Acid modified adhesive compositions

Abstract: An adhesive composition which comprises a polymer-in-monomer system and/or a sulfur-bearing component selected from chlorosulfonated polyethylenes and sulfonyl chlorides (the latter optionally in admixture with a chorinated polyethylene), a polymerisation catalyst, and a strong organic acid. The monomer is usually a vinyl monomer such as (meth)acrylate. The acid is preferably maleic acid. A graft copolymer may be included.

Description: BACKGROUND OF THE INVENTION The present invention is directed to improved polymerizable acrylate and/or methacrylate based adhesive compositions, well suited for bonding typical plastic components, and especially well suited for the bonding of the so-called "difficult to bond" plastics (e.g., chemical-, environmental-, and solvent-resistant plastics) and like components. Traditionally, the adhesive bonding of plastics has been a difficult task, requiring either a great deal of surface preparation and/or the use of highly specialized adhesive formulations. Such methods and compositions are described in U.S. Patent Nos. 4,397,707 to Dawdy, 4,200,480 to Wolinski et al ., 3,987,122 to Bartz et al ., 3,962,498 to Owston, and 3,873,640 to Owston et al . Polymerizable acrylate and/or methacrylate based adhesives generally exhibit good adhesion on unprimed non-crystalline thermoplastic materials. It is believed that this good adhesion results because the base monomer (such as methyl methacrylate) can solvate the plastic prior to hardening to provide the needed "bite" for strong bonds. Many advanced thermoplastic materials that are either currently being used or have been considered for automotive structural applications are designed or have been modified for enhanced heat resistance, dimensional stability, environmental durability and chemical resistance (e.g., to gasoline, detergents, etc). Such designs and modifications often make these plastics inherently difficult to bond through the solvating effect which occurs with typical acrylate or methacrylate based adhesives. Specifically, polyurethane and epoxy adhesives normally used in automotive bonding applications bond many of these materials only with the use of extensive pretreatment, if at all. Both of these adhesive classes require long cure times at ambient temperature and/or exposure to elevated temperatures to effect even handling strength. Systems designed for faster development of strength often have extremely short and impractical working life. US-A-3934056 discloses adhesive compositions which comprise an ethylene-vinyl acetate copolymer, optionally together with polyethylene; chlorinated or chlorosulfonated polyethylene; an unsaturated carboxylic acid that is solid at room temperature; and an organic peroxide. EP-A-0142923 discloses an adhesive composition comprising an acrylate- or methacrylate-based ester monomer; a catalyst; a chlorinated or chlorosulfonated polyethylene polymer including organic sulfonyl chloride; and a graft copolymer resin. SUMMARY OF THE INVENTION An adhesive composition according to the present invention comprises: 10 to 75% by weight of a polymer-in-monomer solution, the monomer being an acrylic or methacrylic ester-based monomer and the polymer comprising (i) a sulfur-bearing component selected from chlorosulfonated polyethylenes and mixtures of sulfonyl chloride with a chlorinated polyethylene and (ii) a graft copolymer which is a polymer having a glass transition temperature substantially below 20°C to which is grafted a polymer having a glass transition temperature substantially above 25°C; up to 15% by weight of a polymerisation catalyst; and 0.1 to 20% by weight of a strong organic acid having a dissociation constant (K d ) of 0.01 to 1 and/or, as a 0.2 N aqueous solution, a pH of 1.3 to 2.0. The novel compositions can be used to bond certain solvent-resistant plastics and like materials as defined herein, with bond strengths preferably exceeding the deformation or breaking strength of the bonded materials themselves. It has been discovered that by adding one or more strong organic carboxylic acids to conventional acrylate and/or methacrylate based adhesive compositions, the bonding characteristics thereof change dramatically. It is believed that the addition of a strong organic acid to acrylate and/or methacrylate based adhesives acts to promote adhesion to solvent-resistant and/or heat-resistant plastics, and the like, due to interactions at the molecular level, e.g., through hydrogen bonding, and the like. As used herein, the terms "solvent-resistant, "chemical-resistant," "environmental-resistant," and "heat-resistant" are used when referring to plastics to describe those materials which in the past have been considered "difficult" (if not impossible) to bond with conventional acrylate or methacrylate based adhesive compositions. It is believed