CONJUGATED POLYMER AS SUBSTRATE FOR THE PLATING OF ALKALI METAL IN A NONAQUEOUS SECONDARY BATTERY

Abstract: This invention relates to a novel anode for use in batteries, and to batteries containing the anode, which anode comprises of an electronically conductive n-doped conjugated backbone polymer having finely divided elemental alkali metal particles dispersed therein.

Description: This invention relates to batteries having polymeric electrodes. More particularly, this invention relates to non-aqueous secondary batteries having negative electrodes composed of conjugated backbone polymers and alkali metals which are plated on or distributed throughout the polymer matrix. Conjugated backbone polymers, e.g, polyacetylene, polyphenylene, polyacenes, polythiophene, poly(phenylene vinylene), polyazulene, poly(phenylene sulfide), poly(phenylene oxide), polythianthrene, poly(phenylquinoline), polyaniline, poly(N-methyl carbazole), and polypyrrole, have been suggested for use in a variety of applications based upon their characteristic of becoming conductive when oxidized or reduced either chemically or electrochemically. The secondary battery application described by, e.g., MacDiarmid, et al. in US-A-4 442 187; J. de Physique , Colloque C3, Vol. 44 (1983), articles beginning on page 579, page 615 and page 537; and K. Kaneto, et al., Japanese J. of Applied Physics , Vol. 22, pp. L567-L568 (September 1983) and pp. L412-L414 (July 1983), employs one or more electrodes having conjugated backbone polymers as the electroactive material. Such electrodes can, for example, be electrochemically n-doped by reversible insertion of alkali metal cations or tetraalkylammonium cations during battery cycling, most commonly with insertion of cations into a polymer anode (the negative battery electrode) occurring during charging. The more such cations are inserted, the more conductive the electrode becomes and the more cathodic the potential of the anode becomes. This electrochemical doping process is described by MacDiarmid, et al. in US-A-4 321 114. Lithium and lithium alloys have been suggested for use as the negative electrode in electrochemical cells. For example, US-A-4 002 492 discloses electrochemical cells having an anode consisting essentially of lithium aluminum alloys that contain lithium in amounts between 63% and 92% and the balance essentially aluminum. Anodes composed of lithium and aluminum are also disclosed in Rao, et al., J. Electrochem. Soc. 124 , 1940 (1977), and Besenhard, J. Electroanal. Chem., 94 , 77 (1978). An application of Matsushita (Kokai 58-163184) discloses the use of electroconductive polymer as a covering at the surface of the electrode to protect against short circuiting because of dendrite growth. EP-A-0070107 Murphy, et al., J. Electrochem. Soc. , 126 , 349 (1979) and Murphy, et al., Mat. Res. Bull. , 13 , 1395 (1978) disclose batteries based on lithium intercalation in layered dichalcogenides for use as cathodes. Composite structures of a conjugated backbone polymer and a non-electroactive material have been described in US-A-4 294 304 and in the above J. de Physique issue, articles beginning on page 137 and on page 151. Representative other components that have been blended with polyacetylene or onto which polyacetylene or polypyrrole have been deposited include polyethylene, polystyrene, graphite, carbon black, NESA glass and silicon. In selected instances, such composite structures have been suggested for use in batteries, see Showa Denko K. K., EP-A-0 076 119. While batteries have heretofore been constructed in which a conjugated backbone polymer comprises the largest part of the electroactive material, such batteries suffer from a number of disadvantages. For example, such cells have heretofore exhibited strongly varying discharge potentials. Moreover, such cells have relatively low volumetric energy densities. Batteries to be used at room temperature which are constructed with anodes composed of lithium or lithium alloys such as lithium/aluminum alloys, also suffer from a number of disadvantages. While lithium is inherently rechargeable, it's practical rechargeability is poor because at