Process for making collagen membranous materials for medical use

Abstract: Collagen membranes with desired properties are prepared by using a variety of gel-forming techniques in combination with a method for converting the gels to solid forms which involves disrupting and centrifuging a matrix, harmonizing the precipitate auto or paste and casting and drying the paste. The properties of these membranes or other solid forms may be further altered by cross-linking the collagen preparation either after formation of the membrane or gel, or most preferably by mixing cross-linked collagen with solubilized collagen in the original mixture used to create the gel.

Description: The invention relates to the field of materials useful for repair of tissue and relevant to wound healing. More precisely, the invention relates to a collagen membranous material prepared by a novel process, which membranes are biocompatible, noninflamatory, and useful in the repair of tissue as artificial implants. Numerous attempts have been made to obtain artificial membranes which can be used as substitutes for skin blood vessels, ligaments, or other connective tissue. Many of these membranes utilize collagen, as collagen is the major component of connective tissue in general. An extensive literature exists with respect to methods for preparing such membranes, either of collagen alone, (see, for example, US-A-4,412,947; Japanese JP-A-74/039174; and US-A-4,242,291) or of collagen in combination with other materials (see, e.g., US-A-4,453,939). Other membranes use combinations of materials such as glycoproteins with fibrinogen and thrombin (EP-A-92200), and a combination of keratin derived and glucosaminoglycan polymers EP-A-89152. The properties and quality of the resulting membranes with respect to physical characteristics useful in the particular application intended, and their biological characteristics, such as biocompatibility, stability, and integration with surrounding tissue are determined by the nature of the material, e.g. the nature of the collagen used to form the membranes, and on the process used in their formation. The membranes in the art have had variable success for their intended uses, which include cornea replacements, artificial skin, and wound healing. Many cause inflamation, and have less than optimum properties of flexibility, biological stability, and strength. In US-A-2934447 reconstituted leather is formed from a mixture of partially tanned collagen fibres on the one hand and a collagen solution on the other. The solution is sometimes described as a gel. The present invention offers a process whereby desirable properties can be obtained in the resulting membrane through the use of nonimmunogenic collagen formed into a membranous material by a process which offers flexibility in the physical properties of the product, so as to permit these properties to be adapted to intended use. The membranous material can be used as a "two-dimensional" membrane, including membranes which can be shaped to form tubular vessels, shaped into a three-dimensional implant, or formed into a "one-dimensional" fiber. The invention provides collagen membranous material whose physical properties are designed to be suitable for uses in a variety of medical applications including blood vessel repair, uterus repair, reconstruction of lumen surfaces, tendon replacements, and artificial skin. The membranes may also be used as substrates for production of desired cell cultures in vitro . The properties of the membranous material are determined by appropriate selection from a spectrum of preparation processes so as to obtain those characteristics appropriate for a selected use. Similar flexibility is available in the properties of the one- and three-dimensional constructs prepared by modification of, or additions to, the membrane preparation process. The resulting fibers are useful as replacement materials for tendons or ligaments, and may also be used for suturing; the three-dimensional blocks or solids provide implants for use in tissue repair or wound-gap closure. Thus, in one aspect, the invention relates to a process for making collagenous membranous materials by obtaining a gel e.g. from a solution of atelopeptide collagen, optionally mixed with a suspension of cross-linked collagen, and converting the gel into membrane form. In another aspect the invention relates to fibers or solids prepared from the gel. In still another aspect, the invention relates to the specific methods used within the context of the general process to obtain "two-dimensional" membranes, "one-dimensional" fibers, and three-dimensional solids of desired properties. The gel may be obtained from solubilized collagen or mixture by three alternative approaches. In one approach, the solution of collagen is treated with a precipitating buffer which insolubilizes the collagen by raising the pH. In this approach, both collagen and buffer solutions are precooled almost to freezing, mixed, and then allowed to incubate at approximately room temperature to induce gel formation. In a second approach, the above mixture of collagen and buffer is centrifuged, rather than incubated without gravitational pressure, and the supernatant from the centrifugation is recovered and allowed to incubate at approximately room temperature. In a third approach, the solution of collagen is treated with an insolubilizing solution at ambient temperature, and the