PROCESS FOR PREPARING POLYMER POLYAHLS

Abstract: Process for preparing a polymer polyahl comprising polymerizing an ethylenically unsaturated monomer or mixtures thereof in a polyahl or polyahl mixture whereby a dispersion of polymer particles is prepared in a continuous polyahl phase. The process is characterized by conducting said polymerization in the presence of a triiodomethyl compound. The use of the triodomethyl compound provides a lower viscosity, more stable polymer polyahl.

Description: PROCESS FOR PREPARING POLYMER POLYAHLS This invention relates to a graft polymer dispersion prepared by the polymerization of an ethyleni¬ cally unsaturated monomer or mixtures thereof in a polyahl (hereinafter "polymer polyahl" or "copolymer polyahl"). More particularly, the invention relates to an improved process for preparing said copolymer polyahl In recent years it has been known to prepare polymer dispersions in a polyahl mixture. In such dispersions, a polymer of an ethylenically unsaturated monomer or mixture of monomers is dispersed in a po'-lyahl or mixture thereof. The dispersed polymer is normally grafted to the polyahl through some unsaturation in -the polyahl. Such unsaturation is commonly introduced into the polyahl by reaction thereof with a small amount of an unsaturated acid, or acid anhydride such as fumaric or aleic acid, or their anhydrides or more recently, isocyanatoethylmethacrylate (IEM). In these copolymer polyahls, the polyahl makes up a continuous phase into which the copolymer is dispersed as a plurality of small particles. These copolymer polyahls have found great utility in the production of diverse polyurethanes. In particular, the use of copolymer polyahls in preparing polyurethanes has been found to improve the process- ability of the polyurethane, as well as physical proper¬ ties such as load bearing or modulus. It is often desirable to provide a copolymer polyahl with as high a dispersed phase content as possible. However, it has heretofore been difficult to prepare and/or use copoly- mer polyahl containing more than about 35 to 40 percent by weight dispersed phase. A high concentration of dispersed phase greatly increases the viscosity of the copolymer polyahl. When the viscosity exceeds about 6500 cps (6.5 Pa*s), it is usually too viscous to be pumped using conventional urethane molding and/- or foaming equipment. With conventional copolymer polyahl, a viscosity of 6500 cps (6.5 Pa*s) is usually reached at a dispersed phase concentration of 35 to 40 percent or lower. Even at a lower dis- persed phase concentration, it is normally preferred to have a viscosity as low as possible to ease the handling of the copolymer polyahl. Another problem associated with high dis¬ persed phase concentrations is that the stability of the dispersed phase is greatly reduced as the dis- • persed phase concentration exceeds about 35 to 40 percent. At higher dispersed phase ' concentration (higher solids), the copolymer particles tend to coalesce and phase separate. The phase separation of the copolymer greatly impairs the utility of the copolymer polyahl and polyurethane prepared therewith. Yet another common disadvantage of conven¬ tional copolymer polyahls is that in order to provide a stable copolymer dispersion one must introduce substantial amounts of unsaturation into the polyahl through which to graft the dispersed phase. It is generally easier and cheaper to prepare copolymer polyahl having smaller amounts of unsaturation in the polyahl. It is known to prepare copolymer polyahls by polymerizing ethylenically unsaturated monomers in the presence of the polyahl and a chain transfer agent. The chain transfer agent is used in the preparation of copolymer polyahls in a manner analogous to the use thereof in conventional polymerizations, that is, to control the molecular weight distribution of the polymer. However, the choice of chain transfer agent. has not heretofore been attributed to significant improvements in the properties of the copolymer polyahl. In addition, the use of triiodomethyl compounds in making copolymer polyahls has not heretofore been known. In view of the aforementioned deficiencies of previously known copolymer polyahls, it would be desirable to provide a copolymer polyahl that exhibits high stability and an acceptable viscosity of a high dispersed phase content, or a lower viscosity at an equivalent dispersed phase content than exhibited by a conventional copolymer polyol. This invention is a process for prepar¬ ing a polymer polyahl comprising polymerizing