2-DECALYL-2-CYCLOHEXYL DERIVATIVES OF PROPANE, PROCESS FOR THEIR PREPARATION, AND THEIR USE

Abstract: The invention provides a method for the preparation of a fluid for traction drive by Friedel-Crafts reaction of naph­ thalene or tetrahydronaphthalene with an alkenylaromatic compound and the like followed by catalytic hydrogenation. In place of the conventional nickel catalyst, the hydrogena­ tion reaction in the inventive method is performed by use of a catalyst of a platinum group metal selected from the class consisting ruthenium, platinum, rhodium and iridium to give an advantage that the product oil according to the inventive method has a remarkably increased traction coefficient and a small temperature dependence thereof in comparison with conventional products.

Description: A METHOD FOR THE PREPARATION OF A FLUID FOR TRACTION DRIVE BACKGROUND OF THE INVENTION The present invention relates to a method for the preparation of a fluid for traction drive or, more particularly, to a method for the preparation of a fluid for traction drive having a remarkably increased traction coefficient. A fluid for traction drive is employed in a variety of traction drive apparatuses such as continuously variable transmissions. Along with the requirement for a smaller and more compact design, apparatuses of this type for power transmission are required to be capable of being driven at a high velocity and under a high load as a trend in recent years. Therefore, it is eagerly desired to develop a highperformance fluid for traction drive capable of withstanding severer and severer working conditions. Various compounds have been hitherto proposed as usable as a fluid for traction drive, of which those compounds having two or more naphthenic rings in a molecule are known to belong to a class of preferable ones. The inventors also have since long pertained extensively to the investigations for the development of a high-performance fluid for traction drive and proposed several compounds, of which it has been disclosed that a compound represented by the structural formula EMI1.1 in which each of the symbols R11 to R15 denotes a hydrogen atom or an alkyl group having 1 to 4 carbon atoms and each of the suffixes r, s and t is an integer of 1, 2 or 3, is particularly preferable as a fluid for traction drive with a remarkably large traction coefficient, in particular, at elevated temperatures. On the way of the development works of the above mentioned compound usable as a base stock of a fluid for traction drive, the inventors have become aware that the performance of the compound as a fluid for traction drive depends considerably on the conditions of the manufacturing process or, in particular, of the step of the hydrogenation reaction to give different values of the traction coefficient. SUMMARY OF THE INVENTION It is therefore an object of the present invention to provide a novel and improved method for the preparation of the compound represented by the above given general formula (I) and having a large traction coefficient with a remarkably small temperature dependence with reproducibility. Another object of the invention is to provide a method in which the compound represented by the general formula (I) can be imparted with a remarkably and reproducibly increased traction coefficient by virtue of the improvement in the conditions of the hydrogenation reaction or, in particular, proper selection of the catalyst used in the hydrogenation reaction. Thus, the method of the invention for the preparation of a compound represented by the above given general formula (I), i.e. a decahydronaphthyl- and cyclohexyl-substituted alkane compound, usable as a fluid for traction drive comprises hydrogenating a compound represented by the general formula EMI3.1 in which each of the symbols R1 to R8 denotes a hydrogen atom or an alkyl group having from 1 to 4 carbon atoms, X (R9)p (R10)q denotes a group of the formula or# R9 and R10 each being a hydrogen atom or an alkyl group having from 1 to 4 carbon atoms, and each of the suffixes k, 1, m, n, p and q is an integer of 1, 2 or 3, in the presence of a catalyst of a platinum group metal selected from the class consisting of ruthenium, platinum, rhodium and iridium. BRIEF DESCRIPTION OF THE DRAWING FIGURES 1 and 2 graphically show the traction coefficients of the compounds prepared in the Examples and Comparative Examples as a function of the temperature. DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS