LOW OVER-VOLTAGE ELECTRODES FOR ALKALINE ELECTROLYTES

Abstract: This invention relates to an electrode having a novel electrocatalyst coating and to a method for the preparation of the electrode for use in electrochemical cells, particularly those employing alkaline electrolytes in the anolyte compartment of the cell. The electrode of the invention comprises an electrically conductive substrate coated with the oxides of cobalt and tungsten. The electrode is particularly suitable as an anode since the electrocatalyst coatings resist destruction by oxygen.

Description: The invention relates to improved electrodes for use in electrolytic cells utilizing alkaline electrolytes. In an electrochemical cell having as basic components at least one anode and one cathode and an electrolyte, a chemical reaction may be achieved such as the oxidation or reduction of a chemical compound, as in an electrolytic cell or the conversion of chemical energy in a fuel into a low voltage direct current, as in a fuel cell. When the electrodes in such a cell are of relatively inexpensive material such as for instance iron or nickel, the electrodes tend to have low activity. The problem is particularly acute in electrochemical cells used, for example, in the electrolysis of water to produce hydrogen and oxygen utilizing an alkaline electrolyte (for instance a 25 percent aqueous solution of potassium hydroxide). The use of nickel as an anode material for commercial water electrolyzers is unsatisfactory because the over-voltage for oxygen evolution on nickel is high and increases with length of service. Electrode coatings of mixed ruthenium-titanium oxides are useful for the production of oxygen in acidic solutions but the chemical stability of such anodes in a strongly alkaline environment, as used in water electrolyzers, is inadequate. Graphite which is useful as an anode for chlorine production is rapidly destroyed by oxygen if used for water electrolysis. In U.S. Patent No. 4,342,792, electrocatalysts are disclosed which can be coated over a metal electrode substrate to provide an electrode of high activity and stability when used as an anode in a strongly alkaline electrolyte. Such anodes are produced by coating said electrode substrate with a homogeneous solution of a mixture of (1) at least one compound selected from iron, cobalt, nickel, and manganese, (2) at least one compound selected molybdenum, tungsten, and vanadium, and (3) at least one rare earth metal selected from the lanthanides having an atomic number of 57 to 71 inclusive. When such compounds are coated on an electrode substrate, and if such compounds are not oxides, the compound must be capable of thermo-decomposition to the corresponding metal oxide. The oxide coated substrate is thereafter cured in a reducing atmosphere. In U.S. Patent No. 4,428,805, electrodes for oxygen manufacture are disclosed. The electrodes are prepared by coating an electro-conductive substrate with a first coating of one or more metal oxides in which the metals are selected from tin, lead, antimony, aluminum, and indium followed by a second coating of a monometal or a polymetal oxide having a spinel structure. In U.S. Patent No. 4,464,239 lithiated cobaltocobaltic oxides are used as coatings for electrode substrates as a means for reducing the electrode over-voltage in a water electrolysis cell having an alkaline electrolyte. In European Patent Publication No. 0,009,406, electrodes are disclosed having electrocatalytic coatings of the nickel-molybdenum type including mixtures of cobalt and tungsten. Such electrodes are coated on electrode substrates such as nickel, iron, copper, and titanium and their alloys from a solution of compounds of these metals. The compounds used must be capable of thermal decomposition to their oxides. Subsequently, the oxide coated substrate is cured in a reducing atmosphere. In U.S. Patent No. 4,142,005 electrodes are disclosed which are particularly suitable for use as anodes in electrolytic cells. These electrodes are prepared by coating a substrate with a thermally-decomposable inorganic cobalt compound and then thermally oxidizing the inorganic cobalt compound under conditions at which the single-metal spinel is formed. In FR-A 2 099 647 electrodes are disclosed having a coating of a mixed oxide A₂BO₆ wherein A is an element selected from the group consisting of Co, Cr, Fe, Mn, Al, Ga, Ir, Rh and V and B is an element having a valence of 6 and is selected from the group consisting of Te, W, Mo and Re. The present invention resides in a process for the production of hydrogen peroxide in an electrolytic cell for the electrolysis of a mixture comprising an aqueous solution of an alkali metal hydroxide to produce an alkaline hydrogen peroxide aqueous solution, said electrolytic cell comprising an anode, said anode comprising a substrate selected from nickel or a nickel coated electro conductive substrate and an electrocatalyst coating deposited on the substrate, said electro-catalytic coating comprising the oxides of cobalt and tungsten. The anode is prepared by coating an electrically conductive substrate with an effective amount of a electrocatalytically active compound