A METHOD FOR BONDING A LAYER CONTAINING A REFRACTORY METAL TO A SUBSTRATE

Abstract: A method for fabricating a structure, which includes a layer (2) containing a refractory metal and a substrate (3) to which the refractory metal-containing layer does not strongly adhere, there being a thin bonding layer (5) between the substrate (3) and the refractory metal-­ containing layer (2) for providing good adherence between the refractory metal-containing layer and the substrate. The bonding layer (5) is an oxide, nitride or mixed osy-nitride layer initially prepared to be Si-rich in a surface region thereof. Inclusions (7) of the refractory metal are produced in the bonding layer (5) by substitu­ ting the refractory metal for excess free silicon (6) therein. These inclusions become nucleation and bonding sites for refractory metal deposition, ensuring good adhesion.

Description: This invention relates to a method for forming a structure, wherein a refractory metal or refractory metal silicide will strongly adhere to a substrate to which it will not normally adhere well, and more particularly to the use of a specially fabricated bonding layer between the refractory metal and the substrate, in order to ensure strong adhesion therebetween. In the microelectronics industry, it is often desirable to deposit metal layers, such as refractory metals, onto substrates such as glasses, etc. The metal layers are used for several purposes including interconnection metallurgy and contacts. However, it has often been difficult, or impossible, to deposit metal layers which will strongly adhere to the substrates. In particular, it has been difficult to adhere refractory metal layers such as tungsten to dielectric layers, such as glasses. Since tungsten is a preferred metal in the fabrication of VLSI devices, due to its good electromigration properties, a solution to this problem is very important in this technology. U.S. Patent 3,785,862, issued January 15, 1974, shows a method for depositing a refractory metal on an oxide coating by simultaneously etching the oxide with a metallic hexafluoride and depositing a relatively thin layer of the refractory metal by the reduction of the hexafluoride. Thereafter, a relatively thick layer of a refractory metal is deposited by the reduction of the hexafluoride. U.S. Patent 3,477,872 shows a method for depositing a refractory metal on a semiconductor substrate oxide coating which includes the steps of etching the oxide coating with a metallic hexafluoride and then depositing the refractory metal on the oxide coating by the hydrogen reduction of the hexafluoride. In the process, silicon which is exposed through the oxide coating reacts with the tungsten hexafluoride and, by a replacement reaction, a thin layer of tungsten is formed on the silicon. U.S. Patent 3,649,884 issued March 14, 1972 shows a process for the formation of pyrolytic oxide layers which contain excess silicon. U.S. Patent 4,404,235 issued September 13, 1983, shows the surface of a dielectric such as silicon dioxide being exposed to gaseous tungsten hexafluoride and hydrogen at a temperature of approximately 600°C. This initiates the formation of tungsten islands on the dielectric surface without damaging the surface. An appropriate metallization layer is then deposited from the vapor phase onto the tungsten island-covered dielectric surface. A layer of platinum is then sputtered over the discontinuous tungsten islands. U.S. Patent 3,704,166, issued November 28, 1972, shows a method for improving adhesion between a conductive layer and a substrate of insulating material which includes the steps of providing a substrate of insulating material such as silicon dioxide which contains a first cation and a first anion. A second cation such as aluminum is introduced into the substrate substitutionally by diffusion or ion bombardment. Finally, a layer of conductive material is deposited on the surface of the substrate by vacuum evaporation or sputtering. The conductive material includes a third cation such as tungsten which has an affinity for the first anion. The introduction of the second cation is carried out in only the surface layers of the substrate such that the dielectric characteristics of the substrate are substantially unaffected. This invention basically teaches providing sites, in an insulating substrate, containing unbound atoms which are capable of chemically bonding with the deposited conductive material thereby obtaining improved adhesion at low temperatures. None of the above-cited prior art references utilizes an insulator which includes silicon particles or nucleation sites within the insulator for bonding a refractory metal and, particularly, tungsten. While substitution reaction which substitute tungsten for silicon are well-known, none of the references cited use the substitution reaction to convert silicon particles to tungsten particles within the insulator and then deposit tungsten to form with the now-formed tungsten particles a highly adherent layer of tungsten on the surface of an oxide or nitride layer. The invention as claimed is intended to provide an improved process and structure for bonding layers of refractory metals and refractory metal