Oil and fuel oil compositions

Abstract: Crude oils, lubricating oils or fuel oils have their flow point improved by adding to the crude oil, lubricating oil or fuel oil a minor proportion by weight of a polymer containing the repeat­ ing units: where (x) is an integer and y is 0 or an integer and wherein in the total polymer x + y is at least two.

Description: This invention relates to crude oil, lubricating oil or fuel oil compositions to which a flow improver has been added. When oils and fuel oils are subjected to low ambient temperatures especially in Northern European countries wax will separate out and impair the flow properties unless a cold flow improver is added. The effectiveness of such additives can be measured by tests such as the CFPPT and SCT and the depression of Cloud Point and Wax Appearance Point can also be ascertained. US-A-4,108,612 describes improving middle distillate fuels with respect to flow and pour point by incorporating therein halogenated polymers comprised of ethylene and free radical polymerisable monomers containing polar groups, preferred such polymers including ethylene-isobutyl acrylate copolymers and ethylene-vinyl acetate copolymers containing from about 5 to about 25 wt% chlorine. Derwent Accession No. 81-46 583D describes a fuel oil composition containing a low temperature fluidity improver comprising a copolymer of a straight chain monoolefin of 8 carbon atoms or more and an unsaturated dicarboxylic acid such as maleic, itaconic or citraconic. We have now discovered certain flow improvers which are effective in improving the cold flow properties of an oil (crude or lubricating) and fuel oils. According to this invention a crude oil, lubricating oil or fuel oil composition comprises a major proportion by weight of a crude oil, lubricating oil or fuel oil and a minor proportion by weight of an additive comprising a polymer containing the units: where x is an integer and y is 0 or an integer and wherein in the total polymer x + y is at least two and the ratio of units (II) to units (I) is between 0 and 2, the ratio of units (II) to (III) is between 0 and 2 and wherein: R¹ and R², the same or different, are C₁₀ to C₃₀ alkyl, R³ is H, -OOC R⁶, C₁ to C₃₀ alkyl, -COO R⁶, -OR⁶, an aryl or alkaryl group or halogen, R⁴ is H or methyl, R⁵ is H, C₁ to C₃₀ alkyl,or -COOR⁶, R⁶ is C₁ to C₂₂ alkyl and provided each of the groups R¹, R², R³, R⁴, R⁵, and R⁶ can be inertly substituted if desired Thus, these polymers are either homopolymers of a dialkyl itaconate or citraconate or copolymers of a dialkyl itaconate or citraconate with an aliphatic olefin, a vinyl ether, a vinyl ester of an alkanoic acid, an alkyl ester of an unsaturated acid, an aromatic olefin, a vinyl halide or a dialkyl fumarate or maleate. The groups R¹ and R² which can be the same or different are C₁₀ to C₃₀ alkyl groups, and these are preferably straight chain although they can be branched. If branched it is preferred that the branch be a single methyl in the 1 or 2 position. Examples of such groups are decyl, dodecyl, hexadecyl and eicosyl. Each of the groups R¹ and R² may be a single C₁₀ to C₃₀ alkyl group or they may be mixtures of alkyl groups. It has been found that mixtures of C₁₂ to C₁₆ alkyl groups are particularly suitable when the polymer is to be used as a flow improver in middle distillate fuel oils. Likewise, suitable chain lengths are C₁₆ to C₂₂ for use of the polymer in heavy fuel oils and crude oils and C₁₀ to C₁₈ for use of the polymer in lubricating oils. These preferred chain lengths are applicable both for homopolymers and for copolymers of dialkyl itaconates or dialkyl citraconates. When copolymers of dialkyl itaconates or dialkyl citraconates are used y is an integer. The comonomer, that is the compound of the formula: where R³, R⁴ and R⁵ are as defined above, can be one or more of a variety of compounds and