APPARATUS AND METHOD FOR CARRYING OUT DRY ETCHING

Abstract: A dry etching apparatus according to the present invention is characterized in that an etching process is applied to a sample by using both physical etching means and chemical etching means. To perform such an etching process, the dry etching apparatus is provided with a chamber (3) for accommodating a sample (15) to be etched, a suction unit for reducing a pressure within the chamber, a gas introducing unit (16) for introducing a reactive gas into said chamber, an excitation unit (17) to excite the reactive gas for producing activated species allowing the sample to be etched due to chemical reaction, and an ion irradiation unit (7,10,11) for irradiating ions to the sample, thereby making it possible to independently control the energy or density of ions and the density of the activated species, thus setting optimum etching conditions in conformity with a material to be etched or an etching pattern.

Description: The present invention relates to an apparatus and a method for carrying out dry etching. The invention may be applied to apparatus and methods for forming patterns of semiconductor integrated circuits. WO 84/02228 discloses dry etching apparatus for accommodating a sample to be etched within a chamber under reduced pressure conditions, comprising: means for providing ions of a controllable energy and/or density within the chamber; means for accelerating the ions and causing them to impinge directionally on the sample and thereby to etch the sample; means for introducing a reactive gas into the chamber; and means for supplying energy to the reactive gas so as to excite it and thereby generate a controlled density of chemically activated, electrically neutral species allowing said sample to be etched by chemical reaction. The document also discloses a method of dry etching in which a sample is accommodated within a chamber under reduced pressure conditions comprising the steps of: exposing the sample to chemically reactive, electrically neutral species to etch said sample by chemical reaction; and generating ions of a gas in the chamber and accelerating said ions directionally towards the sample to effect etching thereof. Other dry etching apparatus and methods are known from EP-A-0127l88. In the fabrication of semiconductor devices, particularly LSI circuits, a dry etching process is necessarily required. Such a dry etching process is roughly classified into a method based on physical reaction and a method based on chemical reaction. A typical method of the former is a sputter etching method and a typical method of the latter is a CDE (Chemical Dry Etching) method. As indicated in Table 1, etching methods of intermediate characteristics therebetween are RIBE (Reactive Ion Beam Etching) method, RIE (Reactive Ion Etching) method, plasma etching method, etc. A study has been made to compare the method based on the physical reaction with the method based on the chemical reaction in connection with the etching characteristic. Since the former method is an etching due to irradiation of ion beam etc., a reaction proceeds along an ion advancing direction, resulting in good anisotropy, but sputtering yields (the numbers of target atoms removed per one incident particle) between materials are not different from each other to much extent, resulting in poor selectivity therebetween. In contrast, since the latter method is an etching utilizing chemical reaction due to activated species, the activated species are isotropically diffused. As a result, anisotropy becomes poor, but the reaction is greatly varied depending upon kinds of activated species and samples, resulting in good selectivity. Further, in regard to damages to the sample, even when either method is employed, the surface of the sample is damaged by the exposure to ion beam or plasma. However, the degree of the damage by the method based on physical reaction is larger than that by the method based on chemical reaction. The method based on physical reaction is mainly used for etching samples such as SiO₂ or Si, etc. and the method based on chemical reaction is mainly used for etching samples such as doped Si or Al, etc. The etching employed in the manufacturing processes for LSI has the following three requirements. First is that anisotropy is excellent. Second is that selection ratio between materials is large. Third is small damage. The first requirement is necessarily required for high precision dimension control. In the recent LSI, pattern formation of the circuit dimension of approximately 1 µm (micron) is required. To effect etching faithful to a resist pattern as a mask, etching having excellent anisotropy is required. The second requirement on the selectivity is necessarily required for etching integrated semiconductor devices. A gate oxide film increasingly becomes thin and the employment of a shallow junction as a junction layer of a semiconductor is now generalised. For instance. in case where there arises a need such that a gate oxide film is left to remove other layers by etching, an employment of an etching process having poor selectivity results in the fact that even the gate oxide film is removed. As a result, there is a possibility that there occurs an opening in the gate oxide film. Accordingly, according as the integration is developed, an etching process having higher selectivity is required. In addition, in regard to the third requirement on the damage, an etching method having less damage is desired for the same reason stated above. However, both the above-mentioned methods have advantages and disadvantages, viz., the etching process based on physical reaction has good anisotropy but poor selectivity, whereas the etching process