LIPID CONTAINING PLASTICS

Abstract: Plastics materials may be plasticised using lipids as the sole plasticiser or in combination with conventional plasticisers. When appropriate lipids are used thermosetting plastics and elastomers may be rendered biocompatible or therapeutic articles and sustained release medicaments may be formed.

Description: Lipid containing plastics. The present invention relates to new plastics materials especially materials suitable for use in biomedical applications, articles formed from such materials and processes for modifying the physical and biological properties of plastics materials. Thermoplastic materials are frequently employed in the construction of a wide variety of articles used in modern medicine but a great deal of medical devices are nowadays made out of either thermosettings or elastomers. Elastomers, by nature of their long-chain molecules, are able to withstand large deformations and return to their original dimensions. A number of elastomers (commonly referred as rubbers) have been tried as implant materials. These include acrylate, butyl rubber, chlorosulfonated polyethylene(Hypalon) , epichlorohydrin rubber(Hydrin) , natural rubber, polyurethanes(Esthane) , and silicone rubbe (Silastic) . The thermosetting plastics, contrary to thermoplastics, cannot be melted, reshaped or reformed upon reheating because the polymerization reactions that have taken place are irreversible. Epoxy polymers are the only thermosetting materials that have been used successfully as implant materials. A plasticiser or softener is a substance or material incorporated in a thermoplastic or an elastomer. to increase its flexibility, workability or distensibility. Plasticisers are also used to alter the physical properties, e.g. brittleness, of thermosetting plastics. A plasticiser may reduce the melt viscosity, lower the temperature of second-order transition or lower the elastic modulus of the product. The plasticiser molecules neutralize the secondary bonds, known as van der Waal's forces, between the polymer molecules increasing the mobility of the polymer chains and reducing their crystallinity. Thus plasticisers are added to plastics mainly to improve flow, and thereby processability, and to reduce brittleness. The plasticiser added is usually required to lower the glass-transition temperature to below ambient temperature. The properties of thermoplastics then change from hard, brittle, glass like materials to soft, flexible, tough materials. To be effective and useful, a plasticiser must be compatible with the host plastic material. Since the molecular weight and size of plasticiser molecules are relatively small, when compared with high polymer molecules, the thermodynamic difficulties in mixing are not as great as with mixtures of high polymers. Nevertheless, since another requirement of a plasticiser is that it be nonvolatile and nonmigrating, substantial molecular weights are desirable and the choice of plasticisers for a given plastic is fairly narrow. Generally, plasticisers depend on polar intermolecular forces between the plasticiser and the polymer, this explains why plasticisation is difficult to achieve in nonpolar polymers, such as the polyolefins. It is also important to note that plasticisation is difficult to achieve with highly crystalline polymers. Amorphous polymers and slightly crystalline materials are most usefully plasticised. The two major sub-groups of plasticisers are the internal plasticisers i.e. a second monomer which is copolymerised into the polymer structure, thereby making it less ordered and, therefore, more difficult for the chains to fit closely together, and the external plasticisers which are often classified into simple and resinous types. Simple plasticisers are usually individual chemical compounds whose constitution and physical and chemical properties are known. Resinous plasticisers include polyesters obtained by polymerization of unsaturated monomers, and usually contain a range of molecular weights so that their chemical constitution is not normally well known. Simple and resinous plasticisers are frequently given the alternative names