LITHIUM ALUMINO-SILICATE GLASS CERAMICS

Abstract: Cerium dioxide or a cerate compound is proposed as a refining agent for β-eucryptite (a lithium aluminium silicate glass-ceramic material whose thermal coefficient of expan­ sion can be adjusted to near zero by controlled substitution and devitrification). Cerium dioxide and cerate refining agents enable transparent β-eucryptite to be obtained, which is useful in applications such as cooker hobs and also lasers. Hitherto, arsenic and antimony oxides, which are volatile at the refining temperature, have been used as refining agents.

Description: Lithium alumino-silicate glass-ceramics. The present invention relates to lithium aluminosilicate based glasses and glass-ceramic materials, that is to say glasses and glass-ceramic materials containing oxides of lithium, aluminium and silicon. The invention particularly relates to microcrystalline lithium aluminosilicate glass-ceramics which are transmissive to infrared and/or visible radiation and which contain 4-eucryptite solid solution as the principal crystal phase. P-eucryptite is a lithium aluminium silicate having a distorted hexagonal structure, in which some of the silicon lattice sites are filled by phosphorus and some of the lithium and aluminium lattice sites are filled by other metals. For example zinc and/or magnesium may substitute for aluminium and magnesium may substitute for lithium to an extent sufficient to balance the ionic changes. K -eucryptite has a negative thermal coefficient of expansion which can be altered in magnitude by varying the nature and degree of substitution in the lattice. In practice t-eucryptite is formed by controlled devitrification from the glass phase (which has a positive temperature coefficient) and the resulting glass-ceramic therefore has a thermal coefficient of expansion (typically near zero) which for a given proportion of-eucryptite (typically 70% by weight) is determined by the nature and degree of substitution in the /-eucryptite lattice. Tran9parent lithium alumino silicate glass-ceramics are particularly desirable materials, since their qualities of transparency, high strength and low thermal expansion make them useful for the construction of laser envelopes, mirrors, cooker hob plates and a wide range of other articles. However the production of transparent lithium ; alumino silicate glass-ceramics has hitherto presented considerable difficulties. It is in general necessary to refine any glass to remove batch and "seed" before it is solidified, if a transparent material is to be obtained. Hitherto, the only refining agents known to be suitable for the production of transparent lithium alumino silicate glass-ceramics have been arsenic and antimony oxides. These materials do not greatly affect the coefficient of thermal expansion of the solid material and do not greatly increase the rate of nucleation of the -eucryptite during the devitrification process. Accordingly glass-ceramics can be obtained in which the -eucryptite micro-crystals are typically in the order of 59*m or less in diameter, resulting in transparency to all. radiation of wavelength appreciably greater than this value. However arsenic and antimony oxides are appreciably volatile at the refining temperature (typically 1400 to 17000C) and their use requires considerable safety and environmental precautions. Cerium dioxide is known as a refining agent for glasses (see "Coloured Glasses by W.A. Weyl, published by the Society of Glass Technology, 1951) but it has not hitherto been used for the production of transparent lithium alumino silicate glass-ceramics. French patent application No. 2,173,694A relates to opal lithium alumino-silicate glasses containing cerium dioxide and small proportions of copper, silver or gold. These metals photosensitise the glasses and enable the glasses to crystallise and form glass-ceramics following exposure to UV radiation. All the examples disclosed incorporate antimony oxide as a refining agent. U.S.patent No. 3,454,386 discloses transparent lithium alumino-silicate glass-ceramic articles containing a very small proportion (0.05%) of cerium dioxide in combination with copper or a precious metal. Crystallisation is induced by irradiating the glass with high energy electrons, when the cerium present interacts with the copper or precious metal to form nucleation sites. In this patent it is stated that the exact role played by cerium in the glass is not clear. However the proportion of cerium dioxide present is much too low for it to have any appreciable refining action. Chemical Abstract No. 26,752 similarly discloses lithium