Magnetic iron oxide film and production thereof

Abstract: Disclosed herein is a perpendicular magnetic film of spinel type iron oxide formed on a surface of a base substrate in the form of columnar grains which are densely arranged perpendicularly to the surface of the base substrate. A vapor of an organic iron compound or a mixed vapor consisting of the organic iron compound vapor and a vapor of an organic metal compound different from the organ­ ic iron compound is added with oxygen to obtain a mixed gas. The mixed gas is subjected to chemical vapor deposition on the substrate at low temperature, at reduced pressure in plasma, thereby to obtain the perpendicular magnetic film.

Description: The present invention is concerned with thin magnetic iron oxide films and with the production thereof. Such thin magnetic films are used as media for magnetic or magneto-optic recording methods which enable ultra high density recording and playback to be obtained in the field of high density memory such as magnetic disk or digital recording for computer memory, video tape recorders, digital recording audio tape recorders and magneto-optic disks. In the field of memory media, there has recently been a trend towards recording with higher densities and digital recording. In the field of magnetic recording by means of a magnetic head which accounts for the most part of the memory field, the in-plane magnetic recording method in which the magnetizing direction is in a plane of magnetic recording medium has been used conventionally. However, there is a limit in this method in the improvement of recording density. On the other hand, there emerged a perpendicular magnetic recording method to provide ultra high density recording method, which employs a magnetic recording medium having an axis of easy magnetization in a perpendicular direction to the head travelling surface of the magnetic recording medium. (For example, S. IWASAKI, Y. NAKAYAMA; "An analysis for the magnetization mode for high density magnetic recording. "IEEE. Trans. Magn., MAG-13-(5) , 1272 (1977)). That is to say, in order to materialize this ultra high density recording method, a perpendicular magnetic film is indispensable as a magnetic recording medium material. On the other hand, active studies have been conventionally continued to develop media which use continuous thin film of magnetic material for the reason that they are more suitable to the ultra high density magnetic recording medium than the coat-type media, and the vacuum vapor deposition method or the sputtering method has been mainly used as a manufacturing process of the continuous thin film of magnetic material. As a material, thin film of Co-Cr alloy in particular, which is easily made into the above-mentioned perpendicular magnetic film, has been studied by a very large number of researchers as a material potentially usable for a medium for the above-mentioned perpendicular magnetic recording. (For example, K. Ouchi: "Co-Cr recording film with perpendicular magnetic anisotropy", IEEE. Trans. Magn. MAG-14(5) 849 (1978)). However, it was found that many problems are involved with environmental resistance such for example as the corrosion of magnetic film caused by moisture in air. Experiments have been carried out for improved corrosion resistance by such means as coating the surface of the magnetic film with a non-magnetic oxide layer of different type. However, a new problem has emerged that the manufacturing process of the magnetic media become complicated. There are many other problems to be solved. As compared to the above, Fe₃O₄ (Magnetite) or γ-Fe₂O₃ (Maghemite) which is the iron oxide having spinel type oxide crystal structure is by itself a magnetic oxide. The γ-Fe₂O₃ in particular has extremely excellent property of environmental resistance and is practically used as raw material magnetic powder for most of the coat-type magnetic recording media such as magnetic tapes and magnetic disks. For this reason, studies have been conducted in an attempt to use these spinel type iron oxide as magnetic film of the magnetic thin film media. Though the continuous magnetic thin film used for media of conventional in-plane magnetic recording method was materialized, the perpendicular magnetic film required for the media of perpendicular magnetic recording method of the above-mentioned ultra high density magnetic recording method has not been materialized. For the purpose of reference, a typical manufacturing process of the magnetic thin film of the media for the spinel type iron oxide in-plane magnetic recording method will hereafter be described. Conventionally, the γ-Fe₂O₃ thin film used to be manufactured by the sputtering method. By means of the reaction sputtering method in which a metallic iron target is used and sputtering is carried out while oxygen is being flowed generally, a thin film of α-Fe₂O₃ (alpha iron oxide) having a non-magnetic corundum type crystal structure is manufactured first. The thin film is reduced in a current of hydrogen and caused to be transformed into Fe₃O₄ having a spinel type crystal structure, which is further caused to be oxidized slightly to finally produce a continuous film of γ-Fe₂O₃ having the same spinel type crystal structure (for example, J.K. Howard; "Thin films for magnetic recording technology; A review" J. Vac. Sci. Technol. A. 4 , 1986). In the above-mentioned manufacturing of continuous film of γ-Fe₂O₃ by means of sputtering method, a metallic iron is used as a target material, a continuous film of α-Fe₂O₃ is first formed by accomplishing the reaction sputtering in a chamber where a small