PALLADIUM-COBALT ALLOYS; MANUFACTURE OF A ROOT CAP

Abstract: The invention relates to magnetic Pd-Co alloys for use in dental prostheses, in particular in root caps. The alloys contain, by weight, 40-60% Pd, 20-59% Co, 0-40% Ni, 0.l-5% Cr, 0.05-0.2% Re, 0.0l-0.5% Fe, 0.5-3% Ga, 0-0.l% B, 0-5% Pt or Au, and the gallium may be replaced, in full or inpart, by Sn In, Zn or Mn.

Description: This invention relates to palladium-cobalt alloys containing 40-60% by weight of Pd, 20-59% by weight of Co and 0-40% by weight of Ni. The invention also relates to a method of making a root cap from a cast palladium-cobalt alloy. Kinouchi et al., J. Dent. Res. (60) l, 50-58 (l98l) have described palladium-cobalt alloys which in combination with samarium-cobalt magnets can be used in dentistry for magnetically retaining dental prostheses. Sm-Co magnets, or in general rare earth-cobalt magnets have proved to be suitable in dimensions as small as in the millimeter range for use in prostheses; see for example Netherlands patent l63,7l3. As, however, the material cannot be cast, the shapes are generally limited to disks, columns or prisms. As a consequence, it is rarely possible to make the magnet in a form suitable for individual cases. To overcome these problems, there has been a search for ferromagnetic alloys which could replace the magnet in the live tissue. Ferromagnetic alloys exhibit magnetic characteristics like those of soft iron. It is important that the alloys should be castable. Ferromagnetic properties and castability can solve the above problems. The magnet in the root can then be replaced by a cast root cap. In this case the magnetic attraction between the samarium-cobalt magnet in the prosthesis and the alloy in the root is used for retention of the prosthesis, for example, dentures. In addition to having ferromagnetism and being castable, the alloy should also have physical and chemical properties which render it suitable for use in the mouth. Known alloys, however, have poor castability and low corrosion resistance, so that they cannot be used as a dental cast metal. Although nearly all conventional dental alloys are non-ferromagnetic, stainless steel containing l3 or l8 percent chromium, and cobalt-chromium and nickel-­ chromium alloys are ferromagnetic. Stainless steel, however, has a poor castability, and the ferromagnetism of the other two alloys is too weak for them to be used for magnetic retention of dental prostheses. In the above publication by Kinouchi et al., palladium-cobalt alloys are proposed for this purpose. The authors describe three alloys, namely 43Pd-57Co; 4l Pd-54Co-5Cr; and 43Pd-27 Co-30Ni (the numbers represent percent by weight). These alloys have the following magnetic characteristics: Maximum permeability µm : l50-280 Saturation flux density B₁₀₀, kG : 6.7-l0.2 Residual flux density B r , kG : l.9-2.8 Coercive force H c , Oersted : 5.3-6.6 The melting point of these alloys ranges between ll85 and l2l2°C. They can be molten at the normal melting temperature in a ceramic crucible and cast in phosphate-­ bonded embedding composition. Corrosion tests in Na₂S solution have shown that the sensitivity to sulfide attack is equal to that of the conventional gold-silver-­ palladium alloys used in dentistry, and is even less than with nickel-chromium alloys. These alloys, however, have the following disadvantages with regard to casting: - as a result of the contraction of the alloy during solidification and cooling, the embedding composition, which does not contract at a temperature above 650°C, exerts a force to which these alloys are not resistant. The result is that cracks are formed in the casting. - during casting, the alloys absorb gas, which during solidification is released again. This leads to blow holes and porosities in the metals, which has an adverse effect on strength, esthetics and corrosion resistance. In Japanese patent publication 82-20l035, magnetic palladium-cobalt-nickel dental alloys are proposed, which are claimed not to crack during casting. These alloys contain 20-40% by weight of cobalt, 20-40% by weight of nickel, 25-60% by weight of palladium, and minor proportions of molybdenum, iridium, chromium, indium and zinc. In them, molybdenum, chromium and indium are used for their grain refining and deoxidizing effect. Iridium is also used to obtain a fine-grained structure. Zinc is used to improve castability. In practice, however, it is found that these known alloys yet exhibit cracks after casting, especially if they are cast at somewhat higher temperatures. Also, many blow holes and considerable porosity are found, and cold deformability is poor. It is an object of the present invention to provide castable ferro-magnetic alloys suitable for use in dentistry and lacking the above disadvantages of known alloys. This object is realized, according to the present invention, with palladium-cobalt alloys containing 40-60% by weight of Pd, 20-59% by weight of Co, and 0-40% by weight of Ni, characterized by containing 0.l-5% by weight of chromium, 0.05-0.2% by weight of rhenium, 0.0l-0.5% by weight of iron, 0.5-3% by weight of at least one element selected from the group consisting of gallium, tin, indium, zinc, and manganese, 0-0.l% by weight of boron, 0-5% by weight of at least one of the metals selected from the group consisting of platinum and gold, and possibly other elements, whether present as impurities or deliberately added, in such small quantities that they do not essentially adversely affect the properties of the alloys. It has been found that, in palladium-cobalt alloys, rhenium is a much more effective grain refiner than iridium, which apparently is dissolved in the palladium. A rhenium concentration of 0.05-0.2% by weight has proved to be very suitable. Preferably, about 0.l% by weight of rhenium is used. To realize a good cold deformability of the alloys, iron should be present in addition to rhenium. If the alloys contain 0.0l-0.5% by weight of iron, the combination of rhenium and iron surprisingly leads to such a suitable fine-grained structure that a good cold deformation is possible. Preferably, the alloys contain 0.05-0.3% by weight of iron. In that case, a reduction in diameter of 90% can be accomplished by cold rolling without the occurrence of cracking. In known alloys, cracks occur already if the reduction in diameter during cold deformation exceeds a value of 45%. The presence of 0.5-3% by weight of gallium leads to a lower melting temperature, to better castability without the formation of porosity, and to higher strength at high temperatures. The elements zinc and indium, present in known alloys, also lead to a lower melting temperature, it is true, but they also lead to lower strength at high temperatures. Nevertheless, in the alloys according to the invention, gallium can be replaced, in full or in part, by tin, indium, zinc or manganese. The alloys according to the invention contain chromium and optionally boron for their deoxidizing activity. Owing to their high affinity to oxygen, these elements neutralize the formation of gaseous products in the melt, as a result of which porosity is fully prevented. The proportion of boron may be 0-0.l% by weight, but is preferably 0.005-0.l% by weight, and most preferably 0.0l-0.03% by weight. The proportion of chromium may be 0.l-5% by weight. When the chromium content is rela­ tively high, however, a chromium oxide slag tends to form on the melt, which makes it difficult to estimate the correct moment of casting, and the chance of oxide inclusions in the alloys is increased. At relatively low chromium concentrations, however, the chance of porosity is increased. Accordingly, the chromium content is preferably 0.l-l.0% by weight, and most preferably 0.2-0.7% by weight. An excellently suitable chromium content is about 0.4% by weight. The alloys may contain 0-40% by weight of nickel, but in practice alloys which do not contain nickel are preferred. To improve corrosion resistance, it may be attractive to replace 0-5% of the palladium by platinum or gold, which, however, does make the alloy more expensive. The alloys according to the invention can be used in dentistry to retain prostheses, such as dentures, in position in cooperation with one or more permanent magnets, such as Sm-Co magnets. By virtue of their castability, they can be brought into a form suitable for each individual case, for example, in the form of a root cap. In this connection reference is made to the above article by Kinouchi et al.. Example The pure metals, such as palladium of 99.9%, electrolytic cobalt, rhenium of 99.9%, iron of 99%, gallium of 99.99%, and boron, were molten together in a Zirkonia crucible in an induction oven under vacuum. The composition was: Palladium 50 percent Cobalt 47.2 percent Chromium 0.4 percent Rhenium 0.l percent Gallium 2.2 percent Iron 0.08 percent Boron 0.02 percent. After casting, the cast turned out to be free from hair cracks and porosities. The magnetic characteristics were as follows: Maximum permeability µm 240 Saturation flux density B₁₀₀.kG l0.0 Residual flux density B₁₀₀.kG 2.5 Coercive force H c , Oested 5.7 The physical properties were as follows: Melting interval, °C ll95-l2l0 Vicker's hardness (after casting) kg/mm² 305 Tensile strength (after casting) daN/mm² 80 Yield point (after casting), daN/mm² 70 Elongation at break (after casting), % l5 In the following table, a number of alloys according to the present invention (Nos. 5-8) are compared with some known alloys.

