STABILIZATION OF HIGH SOLIDS COATINGS WITH SYNERGISTIC COMBINATIONS

Abstract: A method of stabilizing a polymer film coating or molded article against the action of light, moisture, and oxygen is disclosed. The method comprises incorporating in said polymer a stabilizingly and synergistically effective amount of: (A) A 2, 2, 6, 6-tetraalkylpiperidine compound, or the acid addition salts or complexes with metal compounds thereof; and (B) A tris-aryl-s-triazine compound represented by the formula: wherein X, Y and Z are each aromatic, carbocylic radicals of less than three 6-membered rings, and at least one of X, Y and Z is substituted by a hydroxy group ortho to the point of attachment to the triazine ring; and each of R¹ through R⁹ is selected from the group consisting of hydrogen, hydroxy, alkyl, alkoxy, sulfonic, carboxy, halo, haloalkyl and acyla­ mino.

Description: Field This invention relates to synergistic combinations of hindered amine light stabilizers (HALS) and ultraviolet absorbers (UVA). Background The use of HALS and UVA individually or in combination to stabilize synthetic resins, plastics, and the lacquers and coatings made therefrom against light degradation is well known. Formerly, UVA such as benzotriazoles, benzophenones, tris-aryl-triazines, and the like were used to stabilize materials susceptible to degradation by light, particularly ultraviolet (UV) light. When the class of compounds known as HALS was discovered, the use of UVA became secondary in use to the HALS. Thus, for example, patents relating to HALS and their use usually disclosed that UVA may be used in addition to the HALS if desired. U.S. 3,118,887 and U.S. 3,268,474 disclose the stabilization of plastic and resinous compositions against the effects of ultraviolet light by the incorporation therein of one or more members of a class of tris-aryl-triazines. The aryl radicals of the tris-aryl-triazines UVA are carbocyclic groups of less than three 6-membered rings and at least one of the aryl radicals is substituted by a hydroxyl group which is ortho to the point of attachment to the triazine nucleus. The remaining substituents are either hydroxy, alkyl, alkoxy, sulfonic, carboxy, halo, haloalkyl or acylamino (wherein the acyl is derived from a carboxylic acid). See for example, Formula I in Column 1 and Formula II in Column 2 of U.S. 3,118,887, and Formulas I and II in Column 2 of U.S. 3,268,474. U.S. 4,355,071 discloses a substrate having a finish of a clear coat top layer in firm adherence to a color coat layer that is in adherence with the substrate. The clear coat consists essentially of a transparent film forming binder. The color coat consists essentially of a film-forming binder, pigment and ultraviolet light stabilizer. The ultraviolet light stabilizer migrates from the color coat to the clear coat. This migration continues as ultraviolet light stabilizer is lost from the clear coat due to exposure to weathering. This provides an adequate level of ultraviolet light stabilizer to retard deterioration of the finish. The resulting finish is particularly useful for automobile and truck finishes. The ultraviolet light stabilizers that are useful include benzophenones, triazoles, triazines, and benzoates among others -- see the examples given in Columns 3 and 4. U.S. 4,314,933 discloses a method for stabilizing two-layer uni-lacquer coatings based on acrylic, alkyd or polyester resins, melamine/formaldehyde resins, epoxide resins or polyisocyanates against the adverse effects of light, humidity and oxygen. The method comprises incorporating into said resin (1) a 2,2,6,6-tetraalkylpiperidine compound, its acid addition salts or metal complexes, and (2) a ultraviolet light absorbing compound. The 2,2,6,6-tetraalkylpiperidine compounds are generally known. See for example Column 1 (Formulas I and II); Column 3 (Formula III); Column 5 (Formula IV); Column 6 (Formulas VA-C); Column 7 (Formula VI); Column 11 (Formula VII); Column 12 (Formula VIII); Column 14 (polymeric compounds in which the recurring structural unit contains a polyalkylpiperidine radical of Formula I); and Column 15 (compounds which contain, in their molecule, at least one 2-(2'-hydroxyphenyl)-benztriazole group or 