THERMALLY STABLE THERMOPLASTIC RESIN

Abstract: A heat stable thermoplastic epoxy resin is prepared by reacting together in the presence of a catalyst (a) an epoxy resin, (b) optionally, a polyhydric phenol, and (c) a monohydric phenol or alcohol, monocarboxylic acid or anhydride thereof, aliphatic or aromatic mono-secondary amines, mono-thiol, mono-isocyanate, water or combination thereof. The thermoplastic resin does not exhibit an excessive viscosity increase at elevated temperatures making it particularly suitable for use in highway marking paint applications.

Description: THERMALLY STABLE THERMOPLASTIC RESIN The present invention concerns thermoplastic resins and coatings prepared therefrom. Thermoplastic (non-thermoset) epoxy resins have been employed in the formulation of highway,. ■ pavement, marking- paints, as disclosed by J. M. Dale in DEVELOPMENT OF LANE DELINEATION WITH IMPROVED DURABILITY, Report No. FHWA-RD-75-70, July 1975. The paint formula¬ tions are maintained at elevated temperatures, about 450°F (232°C), during application. While they provide an excellent highway marking paint in terms of abrasive resistance, they are deficient in terms of applicability since they exhibit a substantial increase in viscosity while being maintained at the application temperature. The present invention provides a thermo- plastic resin which exhibits a much reduced viscosity increase at elevated temperatures, i.e. more stable. The present invention pertains to a thermally stable, thermoplastic resin prepared by reacting (A) at least one epoxy resin having an average of more than one vicinal epoxy group per molecule; (B) optionally, one or more polyhydric phenols; and (C) at least one material selected from monohydric phenols and alcohols, mono¬ carboxylic acids and anhydrides thereof, aliphatic and aromatic mono-secondary amines, mono-thiols, mono-isocyanates, water and combinations thereof; in the presence of an effective quantity of a suitable catalyst and wherein components (A), (B) and (C) are reacted in quantities which provide an equivalent ratio of component (B) to component (A) of from 0:1 to 0.95:1, preferably from 0.3:1 to 0.9:1, most preferably from 0.45:1 to 0.85:1 and an equivalent ratio of component (C) to component .(A) of from 0.87:1 to 1.1:1, prefer¬ ably from 0.93:1 to 1.05:1, most preferably from 0.95:1 to 1:1, and wherein the equivalent ratio of components (B+C) to component (A) is from 0.87:1 to 1.96:1, prefer- ably from 0.93:1 to 1.95:1, most preferably from 0.95:1 to 1.85:1. The thermoplastic resin of the present inven¬ tion is suitable for incorporation in a paint formula¬ tion comprising (A) the aforementioned thermally stable thermoplastic resin; and (B) at least one of (1) one or more pigments or dyes; and (2) one or more fillers. Suitable epoxy resins which can be employed in the process of the present invention include, for example, those represented by the formulas IV. wherein each A is independently a divalent hydrocarbyl group having from 1 to 10, preferably from 1 to 0 0 0 II II II 6 carbon atoms, -S-, -S-S-, -S-, -S-, -C-, -O-C-O- II 0 or -0-; each A' is independently a divalent hydrocarbyl group having from 1 to 10, preferably from 1 to 6 carbon atoms; each R is independently hydrogen or a hydrocarbyl group having from 1 to 4 carbon atoms; R 1 is hydrogen or a hydrocarbyl group having from 1 to 10, preferably from 1 to 6 carbon atoms; each X is inde¬ pendently hydrogen, a halogen, preferably chlorine or bromine, or a hydrocarbyl group having from 1 to 12 carbon atoms; n has a value of zero or 1; n' has an average value of from zero to 15, preferably from zero to 11.5; m has an average value of from 0.001 to 6, preferably from 0.1 to 3; and m' has an average