MULTI-BED HYDRODEWAXING PROCESS

Abstract: Catalytic dewaxing of hydrocarbon oils is effected with intermediate hydrotreating. A continuous multi-bed technique employs alternating beds of dewaxing and hydrogenation catalysts to improve process performance, whereby partially dewaxed effluent is treated to remove olefins produced during dewaxing and decrease dewaxing catalyst aging.

Description: This invention relates to a process for dewaxing hyrdro­ carbon oils. In particular, it relates to catalytic hydrodewaxing of petroleum oils to produce low pour point distillate and lubricating oil stocks. Dewaxing is often required when paraffinic oils are to be used in products which need to have good fluid properties at low temperatures e.g. lubricating oils, heating oils, jet fuels. The higher molecular weight straight chain normal and slightly branched paraffins which are present in oils of this kind are waxes which are the cause of high pour points in the oils. If adequately low pour points are to be obtained, these waxes must be wholly or partly removed. In the past, various solvent removal techniques were used e.g. propane dewaxing, MEK dewaxing; but, the decrease in demand for petroleum waxes, together with the increased demand for gasoline and distillate fuels, has made it desirable to find economic processes which convert waxy components into other materials of higher value. Catalytic dewaxing processes can achieve this by selectively cracking the longer chain paraffins, to produce lower molecular weight products which may be removed by distillation. Processes of this kind are described, for example, in The Oil and Gas Journal, January 6, 1975; pages 69 to 73 an U.S. Patent No. 3,668,113. It is also known to produce a high quality lube base stock oil by subjecting a waxy crude oil fraction to solvent refining, followed by catalytic hydrodewaxing (HDW) over ZSM-5, with subsequent hydrotreating (HDT) of the lube base stock, as taught in U.S. Patent 4,181,598. In order to obtain the desired selectivity, the catalyst has usually been a zeolite having a pore size which admits the straight chain n-paraffins either alone or with only slightly branched chain paraffins, but which generally excludes more highly branched materials, cycloaliphatics and heavy aromatics. Shape-selective zeolites such as ZSM-5, ZSM-11, ZSM-12, ZSM-23, ZSM-35 and ZSM-38 have been proposed for this purpose in dewaxing processes and their use is described in U.S. Patent Nos. 3,894,938; 4,176,050; 4,181,598; 4,222,855; 4,229,282, 4,247,388, 4,257,872, 4,313,817, 4,436,614, and 4,490,242. A dewaxing process employing synthetic offretite is described in U.S. Patent No. 4,259,174. A hydrocracking process employing zeolite beta as the acidic component is described in U.S. Patent No. 3,923,641. Dewaxing processes of this kind function by cracking waxy components to form lower molecular weight materials, including olefins and other unsaturated compounds which contribute to deactivation of the catalyst. Cracking products, especially lower olefins, tend to further degrade to form carbonaceous deposits on the catalyst. Coking deactivates the catalyst requiring the process temperature to be raised in order to achieve the desired degree of conversion. As the aging of the catalyst has resulted in the process temperature increasing to an upper limit, the production process is interrupted to permit periodic oxidative regeneration of the catalyst. Frequent shutdown of the production unit for catalyst regeneration can render the dewaxing process less economic. Prior work has established the value of metal-exchanged and/or impregnated zeolites, especially acidic Ni-ZSM-5 zeolite, as a hydrodewaxing catalyst. Pd-exchanged ZSM-5 has a lower aging rate than other Group VIII metals, but this requires extra catalyst processing beyond that of the economic standard zeolites employed in commercial HDW processes. It has also been proposed to admix a hydrogenation catalyst, such as palladium on alumina, with a standard HDW catalyst; however, this poses problems in catalyst loading and regeneration techniques. Density differences between the two catalysts make mixed loading difficult. It is an object of the present invention to improve the catalytic hydrodewaxing process by extending the useful production cycle. This can be achieved by the discovery that staged conversion in a multi-bed dewaxing reactor system with an intermediate catalytic hydrotreating zone operatively connected between alternating beds of dewaxing catalyst can improve performance, resulting in improved aging