ORIENTED MULTI-LAYER HEAT SEALABLE FILM

Abstract: An oriented multi-layer heat sealable film structure comprising a polyolefin film substrate, a polymeric skin layer, a primer layer on the polymeric skin layer and a heat sealable layer on the primer layer.

Description: This invention relates to a flexible multilayer heat sealable general purpose packaging film and to a method of forming the same. In the packaging of certain types of foods, for example, loose products such as cookies, potato chips, and the like, it is common practice to employ a multilayer film having two or more polymeric layers wherein one of the layers is known to be an effective heat seal layer. In the packaging process, a supply of such a multilayer film can be shaped into a tube in a vertical form and fill machine. Marginal regions of the heat seal layer are brought into face to face relationship and heat sealed together. Thereafter, the packaging machine automatically forms a heat seal and makes a horizontal severance across the bottom of the bag; product is dispensed into the open end of the tube and thereafter a second horizontal seal is effected across the tube with a simultaneous severing through the tube to result in a product packaged in a tube, heat sealed at both ends and along one seam at right angles to the end seals. While the food or other product is being dispensed into the package, air is also present in the package and this air assists in protecting and cushioning the product during subsequent shipment of the finished packages. During shipment of the product, particularly with larger size bags, e.g., those containing 454 gm (16 ounces) of product, the bags have a tendency to split or burst at the end seals. A multilayered wrapping film of the type having the above mentioned utility is described in U.S. Patent No. 4,214,039. This patent describes a packaging film structure comprising a polypropylene film substrate having a heat sealable vinylidene chloride polymer containing at least 50% by weight of vinylidene chloride. In between the polypropylene film and the vinylidene chloride polymer is a primer coat which consists of the reaction product of an acidified aminoethylated vinyl polymer and an epoxy resin. This primer coat enhances the bond strength between the polypropylene and the heat sealable vinylidene chloride polymer. While this packaging material is effective for the packaging of comparatively small quantities of product, there exists a need to increase its seal strength when used for the packaging of comparatively large quantities of product. Particularly there is a need to increase the seal strength between the polypropylene layer and the primer layer. The present invention provides an oriented heat sealable multi-layer structure which comprises: (a) a substrate comprising a polyolefin film; (b) a polymeric skin layer on at least one surface of (a), this layer comprising: (1) a terpolymer of propylene with ethylene and 1-butene; (2) a blend of (i) a medium density polyethylene, a high density polyethylene or mixtures thereof; and (ii) polypropylene; (3) a blend of (i) a very low density polyethylene and (ii) polypropylene; or (4) a blend of (i) a linear low density copolymer of ethylene with a minor proportion of a C₃-C₁₀ alpha olefin, and (ii) polypropylene (c) a primer coating on at least one surface of said layer (b); and (d) a heat sealable layer on coating (c), the heat sealable layer comprising an acrylic polymer layer or a vinylidene chloride polymer layer. In preferred forms of the above-identified structure one or both sides of the film can have either an acrylic or a vinylidene chloride polymer film. Alternatively, one surface of the film may be a heat sealable acrylic layer while the opposite surface is a heat sealable vinylidene chloride polymer surface. The present invention also provides a method of producing a heat sealable multi-layer film structure comprising: coextruding a substrate comprising a polyolefin film with a polymeric layer skin, the coextrusion being on at least one surface of the polyolefin substrate; biaxially orienting the coextrudate; applying a primer coating to at least one surface of the polymeric skin layer; and applying a heat sealable layer on the primer coating, the heat sealable layer comprising a member selected from an acrylic polymer and a vinylidene chloride polymer. The polyolefins contemplated as the substrate or core material of the subject film structure include polyethylene, polypropylene, polybutene and copolymers and blends thereof. Particularly preferred is an isotactic polypropylene containing at least 80% by weight of isotatic polypropylene. It is preferred that the polypropylene has a