METHOD OF PRODUCING AN OPTICAL RECORDING CARD AND TRANSFER TYPE OPTICAL RECORDING MEDIUM

Abstract: An optical recording card is produced using a transfer type optical recording medium. The transfer type optical recording medium comprises a base film, a peeling layer, an optical recording layer and a light pearmeable adhesive layer which are successively superimposed one above another to constitute a layered structure. A protective layer is adhered to the transfer type optical recording medium with the aid of an adhesive layer and the base film is then peeled off together with the peeling layer. Next, the protective layer to which the optical recording layer is adhered is adhesively attached to a card base in such a manner that the optical recording layer is interposed therebetween whereby an optical recording card is completely produced. The transfer type recording medium can be preserved in such a state that it is wound about a reel. Accordingly, the transfer type recording medium is adhered to the protective layer when the optical recording card is produced, and thereafter it is adhered to the card base. Thus, the optical recording card can be produced at a high productive efficiency.

Description: BACKGROUND OF THE INVENTION The present invention relates to a method of producing an optical recording card and a transfer type optical recording medium employable for carrying out the method. In the recent years a number of cards in which various kinds of information are recorded are increasingly put in practical used as ID card, cash card or bank card. DESCRIPTION OF THE PRIOR ART This kind of card is required to record various kinds of informations such as data concerning individual person, data concerning a company from which the card is issued or the like data. In the earier age such informations were recorded using visual characters and symbols and in the later age they were recorded in response to electrical signals which were generated magnetically. However, due to rapid increase in number of card the conventional card is not in position to take adequate measures for preventing data from being falsified and moreover for the current tendency of increased volume of informations. In view of the current situation as mentioned above a card including an optical recording layer to which the latest optical technology is applied to record informations has been developed in the recent years. This kind of card is called optical recording card. A hitherto proposed optical recording card 1 has a basic structure as shown in Figs. 1 and 2. Specifically, it includes an optical recording layer 4 which is interposed between a card base 2 and a transparent protective layer 3 made of transparent plastics and optical reading is carried out from the side of the protective layer 3. It should be noted that in Fig. 2 an adhesive layer is omitted. The optical recording layer 4 comprises an optical reflective layer which has optical reflection faces on which a number of data pits are formed. Reading is achieved with the use of laser beam 9 by detecting data pits each of which has a different optical reflectivity. In order to produce optical recording cards as mentioned above a variety of technologies have been developed and in the recent years a method of producing optical recording cards with the use of transfer technique has been proposed from the viewpoint of facilitating production of optical recording cards. An example of production technique for producing optical card with the aid of transfer technique is shown in Fig. 9 and a transfer type optical recording medium is used for practicing the production technique. Specifically, a transfer type optical recording medium 101 comprises a base film 102, a peeling layer 103, a transparent protective layer 3 made of transparent synthetic resin, an optical recording layer 4 and an adhesive layer 104 which are successively superimposed one above another. When an optical card is produced using-the transfer type optical recording medium 101, the base film 102 is peeled off together with the parting layer and a card base 2 is adhesively secured to the transfer type optical recording medium 101 to achieve thermal transfer on necessary part, as shown in Fig. 10. Thus, an optical recording card 100 as shown in Fig. 11 is produced. A method of producing an optical recording card as mentioned above is a known technique as disclosed in an official gazette of Japanese laid-open patent (official gazette of Japanese Laid-Open Patent NO. 58894/1986 issued on the day of April 5, 1985). This matter is also described in Patent Abstracts of Japan, Vol. 9, no. 194 (M-403) [1917] 10/8/1985. The protective layer 3 of the transfer type optical recording medium 101 used for practicing the above-mentioned prior method of producing a conventional optical recording card constitutes an upper layer of the optical recording card 100 in order to protect the optical recording layer 4 from damage or injury and moreover reduce a rate of occurrence of error during data reading. Accordingly, the