THIOL/ENE COMPOSITIONS

Abstract: Curable thiol/ene compositions comprise: 1) a multifunctional styryloxy monomer having one or more of the following structures wherein R¹, R² and R³ are selected from vinyl (-CH=CH₂), 1-­ propenyl(-CH=CH-CH₃), isopropenyl hydrogen, lower alkyl or alkoxy, provided that at least one of R¹, R² and R³ must be vinyl, 1-propenyl or isopropenyl; n is an integer ≧ 1; if n = 1, then R⁴ is a monovalent hydrocarbon radical containing one free-radically copolymerisable alkenyl or cycloalkenyl group, if n ≧ 2, R⁴ is a multivalent hydrocarbon radical which may contain a maximum of one free-radically copolymeris­ able alkenyl or cycloalkenyl group; R⁵ is a divalent hydrocarbon radical; or a carbon atom which is part of a cyclic group in the radical G; or a radical of formula -R⁷--O- where R⁷ is a divalent hydrocarbon radical; if n = 1, G is a monovalent organic or inorganic radical, free of phenolic hydroxyl groups or other groups which sub­ stantially interfere with radical polymerisation, containing one free-radically copolymerisable alkenyl or cycloalkenyl group; if n ≧2, G is a multivalent organic or inorganic radical, free of phenolic hydroxyl groups or other groups which sub­ stantially interfere with radical polymerisation, which may contain a maximum of one free-radically copolymerisable alkenyl or cycloalkenyl group; R⁶ is a lower alkyl or cycloakyl group; or if n = 1, R⁶ may also be an alkenyl or cycloalkenyl group, provided that G does not contain an alkenyl or cycloalkenyl group. 2) a multifunctional thiol. 3) a free-radical curing rate accelerator. Novel styryloxy compounds are described which are reaction products of a compound of the formula: where R¹ is vinyl, 1-propenyl or isopropenyl; R² and R³ are H, lower alkyl or alkoxy; and R⁶ is alkyl, with an epoxy functional compound selected from the group consisting of: a) triglycidylether isocyanurate, b) allyl glycidyl ether, c) compounds having plural epoxy cyclohexane groups, and d) a multifunctional epoxidised polydimethylsiloxane which is the reaction product of allyl glycidyl ether with a dimethylsiloxane having 2 or more SiH groups.

Description: This invention relates to curable thiol/ene compositions wherein the -ene component is a multifunctional styryloxy monomer. Numerous proposals have been made for curable compositions based on thiol/ene polymer systems, the essential components of which are a multifunctional alkene and a multifunctional thiol. Representative groups of thiol/ene polymers are described in US-A-3 661 744; 4 008 341 and 4 119 617. US-A-4 308 367 discloses polymerisable compositions of the thiol/ene type in which the -ene component is a compound containing in the same molecule at least one phenolic hydroxyl group and at least two groups chosen from allyl, methallyl and 1-propenyl groups. However, the phenolic hydroxyl group, being a free-radical scavenger, tends to decelerate the polymerisation reaction. US-A-4 145 479 discloses a curable composition comprising at least one unsaturated polyaryloxyphosphazene, at least one aryloxy cyclotriphosphazene and a thiol crosslinking agent. Among the terminal groups suggested for the unsaturated phosphazene components are various styryloxy groups. However these compounds must have the phosphazene backbone structure, which is linked to the oxygen of the styryloxy terminal groups by a P-O- linkage, and the compounds are therefore distinct from those used in the present invention. US-A-4 543 397 discloses polyfunctional cationically polymerizable styryloxy compounds of the formula wherein R¹ and R² are H, or one of R¹ and R² are H and the other is methyl; R³ and R⁴ are H, lower alkyl, or alkoxy if R² is not methyl; R⁵ is a divalent hydrocarbon radical; G is any multivalent organic or inorganic