THERMOSETTING RESIN COMPOSITION

Abstract: Thermosetting resin compositions of the present inven­ tion comprise a thermosetting resin and a specified class of cured polyorganosiloxane resins dispersed as extremely fine particles in the thermosetting resin. Moldings and other shaped articles prepared using these compositions are flex­ ible and exhibit small coefficients of thermal expansion and low shrinkage during molding.

Description: The present invention relates to thermosetting resin compositions and, more particularly to thermosetting resin compositions yielding flexible cured products exhibiting both a small coefficient of thermal expansion and a small degree of mold shrinkage. Thermosetting resin compositions have excellent electrical properties, including dielectric properties, volume resistivity and insulation breakdown strength, and excellent mechanical properties such as flexural strength, compressive strength and impact strength. These resins are therefore useful insulating materials for electric or electronic parts that are fabricated by a variety of methods such as transfer molding, injection molding, potting, casting, powder coating, immersion coating and dipping. Thermosetting resins are generally rigid resins. The coefficient of thermal expansion and shrinkage following molding exhibited by these resins are generally different from that of the electric or electronic part they protect. Electric and electronic part elements have relatively small coefficients of thermal expansion or low shrinkages while these values for the resins are relatively large. These large differences in expansion and shrinkage between the two materials generate excessive internal stress in the element or other structural material of the electric or electronic part after sealing, aftercure or subsequent thermal hysteresis. The stress may cause the part to malfunction or to break. In addition, these differences in coefficients of thermal expansion or shrinkages may cause the thermosetting resin itself to crack or may cause voids between the electric/electronic part and the resin. The coated part is susceptible to deterioration when water or other material invades this void. Although not directed specifically at improving the coefficient of thermal expansion or the shrinkage of molded thermosetting resins, there have been efforts to improve the properties of these materials. For example, Japanese Patent No. 52-36534[77-36534] describes an improvement in the lubricity of the surface of resin moldings by including a polysilsesquioxane powder in the moldable composition. Japanese Kokai [Laid Open] Patent Publication No. 52-14643[77-14643] teaches increasing the wear resistance of synthetic resins with respect to metals by using as the filler a finely divided cured material composed principally of a polysiloxane and an inorganic filler. Japanese Kokai [Laid Open] Patent Publication No. 48-25739 discloses adding cured silicone rubber in powder form to an epoxy resin. None of these methods provides an adequate improvement in the coefficient of thermal expansion, the shrinkage after molding or the flexural modulus of the cured resin. Japanese Kokai Patent Publication No. 58-219218[83-219218] describes a method conceived by the present inventors to solve the above-described shortcomings whereby a finely divided cured elastomeric material containing at least 10 wt. % of a straight-chain siloxane fraction is blended into the thermosetting resin. The problem with this method is that it is not necessarily easy to finely grind the cured elastomeric material. In Japanese Kokai Patent Publication No. 59-96122[84-96122], the present inventors propose overcoming the disadvantages of prior art methods by using as the additive spherical particles of a material that cures into an elastomeric material. The particles are produced by spraying a curable composition in the form of spherical particles. This method is quite effective; however, the cost of the cured particles is high due to the requirement for a plant to produce them. An objective of the present invention is to provide a thermosetting resin composition with good fluidity during molding, and which is easily released from a mold without soiling of the metal molds or exuding of a liquid onto the surface of the cured material. The cured materials exhibit good flexibility, a small coefficient of thermal expansion and a low shrinkage during molding. Summary of the Invention The objectives of this invention are achieved by dispersing a very finely divided, cured polysiloxane resin of specified composition into the thermosetting resin. The cured resin is readily ground or pulverized to produce very fine particles. The particles have an excellent