an ethylenically unsaturated monomer or mixture thereof in a polyahl or polyahl mixture whereby a dispersion of polymer particles is prepared in a continuous polyahl phase, characterized by conducting said polymerization in the presence of a triiodomethyl compound. With the process of this invention, it is possible to prepare copolymer polyahls having a solids content up to 45 percent or more, and which have viscosi¬ ties such that they are processable using conventional polyurethane molding and/or foaming equipment. At a given dispersed phase content, the copolymer polyahl of the invention have a lower viscosity than like copoly¬ mer polyahl prepared in the absence of triiodomethyl compound. Moreover, the copolymer polyahl prepared according to this invention exhibits greater stability, i.e., a smaller tendency for the dispersed particles to agglomerate, than conventionally prepared copolymer polyahl-, and has good- flame retardant properties. The polymerization of monomers in the polyahl or polyahl mixture is conducted in the presence of a triiodomethyl compound as represented by the structure R-CI 3 wherein R is hydrogen, halogen including iodine, or an inertly substituted organic group. In the triiodomethyl compound, when the group R is an organic group, it can be aliphatic, aromatic or aromatic-substituted aliphatic. The group R may further contain substituent groups which do not adversely affect the activity of the triiodocompound or interfere with the subsequent reaction of the copolymer polyahl with a polyisocyanate or polyisothiocyanate to form a polyurethane or polyurea polymer. Exemplary such inert substituent groups include halogens, ether, thioether, and carbonyl groups. Preferably, however, the group R, when it is an organic radical, is lower alkyl, especially methyl or ethyl, or phenyl or benzyl. More preferably, R is a halogen atom, espe¬ cially iodine, and is most preferably hydrogen. Most preferred are 1,1,1-triiodoethane, iodo orm and tetraiodomethane. The triiodomethyl compound is employed in an amount sufficient to provide improved stability to the copolymer polyahl of this invention. .Preferably, the triiodomethyl compound is employed in an amount typical -for chain transfer agents, i.e. from 0.05 to 5, more preferably from 0.2 to 1.0, percent by weight of the monomers to be polymerized. The triiodomethyl com¬ pound may be added batchwise to the polyahl at the beginning of the polymerization of the ethylenically unsaturated monomer. However, if present in too great a concentration, the triiodomethyl compound may inhibit the polymerization reaction. Thus, it may be desirable to add the triiodomethyl compound incrementally or continuously during the polymeriza- • tion reaction in order to maintain optimum amounts thereof of all time during the reaction. In the process of this invention, one or more ethylenically unsaturated monomers are polymer¬ ized in a polyahl or polyahl mixture. The polyahl or polyahl mixture preferably contains a quantity of graft polymerization sites. As discussed more fully hereinafter, such graft polymerization sites are usually sites of ethylenic unsaturation which may be formed in the production of the polyahl or purposefully introduced into the polyahl as described hereinafter. The term "polyahl" as used herein, includes any polyfunctional compound having at least two active hydrogen atoms. For the purposes of this invention, an active hydrogen moiety refers to a moiety containing a hydrogen atom which, because of its position in the molecule, displays significant activity according to the Zerewitnoff test described by Woller in the Journal of American Chemical Society, Vol. 49, page 3181 (1927). Illustrative of such active hydrogen moieties are -COOH, -OH, -NH 2 , -NH-, -CONH 2 , -SH and -CONH-. Typical polyahls include polyό ' ls, polyamines, poly- amides, polymercaptans and polyacids . Of the foregoing polyahls, the polyols are preferred. Examples of such polyols are the polyol polyethers, the polyol polyesters, hydroxy functional acrylic polymers, hydroxyl-containing epoxy resins, polyhydroxy terminated polyurethane polymers, poly- hydroxyl-containing phosphorus ' compounds and alkylene oxide adducts of polyhydric thioethers including poly- thioethers, acetals including polyacetals, polyalkylene carbonates polyols, aliphatic and aromatic polyols and thiols including polythiols, ammonia and amines includ¬ ing aromatic, aliphatic and heterocyclic amines includ- ing polyamines as well as mixtures thereof. Alkylene oxide adducts of compounds