MIXED METAL HYDROXIDES FOR THICKENING WATER OR HYDROPHYLIC FLUIDS

Abstract: Novel monodispersed crystalline mixed metal layered hydroxide compounds of the general formula: Li m D d T(OH) (m+2d+3+na) A n / a·qH₂O where m is from zero to about 1; D is a divalent metal; d is from zero to about 4; T is a trivalent metal; A represents anions or negative-valence radicals of valence n; na is from zero to about -3; (m+d) is greater than zero; a is the number of A ions; q is from zero to about 6; and (m+2d+3+na) is equal to or greater than 3. The D metal is preferably Mg and the T metal is preferably A1. These compounds are useful as gelling agents which impart beneficial thixotropic properties to various fluids, such as drilling fluids, especially when em­ ployed along with fluid loss agents.

Description: This invention concerns the thickening of water or hydrophylic fluids by use of mixed metal layered hydroxides. There are various reasons for thickening water, aqueous solutions, hydrophilic fluids, and the like, such as for use as water-based metal working fluids, fire control fluids, oil field drilling fluids, food additives, hydraulic fluids, water-based paints or coatings, stripping solutions, and other applications wherein thickening of a liquid or solution is beneficial. Water thickening agents, such as guar gum and polyacrylamide are not stable to high shear, hydrothermal treatment above about 250°F (120°C), oxidation, bacterial attack, and salts. To make up for some of these problems, such additives as bacteriacides and antioxidants are sometimes required. Thickening agents or viscosifying agents for aqueous materials, such as drilling fluids, which involve some form of hydrous aluminum compound are disclosed, for example, in US-A-4,240,915; 4,349,443; 4,366,070; 4,389,319; 4,428,845; 4,431,550; 4,447,341; 4,473,479; and 4,486,318. Patents disclosing other forms of aluminum compounds for the same purpose are, for example, US-A-4,240,924; 4,353,804; 4,411,800; and 4,473,480. Similar patents disclosing other types of viscosifying agents are, for example, US-A-4,255,268; 4,264,455; 4,312,765; 4,363,736; and 4,474,667. The above patents deal with the formation of the hydrous aluminum compounds in situ . The major disadvantages to such a process are: (1) The resulting thickened fluid contains copious amounts of reaction salts. This may be undesirable in many situations. For example, in applications such as paints, metal working fluids, or water-based hydraulic fluids, the presence of salt could cause severe corrosion problems. In the case of oil field drilling fluids, many performance additives do not work well if salt is present. Thus it is desirable to drill in fresh water if possible. (2) The reactions described in the cited patents are run in situ (e.g. in the mud pit of a drilling rig); under such conditions the reaction cannot be adequately controlled and the properties of the resultant thickener may be unpredictable. Other problems with the use of Al(OH)₃ as a gelling agent for various processes are as follows: 1. Al(OH)₃ gels are known to detrimentally change with time unless certain anions such as carbonate or citrate are present. 2. The rheology of Al(OH)₃ is not very constant with changing pH values. For example, a slurry of Al(OH)₃ may be very thick and uniform at pH 6 but at pH 10, which the drilling industry prefers, the slurry collapses and the Al(OH)₃ settles out of suspension. This creates significant problems since most drilling operations are run at pH values in the range of 9 to 10.5. A historically popular thickening agent, especially in drilling mud, has been mineral clays, such as bentonite clay, often used with other agents or densifiers, such as Fe₂O₃, BaSO₄ and others. Variations from batch to batch of bentonite clay, and sensitivities to ions and temperature have resulted in erratic results and adjustment of the formulation is often required during use; this hampers the drilling operation. Certain forms of crystalline layered mixed metal hydroxides are disclosed, e.g., in US-A-4,477,367; 4,446,201; and 4,392,979; wherein various Li, Mg, Cu, Zn, Mn, Fe, Co, and Ni compounds form part of the crystal structure. Other layered compounds are disclosed, e.g., in US-A-2,395,931; 2,413,184; 3,300,577; and 3,567,472. These compounds are prepared through various reactions including coprecipitations, intercalations, acid digestions and base digestions. In the drilling of oil wells, drilling fluids or "muds" perform several functions: 1. They remove cuttings from the hole. 2. They cool the drill bit. 3. They provide hydrostatic pressure to balance formation pressure. 4. They control ingress of fluids into the formation and protect the formation. In order to perform some of these functions it is necessary for the fluid to possess pseudoplastic rheology. There are several shear zones in the bore hole of a well and the fluid should have varying viscosities in these zones. In the annulus between the drill pipe and the formation, the shear rate is approximately 100 to 1000 sec⁻¹. At the drill bit the shear rate is between 25,000 and 200,000 sec⁻¹. In the mud pit the shear rate is less than 30 sec⁻¹. In order to carry drill solids at low shear rates, a fluid must have a significant viscosity. However, if the fluid has a high viscosity at the drill bit, a significant amount of energy is lost in pumping the fluid. Thus, a good drilling fluid should be shear thinning. It is very important that the fluid maintain this rheology throughout the drilling process. However, many adverse conditions that typically inhibit the performance of existing drilling fluids are, the presence of various cations (such as calcium and magnesium), fluctuating salt concentrations, high temperatures, oxidative conditions, and the presence of bacteria. Some of the commercially accepted gelling agents that are used in water-based drilling fluids are polymers such as xanthan gum, guar gum and polyacrylamides. Non-polymer gelling agents are typically clays such as bentonite and attapulgite. Each of these gelling agents has its own limitations. The polymers typically have instability to various salts, they are susceptible to oxidation and bacterial attack, they break down under extensive shear, and they are thermally stable to only 120 to 150°C. The most popular clay gelling agent is bentonite. The bentonite is severely affected by polyvalent cations and is limited to about 100°C unless certain thinners are incorporated. However, bentonite cannot be oxidized under hydrothermal conditions, and it is stable in a liquid carrier to high shear conditions. The present invention provides a novel gelling component of a process fluid, for