POLYFUNCTIONAL STYRYLOXY COMPOUNDS AND METHOD OF FORMING A CROSS-LINKED POLYMER

Abstract: Polyfunctional cationically polymerizable styryloxy com­ pounds of the formula where R¹ and R² are H, or one of R¹ and R² are H and the other is methyl; R³ and R⁴ are H, lower alkyl, or alkoxy if R² is not methyl; R⁵ is a divalent hydrocarbon radical; G is any multivalent organic or inorganic radical free of amino, aliphatic hydroxyl, aliphatic thiol or other groups which interfere with cationic polymerization; and n is an integer of two or more.

Description: Field of the Invention It is an object of the present invention to provide a new class of polymerizable monomers which are polyfunctional, so as to be cured to cross-linked high molecular weight polymer networks, and which are readily cationically polymerizable. Background of the Invention In USSR Patents 443874 and 478026 there are described ion exchange polymers prepared by free radical copolymerization of styrene or maleic anhydride, respectively, with p-glycidoxy-α-methyl stryrene (Ia) United States Patent No. 3327019 (Mylenbusch) discloses diethers of formula (Ib) where R₁, R₂ and R₃, which may be the same or different, represent hydrogen or alkyl with up to 4 carbon atoms, cycloalkyl or phenyl; R₄ and R₅, which may be the same or different, represent hydrogen or methyl; R₆ represents a radical with n substitutable positions on aromatic nuclei; and n is a whole number greater than zero. The diethers of formula (Ib) may be produced as reaction products of p-glycidoxy styrenes and polyols. All of the diethers of formula (Ib) will contain aliphatic hydroxyl groups and it is stated at column 5, lines 3 to 8 that, on the basis of these reactive aliphatic hydroxyl groups as well as the double bonds, these compounds are intermediates of wide applicability, for example for the production of plasticizers and of polymerizable esters and polyethers. At col.5, lines 59-63 polymerisation by light and energy rich rays, or according to the cationic mechanism with corresponding catalysts, in known manner, is indicated. However, the presence of these aliphatic hydroxyl groups and the manner in which the diethers are prepared will result in compounds which would not be cationically active, i.e. cationic polymerization would take place only very slowly or not at all. In Macromolecules, 16 , 510-517(1983), there is described the cationic polymerization of p-methoxy and p-(ethoxymethoxy)-α-methyl styrenes with boron trifluoride etherate as initiator in dichloromethane. These polymers are then subjected to ether cleavage reactions to yield linear polymers containing pendant phenolic groups. It is known from kinetic studies of the cationic polymerization of p-methoxy styrene that this monomer has a very high rate of polymerization. See, e.g., Macromolecules, 9 , 931-936(1976); and Polymer, 16 , 819-826(1975). United States Patent No. 2488501 (Moyle) discloses as a general class 1,4-di (alkenylphenoxy) -2-butenes the compounds being said to have utility as constituents of insecticide compositions and as modifiers in plastic compositions, of col.3, lines 48-50 and the compound 1,4-di (4-propenylphenoxy) -2-butene is specifically mentioned. There is no mention in this patent of polymerization of the compounds and certainly no suggestion that they are cationically polymerizable . United States Patent No. 3663625 (Neville) discloses bis[1-alkyl (and aryl)vinyl] para- phenylene oxide monomers of the formula (Ic). where Ar is a homocyclic aromatic structure selected from: and R is C₁₋₅ straight chain alkyl, biphenyl, naphthyl or C₁₋₅ fluroalkyl; R¹ is H or C₁₋₅ straight chain alkyl; n is 1 to 6. It is an essential feature of the monomers of US Patent 3363625 that they are substituted on the carbon atom adjacent to the group Ar (i.e. R cannot be hydrogen). It is stated that the monomers can be polymerized by means of free radical catalysts or Lewis acid catalysts; as such are mentioned metal halides typified stannic chloride, aluminium chloride, ferric chloride, phosphorus chloride, boron trifluoride, of col.3, lines 1 to 7. However, the object is to achieve