LIQUID CRYSTAL POLYMER

Abstract: Liq. crystal polymer comprises a polymer (1) and a low mol. cpd. (2). The polymer (1) has a proton donor and/or a proton acceptor but exhibits no liq. crystal properties. The low mol. cpd. (2) has a proton acceptor and/or a proton donor and/or acceptor of the polymer. The polymer (1) can be polyvinylacetate, polyacrylic acid or polyvinyl alcohol. The low mol. cpd. is one kind of cpd. of formula A-X-Y-Z, where A is an end gp. having a proton donor and/or a proton acceptor; X is a ring gp. (e.g., benzene ring, biphenyl ring, cyclohexane ring); Y is a centre gp. (-O-, -COO-or -OC-) and Z is a chiral end gp.; A contains an OH gp. and/or a carboxylic acid gp. such as B-(CH2)p-D-(CH2)p-E-, where B is OH, -COOH, -C(CH3)(CH2OH)2 or -C(CH3)(CH2OCOCH3)2; D is a single bond or -COO-; E is -COO- or -O-; p is 1-10; q is 1-20; Z is -(CH2)m-RCH-(CH2)n-CH3, where R is a low C alkyl gp., hydrogen atom or nitride gp.; m is 0-5, n = 0 or 1.

Description: (Technical Field) This invention relates to a liquid crystal high molecular material and more particularly, to a liquid crystal high molecular material which can be readily obtained by mere mixing of a low molecular compound and a high molecular compound and in which said low molecular compound is uniformly distributed in the polymer matrix. (Background Technique) Hitherto, various liquid crystals of low molecular compounds have been known, but they have the defect that because of low molecular compounds, they are inferior in self shape retention (generally including the properties of liquid crystal compounds capable of being molded into desired forms). Therefore, there have been proposed compositions comprising a mere mixture of a high molecular compound with a liquid crystal of a low molecular compound or high molecular compounds in which a low molecular liquid crystal compound is bonded to a main chain or side chain through covalent linkage which are improved in self shape retention. However, since the terminal group of a low molecular liquid crystal compound is generally an alkyl group, mixing of a high molecular compound with a low molecular liquid crystal compound results microscopically in a sea-island structure and does not afford a uniform mixed state. That the liquid crystal compound is not uniformly mixed reveals various defects when the composition is utilized as a liquid crystal. For example, non-uniform distribution of a low molecular liquid crystal compound in the matrix of a high molecular compound causes a non-uniform response in the high molecular composition as liquid crystal and a deterioration in definition when applied to display elements. Moreover when a liquid crystal compound is bonded to a high molecular compound through covalent linkage, reaction conditions suitable thereto are necessary and it is not simple to bond a liquid crystal compound to a high molecular compound. JP-A-5 842 685, JP-A-6 137 892 and JP-A-6 160 734 disclose lyotropic liquid crystals, whereas the present invention is concerned with thermotropic liquid crystals. These are completely different systems which do not relate to each other. The preparation of a high molecular weight liquid crystal by the hydrogen bonding of a low molecular weight material with a high molecular weight polymer is not disclosed in said documents. Further, said documents do not disclose the chiral smectic state of the liquid crystals at all. JP-A-6 147 427 discloses a liquid crystal comprising 10-80% by weight of a thermoplastic amorphous polymer, such a polystyrene of polycarbonate, and 20-90% by weight of a low molecular weight liquid crystal, examplified by DOBAMBC. Neither polystyrene nor DOBAMBC have proton-donor functionality and polystyrene has no hydrogen transfer functionality at all. The liquid crystal is said to be finely dispersed in the polymer. As it is clear from table 1 of this document, the material disclosed therein is not hydrogen bonded when considering that there are two temperatures at which the optical response ceased. Example 1 of this document further shows that nearly immobility occurs at about 60° Centigrade and that complete immobility occurs at about 46° Centigrade. This demonstrates that the optical response of the liquid crystal of this document is uneven at best. The object of this invention is to provide a liquid crystal high molecular material which is not a mere mixture of a high molecular compound and a low molecular liquid crystal compound