METHODS OF PREPARING AND APPLYING SUBBING LAYERS FOR OPTICAL DATA DISKS

Abstract: This disclosure includes a description of how a relatively common magnetic recording (metal) disk may be smoothed and prepared for deposition of layers adapted for optical recording of digital data, useful in extended archival data storage; this being effected with certain "subbing" coatings, especially on an anodized aluminum disk surface - prepared and applied according to special techniques.

Description: TITLE METHODS OF PREPARING AND APPLYING SUBBING LAYERS FOR OPTICAL DATA DISKS This invention relates to optical recording of digital data on a rigid substrate and more particularly to smoothing layers for such substrates. BACKGROUND Improvements in high-speed digital magnetic media (e.g., disks, tapes) are increasingly difficult to obtain. A better high-speed, mass storage medium is needed, one more economical, compact, and archival. Optical disk recording is attractive because it allows instantaneous playback, very fast random access, high recording density (better than magnetic recording), and archival storage (e.g., for several years or longer under severe EDP environment). And a particularly promising technique employs an optical disk system that uses laser recording to store encoded information at very high data rates with extremely high density. -- Subbing, generally: Workers in this, and related, arts are familiar with the use of soothing (subbing) layers applied to metal disks to improve the smoothness thereof (e.g., see "Optical Disk Systems Emerge" by Bartolini, et al., IEEE Spectrum, August 1978, p. 26 et segu.). Aluxainum disks for use in digital data recording by optical means ("O.D. disks") are normally supplied with a surface that is too rough to be used for acceptable optical recording layers and thus typically require such a subbing layers te.g., see PIG. 1 and aluminum disk (d), with subbing (sb) on which some sort of optical recording structure ("OL"), is to be coated, with a certain overcoating, ("OC") on this). -#Such recording structures are known in the art (e.g., "tuned media using a wdark mirror" or optical tri-layer effect; for instance, see U.S. 4,222,071 to Bell, et al.; also see 1Review of Optical Storage Medias by Zech, SPIE Vol. 177, Optical Information Storage, 1979, page 56 et sequ.; also see 1Optical Recording Media Reviews by Bartolini, page 2 et seen. of 1977 SPIE Vol. 123, "Optical Storage Materials and Methods"; and see "Melting Holes in Metal Films for Real-Time, High Density Data Storage by Cochran and Ferrier, SPIE Proceedings, August 1977, pages 17-31; "Anti-Reflection Structures for Optical Recording" by Bell and Spong, Journal of Quantum Electronics, Vol. QE 14, No. #, July 1978; and for general prior art, see exemplary article: Optical Storage Materials and Methods", SPIE Proceedings, Vol. 177, Optical Information Storage, 1979, page 56; or see "Optical Properties of Tellurium Films Used for Data Recording by Ash and Allen, SPIE Proceedings, Vol. 222, 1980; Design and Production of Tellurium Optical Data Disks by Rancourt, SPIE Proceedings, No. 299, 1981). Provision of such a subbing layer that is smooth enough, and thick enough, to cover a disk' 8 rough surface (e.g., to yield optical digital readout with acceptable S/N) is an object of this disclosure. More particularly, it is an object hereof to teach fabrication of such media also satisfying other OD disk criteria, such as extended archival life (e.g., order of at least several years). A rough substrate, or inadequate subbing, can determine the quality (e.g., density, defect incidence, error rate) of such optical recording. For instance, the expected minimum bit-error-rate (BER) may be impossible to realize unless the subbing is sufficiently free of oil, fingerprints, dust and other contaminants and is sufficiently level and uniform, One feature hereof is to teach such subbing, and especially preferred formulations therefor. Conventional subbing is not adequate for these goals; for instance, some have proposed a polymer-in-solvent coating (suitable resin-in solvent vehicle) as a subbing formulation for related purposes; but these allow intrusion of far too much contaminant (e.g., moisture) and cannot give the desired archival life. A more particular feature is to teach the use of unique "radiation-cured" polymeric mixtures for such "subbing", preferably on relatively common "Winchester" disks (i.e., aluminum disks, of the kind regularly used in present magnetic digital