METHOD OF PRODUCING FOAMED, MOLDED ARTICLE

Abstract: Method of producing a molded article of a foamed thermo­ plastic resin including the steps of: (a) accumulating in an accumulator a molten mass of an expandable thermoplastic resin while preventing it from foam­ ing; (b) ejecting a predetermined quantity of the accumulated thermoplastic resin all at once from the accumulator into the at­ mosphere so that the ejected thermoplastic resin commences foaming; (c) placing the ejected thermoplastic resin in a mold cavity before thc expansion thereof has been completed; and (d) completing the expansion and molding of the ejected thermoplastic resin in the mold to obtain a foamed molded arti­ cle.

Description: This invention relates to a method of producing a foamed, molded article formed of a thermoplastic resin. Known methods for the production of foamed, molded article of a thermoplastic resin include the bead molding method, the injection molding method and the extrusion molding method. The bead molding method is a method in which pre-foamed particles placed in a mold cavity are heated for further expansion and fuse-bonding thereof in the mold. The bead molding method is thus disadvantageous because it requires two separate expansion steps, and moreover traces or marks of the beads are left in the resulting molded article. Additionally, when a polyolefin resin is used as raw material, it is difficult to obtain molded articles with a low expansion ratio, while modestly expanded polyolefin molded articles obtained by a bead molding method are poor in both bending strength and compression strength because of incomplete fuse-bonding between the particles. The injection molding method is a method in which a molten mass of a foamable resin is injected into a mold cavity and the injected resin is allowed to expand in the mold. This method, however, requires a high injection pressure and, hence, large and strong apparatus to withstand the pressure. Moreover, the injection molding method has the defect that it can only provide an expansion ratio of at most about 2. The extrusion molding method is one in which a molten, expandable resin is extruded through a die, but it can be used only for the purpose of producing foamed articles of a simple shape such as sheet- or rod-like products. Japanese Published, Unexamined Patent Application (Tokkyo Kokai) No. 58-119832 discloses a method in which a molten mass of an expandable resin is extruded using an ordinary extruder into one of a pair of mold sections and after the expansion of the extruded resin is almost complete the other mold section is closed to forcibly contract the expanded resin. The molded product obtained, however, has a low compression strength in the direction along which the resin was contract during the mold closing step. WO-A-8200440 discloses a method of producing a foamed molded article which comprises the steps of: (a) accumulating in an accumulator a molten mass of an expandable thermoplastic resin while maintaining the molten mass at a temperature and a pressure so that it is prevented from foaming; (b) ejecting a predetermined quantity of the accumulated molten thermoplastic resin rapidly from the accumulator into an atmosphere maintained at a pressure lower than that within the accumulator so that the ejected thermoplastic resin commences foaming; (c) placing the ejected thermoplastic resin in a mold cavity before the expansion thereof has been completed; and (d) completing the expansion and molding of the ejected thermoplastic resin in the mold to obtain a foamed molded article. The present invention provides a development of the molding method of WO-A-8200440 and is characterized in that the ejected thermoplastic resin, which has been placed in the mold cavity i.e. in step (c) is subjected to compression, and in that the step of completing the expansion and molding of the ejected thermoplastic resin in the mold i.e. step (d) is performed while controlling the compression pressure. The compression treatment serves to improve the expansion ratio of the molded article. Any known thermoplastic resin may be used as a raw material in the method of the present invention. Illustrative of suitable thermoplastic resins are polyolefin resins such as polyethylenes, polypropylenes, copolymers of ethylene and a mono-olefin (e.g. propylene), copolymers of ethylene and a vinyl monomer (e.g. vinyl acetate), and resins obtained by modifying the above polymers or copolymers with a silane compound; styrene resins such as polystyrenes and ABS resins; polyvinyl chloride resins; polyamide resins; polycarbonate resins; and polyhydroxy ether resins. The method of the present invention is particularly suited for the