IMPROVED SILICONE FOAM CONTROL AGENT

Abstract: There are disclosed improved silicone foam control agents comprising (A) a high viscosity dimethylsilicone; (B) a low viscosity dimethylsilicone; (C) a silicone resin composed of (CH₃)₃SiO¹/₂ units and SiO 4/2 units; and (D) amorhous silica. The improved foam control agents provide more foam (suds) controlling than silicone foam control agents pre­ viously known.

Description: IMPROVED SILICONE FOAM CONTROL AGENT Detergent compositions have a well known tendency to produce suds when used with agitation in water. While a certain amount of suds is generally considered desirable, if only for psychological or esthetic reasons, excessive suds production can be inconvenient and costly. It is a common practice, therefore, to include a foam control agent in detergent formulations to control excessive suds. It is known that some silicone anti foams can be used as foam control agents for detergents. For example, U.S. Patent No. 3,933,672, issued Jan. 20, 1976, discloses a detergent composition containing a silicone anti foam This silicone anti foam is releasably incorporated in a water soluble carrier selected from certain substances. A very effective silicone antifoam is described in U.S. Patent No. 3,445,839, issued July 15, 1969, which discloses a method for reducing or preventing foam in an aqueous system by adding thereto a composition consisting of a polydimethylsiloxane fluid having a viscosity of from 20 centistokes to 1500 centistokes, a resin composed of (CH3)3SiO¸ units and SiO2 units, and a silica aerogel. U.S. Patent No. 3,984,200, issued October 5, 1976 to Van-Doesburg, discloses a foam control agent for carpet dyeing. The foam control agent consists essentially of (1) a silicone-glycol copolymer, (2) a foam control agent consisting essentially of a triorganosilyl endblocked polydimethylsiloxane hatng a viscosity of at least 20 centistokes at 250C, silica, and a silicone resin, and (3) an hydroxyl endblocked polydimethylsiloxane having a viscosity of 50 to 200 centistokes at 250C. Application for U.S. Patent Serial No. 498,378, by Pape and Willing, assigned to the assignee of the present invention, discloses an improved silicone composition especially effective in suppressing foam in industrial and petroleum processes. Said composition consists essentially of,from 758 to 998 of a high viscosity alpha,omega-bis(tri methylsiloxy)polydimethylsiloxane, from 0.75 to 18.75% of a low viscosity alpha ,omega-bis (trimethylsiloxy) polydimethyl- siloxane, a certain silicone resin, and amorphous silica. This invention relates to a silicone composition that is useful as a foam control agent for detergent compositions and for controlling foam generally. In another aspect, this invention relates to improved detergent compositions which contain the silicone foam control agent, and to a method of controlling excessive suds. It is an object of this invention to provide improved silicone foam control agents. It is a further object to provide detergent compositions having controlled sudsing behavior The compositions of the present invention relate to a novel foam control agent comprising: (A) from 1 to 758 of a high viscosity alpha ,omega-bis (trimethylsiloxy) polydimethylsiloxane; (B) from 15.0 to 87% of a low viscosity alpha, omega-bis (trimethylsiloxy) polydimethylsiloxane: - (C} - from 2.0 to 208 of a certain silicone resin; and (D) from 4 to 30% of amorphous silica. In another aspect, the present invention relates to detergent compositions containing said foam control composition. The present invention relates to a composition comprising (1) 100 parts by weight of a detergent, and (2) 0.5 to 5 parts by weight of a foam control agent, said agent comprising (A) from 1% to 75% of alpha,omega-bis(trimethyl siloxy)polydimethylsiloxane having a viscosity of from 10,000 centistokes to 200,000 centistokes at 250C; (B) from 15% to 87% of alpha, omega-bis (trimethylsiloxy) polydimethylsiloxane having a viscosity of from 100 centistokes to 5000 centistokes, at 250C; (C) from 2% to 20% of a silicone resin composed of (CH3)3SiO¸ units and Six4/2 units, the ratio of said (CH3)3SiO¸ units to SiO4,2 units being from 0.4:1 to 1.2:1; and (D) from 4% to 30% of amorphous silica having a surface area of from 50m2/g to 400 m2/g; the above percentages being percentages by weight, based on the total weight of the foam control