POWDER COATING COMPOSITIONS

Abstract: A powder coating composition comprises a component (A) containing carboxylic acid or anhydride functionality and a component (B) containing hydroxy functionality. The components (A) and (B) are both solids at temperatures up to 50°C and at least one of them is a synthetic resin having a glass transition temperature in the range 0 to 120°C. The carboxylic acid or anhydride-functional component (A) is a compound or polymer containing at least two cyclic carboxylic anhydride groups per molecule or is a compound containing a moiety of the formula: where X is a hydrogen atom or an alkyl group, or a cyclic anhydride thereof. The hydroxy-functional component (B) contains at least two hydroxy groups per molecule and contains at least one amine group in its molecule to catalyse the reaction of the carboxylic acid or anhy­ dride groups of component (A) with the hydroxy groups of component (B). The composition is prepared by mixing the ingredients, extruding them at a temperature above the glass transition temperature of at least one of the components but below thefusion temperature, and comminut­ ing the extrudate.The composition is applied to sub­ strates and heated to cause fusion and reaction of the ingredients to cure the coating layer formed.

Description: This invention relates to thermosetting powder coat­ ing compositions. Such a coating composition comprises powdered solid materials containing groups capable of reacting with each other when heated. The coating compo­ sition is applied to a substrate, particularly a metallic substrate, in powder form, usually by electrostatic spray­ ing. The coating composition is heated on the substrate to fuse at least the major component of the coating to cause it to flow and to react with another component to cure the coating. Examples of powder coating compositions comprising a component containing hydroxyl groups and a component containing anhydride groups are described in US Patents 4069275 and 4101606, British Patents 1366081 and 1561828 and European Patent Application 73022. Such powder coat­ ings are generally heat-cured at a temperature in the range from 130 to 200°C. The use of an amine catalyst for the curing reaction between the hydroxyl and anhydride groups is described in US Patent 4069275. The amine catalyst is generally a solid of melting point 50 to 200°C which is mixed into the powder coating composition. Examples of liquid coating compositions comprising a component containing hydroxyl and amine groups and a component containing anhydride groups are described in US Patent 4452948, which relates to a two-pack solvent-­ based coating composition, and US Patent 4308188, which relates to water-borne coatings comprising the half-­ ester zwitterion reaction product of a polymer contain­ ing cyclic acid anhydride groups with a hydroxy-functional tertiary carbinamine. A powder coating composition according to the inven­ tion comprises a component (A) containing carboxylic acid or anhydride functionality and a component (B) con­ taining hydroxy functionality, the components (A) and (B) both being solids at temperatures up to 50°C and at least one of (A) and (B) being a synthetic resin having a glass transition temperature (Tg) in the range 0-120°C, and the composition is characterised in that:- the carboxylic acid or anhydride-functional component (A) is a compound or polymer containing at least two cyclic carboxylic anhydride groups per molecule or is a compound containing a moiety of the formula:- where X is a hydrogen atom or an alkyl group, or a cyclic anhydride thereof, provided that the carboxylic acid or anhydride-functional component (A) does not contain an olefinic double bond in the alpha, beta- or beta, gamma-position with respect to any carboxylic acid or anhydride group and provided that if the component (A) is an addition polymer the carboxylic acid or anhydride groups are separated from the addition polymer chain by at least one interven­ ing carbon atom, and the hydroxy-functional component (B) contains at least two hydroxy groups per molecule and contains at least one amine group in its molecule to catalyse the reaction of the carboxylic acid