NAIL POLISH COMPOSITIONS AND MEANS FOR APPLYING SAME

Abstract: A novel nail polish composition having a low viscosity, i.e. not greater than about 200 cps comprising from about 3.0% to about 24.0% a shade paste, suitable film former and thinner and a pen-like means for applying said nail polish having a substantially non-bristle nib.

Description: The present invention relates to a nail polish composition and means for applying the same. More specifically, the invention is directed to a nail polish formulation having a low viscosity, i.e. not greater than 200 mPas, and a relatively high pigment concentration, and wherein said polish is dispensed by way of a pen, having a substantially non-bristle brush tip. BACKGROUND OF THE INVENTION Conventionally known nail polish formulations have been used in pen-like applicators of the type disclosed in U.S. Patent No. 3,592,202. The pen comprises two bristle brush tips, one at each end and two reservoirs, one containing nail polish, the other containing nail polish remover. Nail polish or remover is delivered to the bristle tip of the pen by compressing the reservoir housing containing the fluid formulation. This technique of delivering either polish or remover to the brush is for all practical purposes similar to the technique of dipping a brush into a reservoir of nail polish or remover, insofar as neither technique requires any special formulation in order to effect proper delivery of the polish or remover to the bristle brush tip. Moreover, said prior art techniques are dependent upon the use of conventional nail polishes, the viscosities of which are sufficiently high enough to enable the polish to be held on the applicator brush. In contrast to the prior art techniques for applying polish to nail surfaces, the present invention utilizes a substantially non-bristle nib, one end of which contacts a reservoir which is filled with a nail polish. When the tip of the nib is depressed polish is released from the reservoir and saturates the nib throughout its entire length, thereby enabling the delivery of a controlled flow of polish to the end of the nib upon contact with the nail surface. Conventional nail polish formulations are unsuitable for use with the applicator means of the present invention, primarily due to their high viscosities, i.e. generally greater than about 300 mPas. As used herein the term viscosity refers to Newtonian viscosity as opposed to the thixotropic viscosity. While reducing the viscosity of conventional nail polishes by dilution with a suitable thinner can result in a composition which may flow easily to the non-bristle nib of the present applicator means, such a composition is essentially useless as a nail polish since the pigment and/or other solids content of the nail polish is reduced to a point where it becomes impossible to obtain satisfactory coverage of the nail surface. Accordingly, the principal objectives of the present invention are two fold; first to provide a method of applying polish to nail surfaces i.e. via a substantially non-bristle tip affixed to a pen; and second, to provide a commercially acceptable nail polish composition, having an extremely low viscosity so as to flow easily throughout the length of the applicator's non-bristle tip and onto the nail surface and yet having a sufficiently high pigment or solid content so as to provide acceptable nail coverage properties. These and other objects will be readily apparent from the detailed description of the invention set forth below. BRIEF DESCRIPTION OF THE DRAWINGS Fig. 1 is an exploded view of the components of the nail polish applicator. Fig. 2 is an exploded view of the valve means used in the applicator. Accordingly, the invention provides a low viscosity nail polish composition comprising - i. from 2 to 40% by weight of primary film former chosen from nitro cellulose, cellulose propionate, cellulose acetate butyrate, ethyl cellulose, sucrose acetate isobutyrate, polyvinyl acetate, polyvinyl alcohol, thermoplastic acrylic esters, homopolymers and copolymers of alkyl acrylates and methacrylates, urethane polymers, nylon, polyesters and alkyds. ii. from 3 to 24% by weight of shade paste which comprises at least one conventional pigment material and an essentially non-flammable, non-explosive mill base comprising a water-insoluble protective colloid compatible with said primary film former and an essentially non-flammable low volatizing plasticiser which is compatible with the primary film former; the composition having a viscosity not greater than 200 mPa.s at 25°C. The invention also provides an applicator means for dispensing the low viscosity nail polish composition of the invention, which applicator comprises a pen characterised by a substantially non-bristle nib. DETAILED DESCRIPTION OF THE INVENTION The nail polish composition of the present invention is generally prepared by mixing a suitable shade paste or slurry with a final lacquer formulation. The shade paste or slurry is prepared by grinding a suitable pigment or combination of pigments and an essentially non-flammable low volatising plasticiser in a mill base. Suitable pigments for use in the mill base include all those known and