NOVEL POLYGLYCIDYL ETHERS, THEIR PREPARATION AND THEIR USE AS THERMOSETTING COATING COMPOSITIONS

Abstract: This invention provides polyglycidyl ethers having on average n epoxy groups per molecule, where 1 < n < 2, which comprise the reaction products of multifunctional polyg­ lycidyl ethers having on average x epoxy groups per molecule, where x > 2, with (x-n) mol of monofunctional phenols per mol of the multifunctional polyglycidyl ether; a process for their preparation and their use as thermosetting coating compositions, particularly for use in electro­ deposition coating of articles.

Description: NOVEL POLYGYLCIDYL ETHERS, THEIR PREPARATION AND THEIR USE AS THERMOSETTING COATING COMPOSITIONS This invention relates to novel polyglycidyl ethers, a process for their preparation and their use as the=csetting coating compositions, particularly for use in electrodeposition coating of articles. US patent No. 4,246,089 discloses a glycidyl ether having on average less than one epoxy group per molecule, which is the reaction product of a bisphenol-A-derived diglycidyl ether and an alkyl phenol, e.g. nonyl phenol, in molar ratio in the range 1:1.1 to 1.9; and the use of such a glycidyl ether in preparing a graft copolymer based on an Acrylic-amine backbone. Such graft copolymers are disclosed as cnmpoments of thermcsetting coating compositions e.g. for electrocoating of vehicle bodies by cathodic electrodeposition. US Patent No. 4,066,525 discloses the preparation of resinous binder materials containing substantially no resiaaal epoxy groups by reaction of a bisphenol-A-derived diglycidyl ether with a phenol, e.g. nonyl phenol, or with a mixture of a phenol and an amino alcohol, e.g. diethanolamine. The resinous binder materials are used in thermosetting coating compositions for electrocoating of appliances by cathodic electrodeposition. According to the present invention there is pravided a polyglycidyl ether having on average n epoxy groups per molecule, where 1 < n < 2, which comprises the reaction product of a multifunctional polyglycidyl ether having on average x epcory groups per molecule, where x > 2, with (x-n) mol of a monofuncional phenol per mol of the multifunctional polyglycidyl ether. The multifunctional polyglycidyl ether may conveniently be a polyglycidyl ether prepared by reaction of a polyhydric phenol having a phenolic hydroxyl functionality greater than 2, with an epihalodrin, preferably epichlorohydrin, in the presence of a hydrogen halide acceptor, e.g. an alkali metal hydroxide. Examples of suitable such polyhydric phenols are novolac resins of general formula EMI2.1 wherein R represents an alkylene, e.g. CH2 group, R1 represents an alkyl group, e.g. a methyl, p-t-butyl, octyl or nonyl group, q and p are numbers having average values 0 < q < 6 and 0 < p < 2, or of general formula EMI2.2 wherein R2 represents an alkylene, e.g. CH2 group, R3 represents an alkylene, e.g. CH2 or C(CH3)2 group, a carbonyl group, an oxygen or sulphur atan and q' is a number having an average value in the range of fran 0 to 2. Other examples of suitable polyhydric polynuclear phenols are 1,1-2,2-tetra(4-hydroxyphenyl)ethane and the tetraphenol derived fran diphenolic acid having the general formula EMI3.1 4 wherein R represents the residue of a diol. Polyglycidyl ethers derived fran polyhydric phenols of formulae I, II and III are known and are described, together with processes for their preparation, in, for example, US Patent 2,844,553, Dutch Patent Application 8100830, W. German Patent Application 2,656,867 and British Patent APplication 2 001 991. Preferably the multifunctional polyglycidyl ether is an epoxy novolac resin wherein x is greater than 2 and is in the range of fran 2 to 6, and more preferably x is in the range of from 3 to 4. Advantageously the epoxy ncvolac resin is derived from a novolac of formula I wherein R is a, q is 1 to 2 and p is o to 1 or a bis-phenol novolac of formula II wherein Rê is CH2, , R3 is C(CH3)2 and q' is O. Preferably n is in the range of fran 1.3 to 2 and advantageously n may be in the range of fran 1.4 to 1.7. The monofunctional phenol may be a single phenol ar a mixture of phenols. For exarple the phenol may conveniently be phenol optionally substituted by one or more of one or more substitutentes selected from C1-16 alkyl, C3-16 alkenyl, C1-4 hydroxyalkyl, C2-13 alkoxycarbonyl and C1-16 alkoxy groups. Examples of such compounds include phenol, the cresols, salicyl alcohol, 2-allyl phenol, 2,4,6-triallyl phenol, dimethyl phenol, 4-hydroxymethyl-2,6-dimethyl phenol, 2-hydroxyphenethyl, alcohol, 4-hydroxybenzyl alcohol and ethyl 4-hydroxybenzoate. Preferably the monofunctional phenol is phenol substituted in the para-position by a C4-12 alkyl substituent. Exartples of such alkyl substituents include n-, isoand tutyI, n- and iso-octyl, n- and iso-nonyl and n- and iso-dodecyl groups. Branched alkyl substituents are particularly suitable. P-iso-octyl phenol has been found to be a very suitable monofunctional phenol. The e invention also provides a process for preparing a poly glycidyl ether of the invention which process comprises reacting the multifunctional polyglycidyl ether with the monofunctional phenol at a temperature in the range of fran 120 to 180 C in the presence of an acid or base catalyst. Preferably reaction is at a temperature in the range of fran 130 to 150 OC. The acid ar base catalyst may be, for example, a tertiary amine, a quaternary ammonium or phosphonium salt or an akali metal hydroxide or carbonate, or sulphuric acid. The tertiary amine may be for example triethanolamine, benzyl dimethylamine or 2-dimethylamino-2-methyl-1-propanol. Quaternary ammonium