NEW SURGICAL MATERIALS AND DEVICES

Abstract: At least partially fibrillated fixation materials for fixation of bone fractures, osteotomies, arthrodesis or joint damages and fixation devices which have been manufactured of these materials, devices like rods, plates, screws, intramedullary nails and clamps, which materials and/or devices have been manufactured of resorbable polymer, copolymer or of polymer mixture. Further this invention describes the application of at least partially fibrillated resorbable materials and especially the application of devices, like rods, plates, intramedullary nails, screws, clamps or chutes in fixation of bone fractures, osteotomies, arthrodesis or joint damages or in augmentation or reconstruction of bone tissue. Resorbable fixation materials and devices of this invention show significantly better mechanical properties than the known resorbable fixation materials and devices. This makes possible the manufacturing of smaller, patient-safe and secure fixation devices than earlier.

Description: NEW SURGICAL MATERIALS AND DEVICES Surgical implants with good mechanical strength proper¬ ties can be manufactured of resorbable polymeric mate¬ rials (resorbable composites) which contain resorbable reinforcing elements. Resorbable or absorbable means in this connection that the material is metabolized by living tissues. Such resorbable materials and implants manufactured of ■ them can be applied e.g. as rods, plates, screws, intramedullary nails etc. for fixation of bone fractures, osteotomies, arthorodesis or joint damages. An advantage of such implants and materials is that they are resorbed (depolymerized to cell nutrients) after the healing of the treated tissue. Therefore the resorb¬ able implants do not need a removal operation, like metallic implants in many cases need. Invention U.S. Pat. 4 279 249 describes resorbable implant materials comprising polyglycolide fibres as reinforce¬ ment and polylactide as a binding polymer (as a resorb¬ able matrix) . In the patent application FI 851 828 describes self-reinforced resorbable materials, where the resorbable polymer matrix has been reinforced with resorbable reinforcement elements which have the same chemical element content as the matrix. Typical reinforce¬ ment elements in this connection are fibres or structures which have been constructed of them. The known resorbable materials reinforced with resorbable organic reinforcement elements have fairly high mechani¬ cal strength values. Therefore such materials can be applied in orthopaedics and traumatology in treatment of cancellous bone fractures, osteotomies, arthrodesis or joint damages. For example the self-reinforced resorb¬ able materials of FI 851 828 describe bending strengths over 300 MPa (S. Vainionpaa, Thesis, Helsinki 1987) , which values clearly are higher than ' even the average strength values of cortical bone. Also the elastic moduli of known self-reinforced resorbable composites are quite high, typically of the order of magnitude of 10 GPa. So the strength values of these materials are clearly better than those of resorbable materials which have been manufactured by melt moulding techniques. When one manufactures of resorbable polymers, copolymers or polymer alloys rods, profiles, plates etc. implants by melt moulding techniques like by injection moulding or by extrusion the mechanical properties of the products remain on the ' level which is typical for thermoplastic polymers. The strength values (like tensile, shear and bending strength) typically do not exceed the value 150 MPa showing typically strength values between 40 and 80 MPa and moduli between 1 and 6 GPa. The reason to this behaviour is the fact that the flow orientation which exists in the flowing polymer melt is re3axed as a consequence of molecular thermal movements when the melt moulded sample is cooled. When it is a question of a crystallizab]e polymer, the sample is crystallized to partially crystalline, spherulitic structure. So the polymeric material manufactured by melt moulding typically consists of folded crystalline lamellae (the thickness 100-300 A, the breadth about 1 μm) , which are surrounded by the amorphous polymer. On the other hand, the lamellae can be thought to consist of mosaic-like folded blocks (the breadth of some hund¬ reds of A) . The lamellae as a rule form ribbon-like structures, which grow from crystallization ' centres, so-called nuclei, to three-dimensional spherical spheru- litic structures. Because the polymer material which has been crystallized with the spherulitic mechanism does not show as a rule significant orientation of po¬ lymer molecules with strong covalence bonds, its me¬ chanical strength values remain on the above mentioned level. Only on the surface of the sample molecular orien¬ tation can remain because of rapid cooling in the mould (like in the case of injection moulding) . Although the reinforced resorbable composites show considerably better strength properties than melt moulded resorbable composites, it