CATALYTIC DEHYDROHALOGENATION PROCESS

Abstract: The invention is an improved process for the manufac­ ture of vinyl chloride from ethylene dichloride. Specifically, the invention is an improved process for the catalyzed de­ hydrohalogenation of ethylene dichloride in the presence of oxygen and a catalyst comprising a rare earth metal chloride on a zeolite. The process enables one to conduct the dehy­ drohalogenation (or cracking) operation at significantly lower temperatures than employed using a thermal process, with­ out the coking problems observed in such cracking proc­ esses.

Description: CATALYTIC DEHYDROHALOGENATION PROCESS BACKGROUND OF THE INVENTION It is well nown that vinyl chloride monomer (VCM) can be produced from 1,2-dlchloroethane (commercially called ethylene dichloride or EDC) by splitting off a molecule of hydrogen chloride. The dehydrohalogenation reaction (commonly called "cracking" in the trade) is typically accomplished by heating the EDC, in the absence of a catalyst, In an inert atmosphere sing high temperature and pressure; usually about 5500C. and at t pressure of about 300 to 600 psi (21 - 42 Kilograms/cer.timeter2; 2,070,000 to 4,i40,000 Pascals). A serious disadvantage of the standard pyrolysis or thermal process is the need of a large amount of costly heat energy to accomplish the cracking. Another serious difficulty encountered in such a process is the rapid deposition of solid by-products (coke) on the tubes which limits the process to relatively short operating periods before cleaning of the tubes is required. Lastly, in these high temperature processes, undesirable side reactions frequently occur which lower the conversion of EDC. To reduce the problems observed in the standard pyrolytic cracking process various catalytic processes have been proposed. For example, U.S. Patent No. 2,877,277 teaches the use of an alkaline earth metal hydroxide in aqueous solution to promote the dehydrochlorination of EDC to VCM, and refers to the prior use of alkali metal hydroxides, These processes suffer from the disadvantages of a very long contact time (30 minutes to 2.5 hours) and difficulty in the separation and purification of the resultant VCM from the aqueous solution. U.S. Patent No. 3,290,399 teaches the use of graphite to promote the cracking reaction, and references the use of activated carbon washed with nitric acid as disclosed in British Patent No. 823,285. The processes suffer in that reaction temperatures and pressures are still high, up to 60doc. Japanese Patent No. 24870/64 teaches the use of a catalyst of a boron compound such as boric acid on activated charcoal, Lastly, U.S. Patent No. 3,896,182 teaches that the clogging of pyrolysis reactor tubes by carbonaceous substances (coking) can be reduced by conducting the reaction in the substantial absence of oxygen, below 2.0 ppm of oxygen present. While such processes may be commercially feasible, there has been and still is a continuing search for catalytic materials which will improve the dehydrohalogenation process by enabling the use of lower operating temperatures anc pressures and further reduction in undesirable side reactions and coking. SUMMARY OF TEE INVENTION It has been unexpectedly found that conversion of EDC to VCM with less energy expenditure and reduced coking can be obtained by a process which comprises dehydrohalogenating the EDC to VCM, in the presence of oxygen, employing, as a catalyst, a composition comprising a rare earth metal chloride on a zeolite. Using the rare earth metal chloride-zeolite catalysts of the instant invention, the cracking process can be operated at a temperature as low as 1530C, up tO 5000C., and more preferredly from about 200 C. to about 3500C., at pressures from atmospheric to about 300 psi (1 - 21 Kilograms/ centimeter2; 101,400 - 2,070,000 Pascals). DETAILED DESCRIPTION Vinyl chloride monomer (VCM) can be prepared by various processes, but the most common process involves the formation of EDC by the reaction between ethylene and chlorine or hydrogen chloride, followed by a dehydrohalogenation step wherein the EDC is thermally cracked under pressure to VCM and by-product hydrogen chloride. The hydrogen chloride is typically recovered and used in an oxyhydrochlorination step wherein the hydrogen chloride is reacted with additional ethylene to produce EDC which is, in turn, fed to the cracking step. The VCM is recovered, purified, and used extensively as a monomer in the manufacture of polyvinyl chloride (VAC) resins, a large volume, versatile plastic material. In the typical cracking