PROCESS FOR MAKING A CONTACT ARRANGEMENT FOR A SEMICONDUCTOR DEVICE

Abstract: A metal or metal silicide is selectively grown on a nucleating layer (14) having a predetermined pattern on an insulating layer (12), and on a substrate (11) in an opening (13) in the insulating layer (12), to form a metal or metal silicide layer (15) in contact with the substrate (11) in the opening (13) and extending there­ from along the pattern of the nucleating layer (14). This process is advantageous in that a high electroconductive metal or metal silicide layer (15) having a precise pattern can be easily formed.

Description: This invention relates to a process for use in fabricating a semiconductor device . Figure 1 is a sectional view of the pertinent portion of a bipolar transistor proposed in the prior art. In this Figure, 1 is an n-type silicon substrate for the collector region, 2 is its principal surface, 3 is a p-type base region, 4 is an n-type emitter region, 5 is a base taking-out electrode of a polycrystalline silicon layer containing a p-type impurity, 6 and 7 are SiO₂ films, 8 is a base electrode, and 9 is an emitter electrode. In this bipolar transistor, the base electrode 8 is connected to the base taking-out electrode 5 made of a polycrystalline silicon. Such a structure can allow the area on the principal surface 2 of the base region 3 to be smaller as compared with the case when the base electrode 8 is connected directly onto the base region 3 without the intermediary base taking-out electrode 5. However, even in this bipolar transistor, since the base taking-out electrode 5 consisting of a polycrystalline silicon layer is commonly formed by etching a polycrystalline silicon layer formed on the entire surface of the base region 3, the emitter region 4, and the SiO₂ film 6, the area occupied by the base taking-out electrode 5 on the base region 3 becomes relatively large . Also, the area occupied by the SiO₂ film 7 on the regions 3 and 4 cannot help but become relatively large for the same reason. Accordingly, there has been proposed a process for fabricating a bipolar transistor which addresses these problems by the progress (process) of self-alignment utilizing the good workability of polycrystalline silicon (Japanese Patent Publication (Kokoku) Nos. 55-26630 and 57-32511). It is also known that silicon, tungsten, etc., can be grown selectively only on a region comprising a specific substance of the substrate. As an application of this selective growth for a semiconductor device, it has been proposed, for example, to form an insulating film selectively on a silicon semiconductor substrate, followed by selective epitaxial growth of silicon only on the portion where no insulating film is formed on the silicon substrate, and utilize the selective epitaxial growth region as an active region for the formation of elements and the above insulating film as an element separating region. Also, it has been proposed to embed silicon in an electrode contact window opened in an insulating film on a silicon semiconductor body by a selective growth of silicon in the window to make the top surface of the silicon the same height as the top surface of the insulating film, followed by the formation of wiring on the insulating film and the thus embedded silicon, thereby attempting to flatten the multi-layer wiring. Further, although different from the selective growth method, in order to produce a symmetric bipolar transistor, it is disclosed in Japanese Unexamined Patent Publication (Kokai) No. 57-34365 to form an insulating film on a single crystalline silicon substrate, further form a thin polycrystalline silicon film thereon, followed by formation of an opening portion at the region for formation of an active region by etching the polycrystalline silicon film and the insulating film, and to form a silicon region continuous from the silicon substrate through the above opening portion to the insulating film by a simultaneous growth of silicon on both the single crystalline silicon substrate below the opening portion and on the polycrystalline silicon film (Polycrystalline epitaxially deposited silicon). The silicon on the insulating film is thereafter subjected to patterning by etching. In the above-mentioned bipolar transistor, the base taking-out electrode is made of a polycrystalline silicon because polycrystalline silicon has an excellent workability and enables fine patterning and because it has an excellent adaptability for the self-aligning step. However, although conductivity may be imparted to polycrystalline silicon by the introduction of impurities at a high concentration, its conductivity is still poor when compared with metals, etc., and therefore, a problem arises in that the base resistance becomes somewhat greater; refer to the example of the above bipolar transistor. Also, because it is necessary to introduce an impurity at a high concentration in order to make polycrystalline silicon conductive, the impurity will be diffused