METHOD OF FORMING SOLDER TERMINALS FOR A PINLESS CERAMIC MODULE

Abstract: Disclosed is a method of forming solder terminals for a pinless ceramic module. The method is comprised of the following steps: a) forming a Metallized Ceramic (MC) substrate (11) having a pattern (12) of conductors formed onto its top surface (13) and an array of preformed via-holes (14), said conductors being terminated by eyelets (15) at the location of said via-holes; b) applying where desired a droplet of flux at each preformed via-hole opening of the bottom surface of the MC substrate to fill the via-holes by capillarity and form a glob of flux (19) at each opening; c) applying a solder preform (20) on each glob of flux to which it will adhere because of the adhesive property of the flux, the volume of the preform being substantially equal to the inner volume of the via hole plus the volume of the bump to be formed; d) heating to cause a solder reflow of the solder preform to fill the via-hole, and the inner volume of the eyelet with solder; and, e) cooling below the melting point of the solder whereby the molten solder solidifies to form solder terminals at each via-hole location simultaneously forming a solder column in the via-hole, a solder mound (23) at the top surface of the MC substrate which makes electrical connections with said eylets and solder bumps (22) at the bottom surface of the MC substrate (11).

Description: Technical Field The present invention relates to the solder bonding of electronic modules to metallized bodies and more particularly to a method of forming solder terminals for Metallized Ceramic (MC) modules having solder bumps appropriate for direct and easy surface mounting onto metallized bodies such as Printed Circuit Boards (PCB's) or Printed Wiring Boards (PWB's). Background of the Invention The basic Metallized Ceramic (MC) substrate process begins with a ceramic square on the top surface of which, metallurgical strata of chromium for adhesion, copper for conduction, and chromium for a solder flow barrier, are deposited. A pattern of conductors is defined in the strata by a photolithographic process using standard photoresist techniques and sequential etching methods. The pattern forms a wiring that will subsequently connect the semiconductor chip solder bumps to the input/output (I/O) pins. The pins provide electrical and mechanical connections with the outside world. The pins are inserted through preformed via-holes in the MC substrate and are mechanically swaged in place to form a bulge. Preformed via-holes are disposed in an array which may have various patterns. The ends of the conductors at those points where pins are provided take the form of eyelets. The heads of connecting pins previously inserted in the MC substrate are bonded to the eyelets of conductors formed on the top surface simultaneously with the bonding of the semiconductor chip to the conductors. The preferred method of bonding the head of connecting pins comprises the steps of: applying a droplet of flux to the head of the pin, then applying a solder ball to said head where it is held in position because of the adhesive capacity of the flux, heating in a furnace containing a nitrogen atmosphere to cause a solder reflow and cooling to enable the solder to solidify. The method is described in details in USP No. 4 462 534 entitled "Method of Bonding Connecting Pins to the Eyelets of Conductors Formed on a Ceramic Substrate", authored by A. Bitaillou et al and assigned to the same assignee as that of the present invention. The chip is attached to the substrate using the "Controlled Collapse Chip Connection" (C-4) process developed for tin-lead interconnections, also known under the generic name of "Flip Chip" technique. A polyimide coating is applied to the top surface, an aluminum cap is placed over the assembly, and an epoxy sealant is dispensed on the underside as a liquid and cured to provide a "quasi-hermetic" seal. After it has been marked and tested, the completed module is then ready for attachment to the appropriate second level package, such as a PCB. MC technology is a simplified version of the well known Multilayer Ceramic (MLC) technology. Compared to the MLC technology which appears to be only appropriate for use in medium and high performance computers, the MC technology aims preferably at more specific applications such as various peripherals, including banking machines..., personal computers, etc... where low cost and simplicity are a must. One of the problems associated with MC technology is related to the use of said pins. These pins are elongated in shape and require perforated PCB's, i.e. PCB's provided with plated via-holes to receive the pins before bonding. Their handling, and automatic insertion into said plated via-holes still remain a problem and are a serious detractor of manufacturing yields. In addition, perforated PCB's are costly and much space is lost due