QUANTUM-COUPLED DEVICE

Abstract: A new genus of electronic devices, wherein at least two closely adjacent potential wells (e.g. islands 10, 12 of GaAs in an AlGaAs lattice 11) are made small enough that at least two components of momentum of carriers within the wells are discretely quantized. This means that, when the bias be­ tween the wells is adjusted to align energy levels of the two wells, tunneling will occur very rapidly, whereas when energy levels are not aligned, tunneling will be greatly reduced. This high-gain mechanism leads to useful electro­ nic device functions.

Description: Background and Summarv of the Invention The present invention relates to electronic devices. It is generally recognized that conventional VLSI integrated technical technology will be prevented from further scaling by the time MOS devices get down to a quarter micron channel lenqth, and perhaps even at much larger geometries. Since much of the advance in integrated circuit capabilities has been based on the continued progress of scaling, this near-future barrier is of substantial concern. Thus it is an object of the present invention to provide an integrated circuit technology wherein active devices can have active regions smaller than one quarter micron in dimension. It is further object of the present invention to provide an integrated circuit technology wherein active devices can be fabricated which occupy a total area of less than k of a square micron average for each active device. A further inherent limitation of conventional integrated circuit technology is speed. MOS devices have inherent limits on their speed due to the channel-length transit time. Intergr able bipolar devices also have inherent speed limitations, due to the base width transit time, and are also likely to have high power dissipation. Thus it is an object of the present invention to provide an active device having higher potential maximum speed than any MOS device. It is a further object of the present invention to provide an active device which is potentially faster than anv bipolar device. It is a further object of the present invention to provide an active device which is potentially faster than any bipolar device, and which also has a very low power dissipation. To achieve these and other objects, the present invention provides: An electronic device comprising: first' and second potential wells each comprising an island of a semiconducting material having a minimum dimension less than 500 Angstroms and another dimension less than 1000 Angstroms; a barrier medium interposed between said first and second wells wherein the minimum potential energy of carriers is at least 50 millielectronvolts higher than the minimum potential enerqv of carriers within said wells, said wells being physically separated by a distance which is less than three times the smallest physical dimension of either of said wells; means for inputting carriers into said first well; and means for removing carriers from said second well. BRIEF DESCRIPTION OF THE DRAWINGS The present invention will be described with reference to the accompanying drawings, wherein: Figures 1A and 1B show spacing and energv levels of potential wells in a simple sample embodiment; Figure 2 shows the structure of Figure 1, biassed to permit resonant tunnelling; Figure 3 shows the structure of Figure 1, biassed at a lower voltaqe than shown in Figure 2, so that resonant tunnelling is forbidden; Figure 4 shows voltage-current characteristics of the structure of Fiqure 1; Figure 5 shows the energv levels of an embodiment using moderatelv large wells, wherein the upper-lying energy levels are more closely spaced, Figure 6 shows the electronic structure of an embodiment including input and output contacts; ; Figure 7 shows the energv levels of an embodiment using a#proximately sinusoidal well boundaries, wherein the energy levels are more equallv spaced; Figure 8 shows a three-terminal quantum-well device according to the present invention; Figure 9 shows another three-terminal quantum-well device according to the present invention, wherein multiPle chains of quantum-well pairs are connected in Parallel; Figure 10 shows a cross-section of the device of Fiqure 9; Figure 11 shows a manv-terminal device, which differs from the device of Figure 9 in having multiple electrodes 208 prime for connection to multiple wells 204 prime in each chain; ; Figure 12 shows a sample set of bias conditions for the embodiment of Figure 13 wherein resonant tunnellinq occurs, and Figures 13 shows a sample set of bias conditions for the embodiment of Figure 11 wherein resonant tunnelling does not occur; Fiqure 14 shows a read-onlv memory according to one embodiment' of the invention; Figure 15 shows a sample output switch configuration used in practicinq the present invention, wherein quantum-well devices switch macroscopic output currents; Figure 16 shows the effect of the electric potential change induced by the population of well levels on the termissible tunnelling transitions in a further class of embodiments; ; Figure 17 shows an AND gate configured using quantum-well logic with self-consistent tunnelling restrictions, and Figure 18 shows a more complex logic element configured using quantum-well logic with self-consistent tunnelling restrictions; Figures 19 and 20 show two embodiments of vertical-tunnelling quantum-well device structures according to the invention; and Figures 21-36 show steps in processing a sample three-terminal device according to the present invention. DESCRIPTION OF THE PREFERRED EMBODIMENTS The present invention teaches active devices which are fundamentally different from the transistor and diode structurestwhich have been used heretofore in the electronics industry to configure integrated circuits. That is, active devices taught by the present invention are neither field effect transistors nor bipolar transistors, but operate according to Principles which are fundamentallv and entirely different. A key feature of many embodiments of the invention is a pair of closely coupled quantum wells which are each extremelv small, so small that their electron populations are auantized, i.e. an electron in a well can only have one of a few allowable energies. The present invention teaches modes of device operation which cannot be analyzed by classical physics7 but must be understood in light of auantum mechanics. Advances in semiconductor processing now permit semiconductor structures to be patterned with exceedingly small dimensions, comparable to the Bloch wave length of an electron. (The Bloch wavelength measures the "width" of an electron in a semiconductor. The location of an electron must be measured by a Drobability distribution, which has a certain width.) The present invention makes use of the availability of patterned structures in dimensions which are close to the Bloch wave length to achieve new tvpes of device structures, capable of new principles of operation of a kind not seen before in semiconductor or integrated circuit devices. A simplified sample embodiment, which demonstrates some of the key principles of operation used in the Dresent invention, is shown in Figure 1. Separate wells of gallium arsenide are embedded in a matrix of aluminum gallium arsenide. As is well known in the semiconductor art, the bandgap of AlGaAs is wider than that of GaAs. (More preciselY, the Dseudo-binary alloys of the formula AlxGai-xA.s are all semiconductors, with a bandnap which increases as a function of x.) This different bandqaD means that conduction-band electrons in the lattice see a lower potential energy in the GaAs reqions than in the AlGaAs regions. A particular advantage of this material system is that the interface between GaAs and AlGaAs is a very well behaved one, that is such interfaces can be fabricated with an extremely low density of surface states (less than the Si/Si02 interface), and can preserve lattice match almost Perfectly between the GaAs and the AlGaAs sides of the