HOT MELT BUTYLENE-ETHYLENE COPOLYMER ADHESIVES

Abstract: Hot melt adhesive with long open time good bonding to cold metals are made of blends of a maleic anhydride modified copolymer of butene-1 and ethylene, an aliphatic substantially non-polar tackifier resin, an antioxidant and, optionally, one or more of a microcrystalline wax, a block copolymer and atactic polypropylene.

Description: This invention relates to a hot melt adhesive which exhibits good cold metal bonding and a long open time and which contains a modified butene-1/ethylene copolymer. Adhesive open time is the longest time that an adhesive material remains capable of auto-adhesion (adhesion to itself or to a substrate) after it has been cooled from the melt to room temperature. Hot melt adhesives which exhibit a long open time (greater than 20 minutes), as well as good cold metal bonding, have long been sought for various applications which require a long open time. For example, extensive surfaces to be coated by adhesives such as table tops to which laminates are bonded or assembly line auto parts which are coated with adhesive and later contacted with other parts at some point further down the assembly line are particularly suited to the use of hot melt adhesives which display long open times. Sometimes adhesive coated parts must remain uncontacted for as long as several hours, and thus require longer open times than are exhibited by and characteristic of polymers typically used in nonpressure sensitive hot melt adhesives. Hot melt adhesives can be formulated to be pressure sensitive and have an infinite open time but these adhesives are usually soft, tacky and have limited strength and adhesion. Conventional hot melts such as formulations of poly(ethylene/vinyl acetate) (EVA) polyethylenes, polyamides or polyesters are rigid, form good strong bonds to certain substrates but have short open times of usually less than 1 minute. Moreover, these adhesives usually have problems in adhering to cold metal substrates which is often required for assembly line production. Solvent applied contact adhesives can be formulated to give good bond strengths and reasonable open times but they require the use of solvents which can be toxant, pollutant and fire hazards. Butene-1 polymers are composed of linear chain molecules with the regular and spatially ordered arrangement of ethyl side groups, the pendant groups that result when butene-1 is polymerized across the 1,2-double bond (along an ethylene chain backbone) (US-A-3,362,940). When cooled from melt, the ethyl side groups initially align in a tetragonal spatial arrangement, developing a little over one half of the ultimate crystallinity (form II). With time, the tetragonal crystalline phase transforms into a stable hexagonal spatial arrangement with subsequent development of additional crystallinity (form I). This is a very slow process, the transformation being completed in the neat polymer over a period of several days. The butene-1 polymers are a unique group of olefinic polymers because they crystallize very slowly. The very slow crystallization rate in contrast to the crystallization rates of other crystalline olefinic polymers such as EVAs, polyethylenes and polypropylenes, has been found to be beneficial in formulating hot melt adhesives which have very long open times as well as good adhesion and bonding to cold, heat-sink type substrates, metals such as stainless steel and anodized aluminum for example. US-A-3,573,240 describes hot melt adhesive compositions for hard cover book binding. The nature of the book binding process is such that an adhesive which rapidly sets and which has an extremely short open time is desired. Column 4, lines 1 to 7 of US-A-3573240 disclose that minor amounts, i.e. up to about 5% by weight of alpha olefin comonomers such as ethylene and propylene may be present in the butene-1 polymerization system without any substantial loss of the desirable properties displayed by the resultant essentially homopolymeric system and also states (column 2, lines 61 to 63) that the hot melt adhesive products display good heat stability and rapid setting speed . Thus, this document teaches that even though up to about 5% by weight of ethylene