affinity for the thermosetting resin and can be homogeneously dispersed in the composition. Detailed Description of the Invention This invention provides a curable, thermosetting resin composition comprising (a) 100 parts by weight of a curable organic thermosetting resin, and (b) from 1 to 100 parts by weight of a finely divided, cured polysiloxane resin (1) with an average particle size of less than 1mm, wherein at least 90 weight percent of said polysiloxane resin (1) consists of R¹R²R³SiO 1/2 units and R⁴SiO 3/2 units, and any remainder up to 10 weight percent of said cured polysiloxane resin (1) consists either of at least one member selected from the group consisting of R⁵R⁶SiO units and SiO 4/2 units, where R¹, R², R³, R⁴, R⁵, and R⁶ are individually selected from hydrogen and substituted or unsubstituted monovalent hydrocarbon radicals, and the molar ratio of R¹R²R³SiO 1/2 units of R⁴SiO 3/2 units is from 0.1 to 3, or of a block copolymer of said polysiloxane resin (1) consisting of R¹R²R³SiO 1/2 units and R⁴SiO 3/2 units and an organic resin (2) other than said resin (1). The curable organic thermosetting resin comprising ingredient (a) is the base material of the present composition and contains at least one member from the known classes of organic thermosetting resins. These classes include, but are not limited to, phenolic resins, formaldehyde resins, xylene resins, xylene-formaldehyde resins, ketone-formaldehyde resins, furan resins, urea resins, imide resins, melamine resins, alkyd resins, unsaturated polyester resins, aniline resins, sulfoamide resins, silicone resins and epoxy resins. Copolymers derived from 2 or more different resins are included within the definition of ingredient (a). Ingredient (a) can be a single resin or a mixture of 2 or more resins. The cured polysiloxane resin (1) referred to herein as ingredient (b) is readily pulverized and imparts a relatively small coefficient of thermal expansion and a low shrinkage following molding to cured products obtained from the present composition. The combined weights of R¹R²R³SiO 1/2 units and R⁴SiO 3/2 units constitute at least 90 percent of the weight of the cured resin (1). The remaining 0 to 10 weight percent can be either selected from said R⁵R⁶SiO units, and SiO 4/2 units, or a block copolymer of said resin (1) and an organic resin (2) other than said polysiloxane resin (1). Any of the R⁵R⁶SiO units can be present as linear polysiloxane blocks made up of disubstituted units and having a degree of polymerization of ten or more. The silicon-bonded radicals represented by R¹-R⁶ in the preceding formulae are individually selected from hydrogen and monovalent hydrocarbon radicals. The hydrocarbon radicals can be substituted or unsubstituted and include, but are not limited to, alkyl such as methyl, ethyl, propyl and octyl; cycloalkyl radicals such as cyclohexyl; akenyl radicals such as vinyl and allyl; aryl radicals such as phenyl and xylyl; aralkyl radicals such as phenylethyl; halogenated monovalent hydrocarbon radicals such as γ-chloropropyl and 3,3,3-trifluoropropyl; and monovalent hydrocarbon radicals substituted by epoxy, amino, hydroxyl, carboxyl, carboxylate ester and/or mercapto groups. The radicals represented by R¹-R⁶ are preferably mainly methyl based on the availability of the corresponding intermediates used to prepare the resin. Radicals such as ethyl, vinyl and/or phenyl radicals are frequently included in ingredient (b) in addition to methyl. Ingredient (b) can be prepared using any of the known methods for obtaining polysiloxane resins. For example, a mixture containing at least one halosilane, alkoxysilane and/or disiloxane which, when hydrolyzed, yields units of the general formula R¹R²R³SiO 1/2 is hydrolyzed and condensed in the presence of at least one trihalosilane or trialkoxysilane which, upon hydrolysis, yields R⁴SiO 3/2 units. The molar ratio of reactants in the reaction mixture is such as will provide a molar ratio of R¹R²R³SiO 1/2 units to R⁴SiO 3/2 units of from 0.1 to 3 in the cured resin. At least a portion of the hydroxyl or alkoxy groups present in the starting materials and/or intermediate hydrolysis products can be present in the final cured resin. The reaction mixture for preparing ingredient (b) can contain various optional reactants, including at least one dihalosilane or alkoxysilane, or a linear polysiloxane which is made up of disubstituted units and terminated with hydrolyzable groups, and which exhibits a degree of polymerization of from 10 to 1000. The units provided by these reactants in the cured resin correspond to the formula R⁵R⁶SiO. Other optional reactants for preparing ingredient (b) include at least one tetrahalosilane, alkyl silicate or