VINYL MONOMERS AND DERIVED LIQUID CRYSTALLINE POLYMERS

Abstract: There is disclosed a new vinyl monomer capable of forming polymeric vesicles, micelles, monolayers, and side-chain liquid crystalline polymers. The vinyl monomer is of the formula wherein R₁ is substituted or unsubstituted long chain alkyl or aryl and R₂ is a hydrogen atom, alkyl, or aryl. The side-chain liquid crystalline polymers can be formed by free radical polymerization or by anionic polymerizations techniques. The different reaction methods give polymers of different configuration; the anionic technique results in a polymer having a nitrogen atom in the backbone. The polymers are useful in film and fiber formation and display good toughness.

Description: The present invention relates to new vinyl monomers and to liquid crystalline polymers which can be obtained therefrom. J. Chem. Soc., Perkin I (1973) 1134-5, discloses compounds of formula I wherein R₁ is benzyl, phenoxymethyl, phenyl or cyclohexyl and R₂ is H. EP-A-0113330 discloses compounds of formula I, wherein R₁ is substituted benzyl and R₂ is H, for use in therapy. GB-A-1354571 discloses compounds of formula I, wherein R₁ is a monocyclic, carbocyclic or heterocyclic group and R₂ is C 1-4 alkyl, for insecticidal use. US-A-2622074 discloses compounds of formula I, wherein R₁ is "alkyl or aryl such as methyl, ethyl, propyl, phenyl etc" and R 2 is a cation, for (co)polymerisation to form fibres. Compounds according to the present invention are of formula I, wherein R₁ is substituted or unsubstituted C 9-20 alkyl and R₂ is a hydrogen atom, alkyl, or aryl group. Because of the amphiphilic nature of these new monomers, they are capable of forming very stable vesicles, micelles, and monolayers that may be polymerized to give stable encapsulated solutions. One method for the production of the alpha-aminopropenoic acid derivatives of the present invention is a multi-step procedure starting from commercially available D,L-serine wherein the serine is treated to form the hydrochloride salt (optionally esterified) which is then reacted with an acid chloride to form a serine derivative of the formula which in turn is reacted to convert the serine to an alanine derivative comparable to the formula of the alpha-aminopropenoic acid derivatives of the present invention. Another method for the production of the alpha-aminopropenoic acid derivatives of the present invention is a multi-step procedure starting from commercially available D,L-serine wherein the serine is treated to form the hydrochloride salt (optionally esterified) which is then reacted with phosphorous pentachloride (PCl₅) and an acid chloride to form an alanine derivative of the formula which in turn is reacted to convert the beta-chloroalanine to an alanine derivative comparable to the formula of the alpha-aminopropenoic acid derivatives of the present invention. Polymers can be made from the monomer using either normal free radical conditions or an anionic procedure that is described in more detail infra. The polymers made with the alpha-aminopropenoic acid derivatives of the present invention have biocompatible and/or biodegradable uses such as (i) encapsulation for controlled drug release, (ii) functional vesicles for antibody or antigen specific diagnostic tests, (iii) in vivo/in vitro studies of the mechanism(s) of endocytosis, (iv) impact modifiers of commercial polymers, i.e., a polymeric plasticizer, and (v) monolayer and Langmuir/Blodgett film-formers which can be subsequently polymerized and used for surface modification and coatings applications. BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is an S.E.M. photograph of vesicles formed by the polymerized monomers of the present invention and is discussed at Example 4, infra, and Fig. 2 is a photograph of the broken vesicles of Fig. 1. Fig. 3 is a pressure vs. area curve of the monolayer composed of N-stearoyldehydroalanine methyl ester at the air/water interface and is discussed at Example 22, infra. DETAILED DESCRIPTION OF THE INVENTION Alpha-aminopropenoic acid derivatives of the present invention are characterized by the presence of a long-chain alkyl group, either substituted or unsubstituted, adjacent the amide-carbonyl moiety. R 1 is preferably C 9-17 . Specific representative groups are C₅H₁₁, C₉H₁₉, C₁₃H₂₇, and