HEAT SHRINKABLE CYLINDRICAL LAMINATED FILM

Abstract: A heat shrinkable cylindrical laminated film having a polyvinylidene chloride type resin (I) as an oxygen gas barrier core layer, on the both surface side of which 1 or 2 resin layers are arranged respectively and consisting of 3-5 layers with total, characterized in that the cylindrical exterior surface resin layer on said layer (I) comprises a crosslinked polyolefin type resin layer (II) having a gel fraction [x] at the outermost layer of 25-70 % by weight, a gel fraction [y] at the surface layer in the side of the layer (I) of 40 % by weight or less and a gradient of gel fraction represented by [y/x] of 0.6 or less and the joint of said layers (I) and (II) comprises a laminate of a joint in a state denaturated by electron rays.

Description: DESCRIPTION A HEAT SHRINKABLE CYLINDRICAL LAMINATED FILM TECHNICAL FIELD This invention relates to an improvement of cylindrical laminated films which are used for heat shrinking packages of irregularly shaped fatty food as contents such as raw meat, processed meat or the like. BACKGROUND ART Heat shrinkable cylindrically laminated films comprising 3 - 5 layers, one of which is a polyvinylidene chloride type resift (hereinafter referred to as PVDC) as an oxygen gas barrier layer and having a total thickness of 40 -80 μ are well known in the art. Typical laminated films which are currently commercially available include, for example, a laminated cylindrical film comprising 3 layers of an ethylene-vinyl acetate copolymer resin (hereinafter referred to as EVA) at the exterior side of the cylinder/a PVDC/a cross-linked EVA at the interior side of the cylinder according to Japanese Patent Application Publication No. 43024/83 (US Patent No. 3,741,253); a laminated cylindrical film comprising 3 - 5 layers of a specific polyolefin resin blend at the exterior side of the cylinder/a PVDC/a specific poly¬ olefin resin blend at the interior side of the cylinder according to Japanese Patent Application Publication No. 40988/85 (US Patent No. 4,390,587); and a laminated cylindrical film comprising 4 - 5 layers of an EVA/a PVDC/an ionomer resin at the interior side of the cylinder according to Japanese Patent Application Publication No. 2192/80 (US Patent No. 4,161 ,562). These laminated cylindrical film have occupied the market share as the packaging materials used for packaging in tight irregularly shaped fatty foods as contents by heat shrinking by proposing as the sales point their unique advantages such as excellent appearance owing to their transparency, their heat shrinkability at low tempera¬ ture which will not damage the freshness of contents, excellent handling and working properties and the like. However, with " the proceeding of the improvement of packaging efficiency by the introduction of high speed packaging technique using a rotary chamber vacuum packaging machine, new problems of quality have happened in the packaging field, which problems are those of quality of design and cannot be solved with the aforementioned packag- ing materials. In other words, as the result of research of the present inventors, the applicability of the high speed packaging technique may be decided by the following three points? first of all, possibility of making a certain sealed part having oil resistance while shorten¬ ing the time required for tight sealing of packing bags filled with contents under reduced pressure; secondly, securing the cruel treatment resistance of the films so as to resisting rough handling of packaged articles accompanied with the increase of packaging speed under severe conditions; and third, enhancement of oil resistance of interior and exterior layers, in particular, on the treatment at high temperature. In addition, these new quality requirements must be satisfied without damaging the conventional quality level and is also in a high level. ' Specifically, referring to the cruel treatment resistance as an index of causing no failures such as pin hole or break of bag on handling of a package, require¬ ment level has been raised and a commercially available film comprising EVA/PVDC/σrosslinked EVA which has been evaluated to have a toughness to ensure that the film can be used for direct- packaging of meat with sharp bone at the initial application (see the effect of Japanese Patent Application Publication No. 43024/83) is now evaluated in the new market requirements to be insuf¬ ficient in toughness owing to high incidence of failures such as pin hole or break of a sealed part during handl- ing the film even if the content is changed to meat without bone so that sharp extrusion will not be detected in it on touching with hand. However, these films are not easily modified or improved. The reason depends on that a PVDC layer as a core layer will be yellowed or deteriorated upon irradiation of electron rays and thus it is difficult to carry out crosslinking in a state of a laminate, which - makes it impossible to employ coextrusion technique ' excellent in interlaminar strength. Furthermore, it is very difficult to form a cylindrical ' coextrusion laminate using the PVDC layer and finally to make a laminated film the exterior surface side of which is crosslinked. There has also been proposed a non-crosslinked resin obtained by the examination of resin species to be used and its laminate construction, but the counterproposal is inferior in effect to that of using a crosslinked layer which improves both film forming property by drawing and film property itself. Accordingly, a laminated film containing as a modifying layer a polyolefin type resin layer having a sufficient degree of crosslinking must be prepared by the method such as described in Fig. 1 of US Patent No. 3,741,253, in which a cylindrical EVA layer is extruded and crosslinked with radiation, a PVDC layer and an EVA layer are cylindrically extruded sequentially on the EVA layer, and these layers are melt-extruded from a coating die in the outside of the die to form a directly adhered laminate each other, which is drawn by an inflation method to form a cylindrical laminated film. This method has disadvantages that it is not economical as it requires technique of a high order and that the crosslinked layer of the film obtained will be an inner¬ most layer of the cylindrical film. As disclosed in Japanese Patent Application Kokai (Laid-Open) No. 23752/87 (by virtue of a right of priority based on US Patent Application No. 735,082/85) , the method of irradiating electron rays over the whole layers of a laminated film which has been prepared by σoextrusion and drawing may be appreciated in the point that an e ' ffeσt of crosslinking-drawing is abandoned and both the modificating effect of crosslinking on the polyolefin type resin and the improving effect on the bonding between the polyolefin type resin and the PVDC layer are utilized. But the method has disadvantages that the PVDC layer is inevitably deteriorated by the irradiation of electron rays (lowering of oxygen gas barrier properties) and that the effect of crosslinking- drawing to be abandoned is very large. Further, it has been confirmed that in the laminated film obtained by irradiating the whole layers typified by the films disclosed in Japanese Patent Application Kokai (Laid- Open) No. 143086/76 (US Patent No. 4,044,187) and US Patent No. 3,821,182 the PVDC layer is deteriorated drastically (see Tables 4 and 5) . DISCLOSURE OF INVENTION The object of this invention from this view- point is to provide a cylindrical laminated film which satisfies the aforementioned new required quality, that is to say, the film in which most of the evaluation items listed in Table 11 is maintained in high levels, characterized in that the yellowing or deterioration of the core layer of a cylindrical laminated film which has a PVDC layer as the core layer and is obtained by coextrusion is minimized to form a laminated film in which the exterior side of the cylinder is modified by crosslinking and the layer construction is adjusted to the optimal. In other words, the object of this inven¬ tion is to provide a heat shrinkable cylindrical laminated film having a polyvinylidene chloride type resin (I) as a gas-impermeable (i.e. oxygen barrier) core layer, on the both surface sides of which 1 or 2 resin layers are arranged respectively and consisting of 3 - 5 layers with total, characterized in that the cylindrical exterior surface resin layer on said layer (I) comprises a crosslinked polyolefin type resin layer (II) having a gel fraction [x] at the outermost layer of 25 - 70% by weight, a gel fraction [y] at the surface layer in the side of the layer (I) of 40% by weight or less an β a gradient of gel fraction represented by [y/x] of 0.6 or less and the joint of said layers (I) and (II) comprises a laminate of a joint in a state denaturated by electron rays. BRIEF EXPLANATION OF THE DRAWINGS Figs. 1, 2, 3-A, 3-B and 4 are respectively graphs illustrating the experimental results referring to doses of electron rays; Fig. 5 is a schematic chart illustrating a manufacturing process of the film of this invention; Figs. 6, 8 and 9 are respectively graphs illustrating the experimental results referring to the effects of irradiation of electron rays; and Fig. 7 is an analytical diagram illustrating the components of the sealable resin layer in the film of this invention. r BEST MODE FOR CARRYING OUT THE INVENTION This invention is now described in detail •referring to the drawings and the tables. First of all, this invention is explained from the aspect of the process for preparing the laminated film of this inven¬ tion as a new laminated film, whereby the source of its novelty will be understood more readily. The process for preparing the laminated film of this invention typically inclμdes the crosslinking- drawing method by (i) forming a cylindrical laminate by a σoextrusion w method, (ii) irradiating electron rays for the exterior surface of the cylindrical laminate, and then (iii) drawing the irradiated laminate to utilize the crosslinking-drawing effect. The process is character¬ ized in that the electron rays are irradiated into the layer (II) at the exterior surface side of the cylinder so as to afford crosslinking (gel fraction) gradient and thus to subject sufficient crosslinking to the layer (II) , while denaturation by electron rays is caused also at the joint area of the layer (II) and the core layer (I) but the radiation has been attenuated to give a small exposed dose to the core layer (I) . The reason is illustrated in Fig. 9 (corre¬ sponding to Experimental Example 1) and in Fig. 8 (corre- sponding to Experimental Example 7) . That is to say, Fig. 9 is a conceptional curves illustrating the relation¬ ship between the exposed dose of electron rays to the film and the (positive or negative) effect afforded by the irradiation (crosslinking) , in which the axis of abscissa represents the exposed dose (Mrad) at the surface of the film and the axis of ordinate represents the non-defective ratio of the film group. In these curves, plotting by the triangle mark O indicates the factor which illustrates the degree of deterioration of the PVDC layer and is represented by the level of non- defective barrier ratio of the film group upon repeated flexing with twisting, and the plotting by the circle mark indicates the factor which illustrates the degree of toughness of the crosslinked-drawn film and is represented by the level of non-defective ratio of the film having a high temperature resistance on sealing of the film. The empty marks indicate the case carried out according to the process of this invention and the black- painted marks indicate the case carried out according to a conventional process (total layer irradiation) . From the result illustrated in Fig. 9, it can be understood that in- the conventional (blank-painted) process the crosslinking effect rapidly increases from about 4 Mrad and reaches the maximum level at about 6 Mrad, but the deterioration of PVDC increases markedly from about 2 Mrad and the half of the PVDC will exhibit defectiveness in oxygen gas barrier property even at an exposed dose of about 3 Mrad in which the aforementioned crosslinking effect does not appear, so that it is impossible to select any appropriate range of exposed dose in which irradiation (crosslinking) effect can be taken without the deterioration of the PVDC layer. On the other hand, Fig. 9 indicates that according to the process of this invention (plotting with empty marks) , development of the crosslinking effect remains at a low level and exposed dose of about 7 - 10 Mrad is required for obtaining the crosslinking effect at a maximum level, but the deterioration of the PVDC at the same dose level is also reduced remarkably, so that it is possible to select an appropriate range of exposed dose for remaining the deterioration of the PVDC layer at a , minimum level while maintaining the crosslinking effect at a high level. Fig. 8 is a graph obtained from experiments for illustrating the improvement of adhesion strength between the core layer and the adjacent layers to the exposed dose. Plotting by empty circles O represents the result obtained by the process of this invention and plotting by black-painted circles © represents the result obtained by the conventional process (i.e. the process for adhering the adjacent layers immediately after irradiation) . To be noted amongst the results of Fig. 8 is the phenomenon of increasing the difference of effects between both curves accompanied with the increase of the exposed dose. In other words, even if the difference of the adhesion strength inherently present between both curves (as compared with each other at the exposed dose of 0 Mrad) be the one generated by the difference of the melt-extruded coating method (a layer is melt-extruded from a coating die onto a tube and directly adhered to a tube in the outside of a die; hereinafter referred to as melt-extruded coating method) and the co-extrusion method as is generally recognized, it can be considered that the increase of the adhesion strength at the neighborhood of the exposed dose of 7 - 10 Mrad is one of the great effects brought about by the process of this invention which makes it possible to apply the exposed dose of 7 - 10 Mrad without the deterioration of the PVDC layer. The improvement of adhesion strength between layers is presumably attributed to the crosslinking generated between layers in some degree. Accordingly, probability of the crosslinking reaction will be increased in propor¬ tion to the exposed * dose passing through the interface of the layers. Therefore, if the irradiation of electron rays onto the layers which have been tightly bonded to each other and the adhesion of layers after the irradi¬ ation are compared, the probability of crosslinking between the adhesion part will be apparently larger in the former than in the latter. _ The difference of the two curves in Fig. 8 should be noted as an index of the aforementioned phenomenon. The phenomena illustrated in Figs. 8 and 9 is the ones which have successfully been utilized for the first time by the process of this invention. Therefore, the laminated film prepared according to the process of this invention is a cylindrical laminated film having a variety of properties that the exterior layer side of the r cylindrical laminated film is first of all modified by crosslinking and the degree of the crosslinking (exposed dose) is sufficient to carry out the modification by crosslinking-drawing of not only the exterior layer itself but also the other layers which will be modified together with drawing of the exterior layer, while most part of the PVDC layer as the core layer is not deterio¬ rated to ensure that