SUPPORTED METAL CATALYSTS AND USE THEREOF

Abstract: A catalyst comprising a carrier on which as metal component iron, nickel, or cobalt promoted by zirconium is supported and, in addition, as promoter a noble metal from Group VIII of the Periodic Table; the promoted cobalt/zirconium catalyst is suitable for the preparation of hydrocarbons from carbon monoxide and hydrogen.

Description: The invention relates to activated catalysts for the preparation of hydrocarbons from hydrogen and carbon monoxide, comprising a carrier on which as metal component nickel or cobalt promoted by zirconium and platinum and/or palladium is supported. The preparation of hydrocarbons from a H₂/CO mixture by contacting this mixture with a catalyst at elevated temperatures and pressures is known in the literature as the Fischer-Tropsch synthesis. Catalysts often used for this purpose comprise one or more metals from the iron group supported on a carrier. A very active catalyst system consists of cobalt supported on a carrier, especially a silica carrier, and, as promoter, zirconium. The Fischer-Tropsch catalysts are suitably prepared by combining the active ingredients and the carrier, e.g. by precipitating the metal on the carrier from an aqueous solution of the metal or, preferably, by impregnating the carrier material with a compound of the metal in the presence of a liquid. Moreover, kneading techniques may be applied, especially if it is intended to prepare catalysts to be used in slurry reactors. In all preparation procedures the liquid is removed from the composition, followed by calcination and reduction. In the calcination step the impregnated metal compound is converted into one or more metal oxides. In order to be catalytically active in the conversion of carbon monoxide and hydrogen, it is necessary that a substantial amount of the metal oxide(s) is reduced under formation of the metal. The reduction is carried out in the presence of hydrogen usually at elevated temperatures, e.g. in the range of 200-300°C. It has been observed that when using silica as carrier, in some cases in the compositions to be used as catalysts metal hydrosilicates occur, which do not exhibit catalytic activity. Because the reduction of these hydrosilicates is laborious, or requires severe conditions, it has been investigated whether the formation of the said hydrosilicates can be minimized, or that their removal can be facilitated. It has now been found that by incorporating a specific further metal promoter in the catalyst the reduction step is considerably facilitated. This holds as well for catalysts in which silica is used as carrier and in which thus formation of hydrosilicates may occur, as for catalysts in which other carriers are used. The invention relates to an activated catalyst for the preparation of hydrocarbons from hydrogen and carbon monoxide, comprising a carrier on which as metal component nickel or cobalt promoted by zirconium and platinum and/or palladium is supported, characterized in that nickel or cobalt is present in the metallic state. The invention relates in particular to a catalyst comprising cobalt supported on a carrier and as promoters zirconium and platinum and/or palladium. A preferred catalyst comprises cobalt together with zirconium and platinum as promoter. Mixtures of platinum and palladium promoters may also be used, if desired. The amounts of cobalt and promoters prevailing in the catalyst may vary, but conveniently the catalyst preparation is performed in such a manner that the ultimate catalyst contains from 5-40 pbw cobalt, 0.25-50 pbw and in particular 0.5-25 pbw of zirconium and 0.0001-5 pbw, in particular 0.001-1 pbw of platinum and/or palladium promoters per 100 pbw of carrier. The carrier material in the catalysts according to the invention suitably consists of silica, silica-alumina or alumina. It is preferred to use silica, which preferably consists of silica per se, although carrier material containing, in addition to SiO₂, minor amounts of other materials such as alumina or alumina silicates may be used as well. The invention further relates to a method for the preparation of a cobalt, zirconium and platinum and/or palladium containing catalyst as hereinbefore defined. A preferred preparation method comprises the contacting of a porous carrier with a cobalt compound and with compounds of the promoters to be incorporated, in the presence of a liquid, e.g. water, followed by the removal of the liquid, e.g. by evaporation, calcination of the composition at elevated temper­ atures and subsequent reduction in the presence of hydrogen. The impregnation of the various metals in the carrier may proceed in successive steps or in a single treatment. Suitable calcination temperatures are in the range of 400-600°C, preferably between 450 and 550 °C. An advantage of the process according to the invention consists in that the reduction may be performed at a temperature which is substantially lower than that required in the reduction of catalysts that do not contain a platinum and/or palladium. In addition the reduction period adequate for the preparation of the catalysts according to the invention is significantly shorter than the period required in reducing calcined catalysts of the type known in the art. Suitable reduction temperatures are in the range of 50-300 °C. The reduction period may be between 30 minutes and 24 hours whereby it will be clear that if a relatively low temperature is selected, a relatively long reduction period will be required and vice versa. The invention further relates to a process for the preparation of hydrocarbons by contacting a mixture of carbon monoxide and hydrogen with a cobalt, zirconium and platinum and/or palladium containing catalyst, as hereinbefore defined. Preferably a silica-comprising catalyst is used. The feed for this process may have been obtained, for instance, from a heavy carbon-containing material such as coal by gasification, or from light hydrocarbons, such as natural gas by steam reforming or partial oxidation. Preferred reaction conditions are temperatures in the range of 125-350°C, in particular in the range of 175-275°C and pressures in the range of from 0.5 to 15 MPa, in particular in the range of from 1 to 10 MPa. A preferred embodiment of the process according to the invention consists in that the preparation of hydrocarbons from carbon monoxide and hydrogen is used as the first step in a two-step process for the preparation of middle distillates. To this end the hydrocarbon product, or at least that part of the product which has an initial boiling point above the final boiling point of the desired middle distillate fraction, is subjected to a catalytic hydrotreatment as the second step in the process. The catalytic hydrotreatment is suitably carried out by contacting the hydrocarbon material from the first step at elevated temperatures and pressures and in the presence of hydrogen with a catalyst comprising one or more metals having hydrogenation activity, supported on a carrier. In the hydrotreatment preference is given to the use of a catalyst comprising one or more metals from Group VIII, supported on a carrier. In particular, a catalyst is preferred comprising platinum on a carrier 13-15%w of which contains of alumina and the rest of silica. The preferred reaction conditions in the hydro­ treatment are temperatures in the range of 175-400°C, in particular in the range of 250-350°C, a hydrogen partial pressure of 1 to 25 MPa, in particular of 2.5 to 15 MPa, a space velocity of 0.1-5 kg.l⁻¹.h⁻¹, in particular of 0.25-2 kg.l⁻¹.h⁻¹ and a hydrogen/oil ratio of 100-5000 Nl.kg⁻¹, in particular of 250-2500 Nl.kg⁻¹. The invention is further illustrated with the following Example. EXAMPLE Catalyst preparation. Catalyst 1 A spherical silica carrier with an internal surface area of 112 m²/ml (bulk volume) and an external surface area of 15 cm²/ml (bulk volume) was dried at 120°C. The carrier was immersed during 15 sec in a solution of cobalt nitrate in ethanol and subsequently dried and calcined at 500°C. The treatment comprising of immer­ sion, drying and calcination was repeated. Subsequently the cobalt-loaded carrier was contacted with a solution of zirconium nitrate in water (pore volume impregnation). The carrier now loaded with cobalt and zirconium was calcined at 500°C. The composition of the catalyst was 10 Co/0.9 Zr/100 SiO₂, its internal surface area was 94 m²/ml (bulk volume) and its external surface area 15 cm²/ml (bulk volume). Catalyst 2 A portion of catalyst 1 was loaded with platinum by pore volume impregnation with an aqueous solution of Pt(NH₃)₄(OH)₂, followed by drying at 120°C and calcining at 500°C. The composition of the catalyst was 0.1 Pt/10 Co/0.9 Zr/100 SiO₂, its internal and external surface area were identical with those of catalyst 1. Catalyst testing Catalysts 1 and 2 were tested for the conversion of synthesis gas in a tubular reactor in which the catalyst was present in the form of a fixed bed with a bulk volume of 10 ml. Prior to the testing, the catalysts were reduced under the conditions as specified in the Table. The conditions prevailing during the conversion of synthesis gas were: Pressure : 2 MPa Ratio H₂/CO : 2 (v/v) GHSV (H₂+CO): 900 Nl.l⁻¹.h⁻¹ Further conditions and conversion results are given in the Table. As can be seen from these results, catalyst 2 was by far superior as regards space-time yield and synthesis gas conversion, and a lower rate of deactivation.

