FLEXIBLE CHEMICALLY TREATED BUNDLES OF FIBERS, WOVEN AND NON WOVEN FABRICS AND COATED FABRICS THEREOF

Abstract: More flexible bundles of high modulus, low elongation fi­ bers are provided by the impregnated bundles of the present invention. The flexible bundle of fibers comprise a plurality of fibers having a first treatment of a moisture-reduced residue of an aqueous chemical composition and a second treatment of a moisture-reduced, partially cured impregnant of an aqueous chemical coating composition. The individual fibers in the im­ pregnated bundle were first treated with an aqueous sizing composition having at least a fiber protectorant and optionally an antistatic agent and/or coupling agent. The impregnating composition has one or more elastomeric curable polyure­ thanes that are water soluble, emulsifiable or dispersible and one or more crosslinking materials that are water soluble, emulsifiable or dispersible and water. Optionally, there may be present one or more emulsifiable or dispersible lubricants. plasticizers, polymeric materials, and flame retardants. The flexible impregnated bundles of glass fibers are useful in pro­ ducing woven and nonwoven fabrics where the fabrics can be coated with polymeric films.

Description: FLEXIBLE, CHEMICALLY TREATED BUNDLES OF FIBERS, WOVEN AND NONWOVEN FABRICS AND COATED FABRICS THEREOF The present invention is directed to chemically treated bundles of fibers such as strands and yarns, which can be fabricated into myriad products including braided fabrics and fabrics which can be coated or laminated with polymeric films. Glass fibers, which were originally developed in the 1930's, have been applied over the years as fibers, strands and yarns in numerous end uses such as textiles and reinforcement for polymeric matrices and rubber goods. Glass fibers are traditionally produced through attenuation from small orifices in a bushing of a glass batch melting furnace. The glass fibers issue forth from the orifices in molten streams and are cooled and treated with a sizing composition. The sizing composition is ordinarily an aqueous composition having components like coupling agents, lubricants and film forming polymers. The sized glass fibers are gathered into one or more bundles of fibers or strands and wound into a forming package or chopped. For textile applications, the bundles of fibers in the forming packages can be twisted or false twisted or combined with other strands and twisted or false twisted to form yarns. In producing fabrics from the yarns, the yarns which will constitute the fill yarns are usually further treated with a slashing sizing composition so that they can undergo the rigors of weaving. Fabrics having the warp and weft yarns usually are heat-cleaned to remove both the forming and slashing sizing compositions. When the glass fiber strands from the forming packages are used for reinforcement of rubber goods, a second chemical treatment or coating is usually applied to the strands to make the strands or bundles of strands or cords compatible with the rubber matrix. This second coating is known in the industry as an RFL dip coating, where the term "RFL" means resorcinol formaldehyde latex coating and where the latex material includes a diene-containing elastomer to participate in the vulcanization of the rubber matrix. Some of the outstanding properties of glass fibers that have fostered their growth in these numerous commercial applications include: relative nonflammability, heat and chemical resistances, excellent tensile and excellent dimensional stability. These advantageous characteristics of glass fibers have not been fully utilized in numerous textile fabrics because other fibers such as polyesters and nylons have much better flex fatigue characteristics than the glass fibers. tIany textile fabrics could utilize the advantageous characteristics of glass fibers, if the glass fibers were more flexible and had a better flex fatigue characteristic like polyester and nylon textiles. A few examples include woven or knitted fabrics and nonwoven scrim and chemically coated textile fabrics useful in wall coverings, carpet backings, filter fabrics, tarpaulins, pond liners or pond covers, awnings, sail cloth, electrical sleevings and harnesses and the like. For instance, textile fabrics of polyesters and polyamides such as nylon, aramide fibers like KevlarS fibers, rayon and other organic and even some inorganic man made fibers like griege glass fiber fabric, have been coated with polymers such as polyvinyl chloride, polyurethanes, silicones, polytetrafluoroethylene, neoprene and synthetic rubbers, to produce coated fabrics. These have found wide application in the industrial and commercial, architectural and building industries and for sundry geotextile applications. The performance requirements of the textile fabric in the polymeric coated textile fabric include: high tensile strength, good flexibility, good weatherability, good chemical resistance, good flexibility in various climates, high tear strength and resistance to tear propagation, good dimensional stability to minimize stretch underload, good stability under various temperature and humidity conditions, good abrasion and good adhesion to the polymeric film coating. These performance requirements are applicable to coated fabrics used in large applications such as air and tension structures like air supported covers over athletic stadiums and airport facilities to smaller applications such as awnings and tarpaulins. For instance, in the air and/or tension structures, the air supported covers can be huge, ranging from 26,000 square meters for an athletic stadium to 425,000 square meters for an airport facility. Two desirable properties in this application and the other applications are good flame resistance and dimensional stability. These are two of the excellent properties of glass fibers but the lack of the requisite flexibility, abrasion resistance and adhesion to the polymeric film coating have limited the use of glass fibers in coated textile fabrics. It is an object of the present invention to provide coated bundles of fibers having a high modulus and low elongation with improved flexibility and abrasion resistance to result in improved woven and nonwoven fabrics, which can be manufactured into numerous woven and nonwoven fabrics taking advantage of the nonflammability and dimensional stability provided by the fibers, and where the fabrics prepared from the bundles need not be heat cleaned to remove various chemical sizing compositions applied to the fibers. SUMMARY OF THE INVENTION Accordingly, the aforementioned objects and other objects gleaned from the following disclosure are accomplished by the bundles of fibers impregnated with the moisture reduced, partially cured residue of an aqueous chemical treating composition. The fibers can be any fiber having modulus of elongation of at least(7 x 106 psi) 48 x 109 K pascals and an elongation at break of less than 5% and where the fibers are sensitive to interfilament abrasion. The bundles of fibers have a plurality of fibers, where each fiber has a first chemical treatment and the bundle of fibers has a second chemical treatment impregnating the bundle. The first chemical treatment is present on a substantial portion of the surfaces of the fibers as a moisture-reduced residue of an aqueous chemical treating composition. The aqueous chemical treating composition, referred to as a sizing composition, has at least a fiber protectorant such as a film forming polymer and/or lubricant, and, if the hydrophilic character of the fibers would limit compatibility with polymers, a hydrophilicity reducing agent such as a coupling agent can be present. The type of protectorant and the absence of interfering components enables the fibers in the form of a bundle to separate one from another when confronted with a disturbing force. The disturbing force can be mechanical contact, gaseous contact, hydrodynamic force or any other frictional contact to disturb the fibers one from the other to allow for fiber separation. The amount of the moisture reduced residue of the sizing composition that is present is in the range of about 0.05 to about 5 weight percent of the treated fiber. The one or more bundles of gathered sized fibers have the moisture-reduced, partially cured impregnating coating resulting from an aqueous impregnating composition having an elastomeric polyurethane that is curable to the extent of about 10 weight percent or less, and crosslinking material and water. Furthermore, the aqueous impregnating composition has an effective viscosity for impregnating the bundles of fibers and the amount of moisture-reduced impregnant on the bundles is greater than around 5 