INSTANTANEOUSLY CURABLE COMPOSITION

Abstract: A curable composition comprises (A) a polymer whose molecules have a main chain comprising carbon-carbon bonds and one or more isocyanatocarbonyl groups pendant to the main chain, the content of the isocyanatocarbonyl groups per polymer molecule being from 0.1 to 72.2% by weight, and (B) an active hydrogen atom-containing compound. Various poiymers of the given type, including polymers having pendant isocyanatocar­ bonyl and/or isocyanato groups, are novel.

Description: The present invention relates to an instantaneously curable composition. More particularly, it relates to an instantaneously curable composition useful as a coating composition, an adhesive agent, a molding material or the like, and an isocyanate group-containing polymer to be used as an essential component therein. Throughout the specification, the terms "curable" and "cured" may be taken substantially in the name meanings as the terms "hardenable" and "hardened" or the terms "crosslinkable" or "crosslinked". Further, the term "lower alkyl" is intended to mean alkyl having 1 to 5 carbon atoms, preferably 1 to 3 carbon atoms, more preferably methyl. The term "halogen" is intended to mean chlorine, bromine, iodine and fluorine, inclusively. Among them, preferred are chlorine and bromine, particularly chlorine. The term "inert solvent" may be understood to mean any solvent which does not afford any unfavorable influence on achievement of the purpose as aimed at during the reaction or operation in which the solvent is used. In this invention, a highly reactive isocyanatocarbonyl group and/or a compound or polymer having such isocyanatocarbonyl group are created and/or handled so that, in general, any solvent which has an active hydrogen atom in the molecule or contain any substantial amount of moisture is not usable. Unless otherwise stated, the inert solvent may be chosen, for instance, from aliphatic hydrocarbons (e.g. pentane, hexane, heptane), aromatic hydrocarbons (e.g. benzene, toluene, xylene), alicyclic hydrocarbons (e.g. cyclohexane, methylcyclohexane, decalin), petrolic hydrocarbons (e.g. petroleum ether, petroleum benzin), halogenated hydrocarbons (e.g. carbon tetrachloride, chloroform, 1,2-dichloroethane), ethers (e.g. diethyl ether, diisopropyl ether, anisole, dioxane, tetrahydrofuran), esters (e.g. methyl acetate, ethyl acetate, butyl acetate), ketones (e.g. acetone, methylethylketone, methylisobutylketone, cyclohexanone, acetophenone, isophorone), acetonitrile, dimethylformamide, dimethylsulfoxide, etc. As a curable composition, there is known a polyol-curable polyurethane composition which comprises as the essential components a polyisocyanate and an alkyd resin. This polyol-curable polyurethane composition is based on utilization of the room temperature reactivity between the isocyanate groups in the polyisocynate and the active hydrogen atoms in the alkyd resin. For attainment of prompt curing with such polyol-curable polyurethane composition, a catalyst (e.g. dibutyltin dilaurate) is usually incorporated therein. In the course of the study seeking a curable composition which can attain curing rapidly, it has been found that a polymer having an isocyanatocarbonyl group (-CO-NCO) as a pendant shows such a high reactivity as more than 10⁴ times that of the corresponding polymer having an isocyanato group (-NCO). It has also been found that the high reactivity of said isocyanatocarbonyl group-containing polymer can be controlled by blocking the isocyanatocarbonyl group therein. Such polymer having a blocked isocyanatocarbonyl group (-CO-NHCO-B wherein B is a blocking group such as the residue of an alkanol excluding a hydrogen atom therefrom) can be readily convered into a non-blocked isocyanatocarbonyl group-containing polymer at a relatively low temperature in comparison with the conversion of the corresponding blocked isocyanato group-containing polymer into a non-blocked isocyanato group-containing polymer. Based on these findings, there has now been provided an instantaneously curable composition comprising a polymer having an isocyanatocarbonyl group and a compound having an active hydrogen as the essential components. The instantaneous curability can be approptiately controlled by blocking a portion or all of the isocyanatocarbonyl groups in the polymer. Said polymer having an isocyanatocarbonyl group in a free or blocked state has been provided by thin invention for the first time. Accordingly, a basic object of the present invention is to provide an instantaneously curable composition, which is useful as a coating composition, an adhesive agent, a molding material, etc. Another object of the invention is to provide a curable composition of which the curing rate is appropriately controlled. A further object of the invention is to provide a polymer having a free or blocked isocyanatocarbonyl group as a pendant, which is used as an essential component in a curable composition. A still further object of the invention is to provide a process for preparing a free or blocked isocyanatocarbonyl group-containing polymer. These and other objects will be apparent to those skilled in the art from the foregoing and subsequent descriptions in this specification. The instantaneous curable composition of the invention comprises as the essential components (A) a polymer having a main chain comprising carbon-carbon bonds and an isocyanatocarbonyl group as a pendant to the main chain, the content of the isocyanatocarbonyl groups present in the molecule of the polymer being from 0.1 to 72.2 % by weight, and (B) an active hydrogen atom-containing compound which has one or more, preferably at least two, active hydrogen atoms in the molecule. The proportion of the isocyanatocarbonyl group-containing polymer (A) and the active hydrogen atom-containing compound (B) may be such that the equivalent ratio of the isocyanatocarbonyl group in the former and the active hydrogen atom in the latter is 1 : 0.1 - 100, preferably 1 : 0.5 - 5. The isocyanatocarbonyl group-containing polymer (A) as one of the essential components in the curable composition of the invention may comprise units of an isocyanatocarbonyl group-containing monomer, optionally with units of one or more of other polymerizable monomers. For the use in the composition of the invention, it should have a main chain comprising carbon-carbon bonds and contain isocyanatocarbonyl groups in an amount of 0.1 to 72.2 % by weight in the molecule. It is preferred to have a molecular weight of 1,000 to several hundred thousands, especially of 1,000 to 100,000. The isocyanatocarbonyl group-containing polymer (A) can be manufactured by various procedures. One typical procedure is polymerization of an alkenoyl isocyanate of the formula: wherein R is a hydrogen atom or a lower alkyl group (e.g. methyl, ethyl, propyl), optionally blocked at the isocyanatocarbonyl group, or an alkenyloxazolinedione hydrohalide of the formula; wherein X is a halogen atom (e.g. chlorine, bromine) and