PERPENDICULAR MAGNETIC RECORDING MEDIUM

Abstract: Disclosed is a perpendicular magnetic recording medium wherein an under layer (2) made of a material containing Si and/or Ge as its principal ingredient is depo­ sited on a substrate (1), and a perpendicular magnetic film (3) made of a Co-based alloy is deposited on the under layer. With the perpendicular magnetic recording medium, the perpendicular magnetic film has an enhanced degree of C-axis orientation, and the bond strength between the perpendicular magnetic film and the substrate is also enhanced when the substrate is non-metallic.

Description: Background of the invention: The present invention relates to a magnetic recording medium suited for a perpendicular magnetic recording system. The perpendicular magnetic recording system performs recording in a direction perpendicular to the plane of a recording medium film, and it is a system which is suitable for enhancing a recording density because a demagnetizing field within each bit in the case of high density recording is low. As magnetic recording media which are used for this purpose, there are Co-based alloy films such as Co-Cr, Co-V, Co-Mo, Co-W, Co-Re, Co-O, Co-Cr-Rh, Co-Cr-Ru and Co-Ni-O films. Any of these Co-based alloys has an hexagonal close-packed (h.c.p.) crystal structure, and possesses the merit that fine crystal grains constituting the thin film are liable to c-axis orientation. In order to enhance magnetic recording characteristics, the degree of c-axis orientation of the thin film needs to be raised. The perpendicular magnetic recording media presently in use are such that the Co-based alloy film is stuck on a non-magnetic substrate directly or through a soft magnetic thin film such as a permalloy film (an Ni-Fe alloy whose principal ingredient is Ni and which exhibits a high magnetic permeability). For example a plastics film of polyimide or polyethylene terephthalate, an Al or glass plate are employed as the non-magnetic substrates. In case of forming the Co-based alloy film on such a substrate, this Co-based alloy film must have a good adhesion with the substrate and a high degree of c-axis orientation. However, in a case where the Co-based alloy film is directly stuck to the plastics film or the glass plate by an evaporation method, there are the problems that the bond strength is insufficient, so the Co-based alloy film is prone to peel off from the substrate, and that the property of c-axis orientation has variation due to a subtle difference in the cleanness of the substrate surface. Besides, in a case where the Co-based alloy film is stuck on the metal substrate such as the Al substrate or on the soft magnetic metal film such as a permalloy film, the crystal orientation of the grains of the underlying metal exerts an adverse effect on the degree of c-axis orientation of the Co-based alloy which is to be stuck on the metal. For example, the materials Al and permalloy have a face-centered cubic (f.c.c.) crystal structures, and it is known that as the (111) plane of the f.c.c. structure is more parallel to the plane of the substrate, the degree of c-axis orientation of the Co-based alloy to be stuck thereon is better. Since, however, the parallelism of the (111) plane of the actual substrate or soft magnetic metal thin film to the substrate plane is not very good, there is the problem that the degree of c-axis orientation of the Co-based alloy becomes worse than in the case of sticking the alloy film to the plastics or glass substrate. Further, as disclosed in the official gazette of JP-A-56-70618, the degree of c-axis orientation of a Co-Cr alloy film is improved when the Co-Cr alloy film is formed on a substrate which is so prepared that the c-axis of a substance having the crystal structure of hexagonal close-packed lattice is oriented perpendicularly to the surface of the substrate. Since, however, the crystal orientation of the underlying substances of the h.c.p. structure is problematic also in this case, unfavorably the characteristics of the Co-based alloy are governed by the property of crystal orientation of the underlying film. The following references are cited to show the state of the art; i) Official Gazette of JP-A-56-70618, ii) Official Gazette of JP-A-58-91 and iii) EP-A-0 048 418. EP-A-0 048 414 discloses a perpendicular magnetic recording medium comprising a magnetic recording layer made of a Co-Cr alloy and formed on a layer of a material of low coercive force. The layer of low coercive force is formed on a nonmagnetic base and may be made of a Ni-Fe alloy as well as of a Ni-Fe-Mo alloy or Ni-P alloy. Summary of the invention: An object of the present invention is to eliminate the difficulties of the prior arts, and to provide a perpendicular magnetic recording medium according to which, in case of employing a non-metallic substrate such as plastics or glass substrate, the bond strength thereof with a Co-based alloy film to be stuck thereon is enhanced and besides enhancement in the degree of c-axis orientation of the Co-based alloy film is permitted, and in case of