MODIFIED CO-POLYESTER-CARBONATE RESINS

Abstract: A thermoplastic polyester-carbonate resin containing in the polymer chain, divalent moieties of the formula:- wherein R represents aliphatic hydrocarbyl of from 1 to 9 carbon atoms, inclusive, halogen substituted aliphatic hydrocarbyl of 1 to 9 carbon atoms, inclusive, aralkyl of 7 to 10 carbon atoms, inclusive and halogen sub­ stituted aralkyl of 7 to 10 carbon atoms, inclusive; a and b are each whole number integers of from 0 to 1; and the sum of a + b is 1 and wherein there are suffi­ cient linkages of formula I to lower the glass transi­ tion temperature of the polymer.

Description: The invention relates to polycarbonate and copoly ester-carbonate resins and more particularly to such resins modified to provide particular physical properties useful for thermoplastic processing. A wide variety of polycarbonate and copolyester-carbonate resins are known and usefully employed as thermoplastics for a wide variety of molded articles and components of useful articles. In spite of the wide diversity of physical properties associated with the prior art resins, there has remained a need for even more diverse physical properties. The resins of the present invention are noteworthy in that they have lowered glass-transition temperatures while retaining to a significant extent the desirable attributes of thermoplastic molding resins. The invention comprises a copolyester-carbonate resin, containing in the polymer chain recurring divalent moieties of the formula:- wherein R is selected from the group consisting of aliphatic hydrocarbyl of 1 to 9, preferably 1 to 6, carbon atoms, inclusive, halogen substituted aliphatic hydrocarbyl of 1 to 9 carbon atom, inclusive, aralkyl of 7 to 10 carbon atoms, inclusive and halogen substituted aralkyl of 7 to 10 carbon atoms, inclusive; a and b are each 0 or 1 and a + b is 1. The copolyester-carbonates of the invention are useful as thermoplastic molding compositions. The moldable resins and resin compositions are useful to mold a wide variety of useful articles such as component parts of automobiles, tool housings and like articles. The term "hydrocarbyl" as used herein means the monovalent moiety obtained upon removal of a hydrogen atom from a parent hydrocarbon. Representative of aliphatic hydrocarbyl are alkyl of 1 to 9 carbon atoms, inclusive, i.e. methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl, octyl, nonyl and isomers thereof; cycloalkyl of 3 to 8 carbon atoms, inclusive, i.e. cyclopropyl, cyclobutyl, cyclopentyl, cyclohexyl, cycloheptyl, cyclooctyl; alkyl substituted cycloalkyl of 4 to 12 carbon atoms, inclusive, such as 2-methylcyclopropyl, 3,4-dimethylcyclohexyl; alkenyl of 3 to 9 carbon atoms, inclusive, such as allyl, 3-hexenyl, 2,4-pentadienyl; and aralkyl of 7 to 10 carbon atoms, inclusive, such as benzyl, phenethyl, phenpropyl and phenbutyl . Preferred hydrocarbyl groups do not have a hydrogen atom on the carbon β to the oxa atom, for example benzyl and neopentyl. The term "halogen substituted hydrocarbyl" as used herein means hydrocarbyl as defined above wherein one or more hydrogen atoms have been replaced with a halogen atom. The term "halogen" as used herein is embracive of chlorine, bromine, iodine and fluorine. The copolyester-carbonate resins of the invention may be prepared by the reaction of a carbonate precusor, a dihydric phenol, and a dicarboxylic acid or mixture of dicarboxylic acids selected from those of the formula:- and wherein R, is as defined above. The compounds of the formula (IIA) are isomers of the compounds of formula (IIB) and they will be referred to hereinafter collectively as compounds of the formula (II). The reaction is carried out under conditions to produce a copolyester-carbonate resin. Such reaction conditions are well known to those skilled in the art of polycarbonate polymer resins and are described, for example, in the U.S. Patents 3,028,365; 3,334,154; 3,275,601; 3,915,926; 3,030,31; 3,169,121; 3,027,814; and 4,188,314. In general, the preparation may be carried out by interfacial polymerization or phase boundary separation, transesterification, solution polymerization, melt polymerization or interesterification. Interfacial polymerization is preferred. Although the preparative processes may vary, several of the preferred processes typically involve dissolving or dispersing the reactants in a suitable water immiscible solvent medium and contacting the