ENZYME IMMOBILIZED MEMBRANE FOR A SEMICONDUCTOR SENSOR AND METHOD FOR PRODUCING SAME

Abstract: An enzyme immobilized membrane and a method for pro­ ducing the same are disclosed in which the portion of an en­ zyme membrane having photo crosslinking, even if containing an excessive amount of an enzyme, does not peel off from a sensitive portion of an enzyme sensor. Elution of the enzyme from the enzyme membrane can be effectively prevented, and an enzyme immobilized membrane having a limited area and high mechanical strength can be produced with good re­ produceability. An aqueous solution, composed of a water soluble photosensitive resin including polyvinyl pyrrolidone (109) and a cyclopentanone sodium salt (110) and an enzyme (102), is coated on a base (101) and dried so as to form an en­ zyme membrane. Then, light of an appropriate wavelength such as ultraviolet light is irradiated on the enzyme membrane to provide photo crosslinking between the polyvinyl pyrroli­ done, the cyclopentanone sodium salt, and the enzyme. Such enzyme immobilized membranes can be directly formed on the ion-sensitive portions of pH-ISFETs so as to form a semicon­ ductor enzyme sensor.

Description: BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates generally to membrane immobilized enzymes and a method for producing the same, and more specifically, to a semiconductor enzyme sensor utilizing suchmembraneimmobilized enzymes . 2. Description of the Prior Art In the past, enzymes have been industrially utilized as catalists particularly in the fermentation industry, and the like. In general, enzymes were dissolved or dispersed in aqueous solutions for promoting various chemical reactions and, after completion of the reactions, the enzymes were not recovered from the solutions but discarded uselessly each time respective reactions had been finished. In recent years, however, enzyme immobilization techniques have been developed which enable repeated use of enzymes in a stable state, whereby areas of utilization of enzymes have been rapidly expanded, for example, to a field of measuring various items of chemical substances in addition to traditional fields of fermentation, syntheses of chemical substances, and the like. The measurements of concentrations of respective components contained in body fluids such as blood or urine are very important for clinical diagnosis and thus there have been made developments and/or improvements of various kinds of quantitative measurements. Of these, many enzyme sensors have been proposed which are able to effect quick and continuous measurements by employing membrane immobilized enzymes and varying kinds of electrodes. Such enzyme sensors have been studied since about 1970 and today it becomes possible to measure chemical and physical quantities of a wide variety of substances by the use of enzyme sensors. In the enzyme sensors fabricated in the early years, a membrane immobilized enzyme was physically or chemically adhered to a sensitive portion of an enzyme sensor which is adapted to convert physical or chemical quantities such as temperature, ion concentration, gas concentration or the like into electrical signals. In these days, however, in accordance with miniaturization and/or multiplication of enzyme sensors, it becomes necessary to selectively form a membrane immobilized enzyme on a limited area of a sensitive portion of a sensor. In order to measure chemical quantities of a substance, a membrane immobilized enzyme is suited which has a thin thickness and a limited area. Biosensors are typical examples of sensors utilizing membrane immobilized enzymes for measurements of chemical substances. Such a biosensor comprises a membrane immobilized enzyme, and a transducer adapted to detect substances consumed or produced in the membrane and generate electrical signals upon detection of such substances. In this case, the membrane immobilized enzyme serves to discriminate a specific chemical substance to be measured, and cause a change in quantity of a material which corresponds to a change in the chemical substance and which is able to be detected by the transducer. Among such biosensors, there are known those which employ a combination of a glucose-oxidase immobilized membrane and an oxygen electrode, a combination of a glucose-oxidase immobilized membrane and a hydrogen peroxide electrode, a combination of glucose-oxidase enzyme immobilized membrane and a pH electrode, or the like. Glucose oxidase acts to decompose the glucose in a membrane immobilized enzyme into gluconic acid and hydrogen peroxide according to the following reaction equation: glucose + O₂ ⇄ -gluconic lactone + H₂O₂ ⇄ gluconic acid + H₂O₂ (1) Accordingly, it is possible to measure the concentration of glucose by detecting the quantity of oxygen consumed in the above reaction at the oxygen electrode, the quantity of hydrogn peroxide produced in the above reaction at the hydrogen peroxide electrode, and a reduction of pH due to production of gluconic acid at the pH electrode. Further, in order to form a membrane immobilized enzyme as employed in a miniaturized or multiplicated enzyme sensor as referred to above, a water soluble photosensitive resin such as, for example, photosensitive polyvinyl alcohol (PVA) is subject to a photolithographic process. Figs. 1A through 1C show a series of procedures in a conventional method for forming a membrane immobilized enzyme from a photosensitive resin by means of photolithography. In these figures, reference numeral 1 designates a base or substrate such as, for example, a silicon wafer having a thermally grown oxidized film or membrane, a base board having amino groups introduced therein through a silane coupling agent, a transducer, a semiconductor sensor or the like. Provided on the entire surface of the substrate 1 by spin coating is an enzyme membrane 3 formed of a water soluble photosensitive resin containing an enzyme 2 such as glucose oxidase dissolved therein, as illustrated in Fig. 1A. Then, the enzyme membrane 3 thus formed is irradiated by ultraviolet light or visible light 6 through an appropriate photomask or filter 5 so that only a specific portion 4 of the enzyme membrane 3 or a sensitive portion 4 of the substrate 1 is subject to the irradiation of the light to provide photo crosslinking therein (see Fig. 1B). Thereafter, the remaining portion of the enzyme membrane 3, not irradiated by the lihght 6 and having no photo crosslinking, is developed and washed with water (see Fig. 1C). With the above-described conventional method for forming a membrane immobilized enzyme, there arise the following problems due to the water development carried out after formation of photo crosslinking. Specifically, the specific portion having photo crosslinking is liable to be peeled off during the water development, and has no sufficient mechanical strength for use in an aqueous solution; and the enzyme immobilized in the enzyme membrane 3 is liable to elute therefrom. Such phenomena become more remarkable as the amount of enzyme in the enzyme membrane 3 increases. In particular, with a PVA membrane, a great amount of enzyme can not be dissolved into the membrane because