COPOLYMER AND PROCESS FOR PRODUCING THE SAME

Abstract: There are disclosed a novel copolymer comprising having recurring unit represented by the formula: wherein Y represents a phenylene group or a naphthylene group, with a recurring number of k and a recurring unit represented by the formula: wherein Ar represents a divalent aryl group, with a recurring number of ℓ, a value of k/(k + ℓ) is 0.5 to 0.97 and having a reduced viscosity [η sp/c ] of 0.3 dℓ/g or higher as measured in p-chlorophenol solution at a concentration of 0.2 g/dℓ at 60 °C, and a process for producing the novel copolymer comprising the steps of: (A) reacting dihalogenobenzonitrile represented by the following formula: wherein X represents a halogen atom, an alkali metal salt of hydroquinone or dihydroxynaph­ thalene represented by the following formula: MO-Y-OM (IV) wherein Y represents a phenylene group or a naphthylene group and M represents an alkali metal, and an alkali metal salt of a divalent phenol represented by the formula: MO-Ar-OM (V) wherein in Ar represents a divalent aryl group and M represents an alkali metal, in the presence of a solvent, and (B) treating the obtained reaction product with water or an alcohol.

Description: This invention relates to a novel copolymer and a process for producing the same, and more particularly, to a novel copolymer which is excellent in heat resistance and capable of controlling its heat resistance, and good in mechanical strength, solvent resistance and flame resistance and also excellent in mechanical properties, particularly in elongation and impact strength than the conventional cyanoaryl ether polymer, and to a process for producing the same. FR-A-2 122 562 discloses a polymer composition which is characterized by a recurring unit of the following formula: wherein R' is a divalent group selected from the group consisting of the groups and -O-R'-O being in positions ortho or para respective to the neighbouring cyano groups, and m being an integer of 0 or 1. R' is not derived from 2,7-naphthylene. For some uses the glass transition temperatures of these prior art polymers are insufficiently high. There are disclosed a polycyanoaryl ether having various structures in Japanese Laid-Open Patent Publication No. 14270/1972. However, there is a disadvantage that these polycyanoaryl ethers are insufficient in heat resistance. Further, in Japanese Laid-Open Patent Publication No. 206433/1984, there is disclosed a cyanoaryl ether polymer obtained by dihalogenobenzonitrile and hydroquinone or biphenol as starting materials. While this polymer is excellent in mechanical strength and heat resistance, its heat resistance cannot be freely controlled and thus it has disadvantage that it cannot flexibly cope with various requests in the various field of use. Further, such a polymer is not necessarily sufficient in view of characteristics such as a mechanical characteristics required for raw materials of electronics and electric devices or mechanical parts. Accordingly, it has earnestly been desired to develop a cyanoaryl ether polymer having excellent mechanical characteristics than that of the conventional one. An object of this invention is to solve the problems as mentioned above and to provide a novel copolymer which is excellent in heat resistance and capable of controlling its heat resistance, and good in mechanical strength, solvent resistance and flame resistance and also excellent in mechanical properties, particularly in elongation and impact strength than the conventional cyanoaryl ether polymer, and to a process for producing the same. The novel copolymer of the present invention comprises having a recurring unit represented by the formula: wherein Y represents a 2,7-naphthylene group, selected from the group consisting of Further, the process for producing the novel copolymer of the present invention comprises the steps of: (A) reacting dihalogenobenzonitrile represented by the following formula: wherein X represents a halogen atom, an alkali metal salt of 2,7-dihydroxynaphthalene represented by the following formula: MO―Y―OM (IV) wherein Y represents a 2,7-naphthylene group and M