Method of manufacturing a semiconductor device free from the current leakage through a semi-conductor layer

Abstract: An improved semiconductor device is disclosed which is free from current leakage due to pin-holes or other gaps. Also an improved method for processing a semiconductor device is shown. According to the invention, gaps produced in fabricating process of the semiconductor layer are filled with insulator in advance of deposition of electrodes.

Description: BACKGROUND OF THE INVENTION This invention relates to a method of manufacturing a semiconductor device in which the performance of the semiconductor device is improved. More particularly, this invention relates to measures for eliminating disadvantages caused by the effect of electrical shorts and shunts due to pinholes or other gaps created during the fabrication process of the device. Recently, considerable efforts have been made to develop systems for depositing amorphous semiconductor alloys, each of which can encompass relatively large areas, and which can be doped to form p-type and n-type materials for the production of p-i-n and other type devices which are, in photovoltaic and other applications, substantially equivalent to their crystalline counterparts. As such device, the applicant disclosed improved photoelectric cells in Japanease Patent Published Applications Nos. sho 55-4994, 55-124274, 56-13777, 56-13778 and 56-13779. One example of prior art photovoltaic device is shown in Fig. 1. In the figure, a transparent conductive film 2 is formed on a glass substrate 1 with a mask aligned above the substrate 1. Semiconductor layers 3 are deposited on the substrate 1 with the conductive film 2 therebetween with a mask aligned above the substrate 1. Further, on the substrate 1 with the conductive film 2 and the semiconductor layers 3, aluminium layer 4 are formed as second electrodes with a mask. Reference numerals 31 and 11 designate photoelectric cells respectively in the figure. The two cells 31 and 11 are connected in series by means of a connection 12. In the connection 12 the second electrode 38 is made in contact with the first electrode 37. Although the figure appears only with two connections, a number of the cells are connected with each other in series. The integrated photovoltaic device tends to be degraded after thermal treatment at 150°C for tens of hours. Such device is not suitable for outdoor use where the device is likely to be subjected to high ambient temperature. Furthermore it is impossible to perform the patterning of the aluminium layer 14 with laser processing, instead of with masks, since the laser beam is likely to injure the thin semiconductor film during processing. Efficiency of the patterning with masks cannot be expected to be high due to low accuracy in aligning the masks with the pattern, no self alignment being enjoyed. Further, as is described in US-A-4166918, the voltage and current output of thin film solar cells may be greatly reduced or completely eliminated by electrical shorts or shunts formed during the fabrication of the solar cell. Electrical shorts occur when there is a pinhole in the semiconductor layer and the front and back electrodes are touching. A shunt is the loss of charge in the semiconductor body due to imperfect barrier formation or the formation of an ohmic contact by a high work function metal rather than a Schottky barrier formation. The problem of solar cell defects which cause shorts or shunts increase greatly with increasing solar cell size. If large area solar cells are to be economically feasible, then methods of eliminating these shorts and shunts during fabrication or removing the defects after processing must be developed. According to US-A-4166918, a conventional method of improving the performance of a solar cell made from gallium arsenide, cadmium telluride, single crystal or amorphous silicon and the like requires the etching out of the defects in the solar cell, and attempts made to remove the defects by the application of a reverse bias voltage tended to increase the incidence of shorts and shunts in the solar cell. The proposal made in US-A-4166918 is for a method of improving the performance of a solar cell which incorporates a thick film cermet electrode contacting the active region of the solar cell opposite to a surface incident to solar radiation, the method comprising applying a reverse bias voltage of sufficient magnitude to burn out the defects in that solar cell but less than the breakdown voltage of the cell. EP-A-0060487 discloses a plugged pinhole thin film and a method of making the same which is said to be particularly useful in the production of thin film insulating or semiconductor layers and thin film devices such as photoconductive and photovoltaic devices. The thin film of EP-A-0060487 has its pinholes plugged with insoluble insulating photoresist material and is substantially opaque to the light wavelength range causing the photoresist material to become insoluble, the method of plugging pinholes in the thin film comprising coating one side of the film with a layer of photoresist material which fills the pinholes and exposing the other side of the film to the light wavelength range which causes the photoresist material in the pinholes to become insoluble. SUMMARY OF THE INVENTION According to the present