A SURFACE TREATED ELECTRODE AND A ZINC-HALOGEN SECONDARY BATTERY INCORPORATING THE SAME

Abstract: A surface treated electrode applicable to an electrode of a zinc-halogen secondary battery, etc. The surface plastic electrode includes (a) an electrically conductive electrode substrate material; and (b) a surface treatment material on the electrode substrate material, the surface treatment material being made of a phenol resin series activated charcoal fiber satisfying predetermined characteristic such that a weight per unit area substantially equal to 100 g/m² or more, pore diameter having a distribution peak in a range from 1.5 nm to 3.5 nm, a surface area of a part substantially equal to or more than 30 m²/g occupied by pores whose diameters range from 1 nm to 11 nm, a whole relative surface area of the entire pore diameter ranging substantially equal to or more than 1500 m²/g, a tensile strength substantially equal to or more than 294 MPa (30 kg/mm²) and a tensile modulus substantially equal to or less than 14710.5 MPa (1500 kg/mm²). The conductive electrode substrate material is, for example, carbon plastic, glassy carbon, or Carbon-Carbon (C/C) composite. In the case of the C/C composite electrode substrate material, an ion exchange fiber is adhered onto one surface of the C/C composite electrode substrate material to form a three-layer type electrode.

Description: The present invention relates to surface treated electrodes particularly applicable to positive electrodes of zinc-halogen secondary batteries such as zinc-bromine secondary batteries and to zinc-halogen secondary batteries incorporating such electrodes. The present invention particularly relates to surface treated electrodes in which active carbon (activated charcoal) fibers whose originating raw materials are phenol formaldehydes are adhered onto conductive electrode substrates, for example, under mechanical pressure and heat or attached thereto. Carbon fibers are effective surface treatment materials for positive electrodes in zinc-halogen secondary batteries. An electrode having such surface treatment material has conventionally been used with a carbon fiber belonging to the cloth-formed rayon and acryl series adhered onto a surface of a carbon plastic (C.P) under mechanical pressure and heat. However, such carbon fibers belonging to the rayon and acryl series in the above-described cloth forms have problems in their activation processing methods so that sufficient activations in zinc-halogen secondary batteries cannot yet be achieved, especially in zinc-bromine secondary batteries. That is to say, the area of a part occupied by pores having diameters of 1 to 11 nm required for a positive electrode reaction in the above-described electric secondary batteries is not yet formed in a sufficient amount to carry out the positive electrode reaction in the above-described carbon fibers. Because of this the over voltage becomes remarkably large when the charge and discharge operations are carried out, especially at high current densities equal to or above 60 mA/cm². In addition, since the above-described carbon fibers have small weights per unit area in a unit of sheet, are thin in thickness, and weak in mechanical strength such as tensile and bending strengths, they cannot withstand the high mechanical pressure under which they are adhered onto the carbon plastics (C.P) by a heat pressing operation. Many such carbon fibers are thus destroyed to become powders and short length fibers during this process so that they drop off the electrode surfaces. Consequently, electrochemical performances of the zinc-bromine secondary batteries will be greatly reduced. With the above-described problems in mind, it is object of the present invention to provide surface treated electrodes which improve battery characteristics in batteries incorporating them and have a high mechanical strength. It is another object of the present invention to provide surface treated electrodes suitable for the positive electrodes of zinc-halogen secondary batteries, such as zinc-bromine secondary batteries, and which improve the battery characteristics in the zinc-halogen secondary batteries and have the high mechanical strength required for zinc-halogen secondary batteries. The above-described objects can be achieved by providing a surface treated electrode, comprising: a) an electrically conductive material constituting a substrate of the electrode; and b) a surface treatment material on the conductive electrode substrate material, the surface treatment material being made of phenol resin series activated charcoal fiber sheet having: c) a weight per unit area substantially equal to 100 g/m² or more, (d) pore diameters having a distribution peak substantially in a range from 1.5 nm to 3.5 nm with pores having diameters in the range from 1 nm to 11 nm having a surface area substantially equal to or more than 30 m²/g of said