Polyether polymer or copolymer, monomer therefor, and process for production thereof

Abstract: A polyether polymer or copolymer with a pendant group of the formula in its molecule, said polymer or copolymer consisting essentially of (l) l to l00 mole% of recurring units re­ presented by the following formula (I) and (2) 0 to 99 mole % of at least one type of recurring units represented by the following formula (II) CH₂- H-O (II) and having a reduced viscosity η red , determined at 45°C in its 0.l% by weight benzene solution or at 80°C in its 0.l% by weight monochlorobenzene solution, of at least 0.0l; a process for producing thereof and novel epoxyether compound therefor.

Description: This invention relates to novel processes for producing solvent soluble polyether polymer or copolymer of the type in which a side chain having an oxirane group is pendant from a main chain having a polyether structure. DE-A-1,570, 547 discloses a process for the preparation of copolymers of monoepoxides and diepoxides, which are diglycidyl ethers, using an anionic organo aluminium catalyst. Various difunctional or higher oxirane compounds have been known and used in various applications. For example, diglycidyl ether of the following formula is known. Furthermore, diglycidyl ethers of bisphenols are known as epoxy resins. The two oxirane rings of these compounds have quite the same reactivity, and it is difficult to expect reaction of only one oxirane ring. Compounds having two or more oxirane rings having different reactivities are known. For example, there is known vinylcyclohexene diepoxide of the following formula having two oxirane groups. It is difficult however to perform ring-opening polymerization of only one of these oxirane rings completely selectively. Generally, in the polymerization of a monomer containing two or more groups having similar polymerizabilities as functional groups as in the above difunctional or higher oxirane compounds, crosslinking reaction occurs and the formation of an insoluble gelled product cannot be avoided. Accordingly, it is virtually impossible to obtain a high-molecular-weight polymer while keeping one of two functional groups, for example, still reactive. Hence, to obtain a polymer or copolymer having an oxirane group in a side chain, there has been exclusively used a method which comprises polymerizing a monomer having a vinyl polymerizable functional group and an oxirane group which have quite different reactivities, for example glycidyl methacrylate, in the presence of a radical initiator such as a peroxide. It has previously been known to synthesize a polymer having a main chain of a polyether structure by ring-opening polymerization of an oxirane compound. There has been no example known heretofore in which a solvent-soluble polyether polymer or copolymer of high molecular weight is obtained by ring-opening polymerization of a difunctional oxirane compound to polymerize one oxirane ring selectively while leaving the other oxirane ring unpolymerized as a side chain. Polymers or copolymers having an oxirane functional group in a side chain have attracted attention because various functions are expected owing to the presence of the oxirane functional group. Various attempts have been made in the past to polymerize monomers having functional groups. The present inventors have made investigations in order to develop a difuctional oxirane compound of a new type which serves to realize such expectation. These investigations have led to the discovery that a difunctional oxirane compound of the following formula (I-a) has unique reaction specificity in that the oxirane ring on the left end of the formula participates very selectively in its ring-opening polymerization by a polymerization catalyst in accordance with this invention which is described hereinafter, but the oxirane ring having a methyl substituent on the right end does not participate in the reaction but remains unchanged, and that no crosslinking reaction occurs in spite of its difunctionality. It has further been found that because of this reaction specificity, the difunctional oxirane compound of formula (I-a) does not form a solvent-insoluble gelled product by crosslinking reaction, and by the ring-opening polymerization catalyst in accordance with this invention, it can give a novel solvent-soluble reactive polyether polymer or copolymer of the type in which a group of the formula is pendant from a main chain of the polyether structure, and that the resulting polyether polymer or copolymer is very useful in such applications as an epoxy resin, a rubber or elastomeric material, an adhesive, a paint and a reactive polymer