in all cases mixtures of compounds having this formula can be used. When the comonomer is an aliphatic olefin R³ and R⁵ are hydrogen or identical or non-identical C₁ to C₃₀ alkyl groups, preferably n-alkyl groups. Thus, when R³, R⁴ and R⁵ are all hydrogen, the olefin is ethylene, and when R³ is methyl, R⁴ and R⁵ are hydrogen, the olefin is propylene. When R³ is an alkyl group it is preferred that R⁴ and R⁵ are hydrogen. Examples of other suitable olefins are butene-1, butene-2, isobutylene, pentene-1, hexene-1, tetradecene-1, hexadecene-1 and octadecene -1 and mixtures thereof. Other suitable comonomers are vinyl esters or alkyl substituted vinyl esters of C₂ to C₃₁ alkanoic acids, i.e. for vinyl esters when R³ is R⁶ COO-, R⁴ is H and R⁵ is H, and for alkyl substituted vinyl esters when R³ is R⁶ COO- and R⁴ is methyl and/or R⁵ is C₁ to C₃₀ alkyl. Non-substituted vinyl esters are preferred and suitable examples are vinyl acetate, vinyl propionate, vinyl butyrate, vinyl decanoate, vinyl hexadecanoate and vinyl stearate. Another class of comonomers are the alkyl esters of unsaturated acids, i.e. when R³ is R⁶OOC- and R⁵ is H or C₁ to C₃₀ alkyl. When R⁴ and R⁵ are hydrogen these comonomers are alkyl esters of acrylic acid. When R⁴ is methyl the comonomers are esters of methacrylic acid or C₁ to C₃₀ alkyl substituted methacrylic acid. Suitable examples of alkyl esters of acrylic acid are methyl acrylate, n-hexyl acrylate, n-decyl acrylate, n-hexadecyl acrylate, n-octadecyl acrylate, and 2-methyl hexadecyl acrylate, whilst suitable examples of alkyl esters of methacrylic acid are propyl methacrylate, n-butyl methacrylate, n-octyl methacrylate, n tetradecyl methacrylate, n-hexadecyl methacrylate and n octadecyl methacrylate. Other examples are the corresponding esters where R⁵ is alkyl, e.g. methyl, ethyl, n-hexyl, n-decyl, n tetradecyl and n-hexadecyl. Another suitable class of comonomers is when both R³ and R⁵ are R⁶OOC- i.e. when they are C₁ to C₂₂ dialkyl fumarates or maleates and the alkyl groups may be n-alkyl or branched alkyl e.g. n-octyl, n-decyl, n-tetradecyl, n-hexadecyl or n-octadecyl. Other examples of comonomer are when R³ is an aryl group. When R⁴ and R⁵ are hydrogen and R³ is phenyl the comonomer is styrene and when one of R⁴ and R⁵ is methyl the comonomer is a methyl styrene, e.g. α-methyl styrene. Another example when R³ is aryl is vinyl naphthalene. Other suitable examples when R³ is alkaryl are for example substituted styrenes such as vinyl toluene, or 4-methyl styrene. Another suitable co-monomer is when R³ is halogen, e.g. chlorine, such as vinyl chloride (R⁴ and R⁵ hydrogen). In all cases it is to be understood that some or all of the groups R¹, R², R³, R⁴, R⁵ and R⁶ can be inertly substituted, for example, by one or more halogen atoms, for instance, chlorine or fluorine. Thus, for example, the comonomer could be vinyl trichloroacetate. Alternatively, the substituent could be an alkyl group, e.g. methyl. The ratio of units (II) to units (I) has to be between 0 (when the polymer is an itaconate or citraconate homopolymer) and 2 (when the polymer is a copolymer) but in practice the ratio for the copolymer will usually be between 0.5 and 1.5, for example, about one. For both homopolymers and copolymers the molecular weight of the polymer will usually be between 1000 and 500,000, for example, between 2000 and 200,000. Usually the copolymer will consist of only units (I) and (II) or units (II) and (III), but other units are not excluded. However, in practice, it is desirable that the weight percentage of units (I) and (II) or of units (II) and (III) in the copolymer is at least 80% and preferably at least 90%. The homopolymers and copolymers are generally prepared by polymerising the monomers in a solution of a hydrocarbon solvent such as heptane, benzene, cyclohexane, or white oil, at a temperature generally in