STRONTIUM ALUMINOSILICATE GLASS SUBSTRATES FOR FLAT PANEL DISPLAY DEVICES

Abstract: This invention is concerned with the fabrication of flat panel display devices wherein a film of large crystal polysilicon is grown on a substrate. More particularly, the present inven­ tion is drawn to such devices wherein the substrate is prepared from a strontium aluminosilicate glass consisting essentially, in mole percent, of about 9-12% SrO, 9-12% Al₂O₃, and 77-82% SiO₂.

Description: This invention relates to glass substrates for flat panel display devices. Two recent technological advances have made large, flat-panel display devices a distinct practical possibility: (1) the preparation of liquid crystals exhibiting improved characteristics; and (2) the production of a surface layer of fine-grained polysilicon. The development of liquid crystals has progressed to the point where miniature color television receiver sets have been produced from them and much larger information display panels are technically possible. Liquid crystals inherently demonstrate slow responses to electrical signals and, therefore, a "switch" to rapidly respond to an electrical stimulus is required to set up an active matrix display. The thin film transistor (TFT) performs that function. It is well-known that a TFT can be fabricated from single crystal silicon; however, by the very nature of single crystal silicon, there is a limitation on the size of a TFT that can be fashioned therefrom. It has been discovered that a fine-grained polysilicon layer which has been deposited onto a substrate can be recrystallized to large-grained polysilicon by scanning with a heat source such as a laser. It has been observed that a TFT prepared from large-grained polysilicon evidences only slight deterioration in electrical characteristics when compared with those displayed by a TFT fabricated from single crystal silicon, and operates very satisfactorily in multiplexing a liquid crystal display. A large-grained polysilicon active matrix display requires a substrate which is transparent, flat, smooth, inert, compatible with silicon, in terms of thermal expansion, and capable of withstanding processing temperatures of at least 850°C. Accordingly, a glass will meet those requirements if it is free from alkali metal ions, it displays a linear coefficient of thermal expansion (25°-300°C) of 30-40x10⁻⁷/°C, and an annealing point greater than 875°C. In order to utilize the glass sheet forming method described in United States Patent No. 3,338,696, the glass must exhibit a liquidus viscosity of at least 10kPa.s (100,000 poises), preferably over 25kPa.s (250,000 poises). Also, transparent, homogeneous glasses with annealing points in the vicinity of 900°C are very difficult to obtain by melting batches at temperatures no higher than 1800°C. 1800°C represents the practical limit for melting materials in contact with platinum-rhodium and most refractories used in an oxidizing atmosphere. Finally, to permit glass forming to be carried out utilizing conventional equipment and techniques, the liquidus temperature should be no more than 1400°C. Therefore, the primary objective of the present invention is to prepare transparent, homogeneous glasses demonstrating a linear coefficient of thermal expansion (25°-300°C) of 30-40x10⁻⁷/°C, an annealing point greater than 875°C, a liquidus temperature no higher than 1400°C, a liquidus viscosity of at least 10kPa.s (100.000 poises), which can be melted at temperatures not exceeding 1800°C. The present invention provides a clear, transparent, homogeneous strontium aluminosilicate glass capable of being melted at temperatures no higher than 1800°C which exhibits an annealing point greater than 850°C, a linear coefficient of thermal expansion over the temperature range of 25°-300°C of 30-40x10⁻⁷/°C, a liquidus temperature not exceeding 1400°C, and a liquidus viscosity of at least 10kPa.s (10⁵ poises), said glass being essentially free from alkali metal oxides, MgO,CaO, ZnO, La₂O₃,MnO, and consisting essentially, expressed in terms of mole percent on the oxide basis, of 9-12% Sr0 9-12% Al₂0₃ 77-82% Si0₂ The limits of the component regimes are extremely critical. To illustrate, where the level of SrO is too high, the annealing point falls below the desired target and the linear coefficient of thermal expansion may be raised to an unacceptably high value. Conversely when the SrO content is too low, the glass becomes very difficult to melt and/or the liquidus temperature is raised to an unacceptable level. Al₂0₃ concentrations lower than those specified lead to annealing points that are too low. Al₂0₃ contents greater than those specified result in undesirably high liquidus temperatures. When the amount of Si0₂ exceeds the prescribed maximum, the glasses become too difficult to melt; at Si0₂ levels below the stated minimum, either the annealing point becomes too low or the liquidus temperature becomes too high. Whereas a precise conversion of composition ranges expressed in mole percent to ranges in weight percent is not possible, an approximation of the ternary system expressed in weight percent comprises 13-18% SrO, 13-18% Al₂O₃, and 66-72% SiO₂. Minor substitutions of MgO, CaO, ZnO, La₂O₃, and MnO for SrO in the ternary system undesirably affect the linear coefficient of expansion and/or the annealing point and/or the liquidus temperature