VYNIL ESTER RESINS FROM GLYCIDYL ETHERS OF REACTION PRODUCT OF A PHENOL AND UNSATURATED HYDROCARBONS

Abstract: Vinyl ester resins are prepared by reacting a polymerizable unsaturated carboxylic acid-containing compound with an epoxy resin prepared by dehydrohalogenating the reaction product of an epihalohydrin with the reaction product of an aromatic hydroxyl-containing compound and an unsaturated hydrocarbon. The resulting vinyl ester resin, with or without a polymerizable monomer, may be cured by the application of heat and/or pressure in the presence of a free radical yielding catalyst to form such products as coatings, pottings and castings.

Description: -l- * VINYL ESTER RESINS FROM GLYCIDYLJETHERS OF REACTION PRODUCT OF A PHENOL AND UNSATURATED HYDROCARBONS ___. The present invention pertains to vinyl ester resins prepared from epoxy resins derived from the reaction product of an aromatic hydroxyl-containing compound and unsaturated hydrocarbons. 5 Vinyl ester resins are conventionally prepared from epoxy resins and unsaturated carboxylic acids or half esters of such acids as disclosed by R. L. Bowen in U.S. Patent 3,066,112, by C. R. Bearden in U.S. Patent 3,367,992 and by D. H. Swisher and D. C. Garms 10 in U.S. Patent 3,564,074. The vinyl ester resins of the present invention provide for an improvement in one or more properties such as chemical resistance, moisture resistance or electrical properties. * » 15 The present invention-concerns vinyl ester resin compositions comprising " -. (I) from 30 to 100, preferably from 40 to 70 percent by weight of a vinyl ester resin prepared by reacting (A) at least one ethylenically unsaturated 5 monocarboxylic acid; . '" ■ - (B) at least one epoxy resin prepared by dehydrohalogenating the reaction product of . ' - . " -*. -,- ■ " ' -• . ' . ' - " . (1) an epoxy alkyl halide and 10 - « --- - • ^) ' the reaction product of (a) an aromatic hydroxyl-containing compound having from one to two aromatic rings and at -" * least one ortho or para posi- 15 tion with respect to the hydroxyl group available for ring alkylation with (b) at least one unsaturated hydrocarbon selected from 20 (i) mono- and di-unsaturated hydrocarbons containing 4 to 6 carbon atoms and (ii) unsaturated hydrocarbons containing an average of 25 7-55 carbon atoms per molecule; and optionally Components (B-2-a) and (B-2-b) are employed in quantities which provide a mole ratio of (B-2-a) to (B-2-b) of from 1.8:1 to 30:1, preferably from about 30 1.8:1 to about 20:1 and components (B-1) and (B-2) are employed in quantities which provide an epoxy group to phenolic hydroxyl group ratio of from 1.5:1 to 20:1, preferably from 3:1 to 5:1, it being fully understood that the excess aromatic hydroxyl-containing material and epoxy alkyl halide are removed from the product. The present invention also pertains to the product resulting from polymerizing the aforesaid vinyl ester resin composition in the presence of a suitable quantity of at least one suitable polymerization __ catalyst optionally also in the presence of a suitable quantity of a suitable accelerating agent. Suitable ethylenically unsaturated monocar- boxylic acids which can be employed herein include, for example, the α,β-unsaturated monocarboxylic acids and the hydroxyalkyl acrylate or ethacrylate half esters of dicarboxylic acids. The α,β-unsaturated monocarbox- ylic acids include acrylic acid, methacrylic acid, crotonic acid, cinnamic acid and the like. The hydroxy¬ alkyl groups of the acrylate or methacrylate half esters preferably contain from two to six carbon atoms and include such groups as hydroxyethyl, beta-hydroxy- propyl, beta-hydroxybutyl and the like. It is also intended to include those hydroxyalkyl groups in which an ether oxygen is present. The dicarboxylic acids or acid anhydrides can be either saturated or unsaturated. Saturated acids include phthalic acid, phthalic anhydride, chlorendic acid, chlorendic anhydride, tetrabro ophthalic acid, tetrabromophthalic anhydride, adipic acid, succinic acid, glutaric acid and the like. Unsaturated