FOAMABLE MOLDINGS COMPOSITIONS

Abstract: Foamable, thermoplastic molding composition ex­ hibiting an improved level of impact resistance is pro­ vided. The composition, which is suitable for the pre­ paration of expanded molded parts, comprise a thermo­ plastic resin, preferably at least one selected from a group consisting of polycarbonate, polyalkylene tereph­ thalate, aromatic polyester and polyester carbonate, a nucleating agent, a chemical blowing agent and an anhydride. It was unexpectedly found that the composi­ tion is suitable for the molding of articles having an improved level of impact resistance.

Description: Foamable molding compositions containing chemical blowing agents are known. U.S. Patent 3,888,801 disclo­ ses the chemical blowing agents which are suitable in the context of the present invention. Resins which are suitable in the present invention are also disclosed in that patent. Also known are the anhydrides of the invention; U.S. Patent 4,420,584 discloses glass filled polycarbonate compositions having an improved impact strength, containing these anhydrides. The art however does not appear to have recognized the unexpected advan­ tages associated with the combination of these compo­ nents in the context of the present invention. Thus the subject of the istant invention is a foamable thermoplastic molding composition comprising (i) a foamable thermoplastic resin, (ii) about 0.01 to 10 percent of a polymeric com­ pound containing at least one cyclic anhydride in its repeating unit, (iii) 0.05 to 15 percent of a chemical blowing agent which decomposition product comprises a prima­ ry amine, and (iv) an amount of a nucleating agent for structural foam sufficient to produce a substantially uniform cell size in the resulting foam, said percents being in relation to the weight of said (i). DETAILED DESCRIPTION OF THE INVENTION The polymeric resin component of the composition of the invention is a thermoplastic resin which is both suitable for foaming, i.e. foamable, and sensitive to the foaming agent's decomposition products which contain primary amines, for instance, an amino urazole. Sensiti­ vity in the present context is considered to be a proclivity to structural degradation which is expressed in terms of a reduction in molecular weight whichr re­ sults upon exposing the resins to the decomposition pro­ ducts at the molding temperature of the resin. Among the sensitive resins, there are thermoplastic polycarbonate, thermoplastic polyalkylene terephthalate, thermoplastic aromatic polyester and thermoplastic polyester-carbo­ nate. The preferred resins are thermoplastic carbonate and thermoplastic polyalkylene terephthalate. In the present context, polycarbonate resins have a molecular weight (weight average) of about 10,000 to about 200,000, preferably about 20,000 to about 80,000, and may alternatively be characterized as having a melt flow rate per ASTM D-1238 at 300°C, of about 1 to about 24 gm/10 minutes, preferably about 2-6 gm/10 minutes. Polycarbonates which are suitable for the preparation of the preferred compositions of the invention are known in the art and in the market. Dihydroxy compounds suitable for the preparation of the polycarbonates of the invention are for example hydroquinone, resorcinol, bis(hydroxyphenyl)-alkanes, bis-(hydroxyphenyl)-cycloalkanes, bis-(hydroxyphenyl)-­ ethers, bis-(hydroxyphenyl)-ketones, bis-(hydroxyphe­ nyl)-sulfoxides, bis-(hydroxyphenyl)-sulfides, bis-­ (hydroxyphenyl)-sulfones and α,α-bis-(hydroxyphenyl)-­ diisopropyl-benzenes. These and further suitable aroma­ tic dihydroxy compounds are described, for example, in the U.S. Patent 3,028,365 and in the monograph H. Schnell, Chemistry and Physics of Polycarbonates, Interscience Publisher, New York, 1964. Further examples of suitable bisphenols are 2,2-bis-(4-hydroxyphenyl)-­ propane (bisphenol A), 2,2-bis-(4-hydroxyphenyl)-2-­ methyl-butane, 1,1-bis-(4-hydroxyphenyl)-cyclohexane, α,α-bis-(4-hydroxyphenyl)-p-diisopropylbenzene, 2,2-bis-­ (3-chloro-4-hydroxyphenyl)-propane, dihydroxybenzo­ phenone and 4,4'-sulfonyl diphenol. The most preferred dihydroxy compound is 2,2-bis-­ (4-hydroxyphenyl)-propane (bisphenol A). The