RECOVERY OF LIGNIN

Abstract: Lignin is precipitated in high yields and at high rates from a black liquor produced by pulping wood at high temperatures and pressures with an aqueous lower aliphatic alcohol solvent. The lignin is precipitated by diluting the black liquor with water and an acid to form a solution with a pH of less than 3, an alcohol content of less than 30% by volume and a temperature of less than 75°C. The precipitated lignin, when subsequently dried, is in the form of a powder which requires little or no crushing to convert it into a fine uniform size suitable for use without further significant processing.

Description: BACKGROUND OF THE INVENTION This invention relates to a process for precipitating lignin from a solution of lignin in a water miscible organic solvent, and to an apparatus for carrying out the process. Processes far treating wood with organic solvents, such as alcohols, to separate the wood's lignin, hemicellulose, sugar and cellulose fractions are now well known, see, for example, U.S. patent 1,856,567 and U.S. Patent 3,585,104. Such solvent pulping processes have appeared to be attractive alternatives to conventional chemical pulping processes, such as kraft and sulfite pulping processes which suffer from relatively high equipment costs and pollution problems. One solvent pulping process, disclosed in U.S. Patent 4,100,016, has appeared to be particularly attractive in providing highly efficient recovery of its alcohol solvent, separation of the cellulose and lignin fractions of wood, and recovery of cellulose pulp with no appreciable air or water pollution or solid waste products. This patented process has also provided hardwood pulps with yields, strengths, Kappa numbers, viscosities, fiber strengths and bleachability characteristics that are equal to or better than kraft and sulfite hardwood pulps. However, the recovery of lignin from the alcohol/water extract or "black liquor", produced as a by-product of the solvent pulping process of U.S. Patent 4,100,016, has been relatively inefficient and difficult to control. Lignin has been recovered from the black liquor in this patent by first stripping (preferably vacuum stripping) alcohol from the black liquor and then separating the lignin which precipitates from the stripper bottoms or tails (preferably by thickening and then centrifuging the settled solids from the stripper bottoms). However, a portion of the lignin has tended to precipitate as a sticky tar or gum on the internal surfaces of the stripper, thereby fouling the stripper and reducing its efficiency in recovering alcohol from the black liquor. The lignin also has tended to precipitate from the stripper bottoms as a sticky amorphous mass which has been difficult to handle and has required substantial crushing to convert the lignin mass into a powder. As a result, more efficient ways have been sought for removing lignin from the black liquor produced by a solvent pulping process such as is disclosed in U.S. Patent 4,100,016. One method has involved precipitating lignin from the alcohol/water black liquor by diluting it with water, see Rydholm, "Pulping Processes", pp. 672-673. Interscience Publishers, New York (1971). However, this method has resulted in very slow settling rates of the lignin, and in some cases, a very stable collodial suspension of the lignin has been formed which has been difficult to filter or centrifuge. Tappi Journal, Vol. 68, No. 8, pages 94-97 describes the fractionation of hardwoods into pulp, lignin, and hemicellulose in a multi-stage alcohol extraction pilot plant by Organasolv Pulping. Lignin is obtained as a dry powder having a number average molecular weight of about 1000 and a polydispersity of about 3. SUMMARY OF THE INVENTION An aim of the invention is to provide a relatively simple way of recovering lignin from an alcohol/water black liqour in high yields and high rates in an easy to handle and useful form. This is achieved, in accordance with the invention, by a process for precipitating lignin from a solution of lignin in a water miscible organic solvent, characterized by diluting the lignin-containing solution with water and an acid to form a diluted aqueous solution with: a pH of less than 3, an organic solvent content of less than 30% (by volume), and a temperature of less than 75°C. The lignin, which precipitates from the diluted aqueous solution, can be dried to a powder which requires little or no crushing to convert it into a fine uniform size suitable for use without further significant processing. The lignin product of the above process, preferably has a number average molecular weight of 800 to 1500 g/mol and a polydispersity of less than 4. Further provided, in accordance with another