Method for thermoelectric conversion

Abstract: The disclosure is directed to a method for converting between heat energy and electric energy which is characterized in that a carbon intercalation compound is employed as a thermoelectric material by utilizing temperature difference in a direction perpendicular to the structure of carbon layers, or a method for producing a light-heat converting material which is characterized in that a thin metallic layer like a translucent mirror is caused to adhere to the inner surface of a light transmissive hollow tube by pyrolytically decomposing at a temperature approximately below 1000°C, with hydrocarbons being introduced into the hollow tube (3) at the rate of a predetermined amount an hour.

Description: The present invention generally relates to a method for converting energy to a different kind of energy, for example, a method for generating electric energy from a temperature difference and vice versa and more particularly, to a method for converting between heat energy and electric energy by employing a carbon intercalation compound as a thermoelectric material. It is well known that figure of merit Z is valued for a thermoelectric performance representing a conversion efficiency between heat energy and electric energy. Z-value is estimated by a formula, Z = α²/ρκ , where α is a Seebeck coefficient or a thermoelectric power (µVK⁻¹), ρ is an electrical resistivity (Ωcm) and κ is a thermal conductivity (Wcm⁻¹K⁻¹). Accordingly, it is obvious that large α, small ρ and small κ are required for obtaining a large figure of merit Z. On the other hand, in addition to the above conditions, the thermoelectric material is required to have reliable PN controllability of its own. Furthermore, when used as a thermoelectric generator, the material is required to be operable at high temperatures so as to achieve high thermodynamic efficiency, or when used as a thermoelectric refrigerator, the material is required to realize PN-junction with high heat insulating properties. Conventionally, such various compounds as single-crystalline silicon semiconductor, bismuth or antimony chalcogenides, polycrystalline transition-metal silicides, amorphous bismuth chalcogenides or the like are known as typical thermoelectric materials. However, among graphite intercalation compounds, only one has been found to be used as the thermoelectric material This is carbon fiber and is used as a thermoelectric generator utilizing a temperature difference in the axial direction of fibers wherein an alkali metal or bromine is inserted between carbon layers of carbon fiber. There have been, however, two drawbacks in this practice. That is, since the axial direction of fibers is parallel to the in-plane direction of a graphite structure, not only an electrical conductivity but also a thermal conductivity are large and accordingly, inexhaustible high and low heat sources are required for thermoelectric generation, and this results in limited utilization for such kind of thermoelectric material. In the next place, since alkali metal (potassium) or halogen (bromine) having high reactivity is employed as an intercalant for the graphite intercalation compound, the thermoelectric material is easily deteriorated by moisture or oxygen in air. US-A-3 330 703 discloses a graphite intercalation compound for converting heat energy and electric energy. The energy convertion is carried out by using a temperature difference in a direction perpendicular to the structure of graphit layers of said graphite intercalation compound. Accordingly, an essential object of the present invention is to provide a highly effective method utilizing anisotropy of the carbon intercalation compound, for converting energy between heat energy and electric energy whereby electric energy can be generated from a temperature difference in a direction perpendicular to graphite layers of said carbon intercalation compound, or the temperature difference in a direction perpendicular to the layers can be generated from electric energy. In accomplishing these and other objects, according to one preferred embodiment of the present invention, there is provided a method of converting energy between heat energy and electric energy according to the claim. Fig. 1 is a block diagram of an apparatus for producing a carbon intercalation compound, which is employed for producing a thermoelectric material according to the present invention. Semiconductor or semi-metal is generally employed because of easiness of PN control as the thermoelectric material. For example, although a silicon semiconductor is readily PN-controlled, it has a thermal conductivity approximately a quarter of that of copper at room temperature and it seems difficult to improve this value. Furthermore, it is impossible in principle to alter the thermal conductivity and the electrical conductivity independently due to cubic symmetry of the above described semiconductor. On the contrary, the GIC (graphite intercalation compound) can be of the p-type or n-type by arranging a donor or an acceptor type intercalant between carbon layers and it is capable of obtaining the thermoelectric material wherein the electrical conductivity and the thermal conductivity can be altered independently to some extent. Various kinds of intercalants are known so far and various kinds of graphite intercalation compounds have been produced. However, since each of such kinds of intercalant layers is bound between the graphite layers by a weak bonding force (van der Waals force or