PERINONE COMPOUND

Abstract: A perinone compound represented by the formula wherein R represents arylene; R and R′, which may be the same or different, each represents alkoxyalkyl, hydroxyalkyl, a N,N-dialkylaminoalkyl, cycloalkyl or aralkyl; and X repre­ sents oxygen or sulfur. Preparation methods are by reaction of a compound having the essential structure with either X=C-NHRNHR′ to replace 2 halogen atoms, or with a carbonylating or thiocar­ bonylating agent, in an inert solvent. The compounds fluoresce yellowish green to orange in color and are useful for dyeing fibers, textiles, synthetic plastics molding and films.

Description: This invention relates to a novel perinone compound. More particularly, it relates to a perinone compound which has a fluorescent color of from a yellowish green to orange color and can be utilized as a fluorescent dye or dyestuff. In recent years, the utilizing of dyes or dyestuffs having intense fluorescent property has been repidly broadened. For example, fluorescent dyes or dyestuffs have shown more variety in application, such as not only in dyeing or printing various synthetic fiber materials, dope coloring of various synthetic resins, melt spinning-dyeing, as fluorescent pigments in fluorescent dyes or inks, etc. but also in colored laser beams, solar batteries as a convergent system, display devices, and the like. The present inventors have previously found that the following compounds A and B are fluorescent dyes having excellent fastness to light However, these compounds involve a problem in practical use from the standpoint of affinity for organic substrates. In particular when they are used as disperse dyes for dyeing polyester cloth, they were of low practical use due to their poor build-up property and temperature dependence. Further, when they are used as fluorescent pigments in combination with resin components, such as toluenesulfonamide, formaldehyde, melamine, etc., the compatibility with these resin components is poor, resulting in low fluorescent intensity and fastness to light when spread on a paper substrate. Accordingly, an object of this invention is to provide a highly practical perinone compound having good affinity for various organic substrates. More particularly, an object of this invention is to provide a perinone compound having satisfactory build-up property and temperature dependence when used as a dye and having excellent fluorescent property and fastness to light when used as a fluorescent pigment. The perinone compound according to the present invention is a compound represented by the formula (I) wherein A represents substituted or unsubstituted arylene; R and R', which may be the same or different, each represents alkoxyalkyl, hydroxyalkyl, N, N-dialkylaminoalkyl, cycloalkyl or aralkyl; and X represents oxygen or sulfur. In the above-described formula (I), examples of arylene represented by A include o-phenylene, naphthylene, etc. which may be substituted with, for example, alkyl, alkoxy, alkoxyalkyl, nitro, halogen, etc. Of those, o-phenylene is preferred. Alkoxyalkyl represented by R and R' contains from 1 to 10, and preferably from 1 to 4, carbon atoms in its alkoxy moiety and contains from 1 to 10, and preferably from 1 to 4, carbon atoms in its alkyl moiety. Examples thereof include methoxyethyl, ethoxyethyl, butoxyethyl, methoxypropyl, ethoxypropyl, n-propoxypropyl, isopropoxypropyl, butoxypropyl, 2-ethylhexyloxypropyl. Hydroxyalkyl represented by R and R' contains from 1 to 4 carbon atoms and examples thereof include hydroxyethyl, hydroxypropyl, hydroxybutyl. Example of N,N-dialkylaminoalkyl represented by R and R' include N,N-dimethylaminoethyl, N,N-dimethylaminopropyl, N,N-diethylaminoethyl, N,N-diethylaminopropyl. Examples of cycloalkyl represented by R and R' include cyclohexyl, Examples of aralkyl represented by R and R' include benzyl, phenethyl, The compounds of the formula (I) wherein R and R' each represents alkoxyalkyl are particularly preferred as dyes. In the formula (I), X represents oxygen or sulfur, and oxygen is preferred. The perinone compound represented by the formula (I) according to the present invention can be prepared by the following processes A and B: Process A comprises reacting a compound represented by the formula (II) wherein A is the same as defined above; and Y represents halogen, with a compound represented by the formula (III) wherein R, R' and X are as defined above, in the presence of an inert solvent, such as nitrobenzene or, nitrotoluene, by heating to thereby form a perimidone ring or a thioperimidone ring. Process B comprises reacting a compound represented by the formula (IV) wherein A, R and R' are the same as defined above, with a carbonylating agent or thiocarbonylating agent in the presence of an organic solvent, such as chlorobenzene, to thereby form a perimidone ring or a thioperimidone ring. The perinone compounds (I) according to the present invention exhibit excellent properties as fluorescent dyes or dyestuffs. Fibers which can be dyed with the compounds of the present invention include polyester fibers composed of polyethylene terephthalate, a polycondensate between terephthalic acid and 1,4-bis (hydroxymethyl) cyclohexane, or the like; and blended fabric goods or blended textiles goods (e.g., cloth, textile, fabric, etc.) composed of the above-described polyester fibers and natural fibers, such as cotton, silk or wool, In carrying out dyeing using the compounds of present invention, the compound of the formula (I) is dispersed in an aqueous dispersing medium using a dispersing agent in conventional manner to prepare a dye bath or a printing paste, and dip dyeing or printing is then conducted using the same. In the case of dip dyeing, polyester fibers, or blended fabric goods or blended textile goods thereof can be dyed to have excellent fastness by applying conventional dyeing methods, such as high temperature dyeing, carrier dyeing, thermosol dyeing, and the like. In some cases, further improved results can be attained by adding an acidic substance to a dye bath. Polyester fibers or mixed yarns thereof dyed with the compounds of the present invention by the above-described methods show an extremely clear hue with brilliance by the synergistic effect of the fluorescent color (yellowish green to orange) of the dye with the reflective color of the dyed articles. Further, the dyed articles have superior fastness to light. Moreover, the compounds according to the present invention have extremely excellent build-up property and temperature dependence during dyeing. The compounds according to the present invention can also be applied to coloring of various organic polymeric materials including fibers. The coloring can be carried out at any optional stage of from the production of the material to be colored through the processing thereof. For example, the coloring can be effected by the so-called dope-dyeing method in which the fluorescent dyestuff of the formula (I) is added to a spinning dope before spinning in the manufacture of fibers. Further, in the case of coloring thin films or plates, good results can also be obtained by a method in which the fluorescent dyestuff is incorporated into a molding material before or during the molding process. Examples of the synthetic resin molded articles by these coloring methods include polystyrene resins, acrylic resins, polycarbonate resins, ABS resins, polyethylene resins, etc. Those coloring methods can also be applied to polyethylene, polyvinyl chloride, etc. The compounds of the present invention can further be employed as dyestuffs for fluorescent coating films. Coating films having excellent fluorescent property and fastness to light can be produced by mixing the compound of the present invention with resin components, such as toluenesulfonamide, formamide, melamine, etc., diluting the mixture with an acrylic varnish, etc., and coating the resulting varnish on a substrate, such as paper, metal plates, etc. Furthermore, the compounds of the present invention can effectively be used as dyestuffs for fluorescent synthetic resin plates or films of a convergent system for solar batteries because of their high fastness to light, and as dyestuffs for fluorescence-activated display elements. In addition, the compounds of the present invention are suitable as laser dyes in a wavelength region of from 450 to 560 nm for dye laser apparatuses which are given pulse by a N₂ laser The present invention will now be illustrated in greater detail by reference to the following examples and comparative examples. EXAMPLE 1 0.5 g of a perinone compound of the formula was dispersed in 3 liters of water containing 1.0 g of a naphthalenesulfonic acid-formaldehyde condensate and 2.0 g of a higher alcohol sulfuric acid ester to prepare a dye bath. 100 g of polyester cloth was dipped in the dye bath and dyed at 130°C for 60 minutes, followed by soaping, washing with water, and drying, to obtain a polyester cloth dyed in fluorescent greenish yellow and having excellent fastness to light,fastness to sublimation and wet color fastness. The above-described perinone compound was determined for temperature dependence and build-up property in accordance with the methods described below. The results obtained are shown in Table 1. Temperature Dependence : Dip dyeing was carried out under the dyeing conditions of 120°C x 60 minutes and 130°C x 60 minutes according to the same process as described in Example 1, and the ratio of the amount of the dye of the dyed cloth (120°C/130°C) was determined. The amount of the dye was measured by solvent extraction of the dyed cloth with dimethylformamide. Build-Up Property : Dip dyeing was carried out in the same manner as described in Example 1 but using 1.0 g (1 owf) or 0.5 g (0.5 owf) of the dye cake, and the degree of exhaustion of the dye (the amount of dye exhausted/the amount of dye used x 100) was determined. The perinone compound used in this example was prepared as follows. 