably be the grains such that a latent image is formed chiefly on the surface. The emulsion of the present invention is chemically sensitized according to a conventional method. The emulsion of the present invention can be spectrally sensitized to a desired wavelength with use of a sensitizing dye. There is no particular limitation in the silver halide grains to be used in the emulsion layer(s) other than the above silver halide emulsion layer according to the present invention, but such silver halide grains may preferably have a silver chloride content of 80 mol % or more in the same manner as used in the silver halide emulsion layer according to the present invention. The light-sensitive silver halide photographic material constituted as above can be, for example, a color negative film or positive film and a color photographic paper, but the effect of the present invention can be effectively exhibited when it is used as a color photographic paper used for direct view. In the light-sensitive silver halide photographic material of the present invention, there can be optionally used additives such as hardening agents, plasticizers, latex, surface active agents, matting agents, lubricants and antistatic agents. The light-sensitive silver halide photographic material of the present invention can form an image by carrying out the color development processing known in the present industrial field. A color developing solution may have a pH value of usually 7 or more, most generally about 10 to 13. The color development may be carried out at a temperature of usually 15°C or more, and generally in the range of 20°C to 50°C. For the purpose of the rapid development, it may preferably be carried out at 30°C or more. The development has been carried out conventionally in 3 minutes to 4 minutes, but, in the present invention aiming at the use in the rapid processing, may preferably be carried out in the range of 20 seconds to 60 seconds, more preferably in the range of 30 seconds to 50 seconds. The light-sensitive silver halide photographic material of the present invention is subjected to bleaching and fixing after the color development. The bleaching may be carried out simultaneously with the fixing. After the fixing, washing is carried out usually. In place of the washing, stabilizing may be carried out, or both of them may be combined. As described in the above, the light-sensitive silver halide photographic material of the present invention was found to have a superior color reproducibility, have been improved simultaneously in both the color-forming performance and light-fastness of the magenta dye image to be formed, have a superior rapid processing feasibility, and also suffer less yellowing at the white area. The present invention will be described below by giving specific working examples. Example 1 A variety of coupler dispersions was prepared according to the process shown below and with the composition as shown in Table 1. The resulting dispersions each were mixed in 500 g of a green-sensitive silver halide emulsion prepared according to the process shown below, and 10 ml of an aqueous 10 % solution of sodium 2,4-dihydroxy-6-chloro-s-triazine was added therein as a hardening agent. The resulting solutions each were coated on a polyethylene-coated paper support, followed by drying to obtain Samples 1 to 13. (Preparation of coupler dispersions) In 100 ml of a mixed solvent comprising 40 g of dioctylphthalate (a high-boiling organic solvent) and 100 ml of ethyl acetate, 40 g each of the couplers as shown in Table 1 was dissolved, and the resulting solution was added in 300 ml of an aqueous 5 % gelatin solution containing sodium dodecylbenzenesulfonate, followed by dispersion with us of an ultrasonic homogenizer to make up the coupler dispersions. (Preparation of silver halide emulsion) EM-1: An aqueous solution of silver nitrade and an aqueous solution of sodium chloride were added and mixed with stirring in an aqueous inert gelatin solution according to a double jet method. Here, the conditions were controlled to keep 60°C, pH = 3.0 and pAg = 7.8. Further added in the same manner were an aqueous solution of silver nitrate and an aqueous solution of potassium bromide. Next, the desalting was carried out according to a conventional method to obtain EM-1. EM-1 was found to be a cubic monodispersed silver chloride emulsion (silver chloride: 99.8 %; silver bromide: 0.2 %) having an average grain size of 0.5 µm. EM-2: An aqueous solution of silver nitrate and an aqueous halide solution (an aqueous solution comprising a mixture of potassium bromide with sodium