PHOTOGRAPHIC SUPPORT AND COLOR PHOTOSENSITIVE MATERIAL

Abstract: The present invention relates to a photographic support having a secondary diffuse-reflective surface, and a color pho­ tosensitive material comprising at least one silver halide emul­ sion layer formed on the secondary diffuse-reflective surface of a photographic support. A photographic support of the present invention provides an image having remarkably im­ proved brightness, saturation, tone reproducibility in shadow areas and sharpness. A color photosensitive material of the present invention provides an image having remarkably im­ proved brightness, saturation, tone reproducibility in shades and sharpness and also capable of rapid development.

Description: The present invention relates to a color photosensitive material for prints capable of providing an image having remarkably improved brightness, saturation, tone reproducibility in shades and sharpness and also capable of rapid development. Transparent plastic films such as TAC and PET films are known as photographic supports, and papers, synthetic papers, plastic films containing a white pigment, glass plates and metal plates (such as an aluminum plate having a surface processed by anodic oxidation) are known as reflective materials. To improve the whiteness of the support, it has been proposed to mix or to incorporate a fine powder of a metal oxide or an inorganic compound (such as titanium oxide, barium sulfate or magnesium oxide) as a sizing agent in the surface layer of the support. However, when the whiteness of the support is increased, the sharpness of the image is usually reduced, while the white reproducibility is improved. To solve this problem, it has been proposed to incorporate an anti-irradiation dye in a silver halide-containing photosensitive layer provided on the support or to provide an antihalation layer. Further, so-called Daguerreotype has been known since the early nineteenth century. In this method, gaseous iodine is sprayed over a well polished silver plate to form an AgI layer by the chemical reaction and the development is conducted with gaseous mercury after the image exposure to form a photographic image. However, this method has defects that, since the silver plate used as the support is not well prepared and it is subjected directly to the chemical processes, the surface of the silver plate is stained and its initial mirror plane cannot be maintained and that since the silver/mercury image is deposited directly on the silver surface to mask the surface, the obtained image has only poor brightness and sharpness. When a photographic material comprising ordinary emulsion layers formed on an aluminum support having the surface having a metallic gloss which highly reflects the light is used, the obtained image is only slightly lighter than that obtained by using a baryta paper. When microcapsules of a silver halide emulsion are applied to the support to form a single layer, bright transparent grains can be seen (see, for example, Japanese Patent Publication No. 49-33783). The image thus formed cannot be easily seen due to the reflected light and very small flaws on the surface become unfavorably conspicious. Further, it is known to provide an antistatic layer of a metal such as aluminum or chromium by vacuum deposition (for example, British Patent No. 1340403 and Japanese Patent Publication Nos. 59-41573 and 59-10420). However, these publications are silent on the improvement in or relating to the reproduction of the images and they have no relation with the present invention. Ordinary color photosensitive materials comprise, on a support (such as a film, film containing a white pigment, paper, e.g. baryta paper or paper having water-resistant resin layers on both surfaces), an antihalation layer, a red-sensitive layer, a green-sensitive layer, a yellow filter layer, a blue-sensitive layer or a protective layer, suitably. To form an excellent color image, investigations were made on transparency and reduction in the thickness of the layers, layer structure, prevention of irradiation or halation, spectral absorbing characteristics of colored dyes prepared from color couplers and transparency of the material. For improving particularly the sharpness, the silver halide emulsions such as halogen compositions and grain size are selected so as to exhibit the interlayer effects in the development, and investigations of the layer structure were made. It was also proposed that a material which releases a compound having an effect of inhibiting or accelerating the development in the color development step is used. However, they are yet insufficient particularly when a color image is formed on a reflective support such as a color photographic printing paper. It is known that a bright image can be obtained by using a photosensitive material prepared by applying microcapsules of a silver halide emulsion on an aluminum substrate surface which reflects the light well and which has a metallic gloss (see, for example, Japanese Patent Publication No. 49-33783). However, although the brightness of the image thus obtained by using the photosensitive material comprising, on the aluminum support, a laminate of ordinary emulsion layers is slightly improved, it is yet unsatisfactory. It is also known that the image thus formed cannot be easily seen due to the reflected light and that very small flaws on the surface become unfavorably conspicious. A lithographic plate comprising, on an aluminum support, silver halide emulsion layers is known (see, for example, British Patent No. 1227603 and Japanese Patent Public Disclosure No. 54-90053). The aluminum support used in the lithography has the surface processed by, for example, graining and, therefore, it does not have the above-described effects. Under these circumstances, processes for overcoming the defects by, for example, preventing the halation have been proposed (for example, Japanese Patent Public Disclosure No. 54-124927). Further, color image-forming materials do not have these effects. It is also known that a layer of a metal such as aluminum or chromium is formed by vacuum deposition for obtaining antistatic effects (for example, British Patent No. 130403, and Japanese Patent Publication Nos. 59-41573 and 59-10420). However, they are silent on the improvement of the color image and they have no relation with the present invention. FR-A-1349217 discloses an article for the reproduction of images comprising at least one layer containing a recording of an image, an underlying reflection layer and an uneven surface. It is the object of the present invention to provide a color photographic material capable of forming an excellent color image having an improved saturation and gradation reproduction in shades and having a remarkable improved sharpness particularly in the high frequency region. Said object is achieved by a color photosensitive material comprising two or more silver halide emulsion layers having different spectral sensitivities, a thin solid metal film layer having a secondary diffuse-reflective surface, and a substrate, wherein said thin solid film layer is located between the emulsion layers and the substrate, and wherein said thin solid metal film layer has a reflectance of at least 0.5 and an average uneveness of 0.1 to 2000 unevenness/mm. Fig. 1 shows spectral reflectance curves. Figs. 2 to 4 show the results of the examination of the sectional shapes. Figs. 5 to 7 show spectral absorption curves. Fig. 8 shows relationship between CTF and the frequency. Fig. 9 shows spectral transmission curves obtained through a band-pass filter. Fig. 10 shows spectral reflectance curves. Fig. 11 shows the dependence of diffuse-reflected light on the angle distribution, Now, a detailed description will be made on the support and the color photosensitive material of the present invention. (Photographic support) The reflection on the surfaces of substances are usually roughly classified into a mirror reflection and diffuse reflection. Further, the diffuse reflection can be classified into the primary diffuse reflection and the secondary diffuse reflection. The mirror reflection is the reflection on a smooth surface in accordance with the regular reflection law. The diffuse reflection is observed on the surfaces of papers, coatings, woods and walls, wherein incident light does not only reflect regularly but also irregularly on the surface. The secondary diffuse reflection is observed on all surfaces having minute slant boundaries such as the surface of a ground glass or abraded metal surface. The term "secondary diffuse-reflection" herein indicates a reflection occurring on a smooth mirror surface but on which very small unevennesses are provided to form boundaries thereon. The diffuse-reflected light can be deemed as a collection of regularly reflected lights on the respective, very small reflection surfaces. This is why the secondary diffuse reflection is called "(collected) reflections on small mirror planes" as defined in paragraph 1, chapter 18 in "Shikisai Kagaku Handbook" Edition 5 edited by Nippon Shikisai Gakkai and published by Tokyo Daigaku Shuppan-kai in 1985. The primary diffuse reflection can be distinguished from the secondary diffuse reflection by a difference in the reflectance R. The term "secondary diffuse reflection" herein indicates that the reflectance R is at least 0.5. Therefore, the secondary diffuse-reflective surface according to the present invention has a reflectance R of at least 0.5, preferably 0.7 to 1.0. The reflectance R of a light of rectangular irradiation on the smooth surface of a given material can be determined by means of a spectrophotometer. The secondary diffuse-reflective surface can also be estimated, according to the total reflection measured by a spectrophotometer having an integrating sphere. The term "primary diffuse reflection" means that when a light-transmitting solid is finely pulverized and irradiated with light, the incident light is diffused by the total reflection or the reflection on a part of the surface. The mirror reflection can be distinguished from the diffuse reflection according to the difference in the spectral reflectance. The spectral reflectance is determined as follows: Monochromatic light of 550 nm is irradiated at an angle of 7° from normal line of a sample. A regular reflection fraction is eliminated by providing a trap located at a circumferential angle of 10° from center of incident light and fractions ranging within a circumferential angle of 90° from normal line other than the fraction eliminated by the trap are integrated by an integrating sphere. The spectral reflectance is shown by percentage on the basis of incident light. The secondary diffuse-reflection in the present invention indicates that the spectral reflectance (determined with monochromatic light of 550 nm) is at least 5%. Therefore, the secondary diffuse-reflective surface according to the present invention has a spectral reflectance (monochromatic light of 550 nm) of at least 5%, preferably at least 10% and more preferably at least 20%. The spectral reflectance can be determined with, for example, Color Analyzer 307 of Hitachi, Ltd. Thus, the secondary diffuse-reflection of the present invention can be distinguished from the mirror reflection or the primary diffuse-reflection according to the difference in the reflectance R of the light of the rectangular irradiation on the surface-constituting material and the spectral reflectance determined by means of a spectrophotometer such as the above-mentioned Hitachi Color Analyzer with the trap. The solids, preferably metals, used for providing the secondary diffuse-reflective surface include, for example, metals described on pages 174 to 184 of F. Benford et al., J. Opt. Soc. Amer., 32 (1942) such as silver, aluminum, gold, copper, chromium/nickel alloy, platinum and alloys of them, e.g. aluminum/magnesium alloy, aluminum/copper alloy, aluminum/antimony alloy and brass. The surface of the thin solid film layer, preferably thin metal film layer, having the secondary diffuse-reflecting properties is formed as follows: The mirror-reflective surface of a metal plate is patterned at the time of rolling; it is mechanically processed with, for example, a brush having a suitable rigidity; a jet stream of fine particles of an abrasive such as PUMICE is injected to conduct the graining; or it is etched by an electrolytic method. The thin metal film layer having such reflective properties can be formed on a substrate by lamination to form the support of the present invention. For the formation of a thin metal film layer, various methods are known such as a vacuum deposition method, a sputtering method, an ion plating method, an electrodeposition method and a nonelectrolytic plating method. One or more thin film layers can be formed on a given substrate by these methods. When the product has a mirror reflective surface, it can be converted to the secondary diffuse-reflective surface by the above-mentioned method. The surface unevennesses can be examined by embedding and fixing a sample in a resin, cutting the obtained product according to ultramicrotomy and observing the section of the piece with an electron microscope. The surface unevennesses can be determined directly with a sectional shape-measuring device by the irradiation with electron rays. The degree of accuracy is up to submicrometers. The number of unevennesses can be determined in terms of the frequency of the surface roughness. The average frequency is preferably 0.1 to 2000/mm and more preferably 1 to 1000/mm. When the support of the material of the present invention is used, the visual angle in the observation of the image is widened and the light source is enlarged from points into planes to provide a clearer image. The visual angle can be optimized, according to the directivity of reflected light from the surface. Further, the brightness in the highlights in the image, saturation of the image and the reproducibility of the gradation in shadows are remarkably improved. In addition, the sharpness of the image is surprisingly improved. The substrates of the supports of the material of the the present invention may