quantity of oxygen is introduced, the film is reduced to be changed into Fe₃O₄ film having different crystal structure, and the Fe₃O₄ film is further caused to be oxidized slowly to be changed into a continuous film of γ-Fe₂O₃, thereby a continuous magnetic film of γ-Fe₂O₃ is produced. Therefore, fine cracks are likely to be generated over the film surface due to a large change in volume caused during a changing process of α-Fe₂O₃ → Fe₃O₄ → γ-Fe₂O₃, resulting in poor film surface quality causing the film to be susceptible to defects. Further, since the film is consisted of fine polycrystalline structure, efficiency of magnetic characteristic is lowered as compared with a single crystal film in which a certain regular crystal plane is in a specific orientation. Furthermore, complicated and many processes are involved in manufacturing. That is, there are many problems to be solved. As a manufacturing process to remove these defects, a method is being studied wherein the powder of spinel type iron oxide is pressed and formed into a target material, so that the spinel type iron oxide thin film is directly obtained by sputtering method (for example, Y, Hoshi, M. Naoe; Telecommunication Society Report, Vol. 85, No. 87, p. 9, 1985 in Japanese). In this process, a spinel type iron oxide magnetic film of oriented crystal plane can be obtained by selecting a substrate material. In addition, this process has a defect such as slow film forming speed and cannot be said as a manufacturing process suitable for mass production. On the other hand, an optical recording method which uses a laser beam is available as ultra high density recording method. The magneto-optic recording method is the most prospective rewritable method among the optical recording methods. In the magneto-optic recording method, a laser beam is used to heat a part of a magnetic spin which has previously been oriented in one direction perpendicularly to the magnetic thin film surface of a medium so that the magnetic spin of the laser beam irradiated film surface is magnetized and inverted thereby to record a bit of a signal. The recorded signal is read by a light by utilizing the property of light that the rotational direction of the polarized light plane becomes different depending on the direction of the magnetic spin. Therefore, a perpendicular magnetic film becomes inevitably necessary for the magnetic film of the media of the magneto-optic recording method. Manganese bismuth (MnBi) alloy was a material of the magneto-optical memory used in the first stage, but had defects such as phase transfer, thermal instability, susceptible to oxidation, difficulty to obtain uniform film of small grain, and large noise of media. Then emerged was a film of RE-TM (rare earth-transition metal) amorphous alloy such as Gd-Co, Tb-Fe and Gd-Fe. These alloy films are normally manufactured by the vacuum deposition method or sputtering method. The RE-TM alloy features that signal recording with large signal to noise ratio is achieved by selecting its composition, but it is oxidized, corroded and deteriorated at high temperature and under humidity because it is a metallic film. This defect is being deemed as one of large problems (for example, S. Uchiyama, "Magneto-Optical Recording", Surface Science, Vol. 8, No. 2, P.2, 1987 in Japanese). The material which is attracting attention as a material to solve this defect is an oxide type perpendicular magnetic film which has good magneto-optical characteristic. This film is a spinel type iron oxide film, that is, a cobalt ferrite thin film of which a part of iron ion in the composition is substituted by cobalt ion. Perpendicular magnetic films of Fe₃O₄ or γ-Fe₂O₃ have been disclosed in EP-A-0169928 and in Conf. Proceedings, Magnet. Thin films (PAP.SYMP.10), (56E-MRS), Strasbourg, June 1986 pages 107-114. Further it is possible to manufacture the perpendicular magnetic thin film of cobalt substituted spinel type iron oxide which can be used for magneto-optic recording media. This thin film can be manufactured by a manufacturing process to be described below and is being put to use, but it is currently difficult to obtain a perfect perpendicular magnetic film of low media noise. The manufacturing processes are available to produce the above-mentioned perpendicular magnetic film of cobalt substituted spinel type iron oxide for the magneto-optic recording method. One process is the sputtering method (for example, M. Gomi, T. Yasuhara and M. Abe, "Sputter-Deposition of Co Gr Ferrite Thin Film for Magneto-Optic Memory", Japan Applied Magnetism Society Magn., Vol. 9, No. 2, 133, 1985 in Japanese). As a target, a sintered spinel type iron oxide material containing cobalt is used to manufacture a film under 1.33 to 0.133 Pa and at over 350°C substrate temperature. In the thus obtained film the direction 〈111〉 that is different from the axis of easy magnetization of the cobalt substituted spinel type iron oxide is oriented preferentially. When the produced film is cooled to the room temperature, stress is applied to the film due to the difference in the ratio of thermal expansion between the base substrate and the produced film, causing the magnetic spin of the produced film to be easily directed perpendicularly with respect to the surface of the produced film by the effect of stress-caused magnetic anisotropy, thereby a film having a tendency to the perpendicular magnetic film is obtained. However, because the target is an oxide, such problems still remain that the growth of the sputtered film is not fast as that of the metallic target, it is difficult to obtain a uniform film of large