The compound represented by the above given general formula (II) or (III) and used as the starting material in the inventive method is a known compound and can be prepared by various methods. For example, tetrahydronaphthalene, naphthalene or a derivative thereof and styrene, vinylcyclohexane or a derivative thereof are reacted in the presence of an acid catalyst such as sulfuric acid and the like and separation of the reaction product by distillation under reduced pressure into fractions gives the desired compounds. Examples of the compounds represented by the general formula (II) or (III) are: 1-(5-(1,2,3, 4-tetrahydronaphthyl) )- l-phenyl ethane; 1- (6- (1,2,3, 4-tetrahydronaphthyl) ) -1-phenyl ethane; l-(l-naphthyl)-l-phenyl ethane; l-(2-naphthyl)-1- phenyl ethane; 2- (6- (1,2,3, 4-tetrahydronaphthyl) ) -2-phenyl propane; 1(6- (1,2,3, 4-tetrahydronaphthyl) ) -1-cyclohexyl ethane; benzyl naphthalene; l-methylnaphthyl-l-phenyl ethane; l-dimethylnaphthyl-l-phenyl ethane; 1- (6- (1,2,3, 4-tetra- hydronaphthyl))-l-(4-tert-butyl)phenyl ethane and the like. The compound represented by the general formula (I) can be prepared by the catalytic hydrogenation of the compound represented by the general formula (II) or (III). The catalyst used in this hydrogenation reaction is preferably a catalyst of a platinum group metal selected from the class consisting of ruthenium, platinum, rhodium and iridium and these active ingredients of the catalyst are, in most cases, supported on a conventional catalyst carrier such as silica, alumina, active carbon and the like although the form of the catalyst is not limited thereto. Preferable reaction conditions in the hydrogenation treatment include a reaction temperature in the range from 10 to 3000C, preferably from 50 to 2000C and a reaction pressure in the range from 1 to 200 kg/cm2G, preferably from 5 to 50 kg/cm2G. Examples of the compound represented by the general formula (I) as the reaction product of the inventive method are: l-(2-decahydronaphthyl)-l-cyclohexyl ethane of the formula EMI5.1 l-(l-decahydronaphthyl)-l-cyclohexyl ethane of the formula EMI5.2 1-(2-decahydronaphthyl)-1-(4-tert-butylcyclohexyl) ethane of the formula EMI5.3 1- (l-decahydronaphthyl) -I- (4-tert-butylcyclohexyl) ethane of the formula EMI5.4 l-dimethyldecahydronaphthyl-1-cyclohexyl ethane of either one of the formulas EMI6.1 and EMI6.2 l-methyldecahydronaphthyl-l-cyclohexyl ethane of either one of the formulas EMI6.3 and EMI6.4 2-decahydronaphthyl-2-cyclohexyl propane of the formula EMI6.5 l-decahydronaphthyl-l-cyclohexyl methane of the formula and the like. EMI6.6 The compound represented by the formula (I) obtained by the method of the present invention has a remarkably increased traction coefficient in comparison with those obtained by the hydrogenation using other conventional catalysts such as nickel and the like so that this compound is very excellent as a fluid for traction drive. The reason therefor is presumably that the decahydronaphthalene derivatives as the reaction product of the inventive method contain a predominant amount of the cis-isomeric molecules in respect of the configuration of the decahydronaphthalene nucleus in which the hydrogen atoms at the 9- and 10-positions are in the cis-orientation relative to each other. The compound obtained by the method of the invention can be used as such as a base stock of a fluid for traction drive having a large traction coefficient with a remarkably small temperature dependence thereof in a wide range of temperature. Therefore, traction drive apparatuses using the fluid prepared by the inventive method can be designed remarkably compactly and are capable of running even under very severe operation conditions of high temperatures and high loads so that they are applicable to a wide variety of machines such as continuously variable transmissions for automobiles and industrial machines and hydraulic machines. In the following, the present invention is described in more detail by way of Examples and Comparative Examples, in which the determination of the traction coefficients was performed using a two roller friction tester having two independently rotatable discs of the same size of 52 mm diameter and 6 mm thickness contacting with each other. These two discs were rotated at a constant velocity of 2000 r.p.m. and 1900 r.p.m. respectively under a contacting pressure of 70 kg load by means of a spring. By determining the