PHOTOLITHOGRAPHIC METHOD

Abstract: A photobleachable layer has been found to improve the resolution limits of two-layer photoresists for making inte­ grated circuits.

Description: Significant advantages are achieved in photolithography when two-layer resists are used to produce a pattern on a suitable substrate in the fabrication of electronic deVices or integrated circuitry on semiconductor chips. The use of such two-layer photoresists are described, for example, in EP-A-O 002 999. Depth of focus limitations are minimized by confining primary imaging to a positive photoresist which is uniformly applied as a thin film on top of a thick planarizing polymer layer, such as a polymethylmethacrylate. A suitable dye which absorbs in the active region of the thinly applied upper positive resist layer can be incorporated into the thicker PMMA planarizing base layer. The dye can absorb any stray light which might tend to reflect from the supporting substrate back to the thin upper positive resist layer interfering with a sharp resolution in the resulting portable conformable mask (PCM) obtained from the upper positive photoresist. Methods and compositions useful in the application of the PCM to microlithography are described in IBM Technical Disclosure Bulletin, Vol 25, No. 11B, April 1983, pages 5922-5924. Although improved results have been achieved with the two-layer photoresist procedure as shown by Chen et al., US patent 4,362,809, variations in the profiles and thickness of the upper resist pattern can reduce its effectiveness as a mask during deep UV exposure of the lower resist layer. Rounded contours and lack of uniformity in the thickness of the final vertical resist profiles often can result. As we have previously discovered and disclosed in EP-A-O 110 165, improved results in microlithography can be obtained by applying a Contrast enhancing layer to a novolac resist layer which is developed after exposure to an aerial image obtained by UV light passed through a mask. The present invention is based on the discovery that improvement in wall profiles and problems associated with reflections and diffraction effects, such as remnants of resist residue, as shown by Figures 2a and 3a, can be substantially eliminated as, shown by Figures 2b and 3b, by combining contrast enhanced photolithography with the aforementioned two-layer photoresist technology. In a photolithographic method using a two-layer photoresist resulting in an incomplete resolution of the lower photoresist layer due to variations in the profile and thickness of the upper photoresist pattern, the improvement which comprises, applying a photobleachable film onto the surface of the upper photoresist layer prior to exposing the two-layer photoresist to patterned UV light, thereby reducing the variations and thickness of the resulting portable conformable mask obtained from the development of the exposed upper photoresist layer and improving the resolution of the resulting patterned photoresist relief obtained from the subsequent exposure and development of the lower photo-resist layer. There is shown more particularly in Figure 1, a photoresist composite which can be used in the practice of the present invention which can be used to pattern various substrates during the fabrication of electronic devices and integrated circuits. In Figure I, PMMA means polymethylmethacrylate having an absorbant dye which is used to make a thick planarizing antireflecting photosensitive polymer layer, positive resist layer means a photoresist, such as a polynovolak, which can be used to produce an upper portable conformable mask (PCM). There is also shown at Figure 1, a contrast enhancement layer (CEL) which contains a photo-bleachable compound which will be defined more fully hereinafter. In order to more fully understand the advantages of the invention, reference is made to the drawings. In Figure 1, there is shown a sectional view of a silicon substrate coated with a layer of PMMA, novolac and GEL. Figures 2a, 2b, 3a and 3b show results obtained with and without the use of CEL, such as differences in grating patterns and forked line ends. There is shown more particularly in Figure 2a, line 15 and Figure 3a, line 15, incompletely resolved grating patterns, forked line ends in Figure 2a, line 10 and Figure 3a, line 20, while Figure 3b shows a section free of such defects. The invention also resides in a photolithographic method for forming a patterned photoresist relief from a two-layer photoresist which comprise the steps of (1) depositing at least a first resist on a substrate to produce a bottom resist layer having a substantially planar top surface, and depositing a second resist as a top resist layer to produce a multilayer substrate coating with the bottom resist layer between the substrate and top resist layer, (2) exposing the top resist layer to light in a