STABILIZERS FOR HALOGEN-CONTAINING ORGANIC POLYMERS COMPRISING AN ORGANOTIN COMPOUND AND A DIESTER

Abstract: Compositions for stabilizing halogen-containing organic polymers against the deteriorative effects of heat, light and weathering comprise an organotin compound selected from or­ ganotin sulfides, organotin mercaptides, organotin carboxy­ lates and mixtures thereof, and a diester of an ethylenically un­ saturated dicarboxylic acid having one carboxyl group on each carbon atom of the ethylene group. The diester is present in an amount sufficient to act synergistically with the organotin compound in stabilizing the polymer, but not sufficient to plasticise the polymer.

Description: This invention relates to compositions which are capable of stabilizing rigid (unplasticized) halogen-containing organic polymers against the deteriorative effects of heat, light and weathering. Such stabilizers comprise an organotin mercaptide and/or an organotin sulfide, and a dialkyl ester of an ethylenically unsaturated dicarboxylic acid. The invention also relates to halogen-containing organic polymers stabilized with such compositions. It has long been known that halogen-containing organic polymers, such as the commercially important poly (vinyl chloride), are subject to deterioration or degradation when exposed to heat and light. Various chemical compounds and compositions have been developed to stabilize these polymers against such deterioration. For the most part, these stabilizers have been directed toward stabilization against heat, such as that encountered during processing of the polymer and its fabrication into articles. Among these heat stabilizers, some of the most effective have been the organotin compounds. The organotin compounds which have been found to be effective heat stabilizers for halogen-containing organic polymers include a wide variety of compounds. Mono- and dialkyltin carboxylates and mono- and dialkyltin mercaptides, for example,have been employed successfully as heat stabilizers. Other organic, non-metallic compounds have also been found to be useful as heat stabilizers for halogen-containing organic polymers and are sometimes employed in combination with the organotin stabilizers. For instance, US Patent No.3,379,679 discloses stabilizer compositions containing an organotin maleate of the formula: and a maleate ester of the formula: where R, R₁ and R₂ are each alkyl or alkenyl of up to 12 carbon atoms, or aryl, alkaryl or aralkyl of from 6 to 9 carbon atoms; and R₃ is hydrogen, alkyl or alkenyl of up to 12 carbon atoms, or aryl alkaryl or aralkyl of from 6 to 9 carbon atoms, provided that at least one of said R₃ is other than hydrogen. With the increased use of halogen-containing organic polymers for rigid articles which will be exposed to light and weathering for long periods of time (e.g. housing siding and window profiles) it has become increasingly important to develop a stabilizer which will not only protect the polymer against the high temperatures encountered during processing and fabrication, but will also protect the polymer against the long-term effects of light and weathering. However, until the present invention, no single stabilizer composition was completely satisfactory for protecting the halogen-containing organic polymers against heat, light and weathering. Thus, while an organotin compound, and in particular the organotin mercaptides, provided good heat stability, they were not acceptable weathering stabilizers. Likewise, the aforementioned combination of organotin maleates and maleate esters dislcosed in US-A-3,379,679 does not provide adequate heat stability, is incompatible with normally used ingredients employed in commercial polymer formulations (commonly called "microingredients"), such as calcium stearate, and can cause problems with eye irritation and offensive odours due to the presence of the organotin maleate. Thus, the industry has been unable to use organotin maleates as light stabilizers because of the aforementioned problems. Instead, it chooses to use the organotin mercaptides which overcome the problems of eye irritation and incompatibility with microingredients, but which give less than desired weathering and light stabilization. US-A-4111889 discloses a rigid resin composition comprising 100 parts by weight of a halogen-containing resin and 0.1 to 2.0 weight parts of a diester of a dibasic acid with a C₁₁ to C₃₂ monohydric alcohol. The composition may also include an organotin stabilizer such as a combination of a dioctyl tin mercapto compound and a dioctyl tin maleate polymer. It has now been quite unexpectedly discovered that the problems encountered with the prior art stabilizers can be overcome while still providing excellent stabilization