VINYL CHLORIDE POLYMER RESIN COMPOSITION

Abstract: A vinyl chloride polymer resin composition having ex­ cellent processability and flowability is comprised of (A) 100 weight parts of a vinyl chloride polymer composition com­ prising 5 to 100 weight % of a vinyl chloride polymer having an average polymerization degree of 300 to 700 and 95 to 0 weight % of a vinyl chloride polymer having an average molecular weight higher than 700, and (B) 0.1 to 30 weight parts of a methyl methacrylate polymer comprised of at least 40 weight % of methyl methacrylate and having a re­ duced viscosity (ηsp/C) of 0.1 to 2ℓ/g.

Description: The present invention relates to a vinyl chloride polymer resin composition having excellent processability and flowability, which comprises a vinyl chloride polymer having a low degree of polymerization. A vinyl chloride polymer resin has excellent chemical and physical properties but, as is well known, this resin has poor heat stability, impact resistance and processability. Various methods have been proposed for overcoming these defects. More specifically, various heat stabilizers have been developed for improving the heat stability and various impact modifiers have been developed for improving the impact resistance. These additives have been used by incorporation into vinyl chloride polymer resins. As an agent for improving the processability, there has been proposed a high-molecular weight acrylic polymer processing aid. Namely, the incorporation of a small amount of this processing aid in a vinyl chloride polymer resin can improve the processability of the vinyl chloride polymer resin, for such processes as calendering, vacuum forming or injection molding (Japanese Patent Publication No. 40-5311). The Chapter 7 "Hochpolymere PVC-Verarbeitungshilfsmittel" of "Taschenbuch der Kunststoffadditive", (R. Gächer und H. Müller Ed.), Wien 1979, pages 275 bis 294, general refers to processing aids based on polymethyl methacrylate. These processing aids having a specific viscosity of from 0.05 to 0.6 l/g depending on their molecular weight are used in processing polyvinyl chloride. In chapter 7.2.5.1 and 7.3.2.2 of the above handbook processing aids having a reduced viscosity of 0.05 to 0.13 l/g are recommended for injection moulding. Processing aids having higher polymerisation degrees are reported to increase the viscosity of PVC melts. The GB-A- 981 116 discloses a PVC-composition comprising a polymer of vinylchloride having a K-value of 55 according to a polymerisation degree of 700 and an amount of an acrylic polymer which is a polymer of methyl methacrylate having a reduced viscosity of at least 3. The DE-A-2 014 851 describes a PVC-composition having a polymerization degree of 600 to 1000 comprising at least one polymer of vinyl chloride, and a copolymer of an unsaturated nitril, methyl methacrylate and alkyl acrylate having a viscosity of from 0.4 to 2 l/g. The GB-A-2 017 111 discloses a vinyl chloride resin composition containing a vinyl chloride polymer having a polymerisation degree of 700 and a processing aid comprising a copolymer of an alkyl methacrylate and dialkyl itaconate and as required an alkyl methacrylate copolymerizable with one or more monomers. The non-prepublished EP-A- 123 711 deals with a PVC-composition comprising a PVC having a polymerization degree of 680 and a polymer which is obtained by polymerizing a mixture composed of styrene monomer and an alkyl ester of methacrylic acid in the presence of methyl methacrylate polymer having a specific viscosity of lower than 0.6 l/g. However where a vinyl chloride resin composition is prepared by incorporating this high-molecular weight acrylic polymer processing aid into a commercially available vinyl chloride polymer resin having a high degree of polymerization, the melt viscosity is drastically increased, even though the amount of the processing aid added is small, and the kneading lead in a molding machine is extremely increased. Moreover, since the resin molding temperature must be elevated, the resin is thermally degraded and it is difficult to continue the processing for a long time. The above problem becomes prominent, especially when the processing temperature is high and the processing is performed at a high speed. As means for overcoming this disadvantage, there may be considered a method for improving the flowability by adding a liquid substance such as a plasticizer, but here reduction of the physical properties and processability cannot be avoided. Also in the field of vinyl chloride polymer resins having a low degree of polymerization, development of a product having a good processability is desired but a satisfactory product has not been developed. Object of the present invention is to provide a vinyl chloride polymer resin composition having excellent processability and flowability, comprising a vinyl chloride polymer having a low degree of