RETICULATED CELLULOSE PRODUCT, SHEETS FORMED THEREFROM, METHODS AND MICROORGANISMS FOR THEIR PRODUCTION

Abstract: Strains of Acetobacter that are stable agitated culture conditions are claimed as well as a unique reticulated cellulose product, and a method and media for producing such bacterial cellulose under agitated culture conditions. Sustained production of bacterial cellulose over an average of 70 hours of at least 0.1 g/liter per hour is achieved. Further, sheets comprising the microbially produced cellulose which are characterized by great tensile strength and by substantial resistance to densification when produced by sheet forming means, are claimed.

Description: The invention concerns strains of Acetobacter that are capable of producing cellulose in artificial culture. More specifically, the Acetobacter strains according to the invention are characterized by an ability to produce large amounts of cellulose in agitated culture without manifesting instability leading to loss of cellulose production in culture. Among the Acetobacter strains according to the invention are strains additionally characterized by a substantially reduced ability to produce gluconic acid. The production of cellulose using such gluconate negative (glcA⁻) strains in artificial culture medium, is facilitated as these strains do not substantially acidify the medium. Such gluconate negative Acetobacter strains are useful in high cell concentration cultures. The invention also concerns a bacterial cellulose product having novel properties. In particular, the invention concerns a reticulated cellulose product. This reticulated bacterial cellulose product is characterized by a microscopic structure unlike that of bacterial cellulose produced by cellulose producing microorganisms under static culture conditions. The invention also pertains to a method for producing the reticulated cellulose product by culturing cellulose producing microorganisms for sustained periods of time, generally in excess of four hours, under agitated culture conditions. The sustained and efficient production of bacterial cellulose under agitated culture conditions was unexpected. The production of cellulose by Acetobacter has been the subject of intense study since at least the 1930's. In 1947, it was shown that in the presence of glucose and oxygen, non-proliferating cells of Acetobacter synthesize cellulose. Hestrin, S., Aschner, M. and Mager, J., Nature , 159:64 (1947). Since the observations of Hestrin et al., Acetobacter has been grown with the production of cellulose under a variety of conditions. For example, when grown with reciprocal shaking at about 90-100 cycles per minute, the cells are incorporated into a large gel mass. When grown under conditions in which the culture medium is agitated with swirling motion for four hours, stellate gel bodies form which are comprised of cellulose and cells. When grown as standing-cultures, a pellicle forms at the air/medium interface. The pellicle forms as a pad generally having the same surface shape and are as the liquid surface of the vessel containing the culture. Hestrin and Schramm, Biochem. Journal, 58:345-352 (1954). Hestrin and Schramm observed rapid cellulose production by freeze-dried preparations of Acetobacter containing less than 10% viable cells. These experiments, however, only measured cellulose production in shaking conditions by such freeze dried preparations over a relatively short period of three to four hours, and were run under citrate buffering conditions to control significant pH changes caused by gluconic acid produced by Acetobacter in the presence of glucose. Polysaccharide biosynthesis by Acetobacter has been studied by several groups using non-growing cultures. In some of these studies, Acetobacter strain NRRL B42 was grown, freed from the cellulose pellicle, resuspended in 0.01 M Tris-EDTA, frozen, and then thawed as described in Hestrin and Schramm, (1954). These treated cells were used for biochemical studies under conditions that did not sustain growth of the cells, but which did preserve enzymatic activity permitting the cellulose to be synthesized by the prepared cells. Progress in determining conditions for culturing Acetobacter for cellulose production, however, has not been the subject of wide reporting. Thus, the conditions used for culturing Acetobacter as described in U.K. patent application 2,131,701A, which claims priority of U.S. patent application 450,324, filed December 16, 1982, are those described in Hestrin and Schramm (1954); i.e., an initial pH of about 6, temperatures in a range from 15°C to 35°C and preferably 20°C to 28°C. According to Deley et al., "Acetobacteracea" pp. 267-278 in Bergeys Manual of Systematic Bacteriology , Kreig and Holt, eds., 1st ed., William & Wilkins, Baltimore and London, 1984, the best carbon sources for growth in descending order are ethanol, glycerol and lactic acid. Acid is formed from n-propanol, n-butanol and D-glucose. The carbon sources described in U.K. application 2,131,701A include fructose, mannitol, sorbitol, and glucose, all of which give rapid cellulose production, and glycerol, galactose, lactose, maltose and sucrose, all of which give slower growth. No growth was observed using sorbose, mannose, cellobiose, erythritol, ethanol, and acetic acid. In U.K. patent application 2,131,701A it is desired to produce a coherent gel-like material for use as a wound dressing, after processing to remove the culture medium. To obtain this mat-like form, the culturing material is kept motionless during cell growth and cellulose production for a period ranging from a few hours to days or weeks. Although the formation of a coherent mat or pellicle in motionless or standing culture conditions is the culture mode described in the U.K. patent application 2,131,701A, this patent further explains that intermittent agitation of the culture medium containing cellulose-synthesizing Acetobacter can control the length of the cellulose fibril produced by the microorganism. Intermittent agitation produces fibrils of finite length which is determined by the linear extension rate of the fibril by the microorganism and the period between agitative shearing of the fibril from the surface of the bacterium. Nothing, however, is disclosed about the effects of continuous agitation on the cellulose product. European Patent Application Publication No. 0114481 describes pads loaded with liquid for use as wound and burn dressings. The pads are prepared from pellicles of microbially-produced cellulose. The cellulose is prepared in static (i.e. non-agitated) culture conditions. In fact, as is stated on page 6 of the description, in order to obtain the "coherent gel-like material desired" "... it is essential that the culturing medium remains substantially motionless during the culturing period". The production of cellulose from Acetobacter in continuously agitated cultures is beset with numerous problems, the most difficult of which has heretofore been culture instability. This instability is demonstrated by loss of the ability to make cellulose and gradual overgrowth of cellulose producing cells by non-producing types. Strain instability may be the result of the appearance of spontaneous mutants or variants of the microorganism that are cellulose non-producers. This appearance of non-producers apparently occurs with a frequency high enough to shift the population balance of a culture from cellulose-producing to cellulose non-producing types during growth in agitated culture. The loss of cellulose production in shaking cultures may also be merely the result of physiological factors rather than mutation to non-cellulose producing types due to genetic changes. Leisinger et al., Ueber cellulosefrie Mutanten von Acetobacter xylinum , Arch. Mikrobial , 54:21-36 (1966). Although the cause is not known, the sustained production of bacterial cellulose in agitated culture medium has not heretofore been reported. Cellulose negative (Cel⁻) strains of Acetobacter have been made by chemical mutagenesis with ethyl methane sulfonate (EMS), nitrous acid and N'-nitrosoguanidine (NG). When grown in static cultures, all of the EMS and nitrous acid-, and 90% of the NG-mutated strains reverted to cellulose producing types. Valla et al., Cellulose-Negative Mutants of Acetobacter xylinum , J. Gen. Microbiol. , 128(7):1401-1408 (1982). Growth of mixed cultures of cellulose-producing and non-producing strains in static cultures strongly favored cellulose producing strains in static cultures, whereas growth of such mixed cultures in shake flasks favored non-producing strains. Valla et al. (1982). This result lends support to the hypothesis that the cellulose mat or pellicle produced by this microorganism enables Acetobacter cells to reach the surface of static liquid medium where the supply of oxygen is abundant. Under shaking conditions where oxygen dissolution rate and low oxygen solubility limits growth, cellulose negative strains are favored because of selective aggregation of cellulose producing cells and resulting mass transfer