invention, there is provided a method of manufacturing a semiconductor device in which a semiconductor layer is sandwiched between first and second electrode layers, said method including the filling of pinholes and other gaps in the semiconductor layer with an insulating resin material before the formation of the second electrode, and being characterized in that the second electrode layer comprises a conductive transparent compound or mixture, and further characterised by the application after the second electrode is formed of a reverse voltage less than the breakdown voltage of the semiconductor layer between the first and second electrodes. Further features of the present invention are set forth in the appended claims and, together with the features abovementioned, will be explained hereinafter by reference to the accompanying drawings. BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is a fragmentary, cross sectional view of a prior art solar cell; Figs. 2(A) through 2(D) are fragmentary, cross sectional views showing the manufacturing process of a solar cell with pinholes in the semiconductor layer being plugged with a photoresist resin; Fig. 3 is a graphical diagram showing the relation between time and efficiency for the solar cell of Fig. 1 and a solar cell produced by the process of Figs. 2(A) to 2(D); Figs. 4(A) through 4(D) are fragmentary, cross sectional views showing the manufacture of a solar cell in accordance with the present invention; Fig. 5 is an equivalent circuit illustrating how in the practice of the present invention a reverse voltage is applied to all the cells of a multi-cell device; Fig. 6 is a graphical diagram showing the trend of reverse bias current in response to increasing reverse bias voltage; and Figs. 7(A) through 7(D) are fragmentary, cross sectional views showing the manufacture of a further solar cell in accordance with the present invention. DETAILED DESCRIPTION Referring to Figs. 2(A) through 2(D), a process in which pinholes are plugged with photoresist resin will first be explained. In the figure, a transparent electrode is formed and patterned on transparent substrate 1 made of, for example, glass pane of 1.2 mm thick x 10 cm long x 10 cm wide. The transparent electrode 2 is made, inter alia, from an ITO layer 150nm (1500 angstroms) thick superimposed by a Sn0₂ layer 20 to 40nm (200 to 400 angstroms) thick, an ITO layer 150nm (1500 angstroms) thick superimposed with a Sn₃N₄ layer 50nm (500 angstroms) thick, or a transparent layer doped with halogen of 150 to 200nm (1500 through 2000 angstroms) thickness mainly made of tin oxide or tin nitride by a CVD method in vacuum, a LPCVD method, a spraying method or a sputtering method. The layers thus laminated are irradiated from upper or lower side of the substrate 1 with laser beam of 1.06 micro meters wavelength or 0.53 micro meter wave length from a YAG laser to perform the patterning for the transparent electrode 2. The grooves 13 of 10 cm long formed by the patterning partition adjacent ones of cells, each groove having 10 to 20 nm width. On the layer is formed, by a plasma or photo CVD method, a nonsinglecrystal layer 3 having a p-n or p-i-n junction of 0.2 to 1.0 micro meter thickness, normally of 0.5 to 0.7 micro meter thickness. For instance, the nonsinglecrystal layer can be comprised, with a p-i-n junction, of a p-type semiconductor layer (Si x C 1-x ; 1 >x>0) 5 to 15nm (50 to 150 angstroms) thick, an intrinsic amorphous or intrinsic semiamorphous silicon semiconductor layer 0.4 to 0.9 micro meters thick, and a crystallite layer 200 to 500 micro meters thick. On the semiconductor layer 3, a lot of gaps and pinholes 6 and 6' result unintentionally due to falling out of flakes which are involved into the semiconductor layer 3 during fabrication. There are observed about two to four such defects in ten fields of view through a microscope with a magnification of 100 to 1000. According to the described process, the holes 6 and 6' are filled and stopped with insulator. Hereinbelow, the stopping process will be explained in detail. The semiconductor layer 3 with the holes 6 and 6' is coated with photocurable organic resin by a spinner or a coater in the manner that all the holes are filled completely with the resin. The organic resin may be "photoneeth" distributed from Toray Industries Inc. or other known photoresist. For instance, an amount of photoneeth having viscosity of about 120 mPa·s ( 120 CP ) is applied on the layer 3 to 0.2 through 5.0 micrometers thickness by spinning at 500 rpm for 10 seconds and thereafter at 2000 rpm for 30 seconds followed by a prebaking at 85°C for an hour. The organic layer is irradiated with ultraviolet light 17 having 300 to 400 nanometers wavelength from the glass substrate side. The ultraviolet light cannot penetrate the semiconductor layer 3 because of the absorption in the layer whereas the resin stopping the holes 6 and 6' is cured selectively. In other words, the intensity and the wavelength are chosen so that the semiconductor layer 3 can function as a mask. Then, the uncured resin is eliminated by a known rinsing. The remaining resin cured in the holes is chemically stabilized by sintering and post-curing. Thus the stopping process is completed. After stopping the holes, openings 18 are formed adjacent to the groove 13 as shown in Fig. 2(B) by