polyalkylsilicate, any of which will produce SiO₄/₂ units in the cured resin. The total amount of optional reactants which can be present in the reaction mixture for ingredient (b) is such that the total weight of the units produced upon curing of these reactants constitutes up to 10 percent by weight of ingredient (b). In the alternative, up to 10 weight percent of the polysiloxane resin (1) consisting of said R¹R²R³SiO 1/2 units and said R⁴SiO 3/2 units, referred to herein as ingredient (b), can consist of a block copolymer of said polysiloxane resin containing the latter units, and an organic resin (2). The organic resin portion of these block copolymers can be any of the known thermoplastic or thermosetting types. These block copolymers can accordingly comprise up to 10 percent by weight of the polysiloxane (1), referred to herein as ingredient (b). The polysiloxane resin, ingredient (b), can be prepared by an addition reaction in the presence of a platinum-type catalyst; by a condensation reaction, which includes dehydration, dehydrogenation, alcohol liberation, deoximation, deamination, deamidation, decarboxylation and the liberation of ketone; by heating the uncured resin in the presence of organoperoxide; or by exposing the resin to γ-radiation, ultraviolet radiation or an electron beam. The cured polysiloxane resin, ingredient (b), must be pulverized in order to be dispersed in the form of extremely fine particles into ingredient (a). Unlike rubbery materials, the cured resin that constitutes component (b) is relatively easy to pulverize and usually can be ground in a mortar. When large quantities of this cured product are to be pulverized, this is readily accomplished using any of the known commercially available pulverizers. Spherically shaped resin particles that have been Spray-cured by the method described in Japanese Kokai Patent No. 59-96122[84-96122] can also be employed as ingredient (b). While using the spherical particles is undesirable from the standpoint of cost, this material is superior to the finely ground material from the standpoint of its effect on the properties of the present compositions following curing. The particle size of ingredient (b) cannot be unconditionally specified because it depends on the desired application of the thermosetting resin composition. The average particle size is generally no more than one millimeter. An average particle size of up to 200 micrometers is preferred. The present compositions contain from 1 to 100 parts by weight of ingredient (b) per 100 parts of ingredient (a). A concentration of from 5 to 50 parts by weight is preferred. When too little of ingredient (b) is present, the effect of its addition may not always be apparent. When this quantity exceeds 100 weight parts, the physical properties of the unmodified thermosetting resin, ingredient (a), may be adversely affected. In addition to ingredients (a) and (b), the composition of the present invention contains a curing agent for ingredient (a). These curing agents are known in the art, and include, but are not limited to, acid anhydride curing agents such as phthalic anhydride, pyromellitic anhydride, tetrahydrophthalic anhydride, hexahydrophthalic anhydride, succinic anhydride and benzophenonetetracarboxylic anhydride; amine curing agents such as dicyandiamide, diaminophenylmethane, diaminodiphenyl sulfone, metaphenylenediamine, bis(3-methyl-4-aminophenyl)-methane and bis(4-aminocyclohexyl)methane and phenol novolac curing agents. The choice of an appropriate curing agent is based on the type of thermosetting resin used as ingredient (a). The quantity of curing agent present cannot be unconditionally specified because this will also be dependent upon the type of curing agent used. In addition to the curing agent, a curing accelerator can also be present. Typical curing accelerators include imidazoles, tertiary amines and complexes of metals such as aluminum. In addition to the ingredients described hereinbefore, the present curable compositions can contain additives which include, but are not limited to, internal release agents known in the art such as fatty acid metal salts, ester waxes and liquid polysiloxanes; inorganic fillers such as fumed silica, fused silica, crystalline silica, hydrated alumina, talc, diatomaceous earth, mica, asbestos, calcium carbonate and glass fibers; flame retardants such as antimony oxide, halogen compounds and phosphorus compounds; silane coupling agents and pigments. These additives can be added to either ingredient (a), (b), or to both ingredients prior to blending the two ingredients together. Alternatively, the additives are added when ingredients (a) and (b) are combined. The amount of inorganic additive will