METHOD OF SULFONATING THE INTERIOR SURFACE OF A PLASTICS ENCLOSURE MEMBER

Abstract: Plastic containers are treated to provide increased barrier properties to organics and gases such as oxygen by treating the interior surface of the container with SO₃ gas. The SO₃ gas is provided by inserting a solid pellet of poly-SO₃ into the con­ tainer and evaporating the SO₃ such as with microwave en­ ergy. A solid neutralizing agent such as ammonium carbonate is then placed into the container and evaporated with micro­ wave energy to form ammonia which neutralizes the sulfonic acid groups on the surface interior of the container.

Description: The invention is directed to a method of sulfonating the interior surface of an enclosure member formed of a resinous organic polymer which is capable of being surface sulfonated when contacted with SO₃ vapors wherenin the interior surface is contacted with a sufficient quantity of gaseous SO₃ to form sulfonic acid groups along the backbone of the resinous organic polymer. The use of resinous organic polymers to fabricate enclosure members (plastics containers) such as bottles, tanks and other containers and other molded articles is well known. Plastics containers which are made from most organic polymers, particularly the dominantly hydrocarbon polymers, are non-electroconductive, are non-adherent to polar materials such as inks, paints, dyes and various polar adhesives and are readily permeated and/or stress cracked or swollen by oleophilic materials such as liquid and gaseous hydrocarbons e.g., solvents, fumes, vapors, benzene, cyclohexane, xylene, chlorinated solvents, and hexane; gasses such as nitrogen, oxygen, helium, hydrogen, carbon dioxide, methane, ethane, propane, butane, freons (FREON® is a registered trade mark); fuels such as gasoline, kerosene, fuel oils; oils such as natural fatty oils, lubricating oils, perfumes and agricultural chemicals. Depending on the particular polymer, these materials can adversely affect the container material. For example, natural fatty oils tend to cause stress cracking of polymers formed from olefinic monomers such as polyethylene. As a result of these inherent deficiencies many of such organic polymers must be treated with various agents which impart varying degrees of electroconductivity, adhesion and impermeability. Sulfonation techniques have been developed as one means of treating these polymeric materials to decrease the permeability and protect the polymeric material. Some of these sulfonation techniques are described in the following patents: U.S. Patent Nos. 2,400,720; 2,937,066; 2,786,780; 2,832,696; 3,613,957; 3,740,258; 3,770,706; and 4,220,739. In Patent No. 4,220,739 the sulfonation technique is improved by employing as the sulfonating agent a gaseous mixture comprising sulfur trioxide and a suitably active halogen e.g. chlorine. In DE-A-3 113 919 a process is disclosed for sulfonating the interior surface of an enclosure member formed of a resinous organic polymer which is capable of being surface sulfonated when contacted with a sufficient quantity of gaseous SO₃ to form sulfonic acid groups along the backbone of the polymer, the degree of surface sulfonation of the polymer being 0.001 to 50 mg SO₃/cm². All of these prior sulfonation techniques require the generation of a suitable gaseous sulfonating agent such as, for example, sulfur trioxide. Also, in many of these processes, the sulfur trioxide treated organic resinous container is post-treated with a material which improves the effectiveness of the sulfonation treatment. Neutralization with ammonium, metal ions, as well as expoxidation of the organic polymers employing a suitable organic epoxide have been utilized. These neutralization techniques also many times require the generation of gases. In those processes employing gaseous treating agents, for example, sulfur trioxide, ammonia, etc., gas generating equipment has been employed to generate mixtures of air and sulfur trioxide or neutralizing agents at the site where sulfonation is to be carried out. In many instances this gas generating equipment requires a capital investment which is as great as all the other equipment required to carry out the sulfonation process. Moreover, this equipment takes up considerable space and requires expert maintenance. Use of such equipment also requires start-up and shut-down procedures. It would therefore be an improvement in the art-recognized processes of employing gaseous sulfonating compounds to treat the interior of resinous containers if a different method of generating the sulfonating and/or neutralizing gas could be employed. The present invention concerns such an improved method of sulfonating and/or neutralizing the interior surfaces of plastics containers which are made from resinous organic polymers which are capable of being surface treated with a sulfonating gas to improve certain characteristics (e.g., decrease permeability, stress cracking, swelling) of the polymer. The invention is directed to a method of sulfonating the interior surface of an enclosure member formed of a resinous organic polymer which is capable of being surface sulfonated when contacted with So₃ vapors wherein the