STRUCTURAL ADHESIVE COMPOSITIONS, THREE COMPONENT REDOX CATALYST SYSTEMS AND THEIR USE IN BONDING METAL SURFACES TOGETHER

Abstract: Two-package, equal-mix acrylic adhesive compositions are provided, containing as a curing agent a mixture of peroxygen compound, an organic thiol and certain metal ion-containing compounds. Also provided is a three-­ component oxidation-reduction catalyst system consisting of an organic hydroperoxide, an organic thiol and an inorganic or organic compound of a metal having a standard reduction potential of from +0.9 to -0.5

Description: STRUCTURAL ADHESIVE COMPOSITIONS, THREE COMPONENT REDOX CATALYST SYSTE2wIS AND THEIR USE IN BONDING METAL SURFACES TOGETHER Field of the Invention The present invention relates to structural adhesive compositions. More particularly, the invention relates to equal mix, multi-pack acrylic structural adhesive compositions which are particularly useful for bonding metal substrates. Structural adhesive compositions, such as anue obic and nonanaerobic acrylic, urethane, epoxy and cyanoacrylate adhesives1 are well known articles of commerce which are extensively used commercially for bonding metal and plastic materials. The load-bearing and stressrelieving properties of structural adhesives, as well as their bond strength1 which can exceed the strength of the engineering materials which are being bonded, make these adhesives attractive alternatives to or replacements for mechanical methods, such as riveting or spot welding, cf joining engineering materials, especially where it is preferaDle to distribute load stresses over larger areas rather than to concentrate such stresses at a few points. Their use can reduce or eliminate costly finishing operations necessitated by mechanical joining methods, present a more pleasing exterior and at least reduce the possibility of corrosion of assemblies containing one or more metal components. Additionally, they can be used to bond a diversity of metals without extensive surface preparation. For example, Zalucha et al U.S.A. Patent 4,223,115 and Briggs et al U.S.A. Patent 3,890,407 disclose acrylic structural adhesive compositions which are effective bonding materials for oily metal surfaces. Among the aifferent types of structural adhesives, the acrylic structural adhesives are extremely attractive because they provide very strong bonds with both plastic and metal materials, even though a particular adhesive may not have the capability of bonding both types of materials. The acrylic structural adhesives typically comprise a mixture of one or more olefinically-unsaturated reactive monomers and curing agents, with cure being effected through a free radical polymerization mechanism. The adhesives preferably contain one or more polymeric materials which may or may not be reactive, that is, capable of being polymerized per se or at least capable of interpolymerizing with the reactive monomers, such as grafting onto or crosslinking the growing polymers from the reactive monomer polymerization. In addition, the adhesives can contain other additives for improving adhesion to substrate materials, environmental resistance, impact resistance, flexibility, heat resistance and the like. However, despite their many advantages, the acrylic structural adhesives do have certain characteristics which have tended to inhibit moreSwidespread visage. Among these characteristics are an unpleasant odor, a low flash point which imposes undesirable restrictions on shipping and handling of the adhesives, a disparate mix ratio which presents problems with respect to accuracy in and compatibility with machine dispensing and a cure time which is incompatible, that is, either too slow or too fast, with many applications. While it has been possible to overcome one or more of these negatives with some measure of success, such efforts have always been left with at least one undesirable characteristic. During the course of extensive investigations directed to the problems of odor, flash point, mix ratio and cure rate, it became evident that a new curing agent was a necessity, particularly if the room temperature cure capability of the adhesives were to be maintained. It became equally evident that just providing an equal mix adhesive would require a new curing agent, if the performance characteristics of the disparate mix acrylic adhesives were to be equalled. In accordance with the present invention, there are now provided two-part acrylic structural adhesive compositions wherein the separate parts can be admixed in equal amounts, by volume or weight1 and which provide performance characteristics which equal or surpass those of the previously known disparate mix two-part acrylic adhesive composItions. The two-pack acrylic adhesive compositions of the invention are unexpectedly tolerable to, wide variations in mix ratio, that is, the adhesives are curable at mix ratios other than unity (as well as at unity) with no sub stantial loss in adhesion performance, thus reducing the need for constant calibration of mixing orifices. In addition, the adhesive compositions of the invention allow the fonsulator to more successfully address the problems of odor, flash point and cure rate in his attempts to more fully meet the needs of his customers. The invention also provides a novel, three-component oxidation-reduction catalyst system comprising from 0.05 to 10, preferably 0.2 to 3, most preferably 0.5 to 1.5 parts by weight of at least one organic hydroperoxide; from 0.005 to 2, preferably 0.05 to 1, most preferably 0.1 to 0.5, parts by weight of at least one organic thiol; and from 0.005 to 1, preferably 0.01 to 0.5, most preferably 0.01 to 0.25 of at least one inorganic or organic compound of a metal having a standard reduction potential in the range from +0.9 to -0.5. More particularly, there are provided novel two-part acrylic structural adhesive compositions comprising at least one olefinically unsaturated reactive monomer and a three component curing agent comprising.at least one peroxygen compound selected from the group consisting of hydrogen peroxide, organic hydroperoxides and organic peroxyesters; at least one thicl, and at least one organic or inorganic compound containing certain metal ions. The three component curing agent which must be employed in the practice of this invention unexpectedly permits each of the two packs to be admixed by equal volume or weight without an adverse effect on adhesive performance or shelf stability and also permits the formulator to more effectively modify the acrylic adhesives to the user' 5 needs. The novel acrylic structural adhesive compositions of the invention comprise, in combination (A) at least one olefinically unsaturated monomer; (B) at least one polymeric material selected from the group consisting of (1) at least one olefinically unsaturated urethan reaction product of at least one isocyanate-functional prepolymer and at least one hydroxy-functional monomer having at least one unit of polymerizable olefinic unsaturation, such reaction product being characterized by the presence of at least two units of olefinic unsaturation and the substantial absence of free isocyanate groups; (2) at least one butadiene-based elastomeric polymeric material selected from the group consisting of (a) homopolymer of butadiene; ; (b) copolymer of butadiene and at least one monomer copolymerizable therewith selected from the group consisting of styrene, acrylonitrile, methacrylonitrile and mixtures thereof; (c) modified elastomeric polymeric material selected from the group consisting of butadiene homopolymer and copolymer as previously defined, such homopolymer and copolymer having been modified by copolymerization therein of trace amounts up to 5 percent by-weight, based on weight of modified elastomeric polymeric material, of at least one functional monomer; and (d) mixtures thereof; (3) at least one polymer-in-monomer syrup consisting essentially of - (b) from 2 to 90 percent by weight of at least-one polymer derived from such (3)(a) monomers; and (a) from 10 to 98 percent by weight of at least one olefinically unsaturated monomeric compound having at least one - C : C group; (c) from O to 30 percent by weight of a polymer containing the group (CH2CC1 : CHCH2)n, wherein n is an integer; wherein (3)(b) is present as a partial polymerization product of (3)(a) or of (3)(a) in the presence of (3)(c); the mixture of (3)(a) and (3)(b) or of- (3)(a), (3)(b) and (3)(c) being a syrup of polymer dissolved or dispersed in unpolymerized monomer, in which syrup the amount of (3)(b) derived from (3)(a) is in the range from 2 to 90 percent by weight, based on the total weight of (3)(a), (3)(b) and (3)(c). (4) at least one polymeric material selected from the group consisting of polyvinyl alkyl ether, styrene-acrylonitrile resin, unsaturated polyester resin and mixtures thereof, the alkyl moiety of such ether containing from one to 8 carbon atoms; (5) at least one homopolymer or copolymer of at least one monomer selected from the group consisting of styrene and alkyl or hydroxyalkyl esters of acrylic or methacrylic acid, said ester having from one to 18 carbon atoms in the alkyl moiety; and (6) at least one polymeric material having at least one terminal olefinically unsaturated group, said polymeric material being selected from the group