MULTILAYER CIRCUIT

Abstract: A multilayer circuit consists of two layers of aluminium conductor on a silicon semiconductor body and spaced apart by silicon oxide. The lower layer (2) of aluminium is given a surface coating of a material (12) consisting of titanium and tungsten to inhibit the formation of projecting nodules of aluminium when the silicon oxide is formed at a raised temperature. The upper layer (4) of aluminium is laid on to a flat surface of silicon oxide (7) which is leveled by an etching process, any variations in the original surface of the oxide being filled prior to etching.

Description: MULTILAYER CIRCUIT This invention relates to multilayer electrical circuits and it is particularly applicable to semiconductor devices which carry a number of conductive tracks whose paths intersect each other at multilayer crossovers in which one track is electrically insulated from another by means of an intervening material which serves to support the upper track. It is customary for the upper track to undergo abrupt changes in profile where it crosses over the lower track which is usually formed at the surface of a semiconductor body, and these abrupt changes in profile can render it difficult to manufacture tracks and multilayer interconnections in a reliable manner. It has been found that if the upper track is defined by means of a selective etching technique then the conductive material on the shoulders of the abrupt changes in profile may not be completely removed, thereby resulting in undesired short circuits. The present invention seeks to provide an improved multilayer circuit and a semiconductor device incorporating such an interconnection. According to a first aspect of this invention, a multilayer electrical circuit includes a substrate carrying a first conductive layer of aluminium and means for inhibiting the formation of temperature dependent nodules therein; a silicon oxide deposition overlying said layer so as to follows its contours and having a planar outer surface; and a further conductive layer overlying said outer surface. According to a second aspect of this invention, a semiconductor arrangement includes a body of silicon having at a surface thereof a first aluminium conductor having an overlying metallic layer in contact therewith so as to inhibit the formation of temperature dependent nodules in the aluminium; a silicon oxide deposition overlying at least part of said conductor, the surface of the oxide deposition remote from said body of silicon being of a planar nature; and further conductive aluminium conductor overlying said outer surface. Preferably a layer of material containing tungsten and titanium is placed over the aluminium prior to the formation of the silicon oxide covering. Of necessity, the silicon oxide is formed at a fairly high temperature, even though the deposition process is sometimes referred to as a low temperature oxidisation as it is performed at about the temperature of 4200C, which is very much lower than the temperature at which thermally grown oxide is produced. The coating of the titanium and tungsten material prevents or inhibits the formation of nodules in the aluminium during the high temperature step in which the silicon oxide is deposited. These nodules take the form of raised projections standing proud of the upper surface of the aluminium, and are commonly formed in the absence of a covering layer of the material specified. Alternatively, titanium may be included in the aluminium. which is present at the surface of the body of silicon in order to inhibit the nodules, but such a process is not preferred in view of the additional complexity of introducing the titanium into the aluminium. It is therefore preferred to provide the coating of tungsten and titanium as a separate step following the formation of the first conductive layer of aluminium, which itself may well be defined by means of a selective etching process. Preferably the inhibiting coating consists in the main of tungsten with a contribution of titanium of about 10%. According to a third aspect of this invention a method of making a multilayer circuit for a semiconductor arrangement includes the steps of: forming a localised track of aluminium at the surface of the device; coating at least part of said surface and said tracks with a material which inhibits the formation of temperature dependent nodules in aluminium; forming thereover a layer of silicon oxide at a raised temperature; providing an overlying material which fills any recesses and depressions in the upper surface of the silicon oxide so as to form a relatively flat surface; removing said overlying material with part of said oxide layer to leave a thinner layer of oxide having a relatively flat planar surface; and forming conductive region of aluminium on the surface of the said thinner layer of oxide. 'Ihe layer of silicon oxide is made initially much thicker than would otherwise be the case so that when portions of it are removed, together with said overlying material, a sufficient thickness of the oxide remains so as to provide an electrical insulation between the two regions of aluminium. The invention is further described by way of example with reference to the accompanying drawings in which: Figure 1 shows a conventional multilayer circuit, and Figures 2 and 3 show steps in the formation of a multilayer circuit in accordance with the present invention. Referring to Figure 1, a body of silicon 1 in which one or more semiconductor devices (not shown) have been formed is provided with a localised track 2 of aluminium on its upper surface. The track 2 can be formed by any convenient means and typically a continuous sheet of aluminium is initially sputtered at a temperature of about 4000 on to the upper surface of the silicon body 1 after which regions of it are selectively removed by an etchant to leave a track having the required profile and disposition. In practice many such tracks having intricate paths can be provided to link the semiconductor devices. A layer of silicon oxide 3 is then formed over the conductive track and although the oxide may be formed by what is conventionally termed a low temperature process, i.e. it is deposited from a vapour rather than grown thermally from the body of silicon, the process proceeds 0 at an elevated temperature of about 420 C. Such a temperature can produce nodules in the upper surface of the aluminium, but the process proceeds only for a very short time and overall the upper surface of the oxide tends to follow undulations due to the nodules in the aluminium.These nodules take the form of localised raised portions projecting above the surface of the aluminium. On top of the silicon oxide is produced a continuous layer of aluminium which is then selectively etched to leave a further conductive track 4 of aluminium, in this case at right angles to the first track 2,and it will be seen that both the upper surface of the oxide and the track 4 follow contours introduced by the presence of the track 2. It has proved difficult to reliably and economically remove those portions of the upper layer of aluminium to leave tracks in the required position as in practice thin strips of aluminium tend to remain on the shoulders 5 of the undulations thereby causing short circuits with adjacent conductive tracks, formed from the same layer. Such an effect can significantly reduce the manufacturing yield of semiconductor devices having many conductive tracks in close proximity to each other. The present invention provides an improved multilayer interconnection in which this disadvantage is largely removed. Referring to Figures 2 and 3, there are shown therein sectional views representing steps in the production of a multilayer interconnection which is formed in accordance with the invention. As before tracks 2 are formed on the surface of a semiconductor body 1 of silicon. A thin coating 12 of a material consisting of titanium and tungsten is provided over the aluminium tracks 2. This coating is formed by a sputtering process.The effect of this coating is to inhibit or prevent the formation of nodules on the surface of the aluminium when the tracks and the otherwise open regions of the semiconductor body 1 are covered with a thick oxide layer 7. This oxide layer is an oxide of silicon and is again formed typically by a low temperature vapour deposition process at about 4200C. However, in this case, it is necessary for the oxide to be produced to a much thicker extent than the layer of oxide 3 shown in Figure 1, for reasons which will subsequently be apparent. The upper surface of the oxide layer 7 contains undulations 8 which correspond generally to and conform with the disposition of the aluminium tracks 2. These recesses and other minor depressions are filled by means of a photoresist material 9 which is spun on to the upper surface of the oxide. That is to say the material 9 is applied in liquid form after which the semiconductor body is rotated rapidly so as to spread a layer of the resist having a flat upper surface 10, which covers the peaks of the oxide. In this instance, the photoresist is used as a convenient filler material, and not for its etchant properties. The photoresist and the silicon oxide are subsequently etched using a plasma technique. In this technique the body of silicon is placed in an evacuated chamber, and chlorine and fluorine gas are passed through the chamber whilst the gas is ionized to form a plasma. The ionized plasma combines with the exposed surfaces to remove the resist and the low temperature oxide at a uniform rate. This process is continued until the upper surface of the arrangement is constituted by the line 11, that is to say, after all of the photoresist 9 has been removed. It will be appreciated that there is relatively little thickness of oxide remaining over the aluminium track 2 and it is for this reason that it is neccesary to inhibit the growth of nodules. Any large nodules which were formed at the surface of the track 2 would be exposed when the oxide thickness is reduced by etching, thereby causing a short circuit to any subsequent layer of conductive material. Subsequently, conductive tracks 4 are formed transversely to the original tracks 2, the new tracks 4 being in this example, at right angles to the original tracks. These tracks 4 are formed of aluminium in a manner similar to tracks 2. A continuous coating of aluminium is sputtered at about 4000 on to the planar surface of the silicon oxide, after which regions of the coating are etched using an etch resistant mask formed in a conventional manner. The aluminium is readily and completely etched, as the aluminium is now removed from a flat surface, so there is no longer a risk of leaving slivers of aluminium in regions which are difficult to etch.

