PROCESS FOR THE DIMERIZATION OF OLEFINS

Abstract: A process for the dimerization in the liquid phase of an aliphatic mono-olefin having 2 to 12 carbon atoms with a catalytic system formed by combining, in the presence of water, an alcohol or a carboxylic acid:- a) a palladium compound, b) a chelate ligand having as coordinating atoms at least two Group 5a atoms which are connected through a chain comprising 2 to 6 carbon atoms, and c) a compound containing an anion of an acid, except hydrohalogenic acids.

Description: PROCESS FOR THE DIMERIZATION OF OLEFINS The present invention relates to a process for the dimerization in the liquid phase of an aliphatic mono-olefin having in the range of from 2 to 12 carbon atoms per molecule in the presence of a catalytic system containing palladium. It is known that for dimerizing low molecular weight aliphatic mono-olefins a catalytic system can be used, which is formed by combining a palladium halide with an organoaluminum halide and preferably with a monodentate phosphine, arsine or stibine (cf. UK Patent Specification 1,153,519). It is also known to dimerize propene in the presence of a catalytic system formed by combining pentanedionatopalladium with ethylaluminum dichloride and an organic monodentate phosphine or phosphite (cf. Angew. Chem. Int. Ed. 14 (1975) 104-105. Because of the presence of organoaluminum halides in the catalytic systems the above dimerization reactions should be carried out under strictly anhydrous conditions. Further, it is known to dimerize ethene with a catalytic system formed by combining tetrakis(acetonitrile)palladium ditetrafluoroborate with a monodentate phosphine ligand (cf. J. Am. Chem. Soc. 103 (1981) 4627-4629 and 104 (1982) 3520-3522. Once again, this dimerization has to be carried out under strictly anhydrous conditions (cf. Transition metal catalyzed polymerisations; Alkenes and Dienes, Part A edited by R.P. Quirk, 1983, pp. 341-354). The present invention relates to a process for the dimerization in the liquid phase of an aliphatic mono-olefin having in the range of from 2 to 12 carbon atoms per molecule, characterized in that the dimerization is carried out in the presence of a catalytic system formed by combining, in the presence of water, an alcohol or a carboxylic acid: a) a palladium compound, b) a chelate ligand comprising an organic compound containing as coordinating atoms at least two atoms of Group 5a of the Periodic Table of the Elements which are connected through a chain comprising 2 to 6 carbon atoms, and c) a compound containing an anion of an acid, with the exception of hydrohalogenic-acids. It is an advantage of the process of the invention that the catalytic systems used therein do not require anhydrous reaction conditions. In addition high reaction rates can be achieved whilst maintaining an attractive selectivity to dimers. The selectivity to dimers is defined as the molar percentage of dimers in the product formed. Aliphatic mono-olefins having in the range of from 2 to 12 carbon atoms which can be used in the process according to the present invention are linear or branched alkenes or cycloalkenes, such as, for example, ethene, propene, l-butene, 2-butene, the isomeric pentenes, hexenes, octenes and dodecenes, cyclopentene, cyclooctene and cyclododecene. Examples of other aliphatic mono-olefins are substituted alkenes such as allyl alcohol, acrylic acid and alkylesters of acrylic acid. The preferred olefins are ethene, propene and 1-butene. The word "dimerization" as it is used herein, refers to the reaction of two identical olefins as well as the reaction of two different olefins. According to the invention, both homogeneous and heterogeneous catalytic systems can be used. The use of homogeneous catalytic systems is preferred. Palladium compounds which can be used in the process according to the invention therefore preferably comprise palladium compounds which are soluble in the