PRODUCTION OF POLYURETHANE-FORMING COMPONENTS HAVING FREE-ISOCYANATE OR HYDROXY GROUPS

Abstract: Polymeric materials having free hydroxyl or isocyanate groups are produced by a) polymerizing an ethylenically-unsaturated monomer to form a liquid polymer, b) combining ths liquid polymer with an active compo­ nent having hydroxyl or isocyanate groups, and c) crosslinking the liquid polymer. The resulting polyol or isocyanate prepolymer polymer product can be used in a polyurethane-forming reaction. The process enables the microstructure of the polyol or isocyan­ ate prepolymer polymer to be controlled whereby to provide better control of the properties of the polyurethane.

Description: PRODUCTION OF POLYURETHANE FORMING COMPOSITIONS HAVING FREE ISOCYANATE OR HYDROXY GROUPS The present invention relates to the production of polyols or Isocyanate prenolymers containing a separate polymer. It also relates to the production of polyureth- anes from such compositions. The polyols of the invention are sometimes referred to hereinafter as polymer polyols; the isocyanate compositions are sometimes referred to hereinafter as polymer prepolvmers. Polyurethanes constitute a broad class of polymer ic materials having a wide range of physical characteristics. The polymers are produced through the interaction of a tolyfunctional isocanate with a polvfunctional chemical coirpound having an active hydrogen in its struc ture, such as a polyester or polyether or mixtures of two or more of such materials. The materials conventionally used contain two or more hydroxyl groups and are thus generally termed polyols. In the preparation of flexible polyurethane foams, it is sometimes advantegeous to employ a method known as the quasi-prepol ,mer method where- in a portion of the polyether polyol component is reacted with an excess of isocyanate. Then in a second step the quasi-prepolymer is mixed with the balance of the polyether tolvol along with a blowing agent and catalyst to produce the nolvurethane foam. The type of quasi- prepolymer using an excess of isocyanate is referred to hereinafter as an isocyanate terminated prepolymer. It is known in the art that the addition of a high molecular weight polymer to polyurethane compositions will improve certain of the physical properties of the resultin polyurethane composition. There have been many efforts with respect to incorporating polymers into such polyurethane compositions. For example, US-R 3 383 351 discloses the in situ polymerization of an ethylenically unsaturated monomer in the presence of the polyol component of a polyurethane composition. Prior art techniques include the polymerization of ethylenically unsaturated monomers in the presence of isocyanate-terminated prepolymers to form an isocyanate-terminated polymer prepolymer. A description of this technique may be found in US-A 3 968 089. Also, the preparation of graft copolv- mer dispersions by in situ polymerization of a vinyl monomer in an unsaturated containing polyol is described, for example, in US-A 3 953 393. This invention provides a method whereby a polymer mav be formed so as to achieve a degree of freedom not found in the prior art techniaues. The present invention relates to a method of pro ducking a polvurethane-forming composition containing a cross-linked polymer obtained from an ethylenicallyunsaturated monomer, and an active component containing free hydroxyl or isocyanate groups characterized. in that the active component is mixed with a liquid polymer obtained by polymerizing the ethylenically-unsaturated monomer in a medium differing from the active component, and the liquid polymer is cross-linked in the presence of said active component. The present invention also relates to the use of the resulting compositions in the formation of polyurethanes