PHOTODEGRADANT COMPOSITIONS AND PHOTDEGRADABLE POLYMER COMPOSITIONS MADE THEREFROM

Abstract: A photodegradation composition for incorporation into polymer (such as polyethylene) contains a photodegradant complex of copper and a complex-forming compound (such as copper·2,4-pentadione) and a photostabilizer complex of zinc and a dithio acid (such as zinc·dimethyldithiocarbamate). Polymers containing the composition are synergistically photodegradable and synergistically process stable. The polymers are useful in agricultural and packaging applications (such as clear films for consumer packaging).

Description: This invention relates to photodegradant compositions comprising a photodegradant compound and a photostabilizer compound. This invention also relates to photodegradable polymer composi­ tions comprising a polymer and a photodegradant composition. Such compositions are known from GB 1 586 344. That patent addresses the problem of manufacturing photodegradable polymer compositions. In the manufacture of polymeric materials such as polyolefins, manufacturers have typically attempted to improve the light sta­ bility of their products so that they may be used in outdoor application without premature failure. However, for some applica­ tions, improved light stability is not desired. In fact, in some instances it is desired to have the polymer photodegrade faster than if no additives were present. One such example in agriculture is the use of polyethylene sheets to prevent weed growth and water evaporation between rows of plants. If the polymer is light-stable, it will be necessary to manually remove the sheets prior to plowing. But, if the polymer becomes brittle due to the action of sunlight (principally the ultra-violet light), the sheets may be plowed into the soil where they will be biodegraded. Another example is packaging materials. Most packaging materials are used for a very short period of time, after which they are discarded, causing litter or other disposal/environmental pro­ blems. Untreated polymers may remain in the environment for very long periods of time (perhaps hundreds of years) if their ultra-­ violet exposure is brief and they are then buried. However, if they are treated with a photodegradant, the embrittlement time will be reduced, for example, from 3 to 5 years for untreated plastics, to only several months for plastics containing photo­ degradants. Thus, such a treated plastic will, after a relatively brief ultra-violet exposure, become photodegraded to the point that it may be biodegraded. GB 1 586 344 is directed specifically at formulating a photo­ degradable polymer composition which has a controllable and predictable ultra-violet life, followed by rapid photodegrada­ tion. The solution presented by this patent is to blend carefully controlled ratios of a photodegradant complex of an organic ligand with iron, manganese, or cerium, with a photostabilizer complex of the same or different ligand with nickel, cobalt, or copper. These blends are then incorporated into the polymer to achieve the desired photo-stable lifetime. While this system appears to be operable, it suffers from several disadvantages including undesirable color, corrosion of processing equipment, polymer degradation, lack of polymer compatability, and loss of polymer mechanical properties. The present invention does not have these disadvantages, and is characterized in that the photodegradant compound is a complex of copper and a ketone having an α-hydrogen available such that the ketone may form a keto-enol tautomer and the photostabilizer compound is a complex of zinc and an alkyldithio acid; the photo­ degradant and photostabilizer compounds being present in a ratio of 5:95 to 95:5. The present invention is advantageous in that polymer com­ positions containing the photodegradant compositions, among other things, do not have undesirable color, have excellent photode­ gradation properties, and are process stable. Considering more generally the state of the art, several other patents are relevant. US 3 454 510 discloses the general concept of incorporating photodegradants into opaque polymer films for agricultural use. This patent mentions that useful pro-oxidants include the acetyl­ acetonates of manganese, cobalt, chromium, copper, and vanadium. No mention is made of adding photostabilizers. US 4,048,410 addresses the problem of photodegradant induced pro­ cessing instability by incorporating into the polymer, not the photodegradant itself, but rather incorporating precursors (ligands) of the photodegradant with the expectation that the precursor will react with a suitable metal (no metals are speci­ fied, but iron is implied by a reference to rusty metal) in the environment to form the desired degradant. However, for this approach to be successful outside the laboratory requires that a suitable source of metal ions be made available in contact with the article to be degraded. GB 1 356 107 (referred to in the aforementioned GB 1 586 344) discloses a number of photodegradant complexes, either or both of the complex or the complexing agent being an antioxidant. This patent discloses a mixture of zinc dibutylthiocarbamate and iron dibutylthiocarbamate. The corresponding US Patent (US 4 121 025) discloses a mixture of zinc dibutyldithiocarbamate and copper stearate. One component of the invention is a photodegradant compound. By the term "photodegradant compound" is meant a compound which, when blended with a polymer, will cause the polymer to degrade, upon exposure to light, faster than if the compound were not pre­ sent. The photodegradant compound should be compatable with