PHOSPHAZENE BASED FUNCTIONAL FLUID COMPOSITIONS

Abstract: A functional fluid composition is provided which comprises a plurality of different phosphazene compounds of the general formula (P=N) n (R) a (R') b (R'') c (R''') d wherein R is at least one alkoxy moiety described by the general formula -OCH₂(CF₂) y X, with X being hydrogen or fluorine and y being equal to 1 to about 10; R', R'' and R''' are different aryloxy moieties, each of R', R'' and R''' being selected from the group consisting of phenoxy, alkoxy phenoxys, alkyl phenoxys, chlorinated phenoxys, fluorinated phenoxys, aryl phenoxys, phenoxy phenoxys, fluoroalkyl phenoxys, fluoroalkoxy phenoxys, chlorinated phenoxy phenoxys, fluorinated phenoxy phenoxys and mixtures thereof; n is equal to 3 to about 4; for each of said phosphazene compounds, each of a, b, c and d is equal to or greater than zero such that the sum a+b+c+d is equal to 2n; and for the composition as a whole, the average value of each of a, b, c and d is greater than 0.

Description: This invention relates to novel cyclic phosphazenes and phosphazene based functional fluid compositions. A variety of phosphazene compositions and methods of preparation are known in the art. U.S. Patent No. 3,291,865 discloses non-flammable, hydroly­ tically stable phosphazene compositions for use as hydrau­ lic fluids, lubricants and additives. These phosphazenes are substituted by an aryloxy and a polyfluoroalkoxy substituent, and are synthesized by forming the alkali metal salt of the fluorinated alkanol followed by reaction of the salt and a salt of a phenol with a phosphonitrilic chloride. The alkoxy substituent may be any C₂ to C₂₁ poly­ fluoroalkoxy substituent. Examples of polyfluoro alcohols useful in providing this substituent include 1,1,3-tri-H-­ tetrafluoropropyl alcohol, 1,1,5-tri-H-octofluoropentyl alcohol, 1,1,7-tri-H-dodecafluoroheptyl alcohol, 1,1-di-H-­ trifluoroethyl alcohol, 1,1-di-H-heptaflurobutyl alcohol, 1,1-di-H-pentadecafluorooctyl alcohol and mixtures thereof. The aryloxy substituent may be derived from any of a variety of phenolic compounds, including monohydroxy phenols such as phenol and naphthol, phenoxyphenols, alkoxy-substituted phenols, alkyl-substituted phenols, aryl-substituted phenols, halogen-substituted phenols, halogen-alkyl-substituted phenols, and halogen-alkoxy-sub­ stituted phenols. Only phosphazene based compositions with one type of aryloxy substituent are exemplified. Similar phosphazene based compositions are described in the arti­ cles "Fluoroalkyl Phosphonitrilates: A New Class of Potential Fire-Resistant Hydraulic Fluids and Lubricants", Resistant Hydraulic Fluids and Lubricants", H. Lederle, E. Kober and G. Ottmann, Journal of Chemical and Engineer­ ing Data, Volume 11, No. 2, April 1966; and "Fluoroalkyl Phosphonitrilates: A New Class of Potential Fire-Resistant Hydraulic Fluids and Lubricants", E. Kober, H. Lederle and G. Ottmann, ASLE Transactions 7, 389-397 (1964). Polyfluoroalkoxy-substituted phosphazenes are disclosed in U.S. Patent No. 3,304,350 . Examples of useful polyfluoro alcohols include 1,1-di-H-trifluoroethyl alcohol, 1,1-di-H-pentafluoropropyl alcohol, 1,1-di-H-hepta­ fluorobutyl alcohol, 1,1-di-H-pentadecafluorooctyl alcohol, 1,1,3-tri-H-tetrafluoropropyl alcohol and 1,1,5-tri-H-octa­ fluoropentyl alcohol. A variety of other phosphazene composi­ tions are known in the art. U.S. Patents No. 3,370,020, 3,505,087, 4,081,593, 4,018,967, 4,110,421, 4,157,425 and 4,116,891, U.S. published patent application B 369,221 and U.S. Patents No. 3,990,900 and 3,545,942 disclose phosphazenes which may be substituted by a variety of alkoxy, alkenyloxy, arylalkoxy or aryloxy groups. However, many known phosphazene based compositions, such as those discussed above, have limitations which make them unsuitable for many functional fluid applications. A functional fluid composition usually must demon­ strate acceptable characteristics with regard to at least three properties; (1) fire resistance, (2) low temperature fluidity, and (3) compatibility with seal compositions. Failure of a functional fluid with respect to any of these properties may have serious consequences under the conditions of use. In 1953 and 1954 the U.S. aircraft carriers "Leyte" and "Bennington", respectively, were heavily damaged due in part to explosions caused by flammable hydraulic fluids. Consequently, fire resistance is a critical characteristic for military, industrial or consumer applications. Unfortunately, adequate fire resistance is lacking for many phosphazene based compositions, particularly those wherein the functional groups are moieties which include unhalogenated, relatively large alkyl substituents. However, phosphazene based compositions which exhibit good flame retardancy may also be solids under most conditions of use. This may make them unsuitable for certain applica­ tions, such as hydraulic fluids and lubricants, wherein liquidity may be required. Even if a phosphazene composition initially is a homogenous liquid, many phosphazene based compositions tend to completely or partially solidify or to separate into different phases after standing for a period of time. This tendency is particularly problematic for low temperature applications, such as outdoor hydraulic systems, wherein the functional fluid may be exposed to very low temperatures for prolonged periods of time. Such a tendency to solidify or undergo phase separation may make a composition unsuitable for certain uses, such as functional fluids in sealed hydraulic systems, wherein monitoring of the state of the phosphazene is impossible and replacement is impracti­ cable. Although certain phosphazene based compositions may remain liquid for a relatively long period of time, this liquidity may be due to impurities present in the composition, rather than to the characteristics of the composition per se. These impurities may cause degradation of the phosphazene compounds over a period of time or may corrode the apparatus with which the composition comes in contact, thereby contri­ buting to failure of the system in which the composition is