METHOD OF PRODUCING THERMOPLASTIC ELASTOMER COMPOSITIONS

Abstract: A method of producing compounds in which the rubber phase contains a polyolefin and a halobutyl rubber, which is partially crosslinked, to which composition is then added additional polyolefin and a vulcanizable olefinic rubber, which is then further crosslinked using organic peroxides, and then blended with a styrenic rubber. The TPE compounds incorporate (A) polypropylene 10-90 weight parts (wt. pts.), (B) halobutyl rubber 90-10 wt. pts. (where (A) + (B) = 100), (C) an olefinic rubber 10-120 wt. pts., (D) mineral oil softener 5-120 wt. pts., which are then treated thermally inthe presence of (E) MOx and/or MCl, to which composition of 100 weight parts is added (F) polyolefin 100-600 wt. pts., and (G) a vulcanizable olefinic rubber 50-500 wt. pts. The resulting blend is then thermally treated with (H) organic peroxide(s), to which blend of 100 wt. pts. is then added and uniformly dispersed (I) 5-150 wt. pts. of styrenic rubber. The method produces thermoplastic elastomer compositions which can be molded into large parts with smooth surfaces that accept paint well, have a good balance of flexibility and strength.

Description: - 1 - "METHOD OF PRODUCING THERMOPLASTIC ELASTOMER COMPOSITIONS" BACKGROUND OF THE INVENTION Compounds consisting of polyolefin and a partially crosslinked rubber phase possess good properties as thermo¬ plastic elastomers (TPEs) such as heat resistance, mechani¬ cal strength, flexibility and elasticity etc., but their flowability is poorer than generally used thermoplastics, leading to problems such as flow marks in the manufacture of large molded parts. In order to resolve these problems, for example, partially crosslinked compounds of polyolefin and two rubber components (Japanese Patent 54-23702), partially crosslinked compounds in which polyolefin is blended with a composition of a polyolefin and a rubber component which was treated in the presence of organic peroxide (Japanese Patent 56-15743) as well as the method of manufacture of such com¬ pounds (56-15740) have been proposed. These inventors have developed compounds in which a polyolefin is added to a composition consisting of halo- butyl-containing rubber phase which is partially crosslinked with a polyolefin, using metal oxide (MOx) and/or metal chlorides (MCI) as vulcanizing agents. In addition, the method of manufacture of TPE compositions including styrenic rubber has been proposed, for example Japanese Patent Appl. 59-6236 proposes manufacture of compositions containing a hydrogenated styrene-conjugated diene block copolymer, soft¬ ening agents, olefinic resins, peroxide-curable olefinic rubber, an uncrosslinked hydrocarbon rubber and inorganic fillers, in which the peroxide-curable rubber is partially crosslinked. Although the above-mentioned compositions possess good properties as thermoplastic elastomers (TPEs), in com¬ parison to polyurethane (Pϋ) type elastomers they suffer from inadequate high temperature physical properties and inadequate gloss for a high quality appearance. The present invention prevents the decrease in stiffness with increased temperature and improves the gloss of molded parts for a high quality appearance, without loss in the properties of olefinic TPEs. SUMMARY OF THE INVENTION A method of producing compounds in which the rubber phase contains a polyolefin and a halobutyl rubber, which is partially crosslinked, to which composition is then added additional polyolefin and a vulcanizable olefinic rubber, which is then further crosslinked using organic peroxides, and then blended with