PROCESS FOR PELLETIZATION OF POWDER MATERIALS AND PRODUCTS THEREFROM

Abstract: A method for the production of small, dustless, free-­ flowing pellets of powder chemical additives utilizing a high molecular weight polymeric binder, such as polyvinyl alco­ hol; a surfactant containing oxyethylene groups; and water.

Description: BACKGROUND OF THE INVENTION The market demand for dustless and free-flowing chemical products has increased significantly and is likely to continue in this trend. The demand for dust-free, flowable materials is especially high in the compounding of rubber and polymeric compositions. The use of finely divided materials in compounding of natural and synthetic rubber presents dusting problems which may have adverse consequences relative to productivity, contamination, environmental pollution, and safety. The finely divided nature of most rubber additives causes them to be blown into the air during production operations such as conveying, mixing or milling. This results in a production efficiency reduction due to the loss of some additives. Additionally, the dusting problem can result in the possible contamination of other materials. Further, airborne dust causes environmental and housekeeping problems, as well as safety hazards created by the explosive nature of finely divided dust. Bridging problems of powder materials also adversely affect their use in automatic feeding systems. Thus, it is desirable to have rubber and polymer additives in a dustless, free-flowing form with good dispersion properties so that processors can meet environmental regulations, application needs, and implement automatic feeding systems for improved productivity. Efforts have been made in the art to eliminate the problems associated with finely divided materials by converting such materials into agglomerates. To form such agglomerates, generally an agglomerating agent must be added to the finely divided materials. Frequently, this agglomerating agent has been a material which was objectionable when mixed into a rubber compound with which the finely divided material was used. Some of the prior art agglomerates were cohesive and thus not free-flowing, and do not lend themselves to normal or automatic handling and weighing procedures. Some materials employed for preparing prior art agglomerates were used in such large amounts that they diluted the rubber ingredients or did not readily disperse in rubber during mixing. In many of the prior art agglomerates, the pellet crush strength was either too low or too high. Agglomerates with too low of a crush strength are undesirable because of their inability to withstand normal shipping and handling. Agglomerates having too high of a crush strength generally had poor dispersing properties and did not mix well. Typical processes for agglomerating powder materials are disclosed in US-A-4,362,559; 4,194,901; and 4,298,858; CA-A-890,833; Japanese patent nos. 78 90,116; 78 66,923; 8,205,731 and 82,192,439; and CS-B-185,383. It is the objective of the present invention to solve the above problems associated with powder materials and prior art agglomerates by providing a pelletization process for making small, dustless, and free-flowing products which have good dispersion properties. It is a further objective of the present invention to produce pellets of chemical additives which have a very low level of agglomerating agents and other processing aids. A major advantage of the present invention is the production of pellets with a pellet crush strength range suitable for both shipping and effective dispersion, which is controllable to custom specifications. SUMMARY OF THE INVENTION This invention relates to a method for producing dustless pellets from water insoluble chemical additives for rubber and polymers, which comprises; combining the powders with a processing aid system containing essentially of an effective amount of high molecule weight water soluble polymeric binder, an organic surfactant, and water, wherein the powder chemical additives are essentially 100 parts by weight and is selected from the group consisting of N-oxydiethylene thiocarbamyl N'-oxydiethylene sulfenamide, N-t-butyl-2-benzothiazole sulfenamide, 2-mercaptobenzothiazole disulfide, and N-oxydiethylene-2-benzothiazole sulfenamide, wherein the polymeric binder is from 0.2 to 4 parts by weight and is selected from the group consisting of partially hydrolyzed polyvinyl alcohols, fully hydrolyzed polyvinyl alcohols, alkyl cellulose derivative and hydroxy alkyl