POLYMERIC PRODUCTS AND THEIR MANUFACTURE

Abstract: HB polymers, such as copolymers of beta hydroxy butyric acid and beta hydroxy valeric acid, are provided as melt extruded films having a thickness of 5 to 2OO µm. Sheet materials may consist of such a film or the film may be laminated with other films to increase strength or impermeability. The films are best made by co-extrusion with a thermoplastic that is substantially non-tacky upon solidification. The sheet materials are of particular value as diaper backsheets and ostomy bags. They may include a layer of non-woven material.

Description: This invention relates to novel products of polyesters such as hydroxy butyric acid homopolymers and copolymers with hydroxy valeric acid (referred to below as HB polymers) and to methods of making these products. HB polymers have been known for at least 2O years. See U.S. 3,275,6lO. They are generally made biologically and they have the great advantage that they are biodegradable. This is of particular value with the increasing concern throughout the last decade or more about environmental pollution due to non-biodegradable polymeric products. Because of their environmental attractiveness they are therefore of great commercial potential importance. This is reflected by the very large number of publications in the last decade about their production and uses. Environmental problems arise at present particularly with packaging films in that the environment is increasingly contaminated with plastic bags and plastic sheets that do not degrade, or degrade only very slowly. It would therefore have been expected that HB polymers would have been formulated as packaging films but, despite the enormous amount of work that has been done on them, this has not previously proved possible. In U.S. 3,275,6lO the HB polymer is produced biologically and is then purified by a purification process involving dissolution in a solvent, followed by evaporation of the solvent to produce a film of the polymer. The solvent-cast film was described as a "milky white pliable" film. There have been many other references in the literature to films of HB polymers. Their production has, prior to the invention, always involved solvent casting, as above, and/or calendaring a coarse sheet or article. For instance in EP OO5848O HB polymer gel is oriented uniaxially or biaxially by cold rolling or drawing at temperatures preferably below l6O°C to give tough films, fibres or other shaped articles. The properties of solvent cast and/or cold calendared thin films are not commerically satisfactory in that the films are too brittle for packaging or many other uses. Some of the literature on HB polymers does describe the production of films by a multi-stage process that includes, as an early stage, a melt extrusion step. However the melt extrusion step does not itself form the desired film but instead merely reduces the HB polymer composition to a form that can then be processed into a film, e.g., by cold calendaring. For instance in U.S. 4,427,6l4 a relatively coarse article was reduced in thickness by cold processing. Thus in example 1 plaques were made by compression moulding and were then rolled at room temperature to thicknesses ranging from l.3mm down to 4OO µm. In example 4 a ribbon was made by melt extrusion through a l.5mm slot dye and was then cold calendared down to 45O µm. In example ll a sheet lmm thick was made by solution casting and was then compressed and cold calendared to give an oriented film 25µm thick. Other references to melt extrusion include melt extrusion of a 4mm diameter lace of HB polymer composition in example ll of EP OO52946 and extrusion through an orifice of diameter l.585mm to form a mono-filament, followed by drawing of this filament, in EP OlO473l. That process involves conditioning the extruded filament in a water bath before drawing and the patent notes that, although satisfactory drawing could be achieved with an 8 second conditioning time, satisfactory drawing could not be achieved when the time was only 5 seconds because the polymer was sticky. This reference is directed to a vital characteristic of HB polymers, namely that they remain sticky for a substantial time after their temperature has dropped below their melting point. For this and other reasons it has so far proved impossible to produce thin films of HB polymers and instead their use is restricted to articles that can be made relatively coarse and as performance-improving additives in other polymeric compositions, e.g., as in EP OO5246O. In particuar it has been impossible to utilise HB polymers as a partial or complete replacement for the non-biodegradable polymers (for instance polypropylene and polyvinylidene chloride) from which most modern films are produced. If the biodegradable polymers are to replace these non-degradable polymer films it will be essential to be able to convert the biodegradable polymers into thin, coherent and flexible films by a method that can be operated reliably at high speed for prolonged periods. Despite two decades of research into these polymers, this objective has not previously been attained. Although many synthetic polymeric materials can be reliable manufactured at high speed they do tend to suffer from deficiencies as regards their permeability properties. Important physical properties of films are permeability to oxygen and permeability to moisture vapour. Existing films fall into three main classes. First, films such as polyvinylidene chloride have low permeability to oxygen and to moisture vapour. Second, films such as polyethylene