DISPERSANT CONTAINING COMPOSITION

Abstract: A composition comprising a finely-divided non-magnetic solid and a dispersant comprising a poly(C₂ ₄-­ alkyleneinmine) carrying at least two mono- or poly­ (carbonyl-C₁₋₇-alkyleneoxy) groups, a dispersion of the composition in an organic medium and a dispersant com­ prising a poly(C₂₋₄-alkyleneimine) carrying at least two carbonyl-C₁₋₇-alkyleneoxy groups.

Description: This specification describes an invention relating to a novel dispersible composition of finely divided non-magnetic solid and a dispersant and to a dispersion of the composition in an organic medium. The Composition According to the present invention there is provided a composition comprising a finely-divided non-magnetic solid and a dispersant comprising a poly(C₂₋₄-alkyleneimine) carrying at least two mono- or poly-(carbonyl-C₁₋₇-alkyleneoxy) groups. The composition may comprise an intimate mixture of the two components but preferably comprises a coating of the surfactant on finely divided primary particles of the solid which preferably have a mean diameter below 10 microns and more preferably below 5 microns. The composition may be dry, in which case the primary particles of the solid may be aggregated, or it may be in the form of a dispersion of the solid in an organic medium, preferably one which is a liquid, or is at least plastic, under ambient or processing conditions. The composition preferably contains from 1% to 100%, and more preferably from 1% to 30%, by weight of the dispersant, based on the weight of the solid. In the dispersion form, the composition preferably contains from 5% to 95% by weight of the solid, the precise quantity depending on the nature of the solid and the relative densities of the solid and liquid. For example, a dispersion in which the solid is an organic material, such as an organic pigment, preferably contains from 15% to 60% by weight of the solid, whereas a dispersion in which the solid is an inorganic material, such as an inorganic pigment, filler or extender, preferably contains from 40% to 90% of the solid, based on the total weight of the composition. The composition may be prepared by mixing the components or the dispersant may be added to the solid during the preparation of the latter, preferably during the later or finishing stages of preparation. The composition may also be prepared by subjecting a mixture of the solid, the surfactant, preferably in the organic medium, to a grinding operation sufficient to reduce the particle size of the solid to below 10 microns. Where the organic medium is a volatile liquid this may be subsequently removed by evaporation, if the composition is required in a dry form. Where the organic medium is a solid or plastic material at ambient temperatures, e.g. a polar resin, the mixing of the components and subsequent grinding operation may be carried out at an elevated temperature so that the organic medium and the composition is in a fluid or plastic, form. The composition, whether dry or in the form of a dispersion, may contain other ingredients, such as resins (where these do not already constitute the organic medium), binders, fluidising agents, anti-sedimentation agents, plasticisers, levelling agents and preservatives. The present composition is compatible with the fluidising agents disclosed in GB-A-1508576 and 2108143. The fluidising agent described in GB-A-1508576 is a substituted ammonium salt of a coloured acid wherein there are from 19 to 60 carbon atoms in at least 3 chains attached to the N atom of the substituted ammonium ion. The fluidising agent described in GB-A-2108143 is a water-insoluble disazo compound comprising a central divalent group free from acidic and other ionic substituents linked, through azo groups, to two monovalent end groups, one end group being free from acidic and other ionic substituents and the other carrying a single substituted ammonium salt group. Such fluidising agents are useful for enhancing the fluidity of the dispersion form of the present compositions and especially where the organic medium is an ester, a ketone or an aromatic solvent, such as xylene or chlorobenzene. The composition is particularly suitable for use in paints, especially high solids paints, inks, especially flexographic, gravure and screen inks, and non-aqueous ceramic processes, especially tape-coating, doctor-blade, extrusion and injection moulding type processes. Paint systems in which the composition is particularly suitable include those based on alkyd resins, particularly medium-and short-oil alkyd resins, oil-free polyester resins, polyol resins, urethane resins and acrylic resins. Particularly suitable hardeners or crosslinkers include melamine-formaldehyde resins, particularly butylated melamine- formaldehyde and hexamethoxymethyl-melamine resins, urea- formaldehyde resins, urethanes and isocyanates. Gravure inks in which the composition is particularly suitable include gravure inks of types C, D and E as classified by the Gravure Technical Association of New York. The Solid The solid may