PRODUCTION OF POLYESTER AND TONER CONTAINING THE SAME

Abstract: A polyester to use for an electrophotographic toner composition is obtained by copolycondensation between (a) a diol component of polyoxyalkylene-bis(4-hydroxyphenyl)-­ propane and (b) an acid component, improved by incorporat­ ing into the acid component a copolymer of styrene or a derivative thereof and a carboxylic vinlyl monomer. Instead a copolymer of an unsaturated aliphatic hydrocarbon and an unsaturated carboxylic acid and a polymer and copolymer of an unsaturated carboxylic acid may be used. The toner is improved in prevention of off-set in the fixation step.

Description: The present invention relates to a process for producing a binder resin. More particularly, the invention relates to a process for producing a binder resin useful particularly for the production of a developer composition for developing an electrostatic image in electrophotography, electrostatic recording and electrostatic printing. A conventional electrophotographic process comprises the steps of uniformly charging a photoconductive insulating layer, then exposing this layer to an image, eliminating an electric charge from the exposed part to form an electric latent image, applying a colored, charged, fine powder called a toner to the latent image to visualize the same (developing step), transferring the obtained visible image onto a transfer material such as a transfer paper (transfer step) and permanently fixing the image by heating, compression or other fixing method (fixing step), for example as described in the specifications of U.S. Patents Nos. 2,297,691 and 2,357,809. Thus, the toner must have functions required not only in the developing step but also in the transferring and fixing steps. Generally, a toner deteriorates as a result of mechanical friction due to shear or impact forces whilst thousands to tens of thousands of copies are produced by a mechanical treatment carried out in a developing device. Though the problem of the deterioration of the toner can be solved by using a high-molecular weight tough resin resistant to the mechanical friction, such a resin generally has a high softening point and, therefore, sufficient fixing is impossible by a non-contact fixing method such as an oven fixing method or infra red radiant fixing method due to the poor thermal efficiency of such methods. Further, when said resin is used in a contact fixing method such as a conventional heat roller fixing method, a high temperature is required of the heat roller so as to effect the fixing sufficiently and, therefore, problems such as damage to the fixing device, curling of the paper and increase in energy consumption are posed in this method, since a high thermal efficiency is obtained and, in addition, when such a resin is used, the efficiency of production of the toner by finely pulverizing the resin is substantially reduced. Thus, a binder resin having an excessively high degree of polymerization and softening point cannot be used. Though the heat roller fixing method has been employed widely, ranging from low-speed to high-speed fixing systems, since a remarkably high thermal efficiency is obtained because the surface of the heat roller is pressed against a toner image surface of the sheet to be fixed, a so-called offset phenomenon is caused when the heat roller is brought into contact with the toner image surface, since the toner adheres to the surface of the heat roller and it is then transferred onto the subsequent transfer paper. To prevent this phenomenon, the surface of the heat roller is treated with a material having excellent releasing properties such as a fluororesin and, in addition, a releasing agent such as silicone oil is applied to the surface of the heat roller to inhibit the offset phenomenon completely. However, this process in which silicone oil, etc. are used is not preferred, since it necessitates a large and costly fixing device and a complicated and potentially-troublesome operation. Though a process for preventing the offset phenomenon by widening the molecular weight distribution of the binder resin is disclosed in the specifications of Japanese Patent Publication No. 6895/1980 and Laid-Open No. 98202/1981, the degree of polymerization of the resin is increased and a high fixing temperature is necessitated in this process. Though a further improved process for