CLEANING SYSTEM FOR CONTACT LENSES AND PROCESS FOR CLEANING THE SAME

Abstract: A contact lens cleaning system, process and kit includ­ es an aqueous chlorite solution and a solid component in­ cluding an agent for accelerating decomposion of chlorite and an oxygen consumption agent. The chlorite decompos­ es to form free oxygen which removes impurities from a lens to be cleaned. The oxygen consuming agent prevents excess free oxygen from attacking the lens after the impuri­ ties have been removed.

Description: Title of the Invention: CLEANING SYSTEM FOR CONTACT LENSES AND PROCESS FOR CLEANING THE SAME The present invention relates to a cleaning agent for soft and hard contact lenses (hereinafter referred to as CL) and a process for using the same. It has been known to clean CL by removing oils, fats and dirts from the surface of CL with a cleaning solution containing, for example, an acid, a chlorite and a surfactant (Japanese Patent Laid-Open Nos. 18616/1983 and 18617/1983). It has also been known that substances such as proteins¯which cannot be removed with a surfactant or the like are removed by decomposing them with protease. However, the cleaning solutions used heretofore are those of a two-pack type. In using these solutions, a troublesome operation is required of the users, namely, the two liquids must be measured separately and then placed in a cleaning vessel. Further, containers of a large volume are necessitated for the two liquids. This is inconvenient for a traveler making a trip for a long period of time. After intensive investigations made for the purpose of overcoming the defects of the conventional cleaning solutions for contact lenses and processes for cleaning them, the inventors have developed a cleaning agent of a two-pack type in which one pack comprises an easily measurable solid and a process for cleaning contact lenses. The cleaning agent can be kept compact as a whole and used easily and conveniently for cleaning contact lenses. A first embodiment of this invention is directed to a cleaning system for contact lenses, comprising: (a) a chlorite salt in aqueous solution, capable of decomposition to form free oxygen for removing impurities from a contact lens. (b) a solid component, comprising: an agent for accelerating the decomposition of the chlorite to form free oxygen, selected from the group consisting of acids, organic acid salts, ion exchange resins, reducing agents and sugars; and oxygen-consuming agent for consuming excess free oxygen from the decomposition of the chlorite after impurities have been removed from a contact lens being cleaned. -A second embodiment of the invention provides a process for cleaning contact lenses, comprising placing a lens to be cleaned, and a cleaning system comprising: (a) a chlorite salt in aqueous solution, capable of decomposition to form free oxygen for removing impurities from a contact lens. (b) a solid component, comprising: an agent for accelerating the decomposition of the chlorite to form free oxygen, selected from the group consisting of acids, organic acid salts, ion exchange resins, reducing agents and sugars; and oxygen-consuming agent for consuming excess free oxygen from the decomposition of the chlorite after impurities have been removed from a contact lens being cleaned in a vessel. A third embodiment of the invention provides a cleaning system for contact lenses, comprising: (a) a chlorite salt in aqueous solution, capable of decomposition to form free oxygen for removing impurities from a contact lens; (b) a solid component, comprising: an acid for accelerating decomposition of the chlorite to form free oxygen; a sugar for consuming excess free oxygen from the decomposition from the chlorite after impurities are removed from the lens; and a decomposition inhibitor for the acid. A further aspect of the invention is directed to a process for cleaning contact lenses, comprising placing a lens to be cleaned and a cleaning system comprising (a) a chlorite salt in aqueous solution, capable of decomposition to form free oxygen for removing impurities from a contact lens; (b) a solid component, comprising: an acid for accelerating decomposition of the chlorite to form free oxygen; a sugar for consuming excess free oxygen from the decomposition from the chlorite after impurities are removed from the lens; and a decomposition inhibitor for the acid in a vessel. Yet another aspect of the invention provides a contact lens cleaning kit, comprising: (a) a container with a chlorite salt in aqueous solution, capable of decomposition to form free oxygen for removing impurities from a contact lens; and (b) a plurality of packages containing pre-measured amounts of: an agent for accelerating the