chloride) were added and mixed in an aqueous inert gelatin solution according to a double jet method. Here, the conditions were controlled according to the method described in Japanese patent O.P.I. Publication No. 45437/1984 so as to keep 60°C, pH = 3.0 and pAg = 7.8. Subsequently, the desalting was carried out according to a conventional method to obtain EM-2. EM-2 was found to be a tetradecahedral silver chloride emulsion containing 90 mol % of silver bromide, having an average grain size of 0.5 µm. Next, chemical sensitization was carried out on EM-1 and EM-2 under the conditions shown below to prepare corresponding green-sensitive silver halide emulsions EMB-­ 1 and EMB-2, respectively. Provided that the compound (S) was added at the time the chemical sensitization was completed. Sensitizing dye (D-1): The samples obtained in the above were subjected to wedge exposure according to a conventional method, followed by the processing as shown below. [Processing steps] (Color developing solution) Made up to 1 liter in total amount by adding pure water, and adjusted to pH 10.08. (Bleach-fixing solution) Made up to 1 liter by adding water, and adjusted to pH 7.0 by use of sulfuric acid or potassium hydroxide. On the respective samples processed in the above, the color-forming performance, light-fastness, yellowing by light and color reproducibility (secondary absorption density and stain) were measure in the manner shown below. Results obtained are shown together in Table 1. Color-forming performance: Maximum reflection density (Dmax) of the respective samples was measured, and regarded as a characteristic for "color-forming performance". Light-fastness: Indicated by the retension of the initial density D₀ = 1.0, observed when sunlight was irradiated on the respective samples for 30 days through an ultraviolet-­ absorbing filter with use of an underglass outdoor weathering stand. Retension = D/D₀ x 100 (%) (wherein D = density after color-fading) Yellowing by light: Measured was the increased density of the blue-light reflection density (ΔD) at unexposed areas (white areas), observed when sunlight was irradiated on the respective samples for 30 days through an ultraviolet-­ absorbing filter with use of an underglass outdoor weathering stand. Secondary absorption density: Spectra of spectral reflection of the respective color-formed samples were measured by use of a color analyzer Type-607 (available from Hitachi, Ltd.). Here, the maximum density of the absorption spectra at visible areas of the respective samples were measured by standardizing them to 1.0. The reflection density of the respective samples at 430 nm was regarded as the secondary absorption density, and used as an indication for the color purity. Stain: Measured was the green light reflection density (D) at unexposed areas of the respective samples immediately after processing. As will be clear from Table 1, Samples 1 and 2 in which the comparative couplers are used show a high secondary density and a cloudy colour in magenta images, giving unsharp images. Also, as is seen in Sample 2, the color-forming performance is improved by using silver halide grains having a high silver chloride content even if the comparative coupler is used, but is only improved with insufficiency. Sample 4 in which the magenta coupler of the present invention and the silver halide grains having a silver chloride content of 99.8 mol % are used, shows good results for both color-forming performance and color reproducibility, but a poor result for light-fastness. Also, Sample 5 in which the comparative anti-color-fading agent is used shows a small effect of improving the light-­ fastness, and Sample 6 involves the problem of the yellowing by light or the deterioration of color-forming performance. Thus, these can not satisfy all of the performances. All of the color-forming performance, light-­ fastness, color reproducibility and resistance to yellowing by light are improved only when the silver halide grains of the present invention, the magenta coupler of the present invention and the anti-color-fading agent of the present invention are used. Also, Samples 7 to 12 in which the compound S-14 is used show better light-fastness than Sample 13 in which the compound SC-1 is used, and smaller values also as to the stain, thus being desirable for the color reproduction. Example 2 Preparation of Sample 7 in Example 1 was repeated except that the magenta coupler, the anti-color-fading agent, the high-boiling organic solvent and the silver chloride content in silver halide grains were varied as shown in Table 2, to obtain 18 