METHOD OF LASER-WELDING SHEET METAL PROTECTED BY LOW-TEMPERATURE VAPORIZING MATERIALS

Abstract: Method of laser welding sheet metal protected using low- vaporizing-temperature materials, whereby, before being subjected to a laser welding beam along a weld area (11), two metal sheets (1, 2) are placed on top of each other in such a manner that at least one layer (4) of the said protecting material is located between the sheets (1, 2) at the weld area (11) and communicates externally in es­ sentially direct manner.

Description: The present invention relates to a method of laser weld­ ing sheet metal, in particular, sheet steel to which the ensuing description applies solely by way of a non-limit­ ing example, protected using low-vaporizing-temperature materials. As of the present, laser beam machines are known to be employed, not only for cutting flat or otherwise drawn sheet metal along given cutting lines, but also for spot or seam welding sheets together. According to general practice, two steel sheets for la­ ser welding are held together contacting each other as tightly as possible along the entire weld area by means of grips, so as to ensure, among other things, perfect thermal conduction between the sheets. The latter are then subjected to a laser beam which welds the sheets together by smelting the metal in the weld area swept by the said beam. Whereas the aforementioned method has proved particu­ larly effective for welding bare sheet steel, i.e. hav­ ing no covering material protecting it against external agents, it proves inadequate when welding together metal sheets protected against external agents using low-vapor­ izing-temperature materials. At which point, it should be specified that the term "low-vaporizing-temperature material" is intended to mean material, such as zinc, having a melting and vapor­ izing temperature considerably below that of iron. If two metal sheets protected using similar material are welded together using the same technique employed for welding bare sheet, the resulting welds invariably prove uneven and riddled with craters, faults which, regardless of whether or not the weld is endangered, involve high- cost follow-up machining for their removal, particularly when, as often occurs in the car industry where the use of zinc-plated sheet is practically universal, the said welds extend over visible parts. To avoid the above drawback, and owing to the above craters and faults being created by the protective material between the metal sheets boiling, in gaseous form, through the molten metal of the sheets, two ways are followed. As far as a first of the above ways is concerned, a method is known from US-A-3,881,084, according to which the formation of the above gases is prevented by coating the protective material, at the welding zone, by means of a substance forming, with the protective material, a compound having a vapor pressure substantially the same or less than that of the metal in the metal sheets to be welded together. As far as the second of the above ways is concerned a method is known from EP-A1-0 157 913 (Article 54.3 of EPC), according to which the protected metal sheets are kept at a distance to each other during welding by means of a removable spacer, to provide therebetween a gap through which the gases produced by the vaporized protective material may escape. The present invention follows the way taught by EP-A1-0 157 913, and provides an industrial method for welding protected metal sheets together particularly adapted to be be used by car manufacturers. According to the present invention there is provided a method for laser welding sheet metal protected by a protective layer of a low-vaporizing-temperature material, whereby at least two metal sheets, at least one of which is protected, are kept in an overlapping relationship in a weld area by means of gripping means which clamp the sheets together, and are arranged adjacent to the welding area, at least one layer of the protecting material being located between the metal sheets in the welding area, and the welding area communicating externally through at least one passage, wherein said sheets are kept in direct contact with each other where said gripping means are located, and said passage is determined by the particular shapes of said sheets. The invention will now be described, by way of examples, with reference to the accompanying drawing, in which: - Fig. 1 shows a first technique for welding protected sheet metal according to the present invention; - Fig. 2 shows a variation of the Fig. 1 technique; and - Fig. 3 and 4 show two variations of a further welding technique according to the present invention. In all the attached drawings, numbers 1 and 2 indicate two metal sheets, the first arranged on top of the sec­ ond and each comprising a layer of metal 3 and a protec­ tive layer 4 of low-vaporizing-temperature material, such as zinc. Though, in the attached drawings, sheets 1 and 2 are shown as being separate, needless to say, they may also consist of a single sheet bent to form a U. Furthermore, whereas, in the attached drawings, sheets 1 and 2 are each provided with a single protective layer 4, clearly, the ensuing description would in no way be affected if, as is usually the case in actual practice, sheets 1 and 2 were each provided with two opposed protective layers 4. Finally, whereas, in all the attached drawings, a single protective layer 4, i.e. that of sheet 2, is lo­ cated between sheets 1 and 2, the ensuing description would obviously in no way be affected if the protective layers 4 of both sheets 1 and 2 were located facing each other between the said metal sheets. In all the attached drawings, number 5 indicates an out­ put head on a laser welding machine and numbers 6 and 7 the jaws of a grip 8 for clamping together sheets 1 and 2. As shown in the Fig. 1 example, sheet 1 comprises a cur­ ved section 9 blending with a flat section 10 to be weld­ ed to the upper surface of sheet 2 protected by layer 4. For welding the sheets on the said welding machine, the flat section 10 of sheet 1 is arranged contacting sheet 2 and clamped to the latter by means of a single grip 8 located a given distance from the curved section 9. Sub­ sequently, the head 5 on the welding machine is arranged facing the free surface of sheet 1 in the space between grip 8 and curved section 9, so as to weld area 11 on flat section 10 as close as possible to the end of the latter blending with curved section 9. In like manner, a side edge of weld area 11 communicates essentially ex­ ternally through space 12 between protective layer 4 on sheet 2 and curved section 9 on sheet 1. When the welding machine is started up, the heat releas­ ed by the laser beam emitted by head 5 smelts almost in­ stantly the metal on sheets 1 and 2 located essentially in area 11, while at the same time vaporizing the mate­ rial constituting the portion of layer 4 on sheet 2 lo­ cated in and around area 11. Despite the low resistance of the molten metal on sheets 1 and 2 to the gas produced by the material of layer 4 vaporizing, the said gas is blown straight out through the lesser-resisting passage consisting of space 12. The main outcome of this is that the resulting weld is essentially free of imperfections, especially the craters that would have been formed in area 11 and on the outer surface of sheets 1 and 2, had the gas, produced by pro­ tective layer 4 vaporizing, blown through the molten me­ tal on the said sheets. In the Fig. 2 example, one end of a flat sheet 1 is welded on to sheet 2. Before welding, the free edge of sheet 1 close to weld area 11 is bent slightly so as to form a lip 13 bending away from sheet 2 so as to define with it a space 12 enabling the gas produced by the vaporization of layer 4 to escape. In this case, grip 8 is arranged on the opposite side of weld area 11 in relation to lip 13 so as to essentially reproduce the same situation des­ cribed with reference to Fig. 1. In both Fig. 1 and 2 examples, clamping of sheets 1 and 2 is unilateral, i.e. on one side of weld area 11, whereas, in the Fig. 3 example, clamping may be one- or two-sided as required. Fig. 3 shows the laser welding of two flat sheets 1 and 2 which may be clamped by a single grip 8 (shown by a con­ tinuous line in Fig. 3) on one side of a weld area 11, or by the said grip 8 and a second grip 8 (shown by the dot­ ted line) on the opposite side to the first grip 8 in re­ lation to weld area 11. In the case of the Fig. 3 example, the employment of a second grip 8 is made possible by a channel 14 located between sheets 1 and 2, communicating externally and ex­ tending over the entire weld area 11. Channel 14, which is obviously relatively shallow (about 0.1 mm for steel sheets 1 and 2), is nevertheless sufficient to allow the gas produced by the vaporization of layer 4 to be blown out and is formed by bending sheet 1 (or 2 or both). Fig. 4 shows an arrangement essentially similar to that of Fig. 3, whereby the said channel for exhausting the gas produced by the vaporization of layer 4 is broken up into a number of separate channels forming a knurled sec­ tion 15 on the inner surface of sheet 1 (or 2 or both). Obviously, the examples described with reference to the attached drawings are only a few of the techniques avail­ able for welding together, on a laser welding machine, two, three or even more metal sheets protected using low-­ vaporizing-temperature materials. In this connection, however, it should be pointed out that, where the welding operation is performed, the metal sheets, contrary to what one would logically sup­ pose, must not be clamped together airtight over the welding area. In fact, the only way of obtaining a "clean" weld between two metal sheets protected using low-vaporiz­ ing-temperature materials is to provide between the metal sheets, in any way possible, a passage enabling the weld area to communicate externally, where "externally" is in­ tended to mean any space enabling safe expansion of the said vaporizing gas. Obviously, the hydraulic resistance of the said exhaust passage to the said vaporizing gas must be lower than that of the molten metal on the sheets being welded.

