POLYVINYL ALCOHOL ALLOYS

Abstract: A polymer alloy is prepared by reacting a polyvinyl alcohol polymer having a degree of hydrolysis of less than 98 mole percent with less than the stoichiometric amount of a functional olefin polymer containing functional groups which are reactive with the hydroxyl groups of the polyvinyl alcohol polymer whereby there is obtained a mixture of grafted and ungrafted polyvinyl alcohol polymers, the grafted polyvinyl alcohol polymer having less than all the available hydroxyl groups reacted with said functional groups. This polymer alloy may be blended with a compatible olefin homo- or co-polymer blending resin.

Description: This invention is concerned with polyvinyl alcohol alloys which have a desirable combination of physical characteristics. Polyvinyl alcohol (PVA) has the lowest gas permeability of any polymer yet synthesized and has been widely used as a gas barrier material, especially as an oxygen barrier material. Commercial polyvinyl alcohols have several failings, however. Due at least in part to their high polarity, their melting points are close to their decomposition points and they are thus not melt extrudable. Most films are cast from water or use large percentages of a polyhydric alcohol or polyethylene oxide (with or without added water) to plasticize the melt so that extrusion can be effected. Prior PVA polymers absorb relatively large quantities of moisture. The presence of moisture in turn raises the oxygen permeability of the polymers drastically. One known approach to alleviating these difficulties has been to introduce hydrocarbon units, especially ethylene units, into the chain of the polymer. The resulting materials are known as ethylene-vinyl alcohol (EVOH) copolymers. EVOH copolymers have been used very successfully in a number of commercial applications, but are quite expensive. In addition, close control of composition and elimination of homopolymer by-products are required in the production of EVOH copolymers. A broad distribution of ethylene results in poor water vapor transmission rate properties. The presence of homopolymer leads to a tendency to develop gel specks and/or burn spots during the extrusion process. We have now developed polyvinyl alcohol alloys which have excellent gas barrier characteristics without high sensitivity to water, which are relatively inexpensive, have a melting point below their decomposition point so as to allow melt extrusion, and have reduced moisture absorption characteristics. According to the present invention, there is provided a polymer alloy which is prepared by reacting a polyvinyl alcohol having a degree of hydrolysis of less than 98 mole percent and a degree of polymerization of from 300 to 900 with less than the stoichiometric amount of a functional olefin polymer containing functional groups which are reactive with the hydroxyl groups of the polyvinyl alcohol, at least 70% of the combined weights of the polyvinyl alcohol and the functional olefin polymer being constituted by the polyvinyl alcohol, whereby there is obtained a mixture of grafted and ungrafted polyvinyl alcohol polymers, the grafted polyvinyl alcohol polymer having less than all the available hydroxyl groups reacted with said functional groups and the proportion of unreacted hydroxyl groups being such that the polymer mixture is melt extrudable. As indicated, the mixture of grafted and ungrafted PVA is produced by reacting a quantity of ungrafted PVA with an olefin polymer having functional groups which are reactive with the hydroxyl groups of PVA. The backbone of the functional polymer is an olefin homopolymer or copolymer, and the monomer containing functional groups may form part of the backbone or be present as side chains. The amount of the functional polymer is selected such that substantially less than all the available hydroxyl groups on any given PVA chain are reacted, and such that a substantial proportion of the available PVA chains remain ungrafted. If too high a proportion of available hydroxyl groups are reacted, the mixture will be rendered unprocessable due to an extreme rise in viscosity and a decrease in melt index (MI) resulting from