aspect of the invention, is an apparatus for carrying out the process by precipitating lignin from, a black liquor, that is, an apparatus for pulping wood or other fibrous plant material with a water miscible organic solvent to produce a black liquor as a by-product and for subsequently recovering the solvent from the black liquor, characterized by: a) means for diluting the black liquor with an aqueous acid to precipitate lignin from the resulting diluted black liquor and leave a lignin-depleted supernatant; b) means for thereafter separating the precipitated lignin from the lignin-depleted supernatant; c) means for thereafter removing the organic solvent from the lignin-depleted supernatant to form a solvent- and lignin-depleted supernatant; and d) means for thereafter recycling a portion of the solvent- and lignin-depleted supernatant to the diluting means for use as the aqueous acid. BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is a flow chart of a process for producing cellulose pulp from wood by treating the wood with an aqueous alcohol solvent and for recovering lignin from the alcohol/water black liquor that is a by-product of the process. Fig. 2 is a schematic sectional view of an example of an apparatus for precipitating lignin from the alcohol/water black liquor from the process of Fig. 1. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS The process shown in Fig. 1 initially involves pulping a batch of wood chips that are loaded from a hopper 1 into an extractor 2. The extractor 2 is operated in accordance with the aforesaid U.S. Patent 4,100,016 at an elevated temperature (e.g., 180 to 210°C) and an elevated pressure (e.g., 20 to 35 atmospheres) and with a solvent comprising: 40 to 80% (by volume) of a water miscible lower aliphatic alcohol of 1 to 4 carbon atoms (e.g., methanol, ethanol, isopropanol or tert-butanol); 20 to 60% water; and if needed, a small amount of a strong water soluble acid, such as a mineral acid (e.g., hydrochloric, sulfuric, phosphoric or nitric acid) or an organic acid (e.g., oxalic acid). Preferably, the wood chips in the extractor 2 are preheated with low pressure steam, and then, a twice-used 60% ethanol/40% water, primary solvent from a primary solvent accumulator 3 contacts the wood chips in the extractor 2. The primary solvent is rapidly recirculated through the extractor 2 and through a peak load (e.g., steam-heated) heat exchanger 4 to raise the temperature of the wood chips to 190 to 200°C in a few (preferably not more than 5) minutes. After this first pulping step is completed, the resulting extract or "black liquor" in the extractor 2 is displaced into a recovery feed accumulator 5 by a once-used 60% ethanol/40% water, secondary solvent (preferably heated to 190 to 200°C) from a secondary solvent accumulator 6. At the end of this displacement, the secondary solvent in the extractor 2 is displaced into the primary solvent accumulator 3 by a fresh 60% ethanol/40% water solvent (preferably heated to 190 to 200°C) from a fresh solvent accumulator 7. The fresh solvent in the extractor 2 is then drained into the secondary solvent accumulator 6. Once the extractor 2 has been drained, it is vented, alcohol-rich vapors from the extractor are condensed in a water-cooled ("C.W.") condensor 8, and the resulting ethanol/water mixture from the condensor 8 is recycled to the fresh solvent accumulator 7. After venting the extractor 2, residual alcohol in the pulp in the extractor is then stripped with low pressure steam, and the resulting alcohol/water vapors are condensed and recovered as discussed below. After steam stripping, the pulp in the extractor 2 is sluiced with water, piped to a holding tank 9 and pumped through a pulp screen 10. The pulp can then be suitably subjected to conventional pulp handling, bleaching and paper-making procedures. The extractor 2 can be loaded with another batch of wood chips from the hopper 1, and the wood chips can be contacted by the primary, secondary and fresh solvents from accumulators 3, 6 and 7 as described above. The lignin, hemicelluloses, other saccharides and extractives (e.g., resins, organic acids, phenols and tannins) from the wood and the ethanol, which are all present in the black liquor at a temperature of 180 to 210°C and under a pressure of 20.2 to 35.4 bars (20 to 35 atmospheres) in the recovery feed accumulator 5, are then recovered by first flashing the black liquor into a flash tank 11 to recover part of the ethanol. The flash tank 11 can be at atmospheric pressure for simplicity of operation or at reduced pressure to further cool the black liquor and enhance the alcohol reovery. The reduction in pressure in the flash tank 11 causes partial vaporization of the ethanal and