A PROCESS FOR PREPARING POLYUREA AND/OR POLYUREA-POLYURETHANE POLYMERS

Abstract: A process whereby an amine functional compound having an equivalent weight of at least about 400 is reacted with an excess of a polyisocyanate to form an isocyanate-terminated prepolymer or quasi prepolymer, which prepolymer or quasi prepolymer is reacted with an isocyanate-reactive material to form a polyurea and/or polyurea-polyurethane polymer. The amine functional compound and the polyisocyanate are employed in proportions such that the isocyanate-terminated prepolymer or quasi prepolymer has an isocyanate content of from 3 to 12 percent by weight.

Description: A PROCESS FOR PREPARING POLYUREA AND/OR POLYUREA-POLYURETHANE POLYMERS This invention relates to a process for preparing polyurea and/or polyurea-polyurethane polymers, particularly non-cellular or microcellular elastomeric and structural polyurea-containing polymers. Polyurethane polymers are well known and used to make a wide variety of elastomeric, structural and foamed articles ^ These polymers have been conventionally prepared by reacting a polyisocyanate with what is commonly referred to as a "polyol", i.e. a moderate to high equivalent weight polyhydroxyl-containing compound. The polyol provides "soft segments", i.e. flexible segments which provide good impact strength, elongation and other desirable properties to the polymer. Often, a "chain extender", i.e., a lower equivalent weight polyhydroxyl or polyamine containing compound, is also used to provide crosslinking or "hard segments" in the polymer. These chain extenders impart increased modulus and other desirable properties to the polyurethane. It has been discovered that,not only the mere presence of the hard and soft segments but the manner in which these respective segments are distributed throughout the polymer has great effect on its proper- ties. Generally, it has been found that certain proper¬ ties of the polymer are maximized when the hard and soft segments are well "segregated". Segregation of these domains refers to the presence at a microscopic or submicroscopic level of regions containing a high proportion of hard segments and other regions contain¬ ing a high proportion of soft segments. This desired phase segregation can be accom¬ plished in polyurethane polymers by sequentially reacting the polyisocyanate with all or part of the "polyol" prior to the subsequent reaction thereof with the chain extender and the remainder, if any, of the polyol. In this manner a soft segment prepolymer is formed prior to the formation of the final polymer. Such a technique is described, for example, in U.S. Patent No. 4,297,444. As an alternative, it is possible to employ a hard segment prepolymer by reacting the polyisocyanate sequentially with all or part of the chain extender and then with the polyol and any remaining chain extender. In a separate attempt to improve polyurethane polymers, the hydroxyl-terminated materials commonly employed to make the polymer have been replaced to a greater or lesser extent with amine functional compounds. See, for example, U.S. Patent Nos. 4,444,910 and 4,530,941. The amine functional material gives rise to urea linkages instead of urethane linkages in the polymer. Compared to the urethane linkages, these urea linkages are stronger and more thermally stable. Although these amine functional materials have the aforementioned advantages, several serious problems are presented by their use. Amines react so rapidly with isocyanate groups that their use is gen- erally restricted to reaction injection molding (RIM) processes. Even in RIM processes, it has been found generally necessary to employ sterically hindered amine chain extenders like diethyltoluenediamine (DETDA) in order to slow the polymerization reaction enough so that a molded article can be made. Further, amines are known to engage in a variety of secondary reactions with isocyanates at room temperature, causing undesir¬ able crosslinking and gel formation in polyurea-contain- ing polymers. It would be desirable to provide a polyurea polymer which is more easily processible. In addition, it is always beneficial to provide polymers having improved physical properties and processability. Accordingly, it would be desirable to provide a process for preparing polyurea containing polymers whi ' ch provides for greater processing flexibility and a product polymer having physical properties which are equivalent to or superior than those exhibited by conventionally prepared polyurea polymers. This invention is directed to a process for preparing a polyurea and/or polyurea-polyurethane poly¬ mer comprising reacting an amine functional compound having an equivalent weight