ARTICLE FOR ADMINISTRATION OF PHARMACOLOGICALLY-ACTIVE SUBSTANCES

Abstract: Described is an article of manufacture useful in administration of pharmacologically-active substances, transdermally, orally or by means of subdermal implant comprising a plasticized polyvinyl chloride layer for con­ tacting a patient's tissue, internally or externally, the layer containing from about 20 up to about 70% by weight of a polyvinyl chloride resin or a polyvinyl chloride-­ polyvinyl acetate copolymer containing a minor proportion of vinyl acetate; from about 20-70% plasticizer composition; from about 0.5 up to 35% of a pharmacologically-active sub­ stance such as isosorbide dinitrate, nicotine, clonidine, guanfacine, indomethacin, glyceryl trinitrate and prosta­ glandin and optionally excipients. Also described is the novel plasticizer-polyvinyl chloride composition of matter comprising 1-dodecylhexahydro-2H-azepin-2-one and polyvinyl chloride resin taken together with a pharmacologically-active substance wherein the 1-dodecylhexahydro-2H-azepin-2-one not only acts as a plasticizer but also acts as a penetration enhancer (through tissue) for the pharmacologically-active substance.

Description: BACKGROUND OF THE INVENTION 1. Field of the Invention This invention relates broadly to articles of manufacture for administration of pharmacologically-active substances, transdermally, orally and by means of implant (e.g., sub-dermal implant). The devices consist essentially of a vinyl chloride polymer or copolymer of vinyl chloride containing a majority of vinyl chloride monomeric units and a small amount of other vinyl monomeric units, e.g., vinyl acetate, and intimately dispersed therewith at least one of said pharmacologically-active agents and a plasticizer. Examples of pharmacologically-active agents are isosorbide dinitrate, nicotine, indomethacin, clonidine, glyceryl trinitrate, guanfacine and prostaglandin. Contemplated within the scope of this invention are devices for the controlled release and transdermal administration of such pharmacologically-active agents as nitroglycerine (e.g., in the treatment of conditions, e.g., angina pectoris). 2. The Prior Art Many prior art articles of manufacture have been disclosed for controlled release delivery of various drugs including transdermal delivery of nitroglycerin. In general, however, available commercial devices and indeed devices published in the prior art are limited with respect to rate of delivery of pharmacologically-active substance. Canadian Patent No. 930,668 discloses a bandage for administering drugs comprised of a backing member, a pressure sensitive adhesive, and at least one reservoir disposed between the backing member and pressure sensitive adhesive. The reservoir is comprised of a systemically active drug formulation confined within a wall member, the wall member being formed from a drug release rate controlling material. The reservoir can be in the form of discrete microcapsules or distinct reservoir compartments or layers. The reservoir can also be in the form of walled containers having one or more interior drug-containing chambers, as well as solid matrices having a systemically active drug distributed there-through. The Canadian patent discloses a wide variety of materials which can be used to form the reservoir. Among the materials mentioned are silicone rubbers, hydrophilic polymers of monoesters of an olefinic acid, polyvinylalcohol, polyvinylacetate, plasticized polyvinylchloride, plasticized nylon, collagen, modified collagen, gelatin, and waxes such as polyethylene wax, oxidized polyethylene wax, hydrogenated castor oil and the like, with the silicone rubbers being preferred. Similarly, Zaffaroni, United States Letters Patent 3,921,636 issued on November 25, 1975 discloses a drug delivery device for administering a drug at a controlled rate for a prolonged period of time comprising a plurality of reservoirs containing drug distributed through a matrix. The reservoirs and the matrix are formed of materials permeable to passage of the drug. The rate of drug permeation from the reservoir is lower than the rate of permeation through the matrix so that release from the reservoir is the drug release rate controlling step. Thus, Example 6, at column 15, lines 5-30 of U.S. Letters Patent 3,921,636 relates to a polyvinyl chloride resin containing plasticizer and prednisolone disodium phosphate thusly: "A drug delivery device for the controlled, oral administration of water-soluble prednisolone is prepared as follows: first, a plurality of drug reservoirs comprising porous, discrete particles of polymerized poly(vinyl chloride) of about 100 microns diameter are prepared by mixing 100 g of suspension grade poly(vinyl chloride) resin with 50 g of octyl diphenyl phosphate and 10 g of prednisolone disodium phosphate at room temperature into a sticky, wet mass. Next, the temperature of the mixture is raised to 80°C for about 3 to 7 minutes, while stirring, to form dry, free flowing, discrete drug reservoirs. The reservoirs are uniformly dispersed through a matrix by mixing 50 g of reservoirs containing the prednisolone with 140 g of polydimethylsiloxane, 10 g of silicone oil, and 0.5 g of stannous octoate. After mixing the ingredients, the mixture is charged into pill mods and allowed to cure for 30 minutes. Oral administration of the resulting device yields a controlled essentially constant rate of release of prednisolone phosphate to the gastrointestinal tract to give a more uniform blood level of prednisolone over a longer period of time than is achieved when prednisolone alcohol