PHOSPHONIC ACID/PHOSPHATE MIXTURES FOR CONTROLLING CORROSION OF METAL AND INHIBITING CALCIUM SALT PRECIPITATION IN AQUEOUS SYSTEMS

Abstract: A method of controlling the corrosion of a metal surface in contact with an aqueous system while at the same time preventing the precipitation of potentially scale-forming calcium salts such as calcium phosphate, comprises treating the system with a source of orthophosphate ion and a mixture of methylene phosphonic acid derivatives of C₆ diamines, or the salts thereof.

Description: This invention relates to a method of inhibiting the corrosion of metal surfaces, particularly iron and iron alloys and more particularly low carbon steel, in contact with an aqueous system, such as a cooling water or related water-handling system, and of preventing the precipitation in such systems of scale-forming calcium salts, particularly calcium phosphate. Aqueous systems, such as cooling water and related water-handling systems, include cooling towers and associated pumps, heat exchangers and pipelines, heating systems, gas scrubbing systems and other similar systems. Problems commonly encountered in these water handling systems include not only the electrochemical corrosion of iron and iron alloys in contact with the circulating water but also the precipitation of potentially scale-forming calcium salts. These two processes are, in fact, very closely related because methods of chemical treatment intended to control one of these problems often aggravate the difficulty caused by the other. For many years, the most common method of controlling corrosion in cooling water and related water-handling systems was to treat the water with hexavalent chromium salts, such as sodium chromate. At the same time, scaling due to slightly soluble calcium salts was prevented by treating the water with mineral acids, such as sulfuric acid, to keep the pH low enough to prevent the precipitation of the scale-forming calcium salts. Improvements in this technology over the years included the use of zinc salts and phosphates in combination with the chromates, which could provide good corrosion control at reduced chromate concentrations. However, because of environmental concerns over the discharge of even small amounts of hexavalent chromium in cooling water effluents, new methods continued to be sought that would provide total corrosion inhibition without the use of hexavalent chromium. Some of the ways that this has been achieved include the use of various combinations of zinc salts, phosphates, polyphosphates, and organic phosphonic acid derivatives and their salts. However, all of these methods in the prior art have certain disadvantages, such as requiring close control of the pH to keep it within a very narrow range or using special additives or dispersants to prevent the precipitation of scale-forming salts like calcium phosphate. One commonly used method of cooling water treatment is described by Geiger and May in US Patent 4,305,568. In the Geiger and May patent, it is said at col. 10, begining at line 9, that the aqueous medium must have a pH of 5.5 and above and must also contain calcium ion concentrations, preferably about 15 parts per million. The compositions disclosed in the Geiger and May patent contain a water-soluble orthophosphate, a water-soluble polymer composed primarily of moieties derived from acrylic acid and moieties derived from an hydroxy lower alkyl acrylate. Water-soluble organo-­ phosphonic acid derivatives may also be included. In the Geiger and May method, as practiced, relatively high concentrations of the orthophosphate are maintained in the circulating water to inhibit corrosion by passivating ferrous alloy surfaces in contact with the water, and the formation of calcium phosphate scale is inhibited by the simultaneous use of the copolymers of acrylic acid and hydroxyalkyl acrylates. The latter copolymers were reported by Godlewski in U.S. Patent 4,029,577 to be effective antiprecipitants for calcium phosphate. The main disadvantages of the method of Geiger and May in practice are that it requires the use of relatively high concentrations of orthophosphate and careful control of the calcium concentration in the system. Such requirements complicate trouble-free control of the system. Another type of method of corrosion control that avoids the problem of calcium phosphate deposition involves the use of what is known in the art as "all organic" corrosion inhibitors. Technology of this type is described in U.S. Patents 4,317,744 and 4,406,811. In this type of method, corrosion control is obtained by using organic phosphonic acids (or blends of phosphonic acids) along with aromatic azoles and various water-soluble polymers (polyacrylic acid, polymethacrylic acid). No calcium phosphate precipitation can occur because no orthophosphate is present in the treatment. However in practice, methods of this type give limited corrosion protection and require relatively large amounts of inhibitor, and thus have limited economic feasibility. Despite the limitations of the existing "all organic" inhibitors, organic