PROCESS FOR LUBRICATING MAGNETIC DISKS, AND TO MAGNETIC DISKS

Abstract: A process for lubricating a magnetic disk consists of applying a polymeric lubricant having a functional terminal group to a magnetic disk, heating the lubricant so that the functional group covalently bonds to surface polymers and/or metal oxides of the magnetic disk, and then either removing the unreacted lubricant with a solvent and then contacting the disk with a non-functionalised lubricant or reacting the unreacted lubricant with an aziridine or epoxide compound.

Description: This invention relates to processes for lubricating magnetic disks and to magnetic disks. Lubricants applied, but not bonded, to magnetic disks are subject to removal either by use of cleaning chemicals or by spin-off as the magnetic disk is rotated. US-A-4,268,556 proposes a series of highly polar lubricants which are resistant to solvents. US-A-4,446,193 proposes a diazo compound applied to a disk. This compound is then heated to form a carbene intermediate which bonds to polymeric coatings and metal oxides of most magnetic disks. However, diazo compounds are toxic and highly unstable rendering both the manufacturing process and resulting disk potentially unsafe. According to one aspect of the present invention there is provided a process for lubricating a magnetic disk characterised by applying a polymeric lubircant having a functional terminal group to a magnetic disk, heating the lubricant so that the functional terminal group covalently bonds to surface polymers and/or metal oxides of the magnetic disk, and then either removing the unreacted lubricant with a solvent and then contacting the disk with a non-functionalised lubricant or reacting the unreacted lubricant with an aziridine or epoxide compound. According to a further aspect of the present invention there is provided a process for lubricating a magnetic disk characterised by contacting the disk with a lubricant having a functional terminal group, heating the lubricant for a time sufficient for the functional terminal group of a sufficient portion of the lubricant to bond covalently to the surface of the disk, and reacting the residual unbonded lubricant with an aziridine or epoxide compound. In one embodiment the aziridine compound has three aziridine groups. The aziridine compound having three aziridine groups reacts with three carboxyl groups to form a large polymer of high molecular weight having exceptionally low surface friction and no detectable spin-off. According to another aspect of the present invention there is provided a process for lubricating a magnetic disk characterised by contacting the disk with a functionalised lubricant having at least one functional terminal carboyxl group, heating the lubricant for a time sufficient for the functional terminal groups to bond covalently to the surface of the disk, removing the unbonded lubricant with a solvent, and contacting the disk with a non-functionalised lubricant. The non-functionalised lubricant may be a perfluorinated polyether. The lubricant may be a perfluorinated polyether having at least one terminal carboxyl group. According to a still further aspect of the present invention there is provided a magnetic disk characterised by having a functionalised lubricant part of which is bonded to oxide material and/or binder of the disk and part of which is bonded to an aziridine or epoxide compound. The present inventors have determined that mere application of a carboxyl terminated lubricant, for example as in Examples 9 and 13 of US-A-4,268,556, results in a lubricant having extremely poor surface friction properties and a relatively poor surface retention characteristic. However, heating such a lubricant above 65°C (150°F) for six or more hours dramatically increases the surface retention characteristic. Also the amount of lubricant removable from the disk by solvents dramatically decreases, indicating an increase in the amount of lubricant bonded to polymeric coatings and metal oxides of the magnetic disk. However, unless the residue is removed, the remaining carboxyl terminated polymers cause high surface friction. A disk having only a covalently bonded lubricant may exhibit good frictional and retention properties, but wear characteristics can be expected to be poor in that lubricant, once worn from a location, is not replaced with more mobile lubricant. The present invention solves this problem by the addition of a conventional, non-functionalised lubricant to the surface having the bonded lubricant with an aziridine or epoxide compound. The non-functional lubricant increases wear