METHOD FOR HIGH TEMPERATURE PHASE SEPARATION OF SOLUTION CONTAINING POLYMERS

Abstract: A process is disclosed for recovering polymer from a solu­ tion of the polymer in a solvent by high temperature phase sepa­ ration in which carbon dioxide is added to the solution, the solu­ tion and the added hydrocarbon are subjected to a temperature and pressure so that one liquid phase is formed and the pres­ sure is adjusted to form two phases, namely, a polymer-lean liquid phase and a polymer-rich liquid phase. The polymer-rich liquid phase is separated from the polymer-lean liquid phase, and the polymer is then recovered from the polymer-rich liquid phase.

Description: METHOD FOR HIGH TEMPERATURE PHASE SEPARATION OF SOLUTIONS CONTAINING POLYMERS The present invention relates to a process for recovering hydrocarbon copolymer from a solution of such polymer in a solvent by using temperature to cause a phase separation. More particularlp, the invention re- lates to a process for improving the efficiency of the separation of hydrocarbon -polymers from their solution in a solvent. In the manufacture of such polymers by solution polymerization, a common technique used to separate the polymers from the solution in which they are formed is by steam stripping. In this method, the polymer solution and steam are added to a drum of agitated hot water to flash distill the solvent. As the solvent is removed, the polymer precipitates and is recovered in the form of wet crumb particles by filtration or screening. These particles can then be dried by standard methods such as extrusion. Because of the cost of energy, including steam, the above method is expensive and various techniques have been explored for reducing the amount of steam and energy required for separation of polymers from. the solvents in which they were formed. One such technique is high temperature phase separation. A number of variations of the general technique are known. For example, U.S. Patent No. 3,553,156 discloses a. pro- cess in which a solution of ethylene copolymers elastomer in a solvent is heated, while maintaining a sufficient pressure to keep the solution in one liquid phase, to a temperature and pressure at which two liquid phases form, one of these phases being relatively rich in the elastomer. The polymer-rich phase is decanted and the polymer recovered from it by evaporation of the solvent. In this process, the patentees themselves state that it ii only necessary that the temperature and pressure are selected so that both phases behave like liquids. They also state, however, that the amount of unreacted monomer, such a8 propylene, will have its effect on the phase diagram for the polymer-in-solvent system, Similarly, U.S. Patent No. 3,496,135 discloses a process in which a polymerization reaction product mixture containing ethylene copolymer is admixed with an anti-degradation agent and, while maintaining sufficient pressure to keep the mixture in one liquid phase, the mixture is heated to a temperature at which two liquid phases form. The two liquid phases are separated by decantation and the solvent is evaporated from the copolymer-rich phase. The anti-degradation agent, e.g., a Lewis. base such as furan, diaklyl aluminum alkoxides, etc., is said to protect the copolymer from degradation under the temperature and pressure conditions necessary to produce a phase separation. Another such process is disclosed in U.S. Patent No. 3,726,843 in which a solution of an ethylene copolymer is heated to a temperature and pressure sufficient to form two liquid phases, one of which is a copolymer-rich liquid phase. The copolymer-rich liquid phase is separated from the other phase by decantation, and then passed under substantially adiabatic conditions into an intermediate lower pressure zone maintained at a pressure low enough to vaporize sufficient solvent to maintain a solvent vapor phase. The resultant copolymer-rich phase from the intermediate zone is then extruded under substantially adiabatic conditions into a subatmospheric zone at a rate below that at which fines of the copolymer are formed. The latter zone has a temperature and pressure which volatilizes residual solvent in the copolymer-rich phase, and produces an essentially solvent free product. Such prior art processes are subject to a number of disadvantages. For example, large amounts steam. are usually¯ used to heat the. polymer solutions to a sufficient temperature to obtain the phase separation. Depending upon the solvent used, these temperatures can be quite high, e.g., for ethylene-propylene copolymers dissolved in hexane, temperatures of about .5O.C are required. In view of the rising costs of steam energy, such high temperatures are undesirable. Moreover, aa noted in U.S. Patent No. 3,496,135, discussed above, at the temperatures necessary to achieve phase separation, degradation of the ethylene copolymers is possible. U.S. Patent No. 4,319,021 to Irani, et al., discloses a method for separating polymers from the solvents in which they are dissolved, by using low molecular weight hydrocarbons, e.g., C2-C4 hydrocarbons, to cause a phase separation 'into a polymer rich