salts, e.g. tertiary ammonium chloride, are preferred catalysts. Tertiary amine catalysts are preferably used in amounts from 0.1 to 1%w of reactants and quaternary amrmium salts are preferably employed in amounts from 0.005 to 0.2 %w of reactants. The invention also includes uses of the polyglycidyl ethers of the invention. Those skilled in the art will appreciate that they may be used in applications which are conventional (known) uses of polyglycidyl ethers containing on average more than 1 but not more than 2 epoxy groups per molecule. However, the polyglycidyl ethers of the invention have been found to be particularly useful in the preparation of water thinnable curable binders for coatings. Accordingly the invention further provides a process for the preparation of a water-thinnable curable binder for coatings which comprises reacting a polyglycidyl ether of the invention in aqueous medium with an amino compound containing on average two amuno-hydrogen atoms per molecule or an alkali metal salt of an amino acid. This reaction is preferably carried out at a temperature in the range of fran 100 to 1200C. If desired a quantity of a known liquid or solid diglycidyl ether, such as a liquid or solid bisphenol-A-derived diglycidyl ether, e.g. "EPIKOTE 828" (registered trade mark) having an epoxy molar mass of 182 to 194 g, or "EPIKOIE 1007" (registered trade mark) having an epoxy molar mass of 1550 to 2000 g, may be included with the polyglycidyl ether of the invention in the reaction in aqueous medium in the above process for the preparation of a waterthinnable curable binder for coatings. 2-Amino-2-methyl-1-propanol is the preferred amino compound, and use thereof gives rise to curable binders which, in neutralized form, are suitable for use in cathodic electrodeposition coating. Glycine, neutralized with for example potassium hydroxide, is a preferred amino acid, and use of amino acids gives rise to curable binders which are suitable for use in anodic electrodeposition. Accordingly, the invention also comprises thermosetting coating carpositions comprising (A) a binder prepared as described in the preceding paragraphs and (B) a crosslinking compound in a weight ratio (A:B) of from 95:5 to 65:35, compound (B) having been combined with binder (A) before or after neutralization thereof. It has further been found that water-thinnable curable binders (binders C) for coating with enhanced flexibility may be obtained from the novel polyglycidyl ethers of this invention. Thereto, the invention also provides a process for the preparation of a water-thinnable curable binder (binder C) for coatings which comprises reacting together in queous medium, a novel polyglycidyl ether in accordance with this invention, a diglycidyl ether having an epoxy molar mass in the range of from 300 g to 1500 g and an amino compound containing on average two amino-hydrogen atoms per molecule, the weight ratio of the polyglycidyl ether to the diglycidyl ether being in the range 75:25 to 45: :55 and the amino compound being included in an amount sufficient to provide 1 to 1.5 amino-hydrogen atoms per epoxy group from the polyglycidyl and diglycidyl ethers. This reaction in aqueous medium is preferably carried out at a temperature of from 100 to 120 OC. The diglycidyl ether is preferably a diglycidyl ether of a dihydric phenol, e.g. a bisphenol. Conveniently the diglycidyl ether is a diglycidyl ether of 2,2-bis(4-hydroxyphenyl)propane having an epoxy molar mass in the range 300 g to 15000 g. Preferably the diglyciiyl ether has an epoxy molar mass in the range 400 g to 1100 g. Examples of very suitable diglycidyl ethers of 2,2-bis (4-hydroxyphenyl)propane include "EPIKOTE 1001" (registered trade mark) (epoxy molar mass 450 g to 500 g) and "EPIKOTE 3003" (registered trade mark) (epoxy molar mass 725 g to 825 g). The weight ratio of the novel polyglycidyl ether to the diglycidyl ether is preferably in the range 65:35 to 55:45. Very good results have been obtained when the ratio is about 60:40. The amino catpc is preferably included in an amount sufficient to provide I to 1.2, irrre preferably 1 to 1.1, amino-hydrogen atoms per epoxy group. The most preferred amino compound is 2-amino-2-methyl-1-propanol. The invention further provides aqueous thermosetting coating compositions comprising a binder (C) as described herein before and a crcss-linking compound (B) in a weight ratio C:B in the range from 95:5 to 65:35, preferably 90:10 to 70:30, more preferably 85:15 to 75:25, compound B having been combined with binder (C) before or after neutralization thereof. It has further been found that water-thinnable curable binders (binders D) for coatings with enhanced flow and low porosity may be obtained fran the novel polyglycidyl ethers of this invention. Thereto, the invention also provides a process for the preparation of an essentially epoxy-free, carboxylgroup containing waterthinnable curable binder (binder D) for coatings which comprises reacting together a novel polyglycidyl ether of this invention with a diearboxylic acid in the presence of an esterification catalyst. This reaction is preferably carried out at a temperature of from 60 to 170 OC. The dicarboxylic acid may conveniently be an aliphatic dicarboxylic acid. Examples of such compounds include succinic acid, maleic acid, glutaric acid, itaconic acid, adipic acid, pimelic acid, suberic acid, azelaic acid, sebacic acid, 1,12-dodecanedioic acid, dodecenyl succinic acid, noneyl succinic acid, dinerised fatty acid. Another class of dicarboxylic acids which may conveniently be used are those obtained by partial esterification or amidation of a polycarboxylic acid or a polycarboxylic acid