CAPSULES OF HIGH ALUMINA CEMENT COMPOSITIONS

Abstract: A capsule containing in separate compartments the interactive components of a self-setting composition which comprises as the basic component a paste having a high alumina cement, water and a source of CaO and SiO₂, e.g. as a single-source granulated blast furnace slag, and as a catalyst component a paste of lime, water and a water-­ soluble lithium salt. When reacted the components form a set cement containing hydrated phases typical for an Ordinary Portland cement.

Description: The invention relates to capsules containing the interactive components of a self-setting composition, the components being housed in separate compartments until the capsule is broken. Such a capsule may be used for example to anchor an element in a borehole, e.g. in a mine gallery roof. Capsules of this class are known, and they fall into different types dependent on the nature of the self-setting composition. The composition may be organic as in the case of polyester systems or inorganic as in the case of cementitious systems. This invention is concerned with capsules containing a cementitious system the interactive components of which comprise a cement and water or cement and a catalyst therefor. The components are typically a base component (the cement) and a catalyst component. A cementitious composition may be based on Ordinary Portland Cement (OPC). This has the disadvantage of a slow rate of set. There is claimed in our European patent 0113593 (case CBP139) a capsule containing a cementitious composition based on high alumina cement (HAC) the rate of set of which can be controlled. The use of HAC has its limitations, in particular a tendency for the hydrated cement to undergo HAC conversion which may lead to problems caused by loss of strength. It is an object of this invention to provide a capsule containing a cementitious composition which has the advantages of the use of HAC without the disadvantages. In particular, a long shelf life and controlled rate of set, without any substantial deterioration in the ultimate strength or other adverse effect. The invention is based on the realisation that the incorporation in the base component of a filler which is substantially inert with respect to the other ingredients of the base component but which will be activated by the catalyst component when the components are mixed, will secure these advantages. According to one aspect of the invention there is provided a frangible capsule containing in separate compartments the interactive components of a self-setting cementitious composition, one component being a base component and comprising high alumina cement, retarders and water, and the other component being a catalyst component and comprising catalyst, lime and water, is characterised in that the base component includes granulated rapidly cooled blast furnace slag in sufficient quantity such that when the interactive components are interacted the hydrate phases of a hydrated Portland cement are formed. The granulated rapidly cooled blast furnace slag may be of any known type, and derived from any commercial source. The particle size may vary widely but the size should be related to that of the cement particles. The granulated blast furnace slag preferably has a minimum fineness of 275m²/kg, and a bulk density of 1200 kgm⁻³ and an approximate specific gravity of 2.9. The slag is made by grinding a rapidly cooled blast furnace slag to the degree of fineness indicated. The hydrated phases in a set OPC cement are (cement chemistry notation) typically: CSH C₄AH₁3 Ca(OH)₂ C₂ASH₈ whereas in a set HAG cement the hydrated phases are typically: CAH₁₀ C₂AH₈ C₃AH₆ C₂ASH₈ (minor amount) It is a surprising feature of the invention that by adding the granulated rapidly cooled blast furnace slag to an HAC cement the hydrated phases typical of an OPC are formed. The effect is illustrated in the oxide composition diagram of the accompanying drawing. The three main oxides which occur in cement systems are CaO (lime), Al₂O₃ (alumina) and SiO₂ (silica). It will be seen that the oxide phases in the OPC and in the slag are relatively low in Al₂O₃, whereas that of the HAC is high. According to the invention by adding the defined slag in sufficient quantity to the HAC, the set cement has an oxide composition more typical of OPC. So far as we are aware no one has yet appreciated the effect just described. Blast furnace slag is a well known reactive filler often used in OPC compositions but is not, to our knowledge, present in a commercially available HAC composition. For example, the British Board of Agreement certificate 82/1023 CEMSAVE ground granulated blast furnace slag lists the cements with which that material can be used and does not mention HAC. In a search done by the European Patent Office prior to the date of the present application the following documents were noted: US-A-1803582 which discloses the addition of a granulated cast iron slag to an aluminous cement to improve the properties of the cement. The slag is based on phases which today would be identified as C₂S and C₁₂A₇. Neither of these could be present in the base component of the present invention because of the rate of hydration. The C₁₂A₇ hydrates rapidly so that the base component would have no long term stability and the C₂S hydrate steadily releasing lime which reacts with the C₁₂A₇. FR-A-797493 which discloses a composition comprising HAC and a suitably treated and selected blast furnace slag cement. DE-A-1198723 which discloses a composition comprising both OPC and HAC with the optional addition of calcium oxide. None of these documents discloses the invention of the present application namely that a paste of HAC, the defined slag and water, when reacted with a paste of lime, catalyst and water will form a set cement comprising the hydrate phases of hydrated OPC. It is a feature of the invention that the cement-component be essentially free of OPC otherwise the rate of set of the interactive components will not be suitable. It is also a feature of the invention that the base component be reacted with a catalyst component. It is a further surprising feature of the invention that the proportion of the slag may be varied widely relative to the HAC without substantially affecting the rate of set of the interacted composition. It is a preferred feature of the invention that the composition undergo an initial set within less than 15 minutes, ideally about 4 minutes. In our evaluations we have been able to use ratios from about 1:1 up to about 8:1 by weight and keep the rate of set within the preferred time scale. One advantage of the capsule of the invention is the prolonged shelf life, of at least 6 months and often for a year. The interacted components are capable of achieving initial set times between about 1 and 10 minutes, preferably about 3 to about 5 minutes. The set composition after 30 minutes, will have a shear strength of about 7.5N/mm² and a compressive strength of about 17N/mm². The cementitious material in the composition is so-called high alumina cement. This material is known under a variety of names in different countries, for example "Cement Fondue" and "alumina cement" or "super alumina cement". The content of alumina in the cement varies from country to country, sometimes being as low as 30% and other times being over 77% The invention is applicable to all such alumina cements. The catalyst component comprises a paste of a catalyst, lime and water. A catalyst for the high alumina cement is preferably a lithium derivative which is preferably lithium carbonate, lithium sulphate or lithium hydroxide. Any lithium salt may be used provided it is water soluble and compatible with the other ingredients. Trisodium nitrilotriacetate, which will prevent the lime from forming a thick paste, in a proportion of about 0.5 to 2 parts relative to the base, is preferably present. As taught in our European patent publication 0113593 (my ref: CBP 139) sequestrants and the like may be present. The base component preferably has a pH of the order of about 8.5. When components are mixed the set composition will have a pH of the order of about 11. The composition may include other ingredients, e.g. water reducing agents, expanding agents, surfactants, colourants, latex emulsions, anti-foaming agents and plasticisers. As indicated, OPC should be avoided. Other accelerators may be present, e.g. sodium carbonate, sodium sulphate, calcium chloride, sodium hydroxide, ferrous sulphate, sulphuric acid, acetic acid, calcium sulphate, etc. A thixotropic, thickening agent or air entraining agent may be present if water bleed on storage and a loss of grout composition is to be minimised, a point especially important in overhead or fissured rock applications. Polymeric additives such as cellulose ethers,polyacrylamides and polyethylene oxides, or montmorillonite type clays may be present. The capsule may be of any suitable shape so long as the two interactive components are housed in separate compartments for storage. When required and in known manner, an anchoring element is used to rupture the capsule, open the compartments and intermix the interactive components. The capsule may range from 20 to 40mm in diameter and 200 to 600mm in length, and may be used in boreholes ranging from about 25mm to about 50mm in diameter. The boreholes may be drilled in the wall or roof of a coal mine, gold mine, iron ore mine, quarry or civil engineering structures. The invention further includes a base component for reaction with a catalyst component comprising catalyst, lime and water, the base component comprising high alumina cement and slag, characterised in that the base component comprises a paste of high alumina cement and water and retarder and granulated rapidly cooled blast furnace slag in sufficient quantities such that on hydration of the cement the hydrate phases of a hydrated Portland cement are formed. In order that the invention may be well understood, it will now be described by way of example with reference to the following examples, in which parts are by weight unless otherwise stated. Example 1 A catalyst component was made as a paste of A range of base compositions was made up as shown in Table I. The compositions were stored for several months and then the interactive components mixed. The set times, shear strengths and compressive strengths were measured as shown in Tables II and III. From these results it is clear that the set composition has excellent characteristics. Example II Capsules according to selected formulations of Example I were made up and allowed to set in comparison with two commercially available capsules LOKSET LF6, according to patent publication EPO046037 (LOKSET is a registered trade mark.) EC PHIX W, available from Celtite Ltd., Alfreton, Derbyshire, England. The shear strengths and rate of strength development are shown in Tables IV and V respectively from which it can be see that the capsules of the invention have much better properties.