sticking a Co-based alloy film on a metal substrate such as Al substrate or on a soft magnetic metal film, the degree of c-axis orientation of the alloy film is improved. This object is obtained by a perpendicular magnetic recording medium as defined in claim 1. In accordance with the present invention, a perpendicular magnetic recording medium comprises a substrate, an under layer which is made of a material containing as its principal ingredient at least one element selected from the group consisting of Si and Ge and which is deposited on said substrate, and a perpendicular magnetic film (namely, a film with perpendicular magnetic anisotropy) which is made of a Co-based alloy and which is deposited on said under layer. The inventors' experiments have revealed that, in a case where before sticking a Co-based alloy, an under layer of a thin film, which is made of Si or Ge being a metalloid or an alloy thereof, is formed on a substrate, followed by the sticking of the Co-based alloy film, a film having a favorable property of c-axis orientation is produced with good reproducibility. The degree of c-axis orientation of the Co-based alloy in the case of sticking the thin film of Si, Ge or the alloy thereof exhibited a tendency to have a substantially constant good value irrespective of the kind of the substrate. This tendency was noted with any of the evaporation method, a sputtering method and an ion-beam sputtering method. Accordingly, any of the film depositing methods mentioned above can be used for forming the under layer and the Co-based alloy film. It has also been revealed that, when a Co-based alloy is stuck on a substrate of a non-metallic material such as plastics or glass, a layer of Si, Ge or an alloy thereof is formed between them, thereby to attain an enhanced bond strength which is effective to prevent the exfoliation of the Co-based alloy film or the cracking thereof. The deposition of the under layer of principally Si and/or Ge and that of the Co-based alloy film should desirably be continuously performed within an identical vacuum apparatus. When the under layer is deposited and then exposed to the air, its surface is oxidized or contaminated, so that the degree of c-axis orientation of the Co-based alloy film worsens. The under layer film in the present invention, the principal ingredient of which is Si and/or Ge, forms a new substrate surface for forming the Co-based alloy film and possesses properties desirable for obtaining the film of good c-axis orientation. The provision of such under layer is very effective for forming the Co-based alloy film of good c-axis orientation reproducibly on any of almost all substrate materials such as plastics, glass, Al and permalloy. When the thickness of the under layer of any of the aforementioned materials is less than 10 nm ( 100 Å), the elimination of the influence of the substrate material is insufficient, and hence, the thickness needs to be at least 10 nm (100 Å). Even when the thickness of the under layer is as great as 1 µm or above, the effects stated above hold similarly, and, however, in such a case, a period of time for forming the film becomes long or the film-formed on the plastics material is liable to crack. Accordingly, the thickness of the layer is desired to be from at least 10 nm (100 Å) to at most 1 µm, and the range of the thickness more disirable in practical use is from at least 15 nm (150 Å) to at most 100 nm (1000 Å). The material which constructs the under layer to be interposed between the substrate and the perpendicular magnetic layer is any of Si, Ge, and an Si-Ge alloy (the composition ratio of which is not especially restricted), and one or more other elements may well be further added by employing it as the principal ingredient. In the case of adding any element other than Si and Ge, the quantity of addition thereof shall be within a range in which the crystal structure of the under layer formed maintains a diamond structure, an amorphous structure or the mixed structure thereof. When the addition of the other element in an amount exceeding this range results in the under-layer crystal structure which contains any structure other than the diamond structure and the amorphous structure, unfavorably the effects of the present invention lower. The permissible quantity of addition differs depending upon elements, in such a manner that it is 10 at.% or less for many elements, but that it is as large as 40 at.