SELECTIVE CATALYTIC DEALKYLATION OF 1,4-DIALKYLBENZENES

Abstract: An alumino silicate zeolite "ZSM" type catalyst is mixed with a solution of a metal or metalloid compound e.g. magnesium acetate, the solution is concentrated and the mixture is dried and calcined to form a modified zeolite, e.g. with added MgO. Before or after this modification, the zeolite is treated by ion-exchange with a solution of Na⁺, K⁺, Rb⁺ or Cs⁺, e.g. as a chloride, nitrate, bicarbonate, carbonate, phosphate, acetate or hydroxide, followed by filtration and washing, to give 0.5 - 1.0 atomic ratio of the ion per Al in the catalyst. The catalyst is used to dealkylate secondary and/or tertiary C3-12 alkyl groups in a 1,4-dialkylbenzene mixture, e.g. cymene, at 250° to 600°C, with high select­ ivity and good purity and yield of the recovered olefins.

Description: The present invention relates to a method for selectively dealkylating a dialkylbenzene at the para- position thereof. More particularly, the present invention is intended, by dealkylating a 1,4-­ dialkylbenzene in a dialkylbenzene mixture by a shape-­ selective reaction using a specified zeolite catalyst, to remove the 1,4-dialkylbenzene from the mixture or reduce the 1,4-dialkylbenzene concentration of the mixture, whereby the side reactions (e.g., oligomerization, cracking, etc.) of an olefin produced by the dealkylation are suppressed, and the percent recovery and purity of the eliminated olefin are kept at a high level to facilitate the reuse of the olefin and improve the economy of the dealkylation. Generally, dialkylbenzenes obtained by the dealkylation of benzenes are a mixture of 1,2-, 1,3-, and 1,4-isomers, but a difference in boiling point between these isomers is so small that, in many cases, even rectifying columns having many plates are insufficient to separate these isomers from one another by distillation. A specific example is as follows. Cymene isomers obtained by the alkylation of toluene with propylene have the following boiling points: o-isomer, 178.3°C; m-isomer, 175.1°C; and p-isomer, 177.1°C. The difference in boiling point between m- and p-cymenes which is especially rel­ evant in the cresol manufacturing process, is only 2°C, so that separation by rectification is extremely difficult. In the cresol manufacturing process now in use, therefore, the following procedure is employed: the mixed cymene, without being separated into the isomers, is oxidized as such into a mixed cresol, and thereafter separation of the cresol isomers is carried out. Methods now in use to separate the cresol isomers from one another are: (A) The cresol mixture is alkylated with isobutylene into a mixture of tert-butyl cresol isomers, the isomers are separated from one another by rectification utilizing a large difference in boiling point between them, and then the tertiary butyl group is removed to obtain high-purity m- and p-cresols. (B) A mixture of cresol urea isomeric clathrate compounds is separated into the isomers by recrystallization util­ ising a difference in crystallizability between them, and the separated compounds are decomposed to obtain high-­ purity m- and p-cresols. However, both foregoing methods are so comp­ licated that a further improvement is desired. Another specific example will be given below. Diisopropylbenzene obtained by the alkylation of benzene, which is a starting material for 1,3-dihydroxybenzene (resorcinol) and 1,4-dihydroxybenzene (hydroquinone), comprises the isomers having the following boiling points: o-isomer, 200°C; m-isomer, 203°C; and p-isomer, 210.3°C. The difference in boiling point between m- and p-diiso­ propylbenzenes, which is of special relevance in the resorcinol and hydroquinone manufacturing process, is 7°C, so that separation of both by rectification is possible. This method, however, requires rectifying columns having a fairly large number of plates so that it is not always a method of high efficiency. An alternative recently proposed separation method is intended to selectively dealkylate only the 1,4-dialkyl isomer in the dialkylbenzene, to thereby re­ cover the 1,3-dialkyl isomer (in some cases, 1,2-plus 1,3-dialkyl isomers) as unreacted (Japanese Patent Applications (OPI) Nos. 83716/1980 and 83721/1890 and U.S. Patents Nos 4181811 and 4205189). (The term "OPI" refers to a published unexamined Japanese patent applic­ ation). This method uses a "ZSM type" zeolite as a catalyst, and particularly, a ZSM type zeolite catalyst modified with oxides such as MgO or