A METHOD FOR REMOVING RESIN FROM A PAPER PULP PROCESS LIQUOR

Abstract: The present invention relates to a method for cleansing resin-contaminated liquors in paper-pulp manufacturing processes, in which method there is added to a resin-con­ taminated liquor a floc-promoting metal salt, such as alumi­ nium sulphate, in at least a stoichiometric quantity against ingoing resin, therewith to flocculate the resins present, whereafter there is added an alkali to obtain a pH of 5-6. Subsequent hereto, there is optionally added a flocculating agent in the form of an organic polyelectrolyte. The resultant flocs are then isolated and, optionally after being dewatered to elevate the dry solids content, are reacted with an inor­ ganic acid, such as sulphuric acid, at pH 1-2 and cleaved at a temperature of at least 70° C, whereafter the resultant cleaved resin product is isolated per se and the resultant solution containing cleaved metal salts, such as an alumi­ nium sulphate solution, is isolated per se and, optionally, is then re-cycled or re-used as a flocculating agent. The resul­ tant resin product can be burned as a fuel and/or further refined.

Description: A METHOD IN THE MANUFACTURE OF PAPER PULP Description Technical Field The present invention relates to a method for cleansing resin-contaminated cooking and bleaching liquors in paper-pulp manufacturing processes. The object of the present invention is to provide a method of enabling resin to be removed effectively from the resin-contaminated liquors (aqueous liquors) in paper-pulp manufacturing processes, such as to enable, the quality of the pulp produced to be improved; the energy content of the waste resin to be recovered; emission levels to be reduced, both qualitatively and quantitatively; chip-storage quantities to be reduced; a reduction in the amount of auxiliary material required (e.g. bleaching agent); a reduction in the extent to which resin need be oxidized upon maturing of the pulp; and a reduction in the amount of water required. By reduction in chip-storage is mainly meant a reduction in storage time due to the fact that no attention needs to be paid to the ingoing resin qualities. BacoundAK The paper pulp and waste liquor produced in wood pulping processes contains large quantities of resins deriving from the wood used. These resins must be removed prior to bleaching the pulp, since otherwise they will discolour the pulp. In general practice, these resins are kneaded from the pulp together with waste liquor, in a pulper located upstream of the bleaching department. The resins may also be precipitated from the pulp suspension in colloidal form, by lowering the pH of the suspension. Such colloids are difficult to isolate, however. The removal of resins by flocculation with the aid of polyelectrolytes has also been proposed. This method has also proven to be unsatisfactory and uneconomic, however. Methods for removing resin from resin-contaminated waste liquor with the aid of aluminium sulphate have also been found uneconomical, due to the cost of the aluminium sulphate and also of the auxiliary flocculating agents, when such agents are used. Disclosure of the Invention It has now surprisingly been found possible to deresinate resin-contaminated liquors in a rational and effective manner by means of a method according to the invention, which provides by resinating the waste liquor a resin concentrate which can be subsequently used as fuel and therewith provide energy; which drastically reduces the amount of fresh water and bleaching material required; which shortens the time taken for raw pulp to mature; and which minimizes the load on the recipient. The invention is characterized by the steps of charging to the resin-contaminated liquor a) a floc-forming metal salt in at least stoichiometric quantities, therewith to flocculate the resins present; b) an acid or an alkali, such as to adjust the pH to 54; c) optionally an auxiliary flocculating agent in the form of an organic polyelectrolyte; and further comprising the steps of isolating the resultant flocs; optionally dewatering the flocs to elevate the dry substance content; adding to the flocs a strong inorganic cleaving acid to pH 1-2; cleaving said product at a temperature of at least about IOOC, to obtain a cleaved resin product and a solution containing cleaved metal sulphate; isolating the cleaved resin product per se and the solution containing said cleaved metal sulphate per se; and optionally recycling the metallic salt solution. Further features characteristic of the invention are set forth in the associated claims. By floc-forming metal salts is meant here and in the following essentially trivalent metal salts capable of forming metalhydroxide flocs in water. Such salts substatially comprise aluminium sulphate, aluminium chloride, aluminium nitrate, iron (m) chloride, iron (III) sulphate, iron (uni) chloride sulphate, or basic polynucleate complexes of aluminium hydroxide or iron hydroxide with preferably sulphate anions. The present invention will now be described in more detail with reference to an applicable working example and to the accompanying drawings, in which Figure 1 is a flow sheet illustrating schematically a sulphite mill incorporating a deresination system; Figure 2 is a flow sheet illustrating schematically an existing deresination system; and Figure 3 is a flow sheet illustrating schematically a deresination process according to the invention. Figure 1 is a schematic illustration of a sulphite plant. Pulp wood is debarked in a barking drum A, chipped in a chipper B and the chips transferred to a digester C, in which the chips are treated with cooking liquor. The resultant pulp is washed, together with cooking liquor, in a washer D, whereafter the cooking liquor is evaporated off and reconditioned, and the pulp is screened in a bull screen E and a fine screen F. The pulp is normally then treated in a deresination stage incorporating a filter G, and is then dewatered in a press H, whereafter the pulp is passed to a frotapulper I to which alkali is supplied for freeing the fibres of the pulp therein. The pulp is then transferred to a tower J, in which the pulp is alkalized terminally, to a pH of about 11, whereupon any resins present are saponified. The pulp is then passed to two wash filters K, where the pulp is washed in counter-flow with fresh water, and the resultant resin-contaminated washing liquor is passed to the recovery system of the plant. The pulp is then passed to a bleaching department in which the pulp is bleached in several stages, with chlorine, chlorine dioxide, hypochlorite or oxygen. Subsequent to being bleached, the pulp is again screened and then transferred to and dried on a dryer, before being cut and baled. Figure 2 illustrates in more detail a deresination system with subsequent bleaching department according to Figure 1, in which pulp arrriving from a digester is introduced into a diffuser Al in which the pulp, which has a low pH, meets washing liquid deriving from a subsequent stage. The liquid exiting from the diffuser Al has a pH = 2.2 and is evaporated, while the pulp is passed through a screen B1 to a wash filter C1, where the pulp is washed with washing liquor from a subsequent washing stage. The pH in this first washing stage is 6.5 and the temperature 4500. The pulp is then transferred to a centrifuge D1 (Suder), in which liquid is eliminated, this liquid being passed to the diffusers. Subsequent to being centrifuged, the pulp is supplied with sodium hydroxide and treated in a frotapulper El. The pulp is then passed to a tower F1, in which the pulp is again treated with sodium hydroxide to pH 10, whereupon resins dissolve and are washed out in a subsequent, second washing stage on a filter G1, using herefor a washing liquid of pH 8 obtained from a subsequent third washing stage. The washing liquid from the second washing stage is transferred to the first washing stage, in accordance with the above. Subsequent to passing through the second washing stage, the pulp is treated in a third washing stage on a filter Hl, on which it is washed with incoming fresh water. The resins are separated from the pulp in the washing stages as a result of the high pH levels prevailing therein. A large part of the resins, however, re-precipitate in the diffuser, due to the low pH levels therein. This resin content is taken up by the pulp downstream of the frota-pulper, in quantities of from 4 to 8 girl; resin deposits on the apparatus used and discolouring resin-flocs in the pulp can be readily observed at resin concentrations as low as 6 g/l. Figure 3 illustrates a process according to the invention. In this process, resin containing water obtained from a pulpwashing stage is fed to an inlet tank 1. The pulp is then transferred to the flotation tank 2. During its passage to the tank 2, the pulp is supplied with A12 (SO4)3 and an alkali to pH 54 (normally NaOH) and an auxiliary flocculating agent in the form of an organic polyelectro lyte, such as a polyelectrolyte of the polyacrylamide and/or polyethylene-oxide type. Flocs comprising aluminium hydroxide and auxiliary flocculating agent are formed in the floatation tank and bind thereto resins present in the pulp. The flocs are floated-off, whereupon there is obtained firstly clean water, which can be used for washing pulp, and secondly slime, having a dry solids content of about 10%, this slime being transferred to a slime tank 3 and from there to thickening centrifuge 4, in which there is obtained a filtrate and a slime having a dry solids content of about 25%. This slime is transferred to a cleaving reactor 5, in which the pH is lowered to 1-2, by adding sulphuric acid, and