is often necessary to manufac- ture of resorbable reinforced composites quite big im¬ plants, like rods, intramedullary nai.s, screws .or plates. This is necessary because one must secure for the load carrying capacity (like bending or shear load carrying capacity) of the implants a security marginal high enough to confirm the stability of the fixation also in such a case when outer stresses or muscle stresses are directed to the fixated fracture, osteotomy, arthrodesis or joint damage, because the above mentioned stresses can clearly exceed the weight of the patient. On the other hand, such big implants which the security of the patient demand, cause quite 'big operative- traumas to the bone tissue and/or to the soft tissues when the implant e.g. is located into a drill-hole which has been drilled into the bone or the implant is fastened on the surface of the bone. With the increasing size of the implant the possibilities to a foreign body reaction increase, the reaction may grow stronger or its duration may be pro¬ longed because the implant and the resorption of the implant cause to the living tissues physical and chemi- cal stresses which are in a direct correlation to the size of the implant. So far, the elastic modulus values of resorbable implants which have been manufactured of organic mate¬ rials are at the best the order of magnitude of 10 GPa. This is a lower level of elastic modulus than the elastic moduli of cortical bones, which are typically the order of magnitude of 20 GPa and can even exceed 30 GPa. When the main goal of the surgeon is as good fixation as possible it is advantageous if the elastic modulus of the implant is as near as possible of the elastic modu¬ lus of the bone. In the ideal case the elastic moduli of the bone to be operated and of the implant are equal. Therefore it is evident that an efficient fixation of cortical bone, like long bones, needs resorbable organic composite materials which have higher elastic modulus values than those of the known materials. In this invention we have found unexpectedly that by increasing the strength and elastic modulus values of resorbable polymeric materials by orientation of the molecular structure of the material in such a way that it is at least-partially fibrillated, we get new macros- copical resorbable self-reinforced implant materials, which have considerably higher strength and elastic modulus values than those of the known resorbable im¬ plant materials. When the materials of this invention are applied as surgical fixation materials, -devices or in manu cturing of such devices one can effectively decrease the operative trauma which the implant causes and at the same time one can obtain significantly better fixation than with the known materials. This invention describes at least partially fibrillated (a) fixation materials for treatment of bone fractures, osteotomies, arthrodesis or joint damages, (b) materials for reconstruction and augmentation of bone tissue and (c) the fixation devices, reconstruction devices and augmen- tation devices like rods, plates, screws, intramedullary nails, clamps and chutes manufactured at least paxtially of the above materials using as raw material resorbable polymer, copolymer or polymer mixture. Further this invention describes the application of at least par- tially fibrillated resorbable materials and especially the application of rods, plates, screws, intramedullary nails, clamps or chutes manufactured of the above mentione materials in fixation of bone fractures, osteotomies, arthrodesis or joint damages or in augmentation or re- construction of bone tissue. The orientation and fibrillation of spherulitic polymer systems is a process, which has been studied extensively in connection with the manufacturing of thermoplastic fibres. E.g. the invention U.S. Pat. 3 161 709 describes a three phases drawing process, where the melt moulded polypropylene filament is transformed to a fibre with high mechanical tensile strength. The mechanism of the fibrillation is of its main features the following one (CL. Choy et al. Polym. Eng. Sci., _23 1983, p. 910). When a semicrystalline polymer is drawn, the molecular chains in the crystalline lamellae are aligned rapidly along the draw direction. At the same time, the spherulites are elongated and finally broken up. Crystalline blocks are torn off from the lamellae and are connected by taut tie-molecules origi- nating from partial unfolding of chains. The alternating amorphous and crystalline regions, together with the taut tie-molecules, therefore form long, thin (ca. 100 A width) microfibrils which are aligned in the draw direc¬ tion. Since the intrafibrillar tie-molecules are created at the interfaces between crystalline blocks, they lie mainly on the outside boundary of microfibrils. Tie- molecules which linked different lamellae in the starting isotropic material are now connecting different micro¬ fibrils, i.e., they become interfibrillar tie-molecules locating at the boundary layers between adjacent