A PHOTORECEPTOR FOR ELECTROPHOTOGRAPHY

Abstract: A photoreceptor for electrophotography comprises an electrically conductive substrate (1), a bottom layer (2), a photoconductive layer (4) composed mainly of amorphous silicon, and a surface layer (6),in that order, both the bottom and surface layers having a greater optical bandgap than said photoconductive layer, wherein a first middle layer(3)is disposed between said bottom layer (2) and said photoconductive layer (4), and a second middle layer(5) is disposed between said photoconductive layer (4) and said surface layer (6), both the first and second middle layers being composed mainly of amorphous silicon and having a varied distribution of concentrations of doped atoms from the bottom to the top of the layer.

Description: This invention relates to a photoreceptor for electrophotography which comprises a photoconductive layer composed mainly of amorphous silicon. In photoreceptors provided for electrophotography presently in practical use, a combination of high resistance and high sensitivity is a basic requirement. As a material having such a combination of characteristics, a resin dispersal material in which cadmium sulfide powder is dispersed into an organic resin and an amorphous material such as amorphous selenium (a-Se) or amorphous arsenious selenide (a-As₂Se₃) have been most often used. However, all such materials cause pollution, so the development of a substitute material is desirable. In recent years, amorphous silicon has gained prominence as a different material for the above-mentioned photoreceptors. In addition to it not causing pollution and it having high sensitivity, this substance is also extremely hard, and it is expected to be a superior material for use in photoreceptors. However, amorphous silicon by itself does not have enough resistance to maintain the electrostatic charge necessary during the procedures of electrophotography. Therefore, in order to use amorphous silicon as a photoreceptor for electrophotography, a means by which a large electrostatic potential can be maintained with high sensitivity is necessary. As one such means, it has been proposed to bring about high resistance in the amorphous silicon layer itself which is to become a photoreceptor. However, in order to use with efficiency the superior photoconductive characteristics of amorphous silicon (including its strong optical absorbance, relatively large drift mobility of electrons and positive holes, its sensitivity to long wavelengths, etc.), it would be better to provide a blocking layer having a great energy bandgap on the surface of each of the amorphous silicon layers (i.e., on the photoconductive layer) and the substrate rather than to enhance the capacity to be charged with electricity by bringing about high resistance in the photoconductive layer itself, as has been mentioned. This kind of surface layer with a great energy bandgap does not only hold an electrostatic charge, but also protects the photoreceptor from strong corona shock arising during the process of electrophotography. Such a surface layer also acts as a protective film which minimizes changes in the characteristics of the photoreceptor caused by changes in the environment (in temperature, humidity, etc.) so as to stabilize the surface of the photoreceptor, such a protective surface layer is indispensable. Of course, for it to act as a protective surface layer, a great energy bandgap is desirable for this layer. As mentioned above, the provision of the surface layer having a great energy bandgap is desirable in that not only an electrostatic charge can be effectively held on the photoconductive layer, but also the surface of the photoconductive layer can be protected. However, when a surface layer with a great energy bandgap is formed directly on the amorphous silicon layer which is a photoconductive layer, various phenomena appear that are undesirable in a photoreceptor for electrophotography. One such phenomenon is mechanical instability. When a photoconductive layer of amorphous silicon is constructed with a surface layer having a great energy bandgap, the binding between the photoconductive layer and the surface layer is not stable due to a difference in the coefficient of thermal expansion therebetween, and they tend to peel away from each other. Another phenomenon is deterioration in the electrical characteristics of the photoreceptor. That is, during the process of electrophotography, when a photoreceptor, the surface layer of which has been already electrically charged, is illuminated, the light causes an electric charge on the photoreceptor with a different polarity from the charging polarity of the electric charge on the surface layer. The electric charge on the photoconductive layer then moves through the surface layer to neutralize electrostatically the electric charge on the surface layer. However, the energy bandgap of the surface layer is so large that there is an extremely great energy bandgap at the interface between the photoconductive layer and the surface layer, and smooth transfer of the electric charge does not take place. Instead, the electric charge builds up in the vicinity of the interface between the surface layer and the photoconductive layer, resulting in a residual potential. Such a residual potential is undesirable, and if it increases, it can cause deterioration in the characteristics of the photoreceptor. Moreover, residual potential frequently gives rise to movement