or anhydride groups of component (A) with the hydroxy groups of component (B). Examples of synthetic resins of Tg 0-120°C suitable for use as anhydride component (A) include anhydride-­ functional polymers formed by the reaction of a hydroxy-­ functional polymer with a tricarboxylic compound capable of introducing anhydride groups. Preferred tricarboxylic compounds are those containing a moiety of the formula:- where X is an alkyl group of 1 to 4 carbon atoms or espec­ ially a hydrogen atom, or a cyclic anhydride thereof. Anhydrides are generally preferred to the corresponding acids since the reaction may require less heating and produce higher yields. A particularly preferred anhydride is tricarballylic anhydride of the formula is also effective to introduce anhydride groups on heat­ ing, as is citric acid. Hemimellitic anhydride (benzene 1,2,3-tricarboxylic acid anhydride) or acid can also be used, although the aliphatic compounds are preferred. Alicyclic compounds can also be used, for example anhy­ drides of cyclohexane-1,2,3-tricarboxylic acid and deriva­ tives thereof substituted by an alkyl group. An ali­ cyclic tricarboxylic acid anhydride can be formed by the Diels-Alder reaction of a 2,4-dienoic acid such as sorbic acid with maleic anhydride according to the formula:- where R is hydrogen or an alkyl group (R is methyl when the dienoic acid is sorbic acid). The cyclohexene tri­ carboxylic acid anhydride produced can be hydrogenated to form cyclohexane-1,2,3-tricarboxylic acid anhydride which is reacted with a hydroxy-functional polymer to produce an anhydride-functional component (A) for use in a powder coating composition according to the invention. Anhydride-functional polymers of Tg 0-120°C can also be produced by the reaction of a hydroxy-functional polymer with trimellitic anhydride acid chloride in the presence of a tertiary base; by transacidolysis of the acetate of a hydroxy-functional polymer with trimellitic anhydride; or by thermal esterification of the hydroxy-­ functional polymer with trimellitic anhydride. These three reactions are described by Puskas and Fields in Ind. Eng. Chem. Prod. Res. Develop., Volume 9, No. 3 (1970) at page 403-407. The thermal esterification of hydroxy-functional polymers with trimellitic anhydride is also described in European Patent Application 73022. These anhydride-functional polymers can be used as compon­ ent (A) in the powder coating compositions of the present invention. The reaction products of hydroxy-functional polymers with aliphatic or alicyclic tricarboxylic com­ pounds such as tricarballylic anhydride or acid are how­ ever preferred since the reaction with such a compound converts a substantially greater proportion of the hydroxy groups to anhydride groups compared to reaction with trimellitic anhydride. Moreover, reaction with an ali­ phatic or alicyclic tricarboxylic anhydride can be carried out at lower temperatures and can form an anhydride­ functional polymer from a hydroxy-functional polymer with a smaller increase in molecular weight and less colour in the product than is the case with reaction with trimellitic anhydride. The anhydride component (A) may be an anhydride-­ tipped polymer of Tg 0-120°C formed by the reaction of a tricarboxylic compound capable of introducing anhydride groups with a hydroxy-tipped polymer, for example a hydroxy-tipped polyester. Such polyesters can be prepared by the reaction of an excess of one or more glycols with one or more polycarboxylic acids or anhydrides. The glycol and polycarboxylic acid or anhydride reagents used in preparing the polyester can be those known for preparing polyesters for powder coatings. The glycol component preferably consists at least partly of a branched-chain glycol such as neopentyl glycol or tri­ methylpentane diol, optionally with ethylene glycol or propylene glycol. The polycarboxylic acid or anhydride component preferably consists at least partially of an aromatic acid or anhydride such as isophthalic acid, terephthalic acid or phthalic acid or anhydride, or an alicyclic acid or anhydride such as cyclohexane dicar­ boxylic acid, optionally with an aliphatic dicarboxylic acid such as adipic acid. The