CRACKING CATALYSTS AND PROCESS USING NON-ZEOLITIC MOLECULAR SIEVES

Abstract: Cracking catalysts and their use in cracking processes. The cracking catalyst is prepared using novel non-zeolitic molecular sieves and, optionally, traditional zeolitic aluminosilicate cracking components.

Description: Cracking catalysts and process using non-zeolitic molecular sieves. FIELD OF THE INVENTION The present invention relates to cracking catalysts derived from novel non-zeolitic molecular sieve compositions. The novel catalysts are employed in cracking processes to provide product mixtures substantially more valuable than products obtained by use of zeolite-based cracking catalysts. BACKGROUND OF THE INVENTION The prior art dealing with catalytic cracking catalysts has in large part evolved by the preparation of * modified zeolites for use as components in cracking catalysts. The following patents are representa ive of the prior art dealing with zeolites and matrices. The use of conversion catalysts formed from a zeolite dispersed in a siliceous matrix has been disclosed in U.S. Pat. No. 3,140,249 and U.S. Pat. No. 3,352,796. The use of blended matrix components, e.g., a catalyst comprising a zeolite, an inorganic oxide matrix and inert fines, which may be alpha alumina, is disclosed in U.S. Pat. No. 3,312,615. Catalysts comprising an amorphous silica-alumina, separately added alumina and a zeolite are disclosed in U.S. Pat. No. 3,542,670 and catalyst comprising a zeolite, ah amorphous hydrous alumina and alumina monohydrate are disclosed in U.S. Pat. No. 3,428,550. It has been disclosed that the steam and thermal stability of Y zeolites can be improved by the use of zeolites having a low level of alkali metal content and a unit cell size less than about 24.45 Angstroms (See: U.S. Pat. Nos. 3,293,192 and Re. 28,629 (Reissue of U.S. Pat. No. 3,402,996)). Further, it has been disclosed (U.S. Pat. No. 3,591,488) that the hydrogen or ammonium form of a zeolite may be treated with H 2 O at a temperature ranging from about 800° -to about 1500°F, and then subsequently cation exchange the steam and water treated zeolite with cations which may be rare earth metal cations. U.S. Pat. No. 3,676,368 discloses a rare earth exchanged-hydrogen faujasite containing from 6 to 14 percent rare earth oxides. U.S. Pat. No. 3,957,623 discloses a rare earth exchanged zeolite having a total of 1 to 10 weight percent rare earth metal oxide. U.S. Pat. No. 3,607,043 discloses a process for preparing a zeolite having a • rare earth content of 0.3 to 10 weight percent. U.S. Pat. No. 4,036,739 discloses hydrothermally stable and ' ammonia stable Y zeolite in which a sodium Y zeolite is ion exchanged to partially exchange sodium ions for ammonium ions, followed by steam calcination and a further ion exchange with ammonium to reduce the final sodium oxide content to below l weight percent, followed by calcination of the reexchanged product, or according to U.S. Pat. No. 3,781,199, the second calcination may be conducted after the zeolite is admixed with a refractory oxide. The products obtained by use of such aforementioned catalysts may not be the most desirable in all instances. Accordingly, catalysts and processes have been developed to modify the products of cracking processes. Several patents have disclosed the use of various additives as components in cracking catalysts to modify product distributions. U.S. Patent No. 4,284,529 discloses the use of a catalyst additive comprising a zeolite having an alpha value not less than about 5 and having substantially no activity for cracking n-hexane. U.S. Patent No. 4,239,654 discloses a catalyst composition comprising an ultrastable Y-type crystalline aluminosilicate zeolite, a catalytic inorganic oxide matrix and a small pore crystalline ZSM-type zeolite. U.S. Patent No. 4,289,606 is similar to U.S. Patent No. 4,239,654 in that a small pore crystalline ZSM-5 type zeolite is employed with an ultrastable Y-type crystalline aluminosilicate zeolite as the catalyst. U.S. Patent Nos. 4,309,279 and 4,309,280 relate to the use of a zeolite additive to cracking processes wherein the zeolite is characterized by a Constraint Index of about 1- to 12 and a silica to alumina ratio greater than about 12. The above processes relate to the use of zeolite mixtures and are necessarily limited to zeolites. U.S. Patent No. 4,440,871 discloses a novel class of crystalline microporous silicoalumino¬ phosphate molecular sieves. These silicoalumino¬ phosphates are generally disclosed as being useful for various hydrocarbon, conversion processes, including catalytic cracking processes. The use of the silicoaluminophosphates of U.S. Patent No. 4,440,871 as components in conventional cracking catalysts for the conversion of crude oil feedstocks containing carbon-hydrogen fragmentation compounds is disclosed in copending U.S. Serial No. 490,952, filed May 2, 1983. Although the above generally disclose the use of the silicoaluminophosphates in cracking processes such do not disclose the use of specific silicoaluminophosphates to provide improved product distribution, as hereinafter discussed. The use of silicoaluminophosphate molecular sieves as cracking catalysts is disclosed in copending U.S. Serial No. 675,279, filed concurrently herewith and commonly assigned. The use of silicoaluminophosphates and zeolites as cracking catalysts is disclosed in copending U.S. Serial No. 675,283, filed concurrently herewith and commonly assigned ' . The instant invention relates to the use of non-zeolite molecular sieves as components in cracking catalysts and to their use in catalytic cracking processes. When such non-zeolitic molecular sieves are added to cracking catalysts and employed in catalytic cracking processes such processes give products having product distributions substantially different and more valuable from that obtained in the absence of such non-zeolitic molecular sieves. SUMMARY OF THE INVENTION The instant process relates to the catalytic cracking of crude oil feedstocks to produce lower boiling hydrocarbons and comprises contacting said feedstocks at effective catalytic cracking conditions with a catalyst comprising at least one non-zeolitic molecular sieve, as hereinafter described, and optionally particles having catalytic activity for cracking crude oil feedstocks at effective catalytic cracking- conditions, e.g., particles containing a zeolitic aluminosilicate of the type generally employed in cracking catalysts. The non-zeolitic molecular sieves employed in this instant invention are characterized in their calcined form by an adsorption of isobutane of at least 2 percent by weight at a pressure of 500 torr and a temperature of 20°C. The cracking component, e.g., a zeolitic aluminosilicate, if any, is characterized as being a cracking component, such as heretofore traditionally employed in catalytic cracking process, e.g., the various forms of zeolite Y and silica-alumina components. The non-zeolitic molecular sieves employed in this- invention are unique in,that such are not zeolite aluminosilicates, as heretofore employed in the prior art cracking catalysts, but are specific non-zeolitic molecular sieves. DETAILED DESCRIPTION OF THE INVENTION The present invention relates to new catalytic cracking catalysts, the process for their preparation and to the process of their use in catalytic cracking processes for the conversion of crude oil feedstocks. The catalytic cracking catalysts of the instant invention are derived from a novel class of non-zeolitic molecular sieves, as hereinafter discussed.- It has been found that the use of specific non-zeolitic molecular sieves provide different " __ product distributions when such non-zeolitic molecular sieves are employed alone or in conjunction with conventional cracking catalysts having cracking activity at effective cracking conditions. Heretofore, the catalysts of the prior art have required that certain penalties be endured for the optimization of particular process variables or product characteristics, e.g., octane. For example, an improvement in gasoline octane of the products, as indicated by an increased ratio of branched to linear olefins and isoparaffin to normal paraffins, has been observed to occur with a concurrent decrease in gasoline yield and in feed conversion when zeolitic aluminosilicate-based catalysts are employed. As aforementioned, the presence of isoparaffins and branched olefins have long been employed as indications of higher octane products and their increase or decrease u≤ed as a relative indication of the octane of the gasoline product. The instant process provides for the improved production of isoparaffins and branched olefins and also provides a decrease in the relative amount of normal paraffins and linear olefins without significantly increasing the loss in gasoline yield and feed stock conversion. The non-zeolitic molecular sieves employed in the instant invention are selected from the hereinafter described group of non-zeolitic molecular sieves as being characterized in their calcined form by an adsorption of isobutane of at least 2 percent by weight at partial a pressure of 500 torr and a temperature of 20°C. When the ' v non-zeolitic molecular sieves are employed in conjunction with a zeolitic aluminosilicate cracking component the non-zeolitic molecular sieves are preferably also characterized in their calcined form by an adsorption of triethylamine of less than 5 percent by weight at a partial pressure of 2.6 torr and a temperature of 22°C. In a further embodiment the non-zeolitic molecular sieves are employed without a zeolitic aluminosilicate and in such embodiment the non-zeolitic molecular sieves are preferably characterized by an adsorption of triethylamine greater than 5 percent by weight at a partial pressure of 2.6 torr and temperature of 22°C. NON-ZEOLITIC MOLECULAR SIEVES ("NZ-MS") The term "non-zeolitic molecular sieves" or "NZ-MS" is defined in the instant invention to include the "SAPO" molecular sieves of U.S. Patent No. 4,440,871, "ELAPSO" molecular sieves as disclosed in U.S.. Serial No. 600,312, filed April 13, 1984 EPC App. No. 85104387.7 and certain "MeAPO", "FeAPO" , "TiAPO" and "FCAPO" molecular sieves. Crystalline metal aluminophosphates (MeAPOs where "Me" is at least one of Mg, Mn, Co and Zn) are disclosed in EPC App. No. 84108182.1, Publication No. 0132708 (Feb. 13, 1985); crystalline ferroaluminophosphates (FeAPOs) are disclosed in EPC App. No. 8410834.6.2, Publication No. 0131946 (Jan. 23, 1985); titanium aluminosphosphates (TAPOs) are disclosed in EPC App. No. 84103424.2, Publication No. 0121232 (Oct. 10, 1985) and non-zeolitic molecular sieves ("FCAPO") are disclosed U.S. Serial r, a No. 600,171, filed April 13, 1984. The aforementioned copending applications are incorporated herein by reference thereto. "ELAPSO" molecular sieves are described in copending U.S. Serial No. 600,312, filed April 13, 1984, as crystalline molecular sieves having three-dimensional microporous framework structures of EL0 2 , AIO,, PO 2 , SiO, oxide units and having an empirical chemical composition on an anhydrous basis expressed by the formula: mR: <E w Al χ P y Si z )O 2 wherein "R" represents at least one organic templating agent present in the intracrystalline pore system; "m" represents the molar amount of "R" present per mole * of (EL Al-.P YSi«JW O * ,£ and has a value of from zero to about 0.3; "EL." represents at least one element capable of forming a three-dimensional oxide framework, "EL" -is ' characterized as an element having a mean "T-O" distance in tetrahedral oxide structures between about 1.51 Angstroms and about 2.06 Angstroms, "EL" has a cation electronegativity between about 125 kcal/g-atom to about 310 kcal/gm-atom and "EL" is capable of forming stable M-O-P, M-O-Al or M-O-M bonds in crystalline three dimensional oxide structures having a "M-O" bond dissociation energy greater- than about 59 kcal/g-atom at 298°K; and "w", "x", "y" and "z" represent the mole fractions of "EL", aluminum, phosphorus and silicon, respectively, present as framework oxides said mole «,-ϋ£j _. fractions being within the.pentagonal compositional area defined by points A, B, c, D and E of FIG. 1. where A, B, C, D and E are: Mole Fraction Point x y (z+w) A 0.60 0.39-(0.01)p O.OKp+1) B 0.