AROMATIC BISMALEIMIDES AND PREPREG RESINS THEREFROM

Abstract: Novel bismaleimides and prepregable resin compositions comprising these bismaleimides and one or more liquid coreactants and optionally, one or more other additives. The novel bismaleimides, such as alpha, alpha-bis-(4-maleimido-phenyl)-meta-diisopropylbenzene, are characterized by the presence of three aromatic rings in the molecular structure and in some respects optimize the desirable characteristics of the one or two and four atomatic ring-containing bismaleimides in resins prepared therefrom.

Description: AROMATIC BISMALEIMIDES AND PREPREG RESINS THEREFROM FIELD OF THE INVENTION This invention relates in general to novel blsmalei ide compositions. In one aspect, this invention is directed to novel aromatic bismaleimides, such as alpha, alpha'-bis (4-maleimidophenyl)-meta-diisopropylbenzene and alpha, alpha-bis(4-malelmidophenyl)-ρara- diisopropylbenzene. In a further aspect, the present invention relates to the use of the novel blsmaleimide compositions in the preparation of prepreg resins and the resins prepared therefrom. BACKGROUND OF THE INVENTION Advanced composites are high strength, high modulus materials which are finding increasing use as structural components in aircraft, automotive, and sporting goods applications. Typically they comprise structural fibers such as carbon fibers in the form of woven cloth or continuous filaments embedded in a thermosetting resin matrix. Most advanced composites are fabricated from prepreg, a ready-to-mold sheet of reinforcement impregnated with uncured or partially cured resin. Resin systems containing an epoxlde resin and aromatic amlne hardener are often used in prepreg since they possess the balance of properties required for this composite fabrication process. State-of-the-art epoxy/carbon fiber composites have high compresslve strengths, good fatigue characteristics, and low shrinkage during cure. However, most epoxy formulations absorb moisture which reduces their high temperature properties. As a result they are not suitable for use at 350°F or greater in a moisture saturated condition. There is therefore a need for resin systems which afford composites which can retain a high level of properties at 3S0°F under such moisture saturated conditions. Most prepreg resins designed for use at 350°F are made by combining bismaleimides of Formula I with liquid coreactants containing other reactive groups such as amines, epoxides, cyanates or comonomers containing -CH « CH-,^C « CH 2 , or -CH«CH- groups which can react or polymerize with the carbon-carbon double bonds of the malelmide groups. In common bismaleimides, R is the residue of an aromatic diamine such as methylene dianiline- or m-phenylene diamine. However prior to the present invention the available aromatic bismaleimides usually contained one, two or four aromatic rings in the structure. Few, if any, bismaleimides have been reported containing three aromatic rings in the molecule, primarily due to a lack of available diamine precursors containing three aromatic rings. Accordingly, it was found that novel bismaleimides could be prepared which contained three aromatic rings In the structure and that these novel bismaleimides, in some respects, optimized the desirable characteristics of both the one or two and four aromatic ring-containing bismaleimides. For example, bismaleimides containing one or two aromatic rings tend to give formulations which are characterized by high water absorption, high Tg and low toughness. Equivalent formulations in which the aromatic nucleus has four, or more aromatic rings, tend to be characterized by lower water absorption, low Tg, and higher toughness. It is desirable to provide resins characterized by high Tg, low water absorption, and high toughness. SUMMARY OF THE INVENTION This invention is directed to: (1) bismaleimides of formula (II), II wherein Ar, R, Rj, and 2 are as hereinafter defined, and (11) prepregable resin compositions comprising II and one or more liquid coreactants and optionally, other additives. These compositions may optionally contain a structural fiber. DETAILED DESCRIPTION OF THE INVENTION As indicated above, the present invention Is directed to novel aromatic bismaleimides of formula (II) and prepreg resins prepared therefrom. The novel bismaleimides are those wherein Ar represents a single or fused aromatic nucleus, preferably a hydrocarbon aromatic nucleus of up to 10 carbon atoms, which may optionally contain one or more R or R. substituents. R and R. Individually represent alkyl or halogen groups, and R. represents alkyl groups of from 1-12 carbon atoms and n has a value of from 0 to 4. Preferred bismaleimides which can be prepared by the teachings of this invention are those wherein Ar represents a substituted or unsubstituted meta-or para-phenylene group and R and R. represent lower alkyl groups of from 1 to 4 carbon atoms or halogen, preferably bromine and chlorine, and R- is methyl. In general formula II, it is also meant to include compositions wherein up to 50% of the malelmlde or substituted malelmide groups have been replaced by other terminal imide groups such as succinlmide, phthallmide, or substituted βuccinimlde, or phthallmide groups. Particularly preferred bismaleimides are those represented by the formulas: III IV Aromatic bismaleimides encompassed by formula II above, also include those wherein Ar represents naphthylene or substituted naphthylene with from 0 to 6 R or