be those usually used heretofore such as plastic films, papers, RC-papers, synthetic papers and metal plates. Among them, papers and RC-papers are preferred. An aluminum foil having the unevennesses previously provided according to the present invention can be laminated with the RC paper having a low-density polyethylene layer. The thickness of the support is preferably from 50 to 300 µm. A silver halide emulsion layer can be formed on the support of the material of the present invention via a priming layer. The priming layer comprises a thermoplastic resin such as polyethylene or polypropylene or an ionomer resin containing an epoxy adhesive. A gelatin or gelatin/silver halide emulsion layer can be formed thereon after a corona discharge process or without this process. The prime layer has effects of increasing the adhesion of the silver halide emulsion layer and inhibiting harmful effects of the support on the silver halide emulsion layer such as spot formation, fogging and deterioration of the storage stability. The prime layer is formed uniformly and it is preferably thin. The thickness of the layer is less than 5 µm, preferably less than 2 µm. If necessary, a small amount (such as 1 g/m² or less) of fine grains having the primary diffuse-reflecting properties can be incorporated in the layers such as the priming layer or, alternatively, fine dispersed particles of latexes or a high-boiling organic solvent having the primary diffuse-reflecting properties can be incorporated therein. Further, it is also possible to incorporate a fine powder of titanium oxide or barium sulfate in the substrate and pores are provided in the thin metal film layer provided on the surface thereof according to the present invention to partially replace the secondary diffuse-reflection with the primary diffuse-reflection. As a result, the visual angle of the observation can be widened without reducing the sharpness. The support having the secondary diffuse-reflective surface of the material of the present invention can be prepared by patterning a metal film in the rolling step as described above. The metals include, for example, silver, aluminum, gold, copper, chromium-nickel, platinum and alloys of them. The support of the present invention is widely usable as a photographic reflective support. It is possible to form a silver halide emulsion layer for black-and-white printing paper on the support, via a priming layer if necessary, and to form a protective layer thereon. Further, a photosensitive material for color photographic paper can be prepared by forming two or more photosensitive silver halide emulsion layers having different spectral sensitivities and containing different color couplers, which emulsions are the same as those used in the preparation of ordinary color photographic papers. The support of the material of the present invention is usable for the preparation of reversal color photosensitive materials, color photographic papers of direct positive type and color copying materials of direct positive type by photo-fogging method. The support is also usable for the preparation of printing photosensitive materials of SDB system by forming, on the support, red-sensitive, green-sensitive and blue-sensitive silver halide emulsion layers each comprising silver halide grains having a different spectral sensitivity and a dye usable in silver dye bleach (SDB) method. A mordanting layer can be formed on the support of the material of the present invention to prepare a material for forming a color image by diffusing a color releasing dye and transferring it. Physical development centers can be provided in the priming layer on the support of the material of the present invention to prepare a silver image-forming material of silver diffuse transfer type. The photographic support of the material of the present invention can be used for the preparation of heat development-type photosensitive materials and/or dye-fixing materials (image-receiving materials) described in U.S. Patent No. 4,500,626, Japanese Patent Public Disclosure Nos. 60-133449 and 59-218443 and Japanese Patent Application No. 60-79709 (Japanese Patent Public Disclosure No. 61-238056). (Silver halide emulsion layers) At least one silver halide emulsion layer is formed on the secondary diffuse-reflective surface of the support in the present invention. The description will be made on the silver halide emulsion layers. (a) Silver halide emulsion layer RL: This layer mainly comprises silver halide grains having a spectral sensitivity in the wavelength region of 580 to 700 nm and a cyan coupler. The cyan couplers contained in the RL layer are classified into oil-protecting naphthol couplers and phenol couplers. Typical examples of the naphthol couplers include those described in U.S. Patent No. 2,474,293 and preferably oxygen-linked coupling-off type 2-equivalent naphthol couplers described in U.S. Patent Nos. 4,052,212, 4,146,396, 4,228,233 and 4,296,200. Examples of the phenol couplers are described in U.S. Patent Nos. 2,369,929, 2,801,171, 2,772,162 and 2,895,826. Cyan couplers having excellent fastness to humidity and temperature are preferably used in the present invention. Typical examples of them include phenolic cyan couplers having an alkyl group higher than an ethyl group inclusive at the m-position of the phenol nucleus as described in U.S. Patent No. 3,772,002, 2,5-diacylamino-substituted phenolic couplers described in U.S. Patent Nos. 2,772,162, 3,758,308, 4,126,396, 4,334,011 and 4,327,173, West German Patent Public Disclosure No. 3,329,729 and European Patent No. 121,365 and phenolic couplers having a phenylureido group at position 2 and an acylamino group at position 5 as described in U.S. Patent No. 3,446,622, 4,333,999, 4,451,559 and 4,427,767. The couplers of the following general formulae (I) and (II) are particularly preferred: (b) Silver halide emulsion layer GL: This layer mainly comprises silver halide grains having a spectral sensitivity in the wavelength region of 500 to 580 nm and a magenta coupler. Examples of the magenta couplers contained in GL include oil-protecting indazolone and cyanoacetyl couplers, preferably 5-pyrazolone and pyrazoloazole couplers such as pyrazolotriazoles. Among the 5-pyrazolone couplers, those having an arylamino group or an acylamino group at position 3 are preferred from the viewpoint of the hue of the colored dye or the color density. Typical examples of them are described in U.S. Patent Nos. 2,311,082, 2,343,703, 2,600,788, 2,908,573, 3,062,653, 3,152,896 and 3,936,015. As the release groups of the 2-equivalent 5-pyrazolone couplers, nitrogen-linked coupling-off groups described in U.S. Patent No. 4,310,619 and arylthio groups described in U.S. Patent No. 4,351,897 are particularly preferred. When 5-pyrazolone couplers having a ballast group described in European Patent No. 73,636 are used, a high color density can be obtained. Examples of the pyrazoloazole couplers include pyrazolobenzimidazoles described in U.S. Patent No. 3,061,432 and preferably pyrazolo(5,1-c)(1,2,4)triazoles described in U.S. Patent No. 3,725,067, pyrazolotetrazoles described in Research Disclosure No. 24220 (June, 1984) and pyrazolopyrazoles described in Research Disclosrue No. 24230 (June, 1984) and Japanese Patent Public Disclosure No. 60-43659. Imidazo(1,2-b)pyrazoles described in U.S. Patent No. 4,500,630 are preferred because of low yellow sub-absorption and excellent light fastness of the developed dye, and pyrazolo(1,5-b)(1,2,4)triazole described in U.S. Patent No. 4,540,654 is particularly preferred. Couplers of the following general formulae (III) and (IV) are particularly preferred: (c) Silver halide emulsion layer BL: This layer mainly comprises silver halide grains having a spectral sensitivity in a wavelength region of 400 to 500 nm and a yellow coupler. Typical examples of the yellow couplers contained in BL include oil-protecting acylacetamide couplers. Examples of them are described in U.S. Patent Nos. 2,407,210, 2,875,057 and 3,265,506. 2-Equivalent yellow couplers are preferably used in the present invention. They include, for example, yellow couplers of the oxygen-linked coupling-off type as described in U.S. Patent Nos. 3,408,194, 3,447,928, 3,933,501 and 4,022,620 and yellow couplers of the nitrogen-linked coupling-off type as described in Japanese Patent Publication No. 58-10739, U.S. Patent Nos. 4,401,752 and 4,326,024, RD 18053 (April, 1979), British Patent No. 1,425,020, West German Patent Public Disclosure Nos. 2,219,917, 2,261,361, 2,329,587 and 2,433,812. α-Pivaloylacetanilide couplers are excellent in fastness, particularly light fastness, of the colored dye. Couplers of the following general formula (V) are particularly preferred: In formulae (I) - (V), R₁, R₄ and R₅ each represent an aliphatic group, an aromatic group, a heterocyclic group, an aromatic amino group or a heterocyclic amino group, R₂ represents an aliphatic group, R₃ and R₆ each represent a hydrogen atom, a halogen atom, an aliphatic group, an aliphatic oxy group or an acylamino group, R₇ and R₉ each represent a substituted or unsubstituted phenyl group, R₈ represents a hydrogen atom, an aliphatic or aromatic acyl group or an aliphatic or aromatic sulfonyl group, R₁₀ represents a hydrogen atom or a substituent, Q represents a substituted or unsubstituted N-phenylcarbamoyl group, Za and Zb each represent a methine, substituted methine or =N-, Y₁, Y₂ and Y₄ each represent a halogen atom or a group which can be released upon the coupling reaction with an oxidation product of a developing agent (hereinafter referred to as release group), Y₃ represents a hydrogen atom or a release group, Y₅ represents a release group, R₂ and R₃ or R₅ and R₆ in the general formulae (I) and (II) may together form a 5-, 6- or 7-membered ring, and a dimer or a higher polymer can be formed through R₁, R₂, R₃ or Y₁; R₄, R₅, R₆ or Y₂; R₇, R₈, R₉ or Y₃; R₁₀, Za, Zb or Y₄; Q or Y₅, the aliphatic group herein being a straight chain, branched or cyclic alkyl, alkenyl or alkynyl group. The dye-forming couplers and the above-described special couplers may be in the form of dimers or higher polymers. Typical examples of the polymerized dye-forming couplers are described in U.S. Patent Nos. 3,451,820 and 4,080,211. Typical examples of the polymerized magenta couplers are described in British Patent No. 2,102,173 and U.S. Patent No. 4,367,282. These couplers are dispersed in at least one high-boiling organic solvent and are contained in the emulsion layers. High-boiling organic solvents of the following general formulae (A) to (E) are preferably used: W₁-COO-W₂ (B) W₁-O-W₂ (E) wherein W₁, W₂ and W₃ each represent a substituted or unsubstituted alkyl, cycloalkyl, alkenyl, aryl or heterocyclic ring, W₄ represents W₁, OW₁ or S-W₁ and n represents an integer of 1 to 5, and when n is 2 or larger, the groups W₄ may be either the same or different, and W₁ and W₂ in the general formula (E) may together form a condensed ring. It is preferred to use a colored coupler in combination with a photographing color sensitive material so as to compensate an unnecessary absorption of a colored dye formed by magenta and cyan coupler in a short wave length region. Typical examples of them include yellow-colored magenta couplers described in U.S. Patent No. 4,163,670 and Japanese Patent Publication No. 57-39413, and magenta-colored cyan couplers described in U.S. Patent Nos. 4,004,929 and 4,138,258 and British Patent No. 1,146,368. The standard amount of the color coupler is 0.001 to 1 mol per mol of the photosensitive silver halide, preferably 0.01 to 0.5 mol (yellow coupler), 0.003 to 0.3 mol (magenta coupler) or 0.002 to 0.3 mol (cyan coupler). The standard amount of the color coupler to be applied to a color paper is in the range of 4 to 14 x 10⁻⁴, 2 to 8 x 10⁻⁴ and 2 to 9 x 10⁻⁴ mol/m² for yellow, magenta and cyan couplers, respectively. For the spectral sensitization of the silver halide emulsion of the material of the present invention in a given wavelength region, a dye selected from the group consisting of the following dyes can be used: cyanine, merocyanine, complex cyanine, complex merocyanine, holopolar cyanine, hemicyanine, styryl and hemioxonol dyes. Particularly useful dyes are cyanine, merocyanine and complex merocyanine dyes. These dyes may have any nuclei which are contained in cyanine dyes as basic heterocyclic nuclei. Examples of the nuclei include pyrroline, oxazoline, thiazoline, pyrrole, oxazole, thiazole, selenazole, imidazole, tetrazole and pyridine nuclei; and the nuclei fused with an alicyclic hydrocarbon ring or an aromatic hydrocarbon ring such as indolenine, benzindolenine, indole, benzoxazole, naphthoxazole, benzothiazole, naphthothiazole, benzoselenazole, benzimidazole and quinoline nuclei. These nuclei may have a substituent bonded to the hydrocarbon part. The merocyanine or complex merocyanine dyes may have a 5- or 6-membered heterocyclic nucleus having a ketoethylene structure such as a pyrazolin-5-one, thiohydantoin, 2-thiooxazolidin-2,4-dione, thiazolidin-2,4-dione, rhodanine or thiobarbituric acid nucleus. These sensitizing dyes may be used either singly or in combination. The combination of the sensitizing dyes is frequently used for the purpose of supersensitization. The emulsion contains, in addition to the sensitizing dye, a dye which per se does not have the spectral sensitization effect or a supersensitizing substance which substantially does not absorb visible rays. Examples of them include aminostilbene compounds substituted with a nitrogen-containing heterocyclic nucleus group (such as those described in U.S. Patent Nos. 2,933,390 and 3,635,721), aromatic organic acid/formaldehyde condensates (such as those described in U.S. Patent No. 3,743,510), cadmium salts and azaindene compounds. Combinations described in U.S. Patent Nos. 3,615,613, 3,615,641, 3,617,295 and 3,635,721 are particularly useful. It is preferred to use a sensitizing dye or a supersensitizer selected from the group consisting of compounds of the following general formulae (VI), (VII), (VIII), (IX), (X), (XI) and (XII): wherein Z₁₁ represents an oxygen atom, sulfur atom or selenium atom, Z₁₂ represents a