2-hydroxybenzophenone group and at least one polyalkylpiperidine group). The patent discloses that in order to achieve maximum stability to light, it can be advantageous to use other conventional light stabilizers. Examples of these are UV-absorbers of the type comprising the benzophenones, oxanilides, benztriazoles or acrylic acid derivatives, or metal-containing light stabilizers, for example, organic nickel compounds. U.S. 4,356,307 discloses stabilizers for synthetic resins, especially for polyolefins. The stabilizers have a cyclic imide bound to the 4-position of a 2,2,6,6-tetramethylpiperidine -- see for example the Formula in Column 1. U.S. 4,419,472 discloses ester mixtures of polyalkylpiperidine derivatives in which the ester substituent is in the 4-position of the polyalkylpiperidine -- see Formulas I and II in Column 1. These mixtures are suitable as stabilizers for plastics. Other stabilizers which are known can also be incorporated in the plastics with the ester mixtures. These include UV-absorbers and light stabilizers, such as, 2-(2'-hydroxyphenyl)-benztriazoles, 2-hydroxybenzophenones, and sterically hindered amines, among others -- see Columns 6-7. The patent discloses that known and conventional additives of this type are not only compatable with the mixtures of esters but, in individual cases, can also result in a synergistic effect. U.S. 4,426,471 discloses a stabilized lacquer composition comprising: (a) an acid catalyzed stoving lacquer based on hot crosslinkable acrylic, polyester or alkyd resins; (b) an N-substituted 2,2,6,6-tetraalkylpiperidine compound or its acid addition salt; (c) a UV absorber selected from the group consisting of the benzophenones, benzotriazoles, acrylic and derivatives, organic nickel compounds and oxanilides; and (d) a phenolic antioxidant. The N-substituted 2,2,6,6-tetraalkylpiperidine compounds are generally known. See for example Column 1 (Formula I); Column 2 (Formula II); Column 3 (Formula VIII); Column 5 (Formula IV); Column 6 (Formula V); Column 7 (Formula VI); Column 9 (Formula VII); Column II (Formula VIII); Column 12 (polymeric compounds, the recurring structural units of which contain a group of the Formula I or which are linked through a bivalent group corresponding to Formula I); and Column 15 (compounds which contain in their molecule at least one 2-(2'-hydroxyphenyl)-benztriazole group or 2-hydroxybenzophenone group and at least one polyalkylpiperidine group). Examples of UV absorbers which may be used in conjunction with the aforementioned piperidine compounds are provided in Columns 17-18. U.S. 4,426,472 discloses a method for stabilizing metallic stoving lacquers based on hot-crosslinkable alkyd resins or acrylic resins against the action of light, moisture and oxygen. The method comprises incorporating in the resin an effective stabilizing amount of a 2,2,6,6-tetraalkylpiperidine compound, or of the acid addition salts or complexes with metal compounds thereof. The patent discloses that to obtain maximum stability to light, the concomitant use of other customary stabilizers can be advantageous. Examples of these are UV absorbers of the benzophenone, oxanilide or benzotriazole type, or acrylic acid derivatives, or metal-containing light stabilizers, such as organic nickel compounds. The 2,2,6,6-tetraalkylpiperidine compounds are generally known. See for example Column 1 (Formulas 1 and II); Column 3 (Formula III); Column 5 (Formulas IV and V); Column 7 (Formula VI); Column 11 (Formula VII); Column 13 (Formula VIII); and Column 14 (polymeric compounds of which the recurring structural unit contains a polyalkylpiperidine radical of Formula I). EP-A 0078603 discloses a composition comprising a substantially crystalline polymer of an aliphatic monoalpha-olefin and a hindered amine or its salt, N-oxide, N-hydroxide, or N-nitroxide. The hindered amine has its amino nitrogen contained in a carbon-nitrogen carbon chain which forms part of a non-aromatic heterocyclic ring. Also, each of the two carbon atoms of the chain is bonded to two lower alkyl groups, which may be the same or different, each lower alkyl group containing from 1 to 12 carbon atoms, or to an alicyclic group containing from 4 to 9 carbon