protective layer 3 is constructed by hard material having a thickness of about 400 microns. However, the fact that the protective layer 3 is constructed by thick and hard material makes it difficult to produce the transfer type optical recording medium 101 in tape-shape which can be wound about a reel. This means that it is inconvenient to handle the transfer type optical recording medium 101 when an optical card is produced. Further, since the protective layer 3 has a heavy thickness, there is a fear that it is deformed under the effect of heat during thermal transfer and its surface loses smoothness. This leads to a cause that a rate of occurrence of error during data reading increases. Since laser beam is adapted to pass through the protective layer when data is written in the optical recording layer or data written in the optical recording layer is read, damaged or injured protective layer or contaminated protective layer causes S/N ratio to be reduced. SUMMARY OF THE INVENTION Thus, the present invention has been made with the foregoing background in mind. A first object of the present invention is to provide a method of producing an optical recording card which assures that the optical card is produced at a higher production efficiency and at an inexpensive cost. A second object of the present invention is to provide a transfer type optical recording medium usable for practicing the method of producing an optical recording card wherein the transfer type optical recording medium can assume tape-shape to be wound around a reel and moreover it is simple to be handled during a step of producing. A third object of the present invention is to provide a method of producing an optical recording card wherein the protective layer of the optical recording card is not deformed under the effect of heat, thus it has an excellent flatness and reading of data is achieved at a low rate of occurrence of error. Accordingly, the invention provides a method of producing an optical recording card, in which a transfer type optical recording medium comprises a base film, a peeling layer, an optical recording layer and a light permeable adhesive layer successively superimposed one above another, and said optical recording layer is applied to an optical recording card by said adhesive layer, characterised in that the method comprises the steps of; adhering said transfer type optical recording medium to one surface of a protective layer of said optical recording card by the use of said adhesive layer; removing said base film from said transfer type optical recording medium by peeling operation, and then adhering a card base of said optical recording card to said optical recording layer being adhered to said protective layer. The invention also provides a transfer type optical recording medium comprising a base film, peeling layer, an optical recording layer and a light permeable adhesive layer which are successively superimposed one above another to constitute a layered structure, characterised in that said optical recording layer is sandwiched between said adhesive layer and said peeling layer. The present invention will become readily apparent from reading of the following description which has been prepared in conjunction with the accompanying drawings. BRIEF DESCRIPTION OF THE DRAWINGS The present invention will be illustrated in the following drawings; in which Fig. 1 is an illustrative perspective view of an optical recording card. Fig. 2 is a schematic vertical sectional view of the optical recording card. Fig. 3 is a schematic vertical sectional view of a transfer type optical recording medium. Fig. 4 is a series of vertical sectional views illustrating an example of process of producing a transfer type optical recording medium. Fig. 5 is a series of vertical sectional views illustrating other example of process of producing a transfer type optical recording medium. Fig. 6 is a series of vertical sectional views illustrating another example of process of producing a transfer type optical recording medium. Fig. 7 is a fragmental enlarged vertical sectional view of a transfer type optical recording medium, particularly illustrating that the base film is peeled off. Fig. 8 is a fragmental enlarged vertical sectional view of an optical recording card. Fig. 9 is a schematic vertical sectional view illustrating a conventional transfer type optical recording medium. Fig. 10 is a fragmental enlarged vertical sectional view of the conventional transfer type optical recording medium, particularly illustrating that the base film is peeled off, and Fig. 11 is a schematic vertical sectional view of a conventional optical recording card. DESCRIPTION OF THE PREFERRED EMBODIMENTS Now, the present invention will be described in a greater detail hereunder with reference to the accompanying drawings which illustrate a preferred embodiment thereof. First, description will be made as to transfer type optical recording medium which is employed for practicing the method of producing an optical recording card