that this difficulty may be due to the inability of the acrylate and/or methacrylate monomers to solvate such plastics. Such materials generally have a polymeric structure or a like chemical make-up which makes them inherently resistant to the effect of solvents, heat, and other environmental agents. These materials also generally include within their structure, hydrogen bonding acceptor sites which are formed by electron rich atoms (e.g., N, O, or the like) or by similar electronegative groups. The main classes of these materials are the thermoplastics and thermosets. Solvent-resistant thermoplastic materials whose bondability is most dramatically enhanced by the compositions of the present invention are generally polar and/or crystalline polymers or blends of such polymers and include nylon and blends of nylon and nylon-like materials with other polymers, such as polyimides and blends of polyimide with other polymers such as polyester. Solvent-resistant thermoset materials which exhibit dramatically enhanced bondability with the adhesive compositions of the present invention generally comprise polar, solvent-resistant, materials, and include homogeneous materials such as epoxies and urethanes, and composite materials such as polyesters, urethanes, and/or epoxies, containing fillers such as glass, minerals, carbon, and the like. In the case of composite thermoset materials, either the base material (epoxy, urethane, polyester, etc.) or the filler (or both) may have the requisite hydrogen bonding capability, or other requisite adhesion promoting characteristics. The present invention thus utilizes acrylate and/or methacrylate based adhesive compositions as a base material. To this base material is added an effective amount of one or more strong organic acids, i.e., acids having a relatively high dissociation constant (K d ). It has further been discovered that, the addition of water to compositions containing these acids can increase their effectiveness, apparently through partial or enhanced solubility, which is believed to aid in the dissociation thereof. These adhesive effects can further be enhanced by heat treatment of the bonds either during or after the bonding step (or both). The amount of the strong organic acid to be added to the adhesive base composition varies with both the acid and the adhesive. Most of the strong organic acids used in the adhesive compositions of the present invention are water soluble, and thus many are insoluble in typical acrylate and/or methacrylate based adhesive formulations. The strong organic acids of the present invention can be used in mixtures with the standard adhesive acids, e.g., acrylic and/or methacrylic acid. Typically the acid or mixture of acids is added to the adhesive formulation as a dispersion in an amount ranging from about 0.1 parts to 20 parts per hundred (pph), preferably from about 0.5 to 10 pph (based upon the weight of the formulation). Optionally, the acid can be dissolved in a sufficient amount of water and the mixture added to the adhesive. Those acids which are directly soluble in the adhesive base formulation may be added without prior solubilization. As used herein, the term "strong organic acid" means that the acid is generally an organic carboxylic acid, e.g., R-COOH, (wherein R may be alkyl, aryl, aralkyl, and the like) so long as the relative "acid strength" of the organic acid is high. By definition, di- and poly-basic acids as well as mixed acids are included within this definition. To determine relative acid strength, one of two standards is employed herein: The first standard makes use of the literature value for the dissociation constant (K d ) of the acid (at about 23°C, i.e., room temperature). To be useful herein, the K d value is generally within the range of from about 1 x 10⁻⁴ to about 10 x 10⁻¹, preferably from about 1 x 10⁻² to about 1 x 10⁻¹. In the case of di- or poly-carboxylic acids, the K d value used as a measure of the relative acid strength is the dissociation constant for the first acidic proton, i.e., K 1d . The second standard for determining relative acid strength is generally applied to acids having no readily ascertainable K d value. Under this standard, the pH of an 0.2 N aqueous solution of the acid is measured. Such solutions of the acids useful in the present invention generally have pH values within the range of from about 1.2 to 2.3, preferably from about 1.3 to 2.0. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS The present invention utilizes acrylate and/or methacrylate based adhesive compositions as a base material. To this base material is added an effective amount of one or more strong organic acids and optionally, an effective amount of water, either if necessary, or if desired, to effect dissolution of the acid or to enhance its effectiveness. The present invention represents a dramatic discovery in that acrylate and/or methacrylate based adhesive formulations can be modified such that they will bond many solvent, chemical, and/or heat-resistant plastics. While not wishing to be bound by theory, it is believed that the modified adhesive formulations of the present invention contain efficient hydrogen bonding donors which interact with what are perceived to be hydrogen bonding "acceptor" sites on the nylon and/or plastic polymer surfaces. Alternatively, or additionally, the modified adhesive formulations of the present invention may participate in a solvating-action with the materials being bonded, more effectively than previous adhesives. The improvements noted with adhesive formulations modified in accord with the present invention are surprisingly greater than expected for the following reasons: (1) The preferred strong organic acids useful herein are the strong organic - carboxylic acids. Many of these acids are substantially immiscible with conventional acrylate and/or methacrylate based adhesive compositions (in the absence of water) and are dispersed rather than intimately dissolved therein. It would be expected that little if any interaction between the acids and the adhesive formulation would result from such mixing. (2) The adhesives modified in accordance with the present invention gave very strong bonds at room temperature on standard "as received" nylon which is believed to be a new accomplishment in this art. The conventional method of bonding nylon involves the use of phenol (or its derivatives) and requires heat to effect strong bonding. (3) The modified adhesives of the present invention also provided strong bonds to low-profile fiberglass sheet molding compound (SMC) which has previously been difficult or impossible to bond using conventional acrylate/methacrylate adhesives. As described above, the novel adhesive compositions of the present invention are especially useful for bonding solvent-resistant thermoplastics and thermosets. In addition to the nylon-6, nylon 6-6 and nylon 6-12 types of thermoplastics, the following table (I) lists additional commercially available thermoplastics and thermoplastic alloys, some of which contain nylon or nylon-like polymers that are bondable with the adhesive compositions of the present invention. Table II sets forth a number of commercially available thermoset materials which exhibit superior bonding performance with the adhesive compositions of the present invention. The materials listed in Tables I and II are by no means exclusive, but are intended only to demonstrate the range of materials bondable by the adhesive compositions of the present invention. For example, certain multiphase materials, such as ALCRYN from Du Pont, which is a proprietary, polar, solvent-resistant, modified halogenated polyolefin thermoplastic elastomer, are readily bonded by the adhesive compositions of the present invention. When steel (or other metal) is bonded to any of the above-described plastics, it is often desirable to use a corrosion-resistant primer on the metal such as the commonly employed electrodeposited epoxy pretreatment known as "E" coat, manufactured and sold by the Pittsburgh Paint Glass (PPG) Company. The present invention provides improved acrylic and/or methacrylic ester based adhesive compositions. General adhesive formulations based upon derivatives of acrylic acid and/or methacrylic acid are well known, but they do not have the bonding characteristics of the present adhesive compositions. In one preferred embodiment of the present invention, the adhesive base formulation may be used either as a two-part system or as a system using a primer. In either case, the critical components of such a preferred composition comprise an effective amount of a solution of a sulfur - bearing composition selected from the group of chlorosulfonated polyethylene and a mixture of sulfonyl chloride with chlorinated polyethylene in a polymerizable vinyl monomer or a mixture of monomers and a polymerization catalyst. Such an effective amount of the sulfur-bearing composition should contain from about 25 to 70 weight percent chlorine and from about 3 to 160 mmoles of sulfonyl chloride moiety per 100 grams of polymer and the polyethylene from which the chlorosulfonated or chlorinated polyethylene is prepared should have a melt index of from about 4 to 500. The solution can have a Brookfield viscosity of up to about 1 million. Materials such as these are described in Briggs et al ., U.S. Patent No. 3,890,407, the disclosure of which is incorporated herein by reference. In another preferred embodiment of the present invention, the adhesive base formulation will comprise a polymer-in-monomer solution, an organic sulfonyl chloride species having up to 20 carbon atoms, and/or a chlorosulfonated polymer, a polymerization catalyst and an accelerator. The polymer of the polymer-in-monomer