OXAZOLINE/POLYOL/POLYISOCYANATE POLYMERS AND PROCESS

Abstract: Novel interpolymers obtained by the interpolymerization of an oxazoline, a polyol and a polyisocyanate at a temperature in the range of from about 20°C. and at a pressure in the range of from about atmospheric up to about 50 atmospheres and a process for their preparation are described.

Description: This invention relates to a process for the preparation of interpolymers of oxazolines, polyols and polyisocyanates, to the novel interpolymers thus produced and to some applications for the novel interpolymers. The reaction of a mono-oxazoline with phenyl isocyanate to give a monomeric product has been described in Ann. Chem. 698,167 (1966) by Nehring and Seeliger. U.S. Patent No. 3,661,861 discloses the reaction of an oxazoline with a diisocyanate in a solvent to produce an air-drying coating material which forms a film by reaction with atmospheric moisture. Providing suitable replacements for methylene B is orthochloraniline in US-A-4,028,312 polyurethanes have been prepared and cured with an oxaroline having a propane-1,3-dihydroxy-2-ylene group in the 2-position. EP-A-0001412 relates to derivatives of polyparabanic acid and to a process for their preparation. These derivatives can have NCO groups capable of curing polyols. It has now been discovered that the interaction of oxazolines, polyols and polyisocyanates produces thermosetting polymers which are useful in polymer composites and particularly in reaction injection molding (RIM) applications. The novel thermosetting polymers produced in this process have good physical properties. According to the present application 2-alkyl oxazolines (mono or bis) of general Formula I will react rapidly with mixtures of polyols and polyisocyanates to give thermosetting polymers having good physical properties. In Formula I n represents 2 or 3 and m represents 1 or 2. When m is 1, R represents an alkyl group having from 1 to 20 carbon atoms and an alkaryl group having from 7 to 20 carbon atoms; when m is 2, R represents an alkylene group having from l to l9 carbon atoms and R′ and R″ independently represent hydrogen, an alkyl group having from l to l0 carbon atoms or an aryl group having from 6 to 12 carbon atoms. Alternatively, in the case where the polyol is poly(tetramethylene ether)diol, the oxazoline is 2-hydroxy pentyl-4-methyl-4-hydroxy methyl-2-oxazoline. The polyols useful in this invention include those having at least two hydroxyl groups per molecule and having equivalent weights falling in the range of from 20 to 500. Such polyols include butane diol, cyclohexane dimethanol, tripropylene glycol, amide diols, urethane diols, polyether polyols such as poly (tetramethylene ether) diols, poly (propylene ether) polyols and polyester polyols. Polyhydroxy polyethers are suitable and preferably those having at least 2 hydroxyl groups per molecule can be used. Polyhydroxy polyethers can be prepared by polymerization of epoxides such as ethylene oxide, propylene oxide, butylene oxide, tetrahydrofuran, styrene oxide, or epichlorohydrin either on their own or by chemical addition to other materials. Suitable other materials include ethylene glycol, propylene glycol, trimethylol propanes and 4,4 dihydroxy diphenyl propane. Sucrose polyethers also may be used. Polybutadienes having hydroxyl groups as well as other known hydroxyl containing vinyl addition polymerized polymers can be used. According to this invention, hydroxyl containing polyesters, polythioethers, polyacetals, polycarbonates or polyesteramides of the types known for the formation of polyurethanes may also be used. Particularly useful polyols for the present invention include the following representative aliphatic and aromatic polyhydric alcohols such as ethylene glycol, propylene glycol, trimethylene glycol, triethylene glycol, pentaethylene glycol, polyethylene glycol, l,4-butanediol, diethylene glycol, dipropylene glycol, 2,2-dimethyl-l,3-propanediol, hexamethylene glycol, l,4-cyclohexane dimethanol, xylene alcohols, ethyl resorcinol, propylene resorcinol, 2,4-dimethyl resorcinol, 3,6 dimethyl-l,2,4-benzene triol, dimethylol toluene, dimethylol xylene, bis-hydroxyethyl or bis-hydroxypropyl ethers of resorcinol, catechol, or hydroquinones, l,5-dihydroxy naphthalene and 4,4′-isopropylidene-bis-phenol. The polyisocyanates useful in this invention include organic isocyanates