COLOR STABILIZERS FOR ZINC DITHIOPHOSPHATES

Abstract: A small amount of hydrogen sulfide, an olefin, a mercapatan, an epoxide, a phosphite or a phosphine are added to a zinc dialkyldithiophosphate salt to decrease the rate of color generation upon storage and/or exposure to heat.

Description: The field of this invention relates to a composition comprising a lubricant oil additive useful as an inhibitor of engine wear, lubricant oxidation and engine part corrosion. More particularly, this invention relates to a composition of a lubricating oil additive comprising an oil-soluble zinc dialkyldithiophosphate wherein addition of small amounts of a compound selected from the group consisting of olefins, mercaptans, epoxides, phosphites, and phosphines decreases the rate of oxidation of the zinc dialkyldithiophosphate under conditions of heat and/or prolonged storage. The decreased rate of oxidation decreases the rate of color generation or color formation. It is an object of this invention to provide a composition comprising a wear inhibitor which has increased oxidative stability as an additive in a lubricating oil composition and good color stabilization in storage at elevated temperatures. It is an object of this invention to provide a composition comprising a wear inhibitor mixture which has improved oxidative stability in a lubricating oil composition wherein the wear inhibitor comprises an oil-soluble zinc dialkyldithiophosphate. It is an object of this invention to provide a process for the preparation of a wear inhibitor mixture which demonstrates improved color stability at elevated temperatures. These and other objects will become apparent from the description given hereafter. Oil-soluble zinc dithiophosphates are used as compounding agents or additives in lubricating oils to inhibit engine wear, to inhibit oxidation of the lubrication oil, and to inhibit engine part corrosion. It is highly desirable for such oil-soluble zinc dialkyldithiophosphates to provide the aforesaid properties to the lubricating oil without affecting the appearance characteristics of the formulated lubricant composition even though the performance characteristics of the lubricant composition may not be affected noticeably. As is well known, oil-soluble zinc dialkyldithiophosphates are conventionally prepared by reacting monohydric alcohols or phenols with phosphorus pentasulfide, usually in a mole ratio of 4:1, alcohol to phosphorus pentasulfide, in the presence of a diluent oil at a temperature within the range of from about 70°C to about 135°C to form partial esters of dithiophosphoric acid, a green odoriferous liquid. The so-obtained partial esters are then neutralized with zinc oxide at a temperature within the range of from about 70°C to about 135°C to form a zinc dialkyldithiophosphate, typically a light yellow liquid. It has been found that, upon storage, the zinc dialkyldithiophosphate prepared as described often will acquire a dark objectionable color, often of a brownish hue. The dark color is objectionable as it affects the marketing of the zinc dialkyldithiophosphates. The dark product has been considered as inferior to product of a light color. It has long been known that the metal salts of partial esters of dithiophosphoric acids can be decolorized by incorporation of a small amount of a trialkylolamine whose alkylol groups contain 1 to 4 carbon atoms each. U.S. Patent 2,983,742 teaches that excellent results have been obtained with triethanolamine but other amines of the class disclosed can be used. Amounts can be used of from 0.25 to 1.0 percent by weight. U.S. Patent 3,361,668 teaches and claims a lubricating composition containing light-colored metal phosphorodithioates wherein the said phosphorodithioate is prepared by reacting phosphorus pentasulfide