example, a drilling fluid, drilling mud, fracture fluid, packer fluid, and completion fluid, or other thixotropic fluid, said gelling component, also referred to as a thickening agent, being a mixed metal layered hydroxide of the empirical formula Li m D d T(OH) (m+2d+3+na) A n / a·qH₂O (I) where m is from zero to 1; D represents divalent metal ions; d is from zero to 4; T represents trivalent metal ions; A represents monovalent or polyvalent anions or negative-valence radicals other than the OH⁻ ions; a is the number of ions of A; n is the valence of A; na is from zero to -3; q is from zero to 6; (m+d) is greater than zero; and (m+2d+3+na) is equal to or greater than 3. This layered mixed metal hydroxide is prepared by an instantaneous ("flash") coprecipitation wherein soluble compounds, e.g., salts, of the metals are intimately mixed (using non-shearing agitation or mixing) with an alkaline material which supplies hydroxyl group to form mixed metal hydrous oxide crystals. Said crystals are essentially monolayer, or one layer of the mixed metal hydroxide per unit cell. In a liquid carrier the crystals are essentially monodispersed demonstrating that individual crystals are distinct layers of the mixed metal hydroxide. These monolayer crystals are believed to be novel. In the above formula, the number of Li ions is represented by the value of m and may be from zero to 1, preferably 0.5 to 0.75. The D metal represents divalent metal ions and may be Mg, Ca, Ba, Sr, Mn, Fe, Co, Ni, Cu, or Zn, preferably Mg, Ca, Mn, Fe, Co, Ni, Cu, or Zn, most preferably Mg or Ca, or mixtures of these. The value of d, the number of D ions in formula (I), may be zero to 4, preferably 1 to 3, most preferably about 1. The amount of (m+d) is greater than zero. The T metal may be Al, Ga, Cr or Fe, preferably Al or Fe, most preferably Al. In the subscript (m+2d+3+na), the na is actually a negative number because the anion valence, n, is negative. Addition of a negative number results in a subtraction. The A anions may be monovalent, divalent, trivalent, or polyvalent; and may be inorganic ions such as halide, sulfate, nitrate, phosphate, or carbonate, preferably halide, sulfate, phosphate or carbonate, or they may be hydrophylic organic ions such as glycolate, lignosulfate, polycarboxylate, or polyacrylate or salts thereof, such as sodium polyacrylate. These anions often are the same as the anions which formed part of the metal compound precursors from which the novel crystals are formed. The compound of formula (I) is substantially balanced and preferably neutral in charge. "Substantially balanced" means there is little positive or negative net charge to the compound. The liquid which is gelled by the present described novel mixed metal hydroxides may be an aqueous liquid, such as water or aqueous solution, or a hydrophylic organic material such as alcohol or ketone; also a dispersion or emulsion comprising an aqueous medium which contains non-soluble ingredients (organic and/or inorganic) in dispersed form can be gelled by use of the presently described gelling agent. Whereas the present gelling agent is found useful as a thickening agent for water-based metal working fluids, fire fighting fluids, food additives, hydraulic fluids, latex paints, stripping fluids, lubricants, and others, especially where extreme pseudoplasticity is a desirable property, it is particularly useful when employed as an additive to form thixotropic fluids for use in subterranean operations, such as drilling fluids, drilling muds, fracture fluids, packer fluids, completion fluids, and the like, especially drilling fluids, whether it be for drilling oil wells, water wells, or gas wells, including drilling in the ocean floor. The present invention also provides a process for preparing the compounds of formula I by flash instantaneous coprecipitation resulting from intimate non-shearing mixing of (a) a solution of predetermined quantities of compounds which provide the desired predetermined amounts of Li, D, T, and A ions with (b) an alkaline solutions which provides a source of hydroxyl ions to cause coprecipitation of such Lie, D, and T metals as crystalline mixed metal compounds containing, as anions, hydroxyl ions and A ions. The "flash" co-precipitation technique employed, in preparing the present gelling agents, closely approximates steady-state reaction wherein the ratio of reactant feeds (cations/anions), and other reaction conditions (e.g. concentration, pH, temperature) are substantially constant. Such constant conditions are substantially achieved by mixing or combining a metered stream (or regularly fed portions) of the "cation solution" with a predetermined amount of the "anion solution"; the combined solutions comprise a mixture (containing reaction product as a floc), which is removed from the mixing area or zone. In this manner, each new portion of cation solution "sees" a new portion of anion solution, neither of these new portions having been involved in the mixing of the previous portions. Thus one obtains substantially constant conditions of temperature, pH, and ratio of feed reactants and obtains a more homogeneous, compositionally uniform product, each new portion of product having undergone the same orders (and rates) of reaction as any previous portion of product. By performing the reaction in this meanner the formation of "flocs" is maximized, so long as there is not enough shearing agitation to break up the flocs. This steady-state reaction is in contradistinction to a non-steady reaction wherein reaction conditions (such as temperature, pH, ratio of reactants) are variable rather than constant. For instance, if one has a vessel containing a cation solution to which one slowly adds a stream (or portions) of the anion solution, the first bit of anion solution "sees" all the cations, the second bit sees not as many cations but sees some reaction product as well. Each subsequent bit of anion solution "sees" a different quantity of cations and product; the ratio of cations/anions being united is changing throughout the procedure leading, very likely, to a non-homogeneous or non-uniform product as a result of there having been different orders of reactivity encountered, or different rates of reaction over the course of the anion addition. Here, in such a non-steady state reaction, one encounters the likelihood that some of the subsequent anions may react with some of the already formed product, giving rise to a mixture of products. One may theorize that an absolutely constant, uniform product is prepared under absolutely constant conditions by reacting a molecule of one reactant with the requisite or stoichiometric molecular amount of the