preventing the offset phenomenon by asymmetrizing or crosslinking the resin is disclosed in the specification of Japanese Patent Publication No. 493/1982 and Laid-Open Nos. 44836/1975 and 37353/1982, the problem of the fixing temperature is not solved yet. The practical operation temperature ranges from the minimum fixing temperature to a hot offset temperature, since the minimum fixing temperature lies between a cold offset temperature and the hot offset temperature. Therefore, by lowering the minimum fixing temperature as far as possible and elevating the minimum hot offset temperature as far as possible, the practical fixing temperature can be lowered and the practical operation temperature range can be widened; in addition, energy saving, fixing at a high speed and prevention of curling of the paper can be attained. Further, double copy can be effected by this technique without causing any trouble to obtain advantages such as provision of an intelligent copier and mitigation of the accuracy and allowance of temperature control of the fixing device. Thus, resins and toners having excellent fixing properties and offset resistance are still sought after. Though it is known that when a styrene binder resin is used, a paraffin wax, a low-molecular polyolefin or the like is used as an offset inhibitor for attaining the above-mentioned purposes as disclosed in the specifications of Japanese Patent Laid-Open Nos. 65232/1974, 28840/1975 and 81342/1975, this process also has problems in that the intended effect cannot be obtained when the amount of the offset inhibitor is insufficient and the deterioration of the developer is accelerated when that amount is excessive; and where a polyester resin is used, said offset inhibitor is substantially ineffective and when it is used in a large amount, the deterioration of the developer is also accelerated. Improved polyester resins have been disclosed in EP-A-55449; GB-A-2082788; EP-A-10801; and in JP-A-59 228660. However, further improvements in polyester binder resins for use in toner compositions are still sought. Though polyester resins have essentially excellent fixing properties and sufficient fixing is possible even by a non-contact fixing process as disclosed in the specification of U.S. Patent No. 3,590,000, they could not be used easily in the heat roller fixing process because of the offset phenomenon. As described in the specifications of Japanese Patent Laid-Open Nos. 44836/1975, 37353/1982 and 109875/1982, even when the offset resistance of the polyester resin is improved with a polybasic carboxylic acid, the offset resistance is still insufficient for practical use or, if it is sufficient, the inherent low-temperature fixing property of the polyester resin is sacrificed, the pulverizability thereof in the toner-forming step is very poor and problems are posed also in the production of the developing agent. The present invention is intended to satisfy the above-mentioned requirements. One object of the invention is to provide a binder resin for a developer, which exhibits excellent kneadability and pulverizability in the production of the developer and which can be fixed at a low fixing temperature while offset is prevented without necessitating the application of an offset inhibitor in the heat roller fixing process. Another object of the invention is to provide a binder resin for a blocking-free developer having a high fluidity and good resistance to deterioration. The invention has another object which is to provide a binder resin to use as a toner in dry development in electrophotography which resin can be charged with a negative, strong, uniform charge. An additional object of the invention is to provide a process for producing a binder resin to be used in the production of a developer for forming a transparent, clear, colored image. A further object of the invention is to provide a process for producing a binder resin to be used in the production of a developer capable of inhibiting adhesion to a file in which it is kept in and for preventing the image from migrating to a film. The invention provides a process for producing a polyester by copolycondensing: (a) a diol component of the formula (I): in which R is an ethylene or propylene group and x and y are each an integer of at least 1, the total of x and y being 2 to 7 on the average, with (b) an acid component of a polycarboxylic