polymers having long chains linked by indanyl structures and low cross-link density. There is no suggestion of cationic addition polymerization. Chemical Abstracts 63 9968 c-d (1965), relating to JP-A-8552('65), discloses piperazine derivatives stated to be useful as analgesics and antipyretics and having the structure (Id) where R is methoxy or ethoxy and R' is methyl, ethyl, propyl, allyl or propenyl. There is no disclosure of any polymerization properties of the compounds and, in particular, no suggestion of cationic addition polymerization. The invention concerns the subject matter as defined in the claims. According to one aspect the invention provides a method of forming a cross-linked solid polymer characterized in that a compound having the formula (II) or (III): or wherein R¹ and R² are H, or one of R¹ and R² is H and the other is methyl; R³ and R⁴ are H, lower alkyl, or alkoxy if R² is not methyl; R⁵ is a divalent hydrocarbon radical; G is a multivalent organic or inorganic radical free of amino, aliphatic hydroxyl, aliphatic thiol or other groups which interfere with cationic polymerization; and n is an integer of 2 or more; is polymerized by addition polymerization with a cationic polymerization initiator. In addition to high reactivity to cationic polymerizations, the monomers defined above have been shown to develop an intense coloration when they are polymerized by UV irradiation in the presence of acid generating photoinitiators. Under some circumstances this coloration is sufficient to mask a substrate, providing a useful means of generating opacity in photocurable coatings. This coloration is also observed in chemically initiated cationic polymerizations of these materials. An additional feature of solid polyfunctional styryloxy resins of the invention is an ability of these resins to cure by UV irradiation without added photoinitiator. This cure is believed to involve a radical mechanism. Accordingly this aspect of the invention also provides a method for providing a colored cross-linked coating on a substrate, which method comprises coating the substrate with a composition comprising a compound of formula (II) or (III), and polymerizing the composition by addition polymerization with a cationic polymerization initiator. The cationic polymerization initiator may be a cationic photoinitiator with the compound of formula (II) or (III) being polymerized by irradiation with UV radiation. According to another aspect the invention provides polyfunctional cationically polymerizable styryloxy compounds of the formula (III). wherein R¹ is H, and R² is H or methyl; R³ and R⁴ are H, lower alkyl, or alkoxy if R² is not methyl; R⁵ is a divalent hydrocarbon radical; G is a multivalent organic or inorganic radical free of amino, aliphatic hydroxyl, aliphatic thiol, or other groups which interfere with cationic polymerization; and n is an integer of two or more, excluding 1,4-di (4 - propenylphenoxy) -2-butene. According to a further aspect the invention provides polyfunctional cationically polymerizable styryloxy compounds of the formula (III) wherein R¹ and R² are H, or one of R¹ and R² is H and the other is methyl; R³ and R⁴ are H, lower alkyl, or alkoxy if R² is not methyl; R⁵ is a divalent hydrocarbon radical; G comprises an organopolysiloxane backbone free of amino, aliphatic thiol, or other groups which interfere with cationic polymerisation; and n is an integer of two or more. Detailed Description of the Invention The monomers defined above may readilly be prepared from p-vinyl phenols, p-propenyl phenols or p-isopropenyl phenols by a variety of methods such as etherification with an appropriate multifunctional etherifying agent, or reaction with multifunctional epoxies followed by reaction of the resulting aliphatic hydroxyl with a polyisocyanate or other suitable capping agent. According to one aspect the monomers of formula (III) are addition reaction products of a compound of the formula (IV) with a polyisocyanate resin. According to another aspect the monomers of formula (III) are etherification reaction products of a compound of the formula (V) with a compound