RADIATION-SENSITIVE RESIN COMPOSITION

Abstract: A radiation-sensitive resin composition comprises a sol­ ution of an alkali-soluble resin and a radiation-sensitive com­ pound in a solvent comprising a monooxymonocarboxylic acid ester. This composition has a high storgage stability (i.e., a very small amount of fine particles are formed during stor­ age) and is suited for use as a resist for making integrated circuits.

Description: This invention relates to a radiation-sensitive resin composition comprising a solution of an alkali-soluble resin and a radiation-sensitive compound dissolved in a solvent, which composition is sensitive to various forms of radiation such as ultraviolet rays, far-ultraviolet rays, X-rays, electron beams, molecular beams, gamma-rays, synchrotron radiation, proton beams and the like. Those resist compositions currently used in making integrated circuits generally comprise an alkali-soluble resin and a radiation-sensitive compound, and more specifically known are positive-type resist compositions comprising an alkali-soluble resin and a 1,2-quinonediazide compound. When these resist compositions comprising an alkali-soluble resin and a radiation-sensitive compound are exposed to radiation through a mask and then developed with a developer consisting of an aqueous alkaline solution, the exposed portions (in the case of the positive-type resist compositions) are dissolved in the developer, whereby a resist pattern which is faithful to the mask and has a high resolution is obtained. Therefore, resist compositions comprising an alkali-soluble resin, which have excellent resolution, have often been used in recent years during which higher integration of integrated circuits has been demanded. However, resist compositions comprising a solution of an alkali-soluble resin and a radiation-sensitive compound in a solvent have the following drawbacks: when the resist compositions are filtered through a filter having a pore diameter of, for example, 0.2µm and then allowed to stand, it happens in some cases that fine particles which are too fine to observe visually are formed in the compositions and, when compositions containing these resulting fine particles are further stored for a long period of time, precipitation may be observed. In such resist compositions, the fine particles have, in some cases, a particle diameter of at least 0.5µm. When a resist composition containing fine particles having such a large particle diameter is used to form a resist pattern of about 1µm on a wafer, the fine particles remain at the substrate portion where the resist is removed by development, resulting in a reduction of resolution. Further, when a substrate is etched through a resist pattern formed from a resist composition containing such fine particles, pinholes also appear at the substrate portion covered with the resist pattern, resulting in a reduction of yield in the manufacture of integrated circuits. A radiation-sensitive resin composition is disclosed in FR-A-2 323 170. This invention aims at solving the above-mentioned problems to provide a radiation-sensitive resin composition which gives rise to very little formation of fine particles and is suited for use as a resist. According to this invention, there is provided a radiation-sensitive resin composition comprising a solution of 100 parts by weight of an an alkali-soluble resin as defined in claim 1 and as a radiation-sensitive compound 5 to 100 parts by weight of a 1,2-quinone-diazide in a solvent, characterized in that the solvent comprises a monooxymonocarboxylic acid ester as defined in claim 1. The monooxymonocarboxylic acid ester used as the solvent in this invention is a monohydroxymonocarboxylic acid or a derivative thereof wherein the hydroxy group is alkylated or acylated represented by the formula (I): R¹O-R²-COOR³ (I) wherein R¹ represents a hydrogen atom, an alkyl group having from 1 to 3 carbon atoms or an acyl group