be dependent upon the specific additive and its purpose, and is generally from 5 to 1000 parts by weight per 100 weight parts of ingredient (a). The present curable compositions are particularly useful for the production of moldings which must have precise dimensions. They are also quite useful as sealing agents, casting agents, coating agents, or powder coating materials for various electric and electronic parts such as transistors, integrated circuits, diodes, thermistors, transformer coils and resistors. The following examples disclose preferred compositions of this invention. Comparative examples are also provided to demonstrate the superior properties of cured materials prepared using the present compositions relative to similar compositions of the prior art. In all of the examples, "parts" refers to parts by weight and all viscosities were measured at 25°C. The examples should not be interpreted as limiting the scope of the accompanying claims. Various properties of the cured moldings were measured using the following specifications or methods. (1) Coefficient of thermal expansion: the sample is postcured at 180°C for 5 hours and measured by the method of ASTM-D696. (2) Flexural modulus: measured by the flexural test method in accordance with Japanese Industry Standard (JIS)-K6911. (3) Mold shrinkage: after molding in a metal mold, the cured product is then cooled to room temperature and measured by the method of JIS-K6911. (4) Shrinkage after postcuring: the cured product of item (3) is postcured under the conditions described in each example, cooled to room temperature and then measured by the method of JIS-K6911. (5) Scanning Electron Microscope (SEM) observations: the fracture surface of the test piece ruptured in item (2) is inspected using an electron microscope in order to determine the presence or absence of voids, which reflects the affinity (tight bonding) of ingredient (b) or the thermosetting resin, ingredient (a). Production of Cured Powder A 100 parts of a polysiloxane resin containing 35 mol percent (CH₃)₃SiO 1/2 units, 63 mole percent CH₃SiO 3/2 units, 2 mole percent (CH₃)₂(CH₂=CH)SiO 1/2 units, and exhibiting a viscosity of 0.35 Pa.s was mixed to homogeneity with 3 parts of a polymethylhydrogensiloxane exhibiting a viscosity of 0.05 Pa.s as the crosslinker, an isopropyl alcohol solution of chloroplatinic acid containing 10 ppm as platinum metal based on the total weight, and 0.1 part 3-methyl-1-butyn-3-ol. The composition (I) was cured by heating in a hot air circulation oven at 100°C for 3 hours to prepare an ingredient (b) of this invention. This cured material was easily ground to a fine powder using a mortar and passed through a 100-mesh sieve. The powder passing through the 100-mesh sieve was designated as cured powder A. Production of Cured Powder B The curable polysiloxane composition (I) produced as described in the preceding paragraph pertaining to cured powder A was sprayed from a nozzle into a nitrogen atmosphere at 200°C to prepare spherical particles of cured material having an average particle size of about 20 µm, designated as cured powder B. Production of Cured Powder C 95 parts of a polysiloxane resin containing 35 mol percent of (CH₃)₃SiO 1/2 units, 51 mol percent of CH₃SiO 3/2 units, 12 mol percent of (CH₃)₂(C₆H₅)SiO 1/2 units, 2 mol percent of (CH₃)₂(CH₂=CH)SiO 1/2 units and exhibiting a viscosity of 0.06 Pa.s was mixed, with 5 parts of a vinyl-containing polysiloxane of the average formula: CH₂=CH(CH₃)₂SiO[(CH₃)₂SiO]₅₀Si(CH₃)₂CH=CH₂. The resulting mixture was mixed to homogeneity with 5 parts of a polymethylhydrogensiloxane of the average formula: (CH₃)₃SiO[(CH₃)₂SiO]₃[(CH₃)HSiO]₅Si(CH₃)₃ as the crosslinker, an isopropyl alcohol solution of chloroplatinic acid containing 10 ppm platinum metal and 0.1 part of 3-methyl-1-butyn-3-ol. The resulting composition was cured and ground as described hereinabove for cured powder A to obtain a powder passing a 100-mesh sieve. This was designated cured powder C, and was pulverized using a mortar as easily as cured powder A. Production of Cured Powder D 100 parts of a polysiloxane resin containing 22 mol percent (CH₃)₃SiO 1/2 units, 68 mol percent CH₃SiO 3/2 units and 10 mol percent units was melt-blended at 100°C with 10 parts of a phenol novolac resin exhibiting a softening point of 80°C and a hydroxyl group equivalent weight of 100. One part of 2-methylimidazole was added, the temperature raised to 150°C and the resultant mixture allowed to stand for 30 minutes. The final cured material could be relatively easily ground to a fine powder using a mortar. The cured material passing a 100-mesh sieve was designated as cured powder D. Production of Cured Powder E (comparison example) 100 