THIN FILM FORMATION APPARATUS

Abstract: This thin film is formed from a high density plasma generated by electron cyclotron resonance utilising microwaves. The apparatus comprises (1) an evacuated wave-guide chamber having on one end a window for introducing microwaves connected to a microwave guide tube (2) a plasma generating chamber having radius and length large enough to form a cavity resonator, (3) a sample chamber, (4) a vacuum chamber having a gas introducing entrance, and (5) a mirror magnetic field generating system surrounding both ends of the plasma generation chamber. (1), (2), and (3) are connected in that order, (5) is designed to entrap the plasma inside a plasma generation chamber by a mirror magnetic field. At least one pair of targets is disposed inside the plasma generation chamber in a direction at right angles to the magnetic flux. The target is supplied with a negative voltage. The sample chamber is connected to the plasma generation chamber in a direction at right angles to the magnetic flux. (1) is furnished with at least one curved part. The window for introducing microwaves is built at a position where it can not be seen through the target.

Description: The present invention relates to a sputtering apparatus for forming thin films, of the type comprising: a vacuum chamber having a plasma generation chamber including a gas introduction inlet and a microwave introduction window, said microwave introduction window being connected to a microwave waveguide; and a pair of magnetic field generating means disposed around the outer sides of the plasma generation chamber to produce a mirror magnetic field parallel to the central axis of the plasma generation chamber. The present invention also relates to a method of forming a thin film on a substrate using a sputtering apparatus of this type. The so-called sputtering apparatus, for forming a film by sputtering a target as a thin film forming element in plasma, has been used widely in various fields for forming thin films of various materials. For example, an apparatus for producing conventional high frequency or rectifying diodes is described by F M D'Leurle in Metall Transactions Volume 1, March 1970, pages 725 to 732, in which a target 1 and a substrate 2 are disposed in opposing relationship in a vacuum chamber 4 as shown in Figure 1. Similarly, a triode sputtering apparatus (refer to W.W.Y. Lee and D. Oblas: J. Appl. Phys. Vol. 46, No. 4, 1975 pp 1728-1732) in which, as shown in Fig. 2, a third electrode 3 for emitting electrons is further disposed and (3) the magnetron sputtering process (refer to R.K. Waits: J. Vac. Sci. Technol. Vol. 15, No. 2, 1978, pp 179-187) in which, as shown in Fig. 3, a suitable magnetic field is applied to a target 1 by a magnet 5 to generate high density and low-temperature plasma, thereby forming thin films at a high rate, are known in the technical field of thin film formation. Each of the above-mentioned equipment and process comprises generally a target 1 which is a thin-film forming element, a substrate 2 upon which a thin film is formed, a vacuum chamber 4 in which the target 1 and the substrate 2 are enclosed and gas inlet and outlet systems, whereby plasma is generated in the vacuum chamber 4. In case of forming a thin film at a high rate in each of the above-mentioned apparatus and process, it is essential that the density of plasma must be maintained at a high level. In the case of the diode sputtering apparatus, the higher the density of plasma, the more drastically a voltage applied to the target is increased and concurrently the temperature of the substrate rapidly rises because of the bombardment of high energy particles and high-energy electrons in the plasma thereon. As a result, the damages of the grown thin films are increased, so that the diode sputtering apparatus can be only used with; special heat-resistive substrates, thin film materials and film compositions. In the case of the triode sputtering apparatus, even though the density of the plasma increases by the feeding of electrons from the third electrode, but as in the case of the diode sputtering apparatus, the rapid temperature rise of the substrate results in the case of the formation of a thin film at a higher rate. As a consequence, the triode sputtering apparatus has a defect that only special film-forming materials may be used and the kinds of the substrates to be used are also limited in number. On the other hand, with the high-rate magnetron sputtering apparatus, the gamma (γ-) electrons which are emitted from the target and which are needed to ionize a gas in plasma are confined over the surface of the target by the magnetic and electric field, so that it becomes possible to generate high-rate plasma at a low gas pressure. For instance, the high-speed sputtering process can be carried out at a low pressure as low as 0.132 Pa (10⁻³ Torr) in practice, so that the magnetron sputtering process has been used widely to form various thin films at high rates. However, in this process, the film being formed is subjected to the bombardment of ions (mainly Ar⁺) from the plasma; the high-energy neutral particles (mainly Ar reflected at the surface of the target); and negative ions. Accordingly in almost all the cases, the compositions of the films thus formed are deviated and not only the film but also the substrate are damaged. Furthermore, it is well known in the art that practically in the case of the formation of a ZnO film, the quality of the portion of the ZnO film immediately above the eroded or bombarded portion of the target is considerably different from the quality of the remaining portion. Thus, the magnetron sputtering process presents a problem of the bombardment of high-energy particles over the surface of the substrate. In addition, since the eroded or bombarded portion of the target is locally distributed it has defects that the efficiency of utilization is remarkably low and the productivity is not high in the case of the industrial-scale formation or thin films. Furthermore, in the case of the formation of thin films by the conventional sputtering apparatus, the gas and the particles in plasma are not sufficiently ionized, so that neutral particles which are sputtered and to be deposited on the surface of the substrate are almost neutral when they impinge upon the surface of the substrate. From the standpoint of the reaction, a sufficiently high degree of activation cannot be attained, and therefore in order to obtain an oxide film or films of thermally nonequilibrium materials, the temperature of the substrate must be raised to a high temperature as high as 500 - 800 °C. In addition, almost all the electric power supplied to the plasma is consumed as thermal energy and the ratio of the electric power used to form plasma (ionization) to the whole power applied to the equipment is low, so that there is a defect that the power efficiency is low. Furthermore, with the above-mentioned sputtering apparatus, the stable discharge cannot be maintained at a gas pressure lower than 0.132 Pa (10⁻³ Torr) and accordingly there arises a problem that impurities are trapped in a formed thin film. Meanwhile, Matsuo et al. proposed a method for forming thin films (U.S. Patent No. 4,401,054) by which plasma containing a material to be deposited is generated under electron cyclotron resonance condition and extracting the plasma thus generated toward a specimen; thereby forming a thin film. However, by this method it is impossible to form a thin metal film or metal-compound film. Matsuo and Ono (U. S. Patent No. 4,492,620) and Ono et al. (Jpn, J. Appl. Phys. Vol. 23, No. 8, 1884, L534-L536) disclosed respectively, a microwave plasma deposition apparatus in which a target is sputtered by microwave plasma generated by the electron cyclotron resonance (ECR) and the sputtered particles are deposited on the surface of a substrate, thereby forming a thin film. The microwave plasma has excellent features that the discharge can be produced at a pressure of from 1.32 x 10⁻³ Pa to 1.32 x 10⁻² Pa (10⁻⁵ to 10⁻⁴ Torr) and that the plasma is highly active. This apparatus is superior in that the highly activated plasma is generated at a low gas pressure by utilizing the above-mentioned features of the microwave plasma. However, the target is disposed outside of the plasma generation chamber, so that the sputtering rate is not satisfactorily high and the ratio of ionization of the particles sputtered from the target is low and furthermore the energy control is not satisfactory. Japanese Patent Application Laid-Open Nos. 61-87869 and 61-194174 disclose apparatus in which microwave plasma produced in ECR condition is confined by a mirror field so that the sputtering process can be carried out by the plasma whose density is considerably increased. In both cases, the sputtering process can be carried out at a high vacuum of the order of 1.32 x 10⁻³ to 1.32 x 10⁻² Pa (10⁻⁴ - 10⁻⁵ Torr). However, in the former apparatus, both of the target and the substrate are disposed within high-density plasma. Consequently, there arises a defect that high-energy neutral particles and charged particles directly bombard on the surface of the substrate, so that the quality of the thin film being formed is degraded. Furthermore, there exists an adverse effect that the temperature of the substrate is raised by the high density plasma, so that a cooling mechanism for cooling the surface of the substrate becomes complex in construction. In the latter apparatus, plasma generated in a mirror field is extracted toward the surface of a target by another magnetic field generating means so as to sputter the target. In this case, the target is not disposed in the plasma generation chamber in which high density plasma is generated, so that the ratio of the ionization of the particles sputtered from the target is low. Therefore, the latter apparatus is not adapted to the formation of thin films by highly reactive ions. In the case of the formation of thin films by the sputtering process, it is preferred that the following conditions are satisfied: (1) The film and the substrate are not damaged and their drastic temperature rises must be prevented and the films are formed in a high-rate (In other words, high density plasma must be generated); (2) The