to the presence of said plated via-holes to receive the corresponding pins. Generally the diameter of the elongated pins before tinning is about .6 mm, while the plated via-holes in the PCB have a diameter of about 1 mm. Due to the in ternal construction of the PCB, it is almost impossible to reduce the standard center to center distance of 2.54 mm. Should the use of pins be avoided, perforated PCB's would no longer be necessary and increased density could be reached, because the center to center distance could be reduced to less than 1.27 mm, therefore considerably increasing the number of I/O's permitted on the same surface of the PCB. Further, as the number of pins increases, the operation of inserting the module into the PCB, becomes more difficult, and the likelihood of having pins bent during this step increases too. Lastly, when pins are used as I/O's, the module comes into close contact with the PCB leaving no clearance between them, unless costly stand-offs are provided to the pins; as a result, the cooling of the module is poor. Another problem is that the use of modules having pins as I/O's, in combination with perforated PCB's, prevents bonding of MC modules on both sides of the PCB's. Still another problem raised by the use of such a great number of pins is the difficulty of reworking the module, to make engineering changes. However this technology is still highly appreciated mainly because it provides a great number of I/O's, still useful for present and future VLSI chip packaging. On the other hand, today's packaging techniques are evolving towards the extensive usage of Surface Mount Techniques (SMT) in order to improve the density of circuits at the card level and reduce packaging costs. According to SMT technology, perforated PCB's are no longer used and the terminals of modules are directly bonded to the desired metal lands of the PCB. Commonly used Surface Mount modules such as just mentioned above are provided with peripheral I/O's. In this case the I/O's consist of metal leads bent under the bottom surface of the module that come into contact with the metal lands formed at the surface of the PCB. The cost of these modules becomes rapidly prohibitive when the number of I/O's increases to a high count (typically: 100 to 300) because of the amount of area required. For example, for a given technology, doubling the number of pins leads to a fourfold increase in module area with a similar loss of card area, and a degradation of the module electrical characteristics (inductances, resistances...) which in turn, results in parasitic effects. On the contrary, it is obvious that a module with I/O's placed on a gridded pattern would be more efficient in terms of handling large numbers of I/O's; for example, an increase of I/O count by a factor of two will result in a more reasonable factor of two for the module area. The system designer would then be able to take full advantage of the card density and optimization, and thus cost as well as the resulting electrical performances would be significantly improved. As a matter of fact, a pinless MC module having I/O's placed according to a grid pattern at the center of the bottom surface (opposite to said top surface) of the MC substrate or even occupying the whole bottom surface, would be a highly desirable solution in all respects. An attempt to provide a pinless MC module is described in the IBM Technical Disclosure Bulletin, Vol. 20, No. 10, March 1978, page 3872, in an article entitled: Pinless Module Connector, authored by E. Stephans. An electronic package is shown which includes a printed-circuit card, a metallized ceramic (MC) substrate, and an integrated circuit attached thereon. In this package, the integrated circuit is connected to the MC substrate by small solder joints in a standard way. The solder joints are usually spherical and have a diameter in the order of .1 mm. Unlike the conventional connection between the MC substrate and the PCB by elongated pins, according to the teachings of that disclosure, the MC substrate is connected to the PCB by copper balls. These balls are approximately 1,5 mm in diameter. The package can be fabricated by attaching the copper balls to the MC substrate with conductive epoxy which fills the preformed via-holes of the MC substrate. After the copper balls are attached to the MC substrate, the latter is placed on the PCB. The copper balls are then surface soldered to the metal lands formed on the top surface of the PCB. The described solution, although resulting in a pinless MC module appears to present some obvious drawbacks and insufficiencies. The technique of filling the preformed via-holes of the MC substrate is not detailed. Moreover, conductive epoxy is known to be a relatively high resistive material, therefore, the quality of the electrical connection between the conductive epoxy and the metallization pattern formed onto the top surface of the MC substrate