and polypropylene have low permeability to moisture vapour but high permeability to oxygen. Third, films such as nylon and plasticised PVC and acrylonitrile have low permeability to oxygen but rather high permeability to water vapour and, in particular, the oxygen permeability increases as the humidity increases. It would be desirable to provide a film in which the oxygen permeability is satisfactorily low and is substantially unaffected by its humidity whilst the moisture vapour permeability is sufficiently high that the film is comfortable when in contact with the body. Thus the film breathes. The only other synthetic films that have this breathing property are microperforated film, which is liable to permit leakage of liquid and has a very high oxygen permeability, and plasticised PVC, which is stretchable and liable to be toxic if held against the body for prolonged periods. Products in which an impermeable and preferably biodegradable film would appear to have great value include products such as ostomy bags and diaper backsheets. The manufacture of such products in practice necessitates melt sealing the impermeable sheet to an adjacent surface, which can be of a similar sheet or of a different material. The melt sealing is best effected by RF welding. Unfortunately existing impermeable materials, such as polyvinylidene chloride, are not suitable for melt sealing and have to be provided with an additional melt sealing layer. It would be desirable to provide an impermeable film that did not necessitate this additional layer. There are many instances where it is desirable to provide an article that is impermeable and that has additional physical characteristics, such as strength or softness, that cannot conveniently be achieved by a single ply of a water-impermeable film. In U.s. 4,372,311 a coating of a polymer that can be HB polymer is applied on to a substrate The only coating methods that are specifically described are dip, spray and brush coating methods. In GB 2,083,,762 a coating of polyvinylidene chloride or other material is applied on to a substrate. However the amount of deposited polymer is always low and tends to be variable with the result that the coated substrate is usually not sufficiently impermeable. It would therefore be desirable to be able to provide a laminate of a film of HB polymer, having the desired impermeability and other properties, with a film or other sheet material imparting desired other properties to the laminate. One object of the invention therefore is to provide improved films of HB polymer compositions, and improved ways of making such films. Another object of the invention is to provide films of HB polymer compositions that have particularly beneficial physical properties, especially oxygen impermeability and moisture permeability. Another object of the invention is to provide films that are impermeable and that can be melt bonded without the need for an intervening adhesion layer. Another object of the invention is to provide laminates, and articles formed of such laminates. We have now surprisingly found that it is possible to make a film of HB polymer compositions less than about 2OOµm thick by melt extrusion and that such films, in contrast to films made by solution casting or cold calendaring, have much improved physical properties. In particular we have surprisingly found that these melt extruded films can have very desirable oxygen impermeability and moisture permeability, can be melt sealed without the need of an adhesion layer, can be laminated to other layers and can have satisfactory optical properties even when the polymer composition includes substantial quantities of cellular debris (thereby eliminating the need for extensive purification of the composition). Films according to the invention can be very flexible, especially when a plasticiser is incorporated. In the invention a film of HB polymer composition is provided that is less than about 2OOµm thick and that has been made by melt extrusion. In this specification we use the term "HB polymer" to denote a biodegradable polymer formed of recurring units of which at least 5O% molar, and preferably lOO% molar, are units of Formula l -OC n H 2n CO- where n is 3, 4 or 5. Preferably the group C n H 2n has the formula la -CH(C m H 2m+1 )CH₂- where m is l, 2 or 3 and preferably all the groups of Formula l have m equals l or 2. For instance all the groups may have m equals l (polyhydroxy butyric acid) or at least 5O% molar of the groups may have m equals l with the remainder of the groups having m equals 2 (polyhydroxy butyric-hydroxy valeric acid). Recurring units other than those of Formula l and which are in the polymer are generally units of other hydroxy carboxylic acids of the general Formula 2 -OCR¹R²(CR³R⁴) p CO- where p is zero or an integer and R¹, R², R³ and R⁴ may each be hydrogen, hydrocarbon (e.g., alkyl, aryl, alkaryl or aralkyl), halo substituted hydrocarbon, hydroxy substituted hydrocarbon, hydroxyl or halogen, provided that the values of R¹, R², R³, R⁴ and p are not such that the unit of Formula 2 is a unit of Formula l. Particularly preferred HB polymers are beta hydroxy butyric acid homopolymers and, most preferably, copolymers with beta hydroxy valeric acid. The amount of hydroxy valeric acid units in the copolymer can be up to about 5O% molar and is usually at least about 5% molar. For many purposes amounts of from about lO to about 3O% molar are satisfactory but in some instances amounts of around 30% molar are best, for instance 20 to 40% molar. The HB polymer is preferably made by biosynthesis