of at least 400 with an excess of a polyisocyanate to form an isocyanate- -terminated prepolymer or quasi-prepolymer, and then reacting said isocyanate-terminated polymer or quasi- prepolymer with an isocyanate reactive material to form a polyurea and/or polyurea-polyurethane polymer, wherein the amine functional compound and the polyisocyanate are employed in proportions such that the isocyanate- -terminated prepolymer or quasi-prepolymer has an iso¬ cyanate content of from 3 to 12 percent by weight. Several unexpected advantages are obtained with the process of this invention. The reaction of the isocyanate-terminated prepolymer or quasi-prepolymer with an isocyanate reactive material proceeds unexpec¬ tedly slowly even when such isocyanate reactive material is a primary or secondary amine. This longer cure time permits much greater flexibility in the processing of polymers according to this invention. When glycols or relatively slow-reacting amines are used as the iso¬ cyanate-reactive material, it is usually possible even to hand mix and cast the reacting materials. Of course, the reaction mixture can be catalyzed to provide speedier cures as are often desired in RIM processing. In addition, the process of this invention often permits the use of highly reactive amines such as ethylene diamine and toluene diamine as the isocyanate reactive material. Such highly reactive amines are generally too reactive for use according to conventional processes, even in RIM systems. However, with this invention it is often possible to employ such amines to prepare molded articles, particularly via a RIM process. The polymer prepared according to this process also exhibits unexpected properties. Polymers prepared according to this invention generally exhibit a glass transition temperature which is 5 to 20°C lower than that exhibited by a similar polymer prepared according to a one-shot process. This advantage is especially evident when an aliphatic polyisocyanate is used. In addition, the heat distortion temperature of these poly¬ mers, as measured by a heat sag test, is usually sig- nificantly higher than conventionally prepared urea- -containing polymers of similar flexural modulus. Thus, this invention provides polymers which are use- able or processible over a wider temperature range than similar polymers prepared according to a one-shot process. According to this invention, an isocyanate- terminated prepolymer or quasi-prepolymer is reacted with an isocyanate reactive .material to form a urea- containing polymer. This polymer is preferably non- cellular or microcellular. The term "isocyanate-reactive material" as used herein refers to a compound or mixture thereof containing two or more hydrogen atoms which are active according to the Zerewitnoff test described by Kohler in the Journal of the American Chemical Society, Vol. 49, p. 3181 (1927). The isocyanate reactive material preferably comprises a low equivalent weight polyol or polyamine (sometimes referred to herein as a "chain extender" . ) The isocyanate-terminated polymer or quasi- prepolymer comprises a reaction product of an amine func¬ tional compound or mixture thereof and a stoichiometric excess of a polyisocyanate. The term "prepolymer" is used herein to indicate an isocyanate-terminated entity that is formed in the reaction of an amine-functional compound and a polyisocyanate. The term "quasi-prepoly¬ mer" is employed herein to indicate a prepolymer-contain- ing mixture which also contains unreacted polyisocyanate. A quasi-prepolymer can be prepared by reacting said amine-terminated compound with an amount of a poly¬ isocyanate greater than that needed to react with the amine groups thereon so that excess unreacted poly- isocyanate is present in the product. Alternatively, the quasi-prepolymer can be prepared by forming a prepolymer and then mixing it with additional poly¬ isocyanate. The terms "amine functional compound" or "amine functional material" as used herein refer to compounds or mixtures thereof which contain at least one amine group having an active hydrogen atom which is capable of reacting with an isocyanate group to form a urea. Said amine functional compound or material preferably contains an average of at least two such amine groups, or one such amine group and at least one other functional group containing an active hydrogen atom. The amine-functional compound also has an equi¬ valent weight of at least 400. For the purposes of this invention the equivalent weight of the amine functional compound or material is based on the number of amine groups (or other groups containing active hydrogen atoms) as opposed to the number of hydrogen atoms. For example, a 2000 molecular weight