conventionally used in the cosmetic industry, and hence should be non-toxic, non-sensitizing, non-staining, substantially insoluble in solvents, essentially free from a tendency to bleed, compatible with solvents used in the lacquer formulation and moderately stable to light. The average particle size of the selected pigment should be very small, ie. from 0.1 µm to 2.0 µm to insure satisfactory dispersing properties. As a practical matter, pigments used in nail polish must conform to appropriate national legislation, which in the United States means that the pigment or colorant must be certified by the Food and Drug Administration (FDA). The most widely used pigments include the following: D&C Red 6, D&C Red 30, D&C Red 36, D&C Red 9, D&C Red 7, D&C Red 21, D&C Red 34, FD&C Yellow 5, FD&C Yellow 6, Ferric Ferrocyanide, and cosmetic iron oxides. In addition to the foregoing, titanium dioxide is frequently used as a pigment in combination with other pigments, primarily to impart opacity and to produce pale, finished pigment shades. Pigments may be ground individually as well as in combination to produce a desired pigment shade. The amount of pigment utilized in the preparation of the paste or slurry ranges from 20.0% to 80.0%. In accordance with the present invention, the pigment (or pigments) selected for use is ground in a mill base formulation to provide a paste composition which may be directly incorporated into a lacquer formulation to provide a finished coating composition, eg. nail polish. The essential components of the mill base, into which the pigment is ground, comprise (1) a water-insoluble protective colloid capable of preventing flocculation of the pigment particles and which is compatible with the film former present in the lacquer composition; and (2) a plasticizer, having low volatility and which is both-compatible with the protective colloid in the mill base as well as the film former used in the film coating composition. A preferred mill base is one which is essentially non-flammable and non-explosive and which, when combined with the pigment and plasticizer, will provide a composition having a consistency suitable to permit grinding on high shear equipment. The resultant pigment paste composition, ie. finely ground pigment in combination with the mill base ingredients, should be easily dispersable in a lacquer composition without substantially increasing the viscosity of the finished coating product. The protective colloid utilized in the mill base should be sufficiently soluble in the plasticizer used therein and the amount of the protective colloid should be adequate to provide enough material to completely coat the dispersed, individual pigment particles with at least a mono-molecular layer. Generally, the molecular weight of the colloid should be sufficient to provide an adequate colloidal effect to prevent pigment particles from agglomerating or flocculating. Moreover, the colloid chosen should be compatible with cellulose nitrate or other desired film forming agents present in the lacquer composition. While the foregoing are the primary criteria for selecting a suitable protective colloid, it is also important that it be soluble in the solvent system used in the finished product and not appreciably increase the viscosity of the finished product, i.e. to a degree which impedes flow through the applicator's non-bristle tip. Other considerations which should be taken into account in selecting a suitable protective colloid include: its stability in the final formulation; its suitability for end use, i.e. innocuous to surfaces to which the finished coating composition is to be applied, e.g. fingernails; its effect on the properties of final coating composition, e.g. gloss, adhesion, resistance to environmental conditions, depth of finish, flexibility and hardness of the film coating. Representative chemical groups of preferred suitable protective colloids include: saccharide based polymers, acrylic polymers, polyesters, alkyd resins, polyamides, cellulosic polymers, sulfonated naphthalenes, vinyl polymers, formaldehyde condensates, polyurethanes, substituted pyrrolidone polymers, and polypropylene oxides. Preferred protective colloids for use in the mill base of the present invention include toluene sulfonamideformaldehyde condensates (for example Monsanto's SANTOLITE MHP), methyl-butyl methacrylate copolymer (Rohm & Haas' Acryloid B-66"), sucrose benzoate, ethyl cellulose, dimer acid based polyamide resin (Henkel's Versamide 940) and polymeric esterified pentaerythritol (Hercules' Herco-Flex 900). Generally, the amount of protective colloid utilized in the mill base is that which is necessary to prevent agglomeration or flocculation of the pigment particles. It has been found that acceptable results are achieved when the protective colloid is present in amounts ranging from 2.0% to 25.0% by weight. The selection of the plasticizer component used in the mill base of the present invention should be based on the following general criteria: its low volatility; its ability to sufficiently solubilize the chosen protective colloid; its compatibility with the chosen film former and other ingredients in the lacquer formulation for the