NEGATIVE ELECTRODES FOR NON-AQUEOUS SECONDARY BATTERIES COMPOSED OF CONJUGATED POLYMER AND ALKALI METAL ALLOYING OR INSERTING MATERIAL

Abstract: This invention relates to a novel anode for use in batteries, and to batteries containing the anode, which anode comprises an electroactive material selected from the group consisting of sodium alloying metal, and a mixture of a conjugated backbone polymer and another electroactive material selected from the group con­ sisting of metals which alloy with alkali metals and alkali metal cation inserting materials as for example transition metal chalcogenides.

Description: BACKGROUND OF THE INVENTION (1) Field of the Invention This invention relates to polymeric electrodes. More particularly, this invention relates to negative electrodes for non-aqueous secondary batteries composed of conjugated backbone polymers and alkali metal alloying or alkali metal ion inserting materials. (2) Prior Art Conjugated backbone polymers, e.g., polyacetylene, polyphenylene, polyacenes, polythiophene, poly(phenylene vinylene), polyazulene, poly(phenylene sulfide), poly­ (phenylene oxide), polythianthrene, poly(phenyl­ quinoline), polyaniline, polythiophene, and polypyrrole, have been suggested for use in a variety of applications based upon their characteristic of becoming conductive when oxidized or reduced either chemically or electrochemically. The secondary battery application described by, e.g., MacDiarmid et al. in U.S. Patent 4,321,114 (1981); J. de Physique , Colloque C3, Vol. 44 (1983), articles beginning on page 579, page 615 and page 537; and K. Kaneto et al., Japanese J. of Applied Physics , Vol. 22, pp. L567-L568 (September 1983) and pp. L412-L414 (July 1983), employs one or more electrodes having conjugated backbone polymers as the electroactive material. Such electrodes can, for example, be reversibly complexed with alkali metal or tetraalkyl­ ammonium cations during battery cycling, most commonly with insertion of cations into a polymer anode (the negative battery electrode) occurring during charging. The more such cations are inserted, the more conductive the electrode becomes and the more cathodic the potential of the anode becomes. Lithium and lithium alloys have been suggested for use on the negative electrode of electrochemical cells. For example, U.S. Patent No. 4,002,492 discloses electrochemical cells having an anode consisting essentially of lithium aluminum alloys that contain lithium in amounts between about 63% and 92% and the balance essentially aluminium. Anodes composed of lithium and aluminum are also disclosed in Rao, et al., J. Electrochem. Soc . 124 , 1490 (1977), and Besenhard, J. Electroanal. Chem ., 94 , 77 (1978). European Patent No. 0070107 Al; Murphy et al., J. Electrochem. Soc ., 126 , 349 (1979) and Murphy et al., Mat. Res. Bull ., 13 , 1395 (1978) disclose batteries based on lithium intercalation in layered dichalcogenides. Composite structures of a conjugated backbone poly­ mer and a non-electroactive material have been described in U.S. Patent No. 4,294,304 and in the above J. de Physique issue, articles beginning on page 137 and on page 151. Representative other components that have been blended with polyacetylene or onto which poly­ acetylene or polypyrrole have been deposited include polyethylene, polystyrene, graphite, carbon black, NESA glass and silicon. In selected instances, such com­ posite structures have been suggested for use in bat­ teries, see Showa Denko K.K., European Published Patent Application 76,119 (1982). J. O. Besenhard and G. Eichinger, J. Electroanal. Chem., 78 , I (1976), at pages 8 and 9 describe the difficulty of redepositing sodium metal at room temperature from non-aqueous solutions. SUMMARY OF THE INVENTION While batteries have heretofore been constructed in which a conjugated backbone polymer is the electroactive material, such batteries suffer from a number of disad­ vantages. For example, such cells have heretofore exhibited strongly varying discharge potentials. More­ over, such cells have relatively low volumetric energy densities. Batteries to be used at room temperature construc­ ted with anodes composed of alkali metal alloys, such as lithium/aluminum alloys, also suffer from a number of disadvantages. For example, such batteries have exhi­ bited relatively low capacity (utilization), low rate capability and poor cycle life. Generally speaking, the present invention obviates one or more of the disadvantages of the prior art poly­ mer batteries or alloy anode batteries by providing an improved anode for high energy density electrochemical cells which include a cathode containing a cathode active material, an anode containing an anode active material, and a non-aqueous electrolyte having an ionic salt of the anode active material dissolved therein. More particularly, the improved anode of this invention comprises an anode active material selected from the group consisting of a metal capable of alloying with sodium and a mixture comprising a conjugated backbone polymer or copolymer or a blend of a conjugated polymer with one or more conjugated or non-conjugated backbone polymers and a material selected from the group consisting of metals capable of alloying with an alkali metal and alkali-metal cation inserting materials. The present invention also provides a battery incorporting the novel anode of this invention, which battery comprises: (a) a cathode; (b) an electrolyte comprising an organic solvent and an alkali metal-salt; and (c) an anode comprising an anode active material selected from the group consisting of: (i) a metal capable of alloying with sodium in said electrolyte, and (ii) a mixture comprising a conjugated backbone polymer or copolymer or a blend of a conjugated backbone polymer with one or more conjugated or non-conjugated backbone polymers and a material selected from the group consisting of one or more metals capable of alloying with the alkali metal in said electrolyte and an alkali-­ metal cation inserting material capable of inserting ions of alkali metal in said electroyte; said alkali-metal cations in said electrolyte being introduced into said anode as a metal alloy or as an inserted ion in said ion inserting material during the charging of said battery. DESCRIPTION OF THE PREFERRED EMBODIMENTS As an essential component, the battery of this invention includes an anode which comprises a unique anode active material. One unique anode active material useful in the battery of this invention comprises a mix­ ture of one or more conjugated backbone polymers or copolymers, or blends of one or more conjugated polymers or copolymers with one or more conjugated or non-conju­ gated backbone polymers or copolymers (hereinafter referred to collectively as "conjugated backbone poly­ mer), which polymers, copolymers or blends contain an effective amount of one or more other potential electro­ active materials selected from the group consisting of metals which are capable of alloying with alkali metals and materials capable of inserting alkali-metal cations. The structure of this anode can be varied widely. For example, the anode can be in the form of an intimate mixture of compressed powders. Alternatively, the anode can be in the form of a film of the conjugated backbone polymer impregnated with the other component in finely divided form, or in the form of a composite layered structure in which one of the components is a core structure encapsulated by and in intimate contact with the other component. In the preferred embodiments, the anode is in the form of an intimate mixture of com­ pressed powders, or a casting of the polymer