agent. The present invention further relates to a foam control agent, said agent comprising (A) from 1% to 75% of alpha,omega-bis(trimethylsiloxy)polydimethylsiloxane having a viscosity of from 10,000 centistokes to 200,000 centistokes at 250C; (B) from 15% to 87% of alpha,omega-bis(trimethylsiloxy)polydimethylsiloxane having a viscosity of from 100 centistokes to 5000 centistokes at 250C; (C) from 2% to20% of a silicone resin composed of (CH3)3SiO¸ units and Six,/2 units, the ratio of said (CH3)3SiO¸ units to SiO4/2 units being from 0.4:1 to 1.2:1; and (D) from 4% to 30% of amorphous silica having a surface area of from 50 m2lg to 400 m2/g, all of the above percentages being percentages by weight, based on the total weight of the foam control agent. In an alternate embodiment, the present invention relates to the use of said foam control agent in a method of controlling excessive sudsing. Component (A) of the present invention is a high viscosity alpha,omega-bws(trimethylsiloxyYpolydimethyl- siloxane fluid having a viscosity of from 10,000 centistokes to 200,000 centistokes at 250C; more preferably, said fluid has a viscosity of from about 40,000 centistokes to about 150,000 centistokes at 2500 Component (A) is present in the compositions of the present invention from 1% to 75% by weight, based on the total weight of the composition. More preferably, component (A) is present from 2% to 50% by weight, based on the total weight of the composition. Most preferably, component (A) is present from 5% to 40% by weight, based on the total weight of the composition. Two or more fluids can be blended to form component (A), so long as the fluids all have viscosities of from 10,000 centistokes to 200,000 centistokes at 2500. Component (B) of the compositions of the present invention is a low viscosity alpha,omega-bis(trimethylsiloxy)polydimethylsiloxane fluid having a viscosity of from 100 centistokes to 5000 centistokes at 2500. Preferably, said fluid has a viscosity of 500 centistokes to 2000 centistokes at 2500. Component -(B) is present from 15% to 87t by weight, based on the total weight of the composition. More preferably, component (B) is present from 20% to 85% by weight, based on the total weight of the composition. Most preferably, component (B) is present from 30% to 70%, by weight, based on the total weight of the composition. Two or more fluids can be blended to form component (B), so long as the fluids all have viscosities of from 100 centistokes to 5000 centistokes at 250C. The viscosity of an alpha,omega-bis(trimethyl siloxy)polydimethylsiloxane fluid used as Component (A) or Component (B) of the compositions of the present invention can be measured by a variety of well-known methods. Viscosities as referred to herein are as measured by capillary viscometry. The alpha, omega-bis (trimethylsiloxy) polydimethyl- siloxane fluids used in preparing the compositions of the present invention are quite well known and widely available. Methods of synthesis of said fluids are also well known and need not be elaborated upon herein. Component (C) of the compositions of the present invention is a siloxane resin composed of (CH3)3S iO¸ units and Six412 units. Such resins are well-known and commercially available. The synthesis of such resins is well documented in the organosilicon chemistry literature, and need not be detailed herein. The ratio of (CH3)3SiO¸ units to SiO4/2 units in the siloxane resin, Component (C), is from 0.4:1 to 1.2:1. Preferably, the ratio of (CH3)3SiO¸ units to SiO4/2 units is from 0.6:1 to 1:1. Component (C) is present from 2% to 20% by weight, based on the total weight of the composition. More preferably, Component (C) is present from 4% to 15% by weight, based on the total weight of the composition. Most preferably, Component (C) is present from 5% to 10% by weight, based on the total weight of the composition. Component (D) is an amorphous silica having a surface area of from 50m2/g to 400m2/g. More preferably, component (D) has a surface area of from 100m2/g to 300 m2/g. Amorphous silica is commercially available from numerous sources. Surface area is normally measured and reported by the manufacturer of said silica. Such methods astitration methods, or the B.E.T. differential adsorption method are used to measure the surface area of amorphous silica. Amorphous silica is available in three main types, classified according to