COMPOSITIONS AND PROCESSES FOR PRODUCING SCRATCH RESISTANT POLYSILOXANE COATINGS

Abstract: A prepolymer composition for forming a scratch-­ resistant coating, comprising an acidic, aqueous solution of a polysiloxane prepolymer having non-co-reactive side groups and co-reactive side groups other than alkoxy, the composition being curable by evaporation of solvent and a decrease in acidity causing the co-reactive groups to react together to cross-link the polymer. Suitable co-reactive side groups are amino, epoxy and thiol. Suitable non-co-­ reactive side groups are alkyl and gamma methacryloxy propyl. Acidity is suitably achieved by using a volatilisable organic acid such as acetic acid, so that it evaporates with the solvents to decrease the acidity.

Description: This invention relates to scratch resistant coatings and in particular with a process for producing scratch-resistant polysiloxane coatings with improved extensibility. A variety of products, including plastics mouldings, sheets and lenses are conventionally provided with coatings to improve their resistance to scratching and abrasion. Such coatings may be formed from polymers, such as polyurethanes, melamine-formaldehyde resins and polysiloxanes. While polysiloxanes provide the highest scratch-resistance, they suffer from the disadvantage that known "scratch resistant" polysiloxane coatings show the lowest extensibility. This means that on flexure of the base material, the conventional polysiloxane coating tends to craze. The resulting defect in the surface coating can cause initiation of a crack in the base material. Consequently, the impact strengths of known polysiloxane coated substrates tend to be lower than those of the base material. Furthermore, the impact strength of the coated substrate decreases with increase in polysiloxane coating thickness. There is accordingly a demand for scratch-resistant coatings with improved extensibility which are able to provide a high level of scratch-resistance without adversely affecting the other physical properties of the base substrate. According to one aspect of the present invention there is provided a prepolymer composition for forming a scratch-resistant coating, comprising an acidic, aqueous solution of a polysiloxane prepolymer having first side groups, and second and third side groups, the second and third groups being co-reactive together and being other than siloxane-linkage-forming groups, the composition being curable by evaporation of solvent and a decrease in acidity causing the second and third side groups to co-react together to cross-link the polymer, but the first groups being non-reactive in the system. The prepolymer preferably also has siloxane-linkage-forming groups or acid-stabilised hydrolysable derivatives thereof, whereby the curing process involves further formation of siloxane linkages through the interaction of these groups. The decrease in acidity may be produced by the addition of an alkaline component, but is most suitably brought about by using the combination of a basic second or third side group such as amino on a silane together with a volatilisable acid in the prepolymer composition, whereby the acid evaporates with the solvent during curing. Suitable acids are organic acids, for example lower alkanoic acids such as formic, acetic and propionic acids. Evaporation of solvent can take place at room temperature, but suitably heat is applied, especially to assist in the removal of volatilisable acid. According to a second aspect of the present invention there is provided a process for producing a polysiloxane prepolymer composition for forming a scratch-resistant coating, which comprises: (i) forming an aqueous acidic solution of two or more silanes or their oligomers, said silanes or oligomers having groups capable of forming siloxane linkages together, at least one of the silanes or oligomers having at least one first side group and at least one other of the silanes or oligomers having a second side group other than a siloxane-linkage-forming group, and allowing the solution to form siloxane linkages to yield a polysiloxane; and (ii) adding at least one further silane or its oligomer which has at least one hydrolysable group capable of forming a siloxane linkage and a third side group, and allowing the solution to form siloxane linkages between the polysiloxane of (i) and the added silane or oligomer under dilute and acid conditions, the third side group being capable of co-reacting with the second side group under conditions of lower dilution and lower acidity, but the first side group being non-reactive in this system with the second or third groups. The procedure preferably also includes the further step of (iii) adding further acid to stabilise the prepolymer solution. The first groups will be referred to herein as "non co-reactive groups" and the second and third groups as "co-reactive groups". In addition to water and acid, the solution may also include one or more alcohols or other water-miscible solvents. Alcohols are preferred for a variety of reasons. They assist in wetting the substrate during application of the coating. The lower alcohols are also relatively easily volatilised, and can form azeotropes to assist in solvent removal. Suitable alcohols include methyl, ethyl and isopropyl alcohols, but there is no