radical free of amino, aliphatic hydroxyl, aliphatic thiol or other groups which interfere with cationic polymerization; and n is an integer of two or more. The present invention provides novel curable compositions comprising 1) a multi functional styryloxy monomer having one or more of the following structures wherein: R¹, R² and R³ are selected from vinyl (-CH=CH₂), 1-propenyl(-CH=CH-CH₃), isopropenyl hydrogen, C₁-C₁₀ alkyl or alkoxy, provided that at least one of R¹, R² and R³ must be vinyl, 1-propenyl or isopropenyl; n is an integer ≧ 1; if n = 1, then R⁴ is a monovalent hydrocarbon radical containing one free-radically copolymerisable alkenyl or cycloalkenyl group, if n ≧ 2, R⁴ is a multivalent hydrocarbon radical which may contain a maximum of one free-radically copolymerisable alkenyl or cycloalkenyl group; R⁵ is a divalent hydrocarbon radical; or a carbon atom which is part of a cyclic group in the radical G; or a radical of formula where R⁷ is a divalent hydrocarbon radical; if n = 1, G is a monovalent organic or inorganic radical, free of phenolic hydroxyl groups or other groups which substantially interfere with radical polymerisation, containing one free-radically copolymerisable alkenyl or cycloalkenyl group; if n ≧ 2, G is a multivalent organic or inorganic radical, free of phenolic hydroxyl groups or other groups which substantially interfere with radical polymerisation, which may contain a maximum of one free-radically copolymerisable alkenyl or cycloalkenyl group; R⁶ is a C₁-C₁₀ alkyl or cycloalkyl group; or if n = 1, R⁶ may also be an alkenyl or cycloalkenyl group, provided that G does not contain an alkenyl or cycloalkenyl group. 2) a multifunctional thiol. 3) a free-radical curing rate accelerator. In the preferred embodiments C₁-C₁₀ alkyl is C₁-C₅ alkyl. The mole ratio of styryloxy/thiol groups is suitably from 0.2/1 to 5/1, preferably 0.75/1 to 1.5/1. R₄ may suitably be an alkenyl group e.g. an allylic group. When n = 1, G may suitably be a substituted or unsubstituted monovalent hydrocarbon radical which may be straight or branched chain and which contains one free-radically copolymerisable alkenyl group, for example an allylic group or an allyl alkyl ether group, optionally substituted with a hydroxy group When n ≧ 2, G may suitably be a) a polyorganosiloxane backbone, optionally substituted with styryloxy groups of the kind defined within the square brackets above, b) an n-valent hydrocarbon radical, straight or branched chain. c) a urethane group d) an ester group e) an isocyanurata group f) an acetal group. The invention also provides novel multifunctional styryloxy monomers including reaction products of a compound of the formula: where R¹ is vinyl, 1-propenyl or isopropenyl; R² end R³ are H, C₁-C₁₀ alkyl or alkoxy; and R⁶ is alkyl, with an epoxy functional compound selected from: a) triglycidylether isocyanurate, b) allyl glycidyl ether, c) compounds having plural epoxy cyclohexane groups, and d) a multifunctional epoxidised polydimethylsiloxane which is the reaction product of allyl glycidyl ether with a dimethylsiloxane having 2 or more SiH groups. The multifunctional epoxidised polydimethylsiloxanes d) are generally of the formula wherein n is zero or an integer; preferably less than 50, particularly less than 20; for example 5, and m is an integer greater than about 10 and preferably less than 500; particularly less than 100, for example 30. Preferred novel compounds are selected from the group consisting of: The novel compounds are useful in the Thiol/ene compositions of the invention. In addition to the compounds described in the Examples below other suitable styryloxy monomers include the following: 1. Reaction products of hydroxyl containing styryloxy compounds with: a) Polyfunctional isocyanates. e.g. the