having par­ ticles of the other electroactive material dispersed therein. Useful polymers may be any of the variety of con­ jugated backbone polymers known to those of skill in the art for use as negative electrodes in batteries. Such polymers are preferably conductive in their reduced form and capable of reversibly inserting cations. Useful polymers are also insoluble or substantially insoluble in the electrolyte (i.e., preferably a solubility equal to or less than about 500 ppm). Useful conjugated back­ bone polymers may be conjugated backbone homopolymers or copolymers, or blends of one or more conjugated backbone homopolymers or copolymers with one or more conjugated backbone or non-conjugated backbone homopolymers or copolymers. Useful conjugated backbone polymers can vary widely and include polyacetylene, polyphenylene, (if in the para form), poly(phenylene vinylene) and the like, and blends thereof with other polymers having either conjugated or non-conjugated backbones, such as polyethylene. Other conjugated backbone polymers claimed by others as useful in batteries may also be used in the present invention. Such polymers include polythiophene, polyazulene, poly(phenylquinoline), polyacenes, polyacenediyls, polynaphthalene, and the like and polymeric blends thereof. Amongst these illustrative conjugated backbone polymers, polyacety­ lene, poly(phenylene vinylene) and poly(p-phenylene) are preferred, and polyacetylene and poly(p-phenylene) are particularly preferred. Most preferred for use in the practice of this invention is polyacetylene. Useful conjugated backbone polymers are known com­ pounds which can be prepared by conventional means. For example, high quality polyacetylene, a preferred conju­ gated backbone polymer, can be conveniently prepared by the procedures described in a series of papers by Shirakawa, et al., Polymer Journal , Vol. 2, No. 2, pp. 231-244 (1971); Polymer Journal , Vol. 4, No. 4, pp. 460-­ 462 (1973); Journal of Polymer Science Part A-1 , Polymer Chemistry Edition, Vol. 12, pp. 11-20 (1974), and Journal of Polymer Science Part A-1 , Polymer Chemistry Edition Vol. 13, pp. 1943-1950 (1975), all of which are incorporated herein by reference. Moreover, forms of high quality poly(p-phenylene), another preferred conju­ gated backbone polymer, can be prepared by the method of Kovacic described in detail in J. Am. Chem. Soc . 85 , 454-458 (1963), incorporated herein by reference. Fur­ thermore, poly(phenylene vinylene), another preferred conjugated backbone polymer, can be prepared by the pro­ cedure described in U.S. Patent No. 3,404,132 of R.A. Wessling et al. The second essential component of this unique anode material is a material selected from the group consist­ ing of metals or alloys which are capable of alloying with alkali metals, and materials which are capable of inserting alkali metal cations. Useful alkali metal alloying metals can vary widely. Illustrative of such useful metals are aluminium, lead, magnesium, tin, bismuth, antimony, silicon, and alloys of these or other metals, such as Al-Si, Al-Mg, Al-Si-Sn, or Wood's Metal (Bi-Pb-Sn-Cd) and the like. The preferred alkali metal alloying metals for use in the practice of this inven­ tion are aluminum, lead, tin and alloys thereof. In the particularly preferred embodiments of the invention, aluminum is used for lithium alloying, and lead, tin and tin/lead alloys are used for sodium alloying. Alkali-metal cation inserting materials can vary widely. As used herein, "alkali metal cation inserting materials" are materials into which alkali metal cations can be inserted, as for example, into channels in the material, between layers of the material and the like. Such materials are known to those of skill in the art. Such materials include but are not limited to graphite, transition-metal chalcogenides, and other conjugated backbone polymers which are capable of being reduced, i.e., donor doped. Preferred cation inserting materials are transition-metal chalcogenides such as TiS₂, MoO₂, WO₂, VSe₂, FeCuS₂, and VS₂,. The amounts of the various components of the anode material can vary widely, depending on a number of factors, as for example, the balance chosen between electrochemical capacity, and the desired mechanical properties of the anode, electrode, and the like. In general, the amount of the conjugated backbone polymer component in the anode should be sufficient to impart mechanical stability and good cycle life to the electrode. In the preferred embodiments of this aspect of the invention, the amount of the conjugated backbone polymer component may vary from about 5 to about 75 percent by weight based on the total weight of polymer and other electroactive material in the anode, and in the particularly preferred embodiments up from about 20 to about 50% by weight on the aforementioned basis. Similarly, the amount of the other electroactive material in this aspect of the invention (e.g., alkali metal alloying material and/or inserting material) can also vary widely depending on a number of factors, as for example, the balance chosen between electrochemical capacity and the desired mechanical properties of the electrode and the like. Usually the amount of such material varies from about 25 to about 95 weight percent based on the total weight of conjugated backbone polymer and other electroactive material. In the preferred embodiments of the invention, the amount of the other material may vary from about 50 to about 80 weight percent on the aforemention basis. The particular polymer and alloying metal and/or cation inserting material chosen for use in any par­ ticular situation may vary widely. However, in the preferred embodiments of the invention the polymer and other electroactive material are selected such that the range of electroactivity of the polymer encompasses or closely matches that of the other component. The following table lists exemplary combinations of conjugated backbone polymer and alkali metal alloying metal or alkali metal cation inserting material which can be used in this aspect of the anode of this invention. The table shows that a combination of polyacetylene and the alloying metal, aluminum (Al), and combinations of poly(phenylene) and the lithium cation inserting material WO₂, and poly(phenylquinoline) and the inserting material MoO₂ are combinations of polymers and alloying metal or inserting materials which would be expected to provide good results. The anode of this invention comprises a mixture of conjugated backbone polymer and one or more other electroactive material may include other optional materials known to those of skill in the battery art. These materials are known to those of skill in the art and will not be described herein in great detail. In brief, by way of illustrative examples, the anode may include such other substituents as conductivity aids, inert binders, mechanical supports, and the like. However, in the preferred embodiments, the combination of polymer plus other electroactive material is in the major proportion. The anode of this invention comprises a mixture of conjugated backbone polymer and one or more other electroactive material may also be coated with other materials to allow use of the anode with solvents which would otherwise react with the conjugated backbone polymer in the reduced state. For example, the anode can be coated with the reaction product of an oxirane compound as described in U.S. Patent No. 4,472,487, with the reaction product of an organsulfur compound as described in U.S. Patent No. 4,472,489 and with the reaction product of certain cyclic compounds as described in U.S. Patent No. 4,472,488. Each