interior surface is contacted with a sufficient quantity of gaseous So₃ to form sulfonic acid groups along the backbone of the resinous organic polymer, said method comprising the step of introducing into the interior of the enclosure member a solid composite comprising an inert porous substrate in particulate form containing adhered therein solid SO₃ and heating said composite to form a sufficient quantity of sulfur trioxide gas to react with at least a portion of the interior surface of said enclosure member thereby forming said sulfonic acid groups attached to the resinous organic polymer. In the practice of the present invention a material, in particulate form, which, upon heating, forms the desired treating agent e.g., sulfur trioxide gas and/or gaseous neutralizing agent is introduced into the interior of an enclosure member fabricated from a resinous organic polymer and thereafter heated to form the gaseous treating agent e.g., sulfur trioxide, at least a portion of which reacts with the interior surface of the enclosure member to treat (sulfonate or neutralize) the same. The resinous organic polymer is any organic polymer which is capable of being sulfonated when contacted with a sulfonating gas such as sulfur trioxide. A solid particulate material is employed for the sulfonating treatment, e.g., pellets, encapsulated materials and the like which contain for example solid SO₃ can be used. The particulate material may contain absorbed solid SO₃ or solid SO₃ can be coated with a suitable material such as a fluorocarbon or the like to maintain the SO₃ in a form suitable for use for a sufficient period of time. Gaseous SO₃ is formed by sypplying sufficient heat to the solid SO₃ to cause it to vaporize. Heating elements or other activating devices such as radio frequency energy, e.g., micro waves, heated air or the like can be employed. The sulfonated surface is preferably treated with a suitable material to neutralize the sulfonic acid groups formed on the polymer to prevent the reaction of such groups with materials to be placed in the plastic container. This can be accomplished by contacting the sulfonated surface with a gas or liquid which reacts with the sulfonic acid groups to neutralize them. Ammonia gas is an example of a suitable neutralizing agent. A preferred method is to use a solid material such as ammonium carbonate which when heated by the use of, for example, a heat source or radio frequency energy forms ammonia gas. Other suitable neutralizing agents can also be employed. Resinous organic polymers capable of being sulfonated have hydrogen atoms bonded to the carbon groups which are replacable by sulfonic acid groups having the sulfur bonded directly to the carbon atoms. Polytetrafluoroethylene is an example of a polymer which is not sulfonatable since it does not have any replacable hydrogen atoms. Suitable organic polymers include thermosetting plastics such as epoxy resins, phenol formaldehyde resins, urea-formaldehyde resins, silicones, polyurethanes and the like. Most thermoplastic polymers are also suitable and include for example, addition-type homopolymers, copolymers and blends thereof prepared from aliphatic α-mono-olefins; aliphatic conjugated and non-conjugated dienes, trienes, polyenes, halogenated aliphatic olefins, α, β-ethylenically unsaturated carboxylic acids, vinylesters of non-polymerizable carboxylic acids, alkyl esters of α, β-ethylenically unsaturated carboxylic acids, monovinylidene aromatic monomers, α, β-ethylenically unsaturated nitriles and amides, ethylenically unsaturated ethers and ketones, and other ethylenically unsaturated monomers which polymerize across the ethylenic groups to form polymers having a linear carbon-to-carbon backbone molecular structure with a plurality of free hydrogen atoms attached to the chain and/or attached to carbon atoms of the substituents of the chain. Also included as suitable organic polymers are the thermoplastic condensation-type polymers exemplified by the polyamides such as nylon, the polyimides, the polyesters such as polyethylene, terephthalate, the polycarbonates such as the polyesters of carbonic acid and alkylidene diphenols; the polyethers such as polyformaldehyde and the like. Other organic polymers include thermoplastic addition type homopolymers, copolymers and mixtures of polymers of the following monomers: aliphatic monoolefins having from 2 to 18 carbon atoms such as ethylene, propylene, butene-1 and isobutylene and the like; aliphatic conjugated dienes and trienes having from 4 to 20 carbon atoms such as butadiene, isoprene, heptatriene, monovinylidene aromatic monomers and the like. The particular polymer employed to make the plastic container is not critical to the practice of the invention provided the polymer is capable of being sulfonated. The resinous organic polymers can be fabricated into various enclosure members by techniques well-known in the art. According to the invention, gaseous sulfur trioxide is formed in situ in the interior of the container by placing a particulate form of a sulfur trioxide gas generating material into the interior of the container and thereafter gasifying the material to form sulfur trioxide. The