by reaction with a polyisocvanate or a polyol respectively. The invention disclosed herein is to polymerize a monomer in a chosen medium, stop the polymerization at a chosen point and then disperse the relatively low molecular weight polymer in the active-component (e.g. a polvol or isocyanate-terminated prepolymer), and subsequently to crosslink the polymer to the desired level. By this method, the microstructure of the initial polymer can be controlled by known techniques, including a judicious choice of medium along with choice of initiators for the initial polymerization. This pre-engineered low molecular weight polymer is then dispersed in the active component and crosslinked to the appropriate level, retaining the structural characteristics built into it. The prior art which polymerizes the monomer in the active component does not allow for such engineering to be built into the polymer portion of the polymer polyol or polymer prepolymer. The monomers useful in practicing this invention are polymerizable ethylenically unsaturated monomers containing at least one polymerizable ethylenic group. The monomers can be used singly to produce a homopolymer or in combination to produce a copolymer. These monomers are well known in the art and include hydrocarbon monomers, such as butadiene, isoprene, 1,4-pentadiene, 1,6-hexadiene, 1,7-octadiene, styrene, i-methylstyrene, 2,4-dimethylstyrene, ethylstyrene, iso propylstyrene, butylstyrene, phenylstyrene, cyclohexylstyrene and benzylstyrene; substituted styrenes such as chlorostyrene, 2,5-dichlorostyrene, bromostyrene, fluorostyrene, nitrostyrene, N,N-dimethylaminostyrene, p-vinyl diphenyl sulfide and p-vinylphenyl phenyl oxide; acrylic and substituted acrylic monomers such as methyl acrylate, methyl methacrylate, cyclohexyl methacrylate, benzyl methacrylate, isopropyl methacrylate, octyl methacrylate, methacrylonitrile, methyl -chloroacrylate, ethyl ot- ethoxyacrylate, methyl 9 -acetaminoacrylate, butyl acryl- ate, 2-ethylhexyl acrylate, phenyl acrylate, phenyl methacrylate, and g-chloroacrylonitrile; ; vinyl esters and vinyl ethers, such as vinyl acetate, vinyl chloroacetate, vinyl butyrate, isopropenyl acetate, vinyl formate, vinyl acrylate, vinyl methacrylate, vinyl methoxy acetate, vinyl benzoate, vinyl naphthalene, vinyl bromide, vinyl fluoride, vinylidene bromide, l-chloro-l-fluoroethylene, vinylidene fluoride, vinyl methyl ether, vinyl ethyl ether, vinyl propyl ethers, vinyl butyl ethers, vinyl 2-ethylhexyl ether, vinyl phenyl ether, vinyl 2methoxyethyl ether, methoxybutadiene, vinyl 2-butoxyethyl ether, 3,4-dihydro-l ,2-pyran, 2-butoxy-2'-vinyloxy diethyl ether, vinyl 2-ethylmercaptoethyl ether, vinyl methyl ketone, vinyl ethyl ketone and vinyl phenyl ketone; dimethyl fumarate, dimethyl maleate, monomethyl itaconate, dimethylaminoethyl methacrylate, glycidyl acrylate, dichlorobutadiene, vinyl pyridine and hydroxyethyl methacrylate. Tne compounds listed above are illustrative and not restrictive of the monomers suitable for use in this invention. The ethylenically unsaturated monomers which are preferred in the practice of this invention include hydrocarbon monomers such as butadiene, isoprene, styrene and tQ-methylstyrene; and acrylic and substituted acrylic monomers which are noc-reactive with isocyanato groups, such as methyl acrylate, methyl methacrylate, hydroxvethyl methacrylate, acrylonitrile and methacrlonitrile. The initial polymerization or copoliinerization of these monomers to low molecular weight liquids is accomplished by a variety of techniques knom in the art. These low molecular weight polymers should generally be of molecular weights from 1,800 to 8,000. One skilled in the art may choose the method of pol > merization to provide a desired microstructure for this polymer. Free radical and