leaves the residual black liquor in the flash tank with an ethanol content of 30 to 45%, preferably 35 to 40%. The residual black liquor is cooled during this step to a temperature of less than 95°, preferably down to 80 to 92°, but not below 70° to avoid premature precipitation of lignin in the flash tank 11. The ethanol/water vapors obtained are condensed and recycled, along with any make-up ethanol, water and/or acid, to the fresh solvent accumulator 7 for use in treating subsequent batches of wood chips. Lignin is then separated from the residual black liquor, discharged from the flash tank 11, by the process of this invention. This step is carried out by diluting and preferably cooling the residual black liquor, as it leaves the flash tank 11, with water and acid to form a diluted residual black liquor with: a) an alcohol content of less than 30% (by volume), preferably 10 to 25%, particularly 12 to 21%, with an alcohol content of 8% being a practical minimum for subsequently recovering the alcohol economically; b) a temperature of less than 75°C, preferably less than 60°C, particularly 35 to 55°C; and c) a pH of less than 3, preferably less than 2.5, particularly 1.5 to 2.5. In this step, particular temperatures are not critical, although providing higher temperatures in the diluted residual black liquor will generally increase settling rates of the lignin but will yield a darker colored lignin and may decrease its yields. 75°C is a maximum temperature to avoid the formation of tarry lignin precipitates, and ambient temperature (e.g., 20°C) is a practical minimum, although lower temperatures (e.g., down to 0°C) can be used if low settling rates can be tolerated. Temperatures below 65°C, particularly below 60°C, provide a significantly lighter colored lignin precipitate. Also, particular pH's of the diluted residual black liquor are not critical in this step, but lower pH's increase the yield of precipitated lignin from the diluted residual black liquor and permit the use of higher temperatures in the diluted residual black liquor. However, lowering pH below 1 provides little or no additional improvement in yield, and for this reason, a pH of 1 is a practical minimum although lower pH's can be used. At a pH of less than 3, lignin will precipitate from the residual black liquor in high yield and at a high rate as fine solids. These lignin solids can then be separated from the remaining diluted residual black liquor supernatant in a conventional manner. Preferably, the lignin solids are separated by: allowing them to settle out as a paste of 6 to 12% (by weight) solids in a conventional clarifier or settling tank 12; then concentrating this paste of lignin solids in a conventional centrifugal separator 13 to form a wet cake of 30 to 40% solids; and then drying this wet cake to form a uniform fine, free flowing powder. In diluting the residual black liquor from the flash tank 11 with the water and acid to precipitate lignin, any conventional water soluble acid can be utilized which will provide the diluted residual black liquor with a pH of less than 3.0, preferably less than 2.50. For example, a strong mineral acid (e.g., hydrochloric, nitric, sulfuric or phosphoric acid) or a strong organic acid (e.g., oxalic acid) can be used. Preferably, the water and acid are mixed together before they are used to dilute the residual black liquor. In this regard, a particularly preferred mixture of acid and water is a residual black liquor supernatant that is derived from a previous batch of wood chips and that has been recycled and used to dilute the residual black liquor from the flash tank 11 after: a) the supernatant has been separated from the lignin solids from the previous batch of wood chips in the settling tank 12 and the centrifugal separator 13; and b) the alcohol content of the supernatant has been recovered in a conventional solvent recovery tower 14 provided with a conventional solvent condenser 15 as described below. This recycled residual black liquor supernatant or stripper bottoms, when used for diluting the residual black liquor from the flash tank 11, provides higher yields and faster settling of lignin solids precipitating in the settling tank 12 and centrifugal separator 13. In precipitating lignin from the residual black liquor from the flask tank 11, the method of diluting the residual black liquor with the water and acid also is not critical, so long as there is rapid and intimate mixing of the residual black liquor with the acid and water. For example, the residual black liquor can be suitably diluted by adding it to the acid and water in a conventional static dispersion mixer. The residual black liquor can also be diluted by adding it as a finely divided stream