POLYOLEFIN COMPOSITION

Abstract: Apolyolefin composition is disclosed, which comprises a polyolefin and an inorganic filler, wherein the polyolefin compo­ sition comprising (A) 75 to 97% by weight of a polyolefin com­ ponent comprising (a) 90 to 65 parts by weight of an ethylene­ propylene copolymer having an ethylene content of not more than 7% by weight and/or polypropylene and (b) 10 to 35 parts by weight of a polyethylene having a melt index of not lower than 10 g/min., said melt index being from 1.0 to 50 times that of the polymer (a), and (B) 25 to 3% by weight of a fibery inor­ ganic filler having an average fiber diameter of 0.1 to 2 mi­ crometers and an aspect ratio of 20 to 60. The polyolefin composition is capable of providing, upon molding, articles having good surface appearance, in particular glossiness and improved mechanical strengths with less warp­ ing and deformation.

Description: The present invention relates to a polyolefin composition comprising a specified kind of polyolefin reinforced with a fibery inorganic filler having a specified characteristic. BACKGROUND OF THE INVENTION Polyolefin compositions filled with an inorganic filler generally have a slightly reduced impact strength but have a high stiffness. Those compositions filled with a fibery inorganic filler represented by glass fiber have a highly improved strength such as tensile strength and flexural strength as well as highly improved stiffness. Therefore, such polypropylene compositions are widely used as an industrial material. The US-A-3 487 128 is directed to an improved polypropylene composition comprising crystalline polypropylene having at least 50 % by weight of an isotactic portion, 2 to 30 % by weight of a normally solid polyethylene and 2-30 % by weight of an ethylene-propylene copolymer having an ethylene content of 2 to 20 % by weight and a cristallization degree of 5 to 40% by weight which is obtained as a polymerization solvent-soluble by-product in the presence of a Ziegler-Natta coordination catalyst wherein ethylene or a mixed gas of ethylene and propylene are introduced at the latter stage of the polymerization for forming the block copolymer. The GB-A-1 156 813 discloses a polyolefinic blend comprising a homopolymer of polypropylene or a copolymer or a block-polymer of propylene having a melt flow rate of 0.5 to 10.0 and a density of 0.9 to 0.92 gm/cm³, a homopolymer of ethylene or a copolymer of ethylene having a melt index of 0.5 to 10 and an ethylene/propylene copolymer or an ethylene-propylene terpolymer having an ethylene content of 30 to 65 % by weight and an inherent viscosity of 1.5 to 3.0. The US-A-4 113 806 deals with a propylene impact blend comprising as a necessary third component an amorphous ethylene-propylene copolymer elastomer, with or without a non-conjugated diene having a combined ethylene content of at least 50 % by weight of said elastomer. The FR-A-2 011 235 describes a thermoplastic molding composition comprising an ethylene-propylene copolymer which can comprise up to 30% of ethylene and polyethylene as a second component, which components have a defined melt index of 0.5 to 60 and 0.4 to 80, respectively. The present inventors have already found that a resin composition comprising a polypropylene, a polyethylene and a fibery inorganic filler having a predetermined fiber diameter and aspect ratio has very high stiffness and impact strength (Japanese Patent Application No. 194293/84). This composition is useful as a material for use in automobiles and ordinary electric equipments since it has a high stiffness and impact strength. However, it is not satisfactory as a material for a housing of television set and refrigerator, a fender of automobile and the like which are required to have a glossiness, and therefore improvement has been desired. Further, the present inventors have found that a resin composition comprising a blend of a polypropylene and a polyethylene of which the ratio of melt index of the polypropylene to that of the polyethylene is in a predetermined range, and non-fibery inorganic filler is highly glossy and has a high stiffness and impact strength (Japanese Patent Application No. 18645/85). However, since the inorganic filler contained in the above composition is not fibery, the resin composition is poor in glossiness and stiffness as compared with ABS resin. Further, it is unsatisfactory in the appearance of weld and in mechanical strength. When a pigment is added to the resin composition, the resulting composition is in short of color developing