recording). Such "radiation-curable" (R-C) coatings facilitate quick-curing, i.e., a smoothing layer that cures rapidly compared with other types of coatings (such as those based upon polymer deposition from a solvent solution). They require less cure-energy than solvent-based coatings and are less likely to retain solvents that can volatilize during the media deposition process later. The R-c coatings are preferably contprised of an acrylate pre-po-lyter {especially an acrylated epoxide) with suitable additives; e.g., for cross-linking, for control of cure and viscosity, for wetting and for cureinitiation. Also, a compatible "primer1 coating is preferably used. The subbing composition is preferably applied to the disk surface (preferably anodized) and cured by exposure to radiation, (e.g., brief intense W under inert atmosphere), sufficient to photo-cure the applied composition, with a photo-initiator typically included to decrease cure-time and improve efficiency. Example I In general, a selected subbing mix is preferably applied to a "Winchester disk" (of the type currently in common use as the substrate disks for magnetic recording of digital data for use in high-speed data processing). It has been discovered, as a feature hereof, that it is preferable to anodize such disks in a chromic acid bath; then to pre-clean them in a certain fashion, and then to apply a certain acrylate type (R-c pre-polymer) subbing mixture --Substrate, Anodizing: The mentioned preferred substrate is a relatively common moderate-cost, 14 in. or smaller diameter, Winchester disk leg,, of 15086 alufliintun alloy, about 75 mils thick, with a surface polished or diamond-turned to normal smovthness). The function of anodizing is to oxidize the aluminum disk to form a harder layer of aluminum oxide on its surface. Anodizing improves the corrosion resistance of the aluminum disk so that it can give extended archival life in the optical disk application. This process also works as a "pre-cleaning" to improve adhesion of the subsequent (polymer) subbing coat. With this process, the usual primer coating can be eliminated. There are several types of anodizing; here we prefer to use a "Type I, class I" chromic acid anodizing. The substrate we prefer is a "polished disk", rather than a diamond-turned (which can exhibit deep turning grooves on its surface -- and these grooves may be replicated in the subsequent subbing coat. During anodizing, the polished aluminum disk is "blast-dusted" [ dust particles blown off with a pressurizednitrogen gun), then vapor degreased with methyl ethyl ketone (MEK). In the chromic acid bath (1000F. + 50F,), a D.C. voltage is applied, and increased from 5V to 40V with increasing rate of 5V/min., and current density of 2 Ampsy t2. The anodizing should be "saturated" after about one hour. Next, the non-anodized substrate is rinsed with cold D.I. water, then with hot deionized water for about 5 min. There should be no further sealing or dyeing after the drying is finished. After such anodizing, an anodized thickness of about 0.1 mil to .2 mil will be seen. The (anodized) surface finish resulting will be as smooth and flat as necessary (e.g., max. "waviness-depth" is,0122 i .02 U"/in. over range of 10 mm.) and is quite suitable for the subsequent subbing coat. --Pre-cleaning of Anodized Substrate: Pre-cleaning the anodized substrate is important if a good subbing coat is to be realized. It affects adhesion and can reduce or eliminate surface defects. The anodizing may be thought of as a step in the pre-cleaning sequence. It changes the surface metal structure of the aluminum disk, and should leave a more uniform surface oxide; something that apparently contributes to superior adhesion (of subbing onto anodized aluminum surface). After anodizing pre-cleaning is continued in a 'clean room" atmosphere according to the following: 1. Ultrasonic agitation of disk surface submerged in a 1% solution of detergent (such as Liquinox) in deionized {D.I.) water ( > 10 megohms) for 3 min. 2. Rinse with filtered (to 0.2 um) running D.I. water (spray} for 1 min. 3. Rinse in a 3-step ¯cascade" rinse of filtered D.I. water, for 3 min. in each cascade. 