a styrenic rubber. The TPE compounds incorporate (A) polypropylene 10-90 weight parts (wt. pts.), (B) halobutyl rubber 90-10 wt. pts. (where (A) + (B) = 100), (C) an olefinic rubber 10-120 wt. pts., (D) mineral oil softener 5-120 wt. pts., which are then treated thermally in the presence of (E) MOx and/or MCI, to which composition of 100 weight parts is added (F) polyolefin 100-600 wt. pts., and (G) a vulcanizable olefinic rubber 50-500 wt. pts. The resulting blend is then thermally treated with (H) organic peroxide(s), to which blend of 100 wt. pts. is then added and uniformly dispersed (I) 5-150 wt. pts. of styrenic rubber. DETAILED DESCRIPTION (A) Polypropylene (PP) PP suitable for use in this invention includes homo- polymer or copolymer with ethylene, 1-butene, 1-pentene, 1-hexene or 4-methylpentene or other alpha-olefins with propylene as the main component, including random or block copolymers. Melt flow rate (MFR) is about 0.3-60 g/10 min, preferably 1-40, most preferably 3-30. Component A of the composition has the highest melting point of polyolefins, and imparts heat resistance and improved mechanical proper¬ ties to the compound. (B) Halobutyl Rubber For purposes of this invention halobutyl rubber means halogenated butyl rubber. The halogen can be chlorine or bromine, usual content is 0.5-4.0 wt%. It is preferable that this component has a Mooney Viscosity, ML 1 + 8 (100 β C) of about 30-100 and 0.5-4.0 mol% unsaturation. Halobutyl rubber can be crosslinked using MOx and/or MCI, and exists as a dispersed crosslinked rubber phase, imparting abrasion resistance, impermeability and "anti-slip properties" to the compound. (C) Olefinic Rubber Rubber in which two or more of: ethylene, propylene, butene, 1-hexene, 4-methyl-l-pentene, etc. are copolymerized (e.g., ethylene propylene rubber, EPR) or rubber in which two of the above monomers (preferably ethylene and propy¬ lene) are polymerized with dicyclopentadiene, 1,4-hexadiene, cyclooctadiene, methylene-norbornene or ethylidenenorbornene (ENB) or conjugated dienes such as butadiene or isoprene. The preferred olefinic rubber has Mooney Viscosity, ML 1 + 8 (127°), of 5-300, Iodine Value up to 30, and 35-85 wt% ethy¬ lene content. Such olefinic rubber may be polyisobutylene, butyl rubber, etc. The olefinic rubber is present in the compound as a non-crosslinked rubber, and imparts flexibility, flowability and also acts as a binder at the interface of (A) and (B), improving tensile strength and elongation. (D) Mineral Oil Softener Suitable materials include hydrocarbon petroleum fraction which lessens the hardness of vulcanized rubber. Included are paraffinic, naphthenic, and aromatic types. Among these, aromatic oils have a detrimental effect on paintability, and are unsuitable for use in materials which will be painted. (E) Vulcanizing Agents Metal oxides (MOx) including zinc oxide, magnesium oxide, lead oxide, calcium oxide, etc., but zinc oxide is preferred. Among metal chlorides (MCI) are zinc chloride and stannic chloride. It is also desirable to use magnesium oxide as an accelerator, to avoid corrosion of molds due to generation of free halogen. The amount of vulcanizing agents relative to 100 parts of (A) + (B) + (C) + (D) should be about 0.2-10 parts, preferable 1 to 5 parts. (F) Polyolefin Polyolefin useful in this invention include homo- or copolymers of two or more of ethylene, propylene, 1-butene, 1-ρentene, 1-hexene, 4-methyl-l-pentene, or copolymers of vinyl esters, unsaturated carboxylic acids or their deriva¬ tives with any of the above. Random or block copolymers are encompassed. Melt flow rate, MFR (at 190°C, but 230°C for propylene-based polymers) should be in the range of about 0.1-20 g/10 min. for ethylene-based and about 15-60 g/10 min. for propylene-based polymers. Also, two or more of the above polyolefins may be combined. Preferred among the above are low density polyethylene (LDPE), linear low den¬ sity polyethylene (LLDPE), medium-density polyethylene (PE) or high density polyethylene (HDPE), polypropylene (PP) , or random or block copolymers with propylene as the major com¬ ponent. The presence of polyolefin improves the flowability or paintability of the compounds of the present invention without detriment to rubber elasticity. Since (F) and (A) have a similar function, these components can be added in various ratios. However, the beneficial effect of (F) is particularly observed when it is used with the previously dynamically vulcanized blend of (A)-(D) (in other words heat treated with mixing in the presence of vulcanizing agents). (G) Vulcanizable Olefinic Rubber Useful materials include olefinic rubber which can be crosslinked through mixing and heating to decrease or elimi¬ nate flow of the rubber. For example, ethylene propylene (EP) copolymer rubber (EPR), ethylene-butadiene copolymer rubber, ethylene-nonconjugated diene copolymer rubber, etc. are included. Among these, EPR and EP-ENB (ethylidene norbornene) rubber are preferred. The vulcanizable rubber should have a Mooney Viscosity of'ML 1 + 8 (127°C) of about 5-300 and an iodine value of less than 30. In the final composition, the vulcanizable olefinic rubber is present as a partially crosslinked rubber phase, improving stiffness at elevated temperature. (H) Organic Peroxides The organic peroxides useful for crosslinking of the olefinic rubber are those with a half-life decomposition temperature of 160-220°C; for example di-t-butyl peroxide, dicumyl peroxide, benzoylperoxide, 2,5-dimethyl-2,5-di-(t- butyl peroxy) hexane-3, 2,5-dimethyl-2,5-di(t-butyl peroxy) hexane. In addition, for the treatment with peroxide, it is desirable to use an accelerator such as p,p*-dibenzoyl- quinone dioxime. The organic peroxide is used to partially crosslink the composition of the vulcanizate treated with (E) together with the polyolefin and the vulcanizable - 1 - olefinic rubber, giving improved high temperature stiffness. The accelerator is included for the purpose of carrying out the partial crosslinking reaction smoothly and uniformly. (I) Styrenic Rubber Random or block copolymer of styrene with butadiene, isoprene, etc. Examples include styrene butadiene rubber (SBR), styrene butadiene styrene (SBS), styrene isoprene styrene (SIS), hydrogenated SBS (SEBS), and hydrogenated SIS. The styrenic rubber desirably has a Mooney Viscosity, ML 1 + 4 (100°C) of about 10 to 200, and styrene content of about 5-70 wt%. Styrenic rubber improves the gloss of the final com¬ pound without detriment to the properties of olefinic TPEs. This effect of (G) is particularly observed when added fol¬ lowing the partially dynamically vulcanized blend of (A)-(D). The effect of the styrenic rubber is observed when it is added to the partially vulcanized blend of (A)-(H), fol¬ lowing preparation of the blend composition (A)-(H), and not in other combinations of these components. (J) Other (Optional) Components As necessary for the particular end use, other optional components can be added to the composition includ¬ ing ethylene propylene rubber, polybutadiene-type rubbers, ethylene propylene diene monomer (EPDM) rubber or oil- resistance enhancing nitrile rubbers or other synthetic or natural rubbers. Also, modified polyolefins