the oxygen gas barrier property after flexing with twisting is maintained and the PVDC layer and the exterior layer are bonded satisfactorily. Figs. 8 and 9 also illustrate the aforementioned facts. Next, this invention will be explained refer¬ ring to the prevention of the deterioration of the PVDC layer as the core layer in spite of the irradiation of electron rays onto the exterior layer of the cylindrical laminated film of this invention. Fig. 1 (corresponding to Experimental Example 2) is an experimental graphs of dosage distribution of an electron rays irradiation apparatus, and the axis of ordinate represents dose (%) and the axis of abscissa represents the penetrating depth of electron rays -(μ) . The solid line represents the result with the apparatus used in this invention, the broken line 1 represents the result with a conventional scanning electron rays irradiation apparatus having an acceleration voltage of a high voltage and the broken line 2 represents the result by adjusting the broken line 1 to a maximum. As apparent from Fig. 1, the irradiation apparatus used in this invention is modified in many points of irradiation method, titanium foil, its cooling method and the like to ensure that electron rays will not penetrate a deep point of the film. Fig. 2 (corresponding to Experimental Example 2) represents a schematic diagram for illustrating the application method of dosage distribution of the solid line in Fig. 1, in which the axis of ordinate represents the exposed dose of electron rays (Mrad) and the axis of abscissa represents the enlarged thickness in a sectional direction of a film. That is, the figure represents structural conception of the zone A as the surface layer of a polyolefin type resin layer (II) , the zone 3 as the PVDC layer (I) and the zone C as a part of the adhesive shrinkable resin layer (III) , respectively. Seven curves 0/ 0/ ©( © @r 0 and (f) in Fig. 2 represent the results obtained by the irradiation of electron rays having a variety of dosage distribution in relation with the aforementioned film thickness. The curves (m) , (b) and (c) illustrate the results obtaine by using the film of this invention, and the curves (a), (cT) , (e) and (f) illustrate the results obtained by using a referential article. In other words, the dosage distribution in the film of this invention may be illustrated by the curves which are attenuated obliquely within the surface layer and the terminal parts of the curves pass across the adhesion part of the surface layer and the core layer and penetrate the PVDC layer. However, in the case illust- rated in Fig. 2, the terminal parts presumably remain in substantially central part of the PVDC layer and will not reach the adhesive shrinkable resin layer. Accordingly, it can be considered that the dosage accepted by the surface layer of the laminated film of this invention is sufficient to improve the drawing sate of the polyolefin type resin and also sufficient even at its adhesion part with the PVDC layer to improve the adhesion strength of the two layers, while the PVDC layer will accept the dosage as low as one third of ςhat in the surface layer and thus the deterioration of the PVDC layer is controlled to the minimum. This is to say, this invention is accomplished by conducting researches about the relationship of the dosage level and the distribution profile of the dosage in the direction of the thickness so as to satisfy the required quality of the film from the standpoint of advantages and disadvantages of the polyolefin type resin layer and the PVDC layer. Figs. 3-A and 3-B (corresponding to Ξxperi- mental Example 4) are experimental diagrams illustrated in the same manner as in Fig. 2. In these figures, dosage distribution of a crosslinked film by the irradi¬ ation of electron rays which film has hitherto been proposed as the prior invention, in which the films obtained in the case of dosages of (a - (J) are compara¬ tive products corresponding to those of this invention. In addition, the results of evaluation of the films illustrated in Figs. 2, 3-A and 3-B are listed in Tables 2 and 5 to confirm the excellent properties of the film of this invention. Fig. 4 (corresponding to Experimental Example 5) is a schematic diagram illustrating this invention which is created to adjust the contradictory requirements that the deterioration of film formability accompanied with excessive crosslinking should be avoided and that the degree of crosslinking of the whole layers should be maintained in a high level, in which the axis of abscissa represents thickness of the film and the axis of ordinate is the degree of crosslinking (gel fraction) . Fig. 4 illustrates the effect of a crosslinked polyolefin type resin layer which comprises the lamina¬ tion of two polyolefin type resins having different crosslinking efficiencies, one of which resins having a lower crosslinking efficiency is used as an exterior surface. In this case, the broken line illustrated in the left upper part of the figure represents the crosslinking profile of the polyolefin type resin layer comprising only one resin layer having a moderate crosslinking efficiency, which profile exceeds the limitation for easy film formation by drawing (partial gel fraction of 70% by weight) and enters into the region of defective film formation. But if an outermost layer having a lower crosslinking efficiency (i.e., having a lower gel fraction at the same dosage as above) is further laminated on the polyolefin type resin, the crosslinking profile does not enter into the region of defective film formation as is illustrated by the solid line. In this case of the crosslinking profile illust- rated by solid line an internal surface layer having a higher crosslinking efficiency (i.e., having a higher gel fraction at the same dosage as above) is further arranged to ensure that the whole degree of crosslinking of the crosslinked polyolefin type resin layer will be substan¬ tially in the same level as of the resin layer having a moderate degree of crosslinking. The laminated film of this invention is a novel film which has been accomplished on the basis of inform¬ ation of the irradiation method of electron rays and the layer construction which are illustrated in Figs. 1 -4 and Tables 1 and 2. The usefulness of the film will be explained with reference to the features of the production process of the film of this invention and the films of this invention prepared according to the features, that is, the scope of claims of this invention. Fig. 5 is a schematic diagram of production process of the film of this invention. Referring to the production example of the film of this invention, respective layer constructing resins having been molten in three or four extruders 1, 2 and 3 (and/or 3') are introduced into a circular die 4 to form a laminate and coextruded as a laminated cylindrical parison 5. The cylindrical product 5 is rapidly cooled sufficiently with a cooling apparatus 6, folded into a plain plate with pinch rolls 7 and introduced into electron beam irradiation chamber 8. Numerical marks 9, 9' and 9" represent a group of guide rolls. Within the irradiation apparatus 8 protected with lead plates 10 or the like, the surface side of said parison plate 13 is directly irradiated with electron rays generated from the electron beam irradiation apparatus 11 through a titanium foil 12. The parison 13 is turned around with a turning «roll 14 so that the traveling position will be changed on going and coming and both the surface and back of the parison will be continuously crosslinked by irradiation of electron rays. The crosslinked parison 15 is introduced into a heating bath 17 by the group of guide rolls 16 - 16"", heated to a temperature of about 60 - 98°C with a heat transfer medium 18, subjected to inflation biaxial orientation accompanied with cooling with a air blast cooling ring 22 at a position between a group of pinch rolls 19 and 20, flexed into a flat film by a deflator 21 and batched on as a flat cylindrical film 24 to a rolling axis 23. During a series of this production process, it is basically distinguished from the conventional process (e.g., a process disclosed in US Patent No. 3,741,253) that the laminated cylindrical product having the PVDC layer as a core layer and formed by co-extrusion is directly irradiated with electron rays from not the interior but the exterior surface of the cylinder to obtain a cylindrical laminated film, the exterior surface of which has been crosslinked. Accordingly, it is a main claim that the subject matter of this invention is intended to express the process of denaturation by crosslinking which is distinguished from the conventional technique in the points that in the form of a laminated film without having been crosslinked prior to lamination effect of modification by crosslinking (denaturation) is utilized, while the deterioration of the PVDC layer is reduced to the minimum, by the degree of denaturation by crosslink¬ ing (gel fraction) [y] at the surface layer part of the crosslinked polyolefin type layer (II) in the core layer (I) side, the degree of the denaturation by crosslinking (gel fraction) [x] at the exterior surface layer part of the same resin layer and the-gradient of the gel fraction [y/x] . The aforementioned relationship is listed in Table 2 corresponding to Experimental Example 2 and in Table 14 corresponding to Experimental Example 5. However, as a general principle, said [y] having a value exceeding 40% by weight is excluded from the object of the experiment in this invention. The reason is that even if the gradient of the gel fraction [y/x] may be changed, the PVDC layer of the core layer is deteriorated too much to match the object of this invention. Such a phenomenon can be inferred, for example, from respective curves in Fig. 2. Accordingly, said [y] should be a little value of 40% by weight or less, but it does not include the gel fraction of less than 0.5% by weight and having substantially no difference with that of un- crosslinked article. In order to increase adhesion force between the surfaces of said layer (II) and the (I) , it is important to carry out denaturation by electron rays (which will be recognized, for example, by the improve¬ ment of adhesive strength) while maintaining the surfaces in contact- in tight to each other, and thus said [y] will not be 0.5% by weight or less. As apparent from Tables 2 and 14 under such conditions, if the value of [x] exceeds 70% by weight, film formability by drawing is damaged. If the value is less than 25% by weight, heat resistance of the film is not satisfactory. In addition, even if [y] is 40% by weight or less and [x] is in the range of 70 - 25% by weight, the PVDC layer will be extensively denaturated on the gradient represented by [y/x] being larger than 0.6. From the results of No. 141 in Table 14, practical availability of the film on the gradient of 0.6 is proved. When the crosslinked polyolefin type resin layer (II) has an average gel fraction in the range of 20 - 60% by weight and a ratio of layer thickness in the proportion of 25 - 65% to the total film thickness, preferred degree of crosslinking for exhibiting the crosslinking effect is typified by the results listed in Table 6-A (corresponding to Example, Comparative Example 1) . That is to say, as the advantage of crosslink¬ ing of the polyolefin type resin layer (II) , first of all, drawing ability of itself is improved and then properties relating to toughness such as heat resistance, oil resistance, falling bag resistance at lower tempera¬ ture and the like will be improved. The enhancement of the drawing ability controls the film formability of the whole laminated film. Thus, the sealing resin layer (IV) and the PVDC layer (II) which will not be uniformly drawn with ease are oriented in high degree and uniformly, and high heat shrinkability and mechanical properties are given to the whole laminated film. The relationship of sample Nos. 1 - 9 in Table 6- indicates that in order to improve the properties mentioned above the average gel fraction is preferably in the range of 20 - 60% by weight and the ratio of the thickness as a layer is preferably in a proportion of 25 -65% of the total thickness of the film. In this case, electron rays directly irradiated from the surface side of the laminated film often makes the exterior surface layer of the crosslinked polyolefin type resin layer (II) in an excessive gel fraction to damage the film formability by drawing. It is not easy to increase only the film formability by drawing without decreasing the gel fraction of the whole layer (II) . As a countermeasure against the problem, there is proposed a method utilizing a phenomenon illustrated in Fig. 4, in which the aforementioned layer (II) has a double layer structure constructed from two resin layers, the crosslinking efficiencies of which are different from each other, and one of the resin layers having an lower crosslinking efficiency is arranged as the outermost layer. As another embodiment, the cylindrical film of this invention is a film having excellent interior sealability and high heat shrinkability. Thus, a useful layer construction in the cylindrical interior side is required. The adhesive shrihkable resin layer (III) has a role for adhering the sealing resin layer (IV) and the core layer (I) in tight and for controlling the heat shrinkability of the whole laminated film, particularly heat shrinkability at low temperature in cooperation with the crosslinked layer at the surface side. EVA is generally used in order to carry out the role. It is preferred to use an EVA having a vinyl acetate content in the range of 13 - 20% by weight as the adhesive shrink- able resin layer (III) , which is apparent from the relationship between the vinyl acetate content and adhesion strength as illustrated with the curve plotted with empty circles O in Fig. 6. A further embodiment is the employment of a preferred resin species as the surface layer of the aforementioned sealing resin layer (IV) . This selection of the species will lead to another remarkable effect exhibited by the film of this invention, and thus the selection of the resin species therefore is explained in detail below. The remarkable effect exhibited by the film of this invention is an effect for improving the sealing performance which is exhibited by the combination of a surface crosslinking resin layer and a sealing resin layer. Specifically, it is a combination of two main effects of the effect for satisfying the requirements for reducing the time needed to accomplish sealing and improving packaging ability and the effect for enlarging the range for suitable sealing and thus reducing exten¬ sively the reject rate of sealing on practical use. The effect may be further divided depending on the selected sealing resin layers into a property group for providing a sealing part excellent in fusing ability accompanied with oil resistance and heat resistance or a property group for providing a film excellent in low temperature heat shrinkability, and the effect for improving the sealing performance which is common in both property group should be noted. The sealing mode on packaging in the art comprises first conducting sealing by heat fusion of the opening part of a cylindrical bag having a content under 1 a state to ensure that reduced pressure is accomplished also within the bag in a vacuum chamber and then pressure in the vacuum chamber is raised up to atmospheric pressure. At this time, the bag is deformed and 5 contacted tightly to the content by the pressure of air so that the profile of the external shape of the content will appear clearly, and such deforming force will act to deform or break the unsolidified