practical current densities metallic lithium is electrodeposited in the form of dendrites which can eventually lead to shorting out the cell. High discharge rates can also result in irreversible shape changes in the electrode. In order to minimize the effects of dendritic growth, it has been suggested to employ cell separators, such as permeable membranes or the composite of JP-A-58-163184, which act as physical barriers to dendritic growth. Although these solutions are initially effective, eventually the lithium dendrites may penetrate the barriers and establish transient or permanent electronic shorts. It has been suggested that use of alloys of lithium with a less reactive metal, as for example, alloys of lithium and aluminum obviate certain of the disadvantages attendant to the use of lithium as the anodic material. See, for example, US-A-4002492. However, such batteries have exhibited relatively low capacities (utilization), low rate capabilities and poor cycle lifes. Generally speaking, the present invention obviates one or more of the disadvantages of polymer batteries, and lithium and lithium alloy anode batteries by providing an improved anode for high energy density electrochemical cells which include a cathode containing a cathode active material, an anode containing an anode active material, and a non-aqueous electrolyte having an ionic salt of the anode active material dissolved therein. More particularly, this invention provides a battery comprising an anode, a cathode and an electrolyte comprising an organic solvent containing a dissolved alkali metal salt. According to the invention, the anode comprises a porous conjugated backbone polymer substrate having a porosity of at least 20 volume percent, with an alkali metal in zero valent state dispersed through the substrate, the amounts of polymer and alkali metal in the charged state of the battery being 50 to 95 percent by weight of polymer, and correspondingly 5 to 50 percent by weight of alkali metal, based on total weight of polymer and alkali metal. If desired, the porous conjugated backbone polymer or copolymer can be blended with one or more conjugated or non-conjugated backbone polymers. The conjugated polymer components are in a reduced (n-doped) electronically conductive form during at least part of the battery cycle, having dispersed therein the elemental alkali metal. The alkali-metal cations in said electrolyte diffuse into said porous polymer or copolymer and are deposited as elemental alkali metal during at least part of the charging cycle of said battery, and converted into alkali metal cations during the discharging of said battery. As an essential component, the battery of this invention includes an anode which comprises a mixture of one or more porous conjugated backbone polymers or copolymer, or blends of one or more conjugated polymers or copolymers with one or more conjugated or non-conjugated backbone polymers or copolymers (hereinafter referred to collectively as "conjugated backbone polymers"), with at least one or said conjugated backbone polymers being capable of electrochemical n-doping (insertion by alkali metal cations) to an electronically conductive state (≧10⁻³s/cm), and which polymers, copolymers or blends having dispersed therein elemental alkali metal. The structure of this anode can vary widely. For example, the anode can be in the form of a porous film of the conjugated backbone polymer with the elemental alkali metal being dispersed therein. In the preferred embodiments, the anode is comprised of compressed powders of conjugated backbone polymers filled by elemental alkali metal which has been electrodeposited by reduction of alkali metal ions in a suitable non-aqueous electrolyte at sufficiently low current density to achieve the desired dispersion of elemental alkali metal within the body of the electrode. Useful polymers may be any of the variety of electrochemically n-dopable conjugated backbone polymers known to those of skill in the art for use as negative electrodes in batteries. In general, such polymers are sufficienlty porous to allow the inflow and outflow of electrolyte solvent containing