STABILIZED AROMATIC POLYESTER COMPOSITIONS

Abstract: An aromatic polyester composition comprising an aromatic polyester derived from terephthalic acid and/or isothalic acid and a bisphenol and a stabilizer chosen from P-containing organic esters, O, S, or F-containing organic compounds or their mixtures.

Description: This invention relates to a stabilized aromatic polyester composition and, more specifically, to a stabilized aromatic polyester composition including certain O-containing organic compounds or their mixtures. The aromatic polyester used in this invention is obtained from terephthalic acid and/or functional derivatives thereof; isophthalic acid and/or functional derivatives thereof; or mixtures thereof (with the terephthalic acid/isophthalic acid unit mole ratio being about 9:1 to about 1:9) and a bisphenol of the following general formula (I) wherein -X- is selected from the group consisting of -O-, -S-, -SO₂-,-SO-, -CO-, an alkylene group containing 1 to 4 carbon atoms, and an alkylidene group containing 1 to 4 carbon atoms, and R₁, R₂, R₃, R₄, R₁', R₂', R₃', and R₄', which may be the same or different, each represent a member selected from the group consisting of a hydrogen atom, a chlorine atom, a bromine atom and an alkyl group containing 1 to 4 carbon atoms, or functional derivatives thereof. Known methods of producing such an aromatic polyester include, for example, an interfacial polymerization method which involves mixing an aromatic dicarboxylic acid chloride dissolved in a water-immiscible organic solvent with an alkaline aqueous solution of a bisphenol, a solution polymerization method which comprises heating a bisphenol and an acid chloride in an organic solvent, and a melt polymerization method which comprises heating a phenyl ester of an aromatic dicarboxylic acid and a bisphenol, e.g., as disclosed in U.S. Pat. Nos. 3,884,990 and 3,946,091. It is also known that aromatic polyesters derived from aromatic dicarboxylic acids and bisphenols have superior properties to polyesters derived from aromatic dicarboxylic acids and aliphatic alkylene glycols. Specifically, these polyesters have many superior characteristics, e.g., mechanical properties such as tensile strength, elongation, flexural strength, flexural recovery and impact strength, heat-distortion temperature, dimensional stability, electrical properties, and fire retardency. Because of these superior properties, these polyesters are known to be useful in a wide range of fields as various molded articles, films, fibers, and coating materials obtained by extrusion molding, injection molding, etc. The aromatic polyesters obtained by the above methods frequently assume yellow or brown colors in their as-prepared state. It is also noted that aromatic polyesters turn yellow when heated during injection molding, extrusion molding and other shaping operations which are used to form ordinary molded products or films. Such coloration is extremely inconvenient when a lack of color in the resulting molded articles is important. Furthermore, when a pigment is incorporated into a molding composition to obtain a desired color, the color of the final molded product frequently is quite different from the desired color. The aromatic polyesters used in this invention have a high heat distortion temperature, and therefore, are frequently used under high temperature conditions. The above-described coloration, however, proceeds generally under high temperature conditions and impairs the transparency of the molded product. Consequently, such a product cannot be used in applications which require transparency and a lack of color at high temperatures. Such a coloration is also considered to occur with the decomposition of the polymer. Thus, coloration is synonymous with an irregular reduction in the logarithmic viscosity number (intrinsic viscosity) of the polymers constituting the molded articles. Coloration and reduction of intrinsic viscosity deteriorates the useful properties of these polymers and are therefore extremely disadvantageous in obtaining products which are uniform. A first object of this invention is to provide an aromatic polyester composition that is stabilized against heat and which can be used to produce molded articles which are free from coloration and which do not develop coloration even in use at high temperatures. A second object of the invention is to provide an aromatic polyester composition which is stabilized against decomposition and reduction of intrinsic viscosity at elevated temperatures. Extensive investigations have been made in order to remove the defects of aromatic polyesters described above. These investigations