phosphonic acids and phosphonates have been found effective as corrosion inhibitor components when used in combination with other substances. The evolution of phosphonic acid corrosion control technology began with the direct application of phosphonic acids or their water-soluble salts as corrosion inhibitors. The disadvantages of this technology were twofold. First, the phosphonic acids or phosphonates commonly available required very high feedrates to obtain acceptable corrosion inhibition. In addition, localized corrosion, known in the art as "pitting", could result from insufficient passivation due to poor film formation when the phosphonic acids were used alone. This problem was recognized by Carter (US Patent 3,837,803) who overcame it by utilizing orthophosphate with a water-soluble organo-phosphonic acid compound selected from a wide range of phosphonic acids. However, Carter acknowledged two significant restrictions in the use of his method. First, as explained at column 3, beginning at line 4, the cooling water has to contain at least 50 ppm of calcium ion to allow the use of this method without the supplemental addition of a metal cation of the group zinc, nickel, cobalt, cadmium or chromium. The undesirable evironmental impact of these heavy metal cations is significant, and, as Carter pointed out, governmental regulations often require that they be avoided in effluents. In the teachings of Carter at column 3, one way of getting around the use of these metal cations, at least in systems containing more than 4 ppm of calcium, is to maintain system pH in the range of 8.5 to 9.0 However, as pointed out by Carter at column 3, lines 34-37, this high pH can lead to the delignification of cooling tower wood and may require the supplemental feed of alkali, both of which are undesirable. A second major drawback of the method of Carter is his statement at col. 3, lines 60-65, that it is desirable to use very tight pH controls when calcium concentrations exceed 80 ppm. Specifically, Carter suggests a pH between 7.1 and 7.5 when calcium ion concentration exceeds this level. This is a very significant disadvantage in almost all systems because calcium levels often vary over broader ranges than 50 to 80 ppm. Carter requires one narrow pH range for calcium concentrations below 50 ppm and suggests a different but still narrow pH range for calcium concentrations above 80 ppm. Also, when calcium is above 80 ppm, the suggested restriction of pH to the 7.1-7.5 range is difficult to maintain on a consistent basis in most practical operating cooling water systems. Other combinations of phosphonic acids and inorganic compounds are also mentioned in the prior art. Polyphosphates and polyacrylic acids were combined with phosphonic acids by Gaupp (US Patent 3,992,318). Polyphosphates and polymaleic anhydride or polymaleic acid were combined with phosphonic acids by Sexsmith (US Patent 4,105,581). However, because polyphosphates revert in time to orthophosphates, it is believed that, in practice, these methods also cause problems with calcium phosphate precipitation. We have now found that use of a certain combination of phosphonic acids (or their water-soluble salts) along with orthophosphate, preferably in low concentrations, will provide good corrosion inhibition and simultaneously inhibit the precipitation of insoluble calcium salts and especially calcium phosphate. The present invention, moreover, is effective in both high and low pH waters and in waters with either low or high concentrations of calcium. Thus the present invention provides a method and composition which can be effective over a wider range of water conditions than are the methods of the prior art and without the negative impact on the environment of some of the prior methods. According to the present invention there is provided a method of controlling corrosion of a metal surface in contact with an aqueous system by incorporating into the aqueous system a source of orthophosphate ion characterised in that corrosion of the metal surfaces in contact with the aqueous system is controlled while simultaneously inhibiting the precipitation of insoluble calcium salts by incorporation into the aqueous system of effective amounts of (1) 1,2-diaminocyclohexanetetrakis(methylene phosphonic acid) or a salt thereof; (2) 2-methyl-1,5-pentane­ diaminetetrakis(methylene phosphonic acid) or a salt thereof; and (3) 1,6-hexanediaminetetrakis(methylene phosphonic acid) or a salt thereof. The present invention further provides a composition for controlling corrosion of a metal surface in contact with an aqueous system whilst simultaneously inhibiting the precipitation of insoluble calcium salts characterised in that the composition comprises a source of orthophosphate ion and (1) 1,2-diaminocyclohexanetetrakis(methylene phosphonic acid) or a salt thereof; (2) 2-methyl-1,5-pentane­ diaminetetrakis(methylene phosphonic acid) or a salt thereof; and (3) 1,6-hexanediaminetetrakis­ (methylene phosphonic acid) or a salt thereof. The present invention still further provides a composition for