A LIQUID COATING COMPOSITION, A METHOD OF COATING A METAL SUBSTRATE AND THE METAL SUBSTRATE THUS OBTAINED

Abstract: The invention provides a coating composition for metal surfaces containing a binder, a high amount of an electrically conductive pigment such as zinc, and 0,05-5 per cent by weight, calculated on the coating composition, of at least 2 solid, powdered lubricants, at least one of them being inorganic. The invention also relates to a process for coating a metal surface using said coating composition, and the properly machinable and weldable coated substrate thus obtained.

Description: The invention relates to a liquid coating composition based on a binder and an electrically conductive pigment in an amount of at least 30 per cent by volume, calculated on the pigment and the binder. Coating compositions of this type are applied to metal substrates, such as metal strip and especially steel strip and impart corrosion inhibiting properties to the metal and the high content of electrically conductive pigment renders the metal weldable. The metal substrate thus provided with such a coating is generally deformed by a non-cutting process, for instance by pressing. But there is the chance then that the coating will be flaked off and destroyed, which has a detrimental effect on corrosion inhibiting protection. An additional disadvantage is the contamination of shaping tools, so that production must be interrupted after every 50 or 100 pressing operations to clean the equipment, because soiled equipment will cause undesirable surface depressions in the metal. According to British Patent Specification 1 481 467 this drawback, which is a major problem in, for instance, the automobile industry, is met by applying to the coating another coating composed of 50-70% by weight of a substance promoting sliding and 50-30% by weight of an organic binder. A disadvantage to that method, however, is that production is detrimentally affected and additional capital expenditure is required. GB-A-2 055 875 pertains to a coating composition based on a fluorine-containing polymer and an additive having a density of at least 8 g/cm³. The additive may be metallic lead or a lead compound and is meant to increase the adhesion between the fluorine-containing polymer and the substrate. As an antifriction compound either an organic compound or an inorganic substance is used. In all examples only PTFE is used, and in a high proportion. Moreover, the compound is melted after application. AU-A-205 538 discloses a composition containing 3 essential components, i.e. zinc, zinc oxide and molybdenum sulfide. The latter component is the only lubricant and it is used in the very high proportion of 10-40 parts to 6-10 parts of zinc/zinc oxide. GB-A-1 019 202 pertains to an aqueous 2-phase composition containing an inorganic complex consisting of dissolved phosphate, (di)chromate or molybdate. Also this reference discloses the use of very high proportions of a lubricant. Moreover, the composition applied is heated to above the fusion temperature of PTFE. Surprisingly, it has now been found according to the invention that by adapting the coating composition itself, i.e. without additional capital outlay or detrimental effect on production, the coated metal substrate will remain excellently weldable and keep its corrosion inhibiting property, while the workability of the substrate will be greatly enhanced. The coating composition according to the invention is characterized in that the coating composition contains at least 2 solid, powdered lubricants in a total amount of 0.05-5 percent by weight, calculated on the coating composition, at least one of them being an inorganic lubricant. The composition according to the invention may contain any usual binder, such as a hydroxyl group-containing resin. As examples of representative binders may be mentioned compounds containing at least 1 epoxy group, such as epoxy resins and phenoxy resins, which may optionally be mixed with one or more other resins. Examples of suitable solid or liquid epoxy resins include glycidyl groups-containing resins such as polyacrylic resins, polyesters, polyethers or polyurethanes which all contain one or more glycidyl groups per molecule. Representative epoxy resins include compounds of the following general formula: wherein R represents an aliphatic, cycloaliphatic or aromatic group and n is a number in the range of from 0 to 50, preferably 0 to 10, or an adduct thereof with a (cyclo)aliphatic or heterocyclic diamine, preferably a disecondary amine, such as piperazine. Examples of such epoxy resins include the glycidyl ethers of, say, ethylene glycol, diethylene glycol, triethylene glycol, 1,2-propylene glycol, 1,3-propylene glycol, 1,5-pentane diol, bis - (4 - hydroxycyclohexyl) - 2,2 - propane, 4,4′ - dihydroxybenzophenone, bis - (4 - hydroxyphenyl)methane, bis(4 - hydroxyphenyl) - 1,1 - ethane, bis - (4 - hydroxyphenyl) - 1,1 - isobutane and 1,5 - dihydroxynaphthalene. If desired, used may be made of polyglycidyl ethers of compounds such as glycerol or 1,2,6-hexane triol. More particularly, it is preferred that use should be made of a diglycidyl ether based on bis - (4 - hydroxyphenyl) - 2,2 - propane. Use may also be made of mixtures of epoxy resins. As suitable phenoxy resins may be mentioned, for instance, phenoxy resins available under the trade marks Phenoxy PKHC and Phenoxy PKHH of Union Carbide. These last-mentioned resins are physically drying. Epoxy resins having a relatively low molecular weight may be cured with the aid of, for instance, suitable polyamines, amides, polyaminoamides and blocked or non-blocked polyisocyanates or aminoplasts. As other examples of suitable binders may be mentioned polyacrylate resins, nitrocellulose, epoxy esters and block copolymers of the formula A-(B-A) m , or B-(A-B) n , wherein m and n are numbers in the range of from 1 to 20, and built up of one or more blocks A of a carboxylic polyester resin from terephthalic acid and/or isophthalic acid and a difunctional hydroxy compound and having an acid number of 10-140 and a number average molecular weight of 800-10 000, and of one or more blocks B of an epoxy resin having an epoxy functionality of 1,5-2,5 and an epoxy equivalent weight of 100-2000. As examples of suitable curing agents for the hydroxyl group-containing polymer may be mentioned blocked or non-blocked isocyanurate compounds or blocked or non-blocked aliphatic, cycloaliphatic or aromatic di-, tri- or polyvalent isocyanates. Examples of suitable isocyanates include hexamethylene diisocyanate, 2,2,4 - trimethyl - 1,6 - hexane diisocyanate, 2,4,4 - trimethyl - 1,6 - hexane diisocyanate, cyclohexyl - 1,4 - diisocyanate, isophoron diisocyanate, the adduct of 1 molecule of 1,4-butane diol and 2 molecules is isophoron diisocyanate, the adduct of 1 molecule of 1,4-butane diol and 2 molecules of hexamethylene diisocyanate, dicyclohexylmethane - 4,4′ - diisocyanate, xylylene diisocyanate, 1,3,5 - trimethyl - 2,4 - bis(isocyanatomethyl)benzene, toluene diisocyanate, diphenylmethane - 4,4′ - diisocyanate, the adduct of 3 molecules of hexamethylene diisocyanate and 1 molecule of water, the adduct of 1 molecule of trimethylol propane and 3 molecules of isophoron diisocyanate, the adduct of 1 molecule of trimethylol propane and 3 molecules toluene diisocyanate and the adduct of 1 molecule of pentaerythritol and 4 molecules of hexamethylene diisocyanate. For blocking the isocyanate or isocyanurate compound, if required, use may be made of any conventional or suitable blocking agent. Instead of or in addition to the above-described curing agents other suitable agents that may be used are, for instance, N-methylol groups and/or N-methylol ethers groups-containing aminoplasts obtained by reaction of an aldehyde, such as formaldehyde, with an amino groups- or amido groups-containing compound, such as melamine, urea, N,N′-ethylene urea, dicyandiamide and benzoguanamine; for the preparation of these compounds see for example Houben-Weyl, Methoden der organischen Chemie; Vol. 14/2, pp. 319-371 (1963). It is preferred that these compounds should entirely or partly be etherified with alcohols having 1 to 6 carbon atoms, for instance with methanol, ethanol, n-propanol, isopropanol, n-butanol, isobutanol, amyl alcohol, hexanol or mixtures of the above-envisaged alcohols. More particularly, use is made of a methylol melamine having 4 to 6 methylol groups per molecule of melamine, with at least 3 methylol groups being etherified with methanol, ethanol, a propanol or with a butanol, or a butanol-etherified condensation product of formaldehyde and N,N′-ethylene diurea. The coating composition also contains an electrically conductive pigment in an amount of at least 30, and preferably at least 50 percent by volume, calculated on the pigment and the binder. As examples of suitable electrically conductive pigments may be mentioned micaceous iron oxide, iron phosphide, magnetite, gas black or furnace carbon black. It is preferred that the electrically conductive pigment used should be a metal, for instance: aluminium, copper, (stainless) steel, cadmium and particulary zinc. Use also may be made of mixtures of 2 or more electrically conductive pigments, for instance a mixture of zinc and aluminium. The zinc may be applied in any finely divided form, for instance as zinc dust or as flakes. According to the invention the coating composition contains a mixture of at least 2 solid, powdered lubricants, at least one of them being an inorganic lubricant. As examples of suitable inorganic lubricants may be mentioned metal compounds such as molybdenum disulphide, tungsten disulphide, lead disulphide and compounds such as graphite. A