FLAME RETARDANT POLYMER COMPOSITIONS

Abstract: The present invention relates to fire retardant polymer compositions possessing a non-linear structural configura­ tion resulting by the reaction of N-tribromo­ phenylmaleimide, with or without comonomer, with a pre­ formed backbone polymer, in which the bromine content is above 1.2% by weight bromine. The polymer is selected from polystyrene, polyolefins, polyamides, rubbers, polyesters, acrylics, polymeric dienes and mixtures or copolymers there­ of. The comonomer present with the N-tribromophenyl. maleimide is selected from the group consisting of acrylonit­ rile, styrene and vinyl chloride. According to the invention the non-linear structural configurations are obtained either by grafting or crosslinking of the N-tribromophenylmaleimide onto the preformed backbone polymer in the presence of free radicals producing means. Optionally, synergistic fire retar­ dant additives such as antimony oxide are incorporated in the compositions. The preferred compositions will contain above 4% by weight of the total resin present in the compositions. The flame retardant polymer compositions have improved properties compared with those obtained with known flame retardant reagents.

Description: The present invention relates to flame retardant polymer compositions. More particularly the invention relates to polymer compositions comprising non-linear structural configurations which contain bromo-derivatives of N-phenylmaleimide. It is known that generally, normally flammable polymers can be rendered flame-retardant by the incorporation of halogenated organic compounds. It is also recognized that not all halogenated organic compounds are necessarily useful as flame retardants in all the polymeric compositions which require flame retardation. Consequently, the effectiveness of halogen-containing organic materials intended for use as fire retardants is unpredictable. Some materials release their halogen either too early or too late in the combustion process to provide the degree of fire protection required. Some of the halogenated compounds which have been proposed for use as flame retardants, have one or more of the following disadvantages: volatility, instability towards decomposition and/or discoloration at processing temperatures, inadequate efficiency, incompatibility and UV instability. Some of the above disadvantages make a compound less desirable for use as flame retardant and others actually prevent it from having any practical utility for such applications. The general lack of success of the prior art in producing a wide spectrum flame retardant reagent, or an optimal material for even a more limited range of applicability, is at least partially due to the tendency of the flame retardant to degrade at least one of the properties of the blend produced while improving another. For instance, it has been found that compounds containing cycloaliphatic bromine are sometimes more efficient than other halogenated compounds, but these compounds have poor stability at the processing temperatures of some polymers and frequently have other disadvantages, such as volatility, toxicity and imcompatibility. It is clearly advantageous that a single flame retardant additive find use in a large number of applications. It is well known that halogenated atoms bonded into the polymeric chain, can be efficient or inefficient depending not only on their concentration in the macromolocule, but also on their position. Also, halogen-containing compounds will behave differently when they are used in the additive mode, i.e. simply admixed into the polymeric substrate, or chemically bonded into the polymeric chain. Halo-derivatives of N-phenylmaleimide are described in CS Patent No. 171,355 (filed on November 27, 1974) and CS Patent No 173,355 (filed on December 16, 1974) both published in 1979, as new compounds which are insoluble in water and aliphatic hydrocarbons, some being characterized by their high halogen content. According to CS Patent No. 171,593 the halo-derivatives of N-phenylmaleimide are suggested to be useful as comonomers with various monomers such as vinyl acetate, acrylonitrile, styrene, in the preparation of thermally resistant polymeric materials. The polymers described possess a linear structure and are prepared from the monomers taken in such a ratio that the halogen content of the polymers would be between 16% to 25% by weight. In a review written by the inventors of the above CS Patents [J.Polym.Sci.Pol.Chem.Ed. 14, 2587 (1978) and 17, 2587 (1979)] it is mentioned that