CERAMIC SINTERED BODIES AND A PROCESS FOR MANUFACTURING THE SAME

Abstract: High density fine ceramic sintered bodies are disclosed, which have the maximum pore diameter of not more than 10 µm and porosity of not more than 0.5%. A process for producing such high density fine ceramic sintered bodies comprises the steps of mixing a ceramic raw material powder with a sintering aid, grinding the resulting, granulating and shaping the mixture, and firing the shaped body. The granulated powder is once forcedly dried, and as necessary is subjected to addition of water and/or sieved to obtain a uniform granulated powder having a given amount of water.

Description: The present invention relates to high density silicon nitride fine ceramic sintered bodies useful for engine parts, gas turbine parts, mechanical parts, wear resisting slide members, etc., and a process for manufacturing the same. In order to produce ceramic products, it is a conventional practice that as shown in a flow chart of Fig. 5 by way of an example, a ceramic raw material is first mixed with a sintering aid, and the mixture is ground and passed through a sieve of 44 µm to remove foreign matters such as broken pieces of grinding media used for the grinding. Then, after granulating, water is added to the granulated powder at need, and the granulated powder is shaped by a mold press or a cold isostatic press. The shaped body is finally sintered at a given temperature to obtain a sintered product. However, since a positive measure is not taken to uniformly disperse water in the granulated powder in the above-mentioned conventional ceramic product-producing process, an amount of water locally varies in the granulated powder. As a result, pores are formed in shaped bodies due to ununiform particle fracture which is caused by ununiform water distribution in the granulated powder, so that such pores remain in sintered products. Consequently, ceramic sintered bodies having excellent mechanical characteristics cannot be obtained. Particularly, when ceramic sintered bodies are used as bearing members, wear resisting members or slide members, the presence of pores and hardness largely influence the useful life. Thus, in order to obtain ceramic products having longer life than before, it was necessary to produce high hardness ceramic sintered products having a smaller pore diameter and a smaller porosity. For bearing materials, it is known that it is important to pay attention to rolling fatigue life of the materials. Thus, there has been a demand to develop dense, high strength, and/or high hardness ceramic materials to improve rolling fatigue life. It is an object of the present invention to obviate the above-mentioned drawbacks, and to provide dense ceramic sintered bodies having high strength and/or high hardness, as well as a process for producing the same. The sintered body of the invention is set out in claim 1. Preferably, the four point flexural strength at room temperature is not less than 100 kg/mm² (980 MPa) and/or Knoop hardness is not less than 15.5 GPa. The process according to the present invention is set out in claim 8. In order to obtain the silicon nitride sintered bodies, it is preferable that a silicon nitride raw material containing not less than 90% by weight of a-silicon nitride is used and that firing is effected pressurelessly (i.e. under atmospheric pressure). More preferably, an obtained shaped body is preliminarily treated, and then treated by a hot isostatic press (HIP) in a nitrogen atmosphere. In the above process, a uniform granulated powder having no variation in the content of water over the granulated particles can be obtained by once forcedly drying the granulated powder, and at need, adding water and/or passing the granulated powder through a sieve. That is, pores present between the particles can be reduced by attaining a uniformly press-crushed state during shaping through forcedly drying the granulated powder and adding water thereto at need. As a result, when the thus obtained granulated powder is shaped and fired, for instance, as to silicon nitride sintered bodies, high strength and high density ceramic sintered bodies having the maximum pore diameter of not more than 10 µm, porosity of not more than 0.5%, four point flexural strength of not less than 100 kg/mm² (980 MPa) at room temperature, and Knoop hardness of not less than 15.5 GPa can be obtained even by pressureless sintering. These and other optional features and advantages of the present invention will be appreciated upon reading of the following description of embodiments of the invention taken in conjunction with the attached drawings. For a better understanding of the invention, reference is made to the attached drawings, wherein: Fig. 1 is a flow chart illustrating an example of the producing process according to the present invention; Fig. 2 is a graph showing the relation between the four point flexural strength of sintered bodies according to the present invention and the granulated powder-drying temperature; Fig. 3 is a graph showing the relation between the four point flexural strength of sintered bodies the according to the present invention and