represents an alkali metal, and an alkali metal salt of a divalent phenol represented by the formula: MO―Ar―OM (V) wherein Ar represents a divalent aryl group selected from the group consisting of and M represents an alkali metal, in the presence of a solvent, and (B) treating the obtained reaction product with water or an alcohol. In the copolymer of the present invention besides (I'), the following recurring unit represented by the formula (II') are preferred: wherein Ar represents a divalent aryl group selected from the group consisting of The total numbers k and ℓ of the respective recurring unit are required to be integers satisfying the relationship of 0.5 ≦ k/(k + ℓ) ≦ 0.97 . If k/(k + ℓ) is less than 0.5, the heat resistance will be lowered and thus it is unfavorable. On the other hand, if k/(k + ℓ) exceeds 0.97, while the heat resistance is excellent, improvement in elongation and impact resistance could not be accomplished and moldability is lowered. Preferably, the relationship of 0.8 ≦ k/(k + ℓ) ≦ 0.95 should be satisfied. In the present invention, the value of the above k/(k + ℓ) affects to the heat resistance. Namely, the heat resistance of the copolymer, particularly a glass transition temperature becomes high with increase of the value of k/(k + ℓ) , and thus by setting the value of k/(k + ℓ) to a desired value, the heat resistance of the copolymer can be controlled. The copolymer of the present invention is blocked at terminal ends thereof with a hydrogen atom, a halogen atom, wherein X represents a halogen atom, and R represents a hydrogen atom, an alkyl group having 1 to 10 carbon atoms, an aryl group, an aralkyl group or a cyano group. The copolymer of the present invention also has a molecular weight corresponding to the reduced viscosity [η sp/c ] which is 0.3 dℓ/g or more as measured in parachlorophenol solution at a polymer concentration of 0.2 g/dℓ at 60 °C. If η sp/c is lower than 0.3 dℓ/g, the mechanical strength and heat resistance of the copolymer are lowered and it is poor for practical use. The copolymer of the present invention is prepared as described below. Namely, the first step of formulating a dihalogenobenzonitrile represented by the formula (III), an alkali metal salt of 2,7-dihydroxynaphthalene represented by the formula (IV) and an alkali metal salt of divalent phenol represented by the formula (V) at a proportion as mentioned below, dissolving them in a solvent as mentioned below, and then reacting them at conditions as mentioned below. In the compound of the formula (III), as a halogen of X, F and Cl are particularly preferred, and specific compounds may include 2,6-dichlorobenzonitrile, 2,4-dichlorobenzonitrile, 2,6-difluorobenzonitrile, 2,4-difluorobenzonitrile, and the like. In the each of compounds of the formulae (IV) and (V), M may be any of alkali metals, and Na and K are particularly preferred. Further, in the compound of the formula (V), Ar is a divalent aryl group selected from the group consisting of Each of the compounds of the formulae (IV) and (V) are prepared by neutralization reaction of an alkali metal salt and 2,7-dihydroxynaphthalene or an alkali metal salt and a divalent phenol having the above Ar. As the alkali metal salts to be used at this time, there may be mentioned potassium carbonate and, potassium hydroxide. For carrying out the reaction, for example, 2,7-dihydroxynaphthalene, the divalent phenol having the above Ar and the alkali metal salt may be added all together in the reaction system without using the compounds of the formulae (IV) and (V) at first. In this case, the compounds of the formulae (IV) and (V) are each produced in the reaction system in accordance with proceeding of the reaction. An amount of the each compounds to be formulated is, when the formulating amounts of the compounds of the formulae (III), (IV) and (V) are designated to as j' mole, k' mole and ℓ' mole, respectively, the relationship of j' = k' + ℓ' should be satisfied. Further, when the amount of j' being slightly in excess of (k' + ℓ') , is preferred since polymerization is promoted. Next, the above k' and ℓ' should be required to satisfy the relationship of 