urethane formed by reacting 2 equivalents of 4-(2-hydroxyethoxy)-3-methoxyprop-1-enylbenzene with 1 equivalent of diphenylmethane diisocyanate. b) Polyfunctional carboxylic acids or acid chlorides. e.g. the ester formed by reacting 2 equivalents of 4-([2-hydroxy-3 (oxyprop-2-enyl)-propoxy]-prop-1-enylbenzene with 1 equivalent of sebacoyl chloride. c) Dianhydrides. e.g. the ester formed by reacting 2 equivalents of 4-(2-hydroxyethoxy)prop-1-enylbenzene with 1 equivalent of pyromellitic dianhydride. d) Aldehydes. e.g. the acetal formed by reacting 2 equivalents of 4-(2-hydroxyethoxy)prop-1-enylbenzene with one equivalent of acrolein. e) Polyepoxides. e.g. the styryloxy substituted Novolac resin formed by reacting 2.7 equivalents of 4-(2-hydroxyethoxy)prop-1-enylbenzene with 1 equivalent of epoxy cresol Novolac Resin ECN 1235 (supplied by Ciba Geigy Corp.). f) Polyfunctional esters. e.g. the ester formed by reacting 2 equivalents of 4-(2-hydroxyethoxy)prop-1-enylbenzene with one equivalent of dimethylphthalate. 2. Reaction products of 3-hydroxy-4-alkoxystyrenes with a) Polyfunctional isocyanates. e.g. the urethane formed by reacting 2 equivalents of 2-methoxy-5-prop-1-enylphenol with 1 equivalent of isophorone diisocyanate. b) Dianhydrides. e.g. the ester formed by reacting 2 equivalents of 2-methoxy-5-prop-1-enylphenol with 1 equivalent of 3,3',4,4'-benzophenone-tetracarboxylic dianhydride. c) Polyepoxides. e.g. the isocyanurate formed by reacting 3 equivalents of 2-methoxy-5-prop-1-enylphenol with 1 equivalent of triglycidyl ether isocyanurate. d) Multifunctional acid chlorides. e.g. the ester formed by reacting 2 equivalents of 2-methoxy-5-prop-1-enylphenol with 1 equivalent of terephthaloyl chloride. The multi functional thiol may be chosen from compounds having 2 or more mercapto groups (-SH) per molecule. Suitable polythiols are described in US-A-3 661 744, 4 008 341 and 4 119 617 mentioned above. The polythiol component suitably has a molecular weight in the range from about 50 to about 20,000 and is of the general formula R n -(SH) n where R is a polyvalent organic moiety free from reactive carbon-to-carbon unsaturation and n is at least two. The free radical curing rate accelerator may be of any of the known types of accelerator or polymerisation initiator which activate the composition photochemically, thermally or by chemical (Redox) action. Suitable photocuring rate accelerators are described in US-A-3 661 744, particularly the aldyhyde and ketone carbonyl compounds having at least one aromatic nucleus attached directly to the group. Examples include benzophenone, acetophenone, 2,2-dimethoxy-2-phenylacetophenone and derivatives thereof. The rate accelerator may suitably be present over the range 0.05-10% by weight of the total weight of the composition. Optionally the composition may contain an organic solvent (e.g. ethylacetate or 1,1,1-trichloroethane) and a free radical stablliser or inhibitor to prevent premature onset of curing (e.g. hydroquinones, benzoquinones, naphthoquinones, phenanthraquinones and substituted compounds of any of the foregoing, or phenols such as 2,6-di-tert-butyl-4-methyl phenol). Other optional ingredients of the composition include coinitiators or photosensitizers, thickeners, pigments, dyes, toughening agents, antioxidants, acids (e.g. phosphorous acid), wetting agents, flow control agents and adhesion promoters, all of which are of types known in the prior art. The present invention provides novel thiol/ene compositions which are capable of more rapid curing than commercially available thiol/ene systems and which have good thermal resistance. They can be used for numerous applications which are known for thiol/ene compositions, such as coatings, potting compositions and sealing and