used. Although certain phosphazene based fluids, such as those wherein the phosphazenes are functionalized by fluori­ nated phenoxy and/or fluorinated alkoxy moieties, may exhibit acceptable fire resistance, these compositions may be incompa­ tible with elastomers and other materials used to form seals in hydraulic and other functional systems. Such incompatabi­ lity may cause the seals to swell or shrink excessively, thereby causing system failure. Price and supply are also considerations. Although a variety of alkoxy and aryloxy compounds may be used to form cyclophosphazene ester compositions, these compounds vary widely in cost and availability. It is therefore advantageous to be able to use relatively low cost and readily obtainable materials to synthesize a phosphazene based functional fluid composition having good fire resistance, low temperature fluidity and elastomer compatibility. The present invention is a functional fluid composition comprising a plurality of different phosphazene compounds of the general formula: (P=N) n (R) a (R') b (R'') c (R''') d wherein R is at least one alkoxy moiety described by the general formula: -OCH₂(CF₂) y X, with X being hydrogen or fluorine and y being equal to 1 to about 10; R', R'' and R''' are different aryloxy moieties, each of R', R'' and R''' being selected from the group consisting of phenoxy, alkoxy phenoxys, alkyl phenoxys, chlorinated phenoxys, fluorinated phenoxys, aryl phenoxys, phenoxy phenoxys, fluoroalkyl phenoxys, fluoro­ alkoxy phenoxys, chlorinated phenoxy phenoxys, fluorinated phenoxy phenoxys, and mixtures thereof; n is equal to 3 to about 4; for each of said phosphazene compounds, each of a, b, c and d is equal to or greater than 0 such that the sum a + b + c + d is equal to 2n, and; for the composition as a whole, the average value of each of a, b, c and d is greater than zero. The present ivention also includes the product obtained by the process comprising reacting a dichlorophosphazene compound, having 3 to about 4 phosphazene units, with (a) at least one alkanol reactant generally described by the formula: HOCH₂(CF₂) y X, with X being hydrogen or fluorine and y being equal to 1 to about 10, and (b) at least three different phenolic reactants selected from the group consisting of phenol, alkoxy phenols, alkyl phenols, chlorinated phenols, fluorinated phenols, aryl phenols, phenoxy phenols, fluoro­ alkyl phenols, fluoroalkoxy phenols, chlorinated phenoxy phenols, fluorinated phenoxy phenols, and mixtures thereof, said reaction occurring in a medium comprising a mixture of water, a base, a water-immiscible solvent and a phase-transfer catalyst. The present invention is a functional fluid compo­ sition comprising a plurality of different phosphazene compounds of the general formula: (P=N) n (R) a (R') b (R'') c (R''') d . Each of these compounds includes a cyclic sub­ strate of 3 to about 4 phosphazene units [-P=N-]. The substi­ tuents R, R', R'' and R''' are all organic moieties esterified to the phosphazene substrate, i.e. bonded to phosphorus through oxygen. The phosphazene may be a pentameric, tetrame­ ric or trimeric cyclic compound. However, cyclic trimeric and tetrameric phosphazenes, wherein n is 3 or 4, are preferred. Mixtures of trimeric and tetrameric phosphazenes may also be used; however, a predominance of cyclic trimeric phosphazenes is most preferred. According to the present invention, in each of the phosphazene compounds R is at least one alkoxy moiety which may be described by the general formula: -OCH₂-(CF₂) y X. In this formula X may be hydrogen or fluorine, such as in 2,2-difluoroethoxy or 2,2,2-trifluoroethoxy, respectively. Fluorine is preferred. Further, y may be equal to an integer from 1 to about 10, such as in fluorinated ethoxy, propoxy, butoxy, pentoxy, heptoxy, nonoxy and undecoxy moieties. This fluorinated alkoxy moiety is usually derived from the corres­ ponding fluorinated alkanol, e.g. ethoxy from ethanol, propoxy from propanol, etc. Examples of suitable alkanols include 1,1,9-tri-H-hexadecafluorononyl alcohol; 1,1,11-tri-H-eicosa­ fluoroundecyl alcohol; 1,1-di-H-pentadecafluorooctyl alcohol; 1,1-di-H-pentafluoropropyl alcohol; 1,1,7-tri-H-dodecafluoro­ heptyl alcohol; 1,1,2-tri-H-difluoroethyl alcohol (2,2-difluo­ roethanol); and 1,1-di-H-trifluoroethyl alcohol (2,2,2-tri­ fluoroethanol). Preferably, however, y is equal to 1 to about 3, such as in ethyl, propyl and butyl fluorinated alcohols, as a substantial proportion of longer alkoxy moieties may lead to a significant increase in viscosity. Trifluoroethanol is most preferred. Although preparation of the phosphazene composition may be simplified by the halogenated alkoxy moiety being homogenous, a mixture of different halogenated alkoxy moie­ ties, consistent with the above formula, may be included, such as mixtures of 2,2-difluoroethoxy and 2,2,3,3,3-pentafluoro­ propoxy. When a mixture of different fluorinated alkoxy moieties is included, it is preferred that at least 75% by weight of the alkoxy moieties, based upon the combined weight of all of the alkoxy moieties present in all of the phospha­ zene compounds that together make up the functional fluid composition, be trifluoroethoxy. More preferably, this amount should be at least 90% by weight. The phosphazene composition also includes at least three different aryloxy groups, represented by R', R'' and R''' in the formula above, which are esterified to phosphazene compounds in the composition. These aryloxy groups differ from each other by at least one of (i) the presence or absence of substitution to the aryl ring, (ii) the position of substitution on the aryl ring, (iii) the identity of the substituent(s), and (iv) the number of substituents. Thus, aryloxy groups which are isomers of each other are considered to be distinct for the purposes of the present invention. Consistent with this distinction between isomers, the aryloxy substituents R', R'' and R''' are selected from the group consisting of phenoxy, alkoxy phenoxys such as m-methoxyphenoxy, m,p-dimethoxyphenoxy, p-methoxyphenoxy, m-ethoxyphenoxy and p-propoxyphenoxy as well