METHODS OF AND APPARATUS FOR FORMING CONDUCTIVE PATTERNS ON A SUBSTRATE

Abstract: A method of forming an electrically conductive pattern on a substrate includes the steps of forming a layer of gold (6) on an electrically insulating substrate (2) and coating the gold layer (6) with a photo-resist (8). The resist (8) is exposed to light through a photo mask and the exposed portions of the photo-resist (8) are selectively removed by etching. The now exposed parts of the gold layer (6) are coated with copper (12) and the remaining photo-resist (8) is removed. The exposed parts of the gold layer (6) and the copper (12) are subjected to molten tin (14) which simultaneously acts to dissolve the exposed parts of the gold layer (6) and to form an electrically conductive coating on the copper (12). The process enables the formation of a precise conduc­ tive pattern with enhanced reliability.

Description: The present invention relates to methods of forming conductive patterns on a substrate. European Patent No 0 080 169 discloses a method of manufacturing printed circuits in which a non conductive plate is coated with a metallic layer. A coating preventing metalisation is selectively applied to the metallic layer and the metallic layer is then built up on the uncoated regions to provide reinforced conductive paths. The metallisation preventing coating is removed and the exposed metal is etched away to leave a reinforced pattern of conductive paths. It has been proposed to produce conductive strips on a substrate to form connections between integrated circuits. Such conductive strips are of low cost metals such as copper and tin and are formed on a ceramic substrate or a multi-layered substrate including glass or glass-ceramic materials. One process for forming such conductors is to etch a solid film of conductor formed on a substrate. With such etching techniques, however, the etching fluid tends to undercut the conductors and so there is a limit to the width to which such conductors can in practice be formed. Also etching techniques are wasteful of materials and disposal of the waste products can be difficult. Another method of forming conductors is to screen print the conductors on the substrate. In practice, however, the resolution of screen printing is limited and so again this places a limit on the width of and spacing between the conductors which can be formed on a substrate. A still further method of forming conductors on a substrate is by means of an additive method using a plating or lift-off evaporation process. Again in practice such techniques either require the extensive use of aqueous processes, which is undesirable, or require high cost equipment to achieve high accuracy. It is an object of the invention to provide a high resolution method of forming a conductive pattern on a substrate. According to the present invention, there is provided a method of forming a conductive pattern on a substrate comprising the steps of, coating the substrate with a first electrically conductive material to form a first layer, forming a resist pattern on the first layer, depositing a second electrically conductive material on the parts of the first layer not covered by the resist pattern, removing the resist pattern and temporarily subjecting the now exposed parts of the first layer and the deposits of said second conductive material, with a third electrically conductive material in its molten state, the third electrically conductive material being such that when in its molten state it acts simultaneously to dissolve the first conductive material and to provide a coating on said second electrically conductive material. According to the present invention, there is further provided a method of forming an electrically conductive pattern on a substrate comprising the steps of: forming a layer of gold or silver on an electrically insulating substrate; coating said gold or silver layer with a photo-resist; exposing the photo-resist to light through a photo mask; selectively removing the exposed portions of the photo-resist; coating the now exposed parts of the gold or silver layer with a second electrically conductive material other than gold or silver; removing the remaining photo-resist; and subjecting the exposed parts of the gold or silver layer and the said second electrically conductive material to a third electrically conductive material in molten form, the third electrically conductive material being such that it simultaneously acts to dissolve the exposed parts of the gold or silver layer and form an electrically conductive coating on the second electrically conductive material. conductive material. Methods of forming conductive patterns on a substrate and embodying the invention will now be described by way of example, with reference to the accompanying diagrammatic drawings, in which :- Figures 1 to 5 are fragmentary sections through a substrate at different stages of the process; Figure 6 is a front elevation of the apparatus for performing the last stage of the process illustrated in Figure 5; and Figures 7 to 11 are fragmentary sections through a multilayer system at different stages of the process. As shown in Figure 1, an inorganic substrate 4 of a ceramic, glass, glass-ceramic material is coated with 0.2 micrometers thick layer 6 of gold. This gold layer 6 is formed by screen printing a mixture of a gold metallorganic material (an organic material having gold radicals) and a base metal metall-organic material (which forms a metal oxide on heating) to coat the whole surface of this substrate. The assembly is then fired in an oven to release the organic materials and leave the gold deposited as a layer 6 on the substrate. The adherence of the gold layer 6 to the substrate is effected by the aforesaid metal oxide. A photo-resist is then deposited as a layer to cover the gold layer 6. The photo-resist layer can be formed by laminating a dry film resist on to the layer 6 or coating the layer 6 with a wet film resist and then drying. The photo-resist layer is then selectively exposed to light through a photo mask (not shown) defining a desired pattern and etched to leave the pattern 8 (see Figure 2). In this particular instance, the pattern is in the form of a plurality of parallel strips 10. The assembly is then plated with copper. Since the resist strips 10 are electrically insulating and the exposed gold layer 6 is electrically conductive, electro-plating or electroless