energy of the particles can be controlled over a wide range; (3) The dispersion of the energy of the particle must be minimized as practically as possible; (4) The ionization ratio of plasma is high and plasma is active; and (5) Plasma can be generated even at a low gas pressure. In order to satisfy the above-described conditions, the same inventors disclosed in Japanese Patent Application No. 61-66866 a process in which a target is disposed substantially in parallel with the magnetic flux in front of high density plasma generated in a mirror field so that the sputtering process can be carried out at a high degree of efficiency and the ions generated are extracted in the direction of the magnetic field. In this process, the surface of the target is disposed substantially in parallel with the direction of the magnetic flux, so that the ions must be forced to transverse across the magnetic field and impinge on the target when they are extracted toward the target to sputter the same. Therefore, from the standpoint of a plasma generation efficiency, the process must be improved to exhibit a high efficiency. Furthermore, since the surface of the substrate upon which a thin film is formed is disposed perpendicular to the magnetic flux, there still remains a danger that the substrate is subjected to the bombardment of high-energy neutral particles. A known sputtering apparatus of the aforesaid type is also shown in US-A-4610770. According to an aspect of the present invention there is provided a sputtering apparatus for forming thin films, comprising a vacuum chamber having a plasma generation chamber with a central axis and including a gas introduction inlet and a microwave introduction window, said microwave introduction window being connected to a microwave waveguide; a pair of magnetic field generating means disposed around the outer sides of the plasma generation chamber to produce a mirror magnetic field parallel to the central axis of the plasma generating chamber, the direction of microwave introduction through the waveguide being perpendicular to the direction of the magnetic field; the intensity of the magnetic field being such as to satisfy the electron cyclotron resonance condition at any point within the plasma generation chamber; the vacuum chamber having a specimen chamber connected to the plasma generation chamber including means for supporting a specimen substrate; the plasma generation chamber having dimensions sufficient to define a microwave cavity resonator, causing microwave energy introduced therein to resonate; a first target and a second target being positioned at respective ends of the plasma generation chamber with their surfaces perpendicular to the direction of the magnetic field, each target being connectable to a negative electrical potential; and the specimen chamber being connected to the plasma generation chamber between the two opposing targets and perpendicular to the central axis of the plasma generation chamber so that the microwaves are directed towards the specimen substrate whose surface is positioned parallel to the central axis of the plasma generation chamber. Preferably, the magnetic field has a maximum intensity at the position of each of said first and second targets. Preferably, the vaccum waveguide has at least one bend portion and said microwave introduction window is disposed at a postion which cannot be directly viewed from the target. In a preferred embodiment, the plasma generation chamber and the specimen chamber are connected to each other through a slit-like openning formed through the cylindrical wall of the plasma generation chamber. The vacuum waveguide may have at least one bend and said microwave introduction window may be disposed at a position which cannot be directly reviewed from the target. According to another aspect of the present invention, there is provided a method for forming a thin film on a substrate comprising using the apparatus as claimed in the apparatus claims and placing the substrate in the specimen chamber of the sputtering apparatus. The invention will now be described by way example only, with reference to the accompanying drawings in which: Fig. 1 is a schematic sectional view showing a conventional diode sputtering apparatus; Fig. 2 is a schematic sectional view showing a conventional triode sputtering apparatus; Fig. 3 is a schematic sectional view showing a conventional magnetron sputtering apparatus; Figs. 4 and 5 are a sectional view and a partially cutaway view in perspective respectively, showing an embodiment of the thin film forming apparatus according to the present invention; Fig. 6 is a diagram illustrating the magnetic field, the movement of charged particles and the potential distribution in the embodiment shown in Fig. 4; and Fig. 7 is a partial perspective view showing a further embodiment of the thin film forming apparatus according to the present invention. A sectional view, showing a preferred embodiment of the present invention is shown in Fig. 4 and Fig. 5 is a partially cutaway view in perspective thereof. A vacuum chamber 6 comprises a vacuum waveguide 7, a plasma generation chamber 8 and