as other mono, di and trialkoxy phenoxys; alkyl phenoxys such as m-propylphenoxy, p-tert-butylphenoxy, 3,5-dimethylphenoxy, 2,4-dimethylphenoxy, 2,3-dimethyl-phenoxy, 2,4,6-tri-methylphenoxy, 3,4-dimethyl­ phenoxy, p-ethylphenoxy, m-ethylphenoxy, m-isobutylphenoxy, o-ethylphenoxy, p-methylphenoxy and m-methylphenoxy as well as other mono, di and trialkyl phenoxys; mono, di, tri, tetra and penta chlorinated or fluorinated phenoxys such as p-chlorophenoxy, m-chlorophenoxy, 3,5-dichloro­ phenoxy, 2,4,6-trichlorophenoxy, 2,3,4,5-tetrachlorophenoxy, pentafluorophenoxy and p-fluorophenoxy; aryl phenoxys such as p-phenylphenoxy, m-phenylphenoxy and (methylphenyl)phenoxys; phenoxy phenoxys such as p-phenoxyphenoxy; mono, di and tri-fluoroalkyl phenoxys such as p-(difluoromethyl)phenoxy, m-(trifluoromethyl)-phenoxy, and m,p-di(trifluoromethyl)phe­ noxy; mono, di and tri-fluoroalkoxy phenoxys such as p-(di­ fluoromethoxy)phenoxys and m-(2,2,2-trifluoroethoxy)phenoxys; mono, di, tri, tetra and pentachlorinated or fluorinated phenoxy phenoxys such as 4-(3,4-difluorophenoxy)phenoxy and 4-(3,4-dichlorophenoxy)phenoxy. Preferably, at least 80% by weight of R', R'' and R''', based on the combined weight of R', R'' and R''' for all of the phosphazene compounds taken together, are selected from the group consisting of phenoxy, alkyl phenoxys, alkoxy phenoxys, and mixtures thereof. As fire resistance is generally inversely related to the length of alkyl groups present in the aryloxy moiety, it is more preferred that at least 90% by weight of the aryloxy moieties be selected from the group consisting of phenoxy, methylphenoxys, ethylphenoxys, dimethylphenoxys and mixtures thereof. It is more preferred that at least 80% by weight of the aryloxy moieties be phenoxy, m-methylphenoxy and p-methylphenoxy. Amounts of at least 90% by weight phenoxy, m-methylphenoxy and p-methylphenoxy are most preferred. Any of R', R'' and R''' may also be selected from mixtures of the above aryloxy substituents, such as when R' is phenoxy, R'' is a mixture of m-methylphenoxy and p-methylphenoxy, and R''' is p-ethylphenoxy. Thus tne invention also includes the embodiment wherein the functional fluid composition comprises as many as four, five, six or more of the above aryloxy groups esterified to phosphazene com­ pounds. The phosphazene compounds of the functional fluid composition may be synthesized by the esterification of dichlorophosphazenes. However, incomplete substitution may result in the presence of residual chloride in the phosphazene compound, thereby making the compound susceptible to hydroly­ tic degradation. Although the functional fluid of the present invention may contain small quantities, on the order of a few tenths of a percent by weight, of incompletely substituted phosphazenes without suffering from deleterious effects, the present invention is directed to phosphazene compounds which are fully substituted, e.g. wherein the sum of the number of aryloxy and fluorinated alkoxy substituents, a + b + c + d, is equal to 2n. As long as the sum a + b + c + d for each phospha­ zene compound is equal to 2n, the individual value of each of a, b, c and d may be greater than or equal to zero. Thus, the functional fluid composition may contain one or more phos­ phazene compounds which are substituted by only one, two or three of R, R', R'' and R'''. For the functional fluid composition as a whole, an average value may be defined for each of the subscripts a, b, c and d. This average value is the sum of each subscript for the phosphazene compounds in the functional fluid composition, divided by the total number of different phosphazene compounds in the composition consistent with the above formula. For example, for a functional fluid composi­ tion comprising three different phosphazene compounds (P=N)₃R₂R'₁R'''₃, (P=N)₃ R'₄ R''₂, and (P=N)₃R₂R'₁ R''₂ R'''₁, the average value of a is (2 + 2)/3 or approxi­ mately 1.3, the average value of b is (1 + 4 + 1)/3 or 2, the average value of c is (2 + 2)/3 or approximately 1.3, and the average value of d is (3 + 1)/3 or approximately 1.3. While the individual value of a, b, c and d in each phosphazene compound may be greater than or equal to zero, for the functional fluid composition as a whole, the average value of each of these subscripts must be greater than zero, e.g. each of R, R', R'' and R''' must be present in at least one phosphazene compound of the func­ tional fluid composition. It should further be noted that the present inven­ tion is also directed to a novel phosphazene composition of the general formula (P=N) n (R) a (R') b (R'') c (R''') d , with R, R', R'' and R''' as discussed above, wherein each of a, b, c and d is greater than zero, i.e. at least one fluorinated alkoxy substituent and at least three different aryloxy substituents are present in the same phosphazene compound. Although the ratio of alkoxy to aryloxy substitu­ ents may vary substantially from phosphazene compound to phosphazene compound, an alkoxy:aryloxy ratio may be defined based on the number of alkoxy and aryloxy substi­ tuent groups present in the functional fluid composition as a whole. In the preferred embodiment, the ratio of the average number of halogenated alkoxy groups to aryloxy groups, e.g. the ratio of the average value of a to the sum of the average values of b, c and d, is about 0.5:1 to about 8:1. More preferably, this ratio is about 0.8:1 to about 5:1. Ratios of about 1.3:1 to about 1.9:1 are most pre­ ferred. Preferably, each of the phosphazene compositions in the functional fluid is present in an amount which consti­ tutes less than 70% by weight of the total phosphazene content of the composition, as a more even distribution of phosphazene compounds has been observed to assist in main­ taining prolonged fluidity at low temperatures. For ex­ ample, two phosphazene compounds may be present in ratios by weight of 31:69, 65:35, 50:50, or 57:43. However, an increased tendency toward low temperature fluidity has been observed when more than two different phosphazene compounds are present in the composition. Consistent with this