is administered by standard prior art pills." United States Letters Patent 4,150,109 (Dick, et al) issued on April 17, 1979 entitled "Devices for Protecting Animals from Ectoparasites" discloses and claims: "In an animal collar for controlling fleas and ticks on cats and dogs, a part of said animal collar being formed of a solid vinyl or vinylidene polymer matrix in which is dispersed a pesticidal composition, an improved pesticidal composition consisting essentially of: (a) 0.5 to 15% by weight of an ethylenically unsaturated oil, and (b) a mixture of diethyl-0-(2-isopropyl-4-methyl-6-pyrimidinyl)thionophosphate and diethyl-0-(2-isopropyl-4-methyl-6-pyrimidinyl)phosphate, wherein diethyl-0-(2-isopropyl-4-methyl-6-pyrimidinyl) thionophosphate is 10 to 90% by weight of said mixture and diethyl-0-(2-isopropyl-4-methyl-6-pyrimidinyl) phosphate is 90 to 10% by weight of said mixture." wherein the "solid vinyl...matrix" and the plasticizers are described thusly: "The macromolecular substance preferably has a weight of more than 1000; it is selected from the homopolymers and copolymers obtained starting from vinyl chloride, vinyl acetate, vinyl acetals, vinylalcohol, vinylbenzene and divinylbenzene and vinylidene chloride; the copolymers may, in addition, contain additional components such as ethylenic, propylenic, butadienic, isoprenic, acrylic and methacrylic components. Preferably, the macromolecular substance is a polymer or copolymer of a vinyl compound such as, for example, the polyvinyl halides. The particularly preferred macromolecular substances are polymers or copolymers of vinyl chloride. The macromolecular substance preferably contains one or more plasticizers. The plasticizers are liquid esters with a vapour pressure of less than 0.0001 mm/Hg at 25°C. Some nonrestrictive examples of plasticizers are: diethyl, dimethyl, dipropyl, dibutyl, dihexyl, dioctyl and didecyl phthalate, dibutyl, diamyl, dinonyl, dioctyl, and didecyl adipate, dipropyl, dibutyl, dibenzyl and dioctyl sebacate, diethyl, dipropyl and dibutyl citrate, triphenyl and tricresyl phosphates and the triglycerides. The preferred plasticizers are dibutyl phthalate and dioctyl adipate, which make it possible to obtain an arrangement with good flexibility, on the surface of which the active principle appears rapidly and regularly." Furthermore, as is well known, polyvinyl chloride (PVC) is never used alone, but is always mixed with other ingredients before being processed. Polyvinyl chloride appeared initially to be an unpromising resin because of its thermal instability and high rigidity. PVC, however, was then discovered to form a rubber-like material when dissolved hot in high boiling solvents known as plasticizers and cooled to room temperature. PVC is now available in a number of different physical forms and types, and its manufacture depends on the form desired. Thus, PVC is available as a vinyl latex, a dispersion resin, or a general purpose resin. PVC latexes are true colloidal dispersions of submicrometer particles in water, stabilized by a surfactant system, and need plasticizers in order to form a continuous film. The PVC in vinyl latex is manufactured by emulsion polymerization. Dispersion resins are produced by emulsion polymerization and are mixed with plasticizers to form a colloidal dispersion. Such dispersions are known as plastisols and are easily handled and readily pourable. When heated to a temperature of about 148 to 177°C, the plastisol is transformed to a homogeneous melt which, upon cooling to below 50°C, results in a tough flexible product. The PVC resins made by emulsion polymerization are hard spheres of particle size between about 0.05 and 20µm, such as between 1 and 20µm. They do not have the ability to absorb plasticizers. Therefore, a mixture containing, for example, 30% Plasticizer and 70% PVC resin, produces a flowable liquid, known as "plastisol". General purpose PVC resins are made by mass and suspension polymerization process, and comprise the largest amount of PVC resins produced, such as at least 80% of all PVC resins, and are used chiefly to make so-called 100% vinyl products by a variety of molding and extrusion techniques. Resins intended for flexible applications should have good uptake of plasticizer in a dry blending operation and contain more than 25% of a plasticizer system. PVC compounds that contain less than 25% plasticizers are referred to as semi-rigid compounds The PVC resins manufactured by suspension and bulk polymerization are 50 to 200, such as 100 to 150µm in diameter, and are like sponges. They are capable of absorbing large amounts of plasticizers, so that even a 50% plasticizer, 50% PVC resin composition would result in a non-flowing, solid material. SUMMARY OF THE INVENTION It is an object of the present invention to provide an article of manufacture which offers enhanced delivery capability of pharmacologically-active agents over prior commercial devices (transdermal devices, articles used to orally administer pharmacologically-active agents and subdermal implants used to administer subdermally pharmacologically-active agents) by providing an article capable of efficaciously administering pharmacologically-active agents such as isosorbide dinitrate, nicotine, indomethacin, clonidine, glyceryl trinitrate, guanfacine, and prostaglandin directly from a plastisol resin layer in which the pharmacologically-active agent is incorporated in relatively high concentrations, e.g., from 0.5 up to 35%. This invention also enables the administration of a pharmacologically-active agent, such as isosorbide