CERAMIC COMPOSITOIN FOR DIELECTRIC IN MULTILAYER CAPACITORS

Abstract: Lead oxide-base material for multilayer ceramic capacitors are provided having high dielectric constant and insulation re­ sistance over wide temperature range, e.g. 10°C to 85°C. The dielectric composition comprises by weight 2.49 to 6.67% Fe₂O₃ 24.18 to 28.14% Nb₂O₅ 2.09 to 3.5% MgO 0.025 to 0.10% MnO₂ 0.20 to 1.50% in the aggregate of one or more of the following oxides: GeO₂, SiO₂, Bi₂O₃, CdO, ZnO, Al₂O₃, CuO and B₂O₃, chemically combined with at least 20% by weight of PbO, to form a sinter­ ing aid having a melting point of not higher than 775°C and a resistivity at 25°C of at least 10¹³ ohm-cm, said dielectric composition having a total lead oxide content, as PbO, of from 64.32 to 66.20% and having an atomic ratio of Pb to the sum of Nb, Fe and Mg from 0.893 to 0.913 and a weight ratio of MgO to Fe₂O₃ from 0.34 to 1.3.

Description: Ceramic Composition for Dielectric in Multilayer Capacitors The present invention is related to ceramic compositions having a high dielectric constant and high insulation resistance at temperatures up to 850C and which are capable of being formed by sintering a mixture of oxides at relatively low temperatures in the range of about 900 to 10500C. More particularly, the present invention is directed to ceramic compositions particularly suited for use as the dielectric in multilayer ceramic capacitors. Ceramic compositions using barium titanate have been used successfully as the dielectric materials for ceramic capacitors; however, such compositions require relatively high sintering temperatures e.g. 1200C and higher, and this precludes the use of relatively inexpensive metal, such as silver and nickel, as capacitor electrodes, and mandates the use of higher melting, expensive precious metals, such as platinum. Recently, lead oxide-based perovskite dielectric systems have been proposed to achieve low sintering temperatures while providing a relatively high dielectric constant and insulation resistance, for example, U.S. Patent No.4,216,102 to Furukawa et al. Such prior art lead oxidebased solid solution systems provide significant advantages, however, there remains the need to provide high dielectric constants wi - increased temperature dependence stability and higher insulation resistance at high temperatures, more comparable to barium titanate base dielectrics. Accordingly, it is an object of the present invention to provide a ceramic composition which can be sintered at relatively low temperatures and which is characterised by improved dielectric constant and insulation resistance at temperatures up to 850C. Other objects will be apparent from the following description and claims taken in conjunction with the drawings wherein: Figure 1 shows a photomicrograph (original magnification 570X) of the microstructure of a multilayer capacitor having a dielectric of sintered ceramic material in accordance with the present invention. Figures 2a, b and c are graphs showing the dielectric constant and insulation resistance values obtained from various ceramic compositions. Figure 3 shows the relationship between the s-tarting lead oxide compositions and the final compositions of dielectrics of this invention. Figure 4 is a graph showing insulation resistance as a function of temperature for various lead oxide-based dielectric materials, and Figure 5 is a graph showing temperature dependence characteristics of the lead oxide-based dielectric of the present invention. A ceramic composition in accordance with the present invention is characterised by being sinterable at temperatures in the range of 900 to 10500C and having a dielectric constant (K) of at least 10,000 at 250C and 10,000 (+22% to -56%) over the range of 10-85 0C and insulation resistance of at least 1012 ohm-cm at 250C and 1011 ohm-cm at 850C. These characteristics satisfy EIA standard RS-198-C for Z5U capacitors. The lead oxide-base sintered ceramic dielectric composition of the present invention, on an oxide basis, consists essentially, of, by weight, 2.49 to 6.67% Fe203 24.18 to 28.14% Nb205 2.09 to 3.59% MgO 0.025 to 0.10% Mn02 0.20 to 1.508 in the aggregate of one or more of the following oxides: GeO2, Si02, Bi203, CdO, ZnO, A1203, CuO and B203, chemically combined with at least 20% by weight of PbO, to form a sintering aid having a melting point of not higher than 7750C and a resistivity at 250C of at least 1013 ohn-cm, said dielectric composition having a total lead oxide content, as PbO, of from 64.32 to 66.20% and having an atomic ratio of Pb to the sum of Nb, Fe and Mg from 0.893 to 0.913 and a weight ratio of MgO to Fe203 from 0.34 to 1.3. The above-defined composition provides low sintering ceramic (900 to 10500C) having an optimum combination of dielectric constant and insulation resistance characteristics. The relatively low PbO content is particularly 5 ortant to the achievement of high dielectric constant as are the relationships recited with respect to Pb, Fe, Mg and Nb. The relatively minor amounts of MnO2 and of