PROCESS FOR THE REMOVAL OF POLYNUCLEAR AROMATIC HYDROCARBON COMPOUNDS FROM ADMIXTURES OF LIQUID HYDROCARBON COMPOUNDS

Abstract: A process wherein a feed comprising an admixture of liquid hydrocarbon compounds including polynuclear arom­ atic hydrocarbon compounds, (PNA's) is contacted in the presence of hydrogen over a catalyst comprising elemental iron with one or more alkali or alkaline earth metals at a tem­ perature sufficient to selectively hydrogenate and hydrocrack, or destroy the PNA's of the admixture without excessively hydrogenating and hydrocracking the non-PNA's of said feed.

Description: BACKGROUND OF THE INVENTION I. Field of the Invention This invention relates to a process for removing polynuclear aromatic hydrocarbons from liquid hydrocarbon mixtures which contain polynuclear aromatic hydrocarbons as an undesirable component(s), or contaminants. In particular, it relates to the removal of polynuclear aromatic hydrocarbons from motor fuels, especially reformates such as used for blending into motor gasoline pools. II. Background and Prior Art Gasolines are complex mixtures of hydrocarbons, and include paraffins, naphthenes, olefins, and aromatic hydrocarbons. They contain low boiling components (C₄), but the predominant hydrocarbons are those having from about 5 to 12 carbon atoms; more typically from about 5 to about 10 carbon atoms. Generally, gasoline boils within a range of from 0°C (32°F) to 225°C (437°F), or more typically from 25°C (77°F) to 210°C (410°F). Typically, gasoline contains from 15 vol. % to 20 vol. % paraffins, naphthenes and branched paraffins, which fall within a range of from C₅⁺ to C₁₂, from 15 vol. % to 20 vol. % of olefins which fall within a range of from about C₆ to about C₁₂, and from 60 vol. % to 70 vol. % of aromatics, the preponderance of which fall within a range of from C₆ to C₁₂. Most of the gasolines that are sold for motor vehicle use are derived from petroleum, but may also be derived in whole or in part from hydrocarbons obtained from synthetic sources. In general, the octane requirements of internal combustion engines require that the natural, or virgin naphtha, or other light boiling fraction used in making gasoline, be further processed in a catalytic reforming unit to increase the concentration of higher octane components in the mixture. Catalytic reforming, among other things, converts lower octane aliphatic compounds into higher octane aromatic species. The reforming catalyst contains platinum, often accompanied by other promoter and/or modifier metals, supported on a high acidity alumina base, and the process is run under relatively severe process conditions of low hydrogen pressure, e.g., 100-300 pounds per square inch gauge (psig)(689.5 to 2068.5 kPa gauge), high liquid feed rates LHSV = 2-10, and high temperatures, 450-510°C (842-950°F). Under such conditions, in the presence of such catalysts, condensation reactions (acid-catalyzed and/or free radical initiated) take place between the aromatic molecules present, or those being formed, to give higher molecular weight, multi-ring aromatic molecules known as polynuclear aromatic (PNA) hydrocarbons. The PNA hydrocarbons, or PNA's, are generally outside the nominal boiling range of gasoline but, because reformate is rarely distilled prior to blending into a refinery's gasoline pool, the PNA's typically end up in commercial motor fuels. The presence of PNA's in gasoline, often at several hundred to several thousand parts, per million parts by weight of gasoline (ppm), is well known and is believed to contribute to a problem known as "octane requirement increase," or ORI. In very simple terms, ORI is caused by the build-up of carbonaceous deposits in an internal combustion engine which, by limiting heat transfer from the combustion chamber, leads to preignition. Preignition causes the phenomenon known as engine knock or ping. Engine knock is typically "cured" by switching to and burning a higher octane gasoline. Typically, older engines, which have had time to develop significant carbonaceous deposits, require higher octane fuel than that which was used when the engine was new. The PNA's are major contributors to the build-up of carbon deposits in engines which leads to ORI. In particular, ORI increases dramatically with the presence of the high boiling, polycyclic, or multiple-ring aromatic compounds such as naphthalenes (2-rings), phenanthrenes (3-rings), pyrenes (4-rings) and the like. Depending on gasoline composition, the ORI can be as small as 1-2 octane numbers or as great as 10-12 octane numbers. ORI tends to be highest in unleaded gasoline, wherein reformate is most commonly blended to provide the required octane levels. The simplest way to remove PNA's from gasoline is to redistill the processed reformate before adding it to the motor gasoline pool. The PNA's, being higher molecular weight, higher boiling components, will remain in the distillation bottoms fraction while the overhead fraction will be PNA-free. However, since gasoline is sold on a volume basis, the