METHOD OF DEPOSITING ON A SUBSTRATE A LAYER WHICH CONSISTS SUBSTANTIALLY OF SILICON CARBIDE

Abstract: A layer of SiC is deposited at a comparatively low tempera­ ture (700-1000 °C) and low pressure (25-125 Pa) from a gaseous mixture which comprises preferably SiH₄ and C₂H₄ in a molar ratio of 0.4-4. The resulting layers are hard, adhere readily and are homogeneous.

Description: Method of depositing on a substrate a layer which consists substantially of silicon carbide. The invention relates to a method of depositing on a substrate a layer which consists substantially of silicon carbide (SiC) by causing a gaseous mixture of a silicon compound and a carbon compound to react with each other at elevated temperature in a reactor in which the substrate to be coated is present. A layer which consists substantially of SiC is to be understood to mean herein a layer the composition of which differs little from the stoechiometric composition. The deposition of layers which consist substantially of SiC by means of a thermal CVD-process is known per se. Processes are known which are carried out at temperatures above 1,0000C and at atmospheric or higher pressure. In high-temperature processes the choice of the substrate material is restricted. In processes which are carried out at atmospheric or higher pressure, homogeneous layers are difficult to deposit. In processes in which halides of silicon are used, the corrosive character of halogen compounds formed in the reaction (for example, HCl when SiCl4 or other chlorine-containing silicon compounds or carbon compounds are used) must be taken into account in the choice of the substrate material. It is therefore the object of the invention to provide a method which can be carried out at temperatures up to 1,0000C and at low pressure and in which no halogen or halogen compounds are formed and with which hard, adhering and homogeneous SiC-layers are obtained. According to the invention, this object is achieved by means of a method which is characterized in that a gaseous mixture which contains SiH4 and c 2H4 is heated in the reactor to a temperature between 700 and 0 1,000 C at a pressure between 25 and 125 Pa. The gas mixture may additionally contain a carrier gas, for example, argon or hydrogen or a mixture of both gases. During the investigation which led to the invention it was found that hard, homogeneous and adhering layers of SiC can be deposited on hard metal and various types of steel which contain approximately 49 to 56 at.* of silicon, the quantity of free silicon and free carbon, respectively, being comparatively small. The molar ratio of SiH4 to 02H4 in the gas mixture is preferably between 0.4 and 4. It has been found that the composition of the deposited layer is little influenced within these limits. It has been found that a high molar ratio of SiH4 to C 2H4 can influence the layer thickness of the deposited SiC layers over the length of the reactor. With the molar ratio of SiH4 to C2H4 between 0.4 and 0.6, however, said influence is acceptable for most applications (difference less than 40* over 50 cm). The growth rate of the layers also decreases at temperatures below 70000. Practically useful growth rates of approximately 1 /um (micrometres) and more per hour are found at temperatures between 800 and 9500 G. Between 850 and 9000 C an SiC layer is obtained in which the Si-content in at.* is between 49 and 56 at.. The growth rate is also influenced by the pressure used.When the pressure increases, the growth rate also increases. Above 125 Pa, however, the significance of a homogeneous gaseous phase reaction begins to become greater as a result of which the growth rate decreases again. The resulting SiC layers are polycrystalline, the crystallites have a hexagonal structure. The deposited SiC layers adhere particularly readily to all kinds of hard metals. To obtain a good adhesion to steel substrates it may be necessary to deposit a thin adhering layer consisting of titanium nitride before SiC is deposited (thickness TiN layer : 1 /um). The method according to the invention will now be described in greater detail with reference to the ensuing specific examples. Example 1: Hard metal chisels (type THF from Krupp, 94 WC, 4 Co, 2 other carbides (TiC/TaC/NbC)) are placed in a low-pressure reactor. After the reactor has been brought to sub-ambient pressure, the temperature is adjusted to 8500 C while flushing with 200 sccm of H2 per minute. 0 When 850 C is reached, 30 ml of SiH4 and 30 sccm of C H per minute are admitted to the reactor at a pressure of 0.5 mbar (50 Pa). After 2Q hours a 5 /um thick SiC layer is deposited on the chisels (1 sccm at 76 cm and 200 C). Example 2: A steel electrochemical machining (ECM) electrode (St 33-1 according to 17100) is placed in the reactor and is first covered with an adhering intermediate layer of TiN (8500C, 900 mbay 4 TiCl4, remainder N2 + H2 1:1 for 60 minutes until a thickness of 1 /um). As in example 1, a 5 /um thick SiC layer is then deposited. An insulating Si3N4 layer is then deposited on the electrode starting 0 from a gas mixture of SiH2Cl2 + NH 3 at 850 C and a pres- sure of 0.5 mbar. 200 sccm/minute of NH3 and 25 sccm/ minute of SiH2Cl2 are then admitted for 30 minutes, after which a 0.5 /um thick Si3N4 layer has formed. A 5 /um thick SiC layer is deposited over this layer according to example 1 so that totally an SiC-Si3N4-SiC triple layer is obtained. Such a layer can successfully be used as an insulation on an ECM-electrode.

Claims: A A method of depositing on a substrate a layer which consists substantially of SiC by causing a gaseous mixture of a silicon compound and a carbon compound to react with each other at elevated temperature in a reactor in which the substrate to be coated is present, characterized in that a gaseous mixture which contains SiH4 and C H is heated in the reactor to a temperature between 700 and 1,0000 C at a pressure between 25 and 125 Pa. 2. A method as claimed in Claim 1, characterized in that the molar ratio of SiH4 to C2H4 in the gaseous mixture is between 0.4 and 4. 3. A method as claimed in Claim 1, characterized in that the molar ratio of SiH4 to C2H4 in the gaseous mixture is between 0.4 and 0.6. 4. A method as claimed in Claim 1, characterized in that the temperature to which the gaseous mixture is heated is between 800 and 9500 C. 5. A method as claimed in Claim 1, characterized in that the temperature to which the gaseous mixture is heated is between 850 and 9000 C.

Inventors: JENSMA, JACOB PIETER C/O INT. OCTROOIBUREAU B.V., VERSPUI, GERRIT C/O INT. OCTROOIBUREAU B.V.
Applicants: N.V. PHILIPS' GLOEILAMPENFABRIEKEN
Application year: 1986
Main classification: C23C16
IPC codes: C01B31, C23C16