the range of from 20°C to 150°C and usually promoted with a peroxide or azo type catalyst such as benzoyl peroxide or azodiisobutyronitrile under a blanket of an inert gas such as nitrogen or carbon dioxide in order to exclude oxygen. The polymer may be prepared under pressure in an autoclave or by refluxing. When copolymers are to be prepared the polymerisation reaction mixture should preferably contain 0 to 2 moles of comonomer (e.g. vinyl acetate) per mole of dialkyl itaconate or dialkyl citraconate. The copolymers are suitable for use as flow improvers or dewaxing aids in crude oils, i.e. the oil as obtained from drilling and before refining. They are also suitable for use in lubricating oils, as flow improvers, pour point depressants or dewaxing aids, both mineral and synthetic. The lubricating oil may be animal, vegetable or mineral oil, for example, petroleum oil fractions ranging from naphthas or spindle oil to SAE 30, 40 or 50 lubricating oil grades, castor oil, fish oils or oxidised mineral oil. The final lubricating oil may contain other additives according to the particular use for the oil. For example, viscosity index improvers such as ethylene-propylene copolymers may be present as may succinic acid based dispersants, metal containing dispersant additives and the well known zinc dialkyl-dithiophosphate antiwear additives. The flow improvers are also suitable for use in fuel oils. These fuel oils can be the middle distillate fuel oils, e.g. a diesel fuel, aviation fuel, kerosene, fuel oil, jet fuel, heating oil etc. Generally, suitable distillate fuels are those boiling in the range of 120° to 500°C (ASTM D1160), preferably those boiling in the range 150° to 400°C, for example, those having a relatively high final boiling point (FBP) of above 360°C. A representative heating oil specification calls for a 10 percent distillation point no higher than about 226°C, a 50 percent point no higher than about 272°C and a 90 percent point of at least 282°C and no higher than about 338°C to 343°C, although some specifications set the 90 percent point as high as 357°C. Heating oils are preferably made of a blend of virgin distillate, e.g. gas oil, naphtha, etc. and cracked distillates, e.g. catalytic cycle stock. A representative specification for a diesel fuel include a minimum flash point of 38°C and a 90 percent distillation point between 282°C and 338°C. (See ASTM Designations D-396 and D-975). Improved results are often achieved when the fuel compositions of the invention incorporate other additives known for improving the cold flow properties of distillate fuels generally. Examples of these other additives are the polyoxyalkylene esters, ethers, ester/ethers amide/esters and mixtures thereof, particularly those containing at least one, preferably at least two C₁₀ to C₃₀ linear saturated alkyl groups of a polyoxyalkylene glycol group of molecular weight 100 to 5,000 preferably 200 to 5,000, the alkylene group in said polyoxyalkylene glycol containing from 1 to 4 carbon atoms. European Patent Publication 0,061,895 A2 describes some of these additives. The preferred esters, ethers or ester/ethers may be structurally depicted by the formula: R-O-(A)-O-R¹ where R and R¹ are the same or different and may be i) n-alkyl ii) iii) iv) the alkyl group being linear and saturated and containing 10 to 30 carbon atoms, and A representing the polyoxyalkylene segment of the glycol in which the alkylene group has 1 to 4 carbon atoms, such as polyoxymethylene, polyoxyethylene or polyoxytrimethylene moiety which is substantially linear; some degree of branching with lower alkyl side chains (such as in polyoxypropylene glycol) may be tolerated but it is preferred the glycol should be substantially linear. Suitable glycols generally are the substantially linear polyethylene glycols (PEG) and polypropylene glycols (PPG) having a molecular weight