REACTIVE ION ETCHING DEPOSITION APPARATUS AND METHOD OF USING IT

Abstract: The cathode (31) in a reactive ion etching and deposition apparatus is in the form of a single plate having a matrix of cylindrical hollows (37) therein, each hollow producing a hollow cathode glow when the apparatus is energised. The aspect ratio (largest dimension of each hollow cross-section/depth of the hollow) is preferably at least 1.5. In operation of the apparatus, an RF voltage is applied between the cathode and an evacuated chamber in which the cathode is disposed through a suitable matching network. A plasma gas is supplied from a point outside the cathode and a suitable pumping system is used to maintain operating pressures in the 0.1 to 400 millitorr range.

Description: This invention relates to a reactive ion etching and deposition apparatus comprising a hollow cathode structure. Radio Frequency (RF) sputtering is a technique which is well known and described well in the literature (B Chapman, "Glow Discharge Process", J Wiley and Sons, NY, 1980, page 139-173). It is a type of diode sputtering with a cathode electrode, an effective anode, and a plasma within a vacuum chamber. The electrodes are typically driven at high voltage (1000-1500 volts) and high fre­ quency (13.56 megahertz). The plasma is formed by the high voltage induced breakdown of the gas in the chamber, and typically assumes a plasma potential near ground, which is the potential of the chamber walls. The cathode electrode is bombarded at high energy by ions in the plasma during the "negative" portion of the applied voltage and by electrons during the "positive" part. Thus, no net charge flows through the cathode electrode. The cathode electrode is sputtered by the high energy ion bombardment. This sputtering is used either for erosion of samples on the cathode surface, or net deposition on samples placed on an opposing surface with suitable support. Reactive Ion Etching is a technique which adds a chemical reaction to this ion bombardment process. Certain gases, such as freon, oxygen and silane, etc, are chemically active with a number of common materials used in device fabrication (silicon, quartz, polyimide, etc). When used in an RF sputtering system, these reactive gases cause additional etching of the surface (over sputte­ ring alone) by chemically combining with surface atoms and forming a volatile species which leaves the surface and can be pumped away. Typically, the operating pressure and gas flow rate would be higher in a reactive ion etching device as compared to a simple RF device alone, but the underlying operation of the plasma would be similar and dominated by the RF applied voltages. Recently, a related device has been developed (C Horwitz, Applied. Physics Letter, Vol 43, 1983, page 977), which used a hollow cathode glow to enhance the plasma in the RF plasma. This device was characterized under similar operating conditions to a regular RF device, and produced higher etch rates. An article entitled "Variable Angle Dry Etching with a Hollow Cathode" by C M Horwitz, Applied Physics Letters, Vol 44, (June 1984) describes forming a hollow cathode within two spaced elect­ rodes. In another article by C M Horwitz entitled" Hollow Cathode Reactive Sputter Etching - A New High Rate Process", Applied Physics Letters, Vol 43 (Nov 1983), page 977, he describes a hollow cathode system developed primarily for use in sputtering (or sputter etching) and not particularly for reactive ion etching. The invention seeks to provide a reactive ion etching and deposition apparatus which is capable of relatively low voltage, high current density operation. A reactive ion etching and deposition apparatus comprising a cathode disposed in an evacuable chamber, is characterised, according to the invention, by the cathode being of a form providing a matrix of hollows in its front side and a plain rear side. How the invention can be carried into effect will now be described by way of example, with reference to the accompanying drawings, in which: Figure 1 comprises a cross sectional view of a simplified reactive ion sputter/etching system comprising a hollow cathode structure disposed within a vacuum chamber; Figure 2 comprises a simplified cross sectional view of a reactive ion etching system similar to Figure 1 showing an alterna­ tive hollow cathode structure; Figure 3 is a graph illustrating etching rates of a polyimide film in a reactive ion etching apparatus; Figure 4 is a graph similar to Figure 3 illustrating a similar etching reaction with variations in the active gas pressure; Figure 5 represents a cross section of a hollow cathode structure suitable for use in apparatus embodying the invention; Figure 6 is a perspective view of the hollow cathode plate of Figure 5; Figure 7 is a cross sectional view of one of the individual hollow cathode regions or buckets within the plate of Figure 6; and Figures 8 through 11 are graphs illustrating the difference of deposition rates between a single planar electrode (not a hollow cathode structure) and the bucket electrodes of Figure 6, and also illustrating the effect of different