cross-linking and gelling of the PVA, It has been found that such limited grafting of PVA to provide a physical mixture of grafted and ungrafted PVA results in an alloy material exhibiting excellent moisture resistance and good separation of the melting and decomposition points, without a significant loss of gas barrier properties. Melt blending of the mixture of grafted and ungrafted PVA with a compatible polyolefin blending resin results in the addition of increased hydrocarbon characteristics to the blend, thus increasing moisture resistance, while retaining desirable processability characteristics. The Polyvinyl Alcohol Polymer Polyvinyl alcohol polymers suitable for use in this invention are polyvinyl alcohol homopolymers or copolymers having a degree of hydrolysis of less than 98 mole percent and having a degree of polymerization (DP) of from 300 to 900. The use of PVA polymers having a degree of hydrolysis greater than 98 mole percent results in products having melting points sufficiently close to their decomposition points that melt processing is unfeasible. Preferably, the PVA should be from 70 to 90 mole percent hydrolyzed. The functional polymer Suitable functional polymers include any polyolefin which incorporates functional groups reactive with the hydroxyl groups of the PVA. Suitable functional groups include carboxylic acids, carboxylic acid anhydrides, metal salts of a carboxylic acid, derivatives of carboxylic acids, or mixtures of two or more such groups. Suitable polymers include graft copolymers based on an olefin homopolymer or copolymer backbone. Particular polyolefins suitable for use as graft copolymer backboned in this invention include polyethylene, ethylene copolymers, polypropylene, and propylene copolymers. Other copolymers useful as graft copolymer backbones include olefin-ester copolymers, such as ethylene-vinyl acetate, other ethylene-vinyl esters, ethylene-acrylate esters and ethylene-methacrylate ester copolymers. Specific examples of suitable function polymers include polyethylene and polypropylene homopolymers or copolymers grafted with maleic anhydride, ethylene-acrylic acid or ethylene-methacrylic acid random copolymers or ethylene-acrylic acid or ethylene-methacrylic acid ionomers, and ethylene-propylene, rubbers grafted with fumaric acid. Any unsaturated carboxylic acid or carboxylic acid anhydride can be used to form polyolefin graft copolymers suitable for use in this invention. Compoumds of this kind include for example, maleic anhydride, x-methyl bicyclo(2.2.1)-hept-5-ene-2,3-dicarboxylic anhydride (XMNA), bicyclo-(2.2.1)hept-5-ene-2,3-dicarboxylic anhydride, citraconic anhydride, itaconic anhydride, and 1,4-butenedioic acid monoalkyl esters. Dicarboxylic acids, monoester acid derivatives, or maleamic acids which can form these anhydrides or anhydride derivatives can also be used. Preferred functional olefin polymers for use in accordance with the invention are high density polyethylene homopolymers (HDPE) grafted with 1.5 wt. % XMNA; in the polymer alloys of the invention these are reacted, as stated above, with a least 70 wt. % of PVA. The carboxylic acid, anhydride, metal salt or other carboxylic acid derivative need not be grafted onto the polyolefin backbone of the functional polymer, but may be incorpored into the chain by copolymerization. Examples of copolymers suitable for use as acid functional polymers are ethylene-acrylic acid, ethylene-methacrylic acid, ethylene-alkyl acrylate-acrylic acid copolymers or ethylene-alkyl methacrylate-methacrylic acid copolymers and their partially neutralized salts (known as ionomers). Other useful copolymers are ethylene-vinyl acetate-maleic anhydride, ethylene-methylacrylate-maleic anhydride, ethylene-methylmethacrylate-maleic anhydride, ethylene-maleic anhydride, ethylene-monoester or maleic acid, ethylene-vinyl acetate-1,-4-butenedioic acid and its monoester, ethylene-alkyl acrylate-1,4-butenedioic acid and its monoester copolymers, and many other olefin combinations containing acid functionality such as the partially neutralized metal salt derivatives of these copolymers and maleamic acid derivatives. The blending resin The blending resin