CATALYST FOR PURIFYING MOTOR VEHICLE EXHAUST GASES AND PROCESS FOR PRODUCTION THEREOF

Abstract: A catalyst, and a method for producing the catalyst, and a method for purifying exhaust gases which is very efficient in its use of rhodium has a layered catalytic structure on a refractory substrate, the inner layer containing ceria and platinum, the outer layer containing zirconia and rhodium.

Description: Detailed Description of the Invention This invention relates to a catalyst for purifying exhaust gases from internal combustion engines of automobiles, etc., and to a process for production thereof. More specifically, this invention relates to a catalyst for purifying exhaust gases, essentially comprising a substantially catalytically inert, refractory monolithic support, an inside layer containing a catalytically active refractory oxide on the support, and an outside layer containing a catalytically active refractory oxide on the inside layer, and to a process for production thereof. A catalyst comprising a support and two or more layers of refractory oxide thereon is known. For example, Japanese Laid-Open Patent Publication No. 145381/1975 discloses a catalyst-supported structure for purifying exhaust gases comprising a thermally insulating ceramic carrier and at least two layers of catalyst-containing alumina or -zirconia, the catalysts in the catalyst-containing alumina or -zirconia layers being different from each other. Japanese Laid-Open Patent Publication No. 105240/1982 discloses a catalyst for purifying exhaust gases containing at least two kinds of platinum-group metals, said catalyst comprising at least two carrier layers of a refractory metal oxide containing one kind of the platinum-group metals of different kinds and as required, a layer of a refractory metal oxide free from the platinum-group metal between the carrier layers and/or on the outside of these carrier layers. Japanese Laid-Open Patent Publication No. 52530/1984 discloses a catalyst having a first porous carrier layer composed of an inorganic substrate and a heat-resistant noble metal-type catalyst deposited on the surface of the substrate and a second heat-resistant non-porous granular carrier layer having deposited thereon a noble metal-type catalyst, said second carrier layer being formed on the surface of the first carrier layer and having resistance to the catalyst poison. Japanese Laid-Open Patent Publication No. 127649/1984 discloses a catalyst for purifying exhaust gases, comprising an inorganic carrier substrate such as cordierite, an alumina layer formed on the surface of the substrate and having deposited thereon at least one rare earth metal such as lanthanum and cerium and at least one of platinum and palladium, and another alumina layer formed on the aforesaid alumina layer and having deposited thereon a base metal such as iron or nickel, at least one rare earth metal such as lanthanum, and rhodium. Japanese Laid-Open Patent Publication No. 19036/1985 discloses a catalyst for purifying exhaust gases having an enhanced ability to remove carbon monoxide at low temperatures, said catalyst comprising a substrate composed, for example, of coerdierite and two layers of active alumina laminated to the surface of the substrate, the lower alumina layer containing platinum or vanadium deposited thereon, and the upper alumina layer containing rhodium and platinum, or rhodium and palladium, deposited thereon. Japanese Laid-Open Patent Publication No. 31828/1985 discloses a catalyst for purifying exhaust gases, comprising a honeycomb carrier and a noble metal having a catalytic action for purifying exhaust gases, the carrier being covered with an inside and an outside alumina layer, the inside layer having more noble metal adsorbed thereon than the outside layer; and a process for production of this catalyst. Japanese Laid-Open Patent Publication No. 232253/1985 discloses a monolithic catalyst for purifying exhaust gases being in the shape of a pillar and comprising a number of cells disposed from an exhaust gas inlet side toward an exhaust gas outlet side, an alumina layer being formed on the inner wall surface of each of the cells, and catalyst ingredients being deposited on the alumina layer, the alumina layer consisting of a first alumina layer on the inside and a second alumina layer on the surface side, the first alumina layer having palladium and neodymium deposited thereon, and the second alumina layer having platinum and rhodium deposited thereon. None of the above-cited patent documents disclose a two-layer catalyst comprising an inside layer containng a catalytically active refractory oxide, the inside layer containing cerium oxide and platinum as essential ingredients and having a weight of 10 to 200 g per liter of the catalyst, and an outside layer containing a catalytically active refractory oxide, the outside layer containing a zirconium compound and rhodium