Low temperature, plasma method of making plasma deposited coatings

Abstract: A method of depositing a substantially hydrogen free or controlled hydrogen content multi-element alloy film on a substrate. The method utilizes a microwave excited plasma of a hydrogen free precursor gas to deposit a hard, adherent coating. The method comprises providing a substrate to be coated in a vacuum deposition chamber, with a source of microwave energy coupled to the vacuum deposition chamber. A substantially hydrogen free reaction gas precursor composition is introduced into the reaction chamber at a pressure corresponding substantially to a pressure minimum of the modified Paschen curve for the reaction gas precursor composition. Activation of the source of microwave energy excites the reaction gas precursor composition, in this way forming a plasma in the vacuum deposition chamber to deposit a substantially hydrogen free or controlled hydrogen content multi-element alloy film on the substrate.

Description: This invention relates to glow discharge methods of fabricating films or coatings either substantially hydrogen free or of controlled hydrogen content. The films or coatings, substantially hydrogen free or of controlled hydrogen content, which can have the characteristics of ceramics, dielectrics, and semiconductors, find general utility e.g., as hard coatings, and as passivation structures. Thus, in a preferred exemplification, this invention relates to methods of depositing hard coatings exemplified by tool coatings, and optically transmissive hard coatings. A considerable effort has been made to develop processes for rapidly and readily depositing amorphous or substantially amorphous coatings or films, each of which can encompass relatively large areas, if desired, limited only by the size of the deposition equipment. This work was originally concentrated in the field of amorphous silicon compositions. Thin films may be deposited by plasma enhanced chemical vapor deposition. In plasma enhanced chemical vapor deposition, also referred to as glow discharge deposition, a hydrogen containing feed stock gas, such as a hydride or polyhydride, is decomposed in the plasma by electron collisions to form unstable precursor species, i.e., molecular fragments, principally hydrogen containing free radicals. These unstable precursor species, as ions, or free radicals, diffuse to the substrate surface and deposit thereupon as a film through surface reactions involving partial hydrogen elimination. In the prior art processes, the substrate temperature is the greatest single determinant of the hydrogen content of the deposited film. This is because the hydrogen elimination reaction is strongly dependent on the substrate temperature, and is more efficient at high substrate temperatures. In turn, the deposited film's optical, electrical, and mechanical properties are known to be strongly dependent on the hydrogen content and bonding type. For example, amorphous silicon deposited by conventional plasma assisted chemical vapor deposition from silane feedstock onto a cold substrate has a high hydrogen content, many (Si-H₂) n bonds, poor abrasion resistance, poor corrosion resistance, and poor semiconductor properties. Fluorinated feedstock gases have also been used with the glow discharge process to deposit thin films on substrates. Fluorine is a highly reactive element which forms species in the plasma, principally fluorine free radicals, which are capable of etching the substrate and the deposited film and can thus prevent the film from forming unless controlled. When fluorinated feedstock gases are used with hydrides or polyhydrides, hydrogen acts as a carrier to combine with excess fluorine to form, for example, HF and thereafter remove some of the fluorine from the plasma. Provided the proportions are properly chosen, this fluorine removal process causes a reduction in the etching process otherwise produced by the fluorine, which balances the deposition kinetics in favor of film growth to allow the deposition to take place. In the process, however, both hydrogen and fluorine are inevitably incorporated in the film. This may be desirable for attaining certain properties in the film, such as those related to semiconductor action, but the heretofore unavoidable incorporation of hydrogen and fluorine in such films, particularly at low substrate temperatures, results in the production of films which exhibit other properties totally unacceptable for the intended purpose. Because of the uncontrolled incorporation of hydrogen and in some cases fluorine in films formed using the glow discharge process, it has not been possible to use this process to make certain films which can be deposited using other processes, such as sputtering or evaporation. Because such other processes, e.g., sputtering, are not economical for large scale manufacturing purposes, due to fundamental limitations on deposition rate, many known films, while having highly desirable properties such as hardness and transparency, have not enjoyed widespread commercial use. While some hydrogen free films have been deposited by some workers in the field using glow discharge techniques, because of an incomplete understanding of the separate roles played by plasma species, e.g. gasifier, scavenger, etc. exotic plasma conditioning for instance, electron cyclotron resource excited microwave plasmas, or high substrate temperatures were required to achieve the desired film deposition. For example, United States Patent 4,481,229 to Suzuki et al discloses the formation of a hydrogen free Si-N film using a microwave glow discharge process occurring in magnetic field of intensity B such as to result in near electron cyclotron resonance conditions at the frequency of the applied microwave radiation. Practical deposition systems utilizing this art therefore will require tie creation and control of a uniform large magnetic field throughout the plasma volume. Additionally such a system will require the use of microwave tuning and applicator technology capable of coupling microwave energy into a plasma impedance which is changing rapidly near the resource condition. The additional technological complications brought about by these requirements have significant economic consequences for manufacturing machines employing this art. Other examples, including (but not limited to) M. Janai, et al "Chemical Vapor Deposition of Amorphous Silicon Prepared from SiF₂ Gas," J. Appl. Phys . 52 (5), pp 3622-3623; M. Janai, et al "Properties of Fluorinated Glow-Discharge Amorphous Silicon," Phys. Rev. B , 31 (8), pp 5311-5321; M. Janai, et al "Optical Absorption And Photoluminescense of Glow Discharge Amorphous Si:F Films,: Phys Rev. B , 31 (10) pp 6609-6615; K. Kuppers, et al "Deposition of Fluorine Deoped Silicon Layers From A SiCl₄/SiF y /O₂ Gas Mixture By The Plasma CVD Method," J. Electrochem. Soc: Solid State Science and Technology, August, 1978 pp 1298-1302; D.R. Secrist, et al "Glow Discharge Syntheon of A Fluorosiloxane Polymer", Polymer Letters , 4 , pp 537-540. S. Fujita, et al "Electrical Properties of Silicon Nitride Films Plasma Deposited From SiF₄, N₂, and H₂ Source Gases," J. Appl. Phys ., 57(2), pp 426-431; Fujita, et al "Plasma Enhanced Chemical Vapor Deposition of Fluorinated Silicon Nitride," Jap. J. Appl. Phys. 23(3) , pp L144-146, and Fujita, et al "Plasma Deposited Silicon Nitride," Jap. J. Appl. Phys., L268-L280 ., disclose the use of halogenated feedstock gases with or in some cases, without hydrogen to deposit nominally hydrogen free films by plasma glow discharge decomposition. In all cases these researchers utilize elevated substrate temperatures to control hydrogen and halogen content. Many techniques of exciting conventional glow discharge plasmas have been investigated. These have included direct current (DC) and alternating current (AC) techniques. Various AC frequencies have been utilized, such as audio, radio frequency (RF), and a microwave frequency of 2.56 GHz. The present inventors have shown, in U.S. Application Serial No. 605,575, now U.S. Patent 4,504,518 that the optimum deposition power and pressure are defined by the minimum of the Paschen curve. The Paschen curve defined the voltage (V) needed to sustain the glow discharge plasma at each pressure (P) in a range of pressures, between electrodes separated by a distance (D). In a typically configured, conventional RF glow discharge system, the minimum in the Paschen curve occurs at tens of thousands Pa (a few hundred Torr). It has previously been discovered that increasing the applied RF power increases the gas utilization efficiency and the deposition rate. However, simply increasing the RF power to achieve deposition rates approximately greater than 10 x 10⁻¹⁰ m/s (10 Angstroms/sec) leads to the production of hydrogen containing films of decreasing hardness, abrasion resistance, and electronic quality, and can result in films which include polymeric material and/or the production of powder. The increased deposition rate with increased RF power is a result of an increase in the concentration of excited species resulting principally from collisions between electrons and feedstock molecules. However, the collision rate between excited species and more importantly between excited species and feedstock molecules is also increased. This results in the formation of gas phase polymer chains. These chain, are either incorporated in the growing alloy film degrading its physical and/or electronic quality, or condensed in the gas phase to produce powder particles. To reduce the number of undesirable