IMPROVED FLAMEPROOFING COMPOSITION

Abstract: Polymer systems can be rendered flame retardant by adding a source of halogen and particles of antimony pentoxide that have been dried from colloidal dispersions that have been pH adjusted. The properties of the polymer are conserved when the pH of the colloidal dispersion is adjusted to between about 7.5 and 10 prior to drying. The pH should be adjusted with an alkaline material that forms a water-insoluble antimonate with antimony oxide.

Description: IMPROVED FIAAME'PROOFING COMPOSITION This application is related to U.S. Patents 3,860,523 and RE31214 issued on January 14, 1975, and April 19, 1983, respectively. Background of the Invention This invention relates to flame retardants of the antimony oxide type. It particularly involves improved colloidal antimony pentoxides for use in polyvinyl chloride polymers or for use with aliphatic bromine compounds added to various polymers. For many years, antimony oxide has been used in conjunction with organic chlorides, bromides and other halogen-containing materials as a coating for fabrics, textiles, plastics and the like for rendering the same flame retarding. Such compounds are described, for example, in "The Chemistry and Uses of Fire Retardants," by J.W. Lyons (Wrlley--Interscience: New York, 1970), pp. 17, 18, 21 and 79. While the reasons for the resulting flameretardant properties are not fully understood, one school of thought is that an antimony oxide halogen compound may be generated in situ, which interrupts oxidizing reactions and thus inhibits the flame. In any event, the prior art has principa;ily involved antimony oxide in the form of Sub203 and Nn pigmentary particle size, generally of the order of 1/2 to 1 micron. While these prior antimony oxide compounds have been widely used, they are subject to rather serious deficiencies and drawbacks which have just had to be tolerated. It has been found that the pigmenting characteristics of these pigment-size particles often impair the color of the dyed fabric; or, when cast, as in films, plastics and resins, producing a milky, rather than a clear cast. U.S. Patents 3,860,523 and RE31214 teach that antimony pentoxide in colloidal sol form remarkably overcomes every one of the above-described difficulties and, in addition, does so with greater efficiency, enabling the quantity of antimony required for a predetermined degree of flame-retarding to be substantially reduced below that required by pigment-grade particles. The colloidal par tides of antimony oxide can be used as colloidal dispersions in water or dried to provide powders. Either of these forms can be readily formulated into various polymer systems combined with a source of halogen to provide effective fire retardancy. The lower refractive index of 1.7 together with the small size of the colloid (20 to 1000 angstroms) compared with the large size of the powder (10-40 microns) result in low pigmenting characteristics. Summary of the Invention We have found that polymer systems that include colloidal antimony pentoxide as a fire retardant synergist exhibit minimum changes in certain important properties if the pH of said antimony pentoxide is adjusted prior to addition of the oxide to said polymer. The pH adjusted antimony pentoxide can be in the form of a colloidal dispersion in water, or a powder dried from the aqueous material. Although the benefits of these powders made from the adjusted aqueous colloidal dispersion have been shown in plastisols which are dispersions of polyvinyl chloride in plasticizers, these benefits would be applicable to many other thermoplastic and thermoset resins as well as solutions, dispersions, emulsions and suspensions of such resins. antimony oxide sols are produce & at acid pom values, and their pH is adjusted by adding specific alkaline materials. Alkalies that form insolUble antimonates appear to provide the most satisfactory results. The Invention The starting antimony oxide sol can be made by any suitable method such as colloid milling, chemical peptization or formation of colloidal sized particles in a plasma with subsequent dispersion of the particles in a suitable continuous phase. A particularly desirable cólloidaL antimony oxide dispersion can be prepared by the ion exchange method described in U.S. Patents 3,860,523 and RE31214. These patents are incorporated herein by reference. The sols produced by this method