weight percent of the bundle and depends upon the filament diameter of the fibers in the bundle. The water in the impregnating coating composition is present in a predominant amount so that the total solids and viscosity of the impregnating coating composition are effective for impregnating the bundle of fibers. The impregnation is to such degree so that the moisture reduced, partially-cured residue of the aqueous impregnating composition is present as a coating on a substantial portion of a majority of the filaments in the bundle so that a majority of the filaments are separated to some extent from each other by the moisture reduced, partially cured coating. The crosslinkable material is present in the coating composition in an amount that is effective to engender a partial cure of the elastomeric, curable polyurethane polymer to assure that the polyurethane polymer is not redispersible in water. Optionally, included in the aqueous impregnating composition for the fibers are fiber lubricants, silane coupling agents, plasticizers, pigments, dyes, fire retardants and the like. The use of the lubricant is especially useful when the impregnated bundle of fibers is to be braided or woven, and not coated as a fabric with a polymeric coating. The fibers can be produced by methods well known to those skilled in the art. For example, glass fibers are produced from small orifices in a bushing of a glass batch melting furnace from any fiberizable glass composition, where the filaments are properly treated with an aqueous sizing composition. The aqueous sizing composition is applied to protect the filaments from interfilament abrasion and damage, and, if necessary, render the surface of the glass fibers less hydrophilic to be more compatible with hydrophobic coatings. A plurality of sized glass fibers are gathered into one or more bundles, strands, and collected into a package. One or more bundles of sized glass fibers are removed from one or more packages and treated with the aqueous impregnating composition in such a manner that the sized glass fibers within the bundle separate one from another to a degree to allow the impregnation of the bundle by the aqueous coating composition with the effective viscosity and total solids. The impregnated bundle of glass fibers is dried to partially cure the impregnant to produce impregnated bundles of glass fibers having sufficient flexibility for production of fabrics. The fabric subsequently can be coated to produce coated fabrics by processes such as impregnation or saturation and other surface coating processes like solvent-containing coatings, plastisols and lamination with preformed films or sheets of coating polymeric materials. When the aqueous impregnating composition has a lubricant to provide the bundles of glass fibers with an effective amount of lubricity, the impregnated bundles of glass fibers can be braided into various fabrics. BRIEF DESCRIPTION OF THE DRAWINGS Figure 1 depicts the coated fabric showing the laminated sheets or films used in conjunction with the fabric of impregnated bundles of fibers. Figure 2 is a photograph of a microscopic, enlarged cross-section of the impregnated bundle of treated glass fibers. DETAILED DESCRIPTION OF THE INVENTION When the high modulus, low elongation fibers are glass fibers, they can be produced from any fiberizable glass batch composition and prepared into glass fibers such as "E-glass fibers", "621-glass fibers", "A-glass fibers", "S-glass fibers", "C-glass fibers", and low fluorine and/or boron derivatives thereof. The glass fibers issue forth from orifices in a bushing of the glass batch melting furnace and, when they have cooled sufficiently, the aqueous sizing composition is applied to them. The glass fibers can be mechanically attenuated or prepared by any other method known to those skilled in the art. The aqueous sizing composition can be applied to the glass fibers by any method known to those skilled in the art such as belts, rollers, sprays, and the like. The aqueous sizing composition has present a hydrophilic reducing agent such as a coupling agent to make the fibers less hydrophilic and a protectorant, where the protectorant can be a glass fiber lubricant or a glass fiber film forming polymer. The film forming polymer forms a film upon the evaporation of a carrier, or upon drying or actually forms a liquid film. Also for glass fibers and other types of fibers, additional ingredients like friction-reducing agents and/or antistatic agents may be present. Any coupling agent, glass fiber lubricant or glass fiber film forming polymer known to those skilled in the art can be used. It is preferred that the sized glass fibers do not have present or are essentially free of a starch film forming material or any other material that would provide too much cohesion between the fibers. A nonexclusive example of a suitable nonstarch containing aqueous sizing composition for glass fibers is that disclosed in U.S. Patent 4,390,647 (Girgis), EMI7.1 The sized glass fibers are gathered into bundles or strands of glass fibbers, where the bundles can comprise from 200 to over 3,000 filaments. The bundles of fibers or strands are collected usually by winding onto a forming package or into a precision wound package of roving. The sized glass fibers usually have about 0.05 to about 5 weight percent of the sized glass fiber strands as the sizing composition, which has reduced moisture by the evaporation of water either by air drying or by drying at elevated temperatures. Although the sized glass fibers can also be in a wet condition when treated with the aqueous impregnating composition. In the aqueous sizing composition applied to the glass fibers, the coupling agents employed can be any coupling agent known to those skilled in the art such as silane coupling agents, a few examples of which are 4 aminopropyltrimethoxy silane, methacryloxypropyltrisilane, glycidoxypropyltrimethoxy silane, and the like, and metal halide complex coupling agents like methacrylato chromic chloride complex. Such agents are described in U.S. Patent 2,611,718. Other Werner type coupling agents having vinyl, alkyl, amino, epoxy, mercaptyl, thioalkyl, thioaryl, and phenyl groups are also suitable for incorporation into the size of the instant invention. Nonexclusive examples of the various silane coupling agents that can be used in the sizing composition of the instant invention include in general hydrolyzable vinyl, alkyl, beta- chloropropyl, phenyl, thio-alkyl, thio alkyl aryl, amino-alkyl, methacrylato, epoxy and mercapto silanes, their hydrolysis products, polymers of the hydrolysis products and mixtures of any of these may be employed. The usual amounts of coupling agents employed in sizing compositions for glass fibers can be used such as an amount of 0.1 to 2 percent by weight based on the aqueous sizing composition can be used. The fiber protectorants that can be used in the sizing composition of the present invention include any glass fiber lubricant including wet lubricants and nonionic lubricants or dry lubricants such as cat ionic lubricants like Cation-X, which is an alkyl imidazoline derivative produced as a reaction product of stearic acid, and tetraethylene pentamine stearic acid. Also acid solubilized water, soluble, dispersible stearic amides and anhydrides, acid solubilized water dispersible low molecule weight fatty acid amides, as well as anhydrous acid solubilized and polyunsaturated lower molecular weight fatty acid amides can also be used as the cationic lubricants. Typical hydrogenated vegetable oil lubricants can also be used such as hydrogenated cotton seed oil, hydrogenated corn oil, hydrogenated soy bean oil and the like. An example of the film forming polymeric materials that can be used include the polyoxyalkylene polyols or polyalkylene polyols; gelatin; glucose, cellulosic materials such as carboxymethyl cellulose, hydroxyethyl cellulose, methyl cellulose; oxyethylated stearates; and synthetic resins, such as ureaformaldehyde polymers, melamine-formaldehyde polymers, acetoneformaldehyde polymers, phenol-formaldehyde polymers; alkyd resins such as glyceryl-phthalic anhydride reaction products; polyamides, saturated and unsaturated polyesters, hydrocarbon-siloxane resins, epoxy resins; vinyl resins such as homopolymers and copolymers of ethylene, propylene, styrene, isobutylene, butadiene, acrylonitrile, vinyl chloride, vinyl pyrrolidone, vinylidene chloride, vinyl acetate, vinyl alcohol, acrylic acid and ester thereof, methacrylic acid and esters thereof, and the like. Mixtures of these film formers may also be employed. These film-formers are preferably used in the form of aqueous solutions, dispersions or emulsions. Also known silylated versions