the amount of water added to the granulated powder; Fig. 4 is a graph showing the relation between the four point flexural strength of the sintered bodies according to the present invention and the sieve opening after grinding; and Fig. 5 is an example of a flow chart of a conventional process for the production of a silicon nitride sintered bodies. In order to obtain silicon nitride sintered bodies according to the present invention, any sintering aid may be used so long as it can make the silicon nitride dense, strong and hard. However, it is preferable to use MgO, ZrO₂, Y₂O₃ and/or a compound of Mg, Zr or Y which is converted to MgO, ZrO₂, or Y₂O₃ by heating, respectively. The reason is that MgO, ZrO₂, Y₂O₃ or the Mg-, Zr- or Y-compound promotes a phase transformation to an elongated or rod-like β-silicon nitride crystals which are advantageous for high strengthening and the Zr compound strengthens an intergranular phase when present in the intergranular phase during the sintering. The reason why it is preferable that the Mg compound is added in an amount of from 0.5 to 15% by weight when calculated as MgO and that the Zr compound is added in an amount of from 0.5 to 13% by weight when calculated as ZrO₂ and that Y compound is added in an amount of from 2 to 15% by weight when calculated as Y₂O₃ is that if they fall outside these respective ranges, the above-mentioned effects are reduced. Further, in the case of silicon nitride pressurelessly sintered bodies, it is preferable that not less than 90% by weight of silicon nitride is β-silicon nitride crystals. This is because if it is less than 90% by weight, it is difficult to attain high strength. The forcedly drying temperature is preferably in a range of from 60 to 100°C. The reason is that if it is less than 60°C, it is difficult to attain a desired dried state, while if it is over 100°C, it is also difficult to attain a uniform press-crushed state of the granulated powder due to hardening of an auxiliary used in spray drying. Furthermore, it is preferable that the ground raw material is passed through a sieve having a sieve opening of not more than 32 µm before granulating or the forcedly dried and water-added granulated powder is passed through a sieve having a sieve opening of not more than 250 µm. The reason is that coarse particles after the grinding and foreign matters contained in the raw materials cannot effectively be removed by using a sieve having a larger sieve opening than the above, so that it is difficult to maintain uniformity of the granulated powder. In addition, the amount of water added to the granulated powder is preferably in a range from 0.5 to 5% by weight. The reason is that if it is less than 0.5% by weight, water may not be uniformly distributed among the granulated particles to cause variation in the water content, while if it is over 5% by weight, water may ooze out from the surface of the shaped body during shaping to cause non-uniform water distribution in the shaped body. The granulation is preferably effected by spray drying. The reason is that granulated powder of which packing density can be increased during the shaping can be obtained thereby. Polyvinyl alcohol (PVA), polyethylene glycol (PEG), methyl cellulose (MC), and stearic acid are preferred as an auxiliary used in the spray drying. The reason is that the granulated powder is difficult to harden or break by forcedly drying it and/or adding water thereto when such as auxiliary is used. It takes a long time to mix and grind a raw powder having the average particle size of more than 2 µm. During such a long time mixing and grinding, there is a possibility that impurities enter the raw material due to wearing during the grinding so that characteristics of the sintered body are deteriorated and an effect of densifying the sintered body is lost. Thus, it is preferable to use fine raw materials having the average particle size of not more than 2 µm and more preferably not more than 1 µm. When the thus obtained shaped body is preliminarily treated and is further treated by hot isostatic press (HIP) in an inert gas atmosphere, higher density, higher strength, and/or higher hardness can be attained. Such treatments are preferable because, for instance, the maximum pore diameter of not more than 10 µm and the porosity of not more than 0.3% can be attained. As an inert gas, nitrogen, argon, or the like is used. Furthermore, it is preferable to use a silicon nitride raw material containing not less than 90%, more preferably, not less than 95% of α-silicon nitride in the production of the silicon nitride sintered bodies, because a sufficient amount of needle-like β-silicon nitride crystals which lead to high strength during sintering are precipitated owing to the α → β transformation. In a HIP sintered body as a preferred embodiment according to the present invention, steps of forcedly drying, shaping, preliminarily treating and hot isostatic press treatment are effected in this order. In this process, the preliminary treatment is broken down into two kinds of: a primary sintering method in which the shaped body is primarily fired and an encapsulating method in which a shaped