polymerization. In accordance with the present invention, there is provided a vinyl chloride polymer resin composition having excellent processability and flowability, which comprises (A) 100 parts by weight of a vinyl chloride polymer composition selected from the group consisting of a homopolymer of vinyl chloride having an average polymerisation degree of 400 to 500 according to K-values of 49 to 52, and a polymer mixture consisting of 80 to 20 % by weight of a homopolymer of vinyl chloride having an average polymerisation degree of 400 to 500 according to K-values of 49 to 52, and 20 to 80 % by weight of a homopolymer of vinyl chloride having an average polymerisation degree of 800 to 1000, and (B) 0.1 to 30 parts by weight of a methyl methacrylate polymer, exclusive of the graft-type methacrylate polymers, comprised of at least 40 % by weight methyl methacrylate units and having a reduced viscosity of 0.15 to 2 l/g as measured at 25 o C with respect to a solution of 0.1 g of the polymer dissolved in 100 ml chloroform. Any vinyl chloride polymers prepared by emulsion polymerization, suspension polymerization or bulk polymerization may be used in the present invention. It has been found that the vinyl chloride polymer composition provided by the invention has excellent flowability and processability characteristics for such processes as calendering, blow molding, vacuum forming injection molding and low-expansion molding while retaining the inherent good chemical and physical properties of the vinyl chloride polymer. The numerical relationship among the average polymerization degree, Fikentscher K-value and average molecular weight of vinyl chloride polymers is as shown in Table 1, below. The methyl methacrylate polymer used in the present invention should have a methyl methacrylate unit content of at least 40 % by weight, and it includes a homopolymer of methyl methacrylate, a copolymer of methyl methacrylate with other vinyl monomer copolymerizable therewith and a mixture thereof. The vinyl monomer copolymerizable with methyl methacrylate may be copolymerized in an amount of up to 60% by weight. Specific examples of the vinyl monomer are alkyl acrylates such as methyl acrylate, ethyl acrylate, butyl acrylate and 2-ethylhexyl acrylate, alkyl methacrylates such as ethyl methacrylate and butyl methacrylate, aromatic vinyl compounds such as styrene, α-methylstyrene and vinyltoluene, and vinylcyano compounds such as acrylonitrile and methacrylonitrile. These vinyl monomers may be used alone or in the form of a mixture of two or more thereof. If the amount of the monomer copolymerized with methyl methacrylate exceeds 60% by weight, the compatibility of the resulting copolymer with the vinyl chloride polymer composition used in the present invention is readily lowered and the physical properties and processability of the resulting vinyl chloride polymer resin composition are reduced. Preferably, the methyl methacrylate polymer used in the present invention is a copolymer comprising 95 to 70% by weight of methyl methacrylate and 5 to 30% by weight of ethyl acrylate or butyl acrylate. In the present invention, the methyl methacrylate polymer exclusive of the graft type methacrylate polymers has a reduced viscosity (ηsp/C) of 0.15 to 2 ℓ/g, preferably, 0.3 to 0.4 ℓ/g, as measured at 25°C with respect to a solution of 0.1 g of the polymer in 100 ml of chloroform. If the reduced viscosity (ηsp/C) is lower than 0.15 ℓ/g, it is difficult to attain the intended improvement of the processability. If the reduced viscosity exceeds 2 ℓ/g, the melt viscosity of the resin composition formed by incorporating the methyl methacrylate polymer into the vinyl chloride polymer composition is too high and it is difficult to attain the good flowability intended in the present invention. Any methyl methacrylate polymers prepared by emulsion polymerization, suspension polymerization and bulk polymerization may be used in the present invention. The numerical relation between the reduced viscosity (ηsp/C) and viscosity average molecular weight of the methyl methacrylate polymers used in the present invention is as shown in Table 2. ηsp/C Viscosity average molecular weight 0.05 85,000 0.1 200,000 0.25 476,000 0.3 568,000 0.4 730,000 1.0 1,680,000 2.0 2,920,000 2.2 3,130,000 The viscosity average molecular weight is calculated according to the following Schulz formula: In the above formula, the intrinsic viscosity [η] is calculated according to the following formula: The vinyl chloride polymer resin composition of the present invention is formed by incorporating 0.1 to 30 parts by weight, preferably 1 to 10 parts by weight of the methyl methacrylate polymer exclusive of the graft-type methacrylate polymers having a reduced viscosity (ηsp/C) included within the above-mentioned range into 100 parts by weight of the above-mentioned vinyl chloride polymer composition. If the amount