is an olefin homopolymer or copolymer which is compatible with the mixture of grafted and ungrafted PVA. Suitable blending resin polymers include, but are not limited to, high-, low- and medium density polyethylene, propylene homopolymers and copolymers of propylene and ethylene, including block and random ethylene-propylene copolymers and ethylene-propylene elastomers, and copolymers of ethylene with olefins such as hexene-1, octene-1 and butene-1, including those copolymers known as linear low density polyethylene, for example. The nature of the alloy and proportions of constituents Fourier Transform Infrared (FTIR) spectral analysis of typical alloys and alloy-forming reactants of the invention shows the disappearance of anhydride and the appearance of a new ester in the alloy at from 1225 cm⁻¹ to 1230 cm⁻¹. This new ester can be distinguished from the acetate ester resulting from unhydrolyzed acetate in the polyvinyl acetate homopolymers or copolymers from which the polyvinyl alcohols are prepared. This can be seen in the accompanying drawings, in which: Figure 1 is a Fourier Transform Infrared (FTIR) spectrum of a polyvinyl alcohol which is 87 mole percent hydrolyzed and which has a 4% aqueous solution viscosity of about 5 mPa · s at 20°C; Figure 2 is an FTIR spectrum of a graft copolymer comprising a polyethylene backbone grafted with x-methyl bicyclo(2.2.1 )hept-5-ene-2,3-dicarboxylic anhydride (XMNA); Figure 3 is an FTIR spectrum of a reaction product of the compounds of Figures 1 and 2; and, Figure 4 is an FTIR spectrum representing the subtraction of the spectra of Figures 1 and 2 from that of Figure 3. This demonstrates that a new material is formed and that this material is a reaction product (i.e. a graft copolymer between the PVA and the functional polymer) as opposed to a mere physical association between the PVA and copolymer. The functional level of the functional polymer is defined by the amount of carboxylic acid, anhydride, metal salt or derivative contained therein. If the functional level is too low, the reaction product will not give a useful alloy when blended with the polyolefin polymer. On the other hand, if the functional group level is too high, the viscosity of the blended product becomes so high as to hinder its practical processability. We do not wish to be held to this theory, but one possible reason for decreased flow characteristics could be chain extension and/or cross linking of the PVA by reaction with the functional polymer. The PVA-functional polymer reaction product acts as a compatibilizer to allow optional incorporation of a polyolefin blending resin into the reaction product to form other useful alloys. The presence of unreacted polyolefin blending resin as part of a physical mixture with the PVA alloy allows one to select the proportion of added blending resin and thus balance moisture resistance and gas barrier properties as desired. Without the polvolefin-grafted PVA, the addition of a polyolefin to a melt blend would result in macrophase separation, as demonstrated in the Examples below. In the alloys of the invention, microphases may exist without observable macrophase separation. As a result, the alloys may exhibit the appearance and behaviour of single phase, homogeneous polymer blends. The proportion of grafted PVA to ungrafted PVA, and the proportion of polyolefin blending resin to the mixture of grafted and ungrafted PVA, can be readily empirically determined by one skilled in the art. In general, the proportion of functional polymer in the alloy is selected to provide both a desired level of moisture resistance and desired gas barrier properties. The proportion of functional polymer should be sufficient to separate the melting and decomposition points of the alloy so as to allow melt processing, yet insufficient to result in gelling. If present, the compatible blending resin preferably constitutes from 1 to 15 wt.% of the alloy. The upper limit of the blending resin proportion is dictated by (1) desired gas barrier characteristics and water resistance properties and (2) the amount of functional polymer in the PVA mixture. This can be readily empirically determined and the use of too high a proportion of blending resin results in observable macrophase separation, as shown in the Examples below. The foregoing specific values are based on the use of HDPE homopolymer grafted with 1.5 wt.