Intermediate for composite materials

Abstract: An intermediate for a composite material is disclosed. The intermediate is obtained by impregnating an epoxy resin composition containing a specific additive into a rein­ forcing material. The composite material obtained from the intermediate has improved mechanical properties.

Description: FIELD OF THE INVENTION This invention relates to an intermediate for a composite material having excellent mechanical properties. BACKGROUND OF THE INVENTION Various resin compositions have conventionally been used as matrices for composite materials. In the particular field of thermosetting resins, epoxy resins have widely been employed as matrix resins because of their excellent mechanical properties, such as strength, elongation, heat resistance, etc., satisfactory adhesiveness to reinforcing materials and superiority in manifestation of strength of reinforcing materials. However, the degree of manifestation of strength by reinforcing materials is still unsatisfactory particularly in terms of compression characteristics and, therefore, improvement in this respect has been demanded. An attempt to this effect was directed to an increase in rigidity of resins per se , but such an increase in rigidity is accompanied with an unfavorable increase in heat resistance, i.e., an excessive performance than required, resulting in significant reduction in elongation. Such resins cannot be used in some applications. For example, it was proposed in The British Polymer Journal , 15 , 66 (March, 1983) that a reaction product between an epoxy compound (e.g., and an amide compound (e.g., is added to a system comprising an epoxy resin and a hardener to thereby improve the physical properties of resins, but no consideration is given therein to the compression characteristics of the resins when they are formed into composite materials. In connection to the above proposal, there have also been proposed a reaction product between an epoxy compound and an amine compound in EP-A-103392 and a reaction product between an epoxy compound and an amide compound in EP-A-103968. Epoxy Resins, Chemistry and Technology, Marcel Dekker, Inc New York 1973, gives a review of curing agents and modifiers for epoxy resins. SUMMARY OF THE INVENTION In the light of these circumstances, the present inventors have conducted extensive studies on intermediate for composite materials which can provide various improved mechanical properties, particularly compression characteristics. As a result, they discovered an additive which can remarkably improve the rigidity of resins without impairing their elongation and confirmed that various composite materials containing, as a matrix, an epoxy resin composition comprising an epoxy resin, a hardener, a hardening accelerator and the above-described additive have pronouncedly improved mechanical properties. Subject matter of the present invention is therefore an intermediate for a composite material comprising a carbon fiber impregnated with an epoxy resin composition containing (A) epoxy resin and at least one preliminary condensate which is obtained by subjecting at least one polyamine or acidic substance having a polycarboxylic group, a polycarboxylic acid anhydride group or a mixed group thereof and an epoxy resin having at least one epoxy group at a chemical equivalent ratio of from 1:1 to 1:6 to heat treatment at a temperature of from 50 to 200°C to increase the viscosity of the mixture at least 3-times without inducing gelation, (B) either dicyandiamide and a hardening accelerator represented by the formula (II) wherein Y and Z, which may be the same or different, each represents a hydrogen atom, a chlorine atom, a bromine atom, a nitro group, a methyl group, a methoxy group or an ethoxy group, or the hardening accelerator represented by the formula (II) only, and (C) at least one of compound represented by the formula (I), wherein R₁ represents a hydrogen atom, an unsubstituted saturated aliphatic group having 1 to 17 carbon atoms, a substituted or unsubstituted, saturated alicyclic group having 5 to 17 carbon atoms, a substituted or unsubstituted aromatic group having 6 to 17 carbon atoms, or a substituted or unsubstituted, saturated