LABELLED MACROMOLECULES; A PROCESS FOR THEIR PREPARATION AND THEIR USE FOR IMMUNOLOGICAL OR IMMUNOCYTOCHEMICAL ASSAYS

Abstract: Use of inorganic crystalline phosphors as labels for macromolecules, such as, for example, antibodies. Although covalent bonding is possible, the macromolecules are preferably adsorbed physically onto the phosphors. The phosphors should preferably have a particle size of between 0.02 and 5 mu m, most preferably between 0.1 and 1 mu m.

Description: Title: Labelled macromolecules; a process for their preparation and their use for immunological or immunocytochemical assays. The invention relates to macromolecules, such as proteins, including immunologically specific antibodies, lipoproteins, polynucleotides, etc., provided with luminescent labels. The invention further relates to a process for preparing macromolecules, such as proteins, including immunologically specific antibodies, lipoproteins, polynucleotides, etc., providedwith luminescent labels, and also to the use of labelled immunologically specific macromolecules, such as antibodies, for immunological or immunocytochemical assays. In biomedical examinations, use is often made of the specific immunological reaction between antigen and (monoclonal) antibody. To render visible and quantify this reaction, the antigen or the antibody is provided with a label. The most common labels are enzymes that can be demonstrated with specific colour reactions, luminescent compounds, and radioactive isotopes. Prominent among luminescent labels are photoluminescent compounds, such as fluorochromes, although the suitability of bioluminescents and chemiluminescents has been demonstrated (Pratt et al., 1978; Simpson et al., 1979; Hastings and Wilson, 1976). Apparatus for the qualitative and/or quantitative processing of fluorescence signals (photons) has been greatly improved in the last few years. Single-photon- counting detection systems and highly sensitive cameras of the SIT or ISIT type (with image intensifiers) , as well as high-energetic excitation sources, such as lasers, are at present available. To increase the amount of fluorescence, new fluorochromes, such as phycobiliproteins, with a high fluorescence efficiency have been developed (Oi et al., 1983). Polystyrene or -latex micropheres, which contain thousands of fluorochrome molecules, have also been introduced as cell labels (so-called Covaspheres) (Molday et al., 1975; European Patent Application EP 0002963 (Eastman Kodak Company) , 1979) . Thanks to these improvements, the extreme sensitivity• of fluorescence studies of cells and tissues is at persent determined for the major part by the autofluorescence of the biological object and the optics used (lenses and filters) , and by undesirable excitation light from the radiation source. The auto¬ fluorescence of a single cell, measured with a microscope fluorimeter or a flow cytometer, is in the order of several thousands of fluorescein equivalents (Jong ind et al., 1979) , as a result of which the demonstration of minute amounts of macro olecule in cells and tissues by means of immunofluorescence is not optimally possible. It is especially for the demonstration of minute amounts of macromolecules, therefore that one would often opt for a method using a radioactive label. This method is sensitive, it is true, but in the case of in situ applications (e.g. autoradiography) extremely time-consuming, while in addition the necessary precautionary measures must be taken with regard to working conditions and the processing of the radioactive waste. In analytical chemistry, the problem of autofluorescence can be largely avoided by using. so-called time-resolved fluorescence assays. For this method a luminescent label must be selected with a long after-glow time, such as the lanthanides europium (eu) and terbium (Tb) . After a short exciting light pulse, the- relatively fast autofluorescence (in the order of nano¬ seconds or faster) can be separated in time from the slower lanthanide fluorescence (in the order of milliseconds) The DELFIA (Delayed Fluoro Immuno Assay) system, developed • by LKB, makes use of this principle. This method has been found to be competitive in sensitivity with radioactive assays (Soini et al., 1983; Hemmila et al., 1984). One disadvantage is, however, that the * luminescent label Eu or Tb when bonded to antibodies and dissolved in water does not luminesce, or hardly so, and therefore after the reaction with the antigen-antibody must be liberated to obtain the delayed-fluorescence properties. -As a consequence, detection is only possible in solutions, and uses of this method in which localisation of the antigen at the tissue, cell or chromosomal level is required are impossible. The very low quantum efficiency of the lanthanides in aqueous solutions can