CONJUGATED ALKADIENE TELOMERIZATION TO ORGANO-OXYALKADIENES

Abstract: A process for the telomerization of a conjugated alka­ diene with an alkanol is disclosed for the production of an or­ gano-oxyalkadiene. A palladium catalyst having a phosphine or stibene ligand is employed in a substantially oxygen-free envi­ ronment in the presence of a solvent for the catalyst so that the reaction products may be separated from the catalyst by distillation or solvent extraction.

Description: CONJUGATED ALKADIENE TELOMERIZATION TO ORGANO-OXYALKADIENES The invention is directed to the telomerization of alkadienes with organic hydroxy compounds in the presence of a catalyst to produce an organo-oxyalkadiene. The telomerization of conjugated alkadienes such as butadiene with alkanols in the presence of palladiumphosphine catalyst is a convenient route for the preparation of 8-methoxy-1,6-octadiene. Because of the high cost of palladium catalysts, any industrial process employing catalysts of this type requires recycling of the catalyst in order to minimize the cost of production. Accordingly, catalyst recovery and recycle is of primary concern along with selectivity, yields and speed of reaction in the selection of a catalyst for telomerization reactions of this type. Although palladium-phosphine type catalysts are effective for promoting these types of telomerization reactions after recovering and recycling the catalyst for subsequent reactions, it has been observed that the activity of the catalyst drops off significantly. Additionally, prior to recovering and recycling the catalyst the various products of the telomerization reaction must be separated by a process which does not substantially damage or deactivate the catalyst or cause a loss of the catalyst. The prior art method of recovering the telomerization product generally comprised distillation of the reaction products to remove them from the catalyst and resulted in catalyst loss and/or deactivation. In accordance with the present invention a method is provided for the telomerization of a conjugated alkadiene with an organic hydroxy compound to produce an organooxyalkadiene by reacting the aforesaid alkadiene and hydroxy compound in the presence of a palladium catalyst having a phosphine, arsine or stibene ligand. The process is conducted substantially in the absence of oxygen under anhydrous conditions and in the presence of a solvent for the catalyst. In this way products may be separated from the catalyst. The catalyst can thereafter be recycled for subsequent telomerization reactions. The solvent for the catalyst may be a polar organic solvent such that the reaction products may be separated from the solution of the catalyst by extraction with a solvent such as a hydrocarbon that is substantially immiscible in the polar solvent and which acts as a solvent for the reaction products. By employing this method of the present invention deactivation of the catalyst during the telomerization reaction is avoided by substantially eliminating contact of the reaction mass with oxygen and further, by using a solvent extraction process that minimizes exposure of the reaction products and the catalysts to air catalyst deactivation is further minimized. Alternatively, the solvent may be a high boiling solvent such that the organo-oxyalkadiene product can be distilled from the reaction mixture (which includes the catalyst) without having any substantial adverse affect on the catalyst. Vacuum fractional distillation, in this embodiment, is especially suitable for separating the organo-oxyalkadiene from the solution of catalyst without adversely affecting the catalyst although flash distillation and atmospheric distillation methods may be used. In one embodiment of the present invention a method for the telomerization of a conjugated alkadiene with an organic-hydroxy compound to produce an organo-oxyalkadiene is provided. This method comprises reacting said alkadiene with said hydroxy compound with a catalytically effective amount of a catalyst compound comprising: (I) [PdR1] [YRyê]2 R1 is any anionic group displaced by methanol except the halides. R1 especially comprises an organo acyclic or cyclic carboxylate group having from 1 to about 10 carbon atoms and especially a lower alkyl straight chain or branched chain