Process for preparation of mannich reaction products from oxidized polymers, the obtained products, their use and lubricating oil compositions containing the same

Abstract: A process for the preparation of oil-soluble Mannich con­ densation products wherein an amine is prereacted with a sulfonic acid or ammonium sulfonate, oleic acid, and an oxi­ dized olefin polymer and the prereaction product is reacted with an aldehyde. The reaction products can be used as addi­ tives particularly as dispersant-viscosity index improvers of lubricating oils.

Description: Field Of This Invention The field of this invention relates to lubricating oil compositions. More particularly, this invention relates to a lubricating oil composition containing an improved dispersant-viscosity index improver and to the process for preparing the improved dispersant-viscosity index improver. Even more particularly, this invention relates to a process for preparing oil-soluble Mannich condensation products from oxidized olefin polymers, amines and aldehydes wherein the amine is prereacted with a sulfonic acid or ammonium sulfonate in the presence of said oxidized olefin polymers and oleic acid wherein the mole ratio of oleic acid to amine is in the range of from 0.025 to 10.0, preferably from 0.05 to 1.0, and the prereaction product is reacted with an aldehyde to form the Mannich condensation product. Description Of The Prior Art Lubricant deterioration caused by the operation of diesel and spark ignition internal combustion engines results in the formation of sludge, lacquer and resinous deposits on interior surfaces of the engines. This foreign matter accelerates wear and reduces engine efficiency. In order to prevent or reduce the formation of these deposits, a wide variety of lubricating oil additives have been developed which have dispersancy and detergency properties. These additives have the ability to keep deposit-forming materials suspended in the oil so that the engine remains in a clean and efficient operating condition. It is well known that lubricating oils become thin at elevated temperatures while thickening at low temperatures. Generally certain additives improve lubricant oil temperature viscosity relationships. In the case of crankcase lubricants, the oil must not become so thick when cold that the engine is prevented from operation. At the same time, when the engine has heated up in operation, the oil must remain sufficiently viscous to maintain oil films for lubrication of moving parts. Various additives provide both detergent and viscosity index improvement to lubricants. Culbertson et al., U.S. Pat. No. 3,872,019, issued March 18, 1975, discloses and claims bifunctional lubricant additives exhibiting both dispersant and viscosity index improving properties obtained by the Mannich condensation of an oxidized long chain, high molecular weight amorphous copolymer of essentially ethylene and propylene having a number average molecular weight of at least about 10,000 and at least 140 pendant methyl groups per 1,000 chain carbon atoms with a formaldehyde yielding reactant and a primary or secondary amine or polyamine, said reactants being employed in the molar ratio of from about 1:2:2 to about 1:20:20, respectively. West, U.S. Pat. No. 4,131,553, issued December 26. 1978, discloses and claims a process for preparing a dispersant-viscosity index improver comprising products of the Mannich condensation reaction of oxidized olefinic polymers. The Mannich reaction is carried out in the presence of an oil soluble sulfonic acid. The sulfonic acid catalyzes the reaction, increases the resistance of the Mannich modified oxidized polymer to oxidation and varnish formation, increases the detergent-dispersing properties of the viscosity index improver, does not appreciably harm the color of the product and increases the performance of the additive in engine tests. Schaffhauser et al., U.S. Pat. No. 4,444,956, issued April 24, 1984, teaches and claims a process for the preparation of oil-soluble Mannich condensation products wherein an amine is reacted with a sulfur-containing compound selected from the group consisting of oil-soluble sulfonic acids and their ammonium salts, and reacting the product thereof with formaldehyde and an oxidized polymer derived from an amorphous olefin polymer. It has been found that dispersant viscosity index improvers prepared as Mannich condensation products upon storage at elevated temperatures develop a haze condition wherein clarity of the product is significantly decreased to a degree wherein marketability and customer acceptance of the product is affected. Accordingly, it is an object of this invention to provide a new process for the preparation of oil-soluble Mannich condensation products. Another object of this invention is to provide an improved process for the preparation of oil-soluble Mannich condensation products. A still further object of this invention is to provide an oil-soluble Mannich condensation product having reduced haze