collisions one can reduce the operating pressure, but this moves the deposition process off the minimum of the Paschen curve and substantially higher RF power is required to achieve the same degree of plasma excitation. The physical reason for this phenomenon is that, as pressure is reduced, many electrons that would have been able to collisionally excite feedstock molecules at higher gas pressures now impinge on the substrate or system walls without suffering collisions. The much higher applied RF power required to sustain the plasma at these reduced pressures has the undesirable consequence of raising the substrate self-bias with respect to the plasma, thus producing greatly increased ion bombardment of the deposited film. Attempts have also been made to increase the gas utilization efficiency in RF glow discharge plasmas by high power deposition of a dilute mixture of silane (SiH₄) in an inert carrier gas such as argon. However, this is known to result in undesirable film growth conditions giving rise to columnar morphology as reported by Knights, Journal of Non-Crystalline Solids, Vol. 35 and 36, p. 159 (1980). The one group which has reported glow discharge amorphous silicon-hydrogen seimiconductor alloy deposition utilizing microwave energy at 2.54 GHz treated the microwave energy as just another source of plasma excitation by performing the deposition in a plasma operating at pressures typical of conventional RF or DC glow discharge processes. C. Mailhoit et al in the Journal of Non-Crystalline Solids, Vol. 35 and 36, p. 207-212 (1980) describe films deposited at 22.7 to 40 Pa (0.17 Torr to 0.30 Torr) at deposition rates of between 23 to 34 x 10⁻¹⁰ m/s (23 to 34 Angstroms/sec). They report that their films, which are of poor electrical quality, show clear indication of non-homogeneous structure. Thus, Mailhoit et al failed to find that for a given deposition system the minimum in the Paschen curve shifts to lower pressure values with increasing frequency. Therefore, the use of high frequency microwave energy in a glow discharge deposition system allows one to operate at much lower pressure without production of powder or inclusion of polymeric species in the amorphous semiconductor film. The shift in the minimum of the Paschen curve is believed to occur because, for a given gas pressure at the higher excitation frequency, the rapid reversals of the applied electric field allow the electrons in the plasma to collide with more feedstock molecules in the plasma excitation region before they encounter the walls of the system. Thus, operating at microwave frequencies provides both a substantially increased deposition rate, e.g., 100 x 10⁻¹⁰ m/s (100 Angstroms/sec) or above, and a feedstock conversion efficiency approaching 100%, while still allowing the production of high quality films. This contrasts both with the conventional RF (e.g., 13.56 MHz, 26.7 to 66.7 Pa (0.2 to 0.5 Torr)) glow discharge deposition process which produces high quality films at deposition rates of approximately 10 x 10⁻¹⁰ m/s (10 Angstroms/sec) and feedstock utilization of approximately 10% and with the Mailhoit microwave process (2.54 GHz, 26.7 to 40 Pa (0.2 Torr to 0.3 Torr)) which produced poor quality films at 20 to 30 x10⁻¹⁰m/s (Angstroms/sec) deposition rates. Low pressure deposition, which is achieved with microwave plasmas without substantial increases in power, allows for powderless depositions of a film with only small amounts of incorporated polymeric material. Still further, the higher frequency, and thus the more effective excitation results in the formation of reactive species not previously obtainable in sufficiently large concentrations with prior art processes. As a result new amorphous semiconductor compositions can be produced having substantially different material properties than previously obtainable. All of the above results, by virtue of operation at microwave frequencies, and operation at lower pressures provide compositions improved characteristics made at substantially increased rates. In addition, in order to operate in the most economic manner, it is further necessary to operate in the vicinity of the minimum of the Paschen curve. As disclosed in U.S. Pat. No. 4,217,374, new and improved amorphous and substantially amorphous semiconductor compositions and devices can be made which are stable and composed of chemical configurations which are determined by basic bonding considerations. One of these considerations is that the material is as tetrahedrally bonded as possible to permit minimal distortion of the material without long-range order. Fluorine, for example, when incorporated into these materials performs the function of promoting tetrahedral bonding configurations. Amorphous semiconductor materials having such tetrahedral structures exhibit low densities of dangling bonds making the materials suitable for electronic and photovoltaic applications. However, plasma deposited amorphous silic silicon-hydrogen compositions, as well as amorphous compositions of silicon and hydrogen with one or more of carbon, oxygen, and nitrogen suffer from various shortcomings.The hydrogen content of compositions deposited from hydride feed stocks is strongly dependent on substrate temperature, the content thereof decreasing at high substrate temperatures, and increasing at low substrate temperatures. For example, the presence of hydrogen in the composition deleteriously effects the attainment of certain desirable properties of SiO₂, Si₃N₄, SiC compositions or the like, such as corrosion resistance, hardness, etc. This is a direct consequence of hydrogen's role as a chemical bond terminator. As such, excess hydrogen disrupts the connectivity of the chemical bond network of the deposited film, reducing its average atomic coordination number. The hydrogen rich compositions have lower hardness, lower abrasion resistance, and lower corrosion resistance than stoichiometric materials. Moreover, the use of pyrophoric hydride gases, as SiH₄, introduces hazards into the work place which necessitate the introduction of extra manufacturing costs e.g., for worker safety aid protection systems, insurance and the like. These costs, while they may be already a part of the manufacturing costs of, for example, crystal line silicon semiconductor devices represent new costs for manufacturers who will use plasma deposited coatings in activities such as manufacturing and stamping data storage discs, manufacturing plastic headlight and tail light lenses, and manufacturing opthalmic lenses. The presence of large amounts of hydrogen in the deposited composition reduces the hardness of the deposited compositions, limiting their utility as protective coatings. Moreover, heating the substrate during deposition, e.g. to drive off hydrogen can damage temperature sensitive substrates, as plastic substrates and substrates bearing electronic circuit elements and devices. In the case of plastics, the inability to provide an adherent, abrasion resistant, substantially transparent coating impervious to moisture and oxygen on the plastic substrate without damaging or otherwise degrading the plastic substrate has limited the full potential of the transparent plastics and other soft substrates. Plastics find many applications requiring the transmission, of optical energy. These applications include, for example, opthalmic and optical elements, windows and glazing units, and protective overlays, for example, protective overlays on optical data storage media and photovoltaically operatively activated devices. Plastic overlays are used to protect optical data storage media. Information may be stored in the form of optically detectable differences in the properties of a medium, such as metal, an alloy, a phase change alloy, an organic or inorganic polymer, or an organic or inorganic dye. These media are particularly susceptible to environmental degradation, for example the effects of oxygen and moisture in the air. Heretofore these media have been protected by an organic polymeric overlay, as a poly (acrylate) overlay, e.g., poly (methyl methacrylate), or a poly (carbonate) overlay, as a bisphenol-A based heterochain polymeric overlay or an allyl carbonate heterochain polymeric overlay. However these optically transmissive polymers are water and air permeable and susceptible to surface degradation, as abrasion, scratching, and erosion. Even the slightest transport of air or water vapor across the barrier can force catastrophic failure of the information storage media. The surface degradation can cause skips, and incorrect data reading. Plastic is also used as the refractive element in lenses, for example opthalmic lenses, photographic lenses, and telescope lenses. Especially preferred are polycarbonate and polyallyl carbonate polymers for opthalmic, sun glass, and safety goggle applications, and polymethyl methacrylate polymers for camera lenses, binocular lenses, telescope lenses, microscope objectives and the like. Plastic lenses have found good market acceptance and market penetration. However, the full potential of plastic lenses has been limited by their low resistance to abrasion, hazing, and scratching. Prior art abrasion resistant coatings, exemplified by polysilicate coatings and polysiloxane coatings, have not eliminated the problem of poor adhesion and poor abrasion resistance. Plastic sheets with scratch and abrasion resistant coatings have found market acceptance in various automotive applications. These include headlight panels, parking light lenses, tail light lenses, sunroofs, side windows, and rear