resistance and at the same time does not spin-off to any significant degree. The reacted unbound lubricant exhibits no spin-off whatsoever. It is speculated that the cause of this increase in resistance to spin-off is the uncoiling of the bonded lubricant under heat to form a tree-like structure between which the non-­ functionalised lubricant or the inert functionalised lubricant must flow. The tree-like structure is confirmed by the increased thickness of the bonded coating under the influence of heat. In the following examples, spin-off of lubricant was determined by rotating the lubricated disk at 3600 rpm, providing silicon targets at the periphery of the disk, and periodically analysing the targets for the quantity of fluorine they contain, which is proportional to the quantity of fluorinated lubricant spun off. Surface friction was determined by the magnitude of force necessary to break free a 30g weighted head. Sliding friction was the force on the head at 200ips. Wear was determined by a count of 1000 particles in 6 minutes, which is indicative of catastrophic failure. Thickness was determined by ESCA (electron scanning for chemical analysis). EXAMPLE 1 This first example is of a non-functionalised lubricant conventionally used to lubricate a magnetic disk. The test results provide a basis for comparison with the results of the following Examples. A rigid magnetic disk having magnetisable iron and aluminium oxide particles in a phenolic-phenoxy polymeric binder was lubricated by spraying a 2% by weight solution of a perfluorinated polyether (Krytox 143 AC (Trade Mark) from Dupont) and 1,1,2-­ trichloro-trifluoro-ethane (Freon 113 - Trade Mark). A perfluorinated polyether has the general formula: CF₃--(C₂F₃CF₃O) m --(CF₂CF₂O) n --CF₃ where m and n are varied to provide for varying viscosities. In this Example the average molecular weight was 6,200 and the viscosity was 270 centistokes at 38°C (100°F). After application, the thickness of the lubricant layer on the disk was 70Å and the weight of the lubricant on the disk was 2.5mg. The above-described tests were performed on the disk and the following results obtained: static friction = 3.9 grams sliding friction = 2.3 grams lubricant spin-off rate = 6.3% per 30 days wear time to failure = 8.3 hours. EXAMPLE 2 In this Example a functionalised lubricant was applied to the disk as in the previous Example. The lubricant contained a perfluorinated polyether of an identical structure to that of Example 1 except that one of the terminating CF₃ groups was replaced by a carboxyl group (-COOH). The perfluorinated polyether was that available under the Trade Mark Krytox 157 M from Dupont. The average molecular weight was 4,500 and the viscosity was 280 centistokes at 38°C (100°F). A 2% solution with 1,1,2-­ trichloro-trifluoro-ethane (Freon 113 - Trade Mark) as in Example 1, was applied to a disk by spraying and hand-buffing. The tests were then performed with the following results: static friction = 20.4 grams sliding friction = 7.6 grams lubricant spin-off rate = 5.9% per 30 days wear time to failure = 3.2 hours. The results show that this carboxyl terminated lubricant exhibited poor frictional and wear characteristics while the retention time is not significantly improved. EXAMPLE 3 This Example was the same as Example 2 except that the disk was first heated at 121°C (250°F) for 24 hours: static friction = 18.4 grams sliding friction = 7.0 grams lubricant spin-off rate = 0.8% per 30 days wear time to failure = 4.6 hours These results show a significant reduction in spin-off lubricants. EXAMPLE 4 This Example was the same as Example 3 except that the disk was subsequently exposed to 1,1,2-trichloro-trifluoro-ethane (Freon 113 - Trade Mark). This removed all unbonded lubricant. The total weight of lubricant removed was 6.2mg. A perfluorinated polyether (Krytox 143 AC - Trade Mark) was then applied as in Example 1 using a 2% solution in 1,1,2-trichloro-trifluoro-ethane (Freon 113 - Trade Mark). The disk absorbed 6.0mg of the lubricant, about two-and-one-half times the amount absorbed by the disk of Example 1. The tests were performed giving: static friction = 3.5 grams sliding friction = 2.5 grams lubricant spin-off rate = 1.0% per 30 days wear time to failure = 12.3 hours Static and sliding friction were similar to Example 1 but the lubricant spin-off rate is six times better and wear time one-and-a-half times better. The bonded lubricant contributed to the increased surface retention. EXAMPLE 5 This Example was the same as Example 3 except that the disk used did not include metal oxide particles in the binder. After heat