of the accumulated carriers in the horizontal direction of the photoreceptor, which causes the problem known as image blurring. As mentioned above, a surface layer with a great energy bandgap is essential because it holds the electric charge and protects the surface of the photoconductive layer, but it causes incidental problems both mechanically and electrically. This means that a satisfactory photoreceptor made of amorphous silicon has not yet been achieved. Moreover, in order to prevent the injection of an electric charge from the substrate to the photoconductive layer, it is preferable to form a bottom layer with a great energy bandgap on the bottom of the photoconductive layer which faces the substrate, in the same manner as in the surface layer with a great optical bandgap. However, because of the lack of mechanical matching, it is difficult to form a photoconductive layer, which does not incorporate any nitrogen (N) or carbon (C) directly, wth a thickness of, for example, 8 µm or more on the bottom layer. If an amorphous silicon membrane which does not include any boron is used as the photoconductive layer, it is not suitable for use as a photoconductive layer when positively charged because of a number of difficulties: the resistance is small, the capacity to be charged with electricity cannot be large, and the transport capacity (mobility-carrier lifetime product) of positive holes is poor. In EP-A-0 039 223 there is disclosed a photoreceptor for electrophotography comprising an electrically conductive substrate, a bottom layer, a photoconductive layer composed mainly of amorphous silicon, and a surface layer, in that order, both the bottom and surface layers having a greater energy bandgap than the photoconductive layer, wherein a first middle layer is disposed between the bottom layer and the photoconductive layer, and a second middle layer is disposed between the photoconductive layer and the surface layer, both the first and second middle layers being composed mainly of amorphous silicon and having a uniform distribution of dopant atoms from the bottom to the top of the layer. In accordance with the present invention, there is provided a photoreceptor for electrophotography comprising an electrically conductive substrate, a bottom layer, a photoconductive layer composed mainly of amorphous silicon, and a surface layer, in that order, both the bottom and surface layers having a greater energy bandgap than said photoconductive layer, and comprising furthermore a first middle layer disposed between said bottom layer and the photoconductive layer, and a second middle layer disposed between the photoconductive layer and said surface layer, both the first and second middle layers being composed mainly of amorphous silicon, characterised in that the bottom layer and the surface layer contain either nitrogen or carbon, the photoconductive layer and the first and the second middle layers contain boron, the concentration of which varies through each of said three layers, the first and second middle layers further contain nitrogen or carbon according to whether respectively nitrogen or carbon is contained in the surface layer and the bottom layer, and the concentrations of nitrogen or carbon respectively increase from those surfaces of the first and second middle layers which are in contact with the photoconductive layer towards those surfaces of the first and second middle layers which are in contact with the bottom and surface layers respectively. The surface layer and the bottom layer are, in a preferred embodiment, composed of amorphous silicon nitride or amorphous silicon carbide. When the surface layer and the bottom layer are composed of amorphous silicon nitride, in a preferred embodiment, the first and second middle layers contain nitrogen and boron as dopant atoms, the concentrations of which are not uniform therethrough from the bottom to the top of the layer. Alternatively, when the surface layer and the bottom layer are composed of amorphous silicon carbide, in a preferred embodiment, the first and second middle layers contain carbon and boron as dopant atoms, the concentrations of which are not uniform therethrough from the bottom to the top of the layer. Thus, the invention described herein makes possible the objects of (1) providing a photoreceptor for electrophotography which produces a good image at an early stage of the working life of the photoconductor having especially excellent contrast; and (2) providing a photoreceptor for electrophotography which can make a number of copies (e.g., 300,000 copies) with an excellent quality image which is equal to that at the early-phase. For a better understanding of the invention and to show how the same may be carried into effect, reference will now be made, by way of example, to the accompanying drawings in which: Figure 1 is a cross-sectional view showing the structure of a photoreceptor for electrophotography of this invention; and Figures 2(a) , 2(b) and 2(c) , respectively, are schematic diagrams showing the concentrations of nitrogen atoms and boron atoms contained in each of the layers constituting the photoreceptor of electrophotography shown in Figure 1 . Figure 1 shows a photoreceptor for electrophotography of this invention which comprises an electrically conductive substrate 1 , a bottom layer 2 , a first middle layer 3 , a photoconductive layer 4 , a second middle layer 5 , and a surface layer 6 , in that order. To prevent the injection of