windows. However, the fuller utilization of plastic sheet material has been limited by the susceptibility of the plastic to scratching and abrasion, and the poor adhesion, and mismatch of thermal expansion coefficients between the plastic and the prior art protective coating. Large area plastic sheets have also found utility in applications such as doors, windows, walls, air craft windows, air craft canopies, vandalism and break-in resistant panels, windows and doors, and esthetic barriers. However, the poor abrasion resistance of these large sheets have served to limit the full range of their market penetration capabilities. Plastic materials have also been utilized to provide a shatter resistant layer for large sheets of glass. The glass-plastic structure is exemplified by bi-layer Windshields. Bi-layer windshields have a single sheet of glass on the weather incident side of the windshield, and a polymeric film, for example a polyurethane film, adherent to the glass on the interior side. These bi-layer windshields have not found market acceptance because of the very poor resistance to scratching and abrasion of the internal, polyurethane coating thereof. Other materials which require a hard coating are semiconductors, e.g., photosensitive semiconductors. Exposed layers of semiconductor alloy films, utilized in, for example, imagers, photovoltaic cells, electronic devices, and electrophotographic drums, are subject to abrasion, scratching, and hazing. Photovoltaic cells are subject to these insults during manufacturing and service, while imagers and electrophotographic drums are subject to the scratching, scraping, and abrading effects of rough sliding documents. In the case of electrophotographic drums, these effects are exacerbated by submicron, particulate toners. The invention described herein allows for the independent control or even the elimination of hydrogen from the film while permitting deposition at an independently chosen substrate temperature. The thin films have controlled hydrogen content. By controlled hydrogen content is meant that the hydrogen content of the films is decoupled from the substrate temperature and can therefore be controlled independently of the substrate temperature. This allows achievement of a desired level of hydrogen content in the film to optimize parameters dependent on hydrogen e.g., elastic and plastic properties, and tensile, compressive, shear, and thermal expansion properties, or to eliminate hydrogen altogether where the desired properties are adversely affected by hydrogen. Decoupling of hydrogen content from substrate temperatures allows hard, corrosion resistance, abrasion resistant, and/or dielectric films to be deposited on temperature sensitive and/or thermally degradable substrates without damage thereto. The present invention provides a process for the control or elimination of hydrogen from the deposit without any necessity of establishing or maintaining electron cyclotron resonance or near electron cyclotron resonance in the vicinity of the plasma. Thus, the deposition plasma is formed in a volume in which the magnetic fields present, if any, need not and cannot create an electron cyclotron resonance condition or a condition approaching an electron cyclotron resonance condition. Extraneous magnetic fields, as terrestial magnetism and magnetic fields of nearby apparatus can be tolerated, and are not coupled to the plasma. The present invention provides a process for depositing adherent, hard, hydrogen free or controlled hydrogen content, amorphous films where the fluorine content is determined by the stoichiometry of the films, at substantially lower substrate temperatures, higher deposition rates, and lower hydrogen and fluorine contents than possible in the prior art. Even though deposition occurs at higher deposition rates and lower substrate temperatures, the compositions exhibit high-quality properties suitable for many applications especially including hard coatings. According to the present invention, there is provided a method of depositing a multiple element composition onto a substrate, the method comprising the steps of: establishing a vacuum deposition region and positioning a substrate therein; providing a plurality of feedstock gases, at least one of the feedstock gases containing an element or elements which are components of the multiple element composition in chemically bonded form with a reactive gasifier element and at least another one of the feedstock gases containing at least one scavenger element capable of preferentially bonding with and scavenging the reactive gasifier element, the feedstock gases being free of combined hydrogen except to the extent that it is optionally added to controllably add hydrogen to the composition; providing a source of plasma excitation energy; exciting the source of plasma excitation energy to excite the feedstock gases to form a plasma therein of excited precursor species, wherein the preferentially bonding scavenger element bonds with the reactive gasifier element to form a chemical compound that is carried off as an effluent in the process at rates sufficient to remove reactive gasifier elements from the plasma thereby to provide net film deposition; and, positioning at least a portion of the plasma of excited precursor species adjacent a surface of the substrate to form thereon from the excited precursor species a film of controlled hydrogen content which includes elements derived from the precursor species; characterised by: establishing a pressure of about 13.3 Pa (0.1 Torr) or less within the deposition region during deposition; and in that: the feedstock gases are excited in a volume in which magnetic fields, if present, do not create an electron cyclotron resonance condition, the substrate being at a temperature below 380°C during deposition. By a feed free of combined hydrogen is meant a feed stock that is: (1) free of hydrides, M x H y where M is a metal or semi-metal other then hydrogen, (2) free of compounds of the type H y X x where X is a semi-metal, and (3) free of hydrocarbons, hydrosilanes, and hydrogermanes, except to the extent that such compounds and H₂ may be added to the feed stock to controllably add hydrogen to the composition. A source of energy is activated and coupled to the feedstock gas to form a plasma. A portion of the plasma is positioned in proximity to the substrate onto which the low hydrogen alloy film is to be deposited. The vessel is maintained at a low enough deposition pressure to deposit the film at high deposition rates, and high gas conversion efficiencies without any significant powder or polymeric inclusions and the substrate need not be heated. The plasma excitation energy and the feedstock gases form a glow discharge plasma within the vessel to deposit an amorphous film onto the substrate. In a preferred exemplification the film is an alloy of silicon and/or germanium with nitrogen, carbon, oxygen, and/or boron. The feedstock gases can include silicon tetrafluoride (SiF₄), disilane hexafluoride (Si₂F₆), and higher homologues, germane tetrafluoride (GeF₄), and digermane tetrafluorine (Ge₂F₆), with NO₂, N₂, N₂O, cyanogen, halogenated hydrocarbons, or the like. The method of the invention can be used to deposit boron containing films, including boron nitride or boron carbide films from, e.g., a BF₃ and nitrogen containing feed stock gas in a glow discharge plasma. The present invention can provide hydrogen free, or controlled hydrogen content hard, substantially transparent coated plastic articles where the coatings are hard, abrasion resistant, transparent coatings, and have high transparency and low absorption across a relevant portion of the visible or infrared spectrum. In a particularly preferred exemplification a fluorinated feedstock gas, as a perfluorosilane, a perfluorogermane, or BF₃, is reacted in a plasma with a molecular compound of (1) an element or elements that preferentially scavenge fluorine, as nitrogen, to prevent fluorine etch removal of the deposit, and (2) an element that reacts with the metal or semi-metal of the perfluoro compound to form the multielement deposit. Exemplary reaction pairs, and products include, among others: (1) SiF₄, Si₂F₆ + N₂, N₂O, NO₂ → Si₃N₄ + NF₃ (2) SiF₄, Si₂F₆ + NO₂ → SiO₂ + NF₃ (3) SiF₄, Si₂F₆ + (CN)₂ → SiC, Si₃N₄ + NF₃ (4) BF₃ + N₂ → BN + NF₃ (5) BF₃ + (CN)₂ → B₄C, BN + NF₃ (6) SiF₄, Si₂F₆ + BF₃ + NO₂ → Borosilicate + NF₃ (7) SiF₄, Si₂F₆ + PF₃ + NO₂ → Phosphosilicate + NF₃ While these reaction gas feedstocks and products are shown with stoichiometric coefficients, it is to be noted that thin film deposits formed by condensation and reaction of plasma species may be substantially non-stoichiometric. The method of the invention breaks (1) the necessity for hydrogen in the feedstock gas, and (2) the dependence of the hardness on high substrate temperatures heretofore required to drive off hydrogen, and provides a rapid, high deposition rate, high through-put process throughput for depositing hard coatings at low substrate temperatures. Optically transparent, hard, protective coatings, for example, which are prepared utilizing the method of the invention are characterized by hardness, adhesion to the substrate, and optical smoothness, i.e., freedom from scattering. By abrasion resistance is meant that the protective coatings have either or both of: (1) less than a 10 percentage point increase in haze by the method of either ASTM Standard D-4060-84, Abrasion Resistance of Organic Coatings by the Taber Abrader, or ASTM Standard D-1003-61 (1977), Haze and Luminous Transmittance of Transparent