dissolved alkali metal cations, and to provide sufficient space for the deposition of elemental alkali metal inside of the conjugated backbone polymer substrate during the charging and discharging of the battery, respectively. These objectives are achieved when the porosity of the polymer is at least 20 volume percent (v/o). In the preferred embodiments of the invention, the porosity of the polymer is at least 25 volume percent (v/o), and in the particularly preferred embodiments is from 30 volume percent (v/o), to 70 volume percent (v/o). Amongst these particularly preferred are those embodiments of the invention in which the porosity of the substrate is about 50 volume percent (v/o). Furthermore, the polymer must be of sufficient molecular weight to function as a solid substrate during the charging of the battery. Useful conjugated backbone polymers may be conjugated backbone homopolymers or copolymers, or blends of one or more conjugated backbone homopolymers or copolymers with one or more conjugated backbone or non-conjugated backbone homopolymers or copolymers. Useful conjugated backbone polymers can vary widely and include polyacetylene, polyphenylene, (if in the para form), poly(phenylene vinylene) and the like, and blends thereof with other polymers having either conjugated or non-conjugated backbones, such as polyethylene or polypropylene. Other conjugated backbone polymers claimed by others as useful in batteries may also be used in the present invention. Such polymers include hydrocarbon polymers: polyazulene, poly(perinaphthalene), polyacenes, poly(naphthalene-2,6-diyl), and the like and polymeric blends thereof. Amongst these illustrative conjugated backbone polymers, polyacetylene, poly(phenylene vinylene) and poly(p-phenylene) are preferred, and polyacetylene and poly(p-phenylene) are particularly preferred. Most preferred for use in the practice of this invention is poly(p-phenylene). Useful conjugated backbone polymers are known compounds which can be prepared by conventional means. For example, high quality polyacetylene, a preferred conjugated backbone polymer, can be conveniently prepared by the procedures described in a series of papers by Shirakawa, et al., Polymer Journal , Vol. 2, No. 2, pp 231-244 (1971); Polymer Journal , Vol. 4, No. 4, pp. 460-462 (1973); Journal of Polymer Science Part A-1 , Polymer Chemistry Edition, Vol. 12, pp. 11-20 (1974), and Journal of Polymer Science Part A-1 , Polymer Chemistry Edition Vol. 13, pp. 1943-1950 (1975), all of which are incorporated herein by reference. Moreover, forms of high quality poly(p-phenylene), another preferred conjugated backbone polymer, can be prepared by the method of Kovacic described in detail in J. Am. Chem. Soc. 85 , 454-458 (1963), incorporated herein by reference. Furthermore, poly(phenylene vinylene), another preferred conjugated backbone polymer, can be prepared by the procedure described in US-A-3 404 132. The second essential component of the anode of this invention is elemental alkali metal which is distributed throughout the electrode. Preferred alkali metals are lithium and sodium, and particularly preferred for use is sodium. In the preferred embodiments of the invention, the alkali metal is electrodeposited on and/or in the conjugated backbone polymer substrate in a step prior to battery assembly or during the charging of the battery. The porosity of the polymer substrate and current density are adjusted to achieve the necessary dispersal of alkali metal throughout the bulk of the polymer substrate. The amounts of the various components in the anode can vary widely, depending on a number of factors, as for example, the balance chosen between electrochemical capacity, and the porosity of the polymer, the desired mechanical properties of the anode and the like. In general, the amount of the conjugated backbone polymer component in the anode should be sufficient to provide useful capacities and to impart mechanical stability and good life cycle life to the electrode. According to the invention, the amount of the conjugated backbone polymer component is from 50 to 95 percent by weight based on the total weight of polymer