of halogen-containing organic polymers against heat, light and weathering when stabilizers are employed which comprise certain organotin mercaptides and/or organotin carboxylates in combination with certain lower esters of ethylenically unsaturated dicarboxylic acids. In accordance with the present invention there are provided compositions capable of stabilizing halogen-containing organic polymers against the deteriorative effects of heat, light and weathering, said composition comprising the product produced by combining: A. one or more organotin mercaptides and B. a diester of an ethylenically unsaturated dicarboxylic acid having one carboxyl group on each carbon atom of the ethylene group. The organotin component (A) includes at least one organotin mercaptide having one of the general formulas: (IV) R n -Sn-X p and may also include one or more organotin carboxylates of the general formulas: (VII) R n -Sn-Z p wherein X is at each independent occurrence selected from -SR², with the proviso that; (1) at least one X in formulas III and IV is -SR² and (2) in formula V at least one X is -SR² or at least one Y is -S-R³-W Y is at each independent occurrence selected from -(S)- v , -S-R³-W-, W is at each independent occurrence selected from oxygen or sulfur; R is at each independent occurrence selected from alkyl, alkenyl, cycloalkyl, cycloalkenyl, -R⁹-O-R¹², -R⁹-CN; R² is at each independent occurrence selected from alkyl, alkenyl, cycloalkyl, cycloalkenyl, -R³-S-R⁷,or -R³-O-R⁷; R³ is at each independent occurrence selected from alkylene of at least 2 carbon atoms, alkenylene of at least 2 carbon atoms, cycloalkylene, or cycloalkenylene; R⁴ is at each independent occurrence selected from alkylene, alkenylene, cycloalkylene, or cycloalkenylene; R⁶ is at each independent occurrence selected from a carbon-carbon bond, or R⁴; R⁷ is at each independent occurrence selected from -H or R⁸; R⁸ is at each independent occurrence selected from alkyl, alkenyl, cycloalkyl, or cycloalkenyl; R⁹ is at each independent occurrence selected from C₁ to C₄ alkylene; R¹² is at each independent occurrence selected from -H or a monovalent C₁ to C₂₀ hydrocarbon radical; R¹³ and R¹⁴ are at each independent occurrence selected from C₁ to C₂₀ alkyl or C₁ to C₂₀ alkoxy; at each independent occurrence n=1 or 2 and p=4-n; at each independent occurrence a = 1 or 2; b = 2-a; c = 1 or 2; d = 3-c; and q = 0 or an integer from 1 to 4 inclusive; v is at each independent occurrence selected from an integer from 1 to 8 inclusive; Z is A is and r=O or an integer. In component (B) each of said carboxyl groups is also attached, via an oxygen atom, to a mono-or divalent hydrocarbon residue having from 1 to 10 carbon atoms, which may be hydroxy-substituted. The organotin mercaptides used in this invention are compounds which have at least one tetravalent tin atom which has one or two direct tin to carbon bonds and at least one tin to sulfur to carbon (Sn-S-C) bond. In the above formulas, it is understood that formula V includes those organotin mercaptides which are cyclic, i.e. where formulas V would be written: Examples of organotin mercaptides useful in the practice of this invention include, but are not limited to: (1) alkyltin alkylthioalkanoates, including monoalkyltin tris(alkylthioalkanoates) and dialkyltin bis(alkylthioalkanoates), such as (2) alkyltin mercaptoalkylalkanoates, including the monoalkyltin tris(mercaptoalkylalkanoates) and dialkyltin bis(mercaptoalkylalkanoates), such as (3)bis(alkyltin alkylthioalkanoate) sulfides, including the bis(monoalkyltin di(alkylthioalkanoate))sulfides and bis(dialkyltin mono(alkylthioalkanoate))sulfides, such as (4) bis(alkyltin mercaptoalkylalkanoate)sulfides, including bis(monoalkyltin di(mercaptoalkylalkanoate))sulfides and bis(dialkyltin mono(mercaptoalkylalkanoate))sulfides, such as bis(dioctyltin mono(mercaptoethylpelargonate))sulfide (5) alkyltin alkylmercaptides, including monalkyltin tris(alkylmercaptides) and dialkyltin bis(alkylmercaptides) such as Particularly useful in the practice of this invention are mixtures of monoalkyltin and dialkyltin mercaptides. The organotin carboxylates which may be included in component (A) in accordance with this invention are compounds which have tetravalent tin atoms which each have one or two direct tin to carbon bonds, the remainder of the bonds on the tin atoms being tin to oxygen to carbonyl, i.e. tin-carboxyl bonds. Examples of organotin carboxylates which are useful in the practice of this invention include, but are not limited to, alkyltin alkyl maleates, such as dibutyltin bis(butyl maleate), and polymeric alkyltin maleates, such as dibutyl-tin maleate. The compounds employed in combination with the above-described organotin compounds