alumino-silicate glass containing a small proportion (0.1%) of cerium dioxide, which is too low to give a significant refining action. Crystallisation induced by UV irradiation and heat tratment is disclosed, by a mech anism involving the Ce3+to Ce transformation during 4+ irradiation and the subsequent incorporation of Ce + ions into the Si-O framework on heating. UK Patent No. 1,366,701 (equivalent to French patent No. 2,137,870) in the name of THE ENGLISH ELECTRIC COMPANY LIMITED relates to low-melting point (1450 C to 1550 C) lithium alumino-silicate glasses with a high zinc content (7.5 to 9.0% ZnO) and containing up to 0.5% of one or more of the refining agents arsenic trioxide, antimony trioxide and cerium dioxide. Only one example of a glass incorporating cerium dioxide as the refining agent is disclosed, however, and this glass is described as brownish and opalescent in appearance. Thus there is no indication in this patent that an optically uniform lithium-alumino silicate glass or glass-ceramic can be produced by the method disclosed, or that batch and seed can be fully removed by adding cerium dioxide to the melt. We have found that transparent lithium alumino silicate glass-ceramics of low, reproducible thermal coefficient of expansion may be produced by refining molten lithium alumino silicate glasses with cerium dioxide and/or cerate compounds at somewhat higher temperatures than are disclosed in GB 1,366,701 and subjecting the refined glasses to a controlled thermal devitrification process. According to one aspect of the present invention, in a method of refining a molten lithium alumino silicate glass capable of controlled devitrification,rerium dioxide, or a cerate compound, or a cerium compound capable of reacting with said molten glass to form cerium dioxide is added in a proportion of at least 0.2% by weight (expressed in terms of cerium dioxide) to the molten glass and the resulting mixture is maintained in a molten state at a temperature of at least 15200C until it is substantially free from batch and seed. The refined glass may then be formed into any required shape and partially devitrified in a controlled heat treatment process to form a glass-ceramic article which contains ss-eucryptite as the principal crystalline phase and which is substantially transparent to infra-red and/or visible radiation. The glass may optionally be annealed (suitably at a temperature of 600 to 7000C for a period of up to two hours) after being formed into shape (which may be by any suitable glass-working technique, such as casting, drawing, pressing and rolling for example ) and before devitrification. The devitrification process may be carried out in a single stage by heating the glass at a rate not exceeding 5 0C per minute to a holding temperature between 750 C and 10000C and maintaining this temperature for at least fifteen minutes, as described in U.K. patent specification No. 1,022,681. The final fifteen minute holding stage may be curtailed considerably when thin-section glass articles (having a thickness of less than, say, soma) are devitrified. Alternatively a multi-stage process may be used, in which the temperature is raised at a rate not exceeding 50C per minute to a first holding stage in the range 6500C to 9000C, this holding temperature is maintained for at least 15 minutes, and then the temperature is raised, optionally through one or more further holding stages, to a final holding temperature in the range 80cho to 10000C. It is important to note that the optimum heating rates and number of holding stages in the heat treatment process are strongly influenced by the cross-section of the article being heat-treated. This arises not only from the need to ensure reasonable temperature homogeneity throughout the bulk of the article, with the. heat being applied to outer surfaces and in the context of a low thermal conductivity material, but also because considerable heat-effects can arise during precipitation of crystal phases. These latter effects can give rise to marked temperature rises within the material, leading to stressing and possible fracture. In order to overcome this, it is necessary with thick sections to allow periods of "stabilization" during heat-treatment, so that viscous flow in the residual glassy phase can relieve stresses as they develop. The above thermal effects are discussed by G. Partridge in the article "Nucleation and crystallisation phenomena in low expansion Li20-A1203-SiO2 glass-ceramics" - Glass Technology 23 (3),1982 pp 133-138. This article is hereby incorporated by reference. The rate of formation of R-eucryptite is