C₅⁺ liquid yield loss associated with such a method for removing the PNA's can become economically unacceptable. This problem is further compounded by the additional energy required to redistill this quantity of material. Thus, there exists a profound need for a simple and economical method for the removal of PNA's from PNA-containing admixtures of liquid hydrocarbons, particularly reformates (and/or naphthas or gasoline) without substantial C₅⁺ liquid yield penalties. III. Objects It is, accordingly, an objective of the present invention to fulfill this need; especially by providing a novel process for removing PNA's from PNA-containing liquid hydrocarbon mixtures. It is, in particular, an object of this invention to provide a novel process for the removal of PNA's from gasoline blending stocks, especially high octane reformates, at relatively low temperatures and low hydrogen partial pressures. IV. The Invention These objects and others are achieved in accordance with the present invention embodying a process wherein a feed comprising an admixture of liquid hydrocarbon compounds which includes a polynuclear aromatic hydrocarbon compound, or compounds, is contacted in the presence of hydrogen over an iron catalyst at temperature sufficient to selectively hydrogenate and hydrocrack the polynuclear aromatic hydrocarbon compound, or compounds, of the admixture without excessively hydrogenating and hydrocracking the non-polynuclear aromatic hydrocarbon compound, or compounds, of said feed. The catalyst is characterized as containing elemental iron and one or more of an alkali or alkaline-earth metal [i.e., a Group IA or IIA metal (Periodic Table of the Elements, E. H. Sargent & Co., Copyright 1964 Dyna-Slide Co.)], or compound thereof, and preferably additionally a Group IIIA metal, or metal compound, particularly aluminum, or compound thereof, sufficient to selectively hydrogenate and hydrocrack the PNA compound, or compounds, or admixture thereof, without excessively hydrogenating and hydrocracking the non-PNA hydrocarbon compound, or compounds, at low temperatures, or temperatures ranging no higher than about 430°C (806°F) The catalyst can be supported or unsupported, but in either instance the catalytic surface is one which is constituted essentially of metallic, or elemental iron (Fe°) crystallites about which the alkali or alkaline-earth metals are dispersed, often as a monolayer of an alkaline oxide or alkaline-earth metal oxide. The catalyst is unsulfided, and can function in the presence of sulfur only when a sufficient portion or the catalytic surface of the catalyst is substantially metallic, or elemental iron (Fe°). The formation of sufficiently high concentrations of sulfur at the catalyst surface tends to produce catalyst deactivation via the formation of iron sulfide upon the catalyst surface as a consequence of which the use of feeds which contain high concentrations of sulfur or sulfur compounds should be avoided. High concentration of feed sulfur will soon deactivate the catalyst by converting a major portion of the metallic, or elemental iron surface of the catalyst to iron sulfide. Preferably, the liquid hydrocarbon feed is contacted over the iron catalyst at temperature ranging from 225°C (437°F) to 430°C (806°F), more preferably from 250°C (482°F) to 350°C (662°F), and at hydrogen partial pressures ranging from 0 psig (0 kPa gauge). (one atmosphere or 14.7 psia) to 1000 psig (6,895 kPa gauge), preferably from 100 psig (689.5 kPa gauge) to 600 psig (4137 kPa gauge), sufficient to hydrogenate and hydrocrack, or destroy the PNA's of the admixture of hydrocarbons without excessively hydrogenating and hydrocracking the non-PNA's of said feed. Feeds particularly susceptible to processing in accordance with this invention are PNA-containing admixtures of low sulfur hydrocarbon compounds wherein the high end boiling point of the feed is below 540°C (1004°F), preferably below 375°C (707°F), and more preferably below 225°C (437°F), and the feed is derived from petroleum or a synthetic liquid hydrocarbon admixture obtained from tar sands, coal liquids, shale oil, synthesis gas, methanol or the like. A PNA-containing reformate, whether derived from petroleum naphtha, cracked naphtha, a Fischer-Tropsch naphtha, or the like, is particularly useful as a feed, and very high levels of the PNA's can be removed from such reformates, even when the PNA's are present in relatively high concentrations. The use of a low sulfur feed is essential, and preferably also the feed should be of relatively low nitrogen content. Applicant is aware of work which had demonstrated, that relatively low sulfur, nitrogen-containing hydrocarbon feeds could be hydrodenitrogenated over an iron catalyst, the reaction proceeding via a low hydrogen intensive mechanism at low temperature and pressure. In particular, applicant is aware of a process for the selective denitrogenation of nitrogen-containing hydrocarbons, especially one for the selective cleavage, in the presence of hydrogen, of an aryl carbon-nitrogen