melt flow index of from about 4 to 8 g/10 minutes. The preferred base substrate layer can be homopolypropylene having a melting point range of from about 161° to 169°C (321°-336°F). A commercially available material of this description is ARCO W472 which has a melt flow range of 4 to 5 and contains no slip or anti-block additives. The polymeric skin layer coextruded with the base polyolefin, in some way not completely understood, functions to increase the overall bond strength formed in ESM seals or crimp seals when employing either acrylic or vinylidene chloride polymer heat seals. As mentioned above, the polymeric skin layer is selected from: (1) a terpolymer of propylene with ethylene and 1-butene; (2) a blend of (i) a medium density polyethylene, a high density polyethylene or mixtures thereof; and (ii)polypropylene; (3) (i) a very low density polyethylene or (ii) a blend of a very low density polyethylene and polypropylene; and (4)a blend of (i) a linear low density copolymer of ethylene with a minor proportion of a C₃-C₁₀ alpha olefin, and (ii) polypropylene In one embodiment of the present invention, the polymeric skin layer comprises terpolymers which are comparatively low stereoregular polymers. The terpolymers can have a melt flow rate at 230°C (446°F) ranging from about 2 to 10 and preferably 4 to 6. The crystalline melting point can range from about less than 121°C (250°F) to somewhat greater than 133°C (271°F). The terpolymers will predominate in propylene and the ethylene and 1-butene monomers can be present in approximately from 0.3-1:1 mole percentage in relation to each other. Preferred terpolymers have melting points of about 130°C (266°F) and 124°C (255°F), respectively. The materials are commercially available as Chisso XF 7500 and Chisso XF 7700. These terpolymers contain from about 1-7 wt.% ethylene and 1-7 wt.% 1-butene. In a second embodiment of the present invention, the polymeric skin layer comprises a blend of polypropylene and either a medium density polyethylene, a high density polyethylene or a mixture of the medium and high density polyethylene. The contemplated medium or high density polyethylene can be produced by a number of different processes, but in all cases the pressures and temperatures are much lower than those required by a low density polyethylene process. The American Society for Testing and Materials types polyethylenes as follows: Type 1 is low density polyethylene and can be considered to have a density ranging from about 0.910 to 0.925; Type 2 is medium density polyethylene and it ranges from about 0.926-0.940; and Type 3 is high density polyethylene with a density of from 0.941 to 0.960. This is consistent with the classification given in Modern Plastics Encyclopedia, 1983-1984, Volume 60, No. 10A, page 57. For purposes of the present invention the high density should be extended up to 0.965. These materials, i.e. medium and high density PE, should have a melt index of from about 0.2 to about 5. These low pressure or high density polyethylenes are well known in the art and have very different properties from low density polyethylenes. They are prepared by reacting ethylene monomer in the presence of a metallic oxide catalyst. The medium and high density polyethylenes so produced may be linear, or may contain controlled amounts of branching. These polyethylenes are to be distinguished from high density, high molecular weight polyethylenes having a weight average molecular weight of above about one-half million. The contemplated medium and high density polyethylenes are commercially available from several sources. As mentioned above, the polymeric skin layers in this second embodiment are fabricated from a physical blend of the medium or high density polyethylene or mixtures thereof and polypropylene. The polypropylene employed can be identical to the polypropylene employed for the core layer. The two materials can be blended in a percent by weight of from about 2% by weight to about 100% by weight of the medium or high density polyethylene with the remainder being 98%-0% polypropylene. The physical blend can be accomplished by any means which will form a uniform blend of the two components. The components can be premixed as solid dry granules and later melt blend for subsequent extrusion as skin layers on the core material. Alternatiely, the material may be melt blended first, cooled and subdivided, and thus, be ready for use as a preformed. In a third embodiment of the present invention, the polymeric skin layer comprises very low density polyethylenes (VLDPE) or a blend thereof with polypropylene. When the VLDPE is blended with polypropylene to form the polymeric skin layer, 2-100 wt.% VLDPE and 98-0 wt.