LUMINESCENT CERAMIC PLATES

Abstract: A ceramic plate capable of luminescing under electron X-ray or other ionising radiation comprises a fine powder bound in water glass such as sodium or potassium hydroxy silicates, or sodium or potassium borates. The powder is typically less than 50 mu m mean particle size e.g. 10 mu m size. Powder material includes: calcium borate, yttrium aluminate, zinc yttrium silicate, calcium silicate, calcium germanate, Magnesium borate, Barium borate, strontium borate. Dopant materials may be Tb, Tm, Ce, Eu, Pr, Yb, Mn, Cu, Ag, Pb added in amounts up to 15% weight or more. The plate is formed by mixing powder and water glass into a dough. The dough is pressed in a mould to remove excess water glass and fired at about 950<o>C for about 8 hours. Alternatively excess water is used when mixing powder and water glass. This excess water is allowed to evaporate whilst the plate is in a mould prior to pressing and firing. The plate may be used as a cathode ray tube face plate, the detector in an X-ray thermoluminescent system, or an X-ray scintillator.

Description: LUMINESCENT CERAMIC PLATES Technical Field This invention relates to luminescent ceramic plates capable of luminescing when irradiated * by electrons, X-rays, ultra-violet rays or Q -rays. Such plates are useful as cathode ray tube (C.R.T.) face plates, ther oluminescent plates, or scintill tors. Background Art Face plates for cathode ray tubes are usually a layer of a phosphor powder in a binder settled onto a glass *' plate. Electrons strike the phosphor layer resulting in emission of light. A disadvantage of these powder layers is their susceptibility to damage when high energy electron beams are used to obtain high light outputs. In addition under the latter conditions the glass face plate can be damaged. Attempts at overcoming this disadvantage include the use of a thin single crystalline film grown onto the surface of the glass. This gives increased burn resistance but produces multiple reflections within the film and hence poor performance. Another way of employing a phosphor layer is described in G.B. Patent No. 2,094,823 B and G.B. Patent Application No. 2,1_>6,194A. In the former a dried powder layer is fired at 1,350°C for 8 hours to give a ceramic layer. In the latter specification powdered phosphor is held under pressure, e.g. 15 hectobar, in a mould whilst heated to 1 ,_550°C. The resultant ceramic can be cut and polished and used as a cathode ray tube face plate. Thermoluminescent plates may be used in radiology apparatus. This is described for example in G.B. Patent Application 83 27883. A plate of thermoluminescent material is exposed to an X-ray pattern in the same manner as X-ray photographic film. The plate is heated and radiates visible light corresponding to the X-ray pattern. This visible light is of low intensity and needs to be detected by a sensitive detector such as a photomultiplier. Subsequent heating clears the pattern and the plate can then be re¬ used. Various detector materials can be used. For example single crystal materials such as lithium tetraborate, and doped with copper or manganese, etc.; or recrystallised glass. The detector plate can be a single large plate or a mosaic of smaller plates. In all cases the cost of a detector plate is high. Also it is difficult to produce a plate sensitive enough by the above processes. Scintillators are used in various systems to provide detection of X-rays. For example a sheet of scintillator material can be used as a backing for X-ray film to enhance the image formed on the film on exposure to an X-ray pattern. The invention provides luminescent plates capable of production in quite large sizes e.g. up* ' to 50 x 50 cms at relatively low cost. Disclosure of Invention According to this invention a luminescent plate comprises a powdered material bonded with water glass preferably or any other low melting point glass and formed into a ceramic. The powder material may be selected from:- calcium borate e.g. C B 0 4 , Ca^B p O-, Ca 3 B„0_ yttrium aluminate (YAG) zinc yttrium silicate (ZYS) calcium silicate CaSiO.,, Ca 2 Si0 4 calciu germanate e.g. CaGe 2 0 5 * , CaGe.O- magnesium borate _IgE 2 0 4 , K 2 B 2 0 5 , ι*- 3 B 2 0g barium borate BaB 2 0 4 , BaB 4 0 7 , Ba3 g 0, 3 strontium borate SrB 2 0 4 , SrB 4 0 , Sr 2 3 2 0 5 , Sr 3 B 2 0 6 . Activators for the powders may be ions of rare earth elements such as Tb, Tm, Ce, Ξu, Pr, Yb, Gd, or the ions of Kn, Cu, Ag, Pb and may be added by up to 1 $ by weight. The water glass may be sodium or potassium hydroxy silicate, or sodium or potassium borates. According to this invention a method of producing luminescent plates comprises the steps of:- (i) - preparing a fine powder of material; (ii) - mixing a quantity of the powder with a quantity of water glass to give a dough; (iii) - pressing the dough in a shaped