of about 100 to 5,000, preferably about 200 to 2,000. Esters are preferred and fatty acids containing from 10-30 carbon atoms are useful for reacting with the glycols to form the ester additives and it is preferred to use a C₁₈-C₂₄ fatty acid, especially behenic acids. The esters may also be prepared by esterifying polyethoxylated fatty acids or polyethoxylated alcohols. Further examples of the other additives for use in this invention are ethylene unsaturated ester copolymer flow improvers. The unsaturated monomers which may be copolymerised with ethylene include unsaturated mono and diesters of the general formula: wherein R⁸ is hydrogen or methyl, R⁷ is a -OOCR¹⁰ group wherein R¹⁰ is hydrogen or a C₁ to C₈, straight or branched chain alkyl group; or R⁷ is a -COOR¹⁰ group wherein R¹⁰ is as previously defined but is not hydrogen and R⁹ is hydrogen or -COOR¹⁰ as previously defined. The monomer, when R⁷ and R⁹ are hydrogen and R⁸ is -OOCR¹⁰, includes vinyl alcohol esters of C₁ to C₂₉, more usually C₁ to C₁₈, monocarboxylic acid, and preferably C₂ to C₂₉, more usually C₁ to C₁₈, monocarboxylic acid, and preferably C₂ to C₅ monocarboxylic acid. Examples of vinyl esters which may be copolymerised with ethylene include vinyl acetate, vinyl propionate and vinyl butyrate or isobutyrate, vinyl acetate being preferred. It is preferred that the copolymers contain from 10 to 40 wt% of the vinyl ester, more preferably from 25 to 35 wt% vinyl ester. They may also be mixtures of two copolymers such as those described in US Patent 3,961,916. It is preferred that these copolymers have a number average molecular weight as measured by vapour phase osmometry of 1,000 to 6,000, preferably 1,000 to 4,000. Still further examples of other suitable additives for use in the present invention are polar compounds, either ionic or non-ionic, which have the capability in fuels of acting as wax crystal growth inhibitors. Polar nitrogen containing compounds have been found to be especially effective when used in combination with the glycol esters, ethers or ester/ethers. These polar compounds are generally amine salts and/or amides formed by reaction of at least one molar proportion of hydrocarbyl substituted amines with a molar proportion of hydrocarbyl acid having 1 to 4 carboxylic acid groups or their anhydrides; ester/amides may also be used containing 30 to 300, preferably 50 to 150 total carbon atoms. These nitrogen compounds are described in US Patent 4,211,534. Suitable amines are usually long chain C₁₂-C₄₀ primary, secondary, tertiary or quaternary amines or mixtures thereof but shorter chain amines may be used provided the resulting nitrogen compound is oil soluble and therefore normally containing about 30 to 300 total carbon atoms. The nitrogen compound preferably contains at least one straight chain C₈-C₄₀, preferably C₁₄ to C₂₄ alkyl segment. Suitable amines include primary, secondary, tertiary or quaternary, but preferably are secondary. Tertiary and quaternary amines can only form amine salts. Examples of amines include tetradecyl amine, cocoamine, hydrogenated tallow amine and the like. Examples of secondary amines include dioctacedyl amine, methyl-behenyl amine and the like. Amine mixtures are also suitable and many amines derived from natural materials are mixtures. The preferred amine is a secondary hydrogenated tallow amine of the formula HNR₁R₂ wherein R₁ and R₂ are alkyl groups derived from hydrogenated tallow fat compound of approximately 4% C₁₄, 31% C₁₆, 59% C₁₈. Examples of suitable carboxylic acids or their anhydrides for preparing these nitrogen compounds (and their anhydrides) include cyclohexane 1,2 dicarboxylic acid, cyclohexane dicarboxylic acid, cyclopentane 1,2 dicarboxylic acid, napthalene dicarboxylic acid and the like. Generally, these acids will have about 5-13 carbon atoms in the cyclic moiety. Preferred acids are