CURABLE RESIN COMPOSITIONS

Abstract: A curable resin composition which comprises (1) a copolymer composed of an aminoalkyl acrylate and/or aminoalkyl methacrylate and an ethylenically unsaturated monomer being formulated with (2) a compound having at least two acryloyl groups in the molecule. The composition can be cured at low temperatures in the range of ordinary temperature to 120°C, and therefore advantageously used for the formation of coating films in the application fields, such as plastics, wood and concrete, where heat treatment cannot be performed. Also, the composition which exhibits excellent adherence toward various kinds of substrates can be used as adhesives and different kinds of primers, as well. Furthermore, the com­ position can provide coating films that excel in terms of water resistance, weathering resistance and solvent resist­ ance, and therefore be utilized for overpaints, etc.

Description: This invention relates to curable resin compositions which excel in low-temperature curing properties. It has been proposed to provide curable resin compositions which are made up of the combinations of polymers having at least two (meth)acryloyl groups in the molecule and polyamines having at least two primary or secondary amino groups in the molecule. Since the compositions are of the non-solvent type, nevertheless, the polymer and amino compound to be used as the starting material are both limited to low-molecular-weight compounds, thus providing the resulting cured materials with unsatisfactory physical properties. Besides, an attempt was made to produce linear polymers by reacting piperazine with methylenebisacrylamide in water (The U.S. Patent No. 2,759,913), but this method affords resins, which take the form of linear polymer and therefore exhibit inferior physical properties. On the other hand, a room-temperature drying type of acrylic resins are superior in transparency, gloss, weathering resistance, etc., but inferior in solvent resistance, impact resistance, adherence, etc. In order to improve these defects there is carried out the method which comprises a copolymerization with functional monomers to thereby convert into a reactive type of resin, followed by a crosslinking reaction with a curing agent, such as epoxy and melamine resins. However, the curing of such a type of resins requires heating of 140 to 180°C for 20 to 40 minutes. This raises the cost of energy and also restricts the kind of usable substrates to metal articles, etc. EP―A―0 134 494 relates to organic solvent solution copolymers of monoethylenically unsaturated monomers including a critical proportion of a tertiary amine monomer, used in an admixture with radiation-curable ethylenically unsaturated liquids. DE―A―32 15 513 relates to a copolymer of an aminoalkyl acrylate or methacrylate and an ethylenically unsaturated monomer whereby the aminoalkyl acrylate contains tertiary amino groups which cannot be cross-linked with ethlenically unsaturated monomers. The problem to be solved by the present application is to provide curable resin compositions which comprise a copolymer, composed of a curable aminoalkyl acrylate and/or aminoalkyl methacrylate and an ethylenically unsaturated monomer added as a crosslinking agent. The present inventors, after extensive investigation, found that the combination of copolymers composed of an aminoalkyl acrylate or aminoalkyl methacrylate and an ethylenically unsaturated monomer and compounds having at least two acryloyl groups in the molecule can yield compositions with excellent low-temperature curing properties, and the finding led to completion of the present invention. Thus, the present invention is concerned with a curable resin composition which comprises (1) a copolymer containing at least two amino groups in the molecule composed of an aminoalkyl acrylate and/or aminoalkyl methacrylate represented by the formula: wherein R¹ is hydrogen or methyl group, R² is an alkylene or hydroxyalkylene group of up to 6 carbon atoms except that R² is not a methylene or a hydroxy methylene group and R³ is hydrogen or an alkyl group of 1 to 6 carbon atoms and an ethylenically unsaturated monomer being formulated with (2) a compound added as a cross-linking agent having at least two acryloyl groups in the molecule whereby the maximum molecular weight per acryloyl group is in the range of 1000. Specific examples of the expression "aminoalkyl acrylate" or "aminoalkyl methacrylate" as