cellulose derivatives; wherein the surfactant is from 0.2 to 1 part by weight and is a polyoxyethylene alcohol or acid derivative; and water. The polymeric binder is preferably polyvinyl alcohol or a cellulose derivative. The surfactant preferably contains a polyoxyethylene group. The current method is particularly suitable for the formation of pellets by a screw extrusion process and yields small, dustless, and free-flowing pellets which have good dispersion properties which equal or exceed that of the powder. DETAILED DESCRIPTION The present invention relates to a novel method for the production of dustless pellets from powders and to the pellet products produced thereby. The method comprises using a processing aid system essentially containing an effective amount of a high molecular weight water-soluble polymeric binder, an organic surfactant, and water. Although the method may be carried out utilizing a variety of agglomeration techniques, such as roll pressing, pellet milling, spray drying, and screw extrusion, the method is particularly suitable for pellet formation using screw extrusion. Powders which are suitable for pelletization utilizing the present invention can be any water insoluble chemical powder used as a process additive. The present method is particularly suited for pelleting powders of organic rubber chemicals and chemical additives for plastic polymers. Suitable powders include, for example, accelerators, vulcanizing agents, pigments, stabilizers, antioxidants, fillers, curing additives, reinforcing agents, and the like. Binders are essential aids to economic and effective agglomeration of solids. In the screw extrusion process particularly, the pressure applied is not sufficiently high for compaction and a binder is needed to agglomerate the powders. In order to obtain uniform pellet strength with a very low processing aid ingredient content in the final product, high molecular weight water soluble polymeric binders are used in practicing this invention. These high molecular weight polymeric binders work well with water to provide a thin film between powder particles, and to entangle the particles into agglomerates which exhibit improved plasticity under shear force and pressure. Suitable polymeric binders for the practice of this invention include most water-soluble film-forming resins; for example, partially and fully-hydrolyzed polyvinyl alcohols, polyacrylamides, acrylamide-acrylic acid copolymers, starches, polyacrylic acids, ethylene oxide polymers and alkyl and hydroxyalkyl cellulose derivatives, such as, for example, methyl cellulose, hydroxy propyl methyl cellulose, hydroxy ethyl cellulose. Suitable concentration of binder ranges from 0.2 to 4 parts by weight per 100 parts of dry powder, preferably from 0.2 to 2 parts. The preferred binder is a polyvinyl alcohol or an alkyl or hydroxyalkyl cellulose derivative. Most preferably the polyvinyl alcohol has a molecular weight of 10,000 or greater. The present invention involves the use of an organic surfactant to obtain pellets having the desired characteristics. Suitable organic surfactants include, for example, water soluble or dispersible nonionic surfactants, propylene glycols and polymeric surfactants such as the polyoxyethylene derivatives. The preferred organic surfactants for the practice of this invention are the polyoxyethylene derivatives, such as, for example, polyoxyethylene acids, polyoxyethylene alcohols, oxyethylene-oxypropylene copolymer. More preferably the organic surfactant contains more than two oxyethylene units, and most preferably the surfactant is a polyoxyethylene oleyl ether or a polyoxyethylene stearate. In order to work effectively in the present invention, the surfactant must be stable with the powder chemical additives, especially with accelerators, during processing and storage, and must be fairly soluble in water. Specifically, polyoxyethylene (10) oleyl ether, polyoxyethylene (20) oleyl ether, and polyoxyethylene (50) stearate were found to work well in the process of this invention. The use of an organic surfactant is critical for the practice of the present invention regardless of the method of agglomeration used. The use of a surfactant is especially important in pelletization by the screw extrusion process. The surfactant makes the production of desired pellets with screw extrusion possible and provides the following multi-functions: 1) The surfactant serves as a wetting agent to help the aqueous solution wet the particle surfaces of organic powder. Wetting is important for uniformly spreading the binder on powder particles to provide good and uniform binding and reduces the amount of binder required. 