mono- and polyhalophenylmaleimides have a strong tendency to form alternating copolymers with styrene and butadiene, while by themselves they are only hardly polymerizable. Of these alternating copolymers, the system with styrene was most studied. According to the results published [Eur.Polym. J.,Vol.14, 219 (1978) tribromophenylmaleimide copolymers with styrene were found to undergo spontaneous decomposition at 352 degrees C whereas polystyrene decomposes at 280 degrees C. These results support their statement on the thermal resistance of these copolymers. They further stipulate that the presence of the imide monomeric unit, in the alternating polymer, retards the depolymerization of the polymer chain. The result of this finding is that less of the combustible volatile hydrocarbon will be released under thermal stress. Of the various halogen-containing comonomers examined by them, tribromophenylmaleimide was found to produce the least amount of HX, commonly regarded to be the agent responsible for flame retardation by halogen containing compounds. More bromine was found in the thermolized residue than in the starting copolymer. The conclusion drawn by these workers is clear from their CS Patent No. 171,593, where only the chloro-derivative is stated for use as comonomer in polymeric materials for fire retardation. It is well known that halogen-containing compounds generally behave differently when the incorporation is in such a manner that the halogen atom is incorporated in units of the polymeric backbone or in a pendant side chain. It is thought that pendant side chains are sometimes lost under stress conditions and with them the fire retardant properties. The general conclusion is that one cannot predict a priori that a halogen-containing component incorporated into a macromolecule will be efficient or not. This is true even for halogens in the backbone units but distributed differently. This is clearly stated also by the inventors of the above two CS Patents in a paper discussing the thermogravimetric analyses of copolymers of styrene with halogenated N-phenylmaleimide (published in Europ. Polymer J., Vol. 13, 509-513, 1977): "copolymerization of compounds with quenching effects can lead to products ranging from alternating copolymers to polymers with chains consisting of homopolymer sections of the two starting compounds. The thermal stabilities of the two types of polymer and the products of the thermal decomposition may be different even if the halogen contents are the same". According to Japanes Kokai 78, 133298 (Cf. C.A. 90, 104852) polyols are treated with less than an equivalent amount of toluene diisocyanate and then mixed with other diisocyanate or polyisocyanate compounds, producing low volatile polyisocyanate compounds. It has now been found that the tribromoderivative of N-phenylmaleimide is amenable to the production of non-linear polymeric configurations, in which this bromo-derivative is contained in pendant side chains or crosslinks, by its reaction with various preformed polymers, imparting to them fire retardant properties. Thus the invention consists of fire retardant polymer compositions comprising non-linear structural configurations, which result from reacting N-tribromo-phenylmaleimide with or without comonomers with a preformed backbone polymer selected from the group consisting of polyolefins, polystyrene, rubbers, polyesters, polyamides, acrylics, polymeric dienes and mixtures or copolymers thereof, said fire retardant compositions containing at least 1.2% by weight bromine. The above preformed backbone polymers may also contain common substituents. Non-linear structural configurations as used in the present specification, and as described above, are known in the art as graft copolymers. The non-linear polymeric compositions of this invention are obtained either by graft polymerization or cross-linking with N-tribromophenylmaleimide, hereafter referred, for the sake of brevity, by the term TBPMI. The graft polymers have either TBPMI or TBPMI-containing side chains bonded onto a preformed polymeric backbone which does not contain TBPMI. The crosslinked polymer will be obtained by the formation of chemical links containing TBPMI between the preformed polymer chains which do not contain TBPMI. The nature of the final compositions will be determined by the relative proportions of the constituents - TBPMI, comonomers and the respective preformed backbone polymer - and the grafting technique employed; actually a wide variety of novel compositions can be obtained. In order to optimize