MULTI-LAYER FILM STRUCTURE AND ELECTRICAL CABLE INCORPORATING SAME

Abstract: A multi-layered adhesive composition particularly suited for adhesion between metallic substrates and vinyl chloride polymer resins particularly highly plasticized vinyl chloride polymer resins comprising a metal adherent layer and intermediate layer and a vinyl chloride polymer adherent layer.

Description: The present invention relates to metallic substrates having a multiple layer coating of polymers selected to provide adhesion between the metallic substrate and a subsequently applied layer of a vinyl chloride polymer. In one embodiment, the invention is further directed to an electrical cable, particularly a communications cable, comprising the multi-layer coated metallic substrate in the form of a sheath system, and optionally, further comprising a water absorbing composition therein. Polymers of vinyl chloride, such as polyvinyl chloride homopolymers or copolymers of vinyl chloride, and other copolymerizable monomers, such as methyl methacrylate, are desirably employed in the preparation of insulating jacketing resins for use in communications cables and other electrical wiring due to the inherent resistance to burning, ready availability, and low cost of such polymers. Suitable resins additionally comprise large percentages of known plasticizing compounds in order to impart desired flexibility to such resins. Because of the large amount of such plasticizing compounds, vinyl chloride polymer jacketing resins are particularly difficult to bond to other substrates, especially metallic substrates. Communications cables desirably include in their construction a sheath normally provided in the form of a metallic strip which is folded circumferentially around centrally disposed conductors and overlapped or otherwise suitably joined to form a substantially cylindrical structure. The sheath may be corrugated to provide greater flexibility. The sheath provides mechanical integrity to the resulting cable, as well as electromagnetic shielding and physical protection to the inner wires and bonding to ground for protection from lightning strikes. Suitable metals for such sheath include aluminum, copper, steel, lead, stainless steel, and coated varieties of stainless steel, such as copper or chrome coated stainless steel. It is known in the art to prepare coated metal substrates, particularly metal strips coated with one or more polymeric layers, to provide a sheath system for use in cable constructions. Coatings of copolymers of ethylene and an ethylenically unsaturated carboxylic acid, such as acrylic acid, are disclosed in U.S. Patent No. 3,681,515. Additionally, polymers suitable for coating metals comprising high molecular weight uniformly random copolymers of ethylene and acrylic or methacrylic acids have been disclosed in U.S. Patent No. 4,351,931. Multiple polymer coatings for use in bonded sheath containing cables are disclosed in U.S. Patent No. 4,487,641. In this reference, coatings comprising a first adhesive material, which is bondable to the metallic layer, and a second adhesive material, which is bondable to the extruded jacketing resin, are employed. A similar structure is disclosed in U.S. Patent No. 4,449,014. Copolymers of ethylene and carbon monoxide, and optionally, additional copolymerizable comonomers such as vinyl acetate, are also known in the art. In published European Patent Application No. 85 1294, such olefin polymers are disclosed for use as heatable high frequency electro-magnetic radiation receptors. Adhesion of such polymers to polyvinyl chloride and polyvinylidene chloride polymers is disclosed. In published Japanese Kokai 57-165,427, copolymers of ethylene, carbon monoxide, and vinyl acetate are disclosed, which are useful adhesives for laminating polyvinyl chloride substrates including substrates which are highly plasticized, for example, with dioctyl pththalate. Thus, it is previously known in the art to prepare two layered adhesive laminates useful for adhesion to metals on the one hand and polyolefin jacketing resins on the other hand. In addition, it is previously known that copolymers of ethylene and carbon monoxides may be adhesively joined to polyvinyl chloride resins. However, a problem still exists in the art in obtaining adhesion between the single or multiple layer adhesive laminates usefully adhered to metal substrates and the ethylene carbon monoxide containing copolymers usefully adhered to vinyl chloride polymer