METHOD FOR ETCHING ELECTRODE FOILS FOR AN ALUMINIUM ELECTROLYTIC CAPACITOR

Abstract: A method for electrolytically etching an aluminium foil for use as an electrode of an aluminium electrolytic capacitor is described. In the method, an aluminium foil is electrolytic­ ally etching an on the surfaces thereof in a 3 to 25% hydrochloric acid solution containing aluminium chloride by application of an AC current. The AC current has a waveform each cycle of which consists of positive and negative half cycles and an OFF time interval between the respective half cycles at which the AC current becomes zero whereby a size of pits formed by the etching is suitably controlled.

Description: Background of the invention Field of the invention This invention relates to a method for etching an electrode foil for aluminium electrolytic capacitors. Description of the prior art As is well known in the art, aluminium electrolytic capacitors are fabricated by convolutely winding aluminium electrode foils and an insulative paper intervening between the foils and dipping the winding in an electrolytic solution. In order to increase an electrostatic capacitance per unit area of the electrode foil, the foil used is etched to form pits on the surfaces thereof so as to increase the surface area. A recent development of IC, LSI and the like demands electrolytic capacitors which are smaller and thinner in size. This in turn requires an increasing electrostatic capacitance per unit area of the electrode foil. In a known method of etching electrode foils for use in aluminium electrolytic capacitors, an AC current having a sine or rectangular waveform as shown in Fig. 1a or 1b is used for etching while making use of high strength of the aluminium foil. this is described, for example, in Japanese Laid-open Patent Application 58-22390. With known waveforms such as sine wave, rectangular wave and the like in which no OFF time exists, it is difficult to control, by etching, an optimum pit diameter (i.e. a diameter of irregularities caused by etching) which varies according to the formation voltage. For presecuting further miniaturization of aluminium electrolytic capacitors, the known method is disadvantageous in that a ratio of an electrostatic capacitance per unit area of electrode foil after etching to an electrostatic capacitance per unit area of electrode foil before etching is unsatisfactory. This ratio may be hereinafter referred to simply as "capacitance ratio". Document DE 31 27 330 A1 also discloses a method for electrolytically etching an aluminium foil for use as an electrode of an aluminium electrolytic capacitor by use of an AC current. According to this prior art higher capacitance values of the etched aluminium can be obtained by controlling the AC current with respect to the increase and decrease speed of the current intensity which can be both higher or lower than zero. The AC current has a symmetrical waveform wherein the current rises rapidly from zero to a maximum, then subsequently decreases rapidly to an intermediate value and thereafter decreases slowly to zero. Thereafter, the current rises and falls in the opposite direction with the same waveform. Document US-A-3 085 950 discloses another method for electrolytically etching aluminium foils particularly for electrolytic capacitors, in which no AC current, but a pulsating DC current is used. The etching of the aluminium foil depends thereby from the determination of a suitable pulse frequency. Furthermore, the specific type of the electrolyte to be used in this prior art is of particular importance. From document DE 30 20 420 A1 a method for electrolytically roughening the surface of an aluminium plate serving as a support for a lithographic printing plate is known, in which also an AC current is used. The AC current used here has so-called intermission periods in which voltage and current intensity are equal to zero. Hereby it is essential that for achieving the desired roughness of the aluminium surface the quantity of electricity flowing during the anode phase is larger than the quantity of electricity flowing during the cathode phase. In addition to the use of different voltages the intermission periods are provided for the different control of the quantity of electricity flowing during the anode and cathode phase, wherein the quantity of electricity is adjusted to a desired value by the duration of a voltageless, respectively currentless intermission period. Hereby it is irrelevant where the intermission period lies and how long it lasts. SUMMARY OF THE INVENTION It is accordingly an object of the invention to provide a method for electrolytically etching an aluminium foil for use as an electrode of an aluminium electrolytic capacitor in which the foil is more efficiently etched and thus has an improved electrostatic capacitance per unit area. It is further object of the invention to provide such a method for electrolytically etching an aluminium foil to ensure a larger surface area than prior art methods, so that an aluminium electrolytic capacitor can be suitably miniaturized and can be fabricated at a lower cost. The invention provides a method for electrolytically etching an aluminium foil for use as an electrode of an aluminium electrolytic capacitor, comprising electrolytically etching an aluminium foil on the surfaces thereof in a 3 to 25 % hydrochloric acid solution containing aluminium chloride at a temperature of 20° to 60° C by application of an AC current wherein the aluminium foil is placed between and in parallel to a pair of equally spaced electrodes in said hydrochloric solution, and the AC current is applied across the paired electrodes without direct application to the aluminium foil to etch the foil, said AC current having a waveform which has each cycle consisting of identical positive and negative half cycles in the form of a sine, rectangular or trapezoidal wave with or without ripples during the ON time intervals and an OFF time interval between the half cycles at which the AC current becomes zero, wherein each OFF time interval at which the AC current becomes zero is in the range of 2 to 30 ms and each ON time interval at which the AC current is passed is in the range of 10 to 100 ms, whereby a size of pits formed by the etching is suitably controlled. Brief description of the invention Figs. 1a and 1b are, respectively, sine and rectangular waveforms of an etching current used in a known etching method; Figs. 2a and 2b are, respectively, sine and rectangular waveforms of an etching current including OFF time intervals according to the invention; and Fig. 3 is a graphical representation of the relation between formation voltage and electrostatic capacitance for different OFF time intervals. Detailed description and embodiments of the invention According to the method of the invention, an aluminium foil is electrolytically etched in a hydrochloric acid solution containing aluminium chloride at a temperature of the solution of 20 to 60°C. The hydrochloric acid solution has an HCl concentration of 3 to 25%. Aluminium chloride is generally used in an amount of 1 to 10% by weight of the solution. In the practice of the invention, an AC current is used and applied for the etching. The AC current should have such a waveform whose one complete cycle consist of positive and negative half cycles and an interval between the half cycles at which the AC current becomes zero. When the etching of an aluminium foil is conducted using the AC current as described above, fine irregularities or pits are formed on the surfaces of the aluminium foil during the ON time intervals. However, the etching or chemical corrosion, which proceeds in the hydrochloric acid solution, can be suitably controlled by controlling the length of each OFF time interval during which no etching current is passed. Thus, it becomes possible to make an optimum pit diameter according to the formation voltage. The resultant aluminium foil has an increasing capacitance ratio. For the optimum electrolytic etching, it is necessary to optimumly control the chemical corrosion which proceeds in the hydrochloric solution during the OFF time, in accordance with the distribution and size of the individual pits formed by chemical etching during the ON time. In other words. the ON and OFF times have an optimum relation in order to form a desired pit diameter. For instance, if the OFF time is increased tog much, the pit diameter becomes too large, leading to a lowering of electrostatic capacitance. According to our experiment, it has been found that the individual OFF time at which the etching current is kept zero is in the range of from 2 to 30 ms., and the ON time is in the range of from 10 to 100 ms. The current during the ON time in complete cycles may be in the form of a sine, rectangular and trapezoidal wave with or without ripples. In Figs. 2a and 2b, there are, respectively, shown sine and rectangular waveforms inclusing an OFF time between the half cycles. Preferably, the etching is effected in such a way that the aluminium foil is placed in the hydraulic acid solution between and in parallel to a pair of equally spaced electrodes and the AC current is applied across the paired electrodes without direct application of the current to the aluminium foil. This is very suitable for the production of a uniformly etched aluminium foil and contributes to reduce troubles such as breakage of the foil and formation of defects on the foil as will be produced by direct application of the current to the foil. As a matter of course, the etching may be effected continuously or in a batchwise manner. The present invention is more particularly described by way of example. Example Aluminium foils were etched in a hydrochlorid acid solution under the following conditions. Etching solution: 5% HCl solution containing 2 % AlCl₃. Aluminium foil: 4N O Al material having a purity of 99.99°/a and softened by annealing. Etching temperature (solution temp.): 40°C. Etching time: 5 minutes. Etching current waveform: sine wave of an ON time of 50 ms and an OFF time of (a) nil, (b) 10 ms. or (c) 20 ms. The relationship between formation voltage and electrostatic capacitance of each etched aluminium foil is shown in Fig. 3. As will be seen from curves a, b and c of the Figure, the electrostatic capacitance attained by etching using the waveforms (b) and (c) having of times according to the invention is higher by 20 to 100% than in the case of the known waveform a which is free of any OFF time. A longer OFF time results in a larger pit diameter, so that the difference in electrostatic capacitance between the invention and the prior art becomes more significant at a higher formation voltage. In the above example, the etching solution was a 5% hydrochloric acid solution and similar results were obtained when the concentration of HCl was in the range of 3 to 25%. Also, similar results were obtained when the concentration of aluminium chloride was in the range of 1 to 10% by weight. When using an aluminium foil having a higher capacitance ratio, aluminium electrolytic capacitors can be beneficially miniaturized with a reduced cost.

