PROCESS FOR PRODUCING A MODIFIED PROPYLENE POLYMER

Abstract: A modified propylene polymer having exceedingly superior coloring-preventive property is provided according to a process which comprises blending a specified phenolic antioxidant, a polyol or a fatty acid partial ester of the polyol, and a radical generating agent with a propylene polymer containing 5 ppm or more of titanium portion or 0.5 ppm or more of vanadium portion of catalyst residue and subjecting the resultant blend to the melting and kneading treatment at a temperature of l50°C - 300°C.

Description: FIELD OF THE INVENTION This invention relates to a process for producing a modified propylene-polymer. More particularly, it relates to a process for producing modified propylene-polymer characterized in blending a specified phenolic antioxidant, a polyol or a fatty acid partial ester of the above-mentioned polyol (hereinafter this will be abbreviated as compound A) and a radical generating agent with a propylene polymer containing 5 ppm or more of titanium portion or 0.5 ppm or more of vanadium portion of catalyst residue, and subjecting the resultant blend to the melting and kneading treatment at a temperature of l50°C - 300°C. BACKGROUND OF THE INVENTION PRIOR ART As propylene polymer is relatively inexpensive and has superior mechanical properties, it is used in the production of various kinds of shaped articles such as injection-moldings, blow moldings, films, sheets, fibers or the like. Propylene polymers are fabricated at a temperature higher than the melting points of the said propylene polymers, but they undergo oxidative deterioration by the heat at the time of their melting and kneading and give rise to the reduction of mechanical strength due to the scission of molecular chain of the said propylene polymer and problems of coloring and smell due to the oxidative deterioration. Particularly, as propylene-polymers have tertiary carbons susceptible to oxidation, in the polymers, they are liable to undergo heat oxidative deterioration and further there are also problem in thermal stability at the time of practical use. On this account, with the object of preventing thermal oxidative deterioration at the time of melting and kneading, a low molecular weight phenolic antioxidant such as 2,6-di-t-butyl-p-cresol (BHT) and with the object of providing heat-stability at the time of practical use, a high molecular weight phenolic antioxidant have been widely used so far. However, when a propylene-polymer blended with the above-mentioned phenolic antioxidants is melted and kneaded, a phenolic antioxidant is oxidized by a complex compound of titanium or vanadium of catalyst residue in the propylene polymer to form a quinone compound at the time of melting and kneading and such a problem occurs that resultant propylene polymers are colored. On this account, a propylene polymer composition obtained by blending pentaerythritol or a polyol which is a reaction product of pentaerythritol with propylene oxide, with a propylene polymer [official gazette of Japanese unexamined patent application (Toxukai) NO. 213036 of 1983] and propylene polymer composition obtained by blending one or more than one compound of a polyol, a partial or perfect ester of fatty acid and polyol, or phosphite or thiophosphite with a propylene polymer [Journal of applied polymer science, 29 , pages, 4421 - 4426 (1984)] have been proposed. Further, a process for producing modified propylene polymer is well known, in which a propylene polymer is subjected to a treatment of melting and kneading in the presence of a radical generating agent to degradate a molecular chain, i.e. to reduce the molecular weight of the propyene polymer, in order to improve shaping and fabricating property of the propylene polymer. OBJECT We, the inventors of this application have found during the course of study on the coloring of propylene polymers containing a large amount of titanium portion as a catalyst residue or vanadium portion as a catalyst residue, that even if the above-mentioned phenolic antioxidant is blended with propylene polymer containing a large amount of titanium portion or vanadium portion as a catalyst residue, followed by the treatment of melting and kneading, no coloring occurs to the extent of practical problem but if the propylene polymer containing such a blended phenolic antioxidant is subjected to the treatment of melting and kneading in the presence of a radical generating agent to obtain modified product, resultant modified propylene polymer is remarkably colored. This phenomenon is not described in the above-mentioned official gazette of Japanese unexamined patent application No. 213036 of 1983 and Journal of applied polymer science 29 , pages 4421-4426 (1984). With the object of improving the shaping and fabricating property of the propylene polymers containing a large amount of titanium portion as a catalyst residue or the propylene polymers containing a large amount of vanadium portion as a catalyst residue, and blended with a phenolic antioxidant, we made strenuous studies on the process for obtaining modified propylene polymer which does not show coloring even when subjected to the treatment of melting and kneading in the presence of a radical generating agent. As the result of this study, we have found that when a propylene-polymer containing 5 ppm or more of titanium portion as a catalyst residue or 0.5 ppm or more of vanadium portion as a catalyst residue is blended with a specified amount of a phenolic antioxidant, a polyol or partial ester