IMPROVED CHEMICAL VAPOR DEPOSITION METHOD OF PRODUCING FLUORINE-DOPED TIN OXIDE COATINGS

Abstract: A fluorine-doped tin oxide coating having a minimum and constant sheet resistance under different process condi­ tions is produced by a chemical vapor deposition method using a liquid coating composition containing 1-30 wt % of an organic fluorine dopant and 70-99 wt % of an organotin compound and optionally up to 10% of a polar organic solvent. This composition is vaporized into a wet carrier gas which is decomposed on the substrate, the vapor concentrations satisfying the condition that the parameter M defined by the equation given below is 50,000 or less: where (AIR) (H₂O) and (OFD) and (O) are respectively in moles the concentration of the carrier gas, the concentration of water in the carrier gas, the concentration of the organic fluorine dopant in the carrier gas and the concentration of organotin compound in the carrier gas.

Description: IMPROVED CHEMICAL VAPOR DEPOSITION METHOD OF PRODUCING FLUORINE-DOPED TIN OXIDE COATINGS BACKGROUND OF THE INVENTION 1. Field of the Invention This invention relates to tin oxide coatings, and more particularly, to an improved method of producing fluorinedoped tin oxide coatings by chemical vapor deposition. 2. Description of the Prior Art Fluorine-doped tin oxide coatings are known to impart useful properties to many different substrate surfaces, including glass, ceramics, metals and elemental filaments. Such coated substrates find use as heat reflective elements, in energy efficient windows and in opto-electronic and semiconductor devices. Chemical vapor deposition of tin oxide coatings has been described in the literature, See, for example, United States Patents 3,677,814; 3,949,146; 4,130,673; 4,146,657; 4,213,594; 4,265,974; Thin Solid Films 77, 51-63 (1981); 65-66; and J. Electrochem. Soc. 122, 1144 (1975). The chemical vapor deposition method described in the prior art suffers from one or more disadvantages in that the process conditions, or compositions used, or the properties of the resulting tin oxide coatings, are not entirely satisfactory for certain commercial applications. For example, where the product is an energy efficient window, success has been limited by the relatively high and variable sheet resistance of the coatings obtained in the process, and the low deposition rates. Kane in U.S. Patent No. 3,949,146 describes chemical vapor deposition of tin oxide coatings from dibutyltin diacetate, bis(tri-n-propyl)tin oxide or bis(tri-n-butyl)tin oxide doped with antimony. However, there is no disclosure of a method of producing a low sheet resistance fluorinedoped coating whose resistance is independent of process variables. A chemical deposition method also is disclosed by Kato in U.S. patent 4,500,567. This process uses a gaseous mixture of monobutyltin trichloride and a halodifluoromethane which is formed from separate gaseous streams of each reactant. The gaseous mixture then is deposited onto a glass surface. However, in this method the electrical properties of the coating are not adequate, and the deposition times are long. As will be apparent from the above-described review of the prior art, there is a need for an improved chemical vapor deposition process of making fluorine doped tin oxide coatings, particularly a process which will provide such coatings having a constant and minimum sheet resistance under a range of process conditions. SUMMARY OF THE INVENTION In accordance with the invention, there is provided herein an improved chemical vapor deposition method for forming fluorine-doped tin oxide coatings using a liquid coating composition which includes a reactive organic fluorine dopant and an organotin compound. The method is carried out under a defined set of process conditions such that the coating produced has a minimum and constant sheet resistance which is substantially independent of temperature. The variables in this process are the concentrations, in the vapor phase, of carrier gas, water, organic fluorine dopant and organotin compound. These concentrations are related by a parameter M, which is defined by the equation: M = (AIR) (H 0) (OFD) (OZ where (AIR) is the concentration in moles of carrier gas; (H2O) is the concentration in moles of water in the carrier gas; (OFD) is the concentration in moles of organic fluorine dopant in the carrier gas, and (O) is the concentration in moles of organotin compound in the carrier gas. Suitably, M has a value of 50,000 or less, preferably 20,000 or less. At these M values, the deposited tin oxide coating has a minimum and constant sheet resistance which is substantially independent of deposition temperature. At M values higher than those proscribed herein, the sheet resistance increases substantially with increasing M and increases with deposition temperature. The chemical vapor deposition process is carried out using a liquid coating composition which comprises 1-30 wt.