gasifying technique includes heating a solid sulfur trioxide containing material, e.g., a pellet or pill, for example, by contact with radio frequency energy e.g., microwaves, employed at an energy level sufficient to gasify the material. Other methods of gasifying the material can be employed e.g., hot air, heating elements, infrared energy and the like. It is remarked that the article 'Modification of polyethylene with sulphur trioxide' in International Polymer Science and Technology, Vol. 4, No. 1, 1977, pp T/42 and T/43, discloses the use of solid, i.e. polymeric SO₃ for the generation of pure SO₃. One form of solid material which can be employed to generate sulfur trioxide is the solid polymerized form of sulfur trioxide itself. The sulfur trioxide polymer may be formed into pellets with a coating or casing of a suitable protective material. Suitable coatings include for example polytetrafluoro-ethylene and fluorochlorocarbon polymers such as polychlorotrifluoroethylene. Other suitable coatings include for example, elemental sulfur, tetrachlorophthalic anhydride, shellac modified by reaction with the tetrachlorophthalic anhydride and relatively high melting polyolefins such as polyethylene and the like. British Patent No. 1,125,091 teaches various coated sulfur trioxide solids which can be employed in the practice of the present invention. Liquid sulfur trioxide can also absorb or be coated onto various inert substrates and permitted to solidify. Substrates such as clay, glass or silicon are preferably used. In a preferred embodiment of the invention, the sulfonated interior of an enclosure member is treated with an agent which neutralizes the sulfonic acid groups on the polymer. Suitable neutralizing agents are taught for example in U.S. Patent Nos. 3,613,957; 4,220,739, and 3,770,706. In this embodiment, the neutralizing agent is preferably employed in the form of a solid material, e.g., a solid pellet or a pill-like material, which when suitably activated (e.g., sufficiently heated) produces a gas. For example, if it is desired to neutralize the sulfonated surface with ammonia, a solid ammonium compound, which upon heating forms ammonia vapors, such as ammonium carbamate, ammonium bicarbonate, ammonium carbamate acid carbonate or the like, in a particulate form, may be inserted into the container and heated with radio frequency energy, for example microwaves, to form ammonia. The heating source employed in both the sulfonation and neutralization steps is preferably radio frequency energy, e.g., microwaves. Radio frequency of suitable wavelength to heat the sulfur trioxide source and the neutralizing agent is employed. The wavelength may vary depending on the particular material employed and the nature of the resinous organic polymer. Suitable wavelengths can easily be determined experimentally or from literature sources. For polymerized solid SO₃ a wavelength of from 3 x 10⁻² to 3 x 10⁴cm⁻¹ or from 10¹² to 10⁶ Hertz is suitable. A preferred wavelength is from 3 to 3,000 cm⁻¹ (10¹⁰ to 10⁷ Hertz). Temperature is not critical in carrying out the sulfonation or neutralization steps (other than activating the source materials). Temperatures within the range of from 0°C to 110°C, preferably from 20° to 40°C, are suitable. The sulfonation and neutralization steps can be carried out at atmospheric, elevated pressures or under partial vacuum. The amount of sulfur trioxide gas required for the surface area contacted can easily be determined from simple laboratory tests or from the teachings of the art. Sufficient gas should be employed to impart sufficient sulfonation to the polymer to provide the desired improved characteristics. For example, it is taught in U.S. Patent No. 4,220,739 that the concentration of the sulfur trioxide should be sufficient and in an amount to provide a degree of surface sulfonation of the organic polymer in a range of from 0.001 to 50 milligrams of sulfur trioxide equivalence in the form of sulfonic acid groups per square centimeter of surface. Preferably from 0.06 to 10 milligrams per square centimeter is employed. The use of an excess of gas is desirable from the standpoint of speed of the sulfonation process. From 1 to 5 grams of SO₃ per liter of container volume is desirable. As one illustration of the practice of the present invention, a gasoline tank formed of high density polyethylene is treated in the following manner. A sufficient amount of polymerized sulfur trioxide pellets are placed into the container. After the solid sulfur trioxide has been placed inside the container, the solids are heated employing a microwave generating source having a suitable energy output and wavelength to gasify the solid polysulfur trioxide to form sulfur trioxide gas. Following a sufficient contact time of from 5 to 15 minutes, a neutralizing agent formed of solid ammonium carbonate is introduced into the container. The solid ammonium carbonate is subjected to sufficient microwave energy to form a gas which comprises ammonia, CO₂, and water. The ammonia will react with the sulfonic acid groups on the organic polymer to neutralize it to -SO - / 3NH₄⁺. The ammonia also neutralizes unreacted SO₃ to form ammonium