METHOD AND APPARATUS FOR PROVIDING CENTRIFUGAL FIBRE SPINNING COUPLED WITH EXTRUSION

Abstract: A method and apparatus wherein there is provided a source (11) of fiber forming material, with said fiber forming material being pumped into a die (23) having a plurality of spinnerets about its periphery. The die (23) is rotated at a predetermined adjustable speed, whereby the liquid is ex­ pelled from the die (23) so as to form fibers (25). it is pre­ ferred that the fiber forming material be cooled as it is leav­ ing the holes in the spinnerets during drawdown. The fibres (25) may be used to produce fabrics, fibrous tow and yarn through appropriate take-up systems. The pumping system (14) provides a pumping action whereby a volumetric quan­ tity of liquid is forced into the rotational system independent of viscosity or the back pressure generated by the spinner­ ets and the manifold system of the spinning head, thus creating positive displacement feeding. Positive displace­ ment feeding may be accomplished by the extruder alone or with an additional pump of the type generally employed for this purpose. A rotary union is provided for positive sealing purposes during the pressure feeding of the fiber forming material into the rotating die (23).

Description: The invention relates generally to centrifugal fiber spinning for producing fibers from a fluid fiber-forming material. Wellknown in the art are systems in which the fluid fiber-forming material is expressed under pressure through orifices in a stationary die. The efficiency of such systems is quite low. Because of the latter fact, systems have been developed in which the fluid fiber material is expulsed through a hole arrangement in a fast rotating die by centrifugal forces. Such systems are described e. g. in EP-A1-87 014 and US-A-3,596,312. In both systems, the extrusion rate is determined by the rotational speed of the die. The volumetric pumping rate of the fluid fiber material is selected in such a way that just the amount of material is pumped into the die which is necessary to replace the material which is expulsed from the die by the centrifugal forces. The productivity of such systems is rather low. It is the object of the present invention to provide an apparatus and a method for forming fibers with high efficiency and productivity. The apparatus of the present invention comprises the following features: a source of fluid fiber-forming material; a rotatable die having a hole-arrangement in its surface; at least one conveying means interconnecting said source and said rotatable die; and a control means arranged to control the volumetric pumping rate of said conveying means in such a way that the extrusion rate through said die is solely determined by said volumetric pumping rate independent from the rotational speed of said die. In the method of the present invention, a fluid of said fiber-forming material is pressed into said rotatable die at such a predetermined volumetric pumping rate that the extrusion rate through said die is solely determined by said volumetric pumping rate independent from the rotational speed of said die. It is obvious that in the apparatus and method of the present invention, the extrusion rate is no longer determined by the centrifugal force, and with this by the rotational speed of the die, but by the volumetric pumping rate. Thereby, it is possible to receive fibers of constant quality with high productivity. The rotational speed can be selected based on other viewpoints than on the viewpoint of increasing the extrusion rate. It is preferred that the fiber-forming material be cooled as it is leaving the hole-arrangement during draw down. The fibers are well suited to produce fabrics, fibrous tow and yarn through appropriate collection and take-up systems. The invention will be further explained in conjunction with the following drawings: Fig. 1 is a schematic illustration of the fiber producing system of the present invention; Fig. 2 is a sectional view taken along lines 2-2 of Fig. 1; Fig. 3 is a sectional view taken along the lines 3-3 of Fig. 2; Fig. 4 is a sectional view taken along the lines 4-4 of Fig. 2; Fig. 5 is a graphical illustration of the relationship between extrusion rate, die rotation, filament orbit diameter and filament speed; Fig. 6 is a graphical illustration of denier as a function of die rotation; Fig. 7 illustrates a modification of Fig. 2; Fig. 8 is a schematic