sulfur atom or selenium atom, R₁₁ and R₁₂ each represents a substituted or unsubstituted alkyl or alkenyl group having 6 or less carbon atoms and one of R₁₁ and R₁₂ represents a sulfo-substituted alkyl group. Preferably at least one of R₁₁ and R₁₂ represents a 3-sulfopropyl group, a 2-hydroxy-3-sulfopropyl group, a 3-sulfobutyl group or a sulfoethyl group. The substituents include, for example, alkoxy groups having 4 or less carbon atoms, halogen atoms, a hydroxy group, a carbamoyl group, substituted or unsubstituted phenyl groups having 8 or less carbon atoms, a carboxy group, a sulfo group and alkoxycarbonyl groups having 5 or less carbon atoms. Examples of R₁₁ and R₁₂ include methyl, ethyl, propyl, allyl, pentyl, hexyl, methoxyethyl, ethoxyethyl, phenethyl, 2-p-triethyl, 2-p-sulfophenethyl, 2,2,2-trifluoroethyl, 2,2,3,3-tetrafluoropropyl, carbamoylethyl, hydroxyethyl, 2-(2-hydroxyethyl)ethyl, carboxymethyl, carboxyethyl, ethoxycarbonylmethyl, 2-sulfoethyl, 2-chloro-3-sulfopropyl, 3-sulfopropyl, 2-hydroxy-3-sulfopropyl, 3-sulfobutyl and 4-sulfobutyl groups. When Z₁₁ represents an oxygen atom, V₁₁ and V₁₃ each represents a hydrogen atom and V₁₂ represents a phenyl group, an alkyl or alkoxy group having 3 or less carbon atoms or a phenyl group substituted with a chlorine atom (particularly preferably V₁₂ is a phenyl group). V₁₁ and V₁₂ or V₁₂ and V₁₃ may be connected together to form a condensed benzene ring. It is most preferred that V₁₁ and V₁₃ each represents a hydrogen atom and V₁₂ represents a phenyl group. When Z₁₁ represents a sulfur atom or selenium atom, V₁₁ represents an alkyl or alkoxy group having 4 or less carbon atoms or a hydrogen atom, V₁₂ represents an alkyl group having 5 or less carbon atoms, an alkoxy group having 4 or less carbon atoms, a chlorine atom, a hydrogen atom, a substituted or unsubstituted phenyl group (such as a tolyl, a anisyl or a phenyl group) or a hydroxy group, and V₁₃ represents a hydrogen atom or V₁₁ and V₁₂ or V₁₂ and V₁₃ may together form a condensed benzene ring. Preferably V₁₁ and V₁₃ each represents a hydrogen atom and V₁₂ represents an alkoxy group having 4 or less carbon atoms, a phenyl group or a chlorine atom; or V₁₁ represents an alkoxy or alkyl group having 4 or less carbon atoms and V₁₂ represents a hydroxy group or an alkyl group having 4 or less cabron atoms; or V₁₂ and V₁₃ together form a condensed benzene ring. When Z₁₂ represents a selenium atom, the meanings of V₁₄ and V₁₁, V₁₅ and V₁₂, and V₁₆ and V₁₃ are the same. When Z₁₂ represents a sulfur atom and Z₁₁ represents a selenium atom, V₁₄ represents a hydrogen atom or an alkoxy group having 4 or less carbon atoms, V₁₅ represents an alkoxy group having 4 or less carbon atoms, a substituted or unsubstituted phenyl group (such as a tolyl or an anisyl group or preferably a phenyl group), an alkyl group having 4 or less carbon atoms, a chlorine atom or a hydroxy group, V₁₆ represents a hydrogen atom; or V₁₄ and V₁₅, or V₁₅ and V₁₆ together form a condensed benzene ring. Preferably V₁₄ and V₁₆ each represents a hydrogen atom and V₁₅ represents an alkoxy group having 4 or less carbon atoms, a chlorine atom or a phenyl group; or V₁₅ and V₁₆ together form a condensed benzene ring. When both Z₁₁ and Z₁₂ represent a sulfur atom, V₁₄ and V₁₆ each represents a hydrogen atom and V₁₅ represents an unsubstituted or substituted phenyl group (such as a phenyl or tolyl group); or alternatively, V₁₄ represents a hydrogen atom and V₁₅ and V₁₆ can together form a condensed benzene ring. When Z₁₁ represents an oxygen atom and Z₁₂ represents a sulfur atom, V₁₄ and V₁₆ each represent a hydrogen atom and V₁₅ represents a chlorine atom, an unsubstituted or substituted phenyl group or an alkoxy group having 4 or less carbon atoms; or V₁₅ and V₁₆ can together form a condensed benzene ring; or preferably V₁₄ and V₁₆ each represent a hydrogen atom and V₁₅ represents a phenyl group; or V₁₅ and V₁₆ together form a condensed benzene ring. X₁₁ represents a residual group of an acid anion, and m₁₁ represents 0 or 1 (when the compound is an inner salt, m₁₁ represents 1). wherein Z₂₁ represents an oxygen, sulfur or selenium group or n-R₂₆, Z₂₂ represents an oxygen atom or >N-R₂₇, R₂₁ and R₂₂ have the same meaning as that of R₁₁ or R₁₂ in the above general formula I, or R₂₁ can be bonded with R₂₄ to form a 5- or 6-membered carbon ring and R₂₂ can be bonded with R₂₅ to form this ring. R₂₃ represents a hydrogen atom when at least one of Z₂₁ and Z₂₂ represents >N-R₂₆, or R₂₃ represents an ethyl, propyl or butyl group (preferably ethyl group) in other cases, and R₂₄ and R₂₅ each represents a hydrogen atom. R₂₆ and R₂₇ have the same meaning as that of R₂₁ and R₂₂ with the proviso that both of R₂₁ and R₂₆ cannot have a substituent having a sulfo group at the same time or R₂₂ and R₂₇ cannot have a substituent having a sulfo group at the same time. V₂₁ represents a hydrogen atom when Z₂₁ represents an oxygen atom, V₂₁ represents a hydrogen atom or an alkyl or alkoxy group having 5 or less carbon atoms when Z₂₁ represents a sulfur or selenium atom, or V₂₁ represents a hydrogen or chlorine atom when Z₂₁ represents >N-R₂₆. V₂₂ represents a hydrogen atom, an alkyl or alkoxy group having 5 or less carbon atoms, a chlorine atom or an unsubstituted or substituted phenyl group (such as a tolyl, anisyl or phenyl group) or V₂₂ can form a condensed benzene ring together with V₂₁ or V₂₃ (preferably V₂₂ represents an alkoxy or phenyl group or V₂₂ forms a condensed benzene ring together with V₂₁ or V₂₃) when Z₂₁ represents an oxygen atom and Z₂₂ represents >N-R₂₇; V₂₂ represents an unsubstituted or substituted phenyl group (such as a tolyl, anisyl or phenyl group; a phenyl group being preferred) or V₂₂ forms a condensed benzene ring together with V₂₁ or V₂₃ when Z₂₁ and Z₂₂ each represent an oxygen atom; V₂₂ represents a hydrogen atom, an alkyl or alkoxycarbonyl group having 5 or less carbon atoms, an alkoxy or acylamino group having 4 or less carbon atoms, a chlorine atom or an unsubstituted or substituted phenyl group (preferably an alkyl or alkoxy group having 4 or less carbon atoms, a chlorine atom or a phenyl group) when Z₂₁ represents a sulfur or selenium atom; or V₂₂ can form a condensed benzene ring together with V₂₃ when Z₂₁ represents a sulfur atom. Further, V₂₂ represents a chlorine atom, a trifluoromethyl or a cyano group or a alkylsulfonyl group having 4 or less carbon atoms or an alkoxycarbonyl group having 5 or less carbon atoms when Z₂₁ represents >N-R₂₆ (preferably V₂₁ represents a chlorine atom and V₂₂ represents a chlorine atom or a trifluoromethyl or cyano group when Z₂₁ represents >N-R₂₆). V₂₄ represents a hydrogen atom when Z₂₂ represents an oxygen atom, or V₂₄ represents a hydrogen or chlorine atom when Z₂₂ represents >N-R₂₇. V₂₅ represents an alkoxy group having 4 or less carbon atoms, a chlorine atom or an unsubstituted or substituted phenyl group (such as an anisyl, tolyl or phenyl group) or V₂₅ can form a condensed benzene ring together with V₂₄ or V₂₆ when Z₂₂ represents an oxygen atom; preferably V₂₅ represents an alkoxy group having 4 or less carbon atoms or a phenyl group or V₂₅ can form a condensed benzene ring together with V₂₄ or V₂₆ when Z₂₁ represents >N-R₂₆; and more preferably V₂₅ represents a phenyl group or it forms a condensed benzene ring together with V₂₅ or V₂₆ when Z₂₁ represents an oxygen, sulfur or selenium atom. Further, V₂₅ represents a chlorine atom, a trifluoromethyl or cyano group, an alkylsulfonyl group having 4 or less carbon atoms or a carboxyalkyl group having 5 or less carbon atoms when Z₂₂ represents >N-R₂₇. It is most preferred that V₂₄ represents a chlorine atom and V₂₅ represents a chlorine atom or a trifluoromethyl or cyano group. V₂₆ represents a hydrogen atom. X₂₁ represents a residual group of an acid anion. m₂₁ represents 0 or 1 (when the compound is an inner salt, m₂₁ represents 0). wherein Z₃₁ represents an atomic group forming a thiazoline, thiazole, benzothiazole, naphthothiazole, selenazoline, selenazole, benzoselenazole, naphthoselenazole, benzimidazole, naphthoimidazole, oxazole, benzoxazole, naphthoxazole or pyridine nucleus. These heterocyclic nuclei can be substituted. In case of forming a benzimidazole nucleus or a naphthoimidazole nucleus, the substituents of the nitrogen at position 1 other than R₃₁ are the same as those described above as R₂₆ or R₂₇ in the general formula II. The substituents of the condensed benzene ring of the benzimidazole include a chlorine atom, a cyano group, alkoxycarbonyl groups having 5 or less carbon atoms, alkylsulfonyl groups having 4 or less carbon atoms and a trifluoromethyl group. Particularly preferred is a compound having a chlorine atom at position 5, and a cyano group, a chlorine atom or a trifluoromethyl group at position 6. Examples of the substituents of the heterocyclic nuclei other than the benzimidazole, selenazoline and thiazoline nuclei include unsubstituted or substituted alkyl groups having 8 or less carbon atoms in total (the substituents being, for example, a hydroxy group, a chlorine or fluorine atom or an alkoxy, carboxy, alkoxycarbonyl, phenyl or substituted phenyl group), a hydroxy group, alkoxycarbonyl groups having 5 or less carbon atoms, halogen atoms, a carboxy, furyl, thienyl, pyridyl, phenyl group and substituted phenyl groups (such as tolyl, anisyl and chlorophenyl groups). Examples of the substituents of the selenazoline or thiazoline nucleus include alkyl groups having 6 or less carbon atoms, hydroxyalkyl groups having 5 or less carbon atoms and alkoxycarbonylalkyl groups having 5 or less carbon atoms. R₃₁ has the same meaning as R₁₁ or R₁₂ in the general formula I. R₃₂ has the same meaning as R₁₁ or R₁₂ in the general formula I or it represents a hydrogen atom, a furfuryl group or an unsubstituted or substituted monocyclic aryl group (such as a phenyl, tolyl, anisyl, carboxyphenyl, hydroxyphenyl, chlorophenyl, sulfophenyl, pyridyl, 5-methyl-2-pyridyl, 5-chloro-2-pyridyl, thienyl or furyl group). At least one of R₃₁ and R₃₂ represents a substituent having a sulfo or carboxy group and the other represents a sulfo-free group. R₃₃ represents a hydrogen atom, an alkyl group having 5 or less carbon atoms, or a phenethyl, phenyl or 2-carboxyphenyl group. Among them, a hydrogen atom or a methyl or ethyl group is preferred. Q₃₁ represents an oxygen, sulfur or selenium atom or >N-R₃₄. Preferably Q₃₁ represents a sulfur or selenium atom or >N-R₃₄ when Z₃₁ represents an atomic group forming a thiazoline, selenazoline or oxazole nucleus. R₃₄ represents a pyridyl or phenyl group, a substituted phenyl group (such as a tolyl or anisyl group) or an aliphatic hydrocarbon group having 8 or less carbon atoms in total which may have (1) an oxygen, sulfur or nitrogen atom in the carbon chain and (2) a substituent such as a hydroxy group, a halogen atom or an alkylaminocarbonyl, alkoxycarbonyl or phenyl group. Preferably R₃₄ represents a hydrogen atom, a phenyl or pyridyl group or an alkyl group which can contain (1) an oxygen atom in the carbon chain and (2) hydroxy group. k represents 0 or 1, and n represents 0 or 1. Q₃₁ represents an oxygen atom when n represents 1 and Z₃₁ represents a pyridyl-forming atomic group. Examples of the compounds of the general formulae VI, VII and VIII are as follows: In the above formulae, Z₁₁ represents an atomic group forming benzoxazole, naphthoxazole, benzothiazole, naphthothiazole, dihydronaphthothiazole, benzoselenazole, naphthoselenazole or dihydronaphthoselenazole, and Z₁₂ represents an atomic group forming benzothiazole, naphthothiazole, dihydronaphthothiazole, benzoselenazole, naphthoselenazole or dihydronaphthoselenazole. The nitrogen-containing heterocyclic nucleus represented by Z₁₁ or Z₁₂ can have one or more substituents. Examples of the preferred substituents include lower alkyl groups (more preferably alkyl groups having 6 or less carbon atoms), lower alkoxy groups (more preferably alkoxy groups having 6 or less carbon atoms), a chlorine atom, lower alkoxycarbonyl groups (more preferably alkoxycarbonyl groups having 5 or less carbon atoms), unsubstituted or substituted phenyl groups (such as phenyl, tolyl, anisyl and chlorophenyl groups) and a hydroxy group. Examples of the compounds having the nitrogen-containing heterocyclic nucleus represented by Z₁₁ or Z₁₂ include 5-hydroxybenzoxazole, 5-methoxyoxazole, 5-ethoxybenzoxazole, 5-phenylbenzoxazole, 5,6-dimethylbenzoxazole, 5-methyl-6-methoxybenzoxazole, 6-ethoxy-5-hydrobenzoxazole, naphtho(1,2-d)oxazole, naphtho(2,3-d)oxazole, naphtho(2,1-d)oxazole, 5-methylbenzothiazole, 5-methoxybenzothiazole, 5-ethylbenzothiazole, 5-p-tolylbenzothiazole, 6-methylbenzothiazole, 6-ethylbenzothiazole, 6-butylbenzothiazole, 6-methoxybenzothiazole, 6-butoxybenzothiazole, 5,6-dimethylbenzothiazole, 5,6-dimethoxybenzothiazole, 5-hydroxy-6-methylbenzothiazole, 5-ethoxycarbonylbenzothiazole, 5-chlorobenzothiazole, 5-chloro-6-methylbenzothiazole, naphtho(1,2-d)thiazole, naphtho(2,1-d)thiazole, 5-methylnaphtho(2,1-d)thiazole, 8,9-dihydronaphtho(1,2-d)thiazole, 8-methoxynaphtho(1,2-d)thiazole, benzothiazole, benzoselenazole, 5-methylbenzoselenazole, 6-methylbenzoselenazole, 5-methoxybenzoselenazole, 6-methoxybenzoselenazole, 5,6-dimethylbenzoselenazole, 5-ethoxy-6-methylbenzoselenazole, 5-hydroxy-6-methylbenzoselenazole, naphtho(1,2-d)selenazole and naphtho(2,1-d)selenazole. R₁₁ and R₁₂ may be the same or different and they each represent an unsubstituted or substituted alkyl or alkenyl group having 10 or less carbon atoms. At least one of R₁₁ and R₁₂ has a sulfo group. Examples of the substituents of the alkyl and alkenyl groups include the above-mentioned sulfo group, alkoxy groups having 6 or less carbon atoms, halogen atoms, a hydroxy group, an unsubstituted or substituted aryl group having 8 or less carbon atoms (such as phenyl, furyl, thienyl, tolyl, p-butylphenyl, xylyl, anisyl, sulfophenyl, hydroxyphenyl, carboxyphenyl and chlorophenyl groups), unsubstituted or substituted phenoxy groups having 8 or less carbon atoms (the substituents being, for example, a fluorine or chlorine atom or sulfo, hydroxy, carboxy, alkoxycarbonyl, alkyl or alkoxy groups), acyl groups having 8 or less carbon