DISPLAY SCREEN WITH REDUCED ELECTROSTATIC FIELD, METHOD AND MEANS FOR MAKING SUCH SCREEN

Abstract: A display screen with reduced electrostatic field has applied to it a thin film (3) which contains SnO2 and Sb2O3 in a weight ratio of from 99:1 to 91:9, preferably 95:5, and which is earthed. The display screen is made by applying an aqueous solution which has been prepared from a tin (IV) halide compound and an antimony (III) halide compound in a weight ratio of from 99:1 to 91:9, preferably 95:5, and from which hydrogen halide formed has been removed, to said display screen in the form of a thin film which is dried and connected to earth.

Description: DISPLAY SCREEN WITH REDUCED ELECTROSTATIC FIELD, METHOD AND MEANS FOR MAKING SUCH SCREEN The present invention relates to a display screen with reduced electrostatic field, and also comprises a method and a means for making such screen.- People working with display screens of various types are exposed to a high degree to the electrostatic field of the screen. It is suspected that the electrostatic field constitutes a considerable health hazard since it has been found that people working with display screens are afflicted to a higher degree than others by, for example, skin irritations in the form of eruptions. It is also suspected that pregnant women working with display screens are exposed to considerable risks. It therefore is a matter of great urgency to eliminate or at least substantially reduce the electrostatic field which occurs in connection with a display screen. In view hereof, it is one of the objects of this invention to provide a display screen having a greatly reduced electrostatic field. This object is achieved, according to the present invention, by means of a display screen which is charac¬ terized in that it has applied to it a thin film which contains S 0« and Sb^O-, in a weight ratio of from 99:1 to 91:9, preferably 95:5, and which is earthed. The film preferably has a thickness of 5-100 μm. Another object of the present invention is to provide a method for making a display screen with greatly reduced electrostatic field. This object is achieved, according to the present invention, by a method which is characterized in that an aqueous solution which is prepared from a tin(IV) halide compound and an antimony(III)halide compound in a weight ratio of from 99:1 to 91:9, preferably 95:5, and from which hydrogen halide formed has been removed. is applied to the display screen in the form of a thin film which is dried and earthed. Examples of halide compounds are fluorides, chlorides bromides and iodides of tin(IV) and antimony(III) . The tin halide compound preferably is tin chloride, and the antimony halide compound preferably is antimony chloride. The aqueous solution is preferably applied to the display screen by screening technique. The aqueous solution is applied to the display screen in the form of a thin film having a thickness which preferably is 5-100 μm. A further object of the present invention is to provide a means for making a display screen with greatly reduced electrostatic field. This object is achieved, according to the present invention, by a means which is characterized in that it consists of an aqueous solution which is prepared from a tin(IV)halide compound and an antimon (III)halide compound in a weight ratio of from 99:1 to 91:9, pre¬ ferably 95:5, and from which hydrogen halide formed has been removed. The tin halide compound preferably is tin chloride, and the antimony halide compound preferably is antimony chloride. The invention will now be described in more detail, reference being had to the accompanying drawing which is a schematic sectionalized view of a display screen according to the present invention. The display screen 1 as shown in the drawing com¬ prises a glass wall 2 and an all-covering layer 3 applied to the front face of the glass wall 2. The layer 3 has a thickness of but 5-100 μm. However, in order to enhance the clarity of the drawing, the layer is shown as being considerably thicker in relation to the thickness of the glass wall 2. Furthermore, the display screen 1 has a circumferentially extending metal frame 4 which is earthed, as illustrated schematically by means of an earth connection 5. The layer 3 is connected to the metal frame 4, and thus to earth, by means of a circum- ferentially extending strip 6 of copper or other high- conductivity material. To provide the layer 3, one proceeds as follows. An aqueous solution if prepared from.a tin(IV) halide compound and an antimony(III)halide compound in a weight ratio of from 99:1 to 91:9, preferably 95:5, whereupon hydrogen halide formed therein is removed. The aqueous solution is then applied to the glass wall 2 of the display screen 1 in the form of an all-covering thin film 3. If the film is made too thick, or if the • hydrogen halide formed is not removed prior to applica- tion, the subsequent drying may easily cause fissuring, and if the film is made too thin, the resistivity therei may become too high. In view hereof, the film is prefe¬ rably given a thickness of 5-100 μ . The aqueous solution preferably is applied by screening technique, although it may of course also be applied in some other suitable manner. Application suitably occurs at a temperature of 20-50°C. The applied film 3 is allowed to dry and is finally connected to the earthed metal frame 4 by means of the circumferentially extending strip 6. In a practical test, 1 litre aqueous solution of 234 ml SnCl. and 21.5 g SbCl., was prepared. When SbCl, is dissolved in water, a hydroxo complex according to the reaction SbCl 3 + 4H 2 0 * Sb(0H) 4 + 3HC1 + H + is formed. When SnCl. is dissolved in water a correspond¬ ing reaction SnCl 4 + 5H 2 0 * Sn(0H) 5 " + HCl + H + occurs. The aqueous' solution prepared was stored for one week at atmospheric pressure and room temperature, during which the hydrochloric acid departed from the solution. The aqueous solution was then applied to thoroughly cleaned display screens, in the form of a thin film having a thickness of about 90 μm at room -temperature and by utilizing screening technique. The applied film was then allowed to dry. During drying, the hydro o complexes Sn(0H) 5 and Sb(OH).- are converted into the hydroxides Sn(OH). and Sb(OH)., which in turn are converted into the oxides SnO- and Sb~0, according to the reactions Sn(0H) 4 →- SnO_ + 2H 2 0 2Sb(0H) 3 * Sb 2 0 3 + 3H 2 0 . The water then leaves the film. After drying, there was obtained in this manner a film containing SnO^ and Sb_0, in a weight ratio of 95:5. The film formed was connected with an earthed frame corresponding to the frame 4 in the drawing, by means of a circumferentially extending copper strip, whereby the film was earthed. Measurements conducted before and after application of the film showed that the electrostatic field at the display screens had been reduced from about 15,000 V/m to about 100 V/m. The concentration of the aqueous solution prepared in the above-mentioned practical test may of course be varied. For example, this variation can be achieved by preparing an aqueous solution of a volume varying between 1/2 litre and 2 litres with the same amount of SnCl. (234 ml) and SbCl 3 (21.5 g) . It should be emphasized that the above-described method of reducing the electrostatic field may very well be used also for existing display screens since the application and the drying of the film can be carried out at room temperature.

