TRANSDERMAL METHODS AND ADHESIVES

Abstract: Pressure sensitive adhesives for transdermal devices. The adhesive composition is such that rates of fluid or vapor transmission can be controlled. The invention provides a fluid permeable adhesive in which a pressure sensitive polymer is blended with a cross-linked polysiloxane. Vapor or fluid transmission through the adhesive is controlled by the extent which the cross-liked polysiloxane is blended with the polymer. The adhesive can be coated on a plastic or cloth layer. The adhesive layer is protected by a release substance which is peeled upon use.

Description: TRftNSDERMAL METHODS AND ADHESIVES Background of the Invention This invention relates to adhesives which provide suit¬ able dermal adherence , such as to human skin. The invention relates more particularly to pressure sensitive adhesives for transdermal therapeutic devices. Pressure sensitive adhesives for skin are typically in the form of bandages or therapeutic devices which adhere for prescribed periods of time. Such structures typically include a plastic or cloth layer that is coated with pressure sensi¬ tive adhesive. The latter is protected by a release substrate which is peeled from the adhesive when the device is to be used. There are a number of physical characteristics that should be satisfied. The release substrate should be easily peelable from the adhesive and the latter musjb be sufficiently cohesive to maintain contact with skin for prescribed periods of time. In addition when the adhesive is used with human skin it must be non-toxic and not cause inflammation. In addition transdermal therapeutic devices must meet strict performance standards. The typical transdermal device • ' - is a pouch which contains a liquid medicine that is absorbed gradually into the skin. Such devices typically contain a semi-permeable membrane and are used with absorptive drugs such as nitroglycerine or agents for cardiac treatment. Con¬ sequently any pressure sensitive adhesive that is coated on the therapeutic device must not act as a barrier to the treatment fluid. Furthermore, since a therapuetic device remains in close adhesive contact with skin over an appreciable period of time, typically up to 24 hours, the adhesive must remain active over the entire period. The adhesive should also per¬ mit the therapeutic device to be peeld from the skin without causing discomfort or leaving an objectionable residue. The prior art is illustrated by U.S. patents 2,857,356 and 4,039,707. In U.S. Patent 2,857,356 a pressure sensitive adhesive is formed by the polymerization of a silicate resin and an organopolysiloxane fluid. The silicate resin is . obtained by intercondensation of the cohydrolysis product of a trialkyl hydrolyzable silane and an alkyl silicate. The cohydrolysis product contains a number of silicone-bonded hydroxy groups. The formulation forms a pressure sensitive adhesive with a high degree of tack and cohesion over a wide temperature range. It is principally an adhesive coating for contacting polymeric materials such as glass and a wide range of plastics including polyethylene. The adhesive is also used in the manufacture of pressure sensitive tapes, but there is no suggestion that the adhesive could be applied to skin. In order to achieve a high degree of tack and cohesive strength, the weight ratio of silicate resin to organopoly¬ siloxane fluid is between about 0.5 and 6 to 1, more prefer¬ ably between about 1 to 1 and 3 to 1. Such a range would' not be suitable for transdermal therapeutic devices because of insufficient tack for human skin and too great a time lapse to achieve maximum bonding. U.S. Patent 4,039,707 discloses a siloxane pressure sensitive adhesive which is the intercondensation product of an σrganopolysiloxane resin and an alkylaryl polysiloxane gum. The organopolysiloxane resin has the formula (OH) q (OR 2 ) r R 2 SiO rqrr/2 . It is essential that the organopolysiloxane gum contain aryl groups, such as phenyls, to obtain optimum pressure sensitive adhesion. If a mixture of phenyl- and methyl groups is employed, the number of silicone-bonded phenyl groups should be in a range such that, for each 7 to 75 phenyl groups attached directly to the silicone by a carbon-silicone linkage, there are from 29 to 25 silicone-bonded methyl groups. A preferred range is from about 5 to 15 phenyl groups per 95 to 85 