INSULATING MATERIAL, PREPARATION METHOD AND USE THEREOF

Abstract: A new material on the basis of Ca-hydrolisilicate, consisting predominantly of 11 A &cir& o tobermorite of fibrous structure, wherein there is optionally incorporated a minor quantity of inorganic and/or organic fibres, a wet method for the manufacture thereof and the use of the new material in technical fields requiring very good overall insulating properties and an adequate mechanical strength at severe conditions.

Description: INSULATING MATERIAL,PREPARATION METHOD USE THEREOF The present invention relates to a new material of thermal and electrical insulating and of sound and vibrations damping properti of a high mechanical strength and a permanent water and CO- resistance, based on Ca-hydrosilicate, to a new method for the manufacture thereof and to the use of the n ,w material in technical fields requiring very good universal insulating properties and simultaneously an adequate mechanical strength and high thermal stability. Ther oinsulating materials on the basis of Ca-hydrosilicates which may contain fibres are known. They are, however, not satisfactory e.g. in thermoaggregates or other uses in severe conditions as they either lack mechanical strength - especially when exposed to high temperatures - or insulating properties or both. As their thermal stability, water resistance . etc. have been inferior, their working life wa3 rather short. Ca-hydro¬ silicates available on the market exhibit a compressive resistanc of 49 N/cm 2 after the exposition to 1273.15 K. Accordingly, their field of application is specific and narrow and the problem of finding a universal material combining insulating properties a-s well as mechanical strength and thermal stability has not yet been solved in prior art. It has now been found that a material on the basis of Ca- hydrosilicate, predominantly comprising 11 A tobermorite of fibrous structure, wherein there is optionally incorporated a miner quantity of inorganic and/or organic fibres, exhibits excellent thermal and electrical insulating and sound and vibrations damping properties, a permanent CO_ and water resistance and simultaneously a high mechanical strength, even - . 2 - at severe working conditions. The material possesses the best properties when it comprises at least 80 mass % of 11 Λ toberrnorit of fibrous, well-crystallized structure. Said material of unobvious characteristics is the first object of the present invention. A further object of the present invention is a new method for the manufacture of a Ca-hydrosilicate material, predominantly comprising 11 A toberrnorite of fibrous structure, based on the following equation: 5 Ca(OH)- + 6 SiO + 5.5 H 2 0 + q(J) 5 CaO x 6 i0 2 x 10.5 H 2 0 by means of a "wet" method starting from solutions and suspensions resp., whereas the hitherto known syntheses have been performed in a moist moulded or otherwise formed mass ' . The present inventive method is specifically performed in the following manner: Hydrated lime and pulverized quartz of a particle size of max. 93 ,um and a SiO- content of at least 80 mass % in a ratio of hydrated lime : SiO_ 0.73 to 0.76 are successively added to an aqueous solution containing 0.3 to 1.5 mass % of an alkali salt of carboxymethylcellulose, whereupon there are added to e suspension 5 to 8 mass % - calculated on the solid phase mass - of inorganic or organic fibres of a max. length of about 10 mm so that the ratio of the solid and liquid phases in the suspension lie3 within the range of 4.5 to 5-5, subsequently said suspension is filled into moulds, which are subjected to the action of water vapour at a pressure of 7.0 to 11.0 bar during 12 to 16 hours, and finally the product is removed from the moulds and dried at a temperature of max. 493 K. The alkali salt of carbo ymethylcellulose is preferably sodium carboxymethylcellulose. Inorganic fibres are particularly asbestos fibres of a length of about 10 mm. Organic fibres are preferably flax, hemp or Jute-flbres of a length of about 10 mm. It should be noted that said fibres are not added with the aim of reinforcing the structure of the Ca-hydrosilicate but as additives Inducing the crystallization to proceed towards the desired formation of 11 S toberrnorite of fibrous, well- c s iiize structure. Without restricting herself to any theory, the inventor believes that they act as retardation agent3 during the synthesis, thus enabling the selective crystallization into 11 W toberrnorite to proceed. The high content of well-formed 11 A toberrnorite was confirmed by X-ray difractcgraphic analysis of the product. After the completed formation of the 11 _ toberrnorite crystalls the presence of fibres is not critical any more and they may be destroyed during a subsequent heating of the material to high temperatures . The behaviour of the new material is obviously