carboxylate having from 1 to about 4 carbon atoms especially the acetate group. R2 moreparticulary may comprise a straight chain, branched chain or cyclic radical having from 1 to about 10 carbon atoms and especially may comprise either a phenyl group or a lower alkyl group having from one to about 4 carbon atoms. In the above formula (I) the moiety Y comprises either phosphorous, arsenic or antimony wherein y is the valence of Y. In the above formula (I) ligands [YRyê] may comprise: Tributylphosphine Tripentylphosphine Trihexylphosphine Tritolylphosphine Triphenylphosphine Tris(methoxyphenyl)phosphine Triphenylphosphite Tritolylphosphite Trioctylphosphine and the arsine and stibene homologs thereof. The R2 radical preferably comprises a phenyl group. The stibenes, arsines or phosphines containing alkyl groups are more susceptible to oxidation. The palladium component of the catalyst complex herein can also be zero-valent palladium, a palladiumcontaining composition which will provide zerovalent palladium, i.e., will undergo reduction, under the conditions of the reaction and/or a palladium (II) salt, with or without the additional presence of a reducing agent such as alkali metal alkoxide, alkali metal acetate and/or alkali metal borohydride. Among such palladium-containing compositions are included palladium (II) acetate, palladium (II), formate, palladium (II) octanoate, palladium (II) propionate, palladium (II) nitrate, palladium (II) bis(n-allyl), palladium sulfate. The telomerization reaction is conducted in the substantial absence of oxygen and especially under conditions in which oxygen is excluded to minimize the amount of catalyst ligand that must be replaced due to the oxidation of the stibene, arsine or phosphine moieties in the ligand. It has been discovered that the presence of even small quantities of oxygen has a deleterious affect in that oxygen causes ligand removal from the catalyst and the decomposition of the catalyst. One of the catalysts employed according to the invention and falling within the scope of the above formula (I) is palladium acetate bis(triphenylphosphine) [Pd(OAc)2] [PPh3]2. This is one of the preferred catalysts. In the above catalyst compound, [PdR1] is referred to herein as the palladium component of the catalyst and [YRyê] as the ligand. When the catalyst is employed in the reaction of the present invention, the palladium and ligand dissociate so that under reaction conditions the ratio of palladium to ligand varies. Accordingly, by the addition of ligand or palladium to the reaction mixture containing the catalyst or by the adjustment of the reaction conditions (e.g., exclusion of oxygen) the ratio of ligand to palladium of the catalyst compound in the reaction millieu is controlled to anywhere from about 10:1 to about 1:1 and preferably a ratio of from about 5:1 to about 2:1 on a molar basis. An essential feature of this embodiment of the present invention is to employ a solvent for the catalyst in which the boiling point of the solvent is higher than that of the organo-oxyalkadiene product that is produced as a result of the telomerization reaction. Generally, any solvent may be employed that is inert to the reactants and which does not have an adverse affect on the reaction. Solvents falling into this category may have a normal boiling point up to about 3000C and generally comprise those solvents having a normal boiling point at least 200C higher than the organooxyalkadiene that is produced up to about 3000C. Solvents especially suitable in this regard comprise tetraglyme (dimethyl ether of tetraethylene glycol); dimethyl phthalate; dibutyl phthalate; dioctyl phthalatet methyl oleate; diphenyl oxide; diethylene glycol; diethylene glycol mono-sec butyl ether acetate (butyl Carbitol acetate); diethylene glycol monobutyl ether (butyl ethyl Cellosolve); di-octyl azelate; methyl benzoate; butyrolactone; and NMP (N-methylpyrrolidone). After the organo-oxyalkadiene is formed, it may be separated from the solution of the catalyst and the solvent by distillation, such as by vacuum fractional distillation, flash distillation or atmospheric distillation. The distillation method is dictated by the temperature at which the separation of product by distillation is to be conducted. These temperatures preferably are from about 