CALORIMETER USING REMANENCE TYPE ELECTROMAGNETIC FLOWMETER

Abstract: A calorimeter using a remanence type electro­ magnetic flowmeter includes a core (5a, 5b) made of a semi-hard or hard magnetic material and having a property in which a remanent magnetic flux density is varied in proportion to a temperature, a coil (6a, 6b) excited intermittently to magnetize the core, a metallic pipe (l) forming a fluid path, a yoke (4a, 4b) for conducting remanent magnetic flux of said core, the yoke being fixed to the outer surface of the metallic pipe in close contact therewith without forming an air gap there­ between, and a pair of electrodes (3a, 3b) attached to the inner surface of the metallic pipe through an insulator (7a, 7b).

Description: BACKGROUND OF THE INVENTION The present invention relates to a calorimeter, and in particular, to a calorimeter using a remanence type electromagnetic flowmeter. A calorimeter composed of three sections including a section for measuring a flow rate of a fluid which is a heat transfer medium, a section for measuring a temperature of the fluid, and a computing section for multiplying a volume of the fluid measured in the flow rate measuring section by the temperature of the fluid measured in the temperature measuring section is known from Japanese Patent No. 906509. In the prior art calorimeter, since it is composed of three sections including the flow rate measur­ ing section, the temperature measuring section, and the computing section, there is a problem in that the structure is complicated and the costs are high. SUMMARY OF THE INVENTION A calorimeter in accordance with the present invention is designed to obtain an induced voltage proportional to an amount of heat directly from a pair of electrodes by utilizing a phenomenon in that a remanent magnetic flux density applied to a fluid path of an electromagnetic flowmeter is proportional to a temperature of the fluid. Accordingly, a calorimeter which is simple in the structure and low in the manufacturing costs can be obtained. In the present invention in order to solve the aforemention problem, a calorimeter using a remanence type electromagnetic flowmeter is provided with a core made of a semi-hard or hard magnetic material, a coil intermittently excited to magnetize the core, and a yoke for conducting remanence of the core to a metallic pipe forming a fluid path, and wherein the core has a property in which a remanent magnetic flux density is varied in proportion to a temperature, and an end surface of the yoke is fixed to an outer surface of the metallic pipe in close contact therewith without forming an air gap therebetween. In the remanence type electromagnetic flowmeter, when the fluid which is a heat transfer medium flows in the metallic pipe, an induced voltage proportional to the product of the flux density in the fluid path and the flow rate of the fluid is generated in the pair of electrodes of the electromagnetic flowmeter. The heat of the fluid is conducted from the metallic pipe to the core via the yoke, and the temperature of the core becomes the same temperature as the fluid, and the remanence flux density applied to the fluid path is varied in proportion to the fluid temperature. As a result, the induced voltage proportional to the product of the fluid flow rate and the fluid temperature is generated in the pair of electrodes of the electromagnetic flowmeter. This induced voltage is proportional to the amount of heat of the fluid which is a heat transfer medium. BRIEF DESCRIPTION OF THE DRAWINGS Fig. l is a transverse sectional view showing a part of an embodiment of the present invention; and Figs. 2 and 3 are graphs showing characteristics of a magnetic circuit in the embodiment of the present invention. DESCRIPTION OF THE PREFERRED EMBODIMENTS In Fig. l illustrating an embodiment of the present invention, the reference numeral l designates a metallic pipe of a non-magnetic material constituting a fluid path, and a fluid which is a heat transfer medium flows through the metallic pipe l. The reference numeral 2 designates an insulating lining formed on the inner surface of the metallic pipe l; 3a, 3b electrodes; 4a, 4b yokes; 5a, 5b cores made of a semi-hard or hard magnetic material; and the cores 5a, 5b are respectively wound with exciting coils 6a, 6b. End surfaces of the yokes 4a, 4b constituting a magnetic circuit are fixed to the outer surface of the metallic pipe l in close contact therewith so that no air gap is formed therebetween as shown in Fig. l. This fixing is carried out by securing nuts fitted to opposite ends of each of the cores 5a, 5b. The reference numerals 7a, 7b designate packings for electrically insulating the electrodes 3a, 3b from the metallic pipe l and also for sealing therebetween. The coils 6a, 6b are intermittently excited by an exciting current from an electronic circuit 8, and a voltage which is proportional to the product of a remanent magnetic flux density applied to the fluid path due to the remanence of the cores 5a, 5b during the exciting current is zero and a fluid flow rate is induced in the electrodes 3a, 3b. Such operation of the so-called remanence type electromagnetic flowmeter in which the core is magnetized by supplying the exciting current to the coils inter­ mittently, and the fluid flow rate is measured by the remanence after the exciting current is interrupted is well known, for example, from United States Patent No. 4,409,846. In the present invention, the cores 5a, 5b have a property in which the remanent magnetic flux density is varied in proportion to a temperature. Fig. 2 shows B-H curves of such cores 5a, 5b. In Fig. 2, the B-H curves designated by a , b , c , and d are obtained respectively at temperatures T₁, T₂, T₃, and T₄°C, and differences in the temperatures T₁, T₂, T₃, and T₄ are in a relationship T₁ < T₂ < T₃ < T₄. A coercive force of each B-H curve is represented by H cl , H c2 , H c3 , and H c4 , and an amount of change in the coercive force is proportional to a change in temperature. A straight line L₁ is a performance line of the magnetic circuit, and the gradient of the line L₁ is principally dependent on a magnitude of a magnetoresistance of the magnetic circuit, and a length and a sectional area of the magnetic material. First, at the temperature T₁°C, after exciting according to the line L₁ up to H₀ of L₂, the excitation is interrupted, and next, after exciting up to -H₀ of L₃, the excitation is interrupted. In this manner, by repeating the excitation alternately in the opposite directions intermittently, the B-H curve of a is developed. And the flux density B at the intersection of the B-H curve of a and the straight line (performance line) L₁ represents a remanent magnetic density B ra . When the temperature rises to T₂°C and the coercive force becomes H c2 , by applying the excitation of H₀ and -H₀ alternately and intermittently, the B-H curve of b is obtained, and the remanent magnetic flux density becomes B rb . Further, when the temperature rises to T₃, T₄°C and the coercive force of the core becomes H c3 , H c4 , similarly, the B-H curves of c , d are obtained, and the remanent magnetic flux density varies to B rc , B rd . And, when the temperature is T°C, the remanent magnetic flux density B r is expressed by and, if B o and A o represent the remanent magnetic flux density B r is expressed by B r = B o (l + A o T) ..... (2), and, it is seen that B r is varied in proportion to the temperature T. Also, the A o in the formula (2) can be changed by selecting a magnetic material and by changing the gradient of the performance line L₁. Because of the fact that the remanent magnetic flux density B of the fluid path is proportional to the remanent magnetic flux density B r in the formula (2), if the proportional constant is k, then B is expressed by B = kB r = kB o (l + A o T) ..... (3) . Assuming that a distance between the electrodes is D, and an average velocity is , the voltage e induced in the electrodes is expressed by e = DB = DkB o (l + A o T) ..... (4) . Supposing that the amount of heat passing the fluid path for a time of Δt is ΔQ, the mass of the fluid which is the heat transfer medium is ΔM, the specific heat is C, and the temperature at this time is T°C, then ΔQ = ΔM·C· (T₀ + T) where, T₀ is 273.l5[K]. Further, supposing that the sectional area of the fluid path is S By obtaining from the formula (4) of the induced voltage e, and by substituting in the formula (5), where, K is SCT o /DkB o and it is a constant. Since it is possible to change A o in the formula (2) by changing the gradient of the performance line L₁ by selecting a magnetic material, if the magnetic material is selected so that A o = l/T o = l/273.l5, then the formula (6) is expressed by ΔQ = KeΔ t . Accordingly, the amount of heat Q is expressed by Q = K∫e·d t and Q is proportional to an integrated value of the voltage induced in the electrodes. In the embodiment described in the foregoing, as a material for the cores, the material is used in which the coercive force H c becomes large when the temperature rises as shown in Fig. 2. However, such a material may be used in which as shown in Fig. 3 the coercive force H c is decreased in proportion to a change in temperature as the temperature rises. In this case, as compared with the case in Fig. 2, the gradient of the performance line L₁ is increased, so that remanent magnetic flux densities of B-H curves a , b , c corresponding to temperatures T₁ < T₂ < T₃ are in a relationship B ra < B rb < B rc . And it is possible to make a change in the remanent magnetic flux B r proportional to a change in the temperature. The core may be made of; (I) Iron-Cobalt type alloys i) iron-cobalt-chromium ii) iron-cobalt-niobium iii) iron-cobalt-manganese (II) Alminum-Nickel type alloys i) iron-cobalt-nickel-alminum ii) iron-nickel-alminum (III) Iron-Copper type alloys i) iron-copper ii) iron-copper-manganese Since the remanent magnetic flux density applied to the fluid path of the electromagnetic flowmeter is a value proportional to the temperature, the induced voltage proportional to the amount of heat can be obtained directly in the electrodes. Further, since the thermal resistance between the fluid and the core is small, the induced voltage is accurately responsive to the tempera­ ture of the fluid. Accordingly, a calorimeter having a simple structure can be provided at low cost.

