SOLAR CONTROL GLASS ASSEMBLY AND METHOD OF MAKING SAME

Abstract: A glass assembly (11) includes a glass substrate (14) having an induced transmission filter adhered to one surface thereof. The filter includes at least one coating (17) formed of a layer of reflective material between two layers of dielectric material. The reflective material can be one of aluminum, silver, gold and copper. The dielectric material can be one of zinc oxide, indium oxide, titanium dioxide and tin oxide. The coating (17) can be applied to one side of the plastic carrier sheet (18) and an abrasion resistant material (19) can be applied to the other side of the carrier sheet to form a film (16). The film (16) can be adhered directly to the glass (14) or to an intermediate plastic sheet. In an alternate embodiment, the coating (54) can be applied to a surface of a glass sheet (51) and covered with an abrasion resistant material which can be another sheet of glass (57).

Description: TITLE SOLAR CONTROL GLASS ASSEMBLY AND METHOD OF MAKING SAME Technical Field The present invention concerns glass structures for controlling the transmission of solar energy in general and, in particular, to automotive glass for transmitting light in the visible spectrum while blocking solar radiation outside the visible spectrum. Background Art Two methods, or some combination thereof, are generally utilized to reduce the transmission of solar energy through glass. The first method is absorption wherein the solar energy outside of a particular bandwidth is absorbed by predetermined elements in the glass and reradiated as heat. For example, U.S. Patent No. 2,860,059 discloses a light absorbing glass suitable for automotive and architectural glazing applications. - In a laminated automotive windshield " in which two sheets of glass are bonded to an intermediate layer of polyvinyl butyral resin, the plastic layer is provided with a colored band extending across the upper portion of the windshield which band gradually decreases in light transmittance to provide a built-in glare screen for the windshield. An ultraviolet light absorbing glass is provided at least for the outer glass sheet to protect the colored band from fading and other injurious effects of the sun. The glass is ordinary, soda- lime- silica glass to which ultraviolet cut-off materials such as eerie oxide and titanium dioxide combined with ferric oxide are added. It is important that automotive glass have a low total solar transmission with relatively high transmission in the visible spectrum. United States Federal standards require the Illuminant A value of automotive glass to be at least seventy percent of the value of clear glazed glass at a one quarter inch thickness in the visible spectrum (wavelengths of 400-700 millimicrons) . This requirement insures that the driver will have sufficient transmission through the glass to be able to contrast an automobile headlight and other sources of light from, the background. Since It is also desirable to block infrared radiation, much work has been done on automotive glass which blocks the solar transmission on both ends of the visible spectrum. The United States Federal Illuminant A standard is at least seventy percent transmittance in the visible spectrum at one quarter inch thickness. To be considered to be a heat ab-s_orJb;ijχg glass, the total solar transmittance must be below fi_f-ty- pe-rcent at the same thickness. One method of manufacturing heat absorbing glass is to incorporate iron and tin in the glass and maintain during the glass melting, refining and reforming period at least eighty percent of the Iron in the glass in the ferrous state. Furthermore, sufficient tin must be maintained in the stannous state to act as an internal reducing agent to prevent additional oxidation of the ferrous Iron to ferric species in a subsequent glass reh'eating step. By introducing other infrared absorbing compounds into the glass batch materials, radiation at the infrared end of the spectrum could be absorbed while producing an automotive glass which would meet the Illuminate A standards. The other method of reducing the solar transmission is reflection. A * reflecting material such as silver is coated directly on the surface of the glass or onto the surface of a plastic sheet which is then adhered to the glass. The addition of tin oxide can lower the transmission of basic automotive glass. However, this technique produces only marginal solar gain since the absorbed energy can be reradiated both to the outside and inside of the vehicle. Reradiated energy to the inside of the vehicle becomes a solar gain which is added to the direct solar gain that passes through the glass unabsorbed. As the amount of glass sheet used in vehicles increases, the solar gain will also increase placing an increased strain on air conditioning systems . A better approach is to increase the total solar reflection of the glass by the addition of coatings applied directly to the glass or to a carrier film such as polyester which can be applied to the glass. Light from the sun, which is reflected and not absorbed, is not a gain to the car since it is not transformed into heat but remains as light. The other advantage of a reflecting coating over an absorbing glass is that the reflective coating maintains an increasing edge over the absorbing glass as the wind becomes lower and lower. The glass temperature for an absorbing glass increases with lower wind speed and therefore loses more energy to the inside of the car. Disclosure of Invention The present invention utilizes an