of such a polyol with a fatty acid (hereinafter referred to as compound A) and a radical generating agent and then subjected to the treatment of melting and kneading, a modified propylene polymer which does not undergo coloring, can be obtained. Based upon this finding, we have completed the present invention. As evident from the above-mentioned description, it is an object of the present invention to provide a process for producing a modified propylene polymer which does not undergo coloring, by blending a compound A, a phenolic antioxidant and a radical generating agent with a propylene polymer containing 5 ppm or more of titanium portion as a catalyst residue or 0.5 ppm or more of vanadium portion as a catalyst residue and then subjecting the blend to the treatment of melting and kneading. SUMMARY OF THE INVENTION The present invention has a following constitution: A process for producing a modified propylene polymer comprising blending 0.0l - l parts by weight of a polyol or a partial ester of said polyol with a fatty acid (which will be referred to as compound A); 0.0l - l parts by weight of a phenolic antioxidant; and 0.00l - 0.5 parts by weight of a radical generating agent and then subjecting the blend to the treatment of melting and kneading at a temperature of l50°C - 300°C. DETAILED DESCRIPTION OF THE INVENTION The propylene polymers used in the production process of the present invention are those polymer having propylene units as major portion of polymer sections which contain 5 ppm or more of titanium portion as a catalyst residue or 0.5 ppm or more of vanadium portion as a catalyst residue. They are propylene polymers obtained by a polymerization process, for example, a solution polymerization process carried in a saturated hydrocarbon solvent, a bulk polymerization process, a gas phase polymerization process or a combination of a bulk polymerization process and a gas phase polymerization. In the production process of the present invention, there will be no trouble even if a propylene-polymer containing less than 5 ppm of titanium portion as a catalyst residue or less than 0.5 ppm of vanadium portion as a catalyst residue is used. In this case, resultant modified propylene polymer does not show coloring to the extent of practical problem. The propylene polymers used in the present invention are those containing 5 ppm or more of titanium portion as a catalyst residue or 0.5 ppm or more of vanadium portion as a catalyst residue and include as illustration propylene homopolymer; a crystalline random copolymer or a crystalline block copolymer of propylene and one kind or more of α-olefin, such as ethylene, butene-1, pentene-1, 4-methyl-pentene-1, hexene-1, octene-1, or the like; a copolymer of propylene and vinyl acetate, or an ester of acrylic acid or saponification products of these copolymers, a copolymer of propylene and an unsaturated carboxylic acid or its anhydride, a reaction product of copolymer of propylene and an unsaturated carboxylic acid or its anhydride with a metal ion compound. It is possible to use these propylene polymer not only alone but also in the form of a mixture. A mixture of the above-mentioned propylene polymer with a various kinds of synthetic rubber (such as ethylene-propylene copolymer rubber, ethylene-propylene-nonconjugative diene copolymer rubber, polybutadiene, polyisoprene, chlorinated polyethylene, chlorinated polypropylene, styrene-butadiene rubber, styrene-butadiene-styrene block copolymer, styrene-isoprene styrene block copolymer, styrene-ethylene-butylene-styrene block copolymer, styrene-propylene-butylene-styrene block copolymer, etc.) and thermoplastic synthetic resisns (such as polyolefins other than such propylene polymer as polyethylene, polybutene, poly-4-methylpentene-l, etc., polystyrene, styrene-acrylonitrile copolymer, acrylonitrile butadiene-styrene copolymer, polyamide, polyethylene terephthalate, polybutylene terephthalate, polyvinyl chloride, etc.) can be used. Propylene-polymer containing 5 ppm or more of titanium portion as a catalyst residue or 0.5 ppm or more of vanadium portion as a catalyst residue, of propylene homopolymer, crystalline ethylene-propylene random copolymer, crystalline ethylene-propylene block copolymer, crystalline propylene-butene-1 random copolymer, crystalline ethylene-propylene-butene-1 terpolymer, and crystalline propylene-hexene-butene-1 terpolymer are particularly preferable. As compound A useful in the present invention polyols such as glycerine, trimethylol ethane, trimethylol propane, erythritol, pentaerythritol, dipentaerythritol, tripentaerythritol, xylitol, sorbitol, mannitol or the like, monoester of glycerine with fatty acid, monoester of diglycerine with fatty acid; monoester of triglycerine with fatty acid, monoester of pentaglycerine with fatty acid, monoester of sorbitan with fatty acid, monoester of cane sugar with fatty acid, mono- or diester of pentaerythritol and fatty acid, monoester of trimethylol ethane with fatty acid, monoester of trimethylol propane with fatty acid, monoester of polyoxyethylene glycerine with fatty acid, monoester of polyoxyethylene sorbitan with fatty acid, a partial ester of polyol with a fatty acid such as above-mentioned, (as fatty acid such as lauric acid, myristic acid, palmitic acid, stearic acid, behenic acid, oleic acid) can be illustrated. Particularly, trimethylol ethane, monoester of glycerine with fatty acid, mono-, and di-ester of pentaerythritol with fatty acid are preferable. As phenolic antioxidant, 2,6-di-t-butyl-p-cresol, 