CATALYST MIXTURES

Abstract: The present invention is concerned with catalyst mixtures consisting of two catalysts, characterized in that one is capable of catalysing the conversion of a H₂/CO mixture into oxygen-­ containing organic compounds, and the other is a crystalline iron/­ boron silicate which, after one hour's calcination in air at 500°C, has the following properties. a) an X-ray powder diffraction pattern in which the strongest lines are the four lines mentioned in Table A, and Table A d(Å) 11.1 ± 0.2 10.0 ± 0.2 3.84 ± 0.07 3.72 ± 0.06 b) in the formula which represents the composition of the silicate, expressed in moles of the oxides, the SiO₂/Fe₂O₃ ratio is 20-2000, the SiO₂/B₂O₃ molar ratio 50-5000 and the Fe₂O₃/B₂O₃ molar ratio higher than 1.0. Said catalyst mixtures show higher aromatics selectivity in the preparation of hydrocarbon mixtures from H₂/CO mixtures than such a mixture comprising an iron silicate instead of the above iron/boron silicates.

Description: CATALYST MIXTURES The invention relates to novel catalyst mixtures as well was to the use of these catalyst mixtures in the preparation of hydrocarbon mixtures from mixtures of carbon monoxide and hvdrogen. Mixtures of carbon monoxide and hydrogen can be converted into hydrocarbon mixtures by using a mixture of two catalysts, one being capable of catalysing the conversion of a H2/CO mixture into oxygen-containing organic compounds and the other being a crystalline iron silicate of a special structure, which is capable of catalysing the conversion of organic oxygen compounds into a mixture of hydrocarbons. Said crystalline iron silicates are characterized in that, after one hour's calcination in air at 5000C, they have the following Droperties: a) an X-ray powder diffraction pattern in which the strongest lines are the four lines mentioned in Table A, and TABLE A d(a > 11.1 + 0.2 10.1 + 0.2 3.8lit + 0.07 3.72 + 0.06 b) in the formula which represents the composition of the sili cate, expressed in moles of the oxides, the Si02/Fe203 molar ratio is 20-2000. The crystalline iron silicates which are used in the catalyst mixtures can be prepared starting from an aqueous mixture comprising the following compounds: one or more compounds of an alkali metal (M), one or more organic nitrogen compounds (RN), one or more silicon compounds and one or more compounds containing iron in a trivalent form. The preparation of the crystalline iron silicates is carried out by keeping the mixture at an elevated temperature until the crystalline silicate has formed, separating the latter from the mother liquor, and calcining. When the above-mentioned catalyst mixtures are used for the preparation of hydrocarbon mixtures from H2/C0 mixtures, they show high activity, very high selectivity towards hydrocarbons, very high C3+ selectivity as related to C1+ and good stability. However, the hydrocarbon mixtures obtained have a relatively low aromatics content. In those cases where the preparation of hydrocarbon mixtures with a relatively high aromatics content is desired, the above-mentioned catalyst mixture proves inadequate. Besides the afore-described crystalline iron silicates, there are also knows crystalline boron silicates, which have the same special. structure as the iron silicates. These boron silicates can be prepared in substantially the same manner as the iron silicates, the difference being that in the aqueous mixture from which the iron silicates are prepared, the trivalent iron compound is replaced by a boron compound. In view of the fact that for a number of catalytic uses, such as the isomerization of mixtures of C8 aromatics for the preparation of para-xylene, the boron silicates show the same performance, quality-wise, as the iron silicates, experiments were carried out in order to establish whether the demand for higher aromatics selectivity could be met by substituting in the catalyst mixtures a boron silicate for the iron silicate. The results of these exDeriments were very disappointing. As compared to the catalyst mixtures containing an iron silicate, those in which a boron silicate was present showed considerably lower aromatics selectivities. And also in a number of other areas did the catalyst mixtures containing a boron