is questionable. In addition, the sticking of the copper ball to the conductive epoxy raises some unsolved problems, in particular the alignment of the ball with the via-hole and the reliability of the composite bond between the epoxy and the ball is not assessed. Furthermore, the possibility of reducing the copper ball size is questionable. The behavior of this composite bond during thermal stresses caused by the different dilation coefficients between the MC substrate and the PCB, has not been studied either. Therefore, there still exists a need for a method of forming pinless MC modules having I/O's placed on a gridded pattern at the center of the bottom surface even the whole bottom surface, which obviates all the problems cited above. Summary of the Invention The foregoing problems are solved by the method of the present invention as defined in claim 1. As a consequence, pins are no longer used as I/O's but are replaced by solder terminals. According to the invention, such a solder terminal is comprised of three parts: a solder column which fills the via-hole, a solder mound at the top surface which makes an electrical connection with the corresponding eyelet, and at the bottom surface a bump-shaped protuberance to be used for interconnection with metal lands of the PCB. All parts are integral and formed simultaneously. According to that particular embodiment, a method is described of forming solder terminals on a pinless MC module having solder bumps appropriate for Surface Mounting Techniques, said modules to be bonded onto Printed Circuit Boards (PCBs) and cards. The method is comprised of the following steps: a) forming a Metallized Ceramic (MC) substrate having a pattern of conductors formed onto its top surface and an array of preformed via-holes, said conductors being terminated by eyelets at the location of said via-holes; b) turning the MC substrate upside down so that the bottom surface faces up; c) applying where desired a droplet of flux at each preformed via-hole opening on the bottom surface of the MC substrate to fill the via-holes by capillarity and form a glob of flux at each opening on the bottom surface (17); d) applying a solder preform on each glob of flux to which it will adhere because of the adhesive property of the flux, the volume of the preform being substantially equal to the inner volume of the via hole plus the volume of the bump to be formed; e) heating to cause a solder reflow of the solder preform to fill the via-hole and the inner volume of the eyelet, with solder; and, f) cooling below the melting point of the solder whereby the molten solder solidifies to form solder terminals at each via-hole location simultaneously forming a solder column in the via-hole, a solder mound at the top surface of the MC substrate which makes electrical connections with said eyelets and solder bumps at the bottom surface of the MC substrate. Details on the method are disclosed in the sub claims. A primary advantage of the method of the present invention is to produce pinless (or leadless) electronic modules, typically MC modules where all the problems related to the pin handling and pin inserting, in addition to the use of perforated PCB's are alleviated, therefore allowing such a pinless electronic module to fully comply with SMT requirements. Another advantage of the method of the present invention is to provide solder terminals to MC substrates eliminating the conventional steps of pin inserting and swaging. Another advantage of the method of the present invention is to provide solder terminals to MC substrates terminated with solder bumps formed on its bottom surface, therefore permitting easy repair and rework. Another advantage of the method of the present invention is to provide solder terminals for MC substrates terminated with solder bumps to be bonded to the corresponding metallization lands of a PCB by forming solid solder joints. Another advantage of the method of the present invention is to provide solder terminals to MC substrates terminated with solder bumps formed on its bottom surface according to a very dense grid pattern, either at the center of said bottom surface of the MC substrate or on the whole surface of it. Another advantage of the method of the present invention is to provide solder terminals to MC substrates terminated with solder mounds to make electrical connection with the eyelets of the conductors formed onto the top surface of the MC substrate. Yet another advantage of the method of the present invention is its tolerance to absorb thermal stresses caused by the unusual height of the solder terminal which is very important in this case (equal to the diameter of the solder bump plus the height of the solder column (thickness of the ceramic substrate). Yet another advantage of the method of the present invention is to provide solder joints between the MC substrate and the metallization lands of a PCB having non