induced transmission filter combined with automotive glass to achieve improved filtering characteristics of glass to solar gain. ϊhe filter maintains high transmission over the visible part of the solar spectrum and also has high reflection over the infrared part. The filter includes a stack of coatings which are applied to one side of a polyester film with a hardcoat applied to the other side of the film. The coatings face the inside surface of the glass and the hardcoat faces the inside of the car to prevent damage to the coatings and film during normal use. An additional film of polyester can be applied to the surface of the coatings where certain types of adhesives are utilized to attach the film to the glass. A glass assembly according to the present invention which provides improved resistance to solar transmission and meets the United States Federal Illuminant A standards consists of a PET carrier film having an abrasion resistant coating or hardcoat on one side and layers of a reflective coating on the other side. Each of the layers of reflective coating is a sandwich of a layer of metallic film between two layers of dielectric coatings. For example, the metallic film can be a layer of silver and the dielectric coatings can be layers of zinc oxide. Such a construction is applied to a layer o . polyvinyl butyral on the inside of a glass substrate such as a single sheet of glass or a laminated windshield having two layers of glass with a layer of polyvinyl butyral in between. The two reflective coating layers provide significantly better resistance to solar transmission than one layer and still meet the Illuminant A standards. The film is applied to the glass by either adhering it to a layer of polyvinyl butyral which is then applied to the glass, or by utilizing a pressure sensitive adhesive, or by utilizing a water-activated adhesive. In the latter case, a polyester protective sheet is utilized between the adhesive and the reflective coating. Brief Description of the Drawings The above, as well as other advantages of the present invention, will become readil • apparent to those skilled In the art from the following detailed description of a preferred embodiment when considered in the light of the accompanying drawings in which: Fig. 1 is a fragmentary cross-sectional view of a laminated glass assembly including a film for controlling solar gain according to the present invention; Fig. 2 is a fragmentary cross-sectional enlarged view of the coating layer of Fig. 1; Fig. 3 is a fragmentary cross-sectional view of an alternate embodiment of a glass assembly according to the present invention; Fig. 4 is an enlarged view of the attaching layer shown in Fig. 3 according to the present invention; Fig. 5 is a fragmentary cross -sectional view of a second alternate embodiment of a glass assembly according to the present invention; and Fig. 6 is a fragmentary cross - sectional view of a third alternate embodiment of a glass assembly according to the present invention. Modes for Carrying Out the Invention Referring to Fig. 1, there is shown a glass assembly 11 according to the present invention. The assembly 11 can be, for example, a laminated vehicle windshield including an outer layer of clear glass 12 and intermediate layer 13 of polyvinyl butyral and an inner layer 14 of clear glass. The glass assembly 11 can be of the anti - lacerative type which includes a protective layer 15 of polyvinyl butyral adhered to an inner surface of the inner layer 14 of glass. The glass assembly 11 also includes an induced transmission filter formed as a film 16 adhered to an inner surface of the protective layer 15. The film 16 consists of a coating 17 closest to the protective layer 15, an intermediate carrier 18 farmed of a plastic material such as polyester, and*a protective layer of hardcoat 19 which is substantially abrasion resistant. The intermediate layer 18 can be, for example, formed of a polyethylene terephthalate . The coating 17 is a reflective material which tends to reflect the ultraviolet and infrared wave lengths of solar radiation back out through the polyvinyl butyral layers 13 and 15 and the glass layers 12 and 14. Thus, the assembly has reduced solar gain to the interior of the vehicle and also meets the United States Federal Illuminant A standards. There is shown in Fig. 2 an enlarged fragmentary cross- sectional view of the coating 17. The coating is a sandwich of a reflective metallic material between two layers of dielectric material. For example, the coating 17 can include a first layer 20 of zinc oxide, a second or intermediate layer 21 of silver, a third layer 22 of zinc oxide. The order of the layers is then repeated with a fourth layer 23 of zinc oxide, a fifth layer 24 of silver and a sixth layer the outwardly facing surface of the carrier 18 before being attached to the protective layer 15. Other materials are suitable for use in the coating 17. For example, the dielectric material can be titanium dioxide or Indium or tin oxide. The reflective metallic material can be gold or aluminum or copper. Typically, the total thickness of the two dielectric layers and the one reflective layer is in the range of two hundred twenty-five to one thousand two hundred fifty angstroms. The reflective layer can be from twenty-five to two hundred fifty angstroms and each dielectric layer can be from one hundred to five hundre i angstroms . There is shown in Fig. 3 a fragmentary cross-sectional view of a glass assembly 30 according to an alternate embodiment of the glass assembly 11 of Figs. 1 and 2. A glass