PROCESS FOR PRODUCING A POLYARYLENE SULFIDE

Abstract: A polyarylene sulfide having a low content of heavy metals and excellent heat stability is produced by mixing an alkali metal sulfide, water, and an organic polar solvent in the molar ratio of about 1:10 to 20:1 to 10 and by heating the mixture to remove water and then polymerizing the resulting mixture with a polyhalogenated aromatic compound. Such a polyarylene sulfide is very useful for use in electronic com­ ponents and automotive parts, etc.

Description: This invention relates to a process for producing a polyarylene sulfide (for example, a polyphenylene sulfide) having a low content of heavy metals, excellent electrical characteristics, and excellent heat stability. Polyarylene sulfide, having excellent heat resistance and excellent chemical resistance, has attracted special attention for use in electronic components and automotive parts. Being moldable into engineering parts made of plastics, films, sheets, fibers, polyarylene sulfide is widely used in fields where heat resistance is needed. Japanese Patent Publication No. 3368/1970 discloses a process for producing polyarylene sulfide wherein the reaction between p-dichlorobenzene and sodium sulfide is conducted in an organic polar solvent such as N-methyl-2-pyrrolidone . Sodium sulfide containing 2.8 moles or 9 moles of water of hydration per mole of Na₂S is heated to free the water of hydration under reduced pressure or in N-methyl-2-pyrrolidone solvent with the introduction of bubbles of nitrogen and then p-dichlorobenzene is added thereto, followed by thermal polymerization. This process, however, causes the corrosion of reaction vessels made of iron or stainless steel, because highly corrosive sodium sulfide is maintained at high temperatures in the dehydration stage, resulting in elution of heavy metals such as iron into sodium sulfide. Therefore, a significant amount of heavy metals remains in the polymer produced by the reaction with p-dichlorobenzene, which unfavorably causes a reduction in heat stability and electrical characteristics. It is also conceivable to use titanium, chromium, molybdenum, or tungsten, or stainless steels having a high content of these metals, as the constituent materials of a reaction vessel in order to prevent heavy metals remaining in the polymer. However, these materials are undesirable because of their low reliability at high temperatures and pressure and their high cost. It is therefore an object of the present invention to provide a process for producing a polyarylene sulfide having a low content of heavy metals, excellent electrical characteristics, and excellent heat stability even when a reaction vessel, which is made of low cost materials, such as stainless steel having high reliability at high temperature and pressure is used. Other objects and advantages of the present invention will become apparent to those skilled in the art from the following description and disclosure. The present invention relates to a process for producing a polyarylene sulfide, which comprises mixing an alkali metal sulfide, water and an organic polar solvent in the ratio of :10 to 20:1 to 10 (molar ratio) and by heating the mixture at a temperature of from an initial point of 100 o C to an end point of 180 - 230 o C to remove water, the molar ratio of the alkali sulfide to water thereby being in the range of 1:0.9 to 2.0, and then thermally polymerizing the resulting mixture with 0.90 to 1.1 moles of polyhalogenated aromatic compound per mole of the alkali metal sulfide at a temperature of from 180 to 300 o C and a polymerisation time of between 0.5 and 20 hours. When the water of hydration is removed from a highly corrosive alkali metal sulfide by heating it in a mixture which includes a large excess of water and an organic polar solvent, the highly corrosive alkali metal sulfide at low temperature may be converted to a reaction mixture comprising an extremely low corrosive alkali metal sulfide, water and the organic polar solvent, which causes barely any corrosion of the reaction vessel in the subsequent dehydration at high temperature. Alkali metal sulfides usable in the present invention include lithium sulfide, sodium sulfide, potassium sulfide, and mixtures thereof. An alkali metal hydrosulfide and an alkali metal hydroxide may be mixed to produce an alkali metal sulfide in situ. Moreover, a small amount of alkali metal hydroxide may be added to react with a trace amount of