800C to 1100C and are selected so as to avoid any adverse affects on the catalyst. Vacuum fractional distillation is the preferred method of separating the organo-oxyalkadiene. Standard vacuum distillation apparatus and methods are employed. It has been found that by separating the organo-oxyalkadiene from the catalyst in this manner, that the catalyst is not adversely affected by the separation process and may be recycled for further use in the telomerization reaction of the present invention. It has also been found that by substantially excluding oxygen from the telomerization reaction and by employing the aforesaid class of organic solvents for the catalyst that the catalyst can be separated by distillation and recycled to the telomerization reaction in excess of 15 times without any substantial loss of catalyst activity i.e., selectivity and yield of the organo-oxyalkadiene. Furthermore, between abut 50,000 to 60,000 moles of the organooxyalkadiene may be produced for each mole of catalyst employed according to the method of the present invention. One of the advantages of the present invention is that about 90% selectivity to methoxyoctadiene is obtained at butadiene conversions of up to about 80%. Selectivities of from about 85% to about 95% at conversions of butadiene up to about 100% can be obtained with the catalyst and the method of the present invention when the telomerization reaction is conducted at temperatures from about 600C to about 800C for a period of time from about 15 to about 30 minutes. It has also been found that conversions and selectivities obtained in the telomerization reaction are independent of pressure. It has also been discovered that selectivity and yields of the telomerization reaction may be optimized at about 650C to about 750C at autogenous pressures up to 200 psig in an inert atmosphere such as an atmosphere comprising nitrogen, one of the rare gases selected from group VIII A of the Periodic Table of Elements and various mixtures thereof. In one preferred embodiment, it has been discovered that butadiene may be telomerized with a lower alkanol such as methanol in the presence of a palladium acetate triphenylphosphine catalyst where the ratio of the triphenylphosphine to palladium acetate is from about 3 to 5. A high boiling solvent such as tetraglyme and the equivalents thereof are also employed and the reaction is run at a temperature of about 700C to obtain high yields, selectivities and conversions to methoxyoctadiene. High selectivities to 8-methoxy-1,6-octadiene have been obtained in this regard with smaller amounts of 3-methoxy-1,7-octadiene also being produced, the ratio of 8-methoxy-1,6-octadiene to 3-methoxy1,7-octadiene being greater than 4:1 on a molar basis. Optimum ratios of butadiene to alkanol and especially methanol were obtained by adjusting the molar ratios of butadiene to alkanol (i.e., methanol) to about 1 to about 1.2. By employing the method of the present invention in which oxygen is excluded from the reaction and the high boiling solvent is used for the catalyst so that the methoxyoctadiene may be separated by vacuum distillation the catalyst may be successfully reused in excess of about 15 times and from about 50,000 to about 60,000 moles of methoxyoctadiene may be produced for one mole of the palladium catalyst. It has been found that during the successive recycling of the catalyst by the method described herein that even with substantial exclusion of oxygen from the process that the ligand is diminished and that in subsequent recycles of the catalyst thus recovered, small amounts of the ligand are added to the catalyst to replenish that proportion of ligand that is lost. Anywhere from about 1% to 10% of the theoretical amount of ligand is added to each successive recycle of the catalyst in this respect when proper precautions are taken to exclude oxygen from the reaction. In a second embodiment of the present invention another method for the telomerization of a conjugated alkadiene with an organic-hydroxy compound to produce an organo-oxyadiene is disclosed. In this method a conjugated alkadiene is reacted with said hydroxy compound in the presence of a catalytically effective amount of a catalyst compound comprising: (II) [PdR1] [R2Y(R3 Z) y] R 1. is is any anionic group displaced by