CRYSTALLINE ALUMINOSILICATE AND A METHOD FOR ITS PREPARATION

Abstract: Synthetic layered crystalline aluminosilicates which, apart from the possible presence of water of crystallization, have the general formula expressed as moles of oxides ratios: (M2/nO)x : (SiO2)y : (Al2O3)z, where M represents one or more n-valent cations selected amongst sodium, potassium and any other cations capable of replacing sodium or potassium by ion-exchange, the ratio y/z being between 15 and 300, the ratio x/z being determined from the criterion of electron neutrality between anions and cations, and wherein the structural aluminium is tetrahedrally coordinated in crystal lattice, are suitable as catalysts for the preparation of higher hydrocarbons from a raw material containing lower olefins or oxygenates. These aluminosilicates are prepared from a synthesis mixture the composition of which, expressed as moles of oxides, is: SiO2/Al2O3: 5-500, preferably: 10-300; M2/nO/SiO2: 0.1-10, preferably: 0.1-2; OH/SiO2: 0.1-5, preferably: 0.2-4; H2O/SiO2: 5-200, preferably: 5-75. The synthesis mixture is held under autogenous pressure at a temperature of 80-270 DEG C for 4 hours to 100 days, preferably at 95-160 DEG C for 10 hours to 30 days.

Description: CRYSTALLINE ALUMINOSILICATE AND A METHOD FOR ITS PREPARATION Field of the Invention The present invention relates to a synthetic- layered crystalline aluminosilicate and a method for its preparation. More specifically, the invention relates to a syn¬ thetic layered crystalline aluminosilicate having structural aluminum tetrahedrally coordinated in the crystalline frame¬ work, which exhibits useful properties as a catalyst. Description of the Prior Art Crystalline silicates comprise different classes of materials with varying chemical composition and structure. One of the most well known classes is the zeolites which today are produced in large amounts and used for several different purposes, e.g. as adsorbents, for separation pur¬ poses, and as catalysts. Another class which up to now has attained less interest comprises layered crystalline silicates. An example of a layered crystalline silicate is magadiite. Magadiite is a layered crystalline sodium silicate which in the literature is described by the generally accepted formula NaSi.,0., , (OH) 3 .3H-0. Natural magadiite, depend ent on the place of origin, may contain aluminum as impurities but not incorporated in the crystalline framework. As an example, natural magadiite from Trinity County, California, has a content of aluminum of 0.15-0.18% by weight calculated as oxides (McAtee, J.L. et al. , The American Mineralogist, Vol. 53, Nov.-Dec, 1968, pp. 2061-2069). Preparation of synthetic magadiite has been described in the literature, e.g. in Iler, R.K., The Chemistry of Silica, p. 158, (1979) . Magadiite, either natural or synthetic, may be used for certain purposes, e.g. for ion-exchange or as a molecular sieve or as an absorbent (being able to swell) . For catalytic applications, however, only modifications of magadiite have been described. Catalysts consisting of or containing modified maga¬ diite or other modified layered synthetic crystalline sili¬ cates are already known. It is commonly known that catalysts having activity for certain reactions, e.g. conversion of H-/CO mixtures into hydrocarbons, may be prepared by incorporating σatalytically active metals into a crystalline silicate. This can be performed by per se known methods, e.g. by ion-exchange and/or impregnation. Some reactions are catalyzed by acidic sites in the catalyst. A typical example of such reactions is the con¬ version of oxygenates into hydrocarbons. This conversion is usually carried out using certain types of zeolites being synthetic crystalline aluminosilicates containing aluminum in the crystalline framework. It is known that the aluminum " contained, in the crystalline framework of the zeolites creates acidic sites being active for acid catalyzed reactions. Introduction of aluminum in the crystalline framework takes place during the synthesis of the zeolite. aluminum being present in the synthesis mixture. According to the above-mentioned known techniques, it is not possible to introduce aluminum in the crystalline framework of an already synthesized zeolite. An example of a synthetic layered silicate is given in US patent No. 4,481,174. This patent describes a process for the preparation of a synthetic aluminum and phosphorus containing crystalline layered alkali silicate designated PZ1. Furthermore, the patent describes how to transform PZ1 into a new crystalline aluminosilicate designated PZ2. PZ2 is stated to be