reacted with unsaturated carboxylic acids or their derivatives, e.g., maleic anhydride, endo-bicyclo-(2,2,l)-5-heptene-2,5-dicar- boxylic anhydride may be incorporated. Other components such as antioxidants, UV absorbers, metal aging retardants, antistatic agents, lubricating agents, electrical property improvers, process aids, flame-retardants or coloring agents and inorganic fillers such as talc, barium sulfate, mica, and calcium silicate fillers may be added as required. These may be added at any stage of the manufacturing process. Ratios of Components Ingredients are expressed on the basis of weight parts. The ratios of (A), (B), (C), (D), (E) are: (A) 10-90 pts., preferably 20-70 pts.; (B) 10-90 pts., preferably 30-80 pts.; with (A) + (B) = 100; (C) 10-120 pts., preferably 10-100 pts., (D) 5-120 pts., preferably 5-100 pts. Also, the incorporation of (D) in the Second Stage (to be defined below) is desirably 1-60 pts. (E) (The crosslinking agent) should be used at 0.2-10 pts., preferably 1-5 pts., relative to 100 pts. of (A)-(D) . When (A) is less than 10 pts., the compounds lose mechanical strength and heat resistance is poor. When (A) is greater than 90 pts., hardness and compression set are high and elastomeric properties are lost. When (C) is less than 10 pts., flexibility is low and flowability is poor. In addition, the co patibilization of (A) and (B) becomes poor. On the other hand, when (C) is greater than 120 pts., mechanical strength decreases and compression set increases. When (D) is less than 5 pts., flexibility is inade¬ quate and when (D) is greater than 120 pts., paintability becomes poor, mechanical strength decreases and the com¬ pounds become sticky. The amounts of components (F) and (G) to be used with 100 pts. of the vulcanizate crosslinked with (E) are: (F) 100-600 pts., preferably 200-500, and (G) 50-500 pts., pre¬ ferably 60-400 pts. The amount of (H) (organic peroxide) relative to 100 pts. of the partial vulcanizate (A-E) + (F) + (G) is: 0.005-1 pt., preferably 0.01-0.3 pts. The accelerator should be used at a level of 0.005-1 pt., pre¬ ferably 0.01-0.4 pts. When (F) is less than 100, flowabil¬ ity and paintability are inadequate, while if (F) is greater than 600 pts., the flexibility and rubbery properties of the composition are lost. When (G) is less than 50 pts., flex¬ ibility and molding flowability are low, and in addition co patibilization with the partial vulcanizate from (E) is poor. On the other hand, when (G) is greater than 500 pts., mechanical properties decrease and compression set becomes large. When the amount of (H) is less than the above-men¬ tioned lower bound, the crosslinking of the vulcanizable rubber is inadequate and good high temperature stiffness is not obtained. When (H) exceeds the high end of the range, the flowability of the compound decreases as the degree of crosslinking increases. It is not desirable for the accel¬ erator to exceed the mentioned range because the crosslink¬ ing reaction proceeds too far, resulting in low flowability, and in addition unreacted agent remains in the compound, changing its physical properties. The amount of (I), relative to 100 pts. of the vul¬ canizate from (H), should be 3-200 pts. preferably 5-150 pts. When (I) is less than 3 pts., the gloss of the com¬ position is not improved, while for (I) greater than 200 pts. the physical properties become poorer. It is desirable that other optional components be in the range 0-30 wt.