of the glass. Therefore, only very small additions of those materials can be tolerated when the desired glass properties are to be maintained. Strong fluxes such as the alkali metal oxides will desirably be essentially absent. The substitution of BaO for part of the SrO causes a slight rise in the linear coefficient of expansion and has the very desirable capability of reducing the liquidus temperature without adversely affecting the viscosity of the glass to any substantial extent. Hence, the substitution of BaO for SrO does not alter the annealing point appreciably. That capability of BaO is of practical significance in that, by balancing the SrO and BaO concentrations, the coefficient of thermal expansion can be varied and carefully controlled. Whereas substitutions of BaO for SrO up to 8 mole percent, preferably no more than 6 mole percent, can be useful, volatilization of BaO is a recognized problem when melting temperatures of 1800°C are employed. SrO is much less subject to volatilization at 1800°C. Furthermore, and even more importantly from the standpoint of glass melting, the inclusion of large amounts of BaO leads to the development of seeds in the glass. For example, where BaO is substituted in total for SrO, it is virtually impossible to produce at melting temperatures no higher than 1800°C a glass containing no more than a few seeds. In contrast, laboratory experience has demonstrated that essentially seed-free glasses can be prepared from glasses within the above-prescribed ranges of the ternary system SrO-Al₂O₃-SiO₂. Accordingly, whereas the incorporation of BaO can impart useful properties to the glass, its presence can lead to environment polluting volatilization and renders the glass more difficult to melt to good quality. Prior Art Kh. Sh. Iskhakov, "Region of Glass Formation in a Strontium Oxide-Aluminum Oxide-Silicon Dioxide System", Uzb . Khim . Zh . 15 [1], 10-12 (1971) describes the preparation of glasses composed, in mole percent, of 25-60% SrO, 5-30% Al₂O₃, and 35-65% SiO₂ by melting at 1500°-1550°C for 1-1.5 hours. The SrO contents are quite apparently far removed from those of the present invention. Kh. Sh. Iskhakov, "Properties of Glasses in the Strontia-Alumina-Silica System", Uzb . Khim . Zh ., 15 [2], 79-81 (1971) discusses several physical properties determined on glasses having compositions within the ranges of the above Iskhakov literature reference. It was observed that the glasses manifested coefficients of thermal expansion of 64-97x10⁻⁷/°C. It was stated that as the SrO content is raised, the coefficient of thermal expansion rises. G. I. Zhuravlev, A. I. Kuznetsov, T. I. Semenova, and N. G. Suikovskaya, Glass , USSR SU870,365, January 7, 1984, discloses the preparation of glasses demonstrating higher softening points and special electrical resistivities containing, in weight percent, 25-35% SrO, 11-20% Al₂O₃, and 41-63% SiO₂. The SrO and SiO₂ levels are generally higher and lower, respectively, when compared with their concentrations in the present inventive glasses. G. I. Zhuravlev, V. A. Malov, A. I. Kuznetsov, and T. I. Draunina, "Application of Dispersed Glass of Silicon Dioxide-Aluminum Oxide-Strontium Oxide System on a Niobium Substrate by Electrophoretic Deposition", Zh . Prikl . Khim . ( Leningrad ) 54 [7] 1601-4 (1981) describes the application of a protective electric insulating coating on niobium parts of high pressure lamps through electrophoretic deposition of glass having a composition within the ranges disclosed in the above Zhuravlev et al. literature reference. United States Patent No. 4,180,618 reports the fabrication of electronic devices comprised of a thin film of silicon deposited upon a substrate, wherein the substrate is composed of a glass consisting essentially, in weight percent, of 55-75% SiO₂, 5-25% Al₂O₃, and at least one alkaline earth oxide selected from the group in the indicated proportions of 9-15% CaO, 14-20% SrO, and 18-26% BaO. The CaO and BaO contents are higher than can be tolerated in the present inventive glasses. Whereas the broad ranges of SrO, Al₂O₃, and SiO₂ overlap those of the inventive glasses, there is no recognition of the matrix of superior properties which can be secured from compositions coming within the narrowly circumscribed ranges of the present invention; nor is there a working example provided which falls within the limits of the present inventive glasses. Table 1 records a number of glass compositions, expressed in terms of mole percent on the oxide basis, illustrating the parameters of the instant invention. Thus Examples 1,6,16,19,32,36,37,40,41,47 and 48 are compositions of the invention whereas Examples 2-5,7-15,17,18, 20-31, 33-35, 38, 39 and 42-46 are comparative examples. The actual batch ingredients can comprise any materials, either the oxides or other compounds, which, when melted together, will be converted into the desired oxides in the proper proportions. In the laboratory work described below, the batch materials consisted of high purity sand, Al₂0₃, SrC0₃, BaC0₃, Mg0, Ca0, Zn0, Mn0, and La₂0₃. The batch materials were compounded, ballmilled to assist in achieving a homogeneous melt, and charged into platinum or platinum-rhodium crucibles. Those batches containing 77% Si0₂ and less could be melted at 1600-1650°C for 4-16 hours in an electrically-heated furnace. The batches of higher Si0₂ contents were melted at 1700°-1800°C for 16 hours in a gas-oxygen fired furnace. In each case, the melts were cast into an iron mold to form circularly-shaped slabs having a diameter of about 30.5cm (12") and a thickness of about 1.9cm (0.75"), and those slabs immediately transferred to an annealer. Table IA reports the compositions of Table I in terms of weight percent on the oxide basis. Table II records a number of physical properties measured on the above glasses. The annealing point (Ann. Pt.) and strain point (Str. Pt.) in terms of °C were determined in accordance with the beam bending method described in ASTM C598; the linear coefficient of thermal expansion (Coef. Exp.) in terms of x10⁻⁷/°C over the range of 25°-300°C was ascertained in accordance with ASTM E228 utilizing a fused silica dilatometer; the internal liquidus temperature (Liquidus) in terms of °C was determined by placing the glass in a platinum boat, introducing the boat into a furnace having a temperature gradient spanning the liquidus temperature, and maintaining the boat in that furnace for 24 hours; the viscosity of the glass at the liquidus (Liq. Vis.) in terms of 10 kPa.s (10⁵ poises) was delineated by using a rotational viscometer while cooling the glass at 2°C/minute; the D.C. resistivity (Logρ at 250°C and 350°C) in terms of ohm-cm, dielectric constant (Die. Con.) at ambient temperatures and 1KHz, and the loss tangent (Loss Tan.) at ambient temperature and 1KHz were defined following the techniques set out in ASTM D150, D257, and C657; and the chemical durability of the glass upon individual exposures to 5% aqueous HCl for 24 hours, to 5% aqueous NaOH for 6 hours, and to 0.02N aqueous Na₂CO₃ for 6 hours, each exposure being made at 95°C and each loss being reported in terms of mg/cm², was ascertained on polished plates of glass both in terms of visual appearance (Appear.) and in terms of weight loss (Wt. Loss). With respect to appearance, N.C. indicates no change, S. Frost means slight frosting, and S. Haze reflects slight haze. Glasses 17-26 were melted for 16 hours at 1650°C in an electrically-fired furnace. Glasses 23 and 24 were clear, viscous, and free from seeds; glasses 18, 20, and 22 were clear, but quite seedy; and the remainder of the glasses contained some seeds and were clear. The rest of the exemplary compositions were melted in a gas-oxygen furnace for 16 hours at 1800°C. At SiO₂ levels up to 81 mole percent, the glasses were clear, viscous, and free from seeds. At a concentration of 82 mole percent SiO₂, the glasses were clear, extremely viscous, and surprisingly, free from seeds. At a content of 83 mole percent SiO₂, the glasses appeared to be clear, but so viscous that they barely moved, and contained some seeds. A conjunctional study of Tables I and II clearly illustrates the criticality of maintaining the SrO, Al₂O₃, and SiO₂ concentrations within the prescribed ranges of the ternary system to prepare glasses capable of being melted at temperatures no higher than 1800°C, and which demonstrate annealing points greater than 875°C, linear coefficients of thermal expansion over the temperature range of 25°-300°C of 30-40x10⁻⁷/°C, liquidus temperatures not exceeding 1400°C, and liquidus viscosities of at least 10 kPa.s (100,000 poises). That study also indicates the generally unfavorable effects which the inclusion of MgO, CaO, ZnO, La₂O₃ and/or MnO can have upon the resulting glasses with respect to the above properties. In contrast, the addition of BaO can be useful in reducing the liquidus temperature without significantly affecting the viscosity of the glass, but care must be exercised in such additions because of volatilization of BaO and the development of seeds in the glass.

Claims: A clear, transparent, homogeneous, strontium alumino-silicate glass capable of being melted at temperatures no higher than 1800°C which exhibits an annealing point greater than 875°C, a linear coefficient of thermal expansion over the temperature range of 25°-300°C of 30-40x10⁻⁷/°C, a liquidus temperature not exceeding 1400°C, and a liquidus viscosity of at least 10kPa.s (10⁵ poises), said glass being essentially free from alkali metal oxides, MgO,CaO,ZnO,La₂O₃, and MnO, and consisting essentially expressed in terms of mole percent on the oxide basis, of 9-12% SrO 9-12% Al₂O₃ 77-82% SiO₂ A glass according to claim 1 wherein up to 8 mole percent BaO is substituted for SrO. In a flat panel display service containing a flat transparent substrate for growing large crystal polysilicon semiconductor films thereon, the improvement wherein said substrate is a strontium alumunosilicate glass capable of being melted at temperatures no higher than 1800°C and which exhibits an annealing point greater than 875°C, a linear coefficient of thermal expansion over the temperature range of 25°-300°C of 30-40x10⁻⁷/°C, a liquidus temperature not exceeding 1400°C, and a liquidus viscosity of at least 10kPa.s (10⁵ poises), said glass being essentially free from alkali metal oxides, MgO,CaO,ZnO,La₂O₃, and MnO, and consisting essentially, in terms of mole percent on the oxide basis, of 9-12% SrO 9-12% Al₂O₃ 77-82% SiO₂ A device according to claim 3 wherein up to 8 mole percent BaO is substituted for SrO.

Inventors: DUMBAUGH, WILLIAM HENRY, JR.
Applicants: CORNING GLASS WORKS
Application year: 1986
Main classification: C03C3
IPC codes: G02F1, C03C3, G09F9