polyester-forming reagents preferably include a minor amount of a trifunctional reagent such as trimethylol-propane or trimellitic anhy­ dride to increase the average functionality of the poly­ ester and to introduce branching. Such anhydride-tipped polyesters can be used in the coating composition with synthetic resins containing hydroxy and amine groups or with lower molecular weight crystalline compounds containing at least two hydroxy groups and at least one amine group. The anhydride component (A) can alternatively be an anhydride-functional polymer of Tg 0-120°C formed by the reaction of a tricarboxylic compound capable of introducing anhydride groups with an addition copolymer having pendent hydroxyl groups, for example a copolymer of a hydroxyalkyl ester of an olefinically unsaturated acid such as hydroxyethyl methacrylate, hydroxyethyl acrylate, hydroxypropyl acrylate or hydroxypropylmeth­ acrylate. The addition copolymer preferably contains 10 to 50 per cent by weight hydroxyalkyl acrylate or methacrylate units together with comonomer units of one or more esters of methacrylic or acrylic acid such as methyl methacrylate, ethyl methacrylate or ethyl acrylate and/or styrene. An alternative type of addition copolymer having pendent hydroxyl groups is a styrene/allyl alcohol copolymer. Alternative hydroxy-functional polymers which can be reached with a tricarboxylic compound such as tricar­ ballylic anhydride to form an anhydride-functional compon­ ent (A) are hydrolysed epoxy resins, hydroxy-functional polyurethanes and hydroxy-functional polycarbonates. A hydroxy-functional polymer which is reacted with a tricarboxylic compound capable of introducing anhydride groups to form component (A) preferably contains no amine groups so that anhydride groups can be introduced into the polymer without premature curing. We have found that addition polymers in which a carboxylic acid anhydride group is immediately adjacent the addition polymer chain, for example polymers of an alpha, beta-unsaturated carboxylic acid anhydride such as the maleic anhydride copolymers described in British Patent 1366081 and U.S. Patents 4069275 and 4101606 and the itaconic anhydride copolymers described in U.S. Patent 4452948, as well as materials in which an olefinic double bond is present in the alpha, beta- or beta, gamma-posi­ tion with respect to any carboxylic acid or anhydride group, are not suitable for forming the powder coating compositions of the invention. They lead to a rough, brittle and sometimes foamed product on heat curing. We believe that this may be caused by decarboxylation of the polymers, giving off gas during curing. The anhydride component (A) may be an addition poly­ mer of Tg 0-120°C of a cyclic carboxylic anhydride in which the anhydride groups are separated from the addi­ tion polymer chain by at least one intervening carbon atom. Examples of suitable anhydride monomers are vinyl trimellitate anhydride whose preparation is described in US Patent 4308188, a vinyl ester of an acylated citric acid anhydride as described in European Patedt Application 85884, or a compound of the formula: where R' represents hydrogen or methyl and R" represents an alkylene group having 2 to 4 carbon atoms which can be prepared by the reaction of a hydroxyalkyl acrylate or methacrylate with tricarballylic anhydride. The anhydride component (A) can alternatively be a polymer of Tg 0-120°C containing cyclic carboxylic anhydride groups introduced by the ene reaction. Such polymers are the reaction product of a polymer containing residual unsaturation, for example an unsaturated poly­ ester, with an olefinically unsaturated cyclic carboxylic anhydride, for example maleic anhydride. When the hydroxy-functional component (B) is a syn­ thetic resin of Tg 0-120°C the component (A) can be a tricarboxylic compound containing a moiety of the formula: or a cyclic anhydride thereof. The tricarboxylic compound is preferably an anhydride. Tricarballylic anhydride is the preferred anhydride and is capable of producing particularly smooth hard glossy cured films when used in a powder coating with a hydroxy-functional polymer (B), for example an acrylic polymer containing hydroxy and