gasketting materials. The invention is illustrated in the following examples: Example 1 A mixture of isoeugenol (24.6g), 3,4-epoxycyclohexylmethyl-3,4-epoxycyclohexane carboxylate (18.75g) (available under the trade name ERL-4221 from Union Carbide) and potassium hydroxide (0.09g) was heated at 100°C for 71 hours. After this time, thin layer chromatography (t.l.c.) indicated that the isoeugenol had been almost consumed. On cooling, a yellow solid was obtained. T.l.c. analysis of this material indicated the presence of many compounds and a mass spectrum showed the major component to be the difunctional styryloxy monomer (M⁺ at 580.4 = 12% [C₃₄H₄₄O₈]; (M-164)⁺ at 416.2 = 3% [C₂₄H₃₂O₆]; M/e = 164.1 [C₁₀H₁₂O₂]) exemplified by the formula: along with material isomeric to this structure. Gel permeation chromatography (G.P.C.) showed that 60% of the resin corresponded to the difunctional styryloxy resin, 25% to higher molecular weight analogues and polymer and 15% to lower molecular weight compounds including minor amounts of the starting phenol. Example 2 An ultra-violet (UV) light sensitive composition was prepared by heating to 80°C a mixture of 1.45g of the resin obtained in Example 1, 1.11g of pentaerythrital tetrakis mercaptopropionate (mercaptate Q-43 ester supplied by Cincinnati Milacron Chemicals) and 2,2-dimethoxy-2-phenylacetophenone (0.08g) until a homogeneous blend was obtained. A 100 micron thick coating of the blend was then prepared on a standard 1 x 4" microscope glass slide and the coating exposed to ultraviolet light from a medium pressure mecury arc lamp operating at 200 W/inch (Porta-Cure 1000, American Ultraviolet Co.). After 5 seconds exposure, the coating had cured to a dry film which was found to be insoluble in acetone. The light intensity at the curing surface was measured using an International Light Co. light meter (model 1L-443) with 365nm probe and found to be 60mW/cm². Example 3 Isoeugenol (16.47g), allyl glycidyl ether )11.42g) and Amberlyst A-21 (2.02g) resin were heated together at 105°C for 8 hours. After this time, t.l.c. analysis indicated that most of the starting isoeugenol had been consumed. The Amberlyst resin was separated from the reaction mixture and the remaining brown coloured liquid was analysed by G.P.C. The chromatogram showed only one peak corresponding to a higher molecular weight product than either of the starting compounds. This compound is believed to be the simple condensation product of the phenol and the epoxide and has the structure: Example 4 U.V. sensitive compositions were prepared by blending the following materials together (all parts by weight): Composition A Composition B Resin of Example 3 51.3 66.8 Mercaptate Q 43 45.0 29.3 2,2-dimethoxy-2-phenylacetophenone 3.7 3.9 Coatings were prepared as described in Example 2. After 20 secs. exposure (UV conditions as Example 2), Composition A had cured to a tack-free film with good adhesion to the glass surface. Approximately 60 secs. exposure was required to cure Composition B which was softer than Composition A. Example 5 4-isopropenylphenol (8.9g) [prepared by the method described by J. Kahovec et al, Collection Czechoslov . Chem. Commun. , Vol. 36, page 1986, (1970)1, allylglycidyl ether (7.6g) and Amberlyst A-21 resin (1.0g) were heated together at 115°C for 6.5 hours. After this time, t.l.c. analysis indicated that the starting phenol had been almost consumed. Removal of the Amberlyst resin gave a brown coloured liquid believed to be the condensation product of the starting phenol and epoxide, represented by the formula: Example 6 UV sensitive compositions were prepared by blending the following materials together (wt. in grams): Composition C Composition D Reaction product of Example 5 6.2 6.2 Mercaptate Ester, Q43 6.1 3.0 