polycarbonates of the invention may entail in their structure, unites derived from one or more of the suitable dihydroxy compounds. The preparation of polycarbonate resins may be carried out in accordance with any of the processes known in the art, for example, by the interfacial polycondensation process, polycondensation in a homo­ geneous phase or by transesterification. In the preparation of the polycarbonate resins of the invention, monofunctional reactants such as mono­ phenols may be used in order to limit their respective molecular weights. Also, branching agents may be em­ ployed. Branching may be obtained by the incorporation of small amounts, preferably of between about 0.05 to 2.0 mol % (relative to diphenols employed), of tri­ functional or more than trifunctional compounds, especially compouns having three or more phenolic hydroxyl groups. Polycarbonates of this type are also known in the art (see for example DE-PS 1 570 533 and DE-PS 2 500 092). Some examples of compounds with three of more than three phenolic hydroxyl groups which can be used are phloroglucinol, 4,6-dimethyl-2,4,6-tri-(4-hydroxyphe­ nyl)-heptane, 1,1,1-tri-(4-hydroxyphenyl)-ethane, tri-­ (4-hydroxyphenyl)-phenylmethane, 2,2-bis[4,4-bis-(4-­ hydroxyphenyl)-cyclohexyl]-propane, 2,4-bis-(4-hydroxy­ phenylisopropyl)-phenol, 2-(4-hydroxyphenyl)-2-(2,4-­ dihydroxyphenyl)-propane, hexa-(4-(4-hydroxyphenyliso­ propyl)-phenyl-orthoterephthalic acid ester, tetra-4-­ hydroxyphenyl)-methane, tetra-(4-(4-hydroxyphenyliso­ propyl)-phenoxy)-methane and 1,4-bis-(4' ,4"-dihydroxy­ triphenyl)-methyl-benzene. Some of the other trifunc­ tional compounds are 2,4-dihydroxy-benzoic acid, trime­ sic acid, cyanuric chloride and 3,3-bis-(4-hydroxy­ phenyl)-2-oxo-2,3-dihydroindole. The polyalkylene terephthalate resins which are suitable in the present context are known. The preferred species, polyethylene terephthalate (PET) and poly­ butylene terephthalate (PBT) are available in commerce. Their chemical makeup and processes for preparation are known and have been described in, among others, U.S. Patents 2,465,319 and 3,047,539. Aromatic polyesters and polyester-carbonates are known in the art. (See for example DE-OS 3 346 946 (Le A 22 776), U.S. Patent 4,252,939 and the article "Synthesis of Poly(ester Carbonate) Copolymers", D.C. Prevorsek et al, Journal of Polymer Science: Polymer Chemistry Edition , Vol. 18, 75-90 (1980).) The relative solution viscosity (η rel ) of the aromatic polyesters and polyester carbonates suitable in the present context generally lies in the range of from 1.15 to 1.40 preferably from 1.20 to 1.35 (measured in solutions of 0,5 g of polycarbonate in 100 ml of CH₂Cl₂ solution at 25°C). The blowing agent in the present context is characterized in that its thermal decomposition products comprise a primary amine, preferably an amino urazole. Among the suitable agents, there are hydrazodicarboxyl­ ates which are noted for the great volume of gas evolution attendant upon their thermal decomposition. These hydrzadicarboxylates conform to where R and R₁ independently denote a member selected from the group consisting of primary, secondary and tertiary straight-chain or branched-chain C₁-C₈ alkyl, C₅-C₈ cycloalkyl, C₆-C₁₀ aryl, C₇-C₁₀ aralkyl and C₇-C₁₀ alkaryl radicals. Preferred species have at least one of R and R₁ selected from the group consisting of iso­ propyl, secondary butyl and tertiary butyl and the other of R and R₁ is a C₁-C₄ alkyl. Most preferred species are those wherein both R and R₁ are selected from the group consisting of isopropyl, secondary butyl and tertiary butyl. The foaming agents most suitable is diisopropyl­ hydrozodicarboxylate: U.S. Patent 3,888,801 contains further information res­ pecting the hydrazodicarboxylates of the invention. The most suitable foaming agent may be prepared in accor­ dance with the technique disclosed in U.S. Patent 3,888,801. This agent is characterized in that its melting temperature is about 104-107°C and its decompo­ sition temperature is about 271-310°C. Upon its decompo­ sition, it generates an amount of 4-aminourazole corres­ ponding to about 15% of its original weight. The andhydride of the invention is