CARBONAMIDE MODIFIED THERMOPLASTIC ELASTOMER-POLYOXAZOLINE MOLDING COMPOSITIONS

Abstract: Moldable compositions of a polyoxazoline and a hydrogenated elastomeric block copolymer grafted with ethylenically unsaturated carbonamide are disclosed which have good physical properties and chemical resistance.

Description: This invention relates to novel thermoplastic molding compositions based on blends of an ethylenically unsaturated carbonamide modified thermoplastic elastomer and a polyoxazoline. Blends of partially hydrogenated elastomeric block copolymers with various thermoplastic polymers are taught in U.S. Pat. Nos. 4,101,605 and 4,119,607. It has been found that modifying a hydrogenated elastomeric block copolymer with an ethylenically unsaturated carbonamide and blending the resulting carbonamide modified. copolymer with polyoxazoline results in a composition having enhanced physical properties and improved chemical resistance as compared to either the base hydrogenated elastomer block copolymer or the carbonamide modified copolymer. According to this invention, there is provided a moldable composition comprising (a) at least one polyoxazoline selected from the group consisting of oxazoline homopolymer, poly(2-substituted oxazoline) homopolymers and partially hydrolyzed oxazoline homopolymers, and (b) at least one hydrogenated elastomeric block copolymer grafted with at least one ethylenically unsaturated carbonamide monomer having at least one hydrogen on the carbonamide nitrogen. Also according to this invention, there is provided a method of producing a molded composition comprising the steps of (1) forming a blend comprising (a) at least one polyoxazoline selected from the group consisting of oxazoline homopolymer, poly(2-substituted oxazoline) homopolyomers and partially hydrolyzed oxazoline homopolymers, and (b) at least one hydrogenated elastomeric block copolymer grafted with at least one ethylenically unsaturated carbonamide monomer having at least one hydrogen on the carbonamide nitrogen, and (2) molding the resulting composition. To produce the hydrogenated elastomeric block copolymer grafted with ethylenically unsaturated carbonamide (hereinafter sometimes referred to as "grafted thermoplastic elastomer") any suitable hydrogenated elastomeric block copolymer (hereinafter sometimes referred to as the "block copolymer") having at least one substantially completely hydrogenated diene polymer mid block (B) and at least two monoalkenyl arene polymer end blocks (A) can be employed. The grafted thermoplastic elastomer will contain from about 99.5 to about 89.5 weight percent of hydrogenated elastomeric block copolymer based on the total weight of the block copolymer and the carbonamide. The block copolymer can either be a linear block copolymer represented by the structure A(B-A) n , wherein n represents an integer of from 1 to 5; or a radial block copolymer represented by the structure B(A) x , wherein x represents an integer of from 3 to 7, such that the copolymer has from 3 to 7 arms. Suitable for use in the practice of this invention are the block copolymers taught in U.S. Pats. 3,595,942 and 4,377,647. One particularly suitable series of block copolymers is commercially available from Shell Chemical Company under the trademark Kraton®. Kraton G thermoplastic rubbers are hydrogenated styrene-butadiene-styrene triblock copolymers having number average molecular weights as determined by gel permeation chromatography (polystyrene standards) of from 85,000 to 300,000 and a molecular weight distribution (Mw/Mn) of from 1.05 to 1.7. The butadiene mid blocks of the Kraton G thermoplastic rubbers are at least 95% hydrogenated. Kraton G thermoplastic rubbers (TPR) particularly suitable for use include the hydrogenated styrene-butadiene-styrene triblock copolymers designated 1650, 1651, and 1652. Kraton G1650 TPR has a styrene/rubber ratio of 28/72. Kraton G1651 TPR has a styrene/rubber ratio of 33/67. Kraton G1652 TPR has a styrene/rubber ratio of 29/71. Any suitable ethylenically unsaturated carbonamide monomer having at least one hydrogen on the carbonamide nitrogen can be employed to produce the grafted thermoplastic elastomers usable in the practice of this invention. The grafted thermoplastic elastomer will contain from about 0.5 to about 10.5 weight percent carbonamide based on the total weight of the block copolymer and the carbonamide. Suitable ethylenically unsaturated carbonamide monomers include acrylamide, methacrylamide, Δ-4-tetrahydrophthalamide, and maleimide