dinitrate, nicotine, indomethacin, clonidine, glyceryl trinitrate, guanfacine, and prostaglandin to be achieved through an article of manufacture, e.g., a transdermal delivery device requiring contact with a relatively smaller area of a patient's tissue, such as the epidermis in the case of a transdermal delivery device. Thus, this invention is directed to an article of manufacture incorporating a plasticized polyvinyl chloride resin monolayer for administration of pharmacologically-active agents transdermally, orally or by means of subdermal implant to a patient requiring treatment for a condition such as, for example, angina pectoris (in the case of the use of such materials as nitroglycerin). In particular, it has been found that pharmacologically-active agents such as isosorbide dinitrate, nicotine, indomethacine, clonidine, glyceryl trinitrate, guanfacine and prostaglandin can be homogeneously dispersed in high concentrations in polymerized polyvinyl chloride resin and plasticizer; the composition is fused into a solid layer and the layer is applied onto the tissue of a patient (either transdermally, orally or subdermally) whereby the pharmacologically-active agent is absorbed either (i) through the patient's skin or (ii) through the patient's internal membrane or (iii) directly into the circulation system. BRIEF DESCRIPTION OF THE DRAWINGS Figure 1 is a cross-sectional view of a preferred pharmacologically-active agent delivery device in accordance with this invention. Figure 2 is a plan view of a strip of material in accordance with this invention viewed from the surface which is applied to the patient's skin. Figure 3 is a plan view of material in accordance with this invention viewed from the surface away from the surface which is applied to the patient's skin. Figure 4 is an enlarged sectional schematic view of a specific embodiment of the invention; a transdermal device for controlled release of a pharmacologically-active agent from a plasticized polyvinyl chloride monolayer through a membrane transdermally. Figure 5 is an enlarged sectional schematic view of another embodiment of the invention where there is no membrane separating the plasticized polyvinyl chloride monolayer from the epidermis and whereby pharmacologically-active agent is transported from the plasticized polyvinyl chloride transdermally into the patient. Figure 6 is a perspective view of a roll of material in accordance with this invention. Figure 7 is a graph of tensile strength (expressed in PSI, 1 PSI being equal to 7 kPA) versus percent resin containing either of isosorbide dinitrate, nicotine, indomethacin, clonidine, glyceryl trinitrate or guanfacine, specifically as described herein in the description of Examples VIII-XIII, infra. Figure 8 is a graph showing release rate of pharmacologically-active agent (in micrograms per square centimeter per hour) versus percent resin, individually, for isosorbide dinitrate, nicotine, indomethacin, clonidine, glyceryl trinitrate or guanfacine specifically in relationship to Examples XIV-XIX, infra. Figure 9 is a graph of plasma concentration (picograms per milliliter) versus time detected in a human subject during the clinical study concerning the composition of matter consisting of polyvinyl chloride resin, dioctyl adipate plasticizer and prostaglandin as specifically set forth in Example XX, infra. Figure 10 is a graph showing the effective decrease in diastolic blood pressure of the human subject observed during the period of patch application as specifically set forth in Example XX. Figure 11 is a graph of delivery of nitroglycerin versus time resulting from the use of the formulation of Example XXI. Figure 12 is the infrared spectrum of ADMEX® as used in Examples II-XIX. DETAILED DESCRIPTION OF THE INVENTION In the following, the symbol R indicates a registered trade mark. The invention is described herein with respect to preferred embodiments including transdermal devices containing various pharmacologically-active agents including, but not limited to, indomethacin having the structure: guanfacine having the structure: clonidine having the structure: nicotine having the structure: isosorbide dinitrate having the structure: glyceryl trinitrate and prostaglandin (e.g. methyl (±) - (11α, 5z (and 5E), 13E, 16R(and 16S)-16-ethenyl-11,16 dihydroxy-9-oxoprosta-5, 13-dien-1-oate. It will be understood that other embodiments may be employed within the scope of this invention. The articles of our invention are useful for transdermal, oral and subdermal administration of pharmacologically-active substances and comprise a solid plasticized polyvinyl chloride in the form of a "vinyl plastisol" layer (consisting essentially of polyvinyl chloride and a plasticizer) for contacting a patient's skin or other membrane. The plasticized polyvinyl chloride layer contains from about 20 up to about 70% by weight of a polyvinyl chloride resin which consists essentially of a vinyl chloride polymer containing, predominantly or completely repeating vinyl chloride monomeric units and in an amount of less than about 10% other repeating vinyl units, e.g., repeating vinyl acetate units; from about 20% up to about 70% by weight of the composition of one or more plasticizers; from about 0.5 up to about 35% by weight of the total composition of a pharmacologically-active substance, such as isosorbide dinitrate, nicotine, indomethacin, clonidine, glyceryl trinitrate, guanfacine or prostaglandin and optionally other excipients, such as materials which will accelerate transdermal penetration as exemplified hereinafter. It has now been found that the