charge transfer force), it tends to easily get free from between the carbon layers in air or in moisture. In order to materialize the thermoelectric material which is characterized by the anisotropy peculiar to carbon intercalation compound, it is necessary to interrupt the movement of the intercalant for fixation thereof. This can be realized by the carbon intercalation compound. In the carbon intercalation compound, carbon atoms having SP³-bond are scattered among a great majority of carbon atoms having SP²-bond to maintain the graphite structure and act to fix the intercalants which are intercalated at the same time when the carbon structure is formed. In the next place, the performance index number of the thermoelectric material employing the carbon intercalation compound will be explained in detail hereinafter. Upon comparative examination of a variety of thermoelectric materials, it is conjectured that an electrical resistivity thereof is adequate to be 10⁻³ Ωcm. Graphite has both of a resistivity component (ρ ∥ ) parallel to the layers and that (ρ l ) perpendicular thereto, and ρ ∥ = 5 x 10⁻⁵ Ωcm and ρ l = 0.5 Ωcm . It is well known that the resistivity can be lowered by more than one figure through intercalation. On the other hand, in carbon intercalation compound, the electrical anisotropy is adequately lowered by a small amount of carbon atoms having SP³-bond and as a result, the resistivity of 10⁻³ Ωcm can be easily obtained. At around room temperature, an artificial graphite has thermal conductivities, κ ∥ = 0.8 Wcm⁻¹K⁻¹ and κ l = 2 x 10⁻² Wcm⁻¹K⁻¹ . When the intercalants are introduced between the layers of host graphite, it has been reported that κ l can be lowered by 10⁻² to 10⁻³ times. Accordingly, in the carbon intercalation compound, the thermoelectric material having thermal conductivity in the range of 10⁻² to 10⁻⁴ Wcm⁻¹K⁻¹ can be obtained. Furthermore, the thermoelectric material having lowered thermal conductivity below 10⁻³ Wcm⁻¹K⁻¹ can be easily obtained by choosing a heavy metal as an intercalant. Thus, upon utilization of the anisotropy of the carbon intercalation compound, the thermoelectric material having the electrical resistivity ρ = 10⁻³ Ωcm and thermal conductivity κ = 10⁻³ Wcm⁻¹K⁻¹ can be materialized by adjusting the kind and/or the concentration of the intercalant and an existing ratio of carbons having SP³-bond relative to those having SP²-bond. Subsequently, since the thermoelectric power is a significant physical quantity for the thermoelectric material, it will be described hereinafter. The coefficient graphite shows such an extremely small thermoelectric power as 5 µVK⁻¹ at room temperature, with respect to the temperature difference in the graphite layers. It is, however, well known that when antimony pentachloride is intercalated to the extent far below a saturated value (10th-stage), the thermoelectric power thereof is increased to 40 µVK⁻¹. Furthermore, it has been reported in case of organic charge-transfer complexes that charge-transfer force is a driving force which causes a large thermoelectric power and the value of thermoelectric power is concretely shown by several mVK⁻¹. Hereupon, when the carbon intercalation compound having α = 10⁻³VK⁻¹ , ρ = 10⁻³ Ωcm and κ = 10⁻³ Wcm⁻¹K⁻¹ is employed for the thermoelectric material, the thermoelectric material having Z = 1K⁻¹ can be obtained and this value is 100 to 1000 times larger than the conventional Z-value. In the next place, a method for producing the above described thermoelectric material will be explained hereinafter. Since graphite is a semi-metal having approximately the same number of electron carriers and hole carriers, if atoms or compounds having electron donating characteristic or electron accepting characteristic can be intercalated into this semi-metal, N-type or P-type electrical conductive material can be materialized. The intercalant layer has a staged structure alternating with the graphite layers. The carbon intercalation compounds can be bulk-produced with reliable reproducibility by introducing at a same time atoms or compounds to be intercalated in the process wherein carbon deposit having metallic luster is elaborated by employing a CVD method for hydrocarbons. Fig. 1 shows a block diagram of an apparatus for producing the carbon intercalation compound, which is employed to produce the thermoelectric material according to the present invention. A hydrocarbon compound such as aliphatic hydrocarbons, or more preferably aromatic hydrocarbons can be used as starting materials and these kinds of hydrocarbons are pyrolytically decomposed at approximately 1000°C. Concretely, such a hydrocarbon can be used as cyclohexane, n-hexane, benzene, biphenyl, anthracene, hexamethylbenzene, 1,2-dibromoethylene, 2-butyne, acetylene, diphenylacetylene or the like. Depending upon the kind of hydrocarbon to be used, one of a bubbling method, an evaporation method, a sublimation method or the like method can be employed as a supplying method into a reaction tube which is later explained in detail, and the supply rate is controlled to be constant below several millimols an hour. This constant value considerably depends upon the kind of the starting material. When the supply rate exceeds the predetermined constant value, the carbon deposit obtained has a fairly uneven surface which results in the production of soot-like carbon deposit. Silicon, sapphire, silicon carbide (α-type and β-type), boron nitride, kish graphite, highly orientated graphite or the like is used as a single-crystalline