intermediate. The invention therefore provides a process for producing a polyether polymer or copolymer consisting essentially of (1) 5 to 100 mole% of recurring units of formula (I) and (2) 0 to 95 mole% of at least one type of recurring units of formula (II) wherein R represents hydrogen, substituted or unsubstituted C₁-C₁₈ alkyl, substituted or unsubstituted C₂-C₁₈ alkenyl, substituted or unsubstituted C₃-C₈ cycloalkyl or substituted or unsubstituted C₆-C₁₄ aryl, and having a reduced viscosity η red, determined at 45°C in its 0.1% by weight benzene solution or at 80°C in its 0.1% by weight monochlorobenzene solution, of at least 0.01 and the use of a polyether polymer or copolymer obtainable by such a process as an epoxy resin, a rubber or elastomeric material, an adhesive, a paint, or a reactive polymer intermediate. The difunctional oxirane compound 2,3-epoxypropyl-2',3'-epoxy-2'-methylpropyl ether of the following formula (I-a) used to produce the polymer or copolymer of this invention and used in the process of this invention can be synthesised by properly selecting ether synthesising means and oxirane ring forming means known per se . The compound of formula (I-a) can be synthesised by epoxidising the known compound, allyl methallyl ether of the formula with an oxidizing agent such as hydrogen peroxide or a peroxy acid. When hydrogen peroxide is used in this embodiment, the compound of formula (I-a) can be formed by contacting allyl methallyl ether with hydrogen peroxide in the presence of a weakly alkaline substance such as potassium hydrogen carbonate and a nitrile compound such as acetonitrile, optionally using a solvent such as methanol, to epoxidize allyl methallyl ether. Alternatively, the compound of formula (I-a) can be formed by contacting allyl methallyl ether with hydrogen peroxide in the presence of a catalyst, for example a compound of a metal such as selenium, tungsten, or molybdenum (e.g., selenium dioxide, a tungstic acid or a molybdic acid) to epoxidize allyl methallyl ether. In the practice of the first-mentioned epoxidization reaction, the amount of the weakly alkaline substance can be properly varied, but is, for example, 0.1 to 1 part by weight per part by weight of allyl methallyl ether. The amount of the nitrile compound used can also be properly varied. It is, for example, 1 to 10 moles per mole of the allyl methallyl ether. The amount of the solvent used can also be varied properly, and is, for example, 0 to 10 parts by weight per part by weight of allyl methallyl ether. The reaction temperature and time can also be properly varied. For example, the reaction temperature is 10 to 70°C, and the reaction time is 0.5 to 50 hours. The concentration and amount of hydrogen peroxide can also be varied properly. For example, an aqueous solution of hydrogen peroxide having a concentration of 10 to 60% by weight is used in an amount of 1 to 10 moles per mole of ally] methallyl ether. In the practice of the latter epoxidization reaction, the amount of the metallic compound catalyst can be properly chosen, and is, for example, 0.001 to 0.1 mole per mole of allyl methallyl ether. The reaction temperature and time can also be properly varied. For example, the reaction temperature is 20 to 90°C, and the reaction time is 0.5 to 50 hours. The concentration and amount of hydrogen peroxide can also be varied properly. For example, an aqueous solution of hydrogen peroxide having a concentration of 10 to 60% by weight is used in an amount of 0.1 to 10 moles per mole of allyl methallyl ether. When the peroxy acid is used in the above embodiment, the compound of formula (I-a) can be obtained by contacting ally] methallyl ether with the peroxy acid in the presence or absence of a solvent such as tetrahydrofuran, diethyl ether or methylene chloride to epoxidize it. Examples of the peroxy acid used include organic peroxy acids such as peroxyacetic acid, peroxybenzoic acid, and peroxyformic acid. The amount of the peroxy acid can be varied properly, and is, for example, 1 to 10 moles per mole of ally] methallyl ether. The amount of the solvent used can be varied properly, and is, for example, 0 to 100 parts by weight per part by weight of allyl methallyl ether. The reaction temperature and time can also be suitably selected. The reaction temperature is, for example, 0 to 60°C, and the reaction time is 1 to 100 hours. Alternatively the compound of formula (I-a) can be synthesized by utilizing a halohydrin method known per se . In this way, the compound of formula (I-a) can be synthesized by contacting a suspension of allyl methallyl ether in water with a halogen such as bromine or chlorine to form