decomposition of the chlorite to form free oxygen, selected from the group consisting of acids, organic acid salts, ion exchange resins, reducing agents and sugars; and an oxygen-consuming agent for consuming excess free oxygen from the decomposition of the chlorite after impurities have been removed from a contact lens being cleaned. Figure 1 is a chart showing UV spectra of a lens, wherein the dotted line shows the UV spectrum of the stained lens before cleaning and the solid line shows that of the lens treated with the cleaning agent of the present invention. Examples of the chlorites contained in the liquid A include sodium and potassium chlorites. Among them, sodium chlorite is particularly preferred, since it effectively decomposes excretions from the living body which are deposited on the contact lenses with minimal effect on the lenses. Specifically, it is believed that the chlorite ion decomposes to release free oxygen, which attacks the impurities on the lens. The concentration of the chlorite in the cleaning solution is in the range of about 0.0001 to 5% by weight, preferably 0.0005 to 0.5. For storage stability, a pH in the range of about 6-8 is preferred for the chlorite solution. In the present invention, the component B should be in a solid form so as to facilitate the handling thereof. The form of the solid component B is not particularly limited and it may be in the form of tablet, powder or pellet (including granule). Among them, pellet or powder is particularly effective. It is preferred to pack a batch of the component in a bag. The component B must comprise at least one member selected from the group consisting of acids, organic acid salts, ion exchange resins, reducing agents and sugars. These agents act as a catalyst for accelerating the decomposition of the chlorite contained in the component A. The agents may function by releasing hydrogen ion, which leads to accelerated decomposition of the chlorite to from free oxygen. The sugar may be any one having the above-mentioned function and it may be selected from monosaccharides and polysaccharides. A typical example of the sugar is glucose. The acid may be any one as long as it provides the function required in the present invention. Preferred examples of the acids include organic acids such as adipic, stearic, sebacic, oxalic, itaconic, edetic, ascorbic; and inorganic acids such as hydrochloric and sulfuric acids. It is more preferred to use tartaric and/or citric acid. Acids which are normally liquid can be used in a solid form through absorption on a substrate such as alumina or encapsulation in a suitable acid resistant polymer. In the case of absorption, the chlorite solution itself will release the acid, while some mechanical force may be necessary in the case of encapsulation. The ion exchange resin is preferably a cation exchange resin. The ion exchange resin functions as the acid does, and has the advantage of being in solid form, and thus easily removed after the cleaning is finished. The organic acid salt is at least one of sodium hydrogentartrate and sodium dihydrogencitrate. Polyfunctional acid salts are preferred because of the removable acid functions in such salts, which provide the salts with the same properties as an acid with respect to the present invention. Also, such salts often are conveniently available in solid form. The reducing agent is preferably sodium hydrogensulfite. These compounds accelerate the decomposition of the chlorite. The pH value of the cleaning solution may be selected suitably so far as the purpose of the present invention is not damaged. It is, for example, in the range of 2 to 8, preferably 3 to 6. The cleaning agent of the present invention also may contain known additives which do not interfere with the invention, such as: sodium monohydrogenphosphate, urea, boric acid, sodium borate, and edetic acid salts as well as surfactants. These function as preservatives, protein denaturants, etc. The component B may comprise at least one sugar, an acid and a decomposition inhibitor for the acid. The combination of the sugar with the acid acts as a catalyst for accelerating the decomposition of the chlorite. The sugar may be any one having the above-mentioned function and it may be selected from among monosaccharides and polysaccharides. Examples of the sugars include glucose, sucrose and fructose. Among them, glucose is particularly preferred. The sugar releases hydrogen ions under the influence of the acid, thus contributing to the composition of the chlorite. Furthermore, the sugar function to consume excess free oxygen remaining after the decomposition of impurities to that the excess free oxygen is not available to deteriorate the lens. This latter