Method for preparing n-sulfomethyl acrylamide, acrylic acid terpolymers from polyacrylonitrile

Abstract: N-sulfomethyl acrylamide, acrylamide, acrylic acid terpolymers are prepared by a method characterized by reacting polyacrylonitrile, water and sodium formaldehyde bisulfite at a temperature of at least 100°C.

Description: This invention relates generally to the preparation of terpolymers and, more particularly, to a method for preparing N-sulfomethyl acrylamide, acrylamide, acrylic acid terpolymers from polyacrylonitrile. It is known that polyacrylamide can have a portion or all of its amide groups converted to N-sulfomethyl amide groups by reacting polyacrylamide with sodium formaldehyde bisulfite to sulfomethylate the amide group. This chemistry has been generally described in the article entitled "Ionic Derivative of Polyacrylamide" taken from the publication Industrial and Engineering Chemistry, December, 1956, by A. M. Schiller and T. J. Suen. USSR Inventor's Certificate 724 523 discloses high molecular weight compositions which are the product of the polymerisation of acrylonitrile. The polyacrylonitrile is disclosed as being hydrolyzed when formaldehyde and sodium bisulfate are added and the solution is subjected to temperatures ranging from 90-96°C. U. S. Patent No. 3,979,348 discloses an improved method for producing cationic and anionic acrylamide polymers through the reaction of formaldehyde-secondary amine or formaldehyde-sulfurous acid adduct with finely divided acrylamide in water-in-oil emulsions. The resulting products are disclosed as being easily inverted into aqueous solutions. Recent developments have shown that the sulfomethylation reaction does not occur unless the temperature of the reaction between the polyacrylamide and sodium formaldehyde bisulfite is at least 100°C. One of the drawbacks of preparing the N-sulfomethylated acrylamide polymer is that is requires the use of polyacrylamide as a starting material. If it were possible to prepare N-sulfomethylated polymers without necessitating the use of polyacrylamide as a starting polymer but rather an inexpensive polymer, e.g. polyacrylonitrile, an advance in the art would be afforded. The present invention provides for a method for preparing N-sulfomethyl acrylamide, acrylamide, acrylic acid terpolymers from polyacrylonitrile characterized by reacting the reactants polyacrylonitrile, water and sodium formaldehyde bisulfite at a temperature ranging from 125°-250°C for a period of time sufficient to convert the reactants to an N-sulfomethyl acrylamide, acrylamide, acrylic acid terpolymer and then recovering this terpolymer. In the practice of the invention the N-sulfomethyl acrylamide copolymers may be prepared from polyacrylonitrile via a one- or two-step reaction: A. One-step reaction : A mixture of polyacrylonitrile and sodium formaldehyde bisulfite in water with or without a catalyst (e.g., NH₄OH or a catalytic metal such as copper) is heated up to 200°C until a desired degree of conversion is obtained; B. Two-step reaction : Polyacrylonitrile is first hydrolyzed with or without a catalyst at a temperature up to 200°C. the hydrolyzed polyacrylonitrile is sulfomethylated with NaHSO₃-HCHO at 150°C. The starting polyacrylonitrile should have a molecular weight within the range of at least 1,000-500,000, with a preferred molecular weight range being 3,000-200,000. Polymers within this molecular weight range readily undergo the reactions described herein and produce a finished polymer having a variety of industrial uses such as scale control agents for cooling towers and boilers and dispersants for a variety of aqueous suspensions. It is also beneficial that the surface area of the polyacrylonitrile be sufficiently large so as to increase the reaction rate. Therefore fine particles e.g. in the particle size range of a few microns or less, facilitate the speed and completeness of the reaction. The amount of water may vary although it is necessary that sufficient water be provided in the reaction mixture to furnish at a minimum at least 0.5 mols per mol of nitrile groups present in the starting polymer. A general range is 0.5-55 mols. Generally the amount of water is not critical since it is beneficial that a large excess of water be present to allow for the polyacrylonitrile-water mixture to be reacted in the form of a slurry. The temperature at which the amide groups are formed during the reactions or converted to the N-sulfomethylamide groups must be within the range of 125-250°C. A preferred temperature is 150°C. When polyacrylonitrile is reacted with water at either acid or basic pH's, there is formed a copolymer of acrylamide and acrylic acid. Depending on the pH and the reaction temperature, the ratio of acrylic acid to acrylamide groups may be varied. It is preferred to conduct the reaction at a pH greater than 8. The reaction procedure whereby the polyacrylonitrile is reacted with a metal catalyst capable of converting nitrile groups in the presence of water to amide groups uses catalysts which are well-known and described in detail in cols. 2 and 3 of U.S. Patent 3,997,606. Metallic copper catalysts are preferred with a most preferred catalyst being a special Raney copper catalyst which contains from about 2 to 45% by weight of aluminum. This catalyst in its preferred embodiment contains particles having an average particle diameter ranging from 0.01 to 1.27 cm (0.002 to 0.5 inches) and has a relative activity of at least about 2. Catalysts of this type as well as their method of preparation are disclosed in U.S. Patent 3,920,740. The molecular weight of the finished polymer will generally correspond with a molecular weight of the starting polyacrylonitrile. The sodium formaldehyde bisulfite is formed when formaldehyde and sodium bisulfite are added to water. This reaction is almost instantaneous. In practicing the processes of the invention, the sodium formaldehyde bisulfite can be added either as a pre-prepared solution or the formaldehyde and the bisulfite can be added separately. The amount of the sodium formaldehyde bisulfite should be sufficient to react with at least 5% if the nitrile groups present in the starting polymers in amounts ranging between 5-15% or more are preferred. To illustrate the invention, a variety of polyacrylonitrile polymers were subjected to the reaction conditions described above. The results are set forth in Table I.

Claims: A method for preparing N-sulfomethyl acrylamide, acrylamide, acrylic acid terpolymers from polyacrylonitrile characterized by reacting the reactants polyacrylonitrile, water and sodium formaldehyde bisulfite at a temperature ranging from 125°-250°C for a period of time sufficient to convert the reactants to an N-sulfomethyl acrylamide, acrylamide, acrylic acid terpolymer and then recovering this terpolymer. The method of claim 1, characterized in that the polyacrylonitrile is first reacted with a metal-containing catalyst capable of converting a portion of the nitrile groups of the polyacrylonitrile to amide groups and then reacting said polymer with sodium formaldehyde bisulfite to convert a portion of the acrylamide groups into N-sulfomethyl acrylonitrile groups thereby producing an N-sulfomethyl acrylamide, acrylamide, acrylic acid terpolymer. The method of claims 1 or 2, characterized in that the molecular weight of the starting polyacrylonitrile is between 1,000-500,000. The method of claim 3, characterized in that the molecular weight is between 3,000-200,000.

Inventors: FONG DODD WING, VALLINO BARNEY JR, FONG, DODD WING, VALLINO, BARNEY, JR.
Applicants: NALCO CHEMICAL CO, NALCO CHEMICAL COMPANY
Application year: 1987
Main classification: C08F8
IPC codes: C08F8