PROCESS FOR PREPARING AQUEOUS PAINT COMPOSITION

Abstract: Process for preparing an aqueous paint composition by:- (a) mixing a pigment powder having a particle size less than 20 micrometres, a cross-linking agent and an epoxy resin to form a liquid, solvent-free paste, (b) reacting the resultant paste with a secondary amine, and optionally also a primary amine, to provide for at least one N-H function per epoxy group of the epoxy resin, at a temperature in the range 20 °C to 140 °C, and (c) neutralising the resulting suspension of particles coated with epoxy-amine adduct and cross-linking agent.

Description: This invention relates to a process for preparing an aqueous paint composition and to a process for coating a surface by applying said composition. U.S. Patent Specification 4,100,315 discloses a method of preparing aqueous coating powder dispersions containing as the binder a solid epoxy resin, which is micronized in water in the presence of a specific combination of surfactants. For many applications, however, the presence of surfactants in the cured coating is not desirable. European Patent Application No. 84201186.8 (EP-A 136743) discloses the preparation of a solvent-free aqueous binder composition which comprises:- a) dispersing pigment powder having a particle size less than 20 micrometres in a liquid, solvent-free epoxy resin, b) dispersing the resultant paste in water, c) reacting the resultant dispersion with a secondary amine, and optionally also a primary amine, the amount of amine or amines being sufficient to provide at least one N-H function per epoxy group of the epoxy resin, at a temperature in the range 40 °C to 100 °C, and d) neutralising the resulting suspension of epoxy-amine adduct coated particles, and e) optionally adjusting the concentration of the resulting dispersion within the range 35 to 75 %w solids by addition of water. By "solvent-free" is meant "free from organic solvents". The same EPA also discloses a process for preparing an aqueous paint composition which comprises adding to an aqueous binder composition prepared by the aforesaid process a cross-linking agent which for practical purposes is mixed with pigment powder to form a paste, and adjusting the concentration of the composition by addition of water to ensure a solids content in the range 10 to 65 %w. However, it is not easy to obtain a homogeneous dispersion in step (b) and the suspension obtained in step (c) usually has a high viscosity. Furthermore, the aqueous paint composition has a relatively low solids content at application viscosity. The present invention is concerned with the problem of doing away with these three difficulties, it therefore seeks to conceive a simplified method for preparing solvent-free, aqueous epoxy-resin based paint compositions. Accordingly, the invention provides a process for preparing an aqueous paint composition which comprises:- (a) mixing a pigment powder having a particle size less than 20 micrometres, a cross-linking agent and an epoxy resin to form a liquid, solvent-free paste, (b) reacting the resultant paste with a secondary amine, and optionally also a primary amine, the amount of amine being sufficient to provide at least one N-H function per epoxy group of the epoxy resin, at a temperature in the range of from 20 °C to 140 °C, and (c) neutralising the resulting suspension of particles coated with epoxy-amine adduct and cross-linking agent, and adjusting the concentration of the resulting dispersion to ensure a solids content in the range of from 10 to 80 %w solids by addition of water. It has been found that it is very easy to obtain a homogeneous paste in step (a) and that the viscosity of the suspension obtained in step (b) is relatively low. Furthermore, the aqueous paint composition obtained in step (c) has a relatively high solids content at application viscosity. It is possible to prepare separately a pigment/cross-linking agent paste and an epoxy resin pigment paste. This, however, is not necessary. Therefore, according to a preferred embodiment of the present invention step (a) is carried out by dispersing the pigment powder in a solvent-free liquid mixture of the cross-linking agent and the epoxy resin. The term "pigment powder" includes all water-insoluble solid paint additives such as conventional pigments, fillers and extenders. Examples of such materials include titanium oxide, barytes, clay, microtalc and black iron oxide. The particle size of the pigment powder is less than 20 micrometres, preferably less than 10 micrometres, and advantageously less than 5 micrometres. The epoxy resin is preferably a polyglycidyl ether