PROCESS FOR PREPARING A CATALYST COMPONENT FOR USE IN A PROPYLENE POLYMERIZATION CATALYST

Abstract: A catalyst component for an alpha-olefin polymerization catalyst (comprising an organoaluminium compound, an external electron donor and a solid catalyst component obtained by reaction of a magnesium-containing compound with a titanium halogen compound) is prepared by the steps of: (a) precipitating a water-soluble magnesium compound from an aqueous solution thereof using an alkali; (b) separating the solid magnesium component and dissolving it in hydrochloric acid; (c) evaporating the resultant solution until dry; (d)heating the salt mixture obtained at 130 to 150°C; (e) dissolving the magnesium component in ethanol; (f) drying the ethanolic solution of the magnesium component by periodic azeotropic distillation; (g) precipitating a solid carrier component from the ethanolic solution; and (h) reacting the solid carrier component with a titanium halogen compound in the presence of an internal electron donor or without an electron donor.

Description: The invention concerns catalysts components for alpha olephine-poly­ merizing catalysts which consist of an organoaluminium compound, an electron donor and a solid catalyst component which has been obtained when a compound containing magnesium has reacted with a titanium halogen compound. The invention also concerns a procedure for manufacturing these catalyst components and a procedure for polymerizing alpha olephines, in particular propylene, making use of said catalyst components. For polymerizing alpha olephines, prior art knows catalysts with high activity which have been manufactured of an aluminium alkyl compound, of an electron donor and of a halogenated titanium compound on a carrier substance comprising various magnesium compounds. For magnesium compound usually chlorinated magnesium compounds have been used, which may be for instance water-free magnesium chloride alone or together with other magnesium com­ pounds, or an organic magnesium compound which has been prepared by halogenating organic magnesium compounds with the aid of compounds containing chlorine. In polymerizing catalysts of this type, the properties of the solid carrier component have a significant influence on the properties of the ultimate catalyst, for instance on its activity. These proper­ ties can be substantially influenced through the mode of manufac­ turing the carrier component. The present invention concerns catalyst components in which the carrier component has been prepared from water-soluble compounds containing magnesium, which may be natural minerals or synthetic minerals. There is nothing novel in itself in the use of magnesium minerals for starting material in preparing inert carrier compo­ nents for Ziegler-Natta catalysts to the purpose of polymerizing olephines. It has turned out to be difficult to manufacture, from various magnesium compounds and from minerals containing them, active Ziegler-Natta catalysts, in particular those for the polymerizing of propylene, because in these processes the catalysts are highly sensitive to moisture and to the crystal water contained in the carrier. Minimal quantities of crystal water already reduce the activity of the catalyst significantly. The present invention relates to catalyst components for those alpha olephine-polymerizing catalysts which consist of an organo­ aluminium compound, an external electron donor and a solid catalyst component which has been obtained when a solid carrier component containing magnesium has reacted with a titanium halogen compound and which are free of the drawbacks mentioned and, therefore, are fit to be used in polymerizing propylene. The catalyst component of the invention is characterized in that it has been composed by making a solid carrier component, which has been prepared by precipitating a water-soluble magnesium compound from its aqueous solution with the aid of an alkali; (b) by separating the solid magnesium component and dissolving it in hydrochloric acid; (c) by evaporating the solution until dry; (d) by heating the salt mixture thus obtained at 130 to 150°C; (e) by dissolving the magnesium component in ethanol; (f) by drying the ethanol solution of the magnesium component with the aid of periodic azeotropic distillation; and (g) by precipitating the solid carrier component from the ethanol solution react with a titanium halogen compound in the presence of an internal electron donor or without electron donor. The