be improved considerably by incorporating lanthanides such as e.g. Europium and Terbium by means of crosslinking agents into .latex particles, thereby increasing its fluorescence yield (EP 0002963; Eastman Kodak Company, 1979) . Thus prepared latex particles can be coupled to cells. It is these very cellular uses which command increasing interest, thanks to the development of molecular biology and the possibility of demonstrating one-gene and virus products in tissues and cells using specific monoclonal antibodies. The present inventors have developed a new immunological label which combines many of the advantages of the existing methods, and in addition permits localisation of the antigen- antibody complex at cell level. The invention is characterized in that the labels are inorganic crystalline phosphors. For use in biological systems, the size of the crystalline phosphors must generally not exceed 5 urn. Preferably the labels used are crystalline phosphors with a particle size of 1 urn or smaller. Because, on the other hand, the luminescence intensity decreases rapidly with decrasing size of the phosphors, the phosphors should generally have a size of 0.02 urn or larger. Preferably, the labels used are crystalline phosphors with a particle size of 0.1 urn or larger. The invention accordingly provides a material comprising a label which is a crystalline phosphor, to which the macromolecule, such as antibody, is adsorbed or chemically bonded. These phosphor labels luminesce blue, green or red (depending on the phosphor used) under a fluorescence microscope (UV excitation) or exhibit cathode luminescence in a scanning electron microscope. As their after-glow time is in the order of msec or sec, phosphor-labelled cells can be measured in accordance with the time-resolved principle with microscope-cyto fluorimeters * and flow cytometers adapted for the purpose. With regard to the nature of the inorganic crystalline phosphors, there are no limitations. All known inorganic crystalline phosphors, such as those described in Kirk-Othmer Encyclopedia of Chemical Technology, third edition. Volume 14, pp. 527 ff., and in many patent publications, and also as yet unknown inorganic crystalline phosphors are suitable for use as labels in accordance with the present invention, with their particle size being preferably reduced to 1 um or less. The use of a stable suspension of inorganic crystalline phosphors with macromolecules (antibodies) physically or chemically attached, has not been described before as (immuno)cytochemical. reagent. K. Kosak (US Patent 4000252; 1976) has mentioned the use of a phosphor- antibody complex in a new type of immunoscintillation cell for a new radioimmunoassay method. This cell consists of a support medium with organic phosphors incorporated, to which antibodies are coupled. The cell may have different physical shapes. The support medium serves as a trapping agent for the radioactively labelled or unlabelled antigen; binding of a radioactively labelled antigen induces luminescence of the phosphor in its direct vicinity, which is subsequently measured as is done in a scintillation counter. The present patent application does not relate to a solid phase consisting of an organic phosphor-antibody complex, but relates to a stable suspension of an inorganic phosphor-antibody complex, which is used as (immuno)cytochemical reagent. In 1972 L. Amante et al. have studied the properties of conjugates of immuno- globulins with the amorphous and crystalline form of tetramethyl rhodamine isothiocyanate (TRITC) . However, the fluorophore TRITC was dissolved from its various native states in water, and subsequently coupled to immunoglobulin. Before the coupling between the inorganic crystalline phosphors and the macromolecules, such as antibodies, is brought about, the phosphors, which as stated before preferably have particle sizes of 1 um or less, should preferably be subjected to a pre-treatment to provide their surface with charged groups. As a consequence the individual particles will repel each other and the formation of larger aggregates will be avoided. The nature of the charged groups is not critical. Both groups of negative charge, such as carboxylic acid groups, sulphonic acid groups, phosphoric acid groups, and the like, and positively charged groups, such as amino groups and quaternar ammonium groups, are suitable for the effect contemplated. Experiments conducted and the results achieved therein (see the example) show that, in principle, it is possible to couple antibodies to crystalline phosphors with a particle size of 1 um and smaller in such a manner that specific immunological reactions with this antibody- phosphor conjugate are possible. Of two tested method's, the adsorption of antibodies to phosphors at a pH in the