A BONE INGROWTH CHAMBER

Abstract: The disclosure relates to an apparatus for studying the bone formation or bone ingrowth in an implant in response to locally administered test substances of different types. The apparatus is of a bio-compatible material, preferably pure titanium, and is intented to be implanted in living bone tissue, primarily for animal experiment activities. The apparatus consists of an outer portion (2) with a central recess (2a) in which an inner portion (5) is inserted. The two portions (2, 5) form, in the assembled state, a bone formation through channel (9, 10) which is exposed when the inner portion (5) is removed, whereby examination of tissue (24) which has grown into the channel (9, 10) is made possible. The inner portion (5) further comprises a reservoir (13) for the substance whose bone formation promoting properties are to be tested. The reservoir (13) is connected to the bone formation channel (9, 10) by the intermediary of a capillary aperture (14), so-called diffusion capillary, for the supply of the contemplated test substance without simultaneous liquid flow.

Description: TECHNICAL FIELD The present invention relates to an apparatus for studying bone formation growth in an implant in response to a locally administered test substance. The apparatus is primarily intended for use in animal experimental activities, but a certain clinical, experimental use may also occur. The apparatus is of a biocompatible material, preferably titanium, and is suitable for implantation in living bone tissue. The apparatus consists of a cylindrical outer portion provided with an external thread and with a central recess and a removable inner portion inserted into the recess and lockable to the outer portion. Said portions are together forming at the bottom of the apparatus a bone formation through channel which is exposed when the inner portion is removed in order to make possible examination of tissue ingrowth into the channel. BACKGROUND ART It is previously known in this art how artificial implants may be anchored directly in bone tissue. In order to avoid the risk of loosening or detachment, every attempt is made to achieve a direct contact, i e an exact adaptation between the implant and the surrounding bone tissue, so-called osseointegration. Such an exact adaptation may be achieved by sophisticated operational technique and by a suitable design of the implant. The osseointegration principle developed by professor Bra ˙nemark et al has successfully been used clinically for 20 years for maxillary-anchored dental bridges and is described in, for example: P-I Bra ˙nemark et al, "Osseointegrated titanium fixtures in the treatment of edentulousness". Biomaterials, 1983. Vol 4, January; and Rickard Skalak, "Biomechanical considerations in osseointegrated prostheses". The Journal of Prosthetic Dentistry, June 1983, Volume 49, Number 6. The principle is based on the fact that the implant is of pure titanium, at least in the interface zone between living tissue and implant. SE-A-7 902 035 also discloses and describes the importance of the surface structure of the titanium for a powerful connection between the living bone tissue and the implant. By a special so-called microporous surface structure of the implant, the preconditions are further improved for a more or less permanent anchorage of the implant in the tissue. To be able to assess the preconditions and potential for different implants to form a permanent anchorage with the tissue, there is a need to be able to study in greater detail and under standardized conditions the bone ingrowth of the implant and also those phases which precede the bone formation proper. Thus, it is previously known in this art how a special examination chamber may be operated into the bone tissue of a living animal, the chamber being designed such that samples of newly-formed bone tissue may be harvested from the chamber at regular intervals, and be examined. Hence, the chamber makes possible a quantification of bone ingrowth/implant incorporation under different experimental conditions without the need of sacrificing the animal. Such a test chamber, "The Harvest Chamber", is described in T. Albrektsson, M. Jacobson and P. Kälebo, "The Harvest Chamber-A newly developed implant for Analysis of Bone Remodelling in situ", Biomaterials and Biomechanics 1983, pp. 283-288 From such disclosures as the above-mentioned SE-A-7 902 035, it is apparent that certain substances possess bone growth promoting properties, i e they increase or hasten the growth of bone tissue into an implant and, by such means, shorten the healing time required for the implant. However, prior art methods for studying the effects of such various substances on bone growth have not been without their problems. First, it is difficult to administer a potentially bonestimulating substance locally and, morevover, it is no easy matter to establish that such a substance actually reaches the tissue which is to be examined. Secondly, the evaluation of the new tissue formed once the substance under discussion here has been added requires with all certainty that the newly-formed bone tissue can be distinguished from existing bone tissue. A number of solutions to these problems have been proposed earlier, for example, biomechanical tests have been employed to examine the effects of prostaglandin on animal bone tissue. Furthermore scintigraphic methods have been employed to investigate hormonal growth promoting properties on demineralized cortical bone. Methods based on tetracycline treatment are also previously known in the art. OBJECT OF THE PRESENT INVENTION The object of the present invention is, therefore, to realize an apparatus for testing the potentially bone-stimulating/ retarding effect of a locally administered substance and which obviates the above-indicated problems. To this end, the present invention is based on a test chamber/implant as described above but which has