process, large amounts of natural gas are burned to supply the heat energy to operate the cracking furnaces. In these processes, the EDC is vaporized and passed through a tube-type furnace which is directly heated to a temperature in the range of about 5000C. to about 6000C. In the present, standard commercial cracking process no solid cracking catalyst is employed. In the absence of a catalyst, the reaction is a thermally induced dehydrochlorination whereby one molecule of hydrogen chloride is split out of each EDC molecule, resulting in one molecule of VCM. The present invention encompasses the use of many process design configurations such as a single fluid-bed with reactants fed into the reaction zone through a distributor plate, fluid cat cracking technology where the oxygen is fed in at a separate regeneration zone in the reactor, a fixed bed cracking furnace, or any other known designs. The heat energy can be supplied in any known manner, but typically is supplied by burning natural gas. The EDC is vaporized and passed through the fluid bed or tubes in the furnace where the catalyst is present. The ratio of oxygen to EDC in the feed stream is controlled to accomplish the objectives of this invention and yet operate safely. The temperatures employed in the present process range from as low as 1500C. up to about 5000C., more preferredly from about 2000C. to about 3500C., and most preferredly from about 2500C. to about 3250C. In the process, pressures will range from about one atmosphere (1 kilograms/ centimenter2; 101,400 pascals)up to twenty (20) (21 2 k rams/centimeter2i 2,070,000 pascal) or more atmospheres, but more typically range from about five (5) to about fifteen (15) atmospheres(5 - 11 kilograms/centimeter2; 507,000 - 1,520,000 pascalsk A critical feature of the present invention comprises the use of an improved catalyst for the cracking step. Specifically, the catalyst is comprised of a rare earth metal chloride deposited on a zeolite. Both natural and synthetic zeolites can be used in the present invent ion. Examples of natural zeolites are analcite, erionite, chabczite, faujasite, mordenite, gmelinite, mazzite, offertite, heulandite, natrolite, stilbite, and thomsonite. The synthetic zeolites can be made in a variety of forms ranging from gelatinous to porous and sandlike. Examples of known synthetic zeolites are Type h scribed in U.S. Patent No. 2,882,243); Type X (described in U.S. Patent No. 2,882,244); Type r (described in U.S. Patent No. 3,130,007); Type Ps (described in U.S. Patent No. 3,030,181); and other zeolites as described in the December 13, 1982 article in "Chemical and Engineering News" entitled "Shape Selectivity Key to Designed Catalysts" by Mr. Joseph Hoggin. For the purposes of this invention, the solid zeolites are preferred, and particularly those synthetic solid zeolites having pore openings of 5AO or more. Synthetic zeolites having a pore opening of over SA0 are readily available commercially from Englehard Minerals and Chemicals and Linde Division of Union Carbide Corporation. Examples of such commEercially-availaLle zeolites are Englehard's HFZ-20, ,=;r'Z-33, and HFZ-55. The rare earth metal chloride can be the chloride of any rare earth metal as found in the Periodic Table numbers 57 (Lathanum) through 71 (Lutetium). The rare earth metals Lathanum (La), Praeseodymium (Pr), Neodymium (Nd), and the rare earth metal mixture Dydinlum which consists essentially of La, Nd, Pr, Samarium (Sm) and Cerium (Ce), are all readily available and, hence, are preferred rare earth metals. The most preferred rare earth metal is Lanthanum, and the most preferred rare earth metal chloride is Lathanum Chloride (LaCl3). The amount of rare earth metal chloride employed with the zeolite can -be from about 0.1% up to 30% by weight of the total weight of the catalyst. More prefer redly, the weight of the rare earth metal chloride is from about 2% to about 20%, and most prefer redly from about 4% to about 15% by weight. The optimum level of rare earth metal chloride on the zeolite may vary with the type of zeolite employed. The catalysts of this invention can also contain levels of other metals which are often used to impart stability and the like. Examples of such optional materials are alkali and alkaline earth metal oxides and chlorides such as Lithium and Potassium Oxide and ChlorideS Magnesium Chloride, and Strontium Chloride. These additional metals can be employed in up to 5% by weight based on the total weight of the catalyst. The rare earth metal chloride(s), and other optional metal chlorides