phase and a polymer lean phase. The separation occurs at about 1500C. It has now been. found that efficient phase separation and recovery of polymer from solution, for example, from solution polymerization reaction mixtures, can be achieved at lower temperatures, thereby reducing energy cost and decreasing the incidence of polymer degradation. These objectives are obtained by a process in which carbon dioxide is added to a solution of the polymer in a solvent. The polymer solution and added carbon dioxide are subjected to a temperature and pressure sufficient to form a polymer-rich liquid phase1 a polymer-lean liquid phase, and, optionally, a vapor phase rich in the carbon dioxide. The polymer-rich liquid phase is separated from the polymer-lean liquid phase and the vapor phase, if optionally formed, and the polymer is recovered from the separated polymer-rich liquid phase. In this process, addition of the carbon dioxide reduces the temperature at which an effective phase separation is obtained. Processes h accordance with the present invention for recovering polymer from a solution of said polymer comprises: (i) preparing the solution of polymer; (ii) adding to the thus-prepared solution of polymer an effective amount of carbon dioxide; (if) subjecting said solution including the carbon dioxide to a temperature and pressure at which a polymer-rich liquid phase and a polymer-lean liquid phase can form; (iv) separating said polymer-rich liquid phase from said polymer-lean liquid phase; and (v) recovering said polymer from said polymer-rich liquid phase. The polymer solution is preferably the' re action product mixture from a solution reaction, such as polymerization reaction, in which the polymer has been formed. The solution of polymer exits the reactor as an effluent stream to which the carbon dioxide can be added. If the effluent stream is deashed to remove cata lyst residues, the carbon dioxide could be added to the effluent stream before or after deashing. However, it is preferred that the C02 be added after deashing so as to avoid -the need for high pressure in the deashing equipment. In a preferred embodiment, the process of the present invention is applied to continuously separate polymer from a reaction mixture in which it was formed. In such a continuous process, the solvent from the 'solution reaction mixture is recovered from the polymerlean liquid phase and recycled back for use in forming a new solution reaction mixture. It is also preferred to recycle the vapor phase, if formed, and polymer-lean liquid phase so that they are brought into heat exchange contact with the reaction mixture and added carbon dioxide to supply part of the heat needed to increase the temperature of,the...reaction mixture and added carbon dioxide to the level required for phase separation. In another preferred embodiment, the added carbon dioxide is recovered from the polymer-lean liquid phase and this recovered carbon dioxide is then recycled back for use in the step of adding carbon dioxide. The polymer can be recovered from the polymerrich liquid phase by steam stripping. Alternatively, the polymer can be recovered by desolventizing extrusion. Solvent recovered from the polymer rich phase can also be recycled for use in forming tha polymer solution. Carbon dioxide is added to the solution of the polymer in a solvent in amounts effective for the purpose. These amounts are preferably from 5 to 24.9 wtZ, more preferably from 10 to 23.0 wtZ based on the weight of solution; most preferably from 15 to . 20 wtZ based on the weight of solution. The use of carbon dioxide is particularly advantageous, as compared to prior art compounds, for use in separating polymers from their solutions because removal of the CO2 from the polymer rich and polymer lean phases is substantially complete using minimum energy requirements. The reaction conditions for preparing polymers in solution are well known as are the solvents, comonomers, catalysts and cocatalysts for such systems. I1lustrative solvents which can be used in the reaction mixture for processes in accordance with the present invention include aliphatic or aromatic hydrocarbons and halogenated hydrocarbons such as pentane, hexane, 2methyl hexane, cyclohexane, benzene, toluene, dichloroethane, dichlorobenzene, and tetrachloroethylene. Preferred solvents are C5 to C7 hydrocarbons. Many hydrocarbon polymers can be separated from the solutions containing them by processes in accordance with the present invention. For example, copolymers of ethylene with a higher alpha-olefin such as propylene, l-butene, l-pentene, l-hexene and mixtures thereof can be recovered by the process of the present invention. A preferred ethylene copolymer elastomer is a copolymer of ethylene and propylene. The term "EEtf' as used herein means copolymers of ethylene and propylene. Also, terpolymers of ethylene with one of the above-mentioned higher alpha-olefins and a non-conjugated diene such as ethylidene norbornene, 1,4-hexadiene, cyclopentadiene, methylene norbornene, norbornadiene, tetrahydroindene, and 1,5 cyclooctadiene can also be recovered. A preferred terpolymer:contajns