plating with copper will only deposit a copper layer on the exposed parts of the gold layer. Accordingly, a series of copper strips 12 are formed between the strips 10 of the etched resist layer 8 (see Figure 3). A solvent is used to remove the strips 10 of the resist material so as to leave (as shown in Figure 4) a gold layer 6 carrying a conductive pattern of copper. The assembly is then dipped for a period of a few seconds in molten tin which will dissolve the exposed parts of the gold layer and simultaneously coat the strips 12 of copper with a layer of tin 14. The resultant board with its tin plated copper conductors or tracks is ready for soldering to integrated circuits and the like. Figure 6 shows the apparatus used for simultaneously dissolving the exposed parts of the gold layer and coating the copper conductors or tracks with tin. As shown, a stainless steel container 20 is supported on a heater 22 incorporating a heating element 24. The container 20 is covered by lid 26 having a slotted opening 28 through which an assembly 30 can be introduced in the container and then subsequently withdrawn. The container 20 is partly filled with a fluorinated hydrocarbon 32, such as for example Fluorinert FC 71 manufactured by 3M's. This hydrocarbon has a boiling point of approximately 250°C. A stand 34 supports a ceramic vessel containing pure tin 38, above the level of the liquid hydrocarbon 32. A cooling coil 40 is located in the upper region of the container 20. In operation, the heating coil 24 of the heater is energised to heat the container to a temperature of at least 250°C. At this temperature the fluorinated hydrocarbon boils to fill the volume of the container above the level of the liquid with hot vapour. This hot vapour heats the vessel 36 and the tin therein (which has a melting point of about 230°C), to cause the tin to melt and so provide a bath of molten tin. Any vapour reaching the upper extremity of the container is condensed by the cooling coil 40 and returned to the liquid at the bottom of the container. At this point, the assembly 28, held by a pair of tongs 42 or other support members, is lowered through the opening 28. As it passes into the container 20, it is initially heated by the vapourised hydrocarbon which also acts to inhibit oxidation. Eventually the assembly 30 is immersed in the molten tin for a period sufficient to dissolve the gold and coat the copper conductors with tin. The board is then withdrawn from the bath of molten tin and up through the opening in the lid 26 of the container and left to cool. Because the assembly passes through the hot vapour phase of the hydrocarbon, both before and after being immersed in the molten tin, the pre-heating and pre-cooling action effected by the vapour is conducive to the formation of a thin layer of tin, thereby reducing the risk of the tin bridging the conductors, and reduces the risk of thermal shock to the assembly and therefore damage to the conductors. It will be appreciated that instead of pure tin, a tin based compound can be used, for example a tin/lead,tin/silver alloy or tin/lead/silver alloy. The alloys can also include the elements of Bismuth, Antimony or Indium. In a modification a fluid such as Arklone P (Registered Trade Mark of ICI) or Freon TF (Registered Trade Mark of DuPont) is added to the fluorinated hydrocarbon so that when heated a vapour layer of this material floats on top of the vapourised fluorinated hydrocarbon. This acts to reduce the loss of the fluorinated hydrocarbon from the system. It has been found that with the above described method to produce a series of parallel conductors providing connections between integrated circuits, a particularly high density of conductors has been achieved. Specifically, conductors 20 micrometers thick, 30 micrometers wide, having a spacing of 30 micrometers between conductors, has been consistently achieved with a particularly low failure rate. Narrower conductors and narrower spacings can be achieved with the above described method. It will be appreciated that the use of metallorganic materials to produce a gold layer eliminates the need for either aqueous processing or expensive thin film processing to produce a seed layer. The oxide-glass forming adhesive mechanism between the gold and the substrate, gives a high adhesion, even to glass surfaces. The use of molten tin to dissolve the exposed gold portions eliminates the need for removing a seed layer with ionic aqueous fluids. The use of such fluids generally introduces a reliability hazard. The tinned copper conductors produced by the described method, avoid the need for subsequent preparatory operations such as would be needed when reflowing chip carriers and performing similar operations. It will be appreciated that instead of gold, silver can be used to provide the layer 6. The gold or silver may be alloyed with up to 25% platinum or other material to reduce metal migration or the solubility in the tin. In a modification, following the plating step shown in Figure 2 in which conductors 12 are formed by plating between the strips of resist 10, a further layer of resist is deposited to cover the existing resist strips 10 and the conductors and further selective etching takes place to expose selected ones of the conductors 12 and to keep others covered. A second plating operation is effected and the resist is then removed as shown in Figure 4. The result is that some conductors 12 (which can be used to carry power current) will be thicker than other conductors 12 (which can be used to carry signals). The definition of conductors achieved with this arrangement is high. In yet another modification where a multilayer structure is required the processes may be used to form the top conductive layer of the structure. This is more clearly shown in Figures 7 to 11. As shown in Figure 7, an inorganic substrate 12 of a ceramic, glass, glass-ceramic material supports a multilayer structure. The structure includes a conductive pattern 15 (which may have been formed by thick film plating or cofired ceramic methods for example). The conductive pattern 15 is coated with an insulating layer 14 which is then fired. Through holes 17 are provided in the insulating layer 14 to expose the underlying conductor. The structure is coated with a 0.2 micron thick layer 16 of gold. This gold layer 16 is formed by screen printing a mixture of a gold metallorganic material (an organic material having