«39-<0.01p) 0.60 O.OKp+1) C 0.01 0.60 0.39 D 0.01 0.01 0.98 E 0.60 0.01 0.39 where "p" is an integer corresponding to the number of elements "El" in the (El Al J%P YSi £JΛ O. *ύ constituen . The "ELAPSO" molecular sieves are also described as crystalline molecular sieves having three-dimensional microporous framework structures of EL0 2 , A10 2 , Si0 2 and P0 2 tetrahedral oxide units and having an empirical chemical composition on an anhydrous basis expressed by the formula: * mR: (EL w Al χ P y Si z )O 2 wherein "R" represents at least one organic templating agent present in the intracrystalline pore system; "m" represents the molar amount of "R" present per mole of (EL Al P SiJO, and has a value of from zero to about 0.3; "EL" represents at least one element capable of forming a framework tetrahedral oxide and is selected from the group consisting of arsenic, beryllium, boron, chromium, cobalt, gallium, germanium, iron, lithium, magnesium, manganese, titanium, vanadium and zinc; " t _. and "w", "x", "y" and "z" .represent the mole fractions of "EL", aluminum, phosphorus and silicon, respectively, present as tetrahedral oxides said mole fractions being within the tetragonal compositional area defined by points a, b, c and d of FIG. 1 where a, b, c and d are: . Mole Fraction Point x y (z+w) a 0.60 0.39-(0.01)p O.Ol(p- l) b 0.39-(0.01p) 0.60 0.01(p+l) c 0.10 0.55 0.35 d 0..55 0.10 0.35 where "p" is as above defined. The "ELAPSO" molecular sieves include numerous species which are intended herein to be within the scope of the term "non-zeolitic molecular sieves" such being disclosed in the following copending and commonly assigned applications, incorporated herein by reference thereto: U.S. Serial No. Filed NZ-MS , 600.174 April 13, 1984 ■ CoAPSO 600,173 April 13, 1984 FeAPSO 600,180 April 13, 1984 MgAPSO 600.175 April 13, 1984 MnAPSO 600,179 April 13, 1984 TiAPSO 600,170 April 13, 1984 ZnAPSO 600,168 April 13, 1984 CoMgAPSO 600,182 April 13, 1984 CoMnMgAPSO TiAPSO Molecular Sieves The TiAPSO molecular sieves of U.S. Serial o. 600,179, filed April 13, 1984 have three-dimensional microporous framework structures of Ti0 2 , A10 2 , P0 2 and SiO 2 tetrahedral oxide units having an empirical chemical composition on an anhydrous basis expressed by the formula: mR : (Ti w Al χ P y Si z )O 2 wherein "R" represents at least one organic templating agent present in the intracrystalline pore system; "m" represents the molar amount of "R" present per mole of (Ti Al P SiJO, and has a value of from zero to about 0.3; and "w" , "x", "y" and "z" represent the mole fractions of titanium, aluminum, phosphorus and silicon, respectively, present as tetrahedral oxides and each has a value of at least 0.01. The mole fractions "w" , "x", "y" and "z" are generally defined being within the pentagonal compositional area defined by points A, B, C, D and E of the ternary diagram of Fig. 1. Points A-, B, C, D and E of Fig.'l have the following values for "w" , "x", ' "y", and "z": Mole Fraction Point X Y (z+w) A 0.60 0.38 0.02 B 0.38 0.60 0.02 C 0.01 0.60 0.39 D 0.01 0.01 0.98 E 0.60 0.01 0.39 In a preferred subclass of TiAPSO molecular sieves the values "w", "x", "y" and "z" in the above formula are within the tetragonal compositional area defined by points a, b, c and d of the ternary diagram which is Fig. 2 of the drawings, said points a, b, c and d representing the following values for "w", "x", "y" and "z". Mole Fraction Point X Y ( z+w) a 0 . 55 0 . 43 0 . 02 b . 0 . 43 0 . 55 0 . 02 c 0 . 10 0 . 55 0 . 35 d 0 . 55 0 . 10 0 . 35 TiAPSO compositions are generally synthesized by hydrothermal crystallization from a reaction mixture containing reactive sources of titanium, silicon, aluminum and phosphorus, and preferably an organic templating, i.e., structure-directing, agent, preferably a compound of an element of Group VA of the Periodic Table, and/or optionally an alkali or metal metal. The reaction mixture is generally placed in a sealed pressure vessel, preferably lined with an inert plastic material such as polytetrafluoroethylene and heated, preferably under autogenous pressure at a temperature between 50°C and 250°C, and preferably between 100°C and 200°C until crystals of the TiAPSO product are obtained, usually a period of from hours to several weeks. Generally, the crystallization time is from about 2 hours to about 30 days and typically from about 4 hours to about 20 days. The product is recovered by any convenient method such as centrifugation or filtration. In synthesizing the TiAPSO, it is preferred to employ a reaction mixture composition expressed in terms of the molar ratios as follows: a* : (Ti w Al χ P y Si z )0 2 : bH 2 0 wherein "R" is an organic templating agent; "a" is the amount of organic templating agent "R" and has a value of from zero to about 6 and is preferably an effective amount within the range of greater than zero (.0) to about 6; "b" has a value of from zero (0) to about 500, preferably between about 2 and about 300; and "w" , "x" , "y" and "z" represent the mole fractions of titanium, aluminum, phosphorus and silicon, respectively, and each has a value of at least 0.01. In a preferred embodiment the reaction mixture is selected such that the mole fractions "w", "x", "y" and "z" are generally defined as being within the pentagonal compositional area defined by points E, F, G, H and I of the ternary diagram of FIG. 3. Points E, F, G, H and I of FIG. 3.have the following values for "w" , "x" , "y" and "z"; Mole Fraction Point X Y (z+w) F 0.60 .0.38 0.02 G 0.38 0.60 0.02 H 0.01 0.60 0.39 I 0.01 0.01 0.98 J 0.60 0.01 0.39 In the foregoing expression of the reaction comppsition, the reactants are normalized with respect to the total of "w" , "x", "y" and "z" such that (w + x + y + z) =1.00 mole. MqAPSO Molecular Sieves The MgAPSO molecular sieves of U.S. Serial No. 600,180, filed April 13> 1984 have three-dimensional microporous framework structures —2 — + of Mg0 2 , A10 2 , P0 2 and Si0 2 tetrahedral oxide units and have an empirical chemical composition on an anhydrous basis expressed by the formula: mR : (Mg w Al χ P y Si 2 )0 2 wherein "R" represents at least one organic templating agent present in the intracrystalline pore system; "m" represents the molar amount of "R" present per mole has a value from and "w", "x", "y" and "z" represent the mole fractions of magnesium, aluminum, phosphorus and silicon, respectively, present as tetrahedral oxides and each preferably has a value of at least 0.01. The mole * fractions "w", "x" , "y" and "z" are generally defined as being within the pentagonal compositional area defined by points A, B, C, D and E of the ternary diagram of FIG. 1. Points A, B, C, D and E of FIG. 1 have the following values for "w", "x" , "y" and "z": Mole Fraction Point X Y (z+w) A 0.60 0.38 0.02 B 0.39 0.59 0.02 C 0.01 0.60 0.39 D 0.01 0.01 0.98 E 0.60 0.01 0.39 In a preferred subclass of the MgAPSO molecular sieves the values "w" , "x" , "y" and "z" in the above formula are within the tetragonal compositional area defined by the points a, b, c and d of the ternary diagram of FIG. 2, said points a, b, c and d representing the following values for "w", "x", "y" and "z": Mole Fraction Point x y (z+w) a 0.55 0.43 0.02 b 0.43 0.55 0.02 C . 0.10 0.55 0.35 d 0.55 0.10 0.35 MgAPSO compositions are generally synthesized by hydrothermal crystallization for an effective time at effective pressures and temperatures from a reaction mixture containing reactive sources .of magnesium, silicon, aluminum and phosphorus, an organic templating, i.e., structure-directing, agent, preferably a compound of an element of Group VA of the Periodic Table, a * nd may be an alkali or other metal. The reaction mixture is generally placed in a sealed pressure vessel, preferably lined with an inert plastic material such as polytetrafluoroethylene and heated, preferably under autogenous pressure at a temperature between 50°C and 250°C, and preferably between 100°C and 200°C until crystals of the MgAPSO product are obtained, usually a period of from several hours to several weeks. Generally, the crystallization period will be from about 2 hours to about 30 days with it typically being from about 4 hours to about 20 days for obtaining MgAPSO crystals. The product is recovered by any convenient method such as centrifugation or filtration. In synthesizing the MgAPSO compositions, it is preferred to employ reaction mixture compositions expressed in terms of the molar ratios as follows: R : < M< ? w A1 x P y Si z )0 2 bH 2 0 wherein "R" is an organic templating agent; "a" is the amount of organic templating agent "R" and can have a value within the range of from zero (0) to about 6 and is more preferably an effective amount greater than zero to about 6; "b" has a value of from zero (0) to about 500, preferably between about 2 and about 300; and "w" , "x", "y" and "z" represent the mole fractions of magnesium, aluminum, phosphorus and silicon, respectively, and each has a value of at least 0.01. In a preferred embodiment the reaction mixture is selected such that the mole fractions "w" , "x", "y" and "z" are generally defined as being within the pentagonal compositional area defined by points F, G, H, I and J of the ternary diagram of FIG. 3. Points F, G, H, I and J of FIG. 3 have the following values for "w" , "x", "y" and "z". Mole Fraction Point X _____ (z+w) F 0.60 0.38 0.02 G 0.38 0.60 0.02 H 0.01 0.60 0.39 I 0.01 0.01 0.98 J 0.60 0.01 0.39 in the foregoing expression of the reaction composition, the reactants are normalized with respect to the total of "w" , "x", "y" and "z" such that (w+x+y+z) = 1.00 mole. MnAPSO Molecular Sieves The MnAPSO molecular sieves of U.S. Serial No. 600,175, fi ' led April 13, 1984 have a framework structure of Mn0 — 2 2, A10— 2 , P0+ 2 , and Si0 2 tetrahedral units having an empirical chemical composition on an anhydrous basis expressed by the formula: mR : (Mn w Al χ P y Si z )0 2 wherein "R" represents at least one organic templating agent present in the intracrystalline pore system; "m" represents the molar amount of "R" present per mole of (Mn Al P SiJO, and has a value of zero to about 0.3; and "w" , -"x" , "y" and "z" represent the mole fractions of element manganese, aluminum, phosphorus and silicon, respectively, present as tetrahedral oxides. The mole fractions "w", "x" , "y" and "z" are generally defined as being within the pentagonal compositional area defined by points A, B, C, D and E of the ternary diagram of FIG. 1 and more preferably are generally defined as being.within the tetragonal compositional area defined by points a, b, c and d of the ternary diagram of FIG. 2. Points A, B, C, D and E of FIG. 1 have the following values for "w" , x , y , and z : Mo_le Fraction Point x ____ (w+z) A 0.60 0.38 0.02 B 0.38 0.60 0.02 • C 0.01 0.60 0.39 D 0.01 0.01 0.98 E 0.60 0.01 0.39 W Points a, b, c, and d of FIG. 2 have the following values for "w", "x", "y" . and "z": Mole Fraction Point x y (w+z) a 0.55 0.43 0.02 b 0.43 0.55 0.02 C 0.10 0.55 0.35 d 0.55 0.10 0.35 The MnAPSOs of this invention are useful as adsorbents, catalysts, ion-exchangers, and the like in much the same fashion as aluminosilicates have been employed heretofore, although their chemical and physical properties are not necessarily similar to those observed for aluminosilicates. MnAPSO compositions are generally synthesized by hydrothermal crystallization from a reaction mixture containing reactive sources of manganese, silicon, aluminum and phosphorus, preferably an organic templating, i.e., structure-directing, agent, preferably a compound of an element of Group VA of the Periodic Table, and/or optionally an alkali or other metal. The reaction mixture is generally placed in a sealed pressure vessel, preferably lined with an inert plastic material such as polytetrafluoroethylene and heated, preferably under autogenous pressure at a temperature between about 50°C and about 250-°C, and preferably between about 100°C and about 200°C until crystals of the MnAPSO product are obtained, usually a period of from several hours to several weeks. Typical effective times of from 2 hours to about 30 days with generally from about 4 hours to about 20 days have been observed. The product is recovered by any convenient method such as centrifugation or filtration. In synthesizing the MnAPSO compositions, it is preferred to employ a reaction mixture composition expressed in terms of the molar ratios as follows: aR : (Mn w Al χ P y Si z )0 2 : bH 2 0 wherein ""R" is an organic templating agent; "a" is' the amount of organic templating agent "R" and has a value of from zero to about 6 and is preferably an * effective amount within the range of greater than zero (0) to about 6; "b" has a value of from zero (0) to about 500, preferably between about 2 and about 300; and "w", "x", "y" and "z" represent the mole fractions of manganese, aluminum, phosphorus and silicon, respectively, and each has a value of at least 0.01. In a preferred embodiment the reaction mixture is selected such that the mole fractions "w", "x", "y" and "z" are generally defined as being within the pentagonal compositional area defined by points E, F, G, H and I of the ternary diagram of FIG. 3. Points E, F, G, H and I of FIG. 3 have the following values for "w" , "x" , y" and "z": Mole Fraction Point X __._ (w+z) F 0.60 0.38 0.02 G 0.38 0.60 0.02 H 0.01 0.60 0.39 I 0.01 0.01 0.98 J 0.60 0.01 0.39 In the foregoing expression of the reaction composition, the reactants are normalized with respect to the total of "w" , "x" , "y" and "z" such that (w+x+y+z) = 1.00 mole. CoAPSO Molecular Sieves The CoAPSO molecular sieves of U.S. Serial No. 600,174, filed April 13, 1984 have three-dimensional microporous framework structures » _2 — + of Co0 2 , A10 2 , P0 2 and Sι0 2 tetrahedral units and have,an empirical chemical composition on an anhydrous basis expressed by the formula: mR : (Co w Al χ P y Si z )0 2 wherein "R" represents at least one organic templating agent present in the intracrystalline pore system; "m" represents the molar amount of "R" present per mole of (Co„wAlxPySizJO-2 and has a value of from zero to about 0.3; and "w", "x", "y" and "z" represent the mole fractions of cobalt, aluminum, phosphorus and silicon, respectively, present as tetrahedral oxides, where the mole fractions "w" , "x" , "y" and "z" are . each at least 0.01 and are generally defined, as being within the pentagonal compositional area defined by points A,B, C D and E of FIG. 1, said points A, B, C, D, and E having the following values for "w" , "x", "y" and Mole .Fraction Point X Y (z + w A 0.60 0.38 0.02 B 0.38 0.60 0.02 C 0.01 0.60 0.39 D 0.01 0.01 0.98 E 0.60 0.01 0.39 In a preferred subclass of the CoAPSO molecular sieves the values of "w", "x", "y" , and "z" in the above formula are within the tetragonal compositional area defined by points a, b, c, and d, of FIG. 2,' said points a, b, σ, and d having the following values for "w" , "x", "y" and "z": Mole Fraction Point X Y (z + w a 0.55 0.43 0.02 b 0.43 0.55 0.02 c 0.10 0.55 0.35 d 0.55 0.10 0.35 CoAPSO compositions are generally synthesized by hydrothermal crystallization from a reaction mixture containing reactive sources of cobalt, silicon, luminum and phosphorus, an organic templating, i.e., structure-directing, agent, preferably a compound of an element of Group VA of the Periodic Table, and optionally an alkali metal. The reaction mixture is generally placed in a sealed pressure vessel, preferably lined with an inert plastic material such as polytetrafluoroethylene and heated, preferably under autogenous pressure at an effective temperature which is generally between 50°C and 250°C and preferably between 100°C and 200°C until crystals of the CoAPSO product are obtained, usually for an effective time of from several hours to several weeks. Generally the effective crystallization time will be from about 2 hours to about 30 days and typically from about 4 hours to about 20 days. The product is recovered by any convenient method such as centrifugation or filtration. In synthesizing the CoAPSO, it is preferred to employ a reaction mixture composition expressed in terms of the molar ratios as follows: aR : (Co w Al χ P y Si z )0 2 : bH 2 0 wherein "R" is an organic templating agent; "a" is the amount of organic templating agent "R" and has a value of from zero to about 6 and is preferably an effective amount within the range of greater than zero (0) to about 6; "b" has a value of from zero (0) to about 500, preferably between about 2 and 300; and "w" , "x" , "y" and "z" represent the mole fractions of cobalt, aluminum, phosphorus and silicon, respectively, and each has a value of at least 0.01. In a preferred embodiment the reaction mixture is selected such that the mole fractions "w", "x", "y" and "z" are generally defined as being within the pentagonal compositional area defined by points E, F, G, H and I of the ternary diagram of FIG. 3. Points E, F, G, H and I of FIG. 3 have the following values for "w", "x", "y" and "z" : Mole Fraction Point X Y (z + w F 0.60 0.33 0.02 G 0.38 0.60 0.02 H 0.01 0.60 0.39 I 0.01 0.01 0.98 J 0.60 0.01 0.39 For reasons unknown at present, not every reaction mixture gave crystalline CoAPSO products when reaction products were examined for CoAPSO products by X-ray analysis. Those reaction mixtures from which crystalline CoAPSO products were obtained are reported in the examples hereinafter as numbered examples and those reaction mixtures from which CoAPSO products were not identified by use of X-ray analysis are reported as lettered examples. In the foregoing expression of the reaction composition, the reactants are normalized with respect to the total of "w" , "x", "y" and "z" such that (w+x+y+z) = 1.00 mole. ZnAPSO Molecular Sieves The ZnAPSO molecular sieves of U.S. Serial No. 600,170, filed April 13, 1984 comprise framework structures of Zn0 — 2 2, A10— 2 , P0+ 2 and Si0 2 tetrahedral units having an empirical chemical composition on an anhydrous basis expressed by the formula: t .- mR : (Zn w Al χ P y Si z )0 2 wherein "R" represents at least one organic templating agent present in the intracrystalline pore system; "m" represents the molar amount of "R"p s resent per mole of (ZnwAlxPy_SizJ0 o and has a value of zero to about 0.3; and "w", "x" , "y" and "z" represent the mole fractions of zinc, aluminum, phosphorus and silicon, respectively, present as tetrahedral oxides and each has a value of at least 0.01. The mole fractions "w" , "x", "y" and "z" are generally defined being within the pentagonal compositional area defined by points A, B, C, D and E of the ternary diagram of Fig. 1. Points A, B, C, D and E of Fig. 1 have the following values for "w", "x" , "y", and "z": Mole Fraction Point X Y (z + w *A 0.60 0.38 0.02 B 0.38 0.60 0.02 C 0.01 0.60 0.39 D 0.01 0.01 0.98 E 0.60 0.01 0.39 In a preferred subclass of ZnAPSO molecular sieves the values "w", "x", "y" and "z" in the above formula are within the tetragonal compositional area defined by points a, b, c and d of -the ternary diagram which is Fig. 2 of the drawings, said points a, b, c and d representing the following values for ιι-y-ιι a < .n•__a_-_. ιιz M ii . .. _Mole.Frac ion Point X Y ( z + w a 0 . 55 0 . 43 0 . 02 b 0 . 43 0 . 55 0 . 02 c 0 . 10 0 . 55 0 . 35 d 0 . 55 0 . 10 0 . 35 ZnAPSO compositions are generally synthesized by hydrothermal crystallization at effective process conditions from a reaction mixture containing active sources of zinc, silicon, aluminum and phosphorus, preferably an organic templating, i.e., structure-directing, agent, preferably a compound of an element of Group VA of the Periodic Table, and/or optionally an alkali or other metal. The reaction mixture is generally placed in a sealed pressure vessel, preferably lined with an inert plastic material such as polytetrafluoroethylene and heated, preferably under autogenous pressure at a temperature between 50°C and 250°C " , and preferably between 100°C and 200°C untij." crystals of the ZnAPSO product are obtained, usually a period of from several hours to several weeks. Generally the effective crystallization period is from about 2 hours to about 30 days with typical periods of from about 4 hours to about 20 days being employed to obtain ZnAPSO products. The product is recovered by any convenient method such as centrifugation or filtration. In synthesizing the ZnAPSO compositions, it is preferred to employ a reaction mixture composition expressed in terms of the molar ratios as follows: aR : (Zn w Al χ P y Si z )O 2 : bH 2 0 wherein "R" is an organic templating agent; "a" is the amount of organic templating agent "R" and has a value of from zero to about 6 and is preferably an effective amount within the range of greater than zero (0) to about 6; "b" has a value of from zero (0) to about 500, more preferably between about 2 and about 300; and "w", "x", "y" and "z" represent the mole fractions of zinc, aluminum, phosphorus and silicon, respectively, and each has a value of at least 0.01. In a preferred embodiment the reaction mixture is selected such that the mole fractions "w", "x", "y" and "z" are generally defined as being within the pentagonal compositional area defined by points F, G, H, I and J of the ternary diagram of FIG. 3. Points F, G, H, I and J of FIG. 3 have the following values for "w" , "x" , "y" and "z": Mole Fraction Point X (z + w F 0.60 0, .38 0.02 σ 0.38 0, ,60 0.02 H 0.01 0, ,60 0.39 I 0.01 0, ,01 0.98 J 0.60 0, ,01 0.39 In the foregoing expression of the reaction composition, the reactants are normalized with respect to the total of "w" - "x" , "y" and "z" such that (w+x+y+z) = 1.00 mole. FeAPSO Molecular Sieves The FeAPSO of U.S. Serial No. 600,173, ' filed April 13, 1984 have molecular sieves having a three-dimensional microporous crystal framework structures of Feθ — 2 2, (and/or FeO—J, A10~, P0 2 and Si0 2 tetrahedral oxide units and having a unit empirical formula, on an anhydrous basis, of: mR: (Fe w A1 x P y Si z )0 2 (1) wherein "R" represents at least one organic templating agent present in the intracrystalline pore system; "m" represents the moles of "R" present per mole of (Fe Al P.,-Si O, and has a value of from zero (0) to about 0.3; the maximu value of "m" in each case depends upon the molecular dimensions of the templating agent and the available void volume of the pore system of the particular molecular sieve involved; and "w", "x" , "y" and "z" represent the mole fractions of iron,• aluminum, phosphorus and silicon, respectively, present as tetrahedral oxides, said mole fractions being such that they are within the pentagonal compositional area defined by points A, B, C, D and E of the ternary diagram which is FIG. 1 of the drawings and more preferably are within the tetragonal compositional area defined by points a, b, c, and d of the ternary diagram which is FIG. 2 of the drawings. Points A, B, C, D and E of FIG. 1 represent the following values for "w", "x", "y" and "z" : Mole Fraction Point X __ (z + w) A 0.60 0.38 0.02 B 0.38 0.60 0.02 C 0.01 ■ 0.60 0.39 D 0.01 0.01 0.98 E 0.60 0.01 0.39 Points a, b, c and d of FIG. 2 represent the following values for "w" , "x", "y" and "z": Mole Fraction Point X 2 (z + w) a 0.55 0.43 0.02 b 0.43 0.55 0.02 c 0.10 0.55 0.35 d 0.55 0.10 0.35 The FeAPSOs of the instant invention are generally synthesized by hydrothermal crystallization from a reaction mixture comprising reactive sources of iron, aluminum, phosphorus and silicon, and preferably one or more organic templating agents. Optionally, alkali or other metal(s) may be present in the reaction mixture and may act as templating agents. The reaction mixture is generally placed in a pressure vessel, preferably lined with an inert plastic material, such as polytetrafluoroethylene, and heated, preferably under the autogenous pressure, at an effective temperature which is generally between about 50°C, and about 250°C and preferably between about 100°C and 200°C until crystals of the FeAPSO product are obtained, ususally a period of from several hours to several weeks. CoMnAPSO Molecular Sieves The expressed by the empirical chemical formula (anhydrous): mR : (Co u Mn v Al χ P y Si z )0 2 where "u", "v"-, "x" , "y" and "z" represent the mole. The CoMnAPSO molecular sieves have an empirical chemical composition on an anhydrous basis expressed by the formula: mR : (Co u Mn v Al χ P y Si z )0 2 wherein "R" represents at least one organic templating agent present in the intracrystalline pore system; "m" represents the molar amount of "R" present p s er mole of (Co,u,Mn„vA1xPySiJz O, from zero (0) to about 0.3; and "u", "v" , "x", "y" and "z" represent the mole fractions of cobalt, manganese, aluminum, phosphorus and silicon, respectively, present as tetrahedral oxides. The mole fractions "u", "v" , "x", "y" , and "z" are generally defined as being within the pentagonal compositional area defined by points A, B, C, D and E of FIG. 1, where "w" is the sum of "u" and "v" and where "M w " in FIG. 1 represents the combined mole fractions of cobalt and manganese: Mole Fraction Point X Y (Z + w) A 0.60 0.37 0.03 B 0.37 0.60 0.03 C 0.01 0.60 0.39 D 0.01 0.01 0.98 E 0.60 0.01 0.39 «---Q -- The mole fractions u, v, x, y and z, expressed as in FIG. 1, are preferably defined as being within the tetragonal compositional area defined by points a, b, σ and d of FIG. 2 as follows: Mole Fraction Xx y ( z + w) a 0 . 55 0 . 42 0 . 03 b 0 . 42 0 . 55 0 . 03 c 0 . 10 0 . 55 0 .35 d 0 . 55 0 . 