acid, an anhydride thereof or a lower alkyl ester thereof, containing (II) a polycarboxylic copolymer of a styrene compound selected from alpha-methylstyrene and a compound of the formula (IIa): in which R1 is hydrogen or a hydrocarbon group having 1 to 3 carbon atoms, and a carboxylic group-having vinyl monomer of the formula (IIb), an anhydride thereof or a lower alkyl ester thereof: in which R2 is hydrogen, methyl or carboxyl group and R3 is hydrogen or a methyl group. In the invention, the term. "a lower alkyl group" means an alkyl group which preferably has 1 to 4 carbon atoms. In addition, the invention provides a polyester which has been obtained in the above defined preparation process. The polyester is useful as a binder resin for the electrophotographic toner. Accordingly the toner composition is also covered in the invention. Examples of the diol components (a) in the present invention include polyoxypropylene (2.2)-2,2-bis(4-hydroxyphenyl) propane, polyoxypropylene-(3,3)-2,2-bis(4-hydroxyphenyl)propane, polyoxyethylene(2.0)-2,2-bis(4-hydroxyphenyl)propane, polyoxypropylene(2.0)-polyoxyethylene(2.0)-2,2-bis(4-hydroxyphenyl)propane and polyoxypropylene(6)-2,2-bis(4-hydroxyphenyl)propane. If necessary, the polyol component may contain up to about 10 molar %, based on the polyol component, of other polyols such as polyoxypropylene(12)-2,2-bis(4-hydroxyphenyl)propane, polyoxyphenylethylene(3)-2,2-bis(4-hydroxyphenyl)propane, ethylene glycol, diethylene glycol, propylene glycol, triethylene glycol, tetramethylene glycol, pentamethylene glycol, hexamethylene glycol, heptamethylene glycol, octamethylene glycol, nonamethylene glycol, decamethylene glycol, neopentyl glycol, p-xylylene glycol, m-xylylene glycol, 1,4-cyclohexanedimethanol, 1,4-cyclohexanediethanol, 1,4-cyclohexanediol, 1,3-cyclohexanedimethanol, glycerol, polyoxyethylene(6) glycerol and polyoxypropylene(12) pentaerythritol. However, when a compound having a high steric hindrance, such as polyoxyphenylethylene-(3)-2,2-bis(4-hydroxyphenyl)propane, is used, the reaction does not proceed easily and when a resin produced from a highly hydrophilic polyol such as glycerol or polyoxyethylene(6) pentaerythritol is used, the image-forming capacity of the developer is reduced. Thus, a care should be taken of this point. The compounds of the formula (IIa) herein include, for example, styrene, methylstyrene, ethylstyrene and propylstyrene. Examples of the compounds of the formula (IIb) herein include maleic, fumaric, acrylic and methacrylic acids. They may be in the form of either their anhydrides or lower alkyl esters. The term "lower alkyl group" herein indicates that the alkyl group in the alkyl ester has such a number of carbon atoms that it does not disturb the copolymerization of the compound of the formula (IIa) with the compound of the formula (IIb). In the copolymerization, the compound of the formula (IIa) is used in an amount of preferably 1 to 5 mol per mol of the compound of the formula (IIb). Examples of the polybasic carboxylic acids (II) used in the present invention are shown below; and it is to be noted that those in which the carboxyl group is partially replaced with an alkyl ester group in order to control the reaction to obtain the intended properties may also be used: These polybasic carboxylic acids (II) or their anhydrides or lower alkyl esters are contained in the acid component in an amount of preferably 0.05 to 70 molar %. The acid component of the present invention may contain an alkyl- or alkenylsuccinic acid of the following general formula (III) or its anhydride or lower alkyl having 1 to 4 atoms ester: wherein R₉ represents an alkyl or alkenyl group having 4 to 18 carbon atoms. Examples of the alkyl- or alkenylsuccinic acids include n-dodecenyl-, isododecenyl-, n-dodecyl-, isododecyl-, n-octyl-, n-octenyl- and n-butylsuccinic acids. By using the alkyl- or alkenylsuccinic acid, the minimum fixing temperature can be lowered without lowering of the offset-causing temperature. When the amount of the alkyl- or alkenylsuccinic acid is insufficient, the intended effect cannot be obtained sufficiently and when it is excessive, Tg is lowered to cause caking of the toner and to make the control of the reaction difficult. Therefore, the amount of said compound is preferably 1 to 50 molar % based on the acid component. The dibasic carboxylic acids