R is as defined above, optionally with one or more of other polymerizable monomers having no active hydrogen atom. The alkenoyl isocyanate (I) can be produced by reacting an alkenylamide of the formula: wherein R is as defined above and an oxalyl halide of the formula: (COX)₂ (IV) wherein X is as defined above, optionally followed by dehydrohalogenation of the by-produced haloalkanoyl isocyanate of the formula: wherein R and X are each as defined above. More advantageously, the alkenoyl isocyanate (I) can be produced by reacting the alkenylamide (III) with the oxalyl halide (IV) to produce the alkenyloxazolinedione hydrohalide (II) and subjecting the latter to decomposition. For production of the alkenyloxazolinedione hydrohalide (II), it is preferred that the oxalyl halide (IV) is first charged into a reactor and then the alkenylamide (III) is portionwise added thereto, whereby the reaction proceeds. The molar ratio of the alkenylamide (III) and the oxalyl halide (IV) may be usually about 1 : 1 - 3, preferably about 1 : 1 - 1.5. The use of an inert solvent as the reaction medium is not essential but is usually preferred. Thus, either one or both of the alkenylamide (III) and the oxalyl halide (IV) may be previously dissolved or suspended therein. The reaction temperature is normally higher than -50°C and lower than the decomposition temperature of the alkenyloxazolinedione hydrohalide (II), preferably from about 0 to 40°C. From the industrial viewpoint, the temperature around room temperature or under ice cooling is favorable. For separation of the alkenyloxazolinedione hydrohalide (II) from the reaction mixture, there may be adopted any per so conventional separation procedure such as filtration or distillation under reduced pressure. Addition of seed crystals of the alkenyloxazolinedione hydrohalide (II) to the reaction mixture may be sometimes favorable to accelerate the precipitation of the alkenyloxazolinedione hydrohalide (II). However, separation of the alkenyloxazolinedione hydrohalide (II) from the reaction mixture is not necessarily required. The alkenyloxazolinedione hydrohalide (II) is then subjected to decomposition under the condition affording the alkenoyl isocyanate (I) predominantly or suppressing by-production of the haloalkanoyl isocyanate (V). One typical example of such condition is to carry out the decomposition under an ordinary pressure (atmospheric or autogenic). Namely, the alkenyloxazolinedione hydrohalide (II) as charged in a reactor is heated under an ordinary pressure until the decomposition proceeds sufficiently. When a reaction medium is used, the heat decomposition can take place at such a low temperature as about 40°C. In the absence of any reaction medium, heating up to the decomposition temperature of the 2-alkenyloxazolinedione hydrohalide (e.g. about 102 to 103°C in case of 2-isopropenyloxazoline-4,5-dione hydrochloride) is required. As the reaction medium, there may be used an inert solvent. Another example of the condition is to carry out the decomposition in the presence of a hydrogen halide-eliminating agent. Namely, decomposition of the alkenyloxazoline hydrohalide (II) in the presence of a hydrogen halide-eliminating agent at a temperature of -50 to200°C, preferably from 0 to 150°C under an ordinary or reduced pressure gives predominantly the alkenoyl isocyanate (I). As the hydrogen halide-eliminating agent such as not having an active hydrogen atom or as being reacted with a hydrogen halide not to produe an active hydrogen atom is favorably used. Amines which are the most popular hydrogen halide-eliminating agents are hardly usable in the process of this invention. Specific examples of the preferred hydrogen halide-eliminating agent are metal complex compounds (e.g. (Ph₃P)₂Ru(CO)₃, (Ph₃P)₃Pt), metal halides (e.g. lithium chloride, titanium tetrachloride, aluminum chloride, cuprous chloride), synthetic zeolite (e.g. molecular sieve, microporous glass), etc. The hydrogen halide-eliminating agent is used normally in an amount of about 0.1 to 100 mol, preferably of about 0.1 to 10 mol to 1 mol of the alkenyloxazolinedione hydrohalide (II). Any reaction medium is not necessarily required to use. When used, an inert solvent may be employed. Another example of the conditition is to carry out the decomposition in the presence of a liquid medium having a dielectric constant of not more than 4. Such liquid medium may be constituted with one or more of inert solvents chosen from aliphatic or alicyclic hydrocarbons (e.g. pentane, hexane, heptane, octane, decalin, cyclohexane), aromatic hydrocarbons (e.g. benzene, toluene, xylene, naphthalene), ethers (e.g. propyl ether, butyl ether, dioxane, isopropyl ether), esters, halogenated hydrocarbons (e.g. carbon tetrachloride), etc. A dielectric constant of not more than 4 may be attained by the use of a single solvent or by the use of two or more solvents in combination. The decomposition may be carried out by keeping the alkenyloxazolinedione hydrohalide (II) in a liquid medium of not more than 4 in dielectric constant at a temperature higher than the decomposition temperature of the alkenyloxazolinedione (II), usually from about 40 to 150°C, preferably from about 60 to 120°C, whereby the alkenoyl isocyanate (I) is predominantly produced. Recovery of the alkenoyl isocyanate (I) from the reaction mixture may be accomplished by a per se conventional separation procedure such as distillation under atmospheric or reduced pressure. The alkenoyl isocyanate (I) blocked at the isocyanatocarbonyl group may be produced, for instance, by reacting the alkenoyl isocyanate (I) with a blocking agent in an inert solvent at a temperature of -20 to 100°C, preferably at room temperature or under cooling with ice. Examples of the blocking agent are aliphatic alcohols (e.g. methanol, ethanol, chloroethanol, propanol, butanol, pentanol, hexanol, heptanol, octanol, nonanol, 3,3,5-trimethylhexanol, 2-ethylhexanol, decanol), aromatic ring-containing alcohols (e.g. phenylcarbinol, methylphenylcarbinol), ether bond-containing alcohols (e.g. ethylene glycol monobutylether), phenolic compounds (e.g. phenol, cresol, xylenol, nitrophenol, chlorophenol, ethylphenol, t-butylphenol, nonylphenol), monofunctional polyethylenes or polypropylene oxides (e.g. Carbowax 550), active methylene compounds (e.g. acetylacetone, diethyl malonate), lactams (e.g. propiolactam, butyrolactam, valerolactam, caprolactam), N-hydroxyimides (e.g. N-hydroxyphthalimide, N-hydroxyglutarimide, N-hydroxysuccinimide), oximes (e.g. methylethylketone oxime, acetone oxime, cyclohexanone oxime), imidazoles (e.g. imidazole), triazoles (e.g. 1,2,3-benzotriazole), amines (e.g. dicyclohexylamine), etc. In any of the above reactions and the post-treatments, a small amount of a polymerization inhibitor may be incorporated into the reaction system or the reaction mixture for prevention of the unnecessary polymerization on the double bond. Examples of the polymerization inhibitor are hydroquinone, p-methoxyphenol, 