atoms which groups sterically hinder the amine. The composition may also contain, for example, stabilizing amounts of light stabilizers, e.g., benztriazoles. EP-A 0087294 discloses an irradiation sterilizable composition comprising a semi-crystalline polymer. Incorporated in the polymer is a mobilizing amount of a non-crystalline liquid mobilizing additive which increases the free volume of the polymer. Also, incorporated in the polymer is a sterically hindered amine or its N-oxide, N-hydroxide or N-nitroxide salt. The amine nitrogen of the hindered amine is contained in a carbon-nitrogen-carbon chain which forms part of a non-aromatic heterocylic ring. Each of the two carbon atoms of the chain is bonded either to two alkyl groups which are the same or different and each having 1 to 12 carbon atoms, or to an alicyclic group containing 4 to 9 carbon atoms. The composition may contain stabilizing amounts of, for example, light stabilizers, e.g., benzotriazoles. Berner, G., and Rembold, M. "New Light Stabilizers For High-Solid Coatings", in Organic Coatings, Science and Technology, Volume 6, (1984), Edited by Parfitt, G.D. et al, pp.p. 55 - 85, TP 1175. S607, discloses the synergistic combination of a sterically hindered amine light stabilizer (radical scavenger) with a benztriazole UV-absorber. It is also disclosed that a new HALS-type combined with a benztriazole (designated Benztriazole I - see page 58) in a 1-package high-rated paint proved to be an outstanding stabilizer package. The high-solid paint was based upon a hydroxyl-functional acrylic resin and a HMMM resin (a fully alkylated melamine resin) as the crosslinker. Further disclosed, at pages 83-84, is that light stabilizers are complementary to each other. This synergism can possibly be explained based upon the assumption that fewer radical processes are photochemically induced in the presence of UVA. It has been shown by model experiments that the (relative) stabilizing effect of HALS may depend on the number of radical processes induced with time. Therefore, at high rates of radical initiation (in the absence of UV absorber) the observed efficiency of HALS is lower since the higher radical concentrations are not as effectively controlled by the stabilizers. Although the use of HALS and UVA in combination with each other is well known, there has been relatively little known work on or discovery of combinations of particular HALS and UVA that will produce synergistic results. An exception to this, as noted above, is the use of a benztriazole with a HALS of unknown structure in a high-solid paint (Berner et al above). A welcome contribution to the art would be synergistic combinations of HALS and UVA to provide polymers with protection against degradation by light. Such a contribution is provided by this invention. Summary of the Invention This invention provides a method of stabilizing a polymer film, coating or molded article against the action of light, moisture, and oxygen comprising incorporating in said polymer a stabilizingly and synergistically effective amount of from 0.05 5 wt%, based on the total resin solids, of each of ingredients (A) and (B): (A) A 2,2,6,6-tetraalkylpiperidine compound, or the acid addition salts or complexes with metal compounds thereof; and (B) A tris-aryl-s-triazine compound represented by Formula (I): wherein X, Y and Z are each aromatic, carbocylic radicals of less than three 6-membered rings and at least one of X, Y and Z is substituted by a hydroxy group ortho to the point of attachment to the triazine ring; and each of R¹ through R⁹ is selected from the group consisting of hydrogen, hydroxy, alkyl, alkoxy, sulfonic, carboxy, halo, haloalkyl and acylamino. The invention also provides a synergistic stabilizer combination as defined in Claim 7 and a light stable composition as defined in Claim 8. Detailed Description of the Invention The polymers which can be stabilized according to the methods of this invention include those which form films and coatings, and those from which molded articles are produced. Preferably acid catalyzed thermoset acrylic coatings or alkyd resins are stabilized, most preferably high solids thermoset acrylic coatings are stabilized by the methods