reactants with a carbonate precursor, such as phosgene, in the presence of a suitable catalyst and an aqueous caustic solution under controlled pH conditions. The most commonly used water immiscible solvents include methylene chloride, 1,2-dichloroethane, chlorobenzene and toluene. A molecular weight regulator, that is a chain stopper, is generally added to the reactants prior to or during the contacting of them with a carbonate precursor. Useful molecular weight regulators include, but are not limited to, monohydric phenols such as phenol, chroman-I or paratertiarybutylphenyl. Techniques for the control of molecular weight are well known in the art and may be used for controlling the molecular weight of the copolyester-carbonate resins of the invention. The catalysts employed, if an interfacial polymerization technique is used, accelerate the rate of polymerization of the dihydric phenol reactant with the ester precursor such as the dicarboxylic acid and with the carbonate precursor such as phosgene. Suitable catalysts include but are not limited to tertiary amines such as triethylamine, quaternary phosphonium compounds or quaternary ammonium compounds. The preferred process for preparing resins of the invention comprises a phosgenation reaction. The temperature at which the phosgenation reaction proceeds may vary from below 0°C, to above 100°C. The phosgenation reaction preferably proceeds at temperatures of from room temperatures (25°C) to 50°C. Since the reaction is exothermic, the rate of phosgene addition may be used to control the reaction temperature. The amount of the phosgene required will generally depend upon the amount of the dihydric phenol and the amount of dicarboxylic acid present. Dihydric phenol reactants employed to prepare the copolyester-polycarbonate resins of the invention are generally well known compounds as are methods of their preparation. Representative of such dihydric phenols are phenolic diols of the general formula:- wherein A is selected from the group consisting of a divalent hydrocarbon containing from 1 to 15 carbon atoms; a halogen substituted divalent hydrocarbon radical containing from 1 to 15 carbon atoms and divalent groups such as: Each X in formula (III) is independently selected from the group consisting of halogen, a monovalent hydrocarbon radical such as an alkyl group of from 1 to 8 carbon atoms; an aryl group of from 6-18 carbon atoms, an aralkyl group of from 7 to 14 carbon atoms, an oxyalkyl group of from 1 to 8 carbon atoms, and an oxyaryl group of from 6 to 18 carbon atoms; and wherein m is zero or 1 and y is a whole number integer of from 0 to 4, inclusive. Typical of some of the dihydric phenols that are advantageously employed are bis-phenols such as bis (4-hydroxy-phenyl)methane, 2,2-bis(4-hdyroxyphenyl)propane (also known as bisphenol A), 2,2-bis(4-hydroxy-3-methyl-phenyl)propane, 4,4-bis(4-hydroxyphenyl)heptane, 2,2-bis(4-hydroxy-3,5-dichlorophenyl)propane, 2,2-bis(4-hydroxy-3,5-dibromophenol)propane; dihydric phenyl ethers such as bis(4-hydroxyphenyl)ether, bis(3,5-dichloro-4-hydroxyphenyl)ether; dihydroxydiphenols such as p,p′-dihydroxydiphenol, 3,3-dichloro-4,4′-dihydroxy-diphenyl; dihydroxyaryl sulfones such as bis(4-hydroxyphenyl) sulfone, bis(3,5-dimethyl-4-hydroxyphenyl)sulfone; dihydroxy benzenes, resorcinol, hydroquinone, halo- and alkyl-substituted dihydroxy benzenes such as 1,4-dihydroxy-2,5-dichlorobenzene, 1,4-dihydroxy-3-methylbenzene; and dihydroxy diphenyl sulfides and sulfoxides such as bis(4-hydroxyphenyl)sulfide and bis(4-hydroxyphenyl)sulfoxide. A variety of additional dihydric phenols are also available and are disclosed in U.S. Pat. Nos. 2,999,835; 3,028,365 and 3,153,008. It is of course, possible to employ two or more different dihydric phenols or a combination of a dihydric phenol with glycol. Preferred dihydric phenols of Formula (III) are the 4,4′-bisphenols. The carbonate precursor employed in the preparation of resins of the present invention may be a carbonyl halide, a diarylcarbonate, or a bishaloformate. The carbonyl halides include carbonyl bromide, carbonyl chloride, and mixtures thereof. The bishaloformates include the bishaloformates of dihydric phenols such as bischloroformates of 2,3-bis(4-hydroxyphenyl)propane or hydroquinone; or the bischloroformates of glycols such as the bischloroformates of ethylene glycol, neopentylene, glycol or polyethylene glycol. Typical of the diarylcarbonates which may be