property and brightness. Materials for producing housings and fenders having a stiffness and glossiness as high as possible are desirable, and it has been desired to develop a resin composition which can be molded into an article having an excellent stiffness and glossiness as compared with that described in Japanese Patent Application No. 18645/85 and comparable to ABS resin. SUMMARY OF THE INVENTION An object of the present invention is to provide a polyolefin composition which can give a molded article having a good surface appearance, especially surface glossiness and an improved mechanical strength and surface hardness as well as high stiffness and suffering less warping and deformation. Another object of the present invention is to provide a polyolefin composition which can give a molded article having a very excellent glossiness and yet maintaining a mechanical strength as high as or higher than that composed of conventional resin composition even when the article is of a small thickness. As a result of extensive reseach on the development of polyolefin compositions suitable for a material for use in the field of, for example, automobiles, domestic electric appliances, office automation devices and the like, the present inventors have now found that a polyolefin composition which can be molded into an article having an excellent glossiness and a high mechanical strength such as impact strength as well as having a high stiffness, surface hardness and anti-thermal stiffness is obtained by blending a specified ethylene-propylene copolymer and/or polypropylene, a specified polyethylene and a specified fibery inorganic filler in a specified ratio. The object of the present invention is to provide a polyolefin composition comprising a polyolefin and an inorganic filler, wherein said polyolefin composition comprises (A) 75 to 97 % by weight of a polyolefin component comprising (a) 90 to 65 parts by weight of an ethylene-propylene copolymer having an ethylene content of not more than 7 % by weight and/or a polypropylene and (b) 10 to 35 parts by weight of a polyethylene, an ethylene-butene-1-copolymer or a graft polyethylene having a melt index of not lower than 10g/10min., said melt index being from 1.0 to 50 times as high as that of the polymer (a), and (B) 25 to 3 by weight of a fibery inorganic filler having an average fiber diameter of 0.1 to 2 micrometers and an aspect ratio of 20 to 60. DETAILED DESCRIPTION OF THE INVENTION The component (a) of the polyolefin composition which can be used in the present invention is an ethylene-propylene copolymer having an ethylene content of not more than 7% by weight or a polypropylene (i. e., propylene homopolymer) or a mixture of the ethylene-propylene copolymer and the polypropylene in a desired ratio. The ethylene-propylene copolymer can be polymers which are obtained by polymerizing at least propylene and ethylene, and can be generally used as a molding compound. Suitable examples of the ethylene-propylene copolymer which can be used in the present invention include ethylene-propylene block copolymers, ethylene-propylene random copolymers, and ethylene-propylene-diene copolymers such as those containing dicyclopentadiene as the third monomer. Of these, ethylene-propylene block copolymers are preferred. The term "ethylene-propylene block copolymer" as used herein refers to block copolymers of ethylene and propylene as monomer units, blends of polyethylene and polypropylene, and blends of ethylene-propylene copolymer and polyethylene. In a preferred embodiment of the present invention the polyolefin composition comprises an ethylene-propylene copolymer which is at least one member selected from the group consisting of a block copolymer of ethylene and propylene, a blend of a polyethylene and a polypropylene, an a blend of a block copolymer of ethylene and propylene as monomer units and a polyethylene. As for the component (a), it is essential that the above-described ethylene-propylene copolymer has an ethylene content of not more than 7 % by weight. When the ethylene-propylene copoylmer used has an ethylene content of above 7 % by weight, the resulting molded article not only has a glossiness of 80 % or less, resulting in reduced improvement in glossiness but also has a stiffness of 1.96 x 10⁹ Pa (20,000 kg/cm²) or less: the article is not desirable. The ethylene-propylene copolymer described above can be produced in a conventional polymerization method such as multi-stage polymerization methods with 2 stages or 3 or more stages using Ziegler