be any non-magnetic material, especially a material which it is desired to stabilise in a finely divided state in an organic medium. Examples of suitable solids are pigments for solvent inks; pigments, extenders and fillers for paints and plastics materials; dyes, especially disperse dyes; optical brightening agents and textile auxiliaries for solvent dyebaths, inks and other solvent application systems; solids for oil-based and invert-emulsion drilling muds; dirt and soil particles in dry cleaning fluids; particulate ceramic materials; and biocides, agrochemicals and pharmaceuticals which are applied as dispersions in organic media. A preferred solid is a pigment from any of the recognised classes of pigments described, for example, in the Third Edition of the Colours Index (1971) and subsequent revisions of, and supplements thereto, under the chapter headed "Pigments". Examples of inorganic pigments are titanium dioxide, zinc oxide, Prussian blue, cadmium sulphide, iron oxides, vermillion, ultramarine and the chrome pigments, including chromates, molybdates and mixed chromates and sulphates of lead, zinc, barium, calcium, and mixtures and modifications thereof which are commercially available as greenish-yellow to red pigments under the names primrose, lemon, middle, orange, scarlet and red chromes. Examples of organic pigments are those from the azo, disazo, condensed azo, thioindigo, indanthrone, isoindanthrone, anthanthrone, anthraquinone, isodibenzanthrone, triphendioxazine, quinacridone and phthalocyanine series, especially copper phthalocyanine and its nuclear halogenated derivatives, and also lakes of acid, basic and mordant dyes. Carbon black, although strictly inorganic, behaves more like an organic pigment in its dispersing properties. Preferred organic pigments are phthalocyanines, especially copper phthalocyanines, monoazos, disazos, indanthrones, anthranthrones, quinacridones and carbon blacks. Examples of extenders and fillers are talc, kaolin, silica, barytes and chalk. Examples of suitable particulate ceramic materials are alumina, silica, zirconia, titania, silicon nitride, boron nitride, silicon carbide, boron carbide, mixed silicon-aluminium nitrides and metal titanates Examples of agrochemicals include the fungicides flutriafen, carbendazim, chlorothalonil and mancozeb. The Organic Medium Where the composition of the present invention is in the form of a dispersion, the organic medium is preferably a polar organic medium or a substantially non-polar aromatic hydrocarbon or halogenated hydrocarbon. By the term "polar" in relation to the organic medium is meant an organic liquid or resin capable of forming moderate to strong bonds as described in the article entitled "A Three Dimensional Approach to Solubility" by Crowley et al in Journal of Paint Technology, Vol.38, 1966, at page 269. Such organic media generally have a hydrogen bonding number of 5 or more as defined in the above-mentioned article. Examples of suitable polar organic liquids are amines, ethers, especially lower alkyl ethers, organic acids, esters, ketones, glycols, alcohols and amides. Numerous specific examples of such moderately and strongly hydrogen bonding liquids are given in the book entitled "Compatibility and Solubility" by Ibert Mellan (published in 1968 by Noyes Development Corporation) in Table 2.14 on pages 39 and 40 and these liquids all fall within the scope of the term polar organic liquid as used in this specification. Preferred polar organic liquids are dialkyl ketones, alkyl esters of alkane carboxylic acids and alkanols, especially such liquids containing up to, and including, a total of 6 carbon atoms. As examples of the preferred and especially preferred liquids there may be mentioned dialkyl and cycloalkyl ketones, such as acetone, methyl-ethyl-ketone, di-ethylketone, di-iso-propylketone, methyl-iso-butyl-ketone, di-iso-butylketone, methyl-iso-amyl-ketone, methyl-n-amyl-ketone and cyclohexanone; alkyl esters such as methyl acetate, ethyl acetate, isopropyl acetate, butyl acetate, ethyl formate, methyl propionate and ethyl butyrate, glycols and glycol esters and ethers, such as ethylene glycol, 2-ethoxyethanol, 3-methoxypropylpropanol, 3-ethoxypropylpropanol, 2-butoxyethyl acetate, 3-methoxypropyl acetate, 3-ethoxypropyl acetate and 2-ethoxyethyl acetate, alkanols such as methanol, ethanol, n -propanol, isopropanol, n -butanol and isobutanol and dialkyl and cyclic ethers such as diethylether and tetrahydrofuran. The substantially non-polar, organic liquids which may be used, either alone or in admixture with the aforementioned polar solvents, are aromatic hydrocarbons, such as toluene and xylene, and halogenated aliphatic and aromatic hydrocarbons, such as trichloroethylene, perchloroethylene and chlorobenzene. However, aliphatic hydrocarbons, such as petroleum fractions and white spirit are preferably only employed in admixture with the above-mentioned polar solvents and the proportion of an aliphatic hydrocarbon should preferably not exceed a level which reduces the ability of the mixture