ADJUSTMENT METHOD FOR THE PROPERTIES OF CONCRETE

Abstract: The object of the invention is to get the concrete as well to be of good workability as also tough at same time and in addition desiderable for its several other properties, such as e.g. the unit weight and thermal capacity. In the method according to the invention as components of the concrete in variable proportions are used Portland cement or other hydraulic binders, to its particle size below 8 mm being aggregate as well as to their length in continuous grading or gap-graning distributed natural fibres, e.g. wood fibres, which together with the aggregate contain the main part or all of the water quantity required for the hydration of the binder.

Description: ADJUSTMENT METHOD FOR THE PROPERTIES OF CONCRETE The objective of the invention is a method, by which the usage properties of the concrete can be transformed, such characteristics as the workability, the toughness, the unit weight, the thermal insulation capacity, porosity and the acoustic absorption, by using wood fibres or to their mech¬ anic and moisture technical properties approximately the wood fibres corresponding fibres, such as straw, sisal, bamboo etc. The second part of the invention is formed by the production method of the fibrous concrete, whereby dry fibrous concrete mass is used. Out of the concrete several light and hardened easily work¬ able (sawing, nailing, planing) qualities have been deve¬ loped, such as aerated concrete, expanded clay aggregate concrete, foamed concrete and 3L-concrete. Typical for all of these is, however, in common that they are in their way of fracturing rather brittle, especially as far as ten¬ sile failure is concerned. On the other hand, the toughness and the tensile strenght of the concrete has been improved by adding fibres to it. Such fibres have been e.g. steel, glass and sisal fibres. The quantity of fibres is in general 0.5...2 per cent by volume and the length 20...30 mm. Also wood cellulose fibres have been used. The lenght of the cellulose fibres is 2...5 mm. Such fibre reinforcement as well as the combined use of rigid (e.g. steel fibres) and elastic fibres (e.g. natural or artificial fibres) has been suggested in the British patent 1406442. From the German patent DE 3007012 is known the use of the cement and two-component wood fibre. In the method a large quantity (77...85 per cent by weight) of ce¬ ment is used. The water, cement and wood fibres are first mixed into a gruel-like compound, which is then collected on a belt and pressed dry. A similar method of production is in use also for asbestosce ent products and the cellu¬ lose fibres in cement products. All the methods hitherto have had plenty of disadvantages, wherefore an extensive use of them in the building and other industry has not been possible. The worst disadvan¬ tage has been the fact, that the workability properties of the concrete have not been improved well enough. Many methods require also expensive rawmaterials, in particular plenty of cement, as for instance the method described in DE 3007012. In those methods, where only short fibres are used, no sufficient toughness or workability proper¬ ties have been achieved to the concrete. The admixtures used have often other disadvantages as well: the glass fi- bres are corroded in the concrete abating the properties of the concrete in a short time. In such cases when dense concrete is wanted, such as in roofing slabs, the problem is the porosity caused by water. The object of this invention is to get the concrete as well to be of good workability as also tough at same time and in addition desiderable for its several other proper¬ ties, such as e.g. the unit weight and thermal insulation capacity. The object of the invention has been attained with the method, of which are characteristic the matters appearing from the patent claims. The basic idea of the invention is to get the concrete re¬ markably deviating from ordinary concrete with the help of fibres by using only a small quantity of hydraulic binder the main part of the volume of the material being wood fibres and aggregate. The consistency of the compound has at the same time been made well adaptable to the combined compression-vibration compaction, which makes a simple and economical production possible. The binder of the concrete can be utilized with optimal efficiency by bringing the water required for the hydration into the mass absorbed in the fibres, whereby it is discharged from the fibres slowly and does not form in the compaction phase detrimental ca¬ pillary pores in the cement stone. The concrete in accordance with the invention, which has . good toughness properties at the same time as the workabi¬ lity is also good, and the unit weight, the thermal insu¬ lation capacity, the porosity and the acoustic absorptivity of which are within certain limits as they are desired, is achieved by using fibre reinforcement of different mea¬ surement classes together with a hydraulic binder and the aggregate. Characteristic to the fibre reinforcement in accordance with the invention is, that in the method fibres of different measurement classes are used mixed together with each other. The length distribution of the fibres may •vary and be of continuous grading or within some certain intervening space of gap-grading. Short fibres are used to give the cured cement adhesive workability and toughness, as well as in case of need long fibres to bind together parts of the cement adhesive over the aggregate particles, cracks and short fibres, whereby the concrete is made tough even when the