METHOD OF MANUFACTURE FOR SEMICONDUCTOR ACCELEROMETER

Abstract: An improved method of manufacturing semiconductor accelerometer having a cantilevered beam is shown. In the fabricating process a semiconductor substrate is devided into p-type regions and n-type regions. The substrate is immersed into an electrochemical solution with a cathord with a suitable voltage applied. Certain portion of the substrate is protected from the etching by the voltage.

Description: The present invention relates to a method of manufacturing semiconductor accelerometer with a cantilever beam and a weight. Recently, there has been developed a micro-miniature accelerometer which is formed on a semiconductor substrate. Such a semiconductor accelerometer is formed on a semiconductor substrate using thin film technology such as etching. It is designed to detect the acceleration by sensing a resistance change due to piezoresistance effect of a semiconductor or a minute capacity change due to deflection of a cantilevered beam. Since such a semiconductor accelerometer is formed using thin film technology, as mentioned in the above, it has an excellent feature that it can be formed extremely small in size, for instance, with a length of order of 100 µ, a thickness of order of 1 µ of the vibrating portion, and an overall chip size of order of 1 mm square, and in addition, that it can be formed on the same substrate for integrated circuit with other elements. One such semiconductor accelerometer is described, for instance in "A Batch-Fabricated Silicon Accelerometer, IEEE Electron Devices", Vol. ED-26, No. 12, Dec. 1979, p. 1911. As detailedly described conventional fabricating method is inconvenient to manufacturing accelerometers with high precision because the thickness of the cantilevered beams is controlled by regulating the temperature and the duration for etching. 8179 IEEE Electron Device Letters Vol. EDL-2, February 1981, No. 2, pages 44 and 45 discloses an electrochemical technique allowing the protection of selected areas of silicon in ethylene diamine-based etchants and its application to the formation of silicon microstructures. Dissolution rates for passivated samples are less than 5 Å/minute, a factor of over 3000 times less than for unpassivated silicon. Applications include pressure sensors, accelerometers, reverse-illuminated image sensors, and other devices where a thin silicon area must be formed from a much thicker starting wafer. The object of the invention is to provide a method of manufacturing for semiconductor accelerometer with high precision. In order to accomplish the above object, the present invention is arranged to form the portion which is to become the cantilevered Si beam (including the Si weight) as a second conduction type (n-type, for instance), encompass its rim with a first conduction type (p-type, for instance), and by etching the portion of the first conduction type alone with the electrochemical etching that does not proceed beyond the p-n junction section, to form the support section of the cantilevered beam, that is of a semiconductor of the first conduction type, with semiconductor of the second conduction type. This method can be performed without a strict controlling on the temperature of an etching solution and the duration for etching. An upper weight to improve the characteristics of the accelerometer can be easily formed on top of the cantilevered beam of the accelerometer without damaging the cantilevered beam. BRIEF DESCRIPTION OF THE DRAWINGS Features and advantages of the present invention will be more apparent from the following description of a preferred embodiment, taken in conjunction with the accompanying drawings, in which: Figs. 1(A) through 1(C) show a perspective view and a cross section view of a prior art device, Fig. 2(A) through 2(E) are views showing the manufacting process for the prior art device, Figs. 3(A) through 3(F) show perspective views and cross section views of an embodiment of the semiconductor accelerometer formed in accordance with the method of manufacture of the present invention, Figs. 4(A) through 4(G) are views showing an embodiment of the manufacturing process in accordance with the present invention, Fig 5 is an explanatory diagram for electrochemical etching, and Figs. 6(A) and 6(B) are cross section views of the prior art device and of a modification to it, Figs. 7(A) through 7(H) show perspective views and cross section views of another embodiment of the semiconductor accelerometer formed in accordance with the method of manufacture of the present invention. DESCRIPTION OF THE PREFERRED EMBODIMENTS To facilitate the understanding of the present invention, a brief reference will be made to a prior art illustrates a perspective view and cross-section views of the semiconductor accelerometer mentioned in the above. In Figs. 1(A) through 1(C), an n-type Si substrate 11, a cantilevered Si beam 12, a Si weight 13, and an air gap 14 are shown. When an acceleration is applied to a semiconductor accelerometer shown in Figs. 1(A) through 1(B), the Si weight 13 is deflected, causing a distortion in the cantilevered Si beam 12. Near the support section of the cantilevered Si beam 12 there is formed a diffused resistor which is not shown, and the resistance value of the diffused resistor changes by the piezoresistance effect when a distortion is created in the cantilevered beam. Then, by detecting the change in the resistance value it becomes possible to detect the acceleration