in the practice of this invention are diesters of ethylenically unsaturated dicarboxylic acids having one carboxyl group on each carbon atom of the ethylene group. One preferred class of diesters is represented by compounds having the general formula (I): where R¹⁰⁰ and R¹⁰³ are the same or different, and are at each independent occurrence alkyl, alkenyl, cycloalkyl, cycloalkenyl, or a multivalent hydrocarbyl or hydroxyl-substituted hydrocarbyl group such as alkylene, alkenylene, cycloalkylene, cycloalkenylene, alkynylene or tetravalent carbon; R¹⁰¹ is at each independent occurrence a carbon-oxygen bond, alkylene or alkenylene, with the proviso that the total number of carbon atoms in R¹⁰⁰ plus R¹⁰¹ is from 1 to 10 and the total number of carbon atoms in R¹⁰³ plus R¹⁰¹ is from 1 to 10; R¹⁰² is at each independent occurrence selected from hydrogen, alkyl and alkylene (i.e. the alkylene group forms a ring with the -C=C- group); and t is an integer, preferably from 1 to 20. Another preferred class of diesters is represented by components having the general formula II : where: R²⁰⁰ and R²⁰³ each have from 1 to 10 carbon atoms and are at each independent occurrence selected from alkyl, alkenyl, cycloalkyl, cycloalkenyl, multivalent hydrocarbyl group having a valence equal to z', multivalent hydroxyl substituted hydrocarbyl group having a valence equal to z', and R²⁰¹ is at each independent occurrence selected from alkylene, alkenylene, cycloalkylene, cycloalkenylene, a multivalent hydrocarbyl group and multivalent hydroxyl-substituted hydrocarbyl group; R²⁰² is at each independent occurrence selected from hydrogen, alkyl and alkylene (i.e. the alkylene group forms a ring with the -C=C- group); R²⁰⁴ is at each independent occurrence selected from hydrogen and alkyl; Z²⁰⁰ is at each independent occurrence selected from -O-, and -S-; t' is zero or an integer from 1 to 20; x' is zero or an integer from 1 to 20 with the proviso that if X'=O or t'=O then R²⁰⁰ is y' is an integer from 1 to 10; and z' is an integer from 1 to 4. It should be noted that the diesters useful in this invention include both the cis and trans isomers. The diesters useful in accordance with this invention do not function as lubricants in halogen-containing polymer compositions based on rheological testing commonly used in the industry, such as with a Brabender rheometer. The diesters are essentially non-lubricating in that they do not enhance the stability of the halogen-containing polymer by physically modifying the polymer melt. It is believed that this is due to the relatively short chain (C₁ to C₁₀) alcohol used to prepare the diesters. Examples of the diesters according to formula I which are useful in this invention include, but are not limited to, the following compounds which are identified by both chemical name (or structure) and by the substitutents in formula I: Further examples include the fumarate counterparts to the above maleate diesters. Mixtures of maleate and fumarate diesters (which are commonly formed during the preparation of these diesters) may also be employed. Examples of the diesters according to formula II which are useful in this invention include, but are not limited to, the following compounds which are identified by both chemical name (and/or structure) and by the substituents in formula II: Further examples include the fumarate counterparts to the above maleate diesters. Mixtures of maleate and fumarate diesters (which are commonly formed during the preparation of these diesters) may also be employed. The diesters which are preferred in practice of this invention are those according to formula II where R²⁰⁰ is C₁ to C₁₀ alkyl, R²⁰¹ is C₁ to C₄ alkylene, R²⁰² is hydrogen, Z²⁰⁰ is -O-, t' is at least 1 but not more than 20 and x' is at least 1 but not more than 3. As used in the above formulas and throughout this specification, the term alkyl represents monovalent, straight or branched chain, saturated hydrocarbon radicals containing, for example, 1 to 20 carbon atoms, the term alkylene refers to divalent, straight or branched chain saturated hydrocarbon radicals containing, for example, 1 to 20 carbon atoms and the term alkynylene refers to trivalent straight or branched chain saturated hydrocarbon radicals containing, for example, 1 to 20 carbon atoms. The term alkenyl refers to monovalent, straight or branched chain C₂ to C₂₀ hydro-carbon radicals containing at least one double bond, and the term alkenylene refers to divalent C₂ to C₂₀ hydrocarbon radicals containing at least one double bond. The term cycloalkyl represents monovalent C₃-C₈ saturated cycloaliphatic radicals; cycloalkylene refers to divalent C₃-C₈ cycloaliphatic radicals; cycloalkenyl refers to monovalent C₅-C₈ cycloaliphatic radicals