DEWAXING CATALYSTS AND PROCESSES EMPLOYING NON-ZEOLITIC MOLECULAR SIEVES

Abstract: Dewaxing processes for hydrocarbon feedstocks are disclosed using novel catalysts comprising non-zeolitic molecular sieves, such as the silicoaluminophosphates of U.S. Patent No. 4,440,871. The products of the instant dewaxing processes are characterized by lower pour points than the hydrocarbon feedstock.

Description: The present invention relates to dewaxing and hydrodewaxing catalysts comprising non-zeolitic molecular sieves, as hereinafter described and to processes employing such catalysts. Dewaxing and hydrodewaxing processes are employed in the refining industry to treat petroleum fractions having initial boiling points over about 176.7°C to improve their pour point. The improvement in pour point is generally effected by selective removal of paraffinic hydrocarbons. Since the pour point of liquid hydrocarbon fuels, e.g., diesel fuels and other light gas oil fractions, are strictly controlled, the pour points specification of such fuels must be met if such are to be employed in their intended use. The need to reduce the pour point of petroleum fractions has resulted in the development of numerous dewaxing and hydrodewaxing processes wherein the pour points of petroleum fractions are reduced by selective removal of paraffinic hydrocarbons. Processes relating to dewaxing and hydrodewaxing are well known in both the patent and scientific literature. Such processes have employed crystalline aluminosilicates as catalysts. For example, see U.S. Patent Nos. 3,140,249, 3,140,252, 3,140,251, 3,140,253, 3,956,102 and 4,440,991. These and other patents disclose the use of various crystalline aluminosilicates as catalysts for dewaxing processes. Although a large number of zeolite materials have been disclosed as employable as catalysts for dewaxing and hydrodewaxing catalysts, the use of crystalline non-zeolitic molecular sieves has not received significant attention. This lack of attention is attributable to the scarcity of molecular sieves other than crystalline aluminosilcates. One disclosure of a catalyst containing a crystalline silicate, as opposed to a crystalline aluminosilicate, is disclosed in U.S. Patent No. 4,441,991. The instant invention provides for catalytic dewaxing and hydrodewaxing of hydrocarbon feedstocks by contacting such with catalysts comprising non-zeolitic molecular sieves, as hereinafter described. The present invention relates to catalytic dewaxing and hydrodewaxing (hereinafter jointly referred to as "dewaxing") processes and the catalysts employed in such processes. The catalysts comprise: 1) at least one non-zeolitic molecular sieve, as hereinafter described; and 2) optionally, and in the instance of hydrodewaxing at least one hydrogenation component; and 3) optionally, particles of a traditional dewaxing catalyst having catalytic activity for dewaxing and/or hydrodewaxing hydrocarbon feedstocks at effective dewaxing conditions, e.g., particles of a traditional dewaxing catalyst containing a zeolitic aluminosilicate(s) of the type generally employed in such dewaxing catalysts. The non-zeolitic molecular sieves employed in the instant invention, i.e., catalysts and processes, are characterized in their calcined form by an adsorption of isobutane of at least 2 percent by weight at a partial pressure of 0.67 bar and a temperature of 20°C. The traditional dewaxing catalyst component, e.g., a zeolitic aluminosilicate, if any, is characterized as being a dewaxing catalyst component, such as heretofore traditionally employed in hydroprocessing processes, e.g., the various forms of zeolite Y, silica-alumina, and hydrogenation components. The non-zeolitic molecular sieves employed in this invention are unique in that such are not zeolitic aluminosilicates, as heretofore employed in the prior art, but are specific non-zeolitic molecular sieves, as hereinafter described. Dewaxing and hydrodewaxing processes involve converting high boiling and high pour point paraffinic waxes and hydrocarbons into lower boiling lower pour point products. Further, hydrodewaxing involves hydrogenating unsaturates in the product. The term "dewaxing" is employed herein to generally mean the removal of hydrocarbons which readily solidify from petroleum stocks as waxes and includes catalytic dewaxing and hydrodewaxing. The catalysts of the instant invention have been observed to convert normal paraffins in the hydrocarbon products and, accordingly, reduce the pour point of such products, i.e., act as dewaxing catalysts. This reduction in the pour point by selective normal paraffin conversion is of commercial significance since distillate products have rigid specifications on the acceptable pour point. The non-zeolitic molecular sieves employed in the instant invention are selected from the hereinafter described group of non-zeolitic molecular sieves consisting of CoAPSOs, FeAPSOs, MgAPSOs, MnAPSOs, TiAPSOs, ZnAPSOs, CoMnAPSOs, CoMgAPSOs, CoMnMgAPSOs, MeAPOs, TiAPOs, FeAPOs, ELAPOs and mixtures thereof having an adsorption of isobutane in its calcined form of at least 2 percent by weight at a partial pressure of 0.67 bar and a temperature of 20°C. The non-zeolitic molecular sieves are preferably also characterized in their calcined form by an adsorption of triethylamine of from zero to less than 5 percent by weight, preferably less than 3 percent by weight, at a partial pressure of 3.46 mbar and a temperature of 22°C. The term "non-zeolitic molecular sieves" or "NZ-MS" is defined in the instant invention to include the "ELAPSO" molecular sieves as disclosed in EP-A 0 159 624 and certain "MeAPO", "FeAPO", "TiAPO" and "FCAPO" molecular sieves. Crystalline metal aluminophosphates (MeAPOs where "Me" is at least one of Mg, Mn, Co and Zn) are disclosed in EP-A 0 132 708; crystalline ferroaluminophosphates (FeAPOs) are disclosed in EP-A 0 131 946; titanium aluminophosphates (TiAPOs) are disclosed in EP-A 0 121 232; and non-zeolitic molecular sieves ("ELAPO") are disclosed in EP-A 0 158 349. Reference to figures in the description of the NZ-MSs is to the figures in said copending applications. The aforementioned copending applications are incorporated herein by reference thereto. "ELAPSO" molecular sieves are described in EP-A 0 159 624 as crystalline molecular sieves having three-dimensional microporous framework structures of ELO₂, AlO₂, PO₂, SiO₂, oxide units and having an empirical chemical composition on an anhydrous basis expressed by the formula: mR: (EL w Al x P y Si z )O₂ wherein "R" represents at least one organic templating agent present in the intracrystalline pore system; "m" represents the molar amount of "R" present per mole of (EL w Al x P y Si z )O₂ and has a value of from zero to about 0.3; "EL" represents at least one element capable of forming a three dimensional oxide framework, "EL" is characterized as an element having a mean "T-O" distance in tetrahedral oxide structures between about 0.151 nm and about 0.206 nm "EL" has a cation electronegativity between 523 kj/mol to 1298 kj/mol and "EL" is capable of forming stable M-O-P, M-O-Al or M-O-M bonds in crystalline three dimensional oxide structures having a "M-O" bond dissociation energy greater than about 247 kj/mol at 298 K; and "w", "x", "y" and "z" represent the mole fractions of "EL", aluminum, phosphorus and silicon, respectively, present as framework oxides said mole fractions being within the pentagonal compositional area defined by points A, B, C, D and E of FIG. 1. where A, B, C, D and E are: Point Mole Fraction x y (z+w) A 0.60 0.39-(0.01)p 0.01(p+1) B 0.39-(0.01p) 0.60 0.01(p+1) C 0.01 0.60 0.39 D 0.01 0.01 0.98 E 0.60 0.01 0.39 where "p" is an integer corresponding to the number of elements "El" in the (El w Al x P y Si z )O₂ constituent. The "ELAPSO" molecular sieves are also described as crystalline molecular sieves having three-dimensional