of these patents are incorporated herein by reference. The method of fabricating the anode of this inven­ tion which comprises a mixture of conjugated backbone polymer and other electroactive material is not critical and can be varied widely. Any method known to those of skill in the art for fabricating composites of polymer and a metal or alkali metal ion inserting material can be used. In the preferred embodiments, the anode is composed of an intimate mixture of compressed powders which is prepared through use of the process of this invention. In this process, the anode is fabricated by (1) derivatizing the surface of a finely divided alkali metal alloying metal or alkali metal cation inserting material with active polymer catalyst for conjugated backbone polymers or a catalyst for polymers which can be converted into a conjugated backbone polymer; (2) dispersing the derivatized metal or material having a desired small particle size in a suspension or solution of a monomer and/or a precursor of the desired conju­ gated backbone polymer and polymerizing the monomer and/or precursor in the presence of the dispersed metal or material and; (3) fabricating a cohesive solid by recovering the polymerization product and derivatized metal or material from the polymerization mixture from said suspension or solution and compressing same into a powdered composite, or by casting a film of suspension or gel-like composition comprising the polymerization product, and metal or material. For substrates having a surface suitable for anchoring polymerization catalysts, the first step of the process is the derivatization of the substrate surface by a component of a catalyst system that is active in polymerization reactions forming conjugated backbone polymers or polymers which can be converted to conjugated backbone polymers. The derivatization is performed by contacting a catalyst component with a substrate whose surface contains reactive function­ alities such as oxides, hydroxides, sulfides, hydrogen sulfides and the like. For example, when the substrate consists of a metal, often the surface of the metal pos­ sess an oxide hydroxide layer which may react with a suitable catalyst component such as AlCl₃, Ti(O-nBu)₄, MoOCl₄, MoCl₅ or WCl₆, to yield a metal substrate bonded at the surface via its oxide layer to a modified cata­ lyst component according to the equation: Metal-OH + AX m -------> Metal - O n -AX m-n + HX where, A represents for example a transition metal and X represents for example a halide or an alkoxide. Prior to contacting the derivatized substrate with monomers, the remaining catalyst components are added as necces­ sary to the derivatized substrate to make a complete catalyst bonded to the substrate. For those substrates that do not possess a surface layer which reacts with suitable catalyst components and that are not polymerization catalysts themselves, the process requires a pretreatment of the substrate to introduce surface functional groups such oxides, hydroxides, sulfides, carboxylic acids and the like. Reagents for pretreatment include nitric acid, chromic acid, alkali metal hydroxides, alkaline earth metal oxides, alkali metal sulfides, anhydrides and the like. Derivatization of the treated surface can then proceed as above. For the substrate whose surface is catalytic for polymerization, derivatization is not required and the substrate and the monomers or precursors are merely contacted in a suitable medium. For example, Na x CoO₂, Li x CoO₂, V₂O₅, or other high potential transition metal chalcogenides can be contacted with a solution of reactive monomers such as pyrrole or thiophene in the presence of an electrolyte salt to form oxidized poly­ pyrrole or polythiophene on the substrate surface. In the preferred embodiments of the invention in which the process is used to prepare an anode containing a finely divided electroactive material dispersed in a conjugated backbone polymeric matrix, the substrate is a finely divided metal, alloy or other electroactive material. Preferred metals and alloys include aluminium, lithium-aluminum alloys, lead, tin, tin/lead alloys and other metal and alloys which can alloy with alkali metals. Other useful and preferred electroactive materials which can be used in the manufacture of anodes are the transition metal chalcogenides. Such chalco­ genides for use in the practice of this invention can vary widely and include WO₂, MoO₂, Li x TiS 2 , Li x VSe₂, and Li x VS₂ where 1< x <2. In these preferred embodiments of the invention, the powdered metal, alloy or other electroactive material generally has an average particle diameter of from about 100um to about 0.05um. In the preferred embodiments of the invention, average particle diameter is from about 20um to about 0.1um, and in the parti­ cularly preferred embodiments is from about 0.1um to about 10um. Amongst these particularly preferred embodiments most preferred are those embodiments in which average particle diameter is from about 0.1um to about 5um. In the polymerization step of the process of this the invention, the substrate having a catalytic surface and in a suitable form, as for example, in the form of a finely divided particulate material or large solid sub­ strate is contacted with a gas, suspension or solution of the monomer, monomers or other precursors of the desired conjugated backbone polymer, or other polymer which can be converted into a conjugated backbone polymer after polymerization, if necessary in the presence of a co-catalyst, such as triethylaluminum, tetramethyl tin, tetraphenyl tin and the like. There­ after the monomer, monomers or precursors are poly­ merized, forming the polymer on the surface of the substrate anchored thereto through the bonded catalyst. The polymer-coated substrate may be combined with additional conjugated backbone polymers or polymers which can be converted to a conjugated backbone polymer by blending the polymer-coated substrate with the pre­ formed polymer or by the further polymerization of monomers of the additional polymer by unmodified cata­ lyst in the presence of the polymer-coated substrate. This combination yields a desired ratio of substrate to polymer, and is useful is the fabrication of articles having a continuous conjugated backbone polymer phase containing dispersed substrate. In the preferred embodiments of this invention, the polymerization of monomers or precursors is performed in a mixture of substrates having a catalytic surface and unmodified polymerization catalyst. This combination of steps (b) and (c) yields a composite with good adhesion between substrate and the additional polymer via the polymer coating, as well as the desired weight ratio of sub­ strate to polymer. The types of monomers or precursors employed will vary widely depending on the desired conjugated backbone polymer. Useful monomers are those which are precursors in the production of conjugated backbone polymers known to those of skill in the art or monomers which form other types of polymers which can be converted into the desired conjugated backbone polymer. Illustrative of monomers used in the formation of polymers which are convertible into conjugated backbone polymers is 7,8-­ bis(trifluorometyl)tricyclo[4,2,20]deca-3,7,9-triene whose metathesis polymerization product can be converted to polyacetylene, and monomers which can be polymerized to form poly(5,6-diacetoxycyclohex-2-ene-1,4-diyl) which can be converted to poly(paraphenylene). Mixtures of monomers can be used. For example, various combinations of monomers can be employed to form conjugated backbone copolymers, or blends of one or more conjugated