A CONTINUOUS PROCESS FOR PRODUCING 5-VINYL-2-NORBORNENE

Abstract: A continuous process for producing 5-vinyl-­ 2-norbornene, useful as the raw material of 5-ethylidene-­ 2-norbornene used as a termonomer for EPDM, from a mixture of cyclopentadiene and butadiene or from a mixture of cyclopentadiene and dicyclopentadiene and butadiene by the Diels-Alder reaction which process comprises adding from l0 to l0,000 ppm of N,N-diethylhydroxylamine or 4-­ oxo-2,2,6,6-tetramethylpiperidine-l-oxyl relative to the total weight of cyclopentadiene and butadiene or of a mixture of cyclopentadiene and dicyclopentadiene and butadiene, continuously introducing the resulting mixture into a pressure reaction vessel, allowing them to react in the absence of any gas phase portion within the said pressure reaction vessel, and continuously withdrawing the reaction product.

Description: This invention relates to a continuous process for producing 5-vinyl-2-norbornene which comprises continuously introducing cyclopentadiene and butadiene or a mixture of cyclopentadiene and dicyclopentadiene and butadiene in the presence of N,N-diethylhydroxylamine or 4-oxo-2,2,6,6-tetramethylpiperidine-l-oxyl into a pressure reaction vessel, allowing them to react in the absence of any gas phase portion within said pressure reaction vessel, and continuously withdrawing the reaction product. 5-Vinyl-2-norbornene is very useful as the raw material of 5-ethylidene-2-norbornene used as a termonomer for EPDM. The Diels-Alder reaction is characterized by the additive reaction of an olefin having an activated double bond (a dienophile) with a conjugated diene. Since the reaction proceeds thermally, it is desirable in this respect to carry out the reaction at relatively high temperature, for example at from 70 to 250°C. However, in such a high temperature reaction, cyclo­ pentadiene and butadiene of the raw material and cyclic olefins of the reaction product are liable to polymerize, which causes such troubles as clogging of the apparatus due to the deposition and adhesion of polymer and formation of polymer film on the inner wall surface of the apparatus, making long-time continuous operation difficult in practice. As to the means for preventing the polymerization of reactants in the Diels-Alder reaction conducted at relatively high temperature, for example British Patent No. 923,462 discloses the addition of organic cobalt compounds and U.S. Patent No. 3,20l,484 discloses the addition of organic nickel compounds. However, since these compounds are unstable in the air and hence are troublesome to handle, they are unsuitable to be used in carrying out the Diels-Alder reaction in practice. Further, Japanese Patent Application Kokoku (Post-Exam. Publn.) No. 7,l3l/82 discloses the use of p-phenylene­ diamine or the like as the polymerization inhibitor, but their effect is not satisfactory. Another problem involved in this Diels-Alder reaction is that since both of the reactants are a diene and act as a dienophile, a large variety of reaction products are formed in the reaction. Thus, in addition to intended 5-vinyl-2-norbornene and above-mentioned polymers, there are formed 4-vinyl-l-cyclohexene, tetra­ hydroindene, cyclooctadiene and so forth, particularly a substantial amount of 4-vinyl-l-cyclohexene which is the dimer of butadiene, which causes to reduce the selectivity for 5-vinyl-2-norbornene. The object of this invention is to provide a process for producing 5-vinyl-2-norbornene continuously for a long time and with good selectivity by correcting the above-mentioned defects of prior arts, namely by preventing such troubles as clogging of the apparatus due to the deposition and adhesion of polymers and formation of polymer film on the inner wall surface of the apparatus, in the process for producing 5-vinyl-2-norbornene by the above-mentioned Diels-Alder reaction. This invention relates to a continuous process for producing 5-vinyl-2-norbornene from cyclopentadiene and butadiene or from a mixture of cyclopentadiene and dicyclopentadiene and butadiene by the Diels-Alder reac­ tion which process comprises adding from l0 to l0,000 ppm of N,N-diethylhydroxylamine or 4-oxo-2,2,6,6-tetramethyl­ piperidine-l-oxyl relative to the total weight of cyclo­ pentadiene and butadiene or of a mixture of cyclopentadiene and dicyclopentadiene and butadiene, continuously introduc­ ing the resulting mixture into a pressure reaction vessel, allowing them to react in the absence of any gas phase portion within the said pressure reaction vessel, and continuously withdrawing the reaction product. 