may be added to the butene-1 polymerization system, the polymerization system exhibits rapid setting speed (short open time). It is known that the adhesion of olefinic polymers to various substrates can be improved by incorporating functionality into the chain by copolymerization or by grafting. Ethylene/acrylic acid copolymers are examples of such functional group-containing copolymers. There are disclosures of polypropylene and polyethylene being grafted with maleic anhydride or anhydride derivatives using a free radical (peroxide and heat) which teach that adhesion to substrates such as nylon and glass can be improved. In accordance with the present invention it has been found that modified butene-1 polymers containing small amounts of ethylene can be used with certain resins to provide hot melt adhesives which have extremely long open times. According to the invention there are provided hot melt adhesive compositions which comprise a blend of (i) from 15% by weight to 85% by weight of a copolymer of butene-1 and ethylene modified by reaction with maleic anhydride, the ethylene content of the unmodified copolymer being from 5.5% to 10.0% by weight of said copolymer, (ii) from 15% to 60%, preferably 20% to 60%, by weight of, as tackifying resin, an aliphatic substantially non-polar resin (preferably having a softening point of 70° to 125°C) selected from C₅-C₉ stream resins, polyterpenes and hydrogenated resins, (iii) from 0.1% to 0.5% by weight of an antioxidant, (iv) up to 25%, preferably up to 20%, by weight of a microcrystalline wax, (v) up to 35% by weight of a block copolymer which comprises at least one monoalkenyl arene polymer end block A and at least one substantially completely hydrogenated conjugated diene second block B and (vi) up to 40% by weight of an atactic polypropylene, the weight percentages of (i), (ii), (iv), (v) and (vi) being based upon their combined weight and the weight percentage of (iii) being based upon the total weight of the adhesive. Butene-1 can be polymerized with a variety of alpha-olefins to provide useful copolymers such as those taught in US-A-3,362,940. Butene-1/ethylene copolymers, with ethylene in the 11-20 mole percent range, are of special interest in hot melt adhesives, as the ethylene comonomer produces a lower glass transition temperature (Tg) amorphous phase, reduces further the crystallization rate, and reduces the ultimate level of crystallinity in the polymer. Such properties are advantages in the development of long open time melt adhesives, as a lower Tg polymer and a higher amorphous phase polymer offers wider formulating latitude in combination with compatible resins, waxes, oils, fillers and additives. The adhesive formulations of the present invention exhibit extremely long open times of greater than 20 minutes and in some cases greater than 300 minutes (5 hours). The hot melt adhesives of the invention bond well to glass, as well as cold substrates such as stainless steel and anodized aluminum. They possess good adhesive strength, are flexible and have low melt viscosities. In addition, the shear adhesion failure temperature (SAFT or service temperature) may be controlled to remain sufficiently high for the adhesives to be used in a variety of applications, and T-peel values are high. Uses of the adhesives of the present invention include but are not limited to use as a contact adhesive for assembly of furniture, miscellaneous robot assembly, as an automotive sealant and to improve open time in bonding. A preferred adhesive comprises a blend of (i) from 35% to 55% by weight of a modified copolymer of butene-1 and ethylene, the ethylene content of the unmodified copolymer being about 5.5% by weight, (ii) from 35% to 55% by weight of, as tackifying resin, a hydrogenated C₉ based resin, (iii) from 0.2% to 0.4% by weight of an antioxidant, (v) up to 25% by weight of said block copolymer and (vi) up to 30% by weight of atactic polypropylene. The butene-1/ethylene copolymers which are modified with maleic anhydride to provide one component of the adhesives of the invention contain from about 5.5% by weight (11 mole percent) to about 10% by weight (20 mole percent) ethylene. Polymers discussed herein are identified as H-1 B (homopolymeric butene-1), 1B-coE 1.5 (1.5 mole percent (0.75 weight percent) coethylene with butene-1) and 1B-coE 11.0 (11.0 mole percent (5.5 weight percent) coethylene with butene-1). A summary of neat butene-1 polymer properties contrasting homopolymer butene-1 (H-1B) with coethylene butene-1 polymers (1B-coE 1.5 and 1B-coE 11) is shown in Table 1. The Tg for 1B-coE 11 is substantially lower than that of H-1B and 1B-coE 1.5. The butene-1 polymers can be made to a wide range of melt flow as shown in Table 1 by cracking them in an extruder with heat and peroxides. 