backbone homopolymers or copolymers with one or more conjugated backbone or non-conjugated backbone homopolymers or copolymers. As is apparent from the foregoing, monomers useful in the practice of the method of this invention can vary widely and may include monomers which can be polymerized into unsubstitued and substituted polyace­ tylene, poly(paraphenylene), poly(phenylquinoline), poly(phenylene vinylene) and the like. Other useful monomers include those which can be polymerized into conjugated backbone polymers claimed by others as useful in batteries such as monomers which form polythiophene, polyazulene, poly(phenylquinoline), polypyrrole, poly­ acenes, polyaniline, polyacenediyls, polynaphthalene, substituted derivatives, polymeric blends thereof and the like. Preferred for use in the practice of this invention are monomers which can be directly polymerized to form conjugated backbone polymers useful as battery elect­ rodes, or to form other polymers which can be converted into these conjugated backbone polmers. Conjuated backbone polymers useful as positive electrodes are conductive in their oxidized or reduced form, and are capable of reversibly inserting anions or cations. Amongst these illustrative conjugated backbone polymers, polyacetylene, poly(phenylene vinylene) and poly(p-­ phenylene) are preferred for use in negative electrodes, and polyacetylene and poly(p-phenylene) are particularly preferred for such use. Accordingly, monomers and other precursors which result in the formation of these poly­ mers are preferred and particularly preferred for use in the practice of this invention, respectively. Most preferred for use in the practice of this invention is polyacetylene and accordingly, acetylene is the most preferred monomer. In the second step of the method of this invention, the monomer or monomers are polymerized in the presence of the dispersed material. Polymerization reaction conditions for the polymers and precusor polymers described above as well known in the art. For example, useful conditions are described in detail in H. Shirakawa, et al., Polym. J. , 2 , 231 (1971); J.C.W. Chien, et al., Macromolecules , 14 , 497, (1981), (W.J. Feast et al., European Pat. publication No. 0080 329), Kovacic, J. Am. Chem. Soc. 85:454-458 (1963), and U.S. Patent No. 3,404,132. The monomer or other precursors undergo coordination polymerization to yield a conju­ gated backbone polymer or a polymer which can be con­ verted into a conjugated backbone polymer which adheres to the surface of the substrate. Insoluble polymers form particles and/or gels or films nucleated about the substrate having a catalytic surface, as for example particles of derivatized metal, alloy or other electro­ active material, and are attached to the surface of the substrates. Soluble polymers form mixtures of a solu­ tion of the polymer and the insoluble polymer-coated substrate which may be suspended in the solution if it is finely divided. If the polymer in solution is the same as or is compatible with the polymers bound onto the surface of the substrate, the articles which are cast from the solution suspension will contain polymer tightly bound to the substrate via the polymer coating. The composite of polymer and substrate can be recovered from the polymerization mixture using standard procedures. Composites of soluble polymers nucleated about substrates can be filtered to recover the insol­ ble derivatized fraction. Composites which are powders, gels, or films of insoluble polymers nucleated about derivatized substrates can be extracted with a solvent which is unreactive with the polymer and the sub­ strate. For example, in those embodiments of this invention in which the product is a continuous film of polymer having finely divided electroactive material therein or coated onto a grid of some material, such as nickel, steel, stainless steel, graphite, and the like, the film composite, is removed from the polymerization mixture, extracted with an inert solvent, and thereafter used in battery construction as an electrode in accord­ ance with conventional procedures. Illustrative of such procedures are those described in Kaner and MacDiarmid, J. Chem. Soc. Faraday Trans, 1 , 80 , 2109 (1984) and Nagatomo et al., J. Electrochem. Soc ., 132 , 1380 (1985), which are hereby incorporated by reference. As an essential component, the other anode for use in the practice of this invention is an alloy of sodium. The type of sodium alloy employed is not critical and can vary widely. Such alloys can be binary, ternary or can contain more than three components. The other component or components can be metallic or non-metal­ lic. Illustrative of alloys which are useful in the conduct of this invention are binary sodium alloys such as sodium alloys of tin, lead, silicon, antimony, bismuth, tellurium, thallium, selenium, gold, cadmium, arsenic, mercury, cesium, gallium, and the like. Also illustrative of useful alloys are ternary sodium alloys such as sodium alloys of tin and lead, antimony and lead, selenium and tellurium, and the like. Useful alloys include quaternary alloys such as solium alloys of lead, tin and bismuth. Preferred for use in the practice of this embodi­ ment of the invention are sodium alloys in which the other component or components are metals. Particularly preferred for use in the practice of this invention are alloys of sodium and one or more metals selected from the group consisting of tin, lead, antimony, bismuth, selenium, tellerium, mercury and cadmium. Amongst these particularly preferred embodiments, most preferred are ternary or binary alloys of sodium, and tin, lead, bismuth and/or antimony. The mole ratios of the components of the alloy can vary widely, depending on permissible ratios based on allowed interactions between the components and the desired capacity of the anode. In general, since sodium is the electroactive material in the anode, the greater the mole percent of sodium in the anode, the greater the capacity of the anode; and conversely, the lower the mole ratio of sodium in the anode, the lower the capa­ city. In general, since higher capacities are desira­ ble, higher amounts of sodium in the alloy are desira­ ble. Sodium as compared to lithium is readily adaptable to providing such high capacity anodes because it can form intermetallic compounds or alloys such as Na₅Pb₂, Na₁₅Pb₄, Na₅Sn₂, and Na₁₅Sn₄, which have higher sodium content. In the preferred embodiments of the invention, the mole ratio of sodium to other components in the alloy is about equal to or greater than about 0.5 to 1. In these preferred embodiments, the upper amount of sodium in the alloy is the greatest amount of sodium which can be alloyed with the other component or com­ ponents before pure metallic, un-alloyed sodium is formed. In the particularly preferred embodiments of the invention, the mole ratio of sodium to the other components in the alloy will usually vary from about 1 to about 1, to about 5 to about 1, and in the most pre­ ferred embodiments will vary from about 4 to about 1, to about 1 to about 1. The method of manufacturing the sodium alloy is not critical and can vary widely. Conventional alloying procedures are readily adaptable for use in the practice of this invention. For example, such alloys can be formed electrochemically by plating sodium onto a sub­ strate of the other components as described in more detail in N.N. Tomashova, I.G. Kieseleva and B.N. Kabanov, Elektrokhimiya, vol 8, p112 (1972) which is incorporated herein by reference. Sodium alloys can also be prepared metallurgically by melting appropriate amounts of sodium and the