AMMONIA OXIDATION CATALYST PACK

Abstract: A catalyst pack (1) for the manufacture of nitric acid by oxidising ammonia comprises at least one layer (2, 3, 4, 5, 6) of elongate elements made from at least one platinum group metal or alloy and at least one foraminous layer (7, 8) of ceramics material having a coating of one or more platinum group metals or alloys or mixture. In use the catalyst pack has improved conversion efficiencies. The preferred ceramics material comprises either alumina, silica and boria or zirconia in the form of a cloth.

Description: This invention relates to a catalyst pack for the manufacture of nitric oxide by oxidising ammonia and to a process for the manufacture of nitric oxide by oxidising ammonia in the presence of such a catalyst pack. Conventionally, in the manufacture of nitric oxide by the oxidation of ammonia, a mixture of air and ammonia at 150° to 300°C is passed over an oxidation catalyst comprising platinum and 0 to 20 wt% of rhodium and/or 0 to 40 wt% of palladium (based on the weight of the alloy). Such a catalyst preferably comprises platinum and from 0 to 25 wt% of rhodium (based on the weight of the platinum). The catalyst is in the form of a foraminous layer of elongate elements usually in the form of wires fabricated into one or more gauzes. A simplified equation for the process is 4NH₃ + 50₂ → 4NO + 6H₂O. Generally, a nitric oxide manufacturing plant requires between 2 and 40, and preferably between 4 and 25, catalyst gauzes. The number of gauzes is dependent on the pressure and the loading of reactants required to operate effectively. Both platinum and rhodium are expensive; hence one objective of this invention is to reduce the amount of these elements used in the catalyst. Another objective is to provide a catalyst pack which improves the efficiency of the ammonia oxidation process. According to a first aspect of the invention there is provided a catalyst pack for the manufacture of nitric oxide by oxidising ammonia comprising at least one foraminous layer of elongate elements made from at least one platinum group metal selected from platinum and rhodium or alloy thereof and at least one layer of foraminous ceramics material having a coating of one or more platinum group metals selected from platinum and rhodium or alloys or mixtures thereof. According to a second aspect of the invention there is provided a process for the manufacture of nitric oxide by oxidising ammonia in the presence of a catalyst pack which comprises at least one foraminous layer of elongate elements made from at least one platinum group metal selected from platinum and rhodium or alloy thereof and at least one layer of foraminous ceramics material having a coating of one or more platinum group metals selected from platinum and rhodium or alloys or mixtures thereof. Preferred features of the invention will be apparent from the following description and from the subsidiary claims of the specification. The term 'foraminous layer of elongate elements' is intended to cover any foraminous layer, formed from wires, filaments, fibres, etc and so includes conventional forms of catalyst such as wire gauzes, wire pads, fibre packs, etc. The term 'layer of foraminous ceramics material' is intended to cover any foraminous layer, formed of ceramics material and so includes layers of ceramics fibres which are woven, knitted or felted to form a cloth. The invention will now be illustrated, merely by way of example, with reference to the drawing which shows a schematic cross-section of one embodiment of a catalyst pack according to the invention. The drawing shows a catalyst pack 1 suitable for use in the manufacture of nitric oxide. The direction of flow of the mixture of air and ammonia through the catalyst pack 1 is shown by arrow A. The catalyst pack 1 comprises five catalyst layers 2, 3, 4, 5 and 6 composed of wire with a diameter of 0.076 mm woven to produce a gauze of mesh size 1024 apertures cm⁻² and two ceramic layers 7 and 8. The catalyst pack is arranged with, from the upstream side of the pack to the downstream side thereof, four catalyst layers 2, 