POLYMER MIXTURE WITH POLYPHENYLENE ETHER AND STABILISER

Abstract: The invention relates to polymer mixtures which comprise a polyphenylene ether. The polymer mix­ tures according to the invention are stabilised with an inorganic phosphate.

Description: The invention relates to a polymer mixture which comprises a polyphenylene ether, optionally a vinylaromatic polymer and a stabiliser. Polymer mixtures which comprise a polypheny­ lene ether, a vinylaromatic compound, for example, a high-impact polystyrene, and a stabiliser, are known for example, from US-A-4,255,321. The known stabiliser is an inorganic metal sulphide, for example, zinc sulphide, combined with a zinc oxide. As a stabiliser may further­ more be used an organic phosphite compound. The requirement imposed on stabilisers for polymer mixtures which comprise a polyphenylene ether is that they should be operative in small concentrations and that at the temperatures at which the polymer mix­ tures are processed, they are not volatile, do not cause softening, are not poisonous, do not cause non-uniform discolouring, can easily be handled, and are not too expensive. The polymer mixture according to the invention comprises a new stabiliser. The polymer mixture according to the invention has the advantage that it is not plasticised by the new stabiliser, is not poisonous, since the new stabiliser has "FDA-approval". In contrast with the generally used organic phosphite compounds, the new stabiliser is a solid so that it can more easily be handled. Moreover, the new stabiliser shows an approximately equal stabilising effect while smaller quantities by weight are used. The polymer mixture according to the invention has the advantage that it comprises as a stabiliser an inorganic hydrogen phosphate in a quantity from 0.01 to 3.0 parts by weight per 100 parts by weight of polyphe­ nylene ether. The polymer mixture according to the invention may moreover comprise a mixture of zinc oxide and zinc sulphide in a quantity from 0.01 to 3.0 parts by weight per 100 parts by weight of polyphenylene ether. The polymer mixture according to the invention preferably comprises as an inorganic hydrogen phosphate a hydrogen phosphate of an alkali metal or an alkaline earth metal, for example, monosodiumdihydrogen phosphate. In addition to the compounds mentioned herein­ before, the polymer mixture according to the invention may comprise one or more of the conventional additives. The polymer mixture according to the invention comprises at any rate one or more of the following constituents: A. polyphenylene ethers and B. inorganic hydrogen phosphates. EP-A-0078238 discloses thermoplastic com­ positions to which a calcium phosphate has been added to increase the arc resistance and to decrease the corro­ sive action of compositions comprising a flame retardant also upon contact with metals. One of the calcium phosphates that can be used is calcium hydrogen phosphate. It is claimed that the calcium addition is effective for 16 different classes of polymers. One of the mentioned classes deals with polyphenylene ethers. The described invention has been exemplified with poly­ butylene terephtalate only. The calcium phosphate is added in a quantity of 0.01-40% by weight (in the examples 5-20% by weight) in order to increase the arc resistance; it is added in a quantity of 0.01-4% by weight (in the examples 0.3-2.0% by weight) to decrease the corrosive action of thermoplastics. The only example dealing with calcium hydrogen phosphate deals with an addition of 20% by weight. The present invention deals with the stabili­ sation of polymer mixtures comprising a polyphenylene ether. The polymer mixture according to the invention may moreover comprise one or more constituents selected from the following groups: C. vinylaromatic compounds and/or D. zinc oxide and zinc sulphide and/or E. conventional additives. A. Polyphenylene ethers Polyphenylene ethers (also known as polypheny­ lene oxides ) as used in the invention are a group of polymers which are known per se . They are used in industry on a wide scale, in particular as technical synthetic resins in applications where ductility and thermal resistance