resins. A particular problem exists in obtaining adhesion in such a structure to vinyl chloride polymer resins that additionally contain large quantities of a plasticizer. Accordingly, there remains a difficulty in the art in obtaining a cable construction comprising a metallic sheath in combination with a highly plasticized polyvinyl chloride jacketing resin. An additional problem encountered in the field of communications cables is the need or requirement that the cable jacketing layer be easily removable for installation of grounding connectors yet retain sufficient adhesion to the underlying shielding tape assembly so that abrasion or stretching forces encountered in shipping and installation do not damage the cable structure causing delamination of the polyvinyl chloride jacketing resin. Finally, due to exposure of communications cables to moist environments and even to standing water, it is desirable to provide a communications cable having improved resistance to water permeation and penetration of water longitudinally within the cable such as might occur if the jacketing and/or the protective sheath assembly become abraided or severed thereby exposing the inner conductor assembly to water particularly if the inner conductor assembly is exposed to an elevated hydrodynamic pressure. According to the present invention there is now provided a multiple layer adhesive coating for application to metallic substrates which may be suitably employed to adhere such metallic substrates to a polymer of vinyl chloride. More particularly, the multiple layer adhesive coating of the present invention is usefully employed in obtaining adhesion between such metallic substrates and a highly plasticized polymer of vinyl chloride. The multiple layer adhesive coating of the present invention comprises a metal adherent layer, an intermediate layer, and a vinyl chloride polymer adherent layer. In one embodiment of the invention, the multi-layer coating is employed to adhere a metallic substrate to a vinyl chloride polymer by interposing the multi-layer coating of the invention between the metallic substrate and the vinyl chloride polymer layer, such that the metal adherent layer is adjacent the metal substrate and the vinyl chloride polymer adherent layer is adjacent the vinyl chloride polymer layer. In a further embodiment of the invention, there is provided a communications cable comprising an outer jacket comprising a vinyl chloride polymer and a metallic sheath assembly surrounding an inner conductor means; the metallic sheath assembly being adhered to the vinyl chloride polymer outer jacket by means of a multi-layer coating comprising a metal adherent layer, an interlayer, and a vinyl chloride polymer adherent layer. In a final embodiment of the invention, the inner conductor means comprises one or more conductors each containing a coating of an insulating jacketing resin, optionally a surrounding inner jacket comprising an olefin or a vinyl chloride polymer resin, a water absorbable substrate layer, a metallic sheath, and an outer jacket of a vinyl chloride polymer resin; the sheath being adhered to the outer jacket by means of a multi-layer coating comprising a metal adherent layer, an interlayer, and a vinyl chloride polymer adherent layer. In Figure 1, there is illustrated the multi-layer coating of the present invention adhered to a metallic substrate 5 and to a vinyl chloride polymer substrate 1. The multi-layer coating includes a vinyl chloride polymer adherent layer 2, an interlayer 3, and a metal adherent layer 4. In Figure 2, there is illustrated a cable construction utilizing the multi-layer adhesive structure of the present invention to adhere the vinyl chloride polymer jacketing resin to a metallic sheath and also illustrating the use of the optional water absorbable layer between the sheath and the inner conductor assembly. Accordingly, there is provided an outer jacket of a vinyl chloride polymer 1, a vinyl chloride polymer adherent layer 2, an interlayer 3, a metal adherent layer 4, a metal shield 5, which is folded longitudinally upon itself and optionally sealed to produce an overlap seam 6, a water absorbable layer 7, surrounding a conductor assembly having an insulating layer 8, and inner conductor means 9, which may include one or more conductors 10. Vinyl chloride polymer resins usefully adhered to metallic substrates by use of the present invention include homopolymers and copolymers of vinyl chloride containing up to 