having wherein R¹ represents a hydrogen atom, an alkyl group having from 1 to 3 carbon atoms or an acyl group having from 1 to 4 carbon atoms: R² represents an alkylene group having from 1 to 4 carbon atoms; and R³ represents an alkyl group having from 1 to 4 carbon atoms. Specific examples of the monooxymonocarboxylic acid ester include: alkyl oxyacetates such as methyl oxyacetate, ethyl oxyacetate and butyl oxyacetate; alkyl alkoxyacetates such as methyl methoxyacetate, ethyl methoxyacetate, butyl methoxyacetate, methyl ethoxyacetate and ethyl ethoxyacetate; alkyl 3-oxypropionates such as methyl 3-oxypropionate and ethyl 3-oxypropionate; alkyl 3-alkoxypropionates such as methyl 3-methoxypropionate and ethyl 3-methoxypropionate: alkyl 2-oxypropionates such as methyl 2-oxypropionate, ethyl 2-oxypropionate and propyl 2-oxypropionate; alkyl 2-alkoxypropionates such as ethyl 2-methoxypropionate, propyl 2-methoxypropionate, methyl 2-ethoxypropionate and ethyl 2-ethoxypropionate; alkyl 2-oxy-2-methylpropionates such as methyl 2-oxy-2-methylpropionate and ethyl 2-oxy-2-methylpropionate; alkyl 2-alkoxy-2-methylpropionates such as methyl 2-methoxy-2-methylpropionate and methyl 2-ethoxy-2-methylpropionate; alkyl 2-oxy-3-methylbutanoates such as methyl 2-oxy-3-methylbutanoate and ethyl 2-oxy-3-methylbutanoate; and alkyl 2-alkoxy-3-methylbutanoates such as methyl 2-methoxy-3-methylbutanoate, methyl 2-ethoxy-3-methylbutanoate and ethyl 2-ethoxy-3-methylbutanoate. Alkyl 2-oxypropionates are preferred, and methyl 2-oxypropionate and ethyl 2-oxypropionate are particularly preferred. These monooxymonocarboxylic acids may be used alone or in combination of two or more. In this invention, the solvent may be a mixture of the monooxymonocarboxylic acid ester and at least one other solvent in an amount of, for example, less than 70% by weight, preferably less than 50% by weight and more preferably less than 30% by weight, based on the weight of the mixture. Most preferably, only the monooxymonocarboxylic acid esters are used as the solvent. In this invention, the content of the solvent comprising a monooxymonocarboxylic acid ester in the radiation-sensitive resin composition is usually from 40 to 90%, preferably from 50 to 85%, by weight based on the weight of the composition. Other solvents which may be used with the monooxymonocarboxylic acid ester include: ethers such as ethylene glycol monomethyl ether, ethylene glycol monoethyl ether, diethylene glycol monomethyl ether, diethylene glycol monoethyl ether, benzyl ethyl ether and dihexyl ether; esters such as ethylene glycol monomethyl ether acetate, ethylene glycol monoethyl ether acetate, ethyl acetate, butyl acetate, benzyl acetate, ethyl benzoate, diethyl oxalate, diethyl maleate, ethylene carbonate, propylene carbonate and γ-butyrolactone; ketones such as methyl ethyl ketone, cyclohexanone, diisobutyl ketone, acetonylacetone and isophorone; fatty acids such as caproic acid and capric acid; alcohols such as l-octanol, l-nonanol and benzyl alcohol; aromatic hydrocarbons such as toluene and xylene; and so forth. These solvents may be used alone or in combination of two or more. Typical examples of the alkali-soluble resin used in this invention are alkali-soluble novolak resins (hereinafter referred to simply as "novolaks"). These novolaks can be obtained by subjecting a phenol and an aldehyde to addition condensation in the presence of an acid catalyst. Examples of the phenol include phenol, o -cresol, m -cresol, p -cresol, o -ethylphenol, m -ethylphenol, p -ethylphenol, o -butylphenol, m -butylphenol, p -butylphenol, 2,3-xylenol, 2,4-xylenol, 2,5-xylenol, 3,4-xylenol, 3,5-xylenol, 2,3,5-trimethylphenol, p -phenylphenol, hydroquinone, catechol, resorcinol, 2-methylresorcinol, pyrogallol, α-naphthol, bisphenol A, dihydroxybenzoic acid esters and gallic acid esters. Preferred as these compounds are phenol, o -cresol, m -cresol, p -cresol, 2,5-xylenol, 3,5-xylenol, 