to completely dissolve the resins which may form a part of the dispersion because the are required in end use formulations, such as inks, paints and ceramic moulding compositions. Examples of suitable polar resins, as the medium for the dispersion form of the present invention, are film-forming resins such as are suitable for the preparation of inks, paints and chips for use in various applications such as paints and inks. Specific examples of such polar resins are polyesters, such as polyethylene terephthalate, nitrocellulose, cellulose acetate and propionate and polacrylates, polyamides, such as Versamid (Trade Mark) and Wolfamid (Trade Mark), and celluolose ethers, such as ethyl-cellulose and ethyl-hydroxyethyl-cellulose. The Dispersant Each alkylene group in the carbonyl-C₁₋₇-alkyleneoxy group (hereinafter referred to as the "CAO group") or the poly(carbonyl-C₁₋₇-alkyleneoxy) group (hereinafter referred to as the "PCAO chain") preferably contains from 3 to 6 carbon atoms, an especially preferred alkylene group being pentamethylene wherein the CAO group is 5-oxypentamethylene-1-carbonyl (hereinafter referred to as "OPMC") which is derivable from E-caprolactone. The PCAO chain may contain a mixture of alkylene groups of different length but is preferably a homopolymer, especially of OPMC. The PCAO chain or the CAO group may carry a chain-stopping terminal group at the free end, such as optionally substituted alkyl, e.g. alkyl, alkoxyalkyl or haloalkyl, where the absence of a terminal hydroxy group prevents formation or further growth of the PCAO chain. The PCAO chain preferably contains from 2 to 100, and more preferably from 3 to 80, CAO groups. The CAO group and PCAO chain can be conveniently represented by the general formula: wherein T is H or a terminal chain stopping group; V is a C₁₋₇-alkylene group; and n is a number from 1 to 100. When n = 1 Formula I represents a CAO group and when n > 1 Formula I represents a PCAO chain. Each CAO group or PCAO chain is preferably linked to the poly(C₂₋₄-alkyleneimine) (hereinafter referred to as "PAI") through a covalent "amide" link, formed between a terminal carbonyl group (-CO-) of the CAO group or PCAO chain and the nitrogen atom (N) of a primary or secondary amino group in the PAI, or through an ionic "salt" link, between a terminal carboxylate group (-CO-O⁻) of the CAO group or the PCAO chain and the positively charged nitrogen atom (⁺N) of a substituted ammonium group in the PAI. Because the dispersant contains at least two CAO groups or PCAO chains it may contain a mixture of amide and salt links depending upon the severity of the conditions under which it is prepared. The dispersant can be conveniently represented by the following general formula: wherein X -*-*- X represents a poly(C₂₋₄-alkylene)imine (PAI); Z represents a CAO group or PCAO chain linked to the PAI through an amide or salt link; and p is a number from 2 to 2000. The dispersant preferably contains from 4 to 2000 (p = 4 to 2000) and more preferably from 4 to 1000 (p = 4 to 1000) CAO groups or PCAO chains. The PAI is preferably a poly(ethyleneimine), hereinafter referred to as "PEI", which may be branched or straight-chained. A preferred dispersant comprises PEI carrying at least two CAO groups or PCAO chains attached thereto by amide and/or salt links. The PAI preferably has a weight-average molecular weight from 500 to 600,000 and more preferably from 1,000 to 200,000. The dispersant may be derived from a PAI and a CAO acid or a PCAO acid, i.e. a compound of the formula: in which n is from 1 to 100, or a cyclic precursor thereof, such as a lactone. The length of the PCAO chain in the PCAO acid may be controlled by the presence of chain stopper, such a carboxylic acid free from hydroxy groups, in the preparative process. Where the dispersant carries PCAO chains formed by the polymerisation of a carbonylalkyleneoxy monomer, such as a lactone, in the presence of the PAI, there is less need for a chain stopper, because the PCAO chains grow on the PAI and cannot react together; in such a case the pendant PCAO chains may be terminated by hydroxy groups. The dispersant may be derived from a PAI having at least two primary, secondary or tertiary amino groups, and a CAO or PCAO acid, in which case reaction between a p-, s- or t-amino group in the PAI and a terminal carboxyl group on the CAO or PCAO acid forms an amide or salt link. If the PAI contains a t-amino group only salt links can be formed, otherwise salt and/or amide links are formed depending on the reaction conditions. Generally, mild reaction conditions such as low temperatures and/or short reaction times promote the formation of salt links and more severe conditions, such as high temperatures and/or long reaction times promote the formation of amide links in a manner which is familiar to the skilled chemist. The dispersant comprising a PAI chain carrying CAO groups is novel and forms feature of the invention. Each CAO group is preferably terminated by a group which is free from OH/NH₂ groups, such as alkylcarbonyl. Termination