LIQUID CRYSTAL COMPOUNDS, MIXTURES AND DEVICES

Abstract: Compounds for use in ferroelectric smectic liquid crystal mixtures of general formula (I), where R1 is alkyl, Y is COO or OOC, m, n and p are 0 or 1 provided m + n is 2 or less and when Y is OOC, p is 0, X is a mesogenic group, especially 4<1> -alkyl- or alkyl- biphenyl or bicyclohexyl. Methods for preparation of these compounds are given, and ferroelectric smectic liquid crystal mixtures containing them are described.

Description: LIQUID CRYSTAL COMPOUNDS, MIXTURES AND DEVICES The invention relates to novel compounds which may be used as constituents of ferroelectric smectic liquid crystal mixtures, to such mixtures containing these compounds, and to electro-optical devices which use these mixtures. Ferroelectric smectic liquid crystal materials use the ferro¬ electric properties of the chiral tilted smectic C, P, G, H, I and K phases (designated S* Q etc, the asterisk denoting chirality). The S c phase is generally the most useful, as it is the most fluid, and it is particularly desirable that the material shows an S A or nematic (denoted N) phase at temperatures above the chiral smectic phase, to assist surface alignment in a liquid crystal device. Ferroelectric smectic liquid crystal materials desirably have low viscosity, S c phases that persist over a broad temperature range which includes ambient temperature and have a long helical pitch, chemical and photochemical stability, and a high spontaneous polarisation coefficient, Ps, measured in nC cm~2. Such materials offer the possibility of very fast switched liquid crystal display devices, with bistable characteristics. Although some single compounds show all of the desirable properties outlined above, ferroelectric smectic liquid crystal materials in use today generally consist of a mixture of compounds at least one of which is an optically active compound, ie containing an asymmetrically substituted carbon atom. This asymmetric centre is generally combined with a mesogenic molecular 'core 1 . A principal function of the optically active compound in the mixture is to induce the mixture to show a helical smectic phase, eg S c *, and to have a high Ps. A wide variety of such compounds is- known, but it is not usual to find compounds which result in S c * mixtures with all of the above mentioned desirable properties. For example the alpha-hydroxycarboxylic acid derivatives described in PCT/GB85/00512 which contain the asymmetric centre: CH- -coo-c-coo- H form S c * mixtures with, a very high Ps but a very short helical pitch. It is an object of the invention to explore the possibilities of other asymmetric centres, to provide optically active compounds of increased usefulness in ferroelectric smectic liquid crystal mixtures. According to the invention a novel compound has a formula I: where R]_ is alkyl, Y is selected from -COO- or -00C-; m r n and p are independently 0 or 1, provided that (m+n+p) is no more than 2, and when Y is OOC then p is O; and X is a mesogenic group. The term "mesogenic" used herein with, reference to the group X indicates that X is one of the molecular "cores" composed of chains of linked " cyclic group that induce the molecule to show liquid crystal phases or to be miscible with, liquid crystal materials, particularly those showing a smectic G liquid crystal phase, ie 'smectogenic'. Many such mesogenic or smectogenic cores are known, for example the groups shown attached to the group -C00R* in EP-A-0110299, and the groups represented by the symbol Q in USP 4613209. The asterisk in formula I indicates the asymmetric centre. Also the invention provides a ferrolectric smectic liquid crystal material, being a mixture of compounds, at least one of which is a compound of formula I in an optically active or racemic form, preferably the