2-t-butyl-4,6-dimethylphenol, 2,6-di-t-butyl-4-ethyl-phenol, 2,6-di-t-butyl-4-n-butylphenol, 2,6-di-i-butyl-4-n-butylphenol, 2,6-dicyclopentyl-4-methylphenol, 2-(α-methylcyclohexyl)-4,6-dimethylphenol, 2,6-dioctadecyl-4-methylphenol, 2,4,6-tricyclohexylphenol, 2,6-di-t-butyl-4-methoxymethylphenol, n-octadecyl-β-(4'-hydroxy-3',5'-di-t-butylphenol)propionate, 2,6-diphenyl-4-octadecyloxyphenol, 2,4,6-tris(3',5'-di-t-butyl-4'-hydroxybenzylthio)-1,3,5 triazine, 2,6-di-t-butyl-4-methoxyphenol, 2,5-di-t-butylhydroquinone, 2,5-di-t-amylhydroquinone, 2,2'-thio-bis-(6-t-butyl-4-methylphenol), 2,2'-thio-bis-(4-octylphenol), 2,2'-thiobis-(6-t-butyl-3-methylphenol), 4,4'-thio-bis-(6-t-butyl-2-methylphenol), 2,2'-methylene-bis-(6-t-butyl-4-methylphenol), 2,2'-methylene-bis-(6-t-butyl-4-ethylphenol), 2,2'-methylene-bis[4-methyl-6-(α-methylcyclohexyl)-phenol], 2,2'-methylene-bis-(4-methyl-6-cyclohexylphenol), 2,2'-methylene-bis-(6-nonyl-4-methylphenol), 2,2'-methylene-bis-[6-(α-methylbenzyl)-4-nonylphenol], 2,2'-methylene-bis-[6-(α,α-dimethylbenzyl)-4-nonylphenol], 2,2'-methylene-bis-(4,6-di-t-butylphenol), 2,2'-ethylidene-bis-(4,6-di-t-butylphenol), 2,2'-ethylidene-bis-(6-t-butyl-4-i-butylphenol), 4,4'-methylene-bis-(2,6-di-t-butylphenol), 4,4'-methylene-bis-(6-t-butyl-2-methylphenol), 4,4'-butylidene-bis-(6-t-butyl-2-methyiphenol), 4,4'-butylidene-bis-(6-t-butyl-3-methylphenol), 4,4'-butylidene-bis-(2,6-di-t-butylphenol), 4,4'-butylidene-bis-(3,6-di-t-butylphenol), 1,1-bis-(5-t-butyl-4-hydroxy-2-methyl-phenyl)-butane, 2,6-di-(3-t-butyl-5-methyl-2-hydroxy-benzyl)-4-methylphenol, 1,1,3-tris-(5-t-butyl-4-hydroxy-2-methylphenyl)-butane, bis[3,3-bis(4'-hydroxy-3'-t-butylphenyl)butyric acid] ethylene glycol ester, di-(3-t-butyl-4-hydroxy-5-methylphenyl dicyclopentadiene, di-[2-(3'-t-butyl-2'-hydroxy-5'-methylbenzyl)-6-t-butyl-4-methylphenyl] terephthalate, 1,3,5-trimethyl-2,4,6-tris(3,5-di-t-butyl-4-hydroxybenzyl) benzene, 1,3,5-tris(3,5-di-t-butyl-4-hydroxybenzyl) isocyanurate, 1,3,5-tris-(4-t-butyl-3-hydroxy-2,6-dimethylbenzyl) isocyanurate, 1,3,5-tris-[(3,5-di-t-butyl-4-hydroxy-phenyl)propionyloxyethyl] isocyanurate or tetrakis-[methylene-3-(3',5'-di-t-butyl-4'-hydroxyphenyl) propionate] methane can be illustrated. Blending proportions of said compound A and a phenolic antioxidant are, each 0.01-1 parts by weight preferably 0.05 -0.5 parts by weight per 100 parts of propylene polymer. Blending less than 0.01 part by weight cannot exhibit sufficient effect for preventing modified propylene polymer from being colored. It does not matter even if it is over one part by weight but increase of prevention effect for coloring cannot be expected and hence it is not only unpractical but also uneconomical. As for the radical generating agents used in the present invention, it is preferable for obtaining a uniform composition that the decomposition temperature thereof is not too low. The radical generating agents having a half-life of 10 hours at the temperature of 70°C or higher, preferably 100°C or higher, are preferable. As such organic peroxides, benzyl peroxide, t-butyl perbenzoate, t-butyl peracetate, t-butyl peroxyisopropylcarbonate, 2,5-di-methyl-2,5-di-(benzoyl peroxy)hexane, 2,5-di-methyl-2,5-di-(benzoyl peroxy)hexyne-3, t-butyl-di-peradipate, t-butyl peroxy-3,5,5-trimethyl hexanoate, methyl-ethyl ketone peroxide, cyclohexanon peroxide, di-t-butyl peroxide, dicumyl peroxide, 2,5-di-methyl-2,5-di-(t-butyl peroxy) hexane, 2,5-di-methyl-2,5-di-(t-butyl-peroxy) hexyne-3, 1,3-bis-(t-butyl peroxyisopropyl) benzene, t-butyl cumyl peroxide, 1,1-bis-(t-butyl peroxy)-3,3,5-trimethylcyclohexane, 1,1-bis-(t-butyl peroxy) cyclohexane, 2,2-bis-(t-butyl peroxy) butane, p-menthan hydroperoxide, diisopropylbenzene hydroperoxide, cumenhydroperoxide, t-butyl hydroperoxide, p-cymenehydroperoxide, 1,1,3,3-tetramethylbutyl hydroperoxide or 2,5-di-methyl-2,5-di-(hydroperoxy)hexane, can be illustrated. Particularly, 2,5-di-methyl-2,5-di-(t-butyl peroxy)hexane, 2,5-di-methyl-2,5-di-(t-butyl peroxy)hexyne-3 or 1,3-bis-(t-butyl peroxyisopropyl) benzene is preferable. The blending proportion of the above-mentioned radical generating agent is generally in the range of 0.001 - 0.5 parts by weight, preferably in the range of 0.01-0.2 parts by weight based upon 100 parts by weight of propylene polymer. Further, the method for the treatment of melting and kneading is carried out by various kinds of melting and kneading apparatus hereinafter described at a temperature of 150° - 300°C, preferably 180°C -270°C. If the melting and kneading temperature is lower than 150°C, sufficient modifying effect, i.e. effect of improving processability cannot be attained, and a higher than 300°C is not preferable because heat oxidative degradation is so promoted that coloring of the propylene polymer becomes notable. In the process of the present invention, it is possible to use various kinds of additives to be added generally to the propylene polymer containing 5 ppm or more of titanium portion or 0.5 ppm or more of vanadium portion as catalyst residues, e.g. thioether or phosphorus containing antioxidant, light stabilizer, clarifier, nucleating agent, lubricant, antistatic agent, antifogging agent, antiblocking agent, antidropping agent, pigment, metal deactivator (copper deactivator), dispering agent such as metal soaps, neutralizing agent, inorganic filler (e.g. talc, mica; clay, wallastonite, zeolite, asbestos, calcium carbonate, aluminum hydroxide, magnesium hydroxide, barium sulfate, calcium silicate, glass fibers, carbon fibers, the above-mentioned inorganic