interface. However, as will be discussed below, the Present invention can be practiced with a wide variety of material systems, and not only semiconductors. In the sample embodiment of Figure 1, the wells 10 are about 125 angstroms wide, and the spacing between the wells is also about 125 angstroms. The dimensions of these we ] ls are small enough that the energy states of electrons in the well will be quantized. That is, these#wells are Preferable made cubic, and the allowable energy states of an electron in a cubic well of such dimensions can be calculated easily, using the effective mass approximation for the behavior of the electron, as a simple particle in a box problem in quantum mechanics. Thus, for example, for the well dimensions given above, and an aluminum concentration of 35%, there exist four allowable energy states, and the lowest lving energy state will be above the bottom of the GaAs conduction band minimum and will be separated from the next lowest energv state by .070 electron volts. The next higher lying energy state will lie another .114 electron vo ] ts higher. Note that these energy states must be treated as quantized. That means that the energy of an electron in the well must be exactly equal to one of these permitted discrete energv levels and cannot take any other value. This is key to the present invention. Note that this is a fundamental difference from normal sem'conductor devices (even from the advanced semiconductor devices projected to be achievable by scaling present semiconductor devices), in that all conventional solid state devices - be they field effect or bipolar transistors or anything else - require that the energy levels of an electron within the conduction band of the semiconductor be quasi - continuous. It should be noted that the number of electrons which can populate each energy level in such a quantized system is strictly limited. That is, the lowest lying energy level in each well in this example can be populated bv only two electrons, the next level up can be populated by only six electrons, the next level up can be populated bv only ten electons, and so on. This means that the number of carriers within a well is strictly limited. Thus, a carrier cannot tunnel to an enerqv state in the next well if that energv state is already completely filled. While each well can hold only a few carriers at a time, it should be noted that the transition times are expressly short (tyticaily far less than a pico-second), and total current can be increased by operating many Dairs of wells in parallel. Now, in the sample embodiment the wells are place sufficiently close such that the probability density of an electron in one well extends into the neighboring well; that is, the wells 10 and 12 in Figure 1 are close enouqh together that electrons can tunnel between them easily. In tarticular, as shown in Fiqure lb, an electron in the first well can tunnel easily to a state of equal energy in the second well, but of course it cannot do this unless an unoccupied state having the same enerqy actually exists in the second well. However, suppose that the energy levels in the two wells do not line up. Then an electron in the first well can only tunnel to states of the second well which have a different energy than the first well, and it can onlv tunnel to such states if there is also some mechanism whereby the electron can lose or gain enough energy to reach the energy of the lower-lying available state in the second well. The chief mechanism for the chanqinq of the energy of an electron to achieve tunnelling in this fashion is relaxation via surface states. That rs, even the GaAs to #lGaAs interface, which is exceedinglv benign as semiconductor interfaces go, will have a measurable density of surface states at the interface. Such surface states provide a scattering process which will permit an electron to transfer to higher or lower energy, if it intersects one of the available sites for scattering. That is, the interface can be described as having an areal density of scattering sites which are capable of changing the energy from an electron so that it can make the transition between wells even when the energy levels of the wells do not line up. This mode of transition is known as inelastic tunneling. The alternative mode of tunneling, wherein the electron tunnels from the first well to the second with no change in energy, is known as resonant tunneling. Tunnelino requires conservation both of energy and also of momentum. Momentum is also quantized for small potential wells. That is, in each dimension of the box which defines the boundaries of the potential well, the smaller the length of that dimension the more widely spaced the allowable values of that component of momentum will be Thus, as reported in the *sooner et al. article cited below, resonant tunnelinq can occur between two very closelv spaced thin sheets of lower Potential. Since the potential wells are verv larqe in two dimensions, the momentum components in those two dimensions are not quantized. That is, when one dimension of a potential well is large, the momentum components in that direction are so closely spaced that a background lattice phonon will be available to supply the momentum difference. That is, the density of phonons found in the lattice follows Bose-Einstein statics, i.e. the number of phonons found in the lattice at energy E in a background lattice temperature T varies as 1 over (EXP ((E/k T)-1)). This energy distribution of phonons also implys a distributipn for the magnitude of momentum of the phonons, and, since the phonons can be treated as approximatelv isotropic in reasonable semiconductor materials, this same distribution also specifies the distribution of phonons having a desired value of some one particular component of momentum. Thus, the quantization of momentum in a potential well can be considered as discrete or cuasi-continuous only in relation to temperature. That is, for example, a 1000 anastrom wide box will result in momentum quantization at one degree Kelvin, since the phonon population will be crowded into energetically low states, but at 300R there would be a tremendous lattice background phonon population to bridge gaps between the allowable momentum values, and thus the separation between the allowable momentum values in this direction would not be meaningful, i.e. momentum in this direction would have to be treated as a quasi-continum value, i.e. any value of this momentum component which an incominq carrier had would still permit tunneling, since lattice phonons could adjust this momentum component to one of the allowable values. If all three components of momentum are discretely quantized, then it follows that energy must be discretely quantized also. The quantization of energy levels is (to a rough approximation) merely dependent on the volume of the potential well, so that a thin flat potential well could have quantized energy states and sharply separate discrete allowable levels for one component of momentum, whereas the allowable values of the other two momentum components will be closely spaced, so that thev impose no practical constraint on tunneling. That is, the resonant tunneling gain is enhanced in accordance with the number of parameters which must be met. In tunneling between two closely spaced cubic Potential wells, all three components of momentum (and therefore energy) must match between the state which the carrier is leaving intthe first well and the state which the carrier is entering in the second well. That is, if an incoming carrier does not satisfy all three momentum constraints, the chances of it finding a lattice phonon which has exactly the right components to satisfy the difference in each of the three momentum values is auite small. However, if only one component must be adjusted, the chances of accidentally doing this bv interaction of the lattice phonon are much greater. Thus, the preferred embodiments of the present invention use