C₁₇H₃₅ groups. Representative R₂ groups include hydrogen, C₁ to C₁₈ alkanes, and aryl groups. The alkanes and aryl groups are similar to those shown in the R₁ groups but also include lower alkyl groups such as methyl, ethyl, propyl, and butyl, either substituted or unsubstituted. The new monomers where R₁ is C₉ to C₁₇ can form vesicles because of the presence of both a hydrophilic end group and a hydrophobic tail (amphiphilic) which results in surfactant-like properties. The two methods used for the production of the alpha-aminopropenoic acid derivatives of the present invention are: (i) the methyl esterification of D,L-serine in HCl saturated methanol, with subsequent reaction with the appropriate acid chloride, followed by dehydration of the serine residue by a CuCl catalysed reaction with a carbodiimide and (ii) the methyl esterification of D,L-serine in HCl saturated methanol, with subsequent reaction with phosphorous pentachloride (PCl₄) followed by reaction with the appropriate acid chloride and beta-chloro elimination (dehydrochlorination) using triethylamine base. Other lower alcohols, e.g. C²⁻⁵-alkanols, can be used besides methanol. In addition to the methods disclosed supra for the production of the alpha-aminopropenoic acid derivatives of the present invention, other synthetic routes are available for the production thereof including the treatment of alanine and cysteine. Other techniques include beta-elimination reactions on (i) O-mesylate or O-tosylate derivatives of serine, (ii) sulfinium or sulfinyl derivatives of cysteine, (iii) cysteine reacted with silver carbonate, and (i) N-chloro derivatives of alanine. Also available are (v) the Hofmann degradation of diaminopropionyl residues, (vi) the rhenium sulfide catalyzed reaction of anhydrides with methyl-2-azidopropionate, and (vii) direct dehydration of serine residues with triphenylphosphine and diethyl azodicarboxylate. The new monomers of the present invention can be polymerized using free radical techniques and it has been found that the resulting polymer has a structure as follows: where n is an integer sufficient to give the resulting product a molecular weight of about 10,000 to about 14,000,000 as determined by capillary viscometry and Low Angle Laser Light Scattering [LALLS]. These polymers have been found to be soluble in a variety of organic solvents including acetone, chloroform, 1,4-dioxane, ethyl acetate, methylene chloride, and tetrahydrofuran. The molecular weights of the polymers prepared to date by the free radical polymerization of the alpha-amino propenoic acid derivatives of the present invention range from 100,000 to 3,500,000 daltons, as determined by capillary viscometry and LALLS. Various peroxides and azo initiators can be used in the free radical polymerization. Representative compounds include potassium peroxydisulfate [K₂S₂O₈], 2,2'-azobis-(isobutyronitrile) [AIBN], and 2,2'-azobis-(2-amidinopropane) hydrochloride [V-50]. Photoinitiators such as V-50, 2,2-dimethoxy-2-phenyl acetophenone [Irgacure 651], diethoxy acetophenone [DEAP], and benzophenone can also be used. It is also possible to form polymers from the alpha-aminopropenoic acid derivatives of the present invention by an anionic technique that results in a formation of polymers having the following formula: where n is an integer sufficient to give the resulting product a molecular weight of about 10,000 to about 1,500,000 as determined by capillary viscometry and LALLS. It has been found that a polymer of this type is insoluble in common organic solvents except N,N-dimethylformamide and N,N-dimethylacetamide. The anionic polymerization technique which uses an alkyl lithium (or potassium alkoxide) initiator is similar to the method for preparing Nylon-3 from acrylamide. However, as can be seen from a review of the formula of the polymer, the carbonyl group is not within the backbone and depolymerization should not occur as readily as that for Nylon-3 type polymers. The polymers made by anionic polymerization techniques represent a new class of polymer containing a single nitrogen in the repeating unit with functional side groups and without the associated backbone carbonyl found in conventional polyamides. The polymers of the present invention, including those prepared by free radical and anionic