body is sealed in a capsule. In the primary sintering method of the preliminary treatment, the shaped body is primarily fired, preferably at 1,400 to 1,600°C in an inert gas atmosphere at ordinary pressure. If the firing temperature is less than 1,400°C, open pores do not disappear even after the firing, so that dense sintered bodies cannot be obtained even after the hot isostatic press treatment. On the other hand, if it is more than 1,600°C, decomposition reaction proceeds during sintering, so that dense, high strength, and/or high hardness sintered bodies cannot be obtained even after the HIP treatment, either. Meanwhile, there are two methods for the encapsulating step. That is, a shaped body is sealed in a vacuum-evacuated glass vessel preferably mainly consisting of SiO₂ before the HIP treatment. Alternatively, a shaped body is buried in a glass powder before the HIP, and the glass powder is melted as the temperature rises in the HIP treatment to encapsulate the shaped body. The reason why glass is preferred as an encapsulating material is that glass has more excellent deforming ability and sealability as a capsule during the hot isostatic press treatment. Fig. 1 shows a flow chart of an example of the producing process according to the present invention. First, a ceramic raw material having the average particle size of not more than 2 µm is mixed and ground with a sintered aid, and the thus obtained mixture is passed through a sieve having a sieve opening of, preferably, not more than 32 µm to remove foreign matters and coarse particles such as broken pieces of grinding media used for grinding. Any sintering aid may be used as long as it can densify and strengthen intended ceramic materials. Then, after the mixture is granulated to obtain a granulated powder containing around 1% by weight of water. The granulated powder is sieved similarly in a conventional manner. The resulting granulated powder is forcedly dried, preferably, at a temperature range from 60 to 100°C to obtain a uniform granulated powder containing water at a low variation in an amount of from 0.2 to 0.5% by weight. Next, 0.5 to 5.0% by weight of water is added to the granulated powder at need to obtain the granulated powder having a uniform water content, and a final granulated powder is obtained by removing coarse particles coagulated by the addition of water, with a sieve having a sieve opening of not more than 250 µm. High strength, high density and/or high hardness ceramic sintered bodies having the characteristics of the present invention are obtained by shaping the thus obtained granulated powder in an ordinary manner and firing the resulting shaped body at ordinary pressure. In the following, examples of the present invention will be explained. These examples are merely given in illustration of the invention, but should never be interpreted to limit the scope thereof. Example 1 Into 100 parts by weight of an Si₃N₄ powder having the average particle size of 0.5 µm were added and mixed 3 parts by weight of MgO, 1 part by weight of ZrO₂, 4 parts by weight of CeO₂, and 1 part by weight of SrO as sintering aids. After 60% by weight of water was added to the thus obtained mixture together with grinding media having a diameter of 5 to 10 mm, the mixture was mixed and ground for 4 hours by a batch grinder. Next, the mixed and ground slurry was passed through a JIS standard sieve of a sieve opening of 32 µm, and was added and mixed with 2% by weight of PVA and 0.2% by weight of stearic acid used as auxiliaries in spray drying. Thereafter, a granulated powder having the average particles size of 80 µm and a water content of from 0.5 to 1.0% by weight was obtained by spray-drying. Further, the granulated powder was forcedly dried at a drying temperature shown in Table 1 for 24 hours by using a thermostatic drier, and water was added thereto at need. When water was added, the powder was passed through a JIS standard sieve having a sieve opening shown in Table 1, thus obtaining granulated powders (Sample Nos. 1 to 8). The granulated powder was shaped at a pressure of 3 ton/cm² by cold isostatic press, thereby obtaining a shaped body of 60 mm x 60 mm x 6 mm. Then, after the shaped body was dewaxed at a temperature of 500°C for 3 hours, it was pressurelessly sintered at a temperature of 1,700°C for 1 hour in a nitrogen gas atmosphere, thus obtaining high strength silicon nitride sintered bodies according to the present invention (Sample Nos. 1 to 8). Apart from the above, granulated powders in Sample Nos. 9-11 were prepared as Comparative Example of the present invention under producing conditions shown in Table 1 with no forcedly drying, and were shaped and fired under similar conditions, thereby obtaining sintered bodies. Then, with respect to the thus obtained sintered bodies, flexural strength, maximum pore diameter, and porosity were measured, and measurement results are shown in Table 1. The flexural strength was measured according to a four point flexural strength test method of a fine ceramic flexural strength-testing in JIS R-1601. The maximum pore diameter and the porosity were measured with respect to a mirror-polished surface of