area, all being related to the manufacturing of perpendicular magnetic film for magneto-optic recording media. The other process is to manufacture a film by means of the solution spray-dry pyrolysis method (for example, J.W.D. Martens & A.B. Voermans: "Cobalt Ferrite Thin Films for Magneto-Optical Recording" IEEE Trans. Magn., MAG -29(5), 1007, (1984)). In this method, a dilute alcohol solution of iron nitrate and cobalt nitrate is used as a raw material, a very thin coated film is produced on a base substrate by using the Spinner method, the coated film is dried at a temperature of about 350°C, similar coated films of greater thickness are further formed again on the same substrate by repeating 50 to 60 cycles of film formation and drying processes, and this thick coated film is burned at a temperature of over 600°C to obtain a perpendicular magnetic film of cobalt substituted spinel type iron oxide similar to one as described above. This method also utilizes the difference of the thermal expansion ratio between the base substrate and the produced film to realize the film having a tendency to the perpendicular magnetic film by the effect of stress-caused magnetic anisotropy. Furthermore, because this method is capable of providing a film which is preferentially oriented into the 〈100〉 direction which is the axis of easy magnetization, this method is excellent in forming a film having a tendency to perpendicular magnetic film through coating and burning processes, and has a merit of obtaining uniform film over a large area. However, because many repeated processes of coating and drying are necessary, the burning temperature as high as 600°C or over requires materials of excellent heat resistance for base substrate, and the film is produced by burning, the size and shape of grains are not uniform, which easily causes the media noise. An object of the present invention is to provide not only the cobalt substituted spinel type iron oxide but also various kinds of perpendicular magnetic film of spinel type iron oxide, and another object is to provide a manufacturing process by which a perpendicular magnetic film according to the present invention is uniformly formed on a large area of substrate made of material having low heat resistance such as aluminum, plastics or glass of low melting point. The present invention provides a perpendicular magnetic film of spinel type iron oxide compound formed on a surface of a base substrate in the form of columnar grains which are densely arranged perpendicularly to the surface of the base substrate, said film comprising - γ-Fe₂0₃ grown in the 〈111〉 direction perpendicularly to the surface of the base substrate, wherein the mean height/diameter ratio of the columnar grains is at least 6 and the column diameter of each grain is at most 55 nm. The present invention also provides a perpendicular magnetic film of spinel type iron oxide compound formed on a surface of a base substrate in the form of columnar grains which are densely arranged perpendicularly to the surface of the base substrate, said film comprising a substituted spinel type iron oxide expressed as M x Fe 3-x 0₄ where M is a metal selected from the group consisting of Ni, Mn, Zn and Co, and x is in a range of 0.1≦x≦ 1, grown in the 〈100〉 direction perpendicularly to the surface of the base substrate, wherein the mean height/diameter ratio of the columnar grains is at least 6 and the column diameter of each grain is at most 45 nm. In order to realize the perpendicular magnetic film of the spinel type iron oxide having such a film structure as above, it is necessary to control the formation of the film so that the sizes of the columnar grains are uniform and so that the column diameter of each of the columnar grains does not grow large. Furthermore, it is preferable to control the crystal orientation of the produced film so that the direction of the growing crystal axis of the columnar grains agrees with the direction of the axis of easy magnetization. In the manufacturing process to accomplish these requirements according to the present invention, a vapor produced by heating and vaporizing an organic iron compound or a mixed vapor of this vapor and a vapor produced by heating and vaporizing a different kind of metallic compound is used as a raw material gas, oxygen is selected as a reaction gas, and the mixed gas of the raw material gas and the reaction gas is subjected to plasma excitation to cause chemical vapor deposition (CVD) on a base substrate which is held in a temperature range from the room temperature up to 300°C, whereby columnar grains of small column diameter are caused to grow in a perpendicular direction to the surface of the base substrate and are arranged densely, thereby producing the perpendicular magnetic film of the spinel type iron oxide compound having a film structure whose specific crystallographic planes are oriented preferentially. In the manufacturing process according to the present invention, used as the organic iron compound are β-diketone iron compound represented by iron (III) acetylacetonate (Fe(CH₃COCHCOCH₃)₃), iron (III) trifluoroactylacetonate (Fe(CH₃COCHCOCF₃)₃), iron (III) hexafluoroacetylacetonate (Fe(CF₃COCHCOCF₃)₃) and iron (III) dipivaloylmethane chelate (Fe((CH₃)₃COCHOC(CH₃)₃)₃), and iron cyclopentadienyl compound such as ferrocene derivative represented by ferrocene (Fe(C₅H₅)₂) and vinyl ferrocene. Further, in the manufacturing process according to the present invention, when manufacturing a perpendicular magnetic film of cobalt substituted spinel type iron oxide, a vapor of organic cobalt compound such as β-diketone