with a mixture of from about 95% to 99.95% by weight of a monohydroxy alcohol or phenol having from 1 to 30 carbon atoms and from about 0.05% to 5.0% by weight of an alkyl amine, cycloalkylamine or heterocyclic amine having up to about 20 carbon atoms. In an alternative procedure, the phosphorodithioic acid diester is first prepared and a small amount of a suitable amine is then added. In the prior art, it has been postulated that the cause of the dark color in metal salts of dithiophosphate esters is the presence of traces of heavy metals, principally iron, in the phosphorus pentasulfides. U.S. Patent 2,983,742, Boba, et al, considers that addition of a trialkylolamine forms complexes with traces of the heavy metal compounds in the dithiophosphate ester salt that are more stable than the uncomplexed metal compounds. However, Boba, et al, '742 indicate this postulate is somewhat negatived by the fact that other agents capable of forming complexes with heavy metal compounds do not produce equivalent results. Wiese, U.S. Patent 3,361,668, teaches that commercially prepared phosphorodithioic acid diesters are sufficiently strong acids to be corrosive to metals and the use of special corrosion-resistant equipment is generally required in their manufacture. Wiese '668 teaches that the corrosiveness of the phosphorodithioic acid esters upon mild steel is shown to be reduced in the presence of an amine-reacted product of a phosphorodithioic acid ester. Wiese '668 accordingly teaches that the amine-reacted product of a phosphorodithioic acid is less reactive to iron compounds and retains its light color as prepared. A procedure has now been found for achieving the objects of the invention. In this procedure a small amount of hydrogen sulphide, an olefin, a mercaptan, an epoxide, a phosphite or a phosphine is added to a zinc dialkyldithiophosphate salt to decrease the rate of color formation or color generation upon storage and/or exposure to heat. Specifically, according to the invention there is provided a process comprising incorporating in a metal salt of a partial ester of dithiophosphoric acid a small amount, sufficient to decrease the rate of color generation in the product, of a color stabilizer compound selected from hydrogen sulfide, an olefinically unsaturated compound of from 2 to 100 carbon atoms, a mercaptan of from 4 to 40 carbon atoms, an epoxide of from 2 to 100 carbon atoms, trialkyl or triarylphosphites of the formula (RO)₃P where R is an alkyl group or an aryl group of from 1 to 30 carbon atoms, trialkylphosphines of the formula R¹₃P where R¹ is an alkyl group of 1 to 20 carbon atoms, said small amount being not greater than 1.0 (wt) %, of the weight of said metal salt. The invention further provides a composition comprising a major portion of metal salt of a partial ester of dithiophosphoric acid and a small amount of a color stabilizer compound selected from hydrogen sulfide, an olefinically unsaturated compound of from 2 to 100 carbon atoms, a mercaptan of from 4 to 40 carbon atoms, an epoxide of from 2 to 100 carbon atoms, trialkyl or triarylphosphites of the formula (RO)₃P where R is an alkyl group of a phenyl group of from 1 to 30 carbon atoms, trialkylphosphines of the formula R¹₃P where R¹ is an alkyl group of from 1 to 20 carbon atoms, said small amount being not greater than 1.0 (wt) % of the weight of said metal salt. Expressed in terms of a molar ratio, it is preferred that at least 0.0001 mole of said color stabilizer compound is added per mole of said metal salt of a partial ester of dithophosphoric acid. In more detail it has now been found unexpectedly that acid salts comprising zinc dialkyldithiophosphates substantially retain their original light color despite exposure to elevated temperatures for prolonged periods of time upon