AQUEOUS SUSPENSIONS OF MIXTURES OF INORGANIC PIGMENTS

Abstract: There is disclosed an aqueous suspension containing at least 55% by weight of a mixture of inorganic pigments, which mixture comprises calcium sulphate and at least one other pigment, wherein the or at least one of said at least one other pigment is a pigment which has been treated, prior to its incorporation into the suspension, with a dispersing agent which is (i) a phosphate ester or (ii) a water-soluble salt of polyacrylic acid at least 15% of the carboxylic acid groups of which are esterified. Also disclosed is a paper coating composition which comprises a dispersion of a mixed pigment in an aqueous medium containing an adhesive, wherein the mixed pigment constitutes at least 55% by weight of the composition and wherein the mixed pigment comprises calcium sulphate and at least one other pigment, wherein the or at least one of said at least one other pigment is a pigment which has been tre­ ated, prior to its incorporation into the suspension, with a dispersing agent which is (i) a phosphate ester or (ii) a water-­ soluble salt of polyacrylic acid at least 15% of the carboxylic acid groups of which are esterified.

Description: AQUEOUS SUSPENSIONS OF MIXTURES OF INORGANIC PIGMENTS This invention relates to aqueous suspensions of mixtures of inorganic pigments and, more particularly but not exclusively, is concerned with mixtures of inorganic pigments in which one component is calcium sulphate and another component is kaolin and/or calcium carbonate. The invention is particularly concerned with aqueous suspension of mixtures of inorganic pigments for use in paper coating compositions. Many varieties of coated papers are produced today. They are principally coated with a composition, sometimes known as the coating colour, which essentially comprises an adhesive, also known as a binder, and a pigment. A discussion of the constituents of paper coating compositions and of the methods of applying such compositions to paper is given in Chapter XIX, Volume III, of the 2nd Edition of the book by James P. Casey entitled "Pulp and Paper: Chemistry and Technology". The adhesive used can be, for example, starch, casein or a synthetic resin latex; the particular adhesive used will depend, for example, on the printing process to be used, e.g. offset lithography requires the adhesive to be waterinsoluble. Generally, the pigment will consist of clay together with an amount, which may be up to 60% by weight, of one or more other constituents, for example calcium carbonate, calcium sulphate, lithopone, barium sulphate, titanium pigments, talc or satin white. In many cases a paper coating composition containing two or more inorganic pigments has improved properties as compared with a composition containing only one pigment. For example, a first pigment might confer on a paper coating composition the property of providing a highly glossy coating, but, on the other hand, might render the coating composition very viscous, while a second pigment on its own might give inferior glossing properties but have the property of forming a very fluid aqueous suspension, containing a high concentration of the pigment. A paper coating composition containing a mixture of the two pigments in appropriate proportions would have a balance of good gloss and acceptable rheological properties. Unfortunately, however, it is often difficult to prepare aqueous suspensions of two or more inorganic pigments because one pigment may interfere with another pigment or with the dispersing agent used to deflocculate that other pigment. This problem is especially prevalent when one of the pigments is calcium sulphate because calcium sulphate is soluble in water to the extent of about 2.4 grams of calcium sulphate per litre of water, and the calcium ion is well known for its property of coagulating colloidal particles in aqueous suspension. If a deflocculated aqueous suspension of calcium sulphate is mixed with a suspension containing either kaolin or calcium carbonate deflocculated with a conventional dispersing agent, the phenomenon known in the paper coating art as "shock" is often observed. Shock may be defined as a rapid and pronounced increase in the viscosity of an aqueous suspension containing one or more inorganic pigments. This increase in viscosity is especially serious when it occurs in a paper coating composition since the composition will generally contain at least 60% by weight of inorganic pigment. The addition of only a small proportion of calcium sulphate, typically from 1 to 5% by weight, based on the weight of the other pigments, is sufficient to induce shock. Increasing the proportion of calcium sulphate in the mixture may reduce the ViSCff- sity of the suspension slightly but it is still very difficult to prepare a suspension which contains a high percentage by weight of the mixture of pigments and yet has an acceptable viscosity. DE-A-3203067 describes the use of carboxymethyl cellulose, either alone or in combination with starch, oxidised