METHOD OF STABILIZING FINES

Abstract: A method of preventing or reducing the migration of fines in a permeable structure which method comprises contacting said fines in said permeable structure with an effective amount of an organic copolymer having recurring structural monomer units formed in a random fashion of the formula: wherein each X is independently oxygen or NH; R¹, R⁶, and R⁸ are each independently hydrogen or methyl; R² is an alkylene group having 1 to about 4 carbon atoms; R³ and R⁵ are each independently methyl or ethyl; R⁴ is optionally present and, when present is either an alkyl group having from 1 to about 6 carbon atoms, or a quaternary ammonium group having the general formula: wherein R¹⁰ is an alkylene group having from about 2 to about 6 carbon atoms or a substituted alkylene group having from about 2 to about 6 carbon atoms and containing a hydroxyl group or from 1 to about 3 ether groups; and R¹¹, R¹², and R¹³ are each independently methyl or ethyl; Y is oxygen or NR¹⁶ wherein R¹⁶ is hydrogen, methyl or ethyl; R⁷ is either an alkyl group having from 1 to about 3 carbon atoms, or is of the formula: wherein R¹⁴ and R¹⁵ are each methyl or ethyl; and R²¹ is methylene, ethylene or trimethylene; R⁹ is hydrogen, an alkyl group containing 1 to about 4 carbon atoms, a substituted alkyl group having from 1 to about 4 carbon atoms and containing a hydroxyl group, a carboxyl group, or -SO₃J wherein J is hydrogen, sodium, potassium or the group: where R¹⁷ is methylene, ethylene or trimethylene; and, R¹⁸, R¹⁹, and R²⁰ are each independently methyl or ethyl; Z is oxygen or NH provided that, when Z is oxygen, R⁹ may further be sodium or potassium; A is a chloride, bromide, iodide, methyl sulfate or sulfate anion; m is an integer equal to the number of anions required to maintain electronic neutrality; n, r, and s are integers, the sum of which equals the total number of monomer units in the copolymer required to give a molecular weight in the range of from about 50,000 to about 1,000,000; and, monomer unit I is present in the range of from about 25 to about 95 mole percent of the copolymer; monomer unit II is present in the range of from about 5 to about 75 mole percent of the copolymer; and monomer unit III is present in the range of from about 0 to about 35 mole percent of the copolymer.

Description: This invention relates to a method of treating a permeable structure, such as a subterranean formation, using water-soluble organic copolymers in order to stabilize, in the structure, migrating fines such as silica, iron minerals, and alkaline earth metal carbonates. The recovery of fluids such as oil or gas or combinations thereof has been troublesome in areas where the subterranean formation is composed of one or more layers or zones which contain migrating fines such as silica, iron minerals, and alkaline earth metal carbonates. These fines tend to move or migrate to a well bore during the recovery of formation fluids from the particular layers or zones, and frequently block the passageways leading to the well bore. The movement or migration of fines to the well bore is a particular problem when the fines are contacted with water foreign to the formation. Plugging or materially impairing the flow of the formation fluids towards the well bore results in a loss of these fluids to the producer, and decreases the rate of hydrocarbon recovery from the well which may cause the well to be shut down because it is economically un­ attractive to produce therefrom. An additional adverse factor resulting from the movement of the fines towards the well bore is that they are often carried along with the formation fluids to the well bore and pass through pipes, pumps, etc., being used to recover the formation fluids to the surface with resulting damage to the moving parts thereof as the fines are very abrasive. Secondary and tertiary methods of recovering hydrocarbons from a subterranean formation are well known. In general, such a method involves introducing a fluid, such as water, steam etc., into one or more injection wells which penetrate the formation, and forcing the fluid toward one or more offset producing wells. Migrating fines particles during such an operation can decrease the per­ meability of the formation which may cause a decrease in the rate in which fluid can be injected into the formation which results in a decrease in the rate of hydrocarbon production at the offset production wells. Migrating fines are frequently encountered during acidizing or fracturing operations and during