Semiconductor devices consisting of epitaxial material

Abstract: A semiconductor device consisting of epitaxial material is provided with at least one monoatomic layer of doping atoms, i.e. with a layer which is just one atom thick. A particularly preferred device is a field effect transistor in which case the Dirac-delta doped layer 13 extends between the source and drain zones (18, 19) respectively. The field effect transistor can be constructed either with a homogeneous structure or with a hetero structure or with a superlattice structure. The field effect transistors described herein have a high transconductance and are capable of operating at high current densities.

Description: The present invention relates to improved semiconductor devices consisting of epitaxial material and has particular reference to related devices comprising injection diodes and lasers in accordance with the preamble of claim 1 and claim 2, to a semiconductor light wave detector in accordance with claim 4, and to an improved optically bistable device in accordance with the preamble of claim 4. The principal object underlying the present invention is to provide the named semiconductor devices with decisively improved characteristics without unduly complicating the manufacture thereof. In order to satisfy this object there is provided in one particularly favoured embodiment of the invention an injection diode, which can also be modified to form an injection laser. Thus, according to the present teaching, an injection diode comprises in sequence a first layer of a highly doped n-type semiconducting substrate, a second layer of a highly doped n-type semiconducting material, a third layer of a distinct intrinsic semiconducting material and a fourth layer of a highly doped p-type version of the material of said second layer, wherein the first and second electrical connections are respectively made to said fourth layer and to at least one of said first and second layers, and is characterised in that one or more pairs of Dirac-delta doped monoatomic layers are provided in said third intrinsic layer, the first Dirac-delta doped monoatomic layer of each pair comprising a monoatomic layer of donors and the second Dirac-delta doped monoatomic layer of each pair comprising a monoatomic layer of acceptors positioned parallel to and spaced apart from the first Dirac-delta doped layer of the pair on the side thereof facing said fourth layer, and in that said Dirac delta-doped monoatomic layers have a dopant concentration higher than the bulk solubility limit in the host crystal. In order to convert this injection diode into an injection laser it is only necessary to make one side face of said device disposed parallel to the direction of said sequence of layers specularly reflective and to make a second side face extending parallel to the first side face partially reflective. In the above devices the doping atoms in the Dirac-delta doped layers are confined to a single layer which is just 1 atom thick. Typical surface concentration of the donors (acceptors) in this monoatomic layer are 10¹¹ to 10¹⁴ cm⁻². From these figures it will be seen that only some of the atomic positions in the monoatomic layer are occupied by doping atoms. Nevertheless, the invention makes it possible, surprisingly, to locally exceed the limit of the solubility of the doping element in the host crystal and this leads to a higher concentration of free carriers in the semiconductor material which has beneficial effects on the performance of the semiconductor device (the maximum concentration of free electrons in the semiconductor material is normally determined by the maximum solubility of the doping element in the host crystal). It is admittedly known from the paper by C.E.C. Wood et all entitled "Hyper-thin-Channel MBE GaAs Power FET's By Single Atomic Plane Doping" given to the International Electron Devices Meeting from 3 to 5 December 1979 as published by the IEEE in 1979, pages 388 and 389 to provide doping on only one atomic plane during MBE growth of an FET structure on GaAs. However, here there is only one plane of dopants in the form of donors which extend between the source and the drain electrodes of the FET. The referenced paper does not concern itself with other devices and does not suggest the use of alternating planes of acceptors and donors separated by intrinsic material and extending in planes perpendicular to the direction between spaced apart electrodes. The Dirac-delta doping of the diode or laser structure proposed herein forms V-shaped potential wells in which