inhibiting the precipitation of insoluble calcium salts in aqueous systems containing a source of orthophosphate ion characterised in that the composition comprises (1) 1,2-diaminocyclo­ hexanetetrakis(methylene phosphonic acid) or a salt thereof; (2) 2-methyl-1,5-pentanediaminetetrakis­ (methylene phosphonic acid) or a salt thereof; and (3) 1,6-hexanediaminetetrakis(methylene phosphonic acid) or a salt thereof. Low concentrations of orthophosphate can advantageously be used in the present invention, which reduces the chance of calcium phosphate scale formation. In addition, the combination of phosphonic acids utilized in the present invention is effective both as a corrosion inhibitor and as an antiprecipitant for inhibiting the precipitation of calcium phosphate and other insoluble calcium salts. Unlike the method of Carter as taught in U.S. Patent 3,837,803, the present invention, utilizing a source of orthophosphate ion and the mixture of methylene phosphonic acids described above, does not require close control of the pH or the supplemental addition of heavy metal cations. Unlike the method of Geiger and May , as well as that of Carter , the present invention does not require close control of the calcium concentration. The metal surface on which corrosion is to be controlled may be an iron or iron alloy surface, preferably a ferrous alloy. More preferably, the metal surface is a low carbon steel surface. Preferably, the aqueous system is a cooling water system. The organic phosphonic acids utilized in this invention may be manufactured from the corresonding diamines. These diamines all have 6 carbon atoms in their structures and include 1,2-diaminocyclohexane, 2-methyl-1,5-pentanediamine and 1,6-hexanediamine, all of which are commercially available. The phosphonic acid derivatives are produced through the following phosphonomethylation reaction: where R represents the C6 radicals of the diamines listed above. Hydrochloric acid is usually added to the reaction mixture to suppress the oxidation of phosphite to phosphate. As recited above, the phosphonic acids may be used in salt form. Preferred salts include the sodium, potassium and ammonium salts of these acids, which salts may be formed by partially or completely neutralizing the acids with sodium hydroxide, potassium hydroxide or ammonium hydroxide respectively. According to the present invention, a mixture of the methylene phosphonic acids and/or their salts is used in combination with a source of orthophosphate ion to treat the water in aqueous systems. The amount of phosphonic acid mixture (100% basis) added to the water should generally be in the range of 1 to 100 parts per million (ppm), preferably from 3 to 100 ppm, more preferably from 3 to 50 ppm, most preferably from 9 to 15 ppm, based on the total weight of water in the system. The amount of orthophosphate compound added should generally be sufficient to provide 0.5 to 50 ppm orthophosphate as PO₄, preferably from 1 to 9 ppm, more preferably from 3 to 5.2 ppm, based on the total weight of water in the system. The weight ratio of the orthophosphate ion to the phosphonic acid mixture is generally 1:200 to 50:1, preferably 0.1:1 to 10.1, more preferably 1:2.4 to 1:3.3. Sources of orthophosphate ion suitable for use in this invention including, for example, phosphoric acid (orthophosphoric acid), sodium orthophosphates, potassium orthophosphates, lithium orthophosphates, ammonium orthophosphates, organic amine salts of phosphoric acids and the organic orthophosphates set forth in U.S. Patent 3,510,436. Examples of lithium, sodium, potassium and ammonium orthophosphates include, e.g. lithium diphosphate, trisodium orthophosphate, disodium orthophosphate, monosodium orthophosphate, hemisodium orthophosphate, tripotassium orthophosphate, dipotassium orthophosphate, monopotassium orthophophate, triammonium orthophosphate, diammonium orthophosphates and monoammonium orthophosphate. The methylene phosphonic acid mixture and the source of orthophosphate ion can be added separately and individually to the water system to be treated, but it is preferable to mix all of these materials prior to addition to the water. If necessary, the combined mixture can be diluted with water and/or stabilized by the addition of adjuvants to keep the mixture from separating prior to its addition to the water system to be treated. Other compatible water treatment components, such as e.g. biocides, antifoulants and dispersants, can also be added to the mixture if desired. In a preferred embodiment of the invention, the methylene phosphonic acid mixture produced as described above is analyzed for both total phosphonic acids and total inorganic phosphate and then phosphoric acid is added to the mixture until the concentration of orthophosphate (as PO₄) reaches the desired ratio to the total weight of methylene phosphonic acids in the mixture. This mixture can then be diluted with water to any convenient use concentration. The mixture can also be formulated with other types of water treatment compounds. The following non-limiting examples serve