sand consolida­ tion operations. The presence of the fine particles during these operations can result in a decrease in the permeability of the formation which is being treated. Gravel packing is a widely practiced method of preventing the production of sand from poorly consolidated formations. The migration of fine particles into the gravel pack can greatly reduce the permeability of the gravel pack, which can result in a decrease in the rate of produc­ tion of hydrocarbons from the formation. Consequently, in efforts to overcome these problems, various methods have been developed for treating a subterranean formation in order to stabilize portions of the formation containing migrating fines. For instance, U.S. Patent Nos. 4,366,071; 4,366,072; 4,366,073; 4,366,074; 4,374,739; and 4,460,483 disclose the use of organic polycationic polymers to prevent or reduce the ill effects of swelling clays or migrating fines in sub­ terranean formations. We have now devised a method of stabilizing fines within a permeable structure such as a subterranean formation using organic polymers which are effective in reducing the migration of fine particles in the permeable structure. The copolymers can be either nonionic in a neutral medium or can contain up to 95% be weight of a quanternary ammonium salt monomer. The method of the present invention involves the use of organic copolymers to prevent or reduce the ill effects of migrating fines in a permeable structure such as a permeable earthen formation penetrated by a well bore. The method is carried out by contacting the fines in the permeable structure with an effective amount of certain organic copolymers. The copolymers which are used in the present invention contain two (binary copolymers) or three (ternary copolymers) different repeating monomer units and are random in nature. That is, the distribution of the repeating monomer units is determined by the concentration and relative reactivity of the monomers which form the repeating monomer units. The monomer units are linked together in a random sequence along the copolymer chain. The organic copolymers used in the method of the invention are very effective in treating migrating fines such as silica, iron minerals such as hematite, magnetite, lepidocrocite, wuestite, akageneite, and siderite, and alkaline earth metal carbonates such as calcite and dolomite. The orga­ nic copolymers are particularly effective when used to treat permeable structures which contain about 4% by weight migrating fines in the mass of the structure and less than 2% by weight swelling clays. In addition, the copolymers are par­ ticularly effective when used in conjunction with an acidizing operation that utilizes a strong mineral acid such as 15 percent by weight hydrochloric acid or mixtures of 3 percent by weight hydrofluoric acid and 12 percent by weight hydrochloric acid. A treatment with the organic copolymers of the pre­ sent invention is essentially permanent and the copolymers are very resistant to being removed by brines, oils, or acids. Formations exhibit high permeability retention after the formation has been treated with the organic copolymers. Furthermore, the copolymers are very effective over a wide range of temperatures and are particularly effective from about 90°F to about 200°F, (32°C to 93°C). No well shut-in time is required when the organic copolymers are used to carry out the method of the invention. The present invention involves the use of organic copolymers to prevent the migration of fines contained in a permeable structure such as a subterranean formation. The use of the method of the invention results in stabilizing the permeable structure. These fines may or may not be present with clay materials. Preferably, fines are present in the permeable structure in an amount of about 4% by weight of the structure and the clays are pre­ sent in an amount of less than about 2% by weight of the structure. The organic copolymers which are suitable for use in accordance with this invention have recurring structural units formed in a random fashion of the formula: wherein X is selected from the group consisting of oxygen and NH; R¹, R⁶, and R⁸ are independently selected from the group consisting of hydrogen and methyl; R² is an alkylene group having 1 to about 4 carbon atoms; R³ and R⁵ are independently selected from the group consisting of methyl and ethyl; R⁴ is optionally present and when present is selected from the group consisting of: (1) an alkyl group having from 1 to about 6 carbon atoms; and (2) a quaternary