METHOD FOR THE PRODUCTION OF BENZENE AND CUMENE

Abstract: The heavy by-products of the process for the production of cumene by the catalytic alkylation of benzene with propylene, are treated in an atmosphere of hydrogen on catalysts constituted by a natural silico-aluminate having a silica-alumina ratio greater than or equal to 3/1, pre-treated with a mineral acid, on which a metal of the eighth group is deposited to give a reaction product consisting essentially of benzene and cumene.

Description: "Method for the production of benzene and cumene" The present invention relates to a method for the production of benzene and cumene from the heavy by-products of the process for the production-of cumene by the catalytic alkylation of benzene with propylene. It is known in the art to produce cumene by the catalytic alkylation of benzene with propylene, for example cn supported photphoric-acia catalysts. In these processes, in addition to the cumene (isopropylbenzene), by;products are also formed which result from the further alkylation of the benzene, in particular di-isopropylbenzenes and products of the alkylation of benzene with higher olefines such as butenes, pentenes, hexenes timers of propylene) etc., present in the technical prepylene or which form during the alkylation reaction. These heavy byproducts, which will be termed cumene bottoms or simply bottoms in the present specification, separate at the bottom of the cumene distillation column and result in a smaller yield of the useful reaction product and loss of valued compounds. It has thus been proposed to subject the diisopropylbenzenes in the cumene bottoms to transalkylation by the addition of benzene to the bottoms, the reaction being carried out in the presence of catalysts such as boron and aluminium halides commonly known as Friedel Crafts catalysts. The use of such-catalysts, however, involves various disadvantages due to corrosion and ecological problems as well as problems resulting frbm the high consumption of the catalysts themselves. In order to overcome these disadvantages, it has been proposed in the art to use heterogeneous transalkylation catalysts such as, for example, zeolites (USP 3,385,906) which are active in a temperature range of from 130 to 250 C, or zeolites containing a metal, such as nickel, palladium or platinum within their structure (DE-OS 2,127,481) shiah are active in a hydrogen environment and within a temperature range of from 275 to 350 C. The present invention is based on the finding that catalysts constituted by natural silico-aluminAtes with a silica alumina ratio greater tan or equal to 3/1, pretreated with a mineral acid, and on which a hydrogenating metal has been deposited, are active not only in the transesterification of dialkylbenznes (like the catalysts of the prior art) but also in the dealkylation of monoalkylbenzenes, when the reaction is carried out in a hydrogen environment, in accordance with the following general reactions: EMI2.1 Consequently, some of the benzene required by the transalkylation reaction is generated within the reaction environment itself, with obvious economic advantages. In particular the consumption of benzene is of the order of 0.15 - 0.20 parts by weight per part by weight of cumene produced, compared with the stoichiometric quantity required by the transalkylation reaction which is 0.65 parts by weight of benzene per part by weight of cumene. In accordance with this, the present invention relates to a method for the dealkylation and transesterification of cumene bottoms in which the bottoms, possibly after the addition of benzene, are placed in contact with a catalyst constituted by a natural silico-aluminate with a silica/alumina ratio greater than or equai to 3/1, pretreated with a mineral acid, on which a metal belonging