WATER BASED COATING COMPOSITION AND POLYMER FILM COATED THEREWITH

Abstract: A water based antistatic coating composition comprising: a) at least one water soluble antistatic agent which is acceptable for food packaging polymer films; b) at least one water soluble or water dispersible film-forming polymer; and, c) a solution or dispersion-forming amount of water. When applied to a polymer film substrate, the foregoing antistatic coating composition forms, upon drying, an adherent antistatic coating.

Description: This invention relates generally to a water based antistatic coating composition and, in particular, to polymer films treated with an antistatic composition. U.S. Patent No. 2,063,987 describes the acylated and/or esterified derivatives of aliphatic amino carboxylic acids and the salts of these derivates formed on the amino group or the carboxylic acid group, whichever is free, as aqueous treating agents, in particular, for wetting, cleansing, sizing, de-electrification, prevention of acid fading of dyestuffs, creping and other treatments of textile filaments, threads, yarns, fabrics, etc. At present, N-acyl derivatives of N-methyl glycine (sarcosine) where the acyl group is lauroyl, oleoyl or derived from the combined fatty acids of coconut oil are approved as antistatic and/or as antifogging agents in polyolefin films used for packaging meat, fresh fruits and fresh vegetables (21 C.F.R. 178.3280). Similar approval is given for the use of N,N-bis(2-hydroxyethyl)higher aliphatic amines. U.S. Patent No. 2,678,285 describes treating the surface of a polymer film with an antistatic agent, specifically, an aqueous solution of a surface active agent such as triethanolamine stearate containing a finely divided polymeric material and, optionally, a wax. U.S. Patent Nos. 2,832,696, 2,832,697, 2,832,698, 2,832,699 and 3,937,066 each describe antistatic agents for polymeric materials including, for example, in the case of U.S. Patent No. 2,832,696, fatty amide condensate. Still other disclosures of polymer antistatic components are: U.S. Patent Nos. 3,365,435 (N-(2-hydroxyalkyl)ethanolamine),3,365,437 (hydroxyalkyl fatty acid amide), 3,407,187 (quaternary alkyl ammonium compound), 3,445,396 (a combination of N,N-bis(2-hydroxyethyl)higher aliphatic amine and higher aliphatic alcohol), 3,485,786 (alkyl propylamine), 3,575,902 (ethoxylated amine), 3,631,162 (a combination of N-(2-hydroxy-3-dodecyloxypropyl)ethanolamine and N,N-bis(2-hydroxyethyl)alkylamine), 3,708,464 (tetrahydropyrimidine), 3,821,184 (tetrahydropyrimidine), 3,975,325 (a combination of a fatty acid salt and tertiary amine), 4,147,742 (ethoxylated amine), 4,210,556 (ethoxylated amine), 4,234,664 (quaternary ammonium salt), 4,241,144 (quaternary ammonium sulfate), 4,268,583 (quaternary ammonium salt) and 4,314,040 (ethoxylated amine). Aqueous film-forming compositions containing, in addition to a water soluble or water dispersible film-forming polymer, one or more ingredients intended to impart a particular property or characteristic to the substrate to which the compositions are applied are known. Thus, U.S. Patent No. 3,252,826 describes a polymer film coated with an aqueous coating composition containing a water soluble gum, polyvinyl alcohol, hydroxyethyl cellulose, carboxy methyl cellulose, agar, etc., and an alkali metal salt of a fatty acid to confer clarity, good slip and good anti-block characteristics upon the film. U.S. Patent No. 4,140,822 describes a polyolefin film coated with an aqueous dispersion comprising aluminum chlorhydroxide, phosphoric acid and high molecular weight polyvinyl alcohol to enhance the receptivity of the film surface for paint, ink and glue. U.S. Patent No. 4,596,668 discloses an electrically-conductive surface-coating composition for use as a floor coating to provide electrostatic discharge protection. The composition comprises an emulsion of a film-forming, water soluble, low molecular weight polyampholyte polymer containing free carboxylic groups and carboxylic amino ester groups and an antistatic agent such as a quaternary ammonium salt. This invention provides a water based antistatic coating composition comprising: a) at least one water soluble antistatic agent which is acceptable for food packaging polymer films and which is selected from the group consisting of N -acyl Sarcosinates and N,N-bis(2-hydroxyethyl) higher aliphatic amines; b) at least one water soluble or water dispersible film-forming polymer; and, c) a solution or dispersion-forming amount of water. When applied to a polymer film substrate, the foregoing antistatic coating composition forms, upon drying, an