vicinity of the isoelectric point (for IgG 6.6) turned out to be preferred to covalent coupling via suitable spacer molecules. The adsorption method is known per se and, among other applications, is succesfully used for coating colloidal gold spheres with antibodies, for use in the electro microscope (Geuze et al., 1981). The use of other coupling methods than the methods herein illustrated, however, is . not excluded. Immunologically positive lyphocytes are easily recognized bymeans of fluorescence microscopy with UV excitation. A major advantage is that the phosphors used do not exhibit bleaching. Crystals that have not reacted are easily distinguished as small phosphorescent dots in the background. Nevertheless, we prefer to separate the non-reacted phosphor crystals from the cells, for example, by gradient centrifugation, as a result of which a cleaner background is obtained. The relatively small crystals (about 0.2 um) can easily be removed by centrifugation, because these remain behind in the supernatant at (200-400)xg (conventional for cells) . Tests in which a density gradient was used also gave good results. The luminescence intensity of phosphor-labelled cells was high. Microscope photography required exposure periods of 1 to 5 sec. Comparable conventional fluorescence colourings of membrane components commonly result in exposure times of 30 to 60 sec, partly owing to the occurrence of bleaching. The phosphors cannot only be rendered visible to the human eye by means of the fluorescence microscope and the electron microscope. Measurements of the luminescence signal and reproduction thereof by means of a memory oscilloscope show that the time-resolved luminescence measuring principle can be used. This offers the possibility of adapting the apparatus currently available for the quantitative fluorescence analysis of tissues, cells and cell components in such a manner that the specific (slow) phosphorenscence signals can be separated from the interfering (fast) background fluorescence signals and from possibly reflected excitation light. An additional advantage is that the background luminescence of biological objects such as cells virtually exclusively concerns "fast" fluorescence processes. The apparatus used for the quantitative analysis of cells mainly concerns microscope fluorimeters and flow cytometers. The detection systems of these fluorimeters mostly consist of photomultiplier tubes, photodiodes, television cameras, or arrays of detectors. With a relatively simple electronic circuit, a time delay can be realized between the moment of excitation (in pulsed form) and the moment when the (delayed) luminescence signal is measured. This principle can be used in systems in which the entire microscopic object is bodily excited, but also in systems where the object is scanned point by point by a small excitation light spot (laser scanning, incremental table scanners) . In flow systems in which the excitation of cells flowing past and the measurement of luminescence take place along different optical paths, the time delay can also be realized by positioning the lens registering the luminescence signal somewhat downstream. For example, in a FACS type cell sorter a delay of 100 microseconds can be realized by focussing the detection lens 1 cm lower on the liquid stream. Uses of phosphor-labelled immunological reagents In principle, phosphor conjugates are suitable for use in all applications where fluorochrome, enzyme, or isotope-labelled i muno-reagents are used. Examples are ELISA and RIA techniques for demonstrating and assaying antigens in solution, immunological methods for the detection of macromolecules in filter blots, and immunocytochemical methods for the study of morphologically intact tissues and cells. As regards the cytochemical application, the accent will be on demonstrating superficial antigens, as phosphor particles of 0.1 - 1.0 um cannot easily penetrate cell membranes. By using phosphors, several parameters can be studies and measured at the same time. Not only is it possible to generate three spectrally separate colours (blue, green, red) by means of UV or electron excitation, but phosphors with different decay times can be used, by virtue of which the number of antigens to be measured at the same time can become very large. Time-resolved luminescence assays are comparable in sensitivity to radioactivity assays (Soini and Kojola, 1983) . The immunocytochemical use of phosphor conjugates basically allows a much more sensitive detection of small quantities- of macromolecules in cells. This may be of importance in both fundamental and diagnostic examination for membrane-linked one-gene proteins, viral products and differentiation antigens. In summary, it has accordingly been found that macromolecules, such as immunoglobulins