employed are diphenyl carbonate, and the di(alkylphenyl-carbonates such as di(tolyl) carbonate. Some other non-limiting illustrative examples of suitable diarylcarbonates include di(napthyl) carbonate and phenyl tolyl carbonate. The preferred carbonate precursors are the carbonyl halides, with carbonyl chloride, also known as phosgene, being the preferred carbonyl halide. Dicarboxylic acids of the formula (II) given above may be prepared by the reaction of trimellitic anhydride (IV) with an aliphatic alcohol (V) according to the schematic formulae:- wherein R has the meaning previously ascribed to it. The above-illustrated reaction for preparation of the isomers of formula (IIA) and (IIB) may be carried out by mixing stoichiometric proportions of the reactants (IV) and (V) and heating the mixture, preferably to a temperature of 100°C to 200°C either neat or in the presence of an inert organic solvent. The term "inert organic solvent" as used herein means an organic solvent for the product which does not enter reaction with the reactants (IV) or (V) or adversely affect the desired course of the reaction. Representative of inert organic solvents are methyl ethyl ketone and methyl isobutyl ketone . The general procedure for the preparation of the Compounds (II) may be found, for example, in U.S. Patent 3,578,638. Aliphatic alcohols of the formula (V) given above are well known compounds as are methods of their preparation. Representative of aliphatic alcohols of the formula (V) are methanol, ethanol, n-propanol, n-butanol, neopentanol, hexanol, 2-ethylhexanol, isooctanol, nonanol, allyl alcohol, cyclopropanol, cyclobutanol, cyclohexanol, cyclooctanol, benzyl alcohol, 2-phenylethanol, 4-tert-butyl-cyclohexanol and trifluoroethanol. In addition to the dicarboxylic acids of formula (II) given above, the polyester-carbonate resins of the invention may optionally contain reaction residues of other difunctional carboxylic acids, conventionally used in the preparation of copolyester-polycarbonate resins. In general, any difunctional carboxylic acid conventionally used in the preparation of linear polyesters may optionally be utilized in the preparation of the copolyester-carbonate resins of the instant invention in addition to the dicarboxylic acids of the formula (II) given above. Generally, the difunctional carboxylic acids which may be optionally utilized include the aliphatic carboxylic acids, the aromatic carboxylic acids, and the aliphatic-aromatic carboxylic acids. These acids are well known and are disclosed for example in U.S. Pat. No. 3,169,121. Representatives of such difunctional carboxylic acids are difunctional carboxylic acids of the formula:- wherein R² is an alkylene, alkylidene, or cycloaliphatic group; an alkylene, alkylidene or cycloaliphatic group containing ethylenic unsaturation; an aromatic group such as phenylene or biphenylene ; two or more aromatic groups connected through non-aromatic linkages such as alkylene or alkylidene groups; and a divalent aralkyl radical such as tolylene or xylylene. R¹ is either a carboxyl or a hydroxyl group. The letter q represents one where R¹ is a hydroxyl group and either zero or one where R¹ is a carboxyl group. Preferred difunctional carboxylic acids optionally employed are the aromatic dicarboxylic acids. Particularly useful aromatic dicarboxylic acids are those represented by the general formula:- wherein j is a positive whole integer having a value of from 0 to 4 inclusive; and each R³ is independently selected from the group consisting of alkyl radicals, preferably lower alkyl radicals containing from 1 to 5 carbon atoms. Mixtures of these optional difunctional carboxylic acids may be employed as well as single acids. Therefore, where the term difunctional carboxylic acid is used herein it is to be understood that this term includes mixtures of two or more different difunctional carboxylic acids as well as individual carboxylic acids. Most preferred optional aromatic dicarboxylic acids are isophthalic acid, terephtalic acid, and mixtures thereof. A particularly useful difunctional carboxylic acid comprises a mixture of isophthalic acid and terephthalic acid wherein the weight ratio of terephthalic acid to isophthalic acid is in the range of from 1:10 to 0.2:9.8. Rather than utilizing the optional difunctional carboxylic acid per se, it is possible, and sometimes even preferred, to employ the reactive derivatives of said acid. Illustrative