the temperature is raised to 70 C. The resultant flocs are therewith cleaved into a resin product and an aluminium-sulphate product. These cleaved products are then transferred to a cleaving centrifuge, in which a resin concentrate and an aluminum-sulphate solution are obtained, this solution being returned to the flow of water from the inlet tank. An experiment carried out with sulphite pulp, which contained 16.6 kg resin per ton of pulp and from which 80% of the resin originally present had been 3 removed, gave the following data: the ingoing washing liquid, volume 8.3 m contained 130 g Al and 16.6 kg resin. To this volume there was added aluminium sulphate in an amount corresponding to 900g Al, 4-6 kg NaOH and polymer 28g. The resultant pH was 5.0-5.5. The subsequent flotation resulted in 7.8 m3 of clean water containing 40g Al and 3.4 kg resin. The slime phase, volume 0.5 m3 having a dry solids content of 10%, contained 990g Al and 13.2 kg resin. When thickening the slime in the thickening centrifuge there was obtained 0.3 3 m of filtrate containing 1.0g Al and 0.1 kg resin. The thickened slime phase, volume 0.2 m3 having a dry solids content of 25%, contained 989g Al and 13.1 kg resin. Less than 4 kg H2 SO4 were charged to the cleaving reactor, to lower the pH to 1-2. Treatment in the cleaving centrifuge resulted in a resin concentrate of volume 0.07 m3 having an organic dry solids content of 90%, this solids content comprising 13 kg resin and 382g Al. The A12(S04)3 solution, 3 volume 0.13 m, obtained in the cleaving centrifuge contained 607g Al and 0.1 kg resin. Prior to being introduced into the washing liquid downstream of the inlet tank, the aluminium sulphate solution was supplemented with 3.2 kg BOLIDEN (@ ALG (293g Al), there being obtained an aluminium input of 900 grams. The resin concentrate obtained can be burned as fuel, to recover its energy content, or returned to the pine-oil cooker, and there further refined. As described above, the aluminium sulphate from the cleaving centrifuge can either be re-cycled or used as a paper size, in the case of an integrated paper mill, or used to produce clean water, or to clean other water in or adjacent a paper pulp mill.

Claims: CLAIMS 1. A method of cleansing resin-contaminated liquors in a paper pulp process, characterized by the steps of adding to said resin-contaminated liquors a) a floc-forming metal salt in an amount at least equal to the stoichiometric amount of resin, thereby to precipitate and flocculate the resins present; b) an alkali or an acid so as to obtain a pH of 4-6; c) optionally an auxiliary flocculating agent in the form of organic polyelectrolyte; by isolating the resultant flocculated product, optionally after dewatering the same so as to elevate the dry solids content thereof; adding to said product a strong inorganic cleaving acid, to obtain a pH of 2 or therebeneath; cleaving said product at a temperature of at least 70 0C, to obtain a cleaved resin product and cleaved metal sulphate in solution; isolating the cleaved resin product per se and the solution containing said cleaved metal sulphate per se; and optionally re-cycling said solution. 2 A method according to Claim 1, characterized by adding an auxiliary flocculating agent subsequent to adding a) metal salt solution and b) an alkali or acid, in that order. 3. A method according to Claim 1, characterized by concentrating the flocculated resin from a dry solids content of 5-10% to at least 25%, by devatering the flocs in a thickening centrifuge. 4. A method according to Claim 1, characterized by adding an alkali or acid to obtain a pH of 54. 5. A method according to Claim 1, characterized by adding a strong inorganic acid to obtain a pH of 1-2. 6. A method according to Claim 1, characterized in that respective cleavage products are each isolated per se in a cleaving centrifuge to a dry solids content of 85% with respect to the cleaved resin product, the separation between respective cleaved products being effected so that at least 50% of the ingoing Me is found in the isolated solution containing the cleaved metal salts. 7. A method according to Claim 1-6, characterized in that the floc-forming metal salt used is aluminium sulphate, and in that the cleaving acid is sulphuric acid. 8. A method according to Claims 1-6, characterized in that the floc-forming metal salt is an iron salt, such as ferri chloride, ferri sulphate, ferri chloride sulphate, and in that the cleaving acid is sulphuric acid and/or hydrochloric adic. 9. A method according to Claims 1-6, characterized in that the floc-forming metal salt is aluminium chloride, and in that the cleaving acid is hydrochloric acid.

Inventors: ENGSTROM, BENGT THOMAS, Engström, Bengt Thomas
Applicants: BOLIDEN AKTIEBOLAG
Application year: 1985
Main classification: D21C11
IPC codes: D21C9, C02F9, D21C11, C02F1