the sintered body by means of an optical microscope at a 400 x magnification. The maximum width of a pore was taken as the diameter of the pore, and the maximum diameter of 1,000 pores measured was taken as the maximum pore diameter. With respect to the porosity, the total pore area was determined by actually measuring areas of the above 1,000 pores in the above measurement, and the porosity was determined as a value obtained by dividing the total pore area by a total area as viewed in the measurement. In Table 1 and the other tables herein, strength is given in kg/mm². 1 kg/mm² = 9.8 MPa. As compared with Comparative Examples, it is clear from Table 1 that the sintered bodies according to the present invention using a mixed raw material having been forcedly dried, and added with water and sieved at need, are less porous, excellent sintered bodies having extremely higher strength. Example 2 To α-silicon nitride powder having the average particle size of 0.5 µm were mixed powdery MgO, ZrO₂, and Y₂O₃ as sintering aids at rates of 4% by weight, 3% by weight, and 6% by weight, respectively. After 60% by weight of water was added to the thus obtained mixture together with grinding media of 5 to 10 mm in diameter, the mixture was mixed and ground for 4 hours in a batch grinder. Then, the mixed and ground slurry was passed through a JIS standard sieve of a sieve opening of 32 µm, and 2% by weight of PVA and 0.2% by weight of stearic acid were added to the slurry as spray drying auxiliary, which was spray dried to obtain a granulated powder having the average particle size of 80 µm and a water content of from 0.5 to 1.0% by weight. Further, the granulated powder was forcedly dried at a temperature shown in Table 2 for 24 hours by using a thermostatic drier, and water was added thereto at need. When water was added, the granulated powder was sieved with a JIS standard sieve of a sieve opening shown in Table 2, thus obtaining granulated powders (Sample Nos. 31 to 38). The granulated powder was shaped at a pressure of 2.5 ton/cm² by cold isostatic press, thus obtaining a shaped body of 60 mm x 60 mm x 6 mm. Then, after the shaped body was dewaxed at a temperature of 500°C for 3 hours, the shaped body was pressurelessly sintered at a temperature of 1,700°C in a nitrogen gas atmosphere for 1 hour, thus obtaining high strength silicon nitride sintered bodies according to the present invention (Sample Nos. 31 to 38). Apart from the above, granulated powders of Sample Nos. 39 to 41 were prepared as Comparative Examples of the present invention under producing conditions shown in Table 2 with no forced drying, and the granulated powders were shaped and fired under the same conditions, thereby obtaining sintered bodies. Then, flexural strength, maximum pore diameter, and porosity of the sintered bodies and a ratio of β-silicon nitride crystals in the sintered body were measured in the same manner as in Example 1, and measurement results are shown in Table 2. As is clear from Table 2, the sintered bodies according to the present invention using the mixed powder being force dried, and added with water and sieved as needed, were sintered bodies which had higher strength and were less porous as compared with the Comparative Examples. Example 3 In order to examine influences of the composition of sintered bodies and the sieve opening of the sieve after the grinding, granulated powders (Sample Nos. 42 to 55) were each obtained by force drying granulated powder at a temperature of 80°C for 24 hours in the same manner as in Example 2, adding 4% by weight of water thereto, and passing it through a sieve having a sieve opening of 149 µm. The thus obtained granulated powder was shaped and dewaxed in the same manner as in Example 2, which was pressurelessly sintered in a nitrogen gas atmosphere at an optimum selected firing temperature (1,600 to 1,800°C) as giving a ratio of β-silicon nitride crystals being not less than 90% by weight, thereby obtaining high strength silicon nitride sintered bodies according to the present invention (Sample Nos. 42 to 55). Results are shown in Table 3. As is clear from Table 3, among the sintered bodies of the invention, those in which the granulated powder has been passed through the sieve of 32 µm or less; the mixed raw material contained from 0.5 to 15% by weight of MgO; the mixed raw material contained from 0.5 to 13% by weight of ZrO₂; the mixed raw material contained from 2 to 15% by weight of Y₂O₃; or not less than 90% by weight of β-silicon nitride crystals were contained in the sintered body are preferred. In order to facilitate understanding of results in the above Examples 2 and 3, Figs. 2 and 3 show the relation between the four point flexural strength of sintered bodies obtained according to the present invention and the force drying temperature of granulated powders, and the relation between the four point flexural strength of the sintered bodies and the amount of water added to the granulated powder, respectively, while Fig. 4 shows the relation between the four point flexural strength of the sintered bodies and the sieve opening of the sieve used after the grinding. Example 4 To α-silicon