% polypropylene can be used. The very low density polypropylenes have a density range of less than about 0.910 and more specifically from about 0.890 to 0.910 gm/cm³. These materials are of low crystallinity and are produced in a low pressure process. For processing, melt temperatures of between 204°C (400°F) and 232°C (450°F) are recommended. Specific materials commercially available are DFDA-1137, having a density of 0.906 gm/cm³ and a Melt Index of 0.8g/10 minutes; and DFDA-1138, having a density of 0.900 gm/cm³ and a Melt Index of 0.40 g/10 minutes. These materials are available from Union Carbide Corporation, Danbury, CT. In a fourth embodiment of the present invention, the polymeric skin layer comprises a blend of polyproplene and a linear low density copolymer of ethylene and a C₃-C₁₀ alpha olefin. The C₃-C₁₀ alpha olefin is present in the copolymer in a minor amount. Included among the C₃-C₁₀ olefinic hydrocarbons are propylene, 1-butene, 4-methyl-1-pentene, 1-hexane, 1-octene, 1-decene, etc. Mixtures of such olefinic hydrocarbon monomers also can be employed. These linear low density copolymers are commercially available materials and are manufactured by low pressure processes employing stereospecific catalysts. These materials usually contain from 2-8 wt.%, preferably 2.5-5 wt.%, of the C₃-C₁₀ alpha olefin hydrocarbon copolymerized with the ethylene, in sufficient amount to give from 5-15 branches per 1,000 carbon atoms in the linear polymer. Manufacturing processes for linear low density polyethylenes of this type are disclosed in U.S. Patent Nos. 4,076,698 and 4,205,021. In this embodiment, the polymeric skin layers are fabricated from a physical blend of one of the above-identified liner low density polyethylene copolymers and polypropylene. A typical linear low density copolymer useful in this invention is a copolymer of ethylene and 1-octene (LLDPE-C₈). The 1-octene is present in the copolymer in approximately 2 to 6 wt.%. A suitable material is Dowlex 2047, available from Dow Chemical Co., Midland, Michigan which has a melt index of 2-3 and a density of 0.917 gm/cm³. The polypropylene employed can be identical to the polypropylene employed for the core layer. The two materials can be blended in a percent by weight of from about 2% by weight to about 100% by weight of the linear low density copolymer with the remainder being the polypropylene. The physical blend can be accomplished by any means which will form a uniform blend of the two components. The components can be premied as solid dry granules and later melt blended for subsequent extrusion as skin layers on the core material. Alternatively, the material may be melt blended first, cooled and subdivided, and thus, be ready for use as a preformed material. In preparing the multi-layer structure of the present invention, the polypropylene and the polymer skin layer are coextruded so that the skin layer is from about 2 to about 12% of the total thickness of the two layers. For some purposes, a layer of the terpolymer can be on both surfaces of a core layer of polypropylene, in which case two polymeric skin layers would amount to from 4 to 24% of the total thickness of the three layers. In preparing the coextruded film it has been found advantageous and convenient to recycle certain quantities of scrap extrudate back into the base homopolymer polypropylene. Thus, the homopolymer polypropylene can have from 0 to 25% of reclaimed material inter-blended therein. This recycle material can contain from 0 to about 15% of the skin layer therein. It has been found that the heat seal layers contemplated herein do not adhere well to polyolefin film surfaces even when the latter have been subjected to well known pretreatment operations such as, for example, treatment by corona discharge, flame, or oxidizing chemicals. The same has been found to be true in adhering the heat seal layers contemplated herein to the surface of the contemplated terpolymer. It has been found, however, that the use of certain primers intermediate between the skin layer and the heat seal layer provides an unexpectedly high level of adherence. As a result, all layers adhere to its adjacent layer with unexpectedly high tenacity. The system contemplated for the formation of the multilayer packaging material of the present invention involves the use of three layers applied in succession to the surface of the chosen substrate layer. For example, when the substrate layer is polypropylene, one or both surfaces of the polypropylene film will have applied thereto the following layers progressing in order outwardly from the surface of the polyproplene: A coextruded layer of the polymeric skin layer, an appropriate