cobalt complex represented by cobalt acetylacetonate (Co(CH₃COCHCOCH₃)₃) or cyclopentadienyl compound represented by cobaltcen (CO(C₂H₅)₂) and a vapor of the above-mentioned organic iron compound are mixed and used as the raw material gas. Likewise, when manufacturing a perpendicular magnetic film of nickel substituted spinel type iron oxide, instead of the organic cobalt compound, an organic nickel compound such as β-diketone nickel complex represented by nickel acetylacetonate (Ni(CH₃COCHCOCH₃)₂) is used. When manufacturing a perpendicular magnetic film of manganese substituted spinel type iron oxide, instead of the above-mentioned organic cobalt compound, an organic manganese compound such as β-diketone manganese complex represented by manganese acetylacetonate (Mn(CH₃COCHCOCH₃)₂) is used. When manufacturing a perpendicular magnetic film of zinc substituted spinel type iron oxide, instead of the above-mentioned organic cobalt compound, an organic zinc compound such as β-diketone zinc complex represented by zinc acetylacetonate (Zn(CH₃COCHCOCH₃)₂) is used. Generally, in the chemical vapor deposition method (CVD method) (which causes decomposition and deposit by normal heat), the film forming speed can be increased by flowing a large quantity of the raw material gas and reaction gas into a reaction chamber at high speed, and high vacuum is not required differently from the vacuum deposition method and the sputtering method which are other film forming method generally used. That is to say, the film manufacturing process according to the present invention is suitable to mass production. In the CVD method according to the present invention, by exciting the raw material gas by means of plasma during film forming, the raw material gas and atmospheric gas are decomposed, in the plasma, into active chemical species such as radicals or ions which are effective to cause chemical reaction at low temperature, and the produced chemical species react each other to be deposited as a stable compound film (in the case of the present invention, as a spinel type iron oxide compound film). As stated above, because active chemical species can be generated in large quantity even at low temperature by the plasma excitation, film forming becomes possible at a low temperature which cannot be expected in the ordinary CVD method. Because the manufacturing process according to the present invention is the above-mentioned manufacturing process, by selecting the ratio of the flow rate of the vapor of the raw material gas produced by organic metallic compound and the flow rate of the oxygen used as the reaction gas or by selecting conditions such as power of plasma generating high frequency source used for excitation, it becomes possible to form a thin film of spinel type iron oxide in one process. Moreover, because it is easy to produce uniform film during film forming, the produced film can be easily made into an aggregate film having columnar grains of uniform size, and because the low temperature film forming is possible, the growth of the columnar grains can be restricted and the size of the column diameter can be controlled to be small. Furthermore, by selecting the kind of substrate and by controlling the ratio of the flow rate of the raw material gas and reaction gas (oxygen) or the degree of vacuum in the reaction chamber or the quantity of inactive gas used to introduce these gases into the reaction chamber, it becomes possible to form a film whose specific crystal axis is preferentially oriented and to control so that the preferred orientation is caused to agree with the direction of the axis of easy magnetization. As described above, it is possible to effectively manufacture a perpendicular magnetic film of the present invention by means of the above manufacturing method. Still more, by employing the manufacturing method according to the present invention, the γ-Fe₂O₃ film which is a kind of spinel type iron oxide can be formed in one process and, therefore, this manufacturing method solves such a problem that micro cracks are generated on the film surface caused by a change in volume or a change in crystal structure when manufacturing the film by metamorphosing from α-Fe₂O₃ in the conventional method. The above manufacturing method also solves such a problem that many processes are required for the metamorphosis of α-Fe₂O₃ to Fe₃O₄ to γ-Fe₂O₃ in the conventional method. Still furthermore, because the chemical vapor deposition is accomplished by plasma excitation, a crystalline thin film can be formed at a relative by low temperature and it becomes unnecessary to heat the base substrate at a high temperature as in the case of film forming by the conventional chemical vapor deposition method, which do not use plasma excitation. In addition, because a base substrate material whose quality is changed when heated at high temperature can also be used as a base substrate the selection range of the kind of substrate material can be expanded. Therefore, cost reduction of magnetic recording media can be achieved by using substrates made of inexpensive materials. On the other hand, with respect to the cobalt substituted spinel type iron oxide (CoxFe₃-xO₄) which is regarded as a promising material for iron oxide magneto-optic recording media, if the perpendicular magnetic film of the present invention is used, then, the film is structured with uniformly aggregated columnar grains having fine column diameter. Therefore, when a magneto-optic recording medium is manufactured by using the film of the invention, possibility of occurrence of media noise which would occur during