containing at least one double bond; and cycloalkenylene represents divalent C₅-C₈ cycloaliphatic radicals containing at least one double bond. The term multivalent hydrocarbyl group refers to groups such as alkylene, alkenylene, cycloalkylene, cycloalkenylene, alkynylene and tetravalent carbon, and the term multivalent hydroxyl-substituted hydrocarbyl group refers to groups such as hydroxyl-substituted alkylene, alkenylene, cycloalkylene, cycloalkenylene alkynylene and tetravalent carbon. In the compositions of the invention the weight ratio of component (A) to component (B) is in a range from 2:1 to 1:8. There is further provided in accordance with the present invention a composition comprising a halogen-containing organic polymer and an effective amount of a stabilizer composition as defined above. The halogen-containing organic polymers which are stabilized by the stabilizer compositions of this invention and which are useful in the polymer compositions of this invention include, for example, halogenated polyolefin homopolymers, halogenated polyolefin copolymers, polymer blends containing a halogenated polyolefin homopolymer or copolymer, vinyl halide homopolymers, vinyl halide copolymers and polymer blends containing vinyl halide homopolymer or copolymers. The vinyl halide homopolymers, vinyl halide copolymers and polymer blends containing vinyl halide homopolymers or vinyl halide copolymers usable in the practice of this invention may be, for example, (1) polyvinyl chloride, polyvinylidene chloride, polyvinyl bromide, polyvinyl fluoride, polyvinylidene fluoride, (2) copolymers of vinyl chloride with a copolymerizable ethylenically unsaturated monomer such as vinylidene chloride, vinyl acetate, vinyl butyrate, vinyl benzoate, diethyl fumarate, diethyl maleate, other alkyl fumarates and maleates, vinyl propionate, methyl acrylate, 2-ethylhexyl acrylate, butyl acrylate, ethyl acrylate, and other alkyl acrylates, methyl methacrylate, ethyl methacrylate, butyl methacrylate, hydroxyethyl methacrylate and other alkyl methacrylates, methyl alpha-chloroacrylate, styrene, vinyl ethers such as vinyl ethyl ether, vinyl chloroethyl ether, vinyl phenyl ether; vinyl ketones such as vinyl methyl ketone, vinyl phenyl ketone, 1 -fluoro-1-chloroethylene, acrylonitrile, chloroacrylonitrile, allylidene diacetate, chloroallylidene diacetate, ethylene and propylene, and (3) polymer blends such as blends of polyvinyl chloride and polyethylene, polyvinyl chloride and chlorinated polyethylene, polyvinyl chloride and polymethyl methacrylate, polyvinyl chloride and polybutylmethacrylate, polyvinyl chloride and polystyrene, polyvinyl chloride and acrylonitrile-butadiene-styrene copolymer, and polyvinyl chloride and polyethylene and polymethyl methacrylate. Typical vinyl halide copolymers usable in this invention include vinyl chloride-vinyl acetate (87:13), vinyl chloride-vinylidene chloride (95:5), vinyl chloride-diethylfumarate (95:5), vinyl chloride-trichloroethylene (95:5) and vinyl chloride-2-ethylhexyl acrylate (80:20). The polymer blends usable in the practice of this invention comprises physical blends of at least two distinct polymeric species and contain from 25 to 95 weight percent of vinyl halide homopolymer. The vinyl halide copolymers usable in the practice of this invention are copolymers comprising from 25 to 95 mole percent vinyl halide units. Of these polymers, the vinyl halide homopolymers are preferred. The amount of organotin mercaptide and/or organotin carboxylate and diester in the stabilizer compositions of this invention will depend upon several factors, including, but not limited to, the particular organotin mercaptide compound, diester and organotin carboxylate employed, the particular resin which is intended to be stabilized, the severity of the heat, light and weathering to which the resin will be subjected and the degree of stabilization desired. Thus, the amount of organotin-sulfur compound and/or organotin carboxylate and diester may vary considerably within the defined range provided the stabilizer composition contains enough of each component to stabilize a halogen-containing organic polymer against the deteriorative effects of heat, light and weathering, the diester being present in an amount which will synergize such stabilization while at the same time being insufficient to plasticize the polymer. The stabilizer compositions in accordance with this invention contain an organotin compound and diester in a molar ratio or organotin compound to diester (organotin mercaptide compound formula I diester) of from 2/1 to 1/8, preferably from 1/2 to 1/6. This corresponds for example to a stabilizer composition which contains roughly from about 20% to about 75% formula I diester, with