to group VIII of the periodic system of the elements has been deposited, and the reaction is carried out in the liquid phase under hydrogen at a pressure of from 10 to 60 bar and at a temperature of from 150 to 3500C until a substantial quantity of the bottoms has been converted into benzene and cumene and the benzene and cumene are separated and recovered from the reaction mixture. The catalysts used in - the method of the present invention are constituted by a natural silico-aluminate having a silica alumina ratio greater than or equal to 3/1, pretreated with a mineral acidand containing a metal from group VIII of the periodic system of the elements Natural silico-aluminates suitable for the purpose are bentonites, particulÅarly those having a high montmorillonite content. It is known that montmorillonite is a sodium, calcium and magnesium silico-aluminate having the following general formula: (Al1.67Mg0.33Na0.33) Si4 010 (OH)2 The percentage montmorillonite in bentonites generally varies from 60 to 80% by weight, the remainder being constituted by materials such as silica, calcite, illite, etc. The treatment of the bentonites with mineral acids, such . as sulphuric, hydrofluoric, hydrochloric acld etc., partly or completely removes the alkali metals, which are replaced by hydrogen, and one thus obtains the so-called activated acid earths. The acid earth corn.ercially known under the trademark FILTROL made by the Filtrol Company, Los-Angeles (USA), s, of the commercial acid earths, that most particularly suitable for the purposes of the present invention. These activated acid earths themselves have transalkylating catalytic activities; however under the conditions of the present inventive method, they rapidly becone deactivated and are thus not useful for this purpose. Therefore, according to the present invention, a metal from group VIII of the periodic system, generally palladium, platinum, nickel or cobalt, is deposited on the acid earth. It has- been found, , surprisingly, that these catalysts do not have an appreciable hydrogenating action on the aromatic nucleus under the conditions of the present inventive method and give conversions of the clllene bottoms of from 50 to 100% with a selectivity towards cumene of more than about 90g. Among all the catalytic metals nickel has been found to be the most suitable because it has practically no hydrogenating effect and it has a very high resistance to ageing. The quantity of metal in the catalyst may vary from 0.05 to 5% by weight with respect to the silico-aluminate of the support, with preferred values of from 0.1 to 1% in the case of palladium or platinum and from 1 to 5% by weight in the cage of nickel or cobalt. The catalyst may be prepared by impregnating the activated acid earth wit an aqueous, possibly acidic solution of a salt of the metal which it is intended to cessjosit (for example palladium chloride or nickel nitratej. The acid earth thus treated is then dried at a temperature of the order of 100-130"C and finally calcined t temperatures of the order of 200-400 C. The catalyst obtained is conveniently treated before use in an atmosphere of hydrogen for 3 to 5 hours at a temperature of from 150 to 5000C. In an embodiment of the method of the present invention the cumene bottoms as such, or with an addition of benzene, are fed to and brought into contact with the catalyst In particular, the molar ratio between the added benzene and the bottoms may vary generally from 0/1 to 20/1. It is however noted that the presence of added benzene favours the transalkylation and dealkylation reactions and retards the ageing of the catalyst. On the other hand it is noted that a large quantity of added benzene does not give substantial advantages. Hence in the preferred embodiment, a mixture of benzene