DEWAXING CATALYSTS AND PROCESSES EMPLOYING SILICOALUMINOPHOSPHATE MOLECULAR SIEVES

Abstract: Dewaxing processes for hydrocarbon feedstocks are disclosed using novel catalysts comprising specific silicoalu­ minophosphates of U.S. Patent No. 4,440,871. The products of the instant dewaxing processes are characterized by lower pour points than the hydrocarbon feedstock.

Description: DEWAXING CATALYSTS AND PROCESSES EMPLOYING SILICOALUMINOPHOSPHATE MOLECULAR SIEVES FIELD OF THE INVENTION The present invention relates to dewaxing and hydrodewaxing catalysts comprising silicoaluminophosphate molecular sieves, as hereinafter described, and to processes employing such catalysts. BACKGROUND OF THE INVENTION Dewaxing and hydrodewaxing processes are employed in the refining industry to treat petroleum fractions having initial boiling points over about 3500F. to improve their pour point. The improvement in pour point is generally effected by selective removal of paraffinic hydrocarbons. Since the pour point of liquid hydrocarbon fuels, e.g., diesel fuels and other light gas oil fractions, are strictly controlled, the pour point specification of such fuels must be met if such are to be employed in their intended use. The need to reduce the pour point of petroleum fractions has resulted in the development of numerous dewaxing, and hydrodewaxing processes wherein the pour points of petroleum fractions are reduced by selective removal of paraffinic hydrocarbons. Processes relating to dewaxing and hydrodewaxing are well known in both the patent and scientific literature. Such processes have employed crystalline aluminosilicates as catalysts. For example, see U.S. patent Nos. 3,140,249, 3,140,252, 3,140,251, 3,140,253, 3,956,102 and 4,440,991. These and other patents disclose the use of various crystalline aluminosilicates as catalysts for dewaxing processes. Although a large number of zeolite materials have been disclosed as employable as catalysts for dewaxing and hydrodewaxing catalysts, the use of other crystalline molecular sieves has not received attention. This lack of attention is attributable to the scarcity of molecular sieves other than crystalline aluminosilcates. One disclosure of a catalyst containing a crystalline silicate, as opposed to a crystalline aluminosilicate, is disclosed in U.S. Patent No. 4,441,991. The instant invention provides for catalytic dewaxing and hydrodewaxing of hydrocarbon feedstocks by contacting such with catalysts comprising silicoaluminophosphate molecular sieves, as hereinafter described BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a plot of the pour point (OF) as a function of conversion of Catalyst A (SAPO-ll) and comparative Catalyst C (SAPO-34). FIG. 2 is a plot of the pour point (OF) as a function conversion of Catalyst B (SAPO-31) and comparative Catalyst C (SAPO-34). SUMMARY OF THE INVENTION The present invention relates to catalytic dewaxing and hydrodewaxing (hereinafter jointly referred to as "dewaxing") processes and the catalysts employed in such processes. The catalysts comprise: 1) at least one silicoaluminophosphate molecular sieve, as hereinafter described; and 2) optionally, and in the instance of hydrodewaxing at least one hydrogenation component. The catalyst of this invention may optionally contain particles of a traditional dewaxing catalyst having catalytic activity for dewaxing and/or hydrodewaxing hydrocarbon feedstocks at effective dewaxing conditions, e.g., particles of a traditional dewaxing catalyst containing a zeolitic aluminosilicate(s) of the type generally employed in such dewaxing catalysts. The silicoaluminophosphate molecular sieves employed in the instant invention, i.e., catalysts and processes, are disclosed in U.S. Patent No. 4,440,871 and as characterized in their calcined form by an adsorption of isobutane of at least 2 percent by weight at a partial pressure of 500 torr and a temperature of 20"C. The traditional dewaxing catalyst component, e.g., a zeolitic aluminosilicate, if any, is characterized as being a dealing catalyst component, such as heretofore traditionally employed in dewaxing processes, e.g., the varicus forms of zeolite Y, silica-alumina, and hydrogenation components. The silicoaluminophosphate molecular sieves employed in this invention are unique in that such are not zeolitic aluminosilicates, as heretofore employed in the prior art, but are specific silicoaluminophosphate molecular sieves, as hereinafter described. DETAILED DESCRIPTION OF THE INVENTION Dewaxing and hydrodewaxing processes involve converting high boiling and high pour point paraffinic waxes and hydrocarbons to lower boiling and lower pour point products. Further, hydrodewaxing involves hydrogenating unsaturates in the product. The term "dewaxing" is employed herein to generally mean the removal of hydrocarbons which readily solidify from petroleum stocks as waxes and includes catalytic dewaxing and hydrodewaxing. The catalysts of the instant invention have been