structures wherein all three components of momentum are quantized. However, a class of less preferred alternative embodiments of the present invention uses structures wherein only two components of momentum but not energy are quantized, i.e. closely spaced thin wires. It is easy to satisfy the momentum constraint alone by a phonon-assisted process, but the necessity for satisfying both energy and momentum conversation is what keeps the rate for inelastic tunnelinq background controlled. That is, if a scattering center at the metallurgical interface can change the energy of a carrier, it is easy for one of the lattice phonons to provide the appropriate adjustment in momentum. As device dimensions are made smaller, two desirable effects are achieved: First, the separation of the quantized energy states in a well increases as the well dimension becomes smaller Second, as the wells become closer together, the rate of tunneling is increased. That is, the probability of. tunneling can be expressed as a constant times expt-2d x f(E)), where d is the distance between the wells and E is the energy difference. vhis exponential dependance means that the probability of resonant tunneling is tremendous!. v increased as the distance between wells is reduced. Inelastic tunnelling will not be increased comparably, since as noted above inelastic tunnelling is limited, in good material, by the density of scattering centers. Thus, room temperature operation becomes possible at interwell spacing of about 125A or less. A limitation on resonant tunneling is Drovided bv therma ] "smearing", i.e. redistribution of energy level populations caused bv background thermal energy. shat is, the density of states distribution within each well of the discrete energy levels is broadened somewhat by thermal smearing. At higher temperatures, the thermal smearing is greater. The problem thermal smearing causes is that the operating temperature must be low enough that themal smearing does not populate higher energy level states. That is, the electrons should reside in the lowest energy level to eliminate accidental coincidences and bidirectional elastic tunneling. This reduces to the condition that the energv spacing must be much larger than the thermal energy of the electrons Thus, for operation at 40K with GaAs wells in an A1,3Ga,7As matrix, the well width (and well spacing) should be in the neighborhood of .1 to .2 microns or less. However, to increase the operating temperature to 3000R, the critical dimension needs to be reduced merely to a number on the order of 125 Angstroms or less. It should be further noted that the energy levels in adjacent wells can be made to line up or not line up simply by applying a bias, as shown in Figure 2. In this case, a sufficient, bias voltage has been applied in the direction of conduction, so that the second level in the second well is lined up with the first level in the first well. Under these conditions resonant tunneling will regularly occur, and the fast relaxation from the second revel to the ground state in the second well ensures that the device is unidirectional. If zero bias were applied to this same structure, resonant tunnelinq would still be possible but would be bidirectional. That is, at zero bias the energy levels in two adjacent wells will line up, but electrons will tunnel from the first well to the second well just as fast as they tunnel from the second well to the first well. Note, however, that if half as much bias as shown in Figure 2 is applied, resonant tunneling will be forbidden (at sufficiently low temperature) and only inelastic tunneling is permissible. In this bias condition, as shown in Figure 3, an electron can make a transition from a state in well one to an lower lying state in well two only if a scattering event also occurs, as discussed above. Thus, at small dimensions, the frequency of inelastic transitions is limited by the density of available scattering sites. However, the density of scattering sites is in effect an areal density, since it arises primarily from surface states rather than from bulk defects or particles within the crystal lattice. Thus, since the limiting factor is a areal density of defects, the inelastic tunneling current is relatively insens'tive to the distance between wells. This means that, for good quality material, as the dimensions are scaled the resonant tunneling current increases tremendously, but the inelastic tunneling current does not increase much. The result of these phenomena is that the current/voltage graph for tunneling between two wells looks approximately as seen in Figure t. That is, inelastic tunneling will suDply a current which increases apDroximately exponentiÅally with the applied voltage. Resonant tunneling will also supply at least one current peak added on to this curve, at a bias voltage where the energy levels of the wells line up. Thus, a regime of substantial negative differential resistance is available, i.e. a millimeter diode with gain is available, as reported in Sollner et al., "Resonant Tunneling Through Quantum-Wells at Frequency UD to 2.5 THz," 43 Applied physics Letters 588 (1983). (However, this article used potential wells in which only one momentum component was discrete as discussed above.) Other background reference which set forth generally known physics of resonant tunneling are Chang et al., "Resonant Tunneling in Semiconductor Double Barriers," 24 Applied Physics Letters 593 (1974); Tsu et al., "Nonlinear Optical Response of Conduction Electrons in a Super Lattice," 19 Applied Physics Letters 26 (1971); Lebwohl et al., "Electrical Transport Properties in a SuPer Lattice," 41 Journal of Applied Phvsics 26#4 (1970); ; and Voiak et al., "Low-temperature operation of Multiple Ouantum-Well AlxGal-xAs-GaAs P-n Hetero Structure Lasers Grown by a Metal Organic Chemical VaPor Diposition," So Journal of Applied Physics 5830 (1479). These five references are hereby incorporated by reference. (It should be noted that portions of the foregoing discussion merely reflect generally known physics, as reflected in these articles and pressumably elsewhere, but other portions of the foregoing discussion are not generally known and do not reflect any understanding available in the prior art.) However, the prior art has taught potential wells whjch are quantized only in one dimension, which implies relaxed constraints on the selection rules for elastic tunnelinq. The preferred embodiments of the present invention have more stringent selection rules, and should (because all 3 dimensions are quantized) have dramatically more gain than the 1-D quantized devices. vhis invention is significantv* different from the Esaki tunnel diode or 2-dimensional electron Sas structures in that all three dimensions are auantized h#ere, which imposes a constraint on the tunneling conditions much different than other structures; that is, the momentum constraint sigificantly depresss other than the desired elastic resonant tunneling. The foregoing has supposed that only a few quantum levels are found in a well, but this is not correct for the most convenient well dimensions. A more realistic energy diagram of the levels in such a structure wherein 1000 angstrom GaAs wells are incorporated in an AlGaks lattice would be as shown in Figure 5. Note that, in the familiar statics of the solution to the particle in a box problem, the successively higher energy levels are spaces progressively closer together. This means that, even when the bias voltage is such that the lowest few levels between the two wells do not line up, some of the higher lying levels are likely to. However, this is not a major problem, since the hiqher lying levels will typically be depoPulated because of the temperature constraint mentioned previously. That is, the lifetime for relaxation from a higher lying state to an emPty lower state will typically be much shorter than the typical time for tunneling. Thus; after a lower level#has been depleted by tunneling, a