CERAMIC PAINT COMPOSITION

Abstract: This invention relates to a ceramic paint composition comprising a mixture of metal oxides which together act as a coloring agent for the ceramic paint. The metal oxides are nonreactive with one another and nonreactive with any elements or compounds they come in contact with while being heated to temperatures in a range up to 704°C. A low melting point glass frit is also included in the paint composition. A metal oxide powder having at least a low valence oxidation state and a high valence oxidation state is also included in the paint composition. The metal oxide is included in the ceramic paint composition in its low valence oxidation state. A vehicle is mixed with the metal oxides, the low melting point glass frit, and the metal oxide powder having at least two valence states to form all of the mentioned materials into a ceramic paint which can be applied to a glass surface. The use of the metal oxide powder in its low valence oxidation state is credited with making the ceramic paint nonstickable with respect to fiberglass surfaces which may come into contact therewith during the forming of the glass sheet upon which the paint has been placed.

Description: This invention relates to a new ceramic paint composition. The ceramic paint composition is one which does not stick to fiberglass materials at elevated temperatures when the fiberglass is brought into contact therewith. A method of forming a glass sheet is disclosed which allows a ceramic painted glass sheet to be contacted by a fiberglass covered forming die which forms the glass in a heated condition into a desired shape. The forming operation may be carried out without any sticking of the new ceramic paint composition to the fiberglass forming die. Ceramic paint compositions are generally well known to the skilled artisan. These ceramic paint compositions can be used, for example, to form borders around the edge of glass sheets which are used as windshields, sidelites or backlites in motor vehicle. Such ceramic paints usually include a mixture of metal oxides which together act as a coloring agent for the ceramic paint. The metal oxides are nonreactive with one another and nonreactive with any elements or compounds they come in contact with while being heated to temperaturs up to about 704°C. The mixture of metal oxides can be controlled so as to get a selected color from the ceramic paint composition. Normally in automotive applications, the selected color is black. Such ceramic paint compositions also include a low melting point glass frit which generally melts at a temperature below 704°C. The low melting point glass frit is the material which bonds the mixture of metal oxides to a glass sheet and ensures that it remains after the glass sheet has been cooled back to room temperature. A vehicle is normally mixed with the metal oxides and low melting point glass to allow the ceramic paint composition to be applied in a paint application process. For example, if the paint application process is a silk screen printing operation, the vehicle may be an organic medium which forms the vehicle for carrying the other materials during the silk screen printing operation. Many different types of ceramic paint compositions of the above general type are well known to skilled artisans. The exact metal oxides and low melting point glass frit and vehicle selected for such paints is well within the skill of artisans in this area. The manner in which the different materials may be varied in order to achieve the results desired in a particular application is again well within the skill of an artisan. However,it is found that in the situation where a sheet having a ceramic paint thereon was contacted by a fiberglass forming die that ceramic paints of the above described general composition had a great tendency to stick on the fiberglass covered die. It is, of course, obvious that the sheet of glass has to be heated to an elevated temperature, generally less than 1300°F, so that it may be engaged by a forming die and formed into a configuration other than flat. Thus, the difficulty arose that the ceramic paint compositions generally known to skilled artisans would not operate in a glass forming process in which a heated glass sheet containing the ceramic paint composition was engaged by a fiberglass covered forming die. No other materials are known for covering the forming die because the fiberglass is the only material which will withstand the heat and rigorous requirements of the environment to which it is subjected. Other materials that have been used to cover forming dies quickly break down and wear out when repeatedly brought into engagement with the surface of a heated glass sheet. Thus, fiberglass is the material which is used to cover forming dies and this material unfortunately sticks to the ceramic paint compositions known to skilled artisans when those compositions are heated to an elevated temperature necessary in order to