Sanitary absorbent structure

Abstract: An absorbent structure is disclosed having opposed longitudinal ends and including a body-facing liquid permeable liner (2), an outer liquid impermeable cover (3), and liquid absorbing materials (4) therebetween. The liquid absorbing material (4) includes a body of cellulosic fibres and superabsorbent material (9). In order to improve absorbing properties, the superabsorbent material (9) is localized in an area (17) slightly above a region midway between the target area (7) and an upper end of the structure, while the body (4) of cellulosic fibres is effective in use to draw some of the liquid accumulating on the target area (7) from the target area (7) to the superabsorbent material so that the superabsorbent material provides an additional reservoir for liquid absorbed without the necessity of superabsorbent material to be spread over the entire extent of the structure.

Description: This invention relates to a diaper as outlined in the preamble of claim 1. A diaper of this type is disclosed in US-A-4 381 783. The known diaper includes an absorbent body which contains superabsorbent material. The superabsorbent material is contained in a plurality of pockets which either are arranged separately from each other but concentrated in the target area, or which are connected to each other in order to form a sheet covering the complete surface of the absorbent body. GB-A-2 087 240 describes an absorbent diaper having a body of cellulosic fibres which is provided with two reservoirs. The first reservoir is formed by compression of the cellulosic fibrous batt, and is arranged in the target area in the front half of the diaper. The second reservior contains superabsorbent material, and is of substantially the same size as the first reservoir. The second reservoir is located below the first reservoir, i.e. also in the target area in the front half. The absorbent diaper is therefore designed to store the body fluids within the target area. It is an object of the present invention to provide a low cost diaper having improved absorbing properties. A diaper fulfilling this need contains the characterising features of claim 1. When locating the superabsorbent material in accordance with the present invention, it could be found that a maximum absorbent capacity could be achieved by minimum amount of superabsorbent material. The diaper of the present invention is effective to draw some of the excess liquid away from the target area and to store it at a location which is safe to leakage. Further developments of the diaper of the present invention are disclosed in the sub claims. Embodiments of the present invention are hereinafter described by reference to the figures, wherein: FIG. 1 is a perspective plan view of an embodiment of the present invention, including a portion of superabsorbent material incorporated therein. FIG. 2 is a longitudinal cross-sectional view taken along line 7-7 of FIG. 1. FIG. 3 is a perspective plan view of a further embodiment of the present invention including a portion of superabsorbent material incorporated therein. FIG. 4 is a longitudinal cross-sectional view taken along line 9-9 of FIG. 3. FIG. 5 is an absorbency profile for the control diaper tested in Example 1. FIG. 6 is an absorbency profile for the diaper containing one ply of compressed fluff in addition to the regular fluff component as discussed in Example 1. FIG. 7 is an absorbency profile for the diaper containing two plies of compressed fluff in addition to the regular fluff component as discussed in Example 1. FIG. 8 is the absorbency profile for the diaper containing three plies of compressed fluff in addition to the regular fluff component as described in Example 1. FIG. 9 is the absorbency profile for the diaper containing two plies of compressed fluff plus a portion of superabsorbent material as described in Example 1. Turning now to the drawings, the disposable diaper 1 in which the present invention is embodied comprises generally a body facing, liquid permeable liner 2, an outer liquid impermeable cover 3, and a liquid absorbing material indicated generally as 4 therebetween. The liquid absorbing material 4 preferably comprises a first, lower density layer 5 of cellulosic fibers such as comminuted wood pulp (fluff) which lies beneath the inner liner 2. A second, higher density layer 6 of