production of foamed articles formed of polyolefins such as high density polyethylene and polypropylene. In carrying out the method of this invention the thermoplastic resin may be homogeneously commingled with a blowing agent at a temperature higher than the melting point of the resin under a pressurized condition to obtain a molten, expandable thermoplastic resin composition. Both decomposition-type blowing agents and solvent-type blowing agents may be used for the purpose of the present invention. However, the use of the solvent-type blowing agents is recommended. Examples of solvent-type blowing agents include cycloparaffins such as cyclobutane and cyclopentane; aliphatic hydrocarbons such as propane, butane, pentane, hexane and heptane; and halogenated hydrocarbons such as trichlorofluoromethane, dichlorodifluoromethane, methyl chloride, methylene chloride, dichlorotetrafluoroethane, tetrafluoroethane, tetrafluorochloroethane, trifluorochloroethane, pentafluoroethane, trifluoroethane, difluorochlroethane, ethyl chloride, trifluoropropane, difluoropropane and octafluoropropane. The molten, expandable resin composition may further contain a conventional expansion aid such as a metal salt or metal hydrogen salt of an organic acid, a metal salt or metal hydrogen salt of carbonic acid, or talc. The present invention will now be described in more detail with reference to the accompanying drawings, in which: Fig. 1 is a schematic flow diagram of apparatus suitable for carrying out the method of the present invention; and Fig. 2(a) through 2(d) are vertical cross-sections schematically showing one embodiment of the molding step of the method according to the present invention. Designated generally as 1 is a mixing zone where the thermoplastic resin raw material, such as thermoplastic resin pellets and optionally an expansion aid, introduced from a hopper 2 are commingled with a blowing agent supplied through a line 2a at a temperature higher than the melting point of the thermoplastic resin and under a pressure to obtain a molten, expandable resin. Customarily employed temperatures and the pressures, which are generally determined according to the resin used, are adopted in the present invention. In the case of high density polyethylene or polypropylene, for example, a temperature of 120-200 °C and a pressure of 30-200 kg/cm²G are used. The mixing is generally effected by means of an extruder 3 provided with an auger 4. The molten, expandable resin composition thus prepared in the mixing zone 1 is fed to an accumulator 5 through a passage 6 and accumulated therein. During the accumulation of the molten resin, the interior of the accumulator is maintained at a temperature and under a pressure such as to prevent expansion thereof. Generally, the molten resin is maintained at a temperature lower than in the mixing zone 1. For example, when a high density polyethylene is used, the accumulator is preferably maintained at a temperature of 120-150 °C and a pressure of 30-200 kg/cm²G. When a predetermined amount of the molten expandable resin has accumulated in the accumulator 5 it is discharged from the accumulator 5 through a die 7 all at once into an atmosphere maintained at a pressure lower than that in the accumulator 5, generally ambient pressure, so that the discharged molten resin 10 commences expanding. The rate at which the molten resin accumulated in the accumulator is discharged therefrom is preferably 250 kg/hr or more. To expedite the discharge of the molten resin, it is preferably to use a means for forcibly discharging the molten resin. Thus, in the embodiment shown in Fig. 1, the accumulator 5 has a cylindrical shape and is provided with a gate (not shown) for opening and closing the aperture of the die 7 and with a ram 8 reciprocally slidably disposed therewithin. The ram 8 is secured to a piston rod 9 of a hydraulic means (not shown). The ram 8 is operated in the following manner. The molten resin prepared in the mixing zone 1 is introduced under pressure into the accumulator 5 through the passage 6 while closing the aperture of the die 7 with the gate. The pressure is transmitted to the ram 8 so that the ram 8 is gradually moved back as the molten resin is accumulated within the accumulator 5. When the molten resin accumulated in the accumulator 5 reaches a predetermined volume, the hydraulic means is actuated and, simultaneously, the gate is opened. Thus, the piston rod 9 is driven to advance the ram 8 toward the die 7, thereby ejecting the accumulated molten resin through the die 7 into the atmosphere. Thereafter, the gate is closed and the pressure of the hydraulic means is released so as to decrease the pressing force of the ram 8 to a predetermined