and sediment. Summary Of The Invention The present invention is directed to a process for the preparation of oil-soluble condensation product which comprises: (a) reacting at least one amine selected from the group consisting of primary and secondary aliphatic amines having from 1 to 24 carbon atoms, aliphatic diamines of the formula H₂N(CH₂) x NH₂ wherein x is an integer from 3 to 10, and polyamines of the formula H₂N(A--NH) y H wherein. A is a divalent alkylene radical of from 2 to 6 carbon atoms and y is an integer from 1 to 10, with at least one sulfur-containing material selected from the group consisting of oil-soluble sulfonic acids and their ammonium salts, and oleic acid wherein the ratio of mole equivalents of said sulfur-containing material to mole equivalents of said amine is from about 0.05 to 10; and ratio of mole equivalents of said oleic acid to equivalents of said amine is from about 0.025 to 10; and an oxidized polymer wherein said oxidized polymer is derived from an amorphous olefin polymer, being an amorphous addition polymer derived from olefinically unsaturated hydrocarbon monomers or mixtures thereof, and has a number average molecular weight of at least 3,000 and (b) reacting the product of (a) with formaldehyde or a formaldehyde-yielding reagent, (c) recovering the oil-soluble condensation product which has a viscosity increase of from 17.2 x 10⁻³ to 365 x 10⁻³ Pa·s (100 to 2,000 Saybolt Universal Seconds) at 100°C over the viscosity of said oxidized polymer. The oil-soluble Mannich-condensation products prepared thereby have reduced haze and sediment. Furthermore, this invention refers to the use of the oil-soluble condensation products as additives for lubricant oils and as a dispersant-viscosity index improver, as well as to lubricating oil compositions containing the same. Details Of The Invention We have found that oil-soluble Mannich condensation products prepared in accordance with this invention possess excellent dispersancy and viscosity improving properties when incorporated into lubricating oils. In addition, the Mannich products of this invention also possess improved filterability and reduced haze or sediment in comparison with prior art products. In particular, the subject invention is an improvement in the process which is disclosed by the above-mentioned U.S. Pat. No. 4,444,956 to Schaffhauser et al., which, in turn, is an improvement in the process which is disclosed in the above mentioned U.S. Pat. No. 4,131,553 to West. As used herein, the terminology "amorphous olefin polymer" refers to amorphous addition polymers derived from olefinically unsaturated hydrocarbon monomers or mixtures thereof. Such olefin monomers include olefins of the formula R-CH=CH₂ wherein R is selected from the group consisting of hydrogen and aliphatic groups of from 1 to 20 carbon atoms. Suitable olefin monomers include, but are not limited to, ethylene, propylene, isobutylene, 1-butene, 1-hexene, and 4-methyl-1-pentene. Olefin monomers having a plurality of double bonds and containing from 4 to 25 carbon atoms can also be used. Suitable monomers containing a plurality of double bonds include, for example, 1,3-butadiene, 1,4-hexadiene, 1,4-pentadiene, 2-methyl-1,5-hexadiene, 1,7-octadiene, 5-methylene-2-norbornene and norbornadiene. Preferred amorphous olefin polymers are derived from 30 to 80 mole percent ethylene and from 20 to 70 mole percent of at least one comonomer selected from the group consisting of olefins of the formula R-CH=CH₂ wherein R is an aliphatic group of from 1 to 20 carbon atoms and diolefins of from 4 to 25 carbon atoms. Highly preferred amorphous olefin polymers include ethylene-propylene copolymers which are derived from 35 to 80 and preferably from 55 to 65 mole percent of ethylene, and from 20 to 65 and preferably from 35 to 45 mole percent of propylene. These ethylene-propylene copolymers have a number average molecular weight in the range of from 5,000 to 200,000, preferably from 20,000 to 70,000, and contain at least 100 pendant methyl groups per 1,000 chain carbon atoms. Methods for the preparation of the amorphous olefin polymers are well known. For example, methods for the preparation of such polymers are described in U.S. Pat. Nos. 2,700,633; 2,726,231; 2,933,480; 3,000,866; 3,063,973; 3,093,621; and 3,872,019. The amorphous olefin polymer must be oxidized prior to use in the process of this invention. The oxidation can be accomplished by contacting the polymer at a suitable temperature and pressure with an oxidizing agent such as air, free oxygen or any oxygen-containing material which is capable of releasing oxygen under the oxidation conditions selected. If desired, the oxidation can be conducted in the presence of known oxidation catalysts, such as platinum or a platinum group metal and compounds containing metals such as copper, iron, cobalt, cadmium, manganese, and vanadium. The oxidation can be carried out, for example, by the methods which are described in U.S. Pat. Nos. 2,982,728; 3,153,025; 