% of the organic fluorine dopant, and 70-99% of the organotin compound. A preferred composition is 2-10% of the organic fluorine donant and 90-98 wt.Z of the ornanotin compound. may contain up to The Composition / 10 wt.% of a polar organic solvent. may be Deposition / carried out on glass to produce a fluo- rine-doped tin oxide coating of a thickness of 180-210 nm which has a minimum and constant sheet resistance of about 25 ohms/sq. for M values which are 50,000 or below, prefer- ably 20,000 or below. BRIEF DESCRIPTION OF THE DRAWINGS FIG. 1 is a schematic illustration of an apparatus for carrying out a suitable chemical vapor deposition process. FIG. 2 is a graph of sheet resistance vs. M values for tin oxide coatings produced in accordance with the process of this invention. DETAILED DESCRIPTION OF THE INVENTION Referring now to FIGURE 1, there is shown a diagrammatic representation of an apparatus suitable for carrying out the chemical vapor deposition process of the present invention. A carrier gas 10 which includes oxygen, with air being preferred, is metered through a feed line 11 and through an air dryer tower 12 to provide a stream 13 of dry air. A separate air stream is directed through a humidifier 14 containing a suitably quantity of water 15 to provide a wet air stream 16 at a desired relative humidity. Thereby a wet air stream 17, is passed through an evaporator 18 containing vessel 19 which holds a liquid coating composition supplied to evaporator 18 by syringe pump 20 and syringe 21. The air stream is heated from an oil bath (not shown) to a desired vaporization temperature. The vaporized liquid coating composition in the air stream 22 then travels to a deposition chamber 23 having a coating nozzle 24 in which a substrate 25 is mounted on a heated plate 26. After deposition of the desired coating the gaseous by-products of the deposition are exhausted. The liquid coating composition in the process of the invention comprises: a) 1-30 wt. Z of a reactive organic fluorine dopant compound where at least one fluorine atom is located alpha or beta to a functional group wherein carbon is bonded to oxygen selected from carboxylic acid, anhydride, ester, alcohol, ketone, acid halide or ether; and b) 70-99 wt. Z of an organotin compound which is an alkyltin trichloride, a dialkyltin dichloride, an alkyldichlorotin acetate, an alkyl chlorotindiace tate, or an ester tin trichloride, or tin tetra chloride. Accordingly, suitable functional groups and reactive organic fluorine dopants include the following: Carboxylic acids trifluoroacetic acid chlorodifluoroacetic acid difluoroacetic acid heptafluorobutyric acid pentafluoropropionic acid 3-trifluoromethylcrotonic acid Anhydrides trifluoroacetic anhydride heptafluorobutyric anhydride pentafluoropropionic anhydride chlorodifluoroacetic anhydride perfluoroglutaric anhydride perfluorosuccinic anhydride Esters ethyl trifluoroacetate butyl trifluoroacetate ethyl bromodifluoroacetate ethyl chlorofluoroacetate methyl pentafluoropropionate methyl heptofluorobutyrate methyl trifluoroacetate methyl perfluorobuten-3-oate 2 , 2, 2-trifluoroethyltrifluoroacetate l,l,l-trifluoroisopropylacetate Alcohols 2,2,2-trifluoroethanol IH, 1H-heptafluorobutanol- 1 3,3,4,4,5,5,5-heptafluoropentanol-2 heptafluoroisopropanol hexafluoro-2-methylisopropanol 1H, lH,5H-octafluoro-l-pentanol perfluoro-t-butanol 2-trifluoromethylpropanol-2 1 , 1, 1-trifluoropropanol-2 Ketones ethyl 4,4,4-trifluoroacetoacetate l,l,l-trifluoroacetylacetone bis(perfluoroisopropyl)ketone 3-bromo-1,1,1-trifluoropropanone ethyl 4,4,4-trifluoroacetoacetate hexafluoroacetylacetone pentafluoroethyl ethyl ketone l,l,l-trifluoroacetone methyl heptafluoropropyl ketone Acid halides heptafluorobutyryl chloride perfluoroglutaryl fluoride perfluoroctanoyl chloride perfluorosuccinyl chloride Ethers 2-chloro-1,1,2-trifluoroethyl methyl ether 2-chloro-1,1,2-trifluoroethyl ethyl ether Representative reactive organic fluorine dopants include trifluoroacetic acid, trifluoroacetic anhydride, ethyl trifluoroacetoacetate, trifluoroethanol, ethyl trifluoroacetate, pentafluoropropionic acid, 2-chloro-1,1,2trifluoroethyl methyl ether, 1,1, l-trifluoroacetylacetone and heptafluorobutyryl chloride. Topical ornanotin comPounds include monobutvltin - - - - mehv1tin trichloride, isobutyltin