aggregate particles are broken or disjoined in the fracture situation. The other propeties, such as the unit weight, the thermal insulation capacity, the po- rosity and the acoustic absorptivity can be varied by chan¬ ging the proportions of short and long fibres as well as that of the aggregate. The fibres can most suitably be wood fibres, but also other natural and artificial fibres possessing approximately the mechanical and moisture tech- nical properties of the wood fibres can be used. Normally two types of cracks occur in the concrete, which deteriorate the toughness of the concrete particularly under tensile stress. In the cement stone occur small microcracks and in the cement under extension strain macro- cracks set on. In the two-component fibre reinforcement short fibres are used to transfer the tensions over the macrocracks. In this manner the toughness properties of the concrete can be increased in a desired way. The method in accordance with the invention has been illus- trated in the figure, which shows a principal figure of the co-operative functions of the short and the long fibres. In the figure there has been described short wood fibre 1, long wood fibre 2, small aggregate particles 3, large aggre¬ gate particles 4, cement adhesive 5, macrocrack 6 and micro- cracks 7. Generally it is suited to use such a quantity of short fibres as is required in order to achieve a good workability of the fresh concrete mass and the hardened concrete. In such cases where the main goal is to get a dense and tough concrete, only short, water imbibed fibre is used. By varying the total quantity of fibres as well as the proportions of the short and long fibres the properties of the hardened concrete can be adjusted in the desired way. By increasing teh quantity of the shoet fibres the variable properties of the concrete can be improved up to a certain degree. The workability of the concrete mass in fresh form gives, however, a limit to the quantity of the short fibres, whereafter the variation of the properties of the concrete takes place by increasing the quantity of the long fibres. The increased quantity of fibres improves on the toughness of the concrete, on the thermal insulation capacity, on the workability in hardened form, adds to the porosity and improves the acoustic absorption. These pro- perties play an important role in several constructions of the workshop and residential buildings. When a dense but still to a certain degree tough and in hardened form work¬ able concrete is wanted, only short fibres are applied. When using wood fibres or other natural fibres of different measurement classes mixed together with each other even very large quantities of fibres can easily and economically be mixed into the concrete, up to several tens of per cent by volume. Hereby the properties of the concrete can be varied favourably approximately within the following limits: Workability of the hardened concrete with saw, ax, knife nad ordinary nails from processable up to the hardness of the ordinary concrete. Tensile strength generally between 1...5 MN/m 2 . The ratio between the tensile and compressive strength generally between 0.25...1.0 the ratio being for ordi- nary concrete about 0.10. The density approximately between 800...2000 kg/m 3 . The toughness measured as deformation work approxi¬ mately 5...50 times bigger compared with concrete possessing the same compressive strength. - The compressive strength approximately between 1 MN/m 2 ...20 MN/m 2 . The modulus of elasticity between 5000...20000 MN/m 2 . The thermal insulation capacity between 0.10...0.80 W/m°C. - The permeability of aqueous vapour between (10...50)- 10 -1 kg/msPa. In surveys it has been proved, that the cement adhesive gives the wood fibres a rather good protection against rot. The wood fibrous concrete has also depending on the quanti¬ ty of the wood fibres a fire resistance of different degree and it is a non-flammable material. The material is made economical by using only fairly little, about 15...40 per cent by the volume, of the binder, which is more expensive than the other components, and in addi¬ tion to that always aggregate, whereby the joining together of the wood fibres is taking place with the help of the cast stone formed together by the hydraulic binder and the aggregate. As aggregate can be used either to its particle size mainly between 0.1...8 mm being natural aggregate or to its particle size within the same range being other aggregate, such as pulverized fuel ash, expanded clay aggregate or perlite. The binder can be either Portland cement or other hydraulic binder, such as blast-furnace cement, pulverized fuel ash or natural pozzuolana. The wood fibrous concrete can not due to the elasticity of the wood fibres be compacted efficiently by vibration alone,as in the case in common, when it is the question of ordinary concrete. When making other fibrous products, such as asbestoscement products usually a compression or a combined compression and vibration compaction is applied. The mass of the asbestoscement products and e.g. that of the German patent DE 3007012 regarding wood fibrous cement is produced by mixing a large quantity of water, the fibres and the cement into a watery sludge, which is collected on a belt and compressed dry and compact. This production method is fairly complicated and expensive and it succeeds only then, when plenty of cement is used and the product to be made is a thin sheetlike product. In order to achieve a sufficient strength and a small shrinkage to the concrete it is worth while to make the water-cement ratio