dicarboxylic acids include maleic acid, maleic anhydride, fumaric acid, citraconic acid, citraconic anhydride, itaconic acid, halogenated maleic or fumaric acids, mesaconic acid and the like. Mixtures of ethylenically unsaturated carboxylic acids or anhydrides may be used. Preferably, the half esters are prepared by reacting substantially equal molar proportions of a hydroxyalkyl acrylate or methacrylate with a dicar¬ boxylic acid anhydride. Preferred unsaturated anhy- drides include maleic anhydride, citraconic anhydride, and the like and preferred saturated anhydrides include phthalic anhydride, tetrabromophthalic anhydride, chlorendic anhydride and the like. Advantageously,-a polymerization inhibitor, such as the methyl ether of hydroquinone or hydroquinone, may be added since elevated temperatures are useful in preparing the half esters. The reaction temperature may range from 20° to 150°C, but preferably from 80° to 120°C. The polyepoxide is reacted with the ethylen- ically unsaturated monocarboxylic acid either with or without a solvent at a temperature of 20° to 120°C. The reaction may also be conducted in the presence or absence of suitable catalysts such as alcoholates, tertiary amino phenols or others well known to the art. Preferably, the polyepoxide is added in an amount sufficient to provide 0.8 to 1.2 equivalents of epoxide per equivalent of carboxylic acid. The reaction is continued until the acid content (as -COOH) drops below 2 percent by weight. If desired, the ethylenically unsaturated monocarboxylic acid-polyepoxide reaction product contain¬ ing secondary hydroxyl groups is further reacted with 0.1 to 1.2 mole proportions of dicarboxylic acid anhy¬ dride per equivalent of epoxide. The dicarboxylic acid anhydride may be selected from either the saturated or unsaturated dicarboxylic acid anhydrides previously recited or mixtures thereof. A reaction temperature from 25° to 150°C is suitable, but 80° to 120°C is preferred. Also, if desired, the dicarboxylic acid anhydride, the ethylenically unsaturated monocarboxylic acid and the epoxy resin can be reacted simultaneously. Suitable aromatic hydroxyl-containing com¬ pounds which can be employed herein include any such halogen free compounds which contain_one or two aro¬ matic rings, at least one phenolic hydroxyl group and at least one ortho or para ring position with respect to a hydroxyl group available for alkylation. Particularly suitable aromatic hydroxyl- -containing compounds which can be employed herein include, for example, phenol, hydroquinone; catechol; resorcinol; guaiacol; pyrogallol; phloroglucinol; C, to C g alkyl phenol such as meth lphenol, isopropylphenol, ethylphenol, propylphenol, t-butylphenol, isobutylphenol, octylphenol, nonylphenol; cumylphenol; p-phenylphenol; o-phenylphenol; m-phenylphenol; bisphenol A; dihydrox - diphenyl sulfone; and mixtures thereof. Suitable unsaturated hydrocarbons which, either in a crude or purified state, can be employed herein include, for example, butadiene, isoprene, piperylene, cyclopentadiene, cyclopentene, 2-methyl butene-2, cyclohexene, cyclohexadiene, methyl cyclo¬ pentadiene, dicyclopentadiene, limonene, dipentene, linear and cyclic dimers of piperylene, methyl dicyclo- pentadiene, dimethyl dicyclopeήtadiene, norbornene, norbornadiene, ethylidiene norbornene, and mixtures thereof. Also suitable unsaturated hydrocarbons include the other dimers, codimers, oligomers and cooligomers of the aforementioned unsaturated hydrocarbons contain¬ ing an average of 7-55 carbon atoms per molecule. Particularly suitable unsaturated hydrocarbons which can be employed herein include, for example, essen¬ tially pure dicyclopentadiene, a dicyclopentadiene concentrate containing from 70 to 97 -percent by weight of dicyclopentadiene; from 3 to 30 percent by weight of c 9 " c i 2 dimers or codimers of C 4 -C 6 _dienes such as, for example, cyclopentadiene-isoprene, cyclopentadiene- piperylene, cyclopentadiene-methyl cyclopentadiene, * z and/or dimers of isoprene, piperylene, methyl cyclo¬ pentadiene and the .like; from zero to 7 percent by weight of c 14 _C,g oligomers of C 4 -C & dienes and from zero to 10 percent by weight of aliphatic diolefins such as, for example, piperylene, isoprene, 1,5-hexa- diene and cyclic olefins such as cyclopentadiene, methyl cyclopentadiene, cyclopentene and the like. Methods of preparation for these dicyclopentadiene concentrates and more detailed descriptions thereof can be found collectively in U.S. Pat. No. 3,557,239 issued to Gebhart et al and U.S. Pat. No. 4,167,542 issued to Nelson. Also, particularly suitable unsaturated hydrocarbons which can be employed herein include a crude dicyclopentadiene stream containing from 20 to 70 percent by weight dicyclopentadiene, from 1 to 10 percent codimers and dimers of C.-C, dienes (described above), from zero to 10 percent oligomers of C..-C,- dienes and the balance to provide 100 percent, C 4.-C6, alkanes, C 4 ~C 6 alkenes and/or C 4 -C β dienes. Also, particularly suitable unsaturated hydrocarbons which can be employed herein include a crude piperylene or isoprene stream containing from 30 to 70 percent by weight piperylene or isoprene, zero to ten percent by weight C 8 -C-, 2 dimers and codimers of C 4 -C 6 dienes, and the balance to provide 100 percent C 4 ~ C 6 a ** L k anes , alkenes and dienes. *_ "- * Also, particularly suitable are hydrocarbon oligomers prepared by polymerization of the reactive components in the above hydrocarbon streams e.g.,- dicyclopentadiene concentrate, crude dicyclopentadiene, crude piperylene or isoprene, individually or in combi¬ nation with one another or in combination with high purity diene streams. Suitable acid catalysts which can be employed herein include, for example, Lewis Acids, alkyl, aryl and aralkyl sulfonic acids and disulfonic acids of _> . . , diphenyloxide and alk lated diphenyloxide, sulfuric acid, mixtures thereof and the like. Particularly suitable are such Lewis Acids as BF 3 gas, organic complexes of boron trifluoride such as those complexes formed with phenol, cresol, ethanol, acetic acid and the like. Also suitable Lewis acids include aluminum chloride, zinc chloride, stannic chloride, and the like. Also suitable catalysts include, for example, activated clays, silica, silica-alumina complexes, and the like. Suitable epoxy alkyl halides which can be employed herein include those represented by the formula wherein each R is independently hydrogen or an alkyl group having from 1 to 6 carbon atoms and X is a halogen. ' _- ... :.. Particularly suitable epoxy alkyl halides include, for example, epichlorohydrin, epibromohydrin, epiiodohydrin, methylepichlorohydrin, methylepibromo¬ hydrin, methylepiiodohydrin, and mixtures thereof Advantageously, a suitable vinyl polymerization inhi- bitor such as the methyl ether of hydroquinone, pheno- thiazine or hydroquinone may be added. Following completion of the reaction, . the reaction mixture is cooled and the polymerizable monomer may be blended therewith. A wide selection of polymerizable monomers containing the >C=CH 2 group is available from the many known classes of vinyl monomers. Representative species are the vinyl aromatic compounds which include such monomers as styrene, vinyl toluene, halogenated styrenes, p-t-butyl styrene, and divinyl benzene. Other suitable monomers include the methyl, ethyl, isopropyl, octyl, etc., esters of acrylic or methacrylic acid, vinyl acetate, diallyl maleate, diallyl phthalate, dimethallyl fumarate, acidic mono- mers such as acrylic acid, methacrylic acid, crotonic acid and amide monomers such as acrylamide, N-alkyl acrylamides and mixtures thereof. Preferred polymerizable monomers containing the >C=CH 2 group are styrene, vinyl toluene, ortho-, meta- and para-halostyrenes, vinyl naphthalenes, the various alpha-substituted styrenes, as well as the various di-, tri- and tetrahalo styrenes, and acrylic, methacrylic and crotonic acid esters whic include both the saturated alcohol esters and the hydroxyalkyl esters. " ._ The blended vinyl ester resin composition may consist of up to 70 percent by weight of