and further is not one where a high molecular compound and a low molecular liquid crystal compound are bonded through covalent linkage. Another object of this invention is to provide a liquid crystal high molecular material which can be simply produced by the simple operation of mixing. (Disclosure of the Invention). According to the present invention, the above objects are obtained by a liquid crystal high molecular material, characterized by containing a non-liquid crystalline polymer having functional groups selected from > C=O, -OH, -COOH, -CONH-, -NH₂ and -CO-O-CO- capable of bonding through hydrogen bond; and a low molecular compound represented by the formula A-X-Y-Z, wherein A is a terminal group having functional groups selected from >C=O, -OH, -COOH, -CONH-, -NH₂ and -CO-O-CO- capable of bonding through hydrogen bond to the functional groups in the non-liquid crystalline polymer, X is a cyclic group, Y is a divalent group and Z is a chiral terminal group. The basis of this invention is that a functional group capable of bonding through hydrogen bond is bonded to a low molecular liquid crystal compound and the resulting non-liquid crystal compound or liquid crystal compound is mixed with a non-liquid crystalline polymer having a functional group capable of bonding through hydrogen bond, whereby a liquid crystal high molecular material which is not a mere mixture is obtained. It is surprising that a liquid crystal high molecular material is obtained from a low molecular compound rendered non-liquid crystalline by introduction of functional group and a non-liquid crystalline polymer. Therefore, the non-liquid crystalline polymer in this invention is required to have a functional group capable of bonding through hydrogen bond to a functional group in the low molecular compound to be mixed. Generally, the hydrogen bond is a bonding small in bond energy of 2-8 kcal/mol which is shown diagrammatically, for example, by the following formula with reference to proton donator and proton acceptor: -OH··O=C<. In this case, for example, >C=O is a proton acceptor and -OH is a proton donator and -COOH is a functional group having both proton donator and proton acceptor. As non-liquid crystalline polymers having such functional groups capable of bonding through hydrogen bond, mention may be made of, for example, polyacrylic acid, polymethacrylic acid, polyacrylate, polymethacrylate, polyacrylamide, polyvinyl alcohol and its partial hydrolysate, polyester and polyvinyl acetate. Thus, the functional group capable of bonding through hydrogen bond may bond to the main chain or the side chain in the polymers. These non-liquid crystalline polymers may be used alone or in combination of two or more. Polyacrylic acid and polyvinyl alcohol are preferred among the above exemplified non-liquid crystalline polymers. Furthermore, in this invention, it is desired that the polymerization degree of said non-liquid crystalline polymers is 10-10,000, preferably 100-2,000. When it is less than 10, the liquid crystal high molecular material tends to lack self form retention and when more than 10,000, the liquid crystal high molecular material tends to show difficulty in workability. The low molecular compound has a terminal group A having functional groups selected from >C=O, -OH, -COOH, -CONH-, -NH₂, and -CO-O-CO-, a cyclic group X, a divalent group Y and a chiral terminal group Z, and is represented by the following formula: A-X-Y-Z (1) A suitable terminal group A can be shown by the following formula: B-(CH₂) p -D-(CH₂) q -E- (2) (wherein B represents either one of -OH, -COOH, -C(CH₃)(CH₂OH)₂ and -C(CH₃)(CH₂OCOCH₃)₂, D represents a single bond or -COO-, E represents -COO- or -O-, p represents an integer of 0-10 and q represents 1-20). The following can be shown as further suitable terminal groups A among those represented by said formula (2) HOOC-CH₂CH₂-COO-(CH₂)₁₂-O- HOOC-CH₂CH₂-COO-(CH₂)₁₁-C(=O)- H₃C-C(CH₂OH)₂-COO-(CH₂)₁₂-O- H₃C-C(CH₂OH)₂-COO-(CH₂)₁₁-C(=O)-O- HO-C(CH₂OH)₂-COO-(CH₂)₁₂-O- HO-C(CH₂OH)₂-COO-(CH₂)₁₁-C(=O)-O- HO-CH₂CH₂-COO-(CH₂)₁₂-O- HO-CH₂CH₂-COO-(CH₂)₁₁-C(=O)- HOOC(CH₂)₃COO(CH₂)₆-O- HO-(CH₂)₁₂-O- HOOC(CH₂)₈C(=O)-O- As the cyclic group X, the following can be enumerated as examples thereof. (in the above formulas, k represents an integer of about 1 or 2.) A phenylene group and a biphenylene group are especially preferred among these cyclic groups X. As said divalent group Y, mention may be made of, for