A METHOD OF MAKING A MAGNETIC RECORD DISK

Abstract: In order to form micropores in a magnetic coating for the retention of a liquid lubricant, water and an inverse micelle forming surfactant are added in an appropriate molar ratio to the organic binder for the magnetic particles. Micropores of uniform size and distribution are formed in the coating when the water evaporates during curing of the coating. The size and number of the micropores is controlled by the water/surfactant molar ratio, the amount of water and the amount of surfactant. This permits the design and control of the amount of liquid lubricant retained in the magnetic coating.

Description: This invention relates to a method of making a magnetic record disk of the type which has a coating of magnetic particles dispersed within an organic binder. The coating for a particulate magnetic record disk includes magnetic particles, such as gamma Fe₂O₃ particles, within an organic binder. Load bearing particles, such as Al₂O₃ particles, may also form part of the coating to improve the durability of the coating. The binder typically includes heat-hardenable polymers (such as epoxy or phenolic resins or combinations thereof, polyurethanes or acrylates), solvents, dispersing agents, and flow agents. In addition, the binder may include certain substances, such as organic additives which may decompose during curing of the coating and leave micropores on the surface of the cured coating, the micropores serving as minute reservoirs for a liquid lubricant which is later applied to the cured disk coating. In the manufacture of a particulate magnetic recording disk, the magnetic particles are typically placed first in a media mill or ball mill to break-up agglomerations and to further enhance disper­ sion of the particles. The magnetic particles are then mixed in the organic binder. The resulting formulation is applied as a coating to the disk substrate by pouring it onto the substrate while it is spinning. A magnetic field is applied to the coating to orient the magnetic particles within the coating so that the particles are aligned in the preferred direction. The disk is then placed in a curing oven to cross-link the polymers in the organic binder and thus harden the coating. During the curing process, some substances may decompose or evaporate to leave micropores in the cured coating. After curing, the disk coating is buffed and then washed to remove any debris, followed by an optional burnishing operation to remove any asperities. The final step in the manufacturing process is the application of a liquid lubricant to the disk. The lubricant is absorbed into the micropores in the coating to provide lubrication between the head and the disk. While certain substances used in the binder for other purposes may inherently decompose or evaporate during curing to form the micropores, it is also known to add certain substances for the specific purpose of micropore formation. Fore example, German patent application number DE 33 41 205, published 17 May 1984 discloses the addition to the binder of a volatile material which evaporates during curing to leave micropores for retention of a liquid lubricant. EP-A-129721 discloses the use of polymeric additives, such as polybutene, which thermally degrade during curing and which have high volatilisation efficiency to produce microvoids in the coating surface. The use of decomposing additions which form the micropores in the disk coating surface is difficult to control. If there are not enough micropores or if they are not of sufficient size, the disk will be under-lubricated which may result in wear between the disk and the head. On the other hand, if there are too many micropores or if they are of too large a size, the disk will be over-lubricated which may make it difficult for the head to break loose from the disk at start-up of the disk file. The invention seeks to provide an improved method of making a magnetic record disk. A method of making a magnetic record disk which includes the steps of preparing an organic-based binder which includes a solvent and has magnetic particles dispersed therein, coating the binder onto a suitable substrate, orienting the magnetic particles in alignment with a magnetic field, curing the coating and applying a lubricant to the cured coating, is characterised, accor­ ding to the invention, by adding in a predetermined molar ratio water and an inverse micelle forming surfactant to the binder, whereby during curing of the binder the water evaporated from the attached inverse micelle forming surfactant forms micropores in the cured coating for retention of the lubricant. The invention takes advantage of the fact that certain amphi­ philic molecules (surfactants) are capable of forming themodyna­ mically stable, monodispersed micro-emulsions of otherwise immis­ cible liquid phases, such as water and the organic binder of the disk coating. Above a certain threshold concentration, these surfactant molecules form, in non-polar, aprotic solvents, such as the solvents used in the disk binder, aggregates of well defined size. These are called 'inverted micelles' or 'inverse micelles'. In any given solvent system, the monodispersed droplet size of the microemulsified water depends only on the chosen surfactant, the temperature and the molar ratio of water to surfactant. With increasing water to surfactant molar ratio, the droplet size in­ creases, resulting at constant surfactant concentration in the formation of fewer but bigger aggregates. In this manner, the