too much dissolution of the enzyme causes phase separation. As a result, it is difficult to produce a highly sensitive biosensor in accordance with the conventional method for forming a membrane immobilized enzyme. In order solve the above-described problems, it is general, for a membrane immobilized enzyme in an enzyme sensor for measuring glucose, to form crosslinking between glucose oxidase and bovine serum albumin by means of glutaraldehyde. Fig. 2 is an imaginary view showing a glucose-oxidase immobilized membrane formed on a base or transducer 1 having amino groups introduced thereinto by a silane coupling agent. In the above glucose-oxidase immobilized membrane forming method, an enzyme 2 in the form of glucose oxidase and bovine serum albumin 7 are dissolved into an aqueous solution, and then mixed with a solution containing an appropriate concentration of glutaraldehyde 8. The mixture thus formed is coated on the base 1 and kept in his state so that chemical crosslinking is produced between enzyme 2 - enzyme 2, enzyme 2 - bovine serum albumin 7, bovine serum albumin 7 - bovine serum albumin 7, and enzyme 2 - amino groups on the surface of the base 1, bovine serum albumin 7 - amino groups on the base surface under the action of glutaraldehyde. In this manner, the enzyme 2 is captured in a three-dimensional polymer membrane, as illustrated in Fig. 2, and thus becomes unsoluble in water and immobilized. With recent enzyme sensors, there is a strong need for miniaturization and hence finely machinable materials and production methods therefor are required for such glucose-oxidase immobilized membranes. The conventional glucose-oxidase immobilized membranes are produced from the above-mentioned finely machinable materials in accordance with the above methods, but involve a problem in that it is impossible to form membrane immobilized enzymes having limited areas with good reproduceability. Although there have been made many attempts to miniaturize the above-described conventional enzyme sensors, it is difficult to reduce the size of a substrate electrode and hence of the enzyme sensors. Further, it is extremely difficult to produce multiple-enzyme sensors each of which is capable of simultaneously detecting various substrates. In addition, in the conventional method, it is necesary to prepare membrane immobilized enzymes respectively which are then mounted on a substrate electrode, and therefore such a method is cumbersome and complicates the construction of each sensor. SUMMARY OF THE INVENTION Accdordingly, the present invention is intended to solve the above-described problems of the prior art. A primary object of the present invention is to provide a novel and improved glucose-oxidase immobilized membrane and a method for producing the same in which the portion of an enzyme membrane having photo crosslinking, even if containing an excessive amount of an enzyme, does not peel off from a sensitive portion of an enzyme sensor, and in which elution of the enzyme from the enzyme membrane can be effectively prevented, and in which a membrane immobilized enzyme having a limited area and high mechanical strength can be produced with good reproduceability. Another object of the present invention is to provide a novel and improved semiconductor enzyme sensor and a method for producing the same in which a membrane immobilized enzyme can be directly formed on an ion-sensitive surface of a hydrogen ion-sensitive field effect transistor (hereinafter referred to as pH-ISFET), thereby making it easy to miniaturize the entire sensor, and which can be manufactured in an easy and efficient manner, and which has high sensitivity. A further object of the present invention is to provide a novel and improved semiconductor enzyme sensor and a method for producing the same in which a plurality of membrane immobilized enzymes can be directly formed on the respective ion-sensitive surfaces of plural pH-ISFETs, thereby making it easy to produce a multiple-enzyme sensor in a simple way, and which has high sensitivity. In order to achieve the above objects, according to one aspect of the present invention, there is provided a membrane immobilized enzyme comprising: a water soluble photosensitive resin including polyvinyl pyrrolidone having an average molecular weight of tens of thousands to hundreds of thousands and an aromatic group-containing azido compound; and an enzyme; characterised in that the aromatic group-containing compound is 2,5-bis (4'-azide-2'-sulfobenzol) cyclopentanone sodium salt. The membrane immobilized enzyme is particularly useful in cases where it contains a limited amount of enzyme. On the other hand, when the amount of enzyme contained in the membrane immobilized enzyme is relatively great, it is preferable that themembraneimmobilized enzyme further comprise glutaraldehyde, and a material adapted to cooperate with glutaraldehyde to form chemical crosslinking for improved mechanical strength. Preferably, the enzyme is selected from the group consisting of glucose oxidase, ureaze and lipase. Preferably, the material adapted to cooperate with glutaraldehyde to form chemical crosslinking is selected from the group consisting of bovine serum albumin, polyamino acid, and polyamino acid copolymer. In a preferred embodiment, the polyvinyl pyrrolidone having an average molecular weight of tens of thousands to hundreds of thousands is 2 - 20 weight %; and the 2, 5-bis (4'-azide-2'-sulfobenzal) cyclopentanone sodium salt is 0.5 - 1.5 weight %; and the enzyme comprises glucose oxidase of 5.0 - 7.5 weight %. Also, the membrane immobilized enzyme further comprises bovine serum albumin of 5 - 10 weight %. According to another aspect of the present invention, there is provided a method for producing a membrane immobilized enzyme which comprises the steps of: coating on a base an aqueous solution which is composed of a water soluble photosensitive resin including polyvinyl pyrrolidone having an average molecular weight of tens of thousands to hundreds of thousands and 2, 5-bis (4'-azide-2'-sulfobenzal) cyclopentanone sodium salt, and an enzyme; drying the aqueous solution thus coated on the base so as to form a membrane immobilized enzyme ; and irradiating ultraviolet light on the membrane immobilized enzyme to provide photo crosslinking between the polyvinyl pyrrolidone, the cyclopentanone sodium salt, and the enzyme. The membrane immobilized enzyme , after having been irradiated by the ultraviolet light, may be dipped into an aqueous solution of glutaraldehyde so as to form chemical crosslinking. As a result, proteins in themembraneimmobilized enzyme are chemically crosslinked with each other under the action of glutaraldehyde whereby the mechanical strength of the membrane immobilized enzyme is markedly increased, thus preventing elution of the enzyme. Preferably, the glucose-oxidase immobilized membrane is washed away by a buffer solution, dipped into an aqueous solution of glycine, and again washed away by a buffer solution for removal of the residual glutaraldehyde. According to a further aspect of the present invention, there is provided a semiconductor enzyme sensor comprising: a first pH-ISFET