microporous framework structures of ELO₂, AlO₂, SiO₂ and PO₂ tetrahedral oxide units and having an empirical chemical composition on an anhydrous basis expressed by the formula: mR: (EL w Al x P y Si z )O₂ wherein "R" represents at least one organic templating agent present in the intracrystalline pore system; "m" represents the molar amount of "R" present per mole of (EL w Al x P y Si z )O₂ and has a value of from zero to about 0.3; "EL" represents at least one element capable of forming a framework tetrahedral oxide and is selected from the group consisting of arsenic, beryllium, boron, chromium, cobalt, gallium, germanium, iron, lithium, magnesium, manganese, titanium, vanadium and zinc; and "w", "x", "y" and "z" represent the mole fractions of "EL", aluminum, phosphorus and silicon, respectively, present as tetrahedral oxides said mole fractions being within the tetragonal compositional area defined by points a, b, c and d of FIG. 1 where a, b, c and d are:. Point Mole Fraction x y (z+w) a 0.60 0.39-(0.01)p 0.01(p+1) b 0.39-(0.01p) 0.60 0.01(p+1) c 0.10 0.55 0.35 d 0.55 0.10 0.35 where "p" is as above defined. The "ELAPSO" molecular sieves include numerous species which are intended herein to be within the scope of the term "non-zeolitic molecular sieves" such being disclosed in the following copending and commonly assigned applications, incorporated herein by reference thereto: EP-publication No. Filed NZ-MS EP-A-161489 April 11, 1985 CoAPSO EP-A-161491 April 11, 1985 FeAPSO EP-A-158348 April 11, 1985 MgAPSO EP-A-161490 April 11, 1985 MnAPSO EP-A-161488 April 11, 1985 TiAPSO EP-A-158975 April 11, 1985 ZnAPSO EP-A-158350 April 11, 1985 CoMgAPSO CoMnMgAPSO TiAPSO Molecular Sieves The TiAPSO molecular sieves of EP-A-161488 filed April 11, 1985 have three-dimensional microporous framework structures of TiO₂, AlO₂, PO₂ and SiO₂ tetrahedral oxide units having an empirical chemical composition on an anhydrous basis expressed by the formula: mR : (Ti w Al x P y Si z )O₂ wherein "R" represents at least one organic templating agent present in the intracrystalline pore system; "m" represents the molar amount of "R" present per mole of (Ti w Al x P y Si z )O₂ and has a value of from zero to about 0.3; and "w", "x", "y" and "z" represent the mole fractions of titanium, aluminum, phosphorus and silicon, respectively, present as tetrahedral oxides and each has a value of at least 0.01. The mole fractions "w", "x", "y" and "z" are generally defined being within the pentagonal compositional area defined by points A, B, C, D and E of the ternary diagram of Fig. 1. Points A, B, C, D and E of Fig. 1 have the following values for "w", "x", "y", and "z": Point Mole Fraction x y (z+w) A 0.60 0.38 0.02 B 0.38 0.60 0.02 C 0.01 0.60 0.39 D 0.01 0.01 0.98 E 0.60 0.01 0.39 In a preferred subclass of TiAPSO molecular sieves the values "w", "x", "y" and "z" in the above formula are within the tetragonal compositional area defined by points a, b, c and d of the ternary diagram which is Fig. 2 of the drawings, said points a, b, c and d representing the following values for "w", "x", "y" and "z". Point Mole Fraction x y (z+w) a 0.55 0.43 0.02 b 0.43 0.55 0.02 c 0.10 0.55 0.35 d 0.55 0.10 0.35 TiAPSO compositions are generally synthesized by hydrothermal crystallization from a reaction mixture containing active resources of titanium, silicon, aluminum and phosphorus, and preferably an organic templating, i.e., structure-directing, agent, preferably a compound of an element or Group VA of the Periodic Table, and/or optionally an alkali or other metals. The reaction mixture is generally placed in a sealed pressure vessel, preferably lined with an inert plastic material such as polytetrafluoroethylene and heated, preferably under autogeneous pressure at a temperature between 50°C and 250°C, and preferably between 100°C and 200°C until crystals of the TiAPSO product are obtained, usually a period of from hours to several weeks. Generally, the crystallization time is from about 2 hours to about 30 days and typically from about 4 hours to about 20 days. The product is recovered by any convenient method such as centrifugation or filtration. In synthesizing the TiAPSO, it is preferred to employ a reaction mixture composition expressed in terms of the molar ratios as follows: aR : (Ti w Al x P y Si z )O₂ : bH₂O wherein "R" is an organic templating agent; "a" is the amount of organic templating agent "R" and has a value of from zero to about 6 and is preferably an effective amount within the range of greater than zero (0) to about 6; "b" has a value of from zero (0) to about 500, preferably between about 2 and about 300; and "w", "x", "y" and "z" represent the mole fractions of titanium, aluminum, phosphorus and silicon, respectively, and each has a value of at least 0.01. In a preferred embodiment the reaction mixture is selected such that the mole fractions "w", "x", "y" and "z" are generally defined as being within the pentagonal compositional area defined by points E, F, G, H and I of the ternary diagram of FIG. 3. Points E, F, G, H and I of FIG. 3 have the following values for "w", "x", "y" and "z"; Point Mole Fraction x y (z+w) F 0.60 0.38 0.02 G 0.38 0.60 0.02 H 0.01 0.60 0.39 I 0.01 0.01 0.98 J 0.60 0.01 0.39 In the foregoing expression of the reaction composition, the reactants are normalized with respect to the total of "w", "x", "y" and "z" such that (w + x + y + z) =1.00 mole . MgAPSO Molecular Sieves The MgAPSO molecular sieves of EP-A-158348, filed April April 11, 1985 have three-dimensional microporous framework structures of MgO -2 / 2, AlO - / 2, PO + / 2 and SiO₂ tetrahedral oxide units and have an empirical chemical composition on an anhydrous basis expressed by the formula: mR : (Mg w Al x P y Si z )O₂ wherein "R" represents at least one organic templating agent present in the intracrystalline pore system; "m" represents the molar amount of "R" present per mole of (Mg w Al x P y Si z )O₂ and has a value from zero (0) to about 0.3; and "w", "x", "y" and "z" represent the mole fractions of magnesium, aluminum, phosphorus and silicon, respectively, present as tetrahedral oxides and each preferably has a value of at least 0.01. The mole fractions "w", "x", "y" and "z" are generally defined as being within the pentagonal compositional area defined by points A, B, C, D and E of the ternary diagram of FIG. 1. Points A, B, C, D and E of FIG. 1 have the following values for "w", "x", "y" and "z": Point Mole Fraction x y (z+w) A 0.60 0.38 0.02 B 0.39 0.59 0.02 C 0.01 0.60 0.39 D 0.01 0.01 0.98 E 0.60 0.01 0.39 In a preferred subclass of the MgAPSO molecular sieves the values "w", "x", "y" and "z" in the above formula are within the tetragonal compositional area defined by the points a, b, c and d of the ternary diagram of FIG. 2, said points a, b, c and d representing the following values for "w", "x", "y" and "z": Point Mole Fraction x y (z+w) a 0.55 0.43 0.02 b 0.43 0.55 0.02 c 0.10 0.55 0.35 d 0.55 0.10 0.35 MgAPSO compositions are generally synthesized by hydrothermal crystallization for an effective time at effective pressures and temperatures from a reaction mixture containing reactive sources of magnesium, silicon, aluminum and phosphorus, an organic templating, i.e., structure-directing, agent, preferably a compound of an element or Group VA of the Periodic Table, and may be an alkali or other metal. The reaction mixture is generally placed in a sealed pressure vessel, preferably lined with an inert plastic material such as polytetrafluoroethylene and heated, preferably under autogeneous pressure at a temperature between 50°C and 250°C, and preferably between 100°C and 200°C until crystals of the MgAPSO product are obtained, usually a period of from several hours to several weeks. Generally, the crystallization period will be from 2 hours to 30 days with it typically being from 4 hours to 20 days for obtaining MgAPSO