led to the discovery that the above-described undesirable coloration or heat decomposition and intrinsic viscosity reduction of aromatic polyesters can be markedly reduced by adding specified amounts of at least one specific oxygen-containing compound to the aromatic polyester and that very stable aromatic polyester compositions are provided. Accordingly, the present invention provides an aromatic polyester composition which comprises: (A) an aromatic polyester derived from (a) terephthalic acid and/or a functional derivative thereof; or isophthalic acid and/or a functional derivative thereof; or mixtures thereof with the terephthalic acid unit/isophthalic acid unit mole ratio being about 9:1 to about 1:9 and (b) a bisphenol of the general formula (I) wherein -X- is selected from the group consisting of -O-, -S-, -SO₂-,-SO-, -CO-, an alkylene group containing 1 to 4 carbon atoms, and an alkylidene group containing 1 to 4 carbon atoms, and each of R₁, R₂, R₃, R₄, R₁', R₂', R₃', and R₄', which may be the same or different, is a member selected from the group consisting of a hydrogen atom, a chlorine atom, a bromine atom and an alkyl group containing 1 to 4 carbon atoms, or functional derivatives thereof and (B) a stabilizer comprising a compound selected from certain oxygen-containing compounds specified hereinafter. The amount of the stabilizer to be added relative to the aromatic polyester (A) will vary depending upon the specific stabilizer used. Broadly, the stabilizer will be present in amounts from 0.01 to 2% by weight relative to the aromatic polyester (A). Molded products made from the aromatic polyester composition of this invention have markedly reduced coloration, and, even when exposed to high-temperature conditions, the molded products develop little coloration and show good stability to heat. The aromatic polyester used in this invention is obtained from terephthalic acid and/or isophthalic acid and/or functional derivatives thereof and a bisphenol of the following general formula (I) wherein -X- is selected from the group consisting of -O-, -S-, -SO₂-,-SO-, -CO-, an alkylene group containing 1 to 4 carbon atoms, and an alkylidene group containing 1 to 4 carbon atoms, and R₁, R₂, R₃, R₄, R₁', R₂', R₃', and R₄', which may be the same or different, are each selected from the group consisting of a hydrogen atom, a chlorine atom, a bromine atom and an alkyl group containing 1 to 4 carbon atoms, or functional derivatives thereof. A mixture of about 90 to about 10 mole% of terephthalic acid and/or a functional derivative thereof and about 10 to about 90 mole% of isophthalic acid and/or a functional derivative thereof is preferred for use as the acid component to be reacted with the bisphenol to prepare the aromatic polyester as referred to in this invention. Preferably, a mixture of 20 to 80 mole% of terephthalic acid and/or a functional derivative thereof and 80 to 20 mole% of isophthalic acid and/or a functional derivative thereof is used. The molar ratio of bisphenol to the sum of the terephthalic acid units and isophthalic acid units is substantially equimolar. Suitable function derivatives of terephthalic or isophthalic acid which can be used include acid halides, dialkyl esters and diaryl esters. Preferred examples of acid halides include terephthaloyl dichloride, isophthaloyl dichloride, terephthaloyl dibromide and isophthaloyl dibromide. Preferred examples of dialkyl esters include dialkyl esters of terephthalic and isophthalic acids containing 1 to 6 (especially 1 to 2) carbon atoms in each alkyl moiety thereof. Preferred examples of diaryl esters include diphenyl terephthalate and diphenyl isophthalate. Examples of suitable bisphenols of the general formula (I) above are 4,4′-dihydroxy-diphenyl ether, bis(4-hydroxy-2-methylphenyl) ether, bis(4-hydroxy-3-chlorophenyl) ether, bis(4-hydroxyphenyl) sulfide, bis(4-hydroxyphenyl) sulfone, bis(4-hydroxyphenyl) ketone, bis(4-hydroxyphenyl)methane, bis(4-hydroxy-3-methylphenyl)methane, bis(4-hydroxy-3,5-dichlorophenyl)methane, bis(4-hydroxy-3,5-dibromophenol)methane, 1,1-bis(4′-hydroxyphenyl)ethane, 2,2-bis(4′-hydroxy-3′-methylphenyl)propane, 2,2-bis(4′-hydroxy-3′-chlorophenyl (propane, 2,2-bis(4′-hydroxy-3′, 5′-dichlorophenyl)propane, 2,2-bis(4′-hydroxy-3,5′-dibromophenyl)propane, and 1,1-bis(4′-hydroxyphenyl)-n-butane. 