phenol resin series activated charcoal fiber sheet, e) a tensile strength substantially equal to or more than 294 MPa (30 kg/mm²), and f) a tensile modulus substantially equal to or less than 14710.5 MPa (1500 kg/mm²). Furthermore the surface treated electrode should have a whole surface area of pore diameter range equal to or more than 1500 m²/g. It should be pointed out that the use of phenolic resin treated woben carbon fibre cloths in ribbed fuel cell electrodes is known from the abstracts with the numbers 126558b and 126559c published in Chemical Abstracts vol. 103 no. 16 of October 21st 1985 on page 185. However the abstracts do not disclose the specific characteristics listed above, nor do they suggest the use of such electrodes in secondary batteries. In any event the fuel cell electrodes disclosed in the abstracts are not of any particular relevance to secondary battery electrodes since fuel cell electrodes and secondary battery electrodes are quite different fields of technology. Inventors exercised experiments on battery characteristics using various kinds of activated charcoal fibers for carrying out surface treatments on electrode substrates such as carbon plastic electrode substrates. The experiments established that when an activated charcoal fiber belonging to the phenol resin series (novoloid of a phenol formaldehyde) is adhered onto a conductive electrode substrate surface and the electrode whose surface is treated in this way is used as a positive electrode of the zinc-halogen secondary battery, the battery characteristics and mechanical strength of the electrode are more advantageous than is the case when cloths formed from activated charcoal fibers belonging to the rayon, cellulose, and acryl series are used as surface treatment materials on electrode substrates. The activated charcoal fibers in phenol resin series are manufactured, e.g. by melt spinning phenol resins (novoloids of phenol formaldehyde) and thereafter activating and sintering them under vaporised water. The activated charcoal fibers whose originating raw materials are phenol formaldehydes are, for example, kynol (trade-mark) activated charcoal fibers manufactured by Nihon Kynol Company Limited, Cloth-ACC series and Felt ACN series. Particularly preferred surface treated electrodes in accordance with the present invention are set forth in claims 2 to 8. The present invention is also applicable to electrodes of other zinc-halogen secondary batteries. Particularly preferred zinc-halogen secondary batteries in accordance with the present invention are set forth in claims 9 to 19. BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 shows a basic construction of a zinc-bromine secondary battery to which a surface treated electrode according to the present invention is applicable. Fig. 2 is a characteristic graph representing a relationship between an electrode potential and discharge current density in the surface treated carbon plastic electrode in a first preferred embodiment according to the present invention. Fig. 3 is a characteristic graph representing the relationship between the electrode potential and discharge current density in the surface treated electrode in a second preferred embodiment according to the present invention. Fig. 4 is a characteristic graph representing the relationship between a discharge duration and battery voltage of the surface treated electrode in a third preferred embodiment according to the present invention. Fig. 5 is a cross sectional view of an electrode having a three-layer construction in the surface treated electrode in a fourth preferred embodiment. Fig. 6 is a cross sectional view of a liquid static type secondary battery in a fifth preferred embodiment. Fig. 7 is a characteristic graph representing a relationship between a charge-discharge duration and battery voltage. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Reference will hereinafter be made to the drawings in order to facilitate understanding of the present invention. Before explaining preferred embodiments according to the present invention, a construction of a zinc-bromine secondary battery will briefly be described. Fig. 1 shows a basic construction of a zinc-bromine secondary battery to which a surface treated carbon plastic electrode according to the present invention is applicable. As shown in Fig. 1, a positive electrode 5 and a negative electrode 6 are separated mutually by a separation member constituted by, e.g., a microporous sheet or ion exchange membrane, denoted by numeral 4, for providing independent electrochemical reactions in each of positive and negative electrode chambers 2, 3. The anolyte and the catholyte for the positive and negative electrode chambers 2, 3 are stored within external electrolyte storage tanks 7, 8, respectively. When charge and discharge of a secondary unit cell generally denoted by 1 are carried out, each electrolyte