illustration of a system for producing a fabric; Fig. 9 is a schematic illustration of a system producing a stretched web of Fig. 8; Fig. 10 is a side view of the system of Fig. 9; and Fig. 11 is a schematic illustration of a system for producing yarn. Brief Description of the Invention The present invention relates to a method and apparatus wherein there is provided a source of liquid fiber forming material, with said liquid fiber forming material being pumped into a die having a plurality of spinnerets about its periphery. The die is rotated at a predetermined adjustable speed, whereby the liquid is expelled from the die so as to form fibers. It is preferred that the fiber forming material be cooled as it is leaving the holes of the spinnerets during drawdown. The fibers may be used to produce fabrics, fibrous tow and yarn through appropriate collection and take-up systems. The pumping system provides a pumping action whereby a volumetric quantity of liquid is forced into the rotational system independent of viscosity or the back pressure generated by the spinnerets and the manifold system of the spinning head, thus creating positive displacement feeding. Positive displacement feeding may be accomplished by the extruder alone or with an additional pump of the type generally employed for this purpose. A rotary union is provided for positive sealing purposes during the pressure feeding of the fiber forming material into the rotating die. Detailed Description of the Invention Turning now to the drawings, there is schematically shown in Fig. 1 a system according to the present invention for producing fibers. The system includes an extruder 11 which extrudes fiber forming material such as liquid polymer through feed pipe 13 to a rotary union 21. A pump 14 may be located in the feed line if the pumping action provided by the extruder is not sufficiently accurate for particular operating conditions. Electrical control 12 is provided for selecting the pumping rate of extrusion and displacement of the extrudate through feed pipe 13. Rotary union 21 is attached to spindle 19. Rotary drive shaft 15 is driven by motor 16 at a speed selected by means of control 18 and passes through spindle 19 and rotary union 21 and is coupled to die 23. Die 23 has a plurality of spinnerets about its circumference so that, as it is rotated by drive shaft 15 driven by motor 16 and, as the liquid polymer extrudate is supplied through melt flow channels in shaft 15 to die 23 under positive displacement, the polymer is expelled from the spinnerets and produces fibers 25 which form an orbit as shown. When used, air currents around the die will distort the circular pattern of the fibers. Figs. 2-4 illustrate one embodiment of the present invention. Fig. 2 is a cross-sectional view taken through spindle 19, rotary union 21, die 23 and drive shaft 15 of Fig. 1. Figs. 3 and 4 are cross sectional views taken along lines 3-3 and 4-4 of Fig. 2 respectively. Bearings 31 and 33 are maintained within the spindle by bearing retainer 34, lock nut 35 and cylinder 36. These bearings retain rotating shaft 15. Rotating shaft 15 has two melt flow channels 41 and 43. Surrounding the shaft adjacent the melt flow channels is a stationary part of rotary union 21. Extrudate feed channel 47 is connected to feed pipe 13, Fig. 1, and passes through rotary union 21 and terminates in an inner circumferential groove 49. Groove 49 mates with individual feed channels 50 and 52, Fig. 3, which interconnect groove 49 with melt flow channels 41 and 43. The rotary union may be sealed by means such as carbon seals 51 and 53 which are maintained in place by means such as carbon seal retainers 54,56. Adjacent lower carbon seal 53 is a pressure adjustable nut 55 which, by rotation, may move the two carbon seal assemblies upwardly or downwardly. This movement causes an opposite reaction from belleville washers 59 and 60 so as to spring-load each sliding carbon seal assembly individually against the rotary union. Lower washer 60 rests on spacer 61 which in turn rests on die 23. Die 23 has a plurality of replaceable spinnerets 67 which are interconnected with flow channels such as flow channel 41 by means of feed channel 69 and shaft port 71 which extends through shaft 15 between channel 41 and circumferential groove 70, Fig. 4 so as to provide a constant source of extrudate. The apparatus is secured in place by means such as plate 73 secured to shaft 