COMPOSITIONS CONTAINING BISPHENOL COMPOUNDS

Abstract: Bisphenol compounds of the formula: (in which R₁ is a C₁-C₃ alkyl group, a C₂-C₄ alkenyl group, a phenyl group or a 2-phenylethenyl group; R₂ is a C₁-C₅ alkyl group or a cyclohexyl group; R₃ is a C₁-C₉ alkyl group, a cyclohexyl group or a phenyl group; and R₄ is a C₁-C₁₁ alkyl group or a phenyl group) are prepared by reacting a carboxylic acid of the formula: (wherein R₁ is as defined above) with a bisphenol compound of the formula: (wherein R₂, R₃ and R₄ are as defined above) by the use of a halogenating agent in the presence of a dehydrohalogenating agent. Stabilized butadiene compositions contain as stabilizer certain compounds of formula (I), namely those in which R₁ is a group -CH=CH₂ or -C(CH₃)=CH₂; R₂ is -C(CH)₃; R₃ is a group -C(CH₃)₂-R′ (in which R′ is C₁-C₅ alkyl or phenyl): and R₄ is C₁-C₄ alkyl.

Description: The present invention relates to polymer compositions containing certain bisphenol compounds. It is well-known that butadiene polymers such as solution polymerized polybutadiene rubbers (BR), solution-polymerized styrene-butadiene copolymer rubbers (SBR), styrene-butadiene block copolymers (SBS) and the like are usually produced in a hydrocarbon solvent by anionic polymerization using a Ziegler catalyst or an organolithium compound as a catalyst. Hitherto, the polymerization solvent has been removed from the solution after the polymerization reaction by the steam stripping method. However, a direct solvent drying method capable of decreasing the consumption of steam down to the theoretical minimum has been proposed in order to save energy. However, this method is usually carried out at a high temperature of about 150-200°C which is considerably higher than the boiling point of the polymerization solvent. Thus, problems of gel formation arise in the course of treatment and coloration of polymer itself occurs after the high temperature treatment. Accordingly, it is desired to improve the heat resistance and coloration resistance of butadiene polymers in the course of their production and particularly in the absence of oxygen. Further, high impact polystyrene modified with BR, SBR, SBS and the like, as well as SBS itself, may be processed by the film extrusion method. As the temperature of this method becomes higher and the processing speed increases, the tendency to form fish eye gel increases due to the low heat resistance of the polymer; as a result of which the film properties are markedly deteriorated and coloration takes place. It is a hitherto known technique to add an antioxidant of phenol type, phosphorus type, sulfur type or the like to a butadiene polymer in the course of its production or processing. For example, phenolic antioxidants such as 2,6-di-t-butyl-4-methylphenol, 2,2'-methylenebis(4-methyl-6-t-butylphenol), n-octadecyl 3-(3,5-di-t-butyl-4-hydroxyphenol)-propionate, triethylene glycol bis[3-(3-t-butyl-4-hydroxy-5-methylphenyl)-propionate], pentaerythritol-tetrakis[3-(3,5-di-t-butyl-4-hydroxyphenyl)propionate] and 1,3,5-trimethyl-2,4,6-tris-(3,5-di-t-butyl-4-hydroxybenzyl)-benzene, have been used in the form of single substance; or these phenolic antioxidants have been used in combination with phosphorus type antioxidants such as tris(nonylphenyl) phosphite, distearyl pentaerythritol diphosphite and the like, or in combination with sulfur type antioxidants such as dilauryl thiodipropionate, dimyristyl thiodipropionate, distearyl thiodipropionate and pentaerythritol tetrakis-(3-laurylthiopropionate). However, all these processes are incapable of exhibiting a sufficient preventive effect against the thermal deterioration (gelation) taking place during high temperature treatment for separating a butadiene polymer from a polymer solution or during high temperature processing of a butadiene