limitation with respect to oxygen. It will thus be readily apparent that the identification and isolation of Acetobacter strains that are stable cellulose producers in agitated culture medium is of critical importance to large scale production of cellulose form Acetobacter in cultures which are concentrated enough to require agitation for sufficient oxygen supply to the medium. Acetobacter is characteristically a gram-negative, rod-shaped bacterium 0.6-0.8 µm by 1.0-4 µm. It is strictly aerobic; metabolism is respiratory, never fermentative. It is further distinguished by the ability to produce multiple poly β-1,4-glucan chains, chemically identical to cellulose. Multiple cellulose chains or microfibrils are synthesized at the bacterial surface at sites external to the cell membrane. These microfibrils have cross sectional dimensions of about 1.6 nm x 5.8 nm. In static or standing culture conditions the microfibrils at the bacterial surface combine to form a fibril having cross sectional dimensions of about 3.2 nm x 133 nm. The cellulose fibrils produced by these microorganisms, although chemical resembling, in many aspects, cellulose produced from wood pulp, are different in a number of respects. Chiefly among the differences is the cross sectional width of these fibrils. The cellulose fibrils produced by Acetobacter are usually two orders of magnitude narrower than the cellulose fibers typically produced by pulping birch or pin wood. The small cross sectional size of these Acetobacter -produced fibrils, together with the concomitantly greater surface area than conventional wood-pulp cellulose and the inherent hydrophilicity of cellulose, leads to a cellulose product having unusually great capacity for absorbing aqueous solutions. This capacity for high absorbency has been demonstrated to be useful in the manufacture of dressings which may be used in the treatment of burns or as surgical dressings to prevent exposed organs from surface drying during extended surgical procedures. Such uses and a variety of medicament impregnated pads made by treatment of Acetobacter -produced intact pellicles are disclosed in U.K. 2,131,701A. The pellicles of this U.K. application are produced by growing Acetobacter in a culture medium tray which remains motionless. Because Acetobacter is an obligate aerobe, i.e., it cannot grow in the absence of oxygen, production of cellulose by Acetobacter occurs at the air-liquid medium interface. Each bacterium continuously produces one fibril at the air-liquid interface. As new cellulose is formed at the surface, existing cellulose is forced downward into the growth medium. As a result, cellulose pellicles produced in static culture conditions consist of layers of cellulose fibers. Significantly, the volume of cellulose so produced is restricted by the interface between air and culture medium. The tendency of known Acetobacter strains to become cellulose non-producers when cultured under agitated conditions at increased dissolved oxygen concentration, severely limits the amount of cellulose that can be made economically. Consequently, high cellulose productivity per unit volume of vessel in extended agitated fermentations has not been previously reported. Another problem associated with cellulose production by Acetobacter in batch culture, whether agitated or motionless, is the ability of Acetobacter to convert glucose to gluconic acid and ketogluconic acids. The pH drop associated with such acid production by the organism also limits the amount of cellulose made, particularly in batch cultures. Moreover, the production of gluconic acid removes glucose from the medium at the expense of cellulose production. This invention provides reticulated cellulose obtainable from a microorganism designated Acetobacter having the ability of microorganisms obtainable from ATCC 53264, ATCC 53263 and ATCC 53524 to produce a cellulose product under agitated culture conditions, which product is obtainable under conditions of continuous culture agitation resulting, when viewed with a scanning electron microscope, in a reticulated structure having frequently thickened strands that interconnect to form a grid-like pattern extending in three dimensions and demonstrating resistance to densification when formed into sheets by sheet forming-means. In another aspect, the invention provides a method of producing a reticulated cellulose as defined above comprising: a) culturing, under agitated conditions, a microorganism designated Acetobacter having the ability of microorganisms obtainable from ATCC 53264, ATCC 53263 and ATCC 53524 to produce a cellulose product under agitated culture conditions, in a liquid medium suitable for cellulose production at an average volumetric productivity of at least 0.1 g/1/hr over a period of time exceeding 70 hours, said micro-organism having a frequency of change in agitated culture conditions from cellulose producing forms to cellulose non-producing forms of less than 0.5% over the course of 42-45 generations, as determined by the appearance of cellulose non-producing colonies on solid medium, and b) removing the reticulated cellulose product obtained. The invention also provides a microorganism designated Acetobacter and having the ability of micro-organisms obtainable from ATCC 53264, ATCC 53263 and ATCC 53524 to produce a cellulose product under agitated culture conditions, and having a frequency of change from cellulose producing forms to cellulose non-producing forms under agitated culture conditions, as determined by the appearance of cellulose non-producing colonies on solid medium, of less than 0.5% over the course of 42-45 generations. In another aspect, the invention includes a micro-organism designated Acetobacter and having the ability of microorganisms obtainable from ATCC 53264, ATCC 53263 and ATCC 53524 to produce a cellulose product under agitated culture conditions and which produces reduced amounts of gluconic acid and ketogluconic acids when grown on D-glucose-containing medium. This bacterial cellulose produced under known static culture conditions is characterized by a disorganized layered structure consisting of overlaying and intertwisted discrete cellulose strands or fibrils. This disorganized layered structure reflects the growth pattern of cellulose-producing microorganisms which is typified by the microorganism Acetobacter. In static cultures, Acetobacter typically grows at the interface of the surface of the liquid medium and air containing oxygen. As the cells grow, cellulose fibers are continuously elaborated and accumulate, sinking deeper into the medium. The cellulose pellicle thus formed is comprised of a mass of continuous layered cellulose fibers which support the growing population of Acetobacter cells at the air medium interface. The macroscopic and microscopic structures of the cellulose produced in accordance with the agitated culture conditions of the invention differ from that made pursuant to the known static culture conditions. Macroscopically, the invention cellulose forms in the culture as pellets rather than as a continuous pellicle at the air medium interface. Microscopically, the cellulose product according to the instant invention is characterized by a three dimensional reticular structure. This structure is characterized by frequently thickened strands of cellulose that interconnect forming a grid-like pattern extending in three dimensions. The bacterial cellulose produced in static cultures is characterized by overlapping adjacent strands of cellulose that are oriented predominantly with the long axis of the strand in parallel but disorganized planes. By contrast, the reticular structure of the cellulose product according to the present invention is characterized by interconnecting, rather than overlapping strands of cellulose. These interconnecting strands have both roughly perpendicular as well as roughly parallel orientations. As a result, the reticular cellulose product according to the invention has a more generally fenestrated appearance in scanning electron micrographs, whereas cellulose produced in static culture has an appearance in scanning electron micrographs of strands piled on top of one another in a crisscrossing fashion, but substantially parallel in any given layer. The strands of the cellulose product according to the invention are generally thicker than those produced in comparable media without agitation. The reticulated cellulose was composed of interconnecting filaments ranging in width from about 0.1 to about 0.2 microns. The filaments or strands of cellulose produced under non-agitated conditions ranged in width from about 0.05 to about 0.2 microns with many strands in the range of 0.05 to 0.10 microns. In addition, the fibrils of the non-reticulated cellulose product as compared to the fibrils of the reticulated product appear to branch and interconnect less frequently. Although the non-reticulated cellulose product appears to have many fibrils that contact one another, the fibrils overlay one another rather than interconnect. By contrast, the fibrils of