for instance as described in U.S. 4,477,654. It may be purified by various methods as described in, for instance, EP 14490, 15123 and 58480. However satisfactory films for many purposes can be obtained even though the composition is contaminated with cellular debris and other by-products of fermentation, as described in more detail below, and so rigorous purification methods may not be required. In this specification we use the term "HB polymer composition" to denote a composition of 50 to 100% by weight HB polymer with up to 50% by weight other materials. These other materials may include other polymers, cells or cell debris from the biosynthesis of the polymers, or additives included in the composition to improve its processing characteristics or its performance properties. Suitable additives include fillers, plasticisers, stabilisers and impact additives. Preferably the HB polymer is the only polymer in the composition and preferably at least 80% by weight of the composition is HB polymer. The composition therefore generally consists essentially of HB polymer, usually hydroxy butyric acid hompolymer or, preferably, copolymer with hydroxy valeric acid. The film is at least 5 and preferably at least about 10 µm thick. It is generally unnecessary for the film to be above about 150 µm thick and best results are generally obtained when the thickness is below about 100, and preferably below about 80 µm and most preferably below about 50 µm. Preferred films are often about 20 to 30 µm thick although for some purposes thicknesses of about 50 µm are preferred. The films of the invention can have satisfactory flexibility, coherence and other physical properties and so, for the first time, it is possible to provide HB polymer compositions in the form of films having a thickness and other properties such that they can replace conventional non-biodegradable films. A difficulty that arises when melt extruding HB polymer compositions is that the compositions remain tacky even after they have cooled to below their melting temperature (typically about l8O°C for a polyhydroxy butyrate homopolymer or about l2O°C for the preferred copolymers). The invention includes a method of melt extruding an HB polymer composition against a molten layer, and preferably between a pair of molten layers, of a thermoplastic that is substantially non-tacky upon solidification, and stretching the extruded layers, generally after solidification. The provision of the substantially non-tacky thermoplastic material reduces the risk of the HB polymer composition film sticking to itself or to the apparatus. A preferred method of the invention comprises co-extruding a laminated tube of a tubular layer of molten HB polymer composition and a tubular layer of molten thermoplastic that is substantially non-tacky on solidification. Generally the resultant laminated tube is cooled and is then inflated in order to stretch the film. The inflated tube may then be flattened. If it is desired for the film to be produced as a flat sheet the tube may subsequently be slit. The general methods of co-extruding a tacky polymer as a tube with an inner tube, and possibly an outer tube, of less tacky material are described in U.S. patents 3,88O,69l and 4,379,ll7 and the same general techniques and apparatus may be used as are illustrated and described in those patents. The said non-tacky thermoplastic is generally extruded as an internal layer of the laminated tube since it facilitates prevention of adhesion of facing surfaces of the laminated tube when that tube is collapsed, for instance prior to slitting. Often however adhesion of the extruded tube to external handling apparatus, for instance for drawing the film away from the extrusion orifice, is potentially a problem and to avoid this it is desirable to co-extrude the said non-tacky thermoplastic on the outside of the tubular layer. In the invention preferably the tubular layer has an inner layer of the said non-tacky thermoplastic, a central layer of the HB polymer composition and, preferably, an outer layer of the said non-tacky thermoplastic. Additional layers may be incorporated. The non-tacky thermoplastic layer or layers may be present solely as sacrificial layers that are to be stripped from the HB layer after that layer has finally solidified or the non-tacky thermoplastic layer, or one of the layers, may remain permanently bonded to the HB polymer layer. When the co-extruded non-tacky thermoplastic layer, or either or both of the layers, is to be sacrificial the material will be chosen such that the HB polymer composition tends to adhere strongly to that layer while the HB polymer composition is non-crystaline but will tend to become non-adherent as the HB composition crystalises. By appropriate choice of materials it is possible easily to separate the substantially non-tacky thermoplastic layer or layers from the HB polymer composition film after that has crystallised. The time necessary for crystallisation to occur will depend upon the ambient temperature and upon whether or not a crystallisation initiator is present in the composition. It may be necessary to allow the laminate to age for as long as 24 hours before delamination but it is often unnecessary to age for longer than 4 hours. Suitable nucleating agents that may be included to accelerate crystallisation include infusible inorganic or organic particulate materials such as talc and fusible organic materials that, upon cooling the polymer composition, will crystallise faster than the polymer, for instance benzoic acid. The resultant film is generally