parts of a vinyl-terminated polysiloxane of the average formula: CH₂=CH(CH₃)₂SiO[(CH₃)₂SiO]₅₀₀Si(CH₃)₂CH=CH₂ was blended to homogeneity with 0.5 part 2,5-dimethyl-2,5-di(t-butylperoxy)hexane and then press-vulcanized at 170°C for 15 minutes. The rubbery cured product could not be ground up using a mortar, and was therefore ground using a pulverizer. The powder passing a 100-mesh sieve was designated as cured powder E. Production of Cured Powder F (comparison example) A polymethylsilsesquioxane produced by the hydrolysis/condensation of methyltrichlorosilane was pulverized and passed through a 100-mesh sieve to obtain cured powder material F. Example 1 30 parts of a phenol novolac resin having a softening point of 80°C and a hydroxyl equivalent weight of 100 was kneaded with 6 parts cured powder A, 70 parts fused quartz powder, 4 parts hexamethylenetetramine and 1 part carnauba wax using a roll heated to 90°C and then pulverized to yield a thermosetting phenol novolac resin composition of this invention. This resin composition was transfer molded at 175°C and 70 kg/cm² for 3 minutes and postcured at 150°C for 2 hours. The properties of the resulting molding are reported in Table 1. Example 2 A thermosetting phenol novolac resin composition was prepared as described in Example 1 with the exception that 6 parts cured powder B were used instead of 6 parts cured powder A. The resulting resin composition of this invention was molded as described in Example 1. Various properties of the molding are reported in Table 1. Comparison Example 1 A thermosetting phenol novolac resin composition outside of the scope of this invention was prepared as described in Example 1, but omitting the 6 parts cured powder material A. The composition was then molded using the method of Example 1. Various properties of the molding are reported in Table 1. Comparison Example 2 A molding was produced as described in Example 1 using 6 parts of cured powder F in place of cured powder A. The various properties of the molding are reported in Table 1. The curable composition is outside the scope of the present invention due to use of a different polysiloxane resin as cured powder F. Example 3 30 parts of a thermosetting polyimide resin obtained under the designation BT2480 from Mitsubishi Gas Chemical Co., Ltd. were kneaded with 6 parts cured powder B, 70 parts fused quartz powder, 0.6 parts carnauba wax and 0.25 parts aluminum benzoate using a roll heated at 90°C, removed from the roll and then pulverized to prepare a thermosetting polyimide resin composition of this invention. The composition was then transfer molded at 200°C and 70 kg/cm² for 6 minutes and postcured at 230°C for 3 hours. Various properties of the molding are reported in Table 2. Comparison Example 3 A molding of a thermosetting polyimide resin composition of the prior art was prepared as described in Example 3, but omitting the 6 parts of cured powder B. Various properties of the molding are reported in Table 2. Comparison Example 4 A molding of a thermosetting polyimide resin composition outside the scope of this invention was produced as described in Example 3 using 6 parts cured powder E in place of cured powder B. Various properties of this molding are reported in Table 2. Powder E is not within the scope of the present invention. Example 4 20 parts of a cresol novolac epoxy resin exhibiting a softening point of 80°C and an epoxy group equivalent weight of 220 were blended to homogeneity with 10 parts of the phenol novolac resin of Example 1, 10 parts cured powder material C, 70 parts fused silica, 0.4 parts carnauba wax and 0.1 part 2-methylimidazole using a hot roll at 90°C. The resulting curable composition was pulverized and subsequently transfer molded at 175°C and 70 kg/cm² for 2 minutes and postcured at 180°C for 12 hours. Various properties of the molding are reported in Table 3. Comparison Example 5 A prior art molding was produced using the composition and method described in Example 4, but omitting the 10 parts cured powder material C, and various properties were then measured. The results are reported in Table 3. Comparison Example 6 A molding was produced using the composition and the method described in Example 4, but substituting 10 parts cured powder E for the 10 parts of cured powder C. Various properties of the molding were measured and the results reported in Table 3. Cured powder E is outside the scope of this invention. Comparison Example 7 A molding was produced from a composition outside the scope of this invention using the method and composition described in Example 4 with 10 parts of cured powder material F instead of the 10 parts of cured powder C. Various properties of the molding are measured and