atoms (such as phenylsulfonyl, tosyl, methylsulfonyl, benzoyl, acetyl and propionyl groups), alkoxycarbonyl groups having 6 or less carbon atoms and a carboxy group. R₁₃ and R₁₆ each represents a hydrogen atom or R₁₃ can form a 5- or 6-membered ring together with R₁₅. R₁₄ represents a hydrogen atom, or when R₁₃ and R₁₆ each represent a hydrogen atom, R₁₄ represents an alkyl group having 4 or less carbon atoms or a phenylalkyl group having 10 or less carbon atoms. Preferably, R₁₄ represents a hydrogen atom and R₁₃ and R₁₅ together form a 5- or 6-membered ring or, alternatively, R₁₃ and R₁₅ each represent a hydrogen atom and R₁₄ represents a benzyl group. R₁₆ represents a hydrogen atom or it can form a 5- or 6-membered carbon ring together with R₁₂. Among the nitrogen-containing heterocyclic nucleus-forming atomic groups represented by Z₁₁, preferred are naphthoxazoles, benzothiazoles having at least one electron-donating group having a negative Hammett's δ p value, dihydronaphthothiazoles, naphthothiazoles and benzoselenazoles. X ⊖ / 11 represents a residual group of an acid anion. m₁₁ represents 0 or 1 (when the compound is an inner salt, m₁₁ represents 0). wherein Z₂₁ represents a sulfur atom or a selenium atom. R₂₁ and R₂₂ have the same meaning as that of R₁₁ or R₁₂ in the general formula I and at least one of them represents a substituent having a sulfo or carboxy group. R₂₃ represents a hydrogen atom or a lower alkyl group having 4 or less carbon atoms. V₂₁ represents a hydrogen atom, an alkyl or alkoxy group having 6 or less carbon atoms, a fluorine or chlorine atom or a hydroxy group. V₂₂ and V₂₅ each represent a hydrogen atom. V₂₃ represents a hydrogen atom, a lower alkyl group (having preferably 6 or less carbon atoms), a lower alkoxy group (having preferably 6 or less carbon atoms) or a hydroxy group. V₂₄ represents a hydrogen atom, a lower alkyl group (having preferably 6 or less carbon atoms), a lower alkoxy group (having preferably 6 or less carbon atoms), a chlorine atom, a lower alkoxycarbonyl group, an unsubstituted or substituted phenyl group (such as a phenyl, tolyl or anisyl group) or a hydroxy group. V₂₂ and V₂₃; V₂₃ and V₂₄; or V₂₄ and V₂₅ can together form a condensed benzene ring which may have a substituent. Examples of the substituents include a chlorine atom, lower alkyl groups (having preferably 4 or less carbon atoms) and lower alkoxy groups (having preferably 4 or less carbon atoms). Among the nitrogen-containing heterocyclic nuclei containing Z₂₁, the most preferred are naphtho(1,2-d)thiazole, naphtho(2,1-d)thiazole, naphtho(1,2-d)selenazole, naphtho(2,1-d)selenazole and benzoselenazoles having at least one electron-donating group having a negative Hammett's δ p value. X ⊖ / 21 represents a residual group of an acid anion. m₂₁ represents 0 or 1 (when the compound is an inner salt, m₂₁ represents 0). wherein Z₃₁ has the same meaning as that of Z₁₂ in the general formula I or it represents a naphthoxazole. The nitrogen-containing heterocyclic nucleus formed by Z₃₁ may have a substituent which is selected from the above-mentioned substituents of the nitrogen-containing heterocyclic nucleus represented by Z₁₁ or Z₁₂ in the general formula I. Z₃₂ represents a sulfur or selenium atom or >N-R₃₆. R₃₆ represents a hydrogen atom, a pyridyl or phenyl group, a substituted phenyl group (such as a tolyl, anisyl or hydroxyphenyl group) or an aliphatic hydrocarbon group having 8 or less carbon atoms which may have (1) an oxygen, sulfur or nitrogen atom in the carbon chain and (2) a substituent such as a hydroxy group, a halogen atom or an alkylaminocarbonyl, alkoxycarbonyl or phenyl group. Preferably R₃₆ represents a hydrogen atom, a phenyl or pyridyl group or an alkyl group which can contain (1) an oxygen atom in the carbon chain and (2) a hydroxy group. R₃₁ has the same meaning as that of R₁₁ or R₁₂ in the general formula I. R₃₂ has the same meaning as that of R₁₁ or R₁₂ in the general formula I or it represents a hydrogen atom, a furfuryl group, an unsubstituted or substituted monocyclic aryl group (such as a phenyl, tolyl, anisyl, carboxyphenyl, hydroxyphenyl, chlorophenyl, sulfophenyl, pyridyl, 5-methyl-2-pyridyl, 5-chloro-2-pyridyl, furyl or thienyl group). R₃₃ and R₃₅ each represents a hydrogen atom or they together form a 5- or 6-membered ring. R₃₄ has the same meaning as that of R₁₄ in the general formula VI. At least one of R₃₁ and R₃₂ represents a sulfo group-free group and the other represents a group containing a sulfo or carboxy group. wherein Y₄₁, Y₄₂, Y₄₃ and Y₄₄ may be the same or different and each represent =CH- or =N-, and at least one of Y₄₁ and Y₄₃ and at least one of Y₄₂ and Y₄₄ represent =N-. R₄₁, R₄₂, R₄₃ and R₄₄ may be the same or different and each represent a hydrogen atom, a hydroxy group, a lower alkoxy group (having preferably 10 or less carbon atoms), an aryloxy group (such as a phenoxy, tolyloxy, sulfophenoxy, β-naphthoxy, α-naphthoxy or 2,4-dimethylphenoxy group), a halogen atom (such as a chlorine or bromine atom), a heterocyclic nucleus (such as a morpholinyl or piperidine group), an alkylthio group (such as a methylthio or ethylthio group), a heterocyclylthio group (such as a benzothiazylthio group), an arylthio group (such as a phenylthio or tolylthio group) , an amino, alkylamino or substituted alkylamino group (such as a methylamino, ethylamino, propylamino, dimethylamino, diethylamino, dodecylamino, cyclohexylamno, β-hydroxyethylamino, di-β-hydroxyethylamino or β-sulfoethylamino group), an arylamino or substituted arylamino group (such as an anilino, o-sulfoanilino, m-sulfoanilino, p-sulfoanilino, o-anisylamino, m-anisylamino, p-anisylamino, o-methylanilino, p-tert-amylanilino, o-carboxyanilino, m-carboxyanilino, p-carboxyanilino, hydroxyanilino, naphthylamino, sulfonaphthylamino, heterocyclylamino (such as 2-benzothiazolamino or 2-pyridylamino), aryl (such as phenyl) or mercapto group. A₄₁ represents a group having an arylene group such as those shown below: wherein M represents a hydrogen atom or a cation which contributes to the water solubility. At least one of R₄₁, R₄₂, R₄₃, R₄₄ and A₄₁ in the above general formula IV contains a sulfo group. The most preferred compounds of the general formula IV are stilbene derivatives. RI, GL and BL used in the present invention are arranged on the support in the following order: BL, GL, and RL; BL, RL and GL; or RL, GL and BL. A protective layer (PL) and an intermediate layer (ML) can be provided above or below each layer or between the layers, and an antihalation layer (HL) or yellow filter layer (YL) can be provided below the layers. The silver halide photosensitive layers can be divided into two or more layers such as a high-speed layer and low speed layer. The structure of the layers may be the same as that of a printing photosensitive material comprising an ordinary film or photographic printing paper as the support. A finely pulverized organic or inorganic white pigment which contributes to the primary diffuse reflection can be incorporated in at least one of the prime layer and the layers formed thereon in an amount of as small as only 1 g/m² or less or preferably 0.5 g/m² or less. When the pigment is used in a larger amount, the excellent properties of the color image, particularly sharpness, are damaged. The silver halide grains used in the present invention can be prepared by any of an acid process, a neutral process or an ammonia process or a combination of them. For example, the silver halide grains can be prepared by preparing nuclei by the acid process and growing them by the ammonia process. The growing process is preferably conducted by introducing only given amounts of silver ion and a halogen ion while the pH and pAg are controlled. The grain diameter is in the range of 0.05 to 1 µm, preferably 0.2 to 0.8 µm. The system may be either monodisperse or polydisperse system. The silver halide may be any of pure silver chloride, silver chlorobromide, silver bromide or silver bromoiodide. The silver halide may have any of crystal habits. The silver halide can be sensitized with an active gelatin or chemically sensitized with a chemical sensitizer such as allyl thiocarbamide, cystine or a thiosulfate; a reducing sensitizer such as a polyamine or stannous chloride; a noble metal sensitizer; or a rhodium or iridium complex salt. An antifoggant selected from the group consisting of mercaptotriazoles, mercaptotetrazoles and benzotriazoles can be incorporated in the silver halide emulsion layers. To conduct the development rapidly, it is preferred to use a silver chlorobromide emulsion or silver chloride emulsion in combination with an antifoggant or stabilizer capable of firmly adsorbing on the silver halide grains such as a mercapto compound, a nitrobenzotriazole compound or a benzotriazole compound. Ordinary additives such as a development accelerator, a halation-preventing agent, an irradiation-preventing agent or a fluorescent brightener may also be used. The fluorescent brightener is preferably dispersed in special layers, particularly a prime layer, an intermediate layer and a protective layer. Usually, a fluorescent brightener is added to the developer before dyeing. However, a stable dyeing is impossible in some cases. Further, a high storage stability of the fluorescent brightener cannot be provided by this method and the removal of dyeing substances frequently contributes to the brightness rather than the brightening effect of the brightener. The fluorescent brighteners usable in the present invention are compounds described in Japanese Patent Public Disclosure No. 60-154251. They are soluble in organic solvents and dispersible by emulsion dispersion, polymer dispersion or coupler dispersion and, therefore, they can be incorporated in special layers of the photosensitive material in an advantageous manner. Compounds of the following general formulae (XIII), (XIV), (XV) and (XVI) are preferred: wherein Y₁ and Y₂ each represent an alkyl group, Z₁ and Z₂ each represent H or an alkyl group, n represents 1 or 2, R₁, R₂, R₄ and R₅ each represent H or an aryl group, an alkyl group, an alkoxy group, an aryloxy group, a hydroxyl group, an amino group, a cyano group, a carboxyl group, an amido group, an ester group, an alkylcarbonyl group, an alkylsulfo group or a dialkylsulfonyl group, R₆ and R₇ each represent H, an alkyl group such as a methyl or ethyl group or a cyano group, R₁₆ represents a phenyl group, a halogen atom or an alkyl-substituted phenyl group and R₁₅ represents an amino group or an organic primary or secondary amine group. Examples of these compounds are as follows: The water-soluble fluorescent brightener is dissolved in a high-boiling organic solvent like a color coupler and the solution is dispersed in a hydrophilic colloid in the presence of a surfactant. This method and the organic solvents are described in, for example, British Patent No. 1,072,915, Japanese Patent Public Disclosure No. 60-134232, Japanese Patent Publication No. 51-30463, Japanese Patent Public Disclosure Nos. 53-1520 and 55-25057, Japanese Patent Publication No. 45-37376 and U.S. Patent No. 3,416,923. The fluorescent brightener can also be used by dissolving it in a low-boiling organic solvent such as acetone, methyl ethyl ketone or methanol and mixing the solution with a prime coating solution such as an ionomer solution. Further, a dispersion of the fluorescent brightener can be mixed in an emulsion for forming a given layer. The brightener is used usually in an amount of 3 to 200 mg/m². In another method, a polymer is prepared by an ionomer polyaddition wherein the fluorescent brightener is used in place of a hydrophobic substance or color coupler as described in Japanese Patent Public Disclosure No. 57-87429 or by mixing it with a condensation product and the polymer is used for forming the prime layer. A fluorescent brightener selected from usual stilbene derivatives and diphenyl derivatives can be used in combination with a polyvinylpyrrolidone, polyvinyl acetate or a polymer comprising the following recurring units to fix the brightener and also to form a layer having a high fluorescence as described in Japanese Patent Publication No. 34-7127, Public Disclosure No. 53-147885 and Publication No. 60-21372: wherein A represents -COR₁, -COOR₂, -CONHR₃, -CONHCOR₄ or -SO₂R₅, R₁, R₂, R₃, R₄ and R₅ each being H or a substituted or unsubstituted alkyl group, aryl group or cycloalkyl group. Examples of the compounds are as follows: Examples of the fluorescent brighteners usable herein are as follows: For example, 0.1 g of WF-1 is dissolved in 100 ml of water to obtain a solution, to which 0.25 g of P-1 polymer is added to obtain a dispersion to be added to the protective layer or prime layer in such a manner that the amount of WF-1 will be 50 mg/m². (Fluorescent brightener 2) The brightening effect of the fluorescent brightener is exhibited in only highlights of an image but not in the image-forming regions. Usually, in color photographic materials, an ultraviolet absorber is contained in a surface layer of image-forming layers and, therefore, the effect of the fluorescent brightener contained in a layer near the support is weakened. It is preferred, therefore, that a compound having the fluorescent brightening effect is contained in the surface layer, particularly in only the highlights. In the present invention, a fluorescent brightener capable of reacting with an oxidation product of a developing agent to release a residue having a fluorescent brightening effect into the developer may be incorporated in a photosensitive layer containing a silver halide or an intermediate layer adjacent thereto. The fluorescent brighteners are compounds of the following general formula (XVIII): A-(L) a -Fl (XVIII) wherein Fl represents a fluorescent brightening compound residue, L represents a bonding group, a represents 1 or 2 and A represents a residue of a compound capable of exchange-reacting with an oxidation product of a developing agent to release Fl such as a color coupler residue, colorless compound-forming coupler residue or hydroquinone residue. Examples of them include those described in Japanese Patent Public Disclosure No. 52-109927, British