Color plus clear coatings employing polyepoxides and polyacid curing agents in the clear coat

Abstract: A color-plus-clear coating system is disclosed. A pig­ mented or colored base coat is first applied to a substrate fol­ lowed by the application of a transparent top coat to the base coat. The transparent top coat composition is a liquid cross-­ linkable composition comprising a polyepoxide and a polyacid curing agent. The polyepoxide-polyacid curing agent in the transparent top coat provides a composite coating with out­ standing gloss and distinctness of image making the compo­ site coating particularly useful as an automotive top coat.

Description: Background of the Invention Field of the Invention: The present invention relates to a process for applying a composite coating to a substrate by applying to the substrate a colored film forming composition to form a base coat and applying to said base coat a liquid clear film-forming crosslinkable composition comprising a curing agent to form a transparent top coat over the base coat and heating the coated substrate to cure the coating layers and, further, to a liquid crosslinkable film forming coating composition comprising an acrylic polymer and a curing agent. Brief Description of the Prior Art: Color-plus-clear coating systems involving the application of a colored or pigmented base coat to a substrate followed by the application of a transparent or clear top coat to the base coat are becoming increasingly popular as original finishes for automobiles. The color-plus-clear systems have outstanding gloss and distinctness of image, and the clear coat is particularly important for these properties. Two-pack clear coat compositions comprising polyols such as polyester polyols, polyurethane polyols and acrylic polyols and polyisocyanate curing agents give outstanding gloss and distinctness of image. However, the polyisocyanates are difficult to handle being sensitive to moisture and require cumbersome safety precautions. US-A-4,403,093 discloses narrow molecular weight hydroxyl functional oligomers synthesized via the reaction of a diol or triol with a cyclic anhydride. The resulting acid-ester is then reacted with a diepoxide to form a low molecular weight tetraol. The tetraol can be crosslinked with any resin which reacts with alcohol functionality such as melamine-formaldehyde resins, or isocyanates. US-A-4,355,071 discloses a substrate having a multiple coating comprising a first colored base coat to which is overcoated a clear top coat. The object of said reference and its solution is the incorporation of an ultraviolet light stabilizer in the color coat to improve the weatherability and durability of the color clear finish. Of the many resinous binders which are disclosed for both use in the color as well as in clear coat, there is no disclosure of the resinous binders of the pipe particularly mentioned in the claims of the present invention, that are polyepoxides and polyacid curing agents which are half-esters formed from reacting acid anhydrides with polyols. It is an object of the present invention to provide a further process for applying a specific composite coating to a substrate. It is another object of the present invention to provide a special film forming coating composition comprising an acrylic polymer and a curing agent. Both objects provide a color-plus-clear coating system which avoids the problems of polyisocyanate curing agents but which provides a finish which has outstanding gloss and distinctness of image so that the coating is useful as an original finish for automobiles. Summary of the Invention In accordance with the present invention, a process for applying a composite coating to a substrate by applying to the substrate a colored film forming composition to form a base coat and applying to said base coat a liquid clear film-forming crosslinkable composition comprising a curing agent to form a transparent top coat over the base coat and heating the coated substrate to cure the coating layers is provided which process is characterized in that the clear film forming composition comprises a polyepoxide is an epoxy group-containing acrylic polymer and a polyacid curing agent which is a half-ester formed from reacting a polyol and an acid anhydride wherein the equivalent ratio of epoxy to carboxyl in the composition is from 1:0.3 to 1:3.0, such that a cured product results. The invention also provides for a liquid crosslinkable film forming coating composition comprising an acrylic polymer and a curing agent which is characterized in that the acrylic polymer is an epoxy-containing polymer and the curing agent is polyacid curing agent which is a half-ester formed from reacting a polyol and acid anhydride and the equivalent ratio of epoxy to carboxyl in the composition is from 1:0.3 to 1:3.0 such that a cured product results. Detailed Description The film-forming composition of the base coat can be any of the compositions useful in coatings applications, particularly automotive applications. The film-forming composition comprises a resinous binder and a pigment to act as the colorant. Particularly useful resinous binders are acrylic polymers, polyesters, including alkyds, and polyurethanes. The acrylic polymers are copolymers of one or more alkyl esters of acrylic acid or methacrylic acid optionally together with one or more other polymerizable ethylenically unsaturated monomers. These polymers may be either of the thermoplastic type or thermosetting crosslinking type. Suitable alkyl esters of acrylic acid or methacrylic acid include methyl methacrylate, ethyl methacrylate, butyl methacrylate, ethyl acrylate, butyl acrylate and 2-ethylhexyl acrylate. Suitable other copolymerizable ethylenically unsaturated monomers include vinyl aromatic compounds such as styrene and vinyl toluene; nitriles such as acrylonitrile and methacrylonitrile; vinyl and vinylidene halides such as vinyl chloride and vinylidene fluoride and vinyl esters such as vinyl acetate. Where the polymer is of the crosslinking type, suitable functional monomers may be used in addition to the other acrylic monomers mentioned above and include, for example, acrylic acid, methacrylic acid, hydroxyethyl acrylate, hydroxyethyl methacrylate, hydroxypropyl acrylate, and hydroxypropyl methacrylate. The coating composition in such cases contains a crosslinking agent such as a condensate of an amine or an amide with formaldehyde such as urea, melamine, or benzoguanamine reacted with formaldehyde or a lower alkyl ether of such condensate in which the alkyl groups contain from 1 to 4 carbon atoms. Other crosslinking agents such as polyisocyanates including blocked polyisocyanates may also be used. Also, the acrylic polymer can be prepared with N-(alkoxymethyl)acrylamides and N-(alkoxymethyl)methacrylamides which result in self-crosslinking acrylic polymers. The acrylic polymer may be prepared by solution polymerization techniques in the presence of suitable catalysts such as organic peroxides or azo compounds, for example, benzoyl peroxide or N,N'-azobis-(isobutyronitrile). The polymerization can be carried out in an organic solution in which the monomers are soluble. Suitable solvents are aromatic solvents