solution (as distinguished from any chlorosulfonated polymer) is present in an amount ranging from about 10 to 75 weight percent (based upon the weight of the entire solution, i.e., polymer, monomer, and organic sulfonyl chloride). The adhesive base formulation has a viscosity between about 2000 centipoise and about 1 million centipoise. The monomers employed in the base formulation are acrylic acid and/or methacrylic acid based esters. The organic sulfonyl chloride is present in an amount such that from about 3 to 160 mmoles of sulfonyl chloride groups are present per 100 grams of polymer. The polymerization catalyst is present in an amount of up to 15 percent by weight of the solution, and usually in an amount within the range of from about 0.2 to 5 percent by weight. Preferred polymerization catalysts for this base formulation include free radical generators such as organic peroxides, organic hydroperoxides and organic peresters. The accelerator (or activator) is present in an amount within the range of from about 0.01 to 10 percent by weight, preferably from about 0.1 to 5 weight percent. Materials such as these are described in Briggs et al ., U.S. Patent No. 4,182,644, the disclosure of which is incorporated herein by reference. Acrylate and/or methacrylate monomers constitute the preferred principal reactants of the base adhesive formulation of the present invention. The preferred acrylate and/or methacrylate monomers comprise an acrylate-based or methacrylate-based material, such as an ester monomer. Such reactants are generally the reaction products of acrylic and/or methacrylic acids with one or more mono- or polybasic, substituted or unsubstituted, alkyl (C₁ to C₁₈), aryl, aralkyl, or heterocyclic alcohols. Preferably, the ester monomers are alkyl monomers, most preferably, C₁ to C₄ alkyl esters. In the case of heterocyclic esters, the preferred heteroatom is oxygen. When the alkyl ester contains more than about six carbon atoms, such esters are preferably used in blends with lower alkyl esters. In the most preferred embodiments, the methacrylate-based ester monomer is selected from materials such as methyl methacrylate, ethyl methacrylate, butyl methacrylate, cyclohexyl methacrylate, 2-ethylhexyl methacrylate, and tetrahydrofurfuryl methacrylate. Still more preferably, the methacrylate-based ester monomer is selected from the group consisting of methyl methacrylate and ethyl methacrylate. Most preferably, the methacrylate-based ester monomer is methyl methacrylate. Adhesive compositions based upon these preferred monomers are described in Briggs, U.S. Patent No. 4,536,546, the disclosure of which is incorporated herein by reference. In certain instances it is desirable that the methacrylate-based ester monomer include an effective amount of an inhibitor for inhibiting or otherwise preventing polymerization of the ester monomer. For example, several of the preferred compositions of the present invention which include methyl methacrylate ester monomer, may also contain from about 10 to about 1500 parts per million (ppm) of hydroquinone or hydroquinone monomethyl ether in the ester monomer as such an inhibitor. The preferred composition of the present invention further includes a catalyst. As used herein, the term "catalyst" means a free-radical generator. Free-radical generators include organic peroxides, organic hydroperoxides, peresters, and peracids. As is well known in the field of acrylate-based and methacrylate-based compositions, such a catalyst is used for triggering polymerization of acrylate-based and methacrylate-based monomers. Preferred catalysts in the composition of the present invention are cumene hydroperoxide and methyl ethyl ketone peroxide, both of which are known free-radical generators. The composition of the present invention includes either a chlorinated or a chlorosulfonated polyethylene polymer resin. Preferably, however, the composition includes chlorosulfonated polyethylene polymer, the resin which, in turn, preferably contains from about 25 to about 70 weight percent chlorine and from about 3 to about 160 millimoles of sulfonyl chloride moiety per 100 grams of polymer. A most preferred chlorosulfonated polyethylene polymer resin employed in the composition of the present invention is marketed under the trademark "HYPALON 30" and is commercially available from E.I. Du Pont de Nemours & Company of Wilmington, Del., 19898. The composition of the present invention also preferably includes a catalyst activator (or initiator). The most preferred initiators comprise condensation products of butyraldehyde and butylamine or aniline. Such condensation products, marketed under the trademarks 'VANAX 833" and "VANAX 808," respectively, are currently commercially available from the R. T. Vanderbilt Company, Inc., 230 Park Avenue, New York, NY 10017. In addition to the preferred catalyst