polymerizable monomer containing the >C=CH 2 group with the balance of the combined weight consisting of said vinyl ester resin. Preferably, the resin composition consists of 30-60 percent by weight of said monomer and 70-40 percent by weight of said vinyl ester resin. While it is preferred in many applications to blend the vinyl ester resin with a polymerizable monomer, the present invention i_ not limited thereto. The vinyl ester resin can be cured and polymerized in the absence of such a monomer and can be applied and utilized as solutions in a nonpolymerizable solvent, such as is practiced in certain coating operations. According to the present invention, the curing of the resin compositions is effected by the application of heat and/or pressure in the presence of a free radical yielding catalyst. Catalysts that may be used for the curing or polymerization are preferably the peroxide catalysts, such as_ benzoyl peroxide, lauroyl peroxide, t-butyl hydroperoxide, t-butylper- benzoate, methyl ethyl ketone peroxide, potassium persulfate and the like. The amount of the catalyst added will preferably vary from 0.1 to about 5 percent by weight of reactants. Temperatures employed may vary over a considerable range but usually are in the range of 20° to 250°C. Additionally, more rapid curing of the thermo- setting resin compositions may be accomplished by the addition of accelerating agents such_as lead or cobalt naphthenate, dimethylaniline and the like, usually in concentrations ranging from 0.1 to 5.0 weight percent. The relatively low molecular weight of the vinyl ester resins of the present invention along with the rapid gel time, high heat distortion and fast cure rate of the thermosetting resin compositions provide many advantages and improved properties in a wide variety of applications. ~ Pottings and castings are conveniently made by the addition of suitable curing agents and acceler¬ ating agents to the resin composition followed by pouring into an appropriate mold or casting and curing at room temperature. Heat may be applied to hasten the cure. Such cured castings have excellent flexural and tensile strengtih, good impact resistance and develop smooth, hard surfaces. In addition, the resultant lower viscosity of said resin compositions allows the incorporation of up to as much as 75 percent by weight or more of inert additives and fillers such as glass, metal filings and inorganic fillers such as sand or clay. The resin -11- cbmpositions, in spite of this heavy loading, exhibit excellent flow characteristics in the molding opera¬ tion. Frequently such fillers are added to further improve and vary the useful properties of the cured compositions. Such cured products develop excellent hardness, strength, weatherability and solvent resis¬ tance. Other commonly used additives, such as pigments, release agents, plasticizers and the like, may be _ advantageously added. '" -- Of particular utility is the use of the present invention in the preparation of reinforced plastic and laminate structures. Reinforcing media may be chosen from many well known suitable materials such as glass cloth and matting, paper, asbestos paper, mica, fabrics and the like. Suitable fillers, previously described, are frequently used to provide improved properties. For example, clays are suggested where improved exterior weathering properties are required. In addition to the advantages and improved properties already recited, this invention provides better glass wetting and increased resistance to stress cracking than unsaturated polyester resins. EXAMPLE 1 A. Reaction of Phenol with a C 10 Diene Stream To a reactor equipped with a stirrer, condenser, thermowell and heater, was added 1882 g (20 moles) of phenol and 8 g (0.4 percent based on total weight) of boron trifluoride etherate. The reaction mixture was heated to 70°C and 132 g (__1 mole) of a C 1Q diene stream was added, containing mainly dicyclopentadiene and cyclopentadiene-isoprene codimers, was added over a 20-minute (1200 s) period. The temperature was increased to 150°C over a 3-hour (10,800 s) time period and held for 3 hours (10,800 s). The unreacted phenol was distilled off with a finishing temperature of 210°C and less than 5 mm Hg. The recovered product . was a dicyclopentadiene bisphenol with an average func- tionality of 2.07.