silicate prove altogether deficient. They showed very low activities, low selectivities towards hydrocarbons, and considerably lower C3+ selectivities in relation to C1+ and stabilities than the catalyst mixtures containing an iron silicate. By reason of these results the crystalline boron silicates must be regarded as totally unfit for use as components in the catalyst mixtures for the preparation of hydrocarbon mixtures from H2/C0 mixtures. In the face of the disappointing results obtained by using the catalyst mixtures containing a crystalline boron silicate, the investigation was continued using catalyst mixtures containing a crystalline silicate in which boron was present in addition to iron. Such silicates, which have the same special structure as the afore-mentioned iron silicates and boron silicates, can be obtained in a simple manner starting from an aqueous mixture which, in addition to the other compounds required for preparing silicates of the desired special structure, contains both a trivalent iron compound and a boron compound. This has surprisingly led to the finding that catalyst mixtures wherein the crystalline silicate component of a special structure is a silicate which, in addition to a given quantity of iron, contains a given quantity of boron, show excellent performance in the preparation of hydrocarbon mixtures from H2/CO mixtures. In comparison with the catalyst mixtures containing an iron silicate, those containing an iron/boron silicate show a considerably higher aromatics selectivity, whilst their activity, selectivity to hydrocarbons, C3+ selectivity as related to C1+ and stability are on an equally high level as for the catalyst mixtures containing an iron silicate. In order for this favourable performance to be achieved it is necessary that in the formula which represents the composition of the silicate used, expressed in moles of the oxides, the SiO2/Fe203 molar ratio is 26-2000, the Si02/B203 molar ratio is 50-5000, and the Fe203/B203 molar ratio is higher than 1.0. The above-descrbied catalyst mixtures containing an iron/boron silicate are novel compositions. The present patent application therefore relates to novel catalyst mixtures comPosed of two catalysts, one being capable of catalysing the conversion of a H2/CO mixture into oxygen-containing organic compounds, and the other being a crystalline iron/boron silicate which, after one hour's calcination in air at 5000C, has the following properties: a) an X-ray powder diffraction pattern in which the strongest lines are the four lines mentioned in Table A, and b) in the formula which represents the comDosition of the sili cate, expressed in moles of the oxides, the Si02/Fe2/03 molar ratio is 20-2000, the Si02/B203 molar ratio is 50-5000 and the Fe203/B203 molar ratio is higher than 1.0 The patent application further relates to the use of these catalyst mixtures in the preparation of hydrocarbon mixtures from H2/CO mixtures. One of the two catalysts in the catalyst mixture according to the invention is a catalyst which is capable of catalysing the conversion of a H2/CO mixture into oxygen-containing organic compounds. The catalyst mixture preferably comprises a catalyst which is capable of converting a H2/CO mixture substantially into methanol and/or dimethyl ether. Very suitable are zinc-containing compositions which, in addition to zinc, comprise one or more of the metals chromium, copper and aluminium. Examples of suitable metal combinations are zinc-chromium, zinc-chromium-copper and zinc-aluminium-copper. Preference is given to the use of catalysts which, in addition to zinc, comprise chromium, in particular catalyst in which the atomic percentage of zinc, calculated on the sum of zinc and chromium, is at least 601 and in particular 60-80%. The above-mentioned zinc-containing compositions are usually prepared by calcining one or more preciDitates which have been obtained by the addition of a basic reacting substance to one or more aqueous solutions containing salts of the metals concerned. Starting from the zinc-containing compositions thus prepared, the catalyst mixtures according to the invention can be obtained by mechanically mixing the particles of the zinc-containing composition and the crystalline iron/boron