Natta catalyst. More particularly, the multi-stage polymerization can be carried out in the presence of Ziegler Natta catalyst in such a manner that for example, preparation of propylene homopolymer is carried out in the first stage, and in the second stage and thereafter, with or without removing unused propylene monomers, polymerizaton reaction is carried out in the co-presence of ethylene or in the co-presence of ethylene and propylene, thus preparing an ethylene-propylene copolymer. The reaction in each stage can be carried out at a pressure of from several to 40 atm and of from room temperature to 80°C. The polymerization can be performed according to various types of reaction such as solution polymerization, slurry polymerization , vapor phase polymerization or combinations thereof. The ethylene-propylene copolymer prepared according to the above-described multi-stage polymerization method would appear to be a copolymer composition consisting of a polyethylene unit and a polypropylene unit bonded to each other in the range where the ethylene content of the polymer is high, and on the other hand it would be probable that the ethylene-propylene copolymer obtained is a blend of a polyethylene and a polypropylene, or a blend of a ethylene-propylene copolymer and a polyethylene in the range where the ethylene content of the polymer is low. In any case, the ethylene-propylene copolymer prepared according to the above-described multi-stage polymerization method can be used advantageously in this invention regardless of what the composition of the product is like as far as ethylene content thereof is not more than 7% by weight. Such ethylene-propylene copolymer is commercially available under trade names of "Idemitsu Polypro 785H", "Idemitsu Polypro J3050H", etc. The polypropylene which is used in the present invention as component (a) can be a homopolymer prepared by polymerization of propylene or the above-described ethylene-propylene copolymer in which the ethylene content thereof is substantially zero. These propylene polymers are generally used as molding compound. The propylene homopolymer can be prepared by a conventional method, for example, a polymerization method using Ziegler Natta catalyst. As for the component (b), high density polyethylene, low desity polyethylene, linear polyethylene, branched chain polyethylene, such as ethylene-butene-1 copolymer, graft polyethylene etc. can be used which have a melt index of not lower than 10g/10min., preferably not lower than 15g/10min., the melt index being from 1.0 to 50 times, preferably from 1.5 to 20 times, as high as that of the polymer defined as component (a). When the polyethylene as the component (b) has melt index of lower than 10g/10min., improvement in glossiness of molded article is undesirably low. The polyethylene having a melt index lower than that of the component (a) is not suitable for the component (b) since it exhibits only a slight improvement in glossiness. On the other hand, when the melt index of the component (b) exceeds 50 times as high as that of the component (a), decrease in the impact strength of molded article occurs. The polyethylene which can be used in the present invention as the component (b) can be prepared in a conventional manner. In the present invention, the components (a) and (b) are blended in a ratio of 90 to 65 parts by weight of the component (a) to 10 to 35 parts by weight of the component (b), preferably, 85 to 70 parts by weight of the component (a) to 15 to 30 parts by weight of the component (b). When the amount of the component (a) exceeds 90 parts by weight, that is, the amount of the component (b) is below 10 parts by weight, the surface glossiness of molded articles tends to decrease undesirably. On the other hand, when the component (a) is contained in an amount of below 65 parts by weight, that is, when the component (b) is contained in an amount of above 35 parts by weight, molded articles tend to have a decreased anti-thermal stiffness, surface hardness or stiffness. In the present invention, the polyolefin component (A) is blended with a fibery inorganic filler having an average fiber diameter of 0.1 to 2 micrometers, preferably 0.2 to 1 micrometer, and an aspect ratio of 20 to 60, preferably 30 to 50. When the average fiber diameter of the component (B) is below 0.1 micrometer, various problems tend to arise in that not only dispersion of the components takes place only sufficiently, resulting in the occurrence of agglomerates on the surface but also the bulk specific density of the