% or more for some elements including Sn. The addition of the other element makes it possible to improve, for example, adhesion and corrosion resistance. Further, as the Co-based alloys of the perpendicular magnetic films, all employed for the perpendicular magnetic recording can be used in the present invention. Especially Co-Cr alloys stated, for example, in the official gazette of JP-A-58-91 are common, and Co alloys each containing V, Mo, W, Re, O, Cr-Rh, Cr-Ru, or Ni-O are also known. It has been known that a magnetic recording medium wherein a substrate at least one surface of which is made of a soft magnetic material such as permalloy is provided with a perpendicular magnetic film of a Co-based alloy on the soft magnetic material surface is advantageous for enhancing recording and reproducing characteristics. The under layer whose principal ingredient is Si and/or Ge is deposited on the soft magnetic material surface, and the perpendicular magnetic film is deposited on the under layer. Brief description of the drawings: Fig. 1 is a sectional view showing a perpendicular magnetic recording medium in an embodiment of the present invention, while Fig. 2 is a sectional view showing a perpendicular magnetic recording medium in another embodiment of the present invention. Description of the preferred embodiments: Example 1: Using a polyimide film as a substrate, films of a structure shown in Fig. 1 were produced by the following steps. While a substrate 1 made of a polyimide film was heated to 150°C in a vacuum of 1.3x 10-4 Pa (1 x 10⁻⁶ Torr), Si was first vacuum-evaporated as an under layer material to a thickness of 30 nm (300 Å) at a rate of 1 nm/s (10 Å/s), to form an under layer 2. Subsequently, in the same vacuum vessel as used for the above step, Co-22 wt.% Cr was vacuum-evaporated to a thickness of 500 nm (5000 Å) at a rate of 8 nm/s (80 Å/s) into a Co-based alloy film 3. Then, a perpendicular magnetic recording medium having the structure shown in Fig. 1 was fabricated. Thenceforth, films of the structure shown in Fig. 1 were produced by employing Ge, Si-10 wt.% Ge, Si-2 wt.% Ti, and Ge-1 wt.% Ti as under layer materials respectively, under similar conditions. As a comparative sample, there was produced one in which a Co-22 wt.% Cr film was deposited to a thickness of 500 nm (5000 Å) at a rate of 8 nm/s (80 Å/s) directly on a polyimide film held at a substrate temperature of 150°C. Table 1 illustrates by comparison the degrees of c-axis orientation and the situations of cracking of the respective Co-Cr films. The degree of c-axis orientation was estimated by the half width of the rocking curve, Δϑ₅₀ (in degree) of an X-ray diffraction line based on the (0002) reflection on the hexogonal close-packed phase of the Co-Cr alloy. As the value of Δϑ₅₀ is smaller, the degree of c-axis orientation of Co-Cr is higher. In Table 1 and Table 2 and 3 described hereinafter, a mark o indicates a case where cracking was not noted in the Co-Cr film at all, whereas a mark x indicates a case where cracking existed even if slightly. As apparent from Table 1, in the case of providing the under layer, the value of Δϑ₅₀ was improved over that in the case of providing no under layer, and the Co-Cr film of good quality free from the appearance of cracks was obtained. Regarding magnetic characteristics, all the samples exhibited the perpendicular magnetic anisotropy and were perpendicular magnetic films. The under layers were recognized to be amorphous by X-ray diffraction. Example 2: Using a polyimide film as a substrate, films of a structure shown in Fig. 2 were produced by the following steps. While a substrate 1 made of a polyimide film was heated to 170°C in a vacuum of 4x 10⁻⁴ Pa (3x10⁻⁶ Torr), permalloy (Ni-20 wt.% Fe) being a soft magnetic material was first evaporated to a thickness of 400 nm (4000 Å) at a rate of 5 nm/s (50 Å/s) into a soft magnetic material film 4. Subsequently, in the same vacuum vessel as used for the above step, Si was evaporated as an under layer material to a thickness of 50 nm (500 Å) at a rate of 1.5 nm/s (15 Å/s), to form an under layer 2. Further, Co-25 wt.% Cr was evaporated to a thickness of 200 nm (2000 Å) at a rate of 10 nm/s (100 Å/s) into a Co-based alloy film 3. Then, the films of the structure shown in Fig. 2 were fabricated. Thenceforth, films of the structure shown in Fig. 2 were produced by employing Ge, Si-25 wt.% Ge, Si-0.5 wt.% Ti, and Ge-0.7 wt.% Zr as under layer materials respectively, under similar conditions. As a comparative sample, there were produced one in which permalloy was evaporated to a thickness of 400 nm (4000 Å) at a rate of 5 nm/s (50 Å/s) on a polyimide film held at a substrate temperature of 170°C and which had Co-25 wt.% Cr subsequently evaporated thereon to a thickness of 200 nm (2000 Å) at a rate of 10 nm/s ( 100 Å/s). Table 2 lists by comparison the characteristics of the respective Co-Cr films. The estimations of the characteristics were conducted similarly to those in Example 1. Owing to the provision of the under layers, the Co-Cr films having high degrees of c-axis orientation and exhibiting the perpendicular magnetic anisotropy could be produced. The under layers were recognized to be amorphous by X-ray diffraction. Example 3: The polyimide film in Example 2 was replaced with a polyethylene terephthalate film, and the film temperature was held at 110°C. Thus, similar samples were produced. When the Δϑ₅₀ values were measured, the value was Δϑ₅₀=14 degrees in the case of providing no under layer, whereas the values fell within a range of Δϑ₅₀=4 to 6 degrees and the Co-Cr films of good c-axis orientation were obtained in all the cases of providing the under layers. The under layers were recognized to be amorphous by X-ray diffraction. Example 4: Using Al for a substrate 1, films of the structure shown in Fig. 2 were produced by the sputtering method in accordance with the following steps. By employing a radio-frequency sputtering apparatus, Fe-6 wt.