negligible height to improve the cooling of the MC module. A further advantage of the method of the present invention is its flexibility in the tight control of the dimensions and the nature of the solder bumps, by using solder balls of different volumes and compositions. A still further advantage of the method of the present invention is its ability to be easily installed in any manufacturing line, and to produce reliable products with high throughputs. These and other advantages of the present invention will appear more fully upon consideration of the various illustrative embodiments, to be now described in detail in connection with the accompanying drawings, forming a material part of this disclosure. Brief Description of the Drawings Fig. 1 is a schematic perspective view of a portion of an MC module the cap of which has been removed and shows the ceramic substrate with its pattern of conductors thereon, just before the conventional pinning step. Fig. 2A to 2C are cross sectional views of the ceramic substrate of Fig. 1 taken along line 2-2, during various steps of fabrication in accordance with a preferred embodiment of the method of the present invention. Fig. 3 is a schematic perspective view of the ceramic substrate of Fig. 1 after formation of solder terminals. Detailed Description Fig. 1 of the drawings illustrates a partially exploded view of a portion of a typical Metallized Ceramic (MC) module 10 in which the concept of the present invention can be applied. The module 10 can be of any suitable size to accommodate the desired number of chips: e.g. 36 × 36 mm, thickness about 1 mm. The module comprises a ceramic substrate 11 provided with a pattern of metal conductors 12 on its top surface 13. One end of each conductor 12 that corresponds to a via-hole 14 (into which an elongated pin is inserted according to the standard process), is enlarged and forms an eyelet 15. At the opposite extremity, each conductor is shrunk to form a finger like structure (not represented ). Said fingers are disposed according to a first array, adapted to be joined to a corresponding array of solder bumps of a semiconductor chip 16. Similarly, the via-holes 14 are disposed according to a second array. It will be appreciated that various arrays can be imagined. The bottom surface 17 may also be provided with a metallization pattern. The material e.g. ceramic of the substrate 11 is chosen for good mechanical, electrical and thermal properties so that the thermal expansion is a reasonably close match to the silicon material of the chips to be mounted on the top surface of the substrate. As shown in Fig. 1, during the formation of the pattern of metal conductor by evaporation of metals mentioned above on the top surface 13, the totality of the sidewalls of the via-holes 14 is metallized by a composite chromium-copper layer, so that the eyelet 15 is a rivet like structure with an annular copper ring 18 formed inside the via-hole. However complete metallization of the via-hole sidewalls is obtained only if a thin ceramic substrate 11 is used (thickness of about 1 mm). Then, the above mentioned metal ring is sufficient to make the inner walls of the via-hole wettable by the solder to be subsequently applied. If a thicker ceramic substrate (1.5 mm) were used, it would be necessary to provide a complementary plating of said inner walls. The technique described in US Patent No. 4 024 629 "Fabrication techniques for MLC modules", issued to J.M. Lemoine et al and assigned to the same assignee as that of the present invention, could be used in that respect. The method of the present invention will be now described with reference to Figs. 2 A to 2C. The technique described hereafter is based on the teachings of above mentioned US Patent No. 4 462,534. A minor improvement thereof has been published in the IBM Technical Disclosure Bulletin, vol. 27, No. 10B, March 1985, pp 6252-6253, an article entitled: "Ball Placement Improvement for Untinned Substrate Process" by A. Bitaillou et al. Both disclosures are incorporated by reference herein, the main steps of which will be briefly summarized hereafter. Only the significant differences between the method of the present invention and the prior art techniques will be detailed. The first step of the process consists in dispensing droplets of flux to be applied at the openings of the desired preformed via-holes. The flux dispensing device schematically shown in Fig. 2 of US Patent 4 462 534 is appropriate to reduce to practice the method of the present invention. According to the latter patent, a flux, such as: Benzylic 102-1500 manufactured by the Alpha Metals Co. with a viscosity of about 20 Pa.s (200 poises) is appropriate. The flux is contained in a Teflon tank housed in a stainless steel cylinder, the removable bottom of which, consisting of a wire cloth, forms a fluxing mask. The holes in the mask are arranged in a pattern corresponding to the