PROCESS FOR PRODUCING A DIENE POLYMER

Abstract: A process for producing a diene polymer, characterized by polymerizing a conjugated diene in an aqueous system in the presence of a catalyst system prepared by adding, to a catalyst obtained preliminarily by contacting (A) a cobalt compound with (B) an organometalic compound or hydride of a metal of Groups I to III of the Periodic Table in the presence of 1 to 100 moles, per mole of (A), of a conjugaged diene, (C) at least one member selected from the group consisting of carbon disulfide, phenylisothiocyanic acid and a xanthogen compound and further in the presence of at least one member selected from the group consisting of a surfactant, a dispersant and a polymer solution. According to this process, there can be obtained a bead polymer having a uniform particle diameter in a good dispersion state.

Description: PROCESS FOR PRODUCING A DIENE POLYMER This invention relates to a process for producing a diene polymer by stereoregularly polymerizing a conjugated diene in the presence of water. Numerous studies have been made on the production of stereoregular polymers using transition metals since the Ziegler invention. The production of stereoregular polymers using transition metals is characterized in that the stereoregularity of the microstructure of the polymer formed is very high. Polymers having a regular microstructure cannot be produced by emulsion polymerization, radical polymerization, or the like. However, polymerization using transition metals is disadvantageous in that it is very liable to be affected by oxygen and water. As the polymerization of a diene monomer using a transition metal, there is known, for example, po;Emeriza- tion of cis-butadiene using a Ni compound-BF3OEt2-AlR3 catalyst system. In this polymerization, water hinders the polymerization strongly. Also in polymerization of cis-isoprene using a TiC14-AlR3 catalyst system, water is a very strong polymerization-inhibitor. It is also known that in production of a 1,2-polybutadiene using a catalyst system consisting of a cobalt compound, an organoa uminum and carbon disulfide, the presence of water reduces the polymerization activity (Japanese Patent Publication Nos. 19,892/72 and 5,436/79). Further, in polymerization using an organic solvent, a 1,2-polybutadiene deposits with the progress of polymerization, the reactor contents become slurry, and sufficient stirring becomes impossible upon further porgress of polymerization. Meanwhile, there are cases where water is used along with a transition metal catalyst component. For example, there are known a cis polymerization of butadiene using a cobalt compound-AlEt2C1-H20 catalyst system [MORRIS GIPPIN et al., I & E PRODUCT RESEARCH AND DEVELOPHENT 1, (1), 32 (1962)] and a 1,2-polymerization of butadiene using a cobalt phosphine complex-AlR3-=20 catalyst system (Japanese Patent Publication No. 32,426/69). It should be noted, however, that the former catalyst system is effective only when water is present in a very samll amount (the amount of water is optimum when the molar ratio of water to aluminum is about 0.2) and no polymerization takes place in the presence of a large amount of water. Even in the latter catalyst system, the optimum amount of water is 0.5 to 1.0 in terms of molar ratio of water to aluminum, and the use of a small amount of water is effective, but no polymerization is caused in the presence of a large amount of water. As in the above cases, in stereoregular polymerization using a transition metal catalyst, it has heretofore been considered that water is effective only when it is present in a very small amount, or water is a strong polymerization inhibitor even in a small amount. Therefore, in solution polymerization using a transition metal, a polymerization solvent is purified to remove oxygen and/or water present in the solvent by applying a special measure to the recovery system of the solvent. The water present in the solvent, in particular, cannot be significantly reduced in many cases by a method such as mere distillation or the like; therefore, the solvent is being treated in a column packed with a drying agent such as a molecular sieve, silica gel or the like. Thus, the process is complicated and the production cost is affected to a not negligible extent. Separately, there are processes for producing a crystalline 1,2-polybutadiene by aqueous suspension polymerization [USP 4,429,085, Japanese Patnet Application No. 2,575/84 and Japanese Patent Application Kokai (Laid Open) No. 78,213/84]. However, polymers obtained by these processes have non-uniform shapes and hence these processes are hardly called suspension polymerization processes, and are rather close to bulk polymerization in water and polymers formed become large lumps, which makes it difficult to control the reaction and product quality, transfer the product and remove the residual catalyst in the product. As a result of extensive study, the present inventors have succeedec in stereoregular polymerization of a diene monomer usinc a transition metal in accordance with a suspension polymerization method in the presence of a large amount of water. We have also succeeded in aqueous polymerization of a diene monomer for obtaining a bead polymer having a uniform particle diameter in a good dispersion state. According to this invention, there is provided a process for polymerizing a conjugated diene, characterized by polymerizing a conjugated diene in an aqueous system in the presence of a catalyst system prepared by adding, to a catalyst obtained preliminarily by contacting (A) a cobalt compound with (B) an organometallic compound or hydride of a metal of Groups I to III of the Periodic Table in the presence of 1 to 100 moles, per mole of (A), of a conjugated diene, (C) at least one member selected from the group consisting of carbon disulfided, phenylisothiocyanic acid and a xanthogen compound and further in the presence of at least one member selected from the group consisting of a surfactant, a dispersant and a polymer solution. According to this invention, polymerization is conducted in an aqueous system in which water is present in the polymerization system. Accordingly, it is advantageous in that the viscosity of the polymerization system can be reduced and the temperature control of the polymerization system becomes easier. Further, as compared with the ordinary solution polymerization requiring a recovery system because of the use a large amount of a solvent, this invention requires only a small scale recovery system or no recovery system. Furthermore, in this invention, there is no need of difficult and complicated treatments such as previous dehydration of monomers or the like, etc. In addition, this invention is further advantageous in that polymerization can be conducted in a good dispersion state, a polymer have a uniform particle diameter, for example, a bead polymer, can be obtained, the control of reaction and product quality is easy, the transfer of product is easy, and the removal of the residual catalyst in the product is also easy. In this invention, when at least one member selected from a surfactant and a dispersant is present in the polymerization system, the following advantages are obtained as compared with the absence of them: (1) The control of polymerization conditions (temperature, stirring, etc.) is easier. (2) In the absence of a dispersant or the like, the resulting polymer is in the form of a large lump and adheres to a stirrer, etc., which makes the transfer of the polymer impossible; hence, polymer production on an commercial scale becomes impossible. On the other hand, when a dispersant or the like is used, the polymer formed is in the form of a dispersion of relatively uniform and small particles; so the transfer and handling of the polymer is easy. (3) Since the resulting polymer particles have fine and uniform diameters, the control of polymer quality is easier. If the polymer particles have large diameters, the quality control is made impossible by heat generaticn inside the particles. (4) Since the polymer particles have fine and uniform diameters, the removal of the residual catalyst in the polymer is easy. Further, in this invention, when a conjugated diene is polymerized in an aqueous system in the presence of a polymer solution, the following advantages are obtained: (1) By addition of water to polymer solution followed by stirring, the whole system becomes heterogeneous (water in polymer solution or polymer solution in water), whereby the viscosity of the polymerization system is greatly reduced and the energy required for stirring is reduced, resulting in an easier stirring. (2) In the production of a cis-1,4-polybutadiene, an EPDS or the like, water is used for termination of polymerization or removal of catalyst. Even a watercontaining polymer solution as obtained above can be used as it is, namely without dehydration, in the polymerization of a conjugated diene of this invention. In this invention, the polymerization of a diene monomer has become possible even in the presence of a large amount of water by the preliminary preparation of the catalyst under specific conditions. The cobalt compound (A) used in the process of this invention includes, for example, cobalt salts of organic acids such as cobalt octylate, cobalt naphthenate, cobalt benzoate, cobalt nitrate, cobalt malonate, cobalt acetate and the like; cobalt complexes such as cobalt bisacetylacetonate, cobalt trisacetylacetonate, cobalt ethylacetoacetate and the like; triarylphosphine complexes of cobalt halides such as triphenylphosphine complex of cobalt bromide, tri-m-tolylphosphine complex of cobalt bromide, tri-m-xylylphosphine complex of cobalt bromide and the like; pyridine- or pyridine derivative-complexes of cobalt halides such as pyridine complex of cobalt chloride, i-picoline complex of cobalt chloride and the like; ethyl alcohol complex of