the results are reported in Table 3. Example 5 15 parts of a polymethylphenylsiloxane resin containing 40 mol percent CH₃SiO 3/2 units, 10 mol percent C₆H₅(CH₃)SiO units, 40 mol percent C₆H₅SiO 3/2 units, 10 mol percent (C₆H₅)₂SiO and 3 weight percent SioH groups was blended with 15 parts of a cresol novolac epoxy resin exhibiting a softening point at 80°C and an epoxy equivalent weight of 220, 6 parts cured powder D, 70 parts fused quartz powder, 0.07 parts aluminum trisacetylacetonate and 1 part carnauba wax using a roll heated to 90°C. The resultant curable silicone-epoxy composition of this invention was removed from the hot roll, pulverized, transfer molded at 175°C and 70 kg/cm² for 2 minutes and then postcured at 180°C for 12 hours. Various properties of the resulting molding are reported in Table 4. Comparison Example 8 A molding was produced by the method and composition described in Example 5, but omitting the 6 parts cured powder D. The properties of the molding are reported in Table 4. The curable composition was outside the scope of this invention due to the absence of a cured powder corresponding to ingredient (b). composition and properties Example 5 Comparison Example 8 (a) silicone resin (parts) 15 15 epoxy resin (parts) 15 15 (b) cured powder material (parts) D 6 - mold shrinkage (%) 0.31 0.52 shrinkage after postcuring (%) 0.23 0.49 flexural modulus (kg/mm²) 1010 1420 coefficient of thermal expansion (x 10⁵/°C) 2.3 2.9 observations (voids) none -

Claims: A thermosetting resin composition comprising (a) 100 parts by weight of a curable organic thermosetting resin, and (b) from 1 to 100 parts by weight of a finely divided cured polysiloxane resin (1) with an average particle size of less than 1mm, wherein at least 90 weight percent of said polysiloxane resin (1) consists of R¹R²R³SiO 1/2 units and R⁴SiO 3/2 units and any remainder up to 10 weight percent of said cured polysiloxane resin (1) consists either of at least one member selected from the group consisting of R⁵R⁶SiO units and SiO 4/2 units, where R¹, R², R³, R⁴, R⁵, and R⁶ are individually selected from hydrogen and substituted or unsubstituted monovalent hydrocarbon radicals, the substituents being selected from the group consisting of halogen, epoxy, glycidoxy, amino, hydroxyl, carboxyl, carboxylate ester and mercapto and the molar ratio R¹R²R³SiO 1/2 units to R⁴SiO 3/2 units is from 0.1 to 3, or of a block copolymer of said polysiloxane resin (1) consisting of R¹R²R³SiO 1/2 units and R⁴SiO 3/2 units and an organic resin (2) other than said resin (1). A composition according to Claim 1, wherein the symbols R¹ - R⁶ relating to said polysiloxane resin (1) are individually selected from alkyl, aralkyl, fluoroalkyl, cycloalkyl, alkenyl and aryl radicals. A composition according to Claim 2, wherein said symbols R¹ - R⁶ are individually selected from the group consisting of methyl, ethyl, vinyl, phenyl and 3-glycidoxypropyl, the average particle size of said polysiloxane resin (1), constituting ingredient (b), being less than 200 micrometers, and wherein said thermosetting resin composition includes a curing agent for said ingredient (a). A composition according to claim 3 wherein said cured polysiloxane resin (1), constituting ingredient (b) comprises (CH₃)₃SiO 1/2 , (CH₃)₂(CH₂=CHCH₂)SiO 1/2 , and CH₃SiO 3/2 units, the average particle size of said polysiloxane resin being less than 200 micrometers, wherein said curable organic thermosetting resin constituting ingredient (a) is selected from the group consisting of phenol novolac resins, polyimide resins, and mixtures of phenol novolac epoxy resins with phenol novolac resins or with polysiloxanes bearing SiOH groups, and wherein said ingredient (b) is cured with a polyhydrogensiloxane. A composition according to Claim 4, wherein said polysiloxane resin (1) includes dimethylphenylsiloxy units. A composition according to Claim 3, wherein said polysiloxane resin (1) , comprises trimethylsiloxy, methylsiloxy and dimethyl-3-glycidoxypropylsiloxy units, and wherein said thermosetting resin composition contains an imidazole as a curing accelerator. A composition according to Claim 1, wherein said polysiloxane resin (1) contains up to 10 weight percent of R⁵R⁶SiO units which are present as linear polysiloxane blocks made up of disubstituted units and having a degree of polymerization of ten or more. A composition according to Claim 7, wherein said linear polysiloxane is a polydimethylsiloxane and the terminal units of said polydimethylsiloxane are dimethylvinylsiloxy units.

Inventors: MORITA, YOSHITSUGU, SHIRAHATA, AKIHIKO
Applicants: TORAY SILICONE COMPANY LIMITED
Application year: 1986
Main classification: C08L101
IPC codes: C08L101, C08L83, C08J3