SPHERICALLY SHAPED PRECIPITATED CALCIUM CARBONATE, ITS PREPARATION AND USE

Abstract: A precipitated calcite of substantially spherical morphol­ ogy having an average spherical diameter of from 2 to 10 microns and a specific surface area of from 1 to 15 square meters per gram is prepared by introducing carbon dioxide gas into an aqueous slurry of calcium hydroxide containing dissolved polyphosphate in the amount of from 0.1 to 1.0 percent, calculated as grams of phosphorus per 100 grams of the calcite equivalent of the calcium hydroxide, the starting temperature of the carbonation being 15 to 50°C. The spherical calcite is particularly suitable for use in dull finish coated paper.

Description: This invention concerns a novel precipitated calcium carbonate of spherical morphology as well as a method for its preparation and its use in such as paper coatings. Today's coated papers are graded primarily on the basis of their brightness. Within each grade, however, exist subcatgories defined by sheet gloss. Papers with a 75° sheet gloss of from 1 to 20% are generally considered matte finish papers, from 20 to 40% dull finish paper, from 40 to 55% mid-gloss papers, and above 55% enamel papers. These definitions are general, with some overlap in sheet gloss and brightness between consecutive grades. Certain esthetic optical properties of paper are also commonly associated with functional performance. This is seen, for example, in the relationship of high sheet gloss to high print gloss and a high degree of printing smoothness. Dull and matte finish papers have historically been rougher and lower in print gloss than enamel papers, a consequence of the pigments and formulations utilized and the finishing techniques employed in their manufacture. While numerous pigment combinations have been employed in attempting to produce a coated paper having a combination of dull finish and good printability, the need still exists for a coating pigment formulation which will accomplish this in a simple and economic manner. This need is satisfied by the present invention. Precipitated calcium carbonate in spherical or globular form is known. In U.S. Patent 3,304,154, for example, a finely divided precipitated calcium carbonate of generally spheroidal form is prepared by reacting a suspension of calcium hydroxide with carbon dioxide in a closed vessel at elevated temperature and pressure while rotating the vessel. In U.S. Patent 3,848,059, spheroidal shaped reticulated precipitated calcium carbonate of 0.1 to 5 micrometers is prepared by the double decomposition of two water-soluble salts such as calcium chloride and potassium carbonate dissolved in water droplets of two water-in-oil emulsions. Nakahara et al, J. Chem. Soc. Japan, 5 , 732 (1976), discloses the preparation of a globular or amorphous calcium carbonate by a similar interfacial reaction technique. Japanese Kokai 55-95617 discloses the preparation of globular-shaped calcium carbonate prepared by solution reaction of soluble calcium and carbonate salts at 70°C or below. Japanese Kokai 57-92520 purportedly prepares a spherical vaterite by a similar technique but in the presence of a divalent cation other than calcium, conversion of the vaterite to calcite being disclosed in Kokai 57-92521. Buehrer et al, J. Phys. Chem., 44 , 552 (1940) discloses a distorted calcite in apparently globular form precipitated from solution in the presence of sodium hexametaphosphate. Such precipitation of calcium carbonate in thee presence of sodium hexametaphosphate is also disclosed in U.S. Patents 3,179,493, 4,018,877 and 4,244,933 68 well as by Reitemeier et al, J. Phys. Chem., 44 , 535 (1940). Of these precipitations, only U.S. Patents 4,018,877 and 4,244,933 contemplate carbonating a lime slurry. U.S. Patent 4,367,207, describes a process for producing precipitated calcite in which carbon dioxide is introduced to an aqueous calcium hydroxide slurry containing anionic organopolyphosphonate polyelectrolyte. An average particle size for the calcite of from 0.08 to 0.4 µm is obtained when other agents for particle size control are used. It has now been found that the controlled addition of gaseous carbon dioxide to aqueous calcium hydroxide in the presence of limited amounts of surface active polyphosphate