polymer. As a stabilizer for such butadiene polymers, 2-t-butyl-6-(3-t-butyl-2-hydroxy-5-methylbenzyl)-4-methylphenyl acrylate is mentioned in US Patent No. 4,525,514. Although this stabilizer exhibits a preventive effect against thermal deterioration (gelation) taking place during high temperature treatment for separating the formed polymer from a polymer solution in the production of the polymer, it has become apparent that this stabilizer is disadvantageous because the separated polymer is practically unsatisfactory in color. Further, as a coloration-resistant antioxidant for preventing various synthetic resins from coloration due to oxidative deterioration in the presence of oxygen, US Patent No. 4,365,032 has proposed monoester compounds of 2,2'-alkylidenebis(4,6-di-substituted phenol). However, in the specification of this patent, the prevention of thermal deterioration and coloration taking place during high temperature treatment, in the absence of oxygen, for separating the formed butadiene polymer from polymer solution in the production of the polymer or during its high temperature processing is not mentioned at all. Further, the monoester compounds of 2,2'-alkylidenebis(4,6-di-substituted phenol), of which the 4-position is substituted by a methyl, ethyl or propyl group, do not exhibit any sufficient preventive effect against the thermal deterioration and coloration, in the absence of oxygen, of butadiene polymer during high temperature treatment for separating the butadiene polymer from a polymer solution in the production of the polymer or during its high temperature processing. Other alkylidene-bis(4,6-disubstituted phenol) monoesters are suggested in EP-A-0144477 and US-A-4562281. It has now been found that certain bisphenol compounds, namely compounds of the formula: [in which R₅ is a C₁-C₄ alkyl group; R₆ is a group -C(CH₃)₂-R' (in which R' is a C₁-C₅ alkyl group or a phenyl group), or a phenyl group; and R₇ is an acrylate or methacrylate residue] are quite effective as stabilizers for butadiene polymers in the absence of oxygen, and that a butadiene polymer composition containing the bisphenol compound (IV) in an amount of 0.05 to 2 parts by weight per 100 parts by weight of butadiene polymer is quite stable to the thermal deterioration and coloration in the absence of oxygen. In the bisphenol compounds of formula (IV), a lower carbon number of the alkyl group of group R₅ is more preferable, and R₅ is most preferably a methyl group, from the viewpoint of preventing gelation of butadiene polymers at high temperatures. Further, R₆ is preferably a group -C(CH₃)₂-R' having a tertiary carbon atom or a phenyl group from the viewpoint of preventing coloration of butadiene polymer. As said group having a tertiary carbon atom, the t-butyl, t-amyl and t-octyl groups are preferred, the t-butyl group being most preferred. Typical examples of bisphenol Compounds of formula (IV) are listed in Table 1. In the structural formulas of Table 1, Known processes for producing bisphenols of formula (IV) include (i) the process described in US-A-3,984,372 which comprises converting a carboxylic acid to an acid halide by the use of a halogenating agent (e.g. a chlorinating agent such as thionyl chloride, phosphorus trichloride or phosphorus pentachloride, or a brominating agent such as phosphorus tribromide) and then reacting the acid halide with a bisphenol compound in the presence of a dehydrohalogenating agent; and (ii) the process described in Japanese Patent Application Kokai (Laid-Open) No. 61323/81 which comprises reacting an acid halide or an acid anhydride with a bisphenol compound in the presence of a basic catalyst such as pyridine, dimethylaniline or the like. In these known processes, the yield of bisphenol compound based on the starting carboxylic acid is necessarily very