Zeolitic reforming catalyst and method of producing the same

Abstract: A highly active and selective zeolitic reforming catalyst comprises a type L zeolite containing platinum metal and at least one promoter selected from iron, cobalt, titanium and the rare earth metals, the catalyst having a platinum to pro­ moter metal mole ratio of less than 10:1. In one embodiment a type L zeolite is formed by combining an aqueous solution of potassium hydroxide, aluminum hydroxide, and ferric ni­ trate with an aqueous solution of silica to form a thickening gel in a mother liquor; heating the thickening gel to form a type L zeolite; cooling the gel containing the type L zeolite; decanting the mother liquor from the gel; filtering the type L zeolite from the gel; washing the filtered type L zeolite so that the pH of the wash is about 10.5 and drying the washed type L zeolite. The catalyst is formed by adding platinum to the dried type L zeolite by pore fill impregnation with an aqueous solution of Pt(NH₃)₄(NO₃)₂ to form a catalyst; drying the catalyst and then calcining the dried catalyst.

Description: This invention relates to a highly active and highly selective dehydrocyclisation catalyst which comprises platinum, a type L zeolite, and at least one promoter metal selected from iron, cobalt, titanium and europium. . Catalytic reforming is a well-known process that is used to raise the octane rating of a naphtha. The reactions that occur during reforming include: dehydrogenation of cyclohexanes, dehydroisomerization of alkylcyclopentanes, dehydrocyclization of acyclic hydrocarbons, dealkylation of alkylbenzenes, isomerization of paraffins, and hydrocracking of paraffins. The hydrocracking reaction should be suppressed because that reaction lowers the yield of hydrogen and lowers the yield of liquid products. Reforming catalysts must be selective for dehydrocyclization in order to produce high yields of liquid product and low yields of light gases. These catalysts should possess good activity so that low temperatures can be used in the reformer. While most reforming catalysts contain platinum on an alumina support, large-pore zeolites have been proposed as catalyst supports. These large-pore zeolites have pores large enough for hydrocarbons in the gasoline boiling range to pass through. The present invention is based on the discovery that a highly active and highly selective type L zeolite-supported platinum, dehydrocyclisation catalyst can be made if the catalyst contains a promoter metal that is selected from iron, cobalt, titanium and europium; wherein said catalyst has a platinum to promoter metal mole ratio of less than 10:1. In one method of producing a catalyst in accordance with the invention, type L zeolite is formed by combining an aqueous solution of an alkali metal hydroxide, preferably potassium hydroxide, aluminum hydroxide, and a ferric salt, for example ferric nitrate, with an aqueous solution of silica to form a thickening gel in a mother liquor; heating and thickening gel to form a type L zeolite; cooling the gel containing the type L zeolite; decanting the mother liquor from the gel; filtering the type L zeolite from the gel; washing the filtered type L zeolite generally so that the pH of the wash is about 10.5; and drying the washed type L zeolite. The catalyst is formed by adding platinum to the dried type L zeolite, preferably by pore fill impregnation, for example with an aqueous solution of Pt (NH 3 ) 4 (NO 3 ) 2 or Pt (NH 3 ) 4 Cl 2 , the platinum being added in an amount sufficient to provide a platinum to promoter metal mole ratio of less than 10:1 in the resulting catalyst; drying the catalyst; and then calcining the dried catalyst. Alternatively, a barium form of the catalyst can be formed by ion exchanging the dried type L zeolite powder prior to platinum impregnation. Barium is added by mixing an aqueous solution of barium nitrate with the zeolite and heating the mixture; filtering the mixture; washing the filtered mixture to remove excess potassium ions; and drying and calcining the mixture. It has been found that the presence of a promoter, in particular iron, cobalt, titanium, or europium, in a zeolite-supported platinum catalyst has a major promoting effect on the aromatization activity of that catalyst. To have a high aromatization activity, the catalyst must have a platinum to promoter metal mole ratio of less than 10:1. As used herein, the term "promoter" means a metal that enhances the dehydrocyclization activity of a catalyst. The function of the promoter is to maintain the high initial activity of the noble metal catalyst. This promoter can be one of iron, cobalt, titanium, or europium. A common characteristic of promoter metals is that they all have either d or f valence electrons. The absolute level of promoter is important for making a highly selective reforming catalyst. With a low ratio of platinum/promoter, the original, highly active, well dispersed, platinum catalyst rapidly loses activity at reforming temperatures. Initial activity is best maintained when the platinum/promoter ratio is about one or less. On the other hand, it is well known that transition metals promote the undesired hydrocarbon cracking reactions. Therefore, one should avoid excess levels of these metals. Several methods exist for adding a promoter to a zeolitic reforming catalyst. In a preferred embodiment, the promoter is added