amine groups. Tricarballylic acid can also be used, as can tricarballylic anhydride in which the free carboxyl group is esterified with an alkanol, e.g. of up to 4 carbon atoms. Alternative low molecular weight anhydride components (A) which can be used in the powder coating composition with a synthetic resin (B) of Tg 0-120°C containing hydroxy and amine groups are oligomers of trimellitic anhydride containing at least two anhydride groups such as those described in British Patent 1561828 and aromatic dianhydrides such as benzophenone tetracarboxylic dianhy­ dride. When component (B) is a synthetic resin of Tg 0-­ 120°C the component (A) can be a mixture of a polymer containing cyclic anhydride groups and a tricarboxylic compound containing a moiety of the formula: or a cyclic anhydride thereof. Such a mixture can be formed by reacting a hydroxy-functional polymer with a stoichiometric excess of the tricarboxylic compound, which is preferably an anhydride such as tricarballylic anhydride. The ratio of anhydride groups in the tricar­ boxylic compound to hydroxy groups in the hydroxyl-func­ tional polymer can for example be 1.5:1 to 4:1. A preferred type of hydroxy component (B) is an addition copolymer of Tg 0-120°C having pendent hydroxyl and amine groups. The amine groups are preferably tert­ iary amine groups.The addition polymer can for example be a copolymer containing 5 to 80 per cent by weight, preferably 10 to 50 per cent by weight, of units of a hydroxyalkyl ester of an olefinically unsaturated car­ boxylic acid such as hydroxyethyl methacrylate, hydroxy­ ethyl acrylate, or hydroxypropyl methacrylate and 2 to 50 per cent by weight, preferably 5 to 20 per cent by weight, of units of a dialkylaminoalkyl acrylate or meth­ acrylate, for example diethylaminoethyl methacrylate or dimethylaminoethyl methacrylate or of a dialkylamino­ alkyl-substituted amide such as dimethylaminopropyl meth­ acrylamide. The amine groups can alternatively be second­ ary amine groups particularly if these are linked to a tertiary alkyl group; for example the addition copolymer may be a copolymer of a hydroxyalkyl acrylate or meth­ acrylate and t-butylaminoethyl methacrylate. Alterna­ tively, tertiary or secondary amine groups can be intro­ duced into an acrylic resin by copolymerising glycidyl acrylate or methacrylate with the unsaturated hydroxyalkyl ester and subsequently reacting all or part of the gly­ cidyl groups with a secondary or primary amine. The hydroxy component (B) suitably contains 2 to 50, prefer­ ably 5 to 20 per cent by weight of the resulting modified units. The addition polymer generally contains one or more comonomers which do not have reactive functional groups, for example an acrylic ester such as methyl meth­ acrylate, ethyl methacrylate or ethyl acrylate, or styrene. Such addition polymers can be used in the powder coating composition with any of the anhydride or acid-functional components (A) described above. The addition polymer can be a grafted copolymer of acrylic monomers, including a hydroxy-functional monomer and an amine-functional monomer, onto an unsaturated polyester. The polyester segment is preferably of low molecular weight formed from the glycol and polycarboxylic acid and/or anhydride reagents described above and includ­ ing an unsaturated acid or anhydride such as maleic an­ hydride or itaconic acid. An alternative type of hydroxy- and amine-functional resin of Tg 0-120°C suitable for use as component (B) can be prepared by the reaction of an epoxy resin and an amine. The epoxy resin can for example be a condensed glycidyl ether of bisphenol A such as that sold under the trade mark "Epikote 1004", an epoxy novolac resin or a cycloaliphatic diepoxide. The product of the epoxy resin and amine contains hydroxy and amine groups accord­ ing to the following reaction: where Z is the residue of the epoxy resin, R IV is an organic group linked to the nitrogen atom through a car­ bon-nitrogen bond, preferably an alkyl or hydroxyalkyl group, and R V is hydrogen or an organic group linked to the nitrogen atom through a carbon-nitrogen bond or R IV and R V are such organic groups joined to form a heterocyclic ring. The amine is