USE OF SCAVENGERS FOR THE REMOVAL OF IMPURITIES FROM INERT FLUIDS

Abstract: Disclosed are macroreticulate polymers which are use­ ful in scavenging Lewis acid and oxidant impurities from inert fluids. The macroreticulate polymers of this invention contain a plurality of metallated functional groups or mix­ tures of metallated functional groups where the function groups correspond to the general formula: where Ar is an aromatic hydrocarbon radical containing from one to three rings; R is selected from the group con­ sisting of alkyl hydrocarbon radicals, benzophenone radi­ cals, salts of benzophenone, fluorenone radicals and salts of fluorenone; and M is selected from the group consisting of lithium, potassium, sodium, alkyl magnesium, and alkyl zinc. Impurities are readily removed from such inert fluids by contacting the fluids with the macroreticulate polymer and then separating the fluids from the scavenger.

Description: This invention relates to organo-metallic polymers used to scavenge oxidants and Lewis acids from inert fluids (both liquids and gases), their preparation, and use. In numerous products and processes the purity of fluids is of critical importance. Often, the presence of even small amounts of Lewis acid or oxidant impurities will dramatically reduce the utility of a fluid. Among the known methods for purification of inert fluids is the use of scavengers. With this method, a fluid is passed over a scavenger that reacts with and removes impurities without affecting the fluid itself. For example, the fluid may be passed through a bed or column containing the scavenger. U.S. Patents 3,079,428 and 3,316,223 disclose processes for scavenging acidic impurities from organic liquids by contacting the liquids with an insoluble polymeric anionic material. However, there is a continuing need for new and better ways of purifying such fluids. Among the properties that are desired in a good scavenger are the ability to remove a wide variety of impurities and to insure that the remaining level of impurities is low, as well as the capacity to remove high levels of impurities. Furthermore, it is desirable that a scavenger should be effective not only when swollen by the liquid to be purified, but also that it should be effective with liquids and gases that cannot swell the scavenger. For many applications, it is also desirable that the scavenger should have "uniform loading", that is, some of its reactive sites should not be more reactive than others. If a scavenger does not have uniform loading, it will not behave consistently throughout its lifetime, thereby making it difficult to predict how the scavenger will perform at any particular time. It is also desirable that the scavenger should have good thermal stability, and that it should change color as it becomes exhausted, so that the need for replacement is readily determinable. U.S. Patents 4,256,840 and 4,297,220 describe "macroreticulate" copolymers, including a styrene-divinylbenzene copolymer, that are adsorbents for fluids and act as ion-exchange resins. They do not disclose the treatment of such polymers to make them capable of removing acidic and oxidant impurities from fluids. The term "macroreticulate" as applied to a polymer backbone means that it must possess a porous and adsorbent reticular structure even in nonswelling fluids. All cross-linked polymers, including copolymers and terpolymers, have what is called "micro-porosity", namely, molecular-sized openings between polymer chains. Macroreticulate polymers also have larger pores between agglomerates of minute polymer particles. These provide larger surface area and reactive sites not only when the polymers are swollen by liquid, but also in liquids and gases that cannot swell polymers. Chemical and Engineering News, November 15, 1982, p. 15, discloses that "functionalized" polystyrene divinyl-benzene, including lithiated polystyrene divinylbenzene, may be used as a catalyst support. Taylor, Macromolecules, 14, (1981), pp. 1134-1135, discloses also the treatment of swollen poly(styrene-divinylbenzene) with n -butyl lithium to form an intermediate in the preparation and halogenation of silylated polystyrene. Bates et al., Macromolecules, 14, (1981), pp. 881-883 discloses the treatment of a divinylbenzene gel with n -butyl lithium to detect the presence of vinyl groups in the gel. None of these references discloses means for removing acidic and oxidant impurities from fluids through the use of porous or "macroreticulate" polymers. According to the invention, all of the desirable properties for a scavenger as discussed above are found in polymeric scavengers having a macroreticulate polymer backbone having pendant aromatic groups, that are characterized in that the said groups are metallated functional groups that have the general formula: where Ar is an aromatic hydrocarbon radical containing from one to three rings, R₁ and R₂ are the same or different and are selected from the group