Resin composition for use in electrodeposition paints

Abstract: A resin composition for use in cationic electro­ deposition paints, said composition comprising a cationic resin and a blocked polyisocyanate compound as a curing agent component, said blocked polyisocyanate compound containing per molecule one low-temperature dissociating blocked isocyanate group having a blocking agent dis­ sociating temperature of 60 to l20°C and at least one high-temperature dissociating blocked isocyanate group which dissociates the blocking agent at a temperature higher than said dissociating temperature by at least 40°C.

Description: This invention relates to a resin composition for use in cationic electrodeposition paints which comprises a blocked polyisocyanate compound as a curing agent component. More specifically, it relates to a resin composition for use in cationic electrodeposition paints which has markedly improved edge covering property without a deterioration in the smoothness, physical properties and chemical properties of coated films and in the stability of an electrodeposition bath prepared therefrom. A typical example of a conventional cationic electrodeposition paint is prepared by reacting an epoxy resin such as bispenol A-epichlorohydrin type epoxy resin with a basic amino compound, and neutralizing a mixture of the resulting cationic resin and an aromatic polyisocyanate compound (curing agent) blocked with an alcohol with a water-soluble acid, and dispersing the resulting neutralization product in water. When the aqueous dispersion is heated to, for example, 170°C in order to electrodeposit it and cure the coated film, the coated film melt-flows before the curing reaction takes place. Thus, a smooth coated film of a given thickness is formed in a planar part of the substrate. However, the melt-flowing coated film is drawn to the planar part owing to surface tension, and the coated film in the edge part becomes thin and is cured as such. The corrosion resistance of the edge part therefore becomes poor. In order to remedy this defect, a technique has previously been employed by which the flowability of the coated film under heat is reduced by increasing the pigment content, and the edge covering property is increased. This technique however has the defect that pigment settling tends to occur or the smoothness of the entire coated film is reduced. The present inventors have made extensive investigations on a method of increasing the corrosion resistance of the edge portions without impairing the smoothness of the coated film. These investigations have led to the unexpected discovery that by using as a curing agent a blocked polyisocyanate compound containing one blocked isocyanate group having a dissociation temperature of 80 to 120°C and at least one blocked isocyanate group having a dissociation temperature at least 40°C higher than said dissociation temperature per molecule, a thick coated film can be formed on the edge part of a substrate, the corrosion resistance of the edge part is improved, and the smoothness and other various properties of the coated film in the planar part and the stability of an electrodeposition bath comprising a resin composition containing the curing agent component are not deteriorated. This is presumably because as soon as the coated film flows under heat and is smoothened, the isocyanate groups from which the blocking agent has been dissociated at low temperatures react with the cationic resin to thicken the flowing coated film and prevent further flowing of the coated film and its thinning at the edge part; the blocked isocyanate groups having a high dissociation temperature are dissociated at higher temperatures, and the solvent effect of the dissociated blocking agent increases the uniformity of the coated film and finally, a cured coated film having excellent edge covering property and smoothness is obtained. WO-A-86/01 526 discloses cationic electrodeposition paints based on an amino and/or hydroxyl-containing synthetic resin which may be made water soluble by acid addition. It is disclosed that this resin contains a mixture of crosslinking agents. It is furthermore disclosed that the mixture of the crosslinking agents contains at least two crosslinking agents with different reactivities based on activated esters and/or with blocked polyisocyanate blocking agents. When the mixture comprising at least two blocked polyisocyanate compounds of WO-A-86/01 526 is used in the first stage of curing, the whole molecule of the low-temperature dissociating blocked polyisocyanate compound causes a crosslinking reaction with the substrate resin. The viscosity of the heat-melted film increases and therefore, the film obtained with the resin known has an inferior smoothness of the coated surface, the edge covering property is not sufficient, and the other properties of the film are also not satisfactory. EP-A-0 083 232 relates to aqueous coating compositions comprising film forming resin bearing reactive