primer material to create a bond between the skin layer and a surface heat seal layer, and the heat seal layer itself. Examples of primer materials include those defined in U.K. Patent No. 1,134,876 which discloses a primer produced by condensing a monoaldehyde with an interpolymer of acrylamide or methacrylamide and at least one other unsaturated monomer; and those defined in U.S. Patent No. 1,174,328 which discloses a material resulting from condensing aminoaldehyde with acrylamide or methacrylamide and subsequently interpolymerizing the condensation product with at least one other unsaturated monomer in the presence of a C₁-C₆ alkanol. A preferred primer coating resin of this type comprises a copolymer containing up to 90% by weight of styrene, up to 80% by weight of an alkyl acrylate, up to 15% by weight of methacrylic acid and 5% to 25% by weight of acrylamide which has been condensed with a solution of formaldehyde in n-butanol containing from 0.2 to 3 equivalents of formaldehyde for each amide group in the copolymer. Another primer resin of this type is a 50% solid solution of a copolymer resin containing 38.5 parts of styrene, 44 parts of ethyl acrylate, 2.5 parts of methacrylic acid and 15 parts of acrylamide which has been condensed with 5.2 parts of formaldehyde in n-butanol. A particularly preferred primer material for the acrylic type heat seal layers contemplated herein has been found to be poly(ethyleneimine). The imine primer provides an overall adhesively active surface for thorough and secure bonding with the subsequently applied heat seal composition of this invention. It has been found that an effective coating solution concentration of the poly(ethyleneimine) applied from either aqueous or organic solvent media, such as ethanol is a solution comprising about 0.1-0.6% by weight of the poly(ethyleneimine). A commercially available material of this type is known as Polymin M, a product of BASF-Wyandotte Corp. Another particularly preferred primer material is the reaction product of an epoxy resin and an acidified amminoethylated vinyl polymer. The contemplated epoxy resins are glycidyl ethers of polyhydroxy compounds. Typical polyhydroxy compounds which may be used include bisphenol A, ring substituted bisphenol A, resorcinol, hydroquinone, phenol-formaldehyde, novolac resins, aliphatic diols, such as ethylene glycol, propylene glycol, 1,4-butanediol, 1,6-hexane-diol, glycerol, lower alkyl hydantoins and mixtures thereof. The preferred epoxy resins of the present invention are those made by the glycidation reaction between epichlorohydrin and bisphenol A. Epoxy resins of this type are commonly classified by their epoxy equivalent weight (EEW) which is defined as the weight of resin in grams which contains one gram equivalent of epoxy groups. Resins with an EEW ranging from 170 to 280 may be used in the present invention, but the preferred range is 180 to 210. Although the specific structure of the epoxy resin is not critical to the primer employed in the present invention, important considerations in the selection of the epoxy resin revolve around its physical state. For example, it must be liquid and capable of being readily dispersed or dissolved with the second component or curing agent as described hereinbelow. If the epoxy resin is of low viscosity, it may be stirred directly into the second component, i.e., curing agent. However, it is preferred to employ the epoxy resin in an aqueous emulsion. The second component in the epoxy primer compositions of the present invention is an amino modified acrylic polymer which is water soluble. This polymer is a curing agent for the epoxy compound. The preferred material is described in U.S. Patent No. 3,719,629. This material may be generically described as an acidified aminoethylated interpolymer having pendent aminoalkylate groups. This material is produced by polymerizing acrylate, methacrylate, styrene or other suitable monomers with sufficient methacrylic or acrylic acid to give a -COOH content of about 7.5 to about 12.5%. Solvent polymerization techniques are preferred. The polymer is then reacted with ethyleneimine monomer and acidified with hydrocholoric acid to render the polymer water soluble. In one embodiment of the present invention, a liquid epoxy resin is emulsified in a solution of the curing agent by rapid stirring, the resultant dispersion is diluted with water to the desired concentration for coating, usually from about 2 to about 25% solids. When mixing the epoxy resin with the curing agent, it is generally preferred to use a stochiometric equivalent balance of epoxy and amine groups. However, it has been found that the stochiometric ratio may be varied over