during subsequent heat treatment from the conductive polycrystalline silicon to the semiconductor substrate in contact therewith, whereby a problem arises in that the impurity always becomes highly concentrated in this region to sometimes give undesirable effects on element characteristics. On the other hand, a metal is highly electroconductive and generally excellent for electrodes or wiring materials, but does not have a satisfactory workability for such as etching, or controllability, and accordingly, it can be used only with difficulty for a precise process such as the fabrication of a bipolar transistor as described above. EP-A-0 097 918 describes a method for manufacturing a semiconductor device whereby a polycrystalline semiconductor layer is formed on an insulating layer covering the substrate. After forming of an opening in the polycrystalline and insulating layers and thereby exposing a surface of the substrate, a conductive film, such as tungsten, is formed on the polycrystalline layer and on the exposed portion of the substrate. According to the present invention, there is provided a process for fabricating a bipolar transistor comprising the steps of: a) providing a structure having a semiconductor substrate of a first conductivity type, and first and second insulating layers on said semiconductor substrate, said first insulating layer being shaped as an island, said second insulating layer being spaced from said first insulating layer through an opening portion surrounding said first insulating layer, said second insulating layer extending outwardly from the outer periphery of said opening portion; forming on said second insulating layer a nucleating layer, which becomes a nucleus for growth of a metal or metal silicide and has a predetermined pattern extending outwardly from the outer periphery of said opening portion; and also forming a base contact region of a second conductivity type opposite to the first conductivity type, provided on said semiconductor substrate adjacent to its principal surface below said opening portion, b) selectively growing a metal or a metal silicide on said base contact region exposed below said opening portion and on said nucleating layer, to form a base taking-out electrode having said predetermined pattern on said second insulating layer and in contact with said base contact region, c) forming a third insulating layer on an exposed surface of said base taking-out electrode, d) forming an active base region of the second conductivity type and an emitter region of the first conductivity type in said semiconductor substrate below a region surrounded by said base taking-out electrode and said third insulating layer from the principal surface into the inside thereof, said active base region being in contact with said base contact region, said emitter region being in said active base region, and e) using a region of the first conductivity type in said semiconductor structure and in contact with said active base region as a collector region. The present invention may remove the above-mentioned problems. The present invention uses a selective growth of a metal or a metal silicide to form an electrode, wiring, etc. Reference is made, by way of example, to the accompanying drawings in which: Figure 1 is a sectional side view of a bipolar transistor in the prior art; Figs. 2A to 2C sectional side views of a semiconductor device in main steps of a process for fabricating the same embodying the present invention; Figs.3A to 3I are sectional side views and a plan view (Fig.3F only) of a bipolar transistor device in main steps of a process for fabricating the same in an example of the present invention; and, Fig.4 is a sectional side view of a MOS (metal-oxide-semiconductor) transistor device. Referring to Figure 2A, an insulating film 12 is formed on a substrate 11, for example, a semiconductor substrate, and the insulating film 12 has an opening portion 13. On the insulating film 12, a layer 14 as a nucleus for growth of a metal or a metal silicide is formed, and the layer 14 has an end periphery (end portion or edge) along at least a part of an end periphery (edge) of the opening portion 13 and already has a certain pattern. The insulating film 12 and the nucleating layer 14 may be formed in forms adapted for the respective purposes of various applications of the present invention, for example, according to the specific method as described later. However, the nucleating layer 14 should consist of a material on which a metal or a metal silicide can be selectively grown as well as on the substrate 11, and the insulating film 12 should be made of a material on which a metal or a metal silicide cannot be grown. Referring to Figure 2B, when a metal or a metal silicide 15a, 15b is grown selectively on the nucleating layer 14 and on the substrate 11 below the opening portion 13, the metal or the metal silicide 15 at first grows separately on the nucleating layer 14 and on the substrate 11 below the opening