array of via-holes. The flux will be forced to flow through these holes during the dispense step. The pressure within the tank is established by a vacuum system controlled, for example, by a logic circuit or by the analog output from a processor. The MC substrate is positioned onto a support fitted with locating pins, its top surface 13 down and the bottom surface 17 is now turned upwards. The flux remains in the tank while the latter is being positioned over the substrate and aligned therewith, and is then released by means of an air pulse supplied by the vacuum system. Each opening of the via-holes of bottom surface 17 creates a sink which attracts the flux. Fig. 2A which is a cross sectional view of the substrate shown in Fig. 1 along line 2-2, shows that each droplet of flux applied to the via-holes 14, fills completely the via-hole by gravity and capillarity, leaving a glob 19 of flux at the opening of the via-holes on the bottom surface 17 now turned upwards. It is to be noted that because the pins (.6 mm of diameter) are no longer used, the via-hole diameter may also be reduced, thus increasing the wiring density on both the top and bottom surfaces. The second step consists in the dispense of solder preforms onto said globs of flux. Because solder balls are the preferred preforms, the other devices also described in US Patent 4 462 534 may also be used to cause a solder ball to be dispensed and applied to any via-hole opening where desired, to which it will then adhere because of the adhesive capacity of the glob of flux deposited thereon during the first step. The solder balls selected for this application are 1 mm in diameter and the solder is an alloy of Pb-Sn (90/10). In view of their light weight, the solder balls should be agitated before they are drawn by suction. To this end, the solder balls are initially placed in a bowl that is caused to vibrate using a vibrating device as shown in Fig. 4A of US Patent 4 462 534. The bowl should be made of some elastic material so as to allow the balls to bounce. Polyethylene was found to be quite satisfactory for this purpose. The vibrations alone proved insufficient to cause the solder balls to bounce. The optimum number of solder balls to be placed in the bowl was determined to correspond to a single layer of solder balls at the bottom of the bowl when not vibrated. In the preferred embodiment mentioned earlier, the bowl is a parallelepiped with a square base (70 mm × 70 mm) and a height of 80 mm. The vibrating device comprises a plate resting on two oblique springs and an electromagnet which causes said plate to vibrate. Under the above conditions, the bouncing solder balls reach a height of about 20 mm. Other means could of course be employed for vibrating the solder balls, such as a container having a porous bottom and receiving compressed air. Fig. 4B of US Patent 4 462 534, shows a suction device which sucks up the moving solder balls contained in the vibrating bowl and dispenses to the previously fluxed substrate. The device comprises a soft iron frame which may be of circular shape and defines a suction chamber connected by a tube to a controlled vacuum system. An electromagnet surrounds said tube and is fed from a main supply (50 Hz) through a diode. The suction chamber is closed by a suction mask fitted with a rod, the far end of which is located within the air gap of the electromagnet. The mask consists of a perforated membrane 0.1 mm in thickness that is made of an alloy of beryllium and copper. The holes in the membrane are 0.4 mm in diameter and also correspond to the array of preformed via-holes of the MC substrate. The operation of the devices shown in Figs. 4A and 4B of US Patent 4 462 534 is as follows. The device is first operated to cause the solder balls in the bowl to vibrate. The device previously connected to the vacuum source, is then inserted in the vibrating bowl such that the distance between the suction mask and the bottom of the bowl is about 5 mm. The time necessary for all the solder balls to be sucked up is of about 1 second. The suction device, including the mask with which the solder balls are maintained in contact by the vacuum, is then removed from the bowl and positioned over the substrate so that the pattern of solder balls and the pattern of globs of flux are aligned; however, it does not matter if the patterns are slightly offset with respect to each other. It is just necessary to ensure that each ball lies over at least a portion of the corresponding glob of flux. The mask may be aligned through the use of locating pins provided on the support on which the electronic substrate rests and which fit into matching cavities in the frame of the device. The solder balls are thus brought into contact with the corresponding globs of flux. The vacuum system is then turned off, and the electromagnet is energized for about half a second to cause the membrane to vibrate. As a