mould under a pressure and for a tine sufficient to remove excess water glass; (iv) - firing the shaped dough at a temperature below the melting point of the powder for a time until a ceramic plate is formed. The powder is preferably less than 50 am particle size. For step (i) the activators may be added as an oxide to the other components and milled together. Following milling the mixture may be heated in air for 8 hours or longer at 1,000°C or more. The final mixture may then be milled to reduce the mean particle size to less than 50 um. After step (iv) the plate may be ground, and polished, to the required shape, and finish, flat or curved. _2 The pressure applied to the dough is typically between 8-10 kg cm 2 (100 and 150 lb/ inch ) applied for 4 to 24 hours . The firing temperature is typically above 950°C e .g. 950° to 1 , 150°C held for around eight hours. Alternatively, after step (ii) the dough is allowed to dry before being pressed as in step (iii). In this case the water glass is diluted with water prior to step (ii). Different moulds may be used for drying and pressing. Brief Description of Drawings Embodiments of the invention will now be described by way of example only with reference to the accompanying drawings of which:- Figure 1 is a part sectional view of a cathode ray tube having a ceramic face plate; Figure 2 is a side view of a patient having a chest X-ray, with a thermoluminescent detector plate; Figure 3 is a side view of apparatus for heating the detector plate and recording the resultant image; Figure 4 is a graph showing light output of the detector plate in Figure 2; Figure 5 is a sectional view of an x-ray cassette having a scintillator for enhancing X-ray film images. Detailed Description of Invention The plates may be prepared as follows:- Example 1 1. Material to be bonded, eg. calcium borate doped with 5% by weight of Tb, was ground into a fine powder. Typically the powder size was less than 50 um, e.g. 10 urn. 2. Powder was slowly added to sodium silicate solution in the ratio 100 gms powder to 40 mis solution. The mixture was stirred until a malleable dough was obtained. 3. The dough was transferred to a mould and subjected to a -2 pressure of between 8-10 kg cm . This pressure was maintained between 4 and 24 hours. During this time about 80^ of the silicate solution was pressed out from the dough. 4. The pressed material is in the form of a hard easily handled article when removed from the press. 5. The shaped article was then fired at a temperature above 950°C but less than the powder-water glass mixture melting point, depending on the ceramic being formed. 6. The fired article is found to be a hard ceramic impervious to moisture that could be ground and polished to its final shape. * Example 2 1. Material to be bonded, eg. calcium borate doped with 5% by weight of Tb, was ground into a fine powder. Typically the powder size was less than 50 _m, e.g. 10 yum. 2. 100 gram of powder was added to a solution of 40 mis sodium silicate (Na^D2Si0 2 50^:H 2 0 0^ approximately) in 200 mis of water. The mixture was stirred until a uniform mixture was obtained. 3. The mixture was transferred to a plastic (impervious), or plaster (pervious) mould and allowed to dry until the weight attained 270 gms. 4. The partly dried plate was transferred to a metal mould and subjected to a pressure of between 8-10 kg cm . This pressure was maintained between 4 and 24 hours. During this time about 80% of the silicate solution was pressed out from the dough. 5. The pressed material is in the form of a hard easily handled article when removed from the press. 6. The shaped article was then fired at a temperature above 950°C but less than the powder-water glass mixture melting point, depending on the ceramic being formed. 7. The fired article is found to be a hard ceramic impervious to moisture that could be ground and polished to its final shape. Figure 1 shows a partly sectional view of a cathode ray tube (C.R.T.) comprising an evacuated glass envelope 1 and a ceramic face plate 2. This face plate 2 is typically 2mm thick and is fixed to the glass by a malleable silver chloride sealant 3 melted into place. Inside the envelope 1 are conventional anode and cathode structures, not shown. The face plate 2 is prepared as described earlier. The powder material may be:- YAG Tb doped, to give green, Eu to give red and Ce to give blue emission; ZYS Tb doped to give green, Eu doped to give red, Ce to give blue emission; or calcium silicate Tb doped to give green, Eu to give red and Ce to give blue emission. Kulti-colour operation may be achieved by forming a face plate of undoped material and selectively implanting dopants e.g. by ion implantation. This doping can be done in different areas or to different depths (penetron operation). The cathode ray tube 2 may be used in head-up displays (HUD) or other high