portion 13. However, as the growth continues, the metal or the metal silicide 15b growing in the opening portion 13 on the substrate 11 and the metal or the metal silicide 15a growing from the end periphery of the nucleating layer 14 existing along the end periphery of the opening portion 13 toward both the upper portion thereof and the opening portion 13 side, at last become continuous with each other. As the growth further continues, as shown in Fig. 2C, a single metal or metal silicide layer 15 in contact with the substrate 11 and in a desired pattern on the insulating film 12 is obtained. This method has the following characteristics or advantages. (1) Since the layer is made of a metal or a metal silicide, it has high conductivity. Particularly, its electroconductivity is higher when compared with polycrystalline silicon. Therefore, it is very advantageous when used for electrode or wiring materials. (2) No step for etching a metal or a metal silicide is required. Since the pattern of the metal or the metal silicide formed by this method is defined by the shape of the opening portion formed on the insulating film and the pattern of the seed layer formed on the insulating film, the metal or the metal silicide itself is not required to be subjected to etching for patterning. For example, the nucleating layer can be made of polycrystalline silicon, etc., and the insulating film can be made of SiO₂, etc., and pattern formation (etching) of these can be done more easily and with better controllability, compared with the etching of a metal or a metal silicide. Accordingly, the severe formation conditions demanded by devices of various embodiments can be met more favorably when a metal or a metal silicide is to be used for electrodes or wiring. (3) In this method, when the substrate is a semiconductor layer and the electrodes made of a metal silicide layer, by formation of a diffusion region (16 in Fig. 2A to 2C) in the semiconductor layer by introducing an impurity through the opening portion of the insulating film, the electrode window (opening portion of the insulating film), the diffusion region and the electrode can be formed in self-alignment with each other. Further, the electrode window (opening portion of the insulating film) and the pattern of the electrode (pattern of the nucleating layer) can be easily formed self-alignedly according to various methods including conventional and elaborate methods. These matters are also advantageous in assembling electrodes or wirings obtained by this method into various devices. In this method, some of the methods for selective growth of a metal or metal silicide per se are already known and thus it is not particularly limited. For example, E.K. Broadbent and C.L. Ramiller report a selective growth of tungsten in "Selective Low Pressure Chemical Vapor Deposition of Tungsten" (Journal of Electrochemical Society, SOLID STATE SCIENCE AND TECHNOLOGY, June, 1984, P. 1427-1433). According to this report, by CVD based on the reducing reaction of tungsten hexafluoride with hydrogen or silicon, tungsten grows selectively on single crystalline or polycrystalline silicon, but not on an insulating material such as SiO₂ , Si₄N₄ , etc. Suitable reaction conditions are stated to be a low temperature (250-500°C) and a low pressure (0.1-5 Torr), and hydrogen or argon is used together with tungsten hexafluoride as source gases. Also, Japanese Patent Application No. 60-23480 filed by Fujitsu Ltd. discloses a method of selective growth of titanium silicide. According to this patent application specification, an excellent titanium silicide can be grown selectively on silicon by the use of titanium tetrachloride and silane tetrachloride and hydrogen as source gases, and it will not grow on SiO₂ , Si₃N , PSG, BPSG, etc. Preferable reaction conditions are a temperature of 600-900°C and a pressure of 100 Torr or lower. In the above examples, single crystalline and polycrystalline silicon are used as the substrate for selective growth thereon; growth is generally possible on the same material as the metal or the metal silicide to be grown. Thus, the substrate is not limited to a semiconductor but it can be also a metal or a metal silicide. For example, when the substrate consists of a metal or a metal silicide and is a lower wiring layer or a taking-out electrode, it is possible to form an upper wiring layer or a proper wiring by selective growth of a metal or a metal silicide. A process is provided for fabricating a bipolar transistor, which eliminates the problems described above in relation to the prior art. In this process, an insulating layer is formed on a first conductive type semiconductor substrate, an opening portion defining a base contact region surrounding an emitter region (shaped as an island) to be formed on this insulating layer is excavated, and a layer having a predetermined pattern extending outwardly from the outer peripheral of the opening portion (which forms the pattern of the base taking-out