means of laser scribing to provide an access to the first electrodes 37 and 37'. Although the openings 18 reach the substrate 1 in the figure, they can be more shallow as long as the first electrodes 37 and 37' are exposed from the opening. A second electrode 4 consisting of two conductive layers 23 and 24 is deposited on the laminated layers and separated into portions by grooves 20 by laser scribing. The lower conductive layer 23 may be 30 to 140nm (300 to 1400 angstroms) thick and made from ITO, In₂0₃, Sn0₂ or ITN (a mixture of indium nitride and tin nitride). The upper conductive layer 24 may be 30 to 50nm (300 to 500 angstroms) thick and made, as a single or double layer, from aluminium, chromium or silver. For example the second electrode 4 may be composed of an aluminium layer 100nm (1000 angstroms) thick on a ITO layer 150nm (1500 angstroms) thick. The aluminium layers 24 provide inside surfaces on which incident light entering from the substrate side can be reflected. The ITO layers 23 are disposed to prevent the aluminium layer from corroding due to interaction with the semiconductor layer. These two layers are fabricated by an electron beam deposition or a plasma CVD method at less than 300°C. As a result an improved solar cell is provided with which light having a wave length of 600 to 800 nm can be efficiently converted into electricity. For proximate contact with a n-type semiconductor, a transparent indium compound or mixture including indium oxide and/or indium nitride is considered adequate as the transparent layer 23. For a p-type semiconductor, a tin compound or mixture of Sn0₂, Sn₃N₄ and/or SbN is adequate in view of high efficiency and reliability for long time. The transparent electrode 23 is made in contact with the first electrode 2 at the opening 18. At this contact there is only a hetero- or homo-junction of a nitride and/or an oxide so that no interaction occurs even at 150°C, unlike the prior art illustrated in Fig.1 forming metal junction. In addition to this, such a laminated electrode 4 is advantageous especially for laser patterning. Namely the aluminium electrode 24 can be removed in the patterning together at one time with the laser scribing of the transparent electrode 23 which is easily sublimated under irradiation of laser beam and carries the aluminium electrode thereon away from the substrate. A passivation film of silicon nitride 21 is deposited to 50 to 200nm (500 to 2000 angstroms) thickness by a photo CVD method or plasma vapor deposition, and a take-out line 5 is provided on the aluminium electrode 24. Thus, following placing an organic resin layer 22 such as of polyimide, polyamide, kapton (R) or epoxy, the semiconductor device is made into a photoelectric conversion device in which a plurality of cells 31 and 11 are connected in series by the connection 12. The organic resin is provided mainly for fixation of the take-out electrode 5. Further a device of 120 cm x 40 cm, two devices of 60 cm x 40 cm, or six devices of 40 cm x 20 cm are integrally packaged into a 120 cm x 40 cm panel according to NEDO standard. Experimental results were obtained with a solar cell manufactured according to the above explained process having a substrate of 10 cm long x 10 cm wide as below; open-circuit voltage 12.77 V fill factor 0.574 short-circuit current 69.0 mA conversion efficiency 7.46 % Also, experimental results were obtained with a solar cell which was manufactured without the stopping process, but with other process steps being similar to the above, as below; sample 1, sample 2 open-circuit voltage 11.49 V 3.02 V fill factor 0.471 0.316 short-circuit current 53.7 mA 54.20 mA conversion efficiency 4.43 % 0.75 % From the above data, it is understood that the stopping hole process makes solar cells more efficient. Fig. 3 shows the trend of normalized efficiencies with time passing obtained by reliability trials of solar cells manufactured with and without the hole stopping process under an atmospheric condition but at 150°C. A curve 25 shows the normalized efficiency of a prior art solar cell having the configuration of Fig. 1; the efficiency is degraded with time passing. In the prior art device, the aluminium electrode 4 is made in contact with the semiconductor layer 3 and in the contact 12 there is the tin oxide layer 37 in contact with the aluminium electrode 4. These contacts give rise to oxidation of the aluminium electrode 4 and to interaction between the electrode 4 and the semiconductor layer 3 of n-type. Because of this, the efficiency is degraded to less than 50 % of the initial value only after ten hours or the like. On the other hand, a curve 26 is plotted for a solar cell made by the process of Figs 2(A) to 2(D) with resin stopping the holes and with the laminated electrode 4. In this configuration only oxide-oxide contacts appear making the contact 12 stable and reliable. The other important feature not illustrated in the figure is that high yield can be obtained since fluctuation of the characteristics among products is small. For instance, 0.27 was obtained as a variance of efficiency from ten samples of 10 cm long x 10 cm wide. Referring to Figs. 4(A) to 4(D), an embodiment of the invention is illustrated. On a substrate 1 such as a glass pane of 1.2 mm thick x 10 cm long x 10 cm wide is formed a conductive transparent film 