of the aforementioned film formers can also be used. The predominant constituent of the solids of the aqueous coating composition is the polyurethane polymer. By the use of the term polyurethane, it is meant to include reaction products of organic compounds having at least two active hydrogens and di and/or polyisocyanates, wherein the resulting polymer is an elastomeric curable polyurethane or polyurethane urea type polymer. By elastomeric, it is meant that the film of the polyurethane alone has a hardness of about 10 shore A to about 75 to 80 shore D with a preferred hardness of shore A 60 to 100 and elongation on the order of 100 to 800 percent. The Shore hardness test is conducted on a Shore durometer by standard procedures, and elongation is measured in accordance with ASTM testing procedure, D412. Preferably, the organic compounds with at least two active hydrogens is a polyol such as a polyester polyol or polyether polyol and most preferably, a polyol which is linear. Examples of polyester-based polyurethane elastomers include those where the polyester is prepared from carboxylic acid such as adipic and the glycol portion can be selected from such materials as ethylene glycol, 1,2-propylene glycol, 1,3-butylene glycol and 1,4-butylene glycol. Further examples of polyfunctional polyesters which can be used are those based on phthalic anhydride, adipic acid, ethylene glycol, trimethylol propane, and the like. A slight amount of branching of the polyol can be tolerated but the degree of functionality or branching of the polyol should be kept to a minimum since increased branching results in films that are tougher, harder and less flexible. The di or polyisocyanates generally used to form the polyurethane are selected from aromatic, aliphatic and mixtures thereof, isocyanates but the aliphatic isocyanates are preferred. Examples of the polyisocyanates that can be used include the aromatic isocyanate of toluene diisocyanate and the aliphatic isocyanates such as hexamethylene diisocyanate, methylcylcohexylene diisocyanate, dicyclohexyl methane diisocyanate, lysine diisocyanate where the aromatic group is methyl or ethyl, bis(2-isocyanato ethyl) fumaric, bis(2-isocyanato ethyl) carbonate and dimeryl diisocyanate, where the organic group is essentially a C36 hydrocarbon radical. Another isocyanate that may be used is 4,4'-diphenyl methane diisocyanate. The polyurethane polymer can be made as a curable material by any method known to those skilled in the art, for instance, additional monomers like diisocyanate, polyols or epoxies can be added to the polymer and/or a curable moiety can be introduced into the polymer. Nonexclusive examples of the aforementioned reactive groups or moieties used to make the curable polyurethane elastomer are hydroxyls, epoxies, ureas, amines, amides, and olefinic groups, or reactive methylene or olefinic groups. The polyurethane polymers can be produced by any one-shot or single step method known to those skilled in the art or by the two step chain extension process utilizing linear or lightly branched polyols with the necessary molar portions of a diisocyanate known to those skilled in the art to produce a water dispersible polyurethane. One or more or a mixture of these various elastomeric curable polyurethanes can be used in the aqueous coating composition of the present invention. Particularly, two or more of the polyurethanes can be blended to achieve a desired hardness and/or elongation property for the coating on the sized glass fibers. These elastomeric curable polyurethanes are water soluble, emulsifiable or dispersible through the use of dispersing agents and emulsifiers which can have a nonionic, cationic, and/or anionic and/or amphoteric or zwitterionic nature. In addition, the polyurethane polymers can be internally emulsified by incorporating one or more dispersing agents or emulsifiers with the other polyurethane producing monomers to produce the polyurethane polymer. The curable polyurethane has a maximum curability through crosslinking of a maximum of around 10 percent or less based on the solids of residue of the aqueous impregnating composition or on a dry basis. Nonexclusive examples of the polyurethane polymers that can be used as the film forming polymers in the impregnating coating include those that are internally emulsified, examples of which are shown in U.S. Patent Nos. 4,143,091; 4,208,494; and 4,208,495, all of which are hereby incorporated by reference. Other types of polyurethane polymers that can be used are those having ionic groups present on the polymer molecule such as those disclosed in U.S. Patent 4,066,591, which is hereby incorporated by reference. Other types of polyurethane ionomers, e.g. polyurethane polymers having ionic groups present on the polymer, that can be used in the composition of the present invention include polyurethane ionomers such as anionomers and cationomers. Nonexclusive examples of the ionomers include anionomers that are produced by reacting organic diisocyanates having molecular weights of from about 160 to about 300 with tri and/or tetra alkylene polyol such as ethylene glycol, and optionally other aliphatic glycols having molecular weights of from about 62 to about 200 in the presence of glycols containing carboxyl, carboxylate, sulfonic acid and/or sulfonate groups and having molecular weight of less than around 500. These polyurethane polymers containing the ionic groups or hydrophilic polyether segments are self-emulsifiable and do not need emulsifiers or high shear forces to be emulsified or dispersed, since they are self-dispersing. Also cationic polyurethanes that are formed by quaternizing polyaddition reactions can be used. Combinations of the ionic polyurethanes with polyesters, polyethers, polyacetals, polyisocyanates, low molecular weight glycols and diamines can also be used. The type and amount of the ionic groups present in the ionic polyurethanes are selected so that the polyurethane is not only self-dispersing but that the particle size of the polyurethane is less than around 5 microns. The properties of these polyurethane polymers can vary from hard film properties to flexible film properties. It is those polymers with the flexible film properties that are most useful in the present invention. Specific examples of commercially available polyurethane polymers that can be used include the aliphatic polyurethane dispersions such as Witcobond W-212 and W-234, available from Witco Chemical Corporation. The Witcobond W-212 material has a milky white appearance with a 30 percent solids level and a density oft,a3 lb/gal). The flash point is greater than 100"C., and the particle charge is cationic and the particle size is 1 m. The pH at 250C. (77OF.) is 4.5, and the viscosity at 250C. ( 77OF. ) in Brookfield LVF (cps) is 50, and the surface tension in dynes/cm is 41. Another polyurethane used in the present invention is the Witcobond W-234 polyurethane, available from Witco Chemical Corporation. The W-234 polyurethane is hazy in appearance and aliphatic in chemical type. The solids is 30 percent, and the density is 8.8 lb/gal. The flash point is similar to the W-2i2 material, and the particle charge is anionic, while the dispersion is colloidal. The pH at 250C. (770F.) is 8.0, and the viscosity at 250C. (770F.) as measured by Brookfield LVF in cps is 100, and the surface tension in dynes cm is 54. The preferred polyurethane is the Witcobond W-290H material, which is milky white in appearance, aliphatic in type with a 65 percent solids level and with a particle size of around L5 m and a pH at 250C (770F) of 7.5 and a viscosity as measured by Brookfield LVF in cps of 200 and a surface tension of 42 dynes/cm. The film properties of the 290H material are(4500 psi).31.06 x 106 K pascals tensile strength, 720 percent elongation and moduli of(250 psi);17.24 x 105 K pascals. at 100%, (540 psi) 37.23 x 105 K pascals at 300% and(1550 psi )10.69 x 106 K pascals at 500%. The crosslinking material is present to cure the curable polyurethane and may even crosslink with itself. Suitable crosslinking materials include: chemical compounds, monomeric compounds, oligomeric compounds, and polymeric materials. The polyermic crosslinking material can be an external and/or internal crosslinking or curing agent that are reactive for crosslinking at room temperature or, preferably, at elevated temperatures. Nonexclusive examples of suitable cross linking materials include chemical compounds like hexakis (methoxymethyl) melamine, lower hydrocarbon epoxides like those containing 2 to 12 carbon atoms including styrene oxide, alpha phenyl propylene oxide, trimethylene oxide, lower alkylene oxides like epoxides containing from 2 to 8 carbon atoms including