of a polyhydric phenol and may be liquid or solid at ambient temperature. Advantageously the epoxy resin is a polyglycidyl ether of a dihydric phenol. Conveniently the epoxy resin is a polyglycidyl ether of 2,2-bis(4-hydroxyphenyl)propane. Provided that the eventual epoxy-amine adduct includes on average at least two hydroxy moieties per molecule, the epoxy resin may, if desired, be a monoglycidyl compound. Another example of an epoxy resin which may be used is an epoxy novolac resin. Further examples of epoxy resins are polyglycidyl ethers having on average n epoxy groups per molecule, where 1 < n < 2, which ethers are the reaction product of a multifunctional polyglycidyl ether having on average × epoxy groups per molecule, where x > 2, with (x - n) mol of a monofunctional phenol per mol of the multifunctional polyglycidyl ether, as described in European patent application No. 0 127 915. Epoxy compounds can react with amines having at least one reactive N-H function according to the general addition reaction: The secondary amine employed in step (b) may contain one or more substituents which do not react with epoxy groups under the reaction conditions, e.g. hydroxyl, ketimine and ester groups. Suitable secondary amines include dialkanolamines, N-alkylalkanolamines, dialkylamines and adducts of alkanolamines with aliphatic monoepoxides. Preferably the secondary amine comprises at least one compound selected from the group consisting of di(C 2-6 -alkanol)amines, N-C 1-6 -alkyl-C 2-6 -alkanolamines, di(C 1-6 -alkyl)amines and adducts of C 2-6 -alkanolamines with C 9-25 -aliphatic monoepoxides, in each of which amines a hydrogen atom bound to a carbon atom may be substituted by a di(C 1-6 -alkyl)amino group. Examples of such secondary amines are diethanolamine, diisopropanolamine, methyl-2-hydroxyethylamine, diethylamine and the adduct of monoethanolamine with a C 9-14 , preferably C 12-14 , aliphatic monoglycidyl ether. The secondary amine may, if desired, have a ketimine function. Mixtures of secondary amines may be employed. The secondary amine may advantageously be employed in admixture with a primary amine. It is a feature of the present invention that the primary and secondary amine may be added simultaneously in step (b). The primary amine is preferably an alkylamine or particularly an alkanolamine in each of which amines a hydrogen atom bound to a carbon atom may be substituted by a di(C 1-6 -alkyl)amino group. Most preferred are C 2-6 -alkanolamines, such as monoethanolamine or monoisopropanolamine. Among the alkylamines C 1-6 -alkylamines are preferred. The reaction temperature in step (b) is preferably at least 30 °C, and is preferably not greater than 100 °C. In step (c), the suspension is preferably neutralised to a degree of neutralisation in the range 0.2 to 1.5, more preferably 0.3 to 1.0, by addition of a monobasic carboxylic acid, advantageously a C 2-6 -carboxylic acid such as acetic acid. The epoxy resin/amine adducts produced in step (b) above have a plurality of alcoholic hydroxyl functions per molecule, at least part of these formed by the addition reaction of epoxy with an N-H function. Additional hydroxyl functions will be present when the amine and/or the epoxy resin starting materials already contain hydroxyl groups. Suitable cross-linking agents are compounds or compositions having a plurality of groups which are reactive with alcoholic functions during cure. Well-known cross-linking agents of this type are phenolic resins, in particular resoles; aminoplast resins such as those derived from urea, melamine or benzoguanamine; blocked polyisocyanates; and preferably non-acidic polyesters of polycarboxylic acids which esters have more than one, and preferably at least two, beta-hydroxyl ester groups per molecule. When such polyesters are used, a transesterification-promoting metal compound is also incorporated in the paint composition. Phenolic resins of the resole type contain methylol groups which may be etherified and which can react with hydroxyl groups of the epoxy resin/amine adduct; in addition cross-linking reactions can occur between the resole molecules themselves. Aminoplast resins as used generally in thermosetting resin systems may be derived from urea, melamine, or benzoguanamine, and an aldehyde, usually formaldehyde, and generally etherified with a lower alcohol such as methanol, ethanol or butanol. Polyisocyanate derivatives to be used in aqueous thermosetting resin systems have to be blocked with a reactant that effectively blocks the isocyanate groups at temperatures used in the preparation of the system, and setting them free at