SUPPORT MEMBERS MADE OF INTERCALATED GRAPHITE

Abstract: A bearing or other support member containing intercala­ ted graphite exhibits many of the properties of a metal (ie: conductivity, luster, ductility) while retaining the lubricating properties of pure graphite. The bearings are made by pres­ sing an intercalated graphite powder either alone or mixed with metal powders, organic polymers or ceramic powders into the desired shape. This results in a bearing that has low friction properties, improved load bearing characteristics, higher operating temperatures and a reduced cost of manu­ facture.

Description: This invention relates to contacts for the support of solid objects, such as bearings and other low friction support members, formed from intercalated graphite and a method of making same. The selection of materials used in bearings and other support members depends on an optimum matching of material properties with the requirements of low friction characteristics and high load-bearing capability. Bearings are fabricated in a variety of ways, including casting, machining and powder metallurgy methods. Most bearings useful in heavy machinery are used in conjunction with a lubricant or general oil to reduce friction. These oil film-bearing materials include lead-tin alloys ("babitt metals"), copper-lead alloys, bronzes, aluminum, cast-iron, brass and steel, as well as commercial resins. Another popular type of bearing material is boundary-lubricating (or "self-lubricating") bearing material. This type of material is useful under dry or sparsely lubricated conditions. Some of the more commonly used materials are oil-impregnating porous metals, wood, rubber and graphite by itself or mixed with resins, copper, babbit, silver or oil. These materials permit design simplification, low maintenance and freedom from oil contamination. They perform best at low speeds and intermittant operations. Bearings of graphite, in particular, may be used with low viscosity liquids and in dry operations. Graphite's usefulness in dry operations stems from the ability of the graphite planes to slip past each other, which is due to the presence of water vapor or oxygen in graphite. Therefore, if conditions are such that the water or oxygen is driven off (i.e. elevated temperatures, high altitudes), the anti-friction properties of the graphite bearings are impaired. Bearings have been prepared from compression molded graphite-containing compacts filled with resins, copper, oil, etc., see Kirk-Othmer Encyclopedia of Chemical Technology, 3rd Ed., Vol. 3, pg. 683 (1978). These graphite bearings have found applications, for example, in machinery such as food or drug processors where contamination by oil and grease must be avoided and in chemical pumps which operate on low-viscosity, non-lubricating fluids. While graphite is a satisfactory, dry lubricant at room temperature in an ordinary atmosphere, at higher temperatures or altitudes, the water vapor leaves the system and the anti-friction properties are impaired. In addition, graphite compositions are characterized by brittleness and a low coefficient of expansion, which impart a tendency to crack when such compositions are struck on an edge or subject to high thermal, tensile, or bending stresses. Thus, it has been necessary to confine application of bearings and other support members containing graphite within a given range of temperature and stress. It has also been required, in the fabrication of graphite bearings, to avoid sharp corners, thin sections and the like, and to relieve edges with a chamfer. It has further been the practice to surround graphite bearings with a steel sleeve to provide mechanical support and minimize changes in shaft clearance with temperature variations. Therefore, a bearing having the low-friction properties of graphite but with improved strength and temperature resistance is desirable. In addition, the need often arises for a member that is not only self-lubricating but also electricly conductive. Examples of such members are small to medium machine gears and bearings used in printers, cash registers and the like. DE-A-20 24 185 discloses a method for producing composite materials containing graphite-like carbon and metals and optionally metal compounds by reducing graphite intercalated compounds, and is characterized in that metals which had been produced intermediarily by electrolysis are used for reducing the graphite intercalated compounds. GB-A-2 131 500 relates to a sealing body, especially a cylinder head gasket, produced by compressing expanded graphite particles, which contains a cured furan resin using rollers. US-A-3 409 563 relates to a hyperconductive graphite structure comprising compressed vermicular graphite having a density of at least about 0.07 g/cm³ and containing in combination therewith from about 0.5 weight percent to about 35 weight percent of an intercalation agent being certain halogens, interhalogens or metal halides. US-A-4 414 142 relates to a highly conductive composite of an organic polymer matrix and a graphite intercalation compound of graphite and a strong acid, a metal halide or a Bronsted acid and a metal halide. US-A-4 293 450 relates to an electrically conductive composition which comprises a graphite intercalation compound formed under anhydrous conditions of graphite, a sulfur-containing reactant, and a halide reactant. Chemical Abstracts 99:107741p relates to graphite intercalation compounds and their use as solid film lubricants. It is desirable to develop a bearing or other members which has low-friction characteristics, which may conduct electricity as well, which is easy and economical to manufacture, and which is sufficiently strong to reduce the need for metal reinforcing. It