PROCESS FOR FABRICATING HEAT-EXCHANGERS

Abstract: An aluminum alloy suitable for heat exchanger components assembled by brazing with a flux of non-corrosive fluoride complexes, the alloy having improved brazing characteristics by containing 0.3 to 0.8% of Mg, 4.0 to 8.0% of Zn, and one or more of 0.05 to 0.30% of Zr, 0.05 to 0.30% of Mn, 0.05 to 0.30% of Cr, and 0.05 to 0.30% of Cu, the balance being aluminum and unavoidable impurities.

Description: The present invention relates to an aluminum alloy suitable for heat exchanger components, wherein the term "heat exchangers" includes condensers and evaporators for automobile cooling systems. More particularly, the present invention relates to aluminum alloys having such improved brazing characteristics as to be suited for heat exchanger components assembled by brazing with a flux of fluoride complexes. In this specification the percentages are represented by weight. The heat exchanger used as evaporator or condenser in automobile cooling systems comprises aluminum tubular elements bent in a zigzag form and a corrugated fins interposed therebetween. In such heat exchangers the tubular elements are connected to coolant conductors with the use of union joints and various types of connectors. The known heat exchangers are composed of tubular elements of pure aluminum alloy such as A1100 or A1050, and fins covered with a brazing sheet, wherein the brazing sheet is made of a core of aluminum alloy such as A3003, clad in a covering of BA4045 or BA4047 alloy. The known joint members are generally made of A7N01 alloy because of its good workability and strength (hardness). The A7N01 alloy contains 1.0 to 2.0% of Mg, 4.0 to 5.0% of Zn, and 0.20 to 0.7% of Mn, the remainders of which are aluminum and unavoidable impurities. Under the known methods the tubes, conductors and fins are jointed to each other by brazing. The brazing agent contains flux, such as alkali metal chlorides or alkaline earth metal chlorides. Recently fluorine flux has been put into use because of its non-corrosive nature. For example, U.S. Patent No. 3,951,328 discloses a flux which consists essentially of potassium fluoaluminate complexes and essentially free of unreacted potassium fluoride. Such fluorine fluxes are non-hygroscopic, chemically stable, and leaves no corrosive residue after the components are brazed to each other. The use of fluorine flux eliminates the necessity of cleaning the brazed joints out of the flux residue after the brazing is finished. This is advantageous over the chlorides fluxes. However the problem is that though the fluorides fluxes are effective for jointing the tubes to the fins, they are not suitable for joining the tubes to the joint members because of the resulting small fillets. When the fillets are small the joint is liable to break. To overcome this difficulty it is proposed that the tubes are first brazed to the fins with a fluorine flux in a furnace filled with a non-oxidizing gas and then the joint members are brazed to the tubes by torch. The process requires at least two steps. This takes time and increases the production cost. The inventors have tried to find out why the fluorine fluxes are unsuitable for joining the tubes to the joint members and discovered that it is due to the presence of magnesium contained therein in a relatively large quantity. The magnesium reacts with the fluorine in the fluxes, thereby negating the fluxing action of fluorine. The present invention aims at solving the problems pointed out above and has for its object to provide a method for fabricating heat exchangers by using an aluminum alloy suitable for heat exchanger components assembled by brazing with a flux of fluoride complexes, the alloy having improved brazing characteristics with respect to each other, thereby securing the permanent, firm joint therebetween. Other objects and advantages of the present invention will become more apparent from the following detailed description, when taken in conjunction with the accompanying drawing which shows, for the purpose of illustration only, one embodiment in accordance with the present invention. The basic principle underlying the present invention is that the content of magnesium is reduced, but it leads to the decreased hardness. The decrease in strength must be compensated for by adding a suitable element. The present invention has adopted zinc for the suitable element. According to the present invention there is provided a method for fabricating a heat exchanger comprising providing components including tubular elements, fins and joint members, the joint members being made of aluminum-based alloy containing 0.3 to 0.8% of Mg, 4.0 to 8.0% of Zn, and one or more of 0.05 to 0.30% of Zr, 0.05 to 0.30% of Mn, 0.05 to 0.30% of Cr, 0.05 to 0.30% of Cu, the balance being aluminum and unavoidable impurities, brazing the components to form a heat exchanger with a flux of fluoride complexes in a furnace filled with a non-oxidizing atmosphere. Preferred embodiments of the invention are given in the dependent claims. The drawing is a perspective fragmentary view particularly showing an assembled unity of joint members, a tube and fins in a typical heat exchanger. In the drawing the tube 1 is made of A1100 alloy and bent in a zigzag form, having a path (not shown) therein for passing a coolant through. The fin 2 is a corrugated plate covered with abrazing sheet. The fin plate 1 is brazed to the tube 1. In the illustrated embodiment a joint member 3 is connected to each terminating end of the tube 1 in such a manner that the coolant path in the tube communicate with a bore of the joint member. The joint member 3 is made of the alloy of the present invention. The magnesium is added to the alloy so as to increase strength, especially to maintain the hardness above a required value after age-hardening. To achieve this at least 0.3% or more Mg is required. However it is preferred that the quantity of it is smaller than that contained in the A7N01 alloy of which the joint members are made. The upper limit is 0.8%. If a greater amount of Mg than 0.8% is contained a more magnesium will react with the fluorine contained in the flux, thereby negating the fluxing action thereof. This leads to a poor joint between the joint member and the tube. The optimum quantity of Mg is in the range of 0.4 to 0.5%. Zinc is also effective to increase the strength of the alloy. Taking advantage of this property a quantity of zinc correlative to the reduced amount of Mg is added so as to compensate for the reduction in strength. The optimum quantity of Zn is in the range of 4.0 to 8.0%. If the quantity of it is smaller than 4.0% the strength will decrease after brazing, whereas, if it is more than 8.0%, the alloy will be liable to corrosion, and become brittle. The optimum quantity of Zn is in the range of 5.1 to 7.0%. Zr, Mn, Cr and Cu are equally effective to improve the brittle property of the alloy but a smaller amount than 0.05% will never be effective, whereas a greater amount than 0.3% would not produce better results. The optimum ranges are as follows: Zr: 0.10 to 0.20% Mn: 0.10 to 0.20% Cr: 0.05 to 0.15% Cu: 0.15 to 0.25% Fe and Si are unavoidably contained as impurities but so long as their quantity is small they will be rather conducive to increase strength. However the corrosion resistance decreases. Their quantity must be limited to 0.3% or less. The invention will be better understood from the example below: Test pieces were made of the aluminum alloys listed in Table 1. Molten alloys were cast into billets and then subjected to a homogenizing treatment at 480°C for 10 hours. The billets were preheated to 400°C, and extruded through an extruder. The extruded masses were subjected to a T₆ tempering, and then cut into the test pieces. For brazing, a fluoride flux containing 8.3% KF and 91.4% KA1F₄ was dissolved into a 10% dispersion. The objects to which the test pieces were to be jointed were submerged in the dispersion. After the test pieces were dried they were brazed to the objects at an atmosphere of N₂ gas at 600°C for 5 minutes with the use of an A4047 alloy as a brazing agent. The brazed conditions of the test pieces were examined and compared. After a month's age-hardening was over, the hardness of each test piece was examined. In addition, the smoothness with which each test piece was extruded through the extruder was examined. The results are shown in Table 2. The evaluation terms are as follows: (Extruding ability) G (good): better than the 7N01 alloy F (fair): equal to the 7NO1 alloy (Brazing ability) G (good): well jointed B (bad): poorly jointed (Corrosion resistance and anti-stress ability) G (good): better than the 7N01 alloy B (bad): inferior to the 7N01 alloy (Hardness) G (good): Vickers' hardness a month after the brazing was carried out: Hv ≧ 80 B (bad): Vickers' hardness a month after the brazing was carried out: Hv < 80 (General Evaluation) G (good): All the pieces are satisfactory. F (fair): Some pieces are unsatisfactory. B (bad): All the pieces are unsatisfactory. As is evident from Table 2, the test pieces No. 1 to 11 exhibit a good extruding ability and brazing ability. However in order to be suited for heat exchanger components the alloys must have Vickers' hardness of at least 80 Hv. If the hardness is less than 80 Hv, the alloys are likely to become deformed when they are tightened up. The test pieces No. 8, 9 and 11 are finely evaluated as unsatisfactory. The test pieces No. 10 and 12 maintain satisfactory hardness after age-hardening but disadvantageously liable to corrosion and stress because of the relatively large content of Zn. The test piece No. 13 made of A7N01 alloy in ordinary use was found inferior in the brazing ability. The test pieces No. 1 to 7 of the invention exhibit better extruding ability than the A7N01 alloy. This tells that the alloy of the invention is suited for fabricating joint members. In addition, they are equal to A7N01 alloys in brazing ability, hardness, corrosion-resistance and anti-stress (anti-SCC). However some of the test pieces No. 1 are inferior in hardness and some of the test pieces No. 7 are inferior in brazing ability. Nevertheless the defectiveness of them is not fatal but to a negligible degree for pratical purpose.