higher level which has been excited in any fashion will tend to relax to the depleted lower level much faster than it will tunnel. However, this assumes that empty lower levels exist below the higher level from which tunnelinq is possible. This imposes a constraint on the input contact, which will now be discussed. Figure 6 shows the energy diaqrams for a svstem of two coupled wells 10 and 12 Plus input and output contacts 14 and 16. Note that the input and output contacts are doped, although the wells and the areas between them are preferably not. Note also that two important limitations on the well size arise from the necessities of makinq input contact and output contact. First, the input contact will fill all levels of the flrst well 10 bv tunneling, up to an energy asproximately equal to the Fermi level of the electrons in the doped semiconductor which provides the input contact. This means that none of the levels thus still filled up must line up with levels in the second well when tunneling is not desired. That is, if the wells are too large, they will have discrete energy states at the bottom of the well but will include densely spaced states below the Fermi level of the input contact. This means that these densely spaced states will be filled, and therefore resonant tunneling current will be seen if any of these dense states line up with states in the second well. This means that the current gain of the device will be greatly reduced. Second, all levels in the second well which are above the Fermi level of the output contact will equilibrate with the output contact, i.e. will essentially always remain filled. This is not itself a problem, since electrons can tunnel from the higher loving energv states in the second well into the continuum of states which exists in the (larqe) output contact, but if any level in the first well lines up with one of these filled levels in the second well, that level in the first well will also remain filled. Note that the input and output contacts are preferably both degenerately doped n-type. The physical well shapes have been described as having perfectly sharp boundaries, but this is not quite realistic. That is, in good quality MBE material, the transitions will tvpically be smooth enough that the potential profile looks more precisely like that drawn in Fiaure 7. This is actually advantaqeous, since the enerqy levels will tend to be more nearly eaual spaced. That is, where the energy level sDacings are more nearlv equal, there is a wider range of bias conditions wherein a large number of the lower lying energy levels will not line up. Of course, for the ultimately preferable small well dimensions, e.g. 125 angstroms, the number of states in each well will be small, e.q. 4 states per well. With such a small number of states, there will be bias conditions under which no actual line ups exist. Each tunneling transition described above is a transition of only a limited number of electrons for each Pair of coincidental states. That is, each of the discrete energy levels in the quantum well can be populated bv only a certain definite number of electrons. In the example discussed above, wherein the energy well has the approximate physical shape of a cube, the lowest lying level can be populated by only two electrons, and no more. The next hither energy level can be populated by only six electrons, and no more. The third energy level can be populated bv only 12 electrons, and no more. Most of the higher-lying levels can also be Populated bv only 12, although some may have a higher maximum occupancy because of accidental degeneracies. Thus, it is important to note that a carrier cannot tunnel into even an allowable energy level unless that allowable energy level is not completely populated. The multiple states at each allowable energy level are distinguished by other quantum numbers. That is, for example, the six electrons in a second energy level can have one of two possible states of spin, and can have one of three possible momentum vector directions. However, this distinction among isoenersetic states is relatively unimportant for understandinq the Present invention. Thus, each tunneling transition can transPort up to a dozen carriers for each pair of lined-up wells. More than one Pair of wells mav be lined up at the same time. Moreover, manv pairs of wells may be operated in parallel. Moreover, the transit time for tunnelling can be extremelv small, less than a pico second. Thus, although only a few electrons are translated in each tunnelinq event, a reasonable current density can be achieved nevertheless. Thus, a basic family of embodiments is structures, ab described above, wherein two quantized wells separate an input contact from an output contact. However, further aspect of the present invention provide numerous other kinds of innovative device structures. For example, a three terminal device according to the Present invention is shown in a plan view in Figure 8. A first quantum dot 202 is coupled to a second quantum dot 204, which is coupled to an output contact 210. The dimensions of the quantum dots 202 and 204 are selected as discussed above for quantum wells, but the output contact 210 is made sufficiently large that a quasi-continuum of states is available. The quantum well 202 is coupled from beneath to an electrode 206, and the quantum well 204 is coupled from beneath an electrode 20R. These are preferably deqeneratelv doped semiconductor regions, or may be metal lines, but in any case provide the long-distance routing necessary for formation of conventional electronic circuits. In the presently preferred version of this embodiment, the quantum wells 202 and 204 have only 2 components of momentum discretely quantized, since they are directly connected to their respective electrodes. That is, the electrodes 206 and 208 can be, for example, tungsten, with a thin layer of a conventional barrier metallization optionally provided on top. The GaAs of quantum wells 202 and 204 are formed directly on top of this conductor. Preferably the electrodes 208 and 20B are n+ Gays. Optionally, a thin barrier of AlGaAs can be provided beneath each of the quantum wells 202 or 204 and above the respective contact 206 or 208. This barrier is sufficiently thin that it is readily tunnelled throuqh, and therefore does not prevent DC coupling of each quantum well to its respective electrode, but even this thin a barrier would be sufficiently small to provide sufficient quantization of all 3 parameters of momentum within each of the wells 202 and 204, and therebv increase the relative resonant tunneling gain at the expense of a small increase in processing complexity and small decrease in overall current. A lager scale version of essentially this structure is shown in Figure 9. This 3-terminal quantum well device can be configured with multiple chains of quantum well pairs 202, 204 in parallel, for greater current flow. Note that electrode 206 can be thought of as acting as a source, electrode 208 can be thought of as a gate electrode, and electrode 210 can be thought of as a drain electrode. Pattern 2)3 can be used to define the well locations 202 and 204. Figure 10 shows a cross section of this structure, including ground plane 211. A further variation of this structure is shown in Figure 11. Note that additional electrodes 208 prime are usei to provide longer chains of wells 202, 204 prime, 204 prime, etc., wherein resonant tunneling will occur only if the voltages on all of the electrodes 206 and 208 prime jointly satisfy one single condition (or some one of a small set of conditions). That is , Figure 12 shows a sample set of electrode bias conditions wherein resonant tunneling will not occur, and Figure 13 shows a different set of bias conditions wherein resonant tunneling wil3 occur. This multiple-gate device is particularly useful for a read only memory. In a read only memory (ROM) embodiment, information is hard-programmed simply by changing the degree