are required. Since their discovery, numerous variations and modifications have been found all of which are suitable for use in the present inven­ tion, including, but not restricted to, those described hereinafter. Polyphenylene ethers comprise a number of units of the formula: In each of these units, independently of each other, each Q₁ is a halogen, a primary or secondary lower alkyl (i.e. alkyl having not more than seven car­ bon atoms), phenyl, haloalkyl, amino alkyl, hydrocar­ bonoxy or halohydrocarbonoxy in which at least two carbon atoms separate the halogen and oxygen atoms; and each Q₂ is independent hydrogen, halogen, primary or secondary lower alkyl, phenyl, haloalkyl, hydrocarbonoxy or halohydrocarbonoxy as indicated for Q₁. Examples of suitable primary lower alkyl groups are methyl, ethyl, n-propyl, n-butyl, isobutyl, n-amyl, isoamyl, 2-methyl-­ butyl, n-hexyl, 2,3-dimethyl-butyl, 2-, 3- or 4-methyl­ pentyl and the corresponding heptyl groups. Examples of secondary lower alkyl groups are isopropyl, sec-butyl and 3-pentyl. Preferably, alkyl radicals, if any, are straight instead of branched. Each Q₁ is often an alkyl or phenyl, in particular a C 1-4 alkyl and each Q₂ is a hydrogen. Suitable polyphenylene ethers are described in a large number of patents. Both homopolymeric and copolymeric polypheny­ lene ethers are suitable. Examples of suitable homopoly­ mers are those with 2,6-dimethyl-1,4-phenylene ether units. Suitable copolymers include random copolymers which comprise such units in combination with (for example) 2,3,6-trimethyl-1,4-phenylene ether units. Many suitable random copolymers and homopolymers are described in the patent literature. Also suitable are polyphenylene ethers which comprise units which change the properties such as a molecular weight, the melt viscosity and/or the impact strength. Such polymers are described in the patent literature and may be prepared by grafting vinyl monomers, for example, acrylonitrile and vinylaromatic compounds (for example, styrene) or polymers such as polystyrenes and elastomers in known manner on the polyphenylene ether. The product usually comprises both grafted and non grafted units. Further suitable polymers are the coupled polyphenylene ethers in which the coupling agent is reacted in known manner with the hydroxy groups to two polyphenylene ether chains while forming a polymer of higher molecular weight which comprises the reaction product of the hydroxy groups and the coupling agent. Examples of suitable coupling agents are polycarbonates with low molecular weight, quinone compounds, heterocyclic com­ pounds and formal compounds. Polyphenylene ethers usually have a number­ -averaged molecular weight between approximately 3,000 and 40,000 and a weight-averaged molecular weight bet­ ween approximately 20,000 and 60,000, as determined by means of gel permeation chromatography. In most of the cases the intrinsic viscosity is between approximately 0.35 and 0.7 dl/g measured in chloroform at 25° C. Polyphenylene ethers are usually prepared by the oxidative coupling of at least one corresponding hydroxyaromatic compound. Particularly suitable and easily obtainable hydroxyaromatic compounds are 2,6-xylenol (in wich each Q₁ is a methyl and each Q₂ a hydrogen), in which the resulting polymer may be indi­ cated as a poly(2,6-dimethyl-1,4-phenylene ether) and 2,3,6-trimethylphenol (in which each Q₁ and one Q₂ is methyl and the other Q₂ is hydrogen). A number of catalyst systems are known for the preparation of polyphenylene ethers by oxidative coupling. There are no restrictions as regards the choice of the catalyst and any known catalyst may be used. They usually comprise at least a heavy metal com­ pound such as a copper, manganese or cobalt compound, usually in combination with various other materials. A first group of catalyst systems preferably to be used consists of those which comprise a copper compound. Such catalysts are described, for example, in US-A-3,306,874; 3,306,875; 3,914,266 and 4,028,341. They usually consist of combinations of monovalent and biva­ lent copper ions, halogen (i.e. chloride and bromide) ions and at least one amine. Catalyst systems which