function of the sugar can be accomplished using other materials so long as the free oxygen attacks the lens impurities before being consumed. An example of a suitable substitute material is a polymer such as polyvinylpyrrolidone. Such a polymer should not be used in the event the lens itself includes the polymer. The acid may be any one so far as it has the function intended in the present invention. Preferred examples of the acids include organic acids such as tartaric, citric, lactic, malic and gluconic acids; and inorganic acids such as hydrochloric and sulfuric acids. It is more preferred to use tartaric and/or citric acid. A preferred combination of the sugar with the acid comprises citric acid and glucose, since it exhibits an excellent cleaning effect without damaging the physical properties of the lenses. They may be used either alone or in the form of a mixture of two or more of them. The sugar alone will provide some acceleration of the chlorite decomposition, but the efficiency is increased by also using acid. The present invention is characterized in that a decomposition inhibitor for the acid is contained in the component B. When a solid mixture of the acid and the sugar is stored for a long period of time, the acid frequently is decomposed, which lowers the cleaning power unfavorably. Though this defect can be prevented by granulating the acid and the sugar separately from each other, this technique is troublesome. According to the present invention, this defect can be overcome by using the decomposition inhibitor. Though any compound having such an effect can be used as said inhibitor, polyvinyl compounds, particularly polyvinylpyrrolidone, are preferred. The molecular weight of the polyvinylpyrrolidone is not particularly limited and it ranges from several thousands to several millions. The cleaning agent of the present invention can be used for cleaning conventional contact lenses to exhibit not only a protein-removing effect but also a decolorizing effect within a short treatment time. A preferred embodiment of the process for cleaning contact lenses with the cleaning agent of the present invention is as follows: a given amount (for example, a batch packed in a bag) of the solid component B is placed in a vessel together with the lenses and then a given amount (for example, corresponding to a scale mark of the cleaning vessel) of the liquid A is added thereto to clean the lenses. The temperature of the cleaning solution may be selected suitably. More particularly, it may be room temperature or from around a boiling point to 1200C. The lower the temperature, the longer the treatment time and, on the contrary, the higher the former, the shorter the latter. The contact lenses thus treated are preferably left to cool to room temperature in the cleaning solution -and then washed with water. If necessary, any remaining chlorite is decomposed with sodium thiosulfate or sodium hydrogensulfite. The lenses are then immersed in a physiological saline and used again. The contact lenses which can be treated by the above-mentioned cleaning process include, for example, highly hydrous, soft contact lenses comprising mainly polyvinylpyrrolidone and lowly hydrous soft contact lenses comprising mainly polyhydroxyethyl methacrylate. Further, hard contact lenses having a polysiloxane bond, oxygen-permeable contact lenses having both siloxane and urethane bonds, etc. may also be treated as a matter of course. Thus, the kinds of the contact lenses which can be treated according to the present invention are not limited. The cleaning agent of the present invention in which one of the components is in solid form has advantages in that it can be weighed easily at the time of the use and it can be stored compact as a whole. The present invention has advantageous effects in that at provides a convenient cleaning agent and procesC; tor the users. Another effect of the invention is that the cleaning agent can be stored for a long period of time and that the cleaning can be effected in a consistent manner. The cleaning agent can be sold in a kit form containing a number of pre-measured units of the solid component (preferably individual package), a container with chlorite solution and instructions for use. Optionally, the kit can include a cleaning container for lenses, marked to indicate the appropriate level for chlorite solution addition. Example 1 12g of polyvinylpyrrolidone having an average molecular weight of about 360,000 was added to a mixture of 80g of D-(+)-glucose and 8g of L-(+)-tartaric acid. 5g of pure water was added thereto and the mixture was stirred well and granulated. The granules were dried at 600C for 1 h and then heat-treated at 400C for 80 h. The tartaric acid content was measured according to ion chromatography before and after the heat treatment to reveal that they were 7.78% and 7.89%, respectively. The difference between them was thus insignificant. This fact suggests that the product has a good storage stability. 