Reinforced shaped article for sanitary ware and method for producing the same

Abstract: The invention relates to a method for producing shaped articles comprising a thermoplastics show surface and a backing layer of a rigid polyurethane or polyisocyanurate foam by applying a foamable polyurethane or polyisocyanurate composition which is substantially free from appreciable amounts of halocarbon blowing agents, in a closed mould to one face of a shaped thermoplastic sheet provided to one of the matching parts constituting said mould

Description: This invention relates to shaped articles of sanitaryware having a show surface of a thermoplastics material with a reinforcement of a foamed rigid polyurethane composition attached to the back convex surface of the articles, and to a method for producing such articles. The manufacture of polyurethane based layered articles is known. Thus, DE-B 1 064 394 discloses a process to manufacture such layered articles by applying onto a supporting layer, a reaction mixture containing a) an isocyanate-ended prepolymer based on a polyester polyol and b) a dispersion in H 2 O of the remaining polyester polyol, whereas the water acts as a blowing agent. It is claimed that this specific formulation offers the possibility to reduce the reactivity of the starting materials, so that unfavorable temperature rises can be avoided during the manufacture of the layered article. It is also known from "Kunstoffe", vol 72 (1982) no. 5, pp. 279-282, to prepare low density rigid PU foams by using H 2 O as blowing agent. It is shown that low density rigid foams have distortion properties at high temperatures. The manufacture of polyurethane foams by using H 2 O as blowing agent is known as such from EP-A 44226. United Kingdom Patent Application no. 2 148 786 describes laminated articles, such as baths or shower trays, comprising a preformed thermoplastics shell with a reinforcing backing layer of a rigid polyurethane foam. The invention is exemplified with reference to a polyol reactant, an isocyanate reactant and a halocarbon blowing agent. It has been found that the service performance of such an article, as judged by a repeated hot/cold water cycling test leaves something to be desired in that defects appear in the laminated article. For example, delamination of the reinforced foam backing from the thermoplastics sheet is prone to occur. In addition, distortion of the termoplastic shell may occur giving observable surface defects. The present invention provides an improvement in the resistance to delamination or distortion of such articles when subject to repeated hot/cold water cycling. Thus, according to the present invention there is provided a shaped article of sanitaryware comprising a thermo-plastics show surface and a backing layer provided on a convex surface of rigid polyurethane or polyisocyanurate foam of density 300 to 600 kg/m 3 characterised in that the foamable composition contains water as blowing agent added to the polyol component in an amount of 0.05 to 1 wt% and contains less than 1 wt% of a halocarbon blowing agent. The halocarbon blowing agent amount is, particular, less than 0.5 % by weight. Accordingly, the present invention provides a method for producing a shaped article of sanitaryware comprising a thermoplastics show surface and a backing layer provided on a convex surface of a rigid polyurethane or polyisocyanurate foarm of density 300 to 600 kg/m 3 firmly adhered to the said layer by applying a foamable polyurethane or polyisocyanurate foam position in a closed mould to one face of a shaped thermoplastic sheet having a nominal thickness of less than 10 mm and a least 1 mm provided to one of the matching parts constituting said mould, characterised in that the said foamable polyurethane or polyisocyanurate composition contains less than 1 % by weight of composition of a halocarbon blow-. ing agent and contains water as blowing agent added to the polyol component in an amount of 0.05 - 1 wt%. Surprisingly, the use of water as a foaming agent enables the production of a shaped article with noticeably improved resistance to delamination or distortion when subject to elevated temperatures in comparison with the use of conventional halocarbon blowing agents, whereas surprisingly the structural properties of the thus foamed reinforcement are not detrimentally affected. The extent of the improvement will depend not only on the severity of the elevated temperature testing conditions but on the nature of the thermoplastics shell to be reinforced. For example for a given test procedure the extent of the problem to be overcome will be greater the thinner the wall of the shell. This is a particularly important consideration in applications such as sanitaryware where it is usual to make very satisfactory articles, such as baths, from a sheet of thermoplastic having a nominal thickness of 3.2 mm. When such sheet is formed into a bath shell the wall thickness in the areas of the shell which have been subjected to greatest stretch will be considerably less than this. Nevertheless, a long service life for the bath is achieved when the bath shell has been reinforced on its underside with conventional reinforcements such as glass fibre/polyester resin reinforcement. Although sheets of greater thickness, say 5mm, could be used to reduce the extent of the problem the cost involved with the thicker sheet add significantly to the cost to the consumer. The present invention enables rigid polyurethane foam to be used in conjunction with the 3.2 mm sheet to produce articles of sanitaryware which meet the requirements. of the standard test used in the industry to assess suitability in