dependant upon the nature and amount of nucleating agents present in the glass. Phosphorus, aluminium and titanium oxides are typical suitable nucleating agents. The proportion of cerium dioxide, cerate compound or cerium dioxide/cerate - forming compound added to the melt may be somewhat greater than the minimum required for refining purposes and will then influence the spectral transmission of the glass-ceramic particularly in the ultra-violet, reducing transmission in the UV and even moving the "UV cut-off" of the transmission curve into the visible blue. This ability, which is known for other glasses, has also been found to occur in the compositions of the present low expansion, transparent glass-ceramics when the proportion of cerium dioxide is greater than about 0.5% by weight, and can be of considerable advantage in a number of applications, for example cooker hob plates, where it is advantageous to limit transmission to the red end of the visible spectrum so that elements below the plate can be seen when on, but are obscured when off. It also enables the materials to be used where the passage of harmful UV radiation must be restricted. According to another aspect of the invention, a lithium alumino-silicate glass-ceramic containing microcrystallinep-eucryptite solid solution as the principal solid phase is characterised by being substantially free of arsenic and antimony and by being substantially optically uniform. The term "microcrystalline" is intended to include all mean crystal sizes less than lOOnm across. The term "optically uniform is intended to include transparency and other states where no appreciable light scattering on a microscopic scale occurs in the bulk of the material (the term "light" including visible and I.R. radiation) but to exclude opalescence and complete opacity. However where the glass-ceramic is required to be non-transmissive to particular wavelengths, oxides of iron, chromium, nickel, copper, cobalt, manganese, vanadium and other metals may be incorporated in glass-ceramic articles in accordance with this aspect of the invention. The glass-ceramic of this aspect of the invention may contain cerium dioxide or a cerate. The glass-ceramic preferably has a coefficient of thermal expansion in the range '25 x 10-7/0r over the temperature range 20 0C to 5000C and more preferably has a coefficient of thermal expansion in the range of ' 5 x 10 7/oC over the range 200 to 1000 and + 10 x 10-7/0r over the range of 200C to 7000C. The glass-ceramic may be in the form of a cooker hob. The coefficient of thermal expansion may be varied by adding controlled amounts of magnesium and/or zinc oxides to the melt and subsequently devitrifying the glass to a controlled extent. For the preparation of the glasses from which the various materials in accordance with the invention are prepared the following typical batch materials may be used, as appropriate, to provide the constituents of the glasses: Constituent Batch material SiO2 Good quality glass making sand, quartz. Li20 Lithium carbonate (Li2CO3), petalite (Li20.A1203.8SiO2) K20 Potassium carbonate (K2C03), potassium nitrate (KNO3). Na2O Sodium car bonate (Na2CO3), sodium sulphate (Na2S04). ZnO Zinc oxide (ZnO). MgO Magnesium oxide (MgO), magnesium carbonate (MgCO3). Constituent Batch Material A1203 Aluminium oxide (Al203), petalite. TiO2 Titanium dioxide (TiO2). Zero, Zirconium dioxide (ZrO2). P205 Metallic phosphate compatible with glass composition, ammonium phosphate. CeO2 Cerium dioxide (CeO2), appropriate cerates. It will be appreciated that the batch materials are not restricted to the above. Others may be used provided they are compatible with the composition and properties of the desired glass-ceramic. It will be further noted that, for certain applications, the batch constituents will need to be of high purity (for example minimum "Analar" grade) whereas for other applications normal commercial purities are acceptable. Examples of applications where high purity materials are required are where high transmission in the visible is required (e.g. laser envelopes, instrumentation) - high purity raw materials reduce the incidence of such oxides as iron oxide (Fe203) which would reduce transmission. Examples of applications where lower purity levels can be tolerated are--in applications where transmission in the visible may need to be restricted (e.g. coOker hob plates) although good transmission in the near infrared is advantageous. The batch materials are preferably chosen so as to result in glasses which have proportions of the constituents, inclusive of the nucleation catalyst expressed in terms of oxide constituents, falling within the following ranges: Wt.