40 percent by weight of a copolymerizable comonomer. Suitably copolymerizable comonomers include the alkyl acrylates and methacrylates, containing up to 6 carbon atoms in the alkyl group, vinyl acetate, and the like. Additional polymeric compounds may be blended with the vinyl chloride polymer also in amounts up to 40 percent by weight. Suitable polymeric compositions usefully blended with the vinyl chloride polymer include chlorinated polyethylene, fluorinated polymers, and elastomers such as rubbery polymers of diolefins, copolymers of ethylene, propylene, copolymers of ethylene, propylene and a copolymerizable nonconjugated diene, and functionalized or grafted derivatives thereof. For particular use as a jacketing resin, greater flexibility in the vinyl chloride polymer resin may be imparted by the use of plasticizers. Examples of suitable plasticizers include the phthalates, such as dioctyl phthalate, dinonyl phthalate, diisodecyl phthalate, and dibutyl phthalate; trimellitates, such as tri-2-ethylhexyl trimellitate and triisooctyl trimellitate; phosphates, such as tricresyl phosphate, trioctyl phosphate, and triphenyl phosphate; adipates, such as diisodecyl adipate and diisooctyl adipate; epoxidized oils prepared by epoxidizing soybean oil, rapeseed oil, and like natural oils; fatty acid esters or chlorinated fatty acid esters, such as butyl oleate or methyl tetrachlorostearate; tetrahydrophthalates, such as di-n-octyl tetrahydrophthalate and diisodecyl tetrahydrophthalate; and the like. The plasticizer is suitably employed in an amount of from 5 to 40, preferably from 10 to 33 percent by weight of the jacketing resin. The metal substrate is suitably selected from copper, aluminum, steel, lead, stainless steel, and coated stainless steel, such as copper or chromium/chrome oxide coated stainless steel substrates. The metal adherent layer suitably comprises a copolymer of ethylene and up to 20 percent by weight, preferably up to 10 percent by weight, of a copolymerizable carboxy substituted comonomer. In addition, such copolymers may be further modified by reaction with a dicarboxylic acid anhydride in an amount up to 10 percent by weight anhydride based on a copolymer weight. Examples include the well-known copolymers of ethylene and acrylic or methacrylic acid, particularly the homogeneous copolymers containing up to 10 percent by weight of acrylic or methacrylic acid, and such copolymers additionally containing in copolymerized form an ethylenically unsaturated carboxylic acid ester such as butyl acrylate. Such adhesive resins are particularly well suited for use with aluminum, steel, or stainless steel substrates. Copolymers of ethylene and vinyl acetate and, in particular, such copolymers further modified by reaction with a reactive dicarboxylic acid anhydride such as maleic anhydride may also be employed. Suitably, this latter class of copolymers is particularly adapted for adhesion to copper or copper coated stainless steel substrates. The intermediate layer suitably comprises an adhesive polymer which is compatible with both the metal adhesive layer and the vinyl chloride polymer adhesive layer. The intermediate layer suitably comprises an adhesive polymer which is compatible with both the metal and the vinyl chloride polymer adhesive layer. Examples of suitable polymers for the intermediate layer include copolymers of (1) ethylene and vinyl acetate containing from 10 to 40 percent by weight of vinyl acetate; (2) ethylene and ethyl acrylate containing from 5 to 20 percent by weight of ethyl acrylate; (3) ethylene and methyl methacrylate containing from 5 to 20 percent by weight of methyl methacrylate. Such copolymers further modified by reaction with a reactive dicarboxylic acid anhydride such as maleic, succinic and phthalic anhydride containing from 0.05 to 10 percent by weight of the anhydride may also be employed as well as blends thereof with additional olefin polymers. Examples of suitable resins include CXA® and ELVAX® brand resins available from E. I. duPont deNemours and Co. Additional suitable polymers include the dicarboxylic acid anhydride modified ethylene polymers containing from 0.05 to 10 percent by weight of the anhydride including blends thereof with additional polyolefin resins. Examples of these compounds include the family of resins know as Plexar® resins available from Norchem Inc. A preferred copolymer of ethylene and vinyl acetate contains from 20 percent to 35 percent by weight vinyl acetate, preferably