crystals. The product is recovered by any convenient method such as centrifugation or filtration. In synthesizing the MgAPSO compositions, it is preferred to employ reaction mixture compositions expressed in terms of the molar ratios as follows: aR : (Mg w Al x P y Si z )O₂ : bH₂O wherein "R" is an organic templating agent; "a" is the amount of organic templating agent "R" and is preferably an effective amount greater than zero to 6; "b" has a value of from zero (0) to 500, preferably between 2 and 300; and "w", "x", "y" and "z" represent the mole fractions of magnesium, aluminum, phosphorus and silicon, respectively, and each has a value of at least 0.01. In a preferred embodiment the reaction mixture is selected such that the mole fractions "w", "x", "y" and "z" are generally defined as being within the pentagonal compositional area defined by points F, G, H, I and J of the ternary diagram of FIG. 3. Points F, G, H, I and J of FIG. 3 have the following values for "w", "x", "y" and "z". Point Mole Fraction x y (z+w) F 0.60 0.38 0.02 G 0.38 0.60 0.02 H 0.01 0.60 0.39 I 0.01 0.01 0.98 J 0.60 0.01 0.39 In the foregoing expression of the reaction composition, the reactants are normalized with respect to the total of "w", "x", "y" and "z" such that (w+x+y+z) = 1.00 mole . MnAPSO Molecular Sieves The MnAPSO molecular sieves of EP-A-161490, filed April 11, 1985 have a framework structure of MnO -2 / 2, AlO - / 2, PO + / 2, and SiO₂ tetrahedral units having an empirical chemical composition on an anhydrous basis expressed by the formula: mR : (Mn w Al x P y Si z )O₂ wherein "R" represents at least one organic templating agent present in the intracrystalline pore system; "m" represents the molar amount of "R" present per mole of (Mn w Al x P y Si z )O₂ and has a value of zero to about 0.3; and "w", "x", "y" and "z" represent the mole fractions of element manganese, aluminum, phosphorus and silicon, respectively, present as tetrahedral oxides. The mole fractions "w", "x", "y" and "z" are generally defined as being within the pentagonal compositional area defined by points A, B, C, D and E of the ternary diagram of FIG. 1 and more preferably are generally defined as being within the tetragonal compositional area defined by points a, b, c and d of the ternary diagram of FIG. 2. Points A, B, C, D and E of FIG. 1 have the following values for "w", "x", "y", and "z": Point Mole Fraction x y (w+z) A 0.60 0.38 0.02 B 0.38 0.60 0.02 C 0.01 0.60 0.39 D 0.01 0.01 0.98 E 0.60 0.01 0.39 W Points a, b, c, and d of FIG. 2 have the following values for "w", "x", "y". and "z": Point Mole Fraction x y (w+z) a 0.55 0.43 0.02 b 0.43 0.55 0.02 c 0.10 0.55 0.35 d 0.55 0.10 0.35 The MnAPSOs of this invention are useful as adsorbents, catalysts, ion-exchangers, and the like in much the same fashion as aluminosilicates have been employed heretofore, although their chemical and physical properties are not necessarily similar to those observed for aluminosilicates. MnAPSO compositions are generally synthesized by hydrothermal crystallization from a reaction mixture containing reactive sources of manganese, silicon, aluminum and phosphorus, preferably an organic templating, i.e., structure-directing, agent, preferably a compound of an element or Group VA of the Periodic Table, and/or optionally an alkali or other metal. The reaction mixture is generally placed in a sealed pressure vessel, preferably lined with an inert plastic material such as polytetrafluoroethylene and heated, preferably under autogeneous pressure at a temperature between 50°C and 250°C, and preferably between 100°C and 200°C until crystals of the MnAPSO product are obtained, usually a period of from several hours to several weeks. Typical effective times of from 2 hours to 30 days with generally from 4 hours to 20 days have been observed. The product is recovered by any convenient method such as centrifugation or filtration. In synthesizing the MnAPSO compositions, it is preferred to employ a reaction mixture composition expressed in terms of the molar ratios as follows: aR : (Mn w Al x P y Si z )O₂ : bH₂O wherein "R" is an organic templating agent; "a" is the amount of organic templating agent "R" and is preferably an effective amount within the range of greater than zero (0) to 6; "b" has a value of from zero (0) to 500, preferably between 2 and 300; and "w", "x", "y" and "z" represent the mole fractions of manganese, aluminum, phosphorus and silicon, respectively, and each has a value of at least 0.01. In a preferred embodiment the reaction mixture is selected such that the mole fractions "w", "x", "y" and "z" are generally defined as being within the pentagonal compositional area defined by points E, F, G, H and I of the ternary diagram of FIG. 3. Points E, F, G, H and I of FIG. 3 have the following values for "w", "x", "y" and "z": Point Mole Fraction x y (w+z) F 0.60 0.38 0.02 G 0.38 0.60 0.02 H 0.01 0.60 0.39 I 0.01 0.01 0.98 J 0.60 0.01 0.39 In the foregoing expression of the reaction composition, the reactants are normalized with respect to the total of "w", "x", "y" and "z" such that (w+x+y+z) = 1.00 mole. CoAPSO Molecular Sieves The CoAPSO molecular sieves of EP-A-161489, filed April 11, 1985 have three-dimensional microporous framework structures of CoO -2 / 2, AlO - / 2, PO + / 2 and SiO₂ tetrahedral units and have an empirical chemical composition on an anhydrous basis expressed by the formula: mR : (Co w Al x P y Si z )O₂ wherein "R" represents at least one organic templating agent present in the intracrystalline pore system; "m" represents the molar amount of "R" present per mole of (Co w Al x P y Si z )O₂ and has a value of from zero to about 0.3; and "w", "x", "y" and "z" represent the mole fractions of cobalt, aluminum, phosphorus and silicon, respectively, present as tetrahedral oxides, where the mole fractions "w", "x", "y" and "z" are each at least 0.01 and are generally defined, as being within the pentagonal compositional area defined by points A,B, C, D and E of FIG. 1, said points A, B, C, D, and E having the following values for "w", "x", "y" and "z": Point Mole Fraction x y (z + w) A 0.60 0.38 0.02 B 0.38 0.60 0.02 C 0.01 0.60 0.39 D 0.01 0.01 0.98 E 0.60 0.01 0.39 In a preferred subclass of the CoAPSO molecular sieves the values of "w", "x", "y", and "z" in the above formula are within the tetragonal compositional area defined by points a, b, c, and d, of FIG. 2, said points a, b, c, and d having the following values for "w", "x", "y" and "z": Point Mole Fraction x y (z + w) a 0.55 0.43 0.02 b 0.43 0.55 0.02 c 0.10 0.55 0.35 d 0.55 0.10 0.35 CoAPSO compositions are generally synthesized by hydrothermal crystallization from a reaction mixture containing reactive sources of cobalt, silicon, aluminum and phosphorus, an organic templating, i.e., structure-directing, agent, preferably a compound of an element of Group VA of the Periodic Table, and optionally an alkali metal. The reaction mixture is generally placed in a sealed pressure vessel, preferably lined with an inert plastic material such as polytetrafluoroethylene and heated, preferably under autogeneous pressure at an effective temperature which is generally between 50°C and 250°C and preferably between 100°C and 200°C until crystals of the CoAPSO product are obtained, usually for an effective time of from several hours to several weeks. Generally the effective crystallization time will be from 2 hours to 30 days and typically from 4 hours to 20 days. The product is recovered by any convenient method such as centrifugation or filtration. In synthesizing the CoAPSO, it is preferred to employ a reaction mixture composition expressed in terms of the molar ratios as follows: aR : (Co w Al x P y Si z )O₂ : bH₂O wherein "R" is an organic templating agent; "a" is the amount of organic templating agent "R" and is preferably an effective amount within the range of greater than zero (0) to 6; "b" has a value of from zero (0) to 500, preferably between 2 and 300; and "w", "x", "y" and "z" represent the mole fractions of cobalt, aluminum, phosphorus and silicon, respectively, and each has a value of at least 0.01. In a preferred embodiment the reaction mixture is selected such that the mole fractions "w", "x", "y" and "z" are generally defined as being within the pentagonal compositional area defined by points E, F, G, H and I of the ternary diagram of FIG. 3. Points E, F, G, H and I of FIG. 3 have the following values for "w", "x", "y" and "z": Point Mole Fraction x y (z + w) F 0.60 0.38 0.02 G 0.38 0.60 0.02 H 0.01 0.60 0.39 I 0.01 0.01 0.98 J 0.60 0.01 0.39 For reasons unknown at present, not every reaction mixture gave crystalline CoAPSO products when reaction products were examined for CoAPSO products by X-ray analysis. Those reaction mixtures from which crystalline CoAPSO products were obtained are reported in the examples hereinafter as numbered examples and those reaction mixtures from which CoAPSO products were not identified by use of X-ray analysis are reported as lettered examples. In the foregoing expression of the reaction composition, the reactants are normalized with respect to the total of "w", "x", "y" and "z" such that (w+x+y+z) = 1.00 mole . ZnAPSO Molecular Sieves The ZnAPSO molecular sieves of EP-A-158975, filed April 11, 1985 comprise framework structures of ZnO -2 / 2, AlO - / 2, PO + / 2 and SiO₂ tetrahedral units having an empirical chemical composition on an anhydrous basis expressed by the formula: mR : (Zn w Al x P y Si z )O₂ wherein "R" represents at least one organic templating agent present in the intracrystalline pore system; "m" represents the molar amount of "R"present per mole of (Zn w Al x P y Si z )O₂ and has a value of zero to about 0.3; and "w", "x", "y" and "z" represent the mole fractions of zinc, aluminum, phosphorus and silicon, respectively, present as tetrahedral oxides and each has a value of at least 0.01. The mole fractions "w", "x", "y" and "z" are generally defined being within the pentagonal compositional area defined by points A, B, C, D and E of the ternary diagram of Fig. 1. Points A, B, C, D and E of Fig. 1 have the following values for "w", "x", "y", and "z": Point Mole Fraction x y (z + w) A 0.60 0.38 0.02 B 0.38 0.60 0.02 C 0.01 0.60 0.39 D 0.01 0.01 0.98 E 0.60 0.01 0.39 In a preferred subclass of ZnAPSO molecular sieves the values "w", "x", "y" and "z" in the above formula are within the tetragonal compositional area defined by points a, b, c and d of the ternary diagram which is Fig. 2 of the drawings, said points a, b, c and d representing the following values for "w", "x", "y" and "z" Point Mole Fraction x y (z + w) a 0.55 0.43 0.02 b 0.43 0.55 0.02 c 0.10 0.55 0.35 d 0.55 0.10 0.35 ZnAPSO compositions are generally synthesized by hydrothermal crystallization at effective process conditions from a reaction mixture containing active sources of zinc, silicon, aluminum and phosphorus, preferably an organic templating, i.e., structure-directing, agent, preferably a compound of an element or Group VA of the Periodic Table, and/or optionally an alkali or other metal. The reaction mixture is generally placed in a sealed pressure vessel, preferably lined with an inert plastic material such as polytetrafluoroethylene and heated, preferably under autogeneous pressure at a temperature between 50°C and 250°C, and preferably between 100°C and 200°C until crystals of the ZnAPSO product are obtained, usually a period of from several hours to several weeks. Generally the effective crystallization period is from 2 hours to 30 days with typical periods of from 4 hours to 20 days being employed to obtain ZnAPSO products. The product is recovered by any convenient method such as centrifugation or filtration. In synthesizing the ZnAPSO compositions, it is preferred to employ a reaction mixture composition expressed in terms of the molar ratios as follows: aR : (Zn w Al x P y Si z )O₂ : bH₂O wherein "R" is an organic templating agent; "a" is the amount of organic templating agent "R" and is preferably an effective amount within the range of greater than zero (0) to 6; "b" has a value of from zero (0) to 500, more preferably between 2 and 300; and "w", "x", "y" and "z" represent the mole fractions of zinc, aluminum, phosphorus and silicon, respectively, and each has a value of at least 0.01. In a preferred embodiment the reaction mixture is selected such that the mole fractions "w", "x", "y" and "z" are generally defined as being within the pentagonal compositional area defined by points F, G, H, I and J of the ternary diagram of FIG. 3. Points F, G, H, I and J of FIG. 3 have the following values for "w", "x", "y" and "z": Point Mole Fraction x y (z + w) F 0.60 0.38 0.02 G 0.38 0.60 0.02 H 0.01 0.60 0.39 I 0.01 0.01 0.98 J 0.60 0.01 0.39 In the foregoing expression of the reaction composition, the reactants are normalized with respect to the total of "w", "x", "y" and "z" such that (w+x+y+z) = 1.00 mole . FeAPSO Molecular Sieves The FeAPSO of EP-A-161 491, filed April 11, 1985 are molecular sieves having a three-dimensional microporous crystal framework structures of FeO -2 / 2, (and/or FeO - / 2), AlO - / 2, PO + / 2 and SiO₂ tetrahedral oxide units and having a unit empirical formula, on an anhydrous basis, of: mR: (Fe w Al x P y Si z )O₂ (1) wherein "R" represents at least one organic templating agent present in the intracrystalline pore system; "m" represents the moles of "R" present per mole of (Fe w Al x P y Si z )O₂ and has a value of from zero (0) to about 0.3; the maximum value of "m" in each case depends upon the molecular dimensions of the templating agent and the available void volume of the pore system of the particular molecular sieve involved; and "w", "x", "y" and "z" represent the mole fractions of iron, aluminum, phosphorus and silicon, respectively, present as tetrahedral oxides, said mole fractions being such that they are within the pentagonal compositional area defined by points A, B, C, D and E of the ternary diagram which is FIG. 1 of the drawings and more preferably are within the tetragonal compositional area defined by points a, b, c, and d of the ternary diagram which is FIG. 2 of the drawings. Points A, B, C, D and E of FIG. 1 represent the following values for "w", "x", "y" and "z": Point Mole Fraction x y (z + w) A 0.60 0.38 0.02 B 0.38 0.60 0.02 C 0.01 0.60 0.39 D 0.01 0.01 0.98 E 0.60 0.01 0.39 Points a, b, c and d of FIG. 2 represent the following values for "w", "x", "y" and "z": Point Mole Fraction x y (z + w) a 0.55 0.43 0.02 b 0.43 0.55 0.02 c 0.10 0.55 0.35 d 0.55 0.10 0.35 The FeAPSOs of the instant invention are generally synthesized by hydrothermal crystallization from a reaction mixture comprising reactive sources of iron, aluminum, phosphorus and silicon, and preferably one or more organic templating agents. Optionally, alkali or other metal(s) may be present in the reaction mixture and may act as templating agents. The reaction mixture is generally placed in a pressure vessel, preferably lined with an inert plastic material, such as polytetrafluoroethylene, and heated, preferably under the autogeneous pressure, at an effective temperature which is generally between 50°C, and 250°C and preferably between 100°C and 200°C until crystals of the FeAPSO product are obtained, usually a period of from several hours to several weeks. CoMnAPSO Molecular Sieves The expressed by the empirical chemical formula (anhydrous): mR : (Co u Mn v Al x P y Si z )O₂ where "u", "v", "x", "y" and "z" represent the mole. The CoMnAPSO molecular sieves have an empirical chemical composition on an anhydrous basis expressed by the formula: mR : (Co u Mn v Al x P y Si z )O₂ wherein "R" represents at least one organic templating agent present in the intracrystalline pore system; "m" represents the molar amount of "R" present