ammonium group having the general formula: wherein: R¹⁰ is selected from the group consisting of an alkylene group having from about 2 to about 6 carbon atoms and a substituted alkylene group having from about 2 to about 6 carbon atoms and containing a hydroxyl group or from 1 to about 3 ether groups; R¹¹, R¹², and R¹³ are indepen­ dently selected from the group consisting of methyl and ethyl; Y is selected from the group consisting of oxygen and NR¹⁶ wherein R¹⁶ is selected from the group consisting of hydrogen, methyl and ethyl; R⁷ is selected from the group consisting of an alkyl group having from 1 to about 3 carbon atoms; and, wherein: R¹⁴ and R¹⁵ are independently selected from the group consisting of methyl and ethyl; and, R²¹ is selected from the group consisting of methylene, ethylene, and trimethylene; R⁹ is selected from the group consisting of hydro­ gen, an alkyl group containing 1 to about 4 carbon atoms, a substituted alkyl group having from 1 to about 4 carbon atoms and containing a hydroxyl group, a carboxyl group, or -SO₃J wherein J is selected from the group consisting of hydrogen, sodium and potassium, and wherein: R¹⁷ is selected from the group consisting of methylene, ethylene, and trimethylene; and R¹⁸, R¹⁹, and R²⁰ are independently selected from the group consisting of methyl and ethyl; Z is selected from the group consisting of oxygen and NH and provided further when Z is oxygen, R⁹ may further be selected from the group consisting of sodium and potassium; and, A is an anion selected from the group consisting of chloride, bromide, iodide, methyl sulfate, and sulfate; m is an integer equal to the number of anions required to maintain electronic neutrality; n, r, and s are integers the sum of which equals the total number of monomer units in the copolymer required to give a molecular weight in the range of from about 50,000 to about 1,000,000; and, monomer unit I is present in the range of from about 25 to about 95 mole percent of the copolymer; monomer unit II is present in the range of from about 5 to about 75 mole percent of the copolymer; and, monomer unit III is present in the range of from about 0 to about 35 mole percent of the copo­ lymer. A preferred organic copolymer of Formula A which is nonionic in character comprises an organic copolymer having recurring structure units formed in a random fashion of the formula: wherein R² is selected from the group consisting of ethylene and methylene. A preferred polycationic organic copolymer of Formula A comprises an organic copolymer having recurring structural units formed in a random fashion of the formula: wherein: R⁶ and R⁸ are independently selected from the group consisting of hydrogen and methyl; R⁹ is selected from the group consisting of hydrogen and sodium; A is selected from the group consisting of chloride, bromide, iodide, methyl sulfate and sulfate; and, m is an integer equal to the number of anions required to maintain electronic neutrality. The organic copolymers of the present inven­ tion can be used to treat both natural and artifi­ cial structures which are permeable, including poorly consolidated and unconsolidated rocks. The method of the invention is particularly suited for stabilizing fine particles having a diameter of less than 10 microns. Furthermore, there is a wide range of application for the organic copolymers. These applications involve using the organic copo­ lymers alone as the primary treating agent, or as an auxiliary in other treatments. Examples of monomer unit I which are suitable in the method of the present invention include dimethylaminoethyl methacrylate, the methyl chloride salt of dimethylaminoethyl methacrylate, and methacrylamido-4,4,8,8-tetramethyl-4,8­ diaza-6-hydroxynonamethylene dichloride (MDTHD). Monomer unit I is preferably present in the copolymer in an amount of from about 60 to about 80 mole percent of the copolymer and most preferably is present in an amount of about 70 mole percent. Examples of monomer unit II which are suitable in the method of the present invention include dimethylaminoethyl methacrylate, dimethylamino­ propyl methacrylamide, dimethylamidopropyl meth­ acrylamide, and dimethyl acrylamide. Monomer unit II is preferably present in the copolymer in an amount of from about 25 to about 35 mole percent of the copolymer and most preferably is present in an amount of about 30 mole percent. Examples of monomer unit III which are suitable in the method of the present invention include methacrylic acid and 2-acrylamido-2-­ methylpropane sulfonic acid. Monomer