example, -O-, -OCO-, -CO-S-, -CH=C(CN)-, -CH=CH- and -CO-CH₂-. -COO-, is preferred among these divalent groups Y. The chiral terminal group Z is represented by the following formula: (wherein R represents a lower alkyl group, a halogen atom or nitrile group, m represents an integer of 0-5 and n represents 0 or 1.) and as examples thereof, mention may be made of 1-methylpropyl group, 2-methylbutyl group, 1-methylbutyl group, 3-methylpentyl group, 2-methylpentyl group, 4-methylhexyl group, 2-chloropropyl group, 2-chlorobutyl group, 3-chlorobutyl group, 3-chloropentyl group, 4-chlorohexyl group, 4-chloropentyl group, 2-cyanopropyl group, 2-cyanobutyl group, 3-cyanobutyl group, 3-cyanopentyl group, 4-cyanopentyl group and 4-cyanohexyl group. Among these groups, 2-methylbutyl group is preferred. The liquid crystal high moleuclar material of this invention can be produced by mixing said specific non-liquid crystalline polymer and said low molecular compound. Theoretically, this liquid crystal high molecular material can be produced by mixing the non-liquid crystalline polymer with the low molecular compound having functional groups in the same mol number as of the functional group in said non-liquid crystalline polymer which are capable of bonding through hydrogen bond. In order to obtain a high molecular material capable of developing the liquid crystallinity, for example, when the non-liquid crystalline polymer is polyacrylic acid or polyvinyl alcohol and the terminal group A of the low molecular compound has one -COOH or two hydroxyl groups, the functional group in polyacrylic acid or polyvinyl alcohol is 1-5 mols, preferably 1.5-4.5 mols per one mol of functional group of the low molecular compound which is capable of bonding through hydrogen bond. Mixing of the non-liquid crystalline polymer and the low molecular compound can be carried out by optional methods, for example, by mixing a solution of the non-liquid crystalline polymer in a polar solvent with a solution of the low molecular compound in a polar solvent, concentrating and drying the mixture. As the polar solvents, mention may be made of lower alcohols such as methanol and ethanol, ketones such as acetone and methyl ethyl ketone, and halogenated hydrocarbons such as methylene chloride and chloroform. No special heating is required for the mixing. After the concentration, the concetrated liquid is cast in a suitable frame and dried to obtain a sheet and film of a desired thickness and shape or a bulk product of the desired shape. The shape of the liquid crystal high molecular material depends on the use of this liquid crystal high molecular material. A thus obtained liquid crystal high molecular material is not a mere mixture of a non-liquid crystalline polymer and a low molecular compound, but is a material where the low molecular compound bonds the functional group in the non-liquid crystalline polymer through hydrogen bond. Therefore, in this liquid crystal high molecular material, a non-liquid crystalline or liquid crystalline low molecular compound is uniformly dispersed in a high molecular matrix and even if a non-liquid crystalline low molecular compound is dispersed, the material can exhibit sufficiently the characteristics as liquid crystal and evenly responses to electrical or optical input. (The best mode for practice of the invention) (Examples 1 and 2) Using Dienstark apparatus, 93 mmols (20g) of 4'-hydroxybiphenyl-4-carboxylic acid and 467 mmols (41 g) of (S)-(-)-2-methyl butanol were refluxed in 150 ml of benzene for 25 hours in the presence of concentrated sulfuric acid (2 ml). The reaction mixture was concentrated and thereafter was recrystallized from toluene-hexane mixed solvent to obtain 26.0 g of 4'-hydroxybiphenyl-4-carboxylic acid 2-methylbutyl ester (ester 1a ) (yield; 98%, [α]²³D=+4.85 (chloroform)). 63 mmols (18 g) of said ester 1 a , 37.7 mmols (10 g) of 12-bromo-1-dodecanol and 151 mmols (20.8 g) of potassium carbonate were refluxed in 400 ml of acetone for 8 hours. The reaction mixture was filtered and the filtrate was concentrated, then purified by column chromatography and recrystallized from ethanol to obtain 17.7 g of 4'-(12-hydroxydodecyloxy)biphenyl-4-carboxylic acid 2-methylbutyl ester {ether 1b , [α]²³D=+2.91 (chloroform)} (yield 58%). 