cobalt chloride; and monovalent or nonvalent cobalt complexes such as (1,3-butadiene) [1-(2- methyl-3-butenyl)-r-allyl]cobalt, tris--allylcobalt, bicyclot3 13,0] -octadienyl-1 ,5-cyclo-octadienecobalt, bis- (E-allyl)-halogenocobalt (the halogen is iodine, bromine or chlorine), octacarbonyldicobalt and the like. These cobalt compounds may be used alone or in admixture of two or more. As the oroanometallic compound or hydride of a metal of Groups I to III of the Periodic Table (B), compounds capable of reducing the cobalt compound (A) are preferably used. As the metals of Groups I to III of the Periodic Table, there may be used metals of Groups Ia, Ib, IIa, IIb, IIIa and IIIb. Of these, metals of Groups Ia, IIa and IIIa are preferred. Preferable metals are specifically Li, Na, K, Mg, Zn and Al and particularly preferable metals are Li and Al. Preferable organometallwc compounds or metal hydrides (B) are alkyl derivatives of the above-mentioned metals, the alkyl group having 1 to 6 carbon atoms, or hydrides of the metals. Specific exarnies of these organometallic compounds or metal hydrides include organolithium compounds such as ethyllithium, n-butyllithium, sec-butyllithium, t-butyllithium and the like; organozinc compounds such as diethylzinc, dimethylzinc and the like; organomagnesium compounds such as butylmagnesium chloride, ethylmagnesium bromide, dibutylmagnesium, dihexylmagnesium and the like; organoaluminum compounds such as trimethylaluminum, triethylaluminum, triisobutylaluminum, tri-n-hexylaluminum, tridecylaluminum, diethylaluminum chloride, diisobutylaluminum chloride, ethyl aluminum sesquichloride, ethylaluminum dichloride, tetraethylaluminoxane and the like; and metal hydrides such as lithium aluminum hydride, sodium boron hydride, lithium boron hydride and the like. These organometallic compounds or metal hydrides can be used alone or in combination of two or more. Carbon disulfide and/or phenylisothiocyanic acid, both of which are used as the (C) component in this invention, are preferably preliminarily freed of oxygen dissolved therein by nitrogen bubbling or the like though this is not critical. The xanthogen compound which is also used as the (C) component in this invention is a compound represented by the general formula EMI8.1 and preferable examples thereof are xanthogenic acids such as methylxanthogenic acid, ethylxanthogenic acid, n-propylxanthogenic acid, isopropylxanthogenic acid, n-butylxanthogenic acid, secbutylxanthogenic acid, 6-butylxanthogenic acid, n-pentylxanthogenic acid, n-hexylxanthogenic acid, nheptylxanthogenic acid, n-octylxanthogenic acid, 2-ethylhexylxanthogenic acid, phenylxanthogenic acid, p-tolylxanghogenic acid and the like; lithium, sodium and potassium salts of these xanthogenic acids; and xanthogen disulfides such as dimethylxanthogen disulfide, diethylxanthogen disulfide, di-n-propylxanthogen disulfide, diisopropylxanthogen disulfide, di-n-butylxanthogen disulfide, dit-butylxanthogen disulfide, 2-ethylhexylxanthogen disulfide, diphenylxanthogen di sulfide, ethylphenylxanthogen disulfide and the like. Of the above xanthogen compounds, the xanthogen disulfides are more preferable, and dimethylxanthogen disulfide, diisopropylxanthogen disulfide and diphenylxanthogen disulfide are most preferable. As the surfactant and the dispersant added in the step of polymerization in this invention, there may be used surfactants, protective colloid substances, metal chlorides1 phosphates, etc. Of these, surfactant and protective colloids are preferred. As the surfactants, there may be used anionic, cationic and nonionic surfactants alone or in combination of two or more. The anionic surfactants include fatty acid salts, salts of alkyl sulfates, alkylbenzenesulfonates, alkylnaphthalenesulfonates, dialkylsulfosuccinates, alkyldiallylethersulfonates, alkyl phosphates, naphthalenesulfonic acid-formalin condensates, polyoxyethylene alkyl ethers and alkylallylethersulfates, salts of copolymers of an olefin (e.g. diisobutylene) and maleic anhydride, etc. The cationic surfactants include alkylamine salts, quaternary ammonium salts. The nonionic surfactants include polyoxyethylene alkyl ethers, polyoxyethylene alkylphenyl ethers, polyoxyethylene alkylphenol ethers, polyoxyethylene alkyl ethers, sorbitan fatty acid esters, polyoxyethylene sorbitan fatty acid esters, polyethylene glycol fatty acid esters, oxyethylene-oxypropylene block polymers, fatty acid monoglycerides, polyoxyethylene alkylamines, etc. Particularly preferable surfactants are alkylbenzenesulfonates, alkyl sulfates, a combination of a salt of an olefin-maleic anhydride copolymer and calcium chloride, etc. The protective colloids include (partially saponified) polyvinyl alcohol, metal salts of polyacrylic acid, gelatin, albumin, starch, polyvinyl methyl ethers, methyl cellulose, polyvinyl pyrrolidones, etc. Of these, partially saponified polyvinyl alcohols are preferred. The metal chlorides include calcium chloride, zinc chloride, aluminum chloride, barium chloride, potassium chloride, sodium chloride, etc. Cf these, potassium chloride is particularly preferred. The phosphates include tricaicium phosphate, trimagnesium phosphate, tribarium phosphate, etc. The amount of the surfactant or the dispersant used may vary depending upon the desired particle size of the polymer formed and the concentration of the monomer used. When the amount is 30 to 0.0001 g, preferably 10 to 0.001 g, per 100 g of the monomer, a suspension polymer having a desired particle size can be obtained. It is desirable that the surfactant and the dispersant be preliminarily added to water which is used in the polymerization. In this invention, a conjucated diene can also be polymerized in the presence of a solution of a polymer such as a rubber, a resin or the like, whereby a specific polymer composition consisting of the polymer and a crystalline polydiene is produced in a low viscosity and uniformly. The polymer of the polymer solution which may co-exist in the polymerization system includes rubbery polymers such as natural rubber, a cis-1,4-polybutadiene, a polyisoprene, a 1,2-polybutadiene, a low cis-polybutadiene, a butadiene-styrene copolymer, a butadiene-isoprene copolymer, an isoprene-styrene copolymer, a styrenebutadiene-styrene block copolymer, a styrene-isoprenestyrene block copolymer, an ethylene-propylene copolymer, an ethylene-propylene-diene copolymer, butyl rubber, a styrene-butadiene copolymer obtained by emulsion polymerization, an acrylonitrile-butadiene copolymer obtained by emulsion polymerization, an acrylic (co)polymer and the like. Of these, the polyisoprene, the cis-1,4polybutadiene, the 1,2-polybutadiene, the low cis-polybutadiene, the butadiene-styrene copolymer, the ethylenepropylene copolymer, etc. are particularly preferable. The polymer of the above polymer solution also includes resins such as a polystyrene, an acrylonitrilestyrene copolymer, an ethylene-vinyl acetate copolymer, an acrylonitrile-butadiene-styrene copolymer, a polyvinyl chloride, a phenolic resin, a polyester, a polyethylene, a polypropylene, a polyvinyl acetate, a polymethacrylate, a polyvinylidene chloride, a polyvinyl ether, a polyvinyl ketone, a polyamide, a trans-1,4-polybutadiene, a trans1,4-polyisoprene, and the like. Of these, the polystyrene and the ethylene-vinyl acetate copolymer are particularly preferable. The organic solvent for dissolving the above polymer therein includes aromatic hydrocarbon solvents such as benzene, toluene, xylene and the like; aliphatic hydrocarbon solvents such as pentane, hexane, heptane, octane and the like; halogenated hydrocarbon solvents such as methylene chloride, ethylene dichloride, trichloroethane, chlorobenzene and the like; ester type solvents such as ethyl acetate, propyl acetate, butyl acetate, ethyl octylate and the like; alcohol type solvents such as methanol, ethanol, isopropanol, n-butanol, sec-butanol, octanol, ethylene glycol and the like; ketone type solvents such as acetone, methyl ethyl ketone, acetophenone, and the like; nitrile type solvents such as acetonitrile, adiponitrile, benzonitrile and the like; and amide type solvents such as E-caprolactam, propiolactam, butyrolactam, y-valerolactam, N-methylpyrrolidone, N-ethylpyrrolidone, N-methylformamide, N-ethylformamide, N,N-dimethylformamide and the like. The polymer concentration of the polymer solution is preferably about 50 to 0.1% by weight, more preferably 20 to 1% by weight. The amount of the solvent in the conjugated diene-polymerization system is preferably 0 to 1,000% by weight, more preferably 0 to 300% by weight, based on the amount of a monomer. However, this invention can be achieved by dissolving the above polymer in monomeric butadiene to be polymerized in the present process without using the above solvent. In the polymerization of a conjugated diene according to the present process in the presence of a polymer solution, if the proportion of the polymer solution in the polymerization system is large, the amount of the resulting diene polymer is small and the viscosity of the polymer solution is low, the surfactant and/or the dispersant may not necessarily be added. However, in all the other cases, at least one member selected from the surfactants and dispersants is added to the polymerization system, whereby the polymerization system can be stabilized and the particles of the diene polymer formed can be made small and uniform. In the process of this invention, the method of preparing the catalyst system used is very important. The method of the preparation of the catalyst system used in this invention comprises contacting and reacting (A) a specific amount of the cobalt compound with (B) a specific amount of the organometallic compound or hydride of a metal of Groups I to III of the Periodic Table in the presence of a conjugated diene. In this preparation method, the molar ratio of the conjugated diene to the cobalt compound (A) is preferably 1 to 100, more preferably 6 to 50, and the molar ratio of the component (B) to the component (A) is preferably 0.3 to 100, more preferably 0.9 to 50. The temperature used in said preparation is preferably -78 to 1000C, more preferably -309 to 500C, most preferably -100 to 400C. The pressure used is preferably such that the conjugated diene in the preparation of the catalyst does not vaporize and is ordinarily 0.01 to 20 kg/cm2G. The reaction between the (A) component and the (B) component can be uniformly effected by, if necessary, stirring the solvent and the catalyst components in the preparation of the catalyst. As the solvent for the catalyst preparation, there can preferably be used aliphatic hydrocarbons of 5 te 12 carbon atoms and aromatic hydrocarbons. Specific examples of the preferable solvents include toluene, benzene, xylene, hexane, heptane, pentane, refined kerosene, etc. The amount of the solvent used is preferably 1 to 0.001 mole, more preferably 0.5 to 0.001 mole, per liter of the reacted cobalt solution containing the (A) and (B) components. A conjugated diene may be used in place of the solvent. It is sufficient that the stirring is effected to such an extent that the contents cf the reactor are uniformly mixed. The reaction time for preparing the catalyst varies depending upon the temperature for preparing the catalyst, etc.; however, is usually about 5 min to 2 hr. The (C) component may preliminarily be added to a monomer, a solvent solution of the monomer or an aqueous suspension of the monomer, or may be added to the polymerization system after the addition of the reaction mixture of the cobalt compound (A) to the system. The amount of the (C) component used is preferably 0.01 to 100 moles, more preferably 0.3 to 10 moles, per mole of the cobalt compound (A). The water used in the polymerization of this invention is preferably freed of the dissolved oxygen preliminarily by nitrogen bubbling or the like. The water is used in an amount necessary for the water and the diene monomer or a solvent solution of the diene monomer to form a suspension. The amount of water is preferably 0.2 part by volume or more, more preferably 1 part by volume or more, per part by volume of the diene monomer or the solvent solution thereof. There is no upper limit of the amount of water; however, the amount is preferably 50 parts by volume or less, more preferably 20 parts by volume or less. If the amount of water is too large, the polymerization efficiency per unit reaction volume is reduced. As the conjugated diene used in this invention, conjugated dienes having 4 to 5 carbon atoms such as butadiene, isoprene and the like are preferred. Together with the conjugated diene, a small amount of other moncmers such as olefins may be present in the polymerization system. In this invention, a conjugated diene monomer is suspension-polymerized in an aqueous system; however, a small amount of an organic solvent for dissolving the conjugated diene therein may also optionally be added to the aqueous system. The organic solvent includes aromatic hydrocarbon solvents such as benzene, toluene, xylene and the like; aliphatic hydrocarbon solvents such as pentane, hexane, heptane, octane and the like; halogenated hydrocarbon solvents such as methylene chloride, ethylene dichloride, trichloroethane, chlorobenzene and the like; ester type solvents such as ethyl acetate, propyl acetate, butyl acetate, ethyl octylate and the like; alcohol type solvents such as methanol, ethanol, isopropanol, n-butanol, sec-butanol, octanol, ethylene glycol and the like; ketone type solvents such as acetone, methyl ethyl ketone, acetophenone and the like; nitrile type solvents such as acetonitrile, adiponitrile, benzonitrile and the like; and amide type solvents such as e-caprolactam, propiolactam, butyrolactam, y-valerolactam, N-methylpyrrolidone, Nethylpyrrolidone, N-methylformamide, N-ethylformamide, N,N-dimethylformamide and the like. Of these, the ester type solvents are particularly preferable. The amount of the solvent is preferably 0 to 1,0005 by weight, more preferably 0 to 300% by weight, based on the monomer. The melting point (Tm) of the polymer formed can be controlled between about 800C and about 2000C by changing the type and amount of the organic solvent used for dissolving the monomer. The larger the amount of the organic solvent, the lower the Tm. When the organic solvent is a hydrocarbon solvent such as toluene or hexane, the change of Tm is small, but when the solvent is a polar solvent such as an ester, an alcohol, a ketone, a nitrile, an amide, a sulfoxide or the like, the Tm-decreasing effect is great. In this invention, the polymerization temperature is 0 to 800C, preferably 5 to 500C. The polymerization method when this invention is practised in the presence of a polymer solution comprises, for example, adding water and butadiene to a solution of a polymer as mentioned above in a solvent, then adding the catalyst components (A) and (B) prepared according to the above-mentioned methods, adding, after stirring, an emulsifier and carbon disulfide (or phenylisothiocyanic acid or a xanthogen compound); and subjecting the resulting mixture to polymerization with stirring. Of course, this method is not critical. In the above polymerization, the polymerization temperature is 0 to 800C, preferably 5 to 500C. In this invention, to the aqueous polymerization system of a conjugated diene may be added various additives such as an antioxidant, an ultraviolet absorber, a flame retardant, a foaming agent, a lubricant, a processing adjuvant, a filler, a reinforcing agent, a dye, a pigment, a polymerization initiator (e.g. a radical generating agent) and the like. The timing of addition of these additives can be before, during or after the polymerization. There is no particular restriction to the additives and they may be water-insoluble or water-soluble. Waterinsoluble additives may be added in an appropriate form such as lumps, granules, powder or the like. Of these additives, the antioxidant is particularly useful from a practical standpoint. As the antioxidant, there may preferably be used those which are ordinarily employed in rubbers and resins, such as 2,6di-tert-butyl-p-cresol, 2,2'-díhydroxy-3,3'-di(a-methyl- cyclohexyl) -5,5 '-dimethyldiphenylmethane, dilauryl 3,3'thiodipropionate, 3,5-di-tert-4-hydroxybenzyl alcohol and the like. The foaming agent includes dinitrosopentamethylenetetramine, azodicarbonamide, p, p' -oxybisbenzenesulfonyl- hydrazine, etc. The processing adjuvant includes metal soaps such as zinc oleate, tin stearate and the like, stearic acid, etc. The polymerization initiator includes radical generating agents, the representatives of which are azo compounds such as azobisisobutyronitrile and the like. By adding additives to the polymerization system of this invention, a polymer can be obtained in which the additives are uniformly dispersed. When the additives are directly added to a polymer according to an ordinary method, for example, a method of mixing the additives with. a polymer in the molten state by means of a hot roll or an extrusion-mixer. Particularly when the polymer is a 1,2polybutadiene having a high melting point, the melting temperature becomes high, and the polymer gels during mixing with the additives and is in some cases denatured. There is also a method of immersing a solid polymer in a solvent in which the antioxidant is dissolved, but according to this method, the antioxidant exists only on the surfaces of the polymer particles and it is difficult to obtain a polymer in which the antioxidant is uniformly dispersed. The polymer produced according to the process of this invention can suitably be used alone or in admixture with other rubbers, synthetic resins, or the like, and is suitable for the production of tires, footwear, films, sponges, rubber vibration insulators and bottles and also for the modification of other rubbers and resins. The polymer composition produced by carrying out the process of this invention in the presence of a polymer solution can be used as a reinforcing rubber, a rubber of good extrudability, an impact resistant resin, a heatresistant processing resin and a reinforcing resin. This invention will be explained more specifically referring to Examples, but is not restricted to the Examples. Example 1 Preparation of catalyst In a 100-ml pressure bottle preliminarily purged with nitrogen were placed a polytetrafluoroethylene (PTFE)coated stirrer and 9.6 ml of a 0.25 mole/liter solution of cobalt octylate in toluene. The bottle was stoppered. Into the bottle was then charged 6 ml of butadiene. The bottle was placed in a water bath at 30 GC and, while rotating the stirrer vigorously, to the bottle was fed 18 ml of 0.4 mole/ liter solution of triisobutylaluminum in toluene. The resulting mixture was subjected to reaction for about 15 min. The resulting reaction mixture was used in the subsequent polymerization as a reacted cobalt solution. Polymerization In an 800-ml autoclave preliminarily purged with nitrogen were placed 200 ml of a distilled water preliminarily subjected to nitrogen bubbling treatment, 0.2 g of a sodium salt of a maleic anhydride-diisobutylene copolymer (trade name: DEMOL EP, manufactured by Kao Corp.) and 0.1 g of calcium chloride. The mixture was cooled to 5CC. To this mixture were added 50 g of butadiene and 3.4 ml of the above preapred reacted cobalt solution (this amount corresponds to 0.24 mM in cobalt). The whole mixture was subjected to stirring for about 10 min at 500 rpm. Upon adding 0.24 mM of carbon disulfide thereto, polymerization was initiated. The polymerization was effected for 1 hr at 150C. The resulting polymer was taken on a cloth, immersed in a 1% methanolic solution of BHT, and then dried at 50"C overnight in a vacuum drier, thereby obtaining 16 g of a bead polymer having an average particle diameter of 0.8 mm. The