been modified such that local administration of a test substance in liquid form is permitted. The invention is characterized in that the inner portion includes a reservoir in communication with the bone ingrowth channel for the supply of a test substance. In one preferred embodiment of the present invention, the reservoir is in communication with the bone growth channel by the intermediary of a capillary opening, so-called diffusion capillary, for the administration of the test substance in question without simultaneous liquid flow. BRIEF DESCRIPTION OF THE ACCOMPANYING DRAWINGS The nature of the present invention and its aspects will be more readily understood from the following brief description of the accompanying Drawings, and discussion relating thereto. In the accompanying Drawings, Fig. 1 is an exploded view of the apparatus in its entirety, partly in section; Fig. 2 illustrates the central portion of the apparatus with a reservoir for the administered solution whose bone growth promoting properties are to be tested; and Fig. 3 schematically illustrates how the apparatus functions in the bone tissue of an animal. DESCRIPTION OF PREFERRED EMBODIMENT As was mentioned by way of introduction, the apparatus, hereinafter designated the implant, is based on the previously known so-called "harvest chamber" which consists of a cylindrical outer portion of pure titanium and an inner, removable central portion. Two diametrically opposed holes are provided in the outer portion which cooperate with grooved recesses in both portions such that an open through channel is formed when the implant is assembled. Once the implant has been inserted in a known manner in the bone tissue, for example in the tibia of a rabbit, a bone formation process commences and the channel is duly filled with newly-formed bone tissue. The bone formation process and the ingrown bone tissue may be studied at regular intervals by removing the central portion of the implant. Fig. 1 shows an implant 1 according to the present invention which, as opposed to the prior art apparatus (the Harvest Chamber) permits the local administration of a test substance. The implant is of pure titanium and comprises an outer, cylindrical portion 2, with a central recess 2a and a base plate 3. The cylindrical portion is provided with an outer thread 4 for the careful threading of the implant into a bore in the bone tissue. Advantageously, use is made of the atraumatic insertion technique of titanium implants as is previously known from Professor Bra ˙nemarks's maxillary-anchored dental bridges, this constituting a precondition for osseointegration. The outer, cylindrical portion 2 is open at its top and permits an inner, cylindrical portion 5 to be inserted such that this portion rests with its lower end surface 6 against the base plate 3. The inner, central portion 5 is fixedly locked to the outer portion 2 by means of two locking screws 7, 8 which are screwed in place in two threaded holes 3a, 3b in the base plate. On its inner surface, the base plate 3 is provided with a recessed groove 9 which cooperates with a corresponding recessed groove 10 in the lower end surface 6 of the central portion. Two holes 11, 12 diametrically disposed in the circumferential surface of the outer portion also cooperate with the grooved recesses such that a through channel is formed for bone ingrowth. Instead of forming the bone growth channel by two cooperating recessed grooves 9, 10 in the base plate and the central portion, respectively, the channel may also be formed by a grooved recess in the central portion, while the interior defining surface of the base plate is planar. In such instance, the grooved recess in the central portion is made slightly deeper. The central portion 5 further includes a liquid reservoir 13 which is in communication with the bone growth channel through a narrow capillary aperture 14 - a so-called diffusion capillary - in the bottom of the reservoir (see Fig. 2). Hereby, administration, or supply, of test substance will be effected without, at the same time, causing liquid flow to the channel. At its top, the liquid reservoir is covered by a cover plate 15 which is locked against the upper end surface 16 of the central portion by the locking screws 7 and 8. Apart from two holes 17 and 18 for the locking screws, the cover plate 15 is also provided with two holes 19 and 20 above the liquid reservoir for hoses 21, 22 for the supply and removal, respectively, of liquid/testing substance. A sealing washer of silicon rubber or the like (not shown) may advantageously be disposed between the cover plate 15 and the upper end surface 16 of the central portion. The liquid reservoir 13 consists of an elongate, diagonally disposed recess in the central portion 5, being of the same orientation as the bone growth channel 9, 10, and with the two locking screws 7 and 8 located on either side of the reservoir. The reservoir extends in a vertical direction down through the central portion 5 so that only a thin partition 6a separates the bottom of the reservoir from the grooved recess 10. The capillary aperture 14 is centrally located in the bottom of the reservoir, while the inlet and outlet hoses have their connections further out towards the edges of the reservoir. In Fig. 3, the implant is shown surgically inserted in the tibia 23 in the one extremity of an experimental animal, for example a rabbit, such that the bone growth channel is located wholly beneath the defining surface of the bone. The figure shows partly how bone tissue 24 has grown into the channel and partly how the reservoir is filled with that test substance whose bone stimulating/retarding effect is to be examined. In this case, the chamber is connected, via an inlet hose 22, to a subcutaneous, osmotically acting minipump 25 of known type, for example ALZET model 2002, from ALZA Corp., California, USA. Hereby the test substance may be continually administered for periods of