NOVEL EXTRACTANTS AND METHOD FOR THE RECOVERY OF PALLADIUM

Abstract: Novel ortho alkoxy substituted phenyl oxime com­ pounds which are useful for selectively separating and re­ covering palladium from aqueous compositions and mix­ tures containing palladium and other metals are disclosed. Also disclosed is a method of separating and purifying palladium which is present in s solution with at least one other platinum group metal by adjusting the pH of the solu­ tion to from about 0 to 5, contacting the acidified solution with an ortho alkoxy substituted phenyl oxime compound by means of solvent using solvent extractions techniques, separating the aqueous phase from the organic phase con­ taining substantially all of the palladium in association with the oxime compound, and stripping the palladium from the association with the oxime compounds in the organic phase by extraction with an aqueous ammonia solution.

Description: NOVEL EXTRACTANTS AND METHOD FOR THE RECOVERY OF PALLADIUM BACKGROUND OF THE INVENTION 1. Field of Art This invention relates to a novel compound for the recovery and purification of palladium. More particularly, this invention relates to novel ortho alkoxy substituted phenyl oxime compounds which are capable of selectively separating and recovering palladium from aqueous compositions and mixtures containing palladium and other metal ions such as aluminum, nickel, iron, copper, other platinum family metals, rhodium, ruthenium, platinum and the like. 2. Prior Art The recovery and purification of platinum group metals, such as palladium and platinum, is an important commercial process. For example, such processes are useful in the recovery of palladium from solutions obtained in the recovery of mineral deposits of the platinum metals, which solutions commonly contain in addition to palladium, ruthenium, rhodium, iridium and platinum, and small quantities of base metals such as iron, and nickel. Such processes are also useful in the recovery of palladium from spent catalyst materials, such as automobile catalytic converters. Several extraction methods have been developed for recovery of palladium metal values. Solvent extraction processes for the recovery of metal values have certain well recognized advantages over other recovery methods, and such solvent extraction processes are increasing in number and types of applications. Fundamental to a successful solvent extraction process for the recovery palladium is the identification of a water immiscible composition (combination of compounds which will selectively bind to palladium and a suitable solvent) which will selectively extract palladium from an aqueous solution containing palladium, other platinum group metals and other metals. A further requirement for a successful palladium metal recovery by the solvent extraction techniques is an extracting composition having the property such that palladium metal values extracted by the extracting solvent can be recovered from same using another suitable aqueous phase. Illustrative of such prior art solvent extraction processes are those described in U.S. Patent No. 3,967,956 and in United Kingdom Patent No. 20,136,443. In the processes of these patents, palladium is recovered from a mixture of palladium and other platinum group metals through use of an extracting composition containing ortho hydroxyoxime compounds, such as alkyl substituted ortho-hydroxyphenyl oxime compounds. The extracted palladium metal is removed from the extracting solvent by contacting same with a strongly acidic aqueous solution. This method is generally a useful procedure for recovering certain metals from the extracting solvent because the recovery procedure is pH dependent. With ortho-hydroxy phenyl oxime compounds, the extraction process is dependent on the ionizable nature of the phenolic hydrogen, and in the Cu+2 system is generally believed to follow the following equilibrium in which "LH" is the un-ionized oxime: EMI2.1 (aqueous (organic (aqueous (organic phase) phase) phase) phase) Presumably, the pd+2 system would operate in a similar manner when being extracted by ortho-hydroxy phenyl oxime compounds, In which case, palladium metal values are extracted into the organic water immiscible extracting solvent as the neutral species PdL2, while LH ionizes so that the acidity of the aqueous phase increases. Recovery by treatment with strong acid is effective because by shifting the equilibrium, the oxime is protonated releasing the palladium as Pd+2 which migrates into the polar aqueous phase. SUMMARY OF THE INVENTION In accordance with this invention there is provided a small glass of ortho alkoxy substituted phenyloxime compounds which are useful in the extraction of palladium from aqueous solution of palladium and other metals. In addition, there is provided a novel method of selectively separating and recovering palladium from aqueous solution containing palladium and other metals such as platinum, aluminum, ruthenium, rhodium, iron, copper, nickel, and the like. The compounds of this invention are of the formula: EMI3.1 wherein: n is an integer of from 1 to 4; R1 is alkyl, cycloalklyl, or aralkyl; R2 is nitro, halogen, hydrogen, or substituted or unsubstituted cycloalkyl, alkoxy, alkyl, aryloxy, aryl, aralkyl or alkaryl wherein permissible substituents are those which are inert under the use conditions of the compound when extracting and isolating palladium metal values; and R3 is alkyl, aryl, cycloalkyl, alkaryl or aralkyl either unsubstituted or substituted with one or more of the above-referenced permissible substitutents. The process of this invention comprises the steps of: (a) adjusting the pH of a solution comprising palladium and at least one other metal to 5 or less (if necessary); (b) contacting said acidic solution of step (a) with one or more oxime compounds of the above formula; (c) removing from contact with said aqueous acidic solution the organic phase containing all or a part of palladium originally present in said solution and said oxime compound; and (d) extracting said palladium from said organic phase with an aqueous ammonia solution. The novel extractants and process of this invention obviate many of the deficiencies of the hydroxy substituted phenyl oxime compounds heretofore used for extraction of palladium metal. For example, certain of the novel compounds of this invention can selectively extract palladium from aqueous solutions of palladium and other metals including copper. Moreover, other of the novel compounds of this invention are able to selectively extract palladium without the need for ion exchange columns. Also, in the process of this invention, the palladium can be recovering from the organic phase merely by treatment with aqueous ammonia, and strong acids are not required. DESCRIPTION OF THE PREFERRED EMBODIMENTS The compounds of this invention are those of the formula: EMI4.1 wherein n, R1, R2 and R3 are as described above. The following compounds are illustrative of compounds within the purview of the generic formula set forth above, all of which can be conveniently prepared by simply selecting appropriate reactants for use in the procedures described herein below: (2-Methoxy-5-methyl)phenyl nonyl ketoxime (2-Methoxy-5-methyl)phenyl pentadecyl ketoxime 2-Methoxy-5-nonyl benzophenone oxime 2-Methoxy-5-heptadecylbenzaldoxime 2-Methoxy-5-nonyl-4'-methyl benzophenone oxime [2-Methoxy-5-( a,a -dimethylbenzyl)] phenyl hexyl ketoxime (2-Ethoxy)phenyl pentadecyl ketoxime 2-Methoxy-4-phenyl benzophenone oxime (2-Methoxy-4-chloro-5-methyl)phenyl pentadecyl ketoxime 2-Methoxy-3 , 5-dinonyl benzophenone oxime 2-Methoxy-3, 5-dinonyl acetophenone oxime 2-Methoxy-5-nonyl-4'-chloro benzophenone oxime 2-Methoxy-5- (t-butyl) -3' -hexyl benzophenone oxime 2-Methoxy-4'-methyl benzophenone oxime (2-Methoxy-5-nitro)phenyl 2'-napthyl ketoxime 2-Ethoxy-5-nonyl benzaldoxime (2-Methoxy-4-methyl)phenyl 4'-fluorophenyl ketoxime (2-Methoxy-4-methyl)phenyl benzyl ketoxime 2-Methoxy-4'-phenyl benzophenone oxime 