PLASTIC PROCESSING METHOD OF PRESSURE OR PRESSURELESS SINTERED CERAMIC BODY AND CERAMICS-MADE MOLDED MATERIAL FORMED BY THE METHOD

Abstract: There are disclosed a plastic processing method of the pressure or pressureless sintered ceramic body composed of at least one aluminum-containing compound selected from the group consisting of aluminum oxide, aluminum nitride and aluminum oxynitride and at least one hard compound selected from the group consisting of carbides, nitrides and oxides of titanium, zirconium, hafnium, vanadium, niobium, tantalum, chromium, molybdenum, tungsten and silicon and mutual solid solutions thereof, the content of said at least one aluminum-containing compound is 5 to 95 % by volume, comprising subjecting the ceramic body to plastic deformation at a temperature of l300 °C or higher, under a stress of l5 kg/mm² or smaller and at a strain rate of l0⁻³/sec or less in a reducing atmosphere or in vacuum, and a ceramics-made molded material comprising a composite ceramic body composed of the same as mentioned above.

Description: BACKGROUND OF THE INVENTION The present invention relates to a plastic processing method of a ceramic body and a ceramics-made molded material prepared by said plastic processing method and more specifically to a plastic processing method of a ceramic body in which the ceramic body is subjected to plastic deformation so that a ceramic product of complex configurations or large dimensions can be produced, for example, by applying pressing, forging or the like thereto and a ceramics-made molded material formed by said method and useful even at elevated temperatures or in a special environment such as an aqueous, acidic or alkaline solution. Pressure or pressureless sintered ceramic bodies have attracted attention in various industrial fields, as materials excellent in heat resistance, wear resistance and corrosion resistance. Due to extremely high hardness of these ceramic bodies, they have generally been worked into desired shapes, for example, by diamond polishing or the like. Therefore, pressure or pressureless sintered ceramic bodies have been accompanied by problems in their working such that they can hardly be produced as bodies of large dimensions or complex configurations and their working lead to increases to their production costs. These problems are serious particularly for Aℓ₂O₃, because this material is employed in the largest volume as a ceramic material having excellent heat resistance, hardness and corrosion resistance and moreover, an economical price. SUMMARY OF THE INVENTION An object of the present invention is, solving such problems involed in the prior art, to provide a plastic processing method of a ceramic body, in which the ceramic body is subjected to plastic deformation so as to permit application of pressing, foregoing or the like in much the same way as metals, and to provide, among the molded material which can be formed by said plastic processing method, a ceramics-made molded material which is useful particularly even at elevated temperatures or in a special environment such as in an aqueous acidic or alkaline solution, a molten salt bath and a radiation environment; is excellent in mechanical strength and have deformability as well as workability. The above and other objects, features and advantages of the present invention will become apparent from the following description and the appended claims, taken in conjunction with the accompanying drawing. In one aspect of this invention, there is thus provided a plastic processing method of a ceramic body, in which the sintered ceramic body is composed, as essential components thereof, of at least one aluminum-containing compound selected from aluminum oxide, aluminum nitride and aluminum oxynitride and at least one hard compound selected from the carbides, nitrides and oxides of titanium, zirconium, hafnium, vanadium, niobium, tantalum, chromium, molybdenum, tungsten and silicon and mutual solid solutions thereof, the content of said at least one aluminum-containing compound is 5 to 95 % by volume, and the ceramic body is subjected to plastic deformation at a temperature of l300°C or higher, under a stress of l5 kg/mm² or smaller and at a strain rate of l0⁻³/sec or less in a reducing atmosphere or in vacuum. Further, among the molded material obtained by plastic deforming and processing the pressure or pressureless sintered body, particularly, a ceramics-made molded material of the present invention