Claims: 1. Palladium - cobalt alloys containing 40-60% by weight of Pd, 20-59% by weight of Co and 0-40% by weight of Ni, characterized by containing 0.l-5% by weight of chromium, 0.05-0.2% by weight of rhenium, 0.0l-0.5% by weight of iron 0.5-3% by weight of at least one element selected from the group consisting of gallium, tin, indium, zinc and manganese, 0-0.l% by weight of boron 0-5% by weight of at least one metal selected from the group consisting of platinum and gold, and possibly other elements, whether present as a conta­ mination or added deliberately, in such small proportions that they do not essentially adversely affect the proper­ ties of the alloys. 2. Palladium-cobalt alloys as claimed in claim l, characterized by not containing nickel. 3. Palladium-cobalt alloys as claimed in claim l or 2, characterized by containing 0.l-l.0% by weight of chromium, preferably 0.2-0.7% by weight of chromium. 4. Palladium-cobalt alloys as claimed in any of claims l-3, characterized by containing 0.05-0.3% by weight of iron. 5. Palladium-cobalt alloys as claimed in any of claims l-4, characterized by containing 0.005-0.l% by weight of boron, preferably 0.0l-0.03% by weight of boron. 6. Palladium-cobalt alloys as claimed in any of claims l-5, characterized by containing 0.5-3% by weight of gallium. 7. A method of making a root cap from a cast palladium-cobalt alloy, characterized by making a root cap, by a method known per se, from an alloy as claimed in any of claims l-6.

Inventors: VAN DER ZEL, JOSEPH MARIA
Applicants: ELEPHANT EDELMETAAL B.V.
Application year: 1986
Main classification: C22C30
IPC codes: C22C5, C22C19, A61K6, C22C30