compound containing two primary amine groups is considered herein to have an equivalent weight of 1000. Preferred are primary or secondary amine- terminated polyethers having an equivalent weight of from 400 to 6000 preferably from 500 to 3000 and con- taining an average of from 1 to 4 amine groups per mol¬ ecule. Suitable such amine-terminated polyethers and methods of their preparation are described, for example, in U.S. Patent Nos. 3,654,376 and 3,666,788, Generally, the processes described in these patents comprise reacting a hydroxyl-terminated polyether with hydrogen and ammonia or a primary amine in the presence of certain catalysts to reductively aminate the polyether. The production of primary amine terminated polyethers is particularly described in U.S. Patent No. 3,654,376. Commercially available primary amine-ter- minated polyethers include Jeffamine T-5000, Jeffamine D-2000 and Jeffamine D-400, all available from the Texaco Chemical Company. Jeffamine is a Trademark of the Texaco Chemical Company. The preparation of secondary amine-terminated polyethers is particularly described in U.S. Patent Nos. 4,152,353, 4,153,581, and 3,666,788. Generally, polyether polyols which have been capped with an ali¬ phatic primary amine, especially a C x to C δ aliphatic amine, and aromatic amine capped materials, especially aniline-capped polyethers, are preferred. In most of the foregoing processes, the amination of the polyether preceeds less than quanti¬ tatively. Accordingly, the product will contain com¬ pounds having only one amine group per molecule and some residual hydroxyl groups. The use of such mater¬ ials is suitable in this invention provided that of the combined number of hydroxyl groups and amine groups, at least 25 percent, preferably at least 50 percent, and more preferably from 50 to 100 percent thereof are amine groups. In addition, mixtures of aminated materials and hydroxyl-terminated materials are suitable herein when at least 25 percent by number of the combined number of amine and hydroxyl groups are amine groups. Other secondary amine-terminated polyethers are advantageously prepared by reacting a primary amine-terminated polyether as described hereinbefore with an unsaturated compound such as an acrylic ester, methacrylic ester, acrylonitrile or other compound containing a carbon-carbon double bond which is suf- ficiently reactive to undergo a Michael addition reac¬ tion with a primary amine terminated polyether. Reac¬ tion products of acrylonitrile and C ^ -Cg alkyl or hydroxyalkyl esters of acrylic or methacrylic acid with a primary amine-terminated polyether are of par- ticular significance herein. In addition, a secondary amine-terminated polyether formed by reacting the corresponding primary amine-terminated polyether with an adduct of formaldehyde and hydrogen cyanide is also useful herein. The reactions described in this para- graph are advantageously conducted by heating the reactants in the presence of a suitable diluent such as a lower alcohol. Suitable reaction conditions are described in U.S. Patent No. 3,666,788. In addition to the foregoing, it is also within the scope,of this invention to employ as the amine-functional-compound a primary or secondary amine terminated material which is-complexed with an acid, acid halide or alkyl chloride, bromide or iodide. Of particular interest are primary or secondary amine terminated polyethers which are complexed with an organic acid halide such as benzoyl chloride or acetyl chloride, a phosphorus acid, a halogen acid, or a C 1 ~C 4 alkyl iodide. The amine-functional compound is reacted with an excess of a polyisocyanate to form an isocyanate- terminated prepolymer or quasi-prepolymer. Aromatic polyisocyanates, i.e. those in which the isocyanate groups are attached directly to aromatic rings, as well as aliphatic isocyanates are useful herein. Typical aromatic polyisocyanates useful herein include phenyl diispcyanate, 2,6-toluene diiso- cyanate, 2,4-toluene diisocyanate, ditoluene diisocy- anate, naphthalene 1,5-diisocyanate, bis(4-isocyanato- phenyl)methane (MDI), bis(3-methyl 2-isocyanato phenyl)- methane, bis(3-methyl 4-isocyanatophenyl)methane, bis(3,5-diisopropyl-4-amino phenyl)methane, 4,4'-di- phenylpropylidene diisocyanate, 4,4'-diphenyl ethane diisocyanate and diverse polymethylene polyphenyl polyisocyanates. Of these, toluene diisocyanate, bis(4-isocyanatophenyl)methane (MDI) and polymethylene polyphenyl polyisocyanates are preferred on the basis of ready availability and generally superior perform- ance. The polymethylene polyphenyl polyisocyanates typically employed herein are those that have an average functionality of from 2.1 to 3.5 and contain 20 to 100 weight