resin composition is too low to carry out compounding. On the other hand, when the average fiber diameter exceeds 2 micrometers and the aspect ratio exceeds 60, molded articles tend to suffer surface unevenness which could lead to poor appearance, while the component (B) has an average fiber diameter above 2 micrometers and an aspect ratio below 20, various problems tend to arise such that only a slight improvement is observed in the stiffness of molded articles. Any inorganic substance can be used as the component (B) as far as it meets the conditions as specified above. There can be used various fibers or fibery substances such as a magnesium oxide fiber, a fibery magnesium oxysulfate, a magnesium hydroxide fiber, a gypsum fiber, a potassium titanate fiber, a glass fiber, a calcium silicate fiber, a carbon fiber, a rock wool, a silicon azide whisker, a silicon carbide whisker, a ceramic fiber which is an alumina-silica based glass fiber, etc. Of these fibery inorganic fibers, a fibery magnesium oxysulfate, a magnesium hydroxide fiber and a gypsum fiber are preferred. In the polyolefin composition of the present invention, the polyolefin component (A) and the fibery inorganic filler (B) are used in such a ratio that 75 to 97% by weight of the component (A) is blended with 25 to 3% by weight of the component (B), preferably 80 to 95% by weight of the component (A) is blended with 20 to 5% by weight of the component (B). When the component (A) is contained in an amount above 97% by weight, that is, the amount of the component (B) is below 3% by weight, only a slight improvement in stiffness of molded articles is obtained. On the other hand, when the amount of the component (A) is below 75% by weight, that is, the amount of the component (B) is above 25% by weight, molded articles are unsatisfatory since they have not only a glossiness of below 80% but also a decreased impact strength. The components (a) and (b) described above are blended in a ratio within the above-described range and kneaded sufficiently by a dry mixing-melt mixing combination method, a multi-stage melt mixing method, a simple melt mixing method or a like method to prepare a polyolefin component (A). Further, the components (a) and (b) and the component (B) described above are blended, melted and kneaded to prepare a polyolefin composition of the present invention. Kneading can be carried out using a Banbury mixer, a co-kneader, an extruder a biaxial kneader and the like. The polyolefin composition of the present invention, which comprises a resin composition containing the above-described ethylene-propylene copolymer and/or propylene homopolymer, above described specific polyethylene and a fibery inorganic filler blended with each other in a specified ratio, not only has improved mechanical strengths such as impact strength, anti-thermal stiffness, surface hardness and stiffness but also is capable of providing molded articles having an excellent surface appearance and also suffering less warpage and deformation. In order to further improve the strength of molded articles composed of the polyolefin composition of the present invention, a silane based coupling agent and/or modified polyolefin can be added to the polyolefin composition. The silane based coupling agent or the modified polyolefin alone, or alternatively, both of them can be added to the polyolefin composition. Suitable examples of the silane based coupling agent include vinyltriethoxysilane, vinyltrimethoxysilane, vinyltrichloro-silane, vinyldichloro-ethylsilane, vinylchlorodiethylsilane, vinyltris(β-methoxyethoxysilane), γ-glycidoxypropyltrimethoxysilane, γ-glycidoxypropyltrimethoxysilane, γ-amino-propyltriethoxysilane, N-β-(aminoethyl)-γ-aminopropyltriethoxysilane, and N-β-(aminoethyl)-γ-aminopropylmethyldiethoxysilane. Preferably, the silane based coupling agent can be added in an amount of 0.1 to 3 parts by weight per 100 parts by weight of the sum of the polyolefin component (A) and the fibery inorganic filler (B). When the amount of the silane based coupling agent is below 0.1 part by weight, substantially no improvement in the mechanical strength of molded articles tend to be observed by the addition of the coupling agent. On the other hand, when the amount of the coupling agent exceeds 3 parts by weight, increase in the mechanical strength of molded articles is saturated. Therefore, it is disadvantageous from the economic viewpoint to add the silane based coupling agent in an amount of above 3 parts by weight. Suitable examples of the modified polyolefin