having at least two isocyanate groups per molecule. The polyisocyanates can be of low, high or intermediate molecular weight and can be any of a wide variety of organic polyisocyanates including ethylene diisocyanate, trimethylene diisocyanate, dodecamethylene diisocyanate, hexamethylene diisocyanate, hexamethylene diisocyanate trimer, tetraethylene diisocyanate, pentamethylene diisocyanate, propylene-l, 2-diisocyanate, 2,3-dimethyl tetramethylene diisocyanate, butylene-l,2-diisocyanate, butylene-l,3-diisocyanate, l,4-diisocyanato cyclohexane, cyclopentene-l,3-diisocyanate, p-phenylene diisocyanate, l-methyl phenylene-2,4-diisocyanate, naphthalene-l,4-diisocyanate, toluene diisocyanate, diphenyl-4,4′-diisocyanate, xylylene-l,3-diisocyanate, 4,4′-diphenylene methane diisocyanate, 4,4′-diphenylene propane diisocyanate, l,2,3,4-tetraisocyanato butane, butane-l,2,3-triisocyanate, polymethylene polyphenyl isocyanate, and other polyisocyanates having an isocyanate functionality of at least two which are more fully disclosed in U.S. Patent Numbers 3,350,362 and 3,382,2l5. Polyisocyanates which are polymeric in nature including isocyanate prepolymers of all types are included in this invention. The equivalent ratio of oxazoline to polyol should be in the range of from l:99 to 95:5, respectively. The oxazoline group should be considered bifunctional towards isocyanate functionality. Thus, the equivalent amount of isocyanate functionality with respect to the combined hydroxyl and oxazoline functionality should be in the range of from 0.8:l to 3:l, respectively. Known polyurethane and isocyanurate catalysts such as organo tin compounds and tertiary amines can be included in the process of this invention. The polymers obtained from the simultaneous or sequential polymerization of oxazolines with polyols and polyisocyanates have been found to have high temperature resistance. The process and products of this invention can be used in the preparation of composite materials by impregnating a reinforcement such as glass fibers or graphite with monomeric or prepolymeric mixtures of these compositions. Although the polymerization process of this invention can be carried out at room temperature or slightly below, it is within the scope of the invention to conduct the reaction at a temperature in the range of from 20 to 200°C, preferably 20 to l00°C and at pressures in the range of from atmospheric up to about 50 bar. Reactions of polyisocyanates with polyols result in polyurethane formation, whereas oxazoline reaction with isocyanates results in urea and amide group containing polymeric material. Thus, in the instant polymeric system based on interaction of oxazoline/polyol/polyisocyanate, polymers with urethane, amide and urea groups are found in the polymers. In addition to this, isocyanurate groups can be generated in the polymers by the use of known isocyanurate catalysts such as hindered tertiary amines and tetraalkylammonium salts in the polymerization reaction. Our invention is further illustrated in the following representative examples. EXAMPLES l-l8 Several experiments were carried out in order to demonstrate the oxazoline/polyol/polyisocyanate reaction. The reactions were carried out in glass jars with thermocouple for recording the reaction temperature. The reactants were initially mixed at room temperature and left undisturbed in the jar for gellation to occur. The gel time was considered to be the maximum exotherm temperature. As can be seen from the results summarized in the Table, all the systems containing some oxazoline reacted at a much faster rate when compared with controls (Examples l, 7, ll, l3 and l5 which are outside the scope of this invention) which did not contain oxazoline. In the Table B.D. means Butanediol; T.P.G. means tripropylene glycol; Teracol 650 means 334 hydroxyl equivalent weight poly(tetramethylene ether) diol; BHED means bis-hy droxy ethyl dimerized linoleic acid; Polymeg® l000 means 492 hydroxyl equivalent weight poly (tetramethylene ether) diol; A means 2-ethyl-2-oxazoline; B means 2-undecyl-4,4-dimethyl-2-oxazoline); C means a mixture of 2,2′-dimethylene bis(4,4-dimethyl-l,2-oxazoline), 2,2′-trimethylene bis (4,4-dimethyl-2-oxazoline) and 2,2′-tetramethylene bis(4,4-dimethyl-2-oxazoline); D means 2,2′-tetramethylene bis (4,4-dimethyl-2-oxazoline); E means 2,2′-decamethylene bis(4,4-dimethyl-2-oxazoline); F means 