curing temperatures, generally above 120 °C. Examples of suitable blocking agents are monohydric alcohols, monohydric phenols and certain nitrogen compounds, such as caprolactam. Non-acidic polyesters of polycarboxylic acids have an acid value not greater than 0.18 meq/g (acid number not more than 10), preferably not more than 0.09 meq/g. Beta-hydroxyl ester in this context means that the alcohol-derived moiety of the ester has a beta-hydroxyl group; in other words the ester function is a derivative of a 1,2-glycol of which only one of the hydroxyl functions has been esterified. The glycol part may have substituents, such as alkyl, ether or stable ester groups. The beta-hydroxyl group is needed for sufficient cross-linking at acceptable temperatures within acceptable times, for example at temperatures up to 200 °C and curing times of up to 30 minutes. By the process of curing or stoving the coating, beta-hydroxyl ester groups of the polyester transesterify to the effect that ester bonds are formed between carboxyl groups of the polyester and hydroxyl groups of the epoxy-amine adduct with release of a glycol-type compound; the latter may then evaporate. The result is a cross-linked coating which is solvent-resistant and infusible. Suitable non-acidic polyesters having beta-hydroxylester groups can be prepared from a polycarboxylic acid or anhydride thereof, and one or more glycols, and/or mono-epoxides, for example from azelaic acid, terephthalic acid, isophthalic acid, phthalic anhydride, trimellitic anhydride, ethylene glycol, ethylene oxide, propylene oxide, glycidyl esters of C₁₀-monocarboxylic acids. Examples of polyesters are bis(2-hydroxyethyl)-terephthalate, lower (2-hydroxyethyl)-terminated polyalkylene glycol terephthalates, and the di-beta-hydroxy ester reaction product of azelaic acid and the glycidyl ester of a saturated C₁₀-monocarboxylic acid or of azelaic acid and n-butyl glycidyl ether. The weight ratio epoxy-amine adduct to cross-linking agent is not critical and may vary within wide limits, suitably in the range of from 0.25 to 4. Suitable transesterification-promoting metal compounds include, for example, salts (e.g. octoates or naphthenates) of lead, zinc, calcium, barium and iron(III). A suitable example of a metal complex is titanium acetylacetonate. Other suitable salts, although in general less active than those mentioned above, are salts of tin(II), manganese, cobalt and dibutyltin, for example dibutyltin dilaurate. Further metal salts that can be mentioned in general are octoates and naphthenates of the alkali and alkaline earth metals, of the lanthanides, and of zirconium, cadmium, chromium, and acetylacetonate complexes of lead, zinc, cadmium, cerium, thorium and copper. Zinc octoate and zinc acetate have been found to give very acceptable results. Mixtures of such salts and/or complexes may be used. Metal content of the transesterification-promoting metal compounds should preferably be in the range 0.3 to 2 %w, advantageously 0.5 to 1.8 %w, based on the combined weight of all organic material in the paint composition. The invention also includes paint compositions prepared by the processes of the invention. In the paint compositions the pigment/(crosslinking agent plus amine adduct) weight ratio preferably lies in the range 0.4 to 1.5. The paint composition may contain, apart form the pigment powder incorporated in step (a) additional components usual in paints, such as pigments, fillers, thixotropic agents, stabilizers, plasticizers, flow control agents and desinfectants. The water to be used in the processes of the invention is preferably purified, by distillation or demineralisation, and may contain suitable additives such as desinfecting agents. The invention also provides a process for coating a surface which comprises applying to the surface a paint composition of the invention containing a transesterification-promoting metal compound, drying the composition and curing by action of heat. The paint compositions may be applied to a substrate by means known in the art, such as by brush or roller, or by spraying or dipping onto a variety of materials, preferably on metals such as bare steel, phosphated steel, zinc, tin plate, as the case may be as the sole coating layer, or as a primer of primer-surfacer (for example on a primer layer applied by electrodeposition). The paint compositions are particularly suitable for spray application as primer-surfacer. For such applications, the concentration of the composition in step (c) should be adjusted to a solids content in the range 25 to 75 %w. Paint compositions whose solids content is adjusted to 10 