OPTICALLY ACTIVE, ANTI HEAD-TO-HEAD COUMARIN DIMER-POLYAMIDES

Abstract: Optically active, anti head-to-head coumarin dimers represented by general formula (I) or (II): a process for their preparation, optically active polyamides represented by general formula (III) or (IV), (wherein A represents a primary or secondary amine residue, and n represents an integer of 2 or more) and a process for their preparation from (I) or (II).

Description: DESCRIPTION Technical Yield The present invention relates to an optically active anti head-to-head coumarin dimer of the following formula (I) or (II): EMI1.1 These two optically active isomers are hereinafter referred to as the (+)-dimer and the (-)-dimer, respectively. Further" the present invention relates to a novel optically active polyamide which corresponds to a derivative of the optically active, anti head-to-head coumarin dither. Technical BacXzround of the Invention The anti head-to-head coumarin dimer can be obtained by photodimerizing coumarin. This compound is optically inactive, i.e. a (#)-dimer. Since the dimer contains two lactone rings which are highly reactive and further a cyclobutane ring which can be cleaved by light, the compound is useful even in the form of the (+)-dimer as a starting material for the production of photopolymers. The (+)- or (-)-dimer which has an optical activity in addition to high reactivity can be more widely used. For example, the lactone ring is reacted with a hydroxyl or amino group to form a ring-opening compound which can be then ring-closed on heating to reform the original dimer, so that the dimer can be used in the optical resolution of compounds containing these reactive functional groups. Derivatives of the (+)- or (-)-dimer are also very useful. For example, they are easily reacted with polynyiric alcohols or polyamines to form polyesters or polyamides, and the obtained optically active polymers can be used in asymmetric synthesis, optical resolution, analysis, etc. Further, we have found that when the obtained optically active isomer, i.e. (+)- or (-)-dimer, is reacted with a diamino compound, a novel optically active polymer can be obtained. Sne present invention is based on these findings. Disclosure of the Invention The present invention provides an optically active, anti head-to-head coumarin dimer of the following formula (I) or (II) : EMI3.1 Further, the present invention provides a process for preparing an optically active, anti head-to-head coumarin dimer of the following formula (I) or (II): EMI3.2 characterized by separating a diamide derived from the racemic, anti head-to-head coumarin dimer and an optically active amine into diastereomers, deaminating each of them and ring-closing the product. The method for obtaining the optically active dimer of the present invention is characterized in that a diarnide derived from the racemic, anti head-tohead coumarin dimer and an optically active amine is resolved into diastereomers, each diastereomer is deaminated and the product is ring-closed. The method involves steps represented by the following formulas: EMI4.1 EMI4.2 separation hydrolysis ring closure EMI5.1 The amidation reaction (a) readily proceeds when the dimer is mixed and reacted with the optically active amine in a solvent such as dioxane. The asides (A) and (B) are diastereomers and differ in solubility from each other. Therefore, when the reaction is carried out in an appropriate solvent under specified conditions, it is possible to precipi tate and separate only one diastereomer as the reaction proceeds. For example, when (-)-1-phenylethylamine is used as the anne, the amide derived from me (+)-dimer is difficultly soluble in dioxane, while the one derived from ibe (-)-dimer is easily soluble. Amino acid derivatives, alkaloid derivatives, etc. can also be used as the gamine in the present invention. The amide which is separated and purified by an appropriate method such as recrystallization can be hydrolyzed by any of conventional methods. For example, a method using alcoholic HC# is preferred. The hydrolyzate is ring-closed by a conventional lactonization method as such or, if necessary, after purification. For example, the ring closure is readily effected by heating in zcetic acid under reflux to form the (+)- or (-)-dimer. The polyamide of the present invention is different in optical properties as well as solubility, thermal properties, etc. from the corresponding racemic polyamide. The polyamide of the present invention contains highly reactive phenol groups in the molecule and the optical activity has a characteristic originating from the cyclobutane ring, so that the polyamide itself or its derivative which has a substituted phenol group or in which part of the cyclobutane rings are cleaved is a matarial suitable for use in asymmetric synthesis, optical resolution analysis, etc. The optically active polyamides of the present invention can be represented by the following formulas: EMI6.1 wherein A is a residue formed by removing one active hydrogen atom from each of two amino groups of a primary or secondary diamine. The diamine may be saturated or unsaturated. It may be a mixture of two or more diamines or modified with a triamine or the like. The polymer chain is usually terminated with either a hydrogen atom or the above dimer (I) or (II), and sometimes with an impurity. The polymers of the present invention are polycondensates, and n in the above formula is at leas 2, preferably from 2 to 1000. Examples of residue A in the above formula are as follows: EMI7.1 EMI8.1 The optically active polyamile of the present invention can be easily obtained by reacting the (+) or (-) anti head-to-head coumarin dinner with the corresponding diamine Usually, the reaction proceeds in the absence of a specific catalyst. Preferably, both reactants in equimolar quantities are reacted in an aprotic polar solvent. Preferred examples of the solvents include dimethylacetamide, dioxane, methyl- pyrrolidone, dimethyl sulfoxide and hexamethyl phosphoric triamide when the coumarin dimer and the diamine are used in a molar ratio of 1:1 in the above polymeriza- tion reaction, a polymer having a relatively high degree of polymerization can be obtained, while when the molar ratio is changed or a monofunctional com- pound such as a monoamine is added, a polymer having a relatively low degree of polymerization can be obtained. The following examples will further illustrate the present invention. Example 1 58.46 g of the (#)-dimer was dissolved in 850 m# of dioxane. 