consisting of, (1) at least one adduct of at least one ethylenically unsaturated monofunctional isocyanate and at least one polymeric material containing one or more active hydrogen atom-containing moiety(ies) selected from the group consisting of -0H, -NH2, H-, EMI5.1 -SH and -COOH; and, (2) at least one adduct of at least one reactive monomer having at least -one terminal olefinically unsaturated group and at least one reactive moiety selected from the group consisting of -0H, -HN2, 4IH-, EMI5.2 -SH and -C00H, and at least one polymeric material which contains at least one moiety which is reactive with said reactive moiety of said reactive monomer, provided that, when said reactive moiety is -0H, said polymeric material does not contain a reactive -NCO group; and (7) mixtures of such polymeric materials; and (C) a redox catalyst curing agent comprising (1) at least one peroxygen compound selected from the group consisting oj hydrogen peroxide, organic peroxyesters and organic hyaroperoxides; (2) at least one organic sulfur-containing compound having at least one -SH group or having a tautomeric form containing at least one -SH group; and, (3) at least one inorganic or organic compound of a metal ion, said metal ion having a standard reduction potential in the range from +0.9 to -0.5. The free radical-polymerizable acrylic structural adhesive compositions of the invention are normally provided as two-package adhesive systems, with equal amounts, by weight or volume, of the package being mixed at the time of use. These adhesive compositions comprise (I) a first package comprising (A) at least one olefinically unsaturated monomer; (B) at least one polymeric material selected from the group consisting of (1) at least one olefinically unsaturated urethane reaction product of at least one isocyanate-functional prepolymer and at least one hydroxy-functional monomer having at least one unit of polymerizable olefinic unsaturation, such reaction product being characterized by the presence of at least two units of olefinic unsaturation and the substantial absence of free isocyanate groups; ; (2) at least one butadiene-based elastomeric polymeric material selected from the group consisting of (a) homopolymer of butadieme; (b) copolymer of butddiene and at least one monomer copolymerizable therewith selected from the group consisting of styrene, acrylonitrile, methacrylonitrile and mixtures thereof; (c) modified elastomeric polymeric material selected from the group consisting of butadiene homopolymer and copolymer as previously defined, such homopolymer and copolymer having been modified by copolymerization therein of trace amounts up to 5 percent by weight, based on weight of modified elastomeric polymeric material, of at least one functional monomer; and (d) mixtures thereof; (3) at least one polymer-in-monomer syrup consisting essentially of (a) from 2 to 90 percent by weight of at least one polymer derived from such (3)(a) monomers; and, (b) from 10 to 98 percent by weight of at least one olefimically unsaturated monomeric compound having at least one - C5 C - group; (c) from 0 to 30 percent by weight of a polymer containing the group (CH2CCL CHCH2)n, wherein n is an integer; wherein (3)(b) is present as a partial polymerization product of (3)(a) or of (3)(a) in the presence of (3)(c); the mixture of (3)(a) and (3)(b) or of (3)(a), (3)(b) and (3)(c) being a syrup of polymer dissolved or dispersed in unpolymerized monomer, in which syrup the amount of (3)(b) derived from (3)(a) is in the range from 2 to 90 percent by weight, based on the total weight of (3)(a), (3)(b) and (3)(c). (4) at least one polymeric material selected from the group consisting of.polyvinyl alkyl ether, styrene-acrylonitrile resin, unsaturated polyester resin and mixtures thereof, the alkyl moiety of such ether containing from one to 8 carbon atoms; (5) at least one homopolymer or copolymer of at least one monomer selected from the group consisting of styrene and alkyl or hydroxyalkyl esters of acrylic or methacrylic acid, said ester having from one to 18 carbon atoms in the alkyl moiety; and, (6) at least one polymeric material having at least one terminal olefinically unsaturated group, said polymeric material being selected from the group consisting of, (1) at least one adduct of at least one ethylenically unsaturated monofunctional isocyanate and at least one polymeric material containing one or more active hydrogen atomcontaining moiety(ies) selected from the group consisting of -OH,-NH2, -NH, EMI7.1 -SH and -COOH; and, (2) at least one adduct of at least one reactive monomer having at least one terminal olefinically unsaturated group and at least one reactive moiety selected from the group consisting of -0H, -HN2, 4IH-, EMI7.2 -SH and -COOH, and at least one polymeric material which contains at least one moiety which is reactive with said reactive moiety of said reactive monomer, provided that, when said reactive moiety is -0H, said polymeric material does not contain a reactive -NCO group; and (7) mixtures of such polymeric materials; and, (C) at least one inorganic or organic compound of a metal ion, said metal ion having a standard reduction potential in the range from +0.9 to -0.5; and (11) a second package comprising (A) at least one olefinically unsaturated monomer; (B) at least one polymeric material selected from the group consisting of (1) at least one olefinically unsaturated urethane reaction product of at least one isocyanate-functional prepolymer and at least one hydroxy-functional monomer having at least 1 unit of polymerizable olefinic unsaturation, such reaction product being characterized by the presence of at least two units of olefinic unsaturation and the substantial absence of free isocyanate groups; (2) at least one butadiene-based elastomeric polymeric material selected from the group consisting of (a) homopolymer of butadiene; (b) copolymer of butadiene and at least one monomer copolymerizable therewith selected from the group consisting of styrene, acrylonitrile, methacrylonitrile and mixtures thereof; ; (c) modified elastomeric polymeric material selected from the group consisting of butadiene homopolymer and copolymer as previously defined, such homopolymer and copolymer having been modified by copolymerization therein of trace amounts up to 5 percent by weight, based on weight of modified elastomeric polymeric material, of at least one functional monomer; and (d) mixtures thereof; (3) at least one polymer-in-monomer syrup consisting, essentially of (b) from 2 to 90 percent by weight of at least one polymer derived from such (3)(a) monomers; and (a) from 10 to 98 percent by weight of at least one olefinically unsaturated monomeric compound having at least one I I - C = C - group; (c) from 0 to 30 percent by weight of a polymer containing the group (CH2CC1 . CHCH2)n, wherein n is an integer; wherein (3)(b) is present as a partial polymerization product of (3)(a) or of (3)(a) in the presence of (3)(c); the mixture of (3)(a) and (3)(b) or of (3)(a), (3)(b) and (3)(c) being a syrup of polymer dissolved or dispersed in unpolymerized monomer, in which syrup the amount of (3)(b) derived from (3)(a) is in the range from 2 to 90 percent by weight, based on the total weight of (3)(a), (3)(b) and (3)(c). (4) at least one polymeric material selected from the group consisting of polyvinyl alkyl ether, styrene-acrylonitrile resin, unsaturated polyester resin and mixtures thereof, the alkyl moiety of such ether containing from one to 8 carbon atoms; (5) at least one homopolymer or copolymer of at least one monomer selected from the group consisting of styrene and alkyl or hydroxyalkyl esters of acrylic or methacrylic acid, said ester having from one to 18 carbon atoms in the alkyl moiety; ; (6) at least one polymeric material having at least one terminal olefinically unsaturated group, said polymeric material being selected from the group consisting of, (1) at least one adduct of at least one ethylenically unsaturated monofunctional isocyanate and at least one polymeric material containing one or more active hydrogen atom-containing moiety(ies) selected from the group consisting of -0H, -NH2, H-, EMI9.1 -SH and -COOH; and, (2) at least one adduct of at least one reactive monomer having at least one terminal olefinically unsaturated group and at least one reactive moiety selected from the group consisting of -OH, -NH2, H-, EMI9.2 -SH and -C00H, and at least one polymeric material which contains at least one moiety which is reactive with said reactive moiety of said reactive monomer, provided that, when said reactive moiety is -OH, said polymeric material does not contain a reactive -NCO group; and. (7) mixtures of such polymeric materials; (C) at least one organic sulfur-containing compound having at least one -SH group or having a tautomer1c form containing at least one -SH group; and (D) at least one peroxygen comocund selectee from the group consisting of hydrogen peroxide, organic peroxyesters ano organic hydroperoxi des; wherein the volume or weight, respectively, of said first package is substantially equal to the volume or weight, respectively, of said second package, at the time when said packages are intermixed. Each individual package of the adhesive compositions of the invention can optionally contain up to 30, preferably not