is conveniently effected by reaction of a CAO acid, or lactone precursor, with a carboxylic acid which is free from hydroxy or amino groups, e.g. an alkane- or an alkoxyalkane-carboxylic acid, such as caproic acid, lauric acid, stearic acid, methoxyacetic acid and especially by a such an acid containing twelve or more, preferably 12 to 25, carbon atoms. Where the dispersant contains free amino groups these may be converted into substituted ammonium groups by reaction with an acid or a quaternising agent so that the dispersant is in the form of a substituted ammonium salt. Suitable reagents for this purpose are mineral and strong organic acids or acidic salts, such as acetic acid, sulphuric acid, hydrochloric acid, alkylsulphonic acids, alkyl hydrogen sulphates and arylsulphonic acids, especially acid forms of dyes and pigments, and quaternising agents such as dimethyl sulphate (DMS), methyl and ethyl halides and diethyl sulphate (DES). Where the solid is an inorganic material, such as an inorganic pigment, extender or filler, it is preferred that the dispersant is in the form of the free amine or a salt with a mineral acid or a quaternary ammonium salt. Where the solid is an organic material, such as an organic pigment or dye, it is often preferred that the dispersant is in the form of a substituted ammonium salt between free amine groups in the PAI portion of the dispersant and an aromatic acid containing from 2 to 10 benzene rings, more especially a coloured acid. Such salts are especially effective dispersants where the organic medium is an alcohol, such as ethanol or iso-propanol. By the term coloured acid is meant an organic pigment or dye containing at least one, preferably from 1 to 6, acid groups, especially sulphonic, phosphonic or carboxylic acid groups. It is convenient to use an acid form of the organic pigment which forms the solid in the composition. Thus, a preferred coloured acid for the preparation of a composition in which the solid is a copper phthalocyanine or a similarly deeply coloured pigment, is a copper phthalocyanine sulphonic acid, especially such an acid containing, on average, from 0.5 to 3 sulphonic acids groups per molecule, The dispersant may be prepared by reaction of a PAI with a PCAO acid or precursor thereof, such as a C₁₋₇-alkylenelactone or hydroxy-C₁₋₇-alkylenecarboxylic acid at a temperature from 25°C to 250°C for up to 24 hours. Under mild conditions (low temperature and/or short reaction time) salt links are formed and under more severe conditions (higher temperature and/or longer reaction time) amide, or a mixture of amide and salt links are formed. The CAO or PCAO acid may be prepared by heating a hydroxycarboxylic acid or lactone with a carboxylic acid which is free from hydroxy groups, such as acetic acid, caproic acid, lauric acid and methoxyacetic acid. The absence or degree of polymerisation is controlled by the relative proportions of the mono and bifunctional reactants. Reaction is conveniently performed at a temperature from 100°C to 250°C, preferably from 130°C to 200°C, in the presence of an esterification catalyst, such as tetrabutyl titanate, zirconium naphthenate, zinc acetate or toluenesulphonic acid. Where the PAI is PEI, the weight ratio of CAO acid or PCAO acid to PEI is preferably at least 1:1 and is more preferably in the range from 1:1 to 30:1. It is especially preferred, in the case of a dispersant based on PEI and a PCAO acid derived from E-caprolactone, that the weight ratio of the PCAO acid to PEI is from 1.5:1 to 30:1. The equivalent molar ratios of the two reactants depends, of course, on their respective average molecular weights. It has been found that a dispersant in which the PCAO chain is fairly short, i.e. containing from 2 to 7 CAO groups (mol wt = 400 to 1000) and the weight ratio of PCAO to PEI is fairly low, i.e. from 1.5:1 to 3:1, is particularly suitable for use in a dispersion of the solid in an alkanol. It has also been found possible to design a dispersant which is particularly suitable for use in a dispersion of the solid in an ester or a ketone by using a similar PCAO chain (i.e. containing 2 to 7 CAO groups) and a somewhat higher weight ratio of PCAO to PEI, i.e. from 3:1 to 5:1 or a rather longer PCAO chain containing 7 or more CAO groups (i.e. mol wt = 1000 or more) and a much higher weight ratio of PCAO to PEI, e.g. from 5:1 to 20:1. To minimise degradation of the reactants and products the reactions are preferably performed under an inert atmosphere, such as nitrogen. The invention is further illustrated by the following examples in which all parts and percentages are by weight unless otherwise indicated. Intermediate 1 A mixture of 112g of E-caprolactone, 9.2g of n-caproic acid and 0.1g of tetrabutyl titanate was stirred under nitrogen for 18 hours at 180°C to 190°C. The product was a hard wax with an acid value of 36mg KOH/g. It thus contains, on average, 12.6 5-oxy-pentamethylene-1-carbonyl (OPMC) groups. Intermediate 2 A mixture of 582g of E-caprolactone, 32.25g of methoxyacetic acid and 0.5g of