the alkali metal hydrosulfide and alkali metal thiosulfate which are contained in the alkali metal sulfide. The water referred to in the present invention is the total sum of water present in the reaction system, including the water of hydration of the alkali metal sulfide and the water produced by the reaction between an alkali metal hydrosulfide and an alkali metal hydroxide. Moreover, 10 to 20 moles of water per mole of alkali metal sulfide should be added to the system of reaction prior to the removal of water by heating. Less than 10 moles of water unfavorably leads to a larger proportion of heavy metals being contained in the resulting polymer. More than 20 moles of water requires more energy to remove water, which is undesirable from the economic viewpoint. Preferable organic polar solvents usable in the present invention are aprotic polar solvents which are stable at high temperatures. Examples of them include amides and ureas such as N,N-dimethylacetamide, N-ethyl-2-pyrrolidone, N-methyl-2-pyrrolidone, hexamethylphosphoramide, tetramethylurea, 1,3-dimethyl-2-imidazolidinone sulfones such as sulfolane, dimethyl sulfolane ketones such as methyl phenyl ketone , and mixtures thereof. The amount of the solvents used should be in the range of 1 to 10 moles per mole of alkali metal sulfide. Less than one mole of the solvent unfavorably leads to a larger proportion of heavy metals in the resulting polymer. More than 10 moles of the solvent is undesirable from the economic viewpoint. Polyhalogenated aromatic compounds usable in the present invention are halogenated aromatic compounds in which two or more halogen atoms are bonded directly to the aromatic nucleus. Examples of them include p-dichlorobenzene, o-dichlorobenzene, m-dichlorobenzene, dibromobenzene, diiodobenzene, trichlorobenzene, tribromobenzene, triiodobenzene, tetrachlorobenzene, tetrabromobenzene, tetraiodobenzene, dichloronaphthalene, dibromonaphthalene, diiodonaphthalene, dichlorobiphenyl, dibromobiphenyl, diiodobiphenyl, dichlorodiphenyl sulfone, dibromodiphenyl sulfone, diiododiphenyl sulfone, dichlorobenzophenone, dibromobenzophenone, diiodobenzophenone, dichlorodiphenyl ether, dibromodiphenyl ether, dichlorodiphenyl sulfide, dibromodiphenyl sulfide and mixtures thereof. p-Dichlorobenzene and a mixture of p-dichlorobenzene and a small amount of trichlorobenzene are usually used. The amount of the polyhalogenated aromatic compound used is usually in the range of 0.90 to 1.11 moles per mole of an alkali metal sulfide. Deviation from this range unfavorably caused the polymer to possess a reduced molecular weight. An auxiliary catalyst such as organic alkali metal carboxylate may also be added to produce a polymer having a higher molecular weight. The removal of water by heating in the present invention is usually conducted at a temperature of from an initial point of 100 o C to an end point of 180 - 230 o C. When the temperature is higher than 230 o C, a significant amount of organic polar solvent is undesirably removed together with water by heating. The preferable molar ratio relative to water of the alkali metal sulfide after the removal of water is normally in the range of 1:0.9 to 2.0. Polymerization in the present invention is conducted ordinarily at 180 to 300 o C, preferable 200 to 270 o C, for 0.5 to 20 hours with stirring. When the polymerization temperature is lower than 180°C, the polymerization rate is considerably reduced. When the polymerization temperature is higher than 300⁰C, the thermal decomposition of the polymer may take place. The polyarylene sulfide obtained according to the present invention can be subjected, in heat-treated or untreated conditions, as it is, or after being mixed with a reinforcing filler (e.g. glass fiber), a known inorganic filler (e.g. mica, talc, or silica), a pigment, a flame-retardant, a stabilizer, or other polymers, to injection molding, extrusion molding, etc. to prepare a shaped article, a film, a sheet, a pipe, a fiber. Examples The present invention will be explained more specifically below by way of Examples. However, the present invention is in no way restricted to these Examples. The content of iron in the polymers shown in the Examples and Comparative Examples was measured by (a) subjecting 0.5 g of a sample to wet decomposition with 10 ml of sulfuric acid and about 10 ml of nitric acid in a quartz beaker, (b) adding thereto deionized water to prepare a solution of a predetermined amount and