PROCESS FOR PREPARING HALOGENATED BENZENE DERIVATIVES

Abstract: Halogenated benzene derivatives are prepared at a high selectivity to the p-halogenated isomer by halogenating ben­ zene or benzene derivative in the presenze of a zeolite contain­ ing catalyst which contains an aluminum compound other than the zeolite component in the catalyst in an amount of 0.01 to 40% by weight as Al₂O₃ based on the weight of the catalyst.

Description: PROCESS FOR PREPARING HALOGENATED BENZENE DERIVATIVES The present nvention relates to a process for preparing 2 halogenated benzene derivative by halogenating benzene and/or a benzene derivative in the presence of a zeolite as a catalyst. More particularly, it relates to a process for preparing a p-substituted halogenated benzene derivative by halogenating benzene and/or a benzene derivative by using a zeolite-containing catalyst formed by incorporating a binder with a zeolite. Halogenated benzenes are industrially important compounds, and especially dichlorobenzene (hereinafter referred to as "DCB") is used as a starting compound for the production of valuable compounds such as pigments. DCB includes three isomers, that is, ortho-, meta- and para-isomers, and p-dichlorobenzene (hereinafter referred to as "PDCB") is used not only as the starting compound for the production of various compounds but also directly as an insecticide or deodorizer. Ordinarily, DCB is prepared according to the liquid-phase chlorination process in which benzene or monochlorobenzene (hereinafter referred to as "MCB") is chlorinated in the presence of a Lewis acid, such as ferric chloride, by introducing chlorine into the reaction mixture. It is known that since the chlorination reaction, a MB shows a strong orientation, in the liquid-phase chlorination process using a Lewis acid, o-dichlorobenzene (hereinafter referred to as "ODCB") and PDCB are selectively formed. In this reaction, ODCB is formed at a ratio of 30 to 40% and PDCB is formed at a ratio of 60 to 70%. However, since the demand for PDCB is larger than that for ODCB, it is desired to develop a process in which PDCB is selectively prepared while controlling the formation of ODCB. As the process for halogenating an aromatic compound in the presence of a zeolite catalyst, there can be mentioned, for example, a liquid-phase halogenation process in which a halogenated benzene is brominated in the liquid phase, and a process for selectively preparing a para-isomer by using various ion-exchanged faujasites, that is, X type and Y type zeolites, as the catalyst [see Journal of Catalysis, 60, pages 110-120 (published in 1979)] As the gas-phase halogenation process, there is known a process for chlorinating benzene in the gas phase by using a zeolite such as ZSM-5, mordenite, L type zeolite or Y type zeolite as a catalyst (Tetrahedron Letters, 21, pages 3809-3812, 1980). As pointed out above, it has been clarified that zeolites show an effective catalytic activity for halogenation of aromatic compounds. Ordinarily, zeolites are prepared in the form of a crystalline fine powder. Accordingly, if such a crystalline fine zeolite is directly used as a practical catalyst or industrial catalyst, pressure loss is caused or the difficult operation of separating the catalyst becomes necessary to prevent incorporation of the catalyst into a product. Accordingly, where the catalyst component is in the powdery form, the catalyst component is molded into an appropriate shape or size, for example, into a spherical or columnar pellet or a granule according to the reaction state (liquid phase or gas phase), the manner of use of the catalyst (fixed bed, suspended bed or fluidized bed), the reaction manner (batchwise reaction or continuous reaction) and the shape of the reaction vessel. On the other hand, the performance, stability, and durability, i.e., the life, of the catalyst under application conditions are very important. Especially, in a molded catalyst, mechanical strength characteristics such as a high degree of hardness, high powdering resistance, and high abrasion resistance are required, and a good moldability including a high molding efficiency is required for molding the catalyst. Ordinarily, a binder is used for satisfyTha- these reruireme - s . Since a zeolite powder is non-caking, a synthetic inorganic oxIde such as silica or alumina or a clay such as natural montmorillonite, purified montmorillonite, kaolin or acid clay is often used for molding the zeolite powder. Especially in view of the mechanical strength characteristics of a molded catalyst and the moldability, an alumina type oxide is frequently used. Furthermore, most of the clays used contain an aluminum compound such as aluminum oxide. As seen from the foregoing description, it