other components in an inert atmosphere as described in more detail in R. Kremann and P.V. Reininghaus, Z. Metallkunde , vol 12, p273 (1920) which is hereby incorporated by reference. The anode of this aspect of the invention may also include other optional materials. For example, in the preferred embodiments of invention, the anode includes one or more polymeric binders. In these preferred embodiments of the invention, the alloy is generally in particulate form, bonded together, and maintained in a composite structure by the binder. The use of the polymeric binders with the alloy in particulate form, provides for a large surface area for the sodium alloy to contact with the electrolyte media when the anode is placed in the battery electrolyte solution. Polymeric binders which are useful in the practice of this inven­ tion are those which form porous substrates to allow for contact between the particulate alloy and the electro­ lyte, and which hold the alloy in the composite during the charging and discharging of the cell. These func­ tions can be provided by a single binder or a mixture of binders can be used of which possess one or more of the desirable characteristics. Illustrative of such binders are polyphenylene, and other conjugated backbone polymers such as polythiophene, polyacetylene and the like, and nonconjugated backbone polymers, as for example polyacrylates, polymethacrylates, polyvinyls polyethylene and polypropylene. An especially useful polymer binder is polyphenylene because it swells and also becomes conductive when doped with sodium cations, in combination with polyethylene or polypropylene. However, other materials can be used as binders, pro­ vided they are porous to allow for contact between the electrolyte and the alloy and allow the alloy maintains a good electrical continuity within the anode structure, and they maintain the alloy in the composite during the charging and discharging of the cell. When swellable and dopable polymers such as polyphenylene (PPP) are used, alloys having higher sodium content are employed due to the fact that such polymers will absorb sodium from the alloy. Higher sodium content may not be needed when the swellable polymer does not take sodium from the alloy. The amount of binder used in the preferred embodi­ ments of the invention is not critical and can vary widely. Usually the amount of binder is not greater than about 40 weight percent based on the total weight percent based on the total weight of alloy and binder, and preferably from about 10 to about 30 weight percent on the aforementioned basis. The organic solvents which may be included in the electrolyte of the batteries of the present invention may vary widely and can be organic solvents normally used in batteries. Preferably, these solvents should be electrochemically inert to oxidation and reduction during use while simultaneously being capable of dis­ solving the desired alkali metal salt and providing ionic conductivity equal to or in excess of 10⁻⁴ S/cm. Examples of such useful organic solvents include propy­ lene carbonate, ethylene carbonate, sulfolane, methyl sulfolane, dimethyl sulfolane, 3-methyl-2-oxazolidone, alkane sultones, e.g., propane sultone, butane sultone (the use of sultones as electrolyte compositions is the subject of a related, commonly-assigned U.S. patent application Serial No. 556,717, and the use of sultones for coatings on polymer anodes is the subject of a related, commonly-assigned U.S. Pat. No. 4,472,489), dimethyl sulfoxide (DMSO), dimethyl sulfite, tetrahydro­ furan (THF), 2-methyltetrahydrofuran (2-MTHF), dioxane, dioxolane, 1,2-dimethoxyethane (DME), diemthoxymethane, diglymes, glymes, anisole, nitriles, (e.g., proprioni­ trile, butyronitrile, acetonitrile, benzonitrile), dichloromethane, tetraethylsulfamide, aromatic hydro­ carbons, e.g., toluene, benzene, organo phosphorus compounds, e.g., hexamethylene phosphoramide, and tri­ methyl phosphate. Mixtures of such available organic solvents may also be used, such as mixtures of sulfolane and acetonitrile, or mixtures of propylene carbonate and dimethoxyethane. The organic solvents chosen for use in any particu­ lar situation will, of course, depend upon many factors such as the precise electrolyte composition used and the voltage range desired, as well as the choice of cathode and other components of the battery used. A particu­ larly important consideration in choosing a solvent is whether the conjugated backbone polymer employed is subject to attack by the solvent. In the preferred embodiments of the invention when uncoated anodes are employed, ether-type solvents such as tetrahydrofuran, dimethoxyethane, diglyme, 2-methyltetrahydrofuran and mixtures thereof are employed because these solvents are generally not reactive with conjugated backbone poly­ mers, when in their neutral or reduced forms. Essen­ tially, any of the above-listed solvents can be used with anodes coated with solvent-resistant coatings; however, preferred for use with coated anodes are propylene carbonate, ethylene carbonate, sulfolane, 3-­ methylsulfolane and mixtures of any of the above-listed solvents, which mixtures may also include glymes, par­ ticularly dimethoxyethane. Salts for use in the electrolyte of the battery of this invention are of the formula: MA wherein: M is an alkali metal; and A is a species which is anionic in the electrolyte and stable under operational conditions. Preferred alkali metals are lithium, sodium and potassium, and the particularly preferred alkali metals are lithium and sodium. Suitable anionic species include I⁻, Br⁻, Cl⁻, C10₄⁻, PF₆⁻, AsF₆⁻, SO₃CF₃⁻, BF₄⁻, BCl₄⁻, AlCl₄⁻, alkylborates, such as B(CH₃)₄⁻, arylborates, such as B(C₆H₅)₄⁻, (the use of such borate salts with conjugated polymers being the subject of commonly assigned U.S. Patent Application Serial No. 556,721, incorporated herein by reference), POF₄⁻, CN⁻, SCN⁻, OCN⁻, CF₃CO₂⁻ (trifluoroacetate), C₆H₅CO₂⁻ (benzoate), CH₃C₆H₄SO₃⁻ (tosylate), SiF₆ = , HSO₄⁻, and the like. Preferred anions are alkylborates, arylborates, or alkylarylborates, PF₆⁻, ClO₄⁻, halide ions, SO₃CF₃⁻, and BF₄⁻, and particularly preferred anions are alkylborates, arylborates, alkylarylborates and PF₆⁻. Molten salts may also be employed as the electro­ lyte of the battery of the invention. The use of conju­ gated polymers as anodes in room-temperature molten salt batteries is described in the commonly-assigned U.S. Pat. No. 4,463,071, which is incorporated herein by reference. Room-temperature molten salts suitable for use in batteries of this invention include alkali metal halide-trialkylimidazolium chloroaluminate, alkali metal halide-dialkylimidazolium chloroaluminate, and alkali metal halide alkyl pyridinium chloroaluminate. Since in many cases the polymers, alloys, and other ion inserting materials of this invention are stable at elevated tem­ perature, intermediate temperature molten salts (M.P.