former. The structural preferences for the compound of formula I discussed below are based largely on suitability and desirability for use in such mixtures. Preferably R^, in formula I is C^ - C5 n-alkyl, especially methyl. Preferred structures for compounds of formula I are therefore those listed in table 1 below. Table 1 0CH„ 1 3 OVCH-COO-X 1.1 Table 1 (Contd) OCH., I 3 1.3 Particularly preferred structures are 1.1, 1.2, 1.3, 1.5 and 1.7 listed in table 1. The advantages of the invention derive primarily from the nature of the novelasymmetric group in formula I and the nature of the mesogenic group X is less critical, although for use in ferroelectric smectic liquid crystal mixtures the group X is preferably a smectogenic group. The group X may therefore be a known smectogenic group. Some preferred groups X are listed in table 2, R is alkyl or alkoxy containing 1 to 12 carbon atoms. The phenyl rings shown in table 2 may be substituted, as shown with respect to groups 2.1, 2.2 and 2.3 in table 2 for example. In table 2 - V represents trans cyclohexyl and (F) indicates that the group may carry one or more fluorine substituents on one or more of the rings shown. In table 2, R is preferably n-alkyl or n-alkoxy containing 3 to 10 carbon atoms. Structures 2.1, 2.2 and 2.4 are particularly preferred. Compounds of formula I may be made by a variety of synthetic routes, for example the routes A and B shown schematically in Figs 1 and 2. Route A starts from commercially available 2-hydroxy- 2-phenyl propionic acid. It will be apparent that the individual steps use TJable 2 10 ■ OO 2 -©-o 2.5 15 -o®-* 2.6 0>-<^-H 2.7 -<θ)^-R 2.8 -<^-C00-^θ)- 2.13 35 well known chemical reaction although the products and overall routes are novel. A ferroelectric smectic liquid crystal mixture of the invention contains at least once compound of formula I. Preferably the compound of formula I is in an optically active form. Typically the mixture contains 1-20 wt % of the compound of formula I f for example around 10% or less. The inclusion of a compound of formula I in the mixture offers the advantages of a high Ps combined with a very long helical pitch of the S* c phase. This long pitch is valuable because in many common types of ferroelectric smectic display device it is desirable to have a helical pitch length comparable with the spacing of the electrodes of the device, which is generally around 1-5 μ. An example of such a device is the "Clark Lagerwall device" described in App..Phys. Lett . 36, (1980), 899. A ferroelectric smectic liquid crystal mixture according to the invention contains at least one compound of formula I. Typically the mixture will contain 1-20% by weight of the compound of formula I, eg around 10% or-less., in an optically active enant- -iomeric form. The mixture also contains one or more compounds which either separately or together show an Sc phase. Such compounds are known as smectic hosts. A large number of classes of compounds which may be used as Q smectic hosts are known, and some examples of suitable classes ! are listed in table 3> Of these compounds those of formula 3.1 3.2, 3-3 an d 3.^ are preferred, especially where R A and R B independently contain 5-10 carbon atoms. It is particularly preferred to use a mixture of two or more members, eg homologues, _ of the same class for example to reduce the melting point. These preferred hosts allow the possibility of Sc mixtures showing an Sc phase persisting over a wide temperature range including room temperature, and also an S^ phase at a temperature- above the Sc, to assist in alignmentof the liquid crystal material. 0 Typically the mixture will contain 40-99% of host compounds, eg around 90 - 95 wt fo. -K B where R . A and -, τ R_B a „_r_.„e, r G.