Phosphoric ester compound

Abstract: There is provided a new phosphoric ester compound represented by the formula below (where one or more than one of the three R's are hydroxyl-­ terminated polyester residues obtained by self-polyconden­ sation of a hydroxy-carboxylic acid; and one or two of the three R's, in case of being remained, are hydrogen atoms, cations, or residues of an alcohol excluding the above-­ mentioned polyesters.)

Description: 1. Field of the Invention: The present invention relates to a new phosphoric ester compound and, more particularly to a phosphoric ester compound containing a polyester chain useful as a pigment dispersant or flushing agent in the production of a pigment composition useful as a coloring material such as paint, printing ink or a synthetic resin colorant. 2. Description of the Prior Art: EP-A-0 164 817 discloses surfactants for enhancing the dispersibility of solids, such as e.g. compounds obtained by reacting a hydroxy-terminated polyester with a phosphorylating agent. In the conventional process for producing paints and printing inks, lecithin, which is one of phospholipids has been used both as a dispersant for dispersing a pigment into a paint vehicle or printing ink varnish, and as a flushing agent for flushing the aqueous filter cake into an oil vehicle or oil varnish. Being a natural phospholipid, lecithin is liable to oxidation and rancidity which lead to deterioration and putrefaction. Thus there has been a demand for a dispersant or flushing agent which is stabler and better than lecithin. In view of the above-mentioned drawbacks of the conventional dispersant or flushing agent and in order to develop a new compound which is compatible with vehicles and varnishes and also with pigments and is useful as a pigment dispersant, the present inventors carried out a series of researches which led to the finding that a phosphoric ester obtained by reacting a polyester having a hydroxyl group with phosphoric acid exhibits outstanding properties and effects required for pigment dispersants. The present invention was completed based on this finding. SUMMARY OF THE INVENTION Accordingly, it is an object of the present invention to provide a new phosphoric ester compound wherein the phosphoric ester compound is represented by the formula below and useful for a pigment dispersant or flushing agent. (where one or more than one of the three R's are hydroxyl-terminated polyester residues obtained by self-polycondensation of a hydroxy-carboxylic acid: and R's remaining are residues of an alcohol excluding in the above-mentioned polyesters.) DETAILED DESCRIPTION OF THE INVENTION The phosphoric ester compound which characterizes this invention is a specific phosphoric ester compound as defined above. The phosphoric ester compound of this invention can be obtained by various methods. According to a preferred method, it is obtained by reacting 1 mole of an ester-forming phosphorus compound with 3 moles, 2 moles. or 1 mole of a hydroxyl-terminated polyester (obtained by self-polycondensation of hydroxy-carboxylic acid.) It is also possible to produce the phosphoric ester compound of this invention by the process in which 1 mole of an ester forming phosphorus compound is reacted with 3 to 1 mole of hydroxy-carboxylic acid or lower alcohol ester thereof as a monomer and the resulting ester of phosphoric acid and hydroxy-carboxylic acid undergoes chain growth with the same or different hydroxy-carboxylic acid monomer and/or hydroxyl-terminated polyester. When 1 mole of an ester-forming phosphorus compound is reacted with 3 moles of a hydroxyl-terminated polyester, there is obtained a phosphoric ester compound in which all of the three R's in the above formula are hydroxyl-terminated polyester residues. Also, when 1 mole of an ester-forming phosphorus compound is reacted with 2 moles or 1 mole of hydroxyl-terminated polyester, there is obtained a phosphoric ester compound in which two or one of the three R's in the above formula are hydroxyl-terminated polyester residues. Among the ester-forming phosphorus compounds that can be used in this invention are phosphorus oxychloride, phosphorus pentoxide, phosphorus trichloride, phosphoric anhydride, and acetyl phosphate. Preferable among them is phosphorus oxychloride. The reaction