10 0 .35 CoMnAPSO compositions are generally synthesized by hydrothermal crystallization from a reaction mixture containing reactive sources of cobalt, manganese, aluminum, phosphorus and silicon and preferably an organic templating agent, i.e., structure- directing, agent. The structure-directing agents are preferably a compound of an element of Group VA of the Periodic Table, and may be an alkali or other metal. The reaction mixture is generally placed in a sealed pressure vessel, preferably lined with an. inert plastic material such as polytetra- fluoroethylene and heated, preferably under autogenous pressure and at typical effective temperatures between 50°C and 250°C, preferably between 100°C and ' 200°C until crystals of the CoMnAPSO product are obtained, usually over a period of from several hours to several weeks. Typical effective crystallization times are from about 2 hours to 30 days with from about 4 hours to about 20 days being generally employed to obtain CoMnAPSO products. The product is recovered by any convenient method such as centrifugation or filtration. In synthesizing the CoMnAPSO compositions, it is preferred to employ a reaction mixture composition expressed in terms of the molar ratios as follows: aR : (Co u Mn v Al χ P y Si z )0 2 : bH 2 0 wherein "R" is an organic templating agent; "a" is the amount of organic templating agent "R" and has a value of " from zero to about 6 and is preferably an effective amount within the range of greater than zero (0) to about 6; "b" has a value of from zero (0) to about 500, preferably between about 2 and about 300; and "u" , "v", "x" , "y" , and "z" represent the mole, fractions of elements cobalt, manganese, aluminum, phosphorus and silicon, respectively, and each has a value of at least 0.01. In a preferred embodiment the reaction mixture is selected such -that the mole fractions "w", "x", "y" and "z" are generally defined as being within the pentagonal compositional area defined by points E, F, G, H and I of the ternary diagram of FIG. 3. Points E, F, G, H, and I of FIG. 3 have the following values for "w" , "x" , "y" and "z 1 Mole Fraction X Y (z + w) F 0.60 0.37 0.03 G 0.37 0.60 0.03 H 0.01 0.60 0.39 I 0.01 0.01 0.98 J 0.60 0.01 0.39 «-_. In the foregoing expression of the reaction composition, the reactants -are normalized with respect to the total of "u" " , "v", "x", "y" and "z" such that (u+v+x+y+z)=l.00 mole. CoMnMqAPSO Molecular Sieves The CoMnMgAPSO molecular sieves of U.S. .Serial No. 600, ' l82, filed April 13, 1984 have three-dimensional microporous framework structures -2 —2 -2 - of Co0 2 , Mn0 2 , Mg0 2 , A10 2 , PO$ and Siθ2 tetrahedral oxide units and have an empirical chemical composition on an anhydrous basis expressed by the formula: mR : (Co t Mn u Mg v Al χ P y Si z )0 2 wherein "R" represents at least one organic templating agent present in the intracrystalline pore- system; "m" represents the molar amount of "R" present per mole of (Co.Mn-LMgVAl«XPVSij2 O_,_,, and has a value of from zero to about 0.3; and "t", "u" , "v" , "x", "y" and "z" represent the mole fractions of cobalt, manganese, magnesium, aluminum, phosphorus and silicon, respectively, present as tetrahedral oxides, each having a value of at least 0.01. The mole fractions "t", "u", "v" , "x" , "y" and "z" are generally defined as being within the pentagonal compositional area defined by points A, B, C, D and E of FIG. 1 where "M" denotes cobalt, manganese and magnesium and "w" denotes the combined mole fractions of "t", "u" and "v", such that "w" = "t" + - "u" + "v" and such that "t", "u" "v" and "z".each have a value of at least 0.01. Points A, B, C, D and E of FIG. 1 have the following values for "w" . "x", "y" and "z": Mole Fraction Point X Y (Z + w) A 0.60 0.36 0.04 B 0.36 0.60 0.04 C 0.01 0.60 0.39 D 0.01 0.01 0.98 E 0.60 0.01 0.39 In a preferred subclass, of the CoMnMgAPSO molecular sieves the values of "w" , "x", "y" and "z in the above formula are within the tetragonal compositional area defined by points a, b, c and d of Fig. 2. Points a, b, c and d have the following values for "w" , "x", "y" and "z": Mole Fraction Point X _____ (z + w) a 0.55 0.41 0.04 b 0.41 0.55 0.04 c 0.10 0.55 0.35 d 0.55 0.10 0.35 The CoMnMgAPSOs of this invention are useful as adsorbents, catalysts, ion-exchangers, and the like in much the same fashion as aluminosilicates have been employed heretofore, although their chemical and physical properties are not necessarily similar to those observed for aluminosilicates. CoMnMgAPSO compositions are generally synthesized by hydrothermal crystallization from a reaction mixture containing reactive sources of • cobalt, manganese, magnesium, aluminum, phosphorus and silicon, and preferably an organic templating agent, i.e., structure-directing, agent. The structure-directing agents are preferably a compound of an element of Group VA of the Periodic Table, and/or optionally an alkali or other metal. The reaction mixture is generally placed in a sealed pressure vessel, preferably lined with an inert plastic material such as polytetrafluoroethylene and heated, preferably under autogenous pressure at a temperature between 50°C and 250°C, and preferably between 100°C and 200°C until crystals of the CoMnMgAPSO product are obtained, usually over a period of from several hours to several weeks.. Typical crystallization times are from about 2 hours to about 30 days with from about 4 hours to about 20 days generally being employed to obtain CoMnMgAPSO products. The product is recovered by any convenient method '§uch as centrifugation or filtration. In synthesizing the CoMnMgAPSO compositions, it is preferred to employ a reaction mixture composition expressed in terms of the molar ratios as follows: aR : (Co t Mn u Mg v Al χ P y Si z )0 2 : bH 2 0 wherein "R" is an organic templating agent; "a" is the amount of organic templating agent "R" and has a value of from zero to about 6 and is preferably an effective amount within the range of greater than zero (0) to about 6 and more preferably from greater than zero to about 2; "b" has a value of from zero (0) to about 500, preferably between about 2 and about 300; and "t" , "u" , "v", "x" , "y" , and "z" represent the mole fractions of cobalt, manganese, magnesium, aluminum, phosphorus and silicon, respectively, and each has a value of at least 0.01. In a preferred embodiment the reaction mixture is selected such that the mole fractions "w", "x", "y" and "z", where "w" is the sum of "t" + "u" + "v", are generally defined as being within the pentagonal compositional area defined by points E, F, G, H and I of the ternary diagram of FIG. 3. Points Ξ, F, G, H and I of FIG. 3 have the following values "w", "x" , "y" and "z": Mole Fraction Point X V (z + w) F 0.60 0.36 0.04 G 0.36 0.60 0.04 H 0.01 0.60 0.39 I 0.01 0.01 0.98 J 0.60 0.01 0.39 In the foregoing expression of the reaction composition, the reactants are normalized with respect to the total of "t", "u" , "v", "x", "y" and "z" such that (t + u + v + x + y + z) = 1.00 mole. SAPO Molecular Sieves The silicoaluminophosphate molecular sieves of U.S. Patent No. 4,440,871 are described as microporous crystalline silicoaluminophosphates the pores of which are uniform and have nominal diameters of greater than about 3 Angstroms and whose essential empirical chemical composition in the as-synthesized and anhydrous form is mR:(Si χ Al y P z )0 2 wherein "R" represents at least one organic templating agent present in the intracrystalline pore system; "m" represents the moles of "R" present per mole of (Six„Al,y,PzJO,; "m" has a value of from 0.02 to 0.3; "x", "y" and "z" represent the mole fractions of silicon, aluminum and phosphorus respectively, present as tetrahedral oxides, said mole fractions being such that they are within the pentagonal compositional area defined by points ABCD and E of the ternary diagram which is FIG. 1 of the drawings of U.S. Patent No. 4,440,871. The SAPO molecular sieves of U.S. Patent No. 4,440,871 are also described as silicoaluminophosphates having a three-dimensional microporous framework structure of Po , AloI and Si0 2 tetrahedral units, and whose essential empirical chemical composition on an anhydrous basis is: mR:(Si χ Al y P 2 )0 2 wherein "R" represents at least one organic templating agent present in the intracrystalline pore system; "m" represents the moles of "R" present per mole of (Si ΛAl YP2 O £, * and has a value of from zero to 0.3; "x", "y" and "z" represent respectively, the mole fractions of silicon, aluminum and phosphorus present in the oxide moiety. said mole fractions being within the compositional area bounded by points A, B, C, D and E on the ternary diagram which is FIG. 1, said silicoaluminophosphate having a characteristic X-ray powder diffraction pattern which contains at least the d-spacings set forth below in any one of Tables I, III, V, VII, IX, XII, XVII, XXI, XXIII or XXV of U.S. Patent No. 4,440,871. Further, such crystalline silicoaluminophosphates may be calcined at a temperature sufficiently high to remove at least some of any organic templating agent present in the intracrystalline pore system.- The silicoaluminophosphates of U.S. Patent No. 4,440,871 are generally referred to therein as "SAPO-n", as a class, or as "SAPO-n" wherein "n" is an interger denoting a particular SAPO as its preparation is reported in U.S. Patent No. 4,440,871. NZ-MS CATALYSTS The specific NZ-MSs employed in the instant invention are characterized in their calcined form by an adsorption of isobutane of at least 2 percent by weight at a pressure of 500 torr and a partial temperature of 20°C. When the non-zeolitic molecular sieve is employed in conjunction with a zeolitic aluminosilicate cracking component the non-zelitic molecular sieve is preferably also characterized in its calcined form by and adsorption of triethylamine of less than 5 percent by weight at a partial pressure of 2.6 torr and a temperature of 22°C. In a further embodiment the non-zeolitic molecular sieves are employed without a zeolitic aluminosilicate and in such embodiment the - o non-zeolitic molecular sieve is. preferably characterized by an adsorption of triethylamine greater than 5 percent by weight at a partial pressure of 2.6 torr and a temperature of 22°C. NZ-MSs characterized by the above described adsorption of isobutane include, but are not limited to, ELAPSO-5, E^APSO-11, ELAPSO-31, ELAPSO-37, ELAPSO-40, ELAPSO-41, CoAPSO-5, CoAPSO-11, CθAPSO-31, CoAPSO-37, CoAPSO-40, CoAPSO-41, FeAPSO-5, FeAPSO-11, FeAPSO-31, FeAPSO-40, FeAPSO-41, MgAPSO-5, MgAPSO-11, MgAPSO-31, MgAPSO-37, MgAPSO-40, MgAPSO-41, MnAPSO-5, MnAPSO-11, MnAPSO-31, MnAPSO-37, MnAPSO-40, MNAPSO-41, TiAPSO-5, TiAPSO-11, TiAPSO-31, TiAPSO-37, TiAPSO-40, TiAPSO-41, ZnAPSO-5, ZnAPSO-11, ZnAPSO-31, ZnAPSO-37, ZnAPSO-40, ZnAPSO-41, CoMgAPSO-5, CoMgAPSO-11, CoMgAPSO-31, CoMgAPSO-37', CoMgAPSO-40, CoMgAPSO-41, CoMnMgAPSO-5, CoMnMgAPSO-11, CoMnMgAPSO-31, CoMnMgAPSO-37, CθMnMgAPSO-40, CoMgAPSO-41, MeAPO-5, MeAPO-11, MeAPO-31, MeAPO-37, MeAPO-40, MeAPO-41, TiAPO-5, TiAPO-11, TiAPO-31, TiAPO-37, TiAPO-40, TiAPO-4 , FeAPO-5, FeAPO-11, FeAPO-31, FeAPO-41, FCAPO-5, FCAPO-11, FCAPO-31, FCAPO-37, FCAPO-40, FCAPO-41 and mixtures thereof. The above characterization of the NZ-MSs employed in the instant invention relates to an adsorption characterization that is carried out on a NZ-MS which has been subjected to a post synthesis treatment, e.g., calcination or chemical treatment, to remove a substantial portion of the template "R" which is present as a result of synthesis. Although a particular NZ-MS is characterized herein by reference to its adsorption of isobutane or triethylamine as being to the adsorption characterises of the NZ-MS in its calcined form, the instant invention necessarily includes the use of a non-calcined or modified NZ-MSs which are characterized by such adsorption in the modified or calcined form, since upon use of such a non-calcined NZ-MS in the instant process at catalytic cracking conditions the NZ-MS will be calcined or hydrothermally treated in situ so as to have the characteristic adsorption of isobutane or triethylamine. Thus, the NZ-MS will be rendered in situ to a form characterized by the aforementioned adsorption characteristics. For example, an as-synthesized MgAPO-ll or MgAPSO-11 are not characterized by the aforementioned adsorption of isobutane due to the presence of template "R" which is present as a result of« synthesis, although the calcined form of Mg&PO-ll and MgAPSO-11 are characterized by the aforementioned adsorption of isobutane. Thus, reference to a NZ-MS having a particular adsorption characteristic in its calcined form is not intended to exclude the use of the NZ-MS in its as-synthesized form which upon in-situ calcination, hydrothermal treatment and/or other treatment, e.g., ion exchange with suitable atoms, would have such adsorption characteristics. It has been found that this class of NZ-MS may provide product distributions not formed by cracking catalysts containing .zeolitic aluminosilicates. Heretofore, the catalysts of the v prior art have exhibited a decrease in gasoline yield and/or conversion for the optimization of a particular process variable or product characteristic e.g.