2,6-di-t-butyl-4-methylphenol, 4-t-butylcatechol, bisdihydroxybenzylbenzene, 2,2'-methylenebis(6-t-butyl-3-methylphenol), 4,4'-butylidenebis(6-t-butyl-3-methylphenol), 4,4'-thiobis(6-t-butyl-3-methylphenol), p-nitrosophenol, diisopropylxanthogenesulfide, N-nitrosophenylhydroxylamine ammonium salt, 1,1-diphenyl-2-picrylhydrazyl (free radical), dithiobenzoyl sulfide, p,p'-ditolyl trisulfide, p,p'-ditolyl tetrasulfide, dibenzyl tetrasulfide and tetraethylthiuram disulfide. The alkenoyl isocyanates (I) are, in general, stable liquids at room temperature and therefore can be handled with ease. They are soluble in various organic solvents and can be used in their solution form. Polymerisation of the alkenoyl isocyanate (I), optionally blocked at the isocyanatocarbonyl group, or the alkenoyloxazolinedione (II) optionally with one or more other polymerisable monomers having no active hydrogen atom, may be carried out by a per se conventional procedure for solution polymerisation. As the other polymerisable monomers, examples are monoolefinic or diolefinic hydrocarbons (e.g. styrene, alpha-methylstyrene, alpha-ethylstyrene, 2-methylpropene-1, 2-methylbutene-1, 2-methylpentene-1, 2,3-dimethylbutene-1, 2,3-dimethylpentene-1, 2,4-dimethylpentene-1, 2,3,3-trimethylheptene-1, 2,3-dimethylhexene-1, 2,4-dimethylhexene-1, 2,5-dimethylhexene-1, 2-methyl-3-ethylpentene-1, 2,3,3-trimethylpentene-1, 2,3,4-trimethylpentene-1, 2-methyloctene-1, 2,6-dimethylheptene-1, 2,6-dimethyloctene-1, 2,3-dimethyldecene-1, 2-methylnonadecene-1, ethylene, propylene, butylene, amylene, hexylene, butadiene-1,3, isoprene), monoolefinic or diolefinic halogenated hydrocarbons (e.g. alpha-chlorostyrene, alpha-bromostyrene, 2,5-dichlorostyrene, 2,5-dibromostyrene, 2,6-dichlorostyrene, 3,4-dichlorostyrene, o-, m- or p-fluorostyrene, 2,6-difluorostyrene, 3-fluoro-4-chlorostyrene, 3-chloro-4-fluorostyrene, 2,4,5-trichlorostyrene, dichloromonofluorostyrene, 2-chloropropene, 2-chlorobutene, 2-chloropentene, 2-chlorohexene, 2-chloroheptene, 2-bromobutene, 2-bromoheptene, 2-fluorohexene, 2-fluorobutene, 2-iodopropene, 2-iodopentene, 4-bromoheptene, 4-chloroheptene, 4-fluoroheptene, cis- and trans-1,2-dichloroethylene, 1,2-dibromoethylene, 1,2-difluoroethylene, 1,2-diiodoethylene, vinyl chloride, vinylidene chloride, bromoethylene, fluoroethylene, iodoethylene, 1,1-dibromoethylene, 1,1-difluoroethylene, 1,1-diiodoethylene, 1,1,2-trifluoroethylene, chlorobutadiene), carboxylic alkenyl esters (e.g. vinyl acetates, vinyl propionate, vinyl butyrate, vinyl isobutyrate, vinyl valerate, vinyl caproate, vinyl enantate, vinyl benzoate, vinyl p-chlorobenzoate, vinyl o-chlorobenzoate, vinyl p-methoxybenzoate, vinyl p-ethoxybenzoate, isopropenyl acetate, isopropenyl propionate, isopropenyl butyrate, isopropenyl isobutyrate, isopropenyl valerate, isopropenyl caproate, isopropenyl enanteate, isopropenyl benzoate, isopropenyl p-chlorobenzoate, isopropenyl o-chlorobenzoate, isopropenyl o-bromobenzoate, isopropenyl m-chlorobenzoate, isopropenyl alpha-chloroacetate, isopropenyl alpha-bromopropionate, vinyl alpha-chloroacetate, vinyl alpha-bromoacetate, vinyl alpha-chloropropionate, vinyl alpha-bromopropionate, vinyl alpha-iodopropionate, vinyl alpha-chlorobutyrate, vinyl alpha-chlorovalerate, vinyl alpha-bromovalerate), alkyl alkenoates (e.g. methyl acrylate, ethyl acrylate, n-propyl acrylate, isopropyl acrylate, n-butyl acrylate, sec-butyl acrylate, t-butyl acrylate, isobutyl acrylate, n-hexyl acrylate, 2-ethylhexyl acrylate, 3,5,5-trimethylhexyl acrylate, n-octyl acrylate, lauryl acrylate, tridecyl acrylate, stearyl acrylate, methyl methacrylate, ethyl methacrylate, n-propyl methacrylate, isopropyl methacrylate, n-butyl methacrylate, sec-butyl methacrylate, t-butyl methacrylate, isobutyl methacrylate, amyl methacrylate, n-hexyl methacrylate, 2-ethylhexyl methacrylate, n-octyl methacrylate, lauryl methacrylate, tridecyl methacrylate, stearyl methacrylate, methyl crotonate), alkyl substituted alkenoates (e.g. methyl alpha-chloroacrylate, methyl alpha-bromoacrylate, methyl alpha-fluoroacrylate, methyl alpha-iodoacrylate, ethyl alpha-chloroacrylate, propyl alpha-chloroacrylate, isopropyl alpha-bromoacrylate, amyl alpha-chloroacrylate, decyl alpha-chloroacrylate, methyl alpha-cyanoacrylate, ethyl alpha-cyanoacrylate, amyl alpha-cyanoacrylate, decyl alpha-cyanoacrylate), allyl or methallyl compounds (e.g. allyl chloride, allyl cyanide, allyl bromide, allyl fluoride, allyl iodide, allyl chlorocarbonate, allyl nitrate, allyl thiocyanate, allyl formate, allyl acetate, allyl propionate, allyl valerate, allyl caproate, allyl 3,5,5-trimethylhexoate, allyl benzoate, allyl acrylate, allyl crotonate, allyl oleate, allyl chloroacetate, allyl trichloroacetate, allyl chloropropionate, allyl chlorovalerate, allyl lactate, allyl pyruvate, allyl aminoacetate, allyl acetoacetate, allyl thioacetate, methallyl chloride, methallyl cyanide, methallyl chlorocarbonate, methallyl nitrate, methallyl thiocyanate, methallyl formate, methallyl acetate, methallyl propionate, methallyl valerate, methallyl caproate, methallyl benzoate, allyl acrylate, allyl crotonate, allyl oleate, methallyl chloroacetate, methallyl trichloroacetate, methallyl chloropropionate, methallyl chlorovalerate, methallyl pyruvate, methallyl acetoacetate, methallyl thioacetate), dialkylaminoalkyl alkanoates (e.g. N,N'-dimethylaminoethyl acrylate, N,N'-dimethylaminoethyl methacrylate), isocyanatoalkyl alkanoates (e.g. isocyanatomethyl acrylate, isocyanatoethyl acrylate, isocyanatomethyl methacrylate, isocyanatoethyl methacrylate), glycidyl acrylate, glycidyl methacrylate, cyclohexyl acrylate, cyclohexyl methacrylate, phenyl acrylate, phenyl methacrylate, benzyl acrylate, benzyl methacrylate, dialkyl unsaturated carboxylates (e.g. dimethyl maleate, diethyl maleate, dimethyl fumarate, diethyl fumarate, dibutyl fumarate), unsaturated nitriles (e.g. acrylonitrile, methacrylonitrile, ethacrylonitrile, 3-octenenitrile, crotonitrile, oleonitrile), etc. A mixture comprising the alkenoyl isocyanate (I), optionally blocked at the isocyanatocarbonyl group, or the alkenyloxazolinedione (II) optionally with one or more of the other polymerizable monomers having no active hydrogen atom in an inert solvent is subjected to polymerization, for instance, at a temperature of 20 to 200°C, preferably of 60 to 150°C, more preferably of 80 to 110°C. The content of the alkenoyl isocyanate (I), optionally blocked at the isocyanatocarbonyl group, or the alkenyloxazolinedione (II) in tea mixture is normally not less than 0.1 % by weight. For instance, an inert solvent and, if desired, a portion of the monomeric components are charged in a reactor, and the temperature is retained at 50 to 140°C, preferably 80 to 110°C. Then, solutions of the monomeric components and of the polymerization initiator are dropwise added thereto in about 0.5 to 5 hours, preferably about 1.5 to 3 hours, optionally followed by aging for 0.5 to 2 hours. Preferably, a polymerization initiator is