MULTILAYER PACKAGING FILM

Abstract: This invention relates to a co-extruded multilayer film and particularly for vacuum packaging food products. The film comprises at least one layer formed by an ethylene-vinyl acetate-copolymer with a vinyl acetate content preferably comprised between 9% and 26% range by weight. The film is preferably radiated at a lower level than 20 MRad. The film is adapted to resist high stretch ratios during the packaging proces, so that packaging of bodies with projecting portions or cavities is possible, without breaking the film.

Description: This invention relates to a multilayer packaging film for generic use and in particular for vacuum skin packaging food products. A method of vacuum skin packaging food products, exemplary of the inventive film application, is the one disclosed in Italian Patent No. 937,557, corresponding to UK Patent No. 1,307,054, or the one disclosed in Italian Patent No. 1,001,879, corresponding to UK Patent No. 1,404,417. Known are multilayer films for packaging food products, in particular from US Patent No. 3,741,253, granted on June 26, 1973, which discloses a film comprising a first layer of a radiated ethylene vinyl acetate copolymer, bonded to an intermediate layer of vinylidene chloride, and a third layer bonded directly to the intermediate layer and formed from a copolymer of ethylene vinyl acetate. That film cannot, however, be radiated because the intermediate layer of vinylidene chloride tends to release gas while being radiated, and the layer comprised of the ethylene vinly acetate polymer must be radiated separately from the other layers. The film is suitable for use in making bags typically utilized to receive food products thereinto, thereafter a vacuum is formed within the bag and clip applied to close it, the filled bag being then immersed in a hot water bath at a temperature approximating the temperature at which the film was stretched. One of the problems encountered is the unreliable closure provided by the clip, particularly as the film shrinks around the food product under the heat applied, and the clip tends to be pulled away. UK Patent Application No. 2.134.446 discloses a multilayer film, (inner) A/B/C/D/C/E (outer), where A is a bonding layer comprising an ethylene-propylene copolymer; B is a shrinking layer which may be formed from an ethylene vinyl acetate copolymer having a vinyl acetate content in the range of 6% to 12% by weight, preferably of 6%; C are adhesive layers effective to join the barrier layer D to the remainder of the film. The layer D is formed from a copolymer of ethylene vinyl acetate hydrate (EVOH). The outer layer E isolates the barrier layer against contact with outside moisture and comprises an ethylene vinyl acetate copolymer having a vinyl acetate content ranging form 5% to 12%, preferably of 6%, by weight. Such film can optionally be radiatively cross-linked. UK Patent Application No. 1.522.397 discloses a multilayer film comprising an oxygen barrier situated between two other polymeric layers, at least one of which comprises an oriented cross-linked polymer, wherein such cross-linking can be carried out using irradiation. The two other polymeric layers can be an olefin such as polyethylene or ethylene-vinyl acetate copolymer, the latter having a preferred vinyl acetate content between 3% and 12% and may be up to approximately 15% weight. European Patent Application No. 217.252, disclosing a multilayer film, has a priority date of September 30, 1985 and a publication date of April 8, 1987 and thereby falls within the terms of Article 54(3) EPC. Such application discloses examples of irradiated multilayer films comprising a layer of copolymer of ethylene and alpha-olefins or a layer of ionomeric material and another layer which is ethylene-vinyl acetate copolymer with vinyl acetate contents up to 9%. Also disclosed are non-irradiated films comprising ethylene-vinyl acetate layers with vinyl acetate contents of 14% and 18%. It has been ascertained in actual practice that in the course of the vacuum packaging process, conventional films tend to be broken when subjected to high stretch ratios at particular projections or recesses randomly arranged on the material being packaged. Accordingly, an object of this invention is to provide a suitable film for vacuum skin packaging food products, which exhibits high mechanical strength properties even at high stretch ratios, thereby it can conform to the shape of the product being packaged by deformation without breaking. Another object of the invention is to provide a multilayer film suitable for combined coextrusion and radiation. A further object of the invention is to provide a film which comprises, where required, an oxygen barrier for preservation of food products liable to oxidation. These and other objects are achieved by a film according to the invention, which is characterized in that it comprises at least two co-extruded layers of which: a bonding layer comprising a material selected from olefinic homo- and copolymers and ionomeric materials, and a complementary layer comprising a copolymer of ethylene-vinyl acetate wherein the vinyl acetate content is in the range of 14% to 26% by weight, the remainder being ethylene provided that a vinyl acetate content of 15% or less is excluded; said film being cross-linked by radiation. The vinyl acetate contents is preferably in the range of 14% to 18% range, by weight. The bonding layer comprises a material selected from low-density polyethylene, high-density polyethylene, low-density linear polyethylene, ethylene-vinyl acetate copolymer with a vinyl acetate content in the 3% to 9% range by weight, ionomeric resins, and mixtures thereof. Of preference, that