signal reproducing due to large or not-uniform sizes of the grains. BRIEF DESCRIPTION OF THE INVENTION FIG. 1 is a schematic structural diagram of a plasma CVD equipment used in a manufacturing process (Example 1) according to the present invention; FIG. 2 is a diagram of X-ray diffraction pattern of a perpendicular magnetic film of spinel type iron oxide compound, Fe₃O₄, according to the present invention; FIG. 3 is a cross sectional view of the perpendicular magnetic film of the same compound, Fe₃O₄; FIG. 4 is a diagram showing the surface of the perpendicular magnetic film of the same compound, Fe₃O₄ of; and FIG. 5 is a schematic structural diagram of another plasma CVD equipment used in a manufacturing process (Example 3) according to the present invention. DESCRIPTION OF THE PREFERRED EMBODIMENTS Example 1 A perpendicular magnetic film of spinel type iron oxide γ-Fe₂O₃ according to the present invention was manufactured by using a manufacturing equipment shown in FIG. 1. This manufacturing equipment mainly comprises a tubular chamber 1, a bubbler 2 for vaporizing raw material which can be heated at a fixed temperature by a built-in heater, and an exhaust pump 3. When an organic iron compound 4 placed in the bubbler 2 is heated, the vapor of the organic iron compound is generated, and this vapor is introduced into the tubular chamber 1 by using nitrogen as a carrier gas supplied from a carrier gas cylinder 5. On the other hand, oxygen as a reaction gas from a reaction gas cylinder 6 is also introduced into the chamber 1. In the tubular chamber 1, a substrate heater 9 is disposed at the front center of a blow-off pipe 7 for blowing into the chamber the mixed gas of the vapor of the organic iron compound carried by the carrier gas of nitrogen and the reaction gas of oxygen. A substrate 8 is held on the substrate heater 9. On the outside of the tubular chamber 1 is installed a high frequency coil 10 for generating plasma to accomplish plasma excitation of the mixed gas flowing within the tubular chamber 1. The coil 10 is excited by a high frequency power source (not shown). The exhaust pump 3 is used to maintain a fixed degree of vacuum inside of the reaction chamber 1. Denoted by 11 and 12 are a vacuum meter and a vacuum degree adjusting valve, respectively. As the substrate 8, a 50 mm diameter circular tempered glass whose film-formed surface had been mirror finished was used. Powder of iron (III) acetylacetonate (Fe(CH₃COCHCOCH₃)₃) of 25.0 g was placed in the bubbler 2 as the organic iron compound raw material and heated to 135 ± 0.5°C, and nitrogen containing 10% hydrogen was introduced as the carrier gas into the tubular chamber 1 at a flow rate of 200 cm³/min. through the bubbler 2. At the same time, oxygen as the reaction gas was introduced into the same chamber at a flow rate of 10 cm³/min. While introducing these gases, the exhaust system was adjusted to hold the inside of the chamber 1 at a degree of vacuum of 16.0 Pa. The high frequency power was set to a fixed level of 50W, and the plasma excitation was carried out for 20 minutes to form a CVD film on the substrate. During film forming the substrate was kept heated at 300°C. The thus formed film was observed by the CEMS (Conversion Electron Mössbauer Spectroscopy) analysis of Fe⁵⁷ nucleus, X-ray diffraction analysis, and far-infrared spectra measurement, and it was confirmed that the produced film was a spinel type iron oxide γ-Fe₂O₄ thin film containing only trivalent Fe ion and the direction 〈111〉 thereof was preferentially oriented. Generally, when the hysteresis loop of a perpendicular magnetic film is measured with a vibrating sample magnetometer (VSM), it is difficult to know the degree of perpendicular magnetization of the film because the demagnetizing field acts upon the sample film. Therefore, we used the CEMS measurement of Fe⁵⁷ nucleus by which the property of the magnetic spin can be directly known due to mutual action between the gamma rays and the magnetic spin of the magnetic iron, and determined whether the film was the perpendicular magnetic film based on the peak strength ratio of the spectra obtained. Generally, in the case of γ-Fe₂O₃ of spinel type iron oxide, six peaks appear in the CEMS spectra which attribute to the trivalent Fe ion. Of these six peaks, the sum of strengths of the second and fifth peaks from the end provides information of angle ϑ between the irradiating direction of the gamma rays, that is, the perpendicular direction to the surface of the sample thin film and the direction of the magnetic spin of Fe in the magnetic substance (namely, the magnetizing direction). Generally, the peak strength ratio of a spectrum is expressed by sum of the first and six peaks : sum of the second and fifth peaks : sum of the third and fourth peaks = In the case of a film of which the directions of the magnetic spin in the magnetic film are random, the peak spectrum strength ratio of the above is 3:2:1; but in a case of a perpendicular magnetic film, the ratio is 3:0:1; while in the case of an in-plane magnetic film, the spectra peak strength ratio is 3:4:1. This strength ratio of the sample film of the invention produced by the process described above was 3.0:0.06:1.2. Since the sum of the peak strength of the second and fifth is smaller as compared with the other two sums, it can be judged that the film is a perpendicular magnetic film. The cross section of the obtained magnetic thin film was observed using a high resolution scanning type electron microscope. As the result of the observation, it was found that the film has a structure in which grains grow each in columnar