such as xylene and toluene and ketones such as methyl amyl ketone. Alternately, the acrylic polymer may be prepared by aqueous emulsion or dispersion polymerization techniques. Besides acrylic polymers, the resinous binder for the base coat composition may be an alkyd resin or a polyester. Such polymers may be prepared in a known manner by condensation of polyhydric alcohols and polycarboxylic acids. Suitable polyhydric alcohols include ethylene glycol, propylene glycol, butylene glycol, 1,6-hexylene glycol, neopentyl glycol, diethylene glycol, glycerol, trimethylolpropane, and pentaerythritol. Suitable polycarboxylic acids include succinic acid, adipic acid, azelaic acid, sebacic acid, maleic acid, fumaric acid, phthalic acid, tetrahydrophthalic acid, hexahydrophthalic acid, and trimellitic acid. Besides the polycarboxylic acids mentioned above, functional equivalents of the polycarboxylic acids such as anhydrides where they exist or lower alkyl esters of the polycarboxylic acids such as the methyl esters may be used. Where it is desired to produce air-drying alkyd resins, suitable drying oil fatty acids may be used and include those derived from linseed oil, soya bean oil, tall oil, dehydrated castor oil or tung oil. The polyesters and preferably the alkyd resins contain a portion of free hydroxyl and/or carboxyl groups which are available for further crosslinking reaction. Suitable crosslinking agents are the amine or amide-aldehyde condensates or the polyisocyanate curing agents as mentioned above. Polyurethanes can also be used as the resinous binder of the base coat. Among the polyurethanes which can be used are polymeric polyols which are prepared by reacting the polyester polyols or acrylic polyols such as those mentioned above with a polyisocyanate such that the OH/NCO equivalent ratio is greater than 1:1 so that free hydroxyl groups are present in the product. The organic polyisocyanate which is used to prepare the polyurethane polyol can be an aliphatic or an aromatic polyisocyanate or a mixture of the two. Diisocyanates are preferred, although higher polyisocyanates can be used in place of or in combination with diisocyanates. Examples of suitable aromatic diisocyanates are 4,4'-diphenylmethane diisocyanate and toluene diisocyanate. Examples of suitable aliphatic diisocyanates are straight chain aliphatic diisocyanates such as 1,6-hexamethylene diisocyanate. Also, cycloaliphatic diisocyanates can be employed. Examples include isophorone diisocyanate and 4,4'-methylene-bis-(cyclohexyl isocyanate). Examples of suitable higher polyisocyanates are 1,2,4-benzene triisocyanate and polymethylene polyphenyl isocyanate. Most of the polymers prepared as described above are organic solvent-based polymers, although acrylic polymers can be prepared via aqueous emulsion polymerization techniques and used as aqueous-based base coat compositions. Water-based base coats in color-plus-clear compositions are disclosed in U S-A-4,403,003, and the resinous compositions used in preparing these base coats can be used in the practice of this invention. Also, water-based polyurethanes such as those prepared in accordance with U S-A-4,147,679 can be used as the resinous binder in the base coat. The resinous binder for the base coat can also be the resinous binder used in formulating the clear film-forming composition described below. The base coat composition also contains pigments to give it color. Compositions containing metallic flake pigmentation are useful for the production of so-called "glamour metallic" finishes chiefly upon the surface of automobile bodies. Proper orientation of the metallic pigments results in a lustrous shiny appearance with excellent flop, distinctness of image and high gloss. By flop is meant the visual change in brightness or lightness of the metallic coating with a change in viewing angle, that is, a change from 90° to 180°. The greater the change, that is, from light to dark appearance, the better the flop. Flop is important because it accentuates the lines of a curved surface such as on an automobile body. Suitable metallic pigments include in particular aluminum flake, copper bronze flake and mica. Besides the metallic pigments, the base coating compositions of the present invention may contain nonmetallic color pigments conventionally used in the surface coating compositions including inorganic pigments such as titanium dioxide, iron oxide, chromium oxide, lead chromate and carbon black, and organic pigments such as phthalocyanine blue and phthalocyanine green. In general, the pigment is incorporated into the coating composition in amounts of 1 to 80 percent by weight based on weight of coating solids. The metallic pigment is employed in amounts of 0.5 to 25 percent by weight of the aforesaid aggregate weight. If desired, the base coat composition may additionally contain other materials well known in the art of formulated surface coatings. These would include surfactants, flow control agents, thixotropic agents, fillers, anti-gassing agents, organic co-solvents, catalysts and other customary auxiliaries. These materials can constitute up to 40 percent by weight of the total weight of the coating composition. The base coating compositions can be applied to various substrates to which they adhere. The compositions can be applied by conventional means including brushing, dipping, flow coating and spraying, but they are most often applied by spraying. The usual spray techniques and equipment for air spraying and electrostatic spraying and either manual or automatic methods can be used. Coatings of the present invention can be applied over virtually any substrate including wood, metals, glass, cloth, plastic, foam, including elastomeric substrates. They are particularly useful in applying over metal and elastomeric substrates that are found on motor vehicles. During application of the base coat composition to the substrate, a film of the base coat is formed on the substrate. Typically, the base coat thickness will be 0.25 x 10⁻⁶ to 12.7 x 10⁻⁵ m (0.01 to 5), preferably 0.254 x 10⁻⁵ to 5.08 x 10⁻⁵ m (0.1 to 2 mils) in thickness. After application to the substrate of the base coat composition, a film is formed on the surface of the substrate. This is achieved by driving solvent, i.e., organic solvent or water, out of the base coat film by heating or simply by an air-drying period. Preferably, the heating step will only be sufficient and for a short period of time to insure that the top coat composition can be applied to the base coat without the former dissolving the base coat composition, i.e., "striking in". Suitable drying conditions will depend on the particular base coat composition, on the ambient humidity with certain water-based compositions, but in general a drying time of from 1 to 5 minutes at a temperature of about 20-79°C (80-175°F). will be adequate to insure that mixing of the two coats is minimized. At the same time, the base coat film is adequately wetted by the top coat composition so that satisfactory intercoat adhesion is obtained. Also, more than one base coat and multiple top coats may be applied to develop the optimum appearance. Usually between coats, the previously applied base coat or