from 25 to 35 percent by weight. The vinyl chloride polymer adherent layer of the multi-layer composition of the present invention comprises a copolymer of ethylene and carbon monoxide containing from 5 to 20 percent by weight of carbon monoxide or, optionally, a terpolymer of ethylene, carbon monoxide and one or more copolymerizable ethylenically unsaturated carboxy-substituted comonomers. Optionally, the present invention also contemplates the use of blends of terpolymers with other polyolefin polymers in which such other polyolefin polymers are present in an amount of from 5 to 20 percent by weight of the total weight of the blend. Particularly preferred vinyl chloride polymer adhesive copolymers include: 1) ethylene-carbon monoxide copolymers in which the carbon monoxide comprises from 2 to 20 percent by weight of the total weight of the copolymer, 2) ethylene-acrylic acid-carbon monoxide terpolymers wherein the terpolymer contains from 1 to 10 percent by weight polymerized acrylic acid and from 5 to 20 percent by weight carbon monoxide based on the total weight of the terpolymer, and 3) ethylene-vinyl acetate-carbon monoxide terpolymers wherein the terpolymer contains from 10 to 35 percent by weight of polymerized vinyl acetate and from 2 to 15 percent by weight carbon monoxide based on the total weight of the terpolymer. The ethylenically unsaturated carboxy containing comonomer may be present in an amount of up to 35 percent based on total polymer weight. The multi-layer adhesive coating of the present invention may be prepared by any suitable technique, but preferably is prepared by the multi-feedblock cast coextrusion of the three polymer layers. Alternatively, the multi-layer adhesive film may be prepared by the technique of film blowing employing compressed air or mechanical techniques to expand a coextruded cylindrical shaped thin film. The cylinder may be slit to provide a resulting film of exceptional uniformity. The multi-layer coating may be separately prepared and later heat sealed to one or both substrates or may be coextruded directly into adhesive contact with one or more of the metal and/or vinyl polymer substrates. In one embodiment of the invention, a metal substrate strip is coated on both sides with the multi-layer coating thereby affording improved intercable adhesion where an inner conductor assembly has an insulating layer comprising a polymer of vinyl chloride. Communications cables embodying a center conductor assembly, optionally include an inner jacket comprising a polyolefin or polyvinyl chloride resin, are prepared utilizing known procedures such as a cone former. A water absorbable layer is optionally applied over the outer coating of the conductor assembly, and the metal strip having the multi-layer adhesive coating thereon is formed and optionally seamed into a cylindrical shape and, also optionally, corrugated to securely encapsulate the water absorbable layer leaving the adhesive layer exposed on the surface. A jacketing resin in a final assembly is extrusion coated over the metallic sheath and adhesively joined thereto by means of the three layer adhesive coating of the present invention. In a preferred structure, the metallic sheath comprises copper or copper coated stainless steel, the metal adherent layer comprises a maleic anhydride modified copolymer of ethylene and vinyl acetate containing from 5 to 10 percent vinyl acetate, the intermediate layer comprises a copolymer of ethylene and vinyl acetate containing from 25 to 30 percent vinyl acetate, and the vinyl chloride polymer adherent layer comprises a copolymer of ethylene and carbon monoxide containing from 5 to 15 percent carbon monoxide. The water absorbable layer, where employed, may be any suitable composition able to absorb and retain water. Typically, such compositions contain a polymer or copolymer of acrylamide monomer. Such compositions may be in the form of a powder or fiber, such as a laminated, woven, or nonwoven fabric structure. A suitable composition is known as Firet® tape available from West Point Pepperell, West Point, Georgia. Most suitably, the communications cables according to the present invention are constructed so that the outermost jacket comprising the vinyl chloride polymer layer, may be removed for installation purposes. Suitably, the outer vinyl chloride polymer jacket is adhered to the underlying metallic sheath sufficiently to prevent accidental delamination, but still remain removable by the