consisting of hydrogen, alkyl hydrocarbon radicals containing from 1 to 13 carbon atoms, methylene-bridged benzophenone radicals, alkali or alkaline earth metal salts of methylene-bridged benzophenone, methylene-bridged fluorenone radicals and alkali or alkaline earth metal salts of methylene-bridged fluorenone; and M is selected from the group consisting of lithium, potassium, sodium, alkyl magnesium, and alkyl zinc, where the alkyl groups are alkyl hydrocarbon radicals containing from 1 to 12 carbon atoms. If R₁ and R₂ are alkyl hydrocarbon radicals they may be, for instance, methyl, or ethyl, or the various isomers of propyl, butyl, pentyl, hexyl, octyl, decyl and dodecyl. The preferred alkyl hydrocarbon radicals are pentyl radicals. The macroreticulate polymer scavengers used according to the invention may be synthesized by metallating pendant aromatic vinyl groups in macroreticulate polymers, by addition across the double bond, to produce pendant groups having the more specific general formula: where Ar and M are as defined above and the group R is equivalent to R₂ as defined above, excluding hydrogen and methyl and less a bridging methylene group. The macroreticulate polymeric scavengers may also be synthesized by metallating macroreticulate polymers having pendant aromatic groups with ionizable protons at the alpha carbon atom. That deprotonation reaction will always produce pendant groups that have the general formula I. Those groups will also come within formula II if they conform to the version of formula I in which R₁ is hydrogen and R₂ is the group -CH₂-R in formula II. Normally, the macroreticulate polymer backbone having pendant aromatic vinyl groups will also contain the pendant functional groups having ionizable protons, so that the deprotonation reaction will take place concurrently with the metallation of the aromatic vinyl groups by addition across the double bond. In the absence of pendant aromatic vinyl groups, the deprotonation reaction alone may of course be used to produce the polymers according to the invention. According to one process for making macroreticulate polymeric scavengers by metallating a polymer having a macroreticulate polymer backbone, having pendant aromatic vinyl groups or pendant aromatic groups with ionizable protons at the alpha carbon atom, (preferably macroreticulate poly(styrene-divinylbenzene), the polymer is contacted with a metallating agent selected from the group consisting of alkyl lithium, alkyl sodium, alkyl potassium, dialkyl magnesium, alkyl magnesium halide and dialkyl zinc, where the alkyl group is an alkyl hydrocarbon radical containing from 1 to 12 carbon atoms; alkaline or alkaline earth metal salts of benzophenone and alkali or alkaline earth metal salts of fluorenone. According to the invention a polymeric scavenger having a macroreticulate polymer backbone, optionally macroreticulate poly(styrene-divinylbenzene) having pendant aromatic groups, which groups are metallated functional groups that have the general formula: where Ar is an aromatic hydrocarbon radical containing from one to three rings, R₁ and R₂ are the same or different and are selected from the group consisting of hydrogen, alkyl hydrocarbon radicals containing from 1 to 13 carbon atoms, methylene-bridged benzophenone radicals, alkali or alkaline earth metal salts of methylene-bridged benzophenone, methylene-bridged fluorenone radicals and alkali or alkaline earth metal salts of methylene-bridged fluorenone; and M is lithium, potassium, sodium, alkyl magnesium, or alkyl zinc, where the alkyl groups are alkyl hydrocarbon radicals containing from 1 to 12 carbon atoms, is used for purifying fluids containing Lewis acid and oxidant impurities. While the macroreticulate polymeric scavengers used according to the invention are suitable for most uses, it may be desirable for certain highly specialized applications to produce macroreticulate polymeric scavengers that are capable of yielding ultra-high purity gas streams. To obtain such products, the macroreticulate polymeric scavenger is subjected to a thermal ageing process or to extraction with a hot inert solvent. Therefore in a preferred process for making the macroreticulate polymeric scavengers of this invention the metallated polymer is subsequently purified by heating to a temperature of from about 140° to about 250°C for more than six hours and removing the gaseous reaction products, or by extracting at a temperature of from about 50° to about 120°C with an inert solvent having a low affinity for the macroreticulate polymeric scavenger. Examples of the macroreticulate polymers that can be metallated to form the scavengers according to the invention are copolymers of one or more crosslinking agents such as divinylbenzene or divinylnaphthalene, with styrene, vinyltoluene, vinylisopropylbenzene, vinylethylbenzene, vinylnapthalene, alpha-methylstyrene and beta-methylstyrene or mixtures of such monomers. For commercial reasons, the