Processes for producing silicon carbide particles and sinter

Abstract: Silicon carbide particles containing boron are produced by first reacting silicon or a silicon compound containing no carbon with boron or a boron compound containing no carbon in a first reaction zone at a temperature above the melting point of silicon and then reacting the boron-containing fused silicon particles so produced with a carbon compound in a second reaction zone at a temperature below the boiling-point of silicon. The silicon compound may be silane and the boron compound may be diborane, and they may be mixed before being introduced into the reaction zone.

Description: BACKGROUND OF THE INVENTION 1. Field of the invention The present invention relates to a process for producing silicon carbide particles containing boron suitable for making a dense silicon carbide sinter. More specifically, it relates to a process for producing such particles in which a free carbon content is controlled to a low level. The present invention also relates to a process for producing a sinter from silicon carbide particles obtained by the above process. 2. Description of the Related Art Silicon carbide has attracted attention as an excellent high temperature strength material suitable for use in gas turbines, etc. It is, however, difficult to sinter a silicon carbide body to a density close to the theoretical density of 3.21 g/cm 3 . Processes for obtaining a dense silicon carbide sinter have been proposed, for example, in British Patent Publication No. 1478898, in which a boron-containing compound in an amount corresponding to 0.1 to 3.0 wt% of boron and a carbon source corresponding to 0.1 to 1.0 wt% of elemental carbon as densifying agents are dispersed uniformly with submicron β-type silicon carbide particles, the resultant uniform dispersion is formed into a shape, and the shape is fired to obtain a dense silicon carbide sinter. To produce submicron β-type silicon carbide particles, a gaseous trichloro-methylsilane and hydrogen, or a suitable gaseous hydrocarbon such as silicon trichloride or toluene and hydrogen, are introduced into an argon plasma generated between two concentric electrodes to produce silicon carbide crystallites having a size of 0.1 to .0.3 µm. It is also disclosed that free carbon may be contained in silicon carbide particles by using the carbon source in an amount slightly larger than the stoichiometric amount necessary for producing silicon carbide. It is known that, to obtain an excellent silicon carbide sinter, silicon carbide particles containing boron and free carbon, desirably uniformly dispersed in the particles, as densifying agents, are preferable to a mixture of silicon carbide particles and densifying agents such as a boron source and a carbon source. The former allows a uniform structure of a sinter and an improvement of the mechanical properties of a sinter. Thus, the above British Patent Publication No. 1478898 discloses that free carbon may be contained in silicon carbide particles in a process for synthesizing the silicon carbide particles. The amount of densifying agent is critical to the characteristics of a sinter. If the amount of densifying agent is not appropriate, a good quality sinter cannot be obtained. Therefore, when the free carbon produced in silicon carbide particles during the synthesis of silicon carbide particles is used as a densifying agent, control of the amount of the free carbon produced in the silicon carbide particles is very important. It is, however, impossible to concurrently determine a quantitative amount of free carbon produced during the synthesis of silicon carbide particles. Thus, the amount of free carbon in silicon carbide particles is analyzed after a certain amount of silicon carbide particles have been synthesized to determine whether or not the amount of free carbon produced during the synthesis is appropriate. Further, to control the amount of free carbon produced in silicon carbide particles in accordance with the results of the above analysis, it is necessary to preliminarily examine the relationships between the reaction conditions and the amount of free carbon, by synthesizing silicon carbide particles under various reaction conditions. This necessitates a large number of experiments. Here, the reaction conditions include temperature, pressure, feed of raw materials, shape of a reaction chamber, etc. Even if the reaction is conducted in specified conditions, the amount of free carbon in the silicon carbide particles may vary with the amount of time lapsed, because silicon carbide particles, etc., are deposited on the inside wall of a reaction chamber and, as a result, the residence time of a raw material in the reaction chamber and other factors are varied. This makes it difficult to free carbon in a desired amount. German Patent Publication No. 2,518,950 discloses a process for producing particles comprising a uniform dispersion of β-type silicon carbide, boron and free carbon, in which a gaseous mixture essentially consisting of a silicon halide, a boron halide, and a hydrocarbon is introduced into a plasma jet reaction zone. This application suggests the effectiveness of a concurrent addition of boron halide during the synthesis of silicon carbide particles. If a silicon compound, a carbon compound and a boron