observation, although the functional fluid may comprise two or more different phosphazene compounds, in the pre­ ferred embodiment the functional fluid composition includes at least three different phosphazene compounds. Althougn these compounds may be present in various amounts, it is preferred that each compound constitute less than 50% by weight of the total phosphazene content of the composition. For example, in a functional fluid containing three differ­ ent phosphazene compounds these compounds may be present in ratios by weight of 36:48:16 or 8:49:43. More preferably, however, at least two of the phosphazene compounds each constitute less than 35% by weight of the total phosphazene content of the composition, such as in distributions of 34:48:18, 34:32:34, 28:24:48, etc. The phosphanzene compounds useful in the present invention may be synthesized using processes known in the art, such as the alkali metal salt method of U.S. 3,291,865 or U.S. 3,370,020 or the phase transfer method of EP-A-145 002 the disclosure of which is herein incorporated by reference. Example 9 demonstrates preparation of one embodiment of the functional fluid composition of the present invention by using the alkali metal salt method. However, the phase transfer method of synthesis is preferred as this method yields a variety of different phosphazene compounds, wherein the aryloxy and alkoxy substituents are present in different proportions, using a relatively simple and cost effective procedure. The bulk phase transfer method, wherein the dichlorophosphazene substrate is contacted with the phenolic reactants and the fluorinated alkanol reactant at the same time, is particu­ larly preferred as this method tends to yield a broader, more evenly distributed product mix. Consequently, the preferred embodiment of the present invention may be described as the product of the process comprising reacting a dichlorophosphazene compound with (a) at least one alkanol reactant described by the general formula: HOCH₂(CF₂) y X, where X is hydrogen or fluorine and y is equal to 1 to about 10, and (b) at least three differ­ ent phenolic reactants selected from the group consisting of phenol, alkoxy phenols, alkyl phenols, chlorinated phenols, fluorinated phenols, aryl phenols, phenoxy phenols, fluoro­ alkyl phenols, fluoroalkoxy phenols, chlorinated phenoxy phenols, fluorinated phenoxy phenols and mixtures thereof, said reaction occurring in a medium comprising a mixture of water, a base, a water-immiscible solvent and a phase-trans­ fer catalyst. The fluorinated alkanol reactant and the phenolic reactants correspond, of course, to the fluorinated alkoxy and the aryloxy moieties discussed above. The phase transfer catalyst preferably is an alkyl, aryl or aralkyl ammonium or phosphonium salt. More prefer­ ably, as disclosed in EP-A-145 002, incorporated herein by reference, the phase-transfer catalyst is one having the structure (R iv )₄AX, with the (R iv )'s being the same or different alkyl, aryl or aralkyl group, A being nitrogen or phosphorus, and X being halogen, OH, HSO₄, NO₃, BH₄, IO₄, ClO₄, CN, N₃, OCH₃, tosylate or benzoate. Most preferably, the (R iv )'s are the same or different alkyl group, and X is chlorine or bromine. In order to minimize the presence of any residual phosphazene-bound chlorine in the product, and to encourage complete substitution, it is preferred that the molar ratio of alkanol reactant and phenolic reactants, combined, to phosphazene units be at least 2:1. Consequently, when the dichlorophosphazene compound is a trimeric phosphazene, the molar ratio of the combination of alkanol reactant and phenolic reactants to the dichlorophosphazene compound should be at least 6:1. Although a molar excess of alkanol and phenolic reactants may be present in the reaction mixture, this excess preferably is minimized due to cost considerations. As a result, preferred molar ratios of alkanol and phenolic reactants combined to phosphazene units are about 2.5:1 or less. It is preferred that the molar ratio of alkanol reactant to phenolic reactants be about 5:1 to about 0.8:1, with ratios of about 4:3 to about 2:1 being most preferred. Due to the relatively low cost of phenol in relation to the cost of other phenolic feedstocks, it is further preferred that about 40% to about 60% by weight of the phenolic reactants be phenol. In the presentation of specific embodiments below, the term "PTC bulk" indicates that a particular composi­ tion was synthesized by a catalyzed phase transfer process wherein the dichlorophosphazene feedstock is reacted with all of the substituent reagents at the same time, similar to the procedures described for Example 1 and Comparative Example C13, with post-reaction of the initial product with appropriate alkali metal aryloxy and/or fluorinated alkoxy salts to drive the reaction to completion. The term "PTC sequential" indicates that a particu­ lar composition was synthesized by means of a phase transfer process, similar to that described in Comparative Example C18, wherein the aryloxy reagents are allowed to react with the dichlorophosphazene feedstock for a period of time before contact with the fluorinated alkoxy reagent. Simi­ larly, "Na salt, sequential" indicates a process according to the alkali metal salt method, similar to that described for Example 9, wherein the aryloxy reagents are allowed to react with the dichlorophosphazene feedstock for a period of time before addition of the fluorinated alkoxy reagent. In Table I, and for the subsequent Examples, viscosity was measured according to ASTM D-445; Pour Point was mea­ sured according to ASTM D-97; Acid Number relates to Fed. Test Method 5105.3 Fed-Std-791a; Flash Point was measured by ASTM D-92 (micro-cup method); "AIT" refers to "autogenous ignition temperature", i.e. the temperature at which the composition spontaneously ignites at a specific pressure, according to ASTM G-72; The "Emulsion Test" reported in Table I refers to ASTM Standard D1401; "Foaming Tendency" refers to ASTM Standard D892; "Elastomer Compatibility" refers to Federal Test Method 3603, Fed-Std-791; and "Hydro­ lytic