suitable for catalytic conversion of alcohols into hydrocarbons. PZ1 is prepared from an aqueous synthesis mixture containing Si0 2 , A1 2 0-, and alkali in the presence of an organic template compound containing phosphorus. It is stated that the synthesis must be performed using SiO_/Al 2 0 3 mole ratios of between 50 and about 250 since, otherwise, different products will be the result. PZ1 is, thereafter, transformed into PZ2 by treatment with a dilute acid or by ion-exchange with NH.C1 and subsequent calcination. It is a characteristic feature of the aluminosili¬ cates PZ1 and PZ2 that they both contain phosphorus. Further¬ more, it is emphasized that the transformation of PZ1 to PZ2 is irreversible, i.e. PZ2 can not be transformed into PZl due to some structural changes. U.S. Patent No. 4,481,174 states that PZl and PZ2 have distinctly different X-ray diffraction patterns which both are different from the X-ray diffraction pattern of magadiite. Summary of the Invention The invention relates to a synthetic layered crystal¬ line aluminosilicate having useful properties as a catalyst and a method for its preparation. When disregarding the presence of crystal water, the aluminosilicate of the invention can be characterized by the following general formula expressed as moles of oxides ratios: In this formula, M represents one or more n-valent cations selected from the group consisting of sodium, potassium, and any other cation capable of replacing sodium or potassium by ion-exchange. The ratio y/z is between 15 and 300, prefer¬ ably between 20 and 150. The ratio x/z is determined from the criterion of electron neutrality between anions and cations. The major portion of aluminum is present tetrahedrally coordinated in the crystalline framework. 0 Furthermore, the invention relates to a method for the preparation of the above synthetic crystalline alumino¬ silicate. A characteristic feature of the method according to the present invention is that no template compound is used. 5 Detailed Description of the Invention It is known that " crystalline aluminosilicates, e.g. zeolites, are .active for "siiape selective reactions for 0 instance conversion of ~ τπethanol to higher hydrocarbons such as gasoline fractions. In particular, zeolites with a high silicon to aluminum ratio have shown high stability, whereas other zeolites often deactivate very rapidly. g It has surprisingly been found that the synthetic layered crystalline aluminosilicate of the present invention shows unusually high catalytic activity and selectivity for synthesis of higher hydrocarbons from a starting material comprising lower olefins or oxygenates. Furthermore, this Q aluminosilicate has a long active lifetime. It is assumed that the tetrahedrally coordinated aluminum situated in the layered crystalline aluminosilicate framework is responsible for the catalytic activity. This ,_ assumption is supported by the fact that layered silicates containing no aluminum, for instance magadiite and layered silicates containing aluminum which is not incorporated in the crystalline framework do not have such catalytic activity. The synthetic layered crystalline aluminosilicate according to the present invention can be characterized by its chemical composition, by its X-ray diffraction pattern, by its NMR spectrum, and by its alpha value. The chemical composition as described by the above formula has been determined by conventional chemical analysis, The X-ray diffraction pattern was determined by standard techniques. The radiation was the K-alpha doublet of copper, and a proportional counter diffractometer equipped with a strip chart pen recorder was used. The peak heights, I, and the positions as a function of 2 times theta, where theta is the Bragg angle, were read from the diffractometer chart. From these, the relative intensities, I/I (as per cent) , where I is the intensity of the strongest line or peak, and d/A, the interplanar spacing in A, corresponding to the recorded lines, were calculated. Only lines with I/Io - 1 were taken into account. in Table 1, the X-ray diffraction patterns are given of three typical synthetic layered crystalline aluminosilicat according to this invention and described later on in this specification, namely the aluminosilicates of Examples 1 and and the aluminosilicate A of Example 3, all in their sodium form (Na-form) . Table 1 further gives the X-ray diffraction pattern of natural magadiite and the X-ray diffraction pattern of PZl (as described in U.S. Patent No. 4,481,174). Table 1 X-ray diffraction patterns c >f si:licates on Na~ • form Aluminosilicates according to the invention Naturaιl