compound are concurrently introduced into a single high temperature reaction zone, as in the German Patent Publication No. DE2,518,950, mainly, silicon carbide is grown onto silicon carbide seeds, to give submicron silicon carbide crystals, and boron carbide or boron is grown onto boron carbide or boron seeds to give submicron boron carbide or boron crystals, respectively. Almost all of the boron is not doped in silicon carbide particles. In other words, high temperature stable extremely small seed crystals of silicon carbide, boron carbide and boron are first produced respectively, and then silicon carbide, boron carbide and boron are grown around these seed crystals, respectively, maintaining the same crystal structure, resulting in the formation of submicron silicon carbide, boron carbide and boron particles, respectively. In such a case, boron is not always contained in silicon carbide particles but tends to form boron carbide particles or boron particles, although a silicon compound, a carbon compound and a boron compound are added in a single reaction zone. Thus, almost all of the boron is not dispersed uniformly in the silicon carbide particles and it is difficult to obtain silicon carbide particles with boron uniformly dispersed therein. SUMMARY OF THE INVENTION An object of the present invention is to provide a process for producing silicon carbide particles containing boron which corresponds to almost all of a boron source fed and is dispersed uniformly in the particles Another object of the present invention, in one of its aspects, is to provide a process for obtaining uniform silicon carbide particles in which the amount of free carbon is closely controlled. A further object of the present invention is to provide a process for producing a silicon carbide sinter, which process produces a dense sinter having uniform and improved characteristics. A still further object of the present invention is to provide a process for producing a silicon carbide sinter, which process is simple and provides a sinter having improved characteristics. The above and other objects of the present invention are attained by the process defined in the appended claims. In this process boron-conaining silicon carbide particles may be prepared by introducing silicon or a silicon compound containing no carbon together with boron or a boron compound containing no carbon into a first reaction zone at a temperature higher than the melting point of silicon to form fused boron-containing silicon particles are then reacted with the carbon compound in a second reaction zone at a temperature of less than the boiling point of silicon to produce silicon carbide particles containing a small amount of boron. Preferably, the silicon or silicon compound and the boron or boron compound are preliminarily mixed together before being introduced to the first reaction zone. The silicon carbide particles preferably contain boron, as a densifying agent for sintering silicon carbide particles, in a range of from 0.1 to 5.0% by weight. Thus obtained boron-containing silicon carbide particles can be sintered without the addition of any carbon source even if the silicon carbide particles do not contain free carbon, as explained later in detail. Boron-containing silicon carbide particles can be produced in this two-step process, by monitoring an unsaturated hydrocarbon by-product as described in European Patent Publication No. 199482. Thus, according to the present invention, there is provided a process for producing a silicon carbide sinter, comprising the steps of preparing silicon carbide particles containing 5% or less by weight of boron forming a shape of the boron-containing silicon carbide particles without the addition of a carbon source, and firing the shape. The drawing shows a sectional side view of an apparatus for producing silicon carbide particles in two reaction zones according to the present invention. In the present invention, boron-containing silicon carbide particles are produced in two steps. Silicon or a silicon compound containing no carbon and boron or a boron compound containing no carbon are introduced into a first reaction zone at a temperature higher than the melting point of silicon, 1685K, to produce fused boron-containing silicon carbide particles, and the resultant fused boron-containing silicon particles are then reacted with a carbon compound at a temperature below the boiling point of silicon, 2608K, to produce silicon carbide particles containing a small amount of boron. The boron compound used may be any one that deposits boron in the first reaction zone and includes for example, B 2 H 6 , tetraboron B 4 H 10 and boron tricholoride BCl 3 . A boron compound that relatively easily deposits boron ay a high temperarure, such as diborane, is preferred. Fine boron particles may be used in place of a boron compound. The ratio of boron to silicon may be selected according to the applications of the resultant silicon carbide particles. To obtain a good silicon carbide sinter, the amont of boron may be 5% or less by weight, preferably 4% or less by weight, based on the amount of silicon. The silicon or silicon compound and the boron or boron compound are preferably introduced to the same portion of the first reaction zone. More preferably, they are preliminarily mixed in a given ratio