BICARBAZOLE-OXADIAZOLE ELECTROACTIVE POLYMERS

Abstract: Tractable doped electroactive polymers comprise a charged polymer backbone of recurring units of a 3,3′-N,N′-di-­ substituted-6,6′-bicarbazole-1,3,4-oxadiazole-2,5-diyl ring system, and a sufficient concentration of a charge-­ compensating ionic dopant associated therewith, the polymer backbone being capable of undergoing reversible oxidation to form the charged polymer backbone.

Description: This invention relates to electroactive organic polymeric materials. More specifically, this invention relates to associating electroactivating agents known in the art as dopants with an organic polymer. Recently, research has been conducted into organic polymeric materials in order to modify their room temperature electrical conductivity by reacting them with electron donor or acceptor molecules. The electron donor or acceptor molecules, generally known in the art as n- and p-type dopants respectively, can transform the organic polymeric materials so that these modified organic polymeric materials exhibit semiconducting and metallic room temperature electrical conductivity. Polyacetylene is an example of an organic polymeric material whose room temperature electrical conductivity can be modified over several orders of magnitude above its insulator state, by the incorporation of dopant molecules (see A. J. Heeger et al, U.S. Patent 4,222,903). Other examples of organic polymeric materials whose room temperature electrical conductivity can be enhanced by several orders of magnitude over their insulator state by means of incorporation of dopant molecules are poly-p-phenylene, polypyrrole, poly-1,6 heptadiyne, and polyphenylene vinylene. However, all of the above recited examples are of organic polymeric materials which are completely insoluble or infusable and hence are completely intractable. Other examples of organic polymers whose room temperature electrical conductivity can be modified with the aid of dopants are polyphenylene sulfide and poly-m-phenylene. However, the above recited materials though being tractable in their original virgin state, undergo irreversible chemistry when reacted with dopants which modify their room temperature electrical conductivity. This irreversible chemistry imparts upon these dopant modified organic polymeric materials a state of intractability. Upon removal of the doping agents, these materials do not revert to the chemical structure which they originally exhibited prior to being modified by the dopants. The inorganic material polysulfur nitride is also considered a polymeric conductor. As with the previously recited polymeric materials, polysulfur nitride is also completely intractable. The synthesis of poly(1,3,4-oxadiazole-2,5-diyl-vinylene) and poly(1,3,4-oxadiazole-2,5-diyl-ethynylene) is described by I. Schopov et al. in Makromolecular Chemie , vol. 179, No. 1, pp. 63-71 (1978). These undoped oxadiazole polymers are shown by Schopov to exhibit an electrical conductivity characteristic of insulators. U.S. Patent No. 4,452,725 to Wellinghoff et al. describes an electrically conducting polymer obtained by doping poly(N-alkyl 3,3'-carbazolyl) with a compatible charge transfer acceptor. GB-A-2130593 discloses heterodiazole electroactive polymers. In particular, it is preferred to incorporate heterocyclic connecting units into n-type polymers like poly-2,5(1,3,4)oxadiazoles. For use in a wide variety of electronic device applications, it is highly desirable to have available organic polymeric electrically conducting materials having a preselected room temperature conductivity which can be varied over a broad range. This range should preferably extend from the insulator state of the unmodified organic polymeric material through the semiconducting regime and extending into the highly conducting metallic state. It is also desirable that these organic polymeric electrically conducting materials should be tractable and hence processable so that useful articles of any desired shape and size can be fabricated. Tractable organic polymers are those which can be readily shaped, formed, molded, pressed, cast, etc., into desired articles from the liquid state, i.e. either from the melt, fluid glassy state, or from solution after the completion of the polymerization reaction of the organic polymeric material. According to one aspect of the present invention there is provided a tractable electroactive polymer (as hereinafter defined) which comprises a charged polymer backbone of recurring units of a 3,3'-N,N'-disubstituted-6,6'-bicarbazole-1,3,4-oxadiazole-2,5-diyl, wherein each carbazole nitrogen is substituted by lower alkyl of 1 to 6 carbon atoms or phenyl, and a sufficient concentration (as hereinafter defined) of a charge-compensating ionic dopant (as hereinafter defined) associated therewith, the polymer backbone being capable of undergoing