is eagerly desired in the art to develop a zeolite catalyst excellent as an industrial catalyst and to prepare PDCB selectively while controlling the formation of ODCB. The present inventors carried out research into practical zeolite catalysts for the halogenation of aromatic compounds, and as a result, found that if an aluminum compound other than the aluminum constituent of the zeolite is present in a molded zeolite catalyst in an amount exceeding a certain level, the selectivity to a para-substituted compound is drastically reduced. Since a zeolite is ordinarily prepared from silicon and aluminum compounds as the main starting materials, it is pcssible that the unreacted aluminum compound is often left S an impurity in the formed zeolite. Accordingly, the aluminum compound may be present in the molded catalyst irrespective of the kind of binder used and this aluminum compound reduces the catalytic performance. Surprisingly, it was found that the selectivity to PDCB remains high when the halogenation of benzene and/or a benzene derivative is effected by using a zeolite-containing catalyst containing a specified amount of an aluminum compound other than the zeolite component in the catalyst. In accordance with the present invention, there is provided a process for the preparation of halogenated benzene derivatives, which comprIses halogenating benzene cr a benzene derivative in the presence of a zeolite catalyst. The zeolite catalyst is characterized as being a zeolite-containing catalyst which contains an aluminum compound other than the zeolite component in the catalyst in an amount of 0.01 to 40% by weight as A1203. The main component of the zeolite-containing catalyst used in the present invention is a zeolite. As the zeolite, there can be mentioned faujasite type zeolites such as X type and Y type zeolites, offretiteerionite type zeolites, L type zeolite, mordenite, ferrierite and ZSM-5 type zeolites. Of these, L type zeolite and offretite-erionite type zeolites are preferable. The L type zeolite has a powder X-ray diffraction pattern (Ka doublet of copper) shown in Table 1, by which the L type zeolite is distinguishable from other zeolites. Table 1 Diffraction angle 28 ( ) Lattice spacing d ( ) (+0.2 ) (+0.1 ) Relative intensity I/Ic 5.6 1^.8 100 11.2 7.89 5 - 40 11.8 7.49 10 - 100 14.8 5.98 10 - 100 15.3 5.79 10 - 40 19.4 4.57 30 - 80 20.2 4.39 10 - 70 20.5 4.33 10 - 70 22.7 3.91 30 - 120 23.4 3.80 5 - 40 24.3 3.66 10 - 70 25.6 3.48 20 - 80 27.2 3.28 10 - 60 28.0 3.18 30 - 120 29.1 3.07 20 - 80 29.8 3.00 5 - 40 30.8 2.91 20 - 80 33.8 2.65 10 - 70 34.2 2.62 5 - 50 The L type zeolite is a known zeolite and can be synthesized according to a known process. A typical composition of the L type zeolite is expressed by the following oxide molar ratio formula: xM2/nO.Al2O3.ySiO2.zH2O wherein M is a cation, r; is a valency of the cation M, x is a number of 0.7 to 1.3, y is a number of 4 to 8, and z is a number varying depending upon the extent of hydration of the zeolite and is ordinarily from 0 to 9. A typical example of the L type zeolite has a composition expressed by the following oxide molar ratio formula: M2OAl2O3 6SiO25H2O wherein M is sodium and/or potassium. The as-prepared L type zeolite can be used as the catalyst, but all or a part of the metal cation (M) contained in the as-prepared L type zeolite may be ion-exchanged with another metal cation and/or proton before it is used as the catalyst. The ion exchange treatment may be accomplished, for example, by suspending the zeolite in an aqueous solution containing the intended metal cation and stirring the suspension at 200C to 1000C for 1 to 50 hours. As the offretite-erionite type zeolite, there can be mentioned offretite, tetramethylammonium-offretite (hereinafter referred to as "TMA-offretite"), erionite, and zeolites in which both offretite and erionite structures are present, such as a novel zeolite called "zeolite OE" (EP-0106643), zeolite T, and ZSM-34 zeolite. The zeolite of this type has a characteristic powder X-ray diffraction pattern, by which the zeolite is distinguishable from other zeolites. The X-ray diffraction pattern by the Ra doublet of copper of the offretite-erionite type zeolite is shown in Table 2. Although some of zeolites of this type are naturally produced, zeolites of this type can be synthesized and such synthesis processes are known. Table 2 Diffraction angle 29 (0) Lattice spacing d (A) (+0.2 ) (+0.1 ) Relative intensity I/Io 7.7 11.5 100 9.6 9.2 0 - 10 11.7 7.6 10 - 40 13.4 6.6 40 - 90 14.1 6.3 10 - 40 15.4 5.7 10 - 40 16.6 5.3 0 - 10 19.4 4.6 10 - 60 20.5 4.3 40 - 80 21.3 4.2 0 - 10 23.3 3.8 20 - 70 23.7 3.8 100 - 160 24.8 3.6 50 - 120 26.1 3.4 5 - 30 26.9 3.3 10 - 40 27.6 3.2 0 - 10 28.1 3.2 10 - 40 28.3 3.2 20 - 50 30.5 2. 