2,4-Dimethoxy-4'-methyl benzophenone oxime (2-Ethoxy-4-phenoxy)phenyl propyl ketoxime Illustrative of suitable R1 groups are alkyl such as methyl, ethyl, propyl, isopropyl, isobutyl, butyl, octyl, nonyl, pentyl, hexyl, heptyl and the like; aralkyl such as benzyl, and the like; and cycloalkyl such as cyclopentyl, cyclohexyl and the like. Exemplary of useful R3 substituents are hydrogen, and the above described illustrative R1 substituents. Illustrative of useful R2 substituents are methoxy, nitro, phenoxy, chloro, fluoro, hydrogen and the abovereferenced R1 substituents. These R2 and R3 groups may be unsubstituted or substituted with one or more substituents which are inert to the extraction and stripping process. Illustrative of such permissible substituents are alkyl, halogen, aryl, cycloalkyl, nitro, alkoxy, aryloxy and the like. Preferred are comounds of the above-referenced generic formula in which n is 1 or 2, and R1, R2 and R3 are as described above with the proviso that R2 is substituted at the 4th and/or 5th position on the phenyl ring. Particularly preferred are compounds of the above referenced generic formula in which: n is 1 or 2; R1 is straight chain alkyl having from 1 to about 6 carbon atoms; and R2 and R3 are the same or different and are unsubstituted alkyl, aralkyl, aryl or alkaryl with the proviso that the R2 substituent is substituted at the 4th and/or 5th positions on the phenyl ring, and with the further proviso that R2 and R3 contain a total of from about 15 to about 30 carbon atoms. Amongst these particularly preferred, compounds most preferred are compounds of the aforementioned generic formula in which: n is 1; R1 is straight chain alkyl having from 1 to about 3 carbon atoms; R2 is straight chain alkyl having from 1 to about 12 carbon atoms, with the proviso that the R2 group is substituted at the 4th position on the phenyl ring; and R3 is straight chain alkyl having from about 12 to about 25 carbon atoms and phenyl. Especially efficacious compounds are those of the above-referenced formula in which R1 is methyl, R2 is straight chain alkyl having from 1 to about 9 carbon atoms; and R3 is phenyl or straight chain alkyl having from about 12 to about 25 carbon atoms. Illustrative of these especially efficacious compounds are 2-methoxy-5nonyl benzophenone oxime and (2-methoxy-5-methyl)phenyl pentadecyl ketoxime. The compounds of this invention can be conveniently prepared by a variety of methods. One preferred method for preparing the compounds of this invention is illustrated in the following Reaction Scheme A. Reaction Scheme A EMI7.1 <tb> 5 <SEP> OH <SEP> OH <SEP> O <tb> <SEP> I <tb> <SEP> Acylation <SEP> I <SEP> R3 <tb> (1) <tb> 0 <SEP> d <SEP> 2)n <SEP> ( <SEP> 2)n <tb> <SEP> ooh <SEP> 0 <SEP> 0 <tb> <SEP> R3 <SEP> Alkylation <SEP> R3 <tb> 2) <tb> (R) <SEP> -Q <tb> <SEP> (R2) <SEP> (R2) <SEP> n <tb> <SEP> R1 <tb> 3) <SEP> R3 <SEP> Oximation <SEP> ; <tb> (3) <tb> <SEP> (R,) <SEP> (R2) <tb> wherein n, Rl, R2 and R3 are as described above. In the first step of the process, a substituted phenol is acylated to give the corresponding phenol containing an ortho substituted acyl group, the acylation reaction can be carried out using conventional acylation techniques. The acylation of substituted phenols may be accomplished by several techniques. One method which utilizes the condensation of a phenol with a benzotrichloride catalyzed by aluminum chloride is described by M. S. Newman and A. G. Pinkus (J. Org. Chem., 1954, 19, 985-1002). Another method which can be employed in the acylation step is the condensation of a phenol with a carboxylic acid using boron trifluoride as a catalyst, as described by N. P. Buu-Hoi and J. Seailles (J. Org. Chem., 1955, 20, 606). The acylation reaction may be conducted without a solvent, as the reaction mixtures are generally fluid at typical reaction temperatures of from 75 to about 150 0C. Alternatively, aprotic inert solvents such as trichloroethylene or carbon tetrachloride may be used as a solvent. Generally, when boron trifluoride is used as a catalyst, gaseous boron trifluoride is bubbled subsurface into the reaction mixture at atmospheric pressure. Other equivalent procedures, such as the use of an atuoclave, are apparent to those skilled in the art. Good yields of arylated product are obtained when the phenol or substituted phenol is present in excess (1.2-1.6 molar equivalents) in order to insure monoacylation. Preferably, a para-substituted phenol is also used to insure ortho-acylation. Para-acylation yields material which does not selectively form a complex with divalent palladium and which generally is less stable under the use conditions. Separation of the product (acylated phenol) from the starting phenol will usually depend on the substituents on the phenol and the acyl group, and on other factors known to those of skill in the art and must therefore be determined on a case by case basis through use of known scientific principles. For example, when pcresol is used as the substituted phenol, and the acyl group contains a long hydrocarbon chain, the product can be separated from the starting material by pouring the reaction mixture into methanol. p-Cresol is soluble in methanol whereas the desired product is insoluble. The temperature required for the acylation depends to a large degree on the catalyst used and other factors known to those of skill in the art. For example, when boron trifluoride is used as the catalyst, the reaction rate increases with increasing temperature until a temperature is reached such that gaseous boron trifluoride boils out of the reaction flask when the reaction is conducted at atmospheric pressure. Thus, a temperature of from about 120 to about 1300C seems to be the optimum for carrying out the acylations under these conditions. In the second step of the process, the phenolic group is alkylated with an appropriate alkylating agent such as an alkyl halide or dimethyl sulfate. A number of techniques are possible for the alkylation of the phenolic group. For some phenols, procedures typical of alkyl aryl ether syntheses may be employed. For example, an alkylating agent such as ethanolic NaOH and an alkylating agent such as dimethylsulfate, or potassium carbonate in acetone containing anlalkyl iodide can be employed. Such procedures are exemplified in the literature by G. N. Vyas and N. M. Shah (Org. Synthesis Coll, Vol. 4, 836 (1963). Other alkylation methods which involves phasetransfer catalyzed alkylation of the phenol can be employed. In this procedure, an aqueous phase containing suitable base such as NaOH and a phase transfer catalyst such as tetra-n-butylammonium bromide is contacted with a water-immiscible organic solvent such as methylene chloride containing the dissolved phenol and an alkylating agent such as methyl iodide. In the phase transfer reaction there is considerable flexibility in the choice of base used, the phase transfer catalyst, the organic solvent and the alkylating agent. The base can be an alkali metal hydroxide or carbonate, i.e., bases which are alkaline enough to ionize the acylated phenol. The base is used in at least a stoichiometric amount relative to the phenol. The phase transfer catalyst is usually a quaternary alkyl ammonium halide or hydroxide, and can be used in less than stoichiometric amounts (e.g., 0.01 to 0.1 equivalents). The important feature of the phase transfer catalysts is that, with hydroxide as the counter ion, it has substantial solubility in the organic solvent. Alternatively, crown ethers can be employed as the phase transfer catalyst, but are generally more expensive. The organic solvent should be immiscible with water and should readily dissolve the acylated phenol. Suitable solvents are the chlorinated methanes and ethanes and aromatic hydrocarbons solvents such as toluene and benzene. Alkylation reactions under phase transfer conditions are commonly performed at a temperature of from about 0 to about 400C. The upper temperature is limited by the boiling point of