reaction medium or form in situ soluble compounds therein. Examples of suitable palladium compounds are palladium nitrate, palladium sulphate, palladium halides and palladium carboxylates, preferably carboxylates of carboxylic acids having not more than 12 carbon atoms per molecule. Palladium carboxylates, in particular palladium acetate, are preferably used. Further examples of suitable palladium compounds are palladium complexes such as bis(2,4-pentanedionato)palladium, bis(picolinato)palladium, tetrakis(triphenylphosphine)palladium, tetrakisacetonitrile palladium tetrafluoroborate, bis(tri-otolylphosphine)palladium acetate, bis(triphenylphosphine)- palladium sulphate, palladium olefin complexes for instance di-V-chlorodichlorobis(ethylene)dipalladium (EPd. C2H4.Cl2]2), and di-p-chlorodichlorobis(propylene)dipalladium (EPd.C3U6.Cl 22' and palladium-hydride complexes. The quantity of the palladium compound used may vary within wide ranges and is generally in the range between 10 and 10 mol palladium compound per mol olefin starting material. A range between 10 and 10 mol palladium compound is preferred. The chelate ligand which may be used in the process according to the invention comprises an organic compound containing as coordinating atoms at least two atoms of Group 5a of the Periodic Table of the Elements which are connected through a chain comprising 2 to 6 carbon atoms. The Periodic Table of the Elements mentioned herein refers to that shown on the inside of the cover of "Handbook of Chemistry and Physics", 61st edition (1980-1981), CRC Press, Inc. Suitable compounds may be compounds containing two nitrogen atoms which are connected through a chain comprising 2 carbon atoms such as 1,2-ethanediamine compounds for example N,N,N' N'-tetramethyl-1,2-ethanediamine, N,N,N' ,N1-tetraethyl-2,2- ethanediamine and N,N,N',N'-tetraphenyl-1,2-ethanediamine, heterocyclic diamines for example 1,4-diphenylpiperazine, 1,4-dimethyl-1,4-dihydropyrazine and compounds containing in the molecule a group of the formula EMI4.1 for example N,N'-1,2-ethanediylidenebisphenylamine, N,N'-1,2 ethanediylidenebis [4-chlorophenylamine], N,N'-1,2-ethane- diylidenebis [4-methoxyphenylamine], N-substituted derivatives of 2-pyridinemethanimine, 2 ,21-bipyridyl, 4,4' dimethyl-2,2'bipyridyl, 4,4'-dichloro-2,2'-bipyridyl, 4,4'-dimethoxy-2,2'bipyridyl, l,10-phenanthroline, 5-chloro-l,l0-phenanthroline, 4, 7-diphenyl-1, 10-phenanthroline, 4,7-dimethyl-1,10- phenanthroline, 2,9-dichloro-1,10-phenanthroline, 1,10phenanthroline-5-sulphonic acid, 4,7-diphenyl-l,l0-phenan- throlinedisulphonic acid, and 3, 5-cyclohexadiene-1, 2-diimine. Other suitable compounds may be compounds containing two phosphorus atoms, or two arsenic atoms or optionally a phosphorus atom or an arsenic atom in combination with a nitrogen atom which are connected through a chain comprising 2 carbon atoms such as for example 1,2-ethanediylbisdiphenylphosphine, 1,2-ethenediylbisphenylphosphine, 1,2-ethynediyl- bisdiphenylphosphine, 1,2-ethanediylbisdi(trifluoromethyl)phosphine, 1,2-phenylenebisdiphenylphosphine, 1,2-tetra fluorocyclobutenediylbisdiphenylphosphine, 1,2-hexafluorocyclopentenediylbisdiphenylphosphine, 1,2-octafluorocyclohexenediylbisdiphenylphosphine, 1,4-diphenyl-1,4-diphosphacyclohexane, bis (o-diphenylphosphinophenyl)phenylphosphine, tris(o-diphenylphosphinophenyl)phosphine, 1,2-phenylenebisdimethylarsine, 1,2-ethanediylbisdiphenylarsine, 1-dimethylamino-2-phenyldiethylphosphine, 8-dimethylarsinoquinoline, 10-methyl-5,10dihydrophenarsazine, 1, 2-tetrafluorophenylenebisdimethylarsine. Further suitable compounds may be compounds containing at least two nitrogen atoms, phosphorus atoms or arsenic atoms connected through a chain comprising 3 to 5 carbon atoms such as for example N,N,N',N'-tetramethyl-1,3-propanediamine, N,N,N',N'-tetramethyl-1,4-butanediamine, 1,3-propanediylbisdiphenylphosphine, 