other reactant. Such absolutely constant conditions are not achievable in commercial practice, but one may substantially approach such conditions by employing substantially steady-state conditions where constant conditions are closely approached. The temperature of the reacting mixture should, of course, be above freezing and not above boiling. Going above boiling would require a closed, pressured vessel to prevent evaporation of the liquid and this is generally unproductive, offering no additional benefit commensurate with the added expense. A temperature below 5°C would be expected to slow down the reaction rate. An ambient temperature in the range of 15 to 40°C may be used, but warmer temperatures up to 80°C or more may be quite beneficial, not only in keeping the beginning compounds in solution, but also in speeding the rate at which the compounds react. A mixture of the selected soluble metal compounds, especially the acid salts (e.g. chloride, nitrate, sulphate, phosphate) are dissolved in an aqueous carrier. The ratios of the metal ions in the solution are predetermined to give the ratios desired in the final product. The concentration limit of the metal compounds in the solution is governed, in part, by the saturation concentration of the least soluble of the metal compounds in the solution; any non-dissolved portions of the metal compounds may remain in the final product as a separate phase, which is not a serious problem, usually, if the concentration of such separate phase is a relatively low amount in comparison to the soluble portions, preferably not more than 20% of the amount of soluble portions. The solution is then mixed rapidly and intimately with an alkaline source of OH⁻ ions while substantially avoiding shearing agitation thereby forming monodispersed crystals of layered mixed metal hydroxides. One convenient way of achieving such mixing is by flowing the diverse feed streams into a mixing tee from which the mixture flows, carrying the reaction product, including the monodispersed layered mixed metal hydroxides of formula (I) above. The mixture may then be filtered, washed with fresh water to remove extraneous soluble ions (such as Na⁺, NH₄⁺ ions and other soluble ions) which are not part of the desired product. The particular transmission electron microscope used in conducting crystallographic analyses of the subject mixed metal layered hydroxides was operated at its maximum limits of detection, i.e. a resolution of about 8 angstroms (0.8 nm). The crystals were so thin, with respect to their diameter, that some curling of the monolayer crystals was found, making precise thickness measurements difficult, but reasonable estimates place the crystal thickness in the range of 8 to 16 angstroms (0.8-1.6 nm) for various crystals. During the drying process some agglomeration of crystals is apparent, as detected in the analysis, giving rise to particles which contain a plurality of the monolayer unit cell structures. Many flat, unagglomerated crystals are detectable in the analyses. These monolayer unit crystals are in contradistinction to 2-layer and 3-layer unit cell structures referred to in e.g., US-A-4,461,714. One process for preparing the composition, however not exclusively the only process, is to react a solution of metal salts such as magnesium and aluminum salts (the salt concentrations are preferably less than 2 molar and most preferably about 0.25 molar) with a source of hydroxide ion. Sodium hydroxide may be used, for instance, however, ammonium hydroxide is preferable. The concentration and the quantities of the base are at least sufficient to precipitate the mixed metal hydroxide compound. For ammonium hydroxide, the most preferable range is between 1 to 1.5 moles of OH⁻ per mole of anion, eg. Cl⁻. The flash co-precipitation should be done with little or no shear so that the resultant flocs are not destroyed. One method of accomplishing this is to flow two streams, the salt stream and the base stream, against one another so that they impinge in a low shear, converging zone such as is found in a tee. The reaction product is then filtered and washed, producing a filtercake of approximately 10% solids. At this point if the layered mixed metal hydroxide composition has been washed carefully to reduce the dissolved salt concentration to a relatively low point, for example, about 300 ppm or less, an odd phenomenon occurs. Over a period of time, the filter cake changes from a solid waxy material to an opalescent or iridescent liquid that efficiently scatters light. If ionic material is added back to the dispersion, the viscosity increases drastically and the dispersion gels. The rate of "relaxation" is dependent on the free ion concentrations in the dispersion and will not occur if the concentrations are too high. The effect of various ions on the relaxation process differs. For example, the relaxation process is more tolerant of monovalent ions such as chloride ions than it is of polyvalent ions such as sulfate, carbonate, or phosphate. If the relaxed dispersion is dried, when the solids level reaches 20 to 25%, the material forms a solid hard translucent material that is very brittle. It can be crushed to a powder, even though it is approximately 80% water. This solid will not redisperse well in water or other hydrophylic solvents. Even if shear is applied with a Waring Blender or an ultrasonic cell disrupter, the solids cannot be made to form stable dispersions. One fruitful method of drying the material is to add a quantity of hydrophylic organic material such as glycerine or polyglycol to the relaxed dispersion prior to drying. The material may be dried to 5% water, or less, and still be redispersible. If this is done the resultant dry material will spontaneously disperse in water. If a salt is then added to this dispersion, the fluid will build viscosity in the same manner as the product that has never been dried. This drying technique does not work if significant quantities of dissolved salts are present in the dispersion. In this case some dispersion may be possible, but the resultant fluid will not build viscosity. One of the distinguishing features of the presently disclosed mixed metal hydrous oxides is the fact that upon filtration after the flash coprecipitation there remains on the filter a gel which is predominantly the liquid phase with the crystalline hydrous oxides so swollen by the liquid that they are not visible as a solid phase. One might call the gel a "semi-solution" or "quasi-solution" and it has the appearance and feel of a semi-solid wax. This is in contradistinction to prior art hydrous oxide precipitates which are readily filtered out of liquid as a discreet