pressures within the reaction chamber. A dual layer metallic cathode 15 for a RF-RIE sputter/etching system is shown in Figure 1. An operating embodiment of the device is in a system having 12.7 cm (5 inch) diameter electrodes, so all of the parameters to be described below are consistent with that size system. The electrode consists of two metal disks (12.7 cm diameter) separated by a distance of a few centimeters (1-3). The disks are electrically and structurally connected by narrow metal supports 16 around their outer rim. The connection could also be made by broader supports or walls, but there must be sufficient openings to allow substantial gas flow to the volume between the electrode disks. This is described further later in the specifi­ cation. The electrode structure has been tested with disk sets of Mo, Cu, C and SiO2 with similar results. Other metal or dielectric materials may be appropriate for the reactive ion etching or deposi­ tion of particular materials. An RF energizing voltage is applied to this electrode set 15. This can be done in a number of ways, and is shown schematically here as simply one electrical connection to the bottom electrode. The other connection would be typically to the containment vessel 20 either directly or through ground. An RF power supply 17 of the same type used to drive prior art RF systems is used to supply a potential to the electrodes through a typical matching network 18 (B Chapman op. cit.). Gases 22 are supplied to the system from outside the electrodes and a suitable pumping system shown schematically as 23 is required to allow operating pressures in the 0.1 to 400 millitorr range. Samples 24 are then placed on either of the inside electrode surfaces for etching. The dual electrodes form an effective hollow cathode between their surfaces. Plasma formed in that region is characterized by a sheath at both electrode surfaces. Electrons which are emitted from the electrode surface (due to ion bombardment) are accelerated into the plasma across the sheath. They are repelled, however, by the sheaths at both cathode surfaces, and thus are not able to escape from the discharge region. These entrapped electrons cause a high level of ionization of the gas and very dense plasma between the electrodes. This effect is what is known classically as a hollow cathode glow. In the RF mode, this plasma is characterized by a very low impedance, allowing a high effective current flow at relatively modest power levels. The low plasma impedance is also characterized by a low voltage on the electrodes. Operation is initiated by backfilling the system with one of the reactive gases listed above to a pressure ranging from 2.7 to 53 Pa (20 to 400 millitorr). The scaling of the system with pressure will be discussed below. Applying RF power to the electrode will initiate breakdown of the gas and form a plasma. With electrode spacing dimensions of 1-3 centimeters, the initial RF voltage will be 600-1000 volts until the discharge is initiated (less than 1 sec.), and then the voltage will drop dramatically. The RF voltage can be estimated by the magnitude of the DC bias voltage on the electrodes. The RF peak voltage should be at least 2 times the DC bias voltage. The DC bias can be measured with a meter and is always negative with respect to ground due to the fact that ions are swept out of the area much faster than electrons. The RF oscillates around this negative potential rather than ground. For the structure of FIG. 1 there is a dimensional criticality in order to obtain the requisite intense hollow cathode glow. This criticality may be termed an aspect ratio and may be defined in terms of the dimensions of the hollow cathode electrode structure as the largest dimension of one of the planar electrodes (i.e., a diameter for a circular plate, or a diagonal for a square or rectan­ gular plate) divided by the separation of the plates. This ratio should be equal to or larger than 4. A number of reactive ion etching reactions can be markedly enhanced by employing the hollow cathode technique. Two specific cases are described below, that of polyimide and silicon etching in particular gases, wherein the increase in etch rate is clearly illustrated. Many other etching reactions are possible, however, such as quartz, other types of resists, copper, chromium and other metals. The techniques will be exactly the same, and only the gas combinations will be different. Polyimide Etching Polyimide films are well known polymers, and include any such polymers having an -imide linkage in the backbone or in the side chain of the polymer. These materials are commercially available under several different trade names, and are well known in the packaging of electronic circuits. These films are valued for their high thermal stability and excellent electrical properties. They have high heat resistance, good dielectric properties, are solvent­ resistive, and can be applied by simple processing. While they are often used in molding and composite industries, the electronics industry uses them extensively as thin films. The etching rate of polyimide by prior art techniques (RIE and RF) is in the range of 90 to 120 nm per minute at 300 watts RF. Using the herein disclosed hollow cathode RF electrodes, and with an applied RF power of 300 watts and a peak RF voltage of 200 volts in a gas combination of 10% freon in oxygen at pressures of 20 to 40 Pa (150-300) millitorr, and a DC bias voltage of -100 VDC, the erosion rate of polyimide on Si was 2-4 microns per minute. Increasing the power to 1000 watts, the erosion rate was 10-20 microns per minute, depending on the sample temperature. The lower values are charac­ teristic of room temperature, the higher values characteristic of 100°C. Silicon Etching With a gas combination of 10% oxygen in Freon at pressures of 13.3 to 40 Pa (100-300 millitorr), the etch rate of silicon samples 24 in the hollow cathode RF electrodes was approximately 2 microns per minute at 500 watts applied power as compared to a prior art rate of 60 nm per minute. The DC bias was again low, -75 VDC. The sample temperatures were 50 to 100°C. The peak RF voltage was 150 volts. The DC bias voltages are extremely low, as compared to the normal RF system. This very low voltage, which signifies very low ion energies at very high currents, is the dominant useful feature for enhanced RIE etching rates. The low voltages are also very important to reduce or eliminate metal contamination of the samples by sputtering. At high voltages, there is a sizeable amount of material being sputtered from the electrode surfaces. Due to the low process voltages, the choice of materials for the electrodes is not critical. A straightforward extension in this area is to add additional layers of electrodes to produce multiple hollow cathode glows. This is shown schematically for the case of just one additional electrode in Figure 2. In this figure, the additional electrode, labeled 15', has been mounted above the two electrodes of Figure 1. The new electrode is supported and electrically connected to the previous electrodes by additional support 16. Devices of this type have been constructed and operated in similar modes to the earlier devices and the relevant operating voltages and etching rates measured. The operation of this multiple hollow cathode RF electrode is similar to the case of the single pair RF electrode described previously. Etching rates, comparing a single hollow cathode (2 electrodes) with a double hollow cathode (3 electrodes) are shown in Figure 3. As can be seen in Figure 3, the etching rates for a double hollow cathode are approximately one half the etch rates for a single hollow cathode at the same power level. This is due to an effective sharing of the input power between the two plasmas between the electrodes. The extension to higher numbers of electrodes has also been demonstrated, and the etch rates measured follow similar scaling to the case of a double hollow cathode. The development of this multiple cathode dependance is quite important to the proces­ sing area, particularly for multiple wafer etching. The reduction in etch rate due to the multiple plasmas can be compensated for simply by increasing the applied power level. An equivalent control over the rate of operation is in the choice of the relative sizes of the hollow cathode electrodes and the enclosing chamber, which is usually the vacuum chamber 20. This enclosing chamber 20 functions as the counterelectrode in the RF plasma, and the effective DC bias on the hollow cathode electrodes is related to the ratio of the electrode versus counterelectrode area. By choosing a suitable enclosure dimension, the hollow cathode glow effect can be optimized for high rate, or the degree of isotropy versus anisotropy, which is a function of the operating voltage. At high chamber area to electrode area ratios, the opera­ ting voltage will increase causing a reduction in rate, but a higher degree of anisotropy. At low chamber to electrode area ratios, the voltage is reduced and the rate becomes much higher. Several specific applications are possible with the hollow cathode apparatus, most of which are not otherwise available. For the purposes of patterning, the hollow cathode has several distinct advantages. The first is in mask lifetime. With the high voltages and ion energies present in the prior art, the mask is physically sputtered, and will hence have a relatively short lifetime. The apparatus with the hollow cathode, however, with the low, almost sub-sputtering energies will not sputter the mask, and in addition, a material can be chosen which is non-reactive in the plasma of interest. A second useful feature is the ability to operate over a broad pressure range, including pressures up to 66.3 Pa (500 milli­ torr) without any reduction in reaction rate. The pressure depen­ dence of operation will be discussed below, it being noted that this high operating pressure is not a feature of the prior art. The high operating pressure allows operation in a partial isotropic mode. The etching of the prior art, due to the high energy, is effectively anisotropic. The ability of the device to operate in a partial isotropic mode allows sloping of sidewalls, which is an important feature for