more than 15 percent by weight, based on total weight of the individual package, of at least one polymeric material having an intrinsic viscosity in the range from 0.1 to 1.3, such polymeric material being obtained from the polymerization or copolymerization of at least one styrene monomer, acrylic monomer, substituted acrylic monomer, olefinically-unsaturated non-acrylic monomer or mixtures thereof; the total amount of such optional additive, when present in both packages, not exceeding 60, preferably 30, percent by weight, based on the combined weight of both packages; up to 20, preferably not more than 15, percent by weight, based on total weight of the package, of at least one elastomeric material having a second order glass transition temperature below 50C; with the total amount of elastomeric material, when present in both packages, not exceeding 40, preferably 30, percent by weight, based on the combined weight of both packages; up to 5 percent by weight of at least one unsaturated dicarboxylic acid ester; up to 10 percent by weight of at least one unsaturated polyester resin; up to 20 percent by weight of at least one unsaturated carboxylic acid having one or more, preferably one, carboxylic acid group; and up to one percent by weight of at least one waxy substance selected from the group consisting of paraffin wax, montan wax, beeswax, ceresin wax and spermaceti wax. The invention further provides a method for bonding mating surfaces of two or metal substrates comprising applying to at least one of such surface a room temperature-curable adhesive composition comprising (A) at least one olefinically unsaturated monomer; (B) at least one polymeric material selected from the group consisting of (1) at least one olefinically unsaturated urethane reaction product of at least one isocyanate-functional prepolymer and at least one hydroxy-functional monomer having at least one unit of polymerizable olefinic unsaturation, such reaction product being characterized by the presence of at least two units of olefinic unsaturation and the substantial absence of free isocyanate groups; (2) at least one butadiene-based elastomeric polymeric material selected from the group consisting of (a) homopolymer of butadiene; ; (b) copolymer of butadiene and at least one monomer copolymerizable therewith selected from the group consisting of styrene, acrylonitrile, methacrylonitrile and mixtures thereof; (c) modified elastomeric polymeric material selected from the group consisting of butadiene homopolymer and copolymer as previously defined, such homopolymer and copolymer having been modified by copolymerization, therein by trace amounts up to 5 percent- by weight1 based on weight of modified elastomeric material, of at least one functional monomer; and (d) mixtures thereof; (3) at least one polymer-in-monomer syrup consisting essentially of (a) from 10 to 98 percent by weight of at least on olefinically unsaturated monomeric compound having at least one - C C group; (b) from 2 to 90 percent by weight of at least one polymer derived from such (3)(a) monomers; (c) from zero to 30 percent by weight of at least one polymer containing the group (CH2 C Cl = CH CH2)n, wherein n is an integer; wherein (3)(b) is present as a partial polymerization product of (3)(a) or of (3)(a) in the presence of (3)(c); the mixture of (3)(and (3)(b) or of (3)(a), (3)(b) and (3)(c) being a syrup of polymer dissolved or dispersed in unpoRymerized monomer, in which syrup the amount of (3)(b) derived from (3)(a) is in the range from 2 to 90 percent, based on the total weight of (3)(a), (3)(b) and (3)9cm; (4) at least one polymeric material selected from the group consisting of polyvinyl alkyl ether, styrene-acrylonitrile resin, unsaturated polyester resin and mixtures thereof, the alkyl moiety of such ether containing from one to 8 carbon atoms; ; (5) at least one homopolymer or copolymer of at least one olefinically unsaturated monomer selected from the group consisting of styrene and alkyl or hydroxyalkyl esters of acrylic and methacrylic acic, said ester having one to 18 carbon atoms in the alkyl moiety; (6) at least one polymeric material having at least one terminal olefinically unsaturated group, said polymeric material being selected from the group consisting of, (1) at least one adduct of at least one ethylenically unsaturated monofunctional isocyanate and, at least one polymeric containing one or more active hydrogen moieties selected from the group consisting of -OH, H2, -NH-, EMI11.1 -SH and -COOH; and, (2) at least one adduct of at least one reactive monomer having at least one terminal olefinically unsaturated group and at least one reactive moiety selected from the group consisting of -OH, -NH2,-NH-, EMI11.2 -SH and -C00H, and at least one polymeric material which contains one or more moieties which are reactive with said reactive moiety of said reactive monomer, provided that, when said reactive moiety is -OH, said polymeric material does not contain a reactive -NCO group; and (7) mixtures of such polymeric materials; (C) at least one inorganic or organic compound of a metal ion, said metal ion having a standard reduction potential in the range from +0.9 to -0.5, (D) at least one organic sulfur-containing compound having at least one -SH group or having a tautomeric form containing at least one -SH group; and (E) at least one peroxygen compound selected from the group consisting of hydrogen peroxide, organic peroxyesters and organic hydroperoxides; and placing the mating surfaces in abutting relationship until the adhesive composition cures to effect bonding of said surfaces. Polymer-in-monomer syrups suitable for use in the present invention, compositionally as well as their preparation, are well-known in the art. Representative syrups, including precursor liquid monomer compounds containing at least one olefinically unsaturated group, and their preparation are disclosed in U.S.A. Patents Nos. 3,333,025; 3,725,504; and 3,873,640. Briefly, such syrups are conveniently prepared by de-aerating the starting mixture consisting essentially of at least one polymerizable liquid olefinically unsaturated compound and, when used, polymer containing the group (CH2-CCl : CHCH2)n, for a short period at about 400C under vacuum and then heating the mixture to about 75 0C under an inert gas atmosphere. A catalyst, for example, a free radical-generatins catalyst such as benzoyl peroxide or azodiisobutyric acid dinitrile, is then added, preferably in the form of a solution. The quantity of catalyst added is such that it will be completely consumed when the desired viscosity is reached. After the reaction is completed, the polymer-in monomer syrup is cooled. Preferably, the syrups have a viscosity in the range from about 500 to about 1,000,000 mPa s at 200C. Monomerjc liquid olefinically unsaturated compounds suitable for use in the adhesive compositions of the invention for forming polymer-inmonomer syrups and as additional polymerizable materials are characterized by the presence of at least one - C = C - group. The olefinically unsatu- rated group is preferably a vinyl group, more preferably terminally located, with acrylic and substituted acrylic monomers being currently preferred. When olefinically unsaturated monomers which do not contain acrylic or methacrylic groups are employed, each individual package of the adhesive compositions should not contain more than 30, preferably not more than 15, percent by weight, based on the total weight of the individual package, with the total amount of such non-acrylic monomers being not more than 50, preferably not more than 25 percent by weight, based on the total weight of both packages. Representative olefinically unsaturated monomers include, without limitation, methyl methacrylate, butyl methacrylate, ethyl acrylate, diethylene glycol dimethacrylate, methacrylic acid, acrylic acid, acrylonitrile, methacrylonitrile, styrene, vinyl styrene, vinyl acetate, chlorostyrene, glycidyl methacrylate, itaconic acid, acrylamide, methacrylanide, vinylidene chloride, 2,3-dichloro-1,3- butadiene, 2-chloro-1,3-butadiene, methyl styrene, n-butylstyrene, 2-hydroxyethyl methacrylate, 2-hydroxyethyl acrylate, tetrahydrofurfuryl methacrylate, benzyl methacrylate and cyclohexyl methacrylate. Compounds such as benzyl methacrylate, cyclohexylmethacrylate and tetrahyarofurfuryl methacrylate are currently preferred in low odor formulations, with tetrafurfuryl methacrylate providing not only the least odorous compositions, but also the most rapid-curing. Polymers containing the grouping (CH2-CO' : CHCH2)n, wherein n is an integer, are well-known in the art under the name neoprene, which is produced by the polymerization of 2-chloro-1,3-butadiene. Further elucidation would be superfluous. The isocyanate-functional prepolymers which are suitable for use in the practice of this invention are well-known. Typically, such prepolymers are adducts or condensation products of polyisocyanate compounds having at least 2 free isocyanate groups and monomeric or polymeric polyols having at least two hydroxy groups, including mixtures of such polyols. The reaction between the polyisocyanate and the polyols is effected employing an excess amount of polyisocyanate to ensure that the reaction product will contain at least 2 free, unreacted isocyanate