preferred inorganic lubricant is a heavy metal sulphide and more paraticularly molybdenum disulphide. According to the invention the inorganic lubricant is contained in the coating composition in an amount of generally 0,05-5% by weight, preferably 0,08-3,1% by weight and more particularly of 0,1-1,9% by weight, calculated on the coating composition. As examples of suitable organic lubricants may be mentioned polytetrafluoroethene and polytrifluoroethene. Preferably use is made of a polytetrafluoroethene having a number average molecular weight of 35 000-100 000 and an average particle size of 0,1-40 µm. According to the invention the organic lubricant is contained in the coating composition in an amount of preferably not higher than 3% by weight, particularly 0,02-1,9% by weight, more particularly 0,1-0,8% by weight, based on the coating composition. A particularly preferred mixture of lubricants is a mixture of molybdenum disulphide and polytetrafluoroethene. According to the invention and total amount of lubricant contains in the coating composition is 0,05-5% by weight, preferably 0,1-2,7% by weight, and more particularly 0,3-2% by weight, based on the coating composition. The lubricants may be combined with each other and with the other components of the coating composition in any suitable manner. For instance, the lubricants may be first mixed with each other and the resulting mixture be added to the binder or a solution thereof. The coating composition generally contains an organic solvent for the binder. As examples of suitable solvents may be mentioned ethyl glycol acetate, isophorone, methyl isobutyl ketone or mixtures, optionally with hydrocarbons such as toluene or xylene. The coating composition may optionally contain other additives, such as anti-sag agents, levelling agents, pigment dispersing agents, dyes, pigments and corrosion inhibiting agents. The coating composition may be applied to the substrate in any suitable manner, in actual practice by roller coating or spraying. Applicable coating thickness are for instance generally in the range of 1-60 µm, preferably 5-25 µm. The substrate used is generally of a pretreated or non-pretreated metal or alloy, such as iron, steel, tin plate, galvanized iron, or iron or steel plated in some other way with a coating of zinc or alloy, or of copper or aluminium; preferably use is made of an iron or steel substrate, which is usually in the form of a sheet. Optionally, the metal substrate may have been pretreated, for instance; phosphated or chromated. The coating composition may be cured or baked in the usual manner. When the coating composition is used in coil coating, it is cured at a temperature of, for instance, about 100°-280°C, which is the usual final curing temperature of the substrate; that temperature could as a rule only be obtained by contacting the coated substrate for a short time (for instance: 10-90 seconds) with air or combustion gases at a temperature of 250°-400°C. The application and coating conditions used in the case of coil coatings are well known to any one skilled in the art and require no further description here. For other fields of application use may be made of different temperature ranges. The substrate thus coated may optionally still be top-coated. In the following examples, which give a further description of the invention, the adhesion of the cured coating is measured with a lubricant tester of the Detroit Testing machine Co. in which the test panel is drawn twice through a die in such a way that the panel undergoes an elongation of 44%. Previously, the test panels are provided with a film of lubricating oil. When the coating is found not to be visibly damaged, the adhesion is rated as "good", in the case where more than 1 % of the coating is removed, the adhesion is "poor", and between these two extremes the adhesion is rated as "moderate" (see General Motors Engineering Standards, April 1978, pp. W-23401 and W-23402). Example 1 To a coating composition made up of 8 parts by weight of a phenoxy resin (available under the trade mark Phenoxy PKHH of Union Carbide), 52 parts by weight (50% by volume calculated on the pigment and the binder) of zinc dust and 40 parts by weight of ethyl glycol acetate there is added a mixture of 0,2 parts by weight of molybdenum disulphide and 0,2 parts by weight of polytetrafluoroethene. For comparison, to an identical coating composition 0,4 parts by weight of molybdenum disulphide are added and to another identical coating composition no lubricant is added at all. The compositions were roller coated onto steel panels to a coating thickness of 14 µm (in the cured state) and cured by leaving the panels in an oven for 2535 seconds at a temperature of 300°-400°C, so that the maximum temperature of the panels was about 260°C. The adhesion measured is given in the table below.