48.47 g of (-)-1-phenylethylamine was added dropwise thereto while stirring over a period of 30 min, After stirring for 12 hr, the precipitate was separated by filtration, washed with dioxane and dried at 600C in vacuo to afford 42.29 g of a crystal. The product was diamide (A) derived from the (+)-dimer and the yield was 39.5 %. After the filtrate was concentrated, 150 ma of acetone and 150 mS of methanol were added thereto arid the mixture was dissolved by heating and left to stand at 5 C for 12 hr. The precipitated crystal was dried to afford. 35.54 g (yield 33.3 %) of the diamide (B) derived from the (-)-dimer. The properties of these diamides A and B are shown in Table 1. Table 1 Melting @21*) Elemental analysis point [n]D (calcd.) (%) (.c). C 76.54 (76.38) Diamide A 237-238 -19.0 H 6.27 ( 6.40) N 5.17 ( 5.23) C 76.66 (76.38) Diamide B 246-247 - 177.30 H 6.16 (6.40) N 5.19 (5.23) c 0.5, 99% methanol Example 2 5.346.5 mg of the diamide of the (-)-dimer was added to a mixture of 100 m# of 99% ethanol and 50 m# of concentrated hydrochloric acid, and the mixture was refluxed. After 20'hr, the reflux was terminated and the mixture was concentrated to remove ethanol. 200 mQ of water was added thereto and the mixture was extracted three times with ethyl acetate (each 150 m#) After ethyl acetate was removed, 150 mS of acetic acid was added and the mixture was refluxed. The resulting material was developed on a silica gel column (Wakogel C-2C0, 4 6 x 15 cm) eluting with 500 me of benzene and then 500 m# of a mixture of benznee and ethyl acetate (90:10) successively to afford 2451.9 mg (yield 83.9 %) of the crude (-)-dimer crystal. This crude crystal was recrystallized from a solvent mixture of ethyl acetate and hexane (2:3) to afford 1.92 g (yield 65.7 ) of the (-)-dimer. Example 3 The diamide of the (+)-dimer was treated in a similar manner to that described in Example 2 to afford the (+)-dimer in a yield of 63.4 . The properties of these (+)- and (-)-dimers as well as those of the (#)-dimer as a reference are shown in Table 2. Table 2 Melting [&alpha;]21 *) [&alpha;]21 *) point D 435 ( C) (+)-Dimer 168-169 + 9.0 +66.0 (-)-Dimer 168.5-169 - 9,00 - 65.8 (#)-Dimer 187.5-189 - *) c 1.0, benzene Example 4 0.2552 g (0.9 mmol) of the (-) anti head-to-head coumarin dimer and an equimolar quantity of p-phenylene- diamine were dissolved in 1.7 m2 of dimethylacetamide and left to stand at 800C for 24 hr. After the completion of the reaction, tie product was added dropwise to methanol to afford a polymer (yield 87 %). The resulting polymer had a reduced viscosity of 0.36 (0.3 g/dS in dimethylacetamide at 30 c) and the optical activity was [a]D = - 89.4 and [&alpha;]435 = - 250.00 (0.5 g/100m# in dimethylacetamide). Example 5 The procedure of Example 4 was repeated except that 0.8 mmol of hexamethylanediamine was used as the diamine ar.d the reaction was carried out in 1.6 me of dimethylacetamide. The yield and the properties of the product are Example 6 2.1 mmol, of m-xylenediamine was used and the reaction was carried out in 4.3 m# of dimethylacetamide in a similar manner to that described above. The yield and the properties are shown in Table 3 Example 7 1 mmol of 4,4'-diaminodiphenyl ether was used and the reaction was carried out in 2.0 m# of dimethyl- acetamide in z similar manner to that described above. The yield and the properties are shown in Table 3. Example 8 1 mmol of piperazine was used and the reaction was carried out in 2.1 mS of dimethylacetamide in a similar manner to that described above. The yield and the properties are shown in Table 3. Table 3 Example Diamine Yield Reduced a) [&alpha;]D [&alpha;]435 No. (%) Viscosity .. .... 5 hexamethylenediamine 86 0.68 -59.0 b) -160.9 b) 6 m-xylylenediamine 86 0.63 -26.8 c) - 79.3 c) 7 4,4'-diaminiphenyl ether 65 0.31 -91.6 d) -266.7 d) 8 piperazine 97 0.51 +30.6 c) + 45.4 c) Note: (a) in dimethylacetamide, 0.3 g/d#, 30 C (b) in dimethylacetamide, 0.49 g/d# (c) in dimethylacetamide, 0.5 g/d# (d) in dimethylacetamide, 0.51 g/d#

Claims: WHAT IS CLAIMED IS: 1. An optically active, anti head-to-head coumarin dimer of the formula (I) or (II): EMI15.1 2. A process for preparing an optically active, anti head-to-head coumarin dimer of the formula (I) or (11): EMI15.2 with comprises separating diamides derived from a racemic, anti head-to-head coumarin dimer and an optically active amine into diastereomers, deaminating each diastereomer and ring-closing the product. 3. An optically active polyatnide of the formula (III) or (IV): EMI16.1 wherein A is a residue formed by removing one active hydrogen atom from each of two amino groups of a primary or secondary diamine. 4. A process for preparing an optically active polyamide of the formula (III) or (IV): EMI16.2 wherein A is a residue formed by removing one active hydrogen atom from each of two amino groups of a primary or secondary diamide; which comprises reacting an optically active7 anti head-to-head coumarin dimer with a primary or secondary diamine.

Inventors: KANOE, TOSHIO, SAIGOU, KAZUHIKO, SEKIMOTO, KAZUHIRO, YONEZAWA, NORIYUKI
Applicants: HASEGAWA, MASAKI
Application year: 1985
Main classification: C07D493
IPC codes: C07D493, C08G69