the reticulated cellulose according to the invention, have a large proportion of fibers that interconnect to form a substantially continuous network of interconnecting fibers. The reticulated cellulose product according to the invention has several advantages over cellulose produced under non-agitated conditions. Because the reticulated cellulose product is characteristically produced in agitated cultures of cellulose producing microorganisms such as Acetobacter , it can be produced using conventional high volume fermentation methods. Thus, unlike the production of cellulose pellicles in the slow growing, motionless culture media of the prior art, the reticulated cellulose product of the present invention may be produced in fast growing cultures of Acetobacter with high volumetric productivity and high concentration of the reticulated cellulose product. One way the reticulated cellulose product according to the invention can be distinguished from bacterial cellulose produced under non-agitated conditions is by its characteristics upon consolidation into a paper-like sheet. Batches of the reticulated cellulose product offer a wide range of resistance to densification when formed into a hand sheet by conventional means such as dispersion in water with a British Disintegrator followed by forming in a sheet mold and pressing for various times. Some batches of the reticulated cellulose product were found to offer substantial resistance to densification when formed into handsheets by means such as those mentioned above. By use of different wet pressing loads, a series of sheets was prepared having densities in the range of about 300 to about 900 kg/m³, with those exhibiting substantial resistance to densification being about 300 to about 500 kg/m³. In spite of the low densities, these paper-like sheets have very high tensile strength as measured according to Technical Association of the Pulp and Paper Industry (TAPPI) method T494 om-81 using an Instron Universal test instrument. Typically, the tensile index for sheets of the density range of 300-500 kg/m³ is between 100 and 150 Newton-Meters/gram. Comparable sheets formed from kraft pulp having densities below about 500 kg/m³ have virtually no tensile strength. Handsheets formed from cellulose produced under static culture conditions do not exhibit the above-mentioned resistance to densification. Typically, such sheets from non-agitated cultures of cellulose have densities from about 500 to about 750 kg/m³ depending on the wet pressing load employed. The invention also pertains to a method for producing the reticulated cellulose product by culturing cellulose producing microorganisms for sustained periods of time under agitated culture conditions. The production of bacterial cellulose under agitated culture conditions is surprising in light of the well known tendency of agitated culture conditions to select for cellulose non-producing strains of Acetobacter . Valla et al., (1982). Moreover, the reticulated structure of the cellulose produced under these conditions is entirely unexpected. As used herein, the term Acetobacter refers to a genus of microorganisms, and in particular, to the members of that genus that produce cellulose. Although a number of microorganisms fitting this description are known, their taxonomic classification has been subject to debate. For example, the cellulose producing microorganisms listed in the 15th Edition of the catalogue of the American Type Culture Collection under accession numbers 10245, 10821, and 23769 are classified both as Acetobacter aceti subsp. xylinum and as Acetobacter pasteurianus . Thus, any cellulose producing strain of Acetobacter whether classified as Acetobacter aceti subsp. xylinum , Acetobacter pasteurianus or otherwise, that has the characteristics of stability under agitated culture conditions as further explained below, is considered to be within the scope of the invention. The inventors have discovered and developed a number of strains of Acetobacter that are stable in long term cultures under both non-agitated and agitated culture conditions including fermentor process conditions. The stability of the strains is demonstrated under agitated conditions; the strains according to the invention generally appear to change to cellulose non-producing types at a very low frequency, on the order of less than 0.5% at the end of a fermentation run of 42-45 generations, as determined by colony morphology when subcultures of Acetobacter grown in liquid medium under agitated conditions are plated on solid medium. The Acetobacter strains according to the invention have been mutagenized and a number of derivative strains have been selected. One of the selected strains and its progeny are characterized by a sharply reduced ability to form gluconic acid when grown on a glucose-containing medium. Such strains having a reduced ability to form gluconic acid are stable. At the end of a fermentation run of 42-45 generations, less than 0.5% gluconic acid producing types are detected as determined by the inability of sample subcultures from the fermentor broth to form calcium carbonate-clearing colonies on medium containing glucose. These strains are stable with respect to change to cellulose non-producing type and to change to gluconic acid producing type. Various feed stocks may be used as the carbon source for growth of the cellulose-producing microorganisms and reticulated cellulose product according to the invention so long as they are supplied free of contaminating organisms. Appropriate carbon sources include the monosaccharides and disaccharides in pure or partially purified form or as monosaccharide and disaccharide-containing stocks such as glucose derived from corn starch and molasses. Cellulose production with the strains according to the invention may be carried out under conditions permitting higher dissolved oxygen concentration than possible under standing conditions. The ability of the strain to maintain cellulose production while agitated permits various means for increasing dissolved oxygen in the culture medium to be used. Thus, direct agitation of the culture medium by impellers immersed in the medium has been used successfully, although adherence of the cellulose produced to the impeller blades can be a disadvantage. Means for agitating the culture which increase dissolved oxygen content are well known to those familiar with microbial fermentation. Oxygen tension in the broth can vary between 0.01 and 0.4 atmosphere oxygen. In tests in a fermenter (14 liters) using an impeller to agitate the broth, it was found that the characteristics of the broth (viscosity) and the resulting cellulose (particle size and morphology, settling rate, hand sheet formation) are affected by high impeller speeds (above about 600 rpm in the runs carried out). These effects were more pronounced the longer the cultures were agitated at such speeds. It is not known whether these results will apply to all fermenter volumes and configurations and/or methods of agitation. In the tests conducted, however, the higher impeller speeds/longer agitation times resulted in longer particle settling times, higher suspension viscosity, less cellulose retained in hand sheet tests, and smaller particles. Accordingly, depending on the intended end use for the cellulose, it may be desirable to avoid culturing the organisms under such agitation conditions. It is, therefore, preferred to carry out the fermentation at sufficiently low agitation rates and agitation times so as to avoid any substantial degradation of the properties of the cellulose product. The effective pH range for culturing the cellulose producing microorganisms according to the invention is between 4 and 6, with a preferred range of 4.5 to 5.5. pH may be controlled by means of buffers such as citrate added to the culture medium; or the addition of base or acid to the medium in an amount sufficient to maintain pH in the desired range. Figs. 1A and 1B are photographs showing the macroscopic structure of the reticulated cellulose product of the present invention. Fig. 1A shows the product before base extraction; Fig. 1B shows it after base extraction and purification. The dividing lines are approximately 1 mm apart. Fig. 2 is a scanning electron micrograph at magnification of 5000 X of non-reticulated cellulose produced under non-agitated conditions. Fig. 3 is a scanning electron micrograph at a magnification of 5000 X of the reticulated cellulose of the present invention. Fig. 4 is a scanning electron micrograph at a magnification of 10,150 X of non-reticulated cellulose produced under non-agitated conditions. Fig. 5 is a scanning electron micrograph of a magnification of 10,330 X of reticulated cellulose. Detailed Description of the Invention In the following detailed description of the invention a number of culture media are mentioned. Unless otherwise indicated the media are formulated as is indicated below. R20-2 medium has the following composition: R20-2 Bacto-peptone 5 g/l Yeast Extract 5 g/l Na₂HPO₄ 2.7 g/l Citric Acid 1.15 g/l Carbon