adherent antistatic coating. The useful N-acyl sarcosinates can be represented by the general formula: wherein R¹ is an alkyl radical of from 8 to about 22 carbon atoms, R² is hydrogen, methyl or ethyl, R³ is hydrogen, alkyl of 1 to 4 carbon atoms, hydroxyalkyl of 1 to 4 carbon atoms and M is hydrogen or a salt-forming moiety such as alkali metal, ammonium or propanol substituted ammonium. The N-acyl sarcosinates can be prepared by a variety of methods including those described in U.S. Patent No. 2,063,987 referred to above and U.S. Patent Nos. 2,729,657, 3,074,980 and 3,836,551. Some are commercially available such as Hamposyl L-30 (W.R. Grace), a 30% by weight aqueous solution of sodium lauryl sarcosinate which, in addition to its antistatic capabilities, can also function as a slip agent when applied to polymer film surfaces. The useful N,N-bis(2-hydroxyethyl)higher aliphatic amines can be represented by the general formula wherein R is an alkyl or alkenyl group of from 8 to about 22 carbon atoms. Particularly preferred are N,N-bis(2-hydroxyethyl)alkenyl or mixtures of alkenyl and alkyl (C12-18) amines obtained from distilled coco, soy, oleyl or tallow, or mixtures thereof. Armostat 310 (Armak Company), a diethoxylated tallow (mixed alkenyl and alkyl) amine has been used with good results. The polymeric component of the antistatic coating composition of this invention is preferably one which is soluble or dispersible in water at ambient temperature. Suitable polymers include the homopolymers or acrylamide and methacrylamide; the copolymers of acrylamide and methacrylamide with each other and/or with one or more other monomers such as acrylic acid, methacrylic acid, vinyl alcohol (from hydrolysis of interpolymerized vinyl acetate groups), vinyl acetate, etc.; polyethylene sulfonate; polyesters such as maleinized polyesters, hydrophilic polyesters and polyesters modified with high-functionality organic acids; polymethacrylic acid; polyvinylpyrrolidone; polyvinylmethyl ether; cellulose ethers such as methyl cellulose, ethyl methylcellulose, sodium carboxyethylcellulose, carboxymethly hydroxyethylcellulose; and natural gums, soluble starches and other natural water soluble film-forming polymers. The foregoing recitation is not intended to be exhaustive but merely representative of the many kinds of water soluble and water dispersible film-forming polymers which are useful herein. Of these polymers, the cellulose ethers are preferred with hydroxyethylcellulose (HEC) being especially preferred. The preferred cellulose ethers are generally acceptable for use in food packaging polymer films. If desired, once the coating compositions are applied, the polymer component can be insolubilized. Thus, for example, sodium carboxymethylcellulose can be insolubilized by treatment with aluminum sulfate or with other polyvalent metal ions. The amounts of antistatic agent, water soluble or water dispersible film-forming polymer, optional ingredients such as natural or synthetic wax, surface active agent, particulate such as talc (an antiblocking agent) and colloidal silica (to reduce the coefficient of friction), suspending agent, viscosity modifier, pH adjustor, etc., and water can vary over wide ranges. In general, the amount of antistatic agent should be such that when the coating composition is applied to a polymer film, a significant reduction in the tendency of the film to accumulate static electricity on a surface thereof will be achieved. Amounts of antistatic agent ranging from about 1% to about 99%, and preferably from about 25% to about 75%, weight percent of the total coating composition are usually suitable. When applied to a film surface, coating compositions containing such amounts of antistatic agent will be sufficient to lay down from .01 to 1 g/o.65 m² (about .01 to about 1g/1000 in²), and preferably from 0.03 g to .1g/0.65m² about .03 to about .1g/1000 in.²) of the antistatic agent. The film forming polymer must be employed in at least that amount which will provide a continuous adherent coating when applied to a polymer film surface. The precise amounts will vary depending upon the nature of the polymer, the nature and amount of antistatic agent and other factors readily appreciated by those skilled in the art. From about 1% to about 99%, and preferably from about 25% to about 75% weight percent polymer, based on the total coating composition, can be employed with good results. Optional ingredient(s), when present, can be employed in the customary amounts. The total solids content of the coating composition herein can vary widely, e.g., from about 1 to about 20, and