PROCESS FOR MANUFACTURING A SAFETY GLASS FOR MOTOR VEHICLES AND BUILDINGS, AND PRODUCT SO OBTAINED

Abstract: The invention relates to a manufactured article formed of two transparent layers, preferably one made of glass and the other made of plastic, adapted to be used as glazing for motor vehicle windows and buildings, consisting of a glass substrate onto which is applied a single-layer plastic comprising a composition of polycaprolactones, a vinyl monomer N-vinyl-2-pyrrolidone,mono-, di-, tri-, tetra-acrylic monomers, a photoinitiator, and flow control agents, reaction catalysts, solvents, plasticizers and adhesion promoters, and aliphatic polyisocyanate, which composition is distributed as a liquid with uniform thickness over the surface, which is spun and exposed to ultraviolet radiations to form the coating.

Description: The present invention relates to a manufactured glass article onto which is applied a single-layer plastic coating for the purpose of improving its behaviour on impact damage, and to a method for applying the coating to a glass substrate. The product according to the invention can find advantageous application as a windshield for vehicles, and therefore the specification that follows will be referred to windshields but without for this reason implying any limitation of the uses of the invention, which can include manufacture of other types of article such as side windows for vehicles or glazing for buildings. The automobile industry employs two known types of windshield, normally described as laminated glass products or tempered glass products. In laminated glass windshield a sheet of highly thermoplastic flexible plastic, generally of plasticized polyvinyl butyral and less frequently of polyurethane, is laminated between two sheets of glass bonded to each other under heat and pressure. In the case of tempered glass windshield a single glass panel undergoes a rigorously controlled heat treatment cycle, optionally preceded by a chemical surface treatment. Such types of windshield have been proposed to lessen the risk of injury to driver and/or passengers if the windshield is broken accidentally. In laminated glass windshield, the fragments of broken glass are held together as a result of the flexibility and yieldability of the intermediate layer, its adherence to the glass due to the formation of physical bridges, high tensile strength and good ultimate elongation. Resistance to penetration of the laminated glass windshield by stones and like objects striking is good; but when this type of windshield is broken a certain number of small, needle-shaped glass fragments are always formed, can come off the windshield at a relatively high speed and can seriously injure the eyes and unprotected parts of the skin of the occupants of the vehicle, such types of injury being generally known as lacerated wounds. In tempered glass windshield behaviour on impact damage is entirely different in that this type of windshield fractures over its whole surface into small, regularly sized pieces wholly devoid of sharp cutting edges and there are no needle-shaped particles that can come off. Since the entire windshield fractures, its resistance to penetration by flying objects is however low, and the occupants of the vehicle therefore run the risk of severe injury by such objects. The laminated glass windshield is generally held to be superior to the tempered glass windshield, and it will thus be appreciated that it is desirable to eliminate its characteristic of forming flying particles of the lacerating type, so as to improve the safety of motor vehicles. A standard type of laminated glass windshield consists of two bonded glass sheets, of about 2.5-mm thickness each, and a plasticized polymeric plastic interlayer which is about 0.75-mm thick. The different processes that can be used to assemble the structure are well-known to persons with ordinary skill in the art.Various methods have been employed to attempt to reduce the severity of the lacerated wounds caused: thus U.S. Patent Nos. 3,881,043, 3,931,113 and 4,041,208 granted to P.P.G. describe various polyurethane compounds for forming intermediate layers having improved adhesiveness to the glass than polyvinyl butyral; for example it is suggested to laminate, between two glass sheets, a preformed polyurethane sheet obtained through the reaction of: a) a hydroxylterminated polyester of caprolactone, polybutylene adipate, polybutylene azelate or mixtures; b) a diol with molecular weight less than 250, preferably 1, 4 butane diol, and c) a cycloaliphatic di-isocyanate. Tests have, however, shown that when a laminated glass windshield is broken most of the lacerating fragments are produced by the glass surface not in contact with the intermediate layer, so