characteristics. Accordingly, the present invention provides a process for catalytic hydrodewaxing of waxy, heavy hydrocarbon feedstock characterized by partially dewaxing the feedstock by contacting the feedstock at conventional dewaxing conditions with a first catalyst bed comprising a conventional dewaxing catalyst of a crystalline zeolite with a constraint index of 1 to 12 in the presence of hydrogen, to produce a partially dewaxed effluent containing olefins, subsequently cascading the partially dewaxed effluent from the first bed through at least one separate hydrogenation catalyst bed under conventional hydrotreating conditions to saturate olefinic reaction products of the dewaxing step, further catalytically dewaxing the hydrotreated feedstock at conventional dewaxing conditions in contact with conventional dewaxing catalyst in at least one additional catalytic dewaxing step, to produce a dewaxed feedstock and further hydrogenating the dewaxed feedstock in an additional hydrotreating step. Figure 1 is a vertical cross-section view of a cylindrical reactor vessel showing the disposition of catalyst, flow streams and major equipment schematically; Figure 2 is a graphic plot of process variables vs. time on stream, showing catalyst aging. Figure 3 is a plot of reactor temperature vs. C₃-C₄ olefin content for the alternating layer bed HDW-HDT process. In the embodiment depicted in the drawing a vertical downflow reactor vessel 10 is fabricated as a cylindrical shell having a plurality of stacked serially-connected catalytic zones 12, 14, 16, 18. Each of these operating zones includes support means 12A, 14A, 16A, 18A for retaining a fixed bed of solid catalyst particles. Feedstock and H₂-containing reactant gas may be introduced at conversion conditions at elevated temperature and pressure though top feed inlet 20, which may include a distributor (not shown) for applying the fluid phases across the top of a first solid catalyst bed in zone 12. In a preferred embodiment, the catalyst bed for the hydrodewaxing (HDW) zone is a medium pore crystalline zeolite, such as acidic nickel ZSM-5 or the like. A typical supported catalyst bed may be 1-5 mm extrudate zeolite/alumina on a porous bed of larger inert particles (i.e. ceramic balls) 12B, through which reaction products are withdrawn via plenum 22. The partially treated effluent from the first catalyst zone 12 cascades into the second hydrotreating (HDT) zone 14. The effluent way be cooled by injecting additional cold gas (e.g. H₂) via heat exchanger 24 and coaxial inlet 26 which extends vertically through the reactor shell top into the plenum space 22. The cold fluid quenches at least a portion of the hot first stage effluent to the desired hydrotreating temperature. Optionally, the liquid phase may be separately collected and withdrawn via conduit 28, passed through heat exchanger 30 and redistributed over the second catalyst bed 14 by sprayheader 32 or similar liquid distributor. Liquid distribution may be used in any of the beds, if desired. The partially converted first zone effluent is then treated in contact with a second catalyst, such as hydrogenation catalyst supported in intermediate bed 14. Hydrotreated effluent from the second reactor zone is then combined in the second plenum 34 with hot hydrogen from a bottom coaxial inlet 36 to raise the cascaded effluent to a higher temperature in the subsequent HDW zone 16. Optionally, supplemental heat can be supplied by contacting the reactants with heating tube 40, which may have a heat exchange fluid flowing therethrough. Heat exchanger tubes may be employed in the other zones, if desired. Various techniques are known for controlling reaction temperature for exothermic and endothermic conversions. Tubular reactors may be employed to maintain isothermal conditions by thermal conduction through the reactor walls. Following further conversion in the final HDW zone, the hot effluent from zone 16 is cooled by quench hydrogen via inlet 42 in a manner similar to the handling of the first zone effluent. The catalytically dewaxed and hydrotreated product is recovered from the reactor via bottom plenum 44 and outlet conduit 46. In addition to the above-described reactor system, other reaction equipment and operating techniques are disclosed in U.S. patents 3,498,755 (Borre), and 3,894,937 (Bonacci et al). The hydrodewaxing catalysts preferred for use herein include the crystalline aluminosilicate zeolites having a silica to alumina ratio of at least 12, a constraint index of about 1 to 12 and acid cracking activity (alpha) of 10 to 200, preferably