to 60 %w may also be applied to a substrate by cathodic electrodeposition, as a primer. This application is preferred. In a preferred embodiment of this invention step c is carried out in two successive operations (c₁) and (c₂), (c₁) comprising neutralizing in the presence of water and (c₂) comprising the further adjustment by the addition of water to ensure for the desired final solids content. The water may be evaporated and the coating be cured by usual means, such as by stoving or by heat radiation. Stoving time and temperature will be dependent on the particular paint composition, and will be in a range usual for thermosetting surface coatings, in general from 130 °C to 200 °C with curing times varying from 10 to 60 min. The invention will be further understood from the following illustrative examples. In the Examples, parts and percentages are by weight, unless otherwise indicated. Analytical data are based on non-volatile matter. Filler components (titanium dioxide, barytes, clay, microtalc, black iron oxide) all had particle size less than 20 micrometres. EPIKOTE 828 is a trade name for a commercial liquid polyglycidyl ether of 2,2-bis(4-hydroxyphenyl)propane, which, in the Examples, has an epoxy group content of 5320 mmol/kg. CARDURA E 10 is a trade name for the glycidyl ester of saturated C₁₀-monocarboxylic acids, wherein the alpha-carbon atom with respect to the carboxyl group is attached to three alkyl groups at least one of which is methyl and, in the Examples, has an epoxy group content of 3975 mmol/kg. Water is demineralised water. In each of the examples a glass reactor was used which was equipped with an anchor stirrer, thermocouple, reflux condenser and inlet tubes. Example 1 Azelaic acid (1128 g, 6 mol) and CARDURA E10 (3048 g, 12 epoxy equivalents) were heated together in a glass reactor for one hour at 90 °C. To the resulting clear mass was added benzyldimethylamine (10.4 g) resulting in a temperature rise to 140 °C. After 2 hours at this temperature the reaction mixture was cooled to ambient temperature to yield a liquid di-β+-hydroxy ester having an acid content of 0.01 meq/g, an epoxy group content of 0.07 meq/g and a calculated average molecular weight of 692. The viscosity of the ester at 23 °C was 2.8 Pa.s. A glass reactor was charged with EPIKOTE 828 (188 g, 1 epoxy equivalent) and di-β+-hydroxy ester cross-linking agent (346 g) prepared as described in the previous paragraph and the reactor contents were stirred at ambient temperature until the mixture was homogeneous. The homogeneous mixture was heated to 35 °C and a mixture of titanium dioxide (186 g), barytes (361 g), microtalc extender (29 g) and black iron oxide (5 g) was placed portionwise with high speed stirring into the reactor. Continued high speed stirring for 2.5 hours resulted in a homogeneous paste. Then, monoethanolamine (15.3 g, 0.25 mol) and diethanolamine (52.5 g, 0.50 mol) were added to the paste under stirring which resulted in a temperature rise to 70 °C. This temperature was maintained for 3.5 hours which resulted in an epoxy group content of the paste of 0.01 meq/g. At the end of this period glacial acetic acid (45 g, 0.75 mol) was added portionwise followed by dropwise addition of water (507 g) under high speed stirring. The resulting paint composition was at ambient temperature an easily pourable grey viscous liquid having a degree of neutralisation of 1.0, a pigment to (cross-linking agent plus amine adduct) weight ratio of 1.0 and a solids content of 68% by weight, the solids being the total of pigments, cross-linking agent and amine adduct. The paint composition containing a transesterification-promoting metal compound was obtained by adding 72.6 g of a 25% by weight solution of zinc acetate dihydrate in water with stirring. Example 2 The reactor used in Example 1 was charged with EPIKOTE 828 (105 g, 0.56 epoxy equivalents) and di-β+-hydroxy ester cross-linking agent (254 g) prepared as described in Example 1 and the reactor contents were stirred at ambient temperature for 0.25 hours which resulted in a homogeneous mixture. The mixture was heated to 35 °C and a mixture of titanium dioxide (270.5 g) and barytes (270.5 g) was added portionwise with high speed stirring into the reactor. Continued high speed stirring for 2 hours resulted in a homogeneous paste. The paste was heated to 40 °C and then monoethanolamine (8.6 g, 0.14 mol) and diethanolamine (29.5 g, 0.28 mol) were added under stirring which resulted in a temperature rise to 80 °C. This temperature was maintained for 4 hours, which resulted in an epoxy group content of the paste of 0.02 meq/g. At the end of