observed to convert normal paraffins in the hydrocarbon products and, accordingly, reduce the pour point of such products, i.e., act as dewaxing catalysts. This reduction in the pout point by selective normal paraffin conversion is of commercial significance since distillate products have rigid specifications on the acceptable pour point. The silicoaluminophosphste molecular sieves employed in the instant invention are selected from the hereinafter described group of silicoalumino phosphste molecular sieves as being characterized in their calcined form by an adsorption of isobutane of at least 2 percent by weight at a partial pressure of 500 torr and a temperature of 200C. The silicoaluminophosphate molecular sieves are preferably also characterized in their calcined form by an adsorption of triethylamine of from zero to less than 5 percent by weight, preferably less than 3 percent by weight, at a partial pressure of 2.6 torr and a temperature of 22 C - SilicoaluminoPhosPhste Molecular Sieves The silicoaluminophosphate molecular sieves of U.S. Patent No. 4,440,871 (referred to therein as "SAPOs") are microporous crystalline silicoaluminophosphates, the pores of which are uniform and have nominal diameters of greater than about 3 Angstroms and whose essential empirical chemical composition in the as-synthesized and anhydrous form is mR:(SiXAlyPz)O2 wherein "R" represents at least one organic templating agent present in the intracrystailine pore system; "m" represents the moles of "R" present per mole of (SiXAlyPz)O2; "m" has a value of from 0.02 to 0.3; "x", "y" and "z" represent the mole fractions of silicon, aluminum and phosphorus respectively, present as tetrahedral oxides, said mole fractions being such that they are within the pentagonal compositional area defined by points ABCD and E of the ternary diagram which is FIG. 1 of the drawings of U.S. Patent No. 4,440,871. The SAPO molecular sieves of U.S. Patent No. 4,440,871 are also described as silicoaluminophosphates having a three-dimensional microporous framework structure of PO2, A102 and SiO2 tetrahedral units, 2 and whose essential empirical chemical composition on an anhydrous basis is: mR:(SixAlyPz)O2 wherein eRe represents at least one inorganic templating agent present in the intracrystalline pore system; wm" represents the moles of "R" present per mole of (Si AlyP,)O, and has a value of from zero to 0.3; ; "x", 'y" and "z" represent respectively, the mole fractions of silicon, aluminum and phosphorus present in the oxide moiety, said mole fractions being within the compositional srea bounded by points A, B, C, D and E on the ternary diagram which is FIG. 1, said silicoaluminophosphate having a characteristic X-ray powder diffraction pattern which contains at least the d-spacings set forth below in any one of Tables I, III, V, VII, IX, XII, XVII, XXI, XXIII or XXV of U.S. Patent No. 4,440,871. Further, such crystalline silicoaluminophosphates may be calcined at a temperature sufficiently high to remove at least some of any organic templating agent present in the intracrystalline pore system. The silicoaluminophosphates of U.S. Patent No. 4,440,871 are generally referred to therein as "SAPO-n", as a class, or as "SAPO-n" wherein "n" is an integer denoting a particular SAPO as its preparation is reported in U.S. Patent No. 4,440,871. SAPO CATALYSTS The specific SAPOs employed in the instant invention are characterized in their calcined form by an adsorption of isobutane of at least 2 percent by weight at a partial pressure of 500 torr and a temperature of 200C. The SAPO's are preferably also characterized in their calcined form by and adsorption of triethylamine of less than 5 percent by weight at a partial pressure of 2.6 torr and a temperature of 22"C. SAPOs characterized by the above described adsorption of isobutane include, but are not limited to, SAPO-5, SAPO-li, SAPO-31, SAPO-37, SAPO-40, SAPO-41, and mixtures thereof. The above characterization of the SAPOs employed in the instant invention relates to an adsorption characterization that is carried out on a SAPO which has been subjected to a post synthesis treatment, e.g., calcination or chemical treatment, to remove a substantial portion of the template nR" which is present as a result of synthesis. Although a particular SAPO is characterized herein by reference to its adsorption of isobutane or triethylamine as relating to the adsorption character- is tics of the SAPO in its calcined form1 the instant invention necessarily includes the use of a non-- calcined or modified SAPOs which are characterized by such adsorption in the modified or calcined form, since upon use of such a non-calcined SAPO in the instant process at effective dewaxing conditions the SAPO will be calcined or hydrothermally treated in situ so as to have the characteristic adsorption of isobutane or triethylamine. Thus, the SAPO will be rendered in situ to a form characterized by the aforementioned adsorption characteristics. For example, an