methanol except the halides. Rl especially comprises an organo acyclic or cyclic carboxylate group having from 1 to about 10 carbon atoms especially the acetate group. R more particularly may comprise a straight chain, branched chain or cyclic radical having from 1 to about 10 carbon atoms and especially may comprise either a phenyl group or a lower alkyl group having from one to about 4 carbon atoms. The palladium component of the catalyst complex, lPdR2] herein can also be zero-valent palladium, a palladiumcontaining composition which will provide zerovalent palladium, i.e., will undergo reduction, under the conditions of the reaction and/or a palladium (II) salt, with or without the additional presence of a reducing agent such as an alkali metal alkoxide, alkali metal acetate and/or alkali metal borohydride. Among such palladium-containing compositions are included palladium (II) acetate, palladium (II) formate, palladium (II) octanoate, palladium (II) propionate, palladium (II) nitrate, palladium (II) bis(n-allyl), palladium sulfate and the like. In the above formula (I) the ligand [R2Y(R3 Z) y] comprises compounds wherein: (a) R2 is an organo group such as phenyl, benzyl, naphthyl cyclic or acyclic hydrocarbons having up to 10 carbon atoms. (b) Y is phosphorous, antimony arsenic or nitrogen. (c) x+y is the valence of Y where y is equal to or greather than 1. (d) R is an organo group sucj as a cyclic or acyclic hydrocarbon having up to about 6 carbon atoms such as phenyl, ethylene, benzyl, or naphthyl (e) Z is a hydrophyllic group selected from -SO3Na, -NH2, -COOH, quaternary ammonium groups such as N+Me3NO3 Ligands that are especially suitable comprise: : Tris(aminophenyl)phosphine Bis(aminophenyl)phenylphosphine EMI9.1 aminophenyldiphenylphosphine Sodium diphenylphosphinobenzene-m-sulfonate Trisodium-tris(m-sulphophenyl)phosphine Trisodium-tris(m-sulphophenyl)arsine 2-Diphenylphosphinoethyl trimethylammonium nitrate (a.k.a. amphos nitrate) Tris(carboxyphenyl)phosphine Bis(carboxyphenyl)phenylphosphine Carboxyphenyldiphenylphosphine EMI10.1 The various arsine and stibine homologs of the foregoing ligands may also be employed. The ratio of ligand to palladium is from about 2:1 to about 50:1 on a molar basis. The ligand component is added to the catalyst in subsequent telomerization reactions because of loss due to oxidation, product separation and the like. One of the essential features of this embodiment of the present invention is to employ a solvent for the catalyst which is polar such as N,N-dimethylformamide (DMF) or sulfolane. Generally, the polar solvents useful in this respect comprise the N-substituted amides in which the hydrogen of the amido nitrogen is substituted by a hydrocarbyl group e.g. l-methyl-pyrrolidin-2-one; N,N-dimethylacetamide; N,N-diethylacetamide; N-methylpiperidone; 1,5-dimethylpyrrolidin-2-one; l-benzyl-pyrrolidin-2one; N,N-dimethylpropionamidei hexamethylenephosphoric triamide and similar amides that are liquid at room temperature and the like: sulfolane and glycols such as ethylene glycol, propylene glycol, butylene glycol and the like, polyglycols such as polyethylene glycol, polypropylene glycol, polybutylene glycol and mixtures thereof; mono-lower alkyl ethers of alkylene glycols and polyalkylene glycols e.g. methyl ethers of ethylene glycol, propylene glycol, and di-, tri- and tetra-ethylene glycols: dimethylsulfoxide (DMSO) and mixtures thereof. Those solvents having a high dielectric constant are the most preferred polar solvents. The use of a polar solvent facilitates extraction of the product and recovery and recycling of the catalyst. In the present process, it is possible to extract the telomer product from the reaction mixture by using a hydrocarbon which is a solvent for the telomer such as hexane. Any similar hydrocarbon solvent may be employed for example, n-pentane, n-heptane, n-octane, n-nonane, iso-octane, cyclohexane, methylcyclohexane and the like and mixtures thereof. The hydrocarbon solvents therefore comprise any acyclic or cyclic saturated hydrocarbon having up to about 10 carbon atoms. Where the hydrocarbons may be gaseous at room temperature, the separation is conducted at elevated pressures at temperatures less than the critical temperature of the hydrocarbon. Hexane is one of the preferred organic