METHOD OF PRODUCING CERAMIC ARTICLES

Abstract: Ceramic articles having improved fracture tough­ ness are prepared by ion bombardment of ceramic particles by gas ions to impregnate the particles, cold compacting the gas ion-containing ceramic particles into a form, and hot pressing the gas ion-containing ceramic particle form into a ceramic article whereby gas bubbles are formed in and substantially homogeneously dispersed throughout the ceramic article.

Description: This invention relates to a method or producing ceramic articles, having improved fracture toughness properties, by powder metallurgical techniques. Structural ceramics such as silicon nitride, silicon carbide, partially stabilized zirconia and partially stabilized alumina are being developed for high temperature applications in heat engines of various types (automotive, gas turbine), tools and dies, and other components because of their high strength at elevated temperatures, and erosion and corrosion resistance. However, because of the inherent brittleness (low fracture toughness) of ceramics, their application potential is not as widespread as it could be if their fracture toughness and ductility were enhanced. The fracture strength of a ceramic is expressed by the relationship: σ f = K c (c) -½ where K c is the fracture toughness (resistance to crack propagation) and c is the size of the critical crack that leads to failure. For a fixed flaw size distribution, therefore, strength is dependent on fracture toughness. Improvements in fracture toughness would undoubtedly enhance the use of such ceramics, especially where resistance to any thermal cycling is desired. It has been proposed by F. F. Lange, "The Interaction of a Crack Front with a Second Phase Dispersion", Philosophical Magazine , 22 (1970) pp. 983-92 and further developed by A. G. Evans, "The Strength of Brittle Materials Containing Second Phase Dispersion", Philosophical Magazine , 26 (1972) pp. 1327-44, that the strength (hardness) and fracture toughness of ceramics can be increased by crack pinning by dispersed particles of a second phase. The concept is based on an observation of an increase in the length of a crack front when it interacts with two or more inhomogeneities. The theory further developed by Evans showed that significant improvement in fracture energy (toughness) can be achieved by a presence of closely spaced second phase particles. Evidence of improvement of fracture toughness by a dispersion of voids throughout a solid material was provided by G. E. Hurley and F. W. Clinard, Jr. "Fracture Toughness and Harness of Neutron-Irradiated A1₂O₃, MgA1₂O₄ and Y₃A1₅O₁₂", DOE (Department of Energy)/ER-0048/1 (1981) pp. 51-57. They observed an increase in fracture toughness by a factor of 2 in a single crystal alumina which had been neutron irradiated. The irradiation produced an array of voids. They also found good correlation between theoretically predicted fracture toughness and that observed, assuming the voids to be impenetrable obstacles. While neutron irradiation, with the resultant production of voids can increase the fracture toughness of ceramics, as a technique for producing ceramic with high toughness, such irradiation has several drawbacks. It is costly, it produces an anisotropic distribution of voids, and it renders the material radioactive. Accordingly, the present invention resides in a method of producing ceramic articles having improved fracture toughness properties by a powder metallurgical process characterized by providing a supply of ceramic particles having a particle size of between 0.5-5 micrometers in diameter; injecting ions of an inert gas into the ceramic particles of said supply of particles by impingement therewith of a beam of accelerated said gas ions to produce a supply of gas ion-containing ceramic particles; compacting said gas ion-containing ceramic particles into a form by applying pressure thereabout; and heating said form at a temperature of at least 800°C, whereby said gas ions form gas bubbles, to produce a ceramic article having gas bubbles substantially uniformly disposed throughout. The gas ions may be helium ions, which are impinged onto and impregnated into ceramic particles, such as silicon carbide, silicon nitride, stabilized zirconia or alumina. Conveniently, cold isostatic pressing produces a stabilized form which is then sintered or hot isostatically pressed into the ceramic article. Desirably, the ceramic particles are oxides, nitrides, borides and carbides of silicon, zirconium, aluminum, magnesium, yttrium, and other complex ceramic compounds such as SiAlON. Examples of such ceramic compositions are silicon nitride, silicon carbide, partially stabilized zirconia, alumina, SiAlON and the like. The ceramic compositions are provided in a finely divided powdered state with particles in a size of between 0.5-5 micrometers (µm) in diameter. The small solid particles are of a size which enables impregnation thereof with gas ions at reasonable ion energies. The gas ions used for impregnation may vary depending upon the ceramic particles, and gases, such as helium, argon, neon or krypton may be used. The impregnation of the ceramic particles with gas ions is conveniently effected by impingement of the particles with a high energy beam of accelerated gas ions, under vacuum, at ambient temperatures, and preferably with tumbling of the particles. Typically, an ion impingement of the ceramic powder will be effected with a few hundred KeV accelerated beam of gas ions. Preferably, a 150 KeV beam of ions is used, although the energy of the beam may be varied depending upon the particle size of the ceramic material and the accelerated gas specie used. The particles are continuously tumbled during impingement to uniformly expose all of the powder particles to the ion beam using known accelerators and vacuum tumbling systems, such as a rotating cup, for example as described by L. R. Fleischer, J. S. Spitznagel and W. J. Choyke, "Helium Embrittlement of CRT Materials Simulated by Ion Implantation and Hot Isostatic Pressing of Metal Powders", CONF-750989, Vol. II, 1976, pp. 372-386. The impingement of the ceramic particles with gas ions is carried out for a period of time sufficient to provide the quantity of ions in the particles that will result in the desired quantity of gas bubbles in the ceramic article produced. The gas ion-containing particles are then compacted into ceramic articles by, desirably, first cold compacting to stabilize the same and then hot compacting or sintering. In the cold compacting step, the gas ion-containing particles are compacted at ambient temperature by the application of pressure equally about the supply of gas ion-containing particles. Cold isostatically pressing of the gas ion-containing particles forms a monolithic shape or form which can be subsequently hot compacted. Preferably, the cold compacting is effected at pressures sufficient to compress the particles to a density of from 65 to 80 per cent of theoretical density to provide a form for subsequent hot pressing. Hot compacting of the gas ion-containing ceramic particles is then carried out with or without pressure to achieve substantially maximum density of the particles. Hot isostatic pressing, at super-atmospheric pressure, or sintering at atmospheric pressure, is effected at an elevated temperature, namely, a temperature of at least 800°C. Heating and compacting of the form of gas ion-containing particles causes the gas ions to form gas bubbles throughout the article formed, with the gas bubbles substantially uniformly distributed throughout the ceramic article. The inert gas bubbles formed homogeneously throughout the ceramic article should have a low c/r o ratio, where 2c is equal to interbubble spacing and 2r o is the bubble diameter. It is preferred that the c/r o ratio be between 0.1 and 5. Bubble size during the formation of the ceramic articles can be controlled by process parameters such as time, temperature and amount of gas ions present in the ceramic particles. The size of the gas bubbles dispersed throughout the ceramic article must be less than about 1 micrometer in diameter, with much smaller bubbles preferred, such as bubbles of a size of from 100-400 angstroms (10-40 nm) in diameter. The process is schematically illustrated in the accompanying flow chart which illustrates a supply of ceramic particles (Step 1) of a diameter of 0.5-5 micrometers, into which ions of an inert gas are injected (Step 2) under vacuum. The supply of gas ion-containing ceramic particles are cold compacted (Step 3) into a form that stabilizes the particles, and the form is then heated with or without pressure (Step 4) to produce a ceramic article containing gas bubbles. The finished article (Step 5) comprises a ceramic article containing inert gas bubbles substantially uniformly dispersed throughout the article which induces increased fracture toughness.