micro¬ fibrils. Figure 1a shows schematically, how a group of lamellae is transformed to a fibrillar structure (to a fibril which comprises a group of microfibrils) as a consequence of drawing and Figure 1b shows schematically the molecular structure inside of microfibrils and between them. Figure 1c shows schematically the structure of fibrillated polymer. This Figure shows several fibrils (one of them has been coloured grey because of clarity) which comprise several microfibrils with the length of several micrometres. The fibrillar structure is already formed at rela- tively low draw ratios λ (where λ = the length of the sample after drawing/the length of the sample before drawing). E.g. HD-polyethylene is clearly fibrillated with the λ value of 8 and polyacetal (POM) with the λ value of 3. When the drawing of the fibrillated structure is further continued (this stage of the process is called often ultra-orientation) , the fibrillar structure is deformed by shear displacement of microfibrils, giving rise to an increase in the volume fraction of extended inter- fibrillar tie-molecules. If the drawing is performed at high temperature, the perfectely aligned tie-molecules will be crytallized to form axial crystalline bridges connecting the crystalline blocks. The excellent strength and elastic modulus values of the fibrillated structure are based on the strong orien¬ tation of polymer molecules and molecular segments into the direction of the drawing (into the direction of the long axis of microfibrils) . Regardless of the high tensile strength of fibrillated fibres they cannot be applied as fixation devices of bone fractures, osteotomies, arthrodesis or joint damages, because thin fibres are flexible and therefore they do not show macroscopical bending strength and bending modulus and because of their small cross-sectional area they do not have the necessary shear load carrying capa¬ city which the macroscopical fixation device must have. Fibrillation of macroscopical polymeric samples, like rods and tubes, is known earlier in the case of bio- stable polyacetal and polyethylene (see e.g. K. Nakagawa and T. Konaka, Polymer 21_, 1986, p. 1553 and references therein) . However, the fibrillation of macroscopical samples of resorbable polymers has not been known earlier. A t least partial fibrillation of a macroscopical poly¬ mer sample can be carried out e.g. by cooling in a capillary tube flowing polymer melt rapidly to the solid state in such a way that the molecular orientation of the flowing molecules cannot relax as a consequence of molecular motions to a total or partial state of random orientation. More strong fibrillation and therefore also better mecha¬ nical properties can be achieved by a mechanical defor- mation (orientation) of macroscopical polymer samples. Usually such a mechanical deformation is done by drawing or by hydrostatic extrusion of material in such a physi¬ cal condition (in solid state) , where strong molecular structural changes of crystalline structure and amorphous structure to fibrillar state are possible. As a con¬ sequence of fibrillation the resorbable polymeric material which has been manufactured e.g. by the injection moul¬ ding or extrusion and which material initially is mainly • spherulitic of its crystalline structure, changes first partially and later on totally to a fibrillated structure which is strongly oriented in the direction of drawing or of hydrostatic extrusion. Such a resorbable material consists among other things of oblong crystalline micro¬ fibrils and of tie-molecules connecting microfibrils and of oriented amorphous regions. In a partially fib¬ rillated structure the amorphous regions between micro¬ fibrils form a more significant part of the material than in an ultraoriented material where in the extreme case amorphous material exists only as crystal defects around the ends of the polymer molecule chains. When the degree of fibrillation increases in a material its strength and elastic modulus values increase many times in comparison to the same values of non-fibrillated material. Known resorbable composite materials comprise typically randomly oriented (non-oriented) binding material phase (matrix) , which binds to each other reinforcing elements like fibres which have strongly oriented internal struc¬ ture. Such a structure has been shown schematically in Figure 2, where oriented and non-oriented molecular chains or their parts have been described with thin lines. The strength properties of the binding phase are significantly weaker than the strength properties of the reinforment elements. Therefore the strength pro¬ perties of the composite in the direction of orienta- tion of reinforcement elements increase when the amount of reinforcement elements in the material is increased. As a consequence of practical difficulties the amount of reinforcement elements cannot exceed ca. 70 weight-% of the weight of the composite. Therefore the strength properties of reinforcement elements cannot be utilized