used herein include acrylates, such as aminoethyl acrylate, aminopropyl acrylate, amino-n-butyl acrylate, aminohexyl acrylate, N-methylaminoethyl acrylate, N-tert-butylaminoethyl acrylate and aminohydroxypropyl acrylate; and methacrylates, such as aminoethyl methacrylate, amino-n-butyl acrylate, N-methylaminoethyl methacrylate, N-tert-buylaminoethyl methacrylate and aminohydroxypropyl methacrylate. The content of these aminoalkyl acrylates or aminoalkyl methacrylates in the copolymer is normally in the range of 1 to 40 weight %, preferably in the range of 2 to 20 weight %. On the other hand, examples of the term "ethylenically unsaturated monomer" include acrylates such as methyl acrylate, ethyl acrylate, n-butyl acrylate and 2-ethylhexyl acrylate; methacrylates, such as methyl methacrylate, ethyl methacrylate and n-butyl methacrylate; vinyl esters of fatty acids, such as vinyl acetate, and vinyl propionate; aliphatic monoolefins, such as ethylene, propylene and isobutene; aromatic monoolefins, such as styrene and vinyltoluene; and others, for example, acrylonitrile, vinyl chloride and vinyl fluoride. The copolymers, which are composed mainly of acrylates and methacrylates, among the above monomers, are favorable in terms of weathering resistence and yellowing resistence. One or two kinds of the above monomers may be contained in the copolymer, with the content in the copolymer being normally in the range of 60 to 99 weight %, preferably in the range of 80 to 98 weight %. The copolymer being composed of the aminoalkyl acrylate and/or aminoalkyl methacrylate and ethylenically unsaturated monomer is produced by conducting polymerization in the presence of an aromatic solvent, such as toluene, or alcohol solvent, such as isopropanol, or ester solvent, such as ethyl acetate, in accordance with the conventional method, employing a radical polymerization initiator, such as those based on azo or peroxide compounds, solely or in combination with a chain transfer agent, such as mercaptanes, if necessary. The above-described copolymer contains at least two amino groups in the molecule, with its weight average molecular weight suitably being in the range of 1,000 to 1,000,000, preferably in the range of 5,000 to 500,000. The copolymer is used as such, but may be ketiminized with aliphatic or cyclic ketones, such as methyl ethyl ketone, methyl isobutyl ketone and cyclohexanone. The ketiminized product, when used in combination with the below-described compound having at least two acryloyl groups in the molecule, can provide stable one-component compositions. Examples of the compound (2) having at least two acryloyl groups in the molecule, which is useful for crosslinking of the above-described copolymer (1), include diacrylates, such as ethylene glycol diacrylate, propylene glycol diacrylate, tetramethylene glycol diacrylate, hexamethylene glycol diacrylate and bisacryloyloxyethylhydroxyethylisocyanurate; triacrylates, such as glycerine triacrylate, trimethylolpropane triacrylate, pentaerythritol triacrylate and trisacryloyloxyethylisocyanurate, tetraacrylates, such as pentaerythritol tetracrylate, urethane acrylates made up of aliphatic or alicyclic diisocyanates or polyisocyanates formed by the reactions of excess of these diisocyanates with low-molecular-weight active compounds, such as trimethylolpropane, triethanolamine and water, and acrylates, such as hydroxyethyl acrylate and hydroxypropyl acrylate, acrylamides, such as methylenebisacrylamide and bisacrylamidomethyl ether; Reaction products of compounds having an epoxy group with acrylic acid, such as acrylic acid adduct of ethylene glycol diglycidyl ether, acrylic acid adduct of glycerine diglycidyl ether, acrylic acid adduct of bisphenol A diglycidyl ether and acrylic acid adducts of O-cresol novolac polyglycidyl ethers; and polyester acrylates, such as diacrylate of a polyester diol of succinic acid and propylene glycol, diacrylate of a polyester diol of phthalic acid and diethylene glycol, diacrylate of a polyester diol of tetrahydrophthalic acid and diethylene glycol and polyacrylates of polyester polyols of adipic acid and trimethylolpropane and propylene glycol. The maximum molecular weight per acryloyl group of the above-described compounds (2) to be used for the crosslinking is in the range of 1,000. Among the above-described, those having the molecular weight of 80 to 300 are preferable. These compounds can be used either solely or as a mixture