METHOD FOR THE PREPARATION OF POROUS CARBON STRUCTURES

Abstract: This invention relates to the production of a novel, porous, carbon structure. A stabilised porous polymer comprising cavities joined by interconnecting pores is heated in an inert atmosphere to yield a stable, porous, carbon structure having the inherent structure of the original stabilised polymer.

Description: This invention relates to the preparation of porous carbon structures. US-A-4124691 describes the carbonisation of certain thermosetting polyurethanes. A foam is produced having membranes joined to strands, and the membranes are removed by the combustion process, to give a reticulate structure of strands. In United States Specification No 4 522 953, novel, cross-linked, homogeneous, porous polymeric materials were disclosed which can be made by polymerisation of a high internal phase emulsion comprising as a continuous phase a monomer and cross-linking agent, and as a discontinuous phase water, or aqueous solution. Subsequently, it was found that these porous polymers and other porous polymers will, on sulphonation, generate a sulphonated polymer having outstanding absorption of ionic solutions. Details of this invention are set out in United States Patent Specification No 4 536 521. Other functionalised highly porous cross-linked polymers prepared by a similar process have been disclosed in United States Patent Specifications Nos 4 611 014 and 4 612 334. The porous polymers disclosed in these United States specifications comprise 80% or a higher percentage of voids in the form of cavities interlinked by pores in the cavity walls and generally the porous structure consists of concave surfaces. It has now been found that certain porous polymers of this general type, when suitably stabilised to ensure that they do not de-polymerise on heating, can yield a porous carbon structure, which retains the cavities and interconnecting pores inherent in the original porous polymeric structure, and consists essentially of concave surfaces. The modification required to stabilise the polymeric material against de-polymerisation during heating can be in various forms, such as a high degree of cross-linking and the inclusion in the polymer of groups or elements which effectively reduce or prevent depolymerisation under the heating conditions employed, or the addition of a reinforcing resin. Accordingly the present invention provides a process as set out in claim 1. Preferably, the carbon structure has at least 80% voids and a density of less than 0.5 g/cm³. More preferably the porous carbon structure has at least 90% voids and a density of less than 0.25 g/cm³. Preferably, if maximum thermal stability is required, the degree of cross-linking is greater than 20% and the other modification is of at least 50%. The other modification can be provided by the inclusion of stabilising elements or groups. Suitable elements include the halogens and the preferred halogen is chlorine. Suitable groups to achieve this enhanced stability include nitro groups as well as sulphonates. Other groups include -CN, -CH₂Cl and -OCH₃, which like the sulphonate groups can be introduced into the polymer after its formation or by selection of appropriately modified monomers. As explained in United States Specification No 4 536 521, the sulphonation of the porous polymeric material may be carried out by a number of different routes, but to obtain a stable carbon structure, it is desirable that at least 5% of the polymer is cross-linked and furthermore that at least 10% of the cross-linked polymer is sulphonated. Preferably 20% is cross-linked and 50% of the cross-linked polymer sulphonated. The stability of the porous polymer at high temperature appears to be related both to the degree of cross-linking and to the degree of sulphonation. The preferred polymers are of styrene crosslinked with for example divinyl benzene, but other suitable comonomers may be blended with this monomer providing an adequate amount of cross-linking is achieved to form a rigid polymeric structure able to withstand the heating required in the preparation of the carbon structure. In the process, preferably, the temperature is raised to at least l200°C if the stabilising agent content of the final carboniferous structure is to be reduced. Alternatively, polymers which may be stabilised against depolymerisation may be provided using monomers other than styrene. The only other essential feature of such monomers is that they are sufficiently water-immiscible to form a stable high internal phase emulsion which can be polymerised to form the basic porous structure required in these materials. Suitable monomers include alkyl acrylonitriles such as methacrylonitrile cross-linked with divinyl benzene and crotononitrile cross-linked with divinyl benzene. The rate at which the temperature of the porous polymer is raised and the gaseous environment in which the heating takes place must be carefully controlled to prevent damage to the porous structure by the sudden evolution of degradation products. However, these factors are related to the actual polymer chosen and precise conditions can readily be found by experiment. Clear guidance is given in the following examples concerning various polymer systems. This invention also provides a process in which the porous polymer is a flexible polymer and is modified by the incorporation of a resin to coat the interior surfaces of the polymer, prior to heating to carbonise the polymer. The following examples illustrate the preparation of the porous carbon structures according to this invention. Example l A high internal phase emulsion was prepared by the method disclosed in US Specification No 4 522 953. The continuous phase was made up from the monomer and cross-linking agent which was divinyl benzene containing approximately 50% of ethyl vinyl benzene and present in an amount sufficient to give 20% to 40% cross-linked density. The aqueous phase comprised potassium persulphate initiator at 2.5 g per litre and 0.l M calcium chloride. The aqueous phase was sufficient to generate a 90% void volume in the high internal phase emulsion. The high internal phase emulsion was polymerised and dried in accordance with the teaching of US Specification No 4 522 953. Samples of the dried polymer were heated in an electrically heated tube furnace from ambient temperature to 600°C in an oxygen-free nitrogen atmosphere. The rate of heating was generally controlled below 5°C per minute and in the range l80°C to 380°C the rate of heating was below 2°C per minute. After the heating process the samples were cooled to ambient temperature in an inert atmosphere to prevent oxidation by air. The chemical and physical properties of the carbonised polymers are set out in Tables l and 2 below. In the column headed "Materials", "a" represents the monomer volume in cm³, "b" the cross-linking agent volume in cm³ and "c" the surfactant weight in grams. The surfactant in each case was Span 80 (sorbitan monooleate). Material a, b, c Poly(3-chlorostyrene) 5:5:2 Carbonised 600°C/nitrogen Surface area 40 ± 10 m²/g 520 ± 10 m²/g Permeability 2.8 Darcys 5.4 Darcys Bubble point 0.055 kg/cm ² 0.04 kg/cm ² Electrical resistivity >10⁸ ohm metre >10⁸ ohm metre Material a, b, c Poly (2-Cl styrene) 7:4:2 Poly (3-Cl styrene) 5:5:2 Poly (4-Cl styrene) 5:5:2 Native weight 2.7080 g 1.5801 g 1.5082 g Carbonised to 600°C/N₂ 0.5024 g 0.6884 g 0.2952 g Native compn C=73.21% C=76.70% C=76.66% H=6.51% H=6.16% H=6.57% Cl=13.73% Cl=13.98% Cl=13.96% Carbonised compn C=73.39% C=82.06% C=86.50% H=2.36% H=2.81% H=3.60% Cl< 1% Cl< 1% Cl< 1% Example 2 Using the same processing techniques a flexible porous polymer was prepared comprising ethyl hexyl acrylate:styrene (60:40) at 90% void volume using a 0.lM calcium chloride solution and cross-linked with l0% commercial divinyl benzene. A dried strip of the polymer weighing 0.75 g was soaked in furan resin until the strip was wet throughout in approximately 2 minutes. The excess resin was removed from the strip and the resulting moist sample cured at 60°C for 2 days in air. The cured sample weighed l.80 g. This sample was carbonised carefully to a temperature of l000°C and the resulting product was an electically-conducting porous carbon of extreme fragility weighing 0.59 g. This sample, having dimensions l0 mm × 8 cm, had a resistance of approximately 50 ohms. Example 3 A further porous polymer was prepared using 5 cm³ methylacrylonitrile and 5 cm³ divinyl benzene containing 55% ethyl vinyl benzene to a 90% void volume using 0.lM calcium chloride solution and persulphate initiator. A sample of the dried polymer was heated in an inert atmosphere of argon to l000°C at 3°C per minute, except in the region 300°C to 500°C in which the rate was l°C per minute. The resulting material was porous and approximately 4 times stronger than the original porous polymer. It was also electrically-conducting. A sample l0 mm × 7 mm × 3 cm had resistance of approximately 4 ohms, giving a resistivity of approximately 6 to 7 × l0⁻³ ohms metres. The carbonised polymer had approximately 40% of the weight of the original porous polymer. Table 3 includes physical data relevant to characterise the examples. Example 4 0.233 g of a sulphonated polystyrene, porous polymer, prepared according to Example l7 of United States Patent Specification No 4 536 52l, having a degree of cross-linking of 20% and a degree of sulphonation of 70% and a porosity of 98% voids was heated in an electric furnace under a nitrogen atmosphere for 30 minutes. The sample was cooled under a nitrogen atmosphere and reweighed and found to weigh 0.ll8 g. Elemental analysis showed that negligible amounts of hydrogen were in the product. EDAX (energy dispersive X-ray analysis) indicated that about 40% of the initial sulphur remained in the product. On further heating under an inert atmosphere, this sulphur content can be reduced to effectively zero at about l200°C to yield a porous carbon having a density of 0.04 g/cm³. Figure l is an electron micrograph of the product after heating to 500°C and it will be apparent from the micrograph that the cavities and interconnecting pores and concave structure are present in the carboniferous structure. Example 5 A sample of poly(4-chlorostyrene) 5:5:2 as described in Table 2 was heated to l000°C using the technique set out in Example 3 to produce a further sample of the porous carbon provided by the present invention. Figure 2 is an electron micrograph of this material.

