PIEZOELECTRIC COAXIAL CABLE

Abstract: A structure which allows the maximization of the piezoelectric response in a piezoelectric coaxial cable. A piezoelectrique coaxial cable comprises a conductive polymer core (2) comprising a high molecular weight polymeric material having conductive particles dispersed therein, a piezoelectric polymer layer (3) surrounding the conductive polymer core, and an outer conducter (4) surrounding the piezoelectric polymer layer, and a protective jacket (5) covering the outer conductor. The high molecular weight polymeric material of the conductive polymer core comprises a polymer capable of being intimately bonded to the piezoelectric polymer.

Description: PIEZOELECTRIC COAXIAL CABLE Background of the Invention This invention relates to a piezoelectric coaxial cable and to a method of preparing the cable. In general terms, a piezoelectric coaxial cable, compri¬ ses a central conductor, an intermediate piezoelectric layer surrounding the central conductor, and an outer conductor surrounding the piezoelectric layer. Such piezoelectric coaxial cables have been proposed for use as transducers since, when they are subjected to an applied pressure, for example caused by the impact of an object, or to acoustic pressure changes, a potential difference will be generated between the conductors by the piezoelectric material. Applications for such devices are numerous and include underwater towed-array hydrophones, intrusion detectors, and the like. In recent years certain polymeric materials, for example pol ( inylidene fluoride) (PVF2) and vinylidene fluoride copolymers have been suggested for use as piezoelectric materials. In order to maximize the piezoelectric proper- ' ties of a vinylidene fluoride polymer, it is necessary to orient the polymer by stretching it, preferably up to its "natural" draw ratio of about 4:1 or beyond, in order to convert at least a portion of the polymer from its initial alpha or form II crystalline phase into its beta or form I crystalline phase. Simultaneously with, or subsequent to, the stretching operation, it is necessary to polarize the polymer by applying a high electric field gradient across the polymer in a direction perpendicular to the direction of orientation in order to align the dipoles in the beta phase of the polymer. Electric field gradients of from 5 to 200 MV/m are typical for the polarizing operation, the maxi¬ mum applied field gradient usually being determined by the dielectric breakdown strength of the polymer material. In order to maximize the piezoelectric response of a piezoelectric coaxial cable the intermediate piezoelectric layer would need to be stretched axially and polarized radially between a central conductor and an outer conductor. While the outer electrode may be applied to the intermediate layer after stretching, or, if a corona polarizing method is employed, the cable may be passed through a corona discharge electrode and an outer conductor for the cable be sub¬ sequently provided, significant problems are encountered in the provision of an inner electrode for the cable. It is not possible to extrude the piezoelectric layer onto a con¬ ventional metal conductor, e.g., a copper conductor, in that it would then be impossible subsequently to stretch the intermediate layer in order to convert it into the beta- phase. This problem is particularly acute when attempting to make long lengths of piezoelectric coaxial cable. One solution which has been proposed is to manufacture a piezoelectric coaxial cable by preparing a tape of the piezoelectric polymer, stretching it, polarizing it, and then wrapping it around the inner conductor. (See, for example, U.S. Patent No. 3,798,474 to Cassand et al and U.K. Patent Application No. 2,042,256 to Quilliam. ) However, this process is disadvantageous in that it requires numerous steps and may result in poor electrical contact between the piezoelectric polymer and the inner conductor. U.S. Patent No. 4,303,733 to Bulle discloses filaments which are essentially coaxial cables comprising at least three layers, at least two of which electrically conductive with at least one electrical insulating layer positioned between the two conductive layers. The patent discloses that the intermediate layer may be piezoelectric. It states that where the filament pursuant to the invention is to be provided with piezoelectric characteristics, the core com¬ ponent preferably is compressible, which is achieved either by utilizing hollow filaments or by selection of appropriate synthetic polymers, as for the example, polyolefins with low molecular weight or polyethers. The patent continues to say that a suitable form of execution consists of using as the core component, an electrically conductive, highly viscous liquid with metal and/or carbon black and/or graphite par¬ ticles dispersed