torque using a strain gage and a torque meter from which the traction coefficient was calculated. Each of the discs was made of a bearing steel SUJ-2 and the surface thereof was finished by buffing using an alumina abrasive of 0.03 Vm particle diameter to have a surface roughness of Rmax = 0.2 pom. The temperature of the lubricating oil during measurement was varied in the range from 600C to l400C by heating the oil holder with a heater. Example 1 Into a glass flask of 3 liter capacity were introduced 1000 g (7.58 mole) of tetrahydronaphthalene and 300 g of concentrated sulfuric acid and the mixture was cooled at 00C on ice-sodium chloride bath. Then, 400 g (3.85 mole) of styrene were added dropwise into the mixture under stirring over a period of 3 hours followed by further stirring for additional one hour to complete the reaction. The mixture was kept standing and the separated organic layer was washed with 500 ml of a 1N aqueous solution of sodium hydroxide and followed by 500 ml of a saturated aqueous solution of sodium chloride, three times and dried with anhydrous sodium sulfate. The organic mixture was distilated under reduced pressure to give 750 g of a fraction boiling at 135 to 1480C under a pressure of 0.17 mmHg. The analysis of this fraction gave a result that the fraction was mainly composed of a mixture of l-(5-(l,2,3,4-tetrahydro- naphthyl))-l-phenyl ethane and 1(6- (1,2,3, 4-tetrahydro- naphthyl))-l-phenyl ethane. In the next place, a 500 g portion of the above obtained fraction was introduced into an autoclave of 1 liter capacity together with 50 g of an alumina-supported hydrogenation catalyst containing 0.58 by weight of platinum (a product by Japan Engelhard Co., Ltd.) and the hydrogenation reaction was performed for 4 hours at a reaction temperature of 2000C under a hydrogen pressure of 50 kg/cm2. After cooling, the reaction mixture was filtrated to remove the catalyst and the filtrate was analyzed after stripping of lighter matters to find that the hydrogenation reaction had proceeded to more than 99.9% and that the product was mainly composed of a mixture of l-(l-decahydronaphthyl)-l-cyclohexyl ethane andl-(2-decahydronaphthyl)-1-cyclohexyl ethane. This product had properties including a specific gravity of 0.94 (15/4 C), kinematic viscosities of 34 centistokes at 400C and 4.6 20 centistokes at 100 C and a refractive index n20 of 1.5040. The content of the cis-isomer therein was 71%. The traction coefficient of this product was determined in the temperature range from 600C to 1400C and the results are shown in FIGURE 1 of the accompanying drawing. Example 2 The experimental procedure was substantially the same as in Example 1 except that the platinum catalyst used in the hydrogenation reaction was replaced with 20 g of 5% ruthenium-carbon (a product by Japan Engelhard Co., Ltd.), the reaction temperature was decreased to l200C and the hydrogen pressure was decreased to 20 kg/cm2. The thus obtained product had properties including a specific gravity of 0.94 (15/40C), kinematic viscosities of 39 centistokes at 400C and 4.9 centistokes at 1000C and a refractive index n20 of 1.5048. The content of the cis-isomers was D 88%. The traction coefficient of this product is shown in FIGURE 1 as a function of the temperature in the range from 600C to 1400C. Example 3 The experimental procedure was substantially the same as in Example 1 except that the platinum catalyst used in the hydrogenation reaction was replaced with 15 g of 5% rhodium-carbon (a product by Japan Engelhard Co., Ltd.) and the reaction temperature was decreased to 800C. The thus obtained product had properties including a specific gravity of 0.94 (15/40C), kinematic viscosities of 37 centistokes at 400C and 4.7 centistokes at l000C and a 20 refractive index nD of 1.5047. The content of the cis- isomers was 86%. The traction coefficient of this product is shown as a function of the temperature in the range from 600C to l400C. Example 4 A mixture composed of l-(l-naphthyl)-1#phenyl ethane and l-(2-naphthyl)-l-phenyl ethane was prepared in the same manner as in the reaction of tetrahydronaphthalene and styrene described in Example 1 except that 1000 g of tetrahydronaphthalene were replaced with 1000 g of naphthalenc with further addition of 3000 ml of carbon tetrachloride. The thus obtained reaction product mixture was subjected to the hydrogenation reaction in the same manner as in Example 1 except that the platinum catalyst was