bond from an aryl nitrogen-containing hydrocarbon without prior saturation with hydrogen of a non-nitrogen containing aryl constituting a portion of said aryl nitrogen-containing hydrocarbon; especially a non-nitrogen containing aryl moiety directly attached to the nitrogen being removed. It has now been discovered that at relatively low nitrogen concentrations, the mechanism of this type of reaction is shifted from one favoring carbon-nitrogen bond cleavage to one favoring carbon-carbon bond cleavage. In conducting the process of this invention, in treating feeds boiling within a range greater than 375°C (707°F) to 540°C (1004°F), it is preferred that nitrogen concentrations greater than 5000 ppm, preferably greater than 2000 ppm, and more preferably greater than 500 ppm be avoided. In treating feeds boiling within a range of greater than 375°C (707°F) to 540°C (1004°F), it is also preferred that sulfur concentrations greater than 5000 ppm, preferably greater than 2000 ppm, and more preferably greater than 500 ppm, be avoided. In treating feeds boiling within the range of greater than 225°C (437°F) to 375°C (707°F), it is preferable that nitrogen concentrations greater than 5000 ppm, preferably above 2000 ppm, and more preferably above 500 ppm, be avoided. In treating feeds boiling within a range greater than from 225°C (437°F) to 375°C (707°F) it is also preferable that sulfur concentrations greater than 2000 ppm, preferably greater than 500 ppm, and more preferably greater than 200 ppm, be avoided. In treating feeds boiling below 225°C (437°F) nitrogen concentrations greater than 500 ppm, preferably 200 ppm, more preferably about 20 ppm. should be avoided; and in treating such low boiling feeds, sulfur levels above 500 ppm, preferably above 200 ppm, and more preferably above 20 ppm should be avoided. In a preferred embodiment of the invention, a low sulfur, low nitrogen PNA-containing reformate boiling within a range of from 25°C (77°F) to 225°C (437°F) is contacted with hydrogen, or hydrogen-containing gas, over the iron catalyst at reaction conditions sufficient to selectively hydrogenate and hydrocrack out or destroy the PNA's of the feedstock without excessively hydrogenating and hydrocracking the non-PNA molecules of the feedstock. Suitably, the reaction is conducted at temperatures ranging from 225°C (437°F) to 430°C (806°F), preferably from 250°C (482°F) to 350°C (662°F), and under an atmosphere of hydrogen gas or admixture of hydrogen and another gas, or gases within which the hydrogen partial pressure ranges from 0 psig (0 kPa gauge) to 1000 psig (6895 kPa gauge) preferably from 100 psig (689.5 kPa gauge) to 600 psig (4137 kPa gauge). Some positive pressure of hydrogen is necessary in conducting the reaction, though the hydrogen pressure can thus be at atmospheric pressure, or less. In some instances it can be advantageous to add non-oxiding gases other than hydrogen to the treat gas to modify, improve, or control the reaction, e.g., nitrogen, ammonia, methane, carbon monoxide, carbon dioxide, or the like. The combination of temperature and hydrogen partial pressure are preferably such that a part of the feed, at reaction conditions, is in vapor phase. Temperatures above about 430°C (806°F) generally should not be employed because excessive temperature causes cracking of the feed, and carbon fouling of the catalyst. At temperatures below about 225°C (437°F), on the other hand, the temperature is generally inadequate to hydrogenate and hydrocrack the PNA molecules. Total gauge pressures are not critical, but generally range from 0 psig (0 kPa gauge) to 1200 psig (8274 kPa gauge), preferably from 100 psig (689.5 kPa gauge) to 750 psig (5171 kPa gauge). Treat gas rates, based on hydrogen, range from 500 to 10,000 SCF/B (89.5 to 1780.9 liters H₂/liter oil), preferably from 1000 to 5000 SCF/B (178.1 to 890.5 liters H₂/litre). Space velocities range generally from 0.05 LHSV to 50 LHSV, preferably from 0.2 LHSV to 20 LHSV. Elemental iron, modified with one or more alkali or alkaine-earth metals, or compounds thereof, is present in the catalyst sufficient to produce on contact with a feed at reaction conditions selective hydrogenation of the PNA molecules and subsequent carbon-carbon bond cleavage of the PNA compounds of the feed without significantly hydrogenating and hydrocracking the non-PNA hydrocarbon components of the feed. In such reactions some portion of the PNA molecules are cracked to produce gas, while the remainder is retained as lower molecular weight liquid aromatic hydrocarbons, with the result that C₅⁺ liquid yield loss is minimal. In the case of a catalytically reformed, high octane motor gasoline blending stock which contains objectionable quantities of PNA's, the selective hydrogenation and hydrocracking of PNA's results in minimum C₅⁺ liquid yield loss and, due to the retention of lower molecular weight liquid aromatic hydrocarbons, there is no observable octane debit. The PNA carbon-carbon bond cleavage reaction occurs over catalysts which contain