anhydride. Examples of such carpounds include the monoalkylesters of trimellitic anhydride and the dialkylesters of pyromellitic anhydride, preferably these alkylesters are derived fran primary alkanols having at least 6 carbon atans. Further examples of these ester type dicarboxylic acids can e.g. be obtained by partial esterification or amidation of the reaction product of 2 insoles of trimellitic anhydride and 1 mole of an aliphatic dill. Preferred dicarboxylic acids are those having water solubility below 0.3 g/100 g water of 20 OC, Azelaic acid and sebacic acid have been found to be very suitable dicarboxylic acids. It will be appreciated by those skilled in the art that the ultimate reaction product of the reaction between the dicarboxylic acid and the polyglycidyl ether will be an essentially linear molecule. In order to be potentially water soluble or water dispersible after neutralization and further nore in order to be essentially free of epoxy groups this molecule should have on average a carboxyl group at each end and an acid value in the range of at least 20 ing KOH/g. To this end the dicarboxylic acid and the glycidyl ether ccnnads should be reacted in such amounts that there is an excess of 2 equivalents of acid over the total equivalents of epoxy. When the water-thinnable curable binder (D) is used in compositions which will be applied by an electrodeposition process, the acid value shod not be too high for process technical treasons, hence for such an application it is preferred that the acid value of the water soluble binder is in the range of fran 20 to 80 mg KOH/g. Most preferably the acid value should be in the range of fran 30 to 50 mg ROH/g. If desired a quantity of a known liquid or solid diglycidyl ether, my be included with the above polyglycidyl ether in the reaction with the dicarlic acid in the above process for preparing a water-thinnable curable binder (D). The amount of diglycidyl ether which can optionally be coreacted with the dicarboxylic acid and the polyglycidyl ether is determined by the amount of monofunctional phenol which has to be incorporatea in order to achieve the afore-mentioned improvements. Coatings with improved flow and reduced porosity can be obtained the the amount of monofunctional phenol incorporated in the ultimate water-thinnable binder (D) is in the range of fran 5 to 40 %w. Preferably the amount of monofunctional phenol is in the range of from 10 to 25 %w. In the preparation of the water-thinnable curable binder (D), reaction between aliphatic hydroxyl groups and epoxy groups or carboxyl groups should be avoided. This may be achieved by employing a tertiary amine, e.g. 2-dimethylamino-2-methyl-1-propanol, as catalyst for the reaction of epoxy groups with carboxyl groups, Tertiary amine catalysts are preferably used in amounts of from 0.1 to 1 %w of reactants. Preferably the reaction between. the dicarboxylic acid and the glycidyl ether is conducted at a temperature in the range of fran 100 to 150 OC. The invention fher provides aqueous thermosetting coating compositions carprising a binder (D) as described hereinbefore and a cross-linking compound (B) in a weight ratio D:B in the range of from 95:5 to 60:40, preferably 85:15 to 65:35, m)re preferably 85:15 to 75:25, compound (B) having been combined with binder (D) before or after neutralization thereof. The invention also specifically provides use of a thermosetting coating composition of the invention in electrodeposition of articles (anodic electrodeposition). Preferred cross-linking ccmçcurds, for addition to the binder capounde before or after neutralization, are water-soluble cross-linking agents of the aminoplast type, such as alkoxylated reaction products of formaldehyde with melamine or benzoguanamine. other cross-linking compounds include urea-formaldehyde resins, phenolformaldehyde resins, and blocked polyisocyanates. Pigments, fillers, dispersing agents, and other components knawn in the art of paint formulation may further be added. Addition of small amounts (up to 1 %w) of non-ionic surfactant may be useful for further stabilization of aqueous compositions or improvement of the wetting during application. Co-solvents, such as 2-n-butoxyethanol and, especially, 2-n-hexyloxyethanol, may advantageously be included. The water for use in the aqueous compositions is preferably purified, such as by distillation or demineralization. The water-dilutable compositions may be applied by a variety of methods known in the art, onto a variety of substrates, in particular metals such as bare steel, phosphated steel, chranate-treated steel, zinc, tin plate (for can coating), and aluminium (also e.g. for can coating), to produce cured coatings of desireable thickness, from 2 inicranetres upwards up to in general 40 micrometers. Curing can be performed by staving, for example, at temperatures of fran 150 to 220 OC, with curing times varying from 2 to 30 minutes. The thermosetting coating compositions may generally be applied by electrodeposition and other methods such as spraying or dipping, and are particularly suitable for coating cans by electrodeposition. Those skilled in the art will appreciate the need to select compounds which are approvable by regulatory authorities when food or beverage cans are to be coated. The invention will be further understood fran the following examples, in which parts and percentages are by weight, unless otherwise indicated, and various terms are defined as follows: "Multifunctional polyether I" is a semi-solid multifunctional epoxy novalac resin of average molecular weight 680 g, containing on average 3.5 epoxy groups per molecule, "Multifunctional polyether II" is a