to a stream comprising a solution of the water and acid, for example, by means of a venturi-type device, generally 20, as shown schematically in Fig. 2. The residual black liquor from flash tank 11 in Fig. 1 can be pumped through a small nozzle 21 located at about the center of a pipe 22 in the venturi-type device 20 in Fig. 2, and the acid and water solution can flow in the pipe 22 towards the settling tank 12 in Fig. 1. As the residual black liquor is injected by the nozzle 21 into the acid and water solution in the pipe 22, the residual black liquor is rapidly diluted and cooled by the acid and water in the pipe 22. Lignin rapidly precipitates as fine solids from the resulting diluted residual black liquor in the pipe 22, which solids can be easily collected and concentrated in the settling tank 12 and centrifugal separator 13. In precipitating lignin in accordance with the above-described embodiment of the process of this invention, the yield and settling rates of the lignin are generally a function of: a) the wood species; b) the process conditions utilized in the extractor 2; c) the temperature, pH and solids content of (i) the residual black liquor from the flash tank 11 and (ii) the acid and water used to dilute it; and d) the ratio of residual black liquor to the acid and water used to dilute it. For example, the lignin from softwoods, such as spruce, is preferably precipitated at a temperature after dilution of 40 to 60°C using an acid and water solution with a pH of 1.5 to 2.5 and with a ratio of residual black liquor to the acid and water solution of 0.5 to 1. For hardwoods such as aspen, it is preferred to use an acid and water solution with a pH of 1.2 to 2.2 and a temperature after dilution of less than 50°C. In this regard, it is preferred to use a ratio of residual black liquor to the acid and water solution of: a) 0.2 to 0.8 if the temperature after dilution is above 40°C; and b) 0.6 to 1.0 if the temperature after dilution is less than 40°C (e.g., down to ambient temperature). For hardwoods, such as sweetgum, maple and oak, it is preferred to use a temperature after dilution of 40 to 60°C, an acid and water solution with a pH of 1.5 to 2.5, and a ratio of residual black liquor to the acid and water solution of 0.35 to 0.7. As shown in Fig. 1, the ethanol content of the clarified residual black liquor supernatant from the settling tank 12 and centrifugal separator 13 is preferably recovered in the solvent recovery tower 14 and solvent condenser 15. The ethanol content of the supernatant can be stripped (e.g., down to 200 ppm) in a conventional manner in the solvent recovery tower 14 at atmospheric pressure. Preferably, the tower 14 is heated by heating and recycling a portion of the bottoms stream from the tower 14 in a heat exchanger 24, using the low pressure steam used to strip residual ethanol from the pulp in the extractor 2. The ethanol/water vapors from the tower 14 are condensed in a conventional manner in the water-cooled condenser 15 (or by heat exchange with the stripper feed) and are then recycled to the fresh solvent accumulator 7 together with the ethanol/water mixture which condenses from the low pressure steam in the heat exchanger 24. The ethanol content of the supernatant from the settling tank 12 and centrifugal separator 13 can be suitably recovered in high yield in a simple manner, without lignin precipitating within the solvent recovery tower 14 and forming tarry or gummy deposits on the internal surfaces of the tower. A portion of the bottoms stream removed from the solvent recovery tower 14 is preferably concentrated in a conventional manner, for example, in multiple effect evaporators 26. In this step, scaling or fouling of the evaporation equipment is not a significant problem because there are no substantial amounts of high molecular weight lignin in the bottoms stream from the solvent recovery tower 14. The resulting syrup, containing hemicelluloses together with small amounts of other saccharides, extractives and very low molecular weight lignin (i.e., lignin with a molecular weight of less than 400 g/mol), can be burned to recover its fuel value, used as animal feed, or converted to other chemical products. A second portion of the bottoms stream removed from the tower 14 is preferably used as the acid and water solution for diluting the residual black liquor from the flash tank 11 in order to precipitate lignin therefrom. In this regard, the second portion of the bottoms stream from the tower 14 is preferably cooled to a temperature of less than 50°C, preferably 25 to 40°C (about 0°C being a practical minimum), and its pH is adjusted, if necessary, to 1.0 to 3.0 by adding a strong water soluble acid to it. Then, the cooled and