comprise manganese com­ pounds form a second group which is preferably to be used. They usually consist of alkaline systems in which bivalent manganese has been combined with anions such as halide, alkoxide or phenoxide. The manganese is in most of the cases present in the form of a complex with one or more complex-forming agents and/or chelating agents, such as dialkylamines, alkanolamines, alkylene diamines, o-hydroxyaromatic aldehydes, o-hydroxyazo compounds, alpha-hydroxyamines (monomeric and polymeric), o-hydroxyaryloximes and beta-diketones. Also suitable are the known cobalt-containing catalyst systems. Suitable manganese and cobalt-containing catalyst systems for the preparation of polyphenylene ethers are known by their description in numerous patents and publications. The polyphenylene ethers usually comprise ter­ minal groups which depend on the catalyst systems used and the reaction conditions used. B. Inorganic hydrogen phosphates The polymer mixture according to the invention comprises one or more inorganic hydrogen phosphates in a quantity from 0.01 to 3.0 parts by weight per 100 parts by weight of polyphenylene ether. When quantities of less than 0.01 parts by weight are used, no noticeable stabilisation occurs. Using more than 3.0 parts by weight does not result in a further improvement of the stabilisation. Examples of suitable inorganic hydrogen phosphates are monosodium dihydrogen phosphates, disodium monohydrogen phosphate, ammonium mono- or dihydrogen phosphate, potassium mono- or dihydrogen phosphate, phosphoric acid. Hydrogen phosphates such as disodium diphosphate are also suitable. C. Vinylaromatic compounds The polymer mixture according to the invention may comprise one or more vinylaromatic polymers. Preferably used vinylaromatic polymers are polymers which are built up for at least 25% by weight of recurring units derived from a vinylaromatic compound of the formula: wherein R is a hydrogen atom; a lower alkyl or halogen; Z is a vinyl, halogen or lower alkyl; and p = 0 or an integer of at most 5. As lower alkyl groups are meant alkyl groups having 1-7 carbon atoms. Examples of the above-meant polymers are the homopoly­ mers such as homopolystyrene, poly-alpha-methyl styrene and monochloropolystyrene, modified polystyrenes, such as rubber-modified high-impact polystyrenes, i.e. polystyrene which is mixed with or grafted with natural or synthetic elastomers, such as polybutadiene, styrene­ -butadiene, EPDM rubbers, acrylate rubbers and the like. Further examples are styrene-containing copolymers such as styrene-acrylonitrile copolymers, styrene-butadiene copolymers, styrene-acrylonitrile-alpha-alkylstyrene terpolymers, styrene-acrylonitrile-butadiene copolymers, copolymers of ethylvinylbenzene, divinylbenzene and styrene-maleic acid anhydride copolymers. Furthermore may be mentioned block copolymers of styrene-butadiene or stryrene-butadiene-styrene. These blocks copolymers may be partially hydrogenated. The quantity of vinylaromatic compounds to be used may vary between wide limits. In general, this quantity is between 0 and 900 parts by weight per 100 parts by weight of polyphenylene ether. D. Zinc oxide and zinc sulphide The polymer mixture according to the invention may comprise, in combination with the inorganic phosphate, zinc oxide and zinc sulphide in a quantity from 0.01 to 3.0 parts by weight per 100 parts by weight of polyphenylene ether. E. Usual additives for polymer mixtures which comprise a polyphenylene ether In addition to the above-mentioned consti­ tuents, the polymer mixture according to the invention may comprise one or more of the additives conventionally used for polymer mixtures which comprise a polyphenylene ether. By way of example may be mentioned flame­ -retardants, such as aromatic phosphates and halogen compounds, UV-stabilisers, a small quantity of polyole­ fines such as polyethylene, dyes and pigments, agents to improve the sensitivity to crack formation upon contact with organic solvents, for example, organic sulphonates, blowing agents, lubricants, mould-release agents, rein­ forcing or non-reinforcing fillers, impact strength-­ improving agents. The polymer mixture