THERMOPLASTIC RESIN COMPOSITION HAVING A MATT APPEARANCE

Abstract: Disclosed is a thermoplastic resin composition having a matt appearance comprising: (A) 80-5 parts by weight of graft copolymer obtained by grafting 40-95 parts by weight of diene rubber with 60-5 parts by weight of vinyl compounds consisting of 0.1-40 weight % of at least one glycidyl ester of an α-­ and β-unsaturated acid as an essential component, 10-40 weight % of a least one vinyl cyanide compound, 60-90 weight % of a least one aromatic vinyl compound and 0-30 weight % of other copolymerizable vinyl com­ pounds, and (B) 20-95 parts by weight of a copolymer obtained through reaction of 10-40 weight % of at least one vinyl cyanide compound, 60-90 weight % of at least one aromatic vinyl com­ pound and 0-30 weight % of other copolymerizable vinyl com­ pounds, the intrinsic viscosity of the resin composition in terms of its components soluble in methyl ethyl ketone be­ ing 0.25-1.5 dl/g (N,N′-dimethyl formamide solution, 30 °C).

Description: The present invention relates to a thermoplastic resin composition having a delustered or matt appearance which is excellent in impact resistance, rigidity, anti-thermal deformation ( heat stability against deformation) and molding property. ABS-type resins have been widely in use for various uses for their excellent impact resistance, thermal deformation resistance, molding property and fine surface lustre. Meanwhile, in the field of automobile upholstery, home electric appliances etc. there has been an increasing demand for parts with their surface delustered or made matt for desired fine and quiet appearance, for sense of being high in quality and for ensuring or improving safety through controlling reflection of light. For controlling lustre and for making parts matt there are a number of conventional methods such as a method of improving the die's (mold's inside) surface, of coating with a delustering paint or mixing the resin with inorganic substances or rubbers. So far, however, no satisfactory results have been obtained by any of these methods. That is, improving the die's surface is accompanied by the difficulty of repairing and/or doing maintenance. Worse, the molded part's luster also depends on molding conditions, hence it is difficult to obtain molded parts constant in luster. When an inorganic substance is added to a synthetic resin, it results in a marked drop of the resin's impact resistance, while addition of a rubber or rubbery matter causes lowering of rigidity, is likely to give rise to the so-called flow-mark or weld line, and after all it is difficult to obtain molded articles with excellent appearance. It is proposed to add to ABS resin copolymers of glycidyl methacrylate and ethylene, styrene, acrylonitrile and acrylic ester etc. but even by this method lowering of impact resistance and molding property will result, also giving rise to color uneveness. FR-A-2 536 080 discloses thermoplastic resin compositions for the preparation of molded articles having a matt appearance, wherein said compositions comprise (A) a rubber modified copolymer and (B) an olefinic polymer having epoxy groups or (B') an olefinic polymer modified by an unsaturated carboxylic acid. The purpose of the present invention is to provide a thermoplastic resin composition having a matt appearance and being excelled in impact resistance, rigidity, thermal deformation resistance and molding property. The present inventors have discovered after their intensive studies that a composition obtained by combination of graft copolymer/s (A) containing special components and vinyl copolymer/s (B) has a matt appearance and is excellent in thermal properties and molding properties, and have thus arrived at the present invention. The present invention relates to a thermoplastic resin composition having a matt appearance comprising: (A) 80-5 parts by weight of graft copolymer obtained by grafting 40-95 parts by weight of diene rubber with 60-5 parts by weight of vinyl compounds consisting of 0.1-40 weight % of at least one glycidyl ester of an α- and β-unsaturated acid as an essential component, 10-40 weight % of at least one vinyl cyanide compound, 60-90 weight % of at least one aromatic vinyl compound and 0-30 weight % of other copolymerizable vinyl compounds, and (B) 20-95 parts by weight of a copolymer obtained through reaction of 10-40 weight % of at least one vinyl cyanide compound, 60-90 weight % of at least one aromatic vinyl compound, and 0-30 weight % of other copolymerizable vinyl compounds, the intrinsic viscosity of the resin composition in terms of its components soluble in methyl ethyl ketone being 0.25-1.5 dl/g (N,N'- dimethyl formamide solution, 30°C). Particularly important in connection with this invention is graft copolymer (A). That is, when 60-5 parts by weight of vinyl compounds are caused to react with 40-95 parts by weight of a diene rubber, 0.1-40 weight %, or, still