percent methylene diphenyldiisocyanate iso ers with the remainder being polymethylene polyphenyl polyisocyanates of higher molecular weight. These isocyanate mixtures are commercially available mater¬ ials and can be prepared by the process -described in U.S. Patent No. 3,362,679. Suitable organic aliphatic polyisocyanates include, in addition to the halogenated derivatives of the above mentioned organic aromatic polyisocyanates, 1,6-hexamethylene diisocyanate, isophorone diisocyanate, 1,4-cyclohexyl diisocyanate, l,4-bis(isocyanatomethyl)- cyclohexane methylene bis(4-cyclohexylisocyanate) or mixtures thereof. The reaction of the polyisocyanate and the amine containing material can be conducted neat or in a suitable solvent. Due to the great reactivity of the amine functional compound it tends to form polymers of significant molecular weight upon contact with the polyisocyanate. Such higher molecular weight materials are often insoluble in the unreacted polyisocyanate and form precipates which hinder processing. The formation of higher molecular weight materials also causes the prepolymer or quasi-prepolymer to have a broad molecular weight distribution which also may adversely affect the properties of the product polymer. Conditions for the prepolymer-forming reaction are therefore advantageously selected such that the formation of these higher molecular weight materials are minimized. The formation of higher molecular weight materials can generally be minimized by conducting the reaction in ' such a manner that the formation of high local concentrations of the amine-functional compound in the polyisocyanate is minimized. This is readily accomplished, for example, by gradually adding the amine-functional material to the polyisocyanate under conditions of agitation. Alternatively, particularly when a more highly reactive polyisocyanate and amine functional material are used, the reaction can be conducted in a suitable solvent. Generally, the prepolymer-forming reaction is conducted at moderate temperatures, i.e. from -10 to 100°C, preferably from 15 to 55°C. Lower temperatures, i.e. from -10 to 30° have an added benefit of slowing the reaction so as to inhibit the formation of high molecular weight materials, and are sometimes preferred for that reason. However, at higher temperatures, the reduced viscosity of the amine-containing material permits more rapid intermixing of the component, which also tends to reduce the formation of high molecular weight materials. Obviously, at higher temperatures, it is sometimes difficult to control the formation of high molecular weight materials. The reaction is conducted until substantially all the amine groups on the amine-functional compound have reacted with the polyisocyanate. Due to the reactivity of the amine-functional compounds this reaction is completed almost instantaneously in most cases. When a blend of the amine functional material and a polyol are employed to prepare the prepolymer, a somewhat larger reaction period may be required, i.e. 5 minutes to two hours. It is often desirable to store the prepolymer for an extended period (i.e. several hours to several months) before using it to prepare a polymer. In such cases, it is desirable to prepare a prepolymer which is stable, i.e. does not engage in substantial amount of secondary reactions during storage. Such stability is conventionally measured by determining the -NCO contact of the prepolymer over an interval of time. A decrease in the -NCO content of less than 2 percent by weight of the prepolymer generally indicates adequate stability. o - 1 2 - Generally, the stability of the polyurea isocyanate-terminated prepolymer or quasi-prepolymer depends somewhat on its composition, and more parti¬ cularly on the particular polyisocyanate used and the degree of amination of the amine-functional compound. Generally, stability is favored by the use of less reactive polyisocyanates and the use of amine func¬ tional compounds which are less than quantitively aminated. In addition, secondary amine-terminated amine functional compounds and those amine functional materials which are complexed with acids, acid halides or other halides as described hereinbefore, generally form more stable prepolymers than do primary amine terminated materials. Secondary amine-terminated polyethers which are prepared by reacting the cor¬ responding primary amine with an unsaturated compound in a Michael addition reaction form particularly stable prepolymers, even with highly reactive polyisocyanates. Aliphatic polyisocyanates readily form stable prepolymers with primary amine terminated compounds hav¬ ing a degree of amination up to 100 percent. When reacted with a secondary amine