the best combination of good processing and performance properties (e.g. high tensile strength), it is preferred to obtain products containing from 2% to 60% by weight of TBPMI and the balance of the preformed backbone polymer with or without other polymerizable monomers, wherein the preformed backbone polymer must be no less than 4% of the total resin. The inventors explain the excellent fire retardancy properties of TBMPI, when located in the side chains and crosslinkinks of graft polymers, by the relative weakness of the bonds of such pendant groups. These pendant groups are detached under thermal stress, thereby injecting volatile bromine moieties into the vapor phase. This mechanism stands in strong contrast with the high thermal resistance mentioned to exist by the Czechoslovakian authors (cited in the preamble of the present specification) when TBPMI is present in linear structural copolymers. The present invention is particularly related to TBPMI, although one may conceive to utilize other bromine derivatives of N-phenylmaleimide. The compositions according to the present invention may be prepared by any of the conventional techniques of free radical grafting or crosslinking processes used, e.g. radiation induced or chemically induced and by any of the technologies commonly used such as bulk, solution, emulsion or aqueous suspension. One of the grafting reaction procedures for the above process is grafting in an aqueous medium which enables a ready dissipation of the heat of the reaction and avoids the use of expensive solvent recovery apparatus. The emulsion polymerization in aqueous medium is effected by reacting the ingredients dispersed in water in the presence of a surface active agent such as salts of a long chain alkyl sulfate. The temperatures normally used lie between 20 to 100 degrees C and preferably between 25 to 75 degrees C. The reaction between the preformed backbone polymer and TBPMI with or without additional polymerizable monomers, may be initiated as stated above by any suitable means which produces free radicals, but may often be effected in the presence of a free radical yielding initiator active at the polymerization temperature. Initiation may also be induced by radiation, or known reagents such as azo-compounds (e.g.nitriles) and organic and inorganic peroxides such as lauroyl peroxide, dicumyl peroxide, 2.5-(ditert-butylperoxy)-2,5-dimethylhexyne-3, persulfates, hydrogen peroxide, hydroperoxides, or sulfur (in case of rubber as the preformed backbone polymer) and other compounds containing the peroxide linkage. Whereas the system according to the present invention involves a graft polymerization, between a preformed polymer and TBPMI, one may conceive to incorporate cross-linking activators which will further enhance the efficiency of the grafting reaction. The crosslinking density will depend on the reaction conditions and the ratio between the preformed polymer, TBPMI, cross-linking activator, other monomers when used, as well as on the presence of reactive groups in the preformed polymer. A preferred cross-linking activator is triallyl cyanurate. The type of initiator and its concentration, the chemical nature cyan of the preformed polymer,e.g.the presence of the steric hindrance,are important factors which will influence the efficiency of the grafting reaction. These factors are fully described in the literature and a person skilled in the art after reading this specification will be able to select the factor(s) applicable to the specific system of concern. Although the flame retardant polymer compositions obtained according to the present invention are by themselves very efficent, one may further enhance their effectiveness by including one or more synergists conventionally used in flame retardation. These synergistic compounds include oxides, sulfides or organic salts of antimony, boron, arsenic or zinc borate. The preferred synergistic compound for use in the compositions of this invention is antimony trioxide. It was found that the new non-linear compositions obtained by the reaction of preformed polymers with TBPMI, have improved important mechanical properties. For example it has been found that TBPMI produces crosslinked compositions with various types of polyethylene, which compositions are superior to those obtained with other known fire retardants consisting of bromine-containing compounds such as decabromodiphenyl ether or brominated bisimides (so called BT-93). In the following Table 1 are summarized the comparative results of some of the properties for