more preferably, 0.5-30 weight %, based on the total quantity of vinyl compounds, of a glycidyl esterification product should be contained as an essential component, and (A) should be a graft copolymer obtained by grafting of 10-40 weight % of at least one vinyl cyanide compound, 60-90 weight % of at least one aromatic vinyl compound, and 0-30 weight % of a copolymerizable vinyl compound, on said diene rubber in presence of said glycidyl ester. In this graft copolymer (A) the impact strength is lowered when the amount of diene-type rubber is less than 40 parts by weight. On the other hand it is not advisable to increase it beyond 95 parts by weight, because the molding property of the resin is deteriorated. If the amount of glycidyl ester compound of α-, β-unsaturated acid is less than 0.1 weight %, no satisfactory matting effect is attainable, whereas, if it is in excess of 40 weight %, molding property and impact resistance are undesirably deteriorated or lowered. If the amount of the vinyl cyanide compound should increase to be more than 40 weight %, thermal tinting will result at the time of molding. It is also not desirable that the amount is less than 10 weight %, for this results in lower impact resistance. If the amount of aromatic vinyl compound should be less than 60 weight %, deterioration of the molding property is bound to result, while, if it should be in excess of 90 weight %, the impact resistance undesirably decreases. Although there is no particular limitation with regard to the diene rubber used in the manufacture of graft copolymer (A), its diene component should preferably be more than 50 weight % and the mean particle size should be within the range of 0.05 - 2 µm (500 Å - 2 µm). Examples for suitable glycidyl esters of α-, β-unsaturated acids are glycidyl acrylate, glycidyl methacrylate, glycidyl ethacrylate etc. Examples for suitable vinyl cyanide compounds are acrylonitrile, methacrylonitrile etc.. Examples for aromatic vinyl compounds are styrene, methyl styrene, chlorostyrene and α- methyl styrene. Examples for copolymerizable vinyl compounds are methyl methacrylate, ethyl methacrylate, acrylic acid, methacrylic acid, ethyl acrylate, butyl acrylate, phenyl maleimide etc. In copolymer (B) of the present invention, the content of vinyl cyanide compound is preferably 10-40 weight %. If the amount of vinyl cyanide compound exceeds 40 weight %, undesirable discoloration in the course of molding occurs. The amount of aromatic vinyl compound is preferably 60-90 weight %. If it is less than 60 weight %, the molding property deteriorates, while if it is in excess of 90 weight %, it results in an undesirably lower impact resistance. Examples for vinyl cyanide compounds suitable for the preparation of (B) are acrylonitrile, methacrylonitrile etc. Examples for aromatic vinyl compounds are styrene, methylstyrene, chlorostyrene, α-methyl styrene etc. Examples for copolymerizable vinyl compounds are acrylic acid, methacrylic acid, ethyl acrylate, methyl methacrylate, butyl acrylate, phenyl maleimide etc. The above graft copolymer (A) and the copolymer (B) are preferably obtained by emulsion polymerization, but this does not necessarily mean limitation to emulsion polymerization. As to emulsion polymerization, any conventional method is applicable to this case of emulsion polymerization. That is, the above-mentioned compounds are caused to react with each other in an aqueous medium in the presence of a radical initiator. The above-mentioned compounds may as well be used as a mixture. If necessary, it is also possible to employ the above-mentioned compounds in proper portions. Further, as to the method of adding the above-mentioned compounds it is possible to add either all at once or in portions, and thus there are no particular limitations in this respect. Suitable radical initiators are, among others, water-soluble or oil-soluble peroxides such as potassium persulfate, ammonium persulfate, cumene hydroperoxide, paramentan hydroperoxide etc. Besides, other polymerization accelerators, polymerization degree adjusters, emulsifiers, etc. can be chosen from those widely used for the emulsion polymerization method. The matt appearance, impact resistance, heat resistance, rigidity and molding property of the composition made from the graft copolymer (A) and the copolymer (B) depend not only on the composition and polymerization degree of the above-mentioned (A) and (B), but also on the blending ratio of the two. Hence, desired properties can be achieved by properly adjusting the blending ratio. Generally, however, it is preferred to blend 80-5 parts by weight of the graft copolymer (A) and 20-95 parts by weight of the copolymer (B). That is, if the portion of the graft copolymer (A) exceeds 80 parts by weight, the molding property, rigidity and resistance to thermal deformation are deteriorated or lowered, whereas if it is less than 5 parts by weight, the impact resistance