per mole of (Co u Mn v Al x P y Si z )O₂ from zero (0) to about 0.3; and "u", "v", "x" "y" and "z" represent the mole fractions of cobalt, manganese, aluminum, phosphorus and silicon, respectively, present as tetrahedral oxides. The mole fractions "u", "v", "x", "y", and "z" are generally defined as being within the pentagonal compositional area defined by points A, B, C, D and E of FIG. 1, where "w" is the sum of "u" and "v" and where "M w " in FIG. 1 represents the combined mole fractions of cobalt and manganese: Point Mole Fraction x y (z + w) A 0.60 0.37 0.03 B 0.37 0.60 0.03 C 0.01 0.60 0.39 D 0.01 0.01 0.98 E 0.60 0.01 0.39 The mole fractions u, v, x, y and z, expressed as in FIG. 1, are preferably defined as being within the tetragonal compositional area defined by points a, b, c and d of FIG. 2 as follows: Mole Fraction x y (z + w) a 0.55 0.42 0.03 b 0.42 0.55 0.03 c 0.10 0.55 0.35 d 0.55 0.10 0.35 CoMnAPSO compositions are generally synthesized by hydrothermal crystallization from a reaction mixture containing reactive sources of cobalt, manganese, aluminum, phosphorus and silicon and preferably an organic templating agent, i.e., structure- directing, agent. The structure-directing agents are preferably a compound of an element of Group VA of the Periodic Table, and may be an alkali or other metal. The reaction mixture is generally placed in a sealed pressure vessel, preferably lined with an inert plastic material such as polytetrafluoroethylene and heated, preferably under autogeneous pressure and at typical effective temperatures between 50°C and 250°C, preferably between 100°C and 200°C, until crystals of the CoMnAPSO product are obtained, usually over a period of from several hours to several weeks. Typical effective crystallization times are from 2 hours to 30 days with from 4 hours to 20 days being generally employed to obtain CoMnAPSO products. The product is recovered by any convenient method such as centrifugation or filtration. In synthesizing the CoMnAPSO compositions, it is preferred to employ a reaction mixture composition expressed in terms of the molar ratios as follows: aR : (Co u Mn v Al x P y Si z )O₂ : bH₂O wherein "R" is an organic templating agent; "a" is the amount of organic templating agent "R" and is preferably an effective amount within the range of greater than zero (0) to 6; "b" has a value of from zero (0) to 500, preferably between 2 and 300; and "u", "v", "x", "y", and "z" represent the mole fractions of elements cobalt, manganese, aluminum, phosphorus and silicon, respectively, and each has a value of at least 0.01. In a preferred embodiment the reaction mixture is selected such that the mole fractions "v", "x", "y" and "z" are generally defined as being within the pentagonal compositional area defined by points E, F, G, H and I of the ternary diagram of FIG. 3. Points E, F, G, H, and I of FIG. 3 have the following values for "v", "x", "y" and "z"" Mole Fraction x y (z + w) F 0.60 0.37 0.03 G 0.37 0.60 0.03 H 0.01 0.60 0.39 I 0.01 0.01 0.98 J 0.60 0.01 0.39 In the foregoing expression of the reaction composition, the reactants are normalized with respect to the total of "u", "v", "x", "y" and "z" such that (u+v+x+y+z)=1.00 mole . CoMnMgAPSO Molecular Sieves The CoMnMgAPSO molecular sieves of EP-A-158 350, filed April 11, 1985 have three-dimensional microporous framework structures of CoO -2 / 2, MnO -2 / 2, MgO -2 / 2, AlO - / 2, PO + / 2 and SiO₂ tetrahedral oxide units and have an empirical chemical composition on an anhydrous basis expressed by the formula: mR : (Co t Mn u Mg v Al x P y Si z )O₂ wherein "R" represents at least one organic templating agent present in the intracrystalline pore system; "m" represents the molar amount of "R" present per mole of (Co t Mn u Mg v Al x P y Si z )O₂, and has a value of from zero to about 0.3; and "t", "u", "v", "x", "y" and "z" represent the mole fractions of cobalt, manganese, magnesium, aluminum, phosphorus and silicon, respectively, present as tetrahedral oxides, each having a value of at least 0.01. The mole fractions "t", "u", "v", "x", "y" and "z" are generally defined as being within the pentagonal compositional area defined by points A, B, C, D and E of FIG. 1 where "M" denotes cobalt, manganese and magnesium and "w" denotes the combined mole fractions of "t", "u" and "v", such that "w" = "t" + "u" + "v" and such that "t", "u" "v" and "z" each have a value of at least 0.01. Points A, B, C, D and E of FIG. 1 have the following values for "w", "x", "y" and "z": Point Mole Fraction x y (z + w) A 0.60 0.36 0.04 B 0.36 0.60 0.04 C 0.01 0.60 0.39 D 0.01 0.01 0.98 E 0.60 0.01 0.39 In a preferred subclass of the CoMnMgAPSO molecular sieves the values of "w", "x", "y" and "z" in the above formula are within the tetragonal compositional area defined by points a, b, c and d of Fig. 2. Points a, b, c and d have the following values for "w", "x", "y" and "z": Point Mole Fraction x y (z + w) a 0.55 0.41 0.04 b 0.41 0.55 0.04 c 0.10 0.55 0.35 d 0.55 0.10 0.35 The CoMnMgAPSOs of this invention are useful as adsorbents, catalysts, ion-exchangers, and the like in much the same fashion as aluminosilicates have been employed heretofore, although their chemical and physical properties are not necessarily similar to those observed for aluminosilicates. CoMnMgAPSO compositions are generally synthesized by hydrothermal crystallization from a reaction mixture containing reactive sources of cobalt, manganese, magnesium, aluminum, phosphorus and silicon, and preferably an organic templating agent, i.e., structure-directing, agent. The structure-directing agents are preferably a compound of an element of Group VA of the Periodic Table, and/or optionally an alkali or other metal. The reaction mixture is generally placed in a sealed pressure vessel, preferably lined with an inert plastic material such as polytetrafluoroethylene and heated, preferably under autogeneous pressure at a temperature between 50°C and 250°C, and preferably between 100°C and 200°C until crystals of the CoMnMgAPSO product are obtained, usually over a period of from several hours to several weeks. Typical crystallization times are from 2 hours to 30 days with from 4 hours to 20 days generally being employed to obtain CoMnMgAPSO products. The product is recovered by any convenient method such as centrifugation or filtration. In synthesizing the CoMnMgAPSO compositions, it is preferred to employ a reaction mixture composition expressed in terms of the molar ratios as follows: aR : (Co t Mn u Mg v Al x P y Si z )O₂ : bH₂O wherein "R" is an organic templating agent; "a" is the amount of organic templating agent "R" and is preferably an effective amount within the range of greater than zero (0) to 6 and more preferably from greater than zero to 2; "b" has a value of from zero (0) to 500, preferably between 2 and 300; and "t", "u", "v", "x", "y", and "z" represent the mole fractions of cobalt, manganese, magnesium, aluminum, phosphorus and silicon, respectively, and each has a value of at least 0.01. In a preferred embodiment the reaction mixture is selected such that the mole fractions "w", "x", "y" and "z", where "w" is the sum of "t" + "u" + "v", are generally defined as being within the pentagonal compositional area defined by points E, F, G, H and I of the ternary diagram of FIG. 3. Points E, F, G, H and I of FIG. 3 have the following values "w", "x", "y" and "z": Point Mole Fraction x y (z + w) F 0.60 0.36 0.04 G 0.36 0.60 0.04 H 0.01 0.60 0.39 I 0.01 0.01 0.98 J 0.60 0.01 0.39 In the foregoing expression of the reaction composition, the reactants are normalized with respect to the total of "t", "u", "v", "x", "y" and "z" such that (t + u + v + x + y + z) = 1.00 mole . NZ-MS CATALYSTS The specific NZ-MSs employed in the instant invention are characterized in their calcined form by an adsorption of isobutane of at least 2 percent by weight at a partial