or unsaturated 5- or 6-membered heterocyclic group containing N, O or S as hetero atom; R₂ has the same meaning as defined for R₁ or is a group of formula wherein R₅ and R₆, which may be the same or different, each represents a hydrogen atom or a substituted or unsubstituted, saturated aliphatic group having 1 to 17 carbon atoms (e.g., a methyl group, an ethyl group, an ethylhexyl group), a substituted or unsubstituted, saturated alicyclic group having 5 to 17 carbom atoms (e.g., a cyclopentyl group, a cyclohexyl group, a 2-ethylcyclohexyl group), a substituted or unsubstituted aromatic group having 6 to 17 carbon atoms (e.g., a phenyl group, a tolyl group), or a substituted or unsubstituted, saturated 5- or 6-membered heterocyclic group containing N, O or S as hetero atoms (e.g., R₃ and R₄, which may be the same or different, each has the same meaning as defined for R₅ and R₆, or a group of formula R-OCH₂ - wherein R has the same meaning as defined for R₅ and R₆ (e.g. n-butyl-OCH₂-); and X represents an oxygen atom, a sulfur atom or N-R₇ wherein R₇ has the smae meaning as defined for R₅ and R₆, and wherein the compound or compounds represented by formula (I) is or are present in an amount of from 2 to 150 parts by weight per 100 parts by weight of the total amounts of the epoxy resin composition, the polyamine and/or acidic substance having a polycarboxylic group, a polycarboxylic acid anhydride group and/or a mixed group thereof and the dicyandiamide are all together present in an amount of from 40 to 90% of the chemical equivalent amounts based on the total epoxy functional group, and the hardening accelerator is present in an amount of from 1 to 15 parts by weight per 100 parts by weight of the total amount of the epoxy resin and the additives. Preferred embodiments thereof are subject matter of claims 2 to 11. The substituted aliphatic, alicyclic, aromatic and heterocyclic groups may contain as a substituent a halogen atom (e.g., chlorine, bromine), an alkoxy group having 1 to 3 carbon atoms (e.g, a glycidyloxy group, a methoxy group, an ethoxy group), an aryloxy group having 6 to 17 carbon atoms (e.g., a phenoxy group), an acyl group having 2 to 7 carbon atoms (e.g., an acetyl group, a benzoyl group); DETAILED DESCRIPTION OF THE INVENTION Among the compounds represented by formula (I), those having a bulky and highly rigid substituent, such as an aromatic group, a heterocyclic group and an alicyclic group, in the molecule thereof are particularly effective. Specific examples of the compounds which can preferably be used in the present invention are shown below: Of these, more preferred are the following compounds. The compounds represented by the formula (I) can be obtained, for example, through reactions between epoxy compounds and the corresponding amine compounds, amide compounds and urea compounds, respectively, as shown in the following reaction schemes: wherein R₁ to R₄ and X are as defined above. The epoxy compounds represented by the formula (IV) which can be used in the preparation of the compounds of the present invention include low molecular epoxy compounds, such as phenylglycidyl ether, ethylene oxide, dimethylpentane dioxide, diglycidyl ether, butanediol diglycidyl ether, ethylene glycol diglycidyl ether, vinylcyclohexane dioxide, limonene dioxide, bis(2,3-epoxycyclopentene) ether, divinylbenzene dioxide, resorcin diglycidyl ether, 2-glycidyl phenylglycidyl ether, 3,4-epoxy-6-methylcyclohexylmethyl-3,4-epoxymethylcyclohexenecarboxylate, butylglycidyl ether, styrene oxide, p-butylphenol glycidyl ether, cresylglycidyl ether, glycidyl methacrylate, allylglycidyl ether, cyclohexanevinyl monoxide, dipentene monoxide, α-pinene oxide, 3(pentadecyl) phenylglycidyl ether. The compounds represented by the formula (III) which can be used in the above-described reaction (A) include aliphatic amines, e.g., methylamine, ethylamine, n-propylamine, n-butylamine, isopropylamine, , di-2-ethylhexylamine, diisobutylamine, secbutylamine, 2-ethylhexylamine; alicyclic amines, e.g., cyclohexylamine, dicyclohexylamine; aromatic amines, e.g., aniline, p-aminobenzoic acid, 3,4-xylidine, m-xylylenediamine, diaminodiphenyl ether, dibenzylamine, benzylamine; acetaldehyde