sheet substrate 31 has an attaching layer 32 formed on its inner surface. . The attaching layer 32 can be polyvinyl butyral or some form of adhesive structure utilizing a pressure sensitive adhesive or a water-activated adhesive as shown in Fig. 4. The attaching layer 32 connects a film 33 with the glass sheet 31. The film 33 can consist of a coating layer 34, a carrier layer 35, and a hardcoat 36. Thus, the film 33 is similar to the film 16 shown in Fig. 1. The attaching layer 32 is shown in more detail in Fig. 4. A layer 37 of pressure sensitive adhesive or water- activated adhesive is applied to one side of a carrier layer 38 of a plastic material such as polyester which faces the substrate 31. A layer 39 of pressure sensitive adhesive is applied to the opposite side of the carrier 38 which faces the coating layer 34. There is shown in Fig. 5 a fragmentary cross-sectional view of a second alternate embodiment of a glass assembly 40. A sheet of glass 41 has a coating 42 adhered to an inner surface thereof. The coating 42 is then covered by an abrasion resistant layer 43. The layer 43 can be a hardcoat or a polyvinyl butyral material. Although shown as a laminated glass structure, the glass assembly 11 of Fig. 1 could be a side light or a back light which typically are formed of a single layer of glass. Thus, the outer layer 12 and the intermediate layer 13 could be eliminated. Similarly, the glass assembly of Fig. 3 and the glass assembly 40 of Fig. 4 are shown with single glass sheets. They could also be formed as laminated glass structures by adding an intermediate layer such as the polyvinyl butyral layer 13 and outer layer such as the glass layer 12 of Fig. 1. Thus, the solar control glass assemblies shown in the figures and described above could be utilized in every window in a vehicle. A glass assembly of the type shown in Fig. 1 having two coatings of the zinc oxide and silver combination has been found to meet the United States Federal Illuminant A standards of at least 70% in the visible spectrum with total solar transmission of less than 40%, and total solar •reflection greater than 25%. The coating configuration shown in Fig. 2 has been found to be the most suitable for reducing solar gain and meeting the Federal Illuminant standard. A single set of filter layers does not provide enough reduction in solar transmission to meet the solar gain requirements demanded by the automobile industry. Fig. 6 is a fragmentary cross -sectional view of a third alternate embodiment of a glass assembly 50. A sheet of glass 51 has a layer 52 of polyvinyl butyral or similar material adhered to its inner surface. The next layer 53 is a film formed of a coating layer 54 and a carrier layer 55. The assembly 50 is completed with a second layer 56 of polyvinyl butyral and an outer layer of glass 57. The layers 56 and 57 replace the abrasion resistant layers in the first two embodiments. The present invention has been described in what is considered to represent its preferred embodiment. However, it should be noted that the invention can be practiced otherwise than as specifically illustrated and described without departing from its spirit or scope.

Claims: Claims 1. A glass assembly for controlling solar transmission including : a glass substrate having inner and outer surfaces; an induced transmission filter layer adhered to said inner surface of said glass substrate; and an abrasion resistant layer adhered to said filter layer whereby the Illuminant A transmission through the glass assembly is relatively high and the transmission of ultraviolet and infrared radiation through the glass assembly is relatively low. 2. The glass assembly according to claim 1 wherein the Illuminant A transmission is at least seventy percent. 3. The glass assembly according to claim 1 wherein the solar ultraviolet transmission is less than fifty-five percent . • » 4. The glass assembly according to claim 1 wherein the solar infrared transmission is less than fifty-five percent. 5. The glass assembly according to claim 1 wherein the glass substrate includes a first sheet of glass forming said outer surface, an intermediate sheet of polyvinyl butyral and an inner sheet of glass forming said inner surface. 6. The glass assembly according to claim 5 wherein said glass substrate includes a- sheet of polyvinyl butyral adhered between said inner glass sheet and said filter layer. 7. The glass assembly according to claim 1 wherein to said filter layer includes a first layer of dielectric material, a second layer of reflective material, and a third layer of dielectric material. 8. The glass assembly according to claim 7 wherein -raid filter layer includes a fourth layer of dielectric material, a fifth layer of reflective material, and a sixth layer of dielectric material. 5 9. The glass assembly according to claim 8 wherein said dielectric material is zinc oxide. 10. The glass assembly according to claim 8 wherein O said dielectric material is one of titanium dioxide, indium oxide and tin oxide. 11. The glass assembly according to claim 8 wherein said reflective material is silver. 5 12. The glass assembly according to claim 1 wherein said filter layer is deposited upon a sheet of plastic material. - 0 13. The glass assembly according to claim 12 wherein said plastic material is formed of polyester. 14. The glass assembly according to claim 13 wherein said polyester is polyethylene terethphalate . 5 15. The glass assembly according to claim 1 including an- attaching layer positioned between and adhered to said glass substrate and said filter layer. O " 16. The glass assembly according to claim 15 wherein said attaching layer is formed of polyvinyl butyral. 