and alkali metal in the anode, and in the particularly preferred embodiments from 70 to 90 by weight, on the aforementioned basis. The anode may include other optional materials known to those of skill in the battery art, and these will not be described herein in great detail. In brief, by way of illustrative examples, the anode may include such other substituents as conductivity aids such as carbon black; inert binders such as saturated backbone hydrocarbon polymers and halocarbon polymers such as polyethylene, propylene-trifluoroethylene copolymer, and poly(tetrafluoroethylene); mechanical supports; current collectors and the like. Hydrocarbon binders such as polypropylene are generally employed with powdered forms of theconjugated polymers. The anode may also be coated with other materials to allow use of the anode with solvents which would otherwise react with the conjugated backbone polymer in the reduced state. For example, the anode can be coated with the reaction product of an oxirane compound as described in US-A-4 472 487 with the reaction product of an organsulfur compound as described in US-A-4 472 489 and with the reaction product of certain cyclic compounds as described in US-A-4 472 488. The particular polymer and alkali metal chosen for use in any particular situation may vary widely. However, in the preferred embodiments of the invention, the polymer and metal are selected such that the voltage range of reversible electroactivity of the polymer closely matches or more preferably encompasses the electrochemical potential of the alkali metal. The method of fabricating the anode is not critical and can be varied widely. Any method known to those of skill in the art for fabricating polymer substrates having porosity in the ranges of 25 to 75 volume percent can be used. In the preferred embodiments, the anode is fabricated as follows. The polymer which is conjugated or becomes conjugated in its reduced state is in the form of a dry powder, a gel, or a suspension in a suitable solvent. This conjugated polymer may be combined with other additives, such as binders and conductivity aids. This mixture is mechanically or ultrasonically blended or ground together to form an intimate mixture of small particles (less than 10 µm). This mixture is then compressed onto a current collector into the desired shape of the electrode. In some instances, it may be further desirable to carry out a final heat setting step. The conditions of the final pressing and heat setting step are adjusted to achieve the desired porosity. The conjugated polymer of this electrode may be chemically or electrochemically reduced to an n-type conducting state, preferably after electrode fabrication, but either before or after cell or battery assembly. Finally, excess alkali metal in a zero-valent state (elemental alkali metal) is added to the electrode preferably by electrodeposition either prior to final assembly or during the charging of said battery or electrochemical cell. The current density for the electrodeposition must be maintained at a sufficiently low value to avoid the production of dendrites at the electrode surface and to achieve a dispersal of alkali metal within the interior of the porous electrode. The organic solvents which may be included in the electrolyte of the batteries of the present invention may vary widely and can be organic solvents normally used in batteries. Preferably, these solvents should be electrochemically inert to oxidation and reduction during use while simultaneously being capable of dissolving the desired alkali metal salt at a concentration of preferably about 0.5M and more preferably about 1M, capable of wetting the polymer, and providing an ionic conducitivity equal to or in excess of 10⁻⁴S/cm, preferably equal to or greater than 10⁻²S/cm. Examples of such useful organic solvents include propylene carbonate, ethylene carbonate, sulfolane, methyl sulfolane, dimethyl sulfolane, 3-methyl-2-oxazolidone, alkane sultones, e.g., propane sultone, butane sultone (the use of sultones as electrolyte compositions is the subject of a related, commonly-assigned U.S. Patent Application Serial No. 