VANADIUM OXIDE CATALYST FOR NITROGEN OXIDE REDUCTION AND PROCESS USING THE SAME

Abstract: A catalyst composition effective for selective catalytic reduc­ tion of nitrogen oxides with ammonia in a gas stream has an upstream section comprising a phosphorus getter comprised of a phosphorus retaining material, e. g., activated alumina, and a downstream section comprising a vanadium oxide containing catalyst, e. g., a vanadia/titania catalyst. It has surprisingly been found that vanadium oxide catalysts are poisoned by phosphorus which may be contained in the form of phosphorus contaminant compounds in the gas to be treated, so that the positioning of a phosphorus-retaining material upstream of the catalyst prolongs catalyst life. In operation, the gas to be treated is passed first through the phosphorus getter upstream section of the catalyst composition and then contacted in the presence of ammonia with downstream section catalytic material.

Description: VANADIUM OXIDE CATAi#T FOR R ESN OXIDE =W=ON ffi PROCESS FOR The present invention concerns a catalyst compositio#n for reduct ion of nitrogen oxides contained in a gas stream and more particularly is concerned with a vanadium oxide catalyst which is protected against phosphorus contamination. Catalytic treatment of gas streams containing nitrogen oxides to reduce the nitrogen oxides to nitrogen are of course well known in the art, including the use of catalysts containing vanadium oxide for such purposes. Nitrogen oxides occur in various types of gas streams and must be removed or reduced to nitrogen in order to avoid emissions of noxious pollutants such as NO and NO2 and to meet various governmental regulations concerning control of emissions. Among such gas streams are the off-gas from nitric oxide production and exhaust gases from internal combustion engines such as natural gas or diesel fueled engines of the type commonly employed to drive pipeline pumps,to pressurize oil wells and the like. The prior art discloses that NH3 may be used to selectively reduce nitrogen oxides (NOx) to nitrogen and H20, in the presence of oxygen, by use of a suitable catalyst, including a vanadium containing catalyst. U.S. Patent 4,010,238 discloses a bimetallic oxide catalyst for selective removal of nitrogen oxides, the catalyst comprising vanadium and at least one element selected from copper, zinc, tin, lead, titanium, phosphorus, chromium, iron, cobalt and nickel. This patent discloses that such catalyst, while it might be composed of particles of the bimetallic oxide only, may comprise the bimetallic oxide supported on a suitable support material such as activated alumina, alpha-alumina, silica gel, aluminosilicate, diatomaceous earth, silicon carbide, titanium oxide or the like. Thus, one possible combination from the many disclosed by this patent is a vanadium-phosphorus oxide disposed on a titania support. U.S. Patent 4,233,183 is also concerned with a catalyst for selective reduction of nitrogen oxides and discloses (column 3, line 28 et seq.) as exemplary of catalytically active components for such a purpose a number of metal compounds, including vanadium compounds, used singly or in admixture. It is specifically disclosed that these metal compounds may be used conjointly with a phosphorus compound, a boron compound, an alkaline earth metal compound, or the like. The catalyst is disclosed as being supported upon a metal structure which may be configured into the form of a honeycomb structure. A binder such as an alumina sol, a silica sol, a titania sol, phosphoric acid or boric acid or the like is utilized to adhere the catalyst composition to the metal carrier structure. At column 2, line 28 et seq. of U.S. Patent 4,233,183, it is disclosed that hydrated titanias My be used in conjunction with the sol to form the binder material. U.S. Patent 3,279,884 discloses a process for selective removal of nitrogen oxides from gas mixtures containing oxygen by utilization of a vanadium oxide catalyst disposed on a suitable support material to catalyze the reaction of the nitrogen oxides with ammonia to reduce the former to nitrogen and R2 While some of the gas streams containing nitrogen oxides which are to be treated for removal or reduction of the latter contain little or no phosphorus, other such gas streams contain a considerable quantity of phosphorus compounds. For exaiple, the exhaust gases from internal co bustion engines such as the natural gas and diesel engines mentioned abode contain significant quantities of phosphorus or phosphorus corpombbs because of the normal