cationic catalysts give polymers which are highly branched, while anionic and Ziegler-Natta- catalysts yield products which have a more linear structure. Preferred low molecular weight polymers are obtained by the anionic polymerization or copolymerization of ethylenically unsaturated monomers, the most preferred of which is butadiene. Such polymers include the LITHENE liquid polymers of butadiene from Revertex Ltd., Temple Fields, Harlow, Essex, Great Britain. As described in product data, these preferred LITHENES are prepared by the anionic polymerization of butadiene. An organic lithium catalyst is used in a solvent. Toluene is described as a usual solvent, but is only one of many solvents which can be used. By anionic pol5merization of butadiene monomer (CH2=CH-CH=CH2), three different types of structure are obtained. EMI5.1 EMI5.2 <tb> -CH-CH2-CH <tb> <SEP> 2 <tb> CH <SEP> CH <tb> <SEP> CH2 <tb> Cyclized <tb> By controlling these structures b methods known in the art, the total microstructure of the polymer can be controlled. Therefore, those skilled in the art can choose what type of polymer they wish to then further crosslink in the active component. Other types of low molecular weight liquid polymers preferred for crosslinking in a polyol are hydroxylterminated, have internal unsaturation and molecular weights from 1,800 to 8,000. For example, such polybutadiene and butadiene-ethylene copolymers include Poly bd Liquid Resins from ARCO Chemical Co., division of Atlantic-Richfield Co., which have the following published structures: EMI5.3 <tb> Homopolvmers <tb> <SEP> C <SEP> .6 <SEP> OH <tb> <SEP> /CH=CH\ <SEP> CH=CH <tb> HO <SEP> CH2--2 <SEP> CH2 <SEP> CH <SEP> 2CH2-CHCH2 <tb> <SEP> CH=CH2 <SEP> n <tb> where n = 50. Copolymers EMI5.4 where a = .75, b = .25 and n = 54. These polymers are suggested for use as a component suitable for reaction with polyisocyanates to form polyurethanes. In our invention these hydroxyl terminated polymers are suitable for cross linking in the polyol just as the non-hydroxyl terminated polymers described above. The same monomer groups useful for polvmerizing to the nonhydroxyl terminated polymers are useful for polymerizing to obtain hydroxyl terminated polymers. The method of making these materials is known in the art. In one embodiment of the invention, the isocyanate terminated polyether-based prepolyp-er composition in which the in situ polymerization of the ethylenically unsaturated monomer is effected is formed by the reaction of an organic polyisocyanate with a polyether polyol component. This results in a cor'..position in which one isocyanato group of the polyisocyanate reacts with a hydroxyl group of the polyether polyol to produce a polyether-based prepolymer composition with terminal isocyanato groups. This isocyanate-terminated polyether-based prepolymer composition will have a negligible hydroxyl number indicating that all of the available hydroxyl groups have been reacted with isocyanato groups. The polyether polyol components useful in preparing trite polymer polyol composition include polyols having a functionality of from 2 to 6 and molecular weights of from 2,000 to 10,000, preferably from 2,000 to 7,000. These polyether polyols are preparec by a well known process which involves the reaction of a polyhydric initiator such as trimethvlolpropane, glycerol, 1,2,6-hexanetriol, sorbitol or pentaerythritol, with an alkvlene oxide such as ethylene oxide, propylene oxide and butylene oxide, or mixtures of ethylene oxide with propylene oxide and/or butylene oxide. This reaction is carried out in a well known manner with an alkoxylation catalyst, generally-an alkali metal hydroxide such as potassium hydroxide. The alkoxylation reaction is continued until the product attains the desired molecular weight. Especially