LAMINATED PRODUCT

Abstract: Disclosed is a laminated product, which comprises a layer of a polycyanoaryl ether containing 80 mole % or more of the recurring unit represented by the formula (I): and a layer of a fibrous reinforcing material laminated on one another. The laminated product of this invention is excellent in heat resistance, mechanical strength, solent resistance, flame retardancy, moldability and therefore useful as the materials for electronic and electric instruments as well as mechanical parts.

Description: Laminated product BACKGROUND OF THE INVENTION This invention relates to a novel laminated product, more particularly to a laminated product excellent in heat resistance, mechanical strength, solvent resistance, flame retardancy and molding workability. As the material for electronic and electrical instruments or mechanical parts, laminated products obtained by impregnating and curing a thermosetting resin into a cloth or a mat comprising glass fibers or carbon fibers have been well known in the art. However, in production of the above laminated products, it will take a long time for heat treatment for curing of a thermosetting resin, which is disadvantageous in industrial application. Also, in the manufacturing steps, a solvent is required to be used to bring about worsening of the working environment, and besides the step for recovery of the solvent employed is also required. In order to cancel the problems of thermosetting resins as described above, it has been proposed to use a thermoplastic resin as the constituent material of a laminated product in place of thermosetting resins. However, of thermoplastic resins, for example, a crosslinked polyethylene is inferior in heat resistance, a polytetrafluoroethylene is inferior in molding workability, and a polyphenyleneoxide is unsatisfactory in heat resistance and chemical resistance, thus possessing respective drawbacks, and therefore they were unsuitable as the constituent resin of a laminated product in the field of uses wherein heat resistance and solvent resistance are demanded. SUMMARY OF THE INVENTION An object of this invention is to cancel the above problems and provide a laminated product excellent in heat resistance, mechanical strength, solvent resistance, flame retardancy and molding workability. The laminated product of this invention comprises a layer of a polycyanoaryl ether having 80 mole * or more of the recurring unit represented by the formula: EMI2.1 wherein Ar represents any one of EMI2.2 EMI2.3 and a layer of a fibrous reinforcing material laminated on one another. DESCRIPTION OF THE PREFERRED EMBODIMENTS First, the polycyanoaryl ether which is a component of the laminated product in this invention contains 80 mole % or more of the recurring unit represented by the above formula (I). If the content of the recurring unit represented by the formula (I) is less than 80 mole %, the laminated product obtained will be lowered in heat resistance and mechanical strength. Also, the polycyanoaryl ether to be used in this invention may be a copolymer containing 20 mole % or less of at least one recurring unit represented by the formula (II) shown below, in addition to 80 mole % or more of the recurring unit represented by the formula (I): EMI3.1 wherein Ar' represents a divalent aryl group, with the proviso that Ar in the formula (I) and Ar' do not have the same meaning at the same time. Ar' in the formula (II) may include: EMI3.2 EMI4.1 If the copolymer component of the recurring unit represented by the formula (II) is contained in excess of 20 mole %, the laminated product obtained will be lowered in heat resistance. The polycyanoaryl ether may suitably be one having a number-average molecular weight calculated on polystyrene within the range of from 20,000 to 90,000 as measured by high temperature gel permeation chromatography at 135 0C in a solution of 70 mg/dl in N-methylpyrrolidone as the solvent. If the number-average molecular weight is less than 20,000, the polymer obtained lacks mechanical strength and heat resistance, while the number-average molecular weight over 90,000 will make it difficult to form a composite with the fibrous reinforcing material as hereinafter described Preferably, the number average molecular weight is 25,000 to 70,000. The polycyanoaryl ether may be prepared as follows. For example, dihalogenobenzonitrile and an alkali metal salt of a divalent phenol of either one of: EMI4.2 may be dissolved in a solvent such as N-methylpyrrolidone, sulforane, etc. to carry out the reaction at a temperature within the range of from 150 to 300 C, preferably from 160 to 250 OC, followed by treatment with water or an alcohol. When a copolymer of polycyanoaryl ether is to be prepared, two or more kinds of divalent phenol may be employed. The amount of the above polycyanoaryl ether formulated in preparation of the laminated product is generally 20 to 85 % by weight. If the formulated amount is less than 20 % by weight, the polycyanoaryl ether cannot be sufficiently dispersed among the fibrous reinforcing materials, while an amount over 85 % by weight will make heat resistance insufficient. Next, the fibrous reinforcing material which is the other constituent of the laminated product may be any of those conventionally known, as exemplified by glass fibers, carbon