groups. Polyols useful in preparing isocyanate-functional prepolymer used in the present invention preferably have an average molecular weight of 300 to 3,000. Suitable polyols include polyalkylene glycols such as polyethylene glycols; polyetherpolyols such as those prepared by addition polymerization of ethylene oxide and a polyol such as trimethylol propane in a ratio to provide unreacted hydroxyl groups in the product; organic hydroxylated elastomers exhibiting second order glass transition temperatures below about 50C such as poly(butadiene-styrene) polyols and poly(butadiene) polyols; polyester polyols such as are prepared by polymerizing polyols, such as diethylene glycol, trimethylol propane or 1,4 butanediol, with polycarboxylic acids, such as phthalic, terephthalic, adipic, maleic. or succinic acids, in a ratio to provide unreacted hydroxyl groups in the product; glyceride esters of hydroxylated fatty acids such as castor oil, glycerol monoricinoleate, blown linseed oil and blown soya oil; and polyesterpolyols such as are prepared by the polymerization of a lactone such as ± caprolactone. Polylsocyanates which can be reacted with polyols to form isocyanate-functional prepolymers for use in the present invention can be any monomeric; that is, non-polymeric, isocyanate compound having at least 2 free isocyanate groups, including aliphatic, cycloaliphatic and aromatic compounds. Representative polyisocyanates include, without limitation thereto, 2,4tolylene diisocyanate, 2,6-tolylene diisocyanate, 4,4'-diphenylmethane diisocyanate, m- and p-phenylene diisocyanate, polymethylene poly(phenyl isocyanate), hexamethylene di isocyanate, 4,4'-methylenebis(cyclohexyl isocyanate), hexamethylene diisocyanate, i,4E-nethylene- bis(cyclohexyl isocyanate), isophorone diisocyanate, and other aliphatic cycloaliphatic and aromatic polyisocyanates, and including mixtures of such polyisocyanates. Currently, cycloaliphatic and aromatic polyisocyanates are preferred. Hydroxy-fun & ional compounds which can be employed to introduce olefinic unsaturation into the isocyanate-functional prepolymer include, without limitation, hydroxyethyl acrylate, hydroxyethyl methacrylate, and allyl alcohol. The butadiene-based elastomeric polymeric materials which are suitable for use in the practice of this invention are also well-known and can be any elastomer derived from 1,3-butadiene or its halogenated analogs which has a glass transition temperature below ambient temperature and preferably not above about 50C. Suitable elastomers include butadiene homopolymer, copolymers of butadiene with styrene, acrylonitrile and methacrylonitrile, and such homopolymers and copolymers modified by copolymerization therein of trace amounts (0.05 to 5 percent) of a functional comonomer, such as acrylic acid, methacrylic acid, maleic anhydride, fumaric acid, styrene and methyl methacrylate. Polyvinyl alkyl ethers suitable for use in the adhesive compositions which are described herein are well-known in the art. Such ethers will preferably contain one to 8, more preferably one to 4, carbon atoms in the alkyl moiety of said ether. Likewise, styreneacrylonitrile polymers which are suitable for use in the invention are well-known. The adducts of ethylenically unsaturated monofunctional isocyanates and saturated or unsaturated polymeric materials having one or more active hydrogen atom-containing groups selected from the group consisting of -OH, -NH2, -NH-, -SH and -COOH which are suitable for use in the practice of the invention are readily prepared by procedures well known in the art. Ethylenically unsaturated monofunctional isocyanates are known in the art. Methods of making such compounds, for example, by phosgenation of the corresponding amino alkyl methacrylate, are disclosed in U.S.A. patents 2,718,516 and 2,821,544, which describe isocyanate esters of acrylic methacrylic and crotonic acids. Isocyanatoethyl methacrylate is a currently preferred compound for forming such adducts. Substantially any saturated or unsaturated having at least two active hyarogen atomcontaining group can be reacted with the monofunctional isocyanate esters of the unsaturated monocarooxylic acids. Reprtrntative polymeric materials include polyesters, polyethers, polytiols, polyamines and polyamides, with polyethers, such as poly(tetramethylene ether) glycol being currently preferred. Reactive monomers which have at least one terminal olefinicaliy unsaturated group at least one reactive moiety selected from the group consisting of -OH, -NH2, -NA-, EMI15.1 -SH and -COOH are well known, as are methods for making such compounds and the reactions into which such compounds enter. Representative compounds include 2-hydroxyethyl methacrylate, 2-hydroxyethyl acrylate, allyl alcohol, amino ethyl methacrylate, amino ethyl acrylate, dimethylamino ethyl methacrylate, glycidyl methacrylate, mercapto ethyl methacrylate, acrylic acid, methacrylic acid and crotonic acid. Polymeric materials whic have one or more groups which are reactive with such functional grouos (-OH, -NH2, etc.,) are equally well known. For example, isocyanate-functional polyurethanes are reactive with -NH2 and -NH- groups, polyamines and polymides are reactive with oxirane groups, polyesters, which contain -COOH groups, are reactive with -OH and -SH groups, and polyols, such as polyethers and polythiols are reactive with -COOH groups. The reactive monomer and the polymeric material can be reacted in stoichiometric amounts or, in those cases in which the polymeric material has two or more reactive groups, one can use less than stoichiometric amounts of the reactive monomer if desired, thus leaving some of the polymers reactive groups unreacted. Elastomeric polymeric materials having second order glass transition temperatur below about 5 C can be effective in modifying room temperature flexibility of the adhesive bond. Especially preferred of such elastomers are polychloroprene rubber; polybutadiene rubber; butadiene copolymer rubbers such as acrylonitrile-butadiene, carboxylated acrylonitrile-butadiene and styrene-butadiene rubbers; polyacrylate rubbers such as poly(ethyl acrylate) and poly(ethyl acrylate-halogenated vinyl ether-acrylic acid) rubbers; and ethylene copolymers such as ethylene-vinyl acetate rubbers. Other elastomeric polymers having a glass transition temperature about 5 0C can be employed since, other than the low glass transition temperature, there are no other limitations on the identity of the elastomer except for the specific requirements of the particular adhesive being formulated, such as suitable molecular weight, viscosity characteristics and compatibility with the other ingredients of the adhesive. Such elastomeric polymeric materials are particularly beneficial when incorporated in acrylic adhesives comprising at least one olefini calls unsaturated polyurethane. Non-acrylic monomers which can be employed in the hereindescribed adhesive systems include styrene, chlorostyrene, vinyl styrene and vinyl acetate. Polymeric materials having an intrinsic viscosity of 0.1 to about 1.3 which are suitable for use in the present invention can be obtained by the polymerization of one or more acrylic and nonacrylic monomers, including mixtures thereof. Exemplary polymeric materials include poly(methyl methacryl atein-butyl acryl atelethyl acrylate) (90/515); poly(n-butyl methacryl atel isobutyl methacrylate) (50/50); poly(n-butyl methacrylate) and poly(ethyl methacrylate). Preferably, the viscosity will be about midway in the recited range. The use of polymeric materials having such intrinsic viscosities is especially beneficial in acrylic adhesives containing homopolymers and copolymers of 1,3-butadiene. Phosphorous-containing compounds which are suitable for use in the adhesive compositions of the invention are selected from the group consisting of derivatives of phosphinic acid, phosphonic acid and phos pnoric acid having at least one -POH group and at least one organic moiety characterized -by the presence of at least one olefinically unsaturated group, which is preferably terminally located. More particularly, such olefinically unsaturated organophosphorous compounds have the characteristic formula EMI17.1 wherein each R is the same or different, and each R is independently a divalent organic radical directly bonded to the phosphorous atom through a carbon-phosphorous bond, said divalent radical being selected from the group consisting of divalent unsubstituted organic radical and divalent organic radical having at least one substituent group selected from the class consisting of halogen, hydroxyl, amino1 alkyl radical containing from one to 8,-preferably cne to 4, carbon atoms and aryl radical having at least one moiety containing at least one aromatic nucleus; at least one X is CH2. " and the other X is a functional group selected from the group consisting of hydrogen, hydroxyl, amino1 mercapto, halogen and CH2 s C ; EMI17.2 wherein R is as previously defined; RÚ is hydrogen -Rê-X, wherein Rê is a divalent organic radical directly bonded to the oxygen radical through a carbon-oxygen bond, said divalent radical being selected from the group consisting of divalent unsubstituted organic radical and divalent organic radical having at least one substituent group selected from the class consisting of halogen, hydroxyl, amino, alkyl