2,3,5-trimethylphenol, resorcinol, 2-methylresorcinol and bisphenol A. These phenols may be used alone or in combination of two or more. Examples of the aldehyde include formaldehyde, paraformaldehyde, acetaldehyde, propyl aldehyde, benzaldehyde, phenylacetaldehyde, α-phenylpropyl aldehyde, β-phenylpropyl aldehyde, o -hydroxybenzaldehyde, m -hydroxybenzaldehyde, p -hydroxybenzaldehyde, o -chlorobenzaldehyde, m -chlorobenzaldehyde, p -chlorobenzaldehyde, o -nitrobenzaldehyde, m -nitrobenzaldehyde, p -nitrobenzaldehyde, o -methylbenzaldehyde, m -methylbenzaldehyde, p -methylbenzaldehyde, p -ethylbenzaldehyde and p -butylbenzaldehyde. Preferred as these compounds are formaldehyde, acetaldehyde and benzaldehyde. These aldehydes may be used alone or in combination of two or more. The aldehyde is usually used in an amount of from 0.7 to 3 moles, preferably from 0.7 to 2 moles, per mole of the phenol. Examples of acid catalysts include inorganic acids such as hydrochloric acid, nitric acid and sulfuric acid and organic acids such as formic acid, oxalic acid and acetic acid. The acid catalyst is preferably used in an amount of from 1 x 10⁻⁴ to 5 x 10⁻¹ mole per mole of the phenol. In the condensation reaction, water is usually used as a reaction medium. However, when the phenol does not dissolve in an aqueous aldehyde solution, resulting in a heterogeneous reaction system at the beginning of the reaction, a hydrophilic solvent may be used as the reaction medium. Examples of hydrophilic solvents which may be used in this case include alcohols such as methanol, ethanol, propanol and butanol and cyclic ethers such as tetrahydrofuran and dioxane. The reaction medium is preferably used in an amount of from 20 to 1,000 parts by weight per 100 parts by weight of the reactants. The temperature for the condensation reaction may be varied appropriately depending upon the reactivities of the reactants, although usually it is from 10° to 200°C, more preferably from 70° to 150°C. After completion of the condensation reaction, in order to remove unreacted materials, the acid catalyst and the reaction medium which remain in the reaction system, the temperature of the reaction system is usually elevated to a value from 130° to 230°C, the volatile matter is removed by distillation under reduced pressure and the resulting molten novolak is cast on a steel belt or the like and recovered. The novolak can also be recovered by dissolving the reaction mixture in the above-mentioned hydrophilic solvent after completion of the condensation reaction; adding the resulting solution to a precipitating agent such as water, hexane or heptane to precipitate the novolak; and then separating and heat-drying the precipitate. Examples of alkali-soluble resins other than the novolaks according to claim 1 include polyhydroxystyrenes, their derivatives, styrene-maleic anhydride copolymers, polyvinyl hydroxybenzoates and carboxyl group-containing methacrylate resins. These alkali-soluble resins may be used alone or in combination of two or more. The radiation-sensitive compounds for use in this invention are 1,2-quinonediazide compounds. The nature of the 1,2-quinonediazide compound used in obtaining a positive-type radiation-sensitive resin composition of this invention is not critical, and examples include 1,2-benzoquinonediazide-4-sulfonic acid esters, 1,2-naphthoquinonediazide-4-sulfonic acid esters, 1,2-naphthoquinonediazide-5-sulfonic acid esters, 1,2-naphthoquinonediazide-6-sulfonic acid esters and 1,2-naphthoquinonediazide-8-sulfonic acid esters. Specific examples of these 1,2-quinonediazide compounds are: 1,2-quinonediazidesulfonic acid esters of (poly)hydroxybenzenes such as p -cresol 1,2-benzoquinonediazide-4-sulfonic acid ester, resorcinol 1,2-naphthoquinonediazide-4-sulfonic acid ester and pyrogallol 1,2-naphthoquinonediazide-5-sulfonic acid ester; 1,2-quinonediazidesulfonic acid esters of (poly)hydroxyphenyl alkyl ketones or (poly)hydroxyphenyl aryl ketones such as 2,4-dihydroxyphenyl propyl ketone 1,2-benzoquinonediazide-4-sulfonic acid ester, 2,4-dihydroxyphenyl hexyl ketone 1,2-naphthoquinonediazide-4-sulfonic acid ester, 2,4-dihydroxybenzophenone 1,2-naphthoquinonediazide-5-sulfonic acid ester, 2,3,4-trihydroxyphenyl hexyl ketone 1,2-naphthoquinonediazide-4-sulfonic acid ester, 2,3,4-trihydroxybenzophenone 1,2-naphthoquinonediazide-4-sulfonic acid ester, 2,3,4-trihydroxybenzophenone 1,2-naphthoquinonediazide-5-sulfonic acid ester, 2,4,6-trihydroxybenzophenone 1,2-naphthoquinonediazide-4-sulfonic acid ester, 2,4,6-trihydroxybenzophenone 1,2-naphthoquinonediazide-5-sulfonic acid ester, 2,2',4,4'-tetrahydroxybenzophenone 1,2-naphthoquinonediazide-5-sulfonic acid ester, 2,3,4,4'-tetrahydroxybenzophenone 1,2-naphthoquinonediazide-5-sulfonic acid ester, 2,3,4,4'-tetrahydroxybenzophenone 1,2-naphthoquinonediazide-4-sulfonic acid ester, 2,3,4,4'-tetrahydroxybenzophenone 1,2-benzoquinonediazide-4-sulfonic acid ester, 2,2' ,3,4' ,6'-pentahydroxybenzophenone 1,2-naphthoquinonediazide-5-sulfonic acid ester and 2,3',4',5',4,6-hexahydroxybenzophenone 1,2-naphthoquinonediazide-5-sulfonic acid ester; 1,2-quinonediazidesulfonic acid esters of bis[(poly)hydroxyphenyl]alkanes such as bis( p -hydroxyphenyl)methane 1,2-naphthoquinonediazide-4-sulfonic acid ester, bis(2,4-dihydroxyphenyl)methane 1,2-naphthoquinonediazide-5-sulfonic acid ester, bis(2,3,4-trihydroxyphenyl)methane 1,2-naphthoquinonediazide-5-sulfonic acid ester, 2,2-bis( p -hydroxyphenyl)propane 1,2-naphthoquinonediazide-4-sulfonic acid ester, 2,2-bis(2,4-dihydroxyphenyl)propane 1,2-naphthoquinonediazide-5-sulfonic acid ester and 2,2-bis(2,3,4-trihydroxyphenyl)propane 1,2-naphthoquinonediazide-5-sulfonic acid ester; 1,2-quinonediazidesulfonic acid esters of alkyl or aryl (poly)hydroxybenzoates such as lauryl 3,5-dihydroxybenzoate 1,2-naphthoquinonediazide-4-sulfonic acid ester, phenyl 2,3,4-trihydroxybenzoate 1,2-naphthoquinonediazide-5-sulfonic acid ester, propyl 3,4,5-trihydroxybenzoate 1,2-naphthoquinonediazide-5-sulfonic acid ester and phenyl 3,4,5-trihydroxybenzoate 1,2-naphthoquinonediazide-5-sulfonic acid ester; 1,2-quinonediazidesulfonic acid esters of bis[(poly)hydroxybenzoyl]alkanes or bis[(poly)hydroxybenzoyl]benzenes such as bis(2,5-dihydroxybenzoyl)methane 1,2-naphthoquinonediazide-4-sulfonic acid ester, bis(2,3,4-trihydroxybenzoyl)methane 1,2-naphthoquinonediazide-5-sulfonic acid ester, bis(2,4,6-trihydroxybenzoyl)methane 1,2-naphthoquinonediazide-5-sulfonic acid ester, p -bis(2,5-dihydroxybenzoyl)benzene 1,2-naphthoquinonediazide-4-sulfonic acid ester, p -bis(2,3,4-trihydroxybenzoyl)benzene 1,2-naphthoquinonediazide-5-sulfonic acid ester and p -bis(2,4,6-trihydroxybenzoyl)benzene 1,2-naphthoquinonediazide-5-sulfonic acid ester; 1,2-quinonediazidesulfonic acid esters of (poly)ethylene glycol di[(poly)hydroxybenzoates] such as ethylene glycol di(3,5-dihydroxybenzoate) 1,2-naphthoquinonediazide-5-sulfonic acid ester and polyethylene glycol di(3,4,5-trihydroxybenzoate) 1,2-naphthoquinonediazide-5-sulfonic acid ester; 1,2-quinonediazidesulfonic acid esters of α-pyrone type natural colouring matter having hydroxyl groups; 1,2-quinonediazidesulfonic acid esters of γ-pyrone type natural colouring matter having hydroxyl groups; and 1,2-quinonediazidesulfonic acid esters of diazine type natural colouring matter having hydroxyl groups. Besides the 1,2-quinonediazide compounds exemplified above, there can also be used the 1,2-quinonediazide compounds described in J. Kosar, "Light-Sensitive Systems", 339-352, (1965), John Wiley & Sons (New York) or in S. De Forest, "Photoresist", 50, (1975), MacGraw-Hill, Inc. (New York). When, of all the 1,2-quinonediazide compounds mentioned above, 1,2-quinonediazidesulfonic acid esters of polyhydroxy compounds having at least 3 hydroxyl groups, preferably at least 4 hydroxyl groups, in the molecule are used, the effect of the