starch or a synthetic polymer, as a dispersing agent for calcium sulphate when used as the sole inorganic pigment in a paper coating composition. A paper coating composition can be formed which contains a high proportion by weight of calcium sulphate and at the same time has an acceptable viscosity. According to one aspect of the present invention, there is provided an aqueous suspension containing at least 55% by weight of a mixture of inorganic pigments, which mixture comprises calcium sulphate and at least one other pigment, wherein the or at least one of said at least one other pigment is a pigment which has been treated, prior to its incorporation into the suspension, with a dispersing agent which is (i) a phosphate ester or (ii) a water-soluble salt of polyacrylic acid at least 15% of the carboxylic acid groups of which are esterified. An aqueous suspension of the present invention will have a relatively low viscosity, and may be used in the manufacture of paper coating compositions. Accordingly, in another aspect the present invention provides a paper coating composition which comprises a dispersion of a mixed pigment in an aqueous medium containing an adhesive, wherein the mixed pigment constitutes at least 55% by weight of the composition and wherein the mixed pigment comprises calcium sulphate and at least one other pigment, wherein the or at least one of said at least one other pigment is a pigment which has been treated, prior to its incorporation into the suspension, with a dispersing agent which is (i) a phosphate ester or (ii) a watersoluble salt of polyacrylic acid at least 15% of the carboxylic acid groups of which are esterified. Preferably, the composition of this aspect of the present invention comprises at least 60% by weight of total solids, i.e. dry mixed pigments plus dry adhesive. Advantageously the mixture of inorganic pigments comprises calcium sulphate (e.g. gypsum) and either one or both of calcium carbonate and kaolin. Preferably the calcium sulphate is also treated with a dispersing agent which is (i) a phosphate ester or (ii) a water-soluble salt of polyacrylic acid at least 15% of the carboxylic acid groups of which are esterified, prior to its incorporation into the aqueous suspension. The phosphate ester dispersing agent is advantageously a phosphate ester having the formula: EMI4.1 wherein R1 and R2 are the same or different and each is an alkyl group, an aryl group, an aralkyl group or an alkaryl group. Preferably the alkyl, aryl, aralkyl or alkaryl group does not contain more than 10 carbon atoms. When the dispersing agent is a water soluble salt of polyacrylic acid of which at least 15% of the carboxylic acid groups are esterified, the ester groups are advantageously derived from, for example, an alkyl alcohol, an aralkyl alcohol or a phenol. Preferably, the alkyl alcohol, aralkyl alcohol or phenol does not contain more than 10 carbon atoms. The quantity of the dispersing agent used is preferably in the range 0.2 to 5.0% by weight, based on the weight of dry pigment. The suspension is preferably prepared by mixing an aqueous suspension of calcium sulphate with an aqueous suspension of said at least one other pigment. The invention will now be illustrated by the following Examples. EXAMPLE 1 (COMPARATIVE) A kaolin clay having a particle size distribution such that 80% by weight of the particles had an equivalent spherical diameter smaller than 2 microns was mixed with sufficient water to form a suspension containing 56% by weight of dry kaolin and with 0.3* by weight, based on the weight of dry kaolin, of a sodium polyacrylate dispersing agent having a number average molecular weight of 1650. A ground natural gypsum having a particle size distribution such that 70% by weight of the particles had an equivalent spherical diameter smaller than 2 microns was mixed with sufficient water to form a suspension containing 56% by weight of dry gypsum and with 3% by weight, based on the weight of dry gypsum, of sodium carboxymethylcellulose (CMC), as a dispersing agent for the gypsum. The two suspensions were mixed in various proportions by weight by adding the gypsum suspension to the kaolin with hand mixing. The mixing was continued for 2 minutes after all the gypsum had been added and the viscosity of the mixed suspension was measured by means of a Brookfield Viscometer at a spindle speed of 100 rpm. The viscosity of the kaolin suspension alone and of the gypsum suspension alone was also determined in the same way. The results are set forth in Table 1. TABLE 1 Pasts by weight of Kaolin Gypsum Viscositv mPa.s. 100 0 70 0 100 530 99 1 5000 95 5 9150 90 10 6250 70 30 2550 50 50 1250 These results show that the addition of only 1% by weight of the gypsum suspension to the kaolin suspension causes pronounced shock. If the proportion of gypsum is increased above 10% by weight the viscosity begins to decrease again but is in each case considerably greater than the viscosity of the kaolin suspension alone. EXAMPLE 2 (COMPARATIVE) The experiment of Example 