P₂O₅ and dealkylates only the 1,4-dialkyl isomer with a very high selectivity, so that this method is a notable improvement. From the practical point of view, however, this method also has a large defect that, when the alkyl group to be dealkylated has three or more carbon atoms, olefins obtained by the dealkylation are low in purity and percent recovery. For example, Example 10 of Japanese Patent Application (OPI) No. 83716/1980 discloses that m-cymene is obtained in a high purity (96.6%) by dealkyl­ ating a mixed cymene (o/m/p=2.16/66.16/31.67) using a steam-treated H-ZSM-5, but the purity of propylene re­ covered at that time is about 60% in the volatile gas obtained. Similarly, Example 11 of Japanese Patent App­ lication (OPI) No. 83721/1980 discloses that a high-purity m-cymene is obtained by dealkylating a mixed cymene using a similar catalyst, but the purity of propylene recovered at that time is 43%. When these known methods were verified by the present inventors, many kinds of C₂-C₆ olefins and paraffins were found in the recovered propylene, in addition to propylene, and so it was supposed that the eliminated ispropyl group was subjected to complicated side reactions such as oligomerization, cracking or hydrogenation. Further, from the total carbon content of the C₂-C₆ volatile gases which was lower than that calculated from the eliminated isopropyl groups, it was supposed that some parts of the latter were changed to heavy components having more than six carbon atoms. Thus, these known methods had the disadvantages that the percentage recovery of the recovered olefins was very low and that the purity of the recovered olefins was low and, acordingly, separate olefin-purification equipment was required. On the other hand, Japanese Patent Application (OPI) No.103119/1981 (U.S. Patent 4,251,676) discloses that when the reaction is carried out in the presence of an H-ZSM-5 catalyst while feeding a mixture of cymene together with aniline or ammonia, the dealkylation pro­ ceeds with a high para-selectivity, whereby propylene is recovered in a purity as high as 94%. However, this method also had the following defects: in industrial practice, while the recovered toluene and propylene are recycled into the alkylation region, it is necessary to separate out the aniline or ammonia from the recovered toluene and propylene since the alkylating catalyst would be deactivated by a base such as the entraining aniline or ammonia, if any. Thus, this process is not economical. Our Japanese Patent Application (OPI) No. 216835/1984 and U.S. Patent 4,449,321 disclose using a crystalline zeolite catalyst ion-exchanged with lithium ions as an improved method for selective para-dealkylation of dialkylbenzenes, whereby olefins can be obtained in high yield and purity. However, since the higher the degree of ion-exchange, the better the result, the prep­ aration of the catalyst is not easy. On ion-exchanging a crystalline zeolite with lithium ions, it was not easy to enhance the degree of ion-exchange, probably because the lithium ions were hydrated and their ionic radius was increased, and a special treatment such as a treatment at high temperatures was therefore required. Thus, the method using such catalyst was not necessarily satis­ factory on an industrial scale. Our European Application EPA 85307490.4 de­ scribes the use of a crystalline zeolite of the aforesaid ZSM type, prepared by mixing aqueous solutions of an alkali metal cation and an organic cation, calcining e.g. at 350° to 600°C for several hours, and modifying by mixing with a metal or metalloid compound. We have now found a further method wherein a specified amount of alkali metal ion (other than lithium) is used to treat such zeolite by ion-exchange, but without the need for high temperature during this ion-exchange so that preparation of the catalyst is easy. The present invention provides an industrially excellent method for selectively dealkylating a 1,4-­ dialkylbenzene in a dialkylbenzene mixture by use of, as the catalyst, a crystalline zeolite having a silica/­ alumina molar ratio of at least 12:1 and a constrained index of 1 to 12, modified with a metal or metalloid oxide, wherein the crystalline zeolite was ion-exchanged with a treatment liquor containing an alkaline ion selected from sodium ion, potassium ion, rubidium ion and cesium ion and contains said ion in an atomic ratio of 0.5:1 to 1.0:1 with respect to the aluminum. In the present invention, the dialkylbenzene to which the