^ _ 12 n -- al xk^rl i or n-alkoxy. Additives in such a mixture may serve a number of functions. One such function is as "pitch compensators." "Pitch compensation" is the inclusion in the ferroelectric smectic mixture of two or more compounds which induce the appearance of helical smectic phases of opposite twist sense. In such a case the compounds will unwind the helical phase induced by the other. This may be used to produce a long pitch helical smectic phase, and by the controlled use of appropriate quantities of the two compounds the pitch of the mixture may be closely controlled. In mixtures according to the invention, pitch compensation may be achieved conveniently by using opposite-twisting compounds of formula I as discussed above which may be different compounds of formula I or enantiomers eg the L(+) and S(+) forms of such a compound . Alternatively or additionally other optically active additives may be used, for example the amides described in PCT/GB 87/00223, eg any of those listed in table 6 thereof, or the terphenyls described in UK Patent Application 8703103, the latter being particularly suitable when the host includes one or more compounds of formula - 3 * Examples of pitch compensators of these two types include the compounds: Qfl j{ -<S-<S-C00CHC0N-(Q>-R , . l Cl CH R-<@-<θ)-<@-0-GHG00C 2 H 5 _|.2 where R and R' are independently ^ _ 12 n-alkyl or n-alkoxy. R' is preferably CH_. Many other pitch compensating additives will be apparent to those skilled in the art. For example when the host con ¬ tains one or more compounds of formula 3-1 or 3.2 a suitable pitch compensator may be a compound of formula 3.1or 3.2 where R or/and R A are optically active alkyl or alkoxy. Compounds of formula I frequently form helical 3 G phases of such long pitch in a smectic mixture that pitch compensation is unnecessary. Additives may be used to encourage the appearance of an S^ phase at a temperature above that at which the S phase persists, to assist in alignment of the SQ phase during assembly of the service. When the host consists largely of compounds of formula 3.1 or 3.2 preferred additives to achieve this have a formula: R-©-®-∞o-@-R' where R and R! are independently n-alkyl or n-alkoxy containing 1-12 carbon atoms, especially 5-9. Additives may alternatively serve the function of suppressing undesirable smectic phases such as S^ or Sg so that these appear, if at all, as far as possible from the working temperature range. A preferred class of additives fulfilling this function are the esters of formula: where R and R^are independently n-alkyl or n-alkoxy containing 1-12 carbon atoms, especially 5-9. Compounds of formula may also be used as additives to suppress undesirable smectic phases in mixtures where they are not used as hosts. Additives may also improve other properties of the mixture, for example to increase the switching speed. Compounds which do this include those which contain a group, for example those of general formula CN » ' {X " ■ ,R 7-~ where R and ! are independent alkyl groups especially containing 3 to 10 carbon atoms. Other known additives may be included, for example to improve viscosity, melting point or other properties. Typically a mixture according to the invention may contain 0-50 wt% of additives, preferably 0-20%. Only minute amount- of pitch compensators may be necessary, eg less than 1 wt% of the tight twisting compound preferably no more than about 10 wt% of compounds such as 5, 6 7.1 or 7.2 . A mixture according to the invention may be used in any of the known types of ferroelectric smectic liquid crystal electro- optic device, and a device incorporating such a mixture is another aspect of the invention. The invention will now be described by way of example only with reference to the accompanying drawings, which show: Figs 1 & 2: preparative routes for compounds of the invention. Fig 3 : a liquid crystal * device. Example 1. A. Preparation, via route A of compounds of Formula: OCH, q cHcoo- Step 1. An intimate mixture of L-(+)-mandelic acid (1.52g 10m mol) and silver (I) oxide (4.6g, 20m mol) was added to cooled (ice-salt) θ methyl iodide (5.68g, 40m mol) batchwise during 1 hour, excluding light throughout. The mixture was heated under reflux for 2 hours, then it was cooled, diluted with ether (50 ml) and the inorganic salts removed by filtration. Removal of the solvent gave a pale yellow oil. ]e Step 2. The oil from step 1 was suspended in a mixture of aqueous 10% potassium hydroxide (lOOml) and methanol (30ml), and heated to 70°C for 4 hours. The solution was then cooled, acidified, and extracted with ethyl acetate (3 x 100ml). The combined organic 20 extracts were shaken with aqueous 10% sodium thiosulphate (100ml) and dried over Mg S0 4 . Removal of the solvent gave a white solid which was purified by recrystalisation from petroleum fraction (bp 60-80°C) Yield = 1.41g, 85%. F^] 2 ^ in alcohol was + 150°. Melting point was 63-64°C„ 25 Step 3- The 0-methyl L-(+)-mandelic acid from step 2 above (l-66g, 10m mol), the appropriate alcohol or phenol (11m mol), DCC (2.27g, 11m mol) and 4- pyrrolidinopyridine (0.148g, l mol) were stirred in sieve-dried dichloromethane (50ml) at room temperature until the 30 reaction seemed to be complete by tic (silica gel, dichloromethane: petroleum ether 2:1). The precipitated dicyclohexylurea was filtered off and the filtrate was washed successively with water (3 x 50ml) aqueous 5% acetic acid (3 x 50ml), water (3 x 50ml) then dried over Mg SO4. Removal of the solvent gave a brown residue 35 which was purified by column chromatography on silica gel, using dichloromethane: petroleum fraction (bpt 60-80°C) as elUant, followed by recrystallisation from petroleum fraction (bpt 60-80°C) . Using this method the following compounds were prepared: Compound Yield m pt L < J ^ Liquid Crystal Properties (i) Compound A 25 mole % solution of this compound in the smectic mixture HI, having the composition: o experienced a Sc-S A transition at 58.1°C. The Ps value of this compound, extrapolated to 100%, was measured at various temperatures in HI. The results are tabulated below, where T refers to the temperature below the SC-SA transition. T Ps -10°C 92.5 -20°C 136.2 -30°C 170.8 (ii) Measurement of helical pitch. Indications of the possibility of inducement of a long pitch helical smectic phase by the compounds were made by measurement of the pitch length of cholesteric phases produced by mixing the compounds with the nematic material E7 which has the composition: G 7 H 15 ' ® " ® 'ar 25 Wt% 0 C.3H 17 0-g)-<g -QI 16 wt * C 5 H ll-@-@-@- car 8 wt% (It should be noted that the formation of a long pitch cholesteric phase by a compound in a nematic mixture is an accepted indication - > of the ability of the compound to form long pitch helical phases) . Theresults were as follows: extrapolated pitch OCH. 0 ®~ OK- -™C0C - 2>-<o> CO, 0.63 J- 10 21 5 It is useful to compare these pitch lengths with hose produced in E7 by the smectic lactate compounds described in PCT/GB85/00512: CH, ° G- T ∑L. 7 G-(Q)-(Q)-CCC .Cπ " .CG0-C 2 H ς 0.096 Λ. The very considerably longer pitch induced by the mandelic acid 5 derivatives of the present invention is thus immediately apparent. Example 2. Preparation via route A of compounds of Formula: Borane-tetrahydrofuran complex, (13cm 3 of a 1.0M solution in tetrahydrofuran, 13mmol), was added slowly to a stirred solution of n-nonyl or n-oσtyloxy biphenyl carboxylic acid (lOmmol) in dry tetrahydrofuran (100cm 3 ) at 0°C under an atmosphere of dry nitrogen. The solution was stirred for 3h and the reaction was quenched by the addition of a 1 : 1 mixture of water and tetrahydrofuran (90cm 3 ). The resulting solution was saturated with potassium carbonate, the layers were separated and the aqueous layer was shaken with ether (2x50cm 3 ). The combined extracts were dried and evaporated to give the crude product, which was recrystallised from industrial methylated spirit to give the pure product as white needles. C 9 H 19 - θ)-<@>-GH 2 0H (82%) mp = 100 -102°G G 8 H 1? 