radical containing from one to 8 carbon atoms and aryl radical having at least one moiety containing at least one aromatic nucleus; and wherein X is as previously defined, with the proviso that at least one X moiety must be CH2 . ; EMI17.3 wherein R1 is as previously described, with the proviso that at least one R1 group contains at least one CH2 t C(moiety. A currently preferred group of phosphorous-containing compound has the formula EMI18.1 wherein R3 is selected from the group consisting of hydrogen, halogen, an alkyl group having from one to 8, preferably one to 4, carbon atoms, and CH2 , CH ; R is selected from the group consisting of hydrogen, an alkyl group having from one to 8, preferably one to 4 carbon atoms, and a haloalkyl group having one to 8, preferably one to 4, carbon atoms; A is selected from the group consisting cf -h50- and (R60)n, wherein R5is an aliphatic or cycloaliphatic alkylene group containing from one to 9, preferably 2 to 6, carbon atoms; R6 is an alkylene group having from one to 7, preferably 2 to 4, carbon atoms; n is an integer from 2 to 10, and m is 1 or 2, preferably 1. In the several formulae I-IV, the divalent organic radicals R and Rê can have a compound structure, that is, the radical can contain at least one, or a series of at least 2, unsubstituted or substituted hydrocarbon group(s) containing or separated from each other by -O-, -S-, COO, -NH-, -NHCOO-, and (R70) wherein R7 is an alkylene group p' containing from 2 to 7, preferably 2 to 4 carbon atoms, and p is an integer from 2 to 10. Preferaby, the divalent radical is an alkylene radical having a straight chain or ring of from one to 22, preferably one to 9, carton atoms in any non-repeating unit. It will be understood that divalent radicals having a compound structure would have 2 or more of such straight chains or rings. The divalent radicals can be saturated or unsaturated; aliphatic, cycloaliphatic or aromatic; and, with compound structures, can include mixtures thereof; and generally have from one to about 22 carbon atoms in each chain or ring of carbon atoms. In the several formulae I-III, representative X-R- and X-R2- radicals include, without limitation thereto, lower alkenyl, cyclohexenyl, hydroxy-lower alkenyl, halo-lower alkenyl, carboxy-lower alkenyl, lower alkyl, amino-lower alkyl, hydroxy-lower alkyl, mercapto-lower alkyl, alkoxy-lower alkyl, halo-lower alkyl, di-phosphonomethyf-amino-lower a alkyl, phenyl-hydroxy-phosphonomethyl, aminophenyl-hydroxy-phosphonomethyl, halophenyl-hydroxy-phosphonomethyl, phenyl-amino-phosphonomethyl, halophenyl-amino-phosphomomethyl, hydroxy-phosphonomethyl, lower alkyl hydroxy-phosphonomethyl, halo-lower alkyl -hydroxy-phosphonomethyl and amino-lower alkyl-hydroxy-phosphonomethyl; the term "lower11 referring to a group containing from one to 8, preferably one to 4 carbon atoms. Phosphorous-containing compounds having vinyl unsaturation are preferred over such compounds having allylic unsaturation, with monoesters of phosphinic, phosphonic and phosphoric acids having one unit of vinyl or ailylic, especially vinyl, unsaturation presently being preferred. Representative phosphorous-containing compounds include, without limitation, phosphoric acid; 2-methacryloyloxyethyl phosphate; bi s-( 2-methacryloyl - oxyethyl) phosphate; 2-acryloyloxyethyl phosphate; bis-(2-acryloyloxy- ethyl) phosphate; methyl-(2-methacryloyloxyethyl) phosphate; ethyl methacryloyloxyethyl phosphate; methyl acryloyloxyethyl phosphate; ethyl acryloxyethyl phosphate; compounds of Formula IV wherein R is .hydrogen or methyl and R4 is propyl, isobutyl, ethylhexyl, halopropyl, haloisobutyl or haloethylhexyl; vinyl phosphonic acid; cyclohexene-3 phosphoric acid; alpha-hydroxybutene-2-phosphonic acid; 1-hydroxy-1 phenylmethane-1,1-diphosphonic acid; 1-hydroxy-1-methyl-1-1-diphosphonic acid; 1-amino-1-phenyl-1,1-di-phosphonic acid; 3-amino-1-hyoroxypropane- 1,1-diphosphonic acid; amino-tris (methylenephosphonic acid); gamma- aminopropylphosphonic acid; gamma-glycidoxypropylphosphonic acid; phosphoric acid-mono-2-aminoethyl ester; allyl z phosphoni c acid; allyl phosphinic acid; A -methacryloyl-oxyethyl phosphinic acid; diallyl phosphinic acid; bis( ss -methacryloyl-oxyethyl) phosphinic acid ana allyl methacryloyloxyethyl phosphinic acid. Peroxygen compounds which are suitable for use in the present invention are selected from the group consisting of hydrogen peroxide, organic peroxyesters of peroxymonocarboxylic acids, full and partial organic peroxyesters of monoperoxy dicarboxylic acids and diperoxydicarbo xylic acids, full and partial organic peroxyesters of peroxymonocarbonic acids and peroxydicarbonic acids, full and partial esters of organic peroxymonocarbonic and peroxydicarbonic acids, and organic hydroperoxides. A partial but representative listing of organic peroxygen compounds which can be utilized in the practice of the invention include t-butyl peroxy acetate, t-butyl peroxybenzoate, t-butyl peroxy-( 2-ethyl hexanoate), t-butylperoxyisobutyrate, o,o-t-butyl o-isopropyl monoperoxy carbonate, t-butylperoxypivalate, 2,5-dimethyl- 2,5-di(benzoyl-peroxy)hexane, t-butylperoxy(2-ethylbutyrate), 2,5-dimethyl-2,Sdi(2-ethyl-hexanoyl peroxy) hexane, di-t-butyl diperoxyphthalate, o,o-tbutyl o-hydrogenmonoperoxymaleate, di-sec-butyl peroxydicarbonate, diisopropylperoxy di carbonate, dicyclohexyl peroxydicarbonate, t-butyl peroxycrotonate, N,N-dlethyl-t-butyl peroxycarbonate, N,N-diphenyl t-butyl peroxycarbonate, acetyl cyclohexylsulfonyl peroxide, cumene hydroperoxide, t-butyl hydroperoxide, methyl ethyl ketone hydroperoxide, and diisopropyl benzene hydroperoxide. The peroxygen compound is employed in an amount in the range from 0.05 to 10, preferably 0.2 to 3, most preferably .0.5 to 1.5, percent by weight, based on the total weight of the package into which it is incorporated. The organosulfur compounds which are employed in the practice of the invention must be mercaptan compounds which have at least one -SH group or which exist in a tautomeric form containing at least one -SH group. A partial but-represe,lrative listing of such compounds include mercaptoacetic acid, mercaptosuccinic (malic) acid, 3-mercaptopropionic acid, thioglycerol, polyethylene glycol dimercaptoacetate, 2,2'-dimercaptodiethyl ether, thioglycerol, polyethylene glycol di-3-mercaptoproprionate, polyethylene glycol dimercaptoacetate, dodecyl thioglycolate, methyl thidglycolate, 2mercaptobenzothazol e, dii sopropyl benzothiazyl-2-sulfen amide, 2-thiohydantoin, 2mercapto-6-nitrobenzothi azole, thiophenol, 2-benzimidazolethiol, 3,3'-thiopropionic acid, sodium thioglycolate, polyethylene dimercaptoacetate, isodecyl thioglycolate and mercapto silane. The organic thiols are employed in an amount in the range of 0.005 to 2, preferably 0.05 to 1, most preferably 0.1 to 0.5, percent by weight, based on the total weight of the pack into which they are incorporated. The third component for the oxidation-reduction couple curing agent is an inorganic or an organic compound containing at least one metal ion which has a standard reduction potential in the range from +0.9 to -0.5, preferably +0.8 to -0.3, and more preferably +0.35 to +0.01. The metal ion-containing compounds are interactive with the herein described peroxygen and organosulfur compounds to generate free radicals which are capable of initiating and propogating the polymerization of olefinically unsaturated monomers and polymers, and including graft polymerization and crosslinking between such unsaturated materials and polymers which are normally not considered further polymerizable. The metal ion can be in either the cationic or anionic moiety of the compound in which it is included. Preferred metal ions include copper, tin, cobalt, zinc and iron, with Cm2+, Cu(NH3)4 2+, To2+, Cu(Cl)4 -2, Fe3+, Co2+, Co(Cl)4 -2, Co(NH3)6 2+, Co(H20)4 2+, cupric naphthenate, cupric acetate, cobalt acetate, cobalt acetylacetonate and stannic chloride being especially preferred. Currently, inorganic metal salts, especially the chloride or bromide salts are preferred where increased cure rate. is desired. Reducing or totally eliminating the halogen compound increases the time required for cure, thus providing the formulator with a myriad of options with respect to cure rate. The metal ion-containing compounds are employed in an amount in the range from 0.005 to 1, preferably 0.01 to 0.5, most preferably 0.05 to 0.1, percent by weight, based on the weight of-the pack into which they are incorporated. Halogen-containing compounds will be employed in the range from 0.005 to O.S, preferably 0.01 to 0.25, most preferably 0.05 to O.1, percent by weight, also based on the weight of the pack into which they are incorporated. It has also been discovered that the incorporation f hydroxyl containing materials, such as ethylene glycol, glycerine and tne like in amounts less than 10, preferably less than 5, percent by weight, based on total weight of both packages, provides a more lengthy pot life and a longer cure period. Water has also been found to be effective in increasing pot life and, in addition, improves storage stability of the compositions, when used in amounts not exceeding two percent by weight, based on total weight of the combined packages. The herein-described adhesive compositions are prepared by