preferably a secondary amine and preferably contains at least one hydroxyalkyl group, for example N-methylethanolamine, N-ethylethanol­ amine or diethanolamine, to introduce further hydroxyl groups. Such epoxy resin/amine adducts are preferably used in the powder coating composition with a synthetic resin containing anhydride groups, for example an anhy­ dride-tipped polyester. A further example of a polymer of Tg 0-120°C suitable for use as hydroxy component (B) is a hydroxy-functional polyester modified to contain amine groups, preferably tertiary amine groups. Such a polyester may be prepared by reacting an excess of one or more glycols with a poly­ carboxylic acid and/or anhydride component. The glycols used in preparing the polyester are preferably of the same type as described above in connection with anhydride-­ functional polyesters. The polycarboxylic acid and/or anhydride component preferably consists at least partly of aromatic dicarboxylic acid or anhydride as described above and also includes an olefinically unsaturated di­ carboxylic acid. The hydroxy-functional polyester thereby formed contains double bonds from the unsaturated dicar­ boxylic acid. Amine groups can be introduced by a Michael-type addition to the double bond. For example, a polyester containing itaconic acid residues can be reacted with a secondary amine to introduce tertiary amine groups according to the following reaction: where Z' and Z" represent polymer residues and R IV and R V are defined as above. The amine is preferably a sec­ ondary amine to introduce tertiary amine groups into the polymers, for example diethylamine, di-n-propylamine, di-n-butylamine, N-methylethanolamine, N-ethylethanolamine or diethanolamine. The use of an aminoalcohol such as N-methylethanolamine or diethanolamine introduces further hydroxy groups into the polyester as well as tertiary amine groups. In an alternative method of forming a hydroxy- and amine-functional polyester an unsaturated carboxy-func­ tional polyester is formed by reacting a minor proportion of an unsaturated monocarboxylic acid such as acrylic or methacrylic acid with the glycol and polycarboxylic acid and/or anhydride reagents. The acrylic or meth­ acrylic residue is incorporated at the end of the polymer chain and can be reacted with an aminoalcohol by the Michael-type addition reaction described above, preferably with a di(hydroxyalkyl)amine such as diethanolamine, to introduce hydroxy and amine groups. The hydroxy-functional polyesters of Tg0-120°C containing amine groups are preferably used in powder coating compositions with a low molecular weight anhydride component (A) such as tricarballylic anhydride or with an addition copolymer containing anhydride groups along its chain. Examples of solid, low molecular weight compounds containing at least two hydroxy groups and at least one amino group which can be used as hydroxy component (B) when the anhydride component (A) is a resin of Tg 0-­ 120°C, for example an anhydride-tipped polymer, include tertiary carbinamines of the formula: where R VI represents a methyl group or a hydroxyalkyl group having 1 to 4 carbon atoms, for example tris­ (hydroxymethyl)-methylamine or 2-amino-2-methyl-propane-­ 1,3-diol. The corresponding secondary and tertiary amines in which the amine nitrogen atom is substituted, for example with a methyl group or a hydroxyethyl group, can also be used. Alternative hydroxy amines are the reaction products of glycidol with a diamine, particularly a heterocyclic diamine such as piperazine. The reaction product of glycidol and piperazine is a bis(dihydroxy­ alkyl) amine of the formula: The amine groups in the hydroxy component (B) are most preferably tertiary amine groups, although primary or secondary amine groups adjacent to a tertiary carbon atom are also preferred, particularly when lower molecular weight amino alcohols such as the tertiary carbinamines described above are used. The powder coating compositions can be formulated using known methods. The components (A) and (B) are generally mixed in the dry state together with any other ingredients of the coating composition such as pigments or fillers. The dry mixture is then extruded