part of the afore¬ mentioned sealing by heat fusion. A period of time 0 sufficient for solidifying the fused seal is incorporated in a time required for sealing in the art. The time required for sealing reached about 25% of the total time required for packaging. In the packaging by sealing in the afore- 15 mentioned, fashion, the film of this invention has preferably a heat resistant crosslinked polyolefin type resin layer arranged on the surface layer in the side in which the film touches directly a sealing bar and a resin heat fusible at low temperature arranged on the interior 20 surface sealing resin layer which will control the substantial fusing. That is to say, it may be considered ideal to produce the relationship that even if the interior surface side reaches the heating temperature where fusing proceeds satisfactorily, the surface layer 25. is scarcely molten or at least does not reach such a heated state as to press a fluidizingly deformed grooved damage by the heat sealing bar. In other words, specifically in the case of this invention, even if, for instance, a crosslinked ethylene-vinyl acetate σopolymer is used as the surface resin layer, there can be approached the aforementioned ideal by utilizing directly the very non-fluid property of the crosslinked resin even if the resin reaches the temperature at the upper limit where it can keep heat resistance, that is, the temperature exceeding the crystalline melting point. When a crosslinked ethylene- -olefin σopolymer having a high crystalline melting point such as 120°C or more, it will be easier to form the aforementioned state by the increased difference of the crystalline melting point as compared with that of a resin used as the sealing resin layer as well as the increased heat resistance of the aforementioned cros- slinked resin (corresponding to sample No. 28 in Example, Comparative Examples 1 and 2) . Therefore, it corresponds to the use of sealing condition at relatively low temperature condition side for the surface layer among the sealing resin layer within the integral laminated film. Accordingly, the sealing part solidifies at least at the surface side by cooling in a short time, resists the film deforming force applied on raising the pressure again up to atmospheric pressure and reduces extensively a period of time required for solidification by cooling. That is the so- called "reduction of sealing time" herein used and leads directly to the reduction of the time required for packaging. In the same manner, "reduction of reject rate of sealing" herein used will be explained below. Generally, film fusing at a sealing part is preferably carried out between two flat films positioned opposedly. However, the opening parts of bags continuously conveyed are not always a pair of flat films but rather folded in small wave shapes, and sealing is often carried out in such a state as to press directly the folded films. Therefore, the sealed part will inevitably cause the increased reject rate of sealing such as break of vacuum. To the contrary, if the sealing resin layer of the film of this invention has a range of suitable fusing at a lower temperature as mentioned above, the shape of the surface side of" the film is maintained by the afore¬ mentioned heat resistance, so that the folded sealing part even around the center is satisfactorily within the temperature range of compatible fusing and sealing pressure is also applied to the part. Consequently, the condition for suitable sealing of the sealing resin is satisfied and the tight sealing between the sealing resin layers proceeds. Fig. 7 corresponding to Example, Comparative Example 2 is a diagram from which a resin used as the aforementioned sealing resin layer is judged and also a demonstration of the preferred embodiment of this inven¬ tion. In Fig. 7, the regions illustrated by the plotting with marks (δ) or O generally correspond to the regions of the region species and the composition useful for "reduction of the time required for sealing" and "reduction of reject rate of sealing" provided that the aforementioned surface layer is used. Further, the diagram indicates that the region is a part represented by any one of the resins of an ethylene-α-olefin copolymer resin (resin A) having a density of 0.88 - 0.93 and a crystalline melting point of 110 - 130°C, a mixed resin comprising 60% by weight or more of said resin A and 40% by weight or less of an ethylene-α-olefin copolymer elastomer (resin B) or a mixed resin comprising 40% by weight or more of said resin A, 5 - 40% by weight of said resin B and 55% by weight or less of an ethylene- vinyl acetate copolymer resin (resin C) , .in which the percentages of the components in said mixed resins amount to 100% in total. Fig. 6 corresponding to Experimental Example 6 illustrates the results from the experiment for re- examining the aforementioned resin as the surface layer from another standpoint that when the PVDC layer is used as the core layer, the resin maintains the essential adhesive strength with the core layer. That is, in Fig. 6, the axis of abscissa represents the vinyl acetate content (% by weight) in the resin, the axis of ordinate in the left side represents the adhesive strength with PVDC (g/15 mm of width) , and the axis of ordinate in the right side represents the crystalline melting point (°C) of the resin. Plotting with empty circles O (co-extruded and unσrosslinked) and black-pained circles 9 (co- extruded and 5 Mrad dosed) represent the relationship between the vinyl acetate content and the adhesive content, and plotting with triangles Δ. represents the relationship between the vinyl acetate content and the crystalline melting point, respectively. At the parts corresponding to 0% of the vinyl acetate content, three ethylene-α-olefin copolymers having different crystalline melting points are applied to An, A3 and A5. Difference between the two kinds of circles O and • in Fig. 6 represents the increase of adhesive strength at the bonded part with the PVDC layer. Crosslinking efficiency at a constant dosage is generally considered to be proportional to the vinyl acetate contents. Accordingly, there can be anticipated in principle with the phenomenon that adhesive strength increases in the region of the vinyl acetate of 13% by weight or more in Fig. 6. However, it is extraordinarily found that the increase of the adhesive strength in the side of the lower vinyl acetate content of less than 13% unexpectedly corresponds in its absolute value of the adhesive strength with the increase shown by the un- crosslinked EVA having a vinyl acetate content of about 13 - 20%. The aforementioned phenomenon is effectively utilized in this invention. In other words, in order to maintain the adhesive strength of PVDC with a core layer, it is generally considered necessary to use a specific resin such as EVA, ΞEA (polyethylene ethyl acrylate) , EAA (polyethylene acrylic acid) and the like as an adhesion layer or as an adjacent layer to the core layer. However, it is difficult to maintain the other properties such as heat resistance (crystalline melting point) , oil resistance, heat shrinkability, and the like at high levels while maintaining the adhesive strength according to the conventional technics. Therefore, if heat resistance at a higher temperature side exceeding about 90°C, it is necessary to provide a layer having a further higher melting point such as a layer of an ethylene-α- olefin σopolymer resin or the like. But the resin is poor in the adhesive strength with the PVDC layer, and it cannot be inevitable to provide another EVA layer having a high vinyl aσetate content between the surfaces of the two, which consequently limit the quality design of the whole laminated film. The significanσe represented by Fig. 6 and useful in this invention σonsists in that even if an ethylene-α-olefin σopolymer having a high σrystalline melting point (vinyl aσetate σontent, 0%) is used as a surfaσe layer, an adhesive strength in the level of praσtiσal use can be principally obtained by providing the copolymer adjaσent to the σore layer, and an EVA layer having a relatively high σrystalline melting point (a low vinyl aσetate σontent) σan be used on providing an adhesion layer, so that the heat resistanσe and oil resistance of the whole laminated film can be improved. Further, to be noted is the value of the adhesive strength increased by the σo-extrusion-σrosslinking in the neighborhood of a vinyl aσetate σontent of 13 - 20% by weight. The high adhesive strength is an effeσt whiσh σould not be obtained without any deterioration of the PVDC layer, and the laminated film having a strong - bonding between surfaσe layers σan be obtained. These are exσellent effects produced by the crosslinking - acσording to this invention. A further preferred embodiment σorresponds to Table 3 in Experimental Example 3 and relates to a preferred embodiment of the PVDC layer used as a σore layer.- This σore layer σontrols prinσipally the oxygen gas barrier property of the laminated film and generally arranged in a state σontaining a plastiσizer and a stabilizer in an amount of 2 - 4% by weight. The σore layer has a problem to lower the oxygen gas barrier property by the yellowing by the irradiation of eleσtron rays to deteriorate or deσompose the transparent quality of a σontent. This invention restriσts the transmittanσe of eleσtron rays to reduσe the deterioration or yellowing to the minimum, but the deterioration or yellowing of PVDC σannot be σompletely avoided. Aσσording to the result listed in Table 3, in order to eliminate the deterioration or yellowing of the σore layer to the minimum, when PVDC is a vinylidene σhloride-vinyl σhloride σopolymer, the vinyl σhloride 1 σontent is preferably in the range of 10 - 25% by weight, and when PVDC is a vinylidene σhloride-methyl aσrylate σopolymer, the methyl aσrylate σontent is preferably in ' the range of 3 - 15% by weight. 5 In general, when the level of oxygen gas barrier property is desired to be enhanσed, the vinylidene σhloride-methyl aσrylate σopolymer is preferably seleσted. The b value referred herein is an index of a 10 σolor tone of a PVDC layer having been proσessed to a thiσkness of 100 miσron as an objeσt and represents the value measured in aσσordanσe with JIS Z 8729. The b value of 17 or less is an upper σriterion for satisfying the required quality in which the content (raw meat) 15 within the package are looked clearly. Another embodiment is the one which is obtained from the standpoint of eσonomy for manufaσturing a co- extruded laminated film and thus has a little different appearance from the aforementioned embodiments for 20 satisfying the required quality at a high level. That is to say, there have been investigated for a long time many ideas for preparing a multi-layer film in which resins σompatible with the purposes of respeσtive layers have been laminated to exhibit the best 25 performanσe in laminated films. However, when the multi¬ layer film is proσessed into a laminated film by a co- extrusion method of intra-die lamination, it is un¬ economical techniσally and thus undesirable to carry out σo-extrusion of the multi-layer film σomprising 6 layers or more beσause of the neσessity of the arrangement spaσe of an extruder and the laminating structural space within a die. Aσσordingly, it is also neσessary to reduσe the number of layers and thus the kinds of resins used or to σombine two or more of the resin speσies of whiσh properties are σompatible with eaσh other so that an extruder σan be used for two or more layers to reduσe the number of extruders used. From suσh standpoint, in the film of this invention σomprising laminating respeσtive resin layers in the sequenσe of (II)/(I)/(III)/(IV) or (II)/(II) '/(D/ (III)/(IV) , if resins in the same kind whiσh σan be σommonly used for the "layers (II) and (IV) σan be provided with one extruder, a laminated film σomprising 4 - 5 layers σan be σonveniently manufaσtured by 3 - 4 extruders. Alternately, if a resin whiσh may be σommonly used for the layers (II) ' and (III) is further used, a laminated film σomprising 4 - 5 layers σan be manufaσ- tured with three extruders. A further embodiment relates to an appliσation most suitable to the film of this invention, the film thiσkness for satisfying the required quality for the appliσation and the layer σonstruσtion with the thiσkness (corresponding to Tables 6-A and B in Example, Compara¬ tive Example 1) . As compared with the same kind of commerσially available film, it σan be found that the film of this invention is a film whiσh has required main properties all in high levels and aσσomplishes σompletely the improvement of paσkaging performanσe as the required quality in σurrent market (see Table 11 for Example, Comparative Example 5) . A further embodiment relates to a preferred supplying shape of the σylindriσal film of this inven- tion. That is to say, σylindriσal laminate σo-extrusion is σonduσted, and the product is subjected to inflation orientation and direσtly rolled up to form a seamless σylindriσal laminated film. The seamless σylindriσal laminated film σan be sealed tightly only by bottom sealing and top sealing. This is a desirable film beσause it has only two parts to be sealed and thus produσing a fewer rejeσt rate at the sealing, parts. However, if the seamless σylindriσal laminated film, has a small diameter, the produσtion effiσienσy on film formation is low and the σost will be heightened. In suσh a σase, a wide seamless σylindriσal film is first produσed and folded flatly. Then, a bottom part is provided to the film so as to have a required width, and the film is σut into pieces by a side sealing method. Thus, the σylindriσal laminated film having a small diameter σan be eσonomiσally manufaσtured. Table 11 σorresponding to Example, Comparative Example 5 illustrates the results of σlassifiσation of the qualities and performanσe of the film of this inven¬ tion with referenσe to quality level in comparison with the currently available film in the art. Table 11 also proves the property of the explanation of the σontents of this invention, because almost of the items of the above- mentioned evaluations, of which items have been divided into small classes of items, are listed in combination iι this table and σan be evaluated in the same time. As apparent from the results listed in Table 11, the quality level of the film of this invention typified by the sample Nos. 17 and 28 σan be said to satisfy the high quality levels in many items as σompared with those of σommercially available films. Oil resistance, heat resistance and shrinkability also reach certain levels. It σan be found more preferable to use the sample Nos. 34 and 52 for paσkaging proσessed meat whiσh requires boiling, and. the sample No. 39 "for paσkaging raw meat whiσh needs high level of heat shrinkability at lowe-r temperature. The term "ethylene-α-olefin σopolymer resin" having a density of 0.88 - 0.93 (g/σm-3) and a σrystalline melting point of 110 - 130°C" used in this invention means a σopolymer resin of ethylene and an α-olefin having 4 - 18 σarbon atoms such as 1-butene, 1-pentene 4-methyl-l- pentene, 1-hexene, 1-octene or the like. The term "ethylene-α-olefin σopolymer elastomer" means a thermoplastiσ elastomer having a density of 0.91 - 0.85 (g/σm3) and a Viσat softening point (measured in aσσordanσe with ASTM D 1525 with a load of 1 kg) of 80°C or less and a rubber-like substanσe of a σopolymer of ethylene and an α-olefin having 3 - 8 σarbon atoms suσh as ' propylene, 1-butene, 1-hexene, 1-heptene, 4-methyl-l- pentene, 1-oσtene or the like. Further, the term "polyvinylidene σhloride type resin (PVDC) " used in this invention means a σopolymer resin obtained from vinylidene