terminated compound, particularly stable prepolymers are formed at all degrees of amination. Aromatic polyisocyanates of moderate reactivity, or which have at least one moderately reactive isocyanate group and one or more highly reactive" isocyanate groups, such as 2,4-toluene diisocyanate and 2,- '-methylene diphenyl diisocyanate, generally from stable prepolymers with primary amine terminated compounds having a-degree of amination of from 25 to 90 percent, preferably 25 to 75 percent, more preferably from 25 to 50 percent. When reacted with an arylamine-terminated material, these polyisocyanates typically form a stable pre¬ polymer when the degree of amination is from 25 to 100 percent and preferably 25 to 75 percent. When an alkylamine-terminated material is used to prepare prepolymers with these compounds it is advantageous that it have a degree of amination of 25 to 80 percent, preferably from 25 to 65 percent. A moderately reac¬ tive isocyanate group is for the purpose of this inven- tion, one which has a reactivity intermediate to that of an aliphatic polyisocyanate, which is less reactive, and MDI, which is a highly reactive polyisocyanate. Highly reactive polyisocyanates such as as methylene diphenyl diisocyanate and polymeric deriva- tives thereof typically form stable prepolymers with primary amine terminated compounds having a degree of amination of from 25 to 85 percent, preferably from 25 to 50 percent, and with secondary amine-terminated materials having a degree of amination of from 25 to 100 percent, preferably from 25 to 70 percent, more preferably from 40 to 70 percent. The prepolymer or quasi prepolymer is reacted with at least one isocyanate-reactive material to form a polymer which is preferably non-cellular or microcel- lular. A polymer is considered to be non-cellular or microcellular if it has a density (unfilled) of at least 0.8 g/cc. Preferably, the polymer has a density of at least about 0.9 g/cc, more preferably from 0.95 to 1.2 g/cc (unfilled). The isocyanate-reactive material useful herein includes those compounds containing a plurality - 1. - of moieties containing hydrogen atoms which are active according to the Zerewitnoff test described by Kohler in the Journal of the Americal Chemical Society, Vol. 49, page 3181 (1927). Exemplary such moieties include mercaptan, hydroxyl, primary and secondary amine, and acid groups. Preferred are amine and hydroxyl-contain¬ ing compounds. Suitable isocyanate-reactive compounds include relatively low equivalent weight compounds, relatively high equivalent compounds and mixtures thereof. The relatively low equivalent weight compounds prefer¬ ably have equivalent weights of less than 200, more preferably from 30 to 150. The conditions of the polymerization reaction depend somewhat on the composition of the isocyanate reactive material and the prepolymer or quasi-prepolymer employed in the reaction mixture. When a relatively reactive isocyanate group is present in the prepolymer or quasi prepolymer, or when particularly reactive isocyanate-reactive materials are used, it is desirable to employ reaction conditions which promote rapid mixing and slow reaction of the components. In such instances, it is preferred to mix and react the com¬ ponents at a temperature from -10 to 40°C in the presence of little or no catalyst and using a mechan- ical mixing apparatus which can rapidly mix the com¬ ponents and transfer the mixture into a mold. Prefer¬ ably, RIM type equipment is employed. Once the material is transferred into a mold, greater temperatures can be used to complete the curing reaction. Whfcn the prepolymer or quasi-prepolymer contains less reactive isocyanate groups and/or the isocyanate reactive material is relatively less reac¬ tive, greater flexibility in reaction conditions is possible. In these cases the reactants can be con¬ tacted at ambient to elevated temperatures, i.e. from -10 to 100°C, can be catalyzed if desired and can be either hand or machine mixed. A speedier reaction as is desirable for RIM processing is readily accomplished with the addition of catalyst or the use of higher reaction temperatures, i.e. from 30 to 100°C. Suitable low equivalent weight hydroxyl-con- taining chain extenders include for example, ethylene glycol, propylene glycol, tri ethylol propane, 1,4 butane diol, diethylene glycol, dipropylene glycol, bisphenols, hydroquinone, catechol, resorsinol, tri- ethylene glycol, tetraethylene glycol, glycerine, low molecular weight ethylene- and/or propylene oxide derivaties of glycerine, ethylene diamine, diethylene triamine, and mixtures thereof. Suitable low equivalent weight aliphatic amine-containing compounds include, for example, ethylenediamine, 