methyl groups. Also disclosed is a release substrate for the pressure sensitive adhesive. The release substrate typically is a paper or polymer film coated with a silanol-stopped dimethylpolysiloxane fluid. Another disclosed release coating is a dimethylvinyl-stopped dimethyl polysiloxane fluid. Additionally, the alkylaryl polysiloxane gum should have a viscosity from about 200,000 to 15-million centipoise at 25 β C. and contan an average from about 1.85 to 2.01 silicone- bonded alkyl and aryl radicals per silicone atom. Although the use of an alkylaryl polysiloxane gum with an organopolysiloxane resin is disclosed in Patent 4,039,707, there is no suggestion of combining alkylaryl polysiloxane gums to improve adhesive, shear and liquid permeability, so that the adhesive product could be used with transdermal therapeutic devices. U.S. Serial No. 451,625, filed December 20, 1982, dis¬ closes a transdermal adhesive formed by the polymerization product of an aryl polysiloxane, an alkyl polysiloxane and an MQ polysiloxane with multifunctional siloxane units. This product is suitably non-toxic and non-irritating. It also provides suitable adhesion. It does not, however, permit control over the rate of fluid passage. Consequently this adhesive is not suitable for many medicinal applications. Accordingly, it is an object of the invention to pro¬ vide a transdermal adhesive in which the rate of fluid or vapor transmission can be controlled. A related object is to acheive a transdermal adhesive in which the rate of fluid transmission can be specified with precision. Another object of the invention is to provide a fluid transmission controllable adhesive which can be used to retain a plastic film or therapeutic device in adhesive con- tact with human skin and is both non-toxic and easily remove- able. An important object of the invention is to provide a fluid transmission controllable pressure sensitive adhesive for transdermal therapeutic devices. A related object is to •| provide a pressure sensitive adhesive which can retain a therapeutic device in adhesive contact with skin over a pro¬ longed period of time and not interfere with precision control over the absorption of medicinal fluid. Summary of the Invention In accomplishing the foregoing and related objects, the invention provides a fluid permeable adhesive in which a pressure sensitive polymer is blended with a cross linked polysiloxane. Vapor or fluid transmission through th'e adhesive is controlled by the extent to which the crσsslinked polysiloxane is blended with the polymer. The vapor transmission increases and decreases in sawtooth fashion as the ratio of polysiloxane to polymer changes. In accordance with one aspect of the invention, the amount of crosslinked polysiloxane ranges from more than 0 to less than 100% of the total adhesive composition. A desirable adhesive includes a crosslinked polysiloxane ranging up to 10 , up to 30% or up to 70%, depending upon the polymer. In accordance with another aspect of the invention, the polymer is selected from the class of acrylics, urethanes, elastomers and blends. The final polysiloxane is formed by the crosslinking of a plurality of subordinate siloxanes which can be aryl and/or alkyl. In accordance with yet another aspect of the invention, a fluid permeable adhesive is prepared by blending a crosslinked polysiloxane with an adhesive polymer which can be acrylic, urethanic, elastomeric or a blend. In accordance with still another aspect of the invention, fluids can be administered to an epidermal layer through a contacting blend of a crosslinked polysiloxane and a non- silicone polymer. Fluid is then applied to the blend to permit passage through the adhesive at a prescribed rate. In accordance with a further aspect of the invention, a medical device can be provided by being partially coated with a blend of a pressure sensitive non-silicone polymer and a cross¬ linked polysiloxane. A suitable catalyst for the crosslinking of polysiloxane is a diaryl peroxide which advantageously is included to initiate the polymerization, for example of a siloxane gum and an MQ resin. When the catalyst is omitted the polymerization can be initiated in other ways. Although it has been widely assumed that non-silicone polymers are imcompatible with polysiloxanes, compatability can be achieved in accordance with the invention to control vapor