at a temper­ ature above the glass transition temperature of at least one synthetic resin component but below the temperature at which substantial fusion takes place, for example at a temperature in the range 80 to 120°C. The extrudate is comminuted to form the powder coating composition, which is then applied to the substrate to be coated, which may or may not be preheated, preferably by electro­ static spraying. The coated substrate is then heated to a temperature, usually in the range 120 to 220°C, at which the synthetic resin component of the powder coating flows and the coating cures. The components (A) and (B) are preferably used in relative proportions to provide from about one hydroxy group per carboxylic acid group to about one hydroxy group per carboxylic anhydride group +- 10%. The powder coating can for example be applied to steel pipelines, office furniture, motor car components, reinforcing bars for concrete or aluminium window frames. Whilst any synthetic resin used as a component in the powder coating composition can generally have a Tg in the range 0-120°C, special precautions such as low-­ temperature grinding and storage are required if the Tg is near the lower end of this range. The Tg of any synthetic resin used in the powder coating composition is preferably 25-110°C and most preferably 40-90°C. The powder coatings of the invention are capable of forming cured films with particularly good gloss and weathering properties such as resistance to sunlight, particularly when the anhydride component (A) and hydroxy component (B) are acrylic polymers or when a hydroxy-­ functional acrylic polymer (B) is used with a tricarbox­ ylic compound such as tricarballylic anhydride as compon­ ent (A). The presence of amine groups in the hydroxy-­ functional components (B) allows curing at lower tempera­ ture. For example, a powder coating containing an acrylic polymer containing hydroxyl and amine groups and an anhy­ dride-functional component (A) will cure to a hard solvent-resistant coating at 170°C, whereas if an acrylic polymer containing hydroxyl groups but no amine groups is used there is insufficient curing at 170°C. The invention is illustrated by the following Examples. Example 1 (a) Preparation of Tricarballylic Anhydride Tricarballylic acid was prepared by the method of Clarke and Murray (Org. Synth. Coll. Vol. 1, P.523). Tricarballylic acid (580 g) was mixed with acetic anhy­ dride (679 g), acetic acid (1779 g) and chloroform 25(2834 g) and the mixture stirred at reflux for 4.5 hours and allowed to cool. The precipitate which formed after 32 hours was collected, dried in vacuo below 110°C, and dissolved in 10 times its weight of a crystallisation mixture comprising chloroform (1000 parts), glacial acetic acid (900 parts) and acetic anhydride (100 parts), pre­ mixed at least 12 hours before use. The solution was filtered and allowed to cool. The white precipitate which formed within 36 hours was collected and dried in vacuo below 100°C. 210 g of material containing 90 per cent of tri­ carballylic anhydride, the residue being principally tricarballylic acid, was obtained. Analysis was by gas chromatography of the silanised product. (b) Preparation of Hydroxy - and Amine-Functional Acrylic Polymer Methyl methacrylate (2650 g), ethyl acrylate (600 g), hydroxyethyl acrylate (315 g), diethylaminoethyl methacrylate (500 g), methyl isobutyl ketone (MIBK) (783 g) and azobisisobutyronitrile (AZBN) (160 g) were mixed, filtered and pumped over 4 hours into a further 3000 g of MIBK refluxing at about 112°C in a reaction vessel equipped with stirrer, thermometer and reflux condenser. One hour after addition was complete, a further 4 g of AZBN dissolved in 225 g of MIBK was added, the mixture held at reflux for one hour, and a further "booster" of the same composition added. After a further hour, solvent was distilled off under vacuum to yield a glassy resin of cone and plate viscosity 3.5 poise (0.35 Pas) at 200°C, Tg 40°C, molecu­ lar weight 6000 by g.p.c. and hydroxyl equivalent weight 1560. (c) Powder Coating Compositions The acrylic polymer prepared in Example 1(b) ground to a coarse powder (606.1 g), tricarballylic anhydride (31.9 