finished product; its ability not to appreciably increase the viscosity of the finished product; its suitability for the desired end use, i.e. dermatologically innocuous; and its ability to impart desirable properties to the finished products, e.g. flexibility and adhesion, color fastness and stability. Within these general parameters, those skilled in the art will readily recognise suitable plasticizers among the following chemical groups: abietic acid derivatives, acetic acid derivatives, adipic acid derivatives, azelaic acid derivatives, benzoic acid derivatives, polyphenyl derivatives, citric acid derivatives, epoxy derivatives, proprietary esters, ether derivatives, formal derivatives, glutaric acid derivatives, glycerol derivatives, glycol derivatives, linear dibasic acid derivatives, petroleum derivatives, isobutyric acid derivatives, isophthalic acid derivatives, lauric acid derivatives, mellitates, myristic acid derivatives, nitrile derivatives, oleic acid derivatives, palmitic acid derivatives, paraffin derivatives, pelargonic acid derivatives, pentaerythritol derivatives, phosphoric acid derivatives, phthalic acid derivatives, polyesters, ricinoleic acid derivatives, sebacic acid derivatives, stearic acid derivatives, styrene derivatives, sucrose derivatives, sulfonic acid derivatives, terephthalic acid derivatives, tartaric acid derivatives, carbonic acid derivatives, aconitic acid derivatives, maleic acid derivatives, fumaric acid derivatives, copyrylic acid derivatives, butyric acid derivatives as well as camphor and castor oil. Preferred plasticizers include N-ethyl toluene sulfonamide (Santicizer 8), butyl benzyl phthalate (Santicizer S160), alkyl sulphonic esters of phenol e.g. "Mesamoll" (Mobay Chemical Co.) and tricresyl phosphate. While the amount of plasticizer utilized in the mill base should be sufficient to solubilize the protective colloid, it generally has been found that an amount ranging from 75% to 98% by weight is effective. Surfactants may be optionally included in the mill base to aid pigment dispersion. When present, the amount of surfactant depends on the specific surfactant(s) used and properties desired; however, it has been found that the amount of surfactant(s) may range from 0.1% to 5.0%. While any surfactant compatible with the ingredients in the finished composition may be utilized, Nalco 2395 or Troykyd Solvent Anticrater 366 has been found to produce acceptable results. The combined pigment and preferred mill base composition can be processed (milled) under high-shear conditions to provide a pigment paste composition wherein the average particle size of the pigment is in the range of 0.1 µm to 2.0 µm. The preferred pigment composition has a paste-like consistency which may be directly mixed with a suitable lacquer formulation. However, as a practical matter, the pigment paste is generally first combined with the appropriate lacquer thinner and thereafter, the remaining ingredients are added. The following Examples are illustrative of procedures which have been found useful for the preparation of specific mill bases and pigment compositions made in accordance with the present invention. EXAMPLE 1 A 90.7 kg batch of mill base was prepared in accordance with the following procedure. 72.1 kg. (79.5% by weight) of plasticizer, (Santicizer 8), i.e. , N-ethyl toluene sulfonamide was weighed out on a Toledo floor scale and poured into a steam-jacketed kettle equipped with a "Lightnin" variable-speed, propeller mixer. The plasticizer was heated to a temperature of 87.8°C while being stirred. 18.6 kg. (20.5% by weight) of protective colloid (Santolite MHP), i.e. , toluene sulfonamideformaldehyde condensate was weighed out on a Toledo floor scale and broken into small pieces, the approximate diameters of which were no greater than about 2.5 cm. The mixer speed was then increased to a point just prior to splashing and the protective colloid was slowly added to the plasticizer, the temperature of which was maintained at 76.7°C until all of the protective colloid was dissolved. Thereafter, the mixture was cooled to and maintained at a temperature of between 48.9 to 60°C. EXAMPLE 2 The procedure of Example 1 is repeated in the preparation of 22.7 kg. batches of each of the following mill base formulations: The following general procedure was used in preparing the pigment paste compositions of Examples 4-13. EXAMPLE 3 An amount of mill base, prepared in accordance with Example 1, is placed into a change-can-paste mixer, the temperature of the mill base being between 48.9 to 60°C. A desired pigment shade is determined and appropriate amounts of an individual pigment or pigment mixture is weighed out and hand stirred into the mill base to prevent excessive dusting. The change-can, containing the pigment and mill base is placed under the mixer and mixed until a well dispersed slurry, completely free of lumps or dry pigment, is obtained. The milling equipment, i.e. a Buehler SDX-600 three-roll mill having standardized roller speeds, is prepared for operation by preheating the rolls to temperatures ranging from 22.2°C to 51.1°C; setting the hydraulic pressure of the rolls in a range from 1.5 to 1.85 MPa; and setting the