low, because the process involves two steps and the yield of acid halide or acid anhydride is generally low. We have found, that bisphenols of formula (IV) may be produced, using a novel process, in one step and in good yield, which process comprises reacting acrylic acid or methacrylic acid with a bisphenol compound of the formula: (in which R₅, and R₆ have the meanings defined above) by the use of a halogenating agent in the presence of a dehydrohalogenating agent. Specific examples of bisphenol compounds of formula (III) include 2,2'-ethylidenebis(4,6-di-t-butylphenol), and 2,2'-butylidenebis(4,6-di-t-butylphenol). Particular examples of dehydrohalogenating agents which may be employed include tertiary amines, such as triethylamine, dimethylaniline, N,N-dimethylbenzylamine and, tetramethylurea; pyridine; and pyridine derivatives such as 4-(N,N-dimethylamino)-pyridine. Examples of halogenating agents include phosphorus oxyhalides such as phosphorus oxychloride and, phosphorus oxybromide; and toluenesulfonyl halides such as o -toluenesulfonyl chloride, and p -toluenesulfonyl chloride. The process is usually carried out in the presence of a solvent. Suitable solvents include aliphatic hydrocarbons such as n-hexane, and n-heptane; alicyclic hydrocarbons such as cyclohexane; aromatic hydrocarbons such as benzene, toluene and, xylene; esters such as ethyl acetate and, butyl acetate; ethers such as diethyl ether, tetrahydrofuran, ethylene glycol dimethyl ether and the like; and halogenated hydrocarbons such as dichloromethane, chloroform, carbon tetrachloride and, 1,2-dichloroethane. Among the above-mentioned dehydrohalogenating agents, those which are liquid at room temperature may also be used as solvents. The molar ratio of carboxylic acid to bisphenol compound will usually be from 0.7 : 1 to 1.5 : 1 and more preferably from 0.9 : 1 to 1.2 : 1. The amount of halogenating agent used will depend, inter alia, on its nature. Thus, when it is phosphorus oxychloride or phosphorus oxybromide, the amount of halogenating agent is suitably from 0.5 to 1.0 mole, preferably 0.6 to 0.9 mole and more preferably 0.65 to 0.9 mole, per mole of carboxylic acid. When it is o - or p -toluenesulfonyl chloride, the amount of halogenating agent is suitably 0.8 to 1.6 moles, preferably 0.9 to 1.2 moles, per mole of carboxylic acid. The amount of dehydrohalogenating agent used will also depend on the nature of the halogenating agent. Thus, when phosphorus oxychloride or phosphorus oxybromide is used as halogenating agent, the amount of dehydrohalogenating agent is suitably from 2.7 to 3.6 equivalents, preferably 2.9 to 3.2 equivalents, per mole of halogenating agent. When o- or p-toluenesulfonyl chloride is used as halogenating agent, the amount of dehydrohalogenating agent is suitably from 0.8 to 2.4 equivalents, preferably 0.9 to 2.2 equivalents, per mole of halogenating agent. The term "equivalent" is used herein since some of dehydrohalogenating agents, such as tetramethylurea, can capture two moles of hydrogen halide per mole of dehydrohalogenating agent. The reaction temperature is suitably from -20°C to +150°C, preferably from 0°C to +120°C and more preferably from +20°C to +100°C. After the reaction, the salt formed from the dehydrohalogenating agent is separated or not separated by filtration or the like; and then (1) the reaction mixture is optionally neutralized, subsequently washed with water and the desired product thereafter obtained by evaporating off the solvent from the organic layer; or (2) water is added to the reaction mixture which is subsequently cooled and thereafter the desired product is obtained by removing deposited crystals; or (3) the desired product is separated from the reaction mixture by some other means. The product can further be purified by known procedures such as