the method of manufacture. These three types are silica gel, fume silica, and precipitated silica. Silica gel is manufactured by acidifying an aqueous solution of sodium silicate, which causes the formation of an SiO2 gel. This SiO2 gel is mechanically broken up, washed free of salt and acid, and then dried. Fume silica is obtained by condensing vapors of SiO. SiO2 vapors can be produced by heating crystalline SiO2, such as high purity quartz, passing crystalline SiO2 into a high temperature plasma arc, or, most commonly, the SiO2 vapors can be produced by reacting SiC14 and H2 with 02. Precipitated silica can be produced by chemically destabilizing an aqueous solution of sodium silicate. A fine precipitate is formed upon chemical destabilization, and said precipitate is subsequently washed and dried. While it is believed that any amorphous silica having the required surface area can be used in the compositions of the present invention, the use of precipitated silica- is preferred. Amorphous silica, component (D) in the compositions of the present invention, is present froi 4% to 308 by weight, based on the total weight of the composition. biost preferably, component (D) is present from 9% to 13% by weight, based on the total weight of the composition. The amorphous silica used as Component (D) in the compositions of the present invention can be chemically modified or treated, such as treated with organoalkoxy silages or organohalosilanes in any well-known manner, if desired. At the present time, it is believed that the following formulation represents the optimum foam control agent for incorporating in a detergent composition: Component (A): about 30%; Component (B): about 52.5%; Component (C): about 7%; and Component (D): about 10.5%. Compositions of the present invention can be prepared by two types of general procedures, one of which is preferred. In the first, preferred, general procedure, Components (B), (C), and (D) are thoroughly mixed, and heated to provide a concentrate. The appropriate amount of component (A) or component (A) and additional component (B), is then added to said concentrate with simple mixing, thus producing the compositions of the present invention. In a second type of general procedure, components (A), (B), (C), and (D) are all thoroughly mixed, and heated, thus providing compositions of the present invention. Thorough mixing, as referred to herein, can be accomplished by high shear mechanical mixers, such as high intensity mixers, colloid mills, and the like. Heating can be accomplished by heating either the mixture of components (A), (B), (C), and (D), or mixing components (B), (cox, and (D) together at a temperature of from about 1000C to about 2500C, and maintaining said temperature for a period of time from about 5 minutes to about 6 hours. Exemplary of methods that can be used to prepare the compositions of the present invention are the following: In a first, and preferred exemplary method, components (B), (C), and (D) are first mixed together in a colloid mill, then heated to a temperature of 2000C, and said temperature is maintained for about 2 hours. The resulting concentrate of components (B), (C), and (D) is cooled to room temperature, and the appropriate amount of component (A), or component (A) plus additional component (B), is added to said concentrate. This four component mixture is stirred with a paddle stirrer for 5 minutes. In a second exemplary method, components (A), (B), (C) and (D) are first thoroughly mixed in a high intensity mixer, then transferred to a vessel, where said components are heated to a temperature of 1500C, and said temperature is maintained for 1 hour, resulting in a foam control composition of the present invention. It is beneficial to include a small amount of a basic material in the mixture of components (B), (C), and (D), or in the mixture of components (A), (B), (C), and (D). Thus, for example, adding 1 part of 10% aqueous sodium hydroxide per each 100 parts of silicone has been found to be beneficial, the above parts being parts by weight. The above exemplary methods are set forth for purposes of illustration. Those skilled in the art will recognize a variety of other methods suitable to thoroughly mix and heat the components to form a composition of the present invention. The detergent compositions of the present invention are obtained by combining the foam control agent