Claims: A method of producing ceramic articles having improved fracture toughness properties by a powder metallurgical process characterized by providing a supply of ceramic particles having a particle size of between 0.5-5 micrometers in diameter; injecting ions of an inert gas into the ceramic particles of said supply of particles by impingement therewith of a beam of accelerated said gas ions to produce a supply of gas ion-containing ceramic particles; compacting said gas ion-containing ceramic particles ion a form by applying pressure thereabout; and heating said form at a temperature of at least 800°C, whereby said gas ions form gas bubbles, to produce a ceramic article having gas bubbles substantially uniformly disposed throughout. A method according to claim 1, characterized in that the gas ions comprise ions of helium, argon, neon or krypton. A method according to claim 1 or 2, characterized in that the heating under pressure produces a ceramic article having a c/r o ratio of between 0.1 and 5.0, wherein 2c is the interbubble spacing and 2r o is the bubble diameter. A method according to claim 1, 2 or 3, characterized in that the ceramic particles are oxides, nitrides, borides and carbides of silicon, zirconium, aluminum, magnesium or yttrium, and SiAlON. A method according to claim 4, characterized in that the ceramic particles comprise silicon nitride. A method according to claim 4, characterized in that the ceramic particles comprise silicon carbide. A method according to claim 4, characterized in that the ceramic particles comprise partially stabilized zirconia. A method according to claim 4, characterized in that the ceramic particles comprise alumina. A method according to claim 4, characterized in that the ceramic particles comprise SiAlON. A method according to any of claims 1 to 9, characterized in that the heating of the form is effected under super-atmospheric pressure. A method according to any of claims 1 to 10, characterized in that the compacting of the gas ion-containing ceramic particles into a form is effected to provide a form having a density of from 65 to 80 per cent of theoretical density. A method according to any of claims 1 to 11, characterized in that the gas bubbles have a diameter of less than 1 micrometer. A method according to claim 12, characterized in that the gas bubbles have a diameter of from 100-400 angstroms (10-40 nm).

Inventors: BAJAJ, RAM
Applicants: WESTINGHOUSE ELECTRIC CORPORATION
Application year: 1986
Main classification: C04B35
IPC codes: C04B35, C04B38