and oxides, can be deposited on the zeolite in any known manner. Preferably, an aqueous solution(s) of the metal(s) is prepared and contacted with the zeolite, which mixture is then filtered and dried at temperatures below about 2000C., followed by calcination at a temperature from about 500 C. to 1000 C. for about 2 to 16 hours. A calcination temperature of about 5000C. to about 8000C. is preferred. Calcining the catalyst mixture at high temperatures, i.e. above 800"C., can reduce the stability and/or effectiveness of the resultant catalyst. The concentration of the metalis) in the aqueous solution(s) is determined by the desired level of metal on the final catalyst. If more than one metal is added to the zeolite, this can be done simultaneously or sequentially by adding each metal after each drying step. It is possible to add part or all of the metal(s) to the zeolite while the zeolite is in the reactor are, and also to add additional metal(s) to the zeolite during operation to replenish metal(s) lost during the reaction. The zeolite chosen should have a form or particle size permitting it te be conveniently placed or packed in the cracking reactor. The rare earth metal chloride-zeolite catalyst is place in the cracking reactor in such fashion as to allow the passage of vapor therethrough. The catalyst may be fixed in the reactor bed or used as a fluidized bed. Typically, the cracking reactor is purged with nitrogen before the EDC and oxygen are introduced into the reactor. When the EDC comes in contact with the catalyst the dehydrochlorination reaction or cracking proceeds smoothly, rapidly converting the EDC to VCM and by-product HC1. The amount of oxygen employed in the process, either as pure oxygen or air, is from about 0.05 mole to about 0.5 mole of oxygen per mole of EDC. Below 0.05 mole, increased carbon buildup is observed, and above 0.5 mole, increased formation of carbon oxides is observed. The preferred molar ratio of oxygen to EDC employed is from about 0.15 mole to 0.3 mole per mole of EDC. Not all the oxygen need be added in the reaction zone; i.e. the oxygen can be staged or added in a separate zone. The oxygen is added to the reactor in a manner and flow to ensure safety and operations under non-explosive conditions. While the cracking reaction may be operated at atmospheric pressure, it is preferred in the present invention to operate at superatmospheric pressures of from about 5 to 20 atmospheres (5 - 11 2 kilograms/centimeter ; 507,000 - 1,520,000 pascals) . generally, at higher pressures, less coking and less formation of undesirable chlorohydrocarbon by-products, such as CCl4, occurs than when operating at atmospheric pressure. If necessary, the reactor can be shut down and the carbon formation, if any, can be readily removed by conventional means; i.e. heating the reactor at elevated temperatures usually in the range of over 3000C. to about 7000C. Also, the carbon can be removed and the catalyst regenerated in a continuous manner using a fluid cat cracking reactor design as shown in the "Chemical and Engineering News" article previously referenced. The reaction or contact time of the EDC with tne catalyst in the reactor can be valied depending on the volume and shape of the reactor and the flow rate of EDC and oxygen. The contact time necessary between the EDC and catalyst to promote the desired dehydrochlorination reaction is obtained by controlling the space velocity of the gaseous material passing through the reaction zone. It has been found, however, that for most reactors a contact time as high as about 60 seconds and as low as 0.5 second can be employed. If the contact time is too low the quantity of unreacted EDC is too high. On the other hand, if the contact time is too high, the amount of carbon oxide and by-product impurities increase. One can readily adjust the gaseous fed rate to obtain the optimum contact tine for any particular type reactor. Contact times in the experiments detailed in the following Examples ranged from about 5 seconds to about 30 seconds. The gaseous mixture withdrawn from the reaction zone can be passed directly to a condenser to recover the condensable materials including the EDC, and hydrogen chloride passed overhead to be collected, and then often recycled to an oxyhydrochlorination process to be used in making more EDC. Alternatively, the gases leaving the reaction zone can be cooled and subjected to fractional distillation under pressure, preferably at lower pressure than that used for the cracking. The hydrogen chloride separates first and is recovered