release rate of an active agent, which is uniformly dispersed in the plasticized polyvinyl chloride layer, is critically dependent upon the proportion of the polyvinyl chloride resin in the composition; and the release follows a bell shaped curve (Figure 8), the maximum occurring in the range of 30 to 50% PVC content. This is an unexpected finding, which has not hitherto been known. Such a release behavior permits tailoring of release rates of an agent from the matrix. The reservoir layers of this invention are relatively weak and less than 10.5 MPa (1500 psi), (Figure 7), highly flexible and soft materials. In contrast, the flexible vinyl films of commerce are considerably stronger materials exhibiting tensile strengths of the order of 10.5 to 35 MPa (1,500 to 5,000 psi). The polyvinyl chloride resin content of the commercially useful and available flexible vinyl films range from 50 to 75%. Such materials do not have adequate drug permeating characteristics to serve as suitable drug delivery reservoirs. Referring to Figure 1, the device 1 includes a solid plastisol monolayer 2 which is composed of or comprises resin, plasticizer and a pharmacologically-active agent as set forth supra. A formulation for layer 2 may comprise from about 20 up to about 70% by weight of the vinyl resin, from about 20 up to about 70% by weight of plasticizer composition, from about 0.5 up to about 35% by weight of pharmacologically-active agent and the remainder being other excipients, such as materials which will enhance skin penetration. We have found that the substance 1-dodecylhexahydro-2H-azepin-2-one (also known as AZONE® having the structure: acts as both a plasticizer and as an agent which enhances transdermal penetration of pharmacologically-active agents such as isosorbide dinitrate, indomethacin, and the like as set forth supra. By the same token, N,N-diethyltoluamide having the structure: acts in the same manner as AZONE®. Thus, for example, for a device suitable in the treatment of angina pectoris, a specific formulation for layer 2 comprises about 54% polyvinyl chloride (PVC) resin, about 36% dioctyl phthalate (DOP) plasticizer and 10% nitroglycerin. To prepare layer 2, the PVC and DOP are first blended. Due to the explosive character of the drug, dispersion of the nitroglycerin into the resulting PVC/plasticizer formulation is then carried out under controlled conditions. The articles of the present invention including the transdermal devices as well as subdermal implants and orally ingested articles of the present invention comprises a plasticized polyvinyl chloride layer and a pharmacologically-active agent uniformly dispersed in the plasticized polyvinyl chloride layer which may be referred to as a reservoir for the pharmacologically-active agent. The polyvinyl chloride reservoir in the present invention is prepared from polyvinyl chloride resin and a primary plasticizer for the resin. The polyvinyl chloride resins employed in the practice of the present invention are those which are specifically used in preparing polyvinyl chloride "plastisols" namely PVC resins which are made by the well known emulsion polymerization process, which are hard spheres of particle size between 0.05 and 20µm, such as between 1 and 20µm, for example, between 1 and 5µm, or between 0.05 and 1µm, and which do not have the ability to absorb plasticizers to any great extent. Instead, the plasticizer wets the resin particles at room temperature and only then very slowly penetrates and solvates the resin. These PVC resins when mixed with plasticizers, such as a mixture of 30% primary plasticizer, 70% PVC resin, give a flowable liquid known as plastisol which can then be fused at, for example, approximately 120°C (250°F) for approximately 30 seconds to provide a solid polymer layer. Thus, the PVC resin preferably employed in the present invention is in contrast to the general purpose PVC resins which are produced by suspension or bulk polymerization and which are used in calendaring and extrusion processes, which are 50 to 200µm, such as 100 to 150µm in diameter, and are like sponges. Thus, the general purpose resins are capable of absorbing large amounts of plasticizers so that even a 50% DOP and 50% PVC resin would result in a non-flowing solid material. The molecular weight of the PVC resins employed in the present invention preferably is a weight average molecular weight between 80,000 and 250,000, such as a weight average molecular weight of 123,000. A suitable polyvinyl chloride regin is one sold by Occidental Chemical Co. under the designation FPC 6338 containing about 96% vinyl chloride monomer units of about 4% vinyl acetate monomer units. Thus, the polyvinyl chloride resin can be a copolymer containing preferably at least 90% by weight vinyl chloride monomer units, such as a copolymer based on vinyl chloride and vinyl acetate. The polyvinyl chloride resin generally is present in the layer in an amount of 10 to 75 weight percent, preferably 20 to 70 weight percent, based on the total weight of the plasticized PVC composition. The primary plasticizer which is employed in the present invention can be dioctylphthalate (DOP), benzylbutylphthalate, tri-2-ethylhexylmalaete, dioctyl adipate, epoxidized soybean oil, polymeric adipate plasticizers, which are polymers of adipic acid with a monomer, such as propylene glycol, and for example, can be obtained under the designation Drapex 334F from Witco Chemical Corp., or any other known primary plasticizer for PVC, which is biologically acceptable. The other examples of polyester adipates, glutarates and sebacates