present in the reaction system. Examples of the polymerization initiator are organic peroxides (e.g. benzoyl peroxide, t-butyl perbenzoate, t-butyl peroxide, cumene hydroperoxide, di-t-butyl peroxide,t-butyl peroctoate), azo compounds (e.g. 2,2'-azobisisobutyronitrile, dimethyl azodiisobutyrate, 2,2'-azobis(2,4-dimethylvaleronitrile), 2,2'-azobis(4-methoxy-2,4-dimethylvaleronitrile), etc. The amount of the polymerization initiator is usually from 0.1 to 10 % by weight, preferably from 0.5 to 5 % by weight, based on the total weight of the monomeric components. When desired, a chain transfer agent may be also present in the reaction system. As the chain transfer agent, there may be used any conventional one having no active hydrogen atom. Specific examples include alpha-methylstyrene dimer. The amount of the chain transfer agent is usually from 5 to 20 % by weight based on the total weight of the monomeric components. When the alkenyl isocyanato (I) is used as the starting monomer, the above polymerization affords the isocyanatocarbonyl group-containing polymer (A) as the direct product, the content of the isocyanatocarbonyl groups being 0.1 to 72.2 % by weight and the molecular weight being about 1,000 to 100,000. When the alkenyl isocyanate (I) is blocked at the isocyanatocarbonyl group, the direct product is the blocked isocyanatocarbonyl group-containing polymer (A'), i.e. the polymer which has a blocked isocyanatocarbonyl group as a pendant, the content of the blocked isocyanatocarbonyl groups being from 0.1 to 99.9 % by weight, and a molecular weight of about 1,000 to 100,000. This blocked isocyanatocarbonyl group-containing polymer can be readily converted into the isocyanatocarbonyl group-containing polymer (A) by application of a per se conventional blocking group-eliminating procedure to the former, e.g. treatment of the former with heat, light, a catalyst or the like. When the alkenyloxazolinedione hydrohalide (II) is employed as the starting monomer, the direct product is a polymer having an oxazolinedione hydrohalide group as an pendant, the content of such groups in the molecule being usually from 0.1 to 83.3 %, especially from 5 to 83.3 %, and having normally a molecular weight of about 1,000 to 100,000, especially of about 1,000 to 50,000. This polymer can be easily converted into the isocyanatocarbonyl group-containing polymer (A) by treatment of the former in substantially the same manner as explained on the conversion of the alkenyloxazolinedione hydrohalide (II) into the alkenoyl isocyanate. For the use of the isocyanatocarbonyl group-containing polymer (A) thus obtained as an essential component in the composition of the invention, it may be used in the form of the reaction mixture containing the same or in its dilute or concentrated form obtainable by diluting the reaction mixture with an inert solvent or concentrating the reaction mixture to evaporate volatile components therefrom. In view of the high reactivity of the isocyanatocarbonyl group, however, care should be always taken to exclude water or moisture in any procedure for production of the isocyanatocarbonyl group-containing polymer (A) as stated above and also on storage of the isocyanatocarbonyl group-containing polymer (A). The other essential component in the curable composition of the invention is the active hydrogen atom-containing compound (B) having one or more, preferably at least two, active hydrogen atoms. Such active hydrogen atom-containing compound (B) may be chosen from a wide scope of compounds having an active hydrogen atom, which may be present in functional groups such as hydroxyl, mercapto, carboxyl, amino, imino and active methylene. Thus, it may be chosen preferably from compounds having two or more of said functional groups in their molecules. Specific examples are resins (e.g. acryl resins, epoxy resins, polyester resins, alkyd resins, polyamide resins, amino resins), polyhydroxy compounds (e.g. ethylene glycol, glycerol, trimethylolpropane, pentaerythritol), alkanolamines (e.g. monoethanolamine, diethanolamine, triethanolamine, tripropanolamine), ammonia, amines (e.g. methylamine, ethylenediamine, hexamethylenediamine), carboxylic acids (e.g. succinic acid, adipic acid, azelaic acid, sebacic acid, phthalic acid, trimellitic acid, fumaric acid, itaconic acid), mercaptans (e.g. ethanedithiol, 2-mercaptoethanol, 2-aminoethanethiol, toluenedithiol), active methylene compounds (e.g. dimethyl malonate, tetracyanopropane, 1,3-cyclohexanedione), etc. As stated above, the reactivity of the isocyanatocarbonyl group in the polymer (A) is extremely higher (i.e. more than 10⁴ times) than that of an isocyanato group in the corresponding polymer. Therefore, curing of the composition of the invention, i.e. the reaction between the isocyanatocarbonyl group in the polymer (A) and the active hydrogen atom in the compound (B), proceeds instantaneously at room temperature to give a cured product. One typical example of the reaction between an icocyanatocarbonyl group-containing polymer and a triol on curing as presently assumed is schematically shown below. The cured product has a bond of -CO-NH-COO- and shows high elasticity and toughness. wherein R is as defined above. When the control of the curing rate of the curable composition of the invention is desired, the isocyanatocarbonyl group-containing polymer (A) therein may be partly or wholly substituted with the blocked isocyanatocarbonyl group-containing polymer (A'). As above stated, the blocked isocyanatocarbonyl group-containing polymer (A') can be produced directly by polymerization of the alkenoyl isocyanate (I) blocked at the isocyanatocarbonyl group. Alternatively, the once-produced isocyanatocarbonyl group-containing polymer (A) may be reacted with a blocking agent in the same manner as explained on the blocking of the alkenoyl isocyanate (I) to give the blocked isocyanatocarbonyl group-containing polymer (A'). The curable composition of the invention may be provided in a single component form or in a two component form depending upon the curing rate. With the blocking degree of the isocyanatocarbonyl groups, the curing rate is varied, and the composition form may be decided thereon. When all the isocyanatocarbonyl groups are free and the curing rate is so high as instantaneous, the curable composition is normally presented in a two component form, i.e. a kit comprising two separate packs, of which one contains the isocyanatocarbonyl group-containing polymer (A) and the other contains the active hydrogen atom-containing compound (B). On the use, they may be mixed together, or one of them is first applied and the other may be applied thereon. When almost all the isocyanatocarbonyl groups are blocked and the curing rate is very small, the curable composition may be presented in a single component form, i.e. a single composition comprising the blocked isocyanatocarbonyl group-containing polymer (A') and the active hydrogen atom-containing compound (B). For convenience on handling, at