the aqueous or organic phase, whichever is lower. Finally, in the third step of the process the carbonyl portion of the compound is oximated with a conventional oximation agent, such as hydroxylamine. The oximation of the carbonyl compound can be carried out by treating the compound with hydroxylamine in an alcohol solvent such as ethanol or methanol at reflux for 2 to 3 hours. A typical oximation procedure from the literature is that described by A. Lachman, Org. Synthesis Coll. Vol. 2, 70 (1943). For the oximation of the aryl alkyl ketones, preferably a slight excess (1.05 - 1.15 equivalents) of an hydroxylamine salt (the hydrochloride or sulfate) is neutralized with sodium hydroxide, or sodium or potassium carbonate in aqueous solution or in a wateralcohol co-solvent. If a co-solvent is used which has relatively low water content, the neutralization byproduct, e.g., sodium chloride, will not be soluble and can be filtered, if desired. The ketone, dissolved in alcohol is then added. The reaction mixture is refluxed 1 to 2 hours during which time additional alcohol can be added to maintain homogeneity. On cooling the reaction mixture, the product oxime will often separate as a solid or an oil. Otherwise, the volatile alcohol solvent can be removed and the residue washed with water providing the solid or liquid oxime. Alternatively, the compounds of this invention can be prepared by a variation of the procedure of Reaction Scheme A, which variation is depicted in Reaction Scheme B. Reaction Scheme B EMI11.1 <tb> <SEP> OH <tb> <SEP> Alkylation <tb> <SEP> (R2)n <SEP> (R2)n <tb> <SEP> RO <SEP> RO <tb> (2) <SEP> ss <SEP> Acylation <tb> <SEP> (R2) <tb> <SEP> RO <SEP> 0 <SEP> R10 <SEP> NOH <tb> > <SEP> R3 <SEP> Oximation <SEP> X <SEP> R3 <tb> <SEP> {R2)n <SEP> (R2)n <tb> In Reaction Scheme B, steps one and two of Reaction Scheme A are reversed; that is in step 1 of Scheme B, an appropriate phenol compound is alkylated or arylated as in step 2 of Scheme A, to provide a substituted alkoxy benzene and in step 2 of Scheme B the substituted benzene is acylated as in step a of Scheme A to provide the intermediate ketone which can be oximated in accordance with step 3 of Reaction Scheme A. In practice, Scheme B is less desirable than Scheme A in certain instances. This is because in the presence of acylation catalysts such as boron trifluoride and boron tribromide dealkylation of the alkoxybenzene or aryloxy benzene to give phenol can occur during the acylation procedure. See, for example, J.F.W. McOmie and D.E. West, Org. Synthesis Coll., Vol. 5, 412 (1973). Thus, a second alkylation procedure would be required. The phenols and carboxylic acids or their equivalents employed as reactants in the reactions of Reaction Schemes A and B are known compounds which can be obtained from commercial sources or prepared in accordance with conventional preparation methods known to those of skill in the art. Thus, procedures for preparing these reactants will not be described herein in great detail. Reaction Schemes A and B are carried out over a period of time sufficient to produce the desired compound in adequate yield. Reaction times are influenced to a significant degree by the reaction temperature; the concentration and choice of reactants; the choice and concentration of reaction solvent and by other factors known to those skilled in the art. In general, reaction times can vary from about a few minutes to 24 hours or longer. In most instances, when employing preferred reaction conditions, reaction times will be found to vary from about 1 hour to about 3 hours. The process of Reaction Schemes A and B can be conducted in a batch, semicontinous or continuous fashion. The reactants and reagents may be initially introduced into the reaction zone batchwise or they may be continuously or intermittently introduced in such zone during the course of the process. Means to introduce and/or adjust the quantity of reactants introduced, either intermittently or continuously into the reaction zone during the course of the reaction can be conveniently utilized in the process especially to maintain the desired molar ratio of the reaction solvent, reactants and reagents. The reaction can be conducted in a single reaction zone or in a plurality of reaction zones, in series or in parallel or it may be conducted intermittently or continuously in an elongated tubular zone or series of such zones. The materials of construction employed should be inert to the reactants during the reaction and the fabrication of the equipment should be able to withstand the reaction temperatures and pressure. The reaction zone can be fitted with one or more internal and/or external heat exchanger(s) in order to control undue temperature fluctuations, or to prevent any possible "runaway" reaction temperatures. In preferred embodiments of the process, agitation means to vary the degree of mixing the reactions mixture can be employed. Mixing by vibration, shaking, stirring, rotation, oscillation, ultrasonic vibration or the like are all illustrative of the type of agitation means contemplated. Such means are available and well known to those skilled in the art. The compounds of this invention are useful for the selective extraction of palladium from aqueous solutions containing palladium and other metals such as copper, platinum, rhodium, manganese, iridium, zinc, ruthenium, iron, nickel, cobalt, lead and aluminum. The method of using the novel compounds of this invention includes four steps. In the first step of the process of this invention the pH of an aqueous solution comprising palladium and at least one other metal is adjusted to about 5 or less. Of course, if the pH of the solution already falls within this range, no adjustment is required. The source of the aqueous solution is not critical and can vary widely. For example, such solution can be obtained in the recovery of mineral deposits of the platinum family metals which may contain in addition to palladium, platinum, ruthenium, rhodium, aluminum, cobalt, lead, iron, copper, nickel and like metals. The solution can be obtained from process for recovery of palladium from spent palladium containing catalyst materials. Usually these solutions are obtained directly by the acidic digestion of the palladium containing catalytic material in which palladium is usually in association with inert support materials such as silica or alumina. Because of the acidic digestion no specific pH adjustment step is required. Such solutions can also be obtained by acidic digestion of materials in which palladium is present in conjunction with other materials as for example in an alloy, or simply associated with such metals in base metal parts. Here again, the pH of the solution resulting from the digestion step usually falls within the above-referenced range, and no additional pH adjustment is required. The adjustment of the pH of the aqueous solution is preferrably carried out by addition thereto of an acid or base material usually in the form of an aqueous solution, depending on whether an increase or decrease in pH is desired. The type of acid or base material employed is not critical, and can be varied widely. Usually, the type of material employed will normally depend on the initial pH of the solution; and the desired final pH. Illustrative of useful acidic and basic materials, and preferred for use in the practice of this invention are strong mineral acids such as hydrochloric acid, sulfuric acid, and the like, and strong inorganic bases such as the alkali metal hydroxides such as sodium hydroxide, potassium hydroxide, and lithium hydroxide. Particularly preferred materials for adjusting the pH of the aqueous solution are hydrochloric acid and sodium hydroxide. The pH of the aqueous solution is adjusted to about 5 or less. In the preferred embodiments of the invention, the pH is adjusted to from about -0.5 to about 5 and in the particularly preferred embodiments of the invention is adjusted to from about 0 to about 3. Amongst these