acidified second portion of the bottoms stream (hereinbefore called the "recycled residual black liquor supernatant") is intimately and rapidly mixed (e.g., in the venturi-type device 20 of Fig. 2) with the residual black liquor to dilute and cool the residual black liquor and precipitate lignin. The very pure lignin, which precipitates as fine solids from the diluted residual black liquor in the settling tank 12, can be subsequently removed from the centrifugal separator 13, water-washed and dried in a conventional manner (e.g., by spin flash drying) to form a fine (e.g., _80 mesh) uniform, free flowing, water insoluble powder. This lignin can be characterized as having: a relatively low number average molecular weight of 800 to 1500 g/mol, preferably 900 to 1300 g/mol; a narrow molecular weight distribution, i.e., a polydispersity of less than 4, preferably no more than 3, particularly only 1.5 to 2.7; and a methoxyl content approximately equal to the methoxyl content of native lignin (i.e., 20% for hardwoods and 14% for softwoods). This lignin also has a glass transition temperature which is preferably 100 to 170°, particulaly 130 to 150°. These characteristics show, inter alia , the purity and low degree of chemical modification of the lignin as obtained by the process of this invention. This lignin can be used, for example, as a phenol formaldehyde resin extender in the manufacture of particle board and plywood. This lignin can also be used in the manufacture of molding compounds, urethane and epoxy resins, antioxidants, controlled-release agents and flow control agents. The process, product and apparatus aspects of this invention and many of their attendant advantages will be understood from, the foregoing description, and it will be apparent that various modifications and changes can be made in the process and apparatus for precipitating lignin without departing from the scope of these aspects of the invention of sacrificing all of their material advantages. The process and apparatus hereinbefore described being merely preferred embodiments. For example, the process of this invention can alternatively be carried out by separately adding an acid and water to a solution of lignin dissolved in a water miscible organic solvent to form a diluted aqueous solution with a pH of less than 3, an organic solvent content of les than 30% and a temperature of less than 75°C, from which diluted solution the lignin will precipitate as uniform fine solids. In this regard, the acid can be separately added to the residual black liquor from the flash tank 11 in Fig. 1 by adding the acid to the primary solvent from the primary solvent accumulator 3 before the primary solvent is used in the extractor 2 for pulping wood chips to produce the black liquor (which becomes, after removal of ethanol in the flash tank 11, the residual black liquor). Also, the process of this invention can be carried out with a water miscible organic solvent other than a lower aliphatic alcohol (preferably ethanol), such as acetone, glycol or glycerol, or with a mixture of such solvents. Also, this process can be carried out with lignin extracted from any fibrous plant material, such as bamboo, bagasse, and cereal straws, and not just wood.

Claims: 1. A process for precipitating lignin from a solution of lignin in a water miscible organic solvent, characterised by diluting the lignin-containing solution with water and an acid to form a diluted aqueous solution with a pH of less than 3, an organic solvent content of less than 30% by volume and a temperature of less than 75°C. 2. The process according to claim 1, characterised by providing the organic solvent content of the diluted aqueous solution in the form of a lower aliphatic alcohol of 1 to 4 carbon atoms. 3. The process according to claim 2, characterised by forming the diluted aqueous solution with a pH of less than 2.5. 4. The process according to claim 3, characterised by forming the diluted aqueous solution with a temperature of less than 60°C. 5. The process according to claim 4, characterised by forming the diluted aqueous solution with a temperature of 35 to 55°C. 6. The process according to claim 2, characterised by forming the diluted aqueous solution with an alcohol content of 10 to 25% by volume. 7. The process according to claim 6, characterised by forming the diluted aqueous solution with an alcohol content of 12 to 21% by volume and with a temperature of less than 65°C. 8. The process according to claim 6, characterised by forming the diluted aqueous solution with a temperature of less than 60°C and a pH of 1.5 to 2.5. 9. The process according to claim 8, characterised by forming the diluted aqueous solution with a temperature of 35 to 55°C and alcohol content of 12 to 21% by volume. 