Source As specified (if not specified, 2% glucose) Final pH 5.0 +/- 0.2 R20 is the same as above but final pH is 6.0. R20-3 is the same as above but citric acid is omitted. Y-1 medium, also referred to as minimal medium, has the following composition: For all studies using Y-1 medium the following vitamin mix was added to the minimal medium at a 100 fold dilution: Corn steep liquor (CSL) medium has the following composition: The composition of corn steep liquor varies depending on supplier and mode of treatment. A typical corn steep liquor sample, Lot E804 obtained from Corn Products Unit, CPV North America, Stockton, CA. is described below: Y3-3 medium has the following composition One aspect of the invention concerns a number of stable cellulose producing strains of Acetobacter . The stability of Acetobacter strains according to the invention is demonstrated by a very low frequency of conversion to phenotypes that do not produce cellulose. The frequency of conversion to phenotypes that do not produce cellulose is less than 5 x 10 -3 as determined by colony morphology when subcultures of Acetobacter grown under agitated conditions are plated on solid medium at the end of a fermentation cycle of 42-45 generations. The colonies of the cellulose-producing strains on solid medium are generally beige or white and are small, raised or convex and compact in size. By contrast cellulose non-producing strains form large, usually flat colonies on solid medium. The stable Acetobacter strains according to the invention were derived from an initial isolate of an initial isolate of an A. xylinum strain obtained from the Northern Regional Research Laboratory, Peoria, Illinois USA under Accession No. NRRL B42. Growth of the NRRL strain on agar plates of R20-2 medium revealed two colony morphologies, one white, the other beige. Microscopically, the beige colonies have the elongated rod shape cells typical of the Acetobacter strain. This strain is designated 1306-3. Unlike the parent NRRL B42 strain, 1306-3 produces no water soluble polysaccharide as reported by Couso, R.O. et al., Biosynthesis of Polysaccharides in Acetobacter xylinum ; Sequential Synthesis of a Heptasaccharide Diphosphate Prenol; Eur. J. Biochem. 123:617-627 (1982). Cultures of 1306-3 are stable in both microscopic morphology and macroscopic colony morphology when subcultured on different media containing a variety of carbon sources. Furthermore, colony and cellular morphology of the strain according to the invention remain stable whether grown in static or shaking liquid cultures in various media. Strain 1306-3 and its progeny are capable of producing cellulose in a variety of liquid culture media having various carbon and nitrogen sources. Casein hydrolysate, yeast extract, malt extract, ammonium salts, corn steep liquor and other nitrogen-rich substances can be used as a general source of amino acids, nitrogen, minerals and vitamins. Corn steep liquor is preferred in a range between 0.1% and 10% (v/v). 5% (v/v) corn steep liquor is preferred for shaking flask cultures. In fermentors an initial concentration of 2% (v/v) corn steep liquor is supplemented during the fermentation run with an additional 2% (v/v) corn steep liquor. Numerous carbon sources may be used including mannitol, sorbitol, sucrose, fructose and glucose, although using the latter carbon source, D-gluconic acid and ketogluconic acids, including 2-keto-D-gluconic acid or 5-keto-gluconic acid, are produced by strain 1306-3. Acetobacter strains according to the invention that produce significantly lower amounts of D-gluconic acid have also been developed by the inventors and are further described herein below. Carbons sources useful in the production of the reticulated cellulose product may be characterized as monosaccharides or mixtures thereof such as glucose and fructose, disaccharides such as sucrose, and mixtures of monosaccharide and disaccharides. In addition, the carbon source can be supplied as a complex mixture of sugars such as molasses, or plant biomass hydrolysates such as wood hydrolysate, straw, corn stalks, sorghum and the like. The concentration of monosaccharide and saccharide or mixtures thereof may vary. Glucose alone and fructose alone in a range of 0.5 to 7% (w/v) with a preferred concentration of about 4% (w/v) have been used. In addition, mixtures of glucose and sucrose in a ratio from 1:10 to 10:1 (w/w) having a total of 0.5 to 7% (w/v) of the medium may be used. A concentration of 1% (w/v) glucose and 2% (w/v) sucrose is preferred in flask cultures. In fed batch fermentation in which the carbon source is intermittently or continuously supplied during fermentation, the total carbon substrate added can vary between 4 to 30% (w/v). The carbon source may be supplied as a purified or partially purified feed stock or alternatively as a complex mixture such as molasses. Such carbon sources are pretreated so that they are free of contaminating organisms. The conversion of glucose to D-gluconic acid on glucose-containing medium leads to a significant drop in pH of the medium in batch culture. Since pH below about 4.0 may limit growth of the cells, pH control is desirable. pH control in liquid media culture of gluconic acid producing strains according to the invention can be effected by use of buffers such as citrate. However, the amount of buffer that can be added to neutralize the acid is limited and growth of gluconate-producing strains to high density is limited by the amount of buffer which can be added. In addition, the use of citrate or other salts as buffers adds to the expense of the culture medium. pH control can also be effected by using fructose as the carbon source, since Acetobacter does not metabolize fructose to acid. However, fructose is an expensive substrate and increases the production cost of the cellulose fiber. By treating strain 1306-3 with a mutagen, the inventors have developed stable variant strains exemplified by strains 1306-11 and 1306-21. These strains produce significantly reduced amounts of gluconic acid, yet produces cellulose in a stable manner typical of the parent strain 1306-3. Mutagenesis was accomplished using a concentration of ethyl methane sulfonate (EMS) sufficient to yield a survival rate of approximately 1%. In the case of strain 1306-11 of the surviving mutagenized bacteria, 8100 colonies were screened. Two isolates produced reduced amounts of gluconic acid. Strain 1306-11 was selected by culturing on plates of R20-CaCO₃ medium and screening for colonies having a morphology similar to the parent strain 1306-3 but which do not clear calcium carbonate in the medium. Other pH sensitive assays capable of detecting the absence of pH reducing substances such as gluconate can be used. Strain 1306-21 was selected as described in Example V, infra . Bacterial cultures may be grown under agitated culture conditions by any means known to generate turbulence in the liquid culture medium. Such means are well known to those skilled in the fermentation arts. At small scale, generally less than 10 liters culture volume, liquid cultures may be agitated by reciprocal or shaking incubators, which impart a swirling motion to the medium. At large scale, generally culture volumes exceeding 10 liters, the culture broth may be agitated by a number of means including impellers, buoyant lift fermentors including air lift fermentors, pump driven recirculation of the fermentor broth or combinations thereof. Various reactor designs may be appropriate for the large scale production for the cellulose product according to the invention. See e.g. , chapter 7 of Biochemical Engineering and Biotechnology Handbook , Atkinson and Mavituna, eds., 1st Ed. The Nature Press, New York, 1983. So long as the culture medium is agitated, various fermentation methods are appropriate for growing the cellulose producing microorganism at an average volumetric productivity for cellulose, which is within the scope of the invention, of at least 0.1 g/l/hr for sustained periods of time. Appropriate fermentation methods include batch fermentation, fed batch fermentations, repeated batch fermentation, and continuous fermentation. In batch fermentations the cellulose-producing microorganism is inoculated into a fermentation vessel and the fermentation proceeds without further addition of culture media. At the end of the fermentation, the contents of the fermentation vessel are collected and the cellulose is removed. In fed batch fermentations, various nutrients, such as carbon source or nitrogen source are added to the medium during the fermentation run without removing the fermentation broth for processing until the end of the fermentation run. The nutrients may be added continuously, at predetermined intervals or when nutrient levels in the medium fall below desired values. In repeated batch fermentations, a volume of the culture broth is removed for processing, a volume of fresh medium is added to the culture broth remaining in the culture vessel, and the fermentation is resumed. In repeated batch fermentations, as in fed batch