is supplied to the corresponding electrode chamber 2, 3 by means of corresponding pumps 11, 12 intervened in a lower conduit disposed between the corresponding storage tanks 7, 8 and electrode chambers 2, 3. As the electrolyte for the positive electrode 5, e.g., an aqueous solution of ZnBr₂ plus bromine molecule (Br₂) and bromine complexing agent are used. The addition of the complexing agent contributes the bromine molecule in the positive electrolyte to be changed to a low vapor pressure, low water soluble oily bromine complex. When the discharge action is carried out, ZnBr₂ solution including bromine complex is introduced into the positive electrode chamber 2 by means of the pump 11. In the positive electrode 5, bromine complex is reduced to Br⁻ ion. On the other hand, in the negative electrode 6 on which zinc is electrodeposited, ZnBr₂ solution is introduced by means of the pump 12 and zinc is oxidized to Zn⁺⁺ ion. When the charge action is carried out, bromine molecule is generated in the positive electrode 5 (2Br⁻ → Br₂ + 2e⁻) and zinc is electrodeposited in the negative electrode 6 (Zn⁺⁺ + 2e⁻ → Zn). The electrochemical reaction in the zinc-bromine secondary battery is expressed as follows: The construction and reaction of the zinc-bromine secondary battery are described by a U.S. Patent No. 4,461,817 published on July 24, 1984 and U.S. Patent No. 4,510,218 published on April 9, 1985. The U.S. Patent documents are hereby incorporated by reference. Before explaining preferred embodiments, Table 1 shows lists of article numbers of activated charcoal fiber sheets used in the preferred embodiments and their characteristics. FIRST PREFERRED EMBODIMENT The inventors investigated respective discharge characteristics of the plurality of zinc-halogen secondary batteries using the same electrolytes, each having a concentration of 3 mol/ℓZnBr₂ + Br₂ (0.4 to 1.0 mol/ℓ). Their positive electrodes were formed of surface treated carbon plastic (C.P) electrodes, each having a weight ratio of P.E : C.B (P.E denotes a polyethylene and C.B denotes a carbon black) being 100:50. At this time, four kinds of activated charcoal fiber sheets selected from among phenol resin series activated charcoal fibers (manufactured by Nippon Kynol Company Limited) shown in Table 1 and two kinds of activated charcoal fibers selected from among rayon series activated charcoal fiber sheets (manufactured by Toyobo Incorporation) shown in Table 1 were adhered as surface treatment materials onto the carbon plastic electrodes under mechanical pressure and heat, respectively. In this way, the six surface treated carbon plastic electrodes A through D, M and N were formed. In addition, Fig. 2 shows the experimental results of discharge characteristics of the carbon plastic electrodes (A through D, M and N) whose surfaces were respectively treated with these activated charcoal fibers. As can be appreciated from Fig. 2, the electrodes A through D treated with the phenol resin series activated charcoal fiber sheets have better discharge characteristics than the electrodes M and N treated with the two kinds of rayon series activated charcoal fibers. Especially, although the activated charcoal fiber sheet of article number KF-M-303 in the cloth form used for the electrode N was substantially the same as the phenol resin series activated charcoal fiber sheet of ACC507-15 used in the electrode A in both relative surface area (m²/g) and cloth form as shown in Table 1, the discharge characteristics thereof became considerably lower than ACC507-15 as shown in Fig. 2. This may be caused by differences in the weight per unit area in the unit of fiber and in thickness as estimated from Table 1. SECOND PREFERRED EMBODIMENT The inventors prepared two different carbon plastic electrodes E and O from the same carbon plastics (C.P.U) [each having a weight ratio of P.E (polyethylene)/ C.B (carbon black) / G (graphite) = 50/15/35]. For their surface treatment materials, two kinds of activated charcoal fibers, i.e., ACC507-15(E) and KF-M-303(O) were selected from among six kinds of activated charcoal fibers which were used in the first preferred embodiment and adhered onto the respective surfaces of the carbon plastics under pressure of 5.88 MPa (60 kg/cm²) and temperature of 140°C for three minutes using a metallic die used for manufacturing the electrodes. Table 2 shows several characteristics of the above-described electrodes E and O. Fig. 3 shows respective discharge characteristics thereof. It is noted that requirements for the electrolyte are the same as those in the case of the first preferred embodiment. Characteristics of electrode E and electrode O Thickness Relative Resistance Surface Area Tensile Strength (mm) (Ω-cm) (m²/g) (kg/mm²) E 1.50 0.168 995 315 O 1.33 0.154 330 316 As appreciated from Table 2, although there are little difference between the electrodes E and O in their thickness and relative