present invention can apply particularly advantageously is a compound containing a secondary and/or tertiary alkyl group having 3 to 12 carbon atoms. Specific examples of the 1,4-dialkylbenzene include, for example, 1-isopropyl-4-methylbenzene, 1,4-­ diisopropylbenzene, 1-sec-butyl-4-methylbenzene, 1-tert-­ butyl-4-methylbenzene, and the like. The effect of the present invention consists in not only that the 1,4-dialkylbenzene alone contained in the dialkylbenzene mixture can selectively be dealkylated and the formed olefin (e.g., propylene for 1-isopropyl-4-methylbenzene or isobutylene for 1-tert-butyl-4-methylbenzene) can be recovered in a high yield and a high purity, but also that the catalyst can be prepared very easily. Consequently, by incorporating the method of the present invention after the usual alkylation step, the m-­ dialkyl isomer (or m- and o-dialkyl isomers) can be obtained easily in a high purity, and the benzenes and olefins produced by dealkylation can be recycled as such to the alkylation step, while the catalyst can be prepared easily. This method, therefore, is very advantageous. Next, the method of the present invention will be illustrated specifically. The crystalline zeolite catalyst used in the present invention (hereinafter referred to as zeolite catalyst) is a zeolite having characteristics that the silica/alumina molar ratio is 12/1 or more and besides the constrained index (described later) is 1 to 12, and its typical example is those (pentacyl type zeolites) which were developed by Mobil Oil Co. or Union Carbide Corporation and are generally called "ZSM type zeolite" or "Silicalite". The characteristic of ZSM type zeolites is that they have a high silica/alumina molar ratio, and this molar ratio can be measured by the common analytical methods such as atomic absorption method. The constrained index is defined by the following equation: This index shows the degree to which the channel of the zeolite crystal controls the access to itself of molecules having a section larger than that of n-paraffin. The specific measurement method is described in Japanese Patent Application (OPI) No. 133223/1981. The value of this constrained index approaches the ratio of cracking rates of the both hydrocarbons. A preferred zeolite used in the present invention is one having a constrained index of 1 to 12. The constrained index of some typical zeolites is shown below: The value of the constrained index is the important critical definition of a useful zeolite in the present invention. Since, however, some latitude is allowed in the measurement method described above, the value sometimes varies with the measurement condition. Consequently, the value of the constrained index is a mean value of those obtained under some different measurement conditions. Thus the crystalline zeolite used according to the method of the present invention has been defined by the two values of silica/alumina molar ratio and constrained index. The above-mentioned ZSM type zeolites developed by Mobil Oil Co., such as ZSM-5, ZSM-11, ZSM-­ 12, ZSM-23, ZSM-35, ZSM-38 and ZSM-48, are specific examples of the crystalline zeolite. The preparation method and the X-ray diffraction pattern of these ZSM type zeolites are described in the above-listed references, respectively. Next, the ion-exchanging treatment with a base ion, which constitutes the most important point of the present invention, is explained. H⁺-ZSM type zeolites show various acid strength distributions and acid amounts (the number of acid points) in accordance with their Si/Al ratios. As the result of minute investigations made by the present inventors, however, as the acid strength of the H⁺-ZSM type zeolite used for dealkylation is high and the acid amount is large, side reactions of the olefins produced by the dealkylation occur more likely and the purity and yield of the olefins lower. Therefore, it is necessary to adjust the acid strength and/or the acid amount, in order to recover olefins having a high purity in a high yield. The present inventors have found that zeolite catalysts ion-exchanged with a specified amount of a specified base ion are effective for this purpose and in addition, such zeolite catalysts can be prepared very easily. Examples of the base ion used in the present invention include sodium ion, potassium ion, rubidium ion, and cesium ion, and its content in the zeolite catalyst is 0.5/1 to 1.0/1, preferably 0.7/1 to 1.0/1 in terms of atomic ratio with respect to aluminum in the