3,316,177; 3,365,499; 3,544,520 and 4,011,380. Depending on the activity of the specific oxidizing agent and the rate of reaction desired, the oxidation of the olefin polymer can be carried out over a wide temperature range. With an active oxidizing agent such as sulfur trioxide, temperatures in the range of from -40° to 200°C. can be used. On the other hand, with less active oxidizing agents such as air, temperatures in the range of from 40° to 430°C. can be used. The amorphous olefin polymer is desirably dissolved in oil prior to the oxidation in order to provide a reaction mixture of convenient viscosity. Reaction parameters such as temperature, pressure, oxidizing agent, concentration of oxidizing agent, and oxidation catalyst, if any, are selected and controlled in a conventional manner to obtain optimum results. The oxidized olefin polymer for use in the process of this invention desirably has a number average molecular weight of at least 3,000, preferably from 10,000 to 100,000, and more preferably from 10,000 to 50,000. In addition, the ratio of the weight average to the number average molecular weight ( M w / M n ) of the oxidized polymer is desirably less than 6 and preferably less than 3. Although the invention is not to be so limited, the oxidized olefin polymer is believed to comprise a degradation product of lower molecular weight than the amorphous olefin polymer starting material which contains ketone carbonyl groups. Suitable aldehydes for use in the practice of this invention include low molecular weight aliphatic aldehydes of from 1 to 5 carbon atoms. Such aldehyes include, for example, formaldehyde, acetaldehyde, propionaldehyde and n-butyraldehyde. However, the use of formaldehyde or a formaldehyde-yielding reagent, such as formalin and paraformaldehyde, is highly preferred. Amines which are suitable for use in the process of this invention include amines which are selected from the group consisting of primary and secondary aliphatic amines having from 1 to 24 carbon atoms, aliphatic diamines of the formula H₂N(CH₂) x NH₂ wherein x is an integer from 3 to 10, and polyamines of the formula H₂N(A-NH) y H wherein A is a divalent alkylene radical of from 2 to 6 carbon atoms and y is an integer from 1 to 10. Suitable primary and secondary aliphatic amines are those of the formula R¹R²NH wherein R¹ is selected from the group consisting of hydrogen and aliphatic groups containing from 1 to 12 carbon atoms and R² is selected from the group consisting of aliphatic groups containing from 1 to 12 carbon atoms. The group of amines which is suitable for use in this invention includes, but is not limited to, methylamine, dibutylamine, cyclohexylamine, propylamine, decylamine, ethylenediamine, 1,3-diaminopropane, 1,4-diaminopropane, 1,6-diaminohexane, diethylenetriamine, triethylenetetramine, tetraethylenepentamine, tripropylenetetramine and tetrapropylenepentamine. The oil-soluble sulfonic acids which are suitable for use in the practice of this invention are desirably hydrocarbyl sulfonic acids which have an equivalent weight in the range of from 250 to 2,000, and preferably from 400 to 1,000. In more detail, these sulfonic acids can be represented by formulas I and II: (R¹) x -Ar-(SO₃H) y I R²-(SO₃H) z II In formula I, Ar is a cyclic organic nucleus of the mono- or polynuclear type, including benzenoid or heterocyclic nuclei such as that of benzene, naphthalene, anthracene, 1,2,3,4-tetrahydronaphthalene, thianthrene or biphenyl. Preferably, however, Ar is an aromatic hydrocarbon nucleus, especially a benzene or naphthalene nucleus. R¹ is an aliphatic or substituted aliphatic group, examples of which include alkyl, alkenyl, alkoxy, alkoxyalkyl, carboalkoxyalkyl and aralkyl groups. Both x and y are independently an integer which is at least 1, with the proviso that the variables represented by (R¹) x are such that the acid is oil-soluble. This means that the groups represented by (R¹) x should provide at least about eight aliphatic carbon atoms per molecule of sulfonic acid, and preferably at least twelve aliphatic carbon atoms. Preferably, x and y are integers of from 1 to 3. Finally, the R¹ and Ar groups in formula I can carry substituents such as hydroxy, mercapto, halogen, amino, carboxy or lower carboalkoxy so long as the essentially hydrocarbon character of the groups is not destroyed. In formula II, R² is an aliphatic or substituted aliphatic group which desirably contains a total of at least 12 carbon atoms. Examples of suitable R² groups include alkyl, alkenyl, and alkoxyalkyl groups and also substituted alicyclic groups wherein the substituents are alkoxy, alkoxyalkyl, and carboalkoxyalkyl. Generally, the alicyclic group is a cycloalkane nucleus such as cyclopentane, cyclohexane or cyclohexene, Specific examples of R² include cetylcyclohexyl, laurylcyclohexyl, ethoxycetyl and octadecenyl as well as groups derived from paraffin waxes and polyolefins, including polymerized mono- and diolefins containing from 1 to 8 carbon atoms per olefin