resistance values, the electrode E is larger than the electrode O in their surface areas including the electrode substrates. This may be caused by their weights per unit area and mechanical strengths (tensile strength) of the activated charcoal fibers of the surface treatment materials and by the fact that the electrode E using the activated charcoal fiber of (E) ACC507-15 having both greater weight per unit area and higher mechanical strength (tensile strength) is sealed to the electrode surface with little destruction of fibers during the pressure and heat adhering process. THIRD PREFERRED EMBODIMENT In this embodiment, the inventors prepared the three unit cell type zinc-bromine secondary batteries each having an interelectrode distance of 10 mm without separation member and constituted by the respective positive electrodes of B, D, and N used in the first preferred embodiment, negative electrodes of Zn plates, and electrolytes of 3 moℓ/ℓ ZnBr₂. In addition, the secondary batteries have charged for one hour with the current density of 20 mA/cm². After the charge operation, each electrolyte was renewed with 3 moℓ/ℓ ZnBr₂. Then the secondary batteries were discharged with the same current density to discuss holding capacities of bromine of the respective positive electrodes. The results of the holding capacities are shown in Fig. 4. Fig. 4 shows change patterns of discharge voltages with respect to a discharge duration in minutes. As shown in Fig. 4, one of the batteries I in which ACN210-20 was used as the positive electrode surface treatment material of the electrode D indicated a higher discharge voltage and a longer discharge duration than the battery J in which ACC507-20 was used as the positive electrode surface treatment material of the electrode B. In addition, the battery J had a better characteristic than the battery K in which KF-M-303 was used as the positive electrode surface treatment material of the electrode N. Consequently, as the surface area of the activated carbon fiber sheet is increased, the activated carbon fibers indicate better characteristics. Next, other electrodes in which the activated charcoal fibers made of novoloid fibers of phenol resin series as the originating raw materials are surface treatment materials of the positive electrodes in the same way as described in the first, second, and third preferred embodiments and carbon series composite materials which are different from the carbon plastics used in the first, second, and third preferred embodiments are used as the conductive electrode substrate materials indicated superior characteristics in the zinc-halogen secondary batteries. The following fourth and fifth preferred embodiments indicate superior characteristics of the zinc-halogen secondary batteries in which the other electrodes as described above were used. FOURTH REFERRED EMBODIMENT The inventors selected three kinds of activated charcoal fibers from those shown in Table 1 and adhered them to glassy carbons GCR 101 (article number and manufactured by Kobe Seiko Kabushikikaisha) to discuss comparisons of electrode activities due to a difference in the electrode surface treatment materials. The adhering method is such that a sheet of each of the activated charcoal fibers is laminated via a conductive carbon paste on the corresponding conductive electrode substrate and burned. Then, three unit cells were prepared in which the electrode P comprising FE-400 and GCR 101, the electrode Q comprising KF-M-303 and GCR 101, and the electrode G comprising ACC 509-20 and GCR 101 were used as the respective positive electrodes and GCR 101 was used for each negative electrode, and RASI (trademark) separator material manufactured by Asahi Kasei Kabushikikaisha was used for each microporous sheet constituting the separation member. Each unit cell zinc-bromine secondary battery was charged for eight hours with the current density of 15 mA/cm² and was discharged with the same current density. Thereafter, the inventors compared and discussed each battery characteristic. The result of each battery characteristic is shown in Table 3. Performance of each battery (4), (5) and (6) Battery (No) Kinds of positive and negative electrodes Voltaic Efficiency Coulombic Efficiency Energy Efficiency Remarks Battery (4) Electrode (G) GCR 101 91.4% 90.5% 82.7% 15A/cm² 8 hour charge Battery (5) Electrode (P) GCR 101 82.1% 81.0% 66.5% Battery (6) Electrode (Q) GCR 101 86.5% 82.8% 71.6% It is noted that the electrolyte used was 3 moℓ/ℓ ZnBr₂ with which a bromine complexing agent is mixed and furthermore 4 moℓ/ℓ NH₄Cℓ is added to improve conductivity. The electrolyte is recirculated as described before with reference to Fig. 1. As appreciated from Table 3, the battery (4) in which the electrode G to which ACC 509-20 was adhered had superior characteristic in terms of each efficiency to the other batteries (5) and (6). FIFTH PREFERRED EMBODIMENT