electrons and holes collect. The permitted energy states of the electrons and holes are sub-band levels in the V-shaped potential wells. Radiative electron hole transitions take place between the sub-bands of the V-shaped potential wells. A device of this kind has high efficiency (quantum efficiency) as a result of the immediate proximity of the n-and p-Dirac-delta doped layers. The arrangement also makes possible the emission of light quanta with an energy which is smaller than the band gap of the host crystal. The monoatomic layer of doping atoms is preferably provided, in accordance with the invention, by the use of molecular beam epitaxy. In the normal growth mode of a molecular beam epitaxy installation the host crystal grows by vaporisation of the elements of the crystals from effusion cells, with the elements combining at the surface of the substrate that is being grown to form the semiconductor compound in epitaxial form. In the impurity growth mode only the doping element is vaporised and it is this that creates the (fraction of a) monoatomic layer of donor (acceptors) atoms. The doping only takes place at one particular plane (z = z₀). At all other locations (z ≠ z₀) the intended doping is zero. The unintentional doping by residual impurities should be kept as low as possible. From the above it can be seen that the doping profile is described by the Dirac-delta function: N D = N 2D δ (z-z₀) where N D equals the doping concentration in three dimension, N 2D is the two-dimensional doping concentration, and δ (z-z₀) is the Dirac-delta function having the the value infinity at z = z₀ and the value 0 at all other values of z. For the sake of simplicity the expression Dirac-delta-doping will henceforth be designated D³. Although the doping elements are spatially fixed within one atomic plane, the free carriers diffuse and their typical smearing length is the Debeye screening length 1 D . Furthermore, pronounced carrier confinement of localisation occurs in the V-shaped potential wells which leads to low threshold currents for the laser. The new current injection laser thus consists of a series of n and p-type Dirac-delta function-like doping peaks. The conduction band edge and the valence band edge of the semiconductor are shaped like a sawtooth. Therefore, the structure is called a saw-tooth superlattice (STS). The band gap energy of the STS-light emitting diode (LED) or of the STS-laser is smaller as compared to the intrinsic host material, typically pure, undoped GaAs. The STS is characterised by a large overlap of electron and hole wave functions due to a quantum mechanical coupling of electrons in adjacent V-shaped quantum wells. Typical doping concentration of the STS device is 1x10¹² cm⁻² ≦ N 2D D,A ≦ 1x10¹⁴ cm⁻² typical period length of the STS device 50 Å ≦ Z p ≦ 500 Å The operation of light emitting diode devices (LED's) made from a GaAs sawtooth superlattice has been demonstrated (with doping concentrations and period lengths as specified immediately above) and light emission has been obtained in the wavelength range 900 nm ≦ λ ≦ 970 nm, i.e. at significantly longer wavelengths as compared to the wavelengths obtained with undoped GaAs (λ = 870 nm at room temperature). In corresponding layer devices laser emission has been demonstrated in the wavelength range 900 nm ≦ λ ≦ 910 nm. The sawtooth superlattice can also be used in a light wave detecting device, for example a photoconductor. Thus in accordance with a further embodiment of the present invention as defined in claim 4, there is provided a semiconductor device in the form of a semiconductor light wave detector comprising a first layer of a highly doped n-type semiconducting substrate; a second layer of a highly doped n-type semiconducting material, a third layer of a distinct intrinsic semiconducting material and a fourth layer of a highly doped n-type semiconducting material similar to said second layer, with first and second connections being provided to said fourth layer and to at least one of said first and second layers; the semiconductor device being characterised by a plurality of pairs of Dirac-delta doped monoatomic layers provided in said third intrinsic layer, with the first Dirac-delta doped monoatomic layer of each pair comprising a monoatomic layer of donors and with the second Dirac-delta doped monoatomic layer of each pair comprising a monoatomic layer of acceptors positioned parallel to and spaced apart from the associated first Dirac-delta doped layer on the side thereof facing said fourth layer, and in that said Dirac delta-doped