monooxycarboxylic acid esters used in this invention is exhibited most remarkably. Among these 1,2-naphthoquinonediazide compounds, we prefer 2,3,4-trihydroxybenzophenone 1,2-naphthoquinonediazide-5-sulfonic acid ester, 2,3,4,4'-tetrahydroxybenzophenone 1,2-naphthoquinonediazide-5-sulfonic acid ester, 2,2',4,4'-tetrahydroxybenzophenone 1,2-naphthoquinonediazide-5-sulfonic acid ester, ethylene glycol di(3,4,5-trihydroxybenzoate) 1,2-naphthoquinonediazide-5-sulfonic acid ester and quercetin 1,2-naphthoquinonediazide-5-sulfonic acid ester. These 1,2-quinonediazide compounds may be used alone or in combination of two or more. The amount of the 1,2-quinonediazide compound incorporated into the radiation-sensitive resin composition of this invention is usually from 5 to 100 parts by weight, preferably from 10 to 50 parts by weight, per 100 parts by weight of the alkali-soluble resin. When the amount is less than 5 parts by weight, the 1,2-quinonediazide compound absorbs the radiation applied, and hence, the amount of the carboxylic acid formed becomes insufficient, resulting in difficulty in patterning. When the amount exceeds 100 parts by weight, irradiation in a short time does not enable the whole of the 1,2-quinonediazide compound to be decomposed, which makes it difficult to achieve sufficient development with a developer consisting of an aqueous alkaline solution. The radiation-sensitive resin composition of this invention can contain a sensitizer in order to improve its sensitivity as a resist. Examples of sensitizers include 2 H -pyrido[3,2-b]-1,4-oxazin-3[4 H ]-ones, 10 H -pyrido[3,2-b][1,4]benzothiazines, urazols, hydantoins, barbituric acids, glycine anhydrides, 1-hydroxybenzotriazoles, alloxans, maleimides and the sensitizers described in, for example, Japanese Patent Publication No. 12,242/73, Japanese Patent Publication No. 35,402/73, Japanese Patent Application Kokai (Laid-Open) No. 37,641/83 and Japanese Patent Application Kokai No. 149,042/83. The amount of sensitizer incorporated into the radiation-sensitive resin composition of this invention is usually from 1 to 100 parts by weight, preferably from 4 to 60 parts by weight, per 100 parts by weight of the 1,2-quinonediazide compound. The radiation-sensitive resin composition of this invention can also contain a surfactant or the like in order to improve the coatability and striation of the radiation-sensitive resin composition as well as the developability of the radiation-exposed or radiation-unexposed portions after the formation of the dry coating. Examples of surfactants include: nonionic surfactants such as polyoxyethylene alkyl ethers (e.g., polyoxyethylene lauryl ether, polyoxyethylene stearyl ether or polyoxyethylene oleyl ether), polyoxyethylene alkyl phenol ethers (e.g., polyoxyethylene octyl phenol ether or polyoxyethylene nonyl phenol ether), polyethylene glycol aliphatic acid diesters (e.g., polyethylene glycol dilaurate or polyethylene glycol distearate); fluorine-containing surfactants such as F Top EF 301, EF 303 and EF 352 (these are products of Shin Akita Kasei K.K.), Megafac F 171 and F 173 (these are products of DAINIPPON INK & CHEMICALS), Fluorad FC 430 and FC 431 (these are products of Sumitomo 3M Limited), Asahi Guard AG 710 and Surflon S-382, SC 101, SC 102, SC 103, SC 104, SC 105 and SC 106 (these are products of Asahi Glass Co., Ltd.), and straight chain-like fluorine-containing surfactants having fluorinated alkyl groups or perfluoroalkyl groups as described in Japanese Patent Application Kokai No. 178,242/82; organosiloxane polymer KP 341 (a product of Shin-Etsu Chemical Co., Ltd.); and acrylic or methacrylic (co)polymers such as Polyflow No. 75 and No. 95 (these are products of Kyoeisha Yushi-kagaku Kogyo K.K.). These surfactants can be used alone or in combination of two or more. The amount of surfactant incorporated into the radiation-sensitive resin composition of this invention is usually 2% by weight or