kinds of samples (Samples 14 to 31). The same color-forming performance test, color-­ fastness test and colour reproducibility test as those in Example 1 were carried out on these samples. Results obtained are shown in Table 2. As will be clear from Table 2, in all of the samples of the present invention, there can be obtained sharp magenta color images having an excellent light-fastness and color-forming performance, and also less yellowing by light and a small secondary absorption density (i.e., less colour cloudiness). The color-forming performance also is improved with more preferable results when the silver chloride content in the silver halide grains is not less than 90 mol % and not more than 99.9 mol %. The light-fastness also is further improved in Samples 22, 23 and 24 in which the magenta coupler substituted at the 6-position with an isopropyl group or a t-butyl group is used. Example 3 Respective layers of the composition shown below were provided by coating in sequence from the support side, on supports comprising polyethylene-coated paper to prepare color light-sensitive materials for multicolor photography. The amount of compounds is indicated by the amount per 100 cm². First layer: Blue-sensitive silver chloride emulsion layer Yellow coupler (*), 8 mg; blue-sensitive silver chloride emulsion (Em-A) shown below, 3 mg in terms of silver; high-boiling organic solvent (DNP), 3 mg; and gelatin, 16 mg. Second layer: Intermediate layer A hydroquinone derivative (HQ-1), 0.45 mg; and gelatin, 4 mg. Third layer: Green-sensitive silver chloride emulsion layer Magenta coupler (*), 4 Mg; green-sensitive silver chloride emulsion (Em-B, -C or -D) shown below, 2 mg (B, D) or 4 mg (C) in terms of silver; high-boiling organic solvent (DOP), 4 mg; anti-color-fading agent (*), in an amount equimolar to magenta coupler; and gelatin, 16 mg. Fourth layer: Intermediate layer Ultraviolet absorbent (UV-1), 3 mg; Ultraviolet absorbent (UV-2), 3 mg; DNP, 4 mg; HQ-1, 0.45 g; and gelatin, 14 mg. Fifth layer: Red-sensitive silver chloride emulsion layer Cyan coupler (*), 4 mg; DOP, 4 mg; red-sensitive silver chloride emulsion (Em-E) shown below, 3 mg in terms of silver; and gelatin, 14 mg. Sixth layer: Intermediate layer UV-1, 2 mg; UV-2, 2 mg; DNP, 2 mg; and gelatin, 6 mg. Seventh layer: Protective layer Gelatin, 9 mg. The symbol (*) in the first to seventh layers is meant as shown in Table 3. Silver halide emulsions Em-A to Em-E used are as follows: D-1 (same as in Example 1) was used as the sensitizing dye for Em-B, Em-C and Em-D; D-2, for Em-A; and D-3, for Em-E. These samples were subjected to wedge exposure by white light with use of a sensitometer (produced by Konishiroku Photo Industry Co., Ltd.; KS-7 Type), followed by the same processing as in Example 1. On the samples thus obtained, the same tests as those in Example 1 were carried out. Results obtained are shown in Table 3. As will be clear from Table 3, the samples of the present invention show good results for all the light-­ fastness, color-forming performance, color reproducibility and resistance to yellowing by light, of magenta dye images. There is also attained a good color-fading balance or color-forming balance between the yellow, magenta and cyan images, thus obtaining sharp images. In contrast thereto, in Sample 34 in which the comparative anti-color-fading agent is used, the color-­ forming performance is deteriorated or the yellowing by light is increased although the light-fastness of the magenta image is improved. There is also attained only a poor color-forming balance between the yellow, magenta and cyan images, resulting in the reproduction of a neutral image in a greenish color. Also, when the phenol type antioxidants or the metal complexes are used as the anti-color-fading agent in combination with the compound of the present invention, the light-fastness of the magenta image is improved and the color-fading by light is well-balanced, thus obtaining favorable results. Example 4 A variety of coupler dispersions was prepared according to the process shown below and with the composition as shown in Table 4. The resulting dispersions each were mixed in 500 g of a green-sensitive silver halide emulsion prepared according to the process shown below, and 10 ml of an aqueous 10 % solution of sodium 2,4-dihydroxy-6-chloro-s-triazine was added therein as a hardening agent. The resulting solutions each were coated on a polyethylene-coated paper support, followed by drying to obtain Samples 1 to 13. (Preparation of coupler dispersions) In 100 ml of a mixed solvent comprising 40 g of dioctylphthalate (a high-boiling solvent) and 100 ml of ethyl acetate, 40 g each of the couplers as shown in Table 1 was dissolved, and the resulting solution was added in 300 ml of an aqueous 5 % gelatin solution contianing sodium dodecylbenzenesulfonate, followed by dispersion with use of an ultrasonic homogenizer to make up the coupler dispersions. (Preparation of silver halide emulsion) EM-1: An aqueous solution of silver nitrate and an aqueous solution of sodium chloride were added and mixed with stirring in an aqueous inert gelatin solution according to a double jet method. Here, the conditions were controlled to keep 60°C, pH = 3.0 and pAg = 7.8. Further added in the same manner were an aqueous solution of silver nitrate and an aqueous solution of potassium bromide. Next, the desalting was carried out according to a conventional method to obtain EM-1. EM-1 was found to be a cubic monodispersed silver chloride emulsion (silver chloride: 99.8 %; silver bromide: 0.2 %) having an average grain size of 0.5 µm. EM-2 An aqueous solution of silver nitrate and an aqueous of halides (an aqueous solution comprising a mixture of potassium bromide with sodium chloride) were added and mixed in an aqueous inert gelatin solution according to a double jet method. Here, the conditions were controlled according to the method described in Japanese Patent O.P.I. Publication No. 45437/1984 so as to keep 60°C, pH = 3.0 and pAg = 7.8. Subsequently, the desalting was carried out according to a conventional method to obtain EM-2. EM-2 was found to be tetradecahedral silver chloride emulsion containing 90 mol % of silver bromide, having an average grain size of 0.5 µm. Next, chemical sensitization was carried out on EM-1 and EM-2 under the conditions shown below to prepare corresponding green-sensitive silver halide emulsions EMB-­ 1 and EMB-2, respectively. Provided that the compound (S) was added at the time the chemical sensitization was completed. Sensitizing dye (D-1): The samples obtained in the above were subjected to wedge exposure according to a conventional method, followed by the processing as shown below. [Processing steps] (Colour developing solution) (Bleach-fixing solution) (Stabilizing solution) On the respective samples processed in the above, the color-forming perfrmance, light-fastness, yellowing by light and color reproducibility (secondary absorption density and stain) were measured in the manner shown below. Results obtained are shown together in Table 1. Color-forming performance: Maximum reflection density (Dmax) of the respective samples was measured, and regarded as a characteristic for "color-forming performance". Light-fastness: Indicated by the retension of the initial density D₀ = 1.0, observed when sunlight was irradiated on the respective samples for 30 days through an ultraviolet-­ absorbing filter with use of an underglass outdoor weathering stand. Retension = D/D₀ x 100 (%) (wherein D = density after color-fading) Secondary absorption density: Spectra of spectral reflection of the respective color-formed samples were measured by use of a color analyzer Type-607 (available from Hitachi, Ltd.). Here, the maximum density of the absorption spectra at visible areas of the respective samples were measured by standardizing them to 1.0. The reflection density of the respective samples at 430 nm was regarded as the secondary absorption density, and used as an indication for the color purity. Stain: Measured was the reflection density (Dmin) at unexposed areas of the respective samples immediately after processing. As will be clear from Table 4, Samples 1 and 2 in which the comparative couplers are used show a high secondary density and a cloudy color in magenta images, giving unsharp images. Also, in Sample 2 in which the silver halide grains having a high silver chloride content, the color-forming performance is improved, but only with insufficiency. Sample 4 in which the magenta coupler of the present invention and the silver halide grains having a silver chloride content of 99.8 mol % are used, shows good results for both color-forming performance and color reproducibility, but a poor result for light-fastness. Also, Sample 5 in which the comparative anti-color-fading agent is used shows a small effect of improving the light-fastness, and Sample 6 involves the problem that the color-forming performance is deteriorated. Thus, these can not satisfy all of the performances. All of the color-forming performance, light-fastness and color reproducibility are improved only when the silver halide grains of the present invention, the magenta coupler of the present