silicate. Another very attrac tive method of preparing the catalyst mixtures according to the invention is spray drying. Spray drying is a procedure for preparing small globular particles starting from a solid material or a mixture of solids, which has been in use on a commercial scale for many years now. It is carried out bv vaporizing a dispersion in water of the material to be spray dried through a nozzle or from a rotating disc into a hot gas. It is a very suitable procedure for bringing about a very intimate contact between different substances. The preparation of the present catalyst mixtures by spray drying can be carried out by dispersing the crystalline iron/boron silicate in water, together with one or more pecipitates in which zinc and one or more metals chosen from chromium, copper and aluminium are present. which precipitates have been obtained by adding a basic reacting substance to one or more aaueous solutions of salts of the metals concerned, and spray drying the dispersion thus obtained to prepare the desired catalyst mixture. In view of their form, size and strength, the catalyst particles prepared by spray drying are very suitable for use in a fluidized state. As regards the ratio in which the two catalysts are present in the catalyst mixtures according to the invention, it is preferred that per part by weight of the crystalline iron/boron silicate catalyst, the catalyst mixtures should comprise 2.5-12.5 pbw of the catalyst having activity for the conversion of a H2/CO mixture. The crystalline iron/boron silicates used as catalyst components in the catalyst mixtures according to the invention are defined, among other things, with the aid of the X-ray powder diffraction pattern which they displav after one hour's calcination in air at 5000C. In this pattern the strongest lines should be the four lines mentioned in Table A. The complete X-ray powder diffraction pattern of a typical example of the present crystalline iron/boron silicates after one hour's calcination in air at 5000C, is given in Table B. TABLE B d(X) Rel. int. d(X) Rel. int. 11.1 100 3.84 (D) 57 10.0 (D) 70 3.72 (D) 31 8.93 1 3.63 16 7.99 1 3.47 < 1 7.42 2 3.43 5 6.68 7 3.34 2 6.35 11 3.30 5 5.97 17 3.25 1 5.70 7 3.05 8 5.56 10 2.98 11 5.35 2 2.96 3 4.98 (D) 6 2.86 2 4 60 4 2.73 2 4.35 5 2.60 2 4.25 7 2.48 3 4.07 2 2.40 2 4.00 4 (D) = doublet The crystalline iron/boron silicates which are used in the catalyst mixtures according to the invention can be prepared starting from an aqueous solution comprising the following compounds: one or more compounds of an alkali metal (M), one or more organic nitrogen compounds (RN), one or more silicon compounds, one or more compounds in which iron is present in a trivalent form, and one or more boron compounds. The preparation is carried out by keeping the mixture at an elevated temperature until the silicate has formed, and subsequently separating the silicate crystals from the mother liquor. In the aqueous solution from which the silicates are prepared the various compounds should be present in the following molar ratios, expressed - with the exception of the organic nitrogen compounds - as moles of the oxides: M20 : Si02 = 0.01-0.35, RN : Si02 = 0.04-2.0, Si02 : Fe203 = 30-3000, Si02 : B203 = 50-5000, en H20 : Si02 = 5-100. The preparation of the silicates may be carried out either at atmospheric pressure or at an elevated pressure. If reaction temperatures are used which lie above the boiling point of the mixture it is preferred to use an autoclave under autogeneous pressure. The silicates are preferably prepared by keeping the mixture for at least four hours at a temperature between 125 and 1750C. After the formation of the silicates the crystals are separated from the mother liquor, for instance by filtration, decantation or centrifugation. The crvstal mass is subsequently washed with water and finally dried at a temperature between 100 and 2000C. Examples that may be mentioned of suitable compounds which can be used in the preparation of the iron/boron silicates are nitrates, carbonates, hydroxides and oxides of alkali metals; primary, secondary and tertiary alkyl amines and quaternary alkyl ammonium compounds, such as bromides and hydroxides; heterocyclic nitrogen