Ammonium salt solution as electrolyte for electrolytic capacitors

Abstract: An electrolyte for aluminium electrolytic capacitors comprises a solution in an aprotic solvent mainly (90% or more) composed of γ-butyrolactone of, as a solute, 0.1 to 40 wt% of a quaternary ammonium salt having as an anion the conjugated base of an inorganic acid compound selected from (1) boric acid, (2) phosphoric acid, (3) phosphorous acid and phosphorous acid monoesters, phosphonic acids, and phosphonic acid mono­ esters, (4) hypophosphorous acid and phosphinic acids, (5) alkylboric acids and arylboric acids, (6) silicic acid and (7) carbonic acid and carbonic acid monoesters.

Description: This invention relates to an electrolyte for an aluminum electrolytic capacitor, and more particularly to an electrolyte which can reduce the internal resistance of an electrolytic capacitor and broaden the temperature range over which the capacitor can be used, which electrolyte contains quaternary ammonium salts of inorganic acids dissolved in aprotic solvents. Conventional electrolytes for aluminum electrolytic capacitors generally comprise some type of ionizable compound dissolved in a solvent. The chemical or electric properties of the electrolyte, such as electrical conductivity and scintillation voltage, become main factors for determining the electrical properties of electrolytic capacitors. For example, a solution of boric acid or ammonium borate in ethylene glycol, which has low electrical conductivity and high scintillation voltage, has been used for aluminum electrolytic capacitors operating at 200 V or higher (see U.S. Patent 1,891,207). The maximum operating temperature for such an electrolyte system is less than 100°C and normally 85°C, because a large amount of water formed during the rapid esterification of glycol and borate species at higher temperature impairs the electric properties of the electrolytic capacitors. The minimum operating temperature in such a system is above -20°C since glycol freezes at -17°C. On the other hand, a solution of an amine or a quaternary ammonium salt of carboxylic acid in an aprotic solvent such as N,N-dimethylformamide or γ-butyrolactone is used for low voltage electrolytic capacitors, which have good low temperature characteristics (U.S. Patents 3,812,039 and 4,473,864). However, electrolytes which have higher electric conductivity over the wider temperature range are desirable for imparting lower equivalent series resistance (ESR) and lower impedance at high frequencies to the electrolytic capacitor containing them. According to GB-A-928 820, benzyl triethyl ammonium chloride or phenyl dimethyl allyl ammonium iodide can be used as a solute, together with borates and phosphates, in an electrolyte. As the solvents, propylene carbonate, γ-valerolactone and butyrolactone are mentioned. As the result of various investigations on discovering electrolyte systems having higher electric conductivity, the inventors have discovered that an electrolyte containing a quaternary ammonium salt of an inorganic acid dissolved in an aprotic solvent mainly composed of γ-butyrolactone shows higher electric conductivity than those of conventional electrolyte systems and have thus devised this invention. Therefore, this invention provides an electrolyte for aluminum electrolytic capacitor comprising the features specified in claim 1. This electrolyte can reduce the internal resistance of the electrolytic capacitor and broaden the temperature range over which the electrolytic capacitor can be used. The cation component of the solute for use in this invention is a quaternary tetraalkyl (C₁₋₄) ammonium ion and examples of the ion are aliphatic quaternary ammonium ions such as tetraethylammonium, tetrapropylammonium, tetrabutylammonium, methyltriethylammonium, methyltripropylammonium, methyltributylammonium, dimethyldiethylammonium, dimethyldipropylammonium, dimethyldibutylammonium, ethyltripropylammonium, ethyltributylammonium, diethyldipropylammonium, diethyldibutylammonium, triethylpropylammonium, triethylbutylammonium ; and alicyclic