fillers which are surface-treated with a surface-treating agent such as coupling agent (e.g. silane containing agent, titanate containing agent, boron containing agent, aluminate containing agent, zirco-aluminate containing agent or the like) or organic filler (e.g. wood flour, pulp, waste paper, synthetic fiber, natural fibers or the like) can be used so long as it is not harmful to the object of the present invention. Particularly, simultaneous use of phosphorus containing antioxidant is preferable because coloring-preventive effect can be synergistically exhibited. As preferable phosphorus-containing antioxidant, distearyl pentaerythritol-diphosphite, tetrakis (2,4-di-t-butyl phenyl)-4,4′-biphenylene-di-phosphonite, bis-(2,4-di-t-butylphenyl)pentaerythritol-diphosphite, bis(2,6-di-t-butyl-4-methylphenyl)pentaerythritol-diphosphite and tris(2,4-di-t-butylphenyl)phosphite can be illustrated. The production process of the present invention can be carried out by blending each definite amount of the above-mentioned compound A, a phenolic antioxidant, a radical generating agent and the above-mentioned various kind of additives generally added to propylene-polymer with the propylene polymer containing 5 ppm or more of titanium portion or 0.5 ppm or more of vanadium portion as a catalyst residue in a common mixing apparatus e.g. Henschel mixer (tradename), super-mixer, ribbon blender, banbury mixer at a temperature to the extent that the blended radical generating agent is not decomposed and then subjected to the treatment of melting and kneading at a temperature of 150°C-300°C, preferably 180°C-270°C. [Function] As is well known, a phenolic antioxidant performs a function of inhibitor for extending a radical chain and a radical generating agent generates radicals by the treatment of melting and kneading i.e. heating and performs the scission of principal polymer chain of the propylene polymer to reduce the molecular weight of the propylene polymer and to act to improve the shaping and fabricating property. It is not clear what kind of function does the above-mentioned compound A perform to titanium or vanadium complex compound at the time of the treatment of melting and kneading in the presence of a radical generating agent to the propylene polymer stabilized by a phenolic antioxidant, i.e. mechanism of this function itself is not clear, but in view of the fact that the effectiveness of the present invention cannot be achieved in case of the use of a perfect ester of a polyol with a fatty acid, it is inferred that alcoholic hydroxy group of the compound A acts to the complex compound of titanium or vanadium to form a stable chelate compound. [Effectiveness] Compared with the propylene polymer modified with a propylene-polymer formed by blending a conventionally known phosphorus containing antioxidant or a perfect ester of a polyol with a fatty acid, the modified propylene polymer obtained according to the production process of the present invention, shows less coloring and improved shaping and fabricating property, the latter can be advantageously used in the production of various kind of objective shaped articles by way of various kinds of shaping process such as injection moulding, extrusion moulding, blow moulding or the like. [Specific examples] The present invention will be more fully illustrated by way of Specific examples, Comparative examples and Referential examples hereinafter but it should not be construed to be limited by these. Further, the evaluation method used in the Specific examples, Comparative examples and Referential examples is as follows: Coloring property: The YI (Yellowness Index) of resultant pellets was measured (according to JIS K7l03) and evaluation of coloring was made according to the value of YI. The smaller this value, lesser the coloring. Specific examples 1 - 16, Comparative examples 1 - 3 and Referential examples 1 - 3 In Examples 1 -16, 100 parts by weight of powdered form of propylene homopolymer having a MFR (expressed by extruded amount of melted resin for 10 minutes under a load of 2.16 Kg) of 2.0 g/10 minutes and titanium content of 30 ppm as a propylene polymer, trimethylol ethane, glycerine monostearate, pentaerythritol, pentaerythritol monostearate or pentaerythritol distearate, as a compound A; 2,6-di-t-butyl-p-cresol, tetrakis[methylene-3-(3',5'-di-t-butyl-4'-hydroxyphenyl)propionate]methane, 1,3,5-trimethyl-2,4,6-tris(3,5-di-t-butyl-4-hydroxybenzyl)-benzene, 1,3,5-tris(3,5-di-t-butyl-4-hydroxybenzyl)-isocyanurate or n-octadecyl-β-(4'-hydroxy-3',5'-di-t-butylphenyl)propionate, as a phenolic antioxidant; 2,5-di-methyl-2,5-di(t-butylperoxy)hexane or 1,3-bis-(t-butylperoxyisopropyl)benzene, as a radical generating agent; and other additives each in definite amounts, at the blending proportion indicated in table 1 hereinafter described, were introduced into Henschel mixer (tradename). After mixing with stirring for 3 minutes, resultant blends were modified by subjecting to the treatment of melting and kneading at 200°C by using a single screw extruder having a diameter of 40 mm to obtain pellets of modified propylene polymer. In Comparative examples 1 - 3 and Referential examples 1 - 3, each definite amount of the additives described in Table 1 hereinafter described were blended with 100 parts by weight of powdered propylene homopolymer having a MFR of 2.0 g/10 min (titanium content of 30 ppm) and resulting blends were subjected to melting and kneading treatment based upon the process of Examples 1 - 16. With regard to the resultant pellets, the