a polymeric com­ pound containing at least one cyclic anhydride in its repeating unit. Preferably the anhydride is a polymeric compound containing at least one maleic acid anhydride unit in its repeating unit; most preferably the anhy­ dride is a copolymer of maleic acid anhydride and an olefin. Examples of suitable olefins are styrene, vinyl ether and methyl vinyl ether. Among the most suitable are the anhydrides which are represented by the structu­ ral formula: where R is a substituted or an unsubstituted radical selected from the group consisting of C₆-C₁₂ phenyl, C₁-C₁₂ alkoxy and C₁-C₂₈ alkyl radicals. In general, the carbon atoms of R may not be greater in number than 28, while n is an integer of from 1 to 200, and m is an in­ teger of from 1 to 5. In the most preferred embodiment, n is about 145 and m is 1. The preparation of suitable anhydride, namely copolymers of maleic anhydride and an α-olefin is described in U.S. Patent 3,586,659. Examples of olefin compounds suitable for forming the anhydride of the composition include: ethylene; 1-propane; 1-­ decene, 1-butene; 1-undecene; 1-isobutylene; 1-hexene; 1-dodecene; 1-pentene; 1-tridecene; 1-heptene; 1-octene; 1-tetradecene; 1-octadecene; 1-nonadecene; styrene; 1-­ nonene and mixtures thereof. The copolymerization procedure may involve contac­ ting the olefinic compounds with the maleic anhydride in a suitable solvent in the presence of a catalyst. The molar ratio of the mono-α-olefin to maleic anhydride is desirably between about 1:1 and 8:1. The preferred anhydride suitable in the practice of the invention is a copolymer of 1-octadecene and maleic anhydride of a 1:1 molar ratio, and is available from Gulf Oil Chemical Company under the tradename PA-­ 18®. PA-18® is further characterized by its properties shown in the table below: PA-10® and PA-6® too are anhydrides suitable in the present context and are largely similar to PA-18® except for their respective olefins. In these anhydrides the corresponding olefins are α-decene and α-hexene. Additionally, the composition of the invention needs to contain an amount of a nucleating agent suffi­ cient to bring about a uniform size distribution of the cells. Preferably, the amount of nucleating agent is about 0.05 to 5 percent by weight relative to the weight of the thermoplastic resin (i). The nucleating agent for structural foams are welll known in the art and among them, mention is made of milled glass, glass fibers and talc. Illustrations of the invention In the preparation of the composition in accordance with the invention and of the comparison examples the following materials and conditions were used. The polycarbonate resin was a homopolymer based on bisphenol A, having a melt flow rate, per ASTM D-1238, of about 5.1 gms/10 min., and a w of approx. 30 000. The anhydride was PA-18®. Other anhydrides differing from PA-18® in terms of the chain length of the α-olefin are noted wherever used. The chemical blowing agent used in illustrating the invention conforms to formula (I) above. The prior art chemical blowing agent was 5-phenyl tetrazole. In pre­ paring the examples which are noted below, glass fibers at an amount of about 4.5% were used both as a nuclea­ ting agent and to provide rigidity to the resulting foam. The compositions contained, where noted, a flame retarding agent (potassium perfluorobutane sulfonate), a phosphite stabilizer and a pigment, none of which are believed critical to the invention. Extrusions were carried out using a single screw extruder (2.75:1 screw, 100 rpm at about 275°C). The pellets were injection molded into foamed discs (6,4 mm x 10.16 cm) under the following conditions: mold temperature 77°C cycle time 60 seconds, screw speed 75 rpm, barrel temperature 300° C, melt temperature 295° C, primary injection pressure 127 kg/cm², secondary injection pressure 0, back pressure 7,03 kg/cm². In the process of preparing the molded part, resi­ nous polycarbonate pellets containing the anhydride and no blowing agents were blended with a blowing agent concentrate and injection molded. Variations of the pre­ paration process including using the blowing agent per se rather than the concentrate are also