iron, preferably as the major component, or major metal component. The catalyst may be bulk (unsupported) iron, or iron dispersed upon a support. The unsupported, or bulk iron catalyst is preferred and it may be employed as essentially metallic iron in bulk, or as a bulk iron promoted or modified with alkali or alkaline-earth metals, or the oxides of such metals, exemplary of which are sodium, potassium, cesium, magnesium, calcium, barium, or the like. The active iron catalyst, when a bulk iron catalyst, is preferably one which contains at least 50 percent elemental iron, preferably from 70 percent to 98 percent elemental iron, based on the weight of the catalyst. The iron catalyst, when a catalyst wherein the iron is distributed or dispersed upon a support, contains at least 0.1 percent iron (measured as elemental iron), preferably from 0.1 percent to 50 percent iron, and more preferably from 5 percent to 25 percent iron, based on the total weight of the catalyst. The supported metallic component, exclusive of the support component, or components, contains at least 50 percent iron (measured as elemental iron), and preferably from 70 percent to 98 percent iron. A bulk fused iron catalyst is preferred. The fused iron is one fused by heating and melting the iron, thus fusing the iron with an alkali or alkaline-earth metal, or metals, or with an alkali or alkaline-earth metal compound, or compounds, which are generally present in concentrations ranging from 0.01 percent to 10 percent, preferably from 0.2 percent to 4 percent, based on the total weight of catalyst. Sodium, potassium, cesium, magnesium, calcium, and barium are the preferred alkali or alkaline-earth metals. Aluminum, principally as an oxide, or compound thereof, is also a preferred promoter, or modifier, of the fused iron, and it is preferably contained in the catalyst in concentration ranging from 0.01 percent to 20 percent, preferably from 0.5 percent to 5 percent, calculated as aluminum oxide (Al₂O₃), based on the total weight of the catalyst. Other metals, or metal compounds, may also be used as promoters and/or modifiers, such metals including rhenium, nickel, cobalt, palladium, platinum, and copper and their compounds. Such metals or metal compounds may be added to the catalyst alone or admired one metal with another, or with other metals. The iron based catalyst, as suggested, may also be supported: preferably upon an inorganic oxide support. Supports include, but are not limited to, the oxides of aluminum, silicon, boron, phosphorous, titanium, zirconium, calcium, magnesium, barium, and mixtures of these and other components. Other supports may include clays, such as bentonite, zeolites, and other alumino-silicate materials, e.g., montmorillionite. Additional supports may be selected from the group of refractory carbides and nitrides of the transition metals of Groups IVB, VB, VIB, VIIB, and Group VIII iron group metals. Alumina, magnesia, and mixtures of alumina and magnesia are preferred supports. The iron based catalysts are prepared by methods which include precipitation, coprecipitation, impregnation, vapor deposition, and the formation of metal complexes (i.e., metal carbonyl, etc.) and the like. The impregnation of a porous inorganic oxide support, such as alumina, with a solution of an iron salt with subsequent drying, calcination and activation by reduction of the supported iron catalyst by contact and treatment of the catalyst with hydrogen, or hydrogen and ammonia, or ammonia in admixture with another reducing gas, or gases, has been found to provide a highly active catalyst for the removal of PNA's from admixtures of liquid hydrocarbon compounds. Impregnation of the support with iron, or iron and other metal promoters or modifiers, by the incipient wetness technique, or technique wherein the iron is contained in solution in measured amount and the entire solution absorbed into the support, subsequently dried, calcined, and activated. The supported iron catalyst can be, and is preferably promoted or modified with alkali or alkaline-earth metals, or oxides of such metals as sodium, potassium, cesium, magnesium, calcium, and barium, or the like. The alkali or alkaline-earth metal, or metals, are generally employed in concentrations ranging from 0.01 percent to 10 percent, preferably from 0.2 percent to 4 percent, based on the total weight of metal, exclusive of the weight of the support. Sodium, potassium, cesium, magnesium, calcium and barium are the preferred alkali or alkaline-earth metals. Aluminum principally as an oxide, or compound thereof, is also a preferred promoter, or modifier, and it is preferably employed in the catalyst in concentration ranging from 0.01 percent to 20 percent, preferably from 0.5 percent to 5 percent, calculated as aluminum oxide (Al₂O₃), based on the total weight of the supported component, exclusive of the weight of the support. Rhenium, nickel, cobalt, palladium, platinum, and copper, or compounds thereof, can also be added to the catalyst as promoters or modifiers, these