the addition of color stabilizers in a concentration of not greater than 1.0 (wt) % of the weight of the zinc dialkyldithiophosphate metal salt. A preferred range is 0.002 to 0.05 mole of stabilizer per mole of zinc dialkyldithiophosphate. The color stabilizers are added after the dialkyldithiophosphoric acid diester is neutralized with zinc oxide to prepare the zinc dialkyldithiophosphate. Some of the color stabilizers are preferably added to the dialkyldithiophosphoric acid diester before it is neutralized with zinc oxide. The color stabilizers comprise hydrogen sulfide, olefins, mercaptans, epoxides, phosphites, and phosphines. Although the mechanism has not been definitely established by which the color stabilizers cause the zinc dialkyldithiophosphate to retain a light color, it is believed that the addition of the aforementioned color stabilizers decreases the rate of oxidation of the zinc dialkyldithiophosphate under conditions of heat and/or prolonged storage; nor has the darkening of the zinc dialkyldithiophosphate been definitely established as having been caused by the presence of oxygen and consequent oxidation of the dithiophosphates esters. It is also considered that traces of other compounds may be present which react with zinc dialkyldithiophosphate to cause a darkening of the ester. 0,0'-phosphorodithioic acid diesters are manufactured by reacting about 4 equivalents of an organic monohydroxy compound, e.g., an alcohol or a phenol with one mole of phosphorus pentasulfide at temperatures of from about 70°C to about 135°C with the evolution of hydrogen sulfide as illustrated by the following equation: The oil-soluble metal phosphorodithioate diester salts are usually manufactured by neutralizing the phosphorodithioic acid diester with a basically reacting metal compound, preferably the oxide, frequently with a small amount of water added, at temperatures of from about 50°C to about 150°C. A phosphorodithioic acid diester is usually assumed to have the structure shown in the above equation wherein the thiol group attached to the phosphorus atom accounts for its relatively strong acidic character. In addition, unless the alcohols used are anhydrous, traces of water which are present in the reaction mixture react with the phosphorus pentasulfide to cause the formation of small amounts of monoesters of phosphorodithioic acid or phosphoromonothioic acid and even some unesterified phosphorus and sulfur-containing acids. Suitable monohydroxy organic compounds useful in the preparation of the improved 0,0'-diesters of phosphorodithioic acid include alcohols, phenols, and alkyl phenols, including their substituted derivatives, e.g., nitro-, haloalkoxy-, hydroxy- or carboxy-. Suitable alcohols include, for example, methanol, ethanol, n-propanol, isopropanol, n-butanol, 2-butanol, 2-methyl-propanol, n-pentanol, 2-pentanol, 3-pentanol, 2-methylbutanol, 3-methyl-2-pentanol, n-hexanol, 2-hexanol, 3-hexanol, 2-methyl-2-pentanol, 4-methyl-3-pentanol, cyclohexanol, chlorocyclohexanol, methylcyclohexanol, heptanol, 2-ethylhexanol, n-octanol, 2,2-dimethyloctanol, nonanol, dodecanol, octadecanol and eicosanol,. The phenols suitable for the purposes of this invention include alkyl phenols and substituted phenols, e.g., phenol, chlorophenol, bromophenol, nitrophenol, methoxyphenol, cresol, propylphenol, butylphenol, amylphenol, heptylphenol, octylphenol, nonylphenol and octadecylphenol. Ordinarily, the monohydroxy organic compounds suitable for purposes of this invention may have from 1 to 30 carbon atoms. Mixtures of monohydroxy organic compounds can also be used without penalty to produce oil-soluble metal salts. Alcohols most frequently used are isobutanol, isoamyl, alcohol, isooctanol, 2-propanol, 4-methyl-2-pentanol, capryl alcohol, and nonylphenol. The