replaced with 10 g of the same ruthenium catalyst as used in Example 2 with addition of 10 g of water, the hydrogen pressure was increased to 70 kg/cm2 and the reaction temperature was decreased to l500C. The thus obtained product had properties including a specific gravity of 0.94 (15/40C), kinematic viscosities of 38 centistokes at 400C and 4.9 20 centistokes at 100 C and a refractive index nD of 1.5050. The content of the cis-isomers was 83%. The traction coefficient of this product is shown in FIGURE 1 as a function of the temperature in the range from 600C to 1400C. Example 5 Dry hydrogen chloride gas was blown into 590 g of amethylstyrene contained in a glass flask of 1 liter capacity at room temperature under stirring to give 750 g of cumyl chloride. After, 2000 g of tetrahydronaphthalene and 70 g of titanium tetrachloride were introduced into a glass flask of 5 liter capacity, the mixture which was cooled at 00C on ice-sodium chloride bath and then a mixture of 300 g of tetrahydronaphthalene and 550 g of the cumyl chloride was added dropwise into the mixture in the flask under agitation over a period of 3 hours followed by further stirring for additional 1 hour to complete the reaction. The reaction mixture after the post-treatment in the same manner as in Example 1 was distilled under reduced pressure to give 400 g of a fraction boiling at 133 to l400C under a pressure of 0.03 mmHg. This fraction was identified by analysis to be mainly 2-(6-(1,2,3,4-tetrahydronaphthyl))- 2-phenyl propane. Thereafter, 400 g of this product were introduced into an autoclave of 1 liter capacity together with 30 g of the same ruthenium catalyst as used in Example 2 and the hydrogenation reaction was performed at l500C for 4 hours under a hydrogen pressure of 50 kg/cm2. After cooling and post-treatment undertaken in the same manner as in Example 1, the reaction product was analyzed to find that the hydrogenation reaction had proceeded to an extent of 99.9% or more and it was identified to be 2-decahydronaphthyl-2cyclohexyl propane. This product had properties including a specific gravity of 0.94 (15/40C), kinematic viscosities of 131 centistokes at 400C and 7.7 centistokes at l000C and a refractive index n20 of 1.5105. The content of the and cis-isomer was 90%. The traction coefficient of the product is shown in FIGURE 2 as a function of the temperature in the range from 600C to l400C. Comparative Example 1 The experimental procedure was substantially the same as in Example 1 except that the platinum catalyst used in the hydrogenation reaction was replaced with 50 g of a nickel catalyst for hydrogenation (Catalyst N-113, a product by Nikki Kagaku Co., Ltd.). The thus obtained product had properties including a specific gravity of 0.94 (15/40C), kinematic viscosities of 29 centistokes at 400C and 4.2 centistokes at l000C and a refractive index nD of 1.5025. The content of the cis-isomers was 42%. The D traction coefficient of this product is shown in FIGURE 1 as a function of the temperature in the range from 600C to 1400C. Comparative Example 2 The experimental procedure was substantially the same as in Example 4 except that the ruthenium catalyst used in the hydrogenation reaction was replaced with 50 g of the same nickel catalyst for hydrogenation as used in Comparative Example 1, the reaction temperature was increased to 2500C and the hydrogen pressure was increased to 100 kg/cm2. The thus obtained product had properties including a specific gravity of 0.93 (15/4 C), kinematic viscosities of 27 centistokes at 400C and 4.0 centistokes at 1006C and a refractive index n20 of 1.5020. The content of the cis D isomer was 35%. The traction coefficient of the product is shown in FIGURE 1 as a function of the temperature in the range from 600C to 1400C. Comparative Example 3 The experimental procedure was substantially the same as in Example 5 except that the ruthenium catalyst used in the hydrogenation was replaced with 50 g of the same nickel catalyst for hydrogenation as used in Comparative Example 1 and the reaction temperature was increased to 2500C. The thus obtained product had properties including a specific gravity of 0.94 (15/40C), kinematic viscosities of 120 centistokes at 400C and 7.4 centistokes at l000C 20 and a refractive index n20 of 1.5097. The content of the cis-isomer was 40%. The traction coefficient of the product is shown in FIGURE 2 as a function of the temperature in the range from 600C to l400C.