solvents for extraction of the telomer. The extraction of the product leaves the catalyst in the polar solvent for recycling and thus avoids exposing the catalyst to fractional distillation processes typically used for product-catalyst separation. Multiple extractions can be used since in some cases the telomer may also be soluble to some small extent in the polar solvent. Co-current or counter current extraction processes are also utilized for the separation of the catalyst and the telomer. The polar and the hydrocarbon solvents are employed in combination with one another as noted above and are selected so as to form an immiscible pair which is within the ordinary skill of the art. The reaction may be conducted, in this embodiment, at pressures from atmospheric pressure up to about 200 psig and at temperatures from about 600C to abut 800C and especially from about 65 C to about 750C. Independent of which embodiment of the present invention is practiced it has been discovered that the molar ratio of the alkadiene to the organic hydroxy compound influences the yield and selectivity of the reaction and that an excess of the organic hydroxy compound is required to maximize such yields and selectivities. By an excess it is meant that the organic hydroxy compound is present in more than a stoichiometric amount (i.e., greater than one mole of organic hydroxy compound to two moles of conjugated alkadiene). The molar ratio of the aforesaid hydroxy compound to the aforesaid alkadiene is from about 0.6:1 to about 3:1 and preferably from 0.75:1 to about 2.5:1. The organic hydroxy compound specifically may comprise a compound having from 1 to abut 10 carbon atoms and may be a saturated or unsaturated straight chain, branched chain or cyclic compound having at least one hydroxy group. Organic hydroxy compounds in this respect may comprise methanol, ethanol, l-propanol, 2-propanol, 2-butanol, phenol, hydroxycyclohexane, hydroxycyclopentane and the like. The conjugated alkadiene has anywhere from 4 to about 6 carbon atoms and comprises either butadiene, isoprene, chloroprene, piperylene, 1,3-pentadiene and the like. The following examples are given to illustrate the present invention. EXAMPLE 1 A two liter 316 stainless steel, stirred reactor was charged with 0.16gm (0.72 mmole) Pd(OAc)2, 150 ml (150.5 gm or 677 mmole) tetraglyme, 225 ml (178 gm or 5.565 mmole) methanol, 0.942 gm (3.59 mmole) triphenylphosphine (PPh3), 5.06 gm (46.8 mmole) anisole, and was purged 3 times with nitrogen. Anisole is an internal standard for glc analysis. The reactor was charged with butadiene 265 gm (4900 mmole) and the reactor and its contents heated to 750C held for 30 minutes at this temperature and cooled overnight. The contents of the reactor were then discharged under inert atmosphere and distilled by vacuum distillation at 25 mm Hq pressure and 1,392.0 mmoles of 8-methoxy-1,6octadiene were obtained along with 375.6 mmoles of 3-methoxy- 1 , 7-octadiene. The bottoms from the distillation process contained the palladium acetate triphenylphosphine catalyst and were recycled for subsequent telomerization of butadiene and methanol in substantially the same way as described above with the exception that additional triphenylphosphine ligand was added after each recycle of the catalyst and telomerization reaction. The triphenylphosphine added was anywhere from about 0.4 mmole to about 1.2 mmole in 12 recycles depending upon the amount of ligand that was determined to have been lost and substantially the same results were obtained as set forth in the above paragraph. When the catalyst was recycled in subsequent reactions, anisole was not added to the reactor. EXAMPLE 2 The procedure of Example 1 was substantially repeated in seven different telomerization reactions to study the affect of the methanol to butadiene ratio on the telomerization reaction. The results are shown in Table 1. TABLE I METHANOL:BUTADIEIQE RATIO (a) Ethers(C) Seiectivity (c) M:B Ratio (b) (mmoles) Ethers Octatriene 0.4 51 75% 5% 0.653 78 81 6 0.894 112 87 6 1.115 128 89 6.5 1.35 140 96 4 1.58 102 94 4 1.83 62 95 5 (a) 0.287 mmol Pd(OAc)2, 0.574 mmol PPh3, 30 ml dimethyl phthalate, 5 ml anisole, total volume = 165 ml, 600C. (b) Methanol:butadiene molar ratio (as charged to reactor). Total of 130 ml total volume of