insolubilizing solution is designed to bring the resulting mixture to physiological pH and ionic strength. This mixture is then allowed to incubate at approximately 37°C to create the gel. The third approach may be modified by degassing the mixture immediately upon mixing, and placing the degassed mixture into a mold before incubation. The procedure in each of the three cases recited above may also be applied to formation of a gel which includes, in addition to the dissolved collagen, a suspension of a cross-linked form. The presence of this additional cross-linked substrate permits further variation in the properties of the membrane material which ultimately results from the method of the invention. The procedure set forth above for formation of the gel to include the cross-linked collagen in the starting material appears to be critical in the sense that formation of the gel from solubilized collagen alone, followed by partial cross-linking, or cross-linking of the membranes after their formation from the gel, appears to result in a more brittle and unsatisfactory product. Also, if the gel formation procedure from solubilized collagen is modified by the aforementioned addition of cross-linked material, the third method recited is preferred, i.e., the solution of collagen (containing, in admixture, the desired cross-linked material) is treated with an insolubilizing solution at ambient temperature wherein the insolubilizing solution is designed to bring the mixture to physiological pH and ionic strength. The mixture is allowed to incubate at about 37°C to create the gel. In a particularly preferred embodiment, the mixture is degassed before adding the insolubilizing solution. The conversion of the gel to a membranous material is accomplished by disrupting the gel, the disrupted gel being then centrifuged to obtain a precipitate, and the precipitate cast into molds and dried. Depending on the dimensions and shape of the mold, either a "two-dimensional" membrane or three-dimensional solid can be obtained. Another method for this conversion is seen in EPA 85309194.0 (0187014) from which the present application is divided. Modes of Carrying Out the Invention A. Preparation of CIS The process of the invention may start with a collagen in solution, either alone, or in admixture with cross-linked fibrillar collagen. The collagen may be solubilized and purified from mammalian connective tissue, and has been prepared from bovine skin, porcine skin, and mammalian bone, along with a number of other sources. Purification processes are well known in the art. See, for example, US-A-3,949,073, US-A-4,066,083, and GB-A-1,565,340. Collagen can be readily solubilized in concentrations useful in the invention by disrupting the fibers in acid, is is well known in the art, and is dissolved at pH values between 1-4. Indeed, collagen in solution (CIS) is commercially available, conveniently, under the trademark Zygen® from Collagen Corporation, Palo Alto, California. Native collagen exists in a fibrillar form which results from the triple helical structure of the peptide chains. The helical structure is generated by virtue of repeating triplet sequences composed of glycine linked to two amino acids, commonly proline and hydroxyproline in the amino acid sequence. The regions of these triplet repeating units aggregate themselves into triple helical structures. In addition, all collagen chains contain regions at each end which do not have the triplet glycine sequence and are thus not helical. These regions are thought to be responsible for the immunogenicity associated with most collagen preparations, and are called telopeptides. The immunogenicity of a collagen preparation can, in large part, can be mitigated by removal of these telopeptides to produce "atelopeptide collagen". The removal is accomplished by digestion with proteolytic enzymes such as trypsin or pepsin. The nonhelical telopeptide regions are also required to form the cross-links which are responsible for stability of the fibrillar structure in the native material. Atelopeptide collagen must be cross-linked artificially, if it is desired to obtain this characteristic. The collagen in solution which may form the starting material for the process of the invention is an atelopeptide collagen, preferably a dilute commerically available product such as Zygen® CIS. Concentrations of collagen in the range of 1-10 mg/ml are suitable for use in the invention. This range is, of course, suggestive of suitable concentrations and not meant to represent an absolute limitation; any upper and lower limit is arbitrary in this context. B. Preparation of Cross-Linked Collagen As used herein, "cross-linked collagen" refers to an atelopeptide purified reconstituted collagen preparation which has been artificially cross-linked by chemical or radiation treatment or by other appropriate means to obtain sufficient cross-links that the viscosity of the preparation is 700-3000 mPa.s (centipoise) when measured at 22°C and a shear rate of 5000 sec⁻¹. Again, precise limits are arbitrary and this is illustrative of a useful range. To prepare the cross-linked form, solubilized collagen is first precipitated by neutralizing at room temperature or a preparation of precipitated or reconstituted collagen, such as Zyderm® collagen implant is used, and then cross-linked using standard procedures, including reactivity with chemical cross-linking reagents, such as