based on chemical reaction has good selectivity but poor anisotropy. On the other hand, with other processes, e.g., RIBE, RIE and plasma etching, etc. which lie intermediate the above-mentioned two methods, it can be said that they stand on an appreciable point of compromise but fail to provide excellent anisotropy or excellent selectivity. Further, these methods cannot control the energy or density of ions independently of other parameters, e.g., density of activated species, etc., thus failing to provide optimum etching conditions. For instance, the reduction of energy of ions solely depends upon an indirect method, e.g., a method of lowering a high frequency power used for excitation of activiated species, a method of raising a pressure within a chamber or the like. Thus, this results in changes in other etching conditions. As stated above, the drawback with the above-mentioned conventional dry etching apparatus is that it is unable to set optimum etching conditions depending upon the quality of the sample to be etched or an etching pattern. With the above in view, an object of the present invention is to provide an apparatus for carrying out dry etching, which makes it possible to set optimum etching conditions depending upon the quality of the sample to be etched and the etching pattern. According to one aspect of the invention, there is provided a dry etching apparatus for accommodating a sample to be etched within a chamber under reduced pressure conditions, comprising: means for providing ions of a controllable enery and/or density within the chamber; means for accelerating the ions and causing them to impinge directionally on the sample and thereby to etch the sample; means for introducing a reactive gas into the chamber; and means for supplying energy to the reactive gas so as to excite it and thereby generate a controllable density of chemically activated, electrically neutral species allowing said sample to be etched by chemical reaction; characterised in that the density of said activated species can be controlled simultaneously with and independently of the energy and/or density of said ions. According to another aspect of the invention, there is provided a method of dry etching in which a sample is accommodated within a chamber under reduced pressure conditions comprising the steps of exposing the sample to chemically reactive, electrically neutral species to etch said sample by chemical reaction; and simultaneously generating ions of a gas in the chamber and accelerating said ions directionally towards the sample to effect etching thereof, whereby the density of said reactive species and the energy and/or density of said ions are simultaneously and independently controlled. In the accompanying drawings: Fig. 1 is a diagrammatical view illustrating an embodiment of a dry etching apparatus according to one embodiment of the present invention; Fig.2 is a diagrammatical view illustrating another embodiment of a dry etching apparatus according to the present invention; Figs. 3a to 3g are cross sectional views showing etching processes carried out with the dry etching apparatus according to the present invention; and Fig. 4 is a graph showing the relationship between an etch rate and an ion energy by using an ion current and a high frequency applied to the electrode 17 which is shown in Fig. 1 as parameters. Embodments of the present invention will be described in detail in conjunction with preferred embodiments illustrated. Referring to Fig. 1, there is shown an embodiment of a dry etching apparatus according to the present invention. A chamber 1 comprises an upper chamber 2 and a lower chamber 3 as shown. The upper chamber 2 and the lower chamber 3 are evacuated by a vacuum pump (not shown) through evacuating holes 4 and 5 and through an evacuating hole 6, respectively, thus maintaining a pressure within the chamber 1 constant. The upper chamber 2 is provided at the upper portion thereof with an ionization gun 7 of a large diameter, which ionizes an ion source gas introduced from a gas inlet tube 8 by a power supplied from a power supply unit 9. Below the ionization gun 7, there is provided an insulated multistage grid electrode (solely the first stage grid electrode 10 and the final stage grid electrode 11 are illustrated in the Figure). To grid electrodes, voltages are applied by means of DC power sources 12 and 13, respectively. The voltage applied to the first stage grid electrode 10 functions as an ionization voltage and the voltage applied to the final stage grid electrode 11 functions as an ion acceleration control voltage. The lower chamber 3 is provided with a temperature controlled support 14 on which a sample to be etched, e.g., a Si wafer 15 comprising various kinds of stacked layers is mounted. The chamber 1 is provided in the middle thereof with two gas inlets 16. Reactive gas introduced from each gas inlet tube 16 is filled within the lower chamber 3. The lower chamber 3 is provided with a pair of opposite electrodes 17. To the electrode 17 positioned left in the Figure, a high frequency or a DC voltage is applied to produce glow discharge between the opposite electrodes 17. This glow discharge allows the reactive gas introduced to be excited. On the one side of the support 14, an electron gun 19 is provided. This electron gun 19 is used, when an insulating material is employed as the sample, for neutralizing ions produced due to ion irradiation to prevent charge-up of the sample. In accordance with the apparatus of the invention, an etching based on physical reaction is carried out by ion beam generated within the upper chamber 2. As ion source gas, rare gas ,e.g., He or Ar, etc., halogen gas, e.g., Cl₂ or CF₄ or mixture gas of the rare gas