functionality and blocked polyisocyanate crosslinking agent. The blocked isocyanate crosslinking agent is prepared by reacting an organic diisocyanate with sufficient active hydrogen containing blocking agent and with dihydroxy functional amine containing at least one tertiary nitrogen. According to the known coating composition it is not possible to obtain a satisfactory edge covering property. In addition, the coating composition containing as a crosslinking agent a polyisocyanate compound blocked with a hydroxy functional amine as disclosed in EP-A-0 083 232 has the further disadvantage that gum, soot or the like accumulates in the inner walls of the coated film baking oven. EP-A-0 102 566 relates to an ungelled curable composition comprising an active hydrogen-containing material, a beta-hydroxy urethane and a cure catalyst. In particular, the beta-hydroxy urethane can be prepared by reacting an isocyanate compound or polymer with a combination of a 1,2-polyol and a conventional blocking agent. The coating composition is inferior in its edge covering properties, and the corrosion resistance of the coated film is low. According to this invention, there is provided a resin composition having excellent edge covering property for use in cationic electrodeposition paints, said composition comprising a cationic resin and a blocked polyisocyanate compound as a curing agent component, said blocked polyisocyanate compound containing per molecule one low-temperature dissociating blocked isocyanate group having a blocking agent dissociating temperature of 60 to 120°C and at least one high-temperature dissociating blocked isocyanate group which dissociates the blocking agent at a temperature higher than said dissociating temperature by at least 40°C, wherein the blocked polyisocyanate compound is a blocked polyisocyanate compound containing at least two isocyanate groups having different dissociating temperatures for the same blocking agent, and resulting from combination of a polyisocyanate compound containing aromatic isocyanate groups with a polyisocyanate compound containing aliphatic isocyanate groups through water or a polyol. The cationic resin in the resin composition of this invention which is to be cured with the above specific blocked isocyanate compound as a curing agent component may be a known resin of any desired type which has a cationic group and a functional group capable of reacting with the isocyanate (for example, a hydroxyl or amino group), can be coated by cationic electrodeposition, and forms a stable aqueous dispersion. Examples of the cationic resin that can be used in the invention are shown below. (i) The reaction product of a polyepoxy resin and a cationizing agent. (ii) A resin obtained by protonizing with an acid a polycondensate of a polycarboxylic acid and a polyamine (see U.S. Patent No. 2,450,940). (iii) A resin obtained by protonizing with an acid, a polyaddition product of a polyisocyanate, a polyol and a mono- or poly-amine. (iv) A resin obtained by protonizing with an acid a copolymer of a hydroxyl- and amino-containing acrylic or vinyl monomer (see Japanese Patent Publications Nos. 12395/1970 and 12396/1970). (v) A resin obtained by protonizing with an acid an adduct of a polycarboxylic acid resin and an alkylenimine (see U.S. Patent No. 3,403,088). Specific examples of these cationic resins and methods for production thereof are described, for example, in Japanese Patent Publications Nos. 12395/1970, 12396/1970 and 23087/1974, and U.S. Patents Nos. 2450940, 3403088, 3891529 and 3963663. A reaction product which may have remaining epoxy groups and is obtained by reacting a cationizing agent with the epoxy groups of a polyepoxide compound obtained from a polyphenol compound and an epihalohydrin such as epichlorohydrin is particularly desirable as the cationic resin in this invention in view of its excellent corrosion resistance. The polyepoxide compound is a compound containing at least two epoxy groups per molecule, and those which generally have a number average molecular weight of at least 200, preferably 400 to 4,000, more preferably 800 to 2,000, are suitable. Known epoxide compounds may be used. Examples include polyglycidyl ethers of polyphenols which can be produced by reacting polyphenols with epichlorohydrin in the presence of alkalies. Examples of the polyphenols include bis(4-hydroxyphenyl)-2,2-propane, 4,4'-dihydroxybenzophenone, bis(4-hydroxyphenyl)-1,1-ethane, bis-(4-hydroxyphenyl)-1,1-isobutane,bis(4-hydroxy-tert-butyl-phenyl)-2,2-propane, bis(2-hydroxynaphthyl)methane, 1,5-dihydroxynaphthalene, bis(2,4-dihydroxyphenyl)methane, tetra(4-hydroxyphenyl)-1,1,2,2-ethane,4,4'-dihydroxydiphenyl ether, 4,4'-dihydroxydiphenylsulfone, phenol novolac, and cresol novolac. Among the polyepoxide compounds described above, polyglcidyl ethers of polyphenols having a number average molecular weight of at least about 380, preferably about 800 to 2,000, and an epoxy equivalent of 190 to 2,000, preferably 400 