of the above-mentioned ester-forming phosphorus compound with a hydroxyl-terminated polyester should preferably be carried out in an organic solvent which is both inert to the reactants and reaction products and solubilizes them. Examples of such organic solvents include aliphatic saturated hydrocarbons such as octane, petroleum ether, ligroin, mineral spirit, and kerosene; aromatic hydrocarbons such as benzene, toluene and xylene; halogenated aliphatic hydrocarbons such as trichloroethane and tetrachloroethane; and chlorinated aromatic hydrocarbons such as dichlorobenzene and trichlorobenzene. They have been used for the production of polyesters. In the case where a halogenated phosphorus compound such as phosphorus oxychloride is used as the ester-forming phosphorus compound, it is desirable to use as a catalyst a tertiary amine such as triethylamine; an organic base such as pyridine, 2-6-lutidine, and 1,8-diaza-bicyclo-(5.4.0)undecene-7; or an inorganic base such as oxides, hydroxides, carbonates and organic acid salts of alkali metals or alkaline earth metals. The hydroxy-terminated polyester used is an already known aliphatic, alicyclic or aromatic hydroxy-terminated polyester. The molecular weight of the hydroxyl-terminated polyester used in the above-mentioned reaction is not critical. A dimer or a polymer having an average molecular weight lower than 10,000, preferably about 500 to 5,000, can be used. The hydroxyl-terminated polyester as mentioned above is obtained by self-polycondensation of a hydroxy-carboxylic acid which has both a hydroxyl group and a carboxyl group on the molecule. The preferred hydroxy-carboxylic acid is one which has 4 to 30 carbon atoms. Examples of such hydroxy-carboxylic acids include ricinoleic acid, 12-hydroxy-stearic acid, castor oil fatty acid, hydrogenated castor oil fatty acid, δ-hydroxy-valeric acid, ε-hydroxy-caproic acid, p-hydroxyethyloxybenzoic acid, and hydroxynaphthalene carboxylic acid. They may be used individually or in combination with one another. It is also possible to use, n the same manner, a hydroxyl-terminated polyester obtained by esterifying an alcohol with the terminal carboxyl group of a polyester obtained from the above-mentioned hydroxy-carboxylic acid. Examples of the alcohol used for the terminal esterification are alcohols having 1 to 30 carbon atoms, such as methyl alcohol, ethyl alcohol, propyl alcohol, butyl alcohol, hexyl alcohol, octyl alcohol, decyl alcohol, dodecyl alcohol, tridecyl alcohol, hexadecyl alcohol, octadecyl alcohol, tetracosyl alcohol, hexacosyl alcohol, octadecenyl alcohol, cyclohexyl alcohol, and benzyl alcohol. The phosphoric ester compound of this invention is obtained by reacting 3 moles, 2 moles, or 1 mole of the above-mentioned hydroxyl-terminated polyester with 1 mole of the above-mentioned ester-forming phosphorus compound. Where 2 moles or 1 more of the above-mentioned polyester is reacted with 1 mole of the phosphorus compound, one or two R's other than polyester residues in the above-mentioned formula may be groups other than the above-mentioned polyester, such as residues of alcohol compounds. Examples of the alcohol residues are the residues of the above-mentioned ordinary monohydric alcohols, the hydroxy-carboxylic acid above-mentioned as the monomer and hydroxyl ester of the above-mentioned hydroxyl-carboxylic acid with the above-mentioned alcohol. The above-mentioned phosphoric ester compound of this invention comes in different forms according to the substituent group R. The ones defined below are comparatively hydrophobic dispersants adequately soluble in an organic solvent, and are used directly or in solvent solution to make the surface of a material such as pigment hydrophobic or oily. (1) All of the three R's are residues of hydroxyl-terminated polyester. (2) The three R's are residues of hydroxyl-terminated polyester and residues of other alcohols. The phosphoric ester compound containing a polyester chain of the present inventlon is not in danger of deterioration and putrefaction due to oxidation and rancidity, unlike lecithin as a natural phospholipid, which has been conventionally used as a pigment dispersant for paints, printing inks and plastics colorants. It has good stability and produces an outstanding effect in the surface