Claims: A process for the manufacture of a porous carbon structure comprising heating a porous polymer structure comprising cavities joined by interconnecting pores in an inert atmosphere to a temperature of at least 500°C characterized in that said polymer structure is a porous cross-linked addition polymer structure comprising cavities joined by interconnecting pores formed by polymerizing monomer which contains CH₂=CH- or CH₂=CR- where R is alkyl or is crotonitrile and cross-linking agent as the continuous phase of a high internal phase emulsion, said porous addition polymer structure having sufficient thermal stability to withstand said heating and yield said porous carbon structure retaining the structure of cavities and interconnecting pores of said addition polymer structure. A process as claimed in claim 1 in which the porous polymer structure is a sulphonated polystyrene. A process as claimed in claim 2 in which at least 20% of the polymer structure is cross-linked and 50% of the cross-linked polymer is sulphonated. A process as claimed in claim 1 in which the monomer of the polymer structure is an alkyl acrylonitrile. A process as claimed in claim 1 in which the polymer structure is a polychlorostyrene. A process as claimed in any one of claims 1 to 5 in which the degree of cross-linking of the polymer structure is greater than 20%. A process as claimed in claim 1 in which the porous polymer structure is a flexible polymer and is modified by the incorporation of a resin to coat the interior surfaces of the polymer, prior to heating to carbonise the polymer. A process according to any one of the preceding claims wherein said porous carbon structure has at least 80% voids and a density of less than 0.5 g/cm³. A process according to any one of the preceding claims wherein said porous carbon structure has at least 90% voids and a density of less than 0.25 g/cm³.

Inventors: EDWARDS, CHRISTOPHER JOHN CARRUTHERS, HITCHEN, DAVID ANDREW, SHARPLES, MARTIN
Applicants: UNILEVER N.V., UNILEVER PLC
Application year: 1986
Main classification: C04B35
IPC codes: C04B35, C04B38