and catalyst activator components set forth above, other well known free radical generating moieties or combinations of peroxides and reducing agents (i.e., "redox" catalyst systems) may be used herein, provided that none of the added components interfere with the action of the strong organic acid (or vice versa ). Such formulations are well known to those artisans skilled in the field of acrylate based adhesives. The composition of the present invention further includes a graft co-polymer resin. Such graft co-polymer resins have generally been found useful as physical property-modifiers of PVC, or other normally-rigid plastics or the like. See, for example, U.S. Patent No. 3,845,164 to Goto et al ., the disclosure of which is incorporated herein by reference. Such physical property modifiers, moreover, have been found to increase flexibility and impact resistance of many normally-rigid plastics. In such a use, the graft co-polymer is generally a relatively small particle which, for example, can be dispersed throughout the normally-rigid plastic prior to the injection molding thereof. The preferred graft co-polymers used in the preferred composition of the present invention provide improved spreading and flow properties to the uncured adhesive compositions. Such improved flow properties are highly desirable in certain adhesive applications. For example, when an adhesive is applied to an article by means of a syringe-type applicator, many commercially available adhesives undesirably form a "string"of adhesive which generally extends from a first point of the article (where the adhesive is applied) to a second point (a subsequent position of the applicator) spaced from the first point. The flow properties of the composition of the present invention are such that a relatively small droplet of such adhesive is topically applied to the point of application on the article to be bonded, with no adhesive string extending therefrom. In the preferred composition of the present invention, it is believed that the methacrylate-based ester monomers polymerize and at least partially attach themselves to the chlorosulfonated polyethylene polymer resin backbone. The preferred graft co-polymer resins used in the composition of the present invention are selected from the group consisting of acrylonitrile-butadine-styrene (ABS), methacrylate-butadiene-styrene (MBS), methacrylate-acrylonitrile-butadine-styrene (MABS), acrylate-styrene-acrylonitrile (ASA), all-acrylics, styrene-acrylonitrile grafted onto elastomeric backbones of ethylene-propylene-diene-monomer (SAEPDM), and methacrylic-acrylic rubber-styrene (MAS). The most preferred graft co-polymer resins are selected from the group consisting of MABS, ASA, all-acrylic and MBS. The ABS graft co-polymer resin preferably has a styrene-butadiene rubber core and a styrene-acrylonitrile shell. The MBS graft co-polymer resin preferably has a styrene-butadine rubber core and a shell of acrylic polymer or co-polymer. The MABS graft co-polymer resin preferably has a styrene-butadiene rubber core and a shell of methacrylate-acrylonitrile co-polymer. More preferably, the MABS graft co-polymer resin has a core, which is approximately 75% by weight of the total weight thereof, which consists of butadiene and styrene in the weight ratio of about 50 to 25, and a shell of methyl methacrylate and acrylonitrile in the weight ratio of about 20 to 5. The preferred ASA graft co-polymer resin is substantially as disclosed in U.S. Patent No. 3,944,631 to Yu et al ., the disclosure of which is incorporated herein by reference. A most-preferred ASA graft co-polymer resin, marketed under the trademark "SCC 1015" (see Table III below), is substantially as described in the '631 patent and includes a crosslinked acrylate elastomer, a crosslinked styrene-acrylonitrile co-polymer and a linear styrene-acrylonitrile co-polymer. The most-preferred ASA graft co-polymer resin, moreover, appears morphologically to be made of interpenetrating polymer networks. Preferred all-acrylic graft co-polymer resins are as disclosed in U.S. Patent No. 3,985,703 to Ferry et al ., the disclosure of which is incorporated herein by reference. Most-preferred all-acrylic graft co-polymer resins, marketed under the Trademarks "KM 323 B" and "KM 330" (see Table III below), have a rubber-type core which is approximately 75% of the total weight thereof, which consists of butyl methacrylate-type monomers and a shell of methyl methacrylate. The following table (III) lists manufacturers (past and present) and trademarks of the preferred and most-preferred graft co-polymer resins, discussed hereinabove. The commercial availability of these materials from their original maker is by no means guaranteed by virtue of this listing. As the skilled artisan is well aware, alternate sources and equivalent materials are constantly being formulated by