fibers, aromatic polyamide fibers, etc. In carrying out lamination, chopped strand mat, continuous long fiber mat, woven fabric or knitted fabric of these fibrous reinforcing materials may be used, or alternatively a combination of these may also be used. The amount of the fibrous reinforcing material formulated may generally be 15 to 80 % by weight, preferably 20 to 70 % by weight, and the mechanical strength of the laminated product will be lowered if the formulated amount falls outside of this range. Next, as the method for preparation of the laminated product, there may be employed: (1) the method in which powder or pellets of a polycyanoaryl ether are sprayed uniformly on a mat or a fabric of the above fibrous reinforcing material and compression molded; (2) the method in which a sheet is formed by extrusion molding or compression molding from the pellets of a polycyanoaryl ether, and this sheet of the polycyanoaryl ether and a mat or fabric of the above fibrous reinforcing material are laminated and compression molded; (3) the method in which the above methods (1) and (2) are suitably combined, etc.; but it is possible to employ any known method if it can laminate the polycyanoaryl ether and the fibrous reinforcing material. In either case of (1) and (2), known additives such as antioxidants, thermal stabilizers, crystal nucleation agents, UV-ray absorbers, fillers, etc. may be added to the polycyanoaryl ether without any inconvenience. Also, in the above methods (1) and (2), during preparation of sheets, pellets or powder of polycyanoaryl ether, it is convenient for improvement of heat resistance and mechanical strength to incorporate short fibers such as of carbon fibers, glass fibers and aromatic polyamide fibers, glass beads, mica, potassium titanate, talc, asbestos, etc. in an amount of 30 % by weight or less. The laminated product of this invention produced according to the method as described above may have a structure or thickness, which may be determined depending on uses and not particularly limited. For example, there may be included a laminated product having a three-layer structure in which said polycyanoaryl ether is laminated on the surface and the back of the inner layer comprising said fibrous reinforcing material, a laminated product of a multi-layer structure in which the layers of polycyanoaryl ether and the layers of fibrous reinforcing material are alternately laminated in a large number, or a two-layer laminated product as its minimum unit. This invention is described in more detail by referring to the following Examples. Example 1 (1) Preparation of polycyanoaryl ether In an autoclave of 5-liter inner volume, 137.6 g (1.25 mole) of hydroquinone, 215 g (1.25 mole) of 2,6-dichlorobenzonitrile, 207 g (1.5 mole) of potassium carbonate, 2.5 liters of sulforane and 1.5 liters of toluene were charged and allowed to react in argon stream at 160 0" for 1.5 hours, and then at 200 OC for 1.5 hours. After completion of the reaction, a large amount of water was added to obtain powder of a polycyanoaryl ether. The powder obtained was further washed with hot water and methanol, followed by drying. As a result, the yield of the polymer was found to be 260 g (yield: 100 %), the polymer had a number average molecular weight of 44,000 and the content of the recurring unit represented by the following formula was 100 mole %: EMI7.1 As for the thermal properties of this polymer, it had a glass transition temperature (Tg) of 180 OC, a melting point (Tm) of 340 OC and a thermal decomposition initiating temperature (Td) of 520 OC (in air). (2) Preparation of laminated product After the the powder of polycyanoaryl ether obtained in above (1) was dispersed uniformly in a flat plate mold of 50 mm x 50 mm, a carbon fiber mat (trade name: Toreca mat B0030, produced by Toray K.K.) was covered over the powder, followed further by uniform dispersion of the polycyanoaryl ether powder on said mat. The formulated proportion of the polycyanoaryl ether was set at 80 % by weight and that of the carbon fiber mat at 20 % by weight. subsequently, the mold was closed and, under pressurization of 10 kg/cm2 -G, press molding was carried out at 390 for 5 minutes, and thereafter the mold was transferred into a cooling press, in which it was maintained at 240 OC for 5 minutes to obtain a laminated product with a thickness of 1 mm. For the laminated product obtained, mechanical properties of tensile strength, elongation, tensile modulus, flexural strength and flexural modulus and heat distortion temperature were measured. Also, when the solvent resistance of the laminated product was examined, it was found to be insouble in respective solvents of acetone, toluene, chloroform and methylene chloride. Also, as for flame retardant property, when the laminated product was subjected to the flame of a lighter for 10 seconds and thereafter the flame was moved away, the fire was extinguished soon and no melt dripping was observed. Example 2 For the polycyanoaryl ether, 2,6-dichlorobenzonitrile and 4,41-biphenol were used as the starting materials. A laminated product was prepared in the same manner as in Example 1 except for using the polycyanoaryl ether having 100 mole % of the recurring unit of the following formula: EMI9.1 a number-average molecular weight of 40,000 and thermal properties