comprises a molded material formed by plastic deforming and processing a composite ceramics body composed of an aluminum compound and a hard compound as essential components, and said sintered composite ceramic body having a transverse rupture strength of 80 kg/mm² or high er in a special environment selected from a high-temperature atmosphere, an aqueous acidic or alkaline solution, a molten salt bath and a radiation environment; wherein the aluminum compound as one of the essential components is contained in an amount of 5 - 95 % by volume and is at least one compound selected from aluminum oxide, aluminum nitride and aluminum oxynitride; and the remaining hard compound is at least one hard compound selected from the carbides, nitrides and oxides of titanium, zirconium, hafnium, vanadium, niobium, tantalum, chromium,molybdenum, tungsten and silicon and mutual solid solutions thereof. BRIEF DESCRIPTION OF THE DRAWING Figure l illustrates diagrammatically plastic deformation resistance of an Aℓ₂O₃-Ti(C 0.5 ,N 0.5 ) based hot pressed body at each of l300°C and l400°C as a function of the content of Ti(C 0.5 ,N 0.5 ) and shows single Aℓ₂O₃,Ti(C 0.5 ,N 0.5 ) ruptured but a wide composition region showing plastic deformation is present; Figure 2 is a front view of a ceramics-made molded material according to one embodiment of this invention, in which the molded material takes the form of a lock washer; Figure 3 is a side view of the ceramics-made molded material of Figure 2; and Figure 4 is a cross-sectional view of a ceramics-made molded material according to another embodiment of this invention, in which the molded material takes the form of a belleville spring. DESCRIPTION OF THE PREFERRED EMBODIMENTS The present inventors have carried out an extensive investigation with a view toward achieving the above-mentioned objects. In the course of the investigation, the following conceit came up to the mind. That is, when we think a plastic deformation of a metal as a general example, plastic deformation takes place owing to grain boundary sliding of crystal grains of the metal. This is attributed to metallic bonding which is one type of atomic bonding typical to metals. On the other hand, a ceramic body generally takes another type of atomic bonding which includes both ionic and covalent bonds in combination with some metallic bonds. From the viewpoint of easiness in plastic deformation, a ceramic body with a higher proportion of ionic bonds is preferred because the freedom of electrons is higher in ionic bonds like the above-described metallic bonds. However, a ceramic body containing ionic bonds in such a high proportion is low in high-temperature strength. As a result, it cannot withstand stresses which are applied to cause plastic deformation. Although a ceramic body containing covalent bonds in a high proportion is excellent in high-temperature strength. On the other hand, it has a property that its plastic deformation is difficult to induce. Namely, a ceramic body permitting plastic deformation is required to have at least a certain degree of strength prior to its plastic deformation. With the foregoing in view, the present inventors selected, as materials to be worked, ceramic bodies each of which was composed, at a predetermined volume ratio, of a metal compound containing ionic bonds in a high proportion and another metal compound containing covalent bonds in a high proportion so as to impart a desired degree of strength, namely, each of which contained ionic bonds, metallic bonds and covalent bonds at a desired ratio. In addition, the present inventors also found optimum ranges of various conditions for subjecting such sintered ceramic bodies to plastic deformation, leading to completion of this invention. As a result of the further investigations, the present inventors were interested with grain boundary sliding of crystalline grains in superplastic deformation of a metal because grain boundary sliding is said to take place in zirconia out of ceramics. However, zirconia is accompanied by such inconvenience as strength reduction at temperatures of 200 to 300 °C and at higher, it easily reacts with iron group metals, causes fatigue fracture in water and shows low thermal conductivity, high specific gravity and low hardness. Under the circumstances, zirconia has had limited applications as an engineering structural material at elevated temperatures. Namely, zirconia involves a problem that its application as a