2,2-bis(4′-hydroxyphenyl)propane, bisphenol A, is most typical and is readily available, and, accordingly, is most often used. Typical examples of functional derivatives of bisphenols which can be used are the metal salts thereof and the diesters thereof with aliphatic monocarboxylic acids containing 1 to 3 carbon atoms. Preferred functional derivatives of the bisphenols are the sodium salts, the potassium salts, and the diacetate esters thereof. The bisphenols may be used either alone or as a mixture of two or more thereof. To produce these aromatic polyesters, the interfacial polymerization method which comprises mixing a solution of an aromatic dicarboxylic acid chloride in a water-immiscible organic solvent with an alkaline aqueous solution of bisphenol, the solution polymerization method which comprises heating a bisphenol and an acid chloride in an organic solvent, and the melt polymerization method which comprises heating a phenyl ester of an aromatic dicarboxylic acid and bisphenol, which are described in detail in U.S. Pat. Nos. 3,884,990, and 3,946,091, can, for example, be employed. In order to insure the aromatic polyesters used in this invention have good physical properties they should have an intrinsic viscosity (IV), defined by the following relationship, of about 0.3 to about 1.0, preferably 0.4 to 0.8, wherein t₁ is the falling time (in seconds) of a solution of the aromatic polyester in a solvent; t₂ is the falling time (in seconds) of the solvent; C is the concentration (in g/dl) of the aromatic polyester in the solution; and K' is a constant. For the aromatic polyesters of this invention K' will be about 0.42. The intrinsic viscosity, as used herein, is determined in 1,1,2,2-tetrachloroethane at 30°C. While any of the interfacial polymerization method, solution polymerization method and melt polymerization method described above can be used to produce the aromatic polyesters used in this invention, it has been found that, depending on the polymerization method used, differing amounts of stabilizer are required for effectiveness in reducing coloration and polymer decomposition. Thus, the melt polymerization method of forming the aromatic polyester is preferred. In certain circumstances, the amount of stabilizer added to a melt polymerized aromatic polyester required to achieve the objectives of this invention can be substantially reduced relative to amounts of stabilizer which might be expected to yield improvements when added to interfacially polymerized aromatic polyesters. The present polymerization process is carried out in the presence of an acidic, neutral or basic catalyst, such classifications being based on the reaction of a conventional acid-base indicator and the catalyst when the latter is dissolved in a polar ionizing solvent such as water. More preferably, a basic catalyst is employed. Prior to its introduction into the reaction mass, the preferred basic catalyst is preferably converted to liquid form, e.g. by melting or by dissolution in a liquid or normally solid, low melting solvent. Suitable basic catalysts include the alkali metals, such as lithium, sodium, potassium, rubidium, cesium and francium and the carbonates, hydroxides, hydrides, borohydrides, phenates, bisphenates, (i.e. salt of a bisphenol or bisphenol), carboxylates such as acetate or benzoate, oxides of the foregoing alkali metals. Group II and III elements can also be used in place of the alkali metals of the foregoing classes of compounds such as metals and compounds of calcium, magnesium and aluminum. Other bases include trialkyl or triaryl tin hydroxides, acetates, phenates, and the like. Examples of catalysts are lithium, sodium, potassium, rubidium, cesium and francium metals, potassium or rubidium carbonate, potassium hydroxide, lithium hydride, sodium borohydride, potassium borohydride, calcium acetate, magnesium acetate, aluminum triisopropoxide and triphenyl tin hydroxide. Phenol is the preferred solvent for the normally solid catalysts. Substituted phenols which can be used include those having the formula wherein R is alkyl of 1 to 10 carbon atoms, alkoxy of 1 to 10 carbon atoms, aryl of 6 to 10 carbon atoms, chloro, bromo or mixtures thereof, and wherein n is 1 or 2. Typical solvents include o-benzyl phenol, o-bromo phenol, m-bromo phenol, m-chloro phenol, p-chloro phenol, 2,4 dibromo phenol, 2,6 dichloro phenol, 3,5 dimethoxy phenol, o-ethoxy phenol, m-ethyl phenol, p-ethyl-phenol, o-isopropyl phenol, m-methyoxy phenol, m-propyl phenol, p-propyl phenol, and the like. Other solvents which are particularly useful are of the ether type, for example, tetrahydrofuran and the various glymes, for examples, ethylene glycol dimethylether and the like. Combinations of catalyst and combinations of phenols or phenols and solvents may also be used. Especially preferred liquid basic catalysts are charged dissolved in molten normal solid-low melting organic solvent such as phenol. Especially preferred catalysts providing excellent results