556,717, now US-A-4 528 254, and the use of sultones for coatings on polymer anodes is the subject of a related, commonly-assigned US-A-4 472 489), dimethyl sulfoxide (DMSO), dimethyl sulfite, tetrahydrofuran (THF), 2-methyltetrahydrofuran (2-MTHF), dioxane, dioxolane, 1-2-dimethoxyethane (DME), dimethoxymethane, diglyme and glymes. Mixtures of such available organic solvents may also be ued, such as mixtures of sulfolane and dimethoxyethane, or mixtures of propylene carbonate and dimethoxyethane. The organic solvents chosen for use in any particular situation will, of course, depend upon many factors such as the precise electrolyte composition used and the voltage range desired, as well as the choice of cathode and other components of the battery used. A particularly important consideration in choosing a solvent is whether the n-doped conjugated backbone polymer employed is subject to attack of the solvent. In the preferred embodiments of the invention when either coated or uncoated anodes are employed, ether-type solvents such as tetrahydrofuran, dimethoxyethane, diglyme, 2-methyltetrahydrofuran and mixtures thereof are employed because these solvents are generally not reactive with conjugated backbone polymers, when in their neutral or reduced forms. Salts for use in the electrolyte of the battery of this invention are of the formula: MA wherein: M is an alkali metal cation; and A is a species which is anionic in the electrolyte and stable under operational conditions. Preferred alkali metal cations are lithium, sodium and potassium, and the particularly preferred alkali metal cations are lithium and sodium. Amongst these particularly preferred embodiments sodium is the most preferred cation. Suitable anionic species include I⁻, Br⁻, Cl⁻, ClO₄⁻, PF₆⁻, AsF₆⁻, BF₄⁻, BCl₄⁻, AlCl₄⁻, alkylborates, such as B(C₆H₅)₄⁻, fluorinated organoborates, and organofluoroborates, such as B(p-FC₆H₄)₄⁻ and F₂B(C₆H₄)₂⁻, sulfonates, such as CF₃SO₃⁻, CF₃(C₆H₄)SO₃⁻, C₆H₄SO₃ and CH₃(C₆H₄)SO₃⁻, POF₄⁻, CN⁻, SCN⁻, OCN⁻, CF₃CO₂⁻ (trifluoroacetate), C₆H₅CO₂⁻ (benzoate), HSO₄⁻ and the like. Preferred anions are organoborates such as alkylborates, arylborates, or alkylarylborates, PF₆⁻, ClO₄⁻, fluoroborates and sulfonates such as CF₃SO₃⁻, CH₃(C₆H₄)SO₃⁻ and C₆H₄SO₃⁻, and particularly preferred anions are alkylborates, and arylborates, alkylaryl borates and PF₆⁻. Cathodes for use in the practice of this invention are not critical and can be varied widely. Suitable cathodes include materials selected from the group consisting of graphite, intercalation compounds of graphite, high surface area carbons (>200 m²/g), polymers which are capable of being oxidized (acceptor-doped). Transition-metal chalcogenides and conjugated backbone polymers are preferred cathode materials, especially those having an operating voltage about equal to or greater than 1.5V with respect to the anode. The transition-metal chalcogenides, suitable as cathode materials useful in this invention, can contain inserted alkali metals and include the transition-metal dichalcogenides such as TiS₂ and, among others, those listed on page 392 of "Lithium Batteries" edited by J. P. Gabano (Academic Press, 1983) and in K. M. Abraham, Solid State Ionics, Vol. 7, pp. 199-212 (1982) (both incorporated herein by reference). These include (with approximate open circuit potentials measured in various organic electrolytes when fully charged nearly or devoid of inserted cations): Na x TiS₂ 2.1V versus Na/Na⁺ Na x NbS₂Cl₂ 2.2V versus Na/Na⁺ Li x MoS₂ 2.3V versus Li/Li⁺ Li x Fe 0.25 V 0.075 S₂ 2.4V versus Li/Li⁺ Li x TiS₂ 2.5V versus Li/Li⁺ Li x MoS₃ (amorphous) 2.5V versus Li/Li⁺ Na x WO 3-y 2.6V versus Na/Na⁺ Na x MoS₃ (amorphous) 2.7V versus Na/Na⁺ Na x TaS₂ 2.7V versus Na/Na⁺ Li x MoO₃ 2.8V versus Li/Li⁺ Li x V₆O₁₃ 2.9V versus Li/Li⁺ Li x Cr 0.5 V 0.5 S₂ 2.9V versus Li/Li⁺ Li x W 0.2 V 2.8 O₇ 3.0V versus Li/Li⁺ Li x Cr₃O₈ 3.6V versus Li/Li⁺ Na x CoO₂ 3.7V versus Na/Na⁺ Li x CoO₂ 4.7 versus Li/Li⁺ Suitable polymer cathodes include oxidized polyacetylene, poly(p-phenylene), polyacenes, poly(phenylene vinylene), polyazulene, polynaphthalene, poly(phenylene sulfide), poly(phenylene