1,3-diamino propane, 1,4 diaminobutane, isophorone diamine, diethylene triamine, ethanolamine, aminoeth lethanolamine, diaminocyclohexane, hexamethyl- enediamine, aminoethyl piperazine, bis(a inopropyl) piperazine, 1,2-diamino cyclohexane, poly(oxyalkylene) amines, bis (p-aminocyclohexyl) methane, triethylene tetraamine, and mixtures, thereof- Particularly suitable are aminated polyoxypropylene glycols having an average equivalent weight of 60. to 110, although these materials are usually employed in, conjunction with another amine or glycol chain extender. .Suitable low equivalent weight aromatic amines which can be employed herein include for example, 2,4-bis (p-aminobenzyl) aniline, 2,4-diamino- toluene, 2,6-diaminotoluene, 1,3-phenylenediamine, 1,4-phenylenediamine, 2,4'-diaminodiphenyl methane, 4,4'-diaminodiphenyl methane, naphthalene 1,5-diamine, 1 methyl-2-methylamino 4-amino benzene, polyphenyl polymethylene polyamines, 1,3-diethyl 2,4-diaminobenzene, l-methyl-3,5-diethyl-2,6-diamino benzene, 1,3,5- triethyl 2,6-diamino benzene, and mixtures thereof. Those of the aforementioned aromatic amines which are substituted in each position ortho to an amino group are signifi¬ cantly stearically hindered and react much more slowly than those aromatic amines which are unsubstituted in one or more of the positions ortho to the amine groups. Suitable relatively high equivalent weight compounds, include, for example, a polyether polyol, polyester polyol, the so-called polymer or copolymer polyols, hydroxyl-terminated acetal resins, poly- hydroxyl containing phosphorous compounds and amine- terminated polyethers. Most preferred are those polyols or amine-terminated polyethers having an equivalent weight from 400 to 5000 and an average functionality from 2 to 4, especially from 2 to 3. In addition to the foregoing components, it is often desirable to incorporate various other ingre¬ dients into the reaction mixture. It has already been mentioned that a catalyst for the polymerization reaction may be employed in certain circumstances. Suitable such catalysts commonly include tertiary amines and organo- etal compounds. The organometallic catalyst is suitably a lead, mercury or stannous compound such as, for example, a stannous carboxylate, a trialkyl tin oxide, a dialkyl tin dihalide, or a dialkyl tin oxide wherein the organic groups of the organic portion of the tin compound or hydrocarbon groups contain from 1 to 8 carbon atoms. For example, dibutyltin dilaurate, dibutyltin diacetate, diethyltin diacetate, stannous octoate, di (2-ethylhexyl) tin oxide, stannous oleate or mixtures thereof may be used. Tertiary amine cata- lysts include trialkyl amines, heterocyclic amines such as alkyl orpholines, 1,4 dimethylpiperazine, triethylene diamine, and aliphatic polyamines such as N^N'N 1 tetra- methy1 1,3-butanediamine. Blowing agents may also be employed herein to form a cellular polymer. However, the formation of a cellular polymer is not preferred. Blowing agent can be used, however, to slightly expend the polymer to form a microcellular structure, as long as the polymer has a density of at least 0.8 g/cc. Suitable blowing agents include low boiling halogenated hydrocarbons such as trichloromonofluoromethane and methylene chloride, carbon dioxide, nitrogen, water or other known materials which volatilize or otherwise form a gas under the conditions of the polymerization reaction. Other conventional formulation ingredients may also be employed such as, for example, . stabilizers, extenders, inert fillers, such as glass fibers, carbon fibers or pigments. Internal mold release agents such as disclosed in European Patent Publication 119,471 and in the International Publication Number WO 86/01215 are also suitable for use herein. The polymer prepared according to this inven¬ tion is useful as a static or dynamic elastomer, such as employed, for example in preparing fascia for auto¬ mobile bumpers, or as a foamed cushion, as are used in automobile dashboards and headrests. The following examples are provided to illus¬ trate the invention but are not intended to limit the scope thereof. All parts and percentages are by weight unless otherwise indicated. Example 1 To a resin kettle equipped with a stirrer, heating lamp and nitrogen atmosphere are added 16.9 g. of hexamethylene diisocyanate (HMDI). The HMDI is heated to 40°C. With stirring, 50 g (0.05 moles) of an aminated polyoxypropylene diol containing 50 percent primary amine groups, 37 percent methyamine groups, 10 percent dimethyl amine groups and 3 percent hydroxyl groups are added over a period of 2 hours. The aminated diol is prepared accordingly by reacting methyl amine with the diol in a tube reactor according to the general process described in U.S. Patent No. 4,152,353. The weight ratio of methyl amine to diol is 0.35. The reaction is conducted at a temperature of 265°C and a pressure of 1100 psi (7.58 MPa) and hydrogen is fed to the reactor at a rate of..2 cubic feet/hour (0.057 m 3 /hour). As the amine is added, the viscosity of the reaction mixture is seen to increase, indicating pre¬ polymer formation. Following the addition of amine, a clear colorless viscous- liquid.