irtiltifunctional epoxy diphenylolpropane nooolac resin of average molecular weight 732 g, containing on average 3.5 epoxy groups per molecule, "Multifunctional polyether III" is a semi-solid multifunctional epoxy novolac resin of average molecular weight 665 g, containing on average 3.5 epoxy groups per molecule. "Polyether P" is a solid diglycidyl ether of 2,2-bis(4-hydrdy- phenyl)propane of epoxy molar mass 485 g, containing on average 1.85 epoxy groups per molecule. CYMEL 1141 (trade mark) is a highly alkylated melamine-formaldehyde curing resin containing methoxy and isobutoxy substituents and acidic chelating groups, 85% solids in isobutanol, AV 22#3 mg KOH/g. "AV" is acid value, expressed in mg KOH/g. "Amine value" is expressed in milli-equivalents per gram. EXAMPLE 1 Multifunctional polyether I (680 g, 1 mol, 3.5 epoxy equivalents) and p-iso-octylphenol (412 g, 2 Mol) were heated with stirring to 140 OC. When the mixture was homogeneous, a 50% aqueous solution of tetramethylammonium chloride (0.55 g) was added and the mixture was maintained at 140 C until reaction was complete (4 hours). The product was thinned with 2-n-butoxyethanol (546 g) and cooled to ambient temperature (20 C). The e resulting solution contained 66.7% solids, the desired polyether product having average molecular weight 1092 and an epoxy content of 1.37 ueq./g solids (average of 1.5 epoxy groups per molecule). EXAMPLE 2 Multifunctional polymer I (680 g, 1 mol, 3.5 epoxy equivalents) and p-iso-octylphenol (309 g, 1.5 mol) were heated with stirring to 140 OC, When the mixture was homogeneous, a 50% aqueous solution of tetramethylammonium chloride (0.55 g) was added and the mixture was maintained at 140 C for 4 hours, until reaction was complete. Dilution with 2-n-butoxyethanol (495 g) and cooling to ambient temperature gave a solution containing 66.7% solids, the desired product having average molecular weight 989 and an epoxy content of 2.02 meq./g solids (average of 2 epoxy groups per molecule). EXAMPLE 3 Multifunctional polyether II (732 g, 1 mol, 3.5 epoxy equivalents) and p-iso-octylphenol (412 g, 2 mol) were heated with stirring to 140 OC. When the mixture was hcmogeneous, a 50% aqueous solution of tetramethylammonium chloride (0.55 g) was added and the mixture was mintained at 140 C for 4 hours, until reaction was complete. Dilution with 2-n-butoxyethanol (572 g) and cooling to ambient temperature gave a solution of the desired product (solids content 66.7%), which had average inolecular weight 1144 and an epoxy content of 1.31 meg./g solids (average of 1.5 epoxy groups per molecule). EXAMPLE 4 Multifunctional polyether II (732 g, 1 idol, 3.5 epoxy equivalents) and p-isooctylpheeol (309 g, 1.5 mol) were heated with stirring to 140 OC. When the mixture was homogeneous, a 50% aqueous solution of tetramethylammonium chloride was added and the mixture was maintained at 140 C for 4 hours, until reaction was complete. The mixture was then dilution with 2-n-butoxyethanol (520 g) and the resulting solution of the desired product (solids content 66.7%) was cooled to ambient temperature, The product had average molecular weight 1041 and an epoxy content of 1.92 ireq./g solids (average of 2 epoxy groups per molecule). EXAMPLE 5 Adduct for use as cathodic electrocposition binder A 95% aqueous solution of 2-amino-2-methyl-1-prcpanol (93.7 g, 1 mol) and water (40 g) were heated with stirring to 100 OC, The resulting solution of Example 1 was added over 2 hours, with stirring, while the temperature was maintained at 100 to 110 OC. After addition was complete, the mixture was kept at 100 to 120 C with stirring for a further 8 hours, until reaction was complete (amine value 0.85, on solids). EXAMPLE 6 Adduct for use as cathodic electrodeposition binder A 95% aqueous solution of 2-amino-2-methyl-1-prcpanol (93.7 g, 1 mol) and water (40 g) were heated with stirring to 100 OC. The resulting solution of Example 3 was added over 2 hours, with stirring, while the temperature was maintained at 100 to 110 OC, The mixture was kept for a further 8 hours at 100 to 120 C with stirring, until reaction was complete (amine value 0.81, on solids). EXAMPLE 7 Adduct for use as anodic electrodeposition binder Glycine (56.25 g, 0.75 mol), water (187.5 g) and potassium hydroxide (48.5 g, 0.75 mol) were heated with stirring to 100 C. The polyether product of Example 1 (1638.55 g of a 66.7% solution in 2-n-butoxyethanol, 1 mol polyether product) was added slowly, with stirring, and the reaction mixture was stirred at 100 C for a further 4 hours. Water (941 g) was added and following acidification the precipitated product was isolated from the suspension. (AV 36.6 mg KOH/g, on solids). EXAMPLE 8 Adduct for use as anodic electrodeposition binder The e procedure of Example 7 was repeated using the polyether product of Example 3 (1717.55 g of a 66.7 % solution in 2-n-butoxyethanol, 1 riol polyether product) in place of the polyether product of Example 1. The resulting precipitated product had AV 35.1 mg KOH/g, on solids. EXAMPLES 9 and 10 Cathodic electrodeposition The adducts of Examples 5 and 6, in the form of the respective mixtures obtained in those Examples, were blended with "CYMEL 1141" in binder solids to "CMEL 1141" weight ratio 70:30, neutralized with an equivalent amount (a = 1.0) of lactic acid and thinned by gradual aiMitirm of demineralized water to a final solids content of 158. Electrodeposition was carried out by direct current for electrodeposition time of 0.1 secand at 200 V to obtain a coating with a thickness after baking of 4 to 6 m. The electrodeposition cell comprised a flat stainless steel anode and a flat exchangeable tin plate cathode which