fluff lies beneath at least a portion of the first lower density layer 5 such that waste fluid can be transferred from the lower density layer 5 to the higher density layer 6. Thus, a lower surface of the lower density layer 5 should be contiguous with at least a portion of an upper surface of the higher density layer 6. However, a tissue layer can be placed between the layers 5 and 6 without departing from the scope of this invention. Predominantly softwood pulp fluff can be used for each of the layers 5 and 6. Alternatively, a layer of predominantly softwood fluff can be used for the layer 5 and a layer of preponderantly hardwood fluff can be used for the layer 6, in which case it is the average pore size and not necessarily the density that varies between the layers 5 and 6, as will shortly be explained. For the purposes of this disclosure and the accompanying claims, "predominantly" is intended to mean at least about 80% while "preponderantly" is intended to mean at least about 50%. The higher density layer 6 is formed as a strip extending from a target area 7, where liquid waste will initially accumulate, to an upper edge 8 towards the back of the diaper. The higher density layer 6 draws waste fluid from the lower density layer 5 in the target area 7 upwardly towards the edge 8 at the back of the diaper 1. Further, along upper regions of the higher density layer 6 towards the upper edge 8 there is, surprisingly, substantial fluid transfer back from the higher density layer 6 to the lower density layer 5. It is important to note that although this flowback occurs from the higher density layer 6 to the lower density layer 5, the lower density layer 5 only draws sufficient fluid to satisfy its unsaturated capillary forces proximate to the higher density layer 6, where there is an overlap in pore sizes such that the smallest pores in the lower density layer 5 are smaller than the largest pores in the higher density layer 6. The lower density layer 5 drains fluid from the higher density layer 6 but does not become soaked, with the advantage that the wearer's comfort is maintained while a significant proportion of the absorption capacity of the lower density layer 5 is utilized. A portion of superabsorbent material (SAM) 9 is included as part of the liquid absorbing material 4. The term "superabsorbent material" as used herein refers to one or more hydrocolloid materials capable of absorbing many times its own weight of water or aqueous fluid. These materials are generally prepared by polymerizing one or more monomers which, if homopolymerized by conventional methods, would form water soluble polymers. To render them water-insoluble and suitable for the present invention, these polymers or mixture of polymers are typically reacted, frequently with a crosslinking agent, to form crosslinked polymers, thereby introducing a limited water-insolubility while retaining susceptibility to swelling in water and water-containing fluids. Pseudocrosslinking may also be achieved by chain entanglement of high-molecular weight polymers, thus effecting water insolubility (see, e.g., US-A-4,340,706). Typically, these hydrocolloids are salts of polyacrylic acid and variations thereof, such as methacrylic acid. Commercially they are available under the trademarks WATER LOCK J-500; ABASORB 720; and Aqualic-CA. Alternative superabsorbents also may include hydrophilic polymer grafts onto starch or cellulose backbones and crosslinked carboxylated celluloses. In FIGS. 1 and 2 an embodiment of the absorbent structure is shown wherein the superabsorbent material 9 is sandwiched between a first higher density component 10 and a second higher density component 11 of the higher density layer 6, and is localized in an area 17 slightly above a region midway between the target area 7 and the upper edge 8. Thus, the superabsorbent material 9 provides an additional reservoir for liquid waste that has been draws up the diaper by the higher density layer 6. An important advantage of this arrangement is that it assists in fluid distribution along the length of the superabsorbent material. Generally, superabsorbents 9 disposed in a fiber matrix enhance fluid distribution in the direction corresponding to the thickness of the liquid absorbing material 4. However, due to the swelling nature of the superabsorbent material 9, wicking in the plane of the fiber