15. If desired, a means for cooling the extrudate as it leaves the spinnerets may be provided, such as stationary ring 77 having outlet ports which pass air under pressure in the direction of arrows A. Ring 77 is secured in the position shown by support structure, not shown. Further, electrical heaters 20 and 22, Fig. 3, are preferably provided in stationary segment 20 of rotary union 21 so as to maintain extrudate temperature. As can be seen, the apparatus as described provides a system which is closed between the extruder and the die with the liquid extrudate being extruded through a rotary union surrounding the rotating shaft. Accordingly, as the shaft is rotated, the liquid extrudate is pumped downwardly through the melt flow channels in the rotating shaft and into the center of the circular die. The die, having a plurality of spinnerets 67, Fig. 4, about the circumference thereof, will cause a drawdown of the discharging extrudate when rotated by expelling the extrudate from the spinneret so as to form fibers 25 as schematically illustrated in Fig. 1. Die rotation therefore, is essential for drawdown and fiber formation, but it does not control extrusion rate through the die. The extrusion rate through the die is controlled by the pumping action of extruder 11 and/or pump 14. In order to provide a long lasting high pressure seal between rotary union 21 and die 23, shaft 15 includes helical grooves 101 and 103 about its circumference on opposite sides of feed channels 50 and 52. Helical grooves 101 and 103 have opposite pitch so that, as the shaft is rotated in the direction as indicated by the arrow, any extrudate leaking between the mating surfaces of shaft 15 and rotary union 21, will be driven back into groove 49 and associated channels 50 and 52. Accordingly, leakage is substantially eliminated even under high pressure through the use of this dynamic seal. The major variables involved in this system, besides the choice of polymer, are the pumping rate of the liquid polymer from the extruder and/or pump, the temperature of the polymer and the speed of rotation of the die. Of course, various size orifices may be used in the interchangeable spinnerets for controlling fiber formation without affecting extrusion rate. The rate of extrusion from the die, such as grams per minute per hole, is exclusively controlled by the amount of the extrudate being pumped into the system by the extruder and/or pump. When the system is in operation, fibers are expelled from the circumference of the die and assume a helical orbit as they begin to fall below the rotating die. While the fibers are moving at a speed dependent upon the speed of rotation of the die as they are drawn down, by the time they reach the outer diameter of the orbit, they are not moving circumferentially, but are merely being laid down in that particular orbit basically one on top of the other. The orbit may change depending upon variation of rotational speed, extrudate input, temperature, etc. External forces such as electrostatic or air pressure may be employed to deform the orbit and, therefore, deflect the fibers into different patterns. Figs. 5 and 6 are derived from the following data. DENIER VERSUS PROCESS CONDITIONS EXTRUSION RATE (g/min/hole) DIE ROTATION (r.p.m.) FIL. ORBIT DIAMETER cm ((INCHES)) FIL. SPEED M/MIN FILAMENT DENIER 1.9 500 40,6 (16) 640 27 2.0 1,000 35,6 (14) 1,120 16 2.0 1,500 33,1 (15) 1,800 10 2.1 2,000 36,8 (14.5) 2,300 8 2.1 3,000 38,1 (15) 3,600 5 3 1,000 40,5 (16) 1,300 21 3 1,500 49,5 (19.5) 2,300 12 3 2,000 52,1 (20.5) 3,300 8 3 2,500 54,6 (21.5) 4,300 6 3.8 1,000 48,3 (19.0) 1,500 23 3.8 3,000 64,5 (24.5) 5,900 6 Note : Line speed = orbit circumference x die rotation Denier is based on line speed and extrusion rate Fig. 5 illustrates the relationship of the various parameters of the system for a specific polymer (Example I below) which includes the controlling parameters, pumping rate and die rotation, and their affect on filament spinning speed and filament orbit diameter. In the graph of Fig. 5, there are illustrated three different pumping rates of extrudate, which controls the extrusion rate from the die, in grams per minute per hole. In the illustration, the number inside the symbols indicates averaged pumping rate from which the graph was developed. In Fig. 6, the graph illustrates denier as a function of die rotation. As can be seen from the graphs, as the die rotational speed is