vias and interconnections in thin film devices. The relatively low operating voltage is quite important for reactions with the electrode material. With a correct choice of materials for a given etching reaction (on some sample), the elec­ trode material can be chosen to form a passivating surface layer, which will not be sputtered away due to the low energy of ion bombardment. At the high ion energy present in prior art RF RIE devices, the formation of this layer is not possible due to physical sputtering. The pressure dependance of the present device is shown in Figure 4. Far from decreasing at high pressure as in the prior art, the present device operates well at pressures normally used in commercial devices (100-300 millitorr). A further improvement arises from use of the preferred embodi­ ment of the present invention which is shown in Figure 5 and con­ sists of a reconfiguration of the electrode in the basic hollow cathode enhanced RF sputtering system into an array of small hollow cathode glows on a single plate structure. The hollow cathode glows at the electrode surfaces are characterized by higher plasma densi­ ties and subsequently increased ion bombardment rates of the elect­ rode surface. This increase in bombardment rate causes an increase in the etch rate and a subsequent increase in the deposition rate on a substrate compared with the two planar element electrode struc­ tures. The formation of an array of small hollow cathode glows on the electrode surface is accomplished by making a matrix of close-packed holes in electrode material. These holes are blind, i.e they do not go fully through the electrode material, but stop short of the back. A simple representation of this type of electrode is shown in Figure 5. Each of these holes is separate, and separated by a thin side wall from the next hole. Since the holes do not extend through the electrode, and have a "bucket-like" appearance, they have been designated "bucket-hollow cathodes" to distinguish them from other modes of hollow cathode glows and arcs. In Figure 5, the primary change from the hollow cathode struc­ ture described above with reference to Figures 1 and 2 is in the shape of the hollow cathode structure 31. The other details of the hollow cathode RF sputtering system are unaffected. The primary electrode, 31, is shown in cross-section in Figure 5 and the holes in the electrode are indicated by dashed lines 36. The detail of this design is shown in more clarity in Figures 6 and 7. In Figure 6, the electrode 31 is shown in perspective. The electrode surface is covered with an array of closely packed holes 37. These holes may be circular or of another geometrical cross-section, such as square or hexagonal. The operation of the device will be unaffec­ ted. The formation of these "bucket" structures can also be accom­ plished by an array of short tubes placed side-by-side in a close packed array, making contact with the base electrode, which would in this case be flat. The operation of the apparatus with the bucket-hollow cathode is as follows. A plasma is initiated in the RF device in the same manner as described previously. At the electrode surface 31, the plasma will extend into each of the openings or buckets in the electrode surface. This is shown schematically in FIG. 7. The plasma sheath 38 will penetrate the hole volume 39, and the inner walls of the bucket will be ion bombarded. Secondary electrons ejected from the surface will be accelerated across the sheath, and gain sufficient energy to ionize the background gas. Before they can leave the electrode area, however, they will be reflected by the sheath at the opposite side of the volume 39. The electrons will oscillate many times back and forth in this small volume 39 until they can finally escape into the larger plasma volume above the electrode 31. Because of this trapping of the electrons, the ionization level of the background gas will be increased very close to the electrode surface. This increased plasma density causes increased ion bombardment and a higher sputtering rate. This trapping effect is known as a hollow cathode glow. The increased sputtering will occur on all sides and the bottom of the bucket enclosure. Some of the material sputtered from the walls of the bucket will leave the bucket enclosure, as will a large amount of the material sputtered from the floor of the bucket. In general, the net result is an increase in the total amount of material sputtered from the electrode, and subsequently deposited on some external electrode or sample. The aspect ratio of the hole or bucket helps determine both the net increase in the sputter/deposi­ tion rate and the directionality of the deposition flux. Because the bucket-hollow cathode electrode can operate in lower pressure regions than the equivalent planar electrode, there is less gas scattering and more directionality to the flux. However, if the holes or buckets are too deep, the amount of material sputtered from the bottom of the hole which actually leaves the bucket volume will be reduced. In practice, an aspect ratio (depth/longest cross-sect­ ional dimension) of 1.5 or