less, preferably 1% by weight or less, based on the weight of the solids content of the composition. The radiation-sensitive resin composition of this invention can also contain a dye or a pigment in order to visualize the resist image of the radiation-exposed portions or to reduce the adverse effect of halation when irradiating, as well as an adhesion aid in order to improve the adhesiveness to substrates. The radiation-sensitive resin composition of this invention can also contain, if necessary, a storage stabilizer, a defoaming agent and the like. The radiation-sensitive resin composition of this invention can be prepared by dissolving, in a solvent comprising a monooxymonocarboxylic acid ester, predetermined amounts of an alkali-soluble resin, a radiation-sensitive compound and optionally various additives and then filtering the resulting solution through a filter having a pore diameter of, for example, about 0.2µm. Developers which can be used for the radiation-sensitive resin composition of this invention include: aqueous alkaline solutions of inorganic alkalis, e.g., sodium hydroxide, potassium hydroxide, sodium carbonate, sodium silicate, sodium metasilicate or ammonia; primary amines, e.g., ethylamine or propylamine; secondary amines, e.g. diethylamine or dipropylamine; tertiary amines, e.g., triethylamine or methyldiethylamine; alcohol amines, e.g., dimethylethanolamine or triethanolamine; quaternary ammonium salts, e.g., tetramethylammonium hydroxide or tetraethylammonium hydroxide; and cyclic amines, e.g. pyrrole, piperidine, 1,8-diazabicyclo(5,4,0)-7-undecene or 1,5-diazabicyclo(4,3,0)-5-nonene. The use of an aqueous solution of a quaternary ammonium salt or a cyclic amine is preferred in the production of integrated circuits, when the use of a metal-containing developer is best avoided. The developer can contain an appropriate amount of a water-soluble organic solvent (e.g., methanol or ethanol) or a surfactant. According to this invention, by dissolving an alkali-soluble resin and a radiation-sensitive compound in a specific solvent, the number of fine particles formed can be reduced, which makes it possible to obtain a radiation-sensitive resin composition, the resist performance of which is hardly altered, and this effect is particularly remarkable in the case of a positive-type radiation-sensitive resin composition. This invention is further illustrated by the following Examples. EXAMPLE 1 Whilst shading from light, 244 g of a novolak obtained by the addition condensation of a cresol mixture (m-cresol/ p -cresol = 6/4 by weight) and formaldehyde, 56 g of ethylene glycol di(3,4,5-trihydroxybenzoate) 1,2-naphthoquinonediazide-5-sulfonic acid pentaester and 900 g of ethyl 2-oxypropionate were placed in a 2 liter separable flask equipped with a stirrer. The resulting mixture was stirred to form a solution. The solution was then filtered through a membrane filter having a pore diameter of 0.2 µm, and the filtrate was charged into two 500 ml glass bottles, whereby a positive-type radiation-sensitive resin composition was prepared. Immediately after its preparation, the number of fine particles contained therein was measured, using an automatic fine-particle measurement tester manufactured by HIAC/ROYCO. The number of fine particles having particle diameters of at least 0.5 µm was 15 per ml of the composition. The positive-type radiation-sensitive resin composition prepared above was coated on a silicon wafer having a silicon oxide film using a spinner. The resulting coated wafer was subjected to prebaking for 25 minutes at 90°C in an oven to form a resist layer 1.2 µm thick. Then, a test pattern mask (a product of TOPPAN PRINTING CO., LTD.) was attached to the resist layer. Using an ultrahigh pressure mercury lamp as a light source, ultraviolet rays were applied to the resist layer through a test pattern mask, and the coated wafer was developed for 60 seconds using an aqueous