molded material is unsuitable in a special environment such as that described above. On the other hand, a majority of ceramics which are employed these days are alumina-based ones. If these alumina-based ceramics can be applied to molded materials, enormous advantage can be brought about in view of their properties as starting materials. With the foregoing in view, the present inventors proceeded with a further extensive investigation focused on ceramics bodies of the Aℓ compound base. As a result of the investigation, superplasticity attributable to heterogeneous grain boundary sliding was discovered. A specific material composition was chosen in the light of the superplasticity, thereby making it possible to apply the resultant material to molded materials such as those referred to in the present invention. As described above, the present invention features two matters, i.e., the composition of each ceramic body as a material to be worked and conditions for plastic deformation. First of all, the first feature, namely, the ceramic body contains as a first essential component at least one Aℓ-containing compound selected from alumina (Aℓ₂O₃), aluminum nitride (AℓN) and aluminum oxynitride [Aℓ(O,N)] each of which contains ionic bonds in a high proportion. Among these Aℓ-containing compounds, Aℓ₂O₃ is considered to be preferable because it contains ionic bonds in a particularly high proportion and has a high hardness and low specific density. The ceramic body is required to contain this Aℓ-containing compound in an amount of 5 to 95 % by volume. If its content does not fall within the above-defined range, it becomes difficult to adjust and control ionic bonds, metallic bonds and covalent bonds within their respective suitable proportion ranges. Preferably, the content of Aℓ₂O₃ may range from 40 to 70 % by volume. On the other hand, as the hard compound as a second essential component, no particular limitation is imposed so long as it is selected from the above-listed hard components. It is however preferable to choose a suitable hard compound in accordance with the proportions of ionic bonds and metallic bonds in the above-mentioned Aℓ-containing compound and the application field of the resulting pressure or pressureless sintered body. The above-mentioned hard compound is at least one hard compound selected from the carbides, nitrides and oxides of titanium (Ti), zirconium (Zr), hafnium (HF), vanadium (V), niobium (Nb), tantalum (Ta), chromium (Cr), molybdenum (Mo), tungsten (W) and silicon (Si) and mutual solid solutions thereof. The selection of a specific hard compound is effected by taking the ratio of ionic bonds to metallic bonds in its combined Aℓ-containing compound, required resilience, application environment and the like of the molded material into parallel consideration. As specific examples of this hard compound, may be mentioned TiC, ZrC, HfC, VC, NbC, TaC, Cr₃C₂, Mo₂C, WC and SiC; TiN, ZrN, HfN, VN, NbN, TaN, CrN and Si₃N₄; TiO, TiO₂, ZrO₂, HfO₂, Cr₂O₃, Ta₂O₅ and SiO₂; Ti(C,N), Ti(C,O), Ti(N,O), Ti(C,N,O), (Ti,Zr)(C,N), (Ti,Ta)C, (Ti,Nb)C, (Ti,Ta,W)C, and so on. The above hard compounds may be added either singly or in combination. It is particularly effective to add two or more hard compounds in the form of a solid solution in which the metal compounds are dissolved as solids in each other, because addition of such a solid solution results in the formation of a composite ceramic body havi ng improved strength. This improved strength is brought about because their addition in the form of the solid solution is effective in disappearance of pores during sintering. It is also preferable to use a Ti-containing metal compound in order to impart a low specific gravity, oxidation resistance and high strength to the resulting pressure or pressureless sintered body, or to use a Zr-containing metal compound in order to obtain a sintered body having high toughness and good thermal insulating property. Each ceramic body useful in the practice of this invention must contain the above Aℓ compound and hard compound as two essential components. Owing to the combination of these two components, a grain growth inhibitor effect is exhibited against both crystalline grains upon its sintering. The above-described sintered composite ceramic body can provide a pressure or pressureless sintered body of fine crystals by an incorporation of a grain growth inhibitor in addition to the above essential components, because the grain