zeolite skeleton. When the atomic ratio is higher than 1.0/1, the dealkylating activity of the catalyst is lowered, whereas when the atomic ratio is lower than 0.5/1, the purity and yield of the recovered olefins are much reduced. The ion-exchanging treatment can be carried out by a usual method. That is, the ion-exchanging is effected easily even at room temperature by bringing a calcined ZSM type zeolite into contact with an aqueous solution of the above-mentioned base, followed by filtration and washing steps whereby the ion-exchanged zeolite described above can be obtained. As the source of the base ion, an alkaline compound in the form of a chloride, nitrate, bicarbonate, carbonate, phosphate, acetate, hydroxide, or the like, can be used alone or in admixture. Although it is particularly preferred to use a hydroxide in combination with salt, an excessively high pH region where the zeolite crystal might be dissolved must be avoided. After the ion-exchanging operation, washing with distilled water is carried out sufficiently to remove any matter adhering or remaining on the surface of zeolite. The degree of ion-exchanging with base ions can be measured by a chemical elemental analysis such as the atomic absorption method. Next, the modification method for the ZSM type zeolite with a metal or metalloid oxide, which is a means used in the method of the present invention in combination with the ion-exchanging treatment with base ions, is explained. In this modification method, a ZSM type zeolite is dipped in a solution containing a metal or metalloid compound, and the solution is concentrated (in some cases, a filtration process is included). Thereafter, the zeolite on which the metal or metalloid compound is supported is calcined at a temperature of 400 to 600°C in a stream of air, whereby the ZSM type zeolite is modified with the metal or metalloid in the form of oxide. It is supposed that, by the two effects of such modification method, i.e., poisoning of the acid sites of the surface outside the channels of the ZSM type zeolite and some narrowing of the entrances of the channels, only the acid sites in the channels of the resulting ZSM type zeolite act effectively, and the so-called para-­ selectivity appears (in other words, only a p-isomer among the dialkylbenzenes is dealkylated selectively). The modification treatment may be carried out either before or after the above-mentioned ion-exchanging treatment with a base ion (M⁺). When the modification treatment is carried out after the ion-exchanging treatment with a base ion, however, it is necessary to perform the modification treatment quickly such that any re-exchanging of M⁺ ion does not occur. In the modification method specifically disclosed by the examples described below, the following procedure is employed: M⁺-ZSM-5 is dipped in an aqueous magnesium acetate solution, and after concentrating the solution, the solution is calcined for 3 hours at 500°C in a stream of air, whereby M⁺-ZSM-5 modified with MgO is obtained. Such procedure is one of many combinations of the processes. The methods which are used in the present invention for the modification with a metal or metalloid oxide are known. For example, the method of the present inventors (Japanese Patent Application No. 44241/1982), the methods of Mobil Oil Co. (Japanese Patent Applications (OPI) Nos. 133030/1981, 133031/1981, 133032/1981 133223/1981, 144750/1981, 145227/1981, 10337/1982, etc.), and others are known. The method of the present invention is characterised by using the known modification method in combination with the above-mentioned ion-exchanging treatment with a base ion, optionally preceded by an ammonium ion-exchange treatment. The metal or metalloid compound for modifying the ZSM type zeolite is a compound of at least one element selected from the lanthanum elements (e.g., La, Ce, and Nd), the group IIa elements (Ba, Mg, and Sr.), the group IIb elements (e.g., Zn and Cd), the group IIIa elements (e.g., Ga and In), the group IVa elements (e.g., Ge, Sn, and Pb), the group Va elements (e.g., P), the group IVa elements (e.g., Te), the group VIb elements (e.g., Cr, Mo, and W), and the group VIIb elements (e.g., Mn and Re). This metal compound or metalloid compound is mixed with the ZSM type zeolite in the form of a solution, and through the steps of concentration and calcination, it finally modifies the ZSM type catalyst in the form of, substantially, a metal oxide or metalloid oxide. Examples of a suitable solvent used