a wide range, from about one epoxy to about three amine groups through three epoxy groups to one amine group. The composition of the heat sealable acrylic interpolymer is that defined in U.S. Patent No. 3,753,769. This material consists essentially of an interpolymer of from about 2 to about 15 parts, and preferably from about 2.5 to about 6 parts by weight of acrylic acid, methacrylic acid or any mixture thereof and from about 85 to about 98 parts and preferably from about 94 to about 97.5 parts by weight of neutral monomer esters, the neutral monomer esters preferably comprising (1) methyl acrylate or ethyl acrylate and (2) methyl methacrylate. The interpolymer compositions are further characterized by preferably comprising from about 30% to about 55% by weight of methyl methacrylate when the alkyl acrylate is methyl acrylate, and from about 52.5% to about 69% by weight of methyl methacrylate when the alkyl acrylate is ethyl acrylate. The monomer components of the terpolymer are employed in a ratio such that the alkyl methacrylate monomer is present in an amount of at least 10% by weight of the total terpolymer composition and preferably from about 20 to about 80% by weight, and the alkyl acrylate monomer component in amounts of at least 10% by weight of the total composition, and preferably from about 80 to about 20% by weight. As indicated above it is contemplated herein that one surface of the structure can be of the above described acrylic heat seal material and the opposite surface can be of a vinylidene chloride polymer heat seal material. Commercially available vinylidene chloride latexes having a vinylidene chloride content of at least 50% and preferably from about 75% to about 92% may be employed. The other ethylenically unsaturated comononers may include alpha, beta-ethylenically unsaturated acids, such as acrylic and methacrylic acids; alkyl esters containing 1-18 carbon atoms of these acids, such as, methylmethacrylate, ethyl acrylate, butyl acrylate, etc. In addition, alpha, beta-ethylenically unsaturated nitrile such as acrylonitrile and methacrylonitrile can be employed. In addition, monovinyl aromatic compounds such as styrene and vinyl chloride may be employed. Specific vinylidene polymer latexes contemplated comprise: 82% by weight vinylidene, 14% by weight ethyl acrylate and 4% by weight acrylic acid. Alternatively, a polymer latex comprising about 80% by weight vinylidene chloride, about 17% by weight methylacrylate and about 3% by weight methacrylic acid can likewise be employed. In addition, the heat seal compositions described in U.S. Patent 4,058,649 can also be disclosed. The multiply structure of the present invention can have an overall thickness within a wide range , but it is preferably from about 0.013 mm (0.5) up to about 0.044 mm (1.75 mils) in thickness. When the substrate is the homopolymer polypropylene it can have a film thickness of approximately 0.025 mm (1 mil). In this instance, the associated coextruded polymeric skin layer can be present in a thickness of from about 0.0005 mm (0.02) to about 0.003 mm (0.12 mils). The primer dispersion, to be applied to the surface of the polymeric skin layer, can have a solids concentration of from about 0.1% up to about 25%. The primer dispersion can be applied to the surface of the skin layer utilizing standard coating techniques so that a dry coating weight of from about 0.05 up to about 0.25 gram/0.65 m² (1,000 square inches) of film is obtained. The thus coated film can be subsequently passed through a hot air oven to completely remove water and/or a solvent. Subsequently, this primer coated film can be coated with the appropriate heat seal polymer latex also using standard coating techniques, such as, gravure, roll coating, and the like. The heat seal coated system can thereafter be dried by passing it through a conventional hot air oven. The amount of acrylic polymer applied to the substrate may be varied over a wide range depending upon the specific properties desired in the final film product. Coating weights of from about 0.3 to about 1.2 grams per 0.65 m² (1,000 square inches) may be employed. If a 2-sided coated film is desired, optional but beneficial corona treating of the terpolymer coated substrate, the priming and the opposite heat seal polymer application can be repeated, either in-line or out-of-line. In the following examples, the base films are all biaxially oriented by conventional means. In general, this includes forming the base film in sheet form and machine direction orienting (MDO) or stretching the same at the appropriate or optimum temperature, using transport rollers operating at different speeds. After the desired degree of MDO, the