increased, the filament speed and drawdown is also increased. It is to be understood that the following examples are illustrative only and do not limit the scope of the invention. EXAMPLE - I Polypropylene resin, Hercules type PC-973, was extruded at constant, predetermined extrusion rates into and through a rotary union, passages of the rotating shaft, the manifold system of the die and the spinnerets. Except for the extruder, the apparatus is as shown in the cross-section of Fig. 2. Upon extrusion, the centrifugal energy, acting on the molten extrudate causes it to draw down into fibers. The fibers form circular orbits which are larger than the diameter of the die. A stationary circular air quench ring, located above the die, as shown in Fig. 2, including orifices designed so as to direct the air downwardly and outwardly relative to the perimeter of the die, deflects the fibers at an angle of substantially 45 degrees below the plane of the die. In this example, process parameters are varied and the resultant fibers collected for testing. 3. Data and Results Extrusion Rate (g/min/hole) Die Rotation (r.p.m.) Fiber Orbit Diameter cm ((inches)) Fiber Spinning Speed (meter/min) Fiber Denier (g/9000m) 1.9 500 40,6 (16) 640 27 2.0 1,000 35,6 (14) 1,120 16 2.0 1,500 38,1 (15) 1,800 10 2.1 2,000 36,8 (14.5) 2,300 8 2.1 3,000 38,1 (15) 3,600 5 3.0 1,000 40,5 (16) 1,300 21 3.0 1,500 49,5 (19.5) 2,300 12 3.0 2,000 52,1 (20.5) 3,300 8 3.0 2,500 54,6 (21.5) 4,300 6 3.8 1,000 48,3 (19) 1,500 23 3.8 3,000 64,5 (24.5) 5,900 6 4. Extrusion Conditions Note: (a) Fiber orbit diamter was measured visually with an inch-ruler. (b) Fiber spinning speed was calculated ( speed=orbit circum ference x rotation ). (c) Denier was calculated, based on extrusion rate and fiber spinning speed in the well known manner. According to the results or this experiment, the fibers become smaller with increasing die rotation, Furthermore, increasing extrusion rate, at a given die rotation, increases filament orbit and, therefore, decreases the rate of increase of filament denier. EXAMPLE II In the apparatus described in Example I, a polyethylene methacrylic copolymer (DuPont Ionomer resin type Surlyn - 1601) was extruded. Fibers of various deniers were produced at different die rotations. In another variation of this example, fibers were collected on the surface of a moving screen. The screen was moved horizontally, four inches below the plane of the die. Upon contact of the fibers with each other, the fibers were bonded to each other at the point of contact. The resultant product is a nonwoven fabric. The fabric was then placed between a sheet of polyurethane foam and a polyester fabric. Heat and pressure was then applied through the polyester fabric. The lower melting ionomer fabric was caused to melt and bond the two substrates into a composite fabric. Example III In the apparatus of Example I, the following polymers which are listed in the table below, have been converted into fibers and fabrics. Polymers Converted into Fibers and Fabrics Polymer Extrusion Temp. °C (°F) Die Temp. °C (°F) Polypropylene Amoco CR-34 204-260 (400 - 500) 288-329 (550 - 625) Polyioner Surlyn 1601 177-204 (350 - 400) 232-288 (450 - 550) Nylon terpolymer Henkel 6309 138-149 (280 - 300) 177-204 (350 - 400) Polyurethane Estane 58122 177-204 (350 - 400) 232-204 (450 - 400) Polypropyleneethylene copolymer 204-260 (400 - 500) 288-316 (550 - 600) Spunbonded fabrics are produced by allowing the freshly formed fibers to contact each other while depositing on a hard surface. The fibers adhere to each other at their contact points thus forming a continuous fabric. The fabric will conform to the shape of the collection surface. In this example, fibers were deposited on the surface of a solid mandrel comprising an inverted bucket. The dimensions of this mandrel are as follows. Bottom diameter, inches: 7.0 Top diameter, cm (inches): 20,95 (8.25) Height of mandrel, cm (inches): 17,8 (7.0) Example IV Nylon-6 polymer, 2.6-relative viscosity (measured in sulfuric acid), was converted into low-denier textile fibers and spun-bonded continuously into a nonwoven fabric. The fabric was formed according to the apparatus of Fig. 8. The extrusion head employed is illustrated in the cross section of Fig. 7. The fabric produced in this system is very uniform and even, with good balance in physical properties. The hole diameter of the spinneret is preferably between 