substantially unoriented, at least compared to the highly oriented films obtained by the cold drawing techniques described in, for instance, example ll of U.S. 4,427,6l4 and it is surprising that a melt extruded film that is substantially unoriented can have properties as satisfactory as the properties obtainable in the invention. However if greater degrees of orientation are required the film may be drawn further after it has crystallised and so the invention also includes oriented films. Suitable materials that can be used as the substantially non-tacky thermoplastics include polyolefins, especially polyethylene, and ethylene copolymers, preferably with vinyl acetate copolymers. Lower proportions of vinyl acetate, for instance 2 to lO%, are preferred when it is desired to be able to strip the ethylene vinyl acetate film quickly and easily from the HB polymer composition film but higher vinyl acetate contents, for instance lO to 25%, are preferred when optimum inflation of the tube is required, for instance to produce very thin films. Laminates according to the invention can be formed by calendaring an HB polymer composition film of the invention with another preformed film whilst providing an adhesive between the two layers. Preferably however the laminate is made by co-extrusion of the HB polymer composition film with suitable reinforcing or other film that will permanently adhere to it, even after crystallisation of the HB polymer composition film. The reinforcing film will then serve as the non-tacky thermoplastic layer. The reinforcing film may serve to reinforce the strength properties or to improve the permeability properties or to modify the HB film in any other suitable manner. For some products it is preferred that substantially all material in the laminate other than the biodegradable film should be water soluble so that upon discharging the laminate into water the laminate either dissolves or degrades biologically. A preferred water soluble film is polyvinyl alcohol. It is usually at least 5 and preferably at least lOµm thick. It is generally less than 2OO, preferably less than l5O and most preferably less than lOOµm thick. Preferred thicknesses are lO to 5Oµm, especially 2O to 3Oµm. Another suitable water soluble film is polyethylene oxide but for cost reasons it is desirable to keep its thickness below 2Oµm, typically 5 to l5µm. A preferred laminate comprises HB polymer composition film coextruded with polyvinyl alcohol film with a bonding layer of polyethylene oxide between the HB composition and polyvinyl alcohol. Sometimes it is desirable also to provide another bonding layer between the polyethylene oxide and the polyvinyl alcohol and a very thin layer of ethylene vinyl alcohol may be coextruded with the other films for this purpose. However for other products the incorporation of a water insoluble reinforcing or intermediate film is satisfactory, especially if that insoluble film is sufficiently pliable that it is unlikely to cause drain blockage. For instance any insoluble and non-biodegradable film components would preferably have a total thickness of not more than 5Oµm and when, as is preferred, one of the co-extruded films is polyvinylidene chloride its thickness is preferably not more than l5 or 20 µm. It is particularly preferred that the thickness of any insoluble and non-degradable film should be below 5µm so as to facilitate its physical comminution and destruction during normal water treatment operations. The laminate may consist solely of the biodegradable film and the adherent reinforcing film but it is often desirable to coextrude one or more intermediate films between the biodegradable film and the reinforcing film. These intermediate films are generally present to improve the adhesion between the biodegradable and reinforcing films. Additionally there may be one or more films over the surface of the reinforcing film. Instead of co-extruding the PHB composition film and the reinforcing film or films it is sometimes more convenient to form the HB polymer composition film and then to laminate it to the reinforcing film or films. For this purpose the HB polymer composition film may have a thickness of, for instance, about 2O to about 8O µm, often 3O to 6O µm and permanent adhesion of this film with the reinforcing film may be achieved by provision of a laminating adhesive between the films. Suitable adhesives for the lamination of films are well known and include polyurethane adhesives, especially two-component adhesives, such as the product sold by Morton Thyocol under the trade name Adcote 7lO A & C. The amount of laminating adhesive is usually in the range about l to about l5 g/m², preferably around 5 g/m². The reinforcing film can be, for instance, polyethylene typically of lO to 5O and preferably about 3O µm thickness but if impermeability to oxygen is to be reduced then the reinforcing film preferably comprises an impermeable film such as polyvinylidene chloride, optionally laminated (often on the surface distant from the HB composition) with ethylene vinyl acetate. The PVDC film typically is from 4 to 2O µm thick. It is particularly preferred to use a PVDC film of 4 to l5 µm that is co-extruded with an ethylene vinyl acetate film of 2-l5 µm thickness that provides the outer surface of the resultant laminate. An ethylene vinyl acetate film of 2-l5 µm may also be co-extruded on the side of the PVDC layer adjacent to the HB composition film. Preferably the PVDC layer is 5-ll µm thick, the or each EVA layer is 3-lO µm thick and the co-extruded film lO-2O µm thick. The total laminate preferably