monoatomic layers have a dopant concentration higher than the bulk solubility limit in the host crystal. A light wave detector of this kind specified in the preamble of claim 4 is generally known from US-A-3 882 533, however there the alternating p- and n-type layers can only have a minimum thickness of at least five times and preferably at least ten times the lattice constant. As a result of the arrangement using Dirac-delta doped monolayers of the present proposal electrons and holes are transported in perpendicular direction to the layers of the STS. The new photoconductor has a large gain-bandwidth product. Electrons are transported easily perpendicular to the layers due to their small effective mass m e and their comparatively high subband energy E o e . Holes are less easily transported than electrons in the perpendicular direction due to their comparatively large effective mass m hh and their small-subband energy E hh / o. Electrons therefore have a small transit time t t through the STS as compared to holes. The recombination lifetime τ of the STS can be chosen in a wide range by choosing an appropriate period length of the STS. Therefore, the ratio t t /τ which determines the gain-bandwidth product of the detector can be selected in a wide range. High speed and high gain photodetectors can be made with the STS. The STS can also be applied in optically bistable devices. In this respect, according to an aspect of the present invention as defined in claim 5, there is provided an optically bistable semiconductor device which is characterised in that it comprises, in sequence, a first layer of an n-type semiconducting substrate which may be doped or undoped, a series of alternating n-type and p-type Dirac-delta doped monoatomic layers formed on said substrate with each Dirac-delta doped monoatomic layer being separated from the next adjacent Dirac-delta doped monoatomic layer by a layer of pure, undoped intrinsic semiconductor, and in that said Dirac delta-doped monoatomic layers have a dopant concentration higher than the bulk solubility limit in the host crystal. An optically bistable switch is known from the paper by Miller et al entitled "Novel hybrid optically bistable switch: The quantum well self-electro-optic effect device" published in App. Phys. Lett. 45(1), 1. July 1984 on pages 13, 14 and 15. The optically bistable switch described here however comprises a multiple quantum well structure comprising alternating undoped layers of different materials with no intrinsic material between them. In addition the undoped layers, comprising GaAs well layers of 9.5 nm and GaAlAs barrier layers of 9.8 nm are many times thicker than a single atomic layer. An optically bistable device of this kind proposed herein requires no electrical contacts and is particularly useful as an optical switch. By way of example the device can be made so that it absorbs an incident light beam of low intensity and does not transmit this light beam. On the other hand, if the incident light beam is of high intensity above a certain threshold the device will transmit a beam of light. The optical bistability of the STS is due to a band filling of electron and hole subbands. A reduction of the optical absorption at energies close to the STS energy gap results. The recombination lifetime, which determines the optical threshold intensity at which band filling occurs can be selected by choosing an appropriate superlattice period length z p . If this period length is short then the recombination lifetime is short whereas if it is long the recombination lifetime is also long due to the resulting spatial separation of electrons and holes. For semiconductor devices using only one basic type of semiconductor material the preferred material is gallium arsenide. For semiconductor devices in accordance with the present teaching which require two distinct semiconductor materials (for example heterostructures and superlattice structures) the two distinct semiconductor materials preferably comprise gallium arsenide GaAs and aluminium gallium arsenide Al x Ga 1-x As with suitable dopants, such as silicon to produce n-type conductivity and phosphorus to produce p-type conductivity. The present teaching is generally applicable to silicon and germanium semiconductors and to compound semiconductors, in particular to III-V,II-VI and III-VI compound semiconductors. In all embodiments the doping concentration in the or each Dirac-delta doped monoatomic layer expediently lies in the range up to 10¹⁴ cm⁻² and preferably in the range 10¹¹ to 10¹⁴ cm⁻². Finally, it