Claims: A frangible capsule containing in separate compartments the interactive components of a self-setting cementitious composition, one component being a base component and comprising high alumina cement, retarder and water, and the other component being a catalyst component and comprising a catalyst, lime and water characterised in that the base component includes granulated rapidly cooled blast furnace slag in sufficient quantity such that when the interactive components are interacted the hydrate phases of a hydrated Portland cement are formed. A capsule according to Claim 1 characterised in that the granulated rapidly cooled blast furnace slag is ground to a minimum fineness of 275m²/Kg, a bulk density of 1200 Kgm⁻³ and an approximate specific gravity of 2.9. A capsule according to Claim 1 or 2 characterised in that the granulated rapidly cooled blast furnace slag is present in a weight ratio of from about 1:1 to about 8:1 relative to the high alumina cement. A capsule according to any preceding Claim characterised in that the catalyst component comprises lime, water and a water soluble lithium salt. A base component comprising high alumina cement and a slag characterised in that the component comprises a paste of high alumina cement and water and retarder and granulated rapidly cooled blast furnace slag in sufficient quantities such that on hydration of the cement the hydrate phases of a hydrated Portland cement are formed. A paste according to Claim 5 characterised in that the granulated rapidly cooled blast furnace slag is ground and has a minimum fineness of 275m²/Kg, a bulk density of 1200 Kgm⁻³ and an approximate specific gravity of 2.9. A paste according to Claim 5 or 6 characterised in that the granulated rapidly cooled blast furnace slag is present in a weight ratio of from about 1:1 to about 8:1 relative to the high alumina cement.

Inventors: SMART, RODERICK MACDONALD
Applicants: FOSROC INTERNATIONAL LIMITED
Application year: 1987
Main classification: C04B28
IPC codes: E21D20, F16B13, C04B7, C04B28