as essential ingredients and having a weight of 5 to 60 g per liter of the catalyst. It is known that rhodium exhibits an important catalytic action in the purification of exhaust gases containing carbon monoxide, hydrocarbons and nitrogen oxides. Many exhaust gas purifying catalysts comprising rhodium are known. Rhodium is one of those platinum-group catalysts whose resources are particularly greatly limited. Furthermore, since the price of rhodium is high, it is desirable to minimize the amount of rhodium used in producing exhaust gas purifying catalysts while making use of the characteristics of rhodium as a catalyst. From this standpoint, none of the previously known rhodium-containing catalysts for purifying exhaust gases prove to be satisfactory. It is an object of this invention to provide a catalyst which exhibits the catalytic characteristics of rhodium as much as possible and minimizes the amount of rhodium. It is another object of this invention to provide a process for producing the aforesaid rhodium-containing catalyst. The above object is achieved by a catalyst for purifying exhaust gases essentially comprising a substantially catalytically inert, refractory monolithic support, a first layer containing a catalytically active refractory oxide on the support, and a second layer containing a catalytically active refractory oxide formed on the first layer, characterized in that the first layer contains cerium oxide and platinum and has a weight of 10 to 200 g per liter of catalyst, and the second layer has a weight of 5 to 60 g per liter of the catalyst, and contains i) rhodium in an amount of from 0.002 to 2 g per liter of catalyst, and ii) a zirconium compound. Preferably, the support has continuous longitudinal unobstructed flow channels each extending through the support and defined by a thin wall, the first layer is deposited on the walls of the channels, and the catalytically active refractory oxide of one or both layers is finely divided and has a specific surface area of at least about 10 m²/g. The other object of this invention is achieved by a process for producing a catalyst as described above which comprises depositing a first slurry containing a finely divided catalytically active refractory oxide and/or its precursor, cerium oxide or another cerium compound, and platinum or a platinum compound on a substantially catalytically inert refractory monolithic support, drying the support having the first slurry deposited thereon, thereafter depositing a second slurry containing a finely divided catalytically active refractory oxide and/or its precursor, zirconium oxide or another zirconium compound and rhodium or a rhodium compound on the support, and calcining the support having the second slurry deposited thereon. The present invention will be described below in detail. [A] First, the catalyst of the invention for purifying exhaust gases will be described. The catalyst of the invention for purifying exhaust gases essentially comprises a substantially catalytically inert refractory monolithic support, a first layer, i.e. a lower layer, formed on the support and containing a catalytically active refractory oxide, and a second layer, i.e. an upper layer, formed on the first layer and containing a catalytically active refractory oxide. That the support is "substantially catalytically inert" means that at least a greater part of the catalytic activity of the catalyst of this invention depends upon the catalytic activities of the first and second layers, and does not have to depend upon the catalytic activity of the support. Of course, the support itself may be catalytically active. The support may be made up of, for example, a refractory metal oxide, or a refractory metal. Examples of the refractory metal oxide include cordierite, mullite, alpha-alumina, sillimanite, magnesium silicate, zircon, petalite, spodumene and aluminosilicates. Examples of the refractory metal include refractory iron-base alloys such as stainless steel and Fecralloy, refractory nickel-base alloys, and refractory chromium-base alloys. A support composed of cordierite is one of the most desirable supports. The support is of a monolithic structure and preferably has continuous longitudinal unobstructed flow channels each extending through the support and defined by a thin wall surface. The thickness of the wall may be small to any extent so long as the support has strength required of the final catalyst. A first layer (inside layer) containing a catalytically active refractory oxide is deposited on the support, eg. on the walls of flow channels in the support. Examples of the catalytically active refractory oxide constituting the first layer are active alumina, alpha-alumina, silica, silica-alumina and titania. Active alumina, for example gamma-alumina, is preferred. Desirably, the active alumina has a specific surface area of 10 to 300 m²/g. The weight of the