and the halogen gas is preferably used. Energy and density of the ion beam may be desirably adjustable by varying an amount of gas to be introduced and a voltage applied to each grid electrode. The apparatus in this embodiment can produce ion beam of 0.1 A/cm² as the maximum value and desirably control ion acceleration voltage within a range from 0 to 1 KV. On the other hand, etching based on chemical reaction is carried out by causing discharge between the opposite electrodes 17 to change reactive gas introduced into the lower chamber 3 into an activated species, e.g., radical or plasma, etc. In this instance, halogen gas, e.g., Cl₂ or CF₄, etc. may be used as the reactive gas. The density of the activated species can be independently controlled by adjusting high frequency applied to either of the opposite electrodes. Fig. 2 is a diagrammatical view illustrating another embodiment of a dry etching apparatus according to the present invention. This embodiment differs from the first-mentioned embodiment only in the structure for feeding reactive gas into the lower chamber 3. Other parts in this embodiment are identical to those in the above-mentioned embodiment. Accordingly, these parts are denoted by the same reference numerals, respectively, and therefore their explanation will be omitted. The apparatus is provided outside of the chamber 1 with a gas supply unit comprising a gas inlet tube 20 from which reactive gas is introduced, a microwave generator 21 for generating microwave, and a waveguide 22 joined to the microwave generator 21, whereby the microwave generated in the microwave generator 21 is applied to the reactive gas through the waveguide 22. By the energy of the microwave, activated species is produced within the reactive gas introduced. The activated species thus produced is delivered to the lower chamber 3 through the gas inlet tube 16. The density of the activated species can be controlled by adjusting the microwave power. As stated above, the dry etching apparatus according to the present invention makes it possible to control energy or density of ion beam contributing to physical reaction and density of the active species contributing to chemical reaction in an independent fashion to set optimum etching conditions. Namely, as shown in Table 2, a control is effected to independently vary parameters, respectively, thus making it possible to continuously set etching conditions from the range where the physical reaction is dominant to the range where the chemical reaction is dominant. When, e.g., rare gas is employed as ion source gas, the physical reaction becomes dominant. By mixing reactive gas, e.g., halogen, etc. into such a reactive system, it is possible to increase the ratio of the chemical reaction. Further, by increasing ion current and ion acceleration voltage, the physical reaction becomes dominant. In contrast, by decreasing them, the chemical reaction becomes dominant. Furthermore, by ceasing the irradiation of the ion beam, there occurs condition where only the chemical reaction exclusively exists. In contrast, by ceasing both introduction of the activated species source gas and an application of high frequency, there occurs condition where only the physical reaction due to the radiation of the ion beam exists. In addition, by introducing a reactive gas as the activated species source gas and increasing high frequency power applied, the chemical reaction becomes dominant. An example of etching process performed with a dry etching apparatus according to the present invention will be described. This example indicates that an etching process is applied to a semiconductor device as shown in Fig. 3a to produce a semiconductor device shown in Fig. 3b wherein the semiconductor device comprises a semiconductor substrate 31, a thin gate oxide film 32 (of 100 Å in thickness) and a polysilicon layer 33 stacked in succession on the semiconductor substrate 3l, and a resist pattern of approximately 1 µm in width formed on the polysilicon layer 33. It is assumed that three etching conditons are set in the dry etching apparatus according to the present invention. Fig. 4 is a graph showing etch rates in these three conditions (I), (II) and (III). According to this graph, there is illustrated the relationship between energy of ion beam and the etch rates when a polysilicon and SiO₂ are employed as samples in connection with each condition. The first condition (I) is set for carrying out etching based on physical reaction wherein the setting is made such that the value of an ion current (governing ion density) is 5A and there is no application of high frequency or r.f. to the electrode to be powered within the lower chamber 3. Namely, in accordance with the first condition (I), the etching due to ion beam becomes dominant instead of the etching due to the activated species. Accordingly, the anisotropy becomes desirable whereas the selectivity is degraded. As indicated by the graph, the ratio of polysilicon and SiO₂ (the ratio of etch rates thereof) represents a value from 2 to 3. In contrast, the third condition (III) is set for carrying out etching based on chemical reaction wherein the setting is made such that there is no ion current and there is application of high frequency to the electrode to be powered within the lower chamber 3. Namely, in accordance with the third condition (III), the etching due to activated species becomes dominant instead of the etching due to ion beam. Accordingly, the anisotropy is degraded whereas the selectivity becomes high. As indicated by the graph, the ratio of polysilicon and SiO₂ represents more than ten. In addition, the second condition (II) is set for carrying out both the physical reaction and the chemical reaction