CARBON MONOXIDE OXIDIZING CATALYST

Abstract: A carbon monoxide oxidizing catalyst for removing car­ bon monoxide from an air comprising a porous carrier, on said carrier, a palladium salt and a copper salt as main active components and a vanadium compound or of a vanadium compound and a said main active components and said promotor.

Description: This invention relates to a carbon monoxide oxidizing catalyst particularly for removing carbon monoxide from an air containing it. In general, carbon monoxide (referred to as CO herein after) evolved by uncomplete combustion of simple substance or compounds of carbon become attached very firmly to hemo­ globin in blood, forming CO-hemoglobin, this preventing remarkably the functions of blood to absorb and carry oxy­ gen, resulting in developing acute poisonous symptoms such as headache or dizziness, extremely causing death. Also it is said the long-term exposure to an air containing a high concentration of carbon monoxide induces chronic heart di­ seases. CO oxidizing catalysts are used for converting harmful CO in an air into innocuous carbon dioxide (CO₂). For exam­ ple, they are packed in air cleaners, the absorption chamber of gas masks, or filters. At present, there is a need for the development of CO oxidizing catalyst not only capable of efficiently oxidizing CO and thereby cleaning an air contai­ ning a high concentation of CO but also having a superior durability permitting a long-term use. So far are known many CO oxidizing catalysts usable under normal conditions, i.e. ordinary ambient temperature, atmospheric pressure and humidity. They are roughly classi­ fied as follows: (1) Metal oxide catalysts (2) Precious metal catalysts (3) Redox catalysts. (1) A typical known catalyst is the so-called hopcalite catalyst consisting essentially of manganese dioxide and copper oxide (disclosed in Japanese laid-open patent appli­ cation Nos.72988/1976 and 96399/1978). It however has an disadvantage of being affected by moisture with much rapid destroy in activity, and hence the combined use of it with a powerful dehydrating agent is necessary. (2) Some catalysts containing such as palladium or platinum have been disclosed in Japanese laid-open patent application Nos.73344/1980, 149192/1978 and 137039/1980. Any of these has a disadvantage that though the effect of remo­ ving CO from an air is adequate when it is of a relatively low concentration (2000 ppm), their activity is poor when it is of a relatively high CO concentration (1%) and decays in a short time. (3) A redox pair catalyst is typical which is composed of palladium chloride and cupric chloride and known as the so-called Wacker catalyst. The catalyst which was developed for the purpose of synthesizing acetaldehyde from ethylene also has a high activity of oxidizing CO. The mechanism of oxidation of CO in the presence of Wacker catalyst is represented by the reaction equations (J. Air Pollution Control Assoc. 28: 253, 1978): A problem is encountered also in this catalyst that when carried on a porous carrier and used over a long time as a CO oxidizing catalyst, its temperature is raised by the oxidation heat of CO, and HCl is produced as expressed by equation (1) and volatilized away from the system, thus the redox cycle become gradually unbalanced, resulting in fall in CO oxidation rate. With special regard to these difficulties, the principal object of the invention is to provide a CO oxiding catalyst having a satisfactory durability of high activity permitting in long-term use under natural conditions. The inventors have endeavored to do study on the impro­ vement in the durability of the conventional redox catalyst, which is composed of palladium chloride and cupric chloride permitting to maintain its high CO oxidizing activity throughout a long use time, and as a result found, that the addition of vanadium element or a compound of it and a phosphorus compound as promotor is effective to prevent the activity of the redox catalyst from being destroyed. Thus the invention has been accomplished. The invention provides a CO oxydizing catalyst compri­ sing a porous carrier carrying thereon as main active compo­ nents palladium salt and copper salt and in addition a promotor consisting of a vanadium compound, or of a vanadium compound and a phosphorus compound. Vanadium compounds suitable for use in the invention, which are to be added to redox catalyst, are such as ammo­ nium metavanadate (NH₄VO₃), sodium vanadate (NaVO₃) and vanadium oxide (V₂O₅). Examples of suitable phosphorus com­ pounds are phosphoric acid (H₃PO₄), phosphorus pentoxide (P₂O₅) and ammonium phosphate ((NH₄)₃PO₄). A palladium compound preferred as a component of the redox catalyst is palladium chloride (PdCl₂) but palladium sulfate (PdSO₄) and palladium nitrate (Pd(NO₃)₂) may be used in combination. As copper salt are used preferably cupric chloride (CuCl₂), and also others such as cuprous chloride (CuCl), copper sulfate (CuSO₄) and cupric nitrate (Cu(NO₃)₂). Examples of suitable carriers for use in the invention are γ -alumina, active carbon, silica-alumina and zeolite. Any other porous material suitable for a catalyst carrier may be used without being particularly limited. Carriers of honeycomb-structured material or sponge-tissue ceramic can be used. Suitable ratios of deposited active components to their carrier are as follows: palladium salt, 0.01-02 m mol/g; and copper salt, 0.1-2.0 m mol/g, preferably 0.4-1.0 m mol/g. Further any vanadium compound is deposited onto the carrier (as vanadium) in 0.1-3.0% by weight, preferably 0.5-1.5% by weight. (calculation with respect to vanadium.) Ratio of phos­ phorus compound to a carrier may be within 0.1-1.0% by weight as phosphorus. The deposition of active substances on the carrier is made according to the following procedure: a carrier is immersed in an aqueous solution containing a palladium salt, a copper salt and a vanadium compound, or additionally a phosphorus compound, heated with consequent concentration and evaporation of water, to be deposited on the carrier. Another procedure may be applied in which previously a vanadium compound or both a vanadium compound and a phospho­ rus compound are deposited on the carrier, followed by heat treatment at not less than 100°C, and then a palladium salt and a copper salt are deposited by the above-mentioned procedure. The mechanism of action of the vanadium compound added in accordance with the invention is regarded as expressed by the series of reaction equations: In this way, the temperature of the catalyst is raised through the influence of oxidation heat of CO, accompanied by thermal decomposition in part of palladium chloride and volatilation of hydrogen chloride (HCl), with the resulting conversion into palladium hydroxide (Pd(OH)₂), which com­ bines with vanadium oxide (V₂O₅) to form a redox pair. In this way, oxidation proceeds following the reaction equations (5) through (7). The long-term duration of CO oxidating activity is understood as coming from the fact that the activity of the redox pair consisting of palladium chloride-copper chloride reduces as the result of volatilation of hydrogen chloride but the reduction is compensated by the newly produced redox pair consisting of palladium hydroxide and vanadium oxide. Addition of phosphorus compound as well as vanadium oxide can further promote the above-mentioned effect. Fig. 1 is a graph showing change with the passage of time in CO oxidizing activities of different catalysts acco­ rding to the invention. The invention will be described more fully by way of examples which reference to the accompanying drawings herei­ nafter: (1) Preparation of catalysts Example 1 Palladium chloride, cupric chloride and ammonium metavanadate were used to prepare 1300 ml of an aqueous solution containing 7 g as palladium, 44 g as copper base and 5 g as vanadium. In the resulting preparation, 1 Kg of γ-alumina having particle sizes of 2.38-1.19 mm (8-14 meshes) was immersed for 5 hours. Then water was evaporated at 120°C in a through-flow dryer with occasional agitation. After the drying lasting 12 hours, the resulting catalyst (A) according to the invention was taken out of the dryer. Example 2 By using ammonium metavanadate 1300 ml of an aqueous solution containing 5 g of vanadium ion, was prepared. In the obtained preparation, 1 Kg of γ-alumina having particle sizes of 2.38-1.19 mm (8-14 meshes) was immersed for 4 hours. Then water was evaporated at 130°C in a through-flow dryer with occasional agitation for 12 hours, followed by additional thermal trea­ tment at 500°C for 2 hours. On the resulting V₂O₅ carrying γ-almina, the same quantity of palladium chloride and cupric chloride were deposited by similar procedure to that of Example 1, thus catalyst (B) according to the invention was obtained. Example 3 A honeycomb structure (diameter: 50 mm, height: 8.15 mm, no. of cells per cm²: 44 per inch₂: 112) of cordierite with a γ-alumina layer on the surface was immersed in 500 ml of 0.1 mol/l NH₄VO₃ aqueous solution for 3 hours, followed by drying at 120°C. The same immersion and drying were repeated three times. Then 2 hours' thermal treatment at 500°C was made. In