before being introduced to the first reaction zone. This allows a more thorough mix of the silicon or silicon compound with the boron or boron compound and allows a stable introduction of the boron or boron compound in a well defined ratio to the silicon or silicon compound in the first reaction zone, due to the preliminary mixing. This is also preferred since, if silane and diborane are used, poisonous diborane will be burnt by ignition of the silane if a leak occurs. The silicon compound and the boron compound thus introduced to the first reaction zone are quickly decomposed and form silicon and boron. The silicon is just melted and forms fused silicon particles since the temperature in the first reaction zone is above the melting point of silicon. Almost all the boron is ingested in the fused silicon particles, since fused silicon has a tendency to ingest boron, and fused silicon particles containing uniformly dispersed boron are obtained. The temperature in the first reaction zone is preferably below the boiling point of the silicon, in order to form silicon particles. The fused silicon particles containing boron are then reacted with a carbon compound in a second reaction zone to form silicon carbide particles containing uniformly dispersed boron. The second reaction zone preferably has a temperature at which the fused silicon particles are liquid. The carbon compound used may be the same as that used in the synthesis of silicon carbide particles, i.e., containing no boron. The carbon compound should now flow back into the first reaction zone since, if the carbon compound flows back into the first reaction zone, the carbon compound will come into contact with the silicon compound and the boron compound and, as a result, boron carbide particles and boron particles are easily produced in addition to silicon carbide particles, as described in relation to the related art. In the present invention, however, almost all of the boron is uniformly dispersed in the silicon carbide particles, since boron and fused silicon, which easily ingests boron, are formed together in the first reaction zone, wherein fused silicon particles containing extremely uniformly dispersed boron are produced and are then carbonized in the second reaction zone by the carbon compound to obtain silicon carbide particles. Further, the present inventors found that a dense silicon carbide sinter can be produced from silicon carbide particles without the addition of a densifying agent such as free carbon, if the silicon carbide particles contain boron. Thus, the present invention provides a process for producing a silicon carbide sinter, comprising the steps of preparing silicon carbide particles containing 5% or less by weight of boron by a process described before, forming a shape of the boron-containing silicon particles without the addition of a densifying agent such as free carbon, and firing the shape. As described before, in the prior art, silicon carbide particles containing boron uniformly dispersed in the particles have not been obtained in high temperature gaseous synthesis. The silicon carbide particles produced by a process in the prior art do not contain boron in the particles in practice, or only a portion thereof can contain boron in the particles. In contrast, according to the present invention, silicon carbide particles containing boron uniformly dispersed throughout the particles are obtained. This feature of the invention enables a dense silicon carbide sinter to be obtained without the addition of a densifying agent such as free carbon. Here, the sintering mechanism of silicon carbide with densifying agents of boron and free carbon is considered. A silicon carbide sinter is polycrystalline. This means that fine silicon carbide crystallites are in contact with each other on their different crystal planes. This contact on different crystal planes means chemical bonding between atoms of the different crystal planes, but this is impossible with silicon carbide in its original nature, since silicon carbide is a covalent bonding and the directions of the bonding hands of silicon and carbon are limited, and the angle range within which they can move freely is 6 degrees or less. As the directions of the bonding hands of silicon and carbon at different crystal planes are completely different, and the bonding hands can move only within 6 degrees or less, it is almost impossible for the bonding hands of the different crystal planes to bond together. Thus, chemical bonds between different crystal planes of silicon carbide crystallites are extremely difficult to form, and it is, therfore, practically impossible to produce a sinter of pure silicon carbide. If the bonding hands are made to be able to move in a range of more than 6 degrees, and different crystal planes are made to be chemically bound to each other, the above obstacles are overcome. It is believed that this is the role played by boron. That is, boron is present near grain boundaries in a silicon carbide sinter and makes the directions of bonding hands of silicon and carbon to be free in certain wider angle range, and thus makes it possible to chemically bond different crystal planes to each other. To achieve this, boron should be contained in the silicon carbide crystal grains. It is believed that this is assisted by free