which contain two or more different groups within the above-defined classes may also be used such as amino alcohols which contain an amino group and a hydroxyl group. Also, alkylene adducts of compounds which contain one -SH group and one -OH group as well as those which contain an amino group and a -SH group may be used. Polyether polyols which are most advantage¬ ously employed as the polyahl in the practice of this invention are the polyalkylene polyether polyols including the polymerization products of alkylene oxides and other oxiranes with water or polyhydric alcohols having from two to eight hydroxyl groups . Exemplary alcohols that are advantageously employed in making the polyether polyol include ethylene glycol, 1,3-propylene glycol, 1,2-propylene glycol, 1,4- -butylene glycol, 1,3-butylene glycol, 1,2-butylene glycol, 1,5-pentane diol, 1,7-heptane diol, glycerol, 1,1, 1-trimethylolpropa e, 1,1, 1-trimethylolethane, hexane-1,2, δ-triol, a-methyl glucoside, pentaerythri- tol, erythritol, pentatols and hexatols. Also included within the term "polyhydric alcohol" are sugars such as glucose, sucrose, fructose and maltose as well as compounds derived from phenols such a 2,2-(4, ' -hydroxy- phenyl)propane, commonly known as bisphenol A. Illustra¬ tive oxiranes that are advantageously employed in the preparation of the polyether polyol include simple alkylene oxides such as ethylene oxide, propylene oxide, butylene oxide, and amylene oxide; glycidyl ethers such as t-butyl glycidyl ether and phenyl glycidyl ether; and random or block copolymers of two or more of these oxiranes. The polyalkylene polyether polyols may be prepared from other starting materials such as tetrahydrofuran and alkylene oxidetetrahydro- furan copolymers; epihalohydrins such as epichloro- hydrin; as well as aralkylene oxides such as styrene oxide. The polyalkylene polyether polyols may have primary, secondary or tertiary hydroxyl groups and, preferably, are polyethers prepared from alkylene oxides having from two to six carbon atoms such as ethylene oxide, propylene oxide and butylene oxide. The polyalkylene polyether polyols may be prepared by any known process such as, for example, the process disclosed by Wurtz in 1859 and Encyclopedia of Chemical Technology, Vol. 7, pp. 257-262, published by Int'erscience Publishers, Inc. (1951), or in U.S. Patent No. 1,922,459. Also suitable are polyether polyols and processes for preparing them that are described in Schick, M. J., Nonionic Surfactants, Marcel Dekker, Inc., New York (1967), U.S. Patent Nos. 2,891,073; 3,058,921; 2,871,219 and British Patent No. 898,306. Polyether polyols which are most preferred include, for example, the alkylene oxide addition products of water, trimethylol- propane, glycerine, pentaerythritol, sucrose, sorbitol, propylene glycol and blends thereof having hydroxyl equivalent weights of from 25 to 5000. Polyhydric thioethers which are sometimes advantageously condensed with alkylene oxides include the reaction product of thiodiglycol with alkylene oxides or dihydric alcohols such as disclosed above. Polyhydroxyl-containing phosphorus compounds which are optionally used include those compounds disclosed in U.S. Patent No. 3,639,542. Preferred polyhydroxyl-containing phosphorus compounds are prepared from alkylene oxides and acids of phosphorus having a P ? 0_. equivalency of from 72 percent to 95 percent. Polyacetals (acetal resins) which are option¬ ally reacted with alkylene oxides or other oxiranes include, for example, the reaction product of formalde¬ hyde or other suitable aldehyde with a polyhydric alcohol or an oxirane such as those disclosed above. Polyacetals derived from acetone or from cyclic acetals are also suitably employed. Aliphatic and aromatic thiols which are optionally reacted with alkylene oxides and other oxiranes include, for example, alkane thiols such as 1,2-ethane dithiol, 1,2-propane dithiol and 1,6-hexane dithiol; alkene thiols such as 2-butene-l,4-dithiol; and alkyne thiols such as 3-hexyne-l, 6-dithiol; and arene thiols such as 1,4-benzene dithiol. Other thiols suitable for this purpose are hydrogen sulfide as well as thiol functional polymers such as polyvinylbenzyl thiol. Acids and amides which are optionally reacted with alkylene oxides and other oxiranes include, for example, difunctional fatty acids such as hydroxystearic and dihydroxystearic acid as well as amides such as fatty acid alkanol amides, e.g., lauroyl monoethanol- a ide; diacids such as adipic and terephthalic acid; sulfonamides and other acids