20 g of a perinone compound of the formula was reacted with 45.6 g of N,N-diethylaminoaniline and 30 g of ethyl chloroformate in chlorobenzene at 130°C for 1.5 hours. After cooling, the reaction mixture was filtered, and the solid was washed successively with methanol and water to obtain 13.6 g of yellow crystals. The maximum absorption wavelength (λ max ) (in acetone) of the dye was 450 nm. EXAMPLE 2 0.5 g of a dye of the formula was mixed with 0.5 g of a naphthalenesulfonic acid-formaldehyde condensate, and the mixture was finely pulverized in a paint shaker to obtain a powdery dye. The resulting powdery dye was thoroughly blended with a stock paste having the following composition to prepare a color paste. The resulting color paste was printed on a polyester cloth, intermediately dried at 100°C, held in superheated steam at 170°C for 7 minutes to develop a color, followed by soaping, washing with water and drying, to obtain a cloth dyed in fluorescent yellow and having excellent fastness to light,fastness to sublimation and wet color fastness. The λ max (in acetone) of the dye was 450 nm. The above-described perinone compound was examined for temperature dependence and build-up property in the same manner as in Example 1. The results obtained are shown in Table 1. COMPARATIVE EXAMPLES 1 AND 2 Conventional dyes having the similar structure to the compounds of the present invention as shown in Table 1 were tested for temperature dependence and build-up property in the same manner as in Example 1. The results obtained are shown in Table 1 below. EXAMPLE 3 Polyester cloth was dyed in the same manner as described in Example 1 but using compounds shown in Table 2 below (Compound Nos. 1 to 35). The λ max of the compounds, color tone of the dyed cloth, temperature dependence and build-up property of the dyes were determined in the same manner as in Example 1. The results obtained are shown in Table 2. EXAMPLE 4 With 1,000 parts by weight of polystyrene pellets was blended 0.2 part by weight of the same perinone dyestuff as used in Example 1, and the blend was kneaded at 200 to 240°C and then injection-molded to produce a colored plate having a thickness of 2 mm. During these operations, thermal decomposition of the dyestuff, discoloration or a like phenonemon was not at all observed. The dye exhibited satisfactory dispersibility in and compatibility with the polystyrene. The resulting polystyrene plate was uniformly colored and had an extremely clear fluorescent greenish yellow color. when the colored plate was exposed to light for 100 hours using a fadeometer, neither reduction in fluorescence nor change in color was observed. EXAMPLES 5 TO 7 AND COMPARATIVE EXAMPLES 3 TO 4 18 g of a o- and p-mixed toluenesulfoneamide-formamide resin was heat-melted at 70°C, and 20 g of melamine was added thereto at 130°C. Ten minutes later, 14.3 g of p-formaldehyde was added thereto. After the temperature was further elevated to 170°C, 0.5 g of a perinone compound shown in Table 3 below was added thereto, followed by stirring for 15 minutes. Then, the mixture was cooled, and the thus solidified fluorescent yellow pigment was finely pulverized. The powdering pigment was thoroughly mixed with 1.5 times the amount of a cold-setting acrylic varnish, and the resulting varnish was spread on art paper using a 8 mil applicator. The resulting coated paper had an extremely clear fluorescent yellow color. The color developability of the pigment was evaluated by determining the reflectance at the maximum reflectance wavelength (λ max ) by means of a Macbeth photometer (MS-2020). Further, the coated paper was exposed to light for 300 hours using a fadeometer, and the fastness to light was evaluated by a gray scale. The results obtained are shown in Table 3 below.

Claims: A perinone compound represented by the formula wherein A represents substituted or unsubstituted arylene; R and R', which may be the same or different, each represents alkoxyalkyl, hydroxyalkyl, N,N-dialkylaminoalkyl, cycloalkyl or aralkyl; and X represents oxygen or sulfur. A perinone compound as in Claim 1, wherein A is o-phenylene. A perinone compound as in Claim 1 or 2, wherein R and R' each is alkoxyalkyl. A perinone compound as in Claim 3, wherein R and R' each is alkoxyalkyl containing from 1 to 4 carbon atoms in its alkoxy moiety and from 1 to 4 carbon atoms in its alkyl moiety. A perinone compound as in any of Claims 1 to 4 wherein X is oxygen. Fibers, films, plates or other shaped products dyed with a compound as claimed in any preceding claim.

Inventors: HIMENO, KIYOSHI, NIWA, TOSHIO, YOSHIHARA, JUNJI
Applicants: MITSUBISHI KASEI CORPORATION
Application year: 1985
Main classification: C09B57
IPC codes: C07D471, C09B57