weeks or more, such that a sufficiently high concentration will be maintained in the liquid volume. The outlet hose 21 is opened to subcutis and acts as a drainage. A suitable size of implant may be: height 10 mm, diameter 6 mm. The openings 11, 12 of the bone ingrowth channel may be of a diameter of 1 mm. The diffusion capillary 14 is of a diameter of 0.25 mm and a length of 1 mm. The reservoir may have a volume of 10 microlitres and the intake flow from the minipump 25 is, in this case, 0.5 microlitres per hour. Hereby, there will be obtained a slow, continuous intake flow of liquid/test substance to the reservoir, which gives a concentration gradient along the diffusion capillary 14. The flow through the diffusion capillary will be low, since the reservoir is drained through the hose 21. The newly-formed bone tissue 24 which has grown into the channel is treated locally with the administered test substance without being disturbed by a flowing solution. Treated, or non-treated bone samples 26 (see Fig. 2) of approx. 5 mm in length and 1 mm in diameter may be removed at regular intervals from the implant and be examined. The implant is inserted and functions as follows. An implant is inserted in each tibial metaphysis of an experimental animal by known atraumatic operational techniques (see above). In this operation, it is ensured that the bone growth channel is localized in the cortical bone. After the operation, the implant is covered by the soft tissue, skin and fascia which is sutured. The one implant serves as a test implant, the test substance being administered during periods of weeks or more, while the other implant in the other extremity of the animal serves as a control reference implant. The test substance is supplied to the liquid reservoir of the test implant by means of an osmotically acting minipump of known type. There will hereby be obtained a slow, continous inflow of the test substance, which ensures a sufficiently high concentration of the test substance, in the liquid volume. The flow through the diffusion capillary will be negligibly low, since the reservoir is drained at the same time through the outlet conduit. After a bone formation period of approx. four weeks, the soft tissue is reopened, the locking screws are loosened and the central portion is removed. The newly-formed bone tissue in the form of cylindrical rods defined by the bone growth channels are stored in, for instance, formaldehyde prior to evaluation. The evaluation of the results is effected in that bone formation in the test implant inserted in the one extremity of the experimental animal is compared with the bone formation in the control implant in the other extremity. For purposes of quantification, use is made of databased microradiography which is known in and of itself and does not form part of the present invention, see, for example, the reference "the Harvest Chamber...", above. The present invention should not be considered as restricted to the embodiment described above and shown on the drawings by way of example, but may be varied without departing from the scope of the appended Claims. Hence, in certain cases, it may be sufficient that the test substance is supplied to the liquid reservoir through injection, or in the form of pellets with a slow release of the test substance.

Claims: An apparatus for studying bone formation growth in an implant in response to a locally administered test substance, the apparatus being of a bio-compatible material and suitable for implantation in living bone tissue, the apparatus consisting of a cylindrical outer portion (2) provided with an external thread (4) and with a central recess (2a) and a removable inner portion (5) inserted into the recess and being lockable to the outer portion, said portions together forming at the bottom of the apparatus a bone formation through channel which is exposed when the inner portion is removed in order to make possible examination of tissue ingrowth into the channel characterized in that inner portion (5) includes a reservoir (13) in communication with the bone ingrowth channel (9, 10) for the supply of a test substance. The apparatus as claimed in Claim 1, characterized in that it is made of pure titanium, or at least coated with pure titanium on those surfaces which come into direct contact with bone tissue. The apparatus as claimed in Claim 2, characterized in that the reservoir (13) consists of a cavity provided in the inner portion (5) and being in communication with the bone formation channel (9, 10) by the intermediary of a capillary aperture (14), so-called diffusion capillary, for the supply of the test substance under consideration without simultaneous liquid flow. The apparatus as claimed in Claim 3, characterized in that the reservoir (13) consists of an elongate, diagonally disposed cavity of substantially the same orientation as the bone formation channel (9, 10), two through holes for locking screws (7, 8) for fixed interlocking of the two portions (2, 5) being disposed in the material of the inner portion (5) on either side of the elongate reservoir (13). The apparatus as claimed in Claim 4, characterized in that the reservoir (13) is upwardly covered by a cover plate (15) which is locked to the upper end surface (16) of said inner portion by said locking screws (7, 8). The apparatus as claimed in Claim 5, characterized in that said cover plate (15) is provided with two holes (19, 20) above said liquid reservoir (13) for hoses (21, 22) for the supply and removal (drainage), respectively of test substance . The apparatus as claimed in Claim 6, characterized in that said reservoir (13) is connected to a subcutaneous, osmotically acting minipump (25) for the continuous supply of test substance during a predetermined period of time.

Inventors: ALBREKTSSON, THOMAS, ASPENBERG, PER
Applicants: NOBELPHARMA AB
Application year: 1987
Main classification: A61B10
IPC codes: A61F2, A61M1, A61B10, A61B17