21.8 mmols (10.2 g) of said ether 1b and 23.9 mmols (2.4 g) of succinic anhydride were refluxed in a mixed solvent of 50 ml of pyridine and 300 ml of chloroform for 5 hours. The reaction mixture was washed with dilute hydrochloric acid, washed with water, dried and then recrystallized from ethanol to obtain 7.1 g (yield 57%) of the desired non-liquid crystalline low molecular compound 4'-{12-(3-carboxypropionyloxy)dodecyloxy}biphenyl-4-carboxylic acid 2-methylbutyl ester {non-liquid crystalline low molecular compound 1c , melting point 78.8-80.0°C, [α]²³D=+2.16 (chloroform)}. A solution of 2.4 g of said non-liquid crystalline low molecular compound 1c in 500 ml of acetone was mixed with a solution of 0.91 g of polyacrylic acid in 500 ml of ethanol (said polyacrylic acid had Mw of 250,000 and Tg of 106°C in Example 1 and Mw of 7,000 and Tg of 106°C in Example 2). The mixture was well stirred, concentrated and then dried to obtain 2 kinds of liquid crystal high molecular films. Phase transition behaviors with temperatures of these liquid crystal high molecular films and said non-liquid crystalline low molecular compound 1c are shown in Table 1. (Example 3) 63 mmols (18 g) of the ester 1 a obtained in Examples 1 and 2, 0.12 mol (39.4 g) of dibromododecane and 0.25 mol (34.6 g) of potassium carbonate were refluxed in 600 ml of acetone for 8 hours. The reaction mixture was filtered and the filtrate was concentrated, purified by column chromatography and recrystallized from ethanol to obtain 21.8 g (yield 65%) of 4'-(12-bromododecyloxy)biphenyl-4-carboxylic acid 2-methylbutyl ester {monobromo compound 1d , [α]²³D=+2.85 (chloroform)}. 60.0 mmols of 2,2-dihydroxymethylpropionic acid and 66.0 mmols of tetramethylammonium hydroxide (pentahydrate) were stirred in 300 ml of DMF for 2 hours. Then, thereto was added 85.0 mmols of said monobromo compound 1d and the mixture was stirred for 6 hours. The reaction mixture to which 1 l of water was added was extracted with ether, dried, concentrated and purified by column chromatography to obtain the desired 4'-(12-(2,2-dihydroxymethylpropionyloxy)dodecyloxy)biphenyl-4-carboxylic acid 2-methybutyl ester (liquid crystalline low molecular compound 3a ) {yield 50%, [α]²³D=+2.11 (chloroform)]. A solution of 2.4 g of said liquid crystalline low molecular compound 3a in 500 ml of acetone was mixed with a solution of 0.89 g of polyacrylic acid (Mw: 7,000, glass transition temperature: 106°C) in 500 ml of ethanol and the mixture was well stirred, concentrated and dried to obtain a liquid crystal high molecular film. Phase transition behaviors with temperatures of this liquid crystal film and said liquid crystalline low molecular compound 3a are shown in Table 1. (Example 4) A solution of 2.4 g of the same non-liquid crystalline low molecular compound 1c as used in Examples 1 and 2 in 500 ml of acetone was mixed with a solution of 0.56 g of polyvinyl alcohol (Mw: 70,000 and glass transition temperature: 85°C) in 500 ml of ethanol. The mixture was well stirred, concentrated and then dried to obtain a liquid crystal high molecular film. Phase transition behaviors with temperature of said liquid crystal high molecular film and the non-liquid crystalline low molecular compound 1c are shown in Table 1. (Example 5) Ester 1a (4'-hydroxybiphenyl-4-carboxylic acid 2-methylbutyl ester) was obtained in the same manner as in Example 1. 70 mmols (19.9 g) of said ester 1a , 100 mmols (24.4 g) of 1,6-dibromohexane and 150 mmols (20.7 g) of potassium carbonate were refluxed in 400 ml of acetone for 8 hours. The reaction mixture was filtered and then purified by column chromatography to obtain 4'-(6-bromohexyloxy)biphenyl-4-carboxylic acid 2-methylbutyl ester (ether 5b ; 18.9 g, yield 60%, [α]²³D=+2.93 (chloroform)). Then, a solution of 40 mmols (5.3 g) of glutaric acid and 80 mmols (14.4 g) of tetramethylammonium hydroxide (pentahydrate) in 100 ml of DMF was stirred for 2 hours. Thereto was added dropwise a solution of 20 mmols (8.9 g) of the ether obtained above in DMF, followed by stirring for 8 hours. The reaction mixture was extracted with ether, concentrated and then purified by column chromatography to obtain 4'-[6-(3-carboxybutanoyl) hexyloxy]biphenyl-4-carboxylic acid 2-methylbutyl ester (liquid crystalline low molecular compound 5c ; 62 g, yield 62%, [α]²³D=+2.35 (chloroform)). A solution of 1.00 g of said luqiud crystalline low moleuclar compound 5c in methylene chloride and a solution of 0.52 g of polyvinyl acetate (Mw=250,000, Tg=28°C) were well stirred, concentrated and then dried to obtain a liquid crystal high molecular film. Phase transition behaviors with temperature of this