phosphorus compound content of the engine lubricating oils used in such engines. These compounds find their way into the exhaust gas stream wherein they tend to deposit on the catalyst through which the exhaust gas is flowed for treatment to reduce the nitrogen oxides. However, as noted by the abmreaentioned prior art, it is conventional practice to utilise phosphorus compounds as a component of nitrogen oxide reduction catalysts, including those containing vanadium oxide. It therefore appears that the art has not discerned any adverse effect of phosphorus caaquzrmcas on catalysts for selective nitrogen oxides reduction, including vanadium oxide catalysts. U.S. Patent 4,134,733 discloses a catalytic converter for use in treating internal combustion engine exhaust gases wherein a noble metal catalyst such as one of the platinum group metals is dispersed on the rear section of the catalyst. The forward section of the catalyst is free of the noble metal but has a coating thereon capable of adsorbing catalyst poisons which, for the noble metal catalyst, are exemplified as including lead, phosphorus and zinc compounds. In one embodiment the catalyst comprises a honeycomb type carrier, the forward section of which contains a poison adsorbent alumina coating, and the rear section of which contains the noble metal catalyst dispersed on the alumina coating. (Forward and rear sections are as sensed in the direction of exhaust gas flow through the catalyst.) SUMMARY OF THE INVENTION It has surprisingly been found that vanadium oxide catalysts useful for the selective reduction of nitrogen oxides are poisoned by phosphorus or phosphorus compounds contained in the gas being treated, resulting in a severely shortened useful catalytic life of such catalyst compositions. In particular, vanadia-titania catalyst compositions have been found to be susceptible to such catalyst poisoning by phosphorus contaminant in the gas being treated. In accordance with the present invention there is provided a catalyst composition effective for selective catalytic reduction of nitrogen oxides with ammonia in a gas stream, the composition having an upstream section and a downstream section as sensed relative to the gas flow path through the composition, the upstream section comprising a phosphorus getter comprised of a phosphorus-retaining material, and the downstream section comprising a catalytic member comprised of a catalytic material containing a catalytically-effective amount of vanadium oxide. Other aspects of the invention provide one or more of the following features: the catalytic material further comprises a refractory metal oxide support, preferably titania; the phosphorus getter comprises a refractory carrier on which the phosphorus-retaining material is disposed and the catalytic member comprises a refractory carrier on which the catalytic material is disposed; the phosphorus-retaining material comprises alumina, preferably an activated alumina and more preferably an activated alumina having a surface area of about 10 to 400 m 2/gm or more; and the vanadium oxide comprises about 0.5 to 15%, preferably about 1 to 10%, by weight of the combined weight of the vanadium oxide and refractory metal oxide support. In accordance with another aspect of the invention, there is provided a catalyst composition effective for selective catalytic reduction of nitrogen oxides with ammonia in a gas stream, the conr position having an upstream section and a downstream section as sensed relative to the gas flow path through the composition; the upstream section comprising a phosphorus getter comprised of a refractory boneyco h-li}e carrier having a plurality of gas flow passages extending therethrough, the passages being coated with a phosphorus-retaining material; and the downstream section comprising a catalytic member comprised of a refractory honeycomb-like carrier having a plurality of gases low passages extending therethrough, the passages being coated with a catalytic material comprising a catalytically effective amount of vanedium oxide on a refractory metal oxide support. In another aspect of the invention, the catalytic material cour prises about 2 to 25%, preferably about 5 to 15Z,by weight of the weight of the boweycadb like carrier catalytic member. In yet another aspect of the invention there is provided a process of treating a gas containing phosphorus contaminant and nitrogen oxides to selectively catalytically reduce the nitrogen oxides with ammonia, comprising: (a) flowing the gas through a phosphorus getter comprising a phosphorus-retaining