reversible oxidation to form the charged polymer backbone. The electroactive polymeric material of the invention comprises a dopant modified organic polymer whose room temperature electrical conductivity is controlled in a highly selective and reversible manner. Electroactive polymer is defined as a polymer having a conductivity which has been modified with electron acceptor or donor dopants to be greater than the conductivity of the virgin state of the polymer. The electroactive organic polymeric material is fabricated from a virgin polymer, which in itself is completely tractable and processable and which exhibits excellent mechanical and thermal properties as well as being highly stable to oxidative degradation, by modifying the polymer with a conductivity modifier, i.e. electron donor dopants or electron acceptor dopants. The electroactive organic polymeric material is comprised of recurring units of a 3,3'-N,N'-disubstituted-6,6'-bicarbazole-1,3,4-oxadiazole-2,5-diyl ring system and a conductivity modifier. More specifically, the electroactive polymer is a charged polymer backbone incorporating a sufficient concentration of charge-compensating anionic dopants, i.e., ions of opposite charge to the charge of the polymer backbone. A sufficient concentration of anionic dopants is defined as that concentration which, when associated with the polymer, effects a significant increase in the polymer conductivity, i.e., of the order of 10% or greater. We have discovered that 3,3'-N,N'-disubstituted-6,6'-bicarbazole-1,3,4-oxadiazole-2,5-diyl polymers can be effectively doped with conductivity modifiers to provide electroactive polymers having an electrical conductivity several orders of magnitude greater than the conductivity of the undoped virgin polymers. In addition, the electroactive polymers of the invention are highly tractable and processable and therefore overcome the disadvantages of prior art materials. In general, an n-type electroactive organic polymer is obtained by reacting the virgin polymer with reducing or electron donor dopants. Electron donor dopants induce n-type conductivity in the polymer by donating an electron to the polymer and reducing same to a polyanion and the dopant is oxidized to a cation. Similarly, a p-type electroactive organic polymer is obtained by reacting the virgin polymer with oxidizing electron acceptor dopants. Electron acceptor dopants induce p-type conductivity in the polymer by oxidizing the polymer to a polycation and the dopant is reduced to an anion. The desired value of the room temperature electrical conductivity of the dopant modified electroactive organic polymer is preselected by controlling the level of incorporation of the dopants into the virgin polymer. Alternatively, the desired value of the room temperature electrical conductivity of the dopant modified electroactive organic polymer is preselected by controlling the length of the reaction time between the virgin polymer and dopants. Furthermore, the highly selective and reversible modification of the room temperature electrical conductivity of the virgin polymer can proceed by either chemical or electrochemical means. The highly selective and reversible modification of the electrical conductivity of the dopant containing organic polymeric material together with the tractability and processability of the virgin polymer is highly desirable in that the fabrication of useful articles and devices such as primary and secondary batteries, photovoltaic devices, and Schottky type devices can be accomplished. Furthermore, the materials described in this invention can be utilized as active components in such devices and articles as electrochromic displays and photolithographic processes. The electroactive organic polymers of the invention are tractable and processable virgin polymers consisting of recurring units of a 3,3'-N,N'-disubstituted-6,6'-bicarbazole-1,3,4-oxadiazole-2,5-diyl ring system modified by suitable conductivity modifiers. The polymers are composed of repeating diradical units derived from 3,3'-N,N'-disubstituted-6,6'-bicarbazole-1,3,4-oxadiazole-2,5-diyl ring systems wherein each carbazole nitrogen is substituted with lower alkyl of 1-6 carbon atoms or phenyl. A diradical is defined as a molecule that has two unsatisfied positions available for linking into the polymer chain. Suitable examples of 3,3'-N,N'-disubstituted-6,6'-bicarbazole-1,3,4-oxadiazole-2,5-diyl recurring units include 3,3'-N,N'-diphenyl-6,6'-bicarbazole-1,3,4-oxadiazole-2,5-diyl, 3,3'-N,N'-dimethyl-6,6'-bicarbazole-1,3,4-oxadiazole-2,5-diyl, 3,3'-N,N'-diethyl-6,6'-bicarbazole-1,3,4-oxadiazole-2,5-diyl, and 3,3'-N,N'-dipropyl-6,6'-bicarbazole-1,3,4-oxadiazole-2,5-diyl. Preferably, the N,N'-disubstituted bicarbazole is the N,N'-diethyl derivative. In general, the polymer is rendered electroactive by incorporating into the virgin polymer a