competitors in the polymer resin field. The present invention will be further illustrated by reference to the following examples which are intended to aid in the understanding of the invention but which are not to be construed as limitations thereof. All parts, proportions and percentages reported herein, unless otherwise specified, are by weight. All temperatures are expressed in degrees Celsius (°C). GENERAL EXPERIMENTAL PROCEDURE Unless indicated otherwise, preferred adhesive compositions were prepared by combining two separate (i.e., distinct) mixtures of methyl methacrylate ester monomer. One of the two monomer mixtures contained a chlorosulfonated polyethylene resin plus graft copolymer resins. The other of the monomer mixtures contained a graft co-polymer resin. The following table (IV) is a summary of many of the commercial products that were employed in the examples of the present invention. Adhesive base solutions for examples 1-35 etc. were prepared as follows:- A forty percent solution of HYPALON 30 chlorsulfonated polyethylene in methyl methacrylate monomer (MMA) was prepared by rolling 1200 g of the polymer and 1800 g of MMA in a glass jar for two days. The granular insoluble acids and derivatives thereof, used in Examples 1 to 28 were ground to a fine paste in methyl methacrylate monomer by rolling for two days at high speed 37.5 parts by weight (pbw) of acid and 62.5 pbw of MMA in a 57 g glass jar containing 4-8 glass spheres approximately 1.67 cm (0.66 in.) in diameter. The liquid or soluble acids or derivatives of Examples 29 to 35 were mixed in the monomer as received. Adhesive test solutions were made by combining 20.07 pbw of MMA monomer, 60.20 pbw of the 40 percent solution of HYPALON 30 in MMA, 0.25 pbw of NAUGARD SCC BHT (butylated hydroxy toluene stabilizer) and sufficient acid or derivative to provide 0.116 moles of carboxylic acid functionality per 100 pbw of adhesive. After mixing these ingredients thoroughly with a spatula, 12.46 pbw of ACRYLOID KM 452 resin were added and thoroughly dispersed using a laboratory "Hochmeyer" high speed disperser. The solutions were allowed to stand for one day in order to solvate the ACRYLOID resin and remixed with the Hochmeyer mixer. Cumene hydroperoxide (0.5 pbw) was added followed by a brief final agitation with the Hochmeyer mixer. The activator solution for Examples 1 to 35 was prepared by combining 72.5 pbw of MMA, 10.0 pbw of Stauffer SCC 1015 resin and 10.0 pbw of ACRYLOID KM 330 and mixing thoroughly with a spatula and then with the Hochmeyer mixer. The mixture was allowed to stand overnight to solvate the resins followed by mixing with the Hochmeyer mixer. Then 7.5 pbw of VANAX 808 was added and the solution was again mixed thoroughly with the Hochmeyer mixer. Adhesive bonds were prepared by mixing equal parts of each test adhesive base with the above activator solution until the color was uniform indicating a thorough mix. Bond samples for compressive shear testing (per ASTM D 905) were prepared from 0.635 cm x 2.54 cm x 2.54 cm (0.25 in. x 1 in. x 1 in.) and 0.635 cm x 2.54 cm x 5.08 cm (0.25 in. x 1 in. x 2 in.) pieces of nylon 6-6 bonded such that approximately 0.635 cm (0.25 in.) of overhang and 1.9 cm (0.75 in.) of overhang resulted at the top and bottom of the assembled test piece. Adhesive was applied to the center of the bonded area of the 5.08 cm (2 in.) test piece and a 1.27 cm x 0.051 cm (0.5 in. x 0.010 in.) wire ring spacer was placed in the center. The 2.54 cm (1 in.) test piece was aligned and pressed over the bonded area to squeeze the adhesive out of the perimeter on all sides to ensure complete coverage. Spring clamps were used to secure the bond during the curing process. The bonded assemblies were allowed to set at ambient temperature (about 23°C) for 30 minutes. Half of the bonded assemblies were placed in a constant temperature chamber at 23° C ± 0.5°C for two days prior to testing. The remaining bonded assemblies were placed in an oven at about 121°C for 60 minutes and then allowed to stand at ambient temperature for two days prior to testing. Bond samples for lap shear testing per ASTM D1002 were prepared from 2.54 cm x 114.3 cm x 0.318 cm (1 in. x 4 in. x 0.125 in.) coupons of Noryl GTX. The bonded areas of the coupons were scrubbed with an abrasive nylon ("Scotchbrite") pad soaked with isopropanol followed by wiping with a tissue soaked with fresh isopropanol. The bonds were assembled as above using the wire ring spacers, with an overlap of 1.27 cm (0.5 in.), and clamped during the curing process. Bond test results are given as the average of three individual specimens tested on an Instron tensile tester at 23°C. The compressive shear bonds with nylon 6-6 were tested at a crosshead speed of 0.127 cm (0.05 in.) per minute and the lap shear bonds with Noryl GTX were tested at 1.27 cm (0.5 in.) per minute. In the