benzene dicarboxylic acids such as phthalic acid, tera-phthalic acid, and iso-phthalic acid. Phthalic acid or its anhydride is particularly preferred. The particularly preferred compound is the amide-amine salt formed by reacting 1 molar portion of phthalic anhydride with 2 molar portions of di-hydrogenated tallow amine. Another preferred compound is the diamide formed by dehydrating this amide-amine salt. One or more of these co-additives may be used in combination with said polymers in this invention. The relative proportions of additives used in the mixture are preferably from 0.05 to 20 parts by weight more preerably from 0.1 to 5 parts by weight of the itaconate or citraconate polymer to 1 part of the other additives such as the polyoxyalkylene esters, ether or ester/ether. The amount of polymer (flow improver) added to the fuel oil is preferably 0.0001 to 5.0 wt.%, for example, 0.001 to 0.5 wt.% (active matter) based on the weight of fuel oil. The additive of this invention may conveniently be dissolved in a suitable solvent to form a concentrate of from 20 to 90, e.g. 30 to 80 weight % of the polymer in the solvent. Suitable solvents include kerosene, aromatic naphthas, mineral lubricating oils etc. Such a concentrate is a further aspect of this invention. A still further aspect is the use as a flow improver in a middle distillate fuel of an additive of this invention. Example In this Example four copolymers (IVA) of a dialkyl itaconate and vinyl acetate (K, L, M and N) and four homopolymers (PI) of a dialkyl itaconate (A, B, C and D) were prepared and tests in the Cold Filter Plugging Point Test (CFPPT) and the Slow Cooling Test (SCT). The four homopolymers were those of di-n-decyl itaconate (A), di-n-dodecyl itaconate (B), di-n-tetradecyl itaconate (C) and di-n-hexadecyl itaconate (D) and each had M n 's of about 30,000 and M w 's of about 70,000. The four copolymers were those of vinyl acetate and respectively di-n-decyl itaconate (K), di-n-dodecyl itaconate (L), di-n-tetradecyl itaconate (M) and di-n-hexadecyl itaconate (N) each having M n 's of about 20,000 and M w 's of about 60,000 as measured by gel permeation chromatography relative to polystyrene standard, the mole ratios of vinyl acetate to itaconate being 1.0:1.0. The four copolymers and the four homopolymers were prepared by polymerising the monomers in a cyclohexane solvent using catalysts such as azo-iso bis butyronitrile, di-t-butyl peroxide or t-butyl peroctoate and refluxing. For the copolymers the mole ratio of itaconate to vinyl acetate was 1:1. The copolymers and homopolymers were then added to diesel fuels having the following characteristics: Fuel Wax Appearance Cloud Point Point D 86 Distillation ( o C) IBP 20 50 90 FBP I 1 o C +3 o C 184 226 272 368 398 II -9 o C -6 o C 170 228 316 347 III -15 o C -12 o C 159 210 316 350 IV -10 o C -10 o C 168 231 325 350 V -1.5 o C 3 o C 184 223 267 367 398 VI -3.5 o C 0 o C 166 211 251 334 376 Also each of the copolymers and homopolymers were blended in various weight ratios (active matter) with a 3:1 weight mixture additive X of (A) an ethylene-vinyl acetate copolymer having a vinyl acetate weight content (by 500 MHz NMR) of 36%, a number average molecular weight of 2000 and a degree of side chain branching methyls/100 methylenes (by 500 MHz NMR) of 4 and (B) an ethylene-vinyl acetate copolymer having a vinyl acetate weight content by 500 (MHz NMR) of 17%, a number average molecular weight of 3,500 and a degree of side chain branching methyls/100 methylenes (by 500 MHz NMR) of 8. Each of these eight blends were also added to the diesel fuel oil in a concentration (active matter) of 300 ppm (0.03 wt %) for the blend as a whole. The results were as determined by the CFPPT and the SCT, details of which tests are given below. THE COLD FILTER PLUGGING POINT TEST (CFPPT) The cold flow properties of the blend were