in this case include, for example, water, aromatic or aliphatic hydrocarbons, alcohols, organic acids (e.g., formic acid, acetic acid, and propionic acid), and inorganic acids (e.g., hydrochloric acid, nitric acid, and sulfuric acid). Alternatively, halogenated hydrocarbons, ketones, ethers, etc. also are useful. Of these solvents, water is used most commonly. The ZSM type zeolite is dipped in this solution, and after concentration, it is dried, but in some cases, it is filtered after dipping and then dried. Drying is carried out at a temperature of generally 80°C to 150°C. Calcination after drying is carried out at a temperature of 300°C or higher, preferably 400° to 550°C for several hours in an air stream. The amount of the metal or metalloid oxide modifying the ZSM type zeolite after calcination is selected to be from 1 to 50 wt%. The dealkylation reaction of dialkylbenzenes is carried out by bringing the dialkylbenzene mixture into contact with the ZSM type zeolite catalyst modified with the above-mentioned metal or metalloid oxide. The catalytic system of the present invention may be used alone but it is usually in practice used after admixing with a binder and press molding. The dealkylation is mainly carried out by the gas-phase catalytic reaction. In this reaction, inert gases such as nitrogen, helium or argon may be used as a diluent. The use of the diluent is employed, in some cases, for the purpose of positively aiming to control the occurrence of side reactions by dilution of the substrate, to thereby keep the purity of the recovered olefin high. The reaction temperature cannot be determined simply because it is affected by the kind of alkyl groups to be dealkylated, but generally it is selected from a range of from 250° to 600°C. The alkyl group which is dealkylated in the present invention is a secondary and/or tertiary alkyl group having 3 to 12 carbon atoms. Generally, however, the progress of the dealkylation becomes easy with an increase in the number of carbon atoms of the alkyl group, or it is easier in tertiary alkyl groups than in secondary ones. The reaction temperature, therefore, shifts to a low temperature side. One characteristic of the present catalytic system is that, even if the dealkylation is carried out at high temperatures in order to raise the dealkylation rate, the selectivity to the dealkylation of the 1,4-isomer is kept high (in other words, both the 1,2- and 1,3-isomers are left completely or nearly unreacted) and besides both the purity and percent recovery of the recovered olefin are also kept high. The contact time is selected from a range of from 0.1 to 60 seconds, preferably from 1 to 30 seconds. Another characteristic of the present catalytic system is that, even if the dealkylation is carried out for a long contact time in order to raise the dealkylation rate, the selectivity to the dealkylation of the 1,4-­ isomer as well as the percent recovery and purity of the recovered olefin are kept high. A further characteristic of the present catalytic system is that the catalytic system has a long life, and there is little reduction in the catalytic activity due to deposition of carbonaceous substances even in a pro­ longed reaction. The dealkylation of the present invention is carried out using a fixed-bed or fluidized-bed catalytic system according to a batchwise, semi-continuous, or continuous process. In either case, for the regeneration of the catalyst, carbonaceous substances on the catalyst are burned out at a temperature of about 500°C to 550°C using an inert gas containing a little oxygen (0.5 to 2.0%). The present invention will be illustrated in more detail with reference to the following specific examples. The reaction results in the examples were cal­ culated by means of the following equations. ZEOLITE PREPARATION EXAMPLE 1 Synthesis of ZSM-5: Starting solutions each having the following formulation were first prepared. Solution A Water 162 g H₂SO₄ 16.7 g Al₂(SO₄)₃·17H₂O 1.46 g (n-C₃H₇)₄NBr 20.3 g Solution B Water 119.7 g Sodium silicate Grade No.3 186.3 g Solution C Water 281.7 g NaCl 70.9 g The solutions A and B were dropped to the solution C at the same time and then mixed. At this time, the mixture was vigorously stirred while maintaining the pH at 9 to 11 (for this pH adjustment, 6.0 g of a 48% aqueous NaOH solution was added). The pH when the mixing was completed was 9.55. The mixture was placed in a 1-­ liter SUS autoclave and then was subjected to a hydrothermal reaction while stirring