film is transverse direction oriented (TDO), for example, in a tentering apparatus, to impart an orientation or stretching which is at right angles to the MDO. The extent of orientation can be from about 3 to about 10 times its original dimension for the MDO and from about 3 to 10 times in the TDO. For the base film of Examples 2, 4, 16 and 17, the skin layer can be applied to the propylene film after the polypropylene has been machine direction oriented. In this event, the skin layer will only be transversely oriented while the polypropylene is biaxially oriented. The techniques of U.S. Patent No. 3,620,825 and 3,671,383 can be employed in this respect. In the following examples the ESM heat seal test is a heat seal test designed to simulate conditions under which films might be sealed in a typical over-wrapping machine. For the test two strips of film are cut, 76.2 mm by 355.6 mm (3 by 14 inches), with the long direction being in the machine direction orientation of the film. The two strips of film are superimposed with coated surfaces, i.e. the acrylic surfaces, in contact and placed in a heat sealing machine with one movable heat sealing platen. On actuation, the heated platen lowers and contacts the film combination for a controlled period of time. The pressure used is that resulting from the force of a pressure cylinder set at about 34.5 kPa (5 psi) and the time of contact is two seconds. A plurality of separate seals are simultaneously made on each strip of film. The film strips are cut 25.4 mm (one inch) wide and the seal strengths are determined by placing the free ends of the film in the jaws of a Sutter testing machine and peeling the seals apart at a rate of 508 mm (20 inches) per minute. The maximum force in grams is recorded as the heat seal strength. Also, with respect to the following examples, a crimp seal test is carried out. This is designed to simulate conditions encountered in a device known in the industry as a "vertical form-and-fill" packaging machine. This type of machine is designed to horizontally crimp seals cross a tube of packaging, material dispense product into the tube, and, thereafter, again horizontally crimp seal the opposite end of the tube to form a filled, sealed tubular package. Simulaneously with the sealing of the tube, the tube is severed. In the crimp seal test two heated platens with serrated surfaces are brought together by air pressure at 138 kPa (20 pounds per square inch) on either side of the film strips for three-quarters of a second, then separated. Testing of the seals is carried as above. EXAMPLE 1 A biaxially oriented homopolymer isotactic polypropylene film of approximately 0.025 mm (one mil) thickness was coated with the primer reaction product of the acidified aminoethylated vinyl polymer and epoxy resin of example 5 of aforementioned U.S. Pat. No. 4,214,039. The same general coating process of the examples was employed in coating the polypropylene film. The dry coating weight of the primer material was equivalent to about 0.10 grams per 0.65 m² (1,000 square inches) of film. To the surface of the primer was applied a heat seal layer from an aqueous latex comprising a terpolymer resulting from the polymerization of about 82% by weight of vinylidene chloride, about 14% by weight of ethyl acrylate and about 4% by weight of acrylic acid. The coating was dried to yield a coating weight of approximately 2.6 grams per 0.65 m² (1,000 square inches) of film. EXAMPLE 2 Example 1 was repeated except that the primer composition and heat seal compositon were deposited onto the skin layer surface of a coextruded biaxially oriented composite film of the same polypropylene as in Example 1 and a skin layer comprising an ethylene, propylene, 1-butene terpolymer containing from 1-7 wt.% ethylene and 1-7 wt.% 1-butene. The terpolymer had a melt flow of about 5. The combined thickness of the coextruded film was approximately 0.025 mm (1 mil) with the terpolymer amounting to approximately 6% of the total thickness. ESM and Crimp seals were formed in the multiply structures of Example 1 and the comparative strength of these seals are shown in the following Table. TABLE It is clear by the above showing that the heat seal strength of the film structure of Example 2 is significantly greater than that of Example 1. EXAMPLE 3 For this example, Example 2 is repeated except that the coextruded biaxially oriented composite film is coated with a conventional poly(ethyleneimine) primer. To the surface of the primer is applied a heat seal layer from an aqueous solution comprising a terpolymer resulting from the polymerization of about 51% by weight methyl methacrylate, about 45% by weight of methyl acrylate and about 