include polyethylenes, polypropylenes and ethylene-propylene copolymers each modified with unsaturated carboxylic acids, unsaturated carboxylic acid derivatives, chlorine or vinylsilane. Examples of the unsaturated carboxylic acids which can be used in the modification include acrylic acid, methacrylic acid, maleic acid, fumaric acid, itaconic acid, crotonic acid, citraconic acid, sorbic acid, mesaconic acid, angelic acid, etc. As for the unsaturated carboxylic acid derivative, there can be used acid anhydrides, esters, amides, imides, and metal salts derived from unsaturated carboxylic acids. Specific examples thereof include maleic anhydride, itaconic anhydride, citraconic anhydride, methyl acrylate, methyl methacrylate, ethyl acrylate, butyl acrylate, maleic acid monoethyl ester, acrylamide, maleic acid monoamide, maleimide, N-butylmaleimide, sodium acrylate, sodium methacrylate, etc. Of the various types of modified polyolefins, polypropylenes modified with maleic anhydride are preferred. It is preferred to add the modified polyolefin in an amount of 0.1 to 5 parts by weight per 100 parts by weight of the total of the polyolefin component (A) and the fibery inorganic filler (B). When the amount of the modified polyolefin is below 0.1 part by weight, the mechanical strength of molded articles composed of the polyolefin composition sometimes fails to exhibit a sufficient increase. On the other hand, when the amount of the modified polyolefin is above 5 parts by weight, the mechanical strengths of molded articles do not increase correspondingly as the increase in the amount of the modified polyolefin, and the larger that amount is the more expensive and disadvantageous molded articles are. The polyolefin composition of the present invention can contain various types of additives such as an antioxidant, an antistatic agent, an ultraviolet light absorbent, a lubricant, a flame retardant, mould release agent, a coloring agent and the like, if desired. Suitable examples of the antioxidant include phenol compounds such as 2,6-di-t-butyl-p-cresol, butylated hydroxyanisole, 2,6-di-butyl-4-ethylphenol, steary-β-(3,5-di-t-butyl-4-hydroxyphenyl)propionate, 2,2-methylenebis(4-methyl-6-t-butylphenyl), 2,2-methylenbis(4-ethyl-6-t-butylphenol), 4,4-thiobis(3-methyl-6-t-butylphenol), 4,4-butylidenebis(3-methyl-6-t-butylphenol), tetrakis[methylene-3-(3,5-di-t-butyl-4-hydroxyphenyl)propionate]methane, 1,1,3-tris(2-methyl-4-hydroxy-5-t-butylphenyl)butane, etc., amine compounds such as phenyl-β-naphthylamine, N,N-diphenyl-p-phenylenediamine, etc., phosphor compounds such as tris(nonylphenyl) phosphite, triphenyl phosphite, trioctadecyl phosphite, diphenyl isodecyl phosphite, etc., sulfur compounds such as dilaurylthiodipropionate, dimyristylthiodipropionate, distearylthiodipropionate, etc., and the like. Suitable example of the antistatic agent include nonionic antistatic agents such as polyoxyethylene alkylamines, polyoxyethylene alkylamides, etc., anionic antistatic agents such as alkyl sulfonates, alkyl benzenesulfonates, etc., cationic antistatic agents such as quaternary ammonium chloride, quaternary ammonium sulfate, etc., amphoteric antistatic agents such as alkylbetains, alkylimidazolines, etc. Suitable examples of the ultraviolet light absorbent include salicylic acid based ultraviolet light absorbents such as phenyl salicylate, p-t-butylphenyl salicylate, etc., benzophenone based ultraviolet light absorbents such as 2,4-dihydroxybenzophenone, 2-hydroxy-4-methoxybenzophenone, etc., benzotriazole based ultraviolet light absorbents such as 2-(2-hydroxy-5-methylphenyl)benzotriazole, 2-(2-hydroxy-5-t-butylphenyl)benzotiazole, etc. As for the lubricant, aliphatic hydrocarbons, higher aliphatic alcohols, fatty acid amides, metal soaps, fatty acid esters, etc. can be used. Suitable examples of the flame retardant include halogen-containing flame retardants such as polytribromostylene, decabromodiphenyl ether, tetrabromobisphenol A, etc., phosphor based flame retardants such as ammonium phosphate, tricresyl phosphate, triethyl phosphate, acid phosphate, etc., inorganic flame retardants such as tin oxide, antimony trioxide, etc. and the like. Suitable examples of the mould release agent include carnauba wax, paraffin wax, silicone oil, etc. As for the coloring agent, ordinary coloring agents which are used for coloring plastics can be used. Further, the polyolefin composition of the present invention can contain an elastomer as far as it does not adversely affect the stiffness of the resulting molded