color stabilizers suitable for use in this invention for preparing the improved zinc dialkyldithiophosphate include olefins, mercaptans, epoxides, phosphites, and phosphines. Olefinic compounds useful as color stabilizers can be selected from a large variety of compounds containing olefinic double bonds such as alpha olefins of 2 to 100 carbon atoms, cyclic olefins such as cyclohexene, dicyclopentadiene, terpenenes, and olefinic compounds with functional groups such as allyl and oleyl alcohol, acrylic acid, and methacrylic acid and their esters, oleic acid, styrene, vinylethers, vinylesters, and vnylpyrrolidone. Mercaptans can be selected from primary, secondary, or tertiary mercaptans of 4 to 40 carbon atoms; H₂S can also be used as a color stabilizer. Epoxides are selected from compounds with 2 to 100 carbon atoms, such as epoxybutane or epoxidized soybean oil. Trialkyl or triarylphosphites can be selected from compounds of the formula (RO)₃P where R is an alkyl group or a phenyl or substituted phenyl group of from 1 to 30 carbon atoms. Trialkylphosphines have the general formula R₃P where R is an alkyl group of from 1 to 20 carbon atoms. The proposed color stabilizers are usually added after the dialkyl dithiophosphoric acid is neutralized with zinc oxide. Some of the stabilizers such as phosphites, phosphines, or mercaptans can be added before neutralization with zinc oxide is completed. The color stabilizing additive can be added in concentrations ranging from 0.0001 to 0.5 mole of stabilizer per mole of zinc dialkyldithiophosphate (ZnDTP). A preferred range is 0.002 to 0.05 mole of stabilizer per mole of zinc dialkyldithiophosphate (ZnDTP). The following examples are illustrative of typical compositions of the instant invention and the results obtainable therefrom. EXAMPLE I A sample of 50g ZnDTP was added to a bottle of the dimensions 37 x 155 mm equipped with a screw cap. Color stabilizers were added and mixed with the ZnDTP. After storing the bottles in an oven, the ASTM color of the test samples was measured in a standard apparatus for measuring ASTM color as described in ASTM D-1500. The ASTM procedure uses a color scale ranging from 0.5 to 8.0 color units, 0.5 being light and 8.0 dark in color. A ZnDTP composed of 50 mole % 2-propyl and 50 mole % 4-methyl-2-pentyl alkyl groups was tested; elemental analysis of ZnDTP was: Zn - 8.96%, P - 8.12%, storage temperature 75°C. EXAMPLE II A storage test with ZnDTP of a test series was carried out at 93°C. ASTM D-1500 Color Additive % (wt.) 0 Hrs. 72 Hrs. 15. No Additive (Control) -- 2.0 6.5 16. Epoxybutane 0.62 2.0 3.0 17. Triethylphosphite 0.62 2.0 2.0 18. d-Limonene 0.30 2.0 3.0 EXAMPLE III A ZnDTP composed of 65 mole % isobutyl, 25 mole % isoamyl, and 10 mole % isooctyl alkyl groups was tested; elemental analysis of ZnDTP was: Zn - 8.75%, P - 7.76%, storage temperature - 93°C. ASTM D-1500 Color Additive % (wt.) 0 Hrs. 72 Hrs. 19. No Additive (Control) -- 3.0 7.5 20. C₁₅₋₂₀ alpha Olefin 0.57 3.0 3.5 21. I-Dodecylmercaptan 0.62 3.0 4.0 22. Epoxybutane 0.53 3.0 3.5 23. Triethylphosphite 0.61 3.0 3.0 24. Tri-n-Butylphosphine 0.52 3.0 3.0 EXAMPLE IV A ZnDTP composed of 50 mole % 2-propyl and 50 mole % isooctyl alkyl groups was stored at 93°C; elemental composition of ZnDTP was: Zn - 8.06%, P - 7.13%. ASTM D-1500 Color Additive % (wt.) 0 Hrs. 72 Hrs. 25. No Additive (Control) -- 2.0 7.5 26. C₁₆ alpha Olefin 0.31 2.0 4.0 27. Allyl Alcohol 0.46 2.0 3.0 28. Epoxybutane 0.54 2.0 3.5 29. Triethylphosphite 0.30 2.0 3.5 30. Tri-n-Butylphosphine 0.29 2.0 2.5 31. I-Dodecylmercaptan 0.61 2.0 3.5 EXAMPLE V In the procedure of Example I, amine compounds were added to samples of ZnDTP and stored at 200°F (93°C) for 46 and 70 hours. Colors were determined according to ASTM D-1500. Results are in the following table.