value of from zero to 4, preferably from 0.1 to 2. Particularly suitable epoxy resins include, for example, * the glycidyl ethers of polyhydric phenols such as resorcinol, catechol, hydroquinone, bisphenol A, bisphenol F, bisphenol K, tris-hydroxyphenyl methane, and mixtures thereof. Suitable polyhydric phenolic compounds which can be employed herein include, for example, those represented by the formulas V. wherein A, A', R' , X, n and ' m are as hereinbefore defined. Particularly suitable polyhydric phenolic materials include, for example, resorcinol, catechol, hydroquinone, bisphenol A, bisphenol F, bisphenol K, tris-hydroxyphenyl methane, and mixtures thereof. Suitable monohydric phenolic compounds include, for example, those represented by the formula and each X is as hereinbefore defined. Particularly suitable monohydric phenolic materials include, for example, phenol, alkylphenols, such as nonylphenol and t-butylphenol, cresol, and mix¬ tures thereof. Suitable monohydric alcohols which can be employed herein include, for example, methanol, ethanol, propanol, isopropanol, butanol, pentanol, hexanol, ethylene glycol monomethyl ether, propylene glycol monomethyl ether, ethylene glycol monoethyl ether, propylene glycol monoethyl ether, and com¬ binations thereof. Suit-able monocarboxylic acids which can be employed herein include, for example, acetic acid, propionic acid, butyric acid, valeric acid, caproic acid, caprylic acid, capric acid, lauric acid, myristic acid, palmitic acid, stearic acid, oleic acid, phenyl- acetic acid, toluic acid, and combinations thereof. Suitable anhydrides of monocarboxylic acids which can be employed herein include, for example, acetic anhydride, propionic anhydride, butyric anhy¬ dride, valeric anhydride, and combinations thereof. Suitable mono-secondary amines which can be employed herein include, for example, dimethyl amine, diethyl amine, methyl ethyl amine, dibutyl amine, methyl butyl amine, ethyl butyl amine, and combinations thereof. Suitable mono-thiols which can be employed herein include, for example, propanthiol, butanethiol, pentanethiol, hexanethiol, dodecanethiol, thiocresol, and combinations thereof. Suitable mono-isocyanates which can be employed herein include, for example, ethyl isocyanate, propyl isocyanate, butyl isocyanate, phenyl isocyanate, tolyl isocyanate, and combinations thereof. Suitable catalysts for effecting the reaction between the epoxy resin and the phenolic hydroxyl- containing materials include, for example, those disclosed in U.S. Pat. Nos. 3,306,872; 3,341,580; 3,379,684; 3,477,990; 3,547,881; 3,637,590; 3,843,605; 3,948,855; 3,956,237; 4,048,141; 4,093,650; 4,131,633; 4,132,706; 4,171,420; 4,177,216 and 4,366,295. Particularly suitable catalysts are those quaternary phosphonium. and ammonium compounds such as, for example, ethyltriphenylphosphonium chloride, ethyl- triphenylphosphonium bromide, ethyltriphenylphosphonium iodide, ethyltriphenylphosphonium acetate, ethyltriphenyl¬ phosphonium diacetate (ethyltriphenylphosphonium acetate*acetic acid complex), tetrabutylphosphonium chloride, tetrabutylphosphonium bromide, tetrabutylphos- phonium iodide, tetrabutylphosphonium acetate, tetra¬ butylphosphonium diacetate (tetrabutylphosphonium acetate*acetic acid complex), butyltriphenylphosphonium tetrabromobisphenate, butyltriphenylphosphonium bisphenate, butyltriphenylphosphonium bicarbonate, benzyltri ethyl- ammonium chloride and tetramethylammonium hydroxide. Other suitable catalysts include tertiary amines such as, for example, triethylamine, tripropylamine, tributylamine, 2-methylimidazole, benzyldimethylamine, N-methyl morpholine, and mixtures thereof. Suitable pigments which can be employed herein include any which will