therein. Suitable highly viscous liquids mentioned are, e.g., cis- and transpolyacetylene of relati¬ vely low molecular weight. We have now discovered that an improved piezoelectric coaxial cable results if the core comprises a high molecular weight polymeric material having conductive particles dispersed therein, and the high molecular weight polymer of the core and the piezoelectric polymer are selected such that an intimate bond is formed between the core and the surrounding piezoelectric layer. A central metallic conduc- tor can extend through the center of the conductive polymer core. Summary of the Invention One aspect of this invention comprises a piezoelectric coaxial cable comprising: a) a conductive polymer core comprising a high molecu¬ lar weight polymeric material having conductive particles dispersed therein; b) a piezoelectric polymer layer surrounding the con¬ ductive polymer core; and c) an outer conductive layer surrounding said piezoelectric electric layer; said high molecular weight polymeric material of the core being intimately bonded to the piezoelectric polymer. Another aspect of this invention comprises a piezoelectric coaxial cable comprising: a) a central metallic conductor; b) a conductive polymer layer which surrounds the metallic conductor; c) a piezoelectric polymer layer which surrounds the conductive polymer layer and which has been ren- dered piezoelectric by stretching and polarizing it while it is in contact with the conductive polymer layer; and d) an outer conductor which surrounds the piezoelectric polymer layer. Another aspect of this invention provides a method of preparing a piezoelectric coaxial cable which comprises a) extruding a core of a high molecular weight conduc¬ tive polymeric material having conductive particles dispersed therein; b) extruding a piezoelectric polymer layer around the core thereby forming a composite structure having an intimate bond between the polymer of the core and the piezoelectric polymer; c) stretching the resulting composite structure axially such that the length of the structure is increased about four times its original length; d) applying an outer conductor onto the surface of the piezoelectric polymer layer; and e) polarizing the piezoelectric layer to increase the piezoelectric properties thereof. Yet another aspect of the invention comprises a method for preparing a piezoelectric coaxial cable comprising: a) providing a central metallic conductor; b) extruding a conductive polymer layer over the central conductor; c) extruding a dielectric polymer layer which is capable of being rendered piezoelectric over the conductive polymer layer; d) stretching the dielectric polymer layer; e) polarizing the dielectric, polymer layer to render said layer piezoelectric; and f) applying a second metallic conductor to surround the dielectric layer. The piezoelectric polymer layer is preferably a vinyli¬ dene fluoride polymer and the high molecular weight poly¬ meric material of the conductive polymer core is preferably the same polymer as the piezoelectric layer, an elastomer, such as ethylehe-ethyl aerylate elastomer, or a ther¬ moplastic elastomer, such as a segmented copolyester ther¬ moplastic elastomer. Brief Description of the Drawing Figure 1 shows a cross-sectional view of a typical coaxial cable in accordance with this invention. Figure 2 shows a cross-sectional view of a typical coaxial cable in accordance with this invention wherein there is a center metallic conductor. Detailed Description of the Invention The piezoelectric cable of this invention has a conduc¬ tive polymer core comprising a high molecular weight poly¬ meric material having conductive particles therein. The polymeric material is selected so that it intimately bonds to the piezoelectric polymer used to make the cable. The term "intimately bonds" is used in the context of this application to mean that the polymeric material and the piezoelectric material of the cable form a bond between them which is maintained during the subsequent stretching and polarizing steps during manufacture of the cable. The high molecular weight polymeric material should have an average molecular weight above about 50,000, preferably above about 100,000 and most preferably above 150,000. The average molecular weight, Mw, referred to herein is a weight average molecular weight and is calculated by the following formula n M 2 Mw = x . M x n x H x where n is the number of moles of species x having molecular weight Mx. -8- , Preferably the polymeric materials used for the conduc¬ tive core is the same polymer as the piezoelectric polymer, e.g. polyvinylidene fluoride, or other piezoelectric polymer as discussed below, an elastomer or a thermoplastic elastomer. The term elastomer is used herein to refer to a high molecular weight polymeric material exhibiting a charac¬ teristic rubber-like elastic deformability under the action of comparatively small stresses, and returning substantially to its original size and shape upon the removal of the applied stress, and which has an elastic modulus in the uncrosslinked state -of 30N/mm^ or less, measured at room * temperature using the method of ASTM-D638-72. Elastomers which can be used in the present invention include, for example, acrylic elastomers, acrylonitrile- butadiene copolymers, chloroprene, chlorinated and chloro- sulfonated polyethylenes, epichlorohydrin polymers and fluoroelastomers. Preferred elastomers are acrylic elastomers, such as ethylene/acrylic ester polymers. Examples of such elasto¬ mers include: a) An ethylene/alkyl aerylate or ethylene-alkyl methacrylate copolymer where the alkyl group has 1-4 carbon atoms; the proportion of the acrylic ester being about 2.4-8.0 moles of ester groups per kilogram of the copolymer. b) A terpolymer of ethylene with an alkyl aerylate or methacrylate wherein the alkyl group has 1-4 carbon atoms, and a third copolymerizable monomer, which may be, for example one of the following: i. a C ] _-C_2 alkyl monoester or diester of a butenedioic acid, ii. acrylic acid iii. methacrylic acid, iv. carbon monoxide, v. acrylonitrile, vi. a vinyl ester, vii. an alkyl aerylate or alkyl methacrylate, the alkyl group having at least five carbon atoms ; and viii. maleic anhydride. Typical acrylic elastomers of this type can be a simple copolymer of ethylene with methyl aerylate, ethyl aerylate, propyl aerylate isopropyl aer late, a butyl aerylate, methyl methacrylate, ethyl methacrylate, propyl methacrylate, isopropyl methacrylate, a butyl methacrylate or vinyl ace¬ tate. Such copolymers if not commercially available, can be made by conventional and well know methods. The terpolymer of ethylene with an acrylic ester and a third monomer may contain as the third monomer an ester of fumaric acid or maleic acid, wherein the alcohol moiety can be, for example, methyl, ethyl, propyl, isopropyl, various isomers of butyl, pentyl, hexyl, heptyl, octyl, nonyl. decyl, undecyl, dodecyl and the like. The third monomer may also be, among others, a vinyl ester such as for example, vinyl acetate or vinyl butyrate. Excellent results have been obtained using as the elastomer component of the polymer composition a terpolymer of ethylene, methyl aerylate and a cure-site monomer comprising carboxyl groups available from Du Pont under the trade name Vamac (Registered Trade Mark) . Thermoplastic elastomers include, for example, segmented eopolyesters, thermoplastic polyurethanes, styrene-butadiene block copolymers, and ionomers. Illustrated thermoplastic elastomers are segmented co-polyesters consisting essen¬ tially of recurring intralinear long chain ester units and short chain ester units randomly joined head-to-tail through ester linkages. Such eopolyesters are derived) for example, from terephthalic acid, tetramethylene ether glycol and 1,4-butadiene. The high molecular weight polymer is rendered conductive by dispersing therein conductive particles. The conductive particles can be conductive carbon black, particulate or fibrous graphite, metal particles or metal fibers, or com¬ binations thereof. Preferred are carbon black particles. The resistivity of the conductive polymer material should be less than about 15,000 ohm-cm, preferably less than about 3000 ohm-cm and most preferably less than about 100 ohm-cm. It has been found that during the step of stretching the conductive polymer material during manufacture of the cable. -li¬ the resistivity of the composition tends to rise. This is particularly true if the polymer used is crystalline. Thus, it is preferred to use a non-crystalline polymeric material. Use of an elastomer, such as elastomeric ethylene-acr late copolymer or terpolymers, provides a conductive polymer com¬ position whose resistivity remains essentially constant through coextrusion and stretching processes. If, however, it is desired to use a crystalline polymer for the conduc¬ tive core, annealing of the structure can reduce the resistivity toward its value prior to stretching. A central metallic conductor can extend through the con¬ ductive polymer core. The metallic conductor increases the conductivity of the core. Generally when an electric current is passed through the cable, it will flow through the metallic conductor. However, in the event there is a break in the metallic conductor, the- current can flow through the surrounding conductive core thereby preserving conductivity of the cable. As discussed below, the use of a low melting alloy is preferred for the central metallic con¬ ductor. These alloys tend to be brittle and thus the abi¬ lity for conductive polymer to provide continuity at a break in the central metallic conductor can be important. The central metallic