methanol and liquid butadiene. (c) Based on 15 minutes--0 minutes sample results. The methanol:butadiene stoichiometry is 0.5 and it would therefore be expected that this would be the optimum ratio of these two components in order to obtain methoxyoctadiene. The data in this table, therefore, indicates that the selectivity and ether yield are maximized at a methanol: butadiene molar ratio greater than 1:1 which is unexpected. EXAMPLE 3 The telomerization of butadiene to methoxyoctadiene was also studied in a continuous-stirred tank reactor. The performed complex, PD(OAc)2(PPh3)2, was used as catalyst in dimethyl phthalate-methanol solution. Runs were assumed to have achieved steady-state when two criteria were met: (1) ether production was constant over at least the final three space-times (chemical steady-state) and (2) the dimethyl phthalate pumped in and out of the reactor balanced (physical steady-state) . All such runs met both criteria. In initial studies on temperature effects, highest selectivity to methoxyoctadiene (86%) was obtained at 700C; conversion increased from 168 to 80% as temperature was increased from 600C to 800C (Table II). Since ether yields were equivalent at 700C and 800C (64%) further studies were conducted at 700C. At a ligand to palladium ratio of 2, catalyst decomposition to palladium metal was observed in the reactor and 54% conversion was obtained. At higher ratios the catalyst was stable but conversion decreased above a ratio of 5. Maximum selectivity and conversion were attained at a ratio of 3. The affect of reactant steady-state concentration on reaction rate was also determined in the continuous reactor (Table III). Reaction rates were high in most cases with maximum rate observed at 4.OM butadiene and 3.14M methanol. Butadiene conversion varied from 40 to 55% and ether selectivity varied from 91 to 94% in these runs. These data indicate that as the rate increased, ether selectivity also increased. TABLE II BUTADIENE TELOMERIZATION TEMPERATURE EFFECT AT STEADY @(1) Temp., OC 60 70 80 Ether Selectivity (%) (2) 74 86 79 Product Yield (%) (2) 16 74 80 (1) Space Time = 15 minutes, [Pd = 1.9 X 10-3M, PPh3:Pd = 3. (2) Based on products detected by glc technigues. TABLE III BUTADIENE TELOMERIZATION REACTANT CONCENTRATION EFFECT ON RATE(1) Steady-State Concentration Butadiene Methanol Observed Ethers Space Time Yield m (M) (lbs/ft /hr) 1.60 6.42 29 1.90 6.45 20 2.35 3.92 54 2.40 5.60 56 2.49 6.43 32 2.67 7.90 41 2.93 2.38 42 3.54 5.63 54 4.00 3.14 66 (1) [Pdj = 1.9 X 10 3 M, PPh3/Pd = 3, 700C, 15 minutes space time, 150 ml volume. EXAMPLE 4 The telomerization reaction was also run in a 450 ml plug-flow reactor consisting of 77 ft-5 inches of 1/4 inch I.D. stainless steel tubing immersed in a 73"C water/ethylene glycol bath. To this reactor were fed three streams: a catalyst solution of 0.0063 M Pd(OAc)2(PPh3)2 and 0.0063 M PPh3 in methyl benzoate (containing 9.1 volume percent methanol), fed at an average of 3.4 ml/min.; methanol, fed at an average of 2.3 ml/min.; and butadiene, fed at an average of 5.6 ml/min. The reactor was maintained at 95 psig in order to maintain liquid phase in the reactor. Over an eleven hour period with an average residence time of reactants in the reactor of 40.1 minutes the average yield of 8-methoxy-1,6-octadiene was 57.4% (based on butadiene fed) and 2.5 moles 8-methoxy-1,6-octadiene/liter reactor/hour were obtained. Average selectivity to 8-methoxy-1,6-octadiene was 81.1% (based on butadiene converted). No catalyst decomposition was observed. EXAMPLE 5 To pyrex tube were added 0.0099 g (0.045 mmoles) palladium acetate, 0.049 g (0.134 mmoles) sodium diphenylphosphinobenzene-m-sulfonate, 8 ml methanol and 8 ml butadiene. The tube was sealed and placed in a 750C oil bath for 1.5 hours. Very little butadiene gas remained in the tube and a bright yellow solution with no precipitate was recovered. The product was analyzed by glc on a Silar 10C column and contained 5.6 g, 40 mmoles of methoxyoctadiene. EXAMPLE 6 Butadiene telomerization with methanol, recycle of catalyst. To a pyrex tube was added 0.0103 g. palladium acetate, 0.0500 g of the same ligand employed in Example 5, 8 ml methanol, 5 ml sulfolane and 10 ml butadiene. The tube was sealed and placed in a 700C oil bath for 1 hour. The tube was