conductivity modifier. More specifically, the polymer is rendered electroactive by removing electrons (oxidizing) from the virgin polymer backbone. This can be accomplished by incorporating into the virgin polymer a conductivity modifier which is an electron acceptor dopant. An electron acceptor dopant removes an electron from the polymer, the polymer becoming oxidized to a polycation and the dopant becoming reduced to an anion. Alternatively, the polymer can be rendered electroactive by electrochemical oxidation. In this case an electron is removed from the polymer from an electrode, and charge-compensating anions are incorporated into the polymer from the supporting electrolyte solution. Consequently, the resulting electroactive polymer consists of a charged polymer backbone incorporating charge-compensating ionic dopants. A suitable negatively charged compensating dopant, i.e. anionic dopants, can be an anion such as the halogen ions, other ions such as AsF₄⁻, and preferably ions such as AsF₆⁻, ClO₄⁻, PF₆⁻, SO₃CF₃⁻, BF₄⁻, NO₃⁻, POF₄⁻, CN⁻, SiF₅⁻, SbCl₆⁻, SbF₆⁻, HSO₄⁻, organic anions such as CH₃CO₂⁻ (acetate), C₆H₅CO₂⁻ (benzoate), CH₃C₆H₄SO₃⁻ (tosylate), and strong Lewis bases. Mixtures of the charge-compensating dopants can be employed. These ionic dopants produce a p-type conductivity when associated with an oxidized or positively charged polymer polycation. The dopant modified electroactive polymer has a charge opposite to the conductivity modifier, i.e. ionic dopant. The charges on the dopant modified electroactive polymer and the ionic dopant balance so that the dopant modified electroactive polymer is an electrically neutral system. The association of the virgin polymer with electron acceptor dopants produces an electroactive polymer with p-type conductivity. More specifically, oxidation of the polymer and incorporation of anionic charge-compensating dopants produces a polymer with p-type conductivity. The tractable electroactive polymers of the invention, which comprise a charged polymer backbone and charge-compensating ionic dopants associated therewith, can be represented by the following formula: wherein R is lower alkyl of 1 to 6 carbon atoms (preferably ethyl) or phenyl; n is an integer from 2 to 1,000; d is an integer from 1 to 2,000; S is an integer from 1 to 3; and M is a charge-compensating ionic dopant of opposite electrical charge to the charge of the polymer backbone; wherein the polymer backbone is capable of undergoing reversible oxidation to form the charged polymer backbone. The molecular weight determines the physical properties of the electroactive polymer. The magnitude of n is a function of the molecular weight. Preferably, n is from 5 to 500. Most preferably, n is from 10 to 300. Molecular weights of the polymer should generally be between 1,000 and 250,000. A preferred molecular weight is above 10,000. Tractable films are formed with electroactive polymers wherein n is adjusted so that the molecular weight exceeds 10,000. The enhancement in conductivity of the electroactive polymer above the conductivity of polymer in the virgin state is determined by d. The value for d is not greater than 2 n. The conductivity is increased and adjusted by increasing d. Conductivities in the semiconductor region can generally be achieved with d values of about 5 percent of the n value, e.g., d equals 5 when n equals 100. Preferred electroactive polymers are doped polymers that have conductivities greater than about 1x10⁻¹⁰ ohm⁻¹ cm⁻¹, most preferably greater than 1x10⁻⁴ ohm⁻¹ cm⁻¹. Greater concentrations of the charge-compensating ionic dopant M increase the conductivity to the metallic conductivity regime. The charge-compensating anionic dopant M is selected from the previously recited dopants and the like. Polymer Fabrication The starting material for preparing the electroactive polymers of this invention are polymers comprising recurring units of a 3,3'-N,N'-disubstituted-6,6'-bicarbazole-1,3,4-oxadiazole-2,5-diyl, wherein the substituent on each carbazole nitrogen is lower alkyl of 1-6 carbon atoms or phenyl. These undoped polymers are believed to be novel and hence in accordance with another aspect of the invention, there is provided a polymer represented by the general formula: wherein R is lower alkyl of 1 to 6 carbon atoms or phenyl, and n is an integer from 2 to 1,000. The 3,3'-N,N'-disubstituted-6,6'-bicarbazole-1,3,4-oxadiazole-2,5-diyl polymers useful for making electroactive polymers by appropriate doping techniques are prepared as described below. A preferred process for the preparation of poly[3,3'-N,N'-disubstituted-6,6'-bicarbazole-1,3,4-oxadiazole-2,5-diyl] involves the one-step polycondensation of hydrazine or the hydrazine salt of a non-oxidizing acid with N,N'-disubstituted-6,6'-bicarbazole-3,3'-dicarboxylic acid, wherein each carbazole nitrogen is substituted with lower alkyl of 1 