ethylene oxide, propylene oxide, butylene oxide, isobutylene oxide and the like, and formaldehyde and alkoxysilanes and phenolics. Nonexclusive examples of monomeric crosslinking materials are those monomers which are reactive with polyurethane like diisocyanate and polyisocyanates and organic compounds with at least two active hydrogens. A few nonexclusive examples of oligomeric materials include: aldehyde condensates used in conjunction with acid or basic catalysts, such as melamine formaldehyde, hexakis (methoxymethyl) melamine, phenol formaldehyde and resorcinol formaldehyde including both methylol-containing condensates, monomers, dimers, trimers and higher oligomers. The phenol or resorcinol compounds include cresol and mixtures of its isomers, xylenol or mixtures of its isomers, a mixture of homologs of phenol and dihydric phenols such as phlorglucinol, cresorcinol, and meta-xylorcinol. The aldehyde includes any methylene donor that can be used for the formaldehyde, nonexclusive examples include: paraformaldehyde, hexamethylene-tetramine acid aldehyde and furfural and mixtures thereof. Nonexclusive polymeric materials include methylol-containing condensates of phenolic compounds, polyhydroxyphenolic compounds like resorcinol, urea, melamine, and the like, where the methylol results from any methylene donating compound like formaldehyde in its various forms like paraformaldehyde, hexamethylene-tetramine, acid aldehyde and furfual and mixtures thereof, and also includes aminoplast resins, organic polyisocyanates, and epoxy-containing polymers. Further examples of suitable external and internal crosslinking materials are given in U.S. Patent 4,066,591 (Scriven et al.), EMI13.1 EMI13.2 EMI13.3 It is preferred to have one or more melamine formaldehyde resins because of their ease in crosslinking and their compatibility with the polyurethane polymers. A particularly suitable melamine formaldehyde resin is the aqueous melamine formaldehyde resin available from Monsanto Company under the trade designation Resimene 841 which has less than 2 percent free formaldehyde and less than 5 percent methanol and has a boiling point of(2100) 99"C . The Resimene 841 also has a vapor pressure of 95 for methanol and 17.5 for water, a vapor density of 1.11 for methanol and .64 or water and has a colorless, clear mobile liquid appearance and has a specific gravity at(770Fj 250C of 1.25 and a percent volatile by volume percent of 29. Such a crosslinkable material as the melamine formaldehyde resin may require the use of a crosslinking controlling agent to control the degree of crosslinking between the crosslinkable polymeric material and possibly between the crosslinkable material and the polyurethane polymer. The crosslinking controlling agent can be one which modifies the pH of the coating composition such as ammonium hydroxide or an acid catalyst for the crosslinkable material. A nonexclusive example of the latter is a solution of toluene sulfonic acid in isopropanol such as that available under the trade designation Cycat 4040 with 40 percent acid and 60 percent alcohol available from American Cyanamide Co. Another particularly suitable material is that available from Witco Chemical Corporation under the trade designation Vitcobond XW aqueous epoxy emulsion. This epoxy emulsion has an epoxide equivalent weight of 345 to 385, a percent nonvolatiles of 54 to 56 percent, a viscosity in Brookfield at 250C. (77OF.) poise of 15 to 70 and an appearance which is a milky white liquid, and has a flashpoint of greater than(200 F) 930C , has(pounds per gallons at 250C. of 9.1) EMI14.1 The amount of the crosslinking material present in the aqueous coating composition is that amount to provide effective crosslinking with the polyurethane polymer to cure the curable polyurethane polymer so that the resultant film or residue has a hardness in the range of Shore values from A 10 to about D 80 and preferably from about A 60 to about A 100 and elongation of about 100 to about 800 percent and most preferably, a modulus at 500 percent elongation of about(500 %t 5 x 105 K pascals to about(4,000 psi) 27.6 x 106 K pascals . Most preferably, up to 6 weight percent of the polyurethane is crosslinkable, that is, curable, so that the amount of the crosslinking material is sufficient to crosslink the polyurethane polymer almost up to that degree of crosslinking. Most preferably, the amount of crosslinking material is less than that amount to effect the total possible crosslinking of the polyurethane polymer, and the amount is only that amount ot assure the degree of crosslinking of the polyurethane to prevent the redispersion of the polyurethane in water and save some crosslinkability of the polyurethane for adhesion to a matrix polymer. If a matrix polymer is not to be used with impregnated bundles of fibers, the amount of crosslinking material in the aqueous impregnant can be that amount to totally cure the polyurethane to the extent that the polyurethane can be cured. For self-crosslinkable crosslinking materials, the amount can exceed that for crosslinking the polyurethane, but the amount should not exceed that amount which causes the resultant film of the coating to have a hardness value and an elongation value in excess of the aforementioned values. Amounts greater than that for crosslinking the polyurethane will not increase any further the crosslink density, but it will provide a blend of properties. The water in the aqueous chemical treating composition constltutes a predominant amount of the composition including both volatile and nonvolatile portions. The amount of water results in a total solids concentration and viscosity for the composition that enables the composition to impregnate the bundle of filaments including bundles of strands and yarn. The degree of impregnation of the bundle of filaments is such that a majority of the filaments have a substantial portion of their surfaces covered with a near continuous film of the residue of the aqueous coating composition so that a majority of the filaments are separated from each other. It is not necessary that the bundle is encapsulated, although it may be as long as it is also impregnated. Preferably, when the polyurethane polymer is preemulsified or dispersed for addition to the aqueous coating composition to a solids content of around 50 percent or less, the viscosity of the aqueous coating composition is around 5 or less for a kiss roll type coating application and up to around 15 + 5 centipoise at room temperature for a die coating process. The total solids of the aqueous coating composition varies depending upon the diameter of the filaments in the bundle. The variation is that the finer diameter filaments require a higher total solids in the aqueous chemical treating composition, since the surface area of the finer diameter filaments is higher. In addition to the aqueous dispersible, emulsifiable or soluble polyurethane and cross linking material present in the aqueous coating composition along with water, there may also be present a number of optional components. The type of optional component present depends upon the final end use of the coated bundle of fibers. For instance, where the coated bundle is to be braided and woven for producing electrical harnesses to contain electrical wires, a lubricant should be present in the aqueous coating composition. Any glass fiber lubricant known to those skilled in the art can be incorporated into the aqueous coating composition. A particularly suitable lubricant is a silylated lubricant available from Union Carbide Corporation under the trade designation Y-9662. This material as described in the Product Safety Data Sheet is an organosilane ester with a boiling point of greater than 1500C at 760mm Hg and with a specific gravity of 1.05 at 25/250C, and with a vapor density of greater than one, and with a vapor pressure at 200C of less than litmi Hg and with less than 1 percent volatiles by volume, and with an evaporation rate of less than 1 with butyl acetate equal to one and with an appearance of a clear to slightly hazy colored liquid and with a characteristic odor. Another additional ingredient that can be present in the aqueous coating composition is a silane coupling agent and any of the aforelisted silane coupling agents used in the aqueous sizing composition can be used in the aqueous coating composition. Also, one or more aqueous dispersible, emulsifiable or soluble plasticizers can be included in the aqueous coating composition. The aqueous dispersible or emulsifiable plasticizers would be used with suitable nonionic, cationic, anionic, amphoteric or zwitterionic emulsifiers or dispersing agents having HLB values which are in the same range as the HLB value of the plasticizer. When one or more plasticizers are used in the aqueous coating composition, the type of polyurethane polymer that can be used can have higher hardness values since the plasticizers reduce the hardness value of the film of the coating composition on the bundle of filaments. Suitable examples of plasticizers that can be used include butyl benzyl phthalate available under the trade designation Sanitizer 160, wherein a suitable emulsifier is polyoxyethylene sorbitan monolaurate available from ICI America, Inc. under the trade designation Tween· 21 emulsifier. Another example of a suitable plasticizer is tri-çaLlyl phosphate available under the trade designation Phosflex 179: A available from Stauffer Chemical Company. This material is a liquid with a specific gravity at 20-OC./20-OC. of 1.143, a density of(pounds per gallon of 9.5) 1.02 kg/l , a boiling point in degrees C. at 10 millimeters of mercury of 265-2850C, a pour point of(00F) .