% of XMNA as the functional polymer. It will be appreciated that the properties of the alloy and the proportions of constituents vary with the choice of functional groups, functional polymer backbone, polyolefin blending resin, the hydroxyl content of the PVA polymer, and the molecular weight and melt index of each of the PVA polymer and the functional polymer. Moisture pickup measurements show that the functional polymer hydrocarbon chains reduce the moisture pickup of the alloys (see Table II below). Since oxygen permeability is affected by the amount of moisture absorbed, these alloys will have reduced oxygen permeability under high moisture conditions. Oxygen permeability measurements on dry PVA alloys show that they have excellent barrier properties against oxygen. The alloys have impermeability at least 100 times better than Mylar resins loriented polyethylene terephthalate) and nylon 6, which have heretofore been used in some barrier structures. Gas barrier films, sheets, tubings, coatings, bottles, profiles, etc. can be formed from these alloys by blown and cast extrusion, extrusion coating, coextrusion, coextrusion coating, injection molding, blow molding, rotomolding, compression molding, profile, pipe and tubing extrusion or a combination of these processes. These articles can be fabricated into pouches, bottles, pipe, tubing and other fabricated articles. Other shapes, articles and methods of fabrication for thermoplastics, blends and alloys for which the polymer alloys of the invention are suitable will be apparent to those skilled in the art. In order that the invention may be more fully understood, the following examples are given by way of illustration only. Example 1 a) 50 wt.% PVA (DP=330, 35 mole % hydrolyzed) and 50 wt.% HDPE graft copolymer (graft monomer=XMNA, 1.5 wt.% incorporated, MI=1.5 g/10 min.) were reacted in a Brabender mixer at 325°F (163°C) for 5 min. at 120 rpm. The reaction product, through use of FTIR spectral subtraction, shows the presence of bands at 1750 cm⁻¹ (carbonyl) and 1225 cm⁻¹ (carbon-oxygen) which can be related to an ester other than acetate. b) 80 wt.% PVA (87 mole % hydrolyzed, 4% aqueous solution viscosity at 20°C of 5 mPa · s) and 20 wt.% of the graft copolymer described in part a) above were blended in a Brabender mixer at 425°F (218°C) for 5 minutes at 120 rpm. The reaction product, through use of FTIR spectral subtraction, shows the presence of a band at 1229 cm⁻¹ (carbon-oxygen) which can be related to an ester other than acetate (see Figures 1-4). Example 2 30 wt.% PVA (DP=700, 74 mole % hydrolyzed) and 5 wt.% of the graft copolymer as described in Example 1 were reacted in the presence of 65 wt.% of an ethylene-butene-1 copolymer (MI=2, density=0.918 g/cc). The amount of anhydride found by FTIR is 0.014 wt.%. The amount of anhydride which would be present if no reaction occurred is 0.065 wt.%. Example 3 Alloys with the compositions listed in Table I, below, based on PVA "A" (87 mole % hydrolyzed, M w =10,000, 4% aqueous solution viscosity of 5 mPa · s), PVA "B" (74 mole % hydrolyzed, DP=600), and the graft copolymer described in Example 1, were submitted for FTIR analysis as described in Example 2. The results show that most of the anhydride of the graft copolymer has disappeared. The theoretical percent of anhydride in Table I shows the amount which would be present if no reaction occurred. Example 4 70-95 wt.% of the PVA and correspondingly 30-5 wt.% of the polyolefin graft copolymer used in Example 1, 5000 ppm of Irganox® 1010 (tetrakis [methylene(3,5-di-tert-butyl-4-hydroxyphenyl propionate)] methane from Ciba-Geigy) and 500 ppm of calcium stearate were reacted in an intensive mixer, using a steam heated rotor, for a period of 4-5 minutes. The material was reacted at 430-450°F (221-232°C). The reaction products obtained were extruded into films of various thicknesses by use of a single screw extruder with a temperature profile of: Zone 1=365-380°F (185-193°C) Zone 2=405-440°F (207-227°C) Zone 3=400-440°F (204-232°C) Reaction products from 80 wt.