Plastics, or (2) less than 10 percent haze after 600 strokes by the method of ASTM Standard F-735-81, Abrasion Resistance of Transparent Plastics and Coatings Using the Oscillating Sand Method. Absorption and optical transparency are functions of optical absorption and reflectance at the coating-substrate interface. By optical transparency is meant chat the optical absorption measured through a 3 x 10⁻⁶m thick film is less than 10 percent across a selected portion of the visible or infrared spectrum. The present invention further provides a new and improved process for depositing optically transmissive hard coatings on substrates. The inventive process herein provides substantially increased deposition rates and reaction gas feed stock utilization. The films, coatings, and layers may be optically transmissive, and may be of compositionally and structurally controlled optical band gap. All of the above results are obtained by virtue of the composition having improved optical and mechanical characteristics while being deposited at substantially increased rates, and feedstock gas utilizations. The coated articles prepared thereby are characterized by surface toughness, high optical transmission through the deposited layer, and low reflectivity at the layer-substrate interface. The method of the invention allows deposition to be carried out with the substrate below the temperatures at which organic polymeric substrate degrade, e.g., decompose, melt, soften, and/or undergo phase transformations, typically 170°C, as well as below the temperatures at which thermal diffusion effects interfere with the operation of solid state junction devices, e.g., 380°C or lower, and even as low as 300°C, as well as at standard temperature (20-27°C). In this way thermal degradation of the underlying microelectronic circuit element substrates, data storage materials, or thermally degradable, e.g., plastic, substrates is avoided. The low temperature nature of the invention is especially useful in depositing hard alloys on substrates that are sensitive to thermal damage decomposition, or degradation. These substrates include organic polymeric substrates, as used in lenses, transparent articles, and optically transmissive coatings. Organic polymers of commercial interest have glass transition temperatures of from as high as about 170°C or higher, in the case of bisphenol-A polycarbonates, polyacrylamides and poly (N-vinyl pyrrolidones) to as low as 75 to 105°C in the case of such commercially important organic polymers as poly acrylic acids, polystyrenes, polyacrylonitrides, polyvinyl chlorides, polymethyl methacrylates, diethylene glycol bis (allyl carbonates), and terephthalic acid polycarbonate The herein contemplated hard coatings may be deposited on these organic polymeric substrates while maintaining the substrate temperature below 170°C, preferably below 75°C, and in a particularly preferred exemplification at room temperature, so as to avoid thermal degradation of the substrate. The low temperature deposition process of the invention may also be utilized to deposit hard, optically transmissive, barrier layers atop data storage media, e.g., chalcogenide data storage media, magneto-optic data storage media, ablated data storage media, color change data storage media and the like. In this way damage to thermally sensitive data storage media is avoided. According to a still further exemplification of the invention, electronic features may be deposited e.g., as passivation layers, atop underlying electronic features of controlled dopant content without causing deleterious thermal effects on the dopant content or distribution, or to the function performed by the circuit element. In the drawings:- Figure 1 is a perspective view, partly broken away, of a microwave plasma deposition system for depositing films in accordance with the process of the invention; Figure 2 is a modified Paschen curve for conventional RF deposition conditions; Figure 3 is a modified Paschen curve for the microwave deposition conditions of the present invention; Figure 4 is a cutaway view, not to scale, of an optical data storage device having the hard coating overlay of the invention; Figure 5 is a partial isometric view, not to scale, of a coated plastic lens; Figure 6 is a partial isometric view of a bi-layer windshield having the hard coating on the exposed surface of the plastic; Figure 7 is a partial cutaway view of a plastic window having a hard coating on both external surfaces; Figure 8 is a partial cutaway view of a plastic headlight lens having a hard coating thereon; Figure 9 is a partial cutaway view of a photovoltaic cell having a hard, transparent coating of the invention; and, Figure 10 is a partial cutaway view through cutting plane 10-10 of the windshield of Figure 6 showing the glass substrate, the polyvinyl alcohol adhesive, the polyurethane bi-layer, and the hard coating. The present invention provides a process for depositing adherent, hard films, hydrogen free or of controlled hydrogen content, by plasma deposition. The plasma may be a d.c. plasma, a radio frequency plasma (e.g., a 13.56 mHz plasma), or a microwave plasma (e.g., a plasma excited by a frequency in the Gigahertz range, and exemplified by a 2.45 GHz excited plasma). The feed stock gas mixture contains at least 1. A first multielement gaseous compound of: a. a film constituent species; and b. an element that forms a compound with the film constituent species enabling the compound to be a gas at plasma decomposition temperatures and pressures, i.e., a reactive, gasifier element; and 2. A second gas, which may be either: a. a single element gas which acts as a scavenger for the reactive gasifier of 1-b, above, and which may, optionally, be incorporated into the film; or b. a multi-element gaseous compound, one element of which is incorporated into the film, and the other element of which acts as a scavenger for the reactive, gasifier element, and which may also be incorporated into the film. The feed stock gas mixture may also contain a plasma sustaining gas, as helium and/or argon, as well as controlled amounts of hydrogen (H₂) to provide a controlled hydrogen content in the deposit. The reactive gasifier element is a ligand that enables the film constituent species - reactive gasifier compound to be a gaseous compound at plasma decomposition and/or deposition conditions. As such the reactive gasifier must covalently bond with the film constituent species, in a way which will not form a network e.g., as a metallic, polymeric, or crystalline network, or an ionic bond. For light elements (C, Si, B and P) as well as elements in Group IIIB (B,Al), Group IVB (C, Si, and Ge), and Group VS (P,As) fluorine is a reactive, gasifier element providing gaseous compounds with full coordination spheres and the fluorides of these elements are preferred, as CF₄, C₂F₆, SiF₄, Si₂F₆, BF₃, PF₃, Alf₃, GeF₄, Ge₂F₆, and AsF₃. Especially preferred are the perfluorosilanes, SiF₄, Si₂F₆, and Si₃F₈. For certain metallic elements, as the metals of Groups IVA (Ti, Zr, and Hf), the reactive gasifier may be Cl, as in TiCl₄, ZrCl₄, and HfCl₄. For the metals of Group VA (V, Nb,Ta) and Group VIA (Cl,Mo, and W) the reactive gasifier may be either F or Cl, as WF₆, MoF5, NbF5, or TaF5. For the iron triad (Fe,Co,Ni) and the lighter platinum group metals (Ru,Rh,Pd), carbonyls provide gaseous compounds. The second gas, which scavenges the excess reactive gasifier, e.g., the fluorine, may be nitrogen, or a nitrogen compound, as N₂O, NO, NO₂, N₂O₅, or (CN)₂. The scavenger element bonds with the reactive gasifier to form a chemical compound that is carried off at rates sufficient to remove reactive gasifier from the vicinity fo the substrate. This prevents etching of the deposit, and provides net film deposition. The composition of the film, and especially the amount of incorporated reactive gasifier incorporated therein, is controlled by controlling the amount, i.e., the presence or absence of a stoichiometric excess, of the scavenger gas. Referring now more particularly to Figure 1, a microwave deposition apparatus suitable for practising the process of the present invention, is generally designated 10. The apparatus 10 comprises a tubular chamber or vessel 12 containing a substrate 14 upon which the amorphous semiconductor alloy films are to be deposited. The substrate may, but need not be, heated by a radiant heater 16. The exterior of the chamber is irradiated by an energy source 17 to the plasma. Reaction gases passing from inlets 46 to an outlet 20 at opposite ends of the chamber 12 receive plasma igniting and maintaining energy, e.g., microwave energy, from the source 17 in the area of the substrate. The combination of the reaction gases and the energy from the source 17 causes the formation of the plasma and the deposit of the film 22 in the area of the substrate. In accordance with the present invention, the feedstock gases are substantially free of hydrogen compounds where hydrogen is bonded to another element, and include at least one multielement compound of an element to be deposited. Preferably the feedstock gas includes at least two components, one component being a halide of an element to be deposited, e.g., a fluoride or a chloride, and the other component including one or more elements, at least one element particularly adapted for scavenging the halogen, and at least one element forming the deposit, the two components being substantially free of hydrogen. The temperature of the substrate can be between room temperature and about 380°C and the frequency of the