invention also concerns a procedure for manufacturing catalyst components for alpha olephine-polymerizing catalysts which consist of an organoaluminium compound, an external electron donor and a solid catalyst component containing magnesium which has been obtained when a solid carrier component containing magnesium has reacted with a titanium halogen compound. The procedure of the invention is characterized in that said catalyst component is produced by making a solid carrier component which has been prepared (a) by precipitating a water-soluble magnesium compound from its aqueous solution with the aid of an alkali; (b) by separating the solid magnesium component and dissolving it in hydrochloric acid; (c) by evaporating the solution until dry; (d) by heating the salt mixture thus obtained at 130 to 150°C; (e) by dissolving the magnesium component in ethanol; (f) by drying the ethanol solution of the magnesium component with the aid of periodic azeotropic distillation; and (g) by precipitating the solid carrier component from the ethanol solution react with a titanium halogen compound in the presence of an internal electron donor or without electron donor. The catalyst component of the invention and the carrier component used therein afford several advantages over carrier components containing magnesium which have been prepared by conventional synthesis techniques. For instance, in manufacturing the carrier component it is possible to use an open reaction vessel, and because the synthesis is not sensitive to oxygen and moisture an inert nitrogen atmosphere is not absolutely indispensable in the synthesis. In comparison with carriers which have been prepared by halogenating an organic carrier component containing a magnesium compound, the carrier component of the invention is easier and less expensive to prepare. For chlorinating agent, hydrochloric acid is the cheapest possible substance, and in the manufacturing process conventional aqueous solutions of hydrochloric acid may be used because the crystal water can be removed in a simple manner. Moreover, in preparing the carrier component hydrochloric acid can be used in excess because hydrochloric acid is easy to remove in the next synthesis step. One more advantage of the catalyst compo­ nent and the procedure of the invention is that any magnesium products which may be formed as byproducts, such as MgOHCl, and which impair the properties of the catalyst, escape efficiently from the catalyst component of the invention. As taught by the invention, aqueous magnesium salts of any kind can be used in preparing active catalyst components for polymerizing olephines, in particular propylene. Thus, catalyst components may be prepared for instance from the following magnesium compounds: MgSO₄, Mg(NO₃)₂, MgAc₂, MgNO₂, MgClO, MgClO₃, MglO₄, Mg(CHO₂)₂, Mg(CH₃COO)₂, Mg(C₂H₇COO)₂, MgBr₂, MgBrO₃, Mg(CN)₂, MgI₂, Mg(IO₃)₂, etc. When preparing the catalyst component of the invention, a magnesium compound is first dissolved in water. Thereafter the pH of the solution is raised by adding an alkali to the solution, for in­ stance NaOH and KOH. Most appropriately the alkali is added in the form of an aqueous solution of which the concentration may vary from 0.1 N to saturated solution. The use of concentrated alkali solutions is advantageous because in that case less water will have to be removed from the system. Such a quantity of alkali is added that the solution becomes clearly alkaline, advantageously up to pH 10, whereby the magnesium component will precipitate from the solution as a hydroxide. The magnesium compound is separated from the solution by centri­ fuging or by allowing it to settle. If desired, the precipitate may be washed with water once or several times. Thereafter, it is suspended in water or alcohol. For alcohol one may use for instance methanol, ethanol or propanol. Thereafter, it is suspended in water and such a quantity of hydrochloric acid is added that the pH of the suspension is lowered to 2 or less. Hydrochloric acid is advantageously added in the form of aqueous solution. The concentration of the solution may vary from 0.1 N to saturated solution. Magnesium hydroxide is completely dissolved when the pH of the suspension has gone down far enough. After the magnesium component has been dissolved in hydrochloric acid, the solution is evaporated in the next step until dry. At the same time the excess of hydrochloric acid evaporates. Subsequent to evaporation, the salt mixture is