and amides set forth in Schick, supra. Amines which are optionally reacted with alkylene oxides and other oxiranes include, for example aromatic amines such as aniline, o-chloroaniline, p-amino aniline, 1,5-diamino naphthalene, methylene dianiline, the condensation products of aniline and formaldehyde and 2,4-diamino toluene; aliphatic amines such as methylamine, triisopropanolamine, isopropanol- amine, diisopropanolamine, ethylenediamine, 1,3-propylene- diamine, 1,4-butylenediamine and 1,3-butylenediamine, and mixtures thereof. Additional polyethers and methods for their preparation are set forth in Schick, supra. ' Examples of suitable hydroxy-containing polyesters include those obtained from polycarboxylic acids and polyhydric alcohols. Examples of suitable polycarboxylic acids include oxalic acid, malonic acid, succinic acid, glutaric acid, adipic acid, pimelic acid, suberic acid, azelaic acid, sebacic acid, bras- sylic acid, thapsic acid, maleic acid, fumaric acid, glutaconic acid, α-hydromuconic acid, β-hydromuconic acid, a-butyl-or-ethyl-glutaric acid, cr,β-diethylsuc- cinic acid, isophthalic acid, terphthalic acid, hemi- mellitic acid, and 1,4-cyclohexane-dicarboxylic acid. Any suitable polyhydric alcohol including both ali¬ phatic and aromatic may be used such as, for example, ethylene glycol, 1,3-propylene glycol, 1,2-propylene glycol, 1,4-butylene glycol, 1,3-butylene glycol, 1,2-butylene glycol, 1,5-pentane diol, 1,4-pentane diol, 1,3-pentane diol, 1,6-hexane diol, 1,7-heptane* diol, glycerol, 1,1,1-trimethylolpropane, 1,1,1-tri- methylolethane, hexane-1,2,6-triol, α-methyl glucoside, pentaerythritol and sorbitol. Also included with the term "polyhydric alcohol" are compounds derived from phenols such as 2,2(4,4'-hydroxyphenyl)propane, commonly known as besphenol A, bis(4,4'-hydroxyphenyl)sulfide and bis(4,4'-hydroxyphenyl)sulfone. Other polyahls suitably employed include, for example, polylactones; hydroxy functional acrylic polymers such as polymers of hydroxyethyl acrylate and hydroxypropyl acrylate; polyvinyl acetate and other polymers of vinyl acetate and other ethylenically unsaturated carboxylic acids; hydroxyl-containing epoxy resins, urea-formaldehyde and melamine- -formaldehyde resins; hydroxyl-containing poly¬ carbonates and polyurethanes; methylol resins; starches and other cellu-losic polymers; esters of phosphonic, sulfonic, sulfuric and boric acid; and polypeptides. The polyahl or polyahl mixture preferably contains a proportion of graft polymerization sites . The polyahl or polyahl mixture may contain a single polyahl species, a portion of which contains graft polymerization sites. Alternatively, the polyahl may be a mixture of two or more polyahl species, of which at least one contains graft polymerization sites. The graft polymerization sites are any func¬ tional group on the polyahl through which the polymer of the ethylenically unsatruated monomer or monomer mixture becomes grafted to the polyahl. Preferably, the graft polymerization sites are carbon-carbon double bonds which are copolymerizable with the ethylenically unsaturated monomer or monomer mixture. Said graft polymerization sites may be formed in side reactions which occur in the preparation of the polyahl, such as the unsaturated sites commonly formed in preparing a polypropylene oxide polyether polyol. Such normally occuring graft polymerization sites are most commonly adequate when the monomer being polymer¬ ized comprises a major portion of acrylonitrile. More commonly, however, the graft polymer¬ ization sites are purposefully introduced into the polyahl or polyahl mixture. The graft polymerization site is advantage¬ ously introduced into the polyahl or polyahl mixture by reacting said polyahl or polyahl mixture or a com¬ ponent or portion thereof, with a difunctional compound having an additional polymerizable ethylenically unsat¬ urated group, especially a vinyl group, i.e., -CHR'=CHR', wherein each R' is independently hydrocarbyl, prefer¬ ably lower alkyl or hydrogen, and another functional group which reacts with polyahl to form a bond between the difunctional compound and the polyahl. Suitable such functional groups include, for example, c-arboxylic acid or anhydride, hydroxyl, epoxy and isocyanate groups. Preferably, the functional group is carboxylic acid or isocyanate. Suitable difunctional compounds include, for example, ethylenically unsaturated carboxylic acids such as arcylic acid, methacrylic acid, furmaric acid, maleic acid, and itaconic acid. The preparation of such adducts are