1B-coE11.0 with a melt flow of 0.2 can be changed to a melt flow of 99 by passing it through an extruder with 1000 ppm of Lupersol 101 peroxide from Pennwalt. The average residence time in the extruder was 2 minutes at 200 o C. The cracking process also lends itself to a grafting of the butene-1 with monomers which are capable of undergoing a reaction with free radicals. Examples include vinyl silanes, acrylic acid, maleic anhydride, methacrylates, acrylates, styrene, acrylonitrile, vinyl chloride, vinyl esters and derivatives thereof. Of particular interest is maleic anhydride and derivatives thereof because they are easy to graft and significantly promote adhesion to substrates such as nylon, aluminum, metals in general and silane treated glass. Grafting can be carried out with the butene-1 polymers by simply mixing maleic anhydride with the appropriate polymer and peroxide and then passing the mixture through a heated extruder. The content of maleic anhydride in the modified butene-1 polymer can suitably be from 0.05% to 5% by weight, preferably from 0.05% to 1.5% by weight. The butene-1 polymer grafted with maleic anhydride to provide a modified polymer preferably is 1B-coE11.0. To formulate adhesives the modified butene-1/ethylene copolymer is mixed with, as tackifier resin, a substantially non-polar aliphatic tackifier resin, particularly C₅-C₉ stream resins, polyterpene resins and hydrogenated resins, such as a partially hydrogenated C₉ based hydrocarbon resin, as well as C₅ stream resins and polyterpenes. These tackifier resins are suitably used in amounts of from 20% to 60% by weight and preferably 30% to 50% by weight. Arkon P-85 was used in the Examples below, this being a resin which shows a melting point (Tm) and a glass transition temperature (Tg) above room temperature; T m = 47 o C, Tg = 35 o C. Blends with butene-1 polymers are clear with no color. The adhesives of the present invention can contain microcrystalline waxes. The waxes are optional and may be used in amounts up to 50% by weight, preferably up to 25% by weight and more preferably up to 20% by weight, say 10% to 20% by weight, of the adhesive composition. Shellwax ® 500 was used. A sufficient amount of the wax, preferably 10% by weight, can be used, if desired, to effect a lower viscosity without a substantial decrease in service temperature of the adhesive. A hindered phenolic antioxidant (A.0.) was used in the Examples. Unless otherwise noted, tetrakis methylene (3,5-di-tert-butyl-4-hydroxyhydrocinnamate)methane was used at a level of 0.3% by weight. Optionally, atactic polypropylene (APP) (AFAX 510) may be added in amounts of from 5% to 40% by weight to give good T-peel values. Preferably about 25% by weight is added. The Arkon P-85 is reduced accordingly, to compensate for the APP. A block copolymer, (KRATON G 1657 (styrene-coethylene/butene-1-styrene from Shell Chemical), a SEB (styrene-coethylene/butene-1 copolymer) diblock polymer, for example), may be optionally added in amounts up to 35% by weight, preferably up to 20% by weight. The block copolymer comprises at least one monoalkenyl arene polymer end block A and at least one substantially completely hydrogenated conjugated diene (isoprene or butadiene) second block B, said block copolymer having an 8 to 55 percent by weight monoalkenyl arene polymer block content, each polymer block A having an average molecular weight of between 4,000 and 125,000, and each polymer block B having an average molecular weight of between 10,000 and 300,000. The block copolymers employed in the present invention may have a variety of geometrical structures, since the invention does