polymer had a Tm of 1950C and a vinyl configuration content of 98%. Comparative Example 1 Polymerization was effected using the same catalyst as in Example 1, except that neither surfactant nor calcium chloride were used. The polymer formed adhered to the stirrer and the inner wall of the autoclave. The autoclave was disassembled and the polymer formed was collected and subjected to the same treatment as in Example 1. The polymer obtained was gypsum-like and partially contained beads of 1 to 5 mm in diameter. Therefore, it was presumed that commercial production of this polymer would be almost impossible without using a dispersant. The yield of the polymer was 17 g, the Tm was 192eC and the vinyl configuration content was 98%. Example 2 In this Example, the reacted cobalt solution obtained in Example 1 was used, and methyl acetate was used as a melting point-controlling agent for a polymer formed. Polymerization In an 800-ml autoclave preliminarily purged with nitrogen were placed 200 ml of a distilled water preliminarily subjected to nitrogen bubbling treatment, 0.2 g'of a sodium salt of a maleic anhydride-diisobutylene copolymer and 0.1 g of calcium chloride. Thereto was further added 50 ml of methyl acetate. The resulting mixture was cooled to 50C. Thereto were added 50 g of butadiene and 3.4 ml of the reacted cobalt solution obtained in Example 1 (this amount corresponds to 0.24 mM of cobalt). The whole mixture was subjected to stirring for about 10 min at 500 rpm. Upon adding 0.24 mM of carbon disulfide, polymerization was initiated. The polymerization was effected at 150C for 2 hr. The polymer formed was taken on a cloth and then subjected to the same treatment as in Example 1, thereby obtaining 44.5 g of a bead polymer having an average particle diameter of 0.65 mm. The polymer had a Tm of 120"C, a vinyl configuration content of 83% and a weight average molecular weight by GPC of 186,000. Example 3 Preparation of catalyst In a 100-ml pressure bottle preliminarily purged with nitrogen was placed a Teflon-coated stirrer, and 20 ml of 0.05 mole/liter solution of cobalt naphthenate in toluene was charged thereinto. The bottle was stoppered. To the solution was added 2 ml of butadiene and the bottle was placed in an iced water bath at OOC. With rotating the stirrer vigorously, 4 ml of 0v5 mole/liter solution of n-butyllithium in toluene was added to the mixture. The resulting mixture was subjected to reaction for about 5 min. The reaction mixture was used in the subsequent polymerization. Polymerization Polymerization was effected in the same manner as in Example 2. The polymer had a yield of 46 g, a Tm of 1220C, a vinyl configuration content of 84% and a weight average molecular weight by GPC of 202,000. The polymer formed was a bead polymer having an average particle diameter of 0.58 mm. Example 4 Polymerization was effected under the same polymerization conditions as in Example 1 while applying a mechanical shear force. A polymerization vessel equipped with a pipeline homomixer was used. In an 800-ml autoclave preliminarily purged with nitrogen were placed 400 ml of a distilled water preliminarily subjected to nitrogen bubbling treatment, 0.4 g of a sodium salt of a maleic anhydride-diisobutylene copolymer and 0.2 g of calcium chloride. Further, 100 ml of methyl acetate was added to the resulting mixture. The mixture was cooled to SOC. Thereto were added 100 g of butadiene and 6.8 ml of the reacted cobalt solution obtained in Example 1 (this amount corresponds to 0.48 mM of cobalt). The whole mixture was stirred for about 10 min at 500 rpm, and at the same time, a pump (a flow rate of 150 ml/min) and a pipeline homomixer (7,000 rpm) were allowed to operate. The operation of the pump and the pipeline homomixer was terminated and, with stirring the autoclave contents at 500 rpm, 0.48 mNl of carbon disulfide was added thereto to initiate polymerization. The polymerization was effected at 150C for 2 hr. The polymer formed was subjected to the same post-treatment as in Example 1. Microscopic observation of the polymer obtained revealed that it consisted of fine particles of 10 to 20 m in particle diameter. The polymer had a Tm of 1210C, a vinyl configuration content of 81% and a weight average molecular weight by GPC of 235,000. Examples 5 to 9 Table 1 shows the results of Examples 5 to 9 in which the same procedure as in Example 2 was repeated, except that the sodium salt of a maleic anhydride-diisobutylene copolymer and calcium chloride used in Example 2 were replaced by a polyvinyl alcohol (GOHSENOL GH-23, manufactured by Nippon Synthetic Chemical Industry Co., Ltd.), a polyoxyethylene nonyl phenyl ether 1EMULGEN 950, manufactured by Kao Corp.), sodium laurylsulfate (EMAL 0, manufactured by Kao Corp.), polysodium acrylate (ARON T-40, manufactured by TOAGOSEI CHEMICAL INDUSTRY CO., LTD.) or tertiary calcium phosphate. It is appreciated from these Examples that use of at least one of the specific surfactant, protective colloid and phosphate enables the production of a polymer in a suspension state in which the polymer particles are dispersed very uniformly. Table 1 EMI25.1 <SEP> Polymer <SEP> Average <SEP> Tm <SEP> of <SEP> Vinyl <SEP> con- <SEP> Molecular <tb> Dispersant <tb> yield <SEP> particle <SEP> poly- <SEP> figuration <SEP> wight <SEP> of <tb> diameter <SEP> mer <SEP> content <SEP> in <SEP> polymer <tb> (g) <tb> Amount <SEP> of <SEP> poly <SEP> polymer <tb> Kind <tb> (g) <SEP> mer <SEP> (mm) <SEP> ( C) <SEP> (%) <SEP> (x <SEP> 104) <tb> Example <SEP> 5 <SEP> Polyvinyl <SEP> alcohol <SEP> 0.2 <SEP> 40.5 <SEP> 0.04 <SEP> 118 <SEP> 80 <SEP> 17.5 <tb> <SEP> Polyoxyethylene <SEP> nonyl <tb> Example <SEP> 6 <SEP> 0.2 <SEP> 35.0 <SEP> 0.02 <SEP> 120 <SEP> 81 <SEP> 24.5 <tb> phenyl <SEP> ether <tb> Example <SEP> 7 <SEP> Sodium <SEP> laurylsulfate <SEP> 0.2 <SEP> 42.1 <SEP> 1.5 <SEP> 123 <SEP> 82 <SEP> 15.1 <tb> Example <SEP> 8 <SEP> Polysodium <SEP> acrylate <SEP> 0.2 <SEP> 40.3 <SEP> 1.2 <SEP> 120 <SEP> 81 <SEP> 18.5 <tb> Example <SEP> 9 <SEP> Tricalcium <SEP> phosphate <SEP> 0.2 <SEP> 39.5 <SEP> 1.1 <SEP> 121 <SEP> 82 <SEP> 19.3 <tb> Example 10 Preparation of catalyst In a 300-ml pressure bottle preliminarily purged with nitrogen was placed a Teflon-coated stirrer, and 10 ml of a 0.20 mole/liter solution of cobalt octylate in cyclohexane was charged into the bottle. The bottle was stoppered. To the solution in the bottle was added 3.5 ml of butadiene. The bottle was placed in an iced water bath at 0 C. While rotating the stirrer vigorously, 60 ml of a 0.1 mole/liter solution of sodium boron hydride in isopropanol was added to the mixture in the pressure bottle. The mixture was subjected to reaction for about 15 min. The reaction mixture obtained was used in the subsequent polymerization as a reacted cobalt solution. Polymerization In a 350-ml pressure bottle was placed 200 ml of a distilled water, and nitrogen bubbling was conducted for 5 min. To the distilled water were added, as a dispersant, 0.15 g of a sodium salt of a maleic anhydridediisobutylene copolymer (trade name: DEMOL EP, manufactured by Kao Corp.) and 0.07 g of calcium chloride. Further, 17.7 g of butadiene was added and the pressure bottle was stoppered. To the resulting mixture were added 0.20 mM of carbon disulfide and 7.4 ml of the above reacted cobalt solution (this amount corresponds to 0.20 mM of cobalt). The pressure bottle was vigorously shaken and then placed in a rotary polymerization tank at 200C to effect polymerization for 1 hr. After the polymerization, a crumb slurry polymer was collected by filtration by the use of a Tetoron cloth. The polymer was immersed in a methanolic solution of BHT as an antioxidant and then vacuum-dried at 500C. The polymer obtained had a yield of 92%, a 1,2 content of 96% and a Tm by DSC (abbreviation of differential scanning calorimeter) of 1720C. The Tm was determined by the use of a DSC model 900 of Du Pont. The temperature-elevating speed was 200C/min, 10 mg of a sample was used and alumina was used as a reference. The microstructure of the polymer was calculated from the infrared absorption spectrum in accordance with the Morero method. Example 11 Polymerization was effected using the same catalyst as in Example 10 and also using an ±-caprolactone solution of a monomer. Polymerization In a 350-ml pressure bottle was placed 200 ml of distilled water, and nitrogen bubbling was conducted for 5 min. Then, the same dispersant as in Example 10 was added to the distilled water. Into the pressure bottle were further charged 1 ml of -cprolactone and 17.7 g of butadiene. The pressure bottle was stoppered. To the mixture in the bottle were added 0.20 mM of carbon disulfide and 7.4 ml of the reacted cobalt solution obtained in Example 10. Polymerization and post-treatments were effected in the same manner as in Example 10. The polymer obtained had a yield of 93%, a 1,2 content of 96% and a Tm by DSC of 1690C. Example 12 The same procedure as in Example 11 was repeated, except that the ±-caprolactone was replaced by methyl acetate. The results are shown in Table 2. Example 13 The same procedure as in Example 11 was repeated, except that the ±-caprolactone was replaced by dimethyl fumarate. The results are shown in Table 2. Table 2 EMI29.1 Solvent <SEP> Yield <SEP> Analysis <SEP> of <SEP> polymer <tb> of <tb> Amount <SEP> polymer <SEP> 1,2 <SEP> content <tb> Kind <SEP> Tm <SEP> ( C) <tb> (ml) <SEP> (%) <SEP> (%) <tb> Example <SEP> 10 <SEP> None <SEP> - <SEP> 92 <SEP> 172 <SEP> 96 <tb> Example <SEP> 11 <SEP> @-Caüprolactone <SEP> 1 <SEP> 93 <SEP> 169 <SEP> 96 <tb> Example <SEP> 12 <SEP> Methyl <SEP> acetate <SEP> 30 <SEP> 91 <SEP> 114 <SEP> 81 <tb> Example <SEP> 13 <SEP> Dimethyl <SEP> fumarate <SEP> 1 <SEP> 30 <SEP> 170 <SEP> 96 <tb> Example 14 Polymerization and post-treatments were conducted in the same manner as in Example 10, except that the 17.7 g of butadiene used in Example 10 was replaced by 15.9 g