preferred polyether polyols are the polyether triols. Preferred polyether diols are, for example, polypropylene glycols or mzxedt polypropylene glycol/poly ethylene glycol copolymers having molecular weights from 2,000 to 5,000. These materials are produced by reacting ethylene oxide, propylene oxide, or a butylene oxide, either sequentially or in admixture with an initiator for example, ethylene glycol, propylene glycol or butylene glycol. Other preferred polyols are those made by incorporating an epoxy resin internally in te polyol. These polyols are described, for example, in US-A 4 316 91. The polyisocyanate components Which are useful in preparing the prepolymer compositions include isocyanates having two or more isocyanato groups per molecule. Examples of such isocyanates are toluene diisocyanates, such as the 2,4- and 2,-isomers; and their mixtures, methylene bis(phenylisocyanates), such as the 2,2'-, 2,4'- and 4,5'-isomers and mixtures thereof. Other representative aromatic isocyanates include l,5-naphthylene diisocyanate, phenvl diisocyanate and xylylene diisocyanate, trimethylhexametnylene diisocyanate, lysine diisocyanate methyl ester, methylene bis(cyclohexylisocyanate) and its various isomers and rixtures thereof. Mixtures of diisocyanates and polymeric isocyanates can be employed. Exemplary mixtures are described in US-S 3 362 979. Typical of the isocyanates generally used in preparation of polyurethane foams include toluene diisocyanates, and polymethylene polyphenyl polyisocyanates having a functionality of from 2.1 to 3.0. Diphenylmethane diisocyanates and various aliphatic isocyanates or any of the above-mentioned isocyanates can be suitably employed in the preparation of the isocyanate terminated polyetherbased prepolymers employed in this invention. In preparing the isocyanate-terminated polyetherbased prepolymer compositions, the polyisocyanate and the polyether polyol are combined in amounts such that there is an excess of the organic polyisocanate employed. Generally, an equivalent ratio of isocyanato groups to hydroxy groups, commonly known as the isocyanate index of from 25 to 2 is satisfactory, with an isocuanate index of from 20 to 4 being preferred. The organic olyisocyanate is generally reacted with the polyether polyol under an inert atmosphere, at an elevated reaction temperature, e.g. 500 to 1500C, with a temperature of approximately 100C being preferred, until all of the hydroxyl groups have been treated with isocyanato groups to form the prepolvmer composition. The active component and the pre-engineered low molecular eight liquid polymer are mixed together or dispersed and then further crosslink bv catalysis; for example, free radical catalysts or azo compounds. This crosslinking technique is generally carried out under the following conditions. The crosslinking of the pre-engineered liquid polymer typically takes place at 100 to 1500C, with a preferred temperature of 110 to 14O0C. The crosslinking may take place at atmospheric or near atmospheric conditions. The non-limiting ExamDles which follow will illustrate the practice of our invention. EXAMPLE 1 This example illustrates the preparation of NCO group-containing compositions of this invention. Into a l-liter three-necked flask equipped with a stirrer, thermometer, reflux condenser and nitrogen source were charged 250 g of a 5,000 molecular weight ethylene oxide/propylene oxide adduct of glycerol (THANOL SF-5505; Texaco Chemical Co.), 250 g of a polymeric isocyanate (PAPI 901; Upjohn Co.) 55.5 g of a liquid polymer of butadiene (LITHENE N4-5000; Revertex Ltd.) and 5.55 g of 2,5 dimethyl-2 , 5-di (t-butylperoxy) hexane (LUPERSOL 101; Lucidol Div., Pennwalt Corp.). Maintaining a nitrogen purge, the reaction mixture was heated at 130 to 1350C for three hours. The