CEMENTING BOREHOLES USING SALT-CONTAINING CEMENT COMPOSITIONS

Abstract: A method of cementing a conduit in a borehole penetrat­ ing an earthen formation, by introducing a salt-tolerant cem­ enting composition into the space between said conduit and said formation, wherein the cementing composition com­ prises cement and: (a) water containing in excess of about 10% salt by weight of the water, and (b) a fluid loss additive comprising an admixture of: (i) at least one member selected from carboxymethyl­ hydroxyethylcellulose and copolymers or copolymer salts of N,N-dimethylacrylamide and 2-acrylamido-2-methylpropane sulfonic acid or acid salts thereof, having a mole ratio from about 1:4 to about 4:1 and a molecular weight such that a 0.1% aqueous solution of said copolymer has a Brookfield viscosity reading at 5 rpm of the U.L. Adapter Spindle in the range of about 30 to about 250 centipoise (.03 to .25 Pa s), present in an amount of from about 0.1% to about 1.0% by weight of dry cement: and (ii) a copolymer or copolymer salt of acrylic acid and 2-­ acrylamido-2-methylpropane sulfonic acid or acid salt thereof, having a mole ratio of from about 1:5 to about 5:1 and a molecular weight such that a 10% aqueous solution of said copolymer has a Brookfield viscosity reading at 20 rpm of the U.L. Adapter Spindle in the range of about 5 to about 50 cent­ ipoise (.005 to .05 Pa s), present in an amount of from about 0.1% to about 3.0% by weight of dry cement.

Description: The present invention relates to a method of cementing boreholes using salt-containing cement compositions, and is especially concerned with reducing fluid loss during cementing operations. Certain polymer compositions have long been recognized as cement additives useful for reducing fluid loss from a slurry of cement and water. These compositions are commonly referred to as "fluid loss additives". An example of a fluid loss additive for use in an acidizing or fracturing composition is found in U.S. patent specification no. 4,107,057. In this U.S. patent, a copolymer of a sulfonic-acid modified acrylamide and a polyvinyl cross-linking agent is employed. In the oil well cementing art, a variety of polymers have been disclosed as useful fluid loss additives for hydraulic oil well cements. For example, U.S. patent specification no. 4,015,991 discloses a fluid loss additive for a hydraulic cement slurry, consisting of hydrolyzed copolymers of acrylamide (AA) and 2-acrylamido-2-methylpropane sulfonic acid (AMPS). However, these AA/AMPS copolymers are useful only in operations where the bottom hole circulating temperature (BHCT) ranges from 90° to 125°F (32 to 52°C), whereas BHCT ranges encountered in such operations are often outside such a range. Still further, these copolymers have a salt tolerance of only up to about 10%. The temperature limitation of the AA/AMPS copolymers, that is their loss of usefulness above about 125°F (52°C) BHCT, is believed to be the result of hydrolysis of the amide groups The carboxylate groups formed by such hydrolysis convert the copolymers to materials which function to retard the setting of the cement and to reduce the compressive strength of the set cement. Further, in the lower portion of the above-mentioned temperature range, i.e. between 90° and 100°F (32 to 38°C), the AA/AMPS is less effective as a fluid loss additive, requiring inclusion of larger amounts of such additive than at higher temperatures. The inclusion of a sufficiently large amount of additive to create an acceptable fluid loss composition often creates viscosity and pumpability problems; since the addition of the copolymer directly affects the resultant slurry rheology. Copolymers of acrylamide and AMPS exhibit high viscosity and poor mixability, resulting in cement slurries having poor pumpability characteristics during cementing operations. Mixability is a subjective term used to describe how well the components in the cement composition wet and mix with each other, as well as the energy required to create a generally homogeneous slurry. Industry desires a fluid loss additive that has as little effect on compressive strength, set time, viscosity and thickening time as possible; is salt tolerable, that is, does not exhibit substantial loss of effectiveness in the presence of salt; and is chemically stable during cementing operations. Further, such desired fluid loss additive should be compatible with as many other additives and environmental conditions as possible, should be soluble in cement slurries at normal ambient temperatures encountered in oil well cementing operations, as well as continue to provide fluid loss characteristics over broad temperature and cement pH ranges. U.S. patent no. 4,515,635 (EP-A-0 157 055) discloses the use of copolymere of N,N-dimethylacrylamide (NNDMA) and AMPS having monomer ratios of NNDMA to AMPS oF 1:4 to 4:1 and selected molecular weights as fluid loss additives for cement