such compositions based on 100 parts of high density polyethylene. The cross-linking was carried out at 200 degrees Celsius using 1 part of 2,5-di(tert-butylperoxy)-2,5-dimethylhexyne-3 as catalyst in each case. In all these experiments antimony oxide synergist was added in the final formulations. As seen in the above Table 1, the extent of crosslinking, as shown by the gel content, using the compositions according to the present invention based on TBPMI, is much higher than for the decabromodiphenyl ether and even better than the brominated bisimide which is in particular recommended for polyethylene. The LOI values as well as the mechanical properties, which are better for the compositions according to the present invention, show their advantage over other compositions with known bromine-compounds as fire retardant reagents. Similar improvements are obtained using TBPMI - based flame retardant compositions with low density polyethylene as the base polymer. Table 2 compares the properties of such compositions (based on 100 parts low density polyetylene) with TBPMI and decabromodiphenyl ether, both systems reacted at 150 degrees C in the presence of 4 parts of dicumyl peroxide as catalyst. The results given in Table 2 clearly show that the extent of crosslinking, expressed as percentage of gel, is higher with the compositions according to the present invention than those with decabromodiphenyl ether. The mechanical properties (tensile strength and tensile modulus) are also better with the compositions according to the present invention than those obtained with decabromodiphenyl ether. The mechanical properties mentioned in Tables 1 and 2, were determined for plates of polyethylene crosslinked with TBPMI according to the present invention, said plates being prepared as follows: An amount of 30 g of the mixture (of compositions mentioned above) was introduced into the closed chamber of a Brabender internal mixer heated and maintained at 130 degrees C. The two mixing heads of the Brabender were allowed to turn at a speed of 20 rpm throughout each experiment and the consequent torque was registered on a graph versus the time. The mixture was taken out from the Brabender and pressed between the two plates of a hydraulic press and allowed to crosslink during ten minutes at 210 degrees C. The gel contents were measured according to ASTM D-2765-68 using xylene. Another example of a non-linear polymer found advantageously flame retarded by TBPMI, is a crylonitrile- b utadiene- s tyrene. Such ABS resins are well known engineering thermoplastics possessing excellent physical characteristics. In many of its applications, such as building materials and appliances, business machines etc., it is necessary that the ABS polymer be flame retardant. The commonly used highly brominated aromatic compounds used as flame retardants, confer a number of adverse effects to the products: Mold build-up of the brominated compound during processing with resulting surface degradation. Severe degradation of overall balance of physical properties of the ABS polymer, particularly of impact strength. Poor efficiencies which cause high levels of halogen and antimony oxide in order to impart an adequate flame retardancy. Bloom or exudation of flame retardants onto the surface of the molded specimens. It was found that in accordance with the present invention, TBPMI imparts an excellent flame retardancy to ABS resins. Blooming is not a problem with TBPMI incorporated into this branched polymer and good overall physical properties are obtainable. Example 1 is an ABS formulation with the flame retardant reagent according to the present invention and Example 2 without the reagent, being presented for comparison purposes. EXAMPLE 1. In a test tube the following reagents were introduced: 10 g polybutadiene. 38.6 g styrene. 25.7 g acrylonitrile. 1.5 g azoisobutyronitrile. 25.7 g of TBPMI. The contents of the test tube were thoroughly mixed and purged with nitrogen. After closing the test tube, it was heated at 65 degrees C for about 4 hours and then for an additional period of 12 hours at 100 degrees C. The test tube was broken and the polymerized mass was ground. Its bromine content was 15%. From the ground material a plate was pressed from which specimens were cut, which had an LOI value of 23.3. EXAMPLE 2. A blank experiment was carried out for comparison purposes. The same procedure was used as in Example 1, with the same amounts of reagents but with the omission of the flame retardant reagent. The specimen had an LOI value of only 17.9. Polystyrene