tetrabutyltitanate was stirred under nitrogen for 20 hours at 170°C to 180°C. The product was a hard wax with an acid value of 35.2mg KOH/g. It therefore contains, on average, 13.2 OPMC groups. Intermediate 3 A mixture of 500g of E-caprolactone, 73g of lauric acid and 0.5g of tetrabutyltitanate was stirred under nitrogen for 20 hours at 170°C to 180°C. The product was a hard wax with an acid value of 36.35mg KOH/g. It therefore contains, on average, 11.8 OPMC groups. Intermediate 4 A mixture of 250g of E-caprolactone, 88g of lauric acid and 0.2g of tetrabutyltitanate was stirred under nitrogen for 8 hours at 160°C to 180°C. The product was a wax with an acid value of 75.7mg.KOH/g. It therefore contains, on average, 4.75 OPMC groups. Intermediate 5 A mixture of 485g of E-caprolactone, 34g of lauric acid and 0.1g of tetrabutyltitanate was stirred under nitrogen for 19 hours at 170°C to 190°C. The product was a hard wax with an acid value of 18.6mg.KOH/g. It therefore contains, on average, 24.7 OPMC groups. Intermediate 6 A mixture of 485g of E-caprolactone, 22.4g of lauric acid and 0.1g of tetrabutyltitanate was stirred under nitrogen for 19 hours at 170°C to 190°C. The product was a hard wax with an acid value of 12.4mg.KOH/g. and thus contains, on average, 37.9 OPMC groups. Intermediate 7 A mixture of 500g of E-caprolactone, 17g of lauric acid and 1.0g of tetrabutyltitanate was stirred under nitrogen for 19 hours at 170°C to 190°C. The product was a hard wax having an acid value of 9.9mg KOH/g and thus contains, on average, 47.9 OPMC groups. Intermediate 8 A mixture of 460g of E-caprolactone, 45g of methoxyacetic acid and 1g of tetrabutyl titanate was stirred under nitrogen for 8 hours at 160°C to 180°C. The product was a hard wax with an acid value of 59mg.KOH/g. It thus contains, on average, 7.5 OPMC groups. Intermediate 9 A mixture of 450g of E-caprolactone, 71g of methoxyacetic acid and 1g of tetrabutyl titanate was stirred under nitrogen for 8 hours at 160°C to 180°C. The product was a wax with an acid value of 84mg.KOH/g. It thus contains, on average, 5.1 OPMC groups. Intermediate 10 A mixture of 400g of E-caprolactone, 115g of methoxyacetic acid and 1g of tetrabutyl titanate was stirred under nitrogen for 8 hours at 160°C to 180°C. The product was a wax with an acid value of 147mg.KOH/g. It thus contains, on average, 2.6 OPMC groups. Intermediate 11 A mixture of 228g of E-caprolactone, 200g of lauric acid and 0.2g of tetrabutyl titanate was stirred under nitrogen for 10 hours at 160°C to 180°C. The product was a wax with an acid value of 139.2mg.KOH/g. It thus contains, on average, 1.8 OPMC groups. Intermediate 12 A mixture of 159g of E-caprolactone, 279g of lauric acid and 0.2g of tetrabutyl titanate was stirred under nitrogen for 8 hours at 160°C to 180°C. The product was a wax with an acid value of 193mg.KOH/g. It therefore contains, on average, 0.8 OPMC groups. Dispersant 1 A mixture of 32.5g of Intermediate 1 and 1.25g of a dry polyethylenimine having a weight-average molecular weight in the region of 100,000, available from BASF under the name "POLYMIN Waterfree" (POLYMIN is a trade mark), was stirred under nitrogen for 8 hours at 120°C. The product was a wax of equivalent 3175. Dispersant 2 This was prepared in a similar manner to Dispersant 1, but using 40g of Intermediate 1 and 3. 33g of "POLYMIN Waterfree". The product was a wax of equivalent 1510. Dispersant 3 This was prepared in a similar manner to Dispersant 1, but using 40g of Intermediate 1 and 13. 3g of "POLYMIN Waterfree". The product was a sticky wax of equivalent 475. Dispersant 4 A mixture of 10.8g of the product of Dispersant 1 and 10.8g of tetrahydrofuran was stirred and heated until a clear solution was obtained. The solution was cooled to 35°C and 0.405g of dimethyl sulphate was added. The mixture was then stirred for a further hour at 65-70°C. The tetrahydrofuran was then removed from the mixture by distillation. Dispersant 5 This was prepared in a similar manner to Dispersant 4, but using 10.24g of the product of Dispersant 2, 10.24g of tetrahydrofuran and 0.81g of dimethyl sulphate. Dispersant 6 A mixture of 16.1g of the product of Dispersant 3 and 16.1g of tetrahydrofuran was stirred and heated. A solution was obtained, but it was not completely clear. The solution was cooled to 40°C, and 4.05g of dimethyl sulphate was added slowly. There was a vigorous exotherm. The mixture was then stirred for a further hour at 65-70°C. The tetrahydrofuran was then removed from the mixture by distillation. Dispersant 7 This was prepared in a similar manner to Dispersant 1, but using 95.7g of Intermediate 2 and 7 . 36g of "POLYMIN Waterfree". Dispersant 8 This was prepared in a similar manner to Dispersant 1, but using 97. 