modification of pigments and the dispersion of pigments in a medium. The phosphoric ester compound of this invention is readily adsorbed on the pigment surface due to the electronic attraction produced by the phosphoric ester linkage and the ester linkage contained therein and the affinity for mediums produced by the hydrocarbon chain contained therein. This adsorption improves the wettability, dispersibility and flowability of pigments. Therefore the phosphoric ester compound is useful as a dispersant in dispersing using a dispersing machine or a mixing machine. In addition the phosphoric ester compound is useful as a flushing agent for the aqueous filter cake of pigment. It makes the pigment surface lipophilic or hydrophobic, permitting effective flushing of pigments In addition, the phosphoric ester compound of this invention is also useful for such additive as a dispersant in a medium a fine solid particle such as magnetic recording material; an electroconductive substance such as metallic fiber, high-structure carbon black, carbon fiber; material for electro-magnetic interference; ceramic raw material and so on. The invention is now described in more detail with reference to examples. (In examples, quantities are expressed as parts by weight or percent by weight.) Example 1 (1) Synthesis of hydroxyl-terminated polyester from 12-hydroxy-stearic acid and methylesterification thereof. Into a four-mouth glass reactor equipped with a stirrer, thermometer, reflux condenser with a moisture distilling tube, and inlet and placed in an oil bath were charged 100 parts of 12-hydroxystearic acid and 100 parts of toluene, followed by stirring for dissolution. After heating, there was added 1.0 part of p-toluenesulfonic acid as a polycondensation catalyst. The reaction liquid was heated to 120°C to promote the polycondensation of 12-hydroxystearic acid. The progress of the reaction was measured by means of the volume of distilled water and the infrared absorption spectrum of the reaction product after the lapse of 60 minutes, 120 minutes, and 180 minutes. After 200 minutes, the polycondensation reaction was terminated by cooling. When the reactants were cooled to 63°C, there were added 50 parts of methanol, 100 parts of methyl acetate, and 0.5 parts of p-toluene-sulfonic acid. The reactants were heated to 110°C, with distillation of the solvent, to perform the methylesterification of the terminal carboxyl group of the polyester. When 150 parts of solvent had been distilled away, the reactants were cooled to 63°C. Then 200 parts of methanol were added and the solvent was distilled away by heating to 110°C. The total amount distilled away was 245 parts. The methylesterification took about 5 hours. After the reaction, 300 parts of water were added to the reaction mixture to extract water-soluble components from the reaction mixture. The oil layer was collected from the separating two layers. For dehydration of the oil phase, 150 parts of toluene and 200 parts of methanol were added, followed by heating to 130°C with blowing of nitrogen gas. Thus, water and solvents, 345 parts in total, were distilled away. The reaction product thus obtained was an amber liquid. It was identifed as a methyl ester of a self-polycondensation polyester of 12-hydroxystearic acid by the infrared absorption spectrum and gel permeation chromatograph. It was confirmed by the acid value of the reaction product that the methylesterifiaction of the terminal carboxyl group of the polyester was almost complete. The hydroxyl value of the reaction product was 40:8. This indicates that 1 gram equivalent of the methyl ester of the self-polycondensation polyester of 12-hydroxystearic acid is 1,375 and the average degree of polycondensation is about 5. (2) Synthesis of phosphoric triester compound: Into a four-mouth glass reactor equipped with a stirrer, thermometer, dropping funnel, and reflux condenser and placed in a water bath were charged 188.2 parts of the methyl ester of the polyester obtained in the above-mentioned step (1) (1 gram equivalent was 1,375), 188.2 parts of benzene, and 16.6 parts of triethylamine followed by stirring and dissolution. The dropping funnel was filled with 7.0 parts of phosphorus oxychloride. The equivalent ratio of the hydroxyl-terminated polyester, phosphorus