electrode combined with the opening portion) is formed on the insulating layer. The last layer is a layer which becomes the nucleus for selective growth of a metal or a metal silicide conducted in the later step (hereinafter called "nucleating layer"), and it can be made of a material which can become a nucleus for growth. At least, the same material as the above substrate could become the nucleus for growth. Also, based on the pattern of the above opening portion, a second conductive type dopant is introduced into the base contact region from the principal surface side of the substrate. In this state, by permitting a metal or a metal silicide to grow under selected specific growth conditions, the metal or the metal silicide can be grown selectively on the substrate below the opening porton (base contact region), and on the above nucleating layer, without growth on the exposed portion of the above insulating layer. As a result of this selective growth, the metal or the metal silicide grown on the base contact region and the metal or the metal silicide grown on the nucleating layer become integrated (combine) to form a base taking-out electrode with a metal or a metal silicide which is a good conductor. Then, an insulating layer is formed on the exposed surface of the base taking-out electrode. This insulating layer can be formed preferably by anodic oxidation of the base taking-out electrode, but it is also possible to first deposit additively an insulating layer, followed by patterning. Subsequently, with the use of the insulating layer and the base taking-out electrode as a mask, in the region surrounded by the insulating layer, namely the region within the semiconductor substrate below the region corresponding to the island-shaped region inside of the above opening portion, an active base region adjacent to the base contact region is formed by introduction of a second conductive type dopant, and an emitter region is formed within the active base region by introduction of a first conductive type dopant. Other steps can be the same as in a conventional method for production of a bipolar transistor, or various modifications may be made. In this production process, since the base taking-out electrode is constituted of a metal or a metal silicide, its electroconductivity is high and the base resistance can be reduced. Also, since the base contact region is formed in alignment with the pattern of the opening portion (base contact window) excavated first in the insulating layer on the semiconductor substrate and the base taking-out electrode is formed on the nucleating layer extending outwardly from the window in alignment with the base contact window, it is not necessary at all to make the area of the base contact region unnecessarily great for obtaining base contact. Further, since the emitter region and the emitter electrode can be formed in alignment with the inner periphery of the base taking-out electrode formed by the selective growth method, it is not also necessary at all to make an area between the base contact region and the emitter region or an area for insulating separation between the base taking-out electrode and the emitter electrode unnecessarily great. Thus, according to a process in accordance with the present invention, it is possible to form a base taking-out electrode and an emitter electrode by making the base region and the emitter region with necessary minimum areas and using a metal or a metal silicide. Therefore, a transistor having very good high frequency characteristics reduced in safety capacity (stray capacitance) and parasitic resistance can be obtained. An example of fabricating a bipolar transistor in which a base taking-out electrode (base connecting electrode) is formed by selective growth of a metal or a metal silicide is given below. Referring to Fig. 3A, a single crystalline silicon semiconductor substrate 21 having a principal surface 22, an n⁺ type embedded layer 23, an n⁻ type epitaxially grown single crystalline silicon layer 24, a locally oxidized film for separation 25, and an n⁺ type collector contact region 26 are prepared according to a conventional method for fabricating a bipolar transistor. Further, an oxide film 27 with a thickness of about 0.1 µm is also formed on the surface not covered with the locally oxidized film 25 of the silicon semiconductor body including 21, 23, 24 and 26. The oxide film 27 may be prepared by oxidation of the silicon substrate surface or by the CVD method. After a polycrystalline silicon layer 28 with a thickness of 0.1-0.3 µm is deposited on the oxide films 25 and 27 by the CVD method, and further a silicon nitride layer 29 with athickness of about 0.3-0.5 µm is deposited thereon, the silicon nitride layer 29 is subjected to patterning to leave the emitter forming portion (30 in Fig. 3F) and remove the base taking-out electrode forming portion (31 in Fig. 3F) which surrounds the emitter forming portion. The silicon nitride layer around the base