metals, or the compounds thereof, generally being added in concentrations ranging from 0.01 percent to 10 percent, preferably in concentration ranging from 0.5 percent to 2.5 percent, calculated as metallic metal based on the weight of the supported component, exclusive of the weight of the support. After impregnation of the support, the metal impregnated support is dried generally at temperatures ranging from 65°C (149°F) to 280°C (536°F), preferably from 80°C (176°F) to 110°C (230°F) in circulating air, vacuum or microwave oven. The calcination is suitably conducted at temperatures ranging from 300°C (572°F) to 650°C (1202°F), preferably from 450°C (842°F) to 550°C (1022°F). The iron catalysts can be reduced, activated, or reactivated by contact with hydrogen, by sequential contact with hydrogen and ammonia, or reduced and activated by contact with an admixture of ammonia and hydrogen or by contact with an admixture of ammonia and another reducing gas or gases. The reducing gas and ammonia can be generated in situ or ex situ. The catalysts are more effectively activated if activated by contact with a stream of flowing hydrogen, or by contact with a stream characterised as an admixture or hydrogen and ammonia, or admixture of ammonia and another reducing gas, or gases. In addition, other pretreatment conditions may be used in combination with reduction in order to modify and/or enhance the catalyst. Treatment with a hydrogen rich blend with some carbon containing gas, e.g., carbon monoxide or carbon dioxide, can be used to introduce carbon to the catalyst. The catalyst is reactivated, after deactivation, by contact with hydrogen, or by contact with ammonia in admixture with hydrogen, or ammonia in admixture with another reducing gas, or gases. Similarly, the activity-maintenance of the catalyst can sometimes be improved during an operating run by introducing ammonia, or ammonia in admixture with another gas, or gases, with the nitrogen-containing feed. In general, the ammonia is employed in admixture with another gas, or gases, in concentration ranging from 0.01 percent to 20 percent, preferably from 0.2 percent to 10 percent, based on the volume of the gas. The catalyst is activated, pretreated, or reactivated by contact with the gas, or gaseous admixture, at temperatures ranging from 300°C (572°F) to 600°C (1112°F), preferably from 400°C (752°F) to 500°C (932°F). Suitably pressures range from 0 psig (0 kPa gauge) to 1200 psig (8274 kPa gauge), preferably from 0 psig to 1000 psig (0 kPa to 6895 kPa gauge). Hydrogen partial pressures generally range from 0 psig to 1000 psig, preferably from 100 psig to 600 psig (4137 kPa gauge). Space velocities generally range from 100 GHSV to 10,000 GHSV, preferably from 1000 GHSV to 5000 GHSV. Various PNA-containing hydrocarbon feeds can be processed in accordance with the present process to remove PNA's. Thus, the feedstock can be a liquid hydrocarbon derived from petroleum, or a liquid hydrocarbon derived from a synthetic source such as tar sands, coal, oil shale, Fischer-Tropsch liquids or the like, particularly liquids which have a final or high end boiling point of less than about 540°C (1004°F). Preferred feed stocks are those which have a final or high end point boiling below 375°C (707°F), more preferably below 225°C (437°F); and include, in particular, reformates produced by reforming naphthas, e.g., virgin petroleum naphtha, straight run gasoline, cracked naphtha, Fischer-Tropsch naphtha or the like, which generally contain PNA's ranging as high as about 3000 parts PNA's, per million parts by weight (ppm) of total hydrocarbons, and not infrequently as high as about 6000 ppm PNA's, or greater, based on total hydrocarbons. In accordance with the process of this invention, on a weight basis, generally at least 50 percent to 90 percent, or more, of the PNA's can be removed without excessive methane formation. The invention will be more fully understood by reference to the following demonstrations and examples which present comparative data obtained from runs illustrating its more salient features. All parts are given in terms of weight except as otherwise specified. Table I contains some chemical composition and physical characteristic information on two commercial fused iron catalysts used in the following examples. The Katalco 35-4 catalyst ("Katalco" is a trade name) on an as received basis is constituted of iron oxides modified by controlled amounts of alumina, calcia, potash, silica, and trace impurities. When reduced, the Katalco 35-4 catalyst becomes a highly active stable ammonia synthesis catalyst. The BASF-R catalyst on as as received basis is constituted primarily of reduced iron metal modified by controlled amounts of alumina, calcia, potash, silica, and trace impurities. The BASF-R catalyst was prereduced, or activated, by the manufacturer in a hydrogen containing gas and then surface stabilized (by mild oxidation) for ease of handling. Prior to use the BASF-R catalyst is prereduced in the reactor with hydrogen at mild