as-synthesized SAPO-ll is not character- ized by the aforementioned adsorption of isobutane due to the presence of template "R" which is present as a result of synthesis, although the calcined form of SAPO-ll is characterized by the aforementioned adsorption of isobutane. Thus, reference to a SAPO having a particular adsorption characteristic in its calcined form is not intended to exclude the use of the SAPO in its as-synthesized form which upon in-situ calcination, hydrothermal treatment and/or other treatment, e.g., ion exchange with suitable atoms, would have such adsorption characteristics. The SAPOs of the instant invention may be employed in conjunction with traditional dewaxing catalysts and hydrocracking catalysts and accordingly, optionally, a zeolitic aluminosilicate component may be employed in conjunction with the SAPO-contsining catalysts. The zeolitic aluminosilicate component of such catalysts may be any aluminosilicate heretofore employed as a component in dewaxing catalysts. Representatives of the zeolitic aluminosilicates disclosed heretofore as employable as component parts of traditional dewaxing catalysts are Zeolite Y, steam stabilized Zeolite Y (ultra-stable Y), Zeolite X, Zeolite beta (U.S. Patent No. 3,308,069), Silicalite (U.S. Patent No. 4,061,724),, Zeolite KZ-20 (U.S. Patent No. 3,445,727), Zeolite ZSM-3 (U.S. Patent No. 3,415,736), faujasite, LZ-10 (U.K. Patent 2,014,970, June 9, 1982), US-Y, ZSM-type zeolites, erionite, mordenite, offretite, chabazite, FU-l-type zeolite, NU-type zeolites and mixtures thereof. Traditional dewaxing catalysts containing amounts of Na2O less than about one percent by weight are generally preferred. Zeolite Y is disclosed in U.S. Patent Nos.: 3,130,007; and steam stabilized Y Zeolites, e.g., ultra-stable Y-type zeolites. Another zeolitic aluminosilicate employable herein is "LZ-210", is described in E.P.C. Publication No. 82,211 published June 29, 1983, incorporated herein by reference thereto. In one embodiment the hydrocracking catalyst disclosed in copending,U.S. Serial No. 490,951, filed May 2, 1983, incorporated herein by reference, may be employed as an optional LZ-210 containing hydrocracking component. The term "ZSM-type" zeolites is generally employed in the art to refer to those zeolites denominated by the nomenclature "ZSM-n" where Zn" is an integer. The ZSM-type aluminosilicates include but are not limited to ZSM-5, ZSM-ll, ZSM-12, ZSM-23, ZSM-35, ZSM-38, ZSM-48; and other similar materials. ZSM-5 is described in greater detail in U.S. Patent No. 3,702,886 and Re 29,948. The entire descriptions contained within those patents, particularly the X-ray diffraction pattern of therein disclosed ZSM-5, are incorporated herein by reference. ZSM-ll is described in U.S. Patent No. 3,709,979. That description, and in particular the X-ray diffraction pattern of said ZSM-ll, is incorporated herein by reference. ZSM-12 is described in U.S. Patent No. 3,832,449. That description, and in particular the X-ray diffraction pattern disclosed therein, is incorporated herein by reference. ZSM-23 is described in U.S. Patent No. 4,076,842. The entire content thereof, particularly the specification of the X-ray diffraction pattern of the disclosed zeolite, is incorporated herein by reference. ZSM-35 is described in U.S. Patent No. 4,016,245. The description of that zeolite, and particularly the X-ray diffraction pattern thereof, is incorporated herein by reference. ZSM-38 is more particularly describing U.S. Patent No. 4,046,859. The description of that zeolite, and particularly the specified X-ray diffraction pattern hereof, is incorporated herein by reference. ZSM-48 is more particularly described in U.S. Patent No. 4,423,021. The description of that zeolite, and particularly the specified X-ray diffraction pattern thereof, is incorporated herein by reference. In addition, crystalline silicates such as silicalite (U.S.Patent No. 4,061,724) may be employed with the SAPOs of the instant invention. FORMULATION OF DEWAXING CATALYSTS The catalysts of the instant invention comprise at least one SAPO, as above characterized, and optionally, may also contain a hydrogenation catalyst and optionally, one or more traditional dewaxing or hydrocracking catalysts, including zeolitic aluminosilicate components. The relative amount of the SAPO component or traditional dewaxing component, if any, will depend at least in part, on the selected hydrocarbon feedstock and on the desired pour point of the product, but in all instances an effective amount of at least one SAPO is employed. When a zeolitic aluminosilicate is employed as a part of the traditional dewaxing component the relative weight ratio of the zeolitic aluminosilicate to the SAPO is generally between about 1:10 and about 500:1, desirably between about 1:10 and about 200:1, preferably between about 1:2 and about 50:1, and most preferably is between about 1:1 and about 20:1. The zeolitic aluminosilicate and SAPO may be ion-exchanged