has an oxygen permeability of below l5O ml/m².day.bar, generally below lOO and most preferably below 8O. This laminate is especially suitable for the production of an ostomy bag, with the PVDC layer facing inwards, melt sealed around its edges. Preferred laminates according to the invention comprise an HB composition layer that is plasticised by the inclusion in the HB composition of plasticiser generally in an amount of from 5% to 4O% by weight of the HB polymer composition (including plasticiser). Typical amounts of plasticiser are from about lO to about 35% by weight of the composition. Suitable plasticisers for use in the invention include sulphonamides, such as N-ethyl-o,p-toluene sulphonamide, and glutarates such as dialkyl diether glutarate having a molecular weight of about 45O. The inclusion of plasticiser increases the permeability of the film to oxygen but the lamination, either by co-extrusion or by an adhesive layer, with polyvinylidene chloride or other impermeable film results in the production of a flexible, soft, oxygen-impermeable laminate. This is very suitable for use as a diaper backsheet or an ostomy bag. Polyvinylidene chloride films used in the invention for reducing permeability may be films of any of the appropriate vinylidene chloride polymers of 65 to lOO% vinylidene chloride and O to 35% by weight of one or more copolymerisable unsaturated monomers, such as vinyl chloride. The amounts are usually 65 to 95% and 5 to 35% by weight. Instead of or in addition to laminating the HB composition film of the invention to another film, it may be bonded to a non-woven fabric. The non-woven fabric is generally bonded to the film after the film has been stretched to its final dimensions and is solid. Bonding can be by fusion of the web to the film, for instance as a result of the provision of a very low melting layer over the film, in which event this layer may have been coextruded with the film. Preferably however the non-woven fabric is laminated with the film by calendaring the film with the non-woven fabric with a liquid adhesive composition between the fabric and the film. Suitable adhesives for this purpose are usually water soluble or decomposable adhesives, for instance polyethylene oxide, polyvinylpirrolidone/vinylpirrolidone vinylacetate copolymers, hydroxylated derivatives of polyacrylic acids, polyesters, produced by the reaction of: (a) isophthalic and terephthalic acids, sulphonated acids, one or more glycols, suitabley neutralised with sodium hydroxide. (b) isophthalic and terephthalic acids, maleic anhydride, one or more glycols, suitably neutralised with sodium hydroxide or ammonia. (c) acrylic esters, acrylic acid, acetic esters of polyhydric alcohols. The adhesive may be dispersed or dissolved in water or in an aqueous or anhydrous mixture of organic solvent, generally volatile alcohol, ketone or ester. At least 5O% and preferably at least 8O%, and most preferably all, of the fibres in the non-woven fabric are cellulosic fibres in order that they will swell in water so as to rupture the fabric and facilitate degradation of it. Preferably they are staple fibres, as opposed to continuous filaments. The non-woven fabric can be needled but this is usually unnecessary. The fibres in the fabric are preferably bonded to one another by a water soluble or dipsersable bonding agent so that this bonding agent dissolves or disperses into water when the laminate is immersed in water. Acrylic bonding agents are often suitable. The agent is preferably water soluble or dispersible. The fabric may have been made in conventional manner, for instance by forming a web of the fibres and then impregnating this web with the chosen bonding agent. The weight of fibres is generally from lO to 7O g/m² and the weight of bonding agent is generally from 2 to 5O dry weight g/m². The dry weight of the adhesive used to bond the fabric to the film is generally from 2 to lO g/m². The laminate of the non-woven fabric with the HB polymer film (and optionally other films) can provide an article combining the permeability and biodegradable properties of the film with the softness of the non-woven fabric. The non-woven fabric is prferably arranged on the surface of the film distant from the surface that is to contact liquids and thus, for instance, an ostomy bag according to the invention may have an inner layer of the film and an outer layer of the non-woven fabric. The permeability properties of the HB polymer composition films of the invention will be affected by, for instance, the thickness of the films and the amount of plasticiser or other material that is included in the HB polymer composition but it is easily possible in the invention (especially when the amount of plasticiser is low, e.g., below 10% and preferably below 5% and preferably substantially absent) to produce films that have a very low permeability to oxygen. Thus it is easily possible to produce films that have oxygen permeability of 10 to 200 (preferably 80 to 200 ml /m².day.bar (measured at 23⁰C and 0% R.H.) , It is also easily possible in the invention to produce films of the Ha polymer composition that have a satisfactorily high moisture vapour transmission. Thus it is possible to make films that have moisture vapour transmission (MVT) of at least 30 and up to 200 (preferably 40 to 150) g/m².day measured at 38⁰C and 100% ΔRH. The quoted values are especially suitable for films of 25µm thickness. The permeability to oxygen and the moisture vapour transmission are substantially inversely proportional to thickness and suitable values, per 1µm