METHOD FOR FABRICATING A MASTER RECORDING DISC

Abstract: In a method of fabricating a master recording disc, a pho­ toresist layer is formed on a glass substrate to form a master blank, which is revolved and exposed to an intensity-modu­ lated laser beam so that a series of optically excited regions is formed in track turns in the photoresist layer. The optically ex­ cited regions are removed, forming a series of pits in the pho­ toresist layer. An etchant gas is sputtered onto the master blank until the pits in the photoresist layer extend through the boundary surface of the photoresist layer and the glass sub­ strate to a desired depth and pits having side walls tapered in a direction away from the boundary surface are formed in the substrate. The photoresist layer which remains on the glass substrate is finally removed.

Description: BACKGROUND OF THE INVENTION The present invention relates generally to a method for fabricating a master recording disc to be used for mass-producing digital audio or video discs. EP-A-126 594 describes the fabrication of an optical memory element where grooves are formed by etching a glass substrate coated by a developed resist film. It was published after the date of filing of the present application and shall be considered as comprised in the state of the art according to the provisions of Article 54(3) EPC but shall not be considered in deciding whether there has been an inventive step. This document does not describe the fabrication of a master recording disc and does not therefore describe particular means for adjusting the slope of the boundary of the pits. Master recording discs for digital audio and video disc recording are formed with pits of tapered side walls. The tapered-wall pits are advantageous as they ease the separation of molded plastic discs from the mold and further advantageous for tracking purposes. The concept of this tapering is shown and described in Japanese Laid-open Patent Publication 55-55449. However, it has been difficult to form tapered-wall pits on a glass substrate of the master recording disc. One approach is shown and described in Japanese Laid-open Patent Publication 55-101144 and involves the use of a master blank composed of glass substrate, and a photoresist layer on the SiO₂ layer which is however deposited on the substrate. An intensity-modulated laser beam is directed to the master blank to the photoresist layer to produce a series of optically excited regions in track turns. The master blank is subsequently developed to form a series of pits which extend down to thew boundary surface of the photoresist and SiO₂ layers, and then is exposed to the plasma of CF₄ gas in a vacuum chamber. The SiO₂ layer is etched by the plasma etchant so that the pits are enlarged at the top and tapered downwardly to the boundary surface of the SiO₂ layer and the glass substrate. Although tapered-wall pits are produced in the SiO₂ layer, it is difficult to maintain a consistent taper angle. SUMMARY OF THE INVENTION The present invention has the object of providing a method of fabricating a master recording disc for the mass-production of digital audio and video discs which ensures pits having a consistent taper angle value in an efficient manner. As claimed, the method of the invention comprises forming a photoresist layer directly deposited on a glass substrate to form a master blank, revolving the master blank and directing an intensity-modulated laser beam onto the surface of the revolving photoresist layer so that a series of optically excited regions is formed in track turns in the photoresist layer. The optically excited regions are removed, forming a series of pits in the photoresist layer. The method of the invention includes the step of sputtering the master blank with an etchant gas until the pits in the photoresist layer extend through and beyond the boundary surface of the photoresist layer and the glass substrate to a desired depth from the boundary surface. According to the invention, the thickness of the photoresist layer is chosen in such a manner that when said desired depth is reached, pits having side walls tapered in a direction away from said boundary surface are formed in the substrate. The method of the invention further includes the step of removing the photoresist layer which remains on the glass substrate. BRIEF DESCRIPTION OF THE DRAWINGS The present invention will be described in further detail with reference to the accompanying drawings, in which: Figs. 1A to 1D are cross-sectional views illustrating sequential steps of fabricating a master recording disc; Figs. 2A to 2F are cross-sectional views illustrating sequential changes that a given pit undergoes when the master disc is subjected to sputtered gases; and Fig. 3 is a graphic views illustrating the relationship between the angle of the side walls of pits and the thickness of a photoresist deposited on a glass substrate. DETAILED DESCRIPTION In Fig. 1A, a mirror-polished, soda-lime glass disc 10 having a diameter of 240 mm with a 15-mm center hole and a thickness of 10 mm is prepared. The glass disc is composed of 70 to 75 weight percent of SiO₂, and chemically inactive compositions such as 12 to 18 weight percent of Na₂O, 0 to 1 weight percent of K₂O, 5 to 14 weight percent of CaO, 0 to 4 weight percent of MgO and 0.5 to 2.5 weight percent of Al₂O₃. A photoresist layer 11 (identified as AZ1350, a product of Shipley Chemical Company, U.S.A.) sensitive to laser beam is applied onto the glass disc 10 using a spin coat method to a thickness of about 4000 angstrom units (400 nm) to form a blank master disc 12. To ensure good adhesive contact between disc 10 and photoresist 11, adhesive such as hexamethyldisilazane is preferably applied onto the disc 10 before the photoresist is applied. The master blank 12 is then placed on a turntable and rotated at a predetermined speed. Onto the spinning photoresist layer 11 is directed an argon laser beam having an intensity modulated with a standard digital audio signal or an FM video signal. The beam is moved at a predetermined speed in a radial direction to cause the spot of beam on the photoresist layer to follow a spiral path in a manner well known in the art, thus forming a series of optically excited regions in a spiral pattern. The photoresist 11 is then developed and the optically excited regions are etched away from the master blank to form a series of microscopic pits 13 along a spiral track as shown in Fig. 1B. The intensity of the laser is such that it produces pits having sidewalls perpendicular to the disc surface as illustrated in Fig. 2A. The master disc is then placed in a gas etching apparatus for sputtering the surface of the master disc 12 with an etchant gas in a manner in which the physical properties of the etchant and photoresist layer 11 are considered predominant factors in the formation of pits of desired configuration. This apparatus has a chamber in which are mounted a pair of upper (positive) and lower (cathode) disc electrodes 250 mm in diameter spaced a distance of 65 mm apart. The master disc is placed on the cathode. The chamber is initillay evacuated to a vacuum of 5 x 10⁻³ Torr (0.66 Pa) and then CF₄ (tetrafluoromethane) gas is introduced to the apparatus to a pressure of 2 x 10⁻² Torr (2.66 Pa). 200-watt high frequency energy at 13.56 MHz is applied to the electrodes for a period of 12 minutes and 30 seconds. During the gas etching process, the master disc is bombarded by downward streams of positively ionized etchant gas. Because of the uniformly directed cathode bombardment the photoresist 11 is etched at a higher rate on the edges of pits 13 than on its upper surface and the bottom of pits 13, i.e., the glass disc 10, is etched uniformly. As a function of time, edges of the pits in the photoresist are progressively eroded as seen in Figs. 2B to 2E such that they assume an inverted trapezoidal shape with the height of the trapezoid becoming small with time. Meanwhile, the pits in the glass become increasingly deeper and are tapered downward with their side walls blending continuously with the side walls of pits in the photoresist. At the final stage of sputtering, pits 14 with a depth of about 0.1 micrometer are created in glass disc 10 as seen in Fig. 2F and the side walls of pits 14 forms an angle of 45 degrees with the horizontal. A series of microscopic pits of 0.1-micrometer depth is therefore formed in the glass master disc in a spiral pattern (Fig. 1C). The photoresist 11 which remains on the glass disc is removed under the environment of oxygen plasma to produce a complete master disc 15 (Fig. 1D). Master disc 15 is then applied with a coat of silver which is formed by conventional electroless plating (silvering) to make its surface electrically conductive. A coat of nickel is then applied onto the silver coat using electroforming technique. This process is repeated to produce a number of nickel molds for stamping audio or video discs on a mass-production basis. Fig. 3 is a graphic representation of the results of experiments involving the use of master discs on which photoresist layers of different thicknesses are deposited to determine the relationship between the taper angle ϑ and the photoresist thickness. The experiments show that the thickness of the photoresist plays a key role in forming the tapered-wall pits in a glass disc. In particular, the optimum taper angle of 45 degrees was observed when the thickness of the photoresist layer is 4000 angstrom units (4000 nm). This is considered to arise from the fact that the movement of the etchant gas is oriented only in one direction, rather than in all directions as exhibited by gases in the state of plasma. Since the thickness of the photoresist layer is a predominant factor, the desired taper angle can be easily obtained by controlling the thickness of the photoresist layer, while maintaining the sputtering conditions constant for a given set of glass material and etchant gas. This ensures a stable and efficient manner of production. A further advantage of the invention is that it requires only the photoresist material to be deposited on the glass substrate, which simplifies manufacturing process. It is preferable that the inactive compositions contained in the glass disc 10 be more than 10 weight percent. The inactive compositions of this amount reduce the tendency of the etchant material to provide chemical etching which would otherwise cause etching in sideways in photoresist layer 11 with the result that the pits in glass disc 10 would assume an undesired shape. In an alternative method, argon gas could equally be as well employed instead of CF₄ gas for sputtering the disc.