following Tables, the nylon 6-6 compressive shear strength with room temperature cure is "compress 1" and with heat cure is "compress 2". The Noryl GTX lap strength with room temperature cure is "lapsh 1" and with heat cure is "lapsh 2". All these results are given in kPa. As a guide to the effectiveness of adhesive compositions of the invention, the following Examples report a number of additive materials, some of which improved the adhesive, some of which did not. An indication of improvement can be seen in terms of bond strength, e.g. a minimum value of 3450 kPa (500 psi), preferably at least 5200 kPa (750 psi), more preferably 6900 kPa (1000 psi), and most preferably 13800 kPa (2000 psi). It should be noted that bond strengths vary depending upon the materials being bonded (here, Nylon 6-6 and NORYL GTX), the cure temeprature, e.g. heat curing (about 121°C) versus room temperature (R.T., from about 23°C to 26°C), and, in some cases, the presence or absence of added water. Examples 1 to 35 The following Table V records the additive, its acid strength (K d or K ld ), its pH as a 0.2N aqueous solution at 25°C, and bond strengths. n.a. = not applicable (or no available data); n.t. = not tested. Example 1 is a control. Examples 2 and 3 illustrate the use of conventional acids. Examples 4 to 35 illustrate novel compositions; the acids used in Examples 7 to 11 are structurally related to maleic acid, used in Example 4; the acids used in Examples 17 to 21 have varying chain lengths with respect to maleic acid; the acids and derivatives used in Examples 24 to 28 have structures somewhat related to maleic acid; the acids used in Examples 29 to 35 are soluble. Examples 36 to 45 In Examples 36 to 40, maleic acid, oxalic acid, malonic acid, mesaconic acid (K d /K 1d respectively 1.14 x 10⁻², 5.4 x 10⁻², 1.6 x 10⁻³, 8.2 x 10⁻⁴) and maleic acid monomethyl ester (pH 2.3 as a 0.2N aqueous solution at 25°C), respectively, were used in a composition of the type exemplified above. These five Examples were then repeated, in order, with the addition of 3% H₂O. The results (in kPa) are given in Table VI: Examples 46 to 48 Examples 46-48 illustrate the effectiveness of the preferred acid of the present invention (maleic) in adhesive formulations prepared from a variety of polymer types, individually and in combination. For these Examples, the following adhesive and activator solutions were prepared by rolling each of the polymers in their respective monomer solutions until dissolution was complete. The remaining additives were added and stirred or rolled until uniform mixtures were obtained. The maleic acid was added as an 11.2% ball-milled paste in MMA monomer, and the monomer level was adjusted to provide the proportions indicated. ADHESIVE A B C HYPALON 30 40 -- -- ABS moulding resin -- 25 -- VYNS resin -- -- 11 MMA monomer 59 74 88 DPESC -- 0.5 0.5 Cumene hydroperoxide 1.0 1.0 1.0 ACTIVATOR 1 2 ABS moulding resin 25 -- VYNS resin -- 10 MMA monomer 65 80 VANAX 808 10 10 Results are given, in kPa for bonds shimmed to provide a bond thickness of 1.27 mm, in Table VIII. The results in brackets are comparative, when using 10 parts methacrylic acid rather than 6.7 parts maleic acid: Example Solutions Polymers Compress 1 Compress 2 46 A + 1 CSPE/ABS 11070(4340) 18860(5580) 47 B + 1 ABS/ABS 13370(7240) 9830(6100) 48 C + 2 Vinyl/Vinyl 16550(2000) 7520(2030) Examples 49 to 58 Example 4 was repeated, but using different amounts of maleic acid in Examples 49 to 53. These five Examples were then repeated, in order, in Examples 54 to 58, with the addition of 3% H₂O. The results, in kPa, are given in Table IX: Example Maleic Acid (%) Compress 1 Compress 2 54(49) 0 1030(410) 3790(620) 55(50) 0.05 1240(550) 5170(760) 56(51) 0.5 2210(340) 14480(1720) 57(52) 6.7 28270(11030) 18270(9580) 58(53) 16.0 12760(12760) 18620(7240) Example 59 The following example describes the repair of a section of standard fiberglass (e.g., boat, auto, snowmobile, etc.) using the adhesive formulation of the present invention to improve the strength of the repair site. A. Adhesive/filler: The adhesive used for this repair situation was prepared by combining 60.2 pbw of 40% HYPALON 30 in MMA, 20.07 pbw methyl methacrylate, 0.25 pbw NAUGUARD SCC, 6.67 pbw of a 60% maleic acid/methyl methacrylate paste (prepared as in the General Experimental Procedure), 5 pbw methacrylic acid and 12.46 pbw ACRYLOID KM 452. These ingredients were mixed thoroughly in a Hochmeyer mixer until uniform and allowed to stand at room temperature for one day. Then the mixture was again mixed in the Hochmeyer mixer followed by the addition of 0.5 pbw of cumene hydroperoxide and additional mixing. Finally, 10 pbw P.Q. Corp. Q-Cell 600 hollow glass spheres having a mean particle size of 62 microns were added and the adhesive was mixed by hand until uniform. B. Activator: The activator for this repair system