produces a novel spherically shaped precipitated calcite of uniform particle size and low surface area which is eminently suitable for use in such as dull finish coated paper. Accordingly, the present invention entails a precipitated calcite having particles of substantially spherical morphology with an average spherical diameter of from 2 to 10 microns, a particle size distribution such that at least about 50 weight percent of the particles lie within 50 percent of the average spherical diameter, and a specific surface area of from about 1 to 15 square meters per gram. Preferably the precipitated calcite has an average spherical diameter of from about 2 to 5 microns with at least 60 weight percent of the particles lying within 50 percent of the average spherical diameter. The present invention also entails a process for preparing such a precipitated calcite of substantially spherical morphology, which comprises a process for preparing a precipitated calcite as defined in claim 1 or 2, which comprises bubbling gaseous carbon dioxide through an aqueous slurry of calcium hydroxide having a starting concentration of at least 5% by weight of calcium hydroxide and containing dissolved polyphosphate in an amount of from 0.1 to 1.0 percent, calculated as grams of phosphorous per 100 grams of calcium carbonate molar equivalent of the calcium hydroxide, the introduction of carbon dioxide being started at a temperature from 15° to 50°C and the temperature being permitted to rise by not more than 35°C during the introduction, the introduction being terminated when the pH of the carbonated slurry reaches about 7, after a period of introduction from 40 to 100 minutes. Preferably, the dissolved polyphosphate is sodium hexametaphosphate; and the calcium hydroxide in the slurry is prepared at a concentration of from about 15 to 20 weight percent by reacting lime (calcium oxide) with water at a starting temperature of from about 10 to 45°C. The slurry following termination of the introduction is preferably treated with sufficient polybasic acid to essentially neutralize any unconverted calcium hydroxide in the slurry. The present invention further contemplates a paper sheet having on at least one of its surfaces a coating with a 75° gloss of from about 20 to 40 percent, the coating comprising the presently claimed precipitated calcite. Novel features and advantageous of the present invention will become apparent to those skilled in the art from a reading of the following detailed description in conjunction with the accompanying drawing, wherein: Figure 1 is a photomicrograph at a magnification of 3000 of the precipitated calcite of substantially spherical morphology of the present invention, and Figure 2 is a representation of the particle size distribution of the precipitated calcite. The process of the present invention, by carbonating aqueous lime slurries at a starting temperature of from about 15 to 50°C in the presence of a specified amount of surface active polyphosphate, provides a simple and economic means of obtaining a stable precipitated calcium carbonate of spherical morphology in a size that can be readily controlled. The product of the process, a calcite, normally has an average spherical diameter of from about 2 to 10 micrmeters, a particle size distribution such that 50 weight percent of the particles lie within 50 percent of the overage spherical diameter, and a specific surface area of from about 1 to 15 square meters per gram. Preferably, the average spherical diameter of the particles is from about 2 to 5 micrometers with about 60 weight percent of the particles lying within 50 percent of the average spherical diameter. With proper selection of reactants, the calcium carbonate content of the product can be greater than 97 percent, the only impurities normally being the added polyphosphate, magnesium carbonate and/or hydroxide from the starting lime, and intercrystalline water. The surface active polyphosphates employed in the instant process are surfactants commonly used as scale inhibitants, sequestrants, deflocculants and detergent promoters. Any water-soluble polyphosphate of the formula M (n+2) P n O (3n+1) or (MPO₃) n wherein M is hydrogen, ammonium or alkali metal and n is an integer of 2 or greater, can be