SOIL RELEASE COMPOSITION AND USE THEREOF

Abstract: A soil release composition comprising: (A) a polymer comprising 10 to 100% by weight of constitut­ ing units of the formula: wherein R f is a C₃-C₂₁ fluoroalkyl group; R¹ is a hydrogen atom or a C₂-C₄ acyl group; R², R³, R⁴ and R⁵ are, the same or different, each a hydrogen atom, a methyl group or an ethyl group; A is a group of the formula: -CH₂CH(OR¹)CH₂-OCO- in which R¹ is the same as defined in the above, -CO-, -(CH₂) k N(R²)CO- in which R² is the same as defined in the above and k is an integer of 1 to 10, or -(CH₂) k - in which k is the same ad defined in the above; h is an integer of 0 to 5; p is an integer of 1 to 40; q and r are, the same or different, each an integer of 0 to 40, (B) a hydrophlic resin, and (C) optionally a water- and oil-repellent, a weight ratio of (A) : (B) : (C) being 5-95 ; 95-5 : 0 or 1-95 : 5-95 : 1-50, which can impart stainproofing property with good durability and a method for imparting soil release property to a substrate such as plastics, fabrics and paper.

Description: FIELD OF THE INVENTION The present invention relates to a soil release composition and a method for imparting a soil release property to a substrate. BACKGROUND OF THE INVENTION Plastics, fabrics, paper and the like are often treated with a soil release composition to increase their values including durability of a substrate. Conventional soil release compositions contain silicone, hydrocarbon polymer or fluorocarbon polymer (cf. Japanese Patent Publication No. 18346/1978 and Japanese Patent Kokai Publication (unexamined) Nos. 134786/1978, 163269/1980, 129281/1981, 164181/1982, 171762/ 1982 and 171790/1982). The conventional soil release composition containing silicone or the hydrocarbon polymer, however, imparts only a water absorption property and a soil release property to the substrate or alternatively only a water repellent property to the substrate. The conventional soil release composition containing the fluorine polymer only imparts a water- and oil-repellent property or an undurable soil release property to the substrate. SUMMARY OF THE INVENTION One object of the present invention is to provide a soil release composition which can impart a durable water absorption property and oil-repellency as well as the soil release property to a substrate. Another object of the present invention is to provide a soil release composition which can impart durable water- and oil-repellency as well as the soil release property to a substrate. Further object of the present invention is to provide a method for imparting a soil release property to a substrate with the soil release composition. These and other objects are accomplished by a soil release composition according to the present invention which comprises: (A) a polymer comprising 10 to 100 % by weight of constituting units of the formula: wherein R f is a C₃-C₂₁ fluoroalkyl group; R¹ is a hydrogen atom or a C₂-C₄ acyl group; R², R³, R⁴ and R⁵ are, the same or different, each a hydrogen atom, a methyl group or an ethyl group; A is a group of the formula: -CH₂CH(OR¹)CH₂-OCO- in which R¹ is the same as defined in the above, -CO-, -(CH₂) k N(R²)CO- in which R² is the same as defined in the above and k is an integer of 1 to 10, or -(CH₂) k - in which k is the same as defined in the above; h is an integer of 1 to 5; p is an integer of 1 to 40; q and r are, the same or different, each an integer of 0 to 40, (B) a hydrophilic resin, and (C) optionally a water- and oil-repellent, in a weight ratio of (A) : (B) : (C) of 5-95 : 95-5 : 0 or 1-95 : 5-95 : 1-50. In the case where the soil release composition of the present invention comprises the polymer (A) and the hydrophilic resin (B) but not the water- and oil-repellent (C), it can impart the water absorption property and oil repellency as well as the soil release property to the substrate. In the case where the soil release composition of the present invention comprises the polymer (A), the hydrophilic resin (B) and the water- and oil-repellent (C), it can impart water- and oil-repellency as well as the soil release property to the substrate. DETAILED DESCRIPTION OF THE INVENTION The polymer (A) comprising the constituting unit (I) may be prepared by homopolymerizing an unsaturated monomeric compound of the formula: R f -(CH₂) h CH(OR¹)CH₂-O-(CHR²CH₂O) p -(CHR³CH₂O) q - (CHR⁴CH₂O) r -A-CR⁵=CH₂ (II) wherein R f , R¹ to R⁵, A, h, p, q and r are the same as defined in the above, or copolymerizing the monomer (II) with at least one of other ethylenically unsaturated monomers. The fluoroalkyl group R f in the formulas may be a straight or branched one, and preferably the number of the fluorine atoms in the group is larger than that of the carbon atoms, more preferable the former is twice larger than the latter. The carbon chain in R f may have at least one oxygen atom between the carbon atoms. Specific examples of the monomer (I) are C₅F₁₁CH₂CH(OH)CH₂O(CH₂CH₂O)₄COCH=CH₂, C₇F₁₅CH₂CH(OH)CH₂O(CH₂CH₂O)₈COC(CH₃)=CH₂, C₈F₁₇CH₂CH(OH)CH₂O(CH₂CH₂O)₅CH₂NHCOCH=CH₂, C₈F₁₇CH₂CH(OH)CH₂O(CH₂CH₂O)₈COC(CH₃)=CH₂, C₈F₁₇CH₂CH(OCOCH₃)CH₂O(CH₂CH₂O)₉COCH=CH₂, C₉HF₁₈CH₂CH(OH)CH₂O(CH₂CH₂O)₁₀COC(CH₃)=CH₂, C₉F₁₉CH₂CH(OH)CH₂O(CH₂CH₂O)₁₃CH₂CH=CH₂, C₁₀F₂₁CH₂CH(OH)CH₂O(CH₂CH₂O)₁₆CH₂CH(OH)CH₂OCOC(CH₃)=CH₂, C₁₂F₂₁CH₂CH(OCOCH₃)CH₂O(CH₂CH₂O)₂₂COC(CH₃)=CH₂, C₈F₁₇CH₂CH(OCOCH₃)CH₂O(CH₂CH₂O)₁₀COCH=CH₂, C₉F₁₉(CH₂)₃CH(OH)CH₂O(CH₂CH₂O)₅(CH(CH₃)CH₂O)₅COCH=CH₂, C₁₅F₃₁CH₂CH(OCOCH₂CH₃)CH₂O(CH₂CH₂O)₁₃CH₂CH=CH₂, C₁₁F₂₃CH₂CH(OH)CH₂O(CH₂CH₂O)₈CH₂CH₂NHCOCH=CH₂. Specific examples of the ethylenically unsaturated monomer to be copolymerized with the monomer (II) are vinyl chloride, vinyl acetate, styrene, α-methylstyrene, methyl vinyl ketone, acrylic or methacrylic acid or its derivative of the formula: CH₂=CR⁶COOR⁷ (III) wherein R⁶ is a hydrogen atom or a methyl group; R⁷ is a hydrogen atom, a sodium atom, a potassium atom, an ammonium group, a C₁-C₁₈ alkyl group, a glycidyl group or a group of the formula: -(CH₂CH₂O) p R⁸ in which R⁸ is a hydrogen atom, a C₁-C₁₈ alkyl group or a C₂-C₁₈ acyl group and p is the same as defined in the above, -(CH₂CH₂O) p -(CH₂CH(CH₃)O) q -(CH₂CH₂O) r -R⁸ in which R⁸, p, q and r are the same as defined in the above or -R⁹-OH in which R⁹ is a C₂-C₆ alkylene group; and acryl- or methacryl-amide or its derivative of the formula: CH₂=CR⁶CONHR¹⁰ (IV) wherein R⁶ is the same as defined in the above, R¹⁰ is a hydrogen atom or a group of the formula: -CH₂OH or -(CH₂) p -N(CH₃)₂ in which p is the same as defined in the above. The monomer(s) can be homo- or co-polymerized by a known method described in, for example, Japanese Patent Kokai Publication (unexamined) No. 134786/1978 and the Journal of the Japanese Association of Adhesives, Vol. 17, No. 9 (1981) 371. The hydrophilic resin includes glyoxal resin, melamine resin, polyamide resin, urethane resin, acrylic resin, triazine resin and the like. Some of the hydrophilic resins are commercially available under trade names of HW®-100 (Dainippon Ink and Chemicals), Sumitex® resin 901, 1000, M-3, NR-2, NS-2, W-2, AR-2 and AMH®-3000 (Sumitomo Chemical), Blencope® PWB®-4021, PEB®-4001 and PEB®-4002 (Nippon Oil & Fats), Teisan® urethane SL-1780 and SL®-4780 (Teikoku Chemical Industries) and SR®-1000 (Takamatsu Oil & Fats). The water- and oil-repellent may be a conventionally used one and preferably a copolymer of an acrylic acid derivative of the formula: R f CH₂CH₂XCOCH=CH₂ (V) wherein R f is the same as defined in the above and X is an oxygen atom or a sulphur atom, and an acrylic or methacrylic acid or its derivative of the formula: CH₂=CR⁶COOR¹¹ (VI) wherein R⁶ is the same as defined in the above and R¹¹ is a hydrogen atom, a sodium atom, a potassium atom, an ammonium group or a C₁-C₁₈ alkyl group. The preparation of the copolymer of the compounds (V) and (VI) is described in, for example, Japanese Patent Publication Nos. 851/1969, 31202/1971, 42880/1972, 3438/1975, 4800/1975, 2998/1978, 11324/1982 and 9666/1984 and Japanese Patent Kokai Publication (unexamined) Nos. 132694/1979 and 11888/1983. In the case where the soil release composition of the invention comprises the polymer (A) and the hydrophilic resin but not the water- and oil-repellent (C), the copolymer (A) comprises 10 to 100 % by weight, preferably 20 to 80 % by weight of the constituting unit (I) to impart sufficient oil repellency and the soil release property to the substrate. For the same reason as above, 5 to 95 parts by weight, preferably 20 to 80 parts by weight of the polymer (A) is contained in the composition. 