and cumene bottoms is fed to the catalyst in a molar ratio of 2/1 to 10/1. The preferred reaction temperatures are within the range 200 to 3000C. The hydrogen pressures may vary in general from 10 to 60 bar and, in a preferred embodiment, are within the range 20 to 40 bar. In practice this corresponds roughly to a hydrogen/oranic molar ratio of 1/1 to 10/1 for the wider pressure range and from 2/1 to 5/1 for the preferred pressure range. In practice the reaction may be carried out by passing the liquid reaction mixture over the catalyst deposited in the form of a fixed bed, at a rate of passage of the mixture of from 0.5 to 5 volumes of the mixture per volume of catalyst per hour. The reaction products obtained, after separation of the hydrogen, are treated to separate the valued constituents, particularly benzene and cumene. In a preferred embodiment, the reaction products are conveyed to the distillation reaction stage of the plant for the production of cumene by the alkylation of benzene with propylene. If the activity of the catalyst tes to fall during use, the supply of cumene bottoms may be suspended and the catalyst may be-treated with benzene alone in the presence of hydrogen, in other conditions appropriate for the reaction. Thus complete activation of the catalyst is achieved in a period of the order of 0.5 3 hours. The method of the present invention is particularly advantageous when used in combination with any method for the production of cumene by the catalytic alkylation of benzene with propylene. In these alkylation processes, carried out in the liquid or gaseous phases, at a temperature within the range 50-400tC,* benzene and propylene are conveyed to the catalyst (phosphoric acid, aluminium halide, silica-alumina, acid resins etc.), with a molar excess of the first over the second, and the propylene is converted substantially completely to give a reaction product constituted by the excess benzene, cumene and cumene bottoms. These latter consist essentially of di-isopropylbenzenes (about 70%) and products of the alkylation of benzene with oligomers of propylene (about 25%) and constitute the feed for the process of the present invention once separated from the benzene and the cumene. The experimental examples which follow are illustrative and non-limitative of the invention. In the Examples, the parts and percentages are expressed by weight if not otherwise indicated. Example 1 The commercial acid earth FILTROL G .24, having the following composition Si02 67.28 Al2O3 13.8% Fe203 0.99% Ca Na 0.028 H2O balance - to 100, in the form of 30 to 60 mesh granules, is added to a solution of palladium chloride (Pd Cl2) dissolved in 6N hydrochloric acid, the mass being kept under agitation. The quantity of palladium chloride is such as to ensure a 0.1% by weight of palladium metal in the finished catalyst. The mixture is then kept under agitation at 80 C until the greater part of the hydrochloric acid has evaporated. It is then dried in an oven at 110 C for 4 hours and subsequently in a muffle at 240 C for 4 hours. The catalyst obtained is sieved to remove powder with a grain size of less than 60 mesh and is then loaded into a cylindrical reactor (height 20 cm; diameter 2.5 cm) having a thermostatic jacket. The catalyst is activated in the reactor by heat in a flow of hydrogen (30 l/hour) at a pressure of 35 bar, - at a temperature of 240 C for 5 hours. In this example cumene bottoms are used which result from a process for the alkylation of benzene with propylene on a- supported phosphoric-acid catalyst, and which have the following composition: cumene 1.13 8 butylbenzenes 3¯96 % pentylbenzenes 4.46 z meta-di-isopropylbenzene 23.23 .