other than the alkyl or alkenylsuccinic acids usable in the present invention include, for example, fumaric, maleic, succinic, adipic, suberic, azelaic, sebacic, terephthalic, isophthalic and 2,6-naphthalenedicarboxylic acids. To further improve the fixability, (1) a liquid polybutadiene having a carboxyl group in its free form or in the form of an acid anhydride or lower alkyl ester or a tetracarboxylic acid having an alkylene or alkenylene group may be incorporated in the developer composition as the acid component. Examples of preferred tetracarboxylic acids include: (1) 4-neopentylidenyl-1,2,6,7-heptanetetracarboxylic acid, (2) 4-neopentyl-1,2,6,7-heptene (4)-tetracarboxylic acid, (3) 3-methyl-4-heptenyl-1,2,5,6-hexanetetracarboxylic acid, (4) 3-methyl-3-heptyl-5-methyl-1,2,6,7-heptene(4)-tetracarboxylic acid, (5) 3-nonyl-4-methylidenyl-1,2,5,6-hexanetetracarboxylic acid, (6) 3-decylidenyl-1,2,5,6-hexanetetracarboxylic acid, (7) 3-nonyl-1,2,6,7-heptene(4)-tetracarboxylic acid, (8) 3-decenyl-1,2,5,6-hexanetetracarboxylic acid, (9) 3-butyl-3-ethylenyl-1,2,5,6-hexanetetracarboxylic acid, (10) 3-methyl-4-butylidenyl-1,2,6,7-heptanetetracarboxylic acid, (11) 3-methyl-4-butyl-1,2,6,7-heptene(4)-tetracarboxylic acid, and (12) 3-methyl-5-octyl-1,2,6,7-heptene(4)-tetracarboxylic acid. The binder resin obtained by the process of the present invention has a softening point (as determined by ring-and-ball method according to ASTM E-28-51T) of preferably 90 to 180°C. The binder resin obtained by the process of the present invention is used in the production of a toner for the electrostatic development by a usual process. More particularly, a colorant including carbon black produced by thermal black, acetylene black, channel black, furnace black or lamp black process (in the production of a black toner); or copper phthalocyanine, monoazo pigment (C.I. Pigment Red 5, C.I. Pigment Orange 36 or C.I. Pigment Red 22), disazo pigment (C.I. Pigment Yellow 83), anthraquinone pigment (C.I. Pigment Blue 60), disazo dye (Solvent Red 19) or Rhodamine dye (Solvent Red 49) (in the production of a color toner) is added to the binder resin, and the mixture is thoroughly mixed in a ball mill or the like to obtain a homogeneous dispersion, which is kneaded by fusion in a kneader, cooled and pulverized to form a colored powder, i.e. a toner having an average particle diameter of 5 to 15 µm. The toner is blended with a magnetic powder such as an amorphous carrier, ferrit-coated carrier or spheroidally coated carrier in a suitable ratio to form a developer. A fine magnetic powder may be incorporated in the toner for improving meeting the requirement of a developing mechanism or the quality of the image. Examples of such a powder include those of alloys and compounds containing a ferromagnetic element, such as ferrite and magnetite. The fine magnetic powder having an average particle diameter of 0.05 to 1 µm may be dispersed in the binder resin in an amount of 30 to 70 wt.%. The toner according to the present invention may further contain a known modifier such as an offset inhibitor or a fluidizing agent suitably without hindering the invention. [Examples] The following examples will further illustrate the present invention, which by no means limit the invention. Example 1 3.5 kg of polyoxypropylene(2.2)-2,2-bis(4-hydroxyphenyl)propane, 1.04 kg of fumaric acid, 132 g of dodecenylsuccinic acid anhydride, 110 g of the above-mentioned compound (1) as the polybasic carboxylic acid (II) and 3 g of hydroquinone were placed in a 5 ℓ four-necked glass flask. Then, the flask was provided with a thermometer, a stainless steel stirrer, a dehydration tube having a reflux condenser and a nitrogen inlet tube and the reaction was carried out under stirring at 200°C in a nitrogen stream in an electrically heated mantle. The degree of polymerization was traced from the softening point determined according to ASTM E 28-51T and the reaction was terminated when the softening point reached 125°C. The obtained resin was in the form of a pale yellow solid having a glass transition temperature determined with a DSC (differential scanning calorimeter) of 59°C. 90 parts by weight of the resin obtained as above was mixed with 10 parts by weight of carbon black (Regal 400 R; a product of Cabot Co.) in a ball mill and the mixture was kneaded, pulverized and classified to obtain a toner having