R. βubstituents. Also encompassed by (1) are blends of one or more of the bismaleimides of formula II and also blends which Include up to SOI of bismaleimides other than those of formula II. Particularly useful are blends of the bismaleimides of formulas III and IV. As indicated above, the bismaleimides of the present invention are particularly useful in the preparation of prepreg resins having optimal levels of low water uptake, high Tg and good toughness. The preferred bismaleimides also provide a wide range of solubility properties and melting characteristics due to the presence of para- and meta- linkages in the central aromatic nucleus. Such diversity is useful in the formulation of blsmaleimide prepreg resins to impart high temperature performance, moisture resistance, toughness and processability. The bismaleimides of the present Invention can be prepared by condensing certain aromatic diamines, as hereinafter defined with maleic anhydride, substituted maleic anhydrides, or other anhydrides under a variety of conditions. For example, the novel aromatic bismaleimides can be prepared by reacting maleic anhydride with an alpha, alpha'-bis(4-aminophenyl)- meta/para dilsopropyl benzene in accordance with the following equation: wherein R and j are as indicated above. The diamine starting materials of this Invention may be prepared by one or more methods disclosed in the literature. For example, one general route for preparing the dlamines involves the reaction of alpha, alpha' dihydroxy-para- diisopropyl benzene with aniline in the presence of an acidic alumina catalyst and heating the mixture to 160-220°C to give alpha, alpha'-bis(4-amino)- para-dilsopropylbenzene. Details of the method are reported by H.J. Buysch et al. in German Offen. DE 2,111,194 published September 14, 1972. A similar method Is also disclosed for the preparation of substituted aminoaryl compounds and derivatives in Netherlands patent application 6,408,539 of January 20, 1965 by Allied Chemical Corp. Another general method which can also be employed for the preparation of the diamine starting materials Involves the reaction of a dilsopropenylbenzene with an aniline hydrochloride under a nitrogen atmosphere and at temperatures of from 180-200°C as disclosed in U.S. Patent 3,206,152 assigned to Farbenfabriken Bayer, A.G. A further method for preparing the dlamines starting from dilsopropenylbenzene is disclosed in U.S. Patent 3,365,347 which Issued January 23, 1968 to Allied Chemical Corp. - β - Certain of the diamine starting materials are available commercially, such as for example, alpha, alpha•-bis-(4-aminopheny1)-meta- diisopropylbenzene and alpha, alpha•- bls(4-aminoiρhenyl)-para-dilsoρropylbenzene which can be obtained from Mitsui Petrochemicals Industries Ltd, Japan, having an office at 200 Park Avenue, New York, New York 10017. As indicated above, the novel aromatic bismaleimides of the present Invention are particularly suited for use in the preparation of prepregable resin compositions. These compositions are comprised of the novel blsmaleimide and one or more liquid coreactants and optionally, other additives. The liquid coreactants in composition (ii) of this invention include N-vinyl-2-pyrrolldlnone, N-vinyl caprolactam, ethylene glycol dimethacrylate, diethylene glycol dimethacrylate, trimethylolpropane triacrylate, trimethylolpropane trimethacrylate, pentaerythrltol triacrylate, pentaerythritol tetraacrylate, pentaerythrltol tetra ethacrylate, trlallyl isocyanurate, dlallyl phthalate, o,o'-diallyl bisphenol A, Eugenol, trlallyl trimellltate, dlvinyl benzene, dlcylcopentadienyl acrylate, dlcyclopentadlenyloxyethyl acrylate, vinylcyclohexene onoepoxide, 1,4-butanediol divinyl ether, l,4-dihydroxy-2-butene, βtyrene, alpha methyl βtyrene, chlorostyrene, p-phenylstyrene, p-methylεtyrene t-butylstyrene, phenyl vinyl ather, unsaturated polyesters, vinyl ester resins, and the like. These comonomers are characterized by the presence of one or more -CH « CH 2 ,^C « CH 2 , o -CH-CH- roups which can polymerize or react with the malelmide groups of the blsmaleimide. Other liquid coreactants include epoxy resins which contain one or more epoxy groups having the following formula: Q -c'- - The epoxy groups can be terminal epoxy groups or internal epoxy groups. The epoxides are of two general types: polyglycidyl compounds or products derived from epoxidatlon of dienes or polyenes. Polyglycidyl compounds contain a plurality of 1,2-epoxide groups derived from the reaction of a polyfunctional active hydrogen containing compound with an excess of an epihalohydrin under basic conditions. When the active hydrogen compound is a polyhydric alcohol or phenol, the resulting epoxlde resin contains glycldyl ether groups. A preferred group of polyglycidyl compounds are made via condensation reactions with 2,2-bis(4-hydroxyphenyl) propane, also known as bisphenol A, and have structures such as V where n has a value from about 0 to about 15. These epoxides are blsphenol-A epoxy resins. They are available commercially under the trade names such as "Epon 828," "Epon 1001", and "Epon 1009" from Shell Chemical Co., and as M DER 331", and "DER 334" from Dow Chemical Co. The most preferred blsphenol A epoxy resins have an "n" value between ' 0 and 10. Polyepoxides which are polyglycidyl ethers of 4,4'-dihydroxydiphenyl methane, 4,4'-dihydroxydiρhenyl βulfone, 4,4'-biphenol, 4,4'-dihydroxydiphenyl sulfide, phenolphthalein, resorcinol, 4,2'-blphenol, or tris(4-hydroxyphenyl) methane