this period glacial acetic acid (25.2 g, 0.42 mol) was added portionwise. After further stirring for 10 min water (377 g) was added dropwise under high speed stirring. The resulting paint composition was at ambient temperature a pourable white viscous liquid having a degree of neutralisation of 1.0, a pigment to (cross-linking agent plus amine adduct) weight ratio of 1.4 and a solids content of 70 % by weight, the solids being defined as in Example 1. The paint composition containing a transesterification-promoting metal compound was obtained by adding 47.9 g of a 25% by weight solution of zinc acetate dihydrate in water with stirring. Example 3 Azelaic acid (188 g, 1 mol), n-butyl glycidyl ether (273 g, 2.1 mol) and Cordova Accelerator AMC-2 catalyst (2.3 g, AMC-2 is a trade name for an esterification catalyst sold by Cordova Chemical, U.S.A.) were placed in a glass reactor. The reactor contents were heated to 90 °C at which temperature an exothermic reaction started allowing the temperature to rise to 120 °C. Then, the temperature was allowed to drop to 110 °C and was kept at this temperature for 5.5 hours. The cross-linking agent thus prepared had an epoxy group content of 0.04 meq/g, a carboxylic acid group content of 0.02 meq/g, a viscosity at 23 °C of 0.2 Pa.s and a calculated average molecular weight of 448. A glass reactor was charged with EPIKOTE 828 (65.8 g, 0.35 epoxy equivalents) and cross-linking agent (97.8 g) prepared as described in the previous paragraph. The reactor contents were stirred at ambient temperature for 0.25 hours until the mixture was homogeneous. A mixture of titanium dioxide (121 g) and barytes (121 g) was placed portionwise with high speed stirring into the reactor. Continued high speed stirring for 2.5 hours resulted in a homogeneous paste. Then, the mixture was heated to 40 °C, at which temperature monoethanolamine (5.3 g, 0.09 mol) and diethanolamine (18.4 g, 0.18 mol) were added under stirring which resulted in a temperature rise to 90 °C. This temperature was maintained for 4.5 hours which resulted in an epoxy group content of the paste of 0.01 meq/g. At the end of this period glacial acetic acid (15.8 g) was added portionwise. After further stirring for 10 min water (168.1 g) was added dropwise under high speed stirring. The resulting paint composition was at ambient temperature a pourable, white viscous liquid having a degree of neutralisation of 1.0, a pigment to (cross-linking agent plus amine adduct) weight ratio of 1.3, a solids content of 70 % by weight, the solids being defined as in Example 1. The paint composition containing a transesterification-promoting metal compound was obtained by adding 22.6 g of a 25% by weight solution of zinc acetate dihydrate in water with stirring. Example 4 The reactor used in Example 1 was charged with EPIKOTE 828 (188 g, 1 epoxy equivalent) and a mixture of titanium dioxide (76.2 g), barytes (148.2 g) and microtalc extender (12.0 g) was added portionwise with high speed stirring. Stirring was continued until a homogeneous paste was obtained. Another reactor as used in Example 1 was charged with di-β+-hydroxy ester cross-linking agent (346 g) prepared as described in Example 1 and a mixture of titanium dioxide (110 g), barytes (213 g), microtalc extender (17 g) and black iron oxide (5 g) was added portionwise with high speed stirring. Stirring was maintained until a homogeneous paste was obtained. The two pigment pastes prepared as described hereinbefore were placed in a glass reactor as used in Example 1. The contents of this reactor were heated to 40 °C and stirred until a homogeneous paste was obtained. Then, monoethanolamine (15.3 g, 0.25 mol), methyl-2-hydroxyethylamine (18.8 g, 0.25 mol) and diethylamine (18.3 g, 0.25 mol) were added to the paste under stirring and the temperature was allowed to rise to 60 °C. This temperature was maintained for 3 hours, which resulted in an epoxy group content of the paste of 0.01 meq/g. At the end of this period glacial acetic acid (45 g) was added portionwise followed by dropwise addition of water (452 g) under high speed stirring. The resulting paint composition was at ambient temperature an easily pourable grey viscous liquid having a degree of neutralisation of 1.0, a pigment to (cross-linking agent plus amine adduct) weight ratio of 1.0 and a solids content of 70% by weight, the solids being defined as in Example 1. The paint composition containing a transesterification-promoting metal compound was obtained by adding 70.7 g of a 25% by weight solution of zinc acetate dihydrate in water with stirring. The four paint compositions obtained as described in