are: polyester adipate P-644; polyester glutarate P-530; polyester glutarate P-540; polyester glutarate P-550; polyester glutarate P-7035; polyester glutarate P-7035M; polyester glutarate P-7046; polyester glutarate P-7092; and polyester sebacate P-1070 manufactured by the C.P. Hall Co., 7300 S. Central Avenue, Chicago, Illinois 60638. Other preferred plasticizers are those which are known as "adipate" plasticizers, for example, ADMEX® 760 which is a high molecular weight (MW = 8000) adipate plasticizer manufactured by the Sherex Division of Nuodex Inc. In general, polyester plasticizers which are polyesters of (i) 1,4-terephthalic acid and/or 1,2-phthalic acid and/or adipic acid with (ii) ethylene glycol or 1,3-propylene glycol having molecular weights in the range of 4000-10,000 are preferred. Another preferred plasticizer which also acts as a skin penetrating enhancer for pharmacologically-active drugs which are intended for transdermal delivery from devices such as those set forth in Figures 1, 5 and 6 is the compound having the structure: known as AZONE® marketed by the Nelson Research and Development Co. The composition comprising PVC and the compound having the structure: is a novel composition of matter. Mixtures of known plasticizers can be used. The term "primary plasticizer" as used herein refers to a plasticizer which can be used alone to effect plasticization and is highly compatible with PVC at high concentrations, such as, for example, 150 parts per hundred. Primary plasticizers are contrasted with "secondary plasticizers" which, because of limited compatibility with PVC, cannot be used alone. See, Kirk-Othmer Encyclopedia of Chemical Technology, Volume 23, 3rd Edition, especially pages 913 and 914 for a discussion of primary and secondary plasticizers, which is incorporated by reference herein. The primary plasticizer generally is present in an amount of 20 to 85 weight percent, preferably 20 to 70% based on the total weight of the plasticized PVC layer. The plasticized PVC plastisol may optionally contain other additives or "excipients" useful in the practice of this invention, for example, material which enhance skin penetrated of the pharmacologically-active substances (e.g., 1,6-hexanediol and n-decyloleate) and thickeners, e.g., silica (preferably "fumed" silica, for example, AEROSIL® in an amount of from 1-6% of the layer). With reference to Figure 1, a blended PVC plastisol containing, for example, PVC, DOP and nitroglycerin is then coated at a rate of about 1.2kg/m² (36 ounces/yd²) on a backing, and then fused into solid plastisol layer 2. The backing may be a single layer of drug impermeable plastic or other material, but is preferably composed of two layers 3 and 4. Layer 3 may be MYLAR® (polyester produced from ethylene glycol and phthalic anhydride) about 13 µm (0.5 mils) thick, and layer 4 may be PVC, about 100 µm (4 mils) thick. The backing 3, 4 substantially blocks loss of drug from the plastisol layer 2 other than in the direction of the surface which, in use, will contact the patient's skin. The blended plastisol which is coated on the backing can be fused into a homogeneous solid by heating it for a short period, such as 15 to 30 seconds, at a temperature of, for example, 120 to 137°C (250 to 280°F). The use of a plastisol to form solid layer 2 enables layer 2 to be formed by using a low temperature for a short period of time, and provide conditions which do not affect the stability of the pharmacologically-active agents. A strip of solid plastisol layer 2 and backing 3, 4 is then bonded to a pressure-sensitive adhesive layer 5 which, in turn, is provided with a non-adhesive backing 6 such as one made of plastic, moisture-proof fabric, aluminum foil, etc. When not in use, the entire surface intended for skin contact is preferably covered with a release paper 7 or the like which is removed to expose surfaces of the adhesive layer 5 and drug containing plastisol layer 2 for application to the patient's skin. Figure 2 shows a plan view of a strip of material 20 during the stage of manufacture at which a strip of the plastisol 2 (backing 3, 4 not shown) has been applied to the adhesive tape (backing 6 not shown). For the preferred device for the controlled administration of pharmacologically-active agent, e.g., indomethacin, isosorbide dinitrate, nicotine, clonidine, glyceryl trinitrate, guanfacine or prostaglandin, a plastisol strip preferably about 2.5 cm (one inch) in width is applied to a 6.5 cm (two and one-half inch) wide pressure-sensitive adhesive strip. Figure 3 shows a plan view of a strip of the material 30 in accordance with this invention; spaced lines 31 may be embossed or printed on the surface away from skin contact so that the patient may conveniently measure out and cut off the proper amount of tape device to provide the prescribed daily dosage. For a device for administering the pharmacologically-active agent, e.g., nitroglycerin, for example, a segment 2.5 cm (1") long from the longer tape (resulting in an approximately 6.5 cm² (one square inch) of active surface against the patient's skin) will provide a dosage of about 17 mg/24 hours; this is believed to be an enhanced rate of delivery compared with commercially available transdermal drug delivery devices and also will provide the patient with a bandage device having a surface area much smaller than found in previously available devices. Referring to Figure 4, the components of embodiment 33 are backing layer 34, a reservoir layer 35 that contains supplies of percutaneous absorption enhancer and pharmacologically-active substance, such