none of the processes designed to improve the intermediate layer solves the problem of lacerating fragments. An alternative solution is described in German patent application No. 2,629,799 of July 2, 1986 of St. Gobain, which proposes the preparation of an anti-lacerating windshield wherein a polyvinyl butyral film is bonded between two glass sheets and this laminate has added to it, on an outer glass sheet, a preformed polyurethane layer obtained by the reaction of: a) a polyesther with free hydroxyl groups; b) an aliphatic polyisocyanate. These outer films have shown themselves to be truly optimal in eliminating the formation of lacerating glass fragments, especially in respect of flat glass. However, given that most motor vehicles are fitted with curved windshields calling for different radii of curvature -sometimes very small- the practical problems involved in laminating such sheets to glass surfaces are very great and further difficulties arise from the need to obtain windshields with no optical distortion effects and without delamination tendencies on ageing. U.S. Patent No. 4,197,333 discloses a method for caoating the outer surface of a lamp (for example a photoflash lamp) with a transparent protective film, wherein a coating consisting of a high viscosity (3000 to 5000 centipoise) photopolymerizable composition is applied by a special dispensing method whereby a lamp is rotated under a special dispenser and the resultant coating is cured by ultraviolet light. No methods are known in the art whereby materials of such viscosity can be applied to a vehicle windshield as heretofore described. Moreover, the compositions described do not produce films having the properties called for by windshield coatings. Australian Patent No. 66,655/74 describes a process for preventing glass bottles from shattering, wherein a powder with particle size from 1 to 100 microns of a solid component having a melting point over 20° C is dispersed in a normoliquid polyurethane prepolymer and is coated onto the outside of the bottle, the coating being subsequently cured by heat. Tests have shown unequivocally that such films are wholly without the clarity, adhesion to glass and also scratch resistance required for a windshield coating. Italian Patent Application No. 19779 A/83 of the present Applicant proposes a process for producing a windshield coating to reduce the formation of lacerating fragments, which process provides for the polymerization "in situ" of a crosslinked acrylic vinyl polymer, a polycaprolactone aliphatic polyisocyanate polyurethane, and a prepolymerized linear polyester-acrylated polyurethane in a closely controlled amount. The present-day trend in the trade, especially as regards motor vehicles but also as regards buildings, attempts to reduce the weight of the glass or glazing employed to an appreciable extent, without thereby adversely affecting the safety requirements as per the international requirements lad down by ANSI, ECE, DIN, UNI, etc. Standards. An example of the said trend is for instance provided by duplex glazings, given this name in that they are formed of only two layers of different materials which are intimately joined together. These duplex products consist of a layer of glass and a layer of plastic material, it being necessary for the latter to possess specific mechanical and optical properties in addition to those already mentioned and known in the art, defined as non-lacerating, self-sealing, scratch-and ageing-resistance. To manufacture a product defined as of the duplex type industrially, the problem has to be solved by identifying a particular formulation of organic compounds such as will give rise to a single-layer plastic coating that not only provides the end-product with the physical, mechanical and optical properties required but which can also be distributed on substrates with relatively large and concave surface areas, so as to be of constant thickness at all the points to be coated. In addition, such coating must have good passive resistance to rupture, and such resistance can be obtained with thicknesses generally not below 300 microns. The object of the present invention is, therefore, to provide a single-layer plastic coating, obtained by "in situ" polymerization directly on the glass substrate, such as possesses the properties of clarity, non-laceration, self-sealing, scratch-and ageing-resistance and such as is at the same time adapted to impart to the final duplex product the characteristics of safety required by international Standards. Another object of the present invention is to provide a process for low-cost industrial manufacture of this novel type of duplex article such as having all the characteristics required by safety regulations, it remaining understood