5 to 95 parts by weight, preferably 10 to 80 parts by weight of the hydrophilic resin (B) is contained in the composition to impart the durable water absorption property and oil repellency as well as the soil release property to the substrate. In the case where the soil release composition of the present invention comprises the polymer (A), the hydrophilic resin (B) and the water- and oil-repellent (C), the polymer (A) comprises 10 to 100 % by weight, preferably 20 to 90 % by weight of the constituting unit (I) to impart sufficient oil-repellency and the soil release property to the substrate. For the same reason as above, 1 to 95 parts by weight, preferably 5 to 90 parts by weight of the polymer (A) is contained in the composition. 5 to 95 parts by weight, preferably 10 to 80 parts by weight of the hydrophilic resin (B) is contained in the composition to improve the durability of water- and oil-repellency as well as of the soil release property. 1 to 50 parts by weight, preferably 2 to 40 parts by weight of the water- and oil-repellent (C) is contained in the composition to impart sufficient water- and oil-repellency as well as the soil release property to the substrate. The soil release composition of the invention may further contain at least one additive used in the conventional soil release composition. The additive includes a catalyst which cures the hydrophilic resin (B) (e.g. zinc nitrate, magnesium chloride and the like) One of the commercially available catalyst is Sumitex® accelerator (trade mark of Sumitomo Chemical). The soil release composition of the invention may be applied to the substrate in the form of a solution, a dispersion, a suspension or an emulsion by a conventional method, for example, dip coating, spray coating, flow coating and the like. A medium in which said components are mixed includes water, acetone, ethyl acetate, tetrahydrofuran, trichlorotrifluoroethane, benzotrifluoride, hexafluoro-m-xylene, and mixtures thereof. The components of the invention are usually mixed in the medium in an amount of 0.5 to 1.0 parts by weight per 100 parts by weight of the medium. Now, the present invention will be explained further in detail by following examples. In the examples, the soil release composition comprising the polymer (A) and the hydrophilic resin (B) but not the water- and oil-repellent (C) is examined for the properties of water absorption, oil repellency and soil release as well as their durability. The soil release composition comprising the the polymer (A), the hydrophylic resin (B) and the water- and oil-repellent (C) is examined for the properties of water-repellent, oil-repellent and soil release as well as their durability. In the examples, parts and % are by weight unless otherwise indicated. Copolymers (A1) to (A5) and Polymers (i) to (iii) for comparison to be used in Examples and Comparative Examples were prepared in following Preparation Examples. Preparation Example 1 Preparation of Copolymer (A1) In a four-necked 200 ml flask equipped with a thermometer, a condenser, a stirrer and an inlet for introducing nitrogen, there were added a fluorine-containing monomer mixture (14 g) of the formula: CF₃CF₂(CF₂CF₂) n CH₂CH(OH)CH₂-O-Z-COC(CH₃)=CH₂ in which Z is a polyethyleneoxide residue having an average molecular weight of 400 and which contains the compounds wherein n is 2, 3, 4, 5 and 6 in amounts of 3 %, 55 %, 28 %, 12 % and 3 %, a methacrylate derivative (14 g) of the formula: HO-Z-COC(CH₃)=CH₂ wherein Z is the same as defined in the above, isopropanol (112 g) and dodecylmercaptan (0.4 g), and stirred at 67°C for 30 minutes with introducing nitrogen. Thereafter, perbutyl pivalate (0.17 g) was added to initiate the reaction and the polymerization was carried out at the same temperature for 6 hour with stirring. After removing isopropanol from the reaction mixture, the residue was washed with benzene and dried under reduced pressure to obtain Copolymer (A1). Preparation Examples 2-5 and Comparative Preparation Examples 1-3 Preparation of Copolymers (A2) to (A5) and Polymers (i)-(iii) In the same manner as in Preparation Example 1 but using the following monomers, the polymerization was carried out to obtain the polymer: Preparation Example 2 (Copolymer (A2)) The fluorine-containing monomer mixture as used in Preparation Example 1 (100 parts), the methacrylate derivative as used in Preparation Example 1 (100 parts) and HOCH₂-NHCOCH=CH₂ (20 parts). Preparation Example 3 (Copolymer (A3)) The fluorine-containing monomer mixture as used in Preparation Example 1 (100 parts), styrene (300 parts) and glycidyl methacrylate (100 parts). Preparation Example 4 The fluorine-containing monomer mixture as used in Preparation Example 1 (100 parts), the methacrylate derivative as used in Preparation Example 1 (80 parts) and butyl acrylate (20). Comparative Preparation Example 1 (Polymer (i)) CF₃CF₂(CF₂CF₂)₃CH₂CH₂OCOCH=CH₂ (100 parts), CH₃O-W-COC(CH₃)=CH₂ wherein W is a polyethyleneoxide residue having an average molecular weight of 660 (80 parts) and HOCH₂NHCOCH=CH₂ (20 parts). Comparative Preparation Example 2 (Polymer (ii)) H[SCH₂CH(CH₃)COO(CH₂CH₂O)₄COC(CH₃)CH₂]₁₀SH (10 parts) and C₈H₁₇SO₂N(C₃H₇)CH₂CH₂OCOC(CH₃)=CH₂ (60 parts). Comparative Preparation Example 3 (Polymer (iii)) C₈H₁₇SO₂N(C₃H₇)-W-COC(CH₃)=CH₂ (100 parts) and CH₃O-W-COCH=CH₂ (100 parts) wherein W is the same as defined in the above. Examples 1-4 and Comparative Examples 1-2 Preparation of a soil release composition The copolymer (A) or the comparative polymer, a hydrophilic resin and other additives were added according to the following composition to 100 parts of water and stirred to prepare a soil release composition with water-absorption property and oil-repellency: Composition Examples 1 and 2 Copolymer (A1) (0.5 part), Sumitex® resin 901 (0.5 part) and Sumitex® resin W-2 (0.5 part) (hydrophilic resins), and zinc nitrate (0.5 part). Example 3 Copolymer (A2) (0.5 part), and Blencope® PEB-4201 (0.5 part) (a hydrophilic resin) Example 4 Copolymer (A3) (0.5 part), and Sumitex® resin AR-2 (0.5 part) (a hydrophilic resin). Comparative Example 1 Polymer (ii) (0.5 part), Sumitex resin 901 (0.5 part) and Sumitex resin W-2 (0.5 part), and zinc nitrate (0.5 part). Comparative Example 2 Polymer (ii) (0.5 part), and Sumitex® resin AR-2 (0.5 part). Each composition prepared in Examples 1-4 and Comparative Examples 1-2 was applied to various substrates and its water-absorption property, oil-repellency property and soil release ability as well as their durability were examined. When the substrate was cloth, it was dipped in the composition for 5 minutes, squeezed with rollers, dried at 80°C for 10 minutes and heated at 150°C for 5 minutes. When the substrate was in the form of a plate, it was dipped in the composition for 5 minutes, dried at 80°C for 10 minutes with leaning it against a wall, and then heated at 150°C for 5 minutes. The properties of the treated substrate were evaluated as follows: Water-absorption property A drop of water is dropped on the surface of the treated substrate and a time (seconds) till complete disappearance of water is confirmed by naked eyes is measured. Oil-repellency A drop of 4mm in diameter of a following solvent mixture is dropped on the substrate and a critical composition of the mixture with which the drop maintains its form for three minutes is determined by naked eyes, and following point is assigned to express the oil-repellency. The larger the point, the better the oil-repellency. Point Nujol (vol. %) n-Hexane (vol. %) 100 50 50 90 60 40 80 70 30 70 80 20 50 100 0 0 (100 % Nujol not retained) Stainproofing test The treated substrate was dipped in a waste motor oil for 10 hours and the surface condition was observed by naked eyes. The criteria are as follows: 1: Very bad stain remains. 