PALLADIUM AND PALLADIUM ALLOY COMPOSITE ELECTRODEPOSITS AND METHOD FOR THEIR PRODUCTION

Abstract: Methods for increasing the ductility and reducing the porosity and cracking tendency of a palladium or palladium-­ silver electrodeposit which comprises providing an underlayer of a palladium/nickel or palladium/cobalt alloy electrodeposit. Also dual layer composite electroplated deposits and their use in electrical contacts or connectors.

Description: This invention relates to a method for the production of composite electroplated palladium or palladium alloys. More particularly the invention relates to a method of electrodepositing a first layer of palladium/nickel or palladium/cobalt onto a suitable substrate followed by the electrodeposition of a second layer of palladium or palladium/silver to form the composite alloy. Palladium and palladium alloys have been traditionally used as contact surfaces for electrical contacts and connectors. Primarily, these alloys have been used in the form of wrought alloys or clad inlays as a replacement for gold in such applications. In recent years, many of electrical contacts and connectors have been seeking methods to electroplate palladium or palladium alloys since, in many applications, electroplating would be more economical. Many electrical contacts are manufactured by first electroplating a precious metal deposit in the form of a narrow band or stripe onto a wider strip or surface area of basis metal using high speed, reel-to-reel plating equipment. The electoplated strip is then stamped and formed into a contact with the precious metal electrodeposit located at the exact point where contact is to be made with the mating part. The electrodeposit on this formed part must be tightly adherent, sound, crack-free, and porosity- free, even after the stamping and forming operations. In order for an electrodeposit to withstand such operations, it must have sufficient ductility, good adhesion to the base metal, and freedom from porosity in the electroplated condition. Cracking of the electrodeposits cannot be tolerated in the final product. The electrodeposit should have sufficient ductility to withstand the stresses of stamping and forming without producing further cracks, pores or peeling from the substrate. U.S. Patent No. 4,269,671 discloses a method for electrodepositing a 60% by weight palladium 40% by weight silver alloy from a highly acidic solution containing a large amount of chloride ion. While the alloy obtained is a sound deposit, the plating solution is highly corrosive and causes severe displacement reactions to take place between the plating solution and the basis metal to be plated. These basis metals generally indude copper, nickel or their alloys. This type of high chloride plating solution for palladium/silver alloys is well known in the art as evidenced by Canadian Patent 440,591. U.S. Patent No. 4,269,671 discloses that the copper or nickel basis metals can be protected from the highly corrosive nature of such high chloride plating baths by first coating the basis metal with a thin layer of a precious metal. The precious metals suggested are silver and soft gold with the latter being preferred. U.S. Patent No. 4,463,060 describes a permanently solderable palladium/nickel electrodeposit of a thickness of about 0.1 to 1.5 micrometers having about 46 to 82 atomic percent palladium, balance nickel. This layer is covered by an extremely thin (i.e., about 20 angstroms) second layer of almost pure palladium. The second layer of palladium is formed not by electroplating, but by dipping the first layer into a solution of sulfuric or hydrochloric acid. This combination is described as forming a permanently solderable palladium/nickel electrodeposit. The invention relates to a method for preparing a plated substrate for electrical contacts having at least two layers of palladium or palladium alloys, the first layer consisting of at least 1.27 × 10⁶ cm (0.5 microinches) of an electroplated palladium/nickel or palladium/cobalt alloy which contains between 50 and 95 weight% palladium and which is electroplated onto a substrate from an electroplating solution containing a soluble palladium ion, and the second layer consisting of at least 5.08 × 10⁻⁶ cm (2 microinches) of an electrodeposited palladium or palladium/silver