A method for the production of semiconductor laser devices

Abstract: A method for the production of semiconductor laser devices comprises: (1) growing a multi-layered crystal structure (2,3,4) containing an active layer (3) for laser oscillation, on a p-substrate (1); (2) etching said multi-layered crystal structure to form a striped mesa-portion (11); and (3) surrounding said mesa-portion of the multi-layered crystal structure with a p-n-p multi-layered structure (5,6,7) resulting in a heterojunction at each of both side faces of said active layer.

Description: The present invention relates to a method for the production of semiconductor laser devices, especially those having a buried heterostructure therein. Semiconductor laser devices, which comprise a buried heterostructure resulting from surrounding the active layer for laser oscillation with a heterojunction, have an excellent device characteristic that stabilized laser oscillation can be attained in a transverse mode and a low oscillation threshold current level can be maintained at ambient temperature, and thus they are usable as laser light sources. Especially, in a conventional semiconductor laser device having a structure such as that shown in Figure 2 , in which a p type crystal 10 is employed as a substrate for epitaxial crystal growth, the p-n junction of a current confining region has to withstand voltage at a high level, so that a high output power operation can be achieved by the application of a high voltage. This conventional semiconductor laser device is produced as follows: On the p-InP substrate 10 , a p-InP buffer layer 20 , a non-doped InGaPAs active layer 30 , and an n-InP cladding layer 40 are successively grown by liquid phase epitaxy. Both sides of the resulting multi-layered crystal structure is then etched in a manner to reach the buffer layer 20. On the post-etched portion, an n-InP current blocking layer 50 and a p-current confining layer 60 are grown as burying layers. According to the structure of the above-mentioned device, in order to block the electroconductivity between the cladding layer 40 and the current blocking layer 50, the top of the current blocking layer 50 must be positioned below the active layer 30. For this reason, both the depth of etching in the multi-layered crystal structure and the growth thickness of the current blocking layer 50 must be regulated with high precision. However, neither liquid phase epitaxy nor a wet-etching technique can attain such precise regulation, resulting of a low production yield of semiconductor laser devices of this type. A method for the production of semiconductor laser devices of the present invention which overcomes the above-discussed and numerous other disadvantages and deficiencies of the prior art, comprises: (1) growing a multi-layered crystal structure containing an active layer for laser oscillation, on a p-substrate; (2) etching said multi-layered crystal structure to form a striped mesa-portion having continuous side faces without a step, and protruding from a lower plane portion of the etched structure; and (3) surrounding said mesa-portion of the multi-layered crystal structure with a p-n-p multi-layered buried structure comprising a p-buffer layer, an n-current blocking layer and a p-current confining layer, in sequence, the p-buffer layer continuously covering the side faces and the whole lower plane portion of said striped mesa-portion, resulting in a heterojunction at each of both side faces of said active layer, wherein said multi-layered crystal structure comprises a p-buffer layer, a non-doped active layer, and an n-cladding layer, in sequence, on said p-substrate. The multi-layered crystal structure is, in a preferred embodiment, etched in the range of the upper face thereof to the middle of the p-buffer layer. The p-buffer layer of said p-n-p multi-layered structure is, in a preferred embodiment, a layer, the forbidden band width of which is greater than that of the active layer and the refractive index of which is smaller than that of the active layer. The invention described herein makes possible the object of providing a method for the production of semiconductor laser devices by which semiconductor laser devices having a buried structure can be readily produced without a crystal growth process and an etching process under a highly precise regulation, and thus the production yield thereof can be increased. This invention may be better understood and its numerous objects and advantages will become apparent to those skilled in the art by reference to the accompanying drawings as follows: Figures 1(A) and 1(B) are diagrammatical views showing the production process of a semiconductor laser device according to this invention. Figure 2 is a sectional view showing a conventional semiconductor laser device having a buried heterostructure. Figure 1 shows the production process of a semiconductor laser device according to this invention. On a p-(100)InP substrate 1 , a p-InP buffer layer 2 having a thickness of 3 µm, a non-doped InGaPAs active layer 3 having a radiation wavelength of 1.3 µm and a thickness of 0.2 µm, and an n-InP cladding layer 4 having a thickness of 0.5 µm are successively grown by liquid phase epitaxy. On the cladding layer 4, a photo-resist stripe (not shown) having a width of approximately 3 µm is then formed in the (011) direction by photolithography. The multi-layered crystal structure is then subjected to an etching treatment with a Br-methanol solution in the range of the upper face thereof to the middle of the buffer layer 2, resulting in a striped mesa-portion 11 (Figure 1(A)). When the striped mesa-portion 11 is designed with a stripe width W of 2-4 µm and a height h of 2 µm, the crystal growth can be prevented from proceeding over the mesa-portion 11 in the succeeding burying-growth process (Mito et al., TGOQE 80-116). The burying growth process is then carried out as shown in Figure 1(B) in such a manner that a p-InP buffer layer 7 (the plane portion thereof having a thickness of 0.5 µm), an n-InP current blocking layer 5, a p-InP current confining layer 6 (the plane portion thereof having a thickness of 0.5 µm), and an n-InP burying layer 8 (the plane portion thereof having a thickness of 3 µm) are successively grown along the striped mesa-portion 11 by liquid phase epitaxy. Then, an n-sided ohmic electrode (not shown) and a p-sided ohmic electrode (not shown) are formed on the InP burying layer 8 and the substrate 1 , respectively, followed by cleaving at the (011) face, resulting in a semiconductor laser device. In the semiconductor laser device having the above-mentioned structure, the InGaPAs active layer 3 for laser oscillation has a junction at the interface with each of the InP buffer layer 2 and the InP cladding layer 4 in the thickness direction thereof and has a junction at the interface with the InP buffer layer 7 at each of both sides thereof, resulting in an active region which is limited to a striped form by the said heterojunctions. Since the buffer layer 7 tends to be grown on the sides of the striped mesa-portion 11, the sides of both the cladding layer 4 and the active layer 3 are covered with the p-InP buffer layer 7 so that the cladding layer 4 is electrically separated from the current blocking layer 5 and leakage current never arises between the cladding layer 4 and the current blocking layer 5 . Moreover, since the carrier concentration of the buffer layer 7 is selected to be at a low level, the buffer layer 7 functions as an insulating layer which prevents leakage current from the cladding layer 4 to the current blocking layer 5 . Moreover, since the forbidden band width of the buffer layer 7 is greater than that of the active layer 3 and the refractive index is smaller than that of the active layer 3 , it functions to confine carrier and light within the active layer 3 . When a driving current is injected into the semiconductor laser device through the n-sided ohmic electrode and the p-sided ohmic electrode, the current flows into the electroconductive region alone corresponding to the striped mesa-portion 11 including the cladding layer 4 and the active layer 3 therein and is blocked to flow outside of the striped mesa-portion 11 by the p-n-p multi-layered structure which is composed of the current confining layer 6, the current blocking layer 5 and the buffer layer 7 . The carrier and light are confined within the active layer 3 by the junction at the interface between the buffer layer 7 and the active layer 3 . The top of each p-n junction in the p-n-p multi-layered structure is positioned at the shoulder portion of the cladding layer 4 and the lower portion thereof is curved toward the lateral direction. This is because the buffer layer 7 is grown in the lateral direction during its epitaxial growth around the striped mesa-portion 11 and, on the buffer layer 7 which functions as an underlying layer, the current blocking layer 5 and the current confining layer 6 are successively formed. Because of the above-mentioned structure, a current with a high density can be fed to the active layer 3 , and the semiconductor laser device obtained exhibits an excellent device characteristic that it can oscillate at a low oscillation threshold current level in the range of 15 to 20 mA at ambient temperature and characteristic temperatures of the oscillation threshold current are 70 K or higher up To a temperature of about 100 °C. Moreover, since the depth of etching and the thickness of crystal growth layers are not required to be regulated with accuracy, the production yield is greatly improved. The above-mentioned example discloses only the InGaPAs system materials, as an active layer, which exhibit a radiation wavelength of 1.3 µm, but is not limited thereto. This invention is, of course, applicable to other InGaPAs system materials which have a radiation wavelength ranging from 1.1 µm to 1.7 µm, and/or other semiconductor materials, as well. All of the four layers constituting the buried structure in the above-mentioned example are composed of InP, but they can be InGaPAs, the forbidden band width of which is greater than that of the active layer and the refractive index of which is smaller than that of the active layer. It is understood that various other modifications will be apparent to and can be readily made by those skilled in the art without departing from the scope and spirit of this invention. Accordingly, it is not intended that the scope the claims appended hereto be limited to the description as set forth herein, but rather that the claims be construed as encompassing all the features of patentable novelty which reside in the present invention, including all features which would be treated as equivalents thereof by those skilled in the art to which this invention pertains.

