METHOD OF MOLDING PLASTIC AND INJECTION COMPRESSION MOLDING APPARATUS USING THE METHOD

Abstract: A method of molding a plastic is initiated by inject­ ing molten resin into a mold at a high pressure. The energy of the high pressure is partially stored in the form of elongation of tie bars of a molding machine. After the gate seals completely, the restoring force of the tie bars due to elastic deformation acts on the molded article as the molded article cools down. Each tie bar comprises a first member having a small modulus of elastic­ ity and a second member. When the elongation of each tie bar is small, only the first member of small modulus of elasticity works. After the elongation reaches a certain amount of Δℓ₁, the two members are connected parallel. As a result, the apparent modulus of elasticity of each tie bar increases rapidly. This makes it possible to mold a plastic with high dimensional accuracy.

Description: The present invention relates to a method of quite accurately molding plastics and to an injection compression molding machine for molding plastics with high dimensional accuracy. It is known to manufacture articles by molding a plastic resin using two halves of a mold which are pushed together to form a cavity by hydraulic means. Examples of this are found in EP-A-0102813, US 4025264 and US 3975133. In recent years, plastics have been molded by injection molding with high dimensional accuracy. For example, it has been required that lenses, optical disk substrates, etc. be molded to tolerances of submicron order. For molding an article accurately, it has been common practice to adopt the following process. First, a mold is clamped by applying a high pressure. Then, a molten resin is injected into the cavity of the mold through a nozzle. Immediately after the cavity is filled with a resin, a holding force large enough to prevent the mold from opening is imparted to the mold so that the shape of the molded product becomes as close a possible to the shape of the mold. The holding force is set less than the clamping force. As the specific volume of the molten resin in the mold is made closer to specific volume of resin at room temperature by adjusting the pressure and the temperature, sink marks, or shrink marks, which are produced on the molded product during cooling are reduced. In practice, however, a very large force is needed to satisfy such requirement. Under high pressure conditions, the mold and the construction elements of the molding machine including tie bars must be sufficiently rigid to prevent them from deforming. For this purpose, the mold and the molding machine are rendered bulky. This frequently results in a very large molding system. It is an object of the present invention to provide a method of molding plastics with high dimensional accuracy. It is another object of the invention to provide an injection compression molding apparatus which is simple in structure and capable of molding plastics highly reliably, stably, and accurately. The inventive concept differs entirely from the prior art techniques in that the molding apparatus has portions which are quite low in rigidity. Specifically, the present invention provides an injection molding apparatus for molding a plastic, comprising: a pair of stationary platens connected together by tie bars; a movable platen capable of moving along the tie bars; a pair of stationary and movable molds for forming therebetween a cavity in which molding is performed, the stationary mold being fixed to one of the stationary platens and the movable mold being fixed to the movable platen; an injection nozzle for injecting a molten resin into the cavity; and clamping means for clamping the movable mold, characterized in that each of said tie bars has a small modulus of elasticity when elongated up to a specific length and a large modulus of elasticity when elongated beyond the specific length. In a preferred embodiment the clamping means is activated to to clamp the two molds together so that the tie bars elongate by a specific length prior to the injection of the resin, with the lower modulus of elasticity. Further elongation of the tie bars during injection takes place with the higher modulus of elasticity, and the tie bars are so structured as to yield to a high pressure of the injected plastic material immediately before completion of injection and elongate by a second specific length that can be estimated by a relation between the volumetric coefficient of contraction of the plastic material and the volume of the cavity. Preferably the tie bars of the invention comprise a first member having a small modulus of elasticity, opposite ends of the first member being fixed to the pair of stationary platens, respectively; a second member having a large modulus of elasticity , one end of the second member being fixed to one of the pair of stationary platens; and means for connecting the first and second members when the first member is elongated