<200°C) such as NaAlCl₄ or KAlCl₄, are also suitable for use. Cathodes for use in the practice of this invention are not critical and can be varied widely. Suitable cathodes include a material selected from the group consisting of graphite, intercalation compounds of graphite, high surface area carbons (>200 m²/g), transition-metal chalcogenides, and conjugated backbone polymers which are capable of being oxidized (acceptor-­ doped). Transition-metal chalcogenides and conjugated backbone polymers are preferred cathode materials. The transition-metal chalcogenides, suitable as cathode materials useful in this invention, can contain inserted alkali metals and include the transition-metal dichalcogenides such as TiS₂ and, among others, those listed on page 392 of "Lithium Batteries" edited by J.P. Gabano (Academic Press, 1983) and in K.M. Abraham, Solid State Ionics, vol. 7, pp. 199-212 (1982) (both incor­ porated herein by reference). These include (with approximate open circuit potentials measured in various organic electrolytes when fully charged or devoid of inserted cations): Suitable polymer cathodes include oxidized poly­ acetylene, poly(p-phenylene), polyacenes, poly(phenylene vinylene), polyazulene, polynaphthalene, poly(phenylene sulfide), poly(phenylene oxide), polyphenothiazine, polyaniline, polypyrrole, polythiophene, polythianthrene and substituted versions of the above. Such polymers may be coated by reaction, when oxidized, with pyrroles, thiophenes, azulenes, oxiranes, anilines or furans, as described in commonly-assigned U.S. Pat. No. 4,472,987, the disclosure of which is incorporated herein by reference. The secondary battery of this invention can be charged and discharged in accordance with the procedure described in U.S. Pat. No. 4,321,114. Such procedures are well known to those of skill in the art and will not be described herein in any great detail. The following specific examples are presented to more particularly illustrate the invention and are not to be construed as limitations therein. EXAMPLE 1 Polyacetylene (PA) powder (prepared from a catalyst of triethyl aluminum and tetrabutoxy titanium which was kept wet in toluene in a refrigerator at -40°C in an argon-filled dry box before use) was mixed with aluminum (Al) powder (-40 + 325 mesh) using a mortar and pestle. The mixture was then pressed onto expanded Ni metal in a 1/2 inch (1.27 cm) diameter stainless steel die under pressures in the range of 5,000 to 75,000 psi (34,470 to 517,050 kPa). The weights of Al and PA were .065g and .015g, respectively. This electrode was dried under vacuum before being assembled into a test cell with a lithium counter electrode, a Celgard TM separator, and LiPF₆ in tetrahydrofuran (THF) electrolyte solution. The OCV of the lithium insertion polymer electrode was 1.895V vs. Li/Li⁺ reference. The initial discharge of the cell showed a voltage behavior characteristic of PA down to a potential of 0.3V vs. Li/Li⁺. After reaching 0.3V, the cell voltage remained flat indicating the formation of the Li x Al alloy. The performance of the cell is summarized in the following Table 1 where the discharge capacity was arbitrarily set at the various values given in the second column. EXAMPLE II PA on an Al electrode was prepared by polymerizing PA by the Shirakawa technique (Polymer Journal, Vol. 2 No. 2, pp 231-244 (1971)) on expanded Al metal (wt. 10 mg, diameter 1.0 cm) with a nickel tab welded on as a lead. The PA on Al electrode was assembled into a cell with lithium in LiBBu₄ (Bu = Butyl) in THF solution and discharge at a rate of 0.5 mA/cm². The capacity obtained when the voltage reached 0.25V was 9.46 mAh. The capacity of the flat part (0.3 to 0.25V) of the cell voltage vs. time was 8.54 mAh. Assuming the flat part was completely due to Al, the utilization of Al is 86% (i.e., a final composition of Li 0.86 Al). This electrode was then used as an anode in a cell with a TiS₂ cathode (capacity 6.9 mAh) with LiBBu₄ in THF as the electro­ lytic solution. This cell was cycled between 2.3 and 1.4V at a rate of 0.5 mA/cm². The cell showed a 3.95 mAh discharge capacity and 3.83 mAh charge capacity (coulombic efficiency = 97%). EXAMPLE III A mixture of 0.4g poly(p-phenylene) (PPP) powder (prepared by the method of Kovacic), J. Am. Chem. Soc. 85 : 454-458, (1963), 0.36g LiAl alloy powder (approx. composition: Li 0.5 Al) and 0.14g Shawinigan Black, was bledded together under inert atmosphere. Then 0.03g of EPDM (ethylene-propylene-diene-terpolymer) in 4 ml of cyclohexane was added and the mixture was stirred for 1 hour. The resulting paste was brushed onto an expanded metal nickel screen and allowed to dry under argon. The resulting electrode having dimension 2 cm x 2 cm weighed 212 mg (excluding the weight of the nickel screen). A battery was then assembled employing the above electrode in a glass container as the anode (negative plate) and TiS₂ as the cathode (positive plate). The cell also contained a lithium reference electrode, and an elec­ trolyte of 1M lithium tetrabutyl borate in 2-methyl-­ tetrahydrofuran. Since the anode contained lithium originally present in the LiAl alloy, the anode ini­ tially displayed a voltage of 0.4V vs Li/Li⁺, and the cell could be considered partially charged. More lithium was added to the cell by passing 130 coul between the lithium reference and the TiS₂ electrode. The cell was then completely discharged during which the original lithium in the aluminum alloy was removed. The charge passed corresponded to an initial alloy composi­ tion of Li 0.51 Al. The cell was slowly cycled (approx. one day per half cycle) by charging by a fixed amount followed by complete discharge. The cell voltage varied between about 2.2V and 1.0V during which the potential and capacity of the anode was monitored. A large flat portion was observed in the curve of the anode potential vs. capacity curve primarily due to the capacity of the Al component. Assigning the flat portion entirely to aluminum and the varying portion entirely to PPP implies that the composition changes in the anode between 0.2V and 1.0V vs. Li/Li⁺ are equivalent to Li 0.66 Al Al and [(C₆H₄) -.25 Li⁺ .25 ] x C₆H₄ x . The capacity of the electrode on a weight basis (excluding grid) was 0.24 Ah/g or 12.6 mAh/cm². The cell was cycled six times over a 2 week period without evidencing any loss of this capacity. EXAMPLE IV A. An aluminum-polyacetylene composite film was formed by the polymerization of acetylene gas in a vigorously stirred slurry of surface derivatized alumi­ num powder in a dilute solution of Ti(O-nBu)₄/AlEt₃ (1:8) in toluene at -78°C, using a modification of the procedure described in by H. Shirakawa and S. Ikeda, Polym. J. , 2, 231 (1971) and J. Hocker (Bayer) U.S. Pat. No. 4,408,207 to produce a suspension of polyacetylene powder. Aluminum spheres ca . 20 m in diameter were heated to 465°C in vacuo for 16 hours, stirred in 10% TiCl₄ in cyclohexane at 18°C for 16 hours, washed three times in fresh cyclohexane and vacuum dried to bond a component of an acetylene polymerization catalyst (dis­ tilled TiCl₄ is a polymerization catalyst; see Kambara, Katano & Hosoe, J. Chem. Soc. Japan, Ind. Chem. , 65 , 720 (1962)) to the aluminum spheres via their oxide layer forming the derivatized aluminum spheres. A 500 mL 3-­ necked reactor equipped with a mechanical stirrer was charged with 2g of derivatized Al powder, 50 mL toluene, 0.34 mL AlEt₃, and 0.1 mL Ti(O-nBu)₄ under a constant flow of dry nitrogen. The reactor was cooled to -78°C and vigorous stirring was established before acetylene gas was added to the N₂ flow to make a 1:1 mixture of gases. Polymer particles, which were in part nucleated about the derivatized Al powder, were formed imme­ diately. After ca . 