STABLE TETRAFLUOROETHYLENE COPOLYMERS

Abstract: A tetrafluoroethylene/perfluoro(alkyl vinyl)ether copoly­ mer substantially free of unstable end groups and extractable fluoride that cause corrosion of metal surfaces.

Description: The present invention relates to improved perfluorinated resins, and in particular to melt-fabricable tetrafluoroethylene (TFE)/perfluoro(alkyl vinyl)ether (PAVE) copolymers with stable polymer end groups. Tetrafluoroethylene/perfluoro(alkyl vinyl)ether (TFE/PAVE) melt-fabricable copolymers are widely employed in industrial injection molded goods and wire insulation applications. Their unique combination of chemical stability and high-temperature properties make them a preferred material for a wide range of injection molded parts, extruded pipe and tubing, and vessel liners. TFE/PAVE resins are produced by aqueous polymerization (US-A-3,635,926), or polymerization in a perhalogenated solvent (US-A-3,642,742) or hybrid processes involving both aqueous and perhalogenated phases (EP-A-093 404). Free radical polymerization initiators and chain transfer agents are used in these polymerizations and have been widely discussed in the patent literature. For example, persulfate initiators and alkane chain transfer agents are described for aqueous polymerization of TFE/PAVE copolymers (US-A-3,635,926). Fluorinated peroxide initiators and alcohols, halogenated alkanes, and fluorinated alcohols are described for nonaqueous (US-A-3,642,742) or aqueous/nonaqueous hybrid polymerizations (EP-A-093 404). The particular choices of initiator and chain transfer agent are dictated by the process conditions selected (temperature and reactant concentration) and the resin properties (viscosity and molecular weight distribution) desired. The selections of the initiator and chain transfer agent dictate the end groups on the polymer chain. Persulfate initiators are known to give -COOH end groups in aqueous polymerization. If a polymerization buffer, such as an ammonium salt, is employed, -CO₂NH₄ end groups are obtained which convert to -CONH₂ ends during thermal conditioning. If methane is used as chain transfer agent, -CF₂H and -CF₂CH₃ ends will also be present in the resin. In a nonaqueous polymerization (or aqueous-nonaqueous), peroxides such as (ClF₂C(CF₂) n COO)₂ may be used as initiators, leading to -CF₂Cl end groups. If methanol is used as the chain transfer agent, -CF₂H and -CF₂CH₂OH end groups will also be present. In this type of polymerization, -COF end groups are also formed by unimolecular rearrangement of a PAVE radical on a growing chain, i.e. While the perfluorinated chains of the TFE/PAVE copolymers have extremely good thermal stability and chemical inertness, the end groups of the TFE/PAVE copolymers described above can be chemically reactive and thermally unstable. It has now been discovered that these unstable end groups evolve HF, which is generated by the oxidation, hydrolysis and/or thermal decomposition of certain end groups, especially -COF, -CONH₂ and -CF₂CH₂OH. The HF generated from unstable end groups has been found to be corrosive to metals, leading to metal fluoride corrosion products. As a result of the discovery of the source of corrosivity, an improved TFE/PAVE resin was developed that does not contain the unstable end groups that have the corrosion potential described above. The improved resins have extremely low levels of corrosive extractable fluoride, in the form of dissolved HF or COF₂, and have nearly a quantitative absence of end groups that can oxidize, hydrolyze and/or thermally decompose to generate additional HF. The present invention relates to a melt-fabricable, nonelastomeric, tetrafluoroethylene copolymer substantially free of end groups that can react or decompose to emit HF, comprising recurring units of tetrafluoroethylene and at least one perfluoro(alkyl vinyl)ether where the alkyl group contains 1-8 carbon atoms and wherein the vinyl ether comprises between 1 and 10 weight percent of the copolymer; said copolymer characterized by having a) less than 6 endgroups of -CF₂CH₂OH, -CONH₂ and -COF per 10⁶ carbon atoms and b) an extractable fluoride level of 3 ppm or less by weight. The present invention includes also a process for producing said copolymer which comprises treating a copolymer containing more than 6 per 10⁶ carbon atoms of end groups of -CF₂CH₂OH, -CONH₂ and -COF with a fluorine-containing gas at a temperature, time and pressure sufficient to reduce the end groups -CF₂CH₂OH, -CONH₂ and -COF to less than 6 per 10⁶ carbon atoms, and sparging the fluorinated copolymer with an inert gas until the sparge gas tests negative in the starch/iodide test. The tetrafluoroethylene/perfluoro(alkyl vinyl)ether copolymers that can be fluorinated by the process of this invention are ones that are made by any of the conventional processes described hereinbefore for making TFE/PAVE copolymers. The copolymers contain between 1 and 10 weight percent of recurring units derived from the vinyl ether, perferably 2 to 4 weight percent. The comonomer content is low enough that the copolymers are plastics rather than elastomers, i.e. they are partially crystalline and do not exhibit a rapid retraction to original length from a stretched condition of 2X at room temperature. But the comonomer content is not so low that the copolymer is not melt fabricable. By the term "melt-fabricable" is meant that the copolymer can be processed (i.e. fabricated into shaped articles such as injection molded articles, films, fibers, tubes and wire coatings) by conventional melt-processing equipment. This requires that the melt viscosity of the copolymer should be no more than 10⁶Pas (10⁷ poise) at 372 o C. Preferably, the melt viscosity is in the range of 10³ to 10⁵ Pas (10⁴ to 10⁶ poise) at 372 o C. Melt viscosities of the melt-processible polymers are measured according to American Society for Testing and Materials (ASTM) Method D-1238, modified as follows: The cylinder, orifice and piston tip are made of a corrosion-resistant alloy, such as Haynes Stellite (Registered Trade Mark) 19 or Inconel (Registered Trade Mark) 625. The 5.0 g sample is charged to the 9.53 mm inside diameter cylinder which is maintained at 372 o C ± 1 o C. Five minutes after the sample is charged to the cylinder, it is extruded through a 2.10 mm diameter, 8.00 mm long square-edge orifice under a load (piston plus weight) of 5000 grams. This corresponds to a shear stress of 44.8 kPa. The melt viscosity in 0.1 Pas (poises) is calculated as 53170 divided by the observed extrusion rate in grams per minute. The comonomers have the formula R f -O-CF=CF₂ where R f is perfluoroalkyl of 1-8 carbon atoms. A preferred class is normal perfluoroalkyl. Specific copolymerizable comonomers include perfluoro(methyl vinyl ether), perfluoro(n-propyl vinyl ether) and perfluoro(n-heptyl vinyl ether). Mixtures of these comonomers may be employed. As-polymerized TFE/PAVE copolymer will contain at least 80 end groups of -CF₂CH₂OH, -CONH₂ or -COF, per 10⁶ carbon atoms and during fabrication and/or subsequent heat treatment these unstable end groups can react or decompose to form HF which will result in an appreciable extractable fluoride content in the resin. Of course, in the process of this invention, any starting copolymer can be used regardless of the number of unstable endgroups, for whatever the number, upon fluorination, the number will be reduced. Depending on the method of polymerization, the starting copolymer may not contain any extractable fluoride, in which case, only the number of unstable endgroups will be decreased on fluorination and sparging. The copolymer may contain minor amounts of at least one third comonomer, i.e. up to 5% by weight. Representative such copolymerizable comonomers are represented by the formula: wherein R₁ is -R f or -R f X in which R f is a perfluoroalkyl radical of 1-12 carbon atoms, -R f -is a perfluoroalkylene diradical of 1-12 carbon atoms in which the attaching valences are at each end of the chain, and X is H or Cl; and R₂ is -R f or -R f -X. Specific such copolymerizable fluorinated ethylenically unsaturated comonomers include hexafluoropropylene, 