Claims: A method for fabricating a master recording disc using a master blank (12) comprising a glass substrate (10) and a photoresist layer (11), wherein the master blank is revolved and the photoresist layer is exposed to a laser beam which is modulated in intensity with a signal to be reproduced so that a series of optically excited regions is formed in track turns in said photoresist layer and said optically excited regions are removed to form a series of pits (13) in said photoresist layer, and wherein an etchant gas is used in an etching process to increase the depth of said pits (13), and the photoresist layer is removed after the etching process, characterized in that said photoresist layer (11) is directly deposited on said glass substrate (10) and in that said master blank is sputtered with said etchant gas until the pits (13) in said photoresist layer extend through and beyond the boundary surface of the photoresist layer (11) and the glass substrate (10) to a desired depth from said boundary surface and in that the thickness of the photoresist layer (11) is chosen in such a manner that when said desired depth is reached pits (14) having side walls tapered in a direction away from said boundary surface are formed in said substrate. A method as claimed in claim 1, characterized in that said glass substrate is composed of 90 or less weight percent of SiO₂ and 10 or more weight percent of a composition which is inactive to said etchant. A method as claimed in claim 1 or 2, characterized in that said etchant is CF₄. A method as claimed in claim 3, characterized in that said photoresist layer has a thickness of about 4000 angstrom units (400 nm).

Inventors: ABE, TOSHIRO, KAWAI, NOBORU, MURATA, KEI
Applicants: VICTOR COMPANY OF JAPAN, LIMITED
Application year: 1985
Main classification: G11B7
IPC codes: G11B23, G11B7, G03F7