compounds, such as pyridine and siperidine: sodium silicate, silicic acid and amorphous silica: boric acid and borax; the nitrate, sulphate. chloride and hydroxide of trivalent iron. In the preparation of the crystalline iron/boron silicates it is preferred to start from a base mixture in which M is present in a sodium compound and which comprises butylamine as RN compound, amorphous silica a silicon compound and boric acid as boron compound. In the crystalline iron/boron silicates used in the catalyst mixtures according to the invention the Si02/e203 molar ratio should be 20-2000 and the Si02/B203 molar ratio 50-5000. Preferably use is made of crystalline iron/boron silicates which have a Si02/Fe203 molar ratio of 50-300 and a Si02/B203 molar ratio of 100-1000. The silicates prepared as described hereinabove contain alkali metal ions. By using suitable exchange methods these can be replaced by other cations, such as hydrogen ions or ammonium ions. The crystalline iron/boron silicates which are used in the present catalyst mixtures preferably have an alkali metal content of less than 0.05 %w. As stated hereinbefore, the present patent application also relates to the use of the catalyst mixtures according to the invention in the preparation of hydrocarbon mixtures from H2/CO mixtures. Suitable H2/CO mixtures can be prepared by gasification of heavy carbonaceous materials such as coal, or by steam reforming or partial oxidation of light hydrocarbons such as natural gas. Suitable conditions for the conversion of H2/CO mixtures into hydrocarbon mixtures according to the invention are a temperature of 200-5000C and in particular of 300-4500C, a pressure of 1-150 bar and in particular of 5-100 bar and a space velocity of 50-5000 and in particular 300-3000 Nl.l-1.h-1. The above-described process, in which a hydrocarbon mixture is prepared from a H2/CO mixture can very suitably be carried out as an individual process in which the conversion of the H2/CO mixture is performed in a single step. Unconverted synthesis gas can be recirculated, if desired. The process can also very suitably be carried out as part of a multi-step process for the conversion of H2/CO mixtures into hydrocarbon mixtures, in which case two options offer, viz. a) the process is carried out as the first step of a two-step process in which H2 and CO present in the reaction product from the first step - optionallv together with other components from this reaction product - is contacted in a second step with a catalyst comprising one or more metal components which have activity for the conversion of a H2/CO mixture into paraffinic hydrocarbons, and which have been chosen from the group formed by cobalt, nickel and ruthenium, b) the process is carried out as the first step of a three-step Drocess in which the first two steps are conducted as described under a) the catalyst used in the second step being a zirconium-, titanium- or chromium-promoted cobalt catalyst supported on silica, alumina or silica-alumina as carrier, which catalyst has been prepared by impregnation and/or kneading. In this three-step process advantage is taken from the fact that by using a catalytic hydrocracking the high-boiling part of the reaction product from the second step can be converted in high yield into middle distillates. The three-step process mentioned under b) involves carrying out an additional catalytic hydrocracking as a third step following the two-step process as mentioned under a). As feed for de catalytic hydrocracking treatment is chosen at least the part of the reaction product from the second step of which the initial boiling point lies above the final boiling point of the heaviest middle distillate desired as end product. The hydrocracking treatment, which is characterized by a very low hydrogen consumption, yields middle distillates which have a considerably lower pour point than those obtained by the direct conversion of a H2/CO mixture according to Fischer-Tropsch. Catalysts which are very suitable for carrying out the catalytic hydrocracking are those comprising one or more noble metals from Group VIII supported on a carrier. The invention is now illustrated with the aid of the following example. Example Three crystalline silicates (silicates 