% ortho-di-isopropylbenzene 8.3 % para-di-isopropylbenzene 25.92 8 hexylbenzenes ' 22,g % other alkylaromatics 10.1 % These cumene bottoms are distilled to separate the fraction having the following composition: cumene 1.28 8 butylbenzenes 4.46 t pentylbenzenes 5.02 % meta-di-isopropylbenzene 25.27 z ortho-di-isopropylbenzee 9.5 % para-di-isopropylbenzene 97.74 t hexylbenzenes 26.74 % The fraction distilled is mixed with various quantities of benzene to give the mixtures A, B and C which are treated by the method of the present invention. Mixture A B C benzene 4 64.49% 67.06B cumene 0.5a 0.30% 0.24% butylbenzenes 2.07% 1.31% 1.14% pentylbenzenes 2.18% 1.486 1.20% meta-di-isopropylbenzene 14.12% 9.19% 8.60% ortho-di-isopropylbenzene 5.30% 3.458 3.32% para-di-isopropylbenzene 15.48% 10.08% 9.448 hexylbenzenes 19*948 9.718 9.10% The mixture A has a benzene/bottoms molar ratio of 1.89/1, and a bromine number of 0.6 and is fed continuously to the catalyst described above and treated under the conditions given in Table 1 below. The duration of the test is 130 hours. Table 1 also gives the compositions of the reaction mixture for average samples taken at the times indicated and the values of the molar conversion of the cumene bottoms, the percentage weight ratio of the cumene produced to the bottoms converted and the bromine number of the reaction products. Table 1 Time (hours) 1-35 36-70 71-105 106-130 Benzene/bottoms molar ratio 1.89 1.89 1.89 1.89 Hydrogen/organic molar ratio 2.87 2.87 2.87 2.87 Temperature ( C) 200 200 200 200 Pressure (bar) 34 34 34 34 Rate (volumes/volume hour) 1.33 1.33 1.33 1.33 Composition samples Paraffins + naphthenes (%) 7.86 5.49 5.22 5.04 benzene . (%) 49.75 50.34 50.36 49.74 cumene (%) 11.44 9.46 8.28 7.7 butylbenzenes (%) 0.75 1.00 1.28 1.05 pentylbenzenes (%) 0.26 0.42 0.73 0.81 di-isopropylbenzenes + he > : :ylbenzenes (t) 26.99 30.14 30.51 32.3 heavies (%) 3.00 3.15 3.62 3.35 Bottoms mclar conversion (%) 45.84 39.51 38.78 35.20 (cumene produced/bottoms converted) 100 Bromine number 0.01 0.01 0.01 0.01 Similarly, the mixture B, which has a benzene/bottoms molar ratio of 4.13/1 and a bromine number of 0.5, is treated on the catalyst used in the preceding test, over a period of from 131 to 182 hours. The data from the test are given in Table 2. Table 2 Time (hours) 131-170 171-182 Benzene/bottoms molar ratio 4.13 4.13 Hydrogen/organic molar ratio 2.5 2.5 Temperature ( C) 200 220 Pressure (bar) 34 34 Rate (volumes/volume hour) 1.33 1.33 Composition samples Paraffins + naphthenes (8) 3.83 4.94 benzene (%) 68.52 65.64 cumene (%) 6.40 11.32 butylbenzenes (%) 0.58 0.51 pentylbenzenes (%) 0.32 0.34 di-isopropylbenzenes + hexylbenzenes (%) 19.07 16.03 heavies (t) 1.29 1.20 Bottoms molar conversion (t) 41.19 50.55 (cumene produced/bottoms converted)100 47.9 69.1 Bromine number 0.01 0.01 Similarly, the mixture C, which has a benzene/bottoms molar ratio of 4.59/1 and a bromine number of 0.5, is treated on the catalyst used in the preceding test, over a period of 183 to 320 hours. The data from the test are given in Table 3. Table 3 Time (hours) 183- 221- 265- 281- 291- 302 220 264 280 290 301 320 Benzene/bottoms molar ratio 4.59 4.59 4.59 4.49 4,59 4,59 Hydrogen/organic molar ratio 2.5 2.5 2.5 5.20 1.25 2.5 Temperature ( C) 220 2.20 220 220 220 220 Pressure (bar) 34 34 34 34 34 34 Rate (volumes/volume hour) Composition samples Paraffins + naphthenes (8) 3.89 4.1 4.24 4.41 3.47 3.92 benzene (%) 70.04 67.9 69.51 75.31 67.01 70.2 cumene (%) 9.21 10.48 9.95 11.11 9.96 9.05 butylbenzenes (%) 0.55 0.65 0.64 0.28 0.60 0.62 pentylbenzenes (t) 0.38 0.66 0.64 0.31 0.77 0.76 di-isopropylbenzenes + hexylbenzenes (%) 14.88 14.69, 13.4 8.33 16.69 13.96 heavies (%) 1.06 3.16 1.62 0.26 1.49 1.40 Botooms molar conversion (%) 51.00 51.63 55.88 72.57 45.04 54.03 (cumene produced/botooms converted)100 59.5 66.8 58.6 50.4 72.8 55.1 Bromine nunr 0.01 0.01 0.01 0.01 0.01 