4ml of 100ppm aqueous sodium chlorite solution was added to 0.lg of the granules. A used, stained soft contact lens was immersed therein and boiled at 1000C for 15min. Then, it was left to cool to room temperature. The lens was washed with running pure water for 5 min and its UV spectrum was examined to evaluate the cleaning effects. The results are shown in Table 1. Satisfactory cleaning effects were obtained. The accompanying figure is a chart showing UV spectra of the lens in which the dotted line shows the UV spectrum of the lens before cleaning and the solid line shows that after cleaning. The peak in the dotted line shows the presence of contaminant. Example 2 Cleaning solutions Nos. 2 to 4 as shown in Table 1 were prepared by granulation and pulverization effected in the same manner as in Example 1. A used, stained contact lens was immersed in each solution and boiled at 1000C for 15 min or left to stand at room temperature for 16 h. The lens was washed with running water for 5 min and the UV spectrum thereof was examined to evaluate the cleaning effects. The results are shown in Table 1. The cleaning of the effect which the degree of staining of the lens placed on the colorimetric dish was ranked visually as follows: Rank Degree of staining of the lens 4 The staining and discoloration were serious 3 The staining and discoloration were moderate 2 The staining and discoloration were slight 1 The staining and discoloration were negligible Table I Cleaning solution No. 1 2 3 4 (Composition of the solution) Component A Sodium chlorite 0.01% 0.01% 0.01% 0.01% Pure water 99.99 99.99 99.99 99.99 Amount of component A 4g 4g 4g 4g Component B Glucose 80% 80% 80% Fructose - - - 100% Tartaric acid 8% 8% - Citric acid - - 20% Polyvinylpyrrolidone 12% 12% - (Average molecular weight 360,000 25,00 of polyvinylpyrrolidone) 0.1g 0.1g 0.1g 0.2g Amount of component B (Treatment conditions) Temperature 100 C room temp. 100 C 100 C Time 15min 16h 15min 15min (Cleaning effect) 1 2 1 2 Example 3 12g of polyvinylpyrrolidone having an average molecular weaight of about 25,000 was added to a mixture of 80g of D-(+)-glucose and 8g of L-(+)-tartaric acid and the mixture was stirred thoroughly. 4ml of 100ppm sodium chlorite solution was added to 0.lg of the obtained powder. Further, lml of an aqueous urca solution prepared according to a formulation shown below was added to the mixture. A used, stained contact lens was immersed therein and left to stand at room temperature for 16 h. Thereafter, the lens was taken out and washed with running pure water for Smin. The cleaning effect was determined by a visual method wherein the lens placed in a colorimetric dish was observed before and after the cleaning. The results are shown in Table 2. Excellent cleaning effects were obtained. Aqueous urea solution: polyoxyethylene sorbitan monolaurate 0.3% polyoxyethylene/polyoxypropylene 0.3t sodium carboxymethylcellulose 0.02% potassium sorbate 0.0058 urea 1.0% pure water the balance Table 2 Cleaning solution No. 5 6 7 8 9 (Composition of the solution) Component A Sodium chlorite (%) 0.01 0.01 0.01 0.01 0.01 Pure water (%) 99.99 99.99 99.99 99.99 99.99 Amount of component A (g) 4 4 4 4 4 Component B Glucose (%) 80 80 80 - 80 Tartaric acid (%) 8 8 20 20 Polyvinylpyrrolidone (%) 12 12 - - (Average molecular weight of 2.5 2.5 polyvinylpyrrolidone (x10,000) Amount of component B (g) 0.01 0.1 0.01 0.01 Component C Polyoxyethylene sorbitan - 0.3 - 0.6 0.3 monolaurate (%) Polyoxyethylene/polyoxypropylene - 0.3 - 0.6 0.3 block polymer Sodium carboxymethylcellulose (%) - 0.02 - 0.04 0.02 Potassium sorbate (%) - 0.05 - 0.01 0.005 Urea (%) - 1.0 2.0 - 1.0 Pure water (%) - 98.375 98. 98.75 98.375 Amount of component A (g) - 1 1 1 1 Table 2 (continued) Cleaning solution No. 5 6 7 8 9 (Composition of the solution) (Treatment conditions) Temperature room room room room room temp temp temp temp temp Time (h) 16 16 16 16 16 (Cleaning effect) Before cleaning 4 4 4 4 4 After cleaning 3 2 2 2 3 Example 4 Cleaning solutions Nos. 7 to 9 as shown in Table 2 were prepared by using the same aqueous urea solution as in Example 3 as it was or after modifying tlle composition thereof. A used, stained contact lens was immersed in each solution and left to stand at room temperatur or 16 h. The lens was washed with running water for Smin and the cleaning effect was evaluated using the colorimetric dish. The results are shown in Table 2. The cleaning effect was