not depend on any specific geometrical structure, but rather upon the chemical constitution of each of the polymer blocks. Thus, the structures may be linear, radial or branched so long as each copolymer has at least one end block A and at least one second block B as defined above. Methods for the preparation of such polymers are known in the art. Particular reference will be made to the use of lithium based catalysts and especially lithium-alkyls for the preparation of the precursor polymers (polymers before hydrogenation). US-A-3,595,942 not only describes some of the polymers which may be used in the adhesives of the invention but also describes suitable methods for their hydrogenation. The structure of the polymers is determined by their methods of polymerization. For example, linear polymers result by sequential introduction of the desired monomers into a reaction vessel when using such initiators as lithium-alkyls or dilithiostilbene, or by coupling a two segment block copolymer with a difunctional coupling agent. Branched structures, on the other hand, may be obtained by the use of suitable coupling agents having a functionality with respect to the precursor polymers of three or more. Coupling may be effected with multifunctional coupling agents such as dihaloalkanes or -alkenes and divinyl benzene as well as certain polar compounds such as silicon halides, siloxanes or esters of monohydric alcohols with carboxylic acids. In the Examples parts and percentages are by weight unless indicated otherwise. EXAMPLE 1 Adhesive Preparation The butene-1 polymers were cracked by tumbling pellets thereof with a peroxide (Lupersol 101) at 0-2000 ppm. The mixture was passed through a Brabender extruder at 200 o C. The rpm for the extruder was adjusted to achieve a 2 minute average residence time in the extruder. Butene-1 polymers functionalized with maleic anhydride were prepared by mixing polymer pellets with a peroxide (Lupersol 101) at 2000-10000 ppm and an appropriate amount of maleic anhydride. The mixture was passed through a heated extruder. The temperature of the extruder was chosen so as to melt the butene-1 polymer and to cause at least 75% of the peroxide to decompose into reactive free radicals. Typically 1000-4000 ppm of a peroxide (Lupersol 101) was used with 0.1% to 5% maleic anhydride. A Brabender extruder heated to 200 o C was used. The rpm of the extruder was chosen to obtain a 2 minute residence time. Table 2 shows the various functionalized butene-1 polymers that were made. Adhesives were prepared using either a small Brabender compound head (approximately 50 cc capacity) or a U.S. one quart (0.95 dm³) sigma blade mixer. The test formulations were easily blended using preheated equipment (170-180 o C) by introducing the butene-1 polymer, mixing until a soft, homogeneous mass was formed, and then gradually introducing the remaining ingredients. Batch times were 20 minutes. EXAMPLE II Adhesive Film Thin adhesive films (125 to 200 µm) were prepared by casting onto release coated polyester film (onto release coated side) using a pair of heated nip rolls that are adjusted to produce the desired gap, hence adhesive thickness. Preheated adhesive (at about 130 o C) was poured onto a polyester film and hand drawn through the heated nip rolls. Using this technique, adhesive films a meter in length by 15 centimeters in width were produced with a small quantity (<60 gms) of adhesive, so that very small quantities of adhesive could be evaluated. Once cooled and allowed to set, these adhesives were used to prepare test specimens. For example, Kraft paper to Kraft paper bonds were made by cutting adhesive squares from the polyester film, peeling them off, placing the adhesive between the paper and heat sealing with a hot bar sealer (time, pressure and temperature can be adjusted). Alternatively, the adhesive square or an adhesive strip may be placed on a piece of plastic or metal substrate, melted with a heat gun (or in an oven), and then joined under moderate contact pressure to form T-peel, lap shear or SAFT bonded substrate specimens. TESTING METHODS 1. Adhesive Hot Melt Viscosity - Viscosities were measured at 177 o C in a Brookfield Thermocell Viscometer with an RVT