taking-out electrode forming portion 31 (32 in Fig. 3F), is left. The dimensions of the emitter forming portion 30 may be, for example, 1.0 µm square. Next, when, for example, a PSG layer 33 is deposited to a thickness of about 0.3-0.5 µm by CVD or low pressure CVD on the entire surface of the silicon nitride layer 29 and the polycrystalline silicon layer 28, a concavity or constriction 34 is formed in the layer 33 along the end periphery of the pattern of the silicon nitride layer 29 due to poor coverage at the stepped portion of the ground pattern. Referring to Figure 3B, here the layer 33 is gradually subjected to wet etching by use of, for example, buffer hydrofluoric acid, etching proceeds from the surface of the layer 33 to gradually reduce the thickness of the layer 33, whereupon at the above concavity 34, namely at the outer peripheral portion of the emitter forming portion 30 and the outer peripheral portion of the base withdrawal electrode forming portion 31, etching progresses deeper than at the other portion 33', whereby the surface of the silicon nitride layer 29 and the polycrystalline silicon layer 28 becomes exposed only at that portion. Thus, an opening portion 34 is formed. The opening width of the opening portion 34 is determined by the thickness of the silicon nitride layer 29, the conditions for forming the layer 33, the conditions for etching the layer 33, and the etched thickness of the layer 33, but finally an opening portion 34 with a desired opening width can be formed within a certain range by appropriately selecting the time at which etching of the layer 33 is stopped. For example, here there may be an opening width of 0.2-0.3 µm. Referring to Figure 3C, etching of the polycrystalline silicon layer 28 with the remaining layer 33 acting as the mask results in selective etching only of the portion 35 below the opening portion 34. Subsequently, the layer 33' is removed, whereby, as a consequence, the portions of the oxide films 25 and 27 exposed by the prior etching of the polycrystalline silicon layer 28 are also etched. This is because the layer 33' is made of PSG, while the oxide films 25 and 27 are made of SiO₂. Then, by implantation of boron ions (B⁺) over all the surface, boron ions can be implanted selectively into the n⁻-type epitaxial layer 24 only in the base contact region 36 below the above opening portion 35 along the outer periphery of the emitter forming portion 30 due to the action of the silicon nitride layer 29 and the polycrystalline silicon layer 28 at the mask, whereby at the same time boron ions are selectively implanted into the polycrystalline silicon layer 24 at the base taking-out electrode forming portion 31 due to the action of the silicon nitride layer 29 as the mask. The implantation conditions may be, for example, 30-40 keV, and 1 x 10¹⁴ cm⁻². Referring to Figure 3D, after etching removal of the silicon nitride layer 29, the polycrystalline silicon layer 28 is etched with potassium hydroxide, and the polycrystalline silicon layer 28 remains selectively only at the base taking-out electrode forming portion 31 because the etching speed for the portion implanted selectively with boron ions in the above step is lowered. The structure shown in Figure 3D thus obtained has the insulating layer (oxide film) 27 on the principal surface 22 of the n⁻-type epitaxial silicon layer 24 on which an emitter region and a collector region are to be formed, said insulating layer 27 having an opening portion 35 surrounding the island-shaped emitter forming portion (30) along the outer peripheral portion thereof and a layer (polycrystalline silicon layer) 28 with a predetermined pattern (the pattern which should form the base taking-out electrode) extended outwardly from the outer periphery of the opening portion 25 on the insulating layer 27. The single crystalline silicon in the region 36 and the polycrystalline silicon in the layer 28 are substances which become the seed for a selective growth of tungsten, etc., as hereinafter described. No tungsten, etc., will grow on SiO₂ of layers 25 and 27. The process of the present invention is specific in that the base withdrawal electrode is prepared by selective growth of a metal or a metal silicide with such a structure as the starting point. Accordingly, a series of the steps as explained by referring to Figures 3A to 3D is only an example of the steps for obtaining the structure as shown in Fig. 3D. However, in the series of steps, the base contact region or the base contact window is obtained adjacent to the pattern of the emitter forming portion on a scale of submicron order and besides, the structure as shown in Fig. 3D can be advantageously obtained with the pattern of the silicon nitride layer 29 in Fig. A as the starting point, following subsequently all the self-alignment processes. Referring to Figure 3E, for example tungsten is grown selectively on the epitaxially grown single crystalline silicon 36 (24) exposed below the opening portion 35 and