pressure of 0.67 bar and a temperature of 20°C. The NZ-MS's are preferably also characterized in their calcined form by an adsorption of triethylamine of from zero to less than 5 percent by weight, preferably less than 3 weight percent, at a partial pressure of 3.45 mbar and a temperature of 22°C. The NZ-MSs employed herein are characterized by the aforementioned adsorption criteria. Certain NZ-MS species which may be employed herein are designated in one or more of the aforementioned classes of NZ-MS by an "-n" designation of -5, -11, -31, -33, -36, -37, -40 and -41 to the extent such meet the aforementioned adsorption criteria. NZ-MSs characterized by the above described adsorption of isobutane include, but are not limited to, ELAPSO-5, ELAPSO-11, ELAPSO-40, ELAPSO-41, CoAPSO-5, CoAPSO-11, CoAPSO-31, FeAPSO-5, FeAPSO-11, FeAPSO-31, MgAPSO-11, MgAPSO-31, MnAPSO-11, MnAPSO-31, TiAPSO-11, ZnAPSO-11, ZnAPSO-31, CoMgAPSO-11, CoMnMgAPSO-11, MeAPO-5, MeAPO-11, MeAPO-31, TiAPO-11, TiAPO-31, FeAPO-11, ELAPO-11, ELAPO-31, ELAPO-40, ELAPO-41 and mixtures thereof. The above characterization of the NZ-MSs employed in the instant invention relates to an adsorption characterization that is carried out on a NZ-MS which has been subjected to a post synthesis treatment, e.g., calcination or chemical treatment, to remove a substantial portion of the template "R" which is present as a result of synthesis. Although a particular NZ-MS is characterized herein by reference to its adsorption of isobutane or triethylamine as relating to the adsorption characteristics of the NZ-MS in its calcined form, the instant invention necessarily includes the use of a non-calcined or modified NZ-MSs which are characterized by such adsorption in the modified or calcined form, since upon use of such a non-calcined NZ-MS in the instant process at effective dewaxing conditions the NZ-MS will be calcined or hydrothermally treated in situ so as to have the characteristic adsorption of isobutane or triethylamine. Thus, the NZ-MS will be rendered in situ to a form characterized by the aforementioned adsorption characteristics. For example, an as-synthesized MgAPSO-11 is not characterized by the aforementioned adsorption of isobutane due to the presence of template "R" which is present as a result of synthesis, although the calcined form of MgAPSO-11 is characterized by the aforementioned adsorption of isobutane. Thus, reference to a NZ-MS having a particular adsorption characteristic in its calcined form is not intended to exclude the use of the NZ-MS in its as-synthesized form which upon in-situ calcination, hydrothermal treatment and/or other treatment, e.g., ion exchange with suitable atoms, would have such adsorption characteristics. The NZ-MSs of the instant invention may be employed in conjunction with traditional dewaxing and/or hydrocracking catalysts and accordingly, optionally, a zeolitic aluminosilicate component may be employed in conjunction with the NZ-MS-containing catalysts. The zeolitic aluminosilicate component of such catalysts may be any aluminosilicate heretofore employed as a component in dewaxing catalysts. Representatives of the zeolitic aluminosilicates disclosed heretofore as employable as component parts of traditional dewaxing catalysts are Zeolite Y, steam stabilized Zeolite Y (ultra-stable Y), Zeolite X, Zeolite beta (U.S. Patent No. 3,308,069), Silicalite (U.S. Patent No. 4,061,724),, Zeolite KZ-20 (U.S. Patent No. 3,445,727), Zeolite ZSM-3 (U.S. Patent No. 3,415,736), faujasite, LZ-10 (U.K. Patent 2,014,970, June 9, 1982), US-Y, ZSM-type zeolites, erionite, mordenite, offretite, chabazite, FU-1-type zeolite, NU-type zeolities and mixtures thereof. Traditional cracking catalysts containing amounts of Na₂O less than about one percent by weight are generally preferred. Zeolite Y is disclosed in U.S. Patent Nos.: 3,130,007; and steam stabilized Y Zeolites, e.g., ultra-stable Y-type zeolites. Another zeolitic aluminosilicate employable herein is "LZ-210", is described in E.P.C. Publication No. 82,211 published June 29, 1983 incorporated herein by reference thereto. In one embodiment the LZ-210 containing hydrocracking catalysts disclosed in copending EP-A-124 120, filed April 28, 1984, incorporated herein by reference, may be employed as an optional component of the catalyst. The term "ZSM-type" zeolites is generally employed in the art to refer to those zeolites denominated by the nomenclature "ZSM-n" where "n" is an integer. The ZSM-type aluminosilicates include but are not limited to ZSM-5, ZSM-11, ZSM-12, ZSM-23, ZSM-35, ZSM-38, ZSM-48; and other similar materials. ZSM-5 is described in greater detail in U.S. Patent No. 3,702,886 and Re 29,948. The entire descriptions contained within those patents, particularly the X-ray diffraction pattern of therein disclosed ZSM-5, are incorporated herein by reference. ZSM-11 is described in U.S. Patent No. 3,709,979. That description, and in particular the X-ray diffraction pattern of said ZSM-11, is incorporated herein by reference. ZSM-12 is described in U.S. Patent No. 3,832,449. That description, and in particular the X-ray diffraction pattern disclosed therein, is incorporated herein by reference. ZSM-23 is described in U.S. Patent No. 4,076,842. The entire content thereof, particularly the specification of the X-ray diffraction pattern of the disclosed zeolite, is incorporated herein by reference. ZSM-35 is described in U.S. Patent No. 4,016,245. The description of that zeolite, and particularly the X-ray diffraction pattern thereof, is incorporated herein by reference. ZSM-38 is more particularly describing U.S. Patent No: 4,046,859. The description of that zeolite, and particularly the specified X-ray diffraction pattern hereof, is incorporated herein by reference. ZSM-48 is more particularly described in U.S. Patent No. 4,423,021. The description of that zeolite, and particularly the specified X-ray diffraction pattern thereof, is incorporated herein by reference. In addition, crystalline silicates such as silicalite (U.S.Patent No. 4,061,724) may be employed with the NZ-MSs of the instant invention. FORMULATION OF NZ-MS DEWAXING CATALYSTS The catalysts of the instant invention comprise at least one NZ-MS, as above characterized, and optionally, may also contain a hydrogenation catalyst and/or one or more traditional dewaxing catalysts and/or hydrocracking catalysts, including zeolitic aluminosilicate components. The relative amount of the NZ-MS component or traditional hydroprocessing component, if any, will depend at least in part, on the selected hydrocarbon feedstock and on the desired pour point of the product, but in all instances an effective amount of at least one NZ-MS is employed. When a zeolitic aluminosilicate is employed as a part of the traditional dewaxing component the relative weight ratio of the zeolitic aluminosilicate to the NZ-MS is generally between 1:10 and 500:1, desirably between 1:10 and 200:1, preferably between 1:2 and 50:1, and most preferably is between 1:1 and 20:1. The zeolitic aluminosilicate and NZ-MS may be ion-exchanged with a selected cation(s) and/or thermally treated either before or after mixture with each other or after such have been added separately or concurrently to one or more inorganic oxide matrix components. When the NZ-MS molecular sieves are ion exchanged such are preferably exchanged with a hydrogen-forming cation species, e.g. NH + / 4, H⁺, quaternary ammonium cations, etc. The NZ-MS preferably has at least part of its cations as hydrogen-forming cation species. Hydrodewaxing catalysts may optionally contain a hydrogenation component of the type commonly employed in dewaxing catalysts. The hydrogenation component may be selected from the group of hydrogenation catalysts consisting of one or more metals of Group VI B and Group VIII, including the salts, complexes and solutions containing such metals. The