thickness, are below 2000 and above 2000, respectively, per µm. Thus in the invention it is possible to provide films in which the oxygen permeability is satisfactorily low and is substantially unaffected by its humidity whilst the moisture vapour permeability is sufficiently high that the film is comfortable when in contact with the body. Thus the film breathes. The only other synthetic films that have this breathing property are microperforated film, which is liable to permit leakage of liquid and has a very high oxygen permeability, and plasticised PVC, which is stretchable and liable to be toxic if held against the body for prolonged periods. The extruded HB films of the invention can have good gloss and low haze. The haze is generally below 20%, preferably lO to 2O%, measured by ASTM D-lOO3 using a Gardner haze meter. The gloss of films in the invention is usually 8O to llO or l2O measured by ASTM D-2457 using a sheen gloss meter and an incidence angle of 6O°. When films are made from HB polymer compositions consisting essentially of lOO% HB polymer (for instance including up to about 2% impurities) it is observed that the films have good optical properties, having low haze (below lO%) and high gloss (above 95 or lOO). It would be expected that the inclusion of cellular debris and other impurities would dramatically decrease the optical properties of the films. We have surprisingly found that this is not the case and that instead, it is possible to form melt extruded films generally of below 5Oµm that have satisfactory optical properties from HB polymer compositions containing for instance 5 to 2O%, usually 5 to l5%, impurities remaining from the fermentation of the films. These impurities are generally cell debris. The haze is generally below 2O%, usually lO to 2O%, and the gloss can often be at least 88, e.g., 88 to 98. Thus good films can be made even though the polymer composition has not been subjected to the expensive purification steps that are required for making the purest polymer compositions. Ostomy bags at present are generally made from a laminate of polyvinylidene chloride (to give impermeability) with a surface layer of ethylene vinyl acetate (to give softness and heat sealability). Polyvinylidene chloride cannot satisfactorily be melt sealed. We have surprisingly found that the melt extruded HB composition films of the invention can be melt sealed and so it is not necessary to laminate them with a melt sealing surface layer, such as ethylene vinyl acetate. Thus an ostomy bag, diaper backsheet or other article can be made by laying the face of a melt extruded film of HB polymer composition against a surface and melt sealing it against the surface. The surface is generally the face of melt extruded film of HB polymer composition and thus an ostomy bag may be made by folding such a film upon itself and melt sealing it around the edges. Instead of folding one film upon itself, two separate films may be laid against each other, with the HB polymer composition layers facing each other. Other surfaces to which the film may be melt sealed include articles that are to be secured into the film, e.g., the fitting of an ostomy bag. The melt sealing may be by impulse heating or, preferably, RF welding. This comprises the application of a high frequency electromagnetic field between a pair of metallic jaws that clamp the layers that are to be welded. Parameters that influence the process performances are frequency, sealing time and pressure on the jaws. In the invention preferred frequencies are 27 to 7O MHz; preferred sealing times are O.5 to 5 seconds; preferred pressures are O.5 to lO bars. The invention is illustrated in the accompanying drawings, in which Figure l is a section through a diaper Figure 2 is a perspective view of an ostomy bag Figure 3 is a cross section through the bag, and Figure 4 is a similar cross section through a different bag. The diaper in Figure l comprises a backsheet l of a melt extruded film of HB polymer composition, a permeable, non-woven, top sheet 2 and an absorbent pad 3 of cellulosic or other suitable material. The backsheet l is melt sealed to the top sheet along each side, and across the ends, as shown at 4 and 5, and is melt sealed to the absorbent pad along three longitudinal strips, as shown at 6, 7 and 8. The ostomy bag in Figures 2 and 3 comprises a film 9 formed into a pouch and melt sealed around its facing edges 10 and melt sealed to an ostomy fitting 11. In Figure 4 the film 9 is laminated to an outer layer 12. In one embodiment of the invention this outer layer 12 may be a water-degradable non-woven fabric. In another embodiment it may be a reinforcing film and layers 9 and l2 may be reversed so that layer 12 is inside layer 9 and it may then comprise, for instance, a layer of polyvinylidene chloride film, for instance coated on the inner surface with EVA so as to promote adhesion of the facing surfaces of the layer 12. Instead of forming the bags shown in Figures 3 and 4 from a single sheet that is folded upon itself, they may be formed from two separate sheets that may be bonded to one another around their entire periphery. The following are some examples of the invention. Example 1 A composition of about 98% of a copolymer of 83% hydroxy butyrate and 17% hydroxy valerate is extruded with ethylene vinyl acetate copolymer containing about 3% vinyl acetate as described in U.S. 4,379,117, especially Figure 3. The extrusion dye had a diameter of about 100mm and provided, at the point of extrusion, a tubular laminate of 0.9mm EVA, 1.2mm HB polymer and 0.9 mm EVA. The