is therefore an object of this invention to provide an improved bearing or other support member made from graphite. It is another object of this invention to provide a support member containing graphite which is stable in air and over a wide range of temperatures. It is another object of this invention to provide a support member containing graphite which has superior low-friction characteristics. It is a further object of this invention to achieve superior load-bearing capability due to higher strength and greater edge-holding properties. It is another object of this invention to provide a contact that exhibits low friction properties and conducts electricity simultaneously. It is still another object of this invention to provide a more efficient method of manufacture of a graphite containing support member which requires simplified dies for pressing. Still another object of this invention is to provide a graphite support member requiring reduced amounts of metal reinforcement. According to the invention, these and other objects are achieved by a low friction support member according to the claims. The intercalating species may be any species which produces an intercalated graphite which is stable in air and at elevated temperatures such as a temperature up to 600 o C. In general, the intercalating species may be but is not limited to metal halides of transition elements, of Group III A, IV A, V A and VI A metals or metalloids, as well as the corresponding metals and metalloids themselves. In addition, halogens such as F₂ and Br₂ and interhalogens such as IBr may be useful as intercalating species as well. The graphite to be intercalated may be any natural or synthetic graphite and may be employed in a powdered, fiber or in an exfoliated form. The intercalated graphite is compressed uniaxially such as in a mold or die, or isostatically such as in a pressurized fluid to form a compact body of the desired shape. Alternatively, the intercalated graphite may be compressed into a blank and subsequently milled into desired shape. Metal reinforcement may be included in the support member as a metal edge reinforcement. Intercalated graphite has several properties which are used advantageously in this invention. When graphite is intercalated, it exhibits certain metal-like properties of a metal, including increased conductivity, luster and ductility. While a compression molded body of graphite particles is extremely weak and friable, a body formed of intercalated graphite is found to have coherence and strength proportional to the magnitude of the applied body forming pressure and temperature. This characteristic of intercalated graphite powder enabling compaction to a solid body under pressure and temperature leads to the fabrication of a bearing having attractive engineering properties. Furthermore, intercalated graphite exhibits improved lubrication properties. The intercalated graphites suitable for use in the invention are those which are stable in air and at elevated temperatures such as temperatures of 600 o C or higher. The most stable intercalated compounds are those intercalated with certain metal halides or metals, the main requirement being that the intercalating species is capable of exchanging charge with the host graphite crystal. The metal halides most suitably used in the present invention are halides of transition elements, halides of group III A, IV A, V A and VI A metals or metalloids. The preferred Group III A elements include boron, aluminum, gallium and indium. Graphites intercalated with the halides are formed in general by heating a mixture of graphite and the intercalating species to between 200 o C and 900 o C in the presence of chlorine gas for several hours. It is believed that the chlorine attacks the carbon atoms in the graphite lattice, thus forming positively charged sites throughout the graphite. The chlorine also reacts with the intercalating species to produce a negatively charged species which is attracted to and held by the positively charged carbon atoms thereby intercalating the graphite. This explanation of the mechanism of intercalation, however, is not meant to be definitive or a limitation of the invention. The metal intercalated graphites may be produced by preparing a metal halide intercalated graphite by the process described above and then reducing the metal halide to a metal in situ in the presence of a reducing agent thus producing a graphite containing a metal in its lattice structure. Suitable reducing agents include hydrogen gas, lithium biphenyl and certain hydrides (e.g., LiAlH₄, NaBH₄, NaH, CaH₂). The reduction typically takes place at between 200 o C to about 300 o C. It is believed that all the metal halides, described above, may be used to produce metal intercalated graphites that are equally as stable. Of the above-described species, the metal halides are preferred and of these halides the copper chloride, nickel chloride and chromium chloride are most preferred. If, however, a metal intercalated graphite is desired the graphite preferrably contains copper, nickel or silver which has been reduced in situ from the corresponding halide. The graphite employed in the present invention may be any of the known graphites and may be used in powder, fiber flaked or exfoliated form. In fact, it is believed that using exfoliated graphite facilitates the introduction of the intercalating species into the graphite lattice. The support member of the present invention may be fabricated using a variety of parameters and constituents, depending on the ultimate use to which the member will be put. Where the body to be fabricated does not require metallic reinforcement, the intercalated graphite powder is placed in a mold of the desired shape