form glass by a forming die. Thus, a problem was one of developing a ceramic paint composition which could withstand high temperatures and repeated engagements of painted glass sheets by a forming die without paint sticking to the forming die. This problem has been solved by the addition of a material to the ceramic paint composition which provides for a nonstick barrier between the heated ceramic paint composition on a heated glass sheet and a fiber glass forming die coming into contact therewith. According to the present invention there is provided a ceramic paint composition comprising a mixture of metal oxides which together act as a coloring agent for the ceramic paint, said metal oxides being nonreactive with one another and nonreactive with any elements or compounds they come in contact with while being heated to temperatures in a range up to 704°C, a low melting point glass frit and a metal oxide powder having at least a low valence oxidation state and a high valence oxidation state, said metal oxide being in its low valence oxidation state when formed into the ceramic paint a vehicle mixed with said metal oxides, low melting point glass frit, and metal oxide powder having at least two valence states to form all of said mentioned materials into a ceramic paint which can be applied to a glass surface. There may be some metal oxides in the mixture of metal oxides which also have two or more valence oxidation states. However, because of the way the mixture of metal oxides is made, such metal oxides are oxidized to their highest valence states prior to being formed into the mixture and thus they are nonreactive with one another and nonreactive with any elements or compounds they come in contact with while being heated to temperatures in a range up to 704°C. It is, of course, readily apparent that if the mixture of metal oxides had the same characteristics as the metal oxide powder, the ceramic paint compositions known in the prior art would have nonstick characteristics but, in fact, they do not. Thus, the mixture of metal oxides is not of the type defined herein as the metal oxide powder added to the ceramic paint composition. Further details of the ceramic paint composition will be set out in a later portion of this specification dealing with the Best Mode and Industrial Applicability of my invention. This composition can be used in a method of forming a glass sheet with a ceramic paint thereon. In accordance with the teachings of the use of this ceramic paint composition, the following steps are carried out. The ceramic paint is applied to a glass sheet. The ceramic paint includes the metal oxide powder having at least a low valence oxidation state and a high valence oxidation state, the metal oxide included in the ceramic paint being in its low valence state when applied. The remainder of the ceramic paint may be made up as known by skilled artisans from metal oxides which together act as coloring agents for †he ceramic paint, those metal oxides being nonreactive with one another and nonreactive with any elements or compounds †hey come in contact with while being heated to temperatures up to 1300°F. The ceramic paint, in addition, includes a low melting point glass frit and a vehicle needed to transport the other remaining materials so †hat they may be applied to the glass sheet. After the application of the ceramic paint, the glass sheet is heated to a temperature which softens the glass sheet sufficiently so that the glass can be formed. The glass sheet and the ceramic paint thereon are then engaged with a fiberglass covered forming die to form the heated glass sheet to a desired shape. After shaping, the forming die is removed from engagement with the glass sheet, the metal oxide addition to the ceramic paint being effective to prevent sticking of any of the ceramic paint to †he forming die. The glass sheet is cooled to obtain a formed glass sheet with a ceramic paint thereon. In accordance with the teaching of this invention, a ceramic paint composition comprises the following materials. The first material is a mixture of metal oxides which together act as a coloring agent for the ceramic paint. These metal oxides, because of their manufacturing process, are normally all in their highest oxidation state. A small proportion of the metal oxides may have a lower valence state simply because of manufacturing variability. However, normally the mixture of metal oxides used as a coloring agent is in its highest oxidation state because of †he manufacturing process, and thus the mixture of metal oxides is nonreactive with one another and nonreactive with any elements or compounds they come in contact with while being heated to temperatures in a range up to 1300°F. The nonreactive oxides generally include oxides of material such as chrome, cobalt, nickel, manganese, iron and copper. Such a mixture is commonly known as black oxide powder and is well known in the industry. Any oxide included in this material