silicides to substrates or insulators where the layers are not subject to delamination during further processing steps such as annealing at elevated temperatures. This is accomplished by the use of an intermediate bonding layer strongly adhering to the substrate and having inclusions of the refractory metal to form bonding sites for bonding the refractory metal layer. These and other objects, features and advantages will be more apparent from the following more particular description of the invention as illustrated in the accompanying drawings. Fig. 1 is a cross-sectional schematic illustration of an integrated circuit chip showing a via structure wherein a tungsten interconnection line is connected to a semiconductor substrate and is simultaneously intimately bonded to a BPSG insulator structure by means of an intermediate bonding layer of silicon dioxide or silicon nitriede which contains inclusions of silicon and a refractory metal such as tungsten. Fig. 2 is a schematic drawing which illustrates a typical deposition apparatus used in carrying out the method of the present invention. Fig. 3 is a cross-sectional schematic illustration of a graded oxide/nitride via structure fabricated in accordance with the process of the present invention. The present invention relates to a process for forming highly adherent layers of a refractory metal like tungsten (or a silicide) on the surface of insulators like silicon dioxide or silicon nitride, where the metal and insulator layers are not subject to delamination. The process basically includes the step of forming a silicon-rich silicon oxide or nitride layer (or mixed oxy-nitride layer) on a substrate. The substrate may be any material on which one would normally want to deposit a refractory metal such as tungsten. A material such as boro-phosphosilicate glass (BPSG) is one such material. In the usual case, if tungsten is deposited as a refractory metal silicide (WSi x ) or as tungsten alone, the resulting layer is subject to delamination. After the silicon-rich silicon dioxide or silicon nitride layer is formed on the substrate, the substrate is placed in a Low Pressure Chemical Vapor Deposition (LPCVD) reactor and tungsten hexafluoride (WF₆) is introduced into the reactor, which has been evacuated to below 1.3 Pa. The substrate is held at a temperature between 300-400°C while tungsten hexafluoride flows over it at a volume flow rate in the range of 10-20 sccm for a time in the range of 200-300 seconds. Nucleation sites for tungsten are created in the silicon oxide or silicon nitride by the following reactions: 2 WF₆ + 3Si (from Si-rich oxide) → 2W↓ + 3 SiF₄↑ 2 WF₆ + 3Si (from Si-rich nitride) → 2W↓ + 3 SiF₄↑. Using the above reactions, tungsten is substituted for free silicon particles at or near the surface of the silicon-rich oxide or nitride layer. The resulting layer still retains its basically insulating character of a pure silicon oxide or silicon nitride layer because there is insufficient free silicon and tungsten therein to permit current to flow through such a layer. In a final step, tungsten hexafluoride and hydrogen are introduced at a volume flow rate in the range of 500-2000 sccm at a temperature in the range of 300-400°C for a time sufficient to form a layer of desired thickness. The ability to bond tungsten to tungsten sites, which are themselves bonded into a silicon oxide or silicon nitride matrix, now makes it possible to provide a bonding medium between tungsten and a substrate such as BPSG. This bonding medium is a silicon dioxide or silicon nitride layer which is silicon-rich and wherein at least a portion of the free silicon particles have been substituted for by tungsten creating a bonding medium which contains free silicon and free tungsten inclusions. In this way, tungsten is bonded to the tungsten inclusions and the silicon dioxide or silicon nitride is bonded to the BPSG. In the fabrication of integrated circuits, materials are often used because they possess a certain desirable quality. One example of this is the refractory metal, tungsten, which is often selected because of its good electromigration properties. The same material, however, when used with other materials such as boro-phosphosilicate glass (BPSG) and deposited directly on it, is subject to undesirable events such as delamination during integrated circuit fabrication. One approach has been to provide an intermediate layer of a material such as tungsten silicide (WSi x ) between the BPSG and the over-lying tungsten layer. This has not proved to be a satisfactory solution in that silicon from the WSi x can migrate to the overlying layer of tungsten to convert portions of it to a silicide at elevated processing temperatures. Secondly, WSi x has a very high stress. Also, the delamination properties of such a structure are not significantly improved and the etching of such a structure might be a problem. FIG. 1 is a cross-sectional schematic illustration of an integrated circuit chip 1 showing a via structure wherein a refractory metal interconnection line 2 is connected to a semiconductor substrate 3 and is simultaneously disposed in intimately bonded relationship with a BPSG layer 4 by means of an intermediate bonding