carbon. It is generally said that the role of free carbon is supposedly to remove the surface oxygen of silicon carbide particles, and as a result, boron is easily ingested by silicon carbide particles. In short, it is considered that free carbon plays a role of impregnating silicon carbide with boron, and boron makes chemical bonding between different crystal planes of silicon carbide possible. If this is so, it can be understood that, according to the present invention, silicon carbide is sintered until a sinter becomes dense even in the absence of free carbon, if silicon carbide particles containing boron in the particles are used. Oxygen does not always affect a densification of silicon carbide, even if surface oxygen, etc. is present, if boron can be ingested by the silicon carbide particles or if boron is preliminarily contained in the silicon carbide particles. In general, the high temperature characteristics of a silicon carbide sinter are deteriorated by the presence of oxygen in the sinter and therefore, preferably the amount of oxygen in the silicon carbide particles is reduced. Preferably, the free carbon should be omitted if free carbon is not necessary to make a dense sinter of silicon carbide. Further, sintering silicon carbide without free carbon is a superior process to the sintering of silicon carbide with free carbon, since it is very difficult to ensure that the amount of added free carbon is suitable, in microscale. Free carbon is consumed by surface oxygen, etc., but it is doubtful that free carbon in an amount necessary and sufficient for removing surface oxygen, etc., can be added correctly in microscale. In microscale, it is rather considered that free carbon is present in excess in some locations and is insufficient in other locations. such excess free carbon acts in a manner extremely similar to permanent micro pores and, therefore, is extremely detrimental. Thus, sintering silicon carbide without free carbon, as in the present invention, not only achieves a simple process for obtaining a dense silicon carbide sinter but also provides preferred characteristics of a sinter. As described above, although it is preferred that free carbon be omitted when free carbon is not necessary for obtaining a dense sinter, nevertheless the resultant silicon carbide particles produced in accordance with the present invention are not restricted to having no free carbon. In the prior art, it is however considerably difficult to control a process for synthesizing silicon carbide in a high temperature gaseous phase in such a manner that free carbon is completely absent. On the other hand, a process for synthesizing silicon carbide according to the present invention allows the process to be controlled in such a manner that the produced silicon carbide particles contain no free carbon. By the infrared absorption method after combustion and hydrogen hot extraction technique, no free carbon was detected in silicon carbide particles obtained by a process as mentioned above according to the present invention. Silicon carbide particles containing boron uniformly dispersed in the particles can be obtained by a two-step process comprising first forming silicon particles containing boron but no carbon compound in a first reaction zone, and then reacting the particles with a carbon compound to form silicon carbide particles containing boron in a second reaction zone. The first step can be attained by using a silicon source and a boron source which do not contain a carbon source. The second step is controlled by monitoring an unsaturated hydrocarbon by-product, as described in European Patent Publication No. EP 0 199 482. The content of boron in silicon carbide particles is preferably 5.0% by weight or less based on the silicon carbide particles. More than 5.0% by weight of boron will disturb the sintering of silicon carbide. The thus obtained silicon carbide particles containing boron dispersed throughout the particles can be formed into a shape and fired without the addition of a densifying agent such as free carbon, to give a dense silicon carbide sinter. Shaping can be carried out in any conventional manner. Firing can be achieved, for example, by heating the shaped or compacted silicon carbide particles in an atmosphere inert to silicon carbide at a temperature of 1900 degrees C to 2200 degrees C. The pressure of the atmosphere may be either above atmospheric pressure or at atmospheric or a reduced pressure. Further, the firing may be conducted by hot pressing. Since a sinter may become denser under pressure, this process is preferable. The density of a silicon carbide sinter should be 90% or more of the theoretical density for practical applications. The present invention provides a silicon carbide sinter having a density of from 98% to more than 99%. The drawing illustrates an example of an apparatus for producing silicon carbide particles according to the present invention. In Fig. 1, an electrical discharge is generated between a cathode 11 and an anode 12. Gas is introduced from a gas inlet pipe 13 and excited to form plasma, giving a high temperature higher than the melting point of silicon in two reaction zones 14 and 17. A silicon compound or silicon and a boron compound or boron are introduced to a first reaction zone 14 from inlet pipes 15 and 16 to form