is normally in its highest valence oxidation state because of the process of manufacture and because those who are purchasing the black oxide powder mixture desire a material which does not react when heated to moderate temperatures. Other mixtures of oxides may be put toge†her in order to get different colors, as is well known in the industry. In normal practice, the mixture of nonreactive metal oxides makes up about 8-25% by weight of the ceramic paint composition, preferably 10-20% by weight, and most preferably 16% by weight. A second material forming the ceramic paint composition is a low melting point glass frit. Normally, the low melting point glass frit is a lead borosilicate glass frit high in lead content. Any other low melting point glass frit is also suitable, but the lead borosilicate glass is preferred because it is readily available and relatively cheap. This material is included in a range of 30-50% by weight. In accordance with the teachings of the method of using the ceramic paint of this invention, a metal oxide powder having at least a low valence oxidation state and a high valence oxidation state is also included. In accordance with the teachings of the preferred embodiment, the material used is stannous oxide and it is used in a 5-25% by weight amount in the composition, preferably 10-20% by weight, and most preferably 17% by weight. However, other metal oxides, or mixtures thereof, having at least two valence states may be used. However, when the metal oxide is used, it is incorporated into the ceramic paint in its low valence oxidation state. For example, if iron oxide was used, it would be included as ferrous oxide. Similarly, if copper powder was used, it would be included as cupprous oxide. Similarly, with other metals having more than two valance states, ¦hey would be included in their lower metal oxidation state. A vehicle may be mixed with the metal oxides, the low melting point glass frit, and the metal oxide powder having at least two valence states to form all of the mentioned materials into a ceramic paint which can be applied to a glass surface. For example, if the ceramic paint is to be applied in a silk screen printing operation, a UV curable organic medium may be used. This organic medium would make up 20-35% by weight of a paint composition. However, if electrostatic means were being used to apply the ceramic paint composition, no vehicle would be necessary as the electrostatic application would not require the same. In other operations, for example, water might be the vehicle in order to make a ceramic paint in a water slurry. Such a paint may be applied by a process of air or airless spray system. Other materials which may be used are known to the artisans, for example, pine oil and other organic vehicles. The whole thing that makes the ceramic paint composition of the invention nonstickable is the metal oxide powder having at least a low valence oxidation state and a high valence oxidation state being present in the composition in its low valence oxidation s†ate. It is believedthat when this metal oxide powder is subjected to a heating operation, that portion of the powder on the upper surface of the ceramic paint composition readily oxidizes to form an excellent, fully oxidized metal oxide barrier across the top surface of the paint which insulates the low melting point glass frit and isolates the same from the fiberglass cloth. Thus, the fiberglass cloth, while contacting the surface, does not adhere to the ceramic paint and the paint does not stick to the cloth. As previously stated, ceramic paint compositions are well known in the art and general details thereof have been set forth above. Commercial compositions are available through Drakenfeld as 24-2247 and 24-2279. Also, Ferro Company makes a ceramic paint composition which is marketed under their number 3501. These paint compositions are made generally as described above, but these are materials which are avilable. If one adds to these compositions a metallic oxide powder having at least a low valence oxidation state and a high valence oxidation state in its low valence oxidation state at the levels indicated above, namely, 5-25% of the total weight thereof, these standardly available ceramic paint compositions will also be nonstickable to fiberglass covered surfaces in glass forming operations. In accordance with the use of the ceramic paint of this invention, a method of forming a glass sheet with a ceramic paint thereon is as follows. This process is disclosed on copending application Serial No. 728,645 filed on the same day as this application. The method has the following steps. The ceramic paint is applied to the glass sheet. The ceramic paint includes a mixture of metal oxides which together act as a coloring agent for the ceramic paint. The metal oxides are oxides which are nonreactive with one another and nonreactive with any elements or compounds they come in contact with while being heated to temperatures