at 160°C for 20 hours (at 350 to 400 rpm). After being cooled, the reaction mixture was filtered and thoroughly washed with a large amount (up to 7 liters) of distilled water. In this manner, the washing/filtration cycle was repeated. The reaction product was dried at 120°C for 15 hours and then calcined at 530°C for 3 hours in an air stream to yield 47.5 g of white powdery crystals (yield=84.6%). The X-ray diffraction analysis confirmed that the product was ZSM-5. The degree of crystallinity was 93.2%. The fluorescent X-ray analysis showed that the SiO₂/Al₂O₃ molar ratio was 64.0/1. Next, the Na/H type ZSM-5 thus obtained was ion-exchanged three times with each 200 g of a 5% aqueous ammonium chloride solution at 65°C for 2 hours, and then further ion-exchanged with 200 g of a 5% aqueous ammonium chloride solution at 25°C for one night. After the filtration, the residue was washed five times in total with 200 g of distilled water and then dried at 120°C for 10 hours to give 38 g of NH type ZSM-5. ZEOLITE PREPARATION EXAMPLES 2 TO 3 Synthesis of ZSM-5: The amount of aluminum sulfate in Referential Example 1 was changed to prepare ZSM-5s having various SiO₂/Al₂O₃ molar ratios. During the mixing of the solutions A, B, and C, the pH was maintained at 9 to 11, and the pH after completion of the mixing was adjusted to 9 to 10. For this pH adjustment, caustic soda was used. The results obtained are shown in Table 1. Next, each of the Na/H type ZSM-5s thus obtained was ion-exchanged according to the process as described in the latter half of Referential Example 1 to change it NH type ZSM-5. CATALYST PREPARATION EXAMPLE 1 Ion-exchanging with Na ion and modifying with MgO: Ion-exchanging treatment was carried out by dispersing 4.0 g of the NH type ZSM-5 having an SiO₂/Al₂O₃ molar ratio of 64.0/1 as obtained in Zeolite Preparation Example in 140 ml of an ion-exchanging liquor consisting of 2 parts of an aqueous 0.1 mole/liter NaCl solution and 1 part of an aqueous 0.1N NaOH solution (Na ion amount in the ion-exchanging liquor per Al atom in ZSM-5 (Na/Al)=6.8/1) and stirring the dispersion at room temperature for 1 hour. After the filtration, the residue was well washed with distilled water and then dried at 120°C for 2 hours to give Na⁺-ZSM-5. The Na/Al ratio of the catalyst was 0.95/1. Next, 28 ml of an aqueous 8 wt% magnesium acetate solution was added to 2.5 g of the Na⁺-ZSM-5 thus obtained, and then stirred. The dispersion was concentrated at 80°C under reduced pressure to dryness. Subsequently, the residue was dried at 120°C for 10 hours and calcined at 530°C in an air stream for 3 hours to give 3.1 g of MgO-Na⁺-ZSM-5 (amount of modifying MgO=20 wt%). EXAMPLE 1 Catalytic activity test by fixed-bed flow reaction: Dealkylation of cymene using an ordinary atmospheric pressure fixed-bed flow reactor was carried out as follows: In a quartz glass tubular reactor having a length of 32 cm and an inside diameter of 1 cm was charged 1 g of the 20 wt% MgO-Na⁺-ZSM-5 catalyst prepared in Catalyst Preparation Example 1 (the catalyst was crushed after pressure molding, and arranged to have a particle diameter of 24 to 48 mesh), and the catalyst was preheated at 400°C for 1 hour in a nitrogen stream. Then, cymene (m/p/o=63.6/32.9/3.5) was fed to the reactor at a WHSV (weight hourly space velocity) of 2.7 hr⁻¹ and reacted. The temperature of the catalyst bed (the reaction temperature) was varied stepwise from 350°C to 450°C. The reaction product was collected by trapping by ice-cooling, and the aromatic component was analyzed by gas chromatography. The volatile gas component was analyzed by introducing the mixed reaction gas directly into a gas chromatographic column. The results obtained are shown in Table 2. CATALYST PREPARATION EXAMPLE 2 With each of the two NH-ZSM-5s obtained in Zeolite Preparation Examples 1 and 2 having different SiO₂/Al₂O₃ molar ratios, the ion-exchanging treatment with Na ion was effected according to the manner as described in Catalyst Preparation Example 1. At that time, the treatment was carried out by suitably varying the amount of the ion-­ exchanging liquor. After the filtration and washing, Na⁺-ZSM-5 was obtained. Next, with each of the Na⁺-ZSM-5s, the treatment for modifying with 20 wt% MgO was effected according to the manner as described in Catalyst Preparation Example 1. The catalysts thus obtained are shown in Table 2. EXAMPLE 2 Dealkylation of cymene was carried out according to the manner as described in Example 1, using each