10 min., the stirring causes these particles to be aggregated on the reactor wall forming a smooth film. Scanning electron micrographs indicate a uniform distribution of particles through the film thickness as well as intimate contact between Al metal and polymers fibrils. B. A 1.5-cm² film weighing 30 mg and having a gross composition of (CHAl 1.5 ) x prepared as in Step A. Step A was electrochemically reduced and reoxidized in an electrolyte of IM LiBBu 4 /THF versus a lithium metal counter electrode. During the constant current cycle at 0.33 mA/cm², the composition of the electrode varied from CHAl 1.5 to Li 0.6 CHAl 1.5 and back to Li 0.07 CHAl 1.5 corresponding to a utilization of about 6 mAh/cm² or 380 mAh/g. The initial stage of reduction to Li 0.12 CHAl 1.5 exhibited a sloping voltage vs. charge associated with the n-doping of polyacetylene to 12 mole percent or Li 0.12 CH. The remainder of the reduction process took place at a nearly constant voltage of .28V and is attri­ buted to the alloying of Li with Al to yield a Li dis­ tribution of Li 0.12 CH(Li 0.32 Al) 1.5 . The reoxidation proceeded at ca. 0.48V until the composition was again Li 0.12 CHAl 1.5 at which point voltage began to increase as lithium was removed from the polyacetylene. A second reduction was allowed to proceed until a lower voltage limit of 0.2V was reached, at which point, the electrode composition was consistent with 100% Li alloying of the aluminum and 14% doping of the polyacetylene or Li 0.14 CH (Li 1.0 Al) 1.5 , a utilization equivalent to about 675 mAh/g. EXAMPLE V A. An aluminum-polyacetylene composite was formed by the polymerization of acetylene gas in a stirred slurry of powdered Li/Al alloy in a dilute solution of Ti(O-nBu)₄/AlEt₃ (1:4) in toluene at -78°C. Metallur­ gically prepared Li 1.0 Al alloy was pulverized in a ball mill for 16 hours. A 150 mL reactor was charged with 1g of the powdered alloy, 50 mL of toluene, 0.17 mL of AlEt₃ and finally 0.10 mL of Ti(O-nBu)₄ causing the powder to darken. After chilling to -78°C and degassing the mixture, ca . 0.5 atm. of acetylene was introduced. Since the stirring was slow and insufficient to cause powder formation, a polymer film formed at the top of the catalyst pool and incorporated some of the powdered alloy. After 14 hours, the film was washed in THF and dried. The resulting copper-colored film had a room temperature conductivity of 80 Scm⁻¹ and an open circuit voltage vs. Li of 0.76V consistent with polyacetylene n-­ doped to ca . 7% with Li⁺ as the counterion. B. A 1.0-cm² film weighing 16.5 mg and having an initial composition of Li 0.07 CHAl 0.07 prepared as in Step A was electrochemically reduced and reoxidized in an electrolyte of 1M LiBBU₄/THF versus a Li metal counter electrode after first stripping away the origi­ nal Li content. During the first cycle at 0.5 mA/cm² between voltage limits of 2.5 and 0.2V, the electrode composition varied from CHAl 0.07 to Li 0.19 CHAL 0.07 and back to CHAl 0.07 . The initial stage of reduction to Li 0.12 CHAl 0.07 exhibited the sloping voltage vs. charge associated with n-doping polyacetylene to 12% or Li 0.12 CH. The remainder of the reduction process took place at a nearly constant voltage of 0.3V attributed to the alloying of Li with Al to yield a Li distribution of Li 0.12 CH(LiAl) 0.07 . The reoxidation proceeded at 0.45V until the composition was again Li 0.12 CHAl 0.07 at which point, the lithium content was exhausted and the poly­ acetylene began to undope. An additional 29 cycles between 0.2 and 1.5V exhibited the same voltage charac­ teristics and 100% coulomb efficiency throughout. The utilization ranged from 4.4 mAh/cm² on the fifth cycle to 4.1 mAh/cm² on the fifteenth cycle to 3.8 mAh/cm² on the thirtieth cycle. The amount of Li cycled on the last cycle between the voltage limits of 0.2 and 1.5V was 83% of that observed on the first cycle within the same voltage range. EXAMPLE VI A. An aluminum-polyacetylene composite was pre­ pared by the polymerization of acetylene in a rapidly spinning cylindrical reactor (100 mm I.D. x 120 mm) containing 20g derivatized Al powder (50-1000 um), 35 mL of toluene, 3.5 mL triethyl aluminum, 2.0 mL of titanium tetrabutoxide, and a derivatized cyclinder of expanded nickel screen (314 mm x 120 mm) fitted closely to the inside wall of the reactor. After chilling to -79°C and degassing the catalyst mixture, the reactor was rotated about its axis such that the aluminum/catalyst slurry was uniformly distributed on the reactor wall completely immersing the nickel screen. Both the Al powder and the nickel screen had been dried in vacuo at 450°C and reacted with TiCl₄ as in Example IV. A pressure of 500 torr (66.5 kPa) of C₂H₂ was maintained for 3 hours which allowed the polymer to form throughout the volume of the catalyst-Al slurry, thereby encasing both the Al powder and the nickel screen. After repeated THF washes, two 3.5 cm² samples each weighing ca . 0.22g (0.025g (CH) x , 0.055g Ni, 0.140g Al) were reduced by reaction with a 0.1M solution of sodium naphthalide in THF, washed again in THF, and exposed to 400 torr (53.2 kPa) of ethylene oxide for 1/2 hour to produce poly(ethylene oxide) at the polyacetylene surfaces (U.S. Pat. No. 4,472,487). Following a final THF wash to remove unbonded poly(ethylene oxide), the samples were employed as anodes in the battery cell described in Section B, below. B. A battery cell having an anode comprised of aluminum powder-polyacetylene (CHAl n ) x composite prepared as in Step A which had been surface modified, lithium cobalt dioxide cathode, and an electrolyte of lithium perchlorate in propylene carbonate was charged and deeply discharged 36 times at 1.4 mA/cm² of anode (2.8 mA/cm² based on one side) in the voltage range of 3.0V to 4.1V prior to cycling the cell, consisting of two 3.5 cm² plates of (CHAl n ) x and three plates of LiCoO₂ and having a volume of 1.6 cm³, delivered 36 mA at 3.6V and 120 mA at 2.8V. The amount of charge released per cycle could be held at ca . 50 mAh but not without gradually increasing the upper voltage limit from 3.9 to 4.1V. The onset of the 20mA discharge was at ca . 3.85V and sloped gradually to 3.5V before turning down to the cut-off voltage; the average value of the discharge voltage was ca . 3.7V. The coulomb efficiency remained between 98 and 100% throughout the 36 cycles. The composition of the composite ranged from an initial value of (CHAl₂) x to ca . Li 0.14 CH(Li 0.15 Al)₂ when the cell was charged and back to ca . Li 0.07 CHAl₂ with each cycle. Raising the upper voltage limit was necessary to access more of the Li stored in the LiCoO₂ cathodes because it was not being restored fully from the com­ posite anodes during recharge. This was presumably due to shedding of the large (45-2000 Mm) Al particles occurring during the alloying process and the consequent isolation of some of the Li-loaded fragments. EXAMPLE VII In a three neck round bottom flask, 0.356g of aluminum powder and 6.0g of molybdenum (VI) tetra­ chloride oxide were combined under argon. Using a syringe, 10g of benzene were added and the mixture was stirred under argon for 120 hours at room temperature. The resulting poly(p-phenylene) Al composite was washed repeatedly with benzene, acetonitrile, water, and acetone and dried under vacuum. Infrared spectra showed absorption bands characteristic of poly(p-phenylene). An electrode was fashioned by pressing a mixture of 77% poly(p-phenylene) Al composite, 13% carbon black, and 10% binder onto a nickel grid at 1000hg/cm² in a rectangular press. The electrode was then removed and heat set at 160°C. After low molecular weight oligomers were extracted, this electrode was incorporated into a half cell consisting of a lithium reference and counter electrode and 0.5M LiBBu₄ in THF as the electrolyte. The cell was cycled between 1.1V and 0.1V with respect to the lithium reference. The capacity was 575C per gram of composite of which 345C were due to Li insertion into the aluminum and 230C were due to Li insertion into the poly(p-phenylene). The average coulombic efficiency over twelve cycles was 98% and there was no loss in capacity with cycling. EXAMPLE VIII To prepare Na-Pb alloy metallurgically, proper amounts of Na and Pb were placed in a stainless steel container