Claims: A process for decreasing the rate of color generation in a metal salt of a partial ester of dithiophosphoric acid which comprises incorporating a small amount, sufficient to decrease the rate of color generation in the product, of a color stabilizer compound selected from hydrogen sulfide, an olefinically unsaturated compound of from 2 to 100 carbon atoms, a mercaptan of from 4 to 40 carbon atoms, an epoxide of from 2 to 100 carbon atoms, trialkyl or triarylphosphites of the formula (RO)₃P where R is an alkyl group or an aryl group of from 1 to 30 carbon atoms, trialkylphosphines of the formula R¹₃P where R¹ is an alkyl group of 1 to 20 carbon atoms, said small amount not being greater than 1.0 (wt) % of the weight of said metal salt. The process of claim 1 wherein said olefinically unsaturated compound is selected from alpha olefins of from 15 to 20 carbon atoms, dipentene, styrene, alpha methyl styrene, oleyl alcohol, d-limonene, dicyclopentadiene and allyl alcohol. The process of claim 1 wherein said mercaptan is selected from 1-dodecylmercaptan and tertiary dodecylmercaptan. The process of claim 1 wherein said epoxide is selected from epoxybutane and epoxidized soyabean oil. The process of claim 1 wherein said phosphine is tri- n -butylphosphine. The process of claim 1 wherein said phosphite is trimethylphosphite. The process of any preceding claim wherein said metal salt of a partial ester of dithiophosphoric acid is a zinc dialkyldithiophosphate. The process of any preceding claim wherein at least 0.0001 mole of said color stabilizer compound is added per mole of said metal salt of a partial ester of dithiophosphoric acid. The use as a color stabilizer for a metal salt of a partial ester of dithiophosphoric acid, of a compound selected from hydrogen sulfide, an olefinically unsaturated compound of from 2 to 100 carbon atoms, a mercaptan of from 4 to 40 carbon atoms, an epoxide of from 2 to 100 carbon atoms, trialkyl or triarylphosphites of the formula (RO)₃P where R is an alkyl group or a phenyl group of from 1 to 30 carbon atoms and trialkylphosphines of the formula R¹₃P where R¹ is an alkyl group of from 1 to 20 carbon atoms, said selected compound being used in small amount being not greater than 1.0 (wt) % of the weight of said metal salt. The use of claim 9 wherein said metal salt of a partial ester of dithiophosphoric acid is a zinc dialkyldithiophosphate. The use of claim 9 or claim 10 wherein said olefinically unsaturated compound is selected from an alpha olefin of from 15 to 20 carbon atoms, dipentene, styrene, alpha methyl styrene, oleyl alcohol, d-limonene, dicyclopentadiene and allyl alcohol. The use of claim 9 or claim 10 wherein said mercaptan is selected from 1-dodecylmercaptan and tertiary dodecylmercaptan. The use of claim 9 or claim 10 wherein said epoxide is selected from epoxybutane and epoxidized soyabean oil. The use of claim 9 or claim 10 wherein said phosphine is tri- n -butylphosphine. The use of claim 9 or claim 10 wherein said phosphite is trimethylphosphite. A composition comprising a major portion of a metal salt of an ester of dithiophosphoric acid and a small amount of color stabilizer compound selected from hydrogen sulfide, an olefinically unsaturated compound of from 2 to 100 carbon atoms, a mercaptan of from 4 to 40 carbon atoms, an epoxide of from 2 to 100 carbon atoms and trialkylphosphines of the formula R¹₃P where R¹ is an alkyl group of from 1 to 20 carbon atoms, said small amount being not greater than 1.0 (wt) % of the weight of said metal salt. The composition of Claim 16 wherein said olefinically unsaturated compound is selected from an alpha olefin of from 15 to 20 carbon atoms, dipentene, styrene, alpha methyl styrene, oleyl alcohol, d-limonene, dicyclopentadiene and allyl alcohol. The composition of Claim 16 or Claim 17 wherein said metal salt of an ester of dithiophosphoric acid is a zinc dialkyldithiophosphate. The composition of Claim 16 or 18 wherein said mercaptan is selected from 1-dodecylmercaptan and tertiary dodecylmercaptan. The composition of Claims 16 or 18 wherein said phosphine is tri-n-butylphosphine.

Inventors: CASPARI, GUNTER JOSEPH, VALCHO, JOSEPH JAMES
Applicants: AMOCO CORPORATION
Application year: 1986
Main classification: C07F9
IPC codes: C10M137, C10M163, C10N30, C10N40, C10N10, C10M159, C07F9