g), rutile titanium dioxide (350 g), Modaflow 3 (Trade Mark) acrylic polymer flow promoting agent (10 g), and benzoin (2 g) were premixed and co-extruded at 80°C. The extrudate was micronised to a powder of average particle size 50 microns, electrostatically sprayed onto steel panels and stoved for 15 minutes at 170°C. The films obtained were glossy, hard and crosslinked, resist­ ing rubbing with an acetone-soaked cloth. Example 2 (a) Preparation of Anhydride-Functional Polyester Isophthalic acid (1992 g), adipic acid (584g), pentaerythritol (136 g), neopentyl glycol (1664 g) and xylene (75 g) were charged to a reaction vessel fitted with stirrer, condenser and thermometer, and heated to reflux. After about 12 hours, the temperature had risen to 240°C, 500 g of water had been removed and the acid value fallen to 10. Xylene was removed by distillation in vacuo , and replaced by MIBK (150 g). Tricarballylic anhydride (894 g) was charged at 120°C, and the tempera­ ture maintained for 12 hours, ensuring only gentle reflux. A Dean and Starke trap was then fitted and vigorous re­ fluxing to remove water continued for 4 hours. Solvent was removed in vacuo to yield a glassy polymer of anhy­ dride equivalent weight approx. 1000, Tg 50°C and viscos­ ity 40 poise (4 Pas) at 200°C. (b) Preparation of Powder Coatings The anhydride-functional polyester prepared in (a) above (1000 g), tris(hydroxymethyl)methylamine (40 g), TiO₂ (1350 g), Modaflow 3 (10 g) and benzoin (2 g) were mixed, extruded at 100°C, and micronised, sprayed and stoved as described in Example 1 to yield hard, tough coatings. Example 3 (a) Preparation of Hydroxy-Functional Acrylic Polymer The procedure of Example 1(b) was repeated exactly, except that the monomer mixture comprised only methyl methacrylate (2850 g), ethyl acrylate (900 g) and hydroxy­ ethyl acrylate (315 g) to prepare an amine-free polymer. The product had a viscosity of 4 poise (0.4 Pas) at 200°C, Tg 45°C, molecular weight 8000 by g.p.c., and hydroxyl equivalent weight of 1560. (b) Preparation of Anhydride-Functional Acrylic Polymer The amine-free hydroxyacrylic polymer (1560 g), tricarballylic anhydride (182 g) and MIBK (87 g) were stirred together at 120°C with reflux for 16 hours. A Dean and Starke trap was then fitted, and vigorous reflux continued for 2 hours. The product was then dried in vacuo to a glassy brittle anhydride-functional resin. (c) Preparation of Powder Coating The anhydride-functional resin of Example 3(b) (875 g), tris(hydroxymethyl)-methylamine (20 g) TiO₂ (350 g), Modaflow 3 (10 g) and Benzoin (2 g) were mixed, co­ extruded, micronised, sprayed and stoved as described in Example 1(c) to yield hard, cured coatings. Example 4 The anhydride-functional polymer of Example 3(b) (1750 g) was mixed with the hydroxy- and amine-functional acrylic polymer of Example 1(b) (1560 g), TiO₂ (1815 g), Modaflow 3 (52 g) and benzoin (10 g) and co-extruded, micronised, sprayed, and stoved as described in Example 1(c) to form a hard, solvent-resistant coating. Example 5 (a) Preparation of Anhydride Component The amine-free hydroxyacrylic polymer of Example 3(a) (1560 g), tricarballylic anhydride (33.0 g) and MIBK (95 g) were refluxed together for 8 hours, followed by in vacuo drying below 120°C. The product was a mixture of anhydride-functional acrylic polymer and tricarballylic anhydride, both components active in curing. (b) Preparation of Powder Coating The anhydride component prepared in Example 5(a) (950 g) was mixed with the hydroxy- and amine-functional acrylic polymer of Example 1(b) (1560 g), TiO₂ (1375 g), Modaflow 3 (40 g) and benzoin (8 g) and extruded, micron­ ised, sprayed and stoved as described in Example 1. A hard, smooth cured film was obtained. Example 6 The hydroxy and amine-functional polymer of Example 1(b) (606.1 g) was mixed with tricarballylic acid (34.2 g) and pigments and additives and formed into a powder coating and applied as described in Example 1(c). Comparative Example The procedure of Example 1(c) was repeated using the amine-free hydroxy-functional acrylic polymer of Example 3(a) in place of the polymer of Example 1(b). The films produced were uncured and of poor appearance (low gloss).