of the methyl methacrylate polymer is smaller than 0.1 part by weight, it is difficult to obtain a sufficient high-temperature elongation when vacuum forming the resulting resin composition and it is also difficult to obtain a molded article having an excellent cell uniformity and appearance when low-expansion molding is carried out. Thus, the intended effect of improving the processability would not be attained. If the amount of the methyl methacrylate polymer exceeds 30 parts by weight, increase of the melt viscosity of the resin composition is extreme and it becomes difficult to obtain the intended effect of improving the flowability. If desired, in addition to additives such as a heat stabilizer, a light stabilizer, a lubricant and a filler, an impact modifier and a heat distortion temperature improver such as a chlorinated vinyl chloride polymer resin also may be added to the vinyl chloride polymer resin composition of the present invention according to need. The present invention will now be described in detail with reference to the following examples that by no means limit the scope of the invention as claimed. In the examples and comparative examples, all of "parts" and "%" are by weight. Examples 1 through 4 and Comparative Examples 1 through 3 A reaction vessel equipped with a stirrer was charged with 250 parts of distilled water, 1 part of potassium oleate, 0.5 part of potassium persulfate and the amounts shown in Table 3 of monomers constituting a methyl methacrylate polymer and tert-dodecylmercaptan. Polymerization was carried out at 60°C for 5 hours. The latex obtained by the reaction was coagulated, washed and then dried to obtain a methyl methacrylate polymer having a reduced viscosity as shown in Table 3. The obtained methyl methacrylate polymer was added in an amount shown in Table 3 to a vinyl chloride polymer resin shown in Table 3. Furthermore, 3 parts of tribasic lead sulfate, 1 part of tribasic lead stearate, 1.5 parts of lead stearate and 1 part of calcium stearate were added to the polymer resin mixture. The resin composition was molded into a square plate specimen, having a size of 10 cm x 10 cm x 3 mm (thickness), by a 5-ounce injection molding machine. The flowability and injection moldability of the specimen were evaluated. The obtained results are shown in Table 3. The flowability was evaluated based on the minimum injection pressure (short shot pressure) under which the mold was just filled with the resin. The injection moldability was evaluated based on the degree of a meandering pattern, that is, so-called jetting, generated from the gate under an injection pressure corresponding to the short shot pressure plus 2,04·10³ Pa (2 kg/cm²). As is apparent from the results shown in Table 3, resin compositions falling within the scope of the present invention exhibit excellent flowability and injection moldability. In contrast, in the resin composition of Comparative Example 1, since the reduced viscosity of the methyl methacrylate polymer is too high, the short shot pressure must be high and continuous molding is difficult. Furthermore, in the composition of Comparative Example 2, the short shot pressure is high because a vinyl chloride polymer resin having an average polymerization degree of 1000 is used alone, and thus undesirable jetting is caused. In Comparative Example 3, undesirable jetting is caused because the reduced viscosity of the methyl methacrylate polymer is too low. Examples 5 through 9 and Comparative Examples 4 through 6 Polymerization was carried out according to the same recipe as in Examples 1 through 4 except that monomers constituting a methyl methacrylate polymer were used in the amounts shown in Table 4, whereby a methyl methacrylate polymer having a reduced viscosity shown in Table 4 was obtained. The obtained methyl methacrylate polymer was added in an amount shown in Table 4 to a vinyl chloride polymer resin having a degree of polymerization shown in Table 4. In addition, 10 parts of Metablen C-201 (registered trademark of a product supplied by Mitsubishi Rayon K.K.) as an impact modifier, 2 parts of dibutyltin mercaptide, 0.5 part of butyl stearate and 0.5 part of montanic acid wax were added to the mixture. The resulting composition was extruded into a sheet having a thickness of 3 mm by an extruder having a screw diameter of 40 mm. The flowability and vacuum forming processability of the sheet were evaluated. The flowability was evaluated based on the load on a motor of the extruder having a screw diameter of 40 mm. The vacuum forming processability was evaluated based on the elongation at break of the extruded sheet at 100°C. As is apparent from the results shown in Table 4, for compositions falling within the scope of the present invention, the motor load is small at the extruding step and the flowability is excellent. In view of the elongation at break, these resin compositions have a