evaluation of coloring property were carried out according to the above-mentioned testing method. The results thereof are shown in Table 1. Specific examples 17 - 32, Comparative examples 4 - 6 and Referential examples 4 - 6 In Examples 17 - 32, 100 parts by weight of powdered crystalline ethylene-propylene random copolymer having a MFR of 7.0 g/10 min, ethylene content of 2.5% by weight and titanium content of 33 ppm, as propylene polymer; trimethylolethane, glycerine monostearate, pentaerythritol monostearate or pentaerythritol distearate, as a compound A; 2,6-di-t-butyl-p-cresol, tetrakis[methylene-3-(3',5'-di-t-butyl-4'-hydroxyphenyl)propionate]methane, 1,3,5-trimethyl-2,4,6-tris (3,5-di-t-butyl-4-hydroxybenzyl)-benzene, 1,3,5-tris-(3,5-di-t-butyl-4-hydroxybenzyl)-isocyanurate or n-octadecyl-β-(4'-hydroxy-3',5'-di-t-butylphenyl)propionate, as a phenolic antioxidant; 2,5-di-methyl-2-5-di-(t-butylperoxy)hexane or 1,3-bis-(t-butylperoxyisopropyl)benzene, as a radical generating agent: and other additives, each in definite amounts of the blending proportion indicated in Table 2 hereinafter described were charged to Henschel mixer (tradename). After mixing with stirring for 3 minutes the resultant mixtures were subjected to the treatment of melting and kneading at 200°C by using a single-screw extruder having a diameter of 40 mm to obtain pellets of modified propylene polymer. In Comparative examples 4 -6 and Referential examples 4 -6, 100 parts by weight of powdered crystalline ethylene-propylene random copolymer having a MFR of 7.0 g/10 min ethylene content of 2.5% by weight and titanium content of 33 ppm, and definite amounts of the additives indicated in Table 2 hereinafter described were blended and the resultant blends were subjected to the treatment of melting and kneading based upon the process of Examples 17 - 32 and modified pellets were obtained. With regard to the resultant pellets, the evaluations of coloring property were carried out according to the above-mentioned testing method. The results thereof are shown in Table 2. Specific examples 33 - 48, Comparative examples 7 - 9 and Referential examples 7 - 9 100 parts by weight of powdered crystalline ethylenepropylene block copolymer having a MFR of 4.0 g/10 min, ethylene content of 8.5% by weight and titanium content of 33 ppm as a propylene polymer; trimethylolethane, glycerine monostearate, pentaerythritol monostearate or pentaerythritol distearate, as compound A; 2,6-di-t-butyl-p-cresol, tetrakis[methylene-3-(3',5 -di-t-butyl-4'-hydroxyphenyl)propionate]methane, 1,3,5-trimethyl-2,4,6-tris(3,5-di-t-butyl-4-hydroxybenzyl)benzene, 1,3,5-tris-(3,5-di-t-butyl-4-hydroxybenzyl)isocyanurate or n-octadecyl-β-(4'-hydroxy-3',5'-di-t-butylphenyl)-propionate, as a phenolic antioxidant; 2,5-di-methyl-2,5-di-(t-butylperoxy)hexane or 1,3-bis-(t-butylperoxy-isopropyl)benzene, as a radical generating agent; and other additives each in definite amounts of the blending proportion indicated in Table 3 hereinafter described were charged to Henschel mixer (tradename). After mixing with stirring, the blends were subjected to the treatment of melting and kneading at 200°C by using a single screw extruder having a diameter of 40 mm to obtain modified propylene polymer. Further in Comparative examples 7 - 9 and Referential examples 7 -9, 100 parts by weight of powdered crystalline ethylene-propylene block copolymer having MFR of 4.0 g/10 min., ethylene content of 8.5% by weight and titanium content of 33 ppm as a propylene polymer; were blended with each definite amounts of additives indicated in Table 3 hereinafter described, resultant mixtures were subjected to the treatment of melting and kneading based upon the process of Specific examples 33 -48 to obtain pellets of modified propylene polymer. Resultant pellets were subjected to evaluation of coloring properties according to the above-mentioned testing method. The results thereof are indicated in Table 3. Specific examples 49 - 64, Comparative examples 10 - 12 and Referential examples 10 - 12 100 parts by weight of a powdered crystalline ethylene-propylene-butene-1, terpolymer having a MFR of 7.0 g/10 min., ethylene content of 2.5% by weight, butene-1 content of 4.5% by weight, and titanium content of 33 ppm, as a propylene polymer; trimethylol ethane, glycerine monostearate, pentaerythritol monostearate or pentaerythritol distearate, as a compound A; 2,6-di-t-butyl-p-cresol, tetrakis[methylene-3-(3',5'-di-t-butyl-4'-hydroxyphenyl)propionate]methane, 1,3,5-trimethyl-2,4,6-tris(3,5-di-t-butyl-4-hydroxybenzyl)benzene, 1,3,5-tris-(3,5-di-t-butyl-4-hydroxybenzyl)isocyanurate or n-octadecyl-β-(4'-hydroxy-3',5'-di-t-butylphenyl)-propionate, as a phenolic antioxidant; 2,5-di-methyl-2,5-di-(t-butylperoxy)hexane or 1,3-bis-(t-butylperoxy isopropyl)benzene,as a radical generating agent; and other additives each in definite amounts of the blending proportion indicated in Table 4 hereinafter described were charged to Henschel mixer (tradename). After mixing with stirring for 3 minutes, the blends were subjected to melting and kneading treatment at 200°C by using a single screw extruder having a diameter of 40 mm to obtain pellets of modified propylene polymer. In Comparative examples 10 -12 and Referential examples 10 -12, 100 parts by weight of a powdered crystalline ethylene-propylenebutene-1-terpolymer having a MFR of 7.0 g/10 minutes, ethylene content of 2.5% by weight, butene-1 content of 4.5% by weight and titanium content of 33 ppm and additives each in definite amounts indicated in Table 4 