TREATED NON-WOVEN MATERIAL

Abstract: There is disclosed a non-woven material having a superficial coating of a linear polymeric biguanide in which the recurring unit is of the formula wherein X and Y, which may be the same or different, represent bridging groups in which the total number of carbon atoms in X and Y taken together, directly interposed between the pairs of nitrogen atoms linked thereby, is from 10 to 16, or the salt thereof with an acid. Preferably the polymeric biguanide is polyhexamethylene biguanide dihyd­ rochloride. The material is useful in the form of an article designed for the collection of human body emissions, more particularly disposable nappies, to avoid bacterial activity.

Description: This specification describes a treated non-woven material which is resistant to the activity of microbial species, especially bacteria, and a process for the preparation of such material. It is well known that the generation of noxious malodours, especially the more pungent ammoniacal odours in disposable nappies and the like is caused by the action of micro-organisms on the retained body fluids. This microbiological activity can also result in various skin rashes. Several attempts have been made to control such odours by treating the disposable nappy with a biocide for example chlorhexidine as described in UK 1443086 and a quaternary ammonium compound as described in American Dyestuff Reporter, June 1984, pages 35 to 45. None, however, have found commercial acceptance. It is also known to apply polymeric biguanides to the non-woven materials to be used as wipes for transferring the biocide to a solid surface to be disinfected. Such methods have been described, for example, in US 4311479 and EP 99209. These materials, however, are not designed to retain the biocide and are consequently not adapted to prevent microbiological activity within the non-woven material. It has now been found that polymeric biguanides can be absorbed onto the non-woven materials commonly used in the manufacture of disposable nappies and the like, and that such treated material inhibits the growth of those micro-organisms which give rise to the afore-mentioned malodours and skin rashes. Thus, according to the present invention there is provided an article which is a disposable nappy, a disposable feminine hygiene pad or an incontinence pad, and which is formed from a non-woven material treated with a linear polymeric biguanide in which the recurring unit is of the formula: wherein X and Y, which may be the same or different, represent bridging groups in which the total number of carbon atoms in X and Y taken together, directly interposed between the pairs of nitrogen atoms linked thereby, is from 10 to 16, or the salt thereof with an acid. The bridging groups X and Y, which may be the same or different, preferably comprise polymethylene chains, optionally interrupted by oxygen, nitrogen or sulphur atoms and may incorporate saturated or unsaturated cyclic groups. When the groups X and Y incorporate cyclic groups, the number of carbon atoms directly interposed between pairs of nitrogen atoms include the carbon atoms in the shortest segment of the cyclic group. In a preferred polymeric biguanide, X and Y are both polymethylene groups containing from 3 to 12 carbon atoms and more preferably X and Y are both hexamethylene. The polymeric biguanide preferably has a molecular weight in the range 500 to 20,000 and contains from 5 to 12 biguanide units. Especially preferred is a mixture of polymeric biguanides of the formula: [-(CH₂)₆ - NH - C(:NH) - NH - C(:NH) - NH -] n II wherein n varies from about 6 to 10, having a number average molecular weight from about 1300 to 2200, preferably in the form of salts with hydrochloric acid. The polymeric biguanide has broad spectrum of activity, at very low levels, against bacteria, fungi and yeasts, particularly those associated with the human body. Furthermore, it harmless to macrobiotic systems and, in particular, is not a skin sensitiser. It will, therefore, not give rise to problems when applied to articles which will be in direct contact with the skin for extended periods The article is suitable for the collection of human body emissions, generally fluid emissions, such as urine, and excreta, which are susceptible to bacterial degradation. When such emissions are in contact with bacteria for an extended period, the bacteria can cause changes in the emissions, and chemical substances therein, which can have deleterious effects on the environment, i.e. the body with which the non-woven material is in contact or the