used. Such polyphosphate in which an alkaline earth metal or zinc is the cation may also be used. Particularly suitable polyphosphates include the alkali metal polyphosphates and metaphosphates wherein n is from 2 to 25. Preferred are alkali metal pyrophosphate, tripolyphosphate and especially sodium hexametaphosphate. In employing the surface active polyphosphate of the instant invention, the polyphosphate is added to the calcium hydroxide, or slaked lime, slurry prior to carbonation of the slurry. The polyphosphate is added in levels of from about 0.1 to 1.0 percent, calculated as grams of phosphorus per 100 grams of the calcium carbonate molar equivalent of the lime content of the slurry. The addition of the polyphosphate at a level below about 0.1 percent phosphorus tends to produce scalenohedral calcite rather than the desired calcite of spherical morphology, while additions above about 1.0 percent produce declining amounts of spherical calcite mixed with larger and smaller particles of nondescript morphology. The preferred addition is from about 0.15 to 0.3 percent. The spherical calcite of the present process is obtained only when the temperature for the carbonation of the lime slurry is carefully controlled. To consistently produce the desired product, the starting temperature of the carbonation must be from about 15 to 50°C. By starting temperature is meant the temperature of the lime slurry at the start of the introduction of carbon dioxide gas after the polyphosphate has been added. If the starting temperature of the carbonation is below about 15°C, the product tends to be smaller than the desired minimum of about 2 microns with an unacceptably high surface area, while a starting temperature of greater than about 50°C tends to produce calcite of scalenohedral morphology rather than the desired calcite of spherical morphology. Preferably the starting temperature for producing the desired particle is from about 30 to 35°C. While the starting temperature of the carbonation is critical in producing a precipitated calcite of the desired morphology and size, the temperature during the remainder of the carbonation also tends to influence the resulting precipitate. Therefore, the temperature is limited to a maximum rise of about 35°C during the introduction. The nature of the carbon dioxide gas for the carbonation is not particularly critical, the standard mixtures of carbon dioxide in either nitrogen or air commonly used for such carbonations being satisfactory. Likewise, the nature of the source for the starting calcium hydroxide slurry is not critical; either lime or hydrated lime (calcium hydroxide) may be used. The purity of the carbonating gas and the lime essentially determine the purity of the final product. While the present process is applicable to all concentrations of lime slurries which can be carbonated, it is practically limited to those slurries in which the calcium hydroxide concentration of the starting slurry is greater than about 5 weight percent. Lower concentrations are generally uneconomic. For most economic operation, the concentration of the calcium hydroxide in the slurry to be carbonated is preferably from about 15 to 20 percent by weight. As with the concentration, the particle size of the calcium hydroxide is not critical. When dry hydrated lime (calcium hydroxide) is slurried in water for the carbonation, a maximum particle size of from about 40 to 200 µm is preferred, while when calcium oxide is slaked to form the hydroxide, the slaking is preferably conducted starting at a temperature of from about 10 to 45°C. The carbonation of the lime slurry is continued until the calcite precipitation is substantially complete, being terminated when the pH of the carbonated slurry is at about 7. Such carbonation is usually accomplished in, a period of from about 40 to 100 minutes. Normal care is exercised to neutralize any unreacted calcium hydroxide still present in the carbonated slurry. Various techniques known to those skilled in the art can be used to accomplish this neutralization. These include, for example, monitoring the slurry pH with introduction of additional carbon dioxide gas as is necessary as well as treating the carbonated slurry with a sufficient amount of an organic or inorganic