growth inhibitor can enhance the grain growth inhibiting effect. The grain growth inhibitor is composed of at least one compound selected from the oxides and nitrides of metals of Groups IIa, IIIa and VIII of the Periodic Table and rare earth elements and their mutual solid solutions. Its suitable content range may be 0.l to 7 % by volume. As specific examples of such a grain growth inhibitor, may be mentioned MgO, CaO, Sc₂O₃, Y₂O₃, NiO, CoO, FeO, Fe₂O₃, Fe₃O₄, La₂O₃, Ce₂O₃, Pr₂O₃, Nd₂O₃, Sm₂O₃, Eu₂O₃, Dy₂O₃, Er₂O₃, Tb₂O₃, Mg₃N₂, Ca₃N₂, ScN, YN, CeN, DyN, Y₃Fe₅O₁₂, NiFe₂O₄, MgFe₂O₄, LaFeO₃, etc. If the content of the grain growth inhibitor is smaller than 0.l % by volume, it is difficult to bring about its effect to any significant extent. On the other hand, if it is added in any amounts in excess of 7 % by volume, grain growth is conversely induced and moreover, fragile compounds are caused to segregate at grain boundaries. It is therefore not preferred to add the grain growth inhibitor in any amounts outside the above-specified range. The above-described ceramic body, which is useful as a material to be worked in accordance with this invention, can be produced easily by proportioning and kneading the above-mentioned respective compounds in their powder forms and then forming and sintering the resultant mixture in a manner known per se in the art. The strength of the resultant ceramic body has been significantly improved compared with the strength of sintered bodies obtained respectively by pressure or pressureless sintering the individual components separately. The mechanism of superplastic deformation of a pressure or pressureless sintered body can be attributed to sliding along crystalline grains boundaries as in the case of metals. More and more crystalline grains boundaries are thus formed to facilitate plastic deformation as the crystalline grains size of a ceramic body decreases. For these reasons, the crystalline grains size of a ceramic body may preferably be l µm or smaller. A description will next be made of the second feature of the method of this invention, namely, conditions for the plastic deformation of each ceramic body, specifically, the atmosphere, deformation temperature, stress and strain rate. It is necessary to carry out the plastic processing in a non-oxidizing atmosphere such as Ar or N₂ or in vacuum so as to avoid oxidation of the composite ceramic body and a mold employed for the ceramic body. Further, the deformation temperature is required to be l300 °C or higher. Any deformation temperature lower than l300 °C result in the development of cracks or fracture when a stress is applied. A range of l300 to l500 °C is preferred particularly for the prevention of oxidation of the composite ceramic body and over limitation of the mold strength. Next, the deformation stress is set at l5 kg/mm² or lower. If this stress exceeds l5 kg/mm², the mold is fractured and the ceramic body develops cracks. In order to avoid such inconvenience that expensive molds are fractured or cracks are developed in ceramic bodies, it is preferable to set this stress below l0 kg/mm². On the other hand, the strain rate is set as l0⁻³/sec or smaller. If the strain rate exceeds l0⁻³/sec, the composite ceramic body is fractured without undergoing deformation. Preferably, the strain rate may range from l0⁻⁵ to l0⁻³/sec. Here, the stress and strain rate can be achieved by a press or the like. In the case of a ceramics-made plastic material having a simple shape typified by the belleville spring 2, it can be easy provided by using a jig having a shape close to the final configuration of the intended product. Since these conditions are not independent from one another but are mutually correlated, it is preferable to set them at suitable values collectively. As a material for a mold useful in such a plastic deformation step, it is preferable to employ a material excellent in oxidation resistance, wear resistance and compressive strength. Graphite, Si₃N₄, SiC and the like may be mentioned specifically, with SiC being preferable. When a ceramic product of a complex shape is desired, it is effective to apply plastic deformation after polishing the surface of a ccorresponding ceramic body with grits or a grinding stone in advance because even after the deformation, the surface of the molded material is allowed to retain the same smoothness as its surface before the deformation. EXAMPLES Example l Using powdery raw materials which had