PROCESS FOR PREPARATION OF HYDROGEN-ION-EXCHANGED DEALUMINATED MORDENITE

Abstract: Hydrogen ion-exchanged dealuminated mordenite hav­ ing a reduced alumina content is advantageously prepared by filtering a crystallization slurry composed of a crystalli­ zation mother liquor and synthetic sodium type mordenite and obtained when the crystallization is completed, through a filter to form a wet cake layer of the sodium type morde­ nite; passing through the cake layer an aqueous solution of a mineral acid having a concentration of 0.1N to 5N; and then, washing the cake layer.

Description: The present invention relates to a process for the preparation of hydrogen ion-exchanged mordenite having a reduced aluminum content. Zeolite is a generic term for crystalline aluminosilicates and has a chemical composition represented by the following formula based on Al₂O₃: M₂ / n O·Al₂O₃· x SiO₂· y H₂O wherein M represents a cation having a valency of n , x is a number of at least 2 and y is a number of at least 0. Mordenite having a five-membered oxygen ring is a zeolite having an x , that is, an SiO₂/Al₂O₃ molar ratio, of at least 10, and mordenites with the SiO₂/Al₂O₃ molar ratio of about 10 to about 30 are now synthesized. Mordenite is characterized by high heat resistance and high acid resistance and is widely used as an adsorbent, or a catalyst for the purification of petroleum, the petroleum chemistry and the prevention of environmental pollution. When mordenite is used as a catalyst, it is ordinarily converted to a hydrogen ion-exchanged type and it is used after adjusting the acid intensity by removing a part of the aluminum of the mordenite. This operation of removing a part of the aluminum is called dealumination. The present invention relates to a process for the preparation of dealuminated mordenite that can be used as a catalyst or a catalyst carrier. As known processes for the dealumination of mordenite, there can be mentioned a process in which hydrogen type mordenite is calcined at a temperature higher than 350°C and is then acid-treated with 6N HCl under boiling to increase the SiO₂/Al₂O₃ molar ratio to at least 55 (Japanese Examined Patent Publication No. 46-37,166), a process in which mordenite is pulverized and treated with an acid at a temperature of 60 to 100°C for 10 hours to 14 days to adjust the SiO₂/Al₂O₃ molar ratio to 10 to 45 (Japanese Examined Patent Publication No. 51-30,031), a process in which a steam treatment and an acid reflux treatment are repeated to increase the SiO₂/Al₂O₃ molar ratio to at least 35 (Japanese Examined Patent Publication No. 51-15,000), a process in which a synthesized sodium mordenite powder having an SiO₂/Al₂O₃ molar ratio of 12 to 30 is treated with an acid having a concentration higher than 1N at a temperature of 75 to 125°C to increase the SiO₂/Al₂O₃ molar ratio to at least 40 (Japanese Unexamined Patent Publication No. 46-3,714), and a process in which hydrogen type mordenite is heat-treated at a temperature of at least 600°C in the presence of steam and is then placed in contact with an acid (Japanese Unexamined Patent Publication No. 58-161,916). These known processes for the preparation of mordenite have a common problem in that an acid treatment must be carried out under severe conditions for a long time or a heat treatment such as calcination must be carried out in combination with such an acid treatment so as to attain an intended high SiO₂/Al₂O₃ molar ratio. Accordingly, these known processes are not preferred as an industrial process. We carried out research with a view to solve the foregoing problem of the known processes and providing mordenite having a reduced alumina content and a high hydrogen ion-exchange ratio by a simple acid treatment. As the result, it was found that the dealumination by a mineral acid is greatly influenced by the properties of sodium type mordenite before the acid treatment, especially by whether or not synthesized mordenite is subjected to a heat treatment such as drying or calcination. More specifically, in the case where synthesized sodium mordenite is subjected to a drying or calcination treatment before the acid treatment, little dealumination by a mineral acid is caused and the SiO₂/Al₂O₃ molar ratio cannot be increased as much as expected. On the other hand, if sodium type mordenite which has not been dried or calcined is treated with a mineral acid, the dealumination is accomplished very easily and hydrogen type mordenite having a reduced aluminum content, in which the sodium content is low, can be obtained. We have now completed the present invention based on this finding. More specifically, in accordance with the present invention, there is provided a process for the preparation of hydrogen ion-exchanged dealuminized mordenite wherein synthetic sodium type mordenite prepared by hydrothermal synthesis is treated with an acid to form hydrogen ion-exchanged mordenite having a reduced alumina content, which comprises filtering an aqueous mordenite slurry containing synthetic sodium type mordenite which is obtained without drying an as-synthesized sodium type mordenite, through a filter to form a wet cake layer of the sodium type mordenite; passing through the cake layer an aqueous solution of a mineral acid maintained at a temperature higher than 20°C having a concentration of 0.1N to 5N; for a period of at least 2 minutes and then, washing the cake layer. In synthetic sodium type mordenite used as the starting material in the present invention, the SiO₂/Al₂O₃ molar ratio is not particularly critical, and any sodium type mordenite can be used, so far as it is formed by hydrothermal