-, octane of the gasoline product. Such penalties are reduced by use of the instant catalysts. Further, improved production of isoparaffins and branched olefins and also by the decreased amount of normal paraffins and linear olefins by use of the instant catalysts are indications of higher octane products. The term "crude oil feedstock" is used herein to denominate any crude oil feedstock or portion thereof and includes full range crude oils from primary, secondary or tertiary recovery from conventional or offshore oil fields and feedstocks derived therefrom. "Crude oil feedstocks" may also be "syncrudes" such ' as those that can be derived from coal, shale oil, tar sands and bitumens. The crude oil feedstock may be virgin (straight run) or generated synthetically by blending. Such crude oil feedstocks are traditionally desalted prior to use since sodium chloride is known to be a poison in many cracking operations. ' Further, the term "crude oil feedstocks" is intended to include component parts of crude oils which have heretofore been generally employed as catalytic cracking feeds or potential feeds and includes feeds such as distillate gas oils, heavy vacuum gas oils, VGO, atmospheric and vacuum resids, syncrudes, pulverized coal and fractions boiling above the traditional end of the gasoline boiling range which generally includes compounds containing greater than about eleven carbon atoms and combinations thereof. The NZ-MSs of the instant invention may be employed in conjunction with traditional cracking catalysts and optionally, a zeolitic aluminosilicate cracking component may be employed in conjunction with the NZ-MS containing catalysts. The zeolitic aluminosilicate cracking component of such catalysts may be any aluminosilicate heretofore employed as a component in cracking catalysts. Representative of the zeolitic aluminosilicates disclosed heretofore as employable as component parts of cracking catalysts are Zeolite Y, Zeolite X, Zeolite beta (U.S. Patent No. 3,308,069), Zeolite KZ-20 (U.S. Patent No. 3,445,727), Zeolite ZSM-3 (U.S. Patent No. 3,415,736), faujasite, LZ-10 (U.K. Patent 2,014,970, June 9, 1982), ZSM-type zeolites and mixtures thereof. Traditional cracking catalysts containing amounts of Na,0 less than about one percent by weight are preferred. Representative Y-type zeolites believed employable herein include, but are not limited to, those disclosed in U.S. Patent Nos.: 3,130,007; 3,835,032; 3,830,725; 3,293,192; 3,449,070; 3,839,539; 3,867,310; 3,929,620; 3,929,621; 3,933,983; 4,058,484; 4,085,069; 4,175,059; 4,192,778; 3„676,368; 3,595,611; 3,594,331; 3,536,521; 3,293,192; 3,966,643; 3,966,882 and 3,957,623. Another zeolitic aluminosilicate employable herein is "LZ-210", as described in E.P.C. Publication No. 82,211 published June 29, 1983. The term "ZSM-type" zeolites is generally employed in the art to refer to those zeolites denominated by the nomenclature "ZSM-n" where "n" is an integer. The ZSM-type aluminosilicates include but are not limited to ZSM-5, ZSM-11, ZSM-12, ZSM-23, ZSM-35, ZSM-38, ZSM-48; and other similar materials. ZSM-5 is described in greater detail in U.S. . Patent No., 3,702,886 and Re 29,948. The entire descriptions contained within those patents, particularly the X-ray diffraction pattern of therein disclosed ZSM-5, are incorporated herein by reference. ZSM-ll is described in U.S. Patent No. 3,709,979. That description, and in particular the X-ray diffraction pattern of said ZSM-ll, is incorporated herein by reference. ZSM-12 is described in U.S. Patent No. 3,832,449. That description, and in particular the X-ray diffraction pattern disclosed therein, is incorporated herein by reference. ZSM-23 is described in U.S. -Patent No. 4,076,842. The entire content, thereof, particularly the specification of the X-ray diffraction pattern of the disclosed zeolite, is incorporated herein by reference. ZSM-35 is described in U.S. Patent No. 4,016,245. The description of that zeolite, and particularly the X-ray diffraction pattern thereof, is incorporated herein by reference. ZSM-38 is more particularly describing U.S. Patent No. 4,046,859. The description of that zeolite, and particularly the specified X-ray diffraction pattern hereof, is incorporated herein by reference. ZSM-48 is more particularly described in U.S. Patent No. 4,423,021. The description of that zeolite, and particularly the specified X-ray diffraction pattern thereof, is incorporated herein by reference. FORMULATION OF NZ-MS CRACKING CATALYSTS The catalysts of the instant invention comprise at least one NZ-MS, as above characterized, and optionally may also contain one or more traditional cracking catalysts, including zeolitic aluminosilicate cracking components. The relative amount of the NZ-MS component or zeolitic aluminosilicate component, if any, will depend at least in part, on the selected crude oil feedstock and on the desired product distribution to be obtained therefrom, but in all instances an effective amo,unt of at least one NZ-MS is employed. When a zeolitic aluminosilicate is employed the relative weight ratio of the zeolitic aluminosilicate to the NZ-MS is generally between about 1:10 and about 500:1, desirably between about 1:10 and about 200:1, preferably between about 1:2 and about 50:1, and most preferably is between about 1:1 and about 20:1. The zeolitic aluminosilicate and NZ-MS may be ion-exchanged with a selected cation(s) and/or thermally treated either before or after mixture with each other or after such have been added separately or concurrently to one or more inorganic oxide matrix components. When the NZ-MS molecular sieves are ion exchanged such are preferably exchanged with a hydrogen-forming cation species, e.g. NH , H + , quaternary ammonium cations, etc. The NZ-MS preferably has at least part of its cations as hydrogen-forming cation species. The term "thermal treatment" is employed here to denominate both a thermal calcination in the presence of air or inert gas, e.g., nitrogen, and a hydrothermal calcination (thermal calcination in the presence of steam) . The thermal treatment is carried out at an effective temperature and time and when a hydrothermal treatment in the presence of an effective amount of steam. The thermal treatment is typically carried out at a temperature in excess of 300 o C for a period in excess of 0.25 hours and when the thermal treatment is a hydrothermal treatment it is typically carried out in the presence of at least about 20 percent steam by volume in air and up to about 100 percent steam. The source of the steam is -not important and may be provided from an external source or may be generated in situ at the temperatures employed for the hydrothermal treatment. As aforementioned a NZ-MS may be employed in the instant process in its as-synthesized form since in situ hydrothermal treatment will be provided upon introduction of the NZ-MS to the process under catalytic cracking conditions. Any ion-exchange of the zeolitic aluminosilicate(s) and NZ-MS(s), which aluminosilicate or NZ-MS may have ' been subjected to - thermal treatment, may be carried out by contacting such with a solution of at least one cation, including those selected from the group of cations *- consisting of ammonium, Group IIA, Group IIIA, Group IIIB to VTIB. and rare earth cations selected from the group consisting of cerium, lanthanum, praseodymium, neodymium, promethium, samarium, europium, gadolinium, terbium, dysprosium, holmium, erbium, thulium, ytterbium, lutetium and mixtures thereof. The exact nature of the relationship of rare earth cations and NZ-MS and their effect on the activity of the NZ-MS-containing catalyst is not clearly understood at present. As a result of ion-exchange, the cation(s), e.g., rare earth cation, may replace at least a portion of the cations initially present in the zeolitic aluminosilicate or NZ-MS. The cations provided by ion-exchange may be present in an effective amount which may be between about 0.1 weight percent and about 20 weight percent, typically between about 0.5* and about 10 weight percent, based on the weight of the starting zeolitic aluminosilicate or NZ-MS. The cracking catalysts of this invention are typically employed with an inorganic oxide matrix component which may be any of the inorganic oxide matrix components which have been employed heretofore in the formulation of FCC catalysts including: amorphous catalytic inorganic oxides, e.g., catalytically active silica-aluminas, clays, silicas, aluminas, silica-aluminas, silica-zirconias, silica-magnesias, alumina-borias, alumina-titanias and the like and mixtures thereof. The zeolite and NZ-MS may be mixed separately with the matrix component and then mixed or the zeolite and NZ-MS may be mixed and then formed with the matrix component. . The inorganic oxide matrix component may be in the form of a sol, hydrogel or gel and is typically an alumina, silica, clay and/or silica-alumina component such as employed a conventional silica-alumina cracking catalyst, several types and compositions of which are commercially available. The matrix component may itself provide a catalytic effect or it may be essentially inert. The matrix may act as a- "binder" in some instances, although in some instances the final catalyst may be spray dried or formed without the need of a binder. These materials may be prepared as a cogel of silica and alumina or as alumina precipitated on a preformed and preaged hydrogel. The silica may be present as a component in the solids present in such gels, e.g. present in an amount between about 5 and about 40 weight percent and preferably between about 10 and about 30 weight percent. Silica may also be employed in the form of a cogel comprising about 75 weight percent silica and about 25 weight percent alumina or comprising about 87 weight percent silica and about 13 weight percent alumina. The inorganic oxide matrix component will typically be present in the catalyst in an amount between about 0 and about 99 weight percent, preferably between about 5 and about 95 weight percent, based on the total catalyst weight. It is also within the scope of the instant invention to employ other materials in addition to the zeolitic aluminosilicate, NZ-MS and inorganic oxide matrix components in the final cracking catalysts, including various other types of zeolites, clays, carbon monoxide oxidation promoters, etc. Representative of matrix systems employable herein are disclosed in British Patent Specification No. 1,315,553, published May 2, 1973 and U.S. Patents Nos. 3,446,727 and 4,086,187, such being incorporated herein by reference thereto. As above mentioned, the catalysts of the present invention may be employed with a matrix component and this may be an alumina component. The alumina component may comprise discrete particles of various aluminas, e.g., pseudobeohmite. The alumina component may be in the form of discrete particles having a total surface area, as measured by the method of Brunauer, Emmett and Teller (BET), greater 2 than about 20 square meters per gram (M /g) , 2 preferably greater than 145 M /g, for example, 2 from about 145 to about ,300 M /g. The pore volume of the alumina component is typically greater than 0.35 cc/g. The average particle size- of the alumina particles is generally less than 10 microns and preferably less than 3 microns. The alumina may be employed alone as the matrix or composited with the other matrix components. The alumina component may be any alumina and has preferably been preformed and placed in a physical form such that its surface area and pore structure are stabilized so that when " the alumina is added to an impure, inorganic gel containing considerable amounts of residual soluble salts, the salts will not alter the surface and pore characteristics measurably nor will they promote chemical attack on the preformed porous alumina which could undergo change. For example, the alumina may be any an alumina which has been formed by suitable chemical reaction, the slurry aged, filtered, dried, washed free of residual salt and then heated to reduce its volatile content to less than about 15 weight percent. Further, an alumina hydrosol or hydrogel or hydrous alumina slurry may be used in the catalyst preparation. The inorganic oxide matrix components, e.g. aluminas, silicas, clays, etc., may be present in the final catalyst in an amount ranging between about 5 and about 99 weight