material to remove phosphorus contaxinant from the gas; and (b) flowing the resultant phosphorus contaiinantdepleted gas through a catalytic member comprising a catalytic material containing a catalyticallyeffective amoqint of vanadium oxide, and contacting the gas with the vanadium oxide in the presence of ammonia at a temperature sufficiently high to reduce nitrogen oxides to nitrogen by reaction with ammonia, say, at least about 2500C, e.g., about 250 to 4000C. In another aspect of the invention, step (a) above comprises flowing the gas through a phosphorus getter comprising a honeycomb like structure having a plurality of gas flow passages extending therethrough and coated with the phosphorus-retaining material, and step (b) above comprises flowing the resultant phosphorus contaminantdepleted gas through a catalytic member comprising a refractory carrier having a plurality of gas flow passages extending therethrough and coated with the catalytic material. The ammonia is preferably supplied in at least about 70%, say 70% to 110%, of the stoichiometric amount to react with all the nitrogen oxides present to reduce the latter to nitrogen. Still other aspects of the invention comprise utilizing in the process of the invention the above-described preferred catalyst compositions. BRIEF DESCRIPTION OF THE DRAWINGS Figure 1 is a schematic view in cross-section side elevation showing an embodiment of the invention in which both the upstream, phsophorus getter section and the downstream, catalytic member section comprise a honeycomb-like carrier on which phosphorusretaining material and catalytic material are respectively dispersed; and Figure 2 is another embodiment of the invention in which both the upstream, phosphorus getter section and the downstream, catalytic member section comprise beds of particulate carrier material having coated thereon phosphorus retaining material and catalytic material, respectively. DESCRIPTION OF THE PREFERRED EMBODIMENTS Generally, the catalyst compositions of the invention may comprise any suitable vanadium oxide catalyst in combination with a phosphorus getter comprising the upstream section of the catalyst so that the gas to be treated is flowed through the phosphorus getter prior to contacting the vanadium oxide catalyst. The phosphorus getter contains or comprises a phosphorus-retaining material which will remove phosphorus contaminants from the gas stream and thereby prevent the phosphorus contaminants from being deposited on the vanadium oxide catalyst. An eminently suitable class of phosphorus-retaining materials are porous, relatively high surface area materials which will tend to absorb phosphorus and phosphorus-containing compounds. For example, a suitable phosphorus-retaining material is alumina, preferably activated alumina, by which is meant alumina having a relatively high surface area, say at least 1 and preferably at least 10 square 2 2 meters per gram (m /gm), for example, 10 to 400 m Igm or more. The term activated alumina derives from the fact that such relatively high surface area aluminas, for example, ga-a alumina, display some catalytic activity for certain reactions. However, when used as a phosphorus-retaining material herein the alumina is believed to serve primarily as a physical adsorbent for the phosphorus contaminants. The relatively high surface area, high porosity and pore size distribution of conventional activated aluminas appear to suit the admirably for the purpose of adsorbing and retaining phosphorus contailnant flowed across or through the alumina. As used herein and in the claims, the term "phosphorusgetter" is intended to mean any suitable phosphorus-retaining material present in an amount sufficient to provide the desired degree of protection, i.e., sufficient phosphorus contaminant retention capacity, for the catalytic aember with which it is associated, as described in more detail below. The physical configuration of the phosphorus getter may be of any suitable type such as beads, extrudate or other shaped particles formed into a bed of particles through which the gas is flowed. Alternatively, and preferably from the point of view of reduced pressure drop and the like, the phosphorus getter may conprise a boneycomb-like structure comprising one or more monolithic bodies having a plurality of gas flow passages extending therethrough. Such structures are well known and commercially available and My comprise refractory, relatively catalytically inert metal oxide materials such as cordierite, mullite, zirconia, alpha alumina or the like materials. For