solution containing 2.4% by weight of tetramethylammonium hydroxide, whereby a pattern having a line width of 1.0 µm could be resolved. The yield of residual film thickness at the unexposed portion was 95%. In the same manner as above, a resist pattern was formed on a silicon wafer having a silicon oxide film. The resist pattern was subjected to post-baking for 30 minutes at 130°C and then to etching for 10 minutes at 25°C using an etchant which was a 1 : 6 (by volume) mixture of 49% HF and 40% NH₄F. The resist was stripped off and the pin hole density on the wafer was measured. The pin hole density was 0.1 flaw/cm². The pin hole density was determined by measuring the density of the flaws caused on the substrate by the pin holes of the resist. Separately, the above positive-type radiation-sensitive resin composition in a 500 ml glass bottle was stored for 1 month in a constant temperature bath kept at 40°C. After storage, the composition contained no fine particles when visually checked; the number of fine particles as measured by the automatic fine-particles measurement tester was 10 per ml of the composition and there was substantially no increase in this number. This composition after storage was evaluated for its performance as a resist in the same manner as for the composition immediately after preparation. No change in sensitivity and yield of residual film thickness were found, and there was substantially no change in pin hole density (the pin hole density was 0.08 flaw/cm²). This indicates an excellent storage stability of the composition. COMPARATIVE EXAMPLE 1 A positive-type radiation-sensitive resin composition was prepared by repeating the same procedure as in Example 1, except that the solvent used in Example 1 (ethyl 2-oxypropionate) was replaced by ethylene glycol monomethyl ether acetate. Immediately after preparation, the composition contained 8 fine particles having pore diameters of at least 0.5µm per ml of the composition, and its pin hole density was 0.1 flaw/cm². This composition was stored for 1 month at 40°C in the same manner as in Example 1. After storage, the composition contained no fine particles when visually checked, but the number of particles having particle diameters of at least 0.5 µm as measured by the automatic fine particles measurement tester increased to 1,000 per ml of the composition. Also, the pin hole density increased to 2.0 flaws/cm². EXAMPLES 2 to 6 Positive-type radiation-sensitive resin compositions were prepared by repeating the same procedure as in Example 1, except that the solvent used in Example 1 (ethyl 2-oxypropionate) was replaced by one of those shown in Table 1. On each composition, immediately after preparation and after 1 months storage at 40°C, the number of fine particles having particle diameters of at least 0.5 µm and the pin hole density were measured in the same manner as in Example 1. The results indicate that none of the solvents used caused an increase in the number of fine particles and pin hole density. The results are shown in Table 1. The resist performance of each composition was the same as in Example 1. EXAMPLES 7 TO 13 Positive-type radiation-sensitive resin compositions were prepared by repeating the same procedure as in Example 1, except that the 1,2-quinonediazide compound used in Example 1 was replaced by one of those shown in Table 2. On each composition, immediately after preparation and after 1 months storage at 40°C, the number of fine particles having particle diameters of at least 0.5µm and the pin hole density were measured in the same manner as in Example 1. The results indicate that none of the 1,2-quinonediazide compounds used caused an increase in the number of fine particles and pin hole density, as can be seen from Table 2. Each composition gave no difference in resist performance (sensitivity and yield of residual film thickness) between immediately after preparation and after 1 months storage at 40°C.