preferred macroreticulate polymer is commercially available macroreticulate poly(styrene-divinylbenzene), hereinafter referred to as PSDVB. This material has the requisite macroreticulate backbone and pendant aromatic groups that include both those having ionizable protons at the alpha carbon atom as well and those having vinyl double bonds. In the preferred polymers according to the invention, the aromatic hydrocarbon radical containing from one to three rings, which may be phenylene, naphthylene, fluorethylene and the like, is preferably phenylene. The polymeric backbone of the scavenger may be in any polymer that is both macroreticulate and not degraded by the metallating agent or by the processing conditions. Generally the pore size will be in the range of 1-1000 nanometers. A pore size of 5-10 nanometers is preferred. The polymeric backbone must not react with the metallated functional groups since a functional group that reacts with the backbone is not available to scavenge impurities. The nature of the metal-functional group bond varies depending on the choice of M. Where M is potassium, the bond is highly ionic, whereas where M is an alkyl zinc the bond is much more covalent. The other possible M's fall somewhere between these two extremes. The greater the ionic nature of the bond, the greater the carbanion character of the functionality. It has been found that the greater the carbanion character, the more reactive the functionality and the more intense the color of the scavenger. Only where M is alkyl zinc is the scavenger not intensely colored. In some embodiments it is the most reactive and most intensely colored macroreticulate polymeric scavenger that will be desired. There are other embodiments, however, where less reactivity is sought and in these situations less reactive pendant metallated functional groups or mixtures of metallated functional groups will be employed. The particular metallated functional group or mixture of metallated functional groups best suited for a specific application will be readily ascertained by one skilled in the art. The scavengers of this invention are stable at temperatures as high as 72°C for prolonged periods of time and stable at temperatures as high as 135°C for short periods of time. The macroreticulate polymer backbone is metallated with an organometallic compound such as an alkyl lithium, alkyl sodium, alkyl potassium, dialkyl magnesium, alkyl magnesium halide or dialkyl zinc, where the alkyl group is an alkyl hydrocarbon radical containing from about 1 to 12 carbon atoms; or with a salt of a benzophenone radical-anion or dianion or a salt of a fluorenone radical-anion or dianion. The preferred organo-metallic compounds are tert-butyllithium, dibutylmagnesium and sodium/potassium salts of the benzophenone radical-anion or dianion. Metallation reactions are well known in the art. The metallation can be achieved simply by contacting the macroreticulate polymer backbone with a solution containing the organometallic compound. Typical solvents for the organo-metallic compound include aliphatic hydrocarbons, aromatic hydrocarbons and ethers. The metallation is carried out at ambient temperature and pressure. The contact time is typically in the range of from about 10 minutes to about 10 hours. Other methods of synthesis of the macroreticulate polymeric scavengers of this invention will be known to those skilled in the art. The loading of the polymer backbone of the scavenger is an indication of the number of functional groups present and is expressed in milliequivalents of functional groups per milliliter of scavenger. The greater the loading, the greater the capacity of the macroreticulate polymer scavenger. The optimal loading for a particular scavenger will depend on the polymer backbone, the metallated functional group, the impurities to be removed and the particular application, and can be readily ascertained by one skilled in the art. In general, the loading will be from about 0.01 to about 3.0 milliequivalents, preferably from about 0.05 to about 2.5 milliequivalents, of functional groups per milliliter of scavenger. Macroreticulate polymeric scavengers with impurity absorbance capacities of from about 8 to about 12 liters of oxygen per liter of resin bed, much higher than the capacity of presently available fluid purifiers, can be prepared. Such increased capacity reduces the frequency with which purification columns must be recharged during use. The increased capacity is believed to be due to the presence of excess organometallic metallating agent within the macroreticulate polymer matrix of the scavenger. The excess reagent is believed to be strongly bound in clusters to the metal immobilized in the functional groups on the polymeric backbone. As much as 70% of the capacity of the scavenger could be present as excess metallating agent. The macroreticulate polymeric scavenger according to this invention is used to purify any material that is a gas or liquid