of the formula (XR⁵) n G where X is halogen. According to a further aspect the monomers of fomula (III) are transesterification reaction products of a compound of the formula (VI) where R⁷ is alkyl or substituted alkyl with a compound having a plurality of hydroxyl groups. A suitable p-vinyl phenol is the commercially available vinyl guaiacol (2-methoxy-4-vinyl phenol). Synthetic methods for obtaining other suitable phenols include those reported in U.S. Patent 3,327,019, column 3, line 38 - column 4, line 2; Japanese Kokai Tokkyo Koho 79:55,529 (dehydrogenation of ethyl phenol to give vinyl phenol); J. Kahovec, et al., J. Collect. Czech. Chem. Commun., 36 , 1986 (1971) (various α-methylvinyl phenols); and Macromolecules, 16 510-517 (1983) (p-hydroxy-α-methyl styrene by cleavage of 2,2-bis(p-hydroxyphenyl)-propane). Yet another synthetic procedure involves the modification of the procedure of Macromolecules, 16 , 510-517 (1983), in which p-(ethoxymethoxy)-α-methyl styrene is prepared from p-hydroxyacetophenone by etherifying the hydroxyl group and then using a Wittig reaction on the resulting p-(ethoxymethoxy) acetophenone. One modification required for the synthesis of the inventive monomers is the initial reaction of p-hydroxyacetophenone with an appropriate polyfunctional etherification reagent to form a molecule having multi-acetophenone functionalities. Subjecting such a molecule to a Wittig reaction as in the Macromolecules reference will yield a polyfunctional monomer of the invention. An alternative modification of the Wittig reaction procedure is to use a monofunctional etherification reagent which is capable of entering into subsequent chain extension reactions with polyfunctional moieties. An example is etherification of p-hydroxyacetophenone with allyl bromide, Wittig reaction to give the corresponding allyloxy styrene and hydrosilation using a silicone resin with poly Si-H functionality. In formulae(II) and (III) above, it is generally preferred that R³ is H, methyl, or methoxy and R⁴ is H. However, other lower alkyl or alkoxy (up to C₄) may be included as substituents R³ and/or R⁴). In formula (II) and (III) above, it is particularly preferred that R¹ and R² are both H or that R¹ is CH₃ and R² is H. In formula (II) and (III) above, it is also particularly preferred that R² and R⁴ are both H and R³ is methoxy. Examples of R⁵ groups are methylene, ethylene or cycloaliphatic, aromatic hydrocarbons such as 1,4-di-methylenebenzene or unsaturated linear hydrocarbons such as propenylene or butenylene. The only limitation on G is that it must not interfere with cationic polymerization of the styryloxy groups. G must not include any strongly electron withdrawing group in conjugation with the styryloxy group oxygen atom as such groups will interfere with vinyl cationic polymerizations. Amines, aliphatic hydroxyls, and aliphatic thiols are known to prevent or slow vinyl cationic polymerizations. "Developments in Polymerization -1," R.N. Haward ed., Applied Science Publishers, 1979, pg. 80. Inclusion of these groups in G should therefore also be avoided. One preferred group of compounds according to formula (III) are those in which G comprises a polyorganosiloxane backbone. Addition polymerization of the inventive monomers may be accomplished by conventional acid and Lewis acid cationic initiators such as methane sulfonic acid, toluene sulfonic acid and boron trifluoride etherate. UV cationic initiators may also be used. Such UV cationic photoinitiators include salts of a complex halogenide having the formula: where A is a cation selected from the group consisting of iodonium, sulfonium, pyrylium, thiopyrylium and diazonium cations, M is a metalloid, and X is a halogen radical, d equals e minus f, f equals the valance of M and is an integer equal to from 2 to 7 inclusive, e is greater than f and is an integer having a value up to 8. Examples include di-p-tolyl iodonium hexafluorophosphate, diphenyl iodonium hexafluorophosphate, diphenyl iodonium hexafluoroarsenate and UVE 1014 (trademark of General Electric), a commercially available sulfonium salt of a complex halogenide. Certain