monomeric and polymeric, respectively. However, alternative ways to describe them are as "low molecular weight plasticisers" and "high molecular weight plasticisers". The majority of simple plasticisers are high-boiling esters of polybasic acids such as phthalate, phosphate, adipate and azelate esters. These substances remain in the plastic material after processing and modify its properties. Loss of plasticiser from such systems can occur by volatility, extraction by solvents, and migration into other media. This can lead to the deterioration of the physical properties of the plastic. Polymer plasticisers, which are mostly polyesters, on the other hand, are removed much less readily by these three methods by virtue of their higher average molecular weight and this type of plasticiser, therefore, exhibits a greater degree of permanence than the simple plasticisers. In general, these advantagous properties of polymeric plasticisers are offset to some extent by certain disadvantages as compared with low molecular weight plasticisers. These disadvantages include higher price, greater difficulty in handling and processing, lower plasticising efficiency, and the poorer low-temperature properties shown by the plastic composition. Biomedical applications of polymers include use as implants, prostheses, blood or tissue contacting devices, artificial organs like blood detoxificators and oxygenators. However, there are at the present time many difficulties and problems associated with the use of these polymers, due to the incompatibility of living tissues and foreign materials artificially inserted in the body, and adverse reactions including protein deposition, adhesion and destruction of red blood cells, platelet adhesion and aggregation, and blood coagulation, can occur. Surprisingly we have now found that lipids may be incorporated into plastics to modify the physical properties usually in the manner of an external plasticiser and may therefore replace some or all of the conventional internal or external plasticisers normally included in such plastics. Moreover by choosing appropriate lipids the biological properties of the plastics may be adjusted for instance to improve their biocompatibility, or to confer other important biomedical properties such as thromboresistance or antitumor activity. In appropriate circumstances the lipid plasticiser may leach from the plastics material and this can be exploited by using the materials as sustained release or depot formulations of pharmacologically active lipids. Accordingly the present invention provides a plastics material comprising a polymer and a lipid. Preferably the plastics material is suitable for use in biomedical apparatus, surgical implants and other applications where the biological properties of the plastic are important. Usually the polymer will be one that is already known for use in biomedical applications, a mixture of such polymers or a copolymer. Typical such polymers include thermoplastics such as cellophane, cellulose acetate, polyolefins, fluorinated hydrocarbons(Teflon) , polyhydroxyethylmethacrylate(PHEMA) (Hydron), PMMA, polycarbonate and polyvinylchloride(PVC) and particular examples of known polymer types and their biomedical applications are given in Table I below: - 7 - TABLE 1 POLYMER USES Acrylate elastomers. Prostheses. Chlorosulfonated polyethylene Vascular surfaces. (Hypalon). Pure natural rubber. Polyurethanes (Esthane)(Ostamer) Prostheses, artificial hearts, (Riomer)(Pellethane)(Lycra/Spandex) vascul ar surfaces. (Cardiothane)(Tecoflex). Silfcone rubber (Silastic). Artificial hearts and val ves, blood oxigenator films. Ce lophane. Dialysis membranes. Cellulose acetate. Fluorocarbons (Teflon). Vascular and bulk implants. Polyhydroxyethylmethacrylate (PHEMA). Contact lenses, drug delivery, catheters, Polymethylmethacrylate (PMMA)(Lucite) suture coating, prostheses. (Plexiglas)(Perspex). Polyethylmethacrylate (PEMA). Polya ides (Nylon). Sutures, fabrics. Polyethyleneterephthalate (Dacron) (Terylene)(Mylar). Silk. Polymonochloro-p-xyly1ene. Encapsulants of electronic components Epoxy resins. for implantation. Polyethylene (Vitrathene). Prostheses. Polypropylene. Components of blood oxygenators and dialyzers, heart valves. Polyvlnylalcohol (PVA). Dialysis films. Polyvinylchloride (PVC). Blood bags, blood tubing, prostheses. Polyvinylidenechloride Vascular surfaces. Particular Examples of such known polymers are those in Table II below: TABLE II Glass Transition Molecular Temperature, Density - FO YttER Weight (T , β C) (d.. g. cπf J ) y Poly (acryl amide) 5xl0 6 /6xl0 6 165 1.302 Pal (acryl ic acid) 250000 106 Fσly(acrylonitrile) 85 1.184 Polya ide resin 95/200 0.98 Poly(l-butene) high 0.91 Pαly(l,4-butylene terephthal ate) 66 1.31 PoTy(butyl methacryl ate) high 27 1.07 FαTy(tertbutyl methacryl ate) 107 1.022 Poly(4-tertbutyl st rene) 132 Polycarbonate resin 20000/25000 150 1.20 Poly(cyclohexyl methacryl ate) 104 1.100 Poly(Z,-5-dimethyl-l,4-phenylene oxide) 211 1.06 PoTy(ethylene) 0.92/0.95 FσTy (ethyl ene) chlorinated 1.1/1.2 Foly (ethyl ene glycol) 3000/14000 1.2 Pol y( ethyl ene oxide) Foly(ethylene terephthal ate) 81 1.37 Poly(ethyl methacryl ate) very high 66 1.11 Nylon 6, 6/6, 6/9, 6/10, 6/12, 11, 12 37/242 1.0 Pσlyi ide 310 1.4 Poly (i sobutyl methacryl ate) high 53 1.09 Pαly(4-i sopropyl styrene) 87 FσTy(methyl methacryl te) low 114 1.188 Poly(4-methyl styrene) 106 1.04 Poly(styrene) 100 1.047 PoT sulfone resin 190 1.24 FoTy(tetraf luoro ethylene) 130 2.00 Po-ly (.vinyl acetate) PσTy vinyl alcohol) 115000 99 1.269 Poly (vinyl butyral) 36000 51 1.083 Poly (vinyl chloride) &ry high 85 1.385 Poly(vinyl formal) 108 1.23 Other biomedical applications of interest where excellent biocompatibility is important are blood carrier bags, dialysis membranes, blood oxygenator films, tubing, connectors, stoppers, closures for dialysis and oxygenation machines, adhesives, diagnostic catheters, surgical drapes and tapes, contact lenses, encapsulants for electronic devices and cell culture plastic materials. The lipid used to modify the physical and biological properties of the polymer may be any amphipathic compound having one or more long chain saturated or unsaturated fatty side chains (e.g. fatty acids, alcohols or amines) , or a mixture of such compounds. The lipid may be polar or non-polar (neutral or zwitterionic) and, if polar, may be one which, in aqueous solution, bears a positive or negative charge. Preferably the lipid is a naturally occurring one such as any of the 100 or so distinct lipids which have been identified as being present in cell membranes especially mammalian and particularly in human cell membranes. As used herein the term "lipid" does not include glycerol esters which are commonly regarded as oils, fats or waxes rather than lipids. Suitable lipids for use in the present invention will usually fall into one of the following classes: phospholipids, sphingolipids, glycolipids or cholesterol and cholesterol esters, although certain lipids, such as cerebrosides and gangliosides may be classified as both sphingolipids and glycolipids. A phospholipid contains in its structure a phosphate ester linkage with a glycerol residue and is a diester molecule of long chain acids such as oleic and stearic acids. The major phospholipids present in cell membranes are the phosphatidylcholines. These particular lipids have been shown to have no influence on blood clotting times when examined in Stypven tests of blood coagulation. However there also occur in some biological membranes small amounts of other lipid molecules, for instance, a phospholipid called Platelet Activating Factor (1) because of its potent platelet aggregation activity (2) . This lipid appears to play a major role in various inflammatory and allergic states (3) . Another lipid found in natural membranes is Phospholipid Antithromboplastin, so called because of its potent anti-coagulant properties. It is believed that this lipid is an unsaturated phosphatidylserine (4) . Although it is generally accepted that negatively charged lipids such as phosphatidylserine are procoagulant whilst those which are electrically neutral, such as the phosphatidylcholines, are not (5), cerebroside sulfate (a negatively charged lipid) has also been tested for anti-atherosclerotic and