2, e.g., a laminated film of an ITO layer 150nm (1500 angstroms) thick on a Sn0₂ layer 20 to 40nm (200 to 400 angstroms) thick or a transparent film mainly composed of tin oxide or tin nitride doped with halogen. The film may be fabricated by a LPCVD method, a plasma CVD method, a spraying method, sputtering method and an ECR method. The conductive film 2 is divided into a plurality of sections by patterned grooves 13 which are formed by laser beam of 1.06 micro meters wave length or 0.53 micro meters wave length from a YAG laser controlled by a micro computer. The patterned grooves are 50 micro meter wide and 10 cm long by which each section is partitioned from others with 10 to 20 mm width. On this film a nonmonocrystal layer is formed with a p-n junction or p-i-n junction at 0.2 to 1.0 micro meter thickness, more preferably 0.5 to 0.7 micro meter thickness. A preferred example is a laminated layer composed of a p-type semiconductor layer ( Si x C 1-x ; 1>x>0 ) of 5 to 15nm (50 to 150 angstroms) thick, an intrinsic amorphous or intrinsic semiamorphous silicon semiconductor layer 0.4 to 0.9 micro meter thick, and a crystal layer 200 to 500 micro meter thick. The semiconductor layer 3 with the holes 6 and 6' is coated with photocurable organic resin in the manner that all the holes are filled completely with the resin by a spinner or a coater. The organic resin may be a photoresist of positive type such as OFPR-800 distributed by Tokyo Ohka Kogyo Co., Ltd. or other known photo resist. For instance, an amount of photoresist is applied on the layer 3 to a thickness of 0.1 through 5.0 micro meters by spinning at 500 rpm for 5 seconds and thereafter at 2000 rpm for an appropriate period followed by a prebaking at 85°C for 40 minutes. The organic layer 3 is irradiated with ultraviolet light 17 having 300 to 400 nanometers wavelength from the resist side. As the curing for OFPR-800, irradiation of ultraviolet light of 6 mW/cm² for 5 seconds is carried out, followed by aftertreatments. Then, the uncured resin is eliminated by a known rinsing with pure water for 10 minutes. The remaining resin cured in the holes is chemically stabilized by sinter and post-cure. For instance, the layer is let undergo post baking for an hour at 150°C. Thus the stopping process is completed. After stopping the holes, openings 18 are formed adjacent to the groove 13 as shown in Fig. 4(B) by means of laser scribing to provide an access to the first electrodes 37 and 37'. Although the openings 18 reach the substrate 1 in the figure, they can be more shallow as long as the first electrodes 37 and 37' are accessed. A second electrode 4 consisting of two conductive layers 23 and 24 is deposited on the laminated layers and separated into portions by grooves 20 scribed by laser scribing. The second electrode may be a transparent conductive layer 30 to 50nm (300 to 500 angstroms) thick, for example, made of ITO, In₂0₃ Sn0₂ or ZnO through which incident light can go out of the device. On the other hand, the second electrode may be formed reflective by deposition, on the transparent electrode, of aluminium, chromium or silver as a single-layered reflective film, or aluminium and nickel as a double-layered reflective film. In this embodiment, the second electrode is comprised of an ITO layer 105nm (1050 angstroms) thick and an aluminium layer 100nm (1000 angstroms) thick. The electrode can be formed by sputtering, an electron beam deposition or plasma CVD method at less than 300°C in order not to render the semiconductor degraded. Referring to Fig. 4(D) and Fig. 5, a reverse bias applying circuit is illustrated. The circuit comprises a power supply 240 and a number of Zener diodes 230. Between each adjacent ones of the diodes 23 and between the power supply and the first or last diodes are made contact with the first and second electrodes respectively so that the output voltage is divided into the reverse bias voltage which is applied to each of the cells constituting the device. The reverse bias voltage must be less than the breakdown voltage of the p-i-n junction of the semiconductor layer 3. Because of this the reverse bias voltage does not cause current to pass through flawless portions of the semiconductor layer 2. To preclude breakdown of the p-i-n junction further, the zener diodes are selected out of a variety of voltage dividing element candidates. The zener voltage is chosen slightly below the breakdown voltage of the p-i-n junction. In Fig. 5, the circuit diagram includes the number of the cells constituting the device each of which is represented by a diode corresponding to the semiconductor layer 2 and a resistance corresponding to the defects (holes) as leakage source. The Zener diode 230 is connected in parallel to the diode and the resistance so that the voltage applied to the diode 25 is kept below the breakdown voltage thereof. With the bias voltage less than the breakdown voltage, the holes or flaws in the semiconductor layer 3 filled with the organic resin become current passages which are heated as electric current flows therethrough. The electric power is sometimes short of burning out the holes or flaws completely. To make the burning out easy, the substrate 1 is heated in advance together with the semiconductor to less than the temperature at which the semiconductor may be degraded, normally less