1,4-butanediylbisdiphenylphosphine, bis(bis-3-dimethylarsinopropyl)arsine, tetrakis(3-dimethylarsinopropyl)o-phenylenediarsine. The compounds preferably used in the catalytic system used in the process according to the invention are 1,10-phenanthroline and the derivatives thereof, 2,2'-bipyridyl and the derivatives thereof and bisdiphenylphosphine compounds in which the two phosphorus atoms are connected through a chain comprising 2 or 3 carbon atoms. The quantity of chelate ligands used in the catalytic system is at least 0.1 mol ligand per gram atom palladium and preferably varies between 1 and 25 mol ligand per gram atom palladium. The catalytic system used in the process of the invention is further formed by a compound containing an anion of an acid, with the exception of hydrohalogenic acids. The anion is preferably a non-coordinating anion, by which is meant that little or no covalent interaction takes place between the palladium and the anion (cf. UK Patent Application No. 2,058,074). Typical examples of such anions are PF6 , SbF, , BF4 and Coo4. The anion-containing compound may be a salt or a metal complex compound containing an anion of an acid or may be the acid itself. The acid preferably has a pKa of less than 3 and, more preferably, less than 2, measured in aqueous solution at a temperature of 18 OC, Preferred compounds are those containing anions of for example sulphonic acids and acids that can be formed, possibly in situ, by interacting a Lewis acid such as, for example, BF3, AsF5, SbF5, PF5, TaF5 or NbF5 with a Broensted acid such as, for example, a hydrohalogenic acid, in particular HF, fluorosulphonic acid, phosphoric acid or sulphuric acid. Specific examples of acids of the latter type are fluorosilicic acid, HBF4,HPF6 and HSbF6. Examples of usable sulphonic acids are fluorosulphonic acid and chlorsulphonic acid and the hereinafter specified sulphonic acids. A preferred group of compounds are compounds containing anions of acids having the general formula I EMI6.1 wherein Z represents sulphur or chlorine and, if Z is chlorine, R represents oxygen and, if Z is sulphur, R represents an OH group or an optionally substituted hydrocarbon group. When the hereinbefore-stated anion-containing compounds are used in the process according to the invention, the anions of the compounds can be considered to be non-coordinating. The optionally substituted hydrocarbon group represented by R is preferably an alkyl, aryl, aralkyl or alkaryl group having 1 to 30, in particular 1 to 14, carbon atoms. The hydrocarbon group may, for example, be substituted with the halogen atoms, in particular fluorine atoms. Examples of suitable acids of the general formula I are perchloric acid, sulphuric acid, 2-hydroxypropane-2-sulphonic acid, benzenesulphonic acid, 1- and 2-naphthalenesulphonic acid, p-toluenesulphonic acid and trifluoromethanesulphonic acid, the last two acids being the most preferred. According to another embodiment of the present invention the catalytic system is formed by using a compound containing an anion of a carboxylic acid as component c). Examples of suitable carboxylic acids are formic acid, acetic acid, monochloroacetic acid, dichloroacetic acid, trichloroacetic acid and trifluoroacetic acid. Very good results have been obtained with the latter acid. The anion-containing compound is preferably used in the form of the acid itself. However, under certain conditions it is possible to use salts containing an anion of an acid, which can be exchanged with the anion of the palladium compound used. For example, AgBF4, AgSbF6 or Ag-p-toluene sulphonate can be used when the palladium compound is palladium chloride or a palladium complex compound containing chloride anions. The compound containing an anion of the acid is preferably used in a quantity in the range of from 0.01 to 150 and in particular 1 to 100 equivalents per gram atom palladium. It will be appreciated that when the catalytic system applied in the