particulate solid material. Apparently, the particular crystalline morphology obtained here permits or causes the imbibing and holding of large amounts of the liquid. The gelling agent may also be composed of either pure mixed metal hydroxide compounds or physical mixtures of the layered compounds with themselves or other hydrous oxides of the D or T metals such as, for example, hydrous alumina, hydrous magnesia, hydrous iron oxides, hydrous zinc oxide, and hydrous chromium oxides. In each of the subsequent examples, the mixed metal layered hydroxide compound was prepared by coprecipitation. The compound was then filtered and washed to produce a substantially pure material. This purified product was then dispersed in water to build the thickened fluid. The following examples are to illustrate certain embodiments, but the invention is not limited to the particular embodiments shown. Example 1 A 0.25 molar solution of MgCl₂·AlCl₃ was prepared. This solution then pumped through a peristaltic pump into one arm of a tee. A 2.5 molar solution of NH₄OH was pumped into a second opposite arm of the tee so that the two solutions met in the tee. The product poured out of the third arm and into a beaker. The flows of the two solutions were carefully adjusted so that the product of the coprecipitation reaction would have a pH of about 9.5. In this situation that amounts to about a 10 to 20% excess of NH₄OH. The reactor product consisted of delicate flocs of MgAl(OH) 4.7 Cl 0.3 suspended in an aqueous solution of NH₄Cl. The dispersion was then carefully poured into a Buchner Funnel with a medium paper filter. The product was filtered and washed in the filter with water to remove the excess NH₄Cl. After washing the dissolved Cl⁻ concentration was about 300 ppm as measured by Cl⁻ specific ion electrode. The filter cake that resulted was translucent, but not optically clear. The resultant cake was about 9% solids by weight, determined by drying at 150°C for 16 hrs. The cake had the consistency of soft candle wax. The product was analysed for Mg and Al. It was found that the Mg:Al ratio was essentially 1:1. Electron micrographic analysis of the product showed tiny platelets with diameters of 300 to 500 angstroms. The particles were so thin that in some cases, they curled. Estimates of thicknesses of these particles are 8 to 16 angstroms (0.8-1.6 nm). The maximum resolution on the microscope is about 8 angstroms (0.8 nm). The theoretical thickness of one layer of crystalline MgAl(OH) 4.7 Cl 0.3 is about 7.5 angstroms (0.75 nm). These data strongly suggest that some of the particles are one to two layers thick. It should also be noted that in the process of preparing the sample for electron microscopy, the material was dried which apparently caused a degree of agglomeration of the crystals. After setting undisturbed for about 16 hours, the filter cake had the consistency of petroleum jelly. After about 48 hours, the material was a thixotropic liquid. The relaxation process continued for about 5 days. At the end of this time, the product was more viscous than water but it was pourable. A small amount of NaCl was added to a sample of the liquid and it gelled almost instantaneously. A quantity of glycerine was added to the product that was equal to 17% by weight of the solids present in the dispersion. When the glycerine was added to the dispersion, the apparent viscosity decreased to about 1 centipoise (mPa.s). The slurry was then placed in a pan and dried in an oven for 16 hours. On large scale, more efficient drying equipment would be utilized, such as spray dryers or shelf dryers. The product from the oven was a brittle solid that could be easily crushed. It was 95% solids by weight, including the glycerine. When the solid material was placed in water, it spontaneously dispersed in less than 5 minutes. Phosphate ions in the form of NaH₂PO₄ were added to the dispersion and it increased in viscosity in the same way that it did before drying. Example 2 In a similar manner, a solution of magnesium and aluminum chlorides which had a composition of 4 magnesiums per 1 aluminum was reacted with NH₄OH. The concentration of Mg 3.2 Al(OH) 8.4 Cl₁ was about 1 molar. The product was filtered and washed immediately. After about 24 hours, the filter cake had relaxed to a very thin fluid. The solids content of the fluid was about 10% and the bulk analysis of the solids indicated that the Mg:Al ratio was 3.2:1. Transmission electron microscopy was performed on the material and it was found that the product is made up of platelets having an average diameter of 500 angstroms (±100 angstroms) (50±10 nm). Some of the crystals are lying on edge so that it is possible to estimate the crystallite thickness. It appears that there are crystals that are only about 10 angstroms thick. This suggests that the material is essentially monolayer. The literature (Crystal Structures of Some Double Hydroxide Minerals Taylor, H.F.W., Mineralogical Magazine, Volume 39, Number 304, Dec. 1973) teaches that known magnesium aluminum hydroxide compounds having Mg:Al ratios as high as 4:1 are in the hydrotalcite class of compounds. The crystal structure data that has been accumulated in the literature indicates that there are basically two types of hydrotalcite, one having a c-axis spacing of about 24 angstroms (2.4 nm) and another having a c-axis spacing of about 15 angstroms (1.5 nm). Since the data revealed here indicates that many of the crystals prepared in this example are thinner in the c direction than hydrotalcite, then the crystal structure data indicate that the material must have a crystal structure that is different than hydrotalcite. Example 3 One part of aqueous solution containing 23.8% by weight of MgCl₂·AlCl₃ is diluted with 4 parts of deionized water and sufficient MgSO₄ is added to provide a calculated ratio for Mg:Al of 4:1. The solution, at room temperature, is rapidly and thoroughly mixed, without any substantial shearing forces, with a stoichiometric quantity of NH₄OH, thus providing an instantaneous or flash coprecipitation of Mg 3.2 Al(OH) 8.4 Cl₁. The reaction mixture is filtered, leaving a semi-solid waxy gel on the filter which contains about 6% by wt. of the coprecipitate. The gel is washed on the filter, with additional quantities of deionized water to substantially remove extraneous material such as NH₄OH, SO -2 / 4 , and Cl⁻. However, the final Cl⁻ concentration was greater than 0.02 molar. The filter cake is diluted with deionized water to make a 2.5% dispersion which, measured with a Brookfield viscometer, is found to be about 556 times as viscous as water at low shear rates and is thixotrophic. Enough BaSO₄ was added to the aqueous