improved remarkably by the addition of the aqueous urea solution. Comparative Example 1 A granular component B was prepared in the same manner as in Example 1 except that the polyvinylpyrrolidone used as the decomposition inhibitor for the sugar was not added. More particularly, 98g of D-(+)-glucose was mixed with 2g of L-(+)-tartaric acid. 17g of pure water was added to the mixture and the obtained mixture was granulated. The granules were dried at 600C for 1 h and then heat-treated at 400C for 80 h. The tartaric acid content of the heat-treated granules was analyzed according to ion chromatography to reveal that it was reduced by about 16% from 1.97 to 1.65% by the heat treatment. The product had thus a poor stability. The decomposition products of the acid may not be safe to humans. When the obtained cleaning agent was used for cleaning a contact lens, only a poor cleaning effect was obtained. Example 5 0.003 g of crystalline citric acid was added to 3 g of 0.01% aqueous sodium chlorite solution. Then, a used, stained soft contact lens was immersed therein and boiled at 1000C for 30 min. Then, it was left to cool to room temperature. The lens was washed with running pure water for 5 min and its UV spectrum was examined to evaluate the cleaning effects. The results are shown No.10 in Table 3. Satisfactory cleaning effects were obtained. Example 6 Cleaning solution Nos. 11 to 15 as shown in Table 3 were prepared in the same manner as in Example 5. A used, stained contact lens was immersed in each solution and boiled at 1000C for 10 to 30 min or left to stand at room temperature for 16 h. The lens was washed with running pure water for 5 min and the W spectrum thereof was examined to evaluate the cleaning effects. The results are shown in Table 3. Table 3 Cleaning solution No. 10 11 12 13 14 15 (Composition of the solution) Component A Sodium chlorite (%) 0.01 0.01 0.02 0.02 0.02 0.02 Pure water 99.99 99.99 99.98 99.98 99.98 99.98 Amount of component A (g) 3 3 3 3 3 3 Component B Citric acid (%) 100 Tartaric acid (%) 100 L-Aspartic acid (%) 100 Oxalic acid (%) 100 Ascorbic acid (%) 100 Itaconic acid (%) 100 Amount of component B (g) 0.003 0.03 0.01 0.01 0.01 0.01 (Treatment conditions) Temperature ( C) 100 room temp. 100 100 100 100 Time ( C) 30 (16 hr) 10 10 10 10 (Cleaning effect) 1 1 2 1 2 1 Example 7 Cleaning solution Nos. 16 to 19 as shown in Table 4 were prepared by using a granulated organic acid salt, reducing agent or reducing sugar in the same manner as in Example 5. A used, stained contact lens was immersed therein and boiled at 1000C for 10 to 60 min. Thereafter, the lens was washed with running pure water for 5 min. The cleaning effect was determined from the UV spectrum of the treated lens. The results are shown in Table 4. Table 4 Cleaning Solution No. 16 17 19 20 (Composition of the solution) Component A Sodium chlorite (%) 0.02 0.02 0.02 0.02 Pure water (%) 99.98 99.98 99.98 99.98 Amount of component A (g) 3 3 3 3 Component B Sodium hydrogentartrate 100 (%) Sodium dihydrogencitrate 100 (%) Glucose (%) 100 Sodium hydrogensulfite 100 Amount of component B (g) 0.01 0.01 0.01 0.01 (Treatment conditions) Temperature ( C) 100 100 100 100 Time (min) 10 10 10 10 (Cleaning effect) 2 2 1 1 Example 8 0.01 g of Amberlyst &num;5 (an ion exchange resin of Rohm & Haas) was added to 3 g of 0.02 to 0.05% aqueous sodium chlorite solution. Cleaning solutions No. 20 or 23 as shown in Table 5 was added thereto. A used, stained lens was immersed therein. After boiling at 1000C for 10 min or leaving to stand at room temperature for 16 h, the lens was taken out and washed in running pure water. The UV spectrum of the lens was examined before and after the treatment to evaluate the cleaning effect. The results are shown in Table 5. Table 5 Cleaning Solution No. 20 21 (Composition of the solution) Component A Sodium chlorite (%) 0.02 0.05 Pure water (%) 99.98 99.95 Amount of component A (g) 3 3 Component B Amberlyst- 15 100 100 Amount of component B (g) 0.01 0.01 (Treatment conditions) Temperature ( C) 100 room temp. Time 10 min 16 hr (Cleaning effect) # 2 1 ¯¯¯¯