that both the plastic layer forming object of the invention and the process for applying it can also find advantageous use for coating a normal stratified product consisting of two glass sheets which conventionally are laminated using a sheet of polyvinyl butyral. In accordance with the invention the process for manufacturing a safety glass, in particular for motor vehicles or buildings, consisting of at least one glass sheet to which a plastic coating is bonded, is characterized by: formation if a liquid coating composition comprising: a) a solution of polycaprolactones with molecular weigth between 200 and 1200 and polyethers with molecular weight between 250 and 1000, dissolved in between 10% and 40% of b) a mixture of a vinyl monomer N-vinyl-2-pyrrolidone, with at least 10 and not more than 105% of mono-, di-, tri-, and tetra-acrylate monomers, such as: 2-ethylhexylacrylate; butoxyethoxyethyl acrylate; 1,4-butanediol diacrylate, ethyleneglycol diacrylate; neopentylglycol diacrylate; hexanediol diacrylate, diacrylic derivative of bisphenol A; diethyleneglycol diacrylate; tripropyleneglycol diacrylate; tetraethyleneglycol diacrylate; trimethylolpropane triacrylate; pentaerythritol triacrylate; pentaerythritol tetraacrylate; c) a photoinitiator such as 2-hydroxy-2-metyl-1-phenylpropan-1-one or a substituted derivative thereof or a mixture thereof added in an amount between 0.5 and 3% of the total composition; d) one or more silicone flow control agents or fluorinated flow control agents in an amount of 0.1 to 0.4%; e) reaction catalysts in an amount of 0.02 to 0.4%. f) an aliphatic polyisocyanate in an amount sufficient to react with an amount less than the stoichiometric amount of the hydroxyl groups present in the initial part of the composition (i.e. with an -NCO index ranging from 1.01:1 to 1.1:1) added immediately before use); application to the said glass sheet of the said coating composition with a viscosity between 40 and 200 centipoise immediately after preparation and before any significant change in viscosity caused by the initiation of the reaction between the hydroxyl groups and the isocyanate groups in the composition; after application of the composition, spinning of the glass sheet at around 10 to 50 rpm so as to ensure a constant thickness spread of the coating composition film over the entire surface of the said sheet and to ensure that the thickness is kept constant at between 80 and 150 microns; exposure of the film to a high-intensity ultraviolet light source for a time sufficient to complete the polymerization of the acrylic and vinyl monomers; heat-treatment of the coated glass sheet to complete the formation of polyurethane from the hydroxyl and isocyanate groups of the polyisocyanates. The coating composition in accordance with the invention further advantageously comprises: g) a middle or high-boiling solvent such as toluene, Xylene, acetates, etc., in an amount from 5 to 15%. h) plasticizers such as DOP, DBP, TBP, BBP, DIBP or others, in an amount from 5 to 15%; i) adhesion promoters such as Z r -Methacrylates or titanates or silanes with chemical functions suitable chosen to promote the anchorage between glass support and polymer matrix. Such coating composition is preferably applied by spraying or curtain coating on the concave surface of the glass substrate, previously curved or 'bowed' and/or tempered so as to take on its required final shape and structure. At the time of mixing, the viscosity of the composition is from 40 to 200 centipoise and spraying or curtain coating should be carried out before there is any significant change in viscosity due to the initiation of the reaction between the hydroxyl and isocyanate groups in the composition. Immediately after spraying or curtain coating the glass substrate is spun at around 10-50 rpm so as to ensure a constant spread-thickness of the coating composition film over the entire surface of the substrate and to ensure that thickness uniformity is maintained up to the time of the subsequent ultraviolet radiation treatment. When the coating has been evenly distributed over the surface of the substrate with a wet film thickness of 80 to 150 microns, curing of it has then already started as a result of the reaction of the isocyanate with the hydroxyl groups. Spinning lasts around 5 to 10 minutes, the exact period depending on the viscosity increase of the mixture distributed over the substrate. The film is then exposed to a high-intensity UV light source, preferably an emission of relatively broad spectrum as is produced by a medium mercury pressure lamp operating at an intensity of 40 watts per centimetre, for a period sufficient to complete the polymerization of the acrylic and vinyl monomers, which process can take from 2 seconds to 