to 1,000, are especially preferred for the production of the cationic resin. Above all, compounds of the following formula are preferred. The polyepoxide compounds may be partly reacted with, for example, polyols, polyether polyols, polyester polyols, polyamide amines, polycarboxylic acids and polyisocyanates, or may be grafted-copolymerized with, for example, epsilon-caprolactone or acrylic monomers. Examples of the cationizing agents to be reacted with the polyepoxide compounds are aliphatic, alicyclic or aromatic-aliphatic primary or secondary amines, tertiary amino salts, secondary sulfide salts and tertiary phosphine salts. They react with the epoxy groups to form cationic groups. The hydroxyl groups of an epoxy resin may be reacted with a tertiary amino monoisocyanate obtained by reacting a tertiary amino alcohol and a diisocyanate, to obtain cationic groups. Examples of the amino compounds in the cationizing agents above are shown below. (1) Primary amines such as methylamine, ethylamine, n- or iso-propylamine, monoethanolamine, and n- or iso-propanolamine. (2) Secondary amines such as diethylamine, diethanolamine, di-n- or iso-propanolamine, N-methylethanolamine and N-ethylethanolamine. (3) Polyamines such as ethylenediamine, diethylenetriamine, hydroxyethylaminoethylamine, ethylaminoethylamine, methylaminopropylamine, dimethylaminoethylamine and dimethylaminopropylamine. Among them, alkanolamines having a hydroxyl group are preferred. The primary amino groups may be blocked in advance by reaction with a ketone, and the remaining active hydrogens may be reacted with the epoxy groups. In addition to the amino compounds shown above, basic compounds such as ammonia, guanidine, hydroxylamine, hydrazine and hydroxyethylhydrazine may equally be used. Basic groups formed by using these compounds may be converted to cationic groups by protonization with acids, preferably water-soluble organic carboxylic acids such as formic acid, acetic acid and lactic acid. There can also be used tertiary amines such as triethylamine, triethanolamine, N,N-dimethylethanolamine, N-methyldiethanolamine, N,N-diethylethanolamine and N-ethyldiethanolamine. They may be protonized with acids (salt formation) in advance and may be quaternized together with the epoxy groups. Salts of sulfides such as diethylsulfide, diphenyl sulfide, tetramethylene sulfide and thiodiethanol with boric acid, carbonic acid or organic monocarboxylic acids may be reacted with the epoxy groups to form tertiary sulfonium salts. Salts of phosphines such as triethylphosphine, phenyldimethylphosphine, diphenylmethylphosphine and triphenylphosphine with the above acids may be reacted with the epoxy groups to form quaternary phosphonium salts. The hydroxyl group content of the cationic resin used in this invention, in terms of its hydroxyl value, is preferably about 10 to 400 in general, 20 to 200 in particular, in view of reactivity with the polyisocyanate compound. The content of the cationic groups is desirably one sufficient to disperse the cationic resin stably in water, and is preferably 5 to 100, particuarly 10 to 50, in terms of the number of KOH (mg/g solids). Even when the content of the cationic groups is less than 5, the cationic resin can be dispersed in water by using a surface-active agent. Desirably, the content of cationic groups is adjusted so that the pH of the aqueous dispersion of the composition has a pH of 4 to 9, preferably 6 to 7. Now, the blocked polyisocyanate compound (curing a gent) used in admixture with the cationic resin will be described. The polyisocyanate compound used in the production of the curing agent is a compound having at least two isocyanate groups per molecule. Preferred are those having 2 to 3 isocyante groups per molecule and a molecular weight of 150 to 600. Typical examples of the polyisocyanate groups include polyisocyanate compounds having aromatic isocyanate groups in which the isocyanate groups are directly bonded to an aromatic ring (e.g., a benzene ring), such as 2,4- or 2,6-tolylene diisocyanate and 4,4'-diphenylmethane diisocyanate; polyisocyanate compounds having aliphatic isocyanate groups in which the isocyanate groups are directly bonded to an aliphatic group, such as hexamethylene diisocyanate, dimeric acid diisocyanate, 1,4-dicyclohexylmethane diisocyanate, isophorone diisocyanate, m- or p-xylylene diisocyanate and lysine diisocyanate; and di- to tri-mers of these, water adducts of these, and diol or polyol adducts of these. Among these, 2,4- or 2,6-tolylene diisocyanate, 4,4'-diphenylmethane diisocyanate, and an adduct of one of these aromatic diisocyanates and isophorone diisocyanate with a diol or polyol are especially preferred in view of corrosion resistance. The blocked polyisocyanate compounds are obtained by blocking at least two isocyanate groups of the above polyisocyanate compounds with a blocking agent. When such blocked polyisocyanate compounds are heated at a temperature above a certain point, the blocking