1-3) were prepared by maintaining mixtures of amorphous silica, sodium hydroxide, butylamine and, either ferric nitrate, or boric acid, or both ferric nitrate and boric acid, in water, in an autoclave under autogeneous pressure and with stirring, for 120 hours at 1500C. After cooling of the reaction mixtures the silicates were filtered off, washed with water until the pH of the wash water was about 8, dried at 1200C and calcined in air for one hour at 500Or. The silicates 1-3 had the following properties a) an X-ray powder diffraction pattern substantially corresponding with that mentioned in Table B, and b) an Si02/Fe203 molar ratio of 100 for iron silicate 1, an Si02/B203 molar ratio of 200 for boron silicate 2, and an Si02/Fe203 molar ratio of 120 and an Si02/B203 molar ratio of 215 for iron/boron silicate 3. The molar composition of the aqueous mixtures from which silicates 1-3 were prepared may be rendered as follows 1.0 Na20 . 25 Si02 . 10 C4H9NH2 . x Fe203 . y B203 . 450 H20, wherein x and y have the following values silicate 1 x = 0.2; y = 0 silicate 2 x = 0 ; y = 0.1 silicate 3 x = 0.2; y = 0.1. From silicates 1-3 were prepared silicates I-III, respectively, by boiling silicates 1-3 with a 1.0 molar NH4N03 solution, washing with water, boiling again with a 1.0 molar NH4NO3 solution and washing, drying at 1200C and calcining at 5000C. Subsequently three catalyst mixtures (catalyst mixtures A-C) were prepared by mixing a ZnO-Cr203 composition with each one of silicates I-III. The Zn atomic percentage of the ZnO-Cr203 composition was 70%. All the catalyst mixtures contained per part by weight of silicate 10 parts by weight of the ZnO-Cr203 composition. Catalyst mixtures A-C were tested for suitability in the preparation of hydrocarbon mixtures from a H2/CO mixture. The testing was carried out in a 50 ml reactor containing a fixed catalyst bed of 7.5 ml volume. In three experiments a H2/CO mixture of a H2/CO molar ratio of 0.5 was passed over each one of catalyst mixtures A-C at a temperature of 3750C, a pressure of 60 bar and a space velocity of 850 Nl.kg-1.h-1. The results of these experiments, measured at run hour 50, are given in Table C. Of the catalyst mixtures and experiments mentioned in Table C only catalyst mixture C and experiment 3 are according to the invention. Catalyst mixtures A and B and experiments 1 and 2 fall outside the scope of the invention. They have been included in the patent application for comparison. TABLE C Experiment No. 1 2 3 Catalyst mixture A B C Silicate No. I II III (H20) conversion, %v 59 19 57 Selectivity towards hydrocarbons, %w 100 66 100 C3+ selectivity, ssw on C1+ 94 81 93 Aromatics, %w on C1+ 20 15 26 Loss of (H2+CO) conversion, %v per 100 h 5 10 5

Claims: CLAIMS 1. Catalyst mixtures consisting of two catalysts, characterized in that one is capable of catalysing the conversion of a H2/CO mixture into oxygen-containing organic compounds, and the other is a crystalline iron/boron silicate which, after one hour's calcination in air at 5000 C, has the following properties a) an X-ray powder diffraction pattern in which the strongest lines are the four lines mentioned in Table A, and Table A d(X) 11.1 + 0.2 10.0 + 0.2 3.84 + 0.07 3.72 + 0.06 b) in the formula which represents the composition of the silicate, expressed in moles of the oxides, the Si02/Fe203 molar ratio is 20-2000, the SiO2/B203 molar ratio 50-5000 and the Fe203/B203 molar ratio higher than 1.0. 2. Catalyst mixtures as claimed in claim 1, characterized in that the catalyst present in the catalyst mixture which is capable of catalysing the conversion of a H2/CO mixture into oxygencontaining organic compounds is a zinc-containing composition which, in addition to zinc, comprises one or more of the metals chromium, copper and aluminium. 