determined by the Cold Filter Plugging Point Test (CFPPT). This test is carried out by the procedure described in detail in "Journal of the Institute of Petroleum", Vol. 52, No.510, June 1966 pp.173-185. In brief, a 40 ml. sample of the oil to be tested is cooled by a bath maintained at about -34 o C. Periodically (at each one degree Centigrade drop in temperature starting from 2 o C above the cloud point) the cooled oil is tested for its ability to flow through a fine screen in a time period. This cold property is tested with a device consisting of a pipette to whose lower end is attached an inverted funnel positioned below the surface of the oil to be tested. Stretched across the mouth of the funnel is a 350 mesh screen having an area of about 0.45 square inch. The periodic tests are each initiated by applying a vacuum to the upper end of the pipette whereby oil is drawn through the screen up into the pipette to a mark indicating 20 ml. of oil. The test is repeated with each one degree drop in temperature until the oil fails to fill the pipette within 60 seconds. The results of the test are quoted as Δ CFPPT (°C) which is the difference between the fail temperature of the untreated fuel (CFPPD₀) and the fuel treated with the itaconate polymer (CFPP₁) i.e. Δ CFPP = CFPP₀ - CFPP₁ . PROGRAMMED COOLING TEST (SCT) This is a slow cooling test designed to correlate with the pumping of a stored heating oil. The cold flow properties of the described fuels containing the additives are determined by the SCT as follows. 300 ml of fuel are cooled linearly at 1 o C/hour to the test temperature from a temperature at least 5 o C above its Cloud Point and the temperature then held constant. After 2 hours at the test temperature, approximately 20 ml of the surface layer is removed by suction to prevent the test being influenced by the abnormally large wax crystals which tend to form on the oil/air interface during cooling. Wax which has settled in the bottle is dispersed by gentle stirring, then a CFPPT filter assembly is inserted. The tap is opened to apply a vacuum of 500 mm of mercury, and closed when 200 ml of fuel have passed through the filter into the graduated receiver: a PASS is recorded if the 200 ml are collected within ten seconds through a given mesh size, a FAIL if the flow rate is too slow indicating that the filter has become blocked. The mesh number passed at the test temperature is recorded. CLOUD POINT DEPRESSION Depression of the Cloud Point (IP-219 or ASTM-D 2500) of a distillate fuel is often desirable. The effectiveness of the additives of the present invention in lowering the cloud point of distillate fuels was determined by the standard Cloud Point Test (IP-219 or ASTM-D 2500). Other more accurate measures of the onset of crystallisation are the Wax Appearance Point (WAP) Test ASTM D.3117-72 and the Wax Appearance Temperature (WAT) as measured by differential scanning calorimetry using a Mettler TA 2000B differential scanning calorimeter. In the test a 25 microlitre sample of the fuel is cooled at 2 o C/min. from a temperature at least 30 o C above the expected cloud point of the fuel. The observed onset of crystallisation is estimated, without correction for thermal lag (approximately 2 o C), as the wax appearance temperature as indicated by the differential scanning calorimeter. The results of the test are quoted as Δ WAT ( o C) which is the difference between the WAT of the base, untreated fuel (WAT₀) and the WAT of the fuel treated with additives, (WAT₁), i.e. Δ WAT = WAT₀ - WAT₁ . Good results were achieved by additives A, B, C, K, L and M above and in combination with X which are better than no additive at all or X alone. In the further Examples Polymer Y is a fumarate-vinyl acetate copolymer made from an equimolar mixture of di-n-hexadecyl fumarate and vinyl acetate in cyclohexane as solvent. The catalyst was t-butyl peroctoate. The results of testing the Additives in Fuel V are set out in Tables 1 to 3. Additive Treat (ppm) Δ WAT In FUEL V( o C) Δ WAT In FUEL VI ( o C) N 500 3.3 3.5 D 500 4.0 4.1 Y 500 3.0 3.1 Additive Treat (ppm) Δ WAT ( o C) in FUEL: II III IV M 500 1.5 2.5 3.5 1000 2.0 4.0 4.0 C 500 1.0 2.0 3.0 1000 2.0 3.5 3.0 B 500 0.0 -0.5 1.5 1000 0.0 0.5 1.0