0.5 < k'/(k' + ℓ') ≦ 0.97 in response to the relationship of the aforesaid 0.5 ≦ k/(k + ℓ) ≦ 0.97 . The reaction is carried out in a solvent. The solvent employed may include neutral polar solvent such as dimethylsulfoxide, sulfolane, diphenylsulfone, dimethylacetamide and N-methylpyrrolidone, and it can be used in an amount sufficient to dissolve each of the compounds of the formulae (III), (IV) and (V). The reaction temperature is generally 100 to 350 °C, preferably 150 to 280 °C, more preferably 180 to 210 °C, and the reaction time may be 0.1 to 8 hours, preferably 1 to 6 hours, more preferably 1 to 3 hours. The reaction may be conducted either under ambient pressure or under slight pressurization. In the present invention, during this stage, it is preferred to add a monovalent phenol represented by the following formula as the molecular weight controller: wherein R represents a hydrogen atom, an alkyl group having 1 to 10 carbon atoms, an aryl group, an aralkyl group or a cyano group. In the above formula (VI), R may preferably include a methyl group, (CH₃)₃C-, CH₃(CH₂)₇-, and others. An amount of the molecular weight controller may be decided depending upon the molecular weight of the copolymer to be obtained. In the next step, the reaction product obtained through the above step is treated with water or an alcohol to block the terminals of the copolymer through elimination of the alkali metal at the terminals thereof with H or OH. As the alcohols to be used, methanol or ethanol is preferred. Further, as the treating method, the above reaction product may be thrown into water or the alcohol. Example 1 Into a inner volume of 300-ml separable flask equipped with a fractionating equipment, a stirrer and an argon gas blowing pipe, 17.20 g (0.1 mole) of 2,6-dichlorobenzonitrile, 14.273 g (0.09 mole) of 2,7-dihydroxynaphthalene, 1.09 g (0.01 mole) of hydroquinone, 16.585 g (0.12 mole) of potassium carbonate, 100 ml of sulfolane and 50 ml of toluene were charged, the mixture was stirred while blowing argon gas and reacted at 160 °C for 1.5 hours and further by elevating the temperature to 190 °C for 2 hours. After completion of the polymerization reaction, the resulting product was thrown into methanol to precipitate and recover the copolymer. After the precipitates were crushed by using Blender produced by Warning Co., Ltd., followed by washing with 2 ℓ of boiled water and 2 ℓ of hot methanol, successively and finally dried under reduced pressure at 120 °C for 8 hours. A yielded amount of the resulting copolymer is 25.2 g and a yield is 100 %. Further, the reduced viscosity [η sp/c ] was 1.25 dl/g which was measured in p-chlorophenol solution at a concentration of 0.2 g/dℓ at 60 °C (in the following Examples, the measurement was carried out in the same manner as the above) and the value of k/(k + ℓ) was 0.9. A film was prepared by using this copolymer according to the pressing, and an infrared absorption spectrum (IR) analysis was carried out by using this film. As a result, each absorptions based on C-H bondings of a benzene ring at a portion of 3030 cm⁻¹ and 830 cm⁻¹, C-C bondings of a benzene ring at 1590 cm⁻¹, an aromatic ether bonding at 1240 cm⁻¹ and an absorption based on the presence of a nitrile group at 2220 cm⁻¹, respectively. As to the thermal properties of the copolymer, a glass transition temperature (Tg) was 214 °C, a melting point (Tm) was 308 °C, and a thermal decomposition initiating temperature (Td) was 507 °C (in the air). The following mechanical properties of the copolymer film was measured by using Autograph IS-5000 (trade name) produced by Shimazu Seisakusho K.K. as a tension tester. Yield strength (measured according to ASTM D 638) Fracture strength (measured according to ASTM D 638) Elasticity (measured according to ASTM D 638) Elongation (measured according to ASTM D 638) As results, when a tension speed was 1 mm/min., a yield strength was 13 · 10⁷ Pa (1300 kg/cm²), a fracture strength was 11 · 10⁷ Pa (1100 kg/cm²), an elasticity was 23 · 10⁸Pa (23000 kg/cm²) and an elongation was 50 %. Next, when the solvent resistances of the copolymer were measured, it was insoluble to each