polybasic acid such as citric, maleic, malic, malonic, phthalic, tartaric, boric, phosphoric, sulfurous or sulfuric acid. The calcium carbonate in the final slurry may be utilized as such, or may be filtered, dried and milled for use as a dry product. The product of the present invention has been found to be especially useful as a pigment in formulations used to produce a dull coated paper sheet with a 75° gloss (according to TAPPI standard T480) of from about 20 to 40 percent. Such coating formulations, in addition to showing superior rheology have produced coated paper having good opacity, brightness, smoothness and ink receptivity as well as the desired gloss and printability. Its use in matte and mid-gloss coated papers, as well as in dentrifice formulations as an abrasive, is also contemplated. The following examples are merely illustrative and are not to be construed as limiting the invention, the scope of which is defined by the appended claims. EXAMPLE 1 The following carbonation was conducted in a 32-liter jacketed, baffled, cylindrical stainless steel reactor having an internal diameter of 29 cm, a height of 46 cm and a conical bottom about 4 cm deep, equipped with a high speed agitator having two 15 cm diameter flat-blade turbine impellers positioned about 2.5 cm and 13 cm above the bottom of the straight side of the reactor and driven by a 1.125 kW (1.5 horsepower) continuous duty motor. A carbon dioxide/air gas stream was introduced through vertical copper tubing of about 1 cm internal diameter and distributed by means of a horizontal copper sparge ring of about 15 cm overall diameter positioned near the bottom of the straight side of the reactor and having eight evenly spaced 0.3 cm diameter holes to facilitate gas dispersion. A 15.5 weight percent aqueous calcium hydroxide, or milk of lime, slurry was prepared by adding over about a 90-second period 2.68 kg of granular active lime having an available calcium oxide content of about 93 weight percent, as determined by ASTM procedure C-25-72, to 18.75 kg of tap water at 33°C contained in the carbonator and stirred at about 400 RPM. After stirring the resulting slurry for about 10 minutes, 35.6 g of sodium hexametaphosphate (Baker Grade [NaPO₃]₆, J. T. Baker Chemical Co., Phillipsburg, New Jersey; equal to about 0.24 percent, calculated as grams of phosphorus per 100 grams of the calcium carbonate molar equivalent of the calcium hydroxide content of the slurry) dissolved in 1.62 liters of tap water was added. The slurry was then cooled from the final slaking temperature of 51°C to 35°C by means of the cooling jacket. The agitator was adjusted to about 500 RPM, and the slurry was carbonated by passing a gas mixture of 28 volume percent carbon dioxide in air at about 64 standard liters per minute (SLM) through the slurry over a 60-minute period while allowing the slurry temperature to rise unchecked. To the final carbonated slurry at pH 7-7.5 and 59°C was added 15.7 g of phosphoric acid (Baker Analyzed Reagent 85% H₃PO₄, J. T. Baker Chemical Co.; equivalent to about 0.3 weight percent of the calcium carbonate equivalent of the calcium hydroxide content of the slurry) diluted with 100 g tap water. The slurry was passed through a U.S.A. Standard No. 325 (45 µm) sieve to remove the grit present in the original lime, and then vacuum filtered. The filter cake was air dried overnight at 120°C to yield a precipitated calcite product of substantially spherical morphology having a specific surface area (SSA) of 1.86 m²/g and an average spherical diameter (ASD) of 5.4 micrometers with 77 weight percent of the particles within plus or minus 50 percent of the average spherical diameter, i.e., 2.7 to 8.1 micrometers. A photomicrograph of the product at a magnification of 3000 is shown in Figure 1, while its particle size distribution is shown in Figure 2. The surface area of the product was measured using a Micromeritics DigiSorb 2600, which employs the standard BET theory with nitrogen as the adsorbing gas. The particle size distribution (PSD) of the product was determined by a sedimentation technique using an aqueous dispersion of the product and a Micromeritics SediGraph Model 5000, the aqueous dispersion being prepared by adding 0.75-0.80 g of the dry calcium carbonate to 25 