possible. The concentrates used in the course of preparation of compo­ sitions in accordance with the invention contained poly­ carbonate resin and 10% of the foaming agent of formula (I). The prior art concentrates contained 10% of 5-­ phenyltetrazole and a plasticizer. In evaluating the properties of the molded artic­ les, Gardner impact tester (Model IG1120-M with a tup diameter of 1.27 cm and a 3.18 cm diameter base) was used. Any crack seen or felt opposite the point of impact was regarded as failure of the tested specimen. The quantitative assessment of the impact resistance in N · m (impact resistance) made use of the Bruceton staircase method, per ASTM D-3029. The Instron melt stability is a measure of the apparent viscosity of a resin as a function of time at constant temperature (300° C), and shear rate (56.7 sec.⁻¹). An Instron melt rheometer was used for this determination. Melt flow rate (MFR) was determined in accordance with ASTM D-1238 (300° C - 1200 g load), the units are gm/10 min. The invention is further illustrated, but is not intended to be limited by the following examples in which all parts and percentages are by weight unless otherwise specified. EXAMPLES Examples 1-6 In these examples pellets comprising a polycarbo­ nate resin and an anhydride (PA-18)® were blended with a blowing agent concentrate containing the foaming agent of formula (I) above. A series of comparison examples entailed similar pellets except that the blowing agent concentrate contained 5-phenyl-tetrazole. The amount of the chemical blowing agent in the blends was calculated to yield equal foaming to the molded parts, that is equal reduction in density. The reduction of density was about 20%. Examples 7-13 Additional compositions in accordance with the invention were prepared and foamed molding made there­ from. The base resin in this series consisted of a blend (9.75/5.25 by weight) of bisphenol A based homopolycar­ bonates having a MFR of 4.2 and 9.4 gm/10 min, respec­ tively. The compositions all contained about 4.5% glass fibers as a nucleating agent and the foaming agent of the formula (I) above in an amount calculated to yield equal foaming to the moled parts; composition 13 in this series made use of 5-phenyl tetrazole. The reduction of density was about 20%. Other additives introduced in similar compositions in substitution for the anhydrides of the invention proved unsuccessful. Among these were epoxy-bearing com­ pounds and monomeric anhydrides (pyromellitic dianhy­ dride, phthalic anhydride and tetrabromophthalic anhy­ dride). Example 14-21 Additional compositions in accordance with the in­ vention were prepared and their properties determined. The preparation followed the procedure outlined above. Except for Example 15 where 5-phenyltetrazole served as a foaming agent, the compositions below were foamed using the foaming agent having the formula (I) above; the amount of foaming agent in each case was calculated to bring about equal reduction in density to the molded part. All the compositions maintained about 4.5% of glass fibers as a nucleating agent. The reduction of density was about 20%. Examples 22 - 29 In the series of experiments which are described below, comparisons were drawn between compositions of the invention in terms of the dependence of their melt stability on the degree of hydrolysis of the anhydride resins. The base composition contained the same ingre­ dients entailed in the above compositions except for the noted anhydrides below. Since the lowered melt viscosity indicates mole­ cular weight reduction which is associated with degra­ dation, the data - Instron melt stability - shows that the dehydrated additives caused less of a molecular weight reduction in the compositions of the invention. Generally, the amount of blowing agent used in the present invention depends on the resin to be expanded and on the desired density of the foam thus produced. Usually about 0.05 to about 15, preferably 0.1 to about 5.0 parts of blowing agent are used per 100 parts by weight of the resin. The amount of anhydride to be used in the prepara­ tion of the molding composition is 0.01 to 10 percent, preferably 0.05 to 2 percent in relation