to illustrate the present invention: In determining the corrosion inhibition provided by the compositions and methods of our invention one of the techniques used was the Spinning Disk Test Method, a testing procedure that is widely employed, with many variations, in evaluating the effectiveness of corrosion inhibitors for cooling water treatment. In the Spinning Disk Test Method, a plastic disk is attached to the end of a plastic stirrer shaft. Metal test coupons are mounted vertically on this disk, usually two coupons per test. The shaft is fastened vertically in a stirrer motor chuck and the disk and attached coupons are immersed in water contained in a 4-litre plastic cylindrical tank, which is surrounded by a constant temperature bath. The water volume in the cylindrical tank is maintained at a level that will keep the disk and coupons covered when the stirrer is started and the disk is rotated. The rotation speed of the disk is controlled at 100 rpm so that erosion and velocity effects are kept equal in all tests. The water is automatically replenished from a reservoir, with the addition being controlled with a timer and solenoid valve, at the rate of 60 milliliters of water added every 30 minutes. Excess water overflows through a special outlet to a drain. The cylindrical tank is kept covered except for the hole for the stirrer shaft to minimize evaporation losses. The composition of the water is controlled to simulate the water conditions in typical cooling water and other water-handling systems. The inhibitor being tested is added to this water in an appropriate concentration. For control purposes, tests are run in water with the same composition to which no inhibitor has been added. The metal coupons are cleaned and weighed on an analytical balance before and after exposure to the water. As a rule, the exposure time is at least five days (120 hours). The corrosion rate is calculated from the loss in weight of the coupons, the exposed area of the coupons, the density of the metal, and the time of exposure. The rate is expressed as mils (of thickness) lost per year (mpy). The percent inhibition of corrosion obtained with a given concentration of an inhibitor is calculated from the corrosion rate with this concentration of inhibitor added to the water compared to the corrosion rate in the same water containing no inhibitor, using the following formula: Another method used in evaluating corrosion inhibition efficacy involved treating the water in a Continuous Circulation Test Loop with the corrosion inhibitors to be tested. The Test Loop system consists of a 100-gallon reservoir, a circulation pump, a flow control valve, a rotameter, pipelines in which corrosion test coupons are mounted and instruments for controlling the temperature and pH and monitoring other system variables such as the dissolved oxygen level. The water is pumped from the reservoir at a controlled rate through the pipeline containing the test coupons and then back to the reservoir. The corrosion rate in this system is determined by the weight loss of the test coupons and the calculation of the percent corrosion inhibition is done in the same way as described for the Spinning Disk Test Method. EXAMPLE 1 A 1-litre, 3-neck glass reaction flask was fitted with an agitator, a reflux condenser and a thermometer and placed in a cooling water bath to which ice could be added as needed to control the temperature of the contents of the flask. To this flask were charged 234.3 g of 70% phosphorous acid. To the acid were added, slowly to avoid overheating, 57.5 g of a mixture of diamines composed of approximately equimolar amounts of 1,6-diaminocyclohexane, 2-methyl-1,5-pentanediamine and 1-6-hexanediamine. The temperature was controlled during the reaction to keep it below 70°C and the mixture was stirred continuously. After the diamines were added, 98.6g of concentrated (37.5%) hydrochloric acid were added to the reaction flask and the mixture was heated to 90-95°C. Next, 174.3 g of a 37% formaldehyde solution were added slowly to the reaction mixture over a period of 1-3/4 hours. The mixture was stirred and maintained at 90-95°C for an additional 2 hours. The mixture was allowed to cool to 25°C before being analyzed for its total phosphonic acid content and orthophosphate content. The reation yielded 560 g of solution containing 35.8% by weight of C6 diamine tetrakis(methylene phosphonic acid) mixture, based on an average molecular weight of 492, and 0.15% orthophosphate as PO₄. This solution was used as the source of the phosphonic acids in the tests described in the following examples. EXAMPLE 2 A combination of orthophosphate with the phosphonic acids prepared as described in Example 1 was tested as a corrosion inhibitor using the Spinning Disk Test Method previously described. The source of the orthophosphate ions was phosphoric acid, which was blended with the phosphonic acids prior to addition to the water. The synthetic cooling water ion concentrations, test conditions and results of this evaluation are shown in Table 1. The concentrations of phosphonic