provide the coating with the desired color such as, for example, titanium dioxide, lead chromate, zinc chromate, chome green, pthalocyamine green and blue, iron oxide, and combinations thereof. Suitable fillers which can be employed herein include, for example, calcium carbonate, talc, glass beads, powdered or flaked zinc or alumina, powdered or flaked glass, colloidal silica, and combinations thereof. The following examples are illustrative of the present invention, but are not to be construed as to limiting the scope thereof in any manner. EXAMPLE 1 A. Preparation of Capped Epoxy Resiii To a reaction vessel equipped with a means for stirring and temperature control was added 37.1 lbs (16.8 kg, 10.2 gram epoxy equiv. ) of a diglycidyl ether of bisphenol A having an average epoxide equivalent, weight (EEW) of 1646, 18 lbs (8.2 kg, 43.8 gram epoxy equivalents) of a diglycidyl ether of bisphenol A having an average EEW of 187, 23 lbs (10.4 kg, 47.3 gram hydroxyl equiv.) of nonyl phenol and 0.077 lbs (0.169 kg) of a 70 percent solution of ethyltriphenyl phosphonium acetate*acetic acid complex in methanol. The mixture was heated to 160°C at a rate of 1.5°C/min. (0.025°C/s) and maintained thereat for 2 hours (7200 s). The resultant product was a colorless to pale yellow resin, solid at room temperature. B- Preparation of Traffic Marking Paint A mixture was prepared at 200°C of the follow¬ ing components: 1. 100 parts by weight of the resin from (A) above 2. 20 parts by weight of Ti0 2 3. 20 parts by weight of CaC0 3 4. 28 parts by weight of 200 mesh (0.074 mm sieve opening) glass beads Components 1, 2 and 3 were mixed under high shear conditions. Component 4 was mixed at low speeds. The properties of the traffic paint formula- • tion are given in the following Table. For comparative purposes, a similar paint formulation was prepared from an epoxy resin mixture without nonyl phenol capping. The formulation was as follows: 1. 40 parts by weight of a diglycidyl ether of bisphenol A (DGEBA) having an epoxy equivalent weight (EEW) between 186 and 192 2. 60 parts by weight of a DGEBA having an EEW between 1600 and 2000 3. 20 parts by weight of Ti0 2 4. 20 parts by weight of CaC0 3 5. 28 parts by weight of 200 me.sh (0.074 mm sieve opening) glass beads The properties are given in the following Table. TABLE Formulation Formulation 1-B 1-C Present Invention Comparative Mettler Softening Point, °C 89 77 Cold flow at 25°C No Yes Initial Viscosity @ 450°F (232°C), cps/pa*s 505/0.505 480/0.480 Viscosity after 8 hours (28800 s) at 450°F (232°C), cps/pa*s 510/0.51 1500/1.5 Condition after 24 hours (86400 s) at 450°F (232 !°°CC)) slight gelled, yellowing brown EXAMPLE 2 A ' . Preparation of Non-Capped Epoxy Resin Blend (Epoxy Resin Blend) To a reaction vessel equipped with a means for stirring, nitrogen purge and temperature control was added 725.2 g (3.9 epoxy equiv.) of a diglycidyl ether of bisphenol A having an average epoxide equiva¬ lent weight (EEW) of 186 and 374.8 g (3.29 equiv.) of bisphenol A. The mixture was then heated to 90°C at which time 1.69 g (0.003 mole) of a 70 percent solution of ethyltriphenyl phosphonium acetate*acetic acid complex in methanol was added. The temperature was increased to 150°C and then the reaction mass exothermed to 206°C. The temperature was maintained at 190°C for 1 hour (3600 s). The percent epoxide was 2.48. To this material was added 528.4 g (2.84 epoxy equiv.) of a diglycidyl ether of bisphenol A having an average EEW of 186. The temperature of the mixture was decreased to 150°C. This product had a percent epoxide of 9.1 (473 EEW). B. Preparation of Capped Epoxy Resin To a reaction vessel equipped with a means for stirring and temperature control was added 180 g (0.38 