specimen chamber 9 and has a gas inlet port 10 and a gas discharge port 11. Through a microwave introduction window 12, the vacuum chamber 6 is connected to a microwave waveguide 13, a matching means (not shown) a microwave power meter (not shown) and a microwave waveguide introduction mechanism such as an isolator (not shown) and to a microwave power supply (not shown) in the order named, so that the microwave energy is fed into the vacuum chamber 6 through the microwave introduction window 12. In this embodiment, the microwave introduction window 12 is a quartz glass plate and the microwave power supply is a magnetron operating at 2.45 GHz. The plasma generation chamber 8 is water-cooled in order to mitigate temperature increases due to the generation of plasma. In the specimen chamber 9, a substrate holder 15 for supporting a substrate 14 upon which is formed a thin film, is disposed. A shutter 16, which is able to be opened and to be closed, is disposed above the substrate 14 in order to prevent the impingement of sputtered particles on the substrate. A heater is incorporated in the substrate holder 15 so that the substrate 14 is heated. Furthermore, DC or AC voltage can be applied to the substrate 14 and during the thin film formation process, a bias voltage can be applied to the substrate 14 and the sputtering cleaning of the substrate 14 can be accomplished. The plasma generation chamber 8 satisfies the condition of a microwave cavity resonator, for instance, the cylindrical resonance mode TE₁₁₈. More particularly, the plasma generation chamber 8 is in the form of a cylinder of 20 cm in inner diameter and 20 cm in inner height, so that the intensity of the electric field of the microwave is increased, and therefore the efficiency of the microwave discharge is improved. A pair of electrically conductive target holders 17A and 17B which can be cooled by water are disposed at both ends, respectively, of the plasma generation chamber 8, and targets 18A and 18B are securely held in position to the electrically conductive target holders 17A and 17B, respectively, by soldering or by screws. The target holders 17A and 17B are electrically connected to a DC power supply 19 so that a negative voltage up to -1.5 kV and 10 A can be applied to the targets 18A and 18B. The target holders 17A and 17B and the inner wall of the plasma generaiton chamber 8 are electrically isolated from each other by insulating members 20A and 20B. Furthermore, in order to maintain a desired degree of vacuum in the plasma generation chamber 8, O-rings 21A and 21B are inserted between the inner walls of the plasma generation chamber 8 and the target holders 17A and 17B. Electromagnets 22A and 22B are disposed around both end portions, respectively, of the plasma generaiton chamber 8 so that the electromagnetic field is produced in parallel with an imaginary line interconnecting the targets 18A and 18B, in other words parallel with the center axis of the plasma generation chamber 8, and therefore, the intensity of the magnetic field produced by the electromagnets 22A and 22B can be decided to establish the conditions for causing the electron cyclotron resonance by the microwave inside the plasma generation chamber 8. For instance, in the case of the microwave at a frequency of 2.45 GHz, the condition for producing the electron cyclotron resonance is to attain the magnetic flux density of 875 G. Accordingly, the electromagnets 22A and 22B are so designed such that a maximum magnetic flux density of the order of 3000 G can be obtained. When the two electromagnets 22A and 22B are suitably spaced apart from each other the so-called mirror-field is generated. In the mirror-field arrangement the magnetic flux density becomes minimum within the plasma generation chamber 8, and the energy is efficiently imparted to each electron by electron cyclotron resonance, and further the scattering of produced ions and electrons in the direction perpendicular to the magnetic field can be prevented, and the plasma can be confined with the mirror field. Referring next to Fig. 6, the movement of the charged particles in this embodiment will be described. Same reference numerals are used to designate similar parts in both of Figs. 4 and 6. Here, in case of producing a plasma, the parameters are a gas pressure in the plasma generation chamber, the power of the microwave, a voltage applied to targets, a gradient of mirror field (that is the ratio between the maximum magnetic flux density of Bm at electromagnet portions and the minimum magnetic density Bo at the center between the electromagnets 22A and 22B in the plasma generation chamber 8: Bm/Bo), and the distance between the electromagnets 22A and 22B. For instance, in the case of the microwave at a frequency of 2.45 GHz, the minimum magnetic flux density Bo within the plasma generation chamber 8 must be maintained a suitable level less than 875 G while the maximum magnetic flux density Bm must be varied from 1 kG to 3 kG, so that the magnetic flux density 875 G required for producing the electron cyclotron resonance at any point in the plasma generation chamber 8 can be attained. When the