of Tg of 220 OC, Tm of 360 OC and Td of 540 C, and measurements were also conducted similarly. The results of solvent resistance and flame retandancy were found to be the same as in Example 1. Example 3 For the polycyanoaryl ether, 2,6-dichlorobenzonitrile and 2,7-dihydroxynaphthalene were used as the starting materials. A laminated product was prepared in the same manner as in Example 1 except for using the polycyanoaryl ether having 100 mole % of the recurring unit of the following formula: EMI9.2 a number-average molecular weight of 35,000 and thermal properties of Tg of 215 OC, Tm of 345 OC and Td of 500 OC (in air), and measurements were alsd conducted similarly. The results of solvent resistance and flame retandancy were found to be the same as in Example 1. Example 4 A polycyanoaryl ether was prepared from the reaction between 2,6-dichlorobenzonitrile and a mixture of hydroquinone and 4,4'-biphenol. A laminated product was prepared in the same manner as in Example 1 except for using the thus obtained polycyanoaryl ether copolymer having 80 mole z of the recurring unit of the following formula: EMI10.1 and 20 mole 96 of the recurring unit of the following formula: EMI10.2 a number-average molecular weight of 42,000 and thermal properties of Tg of 190 OC, Tm of 345 C and Td of 525 OC (in air), and measurements were also conducted similarly. The results of solvent resistance and flame retardancy were found to be the same as in Example 1. Example 5 As the fibrous reinforcing material, the carbon fiber mat in Example 1 was replaced with a glass long fiber mat (trade name: CSM-M9600, produced by Asahi Fiber Glass Co.) and, following otherwise the same procedure as in Example 1, a laminated product was prepared and subjected to the same measurements. The results of solvent resistance and flame retandancy were found to be the same as in Example 1. Example 6 A laminated product was prepared in the same manner as in Example 1 except for using as the polycyanoaryl ether a composition prepared by formulating carbon fibers with an average fiber length of 3 mm into the polycyanoaryl ether prepared in Example 1 to a proportion of 10 % by weight based on the whole laminated product, followed by melting and kneading, and the measurements were also conducted similarly. The results of solvent resistance and flame retandancy were found to be the same as in Example 1. Comparative example A laminated product was prepared in the same manner as in Example 1 except for using as the resin component in the laminated product pellets of a polyether ether ketone (trade name: Victorex PEEK, produced by Imperial Chemical Industry Co.) in place of the polycyanoaryl ether, and the same measurements were conducted. The results of measurements are summarized in Table. Table Tensile Elongation Tensile Flexural Flexural Heat strength modulus strength modulus distortion (kg/mmê) (%) (kg/mmê) (kg/mmê) (kg/mmê) temperature ( C) Example 1 33 3 620 36 1210 290 2 35 4 610 29 1100 295 3 49 3 840 46 1370 290 4 35 3 610 31 1250 290 5 32 3 620 33 1110 285 6 38 3 680 40 1350 310 Comparative example 21 3 530 25 1000 300 As is apparent from the Examples of this invention as described above, the laminated product of this invention has heat resistance comparable to that of the laminated product by use of the polyether ether ketone which has been known to be most excellent in heat resistance, and yet more excellent in mechanical strength than that product. As described above, the laminated product of this invention is excellent in heat resistance, mechanical strength, solvent resistance, flame retardancy, moldability and therefore useful as the materials for electronic and electric instruments as well as mechanical parts.

Claims: Claims: 1. A laminated product, which comprises a layer of a polycyanoaryl ether containing 80 mole % or more of the recurring unit represented by the formula (I): EMI14.1 wherein Ar represents any one of EMI14.2 EMI14.3 and a layer of a fibrous reinforcing material laminated on one another. 2. The laminated product according to Claim 1, wherein said laminated product is a three-layer laminated product wherein the layer of said polycyanoaryl ether is laminated on the surface and the back of the inner layer comprising-said fibrous reinforcing material. 3. The laminated product according to Claim 1, wherein said polycyanoaryl ether is contained in an amount of 20 to 85 % by weight and said fibrous reinforcing material in an amount of 15 to 80 % by weight, respectively. 4. The laminated product according to Claim 1, wherein said polycyanoaryl ether is a copolymer containing 80 mole % or more of the recurring unit represented by the formula (I) and 20 mole t or less of at least one recurring unit represented by the formula (it): EMI15.1 wherein Ar' is a divalent aryl group, with the proviso that Ar in the formula (I) and Ar' do not have the same meaning at the same time. 5. The laminated product according to Claim 1, wherein Ar' in the formula {II) represents EMI15.2 6. The laminated product according to Claim 1, wherein said polycyanoaryl ether has the number-average molecular weight of from 20,000 to 90,000.

Inventors: MATSUO, SHIGERU, MURAKAMI, TOMOYOSHI
Applicants: IDEMITSU KOSAN COMPANY LIMITED
Application year: 1986
Main classification: B32B27
IPC codes: C08G65, C08J5, B32B27