shape perpendicularly to the film surface and that the column diameter is about 45 nm. The experimental results of this sample film are shown on Table 1 and Table 2 as sample number 1. Results of sample films produced under varied film forming conditions are shown as sample numbers 2 through 6 on Tables 1 and 2. Likewise, the results shown as sample numbers 7 through 18 on Tables 1 and 2 were obtained by using, as the organic iron compound, iron (III) trifluoroacetylacetonate (Fe(CH₃COCHCOCF₃)₃), iron (III) tetrafluoroacetylacetonate (Fe(CF₃COCHCOCF₃)₃), iron (III) dipivaloylmethane chelate (Fe(C(CH₃)₃COCHCOC(CH₃)₃), ferrocene (Fe(C₅H₅)₂), and vinyl ferrocene. The sample number 19 on Tables 1 and 2 is a sample for comparison different from the samples of the present invention. This comparison sample is a γ-Fe₂O₃ film produced by a conventional method which employs reduction and slight-oxidation processes of γ-Fe₂O₃ film formed by sputtering method. As is known from Table 2, when perpendicular magnetic films of γ-Fe₂O₃ are obtained by controlling the film forming conditions; the film structure is columnar; the ratio of the mean column height/column diameter is 6 or more; and the column diameter is at most 55 nm for the films of preferred orientation of 〈111〉 in the direction of the axis of easy magnetization of γ-Fe₂O₃ film, and at most 45 nm for the films having no orientation in the direction of the axis of easy magnetization. Example 2 The manufacturing of a perpendicular magnetic film of spinel type iron oxide Fe₃O₄ according to the present invention was accomplished in the following manner. The same manufacturing equipment as that used in Example 1 was used. The base substrate 8 was an aluminum circular plate having the same shape as that used in Example 1 and a mirror-finished film-formed surface, and 25.0 g of powder of iron (III) acetylacetonate was placed in the bubbler 2 as the organic metallic compound raw material. The powder was heated at 135 ± 0.5°C. Nitrogen as the carrier gas was supplied at a flow rate of 5 cm³/min, and oxygen as the reaction gas was supplied at a flow rate of 3 cm³/min. Plasma excitation and vapor deposition (VD) were accomplished while introducing the mixed gas of the above two gases into the tubular chamber 1. During the above process, the high frequency power was kept at the same fixed level of 50W as in Example 1 and the degree of vacuum in the tubular chamber 1 was kept at 16.0 Pa. The base substrate was kept heated at 280°C thereby forming the film. The thus obtained film was analyzed by X-ray diffraction analysis, chemical composition analysis and far-infrared spectrum measurement. As the result of the analyses, the produced film was found to be a spinel type iron oxide Fe₃O₄ thin film whose (100) plane was completely oriented toward the substrate surface. X-ray diffraction pattern of this film is shown in FIG. 2. From the CEMS measurement of Fe⁵⁷ nucleus, it was known that this film contained only bivalent Fe ion and trivalent Fe ion. In addition, observation of the cross section of the film with a high resolution scanning type electron microscope revealed that the cross section was, similarly to that of sample 1 of Example 1, such that the film surface was covered with columnar grains standing densely and perpendicularly on the film surface, and further that the column diameter of each of such columnar grains was about 45 nm. FIG. 3 shows the cross section of this sample film and FIG. 4 shows the surface thereof. That is to say, by using the method according to the present invention, a spinel type iron oxide Fe₃O₄ film having densely arranged fine columnar grains was obtained in one process. As to whether the obtained sample film is of a perpendicular magnetic film was judged by analyzing the Fe⁵⁷ nucleus CEMS spectra as in the case of Example 1. Generally, the CEMS spectra of Fe₃O₄ show six peaks attributing to bivalent Fe iron and six peaks attributing to trivalent Fe ion, which can be separated easily into respective six peaks by computer processing. As described in connection with Example 1, with respect to each six peak spectra, it is possible to know the information of the angle ϑ between the irradiating direction of the gamma rays (that is, the perpendicular direction to the surface of the sample thin film) and the direction of the magnetic spin inside of the sample thin film (that is, the magnetizing direction). The strength ratio of spectra can be expressed by the following formula with respect to each of the bivalent Fe ion and trivalent Fe ion: As the tendency toward the perpendicular magnetic film increases, the strength ratio approaches to 3:0:1. Pursuant to a calculation of this ratio with respect to the spectra of the above sample film, the result was 3.0:0.08:1.2 and it was judged that the obtained film was the perpendicular magnetic film. Observation results of this sample film are shown on Table 3 and Table 4 by numbering the film as sample No. 1. Results of the sample obtained under varied film forming conditions are shown with the sample numbers 2 through 5 on Tables 3 and 4. When, instead of the above iron (III) acetylacetonate used for sample No. 1, iron (III) trifluoroacetylacetonate, iron (III) hexafluoroacetylacetonate, iron (III) dipivaloylmethane chelate, ferrocene and vinyl ferrocene were used as organic metallic compounds, and the plasma asisted CVD processes were accomplished under the conditions shown on Table 3, Fe₃O₄ perpendicular magnetic films each having the same film structure as that of sample No. 1 were obtained. The column diameters of columnar grains ranged from 30-45 