Claims: A method for electrolytically etching an aluminium foil for use as an electrode of an aluminium electrolytic capacitor, comprising electrolytically etching an aluminium foil on the surfaces thereof in a 3 to 25 % hydrochloric acid solution containing aluminium chloride at a temperature of 20 to 60° by application of an AC current wherein the aluminium foil is placed between and in parallel to a pair of equally spaced electrodes in said hydrochloric solution, and the AC current is applied across the paired electrodes without direct application to the aluminium foil to etch the foil, said AC current having a waveform which has each cycle consisting of identical positive and negative half cycles in the form of a sine, rectangular or trapezoidal wave with or without ripples during the ON time intervals and an OFF time interval between the half cycles at which the AC current becomes zero, wherein each OFF time interval at which the AC current becomes zero is in the range of 2 to 30 ms and each ON time interval at which the AC current is passed is in the range of 10 to 100 ms, whereby a size of pits formed by the etching is suitably controlled.

Inventors: JUJO, AKIHIRO, KANZAKI, NOBUYOSHI, KOJIMA, KOICHI, OKABAYASHI, MASANORI, SHIMATANI, RYOICHI, TOYAMA, KENJI
Applicants: MATSUSHITA ELECTRIC INDUSTRIAL CO., LTD.
Application year: 1985
Main classification: C25F3
IPC codes: C25D11, C25F3, H01G9