compositions. As illustrated in the patent, however, the copolymer fails to provide desired levels of fluid loss control even at relatively high concentrations to cements containing substantial salt concentrations. It would be desirable to provide additives for use in reducing fluid loss in cement compositions containing substantial salt concentrations where the bottom hole circulating temperatures may range from 100°F (38°C) to in excess of 400°F (204°C) without adversely affecting thickening time, compressive strength or other properties of the cement composition. We have now found some fluid loss additives which are especially useful in high salt concentration cements. One compound used in the method according to the invention, is a copolymer salt from NNDMA and AMPS which is part of a cementing composition which is the subject-matter of our European patent application 86301087.2 published as EP-A-0 192 447. According to the present invention, there is provided a method of cementing a conduit in a borehole penetrating an earthen formation, by introducing a salt-tolerant cementing composition into the space between said conduit and said formation, wherein the cementing composition comprises cement and: a) water containing in excess of about 10% salt by weight of the water, and b) a fluid loss additive comprising an admixture of: (i) at least one member selected from carboxymethylhydroxyethylcellulose and copolymers or copolymer salts of N,N-dimethylacrylamide and 2-acrylamido-2-methylpropane sulfonic acid or acid salts thereof, having a mole ratio from 1:4 to 4:1 and a molecular weight such that a 0.1% aqueous solution of said copolymer has a Brookfield viscosity reading at 5 rpm of the U.L. Adapter Spindle in the range of 30 to 250 centipoise (.03 to .25 Pa s), present in an amount of from 0.1% to 1.0% by weight of dry cement; and (ii) a copolymer or copolymer salt of acrylic acid and 2-acrylamido-2-methylpropane sulfonic acid or acid salt thereof, having a mole ratio of from 1:5 to 5:1 and a molecular weight such that a 10% aqueous solution of said copolymer, has a Brookfield viscosity reading at 20 rpm of the U.L. Adapter Spindle in the range of 5 to 50 centipoise (.005 to .05 Pa s), present in an amount of from 0.1% to 3.0% by weight of dry cement. The cementing compositions are comprised of water, hydraulic cement salt in excess of about 10% by weight of water, and admixtures of at least one member selected from the group consisting of carboxymethylhydroxyethylcellulose (CMHEC) and selected copolymers or salts of copolymers of N,N-dimethylacrylamide (NNDMA) and 2-acrylamido-2-methylpropane sulfonic acid (AMPS) together with copolymers and salts of copolymers of acrylic acid and AMPS. The copolymers or salts of the copolymers of NNDMA/AMPS have a monomer molar ratio of between 4:1 and 1:4 and average molecular weight such that a 0.1% aqueous solution of said copolymers has a Brookfield viscosity reading at 5 rpm of the U.L. Adapter Spindle in the range between about 30 and about 250 centipoise (.03 and .25 Pa s). Preferably, the monomer molar ratio is about 1:1.5. The copolymers or salts of copolymers of acrylic acid/AMPS have a monomer molar ratio of between 5:1 to 1:5 and average molecular weights such that a 10% aqueous solution of said copolymers has a Brookfield viscosity reading at 20 rpm of the U.L. Adapter Spindle in the range between 5 and 50 centipoise (.005 and .05 Pa s). Preferably, the monomer molar ratio is in the range of from about 5:1 to about 1:1. The copolymers and salts of the copolymers used in the present invention are relatively stable to hydrolysis over a wide range of temperature and pH. Such copolymers and salts of the copolymers may be admixed in solid form with any dry hydraulic oil field cement or may be added at the time the cement slurry is being prepared, either to the mixing water or to the slurry. Most preferably, the Brookfield viscosity reading is between 130 and 200 centipoise (.13 and .20 Pa s) for the NNDMA/AMPS copolymers and between 10 and 20 centipoise (.01 and .02 Pa s) for the acrylic acid/AMPS copolymers. Numerous salts of the copolymers can be used, the preferred salts being made by neutralization of the acid form of the AMPS monomer or the copolymers with an alkaline agent such as a source of sodium, calcium, magnesium or ammonium ions. Such alkaline agents can comprise, for example, sodium hydroxide, calcium hydroxide, ammonia or magnesium hydroxide. Although the amount of copolymers present generally may be varied, the CMHEC or NNDMA/AMPS copolymers generally are admixed with the cementing composition in an amount of from 0.1 to 1.0 percent by weight of dry cement. Preferably, the compounds are admixed with the cement in an amount of from 0.25 to 0.75 percent and, most preferably, from 0.25 to 0.5 percent by weight of dry cement. The acrylic acid/AMPS copolymers are admixed with the cementing composition in an amount of from 0.1 