% Al-10 wt.% Si being a soft magnetic material was first deposited on the substrate 1 to a thickness of 500 nm (5000 Å) under the conditions of an Ar pressure of 0.66 Pa (5 mTorr) and a sputtering radio-frequency power of 4 W/cm². Subsequently, Si was deposited as an under layer 2 to a thickness of 60 nm (600 Å) under the conditions of an Ar pressure of 0.4 Pa (3 mTorr) and a sputtering radio-frequency power of 2 W/cm². Further, Co-18 wt.% Cr was deposited to a thickness of 350 nm (3500 Å) under an Ar pressure of 0.4 Pa (3 mTorr) and a radio-frequency power of 8 W/cm². Then, the films having the structure shown in Fig. 2 were fabricated. Thenceforth, films of the same structure were produced by employing Ge, Si-80 wt.% Ge, Si-0.3 wt.% Ti, and Ge.1 wt.% B as under layer materials respectively, under similar conditions. As a comparative material, a film structure with the under layer omitted was produced under similar conditions. In Table 3, the characteristics of the respective Co-Cr films are listed by comparison. Owing to the provision of the under layers, the Co-Cr films having high degrees of c-axis orientation and exhibiting the perpendicular magnetic anisotropy could be produced. The under layers were recognized to be amorphous by X-ray diffraction. Example 5: A perpendicular magnetic recording medium was produced in the same way as in Example 1 (a substrate temperature of 150°C was set for the deposition of the Co-Cr alloy) except that quartz glass was used for the substrate and that Si and Ge were used for the under layer with the substrate temperature set at 400°C during the deposition of the under layer. When the degree of orientation and the situation of cracking of the Co-Cr alloy film were examined, they were similar to those in Example 1. The under layer in this case was a very fine polycrystalline film (the grain size of Ge was not larger than 200 nm (2000 Å), and that of Si was not larger than 80 nm (800 Å). In the above examples, the case of the Co-Cr alloy has been described as one example of the Co-based alloy. However, even when other Co-based alloys such as Co-V, Co-Mo, Co-O, Co-Cr-Rh and Co-Cr-Ru were used, the effect of enhancing the degrees of c-axis orientation owing to the provision of the under layers was noted. Also in a case where different materials such as Fe-Si and Co-Nb-Zr alloys were employed for the soft magnetic material layers, equal effects were noted. In the perpendicular magnetic recording medium of the present invention, matters not mentioned in this specification may be resorted to the knowledge of prior arts in the technical field concerned. As apparent from the description thus far made, when an under layer which is made of Si, Ge or an alloy thereof or an alloy with one or more elements further added to such principal ingredient is provided before the deposition of a Co-based alloy film, a perpendicular magnetic film formed of the Co alloy film of good C-axis orientation can be produced with good reproducibility irrespective of a substrate or an underlying soft magnetic material. Further, in a case where the substrate is of a non-metallic material, the bond strength between the substrate and the Co alloy film is enhanced.

Claims: A perpendicular magnetic recording medium comprising a substrate (1), an under layer (2) which is deposited on said substrate, and a perpendicular magnetic film (3) which is made of a Co-based alloy and which is deposited on said under layer, characterised in that the under layer (2) is made of a material containing as its principal ingredient at least one element selected from the group consisting of Si and Ge, and has amorphous structure or polycrystalline structure and that the under layer has a thickness of at least 10 nm. A perpendicular magnetic recording medium according to claim 1, characterized in that the thickness of said under layer is at most 1 µm. A perpendicular magnetic recording medium according to Claim 2, characterized in that a thickness of said under layer (2) is at least 15 nm (150 Å) and at most 100 nm (1000 Å). A perpendicular magnetic recording medium according to Claim 1, 2 or 3, characterized in that said under layer (2) is made of a material in which at least one element other than Si and Ge is added in such a range of amount that any structure other than a diamond structure and an amorphous structure does not appear in a crystal structure of said under layer (2). A perpendicular magnetic recording medium according to Claim 1, 2 or 3, characterized in that at least that surface of said substrate on which said under layer is formed is made of a soft magnetic material.

Inventors: FUTAMOTO, MASAAKI, HONDA, YUKIO, UESAKA, YASUTARO, YOSHIDA, KAZUETSU
Applicants: HITACHI MAXELL LTD., HITACHI, LTD.
Application year: 1985
Main classification: G11B5
IPC codes: G11B5