cooled, vented and a sample taken for glc analysis. The remainder was extracted with 25 ml hexane and the sulfolane layer returned to the tube with 8 ml methanol and 10 ml butadiene was added. The tube was placed in a 700C oil bath for 1.5 hours. The product solution was extracted twice with 25 ml hexane, then 8 ml methanol and 10 ml butadiene were added to the sulfolane layer and the tube placed in a 70"C oil bath for 1.5 hours. The product obtained after each one of the telomerizations was analyzed in the same manner as set forth in Example 5 and each contained 7.5 g or 50 mmoles methoxyoctadiene. EXAMPLE 7 Butadiene telomerization. To a pyrex tube was added 0.0202 g palladium acetate, 0.1033 g of the ligand employed in Example 5, 16 ml methanol, 10 ml sulfolane and 20 ml butadiene. The tube was sealed and placed in a 70"C oil bath for 1.5 hours. The product solution was extracted twice with 25 ml portions of hexane. To the sulfolane layer was added 16 ml methanol and 20 ml butadiene. The tube was sealed and placed in a 700C oil bath for two hours. The product solution (55 ml) was extracted twice with 75 ml portions of hexane. To the sulfolane layer was added 8 ml methanol and 20 ml butadiene. The tube was returned to a 750C oil bath for two hours. The product solution was extracted with 75 ml hexane and the sulfolane layer analyzed by atomic absorption and 0.068 grams Pd (75E of original) was found. Hexane was removed from the telomer extracted in each run and the residue was weighed. In the first run 1.5 g was recovered, in the second 14.9 g and in the third 17.5 g. These residues were analyzed and were found to contain 29.0 g (207 mmoles) methoxyoctadiene. EXAMPLE 8 To a pyrex tube were added 0.206 gms palladium acetate, 0.1030 gms of the ligand employed in Example 5, 16 ml methanol, 10 ml DMF and 20 ml butadiene. The tube was placed in a 700C oil bath for two hours. The product solution was extracted twice with 75 ml hexane. The DMF solution was returned to the tube with 8 ml methanol and 20 ml butadiene. The tube was placed in a 700C oil bath for 2 hours and the product solution extracted twice with 75 ml of hexane in each extraction. The telomer obtained was analyzed by glc in the same manner as in Example 5 and contained 28 grams (200 mmoles) total methoxyoctadiene. The telomers obtained according to the method of the invention may be carbonylated to form unsaturated esters by art know methods. The esters obtained may be hydrogenated and used as lubricants, plasticizers or functional fluids or may be hydrolyzed to form an acid having unsaturated groups. The acid obtained may be incorporated into polyesters manufactured from phthalic anhydride, glycols and maleic anhydride and which are subsequently cross-linked with styrene, all of which is known in the art. The unsaturated acid obtained provides a site along the polyester chain for cross-linking with styrene or equivalent monomers. Although the invention has been described by reference to certain embodiments, it is not intended that the novel method for the telomerization of butadiene and the separation of the telomer be limited thereby but that modifications are intended to be included as falling within the broad scope and spirit of the foregoing disclosure and the following claims. The telomers obtained according to the method of the invention may be carbonylated to form unsaturated esters by art known methods. The esters obtained may be hydrogenated and used as lubricants, plasticizers or functional fluids or may be hydrolyzed to form an acid having unsaturated groups. The acid obtained may be incorporated into polyesters manufactured from phthalic anhydride, glycols and maleic anhydride and which are subsequently cross-linked with styrene all of which is known in the art. The unsaturated acid obtained provides a site along the polyester chain for cross-linking with styrene or equivalent monomers. Although the invention has been described by reference to certain embodiments, it is not intended that the novel method for the telomerization of conjugated alkadienes with an organic hydroxy compound to produce an organooxyalkadiene be limited thereby but that modifications thereof are intended to be included as falling within the scope and spirit of the foregoing disclosure and the following claims.