monomer unit. The R² group in formula II can carry substituents such as hydroxy, mercapto, halogen, amino, carboxy or carboalkoxy so long as the essentially hydrocarbon character of the group is not destroyed. Finally, z in formula II is an integer of from 1 to 3. Illustrative examples of suitable sulfonic acids include mahogany sulfonic acids, petrolatum sulfonic acids, mono- and polywax-substituted naphthalene sulfonic acids, polyolefin-substituted benzene sulfonic acids, dilaurylbenzene sulfonic acids, laurylcetylbenzene sulfonic acids, cetylchlorobenzene sulfonic acids, cetylphenol sulfonic acids, cetylphenol disulfide sulfonic acids, dilauryl-beta-naphthol sulfonic acids, paraffin wax sulfonic acids, petroleum naphthene sulfonic acids, laurylcyclohexyl sulfonic acids or mono- and polywax-substituted cyclohexyl sulfonic acids. Suitable polyolefin-substituted benzene sulfonic acids for use in this invention include polypropylenealkylated benzene sulfonic acids and polybutylenealkylated benzene sulfonic acids wherein the polypropylene and polybutylene substituents have a molecular weight of at least 100, desirably within the range of 100 to 1,900, and preferably from 250 to 850. Other suitable oil-soluble sulfonic acids are well described in the art including, for example, U.S. Pat. Nos. 2,616,604; 2,626,207; and 2,767,209. Aromatic sulfonic acids of the type set forth in formula I are generally preferred over the aliphatic sulfonic acids of formula II in view of their ready availability and somewhat greater thermal stability at elevated temperatures. Ammonium sulfonates which are suitable for use in the practice of this invention are derived from the above-described oil-soluble sulfonic acids. These ammonium salts can be obtained, for example, by neutralization of the sulfonic acids with ammonia gas or with ammonium hydroxide. It will be appreciated that the sulfonic acid can be at any convenient temperature and in a suitable solvent or neat during the neutralization. In the practice of this invention, the amine is prereacted with sulfonic acid or its ammonium salt in the presence of the oxidized olefin polymer and oleic acid before reaction with the aldehyde. The ratio of equivalents of sulfonic acid or its ammonium salt to equivalents of amine used in the preparation of this prereaction product is desirably from 0.05 to 10 and preferably from 0.1 to 1. The ratio of mole equivalents of oleic acid to mole equivalents of amine is desirably from 0.025 to 10 and preferably from 0.05 to 1.0. Although any suitable reaction temperature can be used, the reaction temperature is desirably between 0° and 250°C., and preferably between 10° and 200°C. The prereaction product can be prepared in the presence of a nonreactive solvent or diluent, if desired. In particular, the amine is preferably substantially anhydrous. If desired, the prereaction product can be prepared and stored for substantial periods of time prior to use. Alternatively, prereaction product of the amine with sulfonic acid or its ammonium salt and oleic acid is condensed in a separate step before reaction with the oxidized olefin polymer and aldehyde. The mole ratio of oxidized olefin polymer to aldehyde to amine in the prereaction product is desirably in the range from 1:2:2 to 1:500:500 (based on the number average molecular weight of the oxidized olefin polymer and either the amount of aldehyde or the potential amount of aldehyde represented by an aldehyde-yielding reagent) and preferably from 1:25:25 to 1:500:500. Although any suitable reaction temperature can be used for this alternative procedure, the reaction temperature is desirably between 0° and 300°C. and preferably between 50° and 250°C. Although not necessary, the condensation is desirably conducted in the presence of a solvent or diluent, for example, an aromatic hydrocarbon solvent such as benzene, toluene, and xylene or an aliphatic hydrocarbon solvent such as hexane. A low viscosity hydrocarbon oil such as a solvent-extracted SAE 5W mineral oil is particularly suitable as a solvent or diluent. The use of a solvent is advantageous to facilitate the mixing of the reactants and for control of the reaction temperature. If desired, the precondensation of the amine with sulfonic acid and/or ammonium sulfonate, oleic acid, and oxidized olefin polymer and the second step condensation reaction between the precondensation product and aldehyde can be carried out under an inert atmosphere, such as nitrogen, in order to prevent any possible oxidative degradation by air. The Mannich reaction product has a viscosity increase of from 17.2 x 10⁻³ to 365 x 10⁻³ Pa·s 100 to 2,000 Saybolt Universal Seconds (SUS) at 100°C, depending upon the mole ratio of the oxidized copolymer to mole ratio of the amine. The viscosity increase is defined as the increase in viscosity over the viscosity of the oxidized copolymer. Although the process of this invention is not to be so limited, it is believed to represent a variation of the Mannich reaction. That