a halohydrin compound, and reacting the halohydrin compound with a suitable base such as slaked lime and sodium hydroxide to perform ring-forming reaction. The amount of water used in the halohydrin-forming reaction can be selected properly, and is, for example, 10 to 1,000 parts by weight per part by weight of allyl methallyl ether. The amount of the halogen can also be properly varied, and is, for example, 1 to 10 moles per mole of allyl methallyl ether. The reaction temperature and time can also be varied properly. For example, the reaction temperature is 10 to 80°C, and the reaction time is 0.5 to 50 hours. In the epoxidization reaction of the resulting halohydrin compound, the amount of the base used can be properly chosen, and is, for example, 1 to 10 moles per mole of allyl methallyl ether. The reaction temperature and time can also be properly chosen. For example, the reaction temperature is 10 to 100°C, and the reaction time is 0.5 to 70 hours. According to still another alternative, the compound of formula (I-a) can be produced by a method which does not go through the form of (I-b). In this embodiment, the compound of formula (I-a) can be obtained by etherifying a mixture of a suitable combination of an epihalohydrin with an alcohol, for example a combination of epichlorohydrin and beta-methyl allyl alcohol or a combination of beta-methylepichlorohydrin and allyl alcohol, using a phase transfer catalyst such as a quaternary ammonium salt or a crown ether and a suitable base such as sodium hydroxide or potassium hydroxide in the presence or absence of a solvent such as dimethyl-formamide, and epoxidizing the resulting ether compound. In the practice of this embodiment, the amount of the base used in the etherification reaction can be properly varied, and is, for example, 0.5 to 5 moles per mole of the halohydrin compound. The amount of the catalyst used can also be varied properly, and is, for example, 0.001 to 0.1 mole per mole of the halohydrin compound. The amount of the alcohol can also be suitably varied, and is, for example, 0.1 to 10 moles per mole of the halohydrin compound. The amount of the solvent which may be used can be varied properly, and is, for example, 0 to 100 parts by weight per part by weight of the halohydrin compound. The reaction temperature and time can also be properly chosen. For example, the reaction temperature is 10 to 80°C, and the reaction time is 0.5 to 50 hours. The epoxidization of the ether compound obtained by this reaction can be carried out also by the aforesaid methods, for example by using hydrogen peroxide or a peroxy acid, or by the reaction of forming a halohydrin compound. The compound of formula (I-a) has in its molecule two reactive oxirane rings having different reactivities. According to this invention, the use of the compound of formula (I-a) can lead to a polyether polymer or copolymer with a pendant group of the formula in its molecule and having a reduced viscosity η red , determined at 45°C in its 0.1% by weight benzene solution or at 80°C in its 0.1% by weight monochlorobenzene solution, of at least 0.01. In the present invention, the reduced viscosity η red of the polymer or copolymer is measured by the following method. As a solvent, benzene is used for the homopolymer and a copolymer with propylene oxide or other copolymers, which are easily soluble in it, and monochlorobenzene is used for copolymers soluble in benzene, with difficulty, for example a copolymer with epichlorohydrin. The homopolymer or the copolymer is dissolved in a concentration of 0.1% by weight in a benzene or monochlorobenzene solution containing 0.1% of 2,2'-methylenebis(4-methyl-6-t-butylphenol). Using the solution, the reduced viscosity of the polymer or copolymer is measured by means of an Ubbelohde viscometer at 45°C for the benzene solution and 80°C for the monochlorobenzene solution. In polymers produced according to the invention, the recurring units of formula (I) are derived by opening only the methyl-free oxirane ring of the two oxirane rings of the compound of formula (I-a) while the other methyl-containing oxirane ring being left unopen. The recurring units of formula (II) are derived by ring-opening of a monoepoxy compound of the following formula (III) wherein R is as defined with regard to formula (II). In the definition of R in formulae (II) or (III), examples of the C₁-C₁₈ alkyl group are methyl, ethyl, propyl, butyl, hexyl and dodecyl groups. These alkyl groups may have a substituent such as halogen, C₁-C₁₀ alkoxy, C₂-C₁₀ alkoxycarbonyl, C₂-C₁₀ acyl, C₁-C₁₀ alkylthio, and optionally substituted C₆-C₁₄ aryl. In the definition of R, examples of the