the sintering aid additives enables optimum densification of the dielectric, and enhance the insulation resistance, especially at high temperatures (e.g. 850C). Further, these additives in combination result in the insulation resistance remaining high during capacitor life testing under high temperature and voltage stresses. In the practice of the present invention, a blended mixture of finely divided particles of PbO, MgO, Fe203 and Nb205 is provided in appropriate proportions and manganese, e.g. in the form of a manganese-containing salt such as manganous nitrate or acetate, is added to provide the desired MnO2 content in the sintered ceramic, and the mixture is calcined at about 720 to 7800C for about 60 to 180 minutes in an air atmosphere. The resulting calcine material is milled to a size of about 0.6 micron and blended with finely divided (e.g. 1 micron) oxide sintering aid additive, in the amount of about 1-396 by weight of the calcine. Suitable sintering aid materials include Pb5Ge195Si105011, (melting point 7200C, resistivity > 1013 Ohn"cm and lead-containing glasses such as compositions A and B in Table A, below. Table A - Sintering Aids A B PbO 61.6 24.8 (wt.t) CdO -- 35.5 Bi203 2.4 24.5 B203 14.S 5.2 sio2 2.5 4.9 ZnO 15.2 4.0 Al 203 -- 1.0 CuO 3.8 - M.P. SOOOC 7000C Resistivity > 1013 ohm-cm > 1013 ohm-cm The mixture thus obtained is sintered at 900 to 10500C for about 60 to 180 minutes in the course of which the calcine and the sintering aid constituents react to provide a reaction product characterised by a microstructure comprising a predominantly lead perovskite solid solution phase surrounding discrete regions of sintering aid metal oxide residues. A representative microstructure (original magnification 570X) is shown in Figure 1 wherein 1 indicates generally the dielectric composition of the invention, and 2 is a capacitor electrode typically made of silver containing 5 to 25 wt.% palladium. The lead-containing perovskite phase of the dielectric composition is indicated at 3. The dark regions 4 surrounded by the perovskite dielectric phase 3 are sintering aid metal oxide residues, SiO2 and GeO2. Ceramic dielectric material in accordance with the present invention is used as the dielectric for multilayer ceramic capacitors following conventional practice and using relatively inexpensive metals such as silver and its alloys as the electrode material. The following example will further illustrate the present invention: Example A calcine material was prepared from the following: PbO sized 4.5 micron ) mean particle MgCO3 sized 3 micron ) size as determined Fe203 sized 0.5 micron ) by the SedigraphTM Nb203 sized 3 micron ) technique. The materials were milled, dried and calcined at 7500C, for 120 minutes. In some instances, Mn(N03)2 was added to the mixture before calcining to provide a desired Mn02 content in the calcine and, in further instances, oxidic sintering aid material was added after calcining to provide a desired sintering aid content. Materials as above described were sintered at 965 to 10500C. for about 120 minutes to obtain a dense ceramic, and conventional practices to make multilayer ceramic capacitors were followed. The multi layer capacitors had individual dielectric layers of about 1.2 mils thickness and a total capacitance of about 1 microfarad (for a dielectric constant of 10,000). The fired dielectric compositions are shown in Table 1 and the dielectric properties are listed in Table II. The data from Table II are plotted in Figures 2a, b and c and Figure 4. Samples A-H, not in accordance with the present invention, reflect the known behaviour of lead magnesium iron niobate as described in U.S. 4,216,102 and elsewhere in the prior art. That is, as the PbO content approaches the stoichiometric value of about 68.25 wt.% for 0.35 Pb(Fe1/2Nb1/2)O3.0.65 Pb(Mg1/3Nb2/3)O3. the dielectric constant and the insulation resistance of the material both increase sharply (Samples A-H as shown in Figures 2(a)-(c) and Table (II). Sample I was made generally in accord with the present invention, but with an incorrect ratio of Pb/Nb+Mg+Fe. The presence of MnO2 (compare series E-H with A-D) increases the insulation resistance of the composition when the PbO content is near its stoichiometric value. In sharp contrast, the compositions of this invention (Samples J, K, L) exhibit a high dielectric constant and very high insulation resistance at a significantly substoichiometric PbO content, at which other formulations exhibit low dielectric constants and very low insulation resistances, particularly at high temperatures, as can be seen in Figures 2(c) and Figure 4. Figure 4 is a graph showing insulation resistance as a function of temperature for the materials of the example. As can be seen, the materials J, K, L in accordance with the present invention are superior. Figure 5 is a graph showing dielectric constant change with temperature for materials in accordance with the present invention. As can be seen, the temperature dependence of the dielectric constant is very good