the four Examples were further diluted with water under stirring until the solids contents stated in Table 1 hereinafter were obtained. Properties of these diluted ready to use paints of the four Examples are presented in said Table 1. In Table 1 hereinbefore, "pigment" denotes all filler components, e.g. titanium dioxide, barytes, microtalc and black iron oxide, and "binder" denotes combined weight of all organic material. In all Examples zinc was present in an amount of 0.9 % by weight based on combined weight of all non-volatile organic material. Viscosity was measured using a Brookfield (trade mark) viscometer. Storage stability was assessed after eight weeks storage. The term "excellent" denotes no more than easily-redispersed, slight settlement of solids, no change in overall viscosity. The diluted ready to use aqueous paint compositions of Examples 1 to 4 were tested by applying by bar coater onto phosphated steel panels which were dried for 10 minutes at 50 °C and cured by stoving for 30 minutes at the temperature indicated in Table 2. After stoving the films of each of the four examples were smooth and matt. Film thickness, appearance, mechanical properties, and solvent and water resistance were assessed. Results of the tests are given in Table 2 hereinbefore, in which "MEK rubs" is the number of double rubs given to the cured coating with a cloth wetted with methyl ethyl ketone until the coating was wiped off. "MEK rubs" greater than 50 is indicative of good cure and good solvent resistance. Impact strength is reversed impact strength determined according to the British Standard Falling ball test, recorded according to the following scale: E (excellent): coating not damaged; G (good) : coating slightly damaged; M (moderate) : coating clearly damaged; P (poor) : coating destroyed, when applying a reverse impact strength of 90 cm.kg. No damage indicates very good flexiblity. Water resistance is assessed visually on the coating submerged in boiling water for three days and according to the following scale: excellent (no blisters), good (some blisters), moderate (many blisters), poor (unacceptable blistering). Salt spray resistance was determined according to ASTM-B-117-64 and is recorded as mm loss of adhesion from scratch after ten days. The appearance was assessed visually according to the scale given in the preceding paragraph. Examples 5-8 The experiment of Example 3 was repeated up to the addition of glacial acetic acid. Then, the resulting suspension of particles coated with epoxy-amine adduct and cross-linking agent was divided into four equal portions, referred to hereinafter as portions 1, 2, 3 and 4. To portion 1 (Example 5) glacial acetic acid (4.0 g) was added portionwise. After further stirring for 10 min water (42.0 g) was added dropwise under high speed stirring. The ready to use paint was obtained by adding with stirring 5.65 g of a 25% by weight solution of zinc acetate dihydrate in water, followed by addition of water (18.4 ml). To portion 2 (Example 6) glacial acetic acid (3.0 g) was added portionwise. After further stirring for 10 min water (43.0 g) was added dropwise under high speed stirring. The ready to use paint was obtained by adding with stirring 5.65 g of 25% by weight solution of zinc acetate dihydrate in water, followed by addition of water (19.3 ml). To portion 3 (Example 7) glacial acetic acid (2.0 g) was added portionwise. After further stirring for 10 min water (44.0 g) was added dropwise under high speed stirring. The ready to use paint was obtained by adding with stirring 5.65 g of a 25% by weight solution of zinc acetate dihydrate in water, followed by addition of water (19.9 ml). To portion 4 (Example 8) glacial acetic acid (1.6 g) was added portionwise. After further stirring for 10 min water (44.4 g) was added dropwise under high speed stirring. The ready to use paint was obtained by adding with stirring 5.65 g of a 25% by weight solution of zinc acetate dihydrate in water, followed by addition of water (23.6 ml). The ready to use paints were at ambient temperature easily pourable, white viscous liquids. They had a pigment to (cross-linking agent plus amine adduct) weight ratio of 1.3. A few properties of these ready to use paints are presented in Table 3 hereinafter. It follows from table 3 that the solids content was relatively high at the viscosity shown. The ready to use paints were applied by bar coater onto bare steel panels. The wet films were dried for 10 min at 50 °C and cured by stoving for 30 min at 170 °C. Each of the four films thus obtained had an excellent impact strength and a MEK rubs value of greater than 50.