the balance being organotin compound, the percentages being by weight based on the combined weight of the diester and organotin compound. These weight percentages may, of course, vary considerably depending upon the particular compounds selected and their molecular weights. When the stabilizer compositions in accordance with this invention employ an organotin mercaptide compound, an organotin carboxylate and a formula I diester, the amount of diester used is normally the same as that employed when the organotin mercaptide compound and diester are used alone. Thus, the molar ratio of organotin compounds (i.e. organotin-mercaptide compound plus organotin carboxylate) to diester would remain 2/1 to 1/8, preferably 1/2 to 1/6. However, the molar ratio of organotin-mercaptide compound to organotin carboxylate (organotin sulfur compound/organotin carboxylate) will generally be from 1/1 to 1/5. In terms of weight percent, the stabilizer would contain roughly about 15% to about 60% formula I diester with the balance being organotin-mercaptide compound and organotin carboxylate, the percentages being by weight based on the combined weight of diester, organotin-mercaptide compound and organotin carboxylate. The organotin portion of the stabilizer would contain 10% to 50% organotin-mercaptide compound and 50% to 90% organotin carboxylate, in this case the percentages being by weight based on the combined weight of only the organotin-mercaptide compound and organotin carboxylate. The stabilizer compositions in accordance with this invention which contain an organotin mercaptide, organotin carboxylate or mixture thereof and a diester according to formula II employ these compounds in a molar ratio of organotin compound to formula II diester (organotin compound/diester) of from 2/1 to 1/8, preferably from 1/2 to 1/6. This corresponds to a stabilizer composition which contains roughly from 20% to 75% formula II diester, with the balance being organotin compounds, the percentages being by weight based on the combined weight of the diester and organotin compound. These weight percentages may,a of course, vary considerably depending upon the particular compounds selected and their molecular weights. When the organotin portion of the stabilizer contains a mixture of an organotin-mercaptide compound and an organotin carboxylate the molar ratio of organotin-mercaptide compound to organotin carboxylate (organotin-mercaptide compound/organotin carboxylate) will generally be from 1/1 to 1/5. In terms of weight percent, the stabilizer would contain roughly 25% to 60% diester with the balance being organotin-mercaptide compound and organotin carboxylate, the percentages being by weight based on the combined weight of only the organotin-mercaptide compound and organotin carboxylate. As with the relative amounts of organotin-mercaptide compounds, diester and organotin carboxylate, the amount of stabilizer composition employed in the halogen-containing organic polymer compositions of this invention can vary considerably. The minimum amount of stabilizer in the polymer composition is that amount which will stabilize the polymer against the deteriorative effects of heat, light and weathering. While this minimum amount can vary depending upon the same factors referred to above with respect to the stabilizer compositions, in general 1.0% to 5.0% of stabilizer composition based on the weight of halogen-containing organic polymer will be sufficient to impart the desired properties to the polymer composition in most cases. Amounts greater than this minimum level of stabilizer can, of course, be employed, although at some point the increase in stabilization of the polymer is not commensurate with the additional amount of stabilizer employed. Thus, while there is no critical upper limit to the amount of stabilizer which may be employed, amounts in excess of about 8% do not give an increase in effectiveness which will justify the use of these higher amounts of stabilizer. In fact, amounts above about 8-10% of stabilizer composition may begin to plasticize the polymer and change its physical properties dramatically. The stabilizer compositions of this invention can be made quite simply. For example, the organotin-mercaptide compounds, diester and, if used, organotin carboxylate can be simply combined physically as by mixing, blending, stirring, shaking or the like. Likewise, the halogen-containing organic polymer compositions of this invention may be prepared by physically blending the stabilizer composition and the polymer (plus any desired additives) in any convenient manner until the stabilizer composition is thoroughly dispersed throughout the polymer composition. In normal commercial practice this is accomplished by high