slurry to raise the density to about 10 lb/gal (1.2 kg/ℓ). The BaSO₄ suspended well and did not settle out over a period of 6 months. Example 4 A similar experiment was performed in which the Mg:Al ratio was 1:4. The product was washed until the Cl - / . content was less than 110 ppm. Upon the addition of salt, this material was capable of building viscosity and supporting BaSO₄ in suspension for extended periods of time. Example A (for comparison) MgSO 4.7 H₂O was dissolved in enough water to make a 0.25 molar solution. This was then reacted with KOH to make Mg(OH)₂ in a reaction tee. The product was filtered and washed to essentially nil Cl⁻ concentration. This fluid was then dispersed in water and found to be thixotropic. BaSO₄ was then dispersed in the slurry and it was allowed to stand undisturbed for 6 months; the BaSO₄ was mostly settled out of the dispersion. Example B (for comparison) A 1-molar solution of Al₂(SO₄)₃ was prepared and precipitated with NH₄OH. The resultant product was thoroughly washed and reslurried to make a 2.5% dispersion. BaSO₄ was added to test the suspension characteristics of the slurry. The slurry was allowed to sit undisturbed for 6 months; the BaSO₄ was mostly settled out of the dispersion. Example 5 A 0.25 molar solution of MgCl₂·AlCl₃ was prepared. This solution was reacted with NH₄OH to precipitate a material having a Mg:Al ratio of 1:1. The product was filtered and washed to a point that the Cl⁻ concentration in the cake was 2800 ppm. The product was then dispersed in water forming a thixotropic slurry. It was then weighted to 9.5 lb/gal (1.15 kg/ℓ). with BaSO₄ and allowed to set for 6 months; there was very little settling. There was a syneresis effect in which the top 10% of the fluid was clear water, but there was only about a 10% density gradient through the remaining other 90% of the fluid. Example 6 100 ml. of 1 molar MgCl₂·AlCl₃ solution was diluted with 200 ml of deionized water and 14.7 grams of CaCl₂ were added. The resulting aqueous salt solution was then flash precipitated with NH₄OH at a reaction pH of 10. The slurry was filtered and washed. The resulting product was then dispersed in water and weighted as described in previous examples. This slurry was also thixotropic. Example 7 A fairly large quantity of flash precipitated MgAl(OH) 4.7 Cl 0.3 was prepared and washed. The following tests were then performed on fluids containing the gelling agent. 1. Rheology data 2. Shear stability 3. Time dependence 4. pH dependence 5. KCl dependence 6. CaCl₂ dependence 7. Filtration data 8. Weighted fluids 9. Thermal stability 10. Na₂SO₃ stability Rheology Data The rheology data that is illustrated here was obtained using a Fann 35 rotary viscometer. Unless otherwise stated all of the data were obtained at 46°C. Table 1 is a comparison of plastic viscosity, yield point and 10 sec and 10 min gel strengths for 7 lb/bbl (20 kg/m³) MgAl(OH) 4.7 Cl 0.3 , 15 lb/bbl (43 kg/m³) Aquagel, (a beneficiated sodium bentonite marketed by Baroid), and 20 lb/bbl (57 kg/m³) Aquagel. The most notable differences are in the plastic viscosities and gel strengths. In the case of the MgAl(OH) 4.7 Cl 0.3 the plastic viscosity is very low, being about one eighth of the value of the yield point. In the case of the Aquagel samples, the plastic viscosity is greater than the yield point. The gel strengths of the MgAl(OH) 4.7 Cl 0.3 are nearly equal while those of the Aquagel fluids are significantly different. These data indicate that the MgAl(OH) 4.7 Cl 0.3 fluid gels vary rapidly and does not continue to build gel strength. Such a fluid is said to produce "fragile gels". The Aquagel fluids gel more slowly and continue to build over a longer period of time forming "progressive gels". Fragile gels are more desirable for the drilling of oil wells because the fluid will not become so strongly gelled that it cannot be easily broken. RHEOLOGY DATA Agent/ Concentration Plastic Viscosity (cp)(mPa.s) Yield Point (lb/100 ft.²) (kg/100m²) Gel strengths 10 sec 10 min (lb 100 ft.²) (kg/100m²) MgAl(OH) 4.7 Cl 0.3 7 lb/bbl (20 kg/m³) 2.5(2.5) 21 (103) 9.5 (46) 11.0 (53.7) Aquagel 15 lb/bbl (43 kg/m³) 7.8(7.8) 4.5 (22) 1.8 (8.8) 2.0 (9.8) Aquagel 20 lb/bbl (57 kg/m³) 15(15) 14.5 (70.8) 3.0 (14.5) 8.3 (41.5) Table 2 tabulates shear stress and shear rate data for a 7 lb/bbl (20 kg/m³) slurry prepared with MgAl(OH) 4.7 Cl 0.3 . These data were generated using a capillary viscometer. The fluid is extremely shear thinning from about 1 sec⁻¹ to about 25,000 sec⁻¹ where it becomes newtonian. This is typical of all water based drilling fluids. The viscosity of this fluid at low shear rates is about 600 cp (mPa.s) but, at the drill bit, the viscosity is only about 4.5 cp (mPa.s). CAPILLARY VISCOMETRY DATA Shear Rate (sec-¹) Shear Stress Viscosity (cp)(=mPa.s) (kg/100 m²) (lb/100 ft.²) 10.35 59.08 12.10 597.40 20.60 80.56 16.50 409.30 40.95 92.28 18.90 235.85 102.80 114.25 23.40 116.32 204.48 130.36 26.70 66.72 393.00 152.14 31.16 40.52 666.75 179.67 36.80 28.20 981.00 190.71 39.06 20.35 1257.50 227.03 46.50 18.90 1720.00 230.74 47.26 14.04 2527.60 292.95 60.00 12.13 6551.60 394.50 80.80 6.30 13694.20 687.93 140.90 5.26 25552.40 1098.55 225.00 4.50 61743.30 2735.62 560.30 4.64 87019.00 3961.11 811.30 4.76 Shear Stability Data Table 3 tabulates plastic viscosity, yield point, and gel strengths versus time of shear in a Waring Blender. Except for some change in the first few minutes, the viscosity parameters remain fairly constant. The capillary viscometry data also indicate that the MgAl(OH) 4.7 Cl 0.3 fluids are shear stable since they were passed through the capillary viscometer three times and no observable shear degradation occurred. SHEAR STABILITY DATA Shear Time (min) Plastic Viscosity(CP) (=mPa.s) Yield Point (lb/100 ft.²) (kg/100 m²) Gel-strengths 10 sec 10 min (lb/100 ft.²) (kg/100 m²) 0.0 3.0 15.0 (73.2) 13.0 (63.5) 15.0 (73.2) 10.0 2.0 8.0 (39.1) 8.0 (39.1) 7.0 (34.2) 35.0 2.0 8.0 (39.1) 8.0 (39.1) 8.0 (39.1) 75.0 2.5 11.0 (53.7) 9.0 (43.9) 10.0 (48.8) Time Dependence Data Table 4 lists the plastic viscosity, yield point and gel strengths for a 7 lb/bbl(20 kg/m³). MgAl(OH) 4.7 Cl 0.3 slurry over a period of 2.5 days. These data indicate that there is some change in yield point over the first several days. However, the change is not considered to be significant. The fluids from these tests were also allowed to set for 3 months and the rheology was again measured on them. There were virtually no changes in the fluids. TIME DEPENDENCE DATA Time days Plastic Viscosity(cp) (=mPa.s) Yield Point (lb/100 ft.²) (kg/100 m²) Gel-strengths 10 sec 10 min (lb/100 ft.²) (lb/100 ft.