Stability" and CFR Compression Ratio refer to Military Specification Mil-H-19457C(SH), Par. 4.5.2. Example 1 exemplifies the preparation of the product of the present invention by a PTC bulk process, with post reaction with potassium phenoxide. Example 1 An aqueous solution containing 217.2g of 2,2,2-trifluo­ roethanol, 63.5g phenol 73.0 g of a mixture of m-methyl­ phenol and p-methylphenol, 223.5g KOH pellets and 365 mL of water is added drop-wise to a solution containing 200g of purified hexachlorocyclotriphosphazene containing 2% or less of octachlorocyclotetra phosphazene, 67g of tetrabutyl ammonium bromide and 888 mL of chlorobenzene to form an organic phase and an aqueous phase. The organic phase was stirred and maintained at 25-30°C during the addition period. After addition of the aqueous solution, the organic phase was heated at 40°C for approximately 4-5 hours, followed by separation of the organic phase and aqueous phase and the extraction of the organic phase with dilute H₂SO₄ to remove the tetrabutyl ammonium halide catalyst. Potassium phenoxide (26g) was added to the organic phase and the resulting solution refluxed for 5 hours. The organic phase was then washed sequentially with a dilute base and a dilute acid, after which the organic phase was passed through a bed of activated alumina to remove residual catalyst. After removal of the chlorobenzene solvent by evaporation under reduced pressure there remained 303g of a clear, colorless oil. This oil was analyzed as containing about 0.15% by weight residual chlorine and as consituting an essentially pure mixture of phosphazene compounds of the average composition: P₃N₃(OCH₂CF₃) 3.6 (OC₆H₅) 1.2 (OC₆H₄CH₃) 1.2 This average composition was confirmed by elemental analy­ sis, gas chromatography and proton magnetic resonance. The physical properties of this composition are reported below in Table I. The distribution of phos­ phazene compounds in 1his composition, as indicated by gas chromatographic analysis, are reported below in Table II. These structures were confirmed by high resolution mass spectroscopy. In reporting the composition of the components in Table II and in subsequent tables, the aryloxy compo­ nents, e.g., for Example 1, phenoxy, m-methylphenoxy and p-methylphenoxy, are combined together and reported as the number of aryloxy components, "OAr". Samples of the composition of Example 1 were stored for one year at -20°C. During this time these samples remained liquid, with no evidence of crystallization or phase separation. Example 2 The proportions and procedure of Example 1 were scaled up to yield approximately 30 gal. of an essen­ tially pure mixture of phosphazene compounds. As indicated by the physical properties reported below in Table III, this composition exhibited physical properties similar to those reported for the composition of Example 1, with the composi­ tion of Example 2 showig an improved CFR Compression Ratio of 50:1. Examples 3-5 Compositions containing various ratios of trifluoro­ ethoxy groups to phenoxy, m-methylphenoxy and p-methylphen­ oxy were prepared from 2,2,2-trifluoroethanol, phenol and a mixture of m-methylphenol and p-methylphenol, according to the procedure outlined above for Example 1. By adjusting the proportion of trifluoroethanol to aryloxy compounds, various ratios of trifluoroethoxy (TFE) to aryloxy (ArO) groups may be obtained in the phosphazene product. The ratios of these groups in the product and the corresponding viscosities and pour points are indicated below in Table IV. Another embodiment of the invention, containing a mixture of trifluoroethoxy, phenoxy, m-methylphenoxy and p-methylphenoxy substituents and prepared by a PTC bulk process with post-reaction with potassium phenoxide, is exemplified in Example 6. Example 6 An aqueous solution containing 984g 2,2,2-trifluoro­ ethanol, 354g phenol, 407g of a mixture of m-methylphenol and p-methylphenol, 1138g KOH pellets and 1835 mL water was added drop-wise to a solution containing 1005g of purified hexachlorocyclotriphosphazene (98% trimer, 2% tetramer), 333.5g of tetrabutyl ammonium bromide and 4000 mL of chloro­ benzene to form an organic phase and an inorganic phase. The organic phase was stirred and maintained at 25-30°C during the addition period, then heated to 40°C for four hours. The organic phase was separated and extracted with 5% aqueous HCl to remove the catalyst. Potassium phenoxide (138g) was added to the organic phase, and the solution refluxed for five hours. The organic phase was sequentially washed with a dilute base and a dilute acid. The solvent was removed by evaporation under reduced pressure, 90g of anhydrous calcium carbonate was added to the residue and the mixture vacuum distilled. This resulted in 1089g of liquid distillate which had a pour point of -23°C, a viscosity at 40°C of 51.3 cPs and an acid number of 0.1. A sample of this distillate had not begun to crystallize or undergo phase separation after storage for one year at -24°C. Comparative Example C7 The PTC bulk procedure of Example 6 was repeated, except that pure m-methylphenol was substituted for the mixture of m-methylphenol and p-methylphenol used in Example 6. This resulted in a fluid product which was completely crystallized after storage at -24°C for several days. Example 8 exemplifies the preparation of a func­ tional fluid composition of the present invention using a tetrameric phosphazene feedstock. Example 8 An aqueous solution containing 67.32g of trifluoroetha­ nol, 24.26g of a mixture of m-methylphenol and p-methylphe­ nol, 21.12g of phenol, 72.09g KOH pellets and 107 mL of water was added gradually to a solution containing 63.74g of purified octachlorocyclotetraphosphazene, 21.28g tetrabutyl ammonium bromide and 290 mL of chlorobenzene. The resulting mixture was reacted according to the conditions and proce­ dures described above in Example 6, except that the crude product was purified by the additional step of contacting it with activiated alumina. This resulted in 125g of product which was a colorless oil. This product had a viscosity at 40°C of 98.0 cPs and a pour point of -26°C. A viscosity and pour point of a fluid made of purified hexachlorocyclo­ triphosphazene, using the same stoichiometry, had a viscosi­ ty at 40°C of 56.3 cPs and a pour point of -21°C. Example 9 exemplifies preparation of an embodiment of the present invention by the alkali metal salt, sequen­ tial addition method. Example 9 Sodium metal (34.5g) was gradually added to a solution containing 103.5g phenol, 1,000 mL of tetrahydrofuran and 67.2g of a tar acid mixture of the following composition wherein "TM Phenol" indicates trimethylphenol and "C₃ Phenols" indicates propylphenols: The resulting mixture was refluxed for 15 hours. A solution of sodium trifluoroethoxide was prepared in a similar manner by adding 37.95g of sodium metal to 172.5g of 2,2,2-trifluoroethanol and 1,000 mL of tetrahydrofuran (THF). The solution of sodium aryloxides in tetrahydrofuran was added drop-wise to a solution containing 174g of puri­ fied hexachlorocyclotriphosphazene in one liter of THF and the resulting mixture heated at 60-65°C for five hours. The mixture was cooled to room temperature, and the solution of sodium trifluoroethoxide added in a drop-wise manner. This resulted in a slurry, which was refluxed for 20 hours, filtered to remove precipitated salts, and stripped of solvent by evaporation of the solvent under reduced pres­ sure. The residue was dissolved in a toluene/diethyl ether mixture, and washed sequentially with 5% HCl, 5% NaOH and 5% Na₂CO₃. After the removal of solvent, there remained 349g of a clear, yellow liquid. The physical properties of this liquid are indicated below in Table V. Samples of this composition had solidified by the end of 1 year's exposure to -24°C. However, other samples of this liquid remain fluid throughout storage at room temperature for a period of two years. Example 10 exemplifies a sodium salt sequential addition process utilizing only tar acids as the aryloxy reagent. Example 10 Sodium (32.2g, 1.40g-atom) was added over a 45 minute period at 20 to 36°C to 188.14g of a tar acid mixture of the same composition as used in Example 9 in 940 mL dry THF. The mixture was heated to 67°C for 3 hours. To 194.0g (1.94 mole) trifluoroethanol in 1060 mL dry THF was added 40.5g (1.76 g-atom) sodium in pieces over a 45 minute period, with cooling. The resulting mixture was heated to 67°C for 5 hours. The sodium tar acid solution was slowly added to a solution of 17.40g (0.50 mole) (PNCl₂)₃ in 1000 mL THF over a 1 hour period at 21 to 31°C. The mixture was heated to 59°C, cooled to 29°C and the sodium trifluoroethoxide solution added over a 1 hour period. The reaction was allowed to proceed overnight (18 hours) at 67°C. The resultant slurry was filtered, and the filtrate washed with 5% NaOH, 5% HCl, and with 5% NaHCO₃, dried over MgSO₄, filtered, and solvent and volatiles were removed at 84°C at 0.05 torr, leaving 303.7g (76.4% yield) of clear yellow liquid. This liquid was analyzed as having the distribution of phosphazene compounds shown in Table VI, and the properties shown in Table VIII. Comparative Example C11 The procedure of Example 10 was repeated, using 188.14g (1.54 mole) m-ethylphenol in place of the tar acid mixture. This resulted in 383.3g (96.3% yield) of a clear amber liquid. This liquid was analyzed as having the components indicated below in Table VII, and the proper­ ties indicated in Table VIII. Samples of this composition remained fluid after long standing at -20°C. However, samples of this composition had a High Pressure AIT of 225°C, which does not meet minimum High Pressure AIT stan­ dards of MIL-H-19457C. Comparative Example C12 The procedure of Example 10 was repeated using 188.14g (1.54 moles) p-ethylphenol in the place of the tar acid mixture. The product was a solid of the average composi­ tion: P₃N₃(OCH₂-CF₃) 3.2 (OC₆H₄-p-CH₂CH₃)- 2.8 . Comparative Example C13 exemplifies preparation of a phenoxy, trifluoroethoxy substituted phosphazene by a PTC bulk procedure. Comparative Example C13 Two samples were prepared using duplicate runs of the following procedure. A 500 ml flask with magnetic stirrer, thermometer, condenser, gas dispersion tube and addition funnel was charged with 14.1g (0.15 mole) phenol, 12.0g (0.15 mole) trifluoroethanol, 19.5g (0.30 mole) KOH pellets and 120 mL H₂O. The flask was purged with N₂ for 30 minutes. A 35°C solution of 17.4g (0.50 mole) cyclic (PNCl₂)₃ and 5.8g (0.018 mole) tetrabutylammonium bro­ mide in 100 mL chlorobenzene was added over a one hour period while the temperature rose from about 30 to about 47°C. The resulting mixture was heated at 70°C for 28 hours. During the last 6 hours an additional 3.0g trifluo­ roethanol, 1.4g phenol and 3.0g KOH were added. The product mixture was cooled, the aqueous phase removed, and the organic phase washed successively with 5% aqueous NaOH, 5% aqueous HCl and 5% aqueous NaHCO₃, dried over MgSO₄, filtered, and the solvent and volatiles removed. The products from the two duplicate runs were liquids nearly identical in physical properties, with an 88% product yield and were identified as having the average composi­ tion: P₃N₃(OCH₂CF₃)₃(OC₆H₅)₃. The physical properties of one of these liquids is indicated below in Table VIII. Both of these liquids partially crystallized on standing at 5°C. Comparative Example C14 When the PTC sequential preparation of the average composition P₃N₃(OCH₂CF₃)₃(OC₆H₅)₃ was performed using the same amounts of reagents as in Comparative Example C13, a crystalline product was obtained. Comparative Example C15 A composition of the average formula P₃N₃(OCH₂CF₃)- 3.25 ­ (OC₆H₅) 2.75 was prepared by a PTC bulk addition proce­ dure. This composition also partially crystallized at 5°C. Comparative Example C16 Three samples were also prepared using a sodium salt, sequential addition procedure. One sample, of average P₃N₃(OCH₂CF₃) 2.9 (OC₆H₅) 3.1 , was a crys­ talline solid at room temperature. A second sample, of average composition P₃N₃(OCH₂CF₂) 4.4 (OC₆H₅) 1.6 , partially crystallized on standing at room temperature, and completely crystallized while testing the pour point. The third sample partially crystallized on