unit III is preferably present in the copolymer in an amount of from about 0 to about 10 mole percent of the copolymer and most preferably is present in an amount of about 3 mole percent. Examples of particularly preferred binary copolymers which are suitable for use in the pre­ sent invention include copolymers containing the following monomer units. In formula D, monomer unit I is preferably present in an amount of about 66.7 mole percent of the copolymer and monomer unit II is preferably present in an amount of about 33.3 mole percent of the copolymer. In formula E, monomer unit I is preferably present in an amount of about 66.7 mole percent of the copolymer and monomer unit II is preferably present in an amount of about 33.3 mole percent of the copolymer. In formula F, monomer unit I is preferably present in an amount of about 90.0 mole percent of the copolymer and monomer unit II is preferably present in an amount of about 10.0 mole percent of the copolymer. In formula G, monomer unit I is preferably present in an amount of from about 95 mole percent to about 70 mole percent of the copolymer and monomer unit II is preferably present in an amount of from about 30 mole percent to about 5 mole per­ cent of the copolymer. wherein A is chloride or methyl sulfate. In formula H, monomer unit I is preferably present in an amount of from about 75 mole percent to about 25 mole percent of the copolymer and monomer unit II is preferably present in an amount of from about 25 mole percent to about 75 mole per­ cent of the copolymer. Examples of particularly preferred ternary copolymers which are suitable for use in the method of the present invention include copolymers con­ taining the following monomer units: In formula J, monomer unit I is preferably present in an amount of from about 32.3 mole per­ cent to about 64.5 mole percent of the copolymer, monomer unit II is preferably present in an amount of from about 32.3 mole percent to about 64.5 mole percent of the copolymer, and monomer unit III is preferably present in an amount of about 3.2 mole percent of the copolymer. In formula K, the monomer unit I and monomer unit II are each preferably present in an amount of about 45.45 mole percent of the copolymer and monomer unit III is preferably present in an amount of 9.1 mole percent of the copolymer and W is When monomer unit III is III(c) the molar percen­ tages of monomer units I, II, and III are pre­ ferably each about 33.3 mole percent of the copolymer. An example of a ternary copolymer containing two (2) different quaternary ammonium salt monomer units which is contemplated for use in the method of the present invention comprises a copolymer con­ taining the following monomer units: The most preferred copolymer for use in accor­ dance with the present invention comprises a copo­ lymer having the following formula: In Formula L, monomer unit I, which is known as methacrylamidopropyl-4,8-diaza-4,4,8,8-tetra­ methyl-6-hydroxynonamethylene dichloride (MDTHD), is preferably present in an amount of about 70 mole percent of the copolymer; monomer unit II, which is known as dimethylaminoethyl methacrylate, is pre­ ferably present in an amount of about 27 mole per­ cent of the copolymer; and monomer unit III, which is known as methacrylic acid is preferably present in an amount of about 3 mole percent of the copo­ lymer. In Formulae D through M, m, n, r, s, and A have the same meaning as they hold in Formula A above. The organic copolymers of the present inven­ tion should have a molecular weight of from about 50,000 to about 1,000,000. Preferably, the organic copolymers have a molecular weight of about 100,000 to about 400,000 and most preferably about 200,000. The molecular weight of the organic copo­ lymers used in the method of the present invention will vary over a wide range depending upon the per­ meability of the formation to be treated and the copolymer used in the method of the invention. An anion selected from the group consisting of chloride, bromide, iodide, methyl sulfate and sulfate is present when the organic copolymer is cationic such as when monomer unit I or monomer unit III or monomer units I and III of the copo­ lymer contain one or more quaternary amine groups and the anion is present in an amount sufficient to maintain electronic neutrality. The amount of organic copolymer employed in the method of the present invention will vary according to, for example, the size and porosity of the particular formation and the types of fines present. Therefore, there are no upper or lower limits