1 was repeated except that the gypsum was treated with 1% by weight of CMC and 2% by weight of starch, both based on the weight of dry gypsum, in accordance with the disclosure of DE-A-3203067. The results are set forth in Table 2. TABLE 2 Parts by weight of Kaolin Gypsum Viscosity mPa.s. 100 0 61 0 100 71 99 1 6000 95 5 9800 90 10 7800 70 30 2800 50 50 1290 The degree of shock experienced with this this system of dispersing agents is seen to be no less than that observed in Example 1. EXAMPLE 3 (COMPARATIVE) The experiment of Example 1 was repeated except that the sodium polyacrylate dispersing agent used for the kaolin was replaced by 0.3% by weight, based on the weight of dry kaolin, of a dispersing agent which consisted of a water soluble salt of a copolymer of acrylic acid and a second monomer having the formula: EMI7.1 The results are set forth in Table 3. TABLE 3 Parts by weight of Kaolin Gypsum Viscosity mPa.s. 100 0 60 0 100 530 99 1 9300 95 5 4400 90 10 2950 70 30 1180 50 50 1070 The degree of shock is slightly reduced, as compared with the results of Example 1 and 2, but is still very pronounced. EXAMPLE 4 The experiment of Example 1 was repeated except that the sodium polyacrylate dispersing agent used for the kaolin was replaced by 0.365% by weight, based on the weight of dry kaolin, of a sodium salt of a polyacrylic acid which was partly esterified with beta-hydroxy-propanol and comprised the following renaatina units: EMI8.1 Approximately 33% of the carboxylic acid groups were esterified. The results are set forth in Table 4. TABLE 4 Parts by weight of Kaolin Gypsum Viscosity mPa.s. 100 0 54 0 100 480 99 1 5500 95 5 3600 90 10 2400 70 30 1150 50 50 1000 The degree of shock experienced by the suspension of mixed pigments is significantly reduced. EXAMPLE 5 The experiment of Example 1 was repeated except that the sodium polyacrylate dispersing agent used for the kaolin was replaced by 4% by weight, based on the weight of dry kaolin, of a phosphate ester of type A, namely The results are set forth in Table 5. TABLE 5 Parts bv weight of Kaolin GYpsum Viscosity Pa.s. 100 0 470 0 100 580 99 1 1560 95 5 1250 90 10 1160 70 30 930 50 50 600 The degree of shock experienced by the suspension has been reduced to a very small value. EXAMPLE 6 The experiment of Example 1 was repeated except that the sodium polyacrylate dispersing agent used for the kaolin was replaced by 4% by weight, based on the weight of dry kaolin, of a phosphate ester of type B, namely The results are set forth in Table 6. TABLE 6 Parts by weight of Kaolin Gypsum Viscosity mPa.s. 100 0 500 0 100 680 99 1 690 95 5 680 90 10 750 70 30 1350 50 50 1380 In this case shock was completely eliminated. EXAMPLE 7 The experiment of Example 1 was repeated except that the sodium polyacrylate dispersing agent used for the kaolin was replaced by 4% by weight, based on the weight of dry kaolin, of a phosphate ester of type A, namely and the CMC dispersing agent used for the gypsum was replaced by 2.6% by weight, based on the weight of dry gypsum, of the same phosphate ester of type A. The results are set forth in Table 7. TABLE 7 Parts by weight of Kaolin Gypsum Viscosity mPa.s. 100 0 480 0 100 55 99 1 1170 95 5 1300 90 10 1180 70 30 980 50 50 820 A very small degree of shock was observed. EXAMPLE 8 The experiment of Example 1 was repeated except that the sodium polyacrylate dispersing agent used for the kaolin was replaced by 4% by weight, based on the weight of dry kaolin, of a phosphate ester of type B, namely and the CMC dispersing agent used for the gypsum was replaced by 2% by weight, based on the weight of dry gypsum, of the same phosphate ester of type B. The results are set forth in Table 8. TABLE 8 Parts by weight of Kaolin Gypsum Viscosity mPa.s. 100 0 510 0 100 112 99 1 170 95 5 170 90 10 230 70 30 155 50 50 125 In this case shock was substantially completely eliminated. EXAMPLE 9 (CONPARATIVl) The experiment of Example 1 was repeated, 0.3% by weight, based on the weight of dry kaolin, of the same sodium polyacrylate dispersing agent being used for the kaolin, but the CMC dispersing agent used for the gypsum being replaced by 2.6% by weight, based on the weight of dry gypsum, of a phosphate ester of type A, namely The results are set forth in Table 9. TABLE 9 Parts by weight of Kaolin Gypsum Viscosity iPa.s. 100 0 69 0 100 66 99 1 + 10,000 95 5 90 10 70 30 50 50 In this case a very serious degree of shock was observed showing that the kaolin must be treated with a dispersing agent in accordance with the invention before mixing with the gypsum suspension. EXAMPLE 10 A ground natural calcium carbonate having a particle size distribution such that 86% by weight consisted of particles having an equivalent spherical diameter smaller than 2 microns was mixed with sufficient water to form a suspension containing 56% by weight of dry calcium carbonate and with 2% by weight, based on the weight of dry calcium carbonate, of a phosphate ester of type A, namely The same ground natural gypsum as was used in Examples 