σhloride and a monomer σopolymerizable therewith (e.g., vinyl σhloride, methyl aσrylate or the like) . The term "gel fraction" used in this invention means a gel fraction obtained by the following operations is acσordance with ASTM D 2765. (1) A sample (ca. 50 mg) taken from a presσribed position is weighed with a balanσe having a presion of 0.01 mg (S g) ; (2) A 150 mesh sσreen pouσh manufaσtured by SUS whiσh has preliminarily dipped into aσetone for 24 hours to remove oil and the sample are weighed with the balanσe (Wl g) ; (3) The sample is paσkaged with the pouσh; (4) The sample paσkaged with the pouσh is plaσed in a separable flask equipped with a σondenser and retained in boiling paraxylene for 1 - 2 hours; (5) The sample paσkaged with the pouσh is dried in a vaσuum drier until it reaσhes a σonstant weight; (6) The sample packaged with the pouch is weighed with the aforementioned balance (W2 g) ; and (7) Gel fraσtion is σalσulated by the equation of Gel fraσtion (% by weight) = [1 - (Wl - W2)/S] x 100. Attention should be paid on preparing the sample for measuring the aforementioned gel fraσtion with reference to the followings: When a speσifiσ layer of a laminate is intended to use as a sample, the layer should be peeled slowly with σoating ethanol thereon; and When a surfaσe layer of a specific layer in a parison is intended to use as a sample, a piece of 10 mm x 20 mm is cut from a portion of the peeled speσifiσ layer having a good flatness and the surfaσe layer is sliσed into a thiσkness of about 20 miσron with a miσrotome for an optiσal miσrosσope to make samples. It is also possible to sliσe a speσifiσ layer of an oriented film whiσh has been peeled in the same manner as above and returned to a parison state by the heat shrinking * treatment. Evaluation methods and evaluation σriteria used in this invention will be explained below. (1) Film formability by drawing An apparatus (or a method) illustrated in Fig. 5 was used. The pinσh rolls 19 were driven at a speed of 7m/min, and film formation by drawing was attempted in order to reaσh a draw ratio in maσhine direσtion to transverse direσtion of 3/4. Evaluation was σonduσted with referenσe to the easiness of start-up of film formation by drawing, interσonneσted stability of a drawn bubble and thiσkness spots of the film obtained. Grade Criteria @ : Easy start-up; good interσonneσted stability of - - Q bubble; thiσkness uniformity of film, within ±15%; Δ : No problem for start-up; drawing starting posi¬ tion vibrated finely; thickness uniformity film, exceeding ±15% and within ±25%; * : Start-up with difficulty; drawing starting position is not fixed; thickness spot of film exσeeds ±25%; and : Drawing with diffiσulty; even if drawing was 10 conducted, undrawn part remained in a zone or bubbles were rapidly broken. (2) Oil resistance of interior surface The seamless film thus produced was cut into a predetermined length, and one end thereof was subjected 15 to heat sealing under a condition for obtaining a maximum strength to make a bag. On the interior side of the bottom sealed part of the bag was σoated lard, roast pork was pushed into the bag until it abuts against the bottom sealing, and vaσuum 20 paσkaging was σonduσted. Twenty paσkages thus prepared were dipped into hot water at 90°C and taken up from the hot water with a predetermined intervals, and the oil resistanσe of interior surfaσe was evaluated by inspeσting the presence of break at the bottom sealing part. The oil 25 resistanσe was σonsidered good when the broken seals remain within one. This evaluation was σonduσted with an antiσi- pation of the paσkage for use of boiling prόσessed meat. Grade Criteria ® good after 20 minutes, o good after 5 minutes, good after 1 minute „ f failed after 1 minute. (3) Oil resistanσe of interior surfaσe II After suet was σoated on the interior side of the bottom sealing part of the bag, raw beef was pushed into the bag until it abuts against the bottom sealing, and vaσuum paσkaging was σonduσted. Twenty paσkages thus prepared were passed through hot water shower at 90°C over a period of time desσribed below, and oil resistanσe • of interior surfaσe was evaluated by inspeσting the , presenσe of break, at the bottom sealing part. The oil resistance was considered good when the broken seals remain within one. This evaluation was σonduσted with an antiσipation of the paσkage for use of σhilled beef. Grade Criteria © good after 12 seσonds, O good after 8 seσonds, Δ good after 4 seσonds failed after 4 seconds. (4) Reduction of time required for sealing Using the bags prepared above, the suitable condition of impulse sealing in a vacuum packaging machine was selected based on strength. Then, meat in an amount of 10 - 15 kg was plaσed in the bag, whiσh was then plaσed at the position as near as possible to the sealing part of a vaσuum packaging machine. Suet was σoated on the interior side of a part to be sealed, and then vaσuum paσkaging was σonduσted with changing the cooling time after sealing as described below. After dipping the sealed bag into hot water at 90°C for 4 seconds, evaluation was conducted referring to break of vacuum, elongation at the sealed part, break, peeling of the surface layer of the film and the like based on the cooling time required for protecting the failure of the film. The number of packages was 30. Grade Criteria (Q) : no failure in 1 second of cooling time; Q : failure did not ' disappear until cooling time was prolonged to 2 seconds; A : failure did not disappear until cooling time was prolonged to 3 seconds; x : failure did not disappear even if cooling time was prolonged to 3 seconds. (5) Reject rate of sealing Using the bags prepared above, a folding part (double layered part) was intentionally made on one of the films, and the condition of impulse sealing was examined required for fusing completely with involving the folding part. Then, raw meat in an amount of 10 - 15 kg was placed in the bag, which was then plaσed at the position as near as possible to the sealing part of a vaσuum paσkaging maσhine. Suet was σoated on the interior side of a part to be sealed, and the opening part of the bag was σonverged with hands and left opening to make intentionally fine flexes with twisting. Then, vaσuum paσkaging was σonduσted under the σondition of σooling time for 2 seσonds after sealing. After dipping the paσkaged produσt into hot water at 90°C for 4 seσonds, evaluation was σonduσted referring to break of vaσuum, elongation at the sealed part, break, peeling of the surfaσe layer of the film and the like referring to the presenσe of the failure of the film. The number of paσkages was 30. Grade Criteria (Q) : within 1 of failed sealing; Q : 2 - 3 of failed sealing; Δ : 4 - 9 of failed sealing; x : 10 or more of failed sealing. (6) Falling bag resistanσe at low temperature After the bottom sealed part of the bag prepared above was σoated with suet, water in an amount of 6 kg at about 2°C was σharged into the bag. The opening side of the bag was held with hands and the bottom sealed part was dipped into hot water at 90°C for 4 seσonds. Then, the opening was σlosed with a string. The bag fallen from a height of 1 m onto a flat σonσrete surfaσe, and evaluation was σonduσted based on the number - 39 of broken bags. The number of bags used in the test was 10. Grade Criteria (§) : within 1 of a broken bag; O : 2 - 3 of broken bags; Δ : 3 - 5 of broken bags; x : 5 or more of broken bags. (7) Oil resistanσe at dints A synthetiσ rubber dummy (having a length and a width of 30 σm, respeσtively and a thiσkness of 10 σm, on the surfaσe of whiσh are arranged semispheriσal dints having a radius of 1.5 σm with an interval of 10 σm) was plaσed into a bag prepared above and paσked under vaσuum. After σoating suet on the exterior surfaσe, the bag was dipped into hot water at 90°C for 4 seσonds and then taken out. The presenσe of damages suσh as break or the like on the dints was examined to judge the total strength (heat resistance and oil resistanσe) of the film. Evaluation was σarried out based on the break rate of the film. Grade Criteria within 10% of the break rate; o 10% - 20% of the break rate; Δ 20% - 50% of the break rate; more than 50% of the break rate. (8) Color tone (b value) of PVDC After a film was shrunk at a temperature of 70°C or more, only PVDC layers having been peeled and taken out were layered to a thiσkness of 100 ±5 μ and plaσed on a white board. The b value was measured with a refleσting light in aσσordanσe with JIS Z 8729 to judge the σolor tone. A mineral oil has been σoated on the interfaσes between the PVDC layers. The larger the b value is, the more extensive the yellowing beσomes. Grade Criteria (g) : 15 or less of the b value; Q : 15 - 17 of the b value; Δ : 17 - 20 of the b value; x : more than 20 of the b value. (9) Transparenσy of the film A film was plaσed on a σylinder having a bottom, the interior surfaσe of whiσh was lined with a black cloth for absorbing light, and the L value was measured with a reflecting light in acσordanσe with JIS Z 8729. The larger the L value is, the more whitish the film is. Grade Criteria (the L value) (§) : 7 or less; .O :' more than 7 and within 8; Δ ■ more than 8 and within 9; x : more than 9. (10) Transparency of the film after shrinking A film was dipped in a hot water bath at 90°C for 4 seσonds and shrunk under a relaxed state. After moisture on the surfaσe had been wiped off, the haze of the film was measured in aσco ' rdance with ASTM D 1003 to evaluate the transparency. Grade Criteria (Haze) 15% or less; o more than 15% and within 25%; Δ more than 25% and within 40%: more than 40%. (11) Heat shrinkability and heat shrinkability at low temperature A film having been cut into a square of 10 cm in length and width was dipped in a hot water at 90°C referring to heat shrinkability or at 75°C referring to heat shrinkability at low temperature for about 4 seconds and shrunk under a relaxed state. The shrinkage factor was obtained by averaging shrinkage faσtors in length and width based on the size at initiation. Grade Criteria (Shrinkage factor) © 30% or more; o 20% or more and less than 30%; Δ 15% or more and less than 20%; less than 15% (12) Oil resistanσe on the exterior surfaσe of the film A film was spread in tension over a wooden frame, and the exterior layer surfaσe was σoated with lard. Then, the film was dipped together with the wooden frame into hot water at 90°C and taken out after the intervals of time mentioned below. The presenσe of damages suσh as swelling of the exterior layer, whitening or the like was examined to evaluate the oil resistanσe of the exterior surfaσe of the film. Grade Criteria good after 20 minutes; O good after 5 minutes; Δ good after 5 seσonds; failed after 5 seσonds. (13) Ply separation resistanσe A film as out into a shape of about 30 σm in length and width, and lard was σoated on the both ex¬ terior and interior surfaσes and ends. Then, the film was dipped in a relaxed state into hot water at 90°C for 20 minutes and then taken out. The presenσe of bubble¬ like ply separation in the film and ply separation at the end parts of the film were examined to σarry out evalua¬ tion. Grade Criteria (Q) : no separation over all surfaσes of the film; Q : partial separation at the ends of the film; Δ : separation at the ends or partial bubble-like separation; x : separation at the ends or bubble-like separation. - - (14) Maintenanσe rate of oxygen barrier property after flexing with twisting of the film A film was dipped in a relaxed state into hot water at 90°C for 4 seσonds and shrunk. Then, the GELBO test in aσσordanσe with MIL STD. B-131 was repeated 100 σyσles at 0 - 2°C, and the oxygen gas penetrating rates before and after test were measured in aσσordance with ASTM D3985. The penetrating rates were compared, and the strength of the PVDC layer against the flexing with twisting was judged. If the inσrease of the penetrating rate was within 30%, judgement of good was given. Evaluation was σarried out by the perσentage of good produσts. The number of films tested was 20. Grade Criteria (defeσtive rate) within 10%; O more than 10% and within 25%; Δ more than 25% and within 50%; more than 50%. (15) Maintenanσe rate of oxygen barrier property after rough treatment under severe σonditions A synthetiσ rubber dummy (having 30 σm in length and width, respeσtively, and 20 σm in thiσkness, all tops and edges of whiσh were rounded in a σurvature radius of 2 σm and on the whole surfaσes of whiσh are arranged semispheriσal extrusion having a radius of 3 σm with an interval of 2 σm) was paσkaged under vaσuum with a bag prepared above and passed through hot shower at 90°C. The bag was plaσed into a octahedral rotary drum lined with a corrugated board. The drum was rotated 200 times at 0 - 2°C. Then, the film was peeled off, and the oxygen gas penetrating rate was measured in the same manner as in (14) and used as judgement of the strength of the surface layer against rubbing with the exterior surface. The film as partly drawn by the extrusions on the dummy, so that the increase of oxygen penetrating rate within 50% of that σalσulated from the average shrinkage faσtor were judged good, and evaluation was σarried out with the perσentages of good produσts. Grade Criteria (Defeσtive rate) © within 10%; O more than 10% and within 25%: Δ more than 25% and within 50%; more than 50%. (16) Heat resistanσe of films Exterior surfaσe side of a film spread in tension over a wooden frame was touσhed softly with a hot plate having a radius of 40 mm and heated to 200°C. The presenσe of a hole at the σontaσt part was examined with a naked eye. The heat resistanσe of the film was evaluated by judging the film having no hole good and the one having a hole defeσtive. The number of the film tested was 20. This evaluation was σarried out with antiσipation of σheσking the pinholes whiσh tend to generate in the neighbourhood of the sealing part on - - sealing when the film is heated to high temperature. Grade Criteria (Hole defeσtive rate) within 10%; c more than 10% and within 25%; Δ more than 25% and within 50%; more than 50%. Experimental Example 1 This experiment is intended to examine the effeσts of the dosage distribution (depth) and dose (strength of irradiation) of eleσtron rays on the film of this invention. In this experiment, films were prepared by σhanging eleσtron beam irradiating methods and irradi¬ ation σonditions with a film produσing apparatus illustrated in Fig. 5, and evaluation was σarried out referring to heat resistanσe and oxygen barrier property after flexing with twisting. In this experiment, films were prepared by changing electron beam irradiating methods and irradi- ation conditions with a film producing apparatus illust¬ rated in Fig. 5, and ' evaluation was σarried out referring to heat resistanσe and oxygen barrier property after flexing with twisting. First of all, preparation methods of films are explained below. In Fig. 5, a parison σomprising four layers was extruded with three extruders 1 - 3, drawn at a speed of about 7 m/min to make a σylindriσal parison having a flat width of 115 mm. The parison σomprised sequentially from its exterior side EVA (having a vinyl aσetate σontent of 13.5% by weight)/PVDC (a vinylidene . σhloride-vinyl σhloride σopolymer resin having a σomonomer σomponent derived from the vinyl σhloride monomer in the resin of 17% by weight)/EVA (having a vinyl acetate of 13.5% by weight) /a sealing resin layers, which layers had a thickness of 275 μ/65 μ/225 μ/165 μ. As the afore¬ mentioned sealing resin, an ethylene-α-olefin copolymer resin (very-low density polyethylene: density, 0.906; σrystalline melting point, 118°C; trade name, NUC-FLX manufaσtured by NIPPON UNICAR Co.) was used. The