of not less than two kinds. The proportion of the copolymer (1) and the compound (2) to be used is preferably: [a number of hydrogen atoms in the amino group of (1)]/[a number of acryloyl groups in (2)] = 0.3 to 5, particularly preferably in the range of 0.5 to 2. The curable resin compound of the present invention as obtained by the above procedure can be used as a solution in organic solvents, such as ethyl acetate, isopropyl alcohol, methyl ethyl ketone, toluene and xylene, and also as an emulsion formed by dispersing in water. If necessary, other resins, such as epoxy resins, plasticisers and fillers can be added. The curable resin composition of the present invention can be cured at low temperatures in the range of ordinary temperatures to 120°C, and therefore advantageously used for the formation of coating films in the application fields, such as plastics, wood and concrete, where heat treatment cannot be performed. Naturally, it can be utilized for the formation of coating films in the application fields, such as metal materials, where high temperature treatment can be affected. Also, the composition of the present invention which exhibits excellent adherence toward various kinds of substrates can be used as adhesives and different kinds of primers, as well. Furthermore, the composition of the present invention can provide coating films that excel in terms of water resistance, weathering resistance and solvent resistance, and therefore be utilized for overpaints. The reference example and examples are described below to illustrate the present invention more specifically. The terms "part" and "%" as shown in the reference example and examples denote "part by weight" and "weight %". Reference Example Resin (A) A 30% toluene solution of a copolymer with a weight average molecular weight of 70,000 having a copolymerization composition of 86 parts of methyl methacrylate and 14 parts of aminoethyl methacrylate. Resin (B) A 30% toluene solution of a copolymer with a weight average molecular weight of 72,000 having a copolymerization composition of 70 parts of methyl methacrylate, 15 parts of butyl acrylate and 15 parts of aminoethyl methacrylate. Resin (C) A 40% toluene solution of a copolymer with a weight average molecular weight of 60,000 having a copolymerization composition of 77 parts of methyl methacrylate, 9 parts of butyl acrylate and 14 parts of aminoethyl methacrylate. Resin (D) A 35% toluene solution of a copolymer with a weight average molecular weight of 30,000 having a copolymerization composition of 40 parts of methyl methacrylate, 40 parts of styrene, 10 parts of butyl acrylate and 10 parts of aminoethyl methacrylate. Resin (E) A 30% toluene solution of a copolymer with a weight average molecular weight of 56,000 having a copolymerization composition of 77 parts of methyl methacrylate, 10 parts of butyl acrylate and 13 parts of aminoethyl acrylate. Resin (F) A resin solution prepared by dissolving the copolymer as described under Resin (A) in methyl iosobutyl ketone to conduct ketiminization, followed by adjustment to 30% of a resin content. Acrylic polyol (1) A 40% toluene solution (an OH equivalent of 1450) of an acrylic copolymer with a weight average molecular weight of 70,000 having a copolymerization composition of 30 parts of methyl methacrylate, 20 parts of styrene, 30 parts of butyl acrylate and 20 parts of hydroxyethyl acrylate. Acrylic polyol (2) Acrydic A―80I® (produced by Dai-Nippon Ink & Chemicals Inc.; with an OH equivalent of 1120). Blocked isocyanate A 60% ethyl acetate/methyl isobutyl ketone (1/1) solution (an NCO equivalent of 445) of a blocked isocyanate prepared by blocking a polyisocyanate formed by the reaction between 1 mole of trimethylolpropane and 3 moles of hexamethylene diisocyanate with methyl ethyl ketoxime. Polyisocyanate A biurettized product of hexamethylene diisocyanate. (Takenate D-165N® produced by Takeda Chemical Industries, Ltd.; with an NCO equivalent of 180). Example 1 A 56 parts portion (as a solid content) of Resin (A), along with 40 parts of titanium dioxide, was allowed to undergo dispersion with a ball mill, and 4 parts of trimethylolpropane triacrylate was added to the dispersion. The mixture was spray-coated onto a mild steel plate to a thickness of baked coating film of 40 to 50 µm, followed by baking at 80°C for 30 min. or at 120°C for 5 min. The resulting coating film showed a pencil hardness of 3H, a 60° specular gloss of 95 and