to 3.0 percent by weight of dry cement. Preferably, the acrylic acid/AMPS copolymers are admixed with the cement in an amount of from 0.25 to 2.5 percent and, most preferably, from 0.25 to 2.0 percent by weight of dry cement. The amount of each polymer admixed in the fluid loss additive will depend upon the amount of salt present, the temperature level to be experienced, rheological considerations, the average molecular weight of the copolymers and other additives present. It also should be understood that larger proportionate amounts of the copolymers may be utilized, but such quantities are unnecessary to achieve the desired fluid loss control. The individual constituents of the fluid loss additives of the present invention generally are effective at reducing fluid loss in non-salt containing cementing compositions. The behavior of the various constituents of the additives, however, in salt-containing cementing compositions are very much different. The constituents of the fluid loss additives of the present invention are generally ineffective individually at reducing fluid loss even at high concentrations from salt-containing cementing compositions. However, they demonstrate a surprising ability in combination to substantially reduce fluid loss from the salt-containing cement compositions. Such reduction in fluid loss from the cement compositions is substantially in excess of any additive effect which the various compounds comprising the fluid loss additive may experience even when utilized at substantially greater individual concentration levels when admixed with cement and as such is totally unexpected. The fluid loss additives of the present invention are effective in reducing fluid loss from cementing compositions containing in excess of about 10% salt by weight of water. The fluid loss additives are particularly effective at reducing fluid loss at elevated temperatures, that is, generally above 125°F (52°C) from cementing compositions containing in excess of 15% salt by weight of water up to the saturated salt concentration level. The salt-tolerant cementing compositions of the present invention are useful in oil, gas and water well cementing operations since such compositions have reduced fluid loss to the surrounding formation. Such compositions are used to cement a conduit penetrating a permeable earthen formation via introducing such composition into the space between such conduit and such formation and allowing the composition to harden. The copolymers and copolymer salts used in the present invention may be manufactured in accordance with various well know free-radical techniques. However, in the present invention new solution polymerization techniques were employed to obtain polymer solutions of NNDMA and AMPS containing 10% by weighs of solids. The mole ratios of the NNDMA and AMPS monomers are variable, but for the purposes of this invention should not vary in ratio amounts greater than 4 to 1 in either direction. Those copolymers which are useful in the present invention are disclosed in U.S. Patent No. 4,515,635. The salts of the various copolymers may be produced in accordance with the various well known techniques. The salt may be formed, for example, by reaction of an alkaline agent with either the AMPS monomer before polymerization or the NNDMA/AMPS copolymer or acrylic acid/AMPS copolymer. The salt may be formed with any alkaline agent which does not adversely react with the monomers of the copolymer or the other constituents present in the cementing composition. Surprisingly, it has been found that the fluid-loss additive composition utilized in the method of the present invention provides fluid-loss control to the salt-containing cement slurry while also providing enhanced dispersant properties. The enhanced properties are found to occur when the acrylic acid/AMPS copolymer has an average molecular weight below about 10,000. Preferably, the acrylic acid/AMPS copolymers of the present invention will have an average molecular weight in the range of from 5000 to 9000 and, most preferably, from 6000 to 8000. To illustrate the unique benefits of the method of the present invention, the following Examples are given by way of illustration only. Example I A number of materials were tested as potential fluid loss additives for cements containing substantial salt concentrations, including NNDMA/AMPS copolymers, acrylic acid/AMPS copolymers and carboxymethylhydroxyethylcellulose. These tests ware performed at 180°F (82°C) using cement slurries comprising Class H cement, 35% silica flour by weight of dry cement, 45% graded particle size hematite by weight of dry cement and 47% water by weight of dry cement. Sufficient sodium chloride was admixed with the cement composition to form a saturated solution. The various additives identified in the following Table I then were mixed with samples of the cement slurries. The additive containing cement slurries were mixed