brightness displays. Being a ceramic material the face plate 2 can withstand high electron beam currents without burning. Another use of ceramic plates is in radiology to replace the conventional X-ray films. This is shown in Figures 2, 3, 4. As shown a patient 11 stands in front of a detector plate 12 mounted on a support 13. An x-ray source 14 is arranged to irradiate the required parts of the patient 11 in a known manner. A typical chest X-ray dose is 1 rad. giving 20 to 50 raillirad. at the plate. On irradiation the plate 12 is selectively ionised in a pattern corresponding to the selective absorption of the patient's body. Such a pattern remains intact for many days until destroyed or cleared by appropriate heating. The ionisation pattern is not visible without heating of the plate 12. The amount of light given off depends upon the amount of X- ray absorption by the plate and the temperature to which it is heated. Figure 4 shows a graph of light output. The phosphor material is calcium borate doped with 10 by weight Tb. To obtain the curves shown the plate was heated as indicated by the temperature/time graph. Light output was measured by a photomultiplier detector -3 , and expressed as counts per second x 10 /m.g. of detector material exposed/K.rad of radiation. Light emissions peak at plate temperature of about 27°C, 65°C, and 150°C. For medical applications low x-ray dosages are needed. This results in low light output from the plate 12. It is therefore usually necessary to employ very sensitive light detectors 15 that are scanned over the exposed plate 12. The detector 15 output is stored e.g. on tape 16 for display e.g. on a cathode ray tube 17. Figure 3 shows one way of reading the ionisation pattern in the plate. The plate 12 is retained by in a holder 18 with an electrical resistance heating tape 19 held against the rear surface. Thermal insulation 20 backs the heater. A second method of heating is point by point or line by line heating using heat supplied by - (a) a laser, carbon dioxide pulsed or continuous operation; (b) a heating stylus consisting of a microject of heated air or a conductively heated roller ball. A low light television camera 15 images the heated plate and sends an output to a monitor cathode ray tube 17 and recorder 16. Alternatively a photomultiplier or image intensifier unit may be used, scanned over a heated plate point by point. This scanning may be achieved by movement of the photomultiplier itself or associated fibre optic light pipes attached, or by x, y translation of the plate. For large plates an array of photo multipliers, arranged e.g. in a line, is traversed over the plate. This reduces the read time. Another method of scanning involves a row of silicon diodes arranged at a pitch of about 100 μ . or more. These detect the light emission through a fibre optic manifold which thermally isolates the plate and diodes. A mask having a 250 um slit is moved over a heated plate. The diodes are positioned just above the slit, and read a line of information at a time as the slit moves down the plate. A further method of scanning is line scan, where the image from a single line is viewed by a rotating 45° mirror situated above the plate. This image is then transferred to the photomultiplier mounted in line with the mirror. This has the advantage of requiring only the plate to be moved and in one direction only. A further use of ceramic plates is for scintillator application. In these applications the scintillator acts as a detector of X- rays, gamma rays, etc. by luminescing when irradiated. The light given off is proportional to the dose received. One use of scintillators is to reinforce the visible image obtained on X-ray films in a cassette. This is shown in Figure 5« A scintillator plate 25 forms a backing for an X-ray film 26, both supported by a holder 27. Clips 28 hold the film 26 in place. The film 26 is sensitive to both X-rays and blue light. On exposure to X-rays, e.g. as in Figure 2, some of the X-rays passing through a patient 11 are absorbed in the film 26; others pass into the scintillator plate 25. This causes blue light emission from the scintillator 25 which is absorbed by the film 26. As a result the X-ray pattern image subsequently developed in the film 26 is enhanced. A suitable scintillator is calcium borate or silicate containing Ce ions. Alternatively the plate 25 may be used both as a scintillator and a thermoluminescent plate. One suitable material is calcium silicate doped with e.g. 0. Yb. An x-ray exposure is taken as above with the plate scintillating and reinforcing the exposure of the x-ray film 26. This film is developed to provide an image quickly. The plate 25 is subsequently heated as described above and the thermoluminescent image obtained by a scanned detector. This detector output is stored for a permanent record of the X-ray exposure.