been obtained by mixing Ti(C 0.5 ,N 0.5 ) powder in various proportions to Aℓ₂O₃ powder, the ceramic bodies of various compositions were produced by mixing, drying, molding and then hot-pressing said mixtures. From each of the ceramic bodies, specimens of 4 × 3 × 35 mm were prepared. Following the procedure of JIS R l60l "Bending of ceramics (l98l)", the bending plastic deformation strength of the specimens were measured respectively at room temperature, l300 °C and l400 °C in an Ar atmosphere. Results are diagrammatically shown in Figure l. As is apparent from Figure l, it has been confirmed that the transverse rupture strength of the complex materials is maximum at room temperature of about 60 % by weight of Ti(C 0.5 ,N 0.5 ) but the materials with 20 to 80 % by volume of Ti(C 0.5 ,N 0.5 ) exhibit plastic deformation at l400 °C, while it occurs within 30 to 60 % by weight at l300 °C. Examples 2 to ll Using starting raw material powders capable of yielding various Aℓ-containing compounds, hard compounds and grain growth inhibitor, a variety of samples were proportioned as shown in Table l. Those samples were mixed, dried, formed and hot-pressed to obtain sintered bodies of 3  × l5 mm and 3 × 4 × 30 mm. Various properties of those hot-pressed bodies are also shown in Table l. Of these hot-pressed bodies, those of 3  × l5 mm were caused to undergo plastic deformation in tensile test. On the other hand, the hot-pressed bodies of 3 × 4 × 30 mm were also caused to undergo plastic deformation in a compression test. The tensile test was carried out in accordance with the tensile test for metal materials in JIS (Japan Industrial Standard) Z 220l. In the tensile test, elongations (%) after rupture were measured. The compression test was conducted by following JIS R l60l. In the compression test, bending angles (°) until development of cracks or rupture were measured. In the tensile and compression tests, the degrees of deformation of the hot-pressed bodies [elongations (%) or bending angle s (°)] and the hardness and the bending strength of deformed parts were measured. Measurement results are shown in Table 2, along with conditions for the plastic deformation in the tensile and compression tests. Comparative examples l to 5 In the same manner as in Examples 2 to ll, ceramic bodies having various proportions as shown in Table l were obtained and the same measurements were carried out as in Examples 2 to ll. The results are shown in Tables l and 2. The molded materials shown in Table 2 of this invention are not limited to those containing an Aℓ compound and a hard compound only as their components but include those added further with a grain growth inhibitor (Examples 6 to ll). After polishing each of the surfaces of the ceramic bodies shown in Table l by a diamond grindstone, they were cause to undergo plastic deformation at elevated temperatures so that molded materials given in the column under "Application examples of molded material" in Table 2 were fabricated. Those produced as the belleville spring 2 had the following dimensions: outer diameter = 23 mm, inner diameter = 8 mm, thickness = 0.8 mm, and inclination = 5°. The thus-obtained molded materials were all able to satisfy the strength and other requirements specified by the Japan Industrial Standard (JIS). Especially, they did not show any appreciable reduction in strength even at elevated temperatures, for example, at ll00 °C and exhibited effective resilience. On the other hand, the compsite ceramic bodies of Comparative Examples l - 4 were fractured and could not prepared as molded materials. While in Comparative Example 5 plastic deformation could be carried out but the molded material lost its resilience at 600 °C or higher. In Figure 2 and Figure 3, a belleville spring prepared in Example l is shown and in Figure 4, a lock washer prepared in Example l is also shown. Referring first to Figure 2 and Figure 3, numeral l indicates a ceramics-made lock washer of a somewhat-twisted and approximately C-like configuration. Owing to the provision of the twisted shape and a slit, resilience has been imparted. On the other hand, Figure 4 illustrates a belleville spring 2, in which resilience has been imparted by its conical configuration. The lock washer l and belleville spring 2 are both made of ceramics as described above. They are each formed of a composite ceramic body composed of the aluminum compound and the hard compound in the aforesaid composition as essential