in this regard. Any suitable method of application can be used to carry out the method of the invention. For some applications such as surface or exposed structures, it may be desirable to merely spray the polymer onto the permeable mass. The essential feature is contact between the fines to be treated and the organic copolymer. When a carrier fluid is used to carry out the method of the invention, the organic copolymers will generally be present in the carrier fluid in a concentration within the range of from about 0.01% to about 5.0% by weight of the carrier fluid. Lower or higher concentrations can be used, but are not generally as practical. When a carrier fluid is used, the preferred concentration of the organic copolymers is in the range of from about 0.25 to about 1.00 percent by weight of the carrier fluid. Carrier fluids which can be used to carry out the method of the present invention include polar and non-polar fluids. Examples of suitable fluids include water, brine, aqueous mixtures of low mole­ cular weight alcohols, ketones, and monoethers of glycol. Examples of suitable low molecular weight alcohols include methanol, ethanol, and isopropa­ nol. When water is used as the carrier fluid, the carrier fluid can contain other ingredients which do not substantially interfere with the dispersion or dissolution of the organic copolymer in the carrier fluid. Furthermore, the water can be gelled or thickened for certain applications. Examples of ingredients which can be included in the water include salts, mineral acids, low molecu­ lar weight organic acids, cationic or nonionic sur­ factants, and wetting agents. When the copolymer used in the method of the present invention does not contain a cationic monomer unit, the water may also contain an anionic surfactant as the copolymer has an electrical charge which is nonreactive with the electronic charge of the anionic surfactant. Preferably the carrier fluid has a viscosity of less than 10 centipoises. High viscosity fluids may be used in certain applications but are not generally very practical due to the pressure and pumping requirements. A preferred aqueous carrier fluid is a saline solution containing about 0.1 to about 40.0 percent by weight of salt. The pre­ ferred salt concentration is about 2 to about 12 percent by weight of the solution. The salt can be an alkali metal salt, alkaline earth metal salt, an ammonium salt or mixtures thereof. Suitable anions include halides, such as chloride, bromide, and iodide, sulfates, carbonates, hydroxides, or mixtures thereof. The halides of potassium, sodium, magnesium, calcium, and ammonium and mix­ tures thereof are preferred due to the economics and solubility. Aqueous acids having a con­ centration of about 0.1 to about 40.0 percent by weight of the solution can also be utilized in carrying out the method of the invention. Examples of suitable acids include hydrochloric acid, hydrofluoric acid, phosphoric acid, acetic acid, formic acid, citric acid, and mixtures thereof. The preferred acids include about 3 to about 15 percent by weight of hydrochloric acid and a mix­ ture of about 3% by weight hydrofluoric acid and about 12% by weight of hydrochloric acid. The method of the present invention can be used in a number of operations. For instance, the method of the present invention can be used in con­ junction with sand consolidation procedures, gravel packing procedures, secondary recovery operations, and acidizing or fracturing operations. In these operations, the organic copolymers can be used to prevent or reduce the migration of fines in the subterranean formation. This results in a greater permeability in the formation and a greater per­ meability increase during acidizing or fracturing operations. The present invention is further exemplified by the examples below which are pre­ sented to illustrate certain specific embodiments of this invention, but are not intended to be construed so as to be restrictive of the spirit and scope thereof. IV. EXAMPLES A number of tests were performed to evaluate the effectiveness of various copolymers as fine stabilizers. The following monomer unit abbre­ viations are used herein: The following copolymers were utilized in the tests: Treatment fluid viscosity was measured using a Brookfield Model LVT viscometer using a UL adapter at 30 rpms. The copolymer solvent was aqueous two percent (by weight) ammonium chloride. The tem­ perature at the time of the measurement was 74°F (23°C). The molecular weight of the copolymers used in the tests was in the range