fermentations, the nutrients may be added continuously, at predetermined intervals or when nutrient levels in the medium fall below desired values. In continuous fermentations, the broth is removed from the fermentation vessel and replaced with fresh medium at a constant rate. In continuous fermentations, by adjusting the flow of medium into and culture broth out of the vessel, the growth rate of the cellulose-producing microorganism can be maintained at an approximately constant rate. Batch fermentations, fed batch fermentations, repeated batch fermentations, and continuous fermentations are all suitable for achieving an average volumetric productivity of at least 0.1 g/l/hr so long as the inoculum of the culture medium is initially at least 1% (v/v). An inoculum in a range of 1-10% (v/v) of the culture medium is effective to obtain an average volumetric productivity of cellulose of 0.1 g/l/hr. An inoculum of about 5-10% (v/v) of the culture medium is preferred. In continuous cultures, as medium, cellulose-producing cells and cellulose are removed, fresh medium will be added at a rate sufficient to maintain the volumetric productivity at an average of at least 0.1 g/l/hr. To determine cellulose concentration and volumetric productivity, cellulose produced by any of the above mentioned fermentation methods is harvested from the fermentation broth. In general, any method for separating the cellulose may be used, but centrifugation is preferred. Each batch of fermentation broth containing the cellulose-producing microorganism, used medium, and cellulose, is centrifuged. The volume of the supernatant medium is determined and the supernatant is discarded. The pellet comprising solid matter including the microorganisms and cellulose is retained. The pellet is washed 2-3 times with deionized water to remove residual medium. Fig. 1A shows the macrostructure of the pellet at this stage. The retained matter is treated with an alkali solution such as 0.1 M NaOH or KOH at 60-65°C for at least two hours. The solution may be mixed to disperse large clumps of cellulose. During the alkali treatment, the mixture is slowly stirred and maintained at 60-65°C. The alkali treated material is centrifuged and the pellet is then washed and centrifuged three or four times in deionized water. Fig. 1B shows the macrostructure of the cellulose at this stage. The cellulose is then dried in a vacuum oven and is weighed. Volumetric productivity is defined as total mass of cellulose produced per volume of medium used per fermentation time from inoculation to harvest for batch cultures (g/l/hr.) The following examples are merely to be exemplary of the invention and are not intended to be limiting. EXAMPLE 1 This example shows cellulose production by A. xylinum 1306-3 growing on fructose as the main substrate under non-shaking conditions. Strain 1499-1 obtained from Dr. Moshe Benziman, Hebrew University, Jerusalem, Israel was grown under identical conditions for purposes of comparison. Seed flasks were set up containing 25 ml of Y3-3 medium with 2% fructose in 50 ml erlenmeyer flasks and were inoculated from agar slants. The cultures were grown for three days at 30°C as standing cultures. The flasks were vigorously shaken by hand to release cells and 0.5 ml of this culture (without cellulose pellicle was inoculated into several flasks of identical Y3-3 medium with 2% w/v fructose (25 ml in 50 ml flasks). Equal inoculation of all strains was accomplished using 0.03 OD at 670 nm cell suspension and inoculating 0.5 ml into each flask. The flasks were incubated at 30°C without shaking. Flasks were removed from incubation and the entire contents were harvested for sampling. Each strain was sampled in duplicate at each time point. Sampling was started when growth was evident and two samples were normally taken each day. To measure cellulose production, the flask contents of each sample were transferred to a 100 ml beaker. The suspension was then macerated for one minute with a large Tekmar probe at 50% of full power. The suspension was centrifuged at 5,000 rpm for 10 minutes. The supernatant was discarded and the pellet was resuspended in 15 ml 1.0 N NaCl saline and vortexed. The suspension was allowed to equilibrate for 15 minutes with occasional vortexing. The sample was again centrifuged and the above wash step repeated. The pellet from the second wash was resuspended in 15 ml of 0.5 N KOH and incubated at 60°C with mild agitation for 120 minutes. The suspension was centrifuged and the KOH supernatant discarded. The pellet was resuspended in 15 ml deionized H₂O and left at room temperature to equilibrate for 15 minutes with occasional vortexing. The sample was centrifuged and the above wash procedure was repeated for a total of four washes. After the last centrifugation step the wet cellulose mat was weighed and then dried at 55°C under vacuum overnight. EXAMPLE II Cellulose Production in Agitated Cultures: Stability Studies The stability of cellulose synthesis in strains 1306-3 and 1499-1 was examined during serial transfers of the strains in liquid agitated cultures, using a homogeneous inoculum in each transfer. Observation of cellulose production in the flasks and appearance of large colonies (L-colonies) from samples on plates was used to evaluate the stability of cellulose synthesis. Cellulose production in 1499-1 appeared to be unstable in aerobic agitated flasks as is shown by a reduction in the amount of cellulose produced and the appearance of increasing numbers of large diffuse colonies which represent cellulose non-producers. Cellulose production in 1306-3 appears to be stable for at least 30 generations in agitated flasks. Seed cultures were inoculated from agar slants of the parental culture into 25 ml of R-20 medium with 2% fructose at pH 5.0 in 50 ml Erlenmeyer flasks. The seed culture was grown for four days at 30°C as a standing culture. The flasks were shaken vigorously by hand to release cells and 0.5 ml of this culture (without cellulose pellicle) was inoculated into several flasks of the R20 medium with 2% fructose (25 ml in 50 ml flasks). These flasks were incubated at 30°C without shaking. After several transfers in standing flasks the 36 hour pellicle was vigorously shaken and the supernatant was used as inoculum (1% v/v) to the flasks containing R20 with 2% fructose, pH 5. The flasks (25 ml medium in 125 ml flasks) were incubated at 30°C and at 200 rpm in a New Brunswick gyratory shaker. After 24 to 48 hours the culture was aseptically blended and used as inoculum for second transfer into fresh medium and for streaking on plates. Each strain was examined for four transfers which is roughly equal to 30 generations. The medium used for plate experiments was R20 with 2% fructose, 1.5% agar, pH 5.0. During growth in shake flasks the culture of strain 1499-1 appeared as a fine suspension of cells and irregular clumps of different sizes. The ratio of clumps to cell suspension decreased from first transfer to the third transfer. This observation was correlated with a significant decrease in the amount of cellulose produced from first transfer to the third transfer, and an increase in the fraction of L-colonies which represent cellulose-non-producing strains. The frequency of L-colonies in strain 1499-1 as a function of growth is shown in Table 2. In sharp contrast, strain 1306-3, during growth in shake flasks, appeared as irregular clumps of different sizes with clear medium between them. Cellulose negative cells appear as single cells in the broth and cause turbidity in the medium between the clumps. No changes in the culture appearance or in the amount of cellulose produced were observed after four transfers. During that time the colonies on plates appeared to be homogeneous; no large, non-producing colonies were observed. EXAMPLE III Mutagenesis of Strain 1306-3 - Strain 1306-3 was mutagenized with 1% or 2% of the chemical mutagen ethyl methane sulfonate (EMS) and the surviving cells were screened for loss of the ability to synthesize gluconate (glcA-). Two glcA- isolates were obtained. The mutagenesis was carried out as follows: Two days old culture 1306-3 on R20-2 medium was used for the mutagenic treatment. Conditions were chosen to give about 99% kill. The conditions selected were 0.1 M potassium phosphate buffer, pH 6.0; 2% EMS and incubation at 28°C for 60 minutes. Cell concentration was approximately 5 x 10⁷ cells/ml. After this treatment the culture was kept frozen at -80°C for further use. EXAMPLE IV Screening for 1306-3 gluconate negative mutants was done with the material from the EMS mutagenesis. Screening was done on R20-2 plates containing 1% CaCO₃. These plates were made by adding sterile 20% CaCO₃ to sterile R20-2 to a final concentration of 1%, mixing well, and dispensing 10 ml per plate. Final pH of the plate medium was 6.0. Plates were incubated at 30°C and scored after 7-10 days. Colonies that had no zones of clearing were picked for verification screen. The colonies were suspended in sterile test tubes that contained 2 ml of R20-2 medium and incubated three days