quaternary ammonium ions such as N,N-dimethylpyrrolidinium, N,N-dimethylpiperidinium, N-methyl-N-ethylpyrrolidinium, N-methyl-N-ethylpiperidinium, N,N-diethylpyrrolidinium, N,N-diethylpiperidinium, N,N-tetramethylenepyrrolidinium, N,N-pentamethylenepiperidinium. The anion component of the solute for use in this invention is a conjugated base of an inorganic acid compound selected from (1) boric acid, (2) phosphoric acid, (3) phosphorous acid and phosphorous acid monoesters, and phosphonic acids and phosphonic acid monoesters, (4) hypophosphorous acid and phosphinic acids, (5) alkylboric acids and arylboric acids, (6) silicic acid, and (7) carbonic acid and carbonic acid monoesters the conjugated bases of compounds (1) to (7) having the formulae specified in claim 1. The anion component of the solute for use in this invention is explained in more detail. (1) The conjugated base of boric acid (pKa 9.2) has the structure shown by the formula (I): [H₂BO₃] ⊖ (I) The quaternary ammonium salt of the acid is obtained by adding at least one equivalent of a quaternary ammonium hydroxide to boric acid followed by heating, vacuum dehydrating, and drying and according to the result of the elemental analysis, the salt is an acid salt represented by R₄N·H₂BO₃·H₂O (wherein R represents a (C₁₋₄) alkyl group). (2) The conjugated base of phosphoric acid (pKa 2.2) has the structure shown by the formula (II): wherein x represents 0, 1 or 2 and may form an acid salt or a neutral salt. (3) The conjugated bases of phosphorous acid and phosphorous acid monoesters, and phosphonic acids and phosphonic acid monoesters are shown by the formula (III): wherein R₁ and R₂ each represent a hydrogen atom or a hydrocarbon group having 1 to 10 carbon atoms. Specific examples of these bases are anions of phosphorous acid (pKa 1.2), phosphorous acid monomethyl esters, alkylphosphonic acids such as methylphosphonic acid (pKa 2.4), alkylphosphonic acid monoesters such as monomethyl methylphosphonate, arylphosphonic acids such as phenylphosphonic acid, arylphosphonic acid monoesters such as monomethyl phenylphosphonate. (4) The conjugated bases of hypophosphorous acid and phosphinic acids are shown by the formula (IV): wherein R₃ and R₄ each represents a hydrogen atom or a hydrocarbon group having 1 to 10 carbon atoms. Specific examples of them are anions of hypophosphorous acid (pKa 1.2), alkylphosphinic acids such as methylphosphinic acid (pKa 3.1) and dimethylphosphinic acid, arylphosphinic acids such as diphenylphosphinic acid, etc. (5) The conjugated bases of alkylboric acids and arylboric acids are shown by the formula (V): wherein R₅ represents a hydrocarbon group having 1 to 10 carbon atoms. Specific examples of them are anions of methaneboric acid, ethaneboric acid, phenylboric acid (pKa 8.3), etc. (6) The conjugated bases of silicic acid (pKa 9.8) are shown by the formula (VI): [H x Si y O z ] n⊖ (VI) wherein x represents from 0 to 9, y represents from 1 to 10, z represents from 3 to 25, and n represents from 1 to 10, it being difficult to obtain a single compound as the conjugated base and the base may be a mixture. (7) The conjugated bases of carbonic acid (pKa 6.4) and carbonic acid monoesters are shown by the formula (VII) wherein R₆ represents a hydrogen atom or a hydrocarbon group having 1 to 10 carbon atoms. Specific examples thereof are anions of monomethyl carbonate, monoethyl carbonate and monophenyl carbonate. R₁ to R₆ in the formulae (III), (IV), (V) and (VII) described above are preferably a hydrocarbon group having a low molecular weight, such as a methyl group, an ethyl group, etc., in the case of obtaining the electrolyte having high electric conductivity and are preferably a hydrocarbon group having 4 or more carbon atoms in the case of obtaining the electrolyte having high scintillation voltage. Also, R₁ to R₆ usually do not contain a functional group but they may contain a functional group such as a hydroxy group, an amino group, a nitro group, etc. The anions of the strong acids are apt to corrode the oxide film because of their high