Claims: A method for fabricating a heat exchanger comprising providing components including tubular elements, fins and Joint members, the joint members being made of aluminum-based alloy containing 0.3 to 0.8% of Mg, 4.0 to 8.0% of Zn, and one or more of 0.05 to 0.30% of Zr, 0.05 to 0.30% of Mn, 0.05 to 0.30% of Cr, 0.05 to 0.30% of Cu, the balance being aluminum and unavoidable impurities, brazing the components to form a heat exchanger with a flux of fluoride complexes in a furnace filled with a non-oxidizing atmosphere. A method according to claim 1, characterized in that the body of the heat exchanger comprises tubular elements each bent in a zigzag form and corrugated fins interposed between the tubular elements. A method according to claim 1 or 2, characterized in that the content of Mg is in the range of 0.4% to 0.5% A method according to claim 1, 2 or 3, characterized in that the content of Zn is in the range of 5.1% to 7.0%. A method according to claim 1, 2 , 3 or 4, characterized in that the content of Zr is the range of 0.10% to 0.20%. A method according to any of claims 1 to 5, characterized in that the content of Mn is in the range of 0.10% to 0.20%. A method according to any of claims 1 to 6, characterized in that the content of Cr is in the range of 0.05% to 0.15%. A method according to any of claims 1 to 7, characterized in that the content of Cu is in the range of 0.15% to 0.25%.

Inventors: IWAI, ICHIRO, NAGAI, SHIGEKAZU, OTUKA, TATSUO
Applicants: SHOWA ALUMINUM KABUSHIKI KAISHA
Application year: 1987
Main classification: B23K35
IPC codes: C22C21, B23K35