of these reactive derivatives are the acid halides. The preferred acid halides are the acid dichlorides and the acid dibromides. Thus, for example, instead of using isophthalic acid, terephthalic acid, or mixtures thereof, it is possible to employ isophthaloyl dichloride, terephthaloyl dichloride, and mixtures thereof. Also included within the scope of the instant invention are randomly branched copolyester-carbonate resins wherein a minor amount (typically between 0.05 and 2 mole percent, based on the quantity of dihydric phenol used) of a polyfunctional aromatic compound is a co-reactant with the dihydric phenol in the reaction mixture, comprising also the carbonate precursor and the ester precursor, to provide a thermoplastic randomly branched copolyester-carbonate. These polyfunctional aromatic compounds may be hydroxyl, carboxyl, carboxylic anhydride, haloformyl, or mixtures thereof. Some illustrative non-limiting examples of these polyfunctional compounds include trimellitic anhydride, trimellitic acid, trimellityl trichloride, 4-chloroformyl phthalic anhydride, pyromellitic acid, pyromellitic dianhydride, mellitic acid, mellitic anhydride, trimesic acid, benzophenonetetracarboxylic acid and benzophenonetetracarboxylic acid anhydride. Other organic polyfunctional compounds useful in making these randomly branched copolyester-carbonates are disclosed in U.S. Pat. Nos. 3,635,895 and 4,001,184. The proportions of reactants employed to prepare the copolyester-carbonate resins of the invention will vary in accordance with the proposed use of the product resin. Sufficient dicarboxylic acid(s) of Formula II should be present to lower the glass transition temperature (Tg) in comparison to the corresponding polycarbonate. Thus, if only dicarboxylic acid(s) of Formula II are employed, a mole percent ester linkage of at least 2%, preferably 5%, should be employed. When 5 moles of bisphenol A reacts with 4.75 moles of phosgene and 0.25 moles of dicarboxylic acid of Formula II a copolyestercarbonate with 5% of ester bonds is formed. As will be appreciated from the above description, the copolyester-carbonate resins of the invention containing divalent moieties of the formula (I) given above will comprise recurring carbonate moieties of the formula:- and carboxylate groups of the formula:- When the optional difunctional carboxylic acids such as those of the formula (VI) given above are not employed in the preparation of the resins of the invention, preferred polymer resins of the invention will contain recurring chain units of the formula:- wherein A, X, R, m, y, a and b are as defined above; z and w are integers such that w/z is generally from 50/1 to 1/9. When the optional difunctional carboxylic acids such as those of the formula (VI) given above are employed in this invention, the resins of the invention will also preferably contain in the polymer chain, ester moieties, such as those of the formula:- wherein R², A, X, m and y are as previously defined. These copolyester-carbonate polymers contain, as stated above, ester and carbonate bonds in the polymer chain. The amount of the ester bonds may be from 5 to 90 mole percent, preferably from 35 to 80 mole percent, relative to the carbonate bonds. For example, 5 moles of bisphenol-A reacting completely with 4 moles of isophthaloyl dichloride and 1 mole of phosgene would give a copolyester-carbonate of 80 mole percent ester bonds as shown in the formula XIII shown above. The resins of the invention may be employed as the base for thermoplastic molding compositions, compounded with conventional molding aids such as, for example, antioxidants; antistatic agents; inert fillers such as glass, talc, mica, and clay; ultraviolet radiation absorbers such as the benzophenones or benzotriazoles; hydrolytic stabilizers such as the epoxides disclosed in U.S. Pat. Nos. 3,489,716, 4,138,379 and 3,839,247; color stabilizers such as the organophosphites; thermal stabilizers such as phosphite; flame retardants; and mold release agents. Some particularly useful flame retardants are the alkali and alkaline earth metal salts of sulfonic acids. These types of flame retardants are disclosed in U.S. Pat. Nos. 3,933,734; 3,931,100; 3,978,024; 3,948,851; 3,926,980; 3,919,167; 3,909,490; 3,953,396; 3,953,300; 3,917,559; 3,951,910 and 3,940,366. Sufficiently activated R groups, for example, halogenated alkyl, preferably trifluoroethyl, will undergo ester exchange reaction with