METHOD FOR COUPLING LIVING POLYMERS OBTAINED BY ANIONIC POLYMMERIZATION

Abstract: Coupling agents of general formula and/or and their use in a method for the termination of living polymers obtained by the anionic polymerization of dienic and/or vinylaromatic monomers.

Description: The anionic polymerization, if carried out under proper conditions and starting from suitable monomers (M. SZWARC, Carbanions, Living Polymers and El. Transfer Processes, Interscience Publishers, J. Wiley and Sons, New York, 1968), allows living polymers to be obtained, which are well fit for suitable transformations. Among these, the reaction of coupling (uniting two or more polymeric segments through a linking agent to yield a polymer having molecular weight nPM, wherein PM is the molecular weight of the polymeric segment and n is the functionality of the linking agent) is certainly one of the most investigated processes, because it allows, by a simple approach, important changes to be obtained also in terms of properties of the polymers processed. For example, in case of polymerization of dienes, by this way increasing Mooney viscosity, reducing the "cold flow", increasing the "green tensile strength" and even succeeding in modifying the molecular weight as desired is possible. In case then of the synthesis of block polymers constituted by linear or branched couplings of A-B ele­ ments (wherein A is an aromatic polyvinyl and/or polyiso­ propenyl sequence and B is a dienic sequence, also hydro­ genated), the use of efficient coupling agents becomes a factor of basic importance because, as known, the pos­ sible presence of unreacted A-B products in the end product impairs the technological properties of the same. In the technical literature, numerous examples are reported of coupling agents [H.L. HSIEH, Rubber Chem. and Tech. 49 (5), 1305 (1976)]. We have found now that the herunder exemplified compounds can be conveniently used as new coupling a­ gents, because, besides the properties typical of the best coupling agents described in technical literature (cfr. H.L. Hsieh, ibid.), they show the following advan­ tages: i) the coupling reaction can be accomplished without the use of activators; ii) the coupling reaction can be accomplished at a tem­ perature lower than that normally used for the tra­ ditional coupling agents, with the reaction time being the same; iii) no side products are formed, because the coupling reaction is an addition, and not a removal reaction. The products which we found to be efficient coupling agents are comprised within the following general formu­ la: and/or wherein: X = aryl, condensed aryl, aryl isolated by a hetero­ atom or by an alkenylic group, alkyl with a number of C atoms comprised between 2 and 20, cycloalkyl, alkylcycloalkyl, radical with heteroatoms; all these groups can possibly contain a functional group of vinylaromatic, ester, aldehydic, ketonic, cyano type, etc... Y = aryl, cycloalkyl, alkyl, alkylaryl, alkylcycloalk­ yl, possibly containing a functional group of vinylaromatic, ester, aldehydic, ketonic, cyano type, etc... n = an integer, comprised within the range of from 1 to 4; n' = an integer, comprised within the range of from 1 to 4; R = H or alkyl group, but preferably H; Z = aryl, alkyl, cycloalkyl, possibly containing a functional group of vinylaromatic, ester, alde­ hydic, ketonic, cyano type, etc... Such coupling agents can be prepared in an easy way, and with yields which in many cases can be quantitative, according to the following procedure: and/or with the water formed being removed by azeotropic distil­ lation with a suitable solvent. In the synthesis of compounds (I), at least one functional group among those reported above must be pres­ ent either in radical X, or in radical Y, on in both of them. Non limitative examples of aminic compounds possibly containing at least one functional group of vinylaromat­ ic, ester, aldehydic, ketonic, cyano group, etc. [see radical X] are: butylamine, aniline, methyl p-aminoben­ zoate, ethyl p-aminobenzoate ad isomeric compounds; p-­ aminostilbene, p-phenylenediamine, 4-aminobenzonitrile, glycine methylester, 1,5-diaminonaphthalene, 1,6-diamino­ hexane, 2,6-diaminopyridine, 4,4'-diaminodiphenylether, 4,4'-diaminodiphenyl, 1,4,5,8-tetraaminonaphthalene, etc... Non limitative examples of aldehydic and/or ketonic and aminic compounds used, possibly containing at least one functional group among those indicated above (see radical Y), are: benzaldehyde, methyl 4-formylbenzoate, 4-cyanobenzaldehyde, 4-formylstilbene, cyclohexanalde­ hyde, butyraldehyde, acetone, methylphenylketone, methyl 4-acetylbenzoate, butylamine, aniline, methyl 4-aminoben­ zoate, etc... Non limitative examples of compounds, possibly con­ taining at least one functional group among those indi­ cated above, to be used for Z, are: benzaldehyde, methyl 4-formylbenzoate, 4-cyanobenzaldehyde, 4-formylstilbene, o-, m-, p-phthalaldehyde, tetramethylenedialdehyde, meth­ yl 4-acetylbenzoate, methyl 4-benzoylbenzoate, p-diacetyl­ benzene, p-dibenzoylbenzene, etc... Also in the synthesis of compounds (II), at least one functional group among those reported above must be present either in radical Z, or in radical Y, on in both of them. The compounds of the present patent application can be used in processes for the polymerization of monomers susceptible of anionic initiation under livingness condi­ tions, and in particular for the polymerization of dienic and/or vinylaromatic monomers. The conjugated dienes used contain from 4 to 12, and preferably from 4 to 8 carbon atoms. Such monomers comprise: 1,3-butadiene, isoprene, 2,3-diemthylbutadiene, piperylene, 3-butyl-1,3-octadiene and 2-phenyl-1,3-butadiene. The vinylaromatic monomers contain from 8 to 20, and preferably from 8 to 14 carbon atoms. Typical examples are: styrene, α-methylstyrene, 1- vinylnaphthalene, 2-­ vinylnaphthalene, 2-isopropenylnaphthalene, p-phenylsty­ rene, 3-methylstyrene, α-methyl-p-methylstyrene and p-­ cyclohexylstyrene. The conjugated dienes and/or the vinylaromatic mono­ mers can be polymerized either alone or in mixture or sequentially, to form homopolymers, random copolymers and block copolymers. The polymerization is carried out in solution at temperatures comprised within the range of from -100 to +200°C and preferably of from 0 to 100°C, and under a pressure which is the pressure of the system under the temperature conditions used; however, higher or lower pressured are not contraindicated. Suitable solvents comprise paraffinic, cycloparaf­ finic and aromatic hydrocarbons. Typical examples are cyclohexane, hexane, pentane, heptane, isooctane, ben­ zene, toluene and mixtures thereof. As known, small amounts of polar compounds can be added to the solvent to the purpose of obtaining, in the polymerization of diene, 1,2-configuration, or of in­ creasing the efficiency of the initiator in case of polymerization of vinylaromatic monomers. The initiators are the typical anionic initiators normally used to this purpose. Preferably, the organometallic compounds of formula R-Me are used, wherein R is an aliphatic, cycloaliphatic or aromatic hydrocarbon radical, and Me is an alkali metal, preferably lithium. The amount of initiator used is related to the molecular weight of the polymer which one wishes to obtain. The polymerization is carried out under such conditions as to secure the livingness of the polymer obtained (M. SZWARC, Carbanions, Living Polymers and El. Transfer Processes, Interscience Publishers, J. Wiley & Sons, New York, 1968). The coupling agents can be introduced into the reac­ tion medium by any way, either by one single addition, or by a portionwise addition and at the desired time. Preferably, it is introduced at the end of the polymerization, in the desired amount. The molar amount of coupling agent (m AC ) to be added is given by the formula: m AC = m CA /f AC wherein m CA = mol of active centres of living polymer and f AC = functionality of the coupling agent (besides the presence of the reactive groups -CH=N-, also other addi­ tional functional groups exist). The amount used of coupling agent conditions the coupling yields: obviously, a stoichiometric ratio of polymer active centre to coupling agent active centre (by taking into account the functionality thereof) favours the highest yield. The temperature at which the "coupling" reaction is carried out depends on the type of agent used, on the type of polymer submitted to the reaction, and on other factors, e.g., on the reaction medium: it can vary gene­ rally within the range of from 20° to 150°C, but the reaction is preferably carried out between 40° and 80°C. The contact times are comprised within the range of from some minutes to some hours: preferably, times com­ prised within the range of from 10 minutes to 2 hours are used. Sometimes, also polar activators, which improve the coupling rate, can be used: in the case of the most active coupling compounds herein claimed, the use of these activators is not required. The solvents are those used in the polymerization. The coupling reaction is carried out under a pres­ sure which is the pressure of the system at the tempera­ ture at which the reaction is carried out, but higher or lower pressure are not contraindicated. Example 1 The polymerization and coupling are carried out inside a reactor of 1 litre of capacity, equipped with stirrer, pressure gauge, thermocouple sheath and inlet way for the reactants and the inert gas. In the order, 500 cm³ of anhydrous cyclohexane, 12 g of styrene and 1,5 mmol of Li-sec.butyl are charged, leaving to polymerize at 60°C for about 1 hour. At the end, 28 g of butadiene is introduced and the reaction is complete at 60°C within 1 hour. A very small aliquot of this polymer is isolated and submitted to the various analyses. At 60°C, 0.50 mmol is then injected of a sol­ ution in benzene-cyclohexane (50-50 v/v) of methyl-N-­ [benzylidene] p-aminobenzoate 15 minutes later the polymer, after the addition of 1 g of antioxidizer, is coagulated with an excess of methanol, 40 g being obtained of a product which is dried at 60°C for 15 hours under vacuum. The properties of the polymers before and after the coupling reaction are reported in Table 1. The polymer A-B-A of Example 1 has the following technological properties: Elongation :900% Ultimate Tensile Strength: 34.4 MPa whilst the corresponding polymer A-B, with the elongation being the same, shows an ultimate tensile strength of about 3 MPa. If, instead of methyl-N-[benzylidene] p-aminoben­ zoate, as the coupling agent dichlorodiphenylsilane is used, under the same experimental conditions, the coupl­ ing efficiency is lower than 10%. Example 2 The test 1 is repeated, with the only variant that p-phenylenediamine-N,N'-bis[(benzylidene)-4-(carbomethox­ y)] (0.25 mmol) is used, and polymers (A-B and A-B-A) having the proper­ ties shown in Table 2 are isolated. Example 3 Into the reactor described at Example 1, 50 g of α-­ methylstytene and 1.5 mmol of Li-sec.butyl are charged, the polymerization being carried out at 20°C for 1 hour and 15 minutes. At the end, 5 g of butadiene is added, the reaction being let proceed for 15 minutes, and subsequent­ ly 500 cm³ of cyclohexane with 25 g of butadiene is added, the polymerization being let proceed at 60°C for 1 hour. A small sample is drawn, and 0.25 mmol of 1,6-­ diamino-hexane-N,N'-bis[(benzylidene)-4-(carbomethoxy)] is then injected, the coupling reaction being carried out at the temperature of 80°C for 15 minutes. In the usual way a polymer (43 g) is isolated, which has the proper­ ties described in Table 3, wherein also the properties of product A-B are reported. Example 4 The test 1 is repeated, with the only difference that as the coupling agent, 4-carbomethoxybenzylideneani­ line is used. Example 5 The polymerization test is carried out as described at Example 1, but with 1.0 mmol of Li-sec.butyl, and, as the coupling agent, 4-[(benzene-ethenyl)-benzylidene]ani­ line is used. The data relevant to the polymers isolated is shown in the following Table. Example 6 The test is carried out as in Example 1, but instead of butadiene, isoprene is polymerized. As the coupling agent, methyl-N-[benzylidene] p-aminobenzoate is used, the reaction being carried out at 60°C for 30 minutes. The data relevant to the polymer isolated (≃40 g) and to the corresponding product A-B is shown hereunder. see Table 1. Example 7 In the same equipment as of the above tests, 40 g of butadiene is polymerized at 60°C for 1 hour, with 1 mmol of Li-sec.butyl in 400 cm³ of cyclohexane. At the end, a mixture of methyl-N[benzylidene] p-aminobenzoate (0.15 mmol) and 1,6-diaminohexane-N,N'-bis-[(benzylidene)-4-­ (carbomethoxy)] (0.09 mmol) is added, the reaction being let proceed 15 minutes at 60°C. The G.P.C. chart of the polymer isolated shows the presence of peaks of products having different coupling degrees, and with a distribu­ tion of molecular weight broader than of polymer A-B.

Claims: 1. Agents for the coupling of "living" macroanions having the general formula: and/or wherein: X = aryl, condensed aryl, aryl isolated by a hetero­ atom or by an alkenylic group, alkyl with a number of C atoms comprised between 2 and 20, cycloalkyl, alkylcycloalkyl, radical with heteroatoms; all these groups can possibly contain a functional group of vinylaromatic, ester, aldehydic, ketonic, cyano type; Y = aryl, cycloalkyl, alkyl, alkylaryl, alkylcycloalk­ yl, possibly containing a functional group of vinylaromatic, ester, aldehydic, ketonic, cyano type;n = an integer, comprised within the range of from 1 to 4;n' = an integer, comprised within the range of from 1 to 4; R = H or alkyl group, but preferably H; Z = aryl, alkyl, cycloalkyl, possibly containing a functional group of vinylaromatic, ester, alde­ hydic, ketonic, cyano type. 2. Method for the termination of "living" macroani­ ons obtained by the anionic polymerization of dienic and/or vinylaromatic monomers, consisting in introducing into the polymerization mixture, in one single addition, or with portionwise additions, and at the desired time, a coupling agent according to preceding claim. 3. Method for the termination of "living" polymers according to preceding claim, characterized in that it is carried out in the presence of activators. 4. Method for the termination of living polymers according to claim 2, characterized in that it is carried out at temperatures comprised within the range of from 20 to 150°C. 5. Method for the termination of living polymers according to claims 2 and 4, characterized in that it is preferably carried out at temperatures comprised within the range of from 40 to 80°C.

Inventors: GANDINI, ALBERTO, ROGGERO, ARNALDO
Applicants: ENIRICERCHE S.P.A.
Application year: 1986
Main classification: C08C19
IPC codes: C08F2, C08C19, C08F297, C08F8