2,2-dimethoxy-2-phenylacetophenone 0.5 0.4 Coatings of these compositions were prepared as described in Example 2. After 50 secs. exposure to UV light (conditions as described in Example 2), cured tack free films were obtained. Composition D was harder than Composition C. Example 7 12.5g of a heptafunctional epoxidised polydimethylsiloxane of approximate molecular weight 3,360 (prepared by a hydrosilation reaction of one equivalent of the corresponding heptafunctional hydro siloxane and seven equivalents of allyl glycidyl ether in the presence of a platinum catalyst), 2.22g of isoeugenol and 1.38 grams of Amberlyst Resin A-21 were heated together at 110°C for 17 hours. After this time, t.l.c. analysis indicated that all of the isoeugenol was consumed. The infra red (I.R.) spectrum of the reaction mixture showed a peak at 3480cm⁻¹ due to the presence of an hydroxyl group. The Amberlyst resin was separated from the reaction mixture to yield a product predominately of the formula: A mixture was prepared by blending 8.4g of this resin with 1.2g of mercaptate ester Q43 and 0.4g of 2,2-dimethoxy-2-phenylacetophenone. A coating of the material was prepared as described in Example 2 and exposed to UV light from a Technocure 200 W/IN mercury lamp at an intensity of 50mW/cm² (365nm) for 30 secs. After this time, a dry to touch, soft, cured film was obtained. Example 8 To a solution of 122g 4-hydroxybenzaldehyde in 500 mls acetone was added 276g potassium carbonate. This mixture was stirred for 15 minutes. A solution of 133g allyl bromide in 200 mls acetone was then added dropwise over 30 minutes. The resulting mixture was heated at reflux for 1 hour, left standing for a further 16 hours and finally heated at reflux for 2 hours. After filtration, the solvent was removed by distillation leaving 175g of a reddish liquid. This residue was distilled under reduced pressure (B.Pt. 104 o -114 o C. at 1.5 mmHg) to yield 130g of a pale yellow liquid which was identified by infrared and n.m.r. spectroscopy as 4-allyloxybenzaldehyde. To a solution of 9.36g potassium metal in 500 mls tert-butanol was added 85.68g methyltriphenylphosphonium bromide. The resulting yellow suspension was stirred for 20 minutes and 32.4g 4-allyloxybenzaldehyde was then added over 10 minutes. This mixture was stirred for 30 minutes and then allowed to stand overnight. After filtration the solvent was removed under reduced pressure leaving 107g of a red semi-solid residue. Petroleum ether (B.Pt. 40 o -60 o C.) was added to the residue precipitating a solid which was filtered. After removal of the petroleum ether, the remaining resin was distilled under reduced pressure (B.Pt. 68 o -82 o C. at 0.4 mmHg) yielding 26.7g of a clear colorless liquid which was identified by infrared and n.m.r. spectroscopy as 4-allyloxystyrene (Proton NMR: (CDCl₃)δ=4.50, 4.58, doublet, allyloxymethylene protons; δ=5.0-6.5, multiplets, allyl and vinyl group protons; δ=6.80, 6.95, 7.30 and 7.45, quartet, aromatic protons). Example 9 UV sensitive compositions based on 4-allyloxystyrene (prepared as in Example 8) were formulated (quantities are all parts by weight): Composition E Composition F Composition G 4-allyloxystyrene 13.0 13.0 8.0 Mercaptate ester, Q43 12.2 12.2 12.2 2,2,-dimethoxy-2-phenylacetophenonone - 1.3 1.3 2,2-diethoxyacetophenone 1.3 - - 4-methyl-2,6-di-t-butylphenol 0.1 0.1 0.1 A one mm thick coating of each of these compositions was prepared on a 1 x 4" microscope glass slide and exposed to UV light from a UVA LOC 1000W mercury lamp (Trade Mark Loctite Corp.) operating at 200W per inch. Compositions E and F gave a cured tack-free film after 30 secs. exposure. Composition G was cured tack-free after 10 secs. exposure. All of these coatings were insoluble in dichloromethane. Composition G gave a