preferred hydrogenation catalyst is at least one of the group of metals, salts and complexes selected from the group consisting of at least one of platinum, palladium, rhodium, iridium and mixtures thereof or at least one from the group consisting of nickel, molybdenum, cobalt, tungsten, titanium, chromium and mixtures thereof. As recognized in the art, the noble and base metals will not generally be employed in the same catalyst system. Reference to the catalytically active metal or metals is intended to encompass such metal or metals in the elemental state or in some form such as an oxide, sulfide, halide, carboxylate and the like. The hydrogenation component is present in an effective amount to provide an effective hydrodewaxing catalyst. When the hydrogenation catalysts is a noble metal it is generally present in an amount between 0.05% and 1.5% by weight based on the total weight of the dewaxing catalyst including the weight of any binder or matrix material which may be present, as hereinafter discussed, although effective amounts outside this range may be employed. Although effective amounts in excess of 1.5 percent by weight may be employed, the preferred effective amount of the noble metal hydrogenation component is between 0.3% and 1.2% by weight. When the hydrogenation catalyst is a base metal(s) the effective amount will generally be between 1.0% and 30% percent by weight or more of the base metal, expressed as the oxide(s), based on the total weight of the dewaxing catalyst, although effective amounts outside this range may be employed. The final form of the hydrogenation component is not narrowly limited herein but may be a metal oxide, metal sulfide or other catalytically active form. Since sulfur is typically present in the hydrocarbon feedstock being treated, the actual form of some of the hydrogenation component(s) may well be at least in part a sulfide due to in situ reactions. When a noble metal is employed as the hydrogenation component the catalyst is generally activated in air and then reduced in a hydrogen atmosphere. When base metals are employed such are usually treated with a sulfur compound. The hydrogenation components can be incorporated into the overall catalyst composition by any one of numerous procedures. In general it has been observed that it is desirable to add the hydrogenation component to the catalyst as a separate component rather than provide such by ion exchange or impregnation of the NZ-MS component. They can be added either to the NZ-MS component, zeolitic aluminosilicate component, if any, or to any metal oxide or to a combination thereof by ion exchange, impregnation and the like. In the alternative, multiple hydrogenation components (two or more) may be added as powders in the formulation of the catalyst. They may be added by co-mulling, impregnation, or ion exchange whereby one or more may be added to NZ-MS and/or zeolitic aluminosilicate by impregnation, co-mulling or co-precipitation. For example, noble or base metal compounds, such as the sulfides, oxides or water-soluble salts, can be added by co-mulling, impregnation or precipitation before the composite is finally calcined. In the alternative these components can be added to the finished particle by impregnation with an aqueous, alcoholic, hydrocarbon or other nonaqeous solution of soluble compounds or precursors. Although the hydrogenation components can be combined with the NZ-MS end/or zeolitic aluminosilicate, if any, as the oxides such is generally not the case. They are usually added as a metal salt which can be thermally converted to the corresponding oxide in an oxidizing atmosphere or reduced to the metal with hydrogen or other reducing agent. The composition can be sulfided by reaction with a sulfur donor such as carbon disulfide, hydrogen sulfide, hydrocarbon thiols, elemental sulfur, and the like, described above. The above oxidizing or sulfiding processes are generally carried out on catalyst compositions which have been partially dried (as desired), tableted, pelleted, extruded (with binder or matrix), or formed by other means and then calcined, e.g., at a temperature above 315.5°C, usually above 426.7°C. It is well known in the art that dewaxing catalysts, are generally employed with a binder material or, as commonly referred to, with an inorganic oxide matrix which can be inert or also catalytically active. For example inorganic matrices such as silica, alumina, silica-alumina, silica-zirconia, silica-magnesia, alumina-boria, alumina-titania and the like and mixtures thereof may be employed. An inorganic oxide need not always be employed such as in the case of a preform containing the NZ-MS or may be employed in an amount between 1% and 95% by weight, preferably between 10% and 80% by weight, based on the total weight of the dewaxing catalyst. The term "crude oil feedstock" is used herein to denominate any crude oil feedstock or portion thereof and includes full range crude oils from primary, secondary or tertiary recovery from conventional or offshore oil fields and to the myriad of feedstocks derived therefrom. "Crude oil feedstocks" may also be "syncrudes" such as those that can be derived from coal, Fischer Tropsch fuel products; shale oil, tar sands and bitumens. The crude oil feedstock may be virgin (straight run) or generated synthetically by blending. Such crude oil feedstocks are traditionally desalted prior to use since sodium chloride is known to be a poison in many hydroprocessing operations. Further, the term "crude oil feedstocks" is intended to include component parts of crude oils which have heretofore been generally employed as feedstocks or potential feeds and includes feeds such as distillate gas oils, heavy vacuum gas oils, VGO, atmospheric and vacuum resids, syncrudes, pulverized coal and fractions boiling above the traditional end of the gasoline boiling range which generally includes compounds containing greater than about eleven carbon atoms and combinations thereof. The hydrocarbon feedstock for dewaxing typically boils above 176.7°C, preferably between 204.4°C and 648.8°C and more preferably between 204.4°C and 482.2°C. The hydrocarbon feedstock may be pre-treated in a hydrotreater to reduce, i.e. remove, compounds which contain sulfur and/or nitrogen. The hydrocarbon feedstock may have a significant sulfur content, present as hydrogen sulfide, ranging from 0.1 to 3 weight percent, and nitrogen content, present as ammonia, in an amount up to 20,000 ppm. Temperature, space velocity, and other process variables may be adjusted to compensate for the effects of nitrogen on the dewaxing catalyst activity. The feedstock is contacted in the dewaxing reaction zone with the dewaxing catalyst and, optionally, in the presence of hydrogen-containing gas. In hydrodewaxing, hydrogen is consumed in the hydrodewaxing process and an excess of hydrogen is typically maintained in the reaction zone. Advantageously, a hydrogen-to-oil (feed) ratio of at least 28.32 m³ hydrogen per 159 liters of feed (1,000 standard cubic feet of hydrogen per barrel of feed (SCFB)) is employed, and the hydrogen-to-oil ratio may range up to 56.6 m³ (20,000 SCFB). Preferably, 113 to 340 m³ (4,000 to 12,000 SCFB) is employed. Typically dewaxing and hydrodewaxing conditions are disclosed in U.S. Patent No. Re 28,398, U.S. Patent No. 3,852,189 and U.S. Patent No. 4,282,085. The instant process is carried out under effective catalystic dewaxing or hydrodewaxing conditions. Catalytic dewaxing is generally carried out at a LHSV (liquid hourly space velocity) between 0.2 and 50, a temperature between 260°C and 648.8°C, a pressure between subatmospheric and 506.5 bar. Hydrodewaxing is generally carried out at a LHSV between 0.1 and 15, a temperature between 204.4°C and 482.2°C, at a pressure between 1.702 bar and 173.3 bar and using molar ratios of hydrogen to hydrocarbon feedstock between 1 and 100.