3,4 and 5, two ceramic layers 7 and 8 and a further catalyst layer 6. The wire is made from an alloy of platinum with 10 wt % (based on the weight of alloy) of rhodium. Ceramic layers 7 and 8 are made from a ceramic material comprising 62 wt% alumina, 24 wt% silica and 14 wt% boria. The ceramic material is in the form of fibres with a diameter of 8 to 10µm which are spun into a thread and woven to produce a gauze of mesh size 50 apertures cm⁻². Such a gauze has an open area of 52.6%. The ceramics material has a coating of 10 wt% platinum (based on the ceramics material) which is deposited by contacting the ceramics material with a solution of tetramineplatinum(II) chloride (Pt(NH₃)₄Cl₂) and then drying and then reducing the salt to platinum by heating. The catalyst gauzes 2, 3, 4, 5 and 6 preferably comprise a platinum/rhodium alloy as described above. Most preferably, the gauzes comprise platinum and from 0 to 20 wt% of rhodium (based on the weight of the alloy) The layers of ceramics material preferably comprise intercrossing threads which define the apertures and which may be woven, knitted or felted to give cloth having an open area of from 10 (or preferably 30) to 60%. A simple weave gives a mesh size of from 9 to 1024 apertures cm⁻². Each thread preferably comprises a body of (for example spun or twisted) fibres, each fibre having a diameter of from 1 to 100 µm and especially 1 to 20µm. 1µm is 10⁻⁶m. The ceramics material should be stable at temperatures of from 800° to 1200°C and be inert to platinum and rhodium. Suitable ceramics include one or more oxides, borides, carbides, silicides, nitrides and/or silicates of aluminium, silicon, zirconium, borium, magnesium, titanium, yttrium, beryllium, thorium, manganese, lanthanum, scandium, calcium, uranium, chromium, niobium, hafnium, or any combination of these. A preferred ceramics composition comprises alumina, 0 to 30 wt% (preferably 0 to 25 wt%) silica and 0 to 15 wt% boria. It is particularly preferred to use a ceramics composition with a silica content as low as possible as silica promotes formation of rhodium oxide. For this reason, the most preferred silica content is from 0 to 25 wt%. Another preferred material is zirconia which has been found to be relatively inert to platinum. The coating of at least one platinum group metal selected from platinum and rhodium on the ceramics material can be continuous or discontinuous. The coating is of platinum or rhodium or alloys or mixtures thereof. Preferably the coating is deposited onto the ceramics material by contacting the ceramics material with a solution containing one or more platinum and/or rhodium salts and then drying the material and reducing the salt to metals. The coating produced by this method may comprise 1.5-70 wt% (based on the ceramics material). Preferably, the coating comprises platinum 3.0-30 wt% and/or rhodium 1-10 wt% (based on the ceramics material). Alternatively, the coating may be deposited by vapour deposition or sputtering. The coating weight can be considerably reduced if it is formed by vapour deposition or sputtering since these methods produce a coating made up of much finer particles than the plating process described above. A coating formed by vapour deposition or sputtering may thus comprise less than 1.5 wt% (based on the ceramic materials). The layers of ceramics material are preferably positioned in the downstream portion of the pack as described. However, they may also be positioned in the upstream portion of the pack in which case the coating weight of the platinum group metals would be towards the upper end of the quoted range in view of the increased activity in that portion of the pack. The invention is further illustrated by the following Examples 1-17 and comparative Examples A, B, C and D. EXAMPLES 1 to 17 AND COMPARATIVE EXAMPLES A, B, C AND D These examples illustrate how the efficiency of the ammonia oxidation process over the catalyst pack is improved when the catalyst pack contains one or more ceramic layers coated with platinum group metal. For the purposes of Example 1, a catalyst pack of the type shown in