small. In particular the demand for a small water-cement ratio is accentuated in the otherwise for the fibrous concrete mass very well suited, with the compression-vibration method performed compaction, where the water content of the mass is very detrimental. The water in the concrete mass causes capillary pores in the mass, which deteriorate the strength and density of the cement stone created in the hydration. When the fibrous concrete is concerned, the water included in the fresh mass makes also the adhesion between the cement stone and the fibres weaker. . In the compression-vibration compaction the water trends towards the surface, whereby the formation of the capillary pores is still increased. A product manu¬ factured with the compression-vibration is made coherent right after the compaction, if the water-cement ratio is small enough. Differently from the situation in the fibrous cement pro- ducts described above, in the fibrous concrete in accor¬ dance with this invention no soft watery compound is formed but a very dry mass. This takes place in such a way, that the fibres are soaked for sufficiently long period of the time, e.g. for 24 hours prior the mixing of the concrete, in water or in a water solution containing substances suitable for a pretreatment of the fibres, whereby water is absorbed into the fibres. When fibres are used in sufficient quantities, the amount of water absorbed in the fibres is enough for hydration of the cement quantity used, wherefore no water is added to the mass in the making process. When using big quantities of fibres, the amount of water contained in the fibres may be unnecessarily and to a certain degree even detrimentally large, whereby the fibres can partly be dried mechanically through pressing or through evaporation of a suitable part of the water before the mixing of the mass. The water required for the hydration of the binder is particularly favourable to be tranferred to the concrete mass absorbed in the fibres for the very reason, that the water is detacted for the use of the binder to be hydrated slowly in the proceeding of the hydration, whereby the cement stone produced develops to be favourably dense and strong. At the same time the bonding between the cement stone and the fibres becomes optimally good. A small part of the water is generally transferred into the concrete mass in form of the moisture contained in the dry aggregate. The in this way produced fibrous concrete mass is suitable to be compacted with the help of the combined compression and vibration method. The manufactured product is well cohe- rent right after the compaction, wherefore it can be re¬ moved in connection with the continued processing. In the method according to the invention it is advantageous when the dry weight proportions of the different component part materials in the concrete vary between the following intervals: wood fibres 2 per cent...40 per cent, binder 20 per cent...50 per cent, aggregate 10 per cent...50 per cent and the water content in the fibres and the aggregate 15 per cent...40 per cent. Furthermore in the concrete can be used desired admixtures, such as e.g. accelerators, air-entraining agents and plasticizers. The dry weight proportions of the length distribution in the fibres can vary within the following limits of the total quantity of the fibres: short wood fibres (length 1...5 mm) 10 per cent...100 per cent, medium long fibres (length 5...15 mm) 0 per cent...30 per cent and long fibres (lengths exeeding 15 mm) 0 per cent...90 per cent. Suitable objects of use for wood fibrous concrete are for instance: bearing and non-bearing walls and plates of small houses, which can easily be machined in prefabri- cation plants for parts and on working site constructions of agricultural production building constructions of small industrial buildings in export objects small, of low cost housing- type, easily assembled residential buildings, which are not-rotting nor inflammable and resis¬ tant against termites and other organisms - roofing slabs and partition walls in apartment houses. The decisive benefit of the fibrous concrete in accordance with this invention is its economical and technical advan- tageousness in regions, where available is cement, fairly fine-grained natural aggregate or e.g. expanded clay aggre- gate and wood fibres. It is worth while to transport cement and wood fibres even fairly long distances due to their small part by the volume. Thanks to its toughness such wood fibrous concrete is favourable to use as relati¬ vely thin, but generally thicker than common sheating-plate sheetlike products. The material is very suitable for as well bearing as partitive constructions. An advantage of it compared with ordinary concrete and with the most of the fibrous cement products is also the possibility to get the density fairly low. Due to the sugar contained in the wood fibres a suitable chemical pretreatment, e.g. a soaking in NaOH or Ca(0H) 2 - solution, is required in order to prevent a prolongation of setting time of the cement. When Using bleached cel¬ lulose fibres the elimination treatment of sugar is super¬ fluous for its parts. Due the elasticity of the wood fibres and in order to improve the adhesion of the fibres the compression-vibration method is the most favourable mode of compaction. In the preceding explanatory part the main forms of appli- cation of the invention have been exposed. The adjustment method for the properties of the concrete in accordance with the invention can to its form of application vary even extensively within the frames of the claims.