an electric charge from the substrate 1 to the photoconductive layer 4 , the bottom layer 2 , which is composed of amorphous silicon nitride (a-Si 1-x N x ) or amorphous silicon carbide (a-Si 1-x C x ) and which has a greater optical bandgap than the photoconductive layer 4 , is disposed on the substrate 1 . In order to achieve electrical and mechanical matching between the bottom layer 2 and the photoconductive layer 4 , which does not contain any nitrogen (N), carbon (C), etc., the first middle layer 3 composed of boron-doped amorphous silicon containing nitrogen (N) or carbon (C) is disposed therebetween in such a manner that the concentration of the N, C, and B are not uniform therethrough in the vertical direction (i.e., from the bottom to the top of the layer). In order to increase the capacity to be charged with electricity of the photoreceptor and the photo-sensitivity thereof, the photoconductive layer 4 is constructed so as to incorporate boron, the concentration of which is not uniform therethrough from the bottom to the top of the layer. Moreover, in order to increase the capacity to be charged with electricity of the photoreceptor and to enlarge the life span thereof, the surface layer 6 , which is composed of a-Si 1-x N x or a-Si 1-x C x and which has a greater optical bandgap than the photoconductive layer 4 , is placed on the upper portion of the photoreceptor. To achieve electrical and mechanical matching between the photoconductive layer 4 and the surface layer 6 , the second middle layer 5 composed of boron-doped amorphous silicon containing N or C is disposed therebetween n such a manner that the concentrations of the N or C, and the B are not uniform therethrough from the bottom to the top of the layer. With the above-mentioned structure, a photoreceptor for electrophotography which produces a good early phase image with especially excellent contrast and which can make a number of copies (e.g., 300,000 copies) with an excellent image which is equal to the images produced in the early phase can be obtained. The photoreceptor for electrophotography of this invention shown in Figure 1 may be produced by the following process, in which nitrogen is incorporated into the first and second middle layers 3 and 5 , the bottom layer 2 , and the surface layer 6 . a-Si constituting the photoconductive layer and other layers is prepared by treating monosilane gas (SiH₄) to glow-discharge decomposition (e.g., plasma chemical vapor deposition) by means of an inductive-coupling apparatus in a reaction chamber in which the electrically conductive substrate on which the photoconductive layer will be formed is electrically grounded, and a high-frequency electrical power is applied to the coil through an impedance-matching circuit. The reaction gas is allowed to flow into the reaction chamber at a controlled flow rate, and the electrically conductive substrate placed in the reaction chamber is kept at 200-300° C (e.g., 250° C). First, the bottom layer 2 made of amorphous silicon nitride with a thickness of, for example, 0.15 µm, is formed on the electrically conductive substrate 1 under the membrane-formation conditions shown in Table 1 . Next, the first middle layer 3 composed mainly of amorphous silicon with a thickness of, for example, 1.5 µm, is formed on the bottom layer 2 under the membrane-formation conditions shown in Table 2 , wherein this first middle layer 3 is formed such that the concentrations of the nitrogen and boron are not uniform therethrough from the bottom to the top of the layer by changing the NH₃ flow rate from 12 sccm to 0 sccm and the B₂H₆ flow rate from 50 sccm to 0.09 sccm either continuously or in a stepwise fashion. Next, the photoconductive layer 4 composed mainly of amorphous silicon with a thickness of, for example, 20-30 µm, is formed on the first middle layer 3 under the membrane-formation conditions shown in Table 3 , wherein this photoconductive layer 4 is formed such that the concentration of boron is not uniform therethrough from the bottom to the top of the layer by changing the B₂H₆ flow rate from 0.12 sccm to 0 sccm either continuously or in a stepwise fashion. Next, the second middle layer 5 composed mainly of amorphous silicon with a thickness, for example, 1.5 µm is formed on the photoconductive layer 4 under the membrane-formation conditions shown in Table 4 , wherein this second middle layer 5 is formed such that the concentrations of nitrogen and boron are not be uniform therethrough from the bottom to the top of the layer by changing the NH₃ flow rate from 0 sccm to 12 sccm and the B₂H₆ flow rate from 0 sccm to 50 sccm either continuously or in a stepwise fashion. Next, the surface layer 6 composed of amorphous silicon nitride with a thickness of, for example, 0.15 µm, is formed on the second middle layer 5 under the membrane-formation conditions shown in Table 5 . Examples of the distribution of the concentrations of nitrogen and boron in the different layers of a photoreceptor for electrophotography constructed as described above are shown in Figures 2(a)-2(c) , wherein the ordinate gives the distance from the substrate 1 , and the abscissa gives the concentrations of nitrogen and boron. The solid line gives the concentration of nitrogen to be doped. The concentration is indicated with the order of a few percents by the atomic ratio of N to Si . The broken line gives the concentration of boron to be doped. The concentration is indicated with the order of ppm by the