of the present invention with conventional components of a detergent composition. The detergent composition typically comprises one or more surfactants, and various other components. The surfactant is chosen from nonionic, cationic, anionic, amphoteric, and zwitterionic surfactants. Suitable surfactants for use as the detergent include synthetic detergents as well as the well known natural "soaps", i.e. salts of fatty acids. Among other components that are useful in the detergent compositions of this invention are builders, softeners; bacteriostats, bactericides, pH adjusters, dyes, fluorescers, corrosion inhibitors, bleaching agents, thickeners, fillers, anticaking agents, perfumes, enzymes, and other optional additives well known to those of skill in the art. Of course, any components known to adversely affect the suds control agent, or discovered to adversely effect the suds control agent, are to be avoided. While the foam control agent can be incorporated directly into many detergents, it will generally be preferred to incorporate the foam control agent into the detergent in a manner such that it is isolated to some degree from alkaline detergent constituents. Such isolation can be achieved by, e.g., adsorbing the suds control agent onto a neutral filler, or encapsulating the suds control agent in a neutral, water-soluble component, such as gelatin, starch or the like. Isolation of a suds con'trol agent in such a manner is an expedient well known to those of skill in the art. Frogs40.05 parts to 5 parts by weight of the suds control agent of this invention are combined with the detergent constituents; more preferably from 0.1 parts to 25-arts are added; most preferably from 0.2 part to 2 parts are added, all the above parts being by weight, based on the total weight of the detergent composition. The detergent compositions of the present invention are useful laundry detergents, dishwashing detergents, especially dishwashing machine detergents, cosmetic detergents, such as hand soaps or shampoos, and other types of detergents. The following examples are presented to further teach how to make and use the composition and how to practice the method of the present invention. All parts and percentages are by weight unless otherwise indicated. Viscosity values reported in the Examples were measured by capillary viscometry at 250C. The performance of suds control agents was measured by the Hot Pump Test. The Hot Pump Test was conducted with a special apparatus, wherein a foaming solution was pumped rapidly from an outlet at the bottom of a 2 liter stainless steel beaker to the top of the beaker through small bore stainless steel tubing. The liquid was-expelled from the tubing into the beaker with considerable velocity, thus producing a high degree of agitation. In addition, a 7.62 cm (3 inch) propeller was rotated at 150 rpm at a distance of 1.27 cm ( inch) below the surface of the liquid. For each test, the beaker was partially filled with 1 liter of tap water, to which was added 2 grams'of Tide@ detergent, a product of Proctor and Gamble, Cincinnati, Ohio. The Tides solution which resulted was heated to a temperature of 38#4 C. Each foam control agent sample being tested was introduced as a 1% dispersion in propylene glycol, and the Tide solution and' sample' being tested were circulated, by a pump, through the apparatus, at a rate of 3.35 liters/minute. The concentration of ench sample as a fraction of the total volume of the Tide@ solution was recorded. As the test proceeded, the time required for the height of foam to re,ach' various heights was recorded. This data was used to determine, by graphical extrapolation, the. time required for the foam height to reach 7.62 cm (3 inches). The number thus obtained was recorded for each sample. Fresh Tides solution was prepared for each sample tested. Examples 1-14 A concentrate of components (B), (C), and (D) was made by mixing together in a vessel equipped with means for agitation: (B) 75% of alpha, omega-bis (trimethylsiloxy)- polydimethylsiloxane having a viscosity of 1000 centistokes; (C) 10% of a silicone resin composed of (CH3) 3Sio@ units and Sio4/2 units in a ratio between 0.6-1 and 1:1; and (D) 15% of precipitated silica having a surface area of approximately 300 m2/g. The mixture of (B),- (Cj, and (D) was heated to a temperature-of about 2000C and the pressure in the vessel was reduced to 