an average particle diameter of 12.5 µm. The obtained toner was mixed with a powdery iron carrier (EFV 200/300; a product of Nihon Teppun Co.). The electric charge thereof determined with a blow-off charge determination device was -23 µc/g. 50 g of the obtained toner was placed in a polymer bottle and left to stand at 50°C for 24 h. No caking was observed at all. 91 g of the toner was mixed with 1209 g of the same powdery iron carrier as above to form a developer. An image was formed with the obtained developer by using a commercially available electrophotographic copier (in which amorphous selenium was used as the sensitizer, the speed of the roller was 255 mm/sec, the heat roller temperature in the fixing device was variable and an oil applicator had been removed) to obtain a clear image free of scumming, blur or dropout in the solid part. The fixing temperature of the fixing device was controlled to 140 to 220°C and the fixing property of the image and offset property were examined to reveal that the image was fixed sufficiently at 142°C and no offset was recognized. After forming 50,000 copies, the clear image could still be obtained and neither fogging nor dropout was recognized in the solid part. The minimum fixing temperature was determined as follows: a load of 500 g was applied to a sand-containing rubber eraser having a size of the bottom of 15 mm x 7.5 mm and an image fixed by passing through the fixing device was rubbed back and forth five times with the eraser. The optical reflection density of the sample was determined with a reflection densitometer (a product of Macbeth Co.) before and after the rubbing. The temperature of the fixing roller determined when the fixing rate as defined below exceeded 70% was defined as the minimum fixing temperature: The optical density of the image before the rubbing was 0.50. Example 2 1.58 kg of polyoxyethylene(2)-2,2-bis(4-hydroxyphenyl)propane, 1.78 kg of polyoxypropylene-(2.2)-2,2-bis(4-hydroxyphenyl)propane, 830 g of terephthalic acid, 464 g of fumaric acid, 132 g of dodecenylsuccinic anhydride, 162 g of the above-mentioned compound (2) as the polybasic carboxylic acid (II) and 3 g of hydroquinone were placed in the same device as in Example 1 and the same procedure as in Example 1 was repeated. The reaction was terminated when the softening point reached 125°C. The obtained resin was in the form of a pale yellow solid having a glass transition temperature of 60°C. A toner was prepared from the obtained resin and it was blended with the powdery iron carrier to form a developer in the same manner as in Example 1. Example 3 2848 g of polyoxypropylene(2.2)-2,2-bis(4-hydroxyphenyl)propane, 208 g of 2,2-dimethyl-1,3-propanediol, 928 g of fumaric acid, 264 g of dodecenylsuccinic anhydride, 616.5 g of the above-mentioned compound (3) as the polybasic carboxylic acid (II) and 3 g of hydroquinone were placed in the same device as in Example 1 and then the same procedure as in Example 1 was repeated. The reaction was terminated when the softening point reached 123°C. The obtained resin was in the form of a pale yellow solid having a glass transition temperature of 62°C. A toner was prepared from the obtained resin and it was blended with the powdery iron carrier to form a developer in the same manner as in Example 1. Example 4 3560 g of polyoxypropylene(2.2)-2,2-bis(4-hydroxyphenyl)propane, 1245 g of isophthalic acid, 104 g of octylsuccinic anhydride, 1717 g of the above-mentioned compound (4) as the polybasic carboxylic acid (II) and 3 g of hydroquinone were placed in the same device as in Example 1 and the same procedure as in Example 1 was repeated. The reaction was terminated when the softening point reached 125°C. The obtained resin was in the form of a pale yellow solid having a glass transition temperature of 65°C. A toner was prepared from the obtained resin and it was blended with the powdery iron carrier to form a developer in the same manner as in Example 1. Comparative Example 1 The same procedure as in Example 1 was repeated except that the compound (1) was not used and the amount of fumaric acid was increased to 1102 g so as to control the ratio of the carboxyl groups to the hydroxyl groups and the reaction was terminated when the softening point reached 125°C. The obtained resin was in the form of a pale yellow solid having a glass transition temperature of 58°C. A toner