monomers, usually solids, will also undergo UV initiated polymerization in the solid state without initiator, yielding an essentially uncolored product. A radical mechanism is believed to be involved. This UV, initiator free, polymerization has also been obtained with a liquid silicone backbone resin of the invention. The production of colored reaction mixtures by cationic initiators has been reported before for styryloxy monomers. Permanent coloration in the cured products of the invention is believed to result from particular termination reactions involving stable carbocations. The development of color can thus be controlled by selecting polymerization conditions designed to select for or against termination by stable carbocations. The development of permanent color as a result of polymerization termination reactions is especially advantageous at certain UV cured opaque coating applications where the use of pigments or dyes in the composition blocks UV, resulting in only surface cure of the coating. Since the inventive resins develop their intense coloration only after initiation of polymerization, initation by UV is not interfered with. The invention may be illustrated by reference to the following nonlimiting examples: EXAMPLE 1 To a mixture of 3.0 grams vinyl guaiacol, 27.0 grams ethanol, 30 grams acetone and 20 grams potassium carbonate stirred in a round-bottom flask was added, dropwise over 30 minutes, a solution of 2.8 grams α, α'-dibromo-p-xylene in 30 grams acetone. The resulting mixture was stirred at room temperature for 24 hours. The potassium carbonate was then filtered off and the solvent removed under reduced pressure. The residue was redissolved in chloroform (250 ml) and extracted with distilled water (3 x 100 ml). The chloroform layer was then dried over sodium sulfate and filtered. Solvent was removed under reduced pressure and the residue was recrystallized from hot ethanol to yield 2.01 grams slightly yellow crystals. This material was identified from proton NMR (CDCl₃; δ =3.87, singlet, methoxy protons; δ =5.05,5.22.5.45 and 5.74 quartet, β-vinyl protons; δ =5.12, singlet, benzyl protons; δ = 6.44 - 7.2 multiplet, α-vinyl and guaiacol ring protons; δ =7.45, singlet, xylene ring protons) and IR (3085cm⁻¹: vinyl C-H; 3010cm⁻¹: aryl-H; 2860cm⁻¹: methoxy C-H; 1625cm⁻¹ conjugated c=c; 1140cm⁻¹: aromatic-O; 1030cm⁻¹: alkyl C-O-aromatic; 995 and 900cm⁻¹: R-CH=CH₂; 860cm⁻¹: 2 adjacent aromatic C-H) spectra as α,α'-bis(2-methoxy-4-vinylphenoxy)-p-xylene. EXAMPLE 2 A mixture of 5.0 grams vinyl guaiacol, 3.47 grams allyl glycidyl ether, 45 grams ethanol, 0.68 grams of a commercially available ion exchange resin (Rohm and Haas Amberlyst A-27) and 0.80 grams benzyl trimethyl ammonium hydroxide was heated for 65 hours at reflux. The mixture was then filtered and solvent was removed under reduced pressure. The residue was chromatographed on a silica gel column using chloroform as the eluent, yielding 6.8 grams of a slightly orange viscous material which was identified by proton NMR and IR spectra as the adduct of vinyl guaiacol and allyl glycidyl ether. A mixture of this adduct (2.64 grams), a commercially available polyfunctional isocyanate resin (Bayer Desmodur L-75) (2.92 grams), 0.06 grams stannous octoate, and 20 grams chloroform was heated at reflux for 90 minutes under nitrogen. At the end of this time infrared analysis indicated that all of the isocyanate groups had been consumed. After solvent was evaporated, the crude product was washed in a soxhlet extractor and dried in a vacuum desiccator to yield 2.44 grams of product. This product was shown by liquid chromatography, NMR and IR spectroscopy to be a high molecular weight resin containing styryloxy functional groups. EXAMPLE 3 A solution of 0.120 grams of the α,α'-bis(2-methoxy-4-vinylphenoxy)-p-xylene prepared in Example 1 and 0.010 grams of a commercially available cationic sulfonium salt photoinitiator (GE UVE-1014) in 1.000 gram chloroform was coated onto a glass slide and the solvent allowed to evaporate. The coating was then irradiated under a medium-pressure mercury lamp at an intensity of 