% PVA and 20 wt.% of a polyolefin graft copolymer (prepared by grafting XMNA onto HDPE) were extruded into 76,2 µm film. These along with those made from 100% PVA "A" and "B", respectively, were dried in a vacuum oven to constant weight. They were then placed in desiccators in which the atmosphere was controlled at 50% and 79.5% relative humidity, respectively. The films were weighed after remaining in these atmospheres for eight days. The percent weight gains are shown in Table II, below. Example 5. PVA/functional polymer reaction products were also made using the PVA polymers listed below. The results shown in Table III demonstrate that PVA polymers having a degree of hydrolysis greater than about 98 mole percent do not form useful alloys according to the present invention. Other anhydride-containing functional polymers which were studied include: 1. A graft of XMNA onto an ethylene-butene-1 copolymer (linear low density PE with a high load melt index (HLMI) of 2.6 g/10 min and density=0.917 g/cc), content of XMNA=1.4 wt.%, MI=1 for the graft copolymer. 2. An EVA containing 14% vinyl acetate and 0.29% of maleic anhydride and a melt index (MI)=6-8. 3. A graft of XMNA onto an EVA containing 28% vinyl acetate, MI=6. Content of XMNA=0.87 wt.% and MI of graft copolymer= 1.2. 4. A graft of maleic anhydride (MA) onto HDPE. Content of MA is 1.02 wt.%. Example 6 This example shows the decrease in melt flow rate (MFR) found when the proportion of functional polymer in the reaction product is increased. A reaction of the polyolefin graft copolymer described in Example 1 with modified PVA, as described in Table IV, below, is performed at 425°F (218°C) for 5 min. in an electrically heated scroll mixer (e.g. a Brabender mixer). The melt flow rates (MFR) are taken at 230°C using a 2160 g weight as described in ASTM 1238 (Condition L). Example 7 (Comparative) Varying percentages of non-grafted PVA, as designated in Table V, below, and an ethylene-butene-1 copolymer (linear low density polyethylene-LLDPE) with an MI of 2 g/10 min. and a density of 0.918 g/cm³ were blended in an electrically heated scroll mixer at 425°F (218°C) for 5 min. at 120 rpm. Gross macrophase separation was observed in which the macrophases were different in color and behavior. The smaller macrophase is indicated as percent separated in Table V, below. These data show that the blends of PVA with LLDPE are not macroscopically homogeneous. Example 8 A number of reaction products were prepared using 20 wt.% of the polyolefin graft copolymer used in Example 1 combined with various amounts of the LLDPE described in Example 7, and PVA "A" as described in Example 4. The results are shown in Table VI, below. No macrophase separation occurs. This demonstrates the utility of the reaction product (the PVA alloy formed in situ) for compatibilization of PVA with LLDPE. Example 9 PVA alloys were prepared by reacting 90, 80 and 70 wt.%, respectively, of PVA "A" described in Example 4 with appropriate amounts of an ethylene copolymer (MI=6.5, 14 wt.% vinyl acetate and 0.29 wt.% maleic anhydride) in the presence of 5000 ppm of Irganox® 1010 and 500 ppm of calcium stearate. The alloys obtained can be extruded into clear films. Example 10 PVA alloys were prepared by reacting 80 and 70 wt.%, respectively, of a PVA with a DP of 500-700, M n =22,000-31,000 and which is 87 mole percent hydrolyzed with the ethylene graft copolymer described in Example 1. The reaction products so obtained are well dispersed without macrophase separation. Example 11 The oxygen permeability of PVA "A", PVA "B", and their alloys as described in Example 3 were measured at room temperature (22-24°C) using an "Ox-Tran 100" oxygen permeability measurement device (Mocon Modern Controls, Inc., Elk River, Minnesota) and compared with Mylar and nylon 6 films according to ASTM D-3985-81. The results are shown below in Table VII. Example 12 90 wt.% of PVA "A" described in Example 3 is blended with 10 wt.