0-<g)-<g)-CH 2 0H - (72 ) mp = 1^5 -1^7°C Step 5- The carboxylic acid from Step 2 (lOmmol), the appropriate alcohol from S tep A 3 (llm ol), dicyclohexyl-carbodii ide (DCC) (llmmol ) and 4-pyrrolidinop yridine (lmmol) were stirred in sieve-dried dichloro ¬ methane (50 ml) at room temperature until the reaction seemed to b e complete by tic. The precipitated dicyclohexyLurea was filtered off and the filtrate was washed successively with water ( 3x50 ml) aqueous 5% acetic acid (3x50 ml), water (3x50 ml) then dried over M g SO . Removal of the solvent gave a brown residue which was purified by column chromatography on silica gel, using dichloromethane: petroleum fraction (bpt 60-80°C) as eluant, followed by recrystal- lisation from petroleum fraction (bpt 60-80°C). The following compounds were prepared in this way: 0CTL. <θ)-CHCδ0CH 2 -<g>-<g)-0C 8 H 17 mp 39°G U] \ 5 - ^ .2° <g)-CHC00GH 2 -<@>- g>-G 9 H 19 mp 32°C ^ = +3.9° Example 3 Preparation of compounds of structure: by route B. Step 12 A solution of (S)-(-)-2-hydroxy-3-phenylpropionic acid (lOmmol), in a mixture of methanol (50cm 3 ) and cone.sulphuric acid (0.5CIΪΪ 3 ), was heated under reflux for 2h. The solution was cooled and the solvent was removed under reduced pressure. The residue was dissolved in ethyl acetate (50cm 3 ) and this solution was shaken successively with saturated aqueous sodium chloride (50cm 3 ) , saturated aqueous sodium hydrogen carbonate (50cm 3 ) and saturated aqueous sodium chloride (50cm 3 ). The organic phase was dried and evaporated to give the curde product which was recrystallised from petroleum fraction (b.p. 40-60°C) to give the pure product (98%) as white needles. m.p. 48-49°C, DΛl =-1.2° in chloroform. The product was identified as: OH Step 13 A solution of methyl (S)-(-)-2-hydroxy-3-phenylpropionate from step 12 (lOmmol) in dry tetrahydrofuran (50cm 3 ) was added, during Ihr, to a cooled, stirred suspension of sodium hydride (llmmol) in dry tetrahydrofuran (75cm 3 ) under an atmosphere of dry nitrogen. Stirring was continued for 30 min. Dry methyl iodide (llmmol) was added during 15 min. and the mixture was heated to 40°C for lhr. The resulting suspension was cooled, excess sodium hydride was destroyed by the addition of "wet" tetrahydrofuran (50cm 3 ) and the mixture was poured into ice (100g). The solution was saturated with potassium carbonate and the organic layer was separated. The aqueous layer was shaken with ether (2x50cm 3 ) and the combined extracts were dried. Evaporation of the solvent followed by distillation under reduced pressue gave the pure product (90%) as a colourless oil b.p. 172-175°C C @ 0.2mmHg. _ ] = -12.4°. The product was identified as : Step l A mixture of methyl (S)-(-)-2-methoxy-3-phenylpropionate from step 1 (lOmmol), aqueous 10% potassium hydroxide (50cm 3 ) and methanol (15cm 3 ) was stirred overnight at room temperature. The solution was cooled, acidified by the addition of dil. hydrochloic acid and saturated with sodium chloride. The resulting mixture was shaken with ethyl acetate (2x50cm 3 ), the combined extracts were dried and the solvent was evaporated to give the crude product. This was purified by column chromatography on silica gel in a 5:1 mixture of dichloro¬ methane and methanol to give the pure product as a colourless oil (95%) [o = -17.7° in chloroform. The dicyclohexylamine salt had m.p.l22-124°C. The product was identified as: OCH- 1 J ©- CH..CHC00H X_/ 2^ Step 15 This was carried out using a scheme analogous