totally, because the composite contains also the weaker matrix material, which also contributes of its part to the total strength of the composite. By means of orientation and fibrillation it is possible to manufacture of resorbable polymers, copolymers and polymer alloys self-reinforced composites, where nearly the whole mass of material has been oriented in a desired way and where the amount of the amorphous phase is small. Therefore these materials show very high mechanical strength properties in the direction of orientation: tensile strength even 1000-1500 MPa and elastic modulus 20-50 GPa. Accordingly these strength values are clearly better than those of known resorbable composites and even about ten times higher than the strength values of melt moulded resorbable materials. Figure 3 shows schematically following structural units which can be seen in the fibrillated structure of polymer fibres and also in the structure of macroscopical, fib¬ rillated polymer samples like rods and tubes: crystal- line blocks which are separated from each other by amorphous material (e.g. free polymer chains, chain ends and molecular folds) , tie-molecules, which connect crystalline blocks with each other (the amount and thickness of tie-molecules increases with increasing draw ratio λ) and possible crystalline bridges between crystalline blocks. Bridges can be formed during drawing when tie-molecules are oriented and grouped themselves to bridges (CL. Choy et al. J. Polym. Sci., Polym. Phys. Ed., _j_9, 1981, p. 335-352) . The oriented fibrillated structure which is shown in Figures 1 and 3 develops already at so-called natural draw ratios 3-8. When the drawing is continued after this as an ultraorientation at a high temperature, the amount of crystalline bridges can increase very high and in the extreme case bridges and crystalline blocks form a continuous crystalline structure. The effects of tie-molecules and bridges are often similar and therefore their exact discrimination from each other is not always possible. Orientation and fibrillation can be characterized ex- perimentally by means of several methods. The orienta¬ tion function £ , which can be measured by means of x-ray diffraction measurements, characteriz s the orien¬ tation of molecular chains of the crystalline phase, f Attains as a rule already at natural drawing ratios (λ < 6) the maximum value 1. The polymeric material with spherulitic structure shows f << 1. Birefringence which can be measured by means of pola¬ rization microscope is also a quantity, which describes molecular orientation of molecular chains. As a rule it grows strongly at natural draw ratios (λ < 6) and thereafter during ultraorientation more slowly, which shows that the molecular chains of the crystalline phase are oriented into the drawing direction at natural draw ratios and the orientation of molecules in the amorphous phase continues further at higher draw ratios (CL. Choy et al. Polym. Eng. Sci., 2_3, 1983, p. 910- 922) . The formation of the fibrillated structure can be shown in many cases illustratively by studying the fibrillated material by means of optical and/or electron microscopy (see e.g. T. Konaka et al. Polymer, 2j_, 1985, p. 462). Even single fibrils which consist of microfibrils can be seen clearly in scanning electron microscopy figures which are taken of the fibrillated structure. Table 1 shows some known resorbable polymers, which can be applied in manufacturing of resorbable materials and devices of this invention. A presupposition to an effi¬ cient fibrillation is, however, that the polymer exists in a partially crystalline form. Therefore such polymers, which because of their physical structure (e.g. configu¬ ration state) are not crystallizable, cannot be effec¬ tively fibrillated. Table 1. Resorbable polymers Polymer Polyglycolide (PGA) Copolymers of glycolide: Glycolide/L-lactide copolymers (PGA/PLLA) Glycolide/trimethylene carbonate copolymers (PGA/TMC) Polylactides (PLA) Stereocopolymers of PLA: Poly-L-lactide (PLLA) Poly-DL-lac ide (PDLLA) L-lactide/DL-lactide copolymers Copolymers of PLA: Lactide/tetramethylglycolide copolymers Lactide/trimethylene carbonate copolymers Lactide/δ-valerolactone copolymers Lactide/ε-caprolactone copolymers Polydepsipeptides PLA/polyethylene oxide copolymers Unsymmetrically 3,6-substituted ρoly-1 ,4-dioxane-2,5- diones Poly-β-hydroxybutyrate (PHBA) PHBA/β-hydroxyvalerate copolymers (PHBA/HVA) continues Poly-β-hydroxypropionate (PHPA) Poly-p-dioxanone (PDS) Poly-δ-valerolactone Poly-ε-caprolactone Methylmethacrylate-N-vinyl pyrrolidone copolymers Polyesteramides Polyesters of oxalic acid Polydihydropyrans Polyalky1-2-cyanoacrylates Polyurethanes (PU) Polyvinylalcohol (PVA) Polypeptides Poly-β-malic acid (PMLA) Poly-β-alkanoic acids R eference: P. Tδrmala, S. Vainionpaa and P. Rokkanen in I VA 's Beijer Symposium "Biomaterials and Biocompatibility" Stockholm, Sweden, August 25-26, 1987. At least partially fibrillated and especially ultra- oriented, resorbable polymer materials are an