when contacted with the scavenger and that is inert to the scavenger's metallated functionalities. Representative of the fluids which may be treated are saturated aliphatic hydrocarbons, including methane, ethane, propane, butane, pentane, hexane, heptane, octane, decane, dodecane and the like; olefins including ethylene, propylene, 1-butene and the like, (but not those olefins which would react with the metallated functionalities of the scavenger such as, those having an adjacent aromatic group including styrene, those having a conjugated double bond, including 1,3-butadiene and those containing acidic protons including allene and cyclopentadiene); and gases inert to the macroreticulate polymeric scavenger including nitrogen, argon, helium, xenon, hydrogen, carbon tetrafluoride, ammonia and silane. The macroreticulate polymeric scavengers of this invention effectively remove a wide variety of impurities such as oxidants and Lewis acids. A Lewis acid is a compound which can accept a pair of electrons. Representative impurities include oxygen, water, alcohols, phenols, aldehydes, ketones, carboxylic acids, carbon dioxide, carbon monoxide, alpha-acetylenes, allene, conjugated dienes, peroxides, sulfur compounds and the like. The metallated functional group of the scavenger is believed to be capable of removing impurities by at least three mechanisms: oxidation, deprotonation and metallation. The macroreticulate polymeric scavenger can be contained in any device comprising a chamber which is impermeable to the fluid to be purified and has an inlet port and an outlet port to allow the impure fluid to enter mid-chamber and the purified fluid to exit. Preferably, the device is translucent so that any loss of color of the scavenger can be observed. Such devices are known in the art. Typical devices include beds and columns. The precise configuration of a device will depend upon the scavenger, the fluid and the impurities to be removed. The optimal size and configuration for a particular use will be readily determinable by one skilled in the art. In some embodiments it will be desirable to initially pack the device with unmetallated macroreticulate polymer and then carry out the above described metallation reaction using the device as the reaction vessel, thus forming the scavenger in situ. Because the macroreticulate polymeric scavengers are largely insensitive to swelling in the inert fluids, columns can be packed to full volume without concern for large volume changes. The impurities are removed in accordance with the process of this invention by passing the fluid containing impurities over the macroreticulate polymeric scavenger, for example, by passing the impure fluid through a bed or column containing the scavenger. The time required will depend on the scavenger, the fluid and the composition and concentration of the impurities. The time required for a particular situation will be readily ascertained by one skilled in the art. To determine if the proper conditions have been chosen for a particular situation, one need only to take an aliquot of the fluid after it has been passed through the macroreticulate polymeric scavenger and test for the presence of impurities using any appropriate analytical method. A particularly useful method is simply to pass the fluid though an indicator solution after the fluid has been passed through the scavenger. There is an additional benefit in using a macroreticulate polymeric scavenger in which the metal-functional group bond has ionic character. Such scavengers are intensely colored. As the metallated functional group reacts with impurities, the metal-functional group bond is destroyed and consequently the scavenger loses its intense color. When the color is gone, the scavenging power has been depleted and the scavenger needs to be replaced. Macroreticulate polymeric scavengers with a metal-functional group bond having sufficient ionic character may also be used as an indicator for the various Lewis acid and oxidant impurities with which they react. A color change indicates that these impurities are present, whereas when there is no change in color, the fluid is free from the impurities. Small amounts of low molecular weight hydrocarbons have occasionally been found in the off gas of the macroreticulate polymeric scavengers of this invention. The source of the low molecular weight hydrocarbons is believed to be an excess of the organometallic compound used as the metallating agent, which, as mentioned previously, is believed to be bound in clusters to the metal immobilized in the functional groups on the polymeric backbone. For most end uses the hydrocarbon emissions from the macroreticulate polymeric scavengers are not a problem. However, as indicated above, it may be desirable for certain highly specialized applications, e.g., in the production of ultra high purity gas streams, to avoid introduction of new impurities into the fluid stream after oxidants and/or Lewis