by the specific length thereby to increase the modulus of elasticity of each tie bar. In this dual structure, when the amount of elongation is small, only the first member having the small modulus of elasticity works. When the amount of elongation reaches a specific amount ▵ℓ 1 , the two members are connected parallel. Thus, the modulus of elasticity increases quickly. The energy of the high pressure applied to the mold cavity by the injection unit during injection is stored in the form of an elongation ▵L of the tie bars each being in the state that the two members are connected parallel. As the molten resin in the mold cools and solidifies, it contracts. At this time, the tie bars having been stretched by ▵L exert a compressing force on the resin in the mold. The mold is thus preferably allowed to open the cavity slightly by the pressure of the injected material. In practice, the plastic material is molded in such a way that, as the molded material cools down, the restoring force of the elongated tie bars due to elastic deformation acts in the direction of reducing the cavity, taking into consideration the length, thickness and modulus elasticity of the material of the tie bars. The energy of the high pressure generated during the injection is stored in the form of elongation of the tie bars. In other words, after the gate of the mold has completely sealed, the molded material cools and, at the same time, the tie bars which were stretched in the direction of the thickness of the molded product are allowed to exert a restoring force due to elastic deformation. The volumetric coefficient of contraction of a plastic material can be calculated in advance from an equation of states of pressure, temperature and specific volume, generally known as P-V-T curve. The present invention further provides a method of molding a plastic using an injection molding apparatus, comprising the steps of: injecting a molten plastic material through a gate into a cavity between a pair of molds at a high pressure; sealing the gate; and cooling the injected molten plastic material while applying a compressing force to the plastic material in the cavity, characterized in that energy of the high pressure in the injecting step is stored in the form of an elastic elongation of tie bars of the injection molding apparatus beyond a specific amount of elongation each of the tie bars having a much larger modulus of elasticity when elongated beyond the specific length than when elongated up to the specific length, and in that the compressing force in the cooling step is caused by a restoring force of the elongated tie bars. This method is characterized in that the physical deformation of the tie bars is utilized as the source of a compressing force and, therefore, as the molten resin in the molds cools, the tie bars quickly respond to the contraction of the resin and contract. consequently, the shape of the mold can be accurately transferred to the molded product. Fig. 1 is a schematic side view of an injection molding apparatus according to the invention; Fig. 2 is a graph for illustrating a relation between stress applied to the tie bars of the apparatus of the invention and elongation of the tie bars; Fig. 3 is a sectional view of the one of the four tie bars incorporated in the apparatus shown in Fig. 1; and Fig. 4 is a view showing that the mold of the apparatus in Fig. 1 has been slightly opened by the secondary pressure of the molten resin in the cavity. DESCRIPTION OF THE PREFERRED EMBODIMENT Referring to Fig. 1, there is shown an injection compression molding apparatus embodying the concept of the present invention. This machine comprises a hydraulic cylinder 1 and a clamp screw 2 constructing a clamp unit 30, a movable platen 3, a front stationary platen 6, a rear stationary platen 10, a movable mold 4 and a stationary mold 5 forming therebetween a cavity 7, tie bars 8 (there are four tie bars) and an injection nozzle 9. A plastic resin that is molten by heat is injected through the nozzle 9 into the cavity 7 under high pressure to mold a disk 7a. The clamp unit 30 is fixed to the rear stationary platen 10 supported at each of its four corners by one end of each tie bar 8. The front stationary platen 6 is supported at each of its four corners by the other end of each tie bar 8. The stationary mold 5 is fixed to the front stationary platen 6. The movable mold 4 is fixed to the movable platen 3 so as to be movable with a movement of the movable platen 3. For closing the pair of molds 4, 5, the clamp unit 30 pushes the movable platen 3 forward toward the front stationary platen 6 while the movable platen 3 is being guided by the tie bars 8 to move the movable mold 4 until parting surfaces 16 of the molds 4, 5 contact each other. At this time, each of the tie bars 8 is stretched by a specific length Δℓ₁ (entire length becomes L₀) so that the parting surfaces 16 of the molds 4, 5 are accurately in contact with each other. In general, since