transmission through the resulting adhesive blend. The end product has characteristics that make it particularly suitable for use as a pressure sensitive adhesive for transdermal thera¬ peutic applications. In the case of a siloxane gum and resin, the weight ratio of gum to resin is preferably in the range between 1 to 3. and 3 to 1. Where a catalyst is employed i ' t may be between 0.1 and 2% by weight of the final adhesive. A preferred catalyst is 2,4 dichlobenzoyl oxide which contains a phlegmatic agent such as dibutylphtalate. The formulation may also include polybutene resin in the amount up to a 15% by weight of the final product. The polymerized product is preferably prepared by forming a raw adhesive solution of reactants and solvents such as toluene, naphtha xylene and acetate. The final adhesive can be prepared by mixing the consti¬ tuents until a homogeneous blend is formed. The blend is then coated on a release substrate which is typically a paper sheet overcoated with a silicone. This forms the desired adhesive laminate. The laminate is dried to vaporize the solivents, after which the laminate is heated to temperatures necessary to initiate a polymerization reaction between the siloxane consti¬ tuents. Alternatively, the siloxane crosslinking may precede the blending operation. The final adhesive laminate may be applied to a surface of a transdermal device with the adhesive coating in direct con¬ tact with the device. Preferably, the adhesive is in contact with a semiper eable membrane of the defice. In use, the release is peeled away to expose the adhesive, which is applied to the skin. The final pressure sensitive adhesive formulation exhibits unique liquid permeability and a high degree of adhesion to skin, with negligible irritation. It also has excellent release properties, permitting easy removal of the release substrate from the adhesive. ■ Dβscription of the Drawings Other aspects of the invention will become apparent after considering several illustrative embodiments taken in conjunction with the drawings, in which: FIGURE 1 is a graph of vapor transmission for one set of transdermal adhesives in accordance with the invention; and FIGURE 2 is a graph of vapor transmission for another set of transdermal adhesives in accordance with the invention. Detailed Description The pressure sensitive adhesive of the invention is a blend of a polymer and a cross-linked polysiloxane. The poly¬ siloxane may be formed from siloxane gums, or one or more βilox- ana gums and one or more siloxane resins. Suitable siloxane gums are dimethyl siloxane and dimethy1- diphenyl siloxane. The term "gum" denotes a relatively high viscosity material, e.g. greater than about 20,000 centipoise. Such gums include linear alkyl aryl polysiloxaneβ or polydiorgano- siloxaneβ that can be converted from a highly viscous plastic state into a predominantly elastic state by cross-linking. W. Noll, "Chemistry and Technology of Siliconeβ", Academic Press. New York (1958) , page 387. Siloxane gums are also known as "organosiloxane elastomers". The term"resin" refers to a siloxane polymer. The pressure sensitive adhesive resulting from the blend of a cross-linked polysiloxane and a polymer is useful for attaching transdermal therapeutic devices to human skin for periods up to about 24-hours. The adhesive exhibits a favorable peel release and a high degree of adhesion over a long period. The adhesive is particularly suited to medical applications by being easily removable and non-irritating. The adhesive permits the medication in the transdermal device to pass through the adhesive into the skin. Transdermal devices known in the art are formed by a semipermeable, microporouβ membrane, or membranes, for storing liquid medication and releasing the medication at a prescribed rate over a prolonged period. The transdermal device containing liquid medication is applied directly to the skin as a bandage. The βe ipermeable membrane in contact with the skin is provided with an adhering pressure sensitive layer. U.S. patents 4,200,093 and 4,201,211 disclose representa¬ tive transdermal devices with which the adhesive of the invention can be used. In general the adhesive of the invention is applicable to all transdermal devices which must be placed in adhesive contact with skin. Adhesives for transdermal therapeutic devices should satisfy a number of requirements. The