especially advantageous special case of oriented, self-reinforced resorbable composite materials where the oriented rein¬ forcement elements (crystalline blocks, tie-molecules and crystalline bridges) form and/or group themselves during the mechanical defromation and where the phase which binds the above mentiones structural units is formed among other things of the following structural elements: amorphous phse, the interfaces between crys¬ talline blocks and the interfaces between crystalline bridges and micrifibrils, which structural elements are also typically oriented strongly in the direction of deformation. The resorbable, at partially fibrillated implant mate¬ rials and osteosynthesis devices of this invention differ by several unexpected ways from known resorbable i of this invention have as a consequence of strong orien¬ tation and of at least partially fibrillated structures excellent tensile-, bending- and shear strength proper¬ ties and elastic modulus properties. This makes possible to apply in orthopaedics and traumatology thinner and smaller rods, plates, screws, nails and clamps etc. than earlier is known. This decreases advantageously the operative trauma and the foreign body load caused by the implant to living tissues. Further the excellent mechanical strength- and elastic modulus properties make possible to apply the materials, implants and devices of this invention also in demanding fixation operations of long bone fractures, osteotomies and arthrodesis. It has been found also unexpectedly that the implants of this invention retain their mechanical properties in hydrolytic conditions longer than the implants of equal size which have have been manufactured of the known-materials. This makes also possible to apply the materials and devices of this invention in treatment of such slowly recovering bone fractures, osteotomies and arthrodesis, where the known materials and implants cannot be applied. __ The at least partially fibrillated rods, tubes, plates etc. profiles of this invention can be applied as such as fixation devices e.g. by the ways described in the inventions FI Pat. No. 69402 and 69403 or the materials can be formed to different kind of fixation devices like screws, rods with scaly covering and other profiled structures and clamps or other bended structures, because in this invention has been also found unexpectedly that the oriented resorbable materials can be hot-worked mechanically at high temperatures without loosing the fibrillated structure. This makes possible e.g. the manufacturing of especially strong and tough screws of the at least partially fibrillated rods of this in¬ vention. It is natural that fibrillated resorbable materials can contain additionally different kinds of additives or auxiliary materials to make the processing of the material more easy (e.g. stabilizators, antioxidants or plasticizers) or to change its properties (e.g. plasticizers or powder-like ceramic materials) or to make its handling more easy (e.g. colours) . The stiff and strong resorbable fixation materials of this invention can be applied in the form of rods, plates or other profiles also in manufacturing of bigger fixation devices as reinforcement elements for example by packing into a cylindrical, oblong injection moulding mould fibrillated rods and by filling the mould then by injecting into it suitable resorbable matrix polymer melt. When the injection is carried out from one end of the oblong mould, the injected melt flows in the direc¬ tion -of resorbable reinforcement elements. When the matrix material (polymer melt) flows and solidifies rapidly,into it is formed an advantageous orientation in the direction of the reinforcement elements. The stiff and strong fixation rods or plates of this invention can be used also to construct stiff net-like and plate-like structures, which can resemble of their mechanical properties more metallic nets than nets which are manufactured of organic textile fibres. Figure 4 shows schematically some types of net structures which are constructed of stiff, strong resorbable rods. Part of the rods has been described as white ,and part as black because of clarity. Such nets can be applied as such e.g. to treatment of comminuted fractures by com¬ bining the comminuted parts of broken bone to each other and by bending the net around the parts of broken bone to support it and by fixing the net e.g. with resorbable sutures or clamps. Such nets of this inven- tion can be manufactured also e.g. by hot-pressing them to curved plates, chutes or box-like etc. corresponding structures, which can be applied to the reconstruction of bone etc. in such a way that a defect in bone tissue (a hole, a cavity, a cyst, etc.) is filled with tissue compatible ceramic powder like hydroxyapatite or tri- calciumphosphate and the curved net is fixed on the defect to a cover, which immobilizes ceramic particles and prevents their movements from the defect. Because such nets of this invention are stiff they function in this connection