the other components. By the term "compatable" is meant that the com­ pound may be blended with the other components without signifi­ cant separation or destructive reaction of the components. While this does not require that the components be soluble in one an­ other, they should at least be capable of forming a uniform, finely dispersed mixture. Specifically, the photodegradant compound is a complex of copper and a ketone having an α hydrogen available such that the ketone can form a keto-enol tautomer. Such suitable ketones include 2-­ hydroxy-2-methyl-1-phenyl-propan-1-one and hydroxycyclohexyl phenyl ketone Desirably, the ketone has more than one carbonyl moiety, more desirably two carbonyl moieties (a diketone). Suitable ketones having more those one carbonyl group include those having the structures and Preferred diketones have the structure wherein each R is independently a C₁ to C₁₈ organic moiety, desirably a C₁ to C₁₂ alkyl or aralkyl moiety. Preferably each R is a C₁ to C₆, still more preferably a C₁ to C₃, still more pre­ ferably a C₁ to C₂, and most preferably a C₁, alkyl moiety. R' is desirably hydrogen or a C₁ to C₁₈ organic moiety, preferably hydrogen. Of course, the organic portions of the ketone may con­ tain a variety of substitutions, and mixtures of ketones may be used. The most preferred photodegradant compound is copper·2,4-­ pentanedione (= copper acetylacetonate). A second component of the invention is a photostabilizer com­ pound. By the term "photostabilizer compound" is meant a compound which will cause a polymer to which it is added to degrade, upon exposure to light, less than if the compound were not present. The photostabilizer compound should be "compatable" with the other components, as defined above. Specifically, the photostabilizer compound is a complex of zinc and a dithio acid. By the term "dithio acid" is meant an organic compound having a dithio acid moiety of carbon, phosphorous, or nitrogen (preferably carbon or phosphorous). Suitable dithio acids include those having the structure wherein R is a C₁ to C₂₂ organic moiety. Desirable dithio acids are dialkyldithiocarbamic acids, dialkyl­ dithiophosphoric acids, and alkylxanthic acids, with dialkyldi­ thiocarbamic acids being greatly preferred. In the alkyldithio acids each alkyl moiety is desirably a C₁ to C₂₂, more desirably a C₁ to C₆, preferably a C₁ to C₃, more preferably a C₁ to C₂, and most preferably a C₁, alkyl moiety. The most preferred photostabilizer compound is zinc dimethyldithiocarbamic acid. The photodegradant compound and photostabilizer compound are pre­ sent in a ratio such that when blended with a polymer, the poly­ mer exhibits a synergistic photodegradation effect and a syner­ gistic process stability effect. By the phrase "synergistic photodegradation effect" is meant that the polymer is more photodegradable than would be expected from an averaging of the effects of the presence of the photodegradation and photosta­ bilizer compounds alone. By the phrase "synergistic process sta­ bility effect" is meant that the polymer is more process stable than would be expected from an averaging of the effects of the presence of the photodegradation and photostabilizer compounds alone. While the precise ratios to be used may vary with factors such as the molecular weight of the compounds, generally the two compounds will be present in a ratio of 95:5 to 5:95, desirably 90:10 to 10:90, preferably 70:30 to 30:70, more preferably 60:40 to 40:60, most preferably about 50:50. The practice of the invention contemplates that the photostabi­ lizer and photodegradant compounds will be added to a polymer, preferably a polyolefin. By "polyolefin" is meant a polymer of one or more ethylenically unsaturated organic compounds, desira­ bly principally (e.g.: at least 50 mole %) α-olefins (1-alkenes). Preferably polymer is polyethylene, polypropylene, or poly(1-­ butene); more preferably polyethylene or polypropylene; still more preferably polyethylene, and most preferably low density polyethylene. The polymer is preferably free of groups such as halogens, which could interfere with the action of the photode­ gradant composition. The photostabilizer and photodegradant may be combined and added to the polymer, or may be separately added, the former being preferred. The compounds may be blended with the polymer using conventional means such as are well known in the art. The photodegradant composition (i.e.: the photodegradant compound and the photostabilizer compound) is present in the polymer in an amount such that the polymer exhibits a synergistic photodegrada­ tion effect and a synergistic process stability effect, as those terms have been hereinbefore defined. Although the precise quan­ tity to be used may vary with such factors as the molecular weight of the compounds and the nature of the polymer, in gene­ ral, the photodegradant composition will be present at 0.001 to 1, more desirably 0.01 to 0.1 weight percent, based on the weight of the polymer. The polymer may also contain other additives such as fillers, lubricants, dyes, pigments, anti-static agents, etc. The polymers may be used for a wide variety of applications where a photodegradant is desired, including agricultural ground covers and industrial and consumer packaging. The invention is particu­ larly suited for use in consumer packaging. This well-known appli­ cation demands a polymer that will be of high quality during the period of use (i.e. one that was not degraded during manufactur­ ing), but which will be readily photodegradable. For instance, the polymers of the invention may be used to produce clear sheets for