hydraulic pressure of the knife at 0.7 MPa. The slurry in the change can is then transferred to the mill and milled by passing the material through the mill a sufficient number of times at the specific parameters necessary to obtain a paste having the desired average pigment particle size, i.e. from 0.1 to 2.0 µm. Slurry material which does not pass through the mill rolls, i.e. "hang-back" material, is moistened with additional amounts of the slurry sufficient to enable it to pass through the rolls. Thereafter, the milled pigment paste is transferred to a clean change-canpaste mixer and mixed until uniform. EXAMPLE 4 In accordance with the procedure of Example 3, a 2300 gram batch of a pigment paste composition was prepared using: The three rolls of the Buehler SDX-600 mill were preheated to 37.2°C and then rolls 1 and 3 were cooled to 36.1°C. The hydraulic roll pressure was set at 1.85 mPa. The hydraulic knife pressure was set at 0.7 MPa. The pigment slurry was passed through the mill three times at the above conditions and the resulting pigment paste composition was found to have an average particle size ranging from 0.1 to 2.0 µm as measured by Precision's grind gauge (N.I.P.I.R.I. 625-1/2 Mu) having a range of 0-12.5 µm. EXAMPLE 5 In accordance with the procedure of Example 3, a 2300 gram batch of a pigment paste composition was prepared using: The three rolls of the Buehler SDX-600 mill were preheated to 41.1°C and then rolls 1 and 3 were cooled to 36.1°C. The hydraulic roll pressure was set at 1.85 MPa The hydraulic knife pressure was set at 0.7 MPa. The pigment slurry was passed three times through the mill at the above conditions and the resulting paste composition was found to have an average pigment particle size ranging from 0.1 to 2.0 µm as measured by grind gauge used in Example 4. EXAMPLE 6 The procedure of Example 3 was repeated in preparing a 2300 gram batch of a pigment paste composition using: The three rolls of the Buehler SDX-600 mill were preheated to 37.2°C and then rolls 1 and 3 were cooled to 32.2°C. The hydraulic roll pressure was set at 1.65 MPa. The hydraulic knife pressure was set at 0.7 MPa. The pigment slurry was passed three times through the mill at the above conditions and the resulting paste composition was found to have an average pigment particle size ranging from 0.1 to 2.0 µm as measured by the grind gauge used in Example 4. EXAMPLE 7 The procedure of Example 3 was repeated in preparing a 2300 gram batch of a pigment paste composition using: The three rolls of the Buehler SDX-600 mill were preheated to 52.7°C and then rolls 1 and 3 were cooled to 47.8°C. The hydraulic roll pressure was set at 18.5 Bars (272 lbs.). The hydraulic knife pressure was set 0.7 MPa. The pigment slurry was passed three times through the mill at the above conditions and the resulting paste size ranging from 0.1 to 2.0 µm as measured by the grind gauge used in Example 4. EXAMPLE 8 The procedure of Example 3 is repeated in the preparation of a 1000 gram batch of a pigment paste composition using: The three rolls of a Buehler SDX-600 mill are preheated to 37.2°C and the rolls 1 and 3 are cooled to 36.1°C. The hydraulic pressure is set 1.85 MPa. The hydraulic knife pressure is set at 0.7 MPa. The pigment slurry is passed three times through the mill at the above conditions to obtain a pigment paste composition having an average pigment particle size ranging from 0.1 to 2.0 µM as measured by the grind gauge in Example 4. EXAMPLE 9 The procedure of Example 3 is repeated in the preparation of a 1000 gram batch of a pigment paste composition using: The three rolls of a Buehler SDX-600 mill are preheated to 37.2°C and then rolls 1 and 3 are cooled to 32.2°C. The hydraulic roll pressure is set at 1.65 MPa. The hydraulic knife pressure is set at 0.7 MPa. The pigment slurry is passed three times through the mill at the above conditions to obtain a pigment paste composition having an average pigment particle size ranging from 0.1 to 2.0 µM as measured by the grind gauge in Example 4. EXAMPLE 10 The procedure of Example 3 was repeated in preparing a 2300 gram batch of a pigment (shade) paste composition using: The three rolls of the Buehler SDX-600 mill were preheated to 41.1°C and then rolls 1 and 3 were cooled to 36.1°C. The hydraulic roll pressure was set at 1.85 MPa. The hydraulic knife pressure was set at 0.7 MPa. The pigment slurry was passed three times through the mill at the above conditions and the resulting paste composition was found to have an average pigment particle size ranging from 0.1 to 2.0 µm as measured by the grind gauge used in Example 4. EXAMPLE 11 The procedure of Example 3 was repeated in preparing a 2300 gram batch of a pigment (shade) paste composition using: The three rolls of the Buehler SDX-600 mill were preheated to 37.2°C and then rolls 1 and 3 were cooled to 32.2°C. The hydraulic roll pressure was set at 1.5 MPa. The hydraulic knife pressure was set at 0.7 MPa. The pigment slurry was passed three times through the mill at the above conditions and the resulting paste composition was found to have an average pigment particle size ranging from 0.1 to 2.0 µm as measured by the grind gauge in Example 4. EXAMPLE 12 