size and uniformity of the water droplets in the coating, and thus the micropores formed during curing of the disk coating, is controlled. This permits the design and control of lubricant retention on the disk. How the invention can be carried out will now be described by way of example, with reference to the accompanying drawings, in which:- Figure 1 represents the formation of a droplet of microemulsi­ fied water by an inverse micelle forming surfactant in the organic binder magnetic coating; and Figure 2 is a graph of disk lubricant retention as a function of the molar ratio of surfactant to gamma iron oxide particles for various molar ratios of water to surfactant. A very simple representation of the structure of an inverse micelle is shown in Figure 1. The polar end 10 of each surfactant molecule 12 is shown surrounding a water droplet 14. In the absence of the surrounding attached surfactant molecules 12, the water droplet 14 would be otherwise immiscible in the surrounding organic binder 16. The number of molecules in each microemulsified water droplet depends for a given binder system upon the molar ratio of the water to the inverse micelle forming surfactant. The relationship of the number of water molecules, and thus the water droplet size, to the number of surrounding attached surfactant molecules is shown in Table 1 (ref: J Rehank, PhD Thesis, University of Basel, Switzer­ land, 1976). The number 'N' in Table 1 is the association number or the number of surfactant molecules which surround the water droplet for the corresponding molar ratio 'W' of water to surfactant. In Table 1 the surrounding immiscible fluid is iso-octane and the surfactant is Aerosol-OT (sodium di-isooctyl sulfosuccinate). As the molar ratio W is increased, the number N of surfactant molecules which surround the water droplet is increased. This results in an in­ crease in water droplet size because each surfactant molecule has an increased number of water molecules attached to it. Not all surfactants are capable of forming inverse micelles with water. While the preferred inverse micelle forming surfactant is Aerosol-OT, other surfactants would also function to form micro­ emulsions in the solvent system of the organic binder. For any particular solvent system, a surfactant can be selected which is compatible with the binder and which has a sufficient polarity to form micelles with water and thus form a microemulsion. The formation of inverse micelles and microemulsions is mainly understood to be due to a minimum in the total free energy of the system brought about by the change in the enthalpy by hydrophobic interactions of the lipophilic parts of the surfactant molecules and by a slight increase in the entropy of the solvent molecules. In practice, the selection of a suitable inverse micelle forming surfactant or surfactant mixture for a given solvent system is mainly governed by the following general guidelines: (a) The formation of inverse micelles and micro-­ emulsions are favoured by increased head-to-chain volume ratio, increased dipole moment and decreased solubility of the surfactant molecules. These parameters typically indicate that anionic surfac­ tants are preferred over cationic surfactants, which are preferred over non-ionic surfactants. (b) For ionic surfactants, large cations and large anions favour the formation of inverse micelles. For anionic surfactants, aggregation increases in the order of carbonates, phosphates and sulfonates. (c) Branching of the lipophilic hydrocarbon chain of the surfactant leads to increased aggregation and to reduced critical micelle concentrations because the hydrophobic interaction between the hydrocarbon tails of the aggregate of inverted micelles is in­ creased. Non-aromaticity of the surfactant molecule additionally favours the formation of inverse micelles by reducing solvent-surfactant interaction. For non-ionic surfactant systems, mixtures of a high and a low molecular weight surfactant or of a surfactant and a low molecular weight alcohol strongly favours the formation of inverse micelles due to sterical optimisation of hydrophobic inter­ actions. (d) For a given surfactant, the formation of inverse micelles slightly increases with decreasing value of the solubility parameter of the solvent. Thus, in the case of Aerosol-OT, the formation of inverse micelles increases with different solvents in the following order: (e) The incorporation of water or other polar sub­ stances, e.g an electrolyte, into the inverse micelle strongly increases the formation of inverse micelles and reduces the critical micelle concentration by further reduction of the total free energy of the system. Surfactants with a high affinity to bond water via hydrogen bonds or via strong Coulomb forces favour water up-take. The size and stability of such 'swollen' micelles, however, depends on the overall energy of the system and therefore on the points con­ sidered above. Due to increased electrostatic attraction, anionic surfactants typically are capable of taking up a larger amount of water than cationic surfactants. For nonionic surfactants, the water up-take exponentially increases with the number of ethoxy groups in the hydrophilic molecule part. In summary, the selection of a suitable surfactant or surfac­ tant mixture first depends on the polarity and the solubility parameter of the solvent system to be used. Therefore, such para­ meters have to be estimated. Next, a choice is made as to whether a nonionic, a cationic or an anionic surfactant should be