ammonium; heterocyclic amines, e.g., 4-aminopyridine, N-aminopropylmorpholine, bisaminopropylpiperazine, etc., heterocyclic compounds, e.g., piperazine, 2-pipecoline, piperidine, pyrrolidine, 5-fluorouracil, N-methylpiperazine; and amino acids, e.g., β-alanine, glycylglycine, glutamic acid, γ-aminobutyric acid, γ-aminocaproic acid, glycine; 4-hydroxyphenylamide, 4-hydroxyphenylacetamide, phenylacetoacetamide, or corresponding monothio- or dithiocarboxylic acids thereof; acetoguanamine; 3-amino-1, 2,4-triazole; isocyanuric acid; imidazoles, e.g., 2-methylimidazole, 2-ethyl-4-methylimidazole, 2-phenylimidazole, 2-undecylimidazole, 2-heptadecylimidazole, 2,4-diamino-6-[2'-methylimidazolyl-(1)']-ethyl-s-triazine, 2,4-diamino-6-[2'-ethyl-4'-methylimidazolyl-(1)']-ethyl-s-triazine, 2-phenyl-4-methyl-5-hydroxymethylimidazole, 2-phenyl-4, 5-dihydroxymethylimidazole, a 2-methylimidazole-isocyanuric acid adduct, a 2-phenylimidazole-isocyanuric acid adduct; 5,5-dimethylhydantoin; benzoguanamine; 1-methylol-5, 5-dimethylhydantoin, melamine; 1,3-diphenylguanidine; di-o-tolylguanidine; 1-o-tolylbiguanide; single or mixed asymmetrical urea or thiourea and compounds derived from ammonia; aliphatic amines, e.g., methylamine, ethylamine, n-propylamine, n-butylamine, isopropylamine, 2-ethylhexyloxypropylamine, 3-ethoxypropylamine, di-2-ethylhexylamine, dibutylaminopropylamine, diisobutylamine, 3-methoxypropylamine, allylamine, sec-butylamine, isopropanolamine, 2-ethylhexylamine, ethylenediamine, hexamethylenediamine; alicyclic amines, e.g., cyclohexylamine, dicyclohexylamine; aromatic amines, e.g., aniline, p-aminobenzoic acid, 3,4-xylidine, dibenzylamine, benzylamine; acetaldehyde ammonium; heterocyclic amines, e.g., 4-aminopyridine, N-aminopropylmorpholine, 1-amino-1-methylpiperazine, bisaminopropylpiperazine; heterocyclic compounds, e.g., piperazine, 2-pipecoline, piperidine, pyrrolidine, 5-fluorouracil, morpholine, N-methylpiperazine; and amino acids, e.g., β-alanine, glycylglycine, glutamic acid, γ-aminobutyric acid, γ-aminocaproic acid, glycine; acetoguanamine, 3-amino-1,2,4-triazole, isocyanuric acid, imidazoles, e.g., 2,4-diamino-6-[2'-methylimidazolyl-(1)']-ethyl-s-triazine, 2,4-diamino-6-[2'-undecylimidazolyl-(1)']-ethyl-s-triazine, 2,4-diamino-6-[2'-ethyl-4'-methylimidazolyl-(1)']-ethyl-s-triazine, a 2-methylimidazole-isocyanuric acid adduct, a 2-phenylimidazole-isocyanuric acid adduct; 5,5-dimethylhydantoin, benzoguanamine, 1-methylol-5,5-dimethylhydantoin, melamine, 1,3-diphenylguanidine, di-o-tolylguanidine, 1-o-tolybiguanide, N,N'-diphenylthiourea, 2-mercapto-2-imidazoline, N,N'-diethylthiourea, N,N'-dibutylthiourea, N,N'-dilaurylthiourea. The reaction (A) can be carried out in the presence or absence of an organic solvent at a temperature of from room temperature to 180°C while stirring for 0.5 to 10 hours. The solvent to be used include aromatic hydrocarbons, e.g., benzene, toluene; aliphatic hydrocarbons, e.g., hexane, ligroin; halogenated hydrocarbons, e.g., carbon tetrachloride, chloroform; and ethers, e.g., dioxane, tetrahydrofuran. In carrying out the reaction, the chemical equivalent ratio of epoxy group to an NH bond ranges from 1/10 to 10/1, and preferably from 1/1.5 to 1.5/1. (cf. Henry Lee and Kris Neville; Handbook of Epoxy Resins", S.5-12 and 5-13 (McGraw-Hill Book Co., 1967)) Synthesis Example 1 Synthesis of Compound B-2 In a flask equipped with a condenser, a dropping funnel and a stirrer, there was placed 168 g of vinylcyclohexene dioxide and heated at 170°C while stirring. Aniline (93 g) contained in the dropping funnel was added portionwise at a rate of 2 g/min. After completion of addition, the mixture was allowed to react for 1 hour to obtain a composition. Formation of Compound B-2 was confirmed by NMR spectral analysis. Synthesis Example 2 Synthesis of Compound B-6 4-Hydroxyphenylacetamide (150 g) was dissolved in 160 g of phenyl glycidyl ether and the solution was stirred for 5 hours at 90°C to obtain a viscous liquid composition. Formation of Compound B-6 was confirmed by NMR spectral analysis. The epoxy resin composition for intermediate for composite materials according to the present invention comprises from 2 to 150 parts by weight, and