were kept 1.0 rtrn apart by means of insulating spacers. The coated area was a rectangle of 40 x 50 mm. After electrodeposition, the coated tin plates were rinsed with water and cured at 200 C for 3, 5 or 10 minutes. The e coatings were assessed visually for appearance (5: smooth, no bubbles, 4: orangepeel surface, 3: orange-peel, few bubbles, 2: many bubbles) and were evaluated for solvent resistance (number of double rubs with a methylethylketone-moistened cloth necessary to remove the coatings ("MEK rubs")) and sterilization resistance (exposure to water at 121 C for 90 minutes, assessment on a scale ranging fran 5: un- affected, to 0: very heavy blushing). Results of the above tests are given in Table I following: TABLE I EMI13.1 <tb> Example <SEP> 9 <SEP> 10 <tb> Adduct <SEP> of <SEP> Example <SEP> 5 <SEP> 6 <tb> pH <SEP> of <SEP> electrodeposition <SEP> (ED) <SEP> 3.8 <SEP> 3.6 <tb> ccmposition <SEP> <tb> specific <SEP> conductivity <SEP> of <SEP> ED <tb> composition <SEP> at <SEP> 23 C <SEP> ( S/cm) <SEP> 514 <SEP> 475 <tb> Stoving <SEP> time <SEP> (min.) <SEP> 3 <SEP> 5 <SEP> 10 <SEP> 3 <SEP> 5 <SEP> 10 <tb> Film <SEP> appearance <SEP> 5 <SEP> 5 <SEP> 5 <SEP> 5 <SEP> 5 <SEP> 5 <tb> MEK <SEP> rubs <SEP> 45 <SEP> > 100 <SEP> > 100 <SEP> 45 <SEP> > 100 <SEP> > 100 <tb> Sterilization <SEP> resistance <SEP> 5 <SEP> 5 <SEP> 5 <SEP> 5 <SEP> 5 <SEP> 5 <tb> EXAMPLES 11 and 12 Anodic electrodeposition The precipitated adducts of <RTI ID=14.1> Examples 7 and 8, were blended with hexamethoxy methyl melamine ("CYMEL 1141") in binder solids to "CYMEL 1141" weight ratio 80:20, neutralized with an equivalent amount (a = 1.0) of 2-dimethylamino-2-methyl-1-propanol and thinned by gradual additian of demineralized water to final solids content of 15% (Exairple 11) and 12% (Example 12). Electrodeposition was carried out by direct current for electrodeposition time of 0.1 second at 125 V (Example 11) and 150 V (Example 12) to obtain coatings with a thickness after baking of 4 to 6 m. The electrodeposition cell comprised a flat stainless steel cathode and a flat exchangeable tin plate anode which were kept 1.0 mm apart by means of insulating spacers. The coated area was a rectangle of 40 x 50 mn. After electrodeposition, the coated tin plates were rinsed with water and cured at 200 C for 3, 5 or 10 iflinutes. The coatings were assessed as in Examples 9 and 10. Results are given in Table II following: TABLE II EMI14.1 <tb> Example <SEP> 11 <SEP> 12 <tb> Adduct <SEP> of <SEP> Example <SEP> 7 <SEP> 8 <tb> <SEP> pH <SEP> of <SEP> ED <SEP> composition <SEP> 9.4 <SEP> 9.6 <tb> specific <SEP> conductivity <SEP> of <SEP> ED <tb> composition <SEP> at <SEP> 23 C <SEP> ( S/cm) <SEP> 650 <SEP> 380 <tb> Stoving <SEP> time <SEP> (min.) <SEP> 3 <SEP> 5 <SEP> 10 <SEP> 3 <SEP> 5 <SEP> 10 <tb> <SEP> Film <SEP> appearance <SEP> 3-4 <SEP> 3-4 <SEP> 3-4 <SEP> 3-4 <SEP> 3-4 <SEP> 3-4 <tb> <SEP> 80 <SEP> 00 <SEP> ¯ <SEP> > 100 <SEP> 1 <SEP> 28 <SEP> 1 <SEP> 40 <SEP> 60 <SEP> <tb> <SEP> Sterilization <SEP> resistance <SEP> 5 <SEP> 5 <SEP> 5 <SEP> 5 <SEP> 5 <SEP> 5 <tb> EXAMPLES 13 and 14 Can coating by cathodic electrodeposition The adduct of Example 5 (1000 g; 67% solids) was blended with "CYMEL 1141" (336 g; 85% solids) (i.e. solids weight ratio 70:30), neutralized with an equivalent amount (a = 1) of lactic acid (43 g of 90% aqueous solution) and thinned with demineralized water (4970 g) to a solids content of 17.5%. The resulting coating ccmposition had pH 3.8 and conductivity 454 x 10-6 mhos at 20 C and contained 6% co-solvent (primarily 2-n-butoxyethanol) (Example 13). A portion of the resulting composition was diluted with 2-n-butoxyethanol to a co-solvent content of 8% (Example 14). These compositions were used to coat 330 ml tin-plate cans by cathodic electrodeposition. The can formed the cathode of an electrodeposition cell, the anode being a stainless steel member inserted within the can at a substantially uniform separation of 2 millimetres fran the can. A potential difference was applied between the can and the anode, for a total tine of 240 milliseconds. After electrodeposition the coated can was vigorously rinsed with demineralized water, and the coating was cured by stoving the coated can for 3 minutes at 200 C. The coating composition of Exnrrple 13 when used at 30 C, at 180 volts gave total cured coating weight 160 mg per can, and at 200 volts gave total cured coating weight 200 mg per can, and at 20 C and at 240 volts gave total cured coating weight 133 mg per can. No trace of coating rupture was observed and the resulting cured coatings were sooth and bubble-free. The coating composition of Example 14 when used at 25 OC, at 180 volts gave total cured coating weight 190 mg per can, at 200 volts gave total cured coatings weight 220 mg per can and at 220 volts gave total cured coated weight 290 mg per can. No trace of coating rupture was observed and the resulting cured coatings were smooth and bubble-free. EXAMPLE 15 Adduct for use as cathodic electrodeposition binder A 95% aqueous solution of 1-amino-2-methyl-1-propanol (187.4 g, 2 mol), water (40 g) and 2-n-butoxyethanol (100 g) where heated with stirring to 110 OC. A liquid bi-no1-A-derived diglycidyl ether of epoxy molar mass 198 g (396 g) was aeded over 1 hour, with stirring, followed by addition aver 2 hours with stirring of a solution of polyether duct prepared as in Example 1 (1638 g; 66.7% solids). The reaction mixture was stirred at 110 C for a further 4 hours, until reaction was complete. EXAMPLE 16 and 17 Can coating by cathodic electrodeposition The adduct of Exanple 15 (1500 g) was blended with "CYMEL 1141" (529.4 g), neutralized with lactic acid (66 g) and