to check for pellicle formation and drop in pH of the broth. Of 8100 colonies screened, two isolates from the 2% EMS treated sample were found to be gluconic acid negative; the better of them was designated as 1306-11. Gluconic acid production by 1306-11 or 1306-3 was determined in liquid R20-glucose and Y1-glucose. Y1 with 2% glucose had an initial pH of 4.21. A loopful of 1306-11 or 1306-3 culture from an R20-2 plate was suspended in 2 ml of Y1 without carbon source. Cell counts for the suspensions were approximately 1.6 x 10⁸ cells/ml. Tubes (16 x 125 mm) containing 3 ml of the appropriate medium were inoculated with 200 µl of the cell suspension and mixed well by vortexing. Tubes were incubated, without shaking, at 30°C for three days. Table 3 shows the pH and gluconate levels at day three for the mutant 1306-11 and for 1306-3, the parent strain. Values are shown for each of the duplicate tubes. EXAMPLE V Preparation and Identification of Strain 1306-21 Strain 1306-3 was mutagenized as in Example III. Organisms were then plated out in CSL plates (2% glucose, 3% corn steep liquor) to establish single colonies. Colonies were picked and placed in microtiter tray wells containing .25 ml of CSL medium (4% glucose, 1% corn steep liquor). The trays were incubated 4-5 days until a clear drop in medium pH as measured with pH paper (range 2.9 to 5.2) was observed. Colonies whose pH was approximately 5 (pH paper green or greenish in color) were passed to a secondary screen. In the secondary screen, selected colonies were inoculated into test tubes containing 2 ml of the high glucose medium used in the microtiter tray wells as described above. The tubes were incubated at 30°C. Colonies were examined for pellicle formation and pH. A gluconic acid negative strain designated 1306.21 was selected in this manner. For comparison purposes, samples of strains 1306-11 and 1306-21 were grown in seed flasks containing CSL medium with varying amounts of glucose and corn steep liquor using the general procedure described in Example I. Cellulose production and medium pH were determined after five days of incubation. These determinations are reported in Table 4 below. As reported, strain 1306-21 exhibited lower acid production (higher pHS) and greater cellulose production than did strain 1306-11 in these tests. EXAMPLE VI Preparation of Reticulated Cellulose Product Strain 1306-14 is a spontaneous mutant of Acetobacter strain 1306-11. It was identified as a large white mucoid colony on R20-2 plates whereas 1306-11 colonies are characteristically even, convex and dark beige in color. A sample of 1306-14 from a frozen stock was inoculated into 100 ml R20-2 medium and was grown in static conditions at 30°C for about three days. The entire contents of the culture were transferred to a sterile blender. Using a small blender head, the culture was blended with short five second bursts. A 5% (v/v) inoculum of the disrupted culture was transferred into 400 ml of R20-2 medium in a 2000 ml baffled flask, and was cultured with shaking at 125 rpm at 30°C for about 2.5 days. The contents of the flask were blended and were used to inoculate fermentors. A 5% (v/v) inoculum of the disrupted culture from the baffled flasks was transferred into 9 1 or R20-2 medium with 2% glucose. The fermentor (Braun) was equipped with an impeller; internal heating coils and baffles were removed. Fermentation conditions during the run were: 600 rpm initially and increased to 1000 rpm after 44 hours to increase mixing of the culture medium which had became viscous. Temperature was controlled at 30°C (-1°C + 3°C). The pH was controlled at 5.0 ± 0.1 and oxygen concentration in the broth was maintained at about 30% of air saturation. At 48 hours the contents of the fermentor were collected. The cellulose was allowed to settle and excess liquid was poured off. The remaining cellulose was blended, washed and filtered as described above. The cellulose was washed with deionized (DI) water, extracted three times in 0.5 M NaOH at 60°C overnight. After the final extractions the cellulose was washed with DI until the pH of the wash water dropped below 6.0. The preparation was used for scanning electron microscopic examination as described in Example VIII. EXAMPLE VII Strain 1306-8 is an Acetobacter isolate selected directly from a sample of NRRL B42. Colonies of 1306-8 are characterized by white, highly raised colonies on R20-2 plates. Strain 1306-8 produced gluconic acid. A sample of 1306-8 from a frozen stock (2.5 ml) was inoculated into 100 ml R20-2 medium and was cultured under static conditions at 30°C in a 500 ml wide mouth Erlenmeyer flask. The seed culture was incubated about 2-4 days under these conditions until a visible pellicle formed. The entire contents of the seed culture were then blended and used to inoculate subsequent cultures. Fermentation was carried out with wide-mouth Fernbach flasks containing 1 liter of R20-2 medium with 0.025 ml of a 10 g/100 ml suspension of Benlate fungicide (Dupont) in a dimethyl formamide (DMF). This concentration of DMF and Benlate was effective to prevent fungal contamination without measurably affecting the growth of Acetobacter strain 1306-8. About 8-10 ml was used to inoculate 1 liter of R20-2 culture medium. The cultures were grown in the Fernbach flasks for 10-14 days at 30°C without agitation (i.e., standing cultures). At the time of harvest a 0.3 to 1.2 cm thick pellicles had formed. Pellicles were removed from Fernback flasks, then blended and washed with deionized water to remove media and part of the cells. Washing was done by filtration through a large buchner funnel using a filter screen (Spectramesh #146382) with mesh opening of 286 µM as a filter. Extraction of blended and washed pellicle was carried out in 0.50 M NaOH at about 60°C for about 14 hours. After mixing and incubating for the desired period of time, the extraction mixture was filtered under the conditions described above. Washes with deionized H₂O were continued until the pH of the wash water dropped below 6.0. The preparation was used for scanning electron microscopic examination. EXAMPLE VIII The cellulose product obtained in Examples VI and VII above were prepared for scanning electron microscopy. Specimens were freeze dried and then sputtered under vacuum with a 60:40 gold:palladium conductive film. Photomicrographs were taken using a Nanometrics scanning electron microscope operated at 16 Kv accelerating voltage. Figures 2 and 4 are representative electron micrographs of the cellulose product obtained. Figures 2 and 4 show the cellulose product produced in static cultures according to Example VII. The figures show that the product consists predominantly of piles of extended cellulose fibrils that appear to overlap and cross one another but do not appear to interconnect. The filaments of cellulose produced under static conditions ranged in width from about 0.05 to 0.2 microns with many strands in the 0.05 to 0.1 micron range. By contrast, Figures 3 and 5 show that the cellulose product produced in agitated culture in Example VI consists of a reticulum of fibrils that are generally thick in cross section - in a range between 0.1 to 0.2 microns - than the cellulose grown in static culture. In addition the cellulose fibrils appear to form a network or predominantly interconnecting, rather than overlapping, fibrils. EXAMPLE IX This example shows some of the characteristics of the reticulated cellulose product according to the invention. Handsheets were prepared from samples of Acetobacter -produced cellulose to an approximate basis weight of 60 g/m² according to the procedure described in TAPPI official test method T205 om-81. Cellulose was produced from strain 1306-3 under static growth conditions in a flask culture using R20-medium with 2% glucose. Reticulated cellulose product was produced using strain 1306-11 in a fermentor under agitation with an impeller at 600 rpm using the same medium. The broth containing the cellulose was cold-stored prior to processing the cellulose. The cellulose was dispersed (1.2 g in 2 litres of water) in a British Disintegrator for 150,000 revolutions. The suspension was then poured into an automatic sheet mold containing a 200-mesh wire screen and allowed to drain at least two hours. The moist handsheet (15 cm in diameter) was removed from the sheet mold and initially pressed gently between blotters to remove excess water. The sheet was then placed in a TAPPI press between blotters for varying times under a 50 psi (345 kPa) load to produce sheets of various densities. Final drying of the sheets was done by passing them through a Noble and Wood laboratory drum dryer. Tensile strength of sheets was measured according to TAPPI method T494 om-81 using an Instron Universal test instrument. The reticulated cellulose product of this Example was found to offer substantial resistance to densification when it was formed into a handsheet. By use of different wet pressing loads, a series of sheets was prepared having densities of about 300 to about 500 kg/m³. In spite of the low