4. Spray with filtered isopropyl alcohol (I.P.A.) for 1 min. 5. Ultrasonic agitation of disk surface in I.P.A. for 3 min. 6. Degrease-soak in I.P.A. for 5 min., or until hot. --Subbing Foroulation "SBZ For various reasons, and according to a feature hereof, it is found preferable to formulate the subbing mixture to comprise a radiation-cured acrylate pre-polymer, such as an acrylated epoxide like wSB-1" below -- along with compatible additives, as needed for cross-linking, cure-control, wetting and photo-initiation. This acrylated epoxide will be recognized as somewhat pre-polymerized and of relatively high modular weight, (e.g., such a ligomer or "pre-polymer" formulation will be understood as including acrylates and/or acryamides or other like groups adapted to be polymerized, or further polymerized, by a radiationcure like that described). A preferred subbing formulation SB-1 is formulated as follows: SB-1 Parts, by wt. Celrad #3701 (Celanese Chemical Co.) 36 TMPTA 25 2-ethylhexyl acrylate (EHA) 36 Zonyl FSN (DuPont) 1 "Irgacure it651" (Ciba Geigy Corp.) 2 Total 100 The "Celrad 3701" is characterized as a diacrylated ester of bisphenol A epoxy resin. Such an "acrylated epoxide", a short-chain polymer with acrylate end-groups, has relatively little cure-shrinkage, good tensile strength, good stability (chemical and thermal), and is found to (here) render a good tough, smooth coating, especially on such disks so-cleaned and so-primed. Now, workers will appreciate that a high molecular weight coating is desirable, being less susceptible to temperature change and involving less cure-shrinkage and associated stress. But high molecular weight materials exhibit a relatively high viscosity and so are inconvenient (slow) to filter, (e.g., through a 47 mm diameter, 0.45 um pore filter). Here, it has appeared feasible to use a relatively high molecular weight ingredient (like the acrylate epoxide pre-polymer), but to cut viscosity with otherwise useful low-viscosity additives, like the 2-ethylhexyl acrylate. the TMPTA ttrirethyl-ol propane triacrylate) is a multi-functional monomer used to promote cross-linking, accelerate cure and lower viscosity (at this concentration -less TMPTA allows cure-time to lengthen). In promoting cross-linkage, the TMPTA enhances the toughness and tensile strength of the cured coat; however it can cause a good deal of shrinkage during cure. TMPTA may be replaced by another like low-viscosity cross-linker, such as TMPT-ma (trimethyl-ol propane trimethacrylate) as workers will understand - The 2-ethylhexyl acrylate (EHA) is a viscosity-reducing organic diluent that reacts with the wmulti-functionalZ TMPTA and that bonds well with the resulting polymer coat and is compatible therewith (e.g., no constituents that will likely migrate and attack the subbing polymer or other coatings on the disk). It yields a good viscosity for these purposes assume "clean-room" conditions, about 680F arr#ient). A multi-functional monomer like TMPTA (three reactive groups) will likely need a co-constituent like EHA to polymerize with any of its groups not cross-linked with the acrylated epoxide -- otherwise, such unreacted groups can react and break-dewn the coating during service life (e.g., react with ambient oxygen, cause cracking of the subbing, etc.). The ERA diluent may, in certain cases, be replaced with other such additives like styrene (see S-2, below) or iso-decyl acrylate (though the latter is a bit more prone to water absorption and associated swelling with some loss of strength). The Zonyl FSN is characterized as a nonionic "f luorosurfactant" apt as a "surfactant"(wetting agent) here. It might be replaced with other like compatible surfactants in certain cases (e.g., FC-430, by 3M), though none can be recommended. Surprisingly, some other closely similar surfactants are unsatisfactory. Other "Zonal" (TM) type monomer surfactants (fluorocarbon methacrylate from DuPont) should also be adequate as a wetting agent. The 'Irgacure 651" (2-dimethoxy-2 phenyl aceto-phenone) serves as the photo-initiator. Other like photo initiators may be substituted in most cases (e.g., Irgacure #lS4, or Darocure it1173 from E.M. Industries -- note: Irgacure it184 needs longer cure time). Some photo initiators may be unsuitable under these conditions (cf. poor solubility, different cure-radiation needed, and some are too oxygen-sensitive; some fail to adequately "quench" the desired photo-cure). The components are all combined and heated, in air, to about 750 F. under "clean-room" conditions, with stirring, until the mixture becomes a homogeneous liquid. This liquid is then filtered while still warm through a series of filters to remove particles larger than 0.45 um. The filtered liquid is then degassed by placing it in a vacuum (25-29 in. Hg) for 30-60 min. prior to applying it to a disk. Here, a subbing