Example 1 Example 2 Exampl .e 3 Magadiite PZl d/A I X o d/A τ /1 o d/A l / τ o d?A o d/A I Io- _ _ — _ _ — 19.4 10 _ — 15.2 100 15.4 100 15.3 100 15.5 100 15.49 100 - - - - - - - - 9.97 7 — - - - - - 9.83 2 - - — - - - - - - 9.18 1 7.68 8 7.73 7 7.67 6 7.76 3 - - — - 7.31 2 - - 7.20 2 7.31 2 — - - - - - 6.83 1 - - - - - - - - 5.60 2 - - 5.14 8 5.16 10 5.13 12 5.17 10 5.15 17 — — - - - - 5.01 9 - - — — - - - - - - 4.84 13 - - - - - - 4.69 3 - - — — - - - - 4.45 14 4.55 7 — - - - 4.23 2 4.24 2 4.23 5 - - - - - - 4.00 7 - - - - - - - - 3.92 5 - - 3.85 5 - - - - 3.85 2 - - 3.73 3 - - - - - - - - 3.64 21 3.64 15 3.65 16 3.62 8 3.68 6 3.56 26 3.56 17 3.55 21 3.54 10 3.56 14 3.45 76 3.45 65 3.45 68 3.43 40 3.44 59 3.31 47 3.31 36 3.30 41 3.30 27 3.30 30 — — — - - - 3.20 11 - - 3.15 56 3.16 63 3.15 53 3.14 30 3.15 28 — — — — — - 3.03 4 - - — — — — — - 2.98 4 - - Table 1 X-ray diffraction patterns of silicates on Na- -form Aluminosilicates according to the invention Natural Example 1 Example 2 Example 3 Magadiite PZl 2.82 5 2.83 5 2.82 4 2.85 4 ... •— - - - - - - 2,81 4 - - - - - - - - 2.73 2 - - 2.61 3 2.60 4 2.62 2- 2.64 2 - - 2.58 5 - - 2.58 5 2.59 3 - - - - - - - - 2.53 3 - _. - - - - - - 2.52 3 - - - - - - - - 2.50 2 - - 2.43 2 - - - - 2.40 2 - - 2.34 4 2.35 5 2.34 4 2.35 4 - - 2.29 3 2.29 4 2.28 2 2.28 2 - .- - - - - - - 2.26 2 - - - - - - - - - - 2.15 18 - - - - - - 2.09 1 - - - - - - - - 2.07 2 - - - - - - - - 2.05 4 - - - - - - - - 2.01 1 - - 1.99 2 1.99 1 - - 2.00 1 - - - - - - - - 1.96 1 - 1.93 2 1.94 2 1.93 2 1.94 2 - - - - - - - - 1.87 2 - - 1.83 15 1.83 13 1.83 13 1.82 6 1.83 6 1.78 1 1.78 2 1.78 1 1.78 1 - - In Table 2, the X-ray diffraction patterns are given for the same aluminosilicates and in the same manner as in Table 1, however, after having been converted to their hydrogen form (H-form) as described in the examples. Table 2 further gives the X-ray diffraction patterns of the H-form of natural magadiite and PZ2 (as described in US Patent No. 4.481.174) . Table 2 X-ray diffraction patterns of silicates on H-form H-form of Aluminosilicates according to the invention Natural Example 1 Example 2 Example 3 Magadiite PZ2 d/A I/I d/A I/I d/A I/I d7I Ϊ7Ϊ 37-. Ϊ7 12.1 30 12.5 17 11.6 32 11.3 16 13.48 100 7.27 7.29 7.15 2 7.34 24 5.58 6 5.33 2 4.09 7 3.81 5 3.82 17 3.63 14 3.66 11 3.60 28 3.64 11 3 56 14 3.55 55 3.37 100 3.41 100 3.39 100 3, 38 100 3.40 85 3.17 3 3.18 3 3 18 13 3, 09 8 2.65 1 2, 65 1 2.46 1 2.51 2 2.29 2 2.22 2.21 3 2.13 3 2.04 1 2.03 1 1.93 1 1.85 8 1.85 10 1.84 1.84 8 1.85 20 1.79 1 1.80 1 1.80 3 Tables 1 and 2 demonstrate that the aluminosilicates according to this invention, both in their Na-form and in their H-form, have X-ray diffraction patterns distinctly different from those of the known silicates such as natural magadiite and the silicates PZl and PZ2 described in U.S. Patent No. 4,481,174. The differences in the X-ray diffraction patterns of the aluminosilicates of the present invention may be ascribed to differences in the composition of the synthesis mixture and in the preparation. The first line of the X-ray diffrac¬ tion pattern (i.e. lines 15.2, 15.4, and 15.3 of Table 1 and lines 12.1, 12.5, and 11.6 of Table 2, respectively) represents the basal spacing and is a measure of the degree of swelling of the layered crystalline aluminosilicate. Thus, it will appear, i.a. from the below Example 3 (Products C, D, E, and G) that heating to an elevated temperature will reduce the basal-spacing. This may be explained by a dehydration of "the aluminosilicate taking place. Even though there is some variation in the X-ray diffraction patterns of the layered crystalline alumino¬ silicates according to the invention, certain lines of the diffraction patterns are characteristic features of these aluminosilicates. These characteristic lines of the Na-form aluminosilicate of the present invention are shown in Table 3: Table 3 Characteristic lines in the X-ray diffraction pattern of the Na-form aluminosilicate of the present invention d/A I/I 15.4 + 0.2 VS 7.7 + 0.1 w 5.13 + 0.05 w 3.64 + 0.02 w 3.56 + 0-.01 MW 3.45 + 0.01 s 3.31 + 0.01 M 3.15 + 0.01 M 2.82 + 0.01 VW 2.58 + 0.02 VW 2.33 + ' 0.02 vw 2.28 + 0.02 vw 1.93 + 0.01 VW 1.83 + 0.01 w 1.78 + 0.01 vw The letters used in Table 3 to indicate the relative intensities have the following.meanings: VS 2 very strong s -= strong M = moderate MW = medium weak W S weak VW = very weak The position of aluminum in the crystalline frame- work was determined by an NMR technique. 