of butadiene and 2.2 g of isoprene. The polymer obtained had a yield of 53%, a Tm of 159 C and a 1,2 content of 968. The polymer was formed into a film and infrared absorption analysis was applied to the film. It gave the absorption of 3,4-polyisoprene at 890 cm. It is appreciated from the low Tm that the polymer is a butadiene-isoprene copolymer. Comparative Example 2 In a 350-ml pressure bottle was placed 200 ml of distilled water, and nitrogen bubbling was conducted for 5 min. The same dispersant as in Example 1 was added to the distilled water. Then, a monomer and three catalyst components (the catalyst components were not subjected to preliminary treatment) were added to the above mixture in various addition orders as shown in Table 3. In all the cases, no polymer was formed. Table 3 Addition order of monomer and catalyst components 1 BD # B # Co # CS2 2 BD # B # CS2 # Co 3 BD # Co # B # CS2 4 BD # Co CS2 i B - Cont'd Table 3 (Cont'd) 5 BD CS2 B Co 6 BD + CS2 # Co # B Note BD: Butadiene (17.7 g) B: Sodium boron hydride (0.72 mM) Co: Cobalt octylate (0.24 mM) CS2: (0.24 mM) After each addition, the pressure bottle was vigorously shaken and was allowed to stand for about 1 min. Example 15 In order to ascertain the effect of this invention, suspension polymerization was effected using an 850-ml autoclave. In the 850-ml autoclave was placed 300 ml of distilled water, and nitrogen purging was conducted for 10 min. As in Example 1, to the distilled water were added 0.2 g of a sodium salt of a maleic anhydride-diisobutylene copolymer and 0.1 g of calcium chloride. The resulting mixture was cooled to 50C and 15 ml of c-caprolactone was added to the mixture. Thereto were further added 26.6 g of butadiene and 0.30 mM of carbon disulfide, and the resulting mixture was vigorously stirred. To this mixture was added 11.0 ml of the catalyst (reacted cobalt solution) prepared in Example 10 (11.0 ml corresponds to 0.30 mM of cobalt). Polymerization was effected for 20 min while maintaining the temperature of the system at 150C. Post-treatments were conducted in the same manner as in Example 10. The results are shown in Table 4. Example 16 The same procedure as in Example 15 was repeated, except that the ±-caprolactone was replaced by methyl acetate. The results are shown in Table 4. Examples 17 and 18 The same procedure as in Example 16 was repeated, except that the amounts of methyl acetate and the catalyst (reacted cobalt solution) were changed. Example 19 The same procedure as in Example 18 was repeated, except that the methyl acetate was replaced by methanol. The results are shown in Table 4. Example 20 The same procedure as in Example 16 was repeated, except that the amount of methyl acetate was changed to 30 ml and the nitrogen purging of the autoclave was not conducted. A polymer was obtained at a yield of 35%. This Example shows that the catalyst of this invention is resistant to not only water but also air. Example 21 In an 850-ml autoclave was placed 300 ml of distilled water, and nitrogen purging was conducted for 10 min. Thereto were added 0.2 g of a sodium salt of a maleic anhydride-diisobutylene copolymer and 0.1 g of calcium chloride. The resulting mixture was cooled to 50C, and thereto were added 23.9 g of butadiene, 3.3 g of isoprene and 0.21 mM of carbon disulfide. The resulting mixture was vigorously stirred and thereto was added 11.0 ml of the catalyst (reacted cobalt solution) prepared in Example 1 (11.0 ml corresponds to 0.30 mM of cobalt). Polymerization was effected for 20 min while maintaining the polymerization system at 150C. Posttreatments were conducted in the same manner as in Example 10. The results are shown in Table 4. Table 4 EMI34.1 <SEP> Polymerization <SEP> recipe <SEP> Yield <SEP> Properties <SEP> of <SEP> polymer <tb> (%) <tb> Organic <SEP> solvent <SEP> Amount <SEP> (Poly <SEP> Butadiene <SEP> Water <SEP> CS2 <tb> of <SEP> meri- <SEP> Tm <SEP> 1,2 <SEP> 30 C <tb> [n] <tb> (g) <SEP> (ml) <SEP> (mM) <SEP> Amount <SEP> cobalt <SEP> zation: <SEP> ( C) <SEP> content <SEP> toluene <tb> Kind <tb> (ml) <SEP> (mM) <SEP> 1hr) <tb> Example <SEP> #-Capro26.6 <SEP> 300 <SEP> 0.30 <SEP> 15 <SEP> 0.30 <SEP> 93 <SEP> 121 <SEP> 83 <SEP> 1.21 <tb> 15 <SEP> lactone <tb> Example <SEP> Methyl <tb> 26.6 <SEP> 300 <SEP> 0.30 <SEP> 15 <SEP> 0.30 <SEP> 15 <SEP> 0.30 <SEP> 92 <SEP> 129 <SEP> 85 <SEP> 1.21 <tb> 16 <SEP> acetate <tb> Example <SEP> Methyl <tb> 26.6 <SEP> 300 <SEP> 0.12 <SEP> 15 <SEP> 0.09 <SEP> 75 <SEP> 114 <SEP> 81 <SEP> 1.01 <tb> 17 <SEP> acetate <tb> Example <SEP> Methyl <tb> 17.7 <SEP> 200 <SEP> 0.30 <SEP> 100 <SEP> 0.30 <SEP> 80 <SEP> 99 <SEP> 80 <SEP> 1.32 <tb> 18 <SEP> acetate <tb> Example <tb> 17.7 <SEP> 200 <SEP> 0.30 <SEP> Methanol <SEP> 100 <SEP> 0.30 <SEP> 83 <SEP> 162 <SEP> 95 <SEP> 19 <tb> Example <SEP> Methyl <tb> 26.6 <SEP> 300 <SEP> 0.30 <SEP> 30 <SEP> 0.30 <SEP> 35 <SEP> 114 <SEP> 81 <SEP> 1.27 <tb> 20 <SEP> acetate <tb> Example <SEP> Butadiene <tb> 21 <SEP> 23.9 <tb> 300 <SEP> 0.30 <SEP> None <SEP> - <SEP> 0.30 <SEP> 55 <SEP> 158 <SEP> 93 <SEP> Isoprene <tb> 3.3 <tb> Example 22 Preparation of catalyst In a 100-ml pressure bottle preliminarily purged with nitrogen was placed a PTFE-coated stirrer, and 10 ml of a 0.20 mole/liter solution of cobalt octylate in cyclohexane was charged thereinto. The pressure bottle was stoppered. To the solution in the bottle was added 4 ml of butadiene, and the pressure bottle was placed in a iced water bath at 0 C. While rotating the stirrer vigorously, 16 ml of a 0.5 mole/liter solution of butylmagnesium chloride in dibutyl ether was fed to the pressure bottle. The resulting mixture was subjected to reaction for about 30 min. The reaction mixture obtained (reacted cobalt solution) was used in the subsequent polymerization. Polymerization In a 350-ml pressure bottle was placed 200 ml of distilled water, and nitrogen bubbling was conducted for 5 min. To the distilled water were added 0.15 g of a sodium salt of a maleic anhydride-diisobutylene copolymer and 0.07 g of calcium chloride. To the resulting mixture was added 17.7 g of butadiene and the pressure bottle was stoppered. Into the bottle were charged 0.20 mM of carbon disulfide and 3.0 ml of the above reacted cobalt solution (3.0 ml corresponds to 0.20 mM of cobalt). The pressure bottle was vigorously shaken and then placed in a rotary polymerization tank at 200C in which polymerization was effected for 1 hr. The polymer formed was subjected to post-treatments in the same manner as in Example 10. The polymer obtained had a yield of 85%, a 1,2 content of 98% and a Tm by DSC of 1870C. Example 23 Preparation of catalyst In a 100-ml pressure bottle preliminarily purged with nitrogen was placed a Teflon coated stirrer, and 20 ml of a 0.05 mole/liter solution of cobalt naphthenate in toluene was charged into the bottle. The pressure bottle was then stoppered. To the solution in the pressure bottle was added 2 ml of butadiene, and the pressure bottle was then placed in an iced water bath at OOC. While rotating the stirrer vigorously, 4 ml of a 0.5 mole/liter solution of n-butyllithium in n-hexane was fed to the pressure bottle. The resulting mixture was subjected to reaction for about 5 min. The reaction mixture obtained (reacted cobalt solution) was used in the subsequent polymerization. Polymerization In a 350-ml pressure bottle was placed 200 ml of distilled water, and nitrogen bubbling was conducted for 5 min. To the distilled water were added 0.15 g of a sodium salt of a maleic anhydride-diisobutylene copolymer and 0.07 g of calcium chloride. To the resulting mixture were added 1 ml of s-caprolactone and 17.7 g of butadiene. The pressure bottle was then stoppered. To the pressure bottle were fed 0.24 mM of carbon disulfide and 6.2 ml of the above reacted cobalt solution (6.2 ml corresponds to 0.24 mM of cobalt). The pressure bottle was vigorously shaken and then placed in a rotary polymerization tank at 200C in which polymerization was effected for 1 hr. The polymer formed was treated in the same manner as in Example 10. The polymer obtained had a yield of 65%, a 1,2 content of 96% and a Tm by DSC of 1810C. Example 24 Preparation of catalyst In a 100-ml pressure bottle preliminarily purged with nitrogen were placed a Teflon-coated stirrer, and 10 ml of a 0.20 mole/liter solution of cobalt octylate in toluene was charged into the bottle. The pressure bottle was stoppered. To the pressure bottle was fed 4 ml of butadiene, and the pressure bottle was then placed in an iced water bath at OOC. While rotating the stirrer vigorously, 16 ml of 0.5 mole/iiter solution of dihexylmagnesium in n-hexane was fed to the pressure bottle. The resulting mixture was subjected to reaction for about 5 min. The reaction mixture obtained (reacted cobalt solution) was used in the subsequent polymerization. Polymerization In a 350-ml pressure bottle was placed 200 ml of distilled water, and nitrogen bubbling was conducted for 5 min. To the distilled water were added 0.15 g of a sodium salt of a maleic anhydride-diisobutylene copolymer and 0.07 g of calcium chloride. Thereto was further added 17.7 g of butadiene, and the pressure bottle was then stoppered. To the pressure bottle were fed 0.20 TaM of carbon disulfide and 3.0 ml of the above reacted cobalt solution (3.0 ml corresponds to 0.20 mM of cobalt). The pressure bottle was vigorously shaken and then placed in a rotary polymerization tank at 200C, in which polymerization was effected for 1 hr. The polymer formed was treated in te same manner as in Example 10. The polymer obtained had a yield of 84%, a 1,2 content of 98% and a Tm by DSC of 1920C. Example 25 Preparation of catalyst In a 100-ml pressure bottle preliminarily purged with nitrogen was placed a Teflon-coated stirrer, and 20 ml of a 0.05 mole/liter solution of cobalt naphthenate in toluene was charged into the bottle. The pressure bottle was stoppered. 