2-hydroxypentyl-4-methyl-4-hydroxy methyl-2-oxazoline and G means 2-(methyl propylene) bis(2-oxazoline). The isocyanate used was liquid 4,4′-methylene bis(phenyl isocyanate). EXAMPLE l9 2-Ethyl-2-oxazoline (40g) and 33g of poly (tetramethylene ether) diol (hydroxyl equivalent weight of 492) were mixed and degassed on a rotary evaporator. This solution was mixed rapidly with l30g of degassed liquid 4,4′-methylene bis (phenyl isocyanate) (isocyanate equivalent weight of l44) and the resulting mixture was poured into a mold formed by two mold release agent coated parallel glass plates held apart by 3.2mm (l/8) inch spacers. The mold was kept in an oven at l00°C. for one hour followed by postcuring for one hour each at l45, l65, l80 and 200°C. The resulting solid opaque polymer sheet was found to have a notched izod impact strength (ASTM-D256) of 0.3 Nm/cm (0.5 foot pounds/inch) of notch and a heat distortion temperature (ASTM-D648) of 220°C. EXAMPLE 20 This example is for comparative purposes only and is outside the scope of the present invention. Following the procedure of Example l9 a polymer sheet was prepared from a mixture of 50g of the oxazoline and l52g of the polyisocyanate. The resulting sheet was found to be too brittle to be tested for its physical properties such as izod impact strength and heat distortion temperature. EXAMPLE 2l The procedure of Example l9 was followed using 29.5g of the oxazoline, 29.5g of bis-hydroxy ethyl dimerized linoleic acid (hydroxyl equivalent weight of 320) in place of the poly (tetramethylene ether) diol, 0.3g of a tertiary amine catalyst (N,N′,N″-tris(dimethyl amino propyl)hexahydrotriazine) and l08.5g of the polyisocyanate. The resulting polymer sheet was found to have a notched izod impact of 0.3 Nm/cm (0.5 foot pound/inch) of notch, a heat distortion temperature of 205°C., flexural strength (ASTM-D790) of 1133 bar (l6,43l psi) and a flexural modulus of 20494 bar (297,l37 psi). EXAMPLE 22 The procedure of Example 2l was followed using 3lg of the oxazoline, 62.lg of the bis-hydroxy ethyl dimerized linoleic acid, 0.3g of the catalyst and ll6g of the polyisocyanate. The resulting polymer sheet was found to have a notched izod impact strength of 90.3 Nm/cm (0.5 foot pounds/inch) of notch, a heat distortion temperature of l43°C., flexural strength of 766 bar (ll,lll) psi and flexural modulus of 13901 bar (20l,544 psi). EXAMPLE 23 A mixture of l4.8g of the oxazoline, and l4.8g of the polyol described in Example 2l was degassed and mixed with 54.3g of the polyisocyanate of Example 21. This solution was used to impregnate 10 layers of a 10.2 cm (4″) wide and 15.2 (6″) long glass cloth. The impregnated cloth was placed between the surfaces of a steel mold about 68.9 to 138 mbar (1 to 2 psi) was applied to the mold and the material was cured at 100°C for one hour followed by postcuring in the mold for one hour each at 140, 160, and 185°C. The resulting reinforced composite material which contained 62% glass was found to have a notched izod impact strength of 7.1 Nm/cm (13.3 foot pounds/inch) of notch (hinged break), heat distortion temperature greater than 220°C., flexural strength of 2901 bar (42,054 psi) and a flexural modulus of 129173 bar (1,872,886 psi). EXAMPLE 24 A glass reinforced composite was prepared by following the procedure of Example 23 using 14.8g of the oxazoline, 13.2g of poly (tetramethylene ether) diol (hydroxyl equivalent weight of 492) as the polyol and 54g of the polyisocyanate. The resulting cured composite which contained 66% glass was found to have a notched izod impact strength of 8.2 Nm/cm (15.3 foot pounds/inch) of notch (hinged break), a heat distortion temperature of greater than 220°C., a flexural strength of 38,829 psi and a flexural modulus of 2678 bar (1,582,432 psi). EXAMPLE 25 A solution of 40g of the oxazoline, 33g of the poly (tetramethylene ether) diol and 135g of the polyisocyanate was prepared by the procedure of Example 19. This solution was injected onto a glass mat placed in a steel mold with Teflon liner and was cured for one hour each at 100, 140, 160 and 180°C. The resulting polymer composite which contained 30% glass was found to have a notched izod impact strength of 4.4 Nm/cm (8.3 foot pounds/inch) of notch, a heat distortion temperature of greater than 210°C., a flexural strength of 1454 bar (21,082 psi), and a flexural modulus of 41468 bar (601,241 psi).