described, for example, in European Patent Publication 0091036. Also preferred are ethyleni¬ cally unsaturated isocyanates, in particular isocyanato- alkyl esters of an ethylenically unsaturated carboxylic acid. Suitable such isocyanates include the isocyanato- alkyl esters of acrylic or methacrylic acid, or,β-ethyleni- cally unsaturated isocyanates, monovinylidenearylisocy- anates and monovinylidene arylmethyl isocyanates. Exemplary isocyanatoalkyl esters include 2-isocyanatoεthyl methacrylate, 2-isocyanoethyl acryl¬ ate, 3-isocyanatopropyl methacrylate, l-methyl-2-isocy- anatoethyl methacrylate and 1, l-dimethyl-2-isocyanato- ethyl acrylate with 2-isocyanatoethyl methacrylate being most preferred. Suitable methods of preparing said isocyanato esters are well known, e.g. as shown in U.S. Patent Nos. 2,713,516 and 2,821,544 and British Patent No. 1,252,099. Exemplary monovinyli- • dene aromatic isocyanates and monovinylidene arylmethyl isocyanates include styrene isocyanate and vinylbenzyl isocyanate. Exemplary cr, β-ethylenically unsaturated isocyanates include vinyl isocyanate and isopropenyl isocyanate. Isocyanatoethyl methacrylate is espe- cially preferred. The preparation of adducts of a mono- or polyahl with such ethylenically unsaturated isocyanates is described, for example, in U.S. Patent Nos. ' .4,390,645 and 4,394,491. An ethylenically unsaturated monomer or mixture of monomers are polymerized in the polyahl or polyahl mixture in the presence of the aforementioned triiodomethyl compound. Suitable ethylenically unsat¬ urated monomers include, for example, aliphatic conju¬ gated dienes such as butadiene and isoprene; monovinyli- dene aromatic monomers such .as styrene, α-methyl styrene, ar-methyl styrene, ar-(t-butyl)styrene, ar-chlorostyrene, ar-cyanostyrene and ar-bromostyrene; a. ,β-ethylenically unsaturated carboxylic acids and esters thereof such as acrylic acid, methacrylic acid, methyl methacrylate, ethyl acrylate-, 2-hydroxyethyl acrylate, butyl acrylate, itaconic acid, and maleic anhydride; or , β-ethylenically unsaturated nitriles and amides such as acrylonitrile, methacrylonitrile, acrylamide, methacrylamide, N,N-dimethyl acrylamide, and N-(dimethylaminomethyl)acrylamide; vinyl esters such as vinyl acetate; vinyl ethers; vinyl ketones; vinyl and vinylidene halides as well as a wide variety of other ethylenically unsaturated materials which are copolymerizable with the aforementioned adduct, many of which have heretofore been employed in the formation of copolymer polyahls as described in U.S. Patent Nos. 3,823,201 and 3,383,351. It is understood that mixtures of two or more of the aforementioned monomers are also suitably employed in making the copolymer. Of the foregoing monomers, the monovinyl- idene aromatic monomers, particularly styrene, and the ethylenically"unsaturated nitriles, particularly acrylo- nitrile, are especially preferred. The amount of ethylenically unsaturated monomer(s) employed in the copolymerization reaction is generally an amount sufficient to provide good reinforce¬ ment in urethane polymers and cell openings in urethane foams. Preferably, the amount of unsaturated monomer(s) is from 1 to 70, more preferably from 5 to 50, most preferably from 10 to 50, weight percent based on the weight of the copolymer dispersion. The amount of the graft polymerization sites employed in the polyahl or polyahl mixture is an amount sufficient to produce a stable dispersion and provide particle size control. Preferably, the amount of the adduct employed is suffi¬ cient to provide from 0.0002 to 1, more preferably from 0.005 to 0.5, most preferably from 0.02 to 0.5 moles of graft polymerization sites per mole of polyahl or polyahl mixture. The copolymerization is readily carried out by simultaneously adding a monomer(s) and a free radical catalyst to the polyahl or polyahl mixture under condi¬ tions sufficient to cause free radical addition polymer¬ ization. The temperature of the copolymerization is dependent upon the initiator and is preferably in the range from 25° to 180°C, most preferably from 110° to 140°C, when azo-type catalysts are used. Alternatively, the free radical catalyst may be dispersed in a portion of the polyahl and thereafter added along with the monomer to the remaining portion of the polyahl or polyahl mixture. Other polymerization processes, both continuous and batch, may be suitably employed. Suitably, the concentration of polymerization catalyst is any amount sufficient to cause copolymer¬ ization of the graft polymerization sites in the polyahl