with a selected cation(s) and/or thermally treated either before or after mixture with each other or after such have been added separately or concurrently to one or more inorganic oxide matrix components. When the SAPO molecular sieves are ion exchanged such are preferably exchanged with a hydrogen-forming cation species, e.g. NH4, H , quaternary ammonium cations, etc. The SAPO preferably has at least part of its cations as hydrogen-forming cation species. Hydrodewaxing catalysts may optionally contain a hydrogenation component of the type commonly employed in dewaxing catalysts. The hydrogenation component may be selected from the group of hydrogenation catalysts consisting of one or more metals of Group VI B and Group VIII, including the salts, complexes and solutions containing such metals. The preferred hydrogenation catalyst is at least one of the group of metals1 salts and complexes selected from the group consisting of at least one of platinum, palladium, rhodium, iridium and mixtures thereof or at least one from the group consisting of nickel, molybdenum, cobalt, tungsten, titanium, chromium and mixtures thereof. As recognized in the art, the noble and base metals will not generally be employed in the same catalyst system. Reference to the catalytically active metal or metals is intended to encompass such metal or metals in the elemental state or in some form such as an oxide, sulfide, halide, carboxylate and the like. The hydrogenation component is present in an effective amount to provide an effective hydrodewaxing catalyst. When the hydrogenation catalysts is a noble metal it is generally present in an amount between about 0.055 and about 1.55 by weight based on the total weight of the dewaxing catalyst including the weight of any binder or matrix material which may be present, as hereinafter discussed, although effective amounts outside this range may be employed. Although effective amounts in excess of 1.5 percent by weight may be employed, the preferred effective amount of the noble metal hydrogenation component is between about 0.35 and about 1.21 by weight. When the hydrogenation catalyst is a base metal(s) the effective amount will generally be between about 1,OI and about 305 percent by weight or more of the base metal, expressed as the oxide(s), based on the total weight of the dewaxing catalyst, although effective amounts outside this range may be employed. The final form of the hydrogenation component is not narrowly limited herein but may be a metal oxide, metal sulfide or other catalytically active form. Since sulfur is typically present in the hydrocarbon feedstock being treated, the actual form of some of the hydrogenation component(s) may well be at least in part a sulfide due to in situ reactions. When a noble metal is employed as the hydrogenation component the catalyst is generally activated in air and then reduced in a hydrogen atmosphere. When base metals are employed such are usually treated with a sulfur compound. The hydrogenation components can be incorporated into the overall catalyst composition by any one of numerous procedures. In general it has been observed that it is desirable to add the hydrogenation component to the catalyst as a separate component rather than provide such by ion exchange or impregnation of the SAPO component. They can be added either to the SAPO component, zeolitic aluminosilicate component, if any, or to any metal oxide or to a combination thereof by ion exchange, impregnation, occulsion and the like. In the alternative, multiple hydrogenation components (two or more) may be added as powders in the formulation of the catalyst. They may be added by co-mulling, impregnation, or ion exchange whereby one or more may be added to SAPO and/or zeolitic aluminosilicate by impregnation, co-mulling or co-precipitation. For example, noble or base metal compounds, such as the sulfides, oxides or water-soluble salts, can be added by co-mulling, impregnation or precipitation before the composite is finally calcined. In the alternative these components can be added to the finished particle by impregnation with an aqueous, alcoholic, hydrocarbon or other nonaqueous solution of soluble compounds or precursors. Although the hydrogenation components can be combined with the SAPO and/or zeolitic aluminosilicate, if any, as the oxides such is generally not the case. They are usually added as a metal salt which can be thermally converted to the corresponding oxide in an oxidizing atmosphere or reduced to the metal with hydrogen or other reducing agent. The composition can be sulfided by reaction with a sulfur donor such as carbon disulfide, hydrogen sulfide, hydrocarbon thiols, elemental sulfur, and the like, described above. The above oxidizing or sulfiding processes are generally carried out on catalyst compositions which have been partially dried (as desired), tableted, pelleted, extruded (with binder or matrix), or formed by other means and then calcined, e.g., at a temperature