70 mw/cm² for 20 seconds, producing a tack-free brittle film with an intense purple coloration. The irradiated film was effective at obscuring the contrast on a Morest chart #05. The irradiated material was insoluble in common organic solvents. EXAMPLE 4 A solution of 0.100 grams of the styryloxy resin prepared in Example 2 and 0.006 grams of ditolyliodonium hexafluorophosphate in 0.100 grams of anisole was coated onto a glass slide and irradiated under a medium-pressure mercury lamp at an intensity of 60mw/cm² for 5 seconds. The film was tack free after irradiation and insoluble in common organic solvents. EXAMPLE 5 A dilute solution of the α,α'-bis(2-methoxy-4-vinylphenoxy)-p-xylene synthesized in Example 1 was prepared by dissolving 0.4022 grams of this material in 50 milliliters of dry dichloromethane. To this solution was added, with stirring, 10 milliliters of a solution prepared by dissolving 0.0574 grams of triphenylcarbenium hexachloroantimonate in 100 milliliters of dry dichloromethane. The reaction mixture developed a red color rapidly and was stirred for three hours at room temperature. The mixture was then added to 50 milliliters of methanol to quench the reaction. Solvents were removed under reduced pressure yielding 0.395 grams of a pink solid polymer. The polymer was dissolved in hot dichloromethane and absolute alcohol was added gradually. On cooling a white precipitate formed. Solvents were removed under reduced pressure yielding 0.352 grams of material. This material was dissolved in tetrahydrofuran and analyzed on a Waters Model 244 Liquid Chromatograph fitted with one 1000 angstrom and two 100 angstrom columns. The material was found to be a high polymer with a peak molecular weight corresponding to 6,500 on a polystyrene calibration. EXAMPLE 6 To a mixture of 20 grams vinyl guaiacol, 180 grams ethanol, 300 grams acetone and 65.6 grams potassium carbonate was added dropwise over 20 minutes 22.27 grams of ethyl bromoacetate. The color of the mixture changed gradually from green to light brown. The mixture was heated at 45°C for two hours, then cooled to room temperature and left for a further sixteen hours. Thin-layer chromatography on a sample of the reaction mixture showed the presence of vinyl guaiacol after this time. Consequently, the mixture was heated to reflux for 7 hours and left at room temperature for a further 64 hours. The mixture was then filtered and solvents were removed under vacuum. then 350 grams of solvent had been removed, a precipitate formed in the mixture. The precipitate (3.84g.) was removed by filtration. The remaining material was distilled into three fractions and a residue (4.32g, 4.91g, 1.48g, and 11g respectively). Gas-liquid chromatographic analysis of the second fraction showed that it consisted principally (85%) of the adduct of ethyl bromoacetate and vinyl guaiacol, 3-methoxy-4-(2-oxo-2-ethoxy)-ethoxy styrene. The adduct was characterized by NMR (CDCl₃; δ =1.27, triplet, ester methyl protons; δ =3.91, singlet, methoxy protons; δ =4.3, quartet, ester methylene protons; δ =4.72, singlet, ether methylene protons; δ =5.1,5.3,5.5, and 5.8, quartet, β-vinyl protons; δ =6.5-7.1, multiplet, α-vinyl and ring protons). The remainder of the second fraction (15%) consisted of vinyl guaiacol. Material from the second fraction (4.0 grams), 1,6-hexanediol (1.0 gram) and lithium ethylene glycolate (0.05 gram) were refluxed in dry heptane for 3 hours. The heptane was removed by distillation to yield 4.73 grams of product. The product was analyzed by liquid chromatography and shown to consist of approximately equal portions of unreacted 3-methoxy-4-(2-oxo-2-ethoxy)-ethoxy styrene (MOES), the monofunctional product of the transesterification of MOES and 1,6-hexanediol, and the difunctional product of the transesterification of MOES and 1,6-hexanediol. A concentrated solution of this product mixture was prepared by dissolving 0.45 grams of the material in 0.65 grams dry dichloromethane. When one drop of methanesulfonic acid was added to the solution the material polymerized instantly to give a red, insoluble product. EXAMPLE 7 To a solution of 