was prepared from the obtained resin and it was blended with the powdery iron carrier to form a developer in the same manner as in Example 1. Comparative Example 2 The same procedure as in Example 1 was repeated except that the compound (1) was replaced with 110 g of trimellitic acid and the reaction was terminated when the softening point reached 125°C. The obtained resin was in the form of a pale yellow solid having a glass transition temperature of 59°C. A toner was prepared from the obtained resin and it was blended with the powdery iron carrier to form a developer in the same manner as in Example 1. An image was formed in the same manner as in Example 1 except that the developers obtained in Examples 2 to 4 and Comparative Examples 1 and 2 were used. The results are shown in Table 1. A density of the initial image developed in each test was found out good. Example 5 A toner was prepared in the same manner as in Example 1 except that the carbon black was replaced with a copper phthalocyanine pigment (C.I. Pigment No. Blue 15:3) and a developer was prepared therefrom. Then a clear, blue image was formed. The formed image was unchanged after storage in a polyvinyl chloride file. Example 6 3.5 kg of polyoxypropylene(2.2)-2,2-bis(4-hydroxyphenyl)propane, 1.04 kg of fumaric acid, 132 g of dodecenylsuccinic acid anhydride, 105 g of the above-mentioned compound (1) as the polybasic carboxylic acid (II) and 3 g of hydroquinone were placed in a 5 ℓ four-necked glass flask. Then, the flask was provided with a thermometer, a stainless steel stirrer, a dehydration tube having a reflux condenser and a nitrogen inlet tube and the reaction was carried out under stirring at 200°C in a nitrogen stream in an electrically heated mantle. The degree of polymerization was traced from the softening point determined according to ASTM E 28-51T and the reaction was terminated when the softening point reached 128°C. The obtained resin was in the form of a pale yellow solid having a glass transition temperature determined with a DSC (differential scanning calorimeter) of 58°C. 90 parts by weight of the resin obtained as above was mixed with 10 parts by weight of carbon black (Regal 400 R; a product of Cabot Co.) in a ball mill and the mixture was kneaded, pulverized and classified to obtain a toner having an average particle diameter of 12.5 µm. The obtained toner was mixed with a powdery iron carrier (EFV 200/300; a product of Nihon Teppun Co.). The electric charge thereof determined with a blow-off charge determination device was -23 µc/g. 50 g of the obtained toner was placed in a polymer bottle and left to stand at 50°C for 24 h. No caking was observed at all. 91 g of the toner was mixed with 1209 g of the same powdery iron carrier as above to form a developer. An image was formed with the obtained developer by using a commercially available electrophotographic copier (in which amorphous selenium was used as the sensitizer, the speed of the roller was 255 mm/sec, the heat roller temperature in the fixing device was variable and an oil applicator had been removed) to obtain a clear image free of scumming, blur or dropout in the solid part. The fixing temperature of the fixing device was controlled to 140 to 220°C and the fixing property of the image and offset property were examined to reveal that the image was fixed sufficiently at 143°C and no offset was recognized. After forming 50,000 copies, the clear image could still be obtained and neither fogging nor dropout was recognized in the solid part. Example 7 1.58 kg of polyoxyethylene(2)-2,2-bis(4-hydroxyphenyl)propane, 1.78 kg of polyoxypropylene(2.2)-2,2-bis(4-hydroxyphenyl)propane, 830 g of terephthalic acid, 464 g of fumaric acid, 132 g of dodecenylsuccinic anhydride, 123 g of the above-mentioned compound (2) as the polybasic carboxylic acid (II) and 3 g of hydroquinone were placed in the same device as in Example 6 and the same procedure as in Example 6 was repeated. The reaction was terminated when the softening point reached 122°C. The obtained resin was in the form of a pale yellow solid having a glass transition temperature of 58°C. A toner was prepared from the obtained resin and it was blended with the powdery iron carrier to form a developer in the same manner as in Example 6. Example 8 2848 g of polyoxypropylene(2.2)-2,2-bis(4-hydroxyphenyl)propane, 208 g of 2,2-dimethyl-1,3-propanediol, 