catalytically active refractory oxide is usually 7 to 160 g, preferably 20 to 130 g, per liter of the catalyst. The catalytically active refractory oxide may occupy 50 to 95% by weight, preferably 60 to 85% by weight, of the first layer. The first layer containing the catalytically active refractory oxide contains cerium oxide and platinum as essential ingredient. The weight of cerium oxide is preferably 5 to 100 g, more preferably 8 to 50 g, per liter of the catalyst. Cerium oxide preferably occupies 5 to 50% by weight, more preferably 15 to 40% by weight, of the inside layer. Desirably, cerium oxide has a specific surface layer of 10 to 300 m²/g. The weight of platinum may be any weight so long as the required catalyst activity can be obtained. Usually, it is 0.01 to 10 g, preferably 0.1 to 3 g, per liter of the catalyst. The first layer containing the catalytically active refractory oxide, cerium oxide and platinum has a weight of 10 to 200 g, preferably 20 to 180 g, more preferably 40 to 100 g, per liter of the catalyst. If the first layer does not contain cerium oxide, the catalyst has a greatly decreased rate of removal of carbon monoxide and hydrocarbons. A second layer (outside layer) containing the catalytically active refractory oxide is further deposited on the first layer. The catalytically active refractory oxide constituting the second layer may be the same as the catalytically active refractory oxide constituting the first layer. The weight of the catalytically active refractory oxide in the second layer is preferably 5 to 55 g, more preferably 10 to 50 g, per liter of the catalyst. The catalytically active refractory oxide may occupy 50 to 95% by weight, preferably 70 to 90% by weight, of the second layer. The second layer containing the catalytically active refractory oxide contains zirconium oxide and rhodium as essential ingredients. The weight of zirconium oxide is preferably 1 to 20 g, more preferably 2 to 15 g, per liter of the catalyst. Zirconium oxide preferably occupies 5 to 50% by weight, more preferably 10 to 30% by weight, of the second layer. The weight of rhodium may be any weight so long as the required catalytic activity is obtained. Usually, it is 0.002 to 2 g, preferably 0.02 to 0.7 g, per liter of the catalyst. The weight of the second layer containing the catalytically active refractory oxide, zirconium oxide and rhodium is 5 to 60 g, preferably 7 to 45 g, more preferably 7 to 40 g, per liter of the catalyst. If the weight of the second layer exceeds 60 g, the resulting catalyst has a rapidly decreased ratio of removal of carbon monoxides, hydrocarbons and nitrogen oxides. If the second layer does not contain zirconium oxide, the catalyst has a reduced ratio of removal of carbon monoxide and hydrocarbons. If the first layer does not contain cerium oxide and the second layer does not contain zirconium oxide, the catalyst has drastically decreased ratios of removal of carbon monoxide, hydrocarbons and nitrogen oxides. The decrease in the ratio of removal of hydrocarbons in this case is especially remarkable. In the present specification, the thicknesses of the first layer (lower layer) and the second layer (upper layer) of the catalyst are calculated on the basis of the catalyst model shown in Figure 1. In the catalyst of this invention, the first layer has a thickness of 5 to 110 microns, and the second layer has a thickness of 3 to 35 microns. [B] The process for producing the exhaust gas purifying catalyst of the invention will now be described. Preparation of a slurry (slurry I) for the first layer (lower layer):- A finely divided catalytically active refractory oxide is put in a mixer. It may be introduced together with its precursor. The precursor of the catalytically active refractory oxide, as used in the present specification, denotes a substance which yields a catalytically active refractory oxide when calcined. Active aluminas such as gamma-alumina may be used as the finely divided catalytically active refractory oxide. Examples of the precursor are alumina hydrates such as gibbsite, bayerite, nordstrandite and boehmite. The finely divided catalytically active refractory oxide and its precursor may have a particle diameter of 1 to 100 microns, preferably 1 to 50 microns, especially preferably 1 to 30 microns. A plantinum compound such as hexahydroxoplatinic acid and chloroplatinic acid is added to the finely divided catalytically active refractory oxide. The platinum compound may be added little by little or at a time to the finely divided catalytically active refractory oxide while they are stirred by a mixer. The platinum oxide may be added as a solution such as an aqueous solution or a suspension such as an aqueous suspension. Preferably, the platinum compound may be added as an aqueous amine solution of hexahydroxoplatinic acid. The amount of the platinum compound added may be 1 to 100 g calculated as