Claims: CLAIMS 1. Method for transformation of certain properties of the concrete, such as the workability, the toughness, the unit weight and thermal insulation capacity, performed by means of using wood fibres, c h a r a c t e r i s t i c in that, as components of the concrete in variable proportions are used Portland cement or other hydraulic binders, to its particle size below 8 mm being aggregate as well as to their length in continuous grading or gap-grading distributed natural fibres, e.g. wood fibres, which together with the aggregate contain the main part or all of the water quan¬ tity required for the hydration of the binder. 2. Method according to the claim 1, c h a r a c t e r i s¬ t i c in that, the properties of the concrete are trans- formed by varying the propotions of the short and long natural fibres, the binder and the aggregate. 3. Method according to claim 1 or claim 2, c h a r a c ¬ t e r i s t i c in that, the dry weight proportions of the different component part materials in the concrete vary between the following intervals: wood fibres 2 per cent... 40 per cent, binder 20 per cent...50 per cent, aggregate 10 per cent...50 per cent and the water content in the fibres and the aggregate 15 per cent...40 per cent. 4. Method according to one of the claims 1-3, c h a r a c¬ t e r i s t i c in that all the water needed for the hardening reactions of the binder is brought into the concrete mass absorbed in the wood fibres by means of soaking the wood fibres prior to mixing of the mass in water or in a water solution containing substances sui¬ table for the pretreatment of the wood fibres. 5. Method according to one of the claims 1-4, c h a r a c- t e r i s t i c in that in the concrete desired admixtures has been used, such as accelerators, air-entraining agents and plasticizers. 6. Method according to one of the claims 1-5, c h a r a c- t e r i s t i c in that the aggregate is natural aggregate or artificial aggregate, pulverized fuel ash, expanded clay aggregate or perlite. 7. Method according to one of the claims 1-6, c h a r a c- t e r i s t i c in that the dry concrete mass is compacted by means of compression or by means of a combined compres¬ sion and vibration. 8. Method according to one of the claims 1-7, c h a r a c- t e r i s t i c in that the density of the concrete varies between 800 kg/m 3 ...2000 kg/m 3 . 9. Method according to one of the claims 3-8, c h a r a c¬ t e r i s t i c in that as fibres instead of wood fibres can also other natural fibres possessing approximately corresponding mechanical and moisture absorption proper¬ ties be used. 10. Method according to one of the claims 1-9, c h a r a c- t e r i s t i c in that the dry weight proportions of the length distribution in the fibres vary within the following limits of the total quantity of the fibres: short wood fibres (length 1...5 mm) 10 per cent...100 per cent, medium long fibres (length 5...15 mm) 0 per cent...30 per cent and long fibres (lengths exceeging 15 mm) 0 per cent...90 per cent.

Inventors: SARJA ASKO, SARJA, ASKO
Applicants: VALTION TEKNILLINEN, VALTION TEKNILLINEN TUTKIMUSKESKUS
Application year: 1985
Main classification: C04B18
IPC codes: C04B18, C04B28