range in which the second resist is insensitive, said light having been passed through a mask to expose only selected portions of the top resist layer, and (3) thereafter developing the top layer to produce a portable conformable mask and the layers of the substrate coating other than the top resist layer processed to replicate the pattern of the portable conformable mask in such layers. whereby an incomplete resolution of the bottom photoresist layer is obtained due to variations in the profile and thickness of the upper photoresist pattern, characterised in that a photobleachable film comprising an arylnitrone and an inert organic polymer binder is applied onto the surface of the upper photo-resist layer prior to exposing the two-layer photoresist to patterned UV light in an amount sufficient to reduce the variations and thickness of the resulting portable conformable mask obtained from the development of the exposed top photoresist layer and to improve the resolution of the resulting patterned photoresist relief obtained from the subsequent exposure and development of bottom photoresist layer. Among the polymethylmethacrylates which can be utilized in the practice of the present invention to make the initial antireflective resist layer at the surface of the interface, as shown in Figure 1, are for example, Elvacite® 2041 and 2010 of the DuPont de Nemours Company, Wilmington, Delaware; KTI standard PMMA resist, etc. As taught in our copending application Serial No. 619,526, the aforementioned PMMA resist can be utilized in combination with an absorbant dye such as the 1,3-propane diol diester of methyl(p-diethylamino-α-cyano)cinnamic acid or coumarin. The PMMA resist layer can be applied onto a substrate such as a silicon substrate or glass substrate in the form of a spin castable mixture, comprising 100 parts of an inert organic solvent, for example, toluene, chlorobenzene, methylisobutylketone, etc., where there can be utilized 100 parts of the organic solvent, 1-15 parts of the PMMA and .01-1.0 parts of the absorbant dye. The dye can be absorbing at about 436 nm and nonabsorbing at about 220-250 nm. Among the positive photoresist compositions which can be used in the production of the PCM (portable conformable mask), there are included novolak resins modified with naphthoquinonediazides as shown in the chemical behavior of positive working systems by Jeffrey C. Streeter, Eastman Kodak Company, Proceedings of the Microelectronic Seminar Interface '76, pp. 116-121. A typical reaction for preparing these positive photoresists is to react the hydroxyl groups on a phenol-formaldehyde resin with naphthoquinone-diazide sulfonyl chloride. The most common solvents used in the novolak positive resists are 2-ethoxyethylacetate and 2-methoxyethylacetate. In some cases, xylene and butylacetate can be incorporated into the solvent system to give various drying and coating characteristics. Spin castable mixtures which can be utilized to form the CEL shown in Figure 1, are more particularly described in our copending application Serial No. 536,923. There can be utilized, for example a mixture comprising by weight, (A) 100 parts of an organic solvent, (B) 1-30 parts, preferably 5-15 parts of an inert organic polymer binder, and (C) 1-30 parts, preferably 5-15 parts of an aryl nitrone. Aryl nitrones which can be used in the practice of the method of the present invention to make the photobleachable layer are included by the formula In formula 1, Z is a monovalent group selected from (R³) a -Q-R⁴- or R⁵-, and Z' is a monovalent group selected from -R⁶(X) b , R, R¹, R² and R³ are monovalent radicals selected from the class of hydrogen, C (1-8) alkyl, C (1-8) substituted alkyl, C (6-13) aryl hydrocarbon and C (6-13) substituted aryl hydrocarbons. Q is a monovalent, divalent or trivalent atom selected from the group F, C, Br, I, O, S, N, where a can have values of 0, 1 or 2. R⁴ is a C (6-13) aryl hydrocarbon or a C (6-13) substituted aryl hydrocarbon. R⁵ is selected from the group of substituted or unsubstituted C (6-20) aromatic heterocyclic compounds incorporating one or more atoms from the group O, N or S. R⁶ is selected from the group of C (6-20) aromatic hydrocarbons and X is selected from the group of halo, cyano, alkyl carbonyl, C (1-8) alkyl, C (1-8) substituted alkyl, C (6-13) aryl hydrocarbon, C (6-13) substituted aryl hydrocarbons, or alkoxy carbonyl in any combination for values of b which can be 0, 1, 2 or 3, n can have a value of 0, 1, 2, 3 or 4. The above compounds can be prepared using procedures such as those described in "Methoden der Organischen Chemie (Houben-Weyl), Vol. 10, part 4 (1968), pages 315-416, or those described in Chemical Reviews 1 (64), Nitrones, by Jan Hamer and Anthony Macaluso, pages 476-483. Various aryl ring systems with a variety of substituents may be constructed to suit the particular