coating about 20-40 um (microns) thick is assumed. --Application of Subbing; Curing: The subbing formulation (e.g., SB-1) will be understood as applied (e.g., 20-40 um thick and very uniform) to the aluminum disk surface anodized and cleaned as specified (unless adhesion is otherwise adequate). One preferred technique is "spin-coatingw as known in the art. Thus, the disk may be spun (e.g., at up to 80 rpm -- or kept fixed) while the coating formulation is deposited on its surface. The disk is then spun (e.g., 150-400 rpm), sufficient to efficiently remove excess coating material; the speed/time of rotation depending upon the desired rate/degree of removal. Such coating thicknesses between 10-50 um are found adequate to satisfactory smooth surfaces of the subject (anodized"} aluminum disks. After the desired amount of coating is so distributed on the disk, radiation-curing is invoked. Here it is preferably photo-cbemically cured, by (UV) radiation under an inert atmosphere. More particularly, one exposes the coating to W for about 1.5 min. before flushing with nitrogen to drive off all surrounding oxygen. Then cure is completed by continuing UV exposure for several min. under this nitrogen flush, while slowly rotating the disk (e.g., 20-50 rpm for total 4 min.). The win-oxygenw UV pre-exposure is preferred -- e.g., it is a bit slower than using a nitrogen-flush throughout, but seems to give a smoother finish and minimize any "replicating". It is preferred to use "non-focused" UV illumination since -- surprising to learn -- focused W light seems to cause wgroove-replicationw and uneven cure" problems in the film (woven where a diffuser is used). The non-focused UV light is found to give a more uniform exposure intensity. The non-focused UV beam p is passed through a quartz window with a trapezoid shape to expose all portions of the coating with the same light intensity. The window opening is wider at the outside area of the disk because there is more coating there. A 1000 watt UV lamp with a 5 inch arc length will be found satisfactory to illuminate the whole coating area evenly while disk is rotating te.g., an American Ultraviolet Co. "Porta Cure" 1000 UV lamp, rated at 95 MW/cm at 8.6 in. from the coating. The subbing layer cured under these conditions will form a tough, strong coating that is very smooth and level. It will not form any "globs", nor will it replicate grooves, etc., on the substrate surface. It also has a very good adhesion to the substrate. This is quite apt for superposing the mentioned optical recording layers. --Process Optimization: 1. Small air bubbles may cause "pinholes" or "streamers" to appear in the smoothing layer; vacuum degassing of the solution and careful handling afterward can eliminate this. 2. Or pinholes may appear for no apparent reason, increasing in number with increasing disk rpm; proper pre-cleaning can eliminate this. 3. Or pinholes may appear where the disk surface is not "wet" properly, or where the coating is too thin to maintain its integrity; keeping disk rotation speed below about 200 rpm seems to minimize this. RESULTS The thickness of the smoothing layer is preferably between 20-30 um (less than about 10 um is not favored) and very smooth. A good, smooth subbing surface will be observed on such fully-polished or polished-anodized disk surfaces, with all the usual bumps, scratches, gouges and like anomalies satisfactorily "buried". For instance, when such a smoothing surface is viewed under a (1000 X) microscope it will be seen to be markedly, and dramatically, smoother than a very highly polished icro-fine aluminum disk ace). To be able to thus render such a "micro-fine" surface using such a simple, convenient, relatively inexpensive treatment (anodizing, cleaning, and subbing coat) is quite remarkable. Also, this subbing will be observed to exhibit superior archival life and long-term stability -- e.g., withstanding extended exposure to a rather extreme temperaturefhumigiey cycling even with the mentioned "optical tri-layer" (e.g., no evident delamination or stress-cracking of tri-layer; no decomposition of subbing polymer; also no evidence that "low molecular weight components like the surfactant, or photosensitizer or their by-products, had migrated and attacked the subbing or tri-layer or upset adhesion). Even more significant, subbing smoothness will be so good that later deposition of prescribed optical tri-layers and satisfactory recording thereon is made possible -- for instance, one can so record