treatment, the disk was exposed to vapour of 1,1,2-trichloro-trifuluoro-ethane and 2.5mg of the lubricant was removed, compared with 6.2mg in Example 4. ESCA analysis showed virtually no remaining lubricant indicating virtually none of the functionalised lubricant polymers bonded to the binder. This indicates that the bonding is to the metal oxide particles, most probably to the oxygen of the metal oxides. It is expected that the lubricant, when heated, will also bond to organic binders having hydroxyl or polar groups. EXAMPLE 6 This Example is the same as Example 3 except that the heat treated lubricant on the disk was then oversprayed with a 1% solution by weight of R-(N-(CH₂)₂)₃, which contains three aziridine groups in 1,1,2-trichloro-trifluoro-ethane (Freon 113 - Trade Mark). In this Example, the aziridine compound is trimethylolpropane-­ tris-(B-(N-aziridinyl) propionate) available from Cordova Chemical Company under the Trade Mark XAMA-2. In this Example the molecular weight of the compound was 425 and the viscosity was 125 centistokes at 22°C (72°F). The carbon atoms of each aziridine molecule react with the terminal carboxyl groups of three of the unbonded lubricant molecules to form a unified molecule having a central R surrounded by three branches of the aziridine-functionalised lubricant. The disk was allowed to stand for several minutes at room temperature prior to testing: static friction = 2.0 grams sliding friction = 1.8 grams lubricant spin-off rate = 0% per 30 days wear time to failure = greater than 24 hours. These results show significant reductions in friction and no observable spin-off. Also the wear time for the disk was dramatically improved over the previous Examples. As mentioned above, it is expected that aziridine containing compounds could have fewer than three aziridine groups of molecules. Also expected to work is an epoxide containing radical, e.g. H₂COCH-R where R is an alkyl group. Th epoxide reacts with the carboxyl terminal group of the functionalised lubricant to form the following product: R f COO - CH₂CHOH - R, where R f is the perfluorinated polyether lubricant and R is an alkyl group. Moreover, a multi epoxy containing molecule can also be utilised. In the above Examples, the lubricated disk was heated for 24 hours at 121°C (250°F). Subsequent testing has determined that sufficient functionalised lubricant retention is obtained when the disk is heated from 65°C (150°F) to 149°C (300°F) for between 6 and 10 hours. Temperatures above 149°C (300°F) may reduce the time factor further.

Claims: 1. A process for lubricating a magnetic disk characterised by applying a polymeric lubricant having a functional terminal group to a magnetic disk, heating the lubricant so that the functional terminal group covalently bonds to surface polymers and/or metal oxides of the magnetic disk, and then either reroving the unreacted lubricant with a solvent and then contacting the disk with a non-functionalised lubricant or reacting the unreacted lubricant with an aziridine or epoxide compound. 2. A process for lubricating a magnetic disk characterised by contacting the disk with a lubricant having a functional terrinal group, heating the lubricant for a time sufficient for the functional terminal group of a sufficient portion of the lubricant to bond covalently to the surface of the disk, and reacting the residual unbonded lubricant with an aziridine or epoxide compound. 3. A process as claimed in any preceding claim characterised in that the aziridine compound has three aziridine groups. 4. A process for lubricating a magnetic disk characterised by contacting the disk with a functionalised lubricant having at least one functional terminal carboxyl group, heating the lubricant for a time sufficient for the functional terminal groups to bond covalently to the surface of the disk, removing the unbonded lubricant with a solvent, and contacting the disk with a non-functionalised lubricant. 5. A process as claimed in claim 4 characterised in that the non-functionalised lubricant is a perfluorinated polyether. 6. A process as claimed in any preceding claim characterised in that the lubricant is a perfluorinated polyether having at least one terminal carboxyl group. 7. A magnetic disk characterised by having a functionalised lubricant part of which is bonded to oxide material and/or binder of the disk and part of which is bonded to an aziridine or epoxide compound.

Inventors: JANSSEN, ROBERT ALLEN, SORENSON, GARY DOUGLAS
Applicants: MAGNETIC PERIPHERALS INC.
Application year: 1986
Main classification: G11B5
IPC codes: G11B5, C10M107, C10N40, C09D171