above 6000F, usually above 8000F. It is well known in the art that dewaxing catalysts, are generally employed with a binder material or, as commonly referred to, with an inorganic oxide matrix which can be inert or also catalytically active. For example inorganic matrices such as silica, alumina, silica-alumina, silica-zirconia, silica-magnesia, alumina-boria, alumina-titania and the like and mixtures thereof may be employed An inorganic oxide need not always be employed such as in the case of 8 preform containing the SAPO or may be employed in an amount between about lX and about 951. by weight, preferably between about 101 and about 805 by weight, based on the total weight of the dewaxing catalyst. The term "crude oil feedstock" is used herein to denominate any crude oil feedstock or portion thereof and includes full range crude oils from primary, secondary or tertiary recovery from conventional or offshore oil fields and to the myriad of feedstocks derived therefrom. "Crude oil feedstocks" may also be "syncrudes" such as those that can be derived from coal, Fisher Tropsch fuel products, shale oil, tar sands and bitumens. The crude oil feedstock may be virgin (straight run) or generated synthetically by blending. Such crude oil feedstocks are traditionally desalted prior to use since sodium chloride is known to be a poison in many dewaxing operations. Further, the term "crude oil feedstocks" is intended to include component parts of crude oils which have heretofore been generally employed as feedstocks or potential feeds and includes feeds such as distillate gas oils, heavy vacuum gas oils, VGO, atmospheric and vacuum resids, syncrudes, pulverized coal and fractions boiling above the traditional end of the gasoline boiling range which generally includes compounds containing greater than about eleven carbon atoms and combinations thereof. The hydrocarbon feedstock for dewaxing typically boils above 3500F, preferably between about 400OF and 1200OF and more preferably between about 4000F and about 900OF. The hydrocarbon feedstock may be pre-treated in a hydrotreater to reduce, i.e. remove, compounds which contain sulfur and/or nitrogen. The hydrocarbon feedstock may have a significant sulfur content, present as hydrogen sulfide, ranging from 0.1 to 3 weight percent, and nitrogen content, present as ammonia, in an amount up to 20,000 ppm. Temperature, space velocity, and other process variables may be adjusted to compensate for the effects of nitrogen on the dewaxing catalyst activity. The feedstock is contacted in the dewaxing reaction zone with the dewaxing catalyst and, optionally, in the presence of hydrogen- containing gas and/or a hydrogen generating compound. In hydrodewaxing, hydrogen is consumed in the hydrodewaxing process and an excess of hydrogen is typically maintained in the reaction zone. Advantageously, a hydrogen-to-oil (feed) ratio of at least 1,000 standard cubic feet of hydrogen per barrel of feed (SCFB) is employed, and the hydrogen-to-oil ratio may range up to 20,000 SCFB. Preferably, about 4,000 to 12,000 SCFB is employed. Typically dewaxing and hydrodewaxing conditions are disclosed in U.S. Patent No. Re 28,398, U.S. Patent No. 3,852,189 and U.S. Patent No. 4,282,085. The instant process is carried out under effective catalystic dewaxing or hydrodewaxing conditions. Catalytic dewaxing is generally carried out at a LHSV (liquid hourly space velocity) between about 0.2 and about 50, a temperature between about 5000F and about 12000F, a pressure between about subatmospheric and about 500 atmospheres. Hydrodewaxing is generally carried out at a LHSV between about 0.1 and about 15. a temperature between about 4000F and about 9000F, st a pressure between about 10 psig and about 2500 psig and using molar ratios of hydrogen to hydrocarbon feedstock between about 1 and about 100. The following examples were carried out to demonstrate the use of the dewaxing catalysts and dewaxing processes of the invention and are not intended to be limiting thereof. Examples 1 to 3 Three catalysts were prepared for evaluation as dewaxing catalysts and were denominated Catalysts A, B and C. All weights are given as anhydrous weights unless otherwise designated. The catalysts were prepared as follows: a) Catalyst A is a catalyst according to the invention and was prepared using SAPO-Il. SAPO-ll was prepared according to example 17 of U.S. Patent No. 4,440,871, except that the digestion time was 24 hours. Catalyst A was prepared by blending 80 grams of SAPO-1l with 80 grams of a nickeltungsten-alumina catalyst, 100 grams of a silica solution (40 percent by weight silica in water) and an ammonium acetate solution (4 grams of ammonium acetate in 70 cubic centimeters (cc) of water). The mixture was extruded as 1/16 inch extrudates and dried at 1000C for about 16 hours and calcined in air at 5000C for 2 hours. The calcination at 5000C was carried out in a stepwise manner by heating the catalyst from room temperature to 220"C over a one