preferably from 10 to 50 parts by weight, of the above-described additive per 100 parts by weight of the total amount of the resin composition (an epoxy resin, a hardener and/or a hardening accelerator). If the amount of the additive is less than 2 parts by weight, a substantial effect cannot be exerted. Amounts exceeding 150 parts by weight seriously reduce heat-resistance. The epoxy resin to be used in the epoxy resin composition includes well-known epoxy resins, such as polyglycidyl ethers of diphenylolalkanes, e.g., diphenylolpropane, diphenylolethane, diphenylolmethane, etc.; polyhydric phenol polyglycidyl ethers, e.g., novolak, resol, etc.; epoxy resins produced by epoxidation of alicyclic compounds (e.g., cyclohexene, cyclopentadiene, dicyclopentadiene, etc.), e.g., a ester of 3,4-epoxy-6-methylcyclohexanecarboxylic acid and methyl 3,4-epoxy-6-methylcyclohexanoate; poly(epoxyalkyl) ethers of aliphatic polyoxy compounds, e.g, ethylene glycol, glycerin, etc.; epoxyalkyl esters of carboxylic acids, e.g., glycidyl esters of aromatic or aliphatic carboxylic acids; and the like. These epoxy resins may be used alone or in combination thereof. A preliminary condensate between the above-enumerated epoxy resin and a hardener is also employed in the epoxy resin composition. The preliminary condensate which can be used in the present invention can be prepared by subjecting at least one polyamine or acidic substance having a polycarboxylic group, a polycarboxylic acid anhydride group or a mixed group thereof and the above-mentioned epoxy resin to heat treatment to increase the viscosity of the mixture at least 3 times without inducing gelation. Examples of the polyamine to be used for obtaining the preliminary condensate are aromatic polyamines, e.g., o-phenylenediamine, m-phenylenediamine, 4,4'-methylenedianiline, 4,4'-diaminodiphenylsulfone, 3,3'-diaminodiphenylsulfone, m-xylylenediamine, etc.; and aliphatic polyamines, e.g., triethylenetetramine, diethylenetriamine, isophoronediamine, 1,3-diaminocyclohexane, menthanediamine, cyanoethylated diethylenetriamine, N-aminoethylpiperazine, methyliminobispropylamine, aminoethylethanolamine, polyethylenediamine, polymethylenediamine, etc. These polyamines can be used alone or in combination thereof. Examples of the acidic substance which can be used as a hardener for obtaining the preliminary condensate are phthalic anhydride, succinic anhydride, maleic anhydride, hexahydrophthalic anhydride, pyromellitic anhydride, benzophenonetetracarboxylic anhydride, trimellitic anhydride, itaconic anhydride, citraconic anhydride, dodecenylsuccinic anhydride, chlorendic anhydride, methylcyclopentadiene-maleic acid adduct, methyltetrahydrophthalic anhydride, maleic anhydride-linoleic acid adduct, cyclopentanetetracarboxylic anhydride, alkylated endoalkylenetetrahydrophthalic anhydrides, ethylene glycol bistrimellitate, glycerin tristrimellitate, and the like. These acidic substances may be used alone or in combination of two or more thereof. The chemical equivalent ratio of the polyamine or acidic substance to the epoxy resin is important and ranges from 1:1 to 1:6, preferably from 1:1.4 to 1:6, and more preferably from 1:1.5 to 1:5. If this equivalent ratio is more than 1:1, the excess polyamine or acidic substance reduces heat resistance and strength of a hardened product. On the other hand, if it is less than 1:6, the polyamine or acidic substance becomes short to deteriorate heat resistance or strength of a hardened product. The term "chemical equivalent ratio" as herein used means that one epoxy group is equivalent to one N-H bond or carboxylic acid group or one half carboxylic acid anhydride group. The temperature for the heat treatment for obtaining the preliminary condensate is determined depending on the time required for reaching a desired viscosity and controllability of viscosity. When the epoxy resin is used in a large excess within the above-described range, it is possible to shorten the treating time by raising the heating temperature. On the other hand, when the epoxy resin is used in a slight excess, the reaction mixture is readily gelled so that the heating temperature should be controlled lower. The heating temperature ranges