addition, the resulting V₂O₅ carrying honeycomb structure was immersed in 500 ml of an aqueous solution containing palladium chloride (0.1 mol) and cupric chloride (1.0 mol). After the immersion lasting 3 hours, the honeycomb structure was removed up, followed by drying at 150°C, and thus anot­ her catalyst (C) was obtained. Example 4 Ammonium metavanadate and phosphoric acid were used to prepare 1300 ml of an aqueous solution containing 5 g of vanadium ion and 3 g of phosphorus ion. In the ob­ tained preparation, 1 Kg of γ-alumina having particle sizes of 2.38-1.19 m (8-14 meshes) was immersed for 4 hours, followed by thermal treatment in the same way as in Example 2. On the resulting V₂O₅-carrying γ-almina, the same quantity of palladium chlo­ ride and cupric chloride were deposited by the similar procedure to that of Example 1. Thus catalyst (D) according to the invention was obtained. Example 5 In the same way as in Example 1 except for omit­ ting ammonium metavanadate (NH₄VO₃), a control catalyst (E) was obtained. (2) Determination of CO oxidizing activity The CO oxidizing activities of catalysts (A), (B), (C) and (D) according to the invention and control catalyst (E) were determined in the following procedure: A sample of catalyst (160 ml) was packed in a glass tube of 50 mm in inner diameter. Through the catalyst column, air (relative humidity: 95%, temperature; 25°C) having CO concentration of 1.0% by volume was passed at a flow rate of 32 l/min. In this state, CO concentration was measured at the outlet with a non-dispersion type infrared spectrophotometer. As seen from Fig.1, compared with the control vanadium-­ free catalyst (E), any of the catalysts according to the invention (A), (B), (C), (D) have proved to be extremely durable without substantially decreasing in CO oxidizing activity throughout a long-term use. As described above, the CO oxidizing catalyst according to the invention, which is a modified redox catalyst which contains a redox catalyst consisting of palladium chloride and copper chloride in combination with a vanadium compound alone or both a vanadium compound and a phosphorus compound, not only has a high CO oxidizing activity but also is marke­ dly superior in duration of the CO oxidizing activity.

Claims: 1. A carbon monoxide oxidizing catalyst com­ prising a porous carrier, on said carrier a palladium salt and a copper salt as main active components and a promotor consisting of a vanadium compound or of a vanadium compound and a phosphorus compound. 2. A carbon monoxide oxidizing catalyst defined in claim 1, wherein said carrier is γ-alumina. 3. A carbon monoxide oxidizing catalyst defined in claim 1, wherein said carrier is silica-alumina. 4. A carbon monoxide oxidizing catalyst defined in claim 1, wherein said carrier is a zeolite. 5. A carbon monoxide oxidizing catalyst defined in any of the claims 1 to 4, wherein said carrier is a honeycomb-structured material. 6. A carbon monoxide oxidizing catalyst defined in claim 1 or 5, wherein said carrier is a sponge-­ tissue ceramic. 7. A carbon monoxide oxidizing catalyst defined in any of the claims 1 to 6, wherein said palladium salt is selected from palladium chloride, palladium sulfate or palladium nitrate. 8. A carbon monoxide oxidizing catalyst defined in any of the claims 1 to 7, wherein said copper salt is selected from cupric chloride, copper sulfate or copper nitrate. 9. A carbon monoxide oxidizing catalyst defined in any of the claims 1 to 8, wherein said vanadium compound is selected from ammonium metavanadate, sodium vanadate or vanadium oxide. 10. A carbon monoxide oxidizing catalyst defined in any of the claims 1 to 9, wherein the ratio of said palladium salt to said carrier is 0.01-0.2 m mol/g. 11. A carbon monoxide oxidizing catalyst defined in any of the claims 1 to 10, wherein the ratio of said copper salt to said carrier is 0.1-2.0 m mol/g, preferably 0.4-1.0 m mol/g. 12. A carbon monoxide oxidizing catalyst defined in any of the claims 1 to 11, wherein the ratio of said vanadium compound to said carrier is 0.1-3.0% by weight, preferably 0.5-1.5% by weight. 13. A carbon monoxide oxidizing catalyst defined in any of the claims 1 to 12, wherein the ratio of said phosphorus compound to said carrier is 0.1-1.0% by weight.

Inventors: HORII, IKUO, ICHINOSE, HIROSHI NIHON TABAKO TSUCHIHASHI, ISHIGURO, SHIGEO, MATSUSHITA, HAJIME NIHON TABAKO, MIZUSAKI, SHIGENOBU NIHON TABAKO, SUGIMORI, KENICHIRO, YAMAMOTO, MASARU
Applicants: JAPAN TOBACCO INC., TOPY INDUSTRIES, LIMITED
Application year: 1986
Main classification: B01D53
IPC codes: B01D53, B01J23, B01J27