result, the solder balls separate more easily from the membrane while continuing to adhere to the via-hole openings because of the flux thereon. Fig. 2B illustrates the configuration of the solder balls 20 on the MC substrate 11 and clearly shows that in some instances a slight offset between the opening of the via-hole and the attached solder ball 20 may happen. In the third step, the ceramic substrate is then introduced in a conventional furnace or oven, containing a reducing atmosphere such as nitrogen, to prevent oxidation and having a peak temperature in the range of about 200°C to 350°C, and the time the solder is above its melting point is about 15-60 seconds, depending on the solder composition, to cause solder reflow, thereby filling the via-hole by capillarity and gravity and leaving unexpectedly a bump of solder. Even if the solder ball is slightly offset with respect to the via-hole opening, the resulting solder bump is perfectly aligned with it. All solder bumps exhibit uniform geometries and volumes. Fig. 2C illustrates the MC substrate before cooling, showing the resulting structure and the shape of the solder which fills the via-hole forms, solder bumps 22 at the openings of the bottom surface 17 now facing upwards, and mounds 23 wetting the inner walls of the eyelet. The volume of the solder ball 20 must take into account the volumes of the via-hole and of the solder bump. The substrate is then allowed to cool below the melting point of the solder, whereby the molten solder will solidify to produce the final solder terminals comprised of three integral parts: a column, a bump and a mound of solidified solder. Fig. 3 shows the resulting structure after cooling, with its top surface 13 upwards again. The solder bumps 22 are to be used as I/O's of the MC module. Solder mounds make the electrical connection between said bumps and the pattern of metal conductors. That third step is then followed by a fourth step, consisting in the cleaning of the resulting MC substrate, for example, by dipping the MC substrate in a perchlorethylene bath, in order to degrease the substrate and eliminate flux residuals. The bottom surface of the MC substrate may be then visually inspected to detect missing solder bumps. In this case, rework is very easy because it is sufficient to add flux at the missing location, place solder bumps and reflow again. Other solder bumps will not flow or spread due to very high capillary forces. The chip may be bonded to the MLC substrate either simultaneously with the formation of solder bumps or before. In the latter case one may use different solder compositions. For example, silicon chip solder bumps may utilize 95/5 solder with a melting point of 320°C and the solder terminals may utilize a 90/10 solder with a melting point of 280°C. The solder terminals may be completed before chip joining, although they have a lower melting temperature than the silicon chips solder bumps, because of the extreme strength of capillarity forces at the location of the via-hole. If the chips are to be joined simultaneously with the solder bumps it suffices to dispense droplets of flux to be applied onto the contact fingers at the ends of the conductors so that they correspond to the solder bumps on the silicon chips, and by positioning the chips. Depending on the specific application, reflow temperatures, reflow times, relative volumes of solder, and solder compositions are parameters which have to be considered by the man skilled in the art . The MC substrate is then processed according to the standard manufacturing steps: test, encapsulation, etc... to provide a completed pinless MC module appropriate for SMT. Surface mounting of the carrier on a printed circuit board (not shown) would comprise depositing solder paste (e.g., 60% Sn and 40% Pb) on predetermined contact zones of the PCB, aligning and contacting the solder bumps of the module with such zones and reflowing the 60/40 solder at 185°C. The PCB is preferably of the multilayer type and is provided with a corresponding grid of copper pads of a diameter of about 0,6 MM. The PCB is covered by a layer of a protective varnish excepted at the pad locations. Use of solder paste and protective varnish avoids misalignment problems. However, if any difficulty is raised, the use of a template to maintain the module where appropriate would overcome the problem. On the other hand, the technique described for the pre-tinning of said zones in the afore mentioned Pottier's reference, may also be used. As can be understood, a significant advantage of the method of the present invention from a manufacturing point of view is its simplicity. In addition, because a wide variety of solder balls in both size and composition, is commercially available, another advantage is the flexibility of the above method, which is easily adapted to any kind of modules, applications,..., etc. Also the volume of the solder bump to be used