928 g of fumaric acid, 264 g of dodecenylsuccinic anhydride, 1825 g of the above-mentioned compound (3) as the polybasic carboxylic acid (II) and 3 g of hydroquinone were placed in the same device as in Example 6 and then the same procedure as in Example 6 was repeated. The reaction was terminated when the softening point reached 124°C. The obtained resin was in the form of a pale yellow solid having a glass transition temperature of 60°C. A toner was prepared from the obtained resin and it was blended with the powdery iron carrier to form a developer in the same manner as in Example 6. Example 9 3560 g of polyoxypropylene(2.2)-2,2-bis(4-hydroxyphenyl)propane, 1245 g of isophthalic acid, 104 g of octylsuccinic anhydride, 2012 g of the above-mentioned compound (4) as the polybasic carboxylic acid (II) and 3 g of hydroquinone were placed in the same device as in Example 6 and the same procedure as in Example 6 was repeated. The reaction was terminated when the softening point reached 122°C. The obtained resin was in the form of a pale yellow solid having a glass transition temperature of 64°C. A toner was prepared from the obtained resin and it was blended with the powdery iron carrier to form a developer in the same manner as in Example 6. An image was formed in the same manner as in Example 6, except that each developer obtained in Examples 2 to 4 was used. Results are shwon in Table 2. Example 10 A toner was prepared in the same manner as in Example 6, except that carbon black was replaced by a pigment of copper phthalocyanine (C.I. Pigment No. Blue 15:3), and a developer was prepared therefrom. Then a clear, blue image was formed. The formed image was unchanged after the storage in a polyvinyl chloride file.

Claims: A process for producing a polyester by copolycondensing: (a) a diol component of the formula (I): in which R is an ethylene or propylene group and x and y are each an integer of at least 1, the total of x and y being 2 to 7 on the average, with (b) an acid component containing (II) a copolymer of a styrene compound selected from alpha-methylstyrene and a compound of the formula (IIa): in which R1 is hydrogen or a hydrocarbon group having 1 to 3 carbon atoms, and a vinyl monomer of the formula (IIb), an anhydride thereof or a lower alkyl ester thereof: in which R2 is hydrogen, methyl or carboxyl group and R3 is hydrogen, or a methyl group. A process as claimed in claimed 1, in which said acid component contains 0.05 to 70 mol percent of said copolymer. A process as claimed in Claim 1, in which said acid component comprises 1 to 50 mol percent of an alkyl- or alkenyl-succinic acid of the formula (III), an anhydride thereof or a lower alkyl ester having 1 to 4 carbon atoms thereof: in which R₉ is an alkyl or alkenyl group having 4 to 18 carbon atoms. A process as claimed in Claim 1, in which the molar ratio of said styrene compound to said vinyl monomer ranges from 1:1 to 5:1. A process as claimed in Claim 1, in which said acid component comprises fumaric acid, maleic acid, succinic acid, adipic acid, suberic acid, azelaic acid, sebacic acid, terephthalic acid, isophthalic acid or 2,6-naphthalene-dicarboxylic acid. A process as claimed in Claim 1, in which R1 of the formula (IIa) is an alkyl group. A process as claimed in Claim 1, in which said vinyl monomer is selected from maleic acid, fumaric acid, acrylic acid, and methacrylic acid. A process as claimed in Claim 1, in which said vinyl monomer is a lower alkyl ester of the same having 1 to 4 carbon atoms in the alkyl. A process as claimed in Claim 1, in which said acid component is a lower alkyl ester of the same having 1 to 4 carbon atoms in the alkyl. A process as claimed in Claim 1, in which said copolymer has a molecular weight of 1500 to 4000. A process as claimed in Claim 1, in which said copolymer (II), further comprises units of a third monomer. A toner composition which comprises the polyester obtained in the process as claimed in Claim 1 or 11 and a coloring matter. A toner composition obtained in the process as claimed in Claim 1, 11 or as claimed in 12, which further comprises 30 to 70 percent by weight of a magnetic powder having an average particle Size of 0.05 to 1 µm (micron).

Inventors: KAWABE, KUNIYASU, NISHIKAWA, HIDEYO, YASUDA, SHINICHIRO
Applicants: KAO CORPORATION
Application year: 1986
Main classification: C08G63
IPC codes: C08G63, G03G9