microwave energy can be 2.45 Gigahertz and preferably above 2.45 Gigahertz. As mentioned, the combined plasma igniting and maintaining energy and the reaction gases form the plasma to permit the deposition process to proceed. During the process, the film 22 is spared from the potentially damaging effects of ion bombardment because of the reduced substrate self bias. Referring now to Figure 1 in greater detail, the tubular chamber 12 comprises a central quartz portion 24 and end portions 26 at opposite ends thereof. The end portions 26 are closed by a pair of end fittings 30 and 32 to complete the chamber. Each of the end fittings includes a sleeve portion 34 extending from a closed end 36 to an open end portion. The open end portion is threaded to receive a collar 40 having an inwardly extending annular flange 42 at one end thereof. An o-ring (not shown) is confined in a space between the flange 42 and the end portion for compression thereof against the quartz portion 26. An air-tight seal is provided in this way between the end fittings 30 and 32 and the tubular chamber 12. The end fittings 30 and 32 are preferably made of stainless steel or other suitable non-corrosive metal, with the closed ends 36 being welded or otherwise permanently joined to the sleeve portions 34. The closed end 36 of the end fitting 32 is provided with gas inlets 46 through which the deposition gases are introduced into the vessel 12. An inert gas such as argon can be introduced through one inlet 46 to assist in sustaining the plasma. The gas inlets 46 are preferably connected to a conventional gas rack (not shown) for establishing regulated flows of feedstock gases therein. The outlet 20 is provided at the closed end 36 to the end fitting 30 for connection to selectable first and second pumps. The first pump provides for initial evacuation of the chamber. The second pump provides withdrawal of unused reaction gases during operation and maintenance of the proper deposition pressure of about 13.3Pa (0.1 Torr) or lower, e.g. 0.53 to 1.33 Pa (0.004 to 0.01 Torr). The energy source, e.g., a microwave energy source 17, preferably comprises a microwave energy generator 18 coupled to an antenna (not shown). The antenna is housed within a reflective housing 21 for concentration of the microwave energy into the chamber 12. The antenna is a vertical antenna being preferably one-quarter wavelength long. The tip of the antenna just touches the outer surface of the vessel 12 to maximize transmission of its output to the reaction gases. Microwave excitation of a multicomponent, multielement feedstock gas, e.g, a feedstock gas of a perfluorosilane component and N₂ or a nitrogen compound component, forms a plasma that yields a hard, adherent deposit on a substrate 14 at temperatures as low as standard temperature (20-27 °C). Thus, it is unnecessary to heat the substrate. However, the substrate may be heated if necessary, e.g., to control the morphology of the deposit. Heating may be done by radiant heater 16. The radiant heater 16 preferably comprises a conventional resistive heater. Heat is transmitted to the substrate 14 and the chamber 12 by radiation, without significant direct heating of the reaction gases. Alternatively, a resistive heating arrangement (not shown) may be provided within the chamber 12 for heating the substrate 14. In that case, power lines for the heating element would be passed through the closed end 36 of one of the end fittings. According to a still further exemplification, cooling can be supplied to the substrate 14 or substrate carrier to prevent thermal degradation of the substrate. In operation, the system 10 is first pumped down to below a desired deposition pressure such as 1.33 x 10⁻³Pa (10⁻⁵ Torr). The feedstock gases, i.e., a hydrogen free, multielement, multiatomic halide compound of the metal or semi-metal to be deposited, and a hydrogen free multiatomic molecular compound of the non-metal to be co-deposited therewith, and of the element to scavenge the halogen, are fed into the chamber 24. Exemplary are silicon tetrafluoride i.e., silane tetrafluoride, (SiF₄), disilane hexafluoride (Si₂F₆), and higher homologues thereof; germane tetrafluoride, digermane hexafluoride, and higher homologues; boron trifluoride, BF₃ and phosphorous trifluoride, PF₃, with the N₂, NH₃, NO₂, cyanogen [(CN)₂], optimally with O₂, and/or a fluorocarbon. The feedstock gases are fed into the inlet chamber 24 through inlet conduits, as separate inlet conduits 46, and chamber 12 is brought up to the desired operating pressure of, for example, about an order of magnitude below that of a comparable r.f., e.g., up to about 6.67 Pa (0.05 Torr). The precursor feed stock gas is a hydrogen free gas. That is, it is free of combined hydrogen, silanes, partially halogenated silanes, hydrocarbons, and partially substituted hydrocarbons, and contains only enough molecular hydrogen, H₂ as may be necessary to control or modify the deposit properties. It is noted that the presence or degree of presence of H₂ is optional and controllable. In this way the total molecular and combined hydrogen content is maintained below the level at which the hydrogen's role as a chemical bond terminator disrupts the connectivity of the chemical bond network of the deposited film, reduces the average atomic coordination number in the deposit, thereby interferes with and harms the deposit. This maximum acceptable hydrogen level is determined by the end use of the coated article, and not by the kinetics, thermodynamics, and reaction path of the deposition process, as has heretofore been the case. When the plasma is maintained by microwave energy, the microwave energy from the antenna 19 is directed by the reflective housing 21 into the vessel 12 to form a plasma in the area of the substrate. As a result, a film 22, such as a substantially optically transmissive, hard protective film 22, is deposited onto the substrate 14. The heater 16, when present, may maintain the substrate 14 at a temperature between about 20° C and a temperature below the onset of thermal degradation thereof. However, the use of a microwave excited perfluorosilane allows the substrate 14 to be at ambient temperature, obviating the necessity of a substrate heater. The output power of the microwave energy generator 18 is adjusted between about 20 and 120 watts depending on the volume of the gas contained in the plasma and the composition of the gas. These power outputs preferably correlate to about 0.1 to 1 watt per cubic centimeter in power density. The flow rate of the reaction gases can be between 1 to 50 SCCM. With the foregoing system parameters, deposition rates of 25 to 250 x 10⁻¹⁰m/s (25 to 250 Angstroms/sec) can he obtained. If it is desired to increase the band gap of the material, band gap increasing elements such as carbon or nitrogen can be incorporated into the films by introducing a halocarbon, nitrogen oxide, nitrogen halide, or other non-hydrogen containing gas into the vessel during deposition. The reaction gases can be sequentially introduced to result in the formation of any desired layer morphology, composition, or mechanical properties. To assist in the maintenance of the plasma, a plasma sustaining gas can be introduced into one of the inlets 46. Argon gas can be utilized for this purpose. While the method of the invention may be carried out with DC excited plasmas, and with AC excited plasmas, e.g. , in the RF domain, the maximum benefits of the invention are obtained with a microwave maintained plasma. The deposition of substantially hydrogen free, hard films by the foregoing process utilizing a microwave initiated and maintained plasma has demonstrated many advantages over prior deposition processes. Firstly, the microwave energy provides a higher density of free radicals than previously possible. This results in higher deposition rates, nearly total utilization of the feed stock reaction gases. Secondly, the higher plasma electron temperature results in formation in the plasma of reactive species otherwise not obtainable and therefore one can deposit films containing unusual elements or combinations of elements or deposit films from unusual gas mixtures. This can result in new materials having unique compositional and structural properties. By the term "amorphous" is a composition or material which has long range disorder, although it may have short or intermediate order or even contain at times some crystalline inclusions. Pursuant to this definition, it should be noted that microcrystalline semiconductor material will fall into the generic category of amorphous films. Figures 2 and 3 are side-by-side comparisons of the modified Paschen curve for SiH₄. The curves are shown for SiH₄ rather then for SiF₄, because of the greater availability of data for SiH₄, enabling SiH₄ to be a standardized basis of comparison. FIGURE 2 illustrates a curve 260 which is produced utilizing conventional RF deposition techniques of SiH₄, which is a modified Paschen curve. The Paschen curve shows the voltage needed to sustain a plasma as a function of pressure. The modified curve is related to the power needed to sustain a plasma as a function of pressure. The normal operating range is dictated by the minimum of the curve, which for the curve shown is about 26.7 to 33.3Pa (0.2 to 0.25 Torr). FIGURE 3 illustrates a modified Paschen curve 262 for the microwave deposition process of the invention again utilizing SiH₄ as the reaction gas. The curve 262 shows the clear shift in the curve to lower pressure for the microwave deposition process of the invention, which results in