process according to the invention is formed by combining in situ a palladium compound, a chelate ligand and a compound containing an anion of an acid, a palladium complex compound with catalytic activity may be formed in the reaction mixture. An example of such a compound is palladium bis(1,10 phenanthroline)diperchlorate or ditosylate. The use of such a palladium complex compound when prepared separately as catalytic system is within the scope of the present invention. In the process of the invention the catalytic system is used in the presence of the protic solvents water, alcohol, or carboxylic acid. The alcohols or carboxylic acids may be aliphatic, cycloaliphatic or aromatic and may be substituted with one or more substituents for example alkoxy, cyano, ester groups or halogen atoms. The alcohols or carboxylic acids preferably contain not more than 20 carbon atoms per molecule. Examples of suitable alcohols are methanol, ethanol, propanol, isobutylalcohol, tert.butylalcohol, stearyl alcohol, benzyl alcohol, cyclohexanol, allyl alcohol, chlorocapryl alcohol, ethylene glycol, 1,2-propanediol, 1,4-butanediol, glycerol, polyethylene glycol, 1,6-hexanediol, phenol, cresol. Special preference is given to alcohols having 1 to 10 carbon atoms per molecule. Examples of suitable carboxylic acid solvents are acetic acid, propionic acid, butyric acid, caproic acid, trimethylacetic acid, benzoic acid, caprylic acid, succinic acid, adipic acid and hydroxycaproic acid. The amount of water, alcohol or carboxylic acid solvent used in the reaction mixture may be any amount that activates the catalytic system. Conveniently, such amounts can be used that water serves as co-solvent and the alcohol or carboxylic acid as solvent or co-solvent. The process according to the invention is carried out in the liquid phase which may comprise a liquid mixture of the olefin, the catalytic system, reaction products, water, an alcohol or a carboxylic acid and preferably a solvent or co-solvent. As stated hereinabove, water, alcohols or carboxylic acids can be used as solvent or co-solvent. Further examples of solvents and co-solvents are hydrocarbons, in particular aromatic hydrocarbons such as hexane, benzene or toluene, halogenated hydrocarbons such as chloroform, chlorobenzene or perfluoroalkanes, ketones such as acetone, diethyl ketone or methyl isobutyl ketone, ethers such as tetrahydrofuran, dimethylether of diethylene glycol (also referred to as "diglyme"), methyl t-butyl ether or 1,4-dioxane, sulphones such as dimethyl sulphone, methyl butyl sulphone, tetrahydrothiophene 1,1-dioxide (also referred to as "sulpholane") and sulphoxides such as dimethyl sulphoxide or diethyl sulphoxide. The liquid phase may comprise a two-phase liquid system. For example when ethene or propene is dimerized using a diol as solvent, the dimerization product may form a separate layer which can be easily separated from diol solvent containing the catalytic system. The process according to the present invention can be carried out at temperatures of up to 200 OC and preferably in the range between 20 "C and 135 OC. The pressure preferably lies between 1 and 100, in particular between 20 and 75, bar gauge. The process according to the invention can be carried out batchwise, semi-continuously or continuously. The reaction time may vary in relation to the temperature used, between 0.5 and 20 hours. The following Examples further illustrate the invention. The Examples 2-9 and Comparative Experiment A were carried out as described for Example 1 except for the catalytic system. The results are presented in Table I. Example 1 A 300 ml magnetically stirred Hastelloy C autoclave ("Hastelloy" is a trade mark) was charged with 50 ml methanol and a catalytic system formed by combining 0.1 mmol of palladium acetate, 0.15 mmol of 1.3-propanediylbisdiphenylphosphine and 2 mmol of p-toluenesulphonic acid. The autoclave was flushed with ethene, filled