example, cylindrical-shaped cordierite members having from 10 to 600 or more parallel, squarecross section, gas flow passages per square inch of face area are commercially available. The phosphorus-retaining material, say an activated alumina, may be coated upon the particulate beads or the like or deposited as a coating within the gas flow passages of the honeycomb-like structure. For example, it is well known in the art to deposit an alumina coating on a honeycomb structure by dipping the structure into an aqueous slurry of alumina particles, removing excess slurry from the honeycomb structure by blowing with compressed air, and then heating the alumina coated honeycomb in air, say at a temperature of up to 5000C or more, to calcine and adhere the alumina coating thereon to fora a high surface area, activated alumina coating. As is known in the art, the alumina coating may be stabilized against thermal degradation by the inclusion therein of stabilizing oxides such as rare earth metal oxides, say in an amount of up to about 10% or more of the combined weight of the alumina and stabilizing metal oxide. Like the phosphorus getter, the catalytic member of the invention may comprise a particulate catalyst such as beads, granules or extrudates of catalytic material. For example, titania beads or granules containing vanadium oxide thereon may be utilized as the catalytic member. Alternatively, the vanadium oxide alone or on a refractory metal oxide support such as titania, may be deposited on beads or particles of alumina or other suitable carrier material. Preferably however, for the same reasons of reduced pressure drop as mentioned above with respect to the phosphorus getter, the catalytic member comprises a honeycomb-like structure having the catalytic material coated on the gas flow passages thereof. For example, a cordierite honeycomb-like structure as described above may have a catalytic material comprising vanadium oxide on titania applied to the gas flow passages thereof in a manner generally similar to that described above with respect to the application of an alumina coating to the phosphorus getter. Titania is preferred as the refractory metal oxide support for the vanadium oxide, particularly for catalysts intended for use in treating gas streams containing sulfur or sulfur compounds, because of the known resistance of titania to poisoning by sulfur. However, the vanadium oxide may be supported on any suitable refractory metal oxide support such as, for example, an alumina support material. In such case, the catalyst composition of the invention may comprise one or more carriers, either particulate carriers or honeycomb-like structures as described above having an, e.g., alumina, coating thereon and at least the downstream section of the catalyst composition containing the vanadium oxide catalyst so that the upstream section acts as the phosphorus getter. As used herein and in the claims, reference to the "upstream section" and the "downstream section" of the catalyst composition is with reference to the direction of gas flow through the catalyst composition. That is, the gas to be treated is flowed through the "upstream section" before being flowed through the "downstream section" in order that phosphorus contaminants may be removed from the gas stream and deposit on the upstream section prior to contacting the downstrP section. The catalyst composition may comprise a monolithic and unitary honeycomb-like structure having an upstream section containing the phosphorus-retaining material and a downstream section containing the catalytic material. In such case, the catalyst will be made oversized for its intended operation to provide a "sacrificial" upstream section of the catalyst which will absorb and retain the phosphorus con tasinants, leaving the downstream section relatively free thereof to provide the desired life of catalyst operation. The upstream section will preferably be free of the vanadium oxide catalyst material in order to reduce the cost of the catalyst composition. Typically, the upstream section will comprise one or more phosphorus getters having, say, an activated alumina coating thereon as the phosphorus retaining material, and one or more downstream sections having vanadium oxide deposited on a support coating such as titania. The phosphorus getters may be separate from the catalyst member to perait removal and replacement thereof by a fresh phosphorus getter when the used one approaches its' phosphorusretaining capacity. The amount of phosphorus contaminant (or any other contaminant) deposited