CATALYST COMPONENTS FOR ALPHA OLEPHINE-POLYMERIZING CATALYSTS AND PROCEDURE FOR MANUFACTURING SAME

Abstract: Catalyst components for alpha-olefin polymerization catalysts (which comprise an organoaluminium compound, an external electron donor and a solid magnesium-­ containing catalyst component obtained by the reaction of a solid magnesium-containing carrier component with a titanium halogen compound) are prepared by the steps of: (a) bringing magnesium sulphate, in the form of an aqueous solution or an alcoholic suspension, into contact with an aqueous or alcoholic solution of barium or calcium chloride and separating the undissolved part from the solution or suspension; (b) selectively evaporating the solution until dry and heating the obtained residue at 130-150°C, and dissolving this residue in alcohol if water has been used as solvent in step (a); (c) drying the alcoholic solution of the magnesium component by periodic azeotropic distillation; (d) precipitating the solid carrier component from the alcohol solution; and (e) reacting the solid carrier component with a titanium halogen compound in the presence of an internal electron donor or without an electron donor.

Description: Catalyst components for alpha olephine-polymerizing catalysts and procedure for manufacturing same The invention concerns catalyst components for alpha olephine-poly­ merizing catalysts which consist of an organoaluminium compound, an electron donor and a solid catalyst component which has been obtained when a compound containing magnesium has reacted with a titanium halogen compound. The invention also concerns a procedure for manufacturing these catalyst components and a procedure for polymerizing alpha olephines, in particular propylene, making use of said catalyst components. For polymerizing alpha olephines, prior art knows catalysts with high activity which have been manufactured of an aluminium alkyl compound, of an electron donor and of a halogenated titanium compound on a carrier substance comprising various magnesium compounds. For magnesium compound usually chlorinated magnesium compounds have been used, which may be for instance water-free magnesium chloride alone or together with other magnesium com­ pounds, or an organic magnesium compound which has been prepared by halogenating organic magnesium compounds with the aid of compounds containing chlorine. In polymerizing catalysts of this type, the properties of the solid carrier component have a significant influence on the properties of the ultimate catalyst, for instance on its activity. These proper­ ties can be substantially influenced through the mode of manufac­ turing the carrier component. The present invention concerns carrier components which have been prepared from magnesium sulphate, or from minerals contain­ ing magnesium sulphate which may be natural minerals or synthetic minerals. There is nothing novel in itself in the use of various magne­ sium salts for carrier for magnesium chlorides treated with titani­ um halogen in preparing catalyst components to the purpose of poly­ merizing olephines. However, it has turned out to be difficult to manufacture, exclusively from magnesium sulphate, active Ziegler-­ Natta catalysts, in particular those for propylene-polymerizing processes, because in these processes the catalysts are highly sensitive to moisture and to the crystal water contained in the carrier. Minimal quantities of crystal water already reduce the activity of the catalyst significantly. Magnesium sulphate, and minerals containing it, contain in general considerable quantities of crystal water, and therefore are not fit to be used in propy­ lene-polymerizing catalysts. The present invention relates to catalyst components for those alpha olephine-polymerizing catalysts which consist of an organo-­ aluminium compound, an external electron donor and a solid catalyst component which has been obtained when a solid carrier component containing magnesium has reacted with a titanium halogen compound and which are free of the drawbacks mentioned and, therefore, are fit to be used in polymerizing propylene. The catalyst component of the invention is characterized in that it has been composed by making a solid carrier component, which has been prepared (a) by bringing magnesium sulphate in the form of an aqueous solu­ tion, or of an alcohol suspension, into contact with an aqueous or alcohol solution of barium or calcium chloride, and by separating the undissolved part from the solution or suspension; (b) by selectively evaporating the solution until dry and heating the obtained residue at 130-150°C, and dissolving this residue in alcohol if in step (a) water has been used for solvent; (c) by drying the alcohol solution of the magnesium component with the aid of periodic azeotropic distillation; and (d) by precipitating the solid carrier component from the alcohol solution; react with a titanium halogen compound in the presence of an internal electron donor or without electron donor. The invention also concerns a procedure for manufacturing catalyst components for alpha olephine-polymerizing catalysts which consist of an organoaluminium compound, an