of the catalysts Nos. 2, 3, and 6 obtained in Catalyst Preparation Example 2. The results obtained are shown in Table 3. COMPARATIVE EXAMPLES 1 AND 2 Dealkylation of cymene was carried out according to the manner as described in Example 1, using each of the Catalyst Nos. 4 and 5 obtained in Catalyst Preparation Example 2. The results obtained are shown in Table 3. CATALYST PREPARATION EXAMPLE 3 Using 3.0 g each of the NH-ZSM-5s obtained in Referential Example 3 having an SiO₂/Al₂O₃ molar ratio of 254/1, the following treatments were carried out: (1) Ion-exchanging treatment was carried out by dispersing 3.0 g of NH-ZSM-5 into a mixed aqueous solution (90 ml) consisting of 60 ml of an aqueous 0.015 mole/liter NaCl solution and 30 ml of an aqueous 0.015 mole/liter NaOH solution and stirring the dispersion at room temperature for 1 hour. After the filtration, washing and drying, Na⁺-ZSM-5 was obtained. Next, the treatment for modifying MgO was effected according to the manner as described in Catalyst Preparation Example 1 to give 20 wt% MgO-supported type Na⁺-ZSM-5. (2) Ion-exchanging treatments with K ion, Rb ion, and Cs ion were effected according to the above treatment (1), using a mixed aqueous solution of KCl/KOH, a mixed aqueous solution of RbCl/RbOH, and a mixed aqueous solution of CsCl/CsOH, respectively. Subsequent treatment for modifying with MgO gave the following 20 wt% MgO-modified catalysts. (3) The NH-ZSM-5 was converted into H⁺-ZSM-5 by subjecting to calcination in an air stream at 530°C for 3 hours without effecting any ion-exchanging treatment. Through the treatment for supporting MgO as described in the latter half of Catalyst Preparation Example 1, the following 20 wt% MgO-modified H⁺-ZSM-5 catalyst was obtained. EXAMPLE 3 Using each of the Catalyst Nos. 7, 8, and 9 obtained in Catalyst Preparation Example 3, dealkylation of cymene was carried out according to the manner as described in Example 1. The reaction temperature employed was 350°C. The results obtained are shown in Table 5. COMPARATIVE EXAMPLE 3 Using the Catalyst No. 11 obtained in Catalyst Preparation Example 3, dealkylation of cymene was carried out in the same manner as described in Example 3. The results obtained are shown in Table 5.

Claims: 1. A method for selectively dealkylating a 1,4-­ dialkylbenzene in a dialkylbenzene mixture in the presence of, as a catalyst, a crystalline zeolite having an SiO₂:AlO₃ molar ratio of at least 12:1 and a constrained index of 1 to 12, modified with a metal or metalloid oxide, characterised in that the crystalline zeolite was ion-­ exchanged with a treatment liquor containing sodium ion, potassium ion, rubidium ion or cesium ion and containing said ion in an atomic ratio of 0.5:1 to 1.0:1 with respect to the aluminum. 2. A method as claimed in Claim 1, wherein said ion is present in the catalyst in an atomic ratio of 0.7:1 to 1.0:1 with respect to aluminum. 3. A method as claimed in Claim 1 or 2, wherein at least one alkyl group of the 1,4-dialkylbenzene is a secondary or tertiary alkyl group having 3 to 12 carbon atoms. 4. A method as claimed in Claim 4, wherein the 1,4-dialkylbenzene is 1-isopropyl-4-methylbenzene, 1,4-­ diisopropylbenzene, 1-sec-butyl-4-methylbenzene or 1-tert-­ butyl-4-methylbenzene. 5. A method as claimed in any of Claims 1 to 4, wherein the crystalline zeolite is ZSM-5, ZSM-11, ZSM-12, ZSM-23, ZSM-35, ZSM-38 or ZSM-48. 6. A method as claimed in any of Claims 1 to 5, wherein the metal or metalloid oxide modifying the crysta­ lline zeolite is an oxide of at least one element selected from La, Ce and Nd of the lanthanum group; Ba, Mg and Sr of the Group IIa of the Periodic Table; Zn and Cd of the Group IIb; Ga and In of the Group IIIa; Ge, Sn and Pb of the group IVa; P of the Group Va; Te of the Group VIa; Cr, Mo and W of the Group VIb; and Mn and Re of the Group VIIb. 7. A method is claimed in Claims 5 and 6, wherein the crystalline zeolite is ZSM-5, and the metal oxide modifying it is magnesium oxide. 8. A method as claimed in any preceding claim, wherein the treatment liquor contains the chloride, nitrate, bicarbonate, carbonate, phosphate, acetate or hydroxide of said ion. 9. A method as claimed in any preceding claim, wherein the zeolite was also ion-exchanged with an ammonium ion solution before the alkali metal ion exchange.

Inventors: HIROSE, KENICHI, ISHII, NORIO, SATO, HIROSHI
Applicants: SUMITOMO CHEMICAL COMPANY, LIMITED
Application year: 1986
Main classification: C07C4
IPC codes: B01J29, C07C4