components. The lock washer l shown in Figures 2 and 3 may be produced, for example, by the following two methods. In a first method, a composite ceramic body in the form of an approximately C-shaped ring with a slit is subjected, as a stock, to hot plastic deformation by means of a die. In a second method, a slit is formed in a presintered ring-like body so as to form the body into an approximately C-like shape. The pre-sintered C-like body is thereafter sintered, under a load, on a base the top surface of which has a shape conforming the intended lock washer. Thus, the first method is usually relied upon in view of surface finishing. Here, conditions for the plastic deformation of the sintered composite ceramic body, i.e., atmosphere, deformation temperature, stress and strain rate are important. The thus-obtained lock washer l has a strength of at least 80 kg/mm² in terms of bending strength up to l000 °C and is superb in heat resistance, oxidation resistance and chemical resistance. It can therefore exhibit its advantages in a special environment. Although the present invention was employed to fabricate lock washers, leaf springs, spring washer and compression springs in the Examples, it can of course be applied to fabricate volute springs, torsion springs and the like. Having now fully described the invention it will be apparent to one of ordinary skill in the art that many changes and modifications can be made thereto without departing from the spirit or scope of the invention as set forth herein. As clearly seen from the above explanation, in the method of this invention, the ceramic body having such a composition that ionic bonds, metallic bonds and covalent bonds are suitably contained in combination is used as a material to be worked and specific conditions such as those described above have been chosen for the plastic deformation of the thus-selected ceramic body. The ceramic body is allowed to undergo plastic deformation more easily compared with the use of a ceramic body containing ionic bonds in a high proportion such as alumina as is, because the ceramic body itself has an improved strength prior to its plastic deformation and contains, in a some proportion, ionic bonds capable of contributing to intergranular slip upon plastic deformation. Accordingly, use of the method of this invention makes it possible to perform pressing, foregoing or the like of ceramic bodies although such working has heretofore been considered to be extremely difficult. The method of this invention can therefore conduct with extreme easy the economical production of parts having large dimensions or complex configurations, for example, torsion materials such as cutting end mill blades; food extrusion feeders; hydraulic pump screws; screws for grain feeder pumps; fastening washers; turbine propellers; spinning thread guides; car rotors; cutters; scissors; magnetic tape slitters; heaters for heating element; etc. Moreover, the thus-deformed bodies can be obtained with smooth surfaces. Therefore, the method of this invention has an extremely large industrial value. Further, since the present invention is a ceramics-made molded material formed by plastic deformation processing of an Aℓ-containing compound series composite ceramics body, the following effects may be expected. First of all, sufficient formability and workability are recognized on the ceramics-made plastic material of this invention. Namely, the composite ceramic body may be provided as a primary stock. After grinding it into a secondary stock, working such as pressing, pulling, bending and/or the like may then be applied to the secondary stock by using conventional means such as press, jig, extruder and the like so that it is obtained as a final product. Secondly, owing to its sufficiently high mechanical strength, it can be used under a high load. This advantage has been brought about, since the selection of the specific composition as a composite ceramic body of mainly the Aℓ-containing compound has led to a high material strength. As a third advantage, it can be used in an expanded application field because it is usable in certain special environments. Owing to its high heat and corrosion resistance, it can be successfully used even in a special environment such as a high-temperature atmosphere, an aqueous acidic or alkaline solution, a molten salt bath or a radiation environment.