anti-coagulant activities with positive results (6) . Sphingosine lipids have been examined as physiological inhibitors of blood clotting whilst crude bovine brain cephalin and soybean phosphatides act as clot promoting agents (7,8). Another group of phospholipids having important biocharacteristics, providing medical applications for lipid plasticisers are the phosphatidylinositol lipids. The animal phosphatidylinositols, in contrast to the plant phosphatidylinositols which differ in the fatty acids acylating positions 1 and 2 of the glycerol moeity, are reported to be able selectively to kill cultured tumor cells (9,10). Other phospholipids, including phosphatidylinositol or phosphatidylserine from animal origin, synthetic phosphatidic acid, phosphatidyl glycerol or phosphatidylcholine have been shown to be non-cytotoxic. The lipids used in the present invention may consist of previously extracted and purified natural membrane components or synthetic materials of the same or similar structures. Of the lipids which may be used in the present invention, particularly suitable or preferred lipids are as follows: Phospholipids Lecithins (e. g. from soybean or egg yolk) β -Lysophosphat i dy 1 chol i nes ^-Lysophosphati dyl ethanol ami nes «f-Lysophosphatid 1 nosi to! s ΛT-Lysophosphati dyl serf nes Λf-Phosphatidic acids -Phosphati dyl chol 1 nes ^-Phosphati dyl ethanol ami nes Ar / -Phosphati dyl glycerol s -Phosphatidyl nosi to! s ■^-Phosphatidyl seri nes 1-0-Al kyl -2-acetyl -sn-glycero-3-phosphoryl chol i nes SPHINGOLIPIDS Ceramides Gangl iosides Glucocerebrosides Sphingomyelin Phytosphingosine Psychos ine Sphingosine Sphi ngosy 1 phosphory 1 chol i ne Sulfatides The amount of lipid included depends upon a number of factors . By controlling the proportion of lipid/polymer , the physical properties of the plastic material can be modulated and if desired , at the same time, by choosing the appropriate type and quantity of lipid or mixture thereof , especially a phospholipid , glycolipid or sphingolipid or a phospholipid and/or sphingolipid and/or glycolipid mixture, the appropriate biocompatibility, thromboresistance, antitumoral activity or other lipid-associated function can be conferred. As regards biocompatibility and thromboresistance the mere presence of appropriate phospholipids entrapped in the polymer matrix at its interface with biological fluid or tissue can modify the interface providing the appropriate biological effect. This idea is supported by the evidence accumulated in favour of the role played by particular phospholipids in conferring haemocompatible characteristics to plasma membranes of red blood cells and platelets. Such membranes present asymmetric lipid compositions between the inner and the outer surfaces of the cells, the negatively charged phospholipids being located predominately in the inner surface which exhibits high procoagulant activities, whereas the zwitterionic phospholipids found in the outer surface are inactive in coagulation tests. It is believed that this asymmetry may serve to keep the adequate thromboresistance of blood cells. Thus by imitating the lipid composition of these cell surfaces when formulating the plasticisers it will be possible to modify the plastic surfaces thereby producing polymers with some of the natural biomembrane characte istics. For sustained release of depot formulations it is possible to take advantage of the diffusion of plasticising lipid molecules and their release from the polymer matrix affording the slow release of the lipid into the surrounding tissue of minute amounts of, for instance, highly active phospholipid or sphingolipid ingredients such as the Phospholipid Antithromboplastin material. However a high rate of diffusion and release may not always be desirable and a compromise between total stability and a controlled diffusion rate can be reached in order to provide the required mechanical and biological properties of the implant. usually plastics materials according to the invention will contain plasticising lipid at up to 30% by weight of the weight of the polymer and this may be present as the sole plasticiser or in combination with