1 - 9 was mixed with sufficient water to form a suspension containing 56% by weight of dry gypsum and 3% by weight, based on the weight of dry gypsum, of CMC as a dispersing agent for the gypsum. The viscosity of the calcium carbonate suspension alone and of the gypsum suspension alone was measured by neans of a Brookfield Viscometer at a spindle speed of 100 rpm. The two suspensions were them mixed in various proportions by weight by adding the gypsum suspension to the calcium carbonate suspension with hand mixing. The mixing was continued for 2 minutes after all the gypsum had been added and the viscosity of the mixed suspension was measured by means of the Brookfield Viscometer. The results are set forth in Table 10. TABLE 10 Parts by weight of Calcium Carbonate Gypsum Viscosity mPa.s. 100 0 180 0 100 380 99 1 327 95 5 2700 90 10 2400 70 30 2200 50 50 2300 Only a very small degree of shock was observed. EXAMPLE 11 The experiment of Example 10 was repeated except that the CMC dispersing agent for the gypsum was replaced by 2.6% by weight, based on the weight of dry gypsum, of the same phosphate ester of type A as was used for the calcium carbonate. The results are set forth in Table 11. TABLE 11 Parts by weight of Calcium Carbonate Gypsum Viscosity mPa.s. 100 0 227 0 100 55 99 1 660 95 5 925 90 10 910 70 30 820 50 50 800 Again the degree of shock observed was very small. EXAMPLE 12 The experiment of Example 10 was repeated except that the type A phosphate ester dispersing agent for the calcium carbonate was replaced by 2% by weight, based on the weight of dry calcium carbonate, of a phosphate, ester of type B, namely and the CMC dispersing agent for the gypsum was replaced by 1.25% by weight, based on the weight of dry gypsum, of the same phosphate ester of type B. The results are set forth in Table 12. TABLE 12 Parts by weight of Calcium Carbonate Gypsum Viscosity mPa.s. 100 0 40 0 100 70 99 1 47 95 5 50 90 10 50 70 30 53 50 50 55 In this case shock was completely eliminated. EXAMPLE 13 (COMPARATIVE} The experiment of Example 10 was repeated except that the type A phosphate ester dispersing agent for the calcium carbonate was replaced by 0.38 by weight, based on the weight of dry calcium carbonate, of the same sodium polyacrylate as was used in Example 1, and the CMC dispersing agent for the gypsum was replaced by 2.6% by weight, based on the weight of dry gypsum, of a type A phosphate dispersing agent, namely The results are set forth in Table 13. TABLE 13 Parts by weight of Calcium Carbonate Gypsum Viscosity mPa.s. 100 0 30 0 100 160 99 1 2200 95 5 1920 90 10 1680 70 30 1540 50 50 1640 In this case a significant degree of shock was observed. It should be noted that commercial paper coating compositions generally contain at least 60% by weight of dry pigment. In the above Examples the aqueous suspensions were prepared at a dry solids content of only 56% by weight in order to ensure that the visosity was measurable over the complete range of proportions by weight of gypsum to the other pigment.

Claims: CLAIMS: 1. An aqueous suspension containing at least 551 by weight of a mixture of inorganiic pigments, which mixture comprises calcium sulphate and at least one other pigment, wherein the or at least one of said at least one other pigment is a pigment which has been treated, prior to its incorporation into the suspension, with a dispersing agent which is (i) a phosphate ester or (ii) a water-soluble salt of polyacrylic acid at least 15% of the carboxylic acid groups of which are esterified. 2. A suspension as claimed in Claim 1, wherein the mixture of inorganic pigments comprises (a) calcium sulphate and (b) calcium carbonate and/or kaolin. 3. A suspension as claimed in Claim 1 or 2, wherein the dispersing agent is a phosphate ester having the formula: EMI15.1 wherein R1 and R2 are the same or different and each is an alkyl group, an aryl group, an aralkyl group or an alkaryl group. 4. A suspension as claimed in any of Claims 1 to 3, wherein the calcium sulphate has been treated, prior to its incorporation into the suspension, with a dispersing agent which is (i) a phosphate ester or (ii) a water soluble salt of polyacrylic acid at least 15% of the carboxylic acid groups of which are esterified. 5. A paper coating composition which comprises dispersion of a mixed pigment in an aqueous medium containing an adhesive, wherein the mixed pigment constitutes at least 55% by weight of the composition and wherein the mixed pigment comprises calcium sulphate and at least one other pigment, wherein the or at least one of said at least one other pigment is a pigment which has been treated, prior to its incorporation into the suspension, with a dispersing agent which is (i) a phosphate ester or (ii) a watersoluble salt of polyacrylic acid at least 15% of the carboxylic acid groups of which are esterified.

Inventors: REID, PAUL IAN, WATERS, BRIAN ROGER
Applicants: ECC INTERNATIONAL LIMITED
Application year: 1986
Main classification: C09C1
IPC codes: C09C3, C09C1, D21H19, C09D7, C09D17