there remains a positioning error of the order of several ten microns even if the relative positions of the platens 3 and 6 are strictly adjusted, the platens 3 and 6 are not in accurately parallel to each other, and thus the parting surfaces of the molds 4 and 5 are not in accurately parallel to each other. Therefore, if the tie bars are rigid, the movable mold 4 cannot move further toward the stationary mold 5 after a part of the parting surface of the movable mold 4 has contacted a part of the parting surface of the stationary mold 5. This means that the molding surfaces of the molds 4 and 5 stay out of accurately parallel to each other. However, since each of the tie bars 8 of the invention is small in modulus of elasticity until elongated by the specific length Δℓ₁, each tie bar yields to the force of the clamp unit 30 to elongate by Δℓ₁. The specific elongation length Δℓ₁ of each of the tie bars is so selected that the parting surfaces 16 of the molds 4 and 5 are in contact at their entire surfaces with each other when the tie bars 8 are elongated by their respective specific elongation lengths Δℓ₁. Accordingly, the molding surfaces of the molds 4 and 5 become in accurately parallel to each other. After the parting surfaces 16 of the molds 4 and 5 are completely in contact with each other in the way as above, the nozzle 9 injects a molten resin into the cavity 7 at a high pressure. At this time, the tie bars 8 are further stretched by a length ΔL of the order of microns due to the high pressure. As a result, the parting surfaces of the mold halves are parted by ΔL as shown in Fig. 4. Each of the tie bars 8 is structured such that its modulus of elasticity changes to a large value when its elongation has exceeded the length Δℓ₁. Thus, each tie bar further stretched by ΔL from Δℓ₁ produces a restoring force exterting as a compressing force on the resin in the cavity 7. Imediately after the injection of resin has been completed, the resin in a gate 31 of the stationary mold 5 cools to be solidified thereby to seal the gate 31. After the gate seal has been completed, the resin in the cavity 7 cools while being applied with the compressing force caused by the tie bars 8. Therefore, the final molded product has a shape accurately identical to a shape defined by the molding surfaces of the molds 4 and 5. Fig. 2 shows a relation between elongation of each tie bar and stress applied thereto. The tie bar is stretched by a small stress along a line a until elongated by the length Δℓ₁, but is required to given a large stress after the elongated length exceeds Δℓ₁ as shown by a line b. In other words, the elongation-stress characteristic curve suddenly become fairly steep when the elongation exceeds the specific length Δℓ₁. The tie bar is elongated along the line a by the force of the clamp unit until the elongation reaches Δℓ₁, when the parting surfaces of the movable and stationary molds become in completely contact with each other (primary clamping step), and further elongated along the line b by the high pressure of the injected resin until the further elongation reaches ΔL. It would be ideal if a material having such a characteristic as shown in Fig. 2 were available. But, there exists no such material. Thus, as a preferable structure, each tie bar is made to have a dual structure as, for example, shown in Fig. 3. Referring to Fig. 3, each tie bar comrises a member 12 having a small modulus of elasticity and a second member 11 having a large modulus of elasticity. The member 11 is hollow cylindrical in shape, and fixed at one end to the front stationary platen 6 with a mounting screw 17. The other end 13 of the member 11 is not fixed but loosely fitted to the rear stationary platen 10 as a free end. The member 12 which is inserted in the hollow inside of the hollow cylindrical member 11 consists of two portions 12a and 12b joined together. These two portions 12a and 12b have different thicknesses from each other. The end 19 of the thinner portion 12a is fixed to the front stationary platen 6 with a screw 21. The end 20 of the thicker portion 12b is fixed to the rear stationary platen 10 with a screw 22. The modulus of elasticity of the thinner portion 12a is smaller than that of the member 11. Preferably, the thicker portion 12b has a modulus of elasticity equal to or larger than the modulus of elasticity of the member 11. After the elongation of the member 12 has reached Δℓ₁, the two members 11 and 12 are connected parallel by abutment of screws 15 and 14 mounted on the members 11 and 12, respectively, so that the apparent modulus of elasticity of the tie bar increases suddenly. The value Δℓ₁ can be set by adjusting the gap Δℓ₁ between the adjusting screws 14 and 15. The screw 14 is mounted on the thicker portion 12b of the inner member 12, while the screw 15 is mounted on the inner wall of the outer member 11. Fig. 4 shows the state in which the parting surfaces 16 of the molds 4 and 5 are separated by a