substrate on which the thin carbon film is formed and the single-crystalline substrate is required to satisfy conditions in which its property is not changed at the reaction temperature of approximately 1000°C. In Fig. 1, benzene is selected as a starting material and the evaporating method is employed for producing the thermoelectric material. Vapor of benzene molecules is led to a quartz reaction tube 3 through a pyrex glass tube 2 from a raw material receptacle 1 wherein benzene purified through vacuum distillation is accommodated. Upon operation of cocks 4, benzene molecules vaporized from the raw material receptacle 1 is supplied to the glass tube 2 and the amount thereof to be supplied is determined by means of a glass capillary 5 arranged on the glass tube 2. Furthermore, an organometal reagent comprising heavy metal accommodated in a chamber 6 is mixed with benzene molecules in the course of the glass tube 2 so as to be simultaneously fed into the reaction tube 3 together therewith. The glass tube 2 is covered with a heating tape 7 so as to be kept at its desired temperature and is connected with the reaction tube 3 through a pyrex-quartz conversion joint. The reaction tube 3 is inserted into a heating furnace 9 so as to be heated up to the reaction temperature and a substrate holder 10 is disposed in the reaction tube 3 for placing a single-crystalline substrate thereon, which enables the carbon deposit to grow up. The remaining vapor led to the reaction tube 3 is discharged outside through a discharge pipe 11. Inside of the reaction tube 3 is kept at a temperature of approximately 1000°C by the heating furnace 9 and thereafter, benzene molecules which are controlled in the supply rate thereof by the capillary 5 and the molecules of the organometal comprising heavy metal are supplied to the reaction tube 3 by a constant amount at the rate of several millimols in total an hour. Benzene molecules led into the reaction tube 3 are pyrolytically decomposed at the above described temperature and the carbon deposit having metallic luster are formed on the single-crystalline substrate. At this moment, since the organometal comprising heavy metal is also pyrolytically decomposed and heavy metal atoms are intercalated between the layers of carbon deposit, the carbon deposit obtained is the carbon intercalation compound composing the above described thermoelectric material. The carbon intercalation compound produced is a thin layer which has received a desirable crystallization under the influence of the single-crystalline substrate and is highly orientated at a lowered temperature as compared with that of conventional case. In addition, benzene molecules led into the reaction tube 3 and the organometal molecules are controlled at a constant amount, and the carbon deposit produced on the single-crystalline substrate is even in thickness and accordingly, the carbon deposit having an improved crystallization can be obtained, with the surface thereof having metallic luster. As is seen from the foregoing description, by the converting method between heat energy and electric energy which utilizes the anisotropy of the carbon intercalation compound, the figure of merit of the thermoelectric material which is more than 100 times larger than the conventional number can be obtained, and a considerably desirable effect can be expected in case of thermoelectric generation or thermoelectric cooling. It is also to be noted that although the evaporating method has been explained above as a method for producing the thermoelectric converting material, the present invention is not limited by this method and various kinds of liquid transfer methods in which the flow amount can be relatively precisely adjusted can be employed for the same purpose, for example, a bubbling method in which raw material liquid is bubbled by injecting inert gas such as argon gas or the like into a raw material such as hydrocarbon or the like and thereby raw material molecules are led into the reaction tube 3 together with the inert gas, or a sublimation method in which raw material is sublimated so that the vapor thereof is transferred, can be employed for producing the thermoelectric converting material. One of the above described methods can be properly selected in accordance with a melting point or a boiling point of the hydrocarbon to be used.

Claims: A method of converting energy between heat energy and electric energy by a carbon intercalation compound composed of a majority of carbon atoms having sp²-bond to maintain a graphite structure, carbon atoms having sp³-bond scattered among said majority of carbon atoms to fix intercalants, and the intercalants as energy converting material, said method comprising the steps of: preparing a thin film of said carbon intercalation compound on a single-crystalline substrate by pyrolytical decomposition of a hydrocarbon compound and an organo metal reagent comprising heavy metal atoms; using a temperature difference in a direction perpendicular to the graphite layers of said carbon intercalation compound to generate electric energy; or using electric energy to generate a temperature difference in said direction perpendicular to the graphite layers.

Inventors: HIGASHIGAKI YOSHIYUKI, INOGUCHI TOSHIO, NAKAJIMA SHIGEO, SUZUKI TOMONARI, YOSHIMOTO YOSHIKAZU, HIGASHIGAKI, YOSHIYUKI, INOGUCHI, TOSHIO, NAKAJIMA, SHIGEO, SUZUKI, TOMONARI, YOSHIMOTO, YOSHIKAZU
Applicants: SHARP KK, SHARP KABUSHIKI KAISHA
Application year: 1986
Main classification: H01L35
IPC codes: H01L35