IMPROVED CUTTING EDGES

Abstract: A process for providing an improved cutting blade (1) comprising the operations of depositing in vacuo upon a re­ gion of a surface of a blade which it is desired to form into a cutting edge (2) a layer (3) of material capable of forming a compound harder than the material of the blade, and bom­ barding the deposited material (3) with ions of a second ma­ terial (6) capable of reacting with the deposited material (3) to form the said compound, the ions of the second material having an energy sufficient to cause at least some ion beam mixing of the hard coating with the material of the blade.

Description: Improved Cutting Edges The present invention relates to the production of cutting edges. Knives and other cutting edges which are intended for use in corrosive environments may be fabricated from alloys such as those of titanium, or stainless steel. Scalpels in particular are made of titanium alloys because of their lightness. Unfortunately, such materials are softer than those usually used for cutting edges, so that the provision and maintenance of sharp cutting edges is difficult. Attempts to provide hard surfaces by conventional coating processes such as chemical vapour or plasma vapour deposition do not give a sharp edge because the coatings produced are too thick, and often are irregular also. According to the present invention there is provided a process for providing an improved cutting blade, wherein there is included the operations of depositing in vacuo upon a region of a surface of a blade which is adapted to form a cutting edge a layer of at least one material which is capable of forming a compound which is harder than the material of the blade, and bombarding the deposited material with ions of at least one other material such as to react with the deposited material to form the said compound or compounds the said ions having an energy sufficient to cause at least some ion beam mixing of the compound or compounds with the material of the blade. There may be included also ions of other materials, which may act to provide coatings of mixed compositions, or to enhance the ion beam mixing of the coating with the substrate material. Suitable materials to be deposited are boron, tungsten, titanium, vanadium or hafnium, and suitable second materials are nitrogen in the form of N+ ions, and/or carbon in the form of CO+ ions. A suitable thickness for the layer of deposited material is O.1 to 0.2 cm. A suitable ion dose is at least 25% of that required for stoichiometry in the surface layer, implanted with energies in the range of 10 to 200 keV. Not only does the ion bombardment process result in a hard surface layer which does not have a distinct boundary between it and the main body of blade material thus ensuring that it does not become detached in use, but the non-equilibrium nature of the process enables hard compounds to be formed which cannot be achieved by other deposition processes such as chemical or plasma vapour deposition. The invention will now be described by way of example, with reference to the accompanying drawings, in which Figure 1 illustrates the stages of a process for carrying out the invention, and Figure 2 shows how a desired distribution of deposited material can be achieved. Referring to Figure 1, (a) shows a section of a blade 1 having a cutting edge 2 of chisel form. Scalpels and single-edged razor blades are examples of cutting edges of this type. The blade 1 is made of a titanium alloy or a stainless steel. A coating 3, of between 0.1 and 0.2 m of boron is deposited on one surface 4 of the cutting edge 2 of the blade 1, by means of electron beam evaporation 5 from a source which is not shown in Figure l(b). The coated surface 4 of the cutting edge 2 of the blade 1 is then bombarded by a beam 6 of nitrogen ions, as is shown in Figure l(c). The nitrogen ions have an energy of 10 to 200 KeV, and the bombardment is continued until sufficient nitrogen has been implanted to cause at least 25 per cent of the boron to be converted to boron nitride. In additionto reacting with the boron, the nitrogen ions cause it to migrate into the main body of blade 1 by means of the process known as ion beam mixing. The result is to produce a region of graded composition 7 between the hard surface ceramic layer 8 of boron nitride and the softer main body of the blade 1, as shown in Figure l(d). The whole process is carried out in a vacuum of about 10-5 torr. In use, the softer main body of the blade 1 wears away preferentially, leaving the hard surface layer 8 and the region 7 exposed to form a self-maintaining fine cutting edge. If desired, carbon can be implanted with the nitrogen so that the surface layer 8 has a mixed composition of boron carbide and nitride. Other materials which form hard nitrides or carbides, such as tungsten, vanadium, hafnium or titanium can be used. Titanium, of course, would not be used if the blade itself is made of titanium. In practice, the coating need only be applied to a restricted region of the blade 1. Advantage can be taken of the straight line trajectory of particles in a vacuum to achieve this, either by stacking a plurality of blades 1 at an angle to the incident atoms and ions, as shown in Figure 2 or causing them to traverse a hump, 31 in a track, 32 as shown in Figure 3, so that only the tip 33 of the blades 1 are exposed to the atoms and ions.

Claims: Claims 1. A process for providing an improved cutting blade, wherein there is included the operations of depositing in vacuo upon a region of a surface (4) of a blade (1) which is adapted to form a cutting edge (2) a layer (3) of at least one material which is capable of forming a compound which is harder than the material of the blade, and bombarding the deposited material with ions (5) of at least one other material such as to react with the deposited material (3) to form the said compound or compounds the said ions (5) having an energy sufficient to cause at least some ion beam mixing of the compound or compounds with the material of the blade (1). 2. A process according to claim 1 wherein the one or more materials which can form a compound or compounds harder than the material of the blade is selected from the group comprising boron, tungsten, titanium, vanadium and hafnium. 3. A process according to claim 1 or claim 2 wherein the other material is nitrogen or carbon. 4. A process according to claim 3 wherein the carbon is in the form of carbon monoxide ions. 5. A process according to any preceding claim wherein the layer of deposited material has a thickness between 0.1 and 0.2sum. 6. A process according to any preceding claim wherein the ion dose of the said other material is greater than 25 per cent of that required for stoichiometry of the said compound or compounds in the surface region (4) of the blade (1). 7. A process according to any preceding claim wherein the ions (5) of the other material are implanted with energies in the range of 10 to 200 keV. 8. A process substantially as hereinbefore described and with reference to the accompanying drawings.

Inventors: DEARNALEY, GEOFFREY
Applicants: UNITED KINGDOM ATOMIC ENERGY AUTHORITY
Application year: 1986
Main classification: C23C14
IPC codes: C23C14, C23C26, B23P15