top coat is flashed, that is, exposed to ambient conditions for 1 to 20 minutes. The clear film-forming composition which forms the transparent top coat is a liquid crosslinkable composition comprising a polyepoxide and a polyacid curing agent as defined thereinbefore. The polyepoxides used are epoxy-containing acrylic polymers. The epoxy-containing acrylic polymer is preferably a copolymer of an ethylenically unsaturated monomer having at least one epoxy group and at least one polymerizable ethylenically unsaturated monomer which is free of epoxy groups. Examples of ethylenically unsaturated monomers containing epoxy groups are those containing 1,2-epoxy groups and include glycidyl acrylate, glycidyl methacrylate and allyl glycidyl ether. Examples of ethylenically unsaturated monomers which do not contain epoxy groups are alkyl esters of acrylic and methacrylic acid containing from 1 to 20 atoms in the alkyl group. Specific examples of these acrylates and methacrylates are those mentioned above in connection with the acrylic polymers for the base coat. Examples of other copolymerizable ethylenically unsaturated monomers are vinyl aromatic compounds, nitriles, vinyl and vinylidene halides and vinyl esters such as those mentioned above. Acid group-containing copolymerizable ethylenically unsaturated monomers such as acrylic and methacrylic acid are preferably not used because of the possible reactivity of the epoxy and acid group. The epoxy group-containing ethylenically unsaturated monomer is preferably used in amounts of from 5 to 60, more preferably from 20 to 50 percent by weight of the total monomers used in preparing the epoxy-containing acrylic polymer. Of the remaining polymerizable ethylenically unsaturated monomers, preferably from 40 to 95 percent, more preferably from 50 to 80 percent by weight of the total monomers are the alkyl esters of acrylic and methacrylic acid. In preparing the epoxy-containing acrylic polymer, the epoxide functional monomers and the other ethylenically unsaturated monomers can be mixed and reacted by conventional free radical initiated organic solution polymerization as generally described above. The epoxy-containing acrylic polymer typically has a number average molecular weight between 1000 and 20,000, preferably 1000 to 10,000, and more preferably 1000 to 5000. The molecular weight is determined by gel permeation chromatography using a polystyrene standard. In determining molecular weights in this fashion, it is not the actual molecular weights which are measured but an indication of the molecular weight as compared to polystyrene. The values which are obtained are commonly referred to as polystyrene numbers. However, for the purposes of this invention, they are referred to as molecular weights. The epoxy-containing acrylic polymers result in products which have the best combination of coating properties, i.e., smoothness, gloss, durability and solvent resistance. Such polymers have been found to be particularly good in the formulation of clear coats for color-plus-clear applications. Preferably, the polyepoxides are those which have a glass transition temperature less than 50°C., preferably less than 30°C. The glass transition temperature (Tg) is described in PRINCIPLES OF POLYMER CHEMISTRY , Flory, Cornell University Press, Ithaca, NY, 1953, pages 52-57. The Tg can be calculated as described by Fox in Bull. Amer. Physic. Soc. , 1 , 3, page 123 (1956). The Tg can be determined experimentally such as by using a penetrometer such as a DuPont 940 Thermomedian Analyzer. The Tg of the polymers as used herein refers to the calculated values unless otherwise indicated. In a preferred embodiment of the invention, the polyepoxide is a mixture of epoxy-containing acrylic polymer mentioned above and a lower molecular weight polyepoxide, preferably an epoxy condensation polymer mentioned above which has a molecular weight less than 800. The blend of epoxy-containing acrylic polymer and low molecular weight polyepoxide provides for the best blend of gloss, solids content and cure response in the resultant cured coating and coating composition. The polyepoxide is present in the liquid crosslinkable composition in amounts of 10 to 90, preferably from 25 to 75 percent by weight based on total weight of resin solids. When the lower molecular weight polyepoxide is used, it is used in amounts of 1 to 40, preferably 5 to 30 percent by weight based on total weight of resin solids. The polyacid curing agent contains two or more acid groups per molecule which are reactive with the polyepoxide to form a crosslinked coating as indicated by its resistance to organic solvent. The acid functionality is preferably carboxylic acid, although acids such as sulfonic acid may be used but their use is not preferred. Preferably, the polyacid curing agent is a carboxyl-terminated material having at least two carboxyl groups per molecule. Among the polyacid curing agents which may be used include carboxylic acid group-containing polymers such as acrylic polymers, polyesters, and polyurethanes; oligomers such as ester group-containing oligomers and monomers. Preferably, the polyacid curing agent has a Tg less than 30°C. Such low Tg materials enable the formation of high solids liquid compositions. Higher Tg materials require the use of more solvent. When the polyacid curing agent is an acrylic polymer, copolymers of (a) an ethylenically unsaturated monomer containing at least one carboxylic acid and (b) a different ethylenically unsaturated monomer which is free from carboxylic acid groups can be used. To be suitable herein, the acrylic polymer preferably has an acid number of 30 to 150, preferably 60 to 120. Examples of epoxy-reactive monomers (a) are acrylic acid, methacrylic acid, maleic acid and partial esters of maleic acid. The other monomeric component (b) is characterized by the group and may be styrene, alpha-substituted lower alkyl styrenes such as alpha-methylstyrene, alkyl esters of acrylic and methacrylic acids, especially the lower alkyl esters thereof, e.g. methyl methacrylate, methyl and ethyl acrylate, and mixtures of these materials. The relative amounts of monomers (a) and (b) in the copolymer may be varied but, in any event, the copolymer must comprise sufficient amounts of monomers (a) and (b) to give an acid number within the limits indicated heretofore. The acrylic copolymer may be prepared in conventional fashion, e.g. by heating monomers (a) and (b) at elevated temperatures, usually of the order of 90 to 140°C., preferably 115°C. to 125°C. This polymerization may be carried out in bulk or in solution using such conventional solvents as aromatic hydrocarbons, typically benzene, toluene and xylene, or alcohols (e.g. butyl alcohol or monoalkyl ethers of ethylene glycol). The polymerization is usually carried out in the presence of a polymerization catalyst, typically, peroxides such as benzoyl peroxide, di-tertiarybutyl-peroxide, di-cumene peroxide and methylethyl ketone peroxide, or other catalysts of the free-radical type. Preferably, the carboxylic acid group-containing acrylic polymer will have a relatively low molecular weight. These products are non-gelled and typically will have number average