external electron donor and a solid catalyst component containing magnesium which has been obtained when a solid carrier component containing magnesium has reacted with a titanium halogen compound. The procedure of the invention is characterized in that a solid carrier component which has been prepared (a) by bringing magnesium sulphate in the form of an aqueus solu­ tion or of an alcohol suspension into contact with an aqueous or alcohol solution of barium or calcium chloride and by separating the undissolved part from the solution or suspension; (b) by selectively evaporating the solution until dry and heating the obtained residue at 130-150°C, and by dissolving this residue in alcohol if in step (a) water has been used for solvent; (c) by drying the alcohol solution of the magnesium component with the aid of periodic azeotropic distillation; and (d) by precipitating the solid carrier component from the alcohol solution; is made to react with a titanium halogen compound in the presence of an internal electron donor or without electron donor. The catalyst component of the invention and the carrier component used therein afford several advantages over carrier components containing magnesium which have been prepared by conventional synthesis techniques. For starting material, magnesium sulphates with crystal water or in dry form can be used. The synthesis is simple, in particular when alcohols are used for solvent. Apart from pure magnesium sulphates, catalyst components of the invention can be prepared also from a multitude of magnesium minerals con­ taining sulphate, which may contain 1-15 mol crystal water. The first step in preparing the catalyst component of the invention is preparing the solution, or suspension, from the magnesium sulphate to be used for starting material. For solvent, water or an alcohol, such as methanol, ethanol or propanol, may be used. When using alcohol, a suspension of magnesium sulphate is obtained, while a solution is obtained when using water. The water used for dissolving has then to be removed at a later stage. The most suitable choice of alcohol is ethanol. The quantity of magnesium sulphate in the solution may vary within wide limits. The usable range is within 1 to 50% by weight of magnesium sulphate. As taught by the invention, bringing the magnesium sulphate solu­ tion, or suspension, into contact with barium or calcium chloride is preferably carried out so that an aqueous, or alcohol, solution is prepared from barium or calcium chloride, its concentration varying from 1% to saturated solution. the magnesium sulphate solution, or suspension, is thereafter mixed with barium or calcium chloride solution, whereby barium or calcium chloride is precipi­ tated. Barium or calcium chloride solution is advantageously used in stoichiometric proportion to magnesium, although this is not indispensable. The precipitated barium or calcium sulphate can easily be separated from the solution by centrifuging or sedimenting. In case alcohol has been used for solvent, the clear solution containing the magnesium component leads directly to the phase in which the crystal water is removed. If water is used for solvent, the clear solution containing the magnesium component is evaporated until dry and warmed up slightly at 110-130°C for removing the extra water and for reducing the crystal water quantity. The heating time may vary from 0.5 hr to 2 hours, whereafter the residue is dissolved in alcohol, preferably in ethanol, and conducted to the crystal water removal step. As taught by the invention, the crystal water is removed by distil­ ling, with the aid of periodic azeotropic distillation. During this distillation, an azeotropic mixture of alcohol and water escapes from the solution, whereby new crystal water is transferred to the alcohol solution. By adding new water-free alcohol and by repeated distillation, total removal of crystal water from the magnesium component is accomplished. The number of azeotropic distilling runs required depends on the amount of water present in the solution and on the intended use of the catalyst. If the catalyst is intended to be used in polymeriz­ ing ethylene, fewer runs are needed, for instance 1 to 5 runs. When manufacturing a carrier component for propylene polymerizing, nearly water-free carrier is required, and experience has shown that this is achieved if the number of distilling runs is 9 to 15, advantageously 10 to 12. Hereby, the water content of the carrier component can be brought down far enough for propylene-polymerizing catalysts. After drying out the crystal water, precipitation of the magnesium carrier component is effected by transferring the dried ethanol solution into a cold solvent, whereby the magnesium component will precipitate. Suitable solvents are common organic hydrocarbons used as solvents. Heptane is a highly appropriate solvent for the reason that its boiling point is high enough so that in the titanizing step which has to be carried out subsequently titanium has time to react, and on the other hand it is low enough to avoid melting of the carrier component in the titanizing step. When the ethanol solution containing magnesium