definite limit on the number of carbon atoms, the alcohol being rather selected according to its physical properties in relation to the other components and the intended mode of use. During the course of polysiloxane formation, alcohols will be formed through the hydrolysis of the alkoxy groups, thereby increasing the alcohol content of the solution. The alkoxy groups can accordingly be selected to produce suitable alcohols in the solution. In general, alkoxy groups of 1 to 6, preferably 1 to 4 carbon atoms will be suitable. The non-coreactive side group or groups can be those conventionally employed in modifying polysiloxane formation; typically lower alkyls such as methyl, ethyl, isopropyl and t-butyl. Other bulky side groups may be used such as aryl and its derivatives or other non-coreactive side groups which may be specifically added to improve adhesion to substrate such as gamma methacryloxy propyl in the case of acrylics. Bulky and/or long non-coreactive side groups limit the extent of cross-linking by providing sites which cannot be cross-linked, and also hold the molecules apart during cross-linking so as to resist contraction as the cross-linking proceeds. The co-reactive groups should be less reactive than the hydrolysable groups under the conditions of prepolymerisation, so that there is no substantial interaction between the co-reactive groups at that stage. This is achieved by appropriate selection of co-reactive groups, and also by selection of the conditions of prepolymerisation, in particular by maintaining a relatively high dilution, and also by appropriate choice of pH. Suitable co-reactive groups are epoxy and amino groups. The amino groups may be primary or secondary amino. These have the advantage that amino groups catalyse the formation of the silicon-oxygen lattice, so that this, and also the interaction of the amino and epoxy groups, can be influenced by controlling the pH: in particular, a decrease in acidity will encourage the formation of cross-linkages. Examples of other co-reactive groups are thiols reacting with epoxy, vinyl, acrylic or methacrylic groups. Usually one, and preferably each, of the co-reactive side groups forms part of a larger group in which the reactive group is separated from the silicon atom by a connecting group so that the larger group has at least one single bond allowing rotation of the reactive group. Examples of connecting groups are -(CH₂) n - and -(CH₂) n -O-, the latter being particularly preferred for epoxy, n preferably being an integer of 1 to 3. A wide variety of silanes or their oligomers having different functional groups are commercially available from e.g. Union Carbide and Dow-Corning. In order to provide sufficient stability in the coating solution (and a viscosity which is not excessively high), the mixture of silanes should preferably contain non-co-reactive groups in a molar amount which is at least equal to 40% of the co-reactive groups and other non-alkoxy groups (e.g. epoxide, amino and alkyl groups). Typically, the mixture of silanes or their oligomers may comprise an epoxyalkylalkoxy silane and an aminoalkylalkoxy silane in which at least two alkoxy groups are present in each silane. Generally, the mixture of silanes will include in addition at least one alkylalkoxy silane in order to increase the proportion of non-coreactive groups in the composition. Typical amino containing silanes are amino (lower alkyl) triethoxy or trimethoxy silanes. Suitable epoxy silanes include glycido lower alkyl triethoxy or trimethoxy silanes. Dimers or oligomers of these alkoxy silanes may be used. The alkyl-alkoxy silane is preferably a lower alkyl triethoxy or trimethoxy silane. As an optional ingredient of the silane mixture, one may use silanes containing other functional groups, e.g. groups which improve adhesion to the substrate, and groups which modify viscosity. For example, the presence of silanes containing methacrylic groups can be used to improve adhesion of the modified polysiloxane coatings to polymethyl methacrylate substrates. As indicated above the mixture of silanes preferably contains non-coreactive groups in a mole per cent of at least 20, normally at least 30, based on the total amount of co-reactive groups and non-coreactive groups, i.e. other non-hydroxyl or non-hydrolyzable groups attached to the silicon atom. It is not essential for the epoxide and amino groups (or other co-reactive groups) to be present in stoichiometric proportions. However, we prefer to formulate the composition so that it contains an excess of amino groups since these groups both catalyse the formation of the Si-O lattice (by virtue of their basic character) as well as reacting with the epoxide groups. The scratch-resistant coating is suitably produced by the application of a prepolymer composition. The first stage in the formation of this composition is to prepare a solution of one or more silanes or their oligomers which can react through their hydrolysable groups to form siloxane linkages, without substantial interaction of the co-reactive groups. One way of achieving this is to omit one of the co-reactive group-containing silanes or their oligomers initially, so that polymerisation can only proceed through the formation of siloxane linkages. This is initiated by the presence of water in the solution. The