particularly preferred embodiments, most preferred are those embodiments of the invention in which the pH of the aqueous solution is adjusted to from about 0 to about 1. In the second step of the process of this invention, the solution is contacted with one or more compounds of the above formula, i.e. EMI15.1 or a composition comprised of one or more of said compounds dissolved in an appropriate organic solvent, wherein n, R1, R2 and R3 are as described above. The following compounds are illustrative of compounds within the purview of the generic formula set forth above, which can be used in the process of this invention, all of which can be conveniently prepared by simply selecting appropriate reactants for use in the procedures described herein below: (2-Methoxy-5-methyl)phenyl nonyl ketoxime (2-Methoxy-5-methyl)phenyl pentadecyl ketoxime 2-Methoxy-5-nonylbenzophenone oxime 2-Methoxy-5-heptadecylbenzaldoxime 2-Methoxy-5-nonyl-4'-methyl benzophenone oxime (2-Methoxy-5- (a,-dimethylbenzyl)i phenyl hexyl ketoxime (2-Ethoxy)phenyl pentadecyl ketoxime 2-Methoxy-4-phenyl benzophenone oxime (2-Methoxy-4-chloro-5-methyl)phenyl pentadecyl ketoxime 2-Methoxy-3, 5-dinonyl benzophenone oxime 2-Methoxy-3, 5-dinonyl acetophenone oxime 2-Methoxy-5-nonyl-4'-chloro benzophenone oxime 2-Methoxy-5-(t-butyl)-3'-hexyl benzophenone oxime 2-Methoxy-4'-methyl benzophenone oxime (2-Methoxy-5-nitro)phenyl 2'-napthyl ketoxime 2-Ethoxy-5-nonyl benzaldoxime (2-Methoxy-4-methyl 4'-fluorobenzophenone oxime (2-Methoxy-4-methyl)phenyl benzyl ketoxime 2-Methoxy-4'-phenyl benzophenone oxime 2,4-Dimethoxy-4'-methyl benzophenone oxime (2-Ethoxy-4-phenoxy)phenyl propyl ketoxime Illustrative of suitable R1 groups are alkyl such as methyl, ethyl, propyl, isopropyl, isobutyl, butyl, pentyl, hexyl, and heptyl; cycloalkyl such as cyclopropyl, cyclohexyl, cyclopentyl, cyclobutyl and the like; aralkyl such as benzyl, phenethyl, phenebutyl and the like. Illustrative of useful R2 substituents are methoxy, phenoxy, ethoxy, chloro, fluoro, hydrogen, phenyl and the above-referenced R1 substituents. Exemplary of R3 substituents are hydrogen; and the above described illustrative R1 substituents. These R2 and R3 groups may be unsubstituted or substituted with one or more substituents which are inert to the process condition. Illustrative of such permissible substituents are alkyl, halogen, nitro, alkoxy, aryloxy, cycloalkyl and the like. Preferred compounds for use in the process of this invention are those of the above-referenced generic formula in which n is 1 or 2, and R1, R2 and R3 are as discribed above, with the provison that R2 is substituted at the 4th and/or 5th positions on the phenyl ring. Particularlyl preferred compounds for use in the process of this invention are those of the above generic formula in which: n is 1 or 2; R1 is straight chain alkyl having from 1 to about 6 carbon atoms; and R2 and R3 are the same or different and are unsubstituted alkyl, aralkyl, aryl or alkaryl with the proviso that the R2 substituents are substituted at the 4th and/or 5th positions on the phenyl ring, and with the further proviso that R2 and R3 together contain a total of from about 15 to about 30 carbon atoms. Amongst the particularly preferred compounds for use in the process of this invention most preferred for use are those of the aforementioned formula in which: n is 1; R1 is straight chain alkyl having from 1 to 3 carbon atoms; R2 is straight chain alkyl having from 1 to about 12 carbon atoms, most preferably about 9 carbon atoms substituted at the 4th or 5th position on the phenyl ring; and R3 is straight chain alkyl having from about 12 to about 25 carbon atoms, and aryl (most preferably phenyl). Especially efficacious compounds for use in the process of this invention are those of the above formula in which R1 is methyl, R2 is straight chain alkyl having about 9 carbon atoms, and R3 is phenyl; and those of the above formula in which R1 and R2 are methyl and R3 is straight chain alkyl having from about 12 to about 25 carbon atoms. Of these compounds, experimentation has shown that (2-methoxy-5-methyl)phenyl pentadecyl ketoxime and 2-methoxy-5-nonylbenzophenone oxime exhibit outstanding efficacy. The oxime compound can be used neat, if liquid at the operating temperature, or, alternatively can be dissolved in an appropriate solvent. As used herein an "appropriate solvent" is any solvent which is substantially water immiscible, has a boiling point higher than the highest temperature employed in the process at the operating pressure, is inert under the process conditions and is capable of dissolving at least about 2% of an oxime compound or a mixture of such compounds based on the total weight of the solution. Illustrative of useful solvents are aromatic, aliphatic and cycloaliphatic hydrocarbons such as toluene, cyclohexane, xylenes, chlorinated hydrocarbons, kerosenes such as the Escaide series marketed by Exxon, or commercial blends of high boiling materials (aliphatic and aromatic) such as Fisher Brand K-10 or Shell Solvent 460. The preferred solvent is kerosene. In the preferred embodiments of the invention, the aqueous solution containing palladium and other metals is contacted with a solution of one or more of the oxime compounds dissolved in an appropriate solvent. In general, the concentration of the oxime compound in said solution is at least about 28 by weight of the solution. In the preferred embodiments of the invention, the concentration of the oxime compound in said solution is from about 2 to about 50% by weight of the solution, and in the particularly preferred embodiments is from about 5 to about 25 weight % on the aforementioned basis. Amongst these particularly preferred embodiments of the invention, most preferred are those embodiments in which the concentration of the oxime compound is from about 10 to about 20% by weight of the solution. In the third step of the process of this invention, the organic phase comprised of the oxime compound, the organic solvent, and the palladium is separated from the aqueous phase containing the remaining metals. In the preferred embodiments of the invention, conventional methods can be used to separate the phases through use of the immiscibility of the aqueous and organic phases. For example, since the oxime compound and organic solvent containing same are immiscible in the aqueous phase, these organic and aqueous phases can be separated using conventional immiscible phase separation techniques. In the fourth step of the process of this invention, the organic phase is extracted with an aqueous ammonia solution. In the preferred embodiments of this invention, the aqueous ammonia solution is at least about 1N in ammonia, and in the particularly preferred embodiments is from about 1N to about 10N in ammonia. Amongst these particularly preferred embodiments, most preferred are those embodiments in which the aqueous ammonia solution is from about 3N to about 6N in ammonia. For the recovery of palladium, use of the aqueous ammonia solution offers unique advantages, as it provides a method for readily isolating the palladium as the insoluble salt Pd (NH3) 2C12. Thus, the addition of hydrochloric acid to the palladium loaded aqueous ammonia solution precipitates palladium as the water insoluble salt Pd (NH3) 2C12. The isolation of this salt is common to many conventional methods for palladium recovery, and procedures for converting this salt to pure palladium metal are well known. Process temperatures are not critical and can be varied widely. In general, process temperatures should be less than the boiling point of the oxime compound or any solvent which is employed. In the preferred embodiments of the invention, the process is conducted and a temperature of from about 100C to about 1500C, and in the particularly preferred embodiments from about 200C to about 1000C. Amongst these particularly preferred embodiments, most preferred are those embodiments in which the process temperature is from about 50 to about 