hour period, heating the catalyst at 2200C for 1.5 hours, heating the catalyst from 220"C to 500 C over a one hour period and then heating the catalyst at 5000C for 2 hours. The nickel-tungsten-alumina hydrogenation component was prepared by pore filling 85 grams of a pseudoboehmite alumina with an aqueous solution (119 cc) containing 31.5 grams of Ni(N03)e6H20 and 33.7 grams ammonium metatungstate. The mixture was dried as above described for Catalyst A except the final temperature was 4800C instead of 5000C. Catalyst A, expressed as the weight percent oxides, was prepared to be: 355 SAPO-Il, 35S Al2O3, 175 SiO2, 31. Ni0 and 105 W03. Chemical analysis of Catalyst A for NiO and WO3 gave 2.8 wt.1. NiO and 9.6 wt.S WO3. b) Catalyst B was prepared according to this invention using a SAPO-31 prepared according to example 51 of U.S. Patent No. 4,440,871. SAPO-31 (72 grams) was blended with 46.5 grams of an aqueous silica solution (40 wt.% silica). The mixture was extruded into 1/16 inch pellets which were dried at 1000C and calcined at 5000C, by the procedure above described for Catalyst A. The calcined extrudates were treated in air (saturated with water at 25QC) at 6500C for three hours. The chemical composition of the catalyst was prepared to be 80 wt.X SAPO-31 and 20 wt.S Si02. c) Catalyst C is a comparative catalyst and was prepared using SAPO-34. SAPO-34 was prepared according to the procedure of examples 32 to 38 of U.S. Patent No. 4,440,871. SAPO-34 is not characterized by an isobutane adsorption of at least 2 percent by weight at a partial pressure of 500 torr and a temperature of 200C whereas SAPO 11 and SAPO-31 are so characterized. Catalyst C was prepared by mixing 30 grams of SAPO-34 with 50 grams of an alumina sold under the trade designation "PA" by American Cyanamide, Stamford, CT.), and 20 grams of a pseudoboehmite alumina. The above mixture was mixed with 3 cc of concentrated nitric acid and 50 cc of water and extruded as 1/16 inch extrudates. The extrudates were dried at 1000C and calcined at 500to. by the procedure above described for Catalyst A. The extrudates (53 grams) were pore filled by mixing them with a solution (35 cc) containing 10.7 grams of Ni(N03)2.6H20 and 20.9 grams of ammonium metatungstate. The extrudates were then dried at 5000C. as above described for Catalyst A. Catalyst C expressed as the weight percent oxides, was prepared to give: 3.51. NiO, 225 W03, 22.42 SAPO-34 and 52.25 alumina. Example 4 The catalysts of examples 1 to 3 were evaluated for hydrodewaxing and their use in reducing the pour point of hydrocarbon feedstocks by contacting a selected feedstock with hydrogen at a total pressure of 2000 psig at a Liquid Hourly Space Velocity (LHSV) between 0.25 to 0.8 and a hydrogen flow rate of 10,000 SCFB (Standard Cubic Feet per Barrel) at temperatures between about 7000F and 8000F. Products boiling below 6000F were collected and evaluated and the conversion given based on these products. The feedstock employed in the dewaxing examples set forth hereinafter was a vacuum gas oil having an IBP (Initial Boiling Point) of 5600F and a FBP (Final Boiling Point) of 1148OF (both determined by ASTM test method D-2887), API Gravity of 22.3 and having a pour point of greater than 95OF. The feedstock was characterized by the following physical and chemical characteristics: : Weight Percent Paraffins 24.1 Mono-nsphthenes 9.5 Poly-naphthenes 8.7 Mono-aromatics 13.3 Di -aromatics 9.3 Tri-aromatics 4.3 Tetra-aromatics 2.7 Penta-aromatics 0.7 The reactor effluents were collected and the fraction of the feed ("Conversion" on a weight basis) converted to products boiling below 6000F determined by simulated distillation (ASTM test method D-2887). The conversion is reported as the weight percent of feedstock converted to products boiling below 6000F. The pour points were determined by ASTM test method D-97-66 on the reactor effluents after maintaining the effluent at about 1300F during its colletion. The results in Tables A, B, C and D demonstrate that at comparable conversions that Catalysts A and B provided a reduction in the pour point of the products superior to that obtained by use of Catalyst C. The data in Tables A and C are graphically depicted in FIG. 1 and show the decrease in pour point as a function of conversion of products obtained using SAPO-il (Catalyst A) as compared to SAPO-34 (Catalyst C). The data in Tables B and D are graphically depicted in FIG. 2 and show the decrease in pour point as a function of conversion of products obtained using SAPO-31 (Catalyst B) as compared to SAPO-34 (Catalyst C). FIGS. 1 and 2 demonstrate the decrease in the pour point of the products obtained by Catalyst A and B as compared to Catalyst C. Further, the decrease in pour point increases at a greater rate using Catalysts A and B with increasing conversion, indicating Catalysts A and B are more selective dewaxing catalysts. TABLE A (CATALYST A) Temp,, OF LHSV Conv. Pour Point. OF 701 0.25 17.3 40 749 0.25 39.8 -15 