with ethene at a pressure of 40 bar, sealed and heated to a temperature as indicated in Table I. After a reaction time as indicated in Table I the contents of the autoclave were analyzed by gas/liquid chromatography. The conversion of ethene to products (dimers, trimers, etc.) was calculated as mol of ethene per gram atom palladium per hour. Example 2 The catalytic system was formed by combining 0.5 mmol palladium acetate, 1 mmol 1,10-phenanthroline and 10 mmol acetic acid. Example 3 The catalytic system was formed by combining 0.5 mmol palladium acetate, 1 mmol 1,10-phenanthroline and 2 mmol monochloroacetic acid. Example 4 The catalytic system was formed by combining 0.5 mmol palladium acetate, 1 mmol 1,10-phenanthroline and 2 mmol dichloroacetic acid. Example 5 The catalytic system was formed by combining 0.5 mmol palladium acetate, 1 mmol 1,10-phenantroline and 2 mmol trifluoroacetic acid. The selectivities to trimers and tetramers were 25X and 2%, respectively. Example 6 As catalytic system was added a composition of'palladium complex compounds containing 0.1 mgram atom palladium. The composition was prepared as follows: Palladium acetate was dissolved in methanol and 3 mol of p-toluenesulphonic acid per gram atom palladium and 1.5 mol of 1,3-propanediylbisdiphenylphosphine per gram atom palladium were added. The resulting precipitate was isolated by filtration and washed with methanol. Comperative Experiment A As catalytic system was added a composition prepared analogously to the composition of Example 6 except that 3 mol of HC1 (11 N) was used instead of 3 mol of p-toluenesulphonic acid. Example 7 As catalytic system were added 0.1 mmol of palladium acetate, 2 mmol of 2,2'-bipyridyl and 1 mmol of p-toluenesulphonic acid. Example 8 As catalytic system were added 0.1 mmol of palladium acetate, 2 mmol of 1,10-phenanthroline and 1 mmol of p-toluenesulphonic acid. Example 9 As catalytic system was added a composition prepared analogously to the composition of Example 6 except that 2 mol of l,10-phenanthroline per gram atom palladium was used instead of 1.5 mol of 1,3-propanediylbisdiphenylphosphine. TABLE I Comparative Example Temp, Time, Conversion Selectivity Experiment No. C h mol/gr.at Pd/h to dimer %mol 1 95 0.5 6000 98 2 75 5 120 3 75 5 200 4 75 5 300 5 75 0.16 5600 73 6 95 0.5 6000 98 7 75 0.5 8000 85 8 90 1 5000 93 9 95 2 2400 95 A 115 5 70 100 Comparative Experiment A, not according to the invention, shows that a high conversion is not achieved in the presence of chloride anions. Example 10 A 300 ml magnetically stirred Hastelloy C autoclave ("Hastelloy" is a trade mark) was charged with 50 ml diglyme, 5 ml water and as catalytic system 0.1 mmol of palladium acetate, 2 mmol of 2,2'-bipyridyl and 2 mmol of p-toluenesulphonic acid. The autoclave was flushed with ethene, filled with ethene at a pressure of 40 bar, sealed and heated to 90 OC. After a reaction time of 1 hour the contents of the autoclave were analyzed by gas/liquid chromatography. The conversion of ethene to dimers and trimers was calculated as 2800 mol of ethene per gram atom palladium per hour. Butenes were present in an amount of 93 %mol in the product. Comparative Experiment B The experiment of Example 10 was repeated except that no water was present and that the autoclave was heated to 120 C during 5 hours. On analysis only traces of butenes were found, showing that the catalytic system effects dimerization in the presence of water as protic compound. Example 11 A 300 ml magnetically stirred Hastelloy C autoclave ("Hastelloy" is a trade mark) was charged with 35 ml phenol and as catalytic system 0.1 mmol of palladium acetate, 4 mmol of 2,2'-bipyridyl and 4 mmol of p-toluenesulphonic acid. The autoclave was flushed with ethene and filled with ethene at a pressure of 40 bar, sealed and heated to 80 OC. After a reaction time of 5 hours the contents of the autoclave were analyzed by gas / liquid chromatography. The