800C. Process pressures are also not critical and can be varied widely. The process can be conducted at superatmospheric, atmospheric and sub-atmospheric pressure. For convenience the process is conducted at autogeneous pressure. The process can be conducted in a batch, semicontinuous or continuous action. The present invention lends itself to operation in a single multi-stagecounter current extraction assembly and accordingly a further feature of the invention includes the use of a counter-current extraction assembly for the separation of palladium from aqueous solutions of one or more of the platinum group metals, rhodium, platinum, ruthenium, osminum, iridium, palladium and base metals as described above. The following specific examples are presented to more particularly illustrate the invention. EXAMPLE I 1. Preparation of (2-Methoxy-5-methyl)phenyl Pentadecyl Ketoxime A mixture of 54g (0.5 mol) p-cresol and 64.5 g (0.25 mol) palmitic acid was heated to 85-900C for 3 hours, during which time a steady stream of BF3 was added. The mixture was brought to 1300C for an additional hour. After cooling, the reaction mixture was poured into ice water, with stirring. The product was collected by filtration, and then treated with 200 mL of boiling methanol to dissolve entrained p-cresol. The slurry was filtered, and the solid washed with cold methanol and dried to give (2-hydroxy-5-methyl)phenyl pentadecyl ketone in 84% yield; mp 54-550C. IR (Nujol): 1640 cm 1 (C=0); NMR (CDC13): 6 6.8-7.5 (3H), 2.95 (t, 2H), 2.2 (s, 3H), 1.2 (31H). The above hydroxyphenyl ketone (50g, 0.15 mol) and 42.6g (0.30 mol) iodomethane were dissolved in 100 mL methylene chloride. This solution was stirred rapidly at 400C with a solution of 42g (0.75 mol) potassium hydroxide and 4.7g (0.015 mol) tetra-n-butylammonium bromide in 100 mL water. The reaction time was 5 hours. After cooling the reaction mixture, the phases were separated. The aqueous layer was extracted with 50 mL methylene chloride which was then added to the original methylene chloride layer. The combined organic layers were dried over anhydrous magnesium sulfate and concentrated under vacuum to an oil. The oil was taken up in petroleum ether and filtered to remove residual ammonium salt. The filtrate was again concentrated under vacuum to provide a light yellow oil, identified as (2-methoxy-5-methyl)phenyl pentadecyl ketone. The yield was 91%. IR (thin film): 1660 cm 1 (C=0); NMR (CDC13 6 6.8-7.1 (3H), 3.8 (s, 3H), Ooh3), 2.75 (t, 2H), 2.2 (s, 3H, ArCH3), 1.2 (31H). The above (2-methoxy-5-methyl)phenyl pentadecyl ketone was transformed into the corresponding ketoxime as follows. A solution of 1.94g (0.028 mol) hydroxylamine hydrochloride in 50 mL methanol was neutralized, under a nitrogen atmosphere, by the addition of 1.57g potassium hydroxide. After stirring 1 hour, the slurry was filtered to remove potassium chloride and 7.8g (0.022 mol) of (2-methoxy-5-methyl)phenyl pentadecyl ketone was added to the filtrate. The resulting mixture was refluxed overnight. Methanol was removed under vacuum and the residue taken up in 100 mL methylene chloride which was then washed with 100 mL water. The methylene chloride layer was dried, and the solvent removed under vacuum to give 8.25g (97% yield) of (2methoxy-5-methyl)phenyl pentadecyl ketoxime, mp 51-520C after recrystallization from ethanol-water. The infrared spectrum indicated the absence of the C=0 bond of the starting material. NMR (CDC1 6 6.7-7.2 (m, 3H), 3.77 (s, 3H, OCz3), 2.75 2.75 (t, 2H), 2.3 (s, 3H, ArCH3), 1.2 (31H, aliphatic). 2. Extraction of Palladium A solution of 5 weight percent (2-methoxy-5methyl)phenyl pentadecyl ketoxime in kerosene (Kermac 627 a kerosene manufactured and sold by Kerr-McGee) was prepared. A second solution was prepared by dissolving K2PdC14 in dilute hydrochloric acid (pH=l). The concentration of palladium was 1028 ppm as determined by atomic absorption spectroscopy. The aqueous solution of K2PdC14 was shaken with an equal volume of the first solution containing the oxime for 12 hours at room temperature. The two phases were separated and the aqueous phase analyzed for palladium content. The palladium concentration in the aqueous phase was found to be only 0.27 ppm, indicating greater than 99.9% extraction of the palladium present in the original aqueous solution. EXAMPLE II 1. Preparation of 2-methoxy-5-nonyl benzophenone oxime A sample of 2-hydroxy-5-nonyl benzophenone (259, 0.077 mol) was dissolved in 100 mL methylene chloride. To this solution was added a solution of 20g (0.5 mol) sodium hydroxide in 100 mL deionized water, followed by the addition of 22g (0.154 mol) iodomethane and 2.5g (0.006 mol) tetra-n-butylammonium bromide. The entire mixture was agitated with vigorous mechanical stirring for 1.5 hours at 450C. The reaction mixture was allowed to cool, and the layers separated. The aqueous phase was extracted with 50 mL methylene chloride. The combined organic layers were dried over anhydrous magnesium sulfate and concentrated under vacuum. The residual oil was taken up in petroleum ether, washed with water, dried over magnesium sulfate and again concentrated under vacuum to provide 22g (85% yield) of 2-methoxy-5-nonyl benzophenone. IR(film): 1660 cm 1 (C=0) ; NMR (CDC13 6 6.8-7.7 (m, 8H), 3.7 (s, 3H, OCH3), 0.4-1.8 (m, 19H). To 50 mL methanol (at OOC under nitrogen) was added 4.6g (0.067 mol) hydroxylamine hydrochloride. Potassium hydroxide 3.75g (0.067 mol) was then added and the mixture stirred 0.5 hours. Filtration of the resultant slurry was performed quickly, and the filtrate returned to the reaction flask. To the methanol solution of hydroxylamine was then added 2-methoxy-5-nonyl benzophenone, 22g (0.065 mol), and the resulting mixture refluxed under nitrogen for 12 hours. The reaction mixture was cooled, and concentrated under vacuum to an oil. The oil was taken up in 75 mL methylene chloride and washed with an equal volume of water. The organic layer was then separated, dried over anhydrous magnesium sulfate and the volatiles removed under vacuum to give an oil (15g, 65% yield) identified as 2-methoxy-5-nonyl benzophenone oxime. IR indicated the loss of C=0 stretch at 1660 cm 1. NMR (CDC1R): 6.8-7.7 (m, 8H), 3.75 (s, 3H, OCH3; a singlet at 6 3.65 also appeared, which corresponds to the second geometrical isomer, the ratio of isomers being about 85:15), 0.4-1.8 (m, l9H). 2. Extraction of Palladium A 5% by weight solution of 2-methoxy-5-nonyl benzophenone oxime in kerosene (Kermac 627) was prepared. This solution was agitated for 12 hours with an equal volume of an aqueous solution containing 930 ppm divalent palladium at a pH of 5. After the extraction period, analysis of the aqueous phase indicated only 1 ppm palladium present. This represents the extraction of about 99.9% of the palladium present in the original aqueous phase. EXAMPLE III 1. Preparation of 2-isopropoxy-5-nonyl benzophenone Oxime 2-Isopropoxy-5-nonyl benzophenone was prepared as follows. To 25g of 2-hydroxy-5-nonyl benzophenone in 100 mL CH2C12 was added 20 g NaOH in 100 mL water, followed by the addition of 48g isopropyl bromide and 2.5g tetra-n-butyl-ammonium bromide. The entire mixture was stirred vigorously at 400C for 3 days. The reaction mixture was worked up as described for the preparation of 2-methoxy-5-nonyl benzophenone (Example II) to give 16g of yellow oil (57% yield), identified as the desired product. IR(film): 1660 cm-l (C=0); NMR (CDC13): 6 6.8-7.7 (m, 8H), 4.2 (m, 1H, (CH3)2CH-), 0.2-1.5 (m, 25H). To 150 mL methanol (at OOC and under nitrogen) was added 2.4g hydroxylamine hydrochloride. Sodium hydroxide (2.0g) was then added to the above solution and stirring continued for 1 hour. The slurry was quickly filtered to remove NaCl, and the filtrate was returned to the reaction flask. The above ketone, 12.0g, was then added and the mixture stirred at room temperature overnight. The next day, an additional 5g hydroxylamine hydrochloride was added, and the mixture refluxed for 12 hour more. The mixture was then cooled, the methanol removed under vacuum, and the residue taken up in 75 mL CH2Cl2. The methylene chloride solution was washed with 75 mL water, separated, dried (MgSO4) and the volatiles removed under vacuum to provide 12.6g (100% yield) of the desired 2-isopropoxy-5-nonyl benzophenone oxime (oil). IR(film) indicated complete loss of the C=0 bond. NMR (CDC13): 6 6.8-7.4 (m, 8H), 4.4 (m, 1H), 0.41.8 (m, 25H). 