conditions or allowed to activate (reduce) on oil at reaction conditions. When using Katalco 35-4, the fused iron catalyst was charged to a reactor, reduced by contact with hydrogen at 450-470°C (843-878°F) for 12 to 16 hours, and various feeds then passed with hydrogen over the catalyst bed at the reaction conditions subsequently described. When using the BASF-R catalyst, the fused iron catalyst was charged to a reactor, reduced by contact with hydrogen at about 400°C (752°F) for 0.5-2 hours or simply allowed to activate on oil as various feeds were passed with hydrogen over the catalyst bed at the reaction conditions subsequently described. In analyzing the feedstock, and product fractions, for PNA's two different analytical procedures were employed. In PNA Test No. 1, as employed in Examples 1-3 which follow, a packed GC column was employed, and the test was based on a standard mixture of multi-ring aromatics compared to an internal standard, triphenylbenzene. Every peak which had a relative retention time (RRT) longer than the RRT of acenaphthene was designated a PNA. The test procedure required that 20 ml of sample be evaporated to a volume of less than 1.0 ml. A known quantity of standard was added and the total volume brought to 1.0 ml with a light boiling solvent. This mixture was than analyzed by gas chromatography. The currently available method for integrating peak areas was found to present a difficulty in assigning proper values due to the lack of separation between the peaks in the PNA region (rough baseline approximations). Thus, the PNA values tended to be overestimated, to give inflated values, especially for samples which contained small amounts of PNA's (less than about 500 ppm). A variation of this technique, PNA Test No. 2, was also applied using a capillary column which gave much better separation of the PNA peaks of interest. A different standard, phenanthrene, was used. Since phenanthrene is a condensed three-ring aromatic molecule, it is more closely related to the majority of PNA's found (about 75-80% are condensed 3- and 4- ring aromatic compounds). Every peak was called a PNA which had a RRT longer than 9,10-dihydroanthracene (a value close to that for acenaphthene used in PNA Test No. 1). This method has proven to be very consistent and is believed to give more representative values for the PNA levels found in these reformates. EXAMPLES 1-3 In conducting these runs (Examples 1-3, tabulated in Table III) a 1/2" (1.27 cm) I.D. stainless steel tubular reactor was employed, the PNA-containing hydrocarbon feed and hydrogen having been cocurrently introduced through a 1/8" (3.2 mm) inlet line into the top of the reactor and passed downwardly over a fixed bed of Katalco 35-4 fused iron catalyst ground and screened to 50-150 Tyler mesh size (4000 - 105 µm) centered within the reactor. In introducing the PNA-containing hydrocarbon feed, a small positive displacement pump was employed. An infrared furnace was employed to heat the reactor, and the temperature of the reaction was measured by a thermocouple located within the catalyst bed, and controlled by the use of an automatic temperature controller in operative association with the infrared furnace. The product was passed through a bottom adapter and collected in a vented, cooled flask located near the bottom of the reactor. A back pressure regulator was employed to maintain the desired reactor pressure. The feedstock used in these runs (F1) was a high octane reformate prepared in a reforming pilot unit at low pressure, high recycle conditions during a testing program. This material analyzed as a typical reformate with a RONC (research octane number clear) of 102. Before use for PNA removal testing, it was weathered (left open to the atmosphere), a procedure which increased the RONC to 103.1 and removed the C₄- light ends to facilitate making accurate material balances. Further details on this feed are given in Table II below. The product collected from the reaction was analyzed by gas chromatography (G.C.) using a packed column to obtain separation of the PNA or multi-ring aromatic peaks, these peaks having been compared to a triphenylbenzene standard (PNA GC Test No. 1). For Example 1, a 24.3 g/10 ml charge of Katalco 35-4 fused iron catalyst was charged to the reactor and reduced at atmospheric pressure with a 5% NH₃/H₂ blend gas flowing at about 300 ml/min at 470°C (878°F) for about 2.5 hours. After activation of the catalyst, the flow of the 5% NH₃/H₂ gas blend was cut off, and the PNA-containing feed and hydrogen then introduced to the reactor. The initial level of PNA's in feedstock F1 was 3000 ppm as determined by the PNA Test No. 1, supra. The results obtained in conducting the reaction at a hydrogen partial pressure of 100 psig (689.5 kPa gauge) and at various temperatures and space velocities, are shown in Table III. The reduction in PNA concentration in the products is evident. In Example 2, a 7.43 g/3.0 ml charge of catalyst was reduced as in Example 1 and run at a hydrogen partial pressure of 150 psig (1034.3 kPa gauge), LHSV of 5.6, and at varying temperatures. The conditions are shown in Table III. At the three temperatures tested, the reduction in PNA levels, as can be observed, was quite significant. In Example 3 the catalyst (7.70 g/3.0 ml) was activated with pure hydrogen flowing at 300 ml/min at 470°C (878°F) for 16 hours. Feed and hydrogen were then introduced to the reactor at a hydrogen pressure of 150 psig (1034.3 kPa gauge), an LHSV of 5.5, and temperature of 350°C (662°F). Once again the reduction in PNA levels, as shown in Table III, was quite significant. Examples 4 and 5 were conducted in a larger pilot plant unit. This unit included a reactor which allowed the combined feed to be heated before it contacted the catalyst bed. The reactor was constituted of a one-half inch stainless steel tube with a one-eighth inch (3.2 mm) or one-quarter inch (6.4 mm) inlet line. A sandbath was used as the heat source. A two-barreled, high pressure syringe pump was used to meter the liquid feed to the reactor. A larger and more efficient product recovery system was used in order to obtain more exacting liquid yields and representative product for analysis. The RONC values were also obtained by a G.C. procedure. EXAMPLE 4 Feedstock F1 having a total aromatics content of 81.5% and an RONC of 103.1, and which initially contained 1600 ppm PNA's (PNA Test No. 2), was charged at a rate of 20 ml/hour over a 10.0 g charge of Katalco 35-4 fused iron catalyst (14-35 Tyler mesh, 1190 - 420 µm) at the conditions, and with results given in Table IV. Analyses of the product were conducted by the use of both PNA Test No. 1 and PNA Test No. 2, and both sets of valued are shown in Table IV. The results illustrate significant reductions (90+ %) in PNA levels. Other observations were made during the testing, to wit: Liquid recoveries were 100 ±1% and gas inlet rates equaled gas exit rates within experimental error. Complete material balances using both GC and MS analyses indicated an average liquid volume yield debit of about 0.4%. EXAMPLE 5 This run was made with a real feedstock, F2; a stabilized reformate obtained from a commercial reforming unit. This gasoline blending stock is believed to represent the best available material with which to test PNA removal for actual commercial application. An analysis of this feedstock is given in Table V below. The reactor was loaded with 4.0 ml (10.0 g) of Katalco 35-4 fused iron in the 14-35 Tyler mesh (1190-420 µm) range. The feed rate was set at 20 ml/h to give a LHSV of 5.0. The results shown in Table VI, it will be observed, illustrate the effectiveness of fused iron for lowering the PNA level in this reformate. There was less total PNA removal in this test than that seen in Example 4. Yet, the average PNA removal was still about 75-80%, a level which appears to be favorable for decreasing the detrimental effects of ORI. On the other hand, the average C₅⁺ LV% yields were higher than in Example 4. EXAMPLE 6 This run further demonstrates effective PNA removal from different reformates, the first a reformate, F3, prepared in a reforming pilot plant unit at low pressure, high recycle conditions during a testing program, and the second a reformate, F4, obtained from a commercial reforming unit. The run was begun using the F3 reformate as feed to the unit, and subsequently F4 reformate was cut into the unit. Analysis of these feedstocks are given in Table VII. The reactor was loaded with 4.0 ml (10.0 g) of BASF-R fused iron catalyst in the 14-35 Tyler mesh (1190-420 µm) range. No additional pretreat, other than that done by the manufacturer, was given to the catalyst prior to starting this run on oil. The feed rate was set at 20 ml/h to give an LHSV of 5.0. The results given in Table VIII illustrate the effectiveness of the fused iron catalyst employed in an operating run, at the conditions given, to lower the PNA level in these reformates over a much longer period of time than in the run described by reference to Example 5. Good operation was achieved over the entire length of the run (129 days), the data typically showing ≧90% PNA removal. Temperature increases were made during the run to maintain the activity of the catalyst, this being a commonly used method in fixed bed catalytic operations. The catalyst activity, it will be observed, was also successfully recovered by hydrogen treats made during the on-oil run. (Note sequence of events between and results for balances 116 and 124.) In this patent specification, the following apply: S.S. is an abbreviation for stainless steel. I.D. is an abbreviation for internal diameter. LHSV stands for liquid hourly space velocity. GHSV stands for gas hourly space velocity. SCF represents "standardized cubic foot". B stands for barrel. 1 inch (") is 2.54 cm. 1 lb (pound) is 0.4536 kg. 1 cu. ft . (cubic foot) is 28.317 liters. 