conversion of ethene to dimers and trimers was calculated as 800 mol of ethene per gram atom palladium per hour. Butenes were present in an amount of 90 Zmol in the product. Example 12 A 300 ml magnetically stirred Hastelloy C autoclave ("Hastelloy" is a trade mark) was charged with 50 ml acetic acid and as catalytic system 0.1 mmol of palladium acetate, 0.15 mmol of 1,3-propanediylbisdiphenylphosphine and 2 mol of trifluoromethanesulfonic acid. The autoclave was flushed with ethene and filled with ethene at a pressure of 40 bar, sealed and heated to 135 "C. After a reaction time of 5 hours the contents of the autoclave were analyzed by gas/liquid chromatography. The conversion of ethene to dimer products (butene 40 Zmol and sec.butyl acetate 60 %mol) was calculated as 500 mol of ethene per gram atom palladium per hour. The selectivity to dimer products was 100 %mol. Examples 13-19 A 300 ml magnetically stirred Hastelloy C autoclave ("Hastelloy" is a trade mark) was charged with a solvent and as catalytic system palladium acetate, a bidentate ligand and an acid with a pKa < 2. The autoclave was flushed with propene, filled with propene in the liquid phase at 30 bar in a quantity of 50 ml, sealed and heated to a certain temperature. After a certain reaction time the contents of the autoclave were analyzed by gas/liquid chromatography. The conversion of propene to products was calculated as mol of propene per gram atom palladium per hour. The selectivity to the dimers is given as Zmol of dimer in the products formed. The linearity of the dimer products is determined by NMR and is given as %mol of linear hexenes in the dimer products. Data and results of the examples 13-19 carried out according to the above are mentioned in Table II. TABLE II Example Palladium Bidentate Acid pKa < 2 Solvent Reaction Temp. Conversion Selectivity Linearity No. acetate ligand time mmol mmol mmol ml ml h C m/g at Pd/h %mol %mol 13 0.2 2,2'bipyridyl p-toluenesul- methanol 2 85 1050 98 65 (4) phonic acid (50) (6) 14 0.5 1,10-phenan- p-toluenesul- butanediol 1 75 1250 94 60 throline phonic acid -(1.4) (1) (1.5) (50) 15 0.5 2,2'bipyridyl p-toluenesul- ethylene 1 75 1100 95 58 (1) phonic acid glycol (1.5) (50) 16 0.5 1,10-phenan- sulphuric acid diethylene 1 70 1050 > 95 60 throline (1.5) glycol (1) (50) 17 0.5 1,10-phenan- HBF4 diethylene 1/4 70 4000 > 95 59 throline (3)4 glycol (1) (50) 18 0.5 4,7-diphenyl- trifluoro- ethylene 1/2 75 1800 > 95 60 1,10-phenan- methane- glycol throline sulphuric acid (50) (1) (1.5) 19 0.5 5-chloro-1,10-naphtalene- diethylene 1 75 930 > 95 59 phenanthroline sulphonic acid glycol (1) (2) (50) Example 20 A 300 ml magnetically stirred Hastelloy C autoclave ("Hastelloy" is a trade mark) was charged with 50 ml 1,4-butanediol and as catalytic system 0.5 mmol of palladium acetate, 1 mmol of 1,10-phenanthroline and 1.5 mmol p-toluenesulphonic acid. The autoclave was flushed with l-butene and filled with l-butene in the liquid phase at 30 bar in a quantity of 60 ml and heated to 75 C. After a reaction time of 5 hours the contents of the autoclave were analyzed by gas/liquid chromatography. The conversion of l-butene to dimers was calculated as 30 mol of 1-butene per gram atom palladium per hour. Dimers were the only products. Example 21 A 300 ml magnetically stirred Hastelloy C autoclave ("Hastelloy" is a trade mark) was charged with 50 ml methanol and as catalytic system 1 mmol of palladium acetate, 2 mmol of 2,2'-bipyridyl and 2.5 mmol p-toluenesulphonic acid. The autoclave was flushed with propene and filled with propene and l-butene in the liquid phase at 30 bar in a quantity of 50 ml and 60 ml, respectively, and heated to 65 "C. The conversion to dimer product was calculated as 800 mol of propene and butene per gram atom palladium per hour. The selectivity to dimers was 100 %mol. The composition of the dimer products was hexenes 69 %mol, heptenes 28 %mol and octenes 3 Zmol.