2. Extraction of Palladium An aqueous solution containing 200 ppm Pd(II) at pH 4 was stirred with an equal volume of a 5 weight/volume percent solution of 2-isopropoxy-5-nonyl benzophenone oxime in kerosene at room temperature for 10 minutes. The two layers were then separated and the aqueous layer analyzed for palladium content. The analysis indicated 110 ppm Pd(II) in the aqueous phase or 45% uptake of the palladium by the oxime extractant. EXAMPLE IV 1. Preparation of 2-n-pentoxy-5-nonyl benzophenone Oxime A solution of 2-hydroxy-5-nonyl benzophenone, 15g, in 100 mL methylene chloride was mixed with a solution of 9.25g NaOH in 100 mL water. To this mixture was added 6.9g n-pentyl bromide and l.48g tetra-n-butylammonium bromide. The whole mixture was then vigorously agitated overnight at 400C. After cooling to room temperature with 50 mL CH2C12. The combined methylene chloride layers were concentrated to an oil, which was taken up in 100 mL petroleum ether and washed with 100 mL water. Finally, the organic layer was dried over anhydrous magnesium sulfate and the volatiles removed under vacuum to give 15g (82% yield) of 2-n-pentoxy-5nonyl benzophenone. NMR (CDC13): 6 6.8-7.4 (m, 8H), 3.8 (t, 2H), 0.21.7 (m, 28H). The above ketone was oximated as described in Examples 2 and 3 using 2.lg hydroxylamine hydrochloride neutralized with 1.7g potassium hydroxide in 125 mL methanol. The methanolic hydroxylamine solution was refluxed overnight with 6g of the above ketone. Work-up provided 6.0g (98% yield) of an oil identified as 2pentoxy-5-nonyl benzophenone oxime. IR (film) indicated complete absence of the C=0 bond, and the presence of an OH stretch at about 3300 cm-l. NMR (CDCl3): 6 6.8-7.3 (m, 8H), 3.8 (t, 2H), 0.81.6 (m, 28H). 2. Extraction of Palladium A solution of 0.5g of the above oxime was dissolved in 10 mL kerosene. (Kermac 627) This was stirred for 10 minutes with 10 mL of an aqueous solution containing 334 ppm Pd(II) at pH 4. After the 10 minute extraction period, the phases were separated and the aqueous phase analyzed for palladium content. The results indicated 38 ppm palladium in the aqueous phase or a 89% uptake of palladium by the oxime extractant. EXAMPLE V 1. Preparation of 2-methoxy-5-nonylacetophenone A solution of p-nonylphenol, 35g, in 125 mL methylene chloride was mixed with a solution of 44.5g KOH in 125 mL water. To this mixture was added 459 iodomethane and 5.0g tetra-n-butylammonium bromide. The whole mixture was vigorously stirred at 400C for one hour. After cooling to room temperature, the phases were separated and the aqueous phase extracted with 50 mL methylene chloride. The combined methylene chloride layers were concentrated to an oil which was taken up in 200 mL of petroleum ether and filtered to remove the residual phase transfer catalyst. Finally, the petroleum ether was removed under vacuum to give 31.lg (84%) of p-nonylanisole. NMR (CDCl3): 6 6.6-7.3 (m, 4H), 3.75 (s, 3H), 0.5-1.8 (m, 19H). A mixture of the above anisole (31 g) and glacial acetic acid (15 g) was heated to 700C for five hours, during which time a steady stream of BF3 was added. After cooling the reaction mixture, it was dissolved in 200 mL methylene chloride and washed with 200 mL water. The organic layer was dried (MgSO4) and the solvent was removed under vacuum to give 32.5g of a red oil identified as a mixture of p-nonyl 2-methoxy-5nonylacetophenone (major product) and 2-hydroxy-5nonylacetophenone. To ensure complete conversion to the methoxyketone, the product mixture was re-alkylated by the phase transfer reaction described above. Work-up of the reaction mixture yielded 31.5g (88%) of 2-methoxy-5nonylacetophenone. NMR(CDC13): 6 7.95 (d, 1H), 6.9 (apparent d 2H), 3.8 (s, 3H), 2.5 (s, 3H), 0.5-1.8 (m, 19H); IR (thin film) 1675 cm 1 (coo). The above methoxyketone was oximated as described in Example II, III, and IV using 10g of hydroxylamine hydrochloride neutralized with 8.lg potassium hydroxide in 250 mL methanol. The methanolic hydroxylamine solution was stirred overnight with 31.5 g of the ketone. Work-up yielded 28.5g of an oil identified as 2-methoxy-5-nonylacetophenone oxime. NMR (CDC1): 6 9.5 (b, 1H), 7.55 (d, 1H), 6.86 (apparent d, 2H), 3.8 (s, 3H), 2.25 (s, 3H), 0.5-1.9 (m, l9H). IR (thin film) indicated complete absence of the C=0 bond. 2. Extraction of Palladium A solution of 5 grams of the above oxime in 95 grams of kerosene was made. Ten mL of this solution was contacted with 10 mL of an aqueous solution containing 1900 ppm Pd(II) at pH 3. After a 12 hour extraction period, the phases were separated and the aqueous phase analyzed for palladium content. The results indicated 4.7 ppm palladium in the aqueous phase or 99.7% uptake of the palladium by the oxime extractant. EXAMPLE VI 1. Preparation of (2-methoxy-5-methyl)phenyl Nonyl Ke tox ime Decanoic acid (43 g) and p-cresol (54 g) were combined and heated to 80-900C for 4-5 hours, while BF3 was slowly bubbled into the solution. The solution was cooled and poured into ice-water. The oil was extracted with benzene and the benzene solution distilled to remove benzene and unreacted p-cresol. The distillation pot residue was washed with aqueous potassium carbonate to provide crude (2-hydroxy-5-methyl)phenyl nonyl ketone. NMR (CDCl3): 6 7.6 (s, 1H, OH), 6.8-7.4 (311, aromatic), 2.95 (t, 2H), 2.35 (s, 3H), 0.8-1.9 (m, 17H); IR (film): 1640 cm 1. A solution of the above ketone (17.5 g) in 100 mL methylene chloride was mixed with a solution of 4.0g NaOH in 100 mL water. To this mixture was added 9.9g iodo methane and l.2g benzyl tri-n-butylammonium bromide. The whole mixture was stirred vigorously at room temperature overnight. After twelve hours an additional 23g iodomethane was added and the reaction mixture heated to 400C with continued stirring for an additional four hours. After cooling to room temperature, the phases were separated and the aqueous phase extracted with 75mL methylene chloride. The combined methylene chloride layers were dried over anhydrous magnesium sulfate and the solvent removed under vacuum to yield 13.6g (74%) of (2-methoxy-5methyl)phenyl nonyl ketone. NMR (CDC1): 6 6.7-7.5 (m, 3H), 3.8 (s, 3H), 2.9 (T, 2H), 2.25 (s, 3H), 0.5-1.9 (m, 19H). IR (thin film): 1670 cm 1 (carbonyl). The ketone was oximated as described earlier in Examples 2 and 3 using 3.5g of hydroxylamine hydroxychloride neutralized with 2.0g sodium hydroxide in 50 mL methanol. The methanolic hydroxylamine solution was stirred overnight with 13.0g of the ketone. The work-up yielded 13.9g of a yellow oil that was vacuum distilled to yield 8.7 g of a compound identified as (2-methoxy-5-methyl)phenyl nonyl ketoxime (bp 154-1850C/lmm Hg). NMR (CDC1 6 6.8-7.2 (m, 3H), 3.8 (s, 3H), 2.7 (t, 2H), 2.2 (s, 3H), 0.5-1.8 (m, 17H). 