PRODUCTION OF GRAPHITE INTERCALATION COMPOUND AND DOPED CARBON FILMS

Abstract: The present invention provide a method for preparing graphite intercalation compounds with metal or metal compounds consisting of a simultaneous thermal decomposition of two kinds of starting materials, modified CVD (Chemical vapor deposition) method in which hydrocarbon as a source material for the host graphite and other organometal reagents or metal halides for guest metal species or metal compound are decomposed at a same time in a reactor in order to intercalate the metal species or metal compound into carbon being depositing on the substrate. Further, the present invention provides a doped carbon film which is capable of P-type or N-type according to kinds of dopant species obtained by partial substitution of dopants for carbon atoms which constitute graphite hexagonal net layer during the growth of carbon films, through simultaneous thermal decomposition of two kinds of source materials for carbon films and for dopant to be substituted.

Description: Field of the invention The present invention relates to a process for preparing a graphite intercalation compound and to a doped carbon film. Background of the invention The graphite has such unique properties associated with its layer structure as anisotropies in thermal and electrical conductivity. However, the synthesis of graphite is required extreme conditions of pressure and temperature due to the fact that it has inaccessible melting point and the extremely low sublimation pressure. For example, so called HOPG is prepared by decomposing a gaseous hydrocarbon (e.g. methane) at 2,000°C and then hot pressing the resulting pyrolytic material at still higher temperature. It is now well known that most carbonaceous materials are well graphitized when they are subjected to a heat treatment at higher temperature above 2,500°C. On the other hand, there have been many efforts to prepare pyrolytic carbons, at the low decomposition temperature utilizing dehydrogenation, dehydrohalogenation, decarbonic acid, dehydration of selected hydrocarbons. However, carbon deposits thus obtained are of so poorly ordered state that they are insufficient to provide anisotropic materials or device. There also has been known carbon fiber which is obtained by heat treatment of fibrous polymer compound at high temperature. These carbon fibers are widely used for structural materials, but their unstableness in physical properties debases the usefulness for new electronic materials or device utilizing anisotropic electrical and thermal conductivity due to lack of reproducibility. To modify graphite leads to establishment of a variety degrees of anisotropy. In the first place, there have been studied many kinds of graphite intercalation compounds which are achieved by allowing metal atoms, metal halides or acids to insert between adjacent graphite layers of host graphite material. However the common method such as zone vapor transport technique and electrochemical reaction method as well as other several novel methods, essentially achieved by direct contact of liquid or gaseous species with host graphite, was applied to such limited reagents to be intercalated readily also have low melting point or high vapor pressure. Most of these compounds with graphite elaborated by those ways are not only unstable but also weak to heat. There have not been reported an air stable GTC in which intercalant is fixed firmly nor a practical utilization of the anisotropic properties involved the new electronic device. Doping of the impurities to the graphite is other method to control the degree of anisotropy or the type of conductivity (P-type or N-type). But the fact that graphite is thermodynamically very stable refuses the diffusion technique often used in the fabrication or doped silicon or geranium semiconductor. Accordingly, doped graphite, positive type nor negative type, in which dopant of acceptor type or donor type are diffused into the graphite hexagonal net plane, has not been reported. Summary of the invention The present invention is to provide a method for preparing graphite intercalation compounds with metal or metal compounds. The method consists of simultaneous thermal decomposition of two kinds of starting materials by a modified CVD (Chemical Vapor Deposition) method in which a hydrocarbon material as a source material for the host graphite and other organometal reagents or metal halides for guest metal species or metal compound are decomposed at a same time at a temperature up to 1000°C in a reactor in order to intercalate the metal species or metal compound into carbon being depositing onto a single-crystalline substrate. The simultaneous thermal decomposition is carried out by adding another organometal reagents or metal halide besides hydrocarbon as source materials. Further, the present invention is to provide a doped carbon film wherein at least a portion of carbon atoms which constitute graphite hexagonal net layer is replaced with B or N-atoms, prepared by simultaneously thermally decomposing a hydrocarbon material and a B or N-source material at a temperature up to 1000°C onto a single-crystalline substrate Brief description of the drawings Fig.1 shows a schematical view of the apparatus for preparing the graphite intercalation compound of the present invention. Fig.2 shows a schematical view of the apparatus for preparing the doped carbon film of the present invention. Detailed description of the present invention The hydrocarbon employed in the present invention as a starting material includes organic hydrocarbons and unsaturated hydrocarbons, which are generally decomposed approximately at 1,000°C. Typical examples of the hydrocarbons are cyclohexane, n-hexane, benzene, biphenyl, anthracene, hexamethylbenzene, 1,2-dibromoethylene, 2-butyne, acetylene, diphenylacetylene and the like. A method for supplying the hydrocarbon varies depending on a kind of the hydrocarbon, but includes bubbling method, vaporization method, sublimation method and the like. The supply rate of the hydrocarbon is regulated to a constant value of not more than 10 mmol/hour in order to prepare carbon films with metals. But the supply rates are not limited because they varies depending on a type of the hydrocarbon. Supply rates larger than 10 mmol/hour forms soot-like carbon deposit over the substrate. The carrier gas used to introduce the above mentioned hydrocarbon into the reaction chamber is hydrogen or an inert gas, such as argon, nitrogen. When the bubbling method for supplying the hydrocarbon is employed, hydrogen or argon is preferable for the carrier gas. For the preparation of graphite