and read-out with good S/N level (order of 30 dB+) and a very low bit-error-rate. And the so-cured so-aged subbing is immediately ready for service (e.g., heating, etc.) -- e.g., without requiring any further aging cycle. Workers will recognize that other related techniques and/or materials and associated adjustments may be substituted in appropriate cases, taking care to assure adequate stability (over extended archival life) and to avoid inducing stress-cracks (of superposed tri-layert) or decomposition of subbing materials (e.g., volatilizing due to thermal effects or because of inadequate curing). Radiation-curing is preferred over other superficially related methods, #like "peroxide curing which is complex, hard to control, and apt to exhibit short "pot life" (e.g., workers will recognize that the peroxide cure reaction is exothermic and subject to overheating, making it difficult to control and dangerous to handle -- e.g., for good control, cure temperature must be kept low, thus extending cure-time; also gases are produced and, if the cure proceeds too quickly, these gases can't adequately escape and be dissipated, but can induce light-scattering, a "cloudy", semi-opaque coating -e.g., trapping gas bubbles). Heretofore, a "primer coat", under the subbing, was thought necessary for good subbing results (e.g., to better resist moisture intrusion over extended service life, while maintaining good adhesion). That is, workers found it unsatisfactory to simply apply a subbing mixture to a bare un-primed aluminum disk surface, however precleaned -- otherwise inadequate uniform smoothness, or a poor bond over extended service life, etc., could result. Somewhat surprisingly, this subbing coat (and others like it) seems to require no "primer" when applied to such an anodized surface (so pre-cleaned, etc.). Also, other (preferably acrylated) like subbing formulations will be applicable in many such cases. Others will not. For instance, workers have at times suggested a "plain epoxy" smoothing coat for other different purposes (cf. for some common magnetic recording disks, an "epoxy-only" pre-layer is used as a "primer" for the magnetic oxide coating). Such epoxy systems have certain advantages (e.g., notoriously hard, readily "contact-cleaned" and relatively low cure shrinkage) -- but they are rather expensive (equipment, processing time, materials); they usually render too coarse a surface (gross "holidays" can appear); and they can crystallize non-homogeneously inducing error zones"). Also, they are solvent-based, require a heat curing (UV is much cooler) and use materials with too brief a wpot life". Thus, an acrylated epoxy is preferred for the subbing. --Alternative Subbing Formulations: Workers will recognize that such an acrylated epoxy system {formulation SB-1) may be modified for various reasons. For instance, to lower viscosity, formulation SB-2 is given as follows: SB-2 Parts, by wt. Celrad 3701 36 THPTA 25 EHA 36 FC-430 {3S Co.) 1 Irgacure 651 2 Total 100 This replaces Zonyl FSN with a FC-430. FC-430 is a "fluorocarbon ester" apt as a surfactant. Its wettability might not be as good as Zonyl FSN. However, it produced a film about as good as SB-1. SB-3 Parts, by wt. CMD 1700 18 Celrad 3701 18 TMPTA 25 Elba 36 FC-430 1 Irgacure 651 2 Total 100 Half of the Celrad 3701 in SB-2 is replaced with CMD 1700. CMD 1700 is an acrylated acrylic. It improves the color and (exterior) durability. However, it is apt to be quite brittle and not as chemically resistant as an epoxy. It tends to be more brittle and crack when subjected to a moist environment. Thus, SB-3 (and like subbing) is less preferred. Parts, by wt. SB-4 (vs SB-2 RDX 52225 ( Co.) 24 Celrad 3701 24 -- (36 TMPTA 22 ---- (25 EHA 24 ---- (36 FC-430 2 ---- (1 Irgacure 651 4 ---- (2 Total 100 Total resin is increased and half of the Celrad 3701 in SB-2 is replaced with RDX 52225. RDX 52225 is an acrylated urethane. It improves flexibility and toughness and also has a good abrasion resistance. The viscosity is increased by so increasing the concentration of main resin ingredient. The purpose is to reduce the number of "defects" -- and a reduced number of defects will be observed here. However, the coating exhibits "orange peel" after it is aluminized and it is not smooth enough for the optical disk application. Thus, this type subbing is definitely non-preferred. SB-5 Parts, by wt. Celrad 3701 36 TMPTA 25 V-pyrol (GAF) 36 FC-430 1 Irgacure 651 2 Total 100 The EHA in sB-2 is replaced by a V-pyrol diluent. V-pyrol