adhesive should allow uninterrupted liquid flow over a prolonged period, up to six hours and preferably 24 to 36 hours and longer. The flow is desirably at a constant rate through the semiper eable membrane into the skin. Therefore, the adhesive cannot form a barrier between the membrane and the skin-during use, and should not measurably retard the flow of medicine. The adhesive of the invention satisfies the foregoing requirements and is to be contrasted with conventional pressure sensitive adhesives which significantly retard the through low of liquids, particularly over prolonged periods. Additionally the adhesive should not cause undue skin irritation, including swelling, redness or itching on prolonged contact. The adhesive should also allow relatively easy removal without discomfort. Nor should the adhesive detoriate or peel or loosen over the period of application. Moreover, there should be little or no adhesive residue remaining on the skin after the transdermal device is removed. A pressure sensitive adhesive blend in accordance with the invention, which satisfies the above requirements, is presented as Formulation A of Table I. Formulation A is composed of raw adhesive solutions which are dried to evaporate the solvents and then cured to form the polymerized adhesive product of Table I. The acrylic resin of Table I is a self cross-linking pro- duct sold under the designation "80-1054" ( DM-808)" from National Adhesives. It is mixed with a suitable solvent such as toluene, naphtha, xylene or n-butyl acetate. No catalyst is needed since this resin is self cross-linking. The cross-linkable polysiloxane is formed from a mixture of MQ resihs. An MQ resin is formed from monofunctional and quadrifunctional siloxane units and has the generic chemical formula (1) t M Q (1) where- M _■ V i0 l2' Q - SiO.,- and R β preferably a methyl group. R may also include other alkyl groups, particularly C. to C 4 , i.e. methyl to butyl. In particular the siloxane gum plus MQ resin of Table I e.g. SR6574 is a mixture of dimethyl-diphenyl siloxane gum and an MQ resin that is separately available under the trade name CR542 from the General Electric Company. In general the combination of an MQ resin or other organopolysiloxane resin is mixed with a meth l/phenyl siloxane gum which typically has a viscosity between 20,000 and 10,000,000 centipoiβe at 25*C, preferably between 20,000 and 1,000,000 centipoise. The molar ratio of phenyl groups to methyl groups in dimethy1/diphβnyl siloxane gum is at least about 0.1 to 1 and preferably in the range up to 0.2 to 1. Another suitable MQ resin is sold under the name C42 -2109 of the Dow Corning Company of Midland, Michigan. This resin mixed with dimethyl siloxane gum is available under the designation 280A from the Dow Corning Company. The preferred catalyst is a diar 1 peroxide type such as that containing 2,4 dichloro benroyl peroxide, which contains a phlegmatic agent such as dibutyl phthalatβ. Such a catalyst is available under the tradename CADOX TOP from the Noury Chemical Company of Burt, New York. Suitable solvents of Table I are tOluene, naptha, xylene and butyl acetate. Other solvents may be used Including ester ethyl acetate. Although the catalyst of Table I Is preferably a dichloro peroxide, other catalysts may be employed, such :.as dlacyl peroxide, ami no- salines, secondary or tertiary amines; or an organic tetanate, such as terrabutyl tltanates available under the tradename TYZO TBT from the DuPont Company of Wilmington, Delaware. Alternatively, the catalyst may be omitted and polymerization Initiated in other ways , such as by radiation or electron beams. The raw adhesive constituents such as those in Table I are mixed In a suitable vat until a homogenous solution is achieved. Although the com¬ ponents may be added in any order, it 1s advantageous to pre-mix the catalysts and solvents followed by the addition of the remaining constituents. The homogenous raw solution is then coated on a release substrate typical ly a paper sheet with a rel ease coating, such as a conventional sil lcone - release fluid. An appropriate sil icone release fluid 1s polydlmethyl vinyl sil icone with appropriate catalysts , including a noble metal complex. The overcoated release substrate forms an adhesive laminate which Is dried, typically 1n conventional convectlve driers operating between about 