in an atmospheric consistometer which was preheated to test temperature and stirred for twenty minutes. The atmospheric consistometer is a non-pressurized device that simulates a cementing pumping process via movement of the consistometer can about a paddle. Temperature can be varied but pressure is atmospheric. Fluid loss was measured at 1000 psi (6.89 MPa) through a 325 mesh screen in cm³/30 min. The foregoing test procedure is more fully outlined in API Spec 10, 1st Ed., Jan. 1982, entitled "API Specification for Materials and Testing for Well Cements". The results of these fluid loss tests are provided in Table I. The Table I test results indicate that certain admixtures of copolymers are effective fluid loss additives under static 180°F (82°C) temperature conditions. The data clearly illustrate the lack of effectiveness of the various individual constituents of the fluid loss additive of the present invention when employed in cementing compositions containing in excess of 10% salt by weight of dry cement. The data also illustrates the effectiveness of the fluid loss additive of the present invention in providing fluid loss control of less than about 100 cm³/30 minutes in comparison to other combinations of the constituents outside the ranges described by Applicant. It should be noted that as the amount of the various copolymer additives are increased, the rheology of the slurry also increased. From an operations standpoint, slurries having a rheology measured above about 12-15 Bearden units of consistency on the atmospheric consistometer become less desirable and increasingly less desirable as that number increases. Example II The test procedure of Example I is repeated utilizing an acrylic acid/AMPS copolymer having a molar ratio of 4:1. The results of the test are set forth in Table II, below: The data of Tables I and II clearly illustrates the operability of the method of the present invention utilizing acrylic acid/AMPS copolymers having varying molar ratios. Example III To illustrate the effectiveness of the composition of the present invention in comparison to a known acrylamide/AMPS copolymer utilized as a fluid-loss additive, the following tests were performed. The tests were performed at 180°F (82°C) using cement slurries comprising Class H cement, 35% silica flour by weight of dry cement, 15% graded particle size hematite by weight of dry cement and 47% water by weight of dry cement. Sufficient sodium chloride was admixed with the cement composition to form a saturated solution. The various additives identified in the following Table III then were mixed with samples of the cement slurries and tested as described in Example I together with 0.25% carboxymethylhydroxyethylcellulose by weight of dry cement. The results of the fluid loss tests are set forth in Table III, below. The data clearly illustrate the benefits of utilizing the method of the present invention in cement slurries containing significant concentrations of salt. Surprisingly, it has been found that when the bottom hole circulating temperature of the well to be cemented is in excess of about 300°F (149°C) and, even more particularly above 350°F (177°C), that the acrylic acid/AMPS copolymer of the fluid-loss additive of the present invention, when utilized at a concentration in excess of about 2 percent by weight of cement, can provide improved fluid-loss control to a cement composition containing salt in excess of about 10% by weight of the mixing water. More particularly, the acrylic acid/AMPS copolymer having an average molecular weight below 10,000 and, preferably, an average molecular weight in the range of from about 5,000 to about 9,000, and, most preferably, 6,000 to about 8,000, and a molar ratio in the range of from about 1:5 to 5:1 and, preferably, from about 5:1 to about 1:1 when present in an amount of from about 2 percent to about 4 percent by weight of dry cement can provide significantly improved fluid-loss control to a cement slurry containing salt in an amount in excess of 10% by weight of the mixing water when emplaced in a formation having a temperature above 300°F (149°C) without adversely affecting cement setting. It is to be understood that larger quantities of the acrylic acid/AMPS copolymer may be utilized, however, the larger quantities generally do not improve the effectiveness of the copolymer as a fluid-loss control additive. The acrylic acid/AMPS copolymer of the present invention is particularly effective at reducing fluid loss from cement compositions which are saturated with salt which are emplaced in formations at temperatures in excess of about 300°F (149°C). While that which previously is considered to be the preferred embodiment of the invention has been described, it is to be understood that variations and modifications which will become apparent to those individuals skilled in the art can be made in this invention without departing from the scope of the claims.