27Al and 29Si magic-angle spinning (MAS) solid state (SS) NMR abbreviated 27 A1 MAS-SS NMR respectively 29 Si MAS-SS NMR was used. This NMR technique is described e.g. in Fyfe et al. , J. Phys. Chem. 1984, 88, pp 3248-3253, and in Thomas, J.M. et al. ACS Symp. Ser. 1983, 218, pp. 159-180. The results of measure¬ ments by this technique are described in Example 1. From the relative intensity of the NMR lines it is furthermore possible to calculate the Si0 2 /Al 2 0- ratio in the crystalline framework. The catalytic activity of the aluminosilicates was evaluated by the so-called alpha test giving the alpha value. The alpha value is an approximate indication of the catalytic cracking activity of a given catalyst compared to that of a standard catalyst, and it gives the relative rate constant expressed as the rate of normal hexane conversion per volume of catalyst per unit time. It is based on the activity of a highly active silica-alumina cracking catalyst taken as an alpha value of 1. The alpha value correlates with the number of acidic sites in the catalyst. The alpha test is described in the Journal of Catalysis, Vol. IV, pp. 522-529 (August 1965) , and in Nature 3J09, 589-591 (1984) . The synthetic layered crystalline aluminosilicate according to this invention is prepared from a synthesis mixture comprising at least one source of aluminum and at least one source of silicon, having the composition expressed as moles of oxides ratios: Broad Preferred Range Range Si0 2 / l 2 0 3 = 5-500 10-300 M 2/n 0/Si0 2 = °' 01 ~ 10 0.1-2 0H/Si0 2 = 0.1-5 0.2-4 H 2 0/Si0 2 = 5-200 5-75 which is maintained under such conditions that crystalliza¬ tion of the synthetic layered crystalline aluminosilicate takes place. It should be emphasized that no template compound or seeding is used in the preparation of the aluminosilicate according to the present invention. It will be understood that each oxide component utilized in the synthesis mixture can be supplied by one or more initial reactants and that they can be mixed intimately together either at once or stepwise. As a source of aluminum may be used one or more alu¬ minum compounds, e.g. alumina hydrates and/or alkali metal aluminates, especially sodium aluminate. As a source of silicon may be used one or more silicon compounds, e.g. silica, especially colloidal silica, and/or alkali metal silicates, especially sodium silicate. The cation M may be added as a component of the above aluminates or silicates or as a separate component, e.g. as an alkali metal hydroxide, especially sodium hydrox¬ ide. The concentration of water in the synthesis mixture is not critical. However, an increased concentration of water increases the preparation time, but on the other hand, re¬ duces the risk of by-product formation. Crystallization can be carried out at either static or stirred condition. In the examples, static conditions were employed using polypropylene jars in stainless steel autoclaves at 130-140°C under autogeneous pressure. The pressure is not critical and can be varied within a wide range. The useful range of temperature is 80-270 C for about 4 hours to 100 days, preferably 95-160°C for about 10 hours to 30 days. Crystal size and crystallization time of the synthe¬ tic layered crystalline aluminosilicate will vary with the nature of the reaction mixture employed and the crystalliza¬ tion conditions. The preparation process shall be interrupted, when crystallization of the layered aluminosilicate is completed since, otherwise, unwanted by-products may be formed. The synthetic layered crystalline aluminosilicate produced is preferably separated from the mother liquor by filtration and, thereafter, is preferably washed, suitably with deionized water at a temperature in the range of, for example, 15-95°C. The content of aluminum in the framework of the catalyst is closely related to the content of aluminum in the synthesis mixture. A high content of aluminum in the framework generally means a- high catalytic activity. On the other hand, a high content of aluminum in the synthesis mixture results in an increased crystallization time, The synthetic layered crystalline aluminosilicates prepared by the method of this-invention may be used as catalysts or as catalyst supports. The synthetic layered crystalline aluminosilicates may be used as such or mixed with a support material such as silica, alumina, or another aluminosilicate. Before use as a catalyst or a catalyst support, it is desirable to modify the synthetic layered crystalline alumino¬ silicate in one or a number of ways. Thus, for many catalytic purposes, it is preferred to reduce the alkali metal content of the synthetic layered crystalline aluminosilicate. This may be achieved by sub¬ jecting the layered aluminosilicate to one or