atomic ratio of B to Si . Figure 2(a) indicates that the concentrations of nitrogen and boron in the first middle layer 3 are both decreased continuously toward the direction of the surface, that the concentration of boron in the photoconductive layer 4 is decreased continuously toward the direction of the surface, and that the nitrogen and boron concentrations of the second middle layer 5 are increased continuously toward the direction of the surface. Figure 2(b) is different from Figure 2(a) in that the concentration of boron is changed in photoconductive layer 4 stepwise. Figure 2(c) is different from Figure 2(a) in that the nitrogen concentration of the first and second middle layers 3 and 5 is changed in one place stepwise, and the boron concentration of the photoconductive layer 4 is changed stepwise, as well. The photoreceptor for electrophotography produced by the above-mentioned process was then incorporated into a copying machine which was already in practical use. The resulting image was excellent in contrast, resolution, and tone reproduction compared to an image produced by conventional photoreceptors for electrophotography. Moreover, the defects of blurring and white patches of the image hardly arose. Such satisfactory results have not been obtained by conventional photoreceptors for electrophotography. In particular, the contrast of an image resulting from the photoreceptor for electrophotography of this invention was excellent compared to that of an image resulting from conventional photoreceptors. That is, the photoreceptor of this invention having a photoconductive layer with a changing boron concentration attained excellent contrast of images compared to conventional photoreceptors having a photoconductive layer with a uniform boron concentration. Moreover, the photoreceptor for electrophotography of this invention which has changing concentrations of nitrogen and boron from the bottom to the top of the layer was much improved in terms of image defects compared to conventional photoreceptors for electrophotography in which the first and second middle layers are not provided, or even compared to photoreceptors having the first and second middle layers with uniform concentrations of nitrogen and boron from the bottom to the top of the layer. Thus, the existence of middle layers with a varied distribution of concentrations is important to prevent image defects. The photoreceptor for electrophotography of this invention was studied in a copy test to make 300,000 copies using an actual copy machine. Even after 300,000 copies were made, an excellent quality image which was equal to that at the early phase was obtained. However, in a copy test of a conventional photoreceptor for electrophotography without a surface layer and a bottom layer, a number of image defects (including a lowering of contrast, blurring, and white patches) appeared at an early stage, after 10,000 copies were made. Thus, the provison of a surface layer and a bottom layer having great optical bandgap achieves good results. The above-mentioned example discloses a photoreceptor in which nitrogen is contained in the first and second middle layers 3 and 5 , the bottom layer 2 , and the surface layer 6 , but it is not limited thereto. Each of the layers can be composed of amorphous silicon carbide containing carbon. The above-mentioned example discloses the formation of each of the layers using a glow discharge decomposition technique, but it is not limited thereto. This invention is, of course, applicable to a photoreceptor for electrophotography which is produced using a membrane-formation method such as sputtering, etc.

Claims: A photoreceptor for electrophotography comprising an electrically conductive substrate (1), a bottom layer (2), a photoconductive layer (4) composed mainly of amorphous silicon, and a surface layer (6), in that order, both the bottom and surface layers (2, 6) having a greater energy bandgap than said photoconductive layer (4), and comprising furthermore a first middle layer (3) disposed between said bottom layer (2) and the photoconductive layer(4), and a second middle layer (5) disposed between the photoconductive layer (4) and said surface layer (6), both the first and second middle layers (3, 5) being composed mainly of amorphous silicon, characterised in that the bottom layer (2) and the surface layer (6) contain either nitrogen or carbon, the photoconductive layer (4)and the first and the second middle layers (3, 5) contain boron, the concentration of which varies through each of said three layers (3, 4, 5), the first and second middle layers (3, 5) further contain nitrogen or carbon according to whether respectively nitrogen or carbon is contained in the surface layer (6) and the bottom layer (2), and the concentrations of nitrogen or carbon respectively increase from those surfaces of the first and second middle layers (3, 5) which are in contact with the photoconductive layer (4) towards those surfaces of the first and second middle layers (3, 5) which are in contact with the bottom and surface layers (2, 6) respectively. A photoreceptor as claimed in Claim 1, wherein said surface layer and said bottom layer are composed of amorphous silicon nitride or amorphous silicon carbide.

Inventors: EHARA, SHAW, HAYAKAWA, TAKASHI, IMADA, EIJI, KOJIMA, YOSHIMI, MATSUYAMA, TOSHIRO, NARIKAWA, SHIRO, NOJIMA, HIDEO
Applicants: SHARP KABUSHIKI KAISHA
Application year: 1986
Main classification: G03G5
IPC codes: G03G5