C₂-C₁₈ alkenyl group are vinyl, allyl and butenyl. The alkenyl groups may have a substituent such as halogen, C₁-C₁₂ alkyl, C₁-C₁₀ alkoxy, C₂-C₁₀ alkoxycarbonyl, C₂-C₁₀ acyl and C₁-C₁₀ alkylthio. In the definition of R, example of the C₃-C₈ cycloalkyl group are cyclopropyl, cyclopentyl and cyclohexyl. The cycloalkyl groups may have a substituent such as halogen, C₁-C₁₂ alkyl, C₁-C₁₀ alkoxy, C₂-C₁₀ alkoxycarbonyl, C₂-C₁₀ acyl and C₁-C₁₀ alkylthio. In the definition of R, examples of the C₆-C₁₄ aryl group are phenyl and naphthyl. The aryl groups may have a substituent such as halogen, C₁-C₁₂ alkyl, C₁-C₁₀ alkoxy, C₂-C₁₀ alkoxycarbonyl, C₂-C₁₀ acyl and C₁-C₁₀ alkylthio. The novel polyether polymer or copolymer has a reduced viscosity η red , determined at 45°C in its 0.1% by weight benzene solution or at 80°C in its 0.1% by weight monochlorobenzene solution, of at least 0.01. The polymer composed only of the recurring units of formula (I) or polymers composed substantially of the recurring units of formula (I) with less than 1 mole% [namely, the proportion of the recurring units of formula (I) exceeding 99 mole%] of the recurring units of formula (II) preferably have a reduced viscosity η red , determined at 45°C in their 0.1% by weight benzene solution, of 0.01 to 2, particularly 0.05 to 2. Copolymers composed of less than 99 mole% of the recurring units of formula (I) and more than 1 mole% (the total 100 mole %) of the recurring units of formula (II) preferably have a reduced viscosity η red , determined at45°C in their 0.1% by weight benzene solution or at 80°C in their 0.1% by weight monochlorobenzene solution, of 0.01 to 5, especially 0.05 to 3. In the case of the copolymers, suitable mole ratios for the intended uses may be selected. For example, when the copolymers are to be used as epoxy resins, it is preferred to adjust the proportion of the recurring unit of formula (I) to at least 30 mole%. For use as a rubber or elastomeric material, the copolymer preferably contains about 5 mole%, or amounts near it, of the recurring unit of formula (I). Such a preferred ranges of the proportion of the recurring units of formula (I) can be preselected and prescribed easily by experiments according to the purpose of use and the type of the recurring units of formula (II) According to the process of the invention the polyether polymer or copolymer is produced by polymerizing the compound of formula (I-a) or copolymerizing the compound of formula (I-a) and a monoepoxy compound of formula (III), in the presence of, as a catalyst, a heat-reaction product of (A) an organotin compound and (B) a complete or partial ester compound of (HO)₃PO which is disclosed in U.S.-A-.3,773,694 in the presence or absence of a solvent and at a temperature of from 10 to 80°C. When, for example, the diepoxy compound of formula (I-a) is polymerized by using organoaluminum-water containing catalysts heretofore well known as a catalyst for ring-opening polymerization of a broad range of oxirane compounds, crosslinking reaction proceeds rapidly, and the solvent-soluble polyether polymer of this invention cannot be obtained. The heat-reaction products used as catalysts in the process of the invention are heat-reaction products of (A) organotin compounds and (B) complete or partial ester compounds of (HO)₃PO, said organotin compounds (A) being selected from compounds of the following formulae (i) to (iv) R 1 / aSnX 4-a (i) wherein R¹ represents a C₁-C₁₂ alkyl group, such as methyl, ethyl, propyl, hexyl and dodecyl, unsubstituted or substituted by a substituent selected from halogen, hydroxy, C₁-C₁₀ alkoxy and C₁-C₁₀ alkylthio, a C₂-C₈ alkenyl group, such as vinyl and allyl, unsubstituted or substituted by a substituent selected from halogen, hydroxy, C₁-C₁₀ alkoxy, C₁-C₁₀ alkylthio, and optionally substituted C₆-C₁₄ aryl, a C₃-C₈ cycloalkyl group, such as cyclopropyl, cyclopentyl or cyclohexyl, unsubstituted or substituted by a substituent selected from halogen, hydroxy, C₁-C₁₂ alkyl, C₁-C₁₀ alkoxy, C₁-C₁₀ alkylthio and optionally substituted C₆-C₁₄ aryl, a C₆-C₁₄ aryl group, such as phenyl and naphthyl, unsubstituted or substituted by a substituent selected from halogen, hydroxy, C₁-C₁₂ alkyl, C₁-C₁₀ alkoxy, C₁-C₁₀ alkylthio and optionally substituted C₆-C₁₄ aryl, or a C₇-C₁₈ aralkyl group, such as benzyl or phenylethyl, unsubstituted or substituted by a substituent selected from halogen, hydroxy, C₁-C₁₂ alkyl, C₁-C₁₀ alkoxy and C₁-C₁₀ alkylthio; X represents an atom or group selected from halogen atoms such as Cl, Br, I or F, C₁-C₁₂ alkoxy groups, aryloxy groups having C₆-C₁₈ aryl, acyloxy groups having C₂-C₁₂ acyl and residues of partial