Claims: What is Claimed is: 1. A cleaning system for contact lenses, comprising: (a) a chlorite salt in aqueous solution, capable of decomposition to form free oxygen for removing impurities from a contact lens. (b) a solid component, comprising: an agent for accelerating the decomposition of the chlorite lo form free oxygen, selected from the group consisting of acids, organic acid salts, ion exchange resins, reducing agents and sugars; and oxygen-consuming agent for consuming excess free oxygen from the decomposition of the chlorite after impurities have been removed from a contact lens being cleaned. 2. The system of claim 1, wherein the solid component is in the form of a pelmet or power. 3. The system of claim 1, wherein the agent for accelerating the decomposition is at least one organic acid. 4. The system of claim 1, wherein the agent for accelerating the decomposition is a cation exchange resin. 5. The system of claim 1, wherein the agent for accelerating the decomposition is at least one member selected from the group consisting of adipic, stearic, sebacic, oxalic, itaconic, edetic, ascorbic, alyinic, aspartic, sorbic, tartaric and citric acids. 6. The cleaning agent of claim 1, wherein the agent for accelerating the decomposition is at least one member selected from the group consisting of sodium hydrogentartrate and sodium dihydrogencitrate. 7. The system of claim 1, wherein the agent for accelerating the decomposition is sodium hydrogensulfite. 8. The system of claim 1, wherein the agent for accelerating the decomposition of glucose. 9. A process for cleaning contact lenses, comprising placing a lens to be cleaned, and a cleaning system comprising: (a) a chlorite salt in aqueous solution, capable of decomposition to form free oxygen for removing impurities from a contact lens. (b) a solid component, comprising: an agent for accelerating the decomposition of the chlorite to form free oxygen, selected from the group consisting of acids, organic acid salts, ion exchange resins, reducing agents and sugars; and oxygen-consuming agent for consuming excess free oxygen from the decomposition of the chlorite after impurities have been removed from a contact lens being cleaned in a vessel. 10. A cleaning system for contact lenses, comprising: (a) a chlorite salt in aqueous solution, capable of decomposition to form free oxygen for removing impurities from a contact lens; (b) a solid component, comprising: an acid for accelerating decomposition of the chlorite to form free oxygen; a sugar for consuming excess free oxygen from the decomposition from the chlorite after impurities are removed from the lens; and a decomposition inhibitor for the acid. 11. The system of claim 10, wherein the solid component is in the form of a pellet or powder. 12. The system of claim 10, wherein the sugar is at least one member selected from the group consisting of glucose, sucrose and fructose. 13. The system of claim 10, wherein the acid is at least one member selected from the group consisting of adipic, stearic, sebacic, oxalic, itaconic, edetic, ascorbic, alginic, aspartic, sorbic, tartaric and citric acids. 14. The system of claim 10, wherein the decomposition inhibitor is polyvinylpyrrolidone. 15. A process for cleaning contact lenses, comprising placing a lens to be cleaned and a cleaning system comprising (a) a chlorite salt in aqueous solution, capable of decomposition to form free oxygen for removing impurities from a contact lens; (b) a solid component, comprising: an acid for accelerating decomposition of the chlorite to form free oxygen; a sugar for consuming excess free oxygen from the decomposition from the chlorite after impurities are removed from the lens; and a decomposition inhibitor for the acid in a vessel. 16. A contact lens cleaning kit, comprising: (a) a container with a chlorite salt in aqueous solution, capable of decomposition to form free oxygen for removing impurities from a contact lens; and (b) a plurality of packages containing pre-measured amounts of: an agent for accelerating the decomposition of the chlorite to form free oxygen, selected from the group consisting of acids, organic acid salts, ion exchange resins, reducing agents and sugars; and an oxygen-consuming agent for consuming excess free oxygen from the decomposition of the chlorite after impurities have been removed from a contact lens being cleaned. 17. The kit of claim 16, wherein the agent for accelerating decomposition is an acid and the consuming-oxygen agent is a sugar. 18. The kit of claim 17, wherein the acid is selected from the group consisting of dipic, stearic, sebacic, oxalic, itaconic, edetic, ascorbic, alginic, aspartic, sorbic, tartaric and citric acids. 19. The kit of claim 17, wherein the sugar is at least one member selected from the group consisting of glucose, sucrose and fructose. 20. The kit of claim 17, wherein the solid component further comprises a decomposition inhibitor for the acid. 21. The kit of claim 20, wherein the decomposition inhibitor is polyvinylpyrrolidone. 22. The kit of claim 21, further comprising a cleaning vessel for accepting a contact lens to be cleaned and instructions for using the kit.

Inventors: JYONO, TERUO, KENJO, HIDEKI
Applicants: TORAY INDUSTRIES, INC.
Application year: 1986
Main classification: C11D7
IPC codes: A61L12, A01N59, C11D3, C11D7