MATERIAL FOR OXYGEN-PERMEABLE HARD CONTACT LENS WITH EXCELLENT IMPACT RESISTANCE

Abstract: Material comprises a copolymer and a siloxane oligomer. The copolymer is made from at least one monomer component, selected from fluorine-contg. (meth)acrylate and silicone-contg. (meth) acrylate. The siloxane oligomer has polymerisable functional gps. at its molecular ends and is selected from cpds. of formulae (I) -(III). In the formulae, 1 is an integer between 10 and 200; the sum m1+m2 is an integer between 12 and 140 (m1 is at least 0, m2 is at least 1); n is an integer between 10 and 500; R1 is of formula (a) or (b). R2 is H or CH3; Ph is a phenyl group; R3 is -CH2-CH2-CH3-O-C(O)-C(R2)=CH2.

Description: The present invention relates to an oxygen-permeable hard contact lens material with excellent impact resistance and more particularly to an oxygen-permeable hard contact lens material with excellent impact resistance characterized by using a siloxane oligomer having a polymerizable functional group at the molecule terminals. In recent years, hard contact lenses use a material of higher oxygen permeability than conventional PMMA (polymethyl methacrylate) materials and these hard contact lenses have wide acceptance in the market as an oxygen-permeable hard contact lens. Because of their excellent oxygen permeability, these oxygen-permeable hard contact lenses permit oxygen supply from the atmosphere to the cornea, have a low risk of causing cacochymia of the cornea, and accordingly have relatively high safety. Further, unlike soft contact lenses made of a material containing a large amount of water, the oxygen-permeable hard contact lenses have good stabilities in dimension, shape, etc., are unlikely to be contaminated with bacteria, etc., allow easy handling, and accordingly can be said to be a lens of high safety. As the materials for the oxygen-permeable hard contact lenses, there have conventionally been proposed various materials, for example, cellulose derivatives [e.g. CAB (cellulose acetate butyrate)], copolymers of a silicone-containing (meth)acrylate and an alkyl (meth)acrylate, styrene derivatives, and copolymers of a fluorine-containing (meth)acrylate and an alkyl (meth)acrylate. In recent years, copolymers composed mainly of a silicon-containing (meth)acrylate or a fluorine-containing (meth)acrylate have been proposed and, because of their very high oxygen permeability, are gaining increasing acceptance in the market. An oxygen-permeable hard contact lens produced by polymerizing 30 to 50 wt% of an alkyl (meth)acrylate, 10 to 40 wt.% of a fluorine-containing monomer, 10 to 35 wt.% of a silicone-containing monomer, 5 to 15 wt.% of an unsaturated carboxylic acid and 0.15 to 15% of a di or tri (meth)acrylate of a dihydric or higher hydric alcohol is disclosed in United States Patent No. 4 540 761. However, a contact lens material with high oxygen permeability made by using an increased amount of such a silicone-containing or fluorine-containing (meth)acrylate as a component for increasing oxygen permeability has reduced mechanical properties and is insufficient Particularly in processability and impact resistance. Meanwhile, a contact lens material with improved processability, mechanical strength and impact resistance, made by appropriately selecting an alkyl (meth)acrylate has low oxygen permeability. European Patent Application No. 30807 discloses a water absorbing material, for use as a soft contact lens, derived from a siloxane oligomer, having hydrophilic sidechains and terminal unsaturation, and certain comonomers, for example, low esters of acrylic and methacrylic acid. Nonetheless, at present there has not yet been developed any hard contact lens material having high oxygen permeability and a good balance in various properties such as mechanical properties, processability, dimensional stability, wettability by water and optical properties. As the oxygen permeability of contact lens is enhanced, the brittleness of the lens increases and the lens tends to be broken even by a small impact. This is a serious problem in the practical application of contact lenses. In view of the above-mentioned problems of the conventional oxygen-permeable hard contact lens materials, the present inventors have made extensive research and, as a result, have completed the present invention. Therefore, an object of the present invention is to provide