2. Extraction of Palladium A solution of 2.5g of the above oxime in 45g kerosene was made. Ten mL of this solution was contacted with 10 mL of an aqueous solution containing 371 ppm Pd(II) at pH = 1. After a twelve hour extraction period, the phases were separated and the aqueous phase analyzed for palladium content. The results indicated 0.6 ppm palladium in the aqueous phase or 99.8% uptake of palladium by the oxime extractant. EXAMPLE VII An aqueous solution containing Pd(II), Fe(III), Ni(II), Cu(II), Mn(II) and Co(II) was prepared. The concentrations, as determined by atomic absorption spectroscopy, are given as the initial concentrations listed in Table 1. The pH of the solution was adjusted to 1 using hydrochloric acid. The aqueous metal solution was agitated with an equal volume of 5% (by weight) of (2-methoxy-5-methyl)phenyl pentadecyl ketoxime in kerosene (Kermac 627 a kerosene marketed and sold by Kerr-McGee) at room temperature for 1 hour. After separating the phases, the aqueous solution was again analyzed, the results being given in Table 1 as the final concentrations (average of three determinations). The results clearly demonstrate the high specificity of this oxime extractant for palladium over the base metals. Table 1 Metal [Initial] ppm [Final] ppm Pd2+ 100 0.8 Fe3+ 1910 1925 Ni2+ 1895 1855 Cu2+ 1970 1988 Mn2+ 1910 1855 Co2+ 1870 1850 Example VIII A solution of 5 weight percent (2-methoxy-5-methyl) phenyl pentadecyl ketoxime in kerosene (Kermac 627 a kerosene marketed and sold by Kerr-McGee Crop.) was prepared. A second solution was prepared by dissolving K2PdC14 in dilute hydrochloric acid (pH = 1). The concentration of palladium was 1028 ppm as determined by atomic absorption spectroscopy. The aqueous solution of K2PdC14 was shaken with an equal volume of the first solution containing the oxime for 12 hours at room temperature. The two phases were separated and the aqueous phase analyzed for palladium content. The palladium concentration in the aqueous was found to be only 0.27 ppm, indicating greater than 99.9% extraction of the palladium present in the original aqueous solution. The example demonstrates that this oxime extractant can remove palladium values from aqueous solutions at pH 1 to the point where residual concentrations of palladium in the aqueous are less than 1 ppm. EXAMPLE IX The extraction of various metals alone using (2methoxy-5-methyl)phenyl pentadecyl ketoxime was also tested under conditions similar to those described in Example VIII. The results are shown in Table 2. In these experiments, the aqueous phase contained only one metal. The results again show that palladium is readily extracted whereas the other metals are poorly extracted or not at all. Worthy of note is the lack of extraction of copper, which occurs readily with o-hydroxyphenyl oximes. Also noteworthy is the lack of extraction of the other platinum group metals, platinum and rhodium. The pH of the aqueous solutions were 1 unless noted otherwise. Table 2 Metal [Initial] ppm [Final] ppm pd2+ 3) 960 9 Pt2+(pH 3) 966 970 Rh3+ 1190 1135 Cu2+ 1010 1000 Mn2+ 1000 1020 Fe3+ 1000 950 A13+(pH 3) 985 960 Pb2+ 1031 1046 EXAMPLE X A 5% by weight solution of 2-methoxy-5-nonyl benzophenone oxime in kerosene (Kermac 627) was prepared. This solution was agitated for 12 hours with an equal volume of an aqueous solution (pH 5) containing 930 ppm divalent palladium. After the extraction period, analysis of the aqueous phase indicated only 1 ppm palladium present, which represents the extraction of about 99.9% of the palladium present in the original aqueous phase. This example demonstrates the use of another preferred oxime extractant and also demonstrates that the extraction of palladium values is effective at pH 5. EXAMPLE XI An aqueous solution containing 200 ppm Pd(II) at pH 4 was stirred with an equal volume of a 5 weight/volume percent solution of 2-isopropoxy-5-nonylbenzophenone oxime in kerosene at room temperature for 10 minutes. The two layers were separated and the aqueous layer analyzed for palladium content. The analysis indicated 110 ppm Pd(II) in the aqueous phase or 45% uptake of the palladium by the oxime extractant in 10 minutes. This example demonstrates the use of another acceptable oxime extractant at pH 4. EXAMPLE XII A solution of 0.5g of 2-pentoxy-5-nonyl benzophenone oxime was dissolved in 10 mL kerosene. This was stirred at room temperature for 10 minutes with an aqueous solution containing 334 ppm Pd(II) at pH 4. After the extraction period, the phases were separated and the aqueous phase analyzed for palladium content, which indicated 38 ppm Pd(II) present, or 89% uptake of palladium by the oxime extractant. The uptake of palladium in this example is significantly higher than that in Example 5, and suggests that branching at the carbon attached to the phenolic oxygen (the R group) is less preferred than a straight chain alkyl group attached to the oxygen or less preferred than R groups having branching sites remote from the phenolic oxygen. EXAMPLE XIII A 5% by weight solution of 2-methoxy-5-nonylacetophenone oxime in kerosene (Fisher) was prepared. The solution was mixed for 12 hours with an equal volume of an aqueous solution (pH 3) containing 1900 ppm divalent palladium. After the extraction period, analysis of the aqueous phase indicated only 4.7 ppm palladium present, which represents the extraction of about 99.7% of the palladium present in the original phase. This example demonstrates the use of another preferred oxime extractant. EXAMPLE XIV A 5% by weight solution of (2-methoxy-5-methyl) phenyl nonylketoxime in kerosene (Fisher) was prepared. The solution was mixed for 12 hours with an equal volume of an aqueous solution (pH 1) containing 371 ppm divalent palladium. After the extraction period, analysis of the aqueous phase indicated only 0.6 ppm palladium present, which represents the extraction of about 99.8% of the palladium present in the original solution. This example demonstrates the use of another preferred oxime extractant. EXAMPLE XV A solution of 0.5g o-hexadecyloxyacetophenone oxime in 10 mL kerosene was rapidly stirred at 65-700C with 10 mL of aqueous Pd(II) (concentration 450 ppm) at pH 4 for 10 minutes. After separating the layers, the concentration of Pd(II) in the aqueous phase was 150 ppm, representing a 67% uptake of Pd(II) by the oxime extractant under these conditions. Elevated temperatures were employed in this example because the oxime was not sufficiently soluble in kerosene at room temperature, which is more preferred. EXAMPLE XVI Direct competition studies using solutions of Pd(II) and another metal were performed using (2methoxy-5-methyl) phenyl pentadecyl ketoxime in kerosene. The pH in each case was 1. The concentration of the two metals in the aqueous phase were measured before and after the extraction. The results are set forth in Table I below. Table 3 Experiment No. Initial Conc., ppm Final Conc., ppm 1 Pd(II) 1031 Pd(II) < 2 Fe(III) 938 Fe(III) 980 2 Pd(II) 969 Pd(II) 2.5 Cu(II) 1035 Cu(II) 1025 3 Pd(II) 938 Pd(II) none detected Pt(IV) 790 Pt(IV) 755 4 Pd(II) 575 Pd(II) 2.5 Ni (Il) 514 Ni(II) 531 EXAMPLE XVII The following example illustrates the stripping step (step 4) whereby palladium is stripped from the loaded oxime extractant using aqueous ammonia. A solution of Pd(II) (five volumes) at pH 1 and a concentration of 500 ppm was extracted with one volume of a kerosene solution of (2-methoxy-5-methyl)-phenyl pentadecyl ketoxime. After the extraction, the aqueous phase contained only 0.6 ppm Pd2+, indicating that the loaded organic phase contained 2500 ppm palladium. The palladium-loaded organic phase was then stripped with an equal volume of 5M NH4OH at 700C for one hour. The concentration of palladium in the aqueous ammonia phase was found to be 2300 ppm after the stripping operation. Repeating the stripping of the same organic phase with another equal volume of fresh ammonia solution removed the remaining 200 ppm palladium from the organic phase. Thus, essentially all the palladium was removed from the oxime extractant with two sequential strippings with aqueous ammonia. Acidifying the palladium rich ammonia solution with HC1 resulted in the precipitation of a yellow solid, identified by its infrared spectrum as Pd(NH3)2C12. Comparative EXAMPLE A 5% by weight solution of (2-methoxy-5-nonyl) benzophenone oxime-O-methyl ether in kerosene was prepared. This solution was mixed for 12 hours with an equal volume of an aqueous solution (pH 3) containing 294 ppm Pd(II). After the extraction period, analysis of the aqueous phase indicated 274 ppm palladium present, representing an extraction of only 6.8% of the Pd(II) present in the original solution. This example demonstrates that alkylation of the oxime oxygen greatly reduces the ability of the oxime compound to effectively extract palladium.