conductor preferably comprises a low melting point (LMPM) so that the inner conductor and the piezoelectric polymer members can be heated to melt the metal and then stretched while the metal is still liquid. In theory any metal having a melting point that is suf¬ ficiently low to allow the metal to melt without thermally degrading the conductive and piezoelectric polymer members may be used, although, because the modulus of such metals in general increases with their . melting point, it is desirable to select a metal having regard to the softening point of the conductive and piezoelectric polymer layers and having regard to the preferred stretching temperature. Preferably the metal has a melting point of not more than about 170°C, more preferably not more than about 160°C, and especially not more than about 150°C. Also it is preferred for the metal to have a melting point of at least about 65°C and most especially at least about 70°C. The metal forming the inner conductor may be formed from an alloy having an eutec- tic composition in which case it will exhibit a single, well defined, melting point, or it may be formed from a non- eutectic composition in which case the metal may enter a phase between the solidus and liquidus lines of its phase diagram in which its ductility increases with temperature. It is not necessary for the metal to melt completely for the stretching operation, provided that it becomes sufficiently ductile so that it will not fracture. In some instances, where it is possible to employ metals having melting points below 100°C, it may be desirable to use bismuth containing alloys that expand as they solidify from the melt. A piezoelectric polymer layer surrounds the conductive polymer core. The piezoelectric polymer can be, for example poly(ethylene terephthalate) , nylon 5, nylon 7, poly(hydroxy-butyrate) , poly(aerylonitrile-co-vinyl acetate) , and vinylidene fluoride polymers. The term "vinylidene fluoride polymer" is intended to include poly¬ vinylidene fluoride), commonly abbreviated to "PVDF" or "PVF2" and those copolymers of vinylidene fluoride which can be rendered piezoelectric by orientation and polarization. Suitable copolymers include copolymers and terpolymers of vinylidene fluoride with vinyl fluoride, trifluoroethylene, tetrafluoroethylene, vinyl chloride, and chlorotrifluoroethylene. Blends of vinylidene fluoride polymers with other polymers, e.g., poly(methyl methacrylate), can be used. Composites made from vinylidene fluoride polymers and filled vinylidene fluoride polymers may also be used. Preferably the piezoelectric member comprises a vinylidene fluoride polymer, more preferably poly(vinylidene fluoride) and especially it consists substantially solely of poly(vinylidene fluoride). The term piezoelectric polymer is used in this applica¬ tion to designate the polymer which in the final form of the coaxial cable exhibits piezoelectric activity. The polymer initially utilized in extruding the polymer layer surrounding the conductive polymer core, may exhibit little, if any, piezoelectric characteristics. The piezoelectric polymer layer in the coaxial cable should be from about 0.1 to about 2 millimeters (mm) thick and preferably from about 0.5 to about 1 mm. The piezoelectric coaxial cable has an outer conductor which surrounds the piezoelectric layer. The outer conduc¬ tor can be metallic or a conductive polymer composition. Optionally an outer insulating jacket may be applied around the outer conductor. The jacket may be made from any material which is a good electrical insulator and which pro¬ vides the desired degree of mechanical protection. For example, polyethylene, vulcanized rubber, or poly(vinyl chloride) can be used. Poly(vinyl chloride) is particularly preferred. Figure 1 illustrates in cross-section a typical coaxial cable, 1, of this invention. In Fig. 1, a conductive polymer core, 2, of an ethylene-methyl aerylate terpolymer having conductive carbon black dispersed therein. A piezoelectric (PVF2) polymer layer, 3, surrounds the core and outer conductor, 4, surrounds the piezoelectric layer. An outer protective jacket, 5, surrounds the outer conduc¬ tor. Figure 2 illustrates in cross-section a typical coaxial cable, 1, of this invention which comprises a central metallic conductor, 6. The conductive polymer core, 2, surrounds the central metallic conductor, 6, and in turn is surrounded by a piezoelectric polymer layer, 3, outer conductor, 4, and protective jacket, 5. In another aspect of this invention, additional layers of the piezoelectric layer, separated from each other by an intervening conductive polymer layer, may be added over the outer conductor, thereby increasing the piezoelectric response. An example of such a construction is a coaxial cable comprising a conductive polymer core, a first piezoelectric polymer layer surrounding