conventional methods, such as are disclosed in U.S.A. patents-3,832,774 and 3,890,407, both of which disclosures are incorporated herein Dy reference. Typically, the compositions are provided as two-part systems, with the sulfur compound and peroxygen compound being kept separate from the metal compound until prior to use. The adhesive systems are especially useful for bonding metal surfaces such as steel, aluminum and copper to a variety of substrates, including metals, fibers, glass, ceramics, wood, and the like, with little, if any.pretreatment of the metal surface prior to application of the primer or adhesive, as the case may be. Thus, bonding can be effected even to oily metal surfaces which are otherwise clean without an extensive pretreatment as is usually required with the vast majority of currently available primers and adhesives. Additionally, the adhesive systems of this invention provide effective bonding at room temperature, thus heat is not required either for applying the adhesive systems to the substrates or for curing. They can also be employed on porous substrates, unlike the anaerobic adhesives which require the excision of air and thus cannot be used on surfaces containing air in the - pores. The invention is illustrated by the following examples, wherein all parts, proportions and percentages are by weight unless otherwise lnd -ated. EXAMPLE I Compositions were prepared according to the following formulations. Adhesive 1-1 1-2 1-3 1-4 Tetrahydrofurfuryl methacrylate 6.72 6.72 6.72 6.72 Bisphenol-A fumarate polyester. 12.48 12.48 12.48 12.48 CuCl2 0.01 0.01 0.01 0.01 t-8utyl perbenzoate 0.25 0.25 0.25 0.25 Mercaptosuccinic acid 0.20 - - - Mercaptobenzothiazole - 0.20 - 3-Mercaptopropionic acid - - 0.20 - Thioglycolic acid - - - 0.20 Water 0.19 0.19 0.19 0.19 The gel time was determined by dipping a glass stirring roo into the composition and noting the time at which the composition no longer flowed. The gel times are reported below. ADHESIVE GEL TIME 1-1 < 60 seconds 1-2 6 minutes 1-3 2 minutes 1-4 1 min. 30 sec. EXAMPLE II Adhesive compositions are prepared from the indicated ingredients. After thorough mixing, the gel times for each formulation was determined following the procedure of Example I. The gel times are reported in the Table. ADHESIVE 2-1 2-2 2-3 2-4 2-5 2-6 2-7 Methyl methacrylate 12.5 12.5 12.5 12.5 12.5 12.5 12.5 Bisphenol-A fumarate polyester 12.5 12.5 12.5 12.5 12.5 12.5 12.5 CuCl2 0.0008 0.0008 0.0008 0.0008 0.0008 0.0008 ---t-Butyl perbenzoate 0.25 0.25 0.25 0.25 0.25 0.25 0.25 Mercaptobenzothiazole 0.10 ---- ---- ---- ---- ---- 0.10 Diisopropylbenzothiazyl-2- ---- 0.10 ---- ---- ---- ---- ---sulfenamide Benzothiazyl disulfide ---- ---- 0.10 ---- ---- ---- --- N-t-butyl-2-benzothiazole- ---- ---- ---- 0.10 ---- ---- ---sulfenamide N-oxydiethylene benzothiazole-2- ---- ---- ---- ---- 0.10 ---- ---sulfenamide N-cyclohexyl-2-benzothiazole- ---- ---- ---- ---- ---- ---- ---sulfenamide gel time, minutes 35 90 NCa NCa NCa NCa NCa a NC is no cure. EXAMPLE III Two formulations are prepared as follows: FORMULATION I 1jT Methyl methacrylate 12.5 Tetrahydrofurfuryl methacrylate - 12.5 Bisphenol-A fumarate polyester 12.5 12.5 CuC12 0.1 0.1 t-8utyl perbenzoate 0.25 0.25 Various sulfur compounds were added to the formulations I and II. Except for ;nercaptobenzothiazole which was added in an amount of 0.1 PBW, the sulfur compounds were added in an amount of 0.2 PSW. The gel times for each resulting mixture was determined following the procedure of Example I. The results are reported below. FORMULATION SULFUR COMPOUND GEL TIME I Mercaptobenzothiazole 43 minutes I 2-Thiohydantoin 60 minutes I Thiourea No Cure I Dithiooxamide No Cure I Trimethylthiourea No Cure I Ethylene trithiocarbonate No Cure I 2-Mercapto-A-ni tro-benzothi azol e 52 minutes I Mercaptosuccinic acid 9 minutes I 3-mercaptopropionic acid 35 minutes I Benzimidazolethiol 4 hours I Dodecyl thioglycollate 4 hours EXAMPLE III FORMULATION SULFUR COMPOUND - GEL TIME II Mercaptosuccinic acid < 60 seconds II Mercaptobenzothiazole . 8 minutes II 3-Mercaptopropionic acid 2 minutes II Thioglycolic acid 1 min. 30 sec. II Ethylene glycol dimercaptoacetate 1 minute II Dimercaoto dimethyl ether 1 minute II Thioglycerol 50 seconds II Polyethylene glycol di-3- 1 minute mercaptoprop i onate II 3,31-Thiopropionic acid > 15 minutes II Sodium thioglycollate > 15 minutes II Mercaptosuccinic acid 50 seconds II Polyethylene glycol dimercapto- 30 seconds acetate II Polyethylene dimercaptoacetate 35 seconds II Isodecyl thioglycollate 55 seconds II Methyl thioglycollate 45 seconds EXAMPLE IV The following compositions were prepared by homogeneously blending the ingredients. Gel times for each composition were obtained following the procedure of Example I. ADHESIVE 4-1 4-2 4-3 4-4 4-5 4-6 4-7 4-8 4-9 Methyl methacrylate 12.5 12.5 12.5 12.5 12.5 12.5 12.5 12.5 12.5 Bisphenol-A fumarate polyester 12.5 12.5 12.5 12.5 12.5 12.5 12.5 12.5 12.5 Mercaptobenzothiazole 0.10 0.10 0.10 0.10 0.10 0.10 0.10 0.10 0.10 t-Butyl perbenzoate 0.25 0.25 0.25 0.25 0.25 0.25 0.25 0.25 0.25 CuCl2 0.003 0.005 0.01 0.02 0.025 0.038 0.02 0.02 0.02 Gel time < 1 50 43 30 25 22 30 25 27 hr. min min min min min min min min ADHESIVE 4-10 4-11 4-12 4-13 4-14 4-15 4-16 4-17 4-18 Methyl methacrylate 12.5 12.5 12.5 12.5 12.5 12.5 12.5 12.5 12.5 Bisphenol A fumarate polyester 12.5 12.5 12.5 12.5 12.5 12.5 12.5 12.5 12.5 Mercaptobenzothiazole 0.10 0.10 0.10 0.15 0.20 0.25 0.30 0.35 0.40 t-Butyl perbenzoate 1.0 1.5 2.0 0.35 0.35 0.35 0.35 0.35 0.35 CuCl2 0.02 0.2 0.2 0.02 0.02 0.01 0.02 0.2 0.2 Gel time, minutes 34 30 26 17 31 24 34 32 40 min min min min min min min min min EXAMPLE VI This example illustrates the effect of metal ions. It should be noted that lead ion is not within the scope of the invention. ADHESIVE 6-1 6-2 6-3 6-4 6-5 6-6 6-7 6-8 6-9 6-10 Bisphenol-A fumarate polyester 23.0 23.0 23.0 23.0 23.0 23.0 23.0 23.0 23.0 23.0 Tetrahydrofurfuryl methacrylate 41.1 40.9 40.9 40.9 40.8 40.9 40.9 41.0 40.9 41.0 PTMO methacrylourethane 18.1 17.9 18.0 17.9 17.8 17.9 17.9 18.0 17.9 18.0 2-hydroxyethyl methacrylate 3.3 3.3 3.3 3.3 3.3 3.3 3.3 3.3 3.3 3.3 HEMA-phosphate 13.3 13.3 13.3 13.3 13.2 13.2 13.2 13.3 13.3 13.3 Mercaptosuccinic acid 0.35 0.35 0.35 0.35 0.35 0.35 0.35 0.35 0.35 0.35 t-butyl perbenzoate 0.45 0.45 0.45 0.45 0.45 0.45 0.45 0.45 0.45 0.45 Water 0.40 0.70 0.70 0.70 0.90 0.90 0.90 0.45 0.75 Methanol - - - - - - - - - 0.50 CuCl2 0.04 - - - - - - - - AlCl3 - 0.04 - - - - - - - CoCl2 - - 0.04 - - - - - - SnCl2 - - - 0.06 - - - - - ZnCl2 - - - - 0.10 - - - - NiCl2 - - - - - 0.05 - - - FeCl2 - - - - - - 0.05 - - Pb(C2H3O2)2 - - - - - - - 0.10 - Cu(C2H3O2)2 - - - - - - - - 0.2 Vanadyl Acetylacetonate - - - - - - - - - 0.03 Gel time 6-1 10 minutes 6-2 5 to 16 hours 6-3 5 to 16 hours 6-4 5 to 16 hours, partial gel 6-5 greater than 16 hours, slight gel 6-6 greater than 16 hours, slight gel 6-7 less than 5 hours, partial gel 6-8 no cure 6-9 3 hours 30 minutes 6-10 less than 6 hours EXAMPLE V The following data illustrate unsaturated monomers which are effectively utilized in the practice of the invention. The gel times are determined following the procedure of Example I. The base adhesive formulations are as follows: BASE ADHESIVE . 5-1 5-2 CuCl2 0.02 0.02 O.G23 Mercaptosuccinic acid 0.05 0.10 0.10 t-Butyl perbenzoate , 0.35 0.35 0.35 Bis-phenol A fumarate polyester 5.0 5.3 5.0 Unsaturated monomer See Table Cyclohexyl methacrylate 5.0 5.0 Gel Time See Table 1 min - 2 min 30 sec 15 sec For Base Adhesive 5-1; ; Unsaturated Monomer Amount, PBW Gel Time Tetranydrofurfuryl methacrylate 5.0 52 seconcs 2-hydroxyethyl methacrylate 5.0 None Ethylene glycol dimethacrylate 5.0 1 minute 2-hydroxyethyl methacrylate/ 2.5/2.5 None methyl methacrylate Cyclohexyl methacrylate 5.0 None Butyl methacrylate 5.0 10 minutes Ethylene glycol dimethacrylate/ 0.5/4.5 45 seconds tetrahydrofurfuryl methacrylate N N 4.0/4.0 35 seconds N N 1.5/3.5 43 seconds N " 2.0/3.0 35 seconds N N 2.5/2.5 23 seconds 2-Hydroxyethyl methacrylatel 0.5/4.5 33 seconds tetrahydrofurfuryl methacrylate N N 1.25/3.75 None EXAMPLE VII The following data illustrate various polymeric materials which can be employed in t-e practice of the invention. The gel times are determined following the procedure of Example I. The base adhesive formulations are as follows: BASE ADHESIVE 7-1 7-2 ¯ 7-3 Triethylene glycol dimethacrylate 2.5 - - Tetrahydrofur-uryl methacrylate 2.5 2.5 2.5 Polyethylene lycol dimethacrylate - 2.5 5.0 Bisphenol-A -smarate.polyester 2.5 2.5 2.5 Polymer See Table See Table See Table CuCl2 .02 0.02 0.02 Mercaptosucct-ic acid 1.00 1.00 1.00 t-butyl perbenzoate 0.35 0.35 0.35 POLYMER AMOUNT, PBW ADHESIVE GEL TIME HEMA-capped pclytetramethylene 2.5 7-1 4 min. 30 sec. ether glycol VTBNa (acrylate terminated) 2.5 7-1 4 min. 15 sec. VTBNX (methacrylate terminated) 2.5 7-1 7 min. 15 sec. PE 1106-63b 2.5 7-2 53 seconds PE 1106-S3b 5.0 7-3 20 seconds VTBN 2.5 7-2 1 minute VTBN 5.0 7-3 30 seconds VTBN (methacrylate terminated) 2.5 7-2 45 seconds VTBN (methacrylate terminated) 5.0 7-3 1 min. 30 sec. VTBN (acrylate terminated) 2.5 7-2 1 min. 15 sec. VTBN (acrylate terminated) 5.0 7-3 45 seconds a VTBN is v-.nyl-terminated butadiene acrylonitrile copolymer b PE-1106-63 PTMO acrylourethane EXAMPLE VIII The following example illustrates the effect