trichloride, trichloride, /dibutyltin dichloride, butyldichlorotin acetate, butylchlorotin diacetate, carbethoxyethyltin trichloride. Tin tetrachloride also may be used as the tin compound. In a preferred form of the invention, the liquid coating composition includes 2-10 wt % of the organic fluorine compound, and 90-98 wt % of the organotin compound. The liquid coating composition of the invention may include also a polar organic compound, in an amount of about 1-10 wt Z of the composition, which will insure stability of the liquid composition at low temperatures. When the polar organic liquid is present, the liquid coating composition may include 2-10 wt % of the organic fluorine dopant, 80-97 wt % of the organotin compound and 1-10 wt % of the polar organic liquid. In a preferred form of the invention the organic fluorine dopant is trifluoroacetic acid, trifluoroacetic anhydride, or ethyl trifluoroacetoacetate, and the organotin compound is monobutyltin trichloride. The vaporization temperature in the process suitably ranges from about 100" to about 400"C., and preferably about 150 to 2500C. The substrate temperature ranges from about 400" to about 700"C., and preferably about 5500 to about 6500C. The carrier gas is an oxygen-containing gas which may be air, or a mixture of oxygen and an inert gas, and is preferably air. The carrier gas contains water vapor in the process of the invention. The substrate to be coated may be glass, ceramics, solid state materials, metals, elemental filaments and the like. The sheet resistance (ohms/sq) of the tin oxide film is measured with a conventional four point probe according to ASTM standard method F374-81. The film thickness is measured by the beta-back-scatter method according to British Standards Institution method BS5411: Part 12, 1981, ISO 3543-1981. Referring now to FIGURE 2, it is seen that the parameter M, which defines the process conditions of this invention, can be varied to provide fluorine-doped tin oxide coatings having a minimum and constant sheet resistance. For M values below 50,000, the sheet resistance of the coating, at a thickness of about 180 to 210 nm is 25 ohm/sq. For M values above 50,000, the sheet resistance increases rapidly with increasing M. Example 1 Tin Oxide Coatings Made Under Conditions in which the "M" Value is Below 50,000. A liquid coating composition of 100 parts monobutyltin trichloride (MBTC), 4.04 parts trifluoroacetic acid (TFA) and 1.45 parts acetic anhydride (AA) (specific gravity 1.62) was pumped at a rate of 10.5 g/hr, into an evaporator heated to 1200C., corresponding to 0.035 mol/hr. of MBTC and 0.0035 mol/hr. of TFA. Then wet air containing 28.8 mol/hr. of air and 0.067 mol/hr. of H2O was passed through the evaporator, and the vapor was deposited in 20 seconds onto a glass slide heated to 5000C. The coating thus produced had a thickness of 210 nm. The calculated M value was 16,000. The measured sheet resistance of the coating was 25 ohms/sq. Example 2 Tin Oxide Coatings Made Under Conditions in which the "M" Value is Above 50,000. A liquid coating composition of 100 parts MBTC, 2 parts TFA and 0.72 parts AA was pumped into the evaporator at a rate of 10.5 g/hr., corresponding to 0.036 mol/hr of MBTC and 0.0018 mol/hr of TFA. Then wet air containing 27.6 mole/hr of air and 1.02 mol/H2O was passed through the evaporator and the vapor mixture thus-formed was deposited onto a glass slide heated to 5000C. In 12 seconds a fluorine-doped tin oxide coating having a thickness of 190 nm was produced. The calculated M value was 4.3 x 10 The measured sheet resistance of the coating was 239 ohms/sq. Example 3 Following the procedure of Exs. 1 and 2, small variations in the concentrations of MBTC, TFA, air and water corresponding to M values below and above 50,000 were tested and recorded in the graph of FIGURE 2. Below 50,000 the sheet resistance was measured as substantially a minimum and constant value of about 30 ohms/sq., while for M values greater than 20,000, the sheet resistance was substantially higher, and increased rapidly with increasing M values. The doped tin oxide coatings of the invention which are made within prescribed M values also are observed to have a minimum and constant sheet resistance over a wide range of deposition temperatures, whereas similar coatings made at higher M values (above 50,000) exhibit an increasing sheet resistance at different deposition temperatures. While the invention has been described with reference to certain embodiments thereof, it will be understood that changes and modifications may be made which are within the skill of the art.