esters of phosphoric acid; and a is an integer of 1 to 4; provided that when a is an integer of 2 to 4, R¹ groups may be identical or different, and when a is 1 or 2, the X's may be identical or different. R 1 / bSnO c (ii) wherein R¹ is as defined with regard to formula (i), b is 1 or 2, and when b is 1, c is 3/2 or when b is 2, c is 1, the compound of formula (ii) may form a complex with the compound of formula (i). R²(R 1 / 2SnOSnR 1 / 2)R² (iii) wherein R¹ is as defined with regard to formula (i), R² is as defined with regard to R¹ and X, and the two R² groups may be identical and different. (R 2 / 3Sn) d X' (iv) wherein R² is the same as defined with regard to formula (iii) provided that at least one of the three R² groups is a group selected from the groups defined for R¹ in formula (i); X' is a member selected from the group consisting of a carbonate group, a phosphorus or oxyacid group, a polybasic carboxylic acid group and a residual moiety of a polyhydric alcohol; and d is a number greater than 1 and corresponds to the basicity of the member X'. Preferably, (B) is a compound represented by the following formula (R³O)₃P=O wherein R³ represents a member selected from the class consisting of a hydrogen atom, C₁-C₁₂ alkyl groups C₂-C₁₂ alkenyl groups and C₃-C₈ cycloalkyl groups which may be substituted by halogen, and at least one of the R³ groups represents groups other than the hydrogen atom. In the organotin compound (A) selected from the compounds of formulae (i) to (iv), specific examples of the compounds of formula (i) are (C₂H₅)₄Sn, (C₆H₅)₄Sn, (CH₃)₃SnF, (C₄H₉)₃SnCl, (CH₃)₃SnBr, (C₈H₁₇)₃SnCl, (CH₃)₂SnF₂, (C₄H₉)₂SnCl₂, (C₁₂H₂₃)₂SnBr₂, (cyclo-C₆H₁₁)₂SnI₂, (C₄H₉)SnF₃, (C₈H₁₇)SnCl₃, (C₄H₉)₃SnOC₄H₉, (C₈H₁₇)₃SnOCOCH₃, (C₈H₁₇)₂Sn(OCOC₁₇H₃₅)₂, and Specific examples of the compounds of formula (ii) are (CH₃)₂SnO, (C₄H₉)₂SnO, (C₈H₁₇)₂SnO, (C₆H₅)₂SnO, CH₃SnO 3/2 , and C₄H₉SnO 3/2 . Examples of the complex of the compound of formula (i) and the compound of formula (ii) include (CH₃)₂SnO·(C₂H₅)₂SnBr₂, (CH₃)₂SnO·(CH₃)₂SnCl₂, and CH₃[(CH₃)₂SnO]₂CH₃·(CH₃)₂SnBr₂. Specific examples of the compounds of formula (iii) are (CH₃)₃SnOSn(CH₃)₃, Cl(C₄H₉) ₂SnOSn(C₄H₉)Cl, and (CH₃COO)(C₆H₅)Sn(C₆H₅)(CH₃COO). Specific examples of the compounds of formula (iv) include [(CH₃)₃Sn]₂CO₃, [(C₄H₉)₃Sn]₂CO₃, (C₄H₉)₃SnOP(O)(OC₈H₁₇)₂, [(C₈H₁₇)₃Sn]₃PO₄, (C₄H₉)₃SnOCH₂CH₂OSn(C₄H₉)₃, (C₄H₉)₂(CH₃O)Sn-OCO(CH₂)₄OCO-Sn(OCH₃)(C₄H₉)₂, and Specific examples of the compounds of formula (R³O)₃P=O include (C₂H₅)₃PO₄, (C₃H₇)₃PO₄, (C₄H₉)₃PO₄, (C₈H₁₇)₃PO₄, (CH₂=CH-CH₂)₃PO₄, (C₆H₁₁)₃PO₄, (ClCH₂-CH₂)₃PO₄, (Cl₂C₃H₅)₃PO₄, (C₂H₅)₂HPO₄, (C₄H₉)₂HPO₄, (C₄H₉)H₂PO₄. The heat-reaction product of (A) the organotin compound and (B) the complete or partial ester compound of (HO)₃PO used as the catalyst can be synthesized by the means known from U. S.-A-.3,773,694. For example, it can be obtained in the form of a condensation product by heating the compound (A) and the compound (B) at a temperature of about 150 to 300°C. As required, a high boiling hydrocarbon such as liquid paraffin can be used as a solvent. The ratio of the compound (A) to the compound (B) used in the formation of the heat-reaction product can be properly selected over a wide range. For example, the ratio of (A):(B), as the ratio of Sn atoms to P atoms, is from 1:10 to 10:1. In the catalyst producing reaction, various relatively simple substances are formed and liberated by condensation reaction depending upon the types of the compounds (A) and (B). The resulting condensation product exhibits the desired activity at various degrees of condensation. The optimum degree of condensation varies depending upon the types of the compounds (A) and (B) and the ratio between them, but can be easily predetermined experimentally. Generally, the condensation product is soluble in solvents such as hexane and benzene in the early stage, but becomes insoluble as the condensation reaction proceeds. According to this invention, there is provided a process for producing a polyether polymer or copolymer with a pendant group of the formula in its molecular and consisting essentially of (1) 5 to 100 mole% of recurring units of formula (I) and (2) 0 to 95 mole% of at least one type of recurring units of formula (II) and having a reduced viscosity η red , determined at 45°C in its 0.1% by weight benzene solution or at 80°C in its 0.1% by weight monochlorobenzene solution, of at least 0.01, which comprises polymerizing 2,3-epoxypropyl-2',3'-epoxy-2'-methylpropyl ether of the following formula (I-a) or copolymerizing a mixture of it with a compound of the following formula (III) wherein R is as defined with regard to formula (II), in the presence of, as a catalyst, the above known heat-reaction product of (A) the organotin compound and (B) the complete or partial ester compound of (HO)₃PO. Specific examples of the monoepoxy compound (III) used include ethylene oxide, propylene oxide, butylene oxide, butadiene monooxide, vinylcyclohexane oxide, styrene oxide, epichlorohydrin, epibromohydrin, allyl glycidyl ether, butyl glycidyl ether, phenyl glycidyl ether, naphthyl glycidyl ether, glycidyl acetate, glycidyl propionate, glycidyl benzoate, glycidyl cinnamate and glycidyl naphthenoate. They may be used singly or in combination. Thus, structural units of formula (II) composed of two or more monomers above may be present in the same polymer chain in the polyether copolymer of this invention. The polymerization or copolymerization may be carried out by contacting the compound of formula (I-a) or a mixture of it with at least one compound of formula (III) in the presence of the aforesaid heat-reaction product as a catalyst in the presence or absence of a solvent. Since the reaction proceeds even at room temperature, heating is not specially required, and the polymerization or copolymerization is carried out at a temperature of 10°C to 80°C. Preferably, the reaction is carried out with stirring or shaking. In the practice of the reaction, the presence of an unnegligible amount of water in the reaction system is inconvenient. Hence, the presence of water in the reaction system is desirably minimized. The amount of the catalyst may be properly varied, and is, for example, 0.01 to 1 part by weight per 100 parts by weight of the compound of formula (I-a) or the monomeric mixture of the compound of formula (I-a) and the compound of formula (III). The reaction pressure may be atmospheric pressure or reduced or elevated pressure, inclusive of an autogeneous pressure. Usually, pressures ranging from atmospheric pressure to 50 kg/cm² are employed. In this invention, a solvent may be optionally present in the polymerization system. A great variety of solvents can be used in this invention. Examples include aliphatic hydrocarbons such as heptane, kerosene, n-paraffin and hexane, aromatic hydrocarbons such as benzene and toluene; halogenated hydrocarbons such as methylene chloride, chloroform, carbon tetrachloride and monochlorobenzene, ketones such as acetone and methyl ethyl ketone, ethers such as diethyl ether, di-isopropyl ether, di-n-propyl ether, di-n-butyl ether, tetrahydrofuran and dioxane, and esters such as ethyl acetate and butyl acetate. The polyether polymer or copolymer is useful, for example, as an epoxy resin, a rubber or elastomeric material, an adhesive, a paint, or a reactive polymer intermediate. The following examples illustrate the present invention in more detail. EXAMPLE 1 (Reference) Compound of formula (I-a) A flask equipped with a reflux condenser, a thermometer and a stirrer was charged with 300 ml of methanol, 331 g (8.0 moles) of acetonitrile, 150 g (1.3 moles) of allyl methallyl ether and 107 g of potassium hydrogen carbonate, and with stirring at 50°C, 402 ml (3.5 moles) of a 30% by weight aqueous solution of hydrogen peroxide was added dropwise over 6 hours. After the addition, the mixture was maintained at the same temperature for 3 hours. After the reaction, the reaction mixture was cooled, and 500 ml of cold water was added. The mixture was extracted with five 150 ml portions of methylene chloride, three 100 ml portions of water, three 100 ml portions of 0.1N sodium thiosulfate, and finally with three 100 ml portions of water, dried over sodium sulfate, and distilled under reduced pressure to give 160 g (yield 83%) of 2,3-epoxypropyl-2',3'-epoxy-2'-methylpropyl ether. The properties and NMR spectral data of the product are shown below. Physical properties bp : 85 °C/8 mmHg d 25 / 4 : 1.069 n 25 / D : 1.4396 Assignment of NMR spectrum Solvent: CDCl₃; internal standard TMS δ : 1.35 (3H, s, a) 2.45 - 2.90 (4H, m, b) 2.90 - 3.35 (1H, m, c) 3.35 - 4.15 (4H, m, d). The infrared absorption spectrum of the resulting product is shown in Figure 1. EXAMPLE 2 A three-necked flask equipped with a stirrer, a thermometer and a distillation device was charged with 12.5 g of dibutyltin oxide and 26.6 g of tributyl phosphate. With stirring in a stream of nitrogen, the compounds were heated at 250°C for 20 minutes, and the distillate was removed. A solid condensation product was obtained as a residue. The inside of a 50 ml glass ampoule was purged with nitrogen, and the ampoule was charged with 40 mg of the condensation product obtained as above and 15 g of 2,3-epoxypropyl-2',3'-epoxy-2'-methylpropyl ether having a concentration