thinned with demineralized water (7495 g), in similar manner to that of Exarrple 13. The resulting coating composition had a solids content of 15.6%, contained 5.58 co-solvent and had pH 4.7 and conductivity 758 x 10-6 mhos at 20 C (Example 16). A portion of the resulting composition was diluted with 2-n-butoxyethanol to a co-solvent content of 7.0% (Example 17). These compositions were used to coat cans by the cathodic electrodeposition process described in Examples 13 and 14. The coating composition of Example 16 when used at 21 C at 200 volts gave total cured coating weight 89 mg per can. There was no film rupture and the resulting cured coatings were smooth and bubble-free. The coating composition of Example 17 when used at 26 C at 180 volts gave total cured coating weight 106 mg per can. When this voltage was applied for a total time of 400 milliseconds total cured coating weight were in excess of 140 mg per can. In each case, there was no film rupture and the resulting cured coatings were smooth and bubble-free. EXAMPLE 18 Adduct for use as cathodic electrodeposition binder A 95% aqueous solution of 2-amino-2-methyl-1-propanol (154.6 g, 1.65 mol), water (40 g) and 2-n-butaxyethanol (100 g) were heated with stirring to 100 OC. To the resulting mixture was added a honogeneous mixture of reaction product fran aip1e 1 (1638 g; 66.7% solids; 1.5 epoxy equivalents) polyether P (727.5 g, 1.5 epoxy equivalents) and 2-n-butoxyethanol (197 g), over 2 hours, with stirring, while the temperature was maintained at 100 to 110 OC. After addition was complete, the mixture was kept at 100 to 120 C with stirring for a further 8 hours, until reaction was complete (amine value 0.84 on solids). The resulting product had a solids content of 68.8 bw. EXAMPLE 19 Adduct for use as cathodic electrodeposition binder The e procedure of Example 18 was followed, with the exception that only 147.6 g (1.575 mol) of the 95 %w aqueous solution of 2-amino-2-methyl-1-propanol was used. The resulting product had a solids content of 68.8 %w and amine value 0.80 on solids. EXAMPLE 20 The e procedure of Example 18 was followed, with the exception that 168.6 g (1.8 mol) of the 95 %w aqueous solution of 2-amino2-methyl-1-propanol was used. The resulting product had a solids content of 68.9 %w and amine value 0.91 on solids. EXAMPLE 21 Cathodic electrodepostion composition The adduct of Example 18 (321.6 g), "CYMEL 1141" (60 g) and 2-n-hexyloxyethanol (61.2 g) were mixed together at ambient temperature (20 C). The resulting homogeneous mixture was neutralized with 90 %w lactic acid in water (12.5 g, a = 0.7) and thinned with demineralized water (2267.4 g). The resulting coating composition had a solids content of 10 bw, pH 4.2 and conductivity 650 us/cm at 20 OC, EXAMPLE 22 Cathodic electrodeposition composition The adduct of Exartple 19 (804 g), "CYMEL 1141" (150 g) and 2-n-hexyloyyethanol (153 g) were mixed together at ambient temperature (20 C). The resulting homogeneous mixture was neutralized with 90 w lactic acid in water (34 g, a = 0.77) and thinned with demineralized water (3400.8 g). The resulting coating corposition had a solids content of 15 %w, pH 4.0 and conductivity 650 vs/cm at 20 OC. EXAMPLE 23 Cathodic electrodeposition composition The e adduct of Example 20 (321.6 g), "CYMEL 1141" (60 g) and 2-n-hexyloxyethanol (61.2 g) were mixed together at ambient temperature (20 C). The resulting homogeneous mixture was neutralized with 90 %w lactic acid in water (12.5 g, a = 0.62) and thinned with demineralized water (1360 g). The resulting coating composition had a solids content of 15 %w, pH 4.9 and conductivity 984 S/cm at 20 OC. EXAMPLES 24 to 26 Use of cathodic electrodeposition compositions in can coating The coating compositions of Examples 21 to 23 were used to coat 330 ml tin-plate cans by cathodic electrodeposition. The can formed the cathode of an elecrodposition cell, the anode being a stainless steel mE°ber inserted within the can at a substantially unifonti separation of 2 millirtletres fran the can. A potential difference was applied between the can and the anode, for a total time of 400 milliseconds. After electodeposition the coated can was vigorously rinsed with demineralized water, and the coating was cured by stoving the coated can for 5 or 10 minutes at 200 OC. After curing and measuring coating weight, porosity was tested by using an electrolyte solution containing a red indicator (6.2 V for 30 sec). Subsequently the cans were filled with a second clear electrolyte solution. The areas of the can not covered by the coating, becarte now red coloured. Using this method it is easy to identify pores ar other coating defects. Similar experiments a, b and c were effected with the coating coicosition of Example 13 (pH 3.8, conductivity 501 ps/cm), and with similar coating compositions based on the adducts of Examples 5 and 15 but wherein the adduct "CYMEL 1141", solids weight ratio was 80:20 instead of 70:30. Results are given in Table III following, in which solvent resistance is expressed in terms of "MEK rubs", i.e. the nutter of double rubs with a methylethylketone-moistened cloth necessary to remove the coatings, and flexibility was determined by the wedge bend test, in which coated tin-plate is bent over a 3 mn mandrel and impacted into a wedge shape, immersed in a CuSO4/HCl solution for 2 minutes, and staining, which is observed wherever breaks in the film occur, is recorded. TABLE III EMI20.1 Example <SEP> Composition <SEP> Adduct <SEP> Application <SEP> Stoving <SEP> Film <SEP> Coating <SEP> Porosity <SEP> MEK <SEP> Flexibility <tb> of <SEP> "CYMEL <SEP> 1141" <SEP> voltage <SEP> time <SEP> thickness <SEP> weight <SEP> rubs <SEP> wedge <SEP> bend <tb> Example <SEP> solids <SEP> wt. <SEP> ratio <SEP> (V) <SEP> (min) <SEP> (microns) <SEP> (mg) <SEP> (mA) <SEP> (% <SEP> failure) <tb> 5 <SEP> 5 <SEP> 216 <SEP> 0.6 <SEP> 70-80 <SEP> 20 <tb> 24 <SEP> 21 <SEP> 81.3 <SEP> : <SEP> 18.7 <SEP> 115 <SEP> 10 <SEP> 5 <SEP> 208 <SEP> 0.6 <SEP> > 100 <SEP> 26 <tb> 5 <SEP> 5 <SEP> 198 <SEP> 0.4 <SEP> 60-80 <SEP> 28 <tb> 25 <SEP> 22 <SEP> 81.3 <SEP> : <SEP> 18.7 <SEP> 110 <SEP> 10 <SEP> 5 <SEP> 194 <SEP> 0.7 <SEP> > 100 <SEP> 25 <tb> 5 <SEP> 5.5 <SEP> 250 <SEP> 0.2 <SEP> 80-90 <SEP> 20 <tb> 26 <SEP> 23 <SEP> 81.3 <SEP> : <SEP> 18.7 <SEP> 110 <SEP> 10 <SEP> 5.5 <SEP> 245 <SEP> 1.5 <SEP> > 100 <SEP> 5 <SEP> 5 <SEP> 225 <SEP> 0.5 <SEP> > 100 <SEP> 70 <tb> a <SEP> 13 <SEP> 70 <SEP> : <SEP> 30 <SEP> 110 <SEP> 10 <SEP> 5 <SEP> 209 <SEP> 0.4 <SEP> > 100 <SEP> 70 <tb> 5 <SEP> 5 <SEP> 192 <SEP> 0.2 <SEP> 14-20 <SEP> 100 <tb> b <SEP> 5 <SEP> 80 <SEP> : <SEP> 20 <SEP> 110 <SEP> 10 <SEP> 5 <SEP> 220 <SEP> 0.5 <SEP> 16-20 <SEP> 100 <tb> c <SEP> 15 <SEP> 80 <SEP> : <SEP> 20 <SEP> 110 <SEP> 10 <SEP> 5 <SEP> 200 <SEP> - <SEP> < 20 <SEP> 100 <tb> EXAMPLE 27 (a) Multifunctional polyether III (665 g, 1 mol, 3.5 epoxy equivalents) and p-(1.1.3.3-tetramethyl-butyl)phenol (309 g, 1.5 mol) were heated with stirring to 140 CC. When the mixture was homogeneous, a 50 %w aqueous solution of tetramethylammonium chloride (1 g) was added and the mixture was maintained at 140-150 C until the reaction was complete (4 hours). The e resulting product having an epoxy content of 2.05 meq./g solids (average of 2 epoxy equivalents per molecule) and a residual phenolic hydroxyl content of 0.01 meq/g solids. (b) Adduct for use as anodic electrodeposition binder Polyether P (1940 g, 4 epoxy equivalents) was added to the reaction product of step (a) and heated at 140 C until the mixture was homogeneous. Subsequently azelaic acid (752 g, 4 idol, 8 acid equivalents) and 2-dimethylamino-2-methyl-1-propanol (5 g) were added and the mixture was heated to 140-150 C with stirring and kept at this temperature for a further 6 hours, until the reaction was complete. The e resulting binder, which had an epoxy content of 0.02 meq/g solids and an acid value of 31 mg KOHIg, was allowed to cool to 120 C whereupon it was diluted with 2-n-butuyethanol (916 g), resulting in a clear viscous solution having a solids content of 80 w. The ultimate binder had an incorporated alkylphenol content of 8.4 %w. EXAMPLE 28 Adduct for use as anodic electrodeposition binder Twice the amunt of the reaction product of Example 27 (a) (i.e. 1948 g, 4 epoxy equivalents), 970 g of polyether P (2 epoxy equivalents) and 752 g azelaic acid (4 idol, 8 acid equivalents) were reacted in the presence of 2-dimethylamino-2-methyl-1-propanol following the procedure described in Example 27. 987 g of 2-n-buthoxyethanol was used to dilute the resulting binder (acid value 32 mg KOH/g), which resulted in a clear viscous solution having a solids content of 78.8 %w. The e ultimate reaction product had an incorporated alkylphenol content of 16.8 %w. EXAMPLE 29 (a) Multifunctional polyether III (665 g, 1 mol, 3.5 epoxy equivalents) and p-tetiary butyl phenol (300 g, 2 mol) were heated with stirring to 140 OC. When the mixture was homogeneous, a 50 %w aqueous solution of tetramethlammonium chloride (1 g) was added and the mixture was maintained at 140-150 C until the reaction was complete (4 hours). The resulting product having an epoxy content of 1.57 meq./g solids (average of 1.51 epoxy equivalents per molecule). (b) Addict for use as anodic electrodeposition binder The e reaction product of Example 29 (a) (965 g, 1.5 epoxy equivalents) was reacted with sebacic acid (253 g, 1.25 mol, 2.5 acid equivalents) in the presence of 2.5 g 2-dimethylamino- 2-methyl-1-propanol following the procedure described in Example 27(b). The ultimate binder (acid value 48 mg KOH/g) was diluted with 304 g of 2-n-butoxyethanol to give a clear viscous solution having a solids content of 80 %w. The incorporated alkylphenol content of the ultimate binder was 24.6 w. EXAMPLE A (comparative) Adduct for use as anodic electrodeposition binder Polyether P (1940 g, 4 epoxy equivalents) was reacted with azelaic acid (564 g, 3 irol, 6 acid equivalents) in the presence of 6 g of 2-dimethylamino-2-methyl-1-propanol under the conditions as described in Example 27(b) to arrive at a binder having an acid value of 43.8 mg KOH/g solids and no residual epoxy functionality. This product was diluted with 628 g of 2-n-butoxyethanol to arrive at a viscous solution having a solids content of 79.9 w. EXAMPLES 30-32 Anodic electrodeposition compositicn The abducts of Examples 27-29, in the form of the resective solutions in 2-n-butoxyethanol obtained in those Examples, were blended with CYMEL 1141 in binder solids to CYMEL 1141 weight ratio 70:30 and subsequently further diluted with 2-n-hexyloxyethanol, to arrive at solutions having a solids content of 76 w, neutralized with a 90% equivalent amount of 2-dimethylamino-2-methyl-1-propanol and diluted by gradual addition of demineralized water to a final solids content of 15.5 %w. EXAMPLE B (comparative) Anodic electrodeposition The e adduct of Example A, in the form of its solution in 2-n-butoxyethanol, as obtained in said Example was processed following the procedure of Examples 30-32. EXAMPLES 33-35 Use of anodic electrodeposition compositions in can coating The e coating compositions of Examples 30 to 32 were used to coat 330 ml tin-plate cans by anodic electrodeposition. The can formed the anode of an electrcdeposition cell, the cathode being a stainless steel member inserted within the can at a substantially uniform separation