Claims: CLAIMS : 1. An improved chemical vapor deposition method of producing a fluorine-doped tin oxide coating which has a minimum and constant sheet resistance under different process conditions, comprising: (a) forming a liquid coating composition which in cludes an organic fluorine dopant and an organotin compound, said composition comprising: (1) 1-30 wt.Z of an organic fluorine dopant wherein at least one fluorine atom is located alpha or beta to a functional group wherein carbon is bonded to oxygen selected from carboxylic acid, anhydride, ester, alcohol, ketone, acid halide, or ether; and (2) 70-99 wt.Z of an organotin compound, which is an alkyltin trichloride, a dialkyltin di chloride, an alkyldichlorotin acetate, a dialkylchlorotin diacetate, or an ester tin trichloride; or tin tetrachloride; (b) vaporizing said liquid coating composition into a wet carrier gas to form a vapor mixture of carrier gas, water, organic fluorine dopant and organotin compound; and (c) decomposing said vapor mixture on a substrate to form said coating, characterized in that: the vapor concentrations of said components are such that a parameter M, defined as: : M = (AIR) (HO) (OFD) (OJ where (AIR) is the concentration of the carrier gas, in moles, (H2O) is the concentration of water in the carrier gas, in moles, (OFD) is the concentration of organic fluorine dopant in the carrier gas, in moles, and (O) is the concentration of organotin compound in the carrier gas, in moles, has a value of less than 50,000, thereby to produce a fluorine-doped tin oxide coating having a minimum and constant sheet resistance for said values of M. 2. A process according to claim 1 wherein M has a value of 20,000 or less or claim 2, 3. A process according to claim 1/in which the sheet . of the,coating produced thereby resistance/is about L otimsisq. at a thlcicness or about 180-210 nm. any preceding 4. A process according to/claim in which the liquid coating composition comprises 2-10 wt.% of said organic fluorine dopant, and 90-98% of said organotin compound. claims 1 to 3. 5. A process according to any of/ wherein said liquid coating composition includesup/10 wt.Z of a polar organic compound. 6. A process according to claim 5 wherein said composition includes 2-10 wt.% of said organic fluorine dopant, 80-97 wt.Z of said organotin compound, and 1-10 wt.% of said polar organic compound. claim 5 or 7. A process according to/claim 6 wherein said polar organic compound is acetic anhydride, ethyl acetate or methylisobutylketone. any preceding 8. A process according to/6laim wherein said vaporization temperature is 100-400 C. . any precedinq Y. A process according tojcia1m wherein said deposition temperature is above 400" and below 700 C. 10. A process according to claim 1 wherein said substrate is glass. 11. The product of the process of claim 1 having a substantially minimum and constant sheet resistance with increasing deposition temperature. claims 1 to 10. 12. A process according to any of/. wherein said organotin compound is monobutyltin trichloride, methyltin trichloride, isobutyltin trichloride, dibutyltin dichloride, di-t-butyltin dichloride, butyldichlorotin acetate, butylchlorotin diacetate, or carbethoxyethyltin trichloride.

Inventors: LINDNER, GEORG H.
Applicants: M & T CHEMICALS, INC.
Application year: 1985
Main classification: C23C16
IPC codes: C03C17, C23C16