is lowered. The intrinsic viscosity of the composition of the present invention made up of the graft copolymer (A) and the copolymer (B) in terms of methyl ethyl ketone-soluble components is desirably in a range of 0.25-1.5 dl/g (N,N' - dimethyl formamide solution, 30 °C). When it is less than 0.25 dl/g, the mechanical strength such as impact resistance is lowered, while if it is in excess of 1.5 dl/g, the molding processability decreases, these both being undesirable. Blending, pelletizing and molding may be carried out by any of the known methods. It is possible to obtain a powder by salting out, coagulating, dehydration and drying a mixture of latices of graft copolymer (A) and copolymer (B) and then have it kneaded under heating by e.g. rolls, screw, Banbury Mixer®, kneader etc. before molding. If necessary, it is possible to add some stabilizer, pigment, lubricant, anti-static agent etc. during blending. It is also possible to blend it with ordinary ABS resin, AS resin, polyvinyl chloride, polycarbonate etc. The composition of the present invention obtained by the method described above has a matt appearance, and is excellent in impact resistance, stiffness, safety from thermal deformation and moldability. Hereafter concrete explanation of the present invention is to be made, referring to preferred embodiments (examples) of the invention. In these embodiments "part" means part by weight and % means weight %. EXAMPLES AND CONTROL EXAMPLES (a) Manufacture of graft copolymer (A) The following substances were charged into a reaction tank equipped with a stirrer. After deoxidation the above mixture in the reaction tank was heated to 60°C under stirring, the compounds shown in Table 1 were continuously added dropwise for 5 hours and after completion of addition thereof, stirring was continued for 1 hour at 60°C until completion of polymerization. (b) Manufacture of copolymer (B) The following substances were charged into a reaction tank equipped with a stirrer. After deoxidation the compounds (I) shown in Table 2 were added after preheating to 60 °C under stirring in a nitrogen atmosphere. After completion of thorough emulsification the compounds (II) shown in Table 2 were added continuously dropwise for 6 hours. Then stirring was continued for 1 hour at 60°C until polymerization was completed. No. Examples B-1 B-2 B-3 Monomer (I) αMSt (%) 75 - - tDM (part) 0.2 - - Monomer ( II) AN (%) 22 20 30 αMSt (%) 3 50 - MMA (%) - 10 - St (%) - 20 70 CHP (part) 0.5 0.5 0.5 tDM (" ) 0.2 0.3 0.3 (Note) αMSt α-methylstyrene AN Acrylonitrile St Styrene MMA Methyl methacrylate CHP Cumene hydroperoxide tDM Tertiary dodecyl mercaptan (c) Manufacture of thermoplastic resin composition The graft copolymer (A) and the copolymer (B) manufactured by the methods described above under (a) and (b) were mixed in the form of latex at a given ratio, and an anti-oxidant was added to the mixed latex and after addition of calcium chloride for coagulation thereof, the resulting composition was rinsed with water, filtered, dried and pelletized for preparation of samples for physical properties. The results are shown in Table 3. As is apparent from the data of Table 3, the compositions of the present invention C-1 to C-5 are matt in surface appearance, and are thermoplastic resin compositions outstanding in rigidity, resistance to thermal deformation and molding property.

Claims: A thermoplastic resin composition having a matt appearance comprising: (A) 80-5 parts by weight of graft copolymer obtained by grafting 40-95 parts by weight of diene rubber with 60-5 parts by weight of vinyl compounds consisting of 0.1-40 weight % of at least one glycidyl ester of an α- and β-unsaturated acid as an essential component, 10-40 weight % of at least one vinyl cyanide compound, 60-90 weight % of at least one aromatic vinyl compound and 0-30 weight % of other copolymerizable vinyl compounds, and (B) 20-95 parts by weight of a copolymer obtained through reaction of 10-40 weight % of at least one vinyl cyanide compound, 60-90 weight % of at least one aromatic vinyl compound, and 0-30 weight % of other copolymerizable vinyl compounds, the intrinsic viscosity of the resin composition in terms of its components soluble in methyl ethyl ketone being 0.25-1.5 dl/g (N,N'- dimethyl formamide solution, 30°C). A composition of claim 1, wherein the amount of glycidyl ester of an α-, β-unsaturated acid used for the preparation of graft copolymer (A) is 0.5-30 weight %, based on the total amount of vinyl compounds. A composition of claim 1, wherein said diene rubber used for the preparation of graft copolymer (A) contains not less than 50 weight % of diene component and has an average particle size of 0.05 - 2 µm (500 Å - 2 µm).

Inventors: MATSUMOTO, SHIGEMI, NAGOSHI, FUMIYA
Applicants: KANEGAFUCHI KAGAKU KOGYO KABUSHIKI KAISHA
Application year: 1986
Main classification: C08L51
IPC codes: C08L51, C08L25, C08F279, C08L7, C08L33, C08L21