an operating range of about 10 to 13.3 Pa (0.075 to 0.1 Torr) or below for the invention. The curve shifts for other reaction gases and deposition system dimensions. Where a transparent coating, film, or layer is deposited, the hard, optically transparent, protective layer is characterized by an optical absorption through a 3 x 10⁻⁶m film of less than ten percent at a relevant bandwidth. The relevant bandwidth may be the visible spectrum (600 nanometers to 400 nanometers) or the infrared spectrum (longer than 600 nanometers and even longer than 700 nanometers). This requires an optical bandgap of greater than 3.5 electron volts for transmission in the visible spectrum, and greater than 2.5 electron volts for transmission in the infrared spectrum. Exemplary, transparent, low cost, hard, abrasion resistant materials include the silicon compounds, especially the silicon carbides, SiCx with x from 0 to 2.0, the silicon nitrides SiN y where y is from 0 to 4/3, the silicon oxides, SiO z , where z is from 0 to 2, and related compositions as SiC x O z , SiC x N y , SiN y O z , and SiC x N y O z , where x, y, and z are as defined above, and the sum of x/2 plus 3y/4 plus z/2 approaches 1.00. The above described coatings may be deposited directly on the substrate. Alternatively, an inner layer or underlayer may be deposited directly on the substrate, with the above described hard coating deposited atop the inner layer or underlayer. The inner layer or underlayer may serve as a stress relieving layer, allowing bending of the laminate and reducing the tendency for stress cracking in the dielectric layer. This allows a thicker layer to be deposited. This also allows a flat substrate as a thermoplastic film or sheet to be coated with the inner layer and the external hard layer and thereafter shaped or formed, i.e., bent, molded, extruded, drawn, oriented, or otherwise thermoformed, without cracking, crazing, hazing, or delumination. The coating may be deposited on a large flexible plastic substrate at one site or factory in one apparatus by one manufacturing enterprise, and the coated plastic substrate shaped or formed in another apparatus, or at a different site or factory, and even by a different manufacturing enterprise. The underlayer or inner layer may also act as an optical filter, being of controlled band gap, so as to selectively block portions of the spectrum, as ultraviolet and/or blue light. The inner layer, when present, should be formed of a material that is compatible with the substrate in one or more of coefficient of thermal expansion, modulus of elasticity, plasticity, or lattice dimensions. In one embodiment the inner layer is deposited carbon. The deposited carbon may be amorphous, microcrystalline, or polycrystalline, and may exhibit tetrahedral short range order and/or graphitic short range order. The carbon may be deposited by sputtering a carbon target, chemical vapor deposition, glow discharge from a halocarbon feedstock gas, or microwave deposition from a halocarbon feedstock gas. Especially preferred is microwave deposition from a halocarbon feedstock gas followed by microwave deposition of silicon composition coating from a fluorosilane-nitrogen containing feedstock gas without breaking vacuum. According to a particularly preferred exemplification, the inner layer of the dielectric is formed of a composition hydrogen and the same constituents as the outer portion of dielectric. The hydrogen content of the inner layer of the dielectric is controlled by introducing a separate hydrogen containing feedstock gas, as a hydride, e.g., silane or germane, or molecular hydrogen. As the deposition rate and substrate temperature are controlled independently of the hydrogen feed rate, it is possible to incorporate hydrogen at a concentration that will relieve stresses within the dielectric layer, thereby reducing hazing, crazing, and delamination. Typically the inner layer, whether a carbonaceous under layer or hydrogen alloy inner layer, may be of uniform composition and properties or of graded composition and properties. The inner layer, when present, has a thickness of from about 0.05 x 10⁻⁶m (500 Angstroms) to about 2 x 10⁻⁶m with a thickness of about 0.1 x 10⁻⁶m to 1.5 x10⁻⁶m being particularly preferred for stress relieving SiO₂ alloys on polycarbonates and polymers of like mechanical and thermal properties. According to a further exemplification there may be multiple inner layers or under layers. For example the coating may contain a gas-impervious intermediate layer, as a Si₃N₄ layer, to hermetically seal an environmentally degradable substrate, as polycarbonate, or polyurethane, from oxygen and/or water vapor, an outer layer of, e.g. SiO₂, for hardness, and an adhesion layer or layers, e.g., of C or SiO₂, or both C and SiO₂ for adhesion, bonding, and mechanical parameter matching. According to this exemplification a polycarbonate or polyurethane substrate may have a hard coating and be protected from moisture and/or O₂ by a multilayer coating of (1) SiO₂, e.g., as an adhesion layer, (2) Si₃N₄, e.g., as a hermetic seal layer, and (3) SiO₂, e.g. as a hard outer layer. The SiO₂ layers have a thickness of about 1 to 2.5 x10⁻⁶m and the Si₃N₄ layer has a thickness sufficient to substantially prevent the permeation of gas, as O₂ or H₂O, therethrough, e.q., about 0.5x10⁻⁶m to 2 x 10⁻⁶m thick. Alternatively, a carbon film may be deposited on the substrate, and the layers of SiO₂ and Si₃N₄ deposited sequentially, e.g., as described above, atop the carbon layer. When stoichiometric is referred to above, it is to be understood that such stoichiometries are approximate, that actual composition may deviate therefrom,and that -F may be incorporated therein. According to a still further exemplification, a multi layer coating may be deposited having an inorganic photochromic or electrochromic composition, as a hexa-coordinated tungsten composition, encapsulated between hermetically sealing layers of silicon nitride, with an external layer of silicon oxide. The photochromic may be deposited by low temperature CVD, from organic solution or by condensation from an organic vapor, as is well known in the art. This multilayer coating may be deposited atop, e.g., a poly(acrylic), poly(carbonate), or poly(allyl glycol carbonate) homopolymer, copolymer, or interpolymer substrate, optionally with a carbonaceous and/or silicon oxide containing bottom layer, a first silicon nitride encapsulating layer, the photochromic or electrochromic layer, a second silicon nitride encapsulating layer, and an external layer of silicon dioxide. Alternatively, the first silicon oxide layer may be dispensed with and the photochromic or electrochromic layer deposited onto the silicon oxide and/or carbon containing under layer, or even directly onto the organic polymeric substrate. Microwave plasma deposited protective, optically transmitting layers meeting these criteria find utility in combination with optically transmissive organic polymeric substrates. Exemplary organic polymers which may be used to provide the organic polymeric substrates include carbon chain polymers such as the polyolefins, styrene and divinyl benzene based polymers, dienes, vinyls, acrylics, and fluorocarbons. Exemplary polyolefins include polyethylene, polyethylene-polyvinyl acetate copolymers, polyethylene-polyethyl acrylate copolymers, polyethylene-polyacrylic acid copolymers, polypropylene - polymethacrylic acid copolymers, polypropylene, polyethylene-polypropylene copolymers, polyethylene-polypropylene-polydiene terpolymers, chlorinated polyethylene, chlorosulfonated polyethylene, polyisobutylene-polyisoprene copolymers, and poly 4-methyl pentene-l. Exemplary aromatic carbon chain polymers include polystyrene, polystyrene-acrylonitrile copolymers, polystyrene-polybutadiene copolymers, polystyrene-divinylbenzene copolymers and terpolymers and polystyrene-polyester copolymers. Exemplary diene polymers include polybutadiene, polybutadiene-polyacrylonitrile copolymers, polyisoprene, polychloroprene, polyisoprene-polystyrene copolymers, arid polyisoprene-polymethyl methacrylate copolymers. Exemplary vinyl polymers include polyvinyl chloride, polyvinylidene chloride, polyvinyl chloride - polyvinylidene chloride copolymers, polyvinyl chloride-polyvinylidene chloride, polyvinyl chloride-polyethylene, polyvinyl acetate, polyvinyl chloride - polyvinyl acetate, hydrolyzed polyvinyl acetate, also known as polyvinyl alcohol, poly N-vinyl pyrrolidone, poly 2-vinyl pyridene, poly vinyl-methyl ether, poly vinyl formal, poly vinyl butyral, and poly acrylic acid-polyethylene copolymers. Exemplary acrylic polymers include polymethacrylic acid, polyethyl acrylate, polymethylmenacrylate, polyethyl acrylate - poly methyl melhacrylate copolymers, poly methyl methacrylate - polystyrene copolymers, and polyacrylamides. Exemplary fluorocarbons include polyvinyl fluoride, poly tetrafluoroethylene, polychlorotrifluoroethylene, polyperfluoropropylene, polyvinylidene fluoride, polyperfluoropropylene - polytetrafluoroethylene copolymers, polyperfluoropropylene-polyvinylidene fluoride copolymers, and polyvinylidene fluoride - poly chlorotrifluoroethylene copolymers. The above enumeration is intended to be illustrative and not exclusive and the useful polymers include various analogs, homologs, and adducts thereof. Especially preferred carbon chain polymers include high density, crystalline polyolefins, with a molecular weight above about 100,000. The method of this invention is also useful in providing hard coatings on substrates of heterochain polymers such as