up to 1300°F. A low melting point glass frit is also included in the ceramic paint composition. A principal ingredient from a functional standpoint in achieving nonstick capabilities for the ceramic paint is a metal oxide powder having at least a low valence oxidation state and a high valence oxidation state. As fully discussed above, the me†al oxide is included in its low valence state in the ceramic paint composition. A vehicle generally is also mixed with the metal oxides, the low melting point glass frit and the metal oxide powder having at least two valence states to form all of the mentioned materials into a ceramic paint which can be applied to a glass surface. As discussed above, the vehicle selected depends on the mode in which the ceramic paint is to be applied. In fact, as discussed above, if the ceramic paint is to be applied in an electrostatic operation, no vehicle may be required at all. After the ceramic paint has been applied to the glass sheet, the glass sheet is heated to a temperature which softens the glass sheet sufficiently so that the glass sheet can be formed. Generally, this temperature is in a range of about 1175-1250, which is below 1300°F. After heating, the glass sheet and the ceramic paint thereon are engaged with a fiberglass covered forming die to form the heated glass sheet into a desired shape. The forming die is removed from engagement with the glass sheet and the ceramic paint thereon. The metal oxide addition to the ceramic paint is effective to prevent sticking of any of the ceramic paint to the forming die. As stated above, it is believed that the mechanism involved is one in which the metal oxide powder along the top surface of the paint is oxidized to its higher oxidation state and thus forms a barrier between the paint and the fiberglass of the forming die which prevents sticking of the paint to the fiberglass covered forming die. After the forming die has been removed from engagement with the glass sheet and the ceramic paint without any sticking of the ceramic paint thereto, the glass sheet may be cooled to obtain a formed glass sheet with ceramic paint thereon. Normally, the glass sheet is rapidly cooled in a glass tempering operation in order to achieve a tempered glass product having the ceramic paint thereon.

Claims: 1. A ceramic paint composition comprising a mixture of metal oxides which together act as a coloring agent for the ceramic paint, said metal oxides being nonreactive with one another and nonreactive with any elements or compounds they come in contact with while being heated to temperatures in a range up to 704°C, a low melting point glass frit and a metal oxide powder having at least a low valence oxidation state and a high valence oxidation state, said metal oxide being in its low valence oxidation state when formed into the ceramic paint a vehicle mixed with said metal oxides, low melting point glass frit, and metal oxide powder having at least two valence states to form all of said mentioned materials into a ceramic paint which can be applied to a glass surface. 2. A ceramic paint composition as claimed in Claim 1, wherein no vehicle is used when the ceramic paint composition is used in an electrostatic deposition operation. 3. A ceramic paint composition, comprising 8-25% by weight of a mixture of metal oxides which together act as a coloring agent for the ceramic paint, said metal oxides being nonreactive with one another and nonreactive with any elements or compounds they come in contact with while being heated to temperatures in a range up to 704°C, 30-50% by weight of a low melting point glass frit, 5-25% of a metal oxide powder having at least a low valence oxidation state and a high valence oxidation state, said metal oxide being in its low valence oxidatin state when formed into the ceramic paint, and 0.35% by weight of a vehicle mixed with said metal oxides, low melting point glass frit, and metal oxide powder having at least two valence states to form all of said mentioned materials into a ceramic paint which can be applied to a glass surface. 4. A ceramic paint composition as claimed in Claim 3 wherein said mixture of metal oxides is present in an amount of 10-20% by weight, said low melting point glass frit is present in a range of 35-45% by weight, and said metal oxide powder is present in a range of 10-20% by weight. 5. A ceramic paint composition as claimed in Claim 4, wherein said mixture of metal oxides is present in an amount of 16% by weight, said low melting point glass frit is present in an amount of 42% by weight, and wherein said metal oxide powder is present in an amount of 17% by weight. 6. A ceramic paint composition as claimed in any one of the preceding claims wherein said metal oxide powder is stannus oxide.

Inventors: BOAZ, PREMAKARAN TUCKER
Applicants: FORD FRANCE SOCIETE ANONYME, FORD MOTOR COMPANY LIMITED, FORD-WERKE AKTIENGESELLSCHAFT
Application year: 1986
Main classification: C03C8
IPC codes: C03C8, C09D1