as significantly more effective immobilizers than the known flexible nets which are manufactured of resorbable fibres. Figure 5 shows schematically a net structure of this invention which is manufactured of resorbable rods and which has been bended to the form of a chute e.g. by hot pressing. Such a chute can be applied especially advantageously with ceramic materials to augmentation of bone tissue of alveolar ridges in the following way. First the subperiosteal tunnel is made surgically below the gingival tissue on the surface of the alveolar ridge. The resorbable tube is pushed inside of the tunnel in such a way that the convex surface of the chute is di¬ rected towards the gingival tissue and the end sur¬ faces of the sides of the chute are placed on the al¬ veolar ridge. This situation has been described sche- matically in Figure 6 in the case of an operation which is done to the right side of the mandible. After in¬ stallation of the chute it can be filled with ceramic bone graft powder and after that the operation incision can be closed. If necessary, it is possible to place on the same alveolar ridge several chutes after another. Such a chute prevents the movements of ceramic powder which has been packed below it. At the same time bone and connective tissue cells grow from the bone tissue of alveolar ridge and from the surrounding soft tissues into the ceramic powder by immobilizing it at last to a part of the bone tissue of alveolar ridge. The resorb¬ able chute is resorbed at the same time or later. Ceramic powders and pieces can be applied also in many other ways to augmentation or reconstruction of bone tissue (as bone graft .materials) . Ceramic materials (bioceramics) , which are tissue compa- tible and/or which form chemical bonds with bone tissue and/or which promote the growth of bone tissue, are e.g. calciumphosphate : apatites like hydroxyapatit , HA, Ca. - (PO g (OH) - (R.E. Luede ann et al. , Second World Congress on Biomaterials (SWCB) , Washington, D.C., 1984, p. 224) , trade names like Durapatite , Calcitite, Alveograf and Permagraft; fluoroapatites ; tricalciumphosphates (TCP) (e.g. trade name Synthograft) and dicalciumphosphates (DCP magnesiumcalciumphosphates , β-TCMP (A. Ruggeri et al. , Europ. Congr. on Biomaterials (ECB) , Bologna, Italy, 1986, Abstracts, p. 86) ; mixtures of HA and TCP (E. Gruendel et al. , ECB, Bologna, Italy, 1986, Abstracts, .p. 5, p. 32) aluminiumoxide ceramics; bioglasses like SiO--CaO-Na-0-P-0 e.g. Bioglass 45S (structure: SiO- -45 wt-%, CaO ' 24,5 %, a 2 0 24,5 % and P_0- 6 %) (C.S. Kucheria et al. , SWBC, Washington, D.C. , 1984, p. 214) and glass ceramics with apatites, e.g. MgO 4,6 wt-%, CaO- 44,9 %, SiO- 34,2 %, P-O- 16,3 % and CaF 0,5 % (T. Kokubo et al . , SWBC, Washing ton, D.C. , 1984, p. 351) and calciumcarbonate (F. Souyris ■ et al. , EBC, Bologna, Italy, 1986, Abstracts, p. 41) . The applications of the above ceramic materials as synthe¬ tic bone grafts have been studied by different means by using them for example both as ' porous and dense powder materials and as porous and dense macroscopical samples as bone grafts. Also ceramic powder - polymer composites have been studied in this means (e.g. W. Bonfield et al . SWBC, Washington, D.C , 1984, p. 77) . The resorbable strong and stiff materials of this inven¬ tion can be applied in many different ways combined with porous bioceramics to biocomposites . The mechanical properties, especially the impact strength, bending strength and shear strength of such composites are sig¬ nificantly better than the corresponding properties of porous bioceramics. The invention FI Pat. Appl. 863573 describes several possibilities to combine resorbable polymeric materials and bioceramics. Those principles can be applied also when the materials of this invention are used in combination with bioceramics. This invention has been illustrated by means of the following examples. EXAMPLE 1. Poly-L-lactide (ELLA) (M = 600.000) was injection moulded to cylindrical rods with a diameter (0) 4 mm. The rods were drawn to the drawing ratio λ = 7 at temperatures from room t .emp r erature to Tm -40 C (where Tm = the melting point of the polymer) . The fibrillated structure of the drawn rods was seen microscopically. Part of the rods was drawn further to a drawing ratio λ = 12 (ultraorien¬ tation) . As reference samples were sintered self-rein- forced rods (0 = 1.5 mm) of ELLA fibres (tensile strengt 800 MEa, 0 = 15 μm) which rods were manufactured by a method described in FI Pat. Appl. 851828. Following strength values were measured for the injec¬ tion moulded, fibrillated and sintered self-reinforced rods: tensile strength, elastic modulus and shear strength. The results of measurements are given in Table 1. Table 1. Strength properties of PLLA rods Sample Manuf cturing Rod Tensile Elastic Shear N:o method thickness strength strength strength (mm) (MPa) (GPa) (MPa) 1 Injection 4 80 5.5 70 moulding 2 Injection 1.4 560 14 360 moulding + fibrillation (λ = 7) 3 Injection 1.2 800 