and pressed. Pressures may range from low enough to barely produce a coherent mass, i.e. about 1000 pounds per square inch (psi) (69 bar), to as high as is practically posible. For example, a forming pressure of 15,000 psi (1034.2 bar) produces a strong, useful member. The temperature applied during compression may range from ambient room temperature (about 20 o C) to about 1000 o C or higher, with room temperature being preferred. Higher temperatures and pressures produce higher strength and higher density bodies. Pressing times for these members range from 1 to about 30 minutes. The materials used for the mold or die are important because intercalated graphite at elevated temperatures and pressures will adhere to most metals, such as steel, which are commonly used for this purpose. Therefore, it is desirable either to fabricate the die parts from solid polytetrafluoroethylene or similar non-stick materials, or to coat the metal of the die or mold with sprayed-on flouropolymite telomer powder. A suitable commercially available spray is GP 1589 available from Acheson Colloids Co., Port Huron, Michigan. An aluminum foil or coatings of fine oxide powders, such as Al₂O₃, may also be helpful as parting materials. The bearings of the present invention may also be fabricated through the use of isostatic pressing. The intercalated graphite material is placed in a bag-like container, the container is evacuated and is then submerged in a pressurized medium. Unlike typical mold or die presses which apply pressure in only one direction, isostatic pressure applies an essentially uniform pressure around the entire pressed object. In addition, isostatic pressing generates much higher pressures than the molds or dies and, therefore, produce support members exhibiting higher density and strength. The bag-like container used in isostatic pressing is typically a shape-retaining rubber-like housing that will transfer pressure evenly around its perimeter. The housing will be shaped to conform with the desired final shape of the intercalated graphite bearing. The pressurized medium may be any suitable fluid such as ethylene glycol, hydraulic oil and the like. Due to the large volume changes experienced when fabricating intercalated graphite members (especially when exfoliated graphite is one of the starting materials), some uniaxial pre-pressing of the intercalated graphite using conventional means is typically done before isostatic pressing is performed. In a preferred embodiment, where the application requires that the bearing or other contact have a metal edge reinforcement, the mold may be shaped to receive and hold the metal reinforcement in position. After the metal reinforcement is in place in the mold, the intercalated graphite is introduced into the mold, and the whole structure is compressed for example at a pressures of from about 10,000 psi to 50,000 psi (689,5 bar to 3449,4 bar) and a temperature of 200 o C. These conditions are sufficient to produce a coherent body. In a second preferred embodiment, the desired properties may be obtained by pressing in a mold, as set forth above, a mixture of intercalated graphite and metal powders. In such applications, any metal powder may be used, such as copper, iron, or nickel, in proportions ranging from about 2 percent by weight up to 30 Vol-% of the composite material. Preparation of a composite bearing or other contact of this type is possible because unlike non-intercalated graphite, intercalated graphite bonds to metals under pressure. Therefore, a mixture of intercalated graphite powder and metal powder will, under pressure, form a coherent mass in which the two constituents are mutually reinforcing. A problem, which is sometimes encountered in members or structures formed from metal halide intercalated graphite, is that of environmental stability, particularly when the intercalated graphite members are stored or used under extremely high humidity. This stability problem takes the form of cracking, swelling and corrosion of the intercalated graphite member which appear after 1 to 6 months of storage or use. It is unclear as to what causes this lack of environmental stability, however, it does appear to be a function of intercalated graphite member forming pressures and temperatures (i.e., the higher the forming pressure or temperature, the more likely it is that this instability will appear) and possibly the type of graphite choosen as the starting material. The present invention is not affected by this. problem when low forming pressures and temperatures such as 10,000 psi (689.5 bar) and 20 o C are used, and when the use of the intercalated graphite members and structures are limited to normal humidity application. However, the lowering of the forming temperature and pressure leads to a comparable reduction in hardness and strength. The problem may also be solved by a composition prepared by mixing the intercalated graphite powder with small amounts of transition metals, such as nickel, copper, silver, molybdenum, or tungsten, prior to forming of an intercalated graphite member. Structural members of this composition, which may contain from about 2 vol. % to about 30 vol. % metal powder, experience none of the environmental stability problems described above even though a high forming pressure and temperature is used and high humidity is present. After the metal powder has been mixed with the intercalated graphite, this mixture may be handled in the same way as the intercalated graphite itself (see above). From the foregoing, it is evident that the present invention provides novel bearings and other low friction support member capable of being formed economically into the desired shape in simple dies or molds and having improved strength. The