having a first membrane immobilized enzyme connected thereto, the first membrane being composed of a first water soluble photosensitive resin including polyvinyl pyrrolidone having an average molecular weight of tens of thousands to hundreds of thousands and 2, 5-bis (4'-azide-2'-sulfobenzal) cyclopentanone sodium salt, and a first enzyme; a second pH-ISFET; and a reference electrode. In a further preferred embodiment, the semiconductor enzyme sensor may further comprise a third pH-ISFET having a second enzyme immobilized membrane connected thereto, the second membrane being composed of a second water soluble photosensitive resin including polyvinyl pyrrolidone having an average molecular weight of tens of thousands to hundreds of thousands and 2, 5-bis (4'-azide-2'-sulfobenzal) cyclopentanone sodium salt, and a second enzyme. The first and/or secondmembraneimmobilized enzyme may be directly coated and hardened on the respective pH-ISFETs so that it becomes easy to miniaturize and manufacture the entire semiconductor enzyme sensor. In addition, the sensor thus formed has an extended satisfactory life in service. Specifically, the above photesensitive resin is by far durable against H₂O₂ which necessarily results as a by-produced during production of a glucose sensor, as compared with conventional photosensitive resins such as PVT. Moreover, the above photesensitive resin is easy to synthesize or prepare, able to have a great amount of enzyme dissolved therein, highly sensitive, and can provide an membrane immobilized enzyme at low costs. On the other hand, PVA conventionally used is sensitive to lights of relatively large wavelength so that when a mask is fitted to a covering layer of PVA before subjected to exposure, such a PVA coverings layer often causes partial crosslinking. To prevent this, an exposure device is required to take a special measure. In contrast, the photosensitive resin of the present invention requires no such measure or any other adjustments. Preferably, each of the first and second membrane immobilized enzymes are formed by coating on a pH-ISFET an aqueous solution containing a water soluble photosensitive resin, glucose oxidase, bovine serum albumin, and hardening the aqueous solution thus coated by irradiation of ultraviolet light. These membrane immobilized enzymes may be dipped into a glutaraldehyde solution to form chemical crosslinking for improved mechanical strength. It is preferable that the first and second membrane immobilized enzymes be formed through patterning on the ion-sensitive surfaces of the respective pH-ISFETs by means of photolithography. In this case, each of themembraneimmobilized enzymes can be readily and efficiently connected or bonded through a water soluble photosensitive resin to only the specific ion-sensitive surface as required of each pH-ISFET which can be very limited in size (for example, several mm in length and width). Thus, a multiple enzyme sensor having a plurality of sensing portions can be obtained in an easy and efficient manner which is sensitive to a plurality of different materials. This multiple sensor is independently usable by itself, or can be formed into an intelligent sensor which has an information processing circuit adapted to receive outputs of the various sensing portions for making comprehensive judgement. The semiconductor enzyme sensor may further include one or more pH-ISFETs each having a further membrane immobilized enzyme connected thereto. In this case, the further membrane is preferably composed of a further water soluble photosensitive resin including polyvinyl pyrrolidone having an average molecular weight of tens of thousands to hundreds of thousands and 2, 5-bis (4'-azide-2'-sulfobenzal) cyclopentanone sodium salt, and a further enzyme. The above and other objects, features and advantages of the present invention will become apparent from the following detailed description of several presently preferred embodiments of the invention when taken in conjunction with the accompanying drawings. BRIEF DESCRIPTION OF THE DRAWINGS Figs. 1A, 1B and 1C are cross sectional views of a conventional semiconductor enzyme sensor, respectively showing a series of processes in accordance with a conventional method for producing a membrane immobilized enzyme ; Fig. 2 is a schematic view showing a conventional glucose oxidase immobilized membrane formed on a base; Figs. 3A, 3B and 3C are schematic views showing a series of processes in accordance with a method of the invention for producing a glucose-oxidase immobilized membrane; Fig. 4 is a partially cutaway plan view of a semiconductor enzyme sensor having a glucose-oxidase immobilized membrane formed on a pH-ISFEF in accordance with the present invention; Fig. 5 is a cross sectional view taken along the line V-V in Fig. 4; Fig. 6 is a perspective view of another semicondutor enzyme sensor in accordance with the present invention; Fig. 7 is a perspective view showing a pH-ISFET chip having a plurality of substrate electordes from which the semiconductor enzyme sensor of Fig. 6 is formed; Fig. 8 is a perspective view showing a glucose sensor having a glucose-oxidase immobilized membrane formed on only a portion of its ion-sensitive surface; Fig. 9 is a perspective view of a multiple enzyme sensor in accordance with the present invention; Fig. 10 is a graphic illustration showing a response characteristic of the glucose sensor of Fig. 8; Fig. 11 is a graphic illustration showing a relationship between the output power and the glucose concentration in the glucose sensor of fig. 8; and Fig. 12 is a graphic representation showing changes in output power of multiple enzyme sensors of the invention over time. DESCRIPTION OF THE PREFERRED EMBODIMENTS The present invention will now be described in detail with reference to the accompanying drawings. In the following description and the accompanying drawings, the same or corresponding components or elements in the illustrated embodiments of the invention are identified by the same reference numerals. Figs. 3A, 3B and 3C schematically illustrate a series of processes in a method for producing membrane immobilized enzymes according to the present invention. In these figures, the enzyme immobilized membrane in the form of a glucose-oxidase immobilized membrane of the invention is formed on a base 101 and comprises an enzyme 102 in the form of glucose oxidase, gultaraldehyde 108, a material 107 in the form of bovine serum albumin adapted to cooperate with glutaraldehyde to form chemical crosslinking, and a water soluble photosensitive resin including polyvinyl pyrrolidone 109 and 2, 5-bis (4'-azide-2'-sulfobenzal) cyclopentanone sodium salt 110. According to the present invention, an aqueous solution A containing glucose oxidase 102, the water soluble photosensitive resin and bovine serum albumin 107 is first coated on the surface of the base 101, and dried to provide a covering layer or membrane of which a specified portion is then irradiated by ultraviolet light 106 so as to form photo crosslinking therebetween, as pictured in Fig. 3A. Subsequently, the covering layer thus formed on the base 101 is developed by water to obtain