least one of the blocked isocyanatocarbonyl group-containing polymer (A') and the active hydrogen atom-containing compound (B) may be provided in the form of a solution in an inert solvent. In such case, the concentration of the essential component in the solution may be usally from not less than 0.1 % by weight. Under a special situation, the active hydrogen atom-containing compound (B) in a gaseous or vapor form may be contacted onto the isocyanatocarbonyl group-containing polymer (A) for curing. Examples of such active hydrogen atom-containing compound are water, ammonia, ethanolamine, etc. Depending on the use, the curable composition may optionally comprise conventional additives such as pigments and fillers. These additives may be also incorporated into either one or both of the isocyanatocarbonyl group-containing polymer (A) and the active hydrogen atom-containing compound (B). Any catalyst is usually not required to use, although it may be incorporated if desired. When the composition is used as a coating composition, a liquid or solution containing the active hydrogen atom-containing compound (B) is usually first applied onto a substrate, and during the liquid or solution is still not completely dried, a liquid or solution containing the isocyanatocarbonyl group-containing polymer (A) is applied thereon in the drying atmosphere, optionally followed by drying at room temperature or under heating. When the composition is used as an adhesive agent, a liquid or solution containing the isocyanatocarbonyl group-containing polymer (A) is applied to a substrate, and a liquid or solution containing the active hydrogen atom-containing compound (B) is applied to another substrate. Then, both of the substrates may be joined together, optionally followed by heating. When the composition is used as a molding material, a liquid or solution containing the isocyanatocarbonyl group-containing polymer (A) and a liquid or solution containing the active hydrogen atom-containing compound (B) are combined together in a mold, followed by curing. Alternatively, said combination may be carried out at a low temperature avoiding curing, and then the resultant mixture is admitted into a mold and brought to room temperature for curing. If necessary, heating may be applied on curing. Paticularly when the content of the blocked isocyanatocarbonyl group-containing polymer is great, heating will be desirable or necessary for curing. As stated above, the isocyanatocarbonyl group-containing polymer (A) shows a high reactivity attributed to the isocyanatocarbonyl group. The reactivity of the blocked isocyanatocarbonyl group-containing polymer (A') is somewhat suppressed, but the blocking group can be readily eliminated, for instance, by heating so that the free isocyanatocarbonyl group is recovered and exerts a high reactivity. Therefore, those can be used not only as the essential component in the curable composition of the invention but also as a resinous component in various fields such as coating compositions, adhesive agents, industrial plastics, etc. Practical and presently preferred embodiments of the invention are illustratively shown in the following examples wherein part(s) and % are by weight, unless otherwise indicated. Reference Example 1 Preparation of 2-vinyloxazoline-4,5-dione hydrochloride:- Oxalyl chloride (130 g; 1.02 mol) was charged in a reactor, and a warm solution of acrylamide (71 g; 1.0 mol) in dichloroethane (250 ml) was dropwise added thereto (reaction temperature, 10 to 30°C). After completion of the dropwise addition, the solvent and excess of the oxalyl chloride were removed by distillation under reduced pressure to obtain 2-vinyloxazoline-4,5-dione hydrochloride (161 g) as a yellow oil, Viscosity, 10² Pa.s (100,000 cp). Reference Example 2 Preparation of 2-isopropenyloxazoline-4,5-dione hydrochloride:- A warm solution of methacrylamide (21,25 g) in dichloroethane (90 ml) was dropwise added in 1 hour to oxalyl chloride (34,5 g) kept at room temperature (20°C) while stirring. The resultant mixture was cooled with water to room temperature. The produced 2-isopropenyloxazoline-4,5-dione hydrochloride (37 g) was collected by filtration under suction, washed with hexane and dried under reduced pressure. Decomposition temperature, 102 to 103°C. Reference Example 3 Preparation of methacryloyl isocyanate:- To 2-isopropenyloxazoline-4,5-dione hydrochloride (200 g), o-dichlorobenzene (800 g) was added, and the resultant mixture was heated to 140°C while stirring for about 40 minutes. After cooling with water, the reaction mixture was distilled under reduced pressure to give methacryloyl isocyanate (70.9 g; b.p., 52 to 53°C 5200 Pa (39 mmHg)) as a colorless liquid and alpha-methyl-beta-chloropropionyl isocyanate (48.7 g). Reference Example 4 Preparation of acryloyl isocyanate:- To 2-vinyloxazoline-4,5-dione hydrochloride (100 g), o-dichlorobenzene (400 g) was added, and the resultant mixture was heated at 110 to 120°C while stirring for about 30 minutes. After cooling with ice, the reaction mixture was distilled under reduced pressure to give acryloyl isocyanate (8.9 g; b.p., 82 to 83°C 10⁵ Pa (760 mmHg)) and beta-chloropropionyl isocyanate (56.4 g). Reference Example 5 1) Preparation of 2-isopropenyloxazoline-4,5-dione hydrochloride:- Oxalyl chloride (139.6 g) and o-dichlorobenzene (400 g; dielectric constant, 9.88) were mixed together and cooled to a temperature of 0 to 10°C. Methacrylamide (85.1 g) was portionwise added thereto in 40 minutes, followed by stirring at 35 to 40°C for 2 hours. A small amount of seed crystals of 2-isopropenyloxazoline-4,5-dione hydrochloride was added thereto, and the resultant mixture was allowed to stand whereby 2-isopropenyloxazoline-4,5-dione hydrochloride was crystallized out. 2) Preparation of methacryloyl isocyanate:- To the above mixture comprising crystals of 2-isopropenyloxazoline-4,5-dione hydrochloride, hexane (600 g; dielectric constant, 1.88) was added so that the dielectric constant of the solvent mixture was made to 3.45. Stirring was continued at a temperature of 70 to 75°C for 1.5 hours. Distillation of the reaction mixture gave methacryloyl isocyanate (55.9 g). Reference Example 6 1) Preparation of 2-isopropenyloxazoline-4,5-dione hydrochloride:- Oxalyl chloride (139.6 g; 1.1 mol) and o-dichlorobenzene (400 g; dielectric constant, 9.88) were mixed together and cooled to a temperature of 0 to 10°C. Methacrylamide (85.1 g; 1.0 mol) was portionwise added thereto in 40 minutes. A small amount of seed crystals of 2-isopropenyloxazoline-4,5-dione hydrochloride was added thereto, and the resultant mixture was allowed to stand whereby 2-isopropenyloxazoline-4,5-dione hydrochloride was crystallized out. Hexane (600 g; dielectric constant, 1.88) was added thereto. Precipitated crystals were collected by filtration to obtain 2-isopropenyloxazoline-4,5-dione hydrochloride in a yield of 98.6 %. 