to that of step 3 with the acid of step 1_J. and the appropriate alcohol or phenol. The following products were prepared: Ξxamυle k . Preparation of compounds of structure; by route A Step 6 Borane - tetrahydrofuran complex (13ml of a 1.0M solution in tetrahydro uran; 13mmol) was added slowly to a stirred solution of (S)-(+)-2-methoxy-2-phenylacetic acid (lOmmol) prepared via step 2 in dry tetrahydrofuran at 0°C under an atmosphere of dry nitrogen. The solution was sitrred for 3h and the reaction was quenched by the addition of a 1:1 mixture of water and tetrahydrofuran (90ml). The resulting solution was aturated with potassium carbonate, the layers were seprated and the aqueous layer was shaken with ether (2 0 x 50ml) . The combined extracts were dried and evaporated to give the crude product (84%) as a colourless oil, b.p. 130-133° @ 0.005mmHg. _θ{] = +118° in chloroform. The product was identifed as: OCH,, 5 (OVCHCH„0H N — ' * Step 7 Ξsterification of the product of step Cl with n-octyloxy biphenyl carboxylic acid was carried out using a scheme analogous to that 20 of step 3 above. 26 was prepared mp = 68°C [0(1 = 6.5' 25 Example - Further examples of ferroelectric smectic liquid crystal mixtures of the invention are listed below. Mixture 5 was made into a mixture with the smectic mixture HI (identified in l.B.(i) above). The Ps was measured and extrapolated to 100 % at two temperatures T below the S-, - S. transition. T Ps -10° 1 .9 nCc "2 -20° 27.0 nCcm "" Mixture 5B Ps was measured at two temperatures T below the S-, - S. transition in a mixture consisting of a mixture of: CH G 3 H 1 7-@"@" C00 ~@" GH 2 ™ G 2 H 5 ( -} and extrapolated to 100 % of the compound. T Ps -10° 67 nCcm "2 -2 -20° 100 nCcm Mixture 5C The compound of the invention used in mixture 5B was ira.de into a 10 vrt% solution in a compound of formula 3 - 5 of table 3 with R being CQH 1 7 . Liquid crystal transitions ( C) were : s ? 5 -. S G -> 74.3 -> S A ■ » 101.3 -> I (116.7 N) Ps extrapolated to 100 % at the temperatures ( C) indicated , and tilt angle ( ) of the S ^ , phase of the mixture were : T Ps Tilt 60 1 16 64.3 96 12 70 72 4 Mixture 5~> The compound of the invention usei in mixture 53 ,/,as ~B- 4 e into a 5 wt % solution in HI ( see example IB( i) ) . Liquid crystal transitions were : S ? 23 . c - * 5 G 94.2 S A » 93. » N* * 1^2 I Ps extraplated to 100 % at the temperatures indicated was : 5D (contd.) 1 Ps Tilt 30 164 11.5 50 130 11.5 70 30 H.5 34.2 44 10.0 Mixture 5E was made into a 3 wi solution in HI. Liquid cryatal transitions were: 25 -. S c -> 95 ■ » S A -* 102 -* N -» 146.5 -* 1 Ps extrapolated to 100 % at the temperatures indicated was: T Ps_ Tilt " 50 °>3 9.5 70 53 9.0 5 23 7.0 Mixture 5 The propylbicyclohexyl compound prepared in example 1 was made up into a 5 wt % solution in HI. Liquid crystal transitions were: Solid -» 28 -> S G -j 77 -* S A - 96 - IT - 142 - I s extrapolated to 100 and tili at the temperatures indicated were: T Ps Tilt 30 60 15 50 40 12 όo 2^ 9-5 77 24 7.0 „ PCI/GB87/0068 An example of the use of a compound of Formula I in a liquid crystal material and device embodying the present invention will now be described with reference to Figure 4. In Figure 4 a liquid crystal cell comprises a layer 1 of liquid crystal material exhibiting a chiral smectic phase sandwiched between a glass slide 2 having a transparent conducting layer 3 on its surface, eg of tin oxide or indium oxide, and a glass slide 4 having a transparent conducting layer 5 on its surface. The slides 2,4 bearing the layers 3,5 are respectively coated by films 6,7 of a polimide polymer. Prior to construction of the cell the films 6 and 7 7 are rubbed with a soft tissue in a given direction the rubbing directions being arranged parallel upon construction of the cell. A spacer 8 eg of polymethyl