hereinafter described, were blended and by the treatment of melting and kneading based upon the process of Specific examples 49 -64, pellets of modified propylene polymer were obtained. With regard to the obtained pellets, evaluations of coloring property were carried out according to the abovementioned testing method. The results thereof are indicated in Table 4. Specific examples 65-80, Comparative examples 13-15 and Referential examples 13 - 15 In specific examples 65 - 80, 100 parts by weight of powdered propylene homopolymer having a MFR of 2.0 g/10 min., vanadium content of 0.6 ppm, as a propylene polymer; trimethylolethane, glycerine monostearate, pentaerythritol monostearate or pentaerythritol distearate, as a compound A; 2,6-di-t-butyl-p-cresol, tetrakis[methylene-3-(3',5'-di-t-butyl-4'-hydroxyphenylpropionate]methane, 1,3,5-trimethyl-2,4,6-tris(3,5-di-t-butyl-4-hydroxybenzyl)benzene, 1,3,5-tris-(3,5-di-t-butyl-4-hydroxybenzyl)isocyanurate or n-octadecyl-β-(4'-hydroxy-3',5'-di-t-butylphenyl)propionate, as a phenolic antioxidant; 2,5-di-methyl-2,5-di-(t-butyl-peroxy)hexane or 1,3-bis-(t-butylperoxyisopropyl)benzene, as a radical generating agent; and other additives each in definite amounts of blending proportion indicated in Table 5 hereinafter described were charged to Henschel mixer (tradename). After the blends were mixed with stirring for 3 minutes they were subjected to melting and kneading treatment at 200°C by using a single screw extruder having a diameter of 40 mm to obtain pellets of modified propylene polymer. In Comparative examples 13 - 15, and Referential examples 13-15, 100 parts by weight of powdered propylene homopolymer having a MFR of 2.0 g/10 min. and a vanadium content of 0.6 ppm as a propylene polymer, and additives each in definite amounts indicated in Table 5 hereinafter described were blended and the blends were subjected to mixing with stirring and then melting and kneading treatment based upon the process of Specific examples 65 - 88 to obtain pellets of modified propylene polymer. Resulting pellets were subjected to the evaluations of coloring property according to the above-mentioned testing method. The results thereof are indicated in Table 5. Specific examples 81 - 96, Comparative examples 16 - 18 and Referential examples 16 - 18 In Examples 81 - 96, 100 parts by weight of powdered crystalline ethylene-propylene random copolymer having a MFR of 7.0 g/10 min., ethylene content of 2.5% by weight and vanadium content of 0.6 ppm, as a propylene polymer; trimethylol ethane, glycerine monostearate, pentaerythritol monostearate or pentaerythritol distearate, as a compound A; 2,6-di-t-butyl-p-cresol, tetrakis[methylene-3-(3',5'-di-t-butyl-4'-hydroxyphenyl)propionate]methane, 1,3,5-trimethyl-2,4,6-tris-(3,5-dit-butyl-4-hydroxybenzyl) benzene, 1,3,5-tris-(3,5-di-t-butyl-4-hydroxybenzyl)iso-cyanurate or n-octadecyl-β-(4'-hydroxy3',5'-di-t-butyl-phenyl)propionate, as a phenolic antioxidant; 2,5-dimethyl-2,5-di-(t-butylperoxy)hexane or 1,3-bis(t-butylperoxyisopropyl)benzene, as a radical generating agent; and other additives indicated in Table 6 hereinafter described each in blending proportion described in Table 6 were charged to Henschel mixer (tradename). After being mixed with stirring for 3 minutes, the blends were subjected to melting and kneading treatment by using a single screw extruder having a diameter of 40 mm to obtain pellets of modified propylene polymer. In Comparative examples 16 - 18 and Referential examples 16 - 18, 100 parts by weight of powdered crystalline ethylene-propylene random copolymer having a MFR of 7.0 g/10 min, ethylene content of 2.5% by weight and vanadium content of 0.6 ppm, as a propylene polymer; and additives indicated in Table 6 hereinafter each in definite amounts were blended the blends were mixed with stirring and subjected to the treatment of melting and kneading based upon the process of Specific examples 81-96 to give pellets of modified propylene polymer. Resultant pellets were subjected to the above-mentioned testing method to evaluate their coloring property. The results thereof are shown in Table 6. Specific examples 97 -112, Comparative examples 19 -21 and Referential examples 19 - 21 In Specific examples 97 -112, 100 parts by weight of a powdered crystalline ethylene-propylene block copolymer having a MFR of 4.0 g/10 min., ethylene content of 8.5% by weight and vanadium content of 0.6 ppm, as a propylene polymer; trimethylol ethane, glycerine monostearate, pentaerythritol monostearate or pentaerythritol distearate, as a compound A; 2,6-di-t-butyl-p-cresol, tetrakis[methylene-3-(3',5'-di-t-butyl-4'-hydroxyphenyl)propionate]methane, 1,3,5-trimethyl-2,4,6-tris (3,5-di-t-butyl-4-hydroxybenzyl)benzene, 1,3,5-tris-(3,5-di-t-butyl-4-hydroxybenzyl)isocyanurate or n-octadecyl-β-(4'-hydroxy-3',5,-di-t-butylphenyl)-propionate, as a phenolic antioxidant; 2,5-di-methyl-2,5-di-(t-butylperoxy)hexane or 1,3-bis-(t-butyl peroxy isopropyl)benzene, as a radical generating agent; and other additive each in definite amounts of blending proportion indicated in Table 7 hereinafter described were charged to Henschel mixer (tradename). After being mixed with stirring for 3 minutes, the blends were subjected to melting and kneading treatment at 200°C by using a single-screw extruder having a diameter of 40 mm to obtain pellets of modified propylene polymer. In Comparative examples 19 - 21 and Referential example 19 - 21, 100 parts by weight of powdered crystalline ethylene-propylene block copolymer having a MFR of 4.0 g/10 min, an ethylene