a glucose-oxidase immobilized membrane B (Fig. 3B) which is further treated by glutaraldehyde 108 to form chemical crosslinking for increased mechanical strength thereof. Futher, where the glucose-oxidase immobilized membrane is formed on the entire surface of the base 1, it is preferable to use an aqueous solution containing glutaraldehyde of 10 - 25 weight percent. On the other hand, in the event that such a glucose-oxidase immobilized membrane is formed on only a specific portion of the base surface, ultraviolet light 6 is irradiated on only the specific portion of the base 1 and then developed by a 1 - 5% glutaraldehyde solution so as form chemical crosslinking in the photo crosslinked portion thereof while dissolving the remaining portion thereof having no photo crosslinking for removal. Figs. 4 and 5 show a semiconductor enzyme sensor which includes two pH-ISFETs having a membrane immobilized enzyme fabricated in accordance with the present invention. The sensor illustrated has a pH-ISFET chip or element 112 firmly or integrally mounted on an epoxy resin board 111 by means of an epoxy resin covering layer 119. The pH-ISFET chip 112 is provided on its one side surface with a first pH-ISFET 117 and a second pH-ISFET 118. The first pH-ISFET 117 has a first source electrode 113 and a first drain electrode 114 extending in a spaced parallel relation with each other, and the second pH-ISFET 118 has a second source electrode 115 and a second drain electrode 116 extending in a spaced parallel relation with each other. These first and second source and drain electrodes 113 through 116 are electrically connected to a measuring circuit (not shown) via respective leads 120. The first pH-ISFET 117 has a pair of first spaced ion-sensitive portions 113a, 114a formed integrally with the first source and drain electrodes 113, 114 at their distal ends. A membrane immobilized enzyme 121 is formed on the first ion-sensitive portions 113a, 114a of the first pH-ISFET 117 in accordance with the method of the invention as described in the foregoing with reference to Figs. 3A through 3C. The second pH-ISFET 118 has a pair of second spaced ion-sensitive portions 115a, 116a formed integrally with the second source and drain electrodes 115, 116 at their distal ends, the second ion-sensitive portions 115a, 116a being provided with no membrane immobilized enzyme and thus exposed outwards. Though not shown in Figs. 4 and 5, a reference or pseude electrode such as, for example, a known silver-silver chloride electrode is usually required. In this manner, the semiconductor enzyme sensor is comprised of the first pH-ISFET 117 provided with the membrane immobilized enzyme 121, the second pH-ISFET 118 having no membrane immobilized enzyme , and the reference electrode (not shown). Fig. 6 shows another pH-ISFET chip or element 112' for a semiconductor enzyme sensor in accordance with the invention, and Fig. 7 shows a substrate from which the pH-ISFET chip is formed. In these figures, the composite pH-ISFET chip 112' comprises a first pH-ISFET 117 including a first source electrode 113 and a first drain electrode 114, a second pH-ISFET 118 including a second source electrode 115 and a second drain electrode 116, and a reference or pseude electrode 122. The composite pH-ISFET chip 112 can be fabricated in accordance with a known method for producing a usual metallic oxide type field effect transistor. The first and second pH-ISFETs 117 and 118 are sensitive to hydrogen ions independently of each other so that they can measure the pH of a solution by measuring the current flowing between the source and drain electrodes 113 and 114 or 115 and 116 of the first or second pH-ISFET 117 or 118 when a predetermined voltage is applied between the source and drain electrodes, or alternately by measuring a source voltage required to be imposed between the source and drain electrodes for causing a predetermined level of current to flow across the source and drain electrodes. The first source and drain electrodes 113 and 114 of the first pH-ISFET 117 have a pair of spaced opposite ion-sensitive porions 113a and 114a integrally formed with their distal ends. Provided on a specified portion of the surface of the pH-ISFET chip 112 is a membrane 121 containing an immobilized enzyme, the ion concentration in the enzyme being adapted to change in accordance with the amount of reaction thereof with a substrate solution. The membrane immobilized enzyme 121 is secured to the surface of the pH-ISFET chip so as to cover the ion-sensitive portions 113a and 114a of the first pH-ISFET. On the other hand, the second source and drain electrodes 115 and 116 of the second pH-ISFET 118 have no membrane immobilized enzyme connected therewith. With this arrangement, if a sample solution contains a substrate reactable with the enzyme in the membrane 121, there will be a difference in pH between the membrane and the solution which is monitored by means of the second pH-ISFET 118. Accordingly, the enzyme sensor acts to measure the respective source voltages required to cause a predetermined level of current flow from the sources 113, 115 to the drains 114a, 116a of the first and second pH-ISFETs, and then amplify a differential output between the measured source voltages of the pH-ISFETs so as to measure the concentration of the substrate in the sample solution. In addition, as illustrated in Fig. 8, it is possible to form a membrane immobilized enzyme 121' on a specified portion of the surface of a pH-ISFET chip by means of photolithography. Fig. 9 shows a semiconductor multiple-enzyme sensor having a plurality (three in the illustrated embodiment) of pH-ISFETs 217, 218 and 224 each having a source electrode 213, 215 or 225 and a drain electrode 214, 216 or 226, and a reference or pseude electrode 222 fabricated in accordance with the present invention. Each of the pH-ISFETs 217, 218 and 224 has a pair of spaced opposite ion-sensitive portions 213a, 214a; 215a, 216a; or 225a, 226a integrally formed with the source and drain electrodes 213, 214; 215, 216; or 225, 226, respectively. The multiple-enzyme sensor has a plurality (two in the illustrated embodiment) ofmembraneimmobilized enzymes 221, 227 which are formed on the ion-sensitive portions 213a, 214a of the pH-ISFET 217, and on the ion-sensitive portions 225a, 226a of the pH-ISFET 227, respectively. Thesemembraneimmobilized enzymes 221 and 227 can be formed in the same manner as described with reference to the one shown in Figs. 4 and 5 or Figs. 6 and 7. The membranes 221 and 227 are different from each other and reactable with different kinds of substrates so that they can measure concentrations of such different substrate solutions. The multiple-enzyme sensor may further include one or more pH-ISFETs each having an enzyme reactable with a corresponding substrate solution. EXAMPLE 1 An aqueous solution of a water soluble photosensitive polymer was prepared by dissolving a 2, 5-bis (4'-azide-2'-sulfobenzal) cyclopentanone sodium salt (Tokyo Ohkakogyo Co., Ltd.) in a 10 weight percent polyvinyl pyrrolidone solution having a molecular weight of about three hundred and sixty thousand at a concentration