Claims: 1. A powder coating composition comprising a compon­ ent (A) containing carboxylic acid or anhydride function­ ality and a component (B) containing hydroxy function­ ality, the components (A) and (B) both being solids at temperatures up to 50°C and at least one of (A) and (B) being a synthetic resin having a glass transition tempera­ ture in the range 0 to 120°C, characterised in that the carboxylic acid or anhydride-functional component (A) is a compound or polymer containing at least two cyclic carboxylic anhydride groups per molecule or is a compound containing a moiety of the formula:- where X is a hydrogen atom or an alkyl group, or a cyclic anhydride thereof, provided that the carboxylic acid or anhydride-­ functional component (A) does not contain an olefinically unsaturated double bond in the alpha, beta- or beta, gamma-­ position with respect to any carboxylic acid or anhydride group and provided that if the component (A) is an addition polymer the carboxylic acid or anhydride groups are separ­ ated from the addition polymer chain by at least one inter­ vening carbon atom, and the hydroxy-functional component (B) contains at least two hydroxyl groups per molecule and contains at least one amine group in its molecule to catalyse the reaction of the carboxylic acid or anhydride groups of component (A) with the hydroxy groups of component (B). 2. A powder coating composition according to Claim 1, characterised in that the hydroxy component (B) is an addition copolymer of glass transition temperature 0 to 120°C having pendent hydroxyl and amine groups. 3. A powder coating composition according to Claim 2, characterised in that the hydroxy component (B) is an addition copolymer containing 10 to 50 per cent by weight of units of a hydroxyalkyl ester of an olefin­ ically unsaturated carboxylic acid and 5 to 20 per cent by weight of units of a dialkylaminoalkyl ester of an olefinically unsaturated carboxylic acid or a dialkyl­ aminoalkyl-substituted amide of an olefinically unsatur­ ated acid. 4. A powder coating composition according to Claim 2, characterised in that the hydroxy component (B) is an addition copolymer containing 10 to 50 per cent by weight of units of a hydroxyalkyl ester of an olefinically unsaturated carboxylic acid and 2 to 50 per cent by weight of units of a glycidyl ester of an olefinically unsatur­ ated carboxylic acid which have been modified by reacting the glycidyl group with a secondary or primary amine. 5. A powder coating composition according to Claim 1, chracterised in that the hydroxy component (B) is a hydroxy-functional polyester modified to contain amine groups and having a glass transition temperature of 0 to 120°C. 6. A powder coating composition according to Claim 1, characterised in that the hydroxy component (B) is a reaction product of an epoxy resin and an amine and has a glass transition temperature of 0 to 120°C. 7. A powder coating composition according to any of claims l to 6, characterised in that the amine groups in the hydroxy component (B) are tertiary amine groups. 8. A powder coating composition according to Claim 1, characterised in that the hydroxy component (B) is a tertiary carbinamine of the formula:- where RVI represents a methyl group or a hydroxyalkyl group having 1 to 4 carbon atoms. 9. A powder coating composition according to Claim 8, characterised in that the tertiary carbinamine is tris(hydroxymethyl)-methylamine. 10. A powder coating composition according to any of Claims 1 to 9, characterised in that the component (A) contains at least two cyclic carboxylic anhydride groups per molecule. 11. A powder coating composition according to Claim 10, characterised in that the component (A) is an an­ hydride-tipped polymer having a glass transition tempera­ ture of 0 to 120°C. 12. A powder coating composition according to Claim 10 or Claim 11, characterised in that the component (A) is the reaction product of a hydroxy -functional polymer with a compound containing a moiety of the formula:- or a cyclic anhydride thereof and has a glass transition temperature of 0 to 120°C. 13. A powder coating composition according to Claim 12, characterised in that the component (A) is the react­ ion product of an addition copolymer having pendent hyd­ roxy groups with a compound containing a moiety of the formula:- or a cyclic anhydride thereof. 14. A powder coating composition according to Claim 12, characterised in that the component (A) is the react­ ion product of a hydroxy-functional polyester with a compound containing a moiety of the formula:- or a cyclic anhydride thereof. 15. A powder coating composition according to any of Claims 1 to 7, characterised in that the component (A) is the cyclic anhydride of a compound containing a moiety of the formula:- 16. A powder coating composition according to Claim 15, characterised in that the component (A) is tricar­ ballylic anhydride. 17. A powder coating composition according to any of Claims 1 to 7, characterised in that the component (A) comprises a cyclic anhydride as defined in Claim 15 and the reaction product of hydroxy-functional polymer with a cyclic anhydride as defined in Claim 15. 18. A powder coating composition according to any of Claims 1 to 7, characterised in that the component (A) is tricarballylic acid. 19. A process for coating a substrate comprising applying a thermosetting powder coating composition to the substrate to form a layer and heating the composition on the substrate to fuse at least one reactive component of the composition to cause it to flow and to react with another component to cure the composition, character­ ised in that the powder coating composition is a composit­ ion according to any of Claims 1 to 18.

Inventors: MARRION, ALASTAIR ROBERT
Applicants: COURTAULDS COATINGS LIMITED
Application year: 1986
Main classification: C09D5
IPC codes: C08G59, C09D167, C09D201, C09D163, C09D5