ethylene, propylene and 5-ethylidene norbornene. The term "EPDN" as used herein is used in ;the context ot its ASTM definition and includes the forego- ing terpolymers. Other polymers to which the process of this invention can be applied include polybutadiene, polyisoprene and styrene-butadiene rubbers produced by solution polymerization. Halogenated butyl rubbers can also be separated from their solutions. These polymers are well-known in the art and include halogenated rubber copolymers of isobutylene and isoprene which are normally produced using methyl chloride as diluent and a cationic catalyst such as aluminum trichloride. Preferably, the copolymers have an isobutylene content of from about 96 to 99.5 wtZ. The halogenated polymer desirably contains chlorine or bromine in an amount from about 0.5 to about 5.0 wtZ. Preferably, it contains from 0.5 to 2.5 wtZ of chlorine or from about 0.5 to 3.5 wtZ bromine. These halogenated butyl rubbers may be prepared by means known in the art. For instance, the butyl rubber may be dissolved in an inert hydrocarbon solvent such as pentane, hexane or cyclohexane and halogenated by addition to the solution of elemental chlorine or bromine. In a typical commercial process. butyl rubber is dissolved in a solvent to form a solution containing from about 5 to about 30 wtZ of rubber. Elemental chlorine or bromine is add sd to the solution, at a temperature of 0 to about lOOeC, in sufficient quantity that the chlorinated or brominated rubber recovered contains eg. 0.5 to 5xt% halogen. The temperature and pressure conditions for obtaining phase. separation' in the process of the present invention vary depending upon many factors including the molecular weight of the polymer and the composition of the solvent. Thus, no one set of temperature and pressure conditions can be defined for the process for the present invention. However, generally, the temperature should be chosen such that good separation of the polymer from the solvent and added carbon dioxide is obtained,ie., the polymer-lean liquid phase resulting after phase separation preferably contains less than 5wt% of the total polymer, more preferably less than lwt%. Preferably, the temperature is in the range of from 400C to 15O0C and the pressure is preferably in the range of from 100 to 3000 psig (0.69-20.7 MPag) during the phase separation step. Typically, the pressure of the polymer solution is increased to the desired level by a suitable pump. Carbon dioxide can be added either before or after pressurization. If added before, the pump must be capable of handling two phase mixtures. Such pressure is preferably in the range of from 100 to 3000 psig (0.69-2.07 MPag) and more preferably in the range of from 500 to 2000 psig (3.45-138 MPag). The temperature of the reaction mixture/carbon dioxide system is then increased by heat exchange with steam and/or recycled solvent and vapor from the phase separator. This temperature is preferably in the range of from 40 to 1500C, more preferably in the range of from 50 to 120 C. The pressure of the reaction mixture/carbon dioxide system is then reduced to. a. point. sufficient to give phase separation into the two liquid phases. Alternatively, the pressure can be reduced to slightly below the bubble point of the reaction mixture-hydrocarbon system. This pressure is normally in the range of from 200 to 1500 psig(l.38-l0.3MPag) but, of course, varies depending upon the solvent and polymer used. The sequence in which the CO2 is added to the polymer solution, the solution pressurized and the temperature raised can' be varied to obtain the most economical operation for the particular solvent/polymeriCO2 system. For instanc-e, it may be preferable to add the CO2 after. the solution is heated to minimize the pressure in the heat exchange equipment. If the C02 is added prior to heating, the pressure can be first raised to a high enough level that one phase is always present as the temperature is increased in subsequent heat es- change steps. After the final temperature is attained the pressure is lowered to cause phase separation. Alternatively, the pressure can be set at a lower level initially so that a two phase mixture forms as the temperature is raised. Depending upon the nature of the phases formed, this procedure may increase the rate of heat transfer to the polymer mixture by reducing the viscosity. Once the final temperature is reached, the pressure is then adjusted to give the desired phase separation. Many other. process variations are possible. However, it is necessary to select process conditions such that the polymer does not precipitate prematurely and cause fouling and plugging of equipment. A preferred process employs C5 to C7 hydrocarbons as the solvent for a reaction mixture containing either ethylene-propylene copolymers or halogenated butyl rubber. With such solvent and the carbon dioxide component, it is preferred to first raise the pressure of the reaction mixture/carbon dioxide system to from 200 to 2000 psig (1.38-13.8 MPag), The temperature is then preferably increased from reaction temperature to between 60 to 120"C, depending upon the solvent and CO2 