contain particulate Sb205 of colloidal size, - about 2 to about 100 nmi the continuous phase of the colloidal dispersion being 'water and the pH being below about 4. Similar sol of Sb203 can also be used. Useful sols contain about 5 to about 50% antimony oxide. The pH of the antimony oxide sÏl is adjusted to the range which produces minimum changes in the properties of the polymer systems that are formulated with our fire retardant synergist. Any inorganic or organic alkali that does not degrade or interfere with formation of the polymer can be used. We most prefer to use alkalies that produce insoluble antimonates, NaOR, Ba(OH)2, Ca(OH) 2 or mixtures thereof. The alkaline materials are used as aqueous solutions containing about 5 to about 30% wt/wt solids. Solutions of these alkalis in high polar solvents can also be used. The pH adjustment is carried out by adding the alkaline solution to the sol. The pH value desired can vary with the polymer system to betformulated with our flame retardant synergist, but a range of about 6.S to about 11 is generally useful. The antimony oxide to be used with a polyvinylchloride plastisol should be adjusted to about 7.5 to 10. We prefer about 8.5 to 10. While aqueous sols may be used with some polymer systems, other polymers require that such sols be dried to form a powder. Such a drying step may be carried out in any convenient manner such as fluid bed drying or similar methods. Any polymer system that can accommodate antimony oxide as a fire retardant synergist can benefit from our improved material, especially if the addition of such retardants leads to the degradation of some property of the polymer or other additives in the composition. Our invention is especially useful in polymer systems that involve solutions. dispersions, emulsions or suspensions of the polymer resin in a suitable continuous liquid phase. Plastisols that are dispersions of resin particles in liquids, usually plasticizers, benefit greatly from use of our antimony oxide. Various vinyl polymers can be formulated into plastisols. A plastisol of polyvinylchloride (PVC) is an excellent example of such materials and the use of pH-modified antimony oxide leads to improved heat stability when compared to use of plain antimony pentoxide. PVC formulated for extrusion or calendered coatings is also an excellent example, as is polypropylene containing ethane bisdibromo-norbornene dicarboximide. Any compound that provides at least one labile halogen at increased temperatures can be utilized as the halogen donor required with the antimony oxide of our invention Examples of useful materials include polyvinylchloride, polyvinylidene chloride, mixtures of these materials, achlorowax,afl tetrabromobisphenol A bis (2,3 dibromo propyl ether), ethane bisdibromo-norbornene dicarboximide, hexabromocyclododecane, and the like. Examples The following examples illustrate certain embodiments of our invention. These examples are not provided to establish the scope of the invention, which is described in the disclosure and recited in the claims. The proportions are in parts by weight (pbw) or percent by weight (% wt/wt) unless otherwise indicated. The antimony pentoxide sol used in these examples was prepared as described in column 4, U.S. Patent 3,860,523. The sol had the following composition and properties: Sb205(%) 17.0 pH 3.0 Viscosity cps 5.0 The plastisol composition used in these examples had the following composition: pbw Geon 121 pvc (polyvinyl chloride plastisol grade 100 resin, B.F. Goodrich) Santicizer 711 (phthalate plasticizer, Monsanto) 50 Paraplex G62 (epoxidized soybean oil, P, Hall) 8 Mark 7100 (barium, cadmium, zinc stablilizer, Argus) 2 Mark 517 (phosphite stabilizer, Argus) 1 Example l - A portion of the Sb205 sol was agitated; then sufficient NaOH solution was added to produce a pH of 7.5. This material was dried in an oven (forced air conditions) at llG C for 18 hours to produce a solid material that contained 0.52 wt/wt moisture. This dried material was ground in a Waring blender to provide a powder with a small particle size. This material (3 pbw) was combined with sufficient of the plastisol described above to provide 100 pbw of the polyvinylchloride resin. This combination was heated at 1850C (365OF) for 30 minutes. This plastisol did not darken as much as similar materials containing other antimony pentoxides. The plastisol is clear and transparent. Further, a