agent is dissociated to regenerate the isocyanate groups which then crosslink with the base resin. The blocked polyisocyanate compounds used in this invention are characterized by the fact that the dissociating temperatures of multiple blocking agents contained for each molecule partly differ from each other. The use of such a blocked polyisocyanate compound can markedly improve the edge covering property. Specifically, among blocking agents bonded to at least two isocyanate groups per molecule of the blocked polyisocyanate compound used in this invention, one blocking agent is dissociated at a low temperature region of about 80 to 120°C, preferably 90 to 110°C, and the remaining one or more blocking agent, at a temperature higher than the above temperature by at least 40°C, preferably 40 to 60°C. If the dissociation temperature of the blocking agent in the low-temperature region is lower than 80°C, a coated film having a high viscosity is formed before it melt-flows, and its smoothness is reduced. On the other hand, if the dissociating temperature of the blocking agent in the low-temperature region is higher than 120°C, a coated film having a low melt viscosity is formed, and its edge covering property is not sufficient. If the difference between the dissociation temperature in the low temperature region and the dissociation temperature in the higher temperature region is smaller than 40°C, the resulting coated film is liable to have poor smoothness or poor edge covering property, or both. The blocked polyisocyanate compounds in which the dissociation temperature of at least two blocking agents contained in each molecule differ at least partly can be easily obtained by using a polyisocyanate compound having at least two isocyanate groups having different dissociation temperatures for the same blocking agent. Examples of the blocking agent include oximes such as methylethyl ketoxime, acetoneoxime and cyclohexanone oxime, phenols such as phenol, nonylphenol and bis(4-hydroxyphenyl)-2,2-propane; lactams such as epsilon caprolactam, and active methylene compounds such as acetylacetone and diethyl malonate. Oximes are particularly suitable for blocking aromatic isocyanate groups. Oximes and phenols are preferred for blocking aliphatic isocyanate groups. In this method a polyisocyanate compound containing per molecule at least two isocyanate groups having different dissociation temperatures for the same blocking agent is used. Examples of such a polyisocyanate compound are compounds obtained by combining polyisocyanate compounds having aromatic isocyanate groups which have the property of dissociating blocking agents at relatively low temperatures, such as tolylene diisocyanate and 4,4'-diphenylmethane diisocyanate with polyisocyanate compounds having aliphatic diisocyanate groups having the property of dissociating blocking agents at relatively high temperatures, such as hexamethylene diisocyanate, isophorone diisocyanate and xylyene diisocyanate, via water or a polyol such as glycerol, trimethylolpropane, ethylene glycol, 1,2-propylene glycol and 1,2-butylene glycol (above all, polyisocyanate compounds obtained by combining 2,4-tolylene diisocyanate and isophorone diisocyanates having isocyanate groups with different reactivities in each molecule via 1,2-propylene glycol, 1,3-butylene glycol or 1,2-butylene glycol having at least two hydroxyl groups with different reactivities in each molecule), and blocking the isocyanate groups of the resulting isocyanate compounds with at least one blocking agent selected from oximes, lactams, active methylene compounds, etc. These blocked polyisocyanate compounds dissociate the blocking agents in the above-specified different temperature regions. In this case, the reaction of the polyisocyanate compound with the polyol may be carried out after the polyisocyanate compound is partially blocked with the blocking agent. In the method described above, the individual reactions for producing the blocked polyisocyanate compounds may be carried out at relatively low temperatures of from room temperature to about 150°C by using an inert solvent, a catalyst, etc. as required in accordance with known methods. The curing agent so produced has a molecular weight of usually 200 to 2,000, preferably 300 to 1,000. The amount of the curing agent to be mixed with the cationic resin may be varied depending upon the type of the cationic resin within a range from a minimum amount sufficient for the resulting coated film to self-cure or be cured under heat to a maximum amount which does not impair the stability of the final aqueous dispersion paint. Generally, the amount of the curing agent is preferably such that the equivalent of the blocked isocyanate groups in the curing agent is equal to, or larger than, the equivalent of the cationic groups in the cationic resin and is equal to, or smaller than, the total equivalent of functional groups containing active hydrogen. Part of the curing agent of this invention may be replaced