as indomethacin, a diffusion membrane layer 36 and a peripheral ring 37 of contact adhesive. The diffusion membrane layer may be composed of a polymer, such as a copolymer of ethylene and methyl acrylate with the methyl acrylate being in the range of 2-90% by weight of the polymer, or blends of such copolymer with low density polyethylene, high density polyethylene or linear low density polyethylene. The contact adhesive component of embodiment 33 is in the form of a peripheral ring. Optionally, backing layer 34 may also be a semi-permeable membrane. Neither the pharmacologically-active agent, e.g., isosorbide dinitrate nor enhancer passes through ring 37 and it therefore need not be permeable to those compositions. Optionally, the contact adhesive may be attached directly to the membrane 36, in which case the adhesive is selected so that is is permeable to the active agent. Secondly, the basal surface from which the pharmacologically-active substance and enhancer (e.g., AZONE®) is transferred to the skin is defined by diffusion membrane layer 36. The backing layer is not flat but instead forms a pocket or cavity in which the reservoir layer is held. The outer edge of the backing layer is sealed to the peripheral ring of the contact adhesive as more specifically set forth in U.S. Letters Patent 4,379,454 issued on April 12, 1983, the disclosure of which is incorporated herein by reference. Similarly, an article within the contemplation of our invention need not have a matrix as is illustrated in Figure 5 wherein the backing 61 totally surrounds the PVC-plastisol-plasticizer matrix 62 and is firmly in placed as with an adhesive on the skin 63. As shown in Figure 6, the device of the invention may conveniently be provided in the form of a tape roll 50 from which daily dosage requirements may be clipped by the patient. The device is capable of application to humans or other animals capable of usefully absorbing drugs through the skin. EXAMPLE I A plastisol was formed by mixing 54% of a polyvinyl chloride resin sold under the designation FPC 6338 by Occidental Chemical Corp. and having a particle size between 1 and 5µm, 36% DOP, and 10% nitroglycerin. The product was coated onto 25µm (1 mil) polyester (MYLAR) film and fused at 137°C (280°F). The final product consisted of 8.8% nitroglycerin, 31.8% DOP, 47.8% FPC 6338, 11.6% polyester. This product can be used for delivery of nitroglycerin percutaneously. EXAMPLES II-XIX FUSED PLASTISOL DRUG RESERVOIR EXAMPLES Fused plastisol drug reservoirs having variable PVC: plasticizer ratios were prepared by heating cast films of the drug-containing plastisols at 142°C (290°F) for 60 seconds. The drugs used were isosorbide dinitrate (ISDN) and nicotine. AZONE® having the structure: (registered trademark of the Nelson Research and Development Co.) and ADMEX® (which is a high molecular weight (MW = 8000) phthalate plasticizer manufactured by the Sherex Division of Nuodex Inc.) were used as primary plasticizers in the case of the ISDN and the nicotine reservoirs, respectively. The films, thus prepared, were optically transparent. Figure 12 is the infrared spectrum of ADMEX® 760. The stress-strain properties of the films were determined employing standard procedures using Instron Universal Testing Instrument. (Instron is a trade mark). The ability of the reservoir to release the drug was evaluated by measuring the dissolution rate of the drug in a fluid medium (receptor phase) when a known surface area of the drug reservoir film was exposed to an excess of the receptor phase at 31°C. The dissolution rate studies were conducted using a Franz diffusion cell. The receptor phase for the nicotine study was pH 4.0 citric acid buffer solution (an aqueous solution containing 1.2% citric acid and 1.1% disodium hydrogen phosphate), and that for the ISDN study was an aqueous solution containing 20% polyethylene glycol 400. The dissolution rate of the drug was calculated from the change in concentration of the drug in the receptor phase at different time intervals. The nicotine and ISDN concentrations were determined by ultra-violet spectroscopy and high pressure liquid chromatographic procedures, respectively. EXAMPLES II-VII In the following formulations (A-F in each of Examples II-VII), the following terms have the following meanings as now given: ISDN : Isosorbide dinitrate having the structure already given above. 6338 : A vinyl chloride-vinyl acetate copolymer having a vinyl acetate content of 4.0-4.5% manufactured and sold by the Occidental Chemical Corporation under the designated FPC 6338. GTN : Glyceryl trinitrate. Guan. : Guanfacine having the structure given above. DOP : Dioctyl phthalate. HG: 1,6-Hexylene glycol. Cer 140 : "Ceraphyl 140" (trade mark) being n-decyl oleate. The remaining terms have the meanings already given above. EXAMPLE II ISDN FORMULATIONS: "A" "B" "C" "D" "E" ISDN 15.0% 15.0% 15.0% 15.0% 15.0% AZONE® 59.5% 51.0% 42.5% 34.0% 25.5% 6338 25.5% 34.0% 42.5% 51.0% 59.5% EXAMPLE III NICOTINE FORMULATIONS: "A" "B" "C" "D" "E" Nicotine 30.0% 30.0% 30.0% 30.0% 30.0% ADMEX® 49.0% 42.0% 35.0% 28.0% 21.0% 6338 21.0% 28.0% 35.0% 42.0% 49.0% EXAMPLE IV INDOMETHACIN FORMULATIONS: "A" "B" "C" "D" "E" Indomethacin 15.0% 15.0% 15.0% 15.0% 15.0% AZONE® 25.5% 34.0% 42.5% 51.0% 55.0% 6338 59.5% 51.0% 42.5% 34.0% 30.0% EXAMPLE V CLONIDINE FORMULATIONS: "A" "B" "C" "D" "E" Clonidine 20.0% 20.0% 20.0% 20.0% 20.0% ADMEX® 60.0% 55.0% 50.0% 45.0% 41.0% 6338 20.0% 25.0% 30.0% 35.0% 44.0% EXAMPLE VI GTN FORMULATIONS: "A" "B" "C" "D" "E" GTN 8.0% 8.0% 8.0% 8.0% 8.0% ADMEX® 62.0% 53.0% 46.0% 39.0% 32.0% 