distance ΔL apart after the injection nozzle 9 has injected resin into the cavity 7, when each of the tie bars 8 has elongated by ΔL further from the Δℓ₁ elongated state. As the resin in the cavity cools, the deformation (elongation) of each tie bar decreases so that ΔL approaches zero. As a result, accurate injection compression molding can be achieved. In the novel molding apparatus of the invention, each tie bar comprises two members that differ from each other in modulus of elasticity. During the primary clamping step of closing of the mold, the member having the smaller modulus of elasticity stretches within the region a of the stress-elongation characteristic line shown in Fig. 2. Therefore, even if the four tie bars stretch by different amounts during the closure of the mold, the stress, or the compressing force, does not differ greatly among the four bars. For this reason, the pressures applied by the four bars are substantially the same. Hence, substantially identical pressures are applied to the platens at the four corners when the mold is closed. After the cavity of the mold has been filled with the resin, the opening force produced by the injection pressure inside the cavity opens the mold. During this process, the stress-elongation characteristic line of each of the tie bars goes into the region b shown in Fig. 2. At this time, a large amount of stress can be stored even if the elongation is small. That is, the energy of the elongation stored in the tie bar members having the larger modulus of elasticity is released as a force that compresses the resin in the cavity after the completion of the injection. Thus, an ideal compression molding can be attained, because the compressing force acts on the resin inside the mold as soon as the injection is completed. Strictly, when the compression stroke starts, the force applied to the resin is equal to the pressure divided by a factor which depends on the modulus of elasticity of the tie bars. Generally, the platens of a molding apparatus are not expected to exhibit a high degree of parallelism as described before. Usually, a deviation of tens of microns from the parallelism occurs even if an adjustment is made most carefully. Therefore, where the molten resin is compressed by the elongation of the tie bars after the injection is complete, the four tie bars must stretch by the same length. Then, compressing forces of the same magnitude must act on the four corners of the bars; otherwise the mold could not be compressed while keeping the parallelism. In view of the foregoing, the invention has been made. The novel molding apparatus, schematically shown in Fig. 1, is characterized in that each tie bar 8 has a dual structure comprising the outer member 11 and the inner member 12 (Fig. 3). The primary clamping step of mold closure is effected prior to injection. For this purpose, the hydraulic cylinder 1 is actuated to stretch the inner member 12 of each tie bar by Δℓ. The opposite ends of the member 12 having the smaller modulus of elasticity are fastened to the stationary platens 10 and 6. Then, the adjusting screw 14 on the member 12 having the smaller modulus of elasticity comes into contact with the stopper screw 15 mounted on the outer member 11 having the larger modulus of elasticity. When the injection step is started, the injection nozzle 9 produces a high pressure inside the cavity 7. This pressure is received by these two members 11 and 12 of different moduli of elasticity. As a result, the apparent modulus of elasticity increases. The turning point at which one modulus of elasticity is switched to the other larger can be set at will by adjusting the gap Δℓ₁ with the screws 14 and 15 mounted on the members 12 and 11, respectively. When an optical disk substrate having a diameter of 130 cm and a thickness of 1.2 cm was molded, the tie bars behaved in the manner described below. The member 12 of each tie bar was designed to stretch by 100 microns when subjected to a load of 10 tons. The primary clamping step of mold closure was performed with a force of 3 tons. At this time, the screws 14 and the stoppers 15 on the four tie bars were so set that ΔL became null. Subsequently, the nozzle 9 injected molten polycarbonate resin at a temperature of 320°C at a pressure of 240 Kg/cm² so that the parting surfaces 16 of the molds 4 and 5 became apart from each other by 30 microns, i.e., the mold opened. At this time, the injection energy was stored in the form of elongation of the tie bar members 11 and 12. Thereafter, the gate 31 sealed. As the disk 7a molded inside the cavity 7 cooled, a compressing force due to the elongated tie bar members 11 and 12 was exerted on the disk being cooling in the cavity to bring ΔL to zero. The molded optical disk 7a had spiral grooves whose width was 0.8 micron, the depth of each groove being 0.01 micron. The double refraction index of the optical disk was less than 12 nm at a frequency at which information is written to the