%. Method of Manufacturing the Composition First, (A), (B), (C), (D), and vulcanizing agent (E) (MOx and/or MCI), and other components as necessary, are mixed and thermally treated, i.e. blended in the melt. The blending should be done at a temperature at which all com¬ ponents melt/flow, usually 160-250°C and desirably 170-220°C for 1-10 min., desirably 3-5 min. In this way, a composi¬ tion in which the dispersed component (B) only is selec¬ tively crosslinked is obtained. The melt blending may be carried out in equipment such as pressure kneaders, Banbury Mixers, screw-type ex¬ truders, etc. (This operation is referred to as the First Stage.) Next, (F), (G) and (H) (organic peroxide plus acceler¬ ator) are added to the blend and melt blending is carried out. For example, pellets of the above components can be pre ixed in a Henschel mixer, ribbon blender, etc., then melt blended in an extruder, Banbury or kneader, etc. At this time, various stabilizers, coloring agents, inorganic fillers, softening agents, etc. can be added as required. (This is referred to as the Second Stage.) Finally, to the above blend is added uniformly com¬ ponent (I). To achieve uniform mixing, these can be pre¬ mixed in a Henschel mixer or ribbon blender, etc,, followed by melt blending in an extruder, Banbury or kneader, etc. At this time, other materials such as synthetic rubbers, modified polyolefins, various stabilizers, coloring agents and inorganic fillers can be added. (This is referred to as the Third Stage.) In the composition produced by the method of this invention, (B) is partially crosslinked, so compatibility is excellent, and without loss of rubbery properties, the mechanical strength is high, and impact strength, especially at low temperature, is improved. In addition, due to the successive vulcanization with components (F) and (G), and the uniform incorporation of (I), heat resistance, paint- ability adhersion, flowability and gloss are improved. Thus, there are no flow marks in large molded parts, and products have good high quality gloss. The composition of the present invention can be processed easily using conven¬ tional techniques for TPEs, such as blow molding, extrusion or injection molding, etc. The compositions of the present invention have a good balance of flexibility, strength and heat resistance, and are especially useful as materials for automotive parts, e.g., rack and pinion boots, hoses, side- moldings, spoilers and bumpers. EXAMPLES Test Methods (1) MFR: JIS K7210 (wt. 2.16 kg, 230°C). (2) MI: JIS K7210 (wt. 2.16 kg, 190°C). (3) Tensile strength and elongation at break: JIS K7113. (4) Bending modulus: JIS K7203. (5) Izod impact: JIS K7110. (6) Gloss: JIS K7105, measured on 60° plane. (7) Heat deflection temperature: JIS K7207. (8) Processability: (a) Conditions Inj. molder: Mitsubishi Natco 350 MV XL40 Inj. molding temperature: 230°C Inj. molding pressure: primary 800 kg/cm^ Inj. molding pressure: secondary 500 kq/cm- Inj. time: 13 seconds Cycle: 38 seconds Gate: ride gate Part: 3 x 100 x 350 mm flat plate (b) Judgement Flow-marks 0: none Flow-marks D: very little Flow-marks X: many, severe ( 9 ) Paintability: ( a ) Primer method After test piece was cleaned in tri- chloroethylene (TCE) vapor for one minute , pr imer ( "Pla-gloss , " Nippon Yushi Co. ) was painted and treated at 120 °C for 30 min¬ utes . Then , over this layer was painted upper coating ( "Flexene 101 , " Nippon Paint Co . ) , and treated at 120 °C for 30 minutes . (b) Plasma method After test piece was cleaned in TCE vapor for one minute, it was plasma treated (O2 plasma, 1.0 KW x 1.0 torr x 60 seconds) and painted with an upper coating ("Flexene 101," Nippon Paint Co.), and treated at 120°C for 30 minutes. (c) Evaluation Initial adhesion: according to JIS K5400 test, "tile". Resistance to warm water: Appearance and "tile" test after immersion in 40°C water for 240 hrs. (10) Gel Fraction: One g. of sample was placed in a 100 mesh gold screen and boiled in hot xylene for 12 hours.. Then, gel fraction was determined as the remaining xylene insolubles after vacuum drying for 24 hours. Examples 1-16, and comparative examples (comp. ex.) 1, 2, 3. Materials Used (A) Propylene-ethylene block copolymer (MFR = 15.0 g/10 min., ethylene 7 wt%), referred to as "PP-Block-1." (B) Chlorobutyl rubber (ML 1 + 8 (100) = 50, chlorine content 1%, 2 mol% unsat.), referred to as "CIIR." (C) ENB-EPDM (ML 1 + 8 (127) = 35. Iodine Valve = 4.0, ethylene = 65 wt%), referred to as "EPDM-1." (D) Naphthenic process oil (viscosity - specific gravity coefficient = 0.880), referred to as "softener." (E) ZnO, MgO (halogen accelerator). (F) Propylene-ethylene block copolymer, (MFR = 40 g/10 min., ethylene content - 7%), referred to as "PP-Block-2") . (G) ENB-EPDM (ML 1 + 8 (127°C) = 45, Iodine Valve = 3, referred to as "EPDM-2"), EPR (ML 1 + 4 (100°C) = 24, ethylene content = 73%, referred to as "EPR"). (H) Organic peroxide (Nippon Yushi Co., "Perhexyne 2,5B"), P,P'-dibenzoylquinone dioxime (acceler¬ ator) . (I) SEBS block copolymer - Shell Chemical Co., Kraton G1657, solution viscosity at 25 β C = 1100 cp, 20 wt% toluene solution, referred to as "SEBS"; SBR - JSR 1778N, ML 1 + 4 (100) = 46, referred to as "SBR." Other: Talc (silane treated, avg. dia. 2.5 microns), EPDM rubber, (ML 1 + 8 (127) = 45, iodine value = 3, ethylene = 65 wt%) , referred to as "EPDM-2"; EPR (ML 1 + 4 (100) = 24, ethylene 73 wt%), referred to as "EPR", MA - modified propy¬ lene-ethylene block copolymer (MA content 0.5 wt%), referred to as "CMPP"; acrylonitrile-buta- diene rubber (ML 1 + 4 (100) = 56, AN content = 35%), referred to as "NBR". Preparation of the Composition (A)-(D) and talc were combined in the proportions shown in Table 1, and to 100 pts. of the resulting composi¬ tion 2 pts. zinc oxide (ZnO) and 0.5 pt. magnesium oxide (MgO) were added and melt blended in a Banbury Mixer at 170°C for 3 minutes. The resulting composition was sheeted, cut, and pelletizied (Stage 1). Next, to the pellets obtained in Stage 1 were added components (F) and (G) in the proportions shown in Table 1, to 100 pts. of this mixture were added 0.3 pts. of organic peroxide and 0.36 pts. of accelerator. After premixing in a Henschel mixer, this was extruded in a twin-screw extruder at 200°C (Stage 2) . Finally, to the pellets obtained in Stage 2 were added (I), EPR and CMPP as shown in Table 1, and after pre¬ mixing in a Henschel mixer this was fed to a twin-screw extruder and extruded at 200°C to obtain the final composi¬ tion (Stage 3) . The characteristics of the resulting compounds are shown in Table 1. In addition, in examples 1-5 the gel con¬ tents were measured and the results, given in Table 1, indicate that partial crosslinking took place. For compari¬ son. Comparative Example 1 shows a case in which no styrenic rubber was added in Stage 3, and Comparative Example 2 shows a case in which SEBS was added in place of EPR in Stage 2. Comparative Example 3 shows a case where vulcanization was not carried out in Stage 2. Resulting properties are shown in Table 1. Table 1 Ex. 1 Ex. 2 Ex. 3 Ex. 4 Ex. 5 Ex. 6 Ex. 7 Ex. 8 Ex. 9 Ex. 10 Ex. 1 Stage 1 PP-Block-1 (pts.) 50 50 50 50 50 50 50 50 50 50 50 CIIR H H 50 50 50 50 50 50 50 50 50 50 50 EPDM-1 M M 100 100 100 100 100 100 100 100 100 100 100 Softener H H 94 94 94 94 94 94 94 94 94 94 94 Talc H H 19 19 19 19 19 19 19 19 19 19 