as well as any other carbonamide monomer having ethylenic unsaturation and at least one hydrogen chemically bonded to the carbonamide nitrogen. Maleimide is the preferred carbonamide monomer. The ethylenically unsaturated carbonamide can be chemically grafted onto the block copolymer elastomer using any suitable method of generating free radicals including introducing a free radical initiator into the composition or through thermomechanical free radical generation or irradiation. Suitable free radical initiators include peroxide initiators such as benzoyl peroxide, t-butyl perbenzoate, and di-t-butyl peroxide and azo initiators such as azobisisobutyronitrile. If used, the free radical initiator will be employed in an amount of from about 0.00001 to about 0.001 weight percent based on the total weight of the block copolymer and the carbonamide. Any suitable oxazoline polymer can be employed in the practice of this invention. Typically, the number average molecular weight of the polyoxazoline polymer should be between about 40,000 to about 700,000 as determined by gel permeation chromatography using polystyrene standards. Suitable oxazoline polymers include oxazoline homopolymer, poly(2-substituted oxazoline) homopolymer, or partially hydrolyzed oxazoline polymers. Particularly suitable for use in this invention are poly(2-ethyl oxazoline) homopolymers. The preparation of poly(2-ethyl oxazoline) homopolymers is taught in U.S. Pat. No. 3,640,909. One suitable poly(2-ethyl oxazoline) homopolymer is available from Dow Chemical U.S.A., an operating unit of the Dow Chemical Company, under the designation Poly(ethyloxazoline) developmental polymer XAS-10874. To produce a moldable composition of this invention, any suitable method of blending the polyoxazoline with the grafted thermoplastic elastomer can be used, e.g., a Brabender mixing apparatus. The moldable composition will preferably contain from about 1 to about 15 parts by weight of oxazoline polymer per each 100 parts by weight of grafted thermoplastic elastomer. The moldable compositions of this invention can also include other ingredients such as extenders, processing aids, pigments and mold release agents, for their conventionally employed purpose. Also, reinforcing fillers in amounts sufficient to impart reinforcement can be used, such as titanium dioxide, potassium titanate and titanate whiskers, glass flakes and chopped glass fibers. The following examples serve to demonstrate the invention. Example 1 : This example demonstrates the preparation of a hydrogenated elastomeric block copolymer grafted with ethylenically unsaturated carbonamide. A Brabender mixing apparatus was charged with about 54 grams of Kraton G1650 TPR and about 1.45 grams of maleimide monomer at 135°C. Tertiary-butylperbenzoate free radical initiator (0.01 g) was added over a five minute period with the mixing rotors turning at about 63 rpm. The grafted thermoplastic elastomer (i.e. Kraton G1650 TPR grafted with maleimide was removed and analyzed by differential scanning calorimetry, gel permeation chromatography and elemental nitrogen analysis. The analyses results are shown below. Example 2 : This example demonstrates the preparation of a hydrogenated elastomeric block copolymer grafted with ethylenically unsaturated carbonamide. A Brabender mixing apparatus was charged with about 54 grams of Kraton G1650 TPR and about 3.2 grams of maleimide monomer at 135°C. Tertiary-butylperbenzoate free radical initiator (0.01 g) was added over a five minute period with the mixing rotors turning at about 63 rpm. The grafted thermoplastic elastomer was removed and analyzed by differential scanning calorimetry, gel permeation chromatography and elemental nitrogen analysis. The analyses results are shown below. Example 3 : This example demonstrates the preparation of a moldable composition of this invention. About 10 parts by weight of poly(2-ethyloxazoline) [Poly(ethyloxazoline) developmental polymer XAS-10874, Dow Chemical U.S.A.] were incorporated by blending into about 100 parts by weight of the grafted thermoplastic elastomer produced according to the procedure of Example 1. The blend was prepared in a Brabender mixer set at 63 rpm by mixing for about 5 minutes at 200°C. The resulting blend was recovered as a moldable composition of the invention and samples were compression molded. The molded samples were analyzed and compared to molded control samples of Kraton G1650 TPR and Kraton G1650 TPR grafted with carbonamide. The analyses results are set forth in