disk. The depth of the grooves was 0.098 to 0.099 micron. Thus, the disk substrate was molded quite accurately. As described above, an important feature of the invention lies in the use of tie bars whose apparent modulus of elasticity increases rapidly after a certain elongation is reached. This permits a compressing force to be applied to the cavity while maintaining the parallelism of the cavity if the platens and the molds have somewhat low degrees of parallelism. Hence, optical disks and lenses which are required to be fabricated to tolerances of the submicron order can be molded satisfactorily. Since the modulus of elasticity of the tie bars and its turning point can be set at will, it is possible to accommodate any desired compressing force and any amount of opening (ΔL) of the mold by appropriately selecting the moduli of elasticity of the two members 11 and 12 of each tie bar and their thicknesses even if parts having different thicknesses or requiring different amounts of contraction are modled. Therefore, the injection molding apparatus is quite simple in structure and does not need any hydraulic control circuit that is complex in structure and expensive. Consequently, the apparatus is capable of molding plastic parts stably and reliably. The material of the components of the molding apparatus is not limited to steel. For example, the member 12 of each tie bar can be made from a plastic which has a small modulus of elasticity and a large elastic limit. Also, the structure of each tie bar is not restricted to one consisting of a hollow member and a second member inserted in the hollow member. For instance, the tie bar may consist of two parallel cylindrical or prismatic members.

Claims: A method of molding a plastic using an injection molding apparatus, comprising the steps of: injecting a molten plastic material through a gate into a cavity between a pair of molds at a high pressure; sealing the gate; and cooling the injected molten plastic material while applying a compressing force to the plastic material in the cavity, characterized in that energy of the high pressure in the injecting step is stored in the form of an elastic elongation of tie bars of the injection molding apparatus beyond a specific amount of elongation each of the tie bars having a much larger modulus of elasticity when elongated beyond the specific length than when elongated up to the specific length, and in that the compressing force in the cooling step is caused by a restoring force of the elongated tie bars. A method as set forth in claim 1 further comprising the step of clamping the molds together wherein during said clamping step, the tie bars are elongated to said specific length. An injection molding apparatus for molding a plastic, comprising: a pair of stationary platens (6, 10) connected together by tie bars (8); a movable platen (3) capable of moving along the tie bars; a pair of stationary and movable molds (5, 4) for forming therebetween a cavity (7) in which molding is performed, the stationary mold (5) being fixed to one (6) of the stationary platens and the movable mold (4) being fixed to the movable platen; an injection nozzle (9) for injecting a molten resin into the cavity; and clamping means (30) for clamping the movable mold, characterized in that each of said tie bars (8) has a small modulus of elasticity when elongated up to a specific length and a large modulus of elasticity when elongated beyond the specific length. An apparatus as set forth in claim 3, wherein the length, thickness and larger modulus of elasticity of the tie bars are determined from a relation between a volumetric coefficient of contraction of the plastic material to be molded and a volume of the cavity. An apparatus as set forth in claim 3 or 4, wherein each of said tie bars (8) comprises: a first member (12) having a small modulus of elasticity, opposite ends of the first member having a small modulus of elasticity, opposite ends of the first member being fixed to the pair of stationary platens, respectively; a second member (11) having a large modulus of elasticity one end of the second member being fixed to one of the pair of stationary platens; and means (15, 14) for connecting the first and second members when the first member is elongated by the specific length thereby to increase the modulus of elasticity of each tie bar. An apparatus as set forth in claim 5, wherein said second member (11) comprises a hollow member, and said first member (12) is disposed in the hollow inside of the hollow member. An apparatus as set forth in claim 5 or 6, wherein said connecting means (15, 14) comprises members mounted on the first and second members, respectively, which abut against each other when the first member is elongated by the specific length.

Inventors: ITO, AKIO, NAKATANI, YOSHIO, SUNOHARA, MASAAKI, TAMURA, TORU
Applicants: MATSUSHITA ELECTRIC INDUSTRIAL CO., LTD.
Application year: 1987
Main classification: B29C45
IPC codes: B29C45