of 2 millimetres fran the can. A potential difference, which would result after baking in a coating weight per can in the range of 180 to 220 mg corresponding with a dry film thickness in the range of 6 to 7 urn, was applied between the can and the cathode, for a total time of 400 milliseconds. After electrodeposition the coated can was vigorously rinsed with demineralized water, and the coating was cured by stoving the coated can for 5 minutes at 200 OC. After curing and treasuring coating weight, porosity was tested by using an electrolyte solution containing a red indicator (6.2 V for 30 sec). Subsequently the cans were filled with a second clear electrolyte solution. The areas of the can not covered by the coating, became red. Using this method it is easy to identify pores or other coating defects. For comparative reasons similar experiments were conducted with the composition of Example A. Results are given in Table IV following, in which solvent resistance is expressed in terms of "MEK rubs", i.e. the number of double rubs with a methylethylketone- moistened cloth necessary to remove the coatings, while the film appearance (flaw) is expressed as a numerical rating resulting from a visual assessment (5: smooth surface, excellent flow, no defects, 4: orange-peel type surface, 3: orange-peel type surface and few rubbles and/or pinholes, 2: many bubbles and/or pinholes). The sterilisation resistance of the coatings was determined by exposure to water at 121 C for 90 minutes and rated according to a numerical scale ranging fran 5: no blushing to 0: very heavy blushing. TABLE IV EMI25.1 Example <SEP> Composition <SEP> Alkylphenol <SEP> Application <SEP> Coating <SEP> Film <SEP> Porosity <SEP> MEK <SEP> Steriliof <SEP> incorporated <SEP> voltage <SEP> weight <SEP> appearance <SEP> rubs <SEP> zation <tb> Example <SEP> (%w) <SEP> (V) <SEP> (mg) <SEP> (flow) <SEP> (mA) <SEP> resistance <tb> 33 <SEP> 30 <SEP> 8.4 <SEP> 90 <SEP> 210 <SEP> 4-5 <SEP> 1.0 <SEP> > 100 <SEP> 5 <tb> 34 <SEP> 31 <SEP> 16.8 <SEP> 100 <SEP> 215 <SEP> 5 <SEP> 0.2 <SEP> > 100 <SEP> 5 <tb> 35 <SEP> 32 <SEP> 24.6 <SEP> 100 <SEP> 205 <SEP> 5 <SEP> 0.8 <SEP> > 100 <SEP> 4-5 <tb> <SEP> B <SEP> A <SEP> 0 <SEP> 110 <SEP> 195 <SEP> 5 <SEP> 70 <SEP> > 100 <SEP> 4-5 <tb>

Claims: CLAIMS 1. A polyglycidyl ether having on average n epoxy groups per molecule, where 1 < n#2, which comprises the reaction product of a multifunctional polyglycidyl ether having on average x epoxy groups per molecule, where x > 2, with (x-n) inol of a monofunctional phenol per mol of the multifunctional polyglycidyl ether. 2. A polyglycidyl ether according to claim 1, wherein the multifunctional polyglycidyl ether is an epoxy nooolac resin wherein 3 # x ç 4. 3. A polyglycidyl ether according to claim 1 or 2, wherein 1.3 6 fl < n # 2. 4. A polyglycidyl ether according to any of claims 1 to 3, wherein the monofunctional phenol is phenol substituted in the para-position by a C412 alkyl substituent. 5. A polyglycidyl ether according to claim 1, substantially as hereinbefore described with reference to any of examples 1 to 4. 6. A process for preparing a polyglycidyl ether according to any of claims 1 to 5, which coMprises reacting the multifunctional polyglycidyl ether with the monofunctional phenol at a temperature in the range 120 to 180 C in the presence of an acid or base catalyst. 7. A process for the preparation of a water-thinnable curable binder for coatings, which comprises reacting a polyglycidyl ether according to any of claims 1 to 5, in aqueous medium with an amino compound containing on average two amino-hydrogen atoms per molecule or an alkali metal salt of an amino acid. 8. A process as claimed in claim 7, in which a diglycidylether is included in the polyglycidyl ether. 9. An aqueous thermosetting coating composition comprising (A) a binder prepared according to claim 7 or 8 and (B) a cross-linking compound in weight ratio of from 95:5 to 65:35, compound (B) having been combined with binder (A) before or after neutralization thereof. 10. A process for the preparation of a water-thinnable curable binder for coatings, which comprises reacting together in aqueous medium, the polyglycidyl ether according to any of claims 1 to 5, a digylcidyl ether having an epoxy molar mass in the range of fran 300 g to 1500 g and an amino compound containing on average two amino-hydrogen atoms per molecule, the weight ratio of the polyglycidyl ether to the diglycidyl ether being in the range of from 75:25 to 45:55 and the amino compound being included in an amount sufficient to provide 1 to 1.5 amino-hydrogen atoms per epoxy group from the polyglycidyl and diglycidyl ethers. 11. A process according to claim 10, wherein the diglycidyl ether has an epoxy molar mass in the range of from 400 g to 1100 g. 12. An aqueous thermosetting coating composition comprising (C) a binder prepared according to claim 10 or 11 and (B) a cross-linking compound in a weight ratio in the range of from 95:5 to 65:35, compound (b) having been combined with binder (C) before or after neutralization thereof. 13. A process for the preparation of an essentially epoxy-free, carboxylgrcup-containing water-thinnable curable binder for coatings which comprises reacting together in the presence of an esterification catalyst a polyglycidyl ether according to anyone of claims 1 to 5 and a dicarboxylic acid. 14. A process according to claim 13, wherein the dicarboxylic acid has a water solubility below 0.3 g/100 g water at 20 OC. 15. A process according to claim 13 or 14, wherein the dicarboxylic acid is reacted with a mixture of the polyglycidyl ether and a diglycidyl ether having an epoxy molar mass in the range of