Claims: CLAIMS 1. A multilayer electrical circuit including a substrate carrying a first conductive layer of aluminium and means for inhibiting the formation of temperature dependent nodules therein; a silicon oxide deposition overlying said layer so as to follow its contours and having a planar outer surface; and a further conductive layer overlying said outer surface. 2. A semiconductor arrangement including a body of silicon having at a surface thereof a first aluminium conductor having an overlying metallic layer in contact therewith so as to inhibit the formation of temperature dependent nodules in the aluminium: a silicon oxide deposition overlying at least part of said conductor, the surface of the oxide deposition remote from said body of silicon being of a planar nature; and further aluminium conductor overlying said outer surface. 3. An arrangement as claimed in claim 2 and wherein the metallic layer is localised to conform to the area profile of the first aluminium conductor. 4. An arrangement as claimed in claim 3, and wherein the coating includes titanium and tungsten. 5. An arrangement as claimed in claim 4, and wherein the ratio of tungsten to titanium is about 10 to 1. 6. An arrangement as claimed in claim 2, and wherein the material Of the first conductor includes a proportion of titanium so as to inhibit the formation of said nodules. 7. A method of making a multilayer circuit for a semiconductor arrangement including the steps of: forming a localised track of aluminium at the surface of the device; coating at least part of said surface and said tracks with a material which inhibits the formation of temperature dependent nodules in aluminium; forming thereover a layer of silicon oxide at a raised temperature; providing an overlying material which fills any recesses and depressions in the upper surface of the silicon oxide so as to form a relatively flat surface; removing said overlying material with part of said oxide layer to leave a thinner layer of oxide having a relatively flat planar surface; and forming a conductive region of aluminium on the surface of the said thinner layer of oxide. 8. A method as claimed in claim 7. and wherein said coating includes titanium and tungsten. 9. A method as claimed in claim 7or 8 and wherein said overlying material is a photoresist material which is applied as a fluid. 10. A method as claimed in claim 9, and wherein the photoresist material and said oxide are removed by an etching process to leave the thinner layer of oxide.

Inventors: HARVEY, PAUL ROBERT
Applicants: MARCONI ELECTRONIC DEVICES LIMITED
Application year: 1985
Main classification: H01L23
IPC codes: H01L23, H01L21