are the basic catalysts, rubidium phenoxide, potassium phenoxide, and potassium borophenoxide, each dissolved in molten phenol. Preferably, also when a basic catalyst is employed, the catalyst is introduced concurrently with the aforementioned molten reactants to the polymerization reactor to avoid heating the reactants in the presence of the catalyst prior to onset of the polymerization. Less preferred catalysts include the metal oxides, metal acetates, titanium and tin compounds. Suitable metal oxides include antimony trioxide, germanium oxide, arsenic trioxide, lead oxide, magnesium oxide, and zinc oxide. Suitable metal acetates include cobalt acetate, zinc acetate, cadmium acetate and manganese acetate. Suitable titanium compounds include the organic titanates such as tetrabutyl titanate and tetraisopropyl titanate. Suitable tin compounds include dibutyloxide, dibutyl tin methoxide and dibutyl tin dilaurate. In accordance with conventional reaction practice, a catalytically effective amount of the catalyst is employed, for example, about 0.005 to about 2 mol percent or more, preferably about 0.01 to 1 mole percent of the bisphenol in accordance with known techniques of polyester formation. The present process can be carried out employing, in general, conditions which are conventional for melt polymerization. According to the conventional practice, the solid reactants are heated above about 100°C, preferably above about 160°C to melt the reactants. Onset of reaction in the presence of catalyst is generally at a temperature ranging from above about 100°C to about 275°C, for example, above about 160°C for reaction of bisphenol A, diphenyl terephthalate and diphenyl isophthalate. The reaction temperature employed is generally above about 100°C to about 400°C or higher, preferably above about 175°C to about 350°C, more preferably about 175°C to about 330°C with the reaction temperature being raised gradually during the polymerization. In the reaction, the aryl group of the diester is displaced as the corresponding relatively volatile monohydroxy aromatic compound, e.g. phenol, for which provision is made for removal e.g. by distillation from the reaction mixture during the tranesterification. Reaction pressure is generally diminished during the reaction, e.g. of about 0.1 mm. of mercury or lower, to aid in the aforementioned removal of the monohydroxy aromatic compound. Generally, it is preferable in accordance with the prior art to carry out reaction in two stages. The first or prepolymerization stage is carried out at above about 100°C to about 350°C preferably about 160°C to about 330°C, especially about 180°C to about 300°C to prepare a low molecular weight pplyester or prepolymer of relatively low intrinsic viscosity, e.g. of less than about 0.1 to about 0.3 dl./g. A subsequent polymerization stage in which the prepolymer is heated at a somewhat higher temperature namely, at above about 200°C to about 400°C or higher, preferably at about 225°C to about 350°C, especially at about 275°C to about 330°C. Conveniently, the polymerization stage is carried out in a different reaction vessel from that employed in the prepolymerization reaction stage with effective agitation of reaction mixture in both stages with generally more extreme agitation being used in the polymerization. In carrying out the present invention, it is preferred prior to catalyst addition to melt the normally sold reactants to provide molten reactants and then heat the reactants if necessary to a temperature sufficient for onset of polymerization. According to this embodiment, a basic catalyst for the polymerization that is normally solid at 30°C is then introduced in the liquid form to the polymerization concurrent with the molten reactants. According to another preferred embodiment of the invention, there is contemplated a semi-continuous process for polymerization wherein the prepolymerization stage of the process is carried out batchwise and the subsequent polymerization stage is carried out substantially continuously in one or more counter-current flow mechanically agitated thin film or wiped film reactors. As an alternative to the aforementioned semi-continuous mode of operation, another preferred embodiment of the invention contemplates a fully continuous polymerization wherein, the prepolymerization is carried out in one or more stirred tank reactors, and preferably, the polymerization stage is carried out in one or more of the aforementioned wiped film reactors or thin film reactors. It is especially preferred in carrying out semi- or fully continuous polymerization according to the aforementioned preferred modes of operation to