head and Number 29 spindle (ASTM D3236); for low viscosity formulations, a number 21 spindle was used. 2. SAFT: Shear Adhesion Failure Temperature - The upper service temperature limit of the adhesive was estimated by the SAFT test. A 25 X 25 mm lap shear specimen was formed with the substrate of interest, the adhesive as the interlayer between the substrate surfaces. In the case of Kraft paper, National Bureau of Standards, Standard Reference Material 1810, Linerboard, was used. The lap shear specimen was suspended in a temperature programmed oven, and the free end of the specimen was loaded at 500 or 1000 gm. The temperature was programmed to rise at a rate of 22 o C/hour. The SAFT was taken at the temperature at which the bond fails and the weight-load falls. 3. Lap Shear Strength - A 25 X 25 mm lap shear specimen was formed with the substrate of interest, the adhesive as the interlayer between the substrate surfaces. Specimens were drawn apart at a rate of 1.27 mm/min. on an Instron tester, and the maximum force required to break the bond was recorded. With the magnitude of force required to break the adhesive bonds of crystalline/olefinic polymer based recipes, substrates chosen for this test were metals. About 0.75 mm (30 mils) thick stainless steel were used for testing. However, 3 mm (125 mils) thick anodized aluminum (AA) affords about an equivalent strength, and will avoid metal yield/stretch in measuring lap shear strength. 4. T-peel Adhesion - a 25 mm X 150 mm laminate sandwich was formed with the substrate of interest, the adhesive as the interlayer between the substrate surfaces. The laminate surfaces were placed in an Instron tester, one surface in the upper jaw, the other surface in the lower jaw. The jaws were separated at a rate of 25 cm/min. Force required to peel the surfaces was recorded continuously. The maximum and minimum values were noted, as well as failure mode, i.e. adhesive, cohesive or combination thereof. This test approximates a peel angle of about 180 o C. 5. Adhesive Open Time - Open time is defined as the maximum time at which auto-adhesion (adhesion of the adhesive to itself or a substrate) can take place for a material which, after melting, has been brought to room temperature. Open time was measured by applying test recipes as a hot melt onto two surfaces at ambient temperature, waiting the specified time, then pressing the adhesive surfaces together under moderate pressure (adhesive to adhesive). Within 10 minutes of this bond formation the surfaces were pulled slowly apart under tension. Bonds that did not fail at the adhesive/adhesive interface (as a function of time) marked maximum open time. 6. Polymer Melt Index - Melt index (abbreviated MI or M.I. throughout) was determined according to ASTM D1238, condition E, temperature (190 o C) and load (2160 g). These conditions are typically used for EVA and polyethylene polymers. 7. Tm and Tg by Differential Scanning Colorimetry (D.S.C.) - Heating and cooling rates were 10 o C/minute. Tm is the temperature at which a maximum occurs in the crystalline melting caloric peak. For resins, Tg was determined by drawing a tangent to the subtle shoulder in the heating portion of the D.S.C. cycle, determining the mid-point of this tangent, and reading the temperature at this mid point. EXAMPLE III Functionalized and non-functionalized butene-1 copolymers were formulated with various ingredients to make hot melt adhesives with long open times. Details of the adhesives thus formulated and their properties are summarised in Table 3. Table 3 illustrates the difference between adhesive formulations based upon the functionalized and nonfunctionalized butene-1 polymers. Formulations containing nonfunctionalized 1B-coE11.0 are compared with 1B-coE11.0 functionalized with 0.1% or 3% by weight maleic anhydride for viscosity, SAFT, T-peel and lap shear results. KRATON G polymer 1657 or SEB1 diblock are present in formulations 1 to 5. All formulations except for formulation 6 contained 50% by weight Arkon P-85. Formulation number 6 contained 25% by weight Arkon P-85 and 25% by weight of atactic polypropylene (AFAX 510). All formulations contained 0.3% by weight Irganox 1010 antioxidant. It can be seen from