-l7.80C , a viscosity at (100OF) 37.80C SUS of 220 and a flashpoint of(C1550F) 235 C Another suitable plasticizer is Benzoflex dibenzoate esters of dipropylene glycol or any of several polyethylene glycols available from Velsicol Chemical Corporation. Another optional component that may be present in the coating composition is a flame retardant, where any flame retardant that is water soluble, emulsifiable or dispersible can be used. A suitable flame retardant is antimony trioxide which can be emulsified with the Tween 21 emulsifier in water. Another suitable flame retardant, which may assist in curing the polyurethane is an aqueous dispersion of a brominated epoxy polymer. A suitable example is the brominated epoxy resin dispersion available from Celanese Corporation under the trade designation RDX-49630. This material is a 60 percent dispersion of a brominated epoxy resin in water, where the epoxy resin contains approximately 20 percent by weight bromine without any organic solvents being present. The viscosity of this material at 250C. is (10,000 centipoise) 10 pascal-seconds with a weight per gallon of 10.1 and a weight per epoxide of 450 and a pH of 7.2. When this epoxy resin is used in the aqueous coating composition, it can be cured with curing agents such as dicyandiamide, various substituted imidazoles and aliphatic means. A suitable curing agent is that available from Celanese Corporation under the trade designation Epicure 8525 polyamine curing agent. This latter material has a viscosity of(800 centipoise) 0.8 pascal-seconds at 75"C. and an equivalent weight on solids of 127 and(pounds per gallon of 8.1) o.97/ cm3. The aqueous coating composition can be prepared by adding all of the components sequentially or simultaneously to the desired volume of water with appropriate emulsifiers for any of the material to be emulsified or dispersed in water. Preferably, the materials that are not water soluble are preemulsified or dispersed with suitable solvents and emulsifiers with appropriate HLB values as known to those skilled in the art and then added to formulate the aqueous coating composition. Most preferably, the aqueous dispersion of the polyurethane polymer has added to it any aqueous dispersed plasticizers and aqueous dispersed waxes and lubricants, fire retardants and the like. The crosslinking material which is in a diluted aqueous medium is added to the polyurethane polymer dispersion or mixture of polyurethane and any plasticizers, lubricants and/or fire retardants. The aqueous coating can be further diluted with water to achieve a desired volume of material to give the aqueous coating composition the total solids and viscosity required for impregnating the bundles of filaments. The aqueous impregnating composition is applied to the bundles of filaments which includes strands, bundles of strands, yarns twisted and untwisted and merely bundles of monofilaments. The application can be by dip coating or die coating or any other process known to those skilled in the art for applying coatings to groups of filaments. For example, the bundle of filaments can be dipped into a bath containing the aqueous impregnating composition or the bundle can contact a kiss roll or other applicator device that carries it to contact the bundle of filaments. Also a die coating arrangement can be employed, where the bundle of filaments is pulled, pushed or stuffed through permament or adjustable orifices. This operates effectively to open the strand immediately in advance of the orifice to expose the innermost regions of the glass fiber bundle to the liquid impregnant located in the container with the orifices. Before the bundle contacts the impregnant, it can ride over a bar or similar device under tension to spread the fibers in the bundle for maximum separation and better impregnation. The sized filaments have the sizing composition which does not provide too much integrity between the filaments when they are gathered into groups or bundles of filaments so that upon the application of a disruptive force, before or during dip or die coating, the filaments separate somewhat one from the other to assist in allowing the coating composition to surround and enter the groups or bundles of filaments. Hence, the sizing assists in producing an impregnation preferably to a degree so that every filament in the bundle or in bundled strands has a substantial portion of its surface covered with the aqueous coating composition so that when the aqueous coating composition is dried and partially cured, the filaments in the bundles will be separated from each other. The bundles of filaments with the treatment of the aqueous coating composition are dried to partially cure and reduce the moisture content of the aqueous coating composition. Any method known to those skilled in the art for curing crosslinkable polymeric materials may be used to dry and cure the coated and impregnated bundle of filaments. It is preferred that the drying is a non-dielectric type drying and that the moisture is reduced to a moisture content in the range of less than around 1 to about 2 percent of the bundles. This and partial curing are accomplished by drying at suitable temperatures and times to result in the desired moisture reduction and partial cure. Preferably, the drying is conducted at a temperature in the range of about(400 F to about 500 F) 200-260 C for a time in the range of about 10 seconds to about 60 seconds or any equivalent temperature and time relationship to accomplish a similar degree of moisture reduction and partial cure. The partially cured coated bundle of filaments is flexible enough to undergo myriad fabric producing processes. Nonexclusive examples of fabric producing processes include weaving, nonwoven fabrics, knitted, braided, weft-knit fabrics such as those produced on the Mayer or Libya weft insertion fabric machine. On this type of machine, the fabric is a bi-directional crosslaid warp and weft structure, where the weft yarns do not interlace as in traditional woven fabrics. A "knit stitch" is run in the warp machine direction to lock the fabric together. For the weaving operation, plain weave, satin weave or any other type of weaving for producing a fabric as known to those skilled in the art can be used. The fabric whether woven or nonwoven or knitted or braided can be coated with numerous types of coatings by myriad processes or remain uncoated. Examples of suitable polymeric coatings include vinyl resins such as polyvinyl chloride, polyethylene and ethylene copolymers, polyurethanes, phenolic resins, melamine formaldehyde resins and elastomeric materials such as chlorosulfonated polyethylene, chlorinated polyethylene, and polymers of ethylene propylene diene monomers, and Hypalonk elastomers and silicone polymers. These types of polymers can be coated onto fabrics of the flexible bundle of filaments by impregnation or saturation processes and surface coating processes such as solvent-containing coatings and 100 percent solids coatings and lamination processes of preformed films or sheets. For example, when a plastisol, 100 percent solids coating, is used, an application of a first coating of poly(vinylchloride) latex is applied to the fabric to improve adhesion of subsequent plastisol coatings. After the application of the plastisol coating paste to the fabric, the fabric is heated to a temperature usually around (350 to 4000F) 177-2050C to permit the resin particles to form a continuous phase over the fabric and to actually contact in the interstices between the fabric. The polymeric coating then cools to a tough coherent film at room temperature. The fusion process is so quick that the coated fabrics may be cooled as soon as the required fusion temperature is obtained. In addition to the