acidity. Also, the anions of the acids containing halogen atom liberate a halogen ion unpreferable for aluminum electrode. On the other hand, the anions of the above-mentioned inorganic acid compounds are preferred since the acidities of the inorganic acid compounds are weak so that the anions of the inorganic acid compounds are excellent in the anodic oxidation film-forming faculty of aluminum and, in particular, boric acid (pKa 9.2) is a good "film-forming anion", and has high scintillation voltage, and hence can be used as medium in high voltage capacitors. The solvent for dissolving the solute for use in this invention is an aprotic solvent containing at least 90% by weight of γ-butyrolactone and less than 10% by weight of other aprotic solvent(s). Examples of other aprotic solvents which can be used as a minor portion of the solvent to be admixed with γ-butyrolactone are amides such as N-methylformamide, N-ethylformamide, N,N-dimethylformamide, N,N-diethylformamide, N-methylacetamide, N-ethylacetamide, N,N-dimethylacetamide, N,N-diethylacetamide, and N-methylpyrrolidinone, lactones such as β-butyrolactone, γ-valerolactone and δ-valerolactone, carbonates such as ethylene carbonate, propylene carbonate, and butylene carbonate, sulfolanes such as sulfolane and 3-methylsulfolane, nitriles such as 3-methoxypropionitrile, and phosphates such as trimethyl phosphate. Furthermore, γ-butyrolactone has a freezing point-boiling point range so broad that the freezing point thereof is -45°C and it is lower than that of ethylene glycol (-13°C), and the boiling point thereof is 204°C and it is higher than that of N,N-dimethylformamide (153°C). Also, γ-butyrolactone is less toxic and inflammable than N,N-dimethylformamide. Furthermore, γ-butyrolactone does not attack the sealing gaskets compared with amide solvents, and the electrolytic capacitor using this solvent does not suffer serious damage from halogen ion generated from the washing agent for solder flux which can be transmitted through a closure. The amount of the quarternary ammonium salt dissolved in the solvent is below the saturation concentration, preferably from 0.1 to 40% by weight based on the total weight of the electrolyte. The electrolyte of this invention is essentially composed of the quaternary ammonium salt of the aforesaid inorganic acid compound and the solvent but may further contain a small amount of an auxiliary solutes for various purposes such as the prevention of electrolytic corrosion, the reduction of leaking current, absorption of hydrogen gas, etc. The quaternary ammonium salt of the inorganic acid compound which is used as a solute in this invention has good solubility in the solvent mainly composed of γ-butyrolactone and the electrolyte containing the quaternary ammonium salt shows high electric conductivity and is suitable for capacitors having a wide usable temperature range. Now, the invention will be explained in greater detail with reference to the following examples, and to the drawing, which shows the relation between the electrolyte conductivity and the temperature for Example 1 and Comparative Example 1. EXAMPLE 1 [Synthesis of the quaternary ammonium salt of boric acid] After adding 110.45 g (0.3 mol) of an aqueous 40% NEt₄OH solution to 6.18 g (0.1 mol) of H₃BO₃, they were reacted at 60°C until the system became homogeneous and then water was distilled off at 60°C in vacuo. When the white powder obtained was subjected to elemental analysis, the following result was obtained. Also, the product obtained by following the same steps as above using 73.63 g (0.2 mol) of an aqueous 40% NEt₄OH solution showed almost the same elemental analysis value as above. An electrolyte was obtained by dissolving the tetraethylammonium salt of boric acid thus obtained in an amount of 10% by weight based on a weight of an electrolyte in γ-butyrolactone as a solvent. The electric conductivity of the electrolyte at 25°C was 4.9 mS/cm and the scintillation voltage was 330 V when a constant electric current of 4 mA/cm² was applied to one set of plus and minus smooth aluminum foils