of less than 10 ppm , and the ampoule was sealed up. With shaking, the compound was reacted at 40°C for 48 hours. After the reaction, the reaction mixture was poured into 100 ml of hexane containing 0.5% by weight of 2,2'-methylenebis(4-methyl-6-t-butylphenol, and immersed overnight. Hexane was then removed by decantation, and the residue was washed twice with 100 ml of the same hexane as used above, and then dried to give 12.7 g (yield 85%) of a polymer. The polymer had a reduced viscosity, measured at 45°C in its 0.1% by weight benzene solution, of 0.45 and an epoxy equivalent of 142 (theory 144). The infrared absorption spectrum of the polymer is shown in Figure 2, and the nuclear magnetic resonance spectrum, in Figure 3. EXAMPLE 3 Tributyltin chloride (10.5 g) and 17.4 g of tributyl phosphate were put in the same flask as used in Example 2. With stirring in a stream of nitrogen, the mixture was heated at 250°C for 30 minutes, and the distillate was removed. A solid condensation product was obtained as a residue. The same polymerization as in Example 2 was carried out except that 25 mg of the resulting condensation product was used as the catalyst and the polymerization was carried out at 80°C for 6 hours. There was obtained 12.2 g (yield 81%) of a polymer having a reduced viscosity, determined at 45°C in its 0.1% by weight benzene solution, of 0.09 and an epoxy equivalent of 143. EXAMPLE 4 Diphenyltin dichloride (11.0 g) and 16.9 g of tributyl phosphate were put in the same flask as used in Example 2. With stirring in a stream of nitrogen, the mixture was heated at 250°C for 35 minutes, and the distillate was removed. A solid condensation product was obtained as a residue. The same polymerization as in Example 2 was carried out except that 25 mg of the resulting condensation product was used as the catalyst and the polymerization was carried out at 30°C for 60 hours. There was obtained 11.8 g (yield 79%) of a polymer having a reduced viscosity, determined at 45°C in its 0.1% by weight benzene solution, of 0.92 and an epoxy equivalent of 145. EXAMPLE 5 Dibutyltin oxide (10.0 g) and 23.4 g of tributyl phosphate were fed into a three-necked flask equipped with a stirrer, a thermometer and a distillation device. With stirring in a stream of nitrogen, they were heated at 260°C for 15 minutes, and the distillate was removed. A solid condensation product was obtained as a residue. The inside of a 50 ml glass ampoule was purged with nitrogen, and 30 mg of the condensation product, a mixture of 12 g of 2,3-epoxypropyl-2',3'-epoxy-2'-methylpropyl ether and 20 g of propylene oxide having a water content of less than 10 ppm were charged into it. The ampoule was sealed up, and with shaking, the mixture was maintained at 40°C for 50 hours. After the reaction, the reaction mixture was put into 100 ml of methanol containing 0.5 % by weight of 2,2'-methylenebis(4-methyl-6-t-butylphenol and immersed overnight. Methanol was removed by decantation, and the residue was washed twice with 100 ml of methanol and then dried under reduced pressure at 100°C for 8 hours to give 29 g of a tacky rubbery polymer. The mole ratios of the monomers charged, the reaction conditions, and the composition of the resulting copolymer are shown in Table 1. The infrared absorption spectrum of the resulting copolymer is shown in Figure 4, and its ¹H NMR spectrum, in Figure 9. EXAMPLES 6-9 Using the same catalyst as used in Example 5, the same copolymerization as in Example 5 was repeated under the conditions indicated in Table 1. The compositions of the resulting copolymers, determined by ¹H NMR spectroscopy, are shown in Table 1. The infrared absorption spectra of the copolymers obtained in Examples 6 to 9 are shown in Figures 5 to 8, respectively, and the ¹H NMR spectrum of the copolymer obtained in Example 6, in Figure 10. Example 5 6 7 8 9 Monomer charged (mole %) 2,3-Epoxypropyl-2',3'-epoxy-2'-methylpropyl ether 20 30 80 5 40 Propylene oxide 80 - 20 - - Epichlorohydrin - 70 - - - Glycidyl acetate - - - 95 - Styrene oxide - - - - 60 Amount of the catalyst (g/mole of monomer) 0.07 0.06 0.08 0.05 0.09 Reaction temperature (°C) 40 45 50 50 50 Reaction time (hours) 50 50 70 60 70 Copolymer produced Yield (%) 91 89 65 70 78 Reduced viscosity, η red 2.48 0.82 0.15 0.35 0.78 Composition as monomers (mole %) 2,3-Epoxypropyl-2',3'-epoxy-2'-methylpropyl ether 18 21 75 4 31 Propylene oxide 84 - 25 - - Epichlorohydrin - 79 - - - Glycidyl acetate - - - 96 - Styrene oxide - - - - 69