5 - 20 31.2 2.9 50 - 120 31.4 2.8 50 - 130 31.9 2.8 0 - 10 33.4 2.7 10 - 30 35.9 2.5 0 - 30 36.2 2.5 5 - 30 The offretite-erionite type zeolite has a composition represented by the following oxide molar ratio formula: : xM2/nO.Al2O3.ySiO2.zH2O wherein M is a cation, n is a valency of the cation M, x is a n=-.=er of 0.7 to 1.3, y is a nmber of 5 to 10, and z is a number varying depending upon the extent of hydration of the zeolite and is ordinarily from 0 to 10. A synthetic zeolite having a low impurity content and a high crystallinity is preferred as the offretiteerionite type zeolite used as the catalyst. The as-synthesized offretite-erionite type zeolite ordinarily contains a metal cation M such as a sodium ion or a potassium ion, but it is known that this metal cation can be easily exchanged with another metal cation by an ion exchange treatment. It is preferred that the exchangeable cation of the offretite-erionite type zeolite used in the present invention be exchanged with a metal cation selected from potassium, rubidium, cesium, calcium, strontium, and barium. It is sufficient if one of the foregoing metal cations is present in the zeolite, but two or more of these metal cations may be simultaneously present in the zeolite. It is preferred that the ion exchange ratio of the metal cation, that is, the ratio of exchange of the exchangeable cation with the metal cation, be at least 70%, more preferably at least 90%. If at least two metal cations are present in the zeolite, it is preferred that the sum of the ion exchange ratios be at least 70%, more preferably at least 90%. If the ion exchange ratio is lower than 70%, a satisfactory selectivity to the para-substituted compound cannot be obtained. The metal cation can be easily introduced into the zeolite by a known ion exchange treatment. If the synthesized offretiteerionite type zeolite is one having an organic cation such as TMA, to increase the ion exchange ratio with the metal cation, it is preferred that the organic cation be removed in advance. This removal can be accomplished by performing a preliminary calcining treatment in an air current at a temperature o from 4000C to 7000 for 1 to 10 hours. The X-type zeolite has a composition represented by the following oxide ..cl¯- ratio formula: xM2/nO.Al2O3.ySiO2.zH2 wherein M is a cation, n is a valencyo of the cation M, x is a number of 0.7 to 1.3, y is a number of 2 to 3, and z is a number varying depending upon the extent of hydration of the zeolite and is ordinarily from 0 to 11. The Y-type zeolite has a composition represented by the following oxide molar ratio formula: xM2/nO.Al2O3.ySiO2.zH2O wherein M is a cation, n is a valency of the cation M, x is a number of 0.7 to 1.3, y is a number of 3 to 6, and z is a number varying depending upon the extent of hydration of the zeolite and is ordinarily from 0 to 20. Mordenite has a composition represented by the following oxide molar ratio formula: xM2/nO.Al2O3.ySiO2.zH2O wherein M is a cation, n is a valency of the cation M, x is a number of 0.7 to 1.3, y is a number of 10 to 20, and z is a number varying depending upon the extent of hydration of the zeolite and is ordinarily from 0 to 11. Ferrierite has a composition represented by the following oxide molar ratio formula: xM2/nO.Al2O3.ySiO2.zH2O wherein M is a cation, n is a valency of the cation M, x is a number of 0.7 to 1.3, y is a number of 10 to 100, and z is a number varying depending upon the extent of hydration of the zeolite and is ordinarily from 0 to 10. The ZSM-5 zeolite has a composition represented by the following oxide molar ratio formula: xM2/nO.Al2O3.ySiO2.zH2O wherein M is a cation, n is a valency of the cation M, x is a number of 0.7 to 1.3, y is a number of 10 to 1000, and z is a number varying depending upon the extent of hydration of the zeolite and is ordinarily fom G to 40. It is preferable that the zeolite used as the catalyst has a high purity. If the above-mentioned method is adopted, a zeolite having a hg: pu'-' ordinarily obtained. The purity of the zeolite can be known from the peak intensity of the powder X-ray diffraction pattern. The zeolite is ordinarily used in a molded form as a catalyst in the process of the present invention. The shape and dimension of the molded catalyst are appropriately determined according to the mode of the reaction, and ordinary molding methods such as extrusion molding, compression molding, and spray-drying granulation can be appropriately adopted. Since the zeolite is a non-caking powder, as pointed out above, a binder is used for molding. Binders customarily used in this field, for example, synthetic inorganic oxides such as alumina and silica-alumina, and natural and refined clays