layer 5 of silicon dioxide or silicon nitride which contains particles 6 of free silicon and inclusions 7 of the refractory metal. In the discussion of FIGS. 1-3, the refractory metal will be illustrated by tungsten, which is a particularly important material and one which most significantly exhibits the benefits of the present invention. In FIG. 1, tungsten interconnection layer 2 contacts substrate 3 by means of a tungsten via 2a through a via hole formed in BPSG layer 4. Recessed oxide regions 8, formed in substrate 3, have on their surfaces polycrystalline regions 9. Tungsten interconnection layer 2 may be connected to a polycrystalline region 9 by means of a tungsten via 2b through a via hole formed in BPSG layer 4. Tungsten interconnection layer 2 is strongly bonded to BPSG layer 4 by means of bonding layer 5. In the fabrication process which will be described in detail hereinbelow in connection with FIG. 2, particles 6 of free silicon at or near the surface of layer 5 are substituted for by a substitution reaction with silicon hexafluoride, forming tungsten inclusions 7 where the reaction is carried out. Then, when tungsten interconnection layer 2 is deposited by the hydrogen reduction of tungsten hexafluoride, the depositing tungsten encounters nucleation centers to which it becomes intimately bonded forming a layer of tungsten which is not subject to delamination. Particles 6 of free silicon may be distributed uniformly throughout bonding layer 5 or they may be distributed in graded fashion in layer 5 so that there are no particles of silicon near the bottom of layer 5 and the maximum number of particles 6 are present at the top of layer 5. To obtain the structure of FIG. 1, the apparatus of FIG. 2 is used to carry out the deposition of tungsten from a hexafluoride gas. However, prior to such deposition, a semiconductor substrate 3 having recessed oxide regions 8 formed in the surface thereof is fabricated using well-known masking, photolithographic, etching and thermal growth to ultimately provide recessed oxide regions 8. Once the recessed oxide regions 8 are formed, polycrystalline regions 9 are formed by the deposition of a blanket layer of polycrystalline silicon using the decomposition of silane, for example, in a well-known way. Then using masking, lithographic and etching steps, regions 9 are provided. After regions 9 are in place, a layer 4 of BPSG is deposited using well-known deposition techniques. A reference which describes techniques for making glass layers is a text by S. K. Ghandhi, entitled VLSI FABRICATION PRINCIPLES, published by John Wiley and Sons, copyright 1983. Specific reference is made to pages 424-427 and 440,441 thereof where the preparation of phosphosilicate type glasses is described. At this point, layer 5 of silicon-rich silicon dioxide or silicon nitride is formed. The technique for forming such layers is well-known and is described in detail in U.S. Patent 3,649,884 which is hereby incorporated by reference. Briefly, layer 5 may be deposited from the vapor phase using an N₂O: SiH₄ ratio of 25 to 30:1. Layer 5, as deposited, contains particles of free silicon which, as previously indicated, may be uniformly distributed throughout the oxide (or nitride) or distributed in a graded manner so that the greatest concentration is at or near the surface of layer 5. A typical thickness of layer 5 is 200-300 Angstroms (20-30 nm). Once layer 5 is formed, substrate 3 along with other similar substrates is introduced into the deposition apparatus shown in FIG. 2 in order to deposit W by the H₂ reduction of tungsten hexafluroide gas (WF₆). The deposition apparatus includes a deposition process chamber 20 which encloses a turret-like holder 21 on which substrates 3 are mounted. Tungsten hexafluoride (WF₆) gas which is commercially available is introduced into chamber 20 via ports 22. A carrier gas such as helium, argon or nitrogen is also introduced into chamber 20 via ports 22, while hydrogen is introduced into the chamber 20 via input ports 24. Excitation is provided by an infrared sensor lamp assembly 26 which is connected to the turrent-like holder 21. Also connected in a tubing to chamber 20 are a high vacuum valve 28, a throttle valve 30, a blower 32, and a pump 34. These components are used to exhaust chamber 20 through output port 36, in order to remove contaminates and to maintain proper pressure in chamber 20. The exposed surfaces of the substrates 3 contain tungsten inclusions that serve as nucleation centers for the tungsten that is to be deposited. These inclusions are formed by introducing WF₆ into the reactor chamber 20, which has been evacuated to a pressure less than 1.3 Pa. The substrates 3 are held at a temperature between about 300-400°C. WF₆ flows over the substrates 3 at a volume flow rate of about 10-20 sccm for a time in the range of 200-300 seconds. Nucleation sites for W are created in the silicon-rich silicon oxide or silicon nitride layer 5 by the following reactions: 2 WF₆ + 3Si (from silicon oxide) → 2W↓ + 3 SiF₄↑ 2 WF₆ + 3Si (from silicon nitride) → 2W↓ + 3 SiF₄↑. In these reactions, W is substituted for free Si particles at or near the surface of oxide or nitride layer 5. To deposit W, WF₆ is introduced into chamber 20 through port 22, while H₂ is introduced through port 24. The volume flow rate for these gases is in the range of about 500-2000 sccm, while the substrates 3 are held at a temperature in the range of about 300-400°C. These conditions are maintained for a time sufficient to deposit W to a desired thickness, using the hydrogen reduction of WF₆ in accordance with the following reaction: WF₆ + 3H₂ → W↓ + 6HF↑. A strongly adherent structure is made by this technique, since the silicon oxide or silicon nitride layer 5 bonds strongly to the BPSG layer 4. Because there is insufficient free Si and W in layer 5, this layer will retain its insulating property. Further, since the tungsten bonds to tungsten sites that are tightly bonded into the silicon oxide or silicon nitride matrix, there will be excellent adhesion between the tungsten layer 2 and the silicon oxide or silicon nitride layer 5. The net result is that the entire structure is very resistant to the potentially adverse effects of heating, etc. which can occur during subsequent VLSI processing steps used to provide the final structure. Another advantage of the present invention is that the Si-rich oxide or nitride layer 5 protects the underlying BPSG layer 4 during the hydrogen reduction of WF₆. This reaction produces as a by-product HF gas which is known to etch BPSG (see J. J. Cuomo, "Selective CVD of Tungsten", Third International Conference on CVD, pp. 270-278, 1972). Thus, layer 5 serves a protective function in addition to being a superior bonding layer. FIG. 3 shows the application of this invention to a graded silicon oxide-silicon nitride via structure, there being a tungsten interconnect between metallization levels. The structure of FIG. 3 includes many of the layers comprising the structure of FIG. 1 and can be made in accordance with the principles described hereinabove. For ease of relating FIG. 3 to FIG. 1, the same reference numerals will be used to denote identical layers or regions. The structure of FIG. 3 includes a silicon substrate 3 having recessed oxide regions 8 therein. Polycrystalline silicon regions 9 are formed on the oxide regions 8. Tungsten interconnection layer 2 contacts substrate 3 by means of a tungsten via 2a through a via hole formed in the BPSG layer 4, and contacts polycrystalline region 9 by means of a tungsten via 2b through another via hole formed in the BPSG layer 4. The tungsten interconnection layer 2 is strongly bonded to the BPSG layer 4 by means of the bonding layer 5, which is a Si-rich silicon oxide layer having free Si particles 6 at the surface thereof which are replaced by tungsten inclusions during processing, as described previously. The inclusions provide strong bonding sites for the subsequently deposited tungsten, which is deposited by hydrogen reduction of WF₆. In the description of the previous paragraph, the processing steps are described only in a very general way, having been already discussed in detail with respect to FIGS. 1 and 2. The rest of FIG. 3 includes an additional insulating layer 38 of Si-rich silicon nitride located over first tungsten interconnect layer 2, and over portions of the Si-rich oxide layer 5. Nitride layer 38 is Si-rich at its tip and bottom surfaces, indicated by the regions 38A on either side of its central region 38B. A second tungsten layer includes tungsten vias 40 and 42, respectively, which contact different portions of the first tungsten interconnect layer 2, through via holes in the nitride layer 38. As with oxide layer 5, the Si particles near the top surface of layer 38 are substituted for by tungsten to provide tungsten inclusions 39 that are strong bonding sites for tungsten vias 40 and 42. The Si-rich bottom portion of nitride layer 38 provides good adhesion to tungsten layer 2. Cu lands 44,46 provide contacts to tungsten vias 40 and 42, respectively, to complete the structure. These lands can be formed by any low resistivity metal (preferably Cu or Al-Cu) with the proper adhesion layer. The Si-rich surface regions 38A are created by the same type of process used to make the Si-rich region of oxide layer 5. Because the density of free Si in regions 38A is not great, and because central region 38B remains relatively thick, layer 38 retains its insulating property. Via holes in it for vias 40 and 42 are made by standard lithography and etching steps. The vias 40 and 42 are formed in the same manner as were the vias 2a,2b. Thus, the structure is again located in the reactor of FIG. 2, and tungsten inclusions are introduced in the top surface region 38A by flowing WF₆ into the reactor chamber 20, while the chamber pressure, substrate temperature, gas flow rate and time of exposure are maintained at the values mentioned previously. To deposit the W vias 40 and 42, WF₆ and H₂ are introduced into the reaction chamber to again deposit W via the hydrogen reduction of WF₆. The conditions of temperature, pressure, and flow are the same as those used to deposit W layer 2, and need not be repeated here. After deposition of vias 40,42 contact lands 44,46 of, for example, Cu can be deposited to complete the structure. While the invention has been described using as an example of the