intensity mixing. The stabilized polymer compositions of this invention are useful to form a variety of rigid articles of manufacture, e.g. housing siding, window profiles and the like, and are especially useful in those articles which are exposed to light and weathering. A variety of conventional techniques may be employed to shape the polymer composition into the desired article. The following examples illustrate the present invention. Unless otherwise indicated, all parts and percentages in the examples and throughout this specification are by weight. Examples 1-6 and I-VII demonstrate the superior heat, light and weathering stabilization of compositions according to this invention which contain an organotin-mercaptide compound and a diester of the formula I type, or an organotin-mercaptide compound, formula I type diester and an organotin carboxylate. EXAMPLE 1-6 The stabilizer compositions indicated in Table I were each in turn blended with a standard poly (vinyl chloride) formulation containing: Each resulting polymer composition was then formed into a plaque and tested for stability to light and weathering by exposing it to ultraviolet light (UV) and moisture in a Q-Panel QUV accelerated weathering tester. Each plaque was weathered at 50°C by exposing it to 4 hours of UV followed by 4 hours of a moisture condensation cycle. This was repeated until the plaque had been exposed for 750 hours, samples being taken for evaluation every 150 hours. The results of these tests are summarized in Table I. The above results demonstrate that: 1. Organotin-mercaptide compounds are poor weathering stabilizers. For instance Control 1, Control 2 and Control 3 discolor severely after only about 150 hours. 2. Organotin carboxylates are adequate weathering stabilizers as demonstrated in Control 4. 3. The weathering stabilization of organotin carboxylates is improved only slightly, if at all, by their use in combination with diesters. (Control 4a shows very little improvement over Control 4.) 4. Stabilizers containing organotin-mercaptide compounds and diesters provide excellent weathering stability. This excellent stabilization, as shown in Ex. No. 1a-1f, Ex. No. 2 and Ex. No. 3, is quite unexpected in view of the poor weathering efficiency of the organotin-mercaptide compounds alone and the failure of the diesters to significantly improve the efficiency of the organotin carboxylates. 5. Stabilizers containing organotin-mercaptide compounds, diesters and organotin carboxylates also exhibit excellent weathering stabilization (see Control 5 vs. Ex. No. 5a-5i and Control 6 vs. Ex. No. 6). The excellent stabilization provided by these compositions is surprising in that they contain an ingredient known to exhibit poor weathering stabilization, i.e. the organotin-mercaptide compound. Thus, one would expect this three component system to perform worse than the organotin carboxylate/diester stabilizer. However, precisely the opposite occurs. When some of the organotin carboxylates of Controls 5 and 6 is replaced with organotin-mercaptide compound, the weathering efficiency, rather than decreasing as expected, improves dramatically. EXAMPLES I-VII The stabilizer compositions indicated in Table II were each in turn blended with the same standard poly (vinyl chloride) formulation used for the weathering stability tests. Each resulting polymer composition was then tested for stability to heat by milling on a two roll dynamic mill at about 180°C. Samples of each composition were taken after every 2 minutes of milling and examined for degradation and discoloration. The results are indicated in Table II. The heat stability results shown in Table II demonstrate that: 1. Organotin-mercaptide compounds are excellent heat stabilizers (see Controls I, II and III). 2. Employing diesters with organotin-mercaptide compounds does not adversely effect nor improve the organotin-mercaptide compounds' heat stabilizing efficiency. (See Examples I, II, III and III'). 3. Organotin carboxylates are extremely inefficient heat stabilizers as demonstrated in Control IV. Also, when the organotin carboxylates are employed in PVC formulations containing calcium stearate (a common ingredient in such formulations) their efficiency decreases even further (see Control IV'). 4. The use of diesters with the organotin carboxylates does not significantly improve the organotin carboxylates' heat stabilization in PVC formulations which do not contain calcium stearate (see Control V) or for those formulations which do contain calcium stearate (see Control V'). 