and well within the specification for Z5U-type capacitors as established by Electric Industries Association Standard RS-198-C (November 1983). A significant aspect of the formulations of this invention is the manner in which they can be sintered. The usual practice is to sinter PbO containing perovskites in closed crucibles often with lead-containing "atmosphere powders" near the bodies to minimize lead loss. In the practice of the present invention sintering can be accomplished in open containers such as those used to make barium titanate multilayer capacitors, using an excess of PbO. PbO loss from the dielectric during sintering results in the achievement of the desired PbO content. Figure 3 shows the PbO content for the presintered mixture and sintered compositions for samples J, K, L of the present invention. A relatively wide range of initial high PbO contents results in a narrow range of final composition in accordance with the present invention. It is usually desirable, however, to use starting compositions which are relatively low in PbO content as illustrated in Figure 3 to minimize the amount of PbO which is evaporated from the body. Variations in the Fe and Mg contents and sintering aid content additive affect somewhat the value of the final PbO content and can be used to adjust the temperature coefficient of capacitance and sintering behaviour of the dielectric. TABLE I Germanium Oxide Sintering Temp. Atomic Ratio Sample PbO Fe2O3 MgO Nb2O5 MnO2 Plus Silicon Oxide ( C) Pb Fe+Mg+Nb A 64.26 4.82 3.02 27.91 - - 1050 .834 B 65.75 4.62 2.90 26.75 - - 1050 .890 C 67.53 4.38 2.74 25.35 - - 1060 .965 D 68.24 4.28 2.68 24.81 - - 1060 .997 E 64.15 4.83 3.02 27.94 0.05 - 1050 .832 F 64.34 4.59 2.87 26.56 0.05 - 1050 .886 G 67.53 4.37 2.74 25.31 0.05 - 1050 .966 H 68.87 4.28 2.62 24.26 0.05 - 1050 1.028 I 65.38 4.62 2.89 26.70 0.06 0.40 1025 .886 J 65.65 4.57 2.86 26.46 0.05 0.04 1025 .899 K 65.75 4.56 2.85 26.37 0.05 0.41 1025 .903 L 65.61 4.58 2.85 26.48 0.05 0.43 1025 .898 M 67.50 4.33 2.71 25.05 - 0.40 975 .976 TABLE II Sample PbO Content K25 C IR25 C IR85 C (Wt. %) # -F # -F A 64.26 1690 56 v.low B 65.75 4020 132 low C 67.53 12500 1000 D 68.24 15440 2430 71 E 64.15 2335 18 w.low F 65.94 6210 175 low G 67.53 9430 4430 44 H 68.87 12740 14590 560 I 65.33 7235 5990 52 J 65.65 11300 14500 1450 K 65.75 11500 21000 1679 L 65.61 12800 16730 1673 M 67.50 7650 2066 455

Claims: CLAIMS 1. A lead oxide-base dielectric ceramic material having high dielectric constant and high insulation resistance which is capable of being formed from a mixture of oxide powders by sintering at temperatures in the range of 900 to 10500C, said ceramic materials comprising by weight, 2.49 to 6.67% Fe203 24.18 to 28.14% Nb205 2.09 to 3.59% MgO 0.025 to 0.10% Mn02 0.20 to 1.50% in the aggregate of one of more of the following oxides: GeO2, sio2, Bi203, CdO, ZnO, A1203, CuO and B203, chemically combined with at least 20 & by weight of PbO, to form a sintering aid additive having a melting point of not more than 7750C, and a resistivity at 250C of at least 1013 ohm-cm, said dielectric composition having a total lead oxide content, as PbO of from 64.32 to 66.20% and having an atomic ratio of Pb to the sum of Nb, Fe and Mg of from 0.893 to 0.913 and the weight ratio of MgO to Fe203 is from 0.34 to 1.3. 2. A ceramic material in accordance with claim 1, wherein the dielectric constant is at least 10,000 and the insulation resistance is at least 1012 ohm-cm at 250C and 1011 ohm-cm at 850C. 3. A ceramic material in accordance with claim 1 or claim 2 which is characterised by a microstructure comprising a predominantly lead perovskite solid solution phase, as determined by X-ray diffraction, surrounding small discrete regions of metal oxide residues of sintering aid additive. 4. A method of forming a lead-oxide based dielectric ceramic material which comprises milling and calcining PbO, Mob205, MgO, MnO2 and Fe203 or precursor salts in air at a temperature of from about 720 to 7800C and sintering the calcined mixture with an oxidic sintering aid material selected from one or more of GeO2, Six2, Bi203, CdO, ZnO, A1203, CaO and B203 in proportions such as to produce a sintered ceramic material containing the following composition: 2.49 to 6.67% Fe203 24.18 to 28.14 & Nb205 2.09 to 3.59% MgO 0.025 to 0.10% Mn02 64.32 to 66.20% PbO said ceramic material having an atomic ratio of Pb to the sum of Nb, Fe and Mg of from 0.893 to 0.913 and the weight ratio of MgO to Fe203 being from 0.34 to 1.3. 5. A method according to claim 4 in which the sintering temperature is from 965 to 10500C. 6. A multilayer capacitor which comprises dielectric layers formed from the material claimed in any one of claims 1 to 3 separated by metal electrodes. 7. A capacitor according to claim 6 wherein the electrodes are formed from silver or an alloy thereof.

Inventors: BROWN, ARTHUR ENGLISH, PARK, HYUN DUK C/O GOLDSTAR ELECTRIC CO. LTD.
Applicants: UNION CARBIDE CORPORATION
Application year: 1985
Main classification: C04B35
IPC codes: H01B3, C04B35, H01G4