such as kaolin, acid clay, montmorillonite, and sepiolite, may be used in the present invention. The kind of the binder is not particularly critical. In view of the mechanical strength and reaction activity of the molded catalyst, the binder is used in an amount of 1 to 90% by weight, preferably 10 to 70% by weight, based on the molded catalyst. In the process of the present invention, the content of an aluminum compound in the zeolite-containing catalyst, other than the alumina component constituting the zeolite, is 0.01 to 40% by weight, preferably 0.01 to 30% by weight, expressed as Al203. If the amount of the Al 203 other than the zeolite is too large and exceeds the range specified in the present invention, the selectivity to a para-substituted compound in the halogenation reaction is drastically reduced. Even if an aluminum compcund-free binder, such as silica, magnesia, titania or silica-magnesia, is used as the binder for the formation of the catalyst, an aluminum compound is sometimes included in the molded catalyst according to the conditions used for the preparation of the zeolite. Accordingly, in this case aiso, the above requirement of the aluminum compound content should be satisfied. The catalyst used in the present invention may be prepared according to known molding methods, and the molding method is not particularly critical. It Is generally preferred that the as-molded catalyst be dried and calcined at a temperature of from 300 CC to 7000C before it is used for the reaction. In the present invention, the term "benzene deriva tive means a compound in which hydrogen of benzene is substituted with a substituent such as a halogen atom or an alkyl group, for example, halogenobenzene or alkylbenzene. As specific examples, there can be mentioned monofluorobenzene, MCB, monobromobenzene (hereinafter referred to as "MBB"), monoiodobenzene, toluene, and ethylbenzene. An elementary halogen may be used as the halogenating agent. For example, chlorine, bromine, and iodine can be mentioned. The halogenation reaction of benzene and/or a benzene derivative according to the present invention may be carried out either in the liquid phase or in the gas phase. When the process of the present invention is carried out in the liquid phase, the reaction apparatus or reaction condition is not particularly critical, in so far as benzene and/or a benzene derivative is placed n contact in the liquid state with the catalyst. For example, either a batchwise reaction vessel or a continuous reaction vessel may be used. The reaction may be carried out in the presence of a sclvent not participating in the halogenation reaction, such as carbon tetrachloride. If a solvent is used, it is preferred that the concentration of benzene and/or a benzene derivative be 5 to 100%, especially 10 to 100%. If the concentration is lower than 5%, the chance of contact of the starting compound with the catalyst is undesirably reduced. Where a halogenating agent is continuously supplied, an inert gas such as nitrogen, helium or carbon dioxide may be fed together with the halogenating agent. It is preferred that the concentration of the halogenating agent be 5 to 1009, more preferably 10 to 100%. When a batchwise or semi-batchwise reaction vessel is used, usually the catalyst is used in the state wherein it is suspended in the solution, and it is preferred that the amount of the catalyst per unit of liquid volume be 0.001 to 1 kg/l, more preferably 0.005 to 0.1 kg/l. If the amount of the catalyst is smaller than 0.001 kg/l, the load on the catalyst is too large and a satisfactory activity cannot be obtained. When the halogenating agent is continuously supplied, it is preferred that the feed rate of the halogenating agent (the feed rate per unit of liquid volume) be 1 to 1000 Q/hr*Q, more preferably 5 to 500 Q/hr Q. If the feed rate is lower than I t/hr Q, a sufficient rate of reaction cannot be obtained. If the feed rate is higher than 1000 t/hr.t, a diffusion rate-controlled state is brought about and a substantial increase of the effect cannot be attained by an increase of the feed rate. The reaction temperature or reaction pressure is not particularly critical, in so far as the benzene and/or a benzene derivative is in the liquid phase. When the reaction temperature is higher than the boiling point of benzene and/or a benzene derivative, the halogenation reaction may be conducted in the liquid phase by elevating the pressure. It is preferred that the reaction temperature be from OOC to 4000C, especially from 200C to 3000C. If the reaction temperature is lower than OOC, a sufficient rate of reaction cannot be obtained. At a temperature higher than 4000C, the selectivity to a para-substituted halogenated benzene derivative