the drawing was used in the manufacture of nitric oxides. The catalyst pack consisted of a total of five layers of woven platinum/rhodium wire gauze made from an alloy of platinum 5 wt% (based on the weight of the alloy) rhodium and two layers of an foraminous ceramics cloth. The catalyst pack was arranged,from the upstream side of the pack, with four layers of woven platinum/rhodium wire, two layers of an foraminous ceramics cloth and a further layer of woven platinum/rhodium wire. The five layers of the platinum/rhodium were made from wire of diameter 0.076 mm woven into a gauze of mesh size 1024 apertures cm⁻² which gives a gauze with an open area of 57%. The ceramics cloth consisted of a ceramics material composed of 62 wt% alumina, 24 wt% silica and 14 wt% boria formed into fibres of diameter 11 µm which in turn were spun into threads and woven to make a cloth of mesh size 50 apertures cm⁻² which gave the cloth an open area of 52.6%. The ceramic cloth had a coating of platinum 2.5 wt% (based on the ceramic cloth) deposited thereon by dipping the cloth in a solution of tetramineplatinum(II) chloride which was then dried. The performance of the catalyst pack was tested in the manufacture of nitric oxide as follows: A reactant mixture consisting of air containing 10 volume % ammonia was passed through the catalyst pack at a pressure of 4 bar. The reactant mixture was heated to 270°C before entry into the catalyst pack. The conversion efficiency for the conversion of ammonia to nitric oxide is conventionally expressed in terms of the amount of nitric acid which can be obtained from the nitric oxide after it has been oxidised to nitrogen dioxide and dissolved in water. The amount of nitric acid which would be obtained for various reactant feed rates (assuming perfect conversion) was therefore determined and the conversion efficiency is given as a percentage of this. For the purposes of Examples 2, 3, 4 and 5, the two ceramic layers were coated with platinum 5.0, 10, 16.5 and 25.7 wt% respectively (based on the ceramic layers) and the procedure of Example 1 repeated. The conversion efficiencies obtained are shown in Table 1. For the purposes of Example 10, the two ceramic layers were coated with platinum 9.7 wt% and rhodium 2.5 wt% (based on the ceramic layers) from a solution containing tetramine-platinum(II) chloride and a second solution containing rhodium nitrate and the procedure of Example 1 repeated. The conversion efficiencies obtained are shown in Table 1. For the purposes of Examples 11, 12 and 13, two ceramic layers were coated with platinum and rhodium as in Example 10. The coatings were as follows:- Example Platinum wt% Rhodium wt% 11 17.8 2.4 12 18.1 3.4 13 18.0 6.3 The procedure of Example 1 was repeated and the conversion efficiencies obtained are shown in Table 1. For the purposes of Example 16, the two ceramic layers were fabricated from a ceramics cloth which consisted of a ceramics material composed of zirconia fibres woven into a cloth of mesh size 54 apertures/cm² with an average open area of 31%. The ceramics cloth had a coating of platinum 19.2 wt% and rhodium 1.6 wt% (based on the ceramic cloth) deposited by dipping into a solution of tetramineplatinum (II) chloride and a second solution of rhodium nitrate and then drying. The procedure of Example 1 was repeated and the conversion efficiencies obtained are shown in Table 1. For the purposes of Comparative Example A, the procedure of Example 1 was repeated except that the ceramics layers were omitted from the catalyst assembly. The conversion efficiencies obtained are shown in Table 1. For the purpose of Comparative Example B, the procedure of Example 1 was repeated except that the ceramics layers were not coated with a platinum group metal. The conversion efficiencies obtained are shown in Table 1. For the purpose of Comparative Examples C and D, the procedure of Example 1 was repeated except that the ceramic layers were omitted and replaced by three and five further layers of woven platinum/rhodium wire giving a pack comprising eight and ten conventional platinum/rhodium gauzes, respectively. The