than 150°C. An experiment was made with a device having 15 cells connected with each other and the bias voltage was chosen at 120 V. As a result, the current trend in response to increasing reverse bias voltage was obtained as shown in Fig.6. In the experiment, the reverse bias voltage increased from 0 V to 120 V. A first leakage current was observed at 30-1. However the leakage current was cured because of burning out due to the concentrated current flow. As the reverse bias voltage increased, a number of current ripples were observed. The magnitude of the leakage current became larger at the higher reverse bias voltage. With the reverse bias voltage decreasing from a point 32, the reverse bias current smoothly dropped without leakage current. For reference, the device thus treated was subjected to increasing reverse bias voltage. No leakage current, however, was observed until reverse current was raised at the withstand voltage. After removing the bias applying circuit, the device integrated on a 10 cm x 10 cm panel was irradiated with light of 100 mW/cm2 (AM1). The characteristics obtained are; open-circuit voltage 12.943 V fill factor 0.6641 short-circuit current 79.34 mA current density 17.290 mA/cm² efficiency 9.90 % With the device fabricated according to a process identical to that of Fig. 4 but without reverse bias curing, the following experimental data 1 were obtained, and without stopping process and reverse bias curing, the following experimental data 2 were obtained: data 1 data 2 open-circuit voltage 12.315 V 11.49 V fill factor 0.597 0.471 short-circuit current 79.34 mA 53.7 mA efficiency 8.33 % 4.43 % Compared with the figures obtained with the initial embodiment, it is understood that the device having undergone the reverse bias voltage demonstrates further improved characteristics. The reason why the reverse bias curing is effective is considered to be that a chemical reaction between the resin and the semiconductor may produce a stable insulator tightly joined to the pin-holes. A further embodiment of the invention is shown in Fig. 7. In this embodiment, the process is similar to that of the preceding embodiment. So only different configurations are described and redundant explanation is not repeated. A substrate 1 is composed of a conductive stainless foil 40 of 10 to 100 micro meters thickness and a heatproof organic resin film or an inorganic insulator film such as made of enamel 41 on the stainless foil 40. On the substrate 1, a first electrode 2 is formed, for example, made of a 20nm (200 angstroms) thick chromium layer, a 150nm (1500 angstroms) thick aluminium layer plus a 50nm (500 angstroms) thick Sn₃N₄ layer or a 150 to 200nm (1500 to 2000 angstroms) thick transparent conductive layer mainly composed of tin oxide or tin nitride doped with halogen. Grooves 8 which provide accesses to the first electrode reach only to the surface of the first electrode 2 at which the second electrode can be in contact with the first electrode 2. After removing the bias applying circuit, the device integrated on a 10 cm x 10 cm panel was irradiated with light of 100 mW/cm² (AM1). The characteristics obtained are; open-circuit voltage 12.618 V fill factor 0.678 short-circuit current 79.710 mA current density 17.371 mA/cm² efficiency 9.82 % With the device fabricated according to the process identical to that in Fig. 7 but without reverse bias curing, the following experimental data 1 were obtained, and without both stopping process and reverse bias curing, the following experimental data 2 were obtained: data 1 data 2 open-circuit voltage 11.30 V 6.54 V fill factor 0.626 0.368 short-circuit current 79.4 mA 75.69 mA efficiency 8.16 % 3.48 % The other important feature is that high yield can be obtained since the fluctuation of the characteristics is small among products. For instance, 0.195 (X 9.63%) was obtained as a variance of efficiency from ten samples of 10 cm long x 10 cm wide prepared according to NEDO standard. Examples of variations which can be made are as follow. The semiconductor layer may be constituted with multijunction structure in place of single junction structure. Namely, the layer can be a laminate composed of a p-type semiconductor (Si x C 1-x ), an intrinsic amorphous silicon semiconductor, an n-type silicon semiconductor, a p-type semiconductor (Si x C 1-x ), an intrinsic semiconductor (Si x Ge 1-x ) and n-type silicon semiconductor layer 30 to 100nm (300 to 1000 angstroms) thick, wherein 0 < X < 1, e.g., X = 0.5. To engrave the grooves, one line of the grooves can be formed at once by irradiating with laser beam extending in lateral direction which is produced from an excimer laser through a cylindrical lens, if necessary, after expansion of original beam. The above technique according to the invention is applicable also to a light emitting semiconductor device with double heterojunctions and a superlattice structure. As such devices, the applicant has disclosed some semiconductor devices in US-A-4,527,179 and US-A-4,616,244. The invention is advantageous also when applied to a diode array of an image sensor or a nonlinear element of a thin film display. In some applications, the reverse bias voltage circuit can be much simplified. For example, an active device can be cured by applying a reverse voltage to source, drain and/or gate electrodes.