other conventional plasticisers. However with particular plastics and when appropriate for a desired application certain plastics materials according to the invention may contain far higher quantities of plasticising lipid, for instance up to 50% (for example in the case of polyvinyl acetate) and even up to 60% (such as in the case of polystyrene) or 70% (for example in the case of polyvinyl chloride) . Other plastics will not accept such large quantities of plasticisers and in some cases (for example with methacrylate polymers) the maximum content of plasticisers may be as low as 2 to 3%. The minimum quantity of lipid to be included depends upon the particular plastic and lipid in question but should always be sufficient to provide detectable modification of the rheological or other physical properties of the plastic polymer. Typically plastics materials according to the invention will contain at least 0.01% lipid by weight of the polymer, preferably 0.1% and more preferably 0.5%. Usually plasticising lipid will be included at a level considerably above the minimum, for instance 1%, 2% or 5% and, depending upon the desired end use of the plastics material, plasticising lipid may be added at 10%, 15% or 20% by weight of the weight of the polymer. Other ingredients conventionally employed in plastics technology such as other plasticisers, fillers, colourants, UV absorbers, antioxidants and preservatives such as biocides, especially fungicides, may be included at the usual levels but should be chosen to be compatible with the lipid plasticiser and to avoid undesirable or adverse effects in view of the desired end use of the plastics material. Many considerations as well as the desired end-use of the plastics material must be taken into account when selecting the particular plasticising lipid or lipids to be used and these are discussed below. Compatibility The lipid which is to be used has to be tested for compatibility with the host polymer. This may be achieved by grinding and mixing different proportions of lipid-polymer together and trying to produce a homogeneous melt by gradually heating the sample, by use of a suitable solvent to disperse both polymer and plasticiser then evaporating the solvent or by other suitable techniques. Glass Transition Temperature (T ) For all compatible mixtures this has to be determined. Differential Scaning Calorimetry (DSC) is one of the best technique to measure this parameter. Melt Flow Rate The samples with a glass transition temperature below the ambient may be used as moulding materials and a simple determination of melt flow rate is used to confirm that such compositions can be injection moulded or extruded. The melt flow rate (πr.f.r.) is defined as the amount of material, in grams, which would be extruded, under tightly specified conditions of temperature and pressure, in a time of ten minutes. The apparatus used is essentially a dead-weight extrusion plasti eter, operating under conditions of low shear rate. The material is heated within a hardened steel barrel and maintained at an accurately defined and controlled temperature. From this it is extruded through a standard orifice or die by means of a piston loaded with a standard weight. The specified dead load is the total weight of the piston and the standard weight. In practice, the determination of the gravimetric m.f.r. is effected by cutting a number of specimens of the extrudate, extruded over identical time periods and weighing these. From the average weight of these specimens and the extrusion time of each, a simple calculation gives the m.f.r. in grams per ten minutes. Alternatively, the time taken for the piston to travel a given distance may be measured and from this the volume of material extruded in the same time, from which, combined with the melt density of the material at the test temperature, the gravimetric m.f.r. can be easily calculated. In practice this can be done by the following procedure: A sample weight of 3.5 g of the composition is charged to the barrel of a melt flow grader apparatus (Utility model, Daventest Ltd., England) provided with a die having a circular orifice of 2 mm diameter