preferably from about 2 to 10, weight percent of the total, the balance being water or a mixture of water and a water soluble organic solvent such as methanol, ethanol, etc., to accelerate drying. The polymer films to be coated with the foregoing water based antistatic coating compositions are, of course, those which tend to accumulate surface electric charges during manufacture and/or while in service. Suitable polymer films include olefin polymers, e.g., homopolymers and copolymers of ethylene, propylene and butene-l; polyvinyl chloride, vinyl chloride/vinylidene chloride copolymers; polystyrene; styrene/butadiene copolymers' polyvinyl acetate, ethylene-vinyl acetate copolymers, ethylene-vinyl acetate-vinyl alcohol terpolymer, and the like. Films encountered in the packaging and handling of foods, notably, oriented polypropylene and vinyl acetate-containing homopolymers and copolymers, are especially well suited for coating by the antistatic coating compositions herein. When, however, the polymer film need not be acceptable for food packaging application, the coating composition can contain essentially any antistatic agent which is suitable for application to the surface of a substrate resin. Thus, any of the known antistatic compositions including many of those referred to above can be employed in coating compositions to be applied to films intended for non-food use. The following examples are illustrative of antistatic coating compositions prepared in accordance with this invention and oriented polypropylene film coated therewith. EXAMPLES 1 -2 Two water based antistatic coating compositions were formulated as shown in Table I and applied to polypropylene film prior to orientation in the transverse direction. The properties of the films coated with the antistatic coating compositions are set forth in Table II as follows: EXAMPLES 3-20 The antistatic coating compositions of these examples were prepared with 0 (control), 25, 50, 75, and 100 wt.% sodium lauroyl sarcosinate antistatic agent (Hamposyl L-30, W.R. Grace) and hydroxyethyl cellulose (Cellosize QP-09), Union Carbide) and diluted with demineralized water to 2, 3.5 and 5 wt.% solids. The compositions were applied to the base polypropylene film with a 200 Q gravure roll. Static tests, coefficient of friction and blocking measurements and coating weights are set forth in Table III as follows:

Claims: A water-based antistatic coating composition comprising: a) at least one water soluble antistatic agent which is acceptable for food packaging polymer films and which is selected from the group consisting of N-acyl sarcosinates and N,N-bis(2-hydroxyethyl) higher aliphatic amines; b) at least one water soluble or water dispersible film-forming polymer; and c) a solution or dispersion-forming amount of water. A composition according to claim 1 where the antistatic agent (a) comprises a compound of the formula: wherein R¹ is an alkyl group of 8 to 22 carbon atoms; R² is a hydrogen atom or a methyl or ethyl group; R³ is a hydrogen atom or an alkyl group of 1 to 4 carbon atoms or a hydroxyalkyl group of 1 to 4 carbon atoms; and M is a hydrogen atom or a salt-forming moiety; and/or a compound of the formula: wherein R is an alkyl or alkenyl group of 8 to 22 carbon atoms. A composition according to claim 2 wherein the salt-forming moiety is an alkali metal or a substituted or unsubstituted ammonium group. A composition according to any preceding claim wherein the antistatic agent (a) comprises an alakali metal alkylsarcosinate. A composition according to any preceding claim wherein the antistatic agent (a) comprises an N , N -bis(2-hydroxyethyl)alkenylamine or a mixture thereof with an N , N -bis(2-hydroxyethyl)alkylamine, wherein the alkenyl group comprises from 12 to 18 carbon atoms. A composition according to anyu preceding claim wherein the water soluble or water dispersible film-forming polymer (b) comprises a cellulose ether or a hydroxyethyl cellulose. A composition according to any preceding claim comprising an antistatic-effective amount of antistatic agent and an antistatic agent-carrying amount of water dispersible film-forming polymer. A polymeric film having on at least one surface thereof the water based antistatic coating composition of any one of the preceding claims. A polymeric film according to claim 8 wherein the polymer comprises a polyolefin. A polymeric film according to claim 9 wherein the polyolefin comprises polypropylene.

Inventors: TOUHSAENT, ROBERT EDWARD
Applicants: MOBIL OIL CORPORATION
Application year: 1987
Main classification: C09D5
IPC codes: C09K3, C08J7, C09D7, C08K5, C09D201, C09D5, A23L3