Claims: 1. A liquid coating composition based on a binder and an electrically conductive pigment in an amount of at least 30 percent by volume, calculated on the pigment and the binder, characterized in that the coating composition contains at least two solid, powdered lubricants in a total amount of 0,05-5 percent by weight, calculated on the coating composition, wherein at least one of the solid lubricants is an inorganic lubricant. 2. A coating composition according to claim 1, characterized in that the inorganic lubricant is a heavy-metal disulphide. 3. A coating composition according to claim 2, characterized in that the inorganic lubricant is molybdenum disulphide. 4. A coating composition according to claim 1, characterized in that the inorganic lubricant is present in an amount of 0,08-3,1% by weight, calculated on the coating composition. 5. A coating composition according to claim 1, characterized in that it contains an organic lubricant. 6. A coating composition according to claim 5, characterized in that the organic lubricant is a polytetrafluoroethane having a number average molecular weight of 35000-100000 and an average particle size in the range of from 0,1 to 40 µm. 7. A coating composition according to claim 5, characterized in that the organic lubricant is present in an amount of 0,02-1,9% by weight, calculated on the coating composition. 8. A coating composition according to claim 5, characterized in that the lubricants are molybdenum disulphide and polytetrafluoroethane. 9. A coating composition according to claim 1, characterized in that the binder comprises an hydroxyl group-containing resin or a compound containing at least one epoxy group. 10. A coating composition according to claim 9, characterized in that the compound containing at least one epoxy group comprises an epoxy resin or a phenoxy resin. 11. A coating composition according to claim 10, characterized in that the epoxy resin comprises a glycidyl group-containing polyacrylic, polyester, polyether or polyurethane resin. 12. A coating composition according to claim 9, characterized in that the hydroxyl group-containing resin comprises a polyacrylate resin, a nitrocellulose or an epoxy ester. 13. A coating composition according to claim 9, characterized in that the hydroxyl group-containing resin comprises a block copolymer of the formula A-(B-A) m or B-(A-B) n , wherein m and n are numbers in the range of 1 to 20, and built up of: (i) one or more blocks A of a carboxylic polyester resin from terephthalic acid and/or isophthalic acid, and a difunctional hydroxy compound, and having an acid number of 10-140 and a number average molecular weight of 800-10000, and (ii) one or more blocks B of an epoxy resin having an epoxy functionality of 1,5-2,5 and an epoxy equivalent weight of 100-2000. 14. A coating composition according to claim 9, characterized in that the binder comprises an hydroxy group-containing resin and the coating composition further comprises a curing agent for the hydroxyl groups of the hydroxyl-group containing resin. 15. A coating composition according to claim 9, characterized in that the binder comprises a compound containing at least one epoxy group and the coating composition further comprises a curing agent for the epoxy group of the compound. 16. A method of coating a metal substrate, characterized in that a coating composition according to any one of the claims 1-15 is applied to a substrate and cured. 17. A method according to claim 16, characterized in that the coating composition is applied by roller coating or spraying. 18. A method according to claim 16, characterized in that the coating composition is cured at a temperature of the metal substrate of 100° to 280°C. 19. A coated metal substrate obtained by the method of any one of the claims 16-18.

Inventors: PICHANT, PATRICK
Applicants: AKZO N.V.
Application year: 1985
Main classification: C09D5
IPC codes: C09D7, C09D5