articles, and also the polyolefin composition can contain a non-fibery inorganic filler such as talc, calcium carbonate, mica, etc. as far as the glossiness of the resulting molded articles is not decreased. The polyolefin composition of the present invention can be molded into articles of desired shape by means of injection molding, extrusion molding, etc. The polyolefin composition of the present invention can upon molding give rise to articles not only having an excellent surface glossiness but also having improved stiffness, impact strength, anti-thermal stiffness, surface hardness and the like, and as a result molded articles which are small in thickness and light in weight can be obtained without sacrificing the mechanical strengths thereof. Therefore, the polyolefin composition of the present invention is very useful as a material for use in domestic electric appliances, office automation devices, materials for automobiles, etc. With the polyolefin composition of the present invention, molded articles can be obtained which not only have excellent surface appearance and gloss but also have improved mechanical strengths such as impact strength as well as increase in stiffness, anti-thermal stiffness and surface handness with less warpage and deformation, resulting in that they can be small in thickness and light in weight. More particularly, molded articles obtained by molding the polyolefin composition of the present invention have a glossiness of 80% or more and a stiffness of 1,96 x 10⁹ Pa (20,000 Kg/cm²) or more. These characteristics of the polyolefin composition of the present invention have not been attained before a resin composition comprising an ethylene-propylene copolymer having a specified ethylene content and/or propylene homopolymer and a polyethylene having a specified melt index ratio in a specified blend ratio with a fibery inorganic filler in a specified blend ratio. The present invention will be explained in more detail with reference to examples and comparative examples. However, the present invention as claimed is not to be construed as being limited to these examples. EXAMPLES 1 to 12 Ethylene-propylene copolymer or polypropylene shown in Table 1, polyethylene shown in Table 1, and fibery inorganic filler shown in Table 1 were mixed well in a V-type blender and melt-mixed using a biaxial kneader to form pellets, and the pellets were injection molded at 200°C to prepare test pieces. These test pieces were subjected to determination of the following properties. Izod Impact Strength This was determined according to the method described in JIS K7110. Glossiness This was determined according to the method described in JIS K7105. Elastic Modulus in Bending This was determined accoring to the method described in JIS K7203. Thermal Deformation Temperature This was determined according to the method described in JIS K7207. Rockwell Hardness This was determined according to the method described in JIS K7207. The results obtained are shown in Table 1. COMPARATIVE EXAMPLES 1 to 14 Test pieces were prepared in the same manner as in Examples 1 to 12 except that the ethylene-propylene copolymer, polyethylene and fibery inorganic filler for Examples 1 to 12 were replaced by those for Comparative Examples 1 to 14 shown in Table 1. The test pieces thus-obtained were subjected to determination of various properties in the same manner as in Examples 1 to 12. The results obtained are shown in Table 1. As will be apparent from the results shown in Table 1, the test pieces, which are composed of the polyolefin composition comprising (A) 75 to 97% by weight of a polyolefin component comprising (a) 90 to 65 parts by weight of an ethylene-propylene copolymer having an ethylene content of not more than 7% by weight and/or polypropylene and (b) 10 to 35 parts by weight of a polyethylene having a melt index of not lower than 10g/10min., said melt index being from 1.0 to 50 times as high as that of the polymer (a), and (B) 25 to 3% by weight of a fibery inorganic filler having an average fiber diameter of 0.1 to 2 micrometers and an aspect ratio of 20 to 60, has a high Izod impact strength, flexural modulus of elasticity, thermal deformation temperature, Rockwell hardness, glossiness, etc. Although the present invention has been described with preferred embodiments, it is to be understood that variations and modifications may be employed as will be apparent to those skilled in the art. Such variations and modifications are to be considered with in the purview and scope of the claims appended hereto.