service. Thus the invention provides an article of sanitaryware formed form a thermoplastics sheet having a nominal thickness of less than 10 mm and at least 1 mm and a polyurethane or polyisocyanurate rigid foam composition as backing wherein the article of sanitaryware meets the standard required of the proposed Final Draft of the CEN Standard No. pr EN 198-1 entitled Baths for Domestic Purposes made from Acrylic Materials : Part 1: Specification for Finished Baths. Generally the standards request that the wall thickness of the shell should not be reduced as a result of the thermoforming of the shell from the sheet to less than 0.7 mm in any area of the shell. It has however been found that in articles of sanitaryware according to this invention the minimum acceptable thickness of the shell after thermoforming may considerably be reduced without negative effects. The polyurethane and polyisocyanurate compositions used in the invention are known in the art. Thus the organic di- or polyisocyanate component of the composition may be any of the isocyanates known to be useful for the formation of polyurethane and polyisocyanurate foams. Of particular interest are aromatic di-or polyisocyantes, for example tolylene diisocyanate and especially diphenylmethane diisocyanate (MDI) which are commerically available in a variety of forms. Suitable diphenylmethane di-isocyanates include : (a) diphenylmethane - 4,4' - diioscyanate and mixtures thereof with other isomers of diphenylmethane diisocyanate; (b) methylene bridged polyphenylpolyisocyanates prepared by phosgenation of mixtures of appropriate polyamines obtained by the condensation of aniline and formaldehyde and known as "polymeric" MDI, the composition of which may subsequently be varied by distillation, crystallisation or other separation techniques to give products with a weight average functionality in the range 2 to at least 3.3; (c) polymers and oligomers obtained by reacting diphenylmethane diisocyanates or "polymeric MDI" with a monomeric glycol or polyhydric alcohol (or mixtures thereof) or with a hydroxylended polyester or polyether and known as "MDI prepolymers"; and (d) modified diphenylmethane diioscyanates or "polymeric MDI" in which a proportion of the isocyanate groups are converted into other groups such as carbodiimide, uretonimine, biuret or allophanate groups, or in which a proportion of the isocyanate groups are reacted with an isocyanate-reactive compound. The polyol component is a polyether or polyester polyol suitable for the preparation of rigid foam polyurethanes. Typical polyols include propylene oxide adducts of polyfunctional hydroxy compounds (pentaerythritol, sorbitol, alpha-methylgluocoside, sucrose. phenol-formaldehyde resins, and others) and propoxylated polyfunctional amino alcohols and diamines. The blowing agent should be substantially free from appreciable amounts of halocarbon blowing agents. Water is used as blowing agent. Suitable foams can be produced using low concentrations of water. The water is used as an additive to the polyol composition in a concentration of 0.05 % to 1 % by weight of the polyol. The concentration should be chosen to give a required density. The thermoplastics material of the shell may be any material which will provide a durable, and preferably aesthetically attractive show surface for the article. A preferred material is the acrylic sheet, widely used for sanitaryware, consisting wholly or partly of poly(methylmethacrylate). Laminates of two types of thermoplastics, in which at least an outer layer of the laminate can provide a durable show surface may be employed. For example, laminates of an acrylic polymer with the acrylonitrile/butadiene/styrene copolymer known as ABS may be employed. The thermoplastics material forming the show surface can contain any of the auxiliary additives conventionally present in such sheet, particularly the colourants which give acrylic sheet its attractive appearance. The composition of the invention is conveniently applied to the underside of the thermoplastics sheet in a closed mould with the thermoplastics sheet being in the form of a shell which conforms closely to the shape of the male mould half of a pair of matching mould halves and the composition being injected into a space left between the female mould and the underside of the sheet. For these applications where the reinforcement is provided on a convex surface, for example the underside of an article of sanitaryware the density of the foam should be within the range 300 - 600 kg/m 3 . The rigid foam may constitute the sole reinforcement in the backing layer of alternatively other aids to reinforcement may be included. Thus the foamable composition may contain a proportion of short glass fibres intimately dispersed in the composition. Yet again, a glass fibre mat of long fibres may be included in the lay-up in the mould so that the composition penetrates between the fibres of the mat during injection. The invention also includes providing reinforcement using glass fibres impregnated with curable polyester compositions which reinforcement is adhered to at least part of the underside of the thermoplastic shell before the shell is placed in the mould and the rigid foam applied. This operation should be avoided if cost is an important consideration but may be useful if additional reinforcement is required. Additional reinforcement may also be provided in the form of a rigid member or members which can be embedded in the rigid foam by inclusion in the mould lay-up between the shell and the female mould half. Such rigid members include metal rods or chipboard. The use of metal rods is particularly useful in the