100°F and 200°F. The solvents are- evaporated from the raw adhesive. The dried adhesive laminate is then cured in an oven at a temperature between 200°F and 350°F, where crossljjiking occurs. The adhesive lcurάnate cont ning the cured product may be transferred directly to a surface of transdermal therapeutic device, such as-the semipermeable membrane. The transfer may be accomplished by passing the laminate and semipermeable membrane of the therapeutic device through a conventional laminate. The adhesively coated membrane is then shaped to match the associated transdermal. In the use of the device, the patient peels the release substrate from the lεurάnate to expose the adhesive membrane so that direct contact can be made between the adhesive and skin. As noted in Table I, the resulting product has a vapor transmission of 9.42 grams per 24 hour period. This result is indicated in the graph of Fig. 1 for a 10% silicone blend with 90% acrylic resin. Other vapor transmission results for other blends and other constituants are also summarized in Fig. 2. It is to be noted that for both Figs. 1 and 2 that the invention permits control over vapor transmission by controlling the ratio of the constituants in the blend. The vapor transmission data of the Examples and Figures 1 and 2 were obtained by testing adhesive, with a thickness of 1.5 mils, placed in a standard testing cup on a urethane film with a thickness of one mil. As a result the data include the influence of the film, which has an average weight loss of 14 grams per 24 hours for a cup with a surface area of about 7 square inches. The testing is conducted in accordance with ASTM (American Society for Testing and Materials) E96-80, for which "E96" is the fixed designation and "80" is either the year of adoption or the year of last revision. - 13 A - In accordance with Standard Test Method E96-80, the Water Method is used with a cup that contains distilled water. Water Vapor transmission rate is the steady water vapor flow in unit time through unit area of a body, normal to specific parallel surfaces under specified conditions of temperature and humidity. The test cup is of noncorroding material, impermeable to water or water vapor. The mouth of the cup is at least 4.65 in. (3000 imr ) . An external flange or ledge around the mouth is used to attach the specimen. Since the specimen is an adhesive it is supported by a membrane which is masked so that the mouth area defines the test area. The cabinet where the test cup is placed has a controlled temperature and relative humidity. The temperature is between 70 and 90°F(21 and 32°C), and maintained constant within 1°F (0.6°C). A temperature of 90°F (32°C) is recommended. The relative humidity is maintained at 50 ± 2%. Air is continuously circulated throughout the chamber, with a sufficient velocity to maintain uniform conditions. Distilled water is used in the test cup. The sealant used for attaching the specimen is resistant to the passage of water vapor. Molten asphalt or wax is used. The sample is of uniform thickness. The specimen is attached to the cup by sealing so that the cup mouth defines the area of the specimen exposed to the vapor pressure in the dish. The test cup is filled with distilled water to a level 3/4 ± 1/4 in. (19 + 6 mm) frcm the specimen. The resulting air space has a small vapor resistance. If the equivalent water vapor transmission (WVT) is desired, it can be obt ned fran equation (1 ) . - 13 B - WVT = G/tA ( 1 ) where G = weight change t = time in hours A = test area (effective mouth area) When metric units are employed WVT is in grams per square meter per hour. When inch-pound units are employed the result is in grains per square foot per hour. The characteristics of the support member can be cαipensated in standard fashion when it is desired to know the water vapor transmission characteristics of the adhesive alone. Dete:_mination of the water vapor transmission can be determined from equation (2) . 1 (2) V t Vm Va where V = total vapor transmission for membrane and adhesive sample V m = vapor transmission of the membrane alone V a = transmission of the sample For example, if the total vapor transmission is 9.0 gms for a sample of 1.5 mils in thickness on a membrane of 1.0 mils with a vapor transmission of 14.0 gms, equation (2) becomes equation (3) : - 13 C - (3) 14 V The result is Va = 25.2 grams for the vapor transmission of the sample. Since the sample has a thickness of 1.5 mils, the- transmission per mil is given by equation (4) . where ta = thickness in mils Va/m = 25 . 