standing at room temperature, and was analyzed as having the properties indicated below in Table VIII. Comparative Example C17 Several trimeric phosphazene compositions were prepared from m-methylphenol and trifluoroethanol using a sodium salt, sequential addition procedure. The resulting composi­ tions on the average had trifluoroethoxy/aryloxy ratios of 4.3:1.7, 1:1, and 1.8:4.2. All three compositions solidi­ fied upon standing at room temperature. The properties of one of these compositions is indicated below in Table VIII. Comparative Example C18 exemplifies the preparation of a phosphazene composition according to a PTC sequen­ tial addition procedure, with post reaction with an aryl­ oxide. Comparative Example C18 A solution of 278.4g (0.80 mole) of (PNCl₂)₃ and 92.85g (0.29 mole) Bu₄NBr in 900 mL chlorobenzene was charged to a flask fitted with stirrer, thermometer, reflux condenser, nitrogen inlet and 1000 mL addition funnel. A mixture of 125.2g (1.92 mole) of KOH pellets, 112.4g (1.04 mole) m-methylphenol, 142.7g (0.94 mole) m-(trifluoromethyl) phenol and water to make a 1000 mL solution was added to the (PNCl₂)₃ solution over approximately one hour, at 18 to 29°C. After stirring for an additional hour at 20 to 29°C, the pH of the aqueous phase was 7.5. A mixture of 187.9g (2.88 mole) of KOH pellets, 288.0g (2.88 mole) trifluoro­ ethanol and water to make one liter of solution was added over the course of approximately one hour, at 20 to 28°C. The reaction mixture was heated to 40°C for 1.5 hours, allowed to stand at room temperature overnight and the phases separated. The organic phase was dried with MgSO₄ and filtered. A 10 mL portion of the filtrate was removed. The remainder of the filtrate was post-reacted with 0.40 mole of sodium-m-(trifluoromethyl)-phenoxide for one hour at 60°C. The product mixture was washed with 5% aqueous HCl and 5% aqueous NaHCO₃, dried with MgSO₄, and filtered. The crude product of this procedure was 597.1g (97.6% yield) of yellow liquid. A 523.4g portion of the crude product was distilled, collecting a 23.84g forecut and a 430.0g (82.2%) main fraction plus 62.5g of residue. The main fraction contained less than 0.05% residual chlorine. It was dissolved in toluene/ether and passed thru a column of ion exchange resin. The solvent was removed and the acid number found to be 0.13. The product was redissolved in 1/1 toulene/ether and washed with 5% aqueous NaCO₃, dried over MgSO₄ and filtered. Solvent and volatiles were removed, leaving a pale yellow liquid with an acid number of 0.04 mg KOH/g of fluid. A 369.2g portion of this material was redistilled, collecting a 332.9g main fraction of clear, colorless liquid. The physical properties of this liquid are indicated below in Table VIII. Samples of this composi­ tion remained fluid after prolonged standing at -20°C. However, this composition had a flash point of 271°C, which is below the minimum standard for MIL-H-19457C. Comparative Example C19 A composition was prepared by a PTC sequential addition procedure, utilizing phenol, m-methylphenol and trifluoro­ ethanol. This procedure resulted in a phosphazene based composition of the average composition: P₃N₃(OCH₂CF₃) 3.4 ­ (OC₆H₅) 1.3 (OC₆H₄-m-CH₃) 1.3 . The crude product obtained was divided into two portions, which were purified using different procedures. In the one procedure, the crude product was rewashed sequentially with 5% aqueous HCl, 5% NaOH and 5% aqueous NaHCO₃. After drying with MgSO₄, filtering and removing solvent, there remained 333.7g yellow liquid product having 0.13% total chloride and an acid number of 4.28. A 295.6g portion of the liquid was distilled, collecting a forecut of 13.7g, a main fraction of 252.1g of nearly colorless liquid, and 29.8g of residue. The main fraction had 0.11% Cl and an acid number of 0.20. It was dissolved in equal volumes of diethylether/toluene, washed with 5% aqueous Na₂CO₃ dried with MgSO₄, filtered and freed of solvents, leaving 237.5g of liquid having an acid number of 0.08. This liquid was redistilled, collecting a first fraction of 12.22g, a main fraction of 200.17g and a third fraction of 8.99g, leaving 2.58g of residue. The main fraction had an acid number of 0.02. On standing, this composition partially crystallized at room temperature. In the other purification procedure, the other half of the crude liquid product was passed through a column of an ion exchange resin to remove residual Bu₄NBr. The liquid was filtered and the solvents removed, leaving 327.2g of straw colored liquid containing 0.20% residual chloride and having an acid number of 2.62. A 293.87g portion of this material was distilled, collecting a 6.36g forecut, a 238.35g main fraction, and 25.5g third fraction, leaving 21.63g of residue. The main and third fractions contained some tributyl amine. They were combined and subjected to 0.05 torr on a rotary evaporator at 80°C for 2 hours, thereby removing approximately 35% of the remaining tributyl amine. The product was dissolved in 1/1 toluene/­ ether, washed with 5% aqueous HCl, and 5% aqueous Na₂CO₃, dried over MgSO₄, filtered and the solvents removed, leaving 258.7g of pale yellow liquid having an acid number of 0.24. A 247.6g portion of this material was redistilled, collecting a forecut of 10.04g and a main fraction of 225.82g leaving a 10.47g residue. The main fraction was a clear colorless liquid. Its properties are indicated below in Table VIII. It also crystallized on standing at -20°C. Comparative Examples C20, C21, C25; Examples 22-24 Several phosphazene based fluid compositions were synthesized. The compositions of Examples 22, 23 and 24 are various embodiments of the present invention. The phosphazene based compositions of Comparative Examples C20, C21 and C25 do not embody the present invention, but are provided as a basis for comparison. The average composition of the fluids for Examples 22-24 and Compar­ ative Examples C20, C21 and C25, as well as these fluids' physical characteristics and their method of preparation, are indicated below in Table IX. All of the compositions of Examples 22-24 and Compara­ tive Examples C20, C21 and C25 were liquid at -20°C. These examples have been presented only to demon­ strate operability and to provide a basis for comparing certain embodiments of the present invention with composi­ tions not included within the scope of the invention. The scope of the present invention, however, is not limited to the specific embodiments presented above, but includes equivalent embodiments and modifications as defined by the following claims:

Claims: 1. A functional fluid composition comprising a plurality of different phosphazene compounds of the general formula: (P=N)n (R)a (R')b (R'')c (R''')d wherein; R is at least one alkoxy moiety described by the general formula: -OCH₂(CF₂)yX, with X being hydrogen or fluorine and y being equal to 1 to about 10; R', R'' and R''' are different aryloxy moieties, each of R', R'' and R''' being selected from the group consisting of phenoxy, alkoxy phenoxys, alkyl phenoxys, chlorinated phenoxys, fluorinated phenoxys, aryl phenoxys, phenoxy phenoxys, fluoro alkyl phenoxys, fluoroalkoxy phenoxys, chlorinated phenoxy phenoxys, fluorinated phenoxy phenoxys and mixtures thereof; n is equal to 3 to about 4; for each of said phosphazene compounds, each of a, b, c and d is equal to or greater than zero such that the sum a+b+c+d is equal to 2n; and for the composition as a whole, the average value of each of a, b, c and d is greater than 0. 2. The functional fluid composition of claim 1 wherein the ratio of the average value of a, for the composition as a whole, to the sum of the average values of b, c and d, for the composition as a whole, is about 0.5:1 to about 8:1. 3. The functional fluid composition of claim 2 wherein the ratio is about 0.8:1 to about 5:1. 4. The functional fluid composition of claim 3 wherein the ratio is about 1.3:1 to about 1.9:1. 5. The functional fluid composition of claim 1 wherein each of said different phosphazene compounds is present in an amount less than 70% by weight of the total phosphazene content of said composition. 6. The functional fluid composition of claim 5 wherein said composition includes at least three of said different phosphazene compounds, each of said different phosphazene compounds being present in an amount less than 50% by weight of the total phosphazene content of said composition. 7. The functional fluid composition of claim 6 wherein at least two of said different phosphazene compounds are each present in an amount less than 35% by weight of the total phosphazene content of said composition. 8. The functional fluid composition of claim 1 wherein at least 90% by weight of the alkoxy moieties present in all of said phosphazene compounds combined are trifluoroethoxy. 9. The functional fluid composition of claim 1 wherein at least 80% by weight of the aryloxy moieties present in all of said phosphazene compounds combined are selected from the group consisting of phenoxy, alkyl phenoxys, and alkoxy phenoxys. 10. The functional fluid composition of claim 9 wherein at least 90% by weight of the aryloxy moieties are selected from the group consisting of phenoxy, methyl­ phenoxys, ethylphenoxys, dimethylphenoxys and mixtures thereof. 11. The functional fluid composition of claim 10 wherein at least 80% by weight of said aryloxy moieties are selected from the group consisting of phenoxy, m-methyl­ phenoxy and p-methylphenoxy. 12. The functional fluid composition of claim 11 wherein at least 90% by weight of said aryloxy moieties are selected from the group consisting of phenoxy, m-methyl­ phenoxy and p-methylphenoxy. 13. The product of the process comprising reacting a dichlorophosphazene compound, having 3 to about 4 phospha­ zene units, with (a) at least one alkanol reactant generally described by the formula HOCH₂(CF₂)yX, with X being hydrogen or fluorine and y being equal to 1 to about 10, and (b) at least three different phenolic reactants selected from the group consisting of phenol, alkoxy phenols, alkyl phenols, chlorinated phenols, fluorinated phenols, aryl phenols, phenoxy phenols, fluoroalkyl phenols, fluoroalkoxy phenols, chlorinated phenoxy phenols, fluorinated phenoxy phenols and mixtures thereof, said reaction occurring in a medium comprising a mixture of water, a base, a water-immis­ cible solvent and a phase-transfer catalyst. 14. The product of claim 13 wherein the phase transfer catalyst is an alkyl, aryl or aralkyl ammonium or phospho­ nium salt. 15. The product of claim 14 wherein the phase transfer catalyst is one having the structure: (Riv)₄AX wherein the (Riv)'s are the same or different alkyl, aryl or aralkyl group, A is nitrogen or phosphorus, and X is halogen, OH, HSO₄, NO₃, BH₄, IO₄, ClO₄, CN, N₃, OCH₃, tosylate or benzoate. 16. The product of claim 15 wherein the (Riv)'s are the same or different alkyl group, and X is chlorine or bromine. 17. The product of claim 16 wherein the molar ratio of said alkanol reactant and said phenolic react­ ants to said dichlorophosphazene units is about 2:1 to about 2.5:1. 18. The product of claim 17 wherein the molar ratio of said alkanol reactant to said phenolic react­ ants is about 5:1 to about 0.8:1. 19. The product of claim 17 wherein about 40% to about 60% by weight of said phenolic reactants is phenol. 20. A phosphazene composition of the general formula: (P=N)n (R)a (R')b (R'')c (R''')d wherein; R is at least one alkoxy moiety described by the general formula: -OCH₂(CF₂)yX, with X being hydrogen or fluorine and y being equal to 1 to about 10; R', R'' and R''' are different aryloxy moieties, each of R', R'' and R''' being selected from the group consisting of phenoxy, alkoxy phenoxys, alkyl phenoxys, chlorinated phenoxys, fluorinated phenoxys, aryl phenoxys, phenoxy phenoxys, fluoro alkyl phenoxys, fluoroalkoxy phenoxys, chlorinated phenoxy phenoxys, fluorinated phenoxy phenoxys and mixtures thereof; n is equal to 3 to about 4; a, b, c and d are each greater than 0; and the sum a+b+c+d is equal to 2n.

Inventors: CARR, LAWRENCE JOHN, NICHOLS, GEORGE MORRILL, ROSE, SELWYN H.
Applicants: GE CHEMICALS, INC.
Application year: 1986
Main classification: C10M105
IPC codes: C08G79, C07F9, C10M105, C10M107