of electrical coupling of a column line to underlving quantum wells. A sample of this embodiment is shown in Fiqure 14. A particular advantage of this embodiment is that the patterning of the metal lines need not be exactlv aliqned to the pattern of the underlying quantum wells. That is, if the pitch of the metal lines can be made twice or more that of the quantum wells, and the ROM will still function. In the sample embodiment shown, column lines 302, 304, 30#, etc. are overlying metal lines. Column line 302 is electrically coupled to row 310 of quantum wells, but not coupled (or less well coupled) to row 312 of quantum wells. This differential coupling can be accomplished by holes cut in a field plate, or by a dielectric patterned in multiple thicknesses. A sample mode of operation of this structure is as follows: A background potential is defined for every column (i.e., all columns fixed at ground) such that resonant tunneling occurs throuah each row of quantum devices 310, 312, etc. When it is desired to read out a column of cells, the column line 302 for that column is changed to some different voltage. This different voltage will perturb resonant tunneling in any row to which that column line is electrically coutied, and thereby disrupt resonant tunneling in that row. In rows to which this column is not electrically coupled resonant tunneling will not be disrupted. Thus, by monitoring the current in a row, the information hard-troarammed into the intersection of the address'9 column and the read-out row will be detected. h sample Process for fabricating auantum well devices according to the present invention will now be described. In particular, fabrication of 3-terminal devices, as discussed above, will be used as an example. The beginning material is a semi-insulating GaAs substrate with 2 epitaxial layers. The substrate is preferably chromium doped, e.g. to 1015 per cubic centimeter, although this is not necessary The first epitaxial layer is n+ GaAs. This layer will provide connections, and is therefore fairly thick and of a fairly high conductivity, e.a. 5000 anastroms thick and doped to 1018 ter cubic centimeter or more n type. On top of this is deposited the thin lightly doped n-type laver which will patterned to form the actual quantum wells. This layer is doted, e.g., about 1016 per cubic centimeter n-type, and, in a sample embodiment, is 150 angstroms thick. (The light doting is used merely so that some carriers are available. Heavi¯r doping would increase inelastic tunnelling.) Figure 21 shows an initial structure, having epitaxial layers 404 and 406 atop substrate,402. Optionally, as discussed above, an extremely thin layer of AlGaAs could be interposed between layers 404 and 406. This structure is preferably fabricated by molecular beam epitaxv, to provide the desired sharp doping transitions, but this is not strictly necessary Published chemical vapor deposition results, particularly using organo metallic CVD CMOCVD#, also state results of extremely sharp transitions. The first patterning step follows. In the presently preferred embodiment, patterning is done usina electron beam with an E beam resist such as PMMA (polymethylmethacrylate). This is the presently preferred embodiment, because it provides a reliable way to make structures smaller than 0.1 microns today. Such dimensions are of course not possible using optical lithography, although x-ray or ion beam lithographv may provide a more convenient to way to do such Patterning in the future. Figure 22 shows the eprtaxial structure of Figure 21, with a patterned layer of PMMA 408 (patterned by e-beam writing and developing) in place. A reactive ion etching (RIE) mask material is then deposited. In the presently preferred embodiment, an aluminum layer 410 and a gold/germanium/nickel layer 412 are used for this. The patterned layer 408 is then lifted off, to expose only selected fine line portions of the ePitaxial laver 406, as seen in Figure 23. Reactive ion etching is now conventionally performed to cut trenches 414 through the epitaxial layer 406 and 404 down into the substrate 402. RIE conditions are conventionally known for such patterning, and extreme anisotropv is readily achieved at low pressure, at the expense of somewhat slow etching. Next, the aluminum layer 410 is removed in dilute HC1 to remove the RIE maskina layer 10 and 412, as seen in Fiqu 25. Nexti an AlGaAs layer 416 is epitaxially regrowr. overall. This fills the trenches 414. It is preferable to perform this regrowth using molecular beam epitaxy. However, again, metal organic CVD is an alternative technology. However, in any case, it is important that this regrowth be of extremely high quality, since the sidewall interface between the GaAs wells formed from laver 406 and the AlGats fill 4)6 are extremely critical, as discussed above. This regrown structure shown in Figure 26. Next, a second patterning step is performed. The pattern used in this case is essentially the same pattern over the wells, but also includes the output contact in the finished structure. This pattern, seen in Figure 27, is converted to a hard mask pattern, seen in Figure 28, which is then reactive ion etched again. However, this reactive ion etching step has a critical depth control. It must be continued to etch into, but not through, the na laver 404. This critical depth control provides one reason for making the n+ layer 404 so thick, as discussed above. Again, the masking metal is stripped (Figure 3owl, and AlGaAs is regrown overall. As discussed above, the AlGaAs needs to have a high enough percentage of aluminum to imPose a significantly different conduction band energy between the AlGaAs and GaAs, but it is preferable that the aluminum percentage not be too high, to provide for the best possible GaAs to AlGaAs interface. In the presently preferred embodiment, a composition of about A10,3 GaO.7As is used. Figure 31 shows the resulting structure, with the new AlGaAs layer 420. Note that, in Figure 30, some portions of the AlGaAs laver 416 survive, and these portions are incorporated in the laver 420. Again, the layer 420 must be epitaxial grown with extremelv qood interface quality. A contact metallization pattern is then applied, as shown in Figure 32. The geometries are less demanding at this E;teD and optical resist 422 with optical patterning is preferablv used. A selective etch is then used, which will etch through AlGaAs and stoP on n+ GaAs. Evdroqen fluoriAe has this propertv. This step provides contact holes 424, as seen in Figure 34. Metallization patterning is then applied, again preferably using an optical resist 426, as seen in Figure 35, and metal (such as AuS,e/Ni) is then deposited, e.g. by evaporation, and lift off patterned, resulting in the structure as shown in Figure 3S. A very similar fabrication technique can be used to fabricate quantum well array structure, e.g. for ROMs, simply by performing the second patterning step (.shown in Figure 27) to define linear patterns at right angles to linear patterns defined by the first patterning step, so that the intersection of the two defines locations of the quantum well dots. A basic difficulty in interconnecting quantum well devices according to the present invention to form random logic circuit is their electrical characteristics. These devices may be considered to have very high input impedence and very low output impedence. In a further aspect of the Dresent invention, a circuit structure for output coupling is described which permits the output of quantum well devices according to the present invention to switch macroscopic currents, i.e. currents comparable to those normally used in integrated circuit wiring. These macroscoPic currents can then be used to change electric potentials and thereby switch further stages of quantum well devices. It is known in the prior art that macrosco#ic resist changes can be detected in a very thin wire due to trapping of a single electron onto a ta at or near the interface