is another resin found to be rendered flame retardant by grafting onto it TBPMI. As known, styrene-based resins are widely used and make up a significant part of the plastic industry. One great deficiency of styrenic resins is their flammability, and there is an ever increasing awareness and interest in providing styrene-based polymers which possess flame retardancy. TBPMI was grafted onto high impact polystyrene, on a Brabender. instrument using two compositions containing different amounts of bromine (Table 3). Grafting is shown by the increase in the torque. The conditions in the Brabender were: temperature = 200 degrees C and the mixing rolls had a speed of 40 rpm. The compositions tested were prepared with the use of peroxide XL-130 (produced by Pennwalt). Grafting of TBPMI onto H igh I mpact P olystyrene (Galirene Q-88-5 produced by Israel Petrochemicals Ltd.). Exp. No. Composition (parts by weight) Torque (newt.meter) LOI HIPS XL-130 Ca-stearate Sb₂O₃ TBPMI Initial Final 1 56 0.4 0.5 5.5 38.1 8.7 12 35.9 2 41.3 0.6 0.5 7.3 50.8 6.5 9.5 40.4 The results clearly show the increase of torque imparted by grafting with TBPMI. The product of Exp. 1 was dissolved in tetrahydrofuran and the Sb₂O₃ which precipitated was filtered off. Chromatographic analysis showed only traces of TBPMI monomer to be present. Essentially all of that initially introduced was therefore grafted onto the HIPS resin. Similar results were obtained with ABS resin. The experiments were performed in the same manner and are summarized in the following Table 4. Grafting of TBPMI onto ABS resin (Ronfalin T-PWD NAT 0001 produced by DSM) Exp. No. Composition (parts by weight). Torque (Newt. meters) LOI ABS XL-130 Mg stearate Irgawax 280 Sb₂O₃ TBPMI Initial Final 3 56 0.4 0.5 0.5 5.5 38.1 10.8 25 37.2 4 41.3 0.6 0.5 0.5 7.3 50.8 10.8 22.5 40.8 EXAMPLE 3. The same procedure as described in Example was used with the following mixture: - 4 g polybutadiene. - 41.2 g styrene. - 27.4 g acrylonitrile. - 27.4 g TBPMI. - 1.5 g azoisobutryonitrile. The resulting polymer contained 16% bromine and had an LOI of 24.5. EXAMPLE 4. 100 parts of natural rubber were blended with 30 parts of TBPMI and irradiated at room temperature with 25 megarads from a Co⁶⁰ source. The resulting vulcanisate had similar mechanical properties to that prepared from the same blend with the addition of 5 parts sulfur using a thermal vulcanisation process at 145 degrees centigrade for 15 minutes. Both products had good flammability resistance. EXAMPLE 5. (The amounts given are by wt.). The following reagents were introduced in a reaction vessel provided with a stirrer: - 500 parts polyethylene powder (low density of a melt flow index 22 g / 10 min). - 1750 parts distilled water. - 9 parts polyvinyl alcohol (as suspending agent). - 20 parts TBPMI, and - 1.5 parts lauroyl peroxide. The above reagents were mixed until a homogeneous suspension was obtained. Then an amount of 480 parts of vinyl chloride monomer was added and the temperature was raised to 68 degrees centigrade. After four hours of reaction, the polymeric product was filtered off and found to exhibit good flammability resistance. EXAMPLE 6. Ethylene-propylene rubber (EPR) is an elastomer of widespread use in wire and cable applications. It is of importance to provide elastomers for this application, fire retarded to meet the UL 94 VO flame resistance specifications without sacrifice of the mechanical properties. This is accomplished by the use of TBPMI as flame retardant. The components (except dicumyl peroxide) described in the following table were blended in a Brabender Plasticorder at 125 degrees centigrade for 20 minutes at 20-25 RPM. Then the peroxide was introduced and mixing was continued for 3 minutes. The molten mass was removed from the mixing cell and pressed and cured into 2 mm thick plates for 30-45 minutes. The specimens were submitted to mechanical and fire resistance tests. From the results listed in the following Table 5, it can be seen that 1. TBMI promotes cross-lining as seen from the time to torque increase. 2. TBPMI provides better fire retardancy than BT-93 on an equivalent bromine content. 