6338 30.0% 39.0% 46.0% 53.0% 60.0% EXAMPLE VII GUANFACINE FORMULATIONS: "A" "B" "C" "D" "E" Guan. 30.0% 30.0% 30.0% 30.0% 30.0% DOP 25.0% 21.0% 18.0% 14.0% 10.0% HG 12.5% 12.5% 12.5% 12.5% 12.5% Cer 140 12.5% 12.5% 12.5% 12.5% 12.5% 6338 20.0% 24.0% 27.0% 31.0% 35.0% NOTE : The hexylene glycol enhances the permeability transdermally of the guanfacine. The Cer 140 adjusts the activity of the guanfacine in the reservoir. EXAMPLES VIII-XIII In the following examples, the chemical terms have meanings as given above already. Figure 7 shows tensile strength versus percent resin for each of the above formulations. The curve indicated by reference numeral 70 is the curve for clonidine. The curve indicated by reference numeral 71 is the curve for guanfacine. The curve indicated by reference 72 is the curve for indocin. The curve indicated by reference numeral 73 is the curve for nicotine. The curve indicated by reference numeral 74 is the curve for isosorbide dinitrate. The curve indicated by reference numeral 75 is the curve for glyceryl trinitrate. EXAMPLE VIII ISDN: % RESIN TENSILE STRENGTH 25.5 57.21 34.0 144.09 42.5 399.54 51.0 663.81 59.5 1077.53 EXAMPLE IX NICOTINE: % RESIN TENSILE STRENGTH 21.0 54.22 28.0 125.51 35.0 204.39 42.0 300.57 49.0 671.30 EXAMPLE X INDOMETHACIN: % RESIN TENSILE STRENGTH 30.0 99.63 34.0 162.00 42.5 495.00 51.0 764.00 59.5 1447.00 EXAMPLE XI CLONIDINE: % RESIN TENSILE STRENGTH 20.0 118.36 25.0 288.70 30.0 308.99 35.0 487.65 44.0 440.16 EXAMPLE XII GTN: % RESIN TENSILE STRENGTH 30.0 17.53 39.0 74.90 46.0 116.43 53.0 738.85 60.0 1339.02 EXAMPLE XIII GUAN.: % RESIN TENSILE STRENGTH 20.0 84.83 24.0 128.40 27.0 180.50 31.0 131.50 35.0 203.21 EXAMPLES XIV-XIX In the following examples, the chemical terms have meanings as set forth above. EXAMPLE XIV ISDN: % RESIN RELEASE 25.5 91.66 34.0 108.90 42.5 93.50 51.0 65.71 59.5 50.29 EXAMPLE XV NICOTINE: % RESIN RELEASE 21.0 40.76 28.0 122.78 35.0 218.25 42.0 243.55 49.0 216.18 EXAMPLE XVI INDOMETHACIN: % RESIN RELEASE 30.0 36.14 34.0 87.01 42.5 68.75 51.0 24.49 59.5 8.65 EXAMPLE XVII CLONIDINE: % RESIN RELEASE 20.0 103.67 25.0 108.22 30.0 80.85 35.0 82.18 44.0 62.81 EXAMPLE XVIII GTN: % RESIN RELEASE 30.0 41.91 39.0 48.54 46.0 42.63 53.0 46.02 60.0 35.81 EXAMPLE XIX GUAN.: % RESIN RELEASE 20.0 31.72 24.0 56.85 27.0 63.06 31.0 88.41 35.0 165.82 Figure 8 is a graph showing release rate in micrograms per square centimeter per hour versus percent resin. The curve indicated by reference numeral 80 is the curve for nicotine. The curve indicated by reference numeral 81 is the curve for clonidine. The curve indicated by reference numeral 82 is the curve for guanfacine. The curve indicated by reference numeral 83 is the curve for isosorbide dinitrate. The curve indicated by reference numeral 84 is the curve for indomethacin. The curve indicated by reference numeral 85 is the curve for glyceryl trinitrate. EXAMPLE XX TRANSDERMAL DELIVERY OF PROSTAGLANDIN FROM DRUG RESERVOIR HUMAN CLINICAL STUDY I. Drug : Prostaglandin (American Cyanamid Co.) Methyl (±) - (11α, 5z (and 5E), 13E, 16R (and 16S)) ethenyl-11,16 dihydroxy-9-oxoprosta-5, 13-dien-1-oate (an analog of Prostaglandin E₂). II. Pharmacological Activity : Antihypertensive III. Patch Formula : PVC Resin 59.7% Dioctyl Adipate 38.2% 50% Prostaglandin in Dioctyl Adipate 2.1% IV. Results : A. The Drug Concentration up to 500 pg/ml was detected in a human subject (Figure 9). B. Effective decrease in diastolic blood pressure of the human subject was observed during the period of patch application (Figure 10). The curve indicated by reference numeral 90 shows plasma concentration in picograms per ml versus time in hours. The curve indicated in Figure 10 by reference numeral 101 shows mean decreases in sitting diastolic blood pressure following administration of the subject patch formula to normal subjects in a cross over study (sample size = 15). The units of pressure are mmHg and the units of time are in hours. EXAMPLE XXI TRANSDERMAL DELIVERY OF NITROGLYCERIN FROM DRUG RESERVOIR-HUMAN CLINICAL STUDY I. Drug : Nitroglycerin (Glyceryl trinitrate) II. Pharmacological Activity : Vasodilator III. Patch Formulation : Nitroglycerin 9.6% Dioctyl Phthalate 76.8% PVC Resin 9.6% Aerosil (Fumed Silica) 4.0% IV. Results : The patch delivered adequate nitroglycerin through skin of human subjects to provide a concentration of 0.1 to 0.2 ng/ml in the blood plasma for a period of 3 days as set forth in Figure 11. The graph indicated by reference numeral 111 is a graph of delivery of glyceryl trinitrate in nanograms/ml versus time (in hours). EXAMPLE XXII IN VIVO TRANSDERMAL DELIVERY OF ISOSORBIDE DINITRATE (ISDN)-FROM DRUG RESERVOIR I. Drug : Isosorbide Dinitrate (ISDN) II. Pharmacological Activity : Vasodilator III. Patch Formula : ISDN (50% on Latose) 15% PVC Resin 30% AZONE® 32% Isopropyl Myristate 20% Aerosil (Fumed Silica) 3% IV. Test Protocol : Formulations containing 7.5% ISDN, and 0, and 32% AZONE® respectively were tested in vivo monkeys. Each formulation was tested on two monkeys for six consecutive days. The patches were firmly placed on the shaved upper innerarm each morning and were left in place for eight hours. For each test condition blood samples of approximately 3-4 ml were withdrawn from an indwelling catheter inserted into the saphenous vein. Blood samples were drawn at 0 (prior to patch application), 4 and 8 hours after dosing. The eight-hour samples were drawn before the patches were removed. The plasma component was immediately separated from the blood by centrifugation at 1200 rpm for 5 minutes, and frozen at -20°C. The samples