Patent No. 945,542 and West German Public Disclosure No. 1800420. The compounds are as follows: The compound is dissolved in a high-boiling organic solvent like the color coupler, the solution is dispersed in a hydrophilic colloid in the presence of a surfactant and the obtained dispersion is incorporated in a photosensitive layer, particularly a photosensitive surface layer containing a photosensitive silver halide or an intermediate layer or protective layer adjacent thereto. In another method, the compound is dispersed in a water-insoluble, organic solvent-soluble polymer such as polyvinyl alcohol, polyvinyl acetate, polyacrylic ester or copolymer or in the above-mentioned polymer or latex in which the fluorescent brightener is dispersible. By using the above-mentioned compound, only the highlights of the images can be brightened relatively selectively. The color photosensitive materials of the present invention can be used as all sorts of color photographic reflective materials, particularly photosensitive materials for color printing papers, color reversal printing papers and direct positive color printing papers as well as photosensitive materials for color copies according to the photofogging process. (Color development process) A color developer usable in the developing process of the photosensitive material of the present invention is preferably an alkaline aqueous solution containing an aromatic primary amine color developing agent as a main component. The color developing agents are aminophenol compounds, and particularly preferably p-phenylenediamine compounds. Typical examples thereof include 3-methyl-4-amino-N,N-diethylaniline, 3-methyl-4-amino-N-ethyl-N-β-hydroxylethylaniline, 3-methyl-4-amino-N-ethyl-N-β-methanesulfonamidoethylaniline, 3-methyl-4-amino-N-ethyl-N-β-methoxyethylaniline and their sulfates, hydrochlorides and p-toluenesulfonates. These diamines in the form of their salts are generally more stable than those in the free form, and the former is preferable to the latter. The color developer usually contains a pH buffering agent such as an alkali metal carbonate, borate or phosphate; a development inhibitor such as a bromide, iodide, benzimidazole, benzothiazole or mercapto compound; and an antifoggant. The color developer may further contain, if necessary, a preservative such as a hydroxylamine or sulfite; an organic solvent such as triethanolamine or diethylene glycol; a development accelerator such as benzyl alcohol, polyethylene glycol, a quaternary ammonium salt or an amine; a dye-producing coupler; a competing coupler; a nucleating agent such as sodium boron hydride; an assistant developer such as 1-phenyl-3-pyrazolidone; a thickening agent; a chelating agent such as an aminopolycarboxylic acid, an aminopolyphosphonic acid, an alkylphosphonic acid or a phosphonocarboxylic acid; and an antioxidant as described in West German Patent Application (OLS) No. 2,622,950. In the development process for a reversal color photosensitive material, a black-and-white development is conducted before the color development. The black-and-white developer contains a known black-and-white developing agent, for example, a dihydroxybenzene such as hydroquinone, a 3-pyrazolidone such as 1-phenyl-3-pyrazolidone, or an aminophenol such as N-methyl-p-aminophenol. The black-and-white developing agent can be used either singly or as a combination of them. The photographic emulsion layers are usually bleached after the color development. The bleaching process may be conducted either simultaneously with the fixing treatment or separately from the fixing treatment. The bleaching agents usable herein include, for example, compounds of polyvalent metals such as iron (III), cobalt (III), chromium (VI) and copper (II), peracids, quinones and nitro compounds. Typical examples of the bleaching agents include ferricyanides; dichromates; organic complex salts of iron (III) or cobalt (III) such as complex salts of them with aminopolycarboxylic acids such as ethylenediaminetetraacetic acid, diethylenetriaminepentaacetic acid, nitrilotriacetic acid and 1,3-diamino-2-propanoltetraacetic acid, and organic acids such as citric acid, tartaric acid and malic acid; persulfates; manganates; and nitrosophenol. Among them, iron (III) ethylenediaminetetraacetate and persulfates are preferred from the viewpoints of rapid process and environmental pollution prevention. Iron (III) ethylenediaminetetraacetate is particularly useful in both of an independent bleaching bath and a combined bleach-fixing bath. The bleaching solution and bleach-fixing bath can contain, if necessary, a bleaching accelerator. Examples of usable bleaching accelerators include bromine ions and iodine ions; thiourea compounds described in U.S. Patent No. 3,706,561, Japanese Patent Publication Nos. 45-8506 and 49-26586 and Japanese Patent Public Disclosure Nos. 53-32735, 53-36233 and 53-37016; thiol compounds described in Japanese Patent Public Disclosure Nos. 53-124424, 53-95631, 53-57831, 53-32736, 53-65732 and 54-52534 and U.S. Patent No. 3,893,858; heterocyclic compounds described in Japanese Patent Public Disclosure Nos. 49-59644, 50-140129, 53-28426, 53-141623, 53-104232 and 54-35727; thioether compounds described in Japanese Patent Public Disclosure Nos. 52-20832, 55-25064 and 55-26506; tertiary amines described in Japanese Patent Public Disclosure No. 48-84440; and thiocarbamoyls described in Japanese Patent Public Disclosure No. 49-42349. They can be used either singly or as a combination of two or more of them. Among them, bromine ions, iodine ions, thiol compounds and disulfide compounds are preferred bleaching accelerators. The bleaching accelerating agents are particularly effective in the bleach-fix of the color photosensitive materials. Examples of the fixing agents include thiosulfates, thiocyanates, thioethers, thioureas and a large amount of iodides. Among them, the thiosulfates are usually used. Sulfites, bisulfites and carbonyl/bisulfite adducts are preferred as the preservative for a bleach-fixing solution or fixing solution. After completion of the bleach-fixing process or fixing process, the product is usually washed with water. Various known additives can be used in order to prevent the precipitation or to save water in the washing step. The additives usable herein include water softeners for preventing the precipitation such as inorganic phosphoric acids, aminopolycarboxylic acids and organic phosphoric acids; germicides and antifungal agents which inhibit the growth of bacteria, algae and molds; hardeners such as magnesium salts and aluminum salts; and surfactants used for preventing drying load or drying mark. These additives can be used if necessary. In addition, the compounds described in L.E. West, Phot. Sci. Eng., Vol. 6, pp. 344 to 359 (1965) can also be used as additives. Particularly, the addition of chelating agents and antifungal agents are effective. In the step of water washing, two or more tanks are used to provide a countercurrent system so as to save water. The step of water washing can be replaced by the multistep countercurrent stabilization step as described in Japanese Patent Public Disclosure No. 57-8543. In such a case, 2 to 9 countercurrent baths are necessary. Various compounds are added to the stabilization bath in order to stabilize the image, in addition to the above-mentioned additives. Concrete examples of the compounds include buffering agents for controlling the pH of the film at, for example, 3 to 9 (such as suitable combinations of borates, metaborates, borax, phosphates, carbonates, potassium hydroxide, sodium hydroxide, aqueous ammonia, monocarboxylic acids, dicarboxylic acids and polycarboxylic acids) and formalin. If necessary, other additives can also be used. The additives are, for example, water softeners (such as inorganic phosphoric acid, aminopolycarboxylic acids, organic phosphoric acids, aminopolyphosphonic acids and phosphonocarboxylic acids), germicides (such as benzoisothiazolinone, isothiazolone, 4-thiazolinebenzimidazole and halogenated phenols) surfactants, fluorescent brightening agents and hardeners. They can be used either singly or as a combination of two or more of them having the same or different effects. It is preferred to add various ammonium salts such as ammonium chloride, ammonium nitrate, ammonium sulfate, ammonium phosphate, ammonium sulfite and ammonium thiosulfate as a pH adjustor, after the processing. The silver halide color photosensitive material of the present invention may contain a color developing agent in order to simplify and to accelerate the processing. In such a case, precursors of the color developing agents are preferably used. Examples of the precursors include indoaniline compounds described in U.S. Patent No. 3,342,597, Schiff base-type compounds described in U.S. Patent No. 3,342,599, Research Disclosure Nos. 14850 and 15159, aldol compounds described in Research Disclosure No. 13924, metal complex salts described in U.S. Patent No. 3,719,492, urethane compounds described in Japanese Patent Public Disclosure No. 53-135628 and various salts described in Japanese Patent Public Disclosure Nos. 56-6235, 56-16133, 56-59232, 56-67842, 56-83734, 56-83735, 56-83736, 56-89735, 56-81837, 56-54430, 56-106241, 56-107236, 57-97531 and 57-83565. The silver halide color photosensitive material of the present invention may contain, if necessary, a 1-phenyl-3-pyrazolidone in order to accelerate the color development. Typical examples of the 1-phenyl-3-pyrazolidones include those described in Japanese Patent Public Disclosure Nos. 56-64339, 57-144547, 57-211147, 58-50532, 58-50536, 58-50533, 58-50534, 58-50535 and 58-115438. The processing solutions are used at a temperature of 10 to 50°C in the present invention. Although the standard temperature is 33 to 38°C, a higher temperature can be employed to accelerate the processing or to reduce the processing time, and a lower temperature can be employed to improve the image quality or the stability of the processing solution. The process described in West German Patent No. 2,226,770 or U.S. Patent No. 3,674,499 wherein a cobalt intensifier or hydrogen peroxide intensifier is used for saving silver in the photosensitive material, can also be employed. The processing baths may have, if necessary, a heater, temperature sensor, liquid level sensor, circulating pump, filter, floating lid or squeegee. The following examples will further illustrate the present invention. Example 1 Metallic aluminum was roughly rolled. The aluminum sheets were then rolled in an apparatus comprising a central roller and two rollers arranged above and below the central one each in contact with the central one. In this step, two sheets of annealed metallic aluminum were put together and passed between the upper roller and the central roller and then between the central one and the lower one to prepare aluminum foils having a thickness of about 10 µm. Surprisingly, the surfaces of the foils contacted with each other had the secondary diffuse-reflecting properties. A photographic white base paper was extrusion-coated with a low-density polyethylene and simultaneously laminated with metallic aluminum. Then the other surface of the support was subjected to a corona discharge and extrusion-coated with the high-density polyethylene to form a polyethylene layer having a thickness of 30 µm. A thin layer or an ionomer resin was formed on the aluminum surface to prepare Support Sample 1. Separately, a polyethylene phthalate film having a thickness of 100 µm was placed in a vacuum deposition apparatus R and aluminum was vacuum-deposited thereon in vacuum (0,001Pa (10⁻⁵ Torr)) to form an aluminum film having a thickness of 100nm (1000 Å) according to a process shown in Example 1 of Japanese Patent Application No. 60-52788. The film was then coated with a low-density polyethylene to form a polyethylene layer having a thickness of 30 µm. The product will be referred to as Comparative Sample a . The Sample 1 (support of the present invention) was superior to the Comparative Sample a , in that the former was free of the reflection of light and had a metallic brightness and a wide visual angle of observation. The thickness of the Sample 1 and the Comparative Sample a were about 120 µm. Example 2 The Support Sample 1 prepared in Example 1 was used. The aluminum foil-having surface of the Sample 1 was subjected to the corona discharge. A priming layer was formed by using gelatin and sodium 1-hydroxy-3,5-dichloro-S-triazine (hardener). A silver chlorobromide emulsion layer (halogen compostion: 67% AgCl, average grain diameter: 0.4 µm) as in ordinary photographic paper was formed thereon and further a protective layer was formed thereon. The amount of silver applied was 2.1 g/m². After image exposure followed by the development with a developer D-72 (1:2 dilution) and fixing, it was washed with water. On the other hand, a Resin-coated paper sample b (a support prepared by extrusion-coating a surface of a white base paper with polyethylene whitened by mixing titanium oxide therein to impart the primary diffuse-reflecting properties and extrusion-coating the other surface thereof with polyethylene) usually used as a photographic paper was processed in the same manner as above. After the image exposure followed by development, fixing and water washing, an image was obtained. The image formed on the Support sample 1 was superior to that formed on the Comparative support sample b in the brightness in the highlights, gradation in shadows and sharpness. Surprisingly, the maximum density and the saturation of the shadows in the image formed on the Support sample 1 were not inferior to those of the comparative one. Example 3 Reversal color photographic papers were prepared by using the Support sample 1 and Comparative samples a and b according to a process shown in Example 1 of Japanese Patent Application No. 61-99122. After image exposure, an usual reversal development was conducted which comprised the first development, water washing, reversal exposure, color development, water washing, bleach-fixing and water-washing to obtain an image. The Sample 1 of the present invention was far superior to the Comparative sample b in saturation and sharpness and, in addition, the former was also superior to the Comparative sample a in that no light was reflected and the visual angle of observation was widened. In particular, when the support of the present invention was used, the gradation in the shadows which had been considered to be a defect of ordinary reversal color photographic papers was improved and the quite excellent image having a high texture could be obtained because microscopically a hard gradation was provided due to an improved sharpness, while macroscopically the image had a soft tone. Example 4 The Support sample 1 was subjected to a corona discharge process and then a priming layer was formed thereon by using gelatin and sodium 1-hydroxy-3,5-dichloro-S-triazine hardener. Preparation of color emulsions : A core/outer shell-type internal emulsion B was prepared as follows: Emulsion B 30 g of gelatin was dissolved in 1 ℓ of a solution containing 0.5 mol of KBr, 0.2 mol of NaCl and 0.0015 mol of KI. 700 ml of 1 mol/l silver nitrate solution was added to the solution at 60°C over 20 min. After physical ripening conducted for 20 min, the product was washed with water to remove water-soluble halides. 