should be pointed out that the structures of the injection diodes and lasers claimed herein can also potentially be realised by substituting n-type materials for p-type materials and vice versa and that the claims hereof also extend to the parallel devices with such inverted structures, in which case references to donors should be read as references to acceptors, and references to electrons should be read as references to holes and vice versa. The invention will now be described in more detail by way of example only and with reference to Figs. 3 to 5a of the accompanying drawings but will be preceded by a discussion of another proposal made by the inventors relating to FET's which are not claimed here but which aid an understanding of the design and operation of the devices of Figs. 3 to 5a. In the accompanying drawings there are shown: Fig. 1 a schematic perspective view of a field effect transistor, Fig. 1a a doping profile showing the position of the Dirac-delta doped layer in the field effect transistor of Fig. 1, Fig. 1b a schematic band scheme illustrating the conductance and valence bands of a homogenous epitaxial semiconductor material used for the field effect transistor of Fig. 1 in the vicinity of the D³ layer, Fig. 1c an alternative doping profile to that shown in Fig. 1a showing the presence of three Dirac-delta doped monoatomic layers in a homogenous epitaxial semiconductor material, Fig. 2 the gate characteristic for the Schottky gate of the field effect transistor of Fig. 1, Fig. 3 a schematic perspective view of an injection laser in accordance with the present invention, Fig. 3a the band scheme for the injection laser of Fig. 3, Fig. 4 a schematic perspective view of a photoconductor in accordance with the present invention, Fig. 4a the band scheme for the photoconductor of Fig. 4, Fig. 5 a schematic perspective view of an optically bistable device in accordance with the present invention, and Fig. 5a the band scheme for the optically bistable device of Fig. 5. Turning first to Fig. 1 there can be seen a field effect transistor 10 which in this case consists of an undoped epitaxial layer of gallium arsenide 11 which is grown on a semi-insulating substrate of gallium arsenide 12 by molecular beam epitaxy. Once the layer 11 has been grown to a thickness of approximately 1 µm the usual crystal growth mode of the molecular beam epitaxy apparatus (hereinafter MBE apparatus) is interrupted by closing the gallium shutter of the gallium effusion cell and leaving the arsenic shutter of the arsenic effusion cell open. This results in an As stabilised crystal surface. The shutter of the silicon cell which is used with gallium arsenide materials is however kept open so that an impurity growth mode results. This impurity growth mode is used to grow a layer 13 which is just 1 atom thick. This layer is conveniently referred to as a monoatomic layer. In fact the surface of the compound semiconductor gallium arsenide contains 1.25 x 10¹⁵ atoms/cm², that is 6.25 x 10¹⁴ gallium atoms/cm². The two dimensional (2D) silicon concentration N 2D used for the layer 13 is smaller than 10¹³/cm² so that only a small fraction of the gallium sites of one monolayer are occupied by silicon atoms. The MBE machine used for the growth of the layers is equipped with a 2 inch (5cm) as azimuthally rotatable substrate holder and the growth region is completely surrounded by a liquid N₂ cryoshroud. The residual impurity concentration of undoped layers is p-type and in the 10¹⁴ cm⁻³ range. After growth of the monoatomic layer 13 the normal growth mode is re-adopted and a layer 14 of undoped gallium arsenide of 13 nm (300A) thickness is grown on top of the monoatomic layer 13. Because the monoatomic layer 13 is very thin the crystalline structure of the top layer 14 of gallium arsenide continues the crystalline structure of the layer 11. The wafer grown in this way is then provided in the usual way with source 15, gate 16 and drain regions 17 to complete the structure of the field effect transistor. The source and drain regions are an alloy of gold and germanium and the gate region is formed of pure aluminium and constructed as a Schottky gate. During the diffusion process the source and drain regions form highly conductive zones 18, 19 within the wafer and the monoatomic layer 13 extends into these two zones 18 and 19. The monoatomic layer 13 represents an abrupt step change in the doping profile which is illustrated in the graph of Fig. 1A which shows the monoatomic layer at a distance z₀ in the z-direction below the surface of the field effect