the core, a second conductive polymer layer surrounding the first piezoelectric polymer layer, and a second piezoelectric polymer, etc., and finally an outermost conductor which may be either a metal or a conductive polymer. The conductive polymer core is formed by extruding the conductive polymeric material in the form of an elongate rod of thickness from about 1 to about 5 mm, . preferably from about 1.5 to about 3.0 mm. When a center metallic conductor is present, the cable can be prepared by first extruding the metal conductor, in wire or rod form and then extruding a conductive polymer layer around the metal conductor. The piezoelectric polymer layer can be coextruded with the core or can be extruded over the core after it has been produced. In either event an intimate bond is preferably formed bet¬ ween the core and the piezoelectric layer. The resulting composite is stretched then polarized to provide the desired piezoelectric activity. Where the piezoelectric polymer is PVF2' it generally must be stretched and then polarized in a strong electric field before significant piezoelectric responsiveness deve¬ lops. Stretching partially or substantially converts PVF2 from the alpha-phase in which it ordinarily crystallizes from the melt into oriented chains of the more highly polar beta-phase. The stretching temperature is important. The temperature should be high enough so that there is suf¬ ficient molecular mobility for individual polymer segments to realign themselves without fracture, but not so high (above about 150°C) so that entire alpha-phase chains are mobile enough to slide past each other instead of stretching to the beta-phase conformation, thus resulting in little conversion, and is preferably between about 60 to 100°C. The amount of stretching should be about 200 to 400 percent, or higher, for example using an ultrahigh drawing procedure. If desired, the PVF 2 Q r the PVF2 and the conductive polymer core may be crosslinked, for example by gamma or electron beam irradiation, and stretching at a temperature above its melting point. The outer conductor can be applied directly to the sur¬ face of the piezoelectric polymer by, for example, coating it with a conductive paint. Conductive paints comprising a suspension of metal particles, in particular silver par¬ ticles, dispersed in a liquid vehicle can be employed. The paint can be applied by spraying, brushing, dipping, coating, or the like. Another technique for attaching the outer conductor is to vacuum deposit a layer of highly con¬ ductive metal, e.g. silver, onto the surface. Conductive polymer outer conductors can be applied by extrusion or coextrusion. The poling process (polarization) converts the randomly oriented dipoles of the beta-phase into uniformly oriented ones. Poling may take place during the stretching process or preferably, after stretching has taken place. For poling P F2, electric fields of 5 to 200 MV/m can be used, but fields of 50 to 150 MV/m are preferred, and about 100 MV/m most preferred. The poling may be done by a contact method, in which case the outer electrode should be provided before the poling. A high voltage connection is made directly to the outer electrode- while the inner electrode is connected to the ground, or vice versa. The device is heated to a temperature above the alpha-transition temperature in order to maximize molecular mobility and poled at temperature for about 0.5 to 2.5 hours, and preferably 1 hour. A poling temperature in the range from about 60 to 120°C is preferred and about 80 C most preferred. At the end of this period, the device is cooled while maintaining the voltage in order to freeze in the dipole orientation. PVF2 can also be poled by a corona discharge, in which case the outer electrode must be provided after the poling. The device is passed through a tubular corona discharge electrode with the inner conductor of the device grounded. Preferred poling times are from a few minutes to half an hour. While corona poling may be performed at temperatures other than room temperature, it is often done at room tem¬ perature because temperature control is sometimes incon¬ venient. Example 1 This example illustrates the preparation of a typical coaxial cable of this invention. A conductive polymer formulation with a resistivity of 12 ohm-cm was prepared by milling an acrylic elastomer (Vamac B-124, DuPont) with 16.0 weight per cent carbon black (Black Pearls 2000, Cabot). It was then extruded using an extruder equipped with a 2.5 mm ID die and operating at a 12 rpm screw speed, 3500-4000 psi head pressure and a 68°C (zone 1) to 145°C (die) temperature profile. Poly(vinylidene fluoride) (Solef 1010, Solvay) was then extruded over the rod using the same extruder but operating at 10-20 rpm screw speed, 800 psi pressure and 210°C (zone 1) to 227°C (die) temperature