ester or carbonate linkages present in a second polymer chain. A crosslinked product will be formed. A catalytic proportion of a transesterification catalyst should be present. A catalytic proportion is generally one within the range of from 0.01 to 0.00001 parts by weight of the composition. Transesterification catalysts useful as ingredients of the thermosetting compositions of the invention are basic catalysts conventionally employed in transesterification reactions. Representative of such catalysts are oxides, hydrides, hydroxides or amides of alkali or alkaline earth metals such as, for example, lithium hydroxide . Also, basic metal oxides such as zinc oxide. Also representative of transesterification catalysts are salts of weak acids such as lithium stearate; organotitanium catalysts such as tetraoctyltitanate; organotin catalysts such as dibutyltin oxide; aluminum of boron anion containing catalysts such as those described in U.S. Patents 4,330,669 and 4,395,062 . In general, the temperature required to achieve crosslinking is one within the range of from 200 to 300°C for a period of from 5 to 30 minutes. The following examples and preparations describe the manner and process of making and using the invention and set forth the best mode contemplated by the inventor of carrying out the invention but are not to be construed as limiting the invention. Where reported, the following tests were carried out. Glass Transition Temperature The glass transition temperatures were determined by using a Perkin-Elmer DSC-2B instrument which measures the glass transition temperature or Tg by differential scanning calorimetry. Intrinsic Viscosity The intrinsic viscosity was measured at a temperature of 25°C in methylene chloride and is reported in deciliters/gram (dl/g). Preparation 1 To a suitable reaction vessel there is charged equimolar proportions of trimellitic anhydride and benzyl alcohol in methyl isobutyl ketone. The charge is heated to reflux temperature (circa 150°c) for about 60 minutes. At the end of this time period an aliquot of the reaction mixture shows an absence of anhydride by infra-red analysis. The solvent is removed under vacuum to obtain a white powder which is the benzyl ester of 1,2,4-benzene tricarboxylic acid (infrared absorption at 1735 cm⁻¹ and 1705 cm⁻¹). Preparation 2 The procedure of Preparation 1 , supra., is repeated except that the benzyl alcohol as used therein is replaced with an equal proportion of allyl alcohol, neopentyl alcohol, isopropyl alcohol, cyclohexanol, or 4- tert -butylcyclohexanol, respectively, to obtain the corresponding ester of 1,2,4-benzene tricarboxylic acid. Preparation 3 The procedure of Preparation 1 , supra ., is repeated except that excess of methanol was used in place of the solvent solution of benzyl alcohol. The mixture was heated to reflux temperature in a 100°C oil bath for 30 minutes to obtain the methyl ester of 1,2,4-benzene-tricarboxylic acid. Preparation 4 The procedure of Preparation 1 , supra ., is repeated except that a 1.5 molar excess of trifluoroethanol is used in place of the solvent solution of benzyl alcohol. The mixture is heated to reflux temperature in a 130°C oil bath for 24 hours to obtain the trifluoroethyl ester of 1,2,4-benzenetricarboxylic acid. Example 1 (Comparative Example) This example is not an example of the invention but is made for comparative purposes. A 1000 ml four neck flask was fitted with a mechanical stirrer, a pH probe, an aqueous caustic inlet tube and a Claisen adapter to which was attached a dry ice condenser and a gas inlet tube. To the flask was added 280 ml water, 350 ml methylene chloride, 1.4 ml triethyl amine (0.01 mole) and 57 g (0.25 mole) bisphenol-A. With stirring, phosgene was introduced into the flask at a rate of 1g/min. for 30 minutes with the pH maintained in a range of 10 to 11 by addition of 25% aqueous sodium hydroxide. The resin layer was then separated from the brine layer, washed with 3 wt. percent aqueous HCl until washing remained acidic, then twice with distilled water. The resin was then precipitated into 1500 ml. of methanol in a Waring blender and washed with 500 ml more methanol. Example 2 Preparation of a 10 mole percent polycarbonate co-polymer with the mono benzyl ester of 1,2,4-benzenetricarboxylic acid. A 1000 ml four neck flask was fitted with a mechanical stirrer, a pH probe, an aqueous caustic inlet tube and a Claisen adapter to which was attached a dry ice