transistor. Because of the sharpness of the change in the doping profile it can be conveniently represented by the mathematical Dirac-delta function and is referred to throughout as a Dirac-delta doped layer. It has been shown by transmission electron microscopy that the layer 13 is indeed just one atom thick. The proximity of the D³ layer to the surface is favourable for FET operation. The distance of the Dirac-delta doped layer from the semiconductor surface (Schottky contact) is at most 1000 Å. The energy band diagram of a Dirac-delta doped epitaxial layer with a metal contact on top is shown in Fig. 1B and the associated doping profile for the D³ layer at z₀ is illustrated immediately below it in Fig. 1C. As a result of electrostatic attraction the electrons stay close to their parent ionised donor impurities and form a two-dimensional electron gas in the V-shaped potentional well. Size quantization takes place in the narrow potential well. The electron de Broglie wavelength is matched to the width of the potential well and the sub-band energies can be calculated from the following expression: where q equals the elementary charge h equals Plancks constant n 2DEG equals the two dimensional electron hole gas concentration ε equals the permittivity of the semiconductor material m* equals the effective electron or hole mass. This formula is valid only for a symmetrically V-shaped potential well. In reality the potential well is not truly symmetrical, as illustrated in Fig. 1b, due to the proximity of the surface. Fig. 1b also shows the position of the Fermi level and the barrier height qB at the metal semiconductor interface. As previously mentioned the gate region is constructed as a Schottky gate. This is done because a stable dielectric is not known which is able to insulate the gate metal from the semiconductor at room temperature. Because of the D³ layer the field between the gate and the two-dimensional electron gas formed at the layer 13 is constant. This results in the breakdown voltage of the reversely biased Schottky diode being substantially larger than in a comparable MESFET. A typical plot for the Schottky diode formed in the gate region is shown in Fig. 2. It will be noted that a large breakdown voltage V B = -11 Volts is observed and is sufficient for FET operation. The diode characteristic in the forward direction is shown for the two temperatures 300 and 77°K with threshold voltages of 0.5 and 0.7 Volts respectively. These voltages indicate that an enhancement type operation of the D³ FET with a forward biased Schottky biased Schottky diode is possible. The ideality factor (n-value) measured from the diode characteristic of Fig. 2 in the forward direction is found to have the excellent value of n = 1.05. In addition the built-in voltage of the diode is determined to be V bi = 0.73 Volts. Application of a reverse voltage depletes the 2 DEG associated with the D³ layer due to the field effect. Measurements on sample FETs constructed in the above manner have shown that the maximum three-dimensional carrier concentration is observed at zero bias about 300Å below the gallium arsenide surface and is 7.5 x 10¹⁸ cm⁻³. Such high electron concentrations are unknown in homogeneously doped material where the maximum doping concentration measured is 6 x 10¹⁸ cm⁻³. The extremely high electron concentrations are favourable for field effect transistor operation because the transconductance g m is proportional to the doping concentration n or square root of n according to the Schottky model and the saturated velocity model respectively. Fig.3 illustrates an injection laser 40 which is also constructed in accordance with the present invention. The laser diode of Fig.3 has a first layer of a highly doped semiconducting substrate 41, in this case gallium arsenide with a donor concentration in the range 10¹⁷ to 10¹⁸/cm⁻³. This first layer 41 is followed by a second layer of a distinct semiconducting material which is also epitaxially grown. In this case the second layer 42 consists of highly doped n-type Al x Ga 1-x As with a donor concentration in the range 10¹⁷ to 10¹⁸ cm⁻³. This second layer 42 is followed by a layer of intrinsic semiconducting material of the same type as the substrate, in this case gallium arsenide. The layer 43 is then followed by a fourth layer of a highly doped p-type version of the material of the second layer, i.e. Al x Ga 1-x As with an impurity concentration in the range 10¹⁷ to 10¹⁸/cm⁻³. A pair of D³ monoatomic layers 45 and 46 are provided parallel to one another and spaced apart in said