oxide), polyphenothiazine, polyaniline, polypyrrole, polythiophene, polythianthrene and substituted versions of the above. Such polymers may be coated by reaction, when oxidized, with pyrroles, thiophenes, azulenes, anilines or furans, as described in US-A-4 472 988. The secondary battery of this invention can be charged and discharged in accordance with the procedure described in US-A-4 321 114. Such procedures are well-known to those of skill in the art and will not be described herein in any great detail. The following specific examples are presented to more particularly illustrate the invention. EXAMPLE I A. Using the method of Migazaki, et al. Syn Metals 6 211-217 (1983), Na x CoO₂ was synthesized in accordance with the following equation: Co₃O₄ + 3/2 Na₂O₂ ------> 3 NaCoO₃ + 1/2 O₂ ↑ In this procedure, Na₂O₂ (Alfa Products, purity: 93% min.) and Co₃O₄ (Cerac, purity: 99.5%) were combined in a 1.5:1.0 molar ratio and thoroughly mixed in a blender. The mixture was then heated to 500°C in a quartz tube for 36 hrs. in air. Some etching of the quartz was observed. Later analysis suggested that a composition, Na 0.8 CoO₂, had been obtained. Subsequent treatment with sodium benzophenone ketyl raised the sodium content to approximately NaCoO₂. Teflon® binder was recovered from DuPont TFE-fluorocarbon Resin Dispersion, Product Type 30 by addition of acetone. After the teflon had settled out, it was filtered, washed with additional acetone and air dried. B. A mixture of 85% NaCoO₂ (prepared as described in section A) 10% Shawinigan black and 5% Teflon® #30 (total mass ∼50mg) was ground with a mortar and pestle until it formed a single cohesive mass. The film-like material was then folded upon itself, wetted with 2-propanol and pressed between 2 polished stainless-steel plates at ca. 100 MPa for 3 s. The material was then folded upon itself once again, rewet, and repressed. This procedure was repeated for a total of 3 times, after which the NaCoO₂ was pressed onto a preweighed platinum screen (0.7 x 2.5 cm²). The electrode was then vacuum dried at 25°C for 12 hrs. A cell was assembled with a sodium counter electrode in an electrolyte of 1.3M NaPF₆, DME. The NaCoO₂ electrode was cycled twice at a current of 0.5mA (0.3 mA/cm²) between the voltage limits of 3.6 to 2.0V vs Na/Na⁺. The capacity was 4.4 mAh (2.5 mAh/cm²) which was equivalent to a composition change from NaCoO₂ to Na 0.58 CoO₂ or approximately 85% of theoretical capacity for the voltage limits used. C. Poly(p-phenylene), PPP, was synthesized by the method of Kovacis, J. Org. Chem. 29 , 100 (1964), using an AlCl₃, CuCl₂ catalyst. Pulpex™ polypropylene synthetic pulp was acquired from Hercules. A mixture of 80% PPP, 10% Shawinigan Black™ and 10% Pulpex P was thoroughly blended then pressed onto pre-weighed nickel grid at 27.5 MPa in a rectangular press (0.7 x 2.5 cm²). The electrode was then removed and heat set at 160°C for 15 mins. in air. D. Sodium hexafluorophosphate, NaPF₆, obtained from Alfa Ventron was dried under vacuum for 24 hours at 100°C. Dimethoxyethane, DME, which had been dried by vacuum distillation from a solution with sodium benzophenone ketyl was added to the NaPF₆ to form a 1.3 molar solution. This solution was further purified by stirring over a liquid amalgam of sodium and mercury. Finally, the solids were allowed to settle and the purified electrolytic solution was removed. E. A battery was assembled as follows. Each of the PPP anode described in Section C and NaCoO₂ cathode described in Section B was wrapped with glass filter paper and inserted into a glass container. The container was evacuated and taken with an Argon-filled dry box. The electrolyte, 1.3M NaPF₆, DME, whose preparation is described in Section D, was added in an amount sufficient to fully cover both electrodes. EXAMPLE II As assembled, the battery of Example I contained enough sodium for approximately 80% theoretical capacity (4 mAh) if no sodium were lost to reaction with impurities during initial cycling. More sodium (2.5 mAh) was added by inserting a third electrode composed of sodium and passing charge between this sodium electrode and the PPP electrode. The cell (PPP vs