5. Unexpectedly, the addition of the organotin carboxylate to a stabilizer containing an organotin-mercaptide compound and a diester still produces a stabilizer composition which yields acceptable heat stability. This is surprising in view of the extremely poor efficiency of the organotin carboxylate and the fact that a portion of the efficient organotin-mercaptide compound is replaced by the inefficient organotin carboxylate (see Example I vs. Examples V and V'). To summarize the results of Tables I and II, no synergism in either weathering or heat stabilization is observed for compositions containing organotin carboxylates and diesters. Synergism in weathering stability is, however, evident in those stabilizers containing organotin-mercaptide compounds and diesters. Likewise, synergism has been found in both weathering and heat stability for compositions containing organotin-mercaptide compounds, diesters and organotin carboxylates. These cases of synergism are unexpected since at least one of the compounds used in the synergized compositions are very inefficient stabilizers, yet their addition to the stabilizer system produces markedly superior results. Examples 7-8 and VIII-IX demonstrate the superior heat, light and weathering stabilization of compositions according to this invention which contain an organotin mercaptide, organotin carboxylate or mixtures thereof in combination with a diester of the formula II type. The stabilizer compositions indicated in Table A were each in turn blended with a standard poly(vinyl chloride) formulation containing: Each resulting polymer composition was then formed into a plaque and tested for stability to light and weathering by exposing it to ultraviolet light (UV) and moisture in a Q Panel QUV accelerated weathering tester. Each plaque was weathered at 50°C by exposing it to 4 hours of UV followed by 4 hours of a moisture condensation cycle. This was repeated until the plaque had been exposed for 750 hours, samples being taken for evaluation every 150 hours. The results of these tests are summarized in Table A. The above results demonstrate that: 1. Organotin-mercaptide compounds are poor weathering stabilizers. For instance, Control No. 7 and Control No. 8 show severe discoloration at the 150 hour point. 2. Stabilizers containing organotin-mercaptide compounds and diesters of the formula II type provide excellent weathering stability, as shown in Ex. No. 7a-7f and Ex. No. 8. Stabilizer compositions in accordance with this invention which contain an organotin carboxylate and diester of the formula II type also exhibit excellent weathering performance. EXAMPLES VIII-IX The stabilizer compositions indicated in Table B were each in turn blended with the same standard poly(vinyl chloride) formulation used for the weathering stability tests. Each resulting polymer composition was then tested for stability to heat by milling on a two roll mill at about 180°C. Samples of each polymer composition were taken after every 2 minutes of milling and examined for degradation and discoloration. The results are indicated in Table B. The heat stability results shown in Table B demonstrate that: 1. Organotin-sulfur compounds are excellent heat stabilizers (see Control VIII and Control IX). 2. Employing diesters of the formula IXa type with organotin-sulfur compounds does not adversely affect nor improve the organotin-sulfur compounds' heat stabilizing efficiency (See Ex. No. VIIIA, VIIIB, IXA and IXB). Organotin carboxylates alone are extremely inefficient heat stabilizers. However, it has been quite unexpectedly found that the addition of an organotin carboxylate to a stabilizer containing an organotin-mercaptide compound and a diester of the formula II type produces a stabilizer composition which yields acceptable heat stability. This is especially surprising in view of the extremely poor efficiency of the organotin carboxylate.

Claims: A composition capable of stabilizing halogen-containing organic polymers against the deteriorative effects of heating, light and weathering, comprising a combination of: A. an organotin compound or mixture of organotin compounds and B. a diester of an ethylenically unsaturated dicarboxylic acid having one carboxyl group on each carbon atom of the ethylene group characterised in that the organotin component (A) includes at least one organotin mercaptide having one of the general formulas: (IV) R n -Sn-X p wherein X is at each independent occurrence selected from -SR², or with the proviso that; (1) at least one X in formulas III and IV is -SR² and (2) in formula V at least one X is -SR² or at least one Y is -S-R³-W Y is at each independent occurrence selected from -(S)- v , -S-R³-W-, W is at each independent occurrence selected from oxygen or sulfur; R is at each independent occurrence selected from alkyl, alkenyl, cycloalkyl, cycloalkenyl, -R⁹-O-R¹², -R⁹-CN; R² is at each independent occurrence selected from