-is obtained. A pre- polymer having a -NCO content of 8.9 percent is obtained. This prepolymer is reacted at a 1.05 index with diethyl- toluenediamine (DETDA) by hand mixing the components and pouring the reacting mixture onto a mold which is preheated to 300°F (149°C). The gel time for this reaction is 30 seconds. The polymer is cured at 300°F (149°C) for 60 minutes. The resulting elastomer has a glass transition temperature of -55°C, compared to an expected value of -40°C. Example 2 In a suitable flask, 99 grams of hexamethyl- ene diisocyanate are placed under a nitrogen atmosphere. To the flask are added, dropwise under constant agita¬ tion, 300 grams of an aminated polyoxypropylene diol as described in Example 1. A prepolymer having an -NCO content of 9.25 percent is obtained. After storing overnight, 209 g of the pre- polymer and 41 g of DETDA are reacted by degassing the prepolymer, adding the DETDA and again degassing at room temperature, and pouring the mixture onto a mold which is preheated to 100°F (37.8°C). The molding is cured at 300°F (149°C) for 30 minutes at 10,000 psi (68.95 MPa) pressure. The properties of the resulting molding are: flexural modulus - 11,900 psi (82.05 MPa); tensile strength - 1,180 psi (8.14 MPa), die "C" tear strength - 405 pounds per linear inch (70.9 KN/m) elongation - 163 percent; heat sag (325°F (163°F) for 30 minutes with 4" (102 mm) overhang) - 0.16'i(4.1 mm); T = -55°C. Example 3 Following the general procedure described in Example 2, 16.65 g of 4,4'-methylene diphenyl diiso- cyanate (MDI) and 23.3 g of an aminated 2000 molecular weight polyoxypropylene glycol are reacted to form a prepolymer having an -NCO content of 10.1 percent. The aminated material is prepared by reacting aniline with a 2000 molecular weight polyol according to the general process described in U.S. Patent No. 4,152,353. The reaction is conducted using 0.9 parts by weight of aniline per part polyol. The temperature is about 205°C and the pressure is 600 psi (4.14 MPa). Hydrogen is fed to the reactor at the rate of 10 cubic feet/hour (78.7 cm 3 /sec). The resulting aminated polyol contains 40 percent primary amine, 39 percent saturated secondary amino terminal group, 4 percent aniline groups and about 11 percent residual ^ hydroxyl groups. About 20.6 g of this prepolymer are reacted with 4.41 g of DETDA by hand mixing the components to form a castable elastomer. The resulting polymer has a glass transition temperature of -53°C. Example 4 A prepolymer is prepared as described in Example 3 using 14.6 g of toluene diisocyanate and 35.4 g of the aminated material of Example 3. A prepolymer having an -NCO content of 9.23 percent is obtained. Twenty grams of this prepolymer are reacted with 3.82 g DETDA as described in Example 2. The resulting polymer has a glass transition temperature of -46°C. Example 5 According to the method described in Example 3, 36.7 g of a 2000 molecular weight isopropy1amine- terminated polyoxypropylene glycol and 13.3 g of hexa- methylene diisocyanate are reacted to form a prepolymer having an -NCO content of 9.5 percent. This prepolymer is reacted with DETDA at a 100 index by hand stirring the components at room temperature, and pouring the mixture onto a mold (12" x 7" x 1/8") (305 mm x 178 mm x 3.2 mm) heated at 100°F (37.8 β C). The mold is then cured for 30 minutes at 300°F (149°C) and 10,000 psi (68.95 MPa). The tensile strength at the resulting molding is 2409 psi (16.61 MPa). Elongation is 503 percent, flex- ural modulus is 32,400 psi (223.4 MPa), die "C" tear strength is 401 pounds per linear inch (70.2 KN/m), and glass transition temperature is -56°C. The molding sags 0.2" (5.1 mm) in 30 minutes at 325°F (163°C) with a 6" (152 mm) overhang. Example 6 A primary amine-terminated polyoxypropylene triol sold commercially as Jeffamine T-5000 is reacted with acrylonitrile to form a derivative containing terminal mono(cyanoethyl) amine groups. This deriva¬ tive is added dropwise at room temperature to MDI in proportiqns sufficient to yield a 12 percent -NCO prepolymer. The resulting prepolymer is reacted with 1,4 butane diol according to the general procedure described in Example 2 at a 1.05 index to yield an elastomer having a tensile strength of 1270 