in accordance with the invention. In Fig. 3 reference numeral 11 designates a transfer type optical recording medium. Specifically, the transfer type optical recording medium is constituted in such a manner that a peeling layer 13 is formed on the base film 12 by employing a peeling process, an optical recording layer 4 is formed on the peeling layer 13 and an adhesive layer 14 is then formed on the optical recording layer 4. The base film 12 is constructed by polycarbonate, polyethyleneterephthalate, polyimide, polyamide, polysulfon, polyethersulfon, polyetherketon, polyetheretherketon or polyetherimide and has a thickness in the range of 5 to 100 µm (microns), preferably in the range of 10 to 50 µm (microns). Next, the optical recording layer 4 is constructed by superimposing the optical reflective layer on a pattern support layer. The optical recording layer 4 is formed on the peeling layer 13 and has an optical reflective layer 15 which includes a number of data pits which can be read (see Figs. 3, 4 and 5). The optical recording layer 4 is so formed that data are recorded in dependence on existence of the readable optical reflective layer 15 or not or by generating phase difference of reading light due to provision of ruggedness on the optical reflective layer 15. The pattern support layer is constructed by acryl-based resin, vinyl-based resin, cellulose-based resin, polyester-based resin, polyurethane-based resin, epoxy-based resin, alkyd-based resin or amino-based resin and has a thickness in the range of 0.5 to 100 µm (microns), preferably in the range of 1 to 50 µm (microns). Generally, the pattern support layer is formed by roll coating or the like process. The optical reflective layer has a thickness in the range of 5 x 10⁻³ to 0.2 µm (50 to 2000 Å) and is constructed by metallic material such as Te, Bi, In, Pb, Sn, Sb, Zn, Se, Cd, Ga, Ag, Au, Cu, Cr, Al or their alloy, or has a thickness in the range of 10⁻² to 10 µm (100 Å to 10 microns) and is constructed by organic and/or inorganic compound material such as Te - C, Te - CS₂, Bi - CS₂, Te - teflon, Ag - gelatine or the like or multi-layer film such as Te - dyestuff, Te - nitro cellulose, matellic film - dielectric film or the like, or has a thickness in the range of 10⁻² to 10 µm (100 Å to 10 microns) and is constructed by dyestuff film such as cyanine dye, phthalocyanine, naphtoquinone dye or has a thickness in the range of 10⁻² to 10 µm (100 Å to 10 microns) and is constructed by compound material of organic material and dye such as nitrocellulose styrene, acetic acid vinyl, gelatine or the like and dyestuff, sub-oxide such as TeOx, GeOx, SbOx, MoOx or the like, layered material of metallic material and organic material such as AuPt - (PS, PMMA PVAC or the like), Al-teflon or the like or magnetic film material such as MnCuBi, CdCo, TbCo, TbFe, GdTbFe, TbFeCo or the like. It should be noted that in order to form the optical reflective layer, a technique suitable for producing a film is employable in consideration of the kind of the optical recording material. With respect to reading light visual light such as near-infrared, white light, tungsten light or the like is preferable. Alternatively, infrared or ultraviolet may be employed. The adhesive layer 14 is formed by coating transparent synthetic resin adhesive on the optical recording layer 4 by employing roll coat, flow coat or the like and then drying it. The adhesive layer 14 is constructed by copolymer of polychloride vinyl - acetic acid vinyl, polyurethane resin, polyester resin or the like transparent thermoplastic resin. The peeling layer 13 is formed by employing flow coat, gravure coat or the like and it is constructed by silicone resine, silicone oil, acryl-based resin, cellulose-based resin or vinyl-based resin and has a thickness less than one micron. Next, description will be made below as to a method of producing transfer type optical recording medium with referenece to Figs. 4 to 6. Fig. 4 illustrates a plurality of steps of producing transfer type otpical recording medium 11a in the case where the optical recording layer 4 is formed by a stamping method. Specifically, the upper surface of the base film 12 is subjected to peeling process to form a peeling layer 13 (a step of peeling treatment) (see Fig. 4(a)). Next, a shaping resin layer 17 is formed on the peeling layer 13 by coating UV hardened resin or the like on the peeling layer 13 (a step of coating shaping resin ) (see Fig. (b)). This shaping resin layer 17 can serve as a peeling layer. In this case the step of peeling treatment layer 17 as shown in Fig. 4(a) is not required. Next, a stamper 18 which is previously formed with a rugged pattern of the optical recording layer is pressed on the shaping resin layer 17 whereby the rugged configuration of the stamper 18 is transferred onto the shaping resin layer 17 and the latter is caused to harden (a step of shaping) (see Fig. 4(c)). Next, a reflective film 21 is formed by vacuum depositing on the shaping resin layer 17 metallic material having