Table 3 that the T-peel values are higher with the use of the maleic anhydride functionalized polymers. However, it is interesting to note that 0.1% maleic anhydride modified polymer gives about the same T-peel value after seven days as does 3.0% maleic anhydride modified polymer as may be seen from formulations 4 and 5. The T-peel value of 20.4 after one day for formulation 6 was better than the T-peel values after seven days of formulations 1 to 3 and 8. It is apparent that the inclusion of atactic polypropylene in this recipe produced a softer adhesive, tending to fail more cohesively, thus yielding higher initial peel values. It is readily apparent from Table 3 that the T-peel value, i.e. the difficulty in separation of the materials bound by the adhesive, is higher for the polymers which have been functionalized with maleic anhydride than for the unmodified polymer. The T-peel value difference between functionalization with 0.1% maleic anhydride and 3.0% maleic anhydride is minimal. The reference Formulations 1, 2 and 8 in Table III each showed poor T-peel values. Each contained non-functionalized 1B-coE11.0. All three formulations showed eventual "adhesive failure" modes with time. All other formulations contained functionalized 1B-coE11.0 (either 0.1% by weight MA or 3.0% by weight MA). Additionally, some contained KRATON G Polymer 1657 or SEB1 diblock. Formulations 2, 3, 4, 7 and 8 showed moderate combination failure modes-cohesive and adhesive. Formulation 3 showed acceptable T-peel values with 0.1% by weight maleic anhydride modified 1B-coE11.0 and SEB1 diblock. Formulation 4 also contained 0.1% by weight maleic anhydride, but contained the KRATON G 1657. The T-peel value after 7 days was higher than that of Formulation 3 (SEB1 diblock) even after 30 days. Formulation 7 contained 30% by weight 1B-coE11.0 functionalized with 3.0% by weight maleic anhydride. T-peel values were moderately better than those of Formulation 3 which contained only 0.1% by weight maleic anhydride. However, Formulation 7 also had less lower limit T-peel value fluctuation than Formulation 3. Formulations 5 and 6 are especially noteworthy. Both exhibited failure mode "C" (cohesive), the preferred mode of failure. Both contained equal amounts of 3.0% MA modified 1B-coE11.0 polymer and KRATON G Polymer 1657 triblock. Formulation 5 contained 50% by weight Arkon P-85, while Formulation 6 contained 25% by weight Arkon P-85 and 25% by weight atactic polypropylene (AFAX 510). Formulation 6 showed better T-peel values than did Formulation 5, however, the T-peel values of Formulation 5 (no APP) were quite acceptable. Interestingly, Formulation 6 which contained APP, had a lower limit T-peel value of almost three times that of Formulation 5 (no APP). Thus, Formulation 6 (APP) showed less lower limit T-peel fluctuation than did Formulation 5, however, Formulation 5 exhibited good maximum T-peel values and, surprisingly, cohesive failure mode. In sum, maleic anhydride modified butene-1 copolymers result in better adhesion. Addition of SEB1 diblock results in acceptable T-peel values and quite good values after 30 days even at only 0.1% MA (Formulation 2). Use of KRATON G 1657 at 3.0% MA gives a higher 1 day T-peel value and yields "cohesive" failure mode. Use of 25% by weight APP (AFAX 510) yields excellent maximum T-peel values, as well as an excellent lower limit T-peel value at 1 day. Thus, if "cohesive" failure is desired, a greater amount of MA should be used. If a high T-peel lower limit is desired, APP will be desired. Good T-peel maximum values may be obtained with 0.1% MA. Lap shear values were adequate for all formulations. As may be seen from Table 4, the only formulations which exhibited both long open time as well as glass and cold metal adhesion were numbers 4, 5 and 6, which contained 50%, 40% and 30% by weight, respectively, 1B-coE11.0 modified with 1% by weight maleic anhydride. Formulation 3, which did not contain a maleic anhydride-modified butene-1 polymer, showed no adhesion to glass and only moderate adhesion to stainless steel. Numbers 4 and 5 also contained 10 and 20% by weight, respectively, of Shellwax 500, a microcrystalline wax. Formulations 1 and 2 (polyethylene and