oxychloride and triothylamine was 3:3:3.6. While stirring and cooling the reaction mixture (below 10°C), phosphorus oxychloride was added dropwise from the dropping funnel over 30 minutes. After addition, the reaction was continued for 2 hours with stirring, followed by cooling. For the removal of triethylamine (as a dehydrochlorination catalyst) and triethylamine hydrochloride, the reaction mixture was washed with an equal amount of deionized water, half an amount of water acidified with hydrochloric acid and three times with half an amount of deionized water using a separatory funnel. The washed benzene layer was dried with sodium sulfate and benzene was distilled away under vacuum. Thus there was obtained a brown liquid reaction product. The reaction product was identified as a phosphoric triester compound of the methyl ester of the self-polycondensation polyester of 12-hydroxy-stearic acid by the infrared absorption spectrum and gel permeation chromatograph. The average molecular weight of the principal component of this compound was 4,200. The above-mentioned phosphoric triester compound of the methyl ester of the poly-12-hydroxystearic acid is effective on the high concentrated charging of pigment, on the reduction of dispersing time and on dispersibility in the dispersion of a pigment such as copper phthalocyanine blue pigment, copper phthalocyanine green pigment, azo lake pigment insoluble azopigment, carbon black pigment and so on. It is also effective as a flushing agent in the flushing of an aqueous press cake of pigment. Examples 2 to 12 Various phosphoric triester compounds were prepared in the same manner as step (2) in Example 1 except that the reactant were replaced by those which are shown in Table 1 below. No. Reactants Ave. M.W. (I) (II) 2 Methyl ester of poly-12-hydroxystearic acid 880 3 2600 Phosphorus oxychloride 3 3 Methyl ester of polyricinolic acid 1430 3 4300 Phosphorus oxychloride 3 4 Butyl ester of poly-12-hydroxystearic acid 920 3 2800 Phosphorus oxychloride 3 5 Butyl ester of polyricinolic acid 1470 3 4500 Phosphorus oxychloride 3 6 Dodecyl ester of poly-12-hydroxystearic acid 1310 3 4000 Phosphorus oxychloride 3 7 Oleyl ester of polyricinolic acid 1110 3 3400 Phosphorus oxychloride 3 8 Tridecyl ester of poly-12-hydroxystearic acid 1050 3 3200 Phosphorus oxychloride 3 9 Oleyl ester of poly-ε-hydroxycaproic acid 960 3 2900 Phosphorus oxychloride 3 11 Poly-1 2-hydroxystearic acid 860 3 2600 Phoshorus oxychloride 3 12 Polyricinolic acid 860 3 2600 Phosphorus oxychloride 3 Example 13 Into a four-mouth glass reactor (the same one as used in step (2) in Example 1 equipped with a stirrer, thermometer, dropping funnel, and reflux condenser were charged 23.6 parts of phosphorus oxychloride. 147.7 parts of methyl ester of poly-12-hydroxystearic acid having an average molecular weight of 1440 (separately prepared in the same manner as in step (1) in Example 1) which had been mixed with and dissolved in 147.7 parts of benzene and 12.5 parts of triethylamine, were slowly added dropwise at 5 to 10°C over 2 hours. The reaction was carried out at 10°C for 1 hour. Further 30.8 parts of the methyl ester of the poly-12-hydroxystearic acid having an average molecular weight of 600 (prepared in the same manner as above), which had been mixed with and dissolved in 30.8 parts of benzene and 6.2 parts of triethylamine, was slowly added dropwise at 10 to 20°C over 1 hour. The reaction was carried out for 1 hour each at 20°C, 40°C, and 60°C and for 2 hours at 80°C with stirring. Finally the reactlon product was cooled. The molar ratio of polyester (average molecular weight 1440), polyester (average molecular weight 600), phosphorus oxychloride, and triethylamine was 2:1:3:3.6. The cooled reaction product was washed, purified, dried concentrated and desolvated in the same manner as in step (2) of Example 1. Thus there was obtained a brown liquid. The reaction product was identified as a phosphoric triester of the methyl ester of the poly-12-hydroxystearic acid in the same way as in step (2) of Example 1. The average molecular weight of the principal component of this compound was about 3,500. Thus the obtained compound is effectively used as a dispersant, flushing agent of pigment, same as the phosphoric triester compound of Example 1. Example 14 