liquid crystal film and said liquid crystalline low molecular compound 5c are shown in Table 2. (Example 6) Ether 1b (4'-(12-hydroxydodecyloxy)biphenyl-4-carboxylic acid 2-methylbutyl ester) was obtained in the same manner as in Example 1. A solution of 1.00 g of this ether 1b and 0.55 g of the same polyvinyl acetate as used in Example 5 in methylene chloride was well stirred, concentrated and then dried to obtain a liquid crystal high molecular film. Phase transition behaviors with temperature of this liquid crystalline high molecular film and said ether 1b are shown in Table 2. (Example 7) A liquid crystalline low molecular compound 3a (4'-[12-(2,2-dihydroxymethylpropionyloxy)dodecyloxy]biphenyl-4-carboxylic acid 2-methylbutyl ester) was obtained in the same manner as in Example 3. A solution of 1.00 g of this liquid crystalline low molecular compound 3c and 0.59 g of the same polyvinyl acetate as used in Example 5 in methylene chloride was well mixed, concentrated and then dried to obtain a liquid crystalline high molecular film. Phase transition behaviors with temperature of this liquid crystalline high molecular film and said liquid crystalline low molecular compound 3a are shown in Table 2. (Example 8) (8-1) Synthesis of 4'-hydroxybiphenyl-4-carboxylic acid 2-methylbutyl ester. The objective ester 1a was obtained in the same manner as in Example 1. (8-2) Synthesis of 4-benzyloxycarbonyloxybenzoic acid 65 mmols (11.1 g) of benzyloxycarbonyl chloride was added dropwise to a solution of 55 mmols (7.4 g) of 4-hydroxybenzoic acid and 65 mmols (2.6 g) of sodium hydroxide in 200 ml of water at ice point. The reaction mixture was stirred for 24 hours and the precipitate was filtered, washed, dried and then purified by column chromatography to obtain the objective carbonic acid ester carboxylic acid 8b . (14.8 g, yield 99%) (8-3) Synthesis of 4-benzyloxycarbonyloxybenzoic acid chloride A solution of 27 mmols (7.3 g) of the carbonic acid ester carboxylic acid 8b obtained in the above (8-2) and 27 mmols (56 g) of phosphorus pentachloride in 50 mmols of ether was stirred at room temperature for 24 hours. After the reaction, removal of ether was effected and the resulting crystal was recrystallised from hexane to obtain the objective acid chloride 8c . (6.4 g, yield 82%) (8-4) Synthesis of 4'-(4''-benzyloxycarbonyloxybenzoyloxy)biphenyl-4-carboxylic acid 2-methylbutyl ester A solution of 16 mmols (4.5 g) of the ester 1a obtained in the above (8-1) and 16 mmols (1.6 g) of triethylamine in 20 ml of THF was stirred at ice point, followed by adding dropwise a solution of 15 mmols (4.4 g) of the acid chloride 8c obtained in the above (8-3) in THF. The solution was stirred for 8 hours with gradually returning the temperature to room temperature. The reaction mixture was extracted with ether, dried, concentrated and then purified by column chromatography to obtain the objective ester 8d. (6.5 g, yield 81%, [α]²³D=+2.25 (chloroform)). (8-5) Synthesis of 4'-(4''-hydroxybenzoyloxy)biphenyl-4-carboxylic acid 2-methylbutyl ester A solution of 10 mmols (5.4 g) of the ester 8d obtained in the above (8-4) and 0.4 g of palladium carbon (5% catalyst) in 40 ml of ethyl acetate was reacted for 4 hours in a hydrogen gas atmosphere. The reaction mixture was filtered, concentrated and then purified by column chromatography to obtain the objective hydroxy ester 8e . (3.9 g, yield 96%, [α]²³D=+2.11 (chloroform)). (8-6) Synthesis of 4'-[4''-(12-bromododecanoyloxy)benzoyloxy]biphenyl-4-carboxylic acid 2-methylbutyl ester A solution of 8 mmols(2.2 g) of 12-bromododecanoic acid and 10 ml of toluene in 5 ml of thionyl chloride was stirred at 80°C for 1 hour. Excess thionyl chloride and toluene were distilled out under reduced pressure to obtain acid chloride 8f . A solution of 8 mmols (3.2 g) of the hydroxy ester 8e obtained in the above (8-5) and 10 mmols (1.0 g) of triethylamine in 100ml of THF was stirred . Thereto was added dropwise a solution of said acid chloride 8f in THF, followed by stirring for 8 hours. The reaction mixture was extracted with ether, washed with an aqueous dilute hydrochloric acid solution, dried, concentrated and then purified by column chromatography to obtain the objective bromo ester 8h . (4.6 g, yield 87%, [α]²³D=+2.15 (chloroform)). (8-7) Synthesis of 4'-[4''-{12-(2,2-dihydroxymethylpropionyloxy) dodecanoyloxy}benzoyloxy]biphenyl-4-carboxylic acid 2-methylbutyl ester 10 mmols (1.3 g) of 2,2-dihydroxymethylpropionic