alloy which comprises between 40 and 80 weight% palladium and which is electroplated onto the first layer. The metal substrate as mentioned above comprises usually copper, nickel or one of their alloys. The above-mentioned first layer is sufficient in thickness to increase the ductility and reduce the porosity and tendency for cracking in the elektrodeposit.The invention also relates to a method for reducing corrosion of a copper, nickel or copper/nickel basis metal substrate during electroplating of palladium/siler alloys from an acidic, high chloride electroplating bath which comprises electroplating a sufficient amount of a first layer of a palladium/nickel or palladium/cobalt alloy upon the substrate prior to electroplating the palladium/silver alloy. In this embodiment, a preferred thickness for the palladium/nickel or palladium/cobalt layer is at least about 25.4 × 10⁻⁶ cm (10 microinches). It has surprisingly been found that a thin undercoating of a palladium/nickel or palladium/cobalt alloy, preferably containing about 20-95 most preferably about 60-80% by palladium, is capable of substantially improving the ductility and reducing the porosity characteristics of the overall electrodeposit. The preferred commercial thickness of the composite is generally from about 50.8 × 10⁻⁶ cm to 152.4 × 10⁻⁶ cm (20 to 60 microinches). When plating such relatively thin deposits onto copper, nickel or their alloys, it is very difficult to obtain ductile and porosity-free electrodeposits even if the basis metal is first coated with a thin layer of gold, silver, or pure palladium. When a palladium/nickel or palladium/cobalt alloy is used as a thin undercoating, however, its combination deposit with pure palladium or palladium/silver alloys shows significant improvements in ductility and reduction of cracking and porosity. A preferred palladium/nickel alloy plating bath is one which contains the following: Ammonium chloride is used as a complexing agent to maintain the metals in solution. Other suitable complexing agents include any solution soluble ammonium salt or compound. The addition agent is an organic compound or salt of an organic compound which imparts brightness and other desirable metallurgical characteristics to the deposit. Suitable addition agents include: sodium vinyl sulfonate, saccharin, sodium salts of benzene or naphthalene sulfonic acids, nicotinic acid, nicotinamide, and quaternized pyridinium compounds, with the latter being preferred. The most preferred palladium-nickel or palladium-cobalt alloy electrodeposits contain 75% palladium and 25% nickel or cobalt by weight, although any deposit containing about 50 to 95 weight percent palladium, balance nickel or cobalt, can be used. The pH of the bath is adjusted to the desired range of about 7-9 with ammonium hydroxide or any other base or basic component. To obtain a palladium/cobalt alloy, the same bath as for palladium/nickel can be used except that slightly higher amounts (i.e., about 5-25 g/l) of cobalt metal are substituted for the nickel metal. Also, the pH for these palladium/cobalt baths may be as low as about 6. When the second layer is pure palladium, it can be obtained from any prior art palladium electroplating solution, providing that such solution is capable of producing a sound, crack-free deposit. Preferred palladium plating baths fall generally within the following formula: Suitable addition agents include those listed above for palladium/nickel or palladium-cobalt electroplating. Also, suitable conductivity salts include any bath soluble organic or inorganic compound such as chloride, phosphate, pyrophosphate or like substituents capable of increasing electrical conductivity of the plating bath. When palladium/silver is deposited as the second layer, the electroplating bath must be capable of producing a sound electrodeposit with the most preferred alloy being 60% palladium, 40% silver by weight. Such a deposit can be obtained from the bath described in U.S. Patent No. 4,269,671 or Canadian Patent No. 440,591. Since the baths of these patents are highly corrosive, the palladium/nickel or palladium/cobalt layer must have a thickness of at least about 25.4 × 10⁻⁶ cm (10 microinches) before the palladium/silver alloy is electrodeposited to prevent corrosion of the basis metal substrate