product was then stabilized with 0.5 g of 2,6-di-t-butyl-4-sec-butyl phenol (ISONOX 132; Schenectady Chemical Co.). The finished product was a dark, viscous liquid which had the following properties. Isocyanate content, meq/g 2.83 Equivalent weight 353.3 Viscosity, 250C, cps 16100 EXA PLE 2 This example illustrates the use of the isocyanate group-containing composition of Example 1 in the prepared tion of moisture-cured adhesives. It further shows the improved properties of adhesives made from the product as compared to one made by reaction of an equivalent weight mixture of THANOL SF-5505 polyol and PAPI 901 isocyanate for three hours at 90 C. The latter product had an isocyanate content of 3.25 meq/g (e.w. 307.6) and a viscosity of 5600 cps at 250C. To 100 g of the product of Example 1 were added 20 g of DARCO G-60 carbon black and 2.5 g of CAB-O-Sil (colloidal silica). The mixture was then thoroughly dispersed with a high shear mixer. This adhesive (A) exhibited thixotropic properties. A similar adhesive (B) made from the THANOL SF-5505/PAPI 901 prepolymer had a tendency to flow. After curing for one week at ambient conditions, adhesive A had a tensile shear (aluninum-to- aluminum as determined by ASTM-1002) of 6.254 MPa as compared to 4.678 MPa for the cured adhesive B. EXAMPLE 3 This example illustrates the use of the product of Example 1 in a flexible foam formulation. It further shows that faster curing foams with comparable properties can be prepared from this product as compared to those made from a THANOL SF-5505/PAPI 901 prepolymer. A B Formulation, pbw THANOL SF-5505 50 50 Water 1 3.0 3.0 THACAT TD-33 0.3 0.3 THASC.T D-702 0.25 0.25 NIX A-13 0.12 0.12 Polymer prepolymer4 4 Pépolymer5 - 116.9 Isocyanate index 1.05 1.05 Details of Preparation Cream time, seconds 12 12 wise time, seconds 135 150 Gel time, seconds 150 195 Properties Density, g/cm3 0.07 0.05 Tensile, MPa 0.133 0.121 Elongation, % 49 63 Tear, N/m 2.31 2.14 Compression set (Method B) 50% 11.7 8.5 75% 9.5 5.7 1338 triethylenediamine in propylene glycol; Texaco Chemical Co. 270% dimorpholinodiethyl ether/30% dimethylpiperazine; Texaco Chemical Co. 3Bis(dimethylaminoethylether); Union Carbide Chemical Corp. 4Product of Example 1, isocyanate content, meq/g 2.83. 550:50 THANOL SF-5505/PAPI 901; isocyanate content 3.25 meq/g. EXAMPLE 4 Into a l-liter three-necked flask, equipped with a stirrer, thermometer, condenser and nitrogen source were charged 320 g of a 5,500 molecular weight propylene oxide/ ethylene oxide (PO/EO) adduct of glycerol (THANOL SF-5505) 80 g of a 5,000 molecular weight butadiene liquid polymer (LITHENE N4-5000) and 4.0 g of 2,5-2irriethyl-2,5-di(t- butylperoxy)hexane (LUPERSOL 101). Maintaining a nitrogen purge, the reaction mixture was heated at 125 to 1350C for five hours. The product was then stabilized with 1.3 g of 2,6-di-t-butyl-4-sec-butyl phenol (ISONOX 132). The finished product was a white, opaque, viscous liquid which had the following properties. This polymer polyol has been stable for three months in glass. Acid number, mg KOH/g 0.01 Hydroxyl number, mg KOH/g 32.6 Water, wt, 0.01 pH, 10:6 isopropanol/water 6.8 Viscosity, 250C, cps 3720 A physical mixture of the above reactants had an initial viscosity of 1800 cps at 25 0C and phase separated within a few days. EXAMPLE 5 This example will illustrate a scale-up of the preparation according to Example 4. Into a 30 liter reactor were charged 3.63 Kg of THANOL SF-5505 polyol, 0.91 Kg of LITHENE N4-5000 and 45.4 g of LUPERSOL 101. The reactor was then evacuated and purged with pre-purified nitrogen. It was then heated at 128 to 1300C for three hours. The reaction was monitored by measuring the viscosity after each hour of reaction. Results were as follows. Time, Hour Viscosity, 25 C, cps 0 1860 1 2100 2 2100 3 2340 