which the concentration of peroxygen compound has on cure rate. ADHESIVE 8-1 8-2 8-3 8-4 8-5 8-6 8-7 Bisphenol-A fumarate polyester 23.1 23.1 23.1 23.1 23.0 23.0 22.9 PTMO methacrylourethane 17.7 17.7 17.7 17.7 17.7 17.6 17.6 Tetrahydrofurfuryl methacrylate 40.9 40.9 40.8 40.8 40.7 40.6 40.4 CuCl2.2H2O .02 .02 .02 .02 .02 .02 .02 2-hydroxyethyl methacrylate 3.7 3.7 3.7 3.7 3.6 3.6 3.6 Mercaptosuccinic acid .37 .37 .37 .37 .37 .37 .37 HEMA-phosphate 13.2 13.2 13.2 13.1 13.1 13.1 13.1 t-butyl perbenzoate - .14 .18 .27 .54 0.80 1.1 Water 1.0 1.0 1.0 1.0 1.0 1.0 1.0 ADHESIVE 8-8 8-9 8-10 8-11 8-12 8-13 Bisphenol-A fumarate polyester 22.8 22.8 22.7 22.6 22.6 22.6 PTMO methacrylourethane 17.5 17.5 17.4 17.4 17.3 17.5 Tetrahydrofurfuryl methacrylate 40.3 40.2 40.1 40.0 39.9 39.8 CuCl2.2H2O .02 .02 .02 .02 .02 .02 2-hydroxyethyl methacrylate 3.6 3.6 3.6 3.6 3.6 3.6 Mercaptosuccinic acid .36 .36 .36 .36 .36 .36 HEMA-phosphate 13.0 13.0 12.9 12.9 12.9 12.8 t-butyl perbenzoate 1.3 1.6 1.9 2.1 2.4 2.6 Water 1.0 1.0 1.0 1.0 1.0 1.0 Gel time 8-1 No cure 8-7 13 minutes 8-2 1 hour 10 minutes 8-8 12 minutes 8-3 10 minutes 8-9 11 minutes 8-4 28 minutes 8-10 11 minutes 8-5 21 minutes 8-11 10 minutes 8-6 15 minutes 8-12 10 minutes 8-13 10 minutes EXAMPLE IX The following Example illustrates the effect of halogen and water concentration on cure rate. ADHESIVE 9-1 9-2 9-3 9-4 9-5 9-6 9-7 2-hydroxyethyl methacrylate 5.0 5.0 5.0 6.28 5.0 5.9 6.28 Bisphenol A fumarate polyester 5.0 5.0 5.0 5.0 5.0 5.0 5.0 Mercaptosuccinic acid 0.1 0.1 0.1 0.1 0.1 0.1 0.1 t-butyl perbenzoate 0.3 0.3 0.3 0.2 0.2 0.2 0.2 Cupric acetate 0.1 - 0.1 - - - Hydrochloric acid - 0.01 0.1 - - - CuCl2 - - - 0.02 0.02 0.02 0.02 Water 0.19 0.19 0.38 - 1.28 0.38 0.9 Gel Time PPOa PPOa 40 1 min > 15 8 > 15 sec 45 sec min min min a Partial polymerization overnight EXAMPLE X The following two-package adhesive is prepared: : PART A PART B Tetrahydrofurfuryl methacrylate 100 100 2-Hydroxyethyl methacrylate 14.4 1.9 Methacryl oyl ethoxyphosphate 74.0 Bis-phenol A fumarate polyester. 100 2-Hydroxyethyl methacrylate-capped - 100 poly(tetramethylene glycol) polyurethane CuCi2 0.1 Mercaptosuccinic acid 1.6 t-butyl perbenzoate 2.0 TOTAL 218.0 276.0 Equal weight amounts of Part A and Part B were combined by mixing Part B into part A. After thorough mixing, the mixed composition was employed to bond various substrates, using a 0.5 in. overlap and a 10 mil glue line. The bones assemblies were cured overnight. Peel strength of the bonded assemblies was obtained following the procedure of ASTM D1002-79. The data is reported in the following table: SUBSTRATE BOND STRENGTH, psi CQ1010 CRS 1588 SAE1010 CRS 2152 Galvanized CRS 155 2024-T3 Alclad Al 1136 6061-T6 Al 1044 Copper 1116 Brass SAE 72 1296 Magnesium 844 EXAMPLE XI The following example illustrates the effect of which concentration of metal ion has on cure rate. ADHESIVE 11-1 11-2 11-3 11-4 11-5 11-6 11-7 11-8 11-9 11-10 Bisphenol-A fumarate polyester 22.9 22.8 22.8 22.7 22.6 22.6 22.5 22.5 22.4 23.6 PTMO methacrylourethane 17.8 17.8 17.7 17.7 17.6 17.6 17.5 17.5 17.4 17.9 Tetrahydrofurfuryl methacrylate 40.7 40.6 40.5 40.4 40.2 40.2 40.0 40.0 39.8 40.8 CuCl2 .01 .03 .04 .05 .07 .08 .10 .11 .12 Mercaptosuccinic acid .37 .37 .37 .36 .36 .36 .36 .36 .36 .37 2-hydroxyethyl methacrylate 3.6 3.8 4.1 4.3 4.5 4.8 5.0 5.3 5.5 3.3 HEMA-phosphate 13.1 13.1 13.1 13.0 13.0 13.0 12.9 12.9 12.9 13.2 t-butyl perbenzoate .45 .45 .45 .44 .44 .44 .44 .44 .44 .45 Water 1.0 1.0 1.0 1.0 1.0 1.0 1.0 1.0 1.0 1.0 Gel Time 11-1 26 minutes 11-6 13 minutes 11-2 16 minutes 11-7 12 minutes 11-3 14 minutes 11-8 12 minutes 11-4 13 minutes 11-9 12 minutes 11-5 13 minutes 11-10 no cure EXAMPLE XII The following example illustrates the effect which concentration of sulfur-containing compound has upon cure rates. ADHESIVE 12-1 12-2 12-3 12-4 12-5 12-6 Bisphenol-A fumarate polyester 24.7 24.7 24.6 24.5 24.5 24.4 PTMO methacrylourethane 17.7 17.7 17.6 17.6 17.5 17.5 Tetrahydrofurfuryl methacrylate 42.5 42.4 42.2 42.1 42.0 41.9 CuCl2 .02 .02 .02 .02 .02 .02 .02 Mercaptosuccinic acid - .03 .06 .08 .11 .14 2-hydroxyethyl methacrylate .33 0.6 0.8 1.1 1.3 1.6 HEMA-phosphate 13.2 13.2 13.1 13.1 13.0 13.0 t-butyl perbenzoate - .50 .50 .50 .50 .50 Water 1.0 1.0 1.0 1.0 1.0 1.0 ADHESIVE 12-7 12-8 12-9 12-10 12-11 Bisphenol-A fumarate polyester 24.3 24.3 24.2 24.1 24.1 PTMO methacrylourethane 17.4 17.4 17.4 17.3 17.3 Tetrahydrofurfuryl methacrylate 41.7 41.7 41.5 41.4 41.4 CuCl2 .02 .02 .02 .02 .02 Mercaptosuccinic acid .17 .19 .22 .25 .27 2-hydroxyethyl methacrylate 1.8 2.1 2.3 2.5 2.8 HEMA-phosphate 13.0 12.9 12.9 12.9 12.8 t-butyl perbenzoate .50 .50 0.5 0.5 0.5 Water 1.0 1.0 1.0 1.0 Gel time 12-1 No cure 12-6 19 minutes 12-2 No cure 12-7 18 minutes 12-3 1 hour 12-8 18 minutes 12-4 25 minutes 12-9 18 minutes 12-5 19 minutes 12-10 18 minutes EXAMPLE XIII This example illustrates the effect which compounds such as glycerine has upon cure rates. ADHESIVE 13-1 13-2 13-3 13-4 13-5 13-6 13-7 Bisphenol-A fumarate polyester 22.8 22.8 22.8 22.8 22.8 22.8 22.8 Tetrahydrofurfuryl methacrylate 39.9 39.5 39.2 38.9 38.6 38.2 36.5 PTMO methacrylourethane 17.1 16.7 16.4 16.1 15.8 15.4 13.7 2-hydroxyethyl methacrylate 4.0 4.0 4.0 4.0 4.0 4.0 3.9 HEMA-phosphate 13.4 13.1 12.9 12.6 12.3 12.1 10.7 Glycerine - 1.0 2.0 3.0 4.0 5.0 10.0 Mercaptosuccinic acid .41 .41 .41 .41 .41 .41 .41 CuCl2.2H2O .018 .017 0.17 0.16 0.16 0.16 0.14 t-butyl perbenzoate 0.25 0.25 0.25 0.25 0.25 0.25 0.25 Water 1.0 1.0 1.0 1.0 0.90 0.90 0.80 Car-o-sil 1.0 1.0 1.0 1.0 0.94 0.90 0.80 Gel time 13-1 24 minutes 13-5 2 hours 15 minutes 13-2 28 minutes 13-6 3 hours 15 minutes 13-3 1 hour 15 minutes 13-7 20 to 30 hours 13-4 1 hour 40 minutes EXAMPLE XIV The following example illustrates the effect of peroxygen concentration on cure speed. ADHESIVE 14-1 14-2 14-3 14-4 14-5 14-6 Bisphenol-A fumarate polyester 23.1 23.0 22.9 22.9 22.8 22.8 Tetrahydrofurfuryl methacrylate 40.8 40.7 40.6 40.5 40.4 40.3 PTMO methacrylourethane 17.8 17.7 17.7 17.6 17.6 17.6 2-hydroxyethyl methacrylate 3.6 3.6 3.6 3.6 3.6 3.6 CuCl2.2H2O 0.01 0.01 0.01 0.01 0.01 0.01 HEMA-phosphate 13.1 13.0 13.0 13.0 12.9 12.9 Water 1.0 1.0 1.0 1.0 1.0 1.0 Dioctyl phthalate 0.10 0.20 0.40 0.50 0.60 .70 t-butyl peroctoate 0.10 0.20 0.40 0.50 0.60 .70 Mercaptosuccinic acid 0.37 0.37 0.37 0.37 0.37 0.36 ADHESIVE 14-7 14-8 14-9 14-10 14-11 14-12 Bisphenol-A fumarate polyester 22.6 22.4 22.2 21.8 21.4 21.0 Tetrahydrofurfuryl methacrylate 40.1 39.7 39.3 38.6 37.9 37.2 PTMO methacrylourethane 17.5 17.3 17.1 16.8 16.5 16.2 2-hydroxyethyl methacrylate 3.6 3.6 3.5 3.4 3.4 3.3 CuCl2.2H2O 0.01 0.01 0.01 0.01 0.01 0.01 HEMA-phosphate 12.8 12.7 12.6 12.4 12.1 11.9 Water 1.0 1.0 1.0 0.9 0.9 0.9 Dioctyl phthalate 1.0 1.4 1.9 2.8 3.7 4.5 t-butyl peroctoate 1.0 1.4 1.9 2.8 3.7 4.5 Mercaptosuccinic acid 0.36 0.36 0.36 0.35 0.34 0.34 Gel time 14-1 1 hour 35 minutes 14-7 19 minutes 14-2 47 minutes 14-8 17 minutes 14-3 30 minutes 14-9 15 minutes 14-4 28 minutes 14-10 13 minutes 14-5 23 minutes 14-11 13 minutes 14-6 21 minutes 14-12 12 minutes EXAMPLE XV The following data illustrate the use of hydroperoxide compounds as the only peroxygen compound in combination with a third compound and an organic or inorganic metal ion-containing compound. ADHESIVE 15-1 15-2 Bisphenol-A fumarate polyester 22.7 22.7 HEMA-capped PTMO urethane 26.0 26.0 Methyl methacrylate 36.7 36.7 Tetrahydrofurfuryl methacrylate 3.8 3.8 Hydroxyethyl methacrylate 0.5 0.5 HEMA-phosphate 4.2 4.2 Ethylene glycol 3.7 3.7 Thiomal-ic acid 0.4 0.4 CuCl2 2H20 0.03 0.03 Cumene hydroperoxide 0.22 t-butyl perbenzoate - 0.22 Cabosil HS-5 1.7 1.7 Gel time 4.0' 3'15" - 4' 15" Shear Strength to 2350 psi 1900 psi Cq1O1OCRS - 10 mil glue line EXAMPLE XVI The following data illustrate the tolerance of the adhesive compositions of the invention. Using the adhesive of Example X, gel times of the mixed adhesives at different mix ratios were determined, following the procedure of Example I. The results are reported below EFFECT OF MIX RATIO ON GEL TIME EMI39.1 <tb> Part <SEP> A <SEP> 1 <SEP> 1 <SEP> 1 <SEP> 1 <SEP> 1 <SEP> 1 <SEP> 1 <SEP> 1 <SEP> 1 <SEP> 1 <SEP> 1 <SEP> 1 <SEP> 1 <tb> <SEP> Part <SEP> B <SEP> 9 <SEP> 4 <SEP> 2.3 <SEP> 2.1 <SEP> 1.9 <SEP> 1.8 <SEP> 1.6 <SEP> 1.5 <SEP> 1.4 <SEP> 1.3 <SEP> 1.2 <SEP> 1.1 <SEP> 1 <tb> Gel <SEP> time <SEP> NC <SEP> 42" <SEP> 22" <SEP> 20" <SEP> 19" <SEP> 19" <SEP> 17" <SEP> 17" <SEP> 17" <SEP> 17" <SEP> 16" <SEP> 16" <SEP> 16" <tb> EMI39.2 Part <SEP> A <SEP> 1 <SEP> 1 <SEP> 1 <SEP> 1 <SEP> 1 <SEP> 1 <SEP> 1 <SEP> 1 <SEP> 1 <SEP> 1 <SEP> 1 <SEP> 1 <tb> Part <SEP> B <SEP> .9 <SEP> .85 <SEP> 0.8 <SEP> 0.7 <SEP> .65 <SEP> 0.6 <SEP> .55 <SEP> 0.5 <SEP> .45 <SEP> 0.4 <SEP> .25 <SEP> .10 <tb> Gel <SEP> time <SEP> 16" <SEP> 16" <SEP> 16" <SEP> 16" <SEP> 15" <SEP> 15" <SEP> 16" <SEP> 15" <SEP> 16" <SEP> 17" <SEP> 19" <SEP> 60" <tb> EXAMPLE XVII The following data demonstrate the effect of inhibitor concentration upon cure rate: ADHESIVE 17-1 17-2 17-3 17-4 17-5 Tetrahydrofurfuryl methacrylate 46.4 46.5 46.6 46.7 46.8 Bisphenol-A fumarate polyester 46.2 46.1 46.0 45.9 45.8 Mercantosuccinic acid 0.46 0.46 0.46 0.46 0.46 CuCl2.2H2O 0.18 0.18 0.18 0.18 0.18 t-butyl perbenzoate 3.2 3.2 3.2 3.2 3.2 Water . 3.5 3.5 3.5 3.5 3.5 Benzoquinone 0.02 0.04 0.07 0.09 0.12 Gel rme, seconds 50 57 67 125 NCa a NC is no cure.