polymeric material, various pigments or fillers can be included and the polymeric materials may be modified by plasticizers and solvents. The polymeric coating and preferably the polyvinyl chloride coating also can be applied by any impregnation process known to those skilled in the art such as passing the fabric over a knife-over-roll coater. Also any wet coating process known to those skilled in the art can be used such as passing the fabric over sequential knife coaters or through a floating knife coater with a support channel. Also blanket knife coaters and inverted knife coaters and levelon coaters with reverse smoothing rolls can be used as can engraved-roll or rotogravure coating units. In applying the plastisols, any dry or 100 percent solids coating process known to those skilled in the art can be used. For instance, hot melt coating can be used or any modified wet coating process, where there is not any solvent evaporation. In addition, cast-coating techniques can be used as well as metal-belt precast coaters. Also a dry powder resin coating method such as hot calendar-coating and extrusion-coating can be used. Also wet lamination and dry lamination involving the union of the fabric with a film or sheet of the polymer, which has been formed in a separate operation, can be used. In the lamination processes, the film or sheet can be formed by calendaring, by extrusion, or by casting in a separate operation and laminated to the fabric base. With these processes an adhesive coating can be applied to the plastic sheet prior to the application of pressure against the fabric and plastic sheet or the plastic sheet can act as the thermoplastic adhesive itself and it can be heated to produce the adhesion and, afterwards, brought into contact with the fabric while hot. The use of the adhesive application is performed in the multiple-ply drum lamination process. Also with foamable polymeric materials, the thermoplastic foam lamination process can be used. In addition to the woven or knitted fabrics or nonwoven scrim end use applications, numerous specialty products can be produced from the impregnated bundles of fibers of the present invention. Such specialty products includes ropes and cordage, dryer felts, conveyor belts, reinforcement mesh for concrete and gypsum, webbing and strapping, slings, electrical sleeving and harnesses and reinforced tapes, cables for aerial dropwires, mattress ticking and fiber optic cables. In most of these specialty products area, the aqueous coating composition would have a lubricant present and preferably a silylated lubricant for facile braiding and weaving of the resultant coated bundle of glass fibers. Also the impregnated bundles of filaments are readily receptive to both aqueous and nonaqueous dying processes. Figure 1 depicts a coated fabric of the present invention, where numeral 12 shows the fabric comprised of the flexible impregnated bundle of glass fibers of the present invention and numerals 11 and 13 indicate the polyvinyl chloride sheets or films that are laminated together sandwiching the fabric in between the laminate sheets. Ordinarily, the thickness of the coated fabric ranges from even less than 0.01 to greater than 0.06 inch (0.025 cm 0.15 cm), and the amount of coating on a unit area of the fabric varies widely, but it is usually around(5 to about 50 ounce/yd 119-1700 gm/m2 Figure 2 is a photograph depicting a cross-sectional view of the coated bundle of glass fibers of the present invention. The cross-section is magnified 600 times on a conventional microscope. The specimen was prepared by making a .01 mil cross-sectional cut with a microtone cutter of the pigmented impregnated bundle of glass filaments of the present invention. The specimen was embedded in expoxy resin. Numeral 14 shows the glass filaments with the residue of the sizing composition and numeral 15 depicts the partially cured, moisture reduced coating impregnating the bundle of sized glass fibers. As noted from Figure 2, the majority of glass filaments are not actually touching each other with a glass surface to a glass surface, but are separated from one another by the partially cured, moisture reduced coating. PREFERRED EMBODIMENT OF THE INVENTION In the preferred embodiment of the present invention, the filaments of glass fibers are usually of the "E-glass" or "621-glass" variety. The glass fibers are formed by attenuation from molten streams of glass issuing forth from orifices in a bushing of a glass batch melting furnace. After the filaments have cooled below the boiling point of water, an aqueous sizing composition is applied to the fibers. The aqueous sizing composition is a nonstarch textile size having a 50/50 blend of polyalkylene polyol available under the trade designation PluracolE V-7 polyol and polyoxyalkylene polyol available under the trade designation Pluracol V-10 polyol from BASF Wyandotte. The amount of the blend is in the range of about 0.5 to about 5 weight percent of the aqueous treating composition and most preferably, about 1 to about 3 weight percent. A silane coupling agent is preferably a lubricant modified amino silane coupling agent available under the trade designation Y-9072 silane from Union Carbide Corporation. This material is present in an amount in the range of about 0.01 to about 2 weight percent of the aqueous treating composition. The preferred cationic lubricant that is present in the aqueous sie is a polyamine lubricant commercially available as an acidified cat ionic fatty acid amide under the trade designation Emery 6760-U. This material is present in the aqueous treating composition in an amount of about 0.1 to about 4 weight percent of the aqueous treating composition. Total solids of the aqueous treating composition can be a convenient solids range for sizing compositions to be applied at a proper and desired LOI to glass fibers. Preferably the total solids is in the range of around 3 to around 20 weight percent. It is preferred to apply the aqueous treating composition to the glass fibers in such a manner to give an LOI for the glass fibers in the range of about 0.1 to about 1 percent and most preferably about 0.5 to about 0.8 percent. The exact components of the aqueous impregnating composition to be applied to the glass fibers treated with the aqueous nonstarch sizing composition depends upon the end use of the coated glass fibers, but the impregnating composition preferably is a one phase polymeric system. When the coated glass fibers are used in cable applications like support cables for fiber optics, the aqueous coating composition has the following formulation: : Aqueous dispersion of 1207 grams polyurethane polymer (Witco 290-H) Water 1034 grams Butyl benzyl phthalate 138 grams (Sanitizer 160) Polyoxyethylene sorbitan 17 grams monolaurate (ICI) (Tween 21 from ICI America, Inc.) Hot Water 347 grams Water 2586 grams Aqueous dispersion 172 grams of polyurethane polymer (Mobay XW 110) Aqueous epoxy dispersion 94 grams (Witco XW) The aqueous coating composition was prepared by combining deionized water and the polyurethane dispersion to a premix tank and stirring for 10 minutes. All of the valves of a main mix tank were closed and an agitator was started and the diluted aqueous dispersion of polyurethane was introduced into the main mix tank. The plasticizer was emulsified in a premix tank with an Eppenbach mixer by adding the plasticizer and the emulsifier and starting the Eppenbach and adding hot deionized water at a rate of 1 to 2 grams per minute until the emulsion was inverted. When inversion was complete, the water addition rate was increased until all of the specified water is added. The emulsified plasticizer is then added to the main mix tank. Deionized water was added to a premix tank and the aqueous polyurethane dispersion available as XW 110 emulsion from Mobay Chemical Company was added. This material is a hazy off-white anionic dispersion of an aliphatic polyester urethane polymer in water with 15% by weight N-methyl-2-pyrrolidone and it is fully reacted with no free isocyanate. The dispersion is 35 percent by weight solids with a specific gravity at 250C of 1.04 and a pli of 8.3. Typically film properties include tensile srength of (6,600 psi) 41.37 x 106 K pascals elongation at break 170X, yield modulus(5700 psi) 39.3 x 106 K pascals , modulus at 100%, elongation of 520%. Also the aqueous epoxy dispersion was added and the mixture was stirred for around 10 minutes. This diluted mixture of aqueous polyurethane and epoxy dispersions was added to the main mix tank. The formulation was diluted to a final volume and stirred for around 25 minutes. The aqueous coating composition was applied in a kiss roll coating operation with an applicator roll