of from about 50,000 to about 1,000,000. EXAMPLE I A. Test Equipment and Procedure The test equipment used in the tests of Example I was a TEFLON sleeved test chamber having a diameter of about 2.5 cm at the bottom of the chamber and a diameter of about 2.6 cm at the top of the chamber. The chamber design insured that, under modest applied pressure, fluid injected during the test would flow through the test sand rather than around the test sand. The test sand comprised 100 grams of a mixture of 85 percent by weight 70-170 U. S. mesh sand and 15 percent by weight silica fine particles. The silica fine par­ ticles had a median particle diameter of 22.4 microns and surface area of 1.20m²/gram. A 100 U. S. mesh screen was placed at the base of the chamber to hold the larger particles in place. The test chamber and fluid reservoir were heated to about 145°F (63°C). The first fluid injected into the top of the chamber during the tests comprised 236cc of an aqueous solution containing 2 percent by weight of ammonium chloride and 0.25 percent by weight of the copolymer. The injection pressure was 5 psia (34.5 kPa). Included in these tests were treatments in which no copolymer was added to the fluid. After completion of the injection of the first fluid the injection pressure was increased to 40 psig (276 kPag) and 500cc of fresh water was injected. The fresh water treatment was optionally followed by an injection at 40 psig (276 kPag) of 400cc of an aqueous fluid comprising 15 percent by weight of hydrochloric acid and an injection at 40 psig (276 kPag) of 500cc of fresh water The effluent of each treatment was collected and filtered through a tared piece of 0.45 micron filter paper. The solids from the effluent were collected in the filter paper, dried and weighed. The results of these tests are shown in Table III. Test No. 1 was a control experiment to deter­ mine the amount of silica fines produced in the absence of any copolymer. An amount of 0.21g of fines was produced during the injection of 500cc of fresh water and a total of 0.34g of fines were pro­ duced after injection of the 15% hydrochloric acid and followed by fresh water. These amounts were defined, for calculations purposes, as 100% fines production. From Table III, it can be seen that the binary and ternary copolymers used in the method of the present invention are very effective as silica fine stabilizers even after exposure of the copolymer to an aqueous 15 percent by weight hydrochloric acid solution. EXAMPLE II A series of tests were performed in the same manner as Example I except the copolymers were eva­ luated as fine stabilizers for calcite and hema­ tite. The calcite had a median particle diameter of 8.9 microns and a surface area of 10.98m²/gram. The hematite had a median particle diameter of 4.4 microns and a surface area of 6.44m²/gram. The results of these tests are shown in Table IV. The results of the tests reported in Table IV show that the copolymers, with the exception of copolymer L, were effective in reducing the produc­ tion of fines from a test column containing 15 per­ cent by weight calcite fine particles. The results of the tests also show that the copolymers, with the exception of copolymers L, E, and R, were effective hematite fines stabilizers. The reason the results of these tests showed that copolymer L did not reduce calcite fine pro­ duction and copolymers L, E, and R did not reduce hematite fine production is not understood. Although the standard tests procedures were used in evaluating copolymer L as a calcite fines stabilizer and copolymer L, E, and R as a hematite fines stabilizer, it is possible that the results observed were due to procedure problems in performing these experiments. Potential procedure problems include: increasing the injection pressure from 5 psia to 40 psig (276 kPag) too rapidly causing pressure surges which disturbed the sand pack in turn causing addi­ tional fines migration over what was observed in the controlled tests; temporarily increasing the injection pressure above 40 psig (276 kPag); difficulties in packing the test columns; and a hole in the 100 U. S. mesh screen allowing additional solids to pass through the screen. EXAMPLE III A series of tests were performed in the same manner as Example I except that the treatment solvent was a strong acid solution comprising aqueous 15% hydrochloric acid. The results of these tests are shown in Table V. The results in Table V indicate that the copo­ lymers tested were quite effective when the treat­ ment solvent was a strong acid.