surrounding atmosphere. Thus, when disposable nappies become contaminated with urine bacteria present in the anal region effect chemical reactions in the urine which raise the pH and lead to the formation of malodorous chemicals; one product of bacterial activity in urine is the formation of ammonia. Extended contact of the degradation products with the skin can lead to "nappy rash" and general discomfort to the wearer. Various attempts have been made to control odours and 'nappy rashes' by incorporating a biocide into disposable nappies (e.g. DC 5700, American Dyestuff Reporter, June 1984, p.35-45, and chlorhexidine as described in UK 1443086, 23.2.73. assigned to Proctor & Gamble) but none have found commercial acceptance. It has now been found that non-woven materials treated with the polymeric biguanide are particularly suitable for use in the preparation of such articles because of the significant inhibition of bacterial activity when the article becomes contaminated with body emissions. In addition to protection against bacterial activity in the body emissions absorbed on the material, the polymeric biguanide will also provide protection of the non-woven material itself against bacterial action during storage prior to use. The non-woven material preferably contains from 100 ppm up to 100,000 ppm, and more preferably from 500 ppm up to 5000 ppm, of the polymeric biguanide. The non-women material may be treated with the polymeric biguanide during the preparation of the material by, so example, soaking the consitutent fibres in a solution of the polymeric biguanide or spraying the material after formation with a solution thereof. As the polymeric biguanide is readily soluble in water an aqueous solution may be used. The polymeric biguanide has a strong affinity for cellulosic, and related synthetic, materials which are conventionally used for the preparation of the present articles, and it is very efficiently taken up by such materials from an aqueous solution. The polymeric biguanide, in the form of its hydrochloride salt, is extremely soluble in water and aqueous solutions thereof are substantially non-foaming. Since, the absorbent wadding or cellulosic material of the present articles is the major structural component responsible for absorbing body fluids such as urine, this is the most logical place to locate the bioactive compound. In order that additional drying costs are avoided, such application should preferably take place from aqueous media during pre-existing wet processing stages during manufacture. In order to ensure uniform uptake of the biocide, such processes involve high speed agitation of the cellulose fibres in aqueous dispersion. In such a process, the water soluble polymeric biguanide is particularly well suited since it is substantially non-foaming. In this respect it is superior to the chlorhexidine cited in UK 1443086 which foams to a greater extent and also produces a more stable foam. Furthermore, the use of ethanolic solutions of chlorhexidine disclosed and exemplified in UK 1443086 constitute an unacceptable industrial hazard compared with the use of aqueous solutions of the polymeric biguanide. Additionally, chlorhexidine must be protected from light which is not required in the case of the polymeric biguanide, and application of the latter to the appropriate support media leads to no discolouration. When chlorhexidine and the polymeric biguanide are applied to cellulosic substrates, they exhibit similar activity to bacteria such as Pr.vulgaris , although the polymeric biguanide surprisingly shows greater activity against the clinically important Ps. aeruginosa . Quaternary ammonium compounds have also been proposed for use in disposable non-woven materials to suppress odours and control micro-organisms. Generally, they suffer from pronounced foaming deficiencies and lack of substantivity leading to problems during application. They are also not particularly effective in controlling micro organisms in this particular application. This is especially true in the case of the reactive silicon based quaternary ammonium compound, commercially available as DC 5700 from Dow-Corning which has recently been recommended for such outlets (cf. American Dyestuffs Reporter, June 1984, p.35-45). Various techniques have been proposed in the past for assessing body odours, and most have resorted to nasal assessment using panels of experts, e.g. odour control in mens socks using DC 5700 ref "A new durable Antimicrobial Finish for Textiles", R.L.Getting and B.L.Triplett, paper presented at the AATCC National Conference 