psi (8.76 MPa), a flexural modulus of 22,600 psi (155.82 MPa), an elongation of 310 percent a die "C" tear strength of 390 p.l.i. (68.3 KN/m) and a heat sag at 250°F (121°C) for 60 minutes with a 4" (102 mm) overhang of 0.15 inches (3.8 mm). Examples 7, 8, 9 and 10 and Comparative Run A A series of polyurea-polyurethane elastomers is prepared in dimethylaceti ide solution by prereact- ing MDI with an animated polyether to form a 12 percent -NCO prepolymer, and chain extending with 1,4-butanediol. Each polymer is precipitated in methanol and dried under vacuum. The thermal properties of each sample are tested by annealing the polymer at 120°C for five minutes in the chamber of a differential scanning calorimeter (DSC), and then conducting a DSC scan to determine the glass transition temperature (T ) of the hard segment and soft segment of each polymer. The ' aminated polyether used in each sample, and the hard and soft segment T are as indicated in Table I- fol¬ lowing. All aminated polyethers are prepared from a 2000 molecular weight polyoxypropylene diol. Table I Example or Comparative Glass Transition Temp, (τ s ^ Run 8 Aminated Polyether Soft Segment Hard Segment 7 - HCH 2 CH 2 CN capped -40 200, 210, 228 8 cyclohexyl amine cappιeedd -47 201 9 isopropylamine capped [ -46 197 10 ethylamine capped -41 197 A hydroxyl terminated -35 190 (control) The soft segment T defines the lower end of tl-a useful temperature range for the polymer. The hard segment T defines the upper end. As can be " seen from the data i;j Table I, each of the polymers prepared according to this invention has both a lower soft segment T and a higher hard segment T . In a practical application, such as an automobile bumper, the lower soft segment T means that the bumper will remain flexible, and not become brittle, at colder temper¬ atures than the control. Further, the higher hard segment T indicates that the polymer will better withstand a hot environment such as is encountered with in-line baked-cure painting procedures.

Claims: 1. A process for preparing a polyurea or polyurea-polyurethane polymer comprising reacting an amine functional compound having an equivalent weight of at least 400 with an excess of a polyisocyanate to form an isocyanate-terminated prepolymer or quasi-pre¬ polymer, and then reacting said isocyanate-terminated prepolymer- or quasi-prepolymer with an isocyanate reactive material to form a polyurea and/or polyurea- polyurethane polymer, wherein the amine functional compound and the polyisocyanate are employed in pro¬ portions such that the isocyanate-terminated prepolymer or quasi-prepolymer has an isocyanate content of from 3 to 12 percent by weight. 2. The process of Claim 1 wherein said amine functional compound has an average equivalent weight of from 400 to 6000 and contains from 1 to 4 amine groups per molecule. 3. The process of Claim 2 wherein the amine-functional compound is an amine-terminated poly- ether. 4. The process of Claim 3 wherein at least 25 percent of the combined number of hydroxyl groups and amine groups of the amine functional compound are amine groups. 5. The process of Claim 4 wherein the polyisocyanate is an aliphatic polyisocyanate or an aromatic polyisocianate. 6. The process of Claim 5 wherein the polyisocyanate is an aromatic polyisocyanate containing at least one moderately reactive isocyanate group, and the amine functional compound is a primary amine ter¬ minated compound having a degree of amination of the amine functional compound of from 25 to 90 percent. 7. The process of Claim 5 wherein the polyisocyanate is an aromatic polyisocyanate containing highly reactive isocyanate groups and the amine-func¬ tional compound is a primary amine terminated compound having a degree of amination of from 25 to 85 percent. 8. The process of Claim 1 wherein the isocyanate reactive material is an amine or hydroxyl- -containing compound having an equivalent weight of less than 200. 9. The process of Claim 1 wherein the isocyanate reactive material is a polyol or amine- terminated polyether. having an equivalent weight from 400 to 5000 and a functionality from 2 to 3. 10. The process of Claim 3 wherein said amine functional material is a Michael reaction product of a primary amine terminated polyether and an unsatur- ated compound containing a carbon-carbon double bond.

Inventors: BUSHMAN KIMBLEY ANN, GONZALES MANUEL JR, PEFFLEY RICHARD D, PLEPYS RAYMOND A, PRIESTER RALPH D, TURNER ROBERT B, BUSHMAN, KIMBLEY, ANN, GONZALES, MANUEL, JR., PEFFLEY, RICHARD, D., PLEPYS, RAYMOND, A., PRIESTER, RALPH, D., TURNER, ROBERT, B.
Applicants: DOW CHEMICAL CO, THE DOW CHEMICAL COMPANY
Application year: 1986
Main classification: C08G18
IPC codes: C08G18