in the electrolyte. Also, the change of the electric conductivity of the electrolyte by the change of temperature is shown in the drawing (□). COMPARISON EXAMPLE 1 An electrolyte was obtained by dissolving ammonium borate in an amount of 10% by weight based on a weight of an electrolyte in ethylene glycol as a solvent. The electric conductivity and the scintillation voltage of the electrolyte were measured in the same manner as in Example 1. The electric conductivity and the scintillation voltage of the electrolyte were 1.06 mS/cm and 450 V, respectively. The electric conductivity thereof at -20°C was 0.14 mS/cm and was frozen at -40°C, which made measurement impossible. The change of the electric conductivity of the electrolyte by the change of temperature is shown in the drawing (▪). COMPARISON EXAMPLE 2 When it was attempted to dissolve ammonium borate in γ-butyrolactone as a solvent, the borate scarcely dissolved in the solvent (less than 0.1%), the electric conductivity of the supernatant liquid at 25°C was 0.01 mS/cm, and the mixture was unsuitable for use as an electrolyte. EXAMPLE 2 Electrolytes were prepared by following the same procedure as in Example 1 while changing the concentration of the solute as shown in Table 1. The electric conductivities and the scintillation voltages of the electrolytes were measured in the same manner as in Example 1. The results are shown in Table 1 below. COMPARISON EXAMPLES 3 TO 5 Electrolytes were obtained by dissolving (C₄H₉)₃CH₃N·BF₄ (Comparison Example 3), (C₄H₉)₄N·BF₄ (Comparison Example 4), and (C₄H₉)₄N·B(C₆H₅)₄ (Comparison Example 5), respectively, in an amount of 1% by weight based on the weight of an electrolyte or high concentration in γ-butyrolactone as a solvent and the electric conductivities and the scintillation voltages thereof were measured in the same manner as in Example 1. The results are shown in Table 2 below. In each case the anodic oxidation film was greatly corroded, so that scintillation was not observed. EXAMPLE 3 [Synthesis of quaternary ammonium salt of phosphoric acid] To 2.31 g (0.02 mol) of an aqueous 85% H₃PO₄ solution was added 44.18 g (0.06 mol) of an aqueous 20% NEt₄OH solution, and after causing reaction at 60°C, water was distilled off in vacuo to provide a white solid. The result of the elemental analysis was as follows. An electrolyte was obtained by dissolving the tetraethylammonium salt of phosphoric acid thus obtained in an amount of 20% by weight based on a weight of an electrolyte in γ-butyrolactone as a solvent. The electric conductivity of the electrolyte at 25°C was 6.7 mS/cm. EXAMPLE 4 An electrolyte was obtained by dissolving monotetraethylammonium phosphite in an amount of 20% by weight based on a weight of an electrolyte in γ-butyrolactone as a solvent. The electric conductivity of the electrolyte at 25°C was 7.4 mS/cm and the highest voltage attained was 140 V when a constant electric current of 5 mA/cm² was applied to one set of plus and minus smooth aluminum foils in the electrolyte. EXAMPLES 5 TO 8 Electrolytes were obtained by following the same procedure as in Example 4 using monotetraethylammonium methylphosphonate (Example 5), methyltriethylammonium methyl methylphosphonate (Example 6), monotetraethylammonium hypophosphite (Example 7), and tetraethylammonium dimethylphosphinate (Example 8), respectively, in place of monotetraethylammonium phosphite. The electric conductivities and the highest voltages attained of these electrolytes were measured in the same manner as in Example 4 and the results obtained are shown in Table 3 below. EXAMPLE 9 [Synthesis of ammonium salt of methaneboric acid] To 1.27 g (0.02 mol) of methaneboric acid was added 7.85 g (0.02 mol) of an aqueous 40% NEt₄OH solution and after causing reaction at 60°C, water was distilled off from the reaction mixture in vacuo to provide a white solid. The product was an acid salt having the structure of An electrolyte was obtained by dissolving the tetraethylammonium salt of methaneboric acid thus obtained in an amount of 20% by weight based on a weight of an electrolyte