percent, preferably between about 5 and about 95 weight percent and more preferably between about 10 and about 85 weight percent, based on the total catalyst weight. Mixtures of the zeolitic aluminosilicate, NZ-MS and the inorganic matrix may be formed into the final form for the catalyst by standard catalyst forming techniques including spray-drying, "pelleting, extrusion and other suitable conventional means. Such catalysts are typically prepared by spray drying, such procedures being well known to those skilled in the art of preparing catalytic cracking catalysts. Although the exact reason for such is not presently understood, the instant catalysts have been observed to provide different results in some instances when employed in cracking processes depending on whether the zeolitic aluminosilicate and NZ-MS are coincidentally or separately mixed with the matrix component. Catalytic cracking catalysts may be prepared by any one of several other conventional methods. One method of preparing such catalysts employing silica-alumina and porous alumina is to react sodium silicate with a solution of aluminum sulfate to form a silica/alumina hydrogel slurry which is then aged to give the desired pore properties, filtered to remove a considerable amount of the extraneous and undesired sodium and sulfate ions and then reslurried in water. The alumina may be prepared by reacting solutions of sodium aluminate and aluminum sulfate under suitable conditions, aging the slurry to give the desired pore prop #erties of the alumina, filtering drying, reslurry in water to remove sodium and sulfate ions and drying to reduce volatile matter content to less than 15 weight percent. The alumina may then be slurried in water and blended in proper amounts, with a slurry of impure silica-alumina "hydrogel. The zeolitic aluminosilicate and NZ-MS may then be added to this blend. A sufficient amount of each component is utilized to give the desired final composition. The resulting mixture is then filtered to remove a portion of the remaining extraneous soluble salts therefrom. The filtered mixture is then dried to produce dried solids. The dried solids are subsequently reslurried in water and washed substantially. free of the undesired soluble salts. The catalyst is then dried to a residual water .content of less than about 15 weight percent. The catalyst is typically recovered after calcination. Catalytic cracking with the catalyst of the present invention can be conducted in any catalytic — o — cracking process under effective catalytic cracking conditions. Suitable catalytic cracking conditions include a temperature ranging between about 400°F and about 1600°F, preferably between about 700°F and about 1600°F and a pressure ranging from about subatmospheric to several atmospheres, typically from about atmospheric to about 100 psig. The process may be carried out in a fixed fluidized bed, moving bed, ebullating bed, slurry, transferline, riser reactor or fluidized bed operation. The catalyst of the present invention can be used to convert any of the conventional hydrocarbon feeds used in catalytic cracking, that is, it can be used to crack naphthas, gas oil and residual oils having a high content of metal contaminants. It is especially suited for cracking hydrocarbons boiling .in the gas oil range, that is, hydrocarbon oils having an. atmospheric pressure boiling point ranging from about 420°F to about 1800°F to naphthas to yield not only products having a lower boiling point than the initial feed and gasoline products having an improved octane number. The mixture of a traditional cracking and a NZ-MS may be carried out in any manner which results in the coincident presence of such in contact with the crude oil feedstock under catalytic cracking ' conditions. For example, a catalyst may be employed containing both the traditional cracking catalyst and a NZ-MS in single catalyst particles or NZ-MS, with or without a matrix component, may be added as a discrete- component to a traditional cracking catalyst. In one embodiment, a NZ-MS may be added to a cracking. process as a make-up catalyst to replace the traditional cracking catalyst that has been lost through attrition. The following examples were carried out to illustrate the instant invention and are not intended to be limiting thereof. The zeolite LZ-210 was prepared in each example according to the disclosure of E.P.C. Publication No. 82,211, published June 29, 1983. SAPO molecular sieves were prepared according to U.S. Patent No. 4,440,871. The SAPO molecular sieves were calcined in air prior to use in the following examples. Calcination procedures for the removal of template are disclosed in U.S. Patent No. 4,440,871. The catalysts prepared in the following examples were evaluated by a procedure substantially the same as ASTM test method D-3907. Accordingly, reference to ASTM test method D-3907 hereinafter is meant to generally refer to the procedure of the ASTM test method with the following four modifications. First, the end boiling point of the products identified as gasoline products was 431°F. Second, the nitrogen post stripping of the catalyst was at 30 milliliters/min for a period of 23 minutes to 27 minutes. Third, the conversion is the measured conversion and not the standardized conversion of the ASTM test method. Fourth, the feedstock employed in the test method had an API gravity of 24.0°, an IBP (Initial Boiling Point) of 354°F, FBP (Final Boiling Point) of 1077°F and a UOP K Factor of 11.8. - J Example 1 A cracking catalyst was prepared according to the invention employing a mixture of SAPO-5 and LZ-210. In addition, a cracking catalyst containing LZ-210 was prepared as a reference catalyst. The catalysts were prepared using LZ-210, having a Si0 2 /Al 2 0 3 ratio, of 9.0, and SAPO-5. Two catalysts were prepared. Catalyst A was the reference catalyst and Catalyst B was a catalyst according to this invention. Catalyst A was prepared by slurrying 18% by weight LZ-210, 18% by weight of pseudobeohmite alumina, 60% by weight of a kaolin clay; 4% by weight of a silica and enough water to form a slurry having a 25% by weight solids content. The aforementioned percentages for the solid components are given on a dry basis. The slurry was then spray dried to obtain a fluidizable catalyst composite that would pass through a 150 micron sieve (U.S. Standard). The catalyst was then calcined at 600°C for 1 hour and then steam deactivated at 740°C for 2 hou'rs in 100% steam. Catalyst B was prepared by mixing Catalyst A and SAPO-5. The SAPO-5 was steam deactivated at 760°C for 2 hours in 100% steam prior to mixing with Catalyst A. The steam deactivation procedures are provided to simulate the environment experienced by commercial cracking catalysts. Catalyst B contained 10 percent by weight of SAPO-5 based on the total weight of Catalyst B. Catalysts A and B were each evaluated according to ASTM test method D-3907. In this and in the subsequent examples the "Wt.% Conversion" is the measured weight percent conversion as defined in ASTM test method D-3907, as above discussed. The "wt. % Gasoline" is defined as those hydrocarbons in the product from C_ hydrocarbons to hydrocarbons boiling below 431°F expressed as a weight percent of feed. The term "alkylate" herein denominates propylene, butylenes and isobutane. The "Wt.% Gas" is defined as those hydrocarbons boiling below C. in the product as a weight percent of feed. The "Wt.% Coke" is defined as the residue left on the used catalyst after post stripping as set forth above and is given as a weight percent. The "Wt.% C.s" is defined as the weight percent of isobutane, n-butane and butylenes of the product. The "Wt.% Cg-C- Aromatics" is defined herein as the weight percent of benzene, ethyl benzene, toluene and xylenes in the gasoline product. The results were as follows: Catalyst . C Caattaallvysst A Catalyst B Wt.% Conversion • 70.3 71.0 Wt.% Gasoline 50.0 49.3 Wt.% Gasoline + Aklylate 60.9 61.6 Wt.% Cg-Cβ Aromatics 14.6 15.4 Wt.% Coke 4.9 4.8 Wt.% Gas 6.2 . 6.7 Wt.% C S 9.1 10.2 The above data demonstrate that Catalyst B was comparable to Catalyst A as to Wt.% Conversion and Wt.% Gasoline while making more aromatic products which are useful in enhancing the octane of the gasoline products. Example 2 Two catalysts were prepared wherein Catalyst C was a reference catalyst containing LZ-210 having a Si0 2 /Al 2 0 3 ratio of 9.0 and Catalyst D was a catalyst according to the invention and contained LZ-210 and SAPO-11.. Catalyst C was prepared by preparing a slurry containing 15% by weight LZ-210, 18% by weight of a pseudobeohmite alumina, 60% by weight kaolin clay and 4% by weight silica in enough water to obtain a slurry having 25 percent by weight solids. The slurry was then spray dried to obtain a fluidizable catalyst having its size characterized by passing through a 150 micron sieve (U.S. Standard). The catalyst was calcined at 600°C for 1 hour and then steam deactivated at 765°C for 2 hours in 100% steam. Catalyst D was prepared according to the procedure employed for Catalyst C, except that 10 percent by weight kaolin clay was replaced by 10 percent by weight of SAPO-ϊl, i.e. 50% by weight kaolin clay was employed. Catalyst C and Catalyst D were evaluated according to ASTM test method D-3907, except that the run temperature was 850°F instead of the 900°F suggested by ASTM test method D-3907. The results were as follows: • 3 5 Catalyst ' Catalyst C Catalyst D Conversion: 61.9 62.9 Wt.% Gasoline: 46.5 47.6 Wt.% Gasoline + Alkylate 55.3 56.7 Wt.Paraffin Analysis 1 : Iso/normal 'C ' 4.8 5.7 Iso/normal Cg 13.6 17.1 Iso/normal C7 15.6 16.8 Iso/normal C3 7.1 8.1 Wt.Gas Product Analysis 2 : Olefin/paraffin C3 2.8 3.8 Olefin/paraffin C4 0.55 0.66 Wt.% Coke 4.1 4.0 1 Iso paraffin to normal paraffin ratios of compounds having the indicated number of carbons. 2 Olefin to paraffin ratio of compounds having the indicated number of carbons. *a-* - The above results demonstrate that the addition ot SAPO-11 as a component of Catalyst D provided products having comparable Wt.% Gasoline and Wt.% Gasoline + Alkylate while also providing for an increase in the iso to normal ratio of the paraffin products, thus indicating higher octane products. The increase in the olefin content of the gas product, as indicated by the Gas Product Analysis, indicates a gas product having more useful and valuable olefin products. Example 3 Two catalysts were prepared wherein Catalyst E was a reference catalyst containing LZ-210 (Si0 2 /Al 2 0 3 ratio of 9.0) and Catalyst F was a catalyst according to this invention containing LZ-210 and SAPO-5. Catalyst E was prepared by forming a slurry of 15% by weight LZ-210, 18% by weight of a pseudobeohmite alumina, 63% by weight kaølin clay, 4% by weight silica and enough water to form a slurry containing 25 percent by weight solids. The slurry was then spray dried calcined and treated by the procedure employed for Catalyst C in example 2. Catalyst F was prepared by forming a slurry of 15% by weight LZ-210, 10% by weight SAPO-5, 18% by weight of a pseudobeohmite alumina, 53% by weight kaolin clay, 4% by weight silica and enough water to form a slurry containing 25% by weight solids. The slurry was then spray dried, calcined and treated by the procedure employed for Catalyst C in example 2. Catalyst E and Catalyst F were each evaluated according to ASTM test method D-3907. The results were as follows: - -- Cata! yst Catalyst E Catalyst F Wt.% Conversion 77 . 2 76 . 8 Wt.% Gasoline + Alkylate 63 . 8 60 . 3 Wt.% Cg-Cg Aromatics 33 . 4 37 . 8 Wt.% Coke 7 . 7 7 . 9 Catalyst/Oil Ra,tio (Weight) 5 3 The above data indicate that Catalyst F, according to this invention, was considerably more active than Catalyst E requiring only a Catalyst/Oil ratio of 3 to achieve a conversion comparable to Catalyst E employed at a Catalyst/Oil ratio of 5. This use of forty percent less catalyst.to achieve comparable conversion demonstrates the surprising increase in activity of the catalyst comprising LZ-210 and SAPO-5. Further, Catalyst F formed products containing ' about 4. ' 4 percent more C 8 -C 8 aromatic products in- the gasoline product with about a 3.5% reduction.in the Wt.