platinum, and 100 ml to 500 ml as the solution of the platinum compound, per kilogram of the finely divided catalytically active refractory oxide. Then, a solution of acetic acid, preferably a 10-20% acetic acid solution, is added to the mixture containing the finely divided catalytically active refractory oxide and the platinum compound. Preferably, the acetic acid solution is added little by little while this mixture is stirred by a mixer. The amount of the acetic acid solution added may be 100 to 300 ml per kilogram of the catalytically active refractory oxide. The resulting refractory oxide containing the platinum compound, cerium oxide, acetic acid and pure water are introduced into a mill and pulverized to form a slurry. The amount of cerium oxide is 50 to 500 g, preferably 150 to 400 g, per kilogram of the refractory oxide. The amount of acetic acid may be 40 to 100 ml per kilogram of the refractory oxide, and the amount of pure water may be 440 to 1100 ml per kilogram of the refractory oxide. The average particle diameter of the refractory oxide and cerium oxide in the slurry is adjusted to 0.1 to 10 microns, preferably 1 to 5 microns, by the above pulverization in the mill. The resulting slurry is transferred to a vessel, and pure water is added to form a slurry having a predetermined specific gravity which may, for example, be 1.20 to 1.75 g/ml. The slurry I can be easily deposited not only on the refractory metal oxide support, but also on the refractory metal support, by adjusting its specific gravity. Deposition of the slurry I on the support The slurry I is deposited on the support described in section [A] above. It may, for example, be a monolithic cordierite carrier such as a cylindrical monolithic carrier (diameter 93 mm; length 147.5 mm; volume 1.0 liter; 46.5 cells/cm² [300 cells/ in²]). The slurry I is deposited on the support for a period of, for example, 1 to 60 seconds, preferably 3 to 10 seconds, and the excess of the slurry I in the cells is removed by a stream of air. Then, at least 50% of water, preferably at least 90% of water, is removed from the support having the slurry I deposited thereon by hot air, preferably hot air at 20 to 100°C. After water is removed, the support may be calcined in air at 200 to 900°C, preferably 300 to 800°C, for 10 minutes to 10 hours, preferably 15 to 60 minutes. When the temperature of the support is gradually raised in the calcination, the above drying (the removal of water) may be omitted. By the above slurry deposition step, the platinumcarrying alumina and cerium oxide may be deposited, for example, in an amount of 5-160 g and 1-60 g, respectively on the support, for example the monolithic carrier. Preparation of a slurry (slurry II) for the second layer (upper layer):- A finely divided catalytically active refractory oxide is introduced into a mixer. This refractory oxide may be identical with, or different from, the refractory oxide used for preparation of slurry I. A precursor thereof may be introduced together into the mixer. Active aluminas, such as gamma-alumina, may be used as the finely divided catalytically active refractory oxide. Examples of the precursor include alumina hydrates such as gibbsite, bayerite, nordstrandite and beohmite. The finely divided catalytically active refractory oxide and its precursor may have a particle diameter of 1 to 100 microns, preferably 1 to 50 microns, especially preferably 1 to 30 microns. A rhodium compound such as rhodium nitrate or rhodium chloride is added to the refractory oxide. The rhodium compound may be added little by little while the refractory oxide is stirred by a mixer. Alternatively, it is possible to add it all at a time, and then stir the mixture. The rhodium compound may be added as a solution, for example an aqueous solution, or a suspension, for example an aqueous suspension. Examples of preferred rhodium compounds are rhodium nitrate and rhodium chloride. The amount of the rhodium compound added may be 0.2 to 50 g calculated as rhodium, and 100 ml to 500 ml as the solution of the rhodium compound, per kilogram of the refractory oxide. Subsequently, an acetic acid solution, preferably a 10-20% acetic acid solution, is added to the mixture of the refractory oxide and the rhodium compound. Preferably, the acetic acid solution is added little by little while the above mixture is stirred by a mixer. The amount of the acetic acid solution added may be 100 to 300 ml per kilogram of the finely divided catalytically active refractory oxide. The resulting finely divided catalytically active refractory oxide containing the rhodium compound, a zirconium compound, acetic acid and pure water are introduced into a mill and pulverized to form a slurry. The zirconium compound used in this invention may, for example, be zirconyl acetate or zirconium hydroxide. The amount of the zirconium compound is 50 to 500 g, preferably 100 to 400 g, per