of this invention. The film-forming binder used in the coatings can be those well known in the art. For instance, solvent- or water-based acrylic lacquers, acrylic dispersion lacquers, solvent- or water-based thermosetting acrylic enamels, polyester enamels, non-aqueous acrylic dispersion enamels, alkyd resin enamels, polyurethane enamels and acrylic or polyester powder coatings can be used. These coatings are described in detail in U.S. 4,355,071. The HALS are well known in the art and can include their salts, N-oxides and N-hydroxides. In general, the HALS can be described as having an amino nitrogen contained in a carbon-nitrogen-carbon chain which forms part of a non-aromatic heterocylic ring where each of the two carbon atoms of the chain is bonded to two lower alkyl groups which may be the same or different, each lower alkyl group containing from 1 to 12 carbon atoms, or to an alicyclic group containing from 4 to 9 carbon atoms, which groups sterically hinder the amine In particular, the HALS to be used in the method of this invention are 2,2,6,6-tetraalkylpiperidines, their acid addition salts or complexes with metal compounds. These HALS are well known in the art and include compounds which contain a group represented by Formula II: wherein R is hydrogen or methyl. HALS utilizable in this invention also include, but are not limited to, compounds represented by the following: 1. Formula III wherein: n is a number from 1-4 inclusive, preferably 1 or 2; R is as defined in Formula II; R¹ is hydrogen, oxyl, C₁-C₁₈ alkyl, C₃-C₈ alkenyl or alkynyl, C₇-C₁₂ aralkyl, C₁-C₈ alkanoyl, C₃-C₅ alkenoyl, glycidyl, a group - CH₂CH(OH)-Z wherein Z is hydrogen, methyl or phenyl, with R¹ preferably being hydrogen, C₁-C₁₂ alkyl, allyl, benzyl, acetyl or acryloyl; R², when n is 1, is hydrogen, C₁-C₁₈ alkyl optionally interrupted by one or more oxygen atoms, cyanoethyl, benzyl, glycidyl, a monovalent radical of an aliphatic, cycloaliphatic, araliphatic or aromatic carboxylic acid, or of carbamic acid, or of a phosphorous-containing acid, or a monovalent silyl radical, preferably a radical of an aliphatic carboxylic acid having 2-18 C atoms, of a cycloaliphatic carboxylic acid having 5-12 C atoms or of an aromatic carboxylic acid having 7-15 C atoms; R², when n is 2, is C₁-C₁₂ alkylene, C₄-C₁₂ alkenylene, xylylene, a bivalent radical of an aliphatic, cycloaliphatic, araliphatic or aromatic dicarboxylic acid, of a dicarbamic acid or of a phosphorus-containing acid, or a bivalent silyl radical, preferably a radical of an aliphatic dicarboxylic acid having 2-36 C atoms, of a cycloaliphatic or aromatic dicarboxylic acid having 8-14 C atoms, or of an aliphatic, cycloaliphatic or aromatic dicarbamic acid having 8-14 C atoms; R², when n is 3, is a trivalent radical of an aliphatic, cycloaliphatic or aromatic tricarboxylic acid, of an aromatic tricarbamic acid or of a phosphorus-containing acid, or a trivalent silyl radical; and R², when n is 4, is a tetravalent radical of an aliphatic, cycloaliphatic or aromatic tetracarboxylic acid; 2. Formula IV wherein: n is the number 1 or 2; R is as defined in Formula II; R¹ is as defined in Formula III; R³ is hydrogen, C₁-C₁₂ alkyl, C₅-C₇ cycloalkyl C₇-C₈ aralkyl, C₂-C₁₈ alkanoyl, C₃-C₅ alkenoyl or benzoyl; R⁴, when n is 1, is hydrogen, C₁-C₁₈ alkyl, C₅-C₇ cycloalkyl, C₂-C₈ alkenyl unsubstituted or substituted by a cyano, carbonyl or carbamide group, or it is glycidyl, a group of the formula - CH₂-CH(OH)-Z or of the formula - CONH-Z wherein Z is hydrogen, methyl or phenyl; R⁴ when n is 2, is C₂-C₁₂ alkylene, C₆-C₁₂ arylene, xylylene, a - CH₂-CH(OH)-CH₂-group, or a group - CH₂-CH(OH)-CH₂-O-X-O-CH₂-CH(OH)-CH₂ - wherein X is C₂ - C₁₀ alkylene, C₆-C₁₅ arylene or C₆-C₁₂ cycloalkylene; or, provided that R³ is not alkanoyl, alkenoyl or benzoyl, R⁴ can also be a bivalent radical of an aliphatic, cycloaliphatic or aromatic dicarboxylic acid or dicarbamic acid, or can be the group -CO- or R³ and R⁴ together, when n is 1, can be the cyclic radical of an aliphatic or aromatic 1,2- or 1,3-dicarboxylic acid; 3. Formula V wherein; n is the number 1 or 2; R is as defined in Formula II; R¹ is as defined in Formula III; R⁵, when n is 1, is C₂-C₈ alkylene or