REAGENT FOR DETECTING ANTIGEN-ANTIBODY REACTIONS

Abstract: A reagent for detecting an antigen-antibody reaction in the form of a latex comprising as its dispersed substance a fluorine-containing polymer up to 1.42 in refractive index and having a protein adsorbed thereon.

Description: Reagent for Detecting Antigen - Antibody Reactions The present invention relates to a reagent for detecting an antigen-antibody reaction which is useful for jinmunoserologic diagnosis. The method of immunoserologic diagnosis is widely used in the field of clinical tests because of its convenience and rapidity. With this method, a latex having an antigen or antibody adsorbed thereby is used for detecting the corresponding antibody or antigen in the serum by the coagulation reaction of the latex involving an antigen-antibody reaction. The known latices useful for this purpose include one comprising polystyrene or a copolymer of styrene and styrenesulfonic acid, acrylic acid, acrylate, methacrylic acid, methacrylate, acetonitrile or the like. For the determination of an antigen or antibody with use of the latex, the coagulation reaction is conducted on a black plate, followed by visual observation, or a spectroscopic quantitative method is resorted to using a spectrophotometer. Polymers of hydrocarbons such as polystyrene have a high refractive index and differ greatly from water in refractive index, so that latices of such polymers themselves have high turbidity. Accordingly the spectroscopic quantitative method resorting to a coagulation reaction with use of the latex is likely to encounter difficulty in recognizing variations in turbidity and therefore in establishing correlation between the concentration and the turbidity. The result obtained by the quantitative method is consequently not fully reliable. The object of the present invention is to provide an antigen-antibody reaction detecting reagent for readily quantitatively determining a substance by a spectroscopic method. The above and other objects of the invention will become apparent from the following description. The present invention provides a reagent for detecting an antigen-antibody reaction in the form of a latex comprising as its dispersed substance a fluoride containing polymer up to 1.42 in refractive index and having a protein thereby adsorbed. We have found that a fluorine-containing polymer latex has high transparency and excellent properties for use as afi an antigen-antibody reaction detecting reagent. Examples of fluorine-containing polymers useful for the fluorine-containing polymer latex of the present invention are homopolymers or copolymers of fluoroolefins such as tetrafluoroethylene, hexafluoropropylene, trifluoroethylene, chlorotrifluoroethylene, vinylidene fluoride, vinyl fluoride and fluoroalkyl(meth)acrylate (exclusive of poly- tetrafluoroethylene), copolymers of such fluoroolefins and at least one of lenin and fluoroalkyl vinyl ether. Examples of olefines are ethylene, propene, fluoroalkyl- ethylene, etc. These polymers are up to 1.42, preferably up to 1.38, in refractive index. When the coagulation reaction of a latex is to be checked spectroscopically, it is desired that the latex have high transparency. To obtain a latex of high transparency, the substance to be dispersed must be a polymer the refractive index of which is not greatly different from that of water (1.33). We have found that the above-mentioned fluorine-containing polymers are lower than polymers of other hydrocarbons in refractive index and afford latices having high transparency. The fluorine-containing polymer latex to be used in this invention is an aqueous dispersion obtained by subjecting such fluorine-containing olefin(s) to emulsion polymerization or emulsion copolymerization in an aqueous medium. The latex particles are suitably 0.01 to 1 Am, preferably 0.03 to 0.3cm, in mean size. When a polymer, such as polyvinylidene fluoride, having a relatively high refractive index (1.42) is desirable or when a stable latex is required, the latex particles preferably have a small mean size, e. g. 0.03 to 0.1J2m. While the latex contains an emulsifier and other additives which are added for the preparation of the latex, it is generally desirable to remove these additives by dialysis or other procedure. Stabilizers, buffers etc. are thereafter added to the latex for the preparation of the present reagent. The method of causing the latex to adsorb a protein serving as an antigen (or antibody) will now be described. Although adsorption can be accomplished usually by mixing the latex with an aqueous solution of the protein serving as an antigen (or antibody), the following adsorption method is desirable. The protein as an antigen (or antibody) is dissolved in an NaHCO3 buffer having a pH of 7 to 9 to a protein concentration of 0.001 to 1%. The solution is admixed with the latex, and the mixture is allowed to stand at 20 to 37C for 1 to 2 hours, whereby the protein is adsorbed by the latex particles. On standing, the latex particles settle. The supernatant is removed. The same NaHCO3 buffer as above is admixed with the reaaining liquid containing the sediment, and the supernatant is removed. This procedure is repeated three times, whereby a major portion of the protein not adsorbed by the latex can be removed. Such a separating procedure is possible because the fluorine-containing polymer latex has a great specific