kilogram of the refractory oxide calculated as zirconium oxide. The amount of acetic acid may be 40 to 100 ml per kilogram of the refractory oxide. The amount of pure water may be 440 to 1100 ml per kilogram of the refractory oxide. The refractory oxide in the slurry obtained by the above pulverization has an average particle diameter of 0.1 to 10 microns, preferably 1 to 5 microns. The resulting slurry is transferred to a vessel, and pure water is added to form a slurry II having a predetermined specific gravity which may, for example, be 1.05 to 1.40 g/ml. Deposition of slurry II on the support having slurry I deposited thereon: The slurry II is deposited on the support on which slurry I has already been deposited. The slurry II is deposited on this support for a period of, for example, 1 to 60 seconds, preferably 3 to 10 seconds, and the excess of the slurry II in the cells is removed by an air stream. The support having the slurry II deposited thereon is then dried with, for example, hot air, preferably hot air at 20 to 100°C, until at least 50% of water, preferably at least 90% of water, is removed. After drying in this manner, the support is calcined, for example in air, at a temperature of 200 to 900°C, preferably 300 to 800°C, for a period of 10 minutes to 10 hours, preferably 15 to 60 minutes. When the temperature of the support is relatively slowly elevated in the calcination, the above drying operation may be omitted. The above slurry deposition step can lead to deposition of 5 to 100 g of the rhodium-carrying alumina and 1 to 50 g of zirconium oxide on the support (e.g., monolithic support). The following examples illustrate the invention in more detail. The invention, however, is not limited by these examples. Production of catalysts EXAMPLE 1 1.2 kg of gamma-alumina (average particle diameter about 20 microns) was put in a mixer. While the gamma-alumina was stirred by the mixer, 400 ml of an aqueous amine solution of hexahydroxoplatinic acid (containing (12.63 g of Pt) was added dropwise little by little and dispersed uniformly. Then, 200 ml of 15% by weight acetic acid was added dropwise little by little to gamma-alumina being stirred by the mixer, and uniformly dispersed. 727 g (calculated as the dry weight) of the platinum-containing alumina, 273 g of cerium oxide (average particle diameter about 15 microns), 50 ml of acetic acid and 550 ml of pure water were put in a porcelain pot, and milled for about 3 hours to form a slurry. The alumina and cerium oxide in the slurry had an average particle diameter of about 3.5 microns. The slurry was transferred to a 2-liter vessel, and pure water was added to adjust the specific gravity of the slurry to 1.56 g/ml. The slurry was deposited for 5 seconds on a cylindrical cordierite monolithic carrier (diameter 93 mm, length 147.5 mm, volume 1.0 liter, 46.5 cells/cm² [300 cells/in²]). The excess of the slurry in the cells was removed by an air stream. Furthermore, about 90% of water was removed by using hot air at 30 to 60°C, and the carrier was calcined in an air stream at 500°C for 30 minutes. By the above series of steps, 80 g of the platinum-carrying alumina (containing 0.83 g of Pt) and 30 g of cerium oxide were deposited on the monolithic carrier to form a first layer (lower layer). Then, 1.2 kg of gamma-alumina was put in a mixer, and while the gamma-alumina was stirred by the mixer, 400 ml of an aqueous solution of rhodium nitrate (containing 13.40 g of Rh) was added dropwise little by little and dispersed uniformly. Subsequently, 150 ml of 15% by weight acetic acid was added dropwise little by little to the gamma-alumina being stirred in the mixer, and uniformly dispersed. 500 g (calculated as the dry weight) of the rhodium-containing alumina, 30 ml of acetic acid and 580 g (117 g as zirconium oxide) of zirconyl acetate, and 350 ml of pure water were put in a porcelain pot, and milled for about 3 hours to form a slurry. The alumina in the slurry had an average particle diameter of about 3 microns. The slurry was transferred to a 2-liter vessel, and pure water was added to adjust its specific gravity to 1.17 g/ml. The slurry was deposited on the monolithic carrier, followed by calcination, by performing the same steps as used in depositing the lower layer on the monolithic carrier. As a result, 15 g of rhodium-carrying alumina (containing 0.17 g of Rh) and 3.5 g of zirconium oxide were deposited as a second layer (upper layer). The above steps gave a catalyst (sample No. 1) having a lower layer (110 g/liter of catalyst) of the platinum-carrying alumina/cerium oxide and an upper layer (18.5 g/liter of catalyst) of the rhodium-carrying alumina/zirconium oxide. EXAMPLE 2 By the same method as in Example 1, a lower layer (110 g/liter of catalyst) of platinum-carrying alumina/cerium oxide was deposited on a monolithic carrier (1 liter). Then, rhodium-carrying alumina and a slurry were prepared