during synthesis of the zeolite. In other embodiments, the promoter can be added after synthesis - either by impregnation or by ion exchange. However introduced, the promoter must be in an oxidized state (i.e. the metal must have a positive charge) prior to the addition of the Group VIII metal. The dehydrocyclization catalyst according to the invention commprises as the catalyst support a type L zeolite. Type L zeolites are synthetic zeolites. A theoretical formula is M 9/n [(Al 2 ) 9 (SiO 2 ) 27 ] in which M is a cation having the valency n. The real formula may vary without changing the crystalline structure; for example, the mole ratio of silicon to aluminum (Si/Al) may vary from 1.0 to 3.5. One method of forming the desired catalyst is by first forming a type L zeolite by combining an aqueous solution of potassium hydroxide, aluminum hydroxide, and ferric nitrate with an aqueous solution of silica to form a thickening gel in a mother liquor, heating the thickening gel, for example in an autoclave at about 302°F (150°C) for about 72 hours, to form a type L zeolite; cooling the gel containing the type L zeolite; decanting the mother liquor from the gel; filtering the type L zeolite from the gel; washing the filtered type L zeolite, for example three times in a ten-fold excess of water, so that the pH of the wash is about 10.5; and drying the washed type L zeolite, for example at about 250°F (121°C) for 16 hours. Then the catalyst is formed by adding platinum to the dried type L zeolite, preferably by pore fill impregnation with an aqueous solution of either Pt (NH 3 ) 4 (NO 3 ) 2 or Pt (NH 3 ) 4 Cl 2 to form a catalyst; drying the catalyst; and calcining the dried catalyst. An inorganic oxide can be used as a binder for the type L zeolite. This binder can be either natural, synthetically produced, or a combination of the two. Preferred loadings of inorganic oxide binders are from 5% to 50% of the weight of the catalyst. Useful binders include silica, alumina, aluminosilicates and clays. The catalyst of the invention can be used to reform a naphtha that is substantially free of sulfur, nitrogen, metals, and other known catalyst poisons. The poisons can be removed first by using conventional hydrofining techniques, then by using sorbents to remove the remaining poisons. Specifically, sulfur should normally be reduced to below 100 ppb in the feed. The naphtha can be contacted with the catalyst in either a fixed bed system, a moving bed system, a fluidized system, or a batch system. The pressure is generally from 1 atmosphere to 500 psig (35 bar). The preferred temperature is from 430°C to 550°C. The liquid hourly space velocity (LHSV) is preferably from 0.1 hr -1 to 10 hr -1 . Enough hydrogen is generally used to ensure an H 2 /HC ratio of from 1:1 to 20:1. The following Examples illustrate the invention. Example I Zeolite Preparation A 90°C solution was formed containing 102 grams KOH, 200 grams water, 47 grams Al(OH) 3 , and a prescribed amount of either Fe(NO 3 ) 3 .9H 2 O or K 3 Fe (CN) 6 . This solution was combined with a solution of 600 grams HS-30 Ludox (SiO 2 ) and 240 grams water. After shaking the combined solution in a Teflon (polytetrafluoroethylene) bottle for three minutes, the solution became a thickening gel. This thickening gel was heated in an autoclave at 25°F (-3.8°C)/hr. to 302°F (150°C) and held at 302°F (150°C) for 72 hours to form a crystalline material. When ferric nitrate was used, an orange-brown precipitate formed before heating, but when potassium ferric cyanide was used, the solution was yellow. However, in each case after crystallization, the zeolite was white and the supernate was colorless. After the solution was cooled, the mother liquor was decanted; the solid was filtered, washed three times in a ten-fold excess of water so that the pH of the wash was about 10.5, and dried. In each case, about 170 grams of zeolite was obtained and all of the added iron had been incorporated in the zeolite. X-ray diffraction measurements showed that all samples were 100% L zeolite. Analyses of the products are given in Table I. It appears that adding small amounts of iron did not affect the synthesis since, save for iron, the elemental analyses, X-ray diffraction data, and scanning electromicrographs showed that all of these materials were alike. The presence of iron and titanium impurities in the synthesis materials can also result in the incorporation of the active promoter metal in the zeolite support. In another preparation L zeolite was synthesized by dissolving 127.8 grams KOH in 127.8 grams of water, followed by the addition of 60.2 grams of Al 2 O 3 ·3H 2 O. This was boiled until everything dissolved. The solution was cooled to 50°C, diluted with 690.5 grams of water, and mixed. Then, 237.6 grams of Hi-Sil 233 (88% SiO 2 ) was added to the mixture and the mixture was homogenized. When the mixture was heated in an autoclave at 150°C for about 40 hours, L zeolite was produced. Elemental analysis of the product showed it to contain SiO 2 = 67.4%; Al 2 O 3 = 17.2%; K 2 O = 17.6%; Fe = 1300 ppm; Ti = 520 ppm (all concentrations are on a weight basis). Catalyst Preparation Platinum was added to the type L zeolite by pore fill impregnation with an aqueous solution of Pt (NH 3 ) 4 (NO 3 ) 2 . After sitting for two hours in a closed bottle, the material was dried at 250°F (121°C) for 16 hours and was calcined at 500°F (260°C) for three hours. Catalyst Testing The platinum-type L zeolite catalysts were tested for aromatization activity by loading the catalysts (as 24 to 80 mesh granules) in the middle of a 1 / 4-inch (6.4 mm) stainless steel reactor. The catalyst sample was surrounded by alundum. The catalyst was reduced in one atmosphere hydrogen (400-500 ml/minute) and heated to operating temperature with 30- and 10-minute stops at 400°F (204°C) and 700°F (371°C), respectively. The operating conditions were a temperature of 920°F (493°C), a pressure of 100 psig (7 bar), and an H 2 HC ratio of 6:1. The amount of catalyst used and the space velocity were adjusted so that the ratio of feed rate to loaded platinum was kept constant (e.g., one gram of a 1% platinum-type L zeolite catalyst would be compared to 0.5 grams of a 2% platinum-type L zeolite at the same feed rate). The catalysts were tested with a C 6 -C 7 naphtha since these light hydrocarbons are difficult to aromatize with conventional reforming catalysts. This feed consisted of 80v% paraffins, 16.2v% naphthenes, and 3.5v% aromatics. The boiling range (D86 distillation) for the naphtha feedstock was 145°F (63°C) initial point, 170°F (77°C) at 10% distilled, 180°F (82°C) at 30% distilled, 192°F (89°C) at 50% distilled, 218°F (103°C) at 80% distilled, 233°F (112°C) at 90% distilled and 277°F (136°C) at end point. The results, taken after 20 hours on stream, are given in Table II. The data in Table II show that the platinum to promoter metal mole ratio must be below 10:1 in order to have a conversion of more than 50%. Example II A series of catalysts was prepared wherein the principal promoter metal was other than iron. The same L-zeolite synthesis described in samples 1 through 6 of Example I was used and in each case the promoter metal was introduced as the nitrate salt. Platinum was added in the manner described previously to the level of 0.8 wt.%. Catalyst testing was carried out in the same way as in Example I. The levels of promoter metals in each catalyst and the corresponding catalytic test results are shown in Table III. A common characteristic of each of the promoter metals which was found to be effective was the presence of d or f valence electrons. Example IV The function of the promoter is to maintain the high initial activity of the noble metal catalyst. With a low ratio of platinum/promoter, the original, highly active, well dispersed, platinum catalyst rapidly loses activity at reforming temperatures. Initial activity is best maintained when the platinum/promoter ratio is about one or less. This is illustrated by the results of the dehydrocyclization tests shown in Table IV. In this test the feed was normal hexane, the pressure was one atmosphere, the temperature was 820°F (438°C), and the hydrogen/hydrocarbon ratio was 6. All of the catalysts consisted of L zeolite loaded with 0.8 wt.% platinum and the indicated level of promoter. The L zeolite supports for these catalysts were made as described in Example I with various amounts of nitrate salts added to the synthesis.

Claims: A dehydrocyclisation catalyst comprising a type L zeolite containing platinum metal and at least one promoter metal selected from iron, cobalt, titanium and europium, wherein said catalyst has a platinum to promoter metal mole ratio of less than 10:1. A method of producing a dehydrocyclisation catalyst as claimed in claim 1, comprising the steps of: (a) forming an aqueous solution of alkali metal hydroxide, aluminum hydroxide, and a ferric salt; (b) combining said solution with an aqueous solution of silica to form a thickening gel in a mother liquor; (c) heating said thickening gel to form a type L zeolite; (d) cooling said gel containing said type L zeolite; (e) decanting the mother liquor from said gel; (f) filtering said type L zeolite from said gel; (g) washing the filtered type L zeolite; (h) drying said washed type L zeolite; (i) adding platinum to the dried type L zeolite in an amount sufficient to provide a platinum to promoter metal mole ratio of less than 10:1 in the resulting catalyst; (j) drying said catalyst; and (k) calcining the dried catalyst. A method according to claim 2, wherein in step (a), the alkali metal hydroxide is potassium hydroxide, and the ferric salt is ferric nitrate; in step (g), the filtered type L zeolite is washed so that the pH of the wash is about 10.5; and in step (i), the platinum is added to the dried type L zeolite by pore fill impregnation. A method according to claim 2 wherein, in step (i), the platinum is added to the dried type L zeolite by pore fill impregnation with an aqueous solution of either Pt(NH 3 ) 4 (NO 3 ) 2 or Pt(NH 3 ) 4 Cl 2 . A method according to claim 2, 3 or 4, wherein: in step (c), said thickening gel is heated in an autoclave at about 302°F (150°C) for about 72 hours to form a type L zeolite; in step (g), said filtered type L zeolite is washed three times in a ten-fold excess of water so that the pH of the wash is about 10.5; in step (j), the catalyst is dried at about 250°F (121°C) for 16 hours; and in step (k), the dried catalyst is calcined at about 500°F (260°C) for three hours.

Inventors: LEWIS ROBERT T, LONG JOHN J, SANTILLI DONALD S, LEWIS, ROBERT T., LONG, JOHN J., SANTILLI, DONALD S.
Applicants: CHEVRON RES & TECH, CHEVRON RESEARCH AND TECHNOLOGY COMPANY
Application year: 1986
Main classification: B01J29
IPC codes: B01J29, C10G35