matrix bearing the superabsorbent 9 is severely hindered. A wicking across the entire length of the superabsorbent material 9 is accomplished by sandwiching the superabsorbent material 9 between the first high density component 10 and the second high density component 11. Thus, the liquid waste is brought into contact across an upper surface 12 and a lower surface 13 of the superabsorbent material 9 rather than across a bottom edge 14 thereof. This is an improvement over border-to-border transfer of liquid waste. FIGS. 3 and 4 show an alternative embodiment wherein the superabsorbent material 9 is disposed adjacent the outer, liquid impermeable cover 3, and then covered with the single higher density layer 6 which is in turn covered with the lower density layer 5. Of course, still further alternative embodiments are provided by using a softwood fluff pulp in the layer 5 and a hardwood fluff pulp in the layers 6 (FIGS. 3 and 4), or 10 and 11 (FIGS. 1 and 2), with uniform densification of all layers to about 0.1g/cm³, or in the range of about 0.1g/cm³ to about 0.15 g/cm³. Yet further variations within the scope of this invention include using a softwood fluff pulp of a first density in combination with a hard wood fluff pulp of a second density, wherein the second density is preferably higher than the first density. The term "density" as used herein refers to the density of the composite structure of the lower density layer 5 or the higher density layer 6, and not the actual fiber density. (The actual fiber density is about 1.5 g/cm³.) The density of the lower density layer 5 should be in the range of about 0.03 to about 0.14 g/cm³, with the preferred range, in light of considerations of integrity and bulk, at about 0.07 to about 0.11 g/cm³. The higher density layer 6 should have a density in the range of about 0.14 to about 0.3 g/cm³, and preferably in the range of about 0.16 to about 0.22 g/cm³ for providing the desired capillarity without excessive stiffness. The density for these preferred ranges is a density measured under a load of 0,00014 kg/mm² (0.2 psi). An important consideration in selecting suitable ranges for the higher density fluff and lower density fluff is that although there should be two distinct pore size distributions, one for each of the respective layers of fluff, these pore size distributions should overlap because this will permit flowback from the high density layer back to the low density layer. The densified layer 6 may be a multiple ply layer rather than merely a single ply layer, and the ply may increase in density across the width or length of the layer 6 within the specified range or can be of uniform density. The basis weight of the lower density layer 5 should be in the range of about 150 to about 500 g/m² to provide the desired aesthetic appearance and comfort of the diaper. The basis weight of the higher density layer 6 should be in the range of about 150 to 1250 g/m². It is preferred that the higher density layer 6 be substantially separately rather than integrally formed with the lower density layer 5, to achieve better moisture distribution therethrough. It should be noted, however, that the layers 5 and 6 are "substantially separately" formed even when formed in the same machine, one on top of the other, with some admixing at the interface. By the "substantial separate" terminology, it is intended only that two substantially discrete layers are formed, rather than a substantially single layer having a "skinned" surface, such as described in US-A-2,952,260, 2,955,641, 3,017,304, 3,060,936, and 3,494,362 to Burgeni. Thus, densification should be achieved uniformly through the higher density layer 6, and care should be taken to avoid substantial skinning, where such skinning is as described in the Burgeni patents or in the Aberson US-A-4,103,062. Skinning produces undue stiffness in the fluff and results in low absorbent capacity in the bonded (skinned) layer. Skinning can be prevented by avoiding excess moisture and by maintaining both platens at approximately the same temperature to avoid condensation through the thickness of the material. The present invention avoids the densification of the fluff to the point of forming a skin layer so that the densified fluff layer 6 retains at least about 80% void volume, resulting in significant absorbent capacity. The layer 6 is densified in