greater is normally necessary for satis­ factory operation. For a cylindrical hole the longest cross-sectional dimension would be a diameter; for an elliptical hole it would be the major axis for a rectangular hole it would be the longest diagonal. Too small an aspect ratio results in weakening of the electron trapping and the intensity of the hollow cathode glow effect. An upper counter electrode 32 is shown in Figure 5 in dotted lines. This electrode would be at the potential of the containment vessel 40 and serves as a mounting surface for sample 42 to be sputtered or etched. In the embodiment of Figures 1 and 2, this is not necessary as the cathode electrode surface may be used for sample support. Experimental Results Sample electrodes of Cu were constructed in accordance with the embodiment of Figure 5 and operated in a small RF sputtering device. They were compared to single planar Cu electrodes of the same diameter under identical operating conditions. The operating conditions were: input RF power of 100-1000 watts, with less than 20 watts reflected; argon gas in the system at pressures of 2.7 to 13.3 Pa (20 to 100 millitorr). One set of results is shown in Figures 8 to 11, which shows the deposition rate as a function of position for a single planar electrode case (not hollow cathode) as compared to the bucket-hollow cathode electrodes at the same RF power and other conditions. These results were characteristic of a number of different experimental conditions and were repeatable. The general results are that the deposition rate onto a sample is higher by a factor of almost 2, and the deposition profile is flatter with the bucket-hollow cathode electrodes. The flatter deposition profile results from the collimation aspect of the bucket hollow cathodes. The electrodes for these experiments were either a flat elec­ trode covered with an array of 1 cm diameter by 1 cm deep holes, or an array of short copper tubes of approximately the same dimensions set closely together on a flat copper plate. The extension of this technique to other electrode materials is straightforward. The effect is primarily geometrical, and operates in the same manner with metal or insulating electrode materials. As stated previously the present invention has wide application in the semiconductor production industry for the making of various layered semiconductor structures which would normally be made utilizing RF reactive ion etching sputter/etching processes either for the deposition of materials upon the substrate or for the removal of materials by the volatization of target materials using a reactive gas. Due to the high current density, high process rates are pos­ sible utilizing the principles of the invention for greater product throughput. Due to the low voltage operating characteristics it is possible to sputter/etch such materials as polyimides without adversely affecting surrounding areas. Another potential application of the invention, due to the unusually high process rates possible, involves the stripping of photoresist material from substrates and also just plain "cleaning" or "glow discharge cleaning" to remove unwanted deposits from sample holders and the like prior to starting a new production run.

Claims: 1. A reactive ion etching and deposition apparatus comprising a cathode (31) disposed in an evacuable chamber, the apparatus being characterised by the cathode (31) being of a form providing a matrix of hollows (37) in its front side and a plain rear side. 2. An apparatus as claimed in claim 1, in which the ratio of the largest dimension of the cross-section of each of the hollows in the front side of the cathode to the depth of the hollow is at least 1.5:1. 3. An apparatus as claimed in claim 1 or claim 2, in which the cathode comprises a plate having a matrix of blind holes in the front side thereof. 4. An apparatus as claimed in claim 3, in which the holes are of circular cross-section. 5. An apparatus as claimed in claim 1 or claim 2, in which the cathode comprises a matrix of short tubes, each mounted at one end on a backing plate and having its other end open. 6. An apparatus as claimed in claim 5, in which the tubes are of circular cross-section. 7. A method of operating an apparatus as claimed in any preceding claim, including supporting a workpiece adjacent the front side of the cathode, evacuating the chamber to a vacuum, of between 0.0013 to 53 Pa (0.01 and 400 millitorr), establishing an ionisable gas flow through said chamber, initiating a hollow cathode glow discharge within the cathode by applying a high RF voltage and then reducing the RF voltage to less than 300 peak RF volts once the hollow cathode glow is ini­ tiated, and maintaining a hollow cathode glow sustaining voltage of not greater than said 300 peak RF volts and an effective DC bias voltage of not greater than 150 volts (negative) on the cathode.

Inventors: BUMBLE, BRUCE, CUOMO, JEROME JOHN, LOGAN, JOSEPH SKINNER, ROSSNAGEL, STEVEN MARK
Applicants: INTERNATIONAL BUSINESS MACHINES CORPORATION
Application year: 1986
Main classification: H01J37
IPC codes: H01L21, H01J37, C23C14, C23F4, C23F1, H05K3