tougher coating than either E or F. In each case, the coating was located 14cms directly under the mercury arc. The light intensity at this point was measured using an Optical Associates Inc., light meter (model 206) with a 365nm probe and found to be 150mW/cm². Example 10 4-allyloxy-3-methoxystyrene was prepared from vanillin by a method analogous to that described in Example 8. In this case, the intermediate product 4-allyloxy-3-methoxybenzaldehyde was obtained by vacuum distillation at 152-158°C and 7mbar in 83% yield and the styryloxy derivative at 92-110°C and 0.5 mbar in 58% yield. A UV sensitive composition was prepared by blending 9.5g 4-allyloxy-3-methoxystyrene, 12.2g of mercaptate ester Q43, 0.9g 2,2-dimethoxy-2-phenylacetophenone and 0.1g 4-methyl-2,6-di-t-butylphenol. A coating of the composition was prepared and irradiated as described in Example 9. In this case, a tack-free, cured film was obtained after 15 secs. Example 11 To a solution of 136g 4-hydroxyacetophenone in 500 mls acetone was added 276.41g potassium carbonate. This mixture was stirred for 15 minutes. A solution of 133g allyl bromide in 200 mls acetone was then added dropwise over 45 minutes, and the resulting mixture was stirred for a further 4 hours and left standing for a further 16 hours. Thin-layer chromatography showed some starting material to be present at the end of this time. The mixture was then heated to reflux for 4 hours and left standing a further 16 hours. After this time the solvent was removed by distillation leaving 230g of a brown liquid. This residue was distilled under reduced pressure (B.Pt. 107-115°C at 0.6mmHg.) to yield 158g of pale yellow liquid which was identified by infrared and n.m.r. spectroscopy as 4-allyloxyacetophenone. To a solution of 5.58g potassium metal in tert-butanol was added 51g methyl triphenylphosphonium bromide. The resulting yellow suspension was stirred for 20 minutes. A solution of 18.86g 4-allyloxyacetophenone in 30 mls tert-butanol was then added gradually and stirred for 16 hours at room temperature. After this time, the mixture was filtered and solvent removed under reduced pressure. The resulting mixture was extracted with petroleum ether to yield 28g of brown resin. This resin was distilled under reduced pressure (B.Pt. 88°C at 1mm Hg) yielding 15.21g of a clear colorless liquid which was identified by infrared and n.m.r. spectroscopy as 4-allyloxy isopropenyl benzene (Proton NMR: (CDCl₃) δ = 2.12 singlet, α-methyl protons; δ = 4.50, 4.58, doublet, allyloxy methylene protons; δ = 5.0-6.5, multiplets, allyl and vinyl group protons; δ = 6.80, 6.95, 7.35 and 7.50, quartet, aromatic protons). A UV sensitive composition was prepared by blending 8.7g of this material, 12.2g of mercaptate ester Q43 and 0.8g 2,2-dimethoxy-2-phenylacetophenone A 0.25mm thick coating was prepared and irradiated with UV light as described in Example 9. A tack-free cured film was obtained after 30 secs. exposure. Example 12 4-allyloxy-3-methoxypropenylbenzene was prepared by refluxing a stirred mixture of isoeugenol (164g),allylbromide (133g) and potassium carbonate (278g) in dry actone (700 mls) for 18 hours. Removal of the solids and solvent gave a crude product 208g which was vacuum distilled to yield 130g of pure 4-allyloxy-3-methoxy-prop-1-enylbenzene (b.p. 104-118 o C at 0.1mbar). A UV sensitive composition was prepared by blending 10.3g of this material with 12.2 g of mercaptate ester Q43 and 0.9g 2,2-dimethoxy-2-phenylacetophenone. A coating (0.25mm thick) was prepared and irradiated under UV light (as detailed in Example 9). A tack-free cured film was obtained after 10 secs. exposure. Example 13 Isovanillin (76g) was dissolved in a stirred mixture of potassium carbonate (104g) and acetone (450mls) followed by the dropwise