²) 0.0 5.0 5.5 (26.9) 3.0 (14.6) 6.0 (29.3) 0.3 5.0 7.0 (34.2) 3.5 (17.1) 6.0 (29.3) 1.0 5.0 7.0 (34.2) 3.5 (17.1) 5.8 (28.3) 2.0 5.0 6.2 (30.3) 3.5 (17.1) 5.8 (28.3) 2.5 5.0 6.0 (29.3) 3.5 (17.1) 5.5 (26.9) pH Effects Table 5 lists plastic viscosity, yield point, and gel strengths versus pH. Below about pH 6 the yield point drops off drastically. It is flat to about pH 11. Above that point, it increases very rapidly. These results are good since the drilling operations are run from pH about 9.5 to about 10.5. pH EFFECTS ON FRESH WATER SYSTEM pH Plastic Viscosity (cp) (=mPa.s) Yield Point (lb/100 ft.²) (kg/100 m²) Gel-strengths 10 sec 10 min (lb/100 ft.²) (kg/100 m²) 4.5 3.0 2.5 (12.2) 2.5 (12.2) 5.0 (24.4) 7.0 3.0 22.0 (107.4) 7.0 (34.2) 7.0 (34.2) 10.5 3.0 25.0 (122.1) 20.0 (97.7) 21.0 (102.5) 12.0 3.0 55.0 (268.5) 12.0 (58.6) 12.0 (58.6) Table 6 tabulates rheology parameters for a fluid composed of 35% CaCl₂ and about 6 lb/bbl (17 kg/m³) of MgAl(OH) 4.7 Cl 0.3 at pH 6 and pH 8.5. There is basically no change in rheology. pH DATA pH Plastic Viscosity (cp) (=mPa.s) Yield Point (lb/100 ft.²) (kg/100 m²) Gel-strengths 10 sec 10 min (lb/100 ft.²) (kg/100 m²) 6.0 8.5 14 (68.4) 6.5 (31.7) 8.5 (41.5) 8.5 8.0 14 (68.4) 8.0 (39.1) 10 (48.8) KCl and CaCl₂ Stability Data KCl is often added in varying quantities to water-based drilling fluids for shale stabilization. Table 7 is a listing of the various rheological properties against KCl concentration from 0% to 27%. The experiment was performed by starting with an aqueous dispersion of MgAl(OH) 4.7 Cl 0.3 and adding quantities of KCl to the slurry. Increasing KCl concentrations had very little effect on the overall rheology of the fluid. A similar experiment was performed with CaCl₂, Table 8, where a drop in yield point is observed between 0.25% and 27.7%. There is also an increase in plastic viscosity. However, these changes are not of great magnitude. These data are important because they indicate that fluctations in commonly encountered salts will not have a detrimental effect on the properties of aqueous dispersions of MgAl(OH) 4.7 Cl 0.3 . KCl STABILITY DATA Concentration KCl (Wt. percent) Plastic Viscosity (cp) (=mPa.s) Yield Point (lb/100 ft.²) (kg/100 m²) Gel-strengths 10 sec 10 min (lb/100 ft.²) (kg/100 m²) 0.00 4.5 11.0 (53.7) 7.5 (36.6) 8.0 (39.1) 0.25 3.2 8.5 (41.5) 9.0 (43.9) 7.5 (36.6) 0.50 3.2 9.0 (43.9) 6.0 (29.3) 5.5 (26.9) 1.00 3.0 10.0 (48.8) 5.5 (26.9) 5.5 (26.9) 3.00 2.5 12.0 (58.6) 5.5 (26.9) 5.0 (24.4) 10.0 3.5 10.0 (48.8) 6.5 (31.7) 5.5 (26.9) 27.0 3.2 11.0 (53.7) 6.5 (31.7) 5.5 (26.9) CaCl₂ STABILITY DATA Concentration CaCl₂ (wt. percent) Plastic Viscosity(cp) (=mPa.s) Yield Point (lb/100 ft.²) (kg/100 m²) Gel-strengths 10 sec 10 min (lb/100 ft.²) (kg/100 m²) 0.35 2.5 21.0 (102.5) 9.5 (46.4) 11.0 (53.7) 27.7 6.5 15.0 (73.2) 8.5 (41.5) 8.5 (41.5) 35.0 8.0 15.0 (73.2) 8.0 (39.1) 10.0 (48.8) Filtration Data Aqueous dispersions of MgAl(OH) 4.7 Cl 0.3 exhibit very high A.P.I. fluid loss values. Thus, it is generally desirable to add fluid loss control agents to a drilling fluid built around mixed metal layered hydroxides. However, it has been found that the addition of commercially available fluid loss control agents such as starch, polyacrylates, carboxymethyl cellulose, and the like provide adequate fluid loss control (less than 10 cm³ loss in 30 min. using an A.P.I. fluid loss cell). The quantities required to give adequate control are roughly the amounts suggested by the manufacturers of the agents. Some of these data are listed in Table 9. As would be expected, the presence of drill solids such as shales is also beneficial to fluid loss control. More than one fluid loss agent may be used in a drilling fluid. FILTRATION DATA Fluid loss control agents Concentration to produce 12cm³ or less API fluid loss (lb/bbl) (kg/m³) Hydroxyethylcarboxymethylcellulose 1.5 (4.3) Hydroxyethylcarboxymethylcellulose (low viscosity) 2.0 (5.7) Cornstarch 6.0 (17.1) Sodium polyacrylate 2.0 15.7) Weighted Fluids Table 10 lists rheology data for 9.5 and 15 lb/bbl (27 and 43 kg/m³) fluids weighted with BaSO₄. One unexpected result is that the plastic viscosity remains very low while there is a high yield point. This runs contrary to current theories concerning viscosities of aqueous dispersions. It is typically thought that as weighting material is added to an aqueous dispersion, the plastic viscosity must increase drastically. One possible explanation is that the MgAl(OH) 4.7 Cl 0.3 may be acting as a lubricant in the system. The potential outcome of such a property is that higher penetration rates may be achieved with weighted fluids than are currently possible. WEIGHTED FLUIDS DATA Mud Weight (lb/gal.) Plastic Viscosity (cp) (=mPa.s) Yield Point (lb/100 ft.²) (kg/100 m²) Gel-strengths 10 sec 10 min (lb/100 ft.²) (kg/100 m²) 9.5 3.0 24.5 (119.6) 11.0 (53.7) 15.0 (73.2) 15.0 4.0 32.0 (156.2) 14.0 (68.4) 14.0 (68.4) Thermal Stability Data Table 11 illustrates shear stress versus shear rate curves for an 8 lb/bbl (23 kg/m³) fluid before and after static thermal treatment at 400°F (204°C) for 20 hours. The result of the test is that the rheological properties, measured at 115°F (46°C) were basically unchanged. THERMAL STABILITY DATA Thermal Conditioning Plastic Viscosity (cp) (=mPa.s) Yield Point (lb/100 ft.²) (kg/100 m²) Gel-strengths 10 sec 10 min (lb/100 ft.²) (kg/100 m²) 46°C/24 hrs. 2.5 21.0 (102.5) 9.5 (46.4) 11.0 (53.7) 204°C/24 hrs. 2.5 20.0 (97.7) 8.6 (42.0) 10.0 (48.8) Na₂SO₃ Stability Na₂SO₃ is commonly added to aqueous drilling fluids in order to control corrosion by scavenging oxygen. Table 12 shows the effect of adding 1500 ppm of Na₂SO₃ to an aqueous dispersion of MgAl(OH) 4.7 Cl 0.3 . The effect is that the viscosity is generally increased. Typical levels of Na₂SO₃ are about 100 to 200 ppm. STABILITY TO Na₂SO₃ Na₂SO₃ Concentration (ppm.) Plastic Viscosity(cP) (=mPa.s) Yield Point (lb/100 ft.²) (kg/100 m²) Gel-strengths 10 sec 10 min (lb/100 ft.