component is added into cold heptane, the carrier component is precipitated in finely divided form. After washing and drying, the carrier component is titanized with the aid of titanium tetrachloride in a manner known in itself in the art, for producing the catalyst component. Titanizing may be accomplished for instance in that the solid carrier component is mixed with a titanium halogen compound once or several times. Before, during or after the titanizing process the catalyst component may furthermore be treated with the aid of an internal electron donor compound. The titanizing is preferably accomplished in two steps, between which may be added internal electron donor, which is usually an amine, ether or ester of its type. A suitable donor is, for instance, diisobutylphthalate, of which the quantity may be 0.05 to 0.3, most appropriately 0.2, mol/mol Mg. In the first step a low temperature is to be recommended, e.g. below 0°C, preferably below -20°C. The second titanizing step may be carried out at higher temperature, e.g. at 85 to 110°C, a reaction time of 1-1.5 hours being sufficient. The solid reaction product is then separated from the liquid phase and washed with hydrocarbon solvents to remove impurities and derivatives. The catalyst component may be dried in light vacuum or in nitrogen gas at room temperature, or at slightly elevated temperature, and it may be homogenized by grinding it in a ball mill. Thereafter, the catalyst component of the invention may be used to polymerize alpha olephines by allowing it to come into contact with an Al compound and an external compound releasing electrons. In the role of external compounds releasing electrons may be used, for instance, amines, ethers, esters (preferably alkyl and arylesters of aromatic carboxylic acids) or silane compounds (alkyl/aryl silanes), examples of such being, among others, the methyl and ethyl esters of benzoic, toluic and phthalic acid, isobutylesters of phthalic acid, triethoxysilanes, etc. Said electron donors are compounds which are able to enter complexes with Al alkyls. The stereo-specificity of the catalyst can be improved with their aid. The external compound releasing electrons, or donor, and the Al alkyl are mixed together, the molar proportion of the compound releasing electrons to the Al compound being about 20 and the Al/Ti molar proportion being between 10 and 300, depending on the poly­ merizing system. Polymerizing may be carried out either as slurry or bulk polymerizing, or in the gas phase. Catalyst components and catalysts prepared as taught by the inven­ tion may be used to polymerize alpha olephines, such as ethylene, propylene and butylene, by the slurry, bulk and gas phase methods, but the catalyst components of the invention are particularly well suited for used in polymerizing propylene because in them the quantity of crystal water in the carrier substance is singularly low and, as a result, the activity of the catalysts is particularly high especially regarding polymerizing of propylene. The invention is more closely illustrated in the following examples. The invention is more closely illustrated in the following examples. Example 1 50 g MgSO₄.7H₂O were suspended in 100 ml water. Thereafter, 44.5 g CaCl₂.2H₂O were added in 100 ml water. The suspension was centri­ fuged for 10 min. at 3000 rpm. The solution was evaporated until dry and heated for 1 hr at 140°C. The salt was poured, with mixing, into 200 ml ethanol. The ethanol solution was centrifuged for 10 min. (3000 rpm). The clear solution was transferred to a three-­ necked flask (1 liter) in which the drying of the ethanol carrier component was carried out by azeotropic distillation. The drying process consumed 500 ml absolute ethanol (moisture content < 100 ppm). The distillation took place in a slow nitrogen flow. The dry (moisture content < 400 µg H₂O/0.1 ml) hot ethanol/carrier solution was transferred into cold heptane (500 ml), in which the carrier component crystallized. The carrier component was henceforward kept in inert conditions (N₂). The extra ethanol was washed off in two heptane washings, whereafter the carrier component was transferred into cold titanium tetrachloride (500 ml, -20°C). After the mixture had warmed up to room temperature, 0.1 mol/mol Mg of diisobutyl­ phthalate were added thereto. The mixture was boiled for 1 hr at 110°C, whereafter the carrier component was allowed to settle and the TiCl₄ solution was exchanged for a new solution, and the treat­ ment was repeated for 1 hr at 110°C. The complete catalyst compo­ nent was washed with heptane and dried in nitrogen. The yield of catalyst was 8.0 g, and the catalyst contained: Mg 13.7%, Ti 2.9%, Cl 47.0%, and Ca 0.50%. The carrier component prepared in the way just described was applied in propylene polymerizing, adding into a 2-litre polymeriz­ ing reactor catalyst which had been prepared by mixing, as alumini­ um alkyl compound, triethylaluminium and, as Lewis compound, di­ phenylmethoxysilane (Al/donor mole proportion: 20) in 50 ml heptane and admixing to this, after 5 minutes, carrier component so as to make the Al/Ti molar proportion 200. Polymerizing was carried out in