0.01 Example 2 258 of the weight of the catalyst discharged from the reactor at the end of the tests of Example 1 is replaced by the same fresh catalyst. The catalytic composition thus obtained is used to treat the following mixtures. To cumene bottoms having the following composition: cumene 0.65% butylbenzenes 3 918 pentylbenzenes 5.35% meta-di-isopropylbenzene 22.61% ortho-di-isopropylbenzene 10.05% para-di-isopropylbenzene 31 50t hexylbenzenes 21.39% other alkylaromatics 4.54% there is added benzene to give the mixture F having the following composition: benzene 81.008 cumene 0.12% butylbenzenes 0.74% pentylbenzenes 1.02% meta-di-isopropylbenzene 4.30% ortho-di-isopropylbenzene 1.918 para-di-isopropylbenzene 5.998 hexylbenzenes 4.06% other alkylaromatics 0.868 The mixture F has a benzene/bottoms molar ratio of 9.64/1 and a bromine number of 0.25. Moreover cumene bottoms, the composition whereof is given above, are distilled to separate the fraction having the following composition: cumene 0.83% butylbenzenes 4.97% pentylbenzenes 6.80% meta-di-isopropylbenzene 25.54% ortho-di-isopropylbenzene 1O.968 para-di-isopropylbenzene 29. 08% hexylbenzenes 21.86 This distilled fraction is mixed with benzene to give mixtures D and E having the compositions: Mixture D: benzene 67.25% cumene 0.278 butylbenzenes --1.63 pentylbenzenes 2.23 meta-di-isopropylbenzene 8.36 ortho-di-isopropylbenzene 3.59 para-di-isopropylb-enzene 9.52 hexylbenzenes 7.1f Mixture E: benzene 80.4% cumeni 0.168 butylbenzenes 0.97% pentylbenzenes - 1.338 meta-di-isopropylbenzene 5 O18 ortho-di-isopropylbenzene 2.15% para-di-isopropylbenzene 5.70% hexylbenzenes 4.28% The mixture D has a benzene/bottoms molar ratio of 4.87/1 and a bromine-number of 0.5 and the mixture E has a benzene/bottoms molar ratio of 10.35/1 and a bromine number of 0.25. Other cumene bottoms having the following composition: cumene 0.12% butylbenzenes 1.76% pentylbenzene 5.34% meta-di-isopropylbenzene 24.32% ortho-di-isopropylbenzene 11 08% para-di-isopropylbenzene 30.19% hexylbenzenes 21.868 other alkylaromatics 5.33% are distilled to separate the fraction having the following composition: cumene 0.148 butylbenzenes 1.998 pentylbenzenes 6 028 meta-di-isopropylbenzene 25.32% ortho-di-isopropylbenzene 12 058 para-di-isopropylbenzene 31.38% hexylbenzenes 22.92% other alkylaromatics 0.108 The distilled fraction is mixed with benzene to give the mixture G having the following composition: benzene 80.96% cumene 0.03% butylbenzenes 0.38% pentylbenzenes 1.15% meta-di-isopropylbenzene 4.828 ortho-di-isopropylbenzene 9.298 para-di-isopropylbenzene 5.978 hexylbenzenes 4.36% The mixture G has a benzene/bottoms molar ratio of 9.64/l and a bromine number of 0.26. The mixture D is used sin the test for 1 to 112 hours (Table 4). The mixture E is used in the test from 113 to 171 hours (Table 5). The mixture F is used in the test from 172 to 308 hours (Table 7). The mixture G is used in the test from 309 to 350 hours (Table 6). Table 4 Time (hours) 1 - 17 - 52 - 83 16 51 82 112 Benzene/bottoms molar ratio 4.87 4.87 4.87 4.87 Hydrogen/organic molar ratio 2.5 2.5 2.5 2.5 Temperature ( C) 220 220 220 250 Pressure (bar) 35 35 25 35 Rate (volumes/volume.hour) 1.67 1.67 1.67 1.67 Composition samples Paraffins + naphthenes (8) 5.22 4.32 4.28 6.01 benzene (t) 71.98 70.76 72.17 63.12 cumene (%) 19.47 18.04 11.81 25.50 butylbenzenes (%) 0.37 0.41 0.37 0.56 pentylbenzenes (%) 0.16 0.48 0.40 0.27 di-isopropylbenzenes + hexylbenzenes (%) 8.75 11.25 10.09 4.14 heavies (%) 0,05 0.73 0.79 0.29 Bottoms conversion ... ..