and the like, are useful in this Invention. In addition, EPON 1031 (a tetraglycidyl derivative of l,l,2,2-tetrakis(hydroxyphenyl)ethane from Shell Chemical Company), and Apogen 101, (a methylolated blsphenol A resin from Schaefer Chemical Co.) may also be used. Halogenated polyglycidyl compounds such as D.E.R. 580 (a brominated blsphenol A epoxy resin from Dow Chemical Company) are also useful. Other suitable epoxy resins Include polyepoxides prepared from polyols such as pentaerythrltol, glycerol, butanediol or trimethylolpropane and an v epihalohydrin. Polyglycidyl derivatives of phenol-formaldehyde novolaks such as (VI) where n - 0.1 to 8 and cresol-formaldehyde novolaks such as VII where n ■ 0.1 to 8 are also usable. The former are commercially available as D.E.N 431, D.E.N. 438, and D.E.N. 485 from Dow Chemical Company. The latter are available as, for example, ECN 1235, ECN 1273, and ECN 1299 (obtained from Ciba-Geigy Corporation, Ardsley, NY). Other epoxldized novolaks such as SU-8 (obtained from Celanese Polymer Specialties Company, Louisville, KY) are also suitable. Other polyfunctional active hydrogen compounds besides phenols and alcohols may be used to prepare the polyglycidyl adducts of this invention. They include amines, aminoalcohols and polycarboxyllc acids. Adducts derived from amines Include N,N-diglycidyl aniline, N,N-dlglycldyl toluidine, N.N.N'.N'-tetraglycidylxylylene diamine, (i.e.,VIH) N.N.N' ,N'-tetraglycidyl-bis (methylamino) cyclohexane (I.e. IX) , N,N,N' ,N'-tetraglycldyl- 4,4 , -diaminodiphenyl methane, (i.e. X) N.N.N'.N'-tetraglycidyl-S^'-diaminodiphenyl •ulfone, and N,N'-dimethyl-N,N'-dlglycidyl- 4,4*-diaminodiphenyl methane. Commercially available resins of this type include Glyamine 135 and Glyamine 125 (obtained from F.I.C. Corporation, San Francisco, CA.), Araldlte MY-720 (obtained from Clba Geigy Corporation) and PGA-X and PGA-C (obtained from The Sherwin-Williams Co., Chicago, Illinois). VIII IX (X) Suitable polyglycidyl adducts derived from aminoalcohols include 0,N,N-triglycidyl-4-amino- phenol, available as Araldlte 0500 or Araldlte 0510 (obtained from Ciba Geigy Corporation) and 0,N,N- triglycidyl-3-aminophenol (available as Glyamine 115 from F.I.C. Corporation). Also suitable for use herein are the glycidyl esters of carboxylic acids. Such glycldyl esters Include, for example, dlglycidyl phthalate, diglycidyl terephthalate, dlglycidyl isophthalate, and diglycidyl adlpate. There may also be used polyepoxides such as triglycidyl cyanurates and lsocyanurates, N,N-dlglycidyl oxamldes, N,N'-diglycidyl derivatives of hydantolns such as "XB 2793" (obtained from Ciba Gelgy Corporation), dlglycidyl esters of cycloaliphatlc dicarboxylic acids, and polyglycidyl thloethers of polythiolε. Other epoxy-containing materials are copolymers of acrylic acid esters of glycldol such as glycldyl acrylate and glycidyl methacrylate with one or more copolymerizβble vinyl compounds. Examples of such copolymers are 1:1 styrene-glycidyl methacrylate, 1:1 methyl methacrylate-glycidyl acrylate and 62.5:24:13.5 methyl methacrylate: thyl acrylate.-glycldyl methacrylate. Sillcone resins containing epoxy functionality, e.g., 2,4,6,8,10-pentakis [3-(2,3-eρoxypropoxy)propy1]-2,4,6,8,10-pentamethy1- cyclopentasiloxane and the diglycidyl ether of l,3-bis-(3-hydroxypropyl)tetramethyldisiloxane) are also usable. The second group of epoxy resins is prepared by epoxidatlon of dienes or polyenes. Resins of this type include bis(2,3- epoxycyclopentyl) ether, XIII, Commercial examples of these epoxides include vinylcyclohexene dioxide, e.g., "ERL-4206" (obtained from Union Carbide Corp.), 3,4-epoxycyclohexylmethyl 3,4-epoxycyclohexane carboxylate, e.g., "ERL-4221" (obtained from Union Carbide Corp.), 3,4-eρoxy-6- methylcyclohexylmethyl 3,4-epoxy-6-methylcyclohexane carboxylate, e.g., "ERL-4201" (obtained from Union Carbide Corp.), bis(3,4-epoxy-6-methylcyclo- hexyl ethyl) adlpate, e.g., "ERL-4289" (obtained from Union Carbide Corp.), dlpentene dioxide, e.g., "ERL-4269" (obtained from Union Carbide Corp.) 2-(3,4-epoxycyclohexyl-5,5-βpiro-3,4-epoxy)cyclo- hexanemetadioxane, e.g., "ERL-4234" (obtained from Union Carbide Corp.) and epoxldized poly-butadiene, e.g., "Oxiron 2001" (obtained from FMC Corp.) Other suitable cycloaliphatic epoxides Include those described in U.S. Patents 2,750,395; 2,890,194; and 3,318,822 which are incorporated herein by reference, and the following: f c- > r- Other suitable epoxides include: where n is 1 to 4, m is (5-n), and R is N, halogen or C. to C. alkyl. Also included as epoxy modifers are epoxy-terminated thermoplastic polymers such as epoxy-terminated polysulfone and other similar resins. If epoxy resins are used, it is desirable to add an aromatic diamine to the formulation. The diamine should have a low level of reactivity with epoxy resin and the blsmaleimide at room temperature. Suitable dlamines Include 4,4'-diaminodiphenyl sulfone, 3,3•-diaminodiphenyl sulfone, 3,4'-diaminobenzophenone, 4,4'-diaminobenzophenone, 4,4'-bis(3-amlnophenoxy) diphenyl sulfone, the dlamino starting materials employed in the preparation of the novel bismaleimides of this invention, e.g., α, α'-bis(4-aminodiphenyl)-meta-diisopropyl- benzene, and the like. A stoichlmetry of 0.1 to 1.0 equivalents of -NH per equivalent of (1,2-epoxlde group plus malelmlde group) may be used. Dlamines may also be used even if no epoxy Is used. In this case the dlamines may react during the cure cycle with the bismaleimides. When epoxies •re present, the dlamines may react with either the epoxy or malelmide groups. The composition may additionally contain an accelerator to increase the rate of cure of the epoxy plus amine reaction. These additives may also be used to increase the degree of cure of an epoxy resin in the absence of an amlne hardener. Accelerators which may be used herein include Lewis acids; amine complexes, such as BF 3* monoethylamine, BF 3 *»piperdine, BF.