3g of Intermediate 3 and 7 .48g of "POLYMIN Waterfree". Dispersants 9 to 41 Table 1 lists a series of preparations carried out in the same manner as described for Dispersant 1, unless otherwise stated, using "POLYMIN Waterfree" as PEI. The other starting materials, the weights thereof, and reaction conditions are indicated in the table. Dispersant 42 65g of Dispersant 7 was stirred above its melting point (approximately 60°C) and 4.05g dimethyl sulphate added, causing the temperature to rise by approximately 15°C. The mixture was then stirred for 1½ hours at 85°C to 95°C. Dispersant 43 This was prepared in a similar manner to Dispersant 17, but using 68g of Dispersant 8 and 4.05g of dimethyl sulphate. Dispersant 44 A mixture of 100g of Intermediate 3 and 7.69g of polyethyleneimine, having a number-average molecular weight of approximately 600, sold by the Dow Chemical Company under the name "MONTREK 6" (MONTREK is a trade mark), was stirred under nitrogen for 8 hours at 110°C to 130°C. The product was a hard wax. Dispersant 45 A mixture of 40g of Intermediate 4 and 20g of polyethyleneimine, having a number-average molecular weight of approximately 1800, sold by Dow Chemical Company under the name "MONTREK 18", was stirred under nitrogen for 5 hours at approximately 120°C. Dispersant 46 A mixture of 10g of "POLYMIN Waterfree", 100g of E-caprolactone and 0.2g of tetrabutyl titanate was stirred under nitrogen for 1 hour at 155-160°C and 45 minutes at 165-170°C. The product, a hard wax, was shown by infra red spectroscopy to be free of unpolymerised E-caprolactone. Comparative Dispersant 1 (CD 1) A mixture of 150g of poly-12-hydroxystearic acid having an acid value of 35mg.KOH/g, and 50g of "Polymin Waterfree" was stirred under nitrogen for 2 hours at 120°C. The mixture then had an acid value of approximately 18mg.KOH/g. To the mixture was then added 200g of iso-propanol to give the product, Comparative Dispersant 1, a solution having a solids content of approximately 50 wt%. Coloured Acid 1 (CA 1) This is copper phthalocyanine (CPC) sulphonic acid having, on average, 1.3 sulphonic acid groups per CPC nucleus. Fluidising Agent 1 (FA 1) To a stirred slurry of 300g of a filter cake containing 85.6g of copper phthalocyanine sulphonic acid (which contains, on average, 1.3 sulphuric acid groups per copper phthalocyanine nucleus) in 2L of water at 70-75°C is added 76g of a commercially available mixture of 75% dioctadecyldimethyl ammonium chloride and 25% iso-propanol (ARQUAD 2HT-75; ARQUAD is a Registered Trade Mark). After stirring at 90-100°C for 2 hours the solid is filtered off, washed with water and dried. Fluidising Agent 2 (FA 2) Solution A : Tetra 3,3'-dichlorobenzidine was prepared by tetrazotising 38g of 3,3'-dichlorobenzidine in 1200g of water at 0°C. Solution B : A mixture of 28g acetoacetanilide (1st coupling component) and 46.5g of potassium N-acetoacetyl-4-sulphanilate (2nd coupling component) was stirred into 500g of water. To the slurry were added 13.5g of 46.7% sodium hydroxide, and the temperature raised to complete solution of the acetoacetanilide. To the solution were added 16g of glacial acetic acid, 18.9g of 36% hydrochloric acid and 700g of water. Coupling : Solution A was added to Solution B over 75 minutes, the pH being controlled at 4.3 by the addition of sodium acetate. The reaction mixture was stirred overnight and then tested to ensure that no excess tetrazo was present. The reaction mixture was then heated to 70°C, 75.5g of dioctadecyldimethylammonium chloride (DODMAC) was added, and the mixture stirred for 1 hour at 70°C. The product, Fluidising Agent 2, made with equimolecular proportions of the two coupling components, was filtered off, washed with water and dried at 50-60°C. Fluidising Agent 3 (FA 3) Solution A : Tetrazo-3,3'-dichlorobenzidine was prepared by tetrazotising 13.45g of 3,3'-dichlorobenzidine in 500g of water at 0°C. Solution B : A mixture of 7.2g of 2-naphthol and 12.3g of the sodium salt of 6-hydroxy-2-naphthalene sulphonic acid (Schaeffer's acid) was stirred into 500g of water. A 30% aqueous solution of sodium hydroxide was then added with stirring until the pH was 8.5. Coupling : Solution A was added to Solution B over 1 hour, during which the temperature was maintained below 10°C and the pH was controlled at 8.5 by the addition of a 30% solution of sodium hydroxide. The reaction mixture was stirred for 1 hour, then heated to 90°C, cooled and filtered. The filter cake was reslurried in 900g of water, heated to 70°C and the pH adjusted to 3 by the addition of dilute hydrochloric acid. To the stirred acid slurry was added 22.5g of DODMAC over 10 minutes and the mixture stirred for 1 hour at 70°C. The product, Fluidising Agent 3, was filtered off, washed with water and dried at 50-60°C. Examples 1 to 75 The 75 dispersions, having the formulations described in Table 2, were prepared by ball milling the ingredients for 16 hours. All the resulting dispersions were fluid, deflocculated and with the pigment particles having a mean diameter below 5 microns. Examples 76 to 82 The dispersions, having the formulations described in Table 3, were prepared by ball-milling the ingredients in a high-energy ball mill with 3mm glass beads for 30 minutes. All the resulting dispersions were fluid, deflocculated and with pigment particles having a mean diameter below 5 microns. The