or recycled. The uncondensed gases can be vented into a separate recovery or treatment zone wherein the VCM and unreacted EDC are recovered and fractionally distilled to remove the VCM. The unreacted EDC is recycled to the cracking zone. Present commercial cracking processes typically operate at above 500 C. to 6000C., at pressures of 300 to 600 psi (21 - 42 2 kilograms/centimeter ; 2,070,000 - 4,140,000 pascals), and have contact times of about 1 to 5 seconds. For example, operating with no catalyst (thermal cracking only), at a temperature of 5600C. with a one second contact time, an EDC conversion of up to 80% can be obtained. At 5300C., the EDC conversion drops to about 50%, and at 5000C., the EDC conversion drops to about 20%. Operation below 5000C is not economically feasible. Hence, the standard thermal EDC cracking processes require high temperature operation and very high energy use. Further, these processes typically suffer from high coking which necessitates shut down and decoking about once each month. In contrast, the process of this invention results in effective cracking of EDC to VCM with significant energy savings and little coke formation, thereby permitting long operation between shut downs. The formation of carbon oxides and by-product chlorinated hydrocarbon can be as low as under 10%. A small amount, up to 5% and usually no more than 2%, of ethylene may be produced. The following Examples are given to more specifically define the present invention. It is understood that the Examples are demonstrative and illustrative only, and not intended to be limiting of the invention. In the examples, all parts and percents are by weight, unless otherwise indicated. Example of Preparation of Catalyst 500 grams of HEZ-55, a synthetic zeolite obtained from Englehard Minerals and Chemicals, was added to an aqueous solution of 5.77 grams of Lanthanum chloride, (LaCl3.6H20) in 40 cc of distilled water, and stirred to obtain uniform mixing. The mixture of LaC13 on HEZ-55 was filtered out of solution, dried at 1100C. for 16 hours, followed by calcination at 5000C for 16 hours. The rare earth metal chloride-zeolite catalyst contained eight percent (8%) by weight of La metal as analyzed by X-Ray flouresence. The procedure was essentially repeated using HFZ-20 zeolite and HFZ-33 zeolite in place of HE5-55 zeolite, and varying the amount of LaC13 impregnated onto the zeolites. If and when additional, optional metals were added, such as lithium, potassium, magnesium, or strontium, these metals were also added as metal chloride salts in aqueous solution and were added simultaneously with the LaC13. Conditions of drying and calcination were essentially the same in all catalyst preparations, except as expressly stated below. Examples of the catalysts of the invention, prepared as described above, are: 8% LaC1 on HFZ-33; 8% LaC13, 48 LiCl on HFZ-33; 16% Lacy3 on HFZ-33; 16t LaC13 on EFZ-55; 8% LaC13, 48 KC1 on HFZ-55; 8% LaC13, 4% MgCl2 on HFZ-20; and 8% LaC13, 48 SrCl2 on HFZ-20. Experiments A series of experiments were conducted using a laboratory reactor comprising a 30 mm diameter by 45 cm. long glass reactor made of pyrex. The catalyst was placed in the reactor and the process was conducted as a one-pass, continuous fluid bea catalytic process. The reactor was first purged with nitrogen gas, followed by introduction of EDC and oxygen las air). The exit gases were collected and periodic samples were analyzed for EDC, VCM, HCl and other products using a gas chromotograph, Model No. 810 made by Bewlett-Packard and using DC-200 as a packing material. The following examples show data that was obtained using the above-described apparatus and at the oxygen/EDC molar ratios, temperatures, and contact times as indicated, operating at a pressure of about 30 psi (2 kilograms/centimeter2; 1,000,000 pascals). Mol% Conversion of EDC was determined using the formula 1- milimoles EDC out x 100 millimoles EDC feed in and % yield cf VACS, carbon oxides, and other products were determined as using the formula milimoles product out x 100 EDC conversion Example 1 This example compares the use of zeolite alone (Z) as a catalyst versus the use of the following catalysts of the invention; (A) a catalyst of 8% LaC13 on zeolite (B) 8% LaC13, 4% LiCl on zeolite; and (C) 16% LaC13 on zeolite. The zeolite used was HFZ-33. Run 02/EDC Contact Temperature Mole% % Yield Ratio Time(Sec) (OC) Conv.EDC VCM CO+C02 Z1 0.26 17.3 250 12.9 61.7 31.1 2 0.26 15.8 300 23.5 58.4 38.7 3 0.21 11.5 300 13.5 61.9 38.1 Al 0.29 13.9 300 51.8 78.1 20.7 2 0.20 10.9 300 