of the wire to the substrate. See the K. Raals et al. paper in 52 Phys. Rev. Letters 228 (1984). That is, in extremely small metal wires, e.g. 100 Angstroms by 100 Angstroms, the cross section of a scattering center which is close to the wire will change bv many orders of magnitude depending on whether an electron is or is not trapped in the scattering center. This tremendous change in scattering causes a net change in the resistance of the wire. This effect need not bel-imited to wires of such small dimension. By using multiple trapping sites (scattering centers), the resistance of a larger wire can be similarly modulated. In particular, where a thin or wide wire is used, a dielectric with traDs coated over the surface of the wire can substantially modulate the wires resistance as the traps are populated and depopulated. To accomplish charging of the traps, a field plate is preferably used, which provides a bias normal to the surface of the wire Thus, the current output of a quantum well device stage (which would of course normally include multiple quantum well chains in parallel) can be coupled into a thin flat wire, while a field plate bias is applied vertically to assist charge injection from the wire over the energic barrier into trapping sites in the dielectric. The charges thus trapped will modulate the resistance of the wire after the vertical bias is removed and the current signal through the wire can then be used to trip a sense amplifier. Thus, this scattering center modulation in effect provides a latch suitable for conversion of the auantum well output signals to macroscopic signals. This embodiment will now be discussed in greater detail. First, the dimensions of the wire next to the scattering site must be such that the wire is in what is known as the Anderson localization regime: the wave function of the electron must significantly overlap the entire periphery of the wire, i.e. all four faces of a square wire In this reqime, the resistance will be extremely sensitive to surface states adjacent to the wire. There will typically be many unintentionally generated surface states, but these normally have low activation energy. Thus, the operating temperature is selected so that these unwanted surface states will boil off readily, i.e., selected such that kT is comparable to or larqer than the activation enerqv of these parasitic surface states, but such that the activation energy of the surface states in which charges to be trapped to effect modulation is more than several times as much as ks. Thus, the principle application of this output amplifier stage is believed to be for devices operating at temperatures in the neighborhood of 77 kelvin, i.e. liauid nitrogen temperatures. However, hiqher operating temperatures can be used if carriers can be iniected into deePer surface states. The surface states used in the presently preferred embodiment are about 20 to 30 meV or more removed from the conduction band energy of the metal. Operation in the Anderson localization regime means that the dimensions of the wire close to the scattering center cannot possibly be greater than 500 x 500 angstroms, and are Dreferably closer to 100 x 100 angstroms. For a 100 x 1 no angstrom wire, the resistance of the wire is roughly 100 K to one meqohm per micron. Each scattering center which is populated or depopulated can impose a resistance change of a percent or so, and by using several such scattering centers, a total resistance change of 5% or so is achieved. Thus, these metal lines are used in pairs, and a change in current of a few percent jis easily enough to trip a conventional sense amplifier. The Dresently preferred embodiment for accomplishirc carrier injection into these traDs is to have the trapping site connected to the last well in a chain of quantum wells bv tunnelinq, i.e., the separation from the trapping site to the last well in the chain should be removed from the trappinq site by no more than a few times the distance between wells, and preferably less. Tunneling out of the trap into the last well. is not a limitation in the preferred embodiment since the electron enters the trap through excited states. The reverse tunneling is onlv inelastic. However, for a sufficiently deep trap, the required phonon energy becomes so large that the inelastic. tunneling is negligible. The trapping site can be written with extreme Precision using a focused ion beam. Thus, the configuration of this output stage is shown in FIG. 15. As mentioned, one-wav well coupling is optionally used to assist injection of carriers into these traps, to modulate the metal lines resistance. This one-way coupling is made possible bv the self-consistant tunnelinq effects of the wells. That is, in addition to the factors discussed above, the presence or absence of electrons in the wells will itself modulate the electric field between wells. Thus, as shown in FIGS. 16 A and B, the chance in electric field caused bv the presence of an additional carrier in a second well can itself be sufficient to forbid tunneling. Thus, a carrier will readily tunnel from well I into a depleted level in well 2, but that same carrier cannot tunnel back into well 1 except through inelastic channels, because now the levels no longer line up. For this self-generated field modification to be useful, it is necessary that the resonant peaks at the given operating temperature be relatively sharp. That is, the well dimensions should preferably be smaller than those necessary, at the operating temperature, or anv resonant tunnelinq qain. wor example, wells of appropriate dimensions for operation at room temperature will show such effects if operated at 77K or at 4K. The smaller wells mean that the field generated bv the potential shift caused bv the addition of one carrier will be greater. These self-generated field effects have other uses also. For example, consider the four-well structure shown in FIG. 17. A field plate or other bias connection is used to define a reference voltage Vo for well 3. The wells are tailored such that tunneling occurs from well I to well 3 only when v3 equals Vo; tunneling occurs from well 2 to well 3 only when V3 equals Vo plus B, i.e., when the potential of well 3 has been modified b the presence of one electron; tunnelinq occurs from well 3 to well 4 only when well 3 has a potential V3 equals V0 plus 2E. Input Signal A sup#1ies carriers tunneling into well 1, and input signal B supplies carriers tunneling into well 2, and an output contact retrieves an output siqnal C from well. Thus, this primitive complex of wells provides an AND gate. Other Boolean primitives are easily created. For example, in the same layout of wells, if we redefine the well couplinqs such that the tunneling occurs from well 1 to well 3 when V3 equals Vg, from well 2 to well 3 when V3 equals Vo, and from well 3 to well 4 when V3 equals Vo plus E, we now have an OR gate. These coupling can be used to configure all primitive Boolean algebraic logic cells and more. In this regime, where self-generated fields are sufficient to disrupt tunnelinq, a problem may be caused bv the presence of excess carriers in a well. That is, if the coupling between wells A and B is designed to admit resonant tunneling when well A is PoPulated and well B is not, tunneling may be disrupted if well A has two states populated rather than merely one. However, in such cases, the 2-carrier population must have been created inelastically. Moreover, inelastic tunnelins will provide a reset mechanism eventuallv. A further family of the embodiments of the present invention utilize vertical tunneling. An attraction of such structures is that extremely small dimensions, with extremely good interface quality are easier to achieve in the vertical dimension then in the lateral dimension. A kev feature of such embodiments is that the sPacing of enerqv states in the well is in general defined bv the volume of the well. Thus, for a given well volume the well mav be configured as