A STRONG STEAM-STERILIZABLE MULTIPLE-LAYER FILM, AND PACKAGES FOR PHYSIOLOGIC SOLUTIONS, MADE THEREFROM

Abstract: Strong and steam sterilizable multiple-layer plastic film for packaging physiologic solutions, (and packages made of this film) comprise one layer (the outer layer) of polyester or polyolefin and a second (an inner or middle layer) of a mixture of polyolefin and an elastomer, the latter layer providing re­ sistance to flex cracking.

Description: The invention relates to a steam-sterilizable multiple-layer plastic film to be used for packaging physiologic solutions, and a strong and sterilizable package, made therefrom, for physiologic solutions. Plastic bags for packaging physiologic solutions are well known in the medical field. They are usable whenever transparent and flexible packages, such as infusion-solution bags and blood bags, are needed. The plastic bags intended for packaging physiologic solutions must be inexpensive and easy to manufacture, must not react with the components of physiologic solutions, and must not yield their additives into physiologic solutions. Their permeability to water-vapor, air and other gases must be low, their resistance to heat must be high since they are subjected to steam sterilization at 100-120 oC , they must be easy to heat seal, and they must withstand mechanical stresses caused by the surroundings. The only plastic material fulfilling these requirements has so far been soft polyvinyl chloride, i.e. PVC (see, for example US Patent 4,507,123), in other words PVC which contains a considerable proportion of softeners, which, being small-molecule compounds, may readily diffuse from the polymer into the physiologic solution. It has been observed that a patient who has for a prolonged period been treated with an infusion solution packed in a PVC bag has absorbed a few grams of softener, which may result in a permanent hazard to the patient's health. An infusion-solution bag made of soft PVC is susceptible to the decomposing action of atmospheric oxygen and to attacks by micro-organisms, in which case they specifically dissolve the softeners and thereby destroy the bag. Attempts have been made to eliminate these disadvantages by, for example, inventing new packaging materials for physiologic solutions. A mixture of PVC and polyurethane, polybutadiene, polyacrylic nitrile and ethylene-vinyl acetate copolymer, which are mentioned in US Patent 4,453,940, are some of such materials. US Patent 4,410,162 describes a mixture of polyolefin substantially containing propylene units, a segment copolymer and possibly a softener, and US Patent 4,516,977 discloses as a packaging material a polyolefin to which some amount of some other polymer has possibly been added and which is preferably coated with a layer of polyamide, PVC, polyvinylidene chloride, polyvinyl fluoride, polytrifluorochloroethylene or polyester. FI Patent Application 84 0092 describes as a sterilizable film material a polyether-ester amide segment polymer, which may also be present in a multiple-layer film in lamination with, for example, a layer of polyolefin, polyester, polyamide, polyvinyl alcohol, ethylene-vinyl acetate elastomer, cellulose acetate, or polyvinylidene chloride. Attempts have also been made to diminish the hazards involved in the use of PVC bags by protecting the bag by means of an outer package, which may be another bag or a package made by using a deep-drawing machine, in which either the lower sheet or both the upper and lower sheets are formed into a cup shape. In addition to the above-mentioned requirements set for the inner package, the outer package must be mechanically very strong and capable of protecting the PVC package from, for example, the action of atmospheric oxygen and micro-organisms. The properties required of the outer package have best been achieved by preparing a multiple-layer film in which the properties of the materials in the different layers supplement one another. Thus the film layer which is of polyester (e.g. polyethylene or polybutylene phthalate) or polyamide (e.g. PA6 or PA66) has a high resistance to heat, a tolerably low permeability to oxygen and nitrogen, and high strength, whereas the layer made of polypropylene can be heat-sealed, is softer, and has a low permeability to moisture. Multiple-layer films of the following types, among others, known in the art, have so far been used as outer packages for physiologic solutions. Layer 1/layer 2 Thickness of layer 1/thickness of layer 2, µm PA/PP 20/75 PA/PP 50/75 PA/PP 80/100 polyester/PP 30/75 polyester/PP 12/75 co-PP/PP 50/100 PA = polyamide PP = polypropylene co-PP = copolymer of polypropylene Also known in the art are multiple-layer films suitable for outer packages, with one layer of polypropylene copolymer and the other layer of polypropylene. These package alternatives in accordance with the state of the art, by means of which endeavors have been made to replace PVC as a packaging material or to reduce the hazards of PVC with the aid of an outer package, have, however, their own disadvantages. The materials replacing PVC are often expensive special-purpose plastics, or they have propeties inferior to those of PVC, and therefore they have not been capable of replacing PVC as a packaging material for physiologic solutions. The polypropylene used as an outer packaging material crystallizes during sterilization and loses some of its elastic properties. When polypropylene is one of the layers in multiple-layer films, the result obtained after steam-sterilization is a package which is unsatisfactory with respect to its mechanical properties, cracking easily when flexed (poor flex crack resistance). Therefore the problem of the present invention is to provide a film which is suitable for replacing the inner and/or outer packages so far used for