can be adsorbed onto crystalline phosphors with a particle sizeι of 1 um or smaller, and that the resulting conjugates, such as phosphor-antibody conjugates, are immunologically and immunocytochemically specific and applicable. Examples of the properties of the phosphors, other than their high physico-chemical stability are that they can be rendered visible by excitation with UV light or with an electron beam, and that the luminescence of the conjugates, such as phosphor-antibody conjugates, does not decrease during excitation (no bleaching) . In addition, the luminescence belongs to the relatively slow luminescence (phosphorescence) As the luminescence decay is in the order of milliseconds, a strong suppression of autofluorescence and undesirable background reflection is possible by means of time-resolved luminescence assays, by virtue of which a high sensitivity can be achieved. The luminescence of phosphors can be observed with microscope fluorimeters and flow cytometers. These can be modified for time-resolved luminescence assays in a relatively simple manner. The use of phosphor-antibody conjugates basically makes it possible to assay a plurality of antigens simultaneously, because the luminescence of phosphors is not only well separated spectrally (blue, green, red) , but also exhibits measurable differences in decay times. The invention is illustrated in and by the following example. EXAMPLE: (a) Preparation of the phosphors. * .The starting products were two types of phosphors: a blue one*consisting of zinc sulfide (ZnS) activated with silver (Ag) , and a red one consisting of yttrium oxysulfide (Y-O-S) activated with europium (Eu) . Both were subjected to a pre-treatment comprising ball-milling the relatively large phosphors (5 - 6 um) until a crystal size of 1 um or smaller was reached. The phosphors were then treated with polyfunctional polymers, including carboxylic acid, amino, and sulphonic acid groups. The slurry was alkaline stabilized to final pH 9.8 - 10.0. The ultimate density of the prepared phosphor slurries was 150 g/1. A slight degree of (reversible) aggregation of the crystals was, if necessary, remedied by treating the slurry ultrasonically for 1 minute (energy 40W) . (b) Preparation of the phosphor-antibody conjugates. Two methods were tested: 1) The covalent coupling of phosphors containing carboxyl groups among others, to antibodies by means of a spacer of ε-aminocapronic acid introduced with water- soluble carbodiimide (EDC) (Molday et al. , 1975; Rembaum, 1979) . This procedure was carried out as follows: The original phosphor slurry was re-suspended in 10 ml 0.01 M ε-amino capronic acid (Merck, Darmstadt, Western Germany) and the pH was adjusted to 5.0 with HCl. Density was 25 mg/ml. In 15 minutes, 4 x 2.5 mg l-ethyl-3- (3-dimethyl- aminopropyl) carboiimide (EDC) (Serva, - Heidelberg, Western Germany) was added. The reaction period was 2 hours at 4 C. Thereafter the crystals were centrifuged (10 minutes, 1200 x g) , and washed 3 times with 0.15 M NaCl. To 2.0 ml "phosphor slurry containing 50 mg solid, 10 mg EDC was added; 1 mg goat anti-mouse total immunoglobulin (Nordic, Tilburg, The ' Netherlands) was dissolved in 100 ul 0.15 M N ' aCl and slowly added in about 50 minutes. The reaction was carried out at 4 C, with slow stirring for 2 hours. The reaction was then stopped with 0.2 ml 0.1 M glycine in H 2 0, and the crystals were washed 3 times with cold 0.15 % NaCl solution (phosphate-buffered) (pH 7.2 - 7.4) . 2) Coupling via strong ionic binding (adsorption) . The original phosphor slurries were diluted in 0.9 % NaCl - 0.15 M HEPES buffer (9 : 1; pH 7.4) to a density of 0.5 g/1. With careful stirring, goat anti-mouse total immunoglobulins (Nordic, Tilburg, The Netherlands) dissolved in the same buffer were added to 1 ml crystal slurry, final concentrations ranging from 0.25 - 0.005 mg/ml. Crystal aggregates were re-suspended by an ultrasonic treatment (at 4 C) , for 1 minute, 40W energy. (c) Immunocytochemical reactions with phosphor-antibody conjugates. The phosphor conjugates prepared by the methods described above were tested for Ficoll-isopaque isolated human mononuclear cells marked with a mouse Leu 3a monoclonal antibody against T helper/inducer cells (Becton Dickinson, Mountain View, CA) . To 1 ml cell slurry in 0.9 % NaCl - 0.15 M HEPES (9 : 1; pH 7.4) containing 1 million of cells, 150 ul Leu 3a (1 : 100) was added. The cells were incubated at room temperature for 30 minutes and washed 3 times with medium. Subsequently, to 1 ml cell suspension, 5 - 10 ul phosphor-antibody conjugate was added (density 0.5 %) . The reaction period was 15 minutes at room temperature. The cells were then centrifuged at 150 g for 10 minutes, carefully re-suspended, and"washed with medium. There was also prepared a