level. As a result, the molten resin in the mixing zone 1 is again introduced into the accumulator 5 and is accumulated therein. In like manner, molten resin is intermittently discharged from the accumulator 5. The pressure inside the accumulator 5 is controlled so that the foaming of the molten resin is prevented. This can be effected by controlling the pressure exerted by the hydraulic means and applied to the ram 8. A preferred example of the accumulator as described above is disclosed in US-A-4,323,528, the disclosure of which is hereby incorporated by reference. The molten resin 10 thus discharged from the accumulator 5 is placed into the mold cavity of a mold 11 before the expansion thereof is completed and is subjected to expansion-molding conditions therewithin as described more fully hereinafter to obtain an expanded, molded article. Preferably, the expansion-molding is started before the expansion of the molten resin has reached 50 %, more preferably before it has reached 30 %. the resulting molded article generally has an expansion ratio of 1.2-50, particularly 2-10. The shape of the cells of the molded article is generally spherical or elliptic with their major axes oriented in the direction along which mold sections of the mold is moveable and, therefore, the molded article can withstand compression applied in that direction. In the present invention, it is preferred that the molten resin 10 discharged from the accumulator 5 exhibit a low expansion speed. The kind of the resin, melt index (MI) value of the resin, the kind and amount of the blowing agent, the kind and amount of the expansion aid (cell adjusting agent) and the shape and size of the cross-section of the die 7 of the accumulator 5 through which the resin is discharged have an influence upon the expansion speed. It is especially effective to select a die having such a size and a shape that can provide only a small difference in pressure between the atmosphere into which the molten resin is discharged therethrough and the interior of the accumulator in which the discharge of the molten resin has just been completed. It is also effective to minimize the amount of the expansion aid. For example, in the case of high density polyethylenes having an MI value of 0.5-20, the use of 5-20 parts by weight of dichlorotetrafluoroethane and/or dichlorodifluoromethane and 0-0.05 part by weight of talc per 100 parts by weight of the polyethylene is recommended. Before expansion-molding the molten resin discharged from the accumulator, the resin may be forcibly cooled for the formation of a skin layer over the surface thereof. The cooling may be effected by allowing the resin to pass through a pair of cooled rolls or by direct contact with cooled water or ice water. The resin having the skin layer is then heated for the softening of the skin layer before conducting the expansion-molding. This method is effective to produce expanded articles having a high mechanical strength. The shape of the resin discharged from the accumulator is not restricted to a plate as shown in Fig. 1. A shapeless lump, a rod or any other shaped body may be used. There is ample time until the expansion of the expandable molten resin placed into a mold cavity is completed and since the environment into which the molten resin is discharged from the accumulator 5 can be under ambient pressure, the expansion molding can be performed in various ways. In the embodiment illustrated in Figs. 2(a) through 2(d), the resin discharged from the accumulator is a shapeless mass. Figs. 2(a)-2(d) show an embodiment in which a pair of stationary, male and moveable, female mold sections 19 and 20 are used. The molten resin discharged from the accumulator is placed into the female mold section (Fig. 2(a)). Then, the female mold section 20 is moved upward to press the resin at a pressure of, for example, 1-10 kg/cm²G (Fig. 2(b)). This pressing treatment serves to improve the expansion ratio of the resin. The mold 11 is heated to accelerate the expansion of the pressed resin. As the expansion proceeds, the female mold section 20 is lowered to any desired level (Fig. 2(c)) by control of the pressure applied to the female mold section 20. During the course of the expansion, the pushing pressure of the female mold section 20 can be maintained at a constant value which may be the same as or lower than the pressure in the pressing step of Fig. 2(b), or can be gradually lowered in correspondence to the increase in the inflating pressure due to expansion of the resin. After completion of the expansion, the mold 11 is opened to recover the molded article 17 (Fig. 2(d)). In this embodiment, the ports 15 and 16 serve to function as vents. For the purpose