profile. A segment of this conductive rod surrounded by PVF2 was stretched at 80°C on an Instron mechanical tester equipped with a hot box at a rate of 2 in./min. to approximately the natural draw ratio, i.e. about 300%. The stretched com¬ posite structure was coated with conductive silver paint and then poled at about 80°C for 1 hour. The applied voltage was about 35 kV. The hydrostatic coefficient was measured using a typical method for such measurement as outlined below. The hydrostatic coefficient was determined to be about 10 pC/N. The coefficient was measured by placing the sample in a cyclical pressure cell, with the cyclical hydrostatic pressure being applied by a piston displacing a dielectric oil. Typical peak-to-peak pressures used during an experi¬ ment are approximately 140 - 1000 kPA (20-140 psi) with a frequency of 3 to 10 Hz. The pressure is measured via a Sensotec A205 transducer and 540D amplifier (accuracy approximately 9 kPa). Signals from both devices were fed into a Nicolet 2090 III digital oscilloscope from which peak-to-peak pressures P and charge Q were determined. The hydrostatic coefficient d3h was then determined as d3h = Q/AP where A is the sample surface area. For a coaxial cable, A is given by A = 2 lt/ln(R/R' ) where 1 is the length, t is the thickness, is the rela¬ tive permittivity of the piezoelectric layer, is the per¬ mittivity of free space, R is the outer radius, and R 1 is the inner radius. A common unit for d3h is pC/N (picoCoulombs/Newton) . The pyroelectric effect product in such an experiment is not corrected for, as it amounts to only about 5% of the measured activities. Such a correc¬ tion, if made, would result in an increase of the reported d3h. Example 2 A conductive polymer formulation with a resistivity of 12 ohm-cm was prepared by milling an acrylic elastomer (Vamac B-124, Du Pont) with 16.0 weight per cent carbon black (Black Pearls 2000, Cabot). It was then extruded over wire made of an alloy containing bismuth (52.5%), lead (32.0%), and tin (15.5%) and melting at 95 C (Belmont Metals 2531). A 1.5 in. extruder operating at 7.5 rpm screw speed, 4500-5000 psi head pressure, and 65°C (zone 1) to 125°C (die) temperature profile was used. The tooling para¬ meters were: die, 0.165 in. ID; tip, 0.100 in. ID and 0.125 in. OD. Poly(vinylidene fluoride) (Solef 1008, Solvay) was then extruded over this construction using the same extruder but operating at 20-25 rpm screw speed, 700 psi head pressure, and 210°C (zone 1) to 232°C (die) temperature profile. The tooling parameters were: die, 0.320 in. ID; tip, 0.170 in. ID and 0.220 in. OD. A segment of this alloy-conductive polymer-PVF2 com¬ bination was stretched at 100°C on an Instron mechanical tester equipped with a hot box at a rate of 2 in/min. to approximately its natural draw ratio, or about 300 per cent. The stretched combination was coated with conductive silver paint and then poled at 65°C for 1 hour by the con¬ tact method. The applied voltage was 35 kV, corresponding to a field of 116 MV/m on allowance for sample thickness. Its hydrostatic coefficient d3h after poling was 12.9 pC/N. Example 3 Example 2 was repeated, except that the poling was done at 80°C for 0.5 hour at 35 kV. Two samples were poled, corresponding to fields of 109 MV/m and 113 MV/m on allowance for sample thickness. The d3h's were 9.2 and 10.2 pC/N, respectively. Example 4 A conductive polymer formulation with a resistivity of 7 ohm-cm was prepared by mixing in a Banbury mixer an acrylic elastomer (Vamac B-124) with 17.5 weight per cent carbon black (Black Pearls 2000, Cabot). It and a layer of PVF2 (Solef 1008) were coextruded over the same alloy as in Example 2 (Belmont Metals 2531), with the PVF2 forming the outermost layer. The alloy was fed as a melt using a zenith gear pump operating at 115°C and 6 rpm. The PVF2 extruder was a 1 in. extruder operating at 30 rpm, 700 psi, and 170°C (zone 1) to 210°C (die). The conductive polymer extruder was a 1.25 in. extruder operating at 10 rpm, 1000 to 3000 psi, and 65°C (zone 1) to 140°C (die). The tooling parameters were: die, 0.215 in. ID; first tip, 0.150 in. OD; second tip, 0.0825 in. OD. A segment of this coextruded combination was stretched under the conditions described for Example 2 and then coated with conductive silver paint. A sample poled at 80°C for 1 hr at 25 kV (54 MV/m) by the contact method had a d3h of 10.2 pC/N. Another sample poled at 80°C for 0.5 hr at 45 kV (134 MV/m) also by the contact method had an activity of 13.1 pC/N. While the invention has been described herein in accor¬ dance with certain preferred embodiments thereof, many modi¬ fications and changes will be apparent to those skilled in the art. Accordingly, it is intended by the appended claims to cover all such modifications and changes as fall within the true spirit and scope of the invention.