is reduced. Where the process of the present invention is carried out in the gas phase, the reaction vessel is not particularly critical and an ordinary fixed bed can be used. Note, the process of the present invention still may be carried out even if a fluidized bed or moving bed is used. In carrying out the gas phase reaction, the molar ratio of the halogenating agent to the benzene derivative is 0.01 to 5.0 mole/mole, preferably 0.1 to 2.0 mole/mole. If the molar ratio of the halogenating agent to the benzene derivative is lower than 0.01 mole/mole, the yield of a para-substituted halogenated benzene derivative is undesirably low. If this molar ratio is higher than 5.0 mole/mole, the amount of a polyhalogenated benzene formed as a by-product is increased. The gas phase reaction may be performed by using only benzene and/or a benzene derivative and the halogenating agent, or a diluent gas may be incorporated. Any of diluent gases inactive to the reaction of the present invention may be used. For example, nitrogen, helium, and hydrogen can be mentioned. The concentration of the starting compound is 1 to 100%, preferably 1 to 50%. The starting material mixture may be supplied so that the contact time W/F [g-cat.hr/mole; W is the weight (g) of the catalyst and F is the total feed rate (mole/hr) of benzene and/or a benzene derivative and the halogenating agent is 5 to 500 g-cathr/mole, preferably 10 to 100 g-cat.hr/mole. If the contact time is smaller than 5 g-cat.hr/mole, a satisfactory conversion of the benzene derivative cannot be obtained. If the contact time exceeds 500 g-cat.hr/mole, the amount of a polyhalogenated benzene formed as a by-product is increased The reaction temperature should be 100"C to 400 CC, preferably 1500C to 3000C. If the reaction temperature is lower than 1000C, a sufficient conversion cannot be obtained. At a temperature higher than 4000C, the selectivity to a para-substituted halogenated benzene is reduced. The reaction pressure is not particularly critical, anQ any pressure condition may be adopted, in so far as the reaction is advanced in the gas phase. The present invention will now be described in detail with reference to the following examples that by no means limit the scope of the invention. In the examples, the conversion and selectivity are values calculated according to the following equations. A-B Conversion (%)= x100 A A: amount (millimoles) of charged or supplied benzene derivative B: amount (millimoles) of unreacted benzene derivative C Selectivity = D x 100 C: amount (millimoles) of intended product formed D: sum (millimoles) of all products formed Example 1 To an overflow type reaction vessel equipped with a stirrer, a sulfuric acid-acidified aqueous solution of aluminum sulfate (A1203 = 4.44 w/v%, H2SO4 = 25.69 w/v%) and an aqueous solution of sodium silicate (Na2O = 6.56 w/v%, SiO2 = 20 w/v%, A1203 = 0.22 w/v%) were simultaneously and continuously supplied at feed rates of 0.25 I/hr and 0.75 l/hr, respectively. Reaction was carried out with stirring. The residence time of the reaction slurry was adjusted to 30 minutes and the reaction was conducted at a pH value of 6.2 and a temperature of 320C. The slurry product overflowing from the reaction vessel was subjected to solid-liquid separation, and the recovered solid was washed with water to obtain an amorphous compound of the following composition. Na2O: 5.2 by weight (dry base} A1203: 7.138 by weight (dry base) SiO2: 87.7% by weight (dry base) H2O 59.7% by weight (wet base) To 176 g of an aqueous solution of potassium hydroxide having a concentration cf 16.4w 3 weight was a 1t2.2 g of the above amorphous compound. The mixture was stirred to form a slurry reaction mixture. This reaction mixture was charged in an autoclave and maintained at 170 C under an autogenerous pressure for 24 hours to effect crystallization. After completion of the reaction, the formed solid was separated, washed with water and dried at 110 C. From the results of chemical analysis, it was found that the product had the following composition expressed by the molar ratio of oxides (dry base): 0.99K2O.0.01Na2O.Al2O3.6.0SiO2 The powder X-ray diffraction pattern of the sample, shown in Table 3, was substantially in accord with the pattern shown in Table 1, and it was confirmed that the product was an L type zeolite. Note, the powder X-ray diffraction pattern was determined by using Ka doublet of copper. Table 3 Diffraction angle ( ) Lattice spacing d ( ) (+0.2 ) (+0.1 ) Relative intensity I/Io 5.6 15.8 100 11.2 7.89 5 11.8 7.49 30 14.8 5.98 36 15.3 5.79 19 19.4 4.57 60 20.2 4.39 19 20.5 4.33 19 22.7 3.91 69 23.4 3.80 9 24.3 3.66 41 25.6 3.48 57 27.2 3.28 32 28.0 3.18 72 29.1 3.07 53 29.8 3.00 9 30.8 2.91 61 33.8 2.65 29 34.2 2.62 