addition of allyl bromide (67g) over ca. 20 mins The mixture was refluxed for 5 hours, cooled and filtered. The solvent was removed from the filtrate under reduced pressure and the residue was distilled under vacuum to yield 3-allyloxy-4-methoxybenzaldehyde (85g), b.p. 137 - 150°C at 1.5mbar. 60MHz, ¹HMR (CDCl₃) τ 0.2 (S , IH, CHO), τ 2.45-3.1 (m, 3H, ArH), τ 3.6-4.9 (m, 3H, CH=CH₂), τ 5.35, (d, 2H, OCH₂), τ 6.1 (S, 3H, OCH₃) Sodium amide (39g) was dispersed in dry tetrahydrofuran (800mls). Methyltriphenylphosphonium bromide (102g) was added and the mixture stirred at R.T. for 2 hours. 3-allyloxy-4-methoxy-benzaldehyde (50g) was then added dropwise over ca . 15mins. and the mixture stirred for a further 3 hours. The mixture was filtered and the solvent removed from the filtrate under reduced pressure. The residue was washed with diethyl ether (1.51) and the solvent removed to yield a brown coloured resin. The washing process was repeated and the residue obtained was distilled under reduced pressure to give 3-allyloxy-4-methoxystyrene (29.5g), b.p.98-104°C at 0.8 mbar. 60MHz, ¹HMR (CDCl₃) τ 2.45-4.90 (m, 9H, ArH + vinyl CH=CH₂ + allyl CH=CH₂), τ 5.35 (d, 2H, OCH₂), τ 6.1 (S, 3H, OCH₃). A UV sensitive composition was prepared by blending 9.5g of this material with 12.2g of mercaptate ester Q43 and 0.9g 2,2-dimethoxy-2-phenylacetophenone 0.5mm thick coatings were prepared and irradiated with UV light as described in Example 9. After 10 secs. exposure, a tack-free cured film had formed. Example 14 Isoeugenol (16.46g), 1,4-dibromobutane (11.88g) and tetra-n-butylammonium bromide (3.22g) were added to a stirred suspension of potassium carbonate (20.7g) in dry toluene (100g). The mixture was heated at 105°C for 20 hrs. After this time t.l.c. analysis indicated that all of the starting isoeugenol had been consumed. The mixture was filtered and the toluene solution washed with water (3 x 100mls). After drying (sodium sulphate), the toluene was removed under reduced pressure to yield 14.25g of a white solid. The solid was recrystallised from a mixture of ethanol and chloroform to give 4.94g of a pure product of the structure: The m.p. was 135°C. The infra red spectrum showed no phenolic hydroxyl group, indicating that the pure dialkylated product had been isolated. A UV sensitive composition was prepared by blending together a hot mixture of 1.9g of this material with 20.4g of 4-allyloxy-3-methoxy-1-propenyl benzene as prepared in Example 12. On cooling, 25.4g of mercaptate ester Q43 and 0.23g of 2,2-diethoxyacetophenone were added. 0.25mm thick coatings of the composition were prepared and irradiated as detailed in Example 9. After 30 secs. exposure, a tack-free cured film was obtained. Example 15 O-propenylphenol (67g) was added to a stirred suspension of potassium carbonate (138g) in dry acetone. Allyl bromide (67g) was then added dropwise over about 20 minutes and the stirred mixture was heated under reflux for 4 hours. After this time, gas liquid chromatography indicated that the phenol had been converted to about 95% of a mixture of cis and trans 2-allyloxy-1-propenylbenzene. The mixture was filtered and the solvent removed under reduced pressure. The residue was vacuum distilled and yielded 58.9g of almost pure 2-allyloxy-1-propenylbenzene which was identified spectroscopically. [b.p. 64-88°C at 0.6mbar]. 60MHz, ¹HMR (CDCl₃) : 2.6-5.0, 9H, multiplets due to AR-H, -CH=CH₂ and -CH=CH- ; 5.5, doublet, 2H,O-CH₂- ; 8.2, doublet 3H, -CH₃ A UV sensitive composition was prepared by blending 8.7g of this styryloxy resin with 12.2g of mercaptate ester Q43 and 0.8g of 2,2-dimethoxy-2-phenylacetophenone. A 0.25mm thick coating was prepared and irradiated as in Example 9. In this case, a tack free surface cure was obtained after 10 seconds irradiation.