*»2-methylimidazole; amines, such as lmldazole and its derivatives, such as 4-ethyl-2-methyllmldazole, 1-methyllmldazole, 2-methyllmidazole; N,N-dlmethylbenzylamine; acid salts of tertiary amines, such as the p-toluene sulfonic acid:lmldazole complex, salts of trifluoro methane sulfonic acid, such ΛS FC-520 (obtained from 3M Company), organophosphonlum halides and dicyandiamide. If used, the accelerator may be from 1 to 6 percent by weight of the epoxy component. The composition may also contain compounds., with one or more cyanate ester groups. By cyanate ester is meant a compound having at least one cyanate group in its molecule. The cyanate ester is represented by the formula R-(0-C-EN>m wherein R is a residue derived from an aromatic hydrocarbon selected from the group consisting of benzene, biphenyl and naphthalene, or a residue derived from a compound in which at least two benzene rings are bonded to each other by a bridging member selected from the group consisting of wherein R an are t e same or different and each represents a hydrogen atom or an alkyl group containing 1 to 4 carbon atoms, -0-, -CH2θCH2-# -S- -0-C-0-, -0- PP--0O aanndd --00-- j-0-; " T- said aromatic nucleus is optionally substituted by a substituent selected from the group consisting of alkyl groups containing 1 to 4 carbon atoms, alkoxy groups containing 1 to 4 carbon atoms, chlorine and bromine; m is an integer of 1 to 5, and the cyanate group is always directly bonded to the aromatic nucleus. Examples of the cyanate ester Include cyanatobenzene, dicyanatobenzene; 1,3,5-tricyanatobenzene; 1,3-, 1,4-, 1,6-, 1,8-, 2,6- or 2,7-dicyanatonaphthalene; 1,3,6-tricyanatonaphthalene; 4,4-'dicyanatobiphenyl; bis(4-cyanatophenyl)methane; 2,2-bis(4-cyanatophenyl)propane, 2,2-bis(3,5-dichloro-4-cyanatophenyl)ρropane, 2,2-biβ(3,5-dibromo-4-dicyanatophenyl)propane; bls(4-cyanatophenyl)ether; bis(4-cyanatophenyl)thioether; bix(4-cyanatophenyl)sulfone; trls(4-cyanatophenyl)phosphite; trls(4-cyanatophenyl)ρhosphate; bis(3-chloro-4-cyanatophenyl)methane; cyanated novolak;cyanated blsphenol terminated polycarbonate or other thermoplastic oligomer; and mixtures thereof. The above mentioned cyanate esters may be used as mixtures. Prepolymers may be used containing a symmetrical trlazine ring which is prepared by the trimerizatlon of the cyanate groups of the cyanate ester, and which have an average molecular weight of at least 400 but no more than 6,000. Such prepolymers can be prepared by polymerizing the above cyanate esters in the presence of, ΛB a catalyst, an acid such as a mineral acid or Lewis acid, a base such as sodium hydroxide, a sodium alcoholate or a tertiary amine, or a salt such ms sodium carbonate or lithium chloride. The cyanate ester can be used in the form of a mixture of the monomer and the prepolymer. The compositions of this Invention may optionally contain a thermoplastic polymer. These materials have beneficial effects on the viscosity and film strength characteristics of the blsmalelmlde/llquid coreactant mixture and may also have beneficial effects on the properties of reinforced composites made from these resins. The thermoplastic polymers used in this invention include polyarylethers of formulaxillwhich are described in U.S. Patents 4,108,837 and 4,175.175, -HO-R'-O-R"**- XIII wherein R' is a residuum of a dihydric phenol such as blsphenol A, hydroquinone, resorcinol, 4,4-biphenol, 4,4'-dihydroxydiphenyl sulfone, 4,4-'dihydroxy-3,3' 5,5'-tetramethyldiphenyl εulfide, 4,4'-dihydroxy-3' ,3' ,5,5'- tetramethyldiphenyl sulfone and the like. R" is a residuum of a benzenoid compound susceptible to nucleophlllc aromatic substitution reactions such as 4,4'-dichlorodiphenyl sulfone, 4,4'-diflurobenzophenone, and the like. The average value of n is from about 8 to about 120. Other suitable polyarylethers are described in U.S. Patent 3,332,209. Also suitable are polyhydroxyethers of the formula: -*0 - R - O - CH, - CH - CH,*- * n ■*■ OH XIV where R haε the same meaning aε for Formula XI11and the average value of n Is between about 8 and about 300; and polycarbonates such ΛS those based on blsphenol A, tetramethyl blsphenol A, 4,4'-dlhydroxydiphenyl sulfone, 4,4*-dihydroxy-3,3*,5,5•-tetramethy1-dipheny1 sulfone, hydroqulnone, resorcinol, 4,4 , -dihydroxy-3,3\5,5 , -tetramethyl diphenyl sulfide, 4,4'biphenol, 4,4'-dihydroxydiphenyl sulfide, phenolphthalein, 2,2,4,4-tetramethyl-l,3- cyclobutane diol, and the like. Other suitable thermoplastics Include poly(c -caprolactone) ; polybutadiene; polybutadlene/acrylonitrlle copolymers, Including those optionally containing epoxy, vinyl, acrylic, methacrylic, amine, carboxyl, hydroxy, or thiol groups; polyesters, such as poly(butylene terephthβlate) and poly(ethylene terephthalate); polyetherimides such as the Ultem resins (obtained from the General Electric Company); acrylonltrlle/butadiene/styrene copolymers; polyamides such as nylon 6, nylon 6,6, nylon 6,12, and Trogamid T (obtained from Dynamlt Nobel Corporation); pol (amideimides) such as Torlon (obtained from