1978, and more recently the use of polymeric biguanides in deodorant formulations claimed in US 4478821 assigned to Gillette. These methods are not particularly sophisticated. In the American Dyestuff Reporter, June 1984, p.35-45, odour assessment based on the ureolytic activity of Proteus mirabilis and measurement of ammonia in the free-air space is described. This approach whilst being an improvement on the "nasal panel" methodology, lacks refinement and sensitivity, being dependent on pH and the buffering capacity of urine. Consequently, we have developed this approach further to enable the total ammonia content to be accurately measured, even from the earliest stage of bacterial ureolytic activity when all the ammonia generated is bound as inorganic and/or organic salts, and does not manifest itself in the free space above such liquids. This method is based on first determining the ureolytic activity of those micro organisms implicated in odour generation using the technique outlined below. 0.5ml nutrient broth into which individual micro organisms had been repeatedly subcultured (containing approximately 10⁸ cfu/ml) was added to 9.5ml synthetic urine devoid of ammonium ion. 1ml of this inoculated urine was entered into a sterile closed vial and incubated at 36°C. The ammonia generated was determined after 6 hours and 24 hours by dilution with 9ml 0.02N hydrochloric acid followed by millipore filtration, and the ammonium ion content determined by column chromatography using a Dionex chromatographic analyser. The ammonia content found in the samples is listed below (in ppm). 6 hrs 24 hrs Entero bacteria Klebsiella pneumoniae 36 420 Escherichia coli 28 100 Proteus vulgaris 500 1290 Gram positive cocci Staphylococcus aureus 6 280 Streptococcus faecalis 3 74 Anaerobes Lacto bacillus sp. 3 50 Pseudomonads Pseudomonas aeruginosa 1 1200 2220 Pseudomonas aeruginosa 2 78 460 Pseudomonas aeruginosa 3 34 380 Pseudomonas aeruginosa 4 28 290 Yeast Endomycopsis (formerly Candida) albicans 0 24 The invention is further illustrated by the following Examples in which all parts and percentages are by weight unless otherwise indicated. Example 1 The absorbent wadding material was stripped from an adult incontinence pad and 2.5 parts dispersed in 200 parts water by rapid agitation. Sufficient quantities of a 20% aqueous solution of a mixture of polyhexamethylene biguanide dihydrochlorides (PHMB), having number average molecular weights from 1300-2200, were added, at neutral pH, to separate samples of the absorbent wadding, to give 100, 500, 1000 and 3000 ppm of PHMB on the substrate. The PHMB was completely adsorbed. A control sample contained no PHMB but was otherwise treated as the test samples. Each sample was then cast into a paper sheet measuring approximately 7" x 5", and dried on a steam heated calender drum. Two 1" squares of each sheet were placed in a sterile petri dish and wetted with 1 part synthetic urine (pH 6.6). The wetted sheet was then inoculated with the gram-negative, ureolytic bacterium, Proteus vulgaris (ca 10⁶ cFu), and incubated at 37°C. Generation of ammonia was followed by monitoring the changes in pH. After 24 and 48 hours, the sheet derived from the sample impregnated with 1000 ppm PHMB showed no change of pH whereas the sheet derived from the control exhibited a marked increase in pH associated with the characteristic smell of ammonia. Example 2 When the Proteus vulgaris used in Example 1 was replaced by a wild bacterium isolated and cultured from a soiled infant's nappy, substantially similar results were obtained. Example 3 Absorbent paper exhibiting similar grammage (ca 100gm/m²) to the sheets cast from wadding material described in Example 1 was passed through aqueous solutions of PHMB at various concentrations, squeezed and dried on a hot calender drum to give the following concentrations of PHMB on the absorbent papers (cf. table below). 