of cobalt and tungsten, such as the nitrates and chlorides. The coating can be applied to the substrate from a homogeneous solution of a mixture of compounds of cobalt and tungsten. Said compounds are converted by thermo-decomposition to their oxides subsequent to application of the coating to the electrically conductive substrate. The anodes are stable to dissolution in strongly alkaline anolyte solutions and exhibit low over-voltage initially and after long periods of service. The anode which is used in the process for the production of hydrogen peroxide may be produced by a method comprising the steps of: A) co-depositing on said substrate a homogeneous solution of compounds of cobalt and tungsten, each of which compound, when not an oxide, being capable of thermo-decomposition to the corresponding oxide and B) thermally decomposing said compounds of cobalt and tungsten, which are present other than in the oxide form, to the corresponding oxide. The present invention further resides in the use for the production of hydrogen peroxide of an electrolytic cell comprising at least an anode and a cathode, a liquid permeable separator, positioned between said anode and said cathode, wherein said cathode is in physical contact with said separator and is porous and self-draining, wherein said anode comprises a substrate selected from nickel or a nickel coated electroconductive substrate and an electrocatalyst coating deposited on the substrate, said coating comprising the oxides of cobalt and tungsten. Nickel is well known as the standard anode material for commercial water electrolyzers because of its good chemical stability in the normally employed 25 to 30 percent by weight concentration of an alkaline electrolyte. However, over the service life of the nickel electrode, the over-voltage for oxygen evolution increases. Reduced efficiency, as indicated by low levels of operational current density, results. This leads to high capital costs for the operation of the cell. Low electrolyte concentrations such as 3 to 5 percent by weight alkali as used in the production of alkaline hydrogen peroxide, are much more corrosive to a nickel electrode. The voltage or potential that is required in the operation of an electrochemical cell such as an electrolytic cell includes the total of (1) the decomposition voltage of the compound being electrolyzed, (2) the voltage required to overcome the resistance of the electrolyte, and (3) the voltage required to overcome the resistance of the electrical connections within the cell. In addition, a potential known as "over-voltage" or "over-potential" is also required in the operation of the cell. The anode over-voltage is the difference between the thermodynamic potential of the oxygen evolving anode (for instance, when utilized for water electrolysis of a strongly alkaline anolyte) when the anode is at equilibrium and the potential of an anode on which oxygen is evolved due to an impressed electric current. The anode over-voltage is related to such factors as the mechanism of oxygen evolution and desorption, the current density, the temperature and the composition of the electrolyte, the anode material, and the surface area of the anode. In recent years, increasing attention has been directed toward improving the oxygen over-voltage characteristics of electrolytic cell anodes, particularly those anodes utilized in the electrolysis of water as well as in the production of hydrogen peroxide where a strongly alkaline anolyte is utilized, for instance, a mixture comprising an alkali metal halide and 3 to 5 percent by weight an alkali metal hydroxide. Electrolytic cells for the production of an alkaline hydrogen peroxide preferably have at least two electrodes, an anode and a cathode, separated by a liquid permeable separator. Preferably the cathode is in physical contact with the separator and is porous and self-draining. In addition to having a reduced oxygen over-voltage, an anode for such purposes should also be constructed from materials which are inexpensive, easy to fabricate, mechanically strong, and capable of withstanding the environment conditions of the electrolytic cell, and particularly capable of resisting dissolution in the alkaline anolyte. The problems of increased over-potential with increasing service of nickel anodes under acidic conditions has been lessened by the recent adoption of coatings on electro-conductive substrates of noble metals of Group VIII of the Periodic Table of the Elements. However, use of expensive metal coatings such as ruthenium oxide in the production of anodes for oxygen evolution has met with the problem of dissolution of the electrode coating in an alkaline electrolyte. Those metals which, when coated on electro-conductive substrates, do not dissolve in strongly alkaline anolytes during oxygen evolution, will generally be covered with an oxide film and suffer a loss of activity with increasing service. The electrodes of European Patent Application 0,009,406 having electrode catalyst coatings such as the mixed nickel-molybdenum type which subsequent to deposition are decomposed to their oxides by heating and thereafter exposed to a reducing atmosphere at