The procedure of Example 3 was repeated in preparing a 2300 gram batch of a pigment (shade) paste composition using: The three rolls of the Buehler SDX-600 mill were preheated to 37.2°C and then rolls 1 and 3 were cooled to 32.2°C. The hydraulic roll pressure was set at 1.65 MPa. The hydraulic knife pressure was set at 0.7 MPa. The pigment slurry was passed three times through the mill at the above conditions and the resulting paste composition was found to have an average pigment particle size ranging from 0.1 to 2.0 µm as measured by the grind gauge used in Example 4. It should be clear, from the foregoing, that the pigment composition is an intermediate product, ultimately to be incorporated into a lacquer formulation for a nail polish composition. While the foregoing disclosure and Examples are all directed to the use of a preferred mill base as a grinding medium for various pigment materials to form a pigment paste composition which may be directly incorporated into the lacquer formulation of the present invention, the pigment materials may also be ground in a nitrocellulose containing mill base to form pigment chips in accordance with the conventional "chipping" technology. However, in accordance with the present invention, if a nitrocellulose pigment chip is to be used, it is critical that the viscosity of the final nail polish composition containing the nitrocellulose prepared pigment ingredient(s) not be greater the 200 mPas. This can be accomplished by using, for example, a grade of nitrocellulose of about 100 mPas nitrocellulose 70% I.P.A. wet in the mill base to form the pigment chip. It is understood that conventional nail polish compositions generally utilize nitrocellulose having a grade not less than approximately 90-100 mPas, i.e. 1/4 sec nitrocellulose. It is also to be understood that a nail polish pigment chip formulation may be prepared using a grade of nitrocellulose having a viscosity of less than 90 mPas, for example 18-25 mPas. Using this grade of nitrocellulose will allow a greater pigment load than could be achieved with the nitrocellulose of a grade 90-100 mPas. Of course if nitrocellulose chips of the type described above are to be utilized it is necessary to dissolve the color chips in an appropriate solvent to form a pigment dispersion or slurry (shade paste) which thereafter can be mixed with a suitable lacquer formulation to provide a final nail polish composition. The lacquer formulation of the present invention, in which the pigment paste or slurry is mixed comprises a suitable film forming agent and various optional ingredients including: one or more modifying resins, thinners, solvents, diluents, surfactants, flocculating agents or suspending agents. A preferred film former is 18-25 mPas nitrocellulose. The primary film former is chosen from nitrocellulose, cellulose propionate, cellulose acetate butyrate, ethyl cellulose, sucrose acetate isobutyrate, polyvinyl acetate, polyvinyl alcohol, thermoplastic acrylic esters, homopolymers and copolymers of alkyl acrylates and methacrylates, urethane polymers, nylon, polyesters and alkyds. The nail polish composition of the invention comprises from 2 to 40% by weight of the primary film former. When nitrocellulose is used as primary film former, it is preferably present in an amount of from 2 to 20% by weight. The amount of preferrred nitrocellulose film former ie. 18-25 mPas generally ranges from 3.0% to 15.5% by weight with the preferred range being from 5.0% to 10.0% by weight. It will, of course, be understood by those skilled in the art that in selecting a suitable film forming agent, it will be necessary to strike a balance between the need for building the solids content of the composition, ie. by way of the film forming agent, but at the same time, insuring that the viscosity of the final composition does not exceed 200 mPas. The optional modifying resin or resins present in the lacquer formulation must be compatible with the desired film forming agent. The primary role of a modifying resin is to impart one or more of the following properties to the final composition: improved gloss, improved depth of gloss, improved adhesion, improved film hardness, reduced film shrinkage, improved water resistance and increased solids. Suitable modifying resins include: toluene sulfonamideformaldehyde condensates (Santolite MHP and/or Santolite MS-80); sucrose benzoate; sucrose acetate isobutyrate, copolymeric mixtures thereof, alkyds, polyvinyl acetate, polyesters, acrylics, formaldehyde condensates, nylon, Rosin resins, acetates and cyclohexahones. A preferred resin mixture comprises either or both Santolite MHP and Santolite MS-80 (80.0% solution) and Cellovar CV-160 (80.0% solution in butyl acetate) i.e. , sucrose benzoate/sucrose acetate-isobutyrate copolymer. The amount of the total modifying resin or mixtures thereof present in the lacquer formulation ranges from 0.0% to 50.0%, with the preferred range being from 4.0% to 13.0%, based on 100% solids. In preferred lacquer formulations, Santolite MHP is present in an amount ranging from 0.2% to 8.0%, Santolite MS 80 is present in an amount ranging from 2.4% to 5.6% and Cellovar CV160 (80%) is present in an amount ranging