2) The surfactant serves as a lubricant and plasticity improving agent. This improves the plasticity of the whole mass and makes it easier to extrude into the desired shape. This also reduces extruder power requirements and increases extruder output. 3) Most importantly, the surfactant acts as a pellet crush strength controller. By adjusting the ratio of primary binder and surfactant, plasticity, ingredient content, and pellet strength can be controlled to desired levels. Suitable levels of surfactant ranges from 0.2 to 1.0 parts by weight per 100 parts of dry powder. Another important component of the processing aid system used in the practice of this invention is water. The primary function of water is to dissolve and carry ingredients such as the binder and surfactant. Water works with the binder and surfactant to provide the lubrication between particles and plasticity for the whole mass. Water also contributes binding action through capillary force in the wet pellet due to its high surface tension. The amount of water needed to wet the particle surface and fill the space between the particles is determined by the particle size, shape, and other properties of the powder particles. Typically the amount of water ranges from 10 parts to 45 parts by weight per 100 parts of dry powder. The water may be added directly to the binder and surfactant or it may be present in wet filter cakes of the powder chemical additives. Where wet filter cakes of the additives are used, the dry binder and surfactant may be added to the filter cakes by blending prior to the pelletization step. In the preferred embodiment of this invention, three main steps are involved, i.e., mixing, extruding and drying. Other agglomerating techniques may be used instead of extrusion, such as, for example, roll pressing, pellet milling, and spray drying. The binder and the surfactants can be dissolved or dispersed in water and subsequently mixed with the dry powder. The dry binder and surfactant can also be mixed with wet powder and then fed to the extruder. The mix is agglomerated through a screw extruder into extrudates. The extrudates are then broken into short pellets either outside or inside of a dryer and dried in the dryer. The present process allows the pellet cutting or breaking to be performed with the minimal generation of fines. In the process, about 98% of the powder is converted to pellets and less than 2% as fines. Good mixing is important for uniformly spreading liquid and processing aids on the powder particle surfaces, and any conventional mixing equipment may be used. Good mixing provides the uniformity of feed material for extruding and, thus, the uniform quality of the final product. The present invention yields small, dustless, free-flowing pellets with a satisfactory crush strength and a low level of processing aid ingredients. These pellets can meet the needs of practically all applications in the rubber and plastic industries. Pellet crush strength is important for shipping and for dispersion. If the pellet is too soft, it cannot withstand shipping and handling conditions, but if it is too hard it causes dispersion problems during compounding. Pellet crush strength is measured by applying weight on the pellet until it is crushed and then dividing the total weight applied by the cross-sectional area of the pellet incurring the weight. A pellet crush strength in the range of 10 to 40 g/mm² is preferred for effective shipping and dispersion. One major advantage of the present process is that the pellet strength can be adjusted by changing the amount of binder and surfactant utilized. Pellets having crush strengths from 5-100 g/mm² are obtainable. The flexibility of making a wide range of uniform pellet sizes is another major advantage of this process. Preferably the pellet size ranges from 0.5mm to 2mm in diameter and from 2mm to 4mm in length. Small pellets of this size exhibit better dispersion and flowability properties. The pellets are preferably cylindrical in shape and have an angle of repose smaller than 40°. After the pellets are dried, the processing aid ingredients in the final pellet product essentially consist of binder and surfactant. A suitable final pellet product should contain 4% or less of processing aid ingredients on a dry weight basis; preferably 2% or less; and most preferably less then 1%. To