solvents of acetone, ethanol, toluene, methylene chloride and chloroform. Further, after the film of this copolymer was exposed to fire of a lighter for 10 seconds, the film was away from fire so that the fire went out at once and no melting away was observed, and thus the film has good flame resistance. Example 2 Copolymer was prepared in the same manner as in Example 1 except that the amount of 2,7-dihydroxynaphthalene to be used in Example 1 was replaced with 9.1 g (0.06 mole) and the amount of hydroquinone to be used was replaced with 4.40 g (0.04 mole). As a result, a yielded amount of a copolymer was 23.9 g (Yield: 100 %) and a reduced viscosity [η sp/c ] was 1.08 dℓ/g and a value of k/(k + ℓ) was 0.6. Results of IR analysis was the same as in Example 1. As to thermal properties of the copolymer, Tg was 204 °C and Td was 526 °C. As to mechanical properties, a yield strength was 13,5 · 10⁷Pa (1350 kg/cm²), a fracture strength was 14 · 10⁷Pa (1400 kg/cm²), an elasticity was 25.10⁸ Pa (25000 kg/cm²) and an elongation was 90 %. As to the solvent resistance and flame resistance of this copolymer, the same results as in Example 1 were obtained. Example 3 Copolymer was prepared in the same manner as in Example 1 except that the hydroquinone was replaced with 2.257 g (0.01 mole) of 2,2-bis(4-hydroxyphenyl)propane as the divalent phenol. As a result, a yielded amount of a copolymer was 26.4 g (Yield: 100 %) and a reduced viscosity [η sp/c ] was 1.34 dℓ/g and a value of k/(k + ℓ) was 0.9. As results of IR analysis, in addition to each absorptions in Example 1, an absorption based on an isopropyl group was observed at a position of 2950 cm⁻¹. As to thermal properties of the copolymer, Tg was 212 °C, Tm was 315 °C and Td was 503 °C. As to mechanical properties, a yield strength was 13 · 10⁷ Pa (1300 kg/cm²), a fracture strength was 11 · 10⁷ Pa (1100 kg/cm²), an elasticity was 26,7 · 10⁸ Pa (26700 kg/cm²) and an elongation was 25 %. As to the solvent resistance and flame resistance of this copolymer, the same results as in Example 1 were obtained. Example 4 Copolymer was prepared in the same manner as in Example 1 except that hydroquinone was replaced with 2.47 g (0.01 mole) of 4,4'-dihydroxydiphenylsulfone as the divalent phenol. As a result, a yielded amount of a copolymer was 26.6 g (Yield: 100 %) and a reduced viscosity [η sp/c ] was 0.48 dℓ/g and a value of k/(k + ℓ) was 0.9. Results of IR analysis were the same as in Example 1. As to thermal properties of the copolymer, Tg was 214 °C, Tm was 511 °C and Td was 519 °C. As to mechanical properties, a yield strength was 10,4 · 10⁷ Pa (1040 kg/cm²), a fracture strength was 11 · 10⁷ Pa (1100 kg/cm²), an elasticity was 28 · 10⁸ Pa (28000 kg/cm²) and an elongation was 40 %. As to the solvent resistance and flame resistance of this copolymer, the same results as in Example 1 were obtained. Comparative Example 1 Into a inner volume of 500-ml separable flask equipped with a fractionating equipment, a stirrer and an argon gas blowing pipe, 17.201 g (0.1 mole) of 2,6-dichlorobenzonitrile, 1.586 g (0.01 mole) of 2,7-dihydroxynaphthalene, 9.811 g (0.09 mole) of hydroquinone, 16.585 g (0.12 mole) of potassium carbonate, 200 ml of sulfolane and 100 ml of toluene were charged, the mixture was stirred while blowing argon gas and reacted at 160 °C for 1.5 hours and further by elevating the temperature to 200 °C for 5 hours. After completion of the polymerization reaction, the resulting product was thrown into water to precipitate and recover the copolymer. After the precipitates were crushed by using Blender produced by Warning Co., Ltd., followed by washing three times with 3.5 l of boiled water and finally dried under reduced pressure at 140 °C over night. A yielded amount of the resulting copolymer was 21.3 g (Yield: 100 %). In order to investigate the molecular weight of the resulting copolymer, the reduced viscosity [η sp/c ], and the value of k/(k + ℓ) were measured, and these results were shown in Table 1. Next, by using this copolymer, a molded product was prepared according to injection molding, and mechanical properties were measured by using this molding