concentration, after which the reaction mixture/hydrocarbon system is preferably passed through a valve into the phase separator lowering the pressure to, a final value of about 150 to about 1500 psig (1.03-10.34 MPag). If the optional vapour phase is to be formed,the final pressure depends upon various factors and is preferably from 0.5 to 10 psig(3.45-6.89 KPag) less than the bubble point of the mixture. Reference is now made to the accompanying drawings in which: Figure 1 is a schematic representation of a process in accordance with the present invention. Figure 2 is a phase diagram representing the polymer/solvent systems before and after addition of low molecular weight hydrocarbon. Figure 3 is a schematic diagram of the test equipment. Figure 4 is a phase diagram for an EPDM/CO2 solvent systems The process of the present invention is illustrated with reference to Figure 1 in which a continuous flow stirred reactor, 17, is fed through line, 1, witha solution of monomer(s) such as ethylene, propylene and ethylidene norbornene for the preparation of the desired polymer. A suitable polymerization catalyst such as Ziegler catalyst and organoaluminum cocatalyst can be fed to the reactor 17 through separate lines 3 and 4. Hydrogen for control of the polymer molecular weight may be added via line 5. The reaction forming the polymer takes place in the reactor, 17. The composition and molecular weight of the polymer can be varied by changing the proportions of the monomers, catalysts and cocatalysts in the reactor system and the temperature in the reactor. The polymer solution leaves the reactor 17 through line, 6, and the catalyst residues, can be removed in a deasher, 26, by techniques well known in the art. This mixture then enters cement pump, 8, and the pressure is raised to a suitable pressure. The carbon dioxide is added to the polymer solution through line, 7, in order to reduce the solubility of the polymer. By heat exchange in exchanger, 9, the temperature of the polymer solution is raised, for example, from about 400C to about 1000C. The temperature is further increased by heat exchange with high pressure steam which enters exchanger, 10, through line, 11. The heated, pressurized polymer solution and added carbon dioxide at this point are in one liquid phase. The solution and added carbon dioxide then pass through a valve, 18, to lower the pressure sufficiently for phase separation to occur and the mixture passes into separator, 13. As a result of the drop in pressure, two liquid phases form in the separator, 13. If it is desired to form the optional vapor phase, the pressure of the solution through valve 18 is-lowered to a point slightly below the bubble point of the solution, and a vapor phase and two liquid phases form in the separator. One of the liquid phases is a polymer-rich liquid phase. This polymer-rich phase leaves the separator via line, 15, and the polymer is recovered from it either by steam stripping to remove the remaining solvent followed by extrusion drying or by desolventizing extrusion. It is preferable that the process be continuous. In order to do so, any vapor generated in the phase separator, 13, is withdrawn through valve, 19, via line, 12. Valve, 19, also serves to maintain a constant pressure in the separator, 13, by means of a pressure control system. The polymer-lean phase is removed from the separator, 13, through line, 14, and combined in line, 16, with the withdrawn vapor, if any. The vapor phase and polymer-lean phase contain a high heat content and are used in heat exchanger, 9, to supply some of the heat needed to raise the temperature of the polymer solution coming from the cement pump, 8. This stream of vapor and polymer-lean solution then goes to a recycle purification system, 24-, which consists of a series of distillation towers, where it is separated into solvent, which is recycled to the reactor, 17, via line, 21, propylene which is recycled via line, 2, for use in the polymerization reaction mixture, and carbon dioxide which can be recycled through line, 20, for reuse. The recycle purification system, 24, also has -two purge streams, 22, and, 23, to dispose of unwanted low boiling components such as hydrogen (purged via line, 23) and higher boiling components such as oligomers (purged via line, 22). The effect of adding the carbon dioxide in accordance with the present invention is illustrated schematically in Figure 2. Diagram 1 represents an exemplary solvent/polymer phase diagram in the absence of any added carbon dioxide. Diagram 2 represents the effect of the addition of carbon dioxide on the same solvent/ polymer system. The pressure, P, is the total pressure on the system and the temperature, T, is the temperature of the polymer solution. In both diagrams, area I represents the temperature and pressure region in which the solution reaction mixture with or without the added carbon dioxide exists as a single liquid phase; area II represents conditions at which the solution reaction mixture with or without the added carbon dioxide form two liquid phases, one being a polymer-rich liquid phase and the other being a polymer-lean liquid phase; and