Claims: A polyolefin composition comprising a polyolefin and an inorganic filler, wherein said polyolefin composition comprises (A) 75 to 97 % by weight of a polyolefin component comprising (a) 90 to 65 parts by weight of an ethylene-propylene copolymer having an ethylene content of not more than 7 % by weight and/or a polypropylene and (b) 10 to 35 parts by weight of a polyethylene, an ethylene-butene-1-copolymer or a graft polyethylene having a melt index of not lower than 10g/10min., said melt index being from 1.0 to 50 times as high as that of the polymer (a), and (B) 25 to 3 % by weight of a fibery inorganic filler having an average fiber diameter of 0.1 to 2 micrometers and an aspect ratio of 20 to 60. A polyolefin composition as claimed in claim 1, wherein said ethylene-propylene copolymer is at least one member selected from the group consisting of an ethylene-propylene block copolymer, an ethylene-propylene random copolymer, and an ethylene-propylene-diene copolymer. A polyolefin composition as claimed in claim 2, wherein said ethylene-propylene block copolymer is at least one member selected from the group consisting of a copolymer of ethylene and propylene as monomer units, a blend of a polethylene and a polypropylene, and a blend of block copolymer of ethylene and propylene as monomer units and a polyethylene. A polyolefin composition as claimed in claimed 1, wherein said ethylene-propylene copolymer is at least one member selected from the group consisting of a block copolymer of ethylene and propylene, a blend of a polyethylene and a polypropylene, and a blend of block copolymer of ethylene and propylene as monomer units and a polyethylene. A polyolefin composition as claimed claim 1, wherein said ethylene-propylene copolymer is a copolymer prepared by carrying out, in a first step, a polymerization reaction of propylene homopolymer in the presence of Ziegler Natta catalyst, and then in a second or subsequent steps, with or without removing unused propylene monomer, a polymerization reaction in the co-presence of ethylene or in the co-presence of ethylene and propylene. A polyolefin composition as claimed in claim 5, wherein said ethylene-propylene copolymer is a copolymer prepared by carrying out said polymerization reaction in the first and second or subsequent steps under the conditions of a pressure of from several to 40.53 bar (40 atm) and a reaction temperature of from room temperature to 80°C. A polyolefin composition as claimed in claim 1, wherein the polypropylene of component (a) is a propylene homopolymer. A polyolefin composition as claimed in claim 1, wherein said component (a) is an ethylene-propylene copolymer having an ethylene content of 7 % by weight or less or a propylene homopolymer. A polyolefin composition as claimed in claim 1, wherein said fibery inorganic filler is at least one member selected from the group consisting of a magnesium sulfate fiber, fibery magnesium oxysulfate, a magnesium hydroxide fiber, a gypsum fiber, a potassium titanic fiber, a glass fiber, a calcium silicate fiber, a carbon fiber, rock wool, silicon azide whisker, a silicon carbide whisker, and a ceramic fiber. A polyolefin composition a claimed in claim 1, wherein said fibery inorganic filler is at least one member selected from the group consist of a fibery magnesium oxysulfate, a magnesium hydroxide fiber and gypsum fiber. A polyolefin composition as claimed in claim 1, wherein said polyolefin composition contains a silane based coupling agent. A polyolefin composition as claimed in claim 1, wherein said silane based coupling agent is contained in an amount of from 0.1 to 3 parts by weight per 100 part by weight of the sum of the component (A) and the component (B). A polyolefin composition as claimed in claim 1, wherein said polyolefin composition contains a modified polyolefin. A polyolefin composition as claimed in claim 1, wherein said modified polyolefin is contained in as amount of from 0.1 to 5 parts by weight per 100 part weight of the sum of the component (A) and the component (B). A polyolefin composition as claimed in claim 1, wherein said polyolefin composition further contains at least one member selected from the group consisting of an antioxidant, an antistatic agent, an ultraviolet light absorbent, a lubricant, a flame retardant, a mould release agent and a coloring agent. A polyolefin composition as claimed in claim 1, wherein said polyolefin composition is in the form of molded article for the use in domestic electric appliances, office devices and automobiles.

Inventors: NOMURA, MANABU, SHIMAZAKI, TOSHIFUMI, TOMOMATSU, RYUZO
Applicants: IDEMITSU PETROCHEMICAL CO. LTD.
Application year: 1986
Main classification: C08L23
IPC codes: C08K7, C08L51, C08L101, C08L23, C08L53, C08L21, C08L7, C08L77