by the same method as in Example 1 except that the amount of Rh in the aqueous solution of rhodium nitrate was decreased to 6.70 g. Subsequently, the specific gravity of the slurry was adjusted to 1.25 g/ml, and the process from deposition to calcination was carried out by the same method as in Example 1 to deposit 30 g of rhodium-carrying alumina (containing 0.17 g of Rh) and 7 g of zirconium oxide (total 37 g) were deposited on the monolithic carrier. The above steps gave a catalyst (sample No. 2) having a lower layer (110 g/liter of catalyst) of the platinum-carrying alumina/cerium oxide and an upper layer (37 g/liter of catalyst) of the rhodium-carrying alumina/zirconium oxide. COMPARATIVE EXAMPLE 1 By the same method as in Example 1, a lower layer (110 g/liter of catalyst) of platinum-carrying alumina/cerium oxide was deposited on a monolithic carrier (1 liter). Then, rhodium-carrying alumina was prepared by the same method as in Example 1 except that the amount of Rh in the aqueous rhodium nitrate solution was decreased to 3.35 g. Then, without adding pure water, a slurry was prepared by the same method as in Example 1. The specific gravity of the slurry was adjusted to 1.48 g/ml by adding pure water, and thereafter, the process from deposition to calcination was carried out by the same method as in Example 1 to deposit 60 g of the rhodium-carrying alumina (containing 0.17 g of Rh) and 14 g of zirconium oxide (total 74 g) on the monolithic carrier. The foregoing steps gave a catalyst (sample No. 3) having a lower layer (110 g/ liter of catalyst) of the platinum-carrying alumina/cerium oxide and an upper layer (74 g/liter of catalyst) of the rhodium-carrying alumina/zirconium oxide. COMPARATIVE EXAMPLE 2 By the same method as in Example 1, a lower layer (110 g/liter of catalyst) of platinum-carrying alumina/cerium oxide was deposited on a monolithic carrier (1 liter). Then, rhodium-carrying alumina was prepared by the same method as in Example 1 except that the amount of Rh in the aqueous rhodium nitrate solution was decreased to 2.23 g. Then, by the same method as in Comparative Example 1, a slurry was prepared. The specific gravity of the slurry was adjusted to 1.53 g/ml by adding pure water, and thereafter, the process from deposition to calcination was carried out by the same method as in Example 1 to deposit 90 g of the rhodium-carrying alumina (containing 0.17 g of Rh) and 21 g of zirconium oxide (total 111 g) on the monolithic carrier. The foregoing steps gave a catalyst (sample No. 4) having a lower layer (110 g/liter of catalyst) of platinum-carrying alumina/cerium oxide and an upper layer (111 g/liter of catalyst) of rhodium-carrying alumina/zirconium oxide. EXAMPLE 3 Platinum-carrying alumina and a slurry were prepared by the same method as in Example 1 except that the amount of Pt in the aqueous amine solution of hexahydroxoplatinic acid was increased to 42.10 g. The specific gravity of the slurry was adjusted to 1.30 g/ml by adding pure water, and then the process from deposition of the slurry on a monolithic carrier (1 liter) to calcination was carried out by the same method as in Example 1 to deposit 24 g of the platinum-carrying alumina (containing 0.83 g of Pt) and 9 g of cerium oxide (total 33 g) on the monolithic carrier. Subsequently, by the same method as in Example 1, an upper layer (37 g/liter of catalyst) of rhodium-carrying alumina/zirconium oxide was deposited on the carrier. The foregoing steps gave a catalyst (sample No. 5) having a lower layer (33 g/liter of catalyst) of the platinum-carrying alumina/cerium oxide and an upper layer (37 g/liter of catalyst) of the rhodium-carrying alumina/zirconium oxide. EXAMPLE 4 Platinum-carrying alumina and a slurry were prepared by the same method as in Example 1 except that the amount of Pt in the aqueous amine solution of hexahydroxoplatinic acid was increased to 21.05 g. The specific gravity of the slurry was adjusted to 1.43 g/ml by adding pure water, and then by the same method as in Example 1, the process from deposition of the slurry on a monolithic carrier (1 liter) to calcination was carried out by the same method as in Example 1 to deposit 48 g of the platinum-carrying alumina (containing 0.83 g of Pt) and 18 g of cerium oxide (total 66 g) on the monolithic carrier. Subsequently, by the same method as in Example 1, an upper layer (37 g/liter of catalyst) of rhodium-carrying alumina/zirconum oxide was deposited on the carrier. The above steps gave a catalyst (sample No. 6) having a lower layer (66 g/liter of catalyst) of the platinum-carrying alumina/cerium oxide and an upper layer (37 g/liter of catalyst) of the rhodium-carrying alumina/zirconium oxide. EXAMPLE 5 Platinum-carrying alumina was prepared by the same method as in Example 1 except that the amount of Pt in the aqueous amine solution of hexahydroxoplatinic acid was decreased to 9.72 g. A slurry was then prepared