utilised. Among the factors to influence this choice are the absorption at the gamma-Fe₂O₃ interface and the Al₂O₃ interface, and chemical compati­ bility of the surfactant type with the binder type. After such consideration, candidate surfactants are screened for maximum head-to-chain volume ratio and maximum dipole moment within the range of still having some solubility in the solvent system em­ ployed. Branched, non-aromatic surfactants are then given priority and for the case where a non-ionic surfactant should be employed, mixtures of such surfactant with low molecular weight alcohols or with lower weight non-ionic surfactants are explored. Experimental values for critical micelle concentration and association number are obtained by vapour pressure osmometry, conductivity measurements, light scattering or spectroscopic methods. Water up-take is esti­ mated by light scattering, turbidity and conductivity measurements, Karl-Fischer analysis or spectroscopic methods. Examples of inverse micelle forming surfactants are the follo­ wing:- For cationic surfactants: Dodecylammonium-propionate For anionic surfactants: Aerosol-OT = Dioctyl ester of sodium sulfosuccinic acid For nonionic surfactants: Polyoxyethylene lauryl-ethers The lubricant retention properties of various magnetic recor­ ding disks made by a method embodying the invention is illustrated in Figure 2. These disks had a coating of an epoxy-phenolic resin blend binder, including isophorone as a solvent, alumina (Al₂O₃) load-bearing particles, and gamma-Fe₂O₃ magnetic particles. To this binder was added water and Aerosol-OT in the various molar weight ratios as shown in Figure 2. The lubricant retention of the subse­ quently cured coatings was significantly increased, once the con­ ditions of microemulsion formation by Aerosol-OT plus water was met. The critical concentration of Aerosol-OT in this type of binder and solvent is approximately 8 × 10⁻² mol/litre, as determined from Figure 2 and the known amount of gamma-Fe₂O₃ particles. Below this concentration, the added water does not become microemulsified and therefore does not follow the described concept of forming micro-­ droplets of uniform size and distribution. Above this critical surfactant concentration, the lubricant retention in the coating increases with increasing micelle concentration and increases with increasing size of the micelles, as determined by the molar ratio of water to the surfactant Aerosol-OT. The critical concentration of surfactant, above which inverse micelle formation occurs, depends, at a constant temperature, on the solvent system, the surfactant used and the concentration of polar additives, which in addition to water, is the gamma iron oxide particles. The critical concentra­ tion of Aerosol-OT in the epoxy-phenolic resin binder with isopho­ rone as a solvent, as shown in Figure 2, may be relatively high, partly due to the concurrent and preferred absorption of surfactant at the gamma iron oxide interface. It is believed that the absorp­ tion of the surfactant at this interface also significantly in­ creases disperson of the magnetic particles and thus the particle orientation ratio in the final coating. Experimentally, the disks made by a method embodying this invention showed that the gamma-­ Fe₂O₃ particle orientation ratio to be increased on the average by approximately 50% compared with the orientation ratio of disks without the Aerosol-OT and water additives. It was also found that the addition of the relatively large amount of surfactant and water to the coating did not deteriorate the disk wear durability as shown from the wear testing of unlub­ ricated disks. The time to failure in a disk durability test for unlubricated disks made with the water and Aerosol-OT additives was approximately six times longer than for unlubricated disks without the Aerosol-OT and water additives. The use of inverse micelle forming surfactants and water in particulate magnetic recording disk coatings enables the size and number of microdroplets in the coating, and thereby the size and number of micropores in the cured films, to be controlled. Since the absorption of the lubricant in the coating is proportional to the film surface area, desirable levels of lubricant retention are achieved on a reproducible basis strictly by designing a proper size and number of microemulsified water droplets. This is achieved by the selection of the concentration of a specific inverse micelle forming surfactant and the molar ratio of water to such surfactant.

Claims: 1. A method of making a magnetic record disk which includes the steps of preparing an organic-based binder which includes a solvent and has magnetic particles dispersed therein, coating the binder onto a suitable substrate, orienting the magnetic particles in alignment with a magnetic field, curing the coating and applying a lubricant to the cured coating, the method being characterised by adding in a predetermined molar ratio water and an inverse micelle forming surfactant to the binder before it is coated onto the substrate whereby during curing of the binder the water evaporated from the attached inverse micelle forming surfactant forms miropores in the cured coating for retention of the lubricant. 2. A method as claimed in claim 1, in which the surfactant com­ prises Aerosol-OT (sodium di-isooctyl sulfosuccinate).

Inventors: ROSSI, EVA-MARIA, TIETZE, ARMIN RUDOLF
Applicants: INTERNATIONAL BUSINESS MACHINES CORPORATION
Application year: 1986
Main classification: G11B5
IPC codes: G11B5