725 0.25 28.5 10 TABLE B (CATALYST B) Temp., OF LHSV Conv. Pour Point. OF 725 1.0 4.3 75 749 1.0 6.9 65 772 1.0 13.0 50 801 1.0 26.5 25 TABLE C (CATALYST C) Temm OF LHSV Conv. Pour Point. OF 702 0.25 17.6 85 725 0.25 23.3 80 750 0.25 35.0 75 774 0.25 47.1 60 TABLE D (CATALYST C) Temw OF LHSV Conv. Pour Point, OF 776 1.0 29.9 80 753 1.0 18.1 85 752 1.0 17.0 85 EXAMPLE 5 A catalyst was prepared employing SAPO-ll to demonstrate the hydrocracking and dewaxing functionality of the catalysts of this invention SAFO-11 was prepared according to the procedure described in example 18 of U.S. Patent No. 4,440,871, except the final molar ratio of di-n-propylamine to A1203 was 1.0 to 1. The catalyst was prepared by mixing 150 grams of SAPO-Il with 100 grams of Kaiser medium density alumina and a sufficient amount of water to form an extrudste mixture (paste). The mixture was extruded into 1/16 inch extrudates and dried in air at 1000C for 16 hours. The extrudates were then calcined in air at 480 C for 2 hours. The extrudates (153 gram) were then mixed (pore filled) with 150 cc of an aqueous solution containing 40.0 grams of nickel nitrate hexahydrate and 48.8 grams of ammonium metatungstate. The mixture was then dried for 16 hours at 1000C and then calcined at 4800C for 2 hours. The catalyst was prepared to contain, given as the weight percent oxide: 5 wt. 1. NiO; 23 wt. 1. WO3; 36 wt. S SAPO-ll; and 365 Awl203. Chemical analysis for NiO and W03 gave 5.4 wt. 1. NiO and 23.0 wt. 1. W03. The catalyst was evaluated by contacting a selected feedstock with hydrogen at a total pressure of 2000 psig at a Liquid Hourly Space Velocity (LHSV) of one and a hydrogen flow rate of 10,000 SCFB (Standard Cubic Feed per Barrel) at temperatures between about 7000F and 8400F. Products boiling below 6000F were collected and evaluated and the conversion given based on these products. The feedstock employed in this example was a vacuum gas oil having an IBP (Initial Boiling Point) of 560OF and a FBP (Final Boiling Point) of 1148OF (both determined by ASTM test method D-2887), API Gravity of 22.3 and having a pour point of greater than 950F. The feedstock was characterized by the following physical and chemical characteristics: Weight Percent Paraffins 24.1 Mono-naphthenes 9.5 Poly-naphthenes 8.7 Mono-aromatics 13.3 Di-aromatics 9.3 Tri-aromatics 4.3 Tetra-aromatics 2.7 Penta-aromatics 0.7 The products of each evaluation were collected and the fraction of the feed (weight basis) converted to products boiling below 6000F determined by simulated distillation. The conversion is reported as the weight percent of feedstock converted to products boiling below 6000F. The pour points were determined according to ASTM test method D-97-66 as in example 4. The conversion and pour point were as follows: TemPerature (OF) Conversion Pour Point ( F) 700 7.52 85 724 9.84 80 749 17.95 70 769 30.06 55 788 41.60 25 797 36.64 35 788 29.89 40 788 33.74 45 807 43.64 30 821 45.12 30 822 45.50 30 840 56.88 20 The above data demonstrate the conversion of the higher boiling feedstock to lower boiling products in the presence of hydrogen and that such products are characterized by a lower pour point than the initial feedstock.

Claims: WHAT IS CLAIMED IS: 1. The process for dewaxing a hydrocarbon feedstock comprising contacting the hydrocarbon feedstock at effective dewaxing conditions with a dewaxing catalyst comprising an effective amount of at least one silicoaluminophosphate (SAPO) of U.S. Patent No. 4,440,871 characterized in its calcined form by an adsorption of isobutane of at least 2 percent by weight at a pressure of 500 torr and a temperature of 200C. 2. The process for hydro-dewaxing a hydrocarbon feedstock to reduce its pour point comprising contacting the hydrocarbon feedstock with a catalyst in the presence of hydrogen at effective hydro-dewaxing conditions wherein the catalyst comprises at least one hydrogenation component and at least one SAPO characterized in its calcined form by an adsorption of isobutane of at least 2 percent by weight at a pressure of 500 torr and a temperature of 200C. 3. The process of claim 1 or claim 2 wherein said SAPO is further characterized in its calcined form by an adsorption of triethylamine of from zero to less than 5 percent by weight at a pressure of 2.6 torr and a temperature of 22"C. 4. The process of claim 3 wherein said adsorption of triethylamine is less than 3 percent by weight. 5. The process of claim 1 or claim 2 wherein said catalyst contains an effective amount of at least one zeolitic aluminosilicate having activity wherein said zeolitic aluminosilicate is present in a weight ratio between about 1:10 and about 500:1 of said zeolitic aluminosilicate to said SAPO molecular sieve. 6. The process of claim 5 wherein the weight ratio of zeolitic aluminosilicate to said SAPO is between about 1:2 and about 50:1. 7. The process of claim 6 wherein the weight ratio of zeolitic aluminosilicate to said SAPO is between about 1:1 and about 20:1. 