nitride powder having the average particle size of 0.5 µm were mixed powdery MgO, ZrO₂, and Y₂O₃ as sintering aids at rates of 4% by weight, 2% by weight, and 7% by weight, respectively. After 60% by weight of water was added to the mixture, the mixture was mixed and ground by a batch grinder. The thus ground mixture was passed through a sieve having a sieve opening of 20 µm, thereby obtaining a slurry of the ground particles having the average particle size of 0.7 µm. Then, 2% by weight of polyvinyl alcohol (PVA) was added to the slurry, which was converted to a granulated powder by using a spray drier. Further, the granulated powder was force dried at a temperature shown in Table 4 for 24 hours by using a thermostatic drier, and water was added thereto upon necessity. When water was added, the powder was sieved by using a JIS standard sieve having a sieve opening of Table 4, thus obtaining granulated powders (Sample Nos. 61 to 69). The granulated powder was shaped at a pressure of 5 ton/cm² by cold isostatic press, thereby preparing a shaped body of 65 mm() x 50 mm(length). Thereafter, the shaped body was dewaxed at a temperature of 500°C for 3 hours, and pressurelessly sintered at a temperature of 1,460°C for 6 hours in a nitrogen (N₂) atmosphere (primary sintering step). Then, the primarily sintered body was treated at a temperature of 1,700°C under a pressure of 400 atms in an N₂ atmosphere by hot isostatic press (HIP), thus obtaining sintered bodies according to the present invention (Sample Nos. 61 to 69). Apart from the above, sintered bodies (Sample Nos. 70 to 72) were prepared as Comparative Examples of the present invention under producing conditions shown in Table 4 with no force drying. Properties of the thus obtained sintered bodies are shown in Table 4. Knoop hardness was measured according to JIS Z2251 after a test sample was held under a load of 300 g for 15 seconds. Rolling fatigue life was evaluated by cutting off a round disc of 50 mm() x 10 mm(thick) from the sintered sample, mirror polishing the surface of the round disc, and subjecting it to a rolling fatigue test at a hertz stress of 500 kg/mm² in a six ball type thrust bearing tester. As is clear from Table 4, the HIP sintered bodies according to the present invention using the mixed raw material being forcedly dried, and added with water and further sieved at need, are sintered bodies which are extremely less porous and have excellent mechanical strengths, as compared with Comparative Examples. Example 5 In order to examine influences of sieving after grinding and the average particle size after the grinding, except that the kind and the addition amount of sintering aids were changed as shown in Table 5, in the same manner as in Example 4, the granulated powder was force dried at 80°C for 24 hours, 4% by weight of water was added thereto, and the powder was passed through a sieve having a sieve opening of 149 µm, thus obtaining granulated powders (Sample Nos. 73 to 77). After the thus obtained granulated powder was shaped and dewaxed in the same manner as in Example 4, the powder was sealed in a silica glass capsule under vacuum. Then, the capsule was placed in a HIP apparatus, which was HIP-treated at a temperature of 1,600°C under a pressure of 1,500 atms, thus obtaining silicon nitride sintered bodies (Sample Nos. 73 to 77). With respect to the thus obtained sintered bodies, rolling fatigue test was effected similarly as in Example 4, and further, a wear resisting test was effected. In the wear resisting test, a cylindrical sample of 15 mm() x 15 mm(length) was cut off from each of Sample Nos. 73 to 77, and abraded with a #140 diamond grind stone, which was subjected to the wear resisting test by using a ball mill. Test conditions were that an alumina vessel having an inner diameter of 120 mm() was used, and rotated at 120 rpm. A slurry liquid in which #100 silicon carbide powder and water were mixed at a weight ratio of 1:1 was filled up to a half of the vessel. Then, five of the above-prepared samples of 15 mm() x 15 mm(length) were placed in the slurry, and then subjected to the wear resisting test for 24 hours. A wear amount was determined from changes in weight and dimension before and after the test. Results in the rolling fatigue test and the wear resisting test are shown in Table 5. It is seen from Table 5 that among the invention products, those in which the ground powder had been passed through the sieve of not more than 32 µm; or the average particle size after the grinding was not more than 1 µm are preferred. Example 6 To a silicon nitride raw powder having the average particle size of 0.7 µm and containing 97% by weight of α-silicon nitride were mixed powdery MgO, SrO, and CeO₂ at rates of 3.5% by weight, 1.5% by weight, and 5% by weight, respectively. After 60% by weight of water was added to the mixture, the mixture was mixed and ground by a batch grinder and then passed through a sieve having a sieve opening of 20 µm, thereby obtaining a slurry containing powder having the average particle size of 0.5 µm. Then, 2% by weight of polyvinyl alcohol (PVA) was added to the slurry, which was converted to a granulated