hydroxyalkylene or C₄-C₂₂ acyloxyalkylene; and R⁵, when n is 2, is the group (-CH₂)₂C(CH₂-)₂; 4. Formula VI wherein: n is the number 1 or 2; R is as defined in Formula II; R¹ is as defined in Formula III; R⁶ is hydrogen, C₁-C₁₂ alkyl, allyl, benzyl, glycidyl or C₂-C₆ alkoxyalkyl; R⁷, when n is 1, is hydrogen, C₁-C₁₂ alkyl, C₃-C₅ alkenyl, C₇-C₉ aralkyl, C₅-C₇ cycloalkyl, C₂-C₄ hydroxyalkyl, C₂-C₆ alkoxyalkyl, C₆-C₁₀ aryl, glycidyl, a group of the formula - (CH)-COO-Q or of the formula - (CH₂) m -O-CO-Q wherein m is 1 or 2, and Q is C₁-C₄ alkyl or phenyl; or R⁷ when n is 2 is C₂-C₁₂ alkylene, C₆-C₁₂ arylene, a group - CH₂-CH-(OH)-CH₂-O-X-O-CH₂-CH(OH)-CH2-wherein X is C₂-C₁₀ alkylene, C₆-C₁₅ arylene or C₆-C₁₂ cycloalkylene, or a group - CH₂CH(OZ')CH₂-(OCH₂-CH(OZ')-CH₂)₂ - wherein Z' is hydrogen, C₁-C₁₈ alkyl, allyl, benzyl, C₂-C₁₂ alkanoyl or benzoyl; 5. Formula VII wherein: n is the number 1 or 2; R⁸ is a group of the formula wherein: R is as defined in Formula II; R¹ is as defined in Formula III, Y is -0- or -NR¹¹-; A is C₂-C₆ alkylene; m is the number 0 or 1; R⁹ is the groups R⁸, NR¹¹, R¹², OR¹³, -NHCH₂OR¹³ or -N(CH₂OR¹³)₂; R¹⁰, when n is 1, is the groups R⁸ or R⁹; R¹⁰, when n is 2, is the group -Y-Q-Y-wherein Q is C₂-C₆ alkylene optionally interrupted by -N(R¹⁴)-; R¹¹ is C₁-C₁₂ alkyl, cyclohexyl, benzyl or C₁-C₄ hydroxyalkyl, or a group of the formula R¹² is C₁-C₁₂ alkyl, cyclohexyl, benzyl or C₁-C₄ hydroxyalkyl; R¹³ is hydrogen, C₁-C₁₂ alkyl or phenyl; R¹⁴ is hydrogen or the group - CH₂OR¹³; or R¹ is a group of the formula 6. Formula VIII wherein: n is the number 1 or 2; R is as defined in Formula II; R¹⁴, when n is 1, is C₄-C₁₈ alkyl, C₇-C₁₂ aralkyl, the group -CO-R¹⁵, or C₁-C₄ alkyl which is substituted by -CN, -COOR¹⁶, -OH, -OCOR¹⁷, or wherein R¹⁵ is C₁-C₁₂ alkyl, C₂-C₄ alkenyl or phenyl, R¹⁶ is C₁-C₁₈ alkyl, R¹⁷ is C₁-C₁₈ alkyl, C₂-C₁₀ alkenyl, cyclohexyl, benzyl or C₆-C₁₀ aryl; or R¹⁴, when n is 2, is C₄-C₁₂ alkylene, 2-butenylene-1,4, xylylene, the group -(CH₂)₂-OOC-R¹⁸-COO-(CH₂)₂ or the group -CH₂OOC-R¹⁹-COO-CH₂- wherein R¹⁸ is C₂-C₁₀ alkylene, phenylene or cyclohexylene, and R¹⁹ is C₂-C₁₀ alkylene, xylylene or cyclohexylene: 7. Formula IX wherein: Q is -N(R³)- or -O-; E is C₁-C₃ alkylene, the group -CH₂-CH(R⁴)-O-wherein R⁴ is hydrogen, methyl or phenyl, the group -(CH₂)₃-NH- or a single bond; R is hydrogen or methyl; R¹ is hydrogen, C₁-C₁₈ alkyl, C₃-C₈ alkenyl, C₃-C₈ alkynyl, C₇-C₁₂ aralkyl, C₁-C₈ alkanoyl, C₃-C₅ alkenoyl or glycidyl; R² is hydrogen or C₁-C₁₈ alkyl; R³ is hydrogen, C₁-C₁₈ alkyl, C₅-C₇ cycloalkyl, C₇-C₁₂ aralkyl, cyanoethyl, C₆-C₁₀ aryl, the group -CH₂-CH(R⁴)-OH- wherein R⁴ has the meaning defined above, a group of the formula or a group of the formula wherein G can be C₂-C₆ alkylene or C₆-C₁₂ arylene; or R³ is a group - E-CO-NH-CH₂-OR²; and 8. Polymeric compounds of which the recurring structural unit contains a polyalkylpiperidine radical of Formula II, especially polyesters, polyethers, polyamides, polyamines, polyurethanes, polyureas, polyaminotriazines, and copolymers thereof which contain such radicals. The aforementioned HALS (1-8) are described in detail in U.S. 4,426,472. It is also possible to use polyalkylpiperidine derivatives of the above Formulas III-VIII which form chemical bonds with the binder of the lacquer. This is the case when the polyalkylpiperidine derivative possesses a reactive group suitable for this purpose, for example a glycidyl group or a methylol group. Examples of such compounds are the polyalkylpiperidine derivatives of Formula IX containing methylol or methylol ether groups. Polyalkylpiperidine derivatives which are basic compounds can form salts with acids. Examples of suitable acids for such salt formation include but are not limited to inorganic acids or organic carboxylic, sulfonic, phosphonic or phosphinic acids, such as hydrochloric acid, boric acid, phosphoric acid, acetic acid, salicylic acid, toluenesulfonic acid or benzenephosphonic acid. The polyalkylpiperidine compounds can form complexes with complex-forming metal compounds, for example, with zinc-II-acetate, cobalt-II-acetylacetonate, nickel-II-acetylacetonate, aluminum-III-acetylacetonate, nickel-II-benzoate or aluminum-III-benzoylacetonate. Preferred