a heated press which includes heated platen operated under suitable conditions of temperature and pressure as known in the art to achieve the desired density. Alternatively, a heated calender nip is suitable for use in the densification process, as known in the art. Comminuted wood pulp (fluff) is preferred for this invention, but other cellulose fibers such as cotton linters can be used. The preferred fluff is southern pine kraft wood pulp (i.e., made according to the sulfate process commonly known in the art) which has been bleached. A suitable hardwood fluff pulp is southern hardwood kraft. The preferred embodiments described herein can be modified by using, for example, the densified fluff layer 6 with other absorbents such as coformed (meltblown polymer fibers combined with wood pulp and/or staple fibers) webs, carded webs, air-formed (staple wood pulp blends) webs and the like, at a lower density. Further, the absorbent structures described herein have applications to embodiments other than diapers, such as to sanitary napkins or other hygienic media. The advantages resulting from this invention will be clearly understood with respect to the following examples and test data. EXAMPLE I The high density fluff was prepared by running the fluff into a hot calender nip (steel on hard rubber) at 121,1°C (250°F) at a speed of 3,05 m/min (10 ft/min). The nip pressure was sufficient to give a measured density on standing overnight of 0.15 g/cm³. Alternatively the fluff could have been pressed in a blotter lined platen press heated to about 121°C (250°F) for about 5 seconds, with sufficient pressure to achieve the desired fluff density. The lower density fluff was prepared by passing it through a calender nip at 121°C (250°F) at a speed of 305 m/min (10ft/min) and sufficient pressure to achieve a measured density on standing overnight of 0.1 g/cm³. In both cases the fluff was prepared from southern pine bleached kraft wood pulp, and was cut to dimensions such that the weight conditions set forth in Table I below were met. The combined low density fluff and high density fluff weight are given in the first column of Table I. The total absorbent weight was maintained at about 37 grams for each diaper, except for the one containing superabsorbent. The diaper with superabsorbent located as shown in FIG. 3 contained an additional 7 grams of superabsorbent composite consisting of about 3 grams of particulate superabsorbent (Water Lock™ A-100); about 3 grams of polyolefin; and about 1 gram of porous nonwoven wrap. The composite was made in accordance with the teaching of Mazurak and Fries, as set forth in US-A-4,381,782. The diaper construction was completed by sandwiching the absorbent composite between a porous spunbonded polypropylene liner of 27,5 g/m² (23 g/yd²) and a polyethylene film outer cover, sealed together with adhesive at the diaper perimeter. Five types of diapers were constructed in this fashion, corresponding to the diaper description of Table I. Each of the diapers was then subjected to a 15 minute vertical wicking test with synthetic urine, followed by 15 minutes of equilibration out of contact with the urine bath. The results of this testing are shown in Table I and FIGS. 5 - 9. In this test the preweighed diapers were mounted on a lucite plate of 9,5 x 330,2 x 355,6 mm (3/8" x 13" x 14") with the impervious poly backing adjacent the plate surface. The diaper was symmetrically wrapped around the edge of the plate with the longitudinal dimension of the diaper parallel to the long dimension of the plate. The waist line edges of the diaper were mounted on the plate with masking tape, the elastic leg bands being cut in 2 or 3 places to facilitate the mounting. The plate was suspended vertically over a fluid bath contained in a glass tray with the longitudinal dimension of the diaper perpendicular to the fluid surface. The fluid was then brought into contact with the lower edge of the diaper so that the diaper edge was slightly immersed, and was maintained in this position for 15 minutes. The diaper was then removed from fluid contact and allowed to hang in the same vertical orientation for 15 minutes equilibration. The fluid used for the diapers in Table I was a synthetic urine composed of by weight 1% urea, .01% Pluronic 10R8 surfactant to bring the surface tension to about 56 dynes/cm, and .04% sodium azide