5 x 1. 5 » 37. 8gms (5) Equation (5) is for a surface area of about 7.0 square inches (and 24 hours). To convert to equation (1) equation (5) is divided by 24 (the number of hours) and multiplied by 221.43 (the reciprocal of the area in square meters) . -14- TABLE I Preaaure Senaitiva Adhaaive (PSA) - Formulation A Raw Adhesive Acrylic rβain (e.g. 80-1054) 39.6 grams Siloxane gum plus MQ resin (e.g. SR6574) 4.41 gxamβ Catalyst (e.g. CADOX TOP) 0.44 grama Solvent 1 42.16 gra s Solvent 2 11.35 grams Temperature 24*C. Relative Humidity 38* Polymerized Preaaure Senaitiva Adhaaive Product A Acrylic resin 90%* Siloxane gum plus MQ resin 10** Catalyst W* - Coating weight 1.5 mils Vapor Transmission 9.42 grams per 24 hours *Percentage of final adhesive composition -15- Exampl e VI Example V was repeated except that the acryl ic resin was reduced to 50X of the final composition and siloxane Increased to 50X. 54.55 grams of wet adhesives were used with 53.00 grams of wet siloxane. The peroxide was 0.532 grams. The vapor transmission as noted In Fig. 1 was 9.83 grams. Example VII Example VI was repeated except that the acryl ic resin was reduced to 25X and the siloxane correspondingly Increased to 75X. 29.3 grams of wet acryl ic were used; 56.77 grams of wet siloxane, and peroxide was 0.569 grams. As noted In Fig. 1 , the vapor transmission after 24 hours was 5.78 grams. Example VIII Example VII was repeated except acryl ic resin was Increased to 90S and siloxane was a gum sold under the designated C-154 of the SWS SIHcone Corp. 's (lot P3404) . The percent sol ids of the siloxane gum was 54.14X, 80.8 grams of wet acryl ic, 8.24 grams of wet gum. The catalyst. was 0.43 grams of peroxide. The vapor transmission after 24 hours amounted to 7.77 grams Examples IX through XIV Prior examples were repeated with a pressure sensitive acryl ic solution resin designated as "1085" from Ashland with 45. I X solids which were used In place of the acryl ic in the prior examples. In al l cases IX peroxide was used. For 100X of acryl ic and no siloxane, vapor transmission was 9.06 grams. For 90X acryl ic, 10X siloxane, vapor transmission 7.69 grams ; for 80X acrylic, 20X siloxane, vapor transmission 10.24 grams ; for 70X acryl ic, 30X siloxane, vapor transmission 10.82 grams.; for 60X acryl ic, 30X siloxane, vapor transmission 4.92 gra s ; for 50X acrylic, 50X siloxane, vapor trans¬ mission 5.04 grams. . Using a pure film as a control with no adhesive, the vapor transmission 1n the first experiment was 14.1 grams and 13.9 grams In the second experiment. -16- Exa ples XV through XVII The prior examples were repeated with an electronbeis curable adhesive fros PPG Industries , designated SR91 3A which was substituted for the acrylic in the prior examples. For 100% adhesive and no siloxane the vapor loss was 7.5 grans, corresponding to vapor transmission 2380.88 grass per sq. meter per 24 hours. For 80X adhesive and 20X siloxane, vapor loss of 8.04 grans, corresponding to transmission 2552.30 grams per sq. meter per 24 hours. For a 50X mix of adhesive and siloxane, vapor loss 1.3 grams , correspond¬ ing to a transmission 2580.87 per sq. meter per 24 hours. Exanples XVI I I through XXI The foregoing were repeated with rubber-base adhesive substituted for acryl ic. The rubber base adhesive had the designation V-88 and 72-9494 (8320) from National Starch. Kith 70 rubber-base adhesive and 30X siloxane, the vapor loss was 2.56 grams, corresponding to 812.67 grams per sq. meter per 24 hours. For 601 rubber-base adhesive and 40X siloxane, vapor loss was 4.36 grams (1379.7 grams per sq. meters per 24 hours) . For a 50/50 blend, the vapor loss was 4.36 grams while for 25X rubber- base adhesive and 75X siloxane, the vapor loss was 9.16 grams or 2898.7 grams per sq. meter per 24 hours. Examples XXII through XXV The foregoing examples were repeated with a siloxane rubber compound C-154 substituted, for prior slloxanes. The resul ts for a 1 OX- 901 blend are reported In Example VIII. For 20X siloxane rubber and 80S acryl ic, the loss was 8.61 grams (27204.6). For 30X rubber siloxane and 70X acryl ic, loss was 6.6 (2088.6) . For 40Ϊ rubber siloxane and 60S acryl ic, loss was 7.78 (2462.0) . ' Exanples