methacrylate, separates the slides 2, 4 to the required distance, eg 5 microns. The liquid crystal material 1 is introduced between the slides 2,4 to the required distance, eg 2 microns. The liquid crystal material 1 is introduced between the slides 2,4 by filling the space between the slides 2, 4 and spacer 8 and sealing the spacer 8 in a vacuum in a known way. Preferably the liquid crystal material is in the smectic A, nematic or isotropic liquid phase (obtained by heating the material) when it is introduced between the slides 2,4 to facilitate alignment of the liquid crystal molecules with the rubbing directions on the slides 2,4. A polarizer 9 is arranged with its polarization axis parallel t° the rubbing direction on the films 6,7 and an analyzer (crossed polarizer) 10 is arranged with its poarization axis perpendicular to that rubbing direction. When a square wave voltage (from a conventional source not shown) varying between about +10 volts and -10 volts is applied across the cell by making contact with the layers 3 and 5 the cell is rapidly switched upon the change in sign of the voltage between a dark state and a light state as explained above. In an alternative device (not shown) based on the cell construction shown in Figure 4 the layers 3 and 5 may be selectively shaped in a known way, eg by photoetching or deposition through a mask, eg to provide one or more display symbols, eg letters, numerals, words or graphics and the like as conventionally seen on displays. The electrode portions formed thereby may be addressed in a variety of ways which include multiplexed operation.

Claims: CLAIMS 1. A compound having a formul t where R-. is alkyl, Y is COO or OOC, m, n and p are independently 0 or 1, provided that (m+ n + p) is no more than 2, and when Y is OOC then p is 0, and X is a mesogenic group. 2. A compound according to claim 1 wherein X is a smectogenic group and P, is methyl. 3. A compound according to claim 2 wherein X is selected from: (F) (1?) (-0 - )- >-* -< 0 E Md _5>- E where P is C, , ? alkyl or alkoxy and (P) indicates that the phenyl ring indicated may carry a lateral fluorine substituent. 4. A compound according to claim 3 having a formula: where p 5. A a formula: where R 6. A a formula: where ?. 7. A a formula: where R is G_ to £.-. n-alkylor n-alkoxy. 8. A compound according to claim 4 having a formula: where R is C, to C_ n n-alkyl or n-alkoxy. 9. A compound according to claim 3 having a formula: OCH- i J 'OVGH-,-CH-C00-X < 10. A comnound according to claim 9 having a formula; 0CH„ (F) (F) \ 3 <g>-CH 2 -CH-C00-g>-<g>-r where R is £, to C, 0 n-alkyl or n-alkoxy. 11. A compound according to claim 3 having a formula: 12. A compound according to claim 10 having a formula: where 13. A compound according to claim 3 having a formula : where R is C_ to C-... n-alkyl or n-alkoxy. 14. A com ound according to claim 13 having a formula; where R is C, to C..-. n-alkyl or n-alkoxy. 15. A ferroelectric smectic liquid crystal material being a mixture of compounds, characterised in that at least one of the compounds is a compound as claimed in any one of claims 3 to 14. 16. A material according to claim 14, characterisei that in addition to the compound as claimed in any one of claims 3 to I 1 - it also contains at least one coπroound of formula: where R n-alkyl or n-alkoxy. 17. An electro-optical display device characterised in that it uses a liquid crystal material as claimed in claim 15.

Inventors: GRAY GEORGE WILLIAM, JACKSON ADAM, LACEY DAVID, SCROWSTON RICHARD MICHAEL, TOYNE KENNETH JOHNSON, GRAY, GEORGE, WILLIAM, JACKSON, ADAM, LACEY, DAVID, SCROWSTON, RICHARD, MICHAEL, TOYNE, KENNETH, JOHNSON
Applicants: SECR DEFENCE BRIT, THE SECRETARY OF STATE FOR DEFENCE IN HER BRITANNI
Application year: 1987
Main classification: C09K19
IPC codes: C07C69, C09K19, G02F1