Claims: A crude oil, lubricating oil or fuel oil composition comprising a major proportion by weight of a crude oil, lubricating oil or fuel oil and a minor proportion by weight of an additive comprising a polymer containing the repeating units: where x is an integer and y is 0 or an integer and wherein in the total polymer x + y is at least two and the ratio of units (II) to units (I) is between 0 and 2, the ratio of units (II) to (III) is between 0 and 2, and wherein: R¹ and R², the same or different, are C₁₀ to C₃₀ alkyl, R³ is H, -OOC R⁶, C₁ to C₃₀ alkyl, -COO R⁶, an aryl or alkaryl group or halogen, R⁴ is H or methyl, R⁵ is H, C₁ to C₃₀ alkyl or -COOR⁶, R⁶ is C₁ to C₂₂ alkyl and provided each of the groups R¹, R², R³, R⁴, R⁵, and R⁶ can be inertly substituted. A composition comprising a solvent and 20 to 90 weight % of an additive comprising a polymer as defined in claim 1. The use as a flow improver in a fuel oil of an additive comprising a polymer as defined in claim 1. The composition, when a fuel oil composition, or use of any of the preceding claims wherein the polymer is in combination with one or more other additives comprising a polyoxyalkylene ester, ether, ester/ether, amide/ester or mixture thereof; an ethylene unsaturated ester copolymer; or a polar amine salt and/or amide compound capable of acting as a wax crystal growth inhibitor in a fuel oil. The composition or use of any of the preceding claims wherein the relative proportions of said polymer is from 0.05 to 20 parts by weight to 1 part by weight of the other additive or additives, where present. The composition or use of any of the preceding claims wherein the groups R¹ and R² are straight chain C₁₀ to C₁₈ alkyl groups. The composition or use of any of the preceding claims wherein y is an integer so that the polymer is a copolymer and R³ and R⁵ are hydrogen or identical or non-identical C₁ to C₃₀ alkyl groups. The composition or use of any one of claims 1 to 6 wherein y is an integer so that the polymer is a copolymer, R³ is R⁶COO - and either R⁴ and R⁵ are hydrogen or R⁴ is methyl and/or R⁵ is C₁ to C₃₀ alkyl. The composition or use of claim 8 wherein the comonomer for the copolymer is vinyl acetate i.e. R⁴ and R⁵ are hydrogen and R³ is CH₃COO-. The composition or use of any one of claims 1 to 6, wherein y is an integer so that the polymer is a copolymer, R⁵ is H or C₁ to C₃₀ alkyl and R³ is -COOR⁶. The composition or use of claim 10 wherein the comonomer for the copolymer is an alkyl acrylate or an alkyl methacrylate i.e. R⁵ is H. The composition or use of any one of claims 1 to 6 where y is an integer so that the polymer is a copolymer and both R³ and R⁵ are R⁶OOC. The composition or use of any one of claims 1 to 6 where y is an integer so that the polymer is a copolymer and R³ is a halogen. The composition or use of any one of claims 1 to 6, wherein y is an integer so that the polymer is a copolymer and R³ is an aryl or alkaryl group. The composition or use of claim 14 wherein the comonomer for the copolymer is styrene, i.e. R³ is phenyl and R⁴ and R⁵ are hydrogen. The composition or use of any one of the preceding claims wherein the weight percent of units (I) and (II) or of units (II) and (III) in the copolymer is at least 80%.

Inventors: LEWTAS KENNETH, TACK ROBERT DRYDEN, LEWTAS, KENNETH, TACK, ROBERT DRYDEN
Applicants: EXXON CHEMICAL PATENTS INC, EXXON CHEMICAL PATENTS INC.
Application year: 1986
Main classification: C10M145
IPC codes: C10M145, C10L1, C10M147, C10G73, C10L10, C10N30