needs of the optical system employed in the photoimaging process. The aryl nitrones exhibit extinction coefficients of 2 to 5 x 10⁴ liter mole⁻¹cm⁻¹ and bleach with quantum yields in the range of 0.1 to 0.5. For direct-step-on-the wafer systems capable of imaging at 405 nm, the following nitrones have been found to be particularly useful, where Ar is a C (6-13) monovalent aromatic organic radical or substituted C (6-13) monovalent aromatic organic radical and n is equal to 0 or 1. Included among this subclass of p-aminoaryl nitrones , are heterocyclic compounds such as Suitable binders for use in providing a spin castable mixture for the formation of a photobleachable layer incorporating the aryl nitrones of formula (1) are: vinyl acetate polymers (homopolymers and copolymers) and their partially saponified products (e.g., polyvinylacetate), copolymers of styrene or its derivatives, polymers and copolymers of acrylate or methacrylate esters, acetal resins, acrylonitrile/butadiene copolymers, ethyl cellulose and other hydrocarbon-soluble cellulose ethers, cellulose propionate and other hydrocarbon-soluble cellulose esters, poly(chloroprene), poly(ethylene oxide), polyvinylpyrrolidone). Suitable solvents for use in providing a spin castable mixture to form the photobleachable layer which incorporates the aryl nitrone of formula (1) are: aromatic hydrocarbons (e.g. toluene xylenes, ethyl benzene, chlorobenzene) with or without aliphatic hydrocarbons (e.g. cyclohexane), halogenated aliphatic compounds (e.g. trichloroethylene, methyl chloroform, alcohols (e.g. propanol, butanol). Diaryl nitrones of formula 2, where R³ is CH₃CH₂-and n = 0 have been found to be particularly useful. For example, α-(4-diethylaminophenyl)-N-phenylnitrone, was found to absorb strongly at 405 nm, and it bleaches to near transparency with high efficiency at the same wavelength by undergoing unimolecular cyclization to an oxaziridine. It is very soluble in solvents of moderately low polarity (e.g., toluene, ethylbenzene) and forms good films at high loading densities with a variety of polymers such as polystyrene, poly(hydroxyethylmethacrylate), poly-α-methylstyrene, poly(methylmethacrylate), polyvinylpyrrolidone, vinylpyridine/styrene copolymers and allyl alcohol/styrene copolymers. In addition, α-(4-diethylaminophenyl)-N-phenyl-nitrone has an extinction coefficient to weight ratio of 130 liters/gram-cm at 405 nm. It can be formed into a contrast enhancing layer by forming a 8% solution in toluene with styrene/allyl alcohol copolymer as a binder. In the practice of the method of the present invention, a composite photoresist structure, as shown by Figure 1 is made by initially spin casting in a conventional manner, a polymethylmethacrylate resin onto a suitable substrate such as a silicon substrate, for example, a silicon wafer, utilizing a solution of the polymethylmethacrylate resin in an organic solvent such as toluene, which also can contain an absorbant dye as previously indicated. There can be used a mixture of 100 parts of the organic solvent, 1-15 parts of the PMMA and .01 to 1 part of absorbant dye. After the PMMA layer has been spun onto the surface of the substrate, it can be baked to a temperature of 140-200°C to produce a polymethylmethacrylate resist layer having a thickness of from 1-3 microns. A positive photoresist then can be applied to a thickness of from about 0.1-1.0 microns. The positive photoresist, which can be a novolak resin modified with naphthoquinonediazide utilized in a solvent, such as 2-ethoxyethylacetate or 2-methoxyethylacetate, or in some cases xylene and butylacetate, also can be spun onto the PMMA surface to a thickness of about 0.5 microns. The positive novolak resist then can be baked at a temperature in the range of 70-90°C for a period of 1-30 minutes. The contrast enhancement layer can be spun onto the surface of the positive photoresist to a thickness of about 0.2 to 1.0 microns. Exposure of the photolithographic composite of Figure 1 can be accomplished with mercury arc lamp having an intensity of 100 mw/cm² and a wavelength of from 360-40 nm for a period of from 0.3 to 1 second. The contrast enhancement layer and positive photoresist layers can be exposed simultaneously using a printer operating at the appropriate wavelength. The removal of the contrast enhancement layer (CEL) is best accomplished by spraying the CEL with an appropriate solvent such as trichloroethylene. After removal of the CEL, the positive resist is then developed with a conventional developing solution, such as an aqueous alkali hydroxide. The NaOH should have a molar concentration in the range of from 0.2 to 0.5 for optimum results. If desired, the developed PCM then can be oxygen plasma cleaned in accordance with the procedure of Petrillo et al, Submicrometer Contact Hole Delineation with a Two-Layer Deep-UV Portable Conformable Masking System, J. Vac. Sci. Technol. B 1(4), Oct.