HALS to be used with the UVA in the methods of this invention are represented by Formula X: wherein R is a saturated or unsaturated, optionally alkyl-or alkenyl-substituted alkylene or cycloalkylene radical having 2-20 C-atoms and R' is selected from the group consisting of hydrogen; an alkyl radical having 1-20 C-atoms with methyl being preferred; an alkenyl radical having 3-5 C-atoms; an aralkyl radical having 7-12 C-atoms; - CH₂ - CH₂ - CN; - CH₂ - CH₂ - COO - alkyl; - CH₂ - CH (CH₃) - COO - alkyl; an acyl radical; and - (CH₂ - CH₂O) n H, wherein n is 1-10. In Formula X, R is preferably; wherein R'' is a C₁₂-C₁₈ alkyl group; a cycloalkylene group; 1,2-cyclohexanediyl or methyl-substituted 1,2-cyclohexanediyl radicals; or a bicyclic divalent aliphatic radical. The HALS represented by Formula X are described in detail in U.S. 4,356,307. Among the aforementioned HALS, the following HALS, when used with the UVA in the methods of this invention, are particularly preferred: Compounds of Formula XI and the mixture in XII are available from Ciba-Geigy as Tinuvin® 440 and Tinuvin® 765, respectively, brand of HALS. The HALS are generally in amounts within the range of from 0.01 to 5 wt.%, preferably about 0,5 wt.%, based on the weight of binder solids. The UVA utilized in this invention, as a class, are well known in the art. See, for example, U.S. 3,118,887 and U. S. 3,268,474, the disclosures of which are incorporated herein by reference. What is not known in the art is the surprising and unexpected degree of stabilization achieved with these UVA due to their synergistic combination with the aforementioned HALS. Preferred UVA are represented by Formula XIV: wherein R is hydrogen or alkyl of 1 to 18 carbon atoms with hydrogen or C₈H₁₇ being preferred. The UVA are used in amounts within the range of from 0.01 to 5 wt %, preferably about 0.5 wt % based on the weight of binder solids. The synergistic combination of HALS represented by Formula X with UVA represented by Formula XIV are preferred. Combinations wherein R of Formula XIV is hydrogen or C₈H₁₇ are more preferred. For example, a preferred synergistic combination is: In addition to the synergistic HALS and UVA combinations, further known stabilizers and co-stabilizers can also be incorporated in the polymers stabilized. These polymer additives can be for example: 1. Antioxidants which are alkylated phenols, alkylated hydroquinones, hydroxylated thiophenyl ethers, alkylidene-bisphenols, benzyl compounds, acylaminophenols, esters of β-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid with monohydric or polyhydric alcohols, esters of β-(3,5-di-tert-butyl-4-hydroxy-3-methylphenyl)propionic acid with monohydric or polyhydric alcohols, and amides of B-(3,5-di-tert-butyl-4-hydroxyphenyl)-propionic acid; 2. Other ultraviolet light stabilizers; 3. Metal deactivators; 4. Phosphites and phosphonites; 5. Compounds which decompose peroxides; 6. Nucleating agents; 7. Fillers; and 8. Other additives, for example, plasticizers, lubricants, emulsifiers, pigments, fluorescent whitening agents, flame proofing agents, antistatic agents and blowing agents. The following examples are provided for the purpose of illustration only. Test Procedure The effectiveness of the light stabilizer systems of the following examples was determined by measuring the gloss retention (ASTM D523) and yellowness index (ASTM D1925) of a coating after exposure in an accelerated weathering unit such as the QUV (ASTM G53). Basic Clear Coating Formulations 13.0 parts ACRYLOID® AT-400 brand of thermosetting acrylic resin (a trademark of Rohm & Haas Co.) (75% solids); 5.25 parts CYMEL® 303 brand of melamine resin (a trademark of American Cyanamid Co.); 0.15 parts CYCAT® 4040 brand of toluene sulfonic acid catalyst (a trademark of American Cyanamid Co.) (40% in isopropanol); 3.3 parts Xylene; and 3.3 parts butanol. In the examples that follow the UVA and HALS utilized are identified as follows: UVA 1. TINUVIN® 900 (Ciba-Geigy Corp) 2. SANDUVOR® 3206 (Sandoz) HALS 1. TINUVIN® 765 (Ciba-Geigy Corp) a mixture of 2. TINUVIN® 440 (Ciba-Geigy Corp) Example 1 Light Stabilizing Effectiveness BONDERITE® 40 brand of cold rolled steel test panels, coated with a