polyesters, polyethers, polyamides and polyimides, polyols, polyurethanes, and polysilicones. Exemplary polyesters include alkyds (as alkyd films having the herein contemplated and described dielectric coatings therein), gylcol-maleic acid anhydride ester polymers, glycol-allyl carbonate polymers (as allyl glycol carbonate polymers, exemplified by diethylene glycol bis(allyl carbonate)), saturated ester polyesters as terephthelate polyesters, and polycarbonates (e.g. bisphenol - A polycarbonates and diphenyl carbonate polycarbonates) and polylactones. Exemplary polyethers, include polyacetal, polyalkylene oxides (as polyethylene oxides, polypropylene oxides, and polyepichlorohydrin), urethane-polyol copolymers, polytetrahydrofuran, polyphenylene oxides, and polysulfones. Exemplary useful polyamides and polyimides include nylons, "dimer acids", aryl nylons, the polymeric reaction products of, e.g., 4-4'-Diaminophenyloxide and pyromellitic dianhydride, and the polymeric reaction products of diphenyl isophthalates. Exemplary polyols include the melamines. Exemplary useful polyurethanes include those used to form elastomers (as cast and thermoplastic polyurethanes) by the reaction of a diisocyanate, methylene-bis (4) phenyl isocyanite, or hexamethylene diisocyanate, optionally with a chain extending agent, and a diol, as a polyester diol. The above enumeration of hetero chain polymers is intended to be illustrative and not exclusive or limiting. The monomers may be homopolymers or copolymers, as terpolymers. The copolymers may be random copolymers or block copolymers. While the organic polymeric substrate is generally substantially cured prior to deposition of the transparent, multielement alloy film, the organic polymer may be partially polymerized, i.e., still containing monomeric bonds, e.g., gummy and viscous, or even having liquid portions, and may contain a photoinitiator or photocatalyst, which completes the polymerization or cure during the glow discharge deposition of the multielement alloy. For example the organic polymeric substrate may contain a partially polymerized vinyl or acrylic material and an optical radiation or ultra violet initiated catalyst, as riboflavin-S-phosphate and sodium, which is initiated by the optical or U.V. radiation from the plasma, to increase the degree of polymerization and further bond the multiple element alloy to the organic polymeric substrate. FIGURE 4 shows an optical data storage device 310 as disk 310. The disk 310 includes a grooved substrate 320, carrying a data storage medium 330, and overlaid with a plastic protective overlay 340. Information is stored in the data storage medium by changing the state thereof, e.g., the microstructure, the surface morphology, the reflectivity, the presence or absence of bubbles or hollows, or ablation of the medium. The individual memory cells of the disk 310 are small, on the order of 0.1 to 2.0 X10⁻⁶m. As a result, any scratches, pits, gauges, imperfections, dust, or the like in the plastic overlay 340 can give rise to improper readings, skips, or the like. However, these defects in the optical path through the plastic overlay 340 are substantially reduced by the hard, optically transmissive protective layer 350. FIGURE 5 shows an opthalmic lens 401 having a plastic substrate 421 with the herein contemplated hard coating 411 thereon. The plastic substrate may be a polycarbonate a polyacrylate, such as poly(methyl methacrylate) or a poly(allyl carbonate) such as PPG Industries "CR-39" (R) diethylene glycol bis (allyl carbonate), polymerized with a suitable peroxide initiator to form a hard, substantially light transmissive polymer. The coating 411 is generally from about 1 to about 10 X10⁻⁶m thick and particularly from about 2 to about 5 X10⁻⁶m thick. It may be a graded coating, with a carbon underlayer, as a vacuum deposited carbon coating, film, or layer of 0.5 to 2.0 X10⁻⁶m thickness, and of graphitic or partially graphitic structure, and a silicon composition layer atop the carbon layer. The silicon containing layer may be comprised of: silicon dioxide, silicon carbide, silicon nitride, silicon carboxynitride, or other microwave deposited, transparent silicon composition hard coating. The coating 411 may be of narrow optical band gap so as to block and/or reflect certain optical band widths, i.e., as an optical filter. When the hard coating 411 is utilized as an optical filter, the coating is a multilayer coating with a deposited carbon underlayer on the plastic substrate 411. The carbon, e.g., the deposited amorphous, graphitic or tetrahedrally coordinated material may have an optical band gap to selectively absorb blue and ultraviolet. The plastic substrate could also be a plastic optical fiber, or laser mirror, or a plastic sheet, as a door, window, sun roof insert, or the like. According to a further exemplification of the invention the coated article may be a glass-plastic laminate having the contemplated hard coating on the surface of the plastic unprotected from the glass. Exemplary is a windshield 501 as shown in Figures 6 and 10. However the article could be a window, a storm door glazing unit, or a sliding door glazing unit. The windshield 501 includes a glass substrate 521 with a thin adhesive layer 523 of, for example, polyvinyl alcohol, and a plastic film 525, for example a substantially water white polyurethane. The hard coating for example the silicon carbide, silicon nitride, or silicon oxide hard coating 531 is on the unprotected surface of the plastic layer 525. This results in a significant reduction in abrasion and scratching of the plastic 525. An alternative exemplification is shown in Figure 7. The exemplification shown in Figure 7 is a plastic sheet 601 having the hard coating 635 on at least the surface exposed to abrasion. Alternatively, hard coatings 635 may be on both surfaces of the plastic sheet 601. In this way both the weather incident surface and the interior surface have abrasion resistant coatings. A still further exemplification is shown in Figure 8 where a plastic head light lens 701 is shown. The plastic head light lens 701 has a plastic substrate, as an injection molded plastic substrate 701, with a thin film of the herein contemplated hard coating 735 deposited thereon. According to a still further exemplification of the invention the film is used as a passivation layer for an electronic device or as an interlevel insulator gate dielectric for a MOSFET, such as a Si₃N₄ or SiO₂ thin film, and especially on Si₃N₄ film, optionally containing fluorine. The dielectric is deposited at a low device temperature, that is, at a temperature low enough to avoid diffusion ofsharp profiles of ion implanted dopants across. According to a still further exemplification, a feedstock gas of a halocarbon, as CF4 or C₂F₆, boron trifluoride, and a nitrogen source, as N₂ or cyanogen (CN)₂, can be decomposed by microwave energy to form a precursor gas that deposits to form a disordered boron-carbon coating. The disordered boron-carbon composition, which may have proportions approaching B₄C, is a hard material useful as, for example, a wear coating, as on razor blades, scissors, cutlery, cutting tools, and the like. Thus, in one particularly preferred exemplification a disordered B₄C coating of about 0.5 to 5 x 10⁻⁶m thick is applied to a cutting surface, as a scissor, razor blade, or knife, by the microwave plasma decomposition of a feedstock gas of (1) at least one alocarbon chosen from CF₄, C₂F₆, and volatile homologous thereof; (2) BF₃, and (3) a nitrogen source as N₂ or (CN)₂. An NF₃ gas is recovered during the deposition. Referring now to Figure 9 a photovoltaic cell, formed of a plurality of successively deposited n-i-p layers, each of which comprises a substantially amorphous thin film semiconductor alloy material is shown generally by the reference numeral 810. More particularly, Figure 9 shows a tandem n-i-p type photovoltaic device, such as a solar cell, made up of individual n-i-p type cells 812 a , 812 b and 812 c . Below the lowermost cell 812 a is a substrate 811 which may be formed of a transparent glass or synthetic polymeric member; or formed from a metallic material such as stainless steel, aluminum, tantalum, molybdenum, chrome; or formed from metallic particles embedded within an insulator. Although certain applications may require the deposition of a thin oxide layer and/or a series of base contacts prior to the deposition of semiconductor material, the term "substrate" shall include not only a flexible film, but also any elements added thereto by preliminary processing. Also included within the scope of the present invention are substrates formed of synthetic polymers and metals coated with a synthetic polymer to which one or more conductive base electrodes are applied. Each of the cells 812 a , 812 b and 812 c is preferably fabricated with a thin film semiconductor body containing at least a silicon or silicon: germanium composition. Each of the semiconductor bodies includes a p-type conductivity semiconductor layer 820 a , 820 b and 820 c ; a substantially intrinsic semiconductor layer 818 a , 818 b and 818 c ; and an n-type conductivity semiconductor layer 816 a , 816 b and 816 c . Note that the intrinsic layer may include traces of n-type or p-type dopant material without forfeiting its characteristic neutrality, hence it may be referred to herein as a "substantially intrinsic layer". As illustrated, cell 812 b is an intermediate cell and additional intermediate cells may be stacked atop the illustrated cells. Similarly, the tandem cell may include only