acid and 10 mmols (1.8 g) of tetramethylammonium hydroxide (pentahydrate) were stirred in 100 ml of DMF for 2 hours. Then, thereto was added 6 mmols (4.0 g) of the bromo ester 8h obtained in the above (8-6) followed by stirring for 8 hours. The reaction mixture was extracted with ether, dried, concentrated and then purified by column chromatography to obtain the objective ester ( liquid crystalline low molecular compound 8i ) (3.1 g, yield 71%, [α]²³D=+2.29 (chloroform)). (8-8) Production of a liquid crystalline high molecular film 1.00 g of said liquid crystalline low molecular compound 8i and a solution of 0.48 g of the same polyvinyl acetate as used in Example 5 in methylene chloride were well stirred, concentrated and dried to obtain a liquid crystalline high molecular film. Phase transition behaviors with temperature of this liquid crystalline high molecular film and said liquid crystalline low molecular compound 8i are shown in Table 2. (Example 9) (9-1) Synthesis of 4-hydroxybenzoic acid 2-methylbutyl ester 90 mmols (12.2 g) of 4-hydroxybenzoic acid and 360 mmols (31.7 g) of 2-methyl butanol were subjected to dehydration reaction in 150 ml of toluene in the presence of 2 ml of concentrated sulfuric acid in a moisture determination tube for 25 hours. The reaction mixture was concentrated and then purified by column chromatography to obtain the objective hydroxy ester 9a (18.7 g, yield 98%, [α]²³D=+4.85 (chloroform)). (9-2) Synthesis of 4-benzyloxycarbonyloxybenzoic acid The desired carbonic acid ester carboxylic acid 8b was obtained in the same manner as in (8-2) of Example 8. (9-3) Synthesis of 4-benzyloxycarbonyloxybenzoic acid chloride The desired acid chloride 8c was obtained in the same manner as in (8-3) of Example 8. (9-4) Synthesis of 4- 4'-(benzyloxycarbonyloxy)benzoyloxy benzoic acid 2-methylbutyl ester A solution of 60 mmols (12.5 g) of hydroxy ester 9a obtained in the above (9-1) and 70 mmols (7.1 g) of triethylamine in 40 ml of THF was stirred and thereto was added dropwise 60 mmols (17.4 g) of the acid chloride 8c obtained in the above (9-3), followed by stirring for 8 hours. The reaction mixture was extracted with ether, dried, concentrated and then purified by column chromatography to obtain the desired carbonic acid ester 9b (20.3 g, yield 73% [α]²³D=+2.64 (chloroform)). (9-5) Synthesis of 4-(4'-hydroxybenzoyloxy)benzoic acid 2-methylbutyl ester A dispersion solution of 30 mmols (13.9 g) of the carbonic acid ester 9b obtained in the above (9-4) and 0.8 g of palladium carbon catalyst (5% pd) in 200 ml of ethyl acetate was reacted for 4 hours in hydrogen gas atmosphere. The reaction mixture was filtered and concentrated and then purified by column chromatography to obtain the desired hydroxy ester 9c (9.6 g, yield 97%, [α]²³D=+2.45 (chloroform)). (9-6) Synthesis of 4-[4'-(12-bromododecanoyloxy)benzoyloxy]benzoic acid 2-methylbutyl ester A solution of 30 mmols (8.4 g) of 12-bromododecanoic acid and 10 ml of toluene in 5 ml of thionyl chloride was stirred at 80°C for 1 hour. Excess thionyl chloride and toluene were distilled out under reduced pressure to obtain 12-bromododecanoyl chloride (acid chloride 9d ). A solution of 25 mmols (8.2 g) of hydroxy ester 9c obtained in the above (9-5) and 30 mmols (3.0 g) of triethylamine in 100 ml of THF was stirred. Thereto was added dropwise a solution of said acid chloride 9c in THF, followed by stirring for 8 hours. The reaction mixture was extracted with ether, washed with dilute aqueous hydrochloric acid solution, dried, concentrated and then purified by column chromatography to obtain the desired bromo ester 9e (12.1 g, yield 82% [α]²³D=+2.36 (chloroform)). (9-7) Synthesis of 4-[4'-{12-(2,2-dihydroxymethylpropionyloxy)dodecanoyloxy}benzoyloxy]benzoic acid 2-methylbutylester 25 mmols (3.4 g) of 2,2-dihydroxymethylpropionic acid and 25 mmols (4.5 g) of tetramethylammonium hydroxide (pentahydrate) were stirred in 100 ml of DMF for 2 hours. Then, thereto was added 20 mmols (11.8 g) of the bromo ester 9e obtained in the above (9-6) and stirring was effected for 8 hours. After the reaction, the reaction mixture was extracted with ether, dried, concentrated and purified by column chromatography to obtain the objective ester (liquid crystalline low molecular compound 9f). (10.9 g, yield 85%, [α]²³D=+2.30 (chloroform)). (9-8) Production of liquid crystal high molecular film A solution of 1.00 g of said liquid crystalline low molecular compound 9f and 0.54 