1 minute. This state can be identified by the fact that the film at once undergoes a noticeable increase in viscosity, and is thus firm and stable. When under exposure to UV radiation, the substrate continues to rotate at a speed of around 10 to 50 rpm. When UV radiation and spinning have been completed, the substrate is given (if necessary) further spraying, spinning and UV radiation treatments until such time as the coating reaches the desired thickness, in any case generally not less than 300 microns. Immediately thereafter the infrared treatment is given, which treatment can be replaced by or supplemented with a different type of heat treatment, in order to complete the formation of polyurethane from the hydroxyl groups and isocyanate groups of the polyisocyanates. The intensity and duration of the heat treatment must be such as to lead to formation of a final single-layer film having clearly defined and wished-for characteristics. It is essential for the surface of the substrate to be clean before applying the coating, and this can certainly involve washing with water-plus-detergent followed by low-temperature drying with a dust-free stream of hot air. Adhesion between glass sheet and substrate can on occasion be improved by pretreating the glass surface with an alcoholic or hydroalcoholic solution of a selected compound of organic silane, for example methylacryl-oxypropyl-trimethoxysilane as a 2% solution in isopropanol, then drying gently in warm air, or with a silane, having a suitable function and capable of reacting both with polymer and glass, dissolved directly in the reaction mass. Such treatments are however not always necessary. Test methods for safety glass windshields are set out in the American Safety Council "Standard Code for Safety Glazing Materials for Glazing Motor Vehicles Operating on Land Highways", July, 1966, Ref. Z 26.1, and these test methods are generally used in industry. The coating in accordance with the invention guarantees both a clarity on a par with that of glass, and the optical and light stability required by the strict ANSI Standards in force in the U.S.A. and the ECE standards in force in E.E.C. states. The degree of optical distortion must be measured, for example, according to ANSI Standard Z 26.1, paragraph 5.15; optical properties must be measured, for example, according to ECE Standard R 43; light stability properties must be measured, for example, according to ANSI Standard Z 26.1 - 1977, paragraph 5.1. The characteristics of the invention will become more apparent from an examination of the following examples of actuation thereof. EXAMPLE 1 A liquid coating composition was prepared as follows: 8.5 x 10⁻² equivalents of a polyether PTHF 300 (supplied by BASF), with molecular weight of approximately 300 and an -OH number of 469 mg KOH/g were added to 2.5 x 10⁻² equivalents of a polycaprolactone with molecular weight 1000, functionality 2 and -OH number 113.5 mg KOH/g (CAPA 214 supplied by INTEROX) were added to with: 1.5 x 10⁻² equivalents of polycaprolactone, functionality 2,4, molecular weight 250 and -OH number 540 mg KOH/G (CAPA 304, supplied by INTEROX) 2.5 x 10⁻² equivalents of a poliether mixture code-named LAB-A-2499, functionality 2,4, molecular weight approximately 800 and -OH number 166 mg KOH/g (supplied by HULS). 4.5 x 10⁻² equivalents of a polycaprolactone with molecular weight 1000, functionality 4 and -OH number 211.46 mg KOH/G (CAPA 800 supplied by INTEROX) 0.5 x 10⁻² equivalents of a polycaprolactone with molecular weight 1000, functionality 2 and -OH number 112 mg KOH/g. After homogenization, addition was made to such mixture of 5 g of tributyl phosphate, 12 g of n-vinylpyrrolidone, 12 g of 2-ethylhexyl acrylate, 1.7 g of trimethylolpropane triacrylate, 8.3 of a middle/high-boiling solvent, 0.15 of a mixture of silicone agents, 0.6 g of a photoinitiator, 0.06 g of catalyst DBTL (dibutyl-dilauryl-Sn). The whole was dried and dearated as taught by the art and addition was then made to it of 29.2 g of an isocyanic polyadduct (31% NCO) supplied by Hüls. Following homogenization, the viscosity of this mixture at 23°C was around 62 centipoise, and it was sprayed onto a curved and physically tempered glass sheet, thickness 3.1 mm, so as to obtain a wet film thickness of approximately 100 to 150 microns. The resultant layer was spun for 5 minutes at approximately 15 to 25 rpm and then underwent a brief exposure to UV radiation lasting between 1 and 5 seconds during the final phase of spinning. The UV radiation and spinning were terminated simultaneously and the coated article underwent further and identical spray, spinning and UV exposure operations until such time as a film thickness of approximately 500 to 700 microns was obtained. When the desired