solution may contain alcohol such as isopropyl alcohol as co-solvent, and the solution will need to be acidic to control the rates of hydrolysis and polymerisation. A weak organic volatilisable acid such as a lower alkanoic acid is preferred. Additional strong mineral acids are not desirable, particularly where amino is one of the reactive groups because of the formation of insoluble salts and the difficulty of their removal from the composition. The procedure is described further in US 4006271. The initial solution at controlled pH may be allowed to age for a period, e.g. 24 hours, to form siloxane linkages, whereupon the silane having the other co-reactive group is added, again controlling pH, either in solution or alone. The solution is allowed to age for a further period, e.g. 30 mins, for the added silane or their oligomers to react with the existing siloxanes through their hydrolysable groups; and then the acidity is adjusted to pH 3 to 6. This stepwise addition of the silanes or their oligomers having co-reactive groups prevents premature reaction between the co-reactive groups. The prepolymer can then be used immediately for coating, or it can be stored until required. In the latter case, it may be desirable to add further solvent or acid, or both, to stabilise the solution and give it appropriate shelf-life. The prepolymer coating solution may be applied by any known coating method to a clean substrate, such as any of the methods described in U.S. Patent No. 4006271. Normally, the substrate will be a polymeric, easily scratched surface, but the coating composition can be applied to any substrate including wood. The composition can be used to coat mouldings, shaped articles and sheet or film. Examples of polymer materials which are advantageously coated with the composition include polyesters, polycarbonates, and polymethyl methacrylates. After application the coating is preferably heated to remove the solvent and acid and bring about cure of the coating by formation of siloxane linkages and cross-linking through the co-reactive groups. However, the coating compositions will dry and cure at ambient temperatures when coated in a thin film on a substrate. The removal of solvent and acid increases the pH so as to make the groups more reactive and increases the concentration (decreases the dilution of molecules) so that the co-reactive groups are brought into closer proximity. The compositions of the invention may also include other conventional ingredients for modifying the properties. Examples of these are dyestuffs, levelling agents and fillers, together with other known adhesion promoting additives such as zirconium and titanium derivatives. The following example will illustrate the invention and the manner in which it may be carried into effect. Example 1 A solution of cross-linkable organo polysiloxane was prepared by adding with stirring a mixture of 88.85g methyl trimethoxysilane (Dow Corning Z6070) and 37.05g of gamma glycidoxypropyl trimethoxysilane (Dow Corning Z6040), to a solution comprising 21.88g of distilled water, 27.71g of propan-2-ol, and 0.85g of glacial acetic acid. The resultant solution was allowed to stand for 24 hours, forming an initial polysiloxane having methyl (non-reactive) groups, epoxy (one of the co-reactive) groups, and some unpolymerised methoxy groups. To this solution was then added an additional 64.09g of water, 39.36g of propan-2-ol, 51.56g of butan-1-ol and 8.80g of glacial acetic acid, to increase the dilution; and then 34.67g of gamma-amino-propyl triethoxysilane (Union Carbide A1100) was added and allowed to stand 30 minutes. This extended the polymer largely by reaction of ethoxy groups of the added silane with methoxy groups of the existing polysiloxane; the lower reactivity of the amino and epoxy groups, especially under the conditions of dilution and acidity, largely preventing these groups from interacting at this stage. An additional 14.37g of glacial acetic acid was then added and the resultant solution aged at 20°C for 5 days before use. This allows acetoxy groups to be formed and produces a stable equilibrium solution of prepolymer under the conditions of high acidity and dilution. The polycarbonate moulding to be coated was cleaned using acetone and air dried. The coating was applied using a wire-wound wet film applicator rod and the coated moulding was placed in an air circulating oven for 2 hours at 97°C. This causes the solvent comprising acetic acid, water and alcohols, to evaporate, resulting in an increase in pH which increases the reactivity of the co-reactive amino and epoxy groups, and a decrease in dilution which brings these groups closer together so that they can co-react to cross-link the polysiloxane. After a further period of 24 hours, the coated area was examined for scratch resistance by rotating 50 times with an 000 steel wool pad under a load of 500g per cm², no scratching occurred in the coated area, whereas the uncoated area suffered severe scratching. Example 2 A solution prepared as in Example 1 was coated onto a 75 × 10⁻⁶ metres thick polyethylene terephthalate film using a wire wound applicator rod and was then dried for 2 hours at 97°C to give a dry film coating weight of 10 grams per square metre. The resultant coated film when wrapped around a 5 mm mandrel did not crack or craze. A 