elevated temperature, show a marked over-voltage improvement over those disclosed heretofore. Useful electro-conductive substrates for use with such electrode catalyst coatings have been disclosed in the prior art as relatively inexpensive materials such as nickel, iron, copper, titanium, and alloys thereof or of other metallic substances coated with any of these materials. The electrodes of the present invention have been found to be more effective when used in water electrolysis and particularly effective when used in the production of an alkaline hydrogen peroxide using an alkali concentration of from 3 to 5 percent by weight. Such electrodes are prepared utilizing coatings of compounds of cobalt and tungsten over an electro-conduction substrate. Preferably, the cobalt and tungsten compounds are deposited as mixtures on an electro-conductive substrate consisting of nickel or a nickel coated electro-conductive substrate such as nickel coated steel. The mixtures are deposited from a homogeneous solution of the cobalt and tungsten compounds which are capable of being thermally decomposed to the oxides. Such compounds can be, for instance, the nitrates of cobalt and tungsten utilized in the preparation of the electrodes of the invention respectively from 1:1 to 5:1. The homogeneous solution of the cobalt and metal compounds utilized for coating the electro-conductive substrates in the formation of the anodes of the invention is defined as an intimate mixture of the respective solid metal compounds in their finely divided state, or a solid solution of the metal compound, or a solution of the compounds in a solvent. An intimate mixture of the solid metal compounds can be prepared in advance or the compounds can be mixed immediately prior to contact with the electro-conductive substrate to be coated. For instance, the compounds of cobalt and tungsten can be applied onto the electro-conductive substrate either separately or simultaneously. The compounds of cobalt and tungsten can be sprayed directly onto the electro-conductive substrate. Alternatively the cobalt and tungsten compounds can be present in a homogeneous solution or a mixture of an aqueous and organic solvent or an organic solvent solution of the compounds. For example, a lower alkyl compound such as methanol, ethanol, propanol, isopropanol or formamide or dimethyl formamide. The choice of a particular solvent will depend upon the solubility of the desired compounds of cobalt and tungsten. If the homogeneous solution is a liquid, it can be applied to the electro-conductive substrate to be coated by dipping, rolling, spraying, or brushing. The coated electro-conductive substrate is thereafter heated in air at an elevated temperature to decompose the metal compounds, if not oxides, to the corresponding oxides. The decomposition is suitably carried out at a temperature of from 250°C to 1200°C, preferably from 350°C and 800°C, most preferably between about 350°C to 550°C. The operation of applying a coating of the homogeneous solution to the electro-conductive substrate followed by thermo-decomposition to the oxides can be repeated successively to ensure adequate coverage of the substrate with the metal oxides so as to provide a coating thickness of from 2 to 200 µm. Coating thicknesses of from 10 to 50 µm are preferred while coatings of less than 10 µm in thickness usually do not have acceptable durability and coatings of more than 200 µm usually do not produce any additional operating advantages. The concentrations and relative proportions of the cobalt and tungsten compounds used in the homogeneous solution generally is respectively in the range of from 1:1 to 5:1, but higher or lower proportions can be used. The concentration of the cobalt and tungsten compounds in the coating bath is not critical. Particularly good coatings are produced when the concentration of the cobalt ions in the bath is within the range of from 0.5 percent to 5 percent by weight and when the relative proportion of tungsten ions to cobalt ions in the bath is maintained at about 0.5:1. The deposit of the homogeneous solution of cobalt and tungsten compounds or their oxides may be obtained by use of sequential application of a mixture, an alloy, or an intermetallic compound, depending upon the particular conditions utilized in depositing the coating. Since any of these particular combinations of metals are within the scope of the present invention, the term "co-deposit", or form thereof, as used in the present application includes any of the various alloys, compounds and intermetallic phase of the cobalt and tungsten compounds or oxides of said compounds and does not imply any particular method of application or process of formulation with respect to these metal compounds used as electrocatalysts. While the electro-conductive substrates to be coated most preferably are of nickel or nickel coated steel, other electrically conductive metal substrates can be used such as stainless steel or titanium or any other electrically conductive metal substrate if coated with nickel. The cobalt compounds used in making the homogeneous solution with tungsten compounds can be any thermally decomposable oxidizable