parison was irradiated with eleσtron rays using an eleσtron beam irradiating apparatus 8. The eleσtron beam irradiating apparatus used in this experiment was two kinds of appa¬ ratuses, that is, ELECTROCURTAIN ® (non-sσanning type) manufaσtured by ENERGY SCIENCE INC. and a sσanning type eleσtron beam irradiating apparatus manufaσtured by NISSIN-HIGH VOLTAGE CO. Irradiation crosslinking was carried out with changing dosages as shown in Table 12 by the use of these two electron beam irradiation appa¬ ratuses. The crosslinked parison was introduσed into a heating bath 17 illustrated in Fig. 5, heated to a temper¬ ature of 80°C and subjeσted to an inflation biaxial orien- tation treatment to draw the film to a maσhine direσtion of about 3 times and a transverse direction of 4 times, respectively, of their original sizes. The film having a flat width of 460 mm and an average thickness of about _ _ 1 60 μ was prepared in a length of 300 m and rolled round a bobbin. For comparison, a further film was prepared without irradiation. The start-up of drawing was acσo panied with 5 diffiσulty in some degrees in the σase of sample Nos. 101, 108, 109, 110 and 116 in Table 12. (Diffiσulty was due to that these samples were irradiated only in low levels or nothing.) Next, the film was left standing while it was 10 rolled round the bobbin for 3 days and then unrolled into a film for 10 days at room temperature. Then, heat resistanσe of the film was evaluated using a part of the sample having a thiσkness of 60 ± 5 μ in the manner desσribed " above. A run of twenty evaluation was 15 σonduσted. Also, the film was dipped in a relaxed state into hot water at 90°C for 4 seσonds and shrunk. Then, retention of oxygen gas barrier property after flexing with twisting of the film was evaluated in the manner desσribed above. A run of twenty evaluation was 20 σonduσted to σalσulate the non-defeσtive rate of the film. The relationship between samples and the irradiation conditions and the non-defective rates obtained by the aforementioned evaluation were listed in 25 Table 12. Fig. 9 illustrates the plotting of non- defective rates to the dosages. In Fig. 9, empty marks mean the plottings of experimental results using a modified non-sσanning type eleσtron beam irradiation apparatus whiσh was used in this invention, in whiσh empty σirσles O illustrate the heat resistanσes of films and empty triangles illustrate the oxygen gas barrier properties after flexing with twisting of films. Blaσk-painted marks mean the plottings of experimental results using a conven¬ tional scanning type electron beam irradiation apparatus, in which black-painted cirσles ® illustrate the heat resistanσes of films and blaσk-painted triangles illustrate the barrier properties after folding of films. The dosage distribution in the direσtion of depth using the modified non-sσanning type eleσtron beam irradiation apparatus whiσh was praσtiσally used in this experiment was illustrated by a solid line based on the dosage at the surfaσe as 100% in Fig. 1. The dosage distribution using the σonventional sσanning type eleσ¬ tron beam irradiation apparatus was illustrated by a broken line 1. (Measurement was desσribed in Experi¬ mental Example 2.) It σan be understood from Fig. 1 that the modified non-scanning type electron beam irradiation apparatus which was used in this invention extensively attenuated dosage at a depth of a sample and thus electron rays does not penetrate a depth of a sample. Acσording to the result shown in Fig. 9, in the σase of the σonventional method (black-painted marks) crosslinking effect increases rapidly from about 4 Mrad and reaches its maximum level at about 6 Mrad. But large dosage of electron rays is irradiated also to the PVDC layer, so that deterioration of the PVDC beσomes remark¬ able, and a half of the PVDC beσomes defeσtive at about 3 Mrad where no σrosslinking effeσt appears. Therefore, it is impossible to seleσt any appropriate range„of exposed dose in whiσh irradiation (crosslinking) effect σan be taken without the deterioration of the PVDC layer. On .the other hand, Fig. 9 indiσates that a ' σσording to the proσess of this invention (plotting with empty marks) , development of the σrosslinking effeσt remains at a low level and exposed dose of about 7 - 10 Mrad is required for obtaining the σrosslinking effeσts at a maximum level, but the dosage irradiated on the PVDC layer is very small and the deterioration of the PVDC at the same dose level is also reduσed remarkably, so that it is possible to seleσt an appropriate range of exposed dose for remaining the deterioration of the PVDC layer at a minimum level while maintaining the σrosslinking effeσt at a high level. Table 12 *1 Not evaluated Experimental Example 2 This experiment is intended to illustrate several dosage distribution referring to irradiating electron rays in the film of this invention and to explain the importance of selecting the dosage distribu¬ tion (depth of irradiation and size of σrosslinking degree) to the film. The dosage distribution is obtained by irradi¬ ating many layers of an EVA film (having a vinyl aσetate content of 13.5%) having a thiσkness of 10 μ under a σondition of irradiating with an apparatus of whiσh dosage distribution is intended to be examined and then measuring with boiling xylene the residual gel fraction of the film as the size of crosslinking degree. The σonstruσtion of the σylindriσal parison proposed to the experiment is sequentially from the exterior side EVA (having a vinyl aσetate σontent of 13.5% by weight)/PVDCX (a vinylidene σhloride-vinyl σhloride copolymer resin having a σomonomer σomponent derived from the vinyl σhloride monomer in the resin of 17% by weight)/EVA (having a vinyl aσetate of 13.5% by weight) /a sealing resin layers, whiσh layers had a thiσkness of 275 μ /65 μ/225 u/165 V m The aforementioned sealing resin is a mixed resin of an ethylene-α-olefin σopolymer resin having a crystalline melting point of 120°C : ethylene-α-olefin copolymer elastomer : EVA (having a vinyl acetate content of 15% by weight) = 8 : 1 : 1. Films are prepared in the same manner as in Experimental Example 1. The relations between the irradiation apparatus and the exposed samples are listed in Table 1. The dosage distribution in the direσtion of depth using the modified non-sσanning type eleσtron beam irradiation apparatus whiσh was praσtiσally used in this experiment was illustrated by a solid line based on the dosage at the surfaσe as 100% in Fig. 1. The dosage distribution using the σonventional sσanning type eleσtron beam irradiation apparatus by applying a high aσσeleration voltage of 500 kV was illustrated by a broken line 1. The dosage distribution by applying an extremely low aσσeleration voltage of 250 kV was illustrated by a broken line 2. The dosage distributions of the exposed samples (Nos. 117 - 122 and 152) were illustrated as (a) to ( ) and (m) in Fig. 2. For the respeσtive samples, evaluation was σarried out by the methods desσribed herein referring to film forming ability by drawing, yellowing of PVDC, oxygen gas barrier property after rough treatment under severe σonditions, the barrier property after flexing the film with twisting, heat resistanσe of the film and gel fraσtion. The results are listed in Table 2. As for the gel fraσtion, measurements were σarried out for the whole layers of a parison from whiσh the σrosslinked polyolefin type resin layer (II) in the exterior surfaσe side of the parison had been peeled, the exterior layer of said layer (II) and the exterior layer in the PVDC layer side of said layer (II) . The gel fraσtion gradient [y/x] was σalσulated from the partial gel fraσtion [x] at the exterior surfaσe layer and the partial gel fraσtion [y] at the surfaσe layer in the PVDC layer side and listed in the table. The samples illustrated by Nos. 117, 152, 118 to 120 (σorresponding to the dosage distributions (a) , ® r ©' © an ^ (D ^ n Fig. 2, respeσtively) in Table 2 are arranged so that the effeσt of the σhange of the dosages of eleσtron rays having a σonstant penetrating level in the direσtion of depth σan be noted. Sample Nos. 118, 121 and 122 (σorresponding to the dosage distribution (b) , (e) and (f) , respeσtively) ,are intended to exglain the effeσt of the irradiation of eleσtron rays having different penetrating levels in the direσtion of depth. First of all, the effeσt of penetrating levels of eleσtron rays in the direction of depth is explained. The sample having the dosage distribution (b) , film form¬ ing ability by drawing and the heat resistance of which are improved by crosslinking and barrier property of which is also retained, is thus preferred. This is probably due to that although the electron rays penet- rates with sufficiently σrosslinking the σrosslinking polyolefin type resin layer (II) into the bonding layer between the layer (II) and the PVDC layer to cause denaturation so as to increase adhesion, it gradually attenuates and penetrates only central position of the PVDC layer, which is irradiated with only a small dosage on the PVDC layer and cause no deterioration. On the other hand, the sample having the dosage distribution (f) (No. 122) , although it has a crosslinking effect, is drastically deteriorated in the PVDC layer (in retention rate of oxygen barrier property after flexing of film and color tone of PVDC) and thus can not be used practiσally. The reason is that the gel fraσtion gradient is 0.63, that is, eleσtron rays penetrates the depth and the PVDC layer is also irradiated with a high dosage of eleσtron rays to σause deterioration. The sample having the dosage distribution (e) (No. 121) exhibits a very interesting phenomenon that eleσtron rays does not penetrate into the bonding part between the PVDC layer and the exterior surfaσe layer, whiσh part is not denaturated by eleσtrσn rays and adhesive strength is not inσreased. Also unσrosslinked part in the exterior surfaσe layer remains in the neighbourhood of the PVDC layer, whiσh probably makes the film too weak to endure external forσe. Next, dosages are explained with referenσe to eleσtron rays having the same penetrating level in a direσtion of depth. From the results obtained from the samples of Nos. 117, 152, 118 to 120 listed in Table 2. The dosage range suitable for the film of this invention has a lower limit illustrated by dosage distribution (σ) (No. 119) , in whiσh the gel fraσtion is 20% by weight in the whole σrosslinking polyolefin type resin layer and 25% by weight in the exterior surfaσe layer. If the dosage is less than the lower limit desσribed above, the gel fraσtion is insuffiσient as illustrated by the dosage distribution (d) (No. 120) , so that properties inσluding film forming ability by drawing, heat resistanσe and resistanσe to rough treatment under severe conditions are not improved. The upper limit is illustrated by the dosage distribution (m) (No. 152) , in which the gel frac¬ tion is 60% by weight in the whole crosslinking polyolefin type resin layer and 70% by weight in the exterior surfaσe layer. If the dosage is larger than the upper limit, the gel fraσtion is slightly exσessive as illustrated by the dosage distribution (a) (No. 117) , so that film forming ability by drawing is less preferred. From the above explanation, it σan be said that the range of dosage distribution suitable for the film of this invention is illustrated by (m) , (S) and (σ) (sample Nos. 152, 118 and 119, respeσtively) in Fig. 2. If it is expressed by the penetrating level of eleσtron rays, the gel fraσtion gradient of the σrosslinking polyolefin type resin layer (II) is 0.6 or less and the bonding part between the layer (II) and the PVDC layer (I) is a bond¬ ing part whiσh has been denaturated with eleσtron rays. If it is expressed by dosage, the gel fraσtion of the whole layer (II) is in the range of 20 - 65% by weight and the gel fraσtion at the exterior surfaσe layer [x] is in the range of 25 - 70% by weight. The range of the gel fraσtion gradient will be explained again in Experimental Example 5 with referenσe to the aforementioned layer (II) σomprising two layers. Table 1 *1 Dosage at the surfaσe part of the σylindriσal parison *2 If it will be further lowered, output will be too decreased to use it industrially. In addition, the dosage distribution is too short against the depth to apply for this invention. Table 2 *1 At the initial stage of rough treatment.under severe condition, the exterior layer is separated from the PVDC layer. Experimental Example 3 This experiment is intended to explain the signifiσanσe of the seleσtion of the kind of PVDC in this invention. This experiment was σarried out in the same manner as in Experimental Example 2 exσept that the σomposition of PVDC used as the σore layer of the sample No. 118 was σhanged as follows. The PVDC's used were a vinylidene σhloride-vinyl σhloride σopolymer resin and a vinylidene σhloride-methyl aσrylate σopolymer resin. In the vinylidene σhloride-vinyl σhloride σopolymer resin, the σontent of the σomonomer σomponent derived from the vinyl σhloride monomer in the resin was varied in 8 levels of 4, 6, 8, 10, 17 { 25, 28 and 30% by weight, and in the vinylidene σhloride-methyl aσrylate σopolymer resin, the σontent of the σomonomer σomponent derived from the methyl aσrylate monomer in the resin was varied in 6 levels of 1, 3, 10, 15, 18 and 20% by weight. The films thus prepared were evaluated by the evaluation methods desσribed herein with referenσe to the σolor tone (b value) of PVDC and oxygen barrier property after flexing of the film with twisting. The results are listed in Table 3. Aσσording to the results shown in Table 3, in the irradiation of eleσtron rays having the dosage distribution (b) (Fig. 2), as the PVDC iri order to avoid deterioration or yellowing whiσh will be σaused at the σore layer there are preferably used a vinylidene σhloride-vinyl σhloride σopolymer resin, in whiσh the σontent of the σomonomer σomponent derived from the vinyl σhloride monomer in the resin is in the range of 10 - 25% by weight, and a vinylidene σhloride-methyl aσrylate σopolymer resin, in whiσh the σontent of the σomonomer σomponent derived from the methyl aσrylate monomer in the resin is in the range of 3 - 15% by weight. As explained above, it is very signifiσant to seleσt suitably the PVDC used as the σore layer. In order to exhibit the effeσt of improving the film forming ability by drawing and the effeσt of improving the film properties to the maximum, it is neσessary to irradiate the polyolefin type resin layer as the surfaσe layer to the direσtion of its depth with eleσtron rays in a suffiσient amount. However, in its σase the σore layer is inevitably irradiated with eleσtron rays. The presenσe of PVDC which is relatively stable to electron rays made possible to directly irradiate the surface of a coextruded layer whiσh has been σonsidered impossible to σomplete direσt irradiation. Table 3 Experimental Example 4 This experiment is intended to explain the σonstruσtion method of the σrosslinking resin layer whiσh is one of the important points for aσσomplishing the film of this invention, that is, the effeσt of the proσesses for providing a σrosslinking polyolefin type resin layer on the surfaσe of a laminated film σomprising- a PVDC layer as the σore layer on the properties of the laminated film obtained. As the methods for σonstruσting the σrosslink¬ ing layer, there were used the following well-known methods; a method aσσording to Fig. 1 in Japanese Patent Appliσation Publiσation No. 43024/83, a method aσσording to Japanese Patent Appli¬ σation Kokai (Laid-Open) No. 143086/76, page 4, a method aσσording to Figs. 6 and 7 of US Patent No. 3,821,182, and a method aσσording to Japanese Patent Appli- σation Kokaid (Laid-Open) No. 82752/83, pages 4 - 5, whiσh methods were repeated as preσisely as possible (sample Nos. 136, 137, 138 and 139, respeσtively) . As the eleσtron beam irradiation apparatus, there was used a 500 kV sσanning type irradiation apparatus manufaσtured by NISSIN-H GH VOLTAGE CO. LTD. The dosage distributions applied to the films were those illustrated in Tables 3-A and 3-B as (g) , (h) , ( ) and For σomparison, a laminated film aσσording to Japanese Patent Appliσation Publiσation No. 1295/86 was prepared as a representative of unσrosslinked (unirradi- ated) artiσles and listed in Table 4 as sample No. 140. The struσtural features of the laminated films prepared above are listed in Table 4. These films (sample Nos. 136 to 140) and the film of this invention (sample No. 118) were evaluated by the methods desσribed herein with referenσe to film forming ability by drawing, rejeσt rate of sealing, σolor tone (b value) of PVDC, oil resistanσe on exterior surfaσe, resistanσe to PLY (interfaσial) separation and oxygen gas barrier property after flexing of film external with twisting. The results are listed in Table 5. Aσσording to the results shown in Table 5, effeσt of improving film forming ability by drawing σan be exhibited by using the laminate σomprising a σros¬ slinking resin layer. But if eleσtron rays for σros- slinking irradiates the PVDC layer largely, the PVDC layer is too extensively deteriorated to use it praσtiσally even if a PVDC having a seleσted σontent of the σomonomer is used. On the other hand, in the films prepared by laminating another layer on the σrosslinked layer (sample Nos. 136 and 139) / resistanσe to PLY (interfaσial) separation σannot be guaranteed. Therefore, it σan be said that the σonstruσtion method of this invention (sample No. 118) , in whiσh the whole layers having a sealing layer in the interior side are laminated by a σo-extrusion method, and the surfaσe layer of the laminate are moderately σrosslinked, is an exσellent method for exhibiting satisfaσtorily properties of respeσtive layers. Table 4 Table 4 (Cont'd) • cont'd - Table 4 (Cont'd) *1 Vinylidene chloride-vinyl chloride copolymer resin, in which a comonomer component derived from the vinyl chloride monomer in the resin is in an amount of 17% by weight. *2 (Resin mentioned in *3) : EVA (having vinyl acetate of 10% by weight. ) *3 Linear low density polyethylene having a crystalling melting point of 120°C and a density of 0.920. Table 5 Experimental Example 5 This experiment is intended to explain specifi- σally the σreative σontent of the method for produσing a σrosslinked surfaσe layer whiσh is advantageous for improving the film of this invention having a high σrosslinking degree (gel fraσtion) without damaging the so-σalled film forming ability by drawing, and the effect thereof. Experiment was σarried out in the same manner as in Experimental Example 2 to obtain a film of sample No. 117 (dosage distribution (a)) . Experiment was also σarried out in the same manner as above exσept that in the layer σonstruσtion, the outermost part having a thiσkness of 170 μ in the interior side of the EVA layer (vinyl aσetate content, 13.5% by weight) having a thick¬ ness of 275 μ at the exterior layer is replaced with an EVA resin layer having a vinyl aσetate σontent of 10% by weight, and the residual part having a thiσkness of 105 is replaσed with an EVA resin layer having a vinyl aσetate σontent of 15% by weight to obtain the sample No. 141. The sample is formed in the same manner as in Experimental Example 1 by the use of an apparatus illust¬ rated in Fig. 5, and speσifiσally film was formed by the use of five extruders inσluding another extruder in addition to four extruders 1 - 3' illustrated in Fig. 5. The sample No. 141 was evaluated in the same manner as in Experimental Example 2 aσσording to the methods desσribed herein with referenσe to film forming ability by drawing, yellowing of the PVDC layer, oxygen gas barrier property after rough treatment under severe conditions, oxygen gas barrier property after flexing of film with twisting, heat resistance of film and the gel fraction of the polyolefin type resin layer. The results are listed together with those of the sample No. 117 in Table 14 for σomparison. The gel fraσtion in Table 14 was measured for that [x] at the exterior surfaσe layer and that [y] at the surfaσe layer in the layer (I) and listed together with the gel fraσtion gradient [y/x] . In order to find the praσtiσal gel fraσtion (σrosslinking degree) to the direσtion of the depth in the surfaσe layer, a film having a thiσkness of 10 μ as layered to obtain a laminate as a model sample.. The sample was subjeσted to irradiation with eleσtron rays, and then evaluation was σarried out in the same way as above. The results were illustrated as the distributions of gel fraσtion (k) and f) in Fig. 4. The differenσe of the distributions of the gel fraσtion (k) and ( ) under the same dosage depends on the differenσe of the σros¬ slinking effiσienσies of resins on irradiation. In other words, in the sample No. 117 the surfaσe layer is an EVA (having a vinyl aσetate σontent of 13.5% by weight) layer and the distribution traσes the σurve of (?) . In the sample No. 141, the EVA having a vinyl aσetate σontent of 10% by weight has a low σrosslinking effiσienσy, so that the gel fraσtion drops down relatively. On the other hand, the intermediate surfaσe layer σomprising EVA having a vinyl aσetate σontent of 15% by weight has a higher σrosslinking effiσienσy, so that the distribution shows a high value. Thus, the sample No. 141 forms the distribution σurve (T) having a σleavage. If suσh a phenomenon is examined from an aspeσt of the σhange of film forming ability by drawing, the failure of film forming ability by drawing in the sample No. 117 will be improved to the maximum by the sample No. 141, as shown in Table 14. A part whiσh has a partial gel fraσtion of 73% by weight and is hardly drawn is present in surfaσe layer of the parison of the sample No. 117, while in the sample No. 141 having the distribution (l) the exσessively σrosslinked part whiσh is hardly drawn is removed. In σonventional art, if the failure of film forming ability by drawing illustrated by the distribution (k)happened, dosage was lowered by σontrolling the irradi¬ ation σondition. But the whole distribution of dosage was also lowered, and σonsequently the gel fraσtion was also lowered. On the other hand, the σreativeness of this invention σonsists in that if the layer σorresponding to the exσessive gel fraσtion is replaσed with a resin having a lower σrosslinking effiσiency, only the excessive crosslinking part σan be removed without levelling down the whole gel reaction. The difference of the crosslinking effect to the same dosage depends oh the relative values of the resins to be used. That is, when an EVA having a vinyl acetate content of 13 - 20% by weight of which PLY (interfacial) adhesive strength is extensively inσreased by irradiation of eleσtron rays are used, a resin having a lower cross¬ linking efficienσy such as specifically an EVA having a vinyl acetate σontent of 10 - 5% by weight, a low density or very-low density linear polyethylene or linear low- density polyethylene, a mixed resin of the two or a sealing resin σomprising three σomponents aσσording to this invention is used. The group of resins having low σrosslinking effiσienσy exhibits very exσellent properties (e.g. thermostability, oil resistanσe, rub resistanσe, toughness and the like) upon σrosslinking σompared with those exhibited by the σrosslinking of the EVA having a vinyl aσetate σontent of 13 - 20% by weight. Based on the teσhniσal aspeσts the σrosslinking resin layer of this invention σomprises two layers having high and low σrosslinking effiσienσy, respeσtively, of whiσh the one having low σrosslinking effiσienσy is used as the outermost surfaσe layer. Referring to the gel fraσtion gradient [y/x] of the sample Nos. 141 and 117, it shows a value of 0.42 in the sample No. 117 and 0.57 in the sample No. 141, beσause the σrosslinking polyolefin type resin layer (II) σomprises two layers having different σrosslinking effiσienσy from each other. Thus, if two layers having crosslinking efficiency are used for the layer (II) , the gel fraction gradient does not exceed a value of 0.63 at the dosage distribution (f) (sample No. 122) shown in Table 2 in Experimental Example 2. Therefore, the film of this invention can be σharacterized in that the gel fraσtion gradient of the layer (II) is 0.6 or less. The partial gel fraσtion [y] of the surfaσe layer in the PVDC layer side in the aforementioned layer (II) is 36% by weight even in the σase of the sample No. 141 in whiσh a resin having a high σrosslinking effiσienσy is used for the intermediate surfaσe layer, at most 40% by weight or less. The sample No. 122 has a partial gel fraσtion [y] of 35% by weight, but the gel fraσtion gradient is 0.6 or more, so that eleσtron rays penetrates into the PVDC layer, whiσh is thus deteriorated. Table 14 Experimental Example 6 This experiment is -intended to distinguish the adhesive strength of an EVA, an ethylene-α-olefin σopolymer resin, three layered of which vinyl acetate con- tents are different from each other and a PVDC, by the irradiating electron rays or not. By means of a σonventional three layered well-known co-extruder equipment, a cylindrical parison having a three layer structure of EVA/PVDC/EVA could be formed by extrusion, an EVA having a vinyl acetate σontent of 15% by weight and a PVDC were fixedly supplied into an extruder for a interior layer and an extruder for a σore layer, respeσtively. In an extruder for an exterior layer were supplied sequentially an ethylene-α-olefin σopolymer resin A5 (very-low density polyethylene: density, 0.900; σrystalline melting point, 115°C; manufaσtured by Sumitomo Chemiσal Co., Ltd.) and EVA's having a vinyl aσetate σontent of 5, 10, 13, 15, 20 and 25% by weight were sequentially supplied. A σo-extruded σylindriσal laminated parison having a flat width of 150 mm and a thiσkness of 30 μ/30 μ/30 μ was extruded and σooled rapidly to be taken out. To this parison was used a ELECTRO CURTAIN® manufaσtured by ENERGY SCIENCE INC.-, described in Table 1, and irradiation with electron rays was conducted at a acceleration voltage of 200 kV and a dosage of 5 Mrad (pattern (σ) in Table 1) . It was left standing for three days at room temperature together with a parison without irradiation for σomparison. After the parison was out out into a flat parison, the adhesive strength of the EVA layer in the exterior layer side and the σore layer was measured by a σonstant speed tensile testing maσhine. The measurement σondition was the sample width of 15 mm, the tensile angle of 180° and 500 mm/min of tensile speed. Fig. 6 illustrates the aforementioned adhesive strengths (g/15 mm width) σlassified by irradiating eleσtron rays or not, to the vinyl aσetate σontent of the resin used. The axis of absσissa in the right side is σrystalline melting point, and the value of the used resin and σatalogue values of used resins and two others (measured by the DSC method) are illustrated. One of these two resins are "a low density polyethylene resin An (density, 0.920; σrystalline melting point, 108°C) , and the other is an ethylene-α-olefin σopolymer resin A3 (linear low density polyethylene: density, 0.923; σrystalline melting point, 122°C; trade name, Dowlex; manufaσtured by DOW CHEMICAL CO.) . The solid line in the graph illustrates the adhesive strength of the PVDC layer and the adjaσent layer in the σylindriσal surface side. The empty marks mean the case without irradiation of eleσtron rays. The blaσk-painted marks mean the σase with irradiation of eleσtron rays. Empty σircles O illustrate the values of EVA, and empty squares □ illustrate the values of the ethylene-α-olefin copolymer resin. Empty triangles Δ and chain line illustrate the σrystalline melting points of respeσtive resins. The differenσe of the empty σirσles O and blaσk-painte σirσles β in Fig. 6 represents the inσrease of the adhesive strength with the PVDC layer at folding part by σrosslinking. Generally, σrosslinking effiσienσy under the σonstant dosage is σonsidered to be in propor¬ tion to the vinyl acetate content. Acσordingly, in the relationship in Fig. 6, the phenomenon of inσreasing the adhesive strength in the region of the vinyl aσetate σontent of 13% by weight or more may be antiσipated. However, it was extraordinarily found that in the region of lower vinyl aσetate σontent side of less than 13% by weight the adhesive strength was remarkably inσreased, whiσh σorresponded to the value exhibited by the unσros- slinked EVA having a vinyl aσetate σontent-of about 13 - 20% by weight. Moreover, also in an ethylene-α-olefin σopolymer resin (having a vinyl acetate content of 0% by weight) whiσh will not usually adhere substantially to PVDC adhesive strength as high as in the EVA having a vinyl aσetate σontent of about 13% by weight σould be obtained. (See the symbol 18 in Fig. 6) Experimental Example 7 This experiment is intended to explain the effeσt of dosage of eleσtron rays on the adhesive strength at the bonding part of the PVDC layer and the adjaσent layer thereof when a σrosslinking layer is provided without deterioration of the PVDC layer by the irradiation of electron rays. The methods for σonstruσting the σrosslinking layer without deteriorating the PVDC layer inσlude methods ( ) irradiating after σo-extrusion with a modified^, non-sσanning type electron beam irradiating apparatus, as shown in Experimental Example 1 of this invention, and (i) extra-die laminating by melt-extruded coating method after ' irradiating electron rays in aσσordanσe with the method of Fig. 1 of US Patent No. 3,741,253. In this experiment, as the method ( ) , a parison σomprising three layers was extruded by the three extruders 1 - 3 in Fig. 5, drawn out at a speed of 3 m/min to make a cylindrical parison having a flat width of 130 „ mm. The parison has a construσtion sequentially from the exterior side of EVA (having a vinyl aσetate σontent of 10% by weight)/PVDC (a vinylidene σhloride-vinyl σhloride σopolymer resin having a σomonomer σomponent derived from the vinyl σhloride monomer in the resin in an amount of 17% by weight)/EVA (having a vinyl aσetate σontent of 15% by weight) with a thiσkness of 275 μ/65 μ/390 μ. The parison was irradiated with eleσtron rays by an electron beam irradiating apparatus 8. The eleσtron beam irradi¬ ating apparatus and dosing σondition used are listed in Table 13. The σrosslinked parison as heated to a temper- ature of 80°C in a heating bath 17, then subjeσted to in¬ flation bi-axial orientation to three times maσhine direσ¬ tion and four transverse direσtion wide, and the film hav- " ing a flat width of 520 mm and an average thiσkness of 61μ was formed in a length of 200 m and rolled round a bobbin ' . For σomparison, a film was also prepared without irradiation. The sample Nos. 142 and 143 listed in Table 13 showed somewhat diffiσulty for the start-up of drawing. As the method ( ) , a σylindriσal EVA (having a thiσkness of 275 μ and a vinyl aσetate σontent of 10% by weight) was first prepared, and the parison was irradi¬ ated with an eleσtron beam irradiating apparatus and dosing σondition listed in Table 13. Immediately after irradiation, a PVDC layer and an EVA layer were laminated with the parison in aσσordanσe with the method illust¬ rated in Fig. 1 of Japanese Patent Appliσation Publi¬ cation No. 43024/83 to make a cylindrical parison having the layer construσtion from the exterior side of EVA (having a vinyl aσetate σontent of 15% by weight)/PVDC (a vinylidene σhloride vinyl σhloride copolymer resin, in which the σontent of the σomonomer σomponent derived from the vinyl σhloride monomer in the resin is 17% by weight)/EVA (having a vinyl aσetate σontent of 15% by weight) with a thiσkness of 390 μ/65 μ/275 μ and a flat width of 130 mm. Then, the σylindriσal parison was subjeσted to inflation bi-axial orientation treatment in the same manner as in ( ) to make a film. A further film was prepared for σomparison without irradiation. The sample Nos. 147 and 148 listed in Table 13 showed some¬ what difficulty for the start-up of drawing. Each sample was left standing while rolled round the bobbin for three days at room temperature, then the adhesive strength between the crosslinked EVA layer and the PVDC layer was measured over all width of the cylindriσal film with a σonstant speed tensile testing maσhine. The measurement was σarried out under the σonditions of a sample width of 20 mm, a tensile angle of 180° and a tensile speed of 500 mm/min. Fig. 8 illustrates the adhesive strength measured above (g/20 mm width) plotted to the dosage of eleσtron rays separately for the irradiation methods of (T) and (2 , in whiσh empty σirσles O represent the σase of this invention and blaσk-painted σirσles © represent the σase of σonventional well-known method. Table 13 Example, Comparative Example 1 Following experiment was σarried out to explain the appropriate σonstruσtions of layer and thiσkness for obtaining the film of this invention. That is, the appa- f ratus (and the method) illustrated in Fig. 5 as used, and twenty-eight kinds of films (sample Nos. 1 - 28) having the layer σonstruσtions and the gel traσtions whiσh are shown in the items (see Tables 6-A and 6-B) "layer σon¬ struσtion of film" and "gel fraσtion of crosslinked poly- olefin type resin layer", respectively, were formed. Films were prepared in the same manner as in Experimental Example 1 in Fig. 5. First of all, a parison was formed with four extruders 1 - 3' for the • sample Nos. 1 - 12, 14 - 16, 22 and 28; five extruders » for the sample Nq_. 