formaldehyde, glutaraldehyde, glyoxal, and so forth, or with ionizing radiation such as gamma ray radiation. Heat and UV radiation can also be used, but are less efficient. The cross-linked material is then collected by centrifugation and washed with a suitable aqueous solution, such as physiological saline, and the concentration adjusted to a workable level in suspension of 1-10 mg/ml. In more detail, the cross-linking agent is a polyfunctional, and more usually bifunctional, compound which is used in concentration to produce a viscous, covalently cross-linked collagen before quenching with an agent which forms an innocuous, water-soluble adduct with the cross-linking agent. The concentration of the collagen in the suspension during the reaction, the concentration of cross-linking agent, and the duration of the cross-linking reaction are significant, but dependent on the nature of the cross-linking agent. The collagen concentration is typically in the range of 0.1-10 mg/ml, more usually 1-5 mg/ml. Aldehydes are preferred as cross-linking agents, and suitable aldehydes include formaldehyde, glutaraldehyde, acid aldehyde, glyoxal pyruvic aldehyde, and aldehyde starch, but preferably glutaraldehyde. Amines are preferred quenching agents, in particular, glycine. The concentration of glutaraldehyde, if this is the selected cross-linker, is typically 0.001%-0.05% by weight/volume, and the cross-linking reaction takes place over about one-half hour to one week. The reaction is carried out at 10°C-35°C before adding the quenching agent in at least stochiometric proportions with the cross-linking agent, although an excess is preferred. One exemplary cross-linking protocol includes a collagen concentration of 3 mg/ml and 0.01% by weight glutaraldehyde for about 16 hours at 22°C. The cross-linked product is washed to remove unreacted cross-linker, polymers formed by the cross-linker, and the unreacted quenching agent, if quenching is employed. A workable buffer is a sodium phosphate/sodium chloride buffer solution of approximately pH 7. The washed product may be concentrated by filtration or centrifugation to a suitable protein concentration range, which is typically 20-50 mg/ml, preferably 25-40 mg/ml. The washed product should have an aldehyde content of less than about 20 ppm and a viscosity in the range of 700-3000 mPa.s (cp) at 22°C measured by an oscillating disc viscosimeter, which measures dynamic, not steady flow, viscosity (Nametre Company, Model 7.006PBD). C. Formation of the Gel The process for forming collagen membranes or related membranous materials, comprises, basically, two steps: the formation of a gel from a collagen in solution, and thus according to the invention the conversion of the gel to the membrane or other desired form. Each of these steps may be performed in a spectrum of temperature, gravitational, and ionic strength conditions, and the intermediate solutions may or may not be degassed, and the resulting product will have properties which vary accordingly. The temperature at which gel formation takes place may be between approximately 4°C and approximately 37°C; the ionic strength may vary between about 0.05 to about physiological ionic strength, and the gravitational field conditions may vary from 1 x g to about 13000 x g. The exemplary processes set forth below typify the extremes of these variables, and it is understood that intermediate cases may also be useful, depending on the nature of the membrane desired. Degassing and molding prior to formation of the gel appears to result in a tougher product, which can be further manipulated to form a fiber, membrane or solid. Three general approaches may be used, as is outlined above. In the first, Zygen® CIS is cooled and mixed with precooled buffer at an ionic strength well below physiological, preferably about 0.05, and the mixture incubated at low temperature. In the second, the CIS is mixed with buffer at physiological ionic strength and temperature conditions and incubated at physiological temperature. In a third approach, the CIS is treated with buffer as in the first method, but subjected to gravitational pressure before incubating at room temperature. The gel may optionally contain an arbitrary amount of previously cross-linked collagen material which is itself prepared from solubilized collagen. The relative amounts of cross-linked and noncross-linked collagen materials appear to determine the properties of the resulting membranes, as well as do the conditions for formation of the gel and membrane stages. The formation of the gel and the conversion to membranes utilizes the same set of options, whether or not the cross-linked material is included in the original composition. In forming the gel, as the intermediate material to the final membranous product to include the cross-linked fibrillar collagen, the gelling procedure is conducted as outlined above, except that, in addition to the collagen in solution, a portion of the suspension containing the cross-linked form at the above-mentioned suspension concentration levels is mixed with the solubilized collagen. The ratio of the two components, based on the relative weights of the collagen contained in each, is quite broad, depending on the nature of the final product desired. For softer and more flexible compositions, a greater proportion of collagen in solution is used; for tougher membranes as final products, a greater concentration of the