densities, these paper-like sheets have very high tensile strength. Typically, the tensile index for such sheets of the above density ranges in between 100 and 500 Newton-meters/gram. Comparable sheets formed from kraft pulp having densities below about 500 kg/m³ have virtually no tensile strength. Handsheets formed from cellulose produced under static culture conditions do not exhibit the above-mentioned resistance to densification. Typically, such sheets from non-agitated cultures of cellulose have densities from about 500 to about 750 kg/m³ depending on the wet pressing load employed. EXAMPLE X This Example compares the resistance to densification of reticulated cellulose produced under agitated culture conditions and non-reticulated cellulose produced under static conditions in two Acetobacter strains. Reticulated cellulose was obtained using strain 1306-14 under agitated growth conditions as described in Example VI. Non-reticulated cellulose was obtained using strain 1306-3 in static flask cultures using R20-2 medium -2% glucose under essentially the same static conditions described in Example VII. Handsheets were prepared from the reticulated cellulose and statically produced cellulose to an approximate weight basis of 60 g/m² as described in Example IX except that various pressing loads were used to produce the sheets. The density and other characteristics of sheet produced in this example from reticulated and non-reticulated cellulose are shown in Table 5. EXAMPLE XI Six strains were tested. 1306-3 and 1306-11 were as described herein above. Two subcultures of Acetobacter aceti sub sp. xylinum ATCC accession number 23769, designated herein as 23769A and 23769B were tested. In addition, ATTC strain 31174 and National Collection of Industrial Bacteria strain 8132 (Aberdeen, U.K.), and strain 1499-1 were also tested. The growth medium for pre-seed culture, seed culture and production stages was CSL medium with 4% (w/v) fructose and 5% (w/v) CSL. Pre-seed cultures were grown in 100 ml of the above-described medium in a 750 ml Falcon #3028 tissue culture flask with 0.01% Dow Corning antifoam under static conditions at 30°C for 24 to 48 hours. The entire contents of the pre-seed culture was blended as described previously and was used to make a 5% (v/v) inoculum of the seed culture. Pre-seeds were streaked on R20-2 plates to check for contamination. All strains had homogeneous colony morphology except strain 1499 which had approximately 50% large colonies. Seed cultures were grown in 25 ml of the above-described medium in baffled 125 ml flasks under shaking conditions in a reciprocal shaker at 125 rpm at 30°C for three days. A sample from each of the blended seeds was streaked on R20-2 plates to check for contamination. All strains had homogeneous colony morphology except 1499-1 which had approximately 50% large colonies. The entire remaining contents of the seed culture was blended as described previously and was used to make a 5% inoculum for the production stage. Duplicate fermentation flasks of each strain were grown in 125 ml baffled shake flasks on a reciprocal shaker at 125 rpm at 30°C. Duplicate flasks of each strain were harvested at days 1, 2, 3 and 4 except for ATCC strain 23769B which was harvested on day 7 due to poor growth. Strain 1499-1 and strain ATCC 31174 both produced a water soluble polysaccharide (WSP) under these conditions. No WSP was produced by strains 1306-3 or 1306-11. Cellulose production was determined for each strain and is reported in Table 6. Values for cellulose production are in g/l. EXAMPLE XII Cellulose production in fermentors: Pre-seed and seed cultures of 1306-11 were grown as in Example X for two days except that the medium contained 4% w/v glucose and 5% w/v CSL. Seed cultures were grown in the same medium for two days except that the culture volume was 400 ml in 2 l baffled flasks. Two fermentor runs in 14 l Chemap fermentors were run with a 5% (v/v) inoculum in initial 12 l volumes. During the 72 hour fermentor run, the cultures were maintained at about 30°C (±1°C). In fermentor #1 the initial glucose concentration was 32 g/l. In fermentor #2 the initial glucose and sucrose concentrations were 10 g/l and 20 g/l, respectively. One hundred and forty three g/l glucose was additionally added intermittantly to fermentor #1 during fermentation. In fermentor #2, 50 g/l glucose and 72 g/l sucrose was added intermittantly during fermentation. The initial 2% v/v CSL concentration was augmented by the addition of an amount equivalent to 2% by volume of the initial volume at 32 hours and 59 hours. The dissolved oxygen concentration was maintained at 30% air saturation. It fell in fermentor #2 to zero at hour 69 for about two hours of the fermentor run. Agitation was maintained initially at 600 rpm. As viscosity increased with increasing cellulose concentration, the impeller speed was increased to 1200 rpm. The concentrations of Cellulose, gluconic acid, and 2-keto-gluconic acid are shown for fermentor 1 in Table 7. The concentration of cellulose is shown for fermentor 2 in Table 8. The maximum cellulose concentration reached in the glucose only fermentor #1 was 12.7 g/l. The maximum cellulose concentration reached in the glucose/sucrose fermentor #2 was 18.3 g/l. Both maxima were reached in 71.6 hours into the fermentation. The volumetric productivities at this time in fermentor #1 and #2 were 0.18 and 0.26 g/l/hr., respectively. EXAMPLE XIII The fermentation described in Example XII was repeated using strain 1306-21 in place of 1306-11 and with the following changes: 1. The preseed and seed were prepared in CSL medium with 2% glucose, 2% corn steep liquor. 2. The agitation rate did not exceed 900 rpm. 3. The initial glucose concentration was 20 g/l, and 109 g/l more were added during the run. 4. Initial CSL concentration was 2% v/v and 2% v/v more were added after 27.8 hours in the run. The concentrations of cellulose, gluconic acid, 2-keto-gluconic acid and 5-keto-gluconic acid observed in this run are reported in Table 9. Comparing the results of Table 9 with those of Table 7, it appears that strain 1306-21 is equal to or better than strain 1306-11 as regards cellulose production while producing much less acid. Lower acid production should, in theory, permit strain 1306-21 to be grown to comparable concentrations with less base addition. EXAMPLE XIV Effects of Agitation on Cellulose Properties Two sets of tests were carried out to assess the effect of agitation on the following four properties: 1. Handsheet formation (TAPPI test of Example IX): the ability of purified, treated and resuspended cellulose fibers from the fermentation to form an integral sheet on a 150 mesh screen. The results are judged according to the percent of the resuspended fibers retained on the screen and to a qualitative assessment of the integrity of the sheet formed. 2. Settling rate: the rate at which a diluted sample of Cellulose from the fermenter settles in a graduated cylinder. The decreasing height of the sediment/supernatant interface of the settling suspension of cellulose is plotted versus time. The instantaneous settling rate can be determined from the slope of the plot at a given time. This property depends on the cellulose particle size and density. 3. Suspension viscosity: the viscosity of suspended cellulose fermenter broth measured by a Thomas-Stormer viscometer calibrated with glycerol solutions. This property depends on the morphology of the cellulose particles. 4. Particle size and morphology: This property is determined from photomicrographs of cellulose from the fermenter. The first set of tests consisted of four fermenter runs using strain 1306-11 during which samples were withdrawn as a function of time from 14 liter Chemap fermenters operated at varying rates of maximum agitation. These four fermenter runs were typical fermentations with growing cultures, but extended past normal fermentation times to allow evaluation of the effect of agitation over prolonged time. Samples from these runs were analyzed for handsheet formation ability. The second set of experiments consisted of agitating old, non-growing cellulose cultures, harvested from a 250 liter fermenter run, in four 14 liter Chemap fermenters. The agitation rate was constant in each fermenter, but was varied among fermenters. Samples were taken with respect to time from each fermenter. The cellulose concentration in this set of experiments was uniform in all the fermenters, but was approximately half the concentration of the final concentrations in the first set of experiments. In this second set of experiments, nitrogen was sparged at about the average gassing rate (air and oxygen) of the first set of experiments. Samples from the second set of experiments were analyzed for handsheet formation, settling rate, viscosity, and particle size and morphology. Handsheet results from the first and second sets of experiments are summarized in Tables 10 and 11, respectively. Table 10 shows that handsheet formation may be adversely affected by both increased agitation rate and