NaCoO₂) was cycled between fixed voltage limits, 3.6 to 1.6V, at a current of 1 mA (0.6 mA/cm²) for the first 8 cycles (the sodium reference being removed after cycle #5), then at 2 mA (1.2 mA/cm²) until cycle number 172 and then at 1 mA until cycle number 223 where cycling was terminated. Because excess sodium was added, it was found on the 8th cycle that the PPP electrode attained a potential of OV vs Na/NA⁺ with sodium metal being plated and stripped from this electrode over about 75% of its observed 4 mAh capacity (i.e., about 3 mAh of sodium was being plated and stripped as sodium metal on each cycle). On cycle #194 when the overall capacity of the cell had declined to about 3 mAh, sodium metal was still being plated and stripped over about 75% of the cell's capacity (2.25 mAh). Thus, very little sodium metal was lost in the 194 cycles and high efficiency for sodium plating and stripping on a PPP substrate has been demonstrated. No evidence for shorting due to sodium dendrites was found over the entire 223 cycles. EXAMPLE III A half cell was assembled which comprised a PPP electrode constructed as in Example I and a sodium reference and counter electrode in an electrolyte of 1M NaPF₆ in DME. An initial cycle was made between 1.5 and 0.0 volts vs Na/Na⁺ such that Na⁺ ions were inserted and extracted from PPP without the plating of sodium metal. Three more cycles were then made (summarized in the Table I below) which involved both the insertion and extraction of Na⁺ ions in PPP and plating of sodium metal on the electronically conductive substrate comprised of the sodium ion complex with PPP. The cycling results demonstrate high efficiency for the plating and stripping of sodium from a conductive PPP substrate. COMPARATIVE EXAMPLE IV A battery was assembled as described in Example I with a sodium metal anode containing no conjugated polymer , NaCoO₂ cathode, and 1.3M NaPF₆, DME electrolyte. The cell was cycled between fixed voltage limits, 3.6 to 2.0, at a current of 1mA (0.6 mA/cm²). Upon the fifth charging cycle, the cell could not attain a voltage of 3.6 even after passing charge equivalent to three times the theoretical capacity. Disassembly of the cell revealed that sodium had grown through the glass filter paper and connected the sodium anode to the NaCoO₂ cathode causing an internal short.

Claims: A battery comprising an anode, a cathode and an electrolyte comprising an organic solvent containing a dissolved alkali metal salt, characterised in that the anode comprises a porous conjugated backbone polymer substrate having a porosity of at least 20 volume percent, with an alkali metal in zero valent state dispersed through the substrate, the amount of polymer in the charged state of the battery being 50 to 95 percent by weight of polymer based on total weight of polymer and alkali metal. A battery according to claim 1 characterised in that backbone polymer is polyacetylene or poly(p-phenylene). A battery according to claim 1 or 2 characterised in that the alkali metal salt of said electrolyte is a lithium salt, sodium salt or mixture thereof. A battery according to anyone of claims 1 to 3 characterised in that the metal salt is selected from alkali metal organoborate salts, hexafluorophosphate salts, fluoroborate salts, organosulfonate salts, perchlorate salts and halide salts. A battery according to claim 4 characterised in that said salt is selected from the group consisting of alkali metal alkylborate, arylborate, arylalkylborate and hexafluorophosphate salts. A battery according to any one claims 1 to 5 characterised in that the cathode is a transition metal chalcogenide. A battery according to claim 6 characterised in that said chalcogenide is Li x TiS₂, Li x V₆O₁₃, Li x MoS₂, Li x CoO₂ or Na CoO₂. A battery according to any one of claims 1 to 7 characterised in that the solvent is an ether or a mixture of ethers.

Inventors: ELSENBAUMER, RONALD LEE C/O ALLIED CORPORATION, SHACKLETTE, LAWRENCE WAYNE C/O ALLIED CORPORATION, TOTH, JAMES EDWARD C/O ALLIED CORPORATION
Applicants: ALLIED-SIGNAL INC. (A DELAWARE CORPORATION)
Application year: 1986
Main classification: H01M10
IPC codes: H01M4, H01M10