3. Catalyst mixtures as claimed in claim 2, characterized in that, in addition to zinc, the zinc-containing composition comprises chromium and that the atomic percentage of zinc, calculated on the sum of zinc and chromium, is at least 60%. Catalyst mixtures as claimed in any one of claims 1-3, characterized in that the silicate present therein has been prepared bv maintaining an aqueous mixture comprising the following compounds: one or more compounds of an alkali metal (M), one or more organic nitrogen compounds (RN), one or more silicon compounds, one or more compounds in which iron is present in a trivalent form and one or more boron compounds, in which mixture the various compounds are present in the following molar ratios, expressed - with the exception of the organic nitrogen compounds in moles of the oxides: M20 : SiO2 = 0.01-0.35, RN : SiO2 = 0.04-2.0, SiO2: Fe203 = 30-3000, Six2: B203 = 50-5000, and H2O : SiO2 = 5-100 at an elevated temperature until the crystalline silicate has formed, which is subsequently separated from the mother liquor and calcined. 5. Catalyst mixtures as claimed in claim 4, characterized in that in the preparation of the silicate a sodium compound is used as alkali metal compound, butylamine as RN compound, amorphous silica as silicon compound and boric acid as boron compound. 6. Catalyst mixtures as claimed in any one of claims 1-5, characterized in that the silicate present therein has an SiO2/Fe203 molar ratio of 50-300 and an SiO2/B203 molar ratio of 100-1000. 7. Catalyst mixtures as claimed in any one of claims 1-6, characterized in that the silicate Dresent therein has an alkali metal content lower than 0.05 tw. 8. Catalyst mixtures as claimed in any one of claims 1-7, characterized in that per part by weight of the crystalline silicate catalyst they comprise 2.5-12.5 parts bv weight of the catalyst with activity for the conversion of the H2/CO mixture. 9. Catalyst mixtures as claimed in any one of claims 1-8, characterized in that they have been prepared by spray drying. 10. Catalyst mixtures as claimed in claim 1, substantially as described hereinbefore, and in particular with reference to the example. 11. A process for the preparation of a hydrocarbon mixture, characterized in that a H2/CO mixture is contacted with a catalyst mixture as claimed in claim 10. 12. A process as claimed in claim 11, characterized in that the H2/CO mixture has been obtained by gasification of a heavy carbonaceous material such as coal, or by steam reforming or partial oxidation of light hydrocarbons such as natural gas. 13. A process as claimed in claim 11 or 12, characterized in that it is carried out at a temperature of 200-5000C, a pressure of 1-150 bar and a space velocity of 50-5000 Nl.l-1.h-1. 14. A process as claimed in claim 13, characterized in that it is carried out at a temperature of 300-4500C, a pressure of 5-100 bar and a space velocity of 300-3000 Nl.l-1.h-1. 15. A process as claimed in any one of claims 11-14, characterized in that it is used as the first step of a two-step process, that H2 and CO present in the reaction product from the first step - together with other components of this reaction product, if desired - is contacted in the second step with a catalyst comprising one or more metal components having activity for the conversion of a H2/CO mixture into paraffinic hydrocarbons, which metal components have been chosen from the group formed by cobalt, nickel and ruthenium. 16. A process as claimed in any one of claims 11-14, characterized in that it is used as the first steD of a three-step process, that the first two steps are carried out as stated in claim 15, that in the second step use is made of a zirconium-, titanium- or chromium-promoted cobalt catalyst supported on silica, alumina or silica-alumina as carrier, which catalyst has been prepared by impregnation and/or kneading, and that middle distillates are prepared by separating from the reaction product from the second step at least the part whose initial boiling point lies above the final boiling point of the heaviest middle distillate desired as end product and subjecting it in the third step to a catalytic hydrocracking treatment. 17. A process for the preparation of a hydrocarbon mixture as claimed in claim 11, substantially as described hereinbefore and in particular with reference to the example. 18. Hydrocarbon mixtures whenever prepared by a process as described in claim 17.

Inventors: HUIZINGA, TOM, MINDERHOUD, JOHANNES KORNELIS, SIE, SWAN TIONG
Applicants: SHELL INTERNATIONALE RESEARCH MAATSCHAPPIJ B.V.
Application year: 1985
Main classification: B01J37
IPC codes: B01J21, B01J23, C07C29, B01J29, C10C3, C07C1, C07C27, C07B61, C10G3, C07C67