of 10 weight percent. In 0.2 ml of the water soluble photosensitive polymer solution thus prepared, 2 mg glucose oxidase was dissolved as an enzyme to form a homogeneous solution which was then widely coated on a specific portion of the surface of the ph-ISFET chip 112, as illustrated in Fig. 6, so as to cover the ion-sensitive portions 113a and 114a of the source and drain electrodes 113 and 114 of the first ph-ISFET 117 as well as a channel portion defined therebetween. The layer of the solution thus coated was made into an even or uniform membrane by the use of a spinner (not shown), and then dried. The dried membrane was subsequently exposed to UV irradiation with a 250 W superhigh voltage mercury-arc lamp for 2 minutes to form a glucose-oxidase immobilized membrane 121. EXAMPLE 2 To 0.2 ml of a 10 weight percent photosensitive polymer solution, which was prepared in the same manner as described in the Example 1, 20 mg glucose oxidase and 10 mg bovine serum albumin, which is a material adapted to form chemical crosslinking with glutaraldehyde, were added to form a homogeneous solution which was then coated on the ion-sensitive portions 113a and 114a of the source and drain electrodes 113 and 114 of the first ph-ISFET 117 in Fig. 6. The layer of the solution thus coated was treated in the same manner as described in Example 1 to provide a glucose-oxidase immobilized membrane 121. Subsequently, the glucose-oxidase immobilized membrane 121 was immersed in a 25 % glutaraldehyde solution for 10 minutes whereby protein molecules in the bovine serum albumin were chemically crosslinked with each other through chemical bondings for increased mechanical strength. The membrane thus treated was then washed with a buffer solution, immersed in a 0.1 M glycine solution for 15 minutes for the purpose of removing the residual glutaraldehyde, and again washed with a buffer solution. In this manner, a glucose sensor having a glucose-oxidase immobilized membrane was obtained. The glucose sensor thus fabricated was measured in terms of response characteristic. The measurement was carried out at a glucose concentration in the range of 0 to 5.5 mM using a 0.01 M acetic acid buffer solution at pH 5.5. The response curve of the glucose sensor at a 1.67 mM glucose concentration is shown in Fig. 10 in which an arrow indicates a sample pouring point in time. From Fig. 10, it is clear that the response of the glucose sensor is fast. Fig. 11 shows a calibration curve of the glucose sensor from which it is seen that the sensor response is linear with respect to the glucose concentration in the range of 0 to 1.7 mM. In addition, the lifetime of the glucose sensor was 60 days, sufficiently long for practical use. EXAMPLE 3 To 0.2 ml of a 10 weight percent photosensitive polymer solution, which was prepared in the same manner as described in Example 1, 2 mg glucose oxidase was added to form a homogeneous solution which was then coated on the surface of the pH-ISFET chip 112'so as to cover the ion-sensitive portions 113a and 114a of the source and drain electrodes 113 and 114 of the first pH-ISFET 117 in Fig. 8. The layer of the solution thus coated was made into an even or uniform membrane by the use of a spinner (not shown), and then dried. Thereafter, by using a photomask through which light is irradiated from a light source to a specified portion of the surface of ph-ISFET chip 112, a glucose-oxidase immobilized enzyme membrane 121' was formed on only a part of the ion-sensitive portions. The light irradiation was carried out with the same device and conditions as those in Example 1. EXAMPLE 4 To 0.2 ml of a 10 weight percent photosensitive polymer solution, which was prepared in the same manner as described in the Example 1, 20 mg glucose oxidase and 10 mg bovine serum albumin were added to form a homogeneous solution which was then coated on the ion-sensitive portions 113a and 114a of the source and drain electrodes 113 and 114 of the first ph-ISFET 117 in Fig. 8. The layer of the solution thus coated was made into a uniform membrane by the use of a spinner (not shown), and then dried. Thereafter, the membrane was treated in the same manner as described in Example 3 to provide a glucose-oxidase immobilized membrane 121'. Subsequently, the glucose-oxidase immobilized membrane was immersed in a 25 % glutaraldehyde solution for 10 minutes whereby protein molecules in the bovine serum albumin were chemically crosslinked with each other through chemical bondings for increased mechanical strength. The glucose-oxidase immobilized membrane thus treated was then washed with a buffer solution, immersed in a 0.1 M glycine solution for 15 minutes for the purpose of removing the residual glutaraldehyde, and again washed with a buffer solution. EXAMPLE 5 In 500 µl of a 10 weight percent photosensitive polymer solution, which was prepared in the same manner as described in the Example 1, 25 mg glucose oxidase and 25 mg bovine serum albumin were dissolved to form a homogeneous enzyme solution. The enzyme solution thus prepared was poured dropwise on the surface of a silicon wafer which has a thermally grown silicon oxide film of about 5000 Å thickness. The enzyme solution was then spin coated by a spinner (not shown) at 2000 rpm for 2 minutes to provide an enzyme membrane A, as illustrated in Fig. 3. After drying at room temperature, the enzyme membrane A was irradiated by ultraviolet light, of which less than 300 nm wavelengths were cut, through a photomask 105 for 180 seconds to form chemical crosslinking so as to provide a membrane immobilized enzyme B (see Fig. 3B). Subsequently, themembraneimmobilized enzyme B thus obtained was developed by aqueous solutions containing glutaraldehyde of various concentrations, the aqueous solutions being adapted to form chemical bondings with glucose oxidase and bovine serum albumin. The pattern of the residual membrane immobilized enzyme C formed by the development was then observed and the results obtanined were as follows: (1) When developed with an aqueous solution containing a 0 % concentration of glutaraldehyde, the most portion of the membrane was peeled off and hence the membrane was poor. (2) When developed with a 1 % glutaraldehyde solution, the most portion of the membrane was not peeled off and the membrane was good. (3) When developed with a 2 % glutaraldehyde solution, the membrane was not peeled off and very good. (4) When developed with a 3 % glutaraldehyde solution, the membrane was not peeled off and very good. (5) When developed with a 4 % glutaraldehyde solution, the membrane was not peeled off and very good. (6) When developed with a 5 % glutaraldehyde solution, the most portion of the membrane was not peeled off and good. (7) When developed with a 10 % glutaraldehyde solution, only half of the membrane pattern remained with a white thin film being formed due to chemical crosslinking at locations from which a half of the membrane pattern was peeled off. (8) When developed with a 25 % glutaraldehyde solution, the most portion of the membrane pattern was peeled off with a white thin film remainig due to chemical crosslinking. From the above, it was found that with