XXVI through XXVIII The prior exanples were repeated with fluorosll gum substituted for the prior slloxanes. This gun was available under the LS420 In ethyl acetate solvent. For 20X gun and 80X acrylic vapor loss 45.19 (1647.56). For 30X gum and 70S acrylic, vapor loss was 6.06 (1923.75). For a 50/50 blend, loss was 4.51 (1431.7). For the film alone without any gum, the loss varied between 12.58 grams (3993.52) and 15.51 grams (4954.47). When the 6574 siloxane was superimposed on the film with the thickness of 1.5 mils., the loss significantly decreased to 6.02 grams (1911.05). Examples XXIX through XXXV The foregoing procedures were repeated with an acrylic pressure- siπsitive adhesive from Monsanto, RA737 (V-75) (lot 7081) substituted for the prior acrylic. For 100X acrylic the vapor loss was 9.66. For 90X acrylic and 10X siloxane, the loss was 6.5. For 80X acrylic and 20X siloxane, the loss was 5.82. For successive reductions to 70 - 65 - 50 and 25X acrylic, corresponding losses were: 5.84 - 6.66 - 6.82 and 5.12. Examples XXXVI and XXXVII When urethane was substituted for the acrylic, 100X urethane gave a vapor loss of 3.2 grams while 90X uretaπe and 10X siloxane gave a loss of 3.36 grams

Claims: - 1 8 - WHAT IS CXAIMED ISi 1. A fluid parsMsbls adhaaive, comprising a prssaurs asnsitivs polymer and a cross-linked polyβiloxana blended with said polymer. 2. The adheβirβ of claim 1 wherein said polymer is selected from the class consisting of acrylics, αrethanea, elastomers and blends thereof. 3. The adhesive of claim 1 wherein aaid cross-linked polysiloxane ia formed by the cross-linking of a plurality of subordinate siloxaneβ. 4. The adhesive of claim 3 wherein aaid subordinate ailoxanaa are aryl and/or alkyl. 5. The adhesive of claim 3 wherein aaid polysiloxane ia formed by cross-linking with a resin. 6. The adhesive of claim 5 wherein aaid reain is MQ organopolysiloxane or a fluororesin. 7. The adhesive of claim 1 wherein said polysiloxane is cross-linked by a catalyst further including a peroxide. θ. The adhesive of claim 7 wherein aaid peroxide ia ,2,4 dichlorobensoyl peroxide. 9. The adhaaive of claim , .1 wherein said cross-linked polysiloxane ranges from more than sero to leas than 100 per¬ cent of the total adhaaive composition. 10. The adhesive of claim 9 wherein aaid cross-linked polysiloxane ranges up to 10 percent. - 1 9 - 11. The method of preparing a fluid permeable adhesive which comprises the steps of (a) providing a cross-linked polysiloxane; and (b) blending said cross-linked polysiloxane with a non- silicone adhesive polymer. 12. The method of claim 11 wherein said adhesive polymer is an acrylic, a urethane, an elastomer, or a blend of the fore¬ going. 13. The method of administering fluids through the skin which comprises the steps of (a) applying a blend of a cross-linked polysiloxane adhesive and a non-ailicone pressure sensitive polymer in contact with an epidermal layer; and (b) applying fluid to said blend to permit passage there¬ through at a prescribed rate. 14. A fluid permeable adhesive as defined in claim 1 further comprising a medical device at least partially coated by said adhesive. 15. A fluid permeable adhesive as defined in claim 14 further including an epidermal layer adhered to said medical device by said adhesive. . 16. A method as defined in claim 10 wherein the ratio of said croβs-linked polysiloxane to said adhesive polymer determines the vapor transmission therethrough. 17. The method as defined in claim 16 wherein the vapor transmission through said adhesive increases as said polysiloxane is added until it reaches a first maximum and thereafter decreases for further polysiloxane additions. -20- 18. The method as defined in claim 16 wherein the vapor transmission through said adhesive increases and decreases in sawtooth fashion as the ratio of polysiloxane to said polymer iacreases. 19. The method of claim 16 wherein said croβs-linked polysiloxane is up to 10 percent of said adhesive polymer. 20. The method of claim 16 wherein said croβs-linked polysiloxane is up to 30 percent of the adhesive polymer.

Inventors: CIUCHTA CHERYL, CONSTANTINE DAVID, LOFTUS TIMOTHY, PENNACE JOHN R, CIUCHTA, CHERYL, CONSTANTINE, DAVID, LOFTUS, TIMOTHY, PENNACE, JOHN, R.
Applicants: FLEXCON CO INC, FLEXCON COMPANY, INC.
Application year: 1985
Main classification: A61K9
IPC codes: A61K9, A61L15