by a conventional blocked polyisocyanate. The resin composition of this invention for use in cationic electrodeposition paints may be prepared by mixing the cationic resin with the curing agent (protonization of the cationic resin may be carried out after this mixing), dispersing the mixture stably in water, and as required, kneading the dispersion with a colored pigment such as carbon black, titanium white or red iron oxide, an extender pigment such as clay and talc, an anticorrosive pigment such as strontium chromate and lead chromate, or other additives. Examples of the other additives are dispersion aids (nonionic surfactants), crater preventing agents (e.g., acrylic resins, fluorine resins, and silicone resins), and curing accelerators (e.g., salts of metals such as lead, bismuth and tin). An electrodeposition bath may be prepared from the resin composition of this invention in accordance with a known method, and cationically electrodeposited on a suitable electrically conductive substrate. For example, the resin composition of this invention is adjusted with deionized water to a solids content of about 5 to about 40% by weight, and its pH is adjusted to 5.5 to 8.0. The electrodeposition paint thus prepared is coated usually at a bath temperature of 15 to 35°C and an applied voltage of 100 to 400 V on a metallic substrate as a cathode. The thickness of the electrodeposited film is not particularly restricted and can be varied widely depending upon the end use of the coated product, etc. Preferably, the thickness of the electrodeposited film formed in a planar part of the substrate is generally 10 to 40 microns, especially 15 to 35 microns, in the cured state. The suitable baking and curing temperature for the coated film is generally 80 to 220°C, preferably 140 to 180°C. The following examples illustrate the present invention more specifically. In these examples, all parts and percentages are by weight. The edge covering property of the electrodepositing composition obtained in these examples was measured by the following method. Method of testing edge covering property A zinc phosphate-treated blade OLFA cutter (OLFA LB-10; length 10 cm; width 1.8 cm; angle of blade edge 22°; a product of OLFA Co., Ltd.) was coated by electrodeposition, and then subjected to a salt spray test in accordance with JIS Z-2871. The coated film on the blade was observed under a magnifying glass and the number of rusts and blisters was measured. The edge covering property was evaluated by this number. EXAMPLE 174 Parts of 2,4-tolylene diisocyanate was dissolved in 52 parts of methyl isobutyl ketone, and 87 parts of methyl ethyl ketoxime was added dropwise at 30°C to give half-blocked tolylene diisocyanate having an isocyanate value of 241 and a solids content of 83%. Then, 222 parts of isophorone diisocyanate was dissolved in 62 parts of methyl isobutyl ketone, and 87 parts of methyl ethyl ketoxime was added dropwise at 30°C to obtain half-blocked isophorone diisocyanate having an isocyanate value of 136. 76 Parts of 1,2-propylene glycol was added to it, and the mixture was heated to 120°C and maintained for 4 hours. After its isocyanate value reached 0, 313 parts of the half-blocked tolylene diisocyanate was added. The mixure was maintained at 120°C for 5 hours, and it was determined that its isocyanate value reached 0. As a result, a curing agent having a solids content of 85% was obtained in which the blocking agents had a dissociation temperature in the presence of a catalsyt of about 100°C and about 140°C. 1900 Parts of bisphenol A-type epoxy resin having an epoxy equivalent of 950 (tradename "Epikote 1004", a product of Shell Chemical Co.) was dissolved in 1012 parts of butyl Cellosolve, and 124 parts of diethylamine was added dropwise at 80 to 100°C. The mixture was maintained at 120°C for 2 hours to give an epoxy resin-amine adduct having an amine value of 47. Then, 1000 parts of a dimeric acid-type polyamide resin having an amine value of 100 (tradename Versamide 460 made by Henkel Hakusui Co., Ltd.) was dissolved in 429 parts of methyl isobutyl ketone. The solution was refluxed at 130 to 150°C, and water generated was evaporated to ketiminize the terminal amino groups of the amide resin. The product was maintained at 150°C for about 3 hours, and after evaporation of water ceased, cooled to 60°C. The product was added to the epoxy resin-amine adduct obtained as above. The mixture was heated to 100°C, maintained for 1 hour at this temperature, and cooled to room temperature to give an epoxy resin/amine/polyamide adduct resin having a solids content of 68% and an amine value of 65. Acetic acid (1.5 parts) was added to 100 parts of the resulting resin to neutralize it and thus obtain a cationic resin. The above curing agent (18 parts) and 3 parts of dibutyltin dilaurate were added to 101.5 parts of the cationic resin. With sufficient stirring, 294 parts of deionized water was added to prepare an electrodeposition bath having a solids content of about 20% and a pH of 6.7. Electrodeposition was carried out from the electrodeposition bath at 30°C and 200 V for 3 minutes. The resulting coated film was baked at 180°C. for 30 minutes to give a coated film having a thickness of 22 microns and a pencil hardness of 5H. The surface smoothness of the coated film was fairly good, and its edge covering property was very good (the number of rusts and blisters was 4). COMPARATIVE EXAMPLE 1 174 Parts of 2,4-/2,6-tolylene diisocyanate (80/20 wt.