70mm long 25mm wide strip of coated film when subjected to an elongation of 10% using a tensometer with crosshead speed of 3mm/min did not cause further fracture of the coating. Example 3 A solution of a cross-linkable organo polysiloxane was prepared by adding, with stirring, a mixture of 7.04g of gamma methacryloxy propyl trimethoxy silane (Union Carbide A-174) with 1.62g of gamma glycidoxy propyl trimethoxy silane (Dow Corning Z6040) to a solution comprising of 2.19g distilled water, 2.77g of propan-2-ol and 0.90g of glacial acetic acid. To this mixture was added, with stirring, a mixture of 2.09g of gamma glycidoxypropyl trimethoxysilane (Dow Corning Z6040) with 5.01g of methyl trimethoxysilane (Dow Corning Z6070). This was allowed to stand for 5 minutes. To this solution, with stirring, was added 6.41g of distilled water, 3.94g of propan-2-ol, 5.16g of butan-1-ol, and 0.88g of glacial acetic acid and then 3.47g of gamma amino propyl triethyoxy silane (Union Carbide A1100). After 30 minutes 1.44g of glacial acetic acid was added. This solution was stored at 20°C for 10 days. The solution prepared as described was then used to coat a 75 × 10⁻⁶ metre thickness polyethylene terephthalate film using a wire wound applicator rod which was then dried for 2 hours at 97°C to give a dry film coating weight of 6 grams per square metre. The resultant film when wrapped around a 5 mm diameter mandrel did not crack or craze. A 70mm long 25mm wide strip of the coated film when subjected to an elongation of 10%, using a tensometer with a crosshead of 3mm/min, did not cause fracture of the coating. Example 4 A solution of a cross-linkable organo polysiloxane was prepared by adding, with stirring, a mixture 8.89g of methyl trimethoxy silane (Dow Corning Z6070) with 3.71g of gamma glycidoxypropyl trimethoxy silane (Dow Corning Z6040) to a solution comprising 2.19g of distilled water, 2.77g of propan-2-ol and 0.09g of glacial acetic acid. This was allowed to stand at 20°C for 24 hours. To this solution, with stirring, was added 6.41g of distilled water, 3.94g of propan-2-ol, 5.16g of butan-1-ol and 0.88g of glacial acetic acid and then 2.50g of gamma mercapto propyl trimethoxy silane (Union Carbide A189). After 30 mins 1.44g of glacial acetic acid was added to the solution. The resultant solution was stored at 20°C for 5 days before use. The solution prepared as described above was used to coat a 75 × 10⁻⁶ metre thick polyethylene terephthalate film using a wire wound applicator rod. The film was dried for 10 mins at 97°C to give a dry coating weight of 4 grams per square metre. The resultant coated film when wrapped around a 5mm diameter rod did not crack or craze. Also when subjected to a 10% elongation as described in Example 3 the coating did not fracture. Example 5 A solution of a cross-linkable organo polysiloxane was prepared by adding, with stirring, a mixture of 8.89g of methyl trimethoxy silane (Dow Corning Z6070) with 3.71g of gamma glycidoxy propyl trimethoxy silane (Dow Corning Z6040) to a solution comprising 2.19g distilled water 2.77g of propan-2-ol and 0.09g of glacial acetic acid. This was allowed to stand for 24 hours at 20°C. To this solution, with stirring, was added 6.41g of distilled water, 3.94g of propan-2-ol, 5.16g butan-1-ol and 0.88g of glacial acetic acid and then 3.07g of gamma mercapto propyl trimethoxy silane. After 30 minutes 1.44g of glacial acetic acid was added. The resultant solution was stored 5 days at 20°C before use. The solution as prepared above was used to coat 8mm thick polymethyl methacrylate using a wire wound applicator. The coating was dried/cured for 2 hours at 97°C to give a dry coating weight of 4 grams per square metre. The resultant coated sheet could be thermoformed around a 20cm diameter mandrel without fracture of the coating. The resulting coating was examined for scratch resistance using an 000 steel wool pad and was found to give excellent scratch resistance. Example 6 A solution of a cross-linkable organo polysiloxane was prepared by adding, with stirring, a mixture of 8.89g of methyl trimethoxysilane (Dow Corning Z6070) with 3.71g of gamma glycidoxypropyl trimethoxysilane (Dow Corning Z6040) to a solution comprising 2.19g distilled water, 2.77g of propan-2-ol and 0.09g of glacial acetic acid. This was allowed to stand at 20°C for 24 hours. To this solution, with stirring, was added 6.41g of distilled water, 3.94g of propan-2-ol, 5.16g of butan-1-ol and 0.88g of glacial acetic acid and then 3.47g of gamma amino propyl triethoxysilane (Union Carbide A1100). After 30 mins 1.44g of glacial acetic acid was added. This solution was stored at 20°C for 5 days. After 5 days the solution was diluted with a solvent mixture comprising of 3.44g distilled water, 2.68g propan-2-ol, 2.06g butan-1-ol and 0.39g glacial acetic acid. To this solution was added 0.16g of amino zirco-aluminate chloride hydroxide polymer (Cavedon Chemical Co - CAVCO MOD APG-2) and dispersed using a high shear mixer for 30 seconds. The solution prepared as described above was used to coat a 75 × 10⁻⁶ metre thick polyethylene terephthalate film, using a wire wound applicator rod. The film was dried for 2 hrs at 97°C to give a dry coating weight of 10.4 grams per square metre. The resultant film when wrapped around a 5mm diameter mandrel did not crack or craze.