compound which when heated in the above prescribed heating range will form an oxide of cobalt. The compound can be organic such as cobalt octoate (cobalt 2-ethyl hexanoate) but is preferably an inorganic compound such as cobalt nitrate, cobalt chloride, cobalt hydroxide, cobalt carbonate, and the like. Cobalt nitrate and cobalt chloride are especially preferred. The tungsten compounds used in making the anodes of the present invention can be any thermally decomposable oxidizable compound which when heated in the above prescribed heating range will form an oxide tungsten. The compound can be organic such as tungsten octoate and the like but is preferably an inorganic compound such as tungsten nitrate, tungsten, chloride, tungsten hydroxide, tungsten carbonate, sodium tungstate, and the like. Tungsten nitrate or tungsten chloride are especially preferred. The following examples illustrate the various aspects of the invention but are not intended to limit its scope. Where not otherwise specified throughout this specification and claims, temperatures are given in degrees centigrade, and parts, percentages, and proportions are by weight. Example 1 Electrodes were prepared in accordance with the invention by preparing a homogeneous solution of 5 percent by weight cobalt chloride and 1 percent by weight tungsten chloride WCl₆ in isopropanol. The measured weight of cobalt chloride was 1 percent, the measured weight of tungsten chloride was 0.5%. Both components were prepared in a single homogeneous solution but individual solutions could be prepared separately and thereafter mixed to form the final solution. The compounds provide a solution which is clear and homogeneous. A nickel plated steel expanded metal sample was used which was degreased in trichloroethane, etched by dipping in hydrochloric acid (about 20 percent by weight concentration) for a few seconds, and rinsed thoroughly in distilled water. Before coating, the water was removed from the sample by air drying and the sample was dried in an oven at a temperature of from 60° to 90°C. A co-catalytic coating of the above mixture of cobalt and tungsten compounds was applied by dipping the nickel coated steel expanded metal into the homogeneous solution and subsequently drying the coated metal in heated air in a furnace at a temperature of 480°C for a period of from 10 to 12 minutes. The operation was repeated several times until a visibility satisfactory film of the metal oxides was formed on the nickel coated steel expanded metal. After the final dipping operation, the coated expanded metal was heated for one hour at a temperature of 480°C to convert the coated metal compounds to their oxides. Example 2 The electrode prepared by the process of Example 1 was tested as an anode in a water electrolysis cell using as an anolyte a 4 percent by weight aqueous solution of sodium hydroxide. The anode showed a start up potential at 0.45 amps/in² (0.07 amp/cm²) of 0.56 volts (versus a saturated calomel electrode). After 104 days of operation the anode potential was 0.645 volts. The anode potential compares favorably with a nickel plated steel electro-conductive substrate used as an anode without any Co-catalytic coating. A nickel plated steel anode showed a start up potential when used in a similar electrolytic cell at 0.45 amp/in² (0.07 amp/cm²) of 0.661 volts and after 86 days of operation an anode potential of 0.730 volts. Example 3 The electrode prepared by the process of Example 1 was also tested in an electrolytic cell utilized for the preparation of an alkaline hydrogen peroxide utilizing as the alkaline electrolyte an aqueous solution consisting of 4 percent by weight sodium hydroxide and 0.6 percent by weight sodium chloride. The initial start up cell voltage was 1.68 volts for the anode coated in accordance with the teaching of Example 1. (This compares with the initial start up cell voltage for an anode of nickel plated steel of 2.21 volts.) The hydrogen peroxide efficiency of the anode having a co-catalytic coating prepared in accordance with the process of Example 1 was 95 percent after 100 days of operation of the cell. (This compares with the hydrogen peroxide efficiency of the nickel plated steel anode which was only 77 percent after 82 days of operation of the electrolytic cell.) The hydrogen peroxide efficiency is the actual amount of hydrogen peroxide produced by the passage of current divided by the theoretical amount of hydrogen peroxide expected to be produced as calculated by Coulombs law. For example, if 1.21 grams of hydrogen peroxide is produced in 40 minutes using a current of 3 amps, then the weight of hydrogen peroxide expected to be produced would be by Coulombs law: Example 4 Example 1 was repeated using a nickel expanded metal to prepare a coated anode. The anode was utilized in an electrolytic cell for the production of an alkaline hydrogen peroxide. The electrolyte fed to the cell was a 4 percent by weight aqueous solution of sodium hydroxide containing 0.5 percent by weight of sodium chloride. The current density was 0.5 amp/in² (0.0775 amp/cm²). The anode did not show any sign of corrosion up to 60 days of cell operation. Example 5 (control-forming