35.8 90.1 9.2 3 0.20 15.7 300 35.7 83.2 15.5 B1 0.29 15.2 250 32.8 48.1 33.3 2 0.20 11.9 250 14.5 60.0 20.3 3 0.20 10.9 300 41.3 68.7 21.9 C1 0.29 15.2 250 10.6 64.1 33.4 2 0.29 13.9 300 24.9 57.0 41.4 3 0.20 10.9 300 12.5 59.9 38.2 As can be seen from the data, the use of a catalyst of a rare earth metal chloride on zeolite results in significantly higher EDC conversion. The level of 16% LaC13 has exceeded the optimum concentration on the HFZ-33 zeolite. Example 5 shows a level of 16% LaC13 on HFZ-55. Example 2 The following data is from runs using a catalyst of (A) 8% LaC13 on HFZ-33 and (B) 8% LaC13, 4% LiCl on HFZ-33, Run O2/EDC Contact Temperature Mole% 9s Yield Ratio Time(Sec) (OC) Conv.EDC VCM CO+C02 A 1 0.29 5.2 250 16.6 91.1 9.1 .2 0.29 4.8 300 37.7 86.9 13.1 3 0.20 10.9 300 35.8 90.1 9.2 4 0.20 15.7 300 38.9 83.3 15.4 B 1 0.29 15.2 250 32.8 48.1 34.3 2 0.29 13.9 300 50.2 59.6 33.0 3 0.20 10.9 300 41.3 68.7 21.9 4 0.20 15.7 300 42.2 65.4 24.8 Example 3 The example shows the use of catalysts of (A) 8% LaC13, 44 MgCl2 on HFZ-20 and (B) 8% LaCl3, 4% SrCl2 on HFZ-20. Run 02/EDC Contact Temperature Mole% % Yield Ratio Time(Sec) ( C) Conv.EDC VCM CO+C02 A 1 0.29 15.2 250 28.8 46.8 41.6 2 0.20 5.8 300 12.0 60. 30.3 3 0.20 10.9 300 25.4 69.0 29.9 4 0.20 26.1 300 63.9 60.0 30.4 B 1 0.29 15.2 250 35.1 36.7 57.7 2 0.20 17.2 250 11.7 65.0 30.7 3 0.29 13.9 300 31.3 52.5 44.6 4 0.20 15.7 300 25.3 54.1 42.6 5 0.20 10.9 300 20.5 63.4 33.2 6 0.20 6.9 300 17.7 73.0 26.0 Example 4 The data shows the use of a catalyst of 8% LaC13 on HFZ-33 calcined at (a) 7000C. and (b) 900"C. Run 02/EDC Contact Temperature Mole% % Yield Ratio Time(Sec) (OC) Conv.wDC VCM CO+C02 a 1 0.29 15.2 250 29.9 56.5 39.8 2 0.29 13.9 300 42.5 63.8 33.3 3 0.20 17.2 250 13.8 80.5 19.3 4 0.20 15.7 300 36.3 71.9 26.4 5 0.20 26.1 300 45.6 62.1 27.4 b 1 0.29 15.2 250 2.7 56.6 40.9 2 0.29 13.9 300 11.5 50.6 45.2 3 0.20 17.2 250 4.7 62.2 26.6 0.20 15.7 300 8.1 48.2 46.1 5 0.20 26.1 300 20.3 52.7 44.1 The data shows that the catalyst calcined at 7000C. is a more effective catalyst, particularly at higher EDC cracking temperatures. Example 5 The following data is from runs using a catalyst of 16% Lacy3 on HFZ-55. Run 02/EDC Contact Temperature Mole% % Yield Ratio Time(Sec) (OC) Conv.EDC VCM CO+C02 1 0.29 15.2 250 22.1 71.9 24.5 2 0.20 17.2 250 16.8 65.1 26.1 3 0.20 28.6 250 26.8 56.0 37.5 4 0.29 13.9 300 27.9 52.5 42.4 5 0.20 26.1 300 23.8 55.9 36.6 6 0.2f 15.7 300 34.9 61.2 33.0 7 Q.2t 8.4 300 18.7 73.9 22.1 8 0.20 5.8 300 17.0 81.8 15.2 The data shows that higher conversions of EDC were obtained at 3000C. than 2500C. and that a contact time of about 15 seconds gave the best results

Claims: CLAIMS 1. In a process of dehydrohalogenation of ethylene chloride to vinyl chloride at elevated temperatures in the presence of oxygen, the improvement which comprises the use as a catalyst of a composition of a rare earth metal chloride deposited on a zeolite. 2. A process of Claim 1 wherein the temperature of the reaction is from about 1500C. to about 5000C. at a pressure from about 1 to about 20 atmospheres (1 - 21 kilograms/centimeter2; 101,400 - 2,070,000 pascals). 3. A process of Claim 2 wherein the catalyst contains from about G.1% to about 30% by weight, based on the total weight of the catalyst of a chloride of the rare earth metal group consisting of Lanthanum, Proseodymium, Neodymium, and mixtures thereof. 4. A process of Claim 3 where the catalyst contains a solid synthetic zeolite having a pore opening of above SA. 5. A process of Claim 4 wherein the catalyst employed contains Lanthanum chloride at from about 4% to about 16% by weight of the total weight of the catalyst. 6. A process of Claim 1 wherein the oxygen is present in from about 0.05 mole to about 0.5 mole per mole of ethylene dichloride. 7. A process for the production of vinyl chloride monomer comprising (a) the dehydrohalogenation of ethylene chloride in the presence of (i) from about 0.05 mole to about 0.5 mole of oxygen per mole of ethylene dichloride and (ii) a catalyst comprising from about 29 to about 20% by weight, based on the total weight of the catalyst, of z rare earth metal chloride on a zeolite, at a temperature from about 15Q C. to about 5000C. at a pressure of from about atmospheric to about 20 atmospheres and (b) the recovery and recycle of the hydrogen chloride by-product into an oxyhydrochlorination reaction zone.

Inventors: MAGISTRO, ANGELO JOSEPH
Applicants: THE B.F. GOODRICH COMPANY
Application year: 1985
Main classification: C07C17
IPC codes: C07C21, C07C17, C07C67, B01J29, C07B61