__- ,--- ■ • • •=:?-..--- - . .*. . . . .-. ■ ---- •-. - B. Preparation of Epoxy Resin -- -. -., -_ " --> ■ To a reactor equipped with a stirrer, conden¬ ser, nitrogen sparge, thermowell ancL_addition funnel were added 805 g (5 OH equivalents) of the product pre- pared in Example 1-A, 900 g of the methyl ether of pro- pylene glycol, 20 g of water, 2 g of 50 percent NaOH and 2312.5 g (25 moles) of epihalohydrin. The solution was heated to 70°C. 909.1 G (5 moles) of 22 percent NaOH was added over a 2-hour and 37 minute (9420 s) time period. The reaction was held at 70°C for an additional 52 minutes (3120 s). The resin was trans¬ ferred to a separating funnel where the brine and resin layers were allowed to separate. The brine layer was discarded, the resin solution was returned to the reaction flask, and 139 g of the methyl ether of propylene glycol was added. The mass was heated to 69°C and 200 g (1.25 moles) of 25 percent NaOH was added over a 21-minute (1260 s) period and then allowed to react an additional 75 minutes (4500 s) . The resin was transferred to a separating funnel, the brine layer drawn off, washed with water and the water layer removed. The resin was returned to the reactor where the methyl ether of propylene glycol and excess epichlorohydrin were removed by vacuum distillation. The resin was finished at 155°C and 3 mm Hg. " The resin was a semi- -solid at room temperature with an epoxy equivalent weight of 245. C. Preparation of Vinyl Ester Resin To a reactor equipped with a heater, tempera¬ ture controller, stirrer and gas sparge tube, 612.5 g (2.5 eq) of the epoxy resin prepared in Example 1-B was added and heated to 80°C. 0.17 G of hydroquinone was added and blended by stirring. 215.0 G (2.5 eq) of methacrylic acid and 0.92 g of DMP-30 (dimethylamino- ethyl phenol) were added. The mass was heated to . 115°C and reacted for 3 hours (10,800 s). The unreacted acid content was 2.5 percent and the unreacted oxirane content was 3.2 percent. An addi¬ tional 6.2 g (0.17 eq) of methacrylic acid was added and reacted for 2.5 hours (9000 s) at 120°C. The COOH content was 1.0 percent and the epoxy content was 0.5 percent. The reactants were cooled to 110°C and blended with 678 g (45 percent) styrene inhibited with 0.3 g of methyl hydroquinone and 0.23 g of phenothiazine. D. Curing of the Vinyl rτrj Ester Resin A clear casting was made from the vinyl ester resin prepared in Example 1-D above using 0.3 percent by weight cobalt naphthenate (6 percent), 0.2 percent by weight N,N-dimethyl toluidine and 1.0 percent methyl- ethyl ketone peroxide. After 16 hours (57,600 s), a post treatment of 2 hours (7200 s) at 155°C was provided, EXAMPLE 2 A. Reaction of Phenol with a C,--C, 0 Crude Hydrocarbon Stream To a reactor equipped as in Example 1-A were added 1035.1 g (11 moles) of phenol and 9.5 g of BF 3 etherate in 200 g of toluene. The temperature was set at 40°C. A crude hydrocarbon stream containing " mainly alkanes, alkenes and dienes in the C 5 to C 10 range, 355.5 g (estimated at 3.33 moles of active product) was added over a 7-hour and 3 minute (25,380 s) time period. A summary analysis of this stream was as follows: .. n-pentane 5.8 wt. % trans-pentene-2 1.6 wt. % cis-pentene-2. 