more ion- exchanges with a solution containing suitable cations. For example, the aluminosilicates may be ion-exchanged with a solution containing ammonium cations and thereafter calcined to produce the active hydrogen- form. Another way is ion-exchange with a solution of an acid, e.g. an aqueous mineral acid at a temperature in the range of 15-95°C, preferably 20-35 C. Furthermore, the lay¬ ered aluminosilicates may be ion-exchanged or impregnated with a compound of one or more metals. Suitable metals include iron, cobalt, nickel, platinum, etc. The compounds of the metals used are suitably those compounds which will decompose on the application of heat to form the corresponding oxides and which are soluble in water, e.g. the nitrates. The synthetic layered crystalline aluminosilicate prepared, with or without the above described treatments and/or modifications, may be used as a catalyst in the form of a fixed or a fluidised bed in e.g. alkylation, oligomerisa- tion, isomerisation, and hydrogenation reactions. Especially, the synthetic layered crystalline aluminosilicate according to this invention may be used as a catalyst for conversion of alcohols and ethers to hydro¬ carbons. In the following, the present invention will be further illustrated by way of examples which are intended to be solely exemplary of the invention. Examples 1-5 show the preparation of preferred em¬ bodiments of the synthetic layered crystalline aluminosilicate according to the invention. Example 6 shows that the reverse transformation of the H-form into the Na-form of the synthetic layered crystal¬ line aluminosilicate according to Example 1, can be carried out using mild conditions. Example 7 shows the preparation of an aluminosilicate with a composition different from that of the aluminosilicate of the present invention, i.e. an aluminosilicate having a molar Si0 2 /Al 2 0 3 ratio of 944. Example 8 is a comparison example showing the cata¬ lytic activity for conversion of methanol into hydrocarbons of a synthetic layered crystalline aluminosilicate according t the present invention (the aluminosilicate of Example 1) com¬ pared to an aluminosilicate not included in the present inven¬ tion (the aluminosilicate of Example 7) . The Example further shows the composition of the produced hydrocarbon mixtures. Example 9 shows the catalytic activity of a synthe¬ tic layered crystalline aluminosilicate according to the present invention (the aluminosilicate of Example 3) for conversion of olefins (exemplified by propylene) to hydro¬ carbon mixtures. The sodium silicate solution employed in the examples has the following composition (% by weight) : sio 2 = 27. 8 Na 2 0 = 8. 2 H 2 0 = 64. 0 The colloidal silica employed in the examples has the following composition (% by weight) : Si0 2 = 40.0 Na 2 0 = 0.5 H 2 0 = 59.5 Example 1 A solution of 20 g sodium aluminate in 250 g deion- ized water was added to 400 g sodium silicate solution while stirring at ambient temperature. To the mixture was added 400 g colloidal silica. The stirring was continued until an intimate mixture was obtained and then further 100 g col¬ loidal silica was added. The resulting synthesis mixture had the following molar composition: Si0 2 / l 2 0 3 = 54 a 2 0/Si0 2 *_ 0.14 0H/Si0 2 = 0.28 H 2 0/Si0 2 = 8.6 The synthesis mixture was heated in an autoclave for 8 days at autogeneous pressure and at a temperature of 140°C. The product was filtered off, washed by deionized water, and dried at ambient temperature. A sample of the dried product was analysed using 27 NMR. Al MAS-SS NMR shows the presence of tetrahedrally coordinated aluminum characterized by a resonance at about 50 ppm referring to Al(H 2 0) g 3+. 29Si MAS-SS NMR presents charac¬ teristic signals at about -111 and -106 ppm (relative to tetramethylsilane) referring to Si(-OSi) . and Si(-OSi) 3 (-OA1) groups, respectively. The presence of the latter groups is indicative of tetrahedral aluminum incorporated in the silica framework. The Si0 2 /Al 2 0_ ratio calculated from the intensities of the 29 Si NMR lines at about -100 (= Si-O-R, R = Na, H) , -106 and -111 ppm (se above) is 32. The X-ray diffraction pattern of the product in its Na-form is shown in Table 4. Table 4 d/A I/I 15.20 100 7.68 8 5.14 8 3.85 5 3,73 3 3.64 21 3.56 26 3.45 76 3.31 47 3.15 56 2.82 5 2.61 3 2.58 5 2.43 2 2.34 4 2.29 3 2.00 2 1.93 2 1.83 15 1.78 1 The X-ray diffraction pattern showed that the Na-form product was crystalline. A sample of the product was transferred into the H-form by ion-exchange using an aqueous 0.1 N HCl solution, washing by deionized water, and drying at ambient temperature, The X-ray