400 mm Hg. After 4 hours of being agitated under the above conditions of,temperature and pressure, the resulting concentrate of components (B), (C), and (D) was removed from the vessel and allowed to cool to room temperature. Examples 1-14 were generated by adding various amounts of alpha, omega-bis (trimethylsiloxy) polvdimethyl siloxane having a viscosity of about 100,000 centistokes, and additional component (B) to the above concentrate. The compositions df Examples 1-14 are found in Table 1, along with the performance results of each sample in the Hot Pump Test. Examples 15-24 In Examples 15-24, compositions were prepared by mixing together components (A), (B), (C), and (D), along with 1 part of 10% aqueous NaOH solution per 100 parts of silica. The resulting mixtures of four components and NaOH solution were passed through a colloid mill with a gap setting of 0.10 cm (0.040 inches). The milled mixtures were heated in a vessel equipped with a stirrer to a temperature of 211 + IOOC, with, a nitrogen purge and continuous stirring, for 2 hours. After 2 hours, the mixtures were removed from the vessel and allowed to come to room temperature. Each Example was tested by the Hot Pump Test. The compositions of Examples 15-245 along with the results obtained for each in the Hot Pump Test are found in Table 2. Comparisons 1, 2, and 3, exemplary of prior art foam control agents, were also tested by the Hot Pump Test, and the results displayed in Table 2. Example 25 A composition of the present invention was made having the following composition: A) 70.0% of alpha,omega-bis(trimethylsiloxy)polydi methylsiloxane having a viscosity of 12,500 centistokes at 25- C, and 4.5% of alpha, omega-bis 9trimethylisiloxy) polydi methylsiloxane having a viscosity of 96,000 centistokes' at 250C; B) - 18% of alpha,omega-bis (trimethylsiloxy) methylsiloxane having a viscosity of 1000 centistokes at 25 C, C) 3.0% of the silicone resin of Example 1; and D) 4.5 % of the precipated silica of Example 1. The foam controlling effectiveness of this composition was evaluated by the following test. Ten and 50 parts per million respectively of the composition of this Example, were added to solutions consisting of 1% Triton X-100 (isoctyl phenyl polyethoxy ethanol), a product of the Rohm and Haas Co. of Philadelphia PA, and 99% water. The resultant mixture was shaken for various lengths of time on a mechanical shaker and the time 'required for the foam to collapse, then break were recorded. The results of this testing are found in Table 3. Test results for comparison 2 are also included. Note that Example 25 is a superior defoamer to Comparison 2 of Table 2, especially at longer shake times. Table 3 Collapse Time and Break Time Collapse/Break Time in Seconds Shake time: 10 sec. 40 sec. 1 min. 2 min. 5 min. 10 min. Example 25 at 10 ppm 19/25 25/27 26/35 21/30 -- - at 50 ppm 4/5 4/6 3/5 6/8 12/17 24/30 Comparison 2 at 50 ppm 3/5 8/12 9/18 9/20 14/29' 25/44 Table 1 SUDS CONTROL PERFORMANCE Component Component Component Component (A) (B) (C) (D) Pump Test Results (min) % 100,000 % 1,000 % % ppm of sude control agent1 Example centistoke fluid centistocke fluid resin SiO2 10 20 30 40 1 2 78 8 12 18.2 2 5 82.5 5 7.5 14.2 3 5 82.5 5 7.5 7.5 4 10 70 8 12 16.1 5 10 70 8 12 20.5 6 18 62 8 12 18.6 7 18 64.5 7 10.5 7.4 13.3 15.9 16.5 8 25 62.5 5 7.5 17.7 9 25 62.5 5 7.5 18.5 10 25 62.5 5 7.5 17.9 11 30 52.5 7 10.5 10 16.3 15.7 19.0 12 40 55 2 3 14.0 13 45 42.5 5 7.5 27.8 14 45 42.5 5 7.5 14.7 1. Parts per million of foam control agent applied to 1 liter of 0.2% Tide# solution. Thus, 10 ppm is the equivalent of 0.5 parts per 100 parts of Tide# detergent, 20 ppm is the equivalent of 0.1 parts, 30 ppm is the equivalent of 1.5 parts, and 40 ppm is the equivalent of 2 parts. Table 2 Suds Control Performance Component Component Component Component (A) (B) (C) (D) % 77,300 % 1,000 % % Pump Test Results (min) Example centistoke fluid centistocke fluid resin SiO2 ppm of foam control agent 10 20 15 14 57 15 14 8.8 11.4 16 15 60 10 15 9.6 13.2 17 15 60 10 15 7.3 12.2 17 15 60 10 15 9.9 12.6 19 16 64 4 16 7.3 13.0 20 16 64 4 16 5.0 13.2 21 28.5 42.5 15 14 12.2 15.6 22 30 45 10 15 10.6 13.6 23 30 45 10 15 8.7 15.4 24 32 48 4 16 10.8 16.3 Comparison 1 0 75 10 15 6.6 9.4 Comparison 2 0 95.41 0 4.6 2.9 4.9 Comparison 3 0 87.5 2.5 10 -- 3.5 1. The viscosity of the fluid was 550 centistockes for Comparison 2.