13; three extruders 1 - 3 for the sample Nos. 17 - 21, 23 - 27; and four layer extrusion was carried out for the sample Nos. 19 and 23, and five layer extrusion was σarried out for all other samples. The modified non-sσanning type eleσtron beam irradiating apparatus whiσh as used in Experimental Example 1 was used as the electron beam irradiating apparatus, in whiσh aσσeleration voltage was σontrolled based on the prelimi¬ narily σalibrated relationship of aσσeleration voltage and dosage distribution (depth) regarding the thickness of the polyolefin type resin layer (I) of each parison so that the dosage will be zero at around the σenter of the PVDC layer. For example, in the sample Nos. 1 and 3 having the same total parison thiσkness of 720 μ, the thiσkness of the polyolefin type resin layer (I) is 120 and 300 μ, respectively, and thus acceleration voltage was adjusted to 150 kV and 200 kV, respeσtively. After σrosslinking, all samples were subjeσted to inflation bi- axial orientation treatment to σa. 3 times maσhine direσtion and σa. 4 time transverse direσtion to form a film having a presσribed layer thiσkness. These films were left standing while rolled round the bobbin for 7 days at room temperature, and then evaluation was σarried out by the methods mentioned herein referring to film forming ability by drawing, heat shrinkability, retention faσtor of oxygen barrier pro¬ perty after rough treatment under severe σondition, heat resistanσe and oil resistanσe (on exterior surfaσe and dint) , falling bag resistanσe at low temperature and heat resistanσe of film. The results are listed in the σolumns of results in Tables 6-A and 6-B. The results in Tables 6-A and 6-B indiσate the followings. That is, the sample Nos. 1 - 5 relate to an appropriate thiσkness of "σrosslinking polyolefin type resin" at the surfaσe layer and the sample Nos. 6 - 9 relate to an appropriate σrosslinking degree (gel fraσ¬ tion) of the resin. Aσσording to the results listed, the σrosslink- ing polyolefin type resin layer requires a thiσkness in a proportion of 25% or more to the total thiσkness (sample No. 2) and a gel fraσtion in a proportion of 20% or more (sample No. 7). However, if the thiσkness is 40 μ or more (sample No. 5) , the proportion to the total thiσk¬ ness exceeds 65%. The σrosslinking polyolefin type resin layer affeσts the other layer σomponents, and thus soft feeling was deσreased because of the decrease of falling bag resistance at low temperature. Further, if the average gel fraction degree is 65% or more (sample No. 9) , film forming ability by drwing is deteriorated. The sample Nos. 3, 17 to 19 and 24 to 28 relate to the resin component of the σrosslinking polyolefin type resin layer. By observing the results obtained from these samples, it is understood that a polyolefin type resin an ethylene-α-olefin σopolymer resin and an EVA σan be used as an σomponent of the σrosslinking polyolefin type resin layer. In the σase of the ethylene-α-olefin σopolymer resin, all of the resins having a density of 0.894 and a σrystalline melting point of 113°C (sample No. 25) and having a density of 0.923 and a σrystalline melting point of 122°C (sample No. 28) exhibit good physiσal properties, and thus it appears that the so- σalled very-low density polyethylene, linear low density polyethylene or low density polyethylene σan be used. To be noted herein is the performanσe of the sample No. 19. As apparent from the sample No. 23, the PVDC and the ethylene-α-olefin σopolymer resin are less adhesive to eaσh other, and thus the film performanσe is deσreased on using them in an adjaσent position to eaσh other in a laminated film. On the other hand, in the sample No. 19, adhesive strength is improved by the irradiation of this invention as desσribed in.Experimental Example 6. The vinylidene σhloride type resin layer is generally required for maintaining a level of gas barrier property in a thiσkness of at least 4 μ. However, the thiσkness beσomes 15 μ or more (sample No. 11) , it beσomes diffiσult to maintain falling bag resistanσe at low temperature. The sample Nos. 3, 10, 17 and 20 - 22 relates to an appropriate thiσkness (upper limit) of the sealing resin layer. It is generally σonsidered that the sealing resin layer requires a thiσkness of at least 3 μ to serve as an oil resistant sealing layer. However, the upper limit is at most 40% (sample No. 21) of the total thiσk¬ ness. If it reaσhes 50% (ample No. 22) , drawing ability is deteriorated and heat shrinkability σannot be inσreased. As for the resin components of the sealing resin layer, explanation is conduσted in detail in Example, Comparative Example 2. By observing the sample Nos. 3, 17 and 24 to 27, it is understood that the ethylene- -olefin σopolymer resin or the mixed resins σontaining said resin as a main σomponent exhibit good physiσal property. This kind of film is generally used in a thiσkness of 40 μ (sample No. 15) to 80 μ (sample No. 16) . If it is thinner than the lower limit, it laσks durability as a paσkage. If it is too thiσk, film forming ability by drawing is deteriorated and besides it laσks eσonomy. The sample Nos. 17 to 21, 23 to 27 are advant¬ ageously prepared eσono iσally by using three extruders. Among them, the sample Nos. 17, 18, 20 and 24 to 27 are σonsidered ^o be a film having exσellent performanσe and .high eσonomy. As the result for the thiσkness σonstruσtion, it is preferred that in the film of this invention in whiσh the layer σomponents are a σrosslinking polyolefin type resin layer/a σore layer/a adhesive shrinkable resin layer/a sealing resin layer and the total thiσkness is in the range of 40 - 80 μ, the σore layer has a thiσkness in the range of 4 μ or more and less than 15 μ, the sealing resin layer has a thiσkness of 4 μ or more but 40% or less of the total thiσkness, the σrosslinking polyolefin type resin layer having a gel fraσtion of 20 - 65% has a thiσkness in a proportion of 25% - 65% to the total thiσkness, and the balanσe with the adhesive shrinkable resin layer. Films having suσh a layer σonstruσtion is exσellent in film forming ability by drawing, heat resistanσe and oil resistanσe and tough, and readily maintains heat shrinkability. The sample No. 28 is a film, in whiσh on the outermost layer a resin having a higher σrystalline melting point than the sealing resin layer and σrosslink- ing treatment was σonduσted so as to improve the heat resistanσe on the outermost layer. Table 6-A Cont'd - Table 6-A (Cont ' d ) Gel fraσ¬ tion of Evaluation result σrosslink¬ ing poly¬ Film Heat Retention rate Oil resistanσe olefin forming shrink¬ of oxygen gas at high tem- type resin ability ability barrier pro¬ perture layer by perty after (% by drawing rough treat¬ Exterior weight) ment under se¬ surface dint vere σondition 30 o o X © X 36 o o o © o 40 © © © © © 37 © © © © <Q) 35 © © o © © 10 o o Δ X X 20 o o o o o 60 © © © © © 65 X © o © © 38 ® © © © © 35 © o o © © 38 © © © © © 38 o © © © © 37 © © © © © 38 ® © o © © 33 o © © © Cont' d - Table 6-A (Cont'd) Note EVAl: Vinyl aσetate σontent, 10% by Falling Heat weight; bag re¬ resist¬ EVA2: Vinyl aσetate σontent, 15% by sistanσe anσe of weight; at low film tempera¬ EVA3: Vinyl aσetate σontent, 20% by ture weight; EEA: Ethylene-methyl acrylate copolymer resin, ethyl acrylate o o content, 7% by weight; PVDCl: Vinylidene chloride-vinyl σhloride σopolymer resin, in © © whiσh a σomonomer σomponent derived from the vinyl chloride monomer in the resin is in an © © amount of 17% by weight; PVDC2: Vinylidene chloride-methyl o © acrylate copolymer resin, in whiσh a σomonomer σomponent - derived from the methyl aσrylate X monomer in the resin is in an . @ amount of 10% by weight. o Δ Blend σomposition 1: Mixture of ethylene-α-olefin © © σopolymer resin (density, 0.920; σrystalline melting © © point, 120°C), trade name -ULTZEX manufaσtured by o © MITSUI PETROCHEMICAL INDUSTRIES, LTD. /EVA2/ ethylene-α-olefin σopolymer © © elastomer (density, 0.88; Vicat softening point, <40°C), trade name TAFMER Δ ® manufactured by MITSUI POLYCHEMICAL CO. = 80/10/10 © , © © © © © o © ■ © © Table 6-B Layer σonstruσtion of σylindriσal film (thiσkness μ) Exterior layer-*=——Interior layer Sample Outermost Intermediate Adhesive Sealing No. layer of surfaσe shrink¬ resin σrosslink- layer of PVDC able layer ing type σrosslinking layer resin resin polyolefin layer layer I type resin layer II 17 A4 EVA2 (10) (15) 18 A4 EVA2 EVA2 A4 (20) (5) (21) 6) 19 A4 No layer PVDCl (25) (8) 20 I EVA2 EVA2 A4 (15) (12) (15) 21 A4 EVA2 EVA2 A4 (10.) (13) (5) (24) 22 EVA2 EVA2 A6 (7) (5) (30) 23 EVA2 No A4 (18) layer (24) 24 A5 A5 (10) (6) 25 A6 A6 (10) (6) 26 Blend com¬ EVA2 EVA2 Blend σo - position 2 (15) (21) position 2 (10) (6) 27 Blend com¬ Blend com¬ position 3 position 3 (10) (6) 28 A3 A5 (10) : 6 ) - Cont'd - Table 6-B (Cont ' d ) Gel frac¬ tion of Evaluation result crosslink¬ ing poly¬ Film Heat Retention rate Oil resistance olefin forming shrink¬ of oxygen gas at high tem- type resin ability ability arrier pro¬ perture ' layer by perty after (% by drawing rough treat¬ Exterior weight) ment under se¬ surface dint vere σondition 38 © © © © © 37 © © © © © 35 © © © © 40 © © © © 39 © © © 38 © © © 40 x © © 36 © © © © © 39 © © © © © 38 © © © © © 40 © © © © © 39 © © © © © - Cont'd - Table 6-B (Cont ' d) Note Al: Ethylene-α-olefin copolymer resin Falling Heat (density, 0.920; crystalline melt¬ bag re¬ resist¬ ing point, 120°C) , trade name sistance ance of ULTZEX manufactured by MITSUI at low film PETROCHEMICAL INDUSTRIES, LTD. tempera¬ ture A3: Ethylene-α-olefin copolymer resin (density, 0.923; crystalline melt¬ ing point, 122°C) , trade name © © DOWLEX manufactured by DOW CHEMI¬ CAL CO. © ® A4: Ethylene-α-olefin copolymer resin (density, 0.906; crystalline melting point, 118°C) , trade name © © NUCFLX manufaσtured by NIPPON UNICAR CO. © A5: Ethylene-α-olefin σopolymer resin (density, 0.900; σrystalline melting point, 115°C) , trade name © EXCELLENT VL manufaσtured by SUMITOMO CHEMICAL CO., LTD. © A6: Ethylene-α-olefin σopolymer resin (density, 0.894; crystalline melting point, 113°C), trade name © NIPOLONL manufactured by TOYO SODA CO. , LTD. © © Blend composition 1: Mixture of A4/A5 = 50/50; © © Blend composition 2: Mixture of A4/A1 = 70/30; © © EVA2: Vinyl acetate content, 15% by weight; PVDCl: Vinylidene chloride- inyl © © chloride σopolymer resin, in whiσh a σomonomer component derived from the vinyl chloride monomer in the resin is in an amount of 17% © © by weight. *1 In falling bag test, sealing parts in all bag samples were in ply separation between the PVDC layer and the inner layer. Example, Comparative Example 2 For this invention, experiment was conduσted in order to speσifiσally explain the σomponent and σomposition of the sealing resin layer whiσh is as significant as the σrosslinking polyolefin type resin layer. That is, the basiσ σonstruction of the film is designed as shown below using a film which was prepared from the sample Nos. 3, 17 and 24 to 28 used in Example, Comparative Example 1, and an apparatus illustrated in Fig. 5 in the same manner as in Example, Comparative Example 1. Samples σomprising the resins listed in the item of "resin σomponent of sealing resin layer" in Table 7-B as the σomponent resin at the part of the sealing resin layer (sample Nos. 29 to 51) were used in experi¬ ment. The laminated films used in the experiment were 30 kinds in total. Crosslinking polyolefin EVA layer having a vinyl resin layer. aσetate σontent of 10%, (gel fraσtion, σa. 40%) 15 μ 25 μ EVA layer having a vinyl aσetate σontent of 15%, 10 PVDC layer (VDC : VC = 87 13) 6 μ EVA layer having a vinyl aσetate σontent of 15%, 23 μ Sealing resin layer 6 μ As for the 30 kinds of films, evaluation was conducted referring to "reduction of defective rate of sealing" and "reduction of time required for sealing" which are the main objects of this invention, and "transparency after shrinking" acσording to the methods desσribed herein. The results are listed in "results of evaluation" in tables 7-A and 7-B. The marks of "synthetiσ evaluation" in Tables 7-A and 7-B represent the grades using the following σriteria from the standpoint of the objeσt (effeσt) of this invention. © : © of all three items; Q : inσluding the grade O referring to at least one item (other may be in the grade Q or©) ; Δ : inσluding " the grade Δ referring to at least one item (other may be in any grade) ; x : inσluding the grade referring to at least one item (other must be in any grade) In Table 7-A, most of the sealing resin layers σomprise an ethylene-α-olefin σopolymer resin, and in Table 7-B, most of the sealing resin layers σomprise mixed resins whiσh σontain an ethylene-α-olefin σopolymer resin as a main σomponent. Ethylene-α-olefin σopolymer resins inσluding those having a density of 0.89 and a σrystalline melting point of 113°C (sample Nos. 24, 28) and a density of 0.923 and a σrystalline melting point of 122°C (sample t No. 38) show excellent physical properties, so that it appears that the so-called very-low density polyethylene, linear low density polyethylene and low density polyethylene can be used. For the purpose of ready understanding of the mixing ratio of an ethylene-α-olefin copolymer elastomer a.nd the EVA of the mixed resin in whiσh the ethylene-α- olefin σopolymer resin is σontained as a main σomponent, Fig. 7 is appended. This figure is an analytiσal diagram of Table 7-A and 7-B, in whiσh the marks of synthetiσ evaluation are plotted on the positions of the σomponents of the sealing resin of the film. Fig. 7 illustrates by spatial restriσtion only the parts whiσh σan be repre¬ sented by the three σomponents of the ethylene-α-olefin σopolymer resin, the ethylene-α-olefin copolymer elastomer and the ethylene-vinyl acetate