diffraction pattern of the product in its H-form is shown in Table 5. Table 5 d/A I/I 12.1 30 7.27 5 3.81 5 3.63 14 3.37 100 3.17 3 1.85 8 1.79 1 The X-ray diffraction pattern showed that the H-form product was crystalline. The H-form product had an alpha value of 14.8. Example 2 A solution of 13,4 g sodium aluminate in 500 g deion¬ ized water was added to 800 g sodium silicate solution while stirring at ambient temperature. To the mixture was added 800 5 g colloidal silica. The stirring was continued until an inti¬ mate mixture was obtained. The resulting synthesis mixture had the following molar composition: 10 Si0 2 /Al 2 0 3 = 140 Na 2 0/Si0 2 = 0. .13 0H/Si0 2 = 0. .26 H 2 0/Si0 2 = 9. .15 T5 The synthesis mixture was placed in an autoclave for 6 days at autogeneous pressure and at a temperature of 135°C. 20 The product was filtered off-, washed by deionized water, and dried at ambient temperature. The X-ray diffraction pattern of the product in its Na-form is shown in Table 6. 25 30 35 Table 6 d/A I/I 15.4 100 5 7.73 7 7.31 2 5.16 10 3.64 15 3.56 17 TO 3.45 65 3.31 36 3.16 63 2.83 5 2.60 4 J5 2.35 5 2.29 4 1.99 1 1.94 2 1.83 13 20 1.78 2 The X-ray diffraction pattern showed that the Na-form product was crystalline. 25 Chemical analysis carried out on the crystalline product showed the following chemical composition (per cent by weight) : Na 2 0 = 5.9 30 1 2 0 3 = 0.85 sio 2 = 82.7 H 2 0 = 10.6 Consequently, the molar Si0 2 /Al 2 0 3 ratio is 165. 35 A sample of the product was transferred into the H-form by ion-exchange using an aqueous 0.1 N HCl solution, washing by deionized water, and drying at ambient temperature. The X-ray diffraction pattern of the product in its H-form is shown in Table 7. Table 7 d/A I/I 0 12.5 17 7.29 4 3.66 11 3.41 100 3.18 3 2.65 1 2.46 1 2.22 1 1.85 10 1.80 1 The X-ray diffraction pattern showed that the H-form product was crystalline. Example 3 A solution of 40 g sodium aluminate in 500 g deion¬ ized water was added to 800 g sodium silicate solution while stirring at ambient temperature. To the mixture was added 1000 g colloidal silica. The stirring was continued until an intimate mixture was obtained. The resulting synthesis mixture had the following molar composition: Si0 2 /Al 2 0 3 -S 54 Na 2 0/Si0 2 = 0. 14 OH/Si0 2 = 0. 28 H 2 0/Si0 2 = 8. 6 The synthesis mixture was heated in an autoclave for 10 days at autogeneous pressure and at a temperature of 130°C. The obtained product A was filtered off, washed by deionized water, and dried at ambient temperature. A product B was obtained by heating a sample of A to 120°C for 16 hours. A product C was obtained by heating a sample of A to 480°C for 4 hours. The X-ray diffraction patterns of the three Na-form products A, B, and C are shown in Table 8. Table 8 3 d/A I/I Q d/A ι/ι 0 d/A I/I 15.3 100 15.2 100 12.5 15 7.67 6 7.60 6 - - 7.22 5.13 12 5.09 4.23 2 3.83 5 3.80 3.65 16 3.64 18 3.55 21 33..5555 2222 3.58 17 3.45 68 33..4444 6677 3.38 100 3.30 41 3.30 42 3.15 53 3.15 49 15 2.82 4 2.81 3 2.62 2 2.62 3 2.58 5 22..5577 33 2.55 2.34 4 2.33 3 2.28 2 20 1.93 2 . 1.93 2 1.83 13 11..8833 1133 1.84 9 1.78 1 11..7788 22 1.78 1 The X-ray diffraction patterns showed that the 25 products were crystalline. A sample of the Na-form product A was transferred into the H-form product D by ion-exchange with an aqueous 2M NH.NO- solution at 80°C, washing by deionized water and 30 calcinating in air for 4 hours at 480°C. Using the same treatment, a sample of the Na-form product C-was transferred into the H-form product E. 35 A sample of the Na-form product A was transferred into the H-form product F by ion-exchange with an aqueous 0.1 N HCl solution at 20 C, washing by deionized water and drying at ambient temperature. A sample of the H-form product F was calcined at 530 C for h hour leading to a H-form product G. The X-ray diffraction patterns of the four H-form products D, E, F, and G are shown in Table 9. Table 9 d/A I/I. d/A I/I ¬ d/A I/I. d/A I/I. 11.6 32 11.1 16 12.5 19 11.1 30 7.33 6 7.25 4 5.91 3 5.46 14 3.82 17 3.83 8 3.81 11 3.60 ' 28 3.63 6 3.64 5 3.39 100 3.39 100 3.40 100 3.38 100 3.16 2 2.99 2.64 1 2.46 1 2.22 1 1.84 1.84 1.85 9 1.85 1.80 1 The X-ray diffraction patterns showed that the products were crystalline. The H-form product D had an alpha value of 14.4. Chemical analysis carried out on the Na-form product A showed the following chemical composition (per cent by weight) : a 2 0 = 5.4 Al 2°3 = 4 *° Si0 2 = 64.4 H 2 0 = 26.3 Consequently, the molar Si0 2 /Al 2 0 3 ratio is 27.4. From NMR analysis carried out on the Na-form pro¬ duct A in the same way as described above, a Si0 2 /Al 2 0 3 ratio of 