1 barrel is 159 liters. Gauge pressure in psig is converted to kPa equivalent by multiplying by 6.895. °F is converted to °C by subtracting 32 and then dividing by 1.8. Mesh sizes quoted are of the Tyler series. Our co-pending European patent application No. 86305799.8 (European patent publication EP-A-219195) describes and claims a process for the conversion of a feed comprised of hydrocarbon compounds selected from the group consisting of a fused multi-ring aromatic hydrocarbon compound, a fused multi-ring hydroaromatic hydrocarbon compound, and an admixture of fused multi-ring aromatic hydrocarbons and fused multi-ring hydroaromatic hydrocarbons, having an initial boiling point of at least about 177°C (350°F), to lower boiling, higher octane hydrocarbons characterised by comprising contacting said feed, in the presence of hydrogen, over a catalyst comprised of elemental iron and one or more alkali or alkaline-earth metal components at a temperature ranging from 225°C to 430°C and hydrogen partial pressure ranging from 0 psig (0 kPa gauge) to 1000 psig (6895 kPa gauge) sufficient to selectively hydrogenate and hydrocrack said fused multi-ring aromatic hydrocarbon compound or fused multi-ring hydroaromatic hydrocarbon compound, or both, to produce a lower molecular weight, higher octane product. Our co-pending European patent application No. 86300749.8 (European patent application EP-A-210709) describes and claims a process for the denitrogenation of a feed comprising a nitrogen-containing hydrocarbon compound containing a carbon-nitrogen bond, and which feed is selected from naphthas, middle distillates including jet fuel, diesel fuel, solvents, light and heavy gas oil, vacuum bottoms and residua, characterised by comprising: contacting said feed, in the presence of hydrogen, over a catalyst comprised of elemental iron and one or more alkali or alkaline-earth metal components at a temperature ranging from 225°C to 430°C and hydrogen partial pressure ranging from 0 psig (0 kPa gauge) to 1000 psig (6895 kpa gauge) sufficient to cleave the carbon-nitrogen bond of said nitrogen-containing hydrocarbon compound and denitrogenate said nitrogen-containing hydrocarbon compound.

Claims: A process for removing polynuclear aromatic hydrocarbons from a feed comprising a molecular admixture of polynuclear aromatic hydrocarbon-containing hydrocarbons having a high end boiling point below 540°C (1004°F), a sulfur level below 5000 ppm, and nitrogen level below 5000 ppm characterized by contacting said feed, in the presence of hydrogen, over a catalyst comprised of elemental iron and one or more alkali or alkaline-earth metal components at a temperature ranging from 225°C (437°F) to 430°C (806°F) and a hydrogen partial pressure ranging from 0 psig (0 kPa gauge) to 1000 psig (6895 kPa gauge) sufficient to hydrogenate and hydrocrack the polynuclear aromatic hydrocarbon molecules of the molecular hydrocarbon admixture without excessively hydrogenating and hydrocracking the non-polynuclear aromatic hydrocarbon molecules of said feed. A process according to claim 1 further characterized in that said catalyst comprises a bulk iron catalyst which contains at least 50 percent elemental iron, based on the weight of the catalyst, and the catalyst is modified with one or more alkali or alkaline-earth metals. A process according to claim 1 further characterized in that said catalyst comprises an iron catalyst wherein the iron is dispersed upon an inorganic oxide support, the catalyst containing at least 0.1 percent iron, based on the total weight of the catalyst, the supported metallic component containing at least 50 percent iron, exclusive of the support component, or components, of the catalyst, and the iron contains one or more alkali or alkaline-earth metals. A process according to any one of claims 1-3 further characterized in that the catalyst with which the feed and hydrogen are contacted at reaction conditions contains one or more alkali or alkaline-earth metals in concentrations ranging from 0.01 percent to 10 percent. A process according to any one of claims 1-4 further characterized in that said catalyst comprises a metal or metal compound of a Group IIIA metal in addition to said elemental iron and one or more alkali or alkaline earth metals. A process according to any one of claims 1-5 further characterized in that said catalyst comprises in addition to said elemental iron and one or more alkali or alkaline earth metal, aluminum in concentration ranging from 0.01 percent to 20 percent, as aluminum oxide. A process according to any of claims 1-6 further characterized in that the feed has a sulfur level below 20 ppm, and a nitrogen level below 20 ppm. A process according to any of claims 1-7 further characterized in that the feed is derived from a petroleum or synthetic hydrocarbon source, and the feed has a high end boiling point below about 225°C (437°F). A process according to any of claims 1-8 further characterized in that the feed is a processed reformate suitable as a motor gasoline blending stock.

Inventors: HAMNER, GLEN PORTER, HUDSON, CARL WAYNE
Applicants: EXXON RESEARCH AND ENGINEERING COMPANY
Application year: 1986
Main classification: C10G45
IPC codes: B01J23, C10G45, C10G47