0.5g of the above papers were entered into a sterile closed vial and impregnated with 1ml inoculated synthetic urine prepared by adding 0.5ml broth culture of Proteus vulgaris to 9.5ml urine. After incubation at 36°C, samples were removed at various times, and the ammonia generated determined by extraction into 9ml 0.02N hydrochloric acid, and millipore filtered. The ammonia content was determined by chromatographic analysis and gave the following results expressed in ppm ammonia. Concn. PHMB applied (ppm) Incubation (hours) 1 2 4 6 8 24 0 53 86 307 442 594 1564 125 32 61 224 446 400 640 250 30 42 64 147 210 133 500 20 25 36 40 30 119 1000 20 - - - 20 53 2000 20 - - - 20 40 3000 20 - - - 20 89 Example 4 Absorbent papers containing 1000 ppm PHMB prepared as above were challenged with various micro organisms including a cocktail prepared by mixing equal parts of all eleven organisms. Incubation and analysis was carried out as described in Example 3 and gave the following results. Concn. PHMB applied (ppm) Incubation (hours) Challenging organism 2 4 6 8 13 18 24 0 211 605 1190 1410 1860 2000 1870 Ps.aeruginosa 1 1000 27 32 47 44 120 56 76 Ps.aeruginosa 1 " 15 23 E.coli " 17 18 S.faecalis " 18 14 Lacto bacillus " 18 35 P.vulgaris " 21 24 St.aureus " 14 16 K.pneumoniae " 8 10 E.albicans " 26 36 Ps.aeruginosa 2 " 26 34 Ps.aeruginosa 3 " 18 33 Ps.aeruginosa 4 0 43 410 590 740 1110 1200 1400 Cocktail 1000 17 39 22 27 29 24 27 Cocktail Example 5 Example 4 was repeated except that the 0.5g substrate was impregnated with 1.66ml inoculated urine in place of the 1ml used in Example 3, giving the following results. Concn. PHMB applied (ppm) Incubation (hours) Challenging organism 2 4 6 8 13 18 24 0 280 840 1200 2040 2500 2770 2700 Ps.aeruginosa 1 1000 65 110 230 110 83 119 156 Ps.aeruginosa 1 0 37 151 366 874 1300 1390 1480 Cocktail 1000 16 17 19 17 21 45 35 Cocktail 1000 23 24 23 18 19 17 22 St.aureus 1000 12 10 13 10 15 19 21 K.pneumoniae Example 6 10g wadding was stripped from a commercially available disposable nappy and dispersed in 800ml water by rapid agitation. An aqueous solution of PHMB was added to give 1000 ppm and 1500 ppm PHMB on weight of substrate. The PHMB was rapidly and completely absorbed. Water was removed from the treated wadding by filtration and rotary evaporation, and the wadding "fluffed" by high speed air agitation. The wadding so obtained exhibited no discolouration, with excellent absorbency. 0.5g samples of the treated wadding was entered into a closed sterile vial and impregnated with 1ml inoculated synthetic urine, and analysed as in the foregoing examples to give the following results. Ammonia content expressed in ppm. Concn. PHMB applied (ppm) Incubation (hours) Challenging organism 2 4 6 8 13 18 24 0 208 662 1272 1432 1542 1602 1522 Pr.vulgaris 1000 8 48 143 311 348 298 346 Pr.vulgaris 1500 0 0 0 10 22 86 135 Pr.vulgaris 0 22 270 732 1042 1122 1072 1212 Cocktail of 11 micro organisms 1000 0 0 152 330 418 446 378 1500 0 0 0 27 21 72 52 In the above example, as in the foregoing examples, the untreated substrate when contacted with urine containing a micro organism rapidly acquired an objectional urinal odour which becomes increasingly noticeable after 8 hours incubation. This is especially true when challenged with the cocktail of micro organisms. The treated substrate containing PHMB remains completely free from such odours even after 24 hours and exhibits the freshness of damp domestic washing. Example 7 The absorbent paper containing 1000 ppm PHMB, following challenge with Pr.vulgaris and synthetic urine and incubated for 24 hours was pressed onto a nutrient agar plate, and the plate incubated overnight at 37°C. The plate displayed no microbial growth. A similar paper containing no PHMB when treated in the same manner resulted in heavy growth of the micro organism. Example 8 Absorbent papers (grammage 102gm/m²) were impregnated with PHMB and chlorhexidine by padding through the appropriate aqueous concentration of the bio-active compound, squeezing between mangles to give 120% liquor retention and dried on a heated calender drum. The aqueous solutions of biocide were calculated to give 1000 ppm of PHMB and chlorhexidine on the support. 0.5g support were folded and placed in a sealed sterile vial, and challenged with 1ml synthetic urine made by adding 0.5ml overnight broth culture of Ps.aeruginosa to 9.5ml synthetic urine. After incubation at 36°C, the ammonia generated was extracted into 9ml 0.02N hydrochloric acid, millipore filtered and analysed. The results are tabulated below in ppm ammonia. Biocide added (ppm) Incubation (hours) 2 4 6 8 13 18 24 0 21 20 62 104 200 305 386 1000 ppm PHMB 21 17 19 29 24 29 27 1000 ppm chlorhexidine NA NA NA NA 19 26 280 1000 ppm Arquad 18 15 20 60 118 221 352 433 3000 ppm DC 5700 15 18 51 113 240 373 418 NA - not available. Arquad 18 is the octadecyl trimethyl ammonium chloride supplied by Armour Chemical Division. DC 5700 is trimethoxy silyl propyl octadecyl dimethyl ammonium chloride, sold by Dow Corning. Example 9 Papers were prepared by taking wadding material stripped from a commercially available disposable nappy (2.5g) and dispersing in 200ml water by rapid agitation. 