Fig. 5 shows a cross sectional view of a three-layer type electrode. Fig. 6 shows a cross sectional view of a liquid static type unit cell of zinc-bromine secondary battery. As shown in Fig. 5, the inventors selected three kinds of the activated charcoal fibers, i.e., FE-400, KF-M-303, and ACC 509-20 shown in Table 1 as the activated charcoal fiber sheet 51A of the surface treatment materials. Each of these activated charcoal fiber sheet 51A was brought in contact with PP-444 manufactured by Nikken Giken Kabushikikaisha as C/C composite 51B (Carbon-Carbon composite) in the carbon series composite material. In addition, an ion exchange membrane 51C was adhered to a surface of the C/C composite 51B (PP-444) opposite to one of the activated charcoal fibers 51A to form the three-layer type electrode 51. It is noted that numeral 51D denotes a mold resin. Such a three-layer type electrode 51 provides a holding effect of a halogen molecule Br₂ and so on. The inventors prepared the liquid static type unit cell of zinc-bromine secondary battery in which the above-described three-layer type electrode 51 was used as the positive electrode 5 and a zinc plate (a rolled zinc plate having a purity of 99.99%) was used as the negative electrode 6, as shown in Fig. 6. It is noted that, in Fig. 6, numeral 61 denotes the electrolyte (3 moℓ/ℓ ZnBr₂ + Br₂), numeral 62 denotes an outer envelope made of a mold resin, numeral 52 denotes a lead terminal of the positive electrode 5, numeral 64 denotes a lead terminal of the negative electrode 6, and numeral 63 denotes an entrance of the electrolyte 61. The three kinds of batteries (7), (8) and (9) prepared in the way described above were charged for one hour with the current density of 15 mA/cm² and discharged with the same current density. Table 4 and Fig. 7 show each battery characteristic of the three kinds of batteries (7), (8), and (9). It should be noted that the discharge voltage was zero volt when the discharge operation is ended. As shown in Table 4 and Fig. 7, the battery (7) in which ACC 509-20 is used as a surface treatment material has a longer duration time than the other two kinds of batteries (8) and (9) and operates with superior values of the charge and discharge voltages to those of the other batteries (8) and (9). Characteristics of Batteries (7), (8) and (9) Battery No. Battery (7) Battery (8) Battery (9) Kinds of Activated Charcoal Fibers Used in Positive Electrode ACC 509-20 Fineguard FE-400 KF-M-303 Voltage (V) at Initial Stage of Charge 2.1 2.2 2.1 Voltage (V) at Final Stage of Charge 2.2 2.4 2.3 Voltage (V) at Initial Stage of Discharge 1.9 1.5 1.7 Discharge Duration (min) 57 48 50 Coulombic Efficiency (%) 95 80 83 Remarks Good Moldability Carbon Powders was Generated During the Molding Operation Carban Powders was Generated During the Molding Operation As the result of fourth and fifth preferred embodiments, the activated charcoal fiber ACC 509-20 of the novoloid type of the phenol resin series indicated a superior characteristic in the activity when any arbitrary electrode substrate material was used. Especially, the activated charcoal fiber ACC 509-20 indicated a superior electrochemical reactivity to the other activated charcoal fibers due to the large relative surface area that it has. Consequently, the inventors admitted that it was reasonable for the activated charcoal fiber ACC 509-20 to used as the surface treatment material of the positive electrode in the zinc-halogen secondary battery. EFFECT Since the phenol resin series activated charcoal fiber sheets have large relative surface areas, large adsorption quantities, and pores whose diameters have distribution peaks from 1.5 nm to 3.5 nm, they indicate good electrochemical reactions for active materials in the electrolytes. In addition, since the above-described activated charcoal fiber sheets have large percentage elongations and small modulus of elasticity, they are flexible and have good workabilities. As described above, since the phenol resin series activated charcoal fibers have higher tensile strength and tensile modulus than the rayon and acryl series carbon fiber sheet, they can only withstand mechanical pressure and heat under which surface treatment materials of electrodes used in zinc-halogen secondary batteries are adhered to the electrode substrate material but also achieve better battery characteristics due to remarkably larger surface areas of the carbon fiber sheets themselves. Table 5 shows general characteristics of each typical activated charcoal fiber sheet. characteristics Phenol Resin Series Rayon Series Acryl Series Granulated Carbon Fiber diameter (µm) 9 to 11 15 to 20 6 to 8 - Relative Surface Area (m²/g) 1500 to 2000 1400 900 800 Pore Diameter (nm) 1.5 to 3.5 114 1.0 1.5 to 2.5 Tensile Strength (kg/mm²) 30 to 40 5 to 10 30 - Tensile Modulus (kg/mm²) 1000 to 1500 - 7000 to 8000 - SI unit : kg/mm² = 9.807 MPa