Claims: 1. A method for laser welding sheet metal (1,2) protected by a protective layer (4) of a low-vaporizing-temperature material, whereby at least two metal sheets (1,2), at least one of which is protected, are kept in an overlapping relationship in a weld area (11) by means of gripping means (8) which clamp the sheets together, and are arranged adjacent to the welding area (11), at least one layer (4) of the protecting material being located between the metal sheets (1,2) in the welding area (11), and the welding area communicating externally externally through at least one passage (12,14,15) wherein said sheets (1,2) are kept in direct contact with each other where said gripping means (8) are located, and said passage (12,14,15) is determined by the particular shapes of said sheets (1,2). 2. A method as claimed in Claim 1, wherein said welding area (11) extends along portions of said two sheets (1,2) having given essentially identical curves; said passage (12) being defined by at least one (10) of said portions blending with at least one further portion having a different curve from a corresponding portion on the other said sheet (1,2), and diverging from the latter; said gripping means (8) is located between the welding area (11) and said further diverging portion. 3. A method as claimed in Claim 1, wherein said passage consists of at least one channel (14) formed between said sheets (1,2) by distorning at least one of said sheets (1,2). 4. A method as claimed in Claim 1, wherein said passage consist in a number of channels formed between said sheets (1,2) by forming a knurled section (15) on at least one of said sheets (1,2).

Inventors: CANTELLO, MAICHI, DELLE PIANE, ALBERTO, GHIRINGHELLO, GUGLIELMO, SARTORIO, FRANCO
Applicants: PRIMA INDUSTRIE S.P.A.
Application year: 1985
Main classification: B23K26
IPC codes: B23K26