Claims: 1. In a plastic processing method of a pressure or pressureless sintered ceramic body, the improvement wherein the ceramic body is composed, as essential components thereof, of at least one aluminum-containing compound selected from the group consisting of aluminum oxide, aluminum nitride and aluminum oxynitride and at least one hard compound selected from the group consisting of carbides, nitrides and oxides of titanium, zirconium, hafnium, vanadium, niobium, tantalum, chromium, molybdenum, tungsten and silicon and mutal solid solutions thereof, the content of said at least one aluminum-containing compound is 5 to 95 % by volume, and the cer amic body is subjected to plastic deformation at a temperature of l300 °C or higher, under a stress of l5 kg/mm² or smaller and at a strain rate l0⁻³/sec or less in a reducing atmosphere or in vacuum. 2. A plastic processing method according to Claim l, wherein said aluminum compound is selected from the group consisting of Aℓ₂O₃, AℓN and Aℓ(O,N). 3. A plastic processing method according to Claim l, wherein said hard compound is selcted from the group consisting of TiC, ZrC, HfC, VC, NbC, TaC, Cr₃C₂, Mo₂C, WC and SiC; TiN, ZrN, HfN, VN, NbN, TaN, CrN and Si₃N₄; TiO, TiO₂, ZrO₂, HfO₂, Cr₂O₃, Ta₂O₅ and SiO₂; Ti(C,N), Ti(C,O), Ti(N,O), Ti(C,N,O), (Ti,Zr)(C,N), (Ti,Ta)C, (Ti,Nb)C and (Ti,Ta,W)C. 4. A plastic processing method according to Claim l, wherein the sintered ceramic body additionally contains at least one grain growth inhibitor, which is selected from the group consisting of oxides and nitrides of elements of group IIa, IIIa and VIII of the Periodic Table and rate earth elements and mutual solid solutions thereof, in an amount of 0.l to 7 % by volume. 5. A plastic processing method according to Claim 4, wherein said grain growth inhibitor is selected from the group consisting of MgO, CaO, Sc₂O₃, Y₂O₃, NiO, CoO, FeO, Fe₂O₃, Fe₃O₄, La₂O₃, Ce₂O₃, Pr₂O₃, Nd₂O₃, Sm₂O₃, Eu₂O₃, Dy₂O₃, Er₂O₃, Tb₂O₃, Mg₃N₂, Ca₃N₂, ScN, YN, CeN, DyN, Y₃Fe₅O₁₂, NiFe₂O₄, MgFe₂O₄ and LaFeO₃. 6. In a ceramics-made molded material formed of a composite ceramic body composed of an aluminum compound and a hard compound as essential components by plastic deformation processing, the improvement wherein the composite ceramic body has a bending strength of 80 kg/mm² or higher in a special environment selected from a high-temperature atmosphere, an aqueous acidic or alkaline solution, a molten salt bath and a radiation environment; the aluminum compound as one of the essential components is contained in an amount of 5 to 95 % by volume is at least one compound selected from the group consisting of aluminum oxide, aluminum nitride and aluminum oxynitride; and the remaining hard compound is at least one hard compound selected form the group consisting of carbides, nitrides and oxides of titanium, zirconium, hafnium, vanadium, niobium, tantalum, chromium, molybdenum, tungsten and silicon and mutal solid solutions thereof. 7. A ceramics-made molded material according to Claim 6, wherein said aluminum compound is selected from the group consisting of Aℓ₂O₃, AℓN and Aℓ(O,N). 8. A ceramics-made molded material according to Claim 6, wherein said hard compound is selcted from the group consisting of TiC, ZrC, HfC, VC, NbC, TaC, Cr₃C₂, Mo₂C, WC and SiC; TiN, ZrN, HfN, VN, NbN, TaN, CrN, and Si₃N₄; TiO, TiO₂, ZrO₂, HfO₂, Cr₂O₃, Ta₂O₅ and SiO₂; Ti(CN), Ti(C,O), Ti(N,O), Ti(C,N,O), (Ti,Zr)(C,N,), (Ti,Ta)C, (Ti,NB)C, and (Ti,Ta,W)C. 9. A ceramics-made molded material according to Claim 6, wherein the composite ceramic body contains 0.l to 7 % by volume of at least one grain growth inhibitor selected from the group consisting of oxides and nitrides of elements of Group IIa, IIIa, and VIII of the Periodic Table and rare earth elements and mutal solid solutions thereof. l0. A ceramics-made molded material according to Claim 9, wherein said grain growth inhibitor is selected from the group consisting of MgO, CaO, Sc₂O₃, Y₂O₃, NiO, CoO, FeO, Fe₂O₃, Fe₃O₄, La₂O₃, Ce₂O₃, Pr₂O₃, Nd₂O₃, Sm₂O₃, Eu₂O₃, Dy₂O₃, Er₂O₃, Tb₂O₃, Mg₃N₂, Ca₃N₂, ScN, YN, CeN, DyM, Y₃Fe₅O₁₂, NiFe₂O₄, MgFe₂O₄, and LaFeO₃ .

Inventors: ASAKAWA, MUTSUO TOSHIBA TUNGALOY CO., LTD., FUKAWA, AKIRA TOSHIBA TUNGALOY CO., LTD., FUKUHARA, MIKIO TOSHIBA TUNGALOY CO., LTD., KATSUMURA, YUJI TOSHIBA TUNGALOY CO., LTD., MIYAKAWA, ISAO TOSHIBA TUNGALOY CO., LTD., SAWADA, KAZUHIRO TOSHIBA TUNGALOY CO., LTD., URUSHIHATA, TOMIO TOSHIBA TUNGALOY CO., LTD.
Applicants: TOSHIBA TUNGALOY CO., LTD.
Application year: 1986
Main classification: C04B35
IPC codes: C04B35