magnetic field is varied gradually in the space as described above, the charged particles in the plasma are confined by the lines of magnetic force 23 to make the spiral movement around the lines of the magnetic force and to be reflected at a portion having a high magnetic flux density while maintaining their angular momentum. As a result, they are forced to reciprocate in the mirror field and confined. In this case, the above-mentioned gradient Bm/Bo of the mirror field plays a very important role in confining the plasma. When a negative voltage (Va) is applied to the targets which are disposed so as to face the high density plasma thus confined, the ions in the high density plasma are efficiently extracted toward the targets 18A and 18B, causing sputtering. In this case, the energy imparted to the targets 18A and 18B is one corresponding to the difference between the plasma potential (Vp) and the voltage (Va) applied to the targets 18A and 18B. Furthermore, a portion of particles which are sputtered from the targets 18A and 18B and which are almost neutral are ionized in the high density plasma with a high electron temperature. Meanwhile, the electrons are confined in the magnetic field due to the mirror field and are reflected toward the center of the plasma due to the negative potential applied to the targets 18A and 18B disposed at both ends of the mirror, so that the confinement of the high-energy electrons can be realized by the effect of both the electric and magnetic fields, and therefore, the neutral gas atoms and molecules can be ionized at a higher degree of efficiency. Furthermore, the atoms or molecules sputtered from the target material and ionized in the plasma, lose their kinetic energy in the process of reciprocal motion in the plasma and finally diffuse out to the outside of the plasma by traversing the lines of the magnetic force. Neutral particles also diffuse out. The ions or neutral particles thus diffused are deposited on the surface of the substrate, thus forming a thin film. This means that the ionization in the plasma is carried out at a higher energy level (in a highly active mode) and when the ions thus ionized are extracted from the plasma to form a thin film, the ions can be extracted with an energy level less than a fraction of the ionization energy, and indicates that the sputtering apparatus with the above-mentioned magnetic field distribution has the most preferable properties used as the thin film forming apparatus. Furthermore, since the targets and the substrate are disposed perpendicular to each other, the substrate is not subjected to the bombardment of the negative ions and the high-energy neutral particles sputtered from the targets, so that the bombardment of the substrate by various high-energy particles which presents the problem in the conventional sputtering technique can be suppressed. When an electrically conductive thin film is formed by sputtering an electrically conductive material such as a metal, if the microwave introduction window is dimmed by the adhesion of the particles sputtered from the targets, the microwave is caused to reflect so that plasma cannot be maintained stably for a long period of time. In the present invention, even though the ions and neutral particles diffused out to the outside of the plasma have low energy levels, it is preferable that the microwave introduction window is spaced apart from the plasma in order to ensure the stable operation. Especially as shown in Figs. 4 and 5, it is preferable that the vacuum waveguide 7 is bent so that the microwave introduction window 12 is located at the position which cannot be viewed directly from the targets 18A and 18B; that is, the position at which the particles flying straight from the targets 18A and 18B will not adhere the window because the particles inevitably impinge on one or more obstacles before they reach the microwave introduction window 12. Furthermore, according to the present invention, the plasma is activated, so that it has the features that the discharge can be maintained in a stable state at lower gas pressures (1.32 x 10⁻³ Pa (10⁻⁵ Torr)) and that a thin film containing less impurities can be formed. Furthermore, the present invention utilizes heating due to the electron cyclotron resonance, the electron temperature in the plasma can be freely controlled. As a result, a high electron temperature sufficient to produce highly charged ions can be attained. Therefore, the present invention has an excellent feature that chemically unstable materials can be synthesized by using the highly charged ions thus produced. In addition, according to the thin film forming apparatus of the present invention, the ionization ratio of plasma is extremely high as described above so that the sputtered neutral particles emitted from the targets are ionized at a high rate in the plasma. Furthermore, the ionized particles, which had constituted the targets, are accelerated due to the potential applied to the targets, thereby increasing the so-called self-sputtering ratio, that is, the ratio of the sputtered particles further sputter the targets. That is, when a plasma generation