A MEDICINE-RELEASING AGENT

Abstract: This invention concerns a medicine-releasing agent which is prepared by wrapping up a medicine-polypeptide compound in a poly-α-amino acid membrane having an ap­ propriate permeability for medicine, which is also excellent in the affinity with living cellualr tissues. A copolymer con­ taining a glutamine with hydrophilic radicals and another glutamine with hydrophobic radicals in the molar ratio of 1/­ 9-3/7 is favorably used as the poly-α-amino acid membrane mentioned above. For about a month after the medicine-­ releasing agent is embedded in a living tissues, for example as much as 50 % of the medicine is recognized to dissove out through the membrane at a constant rate; at the same time, a carrier of the medicine is also found to assimilate in the living tissues perfectly.

Description: A Medicine-Releasing Agent Field of the Invention This invention relates to an agent which permits a medicine carried therein to slowly dissolve in living tissues. More paticularly, this invention pertains to an agent that can release a compounded medicine in living tissues extending over a few months for example, which is not only excellent in the assimilation and the affinity with cellular tissues but widely improved in the durability of the medicinal efficacy. . r... Description of the Prior Art For example, in order toRincrease the medicinal efficacy against' cancer and lessen the undesirable side effect as much as possible, it is considered most effective from the chemotherapeutic point of view to embed a certain kind of carrier impregnated with a carcinostatic substance near an affected part by conducting an operation.. -.For this reason, recently carriers aimed at such effect have been increasingly used as they release impregnated medicines slowly. At present, natural polymers such as gelatin, agar and cellulose derivatives or synthetic polymers such as vinyl acetate, polymethyl methacrylate and polyvinyl alcohol are used as carriers. However, natural polymers liberate medicine so too easily that they are inferior in the durability of medicinal efficacy; contrary to this, synthetic polymers have problems in the affinity with living tissues and the easiness of assimilation in a living body. Summary df t,he Invention Under the circumstances, the present inventors made an extensive study to eliminate the above drawbacks and found. that a poly- < -amino acid having hydrophilic radicals and hydrophobic radicals together shows an appropriate permeability for medicine; and the rate of the permeability depends on the content of hydrophilic radicals. They have thus finally accomplished the present invention. Accordingly, it is an object of the present invention.to provide a medicine-releasingagent not only superior in the assimilation for and affivity with cellualr tissues in a living body but improved in the durability of the medicinal efficacy. The.sbove object is able to be accomplished by a medicine-releasing agent having a three-layered structure formed by wrapping up a medicinal compound which is prepared from a solution mixture composed of a medicine and a synthetics natural polypeptide in a poly-4 -amino acid membrane which has an appropriate permeability for medicine. Brief Description of the Drawings Figs. 1 and 3 are a schematic diagram showing a production process of the medicine-reasing agent according to the present invention. Figs. 2 and 4 are a graph showing a progress that the medicine-releasing agent produced in accordance with Example 1 and Example 2 releases a compounded medicine with the 'passage of time. Detailed Description of the Invention In the present invention, a poly--amino acid that has an good affinity with living cellular tissues and an appropriate permeability for medicine, which is employed to wrap up a medicinal compound therein, is a copolymer that has hydrophilic radicals and hydrophobic radicals together as shown by the following structural formulae, of which molecular weight is about 100,000-200,000. (1) Copoly(g -benzyl-L-glutamyl-L-glutamic acid) EMI3.1 (2) Copoly( r-benzyl-L-glutsmyl-N5-hydroxyalkyl-L-glutamine) EMI4.1 (3) Copoly(r-benzyl-L-glutamyl-N5-dihydroxyethylaminopropyl- L-glutamine) EMI4.2 where x stands for the molar number of hydrophilic radicals. The optimal value of x is different from medicine to medicine according to their molecular weight as they are allowed to pass through the copolymer membrane, but it commonly ranges from 0.1 to 0.3. In connection with this the present inventors have already published a synthesizing process for copolymers of this kind in Journal of Polymer Science, Polymer Chemistry Edition, 21, 1289-1303, (1983). In this invention, generally speaking, a natural/synthetic polypeptide is used for the sake of carrying a medicine and forming a compound therewith. However, considering good affinity with living cellular tissues