intercalation compounds or doped carbon films, another kind of starting material beside hydrocarbon is used. Examples of the source material for metal intercalant are such organo metal compounds as tetraphenyl tin and tetraphenyl lead. Examples of the source material for dopant are boron tetrabromide and pyridine. The simultaneous thermal decomposition of these starting materials together with the starting material for carbon film provides metal intercalant or dopant during growth of carbon films. The metal atoms comprised in the organometal compound are believed to be inserted between adjacent graphite layers of carbon films being growing on the substrate. The dopant such as boron (P type) or nitrogen (N type) are partially substituted for carbon atoms which constitute graphite hexagonal not layer during the growth of carbon films on the substrate. The synthesis of air stable GIC in which the graphite is modified by intercalation provides important application due to a variety degree of anisotropy. Further, the present invention makes it possible that dopants are introduced into the graphite hexagonal net plane to provide doped carbon of P-type or N-type. The single-crystalline substrate is deposited includes silicon, sapphire, silicon carbide (including alpha-type and beta-type), boron nitride, kish graphite, high orientation graphite and the like, which is required to have no modification at about 1,000°C. The following examples illustrates the present invention, but they are not construed as limiting the present invention. Example 1 A graphite intercalation compound was deposited by using the apparatus shown in Fig.1. Benzene was purified by vacuum distillation and stocked in a container 21. By opening a cook 24, the vapored benzene were introduced into a quartz reaction chamber 23 through a pyrex glass tube 22. The benzene supply was controlled by a glass capillary 25 which was equipped with the glass tube 22. The vapor of tetraphenyl tin was supplied from a container 26. It was admixed with the benzene vapor in the glass tube 22, and these were introduced into the reaction chamber 23 together. The glass tube 22 was wrapped with a heating tape 27 to keep its temperature. The glass tube 22 was connected with the quartz reaction chamber 23 with a connector 28. The reaction chamber 23 was inserted in a heater 29 and heated to a reaction temperature. A monocrystal substrate was placed on a holder 30 in the reaction chamber. The remain of the vapor which had been introduced into the reaction tube 23 was drained through a drain tube 31. Benzene whose supply rate was controlled by the capillary 25 and tetraphenyl tin were introduced into the reaction chamber 23 which was kept at 900 to 1,000°C by the heater 29. The supply rate of the mixture was kept under a few mmol/hour. The benzene molecules which had been introduced to the reaction tube 23 were thermally decomposed and formed a pyrolytic carbon which had metallic luster on the substrate. At the same time, tetraphenyl tin was also pyrolytically decomposed to insert tin atoms between the graphite-like carbon layers. A graphite intercalation compound is formed. The obtained film of the graphite intercalation copound possessed high crystallinity under the influence of the crystallinity of the substrate and showed the high orientation at a lower temperature than the conventional method. As the supply rate of benzene and tetraphenyl tin was kept constant, the grown film of graphite intercalation compound had a uniform thickness. It provides metal gloss and mirror surface together with the high crystallinity. It has been confirmed by observing the X-ray image of tin using an electron microscopy the tin atoms have existed uniformly in the film of the graphite. By an X-ray diffraction of the obtained film of the graphite intercalation compound, a reflection corresponding to the sum of the atonic radius of tin and distance between the graphite layers was observed in addition to the reflection of the graphite (002). In addition, the graphite intercalation compound could be also formed when tetraphenyl lead was used instead of tetraphenyl tin. Example 2 In Fig.2, the bubbling method using Ar as carrier gas is employed for the preparation of doped carbon films. Benzene is selected as source material for carbon film and pyridine or boron tribromide is used as source material for nitrogen or boron dopant which will give N type or P type conductivity to carbon films. The benzene purified through vacuum distillation is accommodated in a feed stock 11. In addition, starting materials for dopant purified through vacuum distillation is accommodated in a feed stock 11'. Both benzenes and source reagents for dopant are introduced at a same time into the reaction tube 14 through a pyrex glass tube 13 by bubbling method of the two Ar carrier gases which are regulated independently by valves 15. Supply rate of each material is controlled by each flow rate of Ar gas in which each vapor of starting material is saturated. A piece of single-crystalline substrate, placed at the center position on the pedestal 17, is heated up to 1,000°C by the heating furnace 18 around the reaction tube 14. Thus, the mixture of the two source materials led into the reaction tube 14 are decomposed simultaneously at 1000°C Then, the doped carbon films is obtained by partial substitution of dopants for carbon atoms during the growth of carbon films. The existence of dopant element was confirmed by an Auger spectroscopy and the resistivity of the films varies depending on the amount of the dopant being existing.

Claims: A method for preparing a graphite intercalation compound with metal or metal compounds consisting of simultaneous thermal decomposition of two kinds of starting material by a modified CVD method in which a hydrocarbon material as a source material for the host graphite and other organometal reagents or metal halides for guest metal species or metal compound are decomposed at a same time at a temperature up to 1000°C in a reactor in order to intercalate the metal species or metal compound into carbon being depositing onto a single-crystalline substrate. A doped carbon film wherein at least a portion of carbon atoms which constitute graphite hexagonal net layer is replaced with B or N-atoms, prepared by simultaneously thermally decomposing a hydrocarbon material and a B or N-source material at a temperature up to 1000°C onto a single-crystalline substrate.

Inventors: HIGASHIGAKI, YOSHIYUKI, INOGUCHI, TOSHIO, NAKAJIMA, SHIGEO, SUZUKI, TOMONARI, YOSHIMOTO, YOSHIKASU
Applicants: SHARP KABUSHIKI KAISHA
Application year: 1986
Main classification: C01B31
IPC codes: C30B25, C23C16, C01B31