powder by using a spray drier. Further, the granulated powder was force dried at a temperature shown in Table 6 for 24 hours by using a thermostatic drier, and upon necessity, water was added and the mixture was sieved through a JIS standard sieve having a sieve opening shown in Table 6, thus obtaining granulated powders (Sample Nos. 81 to 88). The granulated powder was shaped at a pressure of 3 ton/cm² by cold isostatic press, thereby preparing a shaped body of 65 mm() x 50 mm(length). Thereafter, the shaped body was dewaxed at a temperature of 500°C for 3 hours, and the pressurelessly sintered at a temperature of 1,460°C for 6 hours in a nitrogen (N₂) atmosphere (primary sintering step). Then, the primarily sintered body was treated by a hot isostatic press (HIP) at a temperature of 1,680°C under a pressure of 400 atms in an N₂ atmosphere, thus obtaining sintered bodies according to the present invention (sample Nos. 81 to 88). Apart from the above, sintered bodies (Sample Nos. 89 to 91) were prepared as comparative Examples of the present invention under producing conditions shown in Table 6 with no force drying. Properties of the thus obtained sintered bodies are shown in Table 6. Flexural strength, maximum pore diameter, and porosity of the thus obtained sintered bodies were measured in the same manner as in Example 1, and measurement results are shown in Table 6. As is clear from Table 6, the HIP sintered bodies according to the present invention using the mixed raw material having been forcedly dried, and added with water and sieved at need, are sintered bodies which are far less porous and have excellent mechanical strength, as compared with Comparative Examples. Example 7 In order to examine influences of the sieving after the grinding and the average particle size after the grinding, an α-silicon nitride raw material (containing 99.5% by weight of α-silicon nitride) was mixed with sintering aids of which kinds and mixing ratios are shown in Table 7. After 60% by weight of water was added to the mixture, the mixture was ground and sieved at a sieve opening as shown in Table 7, thereby obtaining a slurry. The average particle size in the slurry was shown in Table 7. Then, 1% by weight of polyvinyl alcohol and 0.5% by weight of stearic acid were added to the thus obtained slurry, which was converted to a granulated powder by using a spray drier. After the granulated powder was dried at 70°C for 20 hours by using a drier and 4% by weight of water was added thereto, the powder was passed through a sieve having a sieve opening of 149 µm. The resulting powder was shaped at a pressure of 6 ton/cm² by cold isostatic press, thereby obtaining a shaped body of 30 mm() x 60 mm(length). Then, the shaped body was dewaxed at 500°C for 3 hours, and then sealed in a silica glass capsule under vacuum. Next, the capsule was inserted into a HIP apparatus, and HIP-treated at a temperature of 1,700°C under a pressure of 1,500 atms, thus obtaining silicon nitride sintered bodies (Sample Nos. 92 to 97). As is clear from Table 7, among the invention products, those in which the powder had been passed through the sieve of a sieve opening of not more than 32 µm after the grinding; or the average particle size after the grinding was not more than 1 µm are preferred. Example 8 To an α-silicon nitride raw material containing 85% by weight, 92% by weight, or 95% by weight of α-silicon nitride were added 6% by weight of Y₂O₃ and 4% by weight of Aℓ₂O₃ as sintering aids, which were mixed, ground, and sieved by a sieve having a sieve opening of 32 µm, thereby obtaining a slurry. Then, 1% by weight of methyl cellulose was added to the slurry, which was dried by a drier to prepare a granulated powder. The granulated powder was further dried by a thermostatic drier at 100°C for 30 hours, and shaped at a pressure of 3 ton/cm² by cold isostatic press, thereby obtaining a shaped body of 30 mm() x 50 mm(length). Then, the shaped body was dewaxed at 450°C for 5 hours and sealed in a silica glass capsule under vacuum. Next, the capsule was inserted into a HIP apparatus, and HIP-treated at a temperature of 1,600, 1,650, or 1,700°C under a pressure of 1,000 atms for 30 minutes, thus obtaining silicon nitride sintered bodies (Sample Nos. 98 to 104) as shown in Table 8. As is clear from Table 8, it was revealed that the sintered bodies using the silicon nitride raw material containing not less than 90% by weight of α-silicon nitride have higher strength. As is clear from the aforegoing, according to the present invention, high strength, high density and/or high hardness fine ceramic sintered bodies having excellent mechanical strength with smaller maximum pore diameter and porosity can industrially be obtained at an inexpensive cost due to a synergistic effect of forcedly drying of the granulated powder, and water incorporation and/or sieving at need, irrespective of the HIP treatment and the pressureless sintering. Consequently, the ceramic sintered bodies according to the present invention can be applied to, for instance, high temperature bearings, engine parts, gas turbine parts, and the like, and thus have extremely great industrial value.