cross-linked form is used. For example, if the membrane final product is to be used as an artificial tendon to hold sutures or to form a tubular vessel held together by such sutures, a cross-linked collagen percentage of 40-80%, preferably around 50%, is preferred. All compositions of membranes formed wherein the original mixture for gel formation contains both a suspension of cross-linked collagen and collagen in solution are expressed as a percentage by weight of cross-linked collagen to total collagen content. Thus, when a membrane is described as having 10% cross-linked collagen, the original components were supplied such that 10% of the total weight of collagen was contained in a cross-linked collagen suspension and 90% was supplied as soluble collagen in solution. The compositions of the invention may contain up to 90% cross-linked collagen. D. Conversion to the Membrane The conversion of the gel to a membranous material effected by disrupting the gel matrix, centrifuging the disruptate to recover a precipitated collagen, homogenizing the precipitate into a paste, and casting the paste with a mold. The product of disrupting the gel followed by precipitation of the disruptate, is relatively brittle and semitransparent, has a rough surface, and is relatively thick. The membranous material can be characterized as a random fibrillar network wherein the fibrils are approximately of the diameter 70-300 nanometers, and approximately 0.5-5 µm in length. The inclusion of cross-linked collagen does not change these properties, except to toughen the product. The cross-linked material is embedded in the fibrillar network described. The process which utilizes disruption of the gel typically is conducted by mechanically disrupting the matrix, such as with a spatula, followed by centrifugation at approximately 8000-16000 x g, preferably about 13000 x g for about 20-30 minutes to obtain the precipitate. The force of centrifugation is, of course, variable and no definite boundary limitations can be set. The precipitate is then homogenized sufficiently to form a pastelike material, at room temperature, and the paste is cast into a mold and allowed to set at atmospheric pressure at low temperature (below about 37°C). The dried material is then desalted, if desired, by washing in water, and redrying. Cross-linking of the collagen in the resulting membranous material is optional, but can effected by treating the membranous material with glutaraldehyde to obtain the desired cross-links; however, as set forth above, this approach may result in a more brittle product. Procedures for this cross-linking are known in the art. Briefly, in typical procedures, the material is treated with a solution containing 0.05-1% glutaraldehyde for 1-16 hours, and then quenched by addition of a glycine solution to a concentration of 0.1-0.4M glycine. The cross-linking solution is then removed by washing. E. Utility The resulting materials may be employed in the soft tissue repair constructions ordinarily utilizing artificial membranes, such as burned skin replacements, tendon reconstruction, or wound repair. They may also be shaped into various forms and used in connection with hard tissue repair. The cast or compressed membranes may be reformed into three dimensional objects for implantation in replacing sections of bone by rolling into cylinders, or by stacking and cutting to shape. The membranes may also be used in their two dimensional configuration by successively packing the membranes into a defect, such as a cranial or peridontal cavity. In general, onlay-type repair may be done by stacking these membranes into the cavity. Examples The following examples are intended to illustrate, but not to limit the invention. Examples 1-3 represent similar gel forming methods, followed by membrane formation using the disruptate, all starting with CIS alone. Example 4 illustrates formation of cross-links in the resulting membranes. Example 5 shows the formation of a gel which includes a portion of cross-linked collagen, and Example 6 illustrates the conversion of this gel into a membrane. Example 1 90 ml Zygen® (2 mg/ml bovine atelopeptide collagen, in HC1, pH1-4) CIS was cooled to 4°C, and mixed with 10 ml of precooled buffer containing 0.2 M Na₂HPO₄/0.09 M NaOH. The solution was mixed at 4°C, and incubated at room temperature for about 16-20 hours, ie. overnight, for convenience. The gel matrix was broken with a spatula, transferred to a centrifuge bottle, and centrifuged at 13000 x g for 30 minutes. The resulting precipitate was recovered and homogenized into a paste form. The paste was cast into a mold and dried in air at 37°C, then washed with water and redried in air at 37°C to give the membrane P-1. Example 2 90 ml of Zygen® CIS at ambient temperature was mixed with 10 ml of room temperature buffer containing 0.2 M Na₂HPO₄/1.3 M NaC1/0.09 M NaOH, and the mixture incubated at 37°C overnight. The gel was then converted to a membrane using the procedure exactly as set forth in Example 1. The resulting membrane was designated P-2. Example 3 90 ml of Zygen® CIS was cooled to 4°C, and mixed rapidly with 10 ml cold (4°C) buffer containing 0.2 M Na₂HPO₄/0.09 M NaOH, and transferred immediately to centrifuge bottles. The mixture was centrifuged at 8000 x g for 2 hours at about 20°C, and the supernatant recovered from the bottles. The supernatant was incubated at 20°C for overnight, resulting in the gel. The gel was