The above-described surface treated electrodes in which one of the phenol resin series activated charcoal carbon fiber sheet having its weight per unit area equal to or more than 100 g/m², pore diameters whose distribution peaks are 1.5 to 3.5 nm and whole relative surface area equal to or more than 1500 m²/g are used as the positive electrode surface treatment materials according to the present invention has the following superior characteristics than the surface treated electrodes as the treatment materials of which activated charcoal fiber sheets belonging to any one of rayon series, cellulose series. and acryl series are used. (1) Since the phenol resin series activated charcoal fibers manufactured by Nihon Kynol Company Limited as described above have larger halogen (bromine) holding capacities than the cellulose series, rayon series, and acryl series activated charcoal fibers, the actual characteristics thereof when they are adhered to the conductive electrode substrates are remarkably improved and especially the discharge characteristics required for the secondary batteries were remarkably improved. (2) Since the activated charcoal fibers manufactured by Nihon Kynol Company Limited have high mechanical strength, i.e., high tensile strength and low tensile modulus in their fibers themselves, the fibers are seldom destroyed during the adhering process under mechanical pressure and heat to the conductive electrode substrate. Consequently, the carbon plastic electrode having a large relative surface area and to which such an activated charcoal fiber is adhered under mechanical pressure and heat in a metallic die can properly be manufactured. Furthermore, the electrodes in which the activated charcoal fibers whose originating raw materials are the phenol resin series novoloid fibers are adhered to the glassy carbons in a conventional method can achieve superior characteristics than those in which the activated charcoal fibers of the other PAN series or rayon series are adhered to the conductive electrode substrates. In addition. the electrodes having the three-layer constructions using the activated charcoal fibers whose originating raw materials are the phenol resin series novoloid fibers, C/C composites, and ion exchange fibers exhibit proper electrode characteristics such that discharge durations are longer than those manufactured using the PAN series or rayon series activated charcoal fibers. It will clearly be understood by those skilled in the art that the foregoing description is made in terms of preferred embodiments and various changes and modifications are made without departing from the scope of the present invention which is to be defined by the appended claims.

Claims: A surface treated electrode, comprising: a) an electrically conductive material constituting a substrate of the electrode; and b) a surface treatment material on the conductive electrode substrate material, the surface treatment material being made of a phenol resin series activated charcoal fiber sheet having: c) a weight per unit area substantially equal to 100 g/m² or more, d) pore diameters having a distribution peak substantially in a range from 1.5 nm to 3.5 nm, with pores having diameters in the range from 1 nm to 11 nm having a surface area substantially equal to or more than 30 m²/g of said phenol resin series activated charcoal fiber sheet, e) a tensile strength substantially equal to or more than 294 MPa (30 kg/mm²), and f) a tensile modulus substantially equal to or less than 14710.5 MPa (1500 kg/mm²). The surface treated electrode as set forth in claim 1, wherein said conductive electrode substrate material is a glassy carbon. The surface treated electrode as set forth in claim 1, wherein said conductive electrode substrate material is a carbon plastic. The surface treated electrode as set forth in claim 1, wherein said conductive electrode substrate material comprises a Carbon-Carbon composite material, to one surface of which the surface treatment material is adhered and to the opposite surface of which an ion exchange fiber is adhered. The surface treated electrode as set forth in claim 3, wherein the phenol resin series activated charcoal fiber is adhered onto the carbon plastic material under mechanical pressure and heat. The surface treated electrode as set forth in claim 3, wherein the phenol resin series activated charcoal fiber is attached onto the carbon plastic material surface. The surface treated electrode as set forth in claim 1, wherein the surface treated electrode is a positive electrode of a zinc-halogen secondary battery. The surface treated electrode as set forth in claim 7, wherein the surface treated electrode is a positive electrode of a zinc-bromine secondary battery. A zinc-halogen secondary battery, incorporating a positive electrode in the form of a surface treated electrode in accordance with claim 1. A zinc-halogen secondary