complete polymerization in a polymerization reaction zone wherein the aforementioned wiped film reactor is followed by a multi-screw extrusion reaction vessel. A persistent problem in the preparation of linear polyesters of bisphenol and dicarboxylic acids has been the undesirable high color in the product, i.e. the tendency of the polyester to develop an undesirable yellow color during the polyesterification. The color is attributed to thermal decomposition of the product polyester and/or the reactants in the reaction which is carried out at high temperatures ranging up to 400°C, or higher, and generally in the melt, i.e. without the use of a diluent. In accordance with this invention various stabilizers have been found which when added to the aromatic polyesters of this invention greatly improve the undesirable coloration and depolymerization which typically develop. The oxygen-containing organic compound utilized in this invention is a polyphenylene oxide having the general formula VII. The polyphenylene oxide (VII) may be used as the sole stabilizer (B). In certain other embodiments of this invention, the stabilizer (B) consists of a mixture of a polyphenylene oxide with at least one member selected from certain organophosphorus, organosulfur and fluorocarbon compounds, as specified below. The organophosphorus compounds which are useful as stabilizers in the present invention include phenyl phosphates having the following general formula II. wherein R is H, alkyl or aryl. The preferred phosphate stabilizer is diphenyl phosphate. Additionally, phenyl phosphites are also applicable in this invention including those having structural formulas III, and IV. Diphosphites having structural formulas V and VI are also useful in stabilizing the aromatic polyester compositions of this invention. The organosulfur compound which is useful comprises 2-mercaptobenzimidazole which has the following structure (VIII). Additionally, a fluorocarbon wax is also useful as a stabilizer in the present invention. Such wax will have the following structural formula (IX). The amount of the stabilizer to be added to the aromatic copolyester differs according to the type of the stabilizer used, but should be 0.01 to 2% by weight, and is generally less than 2% by weight, preferably 0.02 to 1.0% by weight, based on the weight of the aromatic copolyester. If the amount of the stabilizer is less than 0.01% by weight, the effect of preventing coloration and heat decomposition is not sufficient, and if the amount of the stabilizer exceeds 2% by weight, the dynamic properties of the aromatic copolyester tend to deteriorate. Various methods can be used to add the stabilizer to the aromatic polyester. In the interfacial polymerization method in which a solution of a dicarboxylic acid chloride in an organic solvent and an alkaline aqueous solution of a bisphenol are stirred, the stabilizer can be added to either one of the monomers prior to polymerization. When the polymerization product is isolated as a solution of the aromatic polyester after the polymerisation, a solution of the stabilizer may be added to the aromatic polyester solution. When the aromatic polyester is isolated as a solid, the stabilizer can of course be simply added to the aromatic polyester. Furthermore, the stabilizer may be incorporated in the aromatic polyester by immersing the aromatic polyester in a solution or suspension of the stabilizer in a solvent such as methanol or acetone, and removing the solvent by evaporation after the immersion. In the preferred method of melt polymerization, the stabilizer may be fed together with the monomers at the time of polymerization. Alternatively, the stabilizer may be added to chips or powders of the aromatic polyester during a molding operation such as injection molding, extrusion molding, etc. If the stabilizer is added to a powder or chips of the aromatic polyester and the mixture is molded; molded articles having a uniform color and uniform characteristics can be obtained. It is preferred in melt polymerization to add organophosphorus stabilizers at the beginning of melt polymerization in order to have the antioxidant advantage as soon as possible. However, if there is any moisture present, the organophosphorus esters hydrolyze and form free acids that may neutralize the polymerization catalyst. Therefore, it is better to add this type of stabilizer at some intermediate polymerization stage where the presence of moisture is not very likely. It should also be recognized that the presence of the stabilizer in the polymer as it is made gives better color stability on heating than if the same product is added to a polymer that is