characteristic of a substantially homogeneous structural entity, whereas the prior art products were degraded into their individual ingredients when subjected to increased temperatures. Owing to these novel features of its structure and texture, the claimed material is universally applicable in static and dynamic, thermal and other aggregates. A further object of the present invention is the use of the material, based on Ca-hydrosilicate, predominantly comprising 11 A toberrnorite of fibrous structure, as thermal and electrical insulating, sound and vibrations damping materials of simultaneous high mechanical strength and and a permanent water and C0_ resistance, as may be envisaged by any person skilled in the art . The present invention is illustrated by the following Examples, which are not to be construed as limiting in any way. Example 1 Hydrated lime (330 kg; CaO content 72 mass %) was added to a premix consisting of water ( 1.5 3 ) and sodium carboxymethyl¬ cellulose (3 kg), whereupon there was added pulverized quartz (309 kg; SiO. content 97-5 mass %; particle size 93 ,um). The obtained mixture was added to a premix of chry3θtile asbestos fibres ( 3Q kg; length appr. 10 mm) In water (12.3 m 3 ) . All components were thoroughly mixed by stirring and dosed into moulds (inside dimensions 1.2 m x 0.6 m x 0.3 m). The filled moulds were subjected to a hydrothermal treatment in an autocl during 14 hours at a pressure of 9.18 to 10.2 bar. Af er the completed hydrothermal treatment white coloured blocks were removed from the block, dried and tested. Example 2 Hydrated lime (465.65 kg; CaO content 72 mass 4) was added to solution of sodium carboxymethylcellulose (3.8 kg) in water ( 2000 1). Thereupon there was added pulverized quartz (463.5 k SiO- content 97.5 mass % ; particle size -_ 93.urn) . The componen were stirred and the thoroughly mixed suspension was transferre into a second mixer containing water (2200 1) and fibres (19 k of flax fibres, length 10-12 mm, and 48.5 kg of chrysotile asbestos fibres, length approx. 10 mm). All components were thoroughly mixed and the obtained pulp-like suspension was fill into moulds as defined in Example 1. The filled moulds were subjected to a hydrothermal treatment i an autoc l ave in accordance wi h the following Lemperatur . y.rad procedure: 1. preneating- 2.5 hours (up to 9.5 bar ) 2. Isobaric period: 11 hours at 9.5-10 bar 3. cool ing: 3 hours The blocks which were removed r m the moulds subsequently to the hydrothermal treatment had a total volume of 3.65 m-> and a fr e e water content of 79 mass %. There were dried for about 20 hours at ' approx. 448 K. Report o results Properties of blocks produced In accordance with Examples 1 and ϋulk density: 220-280 kg/m J Compressive resistance: 1.470900-1961200 N/m 2 Flexural strength: 9806OO- 1000000 N/m 2 Total porosity: 75-85 % Linear shrinkage after 24 hours of subjection to heat: 1.8-2 at a mean temperature of 1273.15 K Apparent thermal conductivity at mean temperatures: 473.15 K 0.06978 W/mK 573.15 K 0.0872 W/mK 673-15 K 0.09769 W/mK The above tests were performed in accordance with: ASTM C 165 (compressive properties) ASTM C 203 (flexural strength) ASTM C 303 (density) ASTM C 356 (linear shrinkage) ASTM C 518 (thermal transmission) ASTM (air and Hg) methods for assaying porosity in refractory material (porosity) Standard test JUS.U.J. 1.040, point 7 (burning test): the tested samples were not combustible. Standard test JUS.U.J. 1.060, point 7 (inflammability test): the tested samples were not inflammable and the material was classified into class I. Evaluation according to the Regulations on Technical Measures and Conditions for the Acoustical Insulation of Brickwork (Official Gazette of Yugoslavia, No. 35/70): The acoustical insulation capacity of the tested w ll board.s of a thick of 5 cm was 28 decibel . Mean deviation: - decibel . Mean value of sound trans a ce' reducti on: 2 decibel The vibration damping property i3 a characterizing feature of ' the present inventive material, which is a novel advantage of Ca-hydrosilicate-based thermoinsulating materials. The new inventive material is resistant to humidity and absorbs moisture until an air-dry state is attained. It is also peimansntly, stable in water. It does not leak water prior to complete saturation.The ab3orbable quantity of water might five times exceed its original mass. Thus the material might be used in certain cases for hydroinsulating purposes. It is also frost- resistant, even in humid state. After re-drying the material exhibits its original characteristics The diffusion resistance factor (the water vapour transmission value of a layer of the inventive material divided by the water vapour transmission value of a layer of air of equal thickness) was determined as .u = 17.8. The new material is resistant to CO- gas and pests such as