recrystallization, washing with solvent. By the above-mentioned process, bisphenol compounds of formula (IV) can be produced from appropriate carboxylic acids in one step, in high yield, and easily from an industrial point of view. The amount of bisphenol compound (IV) in the butadiene polymer is 0.05 to 2 parts by weight, preferably 0.1 to 1 part by weight, per 100 parts by weight of butadiene polymer. If the content of bisphenol compound (IV) is below 0.05 part by weight, the intended effect cannot be exhibited sufficiently. If its content is higher than 2 parts by weight, the effect given by it is not so high and the use of so large an amount merely brings about an economical disadvantage. The bisphenol compound (IV) may be incorporated into the butadiene polymer by, for example, adding it into the reaction mixture after completion of the polymerization. The butadiene polymer composition of the invention contains the bisphenol compound (IV) as a stabilizer. If desired, other additives such as ultraviolet absorbers, light stabilizers, antioxidants, metal inactivators, metallic soaps, nucleating agents, slippers; antistatic agents, flame retardents, pigments, fillers and the like may also be incorporated therein. Examples of said ultraviolet absorber and hindered amine type light stabilizer include 2-hydroxy-4-methoxybenzophenone, 2-hydroxy-4-n-octoxybenzophenone, 2-(2-hydroxy-5-methylphenyl) benzotriazole, 2-(2-hydroxy-3-t-butyl-5-methylphenyl)-5-chlorobenzotriazole, 2-(2-hydroxy-3,5-di-t-butylphenyl)-5-chlorobenzotriazole, 2-(2-hydroxy-3,5-di-amylphenyl) benzotriazole, 2,4-di-t-butylphenyl 3,5-di-t-butyl-4-hydroxybenzoate, [2,2'-thiobis(4-t-octylphenolate)] butylamine Ni salt, 2,2,6,6-tetramethyl-4-piperidylbenzoate, bis(2,2,6,6-tetramethyl-4-piperidyl) sebacate, 2-(3,5-di-t-butyl-4-hydroxybenzyl)-2-n-butyl-malonic acid bis(1,2,2,6,6-pentamethyl-4-piperidyl), 1-[2-{3-(3,5-di-t-butyl-4-hydroxyphenyl)propionyloxy}ethyl]-4- [3-(3,5-di-t-butyl-4-hydroxyphenyl)propionyloxy]-2,2,6,6-tetramethylpiperidine, polycondensate of dimethyl succinate and 1-(2-hydroxyethyl)-4-hydroxy-2,2,6,6-tetramethylpiperidine, poly{[6-(1,1,3,3-tetramethylbutyl)amino-1,3,5-triazine-2,4-diyl][(2,2,6,6-tetramethyl-4-piperidyl)imino]-hexamethylene-[(2,2,6,6-tetramethyl-4-piperidyl)imino]}, poly-{6-[morpholino-1,3,5-triazin-2,4-diyl][(2,2,6,6-tetramethyl-4-piperidyl)imino] hexamethylene-[(2,2,6,6-tetramethyl-4-piperidyl)imino]} and 2-methyl-2-(2,2,6,6-tetramethyl-4-piperidyl)amino-N-(2,2,6,6-tetramethyl-4-piperidyl)propionamide. Examples of said sulfur type antioxidant include dilauryl thiodipropionate, distearyl thiodipropionate, dimyristyl thiodipropionate, pentaerythritol tetrakis(3-lauryl thiopropionate) and 3,9-bis(2-dodecylthioethyl)-2,4,8,10-tetraoxaspiro-[5,5]-undecane. Examples of said phosphorus type antioxidant include distearyl pentaerythritol diphosphite, tris(2,4-di-t-butylphenyl) phosphite, tris(2-t-butyl-4-methylphenyl) phosphite, bis(2,4-di-t-butylphenyl) pentaerythritol diphosphite and tetrakis(2,4-di-t-butylphenyl)-4,4'-biphenylene diphosphite. The butadiene polymers to which the present invention is applicable include solution-polymerized polybutadiene rubber (BR), solution-polymerized styrene-butadiene copolymer rubber (SBR), styrene-butadiene block copolymer (SBS), high impact polystyrene (HI-PS) modified with BR, SBR or SBS. These butadiene polymers may be used alone or in combination with other polymers. The butadiene polymer compositions of the invention containing the specified bisphenol compound (IV) are quite stable to the gelation and coloration caused by thermal deterioration. If the formed polymer is separated from the polymer solution by a high temperature treatment after completion of the polymerization, therefore, a product free from gel formation and coloration can be obtained with a