Claims: 1. A calorimeter using a remanence type electro­ magnetic flowmeter comprising: a core (5a, 5b) made of a semi-hard or hard magnetic material, said core having a property in which a remanent magnetic flux density is varied in proportion to a temperature; a coil (6a, 6b) excited intermittently to magnetize said core; a metallic pipe (l) forming a fluid path; a yoke (4a, 4b) for conducting remanent magnetic flux of said core, said yoke being fixed to the outer surface of said metallic pipe in close contact therewith without forming an air gap therebetween; and a pair of electrodes (3a, 3b) attached to the inner surface of said metallic pipe through insulators (7a, 7b). 2. A calorimeter according to Claim l, wherein said core is made of the magnetic material in which a coercive force is increased as the temperature rises. 3. A calorimeter according to Claim l, wherein said core is made of the magnetic material in which a coercive force is decreased as the temperature rises. 4. A calorimeter according to Claim l, wherein said core is made of iron-cobalt type alloys. 5. A calorimeter according to Claim l, wherein said core is made of alminum-nickel type alloys. 6. A calorimeter according to Claim l, wherein said core is made of iron-copper type alloys.

Inventors: AMATA, YOSHITAKA
Applicants: AICHI TOKEI DENKI CO., LTD.
Application year: 1987
Main classification: G01K17
IPC codes: G01K17, G01F1