physiologic solutions. Such a film must be stable and capable of being steam-sterilized at a temperature of at least 120°C, and it must even after steam-sterilization retain its good mechanical properties. According to the invention, this problem has been solved by means of a multiple-layer plastics film for packaging physiologic solutions comprising a first layer (A) consisting of polyester, polypropylene or a mixture of polypropylene and elastomer and characterised by a second layer (B) consisting of a mixture of polypropylene and 10-60% by weight elastomer. According to the invention, by using the multiple-layer film a physiologic-solution package is obtained which is inexpensive and easy to manufacture, and in which stability, heat-sterilizability, heat-sealability, impermeability to air and water vapour, and good mechanical properties are combined. It has surprisingly been observed that by preparing the second layer of the multiple-layer film of a mixture of polypropylene and 10-60% by weight elastomer a physiologic-solution package having the above-mentioned properties is obtained, a package which retains its mechanical properties also after heat-sterilization. This layer does not crystallize as easily during sterilization as does pure polypropylene, and so it retains the strength of the multiple-layer film in spite of heat-sterilization treatment. The elastomer can be any elastomer miscible with polypropylene, for example ethylene-vinyl acetate elastomer. Figure 1 shows diagrammatically the dependence of heat resistance (softening point) and toughness (flex crack resistance) on the composition of the polypropylene-elastomer mixture layer. Since an increase of the elastomer proportion increases the toughness of the multiple-layer film but reduces its resistance to heat, the mixture works within a range of 10-60% by weight elastomer, and best within a range of 15-50% by weight elastomer. This inventive idea can be applied either by preparing a new inner package for physiologic solutions, whereby, in the optimal case, the outer package is rendered unnecessary, or by preparing a new outer package for physiologic solutions. Also the units through which the package is filled and discharged my advantageously contain this mixture of polypropylene and elastomer according to the invention. Preferably, a third layer (C) is provided consisting of, for example, polyethylene, preferably linear polyethylene or polypropylene. The first layer, for example, consists of a more heat-resistant mixture of polypropylene and an elastomer, or a heat-resistant plastic such as a polyester. In a multiple-layer film according to the invention, intended for the outer package, it is also possible to use a polypropylene first layer. The advantage of polypropylene is based on its good adherence to a polymer-elastomer mixture, in which case no adhesive is needed between the layers. Figure 1 depicts diagrammatically the effect of the composition of the polypropylene-elastomer mixture on the softening temperature and flex crack resistance of the mixture. Figure 2 depicts the cross section of one embodiment of the multiple-layer film according to the invention. Figure 3 depicts one embodiment of the outer package for physiologic solutions, according to the invention. Figure 4 depicts another embodiment of the outer package for physiologic solutions. Figure 5 depicts the Flex-Crack apparatus of Wipak Oy. The multiple-layer film can be prepared, for example, by laminating the individual layers together by using an adhesive, by preparing it directly by a coextrusion blowing technique, by a flat coextrusion method, or by a coating technique. These are conventional methods of manufacturing multiple-layer films, well known to an expert in the art, and they are also suitable for the manufacture of a multiple-layer film according to the present invention. Neither the number nor the thickness of the layers is crucial from the viewpoint of the invention, and they can be optimized for each use. According to one preferred embodiment of the invention, a triple-layer film according to Figure 2 is used. The first layer (A) is heat resistant material, e.g. polyester, polypropylene or a heat-resistant mixture of polypropylene and an elastomer. The purpose of this layer of the film is for its part to prevent the penetration of water vapour into the package, and mainly to protect the other layers of the laminate from high temperature. Such temperatures are present when packages are manufactured by heat-sealing, and they are about 160-180°C, i.e. much higher than the steam-sterilization temperatures. A mixture of polypropylene and an elastomer, or a linear polyethylene, or polypropylene is used for the sealed layer (C). This layer may be either the second layer or the third layer. When a linear polyethylene is used it is advantageous to use a quality having greater heat resistance and a density of 0.940-0.960g/cm³. Low permeability to water vapour and good heat-sealability are important among the properties of this layer. Its Vicat Softening Temperature must be high enough so that the product packaged will not adhere to the inner surface of the layer during steam-sterilization at about 120°C. For the second layer (B) it is possible to select a polypropylene-elastomer mixture by means of which very good mechanical properties are achieved. The heat resistance of the second layer need not be so high as that of the first layer. The Vicat Softening Temperature is also not so critical as in the third layer, since the layer will not come into direct contact with the product to be packaged. This layer, in which the proportions of polypropylene and elastomer are according to Claim 1, has a crucial importance for the mechanical properties of the laminate. The toughness of the laminate can be increased by