or polyahl mixture if any and the ethylenically unsat¬ urated monomer(s). Preferably, however, the concentra¬ tion of catalyst is in the range from 0.1 to 20, more _ - preferably from 0.5 to 5, weight percent based on the combined weight of the mono-adduct and other monomer(s)-. Catalysts suitably employed in the practice of the copolymerization are free radical type polymer¬ ization catalysts such as, for example, the peroxides, persulfates, perborates, percarbonates, and azo com¬ pounds . Examples of such catalysts include hydrogen peroxide, t-butyl peroctoate, di(t-butyl)peroxide, t-butyl peroctoate, lauroyl peroxide, cumene hydro- peroxide, t-butyl hydroperoxide, 2, 2 'azobis [2,4- -dimethyl]pentanenitrile, 2-(t-butylazo)-2-methylbutane nitrile, 2-(t-butylazo)-2,4-dimethyl pentanenitrile, azobis(isobutyronitrile) as well as mixtures of such catalysts. Of the foregoing catalysts, the azo catal¬ ysts, especially azobis(isobutyronitrile) and azobis- (methylbutyronitrile) , are preferred. The resulting copolymer polyahl is generally more stable and less viscous than a like copolymer polyahl prepared in the absence of the triiodomethyl compound used herein. Accordingly, higher dispersed phase content copolymer polyahls can be prepared at any given viscosity according to this invention than according to conventional processes. Further reduction in viscosity can be achieved by diluting the copolymer polyahl with an additional polyahl (which may be the same or different than that employed in the copolymer polyahl) to obtain a lower solids blend. This lower solid blend normally exhibits a viscosity lower than that exhibited by a suitable copolymer polyahl prepared directly with the same solids content. For example, a 50 percent s©lids copolymer prepared according to this invention may be diluted with additional polyahl to obtain 40 percent solids. The diluted copolymer polyahl will generally exhibit a lower viscosity than a copolymer polyol prepared according to this invention having 40 percent solids prior to any dilution. The resulting copolymer dispersion is readily reacted with an organic polyisocyanate to form desir¬ able polyurethane products using conventional poly- urethane reaction conditions and procedures. Such reaction and procedures are optionally carried out in the presence additional polyahls, chain extending agents, catalysts, surface active agents, stabilizers, blowing agents, fillers and pigments. In the prepara- tion of foamed polyurethane, suitable procedures for the preparation of same are disclosed in U.S. Patent . No. RE 24,514. When water is added as the blowing agent, corresponding quantities of excess isocyanate to react with the water and produce carbon dioxide may be used. It is also to prepare polyurethane plastics by a prepolymer technique wherein an excess of organic polyisocyanate is reacted in a first step with the graft copolymer dispersion of the present invention to prepare a prepolymer having free isocy¬ anate groups which is then reacted in a second step with water to prepare a foam. Alternatively, the components may be reacted in a single working step commonly known as the "one-shot" technique of pre¬ paring polyurethanes. Furthermore, instead of water, low boiling hydrocarbons such -as pentane, hexane, heptane, pentene, and heptene; azo compounds such as azohexahydrobenzodinitrile; halogenated hydro¬ carbons such as dichlorodifluoromethane, trichloro- fluorome hane, dichlorodifluoroethane, vinylidene chloride and methylene chloride may be used as blowing agents . The foams may also be prepared by the froth technique as described in U.S. Patent Nos. 3,755,212; 3,849,156 and 3,821,130. Organic polyisocyanates which may be employed include aromatic aliphatic and cycloaliphatic polyiso- cyanates and combinations thereof. Representative of these types are the diisocyanates such as m-phenylene diisocyanate, tolylene-2,4-diisocyanate, tolylene-2, 6- diisocyanate, hexamethylene-1, 6-diisocyanate, tetra- methylene-1, -diisocyanate, cyclohexane-1, 4-diisocyanate, hexahydrotolylene diisocyanate (and isomers), naphthyl- ene-1, 5-diisocyanate, l-methoxphenyl-2, 4-diisocyanate, diphenyl-methane-4,4-diisocyanate, 4,4' -biphenylene diisocyanate, 3,3'-dimethoxy-4,4'-biphenyl diisocyanate, 3,3 '-dimethyl-4,4'-diphenyl diisocyanate, and 3,3'- -dimethyldiphenypropane-4,4' ,4'-diisocyanate; the tri- isocyante polymethylene polyphenylisocyante and tolylene- -2,4,6-triisocyanate; and the tetraisocyanates such as 4,4'-dimethyldipheriylmethane-2,2',5,5'-tetraisocyanate. Especially