Claims: A method of manufacturing a semiconductor device in which a semiconductor layer is sandwiched between first and second electrode layers, said method including the filling of pinholes and other gaps in the semiconductor layer with an insulating resin material before the formation of the second electrode, and being characterized in that the second electrode layer comprises a conductive transparent compound or mixture, and further characterised by the application after the second electrode is formed of a reverse voltage less than the breakdown voltage of the semiconductor layer between the first and second electrodes in order to eliminate shorts and shunts of the semiconductor layer. A method as claimed in claim 1 wherein the insulating resin material is a photocurable resin and the method includes the application of the photocurable resin to a surface of the semiconductor layer, the subsequent irradiation of the photocurable resin with the semiconductor layer serving as a mask so as to cure the resin filling the pinholes and other gaps in the semiconductor layer, and the removal of uncured resin from the semiconductor layer. A method as claimed in claim 1 or 2 wherein the application of the reverse voltage between the first and second electrodes is effected with the semiconductor layer heated to an elevated temperature selected so as not to risk degradation of the characteristics of the semiconductor layer. A method as claimed in any of the preceding claims wherein the semiconductor device comprises a plurality of series connected solar cells each comprising a respective semiconductor layer and respective first and second electrodes, and the application of a reverse voltage to each of said cells is effected by use of a voltage source and a plurality of series connected Zener diodes which are coupled to the series connected solar cells so that each cell has applied thereto a reverse voltage determined by a respective one of the Zener diodes and less than the breakdown voltage of the cell. A method as claimed in any of the preceding claims wherein said semiconductor junction layer is an amorphous semiconductor layer incorporating a p-i-n junction. A method as claimed in any of the preceding claims wherein said semiconductor device comprises a photovoltaic device. A method as claimed in any of claims 1 to 5 wherein said semiconductor device comprises a light emitting device. A method as claimed in claim 7 wherein said light emitting device has a superlattice structure. A method according to any preceding claim wherein said substrate is glass. A method according to any preceding claim wherein said first electrode comprises a transparent conductive material. A method according to any preceding claim, wherein said second electrode comprises a metal layer formed over said conductive transparent compound or mixture. A method according to claim 11 wherein said metal is aluminium, silver or chromium. A method according to any preceding, claim in which said conductive transparent compound or mixture comprises ITO, In₂O₃ or SnO₂.

Inventors: IPPEI KOBAYASHI, KAORU KOYANAGI GREEN HILL IKED, KATSUHIKO SHIBATA, MASATO SUSUKIDA, MASAYOSHI ABE, MIKIO KINKA, SUSUMU NAGAYAMA, SUZUKI KUNUO, TAKESHI FUKADA, YAMAZAKI SHUNPEI, IPPEI, KOBAYASHI, KAORU, KOYANAGI GREEN HILL IKEDA 302, KATSUHIKO, SHIBATA, MASATO, SUSUKIDA, MASAYOSHI, ABE, MIKIO, KINKA, SUSUMU, NAGAYAMA, SUZUKI, KUNUO, TAKESHI, FUKADA, YAMAZAKI, SHUNPEI
Applicants: SEMICONDUCTOR ENERGY LAB, SEMICONDUCTOR ENERGY LABORATORY CO., LTD.
Application year: 1986
Main classification: H01L27
IPC codes: H01L31, H01L27