2: Bad stain remains. 3: Slight stain remains. 4: Little stain remains. 5: No stain remains. Durability The treated substrate is washed ten times according to JIS H 103 with a detergent concentration of 2 g/l (detergent: "Super Zabu®" manufactured by Kao) at 40°C with a bath ratio of 1 : 40 and then subjected to the water-absorption test, the oil-repellency test and the soil release tests as described in the above. The results are shown in Tables 1-1 to 1-3. Examples 5-12 and Comparative Examples 3-6 The copolymer (A) or the comparative polymer, a hydrophilic resin, a water- and oil-repellent and other additives in the following amounts were added according to the following composition to 100 parts of water and stirred to prepare a soil release composition with water-absorption property and oil-repellency: Composition Example 5 Copolymer (A1) (0.5 part), Sumitex® resin 901 (0.5 part) And Sumitex® resin W-2 (0.5 part), a water- and oil-repellent (A) 1) (0.1 part), and zinc nitrate (0.5 part). Example 6 Copolymer (A2) (0.5 part), Sumitex® resin M-3 (0.5 part), a water- and oil-repellent (A) (0.1 part), and Sumitex® accelerator (0.5 part). Example 7 Copolymer (A2) (0.5 part), Teisan® urethane SL-4780 (0.5 part), and a water- and oil-repellent (A) (0.1 part). Example 8 Copolymer (A3) (0.5 part), Sumitex® resin M-3 (0.5 part), a water- and oil-repellent (A) (0.1 part), and Sumitex® accelerator (0.5 part). Example 9 Copolymer (A3) (0.5 part), Serbifan® MKP1 (0.5 part) a water- and oil-repellent (A) (0.05 part) and a water- and oil-repellent (B) 2) (0.2 part), and Serbifan® KP2 (0.2 part). Example 10 Copolymer (A5) (0.5 part), Sumitex® resin (0.5 part), a water- and oil-repellent (A) (0.2 part), and Sumitex® accelerator (0.5 part). Example 11 Copolymer (A5) (0.5 part), Blencope® 4001 (0.5 part), and a water- and oil-repellent (A) (0.2 part). Example 12 Copolymer (A5) (0.5 part), Serbifan® MKP1 (0.5 part), a water- and oil-repellent (A) (0.2 part), and Serbifan® KP2 (0.2 part). Comparative Example 3 Polymer (i) (1 .0 part), Sumitex® resin M-3 (0.5 part), a water- and oil-repellent (A) (0.2 part), and Sumitex® accelerator (0.5 part). Comparative Example 4 Polymer (i) (0.5 part), Serbifan® MKP1 (0.5 part) a water- and oil-repellent (A) (0.05 part) and a water- and oil-repellent (B) (0.2 part), and Serbifan® KP2 (0.2 part). Comparative Example 5 Polymer (iii) (0.5 part), Sumitex® resin 901 (0.5 part) and Sumitex® resin W-2 (0.5 part), a water- and oil-repellent (A) (0.1 part), and zinc nitrate (0.5 part). Comparative Example 6 Polymer (iii) (0.5 part), Teisan® urethane SL-4780 (0.5 part), and a water- and oil-repellent (A) (0.1 part). Note: A water- and oil-repellent (A): A copolymer of C₈F₁₇-CH₂CH₂OCOCH=CH₂ and stearyl methacrylate having an average molecular weight of 25,000. A water- and oil-repellent (B): A copolymer of C₈F₁₇-CH₂CH₂SCOCH=CH₂ and stearyl methacrylate having an average molecular weight of 25,000. Each composition prepared in Examples 5-12 and Comparative Examples 3-6 was applied to various substrates and its water-repellency, oil-repellency and soil release ability as well as their durability were examined. The composition was applied to the substrate in the same manner as in Examples 1-4. The water-repellency was evaluated according to JIS L-1005. The oil-repellency and the soil release ability were evaluated in the same ways as in Examples 1-4. The durability of these properties was also evaluated in the same way as in Examples 1-4. The results are shown in Tables 2-1, 2-2 and 2-3.