ml of a 0.1% aqueous carboxylated polyelectrolyte solution (Daxad 30; W. R. Grace and Co., Lexington, MA) and vibrating the mixture with 150 watts of ultrasonic energy for 5 minutes. EXAMPLE 2 Precipitated calcite of spherical morphology was prepared following the slaking, carbonation and isolation procedures of Example 1, except that the initial slaking water temperature was 27°C and the level of sodium hexametaphosphate was varied, with the results as indicated in the following table. Run (NaPO₃)₆, % P Product ASD, µm ± 50% of ASD, % SSA, m²/g 2A 0.12 2.5 85 12.9 2B 0.18 2.8 83 4.3 2C 0.30 4.4 64 3.8 2D 0.46 6.8 69 4.9 2E 0.68 9.6 69 10.9 2F 0.91 10.0 52 9.1 Carbonation of the slaked lime slurry at a sodium hexametaphosphate level of 0.06% phosphorus (% P) produced a calcite of scalenohedral morphology. EXAMPLE 3 Precipitated calcite of spherical morphology was prepared following the procedures of Example 1, except that the initial slaking water temperature was 21°C and the initial carbonation temperature was varied, with the results as indicated in the following table. Temp, °C Product Run Start End ASD, µm ± 50% of ASD, % SSA, m²/g 3A 15 51 2.0 69 8.9 3B 30 59 3.0 76 3.6 3C 45 65 5.8 71 3.1 3D 50 70 3.9 80 3.3 Carbonation at a starting temperature of 5°C produced a precipitated calcium carbonate of nondescript morphology, while carbonation at starting temperatures of 55°C and above produced a precipitated calcite of scalenohedral morphology. EXAMPLE 4 Precipitated calcite of spherical morphology was prepared following the procedures of Example 1, except that the initial slaking water temperature was varied, with the results as indicated in the following table. Run Initial Slaking Temp,°C Product ASD, µm ± 50% of ASD, % SSA m²/g 4A 41 1.9 75 6.8 4B 12 6.8 75 8.1 EXAMPLE 5 Precipitated calcite of spherical morphology was prepared following the procedures of Example 1, except that the initial slaking water temperature was 27°C and the batch carbonation time was varied, with the results shown in the following table. Run Carbonation Time, min Product ASD, µm ± 50% of ASD, % SSA, m²/g 6A 49 2.8 80 4.4 6B 82 4.2 63 3.6 6C 95 5.2 61 3.3 EXAMPLE 6 Precipitated calcite of spherical morphology was prepared following the procedures of Example 1, except that the initial slaking water temperature and the concentration of the calcium hydroxide slurry, as well as the gas delivery rate to maintain a batch carbonation time of about 60 minutes, were varied, with the results as indicated in the following table. Run Ca(OH)₂ g/100 g Slurry Initial Slaking Water Temp, °C Gas Rate, SLM Product ASD, µm ± 50% of ASD, % SSA, m²/gm 7A 5.0 41 19 5.6 72 3.0 7B 10.0 33 41 3.7 72 4.4 7C 20.7 22 64 3.1 79 7.2 7D 24.9 21 90 3.1 72 3.3 EXAMPLE 7 Precipitated calcite of spherical morphology was prepared following the procedures of Example 1, except that the aqueous calcium hydroxide slurry was prepared at a concentration of 14.9 weight percent by adding over a period of about 90 seconds 3.29 kg of commercial dry hydrated lime, or calcium hydroxide, to a total of 18.75 liters of tap water at about 35°C, using two different hydrate particle sizes, with the results as indicated in the following table. Run Hydrate Size,µm Product ASD, µm ± 50% of ASD, % SSA, m²/g 7A 45 3.8 69 5.2 7B 150 3.8 70 5.0 EXAMPLE 8 Precipitated calcite of spherical morphology was prepared using the procedures of Example 1, except that the initial slaking water temperature was 27°C and both the type and level of dissolved polyphosphate were varied, with the results as indicated in the following table. Run Polyphosphate Product Nature g/100g CaCO₃ % P ASD, µm ± 50% of ASD, % SSA m²/g 8A Na₄P₂O₇ .10H₂O 1.3 0.18 2.8 87 1.5 8B " 2.2 0.30 6.7 76 1.0 8C Na₅P₃O₁₀ 0.7 0.18 3.5 81 2.6 8D " 1.2 0.30 3.5 72 2.9 EXAMPLE 9 The unique properties of the spherically shaped precipitated calcite of the present invention as a dull finish paper coating pigment were shown by substituting it for both a standard high gloss paper coating pigment and a typical ground limestone often used in dull coatings on an equal weight basis in a standard high gloss paper coating formulation using typical high gloss supercalendering conditions. The physical properties of the three pigments are given in Table I, while the