Amoco Chemical Corporation, Napierville, IL); polyolefins; polyethylene oxide; poly(butyl methacrylate); Impact-modified polystyrene; sulfonated polyethylene; polyarylates such as those derived from blsphenol A and Isophthallc and terephthallc acid; poly(2,6-dimethyl phenylene oxide) and Its copolymers; polyvinyl chloride and its copolymers; polyacetals; polyphenylene sulfide and the like. Poly(vinyl acetate) and copolymers of vinyl acetate with other vinyl and acrylic monomers may also be used. Thermoplastics such as low profile additives, for example, LP-40A, may also be used. Alεo suitable are vinyl methyl or vinyl phenyl βlllcone rubbers such as polymers of the formula -R 2 SiO- wherein up to 10X of the R groups are vinyl, the remainder being either methyl and/or phenyl. Particularly suitable are rubber modifiers, such as butadiene polymers and butadiene/acrylonltrile copolymers including those optionally containing terminal and/or pendent amlne, epoxy, carboxyl, hydroxyl, thlol, or unsaturated double bond groups, such as acrylates or methacrylates or vinyls. These are exemplified by the Hycar Reactive Liquid Polymers available from B.F. Goodrich, the 1,2-polybutadiene resins available from Nippon Soda Co., the polybutadiene resinε available from Arco Chemical Co. (as poly-BD resins) and others. Elastomers such as ethylene/acrylic copolymers, exemplified by the Va ac resins available from duPont, and other elastomerlc polymers and copolymers may also be used. The preferred thermoplastics include polysulfones, phenoxy resins, and polyarylates and the butadiene/acrylonltrile copolymers described above. The structural fibers which are uεeful in thiε Invention Include carbon, graphite, glaεε, silicon carbide, poly(benzothiazole), poly(benzimidazole), poly(benzoxazole), aluminum, titanium, boron, and aromatic polyamide fibers. These fibers are characterized by a tensile strength of greater than 100,000 psi, a tensile modulus of greater than two million psi, and a decomposition temperature of greater than 200°C. The fibers may be used in the form of continuous tows (1000 to 400,000 filaments each), woven cloth, whlshers, chopped fiber or random mat. The preferred fibers are carbon fibers, aromatic polya lde fibers, such as Kevlar 49 fiber (obtained from E.I. duPont de Nemours, Inc., Wilmington, DE), and silicon carbide fibers. The compositions of component ii contains 1 to 99 weight percent, preferably 20-98 percent of the blsmaleimide; 1 to about 60 percent, preferably 3 to 40 percent of the liquid coreactant or mixture of coreactants comprising molecules with one or more amino, epoxy, cyanate, vinyl groups such as -CH«CH 2 , ^C-CH 2 , or -CH-CH- and other functionalities as described above; and 1 to about 40 percent, preferably 2 to 30 percent of other additives, such as thermoplastic polymers and other coreactantε. Additional components in the composition Include initiators for vinyl polymerization such as di-t-butyl peroxide, dicumyl peroxide, 1,1-bis (t-butylperoxy)cyclohexane, azo bis-(isobutyronitrile), t-butyl perbenzoate, and the like. The initiator comprises from 0 to 3 percent by weight of the total composition. Inhibitors for vinyl polymerizations may also be used. They Include, hydroqulnone, t-butyl hydroqulnone, benzoquinone, p-methoxyphenol, and 4-nitro-m-cresol. Inhibitors are present In amounts of from 0 to 2 percent by weight of the total composition. When a structural fiber is used, the amount of fiber in the total composition is between about 10 and about 90 percent by weight, preferably between about 20 to about 85 percent by weight. PreImpregnated reinforcement nay be made from the compositions of this invention by combining component 11 with a structural fiber. Preimpregnated reinforcement may be prepared by several techniques known in the art such as wet winding or hot melt. In one method of making impregnated tow or undirectlonal tape, the fiber is passed into a bath of the resin mixture. A non-reactive, volatile solvent such as methyl ethyl ketone may be optionally included in the resin bath to reduce viscosity. After Impregnation, the reinforcement is passed through a die to remove excesε resin, sandwiched between plies of release paper, passed through a set of heated rollers, cooled, and taken up on a spool. It is used within a few days or may be stored for months at 0°F.. Compositeε may be prepared by curing the preimpregnated reinforcement using heat and optionally pressure. Vacuum bag/autoclave cures work well with these compositions. Laminates may v also be prepared via wet layup followed by compression molding, resin tranεfer molding, or by resin injection, as described in European Patent Application 0019149 published November 26, 1980. Typical cure temperatures are 100°F to 600°F, preferably 180 β F to 490 β F. The compositions of this invention may also be used for filament winding. In this composite fabrication process, continuous reinforcement in the form of tape or tow - either previously impregnated with resin or impregnated during winding - is placed over a rotating and removable form or mandrel in a previously determined pattern. Generally the shape is a surface of revolution and contains end closures. When the proper number of layers are applied, the wound form is cured in an oven or autoclave and the mandrel removed. Tacky drapable prepreg can be obtained with a wide variety of compositions. Long prepreg shelf lives can be obtβined-typlcally one to four weeks. The compositions of