techniques, are new thermoplastic polymers having a high melting point and good toughness. The polymers can be used for both films and fiber formation. Polymerization of the monomer by either of these techniques usually takes place for a period of seconds (anionic) to greater than four hours (free radical) at a temperature in the range from about room temperature to about 100°C, and at atmospheric pressure. It is preferred to undertake the polymerization for a period of up to 24 hours at temperatures between 60°C to 100°C (for both techniques) and at atmospheric pressure. The following examples are representative of the invention. EXAMPLE 1 The first method for monomer synthesis was accomplished by adapting published methods for the methyl esterification, N-acylation, and dehydration of D,L-serine to form N-alkanoyldehydroalanine methyl ester [methyl N-alkanoyl-alpha-aminopropenoate]. Commercial D,L-serine was reacted with excess HCl saturated methanol at 40°C for 4 hours. After solvent removal under reduced pressure, and vacuum oven drying, the D,L-serine methyl ester hydrochloride salt was dissolved in a mixture of excess chloroform and two molar equivalents of triethylamine. While stirring constantly at 5°C, the appropriate acid chloride was added dropwise over a period of 4 hours. The clear solution so obtained was allowed to stir at 5°C overnight to complete the reaction. The solution was extracted once with 0.1 N HCl and again with an equal volume of pure water to remove the triethylamine hydrochloride salt. The chloroform phase was evaporated under reduced pressure to obtain a clear oil. In some cases, depending upon the length of R₁, the oil crystallized on standing at room temperature. The material so obtained was dissolved in excess methylene chloride to which was added 10% molar excess N,N-diisopropylcarbodiimide and 4% molar CuCl catalyst, and was held at 30°C for at least 4 days or until the reaction was complete (as determined by caillary gas chromatography using a 25 meter SE-54 fused silica column with flame ionization detection). The suspension was filtered to remove the crystalline N,N-diisopropylurea side product. Solvent removal from the filtrate resulted in a green oil. Purification was accomplished by preparative column chromatography using a silica gel-methylene chloride system. Solvent removal resulted in a clear oil which was the N-alkanoyldehydroalanine methyl ester [methyl N-alkanoyl-alpha-aminopropenoate]. The advantage of this method is that the CuCl catalyst also inhibits spontaneous polymerization. A disadvantage of this method is the difficulty in purification for the removal of the copper salts formed in the reaction. EXAMPLE 2 Using the method described in Example I, n-decanoyl chloride [C₁₀H₁₉OCl] was used to obtain N-decanoyldehydroalanine methyl ester [methyl N-decanoyl-alphaaminopropenoate] as a clear oil which was further purified by crystallization in isomeric hexanes at -40°C. EXAMPLE 3 Using the method described in Example 1, n-myristoyl chloride [C₁₄H₂₇OCl] was used to obtain N-myristoyldehydroalanine methyl ester [methyl N-myristoyl-alpha-aminopropenoate] as an off-white mass which was further purified by crystallization in isomeric hexanes at -40°C. EXAMPLE 4 Using the method described in Example 1, n-stearoyl chloride [C₁₈H₃₅OCl] was used to obtain N-stearoyldehydroalanine methyl ester [methyl N-stearoyl-alpha-aminopropenoate] as a white mass which was further purified by crystallization in isomeric hexanes at -15°C. EXAMPLE 5 The second method for monomer synthesis was accomplished by adapting published methods for the methyl esterification, beta-chlorination, N-acylation, and dehydrochlorination of D,L-serine to form N-alkanoyldehydroalanine methyl ester [methyl N-alkanoyl-alpha-aminopropenoate]. Commercial D,L-serine was reacted with excess HCl saturated methanol at 40⁰C for 4 hours. After solvent removal under reduced pressure, and vacuum oven drying, the D,L-serine methyl ester hydrochloride salt was added in small portions over a period of 2 hours to a stirred suspension of 10% molar excess phosphorous pentachloride in 2-nitropropane held at 10°C. The mixture was left at 10°C overnight to complete the reaction. The suspension was filtered and the white crystalline product [3-chloroalanine methyl ester