4-Vinyl-l-cyclohexene, a side reaction product, is formed by the dimerization of butadiene. According to the analytical study of the present inventors, when a gas phase portion is present within the pressure reaction vessel in the reaction of cyclopentadiene or a mixture of cyclopentadiene and dicyclopentadiene with butadiene, the relative concentration of butadiene, which has a higher vapor pressure, becomes high in the gas phase portion of the pressure reaction vessel, which promotes the formation of 4-vinyl-l-cyclohexene. According to the process of this invention, cyclopentadiene or a mixture of cyclopentadiene and dicyclopentadiene and butadiene are continuously introduced into a pressure reaction vessel, allowed to react under conditions such that the vessel is filled with liquid and contains no gas phase portion, and the reaction product is continuously withdrawn, whereby the formation of 4-­ vinyl-l-cyclohexene can be reduced and the selectivity of 5-vinyl-2-norbornene based on butadiene can be enhanced. Further, by continuously injecting into the pressure reaction vessel N,N-diethylhydroxylamine or 4-­ oxo-2,2,6,6-tetramethylpiperidine-l-oxyl as a polymeriza­ tion inhibitor, polymerization in the pressure reaction vessel is suppressed and continuous operation can be carried out for a long time without the troubles of clogging of the apparatus due to deposition and adhesion of polymer and formation of polymer film on the inner wall surface of the apparatus. Also, since the polymer­ ization of butadiene and 5-vinyl-2-norbornene is suppressed, the selectivity of 5-vinyl-2-norbornene base on butadiene can be further enhanced. The process of this invention is carried out by injecting cyclopentadiene and butadiene or a mixture of cyclopentadiene and dicyclopentadiene and butadiene continu­ ously by means of a metering pump or the like into a pressure reaction vessel maintained at a temperature of from about 80 to l80°C, preferably from 90 to l60°C, and at a pressure of from about 5 to 60 kg/cm², preferably from l0 to 45 kg/cm², adding continuously thereto from l0 to l0,000 ppm, preferably from l00 to 5,000 ppm, of N,N-­ diethylhydroxylamine or 4-oxo-2,2,6,6-tetramethyl­ piperidine-l-oxyl relative to the total weight of feed materials, allowing them to react for from about 0.l to 5 hours, preferably from about 0.3 to 2 hours, and simultaneously withdrawing the reaction product continu­ ously. This invention will be described further below with reference to Examples. In the Examples, the amount of polymeric byproducts was quantitatively determined by treating the reaction liquid at 92°C under a reduced pressure of 2 mmHg, and measuring the amount of the remaining heavy matter. Example l Into a pressure vessel of 200 ml volume maintained at a temperature of l40°C and a pressure of 40 kg/cm² were fed with a plunger pump butadiene and cyclopentadiene in a molar ratio of l.2:l so as to give a residence time of 35 minutes. Simultaneously, 2,500 ppm of N,N-diethylhydroxylamine was added thereto as a polymerization inhibitor. The reaction liquid was continuously withdrawn while the reaction vessel being maintained full of liquid, and was analyzed. The reaction was continuously carried out for l000 hours. After the reaction had been stopped, no deposition of polymeric byproducts was observed in the autoclave and the inside of the vessel was clean. The concentration of polymeric byproducts in the reaction liquid was 0.04% by weight. The results of the reaction as examined by gas chromatographic analysis were: conversion of butadiene, 2l.0%; selectivity of 5-vinyl-2-norbornene based on butadiene, 67.8%; selectivity of 4-vinyl-l-­ cyclohexene on the same basis, l6.8%. Example 2 Into a pressure reaction vessel of 200 ml volume maintained at a temperature of l30°C and a pressure of 35 kg/cm² were fed with a plunger pump butadiene and a mixture of 95% by weight of cyclopentadiene and 5% by weight of dicyclopentadiene so as to give a molar ratio of butadiene to cyclopentadiene of