Claims: CLAIMS: 1. A three-component oxidation-reduction catalyst system consisting from 0.05 to 10 parts by weight of at least one organic hydroperoxide; from 0.005 to 2 parts by weight of at least one organic thiol; and from 0.0005 to 1 parts by weight of at least one inorganic or organic compound of a metal having a standard reduction potential in the range from +0.9 to -0.5. 2. A catalyst system according to claim 1 wherein said organic thiol comprises mercaptosuccinic acid. 3. A catalyst system according to claim 1 wherein said metal compound comprises cupric chloride. 4. A catalyst system according to claim 3 wherein said organic thiol comprises mercaptosuccinic acid. 5. A catalyst system according to claim 4 where said hydropersxide comprises cumene hydroperoxide. 6. An acrylic adhesive composition comprising I. a first package comprising (A) at least one olefinically unsaturated monomer; (B) at least one polymeric material selected from the group consisting of (1) at least one olefinically unsaturated urethane reaction product of at least one isocyanate-functional prepolymer and at least one hydroxy-functional monomer having at least one unit of polymerizable olefinic unsaturation, such reaction product being characterized by the presence of at least two units of olefinic unsaturation and the substantial absence of free isocyanate groups; (2) at least one butadiene-based elastomeric polymeric material selected from the group consisting of (a) homopolymer of butadiene; ; (b) copolymer of butadiene and at least one monomer copolymerizable therewith selected from the group consisting of styrene, acrylonitrile, methacrylonitrile and mixtures thereof; (c) modified elastomeric polymeric material selected from the group consisting of butadiene homopolymer and copolymer as previously defined, such homopolymer and copolymer having been modified by copolymerization therein by trace amounts up to 5 percent by weight, based on weight of modified elastomeric material, of at least one functional monomer; and (d) mixtures thereof; (3) at least one polymer-in-monomer syrup consisting essentially of (a) from 10 to 98 percent by weight of at least one olefinically unsaturated monomeric compound having at least one I I - C , C - group; (b) from 2 to 90 percent by weight of at least one polymer derived from such (3)(a) monomers; (c) from zero to 30 percent by weight of at least one polymer containing the grouo (CH2C Cl : CH CH2)n, wherein n is an integer; wherein (3)(b) is present as a partial polymerization product of (3)(a) or of (3)(a) in the presence of (3)(c); the mixture of (3)(a) and (3)(bj or of (3)(a), (3)(b) and (3)(c) being a syrup of polymer dissolved or dispersed in unpolymerized monomer, in which syrup the anount of (3)(b) derived from (3)(a) is in the range from 2 to 90 percent, based on the total weight of (3)(a), (3)(b) and (3)(c); (4) at least one polymeric material selected from the group consisting of polyvinyl alkyl ether, styrene-acrylonitrile resin, unsaturated polyester resin and mixtures thereof, the alkyl moiety of such ether containing from one to 8 carbon atoms; (5) at least one homopolymer or copolymer of at least one olefinically unsaturated monomer selected from the group consisting of styrene and alkyl or hydroxyalkyl esters of acrylic and methacrylic acid, saic ester having one to 18 carbon atoms in the alkyl moiety; ; (6) at least one polymeric material having at least one terminal olefinically unsaturated group, said polymeric material being selected from the group consisting of, (1) at least one adduct of at least one ethylenically unsaturated monofunctional isocyanate and at least one polymeric containing. one or more active hydrogen moieties selected from the.group consisting of -OH, -NH2, -NH-, EMI43.1 -SH and -COOH; and (2) at least one adduct of at least one reactive monomer having at least one terminal olefinically unsaturated grop and at least one reactive moiety selected from the group consisting of H, -NH2, -NH-, EMI43.2 -SH and -COOH, and at least one polymeric material which contains one or more moieties which are reactive with said reactive moiety of said reactive monomer, provided that, when said reactive moiety is -OH, said polymeric material does not contain a reactive -NCO group; and, (7) mixtures of such polymeric materials; and (C) at least one organometallic compound; a II second package comprising (A) at least one olefinically unsaturated monomer; (B) at least one polymeric material selected from the group consisting of (1) at least one olefinically unsaturated urethane reaction product of at least one isocyanate-functional prepolymer and at least one hydroxy-functional monomer having at least one unit of polymerizable olefinic unsaturation, such reaction product being characterized by the presence of at least two units of olefinic unsaturation and the substantial absence of free isocyanate groups; (2) at least one butadiene-based elastomeric polymeric material selected from the group consisting of (a) homopolymer of butadiene; (b) copolymer of butadiene and at least one monomer copolymerizable therewith selected from the group consisting of styrene, acrylonitrile, methacrylonitrile and mixtures thereof; ; (c) modified elastomers polymeric material selected from the group consisting of butadiene homopolymer and copolymer as previously defined, such homopolymer and copolymer having been modified by coolymerization therein by trace amounts up to 5 percent by weight, based on weight of modified elastomeric material, of at least one functional monomer; and (d) mixtures thereof; (3) at least one polymer-in-monomer syrup consisting essentially of (a) from 10 to 98 percent by weight of at least one o efinically unsaturated monomeric compound having at least one - C: C - group; (b) from 2 to 90 percent by weight of at least one pclymer derived from such (3)(a) monomers; (c) from zere to 30 percent by weight of at least one polymer containing the group (CH2C CI : CH CH2)n, wherein n is sn integer; wherein (3)(b) is present as a partial polymerizatic- product of (3)(a) or of (3)(a) in the presence of (3)(c); the mixture of (3)(a) and (3)(b) or of (3)(a), (3)(b) and (3)(c) being a syrup of polymer dissolved or dispersed in unpolymerized monomer, in which syrup the amount of (3)(b) derived from (3)(a) is in the range from 2 to 90 percent, based on the total weight of (3)(a), (3)(b) and 93)(c); (4) at least one polymeric material selected from the group consisting of polyvinyl alkyl ether, styrene-acrylonitrile resin, unsat rat-ed polyester resin and mixtures thereof, the alkyl moiety of such ether containing from one to 8 carbon atoms; ; (5) at least one homopolymer or copolymer of at least one oNefinically unsaturated monomer selected from the group consisting of styrene and alkyl or hydroxyalkyl esters of acrylic and methacrylic acid, said cster having from one to 18 carbon atoms in the alkyl moiety; (6) at least one polymeric material having at least one terminal olefinically unsaturated group, said polymeric material being selected from the group consisting of, (1) at least one adduct of at least one e hylenically unsaturated monofunctional isocyanate and at least one polymeric containing one or more active hydrogen moieties selected from the group consisting of H, -NH2, -NH-, EMI45.1 -SH and -COOH; and, (2) at least one adduct of at least one reactive monomer having at least one terminal olefinically unsaturated group and at least one'reactive moiety selected from the group consisting of -OH, -NH2, -NH-, EMI45.2 -SH and -COOH, and at least one polymeric material which contains one or more moieties which are reactive with said reactive moiety of said reactive monomer, provided that, when said reactive moiety is -OH, said polymeric material does not contain a reactive -NCO group; (7) mixtures of such polymeric materials; (C) at least one organic sulfur containing compouna having at least one -SH group or having a tautomeric form containing at 'east one -°H group; and (D) at least one peroxygen compound selected from the group consisting of hydrogen peroxide, organic peroxyesters and organic hydroperoxi des; wherein the volume or weight, respectively, of said first package is substantially equal to the volume or weight, respectively, of said second package, at the time when said packages are intermixed. 7. An acrylic adhesive composition according to claim 6 containing up to 10 percent by weight of an organic compound containing at teast one hydroxyl group. 8. An acrylic adhesive composition according to claim 6 containing up to 2 percent by weight of water. 9. An acrylic adhesive composition according to claim 7 containing up to 2 percent by weight of water. 10. An adhesive composition according to claim 6 wherein said organic.sulfur-containing compound is mercaptosuccinic acid. 11. An adhesive composition according to claim 6 wherein said metal ion-containing compound is cupric chloride. 12. An adhesive composition according to claim 11 wherein said organic sulfur-containing compound is mercaptosuccimic acid. 13. An adhesive composition according to claim 12 containing up to 10 percent by weight of an organic compound containing at least one hydroxyl group. 14. An adhesive composition according to claim 12 containing up to 2 percent by weight of water. 15. An adhesive composition according to claim 13 containing up to 2 percent by weight of water. 16. A process for bonding mating surfaces of two or more metal substrates comprising applying to at least one of such surfaces a room temoerature-curable adhesive composition comprising (A) at least one olefinically unsaturated monomer; (B) at least one polymeric material selected from the group consisting of (1) at least one olefinically unsaturated urethane reaction product of at least one isocyanate-functional prepolymer and at least one hydroxy-functional monomer having at least one unit of polymerizable olefinic unsaturation, such reaction product being characterized by the presence of at least two units of olefinic unsaturation and the substantial absence of free isocyanate groups; (2) at least one butadiene-based elastomeric polymeric material selected from the group consisting of (a) homopolymer of butadiene; ; (b) copolymer of butadiene and art least one monomer copolymerizable therewith selected from the group consisting of styrene, acrylonitrile, methacrylonitirle and mixtures thereof; (c) modified elastomeric polymeric material selected from the group consisting of butadiene homopolymer and copolymer as previously defined, such homopolymer and copolymer having been modified by copolymerization therein by trace amounts up to 5 percent by weight, based on weight of modified elastomeric material, of at least one functional monomer; and (d) mixtures thereof; (3) at least one polymer-in-monomer syrup consisting essentially of (a) from 10 to 98 percent by weight of at least one olefinically unsaturated monomeric compound having at least one - C : C group; (b) from 2 to 90 percent by weight of at least one polymer derived from such (3)(a) monomers; (c) from zero to 30 percent by weight of at least one polymer containing the group (CH2 C Cl CH CH2)n, wherein n is an integer; wherein (3)(b) is present as a partial polymerization product of (3)(a) or of (3)(a) in the presence of (3)(c); the mixture of (3)(a) and (3)(b) or of (3)(a), (3)(b) and (3)(c) being a syruD of polymer dissolved or dispersed in unpolymerized monomer, in which syrup the amount of (3)(b) derived from (3)(a) is in the range from 2 to 90 percent, based on the total weight of (3)(a), (3)(b) and (3)9c); (4) at least one polymeric material selected from the group consisting of polyvinyl alkyl ether, styrene-acrylonitrile resin, unsaturated polyester resin and mixtures thereof, the alkyl moiety of such ether containing from one to 8 carbon atoms; (5) at least one homopolymer or copolymer of at least one olefinically unsaturated monomer selected from the group consisting of styrene and alkyl or hydroxyalkyl esters of acrylic and methacrylic acid, said ester having one to 18 carbon atoms in the alkyl moiety; ; (6) at least one polymeric material having at least one terminal olefinically unsaturated group, said polymeric material being selected from the group consisting of, (1) at least one adduct of at least one ethylenically unsaturated monofunctional isocyanate and at least one polymeric containing one or more active hydrogen moieties selected from the group consisting of -OH, -NH2, -NH, EMI48.1 -SH and -COOH; and, (2) at least one adduct of at least one reactive monomer having at least one terminal olefinically unsaturated group and at least one reactive moiety selected from the group consisting of -OH, -NH2,-NH, EMI48.2 -SH and -COOH, and at least one polymeric material which contains one or more moieties which are reactive with said reactive moiety of said reactive monomer, provided that, when said reactive moiety is -OH, said polymeric material does not contain a reactive -NCO group; and (7) mixtures of such polymeric materials; (C) at least one inorganic or organic compound of a metal ion, said metal ion having a standard reduction potential in the range from +0.9 to -0.5. (D) at least one organic sulfur-containing compound having at least one -SH group or having a tautomeric form containing at least one -SH group; and (E) at least one peroxygen compound selected from the group consisting of hydrogen peroxide, organic peroxyesters and organic hydroperoxides; and placing the mating surfaces in abutting relationship until the adhesive composition cures to effect bonding of said surfaces.

Inventors: BENNETT, RUTH MARIE, ZALUCHA, DENIS JEROME
Applicants: LORD CORPORATION
Application year: 1985
Main classification: C09J3
IPC codes: C09J4, C08F4, C08F299, C09J175