according to the invention can be prepared according to any conventional method of preparing polymer mixtures. It is usually prepared by the collective extrusion of the desired constituents in an extruder. The invention will now be described in greater detail with reference to the ensuing specific example. Example I and comparative examples A and B. Three polymer mixtures were prepared con­ sisting of 50 parts by weight of poly(2,6-dimethyl-1,4-phenylene)ether having an intrin­ sic viscosity of 0,48 dl/g at 25°C in chloroform, 50 parts by weight of high-impact polystyrene having a polybutadiene content of 9.5% by weight, 1,5 parts by weight of polyethylene and 2,0 parts by weight of tita­ nium dioxide (comparative example A). The polymer mix­ ture according to the comparative example B comprised in addition 0.5 parts by weight of a mixture of organic phosphite compounds consisting substantially of trisno­ nylphenylphosphite and decyldiphenyl phosphite, 0.15 parts by weight of zinc oxide and 0.15 parts by weight of zinc sulphide. In the polymer mixture according to example I 0.15 parts of weight of monosodium dihydrogen phosphate were taken up instead of the organic phosphite compound, while also 0.15 parts by weight of zinc oxide and 0.15 parts by weight of zinc sulphide were taken up. The said constituents were extruded in a Werner Pfleiderer double-blade extruder at an average temperature of 285°C and 300 rpm. The extrudate was chopped up in pellets. The pellets were manufactured to form test pieces by injection moulding to determine the Izod impact strength with notch. The test rods were aged artificially in a furnace at 110 ± 2°C. The Izod notch impact value (according to ASTM D 256) of five rods was determined at regular intervals. The duration in hours until a decrease of the notch impact value of 50% had occurred was determined. The oxidation rate was determined by measuring the oxygen take up at 124 ± 0.2°C in an atmosphere of pure oxygen (pressure 1 atmosphere). For that purpose, always 1.00 g of granulate was provided in a glass tube connected to a gas burette. After thorough rinsing with pure oxygen and after reaching temperature equilibrium, the level of the burette was read regularly. The time until 5 ml and 10 ml, respectively, of oxygen had been taken up was determined. The results of the above test are summarized in the following table. It may be seen from the above results that the polymer mixture according to the invention has a better HDT Value, a more favourable melt viscosity value, and a slightly better value for the oxygen take up at 124°C. These better values are obtained at a concentration of NaH₂PO₄ which is smaller than the concentration of orga­ nic phosphite.

Claims: 1. A polymer mixture which comprises a polypheny­ lene ether, optionally a vinylaromatic polymer, and a stabilizer, characterized in that the polymer mixture comprises as a stabiliser an inorganic hydrogen phosphate in a quantity from 0,01 to 3.0 parts by weight per 100 parts by weight of polyphenylene ether. 2. A polymer mixture as claimed in Claim 1, characterized in that the polymer mixture moreover comprises a mixture of zinc oxide and zinc sulphide in a quantity from 0.01 to 3.0 parts by weight per 100 parts by weight of polyphenylene ether. 3. A polymer mixture as claimed in Claim 1 or 2, characterized in that the polymer mixture comprises as an inorganic phosphate a mono- or dihydrogen phosphate of an alkali metal or an alkaline earth metal. 4. A polymer mixture as claimed in Claims 1-3, characterized in that the polymer mixture comprises one or more of the following additives: an agent to improve the impact strength, an agent to improve the flame resistance, UV-stabilisers, reinforcing or non-­ reinforcing filling materials, dyes or pigments, agents to improve the sensitivity to crack formation under stress upon contact with solvents, blowing agents, lubricants, mould release agents. 5. Articles formed by polymer mixture as claimed in one or more of the claims 1-4.

Inventors: LOHMEIJER, JOHANNES HUBERTUS G. M.
Applicants: GENERAL ELECTRIC COMPANY
Application year: 1987
Main classification: C08K3
IPC codes: B01J31, C08K3, C08L71