% SiO2 5.s-68.o Li2O 3.0- 4.5 K20 0- 3.0 Na2O O- 1.0 ZnO 0.5- 9.0(preferably 0.5 to 4.0) MgO 0- 2.0 A12 3 17.0-26.5 TiO2 0.5- 5.0 Zr02 0- 3.0 P205 0- 8.0 CeO2 0.2- 2.0 In addition to the above, it will be appreciated that other non-essential constituents are permissible in small quantities (up to about 5 weight percent) provided they do not hinder the melting or subsequent crystallization of the glasses to give glass-ceramics having the desired properties. Higher proportions of zinc oxide (4.0 to 9.0%) lower the melting point of the glasses. The low volatility of cerium dioxide in comparison with arsenic and antimony oxides is particularly advantageous when high melting point glasses (of low zinc content) are refined at temperatures above 1550 C for example. Where it is essential to control the transmission of the glass-ceramics, particularly in the visible part of the spectrum, as discussed above, then proportions of the following oxides, for example, can be included in the composition as given below, either alone or in combination: Fe2O3 0-1.0 ) ) Cr203 0.1.0 ) ) NiO 0-1.0 ) CuO 0-1 . O Total Co3O4 0-0.5 ) ) 0-2.0 Wt.% Mn3O4 0-1.0 ) V205 0-1.0 O Examples of glass-ceramic compositions falling within the above ranges are given in Table I. The batch materials were thoroughly mixed before melting and were melted in high alumina, alumino-silicate or platinum/rhodium alloy crucibles until the batch reactions were complete and the glasses were fully refined. The melting temperatures used ranged from 1520 0C to 1650 C and were so arranged as to enable the glass to be batch and seed free. After refining, which requires a period of up to 30 hours, the glasses may be shaped by the normal methods employed in glass working (e.g. casting, drawing, pressing rolling, etc.). The articles obtained may then be annealed at a suitable temperature in the range 6000C to 7000C for a period of up to two hours followed by slow cooling to room temperature. Alternatively the articles may be immediately subjected to the heat-treatment processes described above in order to achieve the required devitrification. Compositions, processes and properties of some glasses and glass-ceramics in accordance with the invention are shown by way of example in Figures 1 to 3 of the accompanying drawings, of which: Figure 1 (Table I) shows the constituents (in proportions by weight) of sixteen glasses in accordance with the invention, Figure 2 (Table II) shows the properties of variousglass-ceramics obtained by heat-treating the above glasses in various ways, and Figure 3 is a plot of transmission:wavelength for a glass ceramic in accordance with the invention and two prior-art glass-ceramics. The Tables are generally self-explanatory, but it will be noted that in each case the glass-ceramics obtained are transparent or nearly so and have coefficients of thermal expansion (sot) which approximate to zero. The precise details of the required heat treatment will depend on the shape and size of the required article and the heat-treatment holding stages listed in Table II are for the purpose of general guidance only. However one specific heat treatment suitable for converting thick pieces of glass No. 3 into transparent low expansion glass-ceramic articles is as follows: (i) Heat at 40C/minute to 7000C (ii) Maintain at 700 C for 24 hours (iii) Heat at 20C/minute to 7400C (iv) Maintain at 7400C for 24 hours - (v) Heat at 20C/minute to 8000C (vi) Maintain at 800 C for 12 hours. (vii) Allow to cool at the natural cooling rate of the furnace but at a rate not exceeding 4 C/minute. In Table II the glass-ceramics numbered l.)to 14.) correspond to the glass compositions 1.) to 14.) listed in Table I. In two cases (glass compositions 3.) and 13.)) various glass-ceramics of the same composition are shown; whose properties differ accoring to the heat treatment applied to the glass. Glass-ceramic 13.)a) has particularly suitable properties for use as a hot-plate material,namely a low thermal coefficient of expansionot,a high crossbreaking strength and a high I.R. transmissivity with a sharp UV cut-off. A plot of % transmission:wavelength for this glass-ceramic (as measured on a 4mn thick hotplate with corrections for losses due to reflection) is shown in Figure 3, with similar plots relating to two comparable prior art hot-plates shown for comparison. The hot-plate in accordance with the present invention is highly transmissive in the red region.(0.6 to 1.0Mm), making the hot plate element visible when it is switched on. This is an important safety aspect.