epoxy equiv.) of epoxy resin blend prepared in A above and 76.2 g (0.38 mole) of lauric acid. The mixture was heated to 90°C whereupon 0.21 g (0.0004 mole) of a 70 percent solution of ethyltriphenyl phos¬ phonium acetate*acetic acid complex in methanol was added. The temperature was increased to 156°C and maintained at about 155°C for 1.5 hours (5400 s). The product was dried in a vacuum oven at 160°C for 2 hours (7200 s). The product had a viscosity of 74.5 cps (0.0745 pa-s) at 450°F (232°C) and a softening point of 60.1°C. EXAMPLE 3 To a reaction vessel equipped with a means for stirring and temperature control was added 150 g (0.32 epoxy equiv.) of epoxy resin blend prepared in Example 2A and 100 g (1.35 mole) of n-butanol. The mixture was heated to 50°C whereupon 0.3 g. (0.002 mole) of boron trifluoride etherate was added. The temper¬ ature was increased to 60°C and maintained between 60° and 63°C for 3.17 hours (11412 s), heated to 200°C and vacuum stripped for 2.08 hours (7488 s). The product was dried in a vacuum oven at 160°C for 2 hours (7200 s) The product had a viscosity of 189.5 cps (0.1895 pa*s) at 450°F (232°C) and a softening point of 78°C. EXAMPLE 4 To a high pressure reaction vessel equipped with a means for stirring, nitrogen purge and tempera¬ ture control was added 200 g (0.42 epoxy equiv.) of epoxy resin blend prepared in Example 2A, 200 g (2.77 moles) of methyl ethyl ketone, 43 g (2.39 moles) of water, 1.7 g (0.003 mole) of a 70 percent solution of ethyltriphenyl phosponium acetate*acetic acid complex in methanol and 2.09 g (0.016 mole) of oxalic acid*2H 2 0. Reactor was purged with nitrogen and then pressure increased to 80 psig (552 kPa gage). The reactor temperature was increased to 135°C and maintained for about 4.5 hours (16200 s) then the temperature was increased to 145°C and maintained for 5 hours (18,000 s) The excess volatiles were removed in the reaction vessel at a temperature of about 200°C for about 0.25 hour (900 s). The product was dried in a vacuum oven at 160°C for 2 hours (7200 s). The product had a viscosity of 362 cps (0.362 pa-s) at 450°F (232°C) and a softening point of 106.6°C. EXAMPLE 5 To a reaction vessel equipped with a means for stirring and temperature control was added 50 g of propylene glycol monomethyl ether acetate and 13.6 g (0.105 mole) of dibutylamine. Over a period of 1 hour (3600 s) added 100 g (0.106 epoxy equiv.) of a 50 percent solution of epoxy resin blend prepared in Example 2A. The temperature was increased to 140°C and maintained for 2 hours (7200 s). The temperature was increased to about 200°C for about 0.25 hour (900 s) to remove the solvent. The product was dried in a vacuum oven at 160°C for 2 hours (7200 s). The product had a viscosity of 100.5 cps (0.1005 pa-s) at 450°F (232°C) and a softening point of 72.4°C. EXAMPLE 6 To a reaction vessel equipped with a means for stirring and temperature control was added 97 g of propylene glycol monomethyl ether acetate, 8 g (0.078 mole) of acetic anhydride, 70 g (0.074 epoxy equiv.) of a 50 percent solution of epoxy resin blend prepared in Example 2A in propylene glycol monomethyl ether acetate and 0.25 g (0.0009 mole) of a 70 percent solution of ethyltriphenyl phosphonium acetate-acetic acid complex in methanol. The temperature was increased to 120°C and maintained for 5.2 hours (18,720 s). A portion of the solvent was removed by heating at 145°C for about 0.5 hour (1800 s). The resultant material was then placed on a hot plate for 1 hour (3600 s) at 206°C. The product was dried in a vacuum oven at 160°C for 2 hours (7200 s). The product had a viscosity of 154 cps (0.154 pa-s) at 450°F (232°C) and a softening point of 79.5°C. EXAMPLE 7 To a reaction vessel equipped with a means for