of the present specification, the expansion ratio of a foamed, molded article is defined as follows: Expansion Ratio = Bulk density of molded article Density of the resin prior to expansion The expansion rate of a molten mass of an expandable thermoplastic resin immediately before it is subjected to molding is obtained by the following manner: The molten resin is placed in a female mold section as shown in Figs. 2(a)-2(d) and is pressed between the female and male mold sections while applying thereto a pressure of 1.5 kg/cm². The inside volume V of the mold defined between the mold section when the female mold section stops moving is measured. The female mold section is then moved as the expansion of the resin proceeds. When the female mold section stops moving, the pressure applied to the resin in the mold is decreased to 0.5 kg/cm² to restart the expansion thereof. When the expansion is completed and the female mold section stops moving, the inside volume V′ of the mold defined between the mold sections is measured. During the course of the molding operation, the temperature of the mold is maintained at a temperature higher by 10 °C than the melting point or softening point of the resin. The expansion rate may be given by the following equation: Expansion Rate (%) = dV - W dV′ - W x 100 where d represents the density of the molten resin prior to expansion and W represents the weight of the molten resin placed in the mold. The following example will further illustrate the present invention. Example Foamed articles were prepared using the apparatus shown in Figs. 1 and 2. Thus, the thermoplastic resin indicated in Table below and the blowing agent shown in the Table were mixed means of an extruder at a temperature of 160 °C and the resulting expandable resin composition was extruded at a rate of 10 kg/hr into an accumulator and accumulated therein at a temperature as shown in the Table. The amount of the blowing agent used was as indicated in the Table. The expandable resin accumulated in the accumulator was ejected through a die with an outlet cross-sectional area of 15 cm² at a rate of 300 kg/hr into the atmosphere. The ejected mass was immediately placed in the mold as shown in Fig. 2 and expansion molded to obtain a foamed, molded article having an expansion ratio as shown in the Table.

Claims: 1. A method of producing a foamed molded article, comprising the steps of: (a) accumulating in an accumulator a molten mass of an expandable thermoplastic resin while maintaining said molten mass at a temperature and a pressure so that said molten mass is prevented from foaming; (b) ejecting a predetermined quantity of the accumulated molten thermoplastic resin rapidly from said accumulator into an atmosphere maintained at a pressure lower than that within said accumulator so that the ejected thermoplastic resin commences foaming; (c) placing the ejected thermoplastic resin in a mold cavity before the expansion thereof has been completed; and (d) completing the expansion and molding of the ejected thermoplastic resin in the mold to obtain a foamed molded article; characterized in that the ejected thermoplastic resin which has been placed in the mold cavity in step (c) is subjected to compression and in that step (d) is then performed while controlling the compression pressure. 2. A method as claimed in Claim 1, wherein said compression pressure is in the range 1-10 kg/cm²G. 3. A method as claimed in Claim 1 or Claim 2, wherein step (d) is effected using a pair of male and female mold sections moveable relatively to each other so that said mold cavity defined therebetween is changeable in length in the direction along which said mold sections are moveable as the thermoplastic resin expands. 4. A method as claimed in any preceding claim, wherein said thermoplastic resin is a polyolefin resin, preferably a polypropylene resin or a high density polyethylene. 5. A method as claimed in any preceding claim, wherein the ejected thermoplastic resin placed in the mold cavity in step (c) is in the form of a shaped body. 6. A method as claimed in Claim 5 wherein, before step (c), said shaped body is cooled to form a skin layer over its surface and then heated to soften the skin layer. 7. A method as claimed in any preceding claim, wherein said molten mass of the expandable thermoplastic resin is obtained by mixing the thermoplastic resin with a blowing agent at a temperature and a pressure so as to cause the resin to melt and to prevent the resin from foaming.

Inventors: AKIYAMA, HIROYIKI, KISHIKA, MASAHIKO, NISHIKA, MITSURU, SUDO, YOSHIMI
Applicants: JAPAN STYRENE PAPER CORPORATION
Application year: 1987
Main classification: B29C67
IPC codes: B29K105, B29C47, B29C44, B29B11