high reflectivity such as aluminum or the like. The thus formed reflective film 21 has the same ruggedness as the stamper 18 and phase difference of reflected light is produced in accordance with difference in position between projected portion and recessed portion whereby required informations can be read optically (a step of coatlng the reflective layer) (see a step 4(d)). Next, an adhesive layer 14 is formed on by coating transparent adhesive on the reflective film 21 (a step of coating an adhesive) (see Fig. 4(e)). A transfer type optical recording medium 11a is produced by way of the steps as mentioned above. Fig. 5 illustrates a plurality of steps of producing transfer type optical recording medium 11b in the case where the optical recording layer 4 is formed by an etching method. Specifically, the upper surface of the base film 12 is subjected to peeling process to form a peeling layer 13 (a step of peeling treatment) (see Fig. 5(a)). Next, an optical pattern support layer 22 comprising a resin having high light absorptivity or high pearmeability relative to reading light is formed on the peeling layer 13 (a step of forming an optical information support layer) (see Fig. 5(b)). The optical pattern support layer 22 serves to support a reflective film 21 which has shortage in mechanical strength by itself and increases smoothness of the reflective film 21. Further, it is possible to have high absorptivity or high pearmeability relative to reading light. Further, by increasing adhesiveness between the reflective film 21 and the optical information pattern support layer 22 it becomes easier to carry out writing (in the form of etching or the like). Generally, the etching process or a resist lift-off process to be described later is practiced by utilizing the portion where a reflective film is existent and the portion where any reflective film is not existent as data. Thus, to assure increased S/N it is necessary that contrast is enlarged. Accordingly, it is required that the support layer has high absorptivity or high pearmeability relative to reading light. It should be noted that the optical information pattern support layer 22 can have a function as peeling layer. In this case the step of peeling treatment as shown in Fig. 5(a) is not required. Next, a reflective film 21 comprising metallic material having high reflectivity relative to reading light is formed on the optical information pattern support layer 22 by vacuum depositing or the like process (a step of coating a reflective film) (Fig. 5(c)). Next, resist 23 is coated on the reflective film 21 by roll coating (a step of coating resist) (Fig. 5(d)). The resist 23 may be either of positive type or of negative type. Next, a mask 24 having a pattern representive of optical information is placed on the resist 23 in close contact therewith and it is exposed to light beam (a step of allowing the mask to be exposed to light beam) (Fig. 5(e)). Next, the thus exposed resist 23 is developed. This enables the optical information pattern to be transferred to the resits 23 whereby a rugged configuration corresponding to the optical informations is produced on the resist 23. The recessed part has no resist due to removal of the latter, causing the surface of the reflective film 21 to be exposed to the outside but the residual part of the reflective film 21 is coated still with the resist 23 (a step of developing) (see Fig. 5(f)). Next, the reflective film 21 is subjected to etching from the above of the resist 23. This leads to a result that the part of the reflective film 21 which is not coated with the resist 23 is removed and thereby the surface of the optical information pattern support layer 22 is exposed to the outside whereas the part of the reflective film 21 which is coated with resist 23 resides on the surface of the optical informations pattern support layers 22 with the resist while maintaining the vacuum deposited state (a step of etching) (see Fig. 5(g)). Next, the residual reisst is removed (a step of removal) (see Fig. 5(h)). Next, transparent adhesive is coated from the above of the optical reflective layer 15 including the residual reflective films 21 to constitute an adhesive layer 14 (a step of coating an adhesive) (see Fig. 5(i)). Thus, a transfer type optical recording medium 11b is obtained. Fig. 6 illustrates a plurality of steps of producing transfer type optical recording medium 11c in the case where the optical recording layer 4 is formed in accordance with the resis lift-off process. Specifically, the upper surface of the base film 12 is subjected to peeling process to form a peeling layer 13 (a step of peeling treatment) (see Fig. 6(a)). Next, an optical information pattern support layer 22 comprising a resin having high light absorptivity or high pearmeability relative to reading light is formed on the peeling layer 13 (a step of forming an optical information support layer) (see Fig. 6 (b)). The optical information pattern support layer 22 can serve as a peeling layer. In this case the step of peeling