molecular weights as determined by gel permeation chromatography using a polystyrene standard of from 500 to 5000, preferably 700 to 3000. The preferred reaction products will also have a uniform molecular weight distribution which is evidenced by polydispersity values which are preferably less than 4, more preferably from 2 to 3. The polydispersity value is the ratio of the weight average molecular weight to the number average molecular weight each being determined by gel permeation chromatography using a polystyrene standard as described above. The acid functional acrylic polymer also provides sag control. The preferred clear film-forming compositions are high solids compositions and have a tendency to sag when applied to vertical surfaces. The acid functional acrylic polymer surprisingly provides sag control to the compositions. Preferably, the acid functional acrylic polymer is not the sole polyacid curing agent, in that it is difficult to formulate high solids compositions with the acid functional acrylic polymers. The acid functional acrylic polymer is preferably used with the other polyacid curing agent, preferably the half-ester mentioned below. Besides acid group-containing acrylic polymers, acid group-containing polyesters can be used as the polyacid curing agents. Such polyesters may be formed by reacting a polyol with a polycarboxylic acid or anhydride. With regard to the polyol-polycarboxylic acid or polycarboxylic acid anhydride, various polyols can be used including ethylene glycol, neopentyl glycol, glycerol, pentaerythritol and trimethylolpropane. Also, acid group-containing polyols such as dimethylolpropionic acid can be used. Various polycarboxylic acids may be employed including dicarboxylic acids such as phthalic acid, tetrahydrophthalic acid, hexahydrophthalic acid, maleic acid, itaconic acid, adipic acid and sebacic acid. Also anhydrides of the polycarboxylic acids where they exist can be used. The preparation of acid group-containing polyesters is well known in the art and usually involves preparation in organic solvent with sufficient acid group-containing ingredients to form an acid group-containing material at the completion of the reaction. A sufficient excess of the acid component is employed in forming the polymers to provide an acid value of from 10 to 120 with a preferred acid value being from 30 to 60. Besides acid group-containing polyesters, ester group-containing oligomers can be used. Examples include half-esters formed from reacting polyols and 1,2-acid anhydrides. The half-esters are preferred because they are of relatively low molecular weight and are quite reactive with epoxy functionality enabling the formulation of high solids fluid compositions while maintaining outstanding properties such as gloss and distinctness of image. The half-ester is obtained by reaction between a polyol and a 1,2-acid anhydride under conditions sufficient to ring open the anhydride forming the half-ester with substantially no polyesterification occurring. Such reaction products are of relatively low molecular weight with narrow molecular weight distributions and provide lower volatile organic contents in the coating composition while still providing for excellent properties in the resultant coating. By substantially no polyesterification occurring means that the carboxyl groups of the anhydride are not esterified by the polyol in a recurring manner. By this is meant that less than 10, preferably less than 5 percent by weight polyester is formed. Two reactions may occur in combining the anhydride and the polyol together under suitable reaction conditions. The desired reaction mode involves ring opening the anhydride ring with hydroxyl, i.e., where X is the residue of the polyol after reaction with the 1,2-dicarboxylic acid anhydride, R is an organic moiety associated with the anhydride and A is equal to at least 2. Subsequently, carboxyl groups formed by opening of the anhydride ring may react with hydroxyl groups to give off water via a condensation reaction. This latter reaction is not desired since it can lead to a polycondensation reaction resulting in products with higher molecular weights. To achieve the desired reaction, the 1,2-acid anhydride and polyol are contacted together usually by mixing the two ingredients together in a reaction vessel. Preferably, reaction is conducted in the presence of an inert atmosphere such as nitrogen and in the presence of a solvent to dissolve the solid ingredients and/or to lower the viscosity of the reaction mixture. Examples of suitable solvents are high boiling materials and include, for example, ketones such as methyl amyl ketone, diisobutyl ketone, methyl isobutyl ketone; aromatic hydrocarbons such as toluene and xylene; as well as other organic solvents such as dimethyl formamide and N-methyl-pyrrolidone. For the desired ring opening reaction and half-ester formation, a 1,2-dicarboxylic anhydride is used. Reaction of a polyol with a carboxylic acid instead of an anhydride would require esterification by condensation eliminating water which would have to be removed by distillation. Under these conditions this would promote undesired polyesterification. Also, the reaction temperature is preferably low, that is, no greater than 135°C., preferably less than 120°C., and usually within the range of 70-135°C., preferably 90-120°C. Temperatures greater than 135°C. are undesirable because they promote polyesterification, whereas temperatures less than 70°C. are undesirable because of sluggish reaction. The time of reaction can vary somewhat depending principally upon the temperature of reaction. Usually the reaction time will be from as low as 10 minutes to as high as 24 hours. The equivalent ratio of anhydride to hydroxy on the polyol is preferably at least 0.8:1 (the anhydride being considered monofunctional) to obtain maximum conversion to the desired half-ester. Ratios less than 0.8:1 can be used but such ratios result in increased formation of less preferred half-esters. Among the anhydrides which can be used in the formation of the desired polyesters are those which exclusive of the carbon atoms and the anhydride moiety contain from 2 to 30 carbon atoms. Examples include aliphatic, including cycloaliphatic, olefinic and cycloolefinic anhydrides and aromatic anhydrides. Substituted aliphatic and aromatic anhydrides are also included within the definition of aliphatic and aromatic provided the substituents do not adversely affect the reactivity of the anhydride or the properties of the resultant polyester. Examples of substituents would be chloro, alkyl and alkoxy. Examples of anhydrides include succinic anhydride, methylsuccinic anhydride, dodecenyl succinic anhydride, octadecenylsuccinic anhydride, phthalic anhydride, tetrahydrophthalic anhydride, methyltetrahydrophthalic anhydride, hexahydrophthalic anhydride, alkyl hexahydrophthalic anhydrides such as methylhexahydrophthalic anhydride, tetrachlorophthalic anhydride, endomethylene tetrahydrophthalic anhydride, chlorendic anhydride, itaconic anhydride, citraconic anhydride and maleic anhydride. Among the polyols which can be used are those which contain from 2 to 20 carbon atoms. Preferred are diols, triols and mixtures