increasing the proportion of elastomer, but on the other hand the increase of elastomer increases the price of the film, and thus there is no reason to increase the elastomer proportion more than is necessary for practical purposes. For cases requiring great elasticity it is possible to increase the proportion of elastomer so that, for example, in the second layer the proportion of elastomer is high, the third layer is linear polyethylene, and the first layer is polyester. Before sterilization the inner package for physiologic solutions is packed in the outer package according to the invention, and air is sucked out of the outer package. The outer package may be a bag made from a multiple-layer film according to the invention, sealed on three sides (Figure 3), or it may be a sheet of a multiple-layer film according to the invention, in which case the packaging is carried out by using a so-called deep drawing machine (Figure 4). In this case the multiple-layer film according to the invention, sealed on three sides (Figure 3), or it may be a sheet of a multiple-layer film according to the invention, in which case the packaging is carried out by using a so-called deep-drawing machine (Figure 4). In this case the multiple-layer film according to the invention is shaped into a cup in which the inner package for physiologic solutions is placed, whereafter the upper sheet made of a multiple-layer film according to the invention is heat-sealed to the lower sheet. Experiment The following experiment was carried out on films according to the invention in order to test their heat-sterilizability and their mechanical properties. The elastomer was Esso's ethylene-vinyl acetate elastomer Ex 233. First, four flat films according to the invention were prepared by a conventional lamination technique; the structures of the films were as follows (layers, see Figure 2): Film 1 according to the invention: Layer Material Thickness, µm A polyester 30 B PP-elastomer mixture 100 C PP 38 Film 2 according to the invention: Layer Material Thickness, µm A polyester 30 C PP-elastomer mixture 100 Film 3 according to the invention: Layer Material Thickness, µm A oriented polyester 12 B PP-elastomer mixture 70 C PP 38 Film 4 according to the invention: Layer Material Thickness, µm A oriented polyester 12 C PP-elastomer mixture 70 Then two films according to the state of the art, with the following structures, were prepared by the lamination technique: Film 1 according to the state of the art: Layer Material Thickness, µm A polyester 30 C PP 75 Film 2 according to the state of the art: Layer Material Thickness, um A PA 50 C PP 75 Wipak Oy's Flex-Crack test was performed on these films according to the invention and according to the state of the art, having normal permeability to gases and water vapor; the test was performed in the following manner (see Figure 5): Film layer 1 is secured to two parallel rings 2 in such a way that it forms a cylindrical surface. One of the rings is then brought towards the other ring by a helical movement, at which time it also rotates, wrinkling the plastic film helically. Thereafter the movement takes place back to the intial position. The duration of one sequence is about 1 s, and the duration of the whole test is about 20 min. After the test, blotting paper 4 is placed on a horizontal, porous board 3 evacuatable from below, on top of it is placed the film 1 just treated, and they are pressed by means of ring 5 tightly against the porous board 3. After evacuation, a drop of colored liquid 6 is dropped on the film surface, whereupon the liquid quickly passes through any holes in the film. By counting the number of colored stains in the blotting paper the number of holes in the film is obtained, which is a measure of the damage caused to the film by the mechanical treatment. The results are shown in Table 8. The experiment shows that the films aaccording to the invention are mechanically superior compared with films intended for the same purpose, and that these excellent mechanical properties are retained also after steam-sterilization. Thus the films according to the invention are very suitable for sterilized and heat-sealed packages for physiologic solutions.

Claims: A multiple-layer plastics film for packaging physiologic solutions comprising a first layer (A) consisting of polyester, polypropylene or a mixture of polypropylene and elastomer and characterised by a second layer (B) consisting of a mixture of polypropylene and 10-60% by weight elastomer. A film according to claim 1 characterised in that the elastomer in the second layer is an ethylene-vinyl acetate elastomer. A film according to claim 1 or claim 2 characterised in that the second layer consists of a mixture of polypropylene and 20-50% by weight elastomer. A film according to any one of claims 1-3 characterised in that the first layer consists of a polyester, e.g. polyethylene terephthalate or polybutylene terephthalate. A film according to claim 4 characterised in that the first layer consists of an oriented polyester. A film according to any preceding claim characterised by a third layer (C) consisting of polypropylene. A film according to any one of claims 1-5 characterised by a third layer (C) consisting of polyethylene, preferably linear polyethylene having a density of 0.94-0.96g/cm³. A plastic package for physiologic solutions comprising a film according to any preceding claim wherein the first layer forms the outer surface of the package. A package according to claim 8 having connection units, through which it may be filled or discharged, characterised by the units consisting of a mixture of polypropylene and 10-60% by weight elastomer.

Inventors: MAASOLA, HANNU OLAVI
Applicants: WIHURI OY
Application year: 1986
Main classification: B32B27
IPC codes: A61J1, B32B27, B65D65