Claims: The process for dewaxing a hydrocarbon feedstock comprising contacting the hydrocarbon feedstock at effective dewaxing conditions with a dewaxing catalyst characterized in that the catalyst comprises an effective amount of at least one NZ-MS selected from the group consisting of CoAPSOs, FeAPSOs, MgAPSOs, MnAPSOs, TiAPSOs, ZnAPSOs, CoMnAPSOs, CoMgAPSOs, CoMnMgAPSOs, MeAPOs, TiAPOs, FeAPOs, ELAPOs and mixtures thereof having an adsorption of isobutane in its calcined form of at least 2 percent by weight at a pressure of 0.67 bar and a temperature of 20°C. The process for hydrodewaxing a hydrocarbon feedstock to reduce its pour point comprising contacting the hydrocarbon feedstock with a catalyst in the presence of hydrogen at effective hydrodewaxing conditions wherein the catalyst comprises at least one hydrogenation component characterized in that the catalyst further comprises at least one NZ-MS selected from the group consisting of CoAPSOs, FeAPSOs, MgAPSOs, MnAPSOs, TiAPSOs, ZnAPSOs, CoMnAPSOs, CoMgAPSOs, CoMnMgAPSOs, MeAPOs, TiAPOs, FeAPOs, ELAPOs and mixtures thereof having an adsorption of isobutane in its calcined form of at least 2 percent by weight at a pressure of 0.67 bar and a temperature of 20°C. The process of one of the foregoing claims wherein said NZ-MS is further characterized in its calcined form by an adsorption of triethylamine of from zero to less than 5 percent by weight at a pressure of 3.46 mbar and a temperature of 22°C. The process of claim 3 wherein said adsorption of triethylamine is less than 3 percent by weight. The process of one of the foregoing claims wherein said catalyst contains an effective amount of at least one zeolitic aluminosilicate having activity wherein said zeolitic aluminosilicate is present in a weight ratio between 1:10 and 500:1 of said zeolitic aluminosilicate to said NZ-MS molecular sieve. The process of claim 5 wherein the weight ratio of zeolitic aluminosilicate to said NZ-MS is between 1:2 and 50:1. The process of claim 6 wherein the weight ratio of zeolitic aluminosilicate to said NZ-MS is between 1:1 and 20:1. The process of one of the foregoing claims wherein said catalyst comprises an inorganic matrix component present in an amount between 0 and 99 percent by weight, based on the total weight of said catalyst. The process of claim 8 wherein said inorganic oxide matrix component is present in an amount between 5 and 95 percent by weight. The process of one of the foregoing claims wherein said NZ-MS has at least part of its cations as hydrogen-forming species. The process of claim 10 wherein said hydrogen-forming species is NH + / 4 or H⁺. The process of claim 1 wherein the process is carried out by contacting a hydrocarbon feedstock boiling between 204.4°C and 648.8°C with said catalyst at a temperature between 260.0°C and 648.8°C, at a pressure between subatmospheric and 506.5 bar and a LHSV between 0.2 and 50. The process of claim 2 wherein the process is carried out by contacting a hydrocarbon feedstock boiling between 204.4°C and 648.8°C, in the presence of hydrogen with said catalyst at a temperature between 204.4°C and 482.2°C, at a pressure between 1.702 bar and 173.3 bar, and at a molar ratio of hydrogen to hydrocarbon feedstock between 1 and 100. The process of claim 5 wherein said zeolitic aluminosilicate is ZSM-5. The process of claim 9 wherein said inorganic oxide matrix component is selected from the group consisting of clays, silicas, aluminas, silica-aluminas, silica-zirconias, silica-magnesia, alumina-borias, alumina-titanias and mixtures thereof. The process of one of the foregoing claims wherein said NZ-MS is selected from the group consisting of ELAPSO-5, ELAPSO-11, ELAPSO-31, ELAPSO-40, ELAPSO-41 and mixtures thereof. The process of one of the foregoing claims wherein said NZ-MS is selected from the group consisting of MeAPOs, TiAPSOs, FeAPOs, ELAPOs and mixtures thereof. The process of claim 17 wherein "Me" is selected from the group consisting of cobalt magnesium, manganese, zinc and mixtures thereof. The process of claim 17 wherein "Me" is selected from the group consisting of magnesium, manganese and mixtures thereof. The process of one of the foregoing claims wherein said hydrocarbon feedstock is selected from the group consisting of heating fuel, jet fuel, lube oils, distillate gas oils, naphtha, reformate, kerosene, diesel fuel, heavy vacuum gas oils, Fischer Tropsch fuel product, VGO, atmospheric resids, vacuum resids, syncrudes, pulverized coal and mixtures thereof. The process of claim 5 wherein said zeolitic aluminosilicate is selected from the group consisting of zeolite Y, ultra-stable zeolites, zeolite X, silicalite, zeolite beta, zeolite KZ-20, faujasite, LZ-210, LZ-10, ZSM-type zeolites and mixtures thereof. The process according to claim 2 wherein the hydrogenation component is at least one metal selected from the group consisting of Pt, Pd, Rh, Ru, Ni, W, Mo, Co, Ti, Cr and mixtures thereof. The process of claim 22 wherein said metal is selected from the group consisting of Pt, Pd, Rh, Ru and mixtures thereof and is present in an effective amount between 0.05 weight percent and 1.5 weight percent. The process of claim 22 wherein the metal is selected from the group consisting of Ni, W, Mo, Co, Ti, Cr and mixtures thereof and is present in an amount between 1.0 and 30 percent by weight. A catalyst comprising a) at least one NZ-MS selected from the group consisting of CoAPSOs, FeAPSOs, MgAPSOs, MnAPSOs, TiAPSOs, ZnAPSOs, CoMgAPSOs, CoMnAPSOs, CoMnMgAPSOs, MeAPOs, TiAPOs, FeAPOs, ELAPOs and mixtures thereof having an adsorption of isobutane in its calcined form of at least 2 percent by weight at a pressure of 0.67 bar and a temperature of 20°C and b) an effective amount of at least one zeolitic aluminosilicate wherein the weight ratio between said aluminosilicate and NZ-MS is between 1:10 and 500:1, and c) at least one metal selected from the group consisting of nickel, cobalt, tungsten, molybdenum, platinum, palladium, chromium, rhodium, ruthenium and titanium. The catalyst of claim 25 wherein said NZ-MS molecular sieve is further characterized in its calcined form by an adsorption of triethylamine of from zero to less than 5 percent by weight at a pressure of 3.46 mbar and a temperature of 22°C. The catalyst of claim 25 or claim 26 wherein said catalyst contains at least one zeolitic aluminosilicate selected from the group consisting of zeolite Y, ultra-stable zeolite, zeolite X, silicalite, zeolite beta, zeolite KZ-20, faujasite, LZ-210, LZ-10, ZSM-type zeolites and mixtures thereof. The catalyst of one of the claims 25 to 27 wherein said catalyst contains from 1 to 99 percent by weight of at least one inorganic oxide matrix component. The catalyst of claim 28 wherein the inorganic oxide matrix component is selected from the group consisting of clays, silicas, aluminas, silica-aluminas, silica-zirconias, silica-magnesia, alumina-borias, alumina-titanias and mixtures thereof. The catalyst of one of claims 25 to 29 wherein said zeolitic aluminosilicate is selected from the group consisting of Y zeolite, ultra-stable zeolite Y, silicalite, LZ-210, LZ-10, ZSM-5 and mixtures thereof.

Inventors: GORTSEMA, FRANK PETER, LONG, GARY NORMAN, PELLET, REGIS JOSEPH, RABO, JULE ANTHONY, SPRINGER, ALBERT RAYMOND
Applicants: UOP
Application year: 1985
Main classification: C10G45
IPC codes: C10G45, B01J29, C10G73