Claims: Curable compositions comprising 1) a multifunctional styryloxy monomer having one or more of the following structures wherein R¹, R² and R³ are selected from vinyl (-CH=CH₂), 1-propenyl (-CH=CH-CH₃), isopropenyl hydrogen, C₁-C₁₀ alkyl or alkoxy, provided that at least one of R¹, R² and R³ must be vinyl, 1-propenyl or isopropenyl; n is an integer ≧ 1; if n = 1, then R⁴ is a monovalent hydrocarbon radical containing one free-radically copolymerisable alkenyl or cycloalkenyl group, if n ≧ 2, R⁴ is a multivalent hydrocarbon radical which may contain a maximum of one free-radically copolymerisable alkenyl or cycloalkenyl group; R⁵ is a divalent hydrocarbon radical; or a carbon atom which is part of a cyclic group in the radical G; or a radical of formula where R⁷ is a divalent hydrocarbon radical; if n = 1, G is a monovalent organic or inorganic radical, free of phenolic hydroxyl groups or other groups which substantially interfere with radical polymerisation, containing one free-radically copolymerisable alkenyl or cycloalkenyl group; if n ≧ 2, G is a multivalent organic or inorganic radical, free of phenolic hydroxyl groups or other groups which substantially interfere with radical polymerisation, which may contain a maximum of one free-radically copolymerisable alkenyl or cycloalkenyl group; R⁶ is a C₁-C₁₀ alkyl or cycloalkyl group; or if n = 1, R⁶ may also be an alkenyl or cycloalkenyl group, provided that G does not contain an alkenyl or cycloalkenyl group. 2) a multifunctional thiol. 3) a free-radical curing rate accelerator. A composition according to claim 1 wherein the mole ratio of styryloxy/thiol groups is from 0.2/1 to 5/1. A composition according to claim 1 or 2 wherein the curing rate accelerator is present in an amount of 0.05-10% by weight of the total weight of the composition. A composition according to any of claims 1 to 3 wherein R⁴ is an alkenyl group. A composition according to claim 4 wherein R⁴ is an allylic group. A composition according to any of claims 1 to 5 wherein when n = 1, G is a substituted or unsubstituted straight or branched chain monovalent hydrocarbon radical which contains one free-radically copolymerisable alkenyl group. A composition according to claim 6 wherein G is an allyl alkyl ether group, optionally substituted with a hydroxy group. A composition according to claim 1 wherein the stryloxy monomer is selected from i) Reaction products of hydroxyl containing styryloxy compounds with a) Polyfunctional isocyanates b) Polyfunctional carboxylic acids or acid chlorides. c) Dianhydrides. d) Aldehydes. e) Polyepoxides. f) Polyfunctional esters. ii) Reaction products of 3-hydroxy-4-alkoxy styrenes with a) Polyfunctional isocyanates b) Dianhydrides c) Polyepoxides. d) Multifunctional acid chlorides. A composition according to any of claims 1 to 8 wherein the free radical curing rate accelerator is a photocuring rate accelerator. A method of providing a cured dry to the touch coating on a substrate comprising; a) applying a composition as in claim 9 to the substrate surface, and b) irradiating the composition on the substrate for a time effective to cure the compound to a dry film. A compound comprising the reaction product of a compound of the formula: where R¹ is vinyl, 1-propenyl or isopropenyl; R² and R³ are H, C₁-C₁₀ alkyl or alkoxy; and R⁶ is alkyl, with an epoxy functional compound selected from: a) triglycidylether isocyanurate, b) allyl glycidyl ether, c) compounds having plural epoxy cyclohexane groups, and d) a multifunctional epoxidised polydimethylsiloxane which is the reaction product of allyl glycidyl ether with a dimethylsiloxane having 2 or more SiH groups. A compound selected from:

Inventors: ROONEY, JOHN M., WOODS, JOHN G.
Applicants: LOCTITE (IRELAND) LTD.
Application year: 1987
Main classification: C08G75
IPC codes: C08G77, C07C43, C08F12