Claims: CLAIMS 1. A method of refining a molten lithium alumino silicate glass capable of controlled devitrification, characterised in that cerium dioxide, or a cerate compound, or a cerium compound capable of reacting with said molten glass to form cerium dioxide, is added to the molten glass in a proportion of at least 0.2% by weight (expressed in terms of cerium dioxide) and the resulting mixture is maintained in a molten state at a temperature of at least 1520C until it is substantially free from batch and seed. 2. A method according to Claim 1, characterised in that the refined glass is formed into shape and partially devitrified in a controlled heat treatment process to form a glass-ceramic article which contains -eucryptite as the principal crystalline phase and which is substantially transparent to infra-red and/or visible radiation. 3. A method according to Claim 2, characterised in that the glass is annealed in a separate annealing stage after being formed into shape and before devitrification. 4. A method according to Claim 2 or Claim 3, wherein the devitrification process is carried out in a single stage by heating the glass at a rate not exceeding 5a°C per minute to a holding temperature between 7500C and 10000C. 5. A method according to Claim 2 or Claim 3 wherein a multi-stage devitrificatipn process is used, in which the temperature of the glass is raised at a rate not exceeding 50C per minute to a first holding stage in the range 650 C to 900 C, this holding temperature is maintained for at least 15 minutes, and then the temperature is raised to a final holding temperature in the range 8000C to 10000C. 6. A method according to Claim 5 wherein said temperature is raised from said first holding stage via one or more further holding stages. 7. A method according to any preceding Claim1 wherein the proportion ot cerium dioxide, cerate compound or cerium dioxide/cerate-forming compound added to the melt is equivalent to at least 0.56 by weight expressed in terms of cerium dioxide. 8. A lithium alumino-silicate glass-ceramic containing;, microcrystalline w -eucryptite solid solution as the prin- cipal solid phase, said glass-ceramic being substantially free of arsenic and antimony and being substantially optically uniform. 9. A glass-ceramic according to Claim 8 containing one or more transition-metal oxides in a proportion sufficient to selectively absorb radiation of certain wavelengths. 10. A glass-ceramic according to Claim 9, incorporating an oxide of at least one of the metals iron, chromium, nickel, copper, cobalt, manganese and vanadium. 11. A glass-ceramic article according to any of Claims 8, 9 and 10 and having the following composition by weight expressed in terms of oxide constituents: SiO2 54 to 68% Li2O 3.0 to 4.5% K20 0.0 to 3.0% Na2O 0 to 1.0% ZnO 0.5 to 9.0% MgO O to 2.0% A1203 17.0 to 26.5% TiO2 0.5 to 5.0% ZrO2 0 to 3.0% P205 0 to 8.06 CeO2 0.2 to 2.0% together with up to 5% by weight of additional or incidental constituents which do not adversely affect the melting or crystallisation behaviour of the glass to a substantial extent. 12. A glass ceramic article according to Claim 11 wherein the proportion of zinc expressed in terms of zinc oxide is between 0.5 and 4.0% by weight. 13. A glass-ceramic as claimed in any of Claims 8 to 12 having a coefficient of thermal expansion of between + 25 x 10 -7/ C over the temperature range 20 C to 500 C. 14. A glass-ceramic as claimed in Claim 13 having a coefficient of thermal expansion between # 5 x 10-7/ C over the temperature range 200C to 1000C and between + 10 x 10-7/OC over the temperature range 200C to 7000C. 15. A glass or a glass-ceramic article having a composition substantially in accordance with any one of the compositions listed in Table 1. 16. Cooking hob composed of a glass-ceramic as claimed in any of Claims 8 to 15. 17. A cooker incorporating a cooking hob as claimed in Claim 16. 18. A laser incorporating a glass-ceramic as claimed in any of Claims 8 to 15.

Inventors: PARTRIDGE, GRAHAM
Applicants: THE ENGLISH ELECTRIC COMPANY LIMITED
Application year: 1985
Main classification: C03C1
IPC codes: C03C10, C03B5, C03C1, C03B32