following abbreviations are used in Tables 2 & 3: Comparative Example 1 A mixture of 7.0g of Pigment Yellow 34, 0.7g of Comparative Dispersant 1 and 2.3g of EOEA was ball-milled for 16 hours under the same conditions as Examples 1 to 75. The mixture became thick and the pigment failed to disperse satisfactorily. To evaluate the use of the dispersions in accordance with the present invention in high solids paint systems, the paints described below in Examples 83 to 91 were prepared. Examples 83 to 87 The high solids paint system employed in Examples 83 to 87 was an oil-free polyester combined with a hexamethoxymethyl melamine resin in the presence of a catalyst, p-toluene sulphonic acid. The oil-free polyester had an acid value of 10mg.KOH/g maximum, a hydroxy value of 110-130mg.KOH/g and is available from Croda Resins Ltd, in the form of an 8O% solution in EOEA, as PLASTOKYD HS-900 (PLASTOKYD is a registered trade mark). The hexamethoxymethyl melamine resin was from British Industrial Plastics Ltd in 100% active form, as BEETLE RESIN 3745 (BEETLE is a registered trade mark). In some paint formulations a levelling agent or resin modifier was also added. Mill-bases were prepared in a ball-mill, and in each case the mean particle diameter of the pigment after milling, was below 5 microns. After milling, the mill-base was converted into a usable paint by the addition of a let-down lacquer. Details of the mill-bases and let-down lacquers are shown in Table 4 in which all quantities are in grams. In Table 4, MODAFLOW, RESIFLOW FL2 and PA 57 are levelling agents or resin modifiers for paints, available from Monsanto Industrial Chemicals, Worlee-Chemie GmbH and Dow Corning Europe respectively (MODAFLOW and RESIFLOW are registered trademarks). Test panels on anodised aluminium were prepared for each of the above paints. Paints were applied with a 250 µm well applicator and a wire-wound K-bar (Meyer bar). Gloss, hardness, adhesion and moisture resistance were all satisfactory. Example 88 A high solids paint system was prepared incorporating an aliphatic polyisocyanate cross-linked with a hydroxyl functional acrylic resin, which also contained an oxazolidine functional modifier to increase paint solids. The aliphatic polyisocyanate used had an -NCO content of 23.5% and is available from Bayer AG in a 100% form as DESMODUR L2291 (DESMODUR is a Registered Trade Mark). The hydroxyl functional acrylic crosslinker used had an equivalent weight of 425 and is available from Rohm and Haas Company in the form of a 67% solution in methyl-n-amyl ketone as Experimental Resin QR-946. The oxazolidine functional modifier used had an equivalent weight of 100 and is also available from Rohm and Haas Company in a 97-99.5% form as Experimental Reactive Modifier QM-1007. A mill-base was prepared in a ball-mill, and the mean particle diameter of the pigment after milling was below 5 microns. After milling, the mill-base was converted into a usable paint by the addition of let-down lacquers. Let-down was carried out in two stages. The product of the first let-down stage is stable almost indefinitely, whilst the second stage let-down gave a usable paint which had a pot-life of a only few hours. Details of the millbase and let-down lacquers are shown in Table 5. Test panels on anodised aluminium were prepared by applying the above paint with a wire-wound K-bar (Meyer Bay). Gloss, hardness, adhesion and moisture resistance were all satisfactory. Example 89 A high solids stoving (baking) paint system was prepared incorporating a short-oil alkyd resin combined with a hexamethoxy-methylmelamine resin in the presence of a catalyst, p-toluene sulphonic acid. The short-oil alkyd resin was of the tall oil fatty acid type, 90% solids by weight in EOEA, and is available from Cargill Inc., USA under the product code 5710. The hexamethoxy-methylmelamine resin was essentially 100% solids, had a viscosity in the range Y-Z3 on the Gardner Holdt scale, and is also available from Cargill Inc. under the product code 2347. The millbase was prepared in a ball mill, and the mean particle diameter of the pigment after milling was below 5 microns. After milling, the mill-base was converted into a usable paint by the addition of let-down lacquer. Details of the mill-base and let-down lacquer are shown in Table 6. BYK 300 is a levelling agent available from Byk-Chemie, USA. (BYk is a Registered Trade Mark). Test panels on tinplate and anodised aluminium were prepared by applying the above paint with a wire-wound K-bar. Gloss, adhesion and moixture resistance were all satisfactory. Examples 90 and 91 High solids air-drying paint systems were prepared incorporating Soya oil alkyd resins. The resins used were Cargill products 5713 (an 80% solids solution in butyl acetate, with viscosity: Z4-Z6 and acid number: 10) and 5725 (an 80% solids solution in EOA, with viscosity: Z4-Z5 and acid number: 6). Millbases were prepared in a ball mill, and the mean particle diameter of the pigment after milling was below 5 microns. After milling the millbases were