Claims: A radiation-sensitive resin composition comprising a solution of 100 parts by weight of a) at least one alkali-soluble resin selected from novolaks, polyhydroxystyrenes and their derivatives, styrene-maleic anhydride copolymers, polyvinyl hydroxybenzoates and carboxyl group-containing methacrylate resins and b) 5 to 100 parts by weight of a 1,2-quinone-diazide compound as radiation-sensitive compound in a solvent comprising a monooxymonocarboxylic acid ester having the formula (I): R¹O-R²-COOR³ (I) wherein R¹ is a hydrogen atom, an alkyl group having 1 to 3 carbon atoms or an acyl group having from 1 to 4 carbon atoms; R² is an alkylene group having 1 to 4 carbon atoms; and R³ is an alkyl group having 1 to 4 carbon atoms. A composition according to Claim 1, wherein the monooxymonocarboxylic acid ester is at least one of alkyl oxyacetates, alkyl alkoxyacetates, alkyl 3-oxypropionates, alkyl 3-alkoxypropionates, alkyl 2-oxypropionates, alkyl 2-alkoxypropionates, alkyl 2-oxy-2-methylpropionates, alkyl 2-alkoxy-2-methylpropionates, alkyl 2-oxy-3-methylbutanoates and alkyl 2-alkoxy-3-methylbutanoates. A composition according to Claim 1, wherein the monooxymonocarboxylic acid ester is methyl oxyacetate, ethyl oxyacetate, butyl oxyacetate, methyl methoxyacetate, ethyl methoxyacetate, butyl methoxyacetate, methyl ethoxyacetate, ethyl ethoxyacetate, methyl 3-oxypropionate, ethyl 3-oxypropionate, methyl 3-methoxypropionate, ethyl 3-methoxypropionate, methyl 2-oxypropionate, ethyl 2-oxypropionate, propyl 2-oxypropionate, ethyl 2-methoxypropionate, propyl 2-methoxypropionate, methyl 2-ethoxypropionate, ethyl 2-ethoxypropionate, methyl 2-oxy-2-methylpropionate, ethyl 2-oxy-2-methylpropionate, methyl 2-methoxy-2-methylpropionate, methyl 2-ethoxy-2-methylpropionate, methyl 2-oxy-3-methylbutanoate, ethyl 2-oxy-3-methylbutanoate, methyl 2-methoxy-3-methylbutanoate, methyl 2-ethoxy-3-methylbutanoate, ethyl 2-methoxy-3-methylbutanoate or ethyl 2-ethoxy-3-methylbutanoate. A composition according Claim 1, wherein the monooxycarboxylic acid ester is at least one of methyl 2-oxypropionate and ethyl 2-oxypropionate. A composition according to any one of the preceding Claims, wherein the solvent comprising a monooxymonocarboxylic acid ester is present in an amount of from 40 to 90% by weight of the composition. A composition according to any one of the preceding Claims, wherein the solvent consists of said monooxymonocarboxylic acid ester and at least one other solvent, the amount of said other solvent(s) being less than 30% by weight of the total weight of the solvent. A composition according to Claim 6, wherein said other solvent is at least one ether, ester, ketone, fatty acid, alcohol or aromatic hydrocarbon. A composition according to Claim 6, wherein said other solvent is at least one of ethylene glycol monomethyl ether, ethylene glycol monoethyl ether, diethylene glycol monomethyl ether, diethylene glycol monoethyl ether, benzyl ethyl ether, dihexyl ether, ethylene glycol monomethyl ether acetate, ethylene glycol monoethyl ether acetate, ethyl acetate, butyl acetate, benzyl acetate, ethyl benzoate, diethyl oxalate, diethyl maleate, ethylene carbonate, propylene carbonate, γ-butyrolactone, methyl ethyl ketone, cyclohexanone, diisobutyl ketone, acetonitrile, isophorone, caproic acid, capric acid, 1-octanol, 1-nonanol, benzyl alcohol, toluene and xylene.

Inventors: HARITA, YOSHIYUKI, HOSAKA, YOSHIHIRO, NOZUE, IKUO, TAKATORI, MASASHIGE
Applicants: JAPAN SYNTHETIC RUBBER CO., LTD.
Application year: 1986
Main classification: G03F7
IPC codes: G03F7, C08K5, G03C1, C08L61, H01L21