0,02 and 0,076 cm (.008 and .030 inches) with the length-to-diameter ratio being between 1:1 and 7:1. This ratio relates to desired pressure drop in the spinneret. Shaped, tubular articles were formed by collecting fibers on the outside surface of a mandrel. The mandrel used in this experiment was a cone-shaped, inverted bucket. The mandrel was placed concentric with, and below a revolving, 6-inch diameter die. The centrifugal action of the die and the conveying action of the air quench system caused fibers to be deposited on the surface of the mandrel (bucket), thus forming a shaped textile article. The resultant product resembles a tubular filter element and a textile cap. In another experiment, a flat plate was placed below the rotating die. The flat plate was slowly withdrawn in a continuous motion thereby producing a continuous, flat fabric. The air quench with its individual air streams causes fiber deflection and fiber entanglement, thereby producing an interwoven fabric with increased integrity. Copolymer and Polymer Blends Virtually every polymer, copolymer and polymer blend which can be converted into fibers by conventional processing can also be converted into fibers by centrifugal spinning. Examples of polymer systems are given below: Polyolefin polymers and copolymers; Thermoplastic polyurethane polymers and copolymers; Polyesters, such as polyethylene and polybutylene terephthalate; Nylons; Polyionomers; Polyacrylates; Polybutadienes and copolymers; Hot melt adhesive polymer systems; Reactive polymers. Example V In the apparatus of Example IV, thermoplastic polyurethane polymer, Estane 58409 was extruded into fibers, collected on an annular plate and withdrawn continuously as a bonded non-woven fabric. Very fine textile fibers were produced at high die rotation without evidence of polymer degradation. Process conditions Extrusion Temperatures, °C (°F) Z-1: 127 (260) Z-2: 166 (330) Z-3: 177 (350) Adapter 177 (350) Melt tube 125 (250) Die (7 amps) 232-260 (450-500) Quench air pressure kg/m² (psi) 14x10³ (20) Die rotation, r.p.m. 2,000.00 Extruder-Screw rotation, r.p.m. 12.0 Process Parameters Controlling Fiber Production As will be evident from the above illustrations, three major criteria govern the control of fiber formation from thermoplastic polymers with the present system: 1. Spinneret hole design and dimension will affect the process and fiber properties as follows: a. control drawdown for a given denier b. govern extrudate quality (melt fracture) c. affect the pressure drop across the spinnerets d. fiber quality and strength and fiber processability (in-line stretching and post-stretching propensity) e. process stability (line speed potential, productivity, stretch, etc.). 2. Extrustion rate, which is governed by pumping rate of the extruder and/or additional pumping means, will affect a. fiber denier b. productivity c. process stability 3. Die rotation, which controls filament spinning speed influences and controls a. drawdown b. spinline stability c. denier d. productivity for a given denier It should be noted that temperature controls process stability for the particular polymer used. The temperature must be sufficiently high so as to enable drawdown, but not so high as to allow excessive thermal degradation of the polymer. In the conventional non-centrifugal fiber extrusion process and in the centrifugal process of this invention, all three variables are independently controllable. However, in the known centrifugal process discussed above these variables are interdependent. Some of this interdependency is illustrated below. 1. Spinneret hole design will affect extrusion rate since it determines part of the backpressure of the system. 2. Extrusion rate is affected by die rotation, the pressure drop across the manifold system, the spinneret size, polymer molecular weight, extrusion temperature, etc. 3. Filament speed will depend on the denier desired and all of the beforementoned conditions, especially die rotation and speed. Thus, it can be seen that the system of the present invention provides controls whereby various deniers can be attained simply by varying die rotation and/or changing the pumping rate. It will be apparent from the above disclosure that since the extrudate is being pumped into the system at a controlled rate, the total weight of the extruded fibers can be increased by increasing the amount of extrudate being pumped into the