% Gasoline + Alkylate. The presence of increased amounts of aromatic products is an indication of higher octane products. Further, aromatic components are valuable as components in other chemical processes. The above data also demonstrate that the order of mixing of the components in Catalyst F resulted in changes in the mixed catalyst, as compared to the mixed catalysts of example 1. The addition of SAPO-5 to the slurry, instead of physically mixing SAPO-5 with a Y zeolite/matrix mixture resulted in a more active catalyst than above described in. example 1 for Catalyst B. The exact reasons for this change in activity as a result of the mixing order is not clearly understood at this time. Example 4 Two catalysts were prepared wherein Catalyst G was a reference catalyst containing ZSM-5 _ (Si0 2 to A1 2 0 3 ratio of 30), as described in U.S. Patent No. 4,239,654, and Catalyst H was a catalyst according to this invention containing SAPO-5. A catalyst base was prepared by rare earth exchanging LZ-210 by use of a solution of a mixture of rare earth chlorides. The rare earth solution contained about 46.0% by weight, expressed on rare earth oxides, with the rare earth component comprising 60.0% lanthanum (La 2 O , 21.5% neodymium (Nd 2 0 , 10.0% cerium (CeOJ, 7.5% praseodymium (PrgO- and about 1.0% other rare earths. The final rare earth exchanged LZ-210 had 9.9% by weight rare earth, measured as the oxide (RE 2 0 3 where "RE" denotes rare earth cations) . A mixture was formed by blending 14.3% by weight of the rare earth LZ-210, 80.7% of a silica-alumina (sold by Davison Division of W..R. Grace under the trademark MS13/110 and containing 86 wt. % Si0 2 and 13 wt. % Al 2 0 3 ) and 5.0% by weight of a microcrystalline cellulose extrusion aid. This mixture was extruded, dried at 110°C in air for 16 hours and then steam deactivated for 5 hours at 760°C in 100% steam. The extrudates were then crushed and sized to 60 to 200 mesh (U.S. Standard). Catalyst G and Catalyst H were prepared by mixing, respectively, 5 percent by weight of ZSM-5 and SAPO-5 with 95 percent by weight of the catalyst base, as above prepared. The two catalysts were evaluated according to ASTM test method D-3907. The results were as follows: Catalyst ' Catalyst G Catalyst H % Conversion: 65.2 66.8 % Gasoline : 42.8 47.3 % g-C- Aromatics in Gasoline: 11.5 14.1 Iso/Normal rati * o (C 6 paraffin) 7.3 11.2 The above data demonstrate the significant improvements in Wt.% Conversion, Wt.% Gasoline, Wt.% Cg-Cg Aromatics in Gasoline and the iso to normal weight ratio of C g paraffins when SAPO-5 is employed as a component of the cracking catalyst as compared to the use of ZSM-5. Example 5 Two catalysts were prepared according to the procedure employed in example 2 'for Catalyst C . and Catalyst D, except that the steam deactivation temperatures were as set forth below in Table I. Catalysts derived from the non-steam deactivated precursor of Catalyst C by changing the steam deactivation temperature are denominated "Catalyst C-n" wherein "n" is an integer. Catalysts derived from the non-steam deactivated precursor of Catalyst D are similarly denominated. The catalysts were evaluated according to ASTM test method D-3907 and the following results obtained: TABLE I Catalyst C C-l C-2 C-3 D D-l D-2 D-3 Steam Deactivation: 765 690 715 740 765 690 715 740 Temperature (°C) Wt.% Conversion: 61.9 74. ' 5 72.1 67.8 62.9 70.5 70.7 66.4 Wt.% Gasoline: 46.5 52.2 52.5 50.2 47.6 51.0 51.3 49.5 C 3 Olefin/ C3 Paraffin Ratio: 2.84 1.47 1.96 2.10 3.79 1.70 2.08 2.54 C_, Olefin/ C3 Paraffin Ratio: 0.55 0.30 0.38 0.42 0.66 0.33 0.40 0.47 σ C Ratios, ό Olefin/paraffin: 0.257 0.075 0.107 0.152 0.265 0.119 0.099 0.170 C Branched/Linear-* * Olefin: 0.64 0.88 1.11 0.49 0.92 0.87 0.96 0.81 C Iso/Normal"-" Paraffin: 13.6 13.0 13.7 13.2 17.1 15.3 15.8 15.1 1 Run Temperature was 850°F instead the 900°F of ASTM test method D-3907. 2 Cβ Branched olefins measured were 2-methyl-2-pentene and 2-methyl-l-pentene. C β linear olefins measured were 1-hexene, trans-2-hexene, cis-2-hexene and trans-3-hexene. 3 C iso-para fins measured were 2-methyl pentane, 3-methyl pentane and 2,2-dimethyl butane. Cg normal paraffin measured was n-hexane. The above data demonstrate that catalysts containing SAPOs retain their selective nature after hydrothermal treatment. The branched to linear olefin weight ratio and the iso to normal paraffin weight ratios were higher at comparable conversions and gasoline yield for the catalysts containing SAPO-ll as compared to catalysts containing no SAPO-11, thus indicating higher octane products. Thus, the advantages derived from use of SAPOs is not significantly affected by hydrothermal deactivation conditions. Example 6 Two catalysts were prepared wherein reference Catalyst J contained a steam stabilized Y zeolite denominated as LZ-10 and a Catalyst K contained LZ-10 and SAPO-ll. LZ-10 was prepared according to U.K. Patent 2,014,970 and was then ammonium exchanged. ' « Catalyst J was prepared by preparing a mixture containing 18% by weight LZ-10, 62% by weight kaolin clay and 20% by weight silica in enough water to form an extrudable mass. This mixture had a paste consistency and was mulled, extruded and calcined at 500°C for 16 hours in air. The extrudates were crushed and sized so as to pass through a 60 mesh screen (U.S. Standard) and not pass through a 200 mesh (U.S. Standard) screen. Catalyst K was prepared as was Catalyst J, except that the initial mixture was 18% by weight LZ-10, 6% by weight SAPO-ll, 56% by weight kaolin clay and 20% by weight silica. - _ __ - The two catalysts were evaluated according to ASTM test method D-3907, except the run temperature was 866°F. All products are given as weight ratios. The results were as follows: W , Catalyst Catalyst J Catalyst K Wt.% Conversion 70.2 69.1 Wt.% Gasoline 50.7 50.1 C 3 01efin/C 3 Paraffin 1.76 1.86 C. 01efin/C 4 paraffin .402 .382 C. Iso/Normal paraffin 4.12 4.64 Wt.% Alkylate 10.9 10.9 Cg olefin/Cg paraffin .154 . 116666 C- iso/normal paraffin 13.4 15.4 C g branched/linear olefin 1.18 1.67 C_ olefin/paraffin .0,769 .086 ♦ 2 C_ iso/normal paraffin 16.9 18.6 C_ branched/linear olefin 2 .739 .799 Cg isoparaffins measured were 2-methyl pentane, 3-methyl pentane and 2,2 dimethyl butane. C g normal paraffin measured was n-hexane. C g branched olefins measured were 3-methyl-l-pen ene, 4-methyl-l-pentene, 2-methyl-l-pentene, 2-methyl-2-pentene and trans-3-methyl-2-pentene. C g linear olefins measured were l-hexene, trans-3-hexene, cis-2-hexene and trans-2-hexene. C_ iso-paraffins measured were 3-methyl hexane, 2-methyl hexane and 2,4-dimethyl pentane. C-, normal paraffin measured was n-heptane. C_ branched olefins measured were determined by measuring all C_ olefins and subtracting from that factor the C_ linear olefins measured. C 7 linear olefins measured were 1-heptene, cis-2-heptene, trans-2-heptene, cis-3-heptene and trans-3-heptene. The above data demonstrate that Catalyst K, according to this invention, provided a gasoline product having higher iso/normal paraffin and branched/linear olefin ratios in the C g and C- hydrocarbons which are indicative of higher octane products and such were formed at comparable gasoline yield and conversion. Comparative Example 7 Two catalysts were prepared wherein reference Catalyst L contained LZ-210 and comparative Catalyst M contained AlP0 4 -5_ and Catalyst L. A1PO.-5 was prepared according to U.S. Patent No. 4,310,440. Catalyst L was prepared by forming a mixture of 15% by weight LZ-210 (Si0 2 to A1 2 0 3 ratio of 9.0), 63% by weight kaolin clay, 18% by weight alumina and 4% by weight silica. The catalyst was extruded and treated similar to the catalysts of example 3 except that the steam deactivation was at 765°C. Catalyst M was prepared by blending 10% by weight of a calcined A1PO.-5 with 90% by weight of Catalyst L. Catalyst L and Catalyst M were evaluated by ASTM test method D-3907. The olefin/paraffin and iso/normal paraffin ratios are given as weight ratios. The results were as follows: Catalyst Catalyst.L Catalyst M Wt.% Conversion 69.9 67.1 Wt.% Gasoline 50.8 48.6 C 3 Ole in/Paraffin 2.87 2.68 C Olefin/Paraffin 0.59 0.57 C4 Iso/Normal Paraffin 4.36 4.36 The above data demonstrate that A1PO 4.-5, having a similar framework to SAPO-5, does not provide the benefits observed when SAPO-5, having Si0 2 tetrahedral framework components, is employed in conjunction with a traditional cracking catalyst. Comparative Example 8 Three catalysts (N, 0 and P) were prepared. Catalysts N and P are comparative catalysts and catalyst 0 is a catalyst prepared according to the instant invention. The catalysts were formed according to the procedure employed in example .1 except that Catalysts O and P employed 54 weight percent kaolin clay and the zeolite and SAPO components were as follows. Catalyst N contained 18 weight percent of an LZ-210 having a Si0 2 to A1 2 0 3 ratio of 9.0. Catalyst O contained 18 weight percent of the LZ-210 employed in Catalyst N and 6 weight percent of SAPO-ll. Catalyst P contained 18 weight percent of .the LZ-210 employed in Catalyst N and 6 weight percent of SAPO-34. Catalysts N, O and P were steam deactivated in 100 percent steam for 2 hours and at 740°C, 740°C and 760°C, respectively, and evaluated according to ASTM test method D-3907. The results of this evaluation were as follows: • So Catalyst Catalyst Catalyst Catalyst N 0 P Wt . % Conversion 72.7 71.5 72.0 Wt . % Gasoline 52.7 51.2 47.7 Wt . % Gas + C 4. s 15.6 15.8 19.5 Wt.% Coke 4.05 4.27 — The above results demonstrate the reduced gasoline yield of catalysts containing SAPO-34. SAPO-34 is not characterized by an adsorption of isobutane of at least 2 percent by weight at a pressure of 500 torr and a temperature of 20°C. Example 9 Two catalysts were prepared for evaluation according to ASTM test method D-3907. The two catalysts were prepared using the silicoaluminophosphate molecular sieve SAPO-5 and the zeolite LZ-210 (Si0 2 to Al 2 0 3 ratio of 9.0). After preparation of SAPO-5 the material was steam deactivated in 100 percent steam at 760°C for 2 hours to simulate the effect of actual use in a cracking process. The LZ-210 component was then rare earth exchanged with a mixture of rare earth chlorides, as described in example 4, to give a rare earth exchanged LZ-210 containing 9.9 weight percent rare earth, expressed as the oxide. A matrix for the SAPO-5 and LZ-210 was prepared by mixing 90 percent by weight of a silica/alumina, sold by the Davison Division of W.R. Grace under the trade designation MS13/110, and 10 percent by weight of a microcrystalline cellulose extrusion aid. The mixture was extruded in the form of 1/16 inch pellets and dried in air at 110°C for about 16 hours and then steam deactivated in 100 percent steam at 760°C for 2 hours. The steam deactivated material was then crushed and sized to 60 to 200 mesh 4 (U.S. Standard). The SAPO-5 and LZ-210 catalysts were each prepared by mixing 15 percent by weight of .the selected material with 85 percent by weight of the matrix. The LZ-210 was steam deactivated in 100% steam at 760°C for 2 hours prior to use in the preparation of the catalyst. The final catalyst mixtures were then calcined at 590°C in air for 3 hours. Each catalyst was evaluated for conversion according to ASTM test method D-3907. The results of the-evaluation were as follows: W ' Catalyst SAPO- -5 LZ-210 Wt.% Conversion 57.7 57.2 Wt.% Gasoline 37.2 41.4 Wt.% Gas 6.6 5. .5 Wt.% Coke 3, .9 3.1 The above results demonstrate the individual activity of SAPO-5 and LZ-210 as cracking catalysts. Although LZ-210 showed a higher Wt.% - - Gasoline, SAPO-5 formed more gas products and C. products under the conditions of ASTM test method D-3907. As observable from the above examples according to the instant invention, the use of a catalyst comprising a traditional cracking catalyst and a SAPO provide products having different components than the products obtained by use of a SAPO or LZ-210 separately. Example 10 A catalyst is prepared according to the procedure described in example 1 for Catalyst B, except MgAPSO-5 is employed in place of SAPO-5. The catalyst is tested according to ASTM test method D-3907 and gives products having a product distribution different from the product distribution obtained by use of catalyst A. ? • Example 11 Two catalysts are prepared according to the procedure described in example 1 for catalyst B, except that one catalyst contains MnAPSO-34 in place of SAPO-5 and one catalyst contains MnAPSO-11. MnAPSO-11 is characterized by a isobutane adsorption as described according to this invention, whereas MnAPSO-34 is not so characterized. Evaluation by ASTM test method D-3907 shows the catalyst containing MnAPSO-11 has to the catalyst containing MnAPSO-34 cracking activity to gasoline products superior to the catalyst containing MnAPSO-34. Example 12 Two catalysts are prepared according to the procedure described in example 1 for catalyst B except that one catalyst contained MnAPO-ll and one catalyst contained MgAPO-5 in place of SAPO-5. Evaluation by ASTM test method D-3907 provides products different from the product distribution obtained using Catalyst A of example 1.