on the polycrstalline silicon layer 28. For example, according to CVD at a low temperature of 250-500°C under a low pressure of 0.1-5 Torr, tungsten can be selectively grown from a mixture of tungsten fluoride (WF6) with argon or hydrogen [ see J. Ecs., June, 1984, P. 1427-1433), see "Selective Low Pressure Chemical Vapor Deposition Method of Tungsten" by E.K. Broadbent at al, supra , etc.,] Thus, after selective growth of tungsten on the base contact region 36 and polycrystalline silicon layer 28, tungstens growing on these two regions become finally integrated to form a base taking-out electrode 37. At this time, the tungsten layer, namely the base taking-out electrode 37, has a thickness of, for example, about 0.3-0.5 µm. Figure 3F is a plan view of Fig. 3E. In this Figure, the dashed portion 37 is the base taking-out electrode, the broken line 38 the outer periphery of the base contact region 36, the broken line 39 the outer periphery of the n⁻-type epitaxial layer 34, the broken line 40 the outer periphery of the n⁺ type collector contact region 36 and the chained line 41 the outer periphery of the n⁺-type embedded layer 23. Referring to Figure 3G, the surface 42 of the base taking-out electrode 37 comprising a metal or a metal silicide is oxidized anodically to be insulated. Next, boron irons (B⁺) are implanted selectively into the active base region 43 with the base taking-out electrode 37 as the mask under conditions of about 30-40 KeV and 5 x 10¹³ cm⁻². During this operation, although not shown in the Figure, the collector contact region is masked with a resist in order to avoid implantation of ions therein. Referring to Figure 3H, emitter diffusion may be effected immediately, but an insulating film 44 with a desired width is provided inside of the inner periphery of the insulating layer 42 in order to avoid inclusion of the outer periphery of the emitter region into the highly concentrated base contact region. This insulating film 44 can be formed by, for example, depositing SiO₂ on the whole surface by CVD and then carrying out anisotropic etching in the direction perpendicular to the principal surface 22 by, for example, reactive ion etching. Since the portion attached to the vertical wall of the step has a thickness with respect to the milling direction (direction perpendicular to the principal surface 22) which is greater when compared with that on the flat insulating layer 42 and on the active base region 43, SiO₂ remains in the latter portion even if the former portion is removed by etching. During this operation, by controlling the amount of etching, the thickness in the lateral direction of the insulating film 44 can be controlled. Also, similar operations can be repeated. Then, a polycrystalline silicon layer 45 doped with arsenic at, for example, about 10²⁰ cm⁻³, is formed inside of the insulating film 44 on the epitaxial silicon layer 24 and, by carrying out heat treatment of, for example, 950-1000°C, for about 30 minutes, arsenic is diffused through the principal surface 22 from the doped polycrystalline silicon layer 45 to form an emitter region 46 with a depth of about 0.15 µm. During the heat treatment, the boron ions previously implanted in the base regions 36 and 43 are also activated at the same time. The base contact region 36 and the active base region 43 become integrated, and the active base region 43 then has a depth of about 0.3 µm. (Here it is clear that the emitter region 46 may be formed by ion implantation, and the emitter electrode may be formed of aluminum, etc., on the principal surface 22). Referring to Figure 31, subsequently, according to conventional methods, an insulating film 47, an emitter electrode 48, a base electrode 49 and a collector electrode 50 are formed. As shown in this Figure, the base electrode 49 is connected to the base taking-out electrode 37. In the series of steps of Figure 3D et seq , the outer periphery of the base contact region 36, and therefore, also the outer periphery of the base region as a whole (36 + 43) and the inner periphery of the base taking-out electrode 37 are defined in alignment with the outer periphery of the opening portion 35, and the inner periphery of the base contact region 36 and the outer periphery of the emitter region 46 are defined in alignment with the inner periphery of the opening portion 35. Thus, since the area of the base region surrounding the emitter region is defined only by the pattern of the opening portion 35, the area can be made smaller with ease. Moreover, since the pattern of the opening portion 35 can be formed with good precision in submicron order only from the pattern of the emitter forming portion of the silicon nitride layer 29 by combination with the steps of Figures 3A to 3D as described above, the area of the base region can be made the minimum necessary size. Also, since the base taking-out electrode of the bipolar transistor obtained according to this process does not consist of a polycrystalline silicon of the