20 To confirm the effect of the present invention, Georgia kaolin was incorporated with the above-obtained L type zeolite to prepare a zeolite-containing catalyst. Namely, 10 g of Georgia kaolin having an SiO2 content of 48.8* by weigh and an A1203 content of 38.1% by weight was incorporated with 10 g of the L type zeolite, and 200 g of water was further added. The mixture was sufficiently since --bJected to evaporatIon to dryness, pulverized, and calcined in an air current at 5400C or 3 hours. Chlorination reaction of MCB was carried out by using the thus-prepared catalyst. The reaction was carried out by using an ordinary semi-batchwise reaction vessel made of Pyrex glass and having an inner diameter of 50 mm. In 40 g of MCB was suspended 2 g of the L type zeolite-containing catalyst. Chlorine gas (together with the same amount of nitrogen) was introduced into the vessel at a rate of 26.9 cc/min under agitation by a magnetic stirrer. The reaction temperature was adjusted to 1000C by controlling the temperature of the periphery of the reaction vessel in an oil bath. The composition of the product obtained at the point when 3 hours had passed from the start of introduction of the chlorine gas was analyzed by gas chromatography. The results obtained are shown in Table 4. Examples 2 through 5 In the same manner as described in Example 1, catalysts were prepared by incorporating Kibushi Kaolin (having an SO? content of 44. 8 by weight and an Al2O3 content of 32.7% by weight), acid clay (supplied by Mizusawa Kagaku and having an SiO2 content of 73.8% by weight and an Al2O3 content of 13.2% by weight), silica-alumina (suppled by Shokubai Kasei and having an SiOz content of 71.3% by weight and an A1203 content of 28.6% by weight), , and sepiolite (supplied by Showa Kogyo and having an SiO2 content of 56.5% by weight and an A1203 content of 2.0% by weight) with the L type zeolite synthesized in Example 1. By using these catalysts, chlorination of MCB was carried out in the same manner as described in Example 1. The results obtained are shown in Table 4. Example 6 A catalyst was prepares in the same manner as described in Example 1 except that 20 g of Georgia kaolin was incorporated with the L type zeolite synthesized in Example 1. By using this catalyst, chlorination reaction of MCB was carried out in the same manner as described in Example 1. The results obtained are shown in Table 4. Example 7 A catalyst was prepared in the same manner as described in Example 1 except that 5 g of alumina (supplied by Sumitomo Chem. Co.) was incorporated, instead of 10 g of Georgia Kaolin, with the L type zeolite synthesized in Example 1. By using this catalyst, chlorination of MCB was carried out in the same manner as described in Example 1. The results obtained are shown in Table 4. Example 8 A catalyst was prepared in the same manner as described in Example 1 except that 1 g of sepiolite used in Example 5 was incorporated, instead of 10 g of Georgia kaolin, with the L type zeolite synthesized in Example 1. By using this catalyst, chlorination of MCB was carried out in the same manner as described in Example 1. The results obtained are shown in Table 4. Comparative Example 1 With 10 g of the L type zeolite synthesized in Example 1 was incorporated 10 g of alumina (supplied by Sumitomo Chem. Co.), and 200 g of water was further added. The mixture was sufficiently stirred, subjected to evaporation to dryness, pulverized, and calcined in an air current at 5400C for 3 hours. By using the thus-prepared catalyst, chlorination of MCB was carried out in the same manner as described in Example 1. The results obtained are shown in Table 4. Comparative Example 2 A catalyst was prepared in the same manner as described in Comparative Example 1 b incorporating 10 g of alumina (supplied by MIzusawa Kagaku) with the L type zeolite synthesized in Example 1. By using the thusprepared catalyst, chlorination of MCB was carried out the same manner as described in Comparative Example 1. The results obtained are shown in Table 4. Table 4 Content of aluminum Selectivities (mole%) to other than zeolite respective products component (% by weight Conversion (%) Binder as Al2O3) of MCB PDCB ODCB MDCB1) Others2) Example 1 Georgia kaolin 19.1 57.1 88.2 10.9 0.9 0.1 Example 2 Kibushi kaolin 16.4 52.5 88.5 10.6 0.8 0.1 Example 3 Acid clay 6.6 52.9 87.9 10.9 1.0 0.2 Example 4 Silica-alumina 14.3 53.6 87.0 12.1 0.8 0.1 Example 5 Sepiolite 1.0 51.1 87.6 11.5 0.8 0.1 Example 6 Georgia kaolin 25.4 50.3 88.3 10.6 0.8 0.2 Example 7 Alumina 31.8 52.8 82.0 16.6 1.1 0.3 Example 8 Sepiolite 0.18 53.1 87.6 11.4 0.9 0.1 Comparative Alumina 47.8 51.8 73.0 25.0 1.5 0.5 Example 1 Comparative Alumina 49.0 52.8 72.5 25.4 1.6 0.5 Example 2 Note 1) MDCB: metadichlorobenzene 2) Others; trichlorobenzenes Example 9 In 970 ml of 2N aqueous ammonia was suspended 30 g of the L type zeolite svnthesized in Example 1, anc an ion exchange treatment was carried out at 90 C for 5 hours with stirring. The zeolite was recovered by filtration, washed with water, and then dried at 120 C for 16 hours. Th product had the following molar oxide composition (= base): 0.24K2O.Al2O3.5.99SiO2 Namely, there was obtained an L type zeolite in which about 76% of exchange sites were occupied by proton. With 10 g of this L type zeolite was incorporated 10 g of Georgia kaolin. Chlorination of MCB was carried out in the same manner as described in Example 1. The conversion of MCB was 54.6% and the selectivity to PDCB was 82.9%. Example 10 Chlorination of MBB was carried out by using the catalyst prepared in Example 1, according to the same procedures as described in Example 1, except that MBB was used instead of MCB. The conversion of MBB was 64.9%, and the obtained bromochlorobenzene comprised 84.9% of the para-isomer, 13.2% of the ortho-isomer, and 1.9% of the meta-isomer. Example 11 By using the catalyst prepared in Example 1, chlorination of toluene was carried out in the same manner as described i example 1 except that 30 g of toluene was used instead of 40 g of MCB. The results obtained after the lapse of 3 hours from the start of the reaction are shown in Table 5. Comparative Example 3 By using the catalyst prepared in Comparative Example 3, chlorination of toluene was carried out in the same manner as described in Example 10. The results obtained are shown in Table 5. Table 5 Content of aluminum Selectivities (mole%) to other than zeolite respective products component (% by weight Conversion (%) Binder as Al2O3) of toluene PCT OCT MCT Others Example 10 Georgia kaolin 19.1 52.3 59.7 34.6 2.1 3.6 Comparative Alumina 47.8 55.4 44.7 46.2 3.6 5.5 Example 3 Note PCT: parachlorotoluene OCT: orthochlorotoluene MCT: metachlorotoluene Others: dichlorotoluenes Example 12 According to the teaching of EP-A 106643, zeolite we, which Is an offretite-erionite type zeolite, was synthesized. More specifically, 23.6 g of solid sodium hydroxide (NaOH=93% by weight), 26.8 g of solid potassium hydroxide (KOH=85% by weight), and 51.4 g of an aqueous solution of sodium aluminate (Na2O=19.2% ry weight, AlO3 = 20.6c% by weight) were added to 701.2 g a cre water to form a homogeneous solution. Then, 142.2 g of amorphous solid silica (white carbon supplied by Nippon Silica Kogyo) was added to the solution with stirring to obtain a reaction mixture having the following molar oxide composition: 3.9Na2O.1.83K2O.Al2O3.18.8SiO2.382H2O This mixture was characterized by the following molar ratios: SiO2/Al2O3=18.8 OH/SiO2 = 0.61 K/(K + Na) = 0.32 H2O/SiO2 = 20.3 The mixture was charged in an autoclave and then heated at 1500C for 40 hours with stirring at 250 rpm. The obtained slurry was subjected to solid-liquid separation, and the recovered solid was sufficiently washed with water and dried at 150 C for 5 hours to obtain a powder having the following composition (dry base): 0.21Na2O.0.76K2O.Al2O3.7.4SiO2 The powder X-ray diffraction pattern of the sample, which is shown n Table 6, was substantially in accord wit the pattern shown in Table 2, and it was confirmed tat the product was an offretite-erionite type zeolite, that is, zeolite OE. This zeolite OE was ion-exchanged with K. Namely, 35 g of this zeolite OE was added to 250 g of an aqueous solution of potassium chloride (1 mole/Q), and the ion exchange treatment was carried out at 900C for 5 hours The slurry was then filtered, and the recovered solid was sufficiently washed with water and dried at 120 C for 16 hours. The powder X-ray diffraction pattern of this K-ion-exchanged zeolite OE was not substantially different from that shown in Table 6, and the zeolite had the following composition (dry base): 0.01Na2O.0.98K2O.Al2O3.7.1SiO2 Table 6 Diffraction angle 20 ( ) Lattice spacing d ( ) (+0.2 ) (+0.1 ) Relative intensity I/Io 7.7 11.5 100 9.5 9.3 8 11.6 7.6 27 13.2 6.7 85 13.9 6.4 17 15.2 5.8 13 16.4 5.4 7 19.3 4.6 15 20.3 4.4 73 21.2 4.2 9 23.1 3.8 33 23.5 3.8 140 24.7 3.6 87 26.0 3.4 7 26.8 3.3 33 28.0 3.2 26 28.2 3.2 57 30.4 2.9 14 31.1 2.9 83 31.3 2.9 117 33.2 2.7 27 36.0 2.5 28 With 10 g of the K-ion-exchanged zeolite OE was incorporated 10 g of Georgia kaolin as the binder, and 200 g of water was further added. The mixture was sufficiently stirred, subjected to evaporation to dryness, pulverized, and compression-molded to 5 mm (diameter) x 5 mm (length). The molded catalyst was calcined in an air current at 540 C for 3 hours. Chlorination of MCB was carried out as follows. An ordinary fixed bed type reaction apparatus was used. 5 g of the