invention and the anti-color-fading agent of the present invention are used. Also, Samples 7 to 12 in which the compound S-14 is used show better light-fastness than Sample 13 in which the compound SC-1 is used, and smaller values also as to the stain, thus being desirable for the color reproduction. Example 5 Preparation of Sample 7 in Example 4 was repeated except that the magenta coupler, the anti-color-fading agent, the high-boiling organic solvent and the silver chloride content in silver halide grains were varied as shown in Table 2, to obtain 18 kinds of samples (Samples 14 to 31). The color-forming performance test, color-fastness test and color reproducibility test same as those in Example 4 were carried out on these samples. Results obtained are shown in Table 5. As will be clear from Table 5, in all of the samples of the present invention, there can be obtained sharp magenta color images having an excellent light-fastness and color-forming performance, and also a small secondary absorption density (i.e., less color-cloudiness). The color-forming performance also is improved with more preferable results when the silver chloride content in the silver halide grains is not less than 90 mol % and not more than 99.9 mol %. The light-fastness also is further improved in Samples 22, 23 and 24 in which the magenta coupler substituted at the 6-position with an isopropyl group or a t-butyl group. Also, in the samples in which the high-boiling organic solvent having a dielectric constant of 7.0 or less is used, the light-fastness and color-forming performance are seen to be improved. Example 6 Respective layers of the composition shown below were provided by coating in sequence from the support side, on supports comprising polyethylene-coated paper to prepare color light-sensitive materials for multicolor photography. The amount of compounds is indicated by the amount per 100 cm². First layer: Blue-sensitive silver chloride emulsion layer Yellow coupler (*), 8 mg; blue-sensitive silver chloride emulsion (Em-A) shown below, 3 mg in terms of silver; high-boiling organic solvent (DNP), 3 mg; and gelatin, 16 mg. Second layer: Intermediate layer A hydroquinone derivative (HQ-1), 0.45 mg; and gelatin, 4 mg. Third layer: Green-sensitive silver chloride emulsion layer Magenta coupler (*), 4 mg; green-sensitive silver chloride emulsion (Em-B, -C or -D) shown below, 2 mg (B, D) or 4 mg (C) in terms of silver; high-boiling organic solvent (DOP), 4 mg; anti-color-fading agent (*), in an amount equimolar to magenta coupler; and gelatin, 16 mg. Fourth layer: Intermediate layer Ultraviolet absorbent (UV-1), 3 mg; Ultraviolet absorbent (UV-2), 3 mg; DNP, 4 mg; HQ-1, 0.45 g; and gelatin, 14 mg. Fifth layer: Red-sensitive silver chloride emulsion layer Cyan coupler (*), 4 mg; DOP, 4 mg; red-sensitive silver chloride emulsion (Em-E) shown below, 3 mg in terms of silver; and gelatin, 14 mg. Sixth layer: Intermediate layer UV-1, 2 mg; UV-2, 2 mg; DNP, 2 mg; and gelatin, 6 mg. Seventh layer: Protective layer Gelatin, 9 mg. The symbol (*) in the first to seventh layers is meant as shown in Table 6. Silver halide emulsions Em-A to Em-E used are as follows: D-1 (same as in Example 1) was used as the sensitizing dye for Em-B, Em-C and Em-D; D-2, for Em-A; and D-3, for Em-E. These samples were subjected to wedge exposure by white light with use of a sensitometer (produced by Konishiroku Photo Industry Co., Ltd.; KS-7 Type), followed by the same processing as in Example 4. On the samples thus obtained, the same tests as those in Example 1 were carried out. Results obtained are shown in Table 6. As will be clear from Table 6, the samples of the present invention show good results for all the light-­ fastness, color-forming performance and color reproducibility, of magenta dye images. There is also attained a good color-fading balance or color-forming balance between the yellow, magenta and cyan images, thus obtaining sharp images. In contrast thereto, in Sample 34 in which the comparative anti-color-fading agent is used, the color-­ forming performance is deteriorated although the light-­ fastness of the magenta image is improved. There is also attained only a poor color-forming balance between the yellow, magenta and cyan images, resulting in the reproduction of a neutral image in a greenish color. Also, when the phenol type antioxidants or the metal complexes are used as anti-color-fading agent in combination with the compound of the present invention, the light-fastness of the magenta image is improved and the color-fading by light is well-balanced, thus obtaining favorable results.