battery as set forth in claim 9, wherein the electrically conductive material comprises a carbon plastic which has a weight ratio of polyethylene to carbon black substantially equal to 100:50 and onto which the surface treatment material is adhered under predetermined mechanical pressure and heat. A zinc-halogen secondary battery as set forth in claim 9, wherein the electrically conductive electrode substrate material comprises a carbon plastic which has a weight ratio of polyethylene, carbon black and graphite substantially equal to 50:15:35 and onto which the surface treatment material is adhered under a predetermined mechanical pressure and predetermined temperature using a predetermined die for a predetermined interval of time. A zinc-halogen secondary battery as set forth in claim 11, wherein the predetermined pressure is substantially 5.88 MPa (60 kg/cm²), the predetermined temperature is substantially 140°C, and the predetermined interval of time is substantially three minutes. A zinc-halogen secondary battery as set forth in claim 11, wherein the surface treatment material is the phenol resin series activated charcoal fiber derived from an activation and sintering of a novoloid of phenol formaldehyde under vaporized water after a melt spinning of the novoloid. A zinc-halogen secondary battery as set forth in claim 11, wherein the surface treatment material has a weight per unit area in a unit of sheet substantially equal to 135 g/m², a thickness substantially equal to 0.53 mm, a relative surface area substantially equal to 1500 m²/g, a pore diameter substantially ranging from 1.5 nm to 3.5 nm, and a cloth form. A zinc-halogen secondary battery as set forth in claim 14, wherein the carbon plastic electrode substrate material has a thickness substantially equal to 1.50 mm, a resistivity substantially equal to 0.168 Ω-cm, a relative surface area substantially equal to 995 m²/g, and a tensile strength substantially equal to 3129.205 MPa (315 kg/mm²). A zinc-halogen secondary battery as set forth in claim 9, wherein the positive electrode surface treatment material is a phenol resin series activated charcoal fiber having a weight per unit area in a unit of sheet substantially equal to 100 g/m², a thickness substantially equal to 2.20 mm, a relative surface area substantially equal to 2000 m²/g, pore diameters substantially ranging from 1.5 nm to 3.5 nm and a felt form. A zinc-halogen secondary battery as set forth in claim 16, wherein the positive electrode constituted by the conductive electrode substrate material comprises a carbon plastic having a weight ratio of polyethylene to carbon black substantially equal to 100:50 and onto the surface of which the positive electrode surface treatment material is adhered under mechanical pressure and heat; a negative electrode formed of zinc plate; and an electrolyte of ZnBr₂ having a concentration substantially equal to 3 mol/l, wherein the battery has an interelectrode distance of 10 mm without an electrode separating member, and wherein the battery including the phenol resin series activated charcoal fiber of the surface treatment material has a higher discharge voltage and longer discharge duration than a zinc-halogen secondary battery including a phenol resin series activated charcoal fiber of the positive electrode surface treatment material having a weight per unit area in a unit of sheet substantially equal to 115 g/m², a thickness substantially equal to 0.44 mm, a relative surface area substantially equal to 2000 m²/g, pore diameters ranging from 1.5 nm to 3.5 nm, and a cloth form when both zinc-halogen secondary batteries are charged for one hour at current densities of 20 mA/cm² and discharged with the same electrolytes being used. A zinc-halogen secondary battery as set forth in claim 9, wherein the conductive electrode substrate material comprises a glassy carbon onto which a sheet of the activated charcoal fiber phenol resin series having a predetermined characteristic is laminated via a conductive carbon paste, said predetermined characteristic being such that the weight per unit area is 170 g/m², the thickness is 0.60 mm, the relative surface area is 2000 m²/g, the pore diameter ranges from 1.5 nm to 3.5 nm, and the fiber form is a cloth form. A zinc-halogen secondary battery as set forth in claim 9, wherein the conductive electrode substrate material comprises a Carbon-Carbon composite material, to one surface of which the phenol resin series activated charcoal fiber is adhered as the surface treatment material and to the opposite surface of which an ion exchange fiber is adhered and which further comprises a rolled zinc plate as a negative electrode having a purity of 99.99% and an electrolyte of 0.3 mol/l ZnBr₂ + Br₂.

Inventors: FUJII, TOSHINOBU, FUSHIMI, KAZUO, HIROTA, AKIHIKO
Applicants: KABUSHIKI KAISHA MEIDENSHA
Application year: 1986
Main classification: H01M4
IPC codes: H01M4, H01M10