primer surfacer (PPG E5584) and a white base coat based on a thermosetting acrylic resin, were coated with the clear resin formulation described above (containing the stabilizer to be evaluated) and cured for 30 min. at 120°C. Clear coating thickness was about 50.8 nm (2 mils). The coated test panels were subjected to weathering in a QUV tester. In this test, the samples were subjected to alternate cycles of UV light at 70 o C for 8 hours and a humid atmosphere with no UV light at 50 o C for 4 hours. Subsequently, the gloss and yellowness index of the surface were measured. The results are reported in Table I. The data reported in Table I demonstrate that the UVA of this invention -- e.g., a compound of Formula XIVB -- is a more effective synergist, and thus more effective stabilization is provided, than TINUVIN® 900 brand of UVA. Example 2 Following the procedure of Example 1, a combination of this invention --i.e., the combination of a compound of Formula XIVB (UVA) with a compound of Formula XIII (HALS) -- was compared with a combination not of this invention --i.e., the combination of TINUVIN ® 900 brand of UVA and TINUVIN® 765 brand of HALS. The results are reported in Table II. The data reported in Table II demonstrate the superiority of the UVA/HALS combinations of this invention in providing stabilization. Example 3 Following the procedure of Example 1, the combination of the compound of Formula XIVA (UVA) with the compound of Formula XIII (a combination of this invention) was compared with the combination of TINUVIN® 900 brand of UVA and TINUVIN® 765 brand of HALS. The results are reported in Table III. The data reported in Table III demonstrate the superiority of the UVA/HALS combination of this invention in providing stabilization. EXAMPLE 4 A high solids polyester enamel is prepared by intimately admixing the following components: The combination stabilizer package of this invention comprising the HALS of Formula XIIIA and the UVA of Formula XIVA is incorporated into the polyester coating formulation as prepared above at a dosage of 2% by weight total resin solids and more particularly the HALS of Formula XIIIA is added at 0.5% by weight total resin solids and the UVA of Formula XIVA is added at 1.5% by weight total resin solids. The polyester formulation is coated onto steel panels and cured and tested in accordance with the method of Example 1. The coating thus obtained exhibits superior light stability. EXAMPLE 5 A high solids two component polyurethane coating composition is prepared as follows: A stabilizer combination of this invention comprising the HALS of Formula XIII and the UVA of Formula XIVB is prepared and added to part A of the formulation at a concentration of 2% by weight based on total resin solids at 1% by weight total resin solids for each additive. Parts A and B are thoroughly blended and the coating composition is applied, cured and tested in accordance with the method of Example 1. A superior light stable coating is provided. EXAMPLE 6 A solventless epoxy coating formulation is prepared as follows: A stabilizer combination comprising 1% by weight total resin solids of the HALS of Formula XIII and 1% by weight total resin solids of the UVA of Formula XIVA is added to the base resin formulation. Thereafter, the hardener is added and thorougly blended to form the curable coating composition. The composition is applied, cured and tested in accordance with the method of Example 1. The high solids epoxide coating exhibits euperior light stability characteristics. Although the present invention has been described with reference to certain preferred embodiments, modifications or changes may be made therein by those skilled in this art. Applicant has found the unique synergistic stabilizer combination of this invention to be effective in coatings applications generally. In every coating tested the stabilizer package provided dramatically improved light stability. It is expected that the combined stabilizer of this invention will provide the same dramatically improved light stabilizing properties to other coatings compositions and substitution of any known coating composition for those exemplified herein is contemplated by this invention.