applied. Referring to Figs. 2(A) through 2(E), the manufacturing process for such a semiconductor accelerometer will be described. In Fig. 2(A), in the first step, following the formation of a diffused resistor which is not shown on the n-type Si substrate 21, both of the top and bottom surfaces are coated with thermal oxide films (SiO₂). In the figure, 22 is the top surface thermal oxide film while 23 is the bottom surface thermal oxide film. From the bottom surface thermal oxide film the cavity section 24 for the cantilevered beam and the cavity section 25 for the lower air gap are removed by photoetching. Next, in Fig. 2(B), etching of the Si substrate is carried out with the bottom surface thermal oxide film with the cavities as the mask. For applying etching, anisotropic etching solution of KOH is used, and the thickness of the film for the portion for the cantilevered Si beam 27 is controlled by regulating the temperature of the etching solution and the duration for etching. Then, in Fig. 2(C), the cavity 26 for the upper air gap is formed by photoetching on the top surface thermal oxide film 22. Next, in Fig. 2(D), a Si substrate 21 etching analogous to the step in Fig. 2(B) is carried out using the top surface thermal oxide film 22 with a cavity and the bottom surface thermal oxide film 23 with the cavities previously formed as the masks. This etching is continued until there is formed an air gap 28. Then, in Fig. 2(E), both of the top surface thermal oxide film 22 and the bottom surface thermal oxide film 23 are removed. As in the above, a cantilevered Si beam 27 and a Si weight 29, and also the air gap 28 that defines the external form of the cantilevered Si beam 27 and the Si weight 29, are formed. As described in the above, in the prior art method of manufacturing a semiconductor accelerometer, it was necessary to apply Si etching twice in forming the cantilevered beam, once from the top surface and once from the bottom surface of the Si substrate. In particular, the necessity to give a Si etching from the top surface gave rise to a problem that limitations are imposed on the manufacturing process and the structure of the cantilevered Si beam. In addition, the film thickness of the cantilevered Si beam is determined as mentioned above by the temperature of the etching solution, the duration of the etching, and the stirring condition of the etching solution that are difficult control with high precision, so that there was a problem that it is not easy to set the film thickness accurately. Moreover, as will be described in detail later by referring to Figs. 6(A) and 6(B), when an upper weight is to be formed, by such method as plating, on the top surface of the Si weight in an attempt to improve the characteristics of the accelerometer, there arose a problem that the working on the upper weight is very difficult and also that it is not easy to increase the accuracy of the pattern. In Figs. 3(A) through 3(F) are shown a perspective view and a cross section view of an embodiment of the semiconductor accelerometer manufactured in accordance with the present invention, in which Figs. 3(A) through 3(C) illustrate the structure before etching, that is, before the formation of a cantilevered Si beam while Figs. 3(D) through 3(F) illustrate the structure after etching, that is, after the formation of the cantilevered Si beam. To begin, in Figs. 3(A) through 3(C) an n-type Si layer 32 is formed on a p-type Si substrate 31. The thickness of the Si layer 32 is set to be identical to the thickness of the cantilevered Si beam. Next, a belt-like p-type Si region 33 is formed in the Si layer 32 to define the forms of the cantilevered Si beam and the Si weight. The Si region 33 is formed from the surface of the Si layer 12 to the deptch until it reaches the Si substrate 31. After forming a strain detecting circuit on the substrate, the p-type portions, namely, the Si substrate 31 and the Si region 33, are etched using a suitable mask 34 (resist, SiO₂, Si₃N₄, or the like) on the back surface of the Si substrate 31, to obtain the state as in Fig. 3(D) through 3(F). The strain detecting circuit comprises piezo-resistances 38, 39 which are arranged in series and applied with a suitable voltage therebetween, and an output electrode 40, functioning as strain detecting means. The method of etching in the above will be described later. In the state in Figs. 3(D) through 3(F), the p-type portions, namely, the Si substrate 31 and the Si region 33, are removed in one operation by the Si etching with the mask that is provided on the back surface of the substrate 31. As a result, there are formed a cantilevered Si beam 35, a Si weight 36, and an air gap 37 that surrounds the cantilevered beam and the weight. Next, in Figs. 4(A) through 4(G) is shown the manufacturing process according to the present invention. Referring to Fig. 4(A), an n-type Si layer 42 is formed on a p-type Si substrate 41. As the Si layer 42, an epitaxial layer is more general, but an n-type impurity diffused layer will do also. Then, an upper insulating film 43 is formed on the Si layer 42. As the upper insulating film 43, a thermal oxide film (SiO₂) is general, but a phospho-silicate glass (PSG) film, an Si₃N₄ film, or the like will do also. Next, in Fig. 4(B), a p-type Si region 44 is formed in the n-type Si layer 42 by impurity diffusion, followed by forming of a strain detecting circuit not shown in Fig. 4(B), but same as that in Fig. 3(D). The Si region 44 which is the portion that