2 ml of butadiene was fed to the pressure bottle. The pressure bottle was then placed in an iced water bath at OOC. While rotating the stirrer vigorously, to the pressure bottle was fed 8 ml of a 0.5 mole/liter solution of dibutylaluminum hydride in hexane. The resulting mixture was subjected to reaction for about 5 min. The reaction mixture obtained (reacted cobalt solution) was used in the subsequent polymerization. Polymerization In a 350-ml pressure bottle was placed 200 ml of distilled water, and nitrogen bubbling was conducted for 5 min. To the distilled water were added 0.15 g of a sodium salt of a maleic anhydride-diisobutylene copolymer and 0.07 g of calcium chloride. To the resulting mixture was added 17.7 g of butadiene. The pressure bottle was stoppered. To the pressure bottle were fed 0.20 mM of carbon disulfide and 6.0 ml of the above reacted cobalt solution (6.0 ml corresponds to 0.20 mM of cobalt). The pressure bottle was vigorously shaken and then placed in a rotary polymerization tank at 200C, in which polymerization was effected for 1 hr. The polymer formed was treated in the same manner as in Example 10. The polymer obtained had a yield of 92%, a 1,2 content of 98% and a Tm by DSC of 1900C. Example 26 Preparation of catalyst In a 100-ml pressure bottle preliminarily purged with nitrogen were placed a Teflon-coated stirrer, and 20 ml of a 0.05 mole/liter solution of cobalt naphthenate in toluene was charged into the bottle. The pressure bottle was stoppered, and 4 ml of butadiene was fed to the pressure bottle. The pressure bottle was placed in an iced water bath at OOC. While rotating the stirrer vigorously, to the pressure bottle was fed 50 ml of a 0.1 mole/liter solution of tetraethylaluminoxane in methylene chloride prepared according to the procedure mentioned hereinafter. The resulting mixture was subjected to reaction for about 5 min. The reaction mixture obtained (reacted cobalt solution) was used in the subsequent polymerization. tPreparation of tetraethylaluminoxanel In a 100-ml pressure bottle preliminarily purged with nitrogen was placed a Teflon-coated stirrer, and 45 ml of methylene chloride and 45 mg of water were charged into the bottle. The pressure bottle was stoppered. While rotating the stirrer vigorously at -100C, 5 ml of a 1.0 mole/liter solution of triethylaluminum in toluene was charged into the bottle. Then, reaction was carried out to synthesize the tetraethylaluminoxane. Polymerization In a 350-ml pressure bottle was placed 200 ml of distilled water, and nitrogen bubbling was conducted for 5 min. To the distilled water were added 0.15 g of a sodium salt of a maleic anhydride-diisobutylene copolymer and 0.07 g of calcium chloride, and 17.7 g of butadiene was further added. The pressure bottle was then stoppered. To the pressure bottle were fed 0.20 mM of carbon sulfide and 14.8 ml of the above reacted cobalt solution (14.8 ml corresponds to 0.20 mM of cobalt). The pressure bottle was vigorously shaken and then placed in a rotary polymerization tank at 200C, in which polymerization was effected for 1 hr. The polymer formed was treated in the same manner as in Example 10. The polymer obtained had a yield of 78%, a 1,2 content of 98% and a Tm by DSC of 1880C. Example 27 Preparation of catalyst In a 100-ml pressure bottle preliminarily purged with nitrogen was placed a PTFE-coated stirrer, and 9.0 ml of a 0.20 mole/liter solution of cobalt octylate in cyclohexane. The pressure bottle was stoppered, after which 6 ml of butadiene was fed to the pressure bottle. The pressure bottle was placed in an iced water bath at OOC. While rotating the stirrer vigorously, 9.0 ml of a 0.4 mole/liter solution of nbutyllithium in hexane was fed to the pressure bottle. The resulting mixture was subjected to reaction for about 15 min. The reaction mixture obtained (reacted cobalt solution) was used in the subsequent polymerization. Polymerization In an 800-ml glass autoclave was placed 10 g of a cis-1,4-polybutadiene rubber (JSR BR 01, manufactured by JAPAN SYNTHETIC RUBBER CO., LTD.), and nitrogen purging was conducted. Into the autoclave was further charged 160 ml of toluene preliminarily freed of oxygen by nitrogen bubbling to completely dissolve the cis-1,4polybutadiene rubber. To the resulting solution was added 200 ml of water preliminarily freed of oxygen, and 40 g of butadiene and 8.0 ml of the reacted cobalt 'solution (8.0 ml corresponds to 0.6 mM of cobalt) were then added thereto. The resulting mixture was thoroughly stirred. To this mixture were added 5 ml of a 2% aqueous solution of sodium dodecylsulfate and 0.6 mM of carbon disulfide. Polymerization was conducted at 200C for 1 hr. A mixture of the added rubber and a crystalline 1,2polybutadiene formed was obtained as a crumb slurry dispersion of low viscosity. After the polymerization, the crumb-like polymer was collected on a cloth. The polymer was allowed to coagulate in methanol containing 1% of BHT as an antioxidant and then vacuum-dried at 500C, whereby 20.4 g of a polymer composition of the added rubber and a crystalline 1,2-polybutadiene (20.4 g corresponds to a butadiene polymerization conversion of 2781. The polymer composition showed a glass transition temperature Tg of -121.0 C and melting points of -11.5 C (Tml, based on cis-1,4-polybutadiene rubber) and 188.5"C (Tm2, based on crystalline 1,2-polybutadiene) as a result of DSC analysis. The polymer composition was uniform. Comparative Example 3 In an 800-ml autoclave was placed 20 g of a cis-1,4-polybutadiene rubber, and nitrogen purging was conducted. Into the autoclave was charged 320 ml of a toluene freed of oxygen. Thereto were added 80 g of butadiene and 16.0 ml of the reacted cobalt solution obtained in Example 27 (16.0 ml corresponds to 1.2 mM of cobalt). The resulting mixture was thoroughly stirred. Thereafter, 1.2 mM of carbon disulfide was added. Polymerization was conducted at 200C for 1 hr. Inside the autoclave, the viscosity of the contents became very high with the progress of polymerization, and sufficient stirring became impossible about 10 min after the start of polymerization. However, polymerization was continued. After the polymerization, the autoclave had to be disassembled to take out a polymer formed. It implied that commercial production of a polymer according to the above procedure is very difficult. The polymer taken out was subjected to coagulation in methanol containing 1% of BHT and vacuum-dried at 500C, thereby obtaining 37.4 g of a composition polymer (37.4 g corresponds to a butadienepolymerization conversion of 21.8%). The polymer showed a Tg of -120 C and Tml of -11.00C and Tm2 of 1880C. Examples 28 to 45 The same procedure as in Example 27 was repeated, except that the amount of the rubber added, the amount of butadiene added, the amount of the reacted cobalt solution added and the amount of carbon do sulfide used were changed and in Examples 29 to 45, the cis-1,4polybutadiene was replaced by other polymers, thereby obtaining composite polymers as in Example 27. The results are shown in Table 5. Example 46 The same procedure as in Example 28 was repeated, except that the polymerization scale was raised to a 10-liter autoclave, whereby 283 g of a composite polymer was obtained. This composite polymer (100 parts) was mixed with carbon black, zinc oxide, stearic acid, etc. in accordance with the following compounding recipe, by a Banbury mixer, the resulting mixture was compounded with a vulcanizing agent and accelerators with the following compounding recipe on a roll, and vulcanization was conducted at 1450C for 40 min: Compounding recipe Polybutadiene composite 100 parts Carbon balck (EAF type) 50 parts Aromatic oil 10 parts Zinc oxide 4 parts Stearic acid 2 parts Accelerator, MSA *1 0.5 part Accelerator, DM *2 1.0 part Sulfur 2.0 parts Note: *1 N-oxydiethylene-2-benzothiazole sulfenamide *2 Di-2-benzothiazyl sulfide The results are shown in Table 6. Comparative Example 4 Preparation of polymer An 800-ml autoclave was purged with nitrogen. In the autoclave were placed 300 ml of toluene preliminarily subjected to nitrogen bubbling treatment and 30 g of butadiene, and further placed 5.0 ml of a 0.5 mole/ liter solution of triisobutylaluminum in toluene, 2.5 ml of a 0.2 mole/liter solution of cobalt octylate in toluene and 2.5 ml of a 0.2 mole/liter solution of carbon disulfide in toluene. Then, polymerization was conducted at 200C for 2 hr. In the course of the polymerization, a polymer started to deposit, and sufficient stirring became impossible. After the completion of the polymerization, the polymer formed was subjected to coagulation in methanol containing 1% of BHT and then vacuum-dried. The polymer obtained had a yield of 23.2 g, a Tm of 197"C and a 1,2 content of 98%. Preparation of composite polymer 200 g of a cis-l,4-polybutadiene rubber was wound around a Ç in. roll. Thereto was slowly added 20 g of the above 1,2-polybutadiene and they were kneaded sufficiently. The thus obtained composite polymer was used as a sample for evaluation. Upon visual checking, particles of the 1,2polybutadiene were found in dots in the composite polymer. This implied that the composite polymer was not uniform. [Evaluation of physical propertiesl The above composite polymer was mixed with carbon black and other additives according to the same compounding recipe as in Example 46 and evaluated. The results are shown in Table 6. Comparative Example 5 A cis-l,4-polybutadiene was mixed with carbon black and other additives according to the same compounding recipe as in Example 46 and evaluated. The results are shown in Table 6. Example 47 Preparation of catalyst In a 100-ml pressure bottle preliminarily purged with nitrogen was placed a Teflon-coated stirrer, and 9 ml of 0.20 mole/liter solution of cobalt octylate in cyclohexane was charged into the bottle. The pressure bottle was stoppered. To the pressure bottle was fed 4 ml of butadiene. The pressure bottle was placed in an iced water bath