fused silicon particles containing boron. A carbon compound is introduced from an inlet pipe 18 to a second reaction zone 17 to react with the fused silicon particles, and silicon carbide particles containing boron, and also, if desired, free carbon, are produced therein. The resultant silicon carbide particles are recovered through an outlet 19. The gas emitted from the second reaction zone 17 through the outlet 19 may be analyzed tro control the reaction conditions in the second reaction zone, as described in patent application EP 0 199 482 The apparatus for producing silicon carbide particles according to the present invention is not limited to that shown in the drawings. For example, the method for heating the first reaction zone may be any of direct current plasma heating, high frequency plasma heating, electric resistance heating, induction heating, microwave heating, infrared heating, laser heating, etc. The second reaction zone may be heated by any of the above methods, or heating may be eliminated, or sometimes it may be necessary to cool the second reaction zone. Example 1 The apparatus used was the same as that shown in the drawing. Argon gas was introduced into the gas inlet pipe 13 at a rate of 20 ℓ/min and an electrical discharge was generated between the cathode 11 and the anode 12 under conditions of 30 V and 700 A to produce a plasma. Silane was introduced to the first reaction zone 14 from an inlet pipe 15 at a rate of 1 ℓ/min and diborane was introduced therein from an inlet pipe 16 at a rate of 0.015 ℓ/min, with argon gas as the carrier gas. The diameter of the first reaction zone 14 was 70 mm and the temperature was about 2000 degrees C. Fused silicon particles containing boron uniformly therein were produced in the first reaction zone 14. The fused silicon particles were fed into a second reaction zone 17 and methane was introduced from an inlet pipe 18 to the second reaction zone at a rate of 1 to 1.3 ℓ/min. The fused silicon particles were carbonized in the second reaction zone at a temperature of 1700 to 1800 degrees C, to produce silicon carbide particles containing boron uniformly in the particles. The resultant silicon carbide particles were recovered from an outlet 17. The exhaust gas emitted from the outlet 17 was analyzed and used to control the flow of methane, and hence the free carbon content by the method of EP 0 199 482. X-ray diffraction revealed that the resultant particles were β - type silicon carbide. By chemical analysis, etc., about 0.8% by weight of boron was detected in addition to silicon carbide and free carbon. X-ray photoelectron spectroscopy revealed the boron was elemental boron. Example 2. The synthesis of silicon carbide particles in this Example is similar to that of Example 1. However, the diameter of the first reaction zone was 60 mm and the temperature in the first reaction zone was about 2500 degrees C. Methane was introduced to the second reaction zone at a temperature of about 2000 degrees C and a rate of about 1.1 ℓ/min. The rate of methane introduction was controlled by monitoring the amount of acetylene by-product so that the resultant silicon carbide particles contained 0.6% by weight of free carbon. The resultant particles extracted from the outlet had a grain size in a range of 0.1 to 0.7 µm and an average specific surface area of 9.6 m 2 /g, from observation by a transmission type electron microscope. X-ray diffraction showed that the particles were β - type silicon carbide. By chemical analysis, etc., 0.8% by weight of boron and 0.6% by weight of free carbon were detected. Observation by x-ray photoelectron spectroscopy showed that the boron was elemental boron. The resultant silicon carbide particles were then subjected to sintering. 100 g of the silicon carbide particles were added and mixed with 5 g of oleic acid solved in acetone. The mixture was dried to evaporate acetone only. The resultant particles were subject to uniaxial forming in a metal die having a size of 5 cm at a pressure of 90 kgf/cm 2 The resultant shape was dried at 250 degrees C to evaporate oleic acid. The shape then had a density of 2.05 g/cm 2 (by the Archimedian method), corresponding to 64% of the theoretical density. The shape was sintered in a 1 atom argon atmosphere at 2160 degrees C for 2 hours. The temperature raising time from room temperature to 2160 degrees C was about 2 hours and 30 minutes, and the sinter was allowed to cool to the room temperature after the above sintering at 2160 degrees C. The resultant sinter had a density of 3.16 g/cm 3 , which corresponds to 98.4% of the theoretical density. The flexural strenghts measured according to the method of JIS R 1601 were 68 kgf/mm 2 at room temperature and 77 kgf/mm 2 at 1500 degrees C. For comparison, commercial β-type silicon carbide particles were added with boron and carbon black and sintered under the same conditions and procedures as the above. As a result, the silicon carbide sinter had flexural strengths of 55 kgf/mm 2 at room temperature and 66 kgf/mm 2 at 1500 degrees C. As can be seen, superior results were obtained by using silicon carbide particles produced by a process according to the present invention. It is believed that this is because the particles obtained by the present invention contain boron as a densifying agent extremely uniformly in all