glutaraldehyde solutions at concentrations ranging from 1 % to 5%, there were obtained good enzyme immobilized membranes. EXAMPLE 6 An enzyme solution, prepared in the same manner as described in Example 5, was spin coated on the surface of a silicon wafer which has a thermally grown silicon oxide film of about 5000 Å thickness with amino groups being introduced on the surface thereof by using γ-aminopropyltriethoxysilane. The coating of the enzyme solution was effected by the use of a spinner (not shown) at 2000 rpm for 2 minutes to provide an enzyme membrane. The enzyme membrane was irradiated by ultraviolet light emitted from a 250 W superhigh voltage mercury-arc lamp, and then immersed in a 25 % glutaraldehyde solution for 5 minutes. Thereafter, the unreacted aldehyde groups in the enzyme membrane were reacted with a 0.1 M glycine solution for 15 minutes to provide a glucose-oxidase immobilized membrane. The membrane thus obtanied had an average thickness of 2 µm and thus was of a very thin film though there were many irregularities formed on the surface thereof. EXAMPLE 7 An enzyme solution, prepared in the same manner as described in Example 5, was spin coated on the surface of a silicon wafer which has a thermally grown silicon oxide film of about 5000 Å thickness with amino groups being introduced on the surface thereof by using γ-aminopropyltriethoxysilane. The coating of the enzyme solution was effected by a spinner (not shown) at 2000 rpm for 2 minutes to provide an enzyme membrane. Thereafter, by the use of a 250 W superhigh voltage mercury-arc lamp, ultraviolet light was irradiated through an appropriate photomask on a specified portion of the surface of a pH-ISFET chip so that only a portion of the enzyme membrane on the pH-ISFET chip surface was phote-set (see Fig. 3A). Subsequently, by dissolving and removing the unset portion of the enzyme membrane with distilled water, a glucose-oxidase immobilized enzyme membrane of a limited area was obtained (see Fig. 3B). The glucose-oxidase immobilized membrane was then treated with a 25 % glutaraldehyde solution for 5 minutes so as to form chemical crossinking for increased mechanical strenth (see Fig. 3C). The membrane thus formed was immersed in a 0.1 M glycine solution for 15 minutes for reaction of the unreacted aldehyde groups in the glutaraldehyde. EXAMPLE 8 An enzyme solution, prepared in the same manner as described in Example 5, was coated on the surface of a silicon wafer which has a thermally grown silicon oxide film of about 5000 Å thickness with amino groups being introduced on the surface thereof by using -aminopropyltriethoxysilane, as in Example 6. The enzyme solution was then spin coated by a spinner (not shown) at 2000 rpm for 2 minutes to provide an enzyme membrane A in Fig. 3A. Subsequently, only a specified portion of the enzyme membrane A was irradiated by ultraviolet light emitted from a 250 W superhigh voltage mercury-arc lamp through an appropriate photomask so as to be phote-set (Fig. 3A). The silicon wafer with the photo-set enzyme membrane was then immersed in a 2 % glutaraldehyde solution whereby the unset portion B of the membrane was dissolved for removal, as shown Fig. 3B, and at the same time, chemical crosslinking was formed in the phote-set portion of the membrane to provide a glucose-oxidase immobilized membrane C of a limited area (Fig. 3C). The unreacted aldehyde groups in the glutaraldehyde solution were immersed in a 0.1 M glycine solution for 15 minutes for reaction therewith. It was possible to reduce the size of the glucose-oxidase immobilized enzyme membrane thus obtained such that it had a line and space pattern with a pitch or interval of 100 µm between adjacent lines or spaces, though the width of the membrane became slightly thick. EXAMPLE 9 A silicon wafer was processed in the same manner as in Example 8, and after being developed with a 2 % glutaraldehyde solution, it was immersed in a 25 % glutaraldehyde solution for 5 minutes so that further chemical crosslinking was produced in an enzyme membrane once chemically crosslinked for further increase in mechanical strength to provide a glucose-oxidase immobilized membrane. Here, it is to be noted that though in Examples 6 through 9 above, pH-ISFETs each in the form of a silicon wafer having amino groups introduced into the surface thereof were used, the present invention can be likewise applicable to a transducer. EXAMPLE 10 A first membrane immobilized enzyme was formed on a hydrogen ion-sensitive portion of a pH-ISFET in the same manner as in Example 5 so as to provide a test piece of a semiconductor enzyme sensor of the invention. On the other hand, using an enzyme solution prepared in the same manner as in Example 5 excepting that there was no addition of bovine serum albumin, a comparative semiconductor enzyme sensor was produced which had a second membrane immobilized enzyme formed on a hydrogen ion-sensitive portion of another pH-ISFET in the same manner as in Example 5. The operations of the above two sensors were examined in the following manner. In case of the comparative sensor in which photo crosslinking was formed by the use of a water soluble photosensitive polymer containing the enzyme alone but no bovine serum albumin, the membrane produced was peeled off in an aqueous solution and hence there was no membrane immobilized enzyme formed. Presumably, this was caused due to a too much amount of enzyme contained. In contrast to this, in the test piece of the sensor produced by using bovine serum albumin, there was no peeling off of the membrane even in an aqueous solution, and thus a membrane immobilized enzyme having sufficient mechanical strength was obtained. The response of this sensor to a 300 mg/l in a 10 mM acetic acid buffer solution was approximately 6 mV at pH 5.5 and 34 o C, and the sensor had high sensitivity. Although in this Example, the semiconductor enzyme sensor having a pH-ISFET is described, the present invention is likewise applicable to a semiconductor oxygen sensor, a semiconductor hydrogen peroxide sensor, or the like with the same effects. EXAMPLE 11 A multiple-enzyme sensor was produced in which an enzyme in the form of glucose oxidase and another enzyme in the form of lipase were used for detecting glucose and neutral lipide, respectively. 