% of a high density polyethylene copolymer (HDPE) with a density of 0.949 g/cm³ and a high load melt index of 20 under the same conditions as described in Example 8. At least 7.5% of the material can be distinguished as a separate macrophase. Example 13 An alloy was prepared in situ by using 80 wt.% of PVA "A", 10% of an ethylene-hexene-1 copolymer with a density of 0.949 g/cm³ and a high load melt index (HLMI) of 20 g/10 min, and 10 wt.% of the polyolefin graft copolymer described in Example 1 under the conditions described in Example 7. Example 14 The HDPE in Example 12 is replaced by low density polyethylene homopolymer (LDPE) with a density of 0.191 g/cm³ and an MI of 2.5. At least 4 wt.% of the material is observed as a separate macrophase. Example 15 An alloy was prepared in the same manner as described in Example 13 except that a branched low density polyethylene with an MI of 2.5 g/10 min and a density of 0.919 g/cm³ was substituted for an ethylene copolymer. Example 16 An alloy was prepared from 80 wt.% PVA (87 mole % hydrolyzed with a 4% aqueous solution viscosity at 20°C of 5 mPa · s) and 20 wt.% of an ethylene-acrylic acid copolymer (EAA-6.5 wt.% acrylic acid) by mixing in a Brabender mixer at 425°F (218°C) for 5 min. Example 17 An alloy was prepared from 85 wt.% of the PVA described in Example 16, 10 wt.% of the EAA described in Example 16, and 5 wt.% of the LLDPE described in Example 7 by mixing in a Brabender mixer at 425°F (218°C) for 15 min. Example 18 An alloy was prepared by mixing in a Brabender mixer at 425°F for 10 minutes 90 wt.% of the PVA described in Example 16 and 10 wt.% of a zinc ionomer of ethylene-methacrylic acid in which 10.1 wt.% methacrylic acid is 70% neutralized. Example 19 An alloy was prepared by mixing in a Brabender mixer at 425°F for 15 minutes 80 wt.% of the PVA described in Example 16 and 20 wt.% of the ionomer described in Example 18. Example 20 An alloy was prepared by mixing in a Brabender mixer at 425°F (218°C) for 5 mins. 80 wt.% of the PVA described in Example 16 and 20 wt.% of a polypropylene grafted with 0.23 weight % of maleic anhydride. Example 21 An alloy was prepared similarly to the procedure of Example 20 by using 80 wt.% of the PVA described in Example 16, 10 wt.% of the grafted polypropylene of Example 20 and 10 wt.% of either a block polypropylene (PP) polymer containing 5% ethylene or 10 wt.% of a random PP polymer containing 1.8% ethylene. Example 22 Similar alloys were prepared by substituting a PVA with a DP of 600 and 74 mole % hydrolysis for the PVA of Examples 20 and 21. Example 23 Varying percentages of PVA, as designated in Table VIII, below, and an ethylene-propylene (EP) elastomer containing 65 wt.% ethylene with a density of 0.86 g/cm³ were blended in an electrically heated scroll mixer at 425°F (218°C) for 5 min. at 120 rpm. Two macrophases were observed which were different in color and behavior. The smaller portion is indicated as separation percent in Table VIII. These data show that EP cannot be completely dispersed in PVA. Example 24 A number of alloys were prepared using PVA "A" and PVA "B" with an EP graft copolymer prepared by using an XMNA graft of the EP elastomer of Example 23 (0.8 wt.% XMNA, 0.04 MI). No separation occurred as shown in Table IX, below. Example 25 85 wt.% PVA "A", 10 wt.% of the EP graft copolymer of Example 24 and 5 wt.% of a HDPE with a density of 0.949 and an HLMI of 20 were blended at 425°F (218°C) for 5 min. to yield an alloy. Example 26 In the same manner as described in Example 25, 70 wt.% of PVA "B", 10 wt.% of the EP graft copolymer of Example 24, and 10 wt.% of an LLDPE with a density of 0.918 and an MI of 2 yields an alloy. All parts and percentages herein are by weight unless otherwise indicated. Glossary of terms Abbreviations used herein to identify chemical ingredients and product characteristics include: DP - degree of polymerization EP - ethylene-propylene elastomer EAA - ethylene-acrylic acid copolymer EVA - ethylene vinyl acetate copolymer EVOH - ethylene vinyl alcohol copolymer FTIR - Fourier Transform Infrared Spectroscopy HDPE - high density polyethylene HLMI - high load melt index LLDPE - linear low density polyethylene MA - maleic anhydride MFR - melt flow rate MI - melt index M n - number average molecular weight M w - weight average molecular weight PE - polyethylene PET - polyethylene terephthalate PVA - polyvinyl alcohol XMNA - x-methyl bicyclo(2.2.1 )hept-5-ene-2,3-dicarboxylic anhydride