acids and orthophosphate are expressed as the amounts of active ingredients present in the water. The results show that very low concentrations of a corrosion inhibitor according to the present invention provide excellent corrosion protection to mild steel in a high calcium, high pH water with a composition typical of a large number of practical operating cooling water systems. A concentration of the corrosion inhibitor equivalent to 14.6 mg/L (ppm) of the diamine phosphonic acids and 4.6 mg/L orthophosphate as PO₄, provided 96.2% corrosion inhibition, and a concentration equivalent to 9.7 mg/L of the phosphonic acids and 3.0 mg/L PO₄ provided over 93% corrosion inhibition. EXAMPLE 3 To demonstrate the effectiveness of the corrosion inhibitors of the invention in a low calcium, low pH system, a composition containing the phosphonic acids and phosphate was tested in the Continuous Circulation Test Loop described previously. In the Test Loop, an automatic controller kept the pH at a fixed value throughout the period of the test. The composition tested again used the phosphonic acids prepared as described in Example 1 to which was added phosphoric acid as the orthophosphate source. The synthetic cooling water ion concentrations, test conditions, and results of this evaluation are shown in Table 2. These results clearly demonstrate that excellent inhibition of corrosion can be obtained in this rather corrosive water with a relatively low concentration of a corrosion inhibitor according to the invention. The corrosion rate of mild steel was reduced from 63 mpy to 2.8 mpy, which is equivalent to 95.6% corrosion inhibition. EXAMPLE 4 The effectiveness of the combination of phosphonic acids of the invention in preventing the precipitation of calcium phosphate was demonstrated by an antiprecipitation test. The combination of phosphonic acids prepared as described in Example 1, designated Composition A, was used for these tests. For comparison, similar tests were run with two other individual phosphonic acids that are widely used in the treatment of cooling water. These are aminotris(methylene phosphonic acid), commonly called AMP, and 1-hydroxyethylidene­ 1,1-diphosphonic acid, commonly called HEDP. Calcium phosphate precipitation inhibition was measured by adding a calcium chloride solution and a disodium hydrogen phosphate solution in amounts that provided 160 mg/L calcium ion as Ca and approximately 10 mg/L phosphate ion as PO₄. The appropriate amount of phosphonic acid inhibitor was added and the solution pH was adjusted to 8.5. The treated sample was capped and placed in an oven at 50°C for 24 hours. After removal from the oven, a portion of the supernatant liquid from each bottle was taken, filtered through a 0.45 micrometer pore size filter to remove any precipitated calcium phosphate and analyzed for orthophosphate. As a "Blank", a sample was prepared in the same way except that the pH was not adjusted to the alkaline side but kept on the acid side so that no precipitation would occur. The percent inhibition of precipitation was calculated from the amount of phosphate added (blank) and the difference between the amount of phosphate in solution in samples without inhibitor (Control) compared to those with inhibitor, using the following formula: The results of these antiprecipitation tests, which are shown in Table 3, clearly demonstrate that the combination of phosphonic acids of the present invention provides significantly greater inhibition of the formation of insoluble calcium phosphate than do AMP or HEDP. Inhibitor concentrations in Table 3 show the amount of active ingredient present. EXAMPLE 5 To demonstrate the effectiveness of the corrosion inhibitors of the invention in preventing deposit formation as well as controlling corrosion, a composition containing the phosphonic acids and phosphate was tested in the Continuous Circulation Test Loop described previously. A high calcium, high pH water was used because this is the type of water in which deposits are more likely to form. The composition tested again used the phosphonic acids prepared as described in Example 1 to which was added phosphoric acid as the orthophosphate ion source. The pH was automatically controlled during the test cycle to keep it on the alkaline, deposit-­ forming side. The synthetic cooling water ion concentrations, test conditions and the results of this test are shown in Table 4. The amount of corrosion inhibitor added to the water provided 12.5 mg/L of the phosphonic acids and 5.2 mg/L of PO₄. In addition to checking the corrosion inhibition in this test, the heating elements in the Test Loop system were also checked for deposition of calcium phosphate or other deposits. No measurable deposits were formed even though, as mentioned previously, the water had a relatively high concentration of calcium salts and high pH. Therefore the results of this test show that not only did this composition provide good corrosion protection (96.2% inhibition), it also prevented the formation of scale on heated surfaces in what is usually a deposit-forming water.