sulfamate. Upon cooling all free ammonia will combine with the excess CO₂ to form solid ammonium carbamate. Following the neutralization step the interior of the container can be rinsed with water to remove these secondary reaction products. All of the above steps can be carried out at atmospheric pressure and room temperature. Improvement in the regularity and evenness of the surface treatment can be achieved by circulating air or an inert gas in the interior of the container during the sulfonation process and/or neutralizaton process. This can be accomplished, for example, by inserting a small fan into the interior of the container during the vaporization of the solid sulfur trioxide. Similar circulation techniques can be employed during the neutralization phase of the process. The container can also be closed after the insertion of the sulfonating agent and/or neutralizing agent thus resulting in a small pressure rise upon evaporation of the material. This will aid in treating the inner surface. Example 1 A one gallon cylindrical pail (formed of high density polyethylene) having a lid and formed of a linear low density polyethylene was treated as follows. The container was white in color. A five gram pellet of polymeric form of SO₃ was placed in the container and the lid placed thereon. No external source of heat was applied to the container. After a period of one hour the lid was removed and the interior of the container and lid had turned a light brown color indicating sulfonation of the interior of the container had taken place. A portion of the pellet remained and the area of the container closely adjacent to the pellet was darker in color evidencing a higher degree of sulfonation of the polyethylene. Example 2 A one quart zippered plastic bag made of polyethylene was treated as follows. A 0.5 gram portion of solid SO₃ was placed in a hollow microscope slide and covered with a flat glass slide. This was placed into the bag which was then closed. The bag was placed between the flat electrodes (20 mm spacing) of a microwave generator (Thermall® brand microwave generator manufactured by W. T. LaRose and Associates Inc., Model EO-1 having a frequency of 60-80 Hertz). The SO₃ evaporated when subjected to about ≅ 5 seconds of microwave energy. Following the SO₃ treatment, 10 ml of an aqueous solution of ammonia was introduced into the bag and swirled around to neutralize the sulfonic acid groups on the polymer. The inside of the bag had turned an orange-brown color indicating sulfonation of the polyethylene. Example 3 A particulate SO₃ material was prepared in the following manner. Particles having a dimension of about 5 mm were prepared from microporous fired clay having about 50 percent by volume of voids. Other particles based on fumed silica (grade M5 Cab-O-Sil from Cabott Corp.) were also prepared. Liquid SO₃ was deposited in various amounts, onto the individual particles. Particles containing from 50 to 90 percent by weight of solid SO₃ were prepared. The liquid SO₃ solidified within a short period of time (about 10 seconds) after being placed on the particles. Weight percent SO₃ was determined by dropping the SO₃ containing particle in water and titrating the resulting acidity. The SO₃ prepared particles were evaluated for shelf life by noting the time it took the particles to fuse together. Fusing was caused by the SO₃ vapor given off by the particles forming needle-like crystals which bridge across the particles interconnecting them. The so-prepared particles can be employed in the process of the invention as hereinbefore described.

Claims: A method of sulfonating the interior surface of an enclosure member formed of a resinous organic polymer which is capable of being surface sulfonated when contacted with SO₃ vapors wherein the interior surface is contacted with a sufficient quantity of gaseous SO₃ to form sulfonic acid groups along the backbone of the resinous organic polymer, comprising the step of introducing into the interior of the enclosure member a solid composite comprising an inert porous substrate in particulate form containing adhered therein solid SO₃ and heating said composite to form a sufficient quantity of sulfur trioxide gas to react with at least a portion of the interior surface of said enclosure member thereby forming said sulfonic acid groups attached to the resinous organic polymer. The method of claim 1 wherein subsequent to the formation of the sulfonic acid groups a solid material, which upon heating forms a gas which is capable of neutralizing the sulfonic acid groups, is introduced into the interior of the enclosure member and subsequently heated to form a gas which neutralizes the sulfonic acid groups. The method of claim 2 wherein the solid neutralizing material is an ammonium compound which upon heating forms ammonia vapors. The method of claims 1, 2 or 3 wherein heating is accomplished with radio frequency waves. The method of claim 1 wherein the said porous substrate is an inorganic material selected from the group consisting of clay, glass or silicon.

Inventors: WALLES, WILHELM E.
Applicants: THE DOW CHEMICAL COMPANY
Application year: 1986
Main classification: C08J7
IPC codes: B65D25, C08J7