use of normal techniques and tools. Preferably, an adhesion between the vinyl chloride polymer jacket and the underlying vinyl chloride polymer adherent layer of from 1.0 to 10.0 pounds per inch (1.75 to 17.5 N/cm) width as tested according to 180° peel testing procedures (Rural Electrification Authority Test PE-39, bulletin 345-67) is desired. Control of adhesion to the vinyl chloride polymer layer may be obtained by adjustment of the amount of carbon monoxide monomer in the vinyl chloride polymer adherent layer. Improved stripability of the vinyl chloride polymer jacket is obtained by employing the preferred range of carbon monoxide previously described. It is desirable that the relatively thick jacket be removable from the metallic sheath of the communications cable. However, it has been discovered that it is not necessary for the relatively thin adhesive layer, which is interposed between the metallic sheath and the relatively thick polyvinyl chloride jacket resin layer, to be removed. During installation, electrical contact with the underlying metallic sheath for purposes of grounding, for example, may be effected by use of a mechanical clamp or other device which has been found to puncture through the relatively thin adhesive layers remaining on the metallic substrate thereby effecting electrical contact. Desirably, the multi-layer adhesive coating is relatively thin, on the order of from 0.01 mm to 0.5 mm in thickness. The vinyl chloride polymer jacketing is somewhat thicker, on the order of from 0.5 mm to 10 mm. Because grounding devices may readily accommodate the relatively thin coatings, i.e., clamping devices equipped with teeth to pierce the thin coating and make electrical contact with the underlying metal shielding, it is generally not required to remove the multi-layer coating as well as the vinyl chloride polymer jacket in order to make electrical connections utilizing cables according to the present invention. It is further desirable that the completed communications cable satisfy certain requirements of water permeability. Most desirably, a cable structure such as that previously described suitably resists permeation of water through the cable in the direction coaxial with the conductors. Desirably, exposure of the severed end of a three foot section of cable to water having a head of approximately 1 met., results in no permeation of water after 24 hours. Most preferably, no water permeation is observed in such a testing procedure after repeatedly heat cycling the cable between temperatures of from -40°C and +60°C over a 30 hour period with a one hour residence time at each temperature and a total cycle time of three hours. Having described the invention, the following examples are provided as further illustrative of the invention. Example 1 A multilayer film comprising a first layer of an ethylene/carbon monoxide copolymer having 10 percent by weight, carbon momoxide, available from The Dow Chemical Company, a second inner layer of ethylene/vinyl acetate copolymer comprising 28 percent by weight vinyl acetate, ELVAX® 3175 available from E. I. duPont deNemours and Co., and a third layer (vinyl chloride polymer adhesive layer) of a maleic anhydride graft modified ethylene/vinyl acetate copolymer, Plexar® 3 available from Norchem, is prepared by a blown film process. The thicknesses of the three layers are 0.025 mm, 0.01 mm, and 0.027 mm, respectively. The film is laminated to one side of a copper alloy tape (0.625 mm thick, 7.5 cm wide) by contacting with the previously heated metal tape (93°C). A two-pair communications cable is prepared by longitudinally wrapping a water swellable tape (Firet® brand tape) and the metal laminated tape having an exposed multilayer film coating about a two-pair cable core. A polyvinyl chloride jacketing resin, 84G048A available from Tehnor Apex Company, is pressure extruded over the outside of the construction and caused to adhere thereto by heat of extrusion. The resulting cable is aged for 48 hours at 60°C. Jacket adhesion value was 6.0 lbs/in (l060 gm/cm) indicating adequate but peelable jacket adhesion. The completed cable is thermal cycled l0 times from -40°C to +60°C with a residence time of one hour at each upper and lower temperature with a total of three hours for each cycle. The cable is severed, the severed end of a 1 meter long section is exposed to water under a hydrostatic pressure of 1 meter of water. No water leakage from the opposite end occurred after 24 hours.