an oxygen-permeable hard contact lens material with excellent impact resistance, more particularly an oxygen-permeable hard contact lens material with excellent impact resistance characterized by using a siloxane oligomer having certain terminal polymerizable functional groups. Another object of the present invention is to provide a hard contact lens material which has high oxygen permeability, is difficult to break and can be used over a long period of time. Other objects and advantages of the present invention will become apparent from the following description. The oxygen-permeable hard contact lens material according to the present invention substantially comprises a copolymer obtainable by copolymerizing a monomer mixture mainly composed of a fluorine-containing (meth)acrylate, a silicone-containing (meth)acrylate, and at least one siloxane oligomer represented by any of the formulae (I) to (III): [ℓ is an integer of 10-200, and R₁ is or (R₂ is H or a methyl group)] [(m₁+m₂) is an integer of 12-140, and m₁ ≧ O and m₂ ≧ 1; Ph is a phenyl group; and R₁ is same as R₁ of the formula (I)]. [n is an integer of 10-500, and R₃ is (R₂ is H or a methyl group)]. The siloxane oligomers used in the present invention can provide the copolymer of the present invention with remarkably improved impact resistance. The molecular weights of the siloxane oligomers are preferably 1,000 to 6,000. The IPDI (isophorone diisocyanate) type oligomers of the formula (I) or (II) [R₁ is (b)] are most preferable because they can provide the copolymer with a striking improvement in impact resistance. The preferable range of the amount used of the siloxane oligomer may vary depending upon, for example, the type and amount of the monomer component used for the improvement of oxygen permeability but is usually 0.1-15% by weight in the copolymer. When the content of the siloxane oligomer in the copolymer exceeds 15% by weight, the resulting copolymer easily undergoes plastic deformation. When the content is less than 0.1% by weight, it is difficult to obtain improved impact resistance. The content of the siloxane oligomer is particularly preferably 1-7% by weight in view of its compatibility with other components, the handleability and the effect of improvement of impact resistance. The main monomer component of the material of the present invention is at least one monomer selected from fluorine-containing (meth)acrylates and at least one monomer selected from silicone-containing (meth)acrylates. As the fluorine-containing (meth)acrylates, there can be preferably used, for example, fluorine-containing C₂-C₁₂ alkyl esters of (meth)acrylic acid such as 2,2,2-trifluoroethyl (meth)acrylate, 2,2,2,2',2',2'-hexafluoroisopropyl (meth)acrylate, 2,2,3,3,4,4,4-heptafluorobutyl (meth)acrylate, 2,2,3,3,4,4,-5,5,6,6,7,7,8,8,8-pentadecafluorooctyl (meth)acrylate, 2,2,3,3,4,4,5,5,6,6,7,7,8,8,9,9-hexadecafluorononyl (meth)acrylate and the like. Preferable examples of the silicone-containing (meth)acrylates are siloxanylalkyl (meth)acrylates such as pentamethyldisiloxanylmethyl (meth)acrylate, tris(trimethylsiloxy)silylpropyl (meth)acrylate, 3-methacryloxypropyl-tris(vinylmethylsiloxy)silane, trimethylsilyl (meth)acrylate, phenyldimethylsilylmethyl (meth)acrylate, bis(methacryloxypropyl)tetramethyldisiloxane, 1,3-bis(methacryloxypropyl)-tetrakis(trimethylsiloxy)-disiloxane and the like. The fluorine-containing (meth)acrylate and the silicone-containing (meth)acrylate can provide the copolymer with high oxygen permeability and are essential components in the present invention. The oxygen permeability of the copolymer can be controlled by changing the amount ratio of the two compounds. The total amount used of fluorine-containing (meth)acrylate monomers and silicone-containing (meth)acrylate monomers is preferably 25-90% by weight in the copolymer, in usual cases. In the present invention, it is preferred that a hydrophilic monomer and/or a crosslinkable monomer be used together with the fluorine-containing (meth)acrylate and the silicone-containing (meth)acrylate. As the hydrophilic monomer, there can be mentioned hydroxyl group-containing (meth)acrylates such as 2-hydroxyethyl (meth)acrylate, 2-hydroxypropyl (meth)acrylate, 2-hydroxybutyl (meth)acrylate and the like; unsaturated carboxylic acids such as acrylic acid, methacrylic acid, itaconic acid, fumaric acid, maleic acid, cinnamic