thereof. Examples include polyols containing from 2 to 10 carbon atoms. Examples include aliphatic polyols such as ethylene glycol, 1,2-propanediol, 1,3-propanediol, 1,4-butanediol, 1,5-pentanediol, glycerol, 1,2,3-butanetriol, 1,6-hexanediol, neopentyl glycol, diethylene glycol dipropylene glycol, 1,4-cyclohexanedimethanol, trimethylolpropane, 2,2,4-trimethylpentane-1,3-diol, pentaerythritol and 1,2,3,4-butanetetrol. Aromatic polyols such as bisphenol A and bis(hydroxymethyl) xylene can also be used. In addition to the acid group-containing polymers and oligomers mentioned above, monomers containing at least two acid groups can be used. Examples of suitable monomeric polycarboxylic acids are those containing from 5 to 20 carbon atoms and include open chain, cyclic, saturated, unsaturated and aromatic acids. Examples include succinic acid, adipic acid, azelaic acid, sebacic acid, hexahydrophthalic acid, maleic acid, cyclohexene-1,2-dicarboxylic acid and phthalic acid. The polyacid curing agent is present in the coating composition in amounts of 10 to 90, preferably 25 to 75 percent by weight based on total weight of resin solids. The polyepoxide-polyacid compositions also preferably contain an anhydride, preferably an anhydride which is a liquid at 25°C. The presence of such an anhydride in the compositions provides an improved cure response. Examples of suitable anhydrides include alkyl-substituted hexahydrophthalic anhydrides wherein the alkyl group contains up to 7 carbons, more preferably up to 4 carbons, such as methyl hexahydrophthalic anhydride and dodecenyl succinic anhydride. The amount of the anhydride which is used can vary from 0 to 40, preferably from 5 to 25 percent by weight based on total weight of resin solids. The equivalent ratio of carboxyl to epoxy in the clear film-forming compositions is preferably adjusted so that there are 0.3 to 3.0, preferably from 0.8 to 1.5 equivalents of carboxyl (anhydride being considered monofunctional) per equivalent of epoxy. Optionally, the crosslinkable composition can contain silane functionality which can be incorporated into the composition by using a reactive silane group-containing material such as gamma-methacryloxypropyltrimethoxysilane or mercaptopropyltrimethoxysilane which can be used in the preparation of the epoxy group-containing acrylic polymer. Such materials coreact with the polymerizing monomers or polymers forming a polymer with silane curing groups. Alternately, a silane group-containing material such as methyltrimethoxysilane can be included in the composition. The compositions will also preferably contain catalysts to accelerate the cure of the epoxy and acid groups. Examples of suitable catalysts are basic materials and include organic amines and quaternary ammonium compounds such as pyridine, piperidine, dimethylaniline, diethylenetriamine, tetramethylammonium chloride, tetramethylammonium acetate, tetramethylbenzylammonium acetate, tetrabutylammonium fluoride, and tetrabutylammonium bromide. The amount of catalyst is typically from 0 to 10, preferably 0.5 to 3 percent by weight based on resin solids. Also, optional ingredients such as auxiliary curing agents such as aminoplasts, plasticizers, antioxidants, and UV light absorbers can be included in the composition. These ingredients typically are present in amounts of up to 25 percent by weight based on total resin weight. The polyepoxide-polyacid compositions are liquid compositions and are preferably formulated into liquid high solids coating compositions. That is, these coating compositions contain greater than 40, preferably greater than 50 percent, most preferably greater than 60 percent by weight resin solids. The solids content is determined by heating the composition to 105-110°C. for 1 to 2 hours to drive off the volatile material. The clear top coat composition can be applied to the base-coated substrate by any of the conventional coating techniques such as brushing, spraying, dipping or flowing, but it is preferred that spray applications be used since this gives the best gloss. Any of the known spray techniques may be employed such as compressed air spraying, electrostatic spraying and either manual or automatic methods. After application of the top coat composition to the base coat, the coated substrate is heated to cure the coating layers. In the curing operation, solvents are driven off and the film-forming material of the top coat and/or of the base coat is crosslinked with the aid of any crosslinking agents present. The heating or curing operation is usually carried out at a temperature in the range of from 71-177°C. (160-350°F.) but if needed lower or higher temperatures may be used depending upon whether it is sufficient to activate any necessary crosslinking mechanisms. The thickness of the top coat is usually from 1.27 x 10⁻⁵ to 12.7 x 10⁻⁵ m (0.5 to 5), preferably 3.05 x 10⁻⁵ to 7.72 x 10⁻⁵ m (1.2 to 3 mils). The invention will be further described by reference to the following examples. Unless otherwise indicated, all parts are by weight. EXAMPLES The following examples (Examples A-H) show the preparation of epoxy-containing acrylic polymers, polyacid half-esters and acid-containing acrylic polymers. Example A An epoxy-containing acrylic polymer was prepared from the following mixture of ingredients: Ingredients Weight in Grams Percentage by Weight Glycidyl methacrylate 320.0 40 Methyl methacrylate 160.0 20 Butyl acrylate 160.0 20 Butyl methacrylate 160.0 20 VAZO-67 24.0 3.0 (on monomers) Tertiary-butyl perbenzoate 16.0 2.0 (on monomers) Tertiary-butyl perbenzoate (post-addition) 4.0 0.5 (on monomers) Tertiary-butyl perbenzoate (post-addition) 4.0 0.5 (on monomers) Xylene (415.3 grams) was charged to a suitable reactor and heated to reflux to remove water through a Dean-Stark trap. The glycidyl methacrylate, methyl methacrylate, butyl acrylate and butyl methacrylate were mixed together. The VAZO-67, first portion of tertiary-butyl perbenzoate and 100 grams of xylene were also premixed together. The premixture of vinyl monomers and the premixture of initiators were added simultaneously to the reaction vessel over a period of about 3 hours while maintaining the reaction temperature at reflux. At the completion of the addition, the reaction mixture was held at reflux for one hour followed by the addition of the second portion of tertiary-butyl perbenzoate and 25 grams of xylene. The reaction mixture was held for one hour at reflux followed by the addition of the third portion of tertiary-butyl perbenzoate and 25 grams of xylene. The reaction mixture was held for two hours at reflux followed by cooling to room temperature. The reaction mixture had a solids content of about 60 percent and a number average molecular weight of 1456 as determined by gel permeation chromatography using a polystyrene standard. Example B An epoxy-containing acrylic polymer containing silane functionality was prepared from the following mixture of ingredients: Kettle Charge Ingredients Parts by Weight (in grams) Xylene 480.0 Charge I Ingredients Parts by Weight (in grams) Percentage by Weight Glycidyl methacrylate 896.0 40.0 Methyl methacrylate 560.0 25.0 Butyl acrylate 448.0 20.0 Gamma-methacryloxypropyltrimethoxysilane 