from 50° to 200°C, and preferably from 120° to 170°C. The condensation reaction is usually carried out under normal pressure, but may be effected under pressure. The reaction is usually conducted in the absence of a solvent, but when any one or more of the epoxy resins, polyamines and acidic substances are solid at room temperature, solvent may be employed. Such being the case, hydrocarbons that do not adversely affect the produced preliminary condensate, such as xylene, toluene, cyclohexane, etc., are preferred. In the case where a solvent is employed, the resulting reaction mixture containing the solvent may be used as such depending upon the application of the product. If necessary, the solvent may be removed from the reaction mixture by distillation under reduced pressure or a like technique. The reaction is stopped at the point when the viscosity of the reaction mixture is increased to at least three times the initial one. The upper limit of the viscosity is not particularly restricted as long as gelation does not occur, but the reached viscosity is usually from 10 to 100 times the initial one. The term "viscosity" as herein used means a viscosity as determined by a Brookfield viscometer. The stopping of the reaction can be effected by a known method appropriately selected according to the purpose, for example, a method of quenching the reaction mixture to room temperature, a method of adding a solvent inert to an epoxy group, e.g., acetone, methyl ethyl ketone, toluene, xylene, etc., a method of spreading the reaction mixture in thin film over a cooled plate, and the like. Use of the above-described preliminary condensate in the epoxy resin composition of the present invention has the following advantages. Those prepared from polyamines and epoxy resins improve working stability (working life) of the composition and also alleviate toxicity and moisture-absorbing property of polyamines as compared with a mere blend of the polyamines (hardener) and epoxy resins. Those prepared from the acidic substances and epoxy resins achieve reduction in a hardening temperature and a hardening time as compared with a mere blend of the acidic substances (hardener) and epoxy resins. Further, these preliminary condensates also have an advantage of possible reduction of a rate of contraction upon hardening. The hardener added to the epoxy resin composition according to the present invention is dicyandiamide in view of sufficient preservability and working stability of the resulting epoxy resin composition. The hardening accelerators which are added to the epoxy resin composition in accordance with the present invention are urea compounds represented by the formula (II): wherein Y and Z, which may be the same or different, each represents a hydrogen atom, a chlorine atom, a bromine atom, a nitro group, a methyl group, a methoxy group or an ethoxy group. Epoxy resin compositions containing urea compounds represented by the formula (II) have sufficient preservability and are rapidly hardenable at relatively low temperatures. Specific examples of the urea compounds of the formula (II) are N-(3-chloro-4-methoxyphenyl)-N',N'-dimethylurea, N-(4-chlorophenyl)-N',N'-dimethylurea, N-(3-chloro-4-ethylphenyl)-N',N'-dimethylurea, N-(3-chloro-4-methylphenyl)-N',N'-dimethylurea, N-(3,4-dichlorophenyl)-N',N'-dimethylurea, N-(4-ethoxyphenyl)-N',N'-dimethylurea, N-(4-methyl-3-nitrophenyl)-N',N'-dimethylurea. The polyamine and/or acidic substance having a polycarboxylic group, a polycarboxylic acid anhydride group and/or a mixed group thereof and the dicyandiamide are all together present in amounts of 40 to 90%, preferably 50 to 80%, of the chemical equivalent amounts based on the total epoxy functional group. If the amounts of hardener is less than 40% of the chemical equivalent amounts, heat resistance of the hardened product is insufficient, and if it exceeds 90% of the chemical equivalent amounts, the hardened product becomes brittle. The hardening accelerator is used in amounts of from 1 to 15 parts by weight per 100 parts by weight of the total amount of the epoxy resin and the additives. If the amount of the hardening accelerator is less than 1.5 parts by weight, reduction of the hardening