Claims: WHAT IS CLAIMED IS: 1. A compound of the formula: EMI34.1 wherein: n is an integer of from 1 to 4; R1 is alkyl, cycloalkyl, or, aralkyl; R2 is nitro, halogen, hydrogen or substituted or unsubstituted alkyl, alkoxy, aryloxy, cycloalkyl, aryl, aralkyl or alkaryl wherein permissible substituents are those which are inert under the use conditions of the compounds when extracting and isolating palladium metal values; and R3 is alkyl, aryl, alkaryl or aralkyl either unsubstituted or substituted with one or more of the aforementioned permissible substituents, with the proviso that R2 and R3 together include 7 or more carbon atoms. 2. A compound according to claim 1 wherein: n is 1 or 2; R1 is straight chain alkyl having from 1 to about 6 carbon atoms; and R2 and R3 are the same or different and are unsubstituted alkyl, aralkyl, aryl or alkaryl with the proviso that R2 is substituted at the meta and/or para positions relative to the oximino function and with the further proviso that R2 and R3 together include from about 15 to about 30 carbon atoms. 3. A compound according to claim 1 wherein: n is 1; R1 is methyl; R2 is straight chain alkyl having from 1 to about 12 carbon atoms substituted at the meta position relative to the oximino function; and R3 is straight chain alkyl having from about 12 to about 25 carbon atoms or aryl. 4. A compound according to claim 1 selected from the group consisting of (2-methoxy-5-methyl)phenyl pentadecyl ketoxime, 2-methoxy-5-nonyl benzophenone oxime, 2-isopropoxy-5-nonyl benzophenone oxime, 2-(npentoxy)-5-nonyl benzophenone oxime, 2-methoxy-5-nonyl acetophenone oxime, and (2-methoxy-5-methyl)phenyl nonyl ketoxime. 5. A process for the separation and purification of palladium which is present in an aqueous solution with at least one other metal, said process comprising the steps of: (a) adjusting, as necessary, the pH of the solution to 5 or less; (b) contacting said acidic solution with one or more oxime compounds of the formula: EMI35.1 or a composition comprised of one or more of said compounds dissolved in an appropriate organic solvent, wherein: n is an integer of from 1 to 4; R1 is alkyl, cycloalkyl, or aralkyl; and R2 is nitro, halogen, hydrogen or substituted or unsubstituted alkyl, alkoxy, aryloxy, cycloalkyl, aryl, aralkyl or alkaryl wherein permissible substituents are those which are inert to the process conditions; and R3 is alkyl, aryl, alkaryl, cycloalkyl, or aralkyl either unsubstituted or substituted with one or more of the above referenced permissible substituents; and (c) removing from contact with said aqueous acidic solution the organic phase containing all or a part of the palladium originally present in said solution and said oxime compound. 6. A process according to claim 5 wherein; n is 1 or 2; R1 is straight chain alkyl having from 1 to about 6 carbon atoms; and R2 and R3 are the same or different and are unsubstituted alkyl, aralkyl, aryl or alkaryl with the proviso that the R2 substituent is substituted at the meta and/or para position relative to the oximino function and with the further proviso that R2 and R3 together contain a total of from about 15 to about 30 carbon atoms. 7. A process according to claim 5 wherein said acidified platinum group metal containing solution is contacted with a solution of one or more of the said oxime compounds dissolved in an appropriate solvent; and which further comprises stripping palladium from the organic phase removed in step (c) with an aqueous ammonia solution. 8.-- A process for the separation and purification of the palladium which is present in platinum group metal-containing solutions which comprises the steps of a. acidifying the platinum group metal-containing solution (if necessary) to give a pH within the range of from about 0.5 to about 5; b. contacting by means of a solvent extraction technique, the acidic solution with an oxime compound of the formula: EMI37.1 or a composition composed of one or more of said compounds dissolved in an appropriate solvent, wherein: n is an integer of from 1 to 4; R1 is alkyl, cycloalkyl, or aralkyl; R2 is nitro, halogen, hydrogen or substituted or unsubstituted alkoxy, aryloxy, cycloalkyl, aryl, alkoxy, aryloxy, aralkyl or alkaryl wherein permissible substituents are those which are inert to the process conditions; and R3 is alkyl, aryl, cycloalkyl, alkaryl, or aralkyl either unsubstituted or substituted with one or more of the above referenced permissible substitutents with the proviso that R2 and R3 together include a total of 7 or more carbon atoms; c. removing from contact with the acidic solution the organic phase containing all or a part of the palladium originally present in said solution and said oxime compounds; and d. extracting said palladium from said organic phase with an aqueous ammonia solution. 9. A composition for separating and purifying palladium-wh-ich----is pr-esent- in- a solution with at leastone other platinum group metal, said composition comprising an effective amount of one or more oxime compounds of the formula: EMI37.2 wherein: n is an integer of from 1 to 4; R1 is alkyl, cycloalkyl, or aralkyl; R2 is nitro, halogen, hydrogen or substituted in unsubstituted alkoxy, aryloxy, cycloalkyl, aryl, alkoxy, aryloxy, aralkyl or alkaryl wherein permissible substituents are those which are inert to the process conditions; and R3 is alkyl, aryl, alkaryl, cycloalkyl, or aralkyl either unsubstituted or substituted with one or more of the above referenced permissible substitutents, with the proviso that R2 and R3 together include a total of 7 or more carbon atoms. 10. A composition according to claim 9 wherein the amount of said oxime compounds in said composition is at least about 2% by weight of the composition.

Inventors: DIMMIT, JEFFREY HOWARD, SORIANO, DAVID SCOTT, VAN DER PUY, MICHAEL
Applicants: ALLIED-SIGNAL INC.
Application year: 1985
Main classification: C07C131
IPC codes: C07C49, B01D11, C22B3, C07C45, C01G55, C22B11, C07C239, C07C251, C07C67