gravity, whereas the latex of polystyrene or like hydrocarbon conventionally used and having a small specific gravity requires the use of a centrifugal separator for the same purpose. In this case, the latex often coagulates to such an extent that the particles will not be smoothly redispersible. I t is also a feature of the present invention that use of the fluorine-containing polymer latex eliminates the need for the centrifugal separation. The above method causes the latex to adsorb the antigen (or antibody), affording a reagent for detecting an antigen-antibody reaction. Examples of proteins to be adsorbed by the latex according to the invention are gamma globulin, choriogonadotropin, thymonucleic protein, thyroglobulin, anti-reactive protein antibody, anti-fibrinogen antibody, anti-gamma globulin antibody, etc. The antigen-antibody reaction can be detected using the reagent of the present invention by admixing with the liquid to be checked the present reagent adsorbing an antigen (or antibody) by the above method and detecting the resulting coagulation reaction. When the liquid contains the corresponding antibody (or antigen), a coagulation reaction occurs owing to an antigen-antibody reaction. Since the coagulation reaction is detectable as a variation in the turbidity of the mixture of reagent and liquid to be checked, the turbidity is measured by a spectrophotometer in terms of absorbance at a specified wavelength. Consequently, the antibody (or antigen) in the liquid can be quantitatively determined from an increase in the absorbance. I n practice, the quantitative determination can be conducted in the following Manner. First, a standard specimen containing a specified amount of an antibody (or antigen) is diluted to varying concentrations to prepare standard specimen dilutions. A reagent of the invention adsorbing the corresponding antigen (or antibody) is admixed with each of the dilutions for reaction. The reaction mixture is placed into a cell having an optical path length of 10om and irradiated with light of specified wavelength, and the absorbance is measured using a spectrophotometer. Based on the result thus obtained, a calibration curve is prepared which shows the relation between the amount (concentration) of the antibody (or antigen) and the absorbance Next, the reagent of the invention adsorbing the antigen (or antibody) is admixed with the liquid to be checked, and the absorbance of the reaction mixture is measured in the same manner as above. The antibody (or antigen) in the liquid can be quantitatively determined from the absorbance with reference to the calibration curve. The present invention will be described in greater detail with reference to the following examples and comparative example. Example 1 Into a three-I iter glass-I ined autoclave having an anchor type stirrer and temperature adiusting means were placed 1.5 liters of deionized and deoxidized water, 60g of paraffin wax (m.p.56C) and 9B of H(CF2CF2)4COONH4 serving as a dispersant, and the air within the autoclave was replaced by N2 gas several times. Hexafluoropropene was thereafter iniected into the autoclave to a pressure of 6.5kg/cm2G. In the meantime, the internal temperature of the autoclave was adJusted to 80 C. The internal pressure was increased to 8.Okg/cm2G with tetrafluoro- ethylene, and the stirrer was set to a speed of 300r.p.m. Subsequently, 15cc of an aqueous solution containing lg of ammonium persulfate was added to the mixture to initiate a reaction. During the reaction, tetrafluoroethylene was continuously supplied to the reaction system to maintain the internal pressure at s.0kg/cm2G, while hexafluoropropene was intermittently supplied to the system to maintain the mixture at a hexafluoropropene concentration of 65 to 75mole%. A 0.2g quantity of ammonium persulfate was further added at an interval of 4 hours. Thirty-six hours after the start of the reaction, the stirrer was stopped, and the reaction was terMinated upon releasing the monomers. A copolymer latex having a polymer concentration of 30.1wt.% was obtained. The polymer obtained was made into a film, which was checked by Abbe's refractometer (at a temperature of 20 C using D lamp) to find that the polymer had a refractive index of 1.34. The latex was purified by ultrafiltration. One part by volume of the purified latex and one part by volume of 1 wt.% human gamma globulin were admixed with 8 parts by volume of NaHCO3 buffer (0.5M Nail, 0.1M NaHCOs, pH 8.3). The mixture was allowed to stand at room temperature for one hour. The procedure of replacing the supernatant by the sane NaHCO3 buffer as above was repeated three times to remove the unadsorbed human gamma gl globulin The product was finally adjusted to a latex concentration of 1 wt.%. A 2cc quantity of the reagent thus obtained and adsorbing human gamma globulin was diluted twentyfold. The dilution was placed into a cell having an optical path length of 10mm and then checked for absorbance at a wavelength of 400nm by a spectrophotometer (Model 556, product of Hitachi, Ltd. ). The absorbance value was 0.05. A 2 cc quantity of the reagent and 0. Ice of serum containing a rheumatoid factor (rheumatoid factor detecting reagent RAS reference positive serum, product of Nippon Lyophilization Lab. Co. , Ltd. ) were mixed together, and the mixture was diluted twentyfold. The absorbance of the dilution similarly measured was 0.3. As a control test, the reagent (2 cc) and 0.lcc of serum free from the rheumatoid factor were mixed together and diluted twentyfold. The absorbance of the dilution similarly measured was 0.06. These results indicate that the presence of the rheumatoid factor (antibody) in the liquid to be tested results in a markedly increased absorbance and that the absence of the factor produces little or no increase in the absorbance. Example 2 A 2cc quantity of a latex of hexafluoro- propene-tetrafluoroethylene copolymer (hereinafter referred to as rF E P latex") having a concentration of 10wt.