temperature cannot be achieved, and amounts exceeding 15 parts by weight decreases the molecular weight to deteriorate heat resistance. Moreover, when the additives of the formula (I) according to the present invention contain a functional group which contributes to hardening, it is desirable to decrease the amount of the hardener depending on the functionality of such a functional group. Reinforcing materials in which the epoxy resin composition is impregnated to prepare an intermediate material for a composite include chops, yarns, tapes, sheets, knitted products, mats and paper-like products made of carbon fiber. Impregnation of the epoxy resin composition of the present invention into the above-described reinforcing materials can be carried out by a hot-melt method or a lacquer method, either directly or after film formation. Direct impregnation by a lacquer method is easier. The intermediate material, the so-called prepreg, thus obtained can be molded under appropriate conditions of pressure, temperature and time to provide composites having extremely excellent mechanical strength. The present invention will now be illustrated in greater detail with reference to examples and comparative examples which are given for illustrative purposes only but not for limitation. EXAMPLES 1 TO 9 AND COMPARATIVE EXAMPLES 1 TO 3 In a heating apparatus equipped with a stirrer were placed 100 g of an epoxy resin ("Epikote 828", a trade mark for a product manufactured by Shell Chemicals Corp.) and 9 g of 4,4'-diaminodiphenylsulfone, and the mixture was polymerized at 150°C for 4 hours while stirring. The reaction mixture was spouted in thin film over an ice-cooled panel to stop the polymerization to obtain Preliminary Condensate (A-1). Additive (B) (the kind and amount are shown in Table 1 below) and 3 g of N-(3,4-dichlorophenyl)-N',N'-dimethylurea were added to 100 g of Preliminary Condensate (A-1), and the mixture was mixed with stirring at 50°C to obtain Resin Composition (C). Resin Composition (C) thus obtained was pasty immediately after the preparation and turned out to be an insoluble and non-melting, transparent solid in 30 minutes at 130°C. The pasty composition had a working life of 1 month or longer at 25°C as determined by allowing a 50 g portion of the composition before hardening to stand at room temperature and measuring the time at which the viscosity sharply increased. Then, Resin Composition (C) was cell-casted and hardened at 130°C for 60 minutes to form a resin plate. The resulting resin plate was subjected to bending test to obtain bending strength, modulus of elasticity in blending and elongation, and the results obtained are shown in Table 1 below. The bending test was carried out under the condition of L/D=16 using a sample piece of 1 t x 4 x 60 mm. Further, 60 g of the pasty resin composition was dissolved in 40 g of methyl ethyl ketone to form a uniform solution. The resulting resinous solution was impregnated into carbon fibers ("Pilofil T-1", a trade mark for a product manufactured by Mitsubishi Rayon Company Limited), and the carbon fiber having impregnated therein the resin solution was wound around a drum, which had previously been covered with a release paper coated with silicone, at a given width. The release paper was taken off from the drum and the resin-impregnated carbon fiber was dried at 70°C for 15 minutes to prepare a prepreg having a resin content of 40% by weight. The resulting prepreg had a gelation time of 45 minutes or more at 140°C as determined in accordance with JIS K-5909 and a working life of 1 month or more at 25°C. The prepregs thus produced were laminated in one direction and hardened at 130°C for 60 minutes, and the hardened product was subjected to heat distortion temperature test and bending test. The heat distortion temperature was determined under a load of 1.82 MPa (264 psi) in parallel to the fiber axis direction in accordance with ASTM D648, and the bending test was conducted under the condition of L/D=40 using a sample piece of 2 t x 10 x 100 mm. The heat distortion temperature was 150°C or higher in each case, and the results of the bending test are shown in Table 1 below. In Table 1, the following compounds were