Claims: 1. A light-sensitive silver halide photographic material comprising a support and, provided thereon, at least one silver halide emulsion layer, wherein at least one silver halide emulsion layer of said silver halide emulsion layer contains silver halide grains containing not less than 80 mol % of silver chloride, a magenta dye-forming coupler represented by formula [M-I] and a compound represented by formula [AO]; wherein Z represents a group of non-metal atoms necessary for the formation of a nitrogen-containing heterocyclic ring, said ring formed including Z may have a substituent; X represents a hydrogen atom or an atom or group capable of being split off upon reaction with the oxidized product of a color developing agent; and R represents a hydrogen atom or a substituent; wherein A is a group of non-metal atoms necessary to complete a 5-member to 8-member nitrogen-containing ring and R⁰ represents an aryl group or a heterocyclic group. 2. The light-sensitive silver halide photographic material of claim 1, wherein said compound is one represented by formula [A]; wherein, R¹ is selected from the group consisting of an alkyl group, a coalkyl group, an alkenyl group, an aryl group, a heterocyclic group, an acyl group, a bridged hydrocarbon group, an alkylsulfonyl group and an arylsulfonyl group, R² is a group capable of being a substituent to a benzene ring and m is an integer of 0 to 4, provided that when m is 2 or more R²s may be either the same or different from each other, provided that when m is 2 or more said R²s may form a ring and that R² or OR¹ may cooperatively be combined to form a ring; A is a group of non-metal atoms necessary to complete a 5-member to 8-member ring. 3. The light-sensitive silver halide photographic material of claim 1, wherein said compound is one represented by formula [B]; wherein R¹ is an aryl group or a hetercyclic group, Z² and Z² independently represent an alkylene group having 1 to 3 carbon atoms provided that the total sum of carbon atoms in the alkylene group is 3 to 6 and n is 1 or 2. 4. A light-sensitive silver halide photographic material according to any one of claims 1 to 3, wherein said magenta dye-forming coupler has in its chemical structure at least one sulfonyl or sulfonamide group. 5. A light-sensitive silver halide photographic material according to any one of claims 1 to 4, wherein said magenta dye-forming coupler has in its chemical structure a group represented by a formula wherein Ra, Rb and Rc independently represent a hydrogen atom or an alkyl group provided that at least two of Ra, Rb and Rc are alkyl groups. 6. A light-sensitive silver halide photographic material according to any one of claims 1 to 5, wherein said silver halide emulsion layer contains a phenol-type anti-oxydant. 7. A light-sensitive silver halide photographic material according to any one of claims 1 to 6 which comprises a compound represented by the formula [S]; wherein Q represents a group of atoms necessary to complete a 5-membered or 6-membered ring which may have a condensed benzene ring and M represents a hydrogen atom, an alkali metal atom or an ammonium group.

Inventors: NISHIJIMA, TOYOKI
Applicants: KONICA CORPORATION
Application year: 1987
Main classification: G03C7
IPC codes: G03C7