hydrochloride] was rinsed with methylene chloride and anhydrous acetone. The 3-chloroalanine methyl ester hydrochloride salt was added to excess benzene and stirred below 10°C before adding a 1 molar equivalent of triethylamine base. Another molar equivalent of triethylamine base and 1 molar equivalent of the appropriate acid chloride were alternately added portionwise to a well stirred suspension over a period of 1 hour. A final equivalent of triethylamine base was added before the reaction mixture was brought to 40°C for 2 hours to ensure complete reaction. Alternatively, the reaction mixture was placed in a refrigerator overnight. Capillary gas chromatography was used to determine if the reaction was complete [25M SE-54 fused silica column with flame ionization detection]. The suspension was filtered to remove the triethylamine hydrochloride salt and the filtrate was washed twice with 0.1 N HCl and once with an equal volume of pure water. A pinch of hydroquinone was added to the organic phase to inhibit polymerization. Solvent removal under reduced pressure and moderate temperature resulted in a clear oil product which was the N-alkanoyldehydroalanine methyl ester [methyl N-alkanoyl-alpha-aminopropenoate]. This method affords a clean product which can be easily purified by repeated cold crystallizations from hexanes. The advantage of this method is the efficacy of the reaction(s) to obtain a pure product. The disadvantage is that the inhibitor has to be removed before polymerization can occur. EXAMPLE 6 Using the method described in Example 5, n-10-undecenoyl chloride [C₁₁H₁₉OCl) was used to obtain N-10-undecenoyldehydroalanine methyl ester [methyl N-10-undecenoyl-alpha-aminopropenoate] as a clear oil which was further purified by crystallisation in isomeric hexanes at -40°C. EXAMPLE 7 Using the method described in Example 5, n-decanoyl chloride [C₁₀H₁₉OCl] was used to obtain N-decanoyldehydroalanine methyl ester [methyl N-decanoyl-alpha-aminopropenoate] as a clear oil which was further purified by crystallization in isomeric hexanes at -40°C. EXAMPLE 8 Using the method described in Example 5, n-lauroyl chloride [C₁₂H₂₃OCl] was used to obtain N-lauroyldehydroalanine methyl ester [methyl N-lauroyl-alpha-aminopropenoate] as a clear oil which was further purified by crystallization in isomeric hexanes at -20⁰C. EXAMPLE 9 Using the method described in Example 5, n-stearoyl chloride [C₁₈H₃₅OCl] was used to obtain N-stearoyldehydroalanine methyl ester [methyl N-stearoyl-alpha-aminopropenoate] as a white mass which was further purified by crystallization in isomeric hexanes at -15⁰C. EXAMPLE 10 Free radical polymerizations were performed in isomeric hexanes using AIBN initiation at 60°C. Approximately one gram of monomer was dissolved in an isomeric mixture of hexanes (dried over 4A molecular sieves) containing about 100 mg AIBN. Dry nitrogen was passed through the mixture contained in a septum-capped test tube for 5 minutes. The polymerization tube was then placed into a constant temperature oil bath maintained at 60°C for at least 4 hours and up to 24 hours. Solvent removal resulted in a clear polymer which was dissolved in tetrahydrofuran and reprecipitated into ice cold methanol. The polymer was vacuum oven dried to remove traces of solvent. EXAMPLE 11 Using the method described in Example 10, six polymerizations of N-decanoyldehydroalanine methyl ester were performed and the polymers were characterized by capillary viscometry and LALLS in tetrahydrofuran. The intrinsic viscosities ranged from 0.36 dl/g to 3.5 dl/g which correspond to weight average molecular weights [Mw] of 100,000 to 3,500,000. Polarized optical microscopy (using a controllable heated stage) revealed a softening point at 80°C with birefringence occurring under slight application of pressure to the sample coverslip. The birefringence is characteristic of thermotropic liquid crystallinity displayed by side-chain comb-like polymers. The polymer was soluble in acetone, chloroform, ethyl acetate, 1,4-dioxane, 2-propanol methylene chloride, and tetrahydrofuran. The polymer only swelled in petroleum ether, methanol, ethanol, N,N-dimethyl acetamide, and N,N-dimethylformamide. EXAMPLE 12 A 1.4 g sample of purified N-decanoyldehydroalanine methyl ester monomer was placed into a small screw cap vial. Within 3 