used as Additive. Additive EXAMPLES 10 TO 13 AND COMPARATIVE EXAMPLES 4 TO 6 In a heating apparatus equipped with a stirrer were charged 100 g of Epikote 828 and Additive B as shown in Table 2 below, and the mixture was uniformly mixed at 60°C for 10 minutes with stirring. A hardener and a hardening accelerator as shown in Table 2 were added thereto, followed by uniformly mixing at 60°C for 10 minutes to obtain Resin Composition (E). Resin Composition (E) was molded into a plate at 130°C for 60 minutes by a cell-casting method, and the resulting molded product was subjected to bending test in the same manner as in Example 1. The results obtained are shown in Table 2 below. Further, Resin Composition (E) was uniformly impregnated into carbon fibers, and the resin-impregnated carbon fibers were orientated in one direction to form a sheet prepreg. The prepregs thus obtained were laminated and hardened in a mold at 90°C for 1 hour and then at 130°C for 1 hour under a pressure of 6.86 GPa (7 Kg/cm²). The hardened product was subjected to bending test in the same manner as in the foregoing examples, and the results obtained are shown in Table 2 below. In Table 2, the following compounds were used as Additive, hardener and hardening accelerator. Additive Hardener H-1 4,4'-Methylenedianiline H-2 Dicyandiamide Hardening Accelerator HA-1 N-(3,4-Dichlorophenyl)-N',N'-dimethylurea HA-2 N-(3-Chloro-4-methylpheny)-N',N'-dimethylurea HA-3 N-(4-Chlorophenyl)-N',N'-dimethylurea HA-4 N-(2-Chlorophenyl)-N',N'-dimethylurea HA-5 N-(4-Ethoxyphenyl)-N',N'-dimethylurea EXAMPLES 14 TO 22 Starting compounds (III) and (IV) were mixed in a weight ratio shown in Table 3 and the mixture was reacted at 150°C for 3 hours to obtain Compounds B-9 to B-13. After completion of reaction, formations of compounds were confirmed by NMR spectral analysis. The procedures of Example 1 were repeated except that the additives shown in Table 3 and the hardeners and the hardening accelerators shown in Table 4 were used to prepare resin plates and carbon fiber composites. The mechanical properties of these samples were determined in the same manner as in Example 1. The results obtained are shown in Table 4 below. EXAMPLE 23 In a heating apparatus equipped with a stirrer and a reflux tube were charged 100 g of Epikote 828 and 8 g of 4,4'-diaminodiphenylmethane, and the mixture was polymerized at 150°C for 3 hours while stirring. Immediately after the polymerization, 27 g of methyl ethyl ketone was added thereto for quenching and dissolving to obtain Preliminary Condensate (A-2). To 135 g of the resulting methyl ethyl ketone solution of Preliminary Condensate (A-2) were added 40 g of Additive B-13 as shown in Table 3, and 7 g of dicyandiamide. After thoroughly dissolving the additive and urea compound, the methyl ethyl ketone was removed from a part of the resulting lacquer solution at 50°C under reduced pressure of 2 mmHg or less to obtain Resin Composition (F). Resin Composition (F) turned out to be an insoluble and non-melting, transparent solid when allowed to stand at 130°C for 50 minutes and had a working life of 1 month or more at 25°C. Resin Composition (F) was molded in a sheet by a cell-casting method at 130°C for 60 minutes. The hardened product was subjected to bending test in the same manner as used for the resin plates in the foregoing examples, and as a result, it showed a bending strength of 245 MPa (25 kg/mm²), a modulus of elasticity in bending of 5.62 GPa (573 kg/mm²) and an elongation of 9.1%. The rest of the above lacquer solution was impregnated in epoxy resin-sized plain-woven glass cloth ("EPC-250X1000" treated with S-420, produced by Arisawa Seisakusho Co., Ltd.) and dried in the same manner as in the foregoing examples to prepare a prepreg. The resulting prepreg had a gelation time of 3.7 minutes at 140°C and a working life of 1 month or more at room temperature (25°C). The prepregs were laminated and hardened at 130°C for 50 minutes, and the hardened product was subjected to bending test in the same manner as in the foregoing examples. As a result, it showed a bending strength of 314 MPa (32 kg/mm²), a modulus of elasticity in bending of 16.7 GPa (1.7 x 10³ kg/mm²) an elongation of 1.6%.