as shown in Fig. 6(a) is not required. Next, resist is placed on the optical information pattern support layer 22 by employing a spin coating process (a step of resist coating) (see Fig. 6(c)). The resist 23 may be either of positive type or of negative type. Next, a mask 24 having a pattern representative of optical informations is placed on the resist 23 in close contact therewith and it is then exposed to light beam (a step of allowing the mask to be exposed to light beam) (see Fig. 6(d)). Next, the thus exposed resist 23 is developed. This enables the optical information pattern to be transferred to the resist 23 whereby a rugged configuration corresponding to the optical informations is produced on the resist 23. The recessed part has no resist due to removal of the latter, causing the surface of the optical information pattern support layer 22 to exposed to the outside but the residual part of the optical information pattern support layer 22 is coated still with the resist 23 (a step of developing) (see Fig. 6(e)). Next, a reflective film 21 comprising metallic material having high reflectivity relative to light is formed on the resist 23 by vacuum depositing (a step of coating a reflective film) (see Fig. 6 (f)). Next, the resist 23 is removed by a lift-off process. Thus, the part of the reflective film 21 located on the resist 23 is removed together with the resist 23 whereby the surface of the optical information pattern support layer 22 becomes exposed to the outside. On the other hand, the part of the reflective film 21 which is not located on the resist 23 resides in such a state that it is vacuum deposited on the surface of the optical information pattern support layer 22 whereby an optical reflective layer 15 is built (a step of lift-off) (see Fig. 6(g)). Next, transparent adhesive is coated from the above of the residual reflective film 21 (optical reflective layer 15) to form an adhesive layer 14 (a step of coating an adhesive) (see Fig. (h)). A transfer type optical recording medium 11c is produced by way of the steps as mentioned above. Incidentally, the optical information pattern as mentioned above may be either preformatting pit pattern or data pit pattern. Next, description will be made below as to a method of producing an optical recording card using a transfer type optical recording medium 11 (11a, 11b, 11c) which is constructed in the above-described manner. First, as shown in Fig. 7, a protective layer 3 comprising plastics or the like having high pearmeability such as polycarbonate or the like is previously provided and a transfer type optical recording medium 11 is superimposed one above another with an adhesive layer 14 superimposed therebetween. Thereafter, heat and pressure are applied to the thus superimposed structure so as to allow the protective layer 3 and the transfer type optical recording medium 11 to be adhesively connected to one another and after completion of adhesive connection the base film 12 is peeled off together with the peeling layer 13. Alternatively, the protective layer 3 may be adhesively superimposed on the transfer type optical recording medium 11 after the peeling layer 13 is peeled off from the latter. When the base film 12 is peeled off, the peeling layer 13 may be located on the base film 12 or it may reside on the optical information pattern support layer 22. The thus obtained superimposed structure comprising the optical recording layer 4 and the protective layer 3 is further superimposed in a card base 2 in such a manner that the optical recording layer 4 and an adhesive layer 25 are interposed therebetween. Thus, an optical recording card 1 as shown in Fig. 8 is obtained. (Example) As a protective layer polycarbonate having a thickness of 0.5 mm was used, while as a card base white and hard polyvinylchloride having a thickness of 0.25 mm of which adhesive surface was coated with urethane-based adhesive having a thickness of 5 microns was used. A transfer type optical recording medium was temporarily attached to a protective layer using a hot plate made of metallic material, rubber board, rubber roll or the like each of which was heated to about 100 °C. It should be noted that at this moment only slight pressing force was required to such an extent that the transfer type optical recording medium was temporarily secured to the protective layer and therefore it was not required that the former was fixedly secured to the latter. After completion of temporal adhesive secuing the base film was peeled off. The protective layer and the card base were thermally adhered to one another in such a manner that they were clamped between mirror surface plates. At this moment the optical recording layer was interposed between the protective layer and the card base. Thermal adhering was achieved at pressure of 30 Kg/cm² and temperature of 110 °C for a period of time of 10 minutes. Thereafter, heating was interrrupted and cooling was effected for a period of time of 15 minutes using water. Finally, the material was cut to dimensions