made without any stabilizer. The aromatic polyester composition of this invention may further contain various other additives such as antioxidants, ultravoilet absorbers, antistatic agents and fire retardants, as needed according to the purpose of use. For example, the effect of the present invention can be increased further by adding the stabilizer in conjunction with an antioxidant. Examples of suitable antioxidants are conventional phenolic antioxidants, phosphite-type antioxidants, amine-type antioxidants sulfur-containing compounds, organometallic compounds, and epoxy compounds. In addition, plasticizers, pigments and lubricants can also be incorporated in the aromatic polyester composition of this invention. Alternatively the aromatic polyester composition may be reinforced with glass fibers. When an aromatic halogen compound such as decabromodiphenyl oxide is added to a resin composition to render the resin composition fire retardant, a molded article prepared from the composition frequently turns yellowish brown presumably due to heat decomposition. In such a case, too, the aromatic polyester composition of this invention is stabilized against heat, and coloration is markedly prevented. If desired, the aromatic polyester composition of this invention may contain at least one additional polymer such as polyalkylene terephthalates (e.g., polyethylene terephthalate or polybutylene terephthalate), poly(ethylene oxybenzoate), polycarbonates, polyethylene, polypropylene, polyamides, polyurethanes, polystyrene, ABS resins, EVA copolymers, polyacrylates, polytetrafluoroethylene, polymethyl methacrylates, polyphenylene sulfide, and rubbers. In other words, a mixture of the aromatic polyester and another polymer exemplified above can be used. The stabilizer used in this invention exhibits a marked effect in this case, too. A decrease in the degree of coloration or degradative decomposition of the aromatic polyester composition of this invention occurs when such is exposed to heat during molding or used at high temperatures. Hence, the aromatic polyester compositions of this invention can be used to form many useful articles employing generally known molding methods such as injection molding, extrusion molding or press molding. Typical examples of final products obtained by molding are films, monofilaments, and injection molded articles such as machine parts, automobile parts, electrical component parts, vessels and springs. The aromatic polyester compositions of this invention also are particularly useful as engineering plastics for various applications where the excellent properties of aromatic polyesters are required. The following examples are given to illustrate the present invention in more detail. It should be noted that the invention is in no way to be construed as being limited to these Examples. Unless otherwise indicated all parts, percents, ratios and the like are by weight. EXAMPLE 1 18.492 Kg (81.0 moles) bisphenol A and 25.910 Kg (81.4 moles) 75/25 diphenyl iso/terephthalate were dried and charged to a melt tank under nitrogen. When molten (about 180°C), the monomers were transferred to a stirred reactor (nitrogen blanketed). 0.041 moles of potassium phenate catalyst in phenol were charged to the stirred reactor (100 cc catalyst + solution). Vacuum was applied gradually and the temperature raised. After about 2 1/2 hours, the temperature was about 280°C, pressure about 70 mmHg (9.33 kPa) and the intrinsic viscosity (measured in 1,1,2,2 tetrachloroethane at 30°C) was about 0.17 dl/g. The material was gradually transferred to a vertical falling film reactor at about 300°C and about 5 mmHg (0.67 kPa) absolute where an intrinsic viscosity of about 0.4 dl/g was reached and finally to a twin screw vented extruder at about 330°C and 0.8 mmHg (0.11 kPa) where the intrinsic viscosity reached 0.58 - 0.61 dl/g. The material was light yellow, clear and tough and was pelletized as it was extruded after cooling. A batch of the above material was blended to assure uniformity. About 10% of the material was ground to about 0.5 mm mesh using a small grinder. The polymer was dried at about 120°C overnight in a vacuum oven prior to use. In each instance below, 20 grams of the finely ground polymer was blended with the stabilizer additive in a micromill. The material was then blended with 280 grams of the pelletized polymer, keeping the material as dry as possible throughout the whole procedure. The blended material was extruded at 370°C in a Brabender single screw extruder through a slit die (340°C). The extrudate was cut into pieces about 6 inches (15.24 cm) long. Several of the pieces were compression molded to