336.0 15.0 Charge II Ingredients Parts by Weight (in grams) Xylene 288.0 VAZO-67 112.0 Charge III Ingredients Parts by Weight (in grams) Xylene 144.0 Mercaptopropyltrimethoxysilane 112.0 Charge IV Ingredients Parts by Weight (in grams) Xylene 24.0 VAZO-67 8.96 Charge V Ingredients Parts by Weight (in grams) Xylene 24.0 VAZO-67 8.96 The kettle charge was heated to reflux in a suitable reactor to remove water through a Dean-Stark trap. Charges I, II and III were added simultaneously over the period of three hours while maintaining the reaction mixture at reflux. Charge IV was added and the reaction mixture held at reflux for one hour, followed by the addition of Charge V and holding the reaction mixture at reflux for one hour, followed by cooling to room temperature. The reaction mixture had a solids content determined at 150°C. of 67.7 percent and a number average molecular weight of 1435 as determined by gel permeation chromatography using a polystyrene standard. Example C An epoxy-containing acrylic polymer was prepared from the following mixture of ingredients: Kettle Charge Ingredients Parts by Weight Butyl acetate 906.0 Charge I Ingredients Parts by Weight (in grams) Percentage By Weight Glycidyl methacrylate 510.0 30 Methyl methacrylate 595.0 35 Butyl acrylate 170.0 10 Butyl methacrylate 425.0 25 Butyl acetate 200 Charge II Ingredients Parts by Weight (in grams) VAZO 67 59.5 Butyl acetate 180.0 Charge III Ingredients Parts by Weight (in grams) VAZO 67 8.5 Butyl acetate 40.0 The kettle charge was heated in a suitable reactor to reflux to remove water through a Dean-Stark trap. Charges I and II were added simultaneously over the period of about three hours while maintaining the reaction mixture at reflux. At the conclusion of the addition of Charges I and II, the reaction mixture was held for one hour at reflux followed by the addition of Charge III over a 30-minute period. The reaction mixture was held at reflux for an additional hour followed by cooling to room temperature. The volatile materials in the reaction mixture were then removed by heating under vacuum to a solids content of 99.8 percent. The reaction product had a number average molecular weight of 4048. Example D A polyacid half-ester of 1,6-hexanediol-methylhexahydrophthalic anhydride was prepared from the following mixture of ingredients: Ingredients Parts by Weight (in grams) 1,6-Hexanediol 590.0 Methylhexahydrophthalic anhydride 1680.0 Methyl isobutyl ketone 972.9 The 1,6-hexanediol and the methyl isobutyl ketone were charged to a reaction vessel and heated under a nitrogen atmosphere to 115°C. The methylhexahydrophthalic anhydride was charged over a 2-hour period while maintaining the reaction temperature between 112-117°C. The reaction mixture was held at this temperature for about 3 to 4 hours to a stalled acid value, i.e., acid value remained essentially constant. The reaction mixture was then cooled to room temperature and found to have a solids content measured at 110°C. of 68.0 percent and an acid value of 176. Example E A polyacid half-ester of trimethylolpropane and methylhexahydrophthalic anhydride was prepared from the following mixture of ingredients: Ingredients Parts by Weight (in grams) Trimethylolpropane 1341.0 Methylhexahydrophthalic anhydride 5040.0 Methyl isobutyl ketone 2734.7 The trimethylolpropane and the methyl isobutyl ketone were charged to a suitable reaction vessel and heated under a nitrogen atmosphere to 115°C. The methylhexahydrophthalic anhydride was charged over a 2-hour period while maintaining the temperature between 112-117°C. The reaction mixture was held at this temperature for about 3 hours. The reaction product was then cooled to room temperature and found to have a solids content measured at 110°C. of 69 percent and an acid value of 200.3. Example F An acid functional acrylic polymer was prepared from the following ingredients: Kettle Charge Ingredients Parts by Weight (in grams) Half-ester prepared as described in Example D 2571.3 Feed A Ingredients Parts by Weight (in grams) Percent 2-Ethylhexyl acrylate 2160 40 Styrene 1080 20 Methacrylic acid 1080 20 Butyl methacrylate 1053 19.5 Methyl methacrylate 27 0.5 Di-tertiary-butyl peroxide 54 1% based on monomers Feed B Ingredients Parts by Weight (in grams) Methyl isobutyl ketone 1800 The kettle charge was heated in a suitable reactor under a nitrogen atmosphere to reflux. Solvent was distilled and the reaction temperature increased to about 240°C. Feed A was added over a period of 30 minutes while maintaining the temperature between 187 and 200°C. At the completion of Feed A, the reaction mixture was held for 10 minutes at 189°C. Solvent was distilled until the reaction temperature reached 220°C. The reaction mixture was then cooled to 120°C. followed by thinning with Feed B. The reaction mixture was then cooled and found to have a solids content of 76.6 percent measured at 110°C., an acid value of 103.5 (theoretical 126) and a number average molecular weight of 840. Example G An acid functional acrylic polymer was prepared from the following ingredients: Kettle Charge Ingredients Parts by Weight (in grams) Butyl acetate 768.0 Charge I Ingredients Parts by Weight (in grams) Methyl methacrylate 864.0 Butyl acrylate 480.0 Isobutyl methacrylate 384.0 Acrylic acid 192.0 Charge II Ingredients Parts by Weight (in grams) Butyl acetate 448.0 VAZO-67 96.0 Charge III Ingredients Parts by Weight (in grams) Butyl acetate 32.0 VAZO-67 7.68 Charge IV Ingredients Parts by Weight (in grams) Butyl acetate 32.0 VAZO-67 7.68 The kettle charge was heated in a suitable reactor under a nitrogen atmosphere to reflux. Charges I and II were added continuously and simultaneously over a 2-hour period while maintaining the reaction mixture at reflux. Charge III was added and the reaction mixture held for one hour at reflux followed by the addition of Charge IV and holding the reaction mixture for 90 minutes at reflux. The reaction was then cooled and found to have a solids content of 59.3 percent (measured at 150°C.), an acid value of 47.95 and a number average molecular weight of 3214. Example H A polyacid half-ester was formed from reacting 2 moles of the 1,6-hexanediol-methylhexahydrophthalic anhydride half-ester of Example D with one mole of 3,4-epoxycyclohexylmethyl 3,4-epoxycyclohexanecarboxylate. The reaction product was prepared from the following mixture of ingredients: Ingredients Parts by Weight (grams) Polyacid half-ester of Example D (70% solids) 610.0 3,4-Epoxycyclohexylmethyl 3,4-epoxycyclohexanecarboxylate 205.0 Ethyltriphenyl phosphonium iodide 0.6 Methyl isobutyl ketone 88.1 The polyacid half-ester of Example D, ethyltriphenyl phosphonium iodide and the methyl isobutyl ketone were charged to a reaction vessel and heated under a nitrogen atmosphere to 125°C. The 3,4-epoxycyclohexylmethyl 3,4-epoxycyclohexanecarboxylate was added over a 2-hour period while keeping the reaction temperature at 125°C. The reaction mixture was held at 125°C. for 3 hours until an acid value of 74.4 was obtained. The reaction mixture was then cooled to room temperature. The following examples (1-12) show the preparation of various clear and pigmented film-forming compositions prepared with