acids have been removed. However, the excess metallating agent cannot be removed by simply washing with an appropriate solvent, nor can the excess be controlled by simple reduction in the amount of reagent added. The hydrocarbon emissions can be reduced to an acceptable level, e.g., to about 0.5 ppm, either by subjecting the macroreticulate polymeric scavenger to a thermal ageing process or by extracting the scavenger with a hot inert solvent, as already mentioned. The thermal ageing process, which involves heating the macroreticulate polymeric scavenger at a high temperature (preferably from about 140° to about 250°c) for more than six hours, in order to decompose the excess metallating agent. The thermal ageing is carried out in such a manner that the gaseous reaction products can be removed either under vacuum or under an inert gas purge to prevent undesirable side reactions. The high impurity absorbance capacity of the macroreticulate polymeric scavenger is not reduced by the ageing process. The excess metallating agent present within the macroreticulate polymer matrix of the scavenger is believed to disproportionate to produce metal hydride, which is also an active scavenger, and olefins. The aged scavenger therefore contains finely divided metal hydride dispersed within the pores of the macroreticulate polymer. As much as 70% of the capacity of the scavenger may be present as the dispersed metal hydride. This type of scavenger cannot be formed by simply mixing metal hydride with the metallated macroreticulate polymer, since the polymer particles would be coated with metal hydride. Commercially available metal hydride also has a lower surface area than the hydride produced by disproportionation of excess metallating agent as in the present invention. Simply mixing commercially available metal hydride with macroreticulate polymer scavenger would therefore result in lowered scavenging efficiency and entrainment of metal salts in the fluid stream to be purified. The extraction process involves treating the macroreticulate polymeric scavenger with a hot inert solvent having a low affinity for the scavenger. The extraction is carried out at a temperature of about 50° to about 120°C for an extended period of time, e.g., 15 hours. Preferred solvents include aliphatic or cycloaliphatic hydrocarbons having a boiling point of about 35° to about 100°C., e.g., pentane, hexane, heptane, cyclopentane and cyclohexane. Hexane is the most preferred solvent. The extracted macroreticulate polymeric scavenger has a somewhat lower impurity absorbance capacity than the aged scavenger. After thermal ageing or extraction the macroreticulate polymeric scavenger can be used in specialized applications that are hydrocarbon-sensitive such as production of ultra high purity gas streams for polysilicon formation, blanketing single crystal ingots, gas chromatographic guard columns, and semiconductor wafer manufacture. Further embodiments of the invention can be found in claims 2 to 11. Example 1 Lithiated poly(styrene-divinylbenzene) scavenger is prepared in the following manner. A macroreticulate PSDVB polymer having a melting point of about 250°C, such as Amberlite XAD4® manufactured by Rohm & Haas, is washed with three bed volumes of water, then methanol, then isopropanol and finally hexane. One bed volume is equal to the volume of the unfilled bed. The polymer is placed in a reaction vessel and dried for about two hours under a stream of nitrogen at 120°C. The reaction vessel is then flooded with 2 molar tert-butyllithium. The mixture is agitated occasionaly for two hours. The resulting scavenger is washed with hexane and dried with nitrogen at room temperature. The product is a lithiated macroreticulate polymer scavenger of this invention which is dark red and turns white upon reaction with impurities. Example 2 Butylmagnesium poly(styrene-divinylbenzene) scavenger is prepared in the following manner. The procedure of Example 1 is followed except that the clean PSDVB polymer is flooded with 0.7 M dibutylmagnesium and reacted at room temperature for one hour. The resulting product is a macroreticulate polymer scavenger of this invention which is yellow and turns white upon reaction with impurities. Example 3 Potassium benzophenone poly(styrene-divinylbenzene) scavenger is prepared in the following manner. Sixty ml of PSDVB polymer are placed in one side of a vessel having two 250 ml round-bottom flasks joined by a coarse frit. Benzophenone (4.2 g) in 75 ml tetrahydrofuran is added to the other side. Sodium/potassium alloy is then added to the benzophenone solution and the solution immediately turns blue, the first of two color changes that occur during the reaction. When the solution becomes purple, the thus formed potassium benzophenone dianion solution is transferred to the side containing the solid polymer. The solution is then returned to the sodium/potassium alloy side and an additional 75 ml of tetrahydrofuran is added. After