wherein the setting is made such that the value of the ion current is 5A and there is application of high frequency to the electrode to be powered within the lower chamber 3. This second condition (II) represents intermediate nature between the conditions (I) and (III) in regard to both the anisotropy and selectivity. Initially, when an etching process is applied to the semiconductor device shown in Fig. 3a in accordance with the first condition (I), a semiconductor device as shown in Fig. 3c is obtained. The semiconductor device which has undergone such an etching process has an excellent anisotropy. Accordingly, there is no possibility that the polysilicon layer 33 is subject to erosion below the resist pattern 34. However, since it has low selectivity, not only the polysilicon layer 33 but also the gate oxide film 32 are removed by etching process. Likewise, when an etching process is applied to the semiconductor device shown in Fig. 3a in accordance with the third condition (III), a semiconductor device as shown in Fig. 3d is obtained. Since the semiconductor device thus obtained has an excellent selectivity, the gate oxide film 32 is not etched. However, since it has poor anisotropy, isotropic etching is carried out, with the result that the polysilicon layer 33 is subject to erosion below the resist pattern 34. Likewise, when an etching process is applied to the semiconductor device shown in Fig. 3a in accordance with the condition (II), a semiconductor device as shown in Fig. 3e is obtained in accordance with a condition obtained as a compromise between the conditions (I) and (III). In view of this, a modified etching process is conducted in order to realize a desired structure as shown in Fig. 3b by varying the setting of the conditions in the middle of the etching process. Namely, an etching process is initiated in accordance with the condition (I) to change into an etching based on the condition (III) at time when an etching process applied to the polysilicon layer 33 is not completely finished. Thus, this makes it possible to carry out an etching representing an excellent anisotropy at the first part of the etching and to carry out an etching representing an excellent selectivity at the latter part thereof. Accordingly, a semiconductor device of a structure shown in Fig. 3g is realized, thus making it possible to perform substantially desired etching. One example of use of the dry etching apparatus according to the present invention has been described. In addition, by varying various parameters shown in Table 2, a wide variety of uses can be realized. As stated above, the dry etching apparatus according to the present invention is configured so that energy or density of ions and density of activated species can be independently controlled. Thus, this enables setting of optimum conditions in conformity with a quality of sample to be etched and an etching pattern to carry out a desired etching process.

Claims: A dry etching apparatus for accommodating a sample (15) to be etched within a chamber (3) under reduced pressure conditions, comprising: means (7,9,10,12) for providing ions of a controllable energy and/or density within the chamber (3); means (11,13) for accelerating the ions and causing them to impinge directionally on the sample (15) and thereby to etch the sample; means (16) for introducing a reactive gas into the chamber (3); and means (17,18) for supplying energy to the reactive gas so as to excite it and thereby generate a controlled density of chemically activated, electrically neutral species allowing said sample to be etched by chemical reaction; characterised in that the density of said activated species can be controlled simultaneously with and independently of the energy and/or density of said ions. A dry etching apparatus as set forth in claim 1, wherein said reactive gas is a gas of halogen compound, and said activated species is a radical or plasma thereof. A dry etching apparatus as set forth in claim 2, wherein said reactive gas is a gas containing chlorine (Cl) or fluorine (F). A dry etching apparatus as set forth in any one of claims 1 to 3, wherein said ions are ions of a rare gas or a gas of a halogen compound, or a mixture of said rare gas and said halogen compound gas. A dry etching apparatus as set forth in claim 4, wherein said ions are ions of helium (He) or argon (Ar). A dry etching apparatus as set forth in claim 4, wherein said ions are ions of a gas containing chlorine (Cl) or fluorine (F). A dry etching apparatus according to any preceding claim wherein there is provided means (10) for effecting ionization of a gas. A dry etching apparatus according to claim 7 wherein there is provided a multistage grid electrode having a first stage grid electrode (10) operable to effect ionization and a final stage grid electrode (11) operable for ion acceleration. A dry etching apparatus according to any one of the preceding claims wherein a pair of opposed electrodes (17) is provided in said chamber (3) for excitation of reactive gas by glow discharge. A method of dry etching in which a sample (15) is accommodated within a chamber (3) under reduced pressure conditions comprising the steps of: exposing the sample (15) to chemically reactive, electrically neutral species to etch said sample by chemical reaction; and simultaneously generating ions of a gas in the chamber (3) and accelerating said ions directionally towards the sample (15) to effect etching thereof, whereby the density of said reactive species and the energy and/or density of said ions are simultaneously and independently controlled.

Inventors: WATANABE, TORU
Applicants: KABUSHIKI KAISHA TOSHIBA
Application year: 1985
Main classification: H01J37
IPC codes: H01L21, H01J37