excellent solvent resistance. The coating film exhibited a gloss retention of 85% and a color of 3.0 after irradiation in an accelerated weathering test machine (manufactured by Q-Panel Co. of the U.S.A.) for 1000 hours. Example 2 The procedure of Example 1 was repeatedly carried out, except that Resin (B) and pentaerythritol triacrylate were used in place of Resin (A) and trimethylolpropane triacrylate, respectively. The coating film after being baked at 120°C for 20 minutes exhibited a pencil hardness of H and excellent solvent resistance. Example 3 In accordance with the procedure of Example 1 except that Resin (C) was used in place of Resin (A), a paint was prepared. The coating film after being baked at 120°C for 15 minutes showed a pencil hardness of 2H and excellent solvent resistance. Example 4 By mixing 57 parts (as a solid content) of Resin (D), 40 parts of titanium dioxide and 3 parts of trimethylolpropane triacrylate, a paint was prepared. The coating film after being baked at 120°C for 15 minutes showed a pencil hardness of H and excellent solvent resistance. Example 5 By employing Resin (E) in place of Resin (A) in Example 1, a paint was prepared. The coating film after being baked at 120°C for 10 minutes showed a pencil hardness of 2H and excellent solvent resistance. Example 6 By mixing 93 parts of Resin (F) with 7 parts of trimethylolpropane triacrylate, a one-component resin was prepared. The resin underwent no change at 40°C over the period of not less than 2 months, and remained usable. The coating film after being baked at 80°C for 30 minutes showed a pencil hardness of 2H and excellent solvent resistance. Comparative Example 1 By mixing 14.5 parts of Acrylic polyol (1) with 4.5 parts of Blocked isocyanate, a one-component urethane resin was prepared. The resulting coating film after being baked at 140°C for 20 minutes showed only unsatisfactory solvent resistance. Example 7 By combining Resins (A) and (C) respectively with trimethylolpropane triacrylate in accordance with the procedure of Example 1, the compositions were prepared, and spray-coated onto mild steel plates to a thickness of baked coating films of 40 to 50 µm, followed by curing at 120°C, 80°C, and ambient temperature. The typical properties of the resulting coating films were measured, with the results being shown in Table 1. As Comparative Example 2, there is illustrated the case for the so-called two-component urethane paint based on Acrylic polyol (2) and a polyisocyanate.

Claims: 1. A curable resin composition which comprises (1) a copolymer containing at least two amino groups in the molecule composed of an aminoalkyl acrylate and/or aminoalkyl methacrylate represented by the formula: wherein R¹ is hydrogen or methyl group, R² is an alkylene or hydroxyalkylene group of up to 6 carbon atoms except that R² is not a methylene or a hydroxymethylene group and R³ is hydrogen or an alkyl group of 1 to 6 carbon atoms and an ethylenically unsaturated monomer being formulated with (2) a compound added as a cross-linking agent at least two acryloyl groups in the molecule whereby the maximum molecular weight per acryloyl group is in the range of 1000. 2. A curable resin composition as claimed in Claim 1, wherein the copolymer is one having a weight average molecular weight of 1,000 to 1,000,000. 3. A curable resin composition as claimed in Claim 1, wherein the content of the aminoalkyl acrylate and/or aminoalkyl methacrylate in the copolymer is in the range of 1 to 40 weight %. 4. A curable resin composition as claimed in Claim 1, wherein the ethylenically unsaturated monomer is an acrylate and/or methacrylate. 5. A curable resin composition as claimed in Claim 1, wherein the compound (2) is one having a molecular weight of 80 to 300. 6. A curable resin composition as claimed in Claim 1, wherein the proportion of the copolymer (1) to the compound (2) is [a number of hydrogen atoms in the amino group of (1)]/[a number of acryloyl groups in (2)] and is 0.3 to 5. 7. A curable resin composition as claimed in Claim 1, wherein the compound (2) is trimethylolpropane triacrylate. 8. A curable resin composition as claimed in Claim 1, wherein the compound (2) is pentaerythritol triacrylate.

Inventors: DOURA, FUMIHIRO, FUJINAMI, KIMIYA, NAKAYAMA, TAKEO, SAKAMOTO, TAKUROU
Applicants: TAKEDA CHEMICAL INDUSTRIES, LTD.
Application year: 1985
Main classification: C08F265
IPC codes: C09J4, C08F220, C08F290, C08F20, C08F265, C09D4, C08F299