20 g of gelatin was added thereto and then water was added thereto to prepare 1200 ml of the mixture. The thus prepared silver halide emulsion had an average grain diameter of 0.4 µm. 500 ml of 1 mol/l aqueous silver nitrate solution and 500 ml of 2 mol/l aqueous sodium chloride solution were added simultaneously to 300 ml of the emulsion to precipitate silver chloride shells. After water washing, a silver halide emulsion B having an average grain diameter of 0.7 µm was obtained. The first layer-forming emulsion : 10 ml of ethyl acetate and 4 ml of solvent (c) were added to a mixture of 10 g of cyan coupler (a) and 2.3 g of color image stabilizer (b) to obtain a solution. The solution was emulsion-dispersed in 90 ml of 10% aqueous gelatin solution containing 5 ml of 10% sodium dodecylbenzenesulfonate. On the other hand, a red-sensitive dye shown below was added to the silver halide emulsion B (containing 70 g/kg of Ag) in an amount of 2.0 x 10⁻⁴ mol per mol of the silver halide to prepare 90 g of a red-sensitive emulsion. The emulsion dispersion was mixed with the emulsion to prepare a solution. The concentration of the solution was controlled with gelatin to prepare a composition shown in Table 1. A nucleating agent (compound 2) in an amount of 3 x 10⁻⁴ mol per mol of Ag and a nucleating accelerator in an amount of 4.7 x 10⁻⁴ mol per mol of Ag were added thereto to prepare the first layer-forming emulsion. The emulsions for forming the second layer to the seventh layer were prepared in the same manner as in the preparation of the first layer-forming emulsion. Sodium 1-hydroxy-3,5-dichloro-S-triazine was used as the hardener in the respective layers. The spectral sensitizers contained in the respective emulsions were as follows: sensitizing dye in blue-sensitive emulsion layer: sensitizing dye in green-sensitive emulsion layer: sensitizing dye in red-sensitive emulsion layer: anti-irradiation dye in green-sensitive emulsion layer: anti-irradiation dye in red-sensitive emulsion layer: The structural formulae of the compounds used as the couplers etc. in the Example were as follows: (a) cyan coupler (b) color image stabilizer a mixing of: and in a molar ratio of 1:3:3 (c) solvent (d) color mixing inhibitor (e) magenta coupler (f) a mixture of: and in a weight ratio of 1:1.5. (Note) (g) a mixture of: and in a weight ratio of 1:2:2. (h) U.V. absorber a mixture of: and in a molar ratio of 1:5:3 (i) color mixing inhibitor (j) solvent (k) yellow coupler (l) color image stabilizer (m) solvent nucleating agent (compound-2) nucleating accelerator 10 Processing step A Time Temperature color developemnt 3 min 30 s 33°C bleach-fixing 40 s 38°C stabilization (1) 20 s 38°C ditto (2) 20 s 38°C ditto (3) 20 s 38°C The replenisher was fed according to a counter current system wherein the replenisher was fed into the stabilization bath (3), an overflow from the bath (3) is introduced in the stabilization bath (2) and an overflow from the bath (2) is introduced in the stabilization bath (1). (Color developer) Mother liquor diethylenetriaminepentaacetic acid 2.0 g benzyl alcohol 12.8 g diethylene glycol 3.4 g sodium sulfite 2.0 g sodium bromide 0.26 g hydroxylamine sulfate 2.60 g sodium chloride 3.20 g 3-methyl-4-amino-N-ethyl-N-(β-methanesulfonamidoethyl)aniline 4.25 g potassium carbonate 30.0 g fluorescent brightening agent (stilbene compound) 1.0 g water ad 1000 ml pH 10.20 The pH was adjusted with potassium hydroxide or hydrochloric acid. (Bleach-fixing solution) Mother liquor ammonium thiosulfate 110 g sodium hydrogensulfite 10 g ammonium iron (III) diethylenetriaminepentaacetate monohydrate 56 g disodium ethylenediaminetetraacetate dihydrate 5 g water ad 1000 ml pH 6.5 The pH was adjusted with aqueous ammonia or hydrochloric acid. (Stabilizer) Mother liquor 1-hydroxyethylidene-1,1'-diphosphonic acid (60%) 1.6 ml bismuth chloride 0.35 g polyvinylpyrrolidone 0.25 g aqueous ammonia 2.5 ml 3Na·nitrilotriacetate 1.0 g 5-chloro-2-methyl-4-isothiazolin-3-one 50 mg 2-octyl-4-isothiazolin-3-one 50 mg fluorescent brightening agent (4,4'-diaminostilbene compound) 1.0 g water ad 1000 ml pH 7.5 The pH was adjusted with potassium hydroxide or hydrochloric acid. A sample of comparative photosensitive material was prepared in the same manner as above except that the comparative support sample b was used. The three samples prepared as above were subjected to the image exposure and development process A. As compared with the image of the comparative photosensitive sample, the image formed according to the present invention had a higher saturation, much more excellent sharpness and particularly improved gradation reproducibility in the shadows. Example 5 Support sample 2 was prepared in the same manner as in Example 1 except that the patterning of the cylinder was conducted suitably in the rolling step. Further, Support sample 3 was prepared by further reducing the patterning of the cylinder. A color reversal photographic paper was prepared by using the Support sample 1 in the same manner as in Example 3. It was developed, omitting the exposure, to obtain a Sample 4. Color Analyzer 307 (a product of Hitachi Ltd.) was used. Regular reflection from light source was eliminated by providing a trap of about 10° in the integrating sphere. The spectral reflectances of the Support Samples 1 to 4 and a were determined using a barium sulfate white plate as the standard. The results are shown in Fig. 1. The spectral reflectances (550 nm) were as follows: Curve No. Sample No. Spectral reflectance (%) A Support sample 1 Present invention without priming layer (aluminum surface) 76.5 B ditto 2 ditto without priming layer 28.0 C ditto 2 ditto with priming layer 28.0 D Support sample 3 ditto without priming layer 16.0 E ditto 4 ditto A priming layer and layers of color reversal photographic paper were formed on the Support sample 1. It was subjected to the development, omitting the exposure, and then bleach-fixed and water-washed. 75.5 F Comparative sample a comparative 1.0 Example 6 The unevennesses on the surfaces of the Support samples 1,2 and 3 (having no priming layer) were determined with a device of measuring the sectional shape (Elionix Co., Ltd.) with a precision of up to 0.1 µm. The results are shown in Figs. 2, 3 and 4. The number of the unevennesses (frequency) was 100 ±50/mm (Support sample 1), 180 ±50/mm (Support sample 2) and 600 ±100/mm (Support sample 3). Example 7 A development photosensitive material having the layer structures as shown in Table 2 was prepared. The preparation methods of emulsions (I), (VI) and (VII) and organic silver salts (1) and (2) will be shown below. Then, a mordant, etc. were applied to the support to prepare a color fixing material. A color image was formed on the material by heat development. high-boiling organic solvent (1): trinonyl phosphate water-soluble polymer (high water-soluble polymer) (1): Sumika Gel L-5 (H) (a product of Sumitomo chemical Co., Ltd.) water-soluble polymer (high water-absorbing polymer) (2): surfactant (1): Aerosol OT surfactant (2): surfactant (3): surfactant (4): surfactant (5): surfactant (6): hardener: 1,2-bis(vinylsulfonylacetamido)ethane silicone oil: acetylene compound: reducing agent (1): mercapto compound (1): mercapto compound (2): sensitizing dye The emulsion used for forming the fifth layer was prepared as follows: Emulsion (I): The following solutions I and II were slowly added to an aqueous gelatin solution (prepared by dissolving 20 g of gelatin, 3 g of sodium chloride and 0.015 g of a compound of the formula: in 800 ml of water and kept at 65°C) under thorough stirring over 70 min. Simultaneously with the start of the addition of the solutions I and II, the addition of a dye solution prepared by dissolving 0.24 g of a sensitizing dye (A): in a solution comprising 120 ml of methanol and 120 ml of water was also started and continued for 60 min. Solution I (600 ml in total) Solution II (600 ml in total) AgNO₃ (g) 100 - KBr (g) - 56 NaCl (g) - 7 Immediately after completion of the addition of the solutions I and II, a solution of 2 g of KBr in 20 ml of water was added thereto and the mixture was left to stand for 10 min. After water washing followed by desalting, 25 g of gelatin and 100 ml of water were added thereto and the pH and pAg were adjusted to 6.4 and 7.8, respectively. The obtained emulsion was a disperse emulsion comprising cubic grains having a size of about 0.5 µm. The emulsion was kept at 60°C. 1.3 mg of triethylthiourea and 100 mg of 4-hydroxy-6-methyl-1,3,3a,7-tetrazaindene were added simultaneously to the emulsion to conduct the optimum chemical sensitization. The yield was 650 g. The emulsion used for forming the third layer was prepared as follows: Emulsion (VI) The following solutions I and II were slowly added to an aqueous gelatin solution (prepared by dissolving 20 g of gelatin, 2 g of sodium chloride and 0.015 g of a compound of the formula: in 800 ml of water and kept at 55°C) under thorough stirring over 60 min. Simultaneously with the start of the addition of the solutions I and II, the addition of a dye solution prepared by dissolving 0.16 g of a sensitizing dye (B): in 80 ml of methanol was also started and continued for 40 min. Solution I (600 ml in total) Solution II (600 ml in total) AgNO₃ (g) 100 - KBr (g) - 56 NaCl (g) - 7 After completion of the addition of the solutions I and II, the mixture was left to stand for 10 min, cooled, washed with water and desalted. 25 g of gelatin and 100 ml of water were added thereto and the pH and pAg were adjusted to 6.5 and 7.8, respectively. Thereafter, triethylthiourea and 4-hydroxy-6-methyl-1,3,3a,7-tetrazaindene were added thereto to conduct the optimum chemical sensitization. The obtained emulsion was a monodisperse emulsion comprising cubic grains having a size of about 0.35 µm. The yield was 650 g. The emulsion used for forming the first layer was prepared as follows: Emulsion (VII): 600 ml of an aqueous solution containing 49 g of potassium bromide and 10.5 g of sodium chloride and an aqueous silver nitrate solution (prepared by dissolving 0.59 mol of silver nitrate in 600 ml of water) were simultaneously added at the same flow rate to an aqueous gelatin solution (prepared by dissolving 20 g of gelatin, 4 g of sodium chloride and 0.02 g of a compound of the formula: in 1000 ml of water and kept at 60°C) under thorough stirring over 50 min. After water washing followed by desalting, 25 g of gelatin and 200 ml of water were added thereto and the pH was adjusted to 6.4. The optimum chemical sensitization was conducted with triethylthiourea and 4-hydroxy-6-methyl-1,3,3a,7-tetrazaindene to obtain 700 g of a monodisperse emulsion (I) comprising cubic grains having an average size of 0.4 µ. The organic silver salts were prepared as follows: Organic silver salt (1): A silver/benzotriazole emulsion was prepared as follows: 28 g of gelatin and 13.2 g of benzotriazole were dissolved in 300 ml of water. The obtained solution was kept at 40°C under stirring. A solution of 17 g of silver nitrate in 100 ml of water was added to the solution over 2 min. The pH of the silver/benzotriazole emulsion was adjusted to form precipitates. The excess salt was removed. The pH was adjusted to 6.30 to prepare 400 g of the silver/benzotriazole emulsion. Organic silver salt (2): 20 g of gelatin and 5.9 g of 4-acetylaminophenylpropiolic acid were dissolved in a mixture of 1000 ml of 0.1% aqueous sodium hydroxide solution and 200 ml of ethanol. The obtained solution was kept at 40°C under stirring. A solution of 4.5 g of silver nitrate in 200 ml of water was added to the solution over 5 min. The pH of the thus prepared dispersion was adjusted to form precipitates and the excess salt was removed. The pH was adjusted to 6.3 to prepare 300 g of the organic silver salt (2) dispersion. The dispersions of the dye-donating substance in gelatin were prepared as follows: 12 g of a yellow dye-donating substance (Y-1), 3 g of (Y-2), 7.5 g of high-boiling organic solvent (1), 0.3 g of reducing agent (1) and 0.3 g of mercapto compound (1) were dissolved in 45 ml of ethyl acetate. The solution was stirred together with 100 g of 10% gelatin solution and 60 ml of 2.5% aqueous sodium dodecylbenzenesulfonate solution. The mixture was treated in a homogenizer at 10000 rpm for 10 min to obtain a dispersion, which will be called "dispersion of yellow dye-donating substance". 15 g of the magenta dye-donating substance (M), 7.5 g of the high-boiling organic solvent (1), 0.3 g of the reducing agent (1) and 0.15 g of the mercapto compound (1) were dissolved in 25 ml of ethyl acetate. The solution was stirred together with 100 g of 10% aqueous gelatin solution and 60 ml of 2.5% aqueous sodium dodecylbenzenesulfonate. The mixture was treated in a homogenizer at 10000 rpm for 10 min to obtain a dispersion, which will be called "dispersion of magenta dye-donating substance". 