A PROCESS FOR PREPARING A COMPOSITE LAMINATE FILM

Abstract: Disclosed herein is a process for preparing a composite laminate film comprising pressure-laminating at least two mutually different films to each other via an adhesive agent of urethanes, which contains microcapsules enclosing a hardening-accelerator.

Description: BACKGROUND OF THE INVENTION: The present invention relates to a process for preparing a composite laminate film, and more in detail, relates to a process for preparing the composite laminate film, comprising pressure-laminating at least two mutually different films to each other via an adhesive agent of urethanes (hereinafter referred to as "urethane adhesive"), which contains microcapsules enclosing a hardening-accelerator, thereby obtaining the composite laminate film. Although plastic films have come to be indispensable material for packaging various articles, the performance demanded for the plastic films used for packaging has come to be strict and numerous day by day, and at present, such performance cannot be provided by a single film. Accordingly, various multi-layered films are utilized for satisfying the demanded performance as a whole. In this case, to the adhesives used for preparing the multi-layered film, there are various demands other than adhesive strength, for instance, heat-resistance, transparency, etc., and in this point, urethane adhesive has been used as the adhesive for various laminate films because of the excellent performance thereof. However, the problem in using a urethane adhesive is that the hardening speed thereof is very low and accordingly, a specified preparation of the laminate film is carried out in ner such as that comprising winding up the laminated film zilch the a adhesive is not yet hardened and aging the thus ::d laminate film in a reaction chamber at a high temperature, ereby completing the hardening of the adhesive. Such a process of preparing the laminate film demands large factory-site and it takes a long time period for the eparation of the laminate film. Accordingly, trials have been carried out for acelerating the hardening of urethane adhesives. One of the -rials is the adoption of a higher temperature in the reaction, however, in the case where laminating is carried out at a higher temperature, a problem due to the difference of the rates cf expansion of the plastic materials to be adhered together las occurred, and there is a demerit that it is very difficult maintain the plastic material at such a high temperature, and as a result, this method is not a practically sufficient * for solving the problem of aging the not-yet hardened adhesive in the laminate film. In addition, there is a method of admixing a hardening-accelerator with the urethane adhesive, however, by ris method, the adhesive composition in which the hardening accelerator has been mixed hardens to a certain extent before me use of the adhesive composition and accordingly, it is .cessary to add the hardening-accelerator to the urethane restive every time in preparing the composite laminate film. Purthermore, the monomer for preparing the urethane adhesive is generally high in viscosity and a complicated operation in preparing the adhesive is required. Accordingly, this method is not practical. In short, since there is no practical and effective countermeasure for accelerating the urethane adhesive, an effective solution thereof has been strongly demanded. In consideration of the above-mentioned conditions, the present inventors have studied the method for completing the preparation of laminate films within a shorter time period by the use of the urethane adhesive, and as a result, they have attained the present invention. Namely, the purpose of the present invention is to satisfy the thus demanded various performances in the plastic films for packaging and to provide a process for preparing the laminate film which can solve the above-mentioned various demerits of the conventional process. SUMMARY OF THE INVENTION: In an aspect of the present invention, there is provided a process for preparing a composite laminate film, comprising pressure-laminating at least two mutually different films to each other via a urethane adhesive containing microcapsules enclosing a hardening-accelerator. DETAILED DESCRIPTION OF THE INVENTION: The characteristic feature of the present invention lies in the step of pressure-laminating at least two mutually different plastic films to each other via a urethane adhesive which contains microcapsules enclosing a hardening-accelerator, thereby obtaining a composite laminate film comprising two mutually