synthesis. It is known that sodium type mordenite having an SiO₂/Al₂O₃ molar ratio of about 10 to about 30 can be synthesized at present, and this synthetic mordenite is generally used in the present invention. As the aqueous mordenite slurry containing synthetic sodium type mordenite which is obtained without drying an as-synthesized sodium type mordenite, there can be used a slurry just after completion of crystallization but before solid-liquid separation, which is composed of an as-synthesized sodium type mordenite and a crystallization mother liquor; a slurry diluted by adding water to the above-mentioned slurry; and a slurry prepared by separating the mother liquor from the above-mentioned slurry and then adding water to the residue. At any rate, mordenite must not be subjected to a drying treatment. Any filtering device capable of forming a layer of a cake of a mordenite crystal can be used as the filter for solid-liquid separation. For example, there can be used a belt filter, a centrifugal filter, a filter press and an Oliver filter. In order to perform the acid treatment efficiently, preferably a cake layer is formed so that the bulk density of the cake is not high. An aqueous solution of a mineral acid is used for the acid treatment. As the mineral acid, there are preferably used hydrochloric acid, nitric acid, and sulfuric acid. In the present invention, the acid concentration may be low. However, if the acid concentration is too low, the dealumination and ion-exchange are not sufficiently advanced. Namely, the intended object of the present invention is attained if the acid concentration is in the range of from 0.1N to 5N, especially from 0.5N to 3.0N. The temperature of the aqueous solution of the mineral acid is an important factor. In the acid treatment process of the present invention, at a higher temperature, the rate of dealumination of the mordenite crystal tends to increase. Accordingly, dealuminated mordenite having an intended SiO₂/Al₂O₃ molar ratio can be prepared stably with a good reproducibility by appropriately setting the temperature of the aqueous solution of the mineral acid. Since the dealumination is intended in the present invention, preferably the temperature of the aqueous solution of the mineral acid is at least 20°C. As the method for passing the aqueous solution of the mineral acid, a method in which the aqueous solution of the mineral acid incessantly flows in a certain direction among particles of the cake layer composed of the sodium type mordenite crystal is preferred because the exchange of the sodium ion with a hydrogen ion is performed at a high efficiency and the dealumination is accomplished effectively. Namely, the treatment must be carried out so that the aqueous solution of the mineral acid flows in a certain direction in the cake layer, naturally or forcibly. If the acid treatment is carried out in this manner, the time for the contact of the mordenite crystal with the aqueous solution of the mineral acid, that is, the treatment time is necessarily at least 2 minutes and is preferably at least 5 minutes, although the treatment time varies more or less according the feed rate of the aqueous solution of the mineral acid and the acid concentration. For example, if a method is adopted in which the crystallization slurry is continuously filtered through a belt filter and an aqueous solution of a mineral acid is supplied to the top of the formed cake layer and passed therethrough, the travelling speed of the belt is adjusted so that the cake layer of the mordenite crystal travels through a zone, to which the aqueous solution of the mineral acid is supplied, for a residence (contact) time of at least 2 minutes, preferably at least 5 minutes. Where the cake layer is stationary, the aqueous solution of the mineral acid is passed through this cake layer for at least 2 minutes, preferably at least 5 minutes. After the acid treatment has been conducted in the above-mentioned manner, the cake is sufficiently washed and dried, whereby hydrogen type mordenite having a reduced aluminum content, in which the amount of sodium is small, can be obtained. According to the present invention, sodium-reduced hydrogen mordenite having an intended high SiO₂/Al₂O₃ molar ratio can be prepared by a simple acid treatment without a severe treatment or complicated operation adopted in the conventional processes, such as a long-time treatment at a high acid concentration or a repetition of a calcination treatment and an acid treatment. Accordingly, the preparation process of the present invention is excellent from the industrial viewpoint. It is presumed that the reason why, according to the acid treatment process of the present invention, the dealumination for preparing hydrogen type mordenite is advanced so simply and easily in a short time, as not expected in the known processes, may be as follows. Since synthetic mordenite is prepared by subjecting a reaction mixture comprising a silica source, an alumina source and an alkali source to hydrothermal synthesis, the mother liquor left after the crystallization is alkaline. Conventionally, after solid-liquid separation, the solid is washed to remove the adhering alkali component and the washed solid is dried to obtain sodium type mordenite powder. The particle size of mordenite is very small and is smaller than several micrometers, and mordenite has in the interior thereof fine pores inherent to zeolite. Accordingly, it is very difficult to completely remove the adhering alkali component from the zeolite, and in the industrial-scale production, washing is very often insufficient. During evaporation of water