corresponding to a card. Thus, a required card was obtained. Advantageous Effects of the Invention The present invention offers the following advantageous effects. According to the method of producing an optical recording card using a transfer type optical recording medium as constructed in the above-described manner it is possible to attach the optical recording medium to a card by transfering operation. In consequence, producing of the optical recording card can be effected at a high productive efficiency. Since the peeling layer of the base film is located opposite to the reading side of the optical recording layer, it is assured that residual foreign material relative to the peeling layer does not hinder entrance and reflection of reading light and no contamination takes place due to adherence of dust or the like to the residual foreign material of the peeling layer. Further, since the transfer type optical recording medium of the invention does not have any hard and thick protective layer, it is possible to form the transfer type optical recording medium in tape-shape. This means that the transfer type optical recording medium can be wound about a reel. Therefore, it is easy to handle the transfer type optical recording medium during a step of producing an optical recording card. Further, since the protective layer can be reserved or treated separately from the transfer type optical recording medium, there is no fear of injuring or degrading the protective layer with the result that an optical recording card can be obtained with a rate of occurrance of error during data reading being minimized. Since a transfer type optical recording medium can be preserved at all time regardless of how a thickness of the protective layer differs from product to product, all that is required is to adhere it to a protective layer having a predetermined thickness in response to the specification of a product. Accordingly, a countermeasure against change in thickness of the protective layer of a product can be taken quickly. Further, in the case where a protective layer has the same size as a card base and a transfer type optical recording medium is prepared smaller than the protective layer, it is very easily achieved by preparing the transfer type optical recording medium separately from the protective layer in accordance with the present invention that an optical recording layer is kept in a closely sealed state within the optical recording card while the protective layer and the card base are fused together along the peripheral part of the optical recording card. Thus, it is possible to prevent the optical recording layer from being oxidized or deteriorated under the influence of outside atmosphere by holding the optical recording layer between the protective layer and the card base in a closely sealed state. Moreover, it is possible to prevent an occurrence of peeling off from the card edge portion.

Claims: A method of producing an optical recording card (1), in which a transfer type optical recording medium (11,11a,11b,11c) comprises a base film (12), a peeling layer (13), an optical recording layer (4) and an adhesive layer (14) successively superimposed one above another, and said optical recording layer (4) is applied to an optical recording card by said adhesive layer (14), and said adhesive layer (14) is light permeable, characterised in that the method comprises the steps of; adhering said transfer type optical recording medium (11,11a,11b,11c) to one surface of a protective layer (3) of said optical recording card (1) by the use of said adhesive layer (14); removing said base film (12) from said transfer type optical recording medium (11,11a,11b,11c) by peeling operation, and then adhering a card base (2) of said optical recording card (1) to said optical recording layer (4) being adhered to said protective layer (3). A method as claimed in claim 1, wherein the optical recording layer (4) is so constructed that an optical reflective layer (15) is superimposed on a pattern support layer (22). A method as claimed in claim 2, wherein said pattern support layer (22) is constructed from an acryl-based resin, vinyl-based resin, cellulosed-based resin, polyester-based resin, polyurethane-based resin, epoxy-based resin, alkyd-based resin or amino-based resin and has a thickness in the range of 0.5 to 100 µm (microns), preferably in the range of 1 to 50 µm (microns). A method as claimed in claim 2 or 3, wherein said optical reflective layer (15) either has a thickness in the range of 5 x 10⁻³ to 0.2 µm (50 to 2000 Å) and is constructed from metallic material such as Te, Bi, In, Pb, Sn, Sb, Zn, Se, Cd, Ga, Ag, Au, Cu, Cr, Al or the like or alloys thereof, or has a thickness in the range of 10⁻² to 10 µm (100 Å to 10 microns) and is constructed by a compound material of organic and/or inorganic material such as Te - C, Te - CS₂, bi - CS₂, Te - teflon, Ag - gelatine, or a multilayer film such as Te - dyestuff, Te - nitrocellulose metallic material film - dielectric material film or the like, or