different plastic films adhered together via the adhesive agent. Namely, the present invention is based on the finding that when the hardening-accelerator for the urethane adhesive is microencapsulated, and after adding and dispersing the microcapsules into the urethane adhesive the thus obtained urethane adhesive containing the microcapsules is used for adhering the two mutually different plastic films to each other, the urethane adhesive containing the microcapsules does not harden before the use thereof and after breaking the microcapsules by pressure-laminating, the hardening-accelerator hardens the urethane adhesive extremely rapidly. Namely, in the present invention, as the adhesive, a urethane adhesive containing microcapsules which is prepared by dispersing a suitable amount of the microcapsules enclosing a hardening-accelerator for a urethane adhesive in the urethane adhesive is used, and the preferable amount of the microcapsules dispersed into the urethane adhesive is in the range of from 0.05 to 5% by weight of the urethane adhesive. The preferable size of the microcapsule is in the range of from 3 to 50 micrometers. As the hardening-accelerator, any publicly known hardening-accelerator may be used. Those tin compounds of a large accelerating effect, for instance, dioctylt3n diiso-octylthioglycolate, dioctyltin maleate, dioctyltin dilaurate, dibutyltin dimaleate, dibutyltin dilaurate and the like are preferably used. The composition of the urethane adhesive which contains the microcapsules enclosing the hardening-accelerator is not restricted. However, as the polyol component which is one of the components of urethane adhesive, for instance, polyol-prepolymer such as polyhydroxypolyester obtained from polybasic acid and hydroxy compound or polyether glycol, or polyvalent alcoholic monomer such as ethylene glycol, diethylene glycol, 1,4-butanediol, 1,5-pentanediol, etc. may be used. As isocyanate which is another component of the urethane adhesive, for instance, tolylene diisocyanate, tolidine diisocyanate, naphthylene diisocyanate, diphenylmethane diisocyanate, etc. or polyisocyanate obtained by preliminarily polycondensing one of the above-mentioned isocyanates may be used. As a diluent of or a viscosity-regulator for the urethane adhesive, a low-boiling solvent such as ethyl acetate, methyl ethyl ketone, toluene and the like is used for improving the applicability of the urethane adhesive. Microencapsulation of the hardening-accelerator which is added to the urethane adhesive of the present invention can be carried out in the case where the hardening-accelerator is possibly microencapsulated and accordingly, any publicly known method for microencapsulation by single membrane or composite membrane comprising membrane of polyurethane, urea-resin, melamine resin, phenol resin, epoxy resin, polyamide resin, gelatin, etc. can be applied. For example, a microcapsule enclosing the hardeningaccelerator is produced by dispersing the hardening-accelerator in an aqueous medium containing a water-soluble cationic urea resin, at least one prepolymer selected from the group consisting of melamine-formaldehyde prepolymer, urea-formaldehyde prepolymer and melamine-urea-formaldehyde prepolymer, and a low molecular weight anionic surfactant selected from the group consisting of salts of aliphatic acids, sulfate esters of higher alcohols and salts of alkylarylsulfonic acid and polycondensing the water-soluble cationic urea resin and the prepolymer by adding an acid catalyst, while causing complexcoacervation between the water-soluble cationic urea resin and the low molecular weight anionic surfactant. According to the present invention, one of the two plastic films to be laminated together is painted with the urethane adhesive containing the microcapsules enclosing the hardening-accelerator, and after superposing another plastic film on the thus painted plastic film, the thus superposed film is given pressure on, thereby breaking the microcapsules and making the thus freed hardening-accelerator react to the urethane adhesive to complete the lamination of the two plastic films mutually different from each other. The pressure for breaking the microcapsules depends mainly on the method for microencapsulation, however, in many cases, it is in the range 2 of from 3 to 30 kg/cm The merit of using the microcapsules enclosing the hardening-accelerator for the urethane adhesive according to the present invention is the remarkable reduction of the time for hardening of the urethane adhesive, of course, and in many cases, the adhesion is completed within 10 to 24 hours at ambient