epoxy-containing acrylic polymers and various polyacid curing agents. The coating compositions were evaluated in color-plus-clear applications. Example 1 A clear film-forming composition was prepared by mixing together the following ingredients: Ingredients Parts by Weight (in grams) Resin Solids TINUVIN 328 3.0 3.0 Hexyl acetate 20.0 - Epoxy-containing acrylic polymer of Example A 103.8 60.2 1,6-Hexanediol-methylhexahydrophthalic anhydride half-ester of Example D 57.5 39.8 DC-200 10 C.S. (10% by weight in xylene) 1.0 0.1 ARMEEN DM 12D 2.0 2.0 The formulated coating composition contained 56 percent by weight resin solids and had a No. 4 Ford cup viscosity of 26.3 seconds. Example 2 A clear film-forming composition, similar to Example 1 but including methylhexahydrophthalic anhydride as a cure promoter, was prepared from the following mixture of ingredients: Ingredients Parts by Weight (in grams) Resin Solids TINUVIN 328 3.0 3.0 Hexyl acetate 20.0 - Epoxy-containing acrylic polymer of Example A 108.6 63.0 1,6-Hexanediol-methylhexahydrophthalic anhydride half-ester of Example D 31.4 21.7 DC-200 1.0 0.1 ARMEEN DM 12D 2.0 2.0 Methylhexahydrophthalic anhydride 15.3 15.3 The resultant coating composition contained 58 percent by weight resin solids and had a No. 4 Ford cup viscosity of 25 seconds. Example 3 A clear film-forming composition similar to Example 2 was prepared but with the trimethylolpropanemethylhexahydrophthalic anhydride half-ester of Example E and also including the diglycidyl ether of cyclohexanedimethanol. The coating composition was prepared from the following ingredients: Ingredients Parts by Weight (in grams) Resin Solids TINUVIN 328 3.0 3.0 Methyl ethyl ketone 14.8 - DC-200 1.0 0.1 Cyclohexanedimethanol diglycidyl ether 16.8 16.8 Methylhexahydrophthalic anhydridc 16.5 16.5 ARMEEN DM 12D 2.0 2.0 Epoxy-containing acrylic polymer of Example A 72.3 41.6 Trimethylolpropane-methylhexahydrophthalic anhydride half-ester of Example E 35.3 25.1 The resultant formulated coating composition contained 65 percent resin solids and had a No. 4 Ford cup viscosity of 18.1 seconds. Example 4 A clear film-forming composition similar to Example 3 but including the acid functional acrylic polymer of Example F was prepared from the following mixture of ingredients: Ingredients Parts by Weight (in grams) Resin Solids TINUVIN 328 3.0 3.0 Methyl ethyl ketone 17.7 - DC-200 1.0 0.1 Cyclohexanedimethanol diglycidyl ether 16.8 16.8 Methylhexahydrophthalic anhydride 16.5 16.5 ARMEEN DM 12D 2.0 2.0 Epoxy-containing acrylic polymer of Example A 64.5 37.4 Trimethylolpropane-methylhexahydrophthalic anhydride half-ester of Example E 21.6 14.7 Acid-containing acrylic polymer of Example F 18.6 14.5 The formulated coating composition contained 65 percent by weight resin solids and had a No. 4 Ford cup viscosity of 24.2 seconds. Example 5 A clear film-forming composition containing the silane group-containing, epoxy group-containing acrylic polymer of Example B and trimethylolpropane-methylhexahydrophthalic anhydride half-ester of Example E was prepared from the following ingredients: Ingredients Parts by Weight (in grams) Resin Solids TINUVIN 328 3.0 3.0 Xylene 16.7 - Hexyl acetate 10.0 - Silane and epoxy group-containing acrylic polymer of Example B 103.4 72.4 Trimethylolpropane-methylhexahydrophthalic anhydride half-ester of Example E 39.4 27.6 DC-200 1.0 0.1 Dibutyltin dilaurate 3.0 3.0 Tetrabutylammonium bromide (25% by weight in butanol) 30.0 7.5 Example 6 A pigmented base coat composition containing aluminum flake pigmentation, the epoxy-containing acrylic polymer of Example A and the 1,6-hexanediol-methylhexahydrophthalic anhydride half-ester of Example D was prepared from the following mixture of ingredients: Ingredients Parts by Weight (in grams) Resin Solids Pigment Solids TINUVIN 328 3.0 3.0 Hexyl acetate 60.9 - Flow control agent 45.4 20.0 Epoxy-containing acrylic polymer of Example A 81.4 47.2 1,6-Hexanediol-methylhexahydrophthalic anhydride half-ester of Example D 47.5 32.8 ARMEEN DM 12D 2.0 2.0 Aluminum flake 15.4 - 10.0 The ingredients were mixed in the order indicated at low shear with good agitation to form the pigmented base coating composition. The clear film-forming compositions of Examples 1-5 were applied to both the pigmented base coat of Example 6 and to a light blue metallic water-based base coat to form color-plus-clear composite coatings over steel substrates. The light blue metallic base coat was available from Imperial Chemical Industries Ltd. as M-979. This product was prepared in accordance with the teachings of U.S-A-4,403,003. The base coats were spray applied by hand to steel panels at a temperature of about 25°C. A 3-minute flash at 82°C. (180°F.) was allowed between coats for the water-base base coat. The solvent-base base coat was given a 90-second flash at ambient conditions. The total film thickness for the base coat of Example 6 was about 1.52 x 10⁻⁵ (0.6 mil) and for the water-base base coat about 7.62 x 10⁻⁶ m (0.3 mil). After application of the second base coat, two coats of the various clear coat compositions described in Examples 1-5 were spray applied with an automatic spraying device. The two coats were applied wet-on-wet to the basecoated panels with a 2-minute flash off at room temperature between the coats. After a final 2-minute flash off, the panels were then baked in both the horizontal and vertical positions (90° from horizontal unless otherwise indicated) at 121°C. (250°F.) for 30 minutes unless otherwise indicated. The properties of the composite coating are reported in the table below and are seen to have excellent gloss and distinctness of image. Example 7 A clear film-forming composition similar to Example 1 but containing the carboxylic acid group-containing acrylic polymer of Example G as a curing agent was prepared from the following mixture of ingredients: Ingredients Parts by Weight (in grams) Resin Solids Methyl ethyl ketone 10.0 - TINUVIN 328 3.0 3.0 TINUVIN 292 1.0 1.0 Hexyl acetate 100.0 - DC-200 1.0 0.1 Epoxy-containing acrylic polymer of Example A 58.8 34.1 Carboxylic acid-containing acrylic polymer of Example G 109.8 65.9 ARMEEN DM 12D 2.0 2.0 The formulated coating composition contained 37.1 percent by weight resin solids and had a No. 4 Ford cup viscosity of 21 seconds. Example 8 A clear film-forming composition similar to Example 1 but containing sebacic acid as a crosslinking agent was prepared from the following mixture of ingredients: Ingredients Parts by Weight (in grams) Resin Solids TINUVIN 328 3.0 3.0 TINUVIN 292 1.0 1.0 Hexyl acetate 15 - DC-200 1.0 0.1 Epoxy-containing acrylic polymer of Example A 135.7 78.7 Sebacic acid (10% by weight in ethanol) 213 21.3 ARMEEN DM 12D 2.0 2.0 The formulated coating composition contained 28.6 percent by weight resin solids and had a No. 4 Ford cup viscosity of 11.2 seconds. Example 9 A clear film-forming composition similar to Example 1 but containing the trimethylolpropane-methylhexahydrophthalic anhydride half-ester of Example E was prepared from the following ingredients: Ingredients Parts by Weight (in grams) Resin Solids TINUVIN 328 3.0 3.0 TINUVIN 292 1.0 1.0 Hexyl acetate 43.4 - DC-200 1.0 0.1 Epoxy-containing acrylic polymer of