has a thickness in the range of 10⁻² to 10 µm (100 Å to 10 microns) and is constructed from a dyestuff film such as cyanine dye, phthalocyanine, naphtoquinone dye or the like or has a thickness in the range of 10⁻² to 10 µm (100 Å to 10 microns) and is constructed from compound material of organic material such as nitrocellulose styrene, acetic acid vinyl, gelatine or the like and dyestuff, or sub-oxide such as TeOx, GeOx, SbOx, MoOx or the like, or layered material of metallic material and organic material such as AuPt - (PS, PMMA, PVAC or the like), Al - teflon or magnetic film material such as MnCuBi, CdCo, TbCo, TbFe, GdTbFe, TbFeCo or the like. A method as claimed in any preceding claim, wherein said base film (12) is constituted by polycarbonate, polyethyleneterephthalate, polyimide, polyamide, polysulfone, polyethersulfone, polyetherketon, polyetheretherketon or polyetherimide and has a thickness in the range of 5 to 100 µm (microns), preferably in the range of 10 to 50 µm (microns). A method as claimed in any preceding claim, wherein said adhesive layer is constructed from transparent thermoplastic resin such as vinyl choride - acetic acid copolymer, polyurethane resin, polyester resin or the like. A method as claimed in any preceding claim, wherein said peeling layer (13) is constructed from silicone-based resin, silicone oil, acryl-based resin, cellulose-based resin or vinyl-based resin and has a thickness less than 1 µm (one micron). A method as claimed in any preceding claim, wherein said protective layer is contructed from plastics material of high light permeability such as polycarbonate or the like. A transfer type optical recording medium (11,11a,11b,11c) comprising a base film (12), peeling layer (13), an optical recording layer (4) and an adhesive layer (14) which are successively superimposed one above another to constitute a layered structure, wherein said adhesive layer (14) is light permeable; characterised in that said optical recording layer (4) is sandwiched between said adhesive layer (14) and said peeling layer (13). A transfer type optical recording medium as claimed in claim 9, wherein the optical recording layer (4) is so constructed that an optical reflective layer (15) is superimposed on a pattern support layer (22). A transfer type recording medium as claimed in claim 10, wherein said pattern support layer (22) is constructed from an acryl-based resin, vinyl-based resin, cellulosed-based resin, polyester-based resin, polyurethane-based resin, epoxy-based resin, alkyd-based resin or amino-based resin and has a thickness in the range of 0.5 to 100 µm (microns), preferably in the range of 1 to 50 µm (microns). A transfer type recording medium as claimed in claim 10 or 11, wherein said optical reflective layer (15) either has a thickness in the range of 5 x 10⁻³ to 0.2 µm (50 to 2000 Å) and is constructed from metallic material such as Te, Bi, In, Pb, Sn, Sb, Zn, Se, Cd, Ga, Ag, Au, Cu, Cr, Al or the like or alloys thereof, or has a thickness in the range of 10⁻² to 10 µm (100 Å to 10 microns) and is constructed by a compound material of organic and/or inorganic material such as Te - C, Te - CS₂, bi - CS₂, Te - teflon, Ag - gelatine, or a multilayer film such as Te - dyestuff, Te - nitrocellulose metallic material film - dielectric material film or the like, or has a thickness in the range of 10⁻² to 10 µm (100 Å to 10 microns) and is constructed from a dyestuff film such as cyanine dye, phthalocyanine, naphtoquinone dye or the like or has a thickness in the range of 10⁻² to 10 µm (100 Å to 10 microns) and is constructed from compound material of organic material such as nitrocellulose styrene, acetic acid vinyl, gelatine or the like and dyestuff, or sub-oxide such as TeOx, GeOx, SbOx, MoOx or the like, or layered material of metallic material and organic material such as AuPt - (PS, PMMA, PVAC or the like), Al - teflon or magnetic film material such as MnCuBi, CdCo, TbCo, TbFe, GdTbFe, TbFeCo or the like. A transfer type recording medium as claimed in any of claims 9 to 12 wherein said base film (12) is constituted by polycarbonate, polyethyleneterephthalate polyimide, polyamide, polysulfone, polyethersulfone, polyetherketon, polyetheretherketon or polyetherimide and has a thickness in the range of 5 to 100 µm (microns), preferably in the range of 10 to 50 µm (microns). A transfer type recording medium as claimed in any of claims 9 to 13, wherein said adhesive layer is constructed from transparent thermoplastic resin such as vinyl choride - acetic acid copolymer, polyurethane resin, polyester resin or the like. A transfer type recording medium as claimed in any of claims 9 to 14, wherein said peeling layer (13) is constructed from silicone-based resin, silicone oil, acryl-based resin, cellulose-based resin or vinyl-based resin and has a thickness less than 1 µm (one micron).

Inventors: FUJITA, MINORU, FUKUSHIMA, YOICHI, HAGA, TOSHIO
Applicants: KYODO PRINTING CO., LTD.
Application year: 1987
Main classification: G06K19
IPC codes: B42D15, G11B7, G06K19