catalyst was packed In a Pyrex reaction tube having a diameter of 20 mm and a length of 500 mm. A starting material mixture comprising MCB, C12 , and N2 at a ratio of 18/9/73 was supplied at a contact time of 23 g-cathr/mole, and the reaction was conducted at 200 C. After the reaction became stationary, the product was sampled and analyzed by gas chromatography. The results obtained are shown in Table 7. Examples 13 and 14 In the same manner as described in Example 12, catalysts were prepared by incorporating acid clay (supplied by Mizusawa Kagaku) or silica-alumina (supplied by Shokubai Kasei) to the zeolite OE synthesized in Example 12. A reaction tube was packed with 5 g of the catalyst, and chlorination of MCB was carried out under the same conditions as described in Example 12. The results obtained are shown in Table 7. Comparative Example 4 A catalyst was prepared in the same manner as described in Example 12 by incorporating alumina (sup- plied by Sumitomo Chem. Co.) to the zeolite OE synthe- sized in Example 12. A reaction tbe was packed with 5 g of this catalyst, and chlorination of MC3 was carried out under the same conditins as described in Example 11. The results obtained are shown in Table 7. Table 7 Content of aluminum Selectivities (mole%) to other than zeolite respective products component (% by weight Conversion (%) Binder as Al2O3) of MCB PDCB ODCB MDCB Others Example 12 Georgia kaolin 19.1 56.3 88.9 9.0 1.2 0.9 Example 13 Acid clay 6.6 56.7 86.8 10.6 1.2 1.4 Example 14 Silica-alumina 14.3 50.3 82.2 14.4 1.6 1.8 Comparative Alumina 47.8 45.0 67.1 26.0 2.2 4.7 Example 4

Claims: CLAIMS 1. A process for the preparation of halogenated benzene derivatives, which ccwprLses halogenating benzene or a benzene derivative in the presence of a zeolite catalyst characterised in that the Catalyst contains an aluminum compound other than the zeolite component in the catalyst in an amount of 0.01 te 40% by weight as A1203 based on the weight of the catalyst. 2. A process according to claim 1, wherein said zeolite catalyst comprises an L type zeolite having a composition represented by the following oxide molar ratio formula: xM2/nO A1203 ySiO2 Z 2 wherein M is a cation, n is a valency of the cation M, x is a number of 0.7 to 1.3, y is a number of 4 to 8, and z is a number varying depending upon the extent of the hydration of the zeolite. 3. A process according to claim 1, wherein said zeolite catalyst comprises an offretite-erionite type zeolite having a composition represented by the following oxide molar ratio formula: xM2/nO.Al2O3.ySiO2.zH2O wherein M is a cation, n is a valency of the cation M, x is a number of 0.7 to 1.3, y is a number of 5 to 10, and z is a number varying depending upon the extent of the hydration of the zeolite. 4. A process according to claim 3, wherein at least 70% of the cation M is at least one metal ion selected from the group consisting cf potassium, rubi - ium, cesium, calcium, strontIum, and barium 5. A process according to any on of the preceding claims, wherein said zeolite catalyst is a molded product of a mixture of zeolite powder and 1 to 90% by weight of a binder selected from the group consisting of synthetic inorganic oxides and natural or refined clays 6. A process according to claim 5, wherein said molded product is calcined at a temperature of 300 CC to 7000C. 7. A process according to any one ofthe preceding claims,wherein the amount of the aluminum compound other than the zeolite component in the catalyst is 0.01 to 30% by weight as Awl 203 based on the weight of the catalyst. 8. A process according to any one of the preceding claims, wherein the benzene derivative is selected from the group consisting of monochlorobenzene, monofluorobenzene, monobromobenzene, monoiodobenzene, toluene, and ethylbenzene. 9. A process according to any one of the preceding claims, wherein said halogenation of the benzene or benzene derivative is carried out in the liquid phase at a temperature of OOC to 4000C by using an elementary halogen as a halogenating agent. 10. A process according to any one of claims 1 to 8, wherein said halogenation of the benzene or benzene derivative is carried out in the gas phase at a temperature of 1000C to 400 "C by supplying a gaseous feed comprising comprising (a) the benzene or benzene derivative, (b) 0.01 to 5.0 mole of an elementary halogen as a halogenating agent per mole of the benzene or benzene derivative and (c) an inert diluent gas at a rate such that the contact time is in the range of 5 to 500 g-cat-hr/mole.

Inventors: HIRONAKA, TOSHIO, SEKIZAWA, KAZUHIKO, TSUTSUMI, YUKIHIRO, NAKANO, MASAO
Applicants: TOSOH CORPORATION
Application year: 1985
Main classification: C07C17
IPC codes: C07C67, B01J29, C07C25, C07C17, C07B61