days, under refrigerated conditions, the monomer had spontaneously polymerized into a clear solid. This is indicative of vinyl monomers which can autopolymerize by a free radical mechanism. The polymer was dissolved in tetrahydrofuran [THF], reprecipitated into ice cold methanol, and vacuum oven dried. The intrinsic viscosity in THF at 25°C was 8.7 dl/g which corresponds to a weight average molecular weight [Mw] of 14,000,000 daltons, as determined by extrapolation from the Mark-Houwink plot of other data. EXAMPLE 13 The anionic polymerization was performed in an isomeric mixture of hexanes using n-butyllithium or potassium tert-butoxide as the initiator. A clean, 120°C oven-dried test tube was charged with about 1 gram of N-decanoyldehydroalanine methyl ester and 5.0 ml isomeric hexanes (dried over 4A molecular sieves). A pinch of N-phenyl-2-naphthylamine was added (to inhibit free radical polymerization) and the tube was capped with a serum stopped. Dry nitrogen was passed through the mixture for 5 minutes before placing in an oil bath held at 60°C. Initiation of the reaction at 60°C was accomplished by using an aliquot of a commercial solution of n-butyllithium in n-hexane, or by adding crystals of potassium tert-butoxide. The hydrogen transfer polymerization resulted in a polymer that immediately precipitated from the reaction medium. The polymer was insoluble in the more common organic solvents except for N,N-dimethyl formamide (DMF) and N,N-dimethylacetamide (DMAC). The polymerization is similar to that of the anionic method used to prepare Nylon-3 from acrylamide; cf, V.R. Pai Verneker et al., Poly. Comm., 25(12), p. 363 (1984) and the references cited therein. However, since the carbonyl functional group is not within the backbone, depolymerization should not occur as readily as that for the Nylon-3 type polymers. This is the first example of a new class of polymers that contain a single nitrogen in the repeat unit without the associated backbone carbonyl found in all polyamides. This polymer also has a reactive carboxylate moiety adjacent to the main chain, as well as another carbonyl connected to the backbone nitrogen. Anionic solution polymerization occurred via a new hydrogen transfer mechanism to give a new class of polymers with backbone nitrogen (similar, but different from polyethyleneimines, which do not have dual functionality). One possible mechanism is as follows: This polymer was soluble only in DMAC and DMF in contrast to the polymer obtained free radically which was soluble in many organic solvents. In addition, the polymer formed by anionic solution polymerization displayed lyotropic crystalline behavior in concentrated DMAC solutions. The liquid crystallinity observed under polarized optical microscopy is probably due to side-chain order. Polarized optical microscopy of a concentrated solution of the anionically derived polymer in DMAC indicated lyotropic liquid crystallinity. Also, evidence for high crystallinity in a solution-drawn fiber indicates the possibility for processing from solutions. EXAMPLE 14 The monomers of Examples 2 and 4 also exhibited amphiphilic behavior in forming stable vesicles at 1-5% by weight in water after sonication. Radical polymerization of these vesicles gave stable spheres. Infrared spectroscopic analysis of the polymerized vesicles suggests a polymer configuration similar to that obtained by the normal free radical solution polymerization. EXAMPLE 15 The formation of vesicles was accomplished by sonication of a 1 to 5% aqueous suspension of N-decanoyldehydroalanine methyl ester at room temperature for one hour. Stable vesicles were formed (liposomes) as observed by optical microscopy. A thermal, water-soluble initiator (potassium peroxydisulfate) was added to the aqueous suspension and resonicated for one-half hour. Polymerization was effected at 60° overnight to form spheres with an average diameter of 1.04 microns. For comparison, this is about 1/6 the size of normal human red blood cells (7.5 microns). A sample of the vesicles was melted on a microscope slide and the resulting polymer mass showed the same birefringent behavior as the polymer obtained from the free radical solution polymerization. A sample of the suspension was air-dried on a glass slide and coated with gold prior to scanning electron