during the electroplating of palladium/silver. Acid palladium/silver electroplating baths are described in U.S. Patent Nos. 4,478,692 and 4,465,563. These patents describe chloride-free electroplating baths containing strong acids for depositing sound palladium/silver alloys suitable for this invention. Other palladium/silver plating baths have been described by Medina in U.S. Patent 3,053,741 which claims non-porous deposits from plating baths based upon the ammoniacal nitrate solution of palladium and silver at a pH of 7.5-11. Other alkaline palladian/silver electrolytes capable of producing sound, crack-free and porosity-free electrodeposits of palladium/silver alloys are described in the assignee's co-pending application, Serial No. 742,258, filed June 7, 1985, now abandoned. Generally, such palladium/silver alloys have a palladium content of between about 20 and 95 weight percent palladium, balance silver. Since the cost of high palladium content alloys is relatively expensive, the usual practice is to use less than 80 weight percent palladium. As mentioned above, the most preferred palladium/silver alloys are those containing between 40 and 80 weight percent palladium, balance silver, and specifically 60 weight percent palladium, 40 weight percent silver. To the extent that these patents disclose such suitable baths and deposition processes, their content is expressly incorporated by reference herein. The thickness of the palladium/nickel or palladium/cobalt undercoating would vary from about 1.27 to 127 × 10⁻⁶ cm (0.5 to 50 microinches) or more depending upon the bath and alloy selected for the second layer. A preferred thickness range is about 12.7 to 25.4 × 10⁻⁶ cm (5 to 10 microinches). When the high chloride acidic plating electrolytes for palladium/silver are used, the thickness of the first layer should be at least about 25.4 to 50.8 × 10⁻⁶ cm (10 to 20 microinches). The thickness of the second layer is that which is sufficient to provide the nesessary properties for the intended application. Typically, at least 5.08 × 10⁻⁶ cm (2 microinches) is utilized, and preferably between about 12.7 × 10⁻⁶ and 254 × 10⁻⁶ cm (5 and 100 microinches). There is no upper limit for the thickness of the second layer, although it is unusual to have more than about 635 × 10⁻⁶ cm (250 microinches) due to economic factors. Typically, the deposit thickness of the composite ranges from about 50.8 × 10⁻⁶ to 152.4 × 10⁻⁶ cm (20 to 60 microinches), since this thickness range is generally specified by the electrical contacts industry. EXAMPLES The scope of the invention is further described in connection with the following examples which are set forth for the sole purpose of illustrating the preferred embodiments of the invention and which are not to be construed as limiting the scope of the invention in any manner. Example 1 . (Prior Art) 76.2 × 10⁻⁶ cm (30 microinches) of pure palladium was electroplated onto a copper strip using conventional electroplating procedures. The electrolyte used contained the following: palladian metal (as palladian tetraamino dichloride) 10 grams/liter ammonium chloride 50 grams/liter quaternized pyridine 1 gram/liter pH 7.5 temperature 48,9°C(120°F) current density 160.5 A/min² (15 ASF) After plating, the strip was tested for porosity using the conventional electrographic porosity test. Another sample of strip was subjected to a bend test commonly used in the industry, described by J. Edwards, Trans. Inst. Met. Fin. Vol. 35, 1958. In this test, the electroplated strip is bent around a logarithmic former, and the deposit is examined for cracks and porosity. Results showed some porosity before the bend test, but considerably increased porosity and cracking after the bend test. Example 2 . A copper strip was first plated with 5 microinches of a 70% palladium/30% nickel alloy followed by 63.5 × 10⁻⁶ cm (25 microinches) of the pure palladium deposit obtained by the electroplating procedure of Example 1. The palladium-nickel electrolyte was as follows: The combined thickness of the resultant electrodeposit was the same as in Example 1. Results showed slight porosity before the bend test, but this example showed a significant improvement in both porosity and cracking after the bend test compared to results of Example 1. Example 3 . (Prior Art) A 