%) was dissolved in 87 parts of methyl isobutyl ketone, and 260 parts of 2-ethylhexyl alcohol was added at 30°C. The mixture was then maintained at 120°C for 5 hours. It was determined that the isocyanate value of the product was 0. As a result, a curing agent having a blocking agent dissociation temperature in the presence of a catalyst of about 160°C. was obtained. The resulting curing agent (26 parts) and 3 parts of dibutyltin dilaurate were added to 101.5 parts of the cationic resin obtained in Example 1. With sufficient stirring, 317 parts of deionized water was added to prepare an electrodeposition bath having a solids content of about 20% and a pH of 6.7. Elecrodeposition was carried out from the electrodeposition bath on a zinc phosphate-treated steel sheet as a cathode at 30°C and 200 V for 3 minutes The resulting coated film was baked at 180°C. for 30 minutes to give a coated film having a thickness of 21 microns and a pencil hardnesss of 5H. The surface smoothness of the coated film was good, but its edge covering property was very poor (the number of rusts and blisters was 45). COMPARATIVE EXAMPLE 2 174 Parts of a mixture of 2,4-/2,6-tolylene diisocyanates (80/20 % by weight) was dissolved in 174 parts of butyl acetate, and 174 parts of methyl ethyl ketoxime was added dropwise at 30 to 40°C. After the addition, the mixture was heated to 60°C to decrease the isocyanate value to 0. The resulting curing agent (37.5 parts) was mixed with 130 parts of the same cationic resin as used in Example 3, and electrodeposition bath as prepared in accordance with the same formulation as in Example 3. Electrodeposition was carried out from the electrodeposition bath as in Example 3, and the coated film was baked at 150°C for 30 minutes to prepare a test panel for evaluating edge covering property. The coated film had very good edge covering property (the number of rusts and blisters was 1) but very inferior surface smoothness, and showed a non-lustrous rough appearance.

Claims: A resin composition for use in cationic electrodeposition paints, said composition comprising a cationic resin and a blocked polyisocyanate compound as a curing agent component, said blocked polyisocyanate compound containing per molecule one low-temperature dissociating blocked isocyanate group having a blocking agent dissociating temperature of 60 to 120°C and at least one high-temperature dissociating blocked isocyanate group which dissociates the blocking agent at a temperature higher than said dissociating temperature by at least 40°C, wherein the blocked polyisocyanate compound is a blocked polyisocyanate compound containing at least two isocyanate groups having different dissociating temperatures for the same blocking agent, and resulting from combination of a polyisocyanate compound containing aromatic isocyanate groups with a polyisocyanate compound containing aliphatic isocyanate groups through water or a polyol. The composition of claim 1 wherein the blocking agent in the low-temperature dissociating blocked isocyanate group has a dissociation temperature of 90 to 110°C. The composition of claims 1 or 2 wherein the dissociation temperature of the high-temperature dissociating blocked isocyanate group is 40 to 60°C higher than the dissociating temperature of the low-temperature dissociating blocked isocyanate group. The composition of any one of claims 1 to 3 wherein that blocking agent is selected from oximes, phenols and lactams. The composition of any one of claims 1 to 4 wherein the blocked polyisocyanate compound has a molecular weight of 200 to 2,000. The composition of any one of claims 1 to 5 wherein the cationic resin is a resin obtained by reacting a cationizing agent with the epoxy groups of a polyepoxide compound prepared from a polyphenol compound and an epihalohydrin. The composition of claim 6 wherein the polyepoxide compound is a polyglycidyl ether of a polyphenol which has an average molecular weight of at least about 380 and an epoxy equivalent of 190 to 2,000. The composition of any one of claims 1 to 7 wherein the cationic resin has a hydroxyl value of about 10 to 400. An electrodeposition coating bath comprising the resin composition of any one of claims 1 to 8.

Inventors: NISHIDA REIZIRO C O GIJUTSUHON, TOMINAGA AKIRA C O GIJUTSUHONB, NISHIDA, REIZIRO C/O GIJUTSUHONBU OF, TOMINAGA, AKIRA C/O GIJUTSUHONBU OF
Applicants: KANSAI PAINT CO LTD, KANSAI PAINT CO. LTD.
Application year: 1987
Main classification: C09D5
IPC codes: C09D5, C08G18, C09D163