Claims: A method of stabilizing a polymer film, coating or molded article against the action of light, moisture, and oxygen comprising incorporating in said polymer from 0.01 to 5 wt.-%, based on the total resin solids, of each of ingredients (A) and (B): (A) A 2, 2,6,6-tetraalkylpiperidine compound, or the acid addition salts or complexes with metal compounds thereof; and (B) A tris-aryl-s-triazine compound represented by the formula: wherein X, Y and Z are each aromatic, carbocyclic radicals of less than three 6-membered rings, and at least one of X, Y and Z is substituted by a hydroxy group ortho to the point of attachment to the triazine ring; and each of R¹ through R⁹ is selected from the group consisting of hydrogen, hydroxy, alkyl, alkoxy, sulfonic, carboxy, halo, haloalkyl and acylamino. A method of Claim 1 wherein said polymer is an acid catalyzed thermoset acrylic coating or an acid catalyzed thermoset alkyd resin. A method of Claim 1, wherein said piperidine is selected from the group consisting of compounds of the formula: A method of Claim 1 wherein said triazine is a compound represented by the formula: wherein R is hydrogen or alkyl of 1 to 18 carbon atoms. A method of Claim 4 wherein R is hydrogen or C₈H₁₇. A method as recited in Claim 1, wherein said piperidine compound and said triazine compound are each added in an amount of about 0.5% by weight based on total resin solids. A synergistic stabilizer combination for a polymer, said combination comprising: (a) a 2,2,6,6-tetraalkylpiperidine compound; and (b) a tris-aryl-s-triazine compound represented by the formula: wherein X, Y and Z are each aromatic, carbocyclic radicals of less than three 6-membered rings, and at least one of X, Y and Z is substituted by a hydroxy group ortho to the point of attachment to the triazine ring; and each of R¹ through R⁹ is selected from the group consisting of hydrogen, hydroxy, alkyl, alkoxy, sulfonic, carboxy, halo, haloalkyl and acylamino; with a weight ratio of (a) to (b) from 1:500 to 500:1. A light stable composition comprising: (A) A synthetic polymer useful in coatings and susceptible to degradation by light; and (B) a synergetic stabilizer combination comprising from 0.01 to 5 wt.-%, based on the total resin solids, of each of ingredients (1 ) and (2): (1) a 2,2,6,6-tetraalkylpiperidine compound; and (2) a tris-aryl-s-triazine compound represented by the formula: wherein X, Y and Z are each aromatic, carbocyclic radicals of less than three 6-membered rings, and at least one of X, Y and Z is substituted by a hydroxy group ortho to the point of attachment to the triazine ring; and each of R¹ through R⁹ is selected from the group consisting of hydrogen, hydroxy, alkyl, alkoxy, sulfonic, carboxy, halo, haloalkyl and acylamino.

Inventors: SUSI, PETER VINCENT
Applicants: AMERICAN CYANAMID COMPANY
Application year: 1986
Main classification: C08K5
IPC codes: C08L33, C08K5, C08L101, C08L67, C07D251, C09D167