Claims: A soil release composition comprising: (A) a polymer containing 10 to 100 % by weight of constituting unit of the formula: wherein R f is a C₃-C₂₁ fluoroalkyl group; R¹ is a hydrogen atom or a C₂-C₄ acyl group; R², R³, R⁴ and R⁵ are, the same or different, each a hydrogen atom, a methyl group or an ethyl group; A is a group of the formula: -CH₂CH(OR¹)CH₂-OCO- in which R¹ is the same as defined in the above, -CO-, -(CH₂) k N(R²)CO- in which R² is the same as defined in the above and k is an integer of 1 to 10, or -(CH₂) k - in which k is the same as defined in the above; h is an integer of 1 to 5; p is an integer of 1 to 40; q and r are, the same or different, each an integer of 0 to 40, (B) a hydrophilic resin, and (C) optionally a water- and oil-repellent, in a weight ratio of (A) : (B) : (C) of 5-95 : 95-5 : 0 or 1-95 : 5-95 : 1-50. The soil release composition according to claim 1, which comprises 5 to 95 parts by weight of the polymer (A) and 95 to 5 parts by weight of the hydrophilic resin (B). The soil release composition according to claim 2, wherein the polymer (A) comprises 20 to 80 % by weight of the constituting units (I). The soil release composition according to claim 2, wherein the weight ratio of the polymer (A) and the hydrophilic resin (B) is 5-80 : 95-20. The soil release composition according to claim 2, wherein the weight ratio of the polymer (A) and the hydrophilic resin (B) is 20-90 :80-10. The soil release composition according to claim 1, which comprises 1 to 95 parts by weight of the polymer (A), 5 to 95 parts by weight of the hydrophilic resin (B) and 1 to 50 parts by weight of the water- and oil-repellent (C). The soil release composition according to claim 6, wherein the polymer (A) comprises 20 to 90 % by weight of the constituting unit (I). The soil release composition according to claim 7, which comprises 5 to 90 parts by weight of the polymer (A), 10 to 80 parts by weight of the hydrophilic resin (B) and 2 to 40 parts by weight of the water- and oil-repellent (C). The soil release composition according to claim 1, wherein the number of the fluorine atoms of the group R f is at least twice larger than that of the carbon atoms of said group. The soil release composition according to claim 1, wherein the polymer (A) is a homopolymer of the constituting unit (I). The soil release composition according to claim 1, wherein the polymer (A) is a copolymer comprising the constituting units (I) and constituting units derived from at least one comonomer selected from the group consisting of vinyl chloride, vinyl acetate, styrene, α-methylstyrene, methyl vinyl ketone, acrylic or methacrylic acid or its derivative of the formula: CH₂=CR⁶COOR⁷ (III) wherein R⁶ is a hydrogen atom or a methyl group; R⁷ is a hydrogen atom, a sodium atom, a potassium atom, an ammonium group, a C₁-C₁₈ alkyl group, a glycidyl group or a group of the formula: -(CH₂CH₂O) p R⁸ in which R⁸ is a hydrogen atom, a C₁-C₁₈ alkyl group or a C₂-C₁₈ acyl group and p is an integer of 1 to 40, -(CH₂CH₂O) p -(CH₂CH(CH₃)O) q -(CH₂CH₂O) r -R⁸ in which R⁸, p, q and r are the same as defined in the above or -R⁹-OH in which R⁹ is a C₂-C₆ alkylene group; and acryl- or methacryl-amide or its derivative of the formula: CH₂=CR⁶CONHR¹⁰ (IV) wherein R⁶ is the same as defined in the above, R¹⁰ is a hydrogen atom or a group of the formula: -CH₂OH or -(CH₂) p -N(CH₃)₂ in which p is the same as defined in the above. The soil release composition according to claim 6, wherein the water- and oil-repellent (C) is a copolymer of an acrylic acid derivative of the formula: R f CH₂CH₂XCOCH=CH₂ (V) wherein R f is a C₃-C₂₁-fluoroalkyl group and X is an oxygen atom or a sulphur atom, and an acrylic or methacrylic acid or its derivative of the formula: CH₂=CR⁶COOR¹¹ (VI) wherein R⁶ is a hydrogen atom or a methyl group and R¹¹ is a hydrogen atom, a sodium atom, a potassium atom, an ammonium group or a C₁-C₁₈ alkyl group. A method for imparting soil release property to a substrate comprising applying a soil release composition of claim 1 mixed in a liquid medium and drying it to remove the liquid medium from the substrate.

Inventors: HIRAI, MASARU, HISAMOTO, IWAO, ISHIKAWA, SUEYOSHI
Applicants: DAIKIN INDUSTRIES, LIMITED
Application year: 1986
Main classification: C08L33
IPC codes: C08L101, C08L33, C09K3, C08L77, C08G65, D06M15