speed, and line speed of the bundle of filaments adjusted to give about 10 to about 12 percent by weight pick tlp of the impregnant. The bundles of filaments are K-15 1/0 bundles. In alternative embodiments, the K-15 3/0 strand construction need not be the only strand construction used for the coated bundle of glass fibers. For instance, K-15 1/0, 2/0, 3/0, 4/0 and K-37 and H-25 1/0 and G-37 1/0 and G-75 1/0 and G-150 1/0 and D-225 1/0 and D-450 1/0 and M-450 are just a few examples of other types of strand constructions that can be used. When the partially cured moisture reduced coated bundle of glass fibers are to be used for braiding and weaving into a fabric for electrical harness or sleeve applications, the aqueous coating composition preferably has the following formulation: Aqueous dispersion of polyurethane 7000 grams (Witco 290-H) Silylated lubricant (Y-9662) 100 grams Cold water 5000 grams Trixylyl phosphate (Phosflex 700 grams 179A) Butyl benzyl phthalate 600 grams plasticizer (Sanitizer 160) Polyoxyethylene sorbitan mono- 100 grams laurate (Tween 21) Water (warm, distilled) 500 grams Melamine formaldehyde resin 400 grams (Resimene 841) Water (distilled) 600 grams Solution of toluene sulfonic 10 grams acid an isopropanol 40% acid and 60% alcohol (Cycat 4040) Aqueous dispersion of 840 grams brominated epoxy polymer (RDX 6315) Water 800 grams Polyamine epoxy curing agent 30 grams (Epicure 8525) Antimony trioxide flame 200 grams retardant Water 800 grams In a main mix tank the aqueous polyurethane dispersion was added along with the silylated lubricant and cold distilled water with agitation. In a premix tank, the mixture of plasticizers was emulsified with warm distilled water and this mixture was added to the main mix tank. In a premix tank, the melamine formaldehyde was combined with the acid catalyst and water and this mixture was added to the main mix tank. In another premix tank, the aqueous dispersion of brominated epoxy polymer was combined with the polyamine curing agent and water and this mixture was added to the main mix tank. The flame retardant was combined with water in a premix tank and added to the main mix tank. The total solids of the formulation was 18 percent and the total volume was 9 gallons. This aqueous coating formulation was applied to the aforementioned sized glass fibers in a similar manner as that of the aqueous coating formulation of the preferred embodiment. The following examples further illustrate the embodiments of the present invention and should not be construed as limiting the present invention which is properly delineated in the claims. Table 1 presents 9 examples of an aqueous coating formulations in accordance with the present invention. These aqueous coating formulations, all of which had viscosities in the range of 4-5 centipoise, were applied to sized glass fibers having the sizing composition of the preferred embodiment in the same manner as for the preferred embodiment. The formulations of Example 1 is the preferred formulation for impregnated yarns that are prepared into fabric and coated with polymeric material to produce a coated fabric. This formulation was prepared by adding the deionized water for the polyurethane dispersion to a premix tank and adding the polyurethane dispersion. This combination was stirred for 10 minutes and transferred to a main mix tank. The plasticizer was emulsified in the same manner as described for the formulation shown on page 25. The melamine formaldehyde and water and acid catalyst were added in a similar manner as described or the formulation of pages 26 and 27. As the last ingredient, the silylated lubricant was mixed with deionized water in a premix tank and added to the main mix tank. Table 2 presents performance data for both impregnated and unimpregnated and uncoated bundles of glass filaments. The filaments for both varieties of bundles were sized with the aqueous sizing composition of the preferred embodiment. The unimpregnated and uncoated bundles were not treated with the aqueous impregnating coating used in the present invention. The impregnated bundles of sized glass fibers were impregnated with the polyurethane impregnants of Examples 1 and 6-9 in Table 1. The performance data of Table 2 are for the impregnated bundles of glass fibers under the first section and for fabric properties of fabrics woven with the impregnated bundles of fibers under the second section. The tests conducted in Table 2 were all conducted in accordance with standard test procedure for these tests as follows: Test Procedure Impregnated bundle strength American Society of Testing including: tensile, Young's Materials (ASTM) test D-2970 modulus, and failure elongation Flex life ASTM-D-2176 with (0.5 lb) 226.8 gm. load Fabric breaking strength ASTM-D-1682 Fabric torque tear test ASTM-D-2262 Fabric MIT Flex life ASTM-D-2176 with(0.5 lb) 226.8 gm, load per end Stoll flex test ASTM-D-1175 with 15 ends per specimen The crease tensile test involves folding a fabric of the impregnated and unimpregnated and uncoated bundle of filaments on itself perpendicular to the warp direction and placing a(10 lb) 4.54 Kg weight on the crease for 18 hours. The tensile strength of the creased fabric is tested according to ASTM-D-1682. Table 2 shows the improvement of the impregnated bundle of filaments in strength, flexibility, and abrasion resistance for application in numerous end uses. The abrasion resistance is shown in the crease tensile test where under the severe biding conditions of this test, the fabric of impregnated yarn retained around 60 percent of its original tensile strength. Also the impregnated bundle of filaments showed good receptivity to dyes. A 10 x 10 plain weave fabric of the impregnated bundles of Example 1 was immersed in an aqueous dye bath containing 3.3 gm/liter of dye. The fabric was stirred in the bath for around 2 minutes and removed and rinsed in both running hot water and running cold water. The fabric was scoured in a water bath containing Triton-X-100 octylphenoxypolyethoxyethanol. Subsequently, the fabric was rinsed in both running hot water and running cold water. This procedure was performed twice on separate similar fabric samples. One procedure was conducted with the basic dyestuff, Kemacryl Red FGL from American Hoechst Corporation. The second procedure was conducted with the acid dyestuff, Lonateryl Bleu B, also from American Hoechst Corporation. Both procedures produced well dyed fabrics. The present invention enables the production of bundles of filaments like glass fibers, where the advantageous properties are maintained, where such properties include: high tensile strength, high tear strength, resistance, dimensional stability like high modulus to minimize stretch under load and yarn stability unaffected by temperature and humidity changes, resistance to chemical attack, resistance to UV degradation and flammability resistance. In addition, improvements are obtained in the properties of flexural strength and abrasion resistance. TABLE 1 Impregnant Coating Formulations Examples 1 2 3 4 Kg/Wt% Sol/Wr% Ag Kg/Wt% Sol/Wr% Ag Kg/Wt% Sol/Wr% Ag Kg/Wt% Sol/Wr% Ag Polyurethane dispersion Witco 29OH (65% solids) 329.4/69.4/14 1207/71.3/15.9 7000/157.2/13.3 1207/79/15.9 Water (deionized) 454.2D 1034 5000 1034 Butyl benzyl phthalate plasticizer (Sanitizer 160) 37.65/12.2/2.5 138/12.5/2.8 800/10/22.3 - Trixylyl phosphate (Phosflex 179A) -- -- 700/8.8/2 - Polyoxyethylene sorbitant monolaurate (Tween 21) 4.7/1.5/.3 17/1.5/.3 50/.6/.1 - Water (warm) 106L 345 1000 - Melamine formaldehyde resin Resimene 841 47.1/15.3/3.1 -- 1000/12.6/2.9 172/17.3/3.5 " " " Resimene 970 -- -- 500/6.3/1.5 - Water 151L -- 2000 517 Acid catalyst (Cycat 4040) .094/.03/.003 -- 30/.2/.3 0.3/.03/ Solution of toluene sulfonic acid in isopropanol (40% acid/607OH) Acetic acid -- -- -- 5.5ml Organosilane ester lubricant Y-9662 4.7/1.5/.3 -- 100/1.3/.3 - Gamme-methacryloxypropyltrimethoxy silane (A-174) -- -- -- 55/3.9/.78 Polyurethane resin dispersion (Mobay XW-100) 33% -- 345/10.3/2.3 -- - Epoxy resin aqueou@ dispersion (Witcobond XW) 50% -- 94/4.3/1 200/1.3/.3 - Antimony trioxide fire retardant -- -- 100/1.3/.3 - Water -- -- 1000 - Polyoxyethylene sorbitan monolaurate (Tween 21) -- -- 50/.63/.1 - Water to desired volume of 1514.161. (400 ml) 492 ml 34.1L 492L Solids % 19#0.5 20#2 23.3 20 pH 8.5 -- -- -- TABLE I (Cont't) Impregnated Conting Formulations Examples 5 6 7 8 9 Kg/Wt% Sol/Wr% Ag Kg/Wt% Sol/Wr% Ag Kg/Wt% Sol/Wr% Ag Kg/Wt% Sol/Wr% Ag Kg/Wt% Sol/Wr% Ag Polyurethane dispersion 1207/82/15.9 1207/80/13 1207/77.3/13 1207/69.8/13 1207/80/13 Witco 29OH (65% solids) Water (deionized) 1034 1034 1034 1034 1034 Butyl benzyl phthalate -- 138/14/2.3 138/13.6/2.3 275/24.5/4.51 