at 0 C. While rotating the stirrer vigorously, 54 ml of a 0.1 mole/liter solution of sodium boron hydride in isopropanol was charged into the bottle. The resulting mixture was subjected to reaction for about 15 min. The reaction mixture obtained was used in the subsequent polymerization as a reacted cobalt solution. Preparation of polymer In an 800-ml glass autoclave was placed 10 g of a cis-1,4-polyisoprene rubber (JSR BR 01, manufactured by JAPAN SYNTHETIC RUBBER CO., LTD.), and nitrogen purging was conducted. To the rubber was added 160 ml of toluene freed of oxygen by nitrogen bubbling treatment to completely dissolve the rubber therein. Then, 200 ml of water freed of oxygen was added. Further, 40 g of butadiene and 22.3 ml of the above reacted cobalt solution. (22.3 ml corresponds to 0.6 mM of cobalt) were added thereto. The resulting mixture was thoroughly stirred. To this mixture were added 5 ml of a 2% aqueous solution of sodium dodecylsulfate and 0.6 mM of carbon disulfide. Polymerization was conducted at 200C for 1 hr. The rubber added and a crystalline 1,2-polybutadiene formed was obtained in the form of a crumb slurry dispersion of low viscosity. After the completion of the polymerization, a crumb-like polymer was recovered by use of a Tetoron cloth, subjected to coagulation in methanol containing 18 of BHT and vacuum-dried at 500C. Thus, 32.0 g of a polymer composition of the rubber and a 1,2-polybutadiene (32.0 g corresponds to a butadiene-polymerization conversion of 558). By DSC analysis, it was found that the composition had a Tg of -720C and a Tm of 175.00C. Visual checking revealed that the cis-1,4-polyisoprene rubber and the crystalline 1,2-polybutadiene were uniformly mixed with each other in the composition. Example 48 Preparation of catalyst In a 100-ml pressure bottle preliminarily purged with nitrogen was placed a Teflon-coated stirrer, and 10 ml of a 0.25 mole/liter solution of cobalt octylate in toluene was charged into the bottle. The pressure bottle was stoppered. To the pressure bottle was fed 6 ml of butadiene. The pressure bottle was placed in an iced water bath at 0 C. While rotating the stirrer vigorously, the pressure bottle 25 ml of a 0.50 mole/ liter solution of triisobutylaluminum in toluene was charged into the bottle. The resulting mixture was subjected to reaction for about 15 min. The reaction mixture obtained was used in the subsequent polymerization as a reacted cobalt solution. Polymerization The same polymerization and post-treatment as in Example 46 were carried out in the presence of a cis1,4-polyisoprene rubber using 9.8 ml of the above reacted cobalt solution (9.8 ml corresponds to 0.6 mM of cobalt). Thus, 26.8 g of a polymer composition of the rubber added and a crystalline 1,2-polybutadiene (26.8 g corresponds to a butadiene-polymerization conversion of 42%) was obtained. By DSC analysis, it was found that the composition had a Tg of -72 C and a Tm of 188 C. Visual checking revealed that the cis-1,4-polyisoprene rubber and the crystalline 1,2-polybutadiene were uniformly mixed with each other in the composition. Table 5 EMI50.1 <SEP> Polymerization <SEP> conditions <tb> Example <tb> No. <SEP> Rubber <SEP> or <SEP> resin <SEP> Amount <SEP> of <SEP> Amount <SEP> of <SEP> Amount <SEP> of <SEP> Amount <SEP> of <SEP> Amount <SEP> of <tb> solvent <SEP> water <SEP> butadiene <SEP> reacted <SEP> carbon <tb> Amount <SEP> (toluene) <SEP> cobalt <SEP> disulfide <tb> Kind <tb> (g) <SEP> (ml) <SEP> (ml) <SEP> (g) <SEP> (mM) <SEP> (mM) <tb> *1 <tb> Cis-1,4-poly27 <SEP> 10 <SEP> 160 <SEP> 200 <SEP> 40 <SEP> 0.6 <SEP> 0.6 <tb> butadiene <tb> 28 <SEP> " <SEP> 20 <SEP> " <SEP> " <SEP> 4 <SEP> 0.2 <SEP> 0.2 <tb> *2 <tb> SBR <SEP> of <SEP> solution <tb> 29 <SEP> 10 <SEP> " <SEP> " <SEP> 40 <SEP> 0.6 <SEP> 0.6 <tb> polymerization <tb> 30 <SEP> " <SEP> 20 <SEP> 160 <SEP> 200 <SEP> 4 <SEP> 0.2 <SEP> 0.2 <tb> *3 <tb> Cis-1,4-poly31 <SEP> 10 <SEP> " <SEP> " <SEP> 40 <SEP> 0.6 <SEP> 0.6 <tb> isoprene <tb> 32 <SEP> " <SEP> 10 <SEP> " <SEP> " <SEP> 10 <SEP> 0.2 <SEP> 0.2 <tb> 33 <SEP> " <SEP> 20 <SEP> " <SEP> " <SEP> 4 <SEP> 0.2 <SEP> 0.2 <tb> Ethylene-propylene <tb> 34 <SEP> 10 <SEP> " <SEP> " <SEP> 40 <SEP> 0.6 <SEP> 0.6 <tb> copolymer <SEP> rubber <SEP> *4 <tb> - Cont' d - Table 5 (Cont' d) EMI51.1 Yield <SEP> Properties <SEP> of <SEP> composite <SEP> polymer <tb> Appearance <tb> Yield <SEP> of <SEP> Butadiene- <SEP> of <SEP> polymer <tb> composite <SEP> polymerization <SEP> Tg <SEP> Tm1 <SEP> Tm2 <tb> polymer <SEP> conversion <tb> ( C) <SEP> ( C) <SEP> ( C) <tb> (g) <SEP> (%) <tb> 20.8 <SEP> 27 <SEP> -121.0 <SEP> -11.5 <SEP> 188.5 <SEP> Crumb-like <tb> 22.6 <SEP> 65 <SEP> -122 <SEP> -8.5 <SEP> 188.5 <SEP> Paste-like <tb> 25.8 <SEP> 40 <SEP> -59.5 <SEP> - <SEP> 188.5 <SEP> Crumb-like <tb> 22.4 <SEP> 62 <SEP> -59.5 <SEP> - <SEP> 187.5 <SEP> Paste-like <tb> 30.1 <SEP> 50 <SEP> -72.0 <SEP> - <SEP> 187.5 <SEP> Crumb-like <tb> 18.6 <SEP> 86 <SEP> -73.0 <SEP> - <SEP> 187.0 <SEP> Crumb-like <tb> 23.6 <SEP> 91 <SEP> -74.0 <SEP> - <SEP> 185.5 <SEP> Paste-like <tb> 28.9 <SEP> 47 <SEP> -65.0 <SEP> - <SEP> 188.0 <SEP> Crumb-like <tb> - Cont'd Table 5 (Cont'd) EMI52.1 Ethylene-propylene <tb> 35 <SEP> 10 <SEP> " <SEP> " <SEP> 10 <SEP> 0.2 <SEP> 0.2 <tb> copolymer <SEP> rubber <SEP> *4 <tb> 36 <SEP> " <SEP> 20 <SEP> " <SEP> " <SEP> 4 <SEP> 0.2 <SEP> 0.2 <tb> Acrylonitrile- <SEP> *5 <tb> 37 <SEP> butadiene <SEP> copolymer <SEP> 10 <SEP> 160 <SEP> 200 <SEP> 40 <SEP> 0.6 <SEP> 0.6 <tb> rubber <tb> 38 <SEP> " <SEP> 20 <SEP> " <SEP> " <SEP> 4 <SEP> 0.2 <SEP> 0.2 <tb> 39 <SEP> Acrylic <SEP> rubber <SEP> *6 <SEP> 10 <SEP> 160 <SEP> 200 <SEP> 40 <SEP> 0.6 <SEP> 0.6 <tb> 40 <SEP> " <SEP> 10 <SEP> " <SEP> " <SEP> 10 <SEP> 0.2 <SEP> 0.2 <tb> 41 <SEP> " <SEP> 20 <SEP> " <SEP> " <SEP> 4 <SEP> 0.2 <SEP> 0.2 <tb> <SEP> Polystyrene <SEP> *7 <tb> 42 <SEP> 10 <SEP> " <SEP> " <SEP> 40 <SEP> 0.6 <SEP> 0.6 <tb> resin <tb> 43 <SEP> " <SEP> 20 <SEP> " <SEP> " <SEP> 4 <SEP> 0.2 <SEP> 0.2 <tb> 44 <SEP> Ethylene-vinyl- <SEP> *8 <tb> 44 <SEP> 10 <SEP> " <SEP> " <SEP> 40 <SEP> 0.6 <SEP> 0.6 <tb> acetate <SEP> resin <tb> - Cont'd - Table 5 (Cont'd) EMI53.1 17.0 <SEP> 69 <SEP> -65.0 <SEP> - <SEP> 188.5 <SEP> Crumb-like <tb> 22.8 <SEP> 71 <SEP> -65.0 <SEP> - <SEP> 188.5 <SEP> Paste-like <tb> 17.8 <SEP> 20 <SEP> -36.5 <SEP> - <SEP> 165 <SEP> Crumb-like <tb> 20.8 <SEP> 20 <SEP> -36.5 <SEP> - <SEP> 160 <SEP> Paste-like <tb> 23.4 <SEP> 33 <SEP> -33.0 <SEP> - <SEP> 188.5 <SEP> Crumb-like <tb> 13.6 <SEP> 35 <SEP> -38.0 <SEP> - <SEP> 182.0 <SEP> Crumb-like <tb> 21.6 <SEP> 39 <SEP> -43.0 <SEP> - <SEP> 176.5 <SEP> Paste-like <tb> 28.0 <SEP> 45 <SEP> 92.0 <SEP> - <SEP> 189.0 <SEP> Crumb-like <tb> 23.0 <SEP> 74 <SEP> 93.0 <SEP> - <SEP> 188.5 <SEP> Paste-like <tb> 23.6 <SEP> 34 <SEP> - <SEP> 174.0 <SEP> 183.5 <SEP> Crumb-like <tb> - Cont' d - Table 5 (Cont'd) EMI54.1 Ethylene-vinyl <SEP> *8 <tb> 45 <SEP> 20 <SEP> " <SEP> " <SEP> 4 <SEP> 0.2 <SEP> 0.2 <tb> acetate <SEP> resin <tb> Cis-1,4-poly- <SEP> *3 <tb> 47 <SEP> 10 <SEP> " <SEP> " <SEP> 40 <SEP> 0.6 <SEP> 0.6 <tb> isoprene <tb> - Cont'd Note: *1 Cis-1,4-polybutadiene rubber JSR BR 01, manufactured by JAPAN SYNTHETIC RUBBER CO., LTD. *2 SBR of solution polymerization JSR SL 552, manufactured by JAPAN SYNTHETIC RUBBER CO., LTD. *3 Cis-1,4-polyisoprene rubber JSR IR 2200, manufactured by JAPAN SYNTHETIC RUBBER (Synthetic rubber of natural CO., LTD. rubber type) *4 Ethylene-propylene copolymer JSR EP 24,manufactured by JAPAN SYNTHETIC RUBBER rubber CO., LTD. *5 Acrylonitrile-butandiene JSR N 230S, manufactured by JAPAN SYNTHETIC RUBBER copolymer rubber CO., LTD. Table 5 (Cont'd) EMI55.1 22.3 <SEP> 57 <SEP> - <SEP> 79.0 <SEP> 173.5 <SEP> Paste-like <tb> 32.0 <SEP> 55 <SEP> -72 <SEP> - <SEP> 175 <SEP> Crumb-like <tb> Note: *6 Acrylic rubber JSR AR 201, manufactured by JAPAN SYNTHETIC RUBBER CO., LTD. *7 Polystyrene resin TORPOLEX 525, manufactured by Mitsui Toatsu Chemicals, Inc. *8 Ethylene-vinyl acetate resin ULTRATHENE 633, manufactured by TOYO SODA MFG CO., LTD. Comparative Example 6 In an 800-ml autoclave preliminarily purged with nitrogen were placed 400 ml of distilled water preliminarily subjected to nitrogen bubbling and 100 g of butadiene. Then, 5.9 ml of the reacted cobalt solution obtained in Example 48 (5.9 ml corresponds to 0.36 mM of cobalt), and was placed in the autoclave, and 0.36 mM of carbon do sulfide was then placed therein to initiate polymerization. The polymerization was effected for I hr while maintaining the polymerization system at 150C. After the completion of the polymerization, the polymer formed was collected on a cloth, immersed in methanol containing 18 of BHT and vacuum-dried overnight at 50 C. As a result, 32 g of a gypsum-like polymer having a Tm of 1920C was obtained. 