thickness had been obtained the coated product was given IR treatment such that the temperature on the coated surface of the glass sheet was between 75 and 120°C, for a duration ranging from 60 to 180 minutes. After this period the product was cooled in air and, after a 7-day interval, was tested in accordance with the regulations in force, which it satisfied, demonstrating among other things great effectiveness in eliminating flying glass fragments and formation of very blunt fragments on fracture. These tests were repeated after 3,000 hours of artificial ageing: the results showed that there was no significant deterioration of the mechanical and optical properties of the coated product. EXAMPLE 2 Spray-application was mde on a chemically tempered, curved glass substrate, thickness 1.8 mm, of a liquid mixture comprising: 4 g of PTHF 300 (polyether) 6.5 g of PTHF 1000 (polyether) 13 g of PTHF 650 (polyether) 3 g of CAPA 212 (polycaprolactone) 8 g of CAPA 305 (polycaprolactone) 3 g of CAPA 800 (polycaprolactone) 2 g of CAPA 793 (polycaprolactone) There were then homogenized and added 7.5 g of NVP (1-vinyl-2-pyrrolidone), 5 g of 2-ethylhexyl acrylate HEA, 0.5 g of pentaerythritol tetracrylate, 0.2 g of silicone flow control agents (SILWET L77 and 7500 in equal parts by weight), 0.3 g of a photoinitiator as at c) above, 0.02 g of a catalyst such as mercury salt type TORCAT 535 (supplier THOR) and the whole was held under stirring in vacuo at a temperature close to 100°C for 3 hours. After the whole had cooled, addition was made to it of 25.5 g of an isophoron diisocyanate adduct (IPDI) code-named LAB-B-2499 supplied by Hüls. The mixture was then distributed, and the coated product then treated, in exactly the same way as in Example 1, and there were likewise obtained physical, mechanical and optical properties that satisfied the tests according to international regulations even after artificial ageing for 3,000 hours. EXAMPLE 3 Using the curtain coating method, a mixture of composition as given below was distributed onto a curved and annealed sheet: 8 x 10⁻² equivalents of PTHF 300 2.3 x 10⁻² equivalents of CAPA 304 0.6 x 10⁻² equivalents of a polyether/polyester code-named CAPA 828-022 (supplied by INTEROX) with molecular weight of 978, functionality 2, -OH number 114.59 mg KOH/g. 2.5 x 10⁻² equivalents of polyetheric mixture code-named LAB-A-2499 (supplied by Hüls) 4.1 x 10⁻² equivalents of a CAPA 800 6.8 x 10⁻² equivalents of a polyether/polyester code-named CAPA 828-021 (supplied by INTEROX), with molecular weight 696, functionality 2, -OH number 160.86 mg KOH/g. 0.20 g of suitable silicone flow control agents (SILWET L77-7500 - 7001) 3.5 of an adhesion promoter code-named SILANE-Y-9030 (supplied by UC) 12% of ethyleneglycol acetate monoethyl ether solvent 5% of a tributyl phosphate plasticizer 30% of a 1 in 1 mixture of NVP and 2-ethylhexyl acrylate 1 g of TMPTA (trimethylolpropane triacrylate) 0.7 g of a photoinitiator (DAROCUR 1116, supplied by MERCK) 0.04 g of a catalyst (mercury salt TORCAT) 35.5 g of isocyanate (31% NCO) The viscosity of the above composition was 50 centipoise. The said mixture was distributed and treated in exactly the same way as in the preceding examples, likewise conferring physical, mechanical and optical properties on the duplex products such as satisfied, even after 3,000 hours of artificial ageing, the requirements of international safety regulations. EXAMPLE 4 A liquid mixture was prepared, of composition as follows: 19 parts of a polytetrahydrofuran with molecular weight 300, functionality 2, -OH number 469 mg KOH/g 5.4 parts of a CAPA 214 (supplied by INTEROX) 1.5 parts of an N,N,N′,N′′,N′′′-Pentamethyldiethylene triamine 17.2 parts of a polyether mixture code-named A2499 20.8 parts of a tetrafunctional polycaprolactone with molecular weight 1000 and -OH number 216.46/KOH/g 20.2 parts of a polytetrahydrofuran, with molecular weight 1000, functionality 2, -OH number 112 KOH/g 0.4 parts of a mixture of silicone surfactants 5.8 parts of a plasticizer of the TBP type 23 parts of NVP 23 parts of neopentylglycol diacrylate 3 parts of pentaerythritol triacrylate 15 parts of a middle-boiling solvent 5 parts of an adhesion promoter wherein the molecule comprises the -NCO function 1 part of photoinitiator DAROCUR 1173 0.03 parts of DBTL. Such mixture was suitable deaerated and homogenized and then addition was made to it of 54 parts of a mixture of IPDI (31% -NCO). After stirring as required, the mixture was sprayed onto a glass substrate and spun for 8 minutes and then exposed to UV radiation for 5 seconds. The final duplex product was found to possess the desired safety characteristics and, in particular, the film showed itself to have excellent adhesion, even after exposure to damp.