stirring and temperature control was added 84 g of Dowanol PM acetate, 8.5 g (0.082 mole) of 1-pentane- thiol, 70 g (0.074 epoxy equiv.) of a 50 percent solu- tion of epoxy resin blend prepared in Example 2A in propylene glycol monomethyl ether acetate and 0.25 g (0.0009 mole) of a 70 percent solution of ethyltri¬ phenyl phosphonium acetate*acetic acid complex in methanol. The temperature was increased to 100°C and maintained for 3.55 hours (12,780 s). An additional 2 g (0.019 mole) of 1-pentanethiol and 0.25 g (0.0009 mole) of ethyltriphenyl phosphonium acetate*acetic acid complex solution was added. After 2.5 hours (9000 s) an additional 0.25 g (0.0009 mole) of ethyltriphenyl phosphonium acetate*acetic acid complex solution was added. After 1 hour (3600 s) an additional 2 g (0.019 mole) of 1-pentanethiol and 0.25 g (0.0009 mole) of ethyltriphenyl phosphonium acetate*acetic acid complex was added. The temperature was maintained for 1 hour (3600 s) at 100°C and then increased to about 150°C for about 1 hour (3600 s) to remove solvent. The product was dried in a vacuum oven at 160°C for 2 hours (7200 s) The product had a viscosity of 119 cps (0.119 pa*s) at 450°F (232°C) and a softening point of 72.4°C. EXAMPLE 8 To a reaction vessel equipped with a means for stirring, nitrogen purge and temperature control was added 200 g (0.423 epoxy equivalent) of epoxy resin blend prepared in Example 2A, 49.5 g (0.416 mole) of phenyl isocyanate. The temperature was maintained between 130° and 145°C. The phenyl isocyanate addition took 0.73 hour (2628 s). After 0.77 hour (2772 s), 0.75 g- (0.0022 mole) tetrabutylphosphonium bromide in 2.5 g of methanol was added. The temperature was increased to 155°C and maintained between 155° and 160°C for 6.75 hours (24,300 s). The product was dried in a vacuum oven at 160°C for 2 hours (7200 s). The product had a viscosity of 670 cps (0.67 pa-s) ' at 450°F (232°C) and a softening point of 123.5°C. EXAMPLE 9 To a reaction vessel equipped with a means for stirring, condensing and temperature control was added 50 g (0.106 epoxy equivalent) of epoxy resin blend prepared in Example 2A and 150 g (1.531 mole) of cyclohexanone. The temperature was increased to 90°C to dissolve the epoxy resin blend then cooled to 45°C, whereupon 12 g (0.375 mole) of methanol was added. The temperature was decreased to 33°C in 0.75 hour (2700 s) then 12.2 g (0.103 mole) of phenyl isocyanate was added. The temperature was increased to 45°C, then 0.12 g (0.0004 mole) of tetrabutylphosphonium bromide in 1 g (0.031 mole) of methanol was added. The tem¬ perature was increased to 145°C and maintained for 2.17 hours (7812 s). Then solvent was removed at 150°C for 0.75 hour (2700 s). The resultant material was placed on a hot plate for 1.5 hours (5400 s) at 208°C. The product was dried in a vacuum oven at 160°C for 2 hours (7200 s). The product had a viscosity of 2520 cps (2.52 pa-s) at 450°F (232°C) and a softening point of 128.3°C. The uncapped epoxy resin blend of Example 2A and the capped epoxy resins prepared in Examples 5, 6 and 8 were subjected to a thermal stability test. The results are given in the following Table. THERMAL STABILITY TEST Test Temperature 450°F (232°C) VISCOSITY EPOXY RESIN TIME AT 450°F (232°C) cps/pa*s Epoxy Resin Blend Initial 211/0.211 8 hours (28,800 s) 495/0.495 Example 5 Initial 100.5/0.1005 7.5 hours (27,000 s) 133.5/0.1335 Example 6 Initial 154/0.154 7 hours (25,200 s) 173/0.173 Example 8 Initial 670/0.670 8 hours (28,800 s) 684/0.684