bonding layer is selected from low-density polyethylene, high-density polyethylene, and a mixture thereof. More preferably, the bonding layer is formed essentially from low-density polyethylene. In a first embodiment, the film comprises two co-extruded layers only: a bonding layer and a complementary layer, and is intended for use in packaging food products which require no oxygen barrier. In a variation of this first embodiment, the film comprises an outer layer which is co-extruded along with the bonding layer and the complementary layer, the outer layer being located outwardly on the remote side from the bonding layer. The outer layer is useful as a protection against wear, and comprises a material selected from low-density polyethylene, high-density polyethylene, low-density linear polyethylene, ethylene-vinyl acetate copolymer with a vinyl acetate content of 3% to 9% by weight, ionomeric resin, and mixtures thereof. Of preference, the outer layer comprises a material selected from: low-density polyethylene, high-density polyethylene, and a material yielded by mixing them together. More preferably, the outer layer is formed essentially from low-density polyethylene. In a second embodiment, the film comprises an oxygen barrier layer. That second embodiment is specially suitable for packaging applications with food products which require preservation against the oxidizing action of air oxygen. In particular, the barrier layer is placed between the complementary layer and outer layer, and is joined to the nearby layers by two adhesive layers. The barrier layer comprises an ethylene-vinyl alcohol copolymer. This second embodiment envisages preferably a double complementary layer. In this case, the sequence for the co-extruded layers would be, from the inside out: a bonding layer, a complementary layer, and adhesive layer, a barrier layer, and adhesive layer, a complementary layer, an outer layer. The adhesive layers are formed in general from an ethylene vinyl acetate copolymer suitable for cross-linking by radiation and being chemically modified to accept functional groups having great affinity for the ethylene-vinyl alcohol copolymer that forms the barrier layer. Suitable commercially available adhesives are identified by the trade names of Bynel 3095, Plexar PX3. Irrespective of the embodiment of choice, the combined thickness of the stretched layer or layers will be 35% to 75% of the overall thickness of the film and preferably from 50% to 65% of the overall film thickness. The film overall thickness ranges from 50µm to 300µm, preferably from 80 to 200µm, and still better from 120µm to 150µm. The thickness of the bonding layer and/or thickness of the outer layer amount to 3-25% of the overall thickness of the film. The bonding layer and/or other layer are formed from low-density polyethylene and have a thickness dimension amounting to 3-10% of the overall thickness of the film. The film according to the invention is obtained by a method which allows to improve the formability and abuse resistance of a known multi-layer, coextruded, thermoplastic packaging film, which has layers of ionomer, EVOH, low density polyethylene and high density polyethylene. Such improvement is obtained replacing the low density polyethylene layers with ethylene vinyl acetate copolymer layers having a vinyl acetate content in the range of 12% to 26%. The entire coextruded multi-layer film is then irradiated with ionizing radiation to induce cross-linking in the ethylene polymers and copolymers. The radiation level is lower than 20 MRads, preferably is in the 8 to 16 MRad range, still better preferably in the 12 to 14 MRad range. The invention will be more clearly understood from the Examples and the drawing herewith, given by way of illustration and not of limitation of this invention. Table 1 shows examples 1-8, wherein examples 1 and 2 are conventional comparative Examples and Examples 3-8 illustrate the inventive film. Abbreviations are standard in the art, as follows. LDPE = Low-Density Polyethylene; HDPE = High-Density Polyethylene; LLDPE = Linear Low-Density Polyethylene; and EVA = Ethylene Vinyl Acetate Copolymer. The last column in the Table (Hole Area) relates to the results of a specially meaningful test to an understanding of this invention objectives. The holes whose areas have been set forth therein are shown in Figure 1 , which depicts a wooden block 1, drilled and vacuum packaged. The film 6 completely envelops the block 1, and of course, also covers the ports of the circular holes 2,3,4, and 5. The depth dimension is the same for all the holes but the area of each hole port increases progressively. During the packaging tests with the wooden block 1, the film tends to undergo a stretching stress which is the higher the larger is the area of a hole. In the Example considered in Figure 1, the film 7,8,9 stretches without breaking over the holes 2,3 and 4, but breaks in 10, over the largest area hole 5. The area of the largest hole before the film becomes broken is entered, therefore, in the last column of Table 1, and is highly representative of the film packaging ability. The packaging tests on the block 1 were conducted throughout examples 1-8 on a Cryovac VS44 ® machine equipped with a rotary vacuum pump and a serially connected auxiliary pump. The temperature under the heater bell was of 200°C, and the films were infrared pre-heated up to 70-80°C. The level of the vacuum provided varied between 3 and 6 millibars. As can be taken from Table 1, with specific reference to examples 5,6,7 and 8, the inventive film affords breakage-free packaging of holes having a section area which is about seven times as large as those of the comparative films in Examples 1 and 2.