preservative. After equiliberation the diapers were removed from the plate and weighed and the fluid pick up noted. The results are summarized in Table I and represent the average of seven measurements on each diaper design. After weighing, the diapers were laid horizontally on a 76,2 x 381 mm (3" x 15") cutting die which was segmented into nine 43,18 mm (1.7-inch) zones with cutting edges across the die width as well as the outer perimeter. Several quick blows with a wooden mallet divided the 76,2 mm (3-inch) wide absorbent strip along the longitudinal axis of the diaper into 9 segments. The absorbent component in each segment was weighed, oven dried and reweighed and the fluid pick up determined on a gram per gram or fiber basis (corrected for deposited solids from the fluid). In the case of the diaper with the superabsorbent pouch, the synthetic urine composition was adjusted to more closely simulate the electrolyte composition of baby urine, namely: 0.31 g. CaH₄(PO₄)₂ H₂O, 0.68 g. K H₂PO₄, 0.48 g. MgSO₄ 7H₂O, 1.33 g. K₂S0₄, 1.24 g. Na₃PO₄ 12H₂O, 4.4 g. NaCl, 3.16 g.KCl, 0.4 g. NaN₃, 8.56 urea and 0.1 g. Pluronic 10R8 per liter, using distilled water as the solvent. The components were added to 900 mls of distilled water in the order given and each dissolved before the next component was added, and finally diluted to 1 liter. The dotted curve in FIG. 5 represents the equilibrium capacity for the low density fluff at the indicated hydrostatic tensions as measured in a capillary tension cell. It is apparent that only at short wicking distances (4.5 cm) does the fluff reach its ultimate capacity. At the greater wicking heights (9-18 cms) it is well below its capacity. Figures 6-8 demonstrate the ability of the densified fluff layer to pull the fluid up against the hydrostatic heads indicated. Comparison of the fluid level in the low density fluff in the back of the diaper with that in the same material in front at the corresponding head is a measure of the effectiveness of the high density fluff to improve the utilization of the low density material (e.g. 2.8 g/g back vs. 0.1 g/g front at 18 cms head, FIG. 8). FIG. 9 shows the effectiveness of the densified layers in carrying and transferring fluid to the superabsorbent. The levels of fluid pickup in the superabsorbents are 12 and 22 g/g respectively at the 9 and 13.5 cm heads. Comparing this to figure 7 illustrates the effectiveness of the superabsorbent in diverting fluid from the fluff components at the highest heads. It is apparent from these results that fluid distribution is greatly enhanced up the back of the diaper in the designs with densified fluff layers. The contrast with the fluid distribution in the front of the diaper, where densified fluff layer is absent, is very evident from the figures. In the instance of the superabsorbent diaper, which was made in accordance with Fig. 1 and 2, the superabsorbent material drained substantial fluid from the higher regions of the diaper. However, these regions toward the upper edge 8 of the diaper provide surplus absorbing capacity if needed. Whole Diaper Vertical Wicking Test Diaper Description Absorbent Weight g. Weight of Comp. Fluff g. Amt. of Fluid Absorbed g. Fluid Absorbed Over Control % Control Diaper 36 0 140 -- Diaper containing 1 ply of compressed fluff 38 7 171 22 Diaper with 2 plies of compressed fluff 37 14 191 37 Diaper with 3 plies of compressed fluff 35 21 203 45 Diaper with 2 plies of compressed fluff & SAM 43 14 215 54 EXAMPLE II The present inventor has discovered that similar functionality to the higher density fluff can be achieved with finer fiber, hardwood pulp fluff but at normal density (0.1 g/cm³). This discovery was made following the observation of a remarkable similarity in the pore volume distribution of 0.1 g/cm³ density hardwood fluff and that of 0.2 g/cm³ softwood fluff. The following tables compare the vertical wicking properties of softwood and hardwood fluff. The vertical wicking test was somewhat similar to that conducted with whole diapers described above. This test was conducted on 76,2 x 381 mm (3" x 15") strips of the absorbent material mounted on a 9,5 x 127 x 355,6 mm (3/8" x 5" x 14") lucite plate in the same orientation and manner described for the diapers. A nylon mesh screen was used to support the fluff strip on the lucite (acrylic) plate. The plate and strip were then