example in the prior art, but of a metal or a metal silicide, it has high electroconductivity, thus cancelling the problem that the resistance of the base taking-out electrode worsens the transistor characteristics or the high frequency characteristics of a bipolar transistor are improved. Also, in this process, the base taking-out electrode is formed of a metal or a metal silicide, and therefore, not only is mask alignment not required, but also a step for etching a metal or a metal silicide to form the base taking-out electrode is not required. This is an advantage of the process of the present invention in view of the poor etching controllability of a metal or a metal silicide. Although the above description includes examples of the present invention, the present invention can be variously modified. For example, the opening portion provided in the insulating layer on the semiconductor body may be formed according to any desired method, and may have any desired shape and dimensions. The method for doping the base contact region, the active base region and the emitter region (ion implantation or heat diffusion), the kind of dopant, the forming conditions, and the order of formation of the active base region and the emitter region, are not limited. The materials for the insulating layer and the seed for growth during selective growth may be selected appropriately depending on the metal or the metal silicide employed for selective growth and its growth conditions. The insulating layer on the surface of the base taking-out electrode can be formed according to a method other than anodic oxidation, such as the CVD method, etc. The process of the present invention is not limited to the case of a process for a bipolar transistor as described above, but is clearly applicable for many processes. For example, Figure 4 shows an example of a MOS transistor, wherein 53 shows a p-type silicon substrate, 54 and element separating oxide film, 55 an SiO₂ film, 56 a polycrystalline silicon layer (layer for the seed for growth of a metal or a metal silicide), 57 a source electrode, 58 a drain electrode, 59 an n⁺-type source region, 60 an n⁺-type drain region, 61 an insulating film, 62 a gate oxide film, and 63 a gate electrode. By comparison of this Figure with Figure 3I, it is apparent that this MOS transistor can be easily prepared according to a process similar to the process explained by referring to Figures 3A to 3I. However, in this example, in place of the base taking-out electrode, a source electrode and a drain electrode or a source taking-out electrode and a drain taking-out electrode, are formed as separate patterns. This can be accomplished by merely changing the pattern of the silicon nitride film in the example shown in Figs.3A to 3C.

Claims: A process for fabricating a bipolar transistor comprising the steps of: a) providing a structure having a semiconductor substrate 21 of a first conductivity type, and first 27 and second 25 insulating layers on said semiconductor substrate, said first insulating layer 27 being shaped as an island, said second insulating layer 25 being spaced from said first insulating layer through an opening portion 35 surrounding said first insulating layer 27, said second insulating layer 25 extending outwardly from the outer periphery of said opening portion 35; forming on said second insulating layer a nucleating layer 28, which becomes a nucleus for growth of a metal or metal silicide and has a predetermined pattern extending outwardly from the outer periphery of said opening portion 35; and also forming a base contact region 36 of a second conductivity type opposite to the first conductivity type, provided on said semiconductor substrate 21 adjacent to its principal surface 22 below said opening portion 35, (b) selectively growing a metal or a metal silicide on said base contact region 36 exposed below said opening portion 35 and on said nucleating layer 28, to form a base taking-out electrode 37 having said predetermined pattern on said second insulating layer 25 and in contact with said base contact region 36, (c) forming a third insulating layer 42 on an exposed surface of said base taking-out electrode 37, (d) forming an active base region 43 of the second conductivity type and an emitter region 46 of the first conductivity type in said semiconductor substrate below a region surrounded by said base taking-out electrode 37 and said third insulating layer 42 from the principal surface 22 into the inside thereof, said active base region being in contact with said base contact region 36, said emitter region 46 being in said active base region 43, and (e) using a region 36 of the first conductivity type in said semiconductor structure and in contact with said active base region 43 as a collector region. A process according to claim 1 wherein said nucleating layer 28 is a semiconductor.

Inventors: GOTO, HIROSHI
Applicants: FUJITSU LIMITED
Application year: 1986
Main classification: H01L21
IPC codes: H01L21