microscopy (SEM). The photograph depicted in Fig. 1 has a representative field at 8100X, showing almost perfect spheres with excess gold between them. The sample was then removed from the SEM chamber and gently scraped with a surgical knife blade. The photograph of Fig. 2 at 8100X shows broken spheres with distinct evidence of the hollow or "eggshell" structure. EXAMPLE 16 The formation of vesicles was also accomplished by higher power sonication of a 1% suspension of N-stearoyldehydroalanine methyl ester in water for 30 seconds. Vesicles were formed with a greater distribution in size, and formation was recorded by light microscopy using videotape equipment. EXAMPLE 17 The formation of a monolayer of material using N-stearoyldehydroalanine monomer was accomplished by depositing a known amount of material dissolved in n-hexane onto the surface of pure water contained within the boundaries of a Lauda-Brinkman Langmuir film balance. Upon evaporation of the n-hexane, the displacement of the moveable barrier was changed at a controlled rate to compress the monomer until collapse. Fig. 3 shows the pressure vs. area isotherm so obtained. The shape of the curve is typical of compounds which form stable monolayers at the air/water interface. EXAMPLE 18 A monolayer of N-stearoyldehydroalanine methyl ester was polymerized by irradiating the monomer at the air/water interface with U.V. light (254nm). A sample of monomer dissolved in n-hexane was deposited as described in Example 17. The barrier was moved in the compression mode until the surface pressure was 12 dynes/cm². The instrument maintained this pressure automatically throughout the experiment by changing the location of the barrier. Leaving the monolayer (without irradiation) for up to 1 hour did not reduce the area, which indicated the stability of the monomeric monolayer. Upon irradiation with U.V. light, an induction period was followed by a measureable decrease in the total area occupied by the monolayer. This implies that the monomer is changing from a condensed liquid/solid state to a more condensed polymeric state. Collection of the film and examination under cross polarization light microscopy revealed thermal behavior similar to a polymeric sample derived from free radical solution polymerization. SUMMARY In summary, these examples demonstrate the novel uses of these new monomers for the formation of: 1. new comblike polymers by radical polymerization; 2. new comblike polymers by anionic hydrogen transfer polymerization which forms a new class of functional polymers; 3. aqueous polymerization to form synthetic liposomes which could have use in the biomedical, biochemical, and organic chemical fields; and 4. monolayers that can be polymerized by U.V. light (without the aide of an initiator) to form a polymeric material which may have application in photoresists, molecular wave-guide supports, and surface modification. The vesicles capable of being formed by the monomers of the present invention are believed to be filled with water although they may also be characterized as microemulsions.

Claims: A compound of the formula wherein R₁ is optionally substituted C 9-20 alkyl; and R₂ is hydrogen, alkyl or aryl. A compound according to claim 1, wherein R₁ is C₉H₁₉, C₁₃H₂₇ or C₁₇H₃₅. A compound according to claim 1 or claim 2, wherein R₂ is CH₃. A polymer containing repeating units of the formula wherein R₁ and R₂ are as defined in any preceding claim. A polymer according to claim 4, which has a molecular weight of 10,000 to 14,000,000. A polymer according to claim 4 or claim 5, in the form of stable vesicles, micelles or monolayers. A polymer containing repeating units of the formula wherein R₁ and R₂ are as defined in any of claims 1 to 3. A polymer according to claim 7, which has a molecular weight of 10,000 to 1,500,000. A process for preparing a polymer according to any of claims 4 to 6, which comprises a free radical polymerisation process. A process for preparing a polymer according to claim 7 or claim 8, which comprises an anionic polymerisation process.

Inventors: HERMES, ROBERT E., MATHIAS, LON J. UNIVERSITY SOUTHERN MISSISSIPPI
Applicants: THE UNIVERSITY OF SOUTHERN MISSISSIPPI
Application year: 1986
Main classification: C07C233
IPC codes: C07C233, A61K9, C07C67, C09K19, C08G73, C07C231, C08F26