was prepared by combining 76.31 pbw methyl methacrylate, 10.41 pbw ACRYLOID KM 330, and 9.63 pbw STAUFFER SCC 1015. These materials were mixed with the Hochmeyer mixer and allowed to stand at room temperature for 1 day. To this solution was next added 10 pbw of VANAX 808 and 0.00003 pbw copper acetlyacetonate, followed by mixing in the Hochmeyer mixer. Finally, 10 pbw P.Q. Corp. Q-Cell 600 hollow glass spheres were added and the mixture was stirred by hand until uniform. C. Optional Primer: While a primer may not be necessary with this repair system, the following primer was prepared and used in this example. A solution of 3.85 pbw Union Carbide VYNS (vinyl resin) and 76.9 pbw methyl ethyl ketone (MEK) was prepared by rolling the ingredients in a glass jar for 1 day. To the resulting solution was added 19.23 pbw VANAX 808 and 0.000008 pbw copper aceteylacetonate. This solution was mixed by hand until uniform. D. Repair Procedure: The hole to be repaired was in a fiberglass auto fender and was approximately 75 mm in diameter. The surrounding 50 mm of fiberglass was sanded with No. 36 grit sandpaper using an air grinder. The area was then cleaned by wiping with a clean tissue soaked with isopropanol. A thin coat of primer was applied to the sanded area with a brush. Approximately 50 g of adhesive and 50 g of activator were mixed together by hand for one minute. A sufficient amount of this mixture was applied to one side of a 152 mm x 152 mm piece of 57 g fiberglass mat to give a uniform coat. This "patch" was placed over the hole in the fiberglass on the interior side of the fender. The remaining mixture was applied to the opposite side of the fiberglass mat, coating the back side of the patch. The patch was allowed to cure for 30 minutes at room temperature. Approximately 50 g of adhesive and 50 g of activator were then mixed and applied over the fiberglass mat from the exterior side of the fender. After 30 minutes cure, the excess adhesive from this side of the fender was removed with a rasp, followed by sanding the area with No. 36 grit sandpaper, then No. 100 grit sandpaper using an air grinder. The area was then boardsanded with No. 100 grit sandpaper. To fill in scratches and rough areas, a coat of polyester-styrene based feather fill was applied over the repaired area. After hardening, the excess material was removed with a rasp, followed by boardsanding and finally sanding with a dual action air sander with No. 220 grit sandpaper. A coat of solvent based grey primer surface was applied with an air spray gun. After drying, this was sanded with No. 200 and No. 400 grit sandpapers. The topcoat for this repaired fender consisted of four coats of SIKKENS black urethane paint applied with an air spray gun. After drying overnight the repaired area was buffed to give a very high gloss black finish with the repaired area being completely undetectable.

Claims: An adhesive composition which comprises: 10 to 75% by weight of a polymer-in-monomer solution, the monomer being an acrylic or methacrylic ester-based monomer and the polymer comprising (i) a sulfur-bearing component selected from chlorosulfonated polyethylenes and mixtures of sulfonyl chloride with a chlorinated polyethylene and (ii) a graft copolymer which is a polymer having a glass transition temperature substantially below 20°C to which is grafted a polymer having a glass transition temperature substantially above 25°C; up to 15% by weight of a polymerisation catalyst; and 0.1 to 20% by weight of a strong organic acid having a dissociation constant (K d ) of 0.01 to 1 and/or, as a 0.2 N aqueous solution, a pH of 1.3 to 2.0. A composition according to claim 1, wherein the sulfur-bearing component is a mixture containing from 3 to 160 mmoles sulfonyl chloride per 100 grams chlorinated polyethylene. A composition according to either preceding claim, wherein the chlorosulfonated polyethylene or the chlorinated polyethylene is obtainable from a polyethylene having a melt index of 4 to 500. A composition according to any preceding claim, wherein K d is 0.01 to 0.1. A composition according to claim 4, wherein the acid is maleic acid. A composition according to any preceding claim, which comprises 0.2 to 5% by weight of the polymerisation catalyst. A composition according to any preceding claim, which additionally comprises 0.01 to 10% by weight of an accelerator. A composition according to claim 7, which comprises 0.1 to 5% by weight of the accelerator. A method of bonding a plastics material to another material using an adhesive, wherein the adhesive is a composition according to any preceding claim.

Inventors: BRIGGS PAUL C, GOSIEWSKI DONALD E, BRIGGS, PAUL C., GOSIEWSKI, DONALD E.
Applicants: ILLINOIS TOOL WORKS, ILLINOIS TOOL WORKS INC.
Application year: 1987
Main classification: C09J151
IPC codes: C08F20, B29C65, C08L51, C09J4, C08L23, C08F255, C08F2, B32B7