then (c) subjecting the solution to atomic absorption spectrometry. The heat stability of the polymers was determined by visual inspection of the color of polymers when heat-treated for 2 hours at 250 o C. Example 1 In a SUS 316, 15-liter autoclave were placed 14.8 moles of Na₂S·2.8H₂O, 121 moles of water, and 44 moles of N-methyl-2-pyrrolidone. They were heated to 210 o C with stirring, whereby 2630 g of a distillate consisting mainly of water was removed. Then, the system was cooled to 170 o C and 14.8 moles of p-dichlorobenzene was added. The system was heated to 250 o C. Polymerization was conducted for 3 hours at that temperature. After the completion of the polymerization, heating was conducted under reduced pressure to remove the solvent, and the resulting polymer was washed with hot water three times, subjected to repeated centrifuging, and then dried overnight by heating to give a light-white powder. The yield, iron content, and heat stability of the polymers were measured. The results are shown in Table 1. Example 2 The procedure of Example 1 was repeated except that 151 moles of water were added. The results are shown in Table 1. Example 3 The procedure of Example 1 was repeated except that 14.8 moles of NaSH (25% aqueous solution) and 14.8 moles of NaOH (48% aqueous solution) were added instead of Na₂S·2.8H₂O and no further water was added. The results are shown in Table 1. Example 4 The procedure of Example 1 was repeated except that 14.73 moles of p-dichlorobenzene and 0.07 mole of 1,2,4-trichlorobenzene were added. The results are shown in Table 1. Comparative Example 1 The procedure of Example 1 was repeated except that no water was added. The results are shown in Table 1. Comparative Example 2 The procedure of Example 1 was repeated except that 14.8 moles of Na₂S·9H₂O were added instead of Na₂S·2.8H₂O and no water was added. The results are shown in Table 1. Example 5 The procedure of Example 1 was repeated except that 16.28 moles of N-methyl-2-pyrrolidone were added prior to the removal of water and then p-dichlorobenzene was added together with 27.72 moles of N-methyl-2-pyrrolidone to conduct polymerization. The results are shown in Table 1. Comparative Example 3 The procedure of Example 1 was repeated except that 13.32 moles of N-methyl-2-pyrrolidone were added prior to the removal of water and then p-dichlorobenzene was added together with 30.68 moles of N-methyl-2-pyrrolidone to conduct polymerization. The results are shown in Table 1. Examples 1 to 4 and Comparative Examples 1 to 2 apparently show that a molar ratio of H₂O/Na₂S of more than 10 before the removal of water gives an extremely low content of iron as compared with those having a molar ratio of less than 10, and further a relatively small degree of discoloration and indicating excellent heat stability after the application of heat. Example 5 and Comparative Example 3 show that a molar ratio of N-methyl-2-pyrrolidone/Na₂S of less than 1.0 before the removal of water gives an extremely high content of iron even when additional N-methyl-2-pyrrolidone was added prior to polymerization, resulting in reduced heat stability. Therefore, the molar ratio of N-methyl-2-pyrrolidone/Na₂S before the removal of water needs to be 1.0 or more. As is obvious from the above explanation, the present invention provides a polyarylene sulfide having a low content of heavy metals and excellent heat stability.

Claims: A process for producing a polyarylene sulfide, which comprises mixing an alkali metal sulfide, water and an organic polar solvent in the molar ratio of 1:10 to 20:1 to 10 and by heating the mixture at a temperature of from an initial point of 100 o C to an end point of 180 - 230 o C to remove water, the molar ratio of the alkali sulfide to water thereby being in the range of 1:0.9 to 2.0, and then thermally polymerizing the resulting mixture with 0.90 to 1.1 moles of a polyhalogenated aromatic compound per mole of the alkali metal sulfide at a temperature of from 180 to 300 o C and a polymerization time of between 0.5 and 20 h. The process according to claim 1 wherein the thermal polymerization is conducted at a temperature of from 200 to 270 o C. The process according to claim 1 wherein an auxiliary catalyst is further added to the thermal polymerization.

Inventors: EMURA, HORIAKI, INOUE, HIROSHI, KATO, TOSHIKAZU
Applicants: HODOGAYA CHEMICAL CO., LTD., TOSOH CORPORATION
Application year: 1986
Main classification: C08G75
IPC codes: C08G75