1.5 wt. % 2-methyl butene-2 4.1 wt. % trans-piperylene 16.3 wt. % cis-piperylene 10.8 wt. % cyclopentene 10.1 wt. % dicyclopentadiene 34.0 wt. % cyclopentadiene/isoprene C l0 3.4 wt. % remainder 12.4 wt. % During the addition time, the temperature was in the 38°C to 45°C range. The reaction mass was heated to 145°C over 5 hours (18,000 s). During this time, 36 g of unreacted hydrocarbon was removed. After 2 hours (7200 s) of slight vacuum, an additional 431 g of hydro¬ carbon toluene and phenol were removed. Full vacuum at 210°C and 0 mm mercury resulted in an additional 565 g of phenol and C 5 alkylated phenol. B. Preparation of Epoxy Resin To a reactor equipped as in Example 1-B were added 316 g (2 OH eq. ) of the hydrocarbon phenolic pre¬ pared in Example 2-A, 320 g of the methyl ether of pro¬ pylene glycol, 7 g of water, 2 g of 50 percent sodium hydroxide in water, and 740 g (8 moles) of epichloro- hydrin. The solution was heated to 70°C. 363.6 G -15- (2 moles) of 22 percent NaOH was added over a 55-minute (3300 s) time period. The reaction was held at 70°C for an additional 36 minutes (2160 s). The resin was transferred to a separating funnel where the brine and resin layers were allowed to separate. The brine layer was discarded, the resin solution returned to the reaction flask and 32 g of the methyl ether of propy¬ lene glycol added. The mass was heated to 70°C and 80 g (0.5 moles) of 25 percent NaOH was added over a 12-minute (720 s) period and then allowed to react for an additional hour (3600 s). The resin was transferred to a separating funnel, the brine layer drawn off, washed with water and the water layer removed. The resin was returned to the reactor where the methyl ether of propylene glycol and excess epichlorohydrin were removed by vacuum distillation. The resin was finished at 155°C and 4 mm Hg. The resin was a semi- -solid at room temperature with an epoxide equivalent weight of 231.5. C. Preparation of a Vinyl Ester Resin To a reactor equipped as in Example 1-C were added 231.5 g (1.0 moles) of the epoxy resin prepared in Example 2-B and 0.29 g of ethyl triphenyl phos- phonium acetate. The components were heated to 125°C and held for 1 hour (3600 s). The temperature was reduced to 100°C and 0.19 g hydroquinone, 72.1 g (0.84 moles) of methacrylic acid and 0.07 g of chromium chloride were added separately and with good mixing. The components were reacted for 3 hours and 45 minutes (13,500 s) at 118°C. 248.9 G (45 percent) styrene and 0.12 g of phenothiazine were added under agitation conditions. D. Curing of the Vinyl Ester Resin The sample was cured with 0.2 percent by weight N,N-dimethyl toluidine, 0.5 percent by weight cobalt naphthenate (6 percent), and 2.0 percent by weight methyl ethyl ketone peroxide at room temperature. After 16 hours (57,600 s) and before release from the mold, a post cure of 2 hours (7200 s) at 155°C was provided. ~ -.. " " " " ~ . . . ^ COMPARATIVE EXPERIMENT A " A vinyl ester resin prepared by reacting a mixture of a diglycidyl ether of bisphenol A having an EEW of 535 and a diglycidyl ether of bisphenol A having an EEW of 186-192, the resultant blend having an EEW of 361, was reacted with glacial methacrylic acid at a ratio of 1.0 equiv. of acid and 1.0 equiv. of epoxide at a temperature of 115°C until the acid content was less than 1.2 percent. This product was then blended with styrene such that the resultant blend contained 45 percent styrene by weight. The resultant blend was cured as in Examples 1-D and 2-D. Each of the cured products from Examples 1-D, 2-D and Comparative Experiment A were subjected to physical testing and chemical solvent resistance. The results are given in the following table. EXAMPLE EXAMPLE COMPARATIVE PROPERTY 1-D 2-D EXPERIMENT A FLEXURAL STRENGTH 1 psi 22,50C 1 23,000 21,000 MPa 155 158 145 FLEXURAL MODULUS 1 , psi 6.1 x 10 5 6.1 x 10 5 5.5 X 10 5 , KPa 42.1 x 10 5 42.1 x 10 s 37.9 x 10 s TENSILE STRENGTH 2 , psi 8,200 11,200 11,600 , MPa 57 77 80 ELONGATION, % 1.6 3.5 4.2 HEAT DISTORTION 3 , °F 2_>6 186 210 130 86 99 1 24-HOUR SOLVENT ABSORPTION 4 TOLUENE, °/ 0 weight gain 0.03 0.04 0.02 WATER, % weight gain 0.16 0.12 0.12 ACETONE, % weight gain 3.27 7.2 >4.50 METHANOL, % weight gain 0.46 0.70 / 1.50 1 Test was conducted according to the procedure of ASTM D 790-71. 2 Test was conducted according to the procedure of ASTM D 638-72. 3 Test was conducted according to the procedure of ASTM D 648. 4 This test was conducted on 1" x 3" (25.4 mm x 193.5 mm) clear casting coupons. Solvent resistance was determined from the percent weight-gain observed after 24 hours (86,400 s) in a room temperature solvent bath.