acid and the like; (meth)acrylamides such as acrylamide, methacrylamide, dimethylacrylamide, diethylacrylamide and the like; vinylpyrldine; vinylpyrrolidone; so forth. The hydrophilic monomer as a comonomer can provide the copolymer with wettability by water, whereby the resulting contact lens can have increased affinity with lacrima and provide lens users with better feeling of lens wearing. Of the above compounds, the unsaturated carboxylic acids are particularly preferable because they provide the copolymer with remarkably improved hardness and wettability by water. The amount used of the hydrophilic monomer is usually 2-30% by weight, preferably 5-15% by weight in the copolymer. As the crosslinkable monomer, there can be mentioned alkylene glycol di(meth)acrylates such as ethylene glycol di(meth)acrylate, diethylene glycol di(meth)acrylate and the like, as well as monomers of at least bifunctionality such as trimethylolpropane tri(meth)acrylate, pentaerythritol tetra- or tri(meth)acrylate and the like. The crosslinkable monomer can provide the copolymer with improved hardness. The amount used of the crosslinkable monomer is usually 0.1-15% by weight, preferably 2-5% by weight in the copolymer. In producing an oxygen-permeable hard contact lens material with excellent impact resistance of the present invention, preferably 0.1-15% by weight of a siloxane oligomer having a polymerizable functional group at the molecule terminals is mixed with preferably 85-99.9% by weight of a fluorine-containing (meth)acrylate and a silicone-containing meth)acrylate, preferably their mixture with a hydrophilic monomer and a crosslinkable monomer; thereto is added a polymerization initiator such as azobisisotyronitrile, azobisdimethylvaleronitrile, benzoyl peroxide, lauroyl peroxide or the like in an amount of preferably 0.05-1% by weight, and they are mixed; the resulting mixture is poured into a casting container made of a metal, plastic or glass; the container is tightly sealed and placed in a water bath or an electric oven to thermally polymerize the contents in the container; thereby an oxygen-permeable hard contact lens material with excellent impact resistance can be obtained in a rod or button shape. If necessary, an ultraviolet absorber and/or a coloring agent usually used may be added. The polymerization may also be conducted by ultraviolet polymerization, etc. It is also possible to conduct the polymerization in a mold capable of forming a lens shape. The thus-produced material of the present invention having a rod or button shape can be made into a hard contact lens according to usual lathe-cutting and polishing. The present invention is explained by referring to the following Examples. The siloxane oligomer having a polymerizable functional group at the molecule terminals, used in the present invention can be used not only in highly oxygen-permeable hard contact lens materials mainly composed of a fluorine-containing (meth)acrylate and a silicone-containing (meth)acrylate, shown in the Examples of the present invention, but also in other oxygen-permeable hard contact lens materials to provide them with improved impact resistance. Example 1 Into a cylindrical polyethlene tube was injected a fluid consisting of 7 parts by weight of a siloxane oligomer [an oligomer of the formula (I), R₁ = (b), R₂ = H, 1 = 13], 43 parts by weight of 2,2,2-trifluoroethyl methacrylate, 43 parts by weight of tris(trimethylsiloxy)silylpropyl methacrylate, 5 parts by weight of methacrylic acid, 2 parts by weight of ethylene glycol dimethacrylate and 0.25 part by weight of azobisisobutyronitrile. The tube was tightly sealed and then heated. The heating conditions were 96 hours in a constant temperature water bath of 42°C, gradual temperature elevation to 90°C in 26 hours in an electric oven, and 10 hours at 90°C in the oven. After the completion of the polymerization, the tube was cooled to room temperature to obtain a copolymer of rod shape. This copolymer was cut and ground to produce a disc of 0.2 mm in thickness. The disc was measured for oxygen permeability constant at 35°C using a Seikaken type film oxygen permeability tester. The disc had an oxygen permeability coefficient of 55x10⁻¹¹ ml(STP).cm²/cm³.sec.mmHg. A disc of 0.5 mm in thickness was also produced in a similar manner. The disc was measured for impact resistance based on a swing angle of a striker