third layer 43. The layer 45 is a layer of donors whereas the layer 46 is a layer of acceptors. The doping concentrations in these two layers again lie in the range 10¹¹ to 10¹⁴ cm⁻². The spacing between the two layers lies in the range 2.5 nm (25A) to 50 nm (500A). It is also possible to provide a plurality of pairs of D³ monoatomic layers in the third intrinsic layer 43. As can be seen from the associated band scheme shown in Fig. 3a the Dirac-delta doping arrangement in the injection laser of Fig. 3 forms two V-shaped potential wells in which the electrons and holes collect. The allowed energy states of the electrons and holes are sub-band levels in the V-shaped potential wells. Radiative electron hole transitions occur between the sub-bands of the V-shaped potential wells and generate photons which are radiated out of the device. The generation of these photons is promoted by the voltage applied across the structure via the two contacts 47 and 48 respectively. In the described form the device is in fact an injection diode. In order to convert it into an injection laser it is necessary to provide one side face with a specularly reflective coating 49 and to provide an opposite parallel side face 50 with a partially reflective coating illustrated by oblique strokes. An injection laser or diode of this kind has a high degree of efficiency (quantum efficiency) due to the immediate proximity of the n- and p D³ layers. Also the operating wavelength can be chosen to be below the wavelength associated with the band gap of the host crystal. Furthermore, pronounced carrier confinement occurs in the V-shaped potential wells which leads to low threshold currents for the device. The pairs of D³ layers lie in the active zone of the laser. Turning now to Fig. 4 there can be seen a schematic diagram of a semiconductor photodetector device. The device comprises, in sequence, a first layer of a highly doped n-type semiconducting substrate 53, a second layer of a highly doped n-type semiconducting material 54, a third layer of a distinct intrinsic semiconducting material 55 and a fourth layer of a highly doped n-type semiconducting material 56 similar to said second layer. First and second electrical connections (not shown) are provided to said fourth layer and to said first layer respectively. A plurality of pairs of Dirac-delta doped monoatomic layers 57, 57′, 58, 58′ are provided in said third intrinsic layer 55, with the first Dirac-delta doped monoatomic layer 57, 58 of each pair 57, 57′, 58, 58′ comprising a monoatomic layer of donors and with the second Dirac-delta doped monoatomic layer 57′, 58′ of each pair comprising a monoatomic layer of acceptors positioned parallel to and spaced apart from the associated first Dirac-delta doped layer on the side thereof facing said fourth layer. The pairs of Dirac-delta doped layers within the intrinsic layer 55 form the STS. The band scheme for this device can be seen from Fig. 4a. It will be noted that so far as the subband energies are concerned the subband energy for electrons E o e is greater than the subband energy for holes E o hh , as mentioned earlier in the introduction to the specification. In the example shown the first, second and fourth layers are all of gallium arsenide and have respective impurity concentrations of 10¹⁷-10¹⁹, 10¹⁷-10¹⁹ and 10¹⁷-10¹⁹ cm⁻³, respectively. The layer 55 consists of GaAs. The acceptor and donor concentrations in the D³ layers again lie in the range 10¹¹ to 10¹⁴ cm⁻². The spacing between sequential D³ layers is typically 2.5-25nm (25-250 Å) and the layers 54, 55 and 56 have respective thicknesses of 0.1-0.5 µm, 0.1-1.0 µm and 0.1-0.5 µm. Turning now to Fig. 5 there is shown a schematic illustration of the build-up of an optically bistable device. This device comprises a gallium arsenide substrate 60, which may be doped or undoped, and a series of alternating n-type and p-type Dirac-delta doped monoatomic layers 61 to 69 formed on the substrate with each said Dirac-delta doped monoatomic layer being separated from the next adjacent Dirac-delta doped monoatomic layer by a layer of pure undoped intrinsic semiconductor material 70, in this case GaAs. The energy band diagram for this optically bistable device is shown in Fig. 5a and the properties of the device may be varied, amongst other things, by varying the separation between the D³ layers, located in the example of Fig. 5 at z1, z2, z3, z4 etc., which controls the superlattice period length z p and affects the recombination lifetime as described earlier in the introduction to the specification.