3,3,3-trifluoropropylene-1, 3,3,4,4,5,5,6,6,6-nonafluorohexene-1. The unstable end groups described above may be virtually eliminated by treatment of the polymer with fluorine. The fluorination may be carried out with a variety of fluorine radical generating compounds but preferably the polymer is contacted with fluorine gas. Since reactions with fluorine are very exothermic, it is preferred to dilute the fluorine with an inert gas such as nitrogen. The reaction conditions are interrelated. No one condition is critical, but the relation between them is important. If higher temperatures are used, shorter reaction times can be used, and vice versa. Similarly, if higher pressures are used, reaction temperatures and times can be reduced. With this in mind, the level of fluorine in the fluorine/inert gas mixture may be 1 to 100 volume % but is preferably 10-25% because it is more hazardous to work with pure fluorine. The temperature may be between 150 and 250°C, preferably 200-250°C, and the fluorination time may be between 4 and 16 hours, preferably 8 and 12. It is preferred to agitate the polymer to expose new surfaces continuously. The gas pressure during fluorination may range from 1 to 10 bars (atmospheres) absolute but preferably atmospheric pressure will be used. If a reactor is used at atmospheric pressure, it is convenient to pass the fluorine/inert gas mixture through the reactor continuously. The unstable ends are converted to -CF₃ ends. Another means of expressing the combination of fluorine concentration and reaction time for the fluorination step is to define the amount of fluorine added per pound of polymer. The range of applicable values is 1.8 to 5.1 grams of fluorine per kilogram of polymer, with the desired range being 2.4 to 3.3 grams per kilogram. These values include the amount of fluorine to bring the reactor from 0.1 to 1 bar (atmosphere) pressure at the beginning of the reaction. Polymer subjected to fluorination may be any particulate form, such as powders, flake, pellets, cubes or beads. For convenience, particle size should not exceed 5 mm square or diameter. After exposure of the polymer to fluorination for the desired length of time, the polymer is subjected to a flow of inert gas, i.e. inert to the copolymer, such as nitrogen, until the level of extractable fluorides is 3 ppm by weight or less. Generally, in this sparging step, the reaction vessel is preferably evacuated to 0.1 bar (atmosphere) before adding the inert sparge gas. Minimum time to complete sparging is defined by contacting, usually by bubbling, the effluent sparge gas with a starch/iodide solution or by passing it over starch/iodide paper. Lack of color development in the indicator indicates the absence of fluorine in the purge. Generally, 1-4 hours of sparging is adequate. The fluorination and sparging conditions are such that after treatment, the copolymer will contain less than 6 end groups of -CF₂CH₂OH, -CONH₂ and -COF per 10⁶ carbon atoms in the polymer chain and will have an extractable fluoride content of 3 ppm or less by weight. The -COF unstable end groups are the most resistant to conversion to stable -CF₃ groups of any of the end groups discussed above; and if they are converted, it is certain that the others have been also. The resulting copolymer exhibits low corrosivity toward metals. TEST PROCEDURES End Group Analysis Thin films (0.25-0.30 mm) are molded at 350 degrees Centigrade using a heated platen press. The films are scanned on a Nicolet Model 5DX Fourier Transform infrared spectrometer. All operational settings used were those provided as default settings in the Nicolet control software, except for the number of scans collected before the transform is performed (40 scans vs. 10 scans in default mode). Similarly, a film of a reference material known to have none of the end groups to be analyzed is molded and scanned. The reference absorbance spectrum is subtracted from the sample absorbance, using the interactive subtraction mode of the software. The -CF₂ overtone band at 4.25 micrometers is used to compensate for thickness differences between