8. The process of claim 1 or 2 wherein said catalyst comprises an inorganic oxide matrix component present in an amount between about 0 and about 99 percent by weight, based on the total weight of said catalyst. 9. The process of claim 8 wherein said inorganic oxide matrix component is present in an amount between about 5 and about 9S percent by weight. 10. The process of claim 1 or claim 2 wherein said SAPO has at least part of its cations as hydrogen-forming species. 11. The process of claim 10 wherein said hydrogen-forming species is N < or H+ 12. The process of claim 1 wherein the process is carried out by contacting a hydrocarbon feedstock boiling between 400OF and about 12000F with said catalyst at a temperature between about 5000F and about 1200OF, at a pressure between about subatmospheric to about 500 atmospheres and a LHSV between about 0.2 an about 50. 13. The process of claim 2 wherein the process is carried out by contacting a hydrocarbon feedstock boiling between about 400OF and about 1200OF., in the presence of hydrogen with said catalyst at a temperature between about 4000F and about 900OF., at a pressure between about 10 psig. and about 2500 psig., and at a molar ratio of hydrogen to hydrocarbon feedstock between about 1 and about 100. 14. The process of claim 4 wherein said zeolite aluminosilicate is ZSM-5. 15. The process of 9 wherein said inorganic oxide matrix component is selected from the group consisting of clays, silicas, aluminas, silica-aluminas, silica-zirconias, silica-magnesia, alumina-borias, alumina-titanias and mixtures thereof. 16. The process of claim 1 or claim 2 wherein said SAPO is selected from the group consisting of SAPO-5, SAPO-11, SAPO-31, SAPO-37, SAPO-40, SAPO-41 and mixtures thereof. 17. The process of claim or claim 2 wherein said hydrocarbon feedstock is selected from the group consisting of heating fuel, jet fuel, lube oils, distillate gas oils, naphta, reformate, kerosene, diesel fuel, heavy vacuum gas oils, Fischer Tropsch reaction products, VGO, atmospheric resids, vacuum resids, syncrudes, pulverized coal and mixtures thereof. 18. The process oF claim 4 wherein said zeolitic aluminosilicate is selected from the group consisting of zeolite Y, ultra-stable Y-type zeolites, zeolite X, zeolite beta, silicalite, zeolite KZ-20, faujasite, LZ-210, LZ-10, ZSM-type zeolites and mixtures thereof. 19. The process according to claim 2 wherein the hydrogenation catalyst is at least one metal selected from the group consisting of Pt, Pd, Rh, Ru, Ni, W, Mo, Co, Ti, Cr and mixtures thereof. 20. The process of claim 19 wherein said metal is selected from the group consisting of Pt, Pd, Rh,Ru and mixtures thereof and is present in an effective amount between about 0.05 weight percent and about 1.S weight percent. 21. The process of claim 19 wherein the metal is selected from the group consisting of Ni, W, Mo, Co, Ti, Cr and mixtures thereof and is present in an amount between about 1.0 and about 30 percent by weight. 22. A catalyst comprising at least one SAPO characterized in its calcined form by an adsorption of isobutane of at least 2 percent by weight at a pressure of 500 torr and a temperature of 200C wherein the weight ratio between said aluminosilicate and SAPO is between about 1:10 and about 500;1, and at least one metal selected from the group consisting of nickel, cobalt, tungsten, molybdenum, platinum, palladium, chromium, rhodium, ruthenium and titanium. 23. The catalyst of claim 22 wherein said SAPO molecular sieve is further characterized in its calcined form by an adsorption of triethylamine of from zero to less than 5 percent by weight at a pressure of 2.6 torr and a temperature of 220C. 24. The catalyst of claim 22 or claim 23 wherein said catalyst contains at least one zeolitic aluminosilicate selected from the group consisting of zeolite Y, ultra-stable Y zeolite, zeolite X, silicalite zeolite beta, zeolite KZ-20, faujasite, LZ-210, LZ-10, ZSM-type zeolites and mixtures thereof. 25. The catalyst of claim 24 wherein said catalyst contains from 1 to 99 percent by weight of at least inorganic oxide matrix component. 26. The catalyst of claim 25 wherein the inorganic oxide matrix component is selected from the group consisting of clays, silicas, aluminas, silica-aluminas, silica-zirconias, silica-magnesia, alumina-borias, alumina-titantas and mixtures thereof. 27. The catalyst of claim 22 or claim 23 wherein said SAPO is selected from the group consisting of SAPO-5, SAPO-il, SAPOt31, SAPO-37, SAPO-40, SAPO-41 and mixtures thereof. 28. The catalyst of claim 27 wherein said zeolitic aluminosilicate is selected from the group consisting of Y zeolite, ultra-stable Y-type zeolite, LZ-210, LZ-10, silicalite and ZSM-5 and mixtures thereof.

Inventors: GORTSEMA, FRANK PETER, LONG, GARY NORMAN, PELLET, REGIS JOSEPH, RABO, JULE ANTHONY, SPRINGER, ALBERT RAYMOND
Applicants: UNION CARBIDE CORPORATION
Application year: 1985
Main classification: C10G45
IPC codes: C10G73, C10G45, B01J29