one-half hour the solution is returned to the side containing polymer and left overnight at room temperature. The resulting product is washed with 400 ml tetrahydrofuran, then 300 ml hexane and finally dried under nitrogen. The product is a macroreticulate polymeric scavenger of this invention which is black to reflected light, is blue-purple when crushed under an inert atmosphere and turns white upon reaction with impurities. Example 4 This example illustrates the use of a lithiated poly(styrene-divinylbenzene) scavenger of this invention to purify propylene monomer. A teflon-covered magnetic stir bar and 400 ml of purified hexane diluent are placed in a crown capped vessel. The diluent is then sparged with purified nitrogen for about 50 minutes. The vessel is placed in a constant temperature bath at 50°C. The vessel is then attached to a propylene manifold and flushed with propylene for several minutes in order to remove the nitro gen. To the hexane diluent is added 1.2 ml of a 1.36 M diethyl-aluminum chloride in hexane and then 0.3 mmoles of TiCl₃. The propylene is polymerized at a temperature of 65°C under 30 psig propylene pressure for 2.5 hours. The polymerization is repeated following the same procedure except the propylene gas is first purified by passing it through a 400 ml column packed with lithiated poly(styrene-divinylbenzene) scavenger prepared as outlined in Example 1. Without purification, the yield of insoluble polymer is 4.0 g and the percent insoluble yield is 97%. With purification, the yield of insoluble polymer is 5.0 g and the percent insoluble yield is 98%. Example 5 This example illustrates the efficacy of the macroreticulate polymer scavengers of this invention in removing oxidants and Lewis acids from an inert gas stream. The lithiated poly(styrene-divinylbenzene) scavenger prepared as in Example 1 is used to fill a 500 ml glass column. Nitrogen containing the impurities listed below is passed through the bed at a flow rate of 40 volumes of gas per volume of bed per hour. In order to determine if any impurities remain in the nitrogen after it is passed through the bed, the nitrogen is subsequently passed through an indicator solution. The indicator solution consists of 5 ml of diglyme which contains 2.5 micromoles of sodium anthracene. The anthracene will decolorize if any impurities are left in the nitrogen. No decolorization is detected. It is found that the lithiated macroreticulate polymer scavenger removes oxygen (41 micromoles), isopropanol (50 micromoles), carbon dioxide (41 micromoles), and acetone (54 micromoles) from the nitrogen stream. A 30 ml serum vial containing about 3 ml of the lithiated macroreticulate polymer scavenger is pressurized to 10 psig with nitrogen. One ml of carbon monoxide is added. After three minutes there is no detectable carbon monoxide present in the nitrogen gas. Example 6 This example describes the thermal ageing process for reducing hydrocarbon emissions from lithiated PSDVB scavenger of this invention. The macroreticulate PSDVB polymer scavenger is washed and dried as in Example 1. The reaction vessel is then flooded with 1.6 M n-butyllithium and the solvent is removed under a nitrogen stream at 65°C. The polymer is washed quickly with 2-4 bed volumes of hexane to remove surface alkyl lithium and dried at 120° for 16 hours. Total hydrocarbon emissions (C₄ hydrocarbons plus solvent) from the control are 0.4 ppm. The measurements are made with a gas chromatograph. The macroreticulate polymer scavenger is then aged by heating under a stream of nitrogen at 210°C (wall temperature of reactor) for 12 hours. Total hydrocarbon emissions after thermal ageing are 0.02 ppm. Example 7 This example describes the extraction process for reducing hydrocarbon emissions from lithiated PSDVB scavenger of this invention. The macroreticulate PSDVB polymer scavenger is washed and dried as in Example 1. The dried scavenger is then flooded with 2.0 M t-butyllithium. The reaction mixture is blown dry overnight using a stream of nitrogen at room temperature. Total hydrocarbon emissions from the control as measured with a gas chromatograph are 4.0 ppm. The macroreticulate polymer scavenger is then extracted with hot hexane at 57-77°C. for 17 hours. Total hydrocarbon emissions after extraction are 0.1 ppm. Example 8 Lithiated poly[vinyl(isopropylbenzene)-divinylbenzene] PVIPBDVB) is prepared in the following manner, primarily by deprotonating the highly ionizable alpha carbon hydrogen in the isopropyl group. A macroreticulate PVIPBDVB polymer having a m.p. of about 250°C is washed with three bed volumes of water, then methanol, then isopropanol, and finally hexane. (One bed volume is equal to the volume of the unfilled bed). The polymer is placed in a reaction vessel and dried for about two hours under a stream of nitrogen at 120°C. The reaction mixture is then flooded with 2 M n-butyllithium. The polymer is blown dry using heated nitrogen at 65°C. The product is