temperature of 400C. In addition, the temperature of painting the urethane adhesive on the plastic film may be raised. Accordingly, the solvent is more easily removed from the painted membrane to improve the operability of painting. Furthermore, it was unexpectedly found that the thus prepared composite laminate film is excellent in transparency as compared to the composite laminate film prepared without using the hardening-accelerator. The present invention will be definitely explained while referring to the examples of preparation of the microcapsules used according to the present invention and the examples of preparing the composite laminate films according to the present invention as follows. PREPARATION EXAMPLE OF MICROCAPSULES CONTAINING HARDENING ACCELERATOR Into a mixture of 300 g of urea and 730 g of an aqueous 37% solution of formaldehyde, 3 g of triethanolamine were added, and the thus formed mixture was reacted for 60 min at 700C, to obtain a prepolymer of urea-formaldehyde resin. A liquid mixture was prepared by mixing 100 g of the thus obtained prepolymer, 20 g of a water-soluble cationic resin (uramin X -P-1500 (an aqueous 38% solution, made by Mitsui-Toatsu Co., Ltd.)), 200 g of water and 10 g of an aqueous 10% solution of triethanolamine, and after adjusting the pH of the liquid mixture to 5.2 by an aqueous 10% solution of citric acid, 3 g of an aqueous 10E solution of sodium alkylbenzene sulfonate (aqueous solution of Neoperex C made by Kao-Atlas Co., Ltd.) were added to the liquid mixture. Then, the total amount of the thus prepared mixture and 1000 g of dibutyltin dilaurate as the hardening-accelerator were subjected to emulsification in a homogenizer, thereby preparing an emulsion of liquid particles of 2 to 8 micrometers in diameter. The thus formed emulsion was warmed to 500C while gently stirring thereof, and the pH of the emulsion was made to 2.8 by further adding the aqueous 10% solution of citric acid. After stirring the emulsion for one hour, it was cooled to room temperature, and by continuing the agitation, a slurry of microcapsules was obtained. By passing the slurry through a membrane-filter, microcapsules were collected, washed with water and dried in a hot air dryer at 380C to obtain 210 g of powdery microcapsules. EXAMPLE 1: Preparation of a composite laminate film A uniform solution was prepared by admixing 10 kg of ethyl acetate with 2 kg of Nippon t -3004 (made by Nippon Polyurethane Co., Ltd.) and 10 kg of Colonate -L (made by Nippon Polyurethane Co., Ltd.), and the thus prepared solution was used as a urethane adhesive as follows. Namely, into the thus prepared solution of the adhesive, 150 g of the microcapsules which had been prepared as above and contains dibutyltin dilaurate were mixed, thereby obtaining the urethane adhesive containing microcapsules. After painting a nylon film of 20 micrometers in thickness and 600 mm in width with the thus prepared urethane adhesive containing microcapsules by using a gravia-coater, ethyl acetate was evaporated off from the thus painted film in a hot-air dryer at 70 C, and a polypropylene film of 20 micrometers in thickness and 600 mm in width was superposed onto the thus painted nylon film while using a pair of rolls under a pressure of 4 kg/cm2, thereby breaking the microcapsules and releasing dibutyltin dilaurate. Then, the thus superposed film was rolled up and the thus rolled film was kept for 24 hours in a room at 420C to permit the adhesive to harden completely, thereby obtaining a te laminate film comprising the nylon film, the adhesive the polypropylene film. For carrying out comparison, another composite innate film was prepared in the same procedures except for sing the microcapsules, as follows. COMPARATIVE EXAMPLE 1: Preparation of a composite laminate film without using microcapsules A composite laminate film was prepared in quite the emSe procedures as in Example except for not using microcapsules. The results of examination of the properties of the -us prepared two composite laminate films (in Example and in comparative Example) are shown in Tables 1 and 2 below. Table 1 Adhesive strength of the laminate film after 24 hours EMI10.1 <tb> <SEP> Product <SEP> prepared <SEP> in <SEP> Peel <SEP> strength <SEP> by <SEP> Tensilon <SEP> tester <tb> Exapmle <SEP> 1 <SEP> Film <SEP> was <SEP> cut. <SEP> larger <SEP> than <SEP> 6000 <SEP> g <SEP> / <SEP> 25 <SEP> mm <tb> Comparative <SEP> 125 <SEP> g <SEP> / <SEP> 25 <SEP> mm <tb> Example <SEP> 1 <tb> Table 2 Physical properties after 5 days of preparation EMI11.1 <tb> <SEP> Transmittance <SEP> of <tb> Product <SEP> in <SEP> Haze* <tb> <SEP> parallel <SEP> light <tb> Example <SEP> 1 <SEP> 90.3 <SEP> 3.4 <tb> Comparative <SEP> 87.9 <SEP> 5.0 <tb> Example <SEP> 1 <tb> (Note) Haze is measured by HAZE METER (Model: TC-HII type) made by Tokyo Denshoku Co., Ltd. As are seen in Tables 1 and 2, the hardening speed of the adhesive was remarkably raised by the process of the present invention, and the physical properties of the composite laminate film according to the present invention was superior to those of the composite laminate film prepared without using the microcapsules enclosing the hardening-accelerator. PLE 2: A uniform solution as a urethan-adhesive was prepared admixing 9 kg of NipporanR 3124 (made by Nippon Polyurethane LTD.) and 1 kg of ColonateR HL (made by nippon Polyurethane LTD.) with 10 kg of ethyl acetate, and with the thus formed ran-adhesive, 80 g of the microcapsules including dibutyltin nitrate as those obtained in Example 1 were admixed to prepare -e urethane adhesive containing microcapsules. After painting a polyethylene terephthalate film of mm in width and 20 micrometers in thickness with the thus pared urethane adhesive containing microcapsules by using - gravia-coater, ethyl acetate was evaporated off from the thus tainted film in a hot-air dryer at 700C, and an aluminum foil of 600 mm in width and 9 micrometers in thickness was superposed onto the painted surface of the polyethylene terephthalate film. hereafter, the naked aluminum surface of the thus prepared composite material was painted with the same urethane adhesive containing microcapsules by using a gravia-coater and ethyl acetate in the thus painted urethane adhesive containing acrocapsules was evaporated off from the thus painted film a 3 hot-air dryer at 700C. Then, polypropylene film of 600 mm < @ width and 60 micrometers in thickness was superposed on the thus just painted surface of the aluminum foil as a component the composite film. In this connection, the thickness of e layer of the urethane adhesive containing microcapsules was Dut 3 micrometers after evaporation of ethyl acetate. The roll-pressure in superposing the polypropylene film on the aluminum foil was 3 kg/cmê thereby breaking the microcapsules in the layer of the urethane adhesive containing microcapsules between the polypropylene film and the aluminum foil and releasing the hardening accelerator, dibutyltin dilaurate from the thus broken microcapsules into the adhesive. The thus obtained laminate composite material in a rolled up state was kept in a chamber at 420C for 24 hours to effect complete hardening. COMPARATIVE EXAMPLE 2: For comparison, a laminate material was prepared by the same procedures as in Example 2 except for not using the microcapsules including dibutyltin dilaurate, and the physical properties of both the laminate materials were determined, the results being shown in Table 3. Table 3 EMI14.1 Reactivity <SEP> test <SEP> Boiling <SEP> test <tb> Example <SEP> or <tb> Rate <SEP> of <SEP> uncreated <SEP> isocyanats <SEP> Change <SEP> of <SEP> appearance <SEP> after <SEP> Adhesive <SEP> strength <SEP> before <tb> Comparative <tb> group <SEP> in <SEP> the <SEP> laminate <SEP> composite <SEP> immersing <SEP> the <SEP> laminate <SEP> com- <SEP> and <SEP> after <SEP> boiling <SEP> test <tb> Example <tb> material <SEP> (%) <SEP> posite <SEP> material <SEP> in <SEP> water <SEP> at <SEP> (kg/25 <SEP> mm) <tb> 100 C <SEP> for <SEP> 30 <SEP> min <tb> before <SEP> after <tb> Example <SEP> 2 <SEP> 28 <SEP> almost <SEP> unchange <SEP> 2.5 <SEP> 2.3 <tb> Comparative <tb> The <SEP> surfaces <SEP> of <SEP> the <SEP> material <tb> 60 <tb> Example <SEP> 2 <SEP> became <SEP> uneven <SEP> with <SEP> a <SEP> partial <SEP> 1.5 <SEP> 0.3 <tb> exfoliation <SEP> of <SEP> film(s) <tb>

Claims: WHAT IS CLAIMED IS: 1. A process for preparing a composite laminate film, comprising pressure-laminating at least two mutually different films to each other via a urethane adhesive containing microcapsules enclosing a hardening-accelerator. 2. A process according to claim 1, wherein an amount of the microcapsules dispersed into the urethane adhesive is in the range of 0.05 to 5% by weight of the urethane adhesive. 3. A process according to claim 1, wherein the hardening-accelerator is selected from the group consisting of dioctyltin diiso-octylthioglycolate, dioctyltin maleate, dioctyltin dilaurate, dibutyltin dimaleate and dibutyltin dilaurate.

Inventors: IGARASHI, YURIKO, OKADA, YOSHIO
Applicants: KUREHA KAGAKU KOGYO KABUSHIKI KAISHA
Application year: 1985
Main classification: B32B7
IPC codes: B32B7, B29C65, C08G18, C09J175, C08K9, C08J3, B32B27, C08J5