high stability. Further, the product of the invention is stable to the thermal deterioration taking place during processing such as injection molding, extrusion or the like. Thus, the formation of fish eye gel in the film forming process and the formation of micro gel in the injection moulding process, causing a deterioration in gloss and transparency, can be prevented, and a high quality product free from coloration can be obtained. In order that the invention may be well understood the following examples are given by way of illustration only. Preparative Example 1 Into a 2 liter four-necked flask equipped with a thermometer, a stirrer, a condenser and a dropping funnel were charged 438.7g (1.0 mole) of 2,2'-ethylidenebis(4,6-di-t-butylphenol), 72.06 g (1.0 mole) of acrylic acid, 400 g of n-heptane and 212.5 g (2.10 moles) of triethylamine. After replacing the inner atmosphere of the flask with nitrogen gas, 200.7 g (0.70 mole) of phosphorus oxybromide was dropwise added with stirring. After dropping it, the resulting mixture was kept hot at 80°C for one hours. Then, 500 g of water was added, the mixture was cooled to room temperature, and the product was collected by filtration. The product thus obtained was washed with water until the washings reached neutrality. Thus, 468.1 g of 2,2'-(ethylidenebis(4,6-di-t-butylphenol) monoacrylate was obtained as a white crystal having a melting point of 189-190°C (Compound No. 1 of Table 1). Preparative Example 2 Into the same flask as used in Example 1 were charged 466.8 g (1.0 mole) of 2,2'-butylidenebis(4,6-di-t-butylphenol), 72.06 g (1.0 mole) of acrylic acid, 600 g of toluene and 242.86 g (2.4 moles) of triethylamine. After replacing the inner atmosphere of the flask with nitrogen gas, 229.14 g (1.2 moles) of o-toluenesulfonyl chloride was dropwise added with stirring. After dropping it, the resulting mixture was kept hot at 90°C for one hour. Then, the organic layer was washed with water until it reached neutrality, and the toluene was distilled off under reduced pressure. n-Hexane was added to the residue and a recrystallization was carried out. Thus, 497.4 g (yield 95.5%) of 2,2'-butylidenebis(4,6-di-t-butylphenol) monoacrylate was obtained as a white crystal having a melting point of 193-194°C (Compound No. 5 of Table 1). Preparative Examples 3 and 4 According to the procedure of Example 1, 2,2'-ethylidenebis(4,6-di-t-butylphenol) monomethacrylate (Compound No. 2 of Table 1) and 2,2'-ethylidenebis(6-phenyl-4-t-butylphenol) monoacrylate (Compound No. 3 of Table 1) were prepared. Example 1 In an atmosphere of nitrogen gas, 1,3-butadiene was polymerized in n-hexane at a temperature of 60 to 65°C in the presence of n-butyllithium as a catalyst. As polymerization stopper, isopropyl alcohol was used. After Completion of the polymerization, a predetermined amount of test compound shown in Table 3 was added, and then the n-hexane was removed by flash evaporation at a temperature of 190°C to 200°C in an atmosphere of nitrogen gas. Thus, a polybutadiene rubber composition was obtained. In Table 3, the amount of test compound added is expressed in terms of parts by weight per 100 parts by weight of polybutadiene. The polybutadiene rubber composition thus obtained was subjected to a kneading test under a stream of nitrogen gas by means of Laboplastmill (Model 40-100, manufactured by Toyo Seiki K.K.). The preventive effect of the composition against the gelation taking place at the time of kneading was evaluated by referring to the torque behavior accompanying the gelation. The results are shown in Table 3. In Table 3, the gelation-preventive effect is expressed by "time of gelation" (the period of time required for reaching peak value of torque). A longer time of gelation means a more excellent gelation-preventive effect. [Conditions of the