²) (kg/100 m²) 0.0 2.0 23.0 (112.3) 8.0 (39.1) 8.0 (39.1) 1500.0 4.0 32.0 (156.2) 8.0 (39.1) 8.0 (39.1) Example 8 A very pure, low salt concentration, monodispersed mixed metal layered hydroxide of the formula MgAl(OH) 4.7 Cl 0.3 at a concentration of 7 lbs/bbl (20 kg/m³) of aqueous solution was mixed with various weight ratios of NaH₂PO₄·H₂O and the viscosity properties at various shear rates (RPM of agitation) were obtained. These data and other rheological properties are shown in Table 13. All tests were made at ambient temperatures in the range of about 74-78°F (about 23-26°C). The addition of PO -3 / 4 ions increases the viscosity significantly. Similar, but less pronounced, results are obtained with other salts, such as NaCl, Na₂CO₃, and CaCl₂. Ratio of NaH₂PO₄·H₂O/MgAl(OH) 4.7 Cl 0.3 Test 0.0 0.1 0.2 0.3 0.4 0.5 0.6 0.7 0.8 600 rpm 5 27.5 28.5 27 27 25 24.5 21 20 300 rpm 3 23 24 22.5 23 21.5 20.5 18 16 200 rpm 2 19 20 19.5 20 19.5 18 15.5 14 100 rpm 1 15.5 16.5 16 17 17.5 15 13.5 12 6 rpm - 10 10.5 10 11.5 12.5 11 10.5 9 3 rpm - 8.5 7.5 6 7 7.5 7 8 7.5 Plastic Viscosity, cp (= mPa.s) 2 4.5 4.5 4.5 4 3.5 4 3 4 Yield Pt.,lb/100ft² (kg/100 m²) 1 18.5 (90.3) 19.5 (95.2) 18 (87.9) 19 (92.8) 18 (87.9) 16.5 (80.6) 15 (73.2) 12 (58.6) 10-sec. gel,lb/100ft² (kg/100 m²) 0 7 (34.2) 6.5 (31.7) 5.5 (26.9) 6.5 (31.7) 6.5 (31.7) 6.5 (31.7) 6 (29.3) 5.5 (26.9) 10-min. gel,lb/100ft² (kg/100 m²) 0 6.5 (31.7) 5.0 (24.4) 4.5 (22.0) 5 (24.4) 6 (29.3) 5.5 (26.9) 5.5 (26.9) 5.5 (26.9) Example 9 A solution of 11.2g of MgCl₂ and 32.7g of FeCl₃ in 300 ml of deionized H₂O is reacted with a stoichiometric amount of NH₄OH in a manner whereby rapid, thorough mixing, without using shearing agitation, is achieved; this provides a flash precipitation of a compound conforming essentially to the approximate formula Mg 1.7 Fe(OH)₆Cl 0.4 after filtering and washing. A 2.5% solids in water slurry exhibits thixotropic rheology. Example 10 In similar manner to Example 9, an aqueous solution of 31.7g AlCl₃·6H₂O, 16.96g CaCl₂·2H₂O and 500 ml of H₂O is reacted with NH₃·H₂O. The slurried product, CaAl(OH) 4.5 Cl 0.5 exhibits thixotropic rheology. Example 11 In similar-manner to Example 9, three samples are prepared in which aliquots of an aqueous 23.8% MgCl₂·AlCl₃ solution are mixed, respectively, with CaCl₂, BaCl₂, and ZnCl₂. These solutions are flash precipitated by reaction with NH₄OH to prepare, correspondingly MgCa 0.3 Al(OH)₆Cl 0.4 , MgBa 0.3 Al(OH)₆Cl 0.4 , and Mg 0.3 Zn 0.3 Al(OH)₆Cl 0.4 . The precipitates are filtered, washed, and diluted to about 2.5% solids; each so-formed dispersion demonstrates thixotropic rheology. Example 12 In a similar manner to Example 9, 0.125 moles of LiCl and 0.25 moles of AlCl₃ are dissolved in deionized H₂O. The resultant solution is reacted with 0.88 moles of NH₄OH with little or no agitation. The product, Li 0.5 Al(OH) 3.5 , is filtered and washed. A diluted sample, 6 lb/bbl (17. kg/m³), exhibits pseudoplastic rheology and, upon dispersion therein of BaSO₄, retains the BaSO₄ in suspension for extending periods of time. Example 13 A sample of MgAl(OH) 4.7 Cl 0.3 prepared by flash precipitation was diluted to 7 lb/bbl (20 kg/m³) (2% wt on a MgAl(OH) 4.7 Cl 0.3 basis) and 1.5 lb/bbl of NaH₂PO₄·H₂O (0.4% wt on a NaH₂PO₄·H₂O basis) was added with mixing. The fluid immediately became thick. The fluid was allowed to sit for 4 days and a series of diluted fluids were prepared having the following concentration; 1 lb/bbl (3 kg/m³), 2 lb/bbl (6 kg/m³), 3 lb/bbl (9 kg/m³), 4 lb/bbl (11 kg/m³), 5 lb/bbl, (14 kg/m³), and 6 lb/bbl 17 kg/m³ fluid. The following Table 14 contains plastic viscosity and yield point data for the fluids. Concentration In the Mixture (lb/bbl) Yield Point (lb/100 ft²) (kg/100 m²) Plastic Viscosity (cp)(=mPa.s) 1 1 (4.9) 1 2 2 (9.8) 1 3 9 (43.9) 2 4 14 (68.4) 2 5 18 (87.9) 2 6 22 (107.4) 3 7 28 (136.7) 3 Example 14 Quantities of 120.7 g of AlCl 3.6 H₂O, and 101.7 g of MgCl₂·6H₂O, were dissolved in 4 liters of deionized water. 20 g of NaOH pellets were dissolved in 2 liters of deionized water. These two stock solutions were pumped against one another in a tee. The resultant flocs were collected, filtered and washed. The resultant product was used to prepare a 7 lb/bbl (20 kg/m³) MgAl(OH) 4.5 Cl 0.5 fluid in water. The fluid was thickened with NaH₂PO₄. The fluid was very thixotropic and capable of supporting BaSO₄ and drill solids. Examples 15 A solution containing 0.5 molar MgCl₂ and 0.25 molar AlCl₃ was prepared in deionized water. This solution was pumped into a tee against an appropriate volume of 0.5 molar NH₄OH. The reaction product pH was 9.5. The product was filtered and washed and the composition was checked. It was found that the approximate composition was Mg 1.81 Al(OH) 5.88 Cl 0.74 ·2.2 H₂O. The product was used to prepare a 7 lb/bbl (20 kg/m³) fluid containing NaH₂PO₄. The fluid was thixotropic and was capable of supporting BaSO₄ and drill solids. Example 16 In a manner similar to Example 15, a solution containing 0.75 molar MgCl₂ and 0.25 molar AlCl₃ was prepared in deionized water. This solution was pumped into a tee against an appropriate volume of 0.5 molar NH₄OH. The reaction product pH was 9.5. The product was filtered and washed and the composition was checked. It was found that the approximate composition was Mg 2.58 Al(OH) 7.14 Cl 1.01 ·2H₂O. The product was used to prepare a 7 lb/bbl (20 kg/m³) fluid containing NaH₂PO₄. The fluid was thixotropic and was capable of supporting BaSO₄ and drill solids. Example 17 In a manner similar to Example 15, a solution containing 1.5 molar MgCl₂ and 0.25 molar AlCl₃ was prepared in deionised water. This solution was pumped into a tee against an appropriate volume of 0.5 molar NH₄OH. The reaction product pH was 9.5. The product was filtered and washed and the composition was checked. It was found that the approximate composition was Mg 3.76 Al(OH) 9.5 Cl 1.02 ·2H₂O. The product was used to prepare a 7 lb/bbl (20 kg/m³) fluid containing NaH₂PO₄. The fluid was thixotropic and was capable of supporting BaSO₄ and drill solids. Example 18 Monolayer Li 0.5 Mg 0.75 Al(OH) 4.6 Cl 0.4 is prepared by mixing together 500 ml of 1 molar LiCl, 750 ml of 1 molar MgCl₂ and 1 liter of 1 molar AlCl₃, then flash precipitating the monolayer crystals by conveying a stream of the solution with a stream of NH₄OH, the precipitate being a floc. After filtering and washing, a waxy-like filter cake is obtained which is about 4.23% solids by weight. The cake is diluted to 2% in water (i.e. about 7lbs/bbl ; 20 kg/m³) and tested with viscosifiers added, each in the amount of about 0.5 lb/bbl (1.5 kg/m³), as shown in Table 16 below. Viscosifier Plastic Viscosity (cp)(=mPa.s) Yield Point (lb/100 ft²) (kg/100m²) None (control) 4.0 7.0 (34.2) NaH₂PO₄ 6.5 15.5 (75.7) NaHCO₃ 4.0 7.0 (34.2) Al₂SO₄·9H₂O 4.5 7.0 (34.2) Miscellaneous Properties Due to the chemical composition it is essentially impossible to oxidise MgAl(OH) 4.7 Cl 0.3 . This is of great interest to the oil industry since it is not possible to totally eliminate oxygen and heat in drilling operations. MgAl(OH) 4.7 Cl 0.3 is also uneffected by typical bacteria. Samples of formulated fluids have been stored with periodic exposure to the air for about 6 months and no bacterial colonies have been observed. MgAl(OH) 4.7 Cl 0.3 is also totally soluble in mineral acids. This is of great importance since it is often desirable to acidize formations after a well is drilled.