alkyl, alkenyl, cycloalkyl, cycloalkenyl, -R³-S-R⁷, or -R³-O-R⁷; R³ is at each independent occurrence selected from alkylene of at least 2 carbon atoms, alkenylene of at least 2 carbon atoms, cycloalkylene, or cycloalkenylene; R⁴ is at each independent occurrence selected from alkylene, alkenylene, cycloalkylene, or cycloalkenylene; R⁶ is at each independent occurrence selected from a carbon-carbon bond, or R⁴; R⁷ is at each independent occurrence selected from -H or R⁸; R⁸ is at each independent occurrence selected from alkyl, alkenyl, cycloalkyl, or cycloalkenyl; R⁹ is at each independent occurrence selected from C₁ to C₄ alkylene; R¹² is at each independent occurrence selected from -H or a monovalent C₁ to C₂₀ hydrocarbon radical; R¹³ and R¹⁴ are at each independent occurrence selected from C₁ to C₂₀ alkyl or C₁ to C₂₀ alkoxy; at each independent occurrence n=1 or 2 and p=4-n; at each independent occurrence a = 1 or 2; b = 2-a; c = 1 or 2; d = 3-c; and q = O or an integer from 1 to 4 inclusive; v is at each independent occurrence selected from an integer from 1 to 8 inclusive; in that in component (B) each of said carboxyl groups is also attached, via an oxygen atom to a mono-or divalent hydrocarbon residue having from 1 to 10 carbon atoms, which may be hydroxy-substituted, and in that the weight ratio of component (A) to component (b) is in a range from 2:1 to 1:8. A composition according to claim 1 wherein component (A) also includes one or more organotin carboxylates of general formulas: (VII) R n -Sn-Z p wherein R, R₂, a, b, c, d, n, p and q are as defined in claim 1, Z is A is and r=O or an integer. A composition according to claim 2, wherein the organotin component (A) includes an alkyltin alkyl maleate. A composition according to claim 3, wherein the alkyltin alkyl maleate is dibutyltin bis(butyl maleate). A composition according to any preceding claim, wherein component (B) comprises a compound having the general formula II: where: R²⁰⁰ and R²⁰³ each have from 1 to 10 carbon atoms and are at each independent occurrence selected from alkyl, alkenyl, cycloalkyl, cycloalkenyl, multivalent hydrocarbyl group having a valence equal to z', multivalent hydroxyl substituted hydrocarbyl group having a valence equal to z', and R²⁰¹ is at each independent occurrence selected from alkylene, alkenylene, cycloalkylene, cycloalkenylene, a multivalent hydrocarbyl group and multivalent hydroxyl-substituted hydrocarbyl group; R²⁰² is at each independent occurrence selected from hydrogen, alkyl and alkylene; R²⁰⁴ is at each independent occurrence selected from hydrogen and alkyl; Z²⁰⁰ is at each independent occurrence selected from -O-, and -S-; t' is zero or an integer from 1 to 20; x' is zero or an integer from 1 to 20 with the proviso that if x'=0 or t'=0 then R²⁰⁰ is y' is an integer from 1 to 10; and z' is an integer from 1 to 4 . A composition according to claim 5, wherein the diester is diethyleneglycol bis(butyl maleate). A composition according to claim 5, wherein the diester is triethylene glycol bis(butyl maleate). A composition according to claim 5, wherein the diester is tetraethylene glycol bis(butyl maleate). A composition according to claim 5, wherein the diester is poly(diethyleneglycol maleate) bis (methyl maleate). A composition according to any one of claims 1 to 4, wherein component (B) is a diester or mixture of diesters having the formula: where R¹⁰⁰ and R¹⁰³ are the same or different and are at each independent occurrence alkyl, alkenyl, cycloalkyl, cycloalkenyl, or a multivalent hydrocarbyl or hydroxyl-substituted hydrocarbyl group; R¹⁰¹ is at each independent occurrence a carbon-oxygen bond, alkylene or alkenylene; R¹⁰² is at each independent occurrence selected from hydrogen, alkyl and alkylene; and t is an integer. A composition according to claim 10, wherein the diester is a dialkyl maleate. A composition according to claim 10, wherein the dialkyl maleate is dibutyl maleate. A composition according to any preceding claim, wherein the molar ratio of the organotin compound of component A to the diester of component B is from 1:2 to 1:6. A composition according to any preceding claim, wherein the organotin component (A) is or includes a mixture of monoalkyltin and dialkyltin mercaptides. A composition comprising a halogen-containing organic polymer and an effective amount of a stabilizer composition according to any preceding claim. A composition according to claim 14, which contains 1.0% to 5.0% of the stabilizer composition, the percentages being by weight based on the weight of the halogen-containing organic polymer.

Inventors: CONROY, GARY MARTIN, MESCH, KEITH ALAN
Applicants: MORTON INTERNATIONAL, INC.
Application year: 1985
Main classification: C08K5
IPC codes: C08L27, C08L1, C08L33, C08K5