suspended from weight-sensing means such as a load cell in an Instron tensile tester. The synthetic urine (in these cases the second or salt-containing formulation) was then put in contact with the lower edge of the absorbent strip and the amount of fluid absorbed as a function of time is recorded at several time intervals for the 15 minute duration of the test. The amount absorbed was calculated as the grams per unit basis weight of 1 g/cm² per unit width of 25,4 mm (1 inch). The vertical wicking capacity is defined as the amount absorbed in the defined units at the end of the 15 minute test. The reported rate was that measured from the plot of amount absorbed/unit basis weight/unit width versus time ½ over the time interval of 7-21 seconds. The test was replicated six times and the results reported are averages of these six measurements. Fluid distribution in this test was measured by die cutting the sample immediately following the completion of the test, the same manner described for the whole diapers. In this case zones corresponding to the same vertical heights were combined to give the results shown in Table III. As may be concluded from the results in Table II, the vertical wicking capacity of 0.1 g/cm³ density hardwood fluff corresponds closely with that of 0.2 g/cm³ density softwood fluff. The initial wicking rate of the hardwood fluff falls between the two softwood fluffs. The fluid distribution pattern in Table III also shows the similarity of the hardwood fluff and the 0.2 g/cm³ density softwood fluff. These results imply a slightly larger average pore size for the former than the latter. Hence, a combination of softwood and hardwood fluff at 0.1 g/cm³ density should have similar fluid distribution properties to a two-density sandwich of softwood fluff, as previously described in this disclosure. VERTICAL WICKING CAPACITY/RATE (Showing similarity in capillarity of softwood kraft at 0.2 g/cm³ and hardwood kraft at 0.1 g/cm³ density) Material Density (g/cm³) Vertical Capacity G/UBW/UW Wicking Rate G/UBW/UW/SEC ½ Softwood Kraft Fluff 0.1 499 48 Softwood Kraft Fluff 0.2 573 36 Hardwood Kraft Fluff 0.1 580 42 FLUID DISTRIBUTION IN VERTICAL WICKING Specific Absorbency (g/g) at Following Tensions 0 cm 4.5 cm 9 cm 13.5 cm 18 cm Softwood Kraft (0.1 g/cm³) 9.0 9.0 6.4 3.0 0.7 Softwood Kraft (0.2 g/cm³) 6.0 6.1 5.8 5.0 4.7 Hardwood Kraft (0.1 g/cm³) 8.2 8.1 7.2 5.3 3.3 EXAMPLE III This example is directed to a double fluff layer of softwood fluff over hardwood fluff. The hardwood fluff was a bleached kraft, South American Eucalyptus hardwood pulp. The two-ply fluff contained equal weights of the softwood and hardwood pulp layers. After densifying the layers to 0.1 g/cm³ density, the vertical wicking properties (same test procedure as for example II) were as follows: VERTICAL WICKING PROPERTIES OF SOFTWOOD/HARDWOOD LAYERED BATT Vertical Capacity ***Wicking Rate ***Specific Absorbency At Following Tensions 0 cm 4.5 cm 9 cm 13.5 cm 18 cm 544 46 7.8 7.8 6.1 4.3 3.0 Comparing the distribution results for the double-layered fluff in Table IV with those for softwood kraft (Table III), it is apparent that the presence of the Eucalyptus layer greatly improves fluid wicking against the upper two hydrostatic heads (i.e. in the 13.5 cm and 18 cm zones). This is particularly impressive since the Eucalyptus only represents 50% of the two-ply structure. EXAMPLE IV A 40 g/m² web of meltblown polypropylene containing 40 percent by weight of superabsorbent (Waterlock J-500) was prepared. The superabsorbent was intermixed with the fine meltblown fibers (surface area about 1 m²/g) containing enough surfactant (e.g., about 0.3 - 0.5 percent Triton X-102 to assure wetting of the fiber matrix, the composite being densified to 0.1 g/cm³ during the manufacturing process. When this web was subjected to the vertical wicking procedure described in Example II, the results presented in Table 5 were obtained. From these results it is apparent that the fluid wicks vertically 4.5 cms but then essentially stops, presumably because the swelling particles have restricted the fluid flow in the web by plugging the pores. When this same web was placed beneath a softwood fluff layer, having a density of 0.2 g/cm³, in a diaper construction, and the whole diaper was subjected to the vertical wicking test (described in Example I), the effect of the fluff