about 50 to 100. Representative of the ZSM-5 type zeolites are ZSM-5, ZSM-11, ZSM-12, ZSM-23, ZSM-35 and ZSM-38. ZSM-5 is disclosed in U.S. Patent No. 3,702,886 and U.S. Patent No. Re. 29,948; ZSM-11 is disclosed in U.S. Patent No. 3,709,979. Also, see U.S. Patent No. 3,832,449 for ZSM-12; U.S. Patent No. 4,076,842 for ZSM-23; U.S. Patent No. 4,016,245 for ZSM-35 and U.S. Patent No. 4,046,839 for ZSM-38. A suitable shape selective medium pore HDW catalyst for fixed bed is Ni-exchanged HZSM-5 zeolite with alumina binder in the form of cylindrical extrudates of about 1-5mm. Other pentasil catalysts which may be used in one or more reactor stages include a variety of medium pore (5 to 9A) siliceous materials, such as borosilicates, ferrosilicates, and/or gallo-silicates. The hydrotreating catalysts employed are typically metals or metal oxides of Group VIB and/or Group VIII deposited on a solid porous support such as silica and/or metal oxides such as alumina, titania, zirconia or mixtures thereof. Representative Group VIB metals include molybdenum, chromium and tungsten and Group VIII metals include nickel, cobalt, palladium and platinum. These metal components are deposited, in the form of metals or metal oxides, on the indicated supports in amounts generally between about 0.1 and about 20 weight percent. The multiple catalyst bed cascade process of this invention is conducted at a pressure within the approximate range of 800 to 20,000 kPa (100 to 3000 psig). The temperature is generally within the approximate range of 200 to 450°C, with an increasing temperature gradient, as the feed passes initially through individually adiabatic beds of hydrotreating catalyst and hydrodewaxing catalyst. Suitably, the temperature of the HDT beds will be within the range of 200 to 450°C and the HDW beds will be about 250°C to 400°C. The feed is conducted through the catalyst beds at an overall space velocity between about 0.1 and 10 parts by weight of feed hourly flow per weight of active catalyst, and preferably between 0.2 and 2 WHSV, along with hydrogen present in the various zones in an amount between about 2 and 25 moles of hydrogen per mole of hydrocarbon. Initial hydrotreating of the hydrocarbon feed prior to the first HDW bed serves to convert heteroatom-hydrocarbon compounds to gaseous products and converts some hydrocarbons to lighter fractions. The effluent from the initial hydrotreating zone can be cascaded directly to the first HDW stage, or the effluent may be topped by flashing or fractionating to remove the light by-products (low boiling hydrocarbons, H₂S, NH₃, etc.). In order to demonstrate the inventive concept, a series of experimental runs is conducted for dewaxing a heavy neutral gas oil (Arab light crude oil stock) by a conventional HDW process and the alternating HDW-HDT technique of this invention. The dewaxing catalyst is a steamed Ni-containing ZSM-5 having a silica-alumina mole ratio of 70:1 and an acid cracking activity (alpha-value) of 98. This catalyst is composited with alumina (35%) to form an extrudate (about 1.5mm diameter). The process is conducted in a tubular reactor under substantially isothermal conditions by heat exchange with the walls of a thermally conductive tube 2.2 cm I.D. (7/8 inch). The HDT catalyst is a standard Pd/Al₂O₃ catalyst available as a 3 mm extrudate (Engelhard Industries). The palladium loading is about 0.5 wt%. The tubular reactor is prepared by sulfiding the HDW catalyst at about 230 to 345°C with 2% H₂S in H₂ at 2900 kPa. After reaching steady state continuous flow conditions at about 200°C, the charge stock is introduced at about 1.6 WHSV (based on Ni-ZSM-5) with hydrogen reactant (445 nM³/M³) and the reactor temperature is initially increased to 290°C to meet a desired pour point of about -6°C. Thereafter the reactor temperature is adjusted incrementally to maintain the pour point desired. The alternating layers of HDW catalyst and HDT catalyst are loaded by uniformly mixed the Pd or NiZSM-5 extrudates with 80/120 mesh silica sand at a volume ratio of about 3:1. The alternating layers are retained by mesh screens at opposing ends and comprise 4 HDT layers between 5 alternating HDW layers, with the total weight of the HDW and HDT catalysts being equal. Figure 2 shows the start-of-cycle-(SOC) catalyst activity and aging behavior for dewaxing the heavy neutral petroleum feedstock over the alternating layer-bed reactor and conventional catalyst bed to pour point. Actual reactor temperature (ART) and normalized reactor temperature (NRT) are plotted at the top for the alternating