is to become the air gap that determines the external form of the cantilevered beam and the weight, has to be diffused deep from the surface of the Si layer 42 until it reaches the Si substrate 41. Next, in Fig. 4(C), a part of the upper insulating film 43 is removed in order to form a contact section 45 for applying voltage to the Si layer 42 in carrying out the electrochemical etching. Next, in Fig. 4(D), a metallic (aluminum or others) film is formed on the entire top surface to create an electrode 46. Here, in case the n-type impurity concentration of the Si layer 42 is insufficient for taking the ohmic contact between the Si layer 42 and the electrode 46, it will become necessary to form beforehand a high concentration n-type region at the area for the contact section 45 on the Si layer 42 surface. Next, in Fig. 4(E), portions, namely, the opening section 48 for the cantilevered beam and the drilling section 49 for the air gap, of the lower insulating film that is formed on the back surface of the Si substrate 41 are removed by photoetching to form a mask for the back surface etching. Next, in Fig. 4(F), an electrochemical etching is given from the back surface of the Si substrate 41 using the mask 47 on which are drilled holes. The electrochemical etching will be described in detail later by referring to Fig. 5. In the electrochemical etching, the n-type Si layer 42 alone is protected by the voltage to increase the resistivity to the etching so that the etching proceeds only in the areas of the p-type Si substrate 41 and Si region 44, until it is halted at the p-n junction surface which is the boundary between 41, 44 and 42. Subsequent to the completion of the above Si etching, the upper insulating film 43 which is above the air gap 52 is removed by carrying out an etching from the back surface. Next, in Fig. 4(G), by removing the electrode 46 which was formed on the entire top surface by etching, there are formed a cantilevered Si beam 50, a Si weight 51, and an air gap 52 which determines their external forms. Next, by referring to Fig. 5, the electrochemical etching method will be described. In Fig. 5, a Si wafer 53 and a cathode 55 (Pt or other metal is used in general) are immersed in a Si etching solution 54 in an etching bath 57. Further, a voltage of order of 0.6V from the power supply 56 is applied between the electrode 46 on the surface of the Si wafer 53 and the cathode 55. The positive voltage which is given by the power supply 56 through the electrode 46 is applied only to the n-type Si layer 42 so that the Si layer 42 alone is protected by the voltage and increases the resistivity against the etching. Because of this, the etching proceeds in the areas of the Si substrate 41 and the Si region 44 which are of p-type, but it is halted at the p-n junction surface which is the boundary between 41, 44 and 42. As the etching solution to be used for the electrochemical etching, use is made of the etching solution, for example, of ethylene diamine series (with mixing ratio of 75 ml of ethylene diamine, 12 mg of pyrocaracole, and 24 ml of water) or strong alkali solution such as the KOH etching solution. In the event the electrode 46 is eroded by the etching solution, it will become necessary to give a coating of an appropriate film on the surface of the electrode 46. As may be clear from the structure shown by Fig. 3(A) and 3(B) and the manufacturing process described in Figs. 4(A) through 4(G) and Fig. 5, it is possible in the present invention to form a cantilevered Si beam 35, a Si weight 36, and an air gap 37 by one Si etching from the back surface. Moreover, since the film thickness of the cantilevered Si beam 35 is determined by the thickness of the Si layer 32 which is set initially, it is affected little by the temperature of the etching solution, the duration of etching, the stirring condition of the etching solution, and other conditions. Therefore, it becomes possible to set the film thickness of the cantilevered Si beam 35 with high precision. Furthermore, the following advantage can be obtained according to the present invention. Fig. 6(A) is a cross section view of the structure which was described in the foregoing as the prior art example and an embodiment according to the present invention. An accelerometer of this construction, however, has the following problem. Namely, in the above accelerometer, when an acceleration Ay is applied in the y direction (up and down direction of the figure), the acceleration is detected due to the deflection of the Si weight 62 in the y direction. Therefore, it is desirable that the Si weight 62 will not be deflected when an acceleration in other direction. (x or z direction) is applied. However, in the structure of Fig. 6(A), the center of gravity 64 of the Si weight 62 is located at a distance h below the position of the cantilevered Si beam 61 since the weight is formed beneath the cantilevered Si beam 61. Denoting the sensitivity to acceleration in the y direction by Sy, the sensitivity to acceleration in the x direction is given by Sx = h / ℓ . Sy . In the above equation, ℓ is the distance from the supported end of the cantilevered Si beam 61 to the center of the Si weight 62. In one sets ℓ = 1 mm and h = 100 µm, then one obtains Sx = 0.1 Sy That is, when an acceleration A is applied in the x direction it will give rise to an equivalent effect in which an acceleration of 0.1A is applied in the y direction. Therefore, in order to minimize the acceleration sensitivity in the