converted into usable paints by the addition of let-down lacquer. Details of the mill-base and let-down lacquers are shown in Table 7. Test panels on tinplate and anodised aluminium were prepared by applying the above paints with a wire-wound K-bar. Gloss and adhesion were both satisfactory. To evaluate the use of a dispersion in accordance with the present invention in a conventional paint system, the paint described in Example 92 below was prepared. Example 92 A stoving (baking) paint system was prepared incorporating a non-drying alkyd resin combined with a melamine-formaldehyde resin. The alkyd resin used was glycerol-based, acid value 7mg.KOH/g and is supplied as a 70% solution in xylene by Croda Resins Ltd., under the name PLASTOKYD C-30AX (PLASTOKYD is a Registered Trade Mark). The melamine-formaldehyde resin used was of the n-butylated type, and is supplied as a 60% solution in n-butanol by British Industrial Plastics Ltd., under the name BEETLE BE 615 (BEETLE is a Registered Trade Mark). The mill-base was prepared in a ball mill, and the mean particle diameter of the pigment after milling was below 5 microns. After milling the mill-base was converted into a usable paint by the addition of let-down lacquers in two stages. Details of the mill-base and the let-down lacquers are shown in Table 8. Test panels on tinplate and anodised aluminium were prepared by applying the above paints using a wire-wound K-bar or an air-driven spray gun as appropriate. Gloss, adhesion and scratch resistance were all satisfactory. Examples 93 to 97 The formulations described in Table 9 below are similar to those used in different types of ceramic tape casting or doctor blade processes. In Examples 93 and 94 typical resin binders and plasticisers are also included in the dispersion formulation. In Examples 95 to 97 only dispersant, solvent(s) and ceramic powder are included in the dispersion formulation. In Examples 93 to 95, the dispersions were prepared by ball milling the ingredients in a high-energy ball mill with 3mm glass balls for 30 minutes. In Examples 96 and 97 the dispersions were prepared by ball milling the ingredients for 16 hours. All the resulting dispersions were fluid and deflocculated. A-16 Alumina is a calcined alumina, ultimate crystal size 0.3 - 0.5µm, supplied by the Aluminium Company of America. The barium titanate is "Grade S" supplied by Anzon Ltd., of Newcastle, England. It has an average particle size of 1.49µm, and it is of the type typically used in ceramic capaciters. The zirconium oxide is "Grade SC15" supplied by Magnesium Elektron Ltd., of England. It has an average particle size of less than 2µm. PEG 2000 is polyethylene glycol, with a molecular weight of about 2000. The polyvinyl butyral was supplied by the Aldrich Chemical Co., and had a molecular weight of about 36000.

Claims: A composition comprising a finely-divided non-magnetic solid and a dispersant comprising a poly(C₂₋₄-alkyleneimine) carrying at least two mono- or poly(carbonyl-C₁₋₇-alkyleneoxy) groups. A composition according to Claim 1 wherein the solid is selected from pigments, extenders, fillers, disperse dyes, optical brightening agents, textile auxiliaries, oil-based and invert-emulsion drilling mud solids, dirt and soil particles, particulate ceramic materials, biocides, agrochemicals and pharmaceuticals. A composition according to Claim 1 or Claim 2 wherein the solid is dispersed in an organic medium. A composition according to Claim 4 wherein the organic medium is a polar organic medium selected from alcohols, dialkyl- and cycloalkyl-ketones, alkyl esters of alkanecarboxylic acids, dialkyl- and cycloalkyl-ethers containing up to 6 carbon atoms, polyester and polyamide resins and cellulose ethers. A composition according to any one of Claims 1 to 4 wherein the dispersant is a compound of the formula: wherein X -*-*- X represents a poly (C₂₋₄-alkyleneimine) (PAI); Z represents a mono(carbonylalkyleneoxy) (CAO) group or a poly(carbonyl-C₁₋₇-alkyleneoxy) (PCAO) group linked to the PAI through an amide or salt link; and p is a number from 2 to 2000. A composition according to Claim 5 wherein the CAO and PCAO groups are of the formula: T -(O - V - CO) n - wherein T is H or a terminal chain stopping group; V is a C₁₋₇ - alkylene group; and n is a number from 1 to 100. A dispersant comprising a poly(C₂₋₄-alkyleneimine) (PAI) carrying at least two CAO groups of the formula: T - O - V - CO - wherein T is H or a terminal chain stopping group; and V is a C₁₋₇-alkylene group; each CAO group being linked to the PAI through an amide or salt link between the terminal carbonyl group on the CAO group and a nitrogen atom in the PAI. A dispersant according to Claim 7 wherein the PAI is a poly(ethyleneimine) having a weight-average molecular weight from 500 to 600,000.

Inventors: CAMPBELL, FREDERICK, GEARY, JOHN MARTIN, SCHOFIELD, JOHN DAVID
Applicants: IMPERIAL CHEMICAL INDUSTRIES PLC
Application year: 1985
Main classification: B01F17
IPC codes: C09B67, B01F17, A01N25, C09D17, C09D11, A61K9, C09K8, D06M13, A61K47, D06M15, B01J13