Claims: An epitaxial device in the form of an injection diode (40) comprising in sequence a first layer (41) of a highly doped n-type semiconducting substrate, a second layer of a highly doped n-type semiconducting material (42), a third layer of a distinct intrinsic semiconducting material (43) and a fourth layer (44) of a highly doped p-type version of the material of said second layer (42), with first and second electrical connections (47, 48) being provided to said fourth layer (44) and to at least one of said first and second layers (41, 42), characterised in that one or more pairs of Dirac-delta doped monoatomic layers (45, 46) are provided in said third intrinsic layer (43), with the first Dirac-delta doped monoatomic layer (45) of each pair comprising a monoatomic layer of donors and with the second Dirac-delta doped monoatomic layer (46) of each pair comprising a monoatomic layer of acceptors positioned parallel to and spaced apart from the associated first Dirac-delta doped layer (45) on the side thereof facing said fourth layer (44), and in that said Dirac delta-doped monoatomic layers (45, 46) have a dopant concentration higher than the bulk solubility limit in the host crystal. A semiconductor device in accordance with claim 1, characterised in that one side face of said device parallel to the direction of said sequence is specularly reflecting (49) and in that a second side face extending parallel to the first side face is partially reflective (50) thereby producing laser action. A semiconductor device in accordance with claim 1, wherein one of the two distinct semiconductor materials comprises gallium arsenide GaAs and the other comprises aluminium gallium arsenide Al x Ga 1-x As. An epitaxial light wave detector comprising a first layer (53) of a highly doped n-type semiconducting substrate, a second layer (54) of a highly doped n-type semiconducting material, a third layer (55) of a distinct intrinsic semiconducting material and a fourth layer (56) of a highly doped n-type semiconducting material similar to said second layer (54), with first and second electrical connections being provided to said fourth layer and to at least one of said first and second layers; the device being characterised by a plurality of pairs of Dirac-delta doped monoatomic layers (57, 57′, 58, 58′) provided in said third intrinsic layer (55), with the first Dirac-delta doped monoatomic layer (57; 58) of each pair (57, 57′; 58, 58′) comprising a monoatomic layer of donors, and with the second Dirac-delta doped monoatomic layer (57′, 58′) of each pair (57, 57′; 58, 58′) comprising a monoatomic layer of acceptors positioned parallel to and spaced apart from the associated first Dirac-delta doped layer (57; 58) on the side thereof facing said fourth layer (56), and in that said Dirac delta-doped monoatomic layers have a dopant concentration higher than the bulk solubility limit in the host crystal. An epitaxial optically bistable semiconductor device, characterised in that the device comprises, in sequence, a first layer (63) of an n-type semiconducting substrate, which may be doped or undoped, a series of alternatingly n-type and p-type Dirac-delta doped monoatomic layers (62, 63, 64, 65, 66, 67, 68, 69) formed on said substrate with each said Dirac-delta doped monoatomic layer (61 to 69) being separated from the next adjacent Dirac-delta doped monoatomic layer by a layer (70) of pure undoped intrinsic semiconductor material, and in that said Dirac delta-doped monoatomic layers have a dopant concentration higher than the bulk solubility limit in the host crystal. A semiconductor device in accordance with any one of the preceding claims wherein the doping concentration in the or each Dirac-delta doped monoatomic layer lies in the range from 10¹¹ to 10¹⁴ cm⁻².

Inventors: FISCHER A, HORIKOSHI YOSHIJI, PLOOG KLAUS, SCHUBERT E, FISCHER, A., HORIKOSHI, YOSHIJI, PLOOG, KLAUS, SCHUBERT, E.
Applicants: MAX PLANCK GESELLSCHAFT, MAX-PLANCK-GESELLSCHAFT ZUR FOERDERUNG DER WISSENSCHAFTEN E.V.
Application year: 1985
Main classification: H01L29
IPC codes: H01L29, H01L21, H01L31, H01L33, H01S5