converted to a membrane as set forth in Example 1. The resulting membrane was designated P-3. Example 4 90 ml Zygen® CIS at ambient temperature was mixed with 10 ml buffer which contained 0.2 M Na₂HPO₄/1.3 M NaC1/0.09 M NaOH, and the mixture incubated at 37°C overnight. The resulting gel was broken with a spatula, transferred to a centrifuge bottle, and centrifuged at 13000 x g for 30 minutes. The precipitate was recovered and homogenized to a paste. The paste was cast into a mold and dried in air at 37°C, and the resulting membrane washed with water. The washed membrane was then treated with a 0.1% solution of glutaraldehyde dissolved in water at 20°C and the cross-linked membrane washed and dried into yield membrane XP-2. Example 5 A. Preparation of Cross-Linked Collagen Fibrous collagen was reconstituted from collagen in solution (a 3 mg/ml solution of atelopeptide bovine collagen in dilute aqueous HCl, pH 1-4) by adding 0.02 M disodium phosphate to the solution at 18-20°C to obtain a pH of 7.4, and allowing fibers to form for 1-2 hours. To 160 ml of the resulting fibrous collagen suspension, 1.62 ml of 1% aqueous glutaraldehyde at pH 3 was added. The glutaraldehyde solution was added gradually with stirring to obtain a final concentration of 0.01% glutaraldehyde, and the mixture was allowed to react for 16 hours at room temperature before quenching by the addition of 3 M glycine to 0.2 M. After a 1 hour quench time, the cross-linked collagen was washed 3 times with approximately 100 ml of a buffer which contains 0.02 M disodium phosphate, 0.13 M NaCl, pH 7.4, with centrifuging at 17,000 x g for 5-7 minutes between each wash. The dynamic viscosity of the collagen was measured by an oscillating disc device (Nametre Company, Model 7.006PBD) measured at a shear rate of about 5,000 sec⁻¹, and found to be approximately 700 cp at 22°C. After the final wash and centrifugation, the collagen was resuspended in the above buffer to obtain a protein concentration of about 30 mg/ml. B. Preparation of the Gel Ten ml of the suspension of ¶A was mixed with 80 ml Zygen® CIS and the thoroughly mixed components were degassed under a vacuum. To the degassed mixture was added 10 ml of room temperature buffer containing 0.2 M Na₂PO₄/1.3 M NaCl/0.09 M NaOH, and the mixture was incubated at 37°C overnight. The resulting gel contains 55.5% cross-linked collagen by weight. Example 6 The cross-linked collagen preparation prepared as in ¶A of Example 5 is used in a ratio of 1:8 to collagen in solution (using a 1:8 mixture of cross-linked to CIS collagen as the starting material), and subjected to the process of Examples 1, 2 and 3, to obtain membranes designated PX-1, PX-2 and PX-3. Variations in the percentage of cross-linked collagen in the product are also obtained by varying the proportions of the suspension of Example 5A to the CIS.

Claims: A process for preparing a collagen membranous material which process comprises: disrupting a collagen gel matrix, centrifuging the disrupted matrix at 8000-16000 x g for about 20-30 minutes, homogenizing the resulting precipitate into a paste, casting the paste into a mold, and drying the cast paste at a temperature less than 37°C. A process according to Claim 1 wherein the centrifuging is carried out at about 13000 x g. A process according to Claim 1 or Claim 2 which further includes cross-linking the membranous material with glutaraldehyde. A process according to Claim 1 or Claim 2 wherein the gel is formed from collagen in solution mixed with a suspension of cross-linked collagen to obtain a percentage of cross-linked collagen of up to 90% by weight. A process according to Claim 1 or Claim 2 wherein the gel is formed by: cooling collagen in solution, optionally mixed with a suspension of cross-linked collagen to obtain a percentage of cross-linked collagen of up to 90% by weight, to approximately 4°C, treating the cooled solution with a buffer solution precooled to approximately 4°C, to obtain a mixture with a pH of approximately 7 and an ionic strength of approximately 0.05, and incubating the mixture at about 20°C for 16-20 hours. A process according to Claim 1 or Claim 2 wherein the gel is formed by: mixing at ambient temperature collagen in solution, optionally mixed with a suspension of cross-linked collagen to obtain a percentage of cross-linked collagen of up to 90% by weight, with sufficient salt/buffer solution to obtain a mixture with a pH of approximately 7 and approximately physiological ionic strength, and incubating the mixture at about 37°C for 16-20 hours. A process of Claim 1 or Claim 2 wherein the gel is formed by: precooling collagen in solution, optionally mixed with a suspension of cross-linked collagen to obtain a percentage of cross-linked collagen of up to 90% by weight, to about 4°C, mixing the cooled collagen in solution with a buffer solution, precooled to about 4°C to obtain a mixture with a pH of approximately 7 and ionic strength of about 0.05, and centrifuging the mixture at 8000 x g-13000 x g for 1-2 hours at about 20°C, immediately after mixing to obtain a supernatant, recovering the supernatant, and incubating the supernatant at about 20°C for 16-20 hours. A membranous collagen material prepared by the process of any one of the preceding claims.

Inventors: CHU GEORGE, CHU, GEORGE
Applicants: COLLAGEN CORP, COLLAGEN CORPORATION
Application year: 1985
Main classification: C08L89
IPC codes: A61F2, C08L89, A61L26, A61L27