particles. Example 3 The synthesis of silicon carbide particles in Example 2 was repeated, except that silane and diborane were preliminarily mixed in a ratio of 1:0.015, followed by introducing the mixture through the inlet pipes into the first reaction zone. The characteristics of the resultant silicon carbide particles containing boron in the particles were similar to those in Example 2. Further, the sintering in Example 2 was repeated for the resultant silicon carbide particles. The resultant silicon carbide sinter had a density of 3.17 g/cm 3 (by the Archimedean method) which corresponds to 98.8% of the theoretical density. The flexural strength of the sinter were 71 kgf/mm 2 at room temperature and 81 kgf/mm 2 at 1500 degrees C. Example 4 The synthesis of silicon carbide particles in Example 1 was repeated except that methane was introduced to the second reaction zone at a rate of about 1 ℓ/min and the rate of methane introduction was controlled so that no free carbon was produced, in accordance with the amount of the acetylene by-product which was monitored. Further, the concentration of oxygen in the first and second reaction zones was kept below 0.2 ppm. X-ray diffraction revealed that the particles were β-type silicon carbide by chemical analysis, only silicon carbide and boron were detected and the boron content was 0.8% by weight of the particles. According to X-ray photoelectron spectroscopy the boron was elemental boron. Free carbon was not detected by the infrared absorption method after combustion or hydrogen hot extraction technique, and the absence of free carbon was thus confirmed. The resultant silicon carbide particles were then subject to sintering. 20 g of silicon carbide particles produced as above were transferred into a glovebox filled with argon gas and containing 0.01 ppm or less of oxygen, while the particles were prevented from coming into contact with air. In the glovebox, the particles were uniaxially formed at 90 kgf/cm2 to make pellets and the pellets were charged in a rubber bag. The rubber bag with the pellets was discharged from the glovebox and the pellets as charged in the rubber bag were statically pressed under a pressure of 7000 kgf/cm2 to form a shape. The shape was fired in a 1 atm argon atmosphere at 2080 degrees C for 2 hours. The temperature raising time from room temperature to 2080 degrees C was about 2 hours 30 minutes. The sinter was allowed to cool to room temperature after firing at 2080 degrees C. The resultant silicon carbide sinter had a density of 3.18 g/cm3 (by the Archimedean method), which corresponds to 99.1% of the theoetical density. Example 5 Example 4 was repeated, except that shapeing was conducted in air without using a glovebox. The resultant silicon carbide sinter had a density of 3.16 g/cm3 (by the Archimedean method), which corresponds to 98.4% of the theoretical density. Example 6 A silicon carbide sinter was produced by the same procedures as in Example 4 except that oleic acid was used as a binder for the shaping. Before uniaxial forming, the silicon carbide particles were added and mixed with 1 g of oleic acid solved in toluene and the mixture was dried to evaporate the acetone only. The oleic acid was evaporated after uniaxial forming and static pressing was conducted. During the above procedure, the glovebox was used and the silicon carbide was prevented from coming into contact with air. The thus-obtained silicon carbide sinter had a density of 3.18 g/cm 3 (by the Archimedean method), which corresponds to 99.1% of the theoretical density. Example 7 Example 6 was repeated except that the shaping was conducted in air without using a glovebox. The resultant silicon carbide sinter had a density of 3.16 g/cm (by the Archimedean method), which corresponds to 98.4% of the theoretical density.

Claims: A process for producing silicon carbide particles containing boron, said process comprising the steps of introducing silicon or a silicon compound containing no carbon together with boron or a boron compound containing no carbon into a first reaction zone (14) at a temperature above the melting point of silicon to produce fused silicon particles containing boron, and the reacting said boron-containing silicon particles with a carbon compound in a second reaction zone (17) at a temperature below the boiling point of silicon. A process according to Claim 1 in which the silicon compound is silane. A process according to Claim 1 or Claim 2 in which the boron compound is diborane. A process according to Claim 3 as dependent on Claim 2 in which the silane and diborane are mixed before being introduced into the reaction zone. A process according to any preceding claim in which the reactants are controlled to give silicon carbide containing 0.1 to 5% of boron by weight based on the weight of silicon. A process according to any preceding claim in which the silicon carbide contains substantially no free carbon. A process according to Claim 6 in which the silicon carbide is formed and fired without the addition of a densifying agent.

Inventors: KONDO JIRO, SAIKI GORO, KONDO, JIRO, SAIKI, GORO, KONDO, JIRO, C/O NIPPON STEEL CORPORATION, SAIKI, GORO, C/O NIPPON STEEL CORPORATION
Applicants: NIPPON STEEL CORP, NIPPON STEEL CORPORATION
Application year: 1986
Main classification: C01B31
IPC codes: C01B31, C04B35