product. Namely, the properties at a tension speed of 1 mm/min. were measured and the results are shown in Table 1. Further, measurements of Izod impact resistance (measured according to ASTM D 256 and used a test piece with notch) were carried out, and the results are shown in Table 1. Thermal properties were also measured and the results are shown in Table 1. Comparative Example 2 Copolymer was prepared in the same manner as in Comparative Example 1 except for using 10.461 g (0.095 mole) of hydroquinone and 0.801 g (0.005 mole) of 2,7-dihydroxynaphthalene and the measurements were carried out in the same manner. A yielded amount of the resulting copolymer was 21.3 g (Yield: 100 %). Properties of the resulting copolymer are shown in Table 1. Comparative Example 3 Copolymer was prepared in the same manner as in Comparative Example 1 except for replacing 2,7-dihydroxynaphthalene with 1.602 g (0.01 mole) of 1,6-dihydroxynaphthalene and the measurements were carried out in the same manner. A yielded amount of the resulting copolymer was 21.4 g (Yield: 100 %). Properties of the resulting copolymer are shown in Table 1. Comparative Example 4 Copolymer was prepared in the same manner as in Comparative Example 1 except for replacing 2,7-dihydroxynaphthalene with 0.551 g (0.005 mole) of resorcin and the measurements were carried out in the same manner. A yielded amount of the resulting copolymer was 20.9 g (Yield: 100 %). Properties of the resulting copolymer are shown in Table 1. Comparative Example 5 Copolymer was prepared in the same manner as in Comparative Example 1 except for using 11.01 g (0.1 mole) of hydroquinone without using 2,7-dihydroxynaphthalene and the measurements were carried out in the same manner. A yielded amount of the resulting copolymer was 20.9 g (Yield: 100 %). Properties of the resulting copolymer are shown in Table 1. The results as mentioned above are summarized in Table 1. As apparently seen from the above explanation, the copolymer of the present invention has an excellent heat resistance and is capable of controlling the heat resistance. Further, mechanical strength, solvent resistance and flame resistance of the copolymer are also good and particularly the copolymer of the present invention is superior to the conventional cyanoaryl ether polymers in the mechanical strength, particularly elongation and impact resistance and thus it is available for use of raw materials of electronics and electric devices or mechanical parts.

Claims: A copolymer which comprises having a recurring unit represented by the formula: wherein Y represents a 2,7-naphthylene group, with a recurring number of k and a recurring unit represented by the formula: wherein Ar represents a divalent aryl group selected from the group consisting of with a recurring number of ℓ, a value of k/(k + ℓ) is 0.5 to 0.97 and having a reduced viscosity [η sp/c ] of 0.3 dℓ/g or higher as measured in p-chlorophenol solution at a concentration of 0.2 g/dℓ at 60 °C. A process for producing the copolymer according to claim 1 which comprises the steps of: (A) reacting dihalogenobenzonitrile represented by the following formula: wherein X represents a halogen atom, an alkali metal salt of 2,7-dihydroxynaphthalene represented by the following formula: MO―Y―OM (IV) wherein Y represents a 2,7-naphthylene group and M represents an alkali metal, and an alkali metal salt of a divalent phenol represented by the formula: MO―Ar―OM (V) wherein in Ar represents a divalent aryl group selected from the group consisting of and M represents an alkali metal, in the presence of a solvent, and (B) treating the obtained reaction product with water or an alcohol. A process for producing a copolymer according to Claim 2, wherein a monovalent phenol of the formula: wherein R represents a hydrogen atom, an alkyl group having 1 to 10 carbon atoms, an aryl group, an aralkyl group or a cyano group, is further allowed to react as the molecular weight controller with the copolymer.

Inventors: MATSUO, SHIGERU, MURAKAMI, TOMOYOSHI, TAKASAWA, RYUICHI
Applicants: IDEMITSU KOSAN COMPANY LIMITED
Application year: 1986
Main classification: C08G65
IPC codes: C08G75, C08G65