good vacuum forming processability. In contrast, in Comparative Example 4, since the average polymerization degree of the vinyl chloride polymer resin is high, even if the methyl methacrylate polymer falling within the scope of the present invention is incorporated into this vinyl chloride polymer resin, the motor load is excessively large at the extruding step. In Comparative Example 5, since the reduced viscosity of the methyl methacrylate polymer is too low, a good vacuum forming processability cannot be attained. In Comparative Example 6, since the amount of the methyl methacrylate polymer incorporated is too large, the motor load of the extruder is extremely large. Examples 10 through 13 and Comparative Examples 7 and 8 Polymerization was carried out according to the same recipe as in Examples 1 through 4 except that the kinds and amounts of the monomers constituting the methyl methacrylate polymer were changed as shown in Table 5, whereby a methyl methacrylate polymer having a reduced viscosity as shown in Table 5 was obtained. The obtained methyl methacrylate polymer was incorporated into a vinyl chloride polymer resin having a polymerization degree shown in Table 3, 10 parts of Metablen C-201 (registered trademark of a product supplied by Mitsubishi Rayon K.K.), 2 parts of dibutyltin mercaptide, 0.5 part of butyl stearate and 0.5 part of montanic acid wax were added to the mixture. The resulting resin composition was treated by 20,32 cm (8-inch) test rolls, whereby the adaptability to the production of a thick film by calendering was evaluated. In order to prepare a thick film, it is ordinarily necessary to broaden the space between rolls, and therefore, rotation of the roll bank becomes insufficient and flow marks become conspicuous. Moreover, since the pressure between rolls is reduced, removal of air becomes insufficient and air bubbles are readily included in the resulting sheet. At the present test, the roll distance was maintained at 0.8 mm while the temperature was maintained at 190°C, and the rotation numbers of the front and back rolls were adjusted to 14 rotations per minute and 16 rotations per minute, respectively. The state of the roll bank and the state of formation of air bubbles in the obtained sheet were examined. The obtained results are shown in Table 5. In Examples 10 through 13, the bank was pencil bank and rotated smoothly, and no air bubbles were found in the sheet. In Comparative Example 7, although the bank was smoothly rotated, removal of air was insufficient and many air bubbles were formed. In Comparative Example 8, the bank waved and a large quantity of air was enfolded, and a sheet having a good quality could not be obtained. According to the present invention, by adopting the above-mentioned structure, there can be provided a vinyl chloride polymer resin composition excellent in processability and flowability. The composition of the present invention can be used for the production of films, sheets and plates by the process including vacuum forming, the production of large-size injection molded articles for which a high flowability is required, or for the production of low-expanded thick extrudates by calendering.

Claims: A vinyl chloride polymer resin composition which comprises (A) 100 parts by weight of a vinyl chloride polymer composition consisting of a homopolymer of vinyl chloride having an average polymerisation degree of 400 to 500 according to K-values of 49 to 52, or a polymer mixture consisting of 80 to 20 % by weight of a homopolymer of vinyl chloride having an average polymerisation degree of 400 to 500 according to K-values of 49 to 52 and 20 to 80 % by weight of a homopolymer of vinyl chloride having an average polymerisation degree of 800 to 1000 according to K-values of 60 to 65, and (B) 0.1 to 30 parts per weight of a methyl methacrylate polymer, exclusive of the graft type methacrylate polymers, comprised of at least 40 % by weight of methyl methacrylate units and having a reduced viscosity (η sp /c) of 0.15 to 2 l/g as measured at 25°C with respect to a solution of 0.1 g of the polymer dissolved in 100 ml of chloroform. A vinyl chloride polymer resin composition according to claim 1 wherein the methyl methacrylate polymer is comprised of 70 to 95 % by weight of methyl methacrylate units and 5 to 30 % by weight of units derived from ethyl acrylate or butyl acrylate. A vinyl chloride polymer resin composition according to claim 1 wherein the methyl methyacrylate polymer has a reduced viscosity (η sp /c) of 0.3 to 0.4 l/g. A vinyl chloride polymer resin composition according to claim 1 wherein the amount of the methyl methacrylate polymer is 1 to 10 % by weight based on 100 parts by weight of the vinyl chloride polymer composition (A).

Inventors: OKANO, KENJI
Applicants: MITSUBISHI RAYON CO., LTD.
Application year: 1985
Main classification: C08L27
IPC codes: C08L33, C08L27, C08J5, C08L1