on a catalyst through which a contaminated gas stream is being flowed will depend on the affinity of the catalyst material for the contaminant anger the conditions of use, the quantity of contaminant contained in the gas being flowed through the catalyst and the volumetric flow rate of the gas through the catalyst. It was noted that failure of vanadium oxide on titania catalysts used for selective reduction of nitrogen oxides in a gas stream generated by a large, stationary internal combustion engine occurred nzch earlier than expected. Investigation showed that the failure, surprisingly, appeared to be caused by a heavy phosphorus loading on the catalyst, which had penetrated the entire depth of the titania coating and appeared to form a chemical compound therewith having a uniform ratio of phosphorus to titania. The source of the phosphorus was determined to be the engine lubricating oil. Analysis of engine oils in use showed from about 20 to 2000 weight parts per pillion (wpp) of phosphorus in the form of various phosphorus compounds. The adverse effect of the phosphorus on the catalyst was surprising in view of the fact that phosphorus compounds are disclosed in the art as being suitable and desirable additives to vanadium oxide catalysts utilized for selective nitrogen oxides reduction, and that performance of the catalyst was found to fail at phosphorus levels apparently within the range of art-disclosed phosphorus content of vanadium oxide catalysts. In order to obtain a desired effective life for a vanadium oxidecontaining catalyst used to treat a phosphorus contaminated gas stream, a phosphorus getter placed upstream of the catalyst should contain a sufficient quantity of phosphorus-retaining material to provide a phosphorus retention capacity equal to the phosphorus contaminant which will be introduced into catalyst during the desired effective life. Obviously, the total capacity of phosphorus retention or absorption which is required will depend on the phosphorus contamination level of the gas being treated and the volumetric flow rate of the gas through the catalyst composition, taking into consideration the retention efficiency of the phosphorus getter. As used herein and in the claims, "vanadium oxide" is intended to mean and include any vanadium oxide suitable for the intended catalytic purpose, V205 being the oxide species usually designated. The vanadium oxide catalyst may be prepared by any known means, for example, the refractory metal oxide support, e.g., the titania, may be impregnated with a solution of a soluble vanadium compound and then heated to convert the compound to vanadium oxide. Any other suitable form of preparing the catalyst may be employed. Referring now to the drawings, Figure 1 shows an embodiment of the invention in which the catalyst composition is contained within a suitable cannister 10 having an inlet section 12 and an outlet section 14 through which the gas to be treated is flowed in the direction indicated by the unnumbered arrows. The upstream section 16 comprises a phosphorus getter comprised of a honeycomb-like structure having a plurality of substantially parallel gas flow passages indicated schematically at 18. A suitable phosphorusretaining material is coated on the walls of the gas flow passages 18. The downstream section 20 of the catalyst composition comprises a catalytic member comprised of a honeycomb-like structure having a plurality of substantially parallel gas flow passages 22 extending therethrough. Upstream section 16 and downstream section 20 are retained within cannister 10 by flanged mounting rings 24, 26 and 28. Mounting ring 26 serves to space upstream section 16 from downstream section 18. it will be appreciated that upstream section 16 and downstream section 18 may be placed in abutting face-toface contact in an alternate embodiment of the invention. In another embodiment, both the upstream and downstream sections may comprise a unitary, monolithic honeycomb-like structure, the opposite ends of which are coated with, respectively, a phosphorus-retaining material to provide the upstream section and a catalytic material to provide the downstream section. Alternatively, either or both of sections 16 and 18 may comprise a plurality of individual honeycomb like structures placed in either abutting or spaced apart relationship to each other. Figure 2 shows another embodiment in which a cannister 10' has an inlet section 12' and an outlet section 14'.Gas flow through the apparatus of Figure 2 is indicated by the unnumbered arrows. Upstream section 