and easiness of assimilation in a living body, poly-d -amino acid homologues, atero collagen and succinylated collagen are desirable, and yet copolymers represented by the above formulae 1, 2 and 3 are preferable among the poly-o(-amino acid homologues. Besides, a water-soluble poly--amino acid can also be employed so long as a water-soluble medicine is employed. (4) Poly(N5-hydroxyalkyl-L-glutamine) EMI5.1 It would rather be said that if only a medicine can form a compound together with the polypeptide mentioned above, there is no other restriction in particular for what kind of medicine to be used. For example, carcinostatic substances such as 5-fluorouracil (5-FU), adriamycin, cispratin, pepleomycin, etc. and steroid hormones such as pledonisolon, estradill, etc. can be enumerated here only for illustration. In the meanwhile, as a result of having examined the relation between the value of x and the permeability for medicine by the employment of a copoly(r -benzyl-L-glutamyl N5-dihydroxyethylaminopropyl-L-glutamine) membrane of thickness 20 um, whose chemical structure is shown by the formula (3), it becomes clear that even a high molecular weight car cinostatic substance such as pepleomycin easily passes through the membrane in a few hours when x is 0.6. Therefore, the copolymer was considered improper for a permeable membrane to wrap up a medicine in according to this invention. However, when x is 0.3, the copolymer membrane allows a low molecular weight medicine to pass through in a few hours and allows a high molecular weight medicine to pass through in a few weeks. From this, the copolymer proved beneficial and promising as a ,,membrane for wrapping up a high molecular weight medicine such as adriamycin and pepleomycin. Moreover, it was proved that when x is 0.2, the copolymer membrane can liberate a low molecular weight medicine extending over a few weeks; therefore, it proved suitable as a membrane for medicines with relatively low molecular weight such as 5-fluorouracil. Like this, as for copoly( -benzyl-L-glutamyl-L-glutamic acid) whose chemical structure is shown by the formula (1) or copoly( -benzyl-L-glutamyl-N5-hydroxypropyl-l-glutamyl) whose chemical structure is shown by the formula (2) (provided m is equal to 3 in this case), there is also an optimal value of x in terms of the membrane permeability which is closely related with the molecular weight of medicines. The medicine-releasing agent of this invention, characterized by having a three-layered structure, can for example be prepared as follows. That is, a medicinal compound which is to for'm,.Åa.,core of.the medicine-releasing agent is prepared by casting a solution mixture on a flat plate and evaporating a solvent therefrom, where the solution mixture is made up by mixing a poly-o(-amino acid solution with a medicine. Separately, a poly-ok -amino acid membrane having an appropriate permeability for medicine which is to form a coat of the medicinal compound is prepared from its solution similarly to the above. Next, the medicinal compound is wrapped up in the poly-ck-amino acid membrane; at this moment, a 801vent, such as chloroform or dimethyl formamide, which can swell or dissolve the poly-o,-amino acid is applied on the membrane a little to help it glue before pressing and. then dried. To how an example of its shape, the medicine-releasing agent of this invention is constructed of a medicinal compound of diameter 1020,,um and thickness 50-100,,um and an outer membrane of thickness 10-50 jim; consequently, the two elements form into a three-layered structure. A manufacturing process and a cross section of the medi cine-releasing agent are schematically shown in Fig. 1. The present invention will be understood more readily with referrence to the following examples; however, these examples are intended to illustrate the invention and are not to be construed to limit the scope of this invention. Example 1 At first, 0.5 g of predonisolon is dissolved in 10 ml of a dimethyl formamide solution containing copoly(r -benzyl-L 5 glutsmyl-N5-hydroxypropyl-L-glutamine) whose chemical structure is shown by the formula (2), of which x is 0.3 so as to make the polymer consistency equal to 5 girl. A sheet of a medicinal compound is made on top of a Teflon plate by casting the solution and evaporating the solvent thereon. The 2 medicinal compound having an area of 1 cm is cutoff from the sheet. Separately, a polymer membrane of thickness 10 pm is made on top of another Teflon plate from a dimethyl formamide solution containing copoly(r -benzyl-L-glutamyl-N5hydroxypropyl-L-glutamine) by casting the solution and evaporating the solvent. A medicine-releasing agent consisting of three layers is manufactured by wrapping up the medicinal compound in the polymer membrane. As a result of studying the amount of released predoni solon, it was proved that 50 percent of the