to the weight of the resin. Optionally, reinforced glass fibers in an amount of 5-30 percent by weight may be included in the com­ position. The composition of the invention may contain further additives which are known in the art for their efficacy in the context of foamable molding composi­ tions. These include various reinforcing agents, fillers, pigments and dyes, plasticizers, UV and hydrolysis stabilizers, flame retardants and mold re­ lease agents. In practicing the invention, it is pre­ ferred to compound first the resin, the anhydride and the auxiliary additives and form pellets therefrom. These pellets are then blended with a blowing agent con­ centrate containing a suitable amount of the blowing agent and nucleating agent of the invention. The mixing may be carried out in a known manner utilizing known equipment. Preferably, mixing may be carried out in an extruder. Reasonable variations and modifications are possible within the scope of the foregoing disclosure and the claims which follow, without departing from the spirit thereof. Reasonable variations and modifications are possible within the scope of the foregoing disclosure and the claims which follow, without departing from the spirit thereof. Although the invention has been described in detail in the foregoing for the purpose of illustration, it is to be understood that such detail is solely for that purpose and that variations can be made therein by those skilled in the art without departing from the spirit and scope of the invention except as it may be limited by the claims.

Claims: 1. A foamable thermoplastic molding composition com­ prising (i) a foamable thermoplastic resin, (ii) about 0.01 to 10 percent of a polymeric com­ pound containing at least one cyclic anhydride in its repeating unit, (iii) 0.05 to 15 percent of a chemical blowing agent which decomposition product comprises a prima­ ry amine, and (iv) an amount of a nucleating agent for structural foam sufficient to produce a substantially uniform cell size in the resulting foam, said percents being in relation to the weight of said (i). 2. The molding compositions of Claim 1 wherein said (i) is selected from the group consisting of polycarbonate, polyalkylene terephthalate, aromatic polyester and poly­ ester-carbonate. 3. The molding composition of Claim 1 wherein said polymeric compound is present at an amount of 0.1 to about 5 percent. 4. The molding composition of Claim 1 wherein said anhydride conforms to where R is a substituted or an unsubstituted radical selected from the group consisting of C₆-C₁₂ phenyl, C₁-C₁₂ alkoxy and C₁-C₂₈ alkyl radicals. n is an integer of from 1 to 200 and m is 1 to 5, 5. The molding composition composition of Claim 1 wherein said (iii) conforms to wherein R and R₁ independently denote a member selected from the group consisting of primary, secondary and tertiary straight-chain or branched-chain C₁-C₈ alkyl, C₅-C₈ cycloalkyl, C₆-C₁₀ aralkyl and C₇-C₁₀ alkaryl radicals. 6. The molding composition of Claim 5 wherein at least one of R and R₁ is selectd from the group consisting of isopropyl, secondary butyl and tertiary butyl radicals and the other of R and R₁ is C₁-C₄ alkyl. 7. The molding composition of Claim 5 wherein R₁ and R independently are selected from the group consisting of isopropyl, secondary butyl and tertiary butyl. 8. A foamable thermoplastic molding composition comprising (i) a thermoplastic polycarbonate resin, (ii) about 0.01 to 10 percent of a 1:1 copolymer of α-octadecene and maleic anhydride having a molecular weight of about 50,000 and (iii) 0.05 to 15 percent of diisopropyl hydrazo­ dicarboxylate, and (iv) 0.05 to 5 percent by weight of a nucleating agent selected from the group consisting of milled glass, glass fibers and talc, said percents being relative to the weight of said (i). 9. The molding composition of Claim 1 further compri­ sing glass fiber reinforcements, 10. The molding composition of Claim 1 further compri­ sing glass fiber reinforcements and flame-retarding agents.

Inventors: KRISHNAN, SIVARAM, SIEBOURG, WOLFGANG, DR., WHITE, ROGER J.
Applicants: MOBAY CORPORATION
Application year: 1986
Main classification: C08J9
IPC codes: C08J9