4% by weight of methacrylic acid. When the multi-layer film of this Example is tested for the strength of its crimp and ESM seals, as in Examples 1 and 2, the strengths of the seal of Example 3 will be seen to be significantly greater than that of Example 1. EXAMPLES 4-9 Example 1 was repeated except that the primer composition and heat seal composition was deposited onto the skin surface of a coextruded biaxially oriented composite film of the same polypropylene as in Example 1 and blends of a medium density polyethylene (MDPE), Phillips Chemical TR 130 having a density of 0.937 and polypropylene (PP) in the proportions shown in the following Table. The combined thickness of the coextruded film was approximately 1 mil with the skin layer amounting to approximately 6% of the total thickness. ESM and Crimp seals were formed in the multiply structures of Examples 1-7 and the comparative strength of these seals are shown in the following Table. TABLE It is clear by the above showing that the heat seal strengths of the film structures of Examples 2-7 are significantly greater than that of Example 1. EXAMPLE 10-15 For these examples, Examples 4-9 are repeated except that the coextruded biaxially oriented composite films are coated with a conventional poly(ethyleneimine) primer. To the surface of the primer is applied a heat seal layer from an aqueous solution comprising a terpolymer resulting from the polymerization of about 51% by weight methyl methacrylate, about 45% by weight of methyl acrylate and about 4% by weight of methacrylic acid. When the multi-layer film of this Example is tested for the strength of its crimp and ESM seals, as in Examples 1-9, the strengths of the seals of Example 10-15 will be seen to be significantly greater than that of Example 1. By employing a high density polyethylene, such as Phillips Chemical, DX 611 having a density of 0.960 results equivalent to that of the MPPE will be obtained. EXAMPLE 16 Example 1 is repeated except that the primer composition and heat seal composition is deposited onto the VLDPE surface of a coextruded biaxially oriented composite film of the same polypropylene as in Example 1 and the very low density polyethylene is DFDA-1137, having a density of 0.906. The combined thickness of the coextruded film is approximately 0.025 mm (1 mil) with the VLDPE amounting to approximately 6% of the total thickness. The Crimp Seal and ESM Seal strength of this material exceed that of Example 1. When the VLDPE is blended with polypropylene to form the skin layer or layers on the base layer it can be in the ratio of about 2-100 wt.% VLDPE and 98-0 wt.% polypropylene. EXAMPLE 17 Example 1 was repeated except that the primer composition and heat seal composition was deposited onto the skin surface of a coextruded biaxially oriented composite film of the same polypropylene as in Example 1 and skin layers of a linear low density copolymer of ethylene and 1-octene (Dowlex 2047) blended with the same polypropylene. The film was 0.025 mm (1 mil) thick with the skins amounting to 6% of the thickness. EXAMPLES 18-24 For these examples, Example 17 was repeated except the ratio of linear low density copolymer (LLDPE) to polypropylene (PP) in the skin layer blends were varied as shown in the table below. ESM and Crimp seals were formed in the multiply structures of Examples 1 and 17-24 and the comparative strength of these seals are shown in the following Table. TABLE It is clear by the above showing that the heat seal strength of the film structure of Example 17-24 are significantly greater than that of Example 1. EXAMPLE 25 For this example, Example 17 is repeated except that the coextruded biasially oriented composite film is coated with a conventional poly(ethyleneimine) primer. To the surface of the primer is applied a heat seal layer from an aqueous solution comprising a terpolymer resulting from the polymerization of about 51% by weight methyl methacrylate, about 45% by weight of methylacrylate and about 4% by weight of methacrylic acid. When the multi-layer film of this Example is tested for the strength of its crimp and ESM seals, as in Examples 1 and 17-24, the strengths of the seal of this example are seen to be significantly greater than that of Example 1. It has been determined that after the application of the primer layer and the heat seal layer it is advantageous to permit the structure to age for a certain minimum period of time in order to obtain the outstanding high heat seal bond that results from the present invention. Optimum aging can be accomplished over a period of time raning from about 25 hours to about 21 days while maintaining the film at a temperature ranging from about 0-66°C (32-150°F).