The product was then stabilized with 6.8 g of di-t-butylp-cresol. Basis GPC the product contained 10 area percent of a polymer which had 2-3 times the molecular weight of the starting materials. EXAMPLE 6 This example illustrates the use of the polybutadiene polymer polyol of Example 5 in the preparation of RIM elastomers. It further shows the improved hydrolytic stability and heat sag properties of elastomers prepared using these materials. These elastomers were prepared using an Accuratio machine. A B C D Formulation, pbw B-Comsonent 1 THANOL SF-55051 12.8 14.4 15.2 16.0 2 Polybutadiene polymer 3.2 1.6 0. & - Ethylene glycol 6.4t 6. 44 6.44 6.44 PLURONIC F-9R3 0.22 0.22 0.22 0.22 THANCAT DME4 0.2 0.2 0.2 0.2 Dibutyltin dilaurate5 0.015 0.015 0.015 0.015 FOMREZ UL-296 0.025 0.025 0.025 0.025 A-Comso¯ent ISONATE 143L7 29.49 29.49 29.49 29.49 Quasi-prepolymer8 5.72 5.72 5.72 5.72 Isocyanate index 1.04 1.04 1.04 1.04 Properties of Elastomer: : Hydrolytic stability, (1 week in water at room temp.) Postcure 1210C #L 0.035 0.023 0.034 0.042 tWt 0.45 0.46 0.51 0.57 Postcure 163 C aL 0.035 0.043 0.029 0.052 #W+ 0.45 0.58 0.57 0.60 Heat sag, mm (1630C/30 min) 15.25 cm overhang 11.05 14.60 16.51 19.18 Heat sag, mm (1210C/30 min) 10.2 cm overhang - 0.76 2.03 4.32 15,500 molecular weight PO/EO adduct of glycerin; Texaco Chemical Co. 2From Example 4. 311,000 molecular weight 80:20 EO/PO diol; BASF Wyandotte. 4Dimethylaminoethanol; Texaco Chemical Co. 5SUL-4; Witco Chemical Co. 6Thioorganotin Compound; Witco Chemical Co. 7Liquid MDI; Upj0hJi Chemical Co. 8Isocyanate rich quasi-prepolymer; THANATE L-55-0; Texaco Chemical Co. EXAMPLE 7 This example illustrates the use of polybutadiene polymer polyol (prepared as in Example 4) in the preparation of high resilience (HR) foams. It further shows the overall good properties of the foams. Formulation, details of preparation and properties are as follows. A Formulation, pbw THANOL SF-5505 60 Polybutadiene polymer polyol 40 Water 1 2.8 Q2-5043 siliconel 2.0 THANCAT TD-33 0.25 NIAX P--13 0.25 THANCAT DM-70- 0.25 Dibutyltin di 1 aurate 0.01 80:20 TDI/PAPI5 35.1 Isocyanate index 1.02 Details of Preparation Cream time, seconds 6 Rise time, seconds 120 Gel time, seconds 195 Properties Density, g/cm3 0.03 & Tensile, MPa 0.092 Elongation, % 119 Tear, N/m 2.28 Compression set, 50% 21.1 95% 18.2 Humid Aginq (5 hours at 1210C) Compression set, % 22.1 CLD loss, 50% 9.99 1A product of Dow-Corning Corp. 233% triethylenediamine in propylene glycol; Texaco Chemical Co. 3bis-dimethylaminoethyl ether; Union Carbide Chemical Co. 470% dimorpholinodiethyl ether/30% N,N'-dimethylpipera zine; Texaco Chemical Co. 52.7 functionality polymeric isocyanate; a product of Mobay Chemical Co. 6Compression Load Deflection. EXAMPLE 8 This example illustrates the polymerization of a hydroxyl terminated polybutadiene liquid polymer in THAtIOL SF-5505 polyol. Into a l-liter three-necked flask, equipped with a stirrer, thermometer, condenser and nitrogen source were charged 400 g of THANOL SF-5505 polyol, 100 g of hydroxy terminated polybutadiene liquid polymer (Poly bd R-45M; ARCO Chemical Co.) and 5.0 g LUPERSOL 101. At this point the reactants had a viscosity of 1340 cps at 250C. Maintaining a nitrogen purge, the reactants were heated 4.75 hours at 128-1350C. The reaction mixture was then cooled and stabilized with 0.5 g of ISONOX 132. The finished product was a white, opaque, viscous liquid which had the following properties. Acid number, mg KOH/g 0.13 Hydroxyl number, mg KOH/g 36.6 Water, wt.