nm. Results of the films obtained are shown as sample numbers 6 through 12 on Tables 3 and 4. The sample numbered as sample No. 13 is an Fe₃O₄ film manufactured by sputtering method and by using the Fe₃O₄ sintered target as a comparative sample. As is apparent from Table 3, a perpendicular magnetic film of spinel type iron oxide, Fe₃O₄, can be obtained by controlling the film forming conditions. Example 3 As a base substrate 8, a tempered circular glass having a film formed surface mirror-finished similar to that used in Example 1 was used, a manufacturing equipment of a structure as shown in FIG. 5 was used, and the base substrate was kept heated at 300°C. Bubblers 2, 2' are for having placed therein raw materials 4, 4' and carrier gas cylinders 5, 5' are for supplying carrier gases at different flow rates from each other. As the organic metallic compound raw material, organic iron compound and organic cobalt compound were used. As the organic iron compound, iron (III) acetylacetonate was used, and as the organic cobalt compound, cobalt acetylacetonate was used. The raw materials each in quantity of 25.0 g were placed in the bubblers 2 and 2' respectively. By flowing the carrier gas (N₂) at different flow rates from the cylinders 5, 5' through the bubblers 2, 2', vapors of the respective raw materials having different flow rates were introduced into the tubular chamber 1 through the pipe 7. Inside each of the bubblers was heated and held at a fixed temperature of 135 ± 0.5°C, the degree of vacuum in the tubular chamber was held at 1.60 Pa, and the high frequency power of 50W was maintained, whereby the plasma excitation and CVD were accomplished to form films. Table 5 shows the film forming conditions of each of the manufactured magnetic films as sample numbers 1 through 4. With respect to each of the films formed on the substrate of tempered glass obtained in the above manner, measurements were made by X-ray diffraction analysis, chemical composition analysis, far-infrared absorbed spectrum measurement, and Fe⁵⁷ CEMS and observation was carrier out using a high resolution scanning type electron microscope. As the result, it was found that the film structure in every case was similar to that shown in FIG. 3 of Example 2, and the column diameter of fine columnar grains of this film was in the range from 30-55 nm. In terms of crystalline structure, each of the film was an iron oxide CoxFe₃-xO₄ having a solid solution of spinel type Co contained therein in a small amount, in which all the 〈111〉 planes were oriented in parallel to the surface of the base substrate. As to whether the obtained sample films were each a perpendicular magnetic film, judgement were made by checking the strength ratio of the respective six peaks attributing to bivalent Fe ion and trivalent Fe ion of the Fe⁵⁷ nucleus CEMS spectra, as in the case of Example 2. As shown on Table 6, because the samples numbered from 1 through 4 indicate no absorption at the second and fifth spectra, it is clear that all the obtained films are perpendicular magnetic films. With regard to the organic iron (III) compound, even if other compounds such as β-diketone iron (III) hexafluoroacetylacetonate, and cyclopentadienyl ferrocene were used instead of the above iron (III) acetylacetonate, the same CoxFe₃-xO₄ films were manufactured by controlling the temperature of the bubbler where these raw materials are placed. With regard to the organic cobalt compound, even if such compound as another β-diketone compound such as cobalt trifluoroacetylacetonate and cyclopentadienyl compound such as cobaltcen were used instead of the above cobalt acetylacetonate, the same CoxFe₃-xO₄ films as the above were manufactured when the bubbler temperature was controlled in a similar manner as the above and the flow rate of the vapor was properly adjusted. Results of these are shown as sample numbers 5 through 8 on Tables 5 and 6. For sample numbers 9 through 11, iron (III) acethylacetonate was used as the organic compound while nickel acetonate, manganese acetylacetonate and zinc acetylacetonate were used as another organic metallic compound to obtain spinel type iron oxide compound thin films. It is understood that all films manufactured in the above process are perpendicular magnetic films. For the purpose of comparison, the same plasma CVD method was used, and the temperature of the base substrate was increased above 320°C, so that sample films whose column diameters were caused to grow large were manufactured. Results of these comparison samples are shown as sample numbers 12 through 16 on Tables 5 and 6. It can be known from Table 6 that perpendicular magnetic films were not obtained in either of these comparison samples. With further respect to the thin film of cobalt substituted spinel type iron oxide, thin films manufactured by conventional sputtering method and solution spray-dry pyrolysis method were used as samples for comparison. The results are shown as sample numbers 17 and 18 on Tables 5 and 6. For the sample obtained by the sputtering method, sintered Co 0.8 Fe 2.2 O₄ of cobalt substituted spinel type iron oxide was used as a target material and the film was formed in vacuum of 0.60 Pa and at the substrate temperature of 400°C. For the sample obtained by the solution spray-dry pyrolysis method, alcohol solution containing both Fe(NO₃)₃ of 0.02 mol/l and Co(NO₃)₂ of 0.01 mol/l was coated over the sample while rotating the substrate. After heat treatment at 300°C, subsequent 30 cycles of coating and heat treatment processes were repeated, and then the film was again heat-treated at a high temperature of 650°C.