increased time of agitation. The results in Table 11 in which more dilute and non-growing cellulose cultures were used showed handsheet formation to be not as sensitive to the agitation rate and time as shown in Table 10. Good handsheets could be made up to 86 hours at 800 rpm or 27 hours at 1000 rpm agitation. The better results in Table 11 may be due to lower cellulose concentration in the fermenter or higher target sheet weights. Other test results do, however, show cellulose properties being affected by agitation rate and time during the second set of experiments. For instance, the viscosity analyses indicate increasing viscosity of the cellulose suspension in the fermenter with agitation time at 800 and 100 rpm. The increased viscosity may reflect the change in the morphology of the cellulose from dense pellets to less densely packed fiberlike form. Such changes were observed in the photomicrographs used to evaluate particle size and morphology. The settling rate studies showed that cellulose agitated at higher rates or for longer times settles more slowly. These results were consistent with the photomicrographs which showed that with increased agitation rate and time the cellulose particles appear to become smaller fibers that are less densely packed. The general results from analyses of the settling rates, viscosities, particle size and form, and handset formation, all appear consistent and to some extent, correlate with each other. The mechanism of change of the cellulose properties with agitation rate and time is not understood completely at this time. It is known that increased agitation rates increase the shear stress on the cellulose particles. However, other forces may also be contributing to the changing cellulose properties; examples include turbulent eddy stresses and cavitation forces. Furthermore, the above forces and stresses, as well as others, are also exerted during recovery and purification of the cellulose. Accordingly, caution must be exercised during all stages of cellulose processing to minimize damage to the cellulose. The present invention also provides for the production by microbial means of a reticulated cellulose product wherein the cellulose strands form a substantially continuous network of branching interconnected cellulose strands. This production may be by a microorganism designated Acetobacter which has the ability to produce a cellulose product under agitated culture conditions and a frequency of change to cellulose non-producing forms under agitated culture conditions as determined by the appearance of cellulose non-producing colonies on solid medium of less than 0.5% over the course of 42045 generations, said microorganism preferably showing substantially reduced D-gluconic acid production when grown on D-glucose-containing medium. It will be appreciated from the foregoing that bacterial cellulose may be produced at high efficiency under agitated conditions for sustained periods of time. Heretofore the sustained production of bacterial cellulose at high productivity has been fraught with difficulties and extremely low productivities. The invention disclosed herein and claimed below clearly represents a major advance in fermentative production of bacterial cellulose. Samples of strains 1306-3, 1306-11, and 1306-21 were deposited under the terms of the Budapest Treaty on the International Recognition of the Deposit of Microorganisms for the Purposes of Patent Procedure and Regulations thereunder at the American Type Culture Collection, 12301 Parklawn Drive, Rockville, Maryland USA 20832. Deposit dates and accession numbers are given below: Said deposits were made pursuant to a contract between the ATCC and the assignee of this patent application, Cetus Corporation. The contract with the ATCC provides for permanent availability of said strains and progeny thereof to the public upon issuance of a U.S. patent related to this application describing and identifying the deposit or upon the publication or laying open to the public of any U.S. or foreign patent application, whichever comes first, and for the availability of these strains and the progeny thereof to one determined by the U.S. Commissioner of Patents and Trademarks to be entitled thereto according to 35 USC §122 and the Commissioner's rules pursuant thereto (including 37 CFR §1.14 with particular reference to 886 0G 638). The assignee of the present application has agreed that if the strains on the deposit should die or be lost or destroyed when cultivated under suitable conditions, it will be promptly replaced upon notification with a viable culture of the same strain. The deposits under the terms of the Budapest Treaty assures that said cultures deposited will be maintained in a viable and uncontaminated condition for a period of at least five years after the most recent request for the furnishing of a sample of the deposited microorganism was received by the ATCC and, in any case, for a period of at least 30 years after the date of the deposit. Availability of the deposited strains is not to be construed as a license to practice the invention in contravention of the rights granted under the authority of any government in accordance with its patent laws. Also, the present invention is not to be considered limited in scope by the strains deposited, since the deposited embodiments are intended only to be illustrative of particular aspects of the invention. Any microorganism strains which are functionally equivalent to those deposited are considered to be within the scope of this invention. Further, various modifications of the invention in addition to those shown and described herein apparent to those skilled in the art from the preceding description are considered to fall within the scope of the appended claims. With the information contained herein, various departures from the precise description of the invention will be readily apparent to those skilled in the art to which the invention pertains without departing from the scope of the invention.

Claims: Reticulated cellulose obtainable from a miroorganism designated Acetobacter having the ability of microorganisms obtainable from ATCC 53264, ATCC 53263 and ATCC 53524 to produce a cellulose product under agitated culture conditions, which product is obtainable under conditions of continuous culture agitation resulting, when viewed with a scanning electron microscope, in a reticulated structure having frequently thickened strands that interconnect to form a grid-like pattern extending in three dimensions and demonstrating resistance to densification when formed into sheets by sheet forming-means. A sheet comprising reticulated cellulose as claimed in Claim 1. A sheet as claimed in Claim 2 wherein said sheet is formed to a basis weight of about 60 g/m² and a thickness between about .15 and about .22 mm, and has a density ranging from about 250 kg/m³ to about 430 kg/m³. A sheet as claimed in Claim 2 wherein said sheet is formed to a density in a range between about 300 and about 500 kg/m³, and has a tensile index in a range between about 100 and 150 newton-meters/gram. A method of producing a reticulated cellulose as defined in Claim 1 comprising: a) culturing, under agitated conditions, a microorganism designated Acetobacter having the ability of microorganisms obtainable from ATCC 53264, ATCC 53263 and ATCC 53524 to produce a cellulose product under agitated culture conditions, in a liquid medium suitable for cellulose production at an average volumetric productivity of at least 0.1 g/1/hr over a period of time exceeding 70 hours, said micro-organism having a frequency of change in agitated culture conditions from cellulose producing forms to cellulose non-producing forms of less than 0.5% over the course of 42-45 generations, as determined by the appearance of cellulose non-producing colonies on solid medium, and b) removing the reticulated cellulose product obtained. A microorganism designated Acetobacter and having the ability of microorganisms obtainable from ATCC 53264, ATCC 53263 and ATCC 53524 to produce a cellulose product under agitated culture conditions, and having a frequency of change from cellulose producing forms to cellulose non-producing forms under agitated culture conditions, as determined by the appearance of cellulose non-producing colonies on solid medium, of less than 0.5% over the course of 42-45 generations. A microorganism designated Acetobacter and having the ability of micro-organisms obtainable from ATCC 53264, ATCC 53263 and ATCC 53524 to produce a cellulose product under agitated culture conditions and which produces reduced amounts of gluconic acid and ketogluconic acids when grown on D-glucose-containing medium. A biologically pure culture of Acetobacter xylinum obtainable from ATCC 53264, ATCC 53263 or ATCC 53524.

Inventors: ALONI, YEHOSHUA, BEN-BASSAT, ARIE, BRUNER, ROBERT, JOHNSON, DONALD CURTIS, NAOGI, AMAR NATH, SHOEMAKER, SHARON PAYNE, WONG, HARRY
Applicants: WEYERHAEUSER CO
Application year: 1986
Main classification: C12P19
IPC codes: C08B15, C12R1, C12P19, C08L1, C12N1, A61L15