l.3:l.0 and a residence time of 50 minutes. Simultaneously, l,500 ppm of N,N-­ diethylhydroxylamine was added thereto as a polymerization inhibitor. The reaction liquid was continuously withdrawn while the reaction vessel being maintained full of liquid, and was analyzed. The reaction was continuously carried out for 500 hours. After the reaction had been stopped, no deposition of polymeric byproducts was observed in the autoclave and the inner wall of the vessel was clean. The concentration of polymeric byproducts in the reaction liquid was 0.03% by weight. The results of the reaction as examined by gas chromatographic analysis were: conversion of butadiene, l6.7%; selectivity of 5-vinyl-2-norbornene based on butadiene, 70.l%; selectivity of 4-vinyl-l-cyclohexene on the same basis, l6.6%. Example 3 A reaction was carried out under the same condi­ tions as in Example l except that 600 ppm of N,N-diethyl­ hydroxylamine was added instead of 2,500 ppm. The reaction was conducted continuously for 500 hours. After stoppage of the reaction, no deposition of polymeric byproducts was observed in the autoclave and the inside of the vessel was clean. The concentration of the polymeric byproducts in the reaction liquid (at the time) was 0.l7% by weight. The results of the reaction as examined by gas chromatographic analysis were: conversion of butadiene, 2l.3%; selectivity of 5-vinyl-2-norbornene based on butadiene, 67.0%; selectivity of 4-vinyl-l-cyclohexene on the same basis, l6.6%. Example 4 Into a pressure reaction vessel of 200 ml volume maintained at a temperature of l40°C and a pressure of 40 kg/cm² were fed with a plunger pump butadiene and cyclopentadiene in a molar ratio of l.2:l so as to give a residence time of 35 minutes. Simultaneously, 2,500 ppm of 4-oxo-2,2,6,6-tetramethylpiperidine-l-oxyl was added thereto as a polymerization inhibitor. The reaction liquid was continuously withdrawn while the reaction vessel being maintained full of liquid, and was analyzed. The reaction was carried out continuously for l20 hours. After stoppage of the reaction, no deposition of polymeric byproducts was observed in the autoclave and the inside of the vessel was clean. The concentration of polymeric byproducts in the reaction liquid was 0.l6% by weight. The results of the reaction as examined by gas chromato­ graphic analysis were: conversion of butadiene, 2l.3%; selectivity of 5-vinyl-2-norbornene based on butadiene, 67.l%; selectivity of 4-vinyl-l-cyclohexene on the same basis, l6.6%. Example 5 Into a pressure reaction vessel of 200 ml volume maintained at a temperature of l30°C and a pressure of 35 kg/cm² were fed with a plunger pump butadiene and a mixture of 95% by weight of cyclopentadiene and 5% by weight of dicyclopentadiene so as to give a molar ratio of butadiene to cyclopentadiene of l.3:l.0 and a residence time of 50 minutes. Simultaneously, l,500 ppm of 4-oxo-­ 2,2,6,6-tetramethylpiperidine-l-oxyl was added thereto as a polymerization inhibitor. The reaction liquid was continuously withdrawn while the vessel being maintained full of liquid, and was analyzed. The reaction was carried out continuously for l40 hours. After stoppage of the reaction, no deposition of polymeric byproducts was observed in the autoclave and the inside of the vessel was clean. The concentration of polymeric byproducts in the reaction liquid was 0.ll% by weight. The results of the reaction as examined by gas chromatographic analysis were: conversion of butadiene, l6.9%; selectivity of 5-vinyl-2-norbornene based on butadiene, 69.6%; selectivity of 4-vinyl-l-cyclohexene on the same basis, l6.5%. Example 6 A reaction was carried out under the same conditions as in Example l except that 600 ppm of 4-oxo-­ 2,2,6,6-tetramethylpiperidine-l-oxyl was added instead of N,N-diethylhydroxylamine. The reaction was conducted continuously for l20 hours. After stoppage of the reaction, no deposition of polymeric byproducts was observed in the autoclave and the inside of the vessel was clean. The concentration of polymeric byproducts in the reaction liquid was 0.6% by weight. The results of the reaction as examined by gas chromatographic analysis were: conversion of butadiene, 22.2%; selectivity of 5-vinyl-2-norbornene based on butadiene, 64.4%; selectivity of 4-vinyl-l-cyclohexene on the same