slightly heated at 130 to 150°C. The requisite heating time ranges from 0.5 to 1.5 hours, most properly about 1 hr. Excessive temperature causes decomposition of the magnesium component into magnesium chloride and hydroxide, whereby the yield is lowered. After the heating, the salt mixture is dissolved in ethanol, where­ by the magnesium component fit to serve as a carrier dissolves completely. The undissolved constituents may be separated by centrifuging or filtering from the ethanol solution. Any insoluble magnesium compounds produced in the calcinating process, such as magnesium chloride for instance, can in this manner be separated quite simply. The clear ethanol solution thus obtained now contains exclusively magnesium component with crystal water. Removal of the crystal water is indispensable for obtaining an active catalyst component. As taught by the invention, the crystal water is removed by distil­ lation, with the aid of periodic azeotropic distillation. During this distillation an azeotropic mixture of alcohol and water escapes from the solution, whereby the water quantity is reduced. By adding new water-free ethanol to the solution and by repeated distillation, total removal of crystal water from the magnesium component is accomplished. The number of azeotropic distilling runs required depends on the amount of water present in the solution and on the intended use of the catalyst. If the catalyst is intended to be used in polymeriz­ ing ethylene, fewer runs are needed, for instance 1 to 5 runs. When manufacturing a carrier component for propylene polymerizing, nearly crystal water-free carrier is required, and experience has taught that this is achieved if the number of distilling runs is 8 to 15, advantageously 10 to 12. The water content of the carrier component can thus be brought down to 0.3 moles of crystal water, which can be considered the upper limit for propylene-polymerizing catalysts. After drying out the crystal water, precipitation of the magnesium carrier component is effected by transferring the dried ethanol solution into a cold solvent, whereby the magnesium component will precipitate. Suitable solvents are common organic hydrocarbons used as solvents. Heptane is a highly appropriate solvent for the reason that its boiling point is high enough so that in the titanizing step which has to be carried out subsequently titanium has time to react, and on the other hand it is low enough to avoid melting of the carrier component in the titanizing step. When the ethanol solution containing magnesium component is added into cold heptane, the carrier component is precipitated in finely divided form. After washing and drying, the carrier component is titanized with the aid of titanium tetrachloride in a manner known in itself in the art, for producing the catalyst component. Titanizing may be accomplished for instance in that the solid carrier component is mixed with a titanium halogen compound once or several times. Before, during or after the titanizing process the catalyst component may furthermore be treated with the aid of an internal electron donor compound. The titanizing is preferably accomplished in two steps between which may be added internal electron donor, which is usually an amine, ether or ester of its tye. A suitable donor is, for instance, diisobutylphthalate, of which the quantity may be 0.05 to 0.3, most appropriately 0.2, mol/mol Mg. In the first step a low temperature is to be recommended, e.g. below 0°C, preferably below ⁻20°C. The second titanizing step may be carried out at higher temperature, e.g. at 85 to 110°C, a reaction time of 1-1.5 hours being sufficient. The solid reaction product is then separated from the liquid phase and washed with hydrocarbon solvents to remove impurities and derivatives. The catalyst component may be dried in light vacuum or in nitrogen gas at room temperature, or at slightly elevated temperature, and it may be homogenized by grinding it in a ball mill. The catalyst component of the invention may then be used to poly­ merize alpha olephines by allowing it to come into contact with an Al compound and an external compound releasing electrons. In the role of external compounds releasing electrons may be used, for instance, amines, ethers, esters (preferably alkyl and arylesters of aromatic carboxylic acids) or silane compounds (alkyl/aryl silanes), examples of such being, among others, the methyl and ethyl esters of benzoic, toluic and phthalic acid, isobutylesters of