paper coating formulation employed is indicated in Table II. In each case, the coating colors were prepared by first slurrying the coating clay at 73 percent solids using 0.1 percent tetrasodium pyrophosphate dispersant, based on the clay, and a 5 cm (2-inch) Cowles-type mixer at 4900 RPM. The calcium carbonate pigment was similarly slurried at the highest possible solids using a sodium polyacrylate dispersant as required by the pigment's dispersant demand. At this point, 50 parts of the calcium carbonate pigment slurry was added to 50 parts of the clay slurry (dry weight basis) with the mixer at about 1500 RPM. The SBR latex and alkali reactive acrylic latex were then added, and the pH of the coating color was adjusted to between 8.5 and 9.0 with ammonium hydroxide. The calcium stearate lubricant and crosslinking agent were then added to complete the coating color formulation, and mixing was continued for about 5 minutes. The percent solids, pH and rheology of each coating color were evaluated as indicated in Table III. The coatings were applied to a 28 kg (62 pound) prime coat base stock with a TIME/LIFE coater (Lewis Chambers Co., Macon, GA). Coatings were applied one side at a time followed by drying on a Duophoto Economy Dryer (Duophoto Corp., New York, NY) at 218°F (104°C) for about 1 minute. All coated sheets were then conditioned for 24 hours at 73°F (23°C) and 50 percent relative humidity. After conditioning, coated paper samples chosen on the basis of nearly equivalent coat weights were calendered 2 nips on a laboratory calender operated at 273 kg (600 pounds) per 2.54 cm (linear inch) with the rolls heated to about 150°F (66°C). To obtain ink gloss and allow detection of any mottling defect in the surface, a common problem with dull coated paper, coated test sheets were printed with a blue gloss ink on a Vandercook printing press. The results are shown in Table IV. With the high gloss pigment producing a 75° paper gloss of 65 percent, it is clear that the coating and calendering conditions were in the normal range for high gloss enamel paper. The unique dulling characteristics of the spherical calcite pigment of the present invention under these conditions are apparent; the pigment not only outperformed the ground limestone in gloss reduction, but did so while maintaining a superior paper smoothness. The results also indicate a slightly more porous and ink receptive surface for the coated paper incorporating the spherical calcite pigment compared to that incorporating the ground limestone pigment. CaCO₃ Pigment Morphology ASD, µm ± 50% of ASD, % SSA, M²/g high gloss hexagonal prisms 0.8 66 8.1 ground limestone irregular 1.9 38 5.6 spherical calcite spherical 2.7 80 6.0 Order of Addition Component Parts (weight) 1 coating clay 50 2 CaCO₃ pigment 50 3 SBR latex 12 4 acrylic latex 3 5 ammonium hydroxide (to pH 8.5-9) 6 lubricant 0.5 7 crosslinking agent 0.5 Test CaCO₃ Pigment Used in Coating Color High Gloss Ground Limestone Spherical Calcite % Solids 67.7 67.8 67.8 pH 9.3 8.9 9.0 Viscosity, centipoise 3900 2750 4150 Rheology Shear Rate, RPM 2600 4400 3200 Shear Stress, 1N (10⁵ dyne) cm 30 17 30 Coated Paper Test CaCO₃ Pigment Used in Coating Color High Gloss Ground Limestone Spherical Calcite Basis Weight (25x38-500) 81.7 81.7 81.6 Caliper, mils 4.0 3.9 3.9 Ash, % 33.5 33.2 33.1 TAPPI Brightness 84.5 83.6 83.8 TAPPI Opacity 97.4 97.4 97.3 Gurley Porosity, sec/100 cc 3700 4400 3800 Sheffield Smoothness, cc/sec 21 34 19 K&N, 2 minutes, % 78.9 82.7 77.1 Paper Gloss (75°), % 65 53 39 Paper Mottle Rating (visual) pass pass pass Print Gloss (75°), % 93.5 92 88 Print Mottle Rating, (visual) pass pass pass EXAMPLE 10 Coated paper utilizing the spherical calcite of the present invention was compared with that utilizing a commercially available kaolin dull finish coating pigment. In this comparison, the procedures of Example 9 were followed, with the exception that the commercial dull finish coating clay constituted 100 percent of the coating pigment, the paper was coated on one side only, and the calendering was increased to 4 nips at 364 kg (800 pounds) per 2.54 cm (linear inch) with the rolls at 120°F (49°C). The physical properties of the pigments are summarized in Table V, the properties of the coating colors in Table