ethylene-vinylacetate adhesives) each exhibited extremely short open times of less than 1 minute. Number 1 did not bond to the cold aluminum or cold stainless steel, nor to the cold glass. Number 2 did not bond to the cold stainless steel or the cold glass. Thus, formulations with Arkon P-85 and from 30% by weight to 50% by weight 1B-coE11.0 modified with 1% maleic anhydride and from 10% by weight to 20% by weight Shellwax 500 exhibit long open time values, as well as good adhesion to glass, as well as to cold anodized aluminum and cold stainless steel. Most preferably, 50% by weight 1B-coE11.0 modified with 1% maleic anhydride, 50% by weight Arkon P-85 resin, and about 0.3% antioxidant, yields an open time of greater than 300 minutes (5 hours) and exhibits moderate adhesion to glass, and good adhesion to cold anodized aluminum and stainless steel, in conjunction with very high peel strength values to steel as shown in comparing formulations 2 and 3 in Table 3. Such properties indicated by formulations 4, 5 and 6 allow adhesion on glass and metal surfaces with open times of the order of anywhere from several minutes to several hours. This is particularly advantageous, for example, in auto plant assembly lines where the adhesive is applied to a large metal surface area which is not bonded to another piece of equipment until some point further down the assembly line. In sum, use of 1B-coE11.0 copolymer modified with maleic anhydride yields a long open time and good bonding to aluminum, stainless steel and glass, as well as good failure modes and T-peel minimum and maximum values.

Claims: A hot melt adhesive which comprises a blend of (i) from 15% by weight to 85% by weight of a copolymer of butene-1 and ethylene modified by reaction with maleic anhydride, the ethylene content of the unmodified copolymer being from 5.5% to 10.0% by weight of said copolymer, (ii) from 15% to 60% by weight of, as tackifying resin, an aliphatic substantially non-polar resin selected from C₅-C₉ stream resins, polyterpenes and hydrogenated resins, (iii) from 0.1% to 0.5% by weight of an antioxidant, (iv) up to 25% by weight of a microcrystalline wax, (v) up to 35% by weight of a block copolymer which comprises at least one monoalkenyl arene polymer end block A and at least one substantially completely hydrogenated conjugated diene second block B and (vi) up to 40% by weight of an atactic polypropylene, the weight percentages of (i), (ii), (iv), (v) and (vi) being based upon their combined weight and the weight percentage of (iii) being based upon the total weight of the adhesive. A hot melt adhesive according to claim 1 wherein the tackifying resin has a softening point of 70° to 125°C. A hot melt adhesive according to claim 1 or 2, which comprises a blend of (i) from 35% to 55% by weight of a modified copolymer of butene-1 and ethylene, the ethylene content of the unmodified copolymer being about 5.5% by weight, (ii) from 35% to 55% by weight of, as tackifying resin, a hydrogenated C₉ based resin, (iii) from 0.2% to 0.4% by weight of an antioxidant, (v) up to 25% by weight of said block copolymer and (vi) up to 30% by weight of atactic polypropylene. A hot melt adhesive according to claim 3 wherein said tackifying resin has a softening point of about 85 o C. A hot melt adhesive according to any one of the preceding claims, wherein said antioxidant is tetrakis methylene(3,5-di-tert-butyl-4-hydroxyhydrocinnamate)methane. A hot melt adhesive according to any one of the preceding claims, wherein said modified copolymer contains from 0.05% to 5% by weight maleic anhydride grafted onto said butene-1/ethylene. A hot melt adhesive according to claim 6, wherein said modified copolymer contains from 0.05% to 3% by weight maleic anhydride grafted onto said copolymer. A hot melt adhesive according to claim 7, wherein said modified copolymer contains from 0.05% to 1.5% by weight maleic anhydride grafted onto said copolymer. Use of a hot melt adhesive as claimed in any one of the preceding claims in the bonding of surfaces.

Inventors: HANSEN, DAVID R., KORCZ, WILLIAM H.
Applicants: MITSUI PETROCHEMICAL INDUSTRIES, LTD., SHELL OIL COMPANY
Application year: 1985
Main classification: C09J123
IPC codes: C09J151