about 30 mils (0.762 mm) in a Carver Press at about 500°F (260°C). A piece of extrudate and a compression molded sample of each type along with a control sample were aged at 170°C in a circulating air oven. A piece of each extrudate was also immersed in boiling water. After weekly intervals, the I.V. of the extrudate samples and the color of the compression molded samples were checked. The results of the testing are summarized in Table 1. It can be seen from Table 1 that substantial reduction in loss of intrinsic viscosity on aging has occurred with the samples containing the stabilizing additives as compared to the control sample without additive. EXAMPLE 2 Samples of the polyester and the polyphenylene oxide stabilizer were formed into a film by casting a film (about 4 mils (0.102mm) thick) in a flat dish from a solution of the polyester containing the additive. The film was air dried. The I.V. of the air dried film as well as color were inspected periodically. The results are shown in Table 2. Additive Level Intrinsic Viscosity (dl/g) 22 days 43 days None - 0.55 0.50 PPO 1.0 0.60 0.57 PPO 0.25 0.58 0.53 From Table 2, it can be seen that the polyphenylene oxide stabilizes the aromatic polyester and is slightly more effective at the 1.0 wt.% level than at the lower level. In addition, it was observed that the samples containing polyphenylene oxide darkened much more than the control sample. Referring to Table 1, it can be seen that when polyphenylene oxide is used in combination with a phosphite, the stabilizing activity is quite good and its color stability is improved

Claims: A resin composition comprising: (A) an aromatic polyester produced by polymerization of a substantially equimolar mixture of the monomeric components (a) terephthalic acid and/or an acid halide, dialkyl ester or diaryl ester thereof and/or isophthalic acid and/or an acid halide, dialkyl ester or diaryl ester thereof, with the terephthalic acid unit/isophthalic acid unit mole ratio being about 9:1 to about 1:9, and (b) at least one bisphenol of the general formula (I) wherein -X- is selected from the group consisting of -O-, -S-, -SO₂-, -SO-, -CO-, an alkylene group containing 1 to 4 carbon atoms or an alkylidene group containing 1 to 4 carbon atoms, and R₁, R₂, R₃, R₄, R₁', R₂', R₃' and R₄', which may be the same or different, are each selected from the group consisting of a hydrogen atom, a chlorine atom, a bromine atom or an alkyl group containing 1 to 4 carbon atoms, or a metal salt or diester of said bisphenol of the general formula (I), and (B) from 0.01 to 2% by weight, based on the aromatic polyester (A), of a stabilizer selected from (1) an oxygen-containing organic stabilizer comprising polyphenylene oxide having the general formula (VII), and (2) a mixture of a polyphenylene oxide having the general formula (VII) given above and at least one member of the group consisting of (a) phenyl phosphates having the general formula (II): wherein R is hydrogen, alkyl or aryl, (b) phenyl phosphites having structural formulas III or IV, (c) diphosphites having the structural formulas V or VI, (d) a sulphur-containing organic stabilizer comprising 2-mercaptobenzimidazole, and (e) a fluorocarbon wax having the general formula (IX) The composition of claim 1 wherein said aromatic polyester is produced by polymerizing a mixture of said terephthalic acid and isophthalic acid units with said bisphenol. The composition of claim 2 wherein said mixture comprises a mixture of diaryl esters of said terephthalic acid and isophthalic acid. The composition of claim 3 wherein said diaryl ester is a diphenyl ester. The composition of any of claims 1 to 4 wherein said bisphenol is bisphenol A. The composition of any of claims 1 to 5 wherein the mole ratio of the terephthalic acid unit to the isophthalic acid unit is 8:2 to 2:8. The composition of claim 6 wherein the mole ratio of terephthalic acid unit to isophthalic acid unit is 1:3. The composition of any of claims 1 to 7 wherein said stabilizer is said polyphenylene oxide of general formula VII. The composition of any of claims 1 to 7 wherein said stabilizer is a mixture of polyphenylene oxide and the phosphite of formula V. The composition of any of claims 1 to 9 wherein said aromatic polyester is formed by melt polymerization of said terephthalic and/or isophthalic acid units and said bisphenol. The composition of any of claims 1 to 10, wherein the stabilizer (B) is present in an amount of at least 0.01% but less than 2% by weight, relative to the aromatic polyester (A). The composition of any of claims 1 to 10, wherein the stabilizer (B) is present in an amount of from 0.02 to 1.0% by weight, relative to the aromatic polyester (A). The composition of any of claims 1 to 11 wherein said stabilizer is polyphenylene oxide in an amount of at least 1.0 wt.