Claims: A method for the production of semiconductor laser devices comprising: (1) growing a multi-layered crystal structure (2,3,4) containing an active layer (3) for laser oscillation, on a p-substrate (1); (2) etching said multi-layered crystal structure to form a striped mesa-portion (11) having continuous side faces without a step, and protruding from a lower plane portion of the etched structure; and (3) surrounding said mesa-portion of the multi-layered crystal structure with a p-n-p multi-layered buried structure (5,6,7) comprising a p-buffer layer (7), an n-current blocking layer (5) and a p-current confining layer (6), in sequence, the p-buffer layer (7) continuously covering the side faces and the whole lower plane portion of said striped mesa-portion (11), resulting in a heterojunction at each of both side faces of said active layer, wherein said multi-layered crystal structure (2,3,4) comprises a p-buffer layer (2), a non-doped active layer (3), and an n-cladding layer (4), in sequence, on said p-substrate (1). A method for the production of semiconductor laser devices as claimed in claim 1, wherein said multi-layered crystal structure is etched in the range of the upper face thereof to approximately the middle of the p-buffer layer (2). A method for the production of semiconductor laser devices as claimed in claim 1 or claim 2, wherein the p-buffer layer (7) of said p-n-p multi-layered structure is a layer, the forbidden band width of which is greater than that of the active layer (3) and the refractive index of which is smaller than that of the active layer.

Inventors: KANEIWA SHINJI, MATSUI SADAYOSHI, TAKIGUCHI HARUHISA, YOSHIDA TOSHIHIKO, KANEIWA, SHINJI, MATSUI, SADAYOSHI, TAKIGUCHI, HARUHISA, YOSHIDA, TOSHIHIKO, KANEIWA, SHINJI 101 KYOBATE MANSION
Applicants: SHARP KK, SHARP KABUSHIKI KAISHA
Application year: 1986
Main classification: H01S3
IPC codes: H01S5