Claims: A multiple layer adhesive film provided between a metal substrate and a vinyl chloride polymer resin; the adhesive film comprising 1) a metal adherent layer of a copolymer of ethylene and up to 20 percent by weight of one or more copolymerizable carboxy containing comonomers, 2) an intermediate layer selected from i) a copolymer of ethylene and vinyl acetate containing from 10 to 40 percent by weight polymerized vinyl acetate, ii) a copolymer of ethylene and ethyl acrylate containing from 5 to 20 percent by weight of ethyl acrylate and iii) a copolymer of ethylene and methyl methacrylate containing from 5 to 20 percent by weight of methyl methacrylate, and 3) a vinyl chloride polymer adherent layer of a copolymer of ethylene and carbon monoxide comprising from 2 to 20 percent by weight of polymerized carbon monoxide, or optionally, a terpolymer of ethylene, carbonmonoxide and one or more copolymerizable ethylenically unsaturated carboxy-substituted comonomers. The film according to Claim 1, wherein the metal adherent layer additionally comprises the reaction product of up to 10 percent by weight of a dicarboxylic acid anhydride. The film according to Claim 1, wherein the vinyl chloride polymer adherent layer comprises an ethylene-acrylic acid-carbon monoxide terpolymer wherein the terpolymer contains from 1 to 10 percent by weight polymerized acrylic acid and from 5 to 20 percent by weight carbon monoxide, and an ethylene-vinyl acetate-carbon monoxide terpolymer wherein the terpolymer contains from 10 to 35 percent by weight of polymerized vinyl acetate and from 2 to 15 percent by weight carbon monoxide, based on the total weight of the terpolymer. The film of Claim 1, wherein the vinyl chloride adherent terpolymer is blended with from 5 to 20 percent by weight of other polyolefin polymers. The film according to Claim 1, wherein the intermediate copolymer layer is modified by a reaction product of a dicarboxylic acid anhydride containing from 0.05 to 10 percent by weight of the anhydride. The film of Claim 5, wherein the reactive dicarboxylic acid anhydride is selected from maleic, succinic, and phthalic anhydride. The film of Claim 1, 5, or 6, wherein the intermediate layer is blended with olefin polymers. A communications cable having improved fire resistance comprising an outer jacket of a vinyl chloride polymer resin; a multi-layer adhesive film comprising a metal adherent layer of a copolymer of ethylene and up to 20 percent by weight of one or more copolymerizable carboxy containing comonomers; an intermediate layer selected from i) a copolymer of ethylene and vinyl acetate containing from 10 to 40 percent by weight polymerized vinyl acetate, ii) a copolymer of ethylene and ethyl acrylate containing from 5 to 20 percent by weight of ethyl acrylate and iii) a copolymer of ethylene and methyl methacrylate containing from 5 to 20 percent by weight of methyl methacrylate; and a vinyl chloride polymer adherent layer of a polymer of ethylene and carbon monoxide wherein the carbon monoxide comprises from 2 to 20 percent by weight of polymerized carbon monoxide, or optionally, a terpolymer of ethylene, carbonmonoxide and one or more copolymerizable ethylenically unsaturated carboxy substituted comonomers; a metallic shield; and a conductor assembly; the metallic shield being wrapped circumferentially around the conductor assembly and adhered to the jacket by means of the multi-layer adhesive film. The cable according to Claim 8, including a water absorbable layer disposed between the metallic shield and the conductor assembly. The cable according to Claim 9, wherein the water absorbable layer comprises a polymer of acrylamide.

Inventors: ACHILLE, FELIX, LENG, PATRICIA B., PIKULA, DANIEL G.
Applicants: THE DOW CHEMICAL COMPANY
Application year: 1987
Main classification: C09J7
IPC codes: H01B7, H01B3, B32B27, C09J7, B32B15