and 8 mm land length. The barrel is maintained at a temperature 10 C above the melting point of the polymer. After a 5 min warm-up period a convenient load is applied to the piston which has a weight of 0.16 kg. The melt flow time is calculated as the total time, including the 5 min warm-up period, taken for a total of 2 g of the composition to be extruded through the die. Tables III and IV provide a guide to the most appropriate test conditions to use when determining the melt flow rate for particular plastics in common use. TABLE III PLASTIC CONDIT IONS Acetal s 5,13 Acryl ics 8,9 Acryl oni tri 1 e-butad i ene-sty rene 7 Cel lulose esters 4,5,6 Nyl on 11,17,18,19 Polycarbonate 15 Polychlorotrif1uoroethylene 10 Polyethylene 1,2,4,5,6,14,21 Polypropylene 12 Polystyrene 7,8,9,16 Polyterephthalate 20 Vinyl acetal 3 TABLE IV CONDITIONS TEMP. °C LOAD jjr 1 125 325 2 125 2160 3 150 2160 4 190 325 5 190 2160 6 190 21600 7 200 5000 8 230 1200 9 230 3800 10 265 12500 11 275 325 12 230 2160 13 190 1050 14 190 10000 15 300 1200 16 190 5000 17 235 1000 18 235 2160 19 235 5000 20 250 2160 21 310 12500 Mouldings Those lipid-polymer proportions which conform to the rheological characteristics of a typical moulding material as determined by the foregoing tests will be finally shaped into moulds. To assess the quality of the resultant shaped articles, thermal, electrical and general mechanical properties such as, impact resistance, tensile strength, flexural modulus, low temperature brittleness, friction coefficient, film permeability, film tear resistance, film shrinkage, surface and volume resistivity, may be measured. The present invention also provides a process for producing a new plastics material as defined above comprising bringing into association a polymer and a lipid as plasticiser therefor. Plastics according to the invention may be produced by conventional techniques for blending solid or liquid materials including known solid state physical mixing techniques such as in a roller mill and by use of dispersions of the materials in a liquid phase such as a solvent which is subsequently evaporated. Such dispersions may be produced by conventional liquid phase mixing technique including use of high or low shear mixers. The present invention relates to plastics from all three classes, i.e. the thermoplastics, the elastomer plastics and the thermosetting plastics. Although the boundaries between these types are not clear, this division is generally accepted in the plastics art. Thermosplastics and elastomer plastics are readily plasticised, either before or after polymerisation has occurred, by mixing techniques as mentioned above. However it is generally impossible to plasticise thermosetting plastics by such methods because they cannot be dissolved, melted or worked even with heating due to the cross-linking which has occurred to form the three-dimensional structure characteristic of thermosetting plastics. It is normally necessary to include plasticiser either with the monomer or monomer mixture prior to polymerisation or, unless the polymerisation leads directly to a cross-linked thermosetting plastic structure, by admixture with linear or branched polymers prior to a cross-linking step. Addition of the lipid components into the plastic formulation at the early stages of the polymerization is only practicable if the lipid can stand the polymerization conditions and further technological operations in the plastic manufacture without decomposing, reacting or changing its natural structure. Another possibility for plasticising thermosetting plastics has been discovered for use with lipid plasticisers. This exploits the ability of polymeric materials to absorb small molecules such as lipids by hydrophobic and/or hydrophilic interactions by causing the plasticiser to permeate the three-dimensional structure of the polymer after its formation. This may advantageously be applied to elastomeric plastics as well. Accordingly the present invention further provides a process for modifying the physical properties of a thermosetting or elastomeric plastic body comprising bringing the plastic into contact with a lipid and