Claims: 1. A method of controlling corrosion of a metal surface in contact with an aqueous system by incorporating into the aqueous system a source of orthophosphate ion characterised in that corrosion of the metal surface in contact with the aqueous system is controlled while simultaneously inhibiting the precipitation of insoluble calcium salts by incorporation into the aqueous system of effective amounts of (1) 1,2-­ diaminocyclohexanetetrakis(methylene phosphonic acid) or a salt thereof; (2) 2-methyl-1,5-pentane­ diaminetetrakis(methylene phosphonic acid) or a salt thereof; and (3) 1,6-hexanediaminetetrakis­ (methylene phosphonic acid) or a salt thereof. 2. A method according to claim 1 wherein component (1), component (2) and component (3) each comprises 20 to 40 weight percent of the total weight of the three components. 3. A method according to claim 1 or claim 2 wherein the weight ratio of orthophosphate ion to total methylene phosphonic acid content is from about 1:200 to 50:1. 4. A method according to claim 3 wherein the weight ratio of orthophosphate ion to total methylene phosphonic acid content is from 0.1:1 to 10:1. 5. A method according to any preceding claim wherein the source of orthophosphate ion is incorporated into the aqueous system in an amount that provides a concentration by weight of 0.5 to 50 parts of orthophosphate as PO₄ per million parts of water. 6. A method according to claim 5 wherein the source of orthophosphate ion is incorporated into the aqueous system in an amount that provides a concentration by weight of 1 to 9 parts of orthophosphate as PO₄ per million parts of water. 7. A method according to any preceding claim wherein the methylene phosphonic acid components are incorporated into the aqueous system in an amount to give a total methylene phosphonic acid concentration by weight of 1 to 100 parts per million parts of water. 8. A method according to claim 7 wherein the methylene phosphonic acid components are incorporated into the aqueous system in an amount to give a total methylene phosphonic acid concentration by weight of 9 to 15 parts per million parts of water. 9. A method acording to any preceding claim wherein the source of orthophosphate ion is orthophosphoric acid, sodium orthophosphate, or potassium orthophosphate. 10. A method according to any preceding claim wherein the aqueous system is a cooling water system. 11. A composition for controlling corrosion of a metal surface in contact with an aqueous system whilst simultaneously inhibiting the precipitation of insoluble calcium salts characterised in that the composition comprises a source of orthophosphate ion and (1) 1,2-diaminocyclohexanetetrakis(methylene phosphonic acid) or a salt thereof; (2) 2-methyl-­ 1,5-pentanediaminetetrakis(methylene phosphonic acid) or a salt thereof; (3) 1,6-hexanediaminetetrakis­ (methylene phosphonic acid) or a salt thereof. 12. A composition according to claim 11 wherein the weight ratio of orthophosphate ion to total methylene phosphonic acid content is from about 1:200 to 50:1. 13. A composition according to claim 12 wherein the weight ratio of orthophosphate ion to total methylene phosphonic acid content is 0.1:1 to 10:1. 14. A composition for inhibiting the precipitation of insoluble calcium salts in aqueous systems containing a source of orthophosphate ion characterised in that the composition comprises (1) 1,2-diaminocyclo­ hexanetetrakis(methylene phosphonic acid) or a salt thereof; (2) 2-methyl-1,5-pentanediaminetetrakis­ (methylene phosphonic acid) or a salt thereof; and (3) 1,6-hexanediaminetetrakis(methylene phosphonic acid) or a salt thereof. 15. A composition according to any one of claims 11 to 14 wherein the component (1), component (2) and component (3) each comprises 20 to 40 weight percent of the total weight of the three components.

Inventors: MAY, OSCAR WILLIAM, TERRY, JOHN PALMER
Applicants: BUCKMAN LABORATORIES INTERNATIONAL, INC.
Application year: 1987
Main classification: C23F11
IPC codes: C02F5, C23F11