17 470 moulding + fibrillation (λ = 12) 4 Self-rein- 1.5 400 10 260 forcing (sintering) Table 1 shows that the strength properties of the fib¬ rillated, resorbable rods of this invention are clearly better than the strength properties of the known resorb¬ able materials. EXAMPLE 2. Resorbable rods of Example 1 (the length 25 mm) were applied to fixation of the arthrodesis of the proximal phalanx of thumb by removing the both joint surfaces, by joining the uncovered bone surfaces temporarily to each others by clamps to an arthrodesis surface, by drilling through the arthrodesis surface ' two drilling channels and by tapping into the drilling channels the resorbable fixation rods. 20 patient were operated. The average area of the arthrodesis surfaces was ca. 2 170 mm . The calculatory shear load carrying capacity of the fixation was 1100 N, when two fibrillated rods N:o 2 were applied. The proportion of drill channels (which describes the operative trauma) of the arthro¬ desis surface was 1.8 %. The corresponding values were for fibrillated rods N:o 3 1060 N and 1.3 % and for sintered rods N:o 4 920 N and 2.1 %. Accordingly the fibrillated rods give a stronger fixation than the sintered rods. Also the operative trauma was smaller in the case of the fibrillated rods. Injection moulded rods were not applied in fixation, because they should have caused clearly bigger operative trauma (ca. 15 %) than the other materials. EXAMPLE 3. Injection moulding was applied to manufacture rods (0 = 3.2 mm) of the following resorbable polymers: polyglycolide (PGA) (M = 100.000) , glycolide/lactide copolymer (PGA/PLA, the molar ratio 87/T3, M w = 120.000) , poly-β-hydroxybutyrate (PHBA) (M = 500.000) and poly-p- dioxanone (PDS) . (Mw = 300.000) . Polarization microscopy and scanning electron microscopy showed that, exclusive of a thin surface layer, the rods had a spherulitic crystalline structure. The mel¬ ting p e oints (Tm) of the materials of the rods were mea- sured by differential scanning calorimetry (DSC) and the following values were obtained for Tm: PGA (225°C) , PGA/PLA (180°C) , PHBA (175°C) and PDS (110°C). The tensile strengths of the rods were: PGA (60 MPa) , PGA/PLA (50 MPa) , PHBA (30 MPa) and PDS (40 MPa) . The rods were fibrillated by drawing them at temperatures from room temperature to T -10°C to drawing ratios λ = 8-16. The diameters of the fibrillated rods were between 0.8 mm and 1.1 mm. The tensile strengths of the fibrillated rods were: PGA (600 MPa) , PGA/PLA (550 MPa) , PHBA (400 MPa) and PDS (300 MPa) . EXAMPLE 4. Fibrillated PGA rods of Example 3 and self-reinforced, sintered rods (0 = 1.1 mm; which were manufactured of PGA sutures trade name Dexon, size 3-0) which were 50 mm long, were hydrolyzed at 37 C in distilled water 5 and 7 weeks. The shear load carrying capacities of fibrillated (f) and sintered (s) rods were after manu¬ facturing f: 570 N and s: 300 N. After hydrolysis of 5 weeks the corresponding values were f: 160 N and s: 30 N. After 7 weeks hydrolysis the sintered rods had already lost their shear load carrying capacity, but the fibrillated rods showed still 75 N shear load carry¬ ing capacity. EXAMPLE 5. Fibrillated PGA rods of Example 3 (the length 50 mm, 0 1.1 mm) were bended in a mould to clamps shown sche¬ matically in Figure 7a in a bending temperature of 180°C. Corresponding self-reinforced clamps were manufactured of PGA sutures (trade name Dexon, size 3-0) by sintering them according to the method of FI Pat. Appl. 851828 at elevated temperature and pressure in a clamp mould. The tensile load carrying capacity of fibrillated and sin¬ tered clamps was measured by fixing the 10 mm long arms of clamps into holes which were in drawing jaws of a tensile testing machine and by drawing the clamps accor¬ ding to Figure 7b. The clamps were broken typically according to Figure 7b from the base of the arm. The fib¬ rillated clamps of this invention showed mean tensile load carrying capacity of 300 N and the sintered clamps a corresponding value of 120 N. EXAMPLE 6. Fibrillated PLLA rods n:o 4 of Example 1 were compression moulded in a mould with a screw-like mould cavity at about 160 C temperature to resorbable 30 mm long screws, with the core thickness of 1.1 mm and the height of threads 0.5 mm and the distance between the threads 0.8 mm. The tensile load carrying capacity of the screws was 300 N. The corresponding screws which were manufactu- red by injection moulding of PLLA showed a tensile load carrying capacity of 80 N and the corresponding self- reinforced, sintered rods which were manufactured, of PLLA fibres of Example 1 showed a tensile load carrying capacity of 150 N. EXAMPLE 7. Fibrillated PLLA rods N:o 3 (the length 60 mm, 0 1.2 mm) of Example 1 were coated with PDLLA (M = 100.000) by immersing the rods in a 5-% acetone solution of PDLLA and by evaporating the solvent. The operation was re- peated so many times that the rods had at last 40 w-% of PDLLA. The coated rods were compressed in a cylindri- - cal mould (the length 60 