g of the same polyvinyl acetate as used in Example 5 was fully stirred, concentrated and dried to obtain a liquid crystal high molecular film. Phase transition behaviors with temperature of this liquid crystal high molecular film and said liquid crystalline low molecular compound 9f are shown in Table 2. (Example 10) Hydroxy ester 8e (4'-(4''-hydroxybenzoyloxy)biphenyl-4-carboxylic acid 2-methylbutylester) was prepared in the same manner as in (8-1)-(8-5) of Example 8. Synthesis of 4'-[4''-(9-carboxynonanoyloxy)benzoyloxy]biphenyl-4-carboxylic acid 2-methylbutyl ester 30 mmols (7.2 g) of sebacoyl chloride was put in a solution of 10 mmols (4.0 g) of hydroxy ester 8e obtained above and 30 mmols (3.0 g) of triethylamine in THF, followed by stirring for 6 hours. The reaction mixture was extracted with ether, washed with dilute aqueous hydrochloric acid solution, dried, concentrated and then purified by column chromatography to obtain the objective ester (liquid crystalline low molecular compound 10a ). (1.9 g, yield 32%, [α]²³D=+2.28 (chloroform)). Production of liquid crystal high molecular film A solution of 1.00g of said liquid crystalline low molecular compound 10a and 0.44 g of the same polyvinyl acetate as used in Example 5 in methylene chloride was well stirred, concentrated and dried to obtain a liquid crystal high molecular film. Phase transition behaviors with temperature of this liquid crystal high molecular film and said liquid crystalline low molecular compound 10a are shown in Table 2. (Example 11) (11-1) Synthesis of 4-hydroxybenzoic acid 2-methylbutyl ester The objective hydroxy ester 9a was obtained in the same manner as in (9-1) of Example 9. (11-2) Synthesis of 4'-(benzyloxycarbonyloxy)biphenyl-4-carboxylic acid 70 mmols (11.9 g) of benzyloxycarbonyl chloride was added dropwise to an aqueous solution of 60 mmols (12.9 g) of 4'-hydroxybiphenyl-4-carboxylic acid and 70 mmols (2.8 g) of sodium hydroxide in 2 l of water at ice point with stirring. The mixture was stirred for 24 hours and then the precipitate was filtered, washed with water, dried and then purified by column chromatography to obtain the objective carbonic acid ester carboxylic acid 11a (19.4 g, yield 98%). (11-3) Synthesis of 4'-(benzyloxycarbonyloxy)biphenyl-4-carboxylic acid chloride A solution of 50 mmols (17.4 g) of the carbonic acid ester carboxylic acid 11a and 50 mmols (10.4 g) of phosphorus pentachloride in 300 ml of ether was stirred at room temperature for 24 hours. After the reaction, the reaction mixture was subjected to removal of ether by distillation under reduced pressure to obtain the objective acid chloride 11b (18.1 g, yield 99%). (11-4) Synthesis of 4-(4''-(benzyloxycarbonyloxy)biphenyl-4'-carbonyloxy)benzoic acid 2-methylbutyl ester A solution of 40 mmols (14.7g) of the acid chloride obtained in said (11-3) in THF was added dropwise to a solution of 40 mmols (8.3 g) of hydroxy ester 9a obtained in said (11-1) and 50 mmols (5.1 g) of triethylamine in 150 ml of THF with stirring, followed by stirring for 8 hours. After the reaction, the reaction mixture was extracted with ether, dried, concentrated and purified by column chromatography to obtain the objective ester 11c (17.2 g, yield 82%, [α]²³D=+2.54 (chloroform)). (11-5) Synthesis of 4-(4''-hydroxybiphenyl-4'-carbonyloxy) benzoic acid 2-methylbutyl ester A dispersed solution of 30 mmols (16.2 g) of the ester 11c obtained in said (11-4) and 0.8 g of palladium carbon catalyst (5% Pd) in 60 ml of ethyl acetate was subjected to reaction in a hydrogen atmosphere for 4 hours. After the reaction, the reaction mixture was filtered, concentrated and then purified by column chromatography to obtain the objective hydroxy ester 11a (11.4 g, yield 94%, [α]²³D=+2.35 (chloroform)). (11-6) Synthesis of 4-[4''-(12-bromododecanoyloxy)biphenyl-4'-carbonyloxy]benzoic acid-2-methylbutyl ester A solution of 30 mmols (8.4 g) of 12-bromododecanoic acid and 10 ml of toluene in 5 ml of thionyl chloride was stirred at 80°C for 1 hour. Excess thionyl chloride and toluene were distilled out under reduced pressure to obtain 12-bromododecanoyl chloride (acid chloride 11e ). 