medicine dissolves out in isotonic sodium chloraide solution for about a month at a constant rate, as shown in Fig. 2. Two other medicine-releasing agents composed of a core comprising predonisolon arid the poly-i-amino acid of the formula (1)/(2) and an outer membrane of copoly( r -benzyl- L-glutamyl-N5-dihydroxyethylaminopropyl-L-glutamine) individually gave a result similar to the above. Example 2 Two grams of succinylated collagen, which has been fully purified by a freeze-drying process, is dissolved in 80 ml of distilled water. A solution prepared by dissolving 1 g of pepleomycin in 20 ml of distilled water is added to the above solution with vigorous stirring by means of a homogenizer while the whole solution is being maintained below 20"C. There forms a cream-like viscqus white solution. The solution is spread on the bottom of a square stainless steel container having a side of 10 cm so as to make a sponge-like medicine-polymer compound by freeze-drying. A pillar of diameter about 10 mm is cut off from the sponge and shaped into 2 a disc by applying a pressure of 600 kg/cm . Separately, a membrane of thickness 30 jim is prepared from a dimethyl formamide solution which contains copoly( -benzyl-L-glutamyl N5-dihydroxyethylaminopropyl-L¯glutamine) by casting the solution flat on a Teflon plate and evaporating the solvent. The medicinal compound thus prepared in the form of a disc is wrapped in the polymer membrane to make up a medicinereleasing agent. This process is shown in Fig. 3. The medicine-releasing agent is soaked in isotonic sodium chloride solution at 37 OC to scrutinize how much medicine is released with the passage of time. The result is given in Fig. 4, from which it is proved that about 50 percent of pepleomycin dissolves ou,t of- t-he.polymer membrane for about a month at a constant rate. Example 3 5 Except that copoly( r -benzyl-L-glutamyl-NS-dihydroxy- ethylaminopropyl-L-glutamine), used in Example 2, is replaced by poly(N5-hydroxyethyl-L-glutamine), all the processes and the materials are left unchanged as in Example 2 to prepare a medicine-releasing agent. Example 4 The medicine-releasing agent prepared in Example 2is used to examine how much medicine is released therefrom in a living body. For the sake of this, after having been sterilized with ethylene oxide, the medicine-releasing agent is embedded in a subcutaneous tissue of the femur of mice. Mice are killed one after another 5 days, 10 days, 15 days, 20 days, 25 days and 30 days after the embedding of the medicine-releasing agent in order to determine the amount of pe pleomycin released in the tissue around the medicine-releasing agent. As a result of each determination, which is made on one gram of the taken-out tissue, it becomes obvious that a certain amount of pepleomycin is liberated from time to time from the medicine-releasing agent at a constant rate extending over a.m,onth. In this way, it becomes apparent that the.assimilation of the medicine-releasing agent is made very well in a living body since poly-i-amino acid, atero collagen or succinylated collagen is used as a carrier for medicine; what is more, the releasing rate of medicines is put under good control supported by an appropriate permeability of the membrane that depends on the amount of hydrophilic radicals contained in the poly-d,- amino acid. Specifically, when the amount of hydrophilic radicals is in the range about 10-20 percent, in other words, when the value of x is in the range 0.1-0.2, the membrane is fit for a medicine with low molecular weight. Furthermore, in terms of a medicine with high molecular weight, a membrane whose value of x is in the range 0.2-0.3 is used appropriately. As apparent from this, according to the present invention, the releasing rate of medicine can be varied at will by changing a molar ratio of hydrophilic radicals to hydrophobic ones in a poly-o, -amino acid to be used as an outer membrane. Besides, all the poly- i-amino acid of this inven tion intended for the use are so excellent that they would never be encapsulated by the surrounding cells with the result that they are eventually absorbed in them, together with a carrier for medicine a few months after embedded.

Claims: What We Claim Is 1. A medicine-releasing agent, which is characterized by having a three-layered structure formed by wrapping up a medicinal compound which is prepared from a solution mixture composed of a medicine and a synthetic/natural polypeptide in a poly-d -amino acid membrane which has an appr9priate .permeability for medicine. 2. A medicine-releasing agent according to Claim 1, in which said poly-d -amino acid is a copolymer containing hydrophilic radicals and hydrophobic radicals.

Inventors: KUBOTA, TETSUAKI, KUROYANAGI, YOSHIMITSU, MIYATA, TERUO, SENO, MANABU
Applicants: KOKEN CO. LTD.
Application year: 1985
Main classification: A61K9
IPC codes: A61K9, A61K47