no part of this invention) An uncoated nickel anode was used in an electrolytic cell under the condition described in Example 4. Within 2 days of cell operation, the uncoated anode showed signs of corrosion. Example 6 Example 1 was repeated using a nickel plated copper expanded metal to prepare a coated anode. The anode was tested in a water electrolysis cell using a 4 percent by weight aqueous sodium hydroxide solution. The initial anode potential was 0.745 volts (versus saturated calomel electrode). Example 7 (comparative example) An anode was prepared by applying a cobalt-molybdenum coating to a nickel substrated in accordance with the procedure described in European Patent Application 0,009,406 except that the oxide-coated substrate was not cured in a reducing atmosphere at elevated temperature. The coated anode was tested in a water electrolysis cell under the conditions described in Example 2. The initial anode potential (versus a saturated calomel electrode) was 0.65 volts at 0,45 amp/in² (0.07 amp/cm²). This compares to the initial anode (start up) potential of an nickel plated steel anode coated with cobalt and tungsten of 0.56 volts, as described in Example 2. Example 8 (comparative example) An anode was prepared by applying a nickel-molybdenum-cerium coating to a nickel substrate in accordance with the procedure described in U.S. Patent No. 4,342,792 except that the oxide coated substrate was not cured in a reducing atmosphere at elevated temperature. The initial anode potential when tested in a water electrolysis cell was 0.88 volts (versus a saturated calomel electrode). This compares with an initial anode potential of 0.56 volts, as described in Example 2 for an anode having a cobalt tungsten coating on a nickel plated steel substrate.

Claims: A process for the production of hydrogen peroxide in an electrolytic cell for the electrolysis of a mixture comprising an aqueous solution of an alkali metal hydroxide to produce an alkaline hydrogen peroxide aqueous solution, said electrolytic cell comprising an anode, said anode comprising a substrate selected from nickel or a nickel coated electro conductive substrate and an electrocatalyst coating deposited on the substrate, said electro-catalytic coating comprising the oxides of cobalt and tungsten. The process of Claim 1, wherein said substrate comprises a nickel coated steel. The process of Claim 1, wherein said coating has a thickness of from 2 to 200 µm, and the weight ratio of cobalt to tungsten is, respectively, from 1:1 to 5:1. The process of Claim 1, wherein said anode having an electro-catalyst deposited on a substrate selected from nickel or a nickel coated electro conductive substrate is produced by a method comprising the steps of: A) co-depositing on said substrate a homogeneous solution of compounds of cobalt and tungsten, each of which compound, when not an oxide, being capable of thermo-decomposition to the corresponding oxide, and B) thermally decomposing said compounds of cobalt and tungsten, which are present other than in the oxide form, to the corresponding oxide. The process of Claim 4, wherein said homogeneous solution consists of a solvent and metal compounds of cobalt and tungsten in a weight ratio, respectively, of from 1:1 to 5:1. The process of Claim 5, wherein said homogeneous solution consists of the nitrates or chlorides of cobalt and tungsten. The process of Claims 4, 5 or 6, wherein said substrate is nickel, nickel coated stainless steel or a nickel coated metal, wherein said homogeneous solution is co-deposited on said substrate by brushing, roll coating, or by dipping said substrate into said homogeneous solution, and wherein said solvent is selected from at least one of an aqueous solvent, a mixed aqueous and organic solvent, and an organic solvent. The process according to Claim 7, wherein said solvent is a lower alkyl alcohol and said substrate is coated with said metal compounds, other than oxides, and is thereafter heated at an elevated temperature to convert said compounds to the corresponding oxides. The process of Claim 4, wherein successive applications of said homogeneous solution are applied to said substrate followed by successive heating at said elevated temperature to convert said metal compounds to the corresponding oxides. The use for the production of hydrogen peroxide of an electrolytic cell comprising at least an anode and a cathode, a liquid permeable separator, positioned between said anode and said cathode, wherein said cathode is in physical contact with said separator and is porous and self-draining, wherein said anode comprises a substrate selected from nickel or a nickel coated electro conductive substrate and an electrocatalyst coating deposited on the substrate, said electro-catalytic coating comprising the oxides of cobalt and tungsten. The use of Claim 10, wherein said substrate comprises nickel or nickel coated steel, said coating having a thickness of from 2 to 200 µm, and the weight ratio of cobalt and tungsten is, respectively, from 1:1 to 5:1.

Inventors: GOPAL, RAM, MATHUR, INDRESH
Applicants: THE DOW CHEMICAL COMPANY
Application year: 1987
Main classification: C25B11
IPC codes: C25B1, C25B11