gas (for instance, Ar) is extremely thin or even when no gas is used, the above-mentioned self-sputtering process continues, so that the present invention has a further feature that it becomes possible to form a thin film having a high degree of purity. Next, the results of the formation of Al₂O₃ films by utilizing the apparatus of the present invention will be described. Metallic aluminum (Al) was used as targets and the specimen chamber 9 was evacuated at 6.60 x 10⁻⁵ Pa (5 x 10⁻⁷ Torr). Thereafter, argon gas and oxygen gas (the partial pressure ratio was 1 : 1) were introuduced until the gas pressure in the plasma generation chamber rises to 3.96 x 10⁻² Pa (3 x 10⁻⁴ Torr). Next, a thin film was formed under the conditions that the microwave power was controlled between 100 and 800 W; the voltage applied to the targets were varied between -300 - -1 kV; and the gradient of the mirror field was maintained at 2 kG/700 G. Under these conditions, the magnetic flux density 875 G required for causing the resonance was attained in the center portion of the plasma generation chamber. The length of this portion in the direction of targets is 3 cm. The sputtering process was started while the specimen holder was not heated. The deposition rate was increased with the increase of the microwave power and the voltage applied to the targets. For instance, when the microwave power was 500 W and the voltage applied to the targets was -500 V, the deposition rate was 80 nm/min. When the microwave power and the voltage applied to the targets were varied in the above-mentioned ranges, thin films were formed efficiently at the deposition rates from 10 to 100 nm/min. As compared with the thin films formed by the conventional sputtering processes, the internal stresses in the films were low, so that the films 2 µm or more in thickness were formed in a stable manner without causing cracks and exfoliation. In these cases, the temperatures of the substrates were about 200°C and it was possible to form a thin film over a polymer film at a high deposition rate. In this case, the average energy of the ions varied from 5 eV to 25 eV, and 10 to 30% of the particles travelled toward the substrates were ions. The thin film forming apparatus in accordance with the present invention can be used to form not only Al₂O₃ but also other various thin films. Fig. 7 is a partial view of a further embodiment of a thin film forming apparatus in accordance with the present invention. This embodiment, especially, adapted for continuously forming a thin film over the surface of a tape-like substrate. In Fig. 7 the positional relationship among the plasma generation chamber 8, the targets 18A and 18B and a tape-like substrate 24 are shown. The microwave introduction mechanism and the generation or a mirror magnetic field are substantially similar to those described above with reference to Fig. 4 showing the first embodiment of the present invention. The tape-like substrate 24 is fed from a feed bobbin 25 and then taken up by a take-up bobbin 26. Both the feed and take-up bobbins 25 and 26 are disposed within the specimen chamber 9 and are driven by a driving system including, for instance, a motor (not shown). At substantially intermediate portion between the targets 18A and 18B a slit-like opening 27 is formed through the cylindrical wall of the plasma generation chamber 8. Within the plasma generation chamber 8, the mode of plasma generation is uniformly around the circumference of a circle indicated by the broken line A which is in parallel with the targets 18A and 18B. It follows therefore that when the tape-like substrate 24 is arranged along the circumference of the circle A, a thin film is formed under the same conditions. Therefore, the slit-like opening 27 of 10 mm in width and 1/3 of the circumference in length is formed through the wall of the cylindrical wall of the plasma generation chamber 8 at a position corresponding to the midpoint between the opposing targets 18A and 18B. This slit-like opening 27 leads to specimen chamber 9. In the specimen chamber, the feed bobbin 25 and the take-up bobbin 26 are arranged in such a way that the tape-like substrate 24 is transported along this slit-like opening 27. Under these conditions, the tape-like substrate 24 was transported and a thin metal film was formed on the surface of the moving tape-like substrate 24. The targets were composed of various metals such as aluminum, copper and so on. After the specimen chamber 9 was evacuated at 6.60 x 10⁻⁵ Pa (5 x 10⁻⁷ Torr), Ar gas was introduced until the gas pressure in the plasma generation chamber 8 became at 3.96 x 10⁻² Pa (3 x 10⁻⁴ Torr). A thin film was formed under the conditions that the microwave power was 100 - 800 W; the voltage applied to the targets was between -300 and -1 kV and the gradient of the mirror field was maintained at 2 kG/700 G. Thus, metal films uniform in thickness were formed across the width of 12 mm of the tape-like substrate 21. In both embodiments described above, the magnetic coils are used to generate a mirror field, but it is apparent to those skilled in the art that a mirror field can be produced by