case of the production of articles, such as sanitaryware, from 3.2 mm thick sheet because of an additional problem which may arise when the shell does not conform closely in shape with the male mould. In such circumstances the heat of reaction evolved in the curing operation may be sufficient to cause distortion of the bath shell with the resulting effect that the demoulding from the original shape of the shell may be so pronounced that the article is unsaleable. The presence of metal rods has been found to provide a means of overcoming this problem when using 3.2 mm thick sheet. In addition to the various additional reinforcements which may be provided in the rigid foam the foamable composition may contain other additives which provide further benefits. Thus chopped glass fiber and other known filler materials may be used as heat sink means to avoid distortion of the thermoplastic bath owing to the heat of reaction evolved in the curing operation of the foam. Comparative Example A A sheet of poly(methyl methacrylate) of thickness 3.2 mm and dimensions 800 mm × 570 mm was shaped into an acrylic shell having a base area approximately 430 mm × 210 mm. The depth of draw was 220 mm resulting in the base having a thickness of about 1 mm with the corner portions being reduced to about 0.75 mm. The underside of the shell was cleaned with solvent before the shell was assembled in a matched epoxy male and female mould assembly, the shape of the male mould conforming closely to that of the shell so that the shell closely contacted the male mould. The moulds were provided with internal water circulation to provide some temperature control. The mould cavity was nominally 10 mm in thickness. The temperature of the male mould was set at 25 deg. Celsius and the female mould at 40 deg. Celsius. A mixture of the polyol 'Daltolac' K1328 and the isocyanate 'Suprasec' DND in the weight ratio 100 : 109, containing 4 parts by weight (based on the K1328) of 'Arcton' 11 blowing agent in the polyol was mixed using a Cannon H40 metering unit and injected into the mould backing for the acrylic shell. ('Daltolac', 'Suprasec' and 'Arcton' are Registered Trade Marks of Imperial Chemical Industries PLC). The shot weight was measured at 2.2 kg. After ten minutes the article was removed from the mould. The polyurethane was firmly bonded to the acrylic shell. The density of the foam backing produced was 330 kg/m 3 . Examination of the show surface of the article showed that the surface was of acceptable quality and that no significant distortion of the shell had occurred during the curing process. This sink was tested on a repeated hot and cold water cycling test based on that used by the acrylic bath manufacturers. Water at 75 deg. Celsius was introduced into the sink to a depth of 11 cms and left in for 10 mins. It was then pumped from the sink and replaced by the same quantity of water at 16 deg. Celsius. After 10 mins the cold water was removed. This double filling operation constitutes one cycle of the water test. The sink was repeatedly cycled until failure of the top surface occurred. Failure was judged to be any surface irregularity caused by the water in particular or blistering of the acrylic sheet away from the reinforcing material. A number of blisters had appeared in the base corner areas of the sink after 45 water cycles and after 68 cycles there were 8 blisters sized 2.5 cm × 2.5 cm (on average) on the base section and on the sides adjacent to the corner areas. The test was terminated at this point. EXAMPLE 1 The procedure of Comparative Example A was repeated except in that the halocarbon blowing agent in the polyol was replaced with 0.25 parts by weight (based on the polyol) of water. Using a total shot weight of 2.2 kg the procedure was repeated. A sink having excellent appearance was produced. The sink was tested by the same water cycling test as used in the comparative Example. After 100 cycles there were no blisters in the acrylic surface. In a more severe test the sink was subjected to 20 further cycles using water at 90 deg. Celsius and 16 deg. Celsius. No damage to the article was observed.

Claims: Method for producing a shaped article of sanitaryware comprising a thermoplastics show surface and a backing layer, provided on a convex surface, of a rigid polyurethane or polyisocyanurate foam of density within the range 300 to 600 kg/m 3 firmly adhered to the said layer by applying a foamable polyurethane or polyisocyanurate composition comprising an organic di- or polyisocyanate component and a polyol component in a closed mould to one face of a shaped thermoplastic shell formed from a thermoplastic sheet having a nominal thickness of less than 10 mm and at least 1 mm provided to one of the matching parts constituting said mould, characterised in that the said foamable polyurethane or polyisocyanurate composition contains water as blowing agent added to the polyol component of the foamable composition in an amount of 0.05 to 1 % by weight based on the polyol weight and contains less than 1 % by weight of a halocarbon blowing agent. Method according to claim 1, characterised in that the foamable composition also contains short glass fibres dispersed in the composition. Shaped article of sanitaryware having a show surface of thermoplastic material with a reinforcement of a rigid polyurethane or polyisocyanurate foam, produced according to the method of claim 1.

Inventors: NICHOLL GERALD NEWTON, WOOD RICHARD, NICHOLL, GERALD NEWTON, WOOD, RICHARD
Applicants: ICI PLC, IMPERIAL CHEMICAL INDUSTRIES PLC
Application year: 1986
Main classification: C08J9
IPC codes: B32B5, B29C44, C08J9, B29C45, B29C39, B29K105, B29L22, B29K75