2 mg lipase was dissolved in a 0.2 ml of a water soluble photosensitive solution as prepared in the same manner as in Example 1. The solution thus formed was coated on a pH-ISFET chip by means of a spinner (not shown) and dried to provide a membrane which was then irradiated by light emitted from an exposure device through an appropriate photomask for 1 minute so as to phote-set only a portion of the membrane. Subsequently, the remaining portion of the membrane (or mixture of the enzyme and the water soluble photosensitive resin) other than the photo-set portion was dissolved in a buffer solution for removal. On the other hand, glucose oxidase was subjected to the same processes as described above with respect to lipase so as to provide a glucose-oxidase immobilized membrane which was secured to a portion of the pH-ISFET chip. EXAMPLE 12 15 mg lipase and 10 mg bovine serum albumin were dissolved in a 0.2 ml water soluble photosensitive resin solution as prepared in the same manner as in Example 1. The solution thus formed was coated on the surface of a pH-ISFET by means of a spinner and dried to provide a membrane. Only a portion of the membrane was exposed to irradiation of ultraviolet light for 2 minutes so as to be photo-set to provide a lipase immobilized membrane. The remaining portion of the membrane other than the photo-set portion was dissolved and removed by an aqueous solution. On the other hand, a water soluble photosensitive resin solution containing glucose oxidase, similar in composition to that in Example 2, was subjected to the same processes as in the above-described water soluble photosensitive resin solution so as to form a glucose-oxidase immobilized membrane on a specific portion of the surface of the pH-ISFET chip. Subsequently, both of the membrane immobilized enzymes thus obtained were immersed in a 25 % glutaraldehyde solution for 10 minutes so that the proteins in the membrane immobilized enzyme were crosslinked with each other through chemical bondings. After being washed with a buffer solution, themembraneimmobilized enzymes were further immersed in a 0.1 M glycine for removal of the residual glutaraldehyde, and then washed again with a buffer solution. In this manner, a multiple-enzyme sensor was produced. The multiple-enzyme sensor thus produced was examined in terms of response characteristic. Fig. 12 illustrates an example of the output power of the sensor in which a sample pouring point in time is designated by an arrow. The output power of the sensor examined was measured by using a 2 mM tris-maleic acid buffer solution (pH 7) containing 1.67 mM glucose and 3 mM triolein. In Fig. 12, curve A represents a differential output between the pH-ISFET having a lipase immobilized membrane and the pH-ISFET without anymembraneimmobilized enzyme. Triolein was hydrolyzed into oleic acid according to the following reaction (2) to provide the output curve A. Triolein + 3H₂O - glycerol + 3C₁₇H₃₃COOH (2) On the other hand, curve B in Fig. 12 represents a differential output between the pH-ISFET having a glucose-oxidase immoblized membrane and the pH-ISFET without any membrane immobilized enzyme. Glucose was changed to gluconic acid, as shown in the above reaction (1), so that pH of the enzyme immobilized membrane was accordingly reduced to provide the output curve B. The measurement by the multiple sensor was possible in a glucose concentration ranging from 0 to 3 mM and at an triolein concentration ranging from 0 to 4 mM. Although in this example, a pseude reference electrode in the form of a thin membrane of a novel metal was used to provide gate voltage, a stable reference electrode such as a silver-silver chloride electrode may be employed. Also, glucose oxidase and lipase were used for enzymes, but instead by the use of other kinds of enzymes, it is possible to produce a semiconductor sensor or a multiple-enzyme sensor, which is sensitive to various substrates. Although in the above-described examples, the mixture of PVP and bis-azide compound is used for a water soluble photosensitive resin, there may be employed with the same effects other types of water soluble photosensitive resins such as photosensitive polyvinyl alcohols each having, as a pendant, a stilbazolium group. Further, enzymes are not limited to glucose oxidase or lipase but other kinds of enzymes such as urease can be used. Moreover, in place of a combination of bovine serum albumin and an enzyme with glutaraldehyde, there may be employed any combination of general reagents which are usable with water soluble immobilized enzymes which are able to easily form chemical crosslinking therewith. For example, poly-L-lysine or copolymers of polyamino acid and poly-L-lysine can be used in place of bovine serum albumin, and a polyfuctional reagent having a plurality of aldehyde groups can be used in place of glutaraldehyde.

Claims: A membrane-immobilized enzyme comprising: a water soluble photosensitive resin including polyvinyl pyrrolidone having an average molecular weight of tens of thousands to hundreds of thousands and an aromatic group- containing azido compound; and an enzyme; characterised in that the aromatic group-containing azido compound is 2,5-bis(4'-azide-2'-sulfobenzal) cyclopentanone sodium salt. A membrane-immobilized enzyme as claimed in claim 1, characterized in that the said enzyme is selected from glucose oxidase, ureaze and lipase. A membrane-immobilized enzyme as claimed in claim 1 or 2, characterized by further comprising: glutaraldehyde; and a material adapted to cooperate with glutaraldehyde to form chemical crosslinking. A membrane-immobilized enzyme as claimed in claim 3, characterized in that the said material adapted to cooperate with glutaraldehyde to form chemical crosslinking is selected from bovine serum albumin. polyamino acid, and polyamino acid copolymer. A membrane-immobilized enzyme as claimed in claim 4, characterized in that the said polyamino acid is poly-L-lysine. A membrane-immobilized enzyme as claimed in claim 4, characterized in that the said polyamino acid copolymer is a copolymer of poly-L-lysine and poly-L-thyrosin. A membrane-immobilized enzyme as claimed in any of claims 1 to 6, characterized in that the said polyvinyl pyrrolidone having an average molecular weight of tens of thousands to hundreds of thousands comprises 2-20 weight %; and said 2,5-bis(4'-azide-2'-sulfobenzal) cyclopentanone sodium salt comprises 0.5 - 1.5 weight %; and said enzyme comprises glucose oxidase of 5.0 - 7.5 weight %; said membrane-immobilized enzyme further comprising bovine serum albumin of 5 - 10 weight %. A method for producing an membrane-immobilized enzyme characterized by comprising the steps of: coating on a base an aqueous solution which is composed of a water soluble photosensitive resin including polyvinyl pyrrolidone having an average molecular weight of tens of thousands to hundreds of thousands and 2,5-bis(4'-azide-2'-sulfobenzal)cyclopentanone sodium salt, and an enzyme; drying the aqueous solution thus coated on the said base so as to form a membrane-immobilized enzyme and irradiating ultraviolet light on the said membrane-immobilized enzyme to provide photo-crosslinking between the polyvinyl pyrrolidone, the cyclopentanone sodium salt, and the enzyme. A method as claimed in claim 8, characterized in that the said enzyme is selected from glucose oxidase, ureaze and lipase. A method as claimed in claim 8 or 9, characterized in that the said aqueous solution further comprises: glutaraldehyde; and a material adapted to cooperate with glutaraldehyde to form chemical crosslinking. A method as claimed in claim 10, characterized in that the said material adapted to cooperate with glutaraldehyde to form chemical crosslinking is selected from bovine serum albumin, polyamino acid, and polyamino acid copolymer. A method as claimed in claim 11, characterized in that the said polyamino acid is poly-L-lysine. A method as claimed in claim 11, characterized in that the said polyamino acid copolymer is a copolymer of poly-L-lysine and poly-L-thyrosin. A