iS a more reactive vinyl-pyrolidone diluent for acrylated epoxy. It has a low volatility. With this ingredient, one might expect to reduce the defects number (less volatile material evaporation than for EHA during the spinning). However, this coating appears cloudy after it is aluminized and is non-preferred for the optical disk. Parts, by. wt. SB-6 (vs SB-2 Celrad 3701 27 -- (36 TMPTA 34 -- (25 EHA 34 -- (36 FC-430 1 -- (1 Z-6Q20 (Dow Corning) 1 Irgacure 184 3 -- (2 Total 100 The Irgacure 651 photoinitiator in SB-2 is replaced by Irgacure 184. Irgacure 184 is a non-yellowing, highly efficient photoinitiator and will produce a better "thru cure" in the coating. Z-6Q20 is a silane adhesion promoter and is added to improve subbing adhesion to the aluminum disk. The viscosity of this formula is reduced, so one can see the effect of viscosity on the coating. Because Irgacure 184 has a lower curing efficiency than Irgacure 651, this SB-6 film is hazy-looking after it is aluminized and is not completely cured. This is non-preferred for the optical disk. --Conclusion: It will be understood that the preferred embodiments described herein are only exemplary, and that the invention is capable of many modifications and variations in construction, arrangement and use without departing from the spirit of the invention. For example, the materials, means and methods disclosed herein may also be applicable, with appropriate adjustments, for micro-fine smoothing coatings on other like metal substrates (especially oxidized-aluminum), such as those used to support high quality coatings for high-speed magnetic recording or for other optical coatings or for other analogous recording. The above examples of possible variations of the present invention are merely illustrative. Accordingly, the present invention is to be considered as including all possible modifications and variations coming within the scope of the invention as defined by the appended claims.

Claims: What is claimed is: 1. In a method of making an archival optical information record comprised of a rigid aluminum substrate disk, a smoothing layer, record-surface portions thereon, and optical film means, carried on the smoothing layer and requiring superior optical flatness thereof, the improvement steps therein of: pre-anodizing the surface portions of the disk; and formulating said smoothing layer to comprise a prescribed radiation-cured acrylate adapted to bond firmly with said disk and said film means; functional groups adapted to firmly bond with compatible groups in the acrylate and on the disk; said smoothing layer being UV-curable in a few minutes and including an associated photo-initiator. 2. The method as recited in claim I, wherein said optical film means comprises a metallic reflector layer, coated upon the smoothing layer and exhibiting a high degree of optical flatness; and wherein said smoothing layer is formulated to comprise a short-chain, relatively high molecular weight, acrylated epoxy plus a compatible eross-linking - constituent and a compatible wetting agent, plus a relatively low molecular weight organic diluent. 3. The method as recited in claim 2, wherein the cross-linking constituent comprises a relatively low molecular weight, multi-functional acrylate and wherein the diluent is selected and adapted to also tie-up random end-groups of said acrylate cross-linking constituent; wherein the cross-linking constituent comprises a compatible cure-accelerating triacrylate or trimethacrylate; and wherein the related diluent is selected from at least one from the diluent family consisting of styrene and acrylates. 4. The method as recited in claim 3, wherein the reflector layer comprises a thin aluminum film which is part of an optical trilayer adapted for high speed optical recording of digital data for archival storage. 5. A method for providing a record blank for use over a relatively extended archival life, the method comprising: providing a disk substrate having a recording surface typically exhibiting a prescribed relatively rough finish; anodizing said recording surface; applying a prescribed acrylate subbing layer on said anodized surface to render a prescribed high degree of optical flatness; and applying a prescribed reflector film of high optical flatness on said subbing layer; said subbing layer being formulated to comprise one or more radiation-cured acrylates, cured by brief exposure to associated UV radiation. 