60% palladium/ 40% silver alloy was obtained from an electroplating solutions described in U.S. Patent 4,478,692 in accordance with the following: A copper strip was prepared for plating using conventional procedures, then plated with about 12.7 × 10⁻⁶ cm (5 microinches) silver from a conventional silver cyanide plating solution, followed by 63.5 × 10⁻⁶ cm (25 microinches) of palladium/silver alloy from the above electrolyte. A porosity test before bending showed some porosity, however, after the bend test, the porosity increased dramatically and substantial cracking of the deposit was observed. Example 4 . (Prior Art) Example 3 was repeated, however, this time a 12.7 × 10⁻⁶ cm (5 microinch) gold undercoat was used in place of silver. The test results obtained for this example were essentially the same as those obtained in Example 3. Example 5 . Example 3 was repeated, however, this time a 12.7 × 10⁻⁶ cm (5 microinch) undercoat of a 70% palladium/ 30% nickel alloy was first plated onto the copper strip. This was followed by the palladium/silver deposit to a thickness of about 63.5 × 10⁻⁶ cm (25 microinches). The porosity test showed slight porosity before the bend test, but the deposit of this example showed a significant improvement in both porosity and cracking after the bend test as compared with results of Examples 3 and 4. Example 6 . (comparison) Example 1 was repeated, however, this time a 12.7 × 10⁻⁶ cm (5 microinches) undercoat of pure palladium was used from a palladium tetramine dichloride bath followed by the palladium/silver electrodeposit of Example 3 to a total thickness of 63.5 × 10⁻⁶ cm (25 microinches). Porosity and cracking characteristics of this composite electrodeposit were not as good as those of Example 5, but were improved over the results of Examples 3 and 4. Example 7 . A copper strip was first plated with 12.7 × 10⁻⁶ cm (5 microinches) of a 90% palladium/ 10% cobalt alloy followed by 63.5 × 10⁻⁶ cm (25 microinches) of the pure palladium deposit obtained by the electroplating procedure of Example 1. The palladium/cobalt electrolyte was as follows: The combined thickness of the resultant electrodeposit was the same as in Example 1. Results showed slight porosity before the bend test, but this example showed a significant improvement in both porosity and cracking after the bend test compared to results of Example 1. While it is apparent that the invention herein disclosed is well calculated to fulfill the objects above stated, it will be appreciated that numerous modifications and embodiments may be devised by those skilled in the art, and it is intended that the appended claims cover all such modifications and embodiments as fall within the true spirit and scope of the present invention.

Claims: 1. A method for preparing a plated substrate for electrical contacts having at least two layers of palladium or palladium alloys, the first layer consisting of at least 1.27 × 10⁻⁶ cm (0.5 microinches) of an electroplated palladium/nickel or palladium/cobalt alloy which contains between 50 and 95 weight% palladium and which is electroplated onto a substrate from an electroplating solution containing a soluble palladium ion, and the second layer consisting of at least 5.08 × 10⁻⁶ cm (2 microinches) of an electrodeposited palladium or palladium/silver alloy which comprises between 40 and 80 weight% palladium and which is electroplated onto the first layer. 2. The method of claim 1 wherein the substrate comprises copper, nickel or copper nickel alloy. 3. The method of claims 1 and 2 wherein the first layer is palladium/nickel. 4. The method of claims 1 and 2 wherein the first layer is palladium/cobalt. 5. The method of claims 1, 2, 3 and 4 wherein the second layer is palladium/silver in a thickness of between 63.5 × 10⁻⁶ cm, and 152.4 × 10⁻⁶ cm (25 and 60 microinches). 6. The method of claims 1, 2, 3 and 4, wherein the first layer has a thickness of at least 12.7 × 10⁻⁶ cm (5 microinches) and the second layer has a thickness of at least 12.7 × 10⁻⁶ cm (5 microinches). 7. The method of any of the preceding claims, wherein the plated substrate forms an electrical contact.

Inventors: MARTIN, JAMES L., NOVEL, TOBEN, MICHAEL P.
Applicants: LEARONAL, INC.
Application year: 1986
Main classification: C25D3
IPC codes: C25D3, C25D7, H01H11, H01H1, C25D5