Claims: A vacuum skin packing film comprising at least two co-extruded layers of which: a bonding layer comprised of a material selected from olefinic homo- and copolymers and ionomeric materials; and a complementary layer comprised of an ethylene-vinyl acetate-copolymer, said film being cross-linked by radiation characterized in that the vinyl acetate content of said complementary layer is in the 14% to 26% range, by weight, the remainder being ethylene, provided that a vinyl acetate content of 15% or less is excluded. A film according to Claim 1, characterized in that said content in vinyl acetate is less than 18% by weight. A film according to Claim 1, characterized in that said bonding layer comprises a material selected from low-density polyethylene, high-density polyethylene, linear low-density polyethylene, ethylene-vinyl acetate copolymer with a vinyl acetate content of 3% to 9% by weight, ionomeric resins, and a mixture thereof. A film according to claim 3, wherein said bonding layer is selected from low-density polyethylene, high-density polyethylene, and a mixture thereof. A film according to claim 4, wherein said bonding layer is formed from low-density polyethylene. A film according to Claim 1, comprising an outer layer co-extruded with the bonding layer and the complementary layer, said outer layer being provided outwardly on the remote side from said bonding layer; said outer layer comprising a material selected from low-density polyethylene, high-density polyethylene, linear low-density polyethylene, ethylene-vinyl acetate copolymer with a vinyl acetate content of 3% to 9% by weight, ionomeric resins, and a mixture thereof. A film according to claim 6, wherein said outer layer comprises a material selected from low-density polyethylene, high-density polyethylene, and a mixture thereof. A film according to claim 7, wherein said outer layer is formed from low-density polyethylene. A film according to any of the preceding claims, characterized in that it comprises a barrier layer provided between said complementary and outer layers. A film according to Claim 9, characterized in that said barrier layer is joined to the nearby layers by means of two adhesive layers, said barrier layer comprising an ethylene-vinyl alcohol copolymer. A film according to any of the preceding claims, characterized in that it comprises the following successive co-extruded layers: said bonding layer, said complementary layer, said adhesive layer, said barrier layer, said adhesive layer, said complementary layer, and said outer layer. A film according to any of the preceding claims, characterized in that the combined thickness of the stretched layer or layers amounts to 35-75% of the overall thickness of the film. A film according to claim 12, wherein the combined thickness of the stretched layer or layers amounts to 50-65% of the overall thickness of the film. A film according to any of the preceding claims, characterized in that the overall thickness of the film is within the range of 50 to 300 µm. A film according to claim 14, wherein the overall thickness of the film is within the range of 80 to 200 µm. A film according to claim 15. wherein the overall thickness of the film is within the range of 120 to 150 µm. A film according to any of the preceding claims, characterized in that the thickness of the bonding layer and/or the thickness of the outer layer amounts to 3-25% of the overall thickness of the film. A film according to Claim 17, wherein said bonding layer and/or outer layer are formed from low-density polyethylene and have a thickness dimension amounting to 3-10% of the overall thickness of the film. A film according to any of the preceding claims, characterized in that it is caused to cross-link by radiation at a lower level than 20 MRad. A film according to claim 19, wherein it is caused to cross-link by radiation at a level of 8 to 16 MRad. A film according to claim 20, wherein it is caused to cross-link by radiation at a level of 12 to 14 MRad. A method of improving the formability and abuse resistance of a multi-layer, coextruded, thermoplastic packaging film having layers of ionomer, ethylene vinyl acetate hydrate, low density polyethylene and high density polyethylene characterized by replacing the low density polyethylene layers with ethylene vinyl acetate copolymer layers having a vinyl acetate content in the range of 12% to 26% and thereafter irradiating the entire multi-layer film with ionizing radiation to induce cross-linking in the ethylene polymers and copolymers. A method according to Claim 22, wherein said ionizing radiation has a level which is lower than 20 MRad. A method according to claim 23, wherein said ionizing radiation has a level in the 8 to 16 MRad range. A method according to claim 24, wherein said ionizing radiation has a level in the 12 to 14 MRad range.

Inventors: BOTTO, PAOLO, FRESCHI, CLAUDIO
Applicants: W.R. GRACE & CO.-CONN. (A CONNECTICUT CORP.)
Application year: 1986
Main classification: B32B27
IPC codes: C08J3, B32B27