from 1.6% to 3.2%, all figures based on 100% solids. Other optional ingredients present in the lacquer formulation include those ingredients well known in the art and conventionally employed in such formulations. Examples of such ingredients include plasticizers, e.g. see the list of plasticizers, supra ; solvents; suspension agents, e.g. Bentone® clay; potentiating compounds which enhance the properties of suspension agents, e.g. malic acid; thinning agents, natural and/or synthetic pearlescent agents, e.g. guanine, metallic powders and U.V. light stabilizers, e.g. , Cyasorb 5411. When pearlescent agents are incorporated in a final nail lacquer formulation, it has been found that it is possible to utilize grades of nitrocellulose up to and including 1/2 sec. Specific examples of acceptable metallic powders include, for example cosmetic grades of leafing aluminum or bronze powder. The amount of said metallic powder(s) generally present in a final nail composition is from 1.0% to 17.0% by weight. The amount actually used however depends upon the cosmetic affect desired. It will be understood, however, that the use of particular ingredients in any specific lacquer formulation, of necessity, will be based upon the specific properties and viscosity sought to be obtained in the final product. Whether incorporated as part of the lacquer formulation or the final nail polish composition, surfactants and flocculating agents may also be utilized. Surfactants, while optional, have been found to produce a leveling effect on the polish, when applied to the nail surface, as well as improved wear and flow properties. Suitable surfactants include anionic, cationic, nonionic or amphoteric surfactants that would otherwise be compatible with the nail polish ingredients. However, it should be understood that if bentone is used as a suspension agent, then an anionic surfactant cannot be used since bentone contains a cationic moeity. Examples of suitable anionic surfactants are well known to those skilled in the art and include compounds within the following classification: The saponification products of fats, sulfated fatty acid esters, sulfated fatty amides, sulfated fatty alcohols, phosphate esters of fatty alcohol, amino caboxylated acids, sulfated rosin and sulfated nonionic type surfactants. Examples of cationic surfactants include aliphatic amines with fatty chains and quarternary ammonium salts. Examples of nonionic surfactants include compounds within the following classifications: polyoxyethylene alkylphenols, polyoxyethylene alcohols, polyoxyethylene esters of fatty acids, polyoxyethylene alkyl amines, polyoxyethylene alkylimides, polyol surfactants, polyalkylene oxide block copolymers, propoxylated surfactants, and fluorinated alkyl esters. In addition to the foregoing, polymeric dispersants may also be incorporated to aid in leveling the nail polish, to aid as a pigment dispersant or to aid flocculation of the pigments into a soft settle. Said dispersants include, among others, silicone polymers and copolymers, polyamides, polyacrylamides and poly-carboxylic acids. The amount of the surfactant or dispersant ingredients present may range from 0.0% to 10.0%. In accordance with a preferred formulation of the present invention, at least one surfactant or dispersant compound is incorporated into the formulation in an amount ranging from 0.01% to 1.0% by weight. Preferred surfactants include: Ethoxylated Castor Oil, e.g., (Nalco Chemicals, "Nalco 2395"); fluorinated alkyl esters, e.g. "3M's" Fluorad FC430; and Troy Chemical's "Troykyd Anticrater 366". As mentioned supra, suspending agents, for example bentones are utilized to aid in the suspension of pigments. In the absence of such agents, pigments tend to settle in a dense hard pack. In accordance with the present invention, it has been found that bentones should not be present in their traditional amounts, i.e. from .75% to 1.2%; but rather, if used, should be present at significantly lower levels, e.g. .25%. A preferred Bentone suspending agent is Bentone 27 (stearalkonium hectorite) which may be prepared for use in the lacquer formulation by placing thinner (75.0%) in a Cowles dissolver equipped with a covered change-can. The mixer is activated and Bentone 27 chips (25.5% Bentone, 18.0% camphor and 57.0% dry cellulose nitrate) are slowly added. These materials are mixed under high shear conditions until the camphor and cellulose nitrate dissolves and the bentone is dispersed. A further optional ingredient that may be used in accordance with the present invention is a flocculent. When present in the final polish formulation, it has been found to promote the soft settling of the pigments. It should be readily apparent to those skilled in the art, that flocculating agents are entirely alien to conventional nail polishes, since it is a generally desired objective in compounding a commercial grade of nail polish to ensure that the ingredients remain in suspension, hence the use of suspending agents such as bentone, etc. Several of the preferred flocculating agents suitable for use include: Nuosperse 700 and Lipophos 42-6. It has also been found that certain amines or quaternized ammonium compounds may be