15 g of the cyan dye-donating substance (C), 7.5 g of the high-boiling organic solvent (1), 0.4 g of the reducing agent (1) and 0.6 g of the mercapto compound (1) were dissolved in 40 ml of ethyl acetate. The solution was stirred together with 100 g of 10% gelatin solution and 60 ml of 2.5% aqueous sodium dodecylbenzenesulfonate solution. The mixture was treated in a homogenizer at 10000 rpm for 10 min to obtain a dispersion, which will be called "dispersion of cyan dye-donating substance". The dye-fixing material was prepared as follows: The following layers were formed on the photographic support of the present invention having the same gelatin priming layer as in the above example to prepare the dye-fixing material. The color photosensitive material comprising the above-mentioned layers was exposed with a xenon flash tube for 1/10⁻⁴ s through a separation filter of G, R and IR (the density being changed continuously). 12 ml/m² of water was applied to the emulsion surface of the exposed photosensitive material with a wire bar and then it was put on the dye-fixing material in such a manner that the layer surfaces were brought in contact with each other. It was heated with a heat roller having a temperature controlled so that the temperature of the water-absorbed film would be 90°C for 20 s. Then, the dye-fixing material was peeled off from the photosensitive material to obtain a yellow, magenta and cyan image corresponding to the separation filter of G, R and IR on the dye-fixing material. Thus, by using the support of the present invention, the transferred dye image having more excellent gradation and higher sharpness than those obtained when an ordinary paper support having the both surfaces laminated with polyethylene was used could be obtained. Example 8 Silver halide emulsion (1) used in this example was prepared as follows: The Solution 1 was heated at 56°C. The Solution 2 and Solution 3 were added to the Solution 1. Then the Solution 4 and Solution 5 were simultaneously added thereto over 30 min 10 min after completion of the addition, the Solution 6 and Solution 7 were simultaneously added thereto over 20 min 5 min after completion of the addition, the temperature was lowered to conduct desalting. Water and gelatin were added thereto and the pH was adjusted to 6.2 to prepare a monodisperse silver chlorobromide emulsion comprising cubic grains having an average grain size of 0.45 µm, a coefficient of variation (calculated by dividing the standard deviation by the average grain size: a/ d ) of 0.08 and a silver bromide content of 70 molar %. Sodium thiosulfate was added to the emulsion and the optimum chemical sensitization was conducted. Silver halide emulsions (2), (3), (4) and (5) having different silver chloride contents were prepared in the same manner as above except that the amounts of KBr and NaCl in the above Solution 4 and Solution 6 and the time required for the simultaneous addition of the Solution 4 and Solution 5 were modified as shown in Table 3. The average grain sizes, coefficients of variation and halogen composition in the Silver halide emulsions (1) to (5) are shown in Table 4. Support (I) of the present invention and a Comparative support (A) used in an ordinary process were prepared as follows: Support (I): Polyethylene was applied to both surfaces of a photographic white base paper to form a laminate. Separately, metallic aluminum was rolled to form a foil. In the rolling by two cylinders, the foil was patterned by means of unevennesses provided on the cylinder surface to make the acid-resistant mirror surface of the aluminum foil uneven and to provide a secondary diffuse-reflective surface. The metallic aluminum foil could be applied to a low-density polyethylene layer, with the diffuse-reflective surface of the foil facing outside, under heating to form a laminate A gelatin prime layer was formed on the thus obtained aluminum foil in the same manner as in the preparation of the Support (I). Comparative support (A): white fine powder of titanium oxide was previously mixed into polyethylene in such a manner that its amount in the resulting laminate would be about 4 g/m². The mixture was applied to the surface of a photographic white base paper and, simultaneously, polyethylene was applied to the other surface of the base paper to form a laminate, i.e. RC paper. A gelatin prime layer was formed on the white polyethylene surface in the same manner as in the preparation of the Support (I). The first to the seventh layers shown in Table 5 were formed on each support to prepare a laminate, i.e. color photographic material. The first layer : Sensitizing dye (a) was added to Silver halide emulsion (5) in an amount of 7.0 x 10⁻⁴ mol per mol of AgX to conduct the spectral sensitization. Yellow coupler (d), Color image stabilizer (e) and Solvent (f) were mixed together to obtain a solution, which was added to the emulsion in a given amount. The mixture was applied to the support to form the first layer. The third layer : Sensitizing dye (b) was added to Silver halide emulsion (3) in an amount of 4.0 x 10⁻⁴ mol per mol of AgX to conduct the spectral sensitization. Magenta coupler (h) and Color image stabilizer (i) were mixed with Solvent (j) to obtain a solution, which was added to the sensitized emulsion in a given amount. The resulting mixture was for forming the third layer. The fifth layer : Sensitizing dye (c) was added to Silver halide emulsion (2) in an amount of 1.0 x 10⁻⁴ mol per mol of AgX to conduct the spectral sensitization. Cyan coupler (n) and Color image stabilizer (o) were mixed with Solvent (f) to obtain a solution, which was added to the sensitized emulsion in a given amount. The resulting mixture was for forming the fifth layer. Emulsions for forming the second layer, the fourth layer, the sixth layer and the seventh layer were prepared in the same manner as above. The emulsions for forming the first, second, third, fourth, fifth, sixth and seventh layers were applied successively on the prime layer formed on the support to prepare Samples 1 and 2 and Comparative Sample a. Support Coating composition Sample 1 Support I Table 3 Comparative sample a Support A ditto The above prepared samples were subjected to sensitometric gradation exposure through a blue/green/red separation filter or to enlargement print image exposure through a negative film by using 2854 K light source. After the color development, bleach fixing and rinse, a photographic image was obtained. (a) blue-sensitive sensitizing dye (b) green-sensitive sensitizing dye (c) red-sensitive sensitizing dye (d) yellow coupler (e) color image stabilizer (f) solvent (g) color-mixing inhibitor (h) magenta coupler (i) color image stabilizer (j) solvent (k) U.V. absorber mixture of and in a molar ratio of 1:5:3 (l) color-mixing inhibitor (m) solvent (n) cyan coupler (o) color image stabilizer mixture of and in a molar ratio of 1:3:3 (p) magenta coupler (Note) (q) cyan coupler Development Developer A 35°C 45 s Bleach-fixing Bleach-fixing solution A 35°C 45 s Rinsing Rinsing solution A 28 to 35°C 1 min 30 s Color developer A: water 800 ml diethylenetriaminepentaacetic acid 1.0 g sodium sulfite 0.2 g N,N-diethylenehydroxylamine 4.2 g potassium bromide 0.6 g sodium chloride 1.5 g triethanolamine 8.0 g potassium carbonate 30 g N-ethyl-N-(β-methanesulfonamidoethyl)-3-methyl-4-aminoaniline sulfate 4.5 g 4,4'-diaminostilbene fluorescent brightener (White x 4; a product of Sumitomo Chemical Co., Ltd.) 2.0 g water ad 1000 ml pH adjusted with KOH to 10.25 Bleach-fixing solution A: ammonium thiosulfate (54 wt.%) 150 ml Na₂SO₃ 15 g NH₄(Fe(III)(EDTA)) 55 g In the visual inspection of the photographic image, it was noted that the saturation, particularly that of yellow and magenta, was quite excellent. Surprisingly, the sharpness was remarkably improved. Further, the details of the shade gradation were reproduced clearly. The results of the inspection will be shown below as the photographic physical properties. Example 9 Silver halide emulsion layers were formed as shown in Table 6. The thus obtained Sample 4 was subjected to the sensitometric stepwise exposure and printing imagewise exposure by using a white light source and developed under the following conditions: (processing step) the first development (black-and-white development) 38°C 1 min 15 s water washing 38°C 1 min 30 s reversal exposure 100 Lux or above 1 min or longer color development 38°C 2 min 15 s water washing 38°C 45 s bleach-fixing 38°C 2 min 00 s water washing 38°C 2 min 15 s The processing solutions had the following compositions: (Compositions of processing solutions) The first developer pentasodium nitrilo-N,N,N-trimethylenephosphonate 0.6 g pentasodium diethylenetriaminepentaacetate 4.0 g potassium sulfite 30.0 g potassium thiocyanate 1.2 g potassium carbonate 35.0 g potassium hydroquinonemonosulfonate 25.0 g diethylene glycol 15.0 ml 1-phenyl-4-hydroxymethyl-4-methyl-3-pyrazolidone 2.0 g potassium bromide 0.5 g potassium iodide 5.0 mg water ad 1 ℓ (pH 9.70) Color developer benzyl alcohol 1.5 ml diethylene glycol 1.2 ml pentasodium nitrilo-N,N,N-trimethylenephosphonate 0.5 g pentasodium diethylenetriaminepentaacetate 2.0 g potassium sulfite 2.0 g potassium carbonate 25.0 g hydroxylamine sulfate 3.0 g N-ethyl-N-(β-methanesulfonamidoethyl)-3-methyl-4-aminoaniline sulfate 5.0 g potassium bromide 0.5 g potassium iodide 1.0 mg water ad 1 ℓ (pH: 10.70) Bleach-fixing solution disodium ethylenediaminetetra<-> 5.0 g acetate dihydrate ammonium Fe(III) ethylenediaminetetraacetate monohydrate 80.0 g potassium sulfite 15.0 g sodium thiosulfate (700 g/ℓ) 160.0 ml glacial acetic acid 5.0 ml water ad 1 ℓ (pH: 6.50) A comparative sample b was prepared in the same manner as in Example 9 except that the Comparative support A was used as the support. The development process was conducted in the same manner as above to obtain an image. As compared with the image formed by using the Comparative sample b, the image formed by using the Sample 4 had remarkably improved saturation, gradation reproduction in the shades and particularly sharpness as shown in Example 8. Experimental Example 1 The Sample 1 prepared in Example 8 and Comparative sample a were subjected to the separation exposure through a band-pass color filter (light source: 2854 K). The spectral transmittance is shown in Fig. 9. After the color development, bleach-fixing and rinsing steps conducted in the same manner as in Example 8, a color image (yellow, magenta and cyan) was formed. The spectral absorption characteristics thereof were examined by means of Color Analyzer 307 (a product of Hitachi, Ltd.) to obtain the results shown in Fig. 5 (BL, yellow color image), Fig. 6 (GL, magenta color image) and Fig. 7 (RL, cyan color image). The results obtained by using the Sample 1 of the present invention are shown by a solid line and those obtained by using the Comparative sample a are shown by a broken line. The maximum density is represented as 1.0. It will be understood that the color image according to the present invention had a sharp spectral absorption distribution and an improved saturation. Experimental Example 2 CTF of each of RL, GL and BL of the color photosensitive material of the present invention was determined. CTF is a ratio of a density amplitude at a frequency of substantially 0 to a density amplitude at a varied frequency. The Sample 1 of the present invention and the Comparative sample a to which a square waves chart of varied frequency was closely applied were exposed through an R, G, B separation filter and then subjected to a given development process in the same manner as in Example 8. The thus obtained image was examined with a microdensitometer (aperture: 2 µm x 100 µm width) to obtain the results shown in Fig. 8. The results obtained by using the Sample 1 are shown by a solid line and those obtained by using the Comparative sample are shown by a broken line. These results indicated that the image obtained by using the Sample 1 of the present invention had a remarkably high sharpness. The closer the silver halide layer to the support, the higher the sharpness. This is a surprising effect. Example 10 Metallic aluminum was roughly rolled. The aluminum sheets were then rolled in an apparatus comprising a central roller and two rollers arranged above and below the central one each in contact with the central one. In this step, two sheets of annealed metallic aluminum were put together and passed between the upper roller and the central roller and then between the central one and the lower one to prepare aluminum foils having a thickness of about 10 µm. Surprisingly, the surfaces of the foils contacted with each other had the secondary diffuse-reflecting properties. A photographic white base paper was extrusion-coated with a low-density polyethylene and laminated with the metallic aluminum. Then the other surface of the support was subjected to a corona discharge and extrusion-coated with the high-density polyethylene to form a polyethylene layer having a thickness of 30 µm. The thus prepared support having the secondary diffuse-reflective aluminum surface will be referred to as Support Sample 1. Separately, an ionomer resin was applied to the aluminum surface. After drying followed by corona discharge treatment, a prime layer comprising gelatin and 2,4-dichloro-6-hydroxy-1,3,5-triazine was formed thereon. The product will be referred to as Sample 1-a. Fluorescent brightener WE-1 was dissolved in a mixture of methanol and water (1:1). The mixture was mixed in an ionomer resin/latex dispersion and the obtained mixture was applied to the aluminum surface in such a manner that the amount of WE-1 in the ionomer resin layer would be 50 mg/m². A gelatin prime layer was formed thereon in the same manner as in Sample 1-a to obtain Sample 1-1. The spectral reflectances of the three Samples 1, 1-a and 1-1 were determined with Color Analyzer 307 (a product of Hitachi, Ltd.) with a xenon lamp to obtain the results shown in Fig. 10. It will be understood that by providing the prime layer, the defect, i.e. yellowing could be overcome by changing it into white or blue under the irradiation with a light of about 420 to 470 nm. Example 11 A polyethylene phthalate film having a thickness of 100 µm was placed in a vacuum deposition apparatus and aluminum was deposited thereon in vacuum (0,001Pa (10⁻⁵ Torr)) to form an aluminum film having a thickness of 10nm (100 Å) according to a process shown in Example 1 of Japanese Patent Application No. 60-52788 (Japanese Patent Public Disclosure No. 61-210346). The film was then coated with a low-density polyethylene to form a polyethylene layer having a thickness of about 15 µm. The product will be referred to as Sample 2. 