conversion efficiencies obtained are shown in Table 1. Example Coating of ceramic cloth REACTANT FEED RATE (Tonnes NH₃m⁻² day ⁻¹) 12 16 Actual Conversion Efficiencies Achieved expressed as % of Perfect Conversion 1 2.5 wt% Pt 80.6 - 2 5.0 wt% Pt 92.3 93.8 3 10.0 wt% Pt 94.4 93.3 4 16.5 wt% Pt 95.9 93.5 5 25.7 wt% Pt 90.2 93.0 10 9.7 wt% Pt 90.0 86.2 2.5 wt% Rh 11 17.8 wt% Pt 96.0 95.4 2.4 wt% Rh 12 18.1 wt% Pt 91.1 92.9 3.4 wt% Rh 13 18.0 wt% Pt 85.0 94.7 6.3 wt% Rh 16 19.2 wt% Pt 95.1 95.2 2.6 wt% Rh A no ceramic layers 81.5 78.7 B no coating 89.0 83.4 C no ceramic layers 92.5 95.6 D no ceramic layers 95.5 94.5 A comparison of examples 1-17 with Examples A and B shows that the conversion efficiency obtained with a catalyst pack comprising a number of ceramic layers having a coating of platinum and/or rhodium is improved compared to that obtained with a pack without such ceramic layers or uncoated ceramic layers. A comparison with Examples C and D shows the conversion efficiency achieved with a catalyst pack comprising five platinum/rhodium wire layers and two ceramic layers coated with platinum group metal with a flow rate of 12 tonnes NH₃m⁻²day⁻¹ is better than that obtained with eight platinum/rhodium wire gauzes and nearly as good as that obtained with ten, and for a flow rate of 16 tonnes NH₃m⁻²day⁻¹ is as good as that obtained with ten platinum/rhodium gauzes.

Claims: A catalyst pack for the manufacture of nitric oxide by oxidising ammonia comprising at least one foraminous layer of elongate elements made from at least one platinum group metal selected from platinum and rhodium or alloy thereof and at least one layer of foraminous ceramics material having a coating of one or more platinum group metals selected from platinum and rhodium or alloys or mixtures thereof. A catalyst pack according to Claim 1, wherein the coating comprises 1.5 to 70 wt% of platinum and/or rhodium or alloy or mixture thereof. A catalyst pack according to Claim 1, wherein the coating comprises up to 1.5 wt% of platinum and/or rhodium or alloys or mixtures thereof deposited by vapour deposition or sputtering. A catalyst pack according to any of Claims 1 to 3, wherein the said at least one layer of foraminous ceramics material comprises intercrossing ceramics fibres which define the apertures of the foraminous material. A catalyst pack according to Claim 4, wherein the fibres make up a woven cloth. A catalyst pack according to any of Claims 1 to 5, wherein the open area of the foraminous ceramics material comprises from 10 to 60% of the area thereof. A catalyst pack according to any of Claims 1 to 6, wherein the ceramics material comprises one or more oxides, borides, carbides, silicides, nitrides and/or silicates of aluminium, silicon, zirconium, borium, magnesium, titanium, yttrium, beryllium, thorium, manganese, lanthanum, scandium, calcium, uranium, chromium, niobium and hafnium. A catalyst pack according to Claim 7, wherein the ceramics material comprises alumina, 0 to 30 wt% silica and 0 to 15 wt% boria. A catalyst pack according to Claim 7, wherein the ceramics material comprises zirconia. A process for the manufacture of nitric oxide by oxidising ammonia in the presence of a catalyst pack, which comprises at least one foraminous layer of elongate elements made from at least one platinum group metal selected from platinum and rhodium or alloy thereof and at least one layer of foraminous ceramics material having a coating of one or more platinum group metals selected from platinum and rhodium or alloys or mixtures thereof. A process according to Claim 10, wherein the said at least one layer of the ceramics material is positioned in the downstream portion of the pack. A process according to Claim 11, wherein the catalyst pack comprises, from the upstream thereof side, four foraminous layers of elongate elements, two layers of foraminous ceramics material and a further foraminous layer of elongate elements.

Inventors: HANDLEY, JACK RICHARD
Applicants: JOHNSON MATTHEY PUBLIC LIMITED COMPANY
Application year: 1987
Main classification: C01B21
IPC codes: B01J35, C01B21, B01J23