present invention is exemplified by the following examples, which are not intended to be limiting. EXAMPLE 1-Graphite Intercalated with Copper Chloride Graphite intercalated with copper chloride was prepared by mixing a quantity of graphite powder with a quantity of CuCl₂ to produce a mixture containing 48 wt % CuCl₂. This mixture was loaded into a glass reaction vessel and heated to 125 o C for 1.5 hours with dry nitrogen flowing through the vessel to remove any water present therein. The temperature of the reaction vessel was then raised to 500 o C, the dry nitrogen gas flow was stopped and a flow of dry chlorine gas at a gauge pressure of 3 (7.5·10⁻³ bar) to 6 (1.5·10⁻² bar) inches of water was begun. The resulting reaction continued for 4 hours. This treatment produced a black powder having a bulk density of from 0.18 to 0.34 gm/cm³ depending on particle size. The intercalated graphite particles are stage III and have a specific gravity of about 2.6 gm/cm³. EXAMPLE 2 A cylindrical bearing block one inch (2.54 cm) long with a diameter of one inch (2.54 cm) was made in a mold of appropriate shape as follows: A 1" (2.54 cm) diameter round piece of thin aluminum foil was placed in the bottom of a cylindrical mold having a 1" (2.54 cm) diameter mold. A mixture of 2 1/2 grams of copper chloride intercalated graphite produced according to the procedures of Example 1 plus 2 volume percent copper powder (Natural Copper Powder Extra Fine, #1400 U from Atlantic Powder Metals, Inc. of New York, N.Y.) was then carefully poured into the mold. A second 1" (2.54 cm) diameter piece of aluminum foil was placed over the mixture and a piston was slowly inserted into the mold. The temperature of the mold was increased to 180 o C and a pressure of 32,000 psi (2206.3 bar) was applied to the mixture by the piston for 3 minutes. After cooling and extracting the piece from the mold, the aluminum parting foils were removed and a scleroscope hardness of 54 was measured. This represents a high degree of hardness and is equivalent to strength approaching 200,000 (13790 bar) psi. The blank described was then converted to a bearing by drilling a hole in the center of the bearing sufficiently sized to accomodate a shaft along the bearing's longitudinal axis. EXAMPLE 3 A teflon mold may be shaped to receive and hold in position a reinforcement of copper metal. After the copper reinforcement having a thickness 0.020" (5.08·10⁻² cm) is inserted, a mixture of intercalated graphite and 5 wt percent copper may be introduced in sufficient amount into the cavity and the whole may be pressed at 50,000 psi (3447.4 bar) and 100 o C for 30 minutes to produce a coherent body. EXAMPLE 4 A mixture of intercalated graphite made according to the procedures of Example 1, and 2 weight percent copper powder (Natural Copper Powder Extra Fine # 1400 U from Atlantic Powder Metals, Inc., of New York, N.Y.) was pressed at room temperature in a 0.33" (0.8 cm) I.D. cylindrical metal mold to 50% of ideal density (maximum theoretical density to which the mixture would be compressed). This compact was then inserted into a neoprene rubber bag having an I.D. of 0.33" (0.8 cm) and a sealed end. The air was evacuated from the open end and sealed. The bag and its contents were enclosed in the pressure cell of an isostatic pressing apparatus; heated to 100 o C and isostatically pressed for 30 minutes at 100,000 psi (6894.8 bar). The result was a dense compact having a scleroscope hardness of 35 and suitable for machining into bearing or bushing parts.

Claims: A low friction support member comprising a compacted body consisting of a compacted intercalated graphite powder, which is stable in air and at an elevated temperature, or of a compacted mixture of said intercalated graphite powder with up to 30 vol. % metal powder. A support member in accordance with claim 1 wherein the intercalated graphite is intercalated with an intercalation species selected from the group consisting of a metal halide and a metal wherein the metal halide preferably is selected from the goup consisting of a halide of a transition element, a halide of a Group III A, IV A, V A and VI A metal or metalloid, and the metal is selected from the group consisting of a transition element, a Group III A, IV A, V A, and VI A metal or metalloid. A support member in accordance with claim 2 wherein the metal halide, prior to forming said member, is reduced in situ to a metal in the presence of a reducing agent thus forming a metal intercalated compound. A support member in accordance with claim 2 or 3 wherein said metal halide is selected from the group copper chloride, nickel chloride and chromium chloride. A support member in accordance with any of claims 1 to 4 further comprising a metal reinforcement disposed on the edge of said support member. A support member in accordance with any of claims 1 to 5 wherein the metal powder is selected from the group comprised of copper, iron, nickel, and cobalt. A support member in accordance with claim 6 wherein the metal powder comprises at least about 2 percent by weight of said support member. A method of forming a support member by compacting intercalated graphite particles at a pressure in excess of about 1000 pounds per square inch (69 bar) and at a temperature of from about 20 o C to about 1000 o C. A method in accordance with claim 8, wherein said pressure is generated uniaxially. A method in accordance with claim 8, wherein said pressure is generated isostatically. A support member producible with the method according to claims 8 to 10.

Inventors: VOGEL, FERDINAND LINCOLN
Applicants: INTERCAL COMPANY
Application year: 1986
Main classification: C04B35
IPC codes: C04B35, F16J15, C10N10, C10M103, C01B31, F16C33, C10N40, C10N50