Claims: A perpendicular magnetic film of spinel type iron oxide compound formed on a surface of a base substrate in the form of columnar grains which are densely arranged perpendicularly to the surface of the base substrate, said film comprising γ- Fe₂0₃ grown in the 〈111〉 direction perpendicularly to the surface of the base substrate, wherein the mean height/diameter ratio of the columnar grains is at least 6 and the column diameter of each grain is at most 55 nm. A perpendicular magnetic film of spinel type iron oxide compound formed on a surface of a base substrate in the form of columnar grains which are densely arranged perpendicularly to the surface of the base substrate, said film comprising a substituted spinel type iron oxide expressed as M x Fe 3-x 0₄ where M is a metal selected from the group consisting of Ni, Mn, Zn and Co, and x is in a range of 0.1<x≦ 1, grown in the 〈100〉 direction perpendicularly to the surface of the base substrate, wherein the mean height/diameter ratio of the columnar grains is at least 6 and the column diameter of each grain is at most 45 nm. A method of producing a perpendicular magnetic film of spinel type iron oxide compound comprising the steps of: heating an organic iron compound to vaporize the organic iron compound to obtain a raw material gas; supplying the raw material gas and oxygen gas as a reaction gas into a vacuum reaction chamber in which a base substrate maintained at a temperature in a range from room temperature to 300°C is placed; and plasma-exciting the raw material gas and the reaction gas in the chamber to cause chemical vapor deposition, thereby forming on a surface of the base substrate a perpendicular magnetic film of spinel type iron oxide compound which is γ-Fe₂O₃ grown in the 〈111〉 direction perpendicularly to the surface of the base substrate, in the form of columnar grains which are densely arranged perpendicularly to the surface of the base substrate and have a mean height/diameter ratio 6 or more and respective column diameters each being at most 55 nm. A method according to claim 3, wherein said organic iron compound is a β-diketone iron complex. A method according to claim 4, wherein said β-diketone iron complex is iron (III) acetylacetonate (Fe(CH₃COCHCOCH₃)₃), iron (III) trifluoroacetylacetonate (Fe(CH₃COCHCOCF₃)₃), iron (III) hexafluoracetylacetonate (Fe(CF₃COCHCOCF₃)₃), or iron (III) dipivaloylmethane chelate (Fe(C(CH₃)₃COCHCOC(CH₃)₃)₃). A method according to claim 3, wherein said organic iron compound is an iron cyclopentadienyl compound. A method according to claim 6, wherein said iron cyclopentadienyl compound is a ferrocene derivative. A method according to claim 7, wherein said ferrocene derivative is ferrocene (Fe(C₅H₅)₂) or vinyl ferrocene. A method of producing a perpendicular magnetic film of spinel type iron oxide compound comprising the steps of: heating an organic iron compound and an organic metal compound different from the organic iron compound to vaporize the organic iron compound and the organic metal compound to obtain a raw material gas which is a mixture of the vaporized organic iron and metal compounds; supplying the raw material gas and oxygen gas as a reaction gas into a vacuum reaction chamber in which a base substrate maintained at a temperature in a range from room temperature to 300°C is placed; and plasma-exciting the raw material gas and the reaction gas in the chamber to cause chemical vapor deposition, thereby forming on a surface of the base substrate a perpendicular magnetic film of a substituted spinel type iron oxide expressed as M x Fe 3-x 0₄ where M is a metal selected from the group consisting of Ni, Mn, Zn and Co, and x is in a range of 0.1<x≦ 1, grown in the 〈100〉 direction perpendicularly to the surface of the base substrate, in the form of columnar grains which are densely arranged perpendicularly to the surface of the base substrate and have a mean height/diameter ratio of 6 or more and respective column diameters each being at most 45 nm. A method according to claim 9, wherein said organic iron compound is a β-diketone iron complex. A method according to claim 10, wherein said β-diketone iron complex is iron (III) acetylacetonate (Fe(CH₃COCHCOCH₃)₃), iron (III) trifluoroacetylacetonate (Fe(CH₃COCHCOCF₃)₃), iron (III) hexafluoracetylacetonate (Fe(CF₃COCHCOCF₃)₃), or iron (III) dipivaloylmethane chelate (Fe(C(CH₃)₃COCHCOC(CH₃)₃)₃). A method according to claim 9, wherein said organic iron compound is an iron cyclopentadienyl compound. A method according to claim 12, wherein said iron cyclopentadienyl compound is a ferrocene derivative. A method according to claim 13, wherein said ferrocene derivative is ferrocene (Fe(C₅H₅)₂) or vinyl ferrocene. A method according to claim 9, wherein said organic compound is an organic cobalt compound. A method according to claim 15, wherein said cobalt compound is a β-diketone cobalt complex.

Inventors: AOKI MASAKI, AOKI NOBUYUKI, FUJII EIJI, OCHIAI KEIICHI, TORII HIDEO, AOKI, MASAKI, AOKI, NOBUYUKI, FUJII, EIJI, OCHIAI, KEIICHI, TORII, HIDEO
Applicants: MATSUSHITA ELECTRIC IND CO LTD, MATSUSHITA ELECTRIC INDUSTRIAL CO., LTD.
Application year: 1987
Main classification: G11B5
IPC codes: C23C16, G11B5