Claims: Claims for the following Contracting States : BE, CH, DE, FR, GB, IT, LI, LU, NL, SE A crystalline mixed metal layered hydroxide compound conforming to the empirical formula Li m D d T(OH) (m+2d+3+na) A n / a·qH₂O (I) D represents divalent metal ions; T represents trivalent metal ions; A represents anions or negative-valence radicals other than OH⁻ ions; m is from zero to 1; d is from zero to 4; a is the number of ions of A; (m+d) is greater than zero; n is the valence of A; na is from zero to -3; q is from zero to 6; and (m+2d+3+na) is equal to or greater than 3, characterized in that the compound is in the form of monolayer unit cell crystals. A compound as claimed in Claim 1, wherein m is in the range of 0.5 to 0.75. A compound as claimed in Claim 1, wherein d is in the range of 1 to 3. A compound as claimed in any one of the preceding claims, wherein D is at least one of Mg, Ca, Ba, Sr, Mn, Fe, Co, Ni, Cu and Zn. A compound as claimed in Claim 4, wherein D is at least one of Mg and Ca. A compound as claimed in any one of the preceding claims, wherein T is at least one of Al, Ga, Cr and Fe. A compound as claimed in Claim 6, wherein T is Fe or Al. A compound as claimed in any one of the preceding claims, wherein the A anion is monovalent, divalent, trivalent or polyvalent and the value of na is not zero. A compound as claimed in any one of the preceding claims, wherein the A anion is at least one of halide, sulfate, nitrate, phosphate, carbonate, glycolate, lignosulfate, polycarboxylate, polyacrylate and sodium polyacylate. A compound as claimed in any one of the preceding claims, wherein D is Mg, T is Al, and A is an inorganic anion. A compound as claimed in Claim 10, wherein the compound is MgAl(OH) 4.7 Cl 0.3 . A compound as claimed in any one of the preceding claims wherein the monolayer unit cell crystals have a thickness in the range of 0.8-1.6 nm (8 to 16 angstroms). The use of a compound as claimed in any one of the preceding claims, as a thickener for an aqueous or hydrophylic organic liquid. A composition comprising a compound as claimed in any one of Claims 1 to 12 and a liquid for use as a drilling fluid component. A composition as claimed in Claim 14, wherein said drilling fluid also contains at least one fluid loss control agent. An aqueous drilling fluid containing a compound as claimed in any one of Claims 1 to 12. A process for preparing a compound conforming to formula (I) of Claim 1, said process comprising intimate non-shearing mixing of (a) a solution of predetermined quantities of compounds which provide the desired predetermined amounts of Li, D, T and A ions with (b) an alkaline solution which provides a source of hydroxyl ions to cause coprecipitation of such Li, D and T metals as crystalline mixed metal compounds containing, as anions, hydroxyl ions and A ions; said mixing being performed in a manner to cause instantaneous precipitation of monolayer unit cell crystals. A process as claimed in Claim 17, wherein said compound is formed by merging, in a reaction zone, a measured or metered quantity of a metal cation-containing feed solution with a predetermined quantity of a hydroxyl ion-containing feed solution in a manner whereby rapid, intimate mixing is achieved in the reaction zone, while substantially avoiding shearing agitation which would break up the flocs which form during said mixing as a result of the reaction which occurs therein; and the so-formed reaction mixture is removed from the reaction zone ahead of subsequent measured or metered quantities of the feed solutions, thereby substantially avoiding the mixing, in the reaction zone, of the subsequent quantities of feed solutions with prior quantities of feed solutions; said method being carried out under substantially steady-state conditions, using substantially constant conditions, in the reaction zone, of temperature, pH, and ratio of reactants. A gelled liquid agent for thickening process fluids being thixotropic and resistant to fluid loss, said gelled liquid agent comprising: a major proportion of a liquid which is compatible or miscible with said process fluid; and a minor proportion of gellant which conforms substantially to the compound as defined in any one of Claims 1 to 12. Claims for following Contracting State : AT The use of a crystalline mixed metal layered hydroxide compound conforming to the empirical formula Li m D d T(OH) (m+2d+3+na) A n / a·qH₂O (I) D represents divalent metal ions; T represents trivalent metal ions; A represents anions or negative-valence radicals other than OH⁻ ions; m is from zero to 1; d is from zero to 4; a is the number of ions of A; (m+d) is greater than zero; n is the valence of A; na is from zero to -3; q is from zero to 6; and (m+2d+3+na) is equal to or greater than 3, and being in the form of monolayer unit cell crystals as a thickener for an aqueous or hydrophylic organic liquid. A use as claimed in Claim 1, wherein m is in the range of 0.5 to 0.75. A use as claimed in Claim 1, wherein d is in the range of 1 to 3. A use as claimed in any one of the preceding claims, wherein D is at least one of Mg, Ca, Ba, Sr, Mn, Fe, Co, Ni, Cu and Zn. A use as claimed in Claim 4, wherein D is at least one of Mg and Ca. A use as claimed in any one of the preceding claims, wherein T is at least one of Al, Ga, Cr and Fe. A use as claimed in Claim 6, wherein T is Fe or Al. A use as claimed in any one of the preceding claims, wherein the A anion is monovalent, divalent, trivalent or polyvalent and the value of na is not zero. A use as claimed in any one of the preceding claims, wherein the A anion is at least one of halide, sulfate, nitrate, phosphate, carbonate, glycolate, lignosulfate, polycarboxylate, polyacrylate and sodium polyacylate. A use as claimed in any one of the preceding claims, wherein D is Mg, T is Al, and A is an inorganic anion. A use as claimed in Claim 10, wherein the compound is MgAl(OH) 4.7 Cl 0.3 . A use as claimed in any one of the preceding claims wherein the monolayer unit cell crystals have a thickness in the range of 0.8-1.6 nm (8 to 16 angstroms). A composition comprising a compound as defined in any one of Claims 1 to 12 and a liquid for use as a drilling fluid component. A composition as claimed in Claim 13, wherein said drilling fluid also contains at least one fluid loss control agent. An aqueous drilling fluid containing a compound as defined in any one of Claims 1 to 12. A process for preparing a compound conforming to formula (I) of Claim 1, said process comprising intimate non-shearing mixing of (a) a solution of predetermined quantities of compounds which provide the desired predetermined amounts of Li, D, T and A ions with (b) an alkaline solution which provides a source of hydroxyl ions to cause coprecipitation of such Li, D and T metals as crystalline mixed metal compounds containing, as anions, hydroxyl ions and A ions; said mixing being performed in a manner to cause instantaneous precipitation of monolayer unit cell crystals. A process as claimed in Claim 16, wherein said compound is formed by merging, in a reaction zone, a measured or metered quantity of a metal cation-containing feed solution with a predetermined quantity of a hydroxyl ion-containing feed solution in a manner whereby rapid, intimate mixing is achieved in the reaction zone, while substantially avoiding shearing agitation which would break up the flocs which form during said mixing as a result of the reaction which occurs therein; and the so-formed reaction mixture is removed from the reaction zone ahead of subsequent measured or metered quantities of the feed solutions, thereby substantially avoiding the mixing, in the reaction zone, of the subsequent quantities of feed solutions with prior quantities of feed solutions; said method being carried out under substantially steady-state conditions, using substantially constant conditions, in the reaction zone, of temperature, pH, and ratio of reactants. A process as claimed in Claim 16 or Claim 17, wherein the compound of formula (I) is as defined in any one of Claims 2 to 12. A gelled liquid agent for thickening process fluids, being thixotropic and resistant to fluid loss, said gelled liquid agent comprising: a major proportion of a liquid which is compatible or miscible with said process fluid; and a minor proportion of gellant which conforms substantially to the compound as defined in any one of Claims 1 to 12.

Inventors: BURBA III, JOHN L., STROTHER, GREENE W.
Applicants: THE DOW CHEMICAL COMPANY
Application year: 1986
Main classification: C01B13
IPC codes: C01F7, C01B13, C10M177, C09K8, C10M173, C10M113, C10M125, C09K3, C01G49