27.2 was calculated. This indicates that essentially all Al is present tetrahedrally coordinated in the crystal¬ line framework. Examples 4 and 5 Two synthesis mixtures were prepared as described in Example 1, the only difference being that the gel preparation was performed at 0°C. The synthesis mixtures were placed in autoclaves for 6 days at autogeneous pressure and at a temperature of 130°C. To the mixtures was then added deionized water for adjustment to the following molar ratios: Ex 4 Ex 5 H 2 0/Si0 2 28.5 135.0 Thereafter the mixtures were placed in autoclaves for further 10 days at the above conditions. The products were filtered off, washed by deionized water, and dried at ambient temperature. The X-ray diffraction patterns of the products in their Na-form are shown in Table 10. Table 10 Ex 4 Ex 5 d/A I/I d/A I/I 15. ,34 00 15.37 100 7. .68 7 7.70 8 7. ,14 2 - 5. ,10 11 5.14 12 3 3.. ,6655 1 155 3 3..6644 18 3. ,56 18 3.56 24 3. ,45 74 3.45 77 3. ,31 41 3.30 46 3. ,15 57 3.15 62 2. ,82 5 2.82 4 2. ,63 3 2.63 3 2. ,57 5 2.58 6 - 2.54 3 2. ,41 2 2.43 2 2. ,34 5 2.32 7 2. ,29 7 2.27 1 - 2.05 2 1. ,99 1 2.00 3 1. ,93 2 1.93 2 1. ,83 15 1.83 15 1. ,78 2 1.78 2 The X-ray diffraction patterns showed that the products were crystalline. Example 6 2 g of the H-form product prepared according to the above Example 1 was added to 100 ml 0.1 M aqueous sodium carbonate solution. The mixture was stirred for 1 hour at ambient temperature. The ion-exchanged product, i.e. the 5 Na-form product, was filtered off, washed by deionized water, and dried at ambient temperature. The dried Na-form product was analyzed as described in the above Example 1. The X-ray diffraction pattern of the O dried Na-form product was practically identical to that of the Na-form product according to Example 1. These findings show that ion-exchange of the H-form into the Na-form can be carried out at mild conditions. 5 Example 7 A solution of sodium aluminate in deionized water was added to 600 g sodium silicate solution and 600 g col¬ loidal silica while stirring at 0 C to obtain a synthesis 0 mixture having the following molar composition: Si0 2 /Al 2 0 3 = 1000 a 2 0/Si0 2 = 0.12 0H/Si0 2 = 0.24 5 H 2 0/Si0 2 = 7.3 The synthesis mixture was heated in an autoclave for 5 days at autogeneous pressure and at a temperature of 130 C. 30 The product was filtered off, washed by deionized water, and dried at ambient temperature. The 'X-ray diffraction pattern of the product in its Na-form is shown in Table 11. -3.2 Table 11 d/A I/I 15.49 100 7.76 10 7.12 4 5.17 17 4.22 1 3.65 12 3.56 19 3.45 75 3.31 43 3.15 64 2.82 4 - 2.64 2 2.59 4 2.50 1 2.42 1 2.35 3 2.28 2 2.06 2 1.94 2 1.83 13 1.79 1 The X-ray diffraction pattern showed that the product was crystalline. A sample of the crystalline product was shown by chemical analysis to have a molar Si0 2 /Al 2 0 3 ratio of 944. The remaining part of the crystalline product was ion-exchanged into the H-form using an aqueous 0.1 N HCl solution at ambient temperature, washed by deionized water and dried at ambient temperature. The X-ray diffraction pattern of the product in its H-form is shown in Table 12. Table 12 d/A I/ 11.1 7 7.27 1 5.43 5 4.08 3 3.61 8 3.40 100 3.17 7 2.87 1 2.50 2 2.45 1 2.29 ' 1 2.19 1 1.85 7 1.80 1 The X-ray diffraction pattern showed that the product was crystalline. Example 8 5 g of the Na-form product prepared according to Example 7 was added to a solution of 1.67 g Al(N0 3 ) 3 .7H 2 0 in 20 g deionized water. The aqueous mixture was evaporated to dryness at 100 C and the dry product was calcined for 2 hours at 400 C to decompose the nitrate. Thereafter, the product was transferred into the H-form by ion-exchange with an aqueous 0.1 N HCl solution, washing by deionized water and drying at am¬ bient temperature. The X-ray diffraction pattern of the H-form product is shown in Table 13. Table 13 d/A I/I 10.8 7 7.27 1 5.40 8 4.09 3 3.83 1 3.57 7 3.39 100 3.18 5 2.86 1 2.49 1 2.21 1 2.17 1 1.85 7 1.79 1 The X-ray diffraction pattern showed that the product was crystalline. The molar Si0 2 / l 2 0- ratio of the product was cal¬ culated to 30.8. The product had an alpha value of 2.5. Example 9 Activity tests for methanol (MeOH) conversion into hydrocarbons (HC) were carried out on the H-form products of Examples 1 and 7 at the experimental conditions shown in Table 14. Table 13 H-form H-form Product of Product of Example 1 Example 7 T°C 380 374 P atmospheric atmospheric WHSV (MeOH) 1.0 1.0 Diluent N 2 N 2 Hours on stream 2 2 Reactor fixed bed fixed bed The reaction products were analyzed using gas chromatography. The results are summarized in Table 15. Table 15 H-form H-form Product Of Product of Example 1 Example 7 Conversion of MeOH to HC (wt%) 45 2.1 Product Analysis, wt% HC: CH 4 5.8 6.3 V 0.7 - 9.1 35.7 V 2.0 10.3 20.2 19.2 C 3- iC 4~ 4.0 - nC 4 - 1.2 13.7 14.1 14.7 43.1 - The results clearly show the effect of the amount of aluminum in the crystalline framework with respect to catalytical activity and selectivity for formation of higher hydrocarbons. Example 10 An activity test for conversion of propylen was carried out using the H-form product A of Example 3 at the experimental conditions shown in Table 16. 