to 6 carbon atoms or phenyl. The dicarboxylic acid starting material is prepared by known procedures, such as the method described in the Journal of the Electrochemical Society, volume 122, page 876 (1975). The polycondensation process comprises polymerizing the N,N'-disubstituted-6,6'-bicarbazole-3,3'-dicarboxylic acid with a 0 to 30% molar excess of hydrazine or the hydrazine salt of a non-oxidizing acid in the presence of a solvent, preferably polyphosphoric acid. Suitable hydrazine salts of non-oxidizing acids include hydrazine hydrochloride, hydrazine hydrobromide, hydrazine phosphate and hydrazine oxalate. The preferred hydrazine salt is hydrazine hydrochloride. The polymerization reaction is generally carried out at a temperature of about 120-180°C and a pressure in the range of about 0.98 - 49 bar (1 to 50 atmospheres). The reaction time will generally vary from about 2 to 25 hours, although longer reaction times may be utilized. The polymer is isolated by coagulation in water, followed by filtration and extraction with methanol or a like solvent, such as ethanol, acetone, tetrahydrofuran and the like. Tractable Polymer Fabrication Subsequent to polymerization, articles such as fibers, ribbons, or free-standing films are cast from solution. The solution is formed by dissolving the desired polymer in a solvent which consists of sulfuric acid, formic acid, methane sulfonic or polyphosphoric acid. The solution temperature is generally from about 20°C to about 100°C. The polymers are coagulated into solid shapes such as fibers, ribbons, or free-standing films in a basic coagulation bath. For free-standing films, the polymers are fabricated from solutions containing about 2 to 25% polymer dissolved in the solvent. At concentrations which exceed 10%, the cast films take on an anisotropic morphology. The anisotropic property enhances the conductivity in the anisotropic direction. An amine, for example triethylamine, dissolved in a protonic solvent such as H₂O and preferably ethyl alcohol comprises the coagulation bath. The bath is maintained at a lower temperature than the dissolution temperature of the polymer in the solvent. Usually room temperature is selected as the operating temperature of the coagulation bath. The fabricated articles are dried. Elevated temperatures, usually 60°C, and reduced pressure accelerated the drying process. Drying is continued until no further weight loss is observed. Alternatively, films are cast into water, comprising the coagulation bath, followed by neutralization in aqueous bicarbonate. Neutralized films are washed in water and dried at elevated temperatures, 60°-100°C, under reduced pressure. Polymer Conductivity Modification After fabrication of the desired articles from the heterocyclic polymers by means of the procedure described above, the articles are rendered electroactive by, for example, chemical or electrochemical procedures. The articles can be rendered electroactive in an atmosphere which is inert with respect to the polymer and dopant, by contacting them with suitable conductivity modifiers, i.e. dopants. An inert atmosphere is defined as an atmosphere which does not react with the polymer, the dopant, or the electroactive polymer. For example, the atmosphere can be argon, helium, and nitrogen and the like. The doping can also be carried out in an inert liquid medium such as tetrahydrofuran, acetonitrile and the like. The inert liquid medium should be able to wet and swell the polymer but not react with it. The dopants used herein are oxidizing or electron accepting molecules. These dopants may be in the form of gases or vapors, pure liquids or liquid solutions. Preferably, oxygen and water moisture are excluded during and after the doping process because the conductive polymers tend to degrade, i.e. lose conductivity, when exposed thereto. For example, the polymer can be contacted with conductivity modifiers, such as AsF₅, Br₂ or NO⁺BF₄⁻, in a tetrahydrofuran solution. The conductivity modifier concentration can be from about 0.001 to about 1 molar and preferably from about 0.01 to about 0.5 molar in the THF or other suitable solvent. Alternative doping methods are taught in U.S. Patent 4,204,216. The incorporation of the dopants into the polymer can be observed by a color change in the polymer as well as an enhanced conductivity. For example, a virgin polymer film having a yellow, orange or brown color, changes to a green, blue or black color with a metallic luster upon doping and the measured conductivity increases by many orders of magnitude. Alternatively, the polymers can be oxidized to their conductive forms using electrochemical techniques. In this method, herein referred to as electrochemical doping, the polymer is immersed in a suitable electrolyte solution and used as one electrode of an electrochemical cell. Upon passing an electric current through such