6. In a method of providing an archival digital record blank of prescribed extended life for use with optical recording and optical detect means, wherein a metal disk "substrate means" is to be provided with a high-reflectivity surface thereon, exhibiting very high, precise optical flatness, and intended to provide a substrate for high-flatness optical film means, the improvement comprising the steps of: polishing, then anodizing record surface portions of the disk sufficient to resist corrosion over said life; rendering improved carrier-coating means on this disk surface, well bonded thereto and serving as the "substrate means" for said film means, this coating means being rendered by applying an acrylated subbing layer on this anodized, cleaned surface, this subbing layer being formed to a thickness of a few dozen um., such that the disk surface is rendered sufficiently flat for said high reflectivity; said anodizing being rendered to optimize adhesion of said subbing layer. 7. The method of claim 6, wherein the subbing includes an acrylated epoxy pre-polymer polymerized by up to a few minutes exposure to related "non-focused ultra-violet radiation at intensities of up to a few hundred mW/cmê. 8. The method of claim 7, wherein said W exposure is conducted briefly in an oxygen-containing atmosphere, then concluded in an inert atmosphere, while rotating the disk. 9. The method of claim 8, wherein the record surface portions anodized comprise finely polished, not diamondturned, aluminum anodized in a Type I, class 1, acid electrolytic bath sufficient to oxidize at least about 0.1 - 0.2 mils very smoothly; the anodizing being followed by rinsing, and related cleaning. 10. The method of claim 9, wherein a chromic acid bath is used for anodizing a Winchester-alloy-disk surface at about 90 - 1100F., about 1/2 - 5 Amp/sf and at about 1 - 5 VDC increased in steps to 30 - 50 VDC. 11. The method of claim 10, wherein the anodizing is followed by an ultra-sonically agitated detergent soak, followed by associated aqueous and solvent rinsing. 12. An archival optical data record comprising a prescribed anodized disk substrate surface and a prescribed optical recording structure supported thereby, with a related subbing thickness disposed therebetween, this thickness comprising the radiation cure-product of an acrylate mix deposited on the anodized substrate. 13. The combination as recited in claim 12, wherein the mix includes a radiation-cured acrylated epoxy prepolymer and the substrate is comprised of aluminum; said anodizing providing at least about 0.1 - .2 mils oxide coating. 14. The combination as recited in claim 13, wherein the mix also includes a multi-functional polymeric crosslinking additive and a related organic diluent capable of combining with this additive; the mix being W-cured with little or no solvent and also including a compatible surfactant and a compatible initiator. 15. The combination as recited in claim 14, wherein the mix includes a fluoro-polymer surfactant and a photo-initiator. 16. The combination as recited in claim 15, wherein the recording structure comprises an optical "tri-layer" and wherein the archival record is designed and adapted for at least 5 - l O years under severe EDP conditions. 17. The combination as recited in claim 16, wherein the cross-linker is comprised of an acrylate of tri-methyl-ol propane and the diluent comprises a related viscosityreducing acrylate and/or styrene; and wherein the substrate comprises a Winchester disk anodized in an electrolytic chromic acid bath. 18. The combination as recited in claim 26, wherein the subbing is W-cured in non-focused UV and spin-coated. 19. The product of the method in claim 1. 20. The product of the method in claim 5. 21. The product of the method in claim 6. 22. In a record blank for optical R/W recording of "transition bits" on an information layer thereof, and adapted for extended-life archival storage, the blank comprising: a substrate disk carrying at least one metallic reflector film having a prescribed optical flatness on at least one disk surface, the improvement therewith comprising: said disk surfaces being anodized sufficient to prevent corrosion thereof over said life, and a related acrylated epoxy smoothing layer deposited on the anodized disk-surfaces in a depth sufficient to render said optical flatness; this anodizing layer being adapted for extended archival service.

Inventors: BELL, IRVING J., HO, WU-JING, LEE, N.
Applicants: UNISYS CORPORATION
Application year: 1985
Main classification: G11B7
IPC codes: G03F7, G03C5, G11B7