Claims: A process for producing a polyether polymer or copolymer consisting essentially of (1) 5 to 100 mole% of recurring units of formula (I) and (2) 0 to 95 mole% of at least one type of recurring units of formula (II) wherein R represents hydrogen, substituted or unsubstituted C₁-C₁₈ alkyl, substituted or unsubstituted C₂-C₁₈ alkenyl, substituted or unsubstituted C₃-C₈ cycloalkyl or substituted or unsubstituted C₆-C₁₄ aryl, and having a reduced viscosity η red, determined at 45°C in its 0.1% by weight benzene solution or at 80°C in its 0.1% by weight monochlorobenzene solution, of at least 0.01 which process comprises polymerising 2,3-epoxypropyl-2'3'-epoxy-2'-methylpropyl ether of formula (I-a) or copolymerising it with a compound of formula (III) wherein R represents hydrogen, substituted or unsubstituted C₁-C₁₈ alkyl, substituted or unsubstituted C₂-C₁₈ alkenyl, substituted or unsubstituted C₃-C₈ cycloalkyl or substituted or unsubstituted C₆-C₁₄ aryl, in the presence of, as a catalyst, a heat-reaction product of (A) an organotin compound and (B) a complete or partial ester compound of (HO)₃PO, said organotin compound (A) being selected from compounds of the following formulae (i) to (iv) R 1 / aSnX 4-a (i) wherein R¹ represents a C₁-C₁₂ alkyl group unsubstituted or substituted by a substituent selected from halogen, hydroxy, C₁-C₁₀ alkoxy and C₁-C₁₀ alkylthio, a C₂-C₈ alkenyl group unsubstituted or substituted by a substituent selected from halogen, hydroxy, C₁-C₁₀ alkoxy, C₁-C₁₀ alkylthio, and optionally substituted C₆-C₁₄ aryl, a C₃-C₈ cycloalkyl group unsubstituted or substituted by a substituent selected from halogen, hydroxy, C₁-C₁₂ alkyl, C₁-C₁₀ alkoxy, C₁-C₁₀ alkylthio and optionally substituted C₆-C₁₄ aryl, a C₆-C₁₄ aryl group unsubstituted or substituted by a substituent selected from halogen, hydroxy, C₁-C₁₂ alkyl, C₁-C₁₀ alkoxy, C₁-C₁₀ alkylthio and optionally substituted C₆-C₁₄ aryl, or a C₇-C₁₈ aralkyl group unsubstituted or substituted by a substituent selected from halogen, hydroxy, C₁-C₁₂ alkyl, C₁-C₁₀ alkoxy and C₁-C₁₀ alkylthio; X represents an atom or group selected from halogen atoms, C₁-C₁₂ alkoxy groups, aryloxy groups having C₆-C₁₈ aryl, acyloxy groups having C₂-C₁₂ acyl and residues of partial esters of phosphoric acid; and a is an integer of 1 to 4, provided that when a is an integer of 2 to 4, R¹ groups may be identical or different, and when a is 1 or 2, the X's may be identical or different; R 1 / bSnO c (ii) wherein R¹ is as defined with regard to formula (i), b is 1 or 2, and when b is 1, c is 3/2 or when b is 2, c is 1, the compound of formula (ii) may form a complex with the compound of formula (i); R²(R 1 / 2SnOSnR 1 / 2)R² (iii) wherein R¹ is as defined with regard to formula (i), R² is as defined with regard to R¹ and X, and the two R² groups may be identical and different; and (R 2 / 3Sn) d X' (iv) wherein R² is the same as defined with regard to formula (iii) provided that at least one of the three R² groups is a group selected from the groups defined for R¹ in formula (i); X' is a member selected from a carbonate group, a phosphorus or oxyacid group, a polybasic carboxylic acid group and a residual moiety of a polyhydric alcohol; and d is a number greater than 1 and corresponds to the basicity of the member X', in the presence or absence of a solvent and at a temperature of from 10 to 80°C. A process according to claim 1 wherein the complete or partial ester compound (B) is a compound of formula (R³O)₃P=O wherein R³ represents hydrogen, C₁-C₁₂ alkyl, C₂-C₁₂ alkenyl or C₃-C₈ cycloalkyl which may be substituted by halogen, and at least one R³ is other than hydrogen. A process according to claim 1 or 2 for producing a polymer or copolymer consisting essentially of from 30 to 100 mole% of recurring units of formula (I) and 0 to 70 mole% of at least one type of recurring units of formula (II). A process according to any one of the preceding claims wherein in the definition of R' in formula (II), the substituent on alkyl is selected from halogen, C₁-C₁₀ alkoxy, C₂-C₁₀ alkoxycarbonyl, C₂-C₁₀ acyl, C₁-C₁₀ alkylthio, and optionally substituted C₆-C₁₄ aryl; and the substituent on alkenyl, cycloalkyl or aryl is selected from halogen, C₁-C₁₂ alkyl, C₁-C₁₀ alkoxy, C₂-C₁₀ alkoxycarbonyl, C₂-C₁₀ acyl and C₁-C₁₀ alkylthio or wherein recurring units of formula (II) are derived from a glycidyl compound which is glycidyl acetate, glycidyl propionate, glycidyl benzoate, glycidyl cinnamate or glycidyl naphthonate. A process according to any one of the preceding claims for producing a polymer or copolymer having a reduced viscosity η red of 0.01 to 5.

Inventors: MIURA KATSUHITO, NAKATA TATSUYA, MIURA, KATSUHITO, NAKATA, TATSUYA
Applicants: DAISO CO LTD, DAISO CO., LTD.
Application year: 1986
Main classification: C08G59
IPC codes: C07D303, C08G59