Claims: 1. A thermally stable, thermoplastic resin prepared by reacting in the presence of an effective quantity of a suitable catalyst (A) at least one epoxy resin having an average of more than one vicinal epoxy group per molecule; (B) optionally at least one polyhydric r phenol; and (C) at least one material selected from monohydric phenols and alcohols, mono¬ carboxylic acids and anhydrides thereof, aliphatic and aromatic mono-secondary amines, mono-thiols, mono-isocyanates, water and combinations thereof; wherein components (A), (B) and (C) are reacted in quantities which provide an equivalent ratio of compo¬ nent (B) to component (A) of from 0:1 to 0.95:1 and an equivalent ratio of component (C) to component (A) of from 0.87:1 to 1.1:1 and wherein the equivalent ratio of components (B+C) to component (A) is from 0.87:1 to 1.96:1. 2. A resin composition of Claim 1 wherein (i) the epoxy groups contained in component (A) are glycidyl ether groups; (ii) the equivalent ratio of component (B) to component (A) is from 0.3:1 to 0.9:1; (iii) the equivalent ratio of component (C) to component (A) is from 0.93:1 to 1.05:1; and (iv) the equivalent ratio of components (A+B) to component (A) is from 0.93:1 to 1.95:1. 3. A resin composition of Claim 2 wherein (i) the equivalent ratio of component (B) to component (A) is from 0.45:1 to 0.85:1; (ii) the equivalent ratio of component ' (C) to component (A) is from 0.95:1 to 1:1; and (iii) the equivalent ratio of gomponents (B+C) to component (A) is from 0.95:1 to 1.85:1. 4. A resin composition of Claim 1 wherein (i) component (A) is an epoxy resin or a mixture of epoxy resins represented by formulas (I), (II), (III) or (IV) in the specification wherein each A is indepen¬ dently a divalent hydrocarbyl group having from 1 to 10 carbon atoms, O O O 0 II It II II -S-, -S-S-, -S-, -S-, -C-, -0-C-O- or -0-; II 0 each A' is independently a divalent hydrocarbyl group having from 1 to 10; each R is independently hydrogen or a hydrocarbyl group having from 1 to 4 carbon atoms; R' is hydrogen or a hydro¬ carbyl group having from 1 to 10 carbon atoms; each X is independently hydrogen, a halogen, or a hydrocarbyl group having from 1 to 12 carbon atoms; n has a value of zero or 1; n 1 has an average value of from zero to 15; m has an average value of from 0.001 to 6; and m' has an average value from 0 to 4; (ii) component (B) is a polyhydric phenolic compound or mixture of such compounds represented by formulas (V), (VI), (VII) or (VIII) in the specification wherein A, A'-, R' , X, n and m are as defined above; and (iii) component (C) is selected from mono¬ hydric phenolic compounds represented by formula (IX) in the specification wherein each X is as defined above, aliphatic alcohols, monocarboxylic acids, water or combinations thereof. 5. A resin composition of Claim 4 wherein (i) component (A) is one or more epoxy resins represented by formula (II) wherein A is a divalent hydrocarbon group having from 1 to 10 carbon atoms, each X is hydrogen or a halogen atom, n has a value of 1 and n' has an average value from 0.035 to 12; (ii) component (B) is one or more polyhydric phenolic compounds represented by formula VI; and (iii) component (C) is selected from nonyl phenol, n-butyl alcohol, lauric acid, water or combinations thereof. 6. A resin composition of Claim 5 wherein (i) component (A) is a mixture of an epoxy resin wherein n' has an average value of from 0.01 to 0.05 and an epoxy resin wherein n has an average value of from 2 to 15; (ii) component (B) is bisphenol A; and (iii) component (C) is nonyl phenol. 7. A paint formulation comprising (A) a thermally stable resin of Claim 1; and (B) at least one of (1) one o more pigments or dyes; and (2) one or more fillers.

Inventors: BEASLEY CHRISTOPHER V, CAVITT MICHAEL B, BEASLEY, CHRISTOPHER, V., CAVITT, MICHAEL, B.
Applicants: DOW CHEMICAL CO, THE DOW CHEMICAL COMPANY
Application year: 1985
Main classification: C08L63
IPC codes: C08G18, C08G59, C09D163