system. Additionally, the consistency and control of fiber production is much greater than that for fibers which are extruded depending solely upon centifugal force to drive the extrudate through the holes in the wall of a cup as described in the patents cited hereinabove. The fibers may be used by themselves or they may be collected for various purposes as will be discussed hereinafter. Fig. 7 discloses a modified system similar to Fig. 1 wherein the central shaft remains stationary and the die is driven by external means so that it rotates about the shaft. The actual driving motor is not shown although the driving mechanism is clearly illustrated. Non-rotatable shaft 101 includes extrudate melt flow channel 105 therethrough which interconnects with feed pipe 13 of Fig. 1. There is also provided a utility channels 102 and 104 which may be used for maintaining electrical heating elements (not shown). Shaft 101 is supported and aligned at its upper end by support plate 107 and is secured thereto by bolt 106 and extends downwardly therefrom. Cylindrical inner member 111 is secured and aligned to plate 107 by means such as bolt 112. At its lower end, inner member 111 has secured thereto a flat annular retainer plate 114 by means of a further bolt. Plate 114 supports outer member 115 of the spindle assembly and has bearings 121 and 123 associated therewith. Onto the lower end of outer member 115 is bolted an annular plate 150 by means of bolts such as 151. A thin-walled tube 152 is welded on the inside wall of member 150. The three interconnected members 152, 150, and 115 form an annular vessel containing bearings 121 and 123 and oil for lubrication. The entire vessel is rotated by drive pulley 116 which is driven by belt 116 and is secured to outer member 115 by means such as bolt 118. The rotating assembly is connected to die 141 by means of adapter 120 and rotates therewith. Bushing 125 surrounds shaft 101 and supports graphite seals 129a and 129b and springs 130 and 131 on either side thereof. Sleeves 126 and 128 are secured to the die by screws 153 and 154 and rotate with die 141. The inside surfaces of the sleeves include integral grooves 137 and 139 which extend above and below melt flow channel 143 so as to drive any liquid extrudate leaking along the sleeves towards channel 143 in the same manner as is described in connection with the grooves on the rotating shaft of Fig. 2. The die 141 is bolted onto the adapter 120 via bolts such as bolt 155. Each melt flow channel, such as 143, contains replaceable spinneret 145 with melt spinning hole 156. Melt flow channel 143 terminate at their inner ends with melt flow channel 105. The die is heated with two ring heaters 157 and 158 which are electrically connected to a pair of slip rings 159 and 160 by means not shown. Power is introduced through brushes 161 and 162 and regulated by a variable voltage controller (not shown). Fig. 8 is a schematic illustration of an assembly using the present invention to form fabrics. Unistrut legs 201, support base frame 203 which in turn supports extruder 205. Extruder 205 feeds into adapter 207 and passes downwardly to die 215. Motor 209 drives belt 211 which in turn rotates the assembly as described in Fig. 7. Stationary quench ring 213 of the type shown in Fig. 2 surrounds the die as previously discussed so as to provide an air quench for the fibers as they are extruded. A web forming plate 219 is supported beneath the base support frame and includes a central aperture 221 which is of a larger diameter than the outside diameter of the rotating die. As the die is rotated and the fibers are extruded, they pass beyond aperture 221 and strike plate 219. Fibers are bonded during contact with each other and plate 219, thus producing non-woven fabric 225 which is then drawn back through aperture 221 as tubular fabric 225. Stationary spreader 220 supported below the die, spreads the fabric into a flat two-ply composite which is collected by pull roll and winder 227. Thus, the fabric which is formed as a result of the illustrated operation may be collected in a continuous manner. Figs. 9 and 10 are schematic representations of a plan and side view of a web forming system using the present invention. The frame structure and extruder and motor drive are the same as described in connection with Fig. 8. The die is substantially the same as in Fig. 8 and includes therewith the quench ring 213. In the web forming