Claims: A method of cementing a conduit in a borehole penetrating an earthen formation, by introducing a salt-tolerant cementing composition into the space between said conduit and said formation, wherein the cementing composition comprises cement and: (a) water containing in excess of about 10% salt by weight of the water, and (b) a fluid loss additive comprising an admixture of: (i) at least one member selected from carboxymethylhydroxyethylcellulose and copolymers or copolymer salts of N,N-dimethylacrylamide and 2-acrylamido-2-methylpropane sulfonic acid or acid salts thereof, having a mole ratio from 1:4 to 4:1 and a molecular weight such that a 0.1% aqueous solution of said copolymer has a Brookfield viscosity reading at 5 rpm of the U.L. Adapter Spindle in the range of 30 to 250 centipoise (.03 to .25 Pa s), present in an amount of from 0.1% to 1.0% by weight of dry cement; and (ii) a copolymer or copolymer salt of acrylic acid and 2-acrylamido-2-methylpropane sulfonic acid or acid salt thereof, having a mole ratio of from 1:5 to 5:1 and a molecular weight such that a 10% aqueous solution of said copolymer has a Brookfield viscosity reading at 20 rpm of the U.L. Adapter Spindle in the range of 5 to 50 centipoise (.005 to .05 Pa s), present in an amount of from 0.1% to 3.0% by weight of dry cement. A method according to claim 1, wherein the N,N-dimethylacrylamide/2-acrylamido-2-methylpropane sulfonic acid copolymer has a Brookfield viscosity reading of from 130 to 200 centipoise (.13 to .20 Pa s). A method according to claim 1 or 2, wherein said water contains in excess of 15% salt by weight of the water. A method according to claim 1,2 or 3, wherein the mole ratio of N,N-dimethylacrylamide to 2-acrylamido-2-methylpropane sulfonic acid in said copolymer is about 1:1.5. A method according to any of claims 1 to 4, wherein said copolymer salts are formed by reaction of the polymer units individually or as a copolymer, with an alkaline agent capable of producing a salt containing ions of at least one of sodium, calcium, magnesium and ammonium. A method according to any of claims 1 to 5, wherein the Brookfield viscosity of said acrylic acid/2-acrylamido-2-methylpropane sulfonic acid copolymer is in the range of 10 to 20 centipoise (.01 to .02 Pa s). A method according to any of claims 1 to 6, wherein the mole ratio of acrylic acid to 2-acrylamido-2-methylpropane sulfonic acid is in the range of 5:1 to 1:1. A method according to any of claims 1 to 7, wherein said copolymer of N,N-dimethylacrylamide/2-acrylamido-2-methylpropane sulfonic acid is present in an amount of from 0.25% to 0.75% by weight of the dry cement. A method according to any of claims 1 to 8, wherein said copolymer of acrylic acid/2-acrylamido-2-methylpropane sulfonic acid is present in an amount of from 0.25% to 2.5% by weight of the dry cement.

Inventors: BROTHERS, LANCE EVERETT
Applicants: HALLIBURTON COMPANY
Application year: 1986
Main classification: E21B33
IPC codes: C04B28, C04B24, C09K8