area III represents conditions at which the two liquid phases and a vapor phase are formed. As illustrated by Figure 2, the whole phase diagram for the polymer/solvent system is shifted to lower temperatures when the carbon dioxide is added. Thus, separation of the solvent/polymer system into two liquid phases or, optionally, into two liquid phases and a vapor phase, in accordance with the present invention occurs at a lower temperature, thus decreasing the amount of energy needed to heat the polymer/solvent system to the temperature necessary to obtain efficient phase separation and also decreasing the incidence of polymer degradation due to high temperatures. Also, by decreasing the pressure in the phase separator to a point slightly below the bubble point of the polymer solvent system a more concentrated polymer-rich liquid phase may be obtained. The advantage of the present invention may be more readily appreciated by reference to the following example which illustrates the effectiveness of CO2 in reducing the temperature at which a polymer solution can be made to separate into phases. Shown in Figure 3 is a schematic diagram of the experimental apparatus used in this study. The carbon dioxide is charged at ambient temperature to a compressor where it is compressed and delivered to a holding tank located in a forced convection air bath where the temperature in the air bath is maintained constant to with t 0.10C. With holding tank inlet and gauge exit valves closed, the pressure of the gas is measured with a Bourdon-tube Heise gauge with a range of 0-5000 psig(O-34.48MPag) and an accuracy of + 5 psi (34.48 MPag) to determine when the gas attains thermal equilibrium with the bath air. The amount of gas in the holding tank is determined from the gas density and the volume of the holding tank. The gas is then transferred to the high pressure view cell to which a measured amount of polymer solution has previously. been charged. The amount of gas transferred is determined by a mass balance based on the density of the gas remaining in the holding tank and the transfer lines, and the volume of the tank and lines. The variable volume, high pressure, view cell is maintained at a constant temperature normally within t 0.1eC as determined by a platinum resistance element located on the outside skin of the cell. The cell contents, illuminated by a 0.25 in. (0.63cm) fiber light pipe, are viewed through a 1.0 in(2.54cm) thick,2.75in(6.98cm) diameter quartz window. The cell contents are mixed by a magnetic stirring bar activated by a magnet located below the cell. The contents can be compressed to any desired operating pressure by a movable piston fitted with teflon o-rings and driven by a low vapor pressure silicon fluid which is pressurized by a syringe type pressure generator. In this manner the pressure of the test mixture is adjusted at fixed overall composition by varying the mixture volume. The boundaries of the three regions shown in Figure 2 were determined in this study. The technique for determining each of these boundary curves is described below. Region III - Region I Boundary (Liquid + Vapor - Liquid Boundary) Initially, both vapor and liquid are generally present in the view cell. While maintaining vigorous mixing, the system pressure is slowly increased at a constant temperature until the final bubble of vapor disappears. with a single liquid now in the view cell, the system pressure is slowly decreased until a small vapor bubble appears. The system pressure is alternatively raised and lowered in this manner to delineate the Region III - Region I phase transition. Region III - Region II Boundary (Liquid + Liquid + Vapor -- Liquid + Liquid Boundary) The experimental technique in this case is similar to that for the above case. However, there are now two liquid phases present throughout the experiment. In this instance, the two liquid phases present were generally opaque and grayish as opposed to théwprevious case where the single liquid phase was very clear. In most cases, the heavier of the two liquid phases appeared to be very viscous, indicating that this phase was very rich in polymer. Although both liquid phases were generally opaque, visual determination of vapor bubble formation was not impeded. Region II- - Region I Boundary- (Liquid + Liquid - Liquid Curvet Initially two grayish liquids were generally present in the view cell. While maintaining vigorous mixing at a constant temperature, the system pressure was isothermally increased until the two grayish liquids merged into a single clear liquid. In the LL region, the heavy polymer phase separates from the light solvent phase and settles within seconds of turning off the mixer. However, when operating very near the Region II Region I phase boundary, settling times increase by as much as two orders of magnitude (i.e., tens of minutes). The pressure for this transition is defined as being in the interval between a clear cell condition in which a second phase does not settle after approximately 10 minutes without mixing, and a cloudy cell condition which is completely opaque and where a meniscus separating the two liquid phases