Claims: A silicon nitride sintered body in which the maximum pore diameter is not more than 10 µm, and the porosity is not more than 0.5%. A sintered body according to claim 1 of which the four point flexural strength at room temperature is not less than 100 kg/mm² (980 MPa). A sintered body according to claim 1 or claim 2 having a Knoop hardness of not less than 15.5 GPa. A sintered body according to any one of claims 1 to 3, which is mainly composed of Si₃N₄ and contains at least one of a Mg compound, a Y compound and a Zr compound. A sintered body according to claim 4, wherein a Mg compound is present in an amount of from 0.5 to 15% by weight calculated as MgO. A sintered body according to claim 4, wherein a Zr compound is present in an amount of from 0.5 to 13% by weight calculated as ZrO₂. A sintered body according to claim 4, wherein a Y compound is present in amount of from 2 to 15% by weight calculated as Y₂O₃. A process for producing a silicon nitride sintered body, which process comprises the steps of: mixing a ceramic raw material powder for said body with a sintering aid, grinding, granulating and shaping the resulting mixture, and firing the shaped body, characterized in that, prior to the shaping, the granulated powder is force dried to a water content in the range 0.2 to 0.5%, and optionally the dried powder is then subjected to addition of water and sieving. A process according to claim 8 wherein in the force drying a temperature of from 60 to 100°C is used. A process according to any one of claims 8 to 9 wherein the ground mixture is passed through a sieve having a sieve opening of 32 µm or less before the granulating. A process according to any one of claims 8 to 10 wherein said addition of water takes place in an amount of from 0.5 to 5% by weight. A process according to any one of claims 8 to 11 wherein prior to the shaping the force dried powder is passed through a sieve having a sieve opening of not more the 250 µm. A process according to any one of claims 8 to 12, wherein the average particle size of the ceramic raw powder after the mixing and grinding is not more than 1 µm. A process according to any one of claims 8 to 13 wherein the granulating is effected by spray drying. A process according to claim 14, wherein at least one of polyvinyl alcohol (PVA), polyethylene glycol (PEG), methyl cellulose (MC) and stearic acid is used as an auxiliary for the spray drying. A process according to any one of claims 8 to 15 wherein the average particle size of the ceramic raw material before mixing and grinding is not more than 2 µm. A process according to any one of claims 8 to 16 wherein the shaped body is subjected to a preliminary treatment and is then treated in an inert atmosphere by hot isostatic pressing. A process according to claim 17 wherein the preliminary treatment of the shaped body is a primary firing at a temperature range from 1,400 to 1,600°C in a nitrogen atmosphere. A process according to claim 17 wherein the preliminary treatment of the shaped body is to seal the shaped body in a capsule. A process according to any one of claims 17 to 19 wherein the silicon nitride raw material contains not less than 90% by weight of α-silicon nitride. A process according to any one of claims 8 to 16 wherein the shaped body is pressurelessly sintered. A process according to claim 21 wherein the silicon nitride raw material contains not less than 90% by weight of α-silicon nitride.

Inventors: HAYAKAWA, ISSEI, MATSUHISA, TADAAKI, MIYAMOTO, MITHURU, UKAI, NORIYUKI
Applicants: NGK INSULATORS, LTD.
Application year: 1987
Main classification: C04B35
IPC codes: C04B35