20 g of the 1,2-polybutadiene obtained above was added to a solution of 200 g of a cis-1,4-polybutadiene in 2500 ml of toluene. The mixture was vigorously stirred. Then, the mixture was freed of toluene by steam stripping. The residue was dried on a roll at 120"C to obtain a dry composite polymer. Upon visual checking, particles of the 1,2-polybutadiene were found in dots in the composite polymer. This implied that the polymer was a non-uniform composition. This composition was vulcanized in accordance with the same compounding recipe as in Example 46. The results are shown in Table 6. For comparison, Table 6 also shows the data of Example 46 and Comparative Examples 4 and 5. This composition had a low tensile strength due to the poor dispersion of the 1,2-polybutadiene in the composition. Table 6 EMI58.1 Comparative <SEP> Comparative <SEP> Comparative <tb> Example <SEP> 46 <SEP> Example <SEP> 4 <SEP> Example <SEP> 5 <SEP> Example <SEP> 6 <tb> (roll-blended) <tb> 300% <SEP> modulus <SEP> (kg/cmê) <SEP> 126 <SEP> 112 <SEP> 88 <SEP> 107 <tb> Stress <SEP> at <SEP> break <SEP> (kg/cmê) <SEP> 255 <SEP> 210 <SEP> 250 <SEP> 174 <tb> Elongation <SEP> at <SEP> break <SEP> (%) <SEP> 590 <SEP> 500 <SEP> 630 <SEP> 430 <tb> Hardness <SEP> (JIS-A) <SEP> 65 <SEP> 67 <SEP> 62 <SEP> 63 <tb> Flex <SEP> test <SEP> (times) <SEP> 100,000 <SEP> 15,000 <SEP> 50,000 <SEP> 10,000 <tb> Extrusion <SEP> test <SEP> (full <SEP> mark: <SEP> 16) <SEP> 16 <SEP> 12 <SEP> 15 <SEP> 8 <tb> Dies <SEP> well <SEP> 1.10 <SEP> 1.29 <SEP> 1.55 <SEP> 1.36 <tb> Extrusion test ASTM D2230 Garvey die Screw diameter: 10 mm L/D = 8 Die temperature: 1000C Revolution rate: 20 rpm As is obvious from Examples 27 to 48 and Table 6, according to this invention, a polymer composition in which a polymer such as a rubber or resin and a crystalline 1,2-polybutadiene are extremely uniformly dispersed can easily be obtained from a reaction system having a low viscosity by subjecting butadiene to 1,2polymerization in the presence of water and in the presence of a solution of the polymer. Example 49 The same procedure as in Example 28 was repeated, except that sodium dodecylsulfate was not used. The results are shown in Table 7. Table 7 EMI59.1 <tb> <SEP> Properties <SEP> of <tb> Yield <tb> <SEP> composite <SEP> polymer <SEP> Apperance <tb> of <tb> <SEP> Tg <SEP> Tm1 <SEP> Tm2 <tb> <SEP> Polymer <SEP> Polybutadiene <SEP> composite <tb> <SEP> (g) <SEP> (%) <SEP> ( C) <SEP> ( C) <SEP> ( C) <SEP> polymer <tb> <SEP> 22.7 <SEP> 68 <SEP> -122 <SEP> -8.0 <SEP> 189 <SEP> Pasty <tb> Example 50 Polymerization was conducted by repeating the procedure of Example 1, except that, in polymerization, 0.5 g of 2,6-di-tert-butyl-p-cresol (BHT) was fed to the autoclave prior to addition of butadiene. As a result, 16.2 g of a bead polymer having an average particle diameter of 0.7 mm was obtained. The polymer had a Tm of 1930C and a vinyl configuration content of 98%. The BHT was uniformly dispersed in the polymer. Example 51 Polymerization was conducted by repeating the same procedure as in Example 2, except that additives were added as shown in Table 7 when effecting the butadiene polymerization. The results are shown in Table 8. Table 8 EMI61.1 <SEP> Butadiene Addition <tb> Run <SEP> polymerization <tb> Additive <SEP> amount <tb> No. <SEP> conversion <tb> (g) <SEP> (%) <tb> 1 <SEP> None <SEP> (same <SEP> as <SEP> in <SEP> Example <SEP> 2) <SEP> 0 <SEP> 89 <tb> 2 <SEP> 2,6-Di-tert-butyl-p-cresol <SEP> 0.5 <SEP> 89 <tb> 2,2'-Dihidroxy-3,3'-di <SEP> (&alpha;-methylcyclohexyl)3 <SEP> 0.5 <SEP> 95 <tb> 5,5'-dimethyldiphenylmethane <tb> 4 <SEP> Dilauryl <SEP> 3,3'-thiodipropionate <SEP> 0.5 <SEP> 88 <tb> 5 <SEP> 3,5-Di-tert-butyl-4-hydroxybenzyl <SEP> alcohol <SEP> 0.5 <SEP> 93 <tb> 6 <SEP> Azodicarbonamide <SEP> 2.5 <SEP> 95 <tb> 7 <SEP> p,p'-Oxybisbenzenesulfonyl <SEP> hydrazine <SEP> 2.5 <SEP> 84 <tb> 8 <SEP> Zinc <SEP> oleate <SEP> 2.5 <SEP> 92 <tb> 9 <SEP> Azobisisobutyronitrile <SEP> 2.5 <SEP> 82 <tb>

Claims: WHAT IS CLAIMED IS: 1. A process for producing a diene polymer, characterized by polymerizing a conjugated diene in an aqueous system in the presence of a catalyst system prepared by adding, to a catalyst obtained preliminarily by contacting (A) a cobalt compound with (B) an organometallic compound or hydride of a metal of Groups I to III of the Periodic Table in the presence of 1 to 100 moles, per mole of (A), of a conjugated diene, (C) at least one member selected from the group consisting of carbon disulfide, phenylisothiocyanic acid and a xanthogen compound and further in the presence of at least one member selected from the group consisting of a surfactant, a dispersant and a polymer solution, 2. A process according to Calim 1, wherein the polymerization of a conjugated diene is conducted in the presence of a surfactant and a dispersant. 3. A process according to Claim 1, wherein the dispersant is at least one member selected from the group consisting of protective colloid substances, metal chlorides and phosphates. 4. A process according to Claim 1, wherein the dispersant is a protective colloid substance. 5. A process according to Claim 1, wherein the surfactant is at least one member selected from the group consisting of anionic, cationic and nonionic surfactants. 6. A process according to Claim 1, wherein the amount of at least one member selected from a surfactant and a dispersant is 30 to 0.0001 g per 100 g of the conjugated diene monomer. 7. A process according to Claim 6, wherein the amount of at least one member selected from a surfactant and a dispersant is 10 to 0.001 g per 100 g of the conjugated diene monomer. 8. A process according to Claim 1, wherein the polymerization of a conjugated diene is conducted in the presence of a polymer solution. 9. A process according to Claim 1, wherein the polymer in the polymer solution is at least one member selected from the group consisting of natural rubber, synthetic rubbers and synthetic resins. 10. A process according to Claim 1, wherein the solvent in the polymer solution is at least one member selected from the group consisting of aliphatic hydrocarbons, aromatic hydrocarbons, halogenated hydrocarbons, esters, alcohols, ketones, nitriles and amides. 11. A process according to Claim 1, wherein the concentration of the polymer in the polymer solution is 0.1 to 50% by weight. 12. A process according to Claim 1, wherein the concentration of the polymer in the polymer solution is 1 to 20% by weight. 13. A process according to Claim 1, wherein the cobalt compound (A) is at least one member selected from the group consisting of organic acid salts of cobalt, acetonate complexes of cobalt, triarylphosphine complexes of cobalt halides, pyridine derivative complexes of cobalt halides and alcohol complexes of cobalt halides. 14. A process according to Claim 1, wherein the metal of the catalyst component (B) is at least one member selected from the group consisting of Li, Na, K, Mg, Zn and Al. 15. A process according to Claim 1, wherein the metal of the cobalt compound (B) is at least one member selected from the group consisting of Li and Al. 16. A process according to Claim 1, wherein the catalyst component (B) is a hydride of a metal of Groups I to III of the Periodic Table. 17. A process according to Claim 1, wherein the metal hydride as the catalyst component (B) is at least one member selected from the group consisting of lithium aluminum hydride, sodium boron hydride and lithium boron hydride. 18. A process according to Claim 1, wherein the metal of the catalyst component (B) is at least one member selected from the group consisting of Li, Na, K, Mg and Zn. 19. A process according to Claim 1, wherein the molar ratio of the conjugated diene to the cobalt compound (A) is from 6 to 50. 20. A process according to Claim 1, wherein the molar ratio of the catalyst component (B) to the catalyst component (A) is from 0.3 to 100. 21. A process according to Claim 1, wherein the molar ratio of the catalyst component (B) to the catalyst component (A) is from 0.9 to 50. 22. A process according to Claim 1, wherein the catalyst component (A) is contacted with the catalyst component (B) at a temperature of -30 to 500C. 23. A process according to Claim 1, wherein the contact between the catalyst component (A) and the catalyst component (B) is conducted in at least one solvent selected from the group consisting of aliphatic hydrocarbons, aromatic hydrocarbons and conjugated dienes. 24. A process according to Claim 1, wherein the component (C) is carbon disulfide. 25. it process according to Claim 1, wherein the component :C) is preliminarily added to at least one member selected from the group consisting of a conjugated diene, a solution of a monomer in a solvent and a water medium. 26. N process according to Claim 1, wherein the component (C) is added to the polymerization system after the components (A) and (B) have been added to the system. 27. IA process according to Claim 1, wherein the component (C) is added at a proportion of 0.01 to 100 moles pet mole of the cobalt compound (A). 28. | A process according to Claim 1, wherein the componen (C) is added at a proportion of 0.3 to 10 moles per mole |of the cobalt compound (A). 29. A process according to Claim 1, wherein the conjugated diene monomer is at least one member selected from the group consisting of butadiene and isoprene. 30. A process according to Claim 1, wherein the polymerization system is prepared by mixing a solution of a polymer in an organic solvent, water and a conjugated diene with a catalyst obtained preliminarily by contacting the component (A) with the component (B) in the presence of a conjugated diene, and then adding the component (C) thereto. 31. A process according to Claim 1, wherein at least one member selected from a surfactant and a dispersant is preliminarily added to water. 32. A process according to Claim 1, wherein at least one member selected from a surfactant and a dispersant is added to the polymerization system after the components (A) and (B) have been added to the polymerization system. 33. A process according to Claim 1, wherein the polymerization system is prepared by mixing the component (C) with a solution of a polymer in an organic solvent, water and a conjugated diene monomer and then adding thereto a catalyst obtained preliminarily by contacting the component (A) with the component (B) in the presence of a conjugated diene. 34. A process according to Claim 1, wherein at least one member selected from the group consisting of an antioxidant, an ultraviolet absorber, a foaming agent, a flame retardant, a lubricant, a processing adjuvant, a filler, a dye, a pigment and a polymerization initiator is added to the polymerization system. 35. A process according to Claim 1, wherein at least one member selected from the group consisting of an antioxidant, a foaming agent, a processing adjuvant and a radical generating agent is added to the polymerization system.

Inventors: MATSUMURA, YOSHIO, OKUYA, EITARO, ONO, HISAO
Applicants: JAPAN SYNTHETIC RUBBER CO., LTD.
Application year: 1985
Main classification: C08F36
IPC codes: C08F36, C08F2