may or may not be discernible after approximately 10 minutes without mixing. EXAMPLE A 5.2 wtZ solution of an ethylene propylene copolymer was prepared in a hexane solvent sample which analyzed about 87.35 wtZ n-hexane, 9.43 wtZ methyl-cyclopentane and about 2,26 wtZ 3-methyl-pentane, the remainder of the solvent being C5-6 hydrocarbon compounds including dimethylbutene, pentane and benzene. The polymer had an ethylene content of 42.8 wtZ, an of 67,000, and an my of 145,000. Carbon dioxide was added to a concentration of 13.5 wtZ based on the total solution weight. The experimental pressure-tepperature data for the system are shown in Table I. As shown in Figure 4, phase separation into two liquid phases is possible at temperatures of 102.5 C or higher. In comparison, in the absence of CO2, a temperature of about 2100C is required. Thus, it is evident that carbon dioxide is an effective agent to lower the temperature at which the polymer can be separated from the solvent in which it is dissolved. Of course the separation temperature can be further reduced by increasing the CO2 concentration. TABLE I Experimental P-T Data for the Hexane-EPM-Carbon Dioxide (13.5 Wt %) Systems Pressure Pressure Temperature Phase (psia) (MPag) ( C) Transitions 794.7 # 2.0 5.48#0.014 95.0 # 0.1 LV --- L 872.7 # 4.0 6.02#0.28 114.8 # 0.4 LLV --- LL 960.7 # 17.0 6.62#0.117 132.3 # 0.2 LLV --- LL 1198.7 # 29.0 8.26#0.200 115.2 # 0.2 LL --- L 1671.7 # 25.0 11.53#0.172 132.2 # 0.2 LL --- L

Claims: CLAIMS 1. A process for recovering hydrocarbon polymer from a solution thereof which comprises subjecting said solution to conditions of temperature and pressure so as to establish therein a polymer-rich liquid phase and a polymer-lean liquid phase, separating the two liquid phases and recovering polymer from the polymer-rich phase, characterised in that carbon dioxide is incorporated in said solution in an amount effective to reduce the temperature required to establish the two liquid phase systems. 2. A process for the recovery of hydrocarbon polymer from a solution of said polymer comprising: (i) preparing the solution of polp erss (ii) adding to the thus-prepared solution of polymer an effective amount of carbon dioxide whereby the solution and added carbon dioxide exhibit a phase separa tion diagram in accordance with Figure 2 (iii) subjecting said solution including said carbon dioxide to a temperature and pressure at which a polymer-rich liquid phase and a polymer-lean liquid phase can form; (iv) separating said polymer-rich liquid phase from said polymer-lean liquid phase; and (v) recovering said polymer from said polymer-rich liquid phase. 3. A process according to Claim 1 or 2 wherein from 5 to 24.9% by weight of carbon dioxide is incorporated in the solution, based on the weight of solution without added carbon dioxide. 4. A process according to Claim 3, wherein from 10 to 23.0 wt% of carbon dioxide is incorporated. 5. A process according to Claim 4, wherein from 15 to 20 wt% of carbon dioxide is incorporated. 6. A process according to any one of the preceding claims, wherein said polymer comprises halogenated butyl rubber, an ethylene higher alpha olefin copolymer elastomer or a terpolymer of ethylene, a higher alpha olefin and a non conjugated diene. 7. A process according to Claim 6, wherein the higher alpha olefin is propylene and/or the non-conjugated diene is 5-ethylidene norbornene. 8. A process according to Claim 6, wherein said halobutyl rubber is chlorinated butyl rubber or brominated butyl rubber. 9. A process according to any one of the preceding claims wherein the solution comprises, as solvent, an aliphatic, aromatic or halogenated hydrocarbon. 10. A process according to any one of the preceding claims wherein said solvent is a C5 to C7 hydrocarbon. 11. A process according to any one of the preceding claims wherein carbon dioxide is incorporated in an amount effective to reduce the temperature at which the two liquid phase system forms by at least 100 C, relative to the system in the absence of carbon dioxide. 12. A process according to any one of the preceding claims wherein the temperature and/or pressure to which the solution is subjected are in the ranges 4O-iSO0C and/or 100-3000 psig(0.69-20.7 MPag) respectively. 13. A process according to any one of the preceding claims wherein the polymer-lean liquid phase contains less than 5 wtt of the total polymer. 14. A process according to any one of the preceding claims wherein the solution of polymer is prepared in a reactor and exits from said reactor as an effluent stream, and wherein said carbon dioxide is added to said effluent stream. 15. A process according to Claim 14, wherein said effluent stream is deashed to remove catalyst residues, prior to addition of the carbon dioxide. 16. A process according to any one of the preceding claims, wherein a vapour phase rich in carbon dioxide is also formed, in addition to the polymer-rich and polymer-lean liquid phase.

Inventors: COZEWITH, CHARLES, HAZELTON, RONALD LEWIS
Applicants: EXXON RESEARCH AND ENGINEERING COMPANY
Application year: 1985
Main classification: C08F6
IPC codes: C08F6, C08F8, C08F210