a thin flat box rather than a rouqhly cubic box. In this case, two of the momentum components would be cuantized with extremely closely spaced values, and the third component would be quantized with extremely widelv spaced allowable momentum values. Such embodiments are shown in FIGS. 19 through 20. Aqain, the wells 604-608 are preferablv made of a first semiconductor and the barrier medium 612 is preferably made of a second, wider-band gat semiconductor. Gallium arsenide and AlG2As are preferable for these two semiconductors. Current flows from n+ electrode 602 to metal electrode 610 only if the potentials of row line 616 and column line l4 permit levels of well 606 to line up with levels of wells 604 and 68, as discussed above. Thus, the present invention provides the above-mentioned obiects, as well as numerous other techincal advantages in accordance with the foregoing description. As will be apparent to those skilled in the art, the present invention is a pioneering invention, and can be modified with an immense varietv of modification and variations. For example, Si wells can be used in an SiO2 barrier medium, or other semiconductor/semiconductor or semiconductor/insulator systems can be used, in place of the preferred GaAs/AlGaAs materials svstem. The scope of the present invention is not limited except as set forth in the accompanying claims.

Claims: What is claimed is: - 1. An electronic device comprising: first and second potential wells each comprising an island of a semiconducting material having a minimum dimension less than 500 Angstroms and another dimension less than 1000 Angstroms; a barrier medium interposed between said first and second wells wherein the minimum potential energy of carriers is at least 50 millielectronvolts higher than the minimum potential energy of carriers within said wells, said wells being physically separated by a distance which is less than three times the smallest physical dimension of either of said well 5; means for inputting carriers into said first well; and means for removing carriers from said second well. 2. An electronic device, for operation at a predetermined maximum temperature greater than 65 elfin, comprising: first and second potential wells each comprising an island of a semiconducting material having a minimum dimension less than 300 Angstroms and another dimension less than 500 Angstroms, a barrier medium interposed between said first and second wells wherein the minimum potential energy of carriers is at least 8 millielectronvolts higher than the minimum potential energy of carriers within said wells, said wells being physically separated by a distance which is less than three times the smallest physical dimension of either of said wells; means for inputting carriers into said first well; and means for removing carriers from said second well. 3. An electronic device, for operation at a predetermined minimum temperature greater than 300 Kelvin, comprising: first and second potential wells each comprising an island of a semiconducting material having a minimum dimension less than 150 Angstroms and another dimension less than 500 Angstroms; a barrier medium interposed between said first and second wells wherein the minimum potential energy of carriers is at least 30 millielectronvolts higher than the minimum potential energy of carriers within said wells, said wells being physically separated by a distance which is less than three times the smallest physical dimension of either of said wells; means for inputting carriers into said first well; and means for removing carriers from said -second well. 4.An electronic device comprising: a barrier medium wherein carriers have a first minimum potential energy; first and second potential wells in said barrier medium, the potential energy of carriers in said wells being less than the potential energy of carriers within said barrier medium; said first and second potential wells being physically separated by a distance which is less than three times the largest physical dimension of either of said wells; said first and second wells being sufficiently small in all three dimensions that energy levels within each of said wells are separated by more than one half millielectronVolt; means for inputting carriers into said first well; means for removing carriers from said second well; and means for selectively appplying bias between said first and second wells so that, under a first bias condition, at least one discrete energy and momentum state in said first well is aligned with a discrete state in said second well, and, under a second bias condition, no one of the lowest-lying three of said discrete states within said first welf is aligned with a discrete state in said second well; both said first and second bias conditions being such that the energetically lowest state in said second well has a lower potential energy for carriers than the the energetically lowest state in said first well. 5. Nn electronic device comprising: first and second potential wells each comprising an island of a semiconducting material having a minimum dimension less than 200 Angstroms, said first and second wells being sufficiently small in all three dimensions that energy levels within each of said wells are separated by more than one half millielectronVolt; a barrier medium interposed between said wells wherein the minimum potential energy of carriers is at least 5 millielectronvolts higher than the minimum potential energy of carriers within said wells, said wells being physically separated by a distance which is less than three times the smallest physical dimension of either of said wells; means for inputting carriers into said first well; and means for removing carriers from said second well. 6. An electronic device comprising: a barrier medium wherein carriers have a first minimum potential energy; first and second potential wells in said h > rier medium, the potential energy of carriers in said wells being less than the potential energy of carriers within r::#t barrier mediu#; said first and second potential wells being physically separated by a distance which is less than one hundred times the Bloch wavelength of a carrier in said barrier medi#um: : said first and second wells being sufficiently small in all three dimensions that energy levels and all three components of momentum of carriers within each 0+ said wells are discrete; means for inputting carriers into said first well; means for removing carriers from said second well; and means +ar selectively appplying bias between said first and second wells so that, under a first bias condition, at least one discrete energy level in said first well is aligned with a discrete energy level in said second well, and, under a second bias condition, no one of the lowest-lying three discrete levels within said first well is aligned with a discrete level in said second well; both said first and second bias conditions being such that the lowest-lying energy level in said second well has a lower potential energy for carriers than the lowestlying potential energy level in said first well. 7. An electronic device womprising: a barrier medium wherein carriers have a first minimum potential energy; first and second potential wells in said barrier medium, the potential energy of carriers in said wells being less than the potential energy of carriers within said barrier medium; said first and second potential wells being physically separated by a distance which is less than one half micron; said first and second wells being sufficiently small in all three dimensions that energy levels and all three components of momentum of carriers within each of said wells are discrete; means for inputting carriers into said first well; means for removing carriers from said second well; and means for selectively appplying bias between said first and second wells so that, under a first bias condition#, at least one discrete energy level in said first well is aligned with a discrete energy level