2) Preparation of methacryloyl isocyanate:- 2-Isopropenyloxazoline-4,5-dione hydrochloride as obtained above (100 g) was suspended in a mixture of hexane (240 g) and o-dichlorobenzene (160 g), the dielectric constant of the solvent mixture being 3.45. The suspension was heated at a temperature of 70 to 75 C under reflux for 1.5 hours. Distillation of the reaction mixture gave methacryloyl isocyanate (49 g; yield, 89.9 %) and alpha-methyl-beta-chloropropionyl isocyanate (1.4 g; yield, 1.7 %). Reference Example 7 Preparation of an active hydrogen atom-containing compound:- Into a reaction vessel, the materiasl under (a) were charged, and heating under reflux was effected for 1 hour to remove water. The materials under (b) were added thereto at 100°C under nitrogen stream, and the resultant mixture was agaed for 30 minutes. The materials under (c) were dropwise added thereto in 30 minutes, followed by aging at 100°C for 1.5 hours. The reaction mixture comprising the produced active hydrogen atom-containing compound has the following physical properties: viscosity (determined by Gardner bubble viscometer), C; non-volatile content, 45 %; number average molecular weight of resin, 10,720; hydroxyl value of resin (mg number of KOH corresponding to the equivalent of hydroxyl groups in 1 g of the solid component of resin), 75. Example 1 Preparation of an isocyanatocarbonyl group-containing polymer:- Into a reaction vessel, the materials under (a) were charged, and heating under reflux was effected for 1 hour to remove water. The materials under (b) were dropwise added thereto at 100°C in 3 hours under nitrogen stream, and the resultant mixture was aged for 30 minutes. The materials under (c) were dropwise added thereto in 30 minutes, followed by aging at 100°C for 1.5 hours. The reaction mixture comprising the produced isocyanatocarbonyl group-containing polymer has the physical properties as shown in Table 1. Example 2 Preparation of an isocyanatocarbonyl group-containing polymer:- In the same manner as in Example 1 but using the above materials, the operation was carried out. The reaction mixture comprising the produced isocyanatocarbonyl group-containing polymer has the physical properties as shown in Table 1. Example 3 Preparation of an isocyanatocarbonyl group-containing polymer:- In the same manner as in Example 1 but using the above materials, the operation was carried out. The reaction mixture comprising the produced isocyanatocarbonyl group-containing polymer has the physical properties as shown in Table 1. Example 4 Preparation of a isocyanatocarbonyl group-containing polymer:- In the same manner as in Example 1 but using the above materials and adopting a polymerization temperature of 140°C, the operation was carried out. The reaction mixture comprising the produced isocyanatocarbonyl group-containing polymer has the physical properties as shown in Table 1. Example 5 Preparation of an isocyanatocarbonyl group-containing polymer:- In the same manner as in Example 1 but using the above materials, the operation was carried out. The reaction mixture comprising the produced isocyanatocarbonyl group-containing polymer has the physical properties as shown in Table 1. Example 6 Preparation of an isocyanatocarbonyl group-containing polymer:- In the same manner as in Example 1 but using the above materials, the operation was carried out. The reaction mixture comprising the produced isocyanatocarbonyl group-containing polymer has the physical properties as shown in Table 1. Example 7 Preparation of an isocyanatocarbonyl group-containing polymer:- In the same manner as in Example 1 but using the above materials, adopting a polymerization temperature of 110°C and taking 2 hours for dropwise addition of the materials under (b), the operation was carried out. The reaction mixture comprising the produced isocyanatocarbonyl group-containing polymer has the physical properties as shown in Table 1. Example 8 Into a flask, the isocyanatocarbonyl group-containing polymer as obtained in Example 3 (4 parts) and chloroform (6 parts) were charged, and a mixture of trimethylolethane (0.076 part) and tetrahydroquinone (4 parts) was dropwise added thereto in 30 seconds while stirring at room temperature in nitrogen stream, whereby the contents in the flask was hardened immediately. Example 9 In the same manner as in Example 8 but replacing the mixture of trimethylolethane and tetrahydroquinone by a mixture of diethanolamine (0.06 part) and tetrahydroquinone (4 parts), that of 1,6-hexanediol (0.10 part) and tetrahydroquinone (4 parts), that of azelaic acid (0.16 part) and tetrahydroquinone (4 parts), that of N-methyl-1,3-propanediamine (0.05 part) and tetrahydroquinone (4 parts) or that of the active hydrogen atom-containing compound as obtained in Reference Example 7 (2.8 parts) and tetrahydroquione (4 parts), mixing was conducted, whereby the contents in the flask was hardened immediately. Example 10 1) Preparation of a blocked isocyanatocarbonyl group-containing polymer:- Into a reaction vessel, dioxane (20.0 parts) was charged and heated to 80°C. A mixture of dioxane (38.3 parts), 2,6-di-t-butyl-p-cresol-blocked methacryloyl isocyanate (8.5 parts), styrene (9.0 parts) and 2,2'-azobis(2,4-dimethylvaleronitrile) (0.35 part) was dropwise added thereto at 80°C in 3 hours to give the reaction mixture comprising a copolymer of 2,6-di-t-butyl-p-cresol-blocked methacryloyl isocyanate and styrene. Number average molecular weight of resin, 9,900. Non-volatile content, 30 %. 2) Preparation of an isocyanatocarbonyl group-containing polymer:- The reaction mixture comprising the 2,6-di-t-butyl-p-cresol-blocked methacryloyl isocyanate/styrene copolymer as above obtained was heated at 110°C with an infrared heating cell, whereby the blocking group was eliminated and a methacryloyl isocyanate/styrene copolymer was produced. The thus produced methacryloyl isocyanate/styrene copolymer was treated with a mixture of trimethylolethane and tetrahydroquinone in the same manner as in Example 8, whereby instantaneous curing was observed. Example 11 1) Preparation of a blocked isocyanatocarbonyl group-containing polymer:- Into a reaction vessel, dioxane (10.0 parts) and 2,6-di-t-butyl-p-cresol-blocked acryloyl isocyanate (6.0 parts) were charged and heated. A mixture of dioxane (2.0 parts) and 2,2'-azobis(2,4-dimethylvaleronitrile) (0.12 part) was dropwise added thereto to give the reaction mixture comprising a homopolymer of 2,6-di-t-butyl-p-cresol-blocked acryloyl isocyanate. Number average molecular weight of resin, 6,400. Non-volatile content, 33 %. 