17. The glass assembly according to claim 15 wherein said attaching layer includes an adhesive. 5 18. The glass assembly according to claim 17 wherein said attaching layer includes a carrier layer of plastic material coated on opposite sides with said adhesive and said adhesive is a pressure sensitive adhesive. 19. The glass assembly according to claim 17 wherein said attaching layer includes a carrier layer of plastic material coated on one side with a pressure sensitive adhesive and coated on an opposite side with said adhesive and said adhesive is a water- activated adhesive. 20. The glass assembly according to claim 1 wherein said abrasion resistant layer is formed of a glass sheet. 21. The glass assembly according to claim 20 wherein said abrasion resistant layer is formed with a sheet of polyvinyl butyral adhered between said filter layer and said glass sheet . 22. A method of making a glass assembly for controlling solar transmission including the steps of: a. obtaining a glass substrate; b. forming an induced transmission filter film having a first layer of dielectric material, a second layer of reflective material and a third layer of dielectric material; c. adhering said film to a surface of said glass substrate; and d. adhering a layer of abrasion resistant material to said film to form the glass assembly. 23. The method according to claim 22 wherein step b. is performed by applying said three layers to a carrier sheet and said step d. is formed by applying said layer of abrasion resistant material to the other side of said carrier sheet. 24. The method according to claim 22 wherein step b. is performed after forming said glass substrate from a first siieet of glass, a sheet of polyvinyl butyral, and a second sheet of glass adhered together. 5 25. The method according to claim 22 wherein said step b. is performed by adding a fourth layer of dielectric material, a fifth layer of reflective material and a sixth layer of dielectric material to said layers. 10 26. The method according to claim 22 wherein said step b. is performed by selecting said first and third layers from a group of dielectric materials including zinc oxide, indium oxide, titanium dioxide and tin oxide. 15 27. The method according to claim 22 wherein said step b. is performed by selecting said second layer from a group of reflective materials Including aluminum, silver, gold and copper. » 20. 28. A method of making a glass assembly for controlling solar transmission including the steps of: a. obtaining a glass substrate; b. forming an induced transmission filter film 25 having at least one layer of reflective material between at least two layers of dielectric material; c. adhering said film to a surface of said glass substrate; and d. adhering a layer of abrasion resistant 30 material to said film to form the glass assembly. 29. The method according to claim 28 wherein said step b. Is performed by selecting said reflective material from a group Including aluminum, silver, gold and copper and 35 selecting said dielectric material from a group including zinc oxide, indium oxide, titanium dioxide and tin oxide. 30. A method of making a glass assembly for controlling solar transmission including the steps of: a. obtaining a glass substrate; b. selecting a reflective material from a group 5 including aluminum, silver, gold and copper; c. selecting a dielectric material from a group including zinc oxide, indium oxide, titanium dioxide and tin oxide ; d. forming an induced transmission filter film 10 having first, third, fourth and sixth layers of said dielectric material selected in step c. and second and fifth layers of said reflective material selected in step b . ; e. adhering said film to a surface of said glass 15 substrate; and f. adhering a layer of abrasive resistant material to said film to form the glass assembly. 31. The rrrethod according to claim 30 wherein step f. is 20 performed by adhering a sheet of glass to said film. 32. A glass assembly for controlling solar transmission including : a glass substrate having a surface; 25 " an induced transmission filter layer adhered to said glass substrate surface, said layer including at least one layer of reflective material between two layers of dielectric material; and an abrasion resistant layer adhered to said filter 3.0 layer. 33. The glass assembly according to claim 32 wherein said reflective material is one of aluminum, silver, gold and copper . 5 34. The glass assembly according to claim 32 wherein said dielectric material is one of zinc oxide, indium oxide, titanium dioxide and tin oxide. 35. The glass assembly according to claim 32 wherein said filter has total solar transmission properties of less than forty percent and the total solar reflection is greater than twenty-five percent. 36. The glass assembly according to claim 32 wherein said reflective material has a thickness in the range of twenty-five to two hundred fifty angstroms. 37. The glass assembly according to claim 32 wherein each layer of dielectric material has a thickness in the range of one hundred to five hundred angstroms. 38. The glass assembly according to claim 32 wherein said abrasion resistant layer is formed of a sheet of polyvinyl butyral adhered to a sheet of glass.

Inventors: GOODMAN RONALD D, GOODMAN, RONALD, D.
Applicants: LIBBEY OWENS FORD CO, LIBBEY-OWENS-FORD CO.
Application year: 1987
Main classification: B32B17
IPC codes: B32B7, B32B9, B32B17, B32B27, B60J1, C03C17, C03C27