extrusion temperature was about 10 to 20⁰C above the melting point of the composition. The tube was inflated to a diameter of about 400mm so as to stretch it laterally fourfold and was stretched longitudinally by adjusting the take-off speed at up to 40 metres per minute, the resultant film thickness being about 25µm. After ageing overnight the film was slit longitudinal and the EVA layers separated from the HB polymer composition layer. The resultant film was labelled A. The process was repeated using a similarly pure composition but based on a copolymer of 78% hydroxy butyrate and 22% hydroxy valerate. The resultant film was labelled B. The process was repeated but using a copolymer of 82% hydroxy butyrate and l8% hydroxy valerate in a composition containing about lO% cell debris. The film was labelled C. Various physical properties of films A, B and C were recorded. As comparisons, the corresponding properties were recorded of film D, biaxially oriented polypropylene about 2Oµm thick and of film E which is film D, perforated with holes about O.4mm diameter. The results are shown in the table below in which, for comparison, typical values for polyvinylidene chloride film, F, are shown. O₂ transmission is recorded in ml/25µm.m².day,bar at 23°C. MVT (moisture vapour transmission) is recorded in g/25µm.m².day at 38°C. Modulus and TS (tensile strength) are recorded in kg/cm². TPR (tear propogation resistance) is recorded in g/µm. The results demonstrate the excellent combination of oxygen and moisture vapour transmission properties of the films according to the invention (A, B and C) compared to the prior art films (D and F) and the prior art perforated film (E). The results also demonstrate the satisfactory haze and gloss values that are obtained despite the presence of substantial amounts of cell debris impurities (C). Films A, B and C are suitable for use as the backsheet l in the diaper of Figure l or the pouch 9 in the ostomy bags of Figures 2 to 4. Example 2 Films are produced by extrusion as in Example l of a composition of a blend of substantially pure HB polymer formed of 79 mole percent hydroxy butyric acid and 2l mole percent hydroxy valeric acid together with varying amounts of plasticiser. In Example 2a the plasticiser is N-ethyl-o,p-toluene sulphonamide (available from Monsanto under the trade name Santicizer 8) in an amount of 6O parts per lOO parts polymer. In Example 2b the plasticiser is a blend of lO parts per lOO parts polymer of this sulphonamide and lO parts per lOO parts polymer of a dialkyl diether glutarate of molecular weight about 45O available from C.P.Hall as Hall 7O5O. In Example 2a the film is extruded to a final thickness of about 4Oµm and in Example 2b it is extruded to a thickness of about 5Oµm. Example 3 The film of Example 2a is laminated with a l2µm biaxially oriented polyvinylidene chloride film using a conventional two-component polyurethane adhesive supplied for laminating films, in particular 5g/m² Adcote 7lO A & C supplied by Morton Thyocol. The resultant laminate is very flexible and soft and could be utilised as a diaper backsheet or an ostomy bag as illustrated or described with reference to any of the accompanying drawings. The laminated film has an oxygen permeability of 5Oml/.m².day.bar at 23°C. Example 4 The film of Example 2b is laminated, using the same adhesive and the same general technique as in Example 3, with the polyvinylidene chloride surface of a laminate of lOµm polyvinylidene chloride and 3Oµm ethylene vinyl acetate containing l8% vinyl acetate (the material from Dupont under the trade name Elvax 3l65), this laminate having been made by co-extrusion through a circular dye followed by hot blowing. The resultant laminate had an oxygen impermeability of l4cc/m².day.bar and could be used as the backsheet in Figure l or as the laminate in Figure 4, with the HB polymer film either on the inside or the outside of the bag. Example 5 The film of Example 2b is laminated by the same general technique and using the same adhesive as is in Example 3 with a 3Oµm film of polyethylene (containing 5% vinyl acetate). Example 6 The process of Example 4 can be repeated with different ethylene vinyl acetates having vinyl acetate contents ranging from 5 to 25% and mfi of O.5 to 7 and can also be repeated using a laminate in which there is an ethylene vinyl acetate layer on the side of the polyvinylidene chloride facing the layer of HB polymer. Example 7 Coextrusion is conducted using method and apparatus as described in U.S. 4,379,ll7, especially Figure 3, but modified to provide four films instead of three. The materials that are extruded are, in sequence, polyvinyl alcohol, polyethylene oxide, HB polymer composition consisting of about 98% of a copolymer of 83% hydroxy butyrate and l7% hydroxy valerate, and ethylene vinyl acetate containing about 3% vinyl acetate. The extrusion dye has a diameter of about lOOmm and provides, at the point of extrusion, a tubular laminate of O.6mm polyvinyl alcohol, O.3mm polyethylene oxide, l.2mm HB polymer and O.9mm EVA. The extrusion temperature is lO to 2O%C above the melting point of the highest melting component of the laminate, namely l4O°C. The tube is inflated to a width of about 4OOmm so as to stretch it laterally fourfold and is stretched longitudinally by adjusting the take-off speed at up to 4O metres per minute. The resultant laminate consists of films of polyvinyl alcohol l3µm thick, polyethylene oxide 6µm thick and HB polymer composition about 25µm thick. After ageing overnight the film is slit longitudinally and the EVA layer separated.