used, e.g., N,N-Bis(2 hydroxyethyl) alkyl amine and soya dimethyl, ethyl ammonium etho-sulphate, respectively. When present, the amount of the flocculating agent utilized in the nail polish ranges from 0.0% to about 10.0% and preferably from 0.1% to 5.0% depending on the specific properties of the flocculant used. The final nail polish is prepared by mixing a suitable pigment paste or slurry with the desired lacquer ingredients to provide a polish having a viscosity not greater than 200 mPas and wherein the pigment concentration ranges from 0.6% to 12.0%. For preparing specific nail polishes those skilled in the art will appreciate that the amounts of the ingredients utilized will depend on the specific ingredients chosen. For example, darker pigments generally require the utilization of a lower concentration than lighter pigments in order to obtain satisfactory coverage properties. This caveat notwithstanding, the following are specific examples of the nail polish formulations of the present invention prepared in accordance with conventional nail polish compounding techniques and procedures, bearing in mind, however, that it has been found that as a first manufacturing step the pigment (shade) paste ingredient is preferably mixed with a suitable thinner and any solid resin that may be used and thereafter the remaining lacquer ingredients. Nail polish formulations within the scope of the present invention and which contain primary film forming agents other than nitrocellulose are set forth in Table 2. Further identification (manufacturers, etc., of various specific ingredients utilized in the above formulation is set forth below: 1) Eastman Kodak 2) Monsanto's 80% solution toluene sulfonamide formaldehyde condensation 3) Example 7 "Pale Lilac" 4) Rohm & Hass's "Acryloid B-67" 5) Eastman Kodak 6) Goodyear 7) Monsanto 8) Cellofilm's 80% solution S.A.I.B. The viscosity of the nail polish formulations disclosed in Tables 1 and 2, do not exceed 200 mPas. This viscosity parameter is a Newtonian viscosity measured at 25°C on a Brookfield viscometer Model LVT. Spindle No. 1, turning at 60 rpm, was used to measure the viscosities of polish formulations having a viscosity of less than 100 mPas. Spindle No. 2, turning at 60 rpm, was used to measure the viscosities of polish formulations having a viscosity between 100 mPas and 200 mPas. The viscosity measurements were all taken after vigorously agitating the nail polish composition in order to eliminate any thixotropic viscosity. More specifically, it was found that the formulations A-F, J, K and M-R all had viscosities less than about 20 mPas. Formulation L was found to have a viscosity of about 25 mPas. Formulations G, H and I were found to have viscosities of about 100 mPas and formulation S has a viscosity of about 200 mPas. While the upper range of the viscosity of the nail polish compositions of the present invention may be as high as 200 mPas it has been found that in preferred compositions, the viscosity should not exceed 75 mPas and preferrably is in the range of from 10 mPas to 25 mPas. The Examples disclosed in TABLE 3 are directed to novel nail polish formulations containing a cosmetic grade of metallic leafing powder, e.g. aluminum powder. The viscosities of each of the formulations A - C were all found to be less than about 40 mPas. The low viscosity nail polish compositions of the present invention have been formulated for use in conjunction with a pen-like dispensing means for applying polish to the nails. With reference to Figures 1 and 2, which depict, respectively, exploded views of the dispensing means and internal valve means, the device comprises a cylindrical sleeve or tube member 11, having a closed end 13 and an open end 15 formed with a projecting cylindrical tip 17 having external threads 19; a substantially cylindrically shaped spring valve assembly 21, adapted to fit snuggly within the open end of sleeve 11, said valve assembly 21 comprising a substantially cylindrical case 23, a spring-biased pin 25 and top hat 27; a substantially cylindrical nib holder 29, the interior of which is formed with internal threads, designed to mate with the external threads 19 of the sleeve 11, said nib holder further comprising a reservoir portion and a cylindrically shaped washer 31 constructed of a porous material; a substantially cylindrically shaped solid nib member 33 constructed of a substantially fibrous material and having a shaped tip portion 35; and a substantially cylindrical cap 37 adapted to cover both the nib 33 and nib holder 29. The nail polish of the present invention is contained within the sleeve 10 along with one or more mixing balls (not shown). The valve assembly 21 prevents leakage of the nail polish. Polish is delivered to the nib 33 by depressing the tip 35 of nib 33 against a rigid surface, which causes the distal end of nib 33 to engage and activate the spring-biased pin 25 of valve assembly 21, thereby discharging an amount of polish contained in the sleeve 11 body portion of the device into a reservoir portion of the nib holder. In this manner, the polish contacts both the porous washer within the nib holder and the distal end of the nib and flows to the nib tip.