136g 4-hydroxyacetophenone in 500 mls acetone was added 276.41g potassium carbonate. This mixture was stirred for 15 minutes. A solution of 133g allyl bromide in 200 mls acetone was then added dropwise over 45 minutes, and the resulting mixture was stirred for a further 4 hours and left standing for a further 16 hours. Thin-layer chromatography showed some starting material to be present at the end of this time. The mixture was then heated to reflux for 4 hours and left standing a further 16 hours. After filtration the solvent was removed by distillation leaving 230g of a brown liquid. This residue was distilled under reduced pressure (B.Pt. 107-115°C at 0.6mmHg.) to yield 158g of pale yellow liquid which was identified by infrared and n.m.r. spectroscopy as 4-allyloxyacetophenone. To a solution of 5.58g potassium metal in tert-butanol was added 51g methyl triphenylphosphonium bromide. The resulting yellow suspension was stirred for 20 minutes. A solution of 18.86g 4-allyloxyacetophenone in 30 mls tert-butanol was then added gradually and stirred for 16 hours at room temperature. After this time, the mixture was filtered and solvent removed under reduced pressure. The resulting mixture was extracted with petroleum ether to yield 28g of brown resin. This resin was distilled under reduced pressure (B.Pt. 88°C at 1mm Hg) yielding 15.21g of a clear colorless liquid which was identified by infrared and n.m.r. spectroscopy as 4-allyloxy isopropenyl benzene (Proton NMR: (CDCl₃) δ =2.12 singlet, α-methyl protons; δ =4.50, 4.58, doublet, allyloxy methylene protons; δ =5.0-6.5, multiplets, allyl and vinyl group protons; δ =6.80, 6.95, 7.35 and 7.50, quartet, aromatic protons). A solution of 13.92g 4-allyloxy isopropenyl benzene in 50.0g toluene was stirred for 5 minutes at room temperature. To this solution was added 0.693g of a 2% solution of dihydrogen hexachloroplatinate hexahydrate in n-butyl acetate. The resulting solution was then heated to 80°C and 40.40g of a difunctional Si-H terminated polydimethylsiloxane resin of molecular weight 1010 was added gradually over 90 minutes. At the end of that time infrared spectroscopy showed that the peak at 2130 cm⁻¹ had disappeared indicating complete consumption of the Si-H groups. Solvent was then removed under reduced pressure to yield 55.78g of a light brown low viscosity liquid. Reaction of 1 gram of this product with 0.02 grams methanesulfonic acid led to rapid formation of a rubbery gel insoluble in common organic solvents. EXAMPLE 8 A mixture of 20.0g 4-hydroxy-3-methoxy styrene, 27.5g potassium carbonate and 180 grams ethanol was heated to 40°C and 17.7g allyl bromide added gradually as a 50% solution in ethanol. The mixture was stirred for two hours at 55-65°C. The solids were then filtered and solvent removed under reduced pressure. The remaining liquid was then distilled under reduced pressure (B.Pt. 96-108°C at 0.2mmHg) to yield 13.2g of clear liquid identified by infrared and n.m.r. spectroscopy as 4-allyl-oxy-3-methoxystyrene (Proton NMR: (CDCl₃) δ =3.87, singlet, methoxy protons; δ =4.55, 4.62, doublet, allyloxy methylene protons; δ =5.05-7.1, multiplets, vinyl, allyl and aromatic protons. To a solution of 9.5g 4-allyloxy-3-methoxy styrene in 34.75g toluene was added 0.459g of a 2% solution of dihydrogen hexachloroplatinate hexahydrate in n-butyl acetate. The resulting solution was then heated to 80°C and 25.3g of a difunctional Si-H terminated polydimethylsiloxane resin of molecular weight 1010 was added gradually over 30 minutes. At the end of that time infrared spectroscopy showed that the peak at 2130 cm⁻¹ had disappeared indicating complete consumption of the Si-H groups. Solvent was then removed under reduced pressure to yield 32.97g of a clear colorless resin. Reaction of 0.5 gram of this product with 0.02 gram methane sulfonic acid led to rapid formation of a rubbery purple gel which was insoluble in common organic solvents. EXAMPLE 9 An aliquot of the difunctional styryloxy silicone resin synthesized in Example 2 was blended with 3% by weight of a commercially available triarylsulfonium salt photoinitiator (UVE-1014, trademark of General Electric). A drop of this formulation was placed on a glass slide and irradiated under a medium-pressure mercury lamp at an intensity of about 100mw/cm² at 365nm for 10 seconds. At the end of this time the formulation had completely cured to a rubbery tack-free film. Irradiation for 30 seconds led to formation of a purple rubbery tack-free film. EXAMPLE 10 To a solution of 122g 4-hydroxybenzaldehyde in 500 mls acetone was added 276g potassium carbonate. This mixture was stirred for 15 minutes. A solution of 133g allyl bromide in 200 mls acetone was then added dropwise over 30 minutes. The resulting mixture was heated at reflux for 1 hour, left standing for a further 16 hours and finally heated at reflux for 2 hours. After filtration, the solvent was removed by distillation leaving 175g of a reddish liquid. This residue was distilled under reduced pressure (B.Pt. 104-114°C at 1.5 mmHg) to yield 130g of a pale yellow liquid which was identified by infrared and n.m.r. spectroscopy as 4-allyloxybenzaldehyde. To a solution of 9.36g potassium metal in 500 mls tert-butanol was added 85.68g methyltriphenylphosphonium bromide. The resulting yellow suspension was stirred for 20 minutes and 32.4g 4-allyloxybenzaldehyde was then added over 10 minutes. This mixture was stirred for 30 minutes and then allowed to stand overnight. After filtration the solvent was removed under reduced pressure leaving 107g of a red semi-solid residue. Petroleum ether (B.Pt. 40-60°C) was added to the residue precipitating a solid which was filtered. After removal of the petroleum ether, the remaining resin was distilled under reduced pressure (B.Pt. 68-82°C at 0.4 mmHg) yielding 26.7g of a clear colorless liquid which was identified by infrared and n.m.r. spectroscopy as 4-allyloxystyrene (Proton NMR: (CDCl₃) δ =4.50, 4.58, doublet, allyloxymethylene protons; δ =5.0-6.5, multiplets, allyl and vinyl group protons; δ =6.80, 6.95, 7.30 and 7.45, quartet, aromatic protons). A solution of 8.0g 4-allyloxystyrene in 33.0g toluene was stirred for 5 minutes at room temperature. To this solution was added 0.414g of a 2% solution of dihydrogen hexachloroplatinate hexahydrate in n-butyl acetate. The resulting solution was then heated to 80°C and 25.25g of a difunctional Si-H terminated polydimethylsiloxane resin of molecular weight 1010 was added gradually over 4 hours. At the end of that time, infrared spectroscopy showed that the peak at 2130 cm⁻¹ had disappeared indicating complete consumption of the Si-H groups. Solvent was then removed under reduced pressure to yield 33g of a light brown low viscosity liquid. Reaction of 1 gram of this product with 0.02 grams methanesulfonic acid led to rapid formation of a rubbery gel insoluble in common organic solvents EXAMPLE 11 Example 3 was repeated except that no photoinitiator is used and the irradiation time was 1 minute. A slightly yellow film insoluble in chloroform and other common organic solvents was obtained. EXAMPLE 12 A mixture of 8.0g 4-allyloxystyrene in 26.57g toluene was stirred at room temperature for 5 minutes and 0.35g of a 2% solution of dihydrogen hexachloroplatinate hexahydrate in n-butyl acetate was added. The mixture was then heated to 80°C and 18.57g of a heptafunctional Si-H containing polydimethylsiloxane resin of molecular weight 2600 was added over 40 minutes. Solvent was then removed under reduced pressure to yield 26.76g of a slightly yellow viscous liquid. Reaction of 0.5 gram of this product with 0.02 gram methane sulfonic acid led to rapid formation of a reddish brown solid mass. EXAMPLE 13 An aliquot of the styryloxy silicone resin synthesized in Example 12 was blended with 3% by weight of a commercially available triarylsulfonium salt photoinitiator (UVE-1014, trademark of General Electric). A drop of this formulation was placed on a glass slide and irradiated under a medium-pressure mercury lamp at an intensity of about 100 mw/cm² at 365g for 30 seconds. At the end of this time the formulation had completely cured to a tack-free rubbery film. Irradiation for 70 seconds led to formation of a purple rubbery tack-free film.