bonding or adhesion layer, a silicon oxide or silicon nitride layer, other bonding layers can be used. For example, the silicon oxide layer can be an SiO or SiO₂ layer which is made Si-rich. Other suitable bonding layers include Si-rich layers of silicon oxy-nitrides or the well known passivation layer tetraethyl orthosilicate (TEOS). Other oxysilicates can also be used. Thus, in the practice of this invention, the bonding layer is preferably a silicon-based oxide, nitride, or mixed oxy-nitride layer which is capable of being made Si-rich in a surface region thereof, where the excess silicon particles can be substituted for by the material (e.g., W) to be adhered to the substrate. In the further practice of this invention, the metal layer to be adhered to the substrate includes not just W, but also other refractory metals such as Nb, Mo, Ti, Ta and Cr and their silicides (such as WSi x , Mo-silicide, etc.) The inclusions introduced into the bonding layer to provide nucleation sites for the depositing refractory metal would then be Nb, Mo, Ti,...particles, respectively. The substrates to which the refractory metals are to be adhered include any materials to which the Si-rich oxide, nitride, or mixed oxy-nitride bonding layers will strongly adhere. The substrate can be used for any purpose, such as a dielectric layer, a semiconducting layer, or even a conducting layer. Examples include single crystal, polycrystalline, or amorphous silicon, insulators including silicon and glasses such as BPSG. Since the substrates contain silicon, the special bonding layers of this invention will strongly adhere to them.

Claims: A method for bonding a layer (2) of a refractory metal, or a refractory metal silicide, to a substrate to which said layer does not strongly adhere, comprising the steps of depositing a silicon rich bonding layer (5), selected from the group consisting of silicon oxides, silicon nitrides, and silicon oxynitrides, on said substrate (3), said bonding layer strongly adhering to said substrate and containing free silicon (6) at least in the surface region thereof that is to be contacted by said layer of said refractory metal or said refractory metal silicide, substituting atoms of said refractory metal for at least some of said free silicon (6) in said bonding layer (5) to produce refractory metal inclusions (7) within the body of said bonding layer, said inclusions being bonding sites for deposition of said layer (2) of said refractory metal, or said refractory metal silicide, and depositing said layer (2) of said refractory metal, or said refractory metal silicide, onto said bonding layer (5), said bonding sites strongly adhering said deposited layer (2) of a refractory metal, or a refractory metal silicide, to said bonding layer. The method of claim 1, where said refractory metal of said layer (2) is selected from the group consisting of W, Nb, Mo, Ti, Cr, and Ta. The method of claim 2, where said refractory metal is W (tungsten). The method of claim 3, where said atoms of tungsten are substituted for said free silicon by contacting said bonding layer (5) with WF₆ gas, and said tungsten layer (2) is deposited on said bonding layer (5) by hydrogen reduction of WF₆ gas in the vicinity of said bonding layer. The method of claim 4, wherein the amount of free silicon and tungsten inclusions in said bonding layer (5) is sufficiently low that said bonding layer is an insulator. The method of claim 1, where the particles (6) of said free silicon are distributed in a graded manner so that the highest concentration is at or near the surface of said bonding layer (5) that is to be contacted by said layer (2) containing said refractory metal. A multilayer structure with a layer (2) of a refractory metal, or a refractory metal silicide, bonded to a substrate, the structure including a substrate (3) of a material which does not bond strongly to said layer of a refractory metal, or a refractory metal silicide, a layer (2) of said refractory metal, or said said refractory metal silicide, a silicon rich bonding layer (5), selected from the group consisting of silicon oxides, silicon nitrides, and silicon oxynitrides, located between said layer (2) of said refractory metal, or said refractory metal silicide, and said substrate (3) and adhering strongly to said substrate, said bonding layer (5) having free silicon (6) therein and inclusions (7) of said refractory metal substituted for some of the free silicon which was initially present within said bonding layer and forming bonding sites, said layer (2) of said refractory metal, or said refractory metal silicide, being strongly bonded to said sites within said bonding layer (5). The structure of claim 7, said substrate further including on its surface an insulating layer (4), having a via hole (2a) therein, wherein said layer (2) of said refractory metal, or said refractory metal silicide, is located as a via interconnection. The structure of claim 8, where said substrate (3) includes a layer of semiconducting material in which an active device is formed.

Inventors: JOSHI, RAJIV VASANT
Applicants: INTERNATIONAL BUSINESS MACHINES CORPORATION
Application year: 1987
Main classification: H01L21
IPC codes: H01L21, H01L23