Claims: A low viscosity nail polish composition comprising: i. from 2 to 40% by weight of primary film former chosen from nitro cellulose, cellulose propionate, cellulose acetate butyrate, ethyl cellulose, sucrose acetate isobutyrate, polyvinyl acetate, polyvinyl alcohol, thermoplastic acrylic esters, homopolymers and copolymers of alkyl acrylates and methacrylates, urethane polymers, nylon, polyesters and alkyds. ii. from 3 to 24% by weight of shade paste which comprises at least one conventional pigment material and an essentially non-flammable, non-explosive mill base comprising a water-insoluble protective colloid compatible with said primary film former and an essentially non-flammable low volatizing plasticiser which is compatible with the primary film former; the composition having a viscosity not greater than 200 mPa.s at 25°C. A nail polish composition according to claim 1, in which the primary film former is nitrocellulose of a grade having a viscosity of less than 90 mPa.s. A nail polish composition according to claim 1 or 2, in which the primary film former is nitrocellulose of a grade having a viscosity of less than 25 mPa.s. A nail polish composition according to claim 1, in which the mill base comprises from 2 to 25% by weight of a protective colloid chosen from saccharide based polymers; acrylic polymers; polyesters; alkyd resins; polyamides; cellulosic polymers; sulfonated napthalenes; vinyl polymers; formaldehyde condensates; polyurethanes; substituted pyrrolidone polymers; and polypropylene oxides. A nail polish composition according to claim 1, in which the mill base comprises from 2 to 25% by weight of a protective colloid chosen from toluene sulfonamideformaldehyde condensate; methyl-butyl methacrylate copolymer; sucrose benzoate; ethyl cellulose; polymeric esterified pentaerythritol; and a dimer acid based polyamide resin. A nail polish according to claim 1, in which the mill base comprises from 75 to 98% by weight of a plasticiser chosen from N-ethyl toluene sulfonamide; butyl benzyl phthalate; and alkyl sulphonic ester of phenol; and tricresyl phosphate. A nail polish composition according to claim 1, in which the shade paste comprises from 20 to 80% by weight pigment material and from 20 to 80% by weight mill base. A nail polish composition according to claim 1, in which the shade paste comprises nitrocellulose pigment chips. A nail polish composition according to claim 8, in which the grade of nitrocellulose is less than 80 mPa.s. A nail polish composition according to any preceding claim, which further comprises from 4 to 13% by weight of a modifying resin chosen from toluene sulfonamideformaldehye condensates; sucrose benzoate; sucrose acetate isobutyrate, copolymeric mixtures thereof, alkyds, polyvinyl acetate, polyesters, acrylics, formaldehyde condensates, nylon, rosin resins, acetates and cyclohexanones. A nail polish composition according to any preceding claim, which further comprises a surfactant from anionic, cationic, nonionic or amphoteric surfactants. A nail polish composition according to any preceding claim, which further comprises from 0.1 to 5% by weight of a flocculant. A nail polish composition according to any preceding claim, which further comprises as a dispersant, stearalkonium hectorite. A nail polish composition according to any preceding claim, which further comprises from 1 to 7% by weight of at least one cosmetic grade metallic leafing powder. An applicator means filled with a nail polish composition according to any of claims 1-14, characterised in that it has a non-bristle nib

Inventors: CUNNINGHAM, JOHN, GORDON, PHILIP J., MELNIK, JOSEPH D., REMZ, HARVEY M.
Applicants: CHESEBROUGH-POND'S INC.
Application year: 1985
Main classification: A61K7
IPC codes: A61K8, A61Q3, A45D34