% based on said aromatic polyester. A process for the preparation of an aromatic polyester comprising polymerizing a substantially equimolar mixture of the monomeric reactants (a) terephthalic acid and/or an acid halide, dialkyl ester or diaryl ester thereof and/or isophthalic acid and/or an acid halide, dialkyl ester or diaryl ester thereof, with the terephthalic acid unit/isophthalic acid unit mole ratio being about 9:1 to about 1:9, and (b) at least one bisphenol of the general formula (I) wherein -X- is selected from the group consisting of -O-, -S-, -SO₂-, -SO-, -CO-, an alkylene group containing 1 to 4 carbon atoms or an alkylidene group containing 1 to 4 carbon atoms, and R₁, R₂, R₃, R₄, R₁', R₂', R₃' and R₄', which may the same or different, are each selected from the group consisting of a hydrogen atom, a chlorine atom, a bromine atom or an alkyl group containing 1 to 4 carbon atoms, or a metal salt or diester of said bisphenol of the general formula (I), and adding from 0.01 to 2% by weight, based on the aromatic polyester, of a stabilizer selected from (1) an oxygen-containing organic stabilizer comprising polyphenylene oxide having the general formula (VII), and (2) a mixture of a polyphenylene oxide having the general formula (VII) given above and at least one member of the group consisting of (a) phenyl phosphates having the general formula (II): wherein R is hydrogen, alkyl or aryl, (b) phenyl phosphites having structural formulas III or IV, (c) diphosphites having the structural formulas V or VI, (d) a sulphur-containing organic stabilizer comprising 2-mercaptobenzimidazole, and (e) a fluorocarbon wax having the general formula (IX) The process of claim 14 wherein the dicarboxylic acid is selected from the group consisting of isophthalic acid, terephthalic acid and mixtures thereof. The process of claim 14 wherein the said monomeric reactant (a) consists of a mixture of isophthalic and terephthalic diphenyl esters. The process of claim 14, 15 or 16 wherein the process is carried out in a series of batch reaction zones, and the mixture of aromatic dicarboxylic acids consists of greater than 20 to less than 80 mole percent of isophthalic acid and greater than 20 to less than 80 mole percent of terephthalic acid. The process of any of claims 14 to 17 wherein said reactants are introduced to the polymerisation reaction in the liquid state and the polymerisation is carried out in the presence of a basic catalyst for said polymerization which is normally solid at 30°C and which is introduced in liquid form to the polymerization zone. The process of any of claims 14 to 17 wherein said reactants are introduced to the polymerization reaction in the liquid state and the polymerization is carried out in the presence of a basic catalyst for said polymerization, said catalyst and said liquid-state reactants being introduced substantially concurrently to the polymerization reaction. The process of any of claims 14 to 17 wherein said reactants are introduced to the polymerization reaction in liquid state and the polymerization is carried out in the presence of a basic catalyst for said polymerization which is normally solid at 30°C, said catalyst being introduced in liquid form to the polymerization reaction substantially concurrently with the introduction of the liquid-state reactants to the polymerization. The process of any of claims 14 to 20 wherein the reaction is conducted in a first stage to prepare a polyester oligomer and the reaction is continued in a second stage to produce the polyester product, said polymerization being carried out batchwise or substantially continuously in said second stage. The process of claim 21 wherein the polymerization in the first stage is carried out batchwise. The process of claim 21 wherein the polymerization in said first stage is substantially continuous. The process of any of claims 14 to 23 wherein said stabilizer is said polyphenylene oxide of general formula IV. The process of any of claims 14 to 23 wherein said stabilizer is a mixture of polyphenylene oxide and the phosphite of general formula V. The process of any of claims 14 to 25 wherein the stabilizer is present in an amount of at least 0.01% but less than 2% by weight, relative to the aromatic polyester. The process of any of claims 14 to 23 directed to the preparation of the composition of any of claims 2 to 13.

Inventors: ROSENFELD, JEROLD C.
Applicants: CELANESE CORPORATION
Application year: 1987
Main classification: C08K5
IPC codes: C08L67, C08K5