5 Table 16 T, °C 350 P, bar 8 O WHSV 0.75 Hours on stream 120 Reactor fixed bed The products of the experiment were analysed using 5 gas chromatography giving the results shown in Table 17. • Table 17 Propylene conversion, wt% 71 Q - Product analysis, wt%: C 4- C 5 2.3 C 6 41.6 8.9 5 C 9 36.3 c ιo "c ιι 2.3 C 12 6.2 C 13 + 2.5 0 5

Claims: What is claimed is: 1. A synthetic layered crystalline aluminosilicate having, when disregarding the presence of crystal water, the general formula expressed as moles of oxides ratios: (M 2/n°>x (Si0 2 ) y < A1 2°3>z where " M represents one or more n-valent cations TO selected from the group consisting of sodium, potassium, and any other cation capable of replacing sodium or potassium by ion-exchange, where the ratio y/z is between 15 and 300, where the ratio x/z is determined from the criterion of electron neutrality T5 between anions and cations, and in which the struc¬ tural aluminum is tetrahedrally coordinated in the crystalline framework. 2. A synthetic layered crystalline aluminosilicate 20 as claimed in claim 1 wherein the ratio y/z is between 20 and 150. 3. A synthetic layered crystalline aluminosilicate according to claim 1 wherein M is sodium and having 25 the X-ray diffraction pattern shown in Table 3. 4. A synthetic layered crystalline aluminosilicate as claimed in claim 1 wherein M is hydrogen. 30 5. A method for the preparation of a synthetic layered crystalline aluminosilicate as claimed in claim 1 from a synthesis mixture comprising at least one source of ■ aluminum and at least one source of silicon, having the composition expressed as moles 35 of oxides ratios: Si0 2 / l 2 0 3 = 5-500 M-2/,nO/SiO, 2. - 0.01-10 OH/Si0 2 = 0.1-5 H 2 0/Si0 2 = 5-200 which is maintained under such conditions that crystallization of the said synthetic crystalline aluminosilicate takes place. 6. A method for the preparation of a synthetic layered O crystalline aluminosilicate as claimed in claim 5 wherein the synthesis mixture has the composition expressed as moles of oxides ratios: 0 H 2 0/Si0 2 = 5-75 7. A method for the preparation of a synthetic layered 0 crystalline aluminosilicate as claimed m claim 5 wherein the synthesis mixture is held under auto¬ ggeenneeoouuss pprreessssuurree aatt aa tteemmppeerraattiure of 80-270 C for a period of 4 hours to 100 days. 5 A method for the preparation of a synthetic layered crystalline aluminosilicate as claimed in claim 5 wherein the synthesis mixture is held under auto¬ geneous pressure at a temperature of 95-160 C for a period of 10 hours to 30 days. 0 A method for the preparation of a synthetic layered crystalline aluminosilicate as claimed in claim 5 wherein M is sodium or potassium. 5 10. A method for the preparation of a synthetic layered crystalline aluminosilicate as claimed in claim 5 wherein M is hydrogen by ion-exchange of a synthetic layered crystalline aluminosilicate as claimed in claim 9. 11. A process for the synthesis of higher hydrocarbons from a raw material comprising lower olefins or oxygenates in the presence of a catalyst contain¬ ing a synthetic layered crystalline aluminosilicate TO having, when disregarding the presence of crystal water, the general formula expressed as moles of oxides ratios: T5 (M 2/n 0) x : {SiC Vy : where M represents one or more n-valent cations selected from the group consisting of sodium, potassium, and any other cation capable of replacing sodium or potassium by ion-exchange, where the ratio 20 y/z is between 15 and 300, where the ratio x/z is determined from the criterion of electron neutrality between anions and cations, and in which the struc¬ tural aluminum is tetrahedrally coordinated in the crystalline framework. 25 12. A process for the synthesis of higher hydrocarbons as claimed in claim 11 wherein the synthetic layered crystalline aluminosilicate is prepared by a method as claimed in claim 5. 30 35

Inventors: BLOM NIELS JOERGEN, BLOM, NIELS, JOERGEN
Applicants: TOPSOE HALDOR AS, HALDOR TOPSOEE A/S
Application year: 1987
Main classification: B01J29
IPC codes: B01J21, B01J29, C01B33, C07C15