5.0ml of 0.05% aqueous solution of PHMB and chlorhexidine were added respectively, stirred for a further 5 minutes, and the treated pulp cast into a hand sheet by discharging onto a wire screen, pressing to express surplus water and drying on a hot calender drum. 0.5g of the paper (90g/m²) so obtained were treated as in Example 8 to give the following results. Biocide added (ppm) Incubation (hours) 2 4 8 24 1000 ppm PHMB 45 38 38 102 1000 ppm chlorhexidine 33 30 87 327 Example 10 Absorbent paper (ca. 100g/m²) was impregnated by padding and squeezing to give the following uptake of bio-active compound as listed below. 0.5g of the treated papers were challenged with 1ml synthetic urine containing Pr.vulgaris in place of the Ps.aeruginosa used in Example 8, otherwise the conditions and analysis were similar to those described in Example 8. The ammonia generated is as listed in the table. Biocide added (ppm) Incubation (hours) 2 4 6 8 13 18 24 0 49 82 170 184 520 580 700 1000 ppm PHMB 27 28 33 33 60 62 75 2000 ppm chlorhexidine 19 24 26 23 38 63 52 1000 ppm Arquad 18 18 26 29 31 68 66 88 3000 ppm DC 5700 34 47 60 77 150 210 200 Example 11 A disposable nappy was sprayed with an aqueous solution of PHMB such as to produce a loading of 1000 ppm PHMB relative to the weight of wadding. After drying, a 0.5g sample comprising "fluffed" wadding and cover stock material was evaluated in a similar manner to that described in Example 4. When challenged with Ps.aeruginosa and a cocktail of 11 organisms, it exhibited similar results. As in previous examples, the material treated with PHMB when challenged with either the single organism or the cocktail produced no objectionable odours even after 24 hours incubation, whereas the untreated substrate when so treated yield the expected objectionable urinal odours even after 8 hours incubation. Example 12 A commercially available incontinence pad whose construction comprised a plastic backing, coverstock and creped paper as absorbent medium was impregnated with PHMB by padding through an aqueous solution of the biocide followed by squeezing and drying on a hot calender. The biocide retained was 1000 ppm PHMB. 0.5g of this material was treated as described in Example 4, and gave similar results.

Claims: An article which is a disposable nappy, a disposable feminine hygiene pad or an incontinence pad, and which is formed from a non-woven material treated with a linear polymeric biguanide in which the recurring unit is of the formula: wherein X and Y, which may be the same or different, represent bridging groups in which the total number of carbon atoms in X and Y taken together, directly interposed between the pairs of nitrogen atoms linked thereby, is from 10 to 16, or the salt thereof with an acid. An article according to claim 1 which contains absorbent wadding which has been treated with the linear polymeric biguanide. An article according to either claim 1 or claim 2 wherein the groups X and Y are polymethylene groups containing from 3 to 12 carbon atoms. An article according to any one of claims 1 to 3 wherein X and Y are hexamethylene groups. An article according to any one of claims 1 to 4 wherein the polymeric biguanide has a molecular weight in the range 500 to 20,000. An article according to any one of claims 1 to 5 wherein the polymeric biguanide contains from 5 to 12 biguanide units. An article according to any one of claims 1 to 6 wherein the polymeric biguanide is present at a concentration ranging from 500 to 5000 ppm. An article according to any one of claims 1 to 7 wherein the polymeric biguanide is a mixture of polyhexamethylene biguanide dihydrochlorides having number average molecular weights from 1300-2200. The use of an article formed from a non-woven material treated with a linear polymeric biguanide for the collection of human body emissions wherein the linear polymeric biguanide is one in which the recurring unit is of the formula: wherein X and Y, which may be the same or different, represent bridging groups in which the total number of carbon atoms in X and Y taken together, directly interposed between the pairs of nitrogen atoms linked thereby, is from 10 to 16, or the salt thereof with an acid. The use of an article according to claim 9 as a disposable nappy, a disposable feminine hygiene pad or an incontinence pad. The use of an article according to claim 10 wherein the non-woven material is absorbent wadding which has been treated with the linear polymeric biguanide.

Inventors: FAWKES, DAVID MELVILLE
Applicants: IMPERIAL CHEMICAL INDUSTRIES PLC
Application year: 1985
Main classification: A61L15
IPC codes: D06M15, A61F13, A61L15, A61F5, A01N47, D04H1, D21H21