Claims: WHAT IS CLAIMED IS: 1. A method for the preparation of a fluid for traction drive comprising a compound represented by the general formula EMI15.1 in which each of the symbols R11 to R15 denotes a hydrogen atom or an alkyl group having from 1 to 4 carbon atoms and each of the suffixes r, s and t is an integer of 1, 2 or 3, which comprises catalytically hydrogenating a compound represented by the general formula EMI15.2 in which each of the symbols R1 to R8 denotes a hydrogen atom or an alkyl group having from 1 to 4 carbon atoms, X is a group expressed by the formula EMI15.3 or EMI15.4 R9 and R10 each being a hydrogen atom or an alkyl group having from 1 to 4 carbon atoms, and each of the suffixes k, 1, m, n, p and q is an integer of 1, 2 or 3, in the presence of a catalyst containing a platinum group metal selected from the class consisting of ruthenium, platinum, rhodium and iridium. 2. The method according to Claim 1, wherein the compound of the formula (I) is 1-(2-decahydronaphthyl)-1- cyclohexyl ethane of the formula EMI16.1 3. The method according to Claim 1, wherein the compound of the formula (I) is l-(l-decahydronaphthyl)-lcyclohexyl ethane of the formula EMI16.2 4. The method according to Claim 1, wherein the compound of the formula (I) is l-(2-decahydronaphthyl)-l- (4-tert-butylcyclohexyl) ethane of the formula EMI16.3 5. The method according to Claim 1, wherein the compound of the formula (I) is l-(l-decahydronaphthyl)-l (4-tert-butylcyclohexyl) ethane of the formula EMI16.4 6. The method according to Claim 1, wherein the compound of the formula (I) is l-dimethyldecahydronaphthyl l-cyclohexyl ethane of either one of the formulas EMI17.1 and EMI17.2 7. The method according to Claim 1, wherein the compound of the formula (I) is l-methyldecahydronaphthyl-lcyclohexyl ethane of either one of the formulas EMI17.3 and EMI17.4 8. The method according to Claim 1, wherein the compound of the formula (I) is 2-decahydronaphthyl-2cyclohexyl propane of the formula EMI17.5 9. The method according to Claim 1, wherein the compound of the formula (I) is decahydronaphthyl cyclohexyl methane of the formula and the like. EMI18.1 10. The method according to Claim 1, wherein the hydrogenation reaction is carried out at a temperature of from 10 to 3000C and a pressure of from 1 to 200 kg/cm2G. 11. The method according to Claim 1, wherein the hydrogenation reaction is carried out at a temperature of from 50 to 2000C and a pressure of from 5 to 50 kg/cm2G.

Inventors: SHIMIZU, NOBUAKI, TSUBOUCHI, TOSHIYUKI
Applicants: IDEMITSU KOSAN COMPANY LIMITED
Application year: 1985
Main classification: C07C13
IPC codes: C10N40, B01J23, C07C13, C10M105, C07C1, C07C5, C07C67, C07B61, C07C2, C10N30, C10N60