Claims: Claims: 1. A method of controlling excessive sudsing in the use of detergent, said method comprising adding for each 100 parts by weight of said detergent from 0.05 to 5 parts by weight of a foam control agent, said agent comprising (A) from 1% to 75% of alpha,omega-bis(trimethylsiloxy)- polydimethylsiloxane having a viscosity of from 10,000 centistokes to 200,000 centistokes at 250C; (B) from 15% to 87% of alpha,omega-bis (trimethylsiloxy) polydimethylsiloxane having a viscosity of from 100 centistokes to 5000 centistokes. (C) from 2% to 20% of a silicone resin composed of (CH3)3SiO¸ units and SiO4/2 units, the ratio of said (CH3)3SiO¸ to SiO4,2 units being from 0.4:1 to 1.2:1; and (D) from 4% to 30% of amorphous silica having a surface area of from 50 m2 Ig to 400 m2/g; the above percentages being percentages by weight, based on the total weight of the suds controlling agent. 2. A method as claimed in claim 1 wherein component (A) is present from 2% to 50%; component (B) is present from 20% to 85%; component (C) is present from 4% to 15%; and component (D) is present from 7% to 16%, all of the above percentages being percentages by weight based on the total weight of the suds control agent. 3. A foam control agent, said agent comprising (A) from 1% to 75% of alpha,omega-bis(trimethylsiloxy)- polydimethylsiloxane having a viscosity of from 10,000 centistokes to 200,000 centistokes at 250C; (B) from 15% to 87% of alpha,omega-bis(trimethyl- siloxy)polydimethylsilox,ane having a viscosity of from 100 centistokes to 5000 centistokes at 250C; (C) from 2% to 20% of a silicone resin composed of (CH3)3SiO¸ units and Six4/2 units, the ratio of said (CH3,)3SiO¸ units to SiO4/2 units being from 0.4:1 to 1.2:1; and (D) from 4% to 30% of amorphous silica having a surface area of from 50m2/g to 400 m2 Ig, all of the above percentages being percentages by weight, based on the total weight of the foam control agent. 4. A foam control agent as claimed in claim 3 wherein the amorphous silica is precipitated silica having a surface area of from 100 m2/g to 300 m2/g. 5. A foam control agent as claimed in claim 3 wherein component (A) is present from 2% to 50%; component (B) is present from 20% to 85%; component (C) is present from 4% to 15%; and component (D) is present from 7% to 16%, all of the above percentages being percentages by weight based on the total weight of the foam control agent. 6. A foam control agent as claimed in claim 5 wherein the amorphous silica is precipitated silica having a surface area of from 100 m2/g to 300 m2/g. 7. A foam controlling agent as claimed in claim 5 wherein component (A) is present from 5% to 408; component (B) is present from 30% to 70%; component (C) is present from 5% to 10%; component (D) is present from 9% to 13%; all of the above percentages being percentages by weight based on the total weight of the foam control agent. 8. A foam control agent as claimed in claim 7 wherein the amorphous silica is precipitated silica having a surface area of from 100 m2/g to 300 m2/g.

Inventors: WILLING, DAVID NELSON
Applicants: DOW CORNING CORPORATION
Application year: 1985
Main classification: C11D3
IPC codes: C11D3, B01D19