2) Preparation of an isocyanatocarbonyl group-containing polymer:- The reaction mixture comprising the 2,6-di-t-butyl-p-cresol-blocked acryloyl isocyanate homopolymer as above obtained was heated, whereby the blocking group was eliminated and an acryloyl isocyanate homopolymer was produced. The thus produced acryloyl isocyanate homopolymer was treated with a mixture of trimethylolethane and tetrahydroquinone in the same manner as in Example 8, whereby instantaneous curing was observed. Example 12 Preparation of an isocyanatocarbonyl group-containing polymer: Into a reaction vessel, the materials under (a) were charged and heated to 90°C. The materials under (b) were dropwise added thereto in 2 hours under nitrogen stream, and the resultant mixture was aged for 30 minutes. The materials under (c) were dropwise added thereto in 30 minutes, followed by aging for 2 hours. The reaction mixture comprising the produced isocyanatocarbonyl group-containing polymer has the physical properties as shown in Table 2. Example 13 In the same manner as in Example 12 but using the above materials, the operation was carried out. The reaction mixture comprising the produced isocyanatocarbonyl group-containing polymer has the physical properties as shown in Table 2. Example 14 In the same manner as in Example 12, but using the above materials, the operation was carried out. The reaction mixture comprising the produced isocyanatocarbonyl group-containing polymer has the physical properties as shown in Table 2. Example 15 In the same manner as in Example 12 but using the above materials, the operation was carried out. The reaction mixture comprising the produced isocyanatocarbonyl group-containing polymer has the physical properties as shown in Table 2. Example 16 In the same manner as in Example 12 but using the above materials, the operation was carried out. The reaction mixture comprising the produced isocyanatocarbonyl group-containing polymer has the physical properties as shown in Table 2. To each of the reaction mixtures comprising the isocyanatocarbonyl group-containing polymer as obtained in Examples 12 and 15, dibutyl tin dilaurate was added in an amount of 0.2 % (in terms of the non-volatile component in the reaction mixture). The resulting mixture was applied onto a tin plate by the use of a bar coater to make a coating film having a thickness of 20 microns, followed by allowing to stand at room temperature. The state of the coating film with the time after the application was observed. The results are shown in Table 3 wherein the rubbing test was conducted by rubbing the coated tin plate with xylene-immersed cloth after 20 hours from the application. From the above results, it is understood that the isocyanatocarbonyl group-containing polymers as obtained in Examples 12 and 15 can afford coating films excellent in initial drying property and curability. Example 17 Preparation of an oxazolinedione hydrohalide group-containing polymer:- To 2-isopropenyloxazoline-4,5-dione hydrochloride (20 g), 2,2'-azobis(4-methoxy-2,4-dimethylvaleronitrile) (600 mg) and ethyl acetate (46 g) were added, and the resulting mixture was heated at 38 to 39°C for 7 hours, whereby a homopolymer of 2-isopropenyloxazoline-4,5-dione hydrochloride was produced. Viscosity, A-3 (determined by Gardner bubble viscometer). Non-volatile content, 30 %. Mw, 1800 (determined by gel permeation chromatography). Example 18 Preparation of an oxazolinedione hydrohalide group-containing polymer:- To a mixture of 2-isopropenyloxazoline-4,5-dione hydrochloride (15 g), methyl methacrylate (20 g), n-butyl acrylate (15 g) and ethyl acetate (75 g), 2,2'-azobis(4-methoxy-2,4-dimethylvaleronitrile) (2.5 g) was added, and the resulting mixture was heated at 38 to 39°C for 14 hours, whereby a copolymer of 2-isopropenyloxazoline-4,5-dione hydrochloride with methyl methacrylate and n-butyl acrylate was produced. Viscosity, A-2 (determined by Gardner bubble viscometer). Mw, 4500 (determined by gel permeation chromatography). Example 19 Preparation of an oxazolinedione hydrohalide group-containing polymer:- To a mixture of 2-isopropenyloxazoline-4,5-dione hydrochloride (15 g), methyl methacrylate (20 g), n-butyl acrylate (15 g), styrene (14 g) and ethyl acetate (84 g), acetylcyclohexylsulfonyl peroxide (a polymerization initiator "Perhexa ACS" manufactured by Nippon Oil and Fat) (225 mg) was added, and the resulting mixture was heated at 38 to 39°C for 14 hours, whereby a copolymer of 2-isopropenyloxazoline-4,5-dione hydrochloride with methyl methacrylate, n-butyl acrylate and styrene was produced. Viscosity, A-3 (determined by Gardner bubble viscometer). Mw, 2500 (determined by gel permeation chromatography). Example 20 1) Preparation of an isocyanatocarbonyl group-containing polymer:- A mixture of 2-isoropenyloxazoline-4,5-dione hydrochloride (15 g), methyl methacrylate (20 g), n-butyl acrylate (15 g), 2,2'-azobis(2,4-dimethylvaleronitrile) (1.25 g) and ethyl acetate (25 g) was dropwise added to toluene (50 g) heated at 100°C in 90 minutes while stirring. Stirring was further continued for 5 hours, whereby a copolymer of methacryloyl isocyanate with methyl methacrylate and n-butyl acrylate was produced. Viscosity, C-D (determined by Gardner bubble viscometer). Non-volatile content, 40 %. Mw, 7100 (determined by gel permeation chromatography). 2) Preparation of a blocked isocyanatocarbonyl group-containing polymer:- To the reaction mixture comprising the methacryloyl isocyanate/methyl methacrylate/n-butyl acrylate copolymer as obtained above, t-butanol (6.3 g) was added to produce a t-butanol-blocked methacryloyl isocyanate/methyl methacrylate/n-butyl acrylate copolymer. Example 21 Preparation of an isocyanatocarbonyl group-containing polymer:- An ethyl acetate solution (non-volatile content, 30 %) containing a homopolymer of 2-isopropenyloxazoline-4,5-dione hydrochloride (Mn, 1800) was heated at 70 to 80°C while stirring for 1 hour to obtain a homopolymer of methacryloyl isocyanate. Viscosity: A-B (determined by Gardner bubble viscometer). Example 22 Preparation of a blocked isocyanatocarbonyl group-containing polymer:- 1-Methoxy-2-propanol-blocked methacryloyl isocyanate (10.05 g), methyl methacrylate (9.99 g), ethyl acrylate (9.96 g) and 2,2'-azobis(2,4-dimethylvaleronitrile) (400 mg) were dissolved in dichloroethane (90 g), and the resultant solution was dropwise added to toluene (20 g) heated at 100°C in 3 hours. Then, 2,2'-azobis(2,4-dimethylvaleronitrile) (200 mg) and toluene (2 g) were added thereto, followed by aging for 1.5 hours to give a copolymer of 1-methoxy-2-propanol-blocked methacryloyl isocyanate with methyl methacrylate and ethyl acrylate. Non-volatile content, 17.5 %. Mn, 6500. Example 23 Preparation of a blocked isocyanatocarbonyl group-containing polymer:- 2-Methyl-2-propanol-blocked methacryloyl isocyanate (6.70 g) was dissolved in a mixture of methyl methacrylate (6.66 g), ethyl acrylate (6.64 g) and dioxane (35 g) at 110°C. A solution of 2,2'-azobis(2,4-dimethylvaleronitrile) (400 mg) in butyl acetate (25 g) was dropwise added thereto in 2.5 hours, followed by aging for 1.5 hours to give a copolymer of 2-methyl-2-propanol-blocked methacryloyl isocyanate with methyl methacrylate and ethyl acrylate. Non-volatile content, 22 %. Mn, 6800. Example 24 1) Preparation of an isocyanatocarbonyl group-containing polymer:- A mixture of methacryloyl isocyanate (4 g), methyl methacrylate (4 g), styrene (1 g), butyl acrylate (4 g), 2,2'-azobis(2,4-dimethylvaleronitrile) (390 mg) and dichloroethane (7.5 g) was dropwise added to toluene (8 g) heated at 100°C in 3 hours. Then, 2,2'-azobis(2,4-dimethylvaleronitrile) (65 mg) and toluene (6 g) were added thereto, followed by aging for 1.0 hour to give a copolymer of methacryloyl isocyanate with methyl methacrylate, stryene and butyl acrylate. Non-volatile content, 43 %. 