is to say, it is believed that the process of this invention involves the replacement of active hydrogen atoms in the oxidized olefin polymer by substituted aminomethyl groups. The subject process results in the formation of a nitrogen-containing product which possesses dispersant properties and is also an excellent viscosity index improver. The chemical composition of the product obtained by the process of this invention cannot be characterized by a precise structural formula. While it is believed that the oxidation of the olefin polymer produces large amounts of ketones, it is known that minor amounts of aldehydes, acids and perhaps esters may also be present. In view of the complex chemical character of the oxidized olefin polymer, this material must be defined by its method of preparation. Since such an oxidized olefin polymer is a starting material for the process of this invention, the resulting product must also be defined by its method of preparation. The Mannich product prepared in accordance with the process of this invention can be incorporated into a lubricating oil by simple mixing. Suitable lubricating oils include, for example, mineral oils; synthetic materials such as olefin polymers, polyoxypropylene and certain dicarboxylic acid esters; vegetable oils such as cotton-seed oil, corn oil and castor oil; and animal oils such as lard oil and sperm oil. A lubricating oil composition will typically comprise a major portion of a lubricating oil in combination with the Mannich product, wherein the amount of Mannich product is from 0.01 to 5 weight percent of the lubricating oil composition. Concentrates containing from 5 to 75 weight percent or more of the subject Mannich product in a suitable base oil, either alone or in combination with other well-known lubricant additives, can be used for blending with lubricating oils in the proportions desired for particular conditions or used to give a finished product containing from 0.01 to 5 weight percent of the Mannich product. The Mannich product of this invention can be used in combination with other conventional lubricating oil additives which include, but are not limited to, wear inhibitors, extreme pressure agents, friction modifiers, antioxidants, corrosion inhibitors, detergents, dispersants, antifoam agents, viscosity index improvers and pour point depressants. The following examples are intended only to illustrate the invention and are not to be construed as imposing limitations on it. Comparative Example I A 7.0% solution of an amorphous ethylene-propylene copolymer (containing about 60 mole percent ethylene and having a number average molecular weight of about 60,000) in a 100 neutral mineral oil, which also contained about 0.2 weight percent of an overbased magnesium alkylbenzene sulfonic acid and about 0.2 weight percent of an alkylbenzene sulfonic acid, was treated with a 50/50 mixture of air and nitrogen with stirring at a temperature of about 180°C. until oxidative degradation of the polymer reduced the viscosity of the mixture to 310 x 10⁻³ Pa·s (1,700 Saybolt Universal Seconds) at 100°C. To 5,000 parts of this oxidized polymer solution at 150°C., were added 17 parts of hexamethylene diamine and 17 parts of the ammonium salt of a polypropylene-substituted benzene sulfonic acid having a molecular weight of 650 under good stirring. After 15 minutes, 30 parts of 37% formaldehyde solution, were added over a 30 minute period. The resulting product has increased viscosity of 465 x 10⁻³ Pa·s (2,150 Saybolt Universal Seconds) at 100°C and contained 717 ppm of nitrogen. Comparative EXAMPLE II Comparative Example I was repeated except that 24.5 parts of 70% aqueous hexamethylenediamine was added. Comparative EXAMPLE III Comparative Example I was repeated except that the amount of the ammonium salt was increased to 34 parts. EXAMPLE I Comparative Example II was repeated except that 1.84 parts of oleic acid (282 equivalent weight) was added after hexamethylene diamine addition. EXAMPLE II Commercial size batches of the products of Comparative Example II and Example I were prepared and tested for product neat haze (undiluted product) in an Amoco hazeometer. Results are in Table I. Products prepared according to the procedure of Comparative Example II were considered as controls. Products prepared according to the procedure of Example I were designated "Oleic". Batch No. Haze Control 8 to 13 B-C 14 to 19 G-H Oleic - A Control 62 to 63 I Oleic 64 C Control 66 to 67 H Oleic 65 C-D The results in Table I demonstrate that the prereaction of the amine with the ammonium sulfonate and oleic acid affords a product having a substantially reduced haze prior to filtration. The reduction in haze and sediment which is provided by the process of this invention is such that filtration is simplified and may be unnecessary. The above Table I uses a scale ranging from A to N, with A representing a crystal clear material which is free of haze and N representing an extremely hazy material which is virtually opaque.