Claims: Claims: - 1. A luminescent ceramic plate comprising a finely powdered luminescent material bonded into water glass and formed into a ceramic. 5 2. The plate of claim 1 wherein the powdered material is a material selected from the group calcium borate e.g. Ca3 2 0 4 , Ca 2 B - 5 , Ca 3 B-0_ yttrium aluminate (YAG) zinc yttrium silicate (ZYS) 10 calcium silicate CaSi0 3 , Ca 2 Si0 4 calcium germanate e.g. CaGe 2 0c, CaGe 4 0 g , CaGe0 3 Magnesium borate MgB 2 0 4 , Kg 2 B 2 0 5 , MggBgOg Barium borate BaB 0 4 , BaB 4 0 7 , BaBgO-- Strontium borate SrB 2 0 4 , SrB 4 0 ? , Sr 2 B 2 0 5 , Sr^Og. 15 3. The plate of claim 2 wherein the powdered material is doped with a material selected from the group Tb, Tm, Ce, Eu, Pr, Yb, Mn, Cu, Nd, Ag, Pb. 0 4« The plate of claim 1 formed as a face plate of a cathode ray tube. 5« The plate of claim 1 formed as a thermoluminescent plate. 5 " 6. The plate of 'claim 1 formed as an X-ray scintillator. 7. A method of making the plate of claim 1 comprising the steps of:- (i) - preparing a fine powder of material; (ii) - mixing a quantity of the powder with a quantity of water glass to give a dough; (iii) - pressing the dough in a shaped mould under a pressure and for a time sufficient to remove excess water glass; (iv) - firing the shaped dough at a temperature below the melting point of the powder for a time until a ceramic plate is formed. 8. The method of claim 7 wherein an excess of water is used in step (ii) and the resultant mixture is allowed to partly dry whilst in a mould prior to step (iii). 9. The method of claim 7 wherein step (iii) utilises a _2 pressure of above 8 Kgms cm for a time of 4 to 24 hours. 10. The method of claim 7 wherein the step (iv) utilises a temperature above 950°C for a time above 4 hours. 11. The method of claim 7 wherein prior to step (i) a dopant is mixed and milled with the constituent material, fired, and then milled again until the mean particle size is less than 50 μm. 12. The method of claim 7 wherein after step (iv) the plate is ground to its final shape and surface finish.

Inventors: BORN PETER JEREMY, ROBERTSON DANIEL STEWART, YOUNG IAIN MALCOLM, BORN, PETER, JEREMY, ROBERTSON, DANIEL, STEWART, YOUNG, IAIN, MALCOLM
Applicants: SECR DEFENCE BRIT, THE SECRETARY OF STATE FOR DEFENCE IN HER BRITANNI
Application year: 1985
Main classification: C09K11
IPC codes: C09K11, G01T1, G21K4, H01J29