Table I below. Example 4 : This example demonstrates the preparation of a moldable composition of this invention. About 10 parts by weight of poly(2-ethyloxazoline) [Poly(ethyloxazoline) developmental polymer XAS-10874, Dow Chemical U.S.A.] were incorporated by blending into about 100 parts by weight of the grafted thermoplastic elastomer produced according to the procedure of Example 2. The blend was prepared in a Brabender mixer set at 63 rpm by mixing for about 5 minutes at 200°C. The resulting blend was recovered as a moldable composition of the invention and samples were compression molded. The molded samples were analyzed and compared to molded control samples of Kraton G1650 TPR and Kraton G1650 TPR grafted with carbonamide according to the procedure of Example 2. The analyses results are set forth in Table II below. The compositions of the invention may be formed by extrusion. Suitable conditions are extrusion temperature of 180 to 260°C, a residence time of 1 to 3 minutes and a pressure in the die of 6.9 to 13.8 MPa (1000 to 2000 psi). The compositions may be converted to shaped articles by moulding e.g. injection moulding. Suitable moulding conditions are a moulding temperature of 180 to 260°C, a moulding pressure of 13.8 to 27.6 MPa (2000 to 4000 psi) and a residence time in the mould of about 1 to 2 minutes. The compositions of the invention exhibit improved solvent resistance and toughness, as shown in energy to break and elongation properties, as compared with either of the components, i.e. the polyoxazoline and the hydrogenated elastomeric block copolymer grafted with ethylenically unsaturated carbonamide monomer, when taken alone. It will be evident from the foregoing that various modifications can be made to this invention. Such, however, are considered as being within the scope of the invention.

Claims: A moldable composition comprising (a) at least one polyoxazoline selected from the group consisting of oxazoline homopolymer, poly(2-substituted oxazoline) homopolymers and partially hydrolysed oxazoline homopolymers, and (b) at least one hydrogenated elastomeric block copolymer grafted with at least one ethylenically unsaturated carbonamide monomer having at least one hydrogen on the carbonamide nitrogen. A moldable composition as claimed in claim 1 characterised in that said hydrogenated elastomeric block copolymer which is grafted has at least one substantially completely hydrogenated diene polymer mid block and at least two mono-alkenyl arene polymer end blocks. A composition as claimed in claim 2 characterised in that said hydrogenated elastomeric block copolymer is selected from (a) linear block copolymers represented by the structure A(B-A) n , wherein A represents the end block, B represents the mid block, and n represents an integer of from 1 to 5, and (b) radial block copolymers represented by the structure B(A) x , wherein A represents the end block, B represents the mid block, and x represents an integer of from 3 to 7 such that the radial block copolymer has from 3 to 7 arms. A composition as claimed in claim 3 characterised in that said linear block copolymer is a hydrogenated styrene-butadiene-styrene triblock copolymer. A composition as claimed in any one of claims 1 to 4 characterised in that said ethylenically unsaturated carbonamide monomer is selected from acrylamide, methacrylamide, Δ-4-tetrahydrophthalamide, and maleimide. A composition as claimed in any one of claims 1 to 5 characterised in that said hydrogenated elastomeric block copolymer grafted with ethylenically unsaturated carbonamide monomer contains from about 0.5 to about 10.5 weight percent of the ethylenically unsaturated carbonamide monomer based on the total weight of the block copolymer and the carbonamide monomer. A composition as claimed in any one of claims 1 to 6 characterised in that said hydrogenated elastomeric block copolymer grafted with ethylenically unsaturated carbonamide contains from about 99.5 to about 89.5 weight percent of the block copolymer based on the total weight of the block copolymer and the carbonamide monomer. A method of producing a molded article comprising the steps of (1) forming a blend comprising a composition as claimed in any one of claims 1 to 7, and (2) molding the resulting composition. A method as claimed in claim 8 in which said blend is molded in contact with a reinforcing filler.

Inventors: DEAN, BARRY D.
Applicants: ARCO CHEMICAL TECHNOLOGY, L.P.
Application year: 1987
Main classification: C08L51
IPC codes: C08L79, C08L51, C08F287