Claims: Claims 1. A piezoelectric coaxial cable comprising: a) a conductive polymer core comprising a high molecu¬ lar weight polymeric material having conductive particles dispersed therein; b) a piezoelectric polymer layer surrounding the con¬ ductive polymer core; and c) an outer conductor surrounding the piezoelectric layer; said high molecular weight polymeric material of the core being intimately bonded to the piezoelectric polymer. 2. A cable in accordance with Claim 1 wherein the con¬ ductive polymer core comprises an elastomeric material having conductive particles dispersed therein. 3. A cable in accordance with Claim 2 wherein said elastomer is an acrylic elastomer. 4. A cable in accordance with Claim 3 wherein said acrylic elastomer comprises an ethylene-methyl acrylate ter¬ polymer. 5. A cable in accordance with Claim 2 wherein the resistivity of the conductive polymer core is less than about 100 ohm-cm. 6. A cable in accordance with Claim 1 wherein the con¬ ductive polymer core comprises a polymer having a molecular weight above about 50,000. 7. A cable in accordance with Claim 1 wherein the con¬ ductive polymer core comprises a polymer having a molecular weight above about 100,000. 8. A cable in accordance with Claim 1 wherein the piezoelectric polymer layer comprises a vinylidene fluoride polymer. 9. A cable in accordance with Claim 8 wherein the viny¬ lidene fluoride polymer is poly(vinylidene fluoride). 10. A piezoelectric coaxial cable comprising: a) a central metallic conductor; b) a conductive polymer layer which surrounds the metallic conductor; c) a piezoelectric polymer layer which surrounds the conductor polymer layer and which has been rendered piezoelectric by stretching and polarizing it while it is in contact with the conductive polymer layer; and d) an outer conductor which surrounds the piezoelectric polymer layer. 11. A device according to Claim 1 wherein the first conductor comprises a metal melting at or below 170°C. 12. A device according to Claim 1 wherein the con¬ ductive polymer layer has a resistivity below about 500 ohm-cm. 13. A device according to Claim 1 wherein the con¬ ductive polymer layer comprises an acrylic elastomer. 14. A device according to Claim 1 wherein the con¬ ductive polymer layer comprises a fluorinated elastomer. 15. A device according to Claim 1 wherein the piezoelectric polymer layer comprises a vinylidene fluoride polymer. 16. A device according to Claim 1 wherein the piezoelectric polymer layer comprises vinylidene fluoride homopolymer. 17. A method of preparing a piezoelectric coaxial cable which comprises a) extruding a core of a high molecular weight conductive polymer material having conductive particles dispersed therein; and b) extruding a piezoelectric polymer layer around the core thereby forming a composite structure having an intimate bond between the polymer of the core and the piezoelectric poly- polymer; c) stretching the resulting composite structure axially such that the length of the structure is increased at least about three times its original length; d) applying an outer conductor onto the surface of the piezoelectric polymer layer; and e) polarizing the piezoelectric layer to increase the piezoelectric properties thereof. 18. A method in accordance with Claim 17 wherein the core and piezoelectric polymer layer are coextruded. 19. A method in accordance with Claim 17 wherein the composite structure is stretched at a temperature between about 60 to 100°C. 20. A method in accordance with Claim 17 wherein the composite structure is stretched prior to the step of polarization. 21. A method in accordance with Claim 17 wherein the composite structure is stretched simultaneously with the step of polarization. 22. A method in accordance with Claim 17 wherein the outer conductor is applied prior to the step of polarization. 23. A method in accordance with Claim 17 wherein the outer conductor is applied after the step of polarization. 24. A method for preparing a piezoelectric coaxial cable comprising: a) providing a central metallic conductor; b) extruding a conductive polymer layer over the inner conductor; c) extruding a dielectric polymer layer which is capable of being rendered piezoelectric over the conductive polymer layer; d) stretching the dielectric polymer layer; e) polarizing the dielectric polymer layer to render it piezoelectric; and f) applying a second metallic conductor to surround the dielectric layer.

Inventors: FARRAR NIGEL RICHARD, RAUWENDAAL CHRISTIAAN JOHN, SONI PRAVIN LAXMINARAYAN, TURK PETER, FARRAR, NIGEL, RICHARD, RAUWENDAAL, CHRISTIAAN, JOHN, SONI, PRAVIN, LAXMINARAYAN, TURK, PETER
Applicants: RAYCHEM CORP, RAYCHEM CORPORATION
Application year: 1985
Main classification: H01L41
IPC codes: H01L41