content of 8.5% by weight and a vanadium content of 0.6 ppm, as a propylene polymer; each definite amounts of the additives indicated in Table 7 hereinafter described were blended and mixing with stirring and melting and kneading treatment were carried out based upon the process of Specific examples 97 - 112 to give pellets of modified propylene polymer. Resultant pellets were subjected to the above-mentioned testing method to evaluated their coloring property. The results thereof are shown in Table 7. Specific examples 113 - 128, Comparative examples 22 - 24 and Referential examples 22 - 24 In Specific examples 113 - 128, 100 parts by weight powdered crystalline ethylene-propylene-butene-1, terpolymer having a MFR of 7.0 g/10 min., ethylene content of 2.5% by weight, butene-1 content of 4.5% by weight and vanadium content of 0.6 ppm, as a propylene polymer; trimethylolethane, glycerine monostearate, pentaerythritol monostearate or pentaerythritol distearate, as a compound A; 2,6-di-t-butyl-p-cresol, tetrakis[methylene-3-(3' ,5'-di-t-butyl-4'-hydroxyphenyl) propionate]methane, 1,3,5-trimethyl-2,4,6-tris(3,5-di-t-butyl-4-hydroxybenzyl)benzene, 1,3,5-tris-(3,5-di-t-butyl-4-hydroxybenzyl)isocyanurate or n-octadecyl-β-(4'-hydroxy-3',5'-di-t-butylphenyl)propionate, as a a phenolic antioxidant; 2,5-di-methyl-2,5-di-(t-butyl peroxy)hexane or 1,3-bis-(t-butyl peroxyisopropyl) benzene, as a radical generating agent; and other additives, each in definite amounts of the blending proportion indicated in Table 8 hereinafter described were charged to Henschel mixer (tradename). After mixed with stirring for 3 minutes, the blends were subjected to melting and kneading treatment at 200°C by using a single screw extruder having a diameter of 40 mm to obtain pellets of modified propylene polymer. Further in Comparative examples 22-24 and Referential examples 22 -24, 100 parts by weight of powdered, crystalline ethylene-propylene-butene-1, terpolymer, having a MFR of 7.0 g/10 min., ethylene content of 2.5% by weight, 4.5% by weight of butene-1 and vanadium content of 0.6 ppm; as a propylene polymer; additives each in definite amounts were blended. Based upon the process of Specific examples 113 -128, mixing with stirring and melting and kneading treatment were carried out to obtain pellets of modified propylene polymer. Evaluation of coloring property for resultant pellets was carried out according to the above-mentioned testing method. Results thereof are indicated in Table 8. Various kinds of compound and additives indicated in Tables 1-8 are as follows: Compound A [I]: trimethylol ethane Compound A [II]: glycerine monostearate Compound A [III]: pentaerythritol monostearate Compound A [IV]: pentaerythritol distearate Phenolic antioxidant [I]: 2,6-di-t-butyl-p-cresol Phenolic antioxidant [II]: tetrakis[methylene-3- (3',5'-di-t-butyl-4'-hydroxyphenyl)propionate]-methane Phenolic antioxidant [III]: 1,3,5-trimethyl-2,4,6-tris(3,5-di-t-butyl-4-hydroxybenzyl)benzene Phenolic antioxidant [IV]: l,3,5-tris-(3,5-di-t-butyl-4-hydroxybenzyl)isocyanurate Phenolic antioxidant [V]: n-octadecyl-β-(4′-hydroxy-3′,5′-di-t-butylphenyl)propionate Radical generating agent [I]: 2,5-di-methyl-,2,5-di-(t-butylperoxy)hexane Radical generating agent [II]: l,3-bis-(t-butyl peroxyisopropyl)benzene Phosphorus-containing antioxidant I: tetrakis(2,4-di-t-butylphenyl)-4,4′-biphenylene-di-phosphonite Phosphorus-containing antioxidant 2: bis(2,4-di-t-butylphenyl)pentaerythritol-diphosphite Polyol compound (perfect ester of polyol with fatty acid): pentaerythritol tetrastearate Ca-St: calcium stearate The Specific examples, the Comparative examples and Referential examples in Table l are directed to the case in which propylene homopolymer is used as propylene polymer. As understandable from Table l, in Specific examples l - l6, compound A, a phenolic antioxidant and a radical generating agent are blended with a propylene homopolymer containing 30 ppm of titanium portion of catalyst residue of the present invention, followed by melting and kneading treatment. If Specific examples l - l6 are compared with Comparative examples l - 2, Specific examples l - l6 provide product less coloring. It is understandable that Comparative examples l - 2, in which a phosphorus-containing antioxidant is used in place of a compound A, provide product of notable coloring. If Comparative example 3 in which a perfect ester of a polyol with a fatty acid is used in place of a compound A, is compared with Specific examples l - l6, Comparative example 3 improves a certain extent of coloring property but its improvement is still insufficient. Further, Specific examples 9 - l0, in which a compound A, a phenolic antioxidant, a radical generating agent which are used in each examples of the present invention, and a phosphorus containing antioxidant are blended and melting and kneading treatment is carried out, is compared with Specific example 5, it is recognizable that a superior coloring-preventing effect of a compound A is not hindered and notable synergistic effectiveness by the simultaneous use of a phosphorus-containing compound. Further in Referential examples l - 3 in which no radical generating agent is used, there occurs no notable coloring as evident by the comparison with Comparative examples l - 2. It can be said that the above-mentioned notable coloring is a phenomenon special observable at the time of melting and kneading treatment carried out in the presence of a radical generating agent. However, modified propylene polymer obtained according to the