Claims: CLAIMS 1. A display screen with reduced electrostatic field, c h a r a c t e r i z e d in that it has applied to it a thin film (3) which contains SnO- and Sb-O, in a weight ratio of from 99:1 to 91:9, preferably 95:5, and which is earthed. 2. A display screen as claimed in claim 1, c h a ¬ r a c t e r i z e d in that the film (3) has a thickness of 5-100 μm. 3. A method for making a display screen with reduced electrostatic field, c h a r a c t e r i z e d in that an aqueous solution which is prepared from a tin(IV) halide compound and an antimon (III)halide compound in a weight ratio of from 99:1 to 91:9, preferably 95:5, and from which hydrogen halide formed has been removed, is applied to the display screen in the form of a thin film which is dried and earthed. 4. A method as claimed in claim 3, c h a r a c ¬ t e r i z e d in that said tin halide compound is tin chloride, and that said antimony halide compound is antimony chloride. 5. A method as claimed in claim 3 or 4, c h a ¬ r a c t e r i z e d in that the aqueous solution is applied to the display screen by screening technique. 6. A method as claimed in claim 3, 4 or 5, c h a - r a c t e r i z e d in that the aqueous solution is applied to the display screen in the form of a thin film having a thickness of 5-100 μm. 7. A means for making a display screen with reduced electrostatic field, c h a r a c t e r i z e d in that it consists of an aqueous solution which is prepared from a tin(IV)halide compound and an antimony(III)halide compound in a weight ratio of from 99:1 to 91:9, pre¬ ferably 95:5, and from which hydrogen halide formed has been removed. 8. A means as claimed in claim 7, c h a r a c ¬ t e r i z e d in that said tin halide compound is tin chloride, and that said antimony halide compound is antimony chloride.

Inventors: PERANDER MICHAEL, PERSSON STELLAN, PERANDER, MICHAEL, PERSSON, STELLAN
Applicants: PERANDER MICHAEL, PERSSON STELLAN, PERANDER, MICHAEL, PERSSON, STELLAN
Application year: 1987
Main classification: H01J29
IPC codes: B32B9, H01J9, H01J29, H05F1