25 mmols (10.1 g) of hydroxy ester 11a obtained in said (11-5) and 30 mmols (3.0 g) of triethylamine were stirred in 100 ml of THF for 2 hours. Thereto was added dropwise a solution of said acid chloride 11e in THF, followed by stirring for 8 hours. The reaction mixture was extracted with ether, washed with dilute aqueous hydrochloric acid solution, dried, concentrated and then purified by column chromatography to obtain the objective bromo ester 11f (13.3 g, yield 80%, [α]²³D=+2.29 (chloroform)). (11-7) Synthesis of 4-{4''-(12-dihydroxymethylpropionyloxy) dodecanoyloxybiphenyl-4'-carbonyloxy]benzoic acid 2-methylbutyl ester 20 mmols (2.7 g) of 2,2-dihydroxymethylpropionic acid and 20 mmols (3.6 g) of tetramethylammonium hydroxide (pentahydrate) were stirred in 60 ml of DMF for 2 hours. Then, thereto was added 15 mmols (10.0 g) of bromo ester 11f obtained in said (11-6), followed by stirring for 8 hours. After the reaction, the reaction mixture was extracted with ether, dried, concentrated and then purified by column chromatography to obtain the objective ester (liquid crystalline low molecular compound 11f ) (9.1 g, yield 84%, [α]²³D=+2.11 (chloroform)). (11-8) Production of liquid crystal high molecular film A solution of 1.00 g of said liquid crystalline low molecular compound 11f and 0.48 g of the same polyvinyl acetate as used in Example 5 in methylene chloride was well stirred, concentrated and dried to obtain a liquid crystal high molecular film. Phase transition behaviors with temperature of this liquid crystal high molecular film and said liquid crystalline low molecular compound 11h are shown in Table 2. (Industrial Applicability) This invention can provide a liquid crystal high molecular material which comprises a non-liquid crystalline polymer in which a low molecular compound is uniformly distributed. In the liquid crystal high molecular material of this invention, the non-liquid crystalline polymer and the low molecular compound bond to each other through hydrogen bond and so can form a smectic phase on the lower temperature side than conventional high molecular liquid crystal compositions in which a non-liquid crystalline polymer and a liquid crystal compound do not bond to each other through hydrogen bond, but are merely mixed. This makes it possible to use the material of the invention in the field of optical electronics which utilize the characteristics of liquid crystals on the lower temperature side. That is, this liquid crystal high molecular material can suitably be applied to optical electronics, namely, electron optical devices such as room temperature switching elements, display elements for desk calculators and watches, electron optical shutter, electron optical diaphragms, optical modulation, optical communication optical path changeover switches, memories, or liquid crystal printer heads. The liquid crystal high molecular material of this invention can be obtained by a simple mixing operation and is superior in self shape retention.

Claims: A liquid crystal high molecular material, characterized by containing a non-liquid crystalline polymer having functional groups selected from > C=O, -OH, -COOH, -CONH-, -NH₂ and -CO-O-CO- capable of bonding through hydrogen bond; and a low molecular compound represented by the formula A-X-Y-Z, wherein A is a terminal group having functional groups selected from >C=O, -OH, - COOH, -CONH-, -NH₂ and -CO-O-CO- capable of bonding through hydrogen bond to the functional groups in the non-liquid crystalline polymer, X is a cyclic group, Y is a divalent group and Z is a chiral terminal group. The liquid crystal high molecular material according to claim 1, wherein said non-liquid crystalline polymer is polyacrylic acid, polyvinyl acetate or polyvinyl alcohol. The liquid crystal high molecular material according to claim 1, wherein said terminal group A comprises a hydroxyl group and /or a carboxylic acid group, said chiral group Z is represented by the formula (wherein R represents a lower alkyl group, a halogen atom or a nitrile group, m represents an integer of 0 - 5 and n represents 0 or 1), said cyclic group X comprises a benzene ring, biphenyl ring or cyclohexane ring and the divalent group Y is -O-, -COO- or -OCO-. The liquid crystal high molecular material according to claim 3, wherein said terminal group A is represented by the following formula B-(CH₂) p -D-(CH₂) q -E- (wherein B represents -OH, -COOH, -C(CH₃)(CH₂OH)₂ or - C(CH₃)(CH₂OCOCH₃)₂, D represents a single bond or -COO-, E represents -COO- or -O-, p represents an integer of 0-10 and q represents 1-20).

Inventors: HACHIYA SATOSHI, MORITA KAZUHARU, HACHIYA, SATOSHI, MORITA, KAZUHARU
Applicants: IDEMITSU KOSAN CO, IDEMITSU KOSAN LIMITED
Application year: 1987
Main classification: C08L101
IPC codes: C09K19