16' and downstream section 20' each comprise cylindrical shaped enclosures filled with, respectively, a particulate phosphorus getter and a particulate catalytic me ber. Thus, upstream section 16' is formed of a cylindrical shaped sidewall 30 closed at its opposite ends by a foraminous inlet plate 32 and a foraminous outlet plate 34. A particulate phosphorus getter material 36 is enclosed within the structure. Upstream section 20' comprises a somewhat larger basket-like enclosure of similar construction defined by a cylindrical shaped sidewall 38, a foraminous inlet plate 40 and a foraminous outlet plate 42. A particulate catalytic material 44 is disposed within the structure. A series of retaining rings 24', 26' and 28' are affixed to the interior of cannister 10' to retain the upstream and downstream section structures in place within cannister 10'. Retaining ring 26' serves also to space the sections one from the other. In an alternate embodiment, the upstream and downstream sections 16', 20' may be placed in abutting contact with each other or a single basket-like enclosure may be utilized, the upstream end of which is filled with a particulate phosphorus getter material and the downstream end of which is filled with a particulate catalyst material, to form upstream and downstream sections of selected respective length. It will be apparent that in other embodiments one of the upstream and downstream sections may be comprised of a particulate material and the other may be comprised of a honeycomb-like structure having parallel gas flow passages extending therethrough. In operation, a phosphorus contaminant-containing gas to be treated is flowed into the inlet section of the devices illustrated in the drawings, in the direction shown by the unnumbered arrows, and passes therethrough, whereby phosphorus contaminant contained therein is absorbed or otherwise retained by the phosphorus-retaining material in the upstream section 16 or 16'. The phosphorus contaminant-depleted gas then passes into downstream section 20 or 20' wherein the nitrogen oxides therein are contacted with the catalytic material in the presence of ammonia which is introduced into the inlet gas, in the embodiments illustrated, at a point upstream of their entry into inlet section 12 or 12'. In other embodiments of the invention, the upstream section and downstream section may be spaced apart and provisions made for interstage introduction of the ammonia, between the upstream and downstream sections. The ammonia is usually provided in an amount sufficient to reduce enough of the nitrogen oxides content of the gas stream to nitrogen as is necessary to meet nitrogen oxides emissions standards. In order to prevent ammonia emissions, less than the stoichiometric amount of ammonia for 100% reduction of the nitrogen oxides may be utilized. For example, about 70Z to 110% of the stoichiometric amount of ammoniayforSdbbX reduction of nitrogen oxides to nitrogen may be used. The nitrogen oxides reduction is usually carried out at a temperature of about 250 to 4000C. In the Figure 1 embodiment the gas flows through parallel gas flow passages 18 and 22. In the Figure 2 embodiment the gas flows through the upstream section 16' by passing through the openings (unnumbered) in foraminous inlet plates 32, 34, 40 and 42 and through the particulate beds of, respectively, phosphorus getter material and catalytic material. While the present invention is primarily concerned with providing a phosphorus-resistant catalyst composition, the phosphorus getter forming part of the invention may well serve to protect the vanadiacontaining catalyst against other poisons. As used herein and in the claims, all references to the surface area of the phosphorus-retaining material are given in square meters per gram of the phosphorus-retaining material itself, e.g., in square meters per gram of activated alumina, and not in square meters per gram of the finished phosphorus getter. The latter basis of course gives a considerably lower value in cases where the phosphorus getter comprises a carrier material having a coating of the phosphorusretaining material thereon. The surface areas are as measured by the standard BET method (Brunnauer-Emitt-Teller). While the invention has been described in detail with respect to specific preferred eibodiments thereof, it will be appreciated that variations thereto may be devised by those skilled in the art upon a reading and understanding of the foregoing, and it is intended to include all such variations within the scope of the appended claims.