Claims: A method of forming a cross-linked solid polymer characterized in that a compound having the formula (II) or (III): or wherein R¹ and R² are H, or one of R¹ and R² is H and the other is methyl; R³ and R⁴ are H, lower alkyl, or alkoxy if R² is not methyl; R⁵ is a divalent hydrocarbon radical; G is a multivalent organic or inorganic radical free of amino, aliphatic hydroxyl, aliphatic thiol or other groups which interfere with cationic polymerization; and n is an integer of 2 or more; is polymerized by addition polymerization with a cationic polymerization initiator. A method as claimed in Claim 1 in which R¹ and R² are both H or R¹ is CH₃ and R² is H. A method as claimed in Claim 1 in which R² and R⁴ are both H and R³ is methoxy. A method as claimed in any of Claims 1 to 3 wherein the compound of formula (III) comprises the addition reaction product of a compound of the formula (IV) with a polyisocyante resin. A method as claimed in any of Claims 1 to 3 wherein the compound of formula (III) comprises the etherification reaction product of a compound of the formula (V) with a compound of the formula (XR⁵) n G where X is halogen. A method as claimed in any of Claims 1 to 3 wherein the compound of formula (III) comprises the transesterification reaction product of a compound of the formula (VI) where R⁷ is alkyl or substituted alkyl with a compound having a plurality of hydroxyl groups. A method as claimed in any of Claims 1 to 3 wherein G in the compound of formula (III) comprises a polyorganosiloxane backbone. A method as claimed in any of Claims 1 to 7 for providing a colored cross-linked coating on a substrate, which method comprises coating the substrate with a composition comprising a compound of formula (II) or (III) and polymerizing the composition by addition polymerization with a cationic polymerization initiator. A method as claimed in any of Claims 1 to 8 wherein the cationic polymerization initiator is a cationic photoinitiator and the compound of formula (II) or (III) is polymerized by irradiation with UV radiation. A method as claimed in Claim 9 wherein the cationic photoinitiator is a salt of a complex halogenide having the formula where A is a cation selected from the group consisting of iodonium, sulfonium, thiopyrylium, pyrylium and diazonium cations, M is a metalloid, and X is a halogen radical, d equals e minus f, f equals the valence of M and is an integer equal to from 2-7 inclusive, e is greater than f and is an integer having a value up to 8. Polyfunctional cationically polymerizable styryloxy compounds of the formula (III) wherein R¹ is H, and R² is H or methyl; R³ and R⁴ are H, lower alkyl, or alkoxy if R² is not methyl; R⁵ is a divalent hydrocarbon radical; G is a multivalent organic or inorganic radical free of amino, aliphatic hydroxyl, aliphatic thiol, or other groups which interfere with cationic polymerization; and n is an integer of two or more, excluding 1,4-di (4-propenylphenoxy)-2-butene. A compound as claimed in Claim 11 in which R² and R⁴ are H and R³ is methoxy. A compound as claimed in Claim 11 or 12 which is the addition reaction product of a compound of the formula (IV) with a polyisocyanate resin. A compound as claimed in Claim 11 or 12 which is the etherification reaction product of a compound of the formula (V) with a compound of the formula (XR⁵) n G where X is halogen. A compound as claimed in Claim 11 or 12 comprising the transesterification reaction product of a compound of the formula (VI) where R⁷ is alkyl or substituted alkyl with a compound having a plurality of hydroxyl groups. A compound as claimed in Claims 11 or 12 wherein G comprises a polyorganosiloxane backbone. Polyfunctional cationically polymerizable styryloxy compounds of the formula (III) wherein R¹ and R² are H, or one of R¹ and R² is H and the other is methyl; R³ and R⁴ are H, lower alkyl, or alkoxy if R² is not methyl; R⁵ is a divalent hydrocarbon radical; G comprises an organopolysiloxane backbone free of amino, aliphatic thiol, or other groups which interfere with cationic polymerization; and n is an integer of two or more. A compound as in Claim 17 in which R¹ and R² are both H, or R¹ is CH₃ and R² is H. A compound as claimed in Claim 17 or 18 in which R² and R⁴ are H and R³ is methoxy.

Inventors: HARRIS, STEPHEN J., ROONEY, JOHN M., WOODS, JOHN
Applicants: LOCTITE (IRELAND) LTD.
Application year: 1985
Main classification: C07C43
IPC codes: C07C43, C08G77, C07C45, C08F12