permitting the lipid to penetrate into the plastic body, preferably until saturated absorption is achieved. Usually this process will be applied to a shaped article, often one in its final form ready for use. Conveniently the lipid may be used in the form of a solution in a suitable solvent which may be aqueous and/or organic. Solvent, lipid concentration, temperature and time requirements have to be determined to optimize the absorption conditions, but the natural tendency of polymeric materials to absorb lipids, will contribute to achieving the most convenient extent of lipid absorption. The invention further provides a shaped article formed from a plastic according to the present invention. Such articles may be formed in conventional manner, for instance by extrusion or by injection or other moulding techniques and/or by machining as necessary for the desired end shape and appropriate to the nature of the particular plastic material in question. Suitable articles formed of plastics of the present invention include sustained release or depot formulations, e.g. for surgical implantation or parenteral, nasal, oral, rectal or vaginal administration to human or animals whether for therapeutic or other purposes, and apparatus and devices for biomedical applications such as those mentioned in Table I above. The invention will now be illustrated by the following Examples. EXAMPLE 1 Polyvinyl formal, (Formvar 15/95E, MW. 24000-40000, BDH Chemical Ltd. England) supplied as a free flowing powder, has been tested for compatibility with soybean and egg yolk lecithins. In both cases different proportions of lipid and polymer, ranging from 0 to 30% of lipid, were mixed-ground manually and then heated (100°C) and compressed in a hydraulic press (5 tons) into a circular mould to form disks of 1 mm in section and 13 mm diameter. Polymer and lipid mixtures form perfect homogeneous melts up to a compositions of 30% of lipid. Increasing amounts of lipid lead to a material which has a more fragile and sticky composition. EXAMPLE 2 Poly-β-hydroxybutric acid, (MW. 1000000, by light scattering, Sigma USA) isolated from Alcaligenes species. This polymer has been mixed with different proportions of soybean and egg yolk lecithins and shaped into disks using the same procedure used in Example 1. Polymer and lipids were shown to form homogenous melts up to a proportion as high as 50% of lipid material. EXAMPLE 3 Polyvinyl acetate, (Aldrich, England, high molecular weight, T 30°C, d: 1.191) supplied as pellets. This polymer was tested for compatibility with soybean and egg yolk lecithins. Solutions of the polymers in ethyl acetate and the lipids in chloroform were brought together, in different proportions, to produce homogenous mixtures of polymer and lipids. After evaporation of the solvents a rubber-like material was obtained. Proportions ranging from 0 to 50% of lipid were tested with similar results. EXAMPLE 4 Polystyrene, (Aldrich, England, T 100°C, T m 237.5°C, d: 1.047) supplied as pellets. Both soybean and egg yolk lecithin were used as plasticisers for compatibility tests with this polymer. Samples containing different proportions of lipids and polymer were weighted and dissolved in chloroform to produce homogenous mixtures of both components. After evaporating the solvent, rather hard and rigid materials were obtained. Very high proportions (up to 60%) of lipids were admitted by the polymer as plasticisers. REFERENCES. 1 .- Hanahan, D.J. , De opoul os , C.A., Li ehr, J. and Pi nckard, R.N. , J. Bi ol . Chem. 255, 5514-5516 (1980). 2 .- Benevi ste, J., Henson, P.M. and Cochrane, C.G., J. Exp. Med. 136 , 1356-1377 (1972). 3.- Siraginian, R.P. and Osier, A.G., J. Immunol.106, 1244-1251 (1971). 4.- Turner, D.L., Arch. Bioche . Biophys.77, 249-257 (1958). 5.- Z aal, R.F.A., Biochim. Biophys. Acta 515, 163-205 (1978). 6.- ago, K., Japan Heart J.2, 354-367 (1961).. 7.- Hecht, E., J. Michigan State Med. Soc.56, 1445 (1957). 8.- Goto, M., Rinsho Shoni Igaku 9, 184-202 (1961). 9.- Jett, M. and Alving, C.R., Biochim, Biophys. Res. Commun.114, 863-871 (1983). 10.- Myher, J.J. and Kuksis, A., Biochim. Biophys. Acta 795, 85-90 (1984).