Claims: An intermediate for a composite material comprising a carbon fiber impregnated with an epoxy resin composition containing (A) epoxy resin and at least one preliminary condensate which is obtained by subjecting at least one polyamine or acidic substance having a polycarboxylic group, a polycarboxylic acid anhydride group or a mixed group thereof and an epoxy resin having at least one epoxy group at a chemical equivalent ratio of from 1:1 to 1:6 to heat treatment at a temperature of from 50 to 200°C to increase the viscosity of the mixture at least 3-times without inducing gelation, (B) either dicyandiamide and a hardening accelerator represented by the formula (II) whrein Y and Z, which may be the same or different, each represents a hydrogen atom, a chlorine atom, a bromine atom, a nitro group, a methyl group, a methoxy group or an ethoxy group, or the hardening accelerator represented by the formula (II) only, and (C) at least one of compound represented by the formula (I), wherein R₁ represents a hydrogen atom, an unsubstituted saturated aliphatic group having 1 to 17 carbon atoms, a substituted or unsubstituted, saturated alicyclic group having 5 to 17 carbon atoms, a substituted or unsubstituted aromatic group having 6 to 17 carbon atoms, or a substituted or unsubstituted , saturated or unsaturated 5- or 6-membered heterocyclic group containing N, O or S as hetero atom; R₂ has the same meaning as defined for R₁ or is a group of formula wherein R₅ and R₆, which may be the same or different, each represents a hydrogen atom or a substituted or unsubstituted, saturated aliphatic group having 1 to 17 carbon atoms, a substituted or unsubstituted, saturated alicyclic group having 5 to 17 carbon atoms, a substituted or unsubstituted aromatic group having 6 to 17 carbon atoms, or a substituted or unsubstituted, saturated 5- or 6-membered heterocyclic group containing N, O or S as hetero atoms; R₃ and R₄, which may be the same or different, each has the same meaning as defined for R₅ and R₆, or a group of formula R-OCH₂- wherein R has the same meaning as defined for R₅ and R₆; and X represents an oxygen atom, a sulfur atom or N-R₇ wherein R₇ has the same meaning as defined for R₅ and R₆, and wherein the compound or compounds represented by formula (I) is or are present in an amount of from 2 to 150 parts by weight per 100 parts by weight of the total amounts of the epoxy resin composition, the polyamine and/or acidic substance having a polycarboxylic group, a polycarboxylic acid anhydride group and/or a mixed group thereof and the dicyandiamide are all together present in an amount of from 40 to 90% of the chemical equivalent amounts based on the total epoxy functional group, and the hardening accelerator is present in an amount of from 1 to 15 parts by weight per 100 parts by weight of the total amount of the epoxy resin and the additives. An intermediate according to claim 1, wherein the substituent for the substituted aliphatic, alicyclic, aromatic or heterocyclic group as represented by R₁, R₂, R₅, R₆ or R₇ is a halogen atom, an alkoxy group having 1 to 3 carbon atoms, an aryloxy group having 6 to 17 carbon atoms or an acyl group having 2 to 7 carbon atoms. An intermediate according to claim 1 or 2, wherein R₂ and R₅ represent a substituted or unsubstituted, aromatic group having 6 to 17 carbon atoms. An intermediate according to any of claims 1 to 3, wherein at least one of R₃ and R₄ represents a substituted or unsubstituted, alicyclic group having 5 to 17 carbon atoms or an aromatic group having 6 to 17 carbon atoms. An intermediate according to any of claims 1 to 4, wherein the compound or compounds of formula (I) is or are present in an amount of from 10 to 50 parts by weight per 100 parts by weight of the total amounts of the epoxy resin composition. An intermediate according to any of claims 1 to 5, wherein the polyamine and/or acidic substance having a polycarboxylic group, a polycarboxylic acid anhydride group and/or a mixed group thereof and the dicyandiamide are all together present in an amount of from 50 to 80 % of the chemical equivalent amounts based on the total epoxy functional group. An intermediate according to any of claims 1 to 6, wherein the hardening accelerator represented by the formula (II) is present in an amount of from 2 to 10 parts by weight per 100 parts by weight of the total amounts of the epoxy resin and the additives. An intermediate according to claim 1, wherein the chemical equivalent ratio of the preliminary condensate of (A) is from 1:1.4 to 1:6. An intermediate according to claim 8, wherein the chemical equivalent ratio is from 1:1.5 to 1:5. An intermediate according to any of claims 1 to 9, wherein the epoxy resin is bisphenol A diglycidyl ether. An intermediate according to any of claims 1 to 10, wherein the polyamine is 4,4'-diaminodiphenylsulfone.

Inventors: AGATA AKIRA, II YASUAKI, TADA HISASHI, AKIRA, AGATA C/O MITSUBISHI RAYON CO., LTD., HISASHI, TADA C/O MITSUBISHI RAYON CO., LTD., YASUAKI, II C/O MITSUBISHI RAYON CO., LTD.
Applicants: MITSUBISHI RAYON CO, MITSUBISHI RAYON CO., LTD.
Application year: 1985
Main classification: C08G59
IPC codes: C08G59, C08J5, C07D303