method as claimed in any of claims 8 to 13, characterized in that said polyvinyl pyrrolidone having an average molecular weight of tens of thousands to hundreds of thousands comprises 2 - 20 weight %; and said 2,5-bis(4'-azide-2'-sulfobenzal)cyclopentanone sodium salt comprises 0.5 - 1.5 weight%; and said enzyme comprises glucose oxidase of 5.0 - 7.5 weight %; said aqueous solution further comprising bovine serum albumin of 5 - 10 weight %. A method as claimed in any of claims 8 to 14, characterized by further comprising dipping said enzyme immobilized membrane irradiated by said ultraviolet light into an aqueous solution of glutaraldehyde so as to form chemical crosslinking. A method as claimed in claim 15, characterized by further comprising washing away the glucose-oxidase immobilized membrane by a buffer solution. A method as claimed in claim 16, characterized by further comprising: dipping said glucose-oxidase immobilized membrane once washed away by said buffer solution into an aqueous solution of glycine; and washing away said glucose-oxidase immobilised membrane by a buffer solution for removal of the residual glutaraldehyde. A semiconductor enzyme sensor, comprising: a first hydrogen ion-sensitive field effect transistor having a first membrane-immobilized enzyme connected thereto; a second hydrogen ion-sensitive field effect transistor; and a reference electrode charactereised in that the said first membrane is composed of a first water soluble photosensitive resin including polyvinyl pyrrolidone having an average molecular weight of tens of thousands to hundreds of thousands and 2,5-bis(4'-azide-2'-sulfobenzal)cyclopentanone sodium salt, and a first enzyme. a second hydrogen ion-sensitive field effect transistor ; and a reference electrode. A semiconductor enzyme sensor as claimed in claim 18, characterized by further comprising a third hydrogen ion-sensitive field effect transistor having a second membrane-immobilized enzyme connected thereto, the said second membrane being composed of a second water soluble photosensitive resin including polyvinyl pyrrolidone having an average molecular weight of tens of thousands to hundreds of thousands and 2,5-bis(4'-azide-2'-sulfobenzal)cyclopentanone sodium salt, and a second enzyme. A semiconductor enzyme sensor as claimed in claim 19, characterized in that the said second enzyme is selected from glucose oxidase, urease and lipase. A semiconductor enzyme sensor as claimed in any of claims 18 to 20, characterized in that the said first enzyme is selected from glucose oxidase, ureaze and lipase. A semiconductor enzyme sensor as claimed in any of claims 18 to 21, characterized by further comprising: glutaraldehyde; and a material adapted to cooperate with glutaraldehyde to form chemical crosslinking. A semiconductor enzyme sensor as claimed in claim 22, characterized in that the said material adapted to co-operate with glutaraldehyde to form chemical crosslinking is selected from bovine serum albumin, polyamino acid, and polyamino acid copolymer. A semiconductor enzyme sensor as claimed in claim 23, characterized in that the said polyamino acid is poly-L-lysine. A semiconductor enzyme sensor as claimed in claim 23, characterized in that the said polyamino acid copolymer is a copolymer of poly-L-lysine and poly-L-thyrosin. A semiconductor enzyme sensor as claimed in any of claims 18 to 25, characterized in that the said polyvinyl pyrrolidone having an average molecular weight of tens of thousands to hundreds of thousands comprises 2 - 20 weight %; and said 2,5-bis(4'-azide-2'-sulfobenzal) cyclopentanone sodium salt comprises 0.5 - 1.5 weight and said enzyme comprises glucose oxidase of 5.0 - 7.5 weight %; said membrane-immobilized enzyme further comprising bovine serum albumin of 5 - 10 weight %. A semiconductor enzyme sensor as claimed in any of claims 18 to 26, characterized in that the said first membrane-immobilized enzyme is directly coated and hardened on said hydrogen ion-sensitive field effect transistor. A semiconductor enzyme sensor as claimed in claim 19, or as claimed in any of claims 20 to 27 when appendant to claim 19, characterized in that the said second membrane-immobilized enzyme is directly coated and hardened on said hydrogen ion-sensitive field effect transistor. A semiconductor enzyme sensor as claimed in any of claims 18 to 28, characterized in that the said first membrane-immobilized enzyme is formed by coating on a hydrogen ion-sensitive field effect transistor a first aqueous solution containing said first water soluble photosensitive resin, glucose oxidase, bovine serum albumin, and hardening said first aqueous solution thus coated by irradiation of ultraviolet light, said first membrane-immobilized enzyme being dipped into a glutaraldehyde solution to form chemical crosslinking for improved mechanical strength. A semiconductor enzyme sensor as claimed in claim 19, or as claimed in any of claims 20 to 29 when appendant to claim 19, characterized in that the said second membrane-immobilized enzyme is formed by coating on a hydrogen ion-sensitive field effect transistor a second aqueous solution containing said second water soluble photosensitive resin, glucose oxidase, bovine serum albumin, and hardening said second aqueous solution thus coated by irradiation of ultraviolet light, said second membrane-immobilized enzyme being dipped into a glutaraldehyde solution to form chemical crosslinking for improved mechanical strength. A semiconductor enzyme sensor as claimed in any of claims 18 to 30, characterized in that the said first hydrogen ion-sensitive field effect transistor has an ion-sensitive surface, and said first membrane-immobilized enzyme is formed through patterning on the ion-sensitive surface of said first hydrogen ion-sensitive field effect transistor by means of photolithography. A semiconductor enzyme sensor as claimed in claim 19, or as claimed in any of claims 20 to 31 when appendant to claim 19, characterized in that the said third hydrogen ion-sensitive field effect transistor has an ion-sensitive surface, and said second membrane-immobilized enzyme - is formed through patterning on the ion-sensitive surface of said third hydrogen ion-sensitive field effect transistor by means of photolithography. A semiconductor enzyme sensor as claimed in any of claims 18 to 32, characterized by further comprising further one or more hydrogen ion-sensitive field effect transistors each having a further membrane-immobilized enzyme connected thereto, said further membrane being composed of a further water soluble photosensitive resin including polyvinyl pyrrolidone having an average molecular weight of tens of thousands to hundreds of thousands and 2,5-bis(4'-azide-2'-sulfobenzal)cyclopentanone sodium salt, and a further enzyme.

Inventors: HANAZATO, YOSHIO CHUO KENKYUSHO OF MITSUBISHI, NAKAKO MAMIKO@C/O CHUO KENKYUSHO@MITSUBISHI, SHIONO, SATORU C/O CHUO KENKYUSHO MISUBISHI, YAMADA, SATOSHI C/O CHUO KENKYUSHO MISUBISHI, Nakako Mamikoµc/o Chuo KenkyushoµMitsubishi
Applicants: SEITAIKINOURIYOU KAGAKUHIN SINSEIZOGIJUTSU KENKYU KUMIAI
Application year: 1986
Main classification: C12N11
IPC codes: C12N11, C12Q1