condenser and a gas inlet tube. To the flask was added 280 ml water, 350 ml methylene chloride, 1.4 ml triethyl amine (0.01 mole), 57 g (0.25 mole) bisphenol-A, 0.85 g (0.009 mole) phenol and 7.45 g (0.025 mole, 10 mole %) of the monobenzyl ester of 1,2,4-benzenetricarboxylic acid. With stirring, phosgene was introduced into the flask at a rate of 1 g/min. for 10 minutes with the pH maintained in a range of 6 to 8 by addition of 25% aqueous sodium hydroxide. The pH was then raised to the range of 10 to 11 and maintained in that range while phosgene was introduced at 1g/min. for an additional 30 minutes. The resin layer was then washed and the resin isolated as in Example 1. Examples 3-13 The procedure of Example 2, supra., is repeated except that there is also included in the reaction vessel charge in place of the monobenzyl ester of 1,2,4-benzenetricarboxylic acid a proportion of an ester of 1,2,4-benzenetricarboxylic acid prepared in accordance with one of the Preparations 2-4, supra. In some examples, the proportion of phenol charge is also reduced. The phosgenation is also carried out for a variety of different times and under differing pH conditions. The ester employed, the proportions charged, the pH ranges and the reaction times are given in the following Table with the intrinsic viscosity and the Tg determined for each resin. As may be seen from the above Table, the Tg value of each resin of the invention (Examples 2-13) were generally 1 to 10°C lower than the control (Example 1) while the intrinsic viscosity of all of the resins, including the control are substantially similar. EXAMPLE 14 In the reaction apparatus described in Example I were first mixed 2.92 g (0.1 mole) of the monotrifluoroethyl ester of trimellitic acid, 600 ml of CH₂CL₂, 1.4 ml triethylamine and 2.0 ml dimethylformamide. With stirring, phosgene was introduced into the flask for 5 minutes at 1 g/min. The mixture was then stirred for an additional 5 minutes. To the flask was then added 45.6 g (0.2 mole) of bisphenol-A, 0.15 g (.001 mole) t -butylphenol, and 400 ml water. Phosgene was then added at 1 g/min. for 34 minutes with pH maintained at 9 to 10. The resin layer was then washed and the resin isolated as in Example 1. The resin exhibited and intrinsic viscosity of 0.998. EXAMPLE 15 2.5 g (0.01 mole) of the resin of Example 14, supra., was dissolved in 10 ml methylene chloride. 0.0019 g (0.000005 mole) of (CH₃)₄NB⊘₄ was added, and dispersed as a fine suspension in the solution. The solvent was then stripped off by drying the solution in an oven at 110°C. The resultant sample was then placed in a 3,8 cm (1,5 inch) diameter circular compression mold, heated to 247°C and held at 247-252°C for 20 minutes. A 1.35 g sample of the resultant disk was then placed in 40 ml CH₂Cl₂. The disk swelled and kept its shape substantially. After exhaustive washing with methylene chloride, the gel portion was isolated and dried and found to be 70% by weight of the original sample.

Claims: A thermoplastic polyester-carbonate resin containing in the polymer chain, at least 2 mol %, based on the total mols of carbonate and ester linkages, of divalent moieties of the formula: wherein R represents aliphatic hydrocarbyl of from 1 to 9 carbon atoms, inclusive, halogen substituted aliphatic hydrocarbyl of 1 to 9 carbon atoms, inclusive, aralkyl of 7 to 10 carbon atoms, inclusive and halogen substituted aralkyl of 7 to 10 carbon atoms, inclusive; a and b are each 0 or 1; a + b is 1. The resin of claim 1 which contains in the polymer chain repeating units, of the formula: wherein A is selected from the group consisting of a divalent hycrocarbon radical containing from 1 to 15 carbon atoms; a halogen substituted divalent hydrocarbon radical containing from 1 to 15 carbon atoms; and wherein each X is independently selected from the group consisting of halogen, a monovalent hydrocarbon radical of from 1 to 8 carbon atoms; an aryl group of 6-18 carbon atoms, an aralkyl group of from 7 to 14 carbon atoms, an oxyalkyl group of from 1 to 8 carbon atoms, and an oxyaryl group of from 6 to 18 carbon atoms; and wherein m is zero or l and y is a whole number integer of from 0 to 4. The resin of claim 1 where in the aliphatic hydrocarbyl radical has from 1 to 6 carbon atoms, inclusive.

Inventors: ROSENQUIST, NILES RICHARD
Applicants: GENERAL ELECTRIC COMPANY
Application year: 1986
Main classification: C08G63
IPC codes: C08G64, C08G63, C07D323, C07D327, D01F6