Claims: CLAIMS What is claimed is: 1. A catalyst composition effective for selective catalytic reduction of nitrogen oxides with ammonia in a gas stream, the composition having an upstream section and a downstream section as sensed relative to the gas flow path through the composition, the upstream section comprising a phosphorus getter comprised of a phosphorus-retaining material, and the downstream section comprising a catalytic member comprised of a catalytic material containing a catalytically-effective amount of vanadium oxide. 2. The composition of claim 1 wherein the catalytic material further comprises a refractory metal oxide support. 3. The composition of claim 2 wherein the phosphorus getter comprises a refractory carrier on which the phosphorus-retaining material is disposed and the catalytic member comprises a refractory carrier on which the catalytic material is disposed. 4. The composition of claim 2 wherein the refractory metal oxide support comprises titania. 5. The composition of claim 1 wherein the phosphorus-retaining material comprises alumina. 6. The composition of claim 5 wherein the alumina has a surface 2 area of about 10 to 400 m 2/gum. 7. The composition of claim 2 wherein the vanadium oxide comprises about 0.5 to 15Z by weight of the combined weight of the vanadium oxide and refractory metal oxide. 8. A catalyst composition effective for selective catalytic reduction of nitrogen oxides with ammonia in a gas stream, the composition having an upstream section and a downstream section as sensed relative to the gas flow path through the composition; the upstream section comprising a phosphorus getter comprised of a refractory honeycomb-like carrier having a plurality of gas flow passages extending therethrough, the passages being coated with a phosphorus-retaining material; and the downstream section comprising a catalytic member comprised of a refractory honeycomb-like carrier having a plurality of gas-flow passages extending therethrough, the passages being coated with a catalytic material comprising a catalytically effective amount of vanadium oxide on a refractory metal oxide support. 9 The cosposltion of claim 8 wherein the phosphorus-retaining material is activated alumina and the catalytic material contains about 0.5 to 15% by weight vanadium oxide and comprises about 2 to 25Z by weight of the catalytic member. 10. The composition of claim 9 wherein the refractory metal oxide is predominantly titania. 11. The composition of claim 9 wherein the alumina has a 2 surface area of about 10 to 400 m Igi, and the catalytic material is comprised of about 1 to lOX by weight vanadium oxide and com- prises about 5 to 15% by weight of the weight of the catalyst member. 12. A process of treating a gas containing phosphorus contaminant and nitrogen oxides to selectively catalytically reduce the nitrogen oxides with ammonia, comprising: (a) flowing the gas through a phosphorus getter comprising a phosphorus-retaining material to remove phosphorus contaminant from the gas; and (b) flowing the resultant phosphorus contaminant-depleted gas through a catalytic member comprising a catalytic material containing a catalytically-effective amount of vanadium oxide, and contacting the gas with the vanadium oxide in the presence of ammonia at a temperature sufficiently high to reduce nitrogen oxides to nitrogen by reaction with a onia. 13. The process of claim 12 wherein the gas is introduced into the catalytic member at a temperature of at least about 250 C. 14. The process of claim 13 wherein the phosphorus-retaining material comprises activated alumina and the catalytic material comprises vanadium oxide and a refractory metal oxide support. 15. The process of claim 14 wherein the catalytic material comprises about 0.5 to 15X by weight vanadium oxide on a predominantly titania support and the phosphorus-retaining material comprises alumina 2 having a surface area of about 10 to 400 m /gum. 16. The process of claim 15 wherein step (a) comprises flowing the gas through a phosphorus getter comprising a honeycomb-like structure having a plurality of gas flow passages extending there through and coated with the phosphorus-retaining material, and step (b) comprises flowing the resultant phosphorus contaminantdepleted gas through a catalytic member comprising a refractory carrier having a plurality of gas flow passages extending there through and coated with the catalytic material. 17. The process of claim 16 wherein the catalytic material comprises about 2 to 25X by weight of the weight of the catalyst member. 18. The process of claim 17 wherein the catalytic material comprises about 1 to lOX by weight vanadium oxide. 19. The process of claim 12 wherein the ammonia is present in necessary at least about 70% ofthe stoichiometric amount/to react with all of the nitrogen oxides present to reduce the latter to nitrogen. 20. The process of claim 12 wherein the gas is introduced into the catalytic member at a temperature of about 250 to 4000 C.

Inventors: FARRAUTO, ROBERT J., HECK, RONALD M., KEITH, CARL D.
Applicants: ENGELHARD CORPORATION
Application year: 1985
Main classification: B01D53
IPC codes: B01D53