% and prepared in the same manner as in Example 1 was admixed with 8 cc of a solution prepared by dissolving 40mg of human gamma globulin in an NaHCO3 buffer (0.15M Nail, 0.1M NaHGO3, pH8.5). The mixture was stirred at 37C for 2 hours to cause the FEP latex particles to adsorb human gamma globulin. Next, 30cc of the same NaH C 0 3 buffer as above which further contained 1% of sucrose, 0.2M of choline chloride and 0.1% of sodium azide was added to the latex as a dispersion stabilizer. The mixture was thereafter allowed to stand1 and the procedure of replacing the supernatant by the NaHCO3 buffer was repeated three times to remove the unadsorbed human gamma globulin. The resulting mixture was finally adjusted to an FEP latex concentration of 1.2wt. % with the N a H C O a buffer. Portions (1.5cc) of the reagent adsorbing human gamma globulin were admixed with 1.5cc quantities of anti-human gamma globulin of varying concentrations. The absorbance of the mixtures was measured at a wavelength of 600nm by the spectrophotometer. The accompanying Fig. 1 shows the relation thus estabilished between the absorbance, plotted as ordinate, and the anti-human gamma globulin concentration, plotted as abscissa. Comparative Example 1 Into a four-necked separable flask having a capacity of 500cc, an anchor type stirrer and temperature adjusting leans were placed ZOOcc of deionized water, 50g of styrene and IOcc of an aqueous solution of 0.5g -of styrenesulfonic acid. The stirrer was driven at a speed of 300r.p.m., the internal temperature of the flask was maintained at 70 C, and the air in the flask was continuously replaced by N2. In this state, 10cc of an aqueous solution of 0.3g of ammonium persulfate was added to the mixture to initiate a polymerization reaction. Twelve hours after the start of the reaction, the stirring and introduction of N2 were discontinued toterminate the reaction. The polystyrene latex obtained was 15wt.% in concentration and 0.21 m in mean particle size. Using the polystyrene in place of the FEP latex of Example 2 , the relation between t-he absorbance and the anti-human gamma globulin concentration was determined as shown in the accompanying drawing by the same method as in Example 2 with the exception of using a centrifugal separator (at an increased pressure of 26,000kg/cm2G) Gr for removing the unadsorbed- human gamma globulin and finally adjusting the polystyrene latex concentration to O.O3wt.%. The polystyrene latex concentration was made lower than the FEP latex concentration (1.2wt.%) to obtain a comparable absorbance in the absence of the antibody. Fig. 1 shows that Example 2 (FEP latex reagent) resulted in a close correlation between the amount of antibody and the absorbance but that Comparative Example 1 (polystyrene latex reagent) resulted in a slight correlation therebetween. Especially the antibody, when in a very small, produces little or no increase in the absorbance. The fluorine-containing polymer latex has high transparency, undergoes a distinctive variation in turbidity owing to an antigen-antibody reaction, assures facilitated spectroscopic quantitative determination and possesses excellent properties for use as antigen-antibody reaction detecting reagent. Fig. 1 shows the results achieved in Example 2 and Corparative Example 1. It is a graph showing the relation between the absorbance and the amount (concentration) of antibody. In the graph, A represents the result achieved by the FEP latex reagent of the invention, and B that achieved by the polystyrene latex reagent of Coiparative Example 1.

Claims: Claims= 1 . A reagent for detecting an antigen-antibody reaction in the form of a latex comprising as its dispersed substance a fluorine-containing polymer up to 1.42 in refractive index and having a protein adsorbed thereon. 2. A reagent for detecting an antigen-antibody reaction as defined in claim 1 wherein the protein is selected from gamma globulin, choriogonadotropin, thymonucleic protein, thyroglobulin, anti-reactive protein antibody, anti-fibrinogen antibody and anti-gamma globulin antibody. 3. A reagent for detecting an antigen-antibody reaction as defined in claim 1 wherein the fluorinecontaining polymer is up to 1.38 in refractive index. 4. A reagent for detecting an antigen-antibody reaction as defined in claim 1 wherein the fluorinecontaining polymer is a copolymer of tetrafluoroethylene and at least one of hexafluoropropene and perfluoroalkyl vinyl ether. 5 . A reagent for detecting an antigen-antibody reaction as defined in claim 1 wherein the fluorinecontaining polymer is a copolymer of vinylidene fluoride and at least one of hexafluoropropene and tetrafluoro- ethylene.

Inventors: KOIZUMI, SHUN, SHIMIZU, TETSUO, SUGIMURA, MUTSUYUKI
Applicants: DAIKIN INDUSTRIES, LIMITED
Application year: 1986
Main classification: G01N33
IPC codes: G01N33