by the same method as usd in Example 1 except that the amount of pure water was decreased to 450 ml. The specific gravity of the slurry was adjusted to 1.62 g/ml by adding pure water. Thereafter, the process from the deposition of the slurry on a monolithic carrier (1 liter) to calcination was carried out in the same way as in Example 1 to deposit 104 g of the platinum-carrying alumina (containing 0.83 g of Pt) and 39 g of cerium oxide (total 143 g) on the monolithic carrier. Subsequently, by the same method as in Example 1, an upper layer (37 g/liter of catalyst) of rhodium-carrying alumina/zirconium oxide was deposited on the carrier. The foregoing steps gave a catalyst (sample No. 7) having a lower layer (143 g/liter of catalyst) of the platinum-carrying alumina/cerium oxide and an upper layer (37 g/liter of catalyst) of the rhodium-carrying alumina/zirconium oxide. EXAMPLE 6 Platinum-carrying alumina and a slurry were prepared by the same method as in Example 1 except taht the amount of Pt in the aqueous amine solution of hexahydroxoplatinic acid was decreased to 7.98 g. The specific gravity of the slurry was adjusted to 1.64 g/ml by adding pure water. Thereafter, the process from the deposition of the slurry on a monolithic carrier (1 liter) to calcination was carried out in the same way as in Example 1 to deposit 128 g of the platinum-carrying alumina (containing 0.83 g of Pt) and 48 g of cerium oxide (total 176 g) on the monolithic carrier. Subsequently, by the same method as in Example 1, an upper layer (37 g/liter of catalyst) of rhodium-carrying alumina/zirconium oxide was deposited on the carrier. The foregoing steps gave a catalyst (sample No. 8) having a lower layer (176 g/liter of catalyst) of the platinum-carrying alumina/cerium oxide and an upper layer (37 g/liter of catalyst) of the rhodium-carrying alumina/zirconium oxide. COMPARATIVE EXAMPLE 3 A lower layer (110 g/liter of catalyst) of platinum-carrying alumina/cerium oxide was deposited on a monolithic carrier having the same size as in Example 1 by the same method as in Example 1. Then, rhodium-carying aluminum was prepared by the same method as in Example 1. The process from the preparation of a slurry (specific gravity 1.18 g/ml) to deposition and calcination was carried out by the same method as in Example 1 except that zirconyl acetate was not added, thereby to deposit 30 g of the rhodium-carrying alumina (containing 0.17 g of Rh) further on the monolithic carrier. The foregoing steps gave a catalyst (sample No. 9) having a lower layer (110 g/liter of catalyst) of the platinum-carrying alumina/cerium oxixde and an upper layer (30 g/liter of catalyst) of the rhodium-carrying alumina. COMPARATIVE EXAMPLE 4 Platinum-carrying alumina was preapared by the same method as in Example 1, and then without adding cerium oxide, a slurry was prepared by the same method as in Example 1. The specific gravity of the slurry was adjusted to 1.48 g/ml by adding pure water. By the same method as in Example 1, the process from deposition of the slurry on a monolithic carrier having the same size as in Example 1 to calcination was carried out to deposit 80 g of the platinum-carrying alumina (containing 0.83 g of Pt). Subsequently, by the same method as in Example 1, an upper layer (37 g/liter of catalyst) of rhodium-carrying alumina/zirconum oxide was deposited on the carrier. The foregoing steps gave a catalyst (sample No. 10) having a lower layer (80 g/liter of catalyst) of the platinum-carrying alumina and an upper layer (37 g/liter of catalyst) of the rhodium-carrying alumina/zirconium oxide. COMPARATIVE EXAMPLE 5 By the same method as in Comparative Example 1, a lower layer of platinum-carrying alumina (80 g/ml of catalyst) was formed on a monolithic carrier having the same size as in Example 1. Then, by the same method as in Comparative Example 3, a layer (30 g/liter of catalyst) of rhodium-carrying alumina was deposited on it to form a catalyst (sample No. 11). EXAMPLE 7 Example 1 was repeated except that a monolithic carrier having the same volume as in Example 1 (1 liter) but having 62 cells/cm² [400 cells/in²] was used. There was obtained a catalyst (sample No. 12) having a lower layer (110 g/liter of catalyst) of platinum-carrying alumina and cerium oxide and an upper layer (37 g/liter of carrier) of rhodium-carrying alumina/ zirconium. Test for the performance of the catalyst Each of the catalysts (samples Nos. 1 to 12) obtained in Examples 1 to 7 and Comparative Examples 1 to 5 was calcined in a muffle furnace at 950°C for 6 hours. A model gas composed of 1.0% of CO, 500 ppm of C₃H₆, 0.1% of NO, 0.33% of H₂, 0.845% of O₂, 14% of CO₂, 10% of H₂O and the balance being N₂ gas was passed over the calcined catalyst at a space velocity of 5 x 10⁴ hr⁻¹, and the conversions of substances to be controlled (CO, C₃H₆, NO) were examined. The temperature of the reaction gas was adjusted to 