phthalic acid, triethoxysilane, etc. Said electron donors are compounds which are able to enter complexes with Al alkyls. The stereo-specificity of the catalyst can be improved with their aid. The external compound releasing electrons, or donor, and the Al alkyl are mixed together, the molar proportion of the compound releasing electrons to the Al compound being about 20 and the Al/Ti molar proportion being between 10 and 300, depending on the polymerizing system. Polymerizing may be carried out either as slurry or bulk polymerizing, or in the gas phase. Catalyst components and catalysts prepared as taught by the inven­ tion may be used to polymerize alpha olephines, such as ethylene, propylene and butylene, by the slurry, bulk and gas phase methods, but the catalyst components of the invention are particularly well suited for use in polymerizing propylene because in them the quantity of crystal water in the carrier substance is singularly low and, as a result, the activity of the catalysts is particularly high especially regarding polymerizing of propylene. The invention is more closely illustrated in the following examples. Example 1 25,6 g Mg(NO₃)₂.6H₂O were suspended in 100 ml water. 8.0 g NaOH were added into the suspension in 100 ml water. The mixture was centrifuged for 10 min. at 3000 rpm, washed twice with water, and thereafter titrated with conc. hydrochloric acid to pH 1.5. There­ after the solution was evaporated until dry, and the dried salt was calcinated for 1 hr at 140°C. The salt was poured, with mixing, into 200 ml ethanol. The solution was centrifuged for 10 min. at 3000 rpm. The clear solution was poured into a three-necked flask (1 liter), in which the drying of the ethanol/carrier component was carried out by azeotropic distillation. The drying process consumed 400 ml absolute ethanol (moisture content < 100 ppm). The distilla­ tion took place in a slow nitrogen flow. The dry (moisture content < 400 µg H₂O/0.1 ml) hot ethanol/carrier solution was transferred, with mixing, into 500 ml cold heptane, whereby the carrier compo­ nent crystallized. The extra ethanol was washed off with two heptane washings, whereafter the carrier component was transferred into cold titanium tetrachloride (400 ml, -20°C). After the mixture had warmed up to room temperature, 0.1 mol/mol Mg of diisobutyl­ phthalate were added thereto. The mixture was boiled for 1 hr at 110°C, whereafter the catalyst component was allowed to settle, and the TiCl₄ solution was exchanged for new solution and the treatment repeated. The completed catalyst component was washed with heptane and dried with nitrogen. The yield was 0.6 g, and the catalyst contained: Mg 18.0%, Ti 4.0%, and Cl⁻ 59%. The carrier component prepared in the way just described was applied in propylene polymerizing, adding into a 2-litre polymeriz­ ing reactor catalyst which had been prepared by mixing, as alumini­ um alkyl compound, triethylaluminium and, as Lewis compound, di­ phenylmethoxysilane (Al/donor mole proportion: 20) in 50 ml heptane and admixing to this, after 5 minutes, carrier component so as to make the Al/Ti molar proportion 200. Polymerizing was carried out in conditions as follows: propylene partial pressure 9.0 bar, hydrogen partial pressure 0.3 bar, temperature 70°C, and polymeriz­ ing time 3 hrs. The activity of the catalyst was found to be 4.6 kg PP per g of catalyst in 3 hours. Example 2 21.4 g Mg(CH₃CO₂)₂.4H₂O were suspended in 100 ml H₂O, and 8.0 g NaOH/100 ml H₂O were added. The produced Mg (OH)₂ suspension (pH 10) was centrifuged for 10 min. at 3000 rpm, washed twice with water, and the centrifuging process was repeated. The precipitate was suspended in 100 ml water and titrated with conc. hydrochloric acid (38%) to pH 1.5, whereafter the solution was evaporated until dry, and the dried salt was calcinated for 1 hr at 140°C. The salt was poured, with mixing, into 200 ml ethanol. The solution was centri­ fuged for 10 min. at 3000 rpm. The clear solution was poured into a three-necked flask (1 litre), in which the drying of the ethanol/-­ carrier component solution was carried out with the aid of azeo­ tropic distillation. The drying process consumed 600 ml absolute ethanol (moisture content less than 100 ppm). The distillation took place in a slow nitrogen flow. The dry (moisture content < 400 µg H₂O/0.1 ml) hot ethanol carrier component solution was transferred into 500 ml of cold heptane, with mixing, whereby the carrier component crystallized. The extra ethanol