-Dec. 1983. The positive resist PMMA composite can be exposed to UV irradiation having a wavelength of from 190 to 250 nm. The resulting exposed PMMA composite can be developed utilizing a standard acetone/isopropanol solution to produce a patterned PMMA photoresist layer on a an appropriate substrate, such as a silicon wafer, useful for making a semi-conductor device. In order that those skilled in the art will be better able to practice the invention, the following example is given by way of illustration and not by way of limitation. All parts are by weight. Example 1 . A chlorobenzene solution of 8% PMMA (Elvacite® 2041) and .4% of the 1,3-propane diol diester of methyl(p-diethylamino-α-cyano)cinnamic acid was spun-cast onto two silicon wafers. Two coats of the resin solution wore applied with a 30 minute bake at 180°C after each coat. The resulting "yellow PMMA" film on each wafer was coated at 5000 rpm with Shipley 1450B photoresist and baked for 7 minutes at 85°C. One of the waters was then coated with a contrast enhancing layer (CEL) using a solution containing 8% by weight of α-(4-diethylaminophenyl)-N-phenyl nitrone and 8% by weight of an ally] alcohol styrene copolymer in ethyl benzene. The wafers were then exposed using an Optimetrix 8010 stepper with a matrix of exposures. The wafer with the CEL was spray stripped for 15 seconds with trichloroethylene and then spray developed for 15 seconds with Shipley 351 developer diluted one part with three parts water. The wafer without the CEL was directly spray developed with a higher contrast developer, i.e. Shipley 351 diluted one part with 5 parts water for 25 seconds. Both wafers were then flood exposed for 75 seconds using a Fusion Systems deep UV source equipped with a mercury lamp. The wafers were subsequently spray developed using diglyme and rinsed with isopropanol. From the original exposure matrix, die with the best quality 0.8 µ line and space patterns were selected. This corresponded to 2150 milliseconds for the wafer with CEL and 660 milliseconds for the wafer without CEL. The wafer without GEL showed resolved 0.8 µ line/space patterns with small defects. The same die, however, had incompletely resolved 0.65 µ grating patterns, as shown by 15 in Figures 2a and 3a and pronounced defects resulting in forked line ends, as by 10 of Figure 2a and 20 of Figure 3a. By contrast, the die on the CEL wafer with good 0.8 µ grating also had line/space patterns of 0.65 µ which were cleanly resolved and free of defects.

Claims: A photolithographic method for forming a patterned photoresist relief from a two-layer photoresist which comprises the steps of (1) depositing at least a first resist on a substrate to produce a bottom resist layer having a substantially planar top surface, and depositing a second resist as a top resist layer to produce a multilayer substrate coating with the bottom resist layer between the substrate and top resist layer, (2) exposing the top resist layer to light in a range in which the second resist is insensitive, said light having been passed through a mask to expose only selected portions of the top resist layer, and (3) thereafter developing the top layer to produce a portable conformable mask and the layers of the substrate coating other than the top resist layer being processed to replicate the pattern of the portable conformable mask in such layers, whereby an incomplete resolution of the bottom photoresist layer is obtained due to variations in the profile and thickness of the upper photoresist pattern, characterised in that a photobleachable film comprising an arylnitrone and an inert organic polymer binder is applied onto the surface of the upper photo-resist layer prior to exposing the two-layer photoresist to patterned UV light in an amount sufficient to reduce the variations and thickness of the resulting portable conformable mask obtained from the development of the exposed top photoresist layer and to improve the resolution of the resulting patterned photoresist relief obtained from the subsequent exposure and development of bottom photoresist layer. A method as claimed in claim 1, characterised in that the two-layer photoresist comprises a polymethylmethacrylate layer coated with a polynovalak resin. A method as claimed in claim 1 or claim 2, characterised in that photobleachable film comprises α-(4-diethylaminophenyl)-N-phenylnitrone and a styrene/allylcohol copolymer. A method as claimed in claim 2 or claim 3, characterised in that the polymethylmethacrylate layer contains an effective amount of 1,3-propanediol diester of methyl(p-diethylamino-α-cyano)-cinnamic acid.

Inventors: GRIFFING, BRUCE FREDRICK, WEST, PAUL RICHARD
Applicants: MICROSI, INC. (A DELAWARE CORPORATION)
Application year: 1985
Main classification: G03F7
IPC codes: G03C1, G03F7, H01L21, G03C5