washed with 1 bed volume of clean hexane and the product is dried at 120°C under a stream of clean nitrogen. The product is a lithiated polymer which is dark red and turns white upon reaction with impurities. Example 9 Lithiated poly[vinyl(ethylbenzene)-divinylbenzene] (PVEBDVB) is prepared in the following manner, again making use of a highly ionizable alpha carbon hydrogen in the alkyl group. A macroreticulate PVEBDVB polymer having a m.p. of about 250°C is washed, dried, and treated 2 M n-butyllithium as described in Example 8. The polymer is blown dry and washed as in the previous example, and yielded a lithiated polymer which is dark red and turns white upon reaction with impurities. Example 10 This example describes the thermal aging process for reducing hydrocarbon emissions from lithiated PVIPBDVB. The macroreticulate PVIPBDVB polymer is washed and dried as in Example 8. The reaction vessel is then flooded with 1.6 M n-butyllithium and the solvent is removed under a nitrogen stream at 65°C. The polymer is washed quickly with 2-4 bed volumes of hexane to remove surface alkyl lithium. The polymer is then aged by heating under a stream of nitrogen at 210°C (wall temperature of reactor) for 12 hours. Total hydrocarbon emissions after thermal aging are 0.02ppm. Example 11 This example describes the extraction process for reducing hydrocarbon emissions from lithiated PVEBDVB. The macroreticulate PVEBDVB polymer is washed and dried. The dried polymer is then flooded with 2.0 M t-butyllithium. The reaction mixture is blown dry overnight using a stream of nitrogen at 65°C. Total hydrocarbon emissions from the control as measured with a gas chromatograph are 4.0 ppm. The resin is then extracted with hot hexane at 55-77°C for 17 hours. Total hydrocarbon emissions after extraction and drying under a hot nitrogen stream are 0.1 ppm.

Claims: Use of a polymeric scavenger having a macroreticulate polymer backbone, optionally macroreticulate poly(styrene-divinylbenzene) having pendant aromatic groups, which groups are metallated functional groups that have the general formula: where Ar is an aromatic hydrocarbon radical containing from one to three rings, R₁ and R₂ are the same or different and are selected from the group consisting of hydrogen, alkyl hydrocarbon radicals containing from 1 to 13 carbon atoms, methylene-bridged benzophenone radicals, alkali or alkaline earth metal salts of methylene-bridged benzophenone, methylene-bridged fluorenone radicals and alkali or alkaline earth metal salts of methylene-bridged fluorenone; and M is lithium, potassium, sodium, alkyl magnesium, or alkyl zinc, where the alkyl groups are alkyl hydrocarbon radicals containing from 1 to 12 carbon atoms, for purifying fluids containing Lewis acid and oxidant impurities. Use of a polymeric scavenger according to claim 1 the scavenger being characterized by the presence of an excess organometallic metallating agent within the macroreticulate polymer matrix. Use of a polymeric scavenger according to claim 1 or 2, characterized in that the functional groups have the general formula: where Ar is an aromatic hydrocarbon radical containing from one to three rings, the group -CH₂-R is selected from the group consisting of alkyl hydrocarbon radicals containing from 2 to 13 carbon atoms, methylene-bridged benzophenone radicals, alkali or alkaline earth metal salts of methylene-bridged benzophenone, methylene-bridged fluorenone radicals and alkali or alkaline earth metal salts of methylene-bridged fluorenone; and M is is lithium, potassium, sodium, alkyl magnesium, or alkyl zinc, where the alkyl groups are alkyl hydrocarbon radicals containing from 1 to 12 carbon atoms. Use of a polymeric scavenger according to claim 1, 2 or 3 characterized in that M is lithium. Use of a polymeric scavenger according to claim 1, 2 or 3 characterized in that M is butylmagnesium. Use of a polymeric scavenger according to claim 3, characterized in that M is lithium and R is a butyl radical. Use of a polymeric scavenger according to claim 3, characterized in that M is butylmagnesium and R is a butyl radical. Use of a polymeric scavenger according to any of the preceeding claims, characterized in that finely divided hydride of the metal component of M is dispersed in the pores of the polymer, the metals of the hydride and of the pendant functional groups being the same. Use of a polymeric scavenger according to any of the preceeding claims, characterized in that the fluid which is to be purified is a saturated aliphatic hydrocarbon or an olefin. Use of a polymeric scavenger according to claim 9, characterized in that the fluid is ethylene or propylene. Use of a polymeric scavenger according to one of claims 1-8, characterized in that the fluid is nitrogen, argon, helium, xenon, hydrogen, carbon tetrafluoride, ammonia or silane.

Inventors: GLENNMCPHERSON, TOM
Applicants: HERCULES INCORPORATED
Application year: 1985
Main classification: C08F8
IPC codes: C08F8, B01J20