using various permanent magnets or any suitable combination thereof. Furthermore, it is also apparent that the gradient of a mirror field can be made asymmetrical. As described above, according to the present invention, plasma is produced by the discharge of a microwave with the condition of the electron cyclotron resonance and it is confined by a mirror field at a high degree of efficiency. The targets are so disposed that the magnetic flux by mirror field is perpendicular to the target. Therefore, the ions in the high-density plasma can be extracted toward the targets at a high degree of efficiency, thereby carrying out the sputtering process. According to the apparatus of the present invention, highly activated plasma can be produced at a low gas pressure. As compared with the conventional sputtering apparatus, a thin film can be formed at a low gas pressure at a high deposition rate by the particles having an extremely high ionization ratio. Furthermore, the energy of the particles can be controlled freely in a wide range between a few electron volts and hundreds electron volts (eV) and the dispersion of the energy is reduced to a minimum. With the thin-film forming apparatus in accordance with the present invention, not only it becomes possible to form a high-quality film having a high degree of purity and extremely less damages at a high deposition rate in the condition of low substrate temperature and a higher degree of efficiency, but also it becomes possible to form a thin film of a nonequilibrium material at a low temperature and in a highly stable manner which has not be hitherto obtained by the conventional apparatus. Furthermore, in the thin film forming apparatus in accordance with the present invention, there exists an equivalent position along the circumference of the cylindrical plasma generation chamber, so that when a slit-like opening can be formed along this position, it becomes possible to continuously form a thin film on the surface of a tape-like substrate.

Claims: A sputtering apparatus for forming thin films, comprising: a vacuum chamber having a plasma generation chamber (8) with a central axis and including a gas introduction inlet (10) and a microwave introduction window (12), said microwave introduction window (12) being connected to a microwave waveguide; and a first target (18A) positioned at one end of said plasma generation chamber, said target being connectable to a negative electric potential; a pair of magnetic field generating means (22A, 22B) disposed around the outer sides of the plasma generation chamber (8) to produce a mirror magnetic field parallel to the central axis of the plasma generating chamber and perpendicular to the surface of the target (18A), the direction of microwave introduction through the waveguide (7) being perpendicular to the direction of the magnetic field; and the intensity of the magnetic field being such as to satisfy the electron cyclotron resonance condition at any point within the plasma generation chamber (8) characterised in that: the vacuum chamber has a specimen chamber (9) connected to the plasma generation chamber (8) including means (15) for supporting a specimen substrate (14); the plasma generation chamber (8) has dimensions sufficient to define a microwave cavity resonator, causing microwave energy introduced therein to resonate; a second target (18B) is positioned at the opposite end of the plasma generation chamber (8) perpendicular to the direction of the magnetic field, said second target (18B) being connectable to a negative electrical potential; and the specimen chamber (9) is connected to the plasma generation chamber (8) between the two opposing targets (18A,18B) and perpendicular to the central axis of the plasma generation chamber (8) so that the microwaves are directed towards the specimen substrate (14) whose surface is positioned parallel to the central axis of the plasma generation chamber (8). Apparatus according to claim 1, wherein the magnetic field has a maximum intensity at the position of said first and second targets (18A, 18B). Apparatus according to claim 1 or claim 2, wherein said vacuum waveguide has at least one bend portion and said microwave introduction window is disposed at a position which cannot be directly viewed from said targets. Apparatus according to any preceding claim, wherein said plasma generation chamber has a cylindrical wall and said plasma generation chamber and said specimen chamber are connected to each other through a slit-like opening formed through the cylindrical wall of said plasma generation chamber. A method of forming a thin film on a substrate which comprises placing the substrate in the specimen chamber of the apparatus as claimed in any of claims 1 to 4, and using the apparatus to form the thin film on the specimen via a plasma confined by a mirror magnetic field under electron cyclotron resonance conditions.

Inventors: MATSUOKA MORITO, ONO KEN ICHI, MATSUOKA, MORITO, ONO, KEN'ICHI
Applicants: NIPPON TELEGRAPH & TELEPHONE, NIPPON TELEGRAPH AND TELEPHONE CORPORATION
Application year: 1987
Main classification: C23C14
IPC codes: H01L21, C23C14, H01J37, H05H1