was washed off with two heptane washings, whereafter the carrier component was transferred into cold titanium tetrachloride (400 ml, -20°C). After the mixture had warmed up to room temperature, 0.1 mol/mol Mg of diisobutyl­ phthalate were added. The mixture was boiled for 1 hr at 110°C, whereafter the catalyst was allowed to settle and the TiCl₄ solu­ tion was exchanged for new solution and the treatment repeated. The completed catalyst component was washed with heptane and dried with nitrogen. The yield was 4.5 g, and the catalyst component contain­ ed: Mg 18.0%, Ti 3.5%, Cl⁻ 60.0%, and CH₃CO₂⁻ < 150 ppm. The catalyst was used to polymerize propylene as in Example 1, and its activity was then found to be 5.8 kg PP per g of catalyst in 3 hours. The bulk density of the polymer was 0.27 g/ml, isotacticity 91.7%, and particle distribution 90% in the range 0.1 to 1.0 mm. Example 3 25 g MgSO₄.7H₂O were suspended in 100 ml H₂O. 8.08 g NaOH were added into the solution in 100 ml water. Hereby, a suspension with pH 10 was obtained. The mixture was centrifuged for 10 min. at 3000 rpm, washed twice with water, and the centrifuging process was repeated. The water suspension of magnesium hydroxide was trans­ ferred into a decanter, and it was titrated with conc. hydrochloric acid to pH 1. Thereafter, the solution was evaporated until dry, and the dried salt was slightly (140°C) calcinated for 1 hr. The salt was poured, with mixing, into 200 ml ethanol. The mixture was centrifuged for 10 min. at 3000 rpm. The clear solution was poured into a three-necked flask (1 litre), in which drying of the ethanol/carrier solution was carried out with the aid of azeotropic distillation. The drying process consumed 600 ml absolute ethanol (moisture content < 100 ppm). The distillation took place in a slow nitrogen flow. The dry (moisture content < 400 µg H₂O/0.1 ml) hot ethanol/carrier solution was transferred, with mixing, into 500 ml cold heptane, whereby the carrier component crystallized. The extra ethanol was washed off with two heptane washings, whereafter the carrier component was transferred into cold titanium tetrachloride (500 ml, -20°C). After the mixture had warmed up to room tempera­ ture, 0.1 mol/mol Mg of diisobutylphthalate were added thereto. The mixture was boiled for 1 hr at 110°C, whereafter the catalyst component was allowed to settle and the TiCl₄ solution was once exchanged for new solution and the treatment repeated. The complet­ ed catalyst component was washed with heptane and dried with nitrogen. The yield was 1.5 g, and the catalyst component contain­ ed: Mg 16.0%, Ti 3.0%, Cl⁻ 54.0%, SO₄ 0.14%, and Na 0.30%. The catalyst was used to polymerize propylene as in Example 1, and its activity was 6.7 kg PP per g of catalyst in 3 hours. The bulk density of the polymer was 0.27 g/ml, isotacticity 90.5%, and particle distribution 90% in the range 0.1 to 1.0 mm.

Claims: 1. A process for preparing a catalyst component for use in an alpha-olefin polymerization catalyst, which process comprises: (a) precipitating a water-soluble magnesium compound from an aqueous solution thereof with the aid of an alkali; (b) separating the solid magnesium component and dissolving it in hydrochloric acid; (c) evaporating the resultant solution until dry; (d) heating the resultant salt mixture at 130 to 150°C; (e) dissolving the magnesium component in ethanol; (f) precipitating a solid carrier component from the ethanolic solution; and (h) reacting the said carrier compound with a titanium halogen compound in the presence of an internal electron donor or without an electron donor. 2. A process according to claim 1, characterised in that after evaporating the hydrochloric acid, the salt mixture is heated for 0.5 to 2 hours. 3. A process according to claim 1 or claim 2, characterized in that the water-soluble magnesium compound is precipitated by raising the pH up to at least pH 10 by means of sodium hydroxide or potassium hydroxide. 4. A process according to any one of the preceding claims characterized in that in the drying of the ethanolic solution, 1-15 periodic azeotropic distillations are effected. 5. An olefin polymerization catalyst comprising a catalyst component obtained by a process as claimed in any one of the preceding claims. 6. A process for polymerizing an olefin, especially propylene, using a catalyst as claimed in claim 5.

Inventors: GAROFF, THOMAS
Applicants: NESTE OY
Application year: 1987
Main classification: C08F4
IPC codes: C08F4, C08F10