mm and 0 4.5 mm) at 160°C to cylindrical resorbable rods which showed a bending strengt of 450 MPa and a bending modulus of 14 MPa. EXAMPLE 8. ' Porous hydroxyapatite (HA-) rods (open porosity about 50 %, 0 = 4 mm and the length 60 mm) , which contained on their outer surface 6 longitudinal grooves shown sche¬ matically in Figure 8a and in a crosssectional. Figure 8b (the cross-section plane A-A of Figure 8a) , and resorb- able reinforcing materials of this invention were applied to manufacture biocomposite rods (intramedullary nails) . The used reinforcing element materials were fibrillated PLLA rods (the length 60 mm, 0 1.0 mm) of Example 1. Also PLLA fibre bundles coated with PDLLA (ca. 0.1 mm thic slightly twisted bundle of fibres; 0 of single fibres 15 μm and tensile strength 800 MPa) were applied as shown below. A 5-% (w/v) acetone solution of PDLLA (M w = 100.000) was spread to the grooves of HA-rods and the fibrillated resorbable rods which were immersed in the same solution were pushed into the grooves. The rods were adhered into the grooves when acetone was evaporated. HA-rods with the fibrillated PLLA rods in their grooves were coated with PLLA fibre bundle (coated with PDLLA) by filament winding method. The filament winding was carried out at 150 C temperature in such a way that the HA-rods were coated with several fibre bundle layers with different directions so that the fibre bundle layer was at the most 0.4 mm thick. The filament winding was carried out in such a way that between fibre bundles remained areas of rod surface without fibres. These uncovered areas of HA-rods could be seen on the surface of biocomposite rods as is shown schematically in Fi¬ gure 8c. The resorbable reinforced coating of rods was pressed smooth in a cylindrical mould (0 = 5.0 mm) . These biocomposites showed a bending strength of 140 MPa, when the bending strength of mere HA-rods was 12 MPa.- The above biocomposite rods were applied to fixation of osteotomies of rabbit femur in the following way. The osteotomy was done with a diamond saw to the .uncovered proximal part of rabbit femur about 1 cm from the neck of the femur. The osteotomy was fixed with clamps. A drill hole (0 = 5 mm) was drilled through the greater trocanter vertically into the intramedullary channel of femur. The biocomposite rod was tapped into the drill hole so that the upper end of the rod.was located on the level of the bone surface. The clamps were removed and soft tissues were closed with a resorbable suture. The animals were returned to their cages and after anes¬ thesia they could move immediately freely. 20 test ani¬ mals were used. The follow-up time of 6 months showed that all the osteotomies were healed well. Histological examinations of bone-biocomposite test samples showed growth of bone tissue from femoral bone into the open porosity of HA-rods.

Claims: Claims : 1. Surgical materials and devices, which have been manufactured of fesorbable polymer, copolymer or polymer mixture and can be used as bone fracture, osteotomy, arthrodesis or joint damage fixation materials or their components and as bone tissue reconstruction- an augmentation materials or their components, c h a r a c t e r i s e d in that the mentioned materials and devices or their components contain at least partially fibrillated structural units. 2. Surgical materials and devices and their components according to claim ^ c h a r a c t e r¬ i s e d in that they contain at least partially ultraoriented structural units. 3. Surgical materials and devices or their components according to claims 1 and 2, c h a r a c¬ t e r i s e d in that they show shear strength value of at least 200 MPa and shear modulus value of at least 4 GPa. 4. Surgical materials and devices or their components according to claims 1 and 2, c h a r a c- t e r i s e d in that they show bending strength value of at least 200 MPa and bending modulus value of at least 4 GPa. 5. Surgical materials and devices or their components according to claims 1-4, c h a r a c¬ t e r i s e d in that they have been constructed to net-like structures. 6. Surgical materials and devices or their components according to claim 5, c h a r a c t e r- i s e d in that the net-like structures have been formed to formed pieces like curve nets and chutes. 7. Use of surgical materials and devices or their components according to claims 1-6 in fixation of bone fractures, osteotomies, arthrodesis or joint damages or in reconstruction or augmentation of bone tissue as formed piece like rod, plate, screw, intramedullary nail and clamp and as reconstruction and augmentation material or device of bone tissue like as plate or chute.

Inventors: HEPONEN VELI-PEKKA, LAIHO JUHA, POHJONEN TIMO, ROKKANEN PENTTI, TOERMAELAE PERTTI, VAINIONPAEAE SEPPO, HEPONEN, VELI-PEKKA, LAIHO, JUHA, POHJONEN, TIMO, ROKKANEN, PENTTI, TOERMAELAE, PERTTI, VAINIONPAEAE, SEPPO
Applicants: MATERIALS CONSULTANTS OY
Application year: 1987
Main classification: A61L31
IPC codes: A61B17, A61C8, A61F2, A61L26, A61L27, A61L31