Claims: 1. A heat sealable multi-layer structure comprising: (a) a substrate comprising a polyolefin film; (b) a polymeric skin layer on at least one surface of (a) comprising: (1) a terpolymer of propylene with ethylene and 1-butene; (2) a blend of (i) a medium density polyethylene, a high density polyethylene or mixtures thereof; and (ii) polypropylene; (3) a very low density polyethylene or a blend thereof with propylene; or (4) a blend of (i) a linear low density copolymer of ethylene with a minor proportion of a C₃-C₁₀ alpha olefin, and (ii) polypropylene; (c) a primer coating between layers (b) and (c) on at least one of layer (b); and (d) a heat sealable layer on coating (c) and selected from a vinylidene chloride polymer and an acrylic polymer. 2. The structure of claim 1 wherein the polyolefin film comprises homopolymer polypropylene interblended with from 0 to about 15 parts by weight of the polymeric skin layer. 3. The structure of claim 1 or 2 wherein the primer comprises a member selected from poly(ethyleneimine); the reaction product of an acidified aminoethylated vinyl polymer and an epoxy resin; the condensation product of a monoaldehyde with an interpolymer of acrylamide or methacrylamide and at least one other unsaturated monomer; and the condensation product of aminoaldehyde with acrylamide or methacrylamide interpolymerized with at least one other unsaturated monomer in the presence of a C₁-C₆ alkanol. 4. The structure of claim 1, 2 or 3 wherein the coextruded layer (b) is on one surface of substrate (a). 5. The structure of claim 1, 2 or 3 wherein the coextruded layer is on both surfaces of substrate (a). 6. The structure of claim 1, 2, 3, 4 or 5 wherein the heat sealable layer (d) comprises a vinylidene chloride copolymer containing at least 50% by weight of vinylidene chloride. 7. The structure of claim 6 wherein said heat sealable layer (d) comprises an interpolymer of a minor amount by weight of acrylic acid, methacrylic acid or mixtures thereof and a major amount of neutral monomer esters comprising (1) methyl acrylate or ethyl acrylate and (2) methyl methacrylate. 8. The structure of any one of claims 1-7 wherein the heat sealable acrylic polymer is on one surface of the structure and the heat sealable vinylidene chloride polymer is on the opposite surface of the structure. 9. The structure of any one of claims 1-8 wherein layer (b) (1) contains from 1-7 wt.% ethylene and from 1-7 wt.% of 1-butene. 10. The structure of any one of claims 1-8 wherein in layer (b)(2) the density of the medium density polyethylene is from 0.926 to 0.940 gm/cc and the high density polyethylene is from 0.941 to 0.965 gm/cc. 11. The structure of any one of claims 1-8 and 10 wherein layer (b)(2) comprises a blend of 2-100% of polyethylene and 98-0% polypropylene. 12. The structure of any one of claims 1-8 wherein the very low density polyethylene has a density of less than 0.910 gm/cc. 13. The structure of any one of claims 1-8 and 12 wherein layer (b)(3) comprises a blend of 2-100 wt.% very low density polyethylene and 98-0 wt.% polypropylene. 14. The structure of any one of claims 1-8 wherein layer (b)(4) comprises a blend of 2-100 wt.% linear low density polyethylene copolymer and 98-0 wt.% polypropylene. 15. The structure of any one of claims 1-8 and 14 wherein the copolymer in layer (d)(i) comprises 2 to 8 wt.% the C₃-C₁₀ alpha olefin and the remainder being ethylene.

Inventors: CLAUSON, MELVIL BERNARD, TOUHSAENT, ROBERT EDWARD, WAGNER, JOHN RALPH, JR.
Applicants: MOBIL OIL CORPORATION
Application year: 1985
Main classification: B32B27
IPC codes: B32B27, C08J7