by drying, this slight amount of the adhering alkali component is precipitated on the surfaces of the zeolites particles or in the interior pores to cover the surfaces or clog the pores and inhibit the contact with an acid at the acid treatment, with the result that the dealumination reaction and hydrogen ion-exchange become insufficient. In fact, we made experiments for clarifying the relationship between the degree of washing of synthetic sodium type mordenite and the rate of dealumination by the acid treatment of dry powder, and as a result, it was confirmed that the dealuminizing effect is increased with increase of the washing degree and that the dealuminizing effect is reduced by the calcination and the dealuminization is not substantially advanced if the calcination temperature is within a certain range. The process of the present invention will now be described in detail with reference to the following examples. Examples 1 through 3 1,000 g of a crystallization slurry (solid concentration = 12.9% by weight) comprising a sodium type mordenite crystal having an SiO₂/Al₂O₃ molar ratio of 14.9 and a crystallization mother liquor, which was obtained as hydrothermal synthesis was completed, was filtered under a vacuum of 53,33kPa (400 mmHg) by using a ceramic Buchner funnel (formed of a polypropylene filter fabric PF660 supplied by Nakao Filter Cloth Co.) having a filtration area of 314 cm². After the filtration, the filter cake was washed with 400 ml of warm water. Then, 2,300 ml of 0.8N HCl maintained at 20°C (Example 1), 50°C (Example 2) or 80°C (Example 3) was passed through the cake layer for 10 minutes while sucking the cake layer. After HCl had been passed, the cake layer was sufficiently washed with water and then dried. When the composition of the obtained crystal was determined by chemical analysis, it was found that the SiO₂/Al₂O₃ molar ratio was 20.8 (Example 1), 29.3 (Example 2) or 48.7 (Example 3) and in each case, the Na₂O content was lower than the detection limit of 0.05% by weight. Furthermore, in each case, the crystallinity (relative X-ray diffraction intensity) was higher than 95% based on the starting mordenite. Comparative Examples 1 and 2 A sodium type mordenited cake obtained by filtration and washing in the same manner as described in Example 1 was dried at 120°C for 4 hours (Comparative Example 1) or thus dried and then calcined in air at 500°C for 1 hour (Comparative Example 2). Then, 129 g (on the dry base) of the sodium type mordenite was formed into a slurry again by using 870 ml of water, and the slurry was filtered. Then, 2,300 ml of 0.8N HCl at 50°C was passed through the cake layer for 10 minutes, and the cake layer was sufficiently washed with water. In the obtained crystal, the SiO₂/Al₂O₃ molar ratio was 21.2 (Comparative Example 1) or 16.8 (Comparative Example 2) and the Na₂O content was 0.13% by weight or 0.25% by weight. Example 4 Hydrogen type mordenite was prepared in the same manner as described in Example 2 except that HNO₃ was used as the mineral acid instead of HCl. From the results of the chemical analysis, it was found that the SiO₂/Al₂O₃ molar ratio was 28.9, the Na₂O content was lower than 0.05% by weight and the crystallinity was 98%. Example 5 A crystallization slurry comprising a sodium type mordenite crystal having an SiO₂/Al₂O₃ molar ratio of 19.9 and a crystallization mother liquor was subjected to decantation to remove the mother liquor, and a slurry obtained by adding water to the residue was acid-treated under the same conditions as adopted in Example 1. In the obtained hydrogen type mordenite, the SiO₂/Al₂O₃ molar ratio was 30.7, the Na₂O content was lower than 0.05% by weight and the crystallinity was 99%.

Claims: A process for the preparation of hydrogen ion-exchanged dealuminized mordenite wherein synthetic sodium type mordenite prepared by hydrothermal synthesis is treated with an acid to form hydrogen ion-exchanged mordenite having a reduced alumina content, which comprises: filtering an aqueous mordenite slurry containing synthetic sodium type mordenite which is obtained without drying an as-synthesized sodium type mordenite, through a filter to form a wet cake layer of the sodium type mordenite; passing through the cake layer an aqueous solution of a mineral acid maintained at a temperature higher than 20°C and having a concentration of 0.1N to 5N for a period of at least 2 minutes; and then, washing the cake layer. A process according to claim 1, wherein the mineral acid is hydrochloric acid, nitric acid or sulfuric acid. A process according to claim 1, wherein the aqueous solution of the mineral acid has a concentration of 0.5N to 3.0N. A process according to claim 1, wherein the synthetic sodium type mordenite has a SiO₂/Al₂O₃ molar ratio of about 10 to about 30. A process according to claim 1, wherein the aqueous mordenite slurry is an aqueous slurry composed of an as-synthesized sodium type mordenite and a crystallization mother liquor. A process according to claim 1, wherein the aqueous mordenite slurry is an aqueous slurry prepared by diluting with water a slurry composed of an as-synthesized sodium type mordenite and a crystallization mother liquor. A process according to claim 1, wherein the aqueous mordenite slurry is an aqueous slurry prepared by separating a crystallization mother liquor from a slurry composed of an as-synthesized sodium type mordenite and the crystallization mother liquor, and then adding water to the residue.

Inventors: IGAWA, KAZUSHIGE, INOUE, TAKAHIKO, SAITO, HIROYUKI
Applicants: TOSOH CORPORATION
Application year: 1986
Main classification: C01B33
IPC codes: B01J29, C01B39