Claims: CLAIMS 1. A process for the dimerization in the liquid phase of an aliphatic mono-olefin having in the range of from 2 to 12 carbon atoms per molecule, characterized in that the dimerization is carried out in the presence of a catalytic system formed by combining, in the presence of water, an alcohol, or a carboxylic acid:a) a palladium compound, b) a chelate ligand comprising an organic compound containing as coordinating atoms at least two atoms of Group 5a of the Periodic Table of the Elements which are connected through a chain comprising 2 to 6 carbon atoms, and c) a compound containing an anion of an acid, with the exception of hydrohalogenic acids. 2. A process as claimed in claim 1, characterized in that the acid mentioned in c) has a pKa of less than 3, measured in aqueous solution at a temperature of 18 "C. 3. A process as claimed in claim 2, characterized in that the acid has a pKa of less than 2. 4. A process as claimed in any one of the preceding claims, characterized in that as anion a non-coordinating anion is used. 5. A process as claimed in any one of the preceding claims, characterized in that the compound containing an anion of an acid contains the anion of an acid of the general formula I EMI16.1 wherein Z represents sulphur or chlorine and, if Z is chlorine, R represents oxygen and, if Z is sulphur, R represents an OH group or an optionally substituted hydrocarbon group. 6. A process as claimed in claim 5, characterized in that the hydrocarbon group R is an alkyl, aryl, aralkyl or alkaryl group having 1 to 30 carbon atoms. 7. A process as claimed in claim 5 or 6, characterized in that the anion of an acid of the general formula I is the anion of p-toluenesulphonic acid. 8. A process as claimed in any one of claims 1 to 4, characterized in that the acid mentioned in c) is trifluoroacetic acid. 9. A process as claimed in any one of the preceding claims, characterized in that the compound containing an anion of an acid is used in the form of the acid itself. 10. A process as claimed in any one of the preceding claims, characterized in that the chelate ligand comprises a compound containing as coordinating atoms 2 nitrogen atoms connected through a chain comprising 2 carbon atoms. 11. A process as claimed in claim 10, characterized in that the chelate ligand comprises a compound containing in the molecule a group of the formula EMI17.1 12. A process as claimed in claim 10 or 11, characterized in that the chelate ligand comprises l,10-phenanthroline or a derivative thereof. 13. A process as claimed in claim 10 or 11, characterized in that the chelate ligand comprises 2,2'-bipyridyl or a derivative thereof. 14. A process as claimed in any one of claims 1 to 9, characterized in that the chelate ligand comprises a compound containing as coordinating atoms 2 phosphorus atoms connected through a chain comprising 2 or 3 carbon atoms. 15 A process as claimed in claim 14, characterized in that the chelate ligand comprises bisdiphenylphosphine compounds in which the phenyl groups are optionally substituted. 16. A process as claimed in claim 14 or 15, characterized in that the chelate ligands comprises 1,3-propanediylbisdiphenylphosphine. 17. A process as claimed in any one of the preceding claims, characterized in that the quantity of the chelate ligand varies between 1 and 25 mol ligand per gram atom palladium. 18. A process as claimed in any one of the preceding claims, characterized in that the compound containing an anion of an acid is used in a quantity in the range of from 1 to 100 equivalents per gram atom palladium. 19. A process as claimed in any one of the preceding claims, characterized in that water is used as a co-solvent. 20. A process as claimed in any one of claims 1 to 18, characterized in that an alcohol is used as solvent or co-solvent.

Inventors: DRENT, EIT
Applicants: SHELL INTERNATIONALE RESEARCH MAATSCHAPPIJ B.V.
Application year: 1985
Main classification: C07C2
IPC codes: B01J31, C07C2