to 19 Various phosphoric triester compounds were prepared in the same manner as in Example 13 except that the reactants were replaced by those which are shown in Table 2 below. These phosphoric triester compounds are effectively used as a dispersant, flushing agent of pigment, and so on, same as the phosphoric triester compound of Example 1. No. Reactants Ave. M. W. (I) (II) 14 Methyl ester of poly-12-hydroxystearic acid 1440 2 Methyl ester of polyricinolic acid 590 1 3500 Phosphorus oxychloride 3 15 Methyl ester of polyricinolic acid 1430 2 Methyl ester of polyricinolic acid 590 1 3500 Phosphorus oxychloride 3 16 Methyl ester of poly-12-hydroxystearic acid 2010 2 Butyl ester of 12-hydroxystearic acid 1 4400 Phosphorus oxychloride 3 17 Methyl ester of polyricinolic acid 2830 1 Mixture of dodecyl ester and tridecyl esters of ricinolic acid 2 3900 Phosphorus oxychloride 3 18 Methyl ester of poly-12-hydroxystearic acid 2010 2 Dodecyl alcohol 1 4200 Phosphorus oxychloride 3 19 Methyl ester of polyricinolic acid 2830 1 Oleyl alcohol 2 3400 Phosphorus oxychloride 3

Claims: Claims for the following Contracting States : BE, CH, DE, FR, GB, NL, SE, IT, LI A phosphoric ester compound represented by the formula below where one or more than one of the three R's are hydroxyl-terminated polyester residues obtained by selfpolycondensation of a hydroxy-carboxylic acid; and any R's remaining are residues of an alcohol excluding the above-mentioned polyester. A phosphoric ester compound as set forth in Claim 1, wherein all of the three R's are the residue of the hydroxyl-terminated polyester obtained from a hydroxy-carboxylic acid. A phosphoric ester compound as set forth in Claim 1, wherein two of the three R's are the residues of the hydroxyl-terminated polyester obtained from a hydroxy-carboxylic acid. A phosphoric ester compound as set forth in Claim 1, wherein one of the three R's is the residue of the hydroxyl-terminated polyester obtained from a hydroxy-carboxylic acid. A phosphoric ester compound as set forth in Claim 1, wherein the hydroxyl-terminated polyester obtained from a hydroxy-carboxylic acid is a polyester obtained from one or more than one kind of hydroxy-carboxylic acid selected from the group consisting of ricinolic acid, hydroxystearic acid, castor oil fatty acid, hydrogenated castor oil fatty acid, hydroxyvaleric acid, hydroxycaproic acid, hydroxy-ethyloxybenzoic acid, and hydroxynaphthalene-carboxylic acid. Claims for the following Contracting State : AT A process for producing a phosphoric ester compound represented by the formula below where one or more than one of the three R's are hydroxyl-terminated polyester residues obtained by selfpolycondensation of a hydroxy-carboxylic acid; and any R's remaining, are residues of an alcohol excluding the above-mentioned polyester by reacting one mol of an ester-forming phosphorous compound with 3 mols, 2 mols or 1 mol of a hydroxyl-terminated polyester obtained by selfpolycondensation of hydroxy-carboxylic acid. A process as set forth in Claim 1, wherein all of the three R's are the residue of the hydroxyl-terminated polyester obtained from a hydroxy-carboxylic acid. A process as set forth in Claim 1, wherein two of the three R's are the residues of the hydroxyl-terminated polyester obtained from a hydroxy-carboxylic acid. A process as set forth in Claim 1, wherein one of the three R's is the residue of the hydroxyl-terminated polyester obtained from a hydroxy-carboxylic acid. A process as set forth in Claim 1, wherein the hydroxyl-terminated polyester obtained from a hydroxy carboxylic acid is a poyester obtained from one or more than one kind of hydroxyl-carboxylic acid selected from the group consisting of ricinolic acid, hydroxy-stearic acid, castor oil fatty acid and hydrogenated castor oil fatty acid, hydroxyvaleric acid, hydroxycaproic acid, hydroxy-ethyloxybenzoic acid, and hydroxynaphthalene carboxylic acid. hydroxy-carboxylic acid.

Inventors: HORIGUCHI SHOJIRO, NAKAMURA MICHIEI, TAKAHASHI TETUJIRO, TAKEUCHI HITOSHI, TAKIZAWA MINORU, HORIGUCHI, SHOJIRO, NAKAMURA, MICHIEI, TAKAHASHI, TETUJIRO, TAKEUCHI, HITOSHI, TAKIZAWA, MINORU
Applicants: DAINICHISEIKA COLOR CHEM, DAINICHISEIKA COLOR & CHEMICALS MFG. CO. LTD.
Application year: 1986
Main classification: C08G63
IPC codes: C08G63, B01F17