as I/O's is very accurate, because the solder balls commercially available have a very precise volume. It is still an advantage of the present invention to provide a method of getting a controlled amount of solder at each bonding location. Depending on the volume of the solder ball, the shape and in particular the height of the solder bump may vary in some degree. This causes an important additional advantage related thereto. Because the volume of the solder ball determines the height of the solder joint formed between the MC module and the PCB obtained after cooling. It has generally the broad shape of a column or pillar, so that the gap between the bottom surface of the MC module and the top surface of the PCB is no longer negligible. As a consequence, this gap significantly contributes, not only to the air cooling of the module, but also to the reduction of thermal stresses due to differences in thermal dilatation coefficients between the substrate and the PCB material. This reduction is very significant due to the presence of the solder column. It is also obvious that the replacing of pins to be inserted in the holes of a perforated PCB by solder bumps results in a significant increase in the ability to repair or rework the MLC module. In particular, as explained above, it is easy to rework the MC substrate if visual inspection has revealed a missing solder bump. It is a significant additional advantage of the present invention to allow the formation of solder bumps at the center of an MC module according to a denser grid pattern therefore resulting in a significant increase of I/O's integration. It must be observed that the method of the present invention allows the whole bottom surface of the MC substrate to be used if desired and not only the periphery of the substrate as in known techniques. It is an additional significant advantage of the method of the present invention to provide a solder terminal which makes, simultaneously with the formation of solder bumps to be used as I/O's, the electrical connection with the eyelets of the pattern of metal conductors formed on the top surface of the ceramic substrate. The method of this invention is applicable to MC substrates having a pattern of metal conductors on both sides. It will provide solder bumps at the two ends of the via-holes.

Claims: Method of forming solder terminals on a pinless module having solder bumps (22) appropriate for Surface Mounting Techniques, said modules to be bonded onto Printed Circuit Boards (PCBs), the method compriseing the steps of a) forming a Metallized Ceramic (MC) substrate (11) having a pattern (12) of conductors formed onto its top surface (13) and an array of preformed via-holes (14), said conductors being terminated by eyelets (15) at the location of said via-holes; b) turning the MC substrate upside down so that its bottom surface faces up; c) applying where desired a droplet of flux at each preformed via-hole opening on the bottom surface (17) of the MC substrate, to fill the via-holes by capillarity and form a glob of flux (19) at each opening on the bottom surface (17); d) applying a solder preform (20) on each glob of flux to which it will adhere because of the adhesive property of the flux, the volume of the preform being substantially equal to the inner volume of the via hole plus the volume of the bump to be formed; e) heating to cause a solder reflow of the solder preform to fill the via-hole and the inner volume of the eyelet with solder; and, f) cooling below the melting point of the solder whereby the molten solder solidifies to form solder terminals at each via-hole location simultaneously forming a solder column in the via-hole, a solder mound (23) at the top surface of the MC substrate which makes electrical connections with said eyelets and solder bumps (22) at the bottom surface of the MC substrate (11). The method of claim 1 characterized in that step a), further comprises the step of: metallizing the sidewalls of said via-holes. The method of claim 1 or 2 characterized in that said array of preformed via-holes is at the center of the MC substrate. The method of claim 1, 2 or 3 characterized in that said solder preforms are solder balls of .7 mm in diameter and 90/10 Pb/Sn composition with a melting point of about 280°C. The method of any above claim 1 to 4 characterized in that it comprises the further step of: g) joining silicon chips having 95/5 Pb/Sn solder bumps at a temperature of about 320°C, to the pattern of conductors formed atop the MC substrate. The method of any of above claims 1 to 4 characterized in that simultaneously to step e), a silicon chip having 90/10 Pb/Sn solder bumps is joined to the pattern of conductors formed atop the MC substrate.

Inventors: BITAILLOU, ALEXIS, GRANDGUILLOT, MICHEL JOSEPH
Applicants: INTERNATIONAL BUSINESS MACHINES CORPORATION
Application year: 1986
Main classification: H01L21
IPC codes: H05K1, H01L21, H05K3