Claims: 1. A polymer alloy which is prepared by reacting a polyvinyl alcohol having a degree of hydrolysis of less than 98 mole percent and a degree of polymerization of from 300 to 900 with less than the stoichiometric amount of a functional olefin polymer containing functional groups which are reactive with the hydroxyl groups of the polyvinyl alcohol, at least 70% of the combined weights of the polyvinyl alcohol and the functional olefin polymer being constituted by the polyvinyl alcohol, whereby there is obtained a mixture of grafted and ungrafted polyvinyl alcohol polymers, the grafted polyvinyl alcohol polymer having less than all the available hydroxyl groups reacted with said functional groups and the proportion of unreacted hydroxyl groups being such that the polymer mixture is melt extrudable. 2. A polymer alloy according to claim 1, in which the polyvinyl alcohol polymer is from 70 to 90 mole percent hydrolyzed prior to reaction with the functional polymer. 3. A polymer allow according to claim 1 or 2, in which the functional groups are carboxylic acid groups, carboxylic acid anhydride groups, carboxylic acid groups which have been salified with a metal, or derivatives of carboxylic acid groups, or mixtures of two or more of such groups. 4. A polymer alloy according to claim 3, in which the functional groups are grafted on to the functional olefin polymer. 5. A polymer alloy according to claim 4, in which the olefin backbone polymer on to which the functional groups are grafted is polyethylene or polypropylene. 6. A polymer alloy according to claim 4 or 5, in which the functional groups are derived from maleic acid or anhydride, x-methyl bicyclo(2.2.1)hept-5-ene-2, 3-dicarboxylic acid or anhydride, bicyclo(2.2.1)-hept-5-ene-2,3-dicarboxylic acid or anhydride, citraconic acid or anhydride, itaconic acid or anhydride, or a 1,4-butenedioic acid monalkyl ester. 7. A polymer alloy according to any of claims 4 to 6, in which the functional groups are derived from x-methyl bicyclo(2.2.1)hept-5-ene-2,3-dicarboxylic acid and the backbone polymer is a linear low density polyethylene comprising ethylene-butene-1 comonomer. 8. A polymer alloy according to any of claims 4 to 6, in which the functional groups are derived from maleic anhydride or x-methyl bicyclo(2.2.1)hept-5-ene-2, 3-dicarboxylic anhydride and the backbone polymer is an ethylene-vinyl acetate copolymer or high density polyethylene. 9. A polymer allow according to claim 3, in which the functional groups are incorporated in the functional olefin polymer by copolymerisation. 10. A polymer alloy according to claim 9, in which the functional olefin polymer is an ethylene-acrylic acid copolymer, an ethylene-methacrylic acid copolymer, an ethylene-alkyl acrylate-acrylic acid copolymer, or an ethylene-alkyl methacrylate-methacrylic acid copolymer, or a partially neutralised salt of any of said copolymers. 11. A polymer alloy according to any of claims 1 to 10, which additionally comprises a blending resin which is an olefin homopolymer or copolymer which is compatible with the mixture of grafted and ungrafted polyvinyl alcohol polymers and which is melt blended with said mixture. 12. A polymer alloy according to claim 11, which comprises from 99 to 85% by weight of the polyvinyl alcohol polymer and, correspondingly, from 1 to 15% by weight of the blending resin. 13. A polymer alloy according to any of claims 1 to 12, formed into a gas barrier film, sheet, tube, coating, bottle or profile. 14. An article formed of a polymer alloy according to any of claims 1 to 12, by blown film extrusion, cast film extrusion, extrusion coating, coextrusion, coextrusion coating, injection moulding, blow molding, rotomolding, compression molding, profile extrusion, pipe extrusion, or tubing extrusion.

Inventors: MACHONIS, JOHN JR., SCHMUKLER, SEYMOUR, SHIDA, MITSUZO
Applicants: QUANTUM CHEMICAL CORPORATION (A VIRGINIA CORP.)
Application year: 1985
Main classification: C08G81
IPC codes: C08L23, C08L29, C08G81, C08L51