370°C. The results are shown in Table 1. It is seen from Table 1 that when the amount of the inside layer (the lower layer) is constant, the ratios of removal of CO, C₃H₆ and NO rapidly decrease if the amount of the outside layer (upper layer) exceeds about 60 g/liter (Examples 1 and 2, Comparative Examples 1 and 2). It is seen on the other hand that when the amount of the second layer (upper layer) is kept constant, variations in the amount of the first layer (lower layer) do not substantially affect the ratios of removal of CO, C₃H₆ and NO (Examples 3 to 6). The use of a monolithic carrier having 400 cells (Example 7) gives the same excellent effects of removing CO, C₃H₆ and NO as in the case of using a monolithic carrier having 300 cells (Examples 1 to 6). The ratios of removal of CO, C₃H₆ and NO are drastically reduced when the first layer (lower layer) does not contain cerium oxide [Comparative Example 3], the second layer (upper layer) does not contain zirconium oxide [Comparative Example 4] and the first layer (lower layer) does not contain cerium oxide and the second layer (upper layer) does not contain zirconium oxide [Comparative Example 5]. 4. Brief Description of the Drawing Figure 1 is a catalyst model used in calculating the thicknesses of the first layer (lower layer) and the second layer (upper layer) of the catalyst in accordance with this invention. 1.....monolithic support; 2.....first layer (lower layer); 3.....second layer (upper layer).

Claims: A catalyst for purifying exhaust gases essentially comprising a substantially catalytically inert, refractory monolithic support, a first layer containing a catalytically active refractory oxide formed on the support, and a second layer containing a catalytically active refractory oxide formed on the first layer, characterized in that the first layer contains cerium oxide and platinum and has a weight of 10 to 200g per litre of the catalyst, and the second layer has a weight of 5 to 60g per litre of the catalyst and contains i) rhodium in an amount of from 0.002 to 2g per litre of catalyst, and ii) a zirconium compound. The catalyst set forth in claim 1 wherein the support has continuous longitudinal unobstructed flow channels each extending through the support and defined by a thin wall, the first layer is deposited on the walls of the channels, and the catalytically active refractory oxide of one or both layers is finely divided and has a specific surface area of at least about 10m²/g. The catalyst set forth in claim 1 or claim 2 wherein the first layer has a thickness of 5 to 110 microns, and the second layer has a thickness of 3 to 35 microns. The catalyst set forth in any preceding claim wherein the catalytically active refractory oxide is active alumina. The catalyst set forth in any one of claims 1 to 4 wherein the support is composed of refractory metal or refractory metal oxide. The catalyst set forth in claim 5 wherein the support is composed of cordierite. The catalyst set forth in any of claims 1 to 6 wherein the weight of cerium oxide is 15 to 40% by weight based on the weight of the first layer. The catalyst set forth in any of claims 1 to 7 wherein the weight of platinum is 0.1 to 3.5% by weight based on the weight of the first layer. The catalyst set forth in any of claims 1 to 8 wherein the zirconium compound is zirconium oxide. The catalyst set forth in any of claims 1 to 9 wherein the weight of the zirconium compound is 10 to 30% by weight based on the weight of the second layer. The catalyst set forth in any of claims 1 to 9 wherein the weight of rhodium is 0.05 to 2.00% by weight based on the weight of the second layer. A process for producing a catalyst according to any preceding claim which comprises depositing a first slurry containing a finely divided catalytically active refractory oxide and/or its precursor, cerium oxide or another cerium compound, and platinum or a platinum compound on a substantially catalytically inert refractory monolithic support, drying the support having the first slurry deposited thereon, thereafter depositing a second slurry containing a finely divided catalytically active refractory oxide and/or its precursor, zirconium oxide or another zirconium compound and rhodium or a rhodium compound on the support, and calcining the support having the second slurry deposited thereon. The process set forth in claim 12 wherein the platinum compound in the first slurry is platinum hydroxide. The process set forth in claim 12 or claim 13 wherein the rhodium compound in the second slurry is rhodium nitrate. The process set forth in any of claims 12 to 14 wherein the zirconium compound in the second slurry is zirconyl acetate.

Inventors: CHIBA, TADAO NUMAZU FACTORY, FUNABIKI, MASAKI NUMAZU FACTORY, WATANABE, TSUNAO NUMAZU FACTORY
Applicants: ENGELHARD CORPORATION
Application year: 1987
Main classification: B01D53
IPC codes: B01J35, B01J23, B01D53, B01J37