POLYARYLENE SULFIDE RESIN COMPOSITIONS, AND ARTICLES MANUFACTURED THEREFROM

Abstract: A polyarylene sulfide resin composition with an improved moldability and heat resistance comprises (a) 40 to 99% by weight of a polyarylene sulfide resin and (b) 1 to 60% by weight of a polyparabanic acid having the following recurring unit: wherein Z and Z¹ are oxygen atoms or NH group, Z and Z¹ being not simultaneously NH groups, and R is wherein R¹, R², R³, R⁴, R⁵ and R⁶ are hydrogen atoms or methyl groups, and X and X¹ are bonds, CH₂ groups, oxygen atoms, sulfur atoms, SO₂ groups, CO groups or

Description: This invention relates to a resin composition with excellent moldability and heat resistance or heat durability, comprising a polyarylene sulfide resin and polyparabanic acid; and moulded articles whenever made in whole or in part therefrom. Polyarylene sulfide resins have been noted as engineering plastics because of their excellence in flame retarding properties, chemical resistance, heat resistance and melt flowability. Compositions comprising polyarylene sulfide resins and polyimide resins or polyamideimide resins are known with a view to improving the heat resistance of the polyarylene sulfide resins, for example, in Japanese Patent Application OPI (Kokai) No. 73228/1978 and Japanese Patent Publication No. 45506/1981. On the other hand, polyparabanic acid has a high glass transition temperature such that it is suitable for use in, for example, manufactured articles such as industrial parts requiring heat resistance, but it can hardly be subjected to molding, e.g. extrusion molding because it tends to decompose at a temperature somewhat higher than the glass transition temperature. Thus, various proposals have been made as to plasticization of polyparabanic acid, for example, a composition comprising polyparabanic acid and a plasticizing amount of an N,N-dialkyl aromatic sulfonamide (as disclosed in Japanese Patent Application OPI (Kokai) No. 119551/1979) or a composition comprising polyparabanic acid and a plasticizer, to which a polyether sulfone or polyester of terephthalic acid is added (as disclosed in Japanese Patent Application OPI (Kokai) No. 13656/1983). EP-A-68695 describes blends of polyparabanic acid with aromatic polyether sulfones and polyesters. It is an object of the present invention to provide a polyarylene sulfide resin composition having an improved moldability and heat resistance or heat durability. It is another object of the present invention to provide a polyphenylene sulfide resin composition with an increased heat resistance and improved melt moldability without causing deterioration of the properties of polyphenylene sulfide resin. These objects can be attained by a polyarylene sulfide resin composition comprising (a) 40 to 99% by weight of a polyarylene sulfide resin and (b) 1 to 60% by weight of a polyparabanic acid having the following recurring unit: wherein Z and Z¹ are oxygen atoms or NH groups, Z and Z¹ being not simultaneously NH groups, and R is wherein R¹, R², R³, R⁴, R⁵ and R⁶ are hydrogen atoms or methyl groups, and X and X¹ are bonds, CH₂ groups, oxygen atoms, sulfur atoms, SO₂ groups, CO groups or In seeking to improve the heat resistance of a polyarylene sulfide resin it has been found that blending of a polyparabanic acid is effective for this purpose. The present invention is based on this finding. Accordingly, the present invention provides a polyarylene sulfide resin composition comprising (a) 40 to 99% by weight, preferably 60 to 95% by weight of a polyarylene sulfide resin and (b) 1 to 60% by weight, preferably 5 to 40% by weight of a polyparabanic acid. In the composition of the present invention, the polyarylene sulfide (hereinafter referred to as PAS) resin has a recurring unit represented by the general formula ( Ar - S ) wherein - Ar - is, for example, or the like. These aromatic groups can be substituted by substituents such as fluorine, chlorine, bromine, methyl group and the like. Typical of the above described PAS resin are polyphenylene sulfides (hereinafter referred to as PPS) represented by the general formula wherein n is about 10 - 1000, which are commercially available as a commercial name "RYTON"® from Phillips Petroleum Co. in USA, and which can, for example, be prepared by reacting and NA₂S.H₂O in a solvent of N-methylpyrrolidone at a temperature of 160 to 250°C under pressure, as disclosed in Japanese Patent Publication No. 3368/1970. The PAS resin used in the present invention is one having a melt viscosity of 100 to 500,000 Pa's at 300°C. R is preferably: Preferably, the polyparabanic acid is a polymer of which 75% or more is constituted by the following recurring unit (hereinafter referred to as Unit (II): wherein R has the same meaning as described above. The polymer having unit (I) is known and can be prepared by, for example, reacting a diisocyanate represented by the general formula OCN-R-NCO wherein R has the same meaning as described above with hydrogen cyanide, as disclosed in US Patent No. 3,661,859. The polyparabanic acid consisting of at least 75% of unit (II), preferably used in the present invention, can be obtained by hydrolyzing a polymer consisting of unit (I). This method is carried out by subjecting the polymer consisting of unit (I) to hydrolysis in the presence of an aqueous solution of a Broensted acid such as hydrochloric acid, hydrobromic acid, sulfuric acid or phosphoric acid, anhydrous hydrogen chloride or anhydrous hydrogen bromide, for example, as disclosed in US Patent No, 3,661,859 and Japanese Patent Application OPI (Kokai) No. 179230/1983. A proportion of at least 75% of Unit (II) can be controlled by broadly varying the hydrolysis conditions, namely, the concentration or quantity of Broensted acid, temperature and time. Examples of the diisocyanate represented by the foregoing general formula, used for the production of a polymer consisting of Unit (I), are m-phenylene diisocyanate, 2,4-toluene diisocyanate, p-phenylene diisocyanate, 1,5-naphthalene diisocyanate, 4,4′-biphenyl diisocyanate, tolidine diisocyanate, 4,4′-diphenylether diisocyanate, 4,4′-diphenylthioether diisocyanate, 4,4′-diphenylisopropylidene diisocyanate, 4,4′-dicyclohexylmethane diisocyanate, 4,4′-diphenylmethane diisocyanate and the like. 4,4′-biphenyl diisocyanate, 4,4′-diphenylether diisocyanate and 4,4′-diphenylmethane diisocyanate are preferred. The polyparabanic acid used in the present invention preferably has a viscosity η inh of 0.1 to 5.0 (0.5 g/100 ml dimethylformamide, 30°C). The composition of the present invention comprises 40 to 99% by weight, preferably 60 to 95% by weight of PAS resin and 60 to 1% by weight, preferably 40 to 5% by weight of the polyparabanic acid. If the quantity of PAS resin is less than 40% by weight, the moldability is insufficient, while if more than 99% by weight, the heat resistance or durability is not so improved. For the purpose of improving the mechanical strength of the composition of the present invention, other components can be added thereto, for example, at most 60% by weight of fibrous fillers such as glass fibers, carbon fibers, boron fibers, silicon carbide fibers, asbestos fibers, metallic fibers and the like and at most 40% by weight of powdered fillers such as calcium carbonate, mica, silica, alumina, talc, barium sulfate, clay, kieselguhr and other metal oxides. Preparation of the composition of the present invention can be carried out by previously dry-blending PAS resin and polyparabanic acid optionally with other components and then melting and kneading the mixture. The melting and kneading can generally be carried out using an extruder, Banbury mixer, kneader and heated rolls, which are commonly used for melting and kneading rubbers or plastics. The kneading temperature is adjusted to a range of a temperature wherein the resin components can be melted to a temperature of thermal decomposition thereof and is ordinarily chosen from a range of 280 to 360°C. The composition of the present invention can readily be melted and molded and the thus resulting moldings are excellent in heat resistance and mechanical properties. Because of these excellent properties, the composition of the present invention is useful for automobile parts, electric and electronic parts, special mechanical parts and the like. The following examples are given in order to illustrate the present invention in detail without limiting the same, in which percents of components are to be taken as those by weight and tests are carried out according to the following standards or procedures. (1) Tensile Strength and Elongation: JIS K 6301 (2) Flexual Modulus: JIS K 7203 (3) Heat Resistance: A weight decrease at 360°C is measured by a thermogravimetric analysis (TGA) at a temperature raising rate of 10°C/min in a nitrogen atmosphere using a thermo-balance (R-TG Type (trade name), manufactured by Rigaku Denki KK). Examples 1 to 5 and Comparative Examples 1 and 2 PPS resin (RYTON® P4 and R4 (trade name) manufactured by Phillips Petroleum Intl., Ltd.), polyparabanic acid powder (TRADLON (trade name) manufactured by Exxon Chemical Co., η inh = 1.0 or less, hereinafter referred to as PPA resin), glass fiber (03 JA 404 (trade name) manufactured by Asahi Fiber Glass Co.) and calcium carbonate (Homocal-D -(trade name) manufactured by Shiraishi Kogyo KK) were dry-blended in proportions as shown in Table I, fed to an extruder where the mixture was melted and kneaded at a temperature of 310°C and then extruded therefrom to form pellets. Test pieces were molded from the resulting pellets and subjected to measurement of the properties. The moldability was estimated by the possibility of injection molding. The results are shown in Table I.