basis, l6.0%. Comparative Example l In a pressure reaction vessel of 200 ml volume were placed 27 g of cyclopentadiene, 27 g of butadiene, and 0.2 g of N,N′-diphenyl-p-phenylenediamine, and allowed to react at l40°C. The reaction time was selected so as to give the same percentage of conversion of butadiene as in Example l. After completion of the reaction, polymeric byproducts were found deposited in the autoclave and the inside of the vessel was soiled. The results of the reaction as examined by gas chromatographic analysis were: conversion of butadiene, 24%; selectivity of 5-­ vinyl-2-norbornene based on butadiene, 43%; selectivity of 4-vinyl-l-cyclohexene on the same basis, 4l%. Comparative Example 2 A continuous operation was carried out for l20 hours under the same conditions as in Example l except that no polymerization inhibitor was added. After stoppage of the reaction, it was found that the autoclave was filled with polymeric byproducts and the inside was soiled. The concentration of polymeric byproducts in the reaction liquid was 2.5% by weight. The results of the reaction as examined by gas chromatographic analysis were: conversion of butadiene, 25%; selectivity of 5-vinyl-2-norbornene based on butadiene, 54%; selectivity of 4-vinyl-l-cyclohexene on the same basis, l7%. In a process for producing 5-vinyl-2-norbornene from cyclopentadiene and butadiene or from a mixture of cyclopentadiene and dicyclopentadiene and butadiene by the Diels-Alder reaction, the reaction can be carried out for a long time with good selectivity and without such troubles as clogging due to the deposition and adhesion of polymer in the apparatus and formation of polymer film on the inner wall surface of the apparatus by adding from l0 to l0,000 ppm of N,N-diethylhydroxylamine or 4-oxo-2,2,6,6-­ tetramethylpiperidine-l-oxyl relative to the total weight of cyclopentadiene and butadiene or of a mixture of cyclopentadiene and dicyclopentadiene and butadiene, continuously introducing the resulting mixture into the pressure reaction vessel, allowing them to react in the absence of any gas phase portion within the said pressure reaction vessel, and continuously withdrawing the reaction product.

Claims: 1. A continuous process for producing 5-vinyl-2-­ norbornene from cyclopentadiene and butadiene or from a mixture of cyclopentadiene and dicyclopentadiene and butadiene by the Diels-Alder reaction which process comprises adding from l0 to l0,000 ppm of N,N-diethyl­ hydroxylamine relative to the total weight of cyclopenta­ diene and butadiene or of a mixture of cyclopentadiene and dicyclopentadiene and butadiene, continuously introduc­ ing the resulting mixture into a pressure reaction vessel, allowing them to react in the absence of any gas phase portion within the said pressure reaction vessel, and continuously withdrawing the reaction product. 2. A continuous process for producing 5-vinyl-2-­ norbornene according to claim l wherein from l00 to 5,000 ppm of N,N-diethylhydroxylamine is added relative to the total weight of cyclopentadiene and butadiene or of a mixture of cyclopentadiene and dicyclopentadiene and butadiene. 3. A continuous process for producing 5-vinyl-2-­ norbornene from cyclopentadiene and butadiene or from a mixture of cyclopentadiene and dicyclopentadiene and butadiene by the Diels-Alder reaction which process comprises adding from l0 to l0,000 ppm of 4-oxo-2,2,6,6-­ tetramethylpiperidine-l-oxyl relative to the total weight of cyclopentadiene and butadiene or of a mixture of cyclopentadiene and dicyclopentadiene and butadiene, continuously introducing the resulting mixture into a pressure reaction vessel, allowing them to react in the absence of any gas phase portion within the said pressure reaction vessel, and continuously withdrawing the reaction product. 4. A continuous process for producing 5-vinyl-2-­ norbornene according to claim 3 wherein from l00 to 5,000 ppm of 4-oxo-2,2,6,6-tetramethylpiperidine-l-oxyl is added relative to the total weight of cyclopentadiene and butadiene or of a mixture of cyclopentadiene and dicyclopentadiene and butadiene.

Inventors: KIMURA, KAZUO, MASUKO, FUJIO, USUI, MASAHIRO
Applicants: SUMITOMO CHEMICAL COMPANY, LIMITED
Application year: 1986
Main classification: C07C13
IPC codes: C07C2, C07C67, C07C1, C07C7, C07C13