Claims: Sheet material comprising a film of HB polymer composition wherein the HB polymer is a biodegradable polymer formed of recurring units of which 5O to lOO% molar are units of formula l -OC n H 2n CO- where n is 3, 4 or 5 and the HB polymer composition comprises 5O to lOO% of the HB polymer and O to 5O% diluent additive, characterised in that the film is a film that has been made by melt extrusion to a thickness of 5 to 2OO µm. A material according to claim l in which the HB polymer is formed of recurring units of which 5O to lOO% molar have the formula la -OCH(C m H 2m+1 )CH₂CO- where m is selected from l, 2 and 3. and O to 5O% molar have the formula 2 -OCR¹R²(CR³R⁴) p CO- where p is zero or an integer and R¹, R², R³ and R⁴ may each be hydrogen, hydrocarbon, halo substituted hydrocarbon, hydroxy substituted hydrocarbon, hydroxyl or halogen, provided that the values of R¹, R², R³, R⁴ and p are not such that the unit of Formula 2 is a unit of Formula l. A material according to claim l in which the HB polymer is selected from beta hydroxy butyric acid homopolymers and copolymers with up to 5O%, preferably lO to 3O% beta hydroxy valeric acid. A material according to any preceding claim in which the diluent additive is selected from byproducts of the biosynthesis of the polymer, fillers, other polymers, plasticisers, stabilisers and impact additives. A material according to any preceding claim in which the film of HB polymer composition has a thickness of lO to lOO µm. A material according to any preceding claim in which the film of HB polymer composition has moisture vapour transmission of 30 to 200 g/25µm.m².day at 38°C. A material according to any preceding claim in which the film of HB polymer composition has an oxygen transmission value of 10 to 200 ml/25µm.m².day.bar at 23°C. A material according to any preceding claim in which the film of HB polymer composition has a thickness of 20 to 80 µm, a moisture vapour transmission of 40 to 150 g/25µm.m².day at 38°C and an oxygen tranmission of 80 to 200 ml/25µm.m². day.bar at 23°C. A material according to any preceding claim in which the film has a haze value, measured by ASTM-D 1003. below 20% and a gloss value measured by ASTM-D 2457 of at least 88. A material according to any preceding claim in which the HB polymer composition includes 5 to 20% by weight byproduct impurities including cell debris and has a haze of l0 to 20% measured by ASTM-D 1003. A material according to any preceding claim in which the HB polymer composition includes 5 to 40% by weight plasticiser. A material according to any preceding claim in which the film of HB polymer composition is permanently laminated with a sheet material selected from non-woven fabrics, water soluble films and water insoluble films. A material according to claim 12 in which the HB polymer composition includes 5 to 40% plasticiser, the film of HB polymer composition is from 10 to 100 µm thick, and the film is laminated to a water insoluble film selected from polyethylene, ethylene vinyl acetate copolymers, polyvinylidene chloride, and laminates comprising polyvinylidene chloride. A material according to claim l2 comprising a laminate of the film of HB polymer composition with a film of polyvinyl alcohol. A material according to claim l2 comprising a laminate of the film of HB polymer composition with a water-degradable non-woven fabric. A material according to any preceding claim comprising the said film of HB polymer composition melt sealed, without any intervening bonding layer, to a surface, preferably of a melt extruded film of HB polymer composition. A material according to claim l6 in the form of a diaper or ostomy bag. A material according to any of claims l3 to l5 in the form of an ostomy bag or diaper backsheet. A method of making a sheet material according to claim l comprising melt extruding a laminated tube of a tubular layer of the said HB polymer composition in molten form and a tubular layer of molten thermoplastic that is substantially non-tacky on solidification, and stretching and solidifying the extruded laminate. A method according to claim l9 in which the laminated tube comprises a laminate of the tubular layer of molten HB polymer composition between tubular layers of molten thermoplastic wherein each thermoplastic layer is substantially non-tacky on solidification. A method according to claim l9 in which the film is stretched by inflation of the tubular laminate and the laminate is then flattened and slit. A method according to claim l9 in which the film of HB polymer composition is allowed to crystallise after the laminate is solidified and the thermoplastic layer or layers, or one of them, is then stripped from the said film.

Inventors: MARTINI, FRANCESCO, PERAZZO, LUIGI, VIETTO, PAOLO
Applicants: W.R. GRACE & CO.-CONN. (A CONNECTICUT CORP.)
Application year: 1986
Main classification: C08J5
IPC codes: A61F13, A61L28, B32B27, C08G63, A61L26, A61L15, C08J5, A61L31