10. The process according to claim 1, characterised by using, as the water for diluting the lignin-containing solution, water which is in addition to water already present in the solution. 11. The process according to claim 10, characterised by intimately and rapidly mixing the lignin-containing solution with a mixture of the acid and the additional water to form the diluted aqueous solution. 12. The process according to claim 1, characterised by utilising, as the lignin-containing solution, a solution obtained by contacting wood or other fibrous plant material with the organic solvent at an elevated temperature and an elevated pressure to produce a cellulose pulp and a black liquor containing lignin and the organic solvent, and then separating the pulp from the black liquor. 13. The process according to claim 12, characterised by utilising the acid and water in a mixture which also contains hemicelluloses, other saccharides, extractives and lignin with a molecular weight of less than 400 g/mol. 14. The process according to claim 13, characterised by utilising, as the acid and water mixture, a recycled aqueous acid obtained by diluting the black liquor with the aqueous acid to form a diluted black liquor from which lignin is precipitated, leaving a black liquor supernatant; removing the organic solvent from the black liquor supernatant to produce a residual black liquor supernatant; and then recycling a portion of the residual black liquor supernatant for use as the aqueous acid in diluting the black liquor. 15. The process according to claim 14, characterised by utilising, as the organic solvent, a lower aliphatic alcohol of 1 to 4 carbon atoms. 16. The process according to claim 15, characterised by providing the diluted black liquor with a pH of less than 2.5. 17. The process according to claim 16, characterised by providing the diluted black liquor with a temperature of less than 60°C. 18. The process according to claim 15, characterised by providing the diluted black liquor with an alcohol content of 10 to 25% by volume. 19. The process according to claim 18, characterised by providing the diluted black liquor with a pH of 1.5 to 2.5 and a temperature of less than 60°C. 20. The process according to claim 19, characterised by providing the diluted black liquor with a temperature of 35 to 55°C and an alcohol content of 12 to 21% by volume. 21. The process according to claim 14, characterised by the fact that the black liquor contains water before it is diluted with the recycled aqueous acid. 22. The process according to claim 21, characterised by the fact that the black liquor is intimately and rapidly mixed with the recycled aqueous acid to form the diluted black liquor. 23. The process according to claim 15, characterised by providing the diluted black liquor with a temperature of 70 to 95°C and the recycled aqueous acid with a temperature of less than 50°C. 24. The process according to claim 23, characterised by providing the diluted black liquor with a temperature of 80 to 92°C and the recycled aqueous acid with a temperature of 25 to 40°C. 25. An apparatus for pulping wood or other fibrous plant material with a water miscible organic solvent to produce a black liquor as a by-product and for subsequently recovering the solvent from the black liquor, characterised by: a) means for diluting the black liquor with an aqueous acid to precipitate lignin from the resulting diluted black liquor and leave a lignin-depleted supernatant; b) means for thereafter separating the precipitated lignin from the lignin-depleted supernatant; c) means for thereafter removing the solvent from the lignin-depleted supernatant to form a solvent- and lignin-depleted supernatant; and d) means for thereafter recycling a portion of the solvent- and lignin-depleted supernatant to the diluting means for use as the aqueous acid. 26. The apparatus according to claim 25, characterised by the fact that the diluting means is associated with means for removing a portion of the solvent from the black liquor before diluting the black liquor. 27. The apparatus according to claim 26, characterised by the fact that the recycling means is associated with means for adding a strong water soluble acid to the solvent- and lignin-depleted supernatant before recycling it to the diluting means. 28. The apparatus according to claim 25, characterised by the fact that the diluting means includes an arrangement for intimately and rapidly mixing the black liquor with the aqueous acid.

Inventors: CRONLUND, MALCOLM, KATZEN, RAPHAEL, LORA, JAIRO H., WU, CHIH FAE
Applicants: REPAP TECHNOLOGIES INC.
Application year: 1986
Main classification: C07G1
IPC codes: C08H3, C07G1, D21C11, C07D307, C08H5