2) Preparation of a blocked isocyanatocarbonyl group-containing polymer:- The reaction mixture comprising the methacryloyl isocyanate/methyl methacrylate/styrene/butyl acrylate copolymer as above obtained was cooled to 10°C, and a solution of methylethylketoxime (3.2 g) in toluene (22 g) was dropwise added thereto, whereby a copolymer of methylethylketoxime-blocked methacryloyl isocyanate with methyl methacrylate, styrene and butyl acrylate was produced. Mn, 6500. Example 25 1) Preparation of an isocyanatocarbonyl group-containing polymer:- A mixture of methacryloyl isocyanate (4 g), styrene (9 g), 2,2'-azobis(2,4-dimethylvaleronitrile) (390 mg) and dichloroethane (0.7 g) was dropwise added to a mixture of toluene (3 g) and butyl acetate (8.3 g) heated at 110°C in 2.5 hours. Then, 2,2'-azobis(2,4-dimethylvaleronitrile) (65 mg) and butyl acetate (1 g) were added thereto, followed by aging for 1.0 hour to give a copolymer of methacryloyl isocyanate with styrene. Non-volatile content, 45 %. 2) Preparation of a blocked isocyanatocarbonyl group-containing polymer:- The reaction mixture comprising the methacryloyl isocyanate/styrene copolymer as above obtained was cooled to 25°C, and a solution of 2,6-di-t-butyl-p-cresol (15.8 g) in butyl acetate (28 g) was dropwise added thereto. Dibutyltin diacetate (250 mg) was added to the resulting mixture, which was then heated at 60°C for 5 hours to produce a copolymer of 2,6-d-t-butyl-p-cresol-blocked methacryloyl isocyanate with styrene. Mn, 9900. Example 26 Preparation of a blocked isocyanatocarbonyl group-containing polymer:- 1-Methoxy-2-propanol-blocked methacryloyl isocyanate (2.1 g) was dissolved in dichloroethane (2.4 g) at 85°C, and a solution of 2,2'-azobis(2,4-dimethylvaleronitrile) (63 mg) in dichloroethane (3.2 g) was dropwise added thereto, followed by aging for 2.0 hours to give a homopolymer of 1-methoxy-2-propanol-blocked methacryloyl isocyanate. Non-volatile content, 22 %. Mn, 2100. Example 27 1) Preparation of an isocyanatocarbonyl group-containing polymer:- Methacryloyl isocyanate (8.9 g), butyl acetate (9 g), dichloroethane (7 g) and 2,2'-azobis(2,4-dimethylvaleronitrile) (166 mg) were mixed together, and the resultant mixture was dropwise added to butyl acetate (4 g) heated at 110°C in 1 hour, followed by aging for 3.0 hours to give a homopolymer of methacryloyl isocyanate. Non-volatile content, 26%. 2) Preparation of a blocked isocyanatocarbonyl group-containing polymer:- The reaction mixture comprising the methacryloyl isocyanate homopolymer as obtained above was allowed to cool to room temperature. A solution of methyl ethyl ketoxime (4.4 g) in butyl acetate (8 g) was added dropwise. The reaction was continued until the infrared absorption attributed to an isocyanato group disappeared. A homopolymer of methyl ethyl ketoxime-blocked methacryloyl isocyanate was obtained. Mn. 1600. For the general purposes of this Application, it may be noted that alkenyl isocyanates (I) and oxazolinedione hydrohalides (II), and the conversion of the latter to the former, are described in EP-A-0202840 (European Patent Application No. 86303601.8).

Claims: A curable composition which comprises (A) a polymer whose molecules have a main chain comprising carbon-carbon bonds and one or more isocyanatocarbonyl groups pendant to the main chain, the content of the isocyanatocarbonyl groups per polymer molecule being from 0.1 to 72.2% by weight, and (B) an active hydrogen atom-containing compound. A composition according to claim 1, wherein the equivalent ratio of the isocyanatocarbonyl groups to the active hydrogen atoms is 1:0.1 to 1:100, preferably 1:0.5 to 1:5. A curable composition according to claim 1 or claim 2, wherein the active hydrogen atom-containing compound has at least two active hydrogen atoms per molecule. An isocyanatocarbonyl group-containing polymer which comprises units of an alkenoyl isocyanate of the formula wherein R is H or C₁₋₅ alkyl, and, optionally, units of one or more other polymerisable monomers having no active hydrogen atom. An isocyanatocarbonyl group-containing polymer having a molecular weight of 1,000 to 100,000, whose molecules have a main chain comprising carbon-carbon bonds and one or more pendant isocyanatocarbonyl groups, the content of the isocyanatocarbonyl groups being 0.1 to 72.2% by weight. A blocked isocyanatocarbonyl group-containing polymer having a molecular weight of 1,000 to 100,000, whose molecules have a main chain comprising carbon-carbon bonds and one or more pendant blocked isocyanatocarbonyl groups, the content of the blocked isocyanatocarbonyl groups being 0.1 to 99.9% by weight. An oxazolinedione hydrohalide group-containing polymer having a molecular weight of 1,000 to 100,000, whose molecules have a main chain comprising carbon-carbon bonds and one or more pendant oxazolinedione hydrohalide groups, the content of the oxazolinedione hydrohalide groups being 0.1 to 99.9% by weight. An isocyanatocarbonyl group-containing polymer whose molecules have a main chain comprising carbon-carbon bonds, one or more pendant isocyanatocarbonyl groups, and one or more pendant isocyanato groups. A polymer according to claim 8, wherein the content of each of the isocyanatocarbonyl groups and the isocyanato groups, independently, is 5 to 30% by weight. A polymer according to claim 8 or claim 9, which has a molecular weight of 3,000 to 100,000. A process for preparing a polymer having pendant isocyanatocarbonyl groups (optionally blocked) and/or pendant oxazolinedione hydrohalide, e.g. a polymer according to any of claims 4 to 10, which comprises polymerising the alkenoyl isocyanate defined in claim 4, optionally blocked at the isocyanatocarbonyl group, or an alkenyloxazolinedione hydrohalide of the formula wherein X is a halogen atom and R is as defined above, optionally together with one or more other polymerisable monomers having no active hydrogen atom; and, if necessary and/or desired, eliminating the blocking group in the polymerisation product or decomposing the polymerisation product. A process for preparing a polymer whose molecules have a pendant blocked isocyanatocarbonyl group, which comprises reacting the corresponding isocyanatocarbonyl group-containing polymer with a blocking agent. A composition according to any of claims 1 to 3, wherein the polymer is as claimed in any of claims 4 to 10. A composition according to any of claims 1, 2, 3 and 13, wherein the polymer has a molecular weight of at least 1,000, preferably 1,000 to 100,000.

Inventors: AOKI, KEI, MIZUGUCHI, RYUZO, TSUBONIWA, NORIYUKI, URANO, SATOSHI
Applicants: NIPPON PAINT CO., LTD.
Application year: 1986
Main classification: C08F8
IPC codes: C08F8