Claims: CLAIMS 1. A plastics material comprising a polymer an a lipid. 2. A plastics material according to claim 1 wherein the polymer is selected from cellophane, cellulose 5 acetate, polyolefins, fluorinated hydrocarbons, polyhydroxyethylmethacrylate, polymethylmethacrylate, poly(acrylamide) , poly(acrylic acid) , poly(acrylonitrile) , polyamide resin, poly(l-butene) , poly(1,4-butylene terephthalate) , poly(butyl ethacrylate) , 0 poly(tertbutylmethacrylate) , poly(4-tertbutyl styrene), * polycarbonate resin, poly(cyclohexylmethacrylate) , ^ poly(2,6-dimethyl-l,4-phenylene oxide), poly(ethylene) , poly(ethylene) chlorinated, poly(ethylene glycol), poly(ethylene oxide), poly(ethylene terephthalate), 5 poly(ethyl methacrylate), nylon, polyimide, poly(isobutyl methacrylate), poly(4-isopropyl styrene), poly(methyl methacrylate), poly(methyl styrene), pol (styrene) , polysulfone resin, poly(tetrafluoro ethylene), poly(vinyl acetate), poly(vinyl alcohol), poly(vinyl butyral), pol (vinyl chloride), pol (vinyl formal), acrylate elastomers, chlorosulfonated polyethylene, pure natural rubber, polyurethanes, silicone rubber, polyethylmethacrylate, polyamides, polyethyleneterephthalate, silk, polymonochloro-p-xylylene. epoxy resin, polyethylene, polypropylene, polyvinylalcohol , and polyvinylidenechloride, mixtures thereof and copolymers comprising repeating units of at least one such polymer. 3. A plastics material according to claim 1 or claim.2 wherein the polymer is an elastomer. 4. A plastics material according to claim 1 or claim 2 wherein the polymer is a thermosetting plastic. 5. A plastics material according to any one of claims 1 to 4 wherein the lipid is a phospholipid, sphingolipid or glycolipid, or cholesterol or a cholesterol ester. 6. A plastics material according to claim 5 wherein the lipid is a phosphatidylcholine, platelet activating factor, phospholipid antithromboplastin, cerebroside sulphate, bovine brain cephalin, or a soybean phosphatide or phosphatidylinositol lipid, phosphatidylserine, synthetic phosphatidic acid, phosphatidyl glycerol or a ζχ-lysophosphatidylcholine, o<-lysophosphatidylethanolamine, oHLysophosphatidylinositol, - -lysophosphatidylserine, o<-phosphatidic acid, &<-phbsphatidylcholine, < -phosphatidylethanolamine, -phosphatidylglycerol, Xrphosphatidylinositol, ^phosphatidylserine, l-0-alkyl-2- acteyl-sn-glycero-3-phosphorylcholine, ceramide, ganglioside, glucocerebroside, sphingomyelin, phytosphingosine, psychosine, sphingosine, sphingosylphosphorylcholine or sulfatide. 7. A plastics material according to any one of claims 1 to 6 comprising up to 30% by weight of the weight of the polymer of a lipid. 8. A plastics material according to any one of claims 1 to 7 comprising at least 0.01% by weight of the weight of the polymer of a lipid. 9. A plastics material according to any of claims 1 to 8 wherein the lipid is the sole plasticiser present in the plastics material. 10. A shaped article formed from a plastics material according to any one of claims 1 to 9. 11. A process for producing a plastics material according to any one of claims 1 to 9 comprising (a) bringing into association a polymer and a lipid plasticiser therefor, or (b) polymerising a monomer in the presence of a lipid plasticiser and where necessary to form a thermosetting plastic, cross-linking the plasticised polymer formed in step (a) or step (b) . 12. A process for modifying the physical properties of a thermosetting or elastomeric plastic material comprising bringing the plastic into contact with a lipid plasticiser therefor and permitting the lipid to penetrate into the plastic material. 13. A plastics material according to any one of claims 1 to 9 or an article according to claim 10 for use in a method of treatment of the human or animal body by surgery or therapy or in a diagnostic method practised on the human or animal body. 14. Use in the production of an article or medicament for use in the treatment of the human or animal body by surgery or therapy or in a diagnostic method practised on the human or animal body, of a plastics material according to any one of claims 1 to 9 or an article according to claim 10. 15. A method for treating the human or animal body comprising implanting a plastics material according to claim 1 or an article formed of said plastics material in said human or animal body..

Inventors: VALENCIA GREGORIO PARERA, VALENCIA, GREGORIO, PARERA
Applicants: BIOCOMPATIBLES LTD
Application year: 1986
Main classification: C08K5
IPC codes: A61K9, A61K47, A61L27, A61L29, A61L31, A61L33, C08K5, C08L101