3. The EPR flame retarded by TBPMI has better mechanical properties than that containing BT-93. The results clearly show the flame retardant property imparted to EPR rubber. The LOI values as well as the mechanical properties are better than the composition with a known fire retardant such as Saytex BT-93. EXAMPLE 7. A. In 30 g liquid polyester resin (based on maleic, phthalic anhydrides and propylene glycol) containing 30∼40% styrene, were dissolved 3.05 g TBPMI and to the mixture was added, by mixing continuosly, 1.1 g Sb₄O₆ until the mixture became homogeneous. Then, to this homogeneous mixture were added 8 drops of a Co-octoate solution and 6 drops of a radical initiator (methylethylketone hydroperoxide). The mixture was quickly cast into a Teflon mould containing cavities of 6x100x3 mm. The curing was performed at room temperature for two hours and then in an oven at 110 degrees C. The specimens were removed and left to cool. The LOI of these specimens was 29.2%. B. The example is similar to the previous one excepting the Sb₄O₆ which here was absent and therefore 6.1 g TBPMI was added. After the same curing protocol the specimens had an LOI of 22.3%. The LOI of the cured polyester resin without TBPMI was 18.7%. EXAMPLE 8. Nylon 66 polyamide (prepared from adipic acid and hexamethylene diamine) in the form of fibers was soaked in a solution of TBPMI in dimethylformamide (DMF) overnight. The drained fibers were washed with water to remove the DMF and then irradiated with 2 meV electrons from a Van de Graaff generator at a 40 megarad dosage. The fibers were then extracted with xylene to remove the excess, unbound TBPMI. The weight gain of the fibers was 21% and they contained 12.5% Br. Twisted yarns of the treated fibers were found to have an LOI of 29.3. Untreated fibers had an LOI of 22.2. EXAMPLE 9. Ten grams of polymethyl methacrylate (PMMA) and 2.71 g TBPMI were dissolved in 90 g. of toluene. The mixture was introduced into a reaction vessel and, under stirring there was added 0.158 g. of dibenzoyl peroxide 80% (the balance of the latter being water commonly used for storage of this material). The temperature was gradually increased to 80-90 degrees centigrade while keeping the mixture under a nitrogen blanket. After 5 hours, the temperature was increased to reflux the toluene, and kept there for two hours. The mixture was subsequently cooled and the copolymer (graft) was precipitated by pouring the viscous solution slowly into vigorously stirred methanol. The polymer was separated and dried at 60 - 70 degrees C under vacuum. Specimens pressed from the product had an LOI of 19.5%. The LOI of PMMA (nongrafted) was 17.7%. EXAMPLE 10. A blend was prepared using the following components: Vistalon 3708 (ethylene-propylene rubber, produced by Exxon) 21 parts FR-1033 50 parts antimony oxide 25 parts dicumyl peroxide 3 parts triallyl cyanurate 1 part An amount of 95 gr of this blend is introduced in a BRABENDER PLASTICORDER PLE 651 heated at 80 degrees C. The mixing blades were rotated at a speed of 15 rpm during 22 minutes. The mixture was then crosslinked by compression molding at 130 degrees C during 30 minutes. Specimens pressed from the product had an LOI of 32.1 An important advantage which characterizes the present invention is its versatility, enabling to obtain a very large number of fire retardant compositions by grafting TBPMI with comonomers onto a preformed backbone polymer. Among the various suitable comonomers the following should be mentioned in particular: acrylate esters; methacrylate esters; vinyl acetate; vinyl halides; vinylidene halides; acrylonitrile; butadiene; chloroprene; styrene; iso-butylene; acrylamide; maleic anhydride and other maleimides. A person skilled in the art will select the proper comonomer according to the specific use of the respective composition. Whereas the compositions according to the present invention are based on a reaction which involves cross-linking, various coagents for this type of reaction may be utilized, as known in the art (see for example page 331 in the Encyclopedia of Polymer Science and Technology, Vol. 4, H.F. Mark, Interscience Publ. Co., N.Y., 1966). Among these coagents the following should be in particular mentioned: triallyl cyanurate; triallyl isocyanurate; divinyl benzene; S₂Cl₂; bis-azodicarboxylates, diallyl phtalate, dimalemides, ethylene dimethacrylate, ethylene glycol dimethacrylate, 1,3 butylene glycol dimethacrylate etc. This fire retardant polymer compositions according to the present invention may further include, depending on the purposes, reinforcing agents such as glass fibers, carbon fibers and asbestos, fillers such as silica, alumina, silica-magnesia, calcium silicate, calcium carbonate, barium sulfate, lubricants such as higher fatty acid esters and paraffin waxes, as well as other stabilizers, antistatic agents, antioxidants, UV absorbers, dyes, pigments e.g. TiO₂ or the like, as generally utilized for such compositions.