two stacked cells. Also, although n-i-p photovoltaic cells are illustrated, this invention may be advantageously practiced with differently configured photovoltaic cells including single or multiple p-i-n cells, Schottky barrier cells, p-n cells as well as with any other semiconductor device having an appropriate top electrode. The term "n-i-p type" as used herein is meant to include any aggregation of n, i and p layers operatively disposed to provide a photoactive region for generating charge carriers in response to the absorption of photon energy. It is to be understood that following the deposition of the layers of semiconductor material, a further deposition process may be either performed in a separate environment or as a part of a continuous process. In this step, a TCO (transparent conductive oxide) layer 822, preferably formed of a material such as tin oxide, indium oxide, indium tin oxide, zinc oxide, cadmium stannate or combinations thereof is added atop the p-layer 820 c of the top most cell 812 c , to function as the top electrode of the cell 810. An electrode grid 824 may be added to the device where the cell is of a sufficiently large area, or if the conductivity of the TCO layer 822 is insufficient to obtain efficient collection of photogenerated current. The grid 824 is adapted to shorten the carrier path and increase the conduction efficiency. As discussed previously, the intrinsic layers 818 a , 818 b and 818 c of the cells 812 a , 812 b and 812 c may be and preferably are formed from semiconductor materials having different bandgaps. For example, intrinsic layer 818 c of cell 812 c may have a band gap of approximately 1.7 eV, intrinsic layer 818 b of cell 812 b may have a band gap of approximately 1.5 eV and intrinsic layer 818 a of cell 812 a may have a band gap of approximately 1.3 eV. In this manner, the most efficient use may be made of a large portion of the incident solar spectrum. It is to be noted that heretofore a solar cell, shown generally as 810, included a layer of about 4.57 x 10⁻⁴m (18 mil) thick transparent flowable organic resin (such as EVA (ethyl vinyl acetate)), generally 826 in Figure 9, which resin would adhere to the subjacent transparent conductive oxide 822 and grid structure 824 as well as provide for step coverage of that non-planar grid structure. The EVA, by itself is characterized by excellent weatherability and no UV absorbtions. However, due to the fact that the layer of flowable organic resin 826 was soft, an outer layer of about a 5 to 10x10⁻⁵m (2-4 mil) thick, relatively hard, transparent laminate, generally 828, provided the outer environmental protection covering. An example of such a laminate was TEDLAR (registered trademark of Dupont Corporation). The problem with the use of such a laminate was that it had additives added thereto in order to prevent ultra-violet degradation, which additives result in short wavelength light absorption giving an overall 8-12 percent loss in transmissivity. Further, when heated to 130 to 140°C to secure the laminate, the EVA would lose transmission of UV wavelengths of incident light. As should be apparent to those ordinarily skilled in the photovoltaic art, such a loss of transmissivity in the laminate translates directly into a substantial loss in solar cell efficiency since portions of incident radiation never reach the photogenerative layers of semiconductor alloy material. Other organic resins which do not absorb as much incident radiation proved to be too soft to serve as environmental protecting laminants for solar cell usage. For instance, FEP (fluorinated-ethylene-propylene) has a relatively soft and reflective outer surface which prevents its use as a hermetic seal for cells. With the present invention, it is now possible to utilize transparent laminates such as FEP with a hard, protective, abrasion resistant, hermetic overcoat, shown generally as 830 in Figure 9. More specifically, the wide bandgap silicon oxi-nitrides, silicon oxides or silicon carbides discussed hereinabove, provide a hard, transparent, flexible, adherent laminate. It is further possible to deposit said hard coatings directly upon the flowable organic resin (such as EVA) 826 or, where step coverage is not a problem, directly upon the TCO layer 822. The invention may be understood by reference to the following examples. Examples A series of polycarbonate substrate coupons were coated with composition hard coatings. In each test a coupon was placed in a vacuum vessel coupled to a source of 2.45 Gigahertz microwave energy. The vacuum vessel was sealed, purged with argon, and pumped down. A feedstock gas mixture was introduced in the vacuum vessel, the microwave energy source energized to initiate and maintain a plasma, and the pressure is adjusted and maintained at 0.467 Pa (3.5 millitorr). The feedstock gas had the composition shown in column 1 (atomic %). The substrate temperature is shown in column 2. The resulting coating had the thickness shown in column 3, and the composition (atomic %) shown in column 5. Column I Gas Composition (Atomic %) Column 2 Substrate Temperature (°C) Column 3 Thickness (x10⁻⁶m) Column 4 Coating Composition or Chemical Bonding Ratios (Atomic %) SiF₄ - 83% 40°C Si - 47% N₂ - 17% 0.05 N - 38% F - 15% SiF₄ - 6.9% 23°C 1.25 Si - 28% N₂O - 23.6% 0-70.6% Ar-69.6% F - 1.4% SiF₄ - 16.3% 23°C 0.80 Si₃-N/B-N N₂ - 81.5% BF₃ - 10% =11 SiF₄ - 15% 23°C 1.25 Si₃-N/B-N N₂ - 75% =1 BF₃ - 10% SiF₄ - 7.6% 23°C 0.53 Si₃-N/B-N N₂ - 81.5% =0.4 BF₃ - 10.9 The analyses for SiO₂ and Si₃N₄ were done by Auger, and the analysis in the SiF₄ - N₂ - BF₃ samples were done by infra red spectroscopy. While the invention has been described and illustrated with respect to microwave plasmas, other high energy plasmas capable of disassociating the precursor compounds, and providing the same reaction pathways and reaction conditions may be used.

Claims: A method of depositing a multiple element composition onto a substrate, the method comprising the steps of: establishing a vacuum deposition region (12) and positioning a substrate (14) therein; providing a plurality of feedstock gases, at least one of the feedstock gases containing an element or elements which are components of the multiple element composition in chemically bonded form with a reactive gasifier element and at least another one of the feedstock gases containing at least one scavenger element capable of preferentially bonding with and scavenging the reactive gasifier element, the feedstock gases being free of combined hydrogen except to the extent that it is optionally added to controllably add hydrogen to the composition; providing a source (17) of plasma excitation energy; exciting the source of plasma excitation energy to excite the feedstock gases to form a plasma therein of excited precursor species, wherein the preferentially bonding scavenger element bonds with the reactive gasifier element to form a chemical compound that is carried off as an effluent in the process at rates sufficient to remove reactive gasifier elements from the plasma thereby to provide net film deposition; and, positioning at least a portion of the plasma of excited precursor species adjacent a surface of the substrate to form thereon from the excited precursor species a film (22) of controlled hydrogen content which includes elements derived from the precursor species; characterised by: establishing a pressure of about 13.3 Pa (0.1 Torr) or less within the deposition region during deposition; and in that: the feedstock gases are excited in a volume in which magnetic fields, if present, do not create an electron cyclotron resonance condition, the substrate being at a temperature below 380°C during deposition. A method according to Claim 1, wherein the reactive gasifier element is fluorine. A method according to claim 2, wherein the reactive gasifier fluorine is in the form of a perfluorosilane. A method according to claim 3, wherein the perfluorosilane is tetrafluorosilane or hexafluorodisilane. A method according to claim 3, wherein the feedstock gas further includes an oxygen source to provide a silicon oxide composition. A method according to claim 5, wherein the oxygen source is chosen from the group consisting of nitrous oxide, carbon monoxide, carbon dioxide, ozone, and oxygen. A method according to claim 3, wherein the feedstock gas further includes a nitrogen source to provide a silicon nitride composition. A method according to claim 7, wherein the nitrogen source is chosen from the group consisting of nitrogen, covalent nitrides, nitrogen oxides, and binary nitrogen halides. A method according to claim 3, wherein the feedstock gas further includes a carbon source to provide a silicon carbide composition. A method according to claim 1, wherein the referentially bonding scavenger element for the highly reactive gasifier element is nitrogen. A method according to claim 10, wherein the compound of the reactive gasifier element is BF₃, the feedstock gas further includes a carbon compound, and the multiple element composition comprises boron and carbon. A method according to any of claims 1 to 11, wherein the source of plasma excitation energy is a microwave source. A method according to claim 1, wherein at least another one of the feedstock gases is a multielement compound.

Inventors: HUDGENS STEPHEN J, JOHNCOCK ANNETTE G, NATH PREM, OVSHINSKY STANFORD R, HUDGENS, STEPHEN J., JOHNCOCK, ANNETTE G., NATH, PREM, OVSHINSKY, STANFORD R.
Applicants: ENERGY CONVERSION DEVICES INC, ENERGY CONVERSION DEVICES, INC.
Application year: 1987
Main classification: C23C16
IPC codes: C23C16