useful due to their availability and proper¬ ties are tolylene diisocyanate, diphenylmethane-4,4'- -diisocyanate and polymethylene polyphenylisocyanate. Crude polyisocyanate may also be used in the practice of the present invention, such as crude toluene diisocyanate obtained by the phosgenation of a mixture of toluene diamines or crude diphenylmethylene diisocy¬ anate obtained by the phosgenation of crude diphenyl- methylenediamine. The preferred undistilled or crude isocyanates are disclosed in U.S. Patent No. 3,215,652. The copolymer dispersions of this invention are -preferably employed in combination with other polyahl(s) commonly employed in the art. Accordingly, any of the polyahls which are described above for use in the preparation of the polymer dispersions of the present invention may be employed. Chain extending agents which may be employed in the preparation of the polyurethane compositions of the present invention include relatively low equivalent weight compounds having at least two functional groups bearing active hydrogen atoms such as, for example, water, hydrazine, primary and secondary diamines, amino alcohols, amino acids, hydroxy acids, glycols or mixtures thereof. A preferred group of chain extending agents includes, for example, water and primary and secondary aromatic diamines which react more readily with the isocyanate than does water such phenylenediamine, -bis(3-chloro-4-aminophenyl)methane, 2,4-diamino-3,5- diethyl toluene, trisecondary butanolamine, isopro- panolamine, diisopropanolamine, N-(2-hydroxypropyl)- ethylenediamine, and N,N'-di(2-hydroxypropyl)ethylene- diamine. The reaction of the polyisocyanate with the copolymer polyahl is advantageously carried out in the presence of an amount of urethane-type catalyst which is effective to catalyze reaction of the polyahl of the copolymer dispersion with the polyisocyanate. Prefer¬ ably, the amount of urethane catalyst is an amount comparable to that used in conventional urethane-type reactions. Any suitable urethane catalyst may be used including tertiary amines, such as for example, tri- ethylenedia ine, N-methyl morpholine, N-ethyf morphol- ine, diethyl ethanolamine, N-coco morpholine, 1-methyl- -4-dimethylaminoethyl piperazine, 3-methoxy-N-dimethyl- propyl amine, N,N-dimethy1-N' ,N'-methyl isopropyl propylenediamine, N,N-diethyl-3-diethylaminopropyl amine, and dimethyl benzyl amine. Other suitable catalysts are, for example, tin compounds such as stannous chloride, tin salts of carboxylic acids such as dibutyltin di-2-ethyl hexoate, as well as other organometallic compounds such as are disclosed in U.S. Patent No. 2,846,408. A wetting agent(s) or surface-active agent(s) is generally necessary for production of high grade polyurethane foam according to the present invention, since in the absence of same, the foams collapse or contain very large uneven cells. Numerous wetting agents have been found satisfactory. Nonionic surfac¬ tants and wetting agents are preferred. Of these, the nonionic surface-active agents prepared by the sequential addition of propylene oxide and then ethylene oxide to propylene glycol and the solid or liquid organosilicones have been found particularly desirable. Other surface- -active agents which are ' operative, although not preferred include polyethylene glycol ethers of long chain alcohols, tertiary amine or alkylolamine salts of long chain alkyl acid sulfate esters, alkyl sulfonic esters and arylsulfonic acids. The following examples are given to illustrate the present invention and are not to be construed as limiting the scope thereof in any manner. All parts and percentages are by weight unless otherwise indicated. Example I To a temperature controlled, stirred vessel, 1,017 grams (g) of polyol A and 766 grams of polyol B are added and heated to 120°C. Over a 45 minute period, an additional 1,799 g of polyol A that has been mixed with 65 g of azobisisobutyronitrile (AIBN) is added to the reactor. Concurrently, 1,149 g of polyol B that has been mixed with 9.6 g (0.28 percent by weight of monomer) of iodoform is added to the reactor. During this 45 minute feed period, 2,210 g of styrene and 1,190 g of acrylonitrile are also added to the reactor. Sufficient heating and cooling is supplied to maintain the reaction temperature at 120°C + 5°C. After the initial 45 minute feed period is completed, an additional 13 g of AIBN mixed in 369 g of polyol A is added to the reactor over a period of 15 minutes to 1 hours. This is followed by vacuum stripping for a period of 1 to 2 hours to