conditions as follows: propylene partial pressure 9.0 bar, hydrogen partial pressure 0.3 bar, temperature 70°C, and polymeriz­ ing time 3 hrs. The activity of the catalyst was 4.1 kg PP per g of catalyst in 3 hours. The bulk density of the polymer was 0.31 g/ml, isotacticity 89.4%, and 95% of the particle distribution were in the range 0.2 mm to 1.0 mm. Example 2 25 mg MgSO₄.7H₂O were suspended in 100 ml water. Thereafter, 24.8 g BaCl₂2H₂O were added in 100 ml water. The suspension was centri­ fuged for 10 min. at 3000 rpm. The solution was evaporated until dry and calcinated for 1 hr at 140°C. The salt was poured, with mixing, into 200 ml ethanol. The ethanol solution was centrifuged for 10 min. (3000 rpm). The clear solution was poured into a three-necked flask (1 litre), in which the drying of the ethanol/-­ carrier solution was carried out with the aid of azeotropic distil­ lation. The drying consumed 500 ml absolute ethanol (moisture ocntent less than 100 ppm). The distillation took place in slow nitrogen flow. Dry (moisture content < 400 µg H₂O/0.1 ml) hot ethanol/carrier solution was transferred into cold heptane (500 ml, -20°C), in which the carrier component crystallized. The carrier component was henceforward kept in inert conditions (N₂). The extra ethanol was washed off in two heptane washings, whereafter the carrier component was transferred into cold titanium tetrachloride (500 ml, -20°C). After the mixture had warmed up to room tempera­ ture, 0.1 mol/mol Mg of diisobutylphthalate were added thereto. The mixture was boiled for 1 hr at 110°C, whereafter the catalyst component was allowed to settle and the TiCl₄ solution was exchang­ ed for new solution, and the treatment was repeated for 1 hr at 110°C. The completed catalyst component was washed with heptane and dried with nitrogen. The yield was 8.0 g and the catalyst contain­ ed: Mg 15.9%, Ti 3.0%, Cl- 54.0%, and SO₄- 0.03%. As in Example 1, propylene was polymerized with the above catalyst component, and its activity was 6.9 kg PP per g of catalyst in 3 hours. The bulk density was 0.20 g/ml and isotacticity 94%, and 95% of the particle distribution were in the range 0.2 to 1.0 mm. Example 3 49 g MgSO₄.7H₂O and 22.2 g CaCl₂ were suspended in 500 ml ethanol. The solution was warmed, with mixing, for 4 hours at 60°C and allowed to settle for 16 hours, and the ethanol solution was separated by decanting. The solution was transferred to a three-­ necked flask in which drying of the ethanol/carrier component was carried out with azeotropic distillation. The drying consumed 1500 ml absolsute ethanol (moisture ocntent less than 100 ppm). When the dry (moisture content < 400 µg H₂O/0.1 ml) hot ethanol/carrier solution was transferred into cold heptane (500 ml, -20°C), the carrier component crystallized. The carrier component was hence­ forward processed in inert conditions (N₂). The extra ethanol was washed off with two heptane washings, and thereafter the carrier component was transferred into cold titanium tetrachloride (500 ml, -20°C). After the mixture had warmed up to room temperature, 0.1 mol/mol Mg of diisobutylphthalate were added thereto. The mixture was boiled for 1 hr at 110°C, whereafter the catalyst component was allowed to settle and the TiCl₄ solution was exchanged for new solution and the treatment repeated for 1 hr at 110°C. The complet­ ed catalyst component was washed with heptane and dried with nitrogen. The yield was 7.5 g and the catalyst component contained: Mg 14.00%, Ti 3.9%, Cl- 51.0%, Ca 300 ppm, and SO₄- 0.01%. The catalyst component was used to polymerize propylene as in Example 1, and its activity was found to be 7.9 PP per g of cata­ lyst. The bulk density was 0.29 g/ml, isotacticity 92.1%, and 90% of the particle distribution were in the range 0.2 to 1.0 mm.

Claims: 1. A process for the manufacture of a catalyst component for use in an alpha-olefin polymerization catalyst, which process comprises: (a) bringing magnesium sulphate, in the form of an aqueous solution or an alcoholic suspension, into contact with an aqueous or alcoholic solution of barium or calcium chloride and separating undissolved material from the solution or suspension; (b) selectively evaporating the solution until dry and heating the residue obtained at 130-150°C, and dissolving this residue in alcohol, if water is used as solvent in step (a); (c) drying the alcoholic solution of the magnesium component by periodic azeotropic distillation; (d) precipitating the solid carrier component from the alcoholic solution; and (e) reacting the solid carrier component with a titanium halogen compound in the presence of an internal electron donor or without an electron donor. 2. A process according to claim 1, characterized in that in drying the ethanol solution, 1-15 periodic azeotropic distillations are effected. 3. An olefin polymerization catalyst comprising a catalyst component obtained by the process of claim 1 or claim 2. 4. A process for the polymerization of an olefin, especially propylene, using a catalyst as claimed in claim 3.

Inventors: GAROFF, THOMAS
Applicants: NESTE OY
Application year: 1987
Main classification: C08F4
IPC codes: C08F4, C08F10