Claims: 1. A method of preventing or reducing the migration of fines in a permeable structure which method comprises contacting said fines in said permeable structure with an effective amount of an organic copolymer having recurring structural monomer units formed in a random fashion of the formula: wherein each X is independently oxygen or NH; R¹, R⁶, and R⁸ are each independently hydrogen or methyl; R² is an alkylene group having 1 to about 4 carbon atoms; R³ and R⁵ are each independently methyl or ethyl; R⁴ is optionally present and, when present is either an alkyl group having from 1 to about 6 carbon atoms, or a quaternary ammonium group having the general formula: wherein R¹⁰ is an alkylene group having from about 2 to about 6 carbon atoms or a substituted alkylene group having from about 2 to about 6 carbon atoms and containing a hydroxyl group or from 1 to about 3 ether groups; and R¹¹, R¹², and R¹³ are each independently methyl or ethyl; Y is oxygen or NR¹⁶ wherein R¹⁶ is hydrogen, methyl or ethyl; R⁷ is either an alkyl group having from 1 to about 3 carbon atoms, or is of the formula: wherein R¹⁴ and R¹⁵ are each methyl or ethyl; and R²¹ is methylene, ethylene or trimethylene; R⁹ is hydrogen, an alkyl group containing 1 to about 4 carbon atoms, a substituted alkyl group having from 1 to about 4 carbon atoms and containing a hydroxyl group, a carboxyl group, or -SO₃J wherein J is hydrogen, sodium, potassium or the group: where R¹⁷ is methylene, ethylene or trimethylene; and, R¹⁸, R¹⁹, and R²⁰ are each independently methyl or ethyl; Z is oxygen or NH provided that, when Z is oxygen, R⁹ may further be sodium or potassium; A is a chloride, bromide, iodide, methyl sulfate or sulfate anion; m is an integer equal to the number of anions required to maintain electronic neutrality; n, r, and s are integers, the sum of which equals the total number of monomer units in the copolymer required to give a molecular weight in the range of from about 50,000 to about 1,000,000; and, monomer unit I is present in the range of from about 25 to about 95 mole percent of the copolymer; monomer unit II is present in the range of from about 5 to about 75 mole percent of the copolymer; and monomer unit III is present in the range of from about 0 to about 35 mole percent of the copolymer. 2. A method according to claim 1, wherein said permeable structure is a subterranean formation. 3. A method according to claim 1 or 2, wherein said copolymer is either of the formula: wherein R² is ethylene or methylene; and n, r and s are as defined in claim 1; or of the formula: wherein R⁶ and R⁸ are each independently hydrogen or methyl; R⁹ is hydrogen or sodium; and A,m,n,r and s are as defined in claim 1. 4. A method according to claim 1 or 2, wherein monomer unit I is derived from dimethylaminoethyl methacrylate, the methyl chloride salt of dimethylaminoethyl methacrylate, or methacrylamido-4,8-diaza-4,4,8,8-tetra­ methyl-6-hydroxynonamethylene dichloride. 5. A method according to claim 1,2 or 4, wherein monomer unit II is derived from dimethylaminoethyl methacrylate, dimethylaminopropyl methacrylamide, dimethylamidopropyl methacrylamide, or dimethylacrylamide. 6. A method according to claim 1,2, 4 or 5, wherein monomer unit III is derived from methacrylic acid or 2-acrylamido-2-methylpropane sulfonic acid. 7. A method according to claim 1 or 2, wherein organic copolymer has the formula: wherein A is chloride or methyl sulfate; or n,p and s is the formulae being as defined in claim 1; or any mixture of two or more thereof. 8. A method acording to any of claims 1 to 6, wherein said molecular weight is in the range of from about 100,000, to about 400,000, and monomer unit I is present in an amount of about 70 mole percent of the copolymer, monomer unit II is present in an amount of about 27 mole percent of the copolymer and monomer unit III is present in an amount of about 3 mole percent of the copolymer. 9. A method according to any of claims 1 to 8, wherein said copolymer is dispersed in a carrier fluid. 10. A method according to claim 9, wherein said carrier fluid comprises from about 0.1 to about 40.0 percent by weight of one or more salts, selected from alkali metal halides, alkaline earth metal halides, ammonium halides and mixtures thereof; the copolymer being present in said carrier fluid in an amount of from about 0.01 to about 5.0 percent by weight of the carrier fluid.

Inventors: BORCHARDT, JOHN KEITH
Applicants: HALLIBURTON COMPANY
Application year: 1985
Main classification: E21B43
IPC codes: C09K8