HDW-HDT configuration, with corresponding plots for pour point and C₃+C₄ olefin offgas data during the continuous run. As compared to dewaxing heavy neutral over Ni-ZSM-5 alone (solid line), the layered mixed-catalyst system has about the same SOC activity, being only slightly more active, but has a 45% slower aging rate (2 vs. 3.5°C/day). The light gas olefinic content (measured as % olefins in C₃+C₄ hydrocarbons) is about two-thirds that of Ni-ZSM-5 alone, demonstrating that Pd can have a beneficial effect without being in intimate contact with the zeolite. This indicates detrimental effects of olefin and their by-products on conventional dewaxing activity and catalyst aging. As shown in Figure 2, programmed reactor temperature increase, while sufficient to maintain product pour point approximately constant, is not adequate to keep the C₃-C₄ olefins from increasing significantly with time on stream, indicating that hydrogenation activity of Pd/Al₂O₃ ages faster than dewaxing activity of Ni/ZSM-5. Figure 2 also reveals that the aging cycle has two segments according to days on stream. During the first segment (days 0-5), the catalyst undergoes a rapid transient aging at about the same rate as Ni⁻ZSM-5 alone. The aging rates during the second segment (days 5-38) becomes smaller. When the reactor temperatures required to meet -6.7°C (20°F) pour throughout the whole dewaxing cycle are plotted against the corresponding % olefins in C₃+C₄, as shown in Figure 3, the reactor temperatures are approximately linearly proportional to % olefins in C₃+C₄. It is believed that the increasing olefinic concentration exerts a greater inhibition on the dewaxing activity and thereby requires a higher reactor temperature to meet the target pour. Olefinic inhibition that affects dewaxing activity may also affect dewaxing aging. Product composition data shown in Table I are obtained from distillation cuts of material-balance total-liquid product and show that the light product compositions for alternating HDW-­ HDT reactors are somewhat different, being higher in paraffins and lower in naphthenes and aromatics. This is consistent with the function of Pd/Al₂O₃ which hydrogenates the bulk-phase olefins and thereby decreases the extent of olefinic cyclization and aromatization reactions. The lube fraction compositions of the layered-catalyst system is about the same as those of Ni/ZSM-5 alone. Table II compares layered catalyst yield and viscosity index (VI) with those of Ni-ZSM-5 and exchanged Pd-ZSM-5 alone. Compared to a Ni-ZSM-5 system, the novel layered-catalyst system has essentially the same lube yield and VI. The presence of Pd in zeolite may result in a somewhat larger exotherm in a large scale adiabatic reactor.

Claims: 1. A process for catalytic hydrodewaxing of waxy, heavy hydrocarbon feedstock characterized by partially dewaxing the feedstock by contacting the feedstock at conventional dewaxing conditions with a first catalyst bed comprising a conventional dewaxing catalyst of a crystalline zeolite with a constraint index of 1 to 12 in the presence of hydrogen, to produce a partially dewaxed effluent containing olefins, subsequently cascading the partially dewaxed effluent from the first bed through at least one separate hydrogenation catalyst bed under conventional hydrotreating conditions to saturate olefinic reaction products of the dewaxing step, further catalytically dewaxing the hydrotreated feedstock at conventional dewaxing conditions in contact with conventional dewaxing catalyst in at least one additional catalytic dewaxing step, to produce a dewaxed feedstock and further hydrogenating the dewaxed feedstock in an additional hydrotreating step. 2. The process of claim 1 further characterized in that all of the conversion steps are conducted in a reactor shell having alternating operatively-connected fixed beds of hydrodewaxing zeolite catalyst and hydrogenation catalyst. 3. The process of claim 2 further characterized in that quenching hydrogen is introduced to partially dewaxed effluent from the first bed prior to hydrotreating, thereby cooling the effluent to hydrotreating temperature. 4. The process of any preceeding claim further characterized in that at least two hydrodewaxing zones are serially connected to intermediate and final hydrotreating zones, and wherein reaction temperature is adjusted between adjacent zones by direct or indirect contact with a heat exchange medium.

Inventors: PENICK, JOE EDWARD
Applicants: MOBIL OIL CORPORATION
Application year: 1986
Main classification: C10G65
IPC codes: C10G65, C10G49, C10G45