production process of the present invention does not show coloring and provides improvement on shaping and fabricating property. Tables 2 - 4 relate to cases in which crystalline ethylene-propylene random copolymer, crystalline ethylene-propylene block copolymer and crystalline ethylene-propylene-butene-l terpolymer are used. The same effectivenesses as those of the above-mentioned were confirmed with regard to these cases also. The Specific examples and Comparative examples described in Table 5, relate to the cases in which propylene homopolymer is used as a propylene polymer. As understandable from Table 5, Specific examples 65 - 80 relates to the case in which a propylene homopolymer containing 0.6 ppm of vanadium portion of catalyst residue of the present invention is blended with a compound A, a phenolic antioxidant and a radical generating agent, subjected to melting and kneading treatment to do modification. If Specific examples 65 - 80 are compared with Comparative examples l3 - l5, it is understandable that products of Specific examples 65 - 80 shows less coloring the products of Comparative examples l3 - l4 in which a phosphorus-containing antioxidant is used in place of a compound A show notable coloring. If Comparative example l5 in which a perfect ester of a polyol with a fatty acid is used in place of a compound A, is compared with Specific examples 65 - 80, Comparative example l5 improves coloring property to a certain extent but its improvement is not yet fully satisfactory. Further it is understandable that in Specific examples 73 - 74, in which a compound A, a phenolic antioxidant, a radical generating agent and a phosphorus-containing antioxidant used in each Specific examples of the present invention are blended and melting and kneading treatment carried out thereafter, is not harmful to the superior preventive effect for coloring of the compound A as compared with Specific example 69 and notable synergistic effect due to the simultaneous use of a phosphorus containing anti-oxidant is recognizable. Further the products of Referential examples l3 - l5, in which melting and kneading treatment is carried out without using a radical generating agent do not show notable coloring, as evident from the comparison with the products of Comparative exmaples l3 - l4. It can be said that the above-mentioned notable coloring is a specific phenomenon observable at the time of melting and kneading treatment carried out in the presence of a radical generating agent. Tables 6 - 8 are directed to the cases in which crystalline ethylene-propylene random copolymer, crystalline ethylene-propylene block copolymer and crystalline ethylene-propylene-butene-l, terpolymer are used as propylene polymer. With regard to these materials the effectivenesses the same as above-mentioned are confirmed. It is understandable that the modified propylene polymer obtained according to the production process of the present invention shows no coloring and has improved shaping and fabricating property. From the foregoing fact, it has become clear that the modified propylene polymer obtained according to the production process of the present invention has exceedingly superior preventive property for coloring as compared with modified propylene polymers obtained by blending compounds which have been known heretofore to have preventive effectiveness for coloring and subjecting to melting and kneading treatment in the presence of a radical generating agent and thus the notable effectiveness of the present invention has been confirmed.

Claims: A process for producing a modified propylene polymer comprising blending 0.0l - l parts by weight of a polyol or a partial ester of said polyol with a fatty acid (which will be referred to as compound A), 0.0l - l parts by weight of a phenolic antioxidant, and 0.00l - 0.5 parts by weight of a radical generating agent with l00 parts by weight of a propylene polymer containing 5 ppm or more of titanium portion as a catalyst residue or 0.5 ppm or more of vanadium portion as catalyst residue and then subjecting resulting blend to melting and kneading treatment at a temperature of l50°C - 300°C. A process for producing a modified propylene polymer described in claim l in which said compound A is trimethylolethane, monoester of glycerine with a fatty acid, monoester of pentaerythritol with a fatty acid, or diester of pentaerythritol with a fatty acid. A process for producing a modified propylene polymer described in claim l in which said phenolic antioxidant is 2,6-di-t-butyl-p-cresol, tetrakis[methylene-3-(3′,5′-di-t-butyl-4′-hydroxyphenyl)propionate]methane, l,3,5-trimethyl-2,4,6-tris(3,5-di-t-butyl-4-hydroxybenzyl)benzene, l,3,5-tris(3,5-di-t-butyl-4-hydroxybenzyl)isocyanurate or n-octadecyl-β-(4′-hydroxy-3′,5′-di-t-butylphenyl)propionate. A process for producing a modified propylene polymer described in claim 1 in which said radical generating agent is 2,5-di-methyl-2,5-di-(t-butyl peroxy)hexane, 2,5-di-methyl-2,5-di-(t-butyl peroxy)hexyne-3 or 1,3-bis-(t-butyl peroxy isopropyl)benzene. A process for producing a modified propylene polymer described in claim 1 in which said propylene polymer is propylene homopolymer, crystalline ethylene-propylene random copolymer, crystalline ethylene-propylene block copolymer, crystalline propylene-butene-1 random copolymer or crystalline ethylene-propylene-butene-1, terpolymer.

Inventors: KOMORI, NOBUTOSHI, NAKAJIMA, HIROKAZU
Applicants: CHISSO CORPORATION
Application year: 1987
Main classification: C08K5
IPC codes: C08K5, C08F10, C08F210