layer as a fluid distributor for the superabsorbent was apparent. In Table 6, the fluid distribution is shown for the total absorbent composite, the fluff layer itself, and for the meltblown/superabsorbent web. Comparing the vertical distribution for the meltblown/superabsorbent web from the diaper (Table 6) with the data in Table 5, it is apparent that the densified fluff acts to wick the fluid higher and improves the distribution to the superabsorbent (compare at 9 cm height, 11.6 g/g vs. 1.1 g/g; and at 13.5 cm height, 2.7 g/g vs. 0.1 g/g). Note that both tests were similarly run for 15 minutes. Furthermore, if the tests were allowed to proceed further, the height wicked in the diaper would continue to increase, whereas wicking in the superabsorbent web alone would virtually stop. VERTICAL WICKING TEST ON DIAPER CONTAINING MELTBLOWN/SUPERABSORBENT WEB Diaper Absorbent Dry Absorbent Weight (g.) Absorbent Component Specific Absorbency at Following Tensions 0.0 cm 4.5 cm 9.0 cm 13.5 cm 18.0 cm Fluff densified to 0.2 g/cm³ over coextensive layer of Meltblown Web with 40% Superabsorbent (basis weight 139 g/m²) 42.7 Fluff 7.5 7.2 4.5 2.5 1.5 MB/SAM 18.8 19.7 11.6 2.7 1.0 Combined Absorbent 9.9 10.1 6.4 2.6 1.5

Claims: A diaper having a front and a back end (8) opposed in longitudinal direction, and a transverse axis defining a front half and a back half of said diaper, said back end (8) being provided with attachment tapes, said diaper including a body-facing liquid permeable liner (2), an outer liquid impermeable cover (3), and liquid absorbing material (4) therebetween, the liquid absorbing material (4) including a body of cellulosic fibres wherein the diaper further comprises superabsorbent material (9), being mounted in liquid transfer contact with said body (4) of cellulosic fibres, and the body (4) of cellulosic fibres being effective in use to draw some of the liquid accumulating on a target area (7) within said front half from said target area (7) to said superabsorbent material (9) so that the superabsorbent material (9) provides an additional reservoir for liquid absorbed, characterized in that said superabsorbent material (9) is localized within said back half in an area (17) slightly above a region midway between the target area (7) and said back end (8) of the diaper. A diaper as claimed in claim 1 wherein said body (4) of cellulosic fibres has a substantially uniform density. A diaper as claimed in claim 1 wherein said body (4) of cellulosic fibres comprises a first layer (5) of fibres having a first density located adjacent the permeable lining (2), and a second layer (6, 10, 11) of fibres having a second density and being located between the first layer (5) and the impermeable cover (3), said second density being greater than the first density. A diaper as claimed in claim 3 wherein the first density is between 0.03 g/cm³ and 0.14 g/cm³. A diaper as claimed in claim 4 wherein the first density is between 0.07 and 0.11 g/cm³. A diaper as claimed in any of claims 3 to 5 wherein the second density is between 0.14 and 0.3 g/cm³. A diaper as claimed in claim 6 wherein the second density is between 0.16 and 0.22 g/cm³. A diaper as claimed in any one of claims 1 to 7 wherein said body of cellulosic fibres comprises softwood fluff. A diaper as claimed in any one of claims 1 to 8 wherein said body (4) comprises preponderantly softwood fluff. A diaper as claimed in any one of claims 1 to 7 wherein said body comprises predominantly softwood fluff. A diaper as claimed in any one of claims 1 to 10 wherein said superabsorbent material (9) is interspersed in a web of fibres. A diaper as claimed in claim 11 wherein said web comprises wettable fibres. A diaper as claimed in claim 11 wherein said web is in the form of a pouch. A diaper as claimed in claim 12 or 13 wherein said web comprises meltblown fibres mixed with said superabsorbent material. A diaper as claimed in any of claims 11 to 14 comprising a layer (5) of cellulosic fibres, located between said superabsorbent material (9) and said impermeable cover. A diaper as claimed in claim 1 wherein said body (4) of cellulosic fibres has a substantially uniform density of substantially 0.2 g/cm³.

Inventors: BERNARDIN LEO J, BERNARDIN, LEO J.
Applicants: KIMBERLY CLARK CO, KIMBERLY-CLARK CORPORATION
Application year: 1985
Main classification: A61F13
IPC codes: A61F13