gold radicals) and a base metal metall-organic material (which forms a metal oxide on heating) to coat the whole surface of the layer 14 and the through holes 17. The assembly is then fired in an oven to release the organic materials and leave the gold deposited as a layer 16 on the insulating layer 14. The adherence of the gold layer 16 to the layer 14 is effected by the aforesaid metal oxide. A photo-resist is then deposited as a layer to cover the gold layer 16. The photo-resist layer can be formed by laminating a dry film resist on to the layer 16 or coating the layer 16 with a wet film resist and then drying. The photo-resist layer is then selectively exposed to light through a photo mask (not shown) defining a desired pattern and etched to leave the pattern 18 (see Figure 8). In this particular instance, the pattern is in the form of a plurality of parallel strips 110. The assembly is then plated with copper. Since the resist strips 110 are electrically insulating and the exposed gold layer 16 is electrically conductive, electro-plating or electroless plating with copper will only deposit a copper layer on the exposed parts of the gold layer. Accordingly, a series of copper stripe 112 are formed between the strips 110 of the etched resist layer 18 (see Figure 9). A solvent is used to remove the strips 110 of the resist material so as to leave (as shown in Figure 10) a gold layer 16 carrying a conductive pattern of copper. The assembly is then dipped in molten tin which will dissolve the exposed parts of the gold layer and simultaneously coat the strips 112 of copper with a layer of tin 114. The resultant multilayer board with its tin plated copper conductors or tracks on the top surface is ready for soldering to integrated circuits and the like.

Claims: A method of forming a conductive pattern on a substrate comprising the steps of, coating the substrate with a first electrically conductive material, to form a first layer; forming a resist pattern on the first layer; depositing a second electrically conductive material on the parts of the first layer not covered by the resist pattern; removing the resist pattern; and temporarily subjecting the now exposed parts of the first layer and the deposits of said second conductive material with a third electrically conductive material in its molten state, the third electrically conductive material being such that when in its molten state it acts simultaneously to dissolve the first conductive material and to provide a coating on said second electrically conductive material. A method according to Claim 1, wherein said first electrically conductive layer comprises gold or an alloy thereof. A method according to Claim 1, wherein said first electrically conductive layer comprises silver or an alloy thereof. A method according to any preceding Claim, wherein said second electrically conductive material comprises copper. A method according to any preceding Claim, wherein said third electrically conductive material is selected from the group consisting of tin, an alloy of tin and silver, an alloy of tin and lead, and an alloy of lead silver and tin. A method according to any preceding Claim, including the steps of: increasing the thickness of selected parts of the deposited second electrically conductive material by forming a further resist pattern following the deposit of the second electrically conductive material, but prior to the removal of the resist pattern; and subjecting the parts of the second electrically conductive material not covered by the further resist pattern, to a further deposit of said second electrically conductive material. A method of forming an electrically conductive pattern on a substrate comprising the steps of: forming a layer of gold or silver on an electrically insulating substrate; coating said gold or silver layer with a photo-resist; exposing the photo-resist to light through a photo mask; selectively removing the exposed portions of the photo-resist; coating the now exposed parts of the gold or silver layer with a second electrically conductive material other than gold or silver; removing the remaining photo-resist; and subjecting the exposed parts of the gold or silver layer and the said second electrically conductive material to a third electrically conductive material in molten form, the third electrically conductive material being such that it simultaneously acts to dissolve the exposed parts of the gold or silver layer and form an electrically conductive coating on the second electrically conductive material. A method according to Claim 7, wherein the step of coating the exposed parts of the gold or silver layer with said second electrically conductive material is performed by an electro-plating method. A method according to Claim 7, wherein the step of coating the exposed parts of the gold or silver layer with said second electrically conductive material is performed by an electroless plating method. A method according to any one of Claims 7 to 9, wherein the step of forming a layer of gold or silver comprises the steps of: screen printing a mixture of a gold or silver metallorganic and a metal oxide forming material on said substrate and then heating to fire said mixture, whereby the metal oxide formed upon firing adheres said gold or silver layer to said substrate. A method according to Claim 10, wherein said step of forming the gold or silver layer comprises forming a gold or silver layer less than 0.5 micrometers thick. A method according to any one of Claims 7 to 11, wherein the step of subjecting the exposed parts of the gold or silver layer and the second electrically conductive material to said third electrically conductive material comprises the steps of: pre-heating the substrate and all that it carries, in an atmosphere which inhibits oxidation; immersing the substrate in a molten bath of said third electrically conductive material; and withdrawing the substrate back through said atmosphere. A method according to Claim 12, wherein said atmosphere is used to heat said third electrically conductive material to its molten state. A method according to any one of Claims 7 to 13, wherein said third electrically conductive material is selected from the group consisting of tin, a tin/lead alloy, a tin/silver alloy and a tin/lead/silver alloy.

Inventors: MORAN, PETER LESLIE
Applicants: MORAN, PETER LESLIE
Application year: 1985
Main classification: H05K3
IPC codes: H05K3, C23F4, C23C2