were then extracted to determine concentrations of ISDN and its metabolites Isosorbide 5-mononitrate (5-ISMN) and Isosorbide 2-Mononitrate (2-ISMN). Upon removal of the patches, the site of application was washed with dilute alcohol and inspected visually. Any changes in the condition of the skin (such as erythema or edema) was scored according to the Draze Scoring System. This inspection was repeated 30 minutes and again before next patch application. V Results : The mean plasma ISDN and metabolite results for the patches are shown in Table I. An increase of 300% to 400% in plasma ISDN concentration was observed for patches containing 32% AZONE®. A maximum of 43.8% ng/ml of plasma ISDN was obtained from 2 patches with a total surface area of 12.5 cm². However, the data did not suggest that there was a linear increase of plasma level with surface area of patch. In general, doubling the patch surface area more than doubled the plasma level, for ISDN as well as the metabolites. 8 HOURS IN VIVO RESULTS OF ISDN PATCHES ON MONKEYS AVERAGE CONCENTRATION (ng/ml) % AZONE® NO. OF PATCHES ISDN 5 ISMN 2 ISMN 0 1 3.46 12.75 3.05 2 19.39 55.52 12.67 12 1 6.08 23.56 4.64 2 30.23 68.43 17.11 32 1 14.14 42.01 9.75 2 43.85 87.85 23.75

Claims: An article for the controlled release and delivery to animal tissue of a pharmacologically active agent, said article comprising a plasticized polyvinyl chloride layer (2) having said pharmacologically active agent uniformly dispersed therethrough, wherein when a surface of said layer (2) is in contact with said animal tissue said pharmacologically active agent is absorbed into and through said tissue and thence into the circulatory system of said animal such that an effective amount of said pharmacologically active agent is absorbed into said animal in a prescribed period of time, characterised in that said plasticized polyvinyl chloride layer (2) is a plastisol and comprises by weight from 20 to 70% of polyvinyl chloride resin, from 20 to 70% of plasticizer and from 0.5 to 35% of said pharmacologically active agent. An article according to claim 1, wherein the plasticizer is a polymeric plasticizer. An article according to claim 2, wherein the polymeric plasticizer is a polyadipate having the IR spectrum of Figure 12 hereof. An article according to any one of claims 1 to 3, in the form of an elongate tape (50) wherein said plastisol layer (2) comprises polyvinyl chloride resin, a polymeric plasticizer or a monomeric plasticizer and said pharmacologically active agent. An article according to any preceding claim, wherein said pharmacologically active agent is selected from the group consisting of isosorbide dinitrate, nicotine, indomethacin, clonidine, glyceryl trinitrate, guanfacine and prostaglandin. An article according to any preceding claim, wherein said polyvinyl chloride is present in an amount of from 30 to 60%, said plasticizer is present in an amount of from 30 to 60% and said pharmacologically active agent is present in an amount of from 0.5 to 35%. An article according to any preceding claim, further comprising a backing layer (3,4) covering the surface of said plastisol layer (2) opposite the tissue contacting surface of said plastisol layer, said backing layer (3,4) forming a barrier substantially blocking release of said pharmacologically active agent from the surface of said plastisol layer opposite the tissue contacting surface, and means for maintaining the tissue contacting surface of said plastisol layer in contact with the tissue of the animal so that transdermal absorption of said pharmacologically active agent takes place. An article according to any preceding claim, wherein the plasticizer is the compound having the structure: An article according to any preceding claim, wherein a rate-controlling membrane (36) for secondary control of release of said pharmacologically active agent is attached on at least one side of the article. A process for manufacturing an article for the controlled release and delivery to animal tissue of a pharmacologically active agent according to any one of claims 1 to 9, comprising the steps of: (i) admixing a polyvinyl chloride resin with a plasticizer to form a polyvinyl chloride resin-plasticizer mixture, said polyvinyl chloride resin being produced by emulsion polymerisation and comprising hard polyvinyl chloride spheres of particle size between 0.05 and 20µm and not having the ability to absorb plasticizer; (ii) admixing said polyvinyl chloride resin-plasticizer mixture with a pharmacologically active agent, wherein the resulting mixture has the following composition: 20 to 70% polyvinyl chloride resin; 20 to 70% plasticizer; and 0.5 to 35% pharmacologically active agent, and wherein said pharmacologically active agent is uniformly dispersed in said polyvinyl chloride resin-plasticizer mixture; and (iii) shaping the resulting mixture into a polyvinyl chloride resin-plasticizer-pharmacologically active agent lamina (2). A process according to claim 10, wherein the mixture of polyvinyl chloride resin, plasticizer and pharmacologically active agent resulting from step (ii) is coated on a backing (3,4) and fused to the backing (3,4) at a temperature of 120 to 137°C (250 to 280°F) for a period of 15 to 30 seconds, thereby forming a polyvinyl chloride layer-backing lamina and the resulting polyvinyl chloride layer-backing lamina is then bonded to a pressure sensitive adhesive layer (5).

Inventors: BERNER, BRET, KYDONIEUS, AGIS, SHAH, KISHORE R.
Applicants: HERCON LABORATORIES CORPORATION
Application year: 1987
Main classification: A61K9
IPC codes: A61K9