Claims: A polyarylene sulfide resin composition comprising (a) 40 to 99% by weight of a polyarylene sulfide resin and (b) 1 to 60% by weight of a polyparabanic acid having the following recurring unit: wherein Z and Z¹ are oxygen atoms or NH group, Z and Z¹ being not simultaneously NH groups, and R is wherein R¹, R², R³, R⁴, R⁵ and R⁶ are hydrogen atoms or methyl groups, and X and X¹ are bonds, CH₂ groups, oxygen atoms, sulfur atoms, SO₂ groups, CO groups or The polyarylene sulfide resin composition as claimed in claim 1, wherein the polyarylene sulfide resin has the following recurring unit: ( Ar - S ) wherein Ar is The polyarylene sulfide resin composition as claimed in claim 2, wherein the AR group has at least one substituent selected from fluorine, chlorine, bromine and the methyl group. The polyarylene sulfide resin composition as claimed in claim 1, wherein the polyarylene sulfide resin is a polyphenylene sulfide resin represented by the general formula: wherein n is about 10 - 1000. The polyarylene sulfide resin composition as claimed in claim 1, wherein the polyparabanic acid is a polymer consisting of at least 75% of the following recurring unit: Moulded articles whenever made in whole or in part from a polyarylene sulfide resin composition as claimed in any one of the preceding claims.

Inventors: IMAI, CHIHIRO, IMAI, YOUICHI, KATO, MASAYUKI, NIWA, TADASHI, TAGUCHI, YOSHIO
Applicants: TOA NENRYO KOGYO KABUSHIKI KAISHA
Application year: 1987
Main classification: C08L81
IPC codes: C08L81, C08L79