Claims: WHAT IS CLAIMED IS: 1. A method for the telomerization of a conjugated alkadiene with an organic hydroxy compound to produce an organo-oxyalkadiene, said organic hydroxy compound being employed in an amount in excess of the stoichiometric amount required for the telomerization of said organic hydroxy compound with said conjugated alkadiene, comprising reacting said conjugated alkadiene and said organic hydroxy compound with a catalytically effective amount of a catalyst compound comprising [PdR1] [YRyê]2 where R1 and Rê comprise organo groups, Y is phosphorous or antimony, y is the valence of Y, the ligand:Pd ratio is maintained at from about 10:1 to about 1:1 during the reaction, said reaction being conducted in the substantial absence of oxygen and in the presence of a high boiling organic solvent, the boiling point of said solvent being greater than the boiling point of said organooxyalkadiene; separating said organo-oxyalkadiene from said catalyst and recycling said catalyst for the further telomerization of said conjugated alkadiene with said organic hydroxy compound. 2. The method of Claim 1 where said conjugated alkadiene has from 4 to about 6 carbon atoms. 3. The method of Claim 1 where said conjugated alkadiene is selected from butadiene, isoprene, chloroprene, piperylene and 1,3-pentadiene. 4. The method of any of Claims 1 to 3 wherein said ligand:Pd ratio is maintained at from about 5:1 to about 2:1. 5. The method of any of Claims 1 to 4 where said organic hydroxy compound is selected from 1 to about 10 carbon atom straight chain, branch chain or cyclic compounds having at least one hydroxy group. 6. The method of Claim 5 where said organic hydroxy compound comprises an alkanol. 7. The compound of Claim 6 where said organic hydroxy compound comprises methanol. 8. The method of any of Claims 1 to 7 where R1 comprises an organo carboxylate group and Rê comprises a straight chain, branch chain or cyclic radical having from 1 to about 10 carbons atoms. 9. The method of Claim 8 where R1 comprises a lower alkyl ester group and Rê comprises an aliphatic or cyclic unsaturated group and the molar ratio of said organic hydroxy compound to said conjugated alkadiene is greater than about 1:1. 10. The method of any of Claims 1-9 where said reaction is conducted at a temperature of from about 650C to about 750C at autogenous pressures up to about 200 psig in an inert atmosphere. 11. A method for the telomerization of a conjugated alkadiene with an organic hydroxy compound to produce an organo-oxyalkadiene comprising reacting said conjugated alkadiene with said organic hydroxy compounds in the presence of a catalytically effective amount of a catalyst compound comprising [PdR1] [R2y(R3z) Z) (a) where R1 comprises an organo group (b) R2 is an organo group (c) Y is selected from phosphorous, antimony and arsenic (d) x + y is the valence of Y where y is equal to or greater than 1. (e) R is an organic group (f) Z is a hydrophilic group said reaction being conducted in the substantial absence of oxygen and water and in the presence of a polar solvent to obtain a telomer and extracting said telomer with a hydrocarbon solvent. 12. The method of Claim 11 where said conjugated alkadiene has from about 4 to 6 carbon atoms. 13. The method of Claim 11 where said conjugated alkadiene is selected from butadiene, isoprene, chloroprene, piperylene and 1,3-pentadiene. 14. The method of any of Claim 11-13 where said organo hydroxy compound is selected from straight chain, branch chain or cyclic compounds having up to about 10 carbon atoms and at least one hydroxy. 15. The method of any of Claims 11-14 where said organic hydroxy compound comprises an alkanol. 16. The method of Claim 15 where said organic hydroxy compound comprises methanol. 17. The method of any of Claims 11-16 where R1 comprises an organo carboxylate group, R comprises a straight chain, branch chain or cyclic radical having from 1 to about 10 carbon atoms, R3 comprises a cyclic or acyclic hydrocarbon having up to about 6 carbon atoms. 18. The method of Claim where R1 comprises a lower alkyl ester group, Rê comprises an aliphatic group or a cyclic unsaturated group R comprises an aliphatic group or a cyclic unsaturated group and Z is a group selected from -SO3Na, -NH2, -COOH2 and quaternary ammonium groups. 19. The method of any of Claims 11-18 where said reaction is conducted at a temperature of from about 600 to about 80"C at autogenous pressures up to about 200 psig in a non-oidizing atmosphere under anhydrous conditions. 20. The method of any of Claims 11-19 where said polar solvent is selected from N-substituted amides, glycols, dimethyl sulfoxide and sulfolane and said hydrocarbon solvents contain up to about 10 carbon atoms and are selected from acyclic or cyclic saturated hydrocarbons. 21. The method of any of Claims 11-20 where said catalyst comprises a complex of palladium acetate and sodium diphenylphosphinobenzene-m-sulfonate.

Inventors: HANES, RONNIE M.
Applicants: QUANTUM CHEMICAL CORPORATION (A VIRGINIA CORP.)
Application year: 1986
Main classification: C07C43
IPC codes: C07C41