x direction, it becomes necessary, as shown by Fig. 6(B), to reduce h, the positional deviation of the center of gravity 64, by providing an upper weight 63 on top of the Si weight 62. As a method of forming an upper weight 63, use can be made of plating or bonding. However, considering that such a formation be made at low cost (that is, to give it a wafer processing) and be accomplished without damaging the cantilevered Si beam 61, it is necessary to form the upper weight prior to the formation of the cantilevered Si beam 61 and the Si weight 62. However, in the prior art example shown in Fig. 2, there are required a photoetching process to the Si surface as shown by Fig. 2(C) and a Si etching process as shown by Fig. 2(D). The upper weight 63 has a thickness in the range of several tens of micrometers to several hundreds of micrometers causing a somewhat large gap between a mask and the substrate so that it is very difficult to photoetch the surface after formation of the upper weight 63, and it is also difficult to improve the pattern precision. In addition the upper weight 63 tend to be an obstacle to forming an uniform mask. In contrast to the above, according to the present invention, it is arranged that the Si etching is carried out only from the back surface, as shown by Fig. 4, so that there will arise no difficulty if the upper weight 63 is to be formed during the processes represented by Figs. 4(D) and 4(E). For instance, the upper weight 63 may be formed by leaving a necessary portion of the electrode 46. Next, another embodiment of the invention for the device as shown in Fig. 6(B) will be described below referring to Figs. 7(A) through 7(H). In this process steps shown in Figs. 7(A) through 7(E) are same as in Figs.4(A) through 4(E), so explanation is dispensed with. After the steps shown in Figs. 7(A) through 7(E), an upper weight 63 is depositted on the substrate to be a main weight as shown in Fig. 7(F). Next, in Fig. 7(G), an electrochemical etching is given from the back surface of the Si substrate 41 using the mask 47 on which are drilled holes in a condition that a voltage of order of 0.6V is applied between the electrode 46 on the surface of the Si wafer 53 and the cathode 55. Subsequent to the completion of the above Si etching, the upper insulating film 43 which is above the air gap 52 is removed by carrying out an etching from the back surface. Next, in Fig. 7(G), by removing the electrode 46 which was formed on the entire top surface by etching, there are formed a cantilevered Si beam 50, a Si weight 51, and an air gap 52 which determines their external forms. It should be noted that although the foregoing description has been made in conjunction with the structure in which a cantilevered Si beam of an n-type Si layer is formed on a p-type Si substrate, the roles of the p-type and the n-type can be interchanged without any difficulty. Furthermore, although the description has been made in conjunction with the structure in which there is formed a Si weight, similar argument can also be made even for the case where there is not such a Si weight formed.

Claims: A method of manufacturing a semiconductor accelerometer with a cantilever beam (50) and a weight (51) encompassed by an air gap (52) within a semiconductor substrate (41), comprising the steps of: (a) forming a semiconductor layer (42) of a first conductivity type on a first surface of the semiconductor substrate (41) of a second conductivity type opposite to the first conductivity type; (b) forming in the semiconductor layer (42) a pattern region (44) of the second conductivity type contacting the semiconductor substrate, the pattern region being patterned so as to define the outlines of the cantilever beam (50) composed of the semiconductor layer (42) and the weight (51) composed of the semiconductor substrate (41) connected to one end of the cantilever beam (50); (c) forming a pattern mask (47) on a second surface opposite to the first surface of the semiconductor substrate (41); and (d) etching the pattern region (44), a semi-conductor substrate portion below the pattern region (44) and another semiconductor substrate portion below the cantilever beam (50), from the second surface of the semiconductor substrate (41) using the pattern mask (47) as an etching mask by electrochemical etching. The method of claim 1, which further comprises the step of forming a strain detecting circuit on the substrate (41) after the pattern region (44) has been formed. The method of claim 1, wherein the substrate (41) is made of silicon. The method of claim 1, wherein the first conductivity type layer (42) is an epitaxial layer. The method of claim 1, wherein the electrochemical etching comprises the steps of: (a) forming an electrode (46) in ohmic contact with the semiconductor layer (42); and (b) immersing the substrate (41) together with a separate cathode (55) into an etching solution (54) in condition that a voltage is applied between the electrode (46) and the cathode (55). The method of claim 5, wherein the etching solution (54) is a solution including ethylene diamine. The method of claim 5, wherein the etching solution (54) is a solution including KOH. The method of claim 1, wherein prior to the electrochemical etching an upper weight (63) is formed on the upper surface of the region to be the weight (62).

Inventors: MURAKAMI, KOICHI
Applicants: NISSAN MOTOR CO., LTD.
Application year: 1985
Main classification: H01L21
IPC codes: G01P15, H01L29, F16C11, H01L21