Test Using Laboplastmill] (1) Mixer Model R-60 (2) Range of torque measurement 0 to 500 kg-cm (3) Amount of charged composition 80 g (4) Flow rate of nitrogen gas 1 liter/minute (5) Test temperature 180°C (6) Rotation speed 10 r.p.m. in the period of preheating (8 min.); 60 r.p.m. thereafter In the production of polybutadiene rubber, the coloration after high temperature treatment was visually evaluated. The results were expressed by the following marks: O : No color Δ : Light yellow color X : Yellow color The comparative compounds used for the purpose of comparison were as shown in Table 2, wherein ┼ means t-butyl group and means cyclohexyl group. Example 2 In an atmosphere of nitrogen gas, 0.08 part by weight of n-butyllithium was added to a solution of 20 parts by weight of 1,3-butadiene in cyclohexane, and the 1,3-butadiene was polymerized at 70°C for one hour. Subsequently, 20 parts by weight of styrene, 15 parts by weight of 1,3-butadiene and 45 parts by weight of styrene were successively added, and they were successively polymerized under the condition of 70°C x 1 hour. After the polymerizations had been completed, a predetermined amount of test compound shown in Table 4 was added and then cyclohexane was removed by heating the mixture in an atmosphere of nitrogen gas. As the result, there was obtained a block copolymer composition having a B-A-B structure of which butadiene content was 35% by weight. In Table 4, the amount of test compound added is expressed in terms of part by weight per 100 parts by weight of block copolymer. The block copolymer compositions thus obtained were subjected to a strand fall extrusion test by the use of Laboplastmill Extruder. The gel content in the stranded product thus obtained was evaluated by referring to its toluene-insoluble fraction. Thus, gel content was determined by dipping about one gram of accurately weighed out stranded product sample into 200 ml of toluene, stirring it for 24 hours, collecting it by filtration using a 200 mesh wire gauze, drying the unfiltered matter, weighing it, and calculating the gel content from the weight difference before and after the test. The results are shown in Table 4. [Conditions of Test] (1) Testing machine: Laboplastmill Model 40-100 (manufactured by Toyo Seiki K.K.) (2) Extruder: Model D20-25, manufactured by Toyo Seiki K.K. (3) Conditions of measurement: Diameter of strand die 0.5 mm  Cylinder temperature 230-260°C Rotation speed 8 r.p.m. Distance of fall 93 cm Further, the extent of coloration in the stranded sample which had been obtained by high temperature processing of styrenebutadiene copolymer (SBS) in the above-mentioned manner was visually evaluated, and the results were expressed by the following marks: O : No color Δ : Light yellow color X : Yellow color

Claims: A butadiene polymer composition containing a bisphenol compound of the formula: [in which R₅ is a C₁-C₄ alkyl group; R₆ is a group -C(CH₃)₂-R' (in which R' is a C₁-C₅ alkyl group or a phenyl group), or a phenyl group; and R₇ is an acrylate or methacrylate residue], in an amount of 0.05 to 2 parts by weight, preferably 0.1 to 1 part by weight, per 100 parts by weight of butadiene polymer. A composition according to claim 1 characterized in that R₅ is a methyl group. A composition according to claim 1 or claim 2 characterized in that R₆ is a t-butyl, t-amyl, t-octyl or phenyl group. A composition according to any one of claims 1 to 3 characterized in that the butadiene polymer is a solution-polymerized butadiene rubber, a solution-polymerized styrene-butadiene copolymer rubber or a styrene-butadiene block copolymer.

Inventors: KANOOYA, TATSUO, OKAMURA, HARUKI, TAKAHASHI, YUKOH, TAKATA, TAKESHI, YACHIGO, SHIN-ICHI
Applicants: SUMITOMO CHEMICAL COMPANY, LIMITED
Application year: 1987
Main classification: C08L9
IPC codes: C08K5