this invention may be uεed aε matrix reεins for composites, high temperature coatings, and adheslves. When reinforced with structural fibers, they may be used aε aircraft parts such as wing skins, wlng-to-body fairings, floor panels, flaps, radomes; as automotive parts, such as driveshafts, bumpers, and springs; and as presεure veεsels, tanks and pipes. They are also suitable for protective armor on military vehicles and sporting goods applications such as golf shafts, tennis rackets, and fishing rods. In addition to structural fibers, the composition may also contain paniculate fillers such as talc, mica, calcium carbonate, aluminum trihydrate, glass mlcroballoons, phenolic thermospheres, and carbon black. Up to half of the weight structural fiber in the composition may be replaced by filler. Thlxotropic agents such as fumed silica may also be used. EXAMPLES The following examples serve to give specific illustrations of the practice of this invention but they are not Intended in any way to limit the scope of this invention. Example 1. Preparation of the blsmaleimide of formula III. α. α'-Bis(4-malelmidopheny1)-meta-dlisopropylbenzene A 3 L 4-neck flask equipped with an overhead stirrer, a nitrogen gas dispersion tube and outlet, an addition funnel, and a thermometer with a temperature controller was charged with 444 ml acetone and 98.2 g maleic anhydride. The mixture was εtirred to dissolve the maleic anhydride and sparged with nitrogen for 15 minutes. A solution of 150 g of α, α'-bis (4-aminophenyl)-meta- diiεopropylbenzene in 444 ml acetone was added over 30 minuteε during which time the reaction mixture formed an opaque, light yellow slurry. The slurry was εtirred and heated at 40°C for one hour. The reaction mixture waε then charged with 4.7 g of MgCl 2 »6H 2 0, 23 ml triethylamine, and 238 g of acetic anhydride which was added over 15 " ' minutes. Stirring and heating at 40°C were continued for three hours and then the heat was turned off while stirring continued for 16 hours. About 20 minutes after the end of the acetic anhydride addition, the slurry changed to a clear gold solution which grew darker with time. After diluting the reaction mixture with 600 ml of dichloromethane, it was washed (12 L separatory flask) with 5 x 1 L of .25M potassium carbonate, once with dilute brine, twice with water and again with brine. The methylene chloride solvent was then removed under vacuum and the residue was taken up in 4 L of acetone and then coagulated in 9 to 10 parts water per portion of acetone solution. The precipitate was collected and dried in an oven under vacuum. Over a period of two days the oven heat was gradually increased until the material formed a brittle melt (- 70°C). The proton NMR was consistent with the expected structure. LC analysis showed one major product with two minor impurities. Example 2. Preparation of the Blsmaleimide of Formula IV. a. tt'-Bls (4-malelmidophenyl)para-dlisopropylbenzene A 5 L 4-neck flask equipped with an overhead stirrer, a nitrogen gas dispersion tube and outlet, an addition funnel, and a thermometer with a temperature controller was charged with 880 ml acetone and 166.7 g maleic anhydride. The mixture was stirred to dissolve the maleic anhydride and then sparged with nitrogen for 15 minutes. A solution of 250 g of α, o'-Bis (4-aminophenyl)- para-dilεopropylbenzene in 1680 ml acetone was added over 30 minutes during which time the reaction mixture formed an opaque yellow slurry. The slurry was stirred and heated at 40°C for one hour. The reaction was then charged with 8.03 g of MgCl 2 *6H 2 0, 39 ml triethylamine, and 404 g of acetic anhydride which was added over 15 minutes. Stirring and heating at 40*C were continued for about 20 hours during which time the slurry changed to green-brown and then to an off-white color. The mixture was diluted with 4.8 L of dlchloromethane and then washed (12 L separatory flask) with 7 x 2 L of .25 M potassium carbonate. Salt was added to some washes to improve phase separation. After 2 additional 2 L washs with water, the organic phase was coagulated in 10 parts of lsopropanol. The precipitate, a fine yellow powder, was collected and dried at - 60°C under vacuum. The dried product (238 g) had a melting point of about 246°C. The proton NMR was consistent with the expected structure. LC analysis showed one major product with two minor impurities. Example 3. Preparation of Blsmaleimlde/Coreactant Casting A mixture of 6.2 R of the blsmaleimide from Example 1 and 3.8 g of o,o'-diallylbiεphenol A was blended in a 25 ml flask on a rotary evaporator at 125°C for 10 minutes to form a transparent gold solution. This was poured Into a small casting frame (~ 4" x 4" glasε plateε with a 1/16" Teflon spacer frame) and cured with the following schedule. The casting was cured by heating from 25°G to 79 β C at 1.5 β C/min.; holding at 79 β C for 2 hours; heating from 79 β C to 177 β C at 1.5 β C/min.; holding at 177 β C for 4 hours, heating to 246 β C at l β C/min.; holding at 246°C for 4 hours; and then cooling to room temperature at 1.5°C/min. Other cure schedules could also be used having shorter or longer hold periods at these or other temperatures. The transparent, dark gold casting was cut into DMA (dynamic mechanical analysis) test specimens which showed a Tg of 237°C when tested at a heating rate of 5°/mlnute. After soaking in water at 160°F for two weeks, the casting samples absorbed 2.21 water. Similar results were obtained with cure schedule of