illustrate this invention, pellets were made following the present inventive process from dry powders of accelerators for rubber. In each example, the binder and surfactant were dissolved in water and subsequently mixed with the dry accelerator powder. The mix was then screw extruded, pelletized, dried and evaluated. The specific recipes used are given in Table I. In all Examples 100 parts by weight of dry accelerator powder were used. Accelerator (100 pbw) EXAMPLES I II III IV (OTOS) (BBTS) (OMTS) (MBTS) Binder (Polyvinyl Alcohol) 0.25 0.75 0.40 0.25 Surfactant (Polyoxyethylene oleyl ether) 0.25 0.50 0.60 0.20 Water 14 40 22 43 OTOS= N-oxydiethylene thiocarbamyl N'-oxydiethylene sulfenamide BBTS= N-t-butyl-2-benzothiazole sulfenamide MBTS= 2-mercapto benzothiazole disulfide OMTS= MBTS/N-oxydiethylene-2-benzothiazole sulfenamide All amounts are parts by weight. In all Examples, essentially dustless, cylindrical pellets were made. The pellets were free-flowing and had angles of repose smaller than 45°. The pellet crush strength in the Examples ranged from 20-35 g/mm². Pellet sizes ranged from 1 to 2mm in diameter and from 1 to 4mm in length. Pellet size was uniform with nearly all the particles being retained on 10-12 mesh screens. Pellets of OTOS made by the present process were evaluated in a typical styrene-butadiene rubber stock. Vulcanizates of the stock were cured for 15 minutes at 320°F (160°C) and tested for stress/strain properties. The OTOS pellets were compared to an equivalent amount of powder to evaluate dispersibility. Poor dispersibility is usually reflected by a lower tensile strength and lower elongation. The results are presented in Table II. OTOS Powder (control) OTOS Pellet Tensile strength Mpa (psi) 18.9 (2744) 20.8 (3016) Elongation (%) 526 566 300% modulus Mpa (psi) 9.1 (1319) 9.1 (1322)

Claims: A method for producing dustless pellets from water insoluble chemical additives for rubber and polymers, which comprises; combining the powders with a processing aid system containing essentially an effective amount of high molecule weight water soluble polymeric binder, an organic surfactant, and water, wherein the powder chemical additives are essentially 100 parts by weight and is selected from the group consisting of N-oxydiethylene thiocarbamyl N'-oxydiethylene sulfenamide, N-t-butyl-2-benzothiazole sulfenamide, 2-mercaptobenzothiazole disulfide, and N-oxydiethylene-2-benzothiazole sulfenamide, wherein the polymeric binder is from 0.2 to 4 parts by weight and is selected from the group consisting of partially hydrolyzed polyvinyl alcohols, fully hydrolyzed polyvinyl alcohols, alkyl cellulose derivatives and hydroxy alkyl cellulose derivatives; wherein the surfactant is from 0.2 to 1 part by weight and is a polyoxyethylene alcohol or acid derivative; and water. The method of claim 1, wherein the surfactant is a polyoxyethylene oleyl other or a polyoxyethylene stearate. The method of Claim 2, wherein said pellets are formed by screw extrusion. The method or Claim 3, wherein the pellet size ranges from 0.5 to 2 mm in diameter and from 2 to 4 mm in length; and the pellets have a pellet crush strength which ranges from 10 to 40 g/mm². The method of Claim 4, wherein the polyvinyl alcohol has a molecular weight of 10,000 or greater. A pellet product, comprising; one or more water insoluble chemical powder additives for rubbers and organic polymers made with a processing aid system containing essentially per 100 parts by weight of said powder additives, which are selected from the group consisting of N-oxydiethylenethiocarbamyl-N'-oxydiethylene sulfenamide, N-t-butyl-2-benzothiazole sulfenamide, 2-mercaptobenzothiazole disulfide, and N-oxydiethylene-2-benzothiazole sulfenamide; from 0.2 to 4 parts by weight of a high molecular weight water soluble polymeric binder comprising partial hydrolyzed polyvinyl alcohols, fully hydrolyzed polyvinyl alcohols, alkyl cellulose derivatives and hydroxy cellulose derivatives; from 0.2 to 1 part by weight of an organic surfactant selected from the group of a polyoxyethylene alcohol or acid derivative, and water. The pellet product of claim 6, wherein the surfactant is a polyoxyethylene oleyl ether or a polyoxyethylene stearate. The pallet product of Claim 7 , wherein the polyvinyl alcohol has a molecular weight of 10,000 or greater.

Inventors: KUO, CHARLES CHIA-CHUEN, MOLLINGER, PAUL JAMES
Applicants: THE B.F. GOODRICH COMPANY
Application year: 1985
Main classification: B01J2
IPC codes: C08J3, B01J2, C08K5, C08K9