VI, and the coated paper results in Table VII. Pigment Morphology ASD, µm ± 50% of ASD, % SSA, M²/g high gloss CaCO₃ hexagonal prisms 0.8 66 8.1 spherical calcite A spherical 2.7 80 6.0 spherical calcite B spherical 4.2 60 3.9 dull finish clay platy 1.8 32 8.7 Test 50/50 Coating Clay/CaCO₃ 100 Dull Finish Clay High Gloss CaCO₃ Spherical Calcite A Spherical Calcite B % Solids 68.0 66.8 67.1 63.4 pH 8.7 8.9 8.7 8.7 Viscosity, 10⁻3 Pa.s (centipoise) (1) 3900 1125 2425 1700 Rheology Shear Rate, RPM 2350 4400 4400 4400 Shear Stress, 1N (10⁵ dyne)cm 30 17 15 10 Coated Paper Test 50/50 coating Clay/CaCO₃ 100 Dull Coating Clay High Gloss CaCO₃ Spherical Calcite A Spherical Calcite B Basis eight (25x38-500) 69.8 69.5 69.9 70.0 Caliper, mils 3.8 3.6 3.7 3.7 Ash, % 23.5 23.9 24.1 24.0 TAPPI Brightness 85.8 85.5 85.3 82.9 TAPPI Opacity 95.2 94.8 94.7 94.7 Gurley Porosity, sec/100 cc 6100 5650 6650 6600 Sheffield Smoothness, cc/sec 31 38 42 37 R, 2 minutes, % 72.8 73.5 73.9 78.6 Paper Gloss (750), % 59 35 31 39 Paper Mottle Rating (visual) pass pass pass Pass Print Gloss (75°), % 86 84 80 85 Print Mottle Rating (visual) pass Pass pass fail Paper coating employing the spherical calcite of the present invention again showed exceptional dulling efficiency while maintaining satisfactory brightness, opacity, porosity, smoothness and ink receptivity as well as an absence of paper and print mottling. This is in contrast to the coating utilizing 100 percent of the commercially available kaolin dull finish coating pigment, which had a satisfactory dull finish gloss but poorer brightness and ink receptivity with a printed surface showing excessive mottling.

Claims: A precipitated calcite having particles of spherical morphology with an average spherical diameter of from 2 to 10 micrometers, particle size distribution such that at least 50 weight percent of the particles lie within plus or minus 50 percent of the average spherical diameter, and a specific surface area of from 1 to 15 square meters per gram. The precipitated calcite of claim 1 wherein the average spherical diameter is from about 2 to 5 micrometers and at least 60 weight percent of the particles lie within plus or minus 50 percent of the average spherical diameter. A process for preparing a precipitated calcite as defined in claim 1 or 2, which comprises bubbling gaseous carbon dioxide through an aqueous slurry of calcium hydroxide having a starting concentration of at least 5% by weight of calcium hydroxide and containing dissolved polyphosphate in an amount of from 0.1 to 1.0 percent, calculated as grams of phosphorous per 100 grams of calcium carbonate molar equivalent of the calcium hydroxide, the introduction of carbon dioxide being started at a temperature from 15° to 50°C and the temperature being permitted to rise by not more than 35°C during the introduction, the introduction being terminated when the pH of the carbonated slurry reaches about 7, after a period of introduction from 40 to 100 minutes. The process of claim 3, in which the dissolved polyphosphate is sodium hexametaphosphate. The process of claim 3 or 4 wherein the introduction is started at a temperature of from 30 to 35°C. The process of claim 3, 4 or 5 wherein the calcium hydroxide in the slurry is present at a starting concentration of from 15 to 20 weight percent. The process of claim 3, 4, 5 or 6 wherein the slurry following termination of the introduction is treated with sufficient polybasic acid to essentially neutralize any unconverted calcium hydroxide in the slurry. The process of any one of claims 3 to 7 wherein the source of the calcium hydroxide in the slurry is dry hydrayted lime and the maximum particle size thereof is from 40 to 200 micrometers. The process of any one of claims 3 to 7 wherein when the source of the calcium hydroxide in the slurry is slaked calcium oxide and the slaking is conducted at a starting temperature of from 10 to 45°C. A paper sheet having on at least one of its surfaces a coating with a 75° gloss of from 20 to 40 percent according to TAPPI standard T480, the coating comprising the precipitated calcite of claim 1 or 2.

Inventors: VANDERHEIDEN, DENNIS BERNARD
Applicants: PFIZER INC.
Application year: 1985
Main classification: C01F11
IPC codes: C01F11, D21H21, D21H19