caused by sample breakage, using a striker type impact tester manufactured by HOYA CORP (the tester for examing the impact resistance of hard contact lens, consisting mainly of a rotary bearing capable of rotating only in one direction, a striker fixed to the rotary bearing and also functioning as a pointer, a dial plate for measuring the angle of swing of the striker and a test piece holder fixed to a table movable in lengthwise, widthwise and vertical directions and also to a pedestal. See Japanese Utility Model Application No. 150022/1986). The disc had an impact resistance of 55°. Incidentally, an impact resistance of smaller angle indicates that the sample has higher impact resistance. The above rod material was cut and ground in a usual manner to produce a hard contact lens. The lathe-cutting property and polishability were good and the lens had good wettability by water and gave good feeling when worn. Comparative Example 1 43 parts by weight of 2,2,2-trifluoroethyl methacrylate, 43 parts by weight of tris(trimethylsiloxy)-silylpropyl methacrylate, 9 parts by weight of methacrylic acid and 5 parts by weight of ethylene glycol dimethacrylate were polymerized in the same manner as in Example 1, and the copolymer obtained was measured for properties. The oxygen permeability coefficient was 52x11⁻¹¹ ml (STP).cm²/cm³.sec.mmHg, which was about equal to that of Example 1. The impact resistance (swing angle) was 72° and apparently inferior to that of the copolymer of Example 1 which used a siloxane oligomer. Examples 2-13 and Comparative Examples 2-4 Using various monomers and various siloxane oligomers in combination, various copolymers were produced in the same manner as in Example 1. They were measured for oxygen permeability and impact resistance. The results are shown in Table 1. As is clear from Table 1, the addition of a siloxane oligomer could provide the resulting copolymer with improved impact resistance. Industrial Applicability As described above, the oxygen-permeable hard contact lens material of the present invention obtained by adding a siloxane oligomer to an oxygen-permeable hard contact lens material composed mainly of a silicone-containing (meth)acrylate and a fluorine-containing (meth)acrylate possesses remarkably improved impact resistance. Hard contact lenses produced from the material of the present invention are less likely to break than conventional oxygen-permeable hard contact lenses which break relatively easily during handling, and accordingly have higher safety and higher economical value.

Claims: An oxygen-permeable hard contact lens material substantially comprising a copolymer obtainable by copolymerizing a monomer mixture mainly composed of a fluorine-containing (meth)acrylate, a silicone-containing (meth)acrylate, and at least one siloxane oligomer represented by any of the formulae (I) to (III): [ℓ is an integer of 10-200, and R₁ is or (R₂ is H or a methyl group)] [(m₁+m₂) is an integer of 12-140, and m₁ ≧ O and m₂ ≧ 1; Ph is a phenyl group; and R₁ is same as R₁ of the formula (I)]. [n is an integer of 10-500, and R₃ is (R₂ is H or a methyl group)]. A material as claimed in claim 1, wherein the siloxane oligomer has a molecular weight of 1,000 to 6,000. A material as claimed in claim 1 or claim 2, wherein the copolymer is obtainable by polymerizing a monomer mixture further comprising a hydrophilic monomer and/or a crosslinkable monomer. A material as claimed in any one of claims 1 to 3, wherein the copolymer is obtainable by polymerizing a monomer mixture comprising 0.1-15% by weight of the siloxane oligomer. A material as claimed in any one of claims 1 to 4, wherein the fluorine-containing (meth)acrylate is a fluorine-containing C₂-C₁₂ alkyl ester of (meth)acrylic acid. A material as claimed in any one of claims 1 to 5, wherein the silicone-containing (meth)acrylate is a siloxanylalkyl (meth)acrylate. An oxygen-permeable hard contact lens made from a material as claimed in any one of claims 1 to 6. The use of a copolymer as specified in any one of claims 1 to 6 in the manufacture of an oxygen-permeable hard contact lens.

Inventors: ONOZUKA SHIGEHARU, TSUCHIYA MAKOTO, YOKOYAMA YUUICHI, ONOZUKA, SHIGEHARU, TSUCHIYA, MAKOTO, YOKOYAMA, YUUICHI
Applicants: HOYA CORP, HOYA CORPORATION
Application year: 1987
Main classification: G02C7
IPC codes: G02C7, C08F299, G02B1, C08F230, C08F30, C08F290, C08F220, C08F20