% 0.01 Viscosity, 250C, cps 6300 Peroxide, ppm 1.95 EXAMPLE 9 Into a l-liter three-necked flask, equipped with a stirrer, thermometer, condenser and nitrogen source were charged 400 g of a 3,500 molecular weight propylene oxide/ ethylene oxide/diglycidyl ether of Bisphenol A adduct of glycerol, 100 g of a 5,000 molecular weight butadiene liquid polymer (LITHENE N4-5000) and 5.0 g of LUPEPSOL 101. Maintaining a nitrogen purge, the reaction mixture was heated at 125 to 135 0C for three hours. The product was then stabilized with 0.75 g of di-t-butyl-p-cresol. The finished product was a white, opaque, viscous liquid which had the following properties. Hydroxyl number, m.g KOH/g 42.3 Viscosity, 250C, cps 1538 A physical mixture of the above reactants had a viscosity of 1275 cps at 25 C. EXAMPLE 10 This example will show the use of the polymer polyol of Example 9 in the preparation of flexible foam. It will further show the improved load bearing properties of foams made from this polyol as compared to those prepared from a 3,000 molecular weight propylene oxide/ ethylene oxide of glycerol (THANOL F-3016) and the base polyol of Example 9. Load bearing properties were measured using a Chatillon gauge (33% indentation). Formulations, details of preparation and foam properties are shown below. A B C D Formulation, pbw THANOL F-3016 100 - 75 3,500 m.w. polyol of Ex. 9 - 100 - 75 Butadiene polymer polyol - - 25 25 Water 1 4.0 4.0 4.0 4.0 L-6202 silicone 1.0 1.0 1.0 1.0 Stannous octoate (50% active) 0.5 0.5 0.5 0.5 THXNCAT TD-332 0.3 0.3 0.3 0.3 Toluene diisocyanate 49.7 48.4 49.7 48.2 Isocyanate index 1.05 1.05 1.05 1.05 Details of Preparation Cream time, seconds 12 12 12 12 Rise time, seconds 75 94 92 93 Properties Density, g/cm 3 0.025 0.026 0.026 0.027 Chatillon gauge (reading at 44% indentation, Kg) 2.588 2.928 2.815 3.382 1A product of Union Carbide Corp. 2Triethylenediamine in propylene glycol; a product of Texaco Chemical Co. 3Manual Slodel LIC compression tester, manufactured by John Chatillon and Sons.

Claims: CLAIMS 1. A method of producing a polyurethane-forming composition containing a cross-)inked polymer obtained from an ethylenically-unsaturated monomer, and an active component containing free hydroxyl or isocyanate groups characterised in that the active component is mixed with a liquid polymer obtained by po]ymerizing the ethylenically-unsaturated monomer in a medium differing from the active component, and the liquid polymer is cross-linked in the presence of said active component 2. A method according to claim 1 characterised in that the molecular weight of the liquid polymer has a molecular weight from 1800 to 8000. 3. A method according to claim 1 or 2 characterised in that the liquid polymer is a butadiene polymer. 4. A method according claim 3 characterised in that the butadiene polymer is a butadiene homopolymer. 5. A method according to claim 3 characterised in that the butadiene polymer is a hydroxyl-terminated butadiene-ethylene copolymer. 6. A method according to any one of claims 1. to 5 characterised in that the active component is a polyether polyol having a functionality from 2 to 6 and a molecular weight from 2000 to 10,000. 7. A method according to any one of claims 1 to 5 characterised in that the active component is a polyol modified with an epoxy resin. 8. A method according to any one of claims 1 to 4 characterised in that the active component is an isocyanate-terminated prepolymer formed by reacting an excess of polyisocyanate with a polyether polyol. 9. A method according to claim 8 characterised in that the isocyanate-terminated prepolymer is formed by reacting an excess of polyisocyanate with a polyol modified with an epoxy resin. 10. The use of polyurethane-forming- composition according to any of claims 1 to 9 in the formation of polyurethanes by reaction with a polyisocyanate or a polyol.

Inventors: CUSCURIDA, MICHAEL, DOMINGUEZ, RICHARD JOSEPH GILBERT, SPERANZA, GEORGE PHILLIP
Applicants: ARCO CHEMICAL COMPANY
Application year: 1984
Main classification: C08G18
IPC codes: C08L75, C08G18