138/14/2.3 plasticizer (Sanitizer 160) Trixylyl phosphate (Phosflex 179A) -- -- -- -- - Polyoxyethylene sorbitan -- 17/1.7/.3 17/1.7/.3 17/8.5/.3 17/1.7/.3 monolaurate (Tween 21) Water (warm) -- 345 345 345 345 melamine formaldehyde resin 172/18/3.5 -- -- -- 43/4.4/.7 Resimene 841 " " " -- -- -- -- - Resimene 970 Water 517 517 517 517 517 Acid catalyst (Cycat 4040) 0.3/.03 -- -- -- - Solution of toluene sulfonic acid in isopropanol (40% acid/607OH) Acetic acid -- -- -- -- - Organosilane ester lubricant -- -- -- -- - Y-8662 Gamma-methacryloxypropyl- -- -- -- -- -trimethoxy silane (A-174) Polyurethane resin dispersion -- -- 86/2.8/.5 -- - (Mobay XW-100) 33% Epoxy resin aqueous dispersion -- 94/4.6/.8 94/4.6/.8 94/4.2/.8 - (Witcobond XW) 50% Antimony trioxide fire retardant -- -- -- -- - Water 4921D 6057D 6057D 6057D 6057D Polyoxyethylene sorbitan monolaurate (Tween 21) Water to desired volume of Solids% -- 16 16 18.5 16.2 pH -- -- -- -- - TABLE 2 PERFORMANCE OF IMPREGNATED BUNDLES OF GLASS FILAMENTS Physical Properties of Bundles Tensile Strength Young's Failure Flex Life Samples psi/denier Modulus Elongation (Z) (cycles) Sized uncoated, 1.6 x 105/6.0 7.8 x 106 3.5 100 unimpre@nated bundles K-15 1/0 Impregnated K-15 3.1 x 105/9.8 7.8 x 106 4.5 2200 1/0 Es. 1 Table I Impregnated K-15 -- -- -- 2920 LID Es. 6 Table 1 Impregnated K-15 -- -- -- 1355 I/D Es. 7 Table 1 Impregnated K-15 -- -- -- 2609 1/0 Es. 8 Table I Impregnated K-15 -- -- -- 2010 1/0 Ex. 9 Table 1 Phvsical Properties of Fabric Made from Bundles of 10x10 Plain Weave Tongue Stoll MIT Crease Breaking Tear Flex- Flex Tensile Wt. 2 Strength 1b/3"wide Abrasion Life Strength Denier Oz/vd lb/15 ends Sample (cycles) (cycles) lb/15ends Sized uncoated, 3000 7.8 532 8 316 430 unimpregnated bundles i-15 1/0 Impregnated K-15 3250 8.5 716 36 2000 4200 566 1/0 Es. 1 Table 1

Claims: WE CLAIM: I. A flexible bundle of sized high modulus, low elongation fibers, where the bundle has an elastomeric coating and impregnant, characterized in that: a) the sizing on the fibers in the bundle is a moisture reduced residue of an aqueous chemical sizing composition having at least a fiber protectorant, b) the elastomeric coating and impregnant is a moisture-reduced, and at least partially cured residue impregnating the bundle of the plurality of fibers where the residue resulted from the aqueous impregnating composition having: : 1) one or more elastomeric, curable polyurethanes that are water soluble, emulsifiable or dispersible, 2) one or more crosslinking materials that are water soluble, emulsifiable or dispersible in an effective amount to at least partially cure the polyurethane, 3) water in an effective amount to provide an impregnating coating composition for the bundles of glass fibers. 2. Flexible bundle of filaments according to Claim 1, characterized in that the aqueous chemical sizing composition there is present an antistatic agent. 3. Flexible bundles according to Claims 1 or 2, characterized in that the one or more elastomeric polyurethanes is a blend of at least two aqueous soluble, emulsifiable or dispersible polyurethanes having film properties with different modulus of elongation at the same percentage of elongation. 4. Flexible bundles according to Claims 1-3, characterized in that the aqueous impregnating composition includes one or more water soluble, emulsifiable or dispersible plasticizers. 5. Flexible bundles according to Claims 1-4, characterized in that tlie aqueous impregnating composition includes one or more silane coupling agents. 6. Flexible bundle according to Claims 1-5, characterized in that the polyurethane is curable to an extent of 10 weight percent or less on a dry solids basis. 7. Flexible bundle according to Claims 1-5, characterized in that the moisture reduced, partially cured residue of the impregnating composition also encapsulates the bundle of fibers. 8. Flexible bundle according to Claims 1-7, characterized in that the aqueous impregnating composition has as the crosslinking material an aqueous soluble, dispersible epoxy resin in an effective amount for partial curing of the curable polyurethane resin. 9. Flexible bundle according to Claims 1-8, characterized in that the aqueous coating composition has a an aqueous soluble, dispersible or emulsifiable brominated epoxy resin. 10. Flexible bundles according to Claims 1-9 characterized in that the residue has a hardness in the range of Shore A 10 to about Shore I) 90 and an elongation of about 500 to about 4,000 psi. 11. Flexible bundle of fibers according to Claims 1-10, characterized in that the fibers are glass fibers and the aqueous chemical sizing composition has present one or more coupling agents. 12. Flexible bundle of fibers according to Claims 1-11 the glass fibers are sized with an aqueous sizing composition which is a non-starch-containing composition having about 0.5 to about 5 weight percent of one or more water dispersible, high molecular weight polyols selected from the group consisting of polyoxyalkylene polyols and polyalkylene polyols having an average molecular weight of about 300 to about 12,000 and mixtures thereof present as flexible film formers, and 0.1 to about 2 weight percent of one or more silane coupling agent, and about t).1 to about 4 weight percent of a cationic lubricant, and water in an amount to give a total solids content for the aqueous composition in the range of about 3 to about 20 weight percent. 13. Flexible bundle of glass fibers according to Claims 1-12 characterized in that the aqueous impregnating composition there is present a glass fiber lubricant. 14. Flexible bundle of glass fibers according to Claims 1-13, characterized in that the lubricant is a silylated lubricant. 15. Flexible bundles according to Claims 1-14 characterized in that the crosslinking material is selected from monomeric or polymeric aldehyde condensate compounds including melamine formaldehyde resin along with an acidic or basic catalyst in an effective amount for partial curing of the curable polyurethane resin. 16. Flexible bundle according to Claims 1-15 characterized in that the aqueous impregnating composition has a water soluble, emulsifiable or dispersible fire retardant. 17. A flexible bundle of sized glass fibers, where the bundle has an elastomeric coating and impregnant, characterized in that: a) the sizing on the glass fibers constituting a bundle, is a moisture reduced residue of an aqueous non-starch-containing sizing composition having a 50/50 blend of a polyalkylene polyol and a polyoxyalkylene polyol, wherein the polyols have an average molecular weight from about 300 to about 12,000 and wherein the blend is present in an amount of about 0.5 to about 5 weight percent of the aqueous sizing composition, silane cotlpl-ing agent in an amount of about 0.1 to about 2 weight percent of the aqueous sizing composition, a cat ionic acidified fatty acid amide polyamine lubricant in an amount of about 0.01 to about 4 weight percent of the aqueous sizing composition, where the total solids of the aqueous sizing composition is in the range of about 3 to about 20 weight percent and the amount of the moisture reduced residue on the glass fibers is in the range of about 0.1 to about 2 percent based on the weight of the sized glass fibers, b) a moisture reduced, partially cured residue impregnating bundle of the plurality of fibers, where the aqueous coating composition has one or more elastomeric polyurethane polymers that are water soluble, emulsifiable or dispersible, and curable to an extent of 10 weight percent or less on a dry solids basis, C) one or more crosslinking materials selected from the group consisting of melamine formaldehyde resin, urea formaldehyde resin, phenol formaldehyde resin, resorcinol formaldehyde resin, along with an acid or basic catalyst in an effective amount to partially cure the curable polyurethane polymer to retard the redispersibility of the polyurethane polymer in water, ) one or more water soluble, dispersible or emulsifiable plasticizers, e) one or more silylated lubricants, f) water in an effective amount to provide an impregnant to impregnate the bundle having a viscosity in the range of up to around 20 centipoise and a total solids in the range of around 1 to around 25. 18. Flexible bundle according to Claims 1-17 characterized in that the elastomeric, curable polyurethane is fully reacted without any free isocyanate group. 19. The use of the flexible bundle according to Claims 1-18, to produce polymeric coated woven and non-woven fabric materials and to produce polymeric coated cables.

Inventors: GIRGIS, MIKHAIL MILAD, LAWTON, ERNEST LINDWOOD
Applicants: PPG INDUSTRIES, INC.
Application year: 1985
Main classification: D06M15
IPC codes: C03C25, B32B27