in said second well, and, under a second bias condition, no one of the lowest-lyin# three discrete levels within said first well is aligned with a discrete level in said second well; both said first and second bias conditions being such that the lowest-lying energy level in said second well has a lower potential energy for carriers than the lowestlying potential energy level in said first well 8. An electronic device for operation at a predetermined operating temperature, comprising: a barrier medium wherein carriers have a first minimum potential energy; first and second potential wells in said barrier medium, the potential energy of carriers in said wells being less than the potential energy of carriers within said barrier medium; said first and second potential wells being physically separated by a distance which is less than one hundred times the Bloch wavelength of a carrier in said barrier medium; ; said first and second wells being sufficiently small in all three dimensions that the lowest-lying two energy levels within each of said wells are separated by at least 7. times Boltzmanns constant times the value in degrees Kelvin of said operating temperature, and all three conponenvrs =f momentum of carriers within each of said wells are disc:ret#; means for inputting carriers into said first well; means for removing carriers from said second well; and means for selectively appplying bias between said first and second wells so that, under a first bias condition, at least one discrete energy level in said first well is aligned with a discrete energy level in said second well, and, under a second bias condition, no one of the lowest-lying three discrete levels within said first well is aligned with a discrete level in said second well; both said first and second bias conditions being such that the lowest-lying energy level in said second well has a lower potential energy for carriers than the lowestlying potential energy level in said first well. 9. An electronic device comprising: a barrier medium wherein carriers have a first minimum potential energy; first and second potential wells in said barrier medium, the potential energy of carriers in said wells being less than the potential energy of carriers within said barrier medium; said first and second potential wells being physically separated by a distance which is less than three times the largest physical dimension of either of said wells; said first and second wells being sufficiently small in all three dimensions that energy levels within each of said wells are separated by more than one half millielectronyolt, and all three components of momentum of carriers within each of said wells are discrete; means for inputting carriers into said first well; means for removing carriers from said second well; and means for selectively appplying bias between said first and second wells so that, under a first bias condition, at least one discrete energy level in said first well is aligned with a discrete energy level in said second well, and, under a second bias condition, no one of the lowest-lying three discrete levels within said first well is aligned with a discrete level in said second well both said first and second bias conditions being such that the lowest-lying energy level in said second well has a lower potential energy for carriers than the lowestlying potential energy level in said first well. 10. An electronic device comprising: a barrier medium wherein carriers have a first minimum potential energy; a plurality of pairs of first and second potential wells in said barrier medium, the potential energy of carriers in said wells being less than the potential energy of carriers within said barrier medium; said first and second potential wells-being physically separated by a distance which is at most three times the minimum physical dimension of said wells; said first and second wells being sufficiently small in all three dimensions that energy levels and all three components of momentum of carriers within each of said wells are discrete; means for inputting carriers into said first well; means for removing carriers from said second well; and means for selectively appplying bias between said first and second wells so that, under a first bias condition, at least one discrete energy level in said first well is aligned with a discrete energy level in said second well, and, under a second bias condition, no one of the lowest-lying three discrete levels within said first well is aligned with a discrete level in said second well; both said first and second bias conditions being such that the lowest-lying energy level in said second well has a lower potential energy for carriers than the lowestlying potential energy level in said first well. 11.The device of Claim 1, wherein said barrier medium has a minimum potential energy for carriers which is at least 10 percent greater than the minimum potential energy for carriers within said wells. 1. The device of claim 1, wherein said wells comprise a first semiconducting material, and said barrier medium comprises a second semiconducting material with a larger bandgap than the bandgap of said first semiconducting material. 13. The device of claim 1, wherein said carriers predominantly comprise electrons. 14.The device of Claim 1, wherein said barrier medium has a potential energy for carriers which is at least one half millielectronVolt greater than the minimum potential energy for carriers within said wells. 15. The device of claim 1, wherein said wells and said barrier medium comprise respective semiconductor materials, and said barrier medium is doped n-type. ; 16. The device of claim 1, wherein said wells comprise a first semiconductor material and said barrier medium comprises a second semiconductor material, and wherein said first semiconductor material is not lattice-matched to said second semiconductor material. 17. The device of claim 1, wherein said wells comprise a first semiconductor material and said barrier medium comprises a second semiconductor material, and wherein said first semiconductor material is lattice-matched to said second semiconductor material. 18. The device of claim 1, wherein each of said first and second wells has a maximum physical dimension which is less than 150 Angstroms. 19. The device of claim 1, wherein each of said first and second wells has a minimum physical dimension which is less than 100 Angstroms. The The device of claim 1, wherein said means for inputting carriers comprises: an input contact physically separated from said first well by a distance which is less than twice the distance separating said first well from said second well; said input contact including at least a quasicontinuum of energy levels. 21. The device of claim 1, wherein said means for removing carriers comprises: an output contact physically separated from said second well by a distance which is less than twice the distance separating said first well from said second well; said output contact including at least a quasicontinuum of states below the lowest-lying state of said second well. 2. The device of claim t, wherein said means for inputting carriers comprises an input contact physically separated from said first well by a distance which is less than twice the distance separating said first well from said second well, said input contact including at least a quasi-continuum of energy levels; and wherein said means for removing carriers comprises an output contact physically separated from said second well by a distance which is less than twice the distance separating said first well from said second well, said output contact including at least a quasi-continuum of states below the lowest-lying state of said second well; and wherein said bias applying means applies bias between said input contact and said output contact.

Inventors: BATE, ROBERT T., REED, MARK A.
Applicants: TEXAS INSTRUMENTS INCORPORATED
Application year: 1985
Main classification: H01L29
IPC codes: H01L29, H01L21