greatly reduced level of pigment color can be used to achieve a dark shade of color compared with a plastisol containing antimony trioxide. Example 2 Three portions of the Sub 205 sol were combined with sufficient NaOH solution to provide pH values of 7.2, 8.36 and 13.4. These materials were dried and ground as described in Example 1 and then combined with the plastisol composition also as described in Example 1. These combinations and a plastisol that contained no antimony oxide were heated at 190.50C (3750F) for 30 minutes. The color of the control and the plastisol containing the Sub 05 adjusted to 8.36 pH was the same. The plastisol with the 7.2 pH Sb205 was somewhat discolored, while the plastisol with the 13.4 pH material was somewhat more discolored. Example 3 A portion of the Sb205 sol was adjusted to a pH of 8.4 with NaOH solution as previously described. This material was spray dried under conditions that produced a free-flowing powder that contained l.5 wt/wt moisture. This material was tested for heat stability as previously described at t 1930C (3800F) for 15, 30, 45 and 60 minutes. The plastisol without any antimony oxide was also tested. There was no difference; the colors devel oped by these materials indicated that both have the same heat stability. Burn tests were carried out on cotton fabric coated with the plastisol of this example and a similar plastisol containing antimony trioxide. The results indicated that the pH adjusted Sb205 is a very effective flame retardant synergist. Color samples containing 1% of a blue, red or green pigment paste had the same visual shade of color as samples containing antimony trioxide (3 phrs) and 4% of the same color pastes. Example 4 A powder was prepared as in Example 3 except that KOH was used instead of NaOH. It was found that the heat stability was poor as with a powder from a non-neutralized sol, that is, samples turned yellow to brown after 15 minutes at 193 C. Potassium antimonate is soluble, whereas sodium antimonate is insoluble in water.

Claims: Claims We claim: 1. A fire-retarding combination for synthetic organic polymer systems, said combination consisting of a source of halogen and particles of Sb205 wherein the said particles are dried from an aqueous colloidal dispersion of 5b2O5, the pH of said colloidal dispersion being adjusted to a value between about 7.5 and 10 with an alkaline material that reacts with antimony oxide to form an antimonate that is insoluble in water. 2. The combination of claim l wherein the Sb205 particles are dried from a colloidal dispersion in an organic solvent. 3. The combination of claim 1 wherein the colloid al dispersion is adjusted to a pH value between about 8.5 and 10 with a solution of NaOH, Ba(O)ar Ca(OH)2 or mixtures thereof before drying. 4. The combination of claim 1 wherein the alkaline material is NaOH, Ea(OB)2, Ca(OH)2 or mixtures thereof. 5. A flame retardant polymer that contains the tire-retarding combination of any of claims 1, 2, 3 or 4. 6. The method of forming a fire-retardant polyvinylchloride comprising the steps of: (a) preparing a plastisol of polyvinylchloride resin in a liquid plasticizer, (b) combining particles of Sb205 with said plastisol, said particles being prepared by drying an aqueous colloidal dispersion of Sub205 and a pH of about 7.5 to 10, said pH being adjusted by the addition of an alkali solution, said alkali being selected from the group that reacts with antimony oxide to form a water insoluble antimonate; and (c) heating said plastisol to induce fusion of resin. 7. The method of claim 6 wherein the colloidal dispersion of Sb205 is adjusted to a pH of 8.5 to 10 prior to drying. 8. The method of either of claims 6 or 7 wherein the pH of the colloidal dispersion of Sb205 is adjusted with NaOH, Ba(OH)2 or Ca(OH)2. 2 9. The method of forming a flame-retardant polyvinylchloride comprising the steps of: (a) preparing a plastisol of polyvinylchloride resin in a liquid plasticizer; (b) combining particles of Sb205 with said plastisol, said particles being prepared by drying an aqueous colloidal dispersion of Sb205 and a pH of 8.5 to 10, said pH being adjusted by the addition of a solu tion of NaOH1 and (c) heating said plastisol to induce fusion of the resin.

Inventors: DAVIS, STEPHEN N., KINTZ, DONALD P.
Applicants: NYACOL PRODUCTS, INC.
Application year: 1985
Main classification: C08K3
IPC codes: C09K21, C08K13, C08K5, C08K3