Example 4. Example 4. Preparation of Blsmalelmide/Coreactant Casting. A mixture of 5.0 g of the blsmaleimide from Example 2 and 5.0 g of o, o'-dlallylbisphenol A was blended in a 25 ml flask on a rotary evaporator at 140°C for about 15 minutes and then poured into a small frame as in Example 3 and cured with the following schedule. The casting was cured by heating from 25°C to 100 β C at l β /min., holding at 100°C for 1 hour, heating from 100°C to 180°C at l°/min., holding at 180 β C for 3 hours, heating from 180 β C to 240°C at l°/min., holding at 240°C for 5 hours and cooling to room temperature at 3°/min. The transparent, dark casting was evaluated as in Example 3 and showed a Tg of 227°C and a water absorption of 2.2%. Control Examples Control examples prepared in a similar manner showed the above castings to exhibit a low level of water absorption relative to that found with lower molecular weight (i.e., 2 aromatic rings) bismaleimides. For example, a casting prepared from 5.4 parts methylene dlanlline blsmaleimide and 4.6 partε dlallylbisphenol A had a Tg of 285°C and absorbed 3.7% water. A similar casting containing oxydianlline blsmaleimide had a Tg of 280°C and absorbed 3.91 water. Controls also showed significantly lower Tg values when higher molecular weight (I.e., four aromatic rings) bismaleimides were used. For example, a casting based on 6.6 parts of 4,4'-bis(3-maleimidophenoxy) dlphenylsulfone had a Tg of only 213 β C even after post-curing at 275°C for 3 hours. This casting had a water absorption of 1.91. The data from Examples 3, 4 and the Control Examples are set forth in Table I below. Table I Com p arative Pro p erties of Multi-ring Bismaleimides Weight Rings Weight _ %H2θ I BMI in BMI Diluent* Tg.°c) Absorbed MDA a 5.4 2 4.6 285 3.7 ODA 5.4 4.6 260 3.9 BAM C 6.2 3 3.8 237 2.2 BAP d 5.0 3 5.0 227 2.2 SED-M e 6.6 4 3.4 213 1.9 a. Methylene dianiline biεmaleimide. b. Oxydianiline biεmaleimide. c. ot , -A '-Biε(4-maleimidediphenyl)-meta- diisopropylbenzene. d. βC, '-Bis(4-maleimidophenyl)-para- diisopropylbenzene. e. 4,4'-Bis(3-maleiπ.idophenoxy)diphenylεulfone f. o,o'-diallyl biεphenol A g. 2 weeks in 160 β F water. It is evident from the data set forth in Table I that bismaleimides containing three aromatic rings provide formulations with lower water absorption than bismaleimides continuing two aromatic rings and also higher Tg values than bismaleimides having four aromatic rings. Such a balance of properties is desirable. Example 5 - Prepreg Composition A carbon fiber prepreg is prepared from the resin of Example 4 by coating the resin on release paper at elevated temperatures to provide a suitable viscosity and contacting two plies of the coated paper with a ribbon of carbon fiber tows in a prepreg machine. In the prepreg machine, the sandwich of fiber and coated release paper is passed over a series of heated rollers to melt the resin into the fibers. The fiber is a polyacrylonltrile-based fiber customarily used in the preparation of high performance carbon fiber composites. Although the Invention has been illustrated by the foregoing examples, it is not to be construed as being limited to the materials employed therein, but rather, the invention relates to the generic area aε hereinbefore disclosed. Various modifications and embodiments thereof can be made without departing from the spirit and scope thereof.

Claims: WHAT IS CLAIMED IS: 1. A blsmaleimide of the formula: II wherein Ar represents a single or fused aromatic nucleus which may optionally contain one or more R or R. groups; R and R. individually represent alkyl or halogen groups; R. represents an alkyl group of from 1 to 12 carbon atoms; and n has a value of from 0 to 4. 2. A blsmaleimide as defined in claim 1 where Ar is phenylene, and R and R. are hydrogen. 3. A blsmaleimide as defined in claim 1 where Ar is meta-phenylene. 4. A biεmaleimide aε defined in claim 1 where Ar is para-phenylene. 5. A biεmaleimide as defined in claim 1 which consists of a mixture of the bismaleimideε of claim 3 and claim 4. 6. A blsmaleimide as defined in claim 1 of the following formula: III 7. A blsmaleimide as defined in claim 1 of the following formula: IV 8. A blsmaleimide as defined in claim 1 which consists of a mixture of the bismaleimides of claim 6 and claim 7. 9. A blsmaleimide as defined in claim 1 in which up to 50% of the malelmide or substituted malelmlde groups have been replaced by the following terminal Imide groups: succlnlmide, phthallmide, and substituted succlnimide, and phthallmide. 10. A prepregable resin composition comprising the blsmaleimide of claim 1 and one or more liquid coreactants. 11. A prepregable resin composition comprising the blsmaleimide of claim 1, a second blsmaleimide and one or more liquid coreactants. 12. A prepregable resin as defined in claim 11 wherein said bismaleimide iε selected from the group consisting of methylene diphenylene blsmaleimide, meta-phenylene blsmaleimide, 4,4-biε(3-maleimldophenoxy)diρhenylsulfone, or 4,4'-bis(4-malelmidophenoxy)diphenylisopropylidene. 13. The prepregable reεln aε defined in claim 10 which contains one or more liquid coreactants containing at least one -CH-CH-, ^C-CH-, or -CH-CH- groups. 