remove the remaining unreacted monomer. For comparison, the foregoing experiment is repeated, this time using no iodoform. The Brookfield viscosity (25°C), percent solids (dispersed phase), color, visual agglomation of dispersed as polymer particles and filterability through a 150 mesh (0.104 mm opening) screen are determined for each run, with the results as reported in Table I following. TABLE I With Without* CHI 3 CHI 3 Percent solids 40 40 Viscosity, cps 5360 8780 (Pa-s) (5.36) (8.78) Visual Agglomation Minimal Severe Filterability 27% 2.2% Not an example of this invention As can be seen from the foregoing results, the copolymer polyol prepared according to this invention, although it has the identical solids content as the comparative resin, is much lower in viscosity. It is also much more highly stable, as indicated by the minimal visual agglomeration and high filterability. Example II To a temperature controlled, stirred vessel, 540 g of polyol A and 407 g of polyol B are added and heated to 120°C. Over a 45 minute period, an additional 2,941 g of polyol A that has been mixed with 65 g of azobisisobutyronitrile (AIBN) is added to the reactor. Concurrently, 610 g of polyol G that has been mixed with 8.5 g (0.25 percent by weight of monomer) of CHI_ is added to the reactor. During this 45 minute feed period, 2,040 g of styrene and 1,360 g of acrylonitrile are also added to the reactor. Sufficient heating and cooling is supplied to maintain the reaction temperature at 120°C + 5°C. After the initial 45 minute feed period is completed, an additional 13 g of AIBN mixed in 602 g of polyol A is added to the reactor over a period of 15 minutes to 1 hour. This is followed by vacuum stripping for a period of 1 to 2 hours to remove the remaining unreacted monomer. The foregoing procedure is repeated twice, one using 18.7 g CHI_ (0.55 percent by weight of monomer) and once using no chain transfer agent. The resulting copolymer polyols are tested as described in Example I with the results as reported in Table II following. TABLE II 0.25 percent 0.55 percent CHI. CHI. No CHI * Percent Solids 40 40 40 Viscosity, cps 3544 3624 4070 (Pa-s) (3.544) (3.624) (4.070) Visual Agglomation minimal very minimal moderate Filterability through 180 mesh screen 12 83 2.0% (0.084 mm opening) * Not an example of this invention. Again, reduced viscosity at an equal solids level, as well as improved stability, are achieved with the practice of this invention.

Claims: CLAIMS -24- 1. A process for preparing a polymer polyahl comprising polymerizing an ethylenically unsaturated monomer or mixtures thereof in a polyahl or polyahl mixture whereby a dispersion of polymer particles is prepared in a continuous polyahl phase, characterized by conducting said polymerization in the presence of a triiodomethyl compound. 2. The process of Claim 1 characterized in that the triiodomethyl compound is represented by the structure: • - RCI 3 wherein R is hydrogen, halogen including iodine, lower alkyl, benzyl or phenyl. 3. The process of Claim 2 characterized in that the triiodomethyl compound is iodoform, 1,1,1- triiodoethane or carbon tetraiodide. 4. The process of Claim 1 characterized in that the triiodomethyl compound is employed in an amount from 0.1 to 2 percent by weight of the ethyleni¬ cally unsaturated monomer or mixture of monomer. 5. The process of Claim 1 characterized in that the polyahl or polyahl mixture contains purpose¬ fully introduced ethylenic unsaturation. 6. The improved process of Claim 5 character¬ ized in that the polyahl or polyahl mixture comprises the reaction product of a polyahl and a difunctional compound having an additional polymerizable ethyleni¬ cally unsaturated group and another functional group which reacts with a polyahl to form a bond between the difunctional compound and the polyahl. 7. The process of Claim 6 characterized in that the difunctional compound is an ethylenically unsaturated carboxylic acid. 8. The process of Claim 6 characterized in that the difunctional compound is an ethylenically unsaturated isocyanate. 9. The process of Claim 8 characterized in that the difunctional compound is an isocyanato- alkylester of acrylic or methacrylic acid. 10. The process of Claim 1 characterized in that said monomer comprises styrene, acrylonitrile, or mixtures thereof.

Inventors: NORTON MICHAEL A, SERRATELLI JOHN F, NORTON, MICHAEL, A., SERRATELLI, JOHN, F.
Applicants: DOW CHEMICAL CO, THE DOW CHEMICAL COMPANY
Application year: 1985
Main classification: C08L25
IPC codes: C08F283, C08F299, C08G18