Claims: -18- 1. A vinyl ester resin composition comprising (I) from 30 to 100 percent by weight of a vinyl ester resin prepared by reacting (A) at least one ethylenically unsaturated 5 monocarboxylic acid; (B) at least one epoxy resin prepared by dehydrohalogenating the reaction product of (1) an epoxy alkyl halide and 10 (2) the reaction product of (a) 1 * an aromatic hydroxyl-containing compound having from one to two aromatic rings and at least one ortho or para position 15 with respect to the hydroxyl group available for ring alkylation with ■ (b) at least one unsaturated hydrocarbon selected from 20 (i) mono- and di-unsaturated hydrocarbons containing 4 to 6 carbon atoms and (ii) unsaturated hydrocarbons containing an average of 25 7-55 carbon atoms per molecule; and optionally - - (C) at least one dicarboxylic acid anhy¬ dride; and ■ - (II) from zero to 70 percent by weight of a poly¬ merizable ethylenically unsaturated monomer; wherein Components (B-2-a) and (B-2-b) are employed in quantities which provide a mole ratio of (B-2-a) to (B-2-b) of from 1.8:1 to 30:1 and components (B-1) and (B-2) are employed in quantities which provide an epoxy group to phenolic hydroxyl ~ group ratio of from 1.5:1 to 20:1, and wherein the excess aromatic hydroxyl- containing material and epoxy alkyl halide are removed from the product. 2. A vinyl ester resin composition of Claim 1 wherein (i) component I is present in a quantity of from 40 to 70 percent by weight; (ii) component II is present in a quantity of from 30 to 60 percent by weight; (iii) components (I-B-2-a) and (I-B-2-b) are employed in quantities which provide a ratio of from 1.8:1 to 20:1; (iv) components (I-B-1) and (I-B-2) are employed in quantities which provide a ratio of 3:1 to 5:1; and (v) component (I-B-l) is an epihalohydrin. 3. A vinyl ester resin composition of Claim 2 wherein (i) component (I-A) is acrylic acid or methacrylic acid; (ϋ) component (I-B-l) is epichlorohydrin; and -20- \ ' (iii) component II is styrene, vinyl toluene, chloro styrene, methyl methacrylate, diallyl phthalate or a mixture thereof. 4. A vinyl ester resin composition of Claims 1, 2 or 3 wherein component (I-B-2-b) is essen- tially pure dicyclopentadiene. * 5. A vinyl ester resin composition of Claim 4 wherein component (I-B-2-a) is phenol, resoreinol, C 1 to C Q alkyl phenol or mixture thereof. 6. A vinyl ester resin composition of Claims 1, 2 or 3 wherein component (I-B-2-b) is a dicyclopentadiene concentrate containing (i) from 70 to 97 percent by weight of dicyclopentadiene; (ϋ) from 3 to 30 percent by weight of C 9 ~ C 12 or codimers of C 4 - C, dienes; (iii) from zero to 7 percent by weight of C, 4 -C-, a oligomers of C 4 ~C 6 dienes; and from zero to 10 percent by weight of aliphatic diolefins and cyclic olefins. 7. ;A vinyl ester resin composition of Claims 1, 2 or 3 wherein component (I-B-2-b) is a crude dicyclopentadiene stream containing (i) 20-70 percent dicyclopentadiene; (ii) 1-10 percent dimers or codimers of C4„-C6, dienes (iii) 0-10 percent oligomers of C 4 -C 6 dienes; (i.v) the balance to provide 100 percent by weight of C 4 -C 8 alkanes, C 4 -C 6 alkenes or C4.-C6.. dienes. - - 8. A vinyl ester resin composition of Claims 1, 2 or 3 wherein component (I-B-2-b) comprises a C-. Q diene stream containing mainly dicyclopentadiene and cyclopentadiene-isoprene codimer. * 5 9. A vinyl ester resin composition of Claims 1, 2 or 3 wherein component (I-B-2-b) comprises: n-pentane 5.8 wt. % trans-pentene-2 ~ ~ 1.6 wt. % cis-pentene-2 1.5 wt. % 10 2-methyl butene-2 4.1 wt. % trans-piperylene 16.3 wt. % cis-piperylene 10.8 wt. % eyelopentene 10.1 wt. % dicyclopentadiene 34.0 wt. % 15 cyclopentadiene/isoprene C 10 3.4 wt. % remainder 12.4 wt. % 10. A cured composition resulting from subjecting a mixture containing (a) a vinyl ester resin composition of any one of Claims 1 to 9 and (b) an 20 effective quantity of one or more polymerization cata¬ lysts and/or accelerators to conditions for curing said mixture. 11. A cured composition of Claim 10 wherein said polymerization catalyst is at least one of benzoyl 25 peroxide, t-butyl perbenzoate, methyl ethyl ketone peroxide, t-butyl peroctoate or di-t-butyl peroxide and said accelerator, when present, is at least one of cobalt naphthenate, cobalt octoate, dimethyl aniline or 2,4,6-tris(dimethylaminomethy1)phenol.

Inventors: LAMONT MARY J, NELSON DONALD L, LAMONT, MARY, J., NELSON, DONALD, L.
Applicants: DOW CHEMICAL CO, THE DOW CHEMICAL COMPANY
Application year: 1986
Main classification: C08F283
IPC codes: C08F283, C08F299, C08G59