14. The resin of claim 13 which Includes one or more liquid coreactants selected from N-vinyl-2-pyrrolidinone, N-vinyl-caprolactam, ethylene glycol dlmethacrylate, diethylene glycol dimethacrylate, trimethylolpropane triacrylate, trimethylolpropane trimethacrylate, pentaerythrltol triacrylate, pentaerythrltol tetracrylate, pentaerythrltol tetramethacrylate, trlallyl lsocyanurate, diallyl phthalate, 0,0'-dlallyl blsphenol A, Eugenol, trlallyl trlmellltate, divinyl benzene, dicyclopentadlenyl acrylate, dicyclopentadlenyl oxyethyl acrylate, vinylcyclohexene oonoepoxide, 1,4-butanedlol dlvinyl ether, 1,4-dihydroxy-l-butene, βtyrene, alpha methyl styrene, chlorostyrene, p-phenylstyrene, p-methylstyrene, t-butylstyrene, phenyl vinyl ether, unsaturated polyesters, and vinyl ester resins. 15. The resin aε defined in claim 10 which contalnε an epoxy reεln. 16. The reεin aε defined in claim 15 wherein the epoxy reεin is bls(2,3-epoxycyclopentyl) ether or an adduct of this compound with ethylene glycol. 17. The resin as defined in claim 15 wherein the epoxy resin Is of the following structure: where n has a value from about 0 to about 15. 18. The resin aε defined in claim 15 wherein the epoxy resin is a phenol-formaldehyde ήovolak of the following formula: wherein n ■ 0.1 to 8 and R ■ hydrogen. 19. The resin as defined in claim 15 wherein the epoxy resin is a cresol-formaldehyde novolak of the following formula: wherein n 0.1 to 8 and R is CH 3 * 20. The reεin aε defined in claim 15 wherein the epoxy reεin is N.N.N'N'-tetraglycidyl 4,4'-diamlnodiphenyl methane. 21. The resin as defined in claim 15 wherein the epoxy resin is N,N,N' ,N'-tetra- glycidylxylylene diamine. 22. The resin as defined in claim 15 wherein the epoxy resin is N,N-diglycldyl toluidine or N,N-diglycidyl aniline. 23. The resin as defined in claim 15 wherein the epoxy resin is diglycidyl iβophthalβte or diglycidyl terephthaiate. 24. The resin aε defined in claim 15 wherein the epoxy reεin is 0,N,N-triglycidyl-4-amino- phenol or 0,N,N-triglycidyl-3-aminophenol. 25. The reεin aε defined in claim 15 wherein the epoxy reεin iε 3,4-epoxycyclohexylmethyl- 3,4-epoxycyclohexane carboxylate. 26. The resin as defined in claim 15 wherein the epoxy resin Is the triglycldyl ether of tris(4-hydroxypheny1)methane. 27. The resin as defined in claims 10, 13, or 15 which includes an aromatic diamine. 28. The resin as defined in claim 27 in which the diamine iε selected from 4,4'-diamlnodi- phenyl methane, meta-phenylenediamine, 4,4'-diaminodiphenyl ether, 3,4'-diaminodlphenyl ether, 4,4'-dlaminodiρhenyl sulfone, 3,3'-diaminodl- phenyl sulfone, 3,4-'diaminobenzophenone, 4,4'-diaminobenzophenone, 4,4'-bis(3-aminophenoxy) diphenyl sulfone, α, α'-bis(4-aminophenyl)-para- diisopropylbenzane, and α, α'-blβ(4-amlnophenyl)- meta-dllβopropylbenzane. 29. The resin as defined in claims 10, 13, or 15, which includes a compound containing one or more cyanate ester groups. 30. The blsmaleimide as defined in claim 29 in which the cyanate ester compound Is 2,2-bls(4-cyanatopheny1)propane. 31. The blsmaleimide of claims 10, 13, or 15, which contains a thermoplastic polymer. 32. The biεmaleimide as defined in claim 31 wherein the thermoplastic polymer iε selected from one or more of a poly(aryl ether), a polyhydroxyether, a polycarbonate, a poly(c-caprolactone), a polybutadiene/ acrylonltrile copolymer, a polyester, an acrylonltrile/butadlene/styrene copolymer, a polyamide, a poly(amlde imlde), a polyolefin, a polyethylene oxide, a polybutyl methacrylate, an impact-modified polystyrene, a sulfonated polyethylene, a polyarylate, ρoly(2,6-dimethyl phenylene oxide) and its copolymers, polyvinyl chloride and its copolymers, polyphenylene sulfide, polyacetals, pol (vinyl acetate) and Its copolymers, and vinyl methyl or vinyl phenyl silicon rubbers. 33. The blsmaleimide as defined in claim 32 wherein the thermoplastic polymer is a polysulfone. 34. The blsmaleimide as defined in claim 32 wherein the thermoplastic polymer is a polyhydroxyether. 35. The biεmaleimide as defined in claim 32 wherein the thermoplastic polymer is a polycarbonate. 36. The blsmaleimide as defined in claim 32 wherein the thermoplastic polymer is a polyetherlmide. 37. The blsmaleimide as defined in claim 32 wherein the thermoplastic polymer is a polyarylate. 38. The biεmaleimide aε defined in claim 32 wherein the thermoplastic polymer is a butadiene polymer or acrylonltrile/butadiene copolymer which may contain vinyl, amlno, epoxy, carboxy, or hydroxy functional groups in the terminal or pendent positions. 39. The resin of claims 10, 13, or 15, which contains up to 40% of an additional blsmaleimide which Is different from that of claims 1 to 7. 40. The resin of claims 10, 13, 14, or 15, which contains a free radical inhibitor, a free radical Initiator, or other accelerators, or fillers. 41. The resin as defined in claims 10, 13, 14, or 15, which contains a structural fiber selected from carbon, graphite, glass, silicon carbide, poly(benzothiazole), poly(benzimidazole), poly(benzoxazole), aluminum, titanium, boron, and aromatic polyamIdes. 42. A prepreg comprising: (a) a blsmaleimide of formula (II), of claim 1 wherein Ar, R, and R., and R- and n are as Indicated therein; (b) one or more liquid coreactants, and optionally other additives, and (c) a structural fiber. 43. A composite comprising (1) a matrix resin comprising: (a) blsmaleimide of formula (II) of claim 1 wherein Ar, R, R. , R 2 , and n are as indicated therein; (b) one or more liquid coreactants, and optionally other additives, and (c) a structural fiber.

Inventors: DOMEIER LINDA ANN, DOMEIER, LINDA, ANN
Applicants: AMOCO CORP, AMOCO CORPORATION
Application year: 1986
Main classification: C07D207
IPC codes: C07D207, C08F283, C08G59, C08G73, C08J5, C08L33, C08L35