4.25 g of gelatin was swelled and dissolved in 50 ml of water. 0.25 g of Polymer P-1 was stirred thoroughly with a mixture of methanol and water (1:4). The solution was thoroughly stirred together with the thus obtained mixture. 1.5 ml of 2% solution of 1,3-bisvinylsulfonyl-2-propanol (hardener) in methanol was added to the mixture. The Sample-2 was subjected to the corona discharge treatment and the coating solution to which a suitable amount of water had been added was applied thereto in such a manner that WE-2 content would be 80 mg/m² to form a prime layer. The product will be referred to as Sample 2-1. On the other hand, a prime layer comprising gelatin and the hardener was formed on the support to prepare Sample 2-a. A silver chlorobromide emulsion layer (halogen composition: 67% AgCl, average grain diameter: 0.4 µm) which was the same as that in ordinary photographic paper was formed thereon and further a protective layer was formed thereon. The products will be referred to as Sample 3 and Sample 3-a. The amount of silver applied was 2.1 g/m². After exposure through a negative film followed by the development with a developer D-72 (1:2 dilution) for 2 min, it was fixed and water washed. In both samples, the highlights were bright and the gradation in the shades was excellent and sharp. Surprisingly, the Sample 2-1 was superior to the Sample 2-a in degree of whiteness in the highlights, and the maximum density and shadow saturation of the former were not inferior to those of the latter. Example 12 1 g of C-4 was dissolved in a mixture of methanol and toluene. 1 g of polyvinyl alcohol and 0.5 g of p-ethoxyacetanilide were dissolved in ethyl acetate. The solutions were dispersed in gelatin and the dispersion was dispersed in the silver halide emulsion of Sample 3-a in such a manner that the amount of C-4 would be 80 mg/m² as in Example 2. The product will be referred to as Sample 4. This product was processed in the same manner as in Example 11 to prepare a photograph, in which the degree of whiteness in the highlights was higher than that in a photograph of Sample 3-a. Example 13 Silver halide emulsion (1) used in this example was prepared as follows: The Solution 1 was heated at 56°C. The Solution 2 and Solution 3 were added to the Solution 1. Then the Solution 4 and Solution 5 were simultaneously added thereto over 30 min 10 min after completion of the addition, the Solution 6 and Solution 7 were simultaneously added thereto over 20 min. 5 min after completion of the addition, the temperature was lowered to conduct desalting. Water and gelatin were added thereto and the pH was adjusted to 6.2 to prepare a monodisperse silver chlorobromide emulsion comprising cubic grains having an average grain size of 0.45 µm, a coefficient of variation (calculated by dividing the standard deviation by the average grain size: S/ d ) of 0.08 and a silver bromide content of 70 molar %. Sodium thiosulfate was added to the emulsion and the optimum chemical sensitization was conducted. Silver halide emulsions (2), (3), (4) and (5) having different silver chloride contents were prepared in the same manner as above except that the amounts of KBr and NaCl in the above Solution 4 and Solution 6 and the time required for the simultaneous addition of the Solution 4 and Solution 5 were modified as shown in Table 8. The average grain sizes, coefficients of variation and halogen composition in the Silver halide emulsions (1) to (5) are shown in Table 9. Emulsion Average grain size (µm) Coefficient of variation (s/ d ) Halogen composition (%) Br Cl (1) 0.45 0.08 70 30 (2) 0.45 0.07 30 70 (3) 0.45 0.07 15 85 (4) 0.45 0.08 5 95 (5) 0.45 0.08 1 99 The Samples 1-1 and 1-a prepared in Example 11 were used as the supports. The first to the seventh layers shown in Table 10 were formed on each supports to prepare a laminate, i.e color photosensitive material. The first layer : Sensitizing dye (a) was added to Silver halide emulsion (5) in an amount of 7.0 x 10⁻⁴ mol per mol of AgX to conduct the spectral sensitization. Yellow coupler (d), Color image stabilizer (e) and Solvent (f) were mixed together to obtain a solution, which was added to the emulsion in a given amount. The mixture was applied to the support to form the first layer. The third layer : Sensitizing dye (b) was added to Silver halide emulsion (3) in an amount of 4.0 x 10⁻⁴ mol per mol of AgX to conduct the spectral sensitization. Magenta coupler (h) and Color image stabilizer (i) were mixed with Solvent (j) to obtain a solution, which was added to the sensitized emulsion in a given amount. The resulting mixture was for forming the third layer. The fifth layer : Sensitizing dye (c) was added to Silver halide emulsion (2) in an amount of 1.0 x 10⁻⁴ mol per mol of AgX to conduct the spectral sensitization. Cyan coupler (n) and Color image stabilizer (o) were mixed with Solvent (f) to obtain a solution, which was added to the sensitized emulsion in a given amount. The resulting mixture was for forming the fifth layer. Emulsions for forming the second layer, the fourth layer, the sixth layer and the seventh layer were prepared in the same manner as above. The emulsions for forming the first, second, third, fourth, fifth, sixth and seventh layers were applied successively on the prime layer formed on the support to prepare Samples 5 and 6 and Comparative Sample A. Sample 7 was prepared by using the supports of Sample 1-1 and Sample 1-a in the same manner as above except that 0.11 g/m² of F-1 was incorporated in the sixth layer and that the composition forming the fifth layer was modified as follows: The fifth layer (red-sensitive layer) silver halide emulsion (2) silver: 0.25 g/m² gelatin 0.80 g/m² cyan coupler (n) 0.30 g/m² C-1 0.30 P-1 0.05 color image stabilizer (o) 0.17 solvent (f) red-sensitive sensitizing dye (c) 0.20 Photosensitive material Support Coating composition Characteristics 5 1-1 Table 8 F-1 was added to the sixth layer and WF-1 was added to the prime layer A (comparative) 1-a ditto - 6 1-1 Table 11 WF-1 was added to the prime layer and C-1/P-1 was added to the fifth layer 7 1-a ditto C-1/P-1 was added to the fifth layer The above prepared samples were subjected to sensitometric gradation exposure through a blue/green/red separation filter or to enlargement print image exposure through a negative film by using 2854°K light source. After the color development, bleach-fixing and rinse, a photographic image was obtained. In the visual inspection of the photographic image, it was noted that the saturation, particularly that of yellow and magenta, was quite excellent. Surprisingly, the sharpness was remarkably improved. Further, the details of the shade gradation were reproduced clearly. The image had a saturation and image sharpness equivalent to those obtained in Example 1 of Japanese Patent Application No. 61-168802. As compared with the Sample A, samples I and II had an improved degree of whiteness. Particularly, an improvement in the degree of whiteness and brightness was observed in the highlights of the Sample II and a photograph having a high natural sense was obtained when the Sample II was used. (a) blue-sensitive sensitizing dye (b) green-sensitive sensitizing dye (c) red-sensitive sensitizing dye (d) yellow coupler (e) color image stabilizer (f) solvent (g) color mixing inhibitor (h) magenta coupler (i) color image stabilizer (j) solvent (k) U.V. absorber mixture of and in a molar ratio of 1:5:3 (l) mixing inhibitor (m) solvent (n) cyan coupler (o) color image stabilizer mixture of and in a molar rating of 1:3:3 (p) magenta coupler (q) cyan coupler (Note) Bleach-fixing solution A: ammonium thiosulfate (54 wt.%) 150 ml Na₂SO₃ 15 g NH₄(Fe(III)(EDTA)) 55 g EDTA·2Na 4 g glacial acetic acid 8.61 g water ad 1000 ml (pH 5.4) Rinsing solution A EDTA·2Na·2H₂O 0.4 g water ad 1000 ml (pH 7.0) Development Developer A 35°C 45 s Bleach-fixing Bleach-fixing solution A 35°C 45 s Rinsing Rinsing solution A 28 to 35°C 1 min 30 s Color developer A: water 800 ml diethylenetriaminepentaacetic acid 1.0 g sodium sulfite 0.2 g N,N-diethylenehydroxylamine 4.2 g potassium bromide 0.6 g sodium chloride 1.5 g triethanolamine 8.0 g potassium carbonate 30 g N-ethyl-N-(β-methanesulfonamidoethyl)-3-methyl-4-aminoaniline sulfate 4.5 g water ad 1000 ml pH adjusted with KOH to 10.25 Example 14 The diffuse-reflectivity of the support of this invention was measured. The Sample 1 of this invention prepared in the Example 1 and the Comparative sample b (resin coated paper) used in the Example 2 were used as samples for the measurement. Light from light source A was directed onto each sample at an angle of 5° from normal and the angle distribution of the scattered light was measured by a goniophotometer (type GP-1R, manufactured by Murakami shikisai Gijutsu Kenkyusho). The result is shown in Fig. 11. In the figure, relative reflectance (logarithmic scale) is shown in the area over the straight line between -90° and 90° and relative transmittance is shown in the area below the straight line between -90° and 90°. In Fig. 11, the solid line a and the broken line b are reflectance of the Sample 1, the solid line c and the broken line d are reflectance of the Comparative sample b , and the solid line e and the broken line f are transmittance of the Comparative sample b . The reflectance and transmittance shown by the solid lines were measured by directing light onto the samples at an angle of 5° from normal in the longitudinal direction of the samples. The reflectance and transmittance shown by the broken lines were measured by directing light onto the samples at an angle of 5° from normal in the transverse direction of the samples. As seen from Fig. 11, the support of the present invention (Sample 1) has stronger reflectance than the conventional support (Comparative sample b ) within the visual angle (± 40°), which is important for the observation of a color photograph, and no light transmitted through the Sample 1 was observed. Further, the anisotropy observed on the sample 1 was relatively small.

Claims: A color photosensitive material comprising two or more silver halide emulsion layers having different spectral sensitivities, a thin solid metal film layer having a secondary diffuse-reflective surface, and a substrate, wherein said thin solid film layer is located between the emulsion layers and the substrate, and wherein said thin solid metal film layer has a reflectance of at least 0.5 and an average uneveness of 0.1 to 2000 unevenness/mm. The color photosensitive material of claim 1 wherein the metal is aluminium, silver, gold, nickel, magnesium or an alloy of them. The color photosensitive material of claim 1 wherein a thermoplastic resin layer of an adhesive layer is provided between the thin solid film layer and the substrate. The color photosensitive material of claim 1 wherein the secondary diffuse-reflective surface of the thin solid film layer is obtained by making a mirror surface of the thin solid film layer uneven to form 0.1 to 2000 unevennesses/mm. The color photosensitive material of claim 1 wherein the substrate is a paper. The color photosensitive material of claim 5 wherein a thermoplastic resin layer or a water resistant resin layer is provided on the surface of the substrate opposite to that having the thin solid film layer. The color photosensitive material of claim 1 which comprises an emulsion layer (BL) containing silver halide grains having a spectral sensitivity in a wavelength region of 400 to 500 nm and finely dispersed yellow color coupler grains, an emulsion layer (GL) containing silver halide grains having a spectral sensitivity in a wavelength region of 500 to 580 nm and finely dispersed magenta color coupler grains and an emulsion layer (RL) containing silver halide grains having a spectral sensitivity in a wavelength region of 580 to 740 nm and finely dispersed cyan color coupler grains in any order. The color photographic sensitive material of claim 1 wherein a resin layer is provided on the support and between the support and the silver halide emulsion layers. The color photosensitive material of claim 1 wherein a fluorescent brightener is contained in at least one of the layers formed on the support. The color photosensitive material of claim 9 wherein the layers formed on the support are a prime layer, a photosensitive layer, an intermediate layer and a protective layer. The color photosensitive material of claim 10 wherein the fluorescent brightener is contained in at least one of the prime layer, intermediate layer and protective layer. The color photosensitive material of claim 1 wherein a fluorescent brightener which liberates a fluorescent brightening residue upon the reaction with an oxidation product of a developing agent is contained in a photosensitive layer, or an intermediate layer or a protective layer adjacent to the photosensitive layer formed on the support. The color photosensitive material of claim 12 wherein the fluorescent brightener is a compound of the general formula (I): A-(L) a -Fl (I) wherein Fl represents a fluorescent brightening compound residue, L represents a connecting group, a represents a number of 1 or 2 and A represents a color compound-forming coupler residue, a colorless compound-forming coupler residue or a hydroquinone residue, the residue being that of a compound capable of participating in an exchange reaction with an oxidation product of a developing agent.

Inventors: FUCHIZAWA, TETSURO C/O FUJI PHOTO FILM CO., LTD., OGAWA, TADASHI C/O FUJI PHOTO FILM CO., LTD., SANO, MASARU C/O FUJI PHOTO FILM CO., LTD., SHIBA, KEISUKE C/O FUJI PHOTO FILM CO., LTD., TAGUCHI, SEIICHI C/O FUJI PHOTO FILM CO., LTD.
Applicants: FUJI PHOTO FILM CO., LTD.
Application year: 1987
Main classification: G03C1
IPC codes: G03C1