Claims: WHAT IS CLAIMED IS: 1. The process for cracking a crude oil feedstock to produce lower boiling hydrocarbons comprising contacting at effective catalytic cracking conditions a crude oil feedstock with a conversion catalyst comprising effective amounts of at least one NZ-MS characterized in its calcined form by an adsorption of isobutane of at least 2 percent by weight at a pressure of 500 torr and a temperature of 20°C. 2. The process of claim 1 wherein said NZ-MS is further characterized in its calcined form by an adsorption of triethylamine of at least 5 percent by weight at a pressure of 2.6 torr and a temperature of 22°C. 3.. The process of claim 1 wherein said catalyst contains an effective amount of,at least one zeolitic aluminosilicate having cracking activity in a weight ratio between about 1:10 and about 500:1 of said zeolitic aluminosilicate to said NZ-MS molecular sieve and from 0 and about 99 weight percent of at least one inorganic oxide matrix component, based on the total weight of said catalyst. 4. The process of claim 3 wherein said NZ-MS is further characterized in its calcined form by an adsorption of triethylamine of less than 5 percent by weight at a pressure of 2.6 torr and a temperature of 22°C. - O - 5. The process of claim 3 wherein the weight ratio of zeolitic aluminosilicate to said NZ-MS is between about 1:2 and about 50:1. 6. The process of claim 5 wherein the weight ratio of zeolitic aluminosilicate to said NZ-MS is between about 1:1 and about 20:1. 7. The process of claim 3 wherein inorganic oxide component is present in an amount between about 5 and about 95 percent by weight, based on the total weight of said catalyst. 8. The process according to claim 3 wherein said zeolite component of the conversion catalyst contains an effective amount of a cation selected from the group consisting of ammonium. Group IIA, Group IIIA, Groups IIIB to VIIB, cerium, lanthanum, praseodymium, neodymium, promethium, samarium, europium, gadolinium, terbium, dysprosium, holmium, erbium, thulium, ytterbium, lutetium and mixtures thereof. 9. The process of claim 1 wherein said NZ-MS has at least part of its cations as hydrogen-forming species. 10. The process of claim 9 wherein said hydrogen-forming species is NH. or H . 11. The cracking process of claim 1 wherein the process is carried out by contacting crude oil feedstock boiling between 420°F and about 1800°F with the conversion catalyst at a temperature between about 400°F and about 1600°F, at a pressure between " about 14.7 psig to about 100 psig. 12. The process of claim 8 wherein said conversion catalyst contains between about 0.1 percent and about 20 weight percent of said multivalent cations. 13. The process of 7 wherein said inorganic oxide matrix component is selected from the group consisting of clays, silicas, aluminas, silica-aluminas, silica-zirconias, silica-magnesia, alumina-borias, alumina-titanias and mixtures thereof. 14. The process of claim 1 or 3 wherein said NZ-MS is selected from the group consisting of CoAPSOs, FeAPSOs, MgAPSOs, MnAPSOs, TiAPSOs, ZnAPSOs, CoMgAPSOs-, CoMnMgAPSOs, MeAPOs, TiAPOs, FeAPOs, FCAPOs and mixture thereof. 15. The process of claim 1 or 3 wherein said NZ-MS is selected from the group consisting of CoAPSOs, FeAPSOs, MgAPSOs, MnAPSOs, TiAPSOs, ZnAPSOs, CoMgAPSOs, CoMnMgAPSOs and mixtures thereof 16. The process of claim 1 or 3 wherein said NZ-MS is selected from the group consisting of ELAPSO-5, ELAPSO-11, ELAPSO-31, ELAPSO-37, ΞLAPSO-40, ELAPSO-41, and mixtures therof. 17. The process of claim 16 wherein said NZ-MS is selected from the group consisting of CoAPSO-5, CoAPSO-11, CoAPSO-31, CoAPSO-37, CθAPSO-40, CoAPSO-41, FeAPSO-5 " , FeAPSO-11, FeAPSO-31, FeAPSO-37, FeAPSO-40, FeAPSO-41, MgAPSO-5, MgAPSO-11, MgAPSO-31, MgAPSO-37, MgAPSO-40, MgAPSO-41, MnAPSO-5, MnAPSO-11, MnAPSO-31, MnAPSO-37, MnAPSO-40, MnAPSO-41, TiAPSO-5, TiAPSO-11, TiAPSO-31, TiAPSO-37, TiAPSO-40, TiAPSO-41, ZnAPSO-5, ZnAPSO-11, ZnAPSO-31, ZnAPSO-37, ZnAPSO-40, ZnAPSO-41, CθMgAPSO-5, CθMgAPSO-11, CoMgAPSO-31, CoMgAPSO-37, CoMgAPSO-40, CoMgAPSO-41, CoMnMgAPSO-5, CoMnMgAPSO-11, CoMnMgAPSO-31, CoMnMgAPSO-37, CoMnMgAPSO-40, CoMnMgAPSO-41 and mixtures thereof. 18. The process of claim 1 or 3 wherein siad NZ-MS is selected from the group consisting of MeAPO-5, MeAPO-11, MeAPO-31, MeAPO-37, MeAPO-40, MeAPO-41, TiAPO-5, TiAPO-11, TiAPO-31, TiAPO-37, TiAPO-40, TiAPO-41, FeAPO-5, FeAPO-11, F.eAPO-31, FeAPO-37, FeAPO-40, FeAPO-41, FCAPO-5, FCAPO-11, FCAPO-31, FCAPO-37, FCAPO-40, FCAPO-41. and mixtures thereof. 19. The process of claim 18 wherein "Me" is selected from the group consisting of cobalt magnesium, manganese, zinc and mixtures thereof. 20. The process of claim 18 wherein "Me" is selected from the group consisting of magnesium, manganese and mixtures thereof. 21. The process of claim 1 wherein said crude oil feedstock is selected from the group consisting of distillate gas oils, heavy vacuum gas oils, VGO, atmospheric resids, vacuum resids, syncrudes, pulverized coal and mixtures thereof. 22. The process of claim 3 wherein said zeolitic aluminosilicate is selected from the group consisting of zeolite Y, zeolite X, zeolite beta, zeolite KZ-20, faujasite, LZ-210, LZ-10, ZSM-type zeolites and mixtures thereof. 23. The process ' of claim 4 wherein said zeolitic aluminosilicate is selected from the group consisting of zeolite Y, zeolite X, zeolite beta, zeolite KZ-20, faujasite, LZ-210., LZ-10, ZSM-type zeolities and mixtures thereof. 24. The process for the preparation of a catalyst comprising: a) forming a mixture of at least one zeolitic aluminosilicate and at least one NZ-MS characterized in its calcined form by an adsorption of isobutane of at least 2 percent by weight at a pressure of 500 torr and a temperature of 20°C a.t a weight ratio of between .about 1:10 and about 500:1, respectively; b) forming a mixture of the product of step a) and at least one inorganic oxide matrix component to form a catalyst. 25. The process for the preparation of a catalyst comprising: a) forming a mixture of at least one inorganic oxide matrix component and at least one zeolitic aluminosilicate; b) forming a mixture of at least one inorganic oxide matrix component and at least one NZ-MS characterized in its calcined form by an - - adsorption of isobutane of at least 2 percent by weight at a pressure of 500 torr and a temperature of 20°C; and c) forming a mixture of the products of steps a) and b) to form a catalyst having a weight ratio of zeolitic aluminosilicate to NZ-MS between about l > :10 and about 500:1. 26. The catalyst prepared by the process of claim 24. 27. The catalyst prepared by the process of claim 25. 28. A catalyst comprising at least one zeolitic aluminosilicate having cracking activity and at least one NZ-MS characterized in its calcined form by an adsorption of isobutane of at least 2 percent by weight at a pressure of 500 torr and a temperature of 20°C wherein the weight ratio between said aluminosilicate and NZ-MS is between about- 1:10 and about 500;1. W 29. The catalyst of claim 28 wherein said NZ-MS molecular sieve is further characterized in its calcined form by an adsorption of triethylamine of less than 5 percent by weight at a pressure of 2.6 torr and a temperature of 22°C. 30. The catalyst of claim 29 wherein said NZ-MS is further characterized in its calcined form by an adsorption of triethylamine of at least 5 percent by weight at a pressure of 2.6 torr and a temperature of 22°C. r 31. The catalyst of claim 28, or claim 29 or claim 30 wherein said zeolitic aluminosilicate is selected from the group consisting of zeolite Y, zeolite X, zeolite beta, zeolite KZ-20, faujasite, LZ-210, LZ-10, ZSM-type zeolites and mixtures thereof. 32. The catalyst of claim 28 wherein said catalyst contains from 1 to 99 percent by weight of at least inorganic oxide matrix component. 33. The catalyst of claim 32 wherein the inorganic oxide matrix component is selected from the group consisting of clays, silicas, aluminas, silica-aluminas, silicas-zirconias, silica-magnesia, alumina-borias, alumina-titanias and mixtures thereof. 34. The catalyst of claim 28 wherein said NZ.-MS is selected from the group consisting of ELAPSO-5, ELAPSO-11, ELAPSO-31, ELAPs5-37, ELAPSO-40, ELAPSO-41 and mixtures thereof. 35. The catalyst of claim 28 wherein said zeolitic aluminosilicate is selected from the group consisting of Y zeolite, LZ-210, LZ-10 and mixtures thereof and said silicoaluminophosphate is selected from the group consisting of ELAPSO-5, ELAPSO-11, ELAPSO-31, ELAPSO-37, ELAPSO-40, ELAPSO-41 and mixtures thereof. 36. The catalyst of claim 28 wherein said zeolitic aluminosilicate contains between about 0.1 - *6 - and about 20 percent by weight of a cation selected from the group consisting of ammonium. Group IIA, Group IIA, Groups II B to VII B, rare earth and mixtures thereof.

Inventors: COUGHLIN PETER KEVIN, LONG GARY NORMAN, PELLET REGIS JOSEPH, RABO JULE ANTHONY, STANIULIS MARK THOMAS, COUGHLIN, PETER, KEVIN, LONG, GARY, NORMAN, PELLET, REGIS, JOSEPH, RABO, JULE, ANTHONY, STANIULIS, MARK, THOMAS
Applicants: UNION CARBIDE CORP, UNION CARBIDE CORPORATION
Application year: 1985
Main classification: B01J29
IPC codes: B01J29, B01J37, C10G11