Claims: A process for preparing an aqueous paint composition which comprises:- (a) mixing a pigment powder having a particle size less than 20 micrometres, a cross-linking agent and an epoxy resin to form a liquid, solvent-free paste, (b) reacting the resultant paste with a secondary amine, and optionally also a primary amine, the amount of amine being sufficient to provide at least one N-H function per epoxy group of the epoxy resin, at a temperature in the range of from 20 °C to 140 °C, and (c) neutralising the resulting suspension of particles coated with epoxy-amine adduct and cross-linking agent, and adjusting the concentration of the resulting dispersion to ensure a solids content in the range of from 10 to 80 %w solids by addition of water. A process as claimed in claim 1 in which step (a) is carried out by dispersing the pigment powder in a solvent-free liquid mixture of the cross-linking agent and the epoxy resin. A process as claimed in claim 1 or 2 in which the epoxy resin is a polyglycidyl ether of a polyhydric phenol. A process as claimed in claim 3 in which the epoxy resin is a polyglycidyl ether of a dihydric phenol. A process according to any one of the preceding claims in which the secondary amine comprises at least one compound selected from the group consisting of di(C 2-6 -alkanol)amines, N-C 1-6 -alkyl-C 2-6 -alkanolamines, di(C 1-6 -alkyl)amines and adducts of C 2-6 -alkanolamines with C 9-25 -aliphatic monoepoxides, in each of which amines a hydrogen atom bound to a carbon atom may be substituted by a di(C 1-6 -alkyl)amino group. A process according to any one of the preceding claims in which the primary amine is a C 2-6 -alkanolamine or a C 1-6 -alkylamine, in each of which amines a hydrogen atom bound to a carbon atom may be substituted by a di(C 1-6 -alkyl)amino group. A process according to any one of the preceding claims in which in step (c) the suspension is neutralised to a degree of neutralisation in the range 0.2 to 1.5 by addition of a monobasic C 2-6 -carboxylic acid. A process according to any one of the preceding claims in which the crosslinking agent comprises a non-acidic polyester of a polycarboxylic acid having more than one beta-hydroxyl group per molecule, and wherein a transesterification-promoting metal compound is incorporated in the composition. A process as claimed in any one of the preceding claims in which step (c) is carried out in two successive operations (c₁) and (c₂), (c₁) comprising neutralizing in the presence of water and (c₂) comprising the further adjustment by the addition of water to ensure the desired solids content. A process according to claim 8 in which the metal compound is water-soluble or is a water-insoluble compound in a water-dispersible formulation and is incorporated in the composition during or after any one of steps (c₁) and (c₂). A process for coating a surface which comprises applying to the surface a composition prepared with a process as claimed in any of claims 8 to 10, drying the composition and curing by action of heat.

Inventors: DIJKSTRA, TETTE JAN, SCHOLTEN, HENRICUS PAULUS HUBERTUS, VAN IPEREN, ROELAND
Applicants: SHELL INTERNATIONALE RESEARCH MAATSCHAPPIJ B.V.
Application year: 1987
Main classification: C09D17
IPC codes: C09D5, C09D7, C09D17, C08G59, C09D163