in γ-butyrolactone as a solvent. The electric conductivity of the electrolyte at 25°C was 5.5 mS/cm and the scintillation voltage was 120 V when a constant electric current of 5 mA/cm² was applied to one set of plus and minus smooth aluminum foils in the electrolyte. EXAMPLE 10 [Synthesis of quaternary ammonium salt of silicic acid] To 2 g of silicic acid (SiO₂·xH₂O) was added 41.68 g of an aqueous 19% NEt₄OH solution and after causing reaction at 60°C until the mixture became homogeneous, water was distilled off from the reaction mixture in vacuo at 60°C to provide a white solid. An electrolyte was obtained by dissolving the tetraethylammonium salt of silicic acid thus obtained in an amount of 20% by weight based on a weight of an electrolyte in γ-butyrolactone as a solvent. The electric conductivity of the electrolyte at 25°C was 6.9 mS/cm and the scintillation voltage was 120 V when a constant electric current of 4 mA/cm² was applied to one set of plus and minus smooth aluminum foils in the electrolyte. EXAMPLE 11 An electrolyte was obtained by dissolving a tetraethylammonium salt of carbonic acid in an amount of 20% by weight based on a weight of an electrolyte in γ-butyrolactone as a solvent. The electric conductivity of the electrolyte at 25°C was 9.6 mS/cm and the scintillation voltage was 125 V when a constant electric current of 4 mA/cm² was applied to one set of plus and minus smooth aluminum foils in the electrolyte. COMPARISON EXAMPLE 6 An electrolyte was obtained by following the same procedure as in Example 11 using a triethylammonium salt of maleic acid in place of the tetraethylammonium salt of carbonic acid in Example 11. The electric conductivity and the scintillation voltage of electrolyte were measured in the same manner as in Example 11. The electric conductivity and the scintillation voltage of the electrolyte were 4.2 mS/cm and 114 V, respectively. EXAMPLE 12 An electrolyte was obtained by dissolving methyltriethylammonium methyl carbonate in an amount of 5% by weight based on a weight of an electrolyte in γ-butyrolactone as a solvent. The electric conductivity of the electrolyte at 25°C was 3.0 mS/cm and the scintillation voltage was 180 V when a constant electric current of 5 mA/cm² was applied to one set of plus and minus smooth aluminum foils in the electrolyte.

Claims: An electrolyte for an aluminium electrolytic capacitor comprising a solution of, as a solute, a quaternary ammonium salt having as the anion component the conjugated base of an inorganic acid compound selected from: (1) boric acid of formula: [H₂BO₃·H₂O] ⊖ (2) phosphoric acid of formula (II): wherein x represents 0,1 or 2; (3) phosphorous acid and phosphorous acid monoesters, phosphonic acids, and phosphonic acid monoesters of the formula (III): (4) hypophosphorous acid and phosphinic acids of formula (IV): (5) alkylboric acids and arylboric acids of formula (V): (6) silicic acid of formula (VI): [H x Si y O z ] n⊖ , wherein x represents from 0 to 9, y represents from 1 to 10, z represents from 3 to 25, and n represents from 1 to 10; and (7) carbonic acid and carbonic acid monoesters of formula (VII): with R₁, R₂, R₃, R₄, R₅ and R₆ each representing a hydrogen atom or a hydrocarbon group having 1-10 carbon atoms; and as a cation component a tetraalkyl (C₁₋₄)ammonium ion wherein two of said alkyl groups may combine to form an alicyclic ring, the solute being dissolved in an aprotic solvent containing at least 90% by weight of γ-butyrolactone. An electrolyte for an aluminium electrolytic capacitor as claimed in Claim 1, wherein the concentration of the quaternary ammonium salt is from 0.1 to 40% by weight based on the total weight of electrolyte.

Inventors: IDA KAZUHIKO C O MITSUBISHI PE, MORI SHOICHIRO C O MITSUBISHI, UE MAKOTO C O MITSUBISHI PETRO, IDA, KAZUHIKO C/O MITSUBISHI PETROCHEM. CO., LTD, MORI, SHOICHIRO C/O MITSUBISHI PETROCHEM. CO., LTD, UE, MAKOTO C/O MITSUBISHI PETROCHEM. CO., LTD
Applicants: MITSUBISHI PETROCHEMICAL CO, MITSUBISHI PETROCHEMICAL CO., LTD.
Application year: 1987
Main classification: H01G9
IPC codes: H01G9