and heated at a temperature about 510 ± 10°C in inert atmosphere or under vacuum for a few hours and then quenched to room temperatures. the alloy was then pulverized before used. Na-Pb alloy of the following composition NaPb₃, Na₅Pb₂ and Na₁₅Pb₄ were prepared using the method described as above. Their electro­ chemical potentials relative to Na were measured using electrometer in the appropriate electrolyte solutions containing sodium ions and listed in Table 1 as follows: EXAMPLE IX Metallurgically formed Na-Pb alloy powder of the composition Na₁₅Pb₄ (32 mg) was pressed onto the expanded nickel metal and used as an electrode. The potential of this electrode was measured while stripping 83% of the Na in the Na₁₅Pb₄ alloy away from the electrode. The potential vs the amount of sodium stripped from the electrode was plotted. Several potential plateaus were observed from the plot. This indicated that Na₁₅Pb₄ and other binary alloys formed during the stripping procedure corresponded well with the potentials measure in Example 1 and with their respective compositions. Less than 100% Na stripping from the alloy was due to the loss alloy resulted from the volume change. EXAMPLE X Sodium alloy can also be formed elecrochemically by plating Na onto Pb foil. By plating Na on Pb foil at a current density of 50 micramp /cm², Na-Pb alloy of various compositions were shown as several potential plateaus. The potential of these plateaus: 0.5, 0.34, 0.17 and 0.12V corresponded well with the values measured in Example 1. EXAMPLE XI Na ternary alloy containing Pb and Sn was prepared by heating the proper amounts of Na, Pb and Sn in a stainless steel crucible in an inert atmosphere or under vacuum at a temperature about 510 ± 10°C for few hours and then quenching to room temperatures. The resulting ternary alloy had the following composition NaPb .26 Sn .74 and a potential of .25 vs Na/Na⁺. EXAMPLE XII A Na alloy electrode was prepared by mixing the NaPb .26 Sn .74 alloy of Example XI in powdered form with 10 weight percent of polyphenylene (PPP) and 10 weight percent of polypropylene binder. The mixture was then pressed onto expanded nickel metal and heated at 160°C for 10 to 20 minutes under vacuum or in an inert atmos­ phere. A cell was constructed which consisted of the anode (68 mg on an area of 0.6 x 2.4 cm²) whose preparation is described above and a Na x CoO₂ cathode was assembled using glass filter paper to separate the two electrodes. The electrolyte solution used was 1.25 M NaPF₆ in DME. Before cycling, 3.77 mAh capacity was added to the anode. This amount of charge was obtained by charging the Na x CoO₂ cathode and plating sodium from the auxilliary sodium electrode. The final potential of this electrode was about .10V. The cell was then cycled at a rate of 0.5 mA/cm² in the voltage range of 3.2 to 2.2V (Na x CoO₂ vs alloy anode) for 22 cycles. The cell was further cycled at a rate of 1.0 mA/cm² in the same voltage range from the 23rd to the 87th cycle. The potential profile of the anode (vs Na/Na+) vs capacity at selected cycles was plotted. The plot indicated that the discharge capacity of the cell decreased from 4.39 mAh at the first cycle to 3.59 mAh at the 21st cycle, 3.35 mAh at the 24th cycle, 3.07 mAh at the 50th cycle and 2.84 mAh at the 87th cycle. The coulombic efficiency of each cycle was varied from 97 to 99%.

Claims: 1. A battery comprising: (a) an electrolyte comprising an organic solvent and an alkali-metal salt, and (b) a cathode; (c) an anode comprising an anode active material selected from the group consisting of: (i) metals which alloy with sodium cations in said electrolyte; and (ii) mixtures of one or more conjugated backbone polymers and one or more electroactive materials selected from the group consisting of metals which alloy with alkali metals and alkali metal cation inserting materials; said alkali-metal cations from said electrolyte being inserted into said anode as a metal alloy or as an inserted ion in said alkali metal cation inserting material during the charging of said battery and said alkali metal in said alloy or said alkali metal inserting material dissolving in said electrolyte during the discharging of said battery. 2. A battery according to claim 1 wherein said anode active material is selected from the group con­ sisting of mixtures of one or more conjugated backbone and one or more electroactive materials selected from the group consisting of metals which alloy with alkali metal. 3. The battery of claim 2 wherein said polymer is polyacetylene or poly(p-phenylene). 4. The battery of claim 2 wherein said alkali-­ metal salt of said electrolyte is a lithium salt, sodium salt or mixture thereof, and said metal is aluminium, lead, tin or tin-lead alloys. 5. The battery of claim 4 wherein said metal salt is a lithium salt and said metal is aluminum. 6. The battery of claim 4 wherein said metal salt is a sodium salt and said metal is lead, tin or lead-tin alloys. 7. A battery according to claim 1 wherein said anode consist essentially of said sodium alloying metal. 8. A battery according to claim 7 wherein said alloys and selected from the group consisting of ternary or binary alloys of sodium and one or two metals selected from the group consisting of tin, lead, bismuth, and antimony. 9. A battery according to claim 8 wherein said alloy is a binary alloy of sodium and lead, or sodium and tin, or a ternary alloy of sodium, tin and lead. 10. A battery according to claim 7 wherein said anode comprises a composite comprising said alloy in particulate form dispersed in one or more polymeric binders at least one of said binders is swellable by said battery electrolyte and allows electrical con­ tinuity between all or a part of the dispersed alloy. 11. A battery according to claim 10 wherein said binders are polyphenylene in combination with polyethylene or polypropylene. 12. A process of fabricating a battery anode which comprises an intimate mixture of a finely divided electroactive material in a matrix composed of a conjugated backbone polymer, said method comprises the steps of: (a) derivatizing the surfaces of a finely divided material selected from the group consisting of alkali-­ metal alloying metals and alkali metal inserting materials with a catalyst for conjugated backbone polymers or a catalyst for polymers which can be converted into a conjugated backbone polymer; (b) dispersing said derivatized metal or material in a gas, suspension or solution of one or more monomers or other precusors for said polymer and polymerizing said monomers or other precursor in the presence of said finely divided metal or material having polymer coated to the surface thereof; (c) polymerizing additional monomer, monomers or other precursors in the presence of polymer coated metal or material to provide a predetermined polymer to metal or material weight ratio; and (d) recovering said polymer coated metal or material or a combination of polymer and polymer coated metal or material from said solution or suspension and fabricating same into a cohesive solid. 13. A method according to claim 12 wherein said monomers or other precusors are selected from the group consisting of those which can be polymerized into poly(p-phenylene) and polyacetylene. 14. A process according to claim 12 wherein said substrate is selected from the group consisting of aluminum, lead, tin and tin/lead alloy.

Inventors: GOULD, SHARON, JOW, TAIGUANG RICHARD, MAXFIELD, MACRAE, SCHACKLETTE, LAWRENCE WAYNE, TOTH, JAMES EDWARD
Applicants: ALLIED-SIGNAL INC. (A DELAWARE CORPORATION)
Application year: 1986
Main classification: H01M4
IPC codes: H01M10, H01M4, H01M6