Claims: Fire retardant polymer compositions comprising non-linear structural configurations which result from reacting N-tribromophenylmaleimide, with or without comonomers, with a preformed backbone polymer selected from the group consisting of polystyrene, polyolefins, polyamides, rubbers, polyesters, acrylics, polymeric dienes and mixtures or copolymers thereof, said fire retardant compositions containing at least 1.2% by weight bromine. Fire retardant polymer compositions according to claim 1, wherein said preformed backbone polymers also contain common substituents. Fire retardant polymer compositions according to claims 1 or 2, wherein the non-linear structural configurations result from the grafting of N-tribromophenylmaleimide, with or without comonomers, onto the preformed backbone polymer. Fire retardant polymer compositions according to claims 1 or 2, wherein the non-linear structural configurations result from the incorporation of N-tribromophenylmaleimide, with or without comonomers, as crosslinks between chains of the preformed backbone polymer. Fire retardant polymer compositions according to claims 1 to 4, wherein said compositions contain from 2% to 60% by weight of N-tribromophenylmaleimide, the balance being the preformed polymer with comonomers, and the backbone polymer being at least 4% by weight of the total resin present in the composition. Fire retardant polymer compositions according to Claims 1 to 5, wherein a cross-linking activator is incorporated in the compositions. Fire retardant polymer compositions according to claim 6, wherein said cross-linking activator is triallyl cyanurate. Fire retardant polymer compositions according to claim 5, wherein said preformed backbone polymer is polybutadiene. Fire retardant polymer compositions according to claim 5, wherein said preformed backbone polymer is polyethylene. Fire retardant polymer compositions according to claim 5, wherein said preformed backbone polymer is an ABS resin. Fire retardant polymer compositions according to claim 5, wherein said preformed polymer is high impact polystyrene. Fire retardant polymer compositions according to claim 5, wherein said preformed polymer is a natural rubber. Fire retardant polymer compositions according to claim 1 to 12, wherein at least one synergistic fire retardant additive is incorporated therein. Fire retardant polymer compositions according to claim 13, wherein said synergistic additive is antimony oxide. Fire retardant polymer compositions according to claims 1 to 5, wherein the comonomer with N-tribromophenylmaleimide is selected from the group consisting acrylonitrile, styrene and vinyl chloride. A method for the preparation of fire retardant polymer compositions comprising non-linear structural configurations which result by grafting N-tribromphenylmaleimide with or without comonomers, onto a preformed backbone polymer selected from the group consisting of polystyrene, polyolefins, polyamides, rubbers, polyesters, acrylics, polymeric dienes and mixtures or copolymers thereof, using conventional techniques. A method for the preparation of fire retardant polymer compositions comprising non-linear structural configurations which result by crosslinking a preformed backbone polymer selected from the group consisting of polystyrene, polyolefins, polyamides, rubbers, polyesters, acrylics, polymeric dienes and mixtures or copolymers thereof, using TBPMI with or without comonomers, by conventional techniques. A method for the preparation of fire retardant polymer compositions according to Claims 16 or 17, wherein the reaction is initiated by conventional free radicals producing means. A method according to Claim 18, wherein the free radicals producing means are azo-compounds, organic and inorganic peroxides, persulfates, hydroperoxides and sulfur. A method according to Claim 18, wherein the free radical initiation means are obtained by radiation. A method according to Claims 16 to 20, wherein conventional additives selected from pigments, fillers, fibers, lubricants, stabilizers and carbon black are incorporated. A method for the preparation of fire retardant polymer compositions comprising non-linear structural configurations substantially as described in the specification and claimed in Claims 16 to 21. Fire retardant polymer compositions comprising non-linear structural configurations substantially as described in the specification and claimed in any of Claims 1 to 15.

Inventors: FISHLER, THEODOR MOREL, RUMACK, MICHAEL, SHORR, LEONARD M., YANAY, SHAUL
Applicants: BROMINE COMPOUNDS LTD.
Application year: 1986
Main classification: C08F291
IPC codes: C08F291