a cell the polymer becomes oxidized, and charge-compensating anions from the supporting electrolyte become incorporated into the polymer. This doping also proceeds with the characteristic color change described above. Thus, the polymer can be electrochemically doped with whatever appropriately charged ion is present in the electrolyte solution. Electrolyte solutions are comprised of a salt dissolved in a solvent. Suitable solvents are acetonitrile, tetrahydrofuran, 2-methyl-tetrahydrofuran, propylene carbonate, dimethylformamide, and dimethylsulfoxide. Alternative electrolytes are specified in our copending Application No.83900470.2 (Publication No.96723). Suitable anions are Cl⁻, Br⁻, ClO₄⁻, BF₄⁻, and PF₆⁻. The extent of doping can be easily controlled by adjusting the amount of charge electrochemically injected into the polymer, either by controlling the magnitude of the current used (galvanostatic charging) or by controlling the potential of the polymer electrode with respect to a reference electrode (potentiostatic charging). The above-described electrochemical doping process is completely reversible. The polymer can be "undoped" and returned to its original, neutral, non-conducting state simply by applying a current opposite in sign to that used for the doping process. Upon complete undoping the color of the polymer reverts back to its original color. Thus, for example, an oxidized, conducting poly-[bicarbazole-oxadiazole] polymer can be rereduced completely to its neutral, non-conducting form, and the charge-compensating anions incorporated during the electrochemical oxidation process are expelled from the article during electrochemical re-reduction. The following Example illustrates the invention. Example Poly[3,3'-N,N'-diethyl-6,6'-bicarbazole-1,3,4-oxadiazole-2,5-diyl a. Polymer Preparation N,N'-diethyl-6,6'-bicarbazole-3,3'-dicarboxylic acid (0.4997g, 0.00105 moles, prepared as described in J. Electrochemical Soc., vol. 122, page 876, 1975) and hydrazine hydrochloride (0.0790g, 0.00115 moles) were stirred together and heated at 140°C in 8.68g of polyphosphoric acid. After heating overnight, the dark green, rubbery polymer was stirred with water and filtered to give a coarse, black solid. The polymer was washed with methanol and then extracted with methanol in a Soxhlet apparatus overnight. After drying, 0.47g (100%) of the polymer was obtained as a black powder. Free-standing films were cast from a 5% solution of the polymer in trifluoromethanesulfonic acid. An infrared spectrum of the polymer had no absorption at the carbonyl region, indicating that all of the carboxylic acid groups had been converted. There was a strong absorbance at 1590 cm⁻¹, indicating C=N bonds, and at 970 cm⁻¹, characteristic of the oxadiazole ring. Analysis of the polymer was as follows. Calculated: C, 78.28%; H, 4.88%; N, 12.33%. Found: C, 72.70%; H, 4.58%; N, 10.38%. b. Electrochemical Doping of Polymer on a Wire Platinum wire was coated with the polymer by dipping the wire in a solution of the polymer in trifluoromethanesulfonic acid and allowing it to dry. This polymer was then examined by cyclic voltammetry which showed a reversible oxidation at +0.65 volts and +0.88 volts vs. a silver/silver nitrate reference electrode.

Claims: A tractable electroactive polymer which comprises a charged polymer backbone of recurring units of a 3,3'-N,N'-disubstituted-6,6'-bicarbazole-1,3,4-oxadiazole-2,5-diyl, wherein each carbazole nitrogen is substituted by lower alkyl of 1 to 6 carbon atoms or phenyl, and associated therewith an anionic charge-compensating dopant capable of producing a p-type conductivity in the polymer, the polymer backbone being capable of undergoing reversible oxidation to form the charged polymer backbone. An electroactive polymer as claimed in Claim 1, wherein the recurring unit is 3,3'-N,N'-diethyl-6,6'-bicarbazole-1,3,4-oxadiazole-2,5-diyl. An electroactive polymer as claimed in Claim 1 or 2, wherein the charge-compensating anionic dopant is an anion selected from halogen ions, AsF₄⁻, AsF₆⁻, ClO₄⁻, PF₆⁻, SO₃CF₃⁻, BF₄⁻, NO₃⁻, POF₄⁻, CN⁻, SiF₅⁻, SbCl₆⁻, SBF₆⁻, HSO₄⁻, acetate, benzoate and tosylate, or a mixture of two or more of said anions. An electroactive polymer as claimed in Claim 1, 2 or 3, wherein the polymer backbone has a molecular weight of from 1,000 to 250,000. An electroactive polymer as claimed in Claim 4, wherein the polymer backbone has a molecular weight above 10,000. A polymer represented by the general formula: wherein R is lower alkyl of 1 to 6 carbon atoms or phenyl, and n is an integer from 2 to 1,000. A polymer as claimed in Claim 6, wherein R is ethyl.

Inventors: DENISEVICH, PETER, JR., KURKOV, VICTOR P., SCHROEDER, ALBERT H., SUZUKI, SHIGETO
Applicants: CHEVRON RESEARCH AND TECHNOLOGY COMPANY
Application year: 1985
Main classification: C08L79
IPC codes: H01B1, H01L51, C08G73, H01M4, C08L79