rodents and insects. The claimed new material has a white - even brilliant white - and very pleasant colour, which is also acceptable in exacting fields of application (architecture, food processing etc.). Workmanship: It may be worked e.g. by means of wood-working tools. The forming may be completely performed during the manufacture of the material, especially if there are required forms not attainable by means of cutting and sawing or if there are^preferred solely or predominantly original, non-machined surf"ices of the final prduct. The surfaces of the formed p eces may be finished, e.g. painted, in any conventional manner. It may be reasonably concluded that the new inventive material has a very broad applicabili y in various technical fields. Therefore there are claimed a3 a further object of the present invention all articles, elements or pieces, formed from the new, inventive material which is defined in the introductory part of this specification. They may be used in any technical field wherein overall insulating properties and simultaneousl a good stability at high temperatures as well as a good press fire-, vibration-, water vapour-, C0 ? - etc. resistance is req Without limiting the scope of possible modes of application, which a worker skilled in the art might find without undue inventive efforts, there are contemplated the following techn fields by way of example: refractory materials.electric and ther insulation, power station equipment, building constructions, especially for unfavourable climates, furniture, protection o metallic constructions, cisterns, refrigerators, con ensors, e.g. in chemical industry, aircraft and shipbuilding elements etc. An interesting use to be envisaged o ht be the use as catalyst carrier.

Claims: WHAT IS CLAIMED IS: 1. A material of thermal and electrical insulating and of sound and vibrations damping properties, of a high mechanical streng and a permanent water and CO- resistance, based on Ca-hydrosili characterized in that the Ca-hydrosilicate comprises predomina preferably at least 80 mass %, 11 A toberrnorite of fibrous stru wherein there is optionally incorporated a minor quantity of inorganic and/or organic fibres. 2. A material as claimed in claim 1 , characterized in that it shows the following characteristics (ASTM)- bulk density: about 220-280 kg/m , apparent thermal conductivity: about 0.06978-0.1 W/mK, compressive resistance: abcut 1500000-1900000 N/m 2 , linear shrinkage after 24 hours of subjection to heat: max. 2 at a mean temperature of 1273-15 K, thermal stability at temperatures exceeding 1573 K, bending strength: up to about 980000 N/m 2 . 3- A material as claimed in claim 1 , wherein inorganic fibres are asbestos fibres of a length of about 10 mm. 4. A material as claimed in claim 1 , wherein organic fibres are flax, hemp or jute fibres of a length of about 10 mm. 5- A method for the manufacture of a material of thermal and electrical insulating and of sound and vibrations damping prop of a high mechanical strength and a permanent water and C0_ resistance, based on Ca-hydrosilicate, characterized in that hydrated lime and pulverized quartz of a particle size of max. 93 ,um and a SiO- content of at least 80 mass % in a ratio of hydrated lime : SiO- 0.73 0.76 are successively added to an aqueous solution containing 0.3 to 1.5 mass % of an alkali sal of carboxymethylcellulose, whereupon there are added to the suspension 5 to 8 mass % - calculated on the solid phase mass of inorganic or organic fibres of a max. length of about 10 mm so that the ratio of the solid and liquid phases in the suspensio lies within the range of 4.5 to 5.5, subsequently said suspe is filled into mouldy which are subjected to the action of water vapour at a pressure of 7.0 to 11.0 bar during 12 to 16 hours, and finally the product is removed from the moulds and dried at a temperature of max. 493 K. % 6. A method as claimed in claim 5, wherein inorganic fibres are asbestos fibres of a length of about 10 ram. 7. A method as claimed in claim 5, wherein organic fibres are flax, hemp or jute fibres of a length of about 10 mm. 8. Products, comprising the material as claimed in any of the claims 1 to 4. 9. Products, comprising the material manufactured in accordance with the method as claimed in any of the claims 5 to 7. 10. Use of the products as claimed in claims 8 or 9 as e.g. refr materials, electric and thermal insulation, power station equipme bulding construction elements, furniture, metallic construct protection, cisterns, refrigerators, condensors in chemical industry, aircraft and shipbuilding elements, catalyst carri and analogous products requiring very good overall insulatin properties and adequate mechanical strength.

Applicants: QUILL QUARZ GMBH, QUILL-QUARZ GMBH
Application year: 1986
Main classification: H01B3
IPC codes: C01B33, C04B35, H01B3, H01B19