Example A 110.2 63.9 Trimethylolpropane-methylhexahydrophthalic anhydride half-ester of Example E 51.6 36.1 ARMEEN DM 12D 2.0 2.0 The formulated coating composition contained 50 percent by weight resin solids and had a No. 4 Ford cup viscosity of 23.0 seconds. Example 10 A clear film-forming composition similar to Example 9 but also containing an aminoplast was prepared from the following ingredients: Ingredients Parts by Weight (in grams) Resin Solids TINUVIN 328 3.0 3.0 TINUVIN 292 1.0 1.0 Hexyl acetate 50.8 - DC-200 1.0 0.1 Epoxy-containing acrylic polymer of Example A 88.1 51.1 Trimethylolpropane-methylhexahydrophthalic anhydride half-ester of Example E 41.3 28.9 CYMEL 325 25.0 20.0 ARMEEN DM 12D 2.0 2.0 The formulated coating composition contained 50 percent by weight resin solids and had a No. 4 Ford cup viscosity of 21.8 seconds. Comparative Example 11 A clear film-forming powder coating composition having a composition similar to that of Example 9 was prepared by mixing together the following ingredients: Ingredients Parts by Weight (in grams) TINUVIN 900 3.0 IRGANOX® 1010 1.0 Benzoin 0.5 FC-430 1.0 Trimethylolpropane-methylhexahydrophthalic anhydride half-ester of Example E 30.8 Epoxy-containing acrylic polymer of Example C 69.2 The ingredients mentioned above were blended together in a planetary mixer, extruded, chilled on a chill roll, flaked and ground into a fine powder in a micromill and then passed through a 0.15 mm (100-mesh) screen to form the final powder coating composition. Example 12 A clear film-forming composition was prepared with the epoxy-containing acrylic polymer of Example A, the 1,6-hexanediolmethylhexahydrophthalic anhydride half-ester of Example D and the half-ester of Example H (20 percent by weight based on weight of resin solids). The coating composition was prepared from the following ingredients: Ingredients Parts by Weight (grams) Percent Resin Solids TINUVIN 328 3.0 3.0 TINUVIN 292 1.0 1.0 Hexyl acetate 26.5 DC-200 1.0 0.1 Epoxy-containing acrylic polymer of Example A 96.9 56.2 Half-ester of Example D 33.4 23.4 Half-ester of Example H 29.1 20.4 ARMEEN DM 12D 2.0 2.0 Methyl isobutyl ketone 8.0 The formulated coating composition contained 53 percent resin solids and had a number 4 Ford cup viscosity of 20.2 seconds. The clear film-forming compositions of Examples 7-10 and 12 were applied to the pigmented base coat of Example 6 to form color-plus-clear composite coatings over steel substrates. The base coats and the clear coats were applied as generally described above in connection with Examples 1-6. The composite coating was then baked at 135°C., (275°F.) for 30 minutes to cure the coating. The powder coating composition of Example 11 was applied to the base coat of Example 6. The base coat was spray applied by hand to steel panels at a temperature of 25°C. Two coats were applied with a 90-second flash at ambient conditions between coats. The total film thickness was 1.52 x 10⁻⁵ m (0.6 mil). After application of the second base coat, two coats of the clear powder coating composition were electrostatically sprayed onto the base coat via a wet-on-wet application. The composite coating was then baked at 177°C. (350°F.) for 30 minutes. The properties of the composite coatings are reported in Table II below.

Claims: A process for applying a composite coating to a substrate by applying to the substrate a colored film forming composition to form a base coat and applying to said base coat a clear film-forming crosslinkable composition comprising a polyepoxide which is an epoxy group-containing acrylic polymer and a polyacid curing agent which is a half-ester formed from reacting a polyol and an acid anhydride to form a transparent top coat over the base coat and heating the coated substrate to cure the coating layers, characterized in that the clear film-forming composition is liquid and and the equivalent ratio of epoxy to carboxyl in the composition is from 1:0.3 to 1:3.0, such that a cured product results. The process of claim 1, in which the polyepoxide is a copolymer of a monoethylenically unsaturated monomer having at least one epoxy group and at least one monoethylenically unsaturated monomer which is free of epoxy groups. The process of claim 2, in which the polyepoxide has a Tg of less that 50°C. The process of claim 2, in which the copolymer has a number average molecular weight of between 1000 and 20000. The process of claim 1, in which the polyepoxide is an epoxy group-containing acrylic polymer which is present in the crosslinkable composition in amounts of 10 to 90 percent by weight based on total weight of resin solids. The process of claim 4, in which the crosslinkable composition contains a blend of epoxy group-containing acrylic polymer and low molecular weight polyepoxide which has a molecular weight less than 800. The process of claim 6, in which the low molecular weight polyepoxide is a polyglycidyl ether of a polyphenol The process of claim 1, in which the polyacid curing agent is a carboxyl-terminated material having at least two carboxyl groups per molecule. The process of claim 1, in which the polyacid curing agent is present in amounts of 10 to 90 percent by weight based on total weight of resin solids. The process claim 1, in which the crosslinkable composition has a resin solids content of at least 50 percent by weight. A crosslinkable film-forming coating composition comprising an epoxy group-containing acrylic polymer and a polyacid curing agent which is a half-ester formed from reacting a polyol and acid anhydride such that a cured product results characterized in that the crosslinkable film-forming coating composition is liquid, and the equivalent ratio of epoxy to carboxyl in the composition is from 1:0.3 to 1:3.0 The composition of claim 11, in which the epoxy group-containing acrylic polymer is a copolymer of glycidyl acrylate or methacrylate with at least one other polymerizable ethylenically unsaturated monomer. The compostion of claim 12, in which the epoxy group-containing acrylic polymer has a Tg of less than 50°C. The composition of claim 13, in which the epoxy group-containing acrylic polymer has a number average molecular weight of from 1000 to 20000. The composition of claim 11, in which the epoxy group-containing acrylic polymer is present in amounts of 10 to 90 percent by weight based on total weight of resin solids. The composition of claim 11, in which the half-ester is present in amounts of 10 to 90 percent by weight based on total weight of resin solids. The composition of claim 13, in which the composition contains a blend of epoxy group-containing acrylic polymer and low molecular weight polyepoxide which has a molecular weight of less than 800. The composition of claim 17, in which the low molecular weight polyepoxide is a polyglycidyl ether of a polyphenol.

Inventors: BLACKBURN WILLIAM PELHAM, DOWBENKO ROSTYSLAW, KANIA CHARLES MARTIN, SIMPSON DENNIS ALLAN, SINGER DEBRA LYNN, BLACKBURN, WILLIAM PELHAM, DOWBENKO, ROSTYSLAW, KANIA, CHARLES MARTIN, SIMPSON, DENNIS ALLAN, SINGER, DEBRA LYNN
Applicants: PPG INDUSTRIES INC, PPG INDUSTRIES, INC.
Application year: 1986
Main classification: B05D1
IPC codes: C08G59, B05D7, C08L33, C09D163, C09D133, B05D1