19 Stage 2 PP-Block-2 (Pts.) 700 700 700 700 700 700 700 700 700 700 700 EPR EPR EPR EPR EPR EPR EPDM EPDM EPR EPR EPR (pts.) 400 400 400 400 400 400 400 400 400 400 400 • Softening Agent 5 Stage 3 SEBS SEBS SEBS SEBS SEBS SEBS SEBS SEBS SEBS SEBS SEBS 75 160 350 610 2,120 610 160 610 610 610 350 Other Components CMP Fundamental L Properties MFR (g/10 min. ) 7 9 12 15 18 17 8 13 11 12 13 Flex. Mod. § 23°C (kg/cm 1 2 ) 2,800 2,900 2,900 2,900 2,900 2,900 3,000 3,000 3,300 3,300 3,100 Flex. Mod. e 8o°c (kg/cm : 2 ) 1,130 1,120 1,120 1,100 1,080 1,100 1,100 1,100 1,120 1,130 1,100 Tens. § Bπ -ak (kg/cm^) 130 125 110 110 110 108 130 125 125 130 120 Elong. @ Bireak («) 300+ 300+ 300+ 300+ 300+ 300+ 300+ 300+ 300+ 300+ 300 Room Temp. IZOD NB NB NB NB NB NB NB NB NB NB NB (kg-cm/cm) β -40°C 58 69 75 77 80 80 72 78 45 73 70 Heat Distort. Temp. (°C) 60 58 55 52 51 50 59 56 59 62 52 Processability Flow Marks 0 0 0 0 0 0 0 0 0 0 0 Gloss (%) 45 58 62 75 82 77 73 75 80 80 65 Paintabilii -Y Primer Method 100/100 100/100 100/100 100/100 100/100 100/100 100/100 100/100 100/100 100/100 100/100 Plasma Method 100/100 100/100 100/100 100/100 100/100 100/100 100/100 100/100 100/100 100/100 100/100 Gel Fracti< 3 (%) 57 54 47 47 24 ——— -»-*— __-.—. —•—— ——— —_—. NB " No Break . Table 1 (Continued Com araitive Exampli 28 Stage 1 Ex. 12 Ex. 13 Ex. 14 Ex. 15 Ex. 16 1 2 3 PP-Block-1 (pts.) 50 50 60 40 60 50 50 50 CIIR " " 50 50 40 60 40 50 50 50 EPDM-1 " " 100 100 110 100 110 100 100 100 Softener " " 94 94 94 94 94 94 94 94 Talc " M 19 19 19 19 19 19 19 19 Stage 2 PP-Block-2 (pts.) 700 700 700 700 700 700 700 _____ EPR EPR EPR EPR EPDM-2 EPR (pts.) 400 400 400 400 400 400 SEBS (pts.) 350 Stage 3 SEBS SEBS SEBS SEBS SEBS 350 610 610 610 610 Other Components NBR CMPP 160 2 Fundamental Properties MFR (g/10 min.) 12 15 17 13 15 5 3 0.1 Flex. Mod. θ 23°C (kg/cm 2 ) 3,100 3,200 3,500 3,000 3,150 2,800 2,700 2,900 Flex. Mod. ~ 80 β C (kq/cm 2 ) 1,100 1,120 1,200 1,030 1,200 1,140 1,150 820 Tens. ~ Break (kg/cm 2 ) 120 115 135 105 137 115 100 95 Elong. ~ Break (%) 300+ 300+ 300+ 300+ 300+ 300+ 300+ 300+ Room Temp. IZOD NB NB NB NB NB NB NB NB (kg-cm/cm) § -40"C 72 69 72 78 74 52 46 20 Heat Distort. Temp. (°C) 53 55 58 50 51 60 58 51 Processability Flow Marks 0 0 0 0 0 0 0 X Gloss (%) 53 83 78 73 75 30 30 25 Paintabllity Primer Method 100/100 100/100 100/100 100/100 100/100 100/100 100/100 90/100 Plasma Method 100/100 100/100 100/100 100/100 100/100 100/100 100/100 95/100 NB No Break.

Claims: CLAIMS What is claimed is: 1. A method of manufacture of thermoplastic elastomer comprising thermally blending a com¬ position comprising (A) polypropylene 10-90 weight parts, (B) halobutyl rubber 90-10 weight parts, wherein (A) + (B) = 100 weight parts, (C) olefinic rubber 10-120 weight parts, and (D) min¬ eral oil softening agent 5-120 weight parts, in the presence of (E) metal oxides and/or metal chlorides, and blending 100 weight parts of said thermally treated composition with (F) polyolefin 100-600 weight parts, and (G) vulcanizable ole¬ finic rubber 50-500 weight parts, and further thermally treating said blend of (A) through (G) in the presence of (H) organic peroxide, and homogeneously blending 100 weight parts of the resulting composition with (I) styrenic rubber 5-100 weight parts.

Inventors: BABA ISAO, KOMATSU MASATO, YAMAMOTO NOBORU, BABA, ISAO, KOMATSU, MASATO, YAMAMOTO, NOBORU
Applicants: TOA NENRYO KOGYO KK, TOA NENRYO KOGYO K.K.
Application year: 1987
Main classification: C08L9
IPC codes: C08K3, C08K5, C08L1, C08L7, C08L9, C08L21, C08L23, C08L27, C08L33, C08L51, C08L53, C08L77, C08L91, C08L101