copolymer. According to the results obtained from Fig. 7, the composition of the sealing resin layer for satisfying the aforementioned object of this invention is an ethylen-α-olefin σopolymer resin (resin A) having a density of 0.93 and a σrystalline melting point of 110 - 130°C, a mixed resin whiσh σomprises 60% by weight or more of aside resin A and 40% by weight or less of an ethylene-α-olefin σopolymer elastomer (resin B) or a mixed resin whiσh comprises 40% by weight or more of said resin A, 5 -40% by weight of said resin B and 55% by weight or less of an ethylene-vinyl acetate copolymer resin (resin C) , in which the total amount being 100%. To be noted is sample No. 28, in whiσh on the outermost surfaσe is arranged a resin having a σrystal¬ line melting point higher than that of the sealing resin layer (the resin at the outermost layer of the σrosslink- ing polyolefin type resin layer: σrystalline melting point, 122°; the resin at the sealing resin layer: σrystalline melting point, 115°C) , and the resin having a higher σrystalline melting point is σrosslinked to improve heat resistanσe. Aσσordingly, the sealing performanσe is remarkably improved. Table 7-A Note Al: Ethylene-α- -olefin copolymer resin (density, 0.920; crystalline melting point, 120°C) trade name ULTZEX manufactured by MITSUI PETROCHEMICAL INDUSTRIES, LTD. A2: Ethylene-α- -olefin copolymer resin (density, 0.920; crystalline melting point, 120°C) trade name ULTZEX manufactured by MITSUI PETROCHEMICAL INDUSTRIES, LTD. A3: Ethylene-α- -olefin copolymer resin (density, 0.930; crystalline melting point, 122°C) trade name DOWLEX manufactured by DOW CHEMICAL CO. A4: Ethylene-α- -olefin copolymer resin (density, 0.906; crystalline melting point, 118°C) trade name NUCFLX manufactured by NIPPON UNICAR CO. A5: Ethylene-α- -olefin copolymer resin (density, 0.900; crystalline melting point, 115°C) trade name EXCELLENT VL manufactured by SUMITOMO CHEMICAL CO., LTD. - Cont'd - Table 7-A (Cont'd) A6: Ethylene-α-olefin copolymer resin (density, 0.894; crystalline melting point, 113°C) trace name NIPOLON L manufactured by TOYO SO 'DA CO., LTD. Bl: Ethylene-α-ole in copolymer elastomer (density, 0.88; VSP, 40°C or less; C2: EVA having a vinyl acetate content of 15% by weight. *1 Reject rate was zero. *2 Reject rate was zero even if cooling time was reduced to zero second. Example, Comparative Example 3 As for 6 kinds of laminated films of the sample Nos. 17, 28, 29, 32, 33 and 344, evaluation was carried out referring to oil resistance of interior surfaσe at high temperature. The results are listed in Table 8. According to the results listed in Table 8, it is understood that the film sample Nos. 17, 28, 29, and 32 to 34 are films of which interior ' surface is excellent in oil resistance at high temperature. Therefore, this kind of the films is useful for packaging the processed meat such as reσeiving a fatty σontent in a σylindriσal film and subjecting to sterilizing treatment at high temperature. Table 8 (referential) Sample No. Oil resistance of Transparency after interior surface shrinking 17 © © 28 @ © 29 © Qr 32 © © 33 © © 34 © . © Table 7-B Resin composition of sealing resin layer Evaluation result Sample No. Resin used iBlendin Reject Reduction Trans¬ g ratio, %) rate of required parency Synthet sealing for seal¬ af er ic eval ing shrinking uation 29 A l (100) - - © o o o 30 2 (100) - - © © © © 31 A 4 (100) - - © © © © 32 (95) A l B l (5) - © o © o 33 , (80) B l (20) - ® ® © © 34 A ι (80) B l (10) (10) C l © © © © 35 , (80) B l (10) C l (10) © © © © 36 A l (70) (5) B l C 2 (25) © o o o 37 (60) B l (40) - o © © o 38 A 3 (60) B l (30) C 2 (10) © © © © 39 A l (60) B l (20) C 2 (20) © © © © 40 A l (50) B l (30) C 2 (20) . © © © © 41 (50) A 3 B l (10) C l (40) © © © © 42 A l (40) B l (40) C 2 (20) o © © o 43 A l (40) B l (5) C 2 (55) o © © o 44 A l (85) - C 2 (15) © o X X 45 A l (60) - C 2 (40). o o X X - Cont ' d - Table 7-B (Cont'd) Note Al: Ethylene-α-olefin copolymer resin (density, 0.920; crystalline melting point, 120°C) , trade name ULTZEX manufactured by MITSUI "PETROCHEMICAL INDUSTRIES, LTD. A2: Ethylene-α-olefin copolymer resin (density, 0.906; crystalline melting point, 118°C) , trade name NUCFLX manufactured by NIPPON UNICAR CO. A3: Ethylene-α-olefin copolymer resin (density, 0.923; crystalline melting point, 122°C) , trade name DOWLEX manufactured by DOW CHEMICAL CO. A4: Ethylene-α-olefin copolymer resin (density, 0.89; crystalline melting point, 116°C) , trade name NUCFLX manufactured by NIPPON UNICAR CO. Bl: Ethylene-α-olefin copolymer elastomer (density, 0.88; VSP, 40°C or less; Cl: EVA having a vinyl acetate content of 10% by weight. C2: EVA having a vinyl acetate content of 15% by weight. Dl: Ethylene-propylene copolymer resin having an ethylene content of 3.5 molar % (density, 0.90; crystalline melting point, 134°C) . El: High density polyethylene (density, 0.953; crystalline melting point, 127°C) . Example, Comparative Example 4 As for the sample Nos. 17, 28, 36 to 43 and 45 to 49, evaluation as carried out referring to shrink¬ ability at low temperature, oil resistance on interior surfaσe II and transparenσy of film aσσording to the methods desσribed herein. The results are listed in Table 9. Aσσording to the results shown in Table 9, it is understood that films in the groups of the sample Nos. 17, 28 and 36 to 42, partiσularly the sample Nos. 17, 28, 36, 38 to 42 are films exσellent in sh inkability at low temperature as well as other properties. Aσσordingly, these films are those whiσh are useful for reσeiving a fatty σontent in a σylindriσal film, heat shrinking extensively the film at a low temperature where the σontent will not be denaturated and forming an attraσtive tight paσkage of raw meat. Table 9 Example, Comparative Example 5 In the apparatus (method) illustrated in Fig. 5, three extruders were respeσtively arranged for the following resins: for σore layer (one extruder) ; PVDC (vinylidene σhloride-vinyl σhloride σopolymer σomprising a σomonomer σomponent derived from the vinyl σhloride monomer in the resin in an amount of 7% by weight) , for intermediate surfaσe layer of the σrosslinked polyolefin type resin layer and adhesive shrinkable resin layer (one extruder) ; an ethylene-vinyl aσetate σopolymer resin having a vinyl aσetate σontent of 15% by weight, the sealing resin and the outermost layer σrosslinking resin layer (one extruder) ; [a mixed resin σomprising an ethylen-α-olefin σopolymer resin having a density of 0.923 and a σrystal¬ line melting point of 122°C, (trade name, DOWLEX, manu¬ faσtured by Dow Chemical Co.) in an amount of 80% by weight, an ethylene-α-olefin copolymer elastomer (trade name, TAFMER, manufaσtured by MITSUI POLYCHEMICAL CO.) in an amount of 10% by weight and an ethylene-vinyl aσetate σopolymer resin having a vinyl aσetate σontent of 15% by weight in an amount of 10% by weight. A σylindriσal laminated film having a layer σonstruσtion illustrated in the sample No. 52 in Table 10 and a gel fraσtion of 36% by weight was aσσomplished. In the same time, σommerσially available films G (manufaσtured by G Co.) and K (manufaσtured by K Co.) were obtained, of whiσh layer σonstruσtion is listed in Table 10. These samples were evaluated together with the representative film sample Nos. 17, 28, 34 and 39 of this invention prepared in Example, Comparative Examples 1 and 2 with referenσe to substantially all of the evaluation methods desσribed herein to examine synthetically the film properties of this invention in the field of application. The results are listed in Table 1. Acσording to the result listed in Table 11, it σan be appreσiated that the films of this invention are superior to σommerσially available films in all evalu¬ ation items and particularly excellent in heat seal- ability which is useful for improving the packaging efficienσy. For the appliσation whiσh requires high temperature oil resistanσe there σan be used the films of the sample Nos. 34 and 52, and for the application which requires heat shrinkability at lower temperature at high level, there can be selected the film of the sample No. 39. Further, the films of the sample Nos. 17 and 28 have both said heat shrinkability and high temperature oil resistance, so that they are convenient films whiσh σan be used for paσkaging either raw meat or proσessed 'meat. Thus, the film performanσe of this invention σan be appreσiated more prominent. Moreover, aσcording to this invention, a film having a five-layer structure and excellent .properties can be advantageously prepared by using three extruders with an appropriate selection of layer construσtion. Table 10 Sample Layer construction of cylindrical film No. Exterior layer -ε =~- Interior layer Crosslinking*! 17 A 4 /EVA(Vac. 15%) λ /PVDC 1 /EVA(Vac. 15%) /A 4 10 μ/ 15 μ / 8 μ / 21 μ /6 μ Crosslinking ^ 28 A 3 /EVA(Vac. 15%) /PVDC 1 /EVA(Vac. 15%) /A 10 μ/ 15 μ / 8 μ 21 μ / 6 μ Crosslinking ^ 39 EVA(Vac. 10%) /EVA(Vac. 15%) /PVDC, /EVA (Vac. 15%) 15 μ / 10 μ / 6 μ / 23 μ / 6 μ Crosslinking*4 34 EVA (Vac. 10%) /EVA (Vac. 15%) /PVDC^EVA (Vac. i5%)/ B si 1 t n i d on 15 μ / 10 μ / 6 μ / 23 μ / 6 μ Crosslinking J 52 Blend compo s 15%) /PVDC, /EVA (Vac. 15%) / Bl nd c sition 4 1 sition i* Cont'd - Table 10 (Cont'd) Commer- tially Crosslinkinq 6 avail¬ able EVA (Vac. 10%) /PVDC/EV (Vac. 10%) film G 15 μ / 10 μ / 35 μ Commer- tially EVA (Vac. 10%) /EVA (Vac. 15%) /PVDC/EVA (Vac. 15%) /lONOMER avail¬ 15 μ / 2 μ / 8 μ / 2 μ / 34 μ able film K - Cont ' d - Table 10 (Cont'd) 41 (part of *6) Table 11 Cont'd Table 11 (Cont'd) •^ Measured in accordance with ASTMD 3985; 2 unit; cc/ .24 hrs.atm. (at 23°C) INDUSTRIAL APPLICABILITY As explained above, this invention aσσomplished for the first time a σo-extruded σylindriσal laminated film having a surfaσe σrosslinking resin layer whiσh was irradiated with eleσtron rays. This σrosslinking resin layer improves film forming ability by drawing during the produσtion proσess and also improves as a resin layer the heat resistanσe, oil resistanσe, rub resistanσe, tough¬ ness and the like, to improve the whole properties of the film. In addition, the σrosslinking resin layer leads to the firm bonding with the σore layer. Partiσularly, in the film of this invention there are arranged a heat resistant σrosslinking resin invention there are arranged a heat resistant σrosslining resin and a sealing resin layer of a seleσted resin at the surfaσe layer and the innermost layer, respeσtively, so that as a σombination effeσt thereof great effeσt is exhibited for the reduσ- tion of the sealing time whiσh serves for improving the paσkaging ability and the elimination of defective rate at sealing part. This effect leads to settlement of the most serious problem in the art of packaging, and thus this invention is very useful to industry.

Claims: CLAIMS 1. A heat shrinkable σylindriσal laminated film having a polyvinylidene σhloride type resin (I) as an oxygen gas barrier σore layer on the both surfaσe sides of whiσh 1 or 2 resin layers are arranged respeσtively and σonsisting of 3 - 5 layers with total, σharaσterized in that the σylindriσal exterior surfaσe resin layer on said layer (I) σomprises a σrosslinked polyolefin type resin layer (II) having a gel fraσtion [x] at the outer¬ most layer of 25 -70% by weight, a gel fraσtion [y] at the surfaσe layer in the side of the layer (I) of 40% by weight or less and a gradient of gel fraction represented b y [ /x] of 0.6 or less and the joint of said layers (I) and (II) σomprises a laminate of a joint in a state denaturated by electron rays. 2. A laminated film acσording to Claim 1, wherein the average gel fraσtion of the crosslinked polyolefin type resin layer (II) is in a range of 20 - 60% by weight and the thiσkness of the layer is in a proportion of 25 - 65% to the total thiσkness of the film. 3. A laminated film aσσording to any one of Claims 1 or 2, ' wherein the σrosslinked polyolefin type resin layer (II) σomprises two resin layers, the σrosslinking effiσienσies of whiσh are different from eaσh other, and has a two layer struσture in whiσh one of the resin layers having a lower σrosslinking efficienσy is arranged as an outermost layer. 4. A laminated film aσσording to Claim 1, wherein a sealing resin layer (IV) is arranged through the adhesive shrinkable resin layer (III) in the interior surface side of said -layer (I) of the σylinder. 5. A laminated film aσσording to Claim 4, wherein said adhesive shrinkable resin layer (III) is an ethylene-vinyl aσetate σopolymer resin having a vinyl aσetate σontent in the range of 13 - 20% by weight. 6. A laminated film aσσording to Claim 4, wherein said sealing resin layer (IV) is any one of the resin layers of an ethylene-α-olefin σopolymer resin (resin A) having a density of 0.88 - 0.93 and a σrystalline melting point of 110 - 130°C, a mixed resin σomprising 60% by weight or more of said resin A and 40% by weight or less of an ethylene-α-olefin σopolymer elastomer (resin B) or a mixed resin σomprising 40% by weight or more of said resin A, 5 -40% by weight of said resin B and 55% by weight or less of an ethylene-vinyl aσetate σopolymer resin (resin C) , in whiσh the perσentages of the σomponents in said mixed resins amount to 100% in total. 7. A laminated film aσσording to Claim 1, wherein said σrosslinked polyolefin type resin layer (II) σom¬ prises any one of an ethylene-α-olefin σopolymer resin (resin A) having a density of 0.88 - 0.93 and a σrystal¬ line melting point of 110 - 130°C or an ethylene-vinyl aσetate σopolymer resin (resin D) , and the σonstruσtion thereof is a single layer of the resin A or the resin D, a double layer σombined with the resin- D, or a σombination of two layers in whiσh the outermost surfaσe layer σonsists of the resin A and the inner surfaσe layer σonsists of the resin D. V 8. A laminated film aσσording to Claim 1, wherein said polyvinylidene σhloride type resin layer (I) is a vinylidene σhloride-vinyl σhloride σopolymer resin having a σontent of the vinyl σhrolide σomponent as a σomonomer of 10 - 25% by weight. 9. A laminated film aσσording to Claim 1, wherein said polyvinylidene σhloride type resin layer (I) is a vinylidene σhloride-methyl aσrylate σopolymer resin having a σontent of the methyl aσrylate σomponent as a σomonomer of 3 - 15% by weight. 10. A laminated film aσcording to Claim 4, wherein in both of the crosslinked polyolefin type resin layer (II) and the sealing resin layer (IV) , the same resin selected from the resins of the sealing resin layer is arranged. 11. A laminated film acσording to Claim 4, wherein in both of inner surfaσe layer of the σrosslinked poly¬ olefin type resin layer (II) and the adhesive shrinkable resin layer (III) , an ethylene-vinyl aσetate σopolymer resin is arranged. 12. A laminated film aσσording to Claim 4, wherein the laminated film has a thiσkness of 40 - 80 in total, the σore layer (I) having a thiσkness of 4 -15 μ , the adhesive resin layer (IV) having a thiσkness of 4 μ or more and 40% or less in proportion to the total thiσkness, the σrosslinked polyolefin type resin layer (II) having a thiσkness of 25 - 65% in proportion to the total thiσkness and the sealing shrinkable resin layer (III) having a thiσkness of balanσe. 13. A laminated film aσσording to Claim 4, wherein the laminated film is used for heat shrinkable paσkaging of the σontent of a fatty irregularly shaped food. 14. A laminated film aσσording to any one of Claims 1 or 4, wherein the laminated film is a σo-extruded and seamless σylindriσal film.

Inventors: ISHIO TADASHI, MATSUMURA DAISUKE, ISHIO, TADASHI, MATSUMURA, DAISUKE
Applicants: ASAHI CHEMICAL IND, ASAHI KASEI KOGYO KABUSHIKI KAISHA
Application year: 1987
Main classification: B65D65
IPC codes: B29C35, B29C47, B29C55, B29C61, B32B27, B65D65, C08J3