Claims: 1. An activated catalyst for the preparation of hydrocarbons from hydrogen and carbon monoxide, comprising a carrier on which as metal component nickel or cobalt promoted by zirconium and platinum and/or palladium is supported, characterized in that nickel or cobalt is present in the metallic state. 2. A catalyst as claimed in claim 1, comprising cobalt promoted by zirconium and platinum and/or palladium supported on a carrier 3. A catalyst as claimed in claim 1 or 2, characterized in that as additional promoter platinum is used. 4. A catalyst as claimed in claim 2 or 3, characterized in that the amount of cobalt is in the range of 5-40 pbw per 100 pbw of carrier, the amount of zirconium in the range of 0.25-50 pbw and the amount of platinum and/or palladium in the range of 0.0001-5 pbw, on the same basis. 5. A catalyst as claimed in claim 4, characterized in that the amount of zirconium is in the range of 0.5-25 pbw and the amount of platinum and/or palladium is in the range of 0.001-1 pbw per 100 pbw of carrier. 6. A catalyst as claimed in claims 1-5, characterized in that the carrier is a silica-, silica-alumina- or alumina-containing carrier, preferably a silica-containing carrier. 7. A method for the preparation of a catalyst as claimed in any of claims 2-6, characterized in that a porous carrier is contacted with a cobalt compound and with compounds of the promoters to be incorporated, in the presence of a liquid, followed by the removal of the liquid, calcination of the resulting composition at elevated temperature and reduction in the presence of hydrogen. 8. A method as claimed in claim 7, characterized in that the calcination is carried out at a temperature in the range of 450-550°C and the reduction at a temperature in the range of 50-300°C. 9. A process for the preparation of hydrocarbons by contacting a mixture of carbon monoxide and hydrogen with a catalyst as claimed in any of claims 1-6. 10. A process for the preparation of middle distillates in two steps, characterized in that the process as claimed in claim 9 is used as the first step and that as the second step at least that part of the product of the first step which has an initial boiling point above the final boiling point of the desired middle distillate fraction, is subjected to a catalytic hydrotreatment.

Inventors: DE JONG, KRIJN PIETER, GLEZER, JOHANNES HENRINA EVERARDUS, POST, MARTIN FRANCISCUS MARIA
Applicants: SHELL INTERNATIONALE RESEARCH MAATSCHAPPIJ B.V.
Application year: 1986
Main classification: B01J23
IPC codes: B01J23, C07C1, C07C67, C07B61