display packages of consumer articles. In contrast, the poly­ mers of GB 1 356 107 and GB 1 586 344 would not be suitable for such a use because of their color. The polymer may be made in a variety of forms such as fibers, sheets (preferably less than 2 mm thick), and shaped articles such as bottles and other containers. The invention is further illustrated by the following examples. Example 1 Zinc dimethyldithiocarbamate was prepared by the room temperature addition and stirring of two gram moles of aqueous sodium di­ methyldithiocarbamate to an aqueous solution of a gram mole of zinc sulphate heptahydrate, causing the precipitation of a white solid which was filtered and washed with warm water (60°C). The white solid was recrystallised from n-heptane to yield fine powder in 95-97% yield. Elemental analysis, IR, and NMR spectro­ scopy data were in good agreement with literature values for zinc dimethyldithiocarbamate. Copper acetylacetonate was prepared by the room temperature in­ teraction of aqueous copper sulphate heptahydrate (19 mole) with acetyl acetone (29 moles) under rigorous stirring in the presence of sodium acetate trihydrate. A grey solid was precipitated in 98% crude yield. The solid was filtered, washed with water and vacuum dried at 50°C to a constant dry weight. Elemental ana­ lysis, IR, and NMR spectroscopy data were in good agreement with literature values for copper acetylacetonate. Low-density polyethylene (ICI, Alkathene 017/040) was compound with additives shown in Table I by mixing the composition on a two-roll mill at 120°C for 5 minutes with frequent cross-blend­ ing. The homogeneous polymer composition was then compression molded to yield polymer films in the thickness range 10-125 µm. The polymer films of a selected thickness and composition were mounted on a sheet of stiff white paper and placed in suitable sample holders for placement in a Xenotest accelerated UV exposure cabinet and the exposure time to cause polymer em­ brittlement was monitored by attenuated total reflection IR spectroscopy and by crack development, growth, and propagation. A linear co-relation between these observations and the time taken to cause embrittlement by flexing the polymer film was obtained through a series of separate experiments. Table I, illustrates the relationship between polymer composition and UV embrittlement time for a film thickness of 25 µm. Similar trends were observed at both higher and lower film thicknesses. These results show that a synergistic effect is achieved in the practice of the invention. Specifically, the data show that com­ binations of ZDC and CAA yield an embrittlement time almost as low as when CAA is used alone. This is the case even when the ZDC to CAA ratio is 9:1. The embrittlement time is less than would be expected from an averaging of the effect of the presence of ZDC and CAA alone. Example 2 The polymer compositions compounded on the two-roll mill at 120°C in Example 1, were used to determine the Melt Flow Index of the polymer under standard conditions at 190°C. The results are reported in Table II. (1) total concentration, 0.1 percent g/10 min at 190°C. Higher values mean more polymer degradation. (3) weighted average of separate values. These results show a second synergistic effect of the invention. In this example, the data show that a combination of ZDC and CAA provide processing stability which is very close to that obtained using ZDC alone. This would not be expected from an averaging of the effects of the presence of ZDC and CAA alone. Comparative Example 2 The procedure of Example 2 was repeated, using zinc and iron dibutyldithiocarbamate, as suggested by GB 1 356 107. The results are shown in Table II-C In contrast to Example 2, these data show that a combination of ZDBTC and FeDBTC have a processing degradation value equal to or worse than expected from averaging the effects of the presence of each alone.

Claims: 1. A photodegradant composition comprising a photodegradant compound and a photostabilizer compound wherein a. the photodegradant compound comprises a complex of (i) copper, and (ii) a ketone having an α hydrogen available such that the ketone may form a keto-enol tautomer. b. the photostabilizer compound comprises a complex of (i) zinc, and (ii) an alkyldithio acid; and c. the photodegradant compound and the photostabilizer compound are present in relative weight proportion of 5:95 to 95:5. 2. A composition according to claim 1 wherein the ketone is a diketone. 3. A composition according to claim 2 wherein the diketone has the structure wherein each R is independently a C₁ to C₂₂ organic moiety. 4. A composition according to claim 3 wherein each R is a C₁ to C₆ alkyl moiety. 5. A composition according to claim 4 wherein the photodegradant is copper acetylacetonate. 6. A composition according to any one of the preceding claims wherein the photostabilizer is a dialkyldithiocarbamic acid. 7. A composition according to claim 6 wherein the photostabilizer is zinc dimethyldithiocarbamate. 8. A photodegradable polymer composition comprising a polymer and from 0,001 to 1 weight percent of a photodegradant composition according to any one of the preceding claims. 9. A photodegradable polymer composition according to claim 8 wherein the polymer is selected from the group consisting of polyethylene, polypropylene and poly(1-butene). 10. A photodegradable polymer composition according to claim 8 or 9 wherein the composition is m the form of a sheet having a thickness of less than 2 mm.

Inventors: COORAY, BULATHSINHALAGE BOYD
Applicants: AKZO N.V.
Application year: 1986
Main classification: C08K5
IPC codes: C08K5