Claims: A process for the preparation of an oil-soluble condensation product which comprises: (a) reacting at least one amine selected from the group consisting of primary and secondary aliphatic amines having from 1 to 24 carbon atoms, aliphatic diamines of the formula H₂N(CH₂) x NH₂ wherein x is an integer from 3 to 10, and polyamines of the formula H₂N(A--NH) y H wherein A is a divalent alkylene radical of from 2 to 6 carbon atoms and y is an integer from 1 to 10, with at least one sulfur-containing material selected from the group consisting of oil-soluble sulfonic acids and their ammonium salts, and oleic acid wherein the ratio of mole equivalents of said sulfur-containing material to mole equivalents of said amine is from 0.05 to 10; and ratio of mole equivalents of said oleic acid to equivalents of said amine is from 0.025 to 10; and an oxidized polymer wherein said oxidized polymer is derived from an amorphous olefin polymer being an amorphous addition polymer derived from olefinically unsaturated hydrocarbon monomers or mixtures thereof, and has a number average molecular weight of at least 3,000 and (b) reacting the product of (a) with formaldehyde or a formaldehyde-yielding reagent (c) recovering the oil-soluble condensation product which has a viscosity increase of from 17.2 x 10⁻³ to 365 x 10⁻³ Pa.s (100 to 2,000 Saybolt Universal Seconds) at 100°C over the viscosity of said oxidized polymer. The process as set forth in Claim 1 wherein said sulfur-containing material is selected from the group consisting of polyolefin-substituted benzene sulfonic acids having an equivalent weight in the range from 250 to 2,000 and their ammonium salts. The process as set forth in Claim 2 wherein said sulfur-containing material is selected from the group consisting of polypropylene-substituted benzene sulfonic acids having an equivalent weight in the range from 400 to 1,000 and their ammonium salts. The process as set forth in Claims 1 to 3, wherein said oxidized polymer is an oxidation product of a polymer which is derived from 30 to 80 mole percent ethylene and from 20 to 70 mole percent of at least one comonomer selected from the group consisting of olefins of the formula R--CH=CH₂ wherein R is an aliphatic group of from 1 to 20 carbon atoms and diolefins of from 4 to 25 carbon atoms. The process as ser forth in Claims 1 to 4, wherein said oxidized polymer is an oxidation product of a polymer which is a copolymer of ethylene and propylene having an ethylene content of 35 to 80 mole percent and a propylene content of from 20 to 65 mole percent. The process as set forth in Claim 5 wherein said copolymer has an ethylene content of 55 to 65 mole percent and a propylene content of 35 to 45 mole percent. The process as set forth in Claims 1 to 5 and 6 wherein said formaldehyde-yielding reagent is selected from the group consisting of formalin and paraformaldehyde. The process as set forth in Claims 1 to 6 and 7 wherein said amine is hexamethylenediamine. The process as set forth in Claims 1 to 8 wherein said amine and said sulfur-containing material are reacted at a temperature in the range from 0° to 250°C. The process as set forth in Claims 1 to 9 wherein said reaction of the product of (a) with formaldehyde or a formaldehyde-yielding reagent is carried out at a temperature in the range from 0° to 300°C. The process as set forth in Claims 1 to 10 wherein said amine is substantially anhydrous. The process as set forth in Claims 1 to 11, wherein the ratio of oxidized polymer to formaldehyde or formaldehyde-yielding reagent to amine is in the range from 1:25:25 to 1:500:500, wherein said ratio is based on the number average molecular weight of the oxidized polymer and either the amount of formaldehyde or the potential amount of formaldehyde represented by said formaldehyde-yielding reagent. Use of the oil-soluble condensation products prepared by the process of Claims 1 to 12 as additives for lubricant oils. Use of the oil-soluble condensation products prepared by the process of Claims 1 to 12 as dispersant-viscosity index improver. Lubricating oil compositions containing an oil-soluble condensation product prepared by the process of Claims 1 to 12.

Inventors: MCCANDLESS HENRY ANDERSON, SONG YOON SOO, MCCANDLESS, HENRY ANDERSON, SONG, YOON SOO
Applicants: ETHYL CORP, ETHYL CORPORATION
Application year: 1987
Main classification: C08F8
IPC codes: C08F8, C10N20, C10N30, C10M159, C10N40