(%) 90.39 60.67 64.76 85.54 (cumene produced/bottoms converted)100 72.5 69.3 63.7 104.1 Bromine number 0.01 0.01 0.01 0.01 Table 5 Time (hours) 113-152 153-171 Benzene/bottoms molar ratio 10.35 10.35 Hydrogen/organic molar ratio 2.3 1.14 Temperature ( C) 250 250 Pressure (bar) 1 35 35 Rate (volumes/volume.hour) 1.67 1.67 Composition samples Paraffins t naphthenes (z) 3.90 3.74 benzene (t) 76.04 79.28 cumene (8) 17.89 15.54 butylbenzenes (%) 0.37 0.28 pentylbenzenes (%) 0.10 0.04 di-isopropylbenzenes + hexylbenzenes (t) 1.70 1.09 heavies (%) Bottoms molar conversion (%) 90.08 93.64 (cumene produced/bottoms converted)100 115.9 96.8 Bromine number 0.01 0.01 Table 6 Time (hours) 309-350 Benzene/bottoms molar ratio 9.64 Hydrogen/organic molar ratio 2.28 Temperature ( C) . 270 Pressure (bar) 35 1.67 (volumes/volume.hour) Composition samples Paraffins + naphthenes (%) 3.11 benzene (%) 78.70 cumene (%) 13.57 butylbenzenes (%) 0.13 pentylbenzenes (%) 0.20 di-isopropylbenzenes + hexylbenzenes (8) 4.05 heavies (%) 0.07 Bottoms molar conversion (%) 76.55 (cumene produced/bottoms converted)10 101.7 Bromine number 0.01 Table 7 Time (hours) 172- 217- 244- 281 216 243 280 308 senzene/bottoms molar ratio 9.64 9.64 9.64 9.64 Hydrogen/organic molar ratio 2.28 2.28 4.56 4.56 Temperature ( C) 250 250 270 270 Pressure (bar) 35 35 35 35 Rate (volumes/volume hour) 1.67 1.67 1.67 1.67 Composition samples Paraffins + naphthenes (t) 3.54 2.94 2.97 2.80 benzene (%) 77.04 78.08 79.07 79.61 cumene , (t) 16.83 13.41 13.78 11.75 butylbenzenes (%) 0.32 0.28 0.23 0.20 pentylbenzenes (%) 0.08 0.22 0.18 0.22 di-isopropylbenzenes + hexylbenzenes (83 1.91 5.21 3.64 5.40 heavies (%) 0.05 0.14 0.08 0.14 Bottoms molar conversion (8) 88.25 67.96 77.61 66.79 (cumene produced/bottoms converted)100 117.3 121.3 109.2 108.2 Bromine number 0.01 0.01 0.01 0.01 Example 3 An aqueous solution of nickel nitrate in distilled water was prepared. The commercial acid earth FILTROL G 24 described in Example 1 was added to this solution in quantities such as to give a nickel content (as the metal) of 2% in the finished catalyst. The addition was carried out with the solution under agitation, at 80 C. The greater part of the water was then evaporated and the solid obtained was dried at 1000C for 4 hours and at 350 C for 4 hours. The solid was sieved to remove fine powder and the catalyst was discharged into a jacketted tubular steel reactor (height 20 cm, diameter 2.5 cm) where it was activated by a flow of hydrogen (30 l/hour) at 350C for 5 hours and at atmospheric pressure. To the catalyst thus activated was fed the mixture H (1 to 10 hours) and the mixture I (103 to 270 hours) given in Example 2 above. The data are given in Tables 8 and 9 below. Table 8 Time (hours) 1-10 11-26 27-54 55-78 79-102 Beniene/bottans molar ratio 3.64 3.64 3.64 3.64 3.64 Hydrogen/orgnnic molar ratio 1.40 1.40 1.40 1.40 1.40 Temperature ( C) 250 250 250 250 250 Pressure (bar) 35 35 35 35 35 Rate (volumes/volume hour) 1.67 1.67 1.67 1.67 1.67 Composition samples Paraffins + naphthenes (%) 4.67 4.44 4.21 3.98 3.46 benzene (%) 77.62 77.98 76.85 76.55 77.55 cumene (%) 16.59 16.03 17.47 17.58 17.47 butylbenzenes (%) 0.14 0.11 0.12 0.09 0.06 pentylbenzenes (%) 0.20 0.29 0.29 0.30 0.23 di-isopropylbenzenes + hexylbenzenes (%) 0.83 1.19 1.06 1.40 1.23 heavies (%) Bottoms molar conversion (%) 95.3 93.2 93.9 92.0 92.9 (cumene produced/botooms converted)100 99.9 . 98.7 106.7 109.6 107.8 Bromine number 0.01 0.01 0.01 0.01 0.01 Table 9 Time (hours) Renzene/bottcs molar ratio 9.64 9.64 9.64 9.64 9.64 9.64 Hydrogen/organic molar ratio 1.40 1.40 1.40 1.40 1.40 1.40 Temperature ( C) 250 250 250 250 250 250 Pressure (bar) , 35 35 35 35 35 35 Rate (volumes/volume hour) 1.67 1.67 1.67 1.67 1.67.1.67 Composition samples Paraffins + naphthenes (%) 3.99 3.78 3.85 3.86 3.44 3.74 benzene (%) 77.98 78.33 77.64 77.77 77.27 77.25 cumene (%) 16.27 15.05 15.70 15.00 15.51 15.40 butylbenzenes (%) 0.04 0.03 0.15 0.20 0.20 0.24 pentylbenzenes (8) 0.25 0.31 0.16 0.23 0.23 0.16 di-isopropylkenzenes + hexylbenzenes (%) 1.46 2.27 2.44 2.78 3.27 3.19 heavies (%) 0.01 0.13 0.07 0.17 0.08 - Pttans molar conversion (%) 9.10 86.0 85.0 83.0 79.9 80.4 (cumene produced/bottoms converted)100 109.9 107.6 113.6 111.3 119.4 117.8 Bromine number 0.01 0.01 0.01 0.01 0.01 0.01 . Example 4 The catalyst of Example 3 was used to treat the mixture L having the following composition: paraffins | naphthenes 2.998 benzene 78:358 cumene 13.00% butylbenzenes 0.09% pentylbenzenes 0.24%. meta-di-isopropylbenzene 1.56% ortho-di-isopropylbenzene 0.798 para-di-isopropylbenzene 1.838 hexylbenzenes 1.02% other alkylaromatics 0.03% This mixture, which has a bromine number of 0,40, is the liquid effluent from the cumene reactors and from the cumene bottoms. The data from this test are given in Table 10 below. Table 10 Time (hours) 1-25 Hydrogen/organic molar ratio 1.4 Temperature ( C) 250 Pressure (bar) 35 Rate (volumes/volume.hour) 1.67 Composition samples Paraffins + naphthenes (%) 5.11 benzene (%) 78.07 cumene (z) 16.81 butylbenzenes (%) 0.06 pentylbenzenes (%) meta-di-isopropylbenzene (%) 0.51 ortho-di-isopropylbenzene (%) para-di-isopropylbenzene (%) 0.24 hexylbenzenes (%) other alkylaromatics {%7 Bottoms molar conversion (%) 82.1 (cumene produced/bottoms converted)100 85.6 Bromine number 0.01

Claims: CLAIMS 1. Method for the dealkylation and transesterification of cumene bottoms, characterised in that the bottoms, possibly after the addition of benzene, are placed in contact with a catalyst constituted by a natural silico-aluminate with a silica/alumina ratio greater than or equal to3/1,pretreated with a mineral acid, and on which a metal belonging to the eighth group of the periodic system of the elements has been deposited and the reaction is carried ogt in the liquid phase under hydrogen at a pressure of from 10 to 60 bar and at a temperature of from 150 to 3500C until a substantial quantity of the bottoms has been converted into benzene and cumene and the benzene and cumene are separated and recovered from the reaction mixture. 2. Method according to Claim 1, characterised in that the natural silico-aluminate is bentonite with a montmorillonite content of from 60 to 80% by weight. 3. Method according to Claim 1, characterised in that the natural silico-aluminate is pretreated with sulphuric acid, hydrofluoric acid or nitric acid. 4. Method according to Claim 1, characterised in that the catalyst contains a group VIII metal in quantities of from 0.05 to 5 by weight with respect to the natural silico-aluminate. 5. Method according to Claim 4, characterised in that the catalyst contains palladium or platinum in quantities of from 0.1 to 18 by weight with respect to the natural silico-aluminate. 6. Method according to Claim 4, characterised in that the catalyst contains nickel or cobalt in quantities of from 1 to 5% by weight with respect to the natural silico-aluminate. 7. Method according to Claim 1, characterised in that the catalyst is activated by treatment in an atmosphere of hydrogen for 3 to 5 hours at 150 to 5000 C. 8. Method according to Claim 1, characterised in that it is carried out with a molar ratio between the benzene and the cumene bottoms df from 0/1 to 20/1. 9. Method according to Claim 8, characterised in that the molar ratio varies from 2/1 to 10/1. 10. Method according to Claim 1, characterised in that it is carried out under a pressure of hydrogen of from 20 to 40 bar. 11. Method according to Claim 1, characterised in that it is carried out with a rate of passage of the liquid reaction mixture over the catalyst cf from 0.5 to 5 volumes of the mixture itself per volume of catalyst per hour.

Inventors: BRUNDU, GAVINO, MESSINA, GIUSEPPE, MORETTI, MARIO DOMENICO
Applicants: ENICHEM ANIC S.P.A.
Application year: 1985
Main classification: C07C15
IPC codes: C07C6