Claims: A prepolymer composition for forming a scratch-resistant coating, comprising an acidic, aqueous solution of a polysiloxane prepolymer having first side groups, and second and third side groups, the second and third groups being capable of co-reaction together and being other than siloxane-linkage-forming groups, the composition being curable by evaporation of solvent and a decrease in acidity causing the second and third side groups to effect said co-reaction to cross-link the polymer, but the first groups being non-reactive in the system. A prepolymer composition according to claim 1 wherein the prepolymer also has siloxane-linkage-forming groups or acid-stabilised hydrolysable derivatives thereof, whereby the curing process involves further formation of siloxane linkages through the interaction of these groups. A process for producing a polysiloxane prepolymer composition for forming a scratch-resistant coating, which comprises: (i) forming an aqueous acidic solution of two or more silanes or their oligomers, said silanes or oligomers having groups capable of forming siloxane linkages together, at least one of the silanes or oligomers having at least one first side group and at least one other of the silanes or oligomers having a second side group other than a siloxane-linkage-forming group, and allowing the solution to form siloxane linkages to yield a polysiloxane; and (ii) adding at least one further silane or its oligomer which has at least one hydrolysable group capable of forming a siloxane linkage and a third side group, and allowing the solution to form siloxane linkages between the polysiloxane of (i) and the added silane or oligomer under dilute and acid conditions, the third side group being capable of co-reacting with the second side group under conditions of lower dilution and lower acidity, but the first side group being non-reactive in this system with the second or third groups. A process according to claim 3 which includes the further step of (iii) adding further acid to stabilise the prepolymer solution. A composition or process of any one of the preceding claims wherein the solvent comprises one or more volatilisable alcohols. A composition or process according to any one of the preceding claims wherein acidity is provided by the presence of a volatilisable organic acid. A composition or process according to any one of the preceding claims wherein the first side groups are alkyl, aryl or methacrylic groups. A composition or process according to any one of the preceding claims wherein the second and third side groups comprise amino and epoxy groups. A composition or process according to any one of claims 1 to 7 wherein the second and third side groups comprise a) thiol and b) epoxy, vinyl, acrylic or methacrylic groups. A composition or process according to any one of the preceding claims wherein at least one of the second or third side groups is part of a larger group and is separated from the silicon atom of the silane by a connecting group so that the larger group has at least one single bond allowing rotation of the co-reactive group. A composition or process according to claim 10 wherein the connecting group comprises -(CH₂) n - or (CH₂) n -O- where n = 1 to 3. A method of forming a scratch resistant coating which comprises coating a substrate with a prepolymer composition according to any one of claims 1, 2 and 5 to 11 (as ultimately appendant to claims 1 and 2) or made by a process according to claims 3 or 4 or 5 to 11 (as ultimately appendant to claims 3 or 4), and curing it through evaporation of solvent and a decrease in acidity. A method according to claim 12 wherein the substrate is a polycarbonate plastics material. A method according to claim 12 or claim 13 wherein the increase in pH is brought about by using a volatilisable acid in the prepolymer composition, whereby the acid evaporates with the solvent during the curing process.

Inventors: GENT, JOHN ARTHUR GOOCH
Applicants: COGENT LIMITED
Application year: 1986
Main classification: C09D183
IPC codes: C08J7, C09D183