Claims: A polymer which is obtained by interpolymerizing an oxazoline, a polyol and a polyisocyanate at a temperature in the range of from 20°C to 200°C at a pressure in the range of from atmospheric up to about 50 bar, wherein the oxazoline conforms to the formula wherein R' and R'' independently represent hydrogen, an alkyl group having from 1 to 10 carbon atoms or an aryl group containing from 6 to 12 carbon atoms and n represents 2 or 3 and m represents 1 or 2 and when m is 1, R represents an alkyl group containing from 1 to 20 carbon atoms or an alkaryl group containing from 7 to 20 carbon atoms; when m is 2, R represents an alkylene group containing from 1 to 19 carbon atoms or wherein the polyol is poly(tetramethylene ether) diol and the oxazoline is 2-hydroxy pentyl-4-methyl-4-hydroxy methyl-2-oxazoline. A process for preparing the polymer of claim 1 comprising interpolymerizing at a temperature in the range of from 20°C to 200°C at a pressure in the range of from atmospheric up to about 50 bar an oxazoline of the formula I according to claim 1, a polyol and a polyisocyanate including the case wherein the polyol is poly(tetramethylene ether) diol and the oxazoline is 2-hydroxy pentyl-4-methyl-4-hydroxy methyl-2-oxazoline. The process of Claim 2 wherein the equivalent ratio of oxazoline to polyol is in the range of from 1:99 to 95:5, respectively and the equivalent amount of isocyanate functionality with respect to the combined polyol hydroxyl and oxazoline functionality is in the range of from 0.8:1 to 3:1, respectively. The process of Claim 3 wherein the polyol is one having at least two hydroxyl groups per molecule and has an equivalent weight falling in the range of from 20 to 500. The process of Claim 4 wherein the polyisocyanate is an organic isocyanate having at least two isocyanate groups per molecule. The process of Claim 5 wherein the polyisocyanate is a diisocyanate. The process of Claim 6 wherein the polyol is butane diol and the oxazoline is 2-ethyl-2-oxazoline. The process of Claim 6 wherein the polyol is butane diol and the oxazoline is 2-undecyl-4,4-dimethyl-2-oxazoline. The process of Claim 6 wherein the polyol is butane diol and the oxazoline is a mixture of 2,2'-dimethylene bis(4,4-dimethyl-2-oxazoline), 2,2'-tri-methylene bis(4,4-dimethyl-2-oxazoline) and 2,2'-tetramethylene bis(4,4-dimethyl-2-oxazoline). The process of Claim 6 wherein the polyol is butane diol and the oxazoline is 2,2'-tetramethylene bis(4,4-dimethyl-2-oxazoline). The process of Claim 6 wherein the polyol is butane diol and the oxazoline is 2,2'-decamethylene bis(4,4-dimethyl-2-oxazoline). The process of Claim 6 werein the polyol is tripropylene glycol and the oxazoline is 2-ethyl-2-oxazoline. The process of Claim 6 wherein the polyol is tripropylene glycol and the oxazoline is 2,2-tetramethylene bis(4,4-dimethyl-2-oxazoline). The process of Claim 6 wherein the polyol is tripropylene glycol and the oxazoline is a mixture of 2,2 `-dimethylene bis (4, 4-dimethyl-l, 2-oxazoline), 2,2'trimethylene bis(4,4-dimethyl-2-oxazoline) and 2,2'tetramethylene bis(4,4-dimethyl-2-oxazoline). The process of Claim 6 wherein the polyol is poly(tetramethylene ether) diol and the oxazoline is 2-ethyl-2-oxazoline. The process of Claim 6 wherein the polyol is bis-hydroxyethyl dimerized linoleic acid and the oxazoline is 2-ethyl-2-oxazoline. The process of Claim 6 wherein the polyol is poly(tetramethylene ether) diol and the oxazoline is 2-(methyl propylene) bis(2-oxazoline). The use of the polymer of claim 1 in polymer composites and reaction injection molding applications.

Inventors: BLACKBURN, PEGGY A., GOEL, ANIL B., TUFTS, TIMOTHY A.
Applicants: ASHLAND OIL, INC.
Application year: 1986
Main classification: C08G18
IPC codes: C08G18