Claims: Process for manufacturing safety glazing, in particular for motor vehicle or buildings, formed of a first layer of at least one glass sheet to which a second layer of a plastic coating is bonded, which consists of: preparing a coating composition which comprises: a) a solution of polycaprolactones with molecular weight between 200 and 1200 and polyethers with molecular weight between 250 and 1000, said polyethers being present in a amount of 30-70% by weight of said solution, said solution being dissolved in an amount of between 10 and 40% of b) a mixture of a vinyl monomer N-vinyl-2-pyrrolidone, with at least 10% and not more than 105% of a mono-, di-, tri- and tetra-acrylate monomers, such as: 2-ethylhexyl acrylate; butoxyethoxyethyl acrylate; 1,4-butandiolo diacrylate; ethyleneglycol diacrylate; neopentylglycol diacrylate; hexane diol diacrylate; diacrylic derivative of bisphenol A; diethyleneglycol diacrylate; tripropylenglycol diacrylate; tetraethyleneglycol diacrylate; trimethylolpropane triacrylate; pentaerythritol triacrylate; pentaerythritol tetraacrylate; c) a photoinitiator such as 2-hydroxy-2-methyl-1-phenyl--propane-1-one or a substituted derivative thereof or a mixture thereof added in an amount between 0.5 and 3% of the total composition; d) one or more silicone flow control agents or fluorinated flow control agents in an amount of 0.1 to 0.4%; e) reaction catalysts in an amount of 0.02 to 0.4%; f) an aliphatic polyisocyanate in an amount sufficient to react with an amount less than the stoichiometric amount of the hydroxyl groups present in the initial part of the composition (i.e. with an -NCO index from 1.01:1 to 1.1:1) added immediately before use; applying to the said glass sheet the said coating composition with a viscosity between 40 and 290 centipoise immediately after preparation and before any significant change in viscosity caused by the initiation of the reaction between the hydroxyl and isocyanate groups in the composition; immediately after applying the composition, spinning the glass sheet at around 10 to 50 rpm so as to ensure a constant thickness spread of the coating composition film over the entire surface of the said sheet and to ensure that the thickness is kept constant at between 80 and 150 microns; exposing the film to a high-intensity UV light source for a time sufficient to complete the polymerization of the acrylic and vinyl monomers, and terminating the spinning of the sheet; heat-treating the coated glass sheet to complete the formation of polyurethane from the hydroxyl and isocyanic groups of the polyisocyanates. Process as described in claim 1, wherein the coating composition also comprises: g) a middle-or high-boiling solvent such a toluene, xylene, acetates, etc., in an amount from 5 to 15%. Process as described in claim 1, wherein the coating composition also comprises: h) plasticizers such as DOP, DBP, TBP, BBP, DIBP or others, in an amount from 5 to 15%. Process as described in claim 1, wherein the coating composition further comprises: i) adhesion promoters such as Z r -Methacrylates or titanates or silanes with chemical functions appropriately chosen to promote the anchorage between glass support and polymer matrix. Process as described in claim 1, wherein the coating composition is applied to the glass sheet by spray-coating. Process as described in claim 1, wherein the coating composition has a viscosity of between 40 and 200 centipoise at the time of spray coating. Process as described in claim 1, wherein the coating composition is applied to the glass sheet in an amount such as to obtain a wet film thickness between 80 and 150 microns. Process as described in claim 1, wherein the glass plate is spun for a duration of 5 to 10 minutes. Process as described in claim 1, wherein the high-intensity UV light source has a relatively wide emission spectrum, and consists in particular of a medium mercury-pressure lamp operating at an intensity of about 40 Watts per centimetre, and wherein the exposure lasts between about 2 seconds and one minute. Process as described in claim 1, wherein after the exposure of one coating layer to UV light a new layer of coating composition is distributed over such layer to form a further coating layer and wherein this procedure is repeated up to the exposure to UV light, i.e. is repeated until such time as there is obtained a coating of total thickness not less than 200 microns, preferably not less than 300 microns, after which the final heat treatment of the process is carried out. Safety glazing, in particular for motor vehicles or for buildings, of the type comprising a glass sheet and a plastic coating, wherein the glazing is obtained in accordance with the process as described in one of the claims from 1 to 10. Safety glazing as described in claim 11, wherein the coating has a thickness of not less than 300 microns. Safety glazing as described in claim 11, wherein the glass sheet consists of an annealed glass sheet. Safety glazing as described in claim 11, wherein the glass sheet is curved and the coating is applied onto the concave side of the sheet. Safety glazing as described in claim 11, wherein the glass sheet is curved and tempered before the coating is applied. Safety glazing as described in claim 15, wherein the glass sheet is of the laminated type, i.e. consists of at least two glass sheets between which a plastic interlayer is applied.

Inventors: CAPRIOTTI, LUIGI, SEBASTIANO, FRANCESCO
Applicants: SOCIETA ITALIANA VETRO - SIV SPA
Application year: 1987
Main classification: C03C17
IPC codes: B32B17, C03C27, C03C17