sample and reference during this interactive subtraction. The difference spectrum, in two ranges - 5.13 to 5.88 micrometers (1950 to 1700 wavenumbers) and 2.70 to 3.45 micrometers (3700 to 2900 wavenumbers) - represents the absorbances due to reactive end groups. Of primary interest to corrosivity are the acid fluoride end group and the carbinol end group, which are easily oxidized to produce HF and an acid fluoride end group. Calibration factors to allow calculation of end groups per million carbon atoms are determined from the absorbance of model compounds. The table below presents wavelengths and factors for determining end groups via the equation: ends/10₆ carbons = absorbance x CF/film thickness in mm ENDGROUP WAVELENGTH CALIBRATION FACTOR (CF) -COF 5.31 micrometers 440 -CH₂OH 2.75 micrometers 2300 -CONH₂ 2.91 micrometers 460 Perfluoropropylvinyl Ether (PPVE) Content Determination The PPVE content in the melt-processible TFE/PPVE copolymers described herein is also determined by infrared spectroscopy. The ratio of absorbance at 10.07 micrometers to that at 4.25 micrometers is determined under a nitrogen atmosphere using films approximately 0.05 mm thick. The films are compression molded at 350°C, then immediately quenched in ice water. This absorbance ratio is then used to determine percent PPVE by means of a calibration curve established with reference films of known PPVE content. F19 NMR is used as the primary standard for calibrating the reference films. Extractable Fluoride Content Ten grams of sample to be tested (pellets, beads, flakes, etc) are placed in a polyethylene bottle. Ten milliliters of a 1:1 mixture (by volume) of methanol/water are added, and 10 mL of a Orion 94-09-09 Total Ionic Strength Adjusting Buffer (normally used in fluoride specific ion measurements) are added. The methanol portion of the mixture is necessary to speed the extraction. The mixture is agitated briefly and allowed to stand for 24 hours. Fluoride concentration is determined directly on the sample mixture, using an appropriately calibrated specific fluoride ion electrode (Orion 96-90-00). Calibration in the range of 0.05 to 50 micrograms fluoride per milliliter of extracting solution is appropriate to analyze concentrations in the range of 0.1 to 100 ppm by weight in the polymer sample. STARCH/IODIDE TEST Sparge gas is passed over a potassium iodide/starch paper (Fisher Scientific Co. paper was used). Lack of color on the paper indicates absence of fluorine in the gas. EXAMPLES The tetrafluoroethylene/perfluoropropyl vinyl ether copolymer (TFE/PAVE) used in these Examples was prepared generally in accordance with US-A-3,642,742 (Carlson). This patent teaches a process for preparing TFE/PPVE copolymers in F-113 (1,1,2-trichloro-1,2,2-trifluoro ethane) solvent, with perfluoropropionyl peroxide initiator, and using methanol as a chain transfer agent. EXAMPLE 1 Extrusion pelletized (average size, about 3 mm) tetrafluoroethylene/perfluoro(propyl vinyl)ether (PPVE) copolymer, 66.3 kg, of melt viscosity of 4.1x10³Pas (4.1x10⁴ poise),and PPVE content of 3.4 weight %) was charged into a double cone blender/reactor fluorination unit. Volume of the reactor was 425 liters. The blender and contents were purged with nitrogen and then evacuated to 0.1 bar (atm) pressure. The temperature was raised to 200 o C, as measured by a thermocouple in the resin bed, and pressure was raised to 1.0 bar (atmosphere) pressure absolute by adding a 25 mole percent fluorine in nitrogen gas mixture. Flow of the gas mixture was continued for 8 hours at which time a total of 1480 gm of fluorine had been passed through the resin. The heat was then turned off and the vessel was evacuated to 0.1 bar (atm). An atmospheric pressure nitrogen sparge was started and allowed to continue until the starch/iodide test was negative (about one hour). At that time, the temperature had cooled to 30 o C, and the polymer was discharged. The resulting sample was analyzed to have 0.8 ppm extractable fluorides and 5 acid fluoride end groups/million carbons and no detectable (less than 1) -CONH₂ or -CH₂-CH₂OH groups. EXAMPLE 2 A 454 kg sample of a copolymer similar to the one used in Example 1 (MV = 4.9 x 10³ Pas, PPVE content = 3 weight percent) was fluorinated as in Example 1 except the fluorine concentration in the fluorine/nitrogen gas was 10 mole percent, the reactor temperature was 200 o C and the reaction time was 15 hours. The resulting resin was analyzed to have 0.5 ppm extractable fluoride and less than 1 acid fluoride end group per million carbon atoms and no detectable -CONH₂ or -CF₂-CH₂OH groups. COMPARISON A 1.36 kg of extruder-pelletized copolymer similar to the one used in Example 1 (MV = 3 x 10³ Pas (3 x 10⁴ poise), PPVE Content = 3.1%) were treated in a 285-290 o C air oven for 3 hours as above. The copolymer was not fluorinated. The resulting polymer was analyzed to contain 39 ppm extractable fluoride and 138 acid fluoride end groups per million carbon atoms. EXAMPLE 3 A 49.5 kg sample of a copolymer similar to the one used in Example 1 (MV = 3.5 x 10³ Pas, and PPVE content was 3.4 weight %) was charged to a fluorinator (reactor volume = 68.5 liters). The vessel and contents were sparged with nitrogen and heated to 210 o C. The reactor was evacuated, then brought up to 1 atmosphere using a 10 mole percent mixture of fluorine in nitrogen. Flow of the mixture was established such that in 6 hours, a total of 247.5 grams of fluorine had been added to the vessel, including the original pressurization to 1 bar (atmosphere). At the end of 6 hours, the fluorine mixture was turned off and a nitrogen purge begun. After 15 minutes sparging, the starch/iodide test was negative. The resulting polymer was analyzed to have 5 acid fluoride end groups per million carbon atoms and no detectable -CONH₂ or -CF₂CH₂OH groups and 3 ppm extractable fluoride. COMPARISON B The copolymer used in this example was prepared in accordance with US-A-3,635,926, which teaches a process for preparing TFE/PAVE copolymers using aqueous polymerization with ammonium persulfate initiator, ammonium carbonate buffer, ammonium perfluorooctanoate dispersing agent and ethane as chain transfer agent. Two 100 gm samples of a tetrafluoroethylene/perfluoropropyl vinyl ether (MV=3.1 x 10³ Pas, PPVE Content = 3.3%) containing 70 -CONH₂ end groups were fluorinated according to the conditions described in GB-A-1,210,794 (250 o C for 2 hours, 0.25 MPa gauge (36 psig) fluorine pressure). The resulting polymer showed 2 acid fluoride end groups per million carbon atoms, 10 ppm residual amide end groups, and more than 4000 ppm extractable fluoride.

Claims: A melt-fabricable, nonelastomeric, tetrafluoroethylene copolymer substantially free of end groups that can react or decompose to emit HF, comprising recurring units of tetrafluoroethylene and at least one perfluoro(alkyl vinyl)ether where the alkyl group contains 1-8 carbon atoms and wherein the vinyl ether comprises between 1 and 10 weight percent of the copolymer; said copolymer characterized by having a) less than 6 endgroups of -CF₂CH₂OH, -CONH₂ and -COF per 10⁶ carbon atoms and b) an extractable fluoride level of 3 ppm or less by weight. A copolymer according to Claim 1 wherein the perfluoro(alkyl vinyl)ether is a normal perfluoro(alkyl vinyl)ether. A copolymer according to Claim 2 wherein the ether is perfluoro(propyl vinyl)ether. A copolymer according to any one of Claims 1 to 3 wherein the ether content is between 2 and 4 weight percent. A process for producing a copolymer as claimed in any one of claims 1 to 4 which comprises treating a said copolymer containing more than 6 per 10⁶ carbon atoms of end groups of -CF₂CH₂OH, -CONH₂ and -COF with a fluorine-containing gas at a temperature, time and pressure sufficient to reduce the end groups -CF₂CH₂OH, -CONH₂ and -COF to less than 6 per 10⁶ carbon atoms, and sparging the fluorinated copolymer with an inert gas until the sparge gas tests negative in the starch/iodide test.

Inventors: IMBALZANO, JOHN FRANCIS, KERBOW, DEWEY LYNN
Applicants: E.I. DU PONT DE NEMOURS AND COMPANY
Application year: 1986
Main classification: C08F214
IPC codes: B29B9, C08J3, C08F8, C08F214