system, mandrel 235 is added below and substantially adjacent die 215. As can be seen, mandrel 235 is substantially domed shaped with a cut out portion to accommodate continuous belts 237 and 239 which constitute a spreader. As the fibers leave die 215 in an orbit fashion, they drop downwardly onto the mandrel and are picked up and spread by continuous belts 237 and 239. Nip roll 243 is located below belts 237 and 239 and draws web 241 downwardly as it passes over the spreader, thus creating a layered web. Layered web 249 then passes over pull roll 245 and 247 and may be stored on a roll (not shown) in a standard fashion. Fig. 11 is a schematic of a yarn and tow forming system using the present invention. Frame 300 supports extruder 301, drive motor 302 and extrusion head 303 in a manner similar to that discussed in connection with Fig. 8. Radial air aspirator 304 is located around die 305 and is connected to air blower 306. Both are attached to frame 300. In operation, fibers are thrown from the die by centrifugal action into the channel provided by aspirator 304. The air drag created by the high velocity air causes the fibers to be drawn-down from the rotating die and also to be stretched. The fibers are then discharged into perforated funnel 308 by being blown out of aspirator 304. The fibers are then caused to converge into a tow 309 while being pulled through the funnel by nip rolls 310. Tow 309 may then be stuffed by nip rolls 311 into crimper 312 and crimped inside of stuffing box 313, producing crimped tow 314. The crimped tow is then conveyed over rolls 315 and continuously packaged on winder 316.

Claims: An apparatus for forming fibers comprising: a source (11) of fluid fiber-forming material; a rotatable die (23, 141, 215, 305) having a hole-arrangement (67, 145) in its surface; at least one conveying means (11, 13, 14, 47, 41, 69, 105, 143) interconnecting said source and said rotatable die; and a control means (12, 18) for controlling the pumping rat of said conveying means and the rotational speed of said die, characterized in that said control means (12, 18) is arranged to control the volumetric pumping rate of said conveying means in such a way that the extrusion rate through said die is governed by said pumping rate. The apparatus of claim 1, characterized by a control means (12) for controlling the pumping rate with which said fluid fiber material is pressed into a channel (13, 47, 41, 63; 105, 143). The apparatus of one of the claims 1 or 2, characterized in that said conveying means is an extruder (11). The apparatus of one of the claims 1 or 2, characterized in that said conveying means is a pump (14) arranged between an extruder (11) and said channel. The apparatus of one of the claims 1 - 4, characterized by means for controlling the temperature of said fluid fiber material within said channel. The apparatus according to one of the claims 1 - 5, characterized by cooling means (77, 304) for cooling said fibers after they are expulsed from said hole-arrangement (67). The apparatus of claim 6, characterized in that said cooling means is a stationary perforated ring (77) substantially surrounding said die (23). The apparatus of claim 6, characterized in that said cooling means is a radial air aspirator (304) located around said die (305) for creating an air drag by high velocity air for cooling and stretching the fibers expulsed from said hole-arrangement (67, 145). The apparatus of one of the claims 1 - 8, characterized in that said hole-arrangement comprises at least one spinneret (67, 145). The apparatus of one of the claims 1 - 9, characterized by means for forming a fabric from said fibers (Fig. 9 and 10). The apparatus of one of the claims 1 - 9, characterized by means for forming a yarn from said fibers (Fig. 11). A method for forming fibers, in which method a fluid fiber-forming material is conveyed into a rotatable die and fibers are expulsed from a hole-arrangement in said die, characterized in that said fiber-forming material is pressed into said rotatable die at such a predetermined volumetric pumping rate that the extrusion rate through said die is governed by said pumping rate. The method of claim 12, characterized in that the fluid fiber material is pressed with a controlled pumping rate.

Inventors: KEUCHEL, HERBERT W.
Applicants: BENOIT, JOHN E., KEUCHEL, HERBERT W.
Application year: 1985
Main classification: D01D5
IPC codes: D01F6, D01D5, D04H3