BSA-phosphor conjugate for control purposes. (d) Fluorescence-microscopy of phosphors and phosphor- antibody-labelled cells. The phosphors and phosphor-labelled cells were inspected with a fluorescence microscope (Zeiss, Oberkochen, Western Germany) , fitted with a HBO 50W Mercury lamp and a filter set for excitation with UV light (2 mm UG 1-TK 400) An LP 420 filter served as an emission-filter for the blue phosphor crystals and an LP 590 filter for the red phosphor crystals (Schott, Mainz, Western Germany). The objective used was a Zeiss Neofluar 63 X, N.A. 1.25 phase-contrast lens. Total magnification was 630 X. The phosphors were also inspected with a scanning electron microscope with a fluorescence-illuminator built-in in the vacuum chamber (Leitz, Wetzlar, Western German) (Ploem and Thaer, 1980). This system makes it possible to view the cathode luminescence of the phosphors generated by the electron beam with the high-aperture fluorescence optics. Emission filters and objective were the same as decribed above. (e) Luminescence assays of phosphor crystals by means of microscope photometry and flow cytometry. To study the slow luminescence phenomena of the phosphors in the time, the fluorescence microscope was fitted with a 1000W Xenon flash lamp (duration of pulse about 6 microseconds) . The luminescence signals were measured with a Zeiss SF microscope-photomultiplier and displayed on a Hewlett Packard 1744A memory oscilloscope. The measuring microscope was interfaced to a PDP 11 micro¬ computer (Digital Equipment), for automatic control of the Xenon flash lamp and data handling. A program was written for "time-resolved" luminescence measurements of immunophosphor labelled lymphocytes. Flow cytometry of phosphor crystal slurries was conducted with a FACS IV cell sorter (Becton Dickinson, Mountain View, CA) , fitted with an argon ions laser tuned to 100 UV (350 - 360 nm) . Luminescence was measured using an LP 420 and an LP 590 emission filter for the flue and red phosphor crystals, respectively. The second flow cytometer used was an ICP 22 (Ortho Diagnostics) with an HBO 100 lamp as the excitation light source and fitted with a filter set for UV excitation. The emission filters were the same as described for the FACS IV experiments. (f) Results The two different methods of preparing phosphor- antibody conjugates were compared. The covalent coupling of phosphor crystals to immunoglobulins (method 1) led to strong irreversible aggregation of the crystals that could not be remedied with ultrasonic treatment. Consequently, the yield of unreacted antibody-coupled crystals was very low. As a result the immunocytochemical results of the experiments with Leu-3a-marked lymphocytes were not optimal. Phosphor-marked lymphocytes were observed, it is true, but the major part of the cells turned out to be in large conglomerates of cells and crystals. Method 2, the adsorption of protein onto phosphor crystals was found not only to be simpler to perform, but additionally led to significantly better results. Specific colouration of the T helper/inducer cell with phosphor-antibody conjugates was observed. The immunological controls used, i.e. mononuclear cells not treated with Leu 3a gave no appreciable reaction with the goat anti-mouse Ig coupled phosphor. Incubations of• uncharged phosphor crystals with cells gave no bonding. Furthermore, a BSA phosphor conjugate also prepared for control purposes did not result in significant colouration with mononuclear cells (whether or not marked with Leu 3a) . In all fluorescence microscopy studies, phase- contrast microscopy was used to identify and exclude aspecifically labelled monocytes. Time-resolved luminescence measurements of immunophosphor labelled cells showed at least a 1 decade improved signal to noise ratio (luminescence contrast) in comparison to conventional cytofluorometry. The luminescence intensity of the crystals, generated by a Xenon flash lamp was large enough for it to be measured with a Zeiss Photometer microscope and to record the luminescence decay in the time via a memory oscilloscope. The -half-life of the luminescence was in the order of magnitude of milliseconds. It was possible to detect the luminescence of the individual phosphor crystals with flow cytometry (both with laser excitation on the FACS IV, and HBO 100 excitation on the ICP 22) . REFERENCES. 1) Pratt JJ, Woldring MG, Villerius L: Chemiluminescenc linked immunoassay. J Immunol Meth 21 : 129 : 184, 1978 2) Simpson JSA^ Campbell AK, Ryall MET, Woodhead J: A stable chemiluminescent-labelled antibody for immunological assays. Nature 279: 646 - 647, 1979 3) Hastings JW, Wilson T: Bioluminescence and chemiluminescence. Photochem Photobiol 23: 461 - 473, 1976 4) Oi VT, Glaser AN, Stryer L: Fluorescent phycobiliprotein conjugates for analysis of cells of molecules. J Cell Biol 93: 981, 1982 5) Molday RS, Dreyer WJ, Rembaum A, Yen SPS: New immunolatex spheres: visual markers of antigens on lymphocytes for scanning electron microscopy. J Cell Biol 64: 75 - 88, 1975 6) Jongkind JF, Verke k A, Visser WJ, " van Dongen JM: Isolation of autofluorescent "aged" human fibroblasts ' by flow sorting. Exp Cell Res 138: 409 - 417, 1982 7) Soini E and Kojola H: Time-resolved fluorometer for lanthanide chelates-A new generation of nonisotopic immunoassays. Clin Chem 29: 65: 68, 1983 8) Hemmila, Dakubu S, Mukkala VM, Siitari H, Lowgren T: Europium As a label in time resolved immunofluorometric assays. Anal Biochem 137: 335 - 343, 1984 9) Rembaum A: Microspheres as immunoreagents for cell identification. In: Flow cytometry and sorting. Eds. Melamed MR, Mullaney PF, Mendelsohn ML, p 335 - 347, 1979 10) Ploem JS, Thaer JS: Luminescence studies with an integrated instrument permitting SEM and fluorescence microscopy of the same specimen. Proc Roy Microsc Soc 15: 9 - 10, 1980 11) Geuze HJ, Slot JW, van der Ley PA, Scheffer RCT: Use of colloidal gold particles in double labelling immuno- electron microscopy of ultrathin frozen tissue section. J Cell Biol 89: 653, 1981 12) A ante L et al: Conjugation of immunoglobulins with tetramethyl rhodamine isothiocyanate. Comparison between the amorphous and the crystalline fluorochrome. J Immunol Methods 1(3): 289 - 301, 1972 13) European Patent Application 0002963 Eastman Kodak Company (July 1979) : Aqueous stabilized fluorescent labels, proteins labelled therewith and methods of use. 14) US Patent US-A-4000252. K. Kosak (december 1976): Immunoscintillation cell.

Claims: C L A I M S 1. Macromolecules, such as proteins, including immunologically specific antibodies, lipoproteins, poly¬ nucleotides, etc., provided with luminescent labels, characterized in that the labels are inorganic crystalline phosphors. 2. Macromolecules as claimed in claim 1, characterized in that the labels are crystalline phosphors with a particle size of 5 um or less, preferably 1. um or less. 3. Macromolecules as claimed in claim 1 or 2, characterized in that the labels are crystalline phosphors with a particle size of 0.02 um or more, preferably 0.1 um or more. 4. A process for preparing macromolecules, such as proteins, including immunologically specific antibodies, lipoproteins, polynucleotides, etc., provided with luminescent labels, characterized by using inorganic crystalline phosphors as the labels. 5. A process according to claim 4, characterized by using as the labels crystalline phosphors with a particle size of 5 um or less, preferably 1 um or less. 6. A process according to claim 4 or 5, characterized by using as the labels crystalline phosphors having a particle size of 0.02 um or more, preferably 0.1 um or more. 7. A process as claimed in any of claims 4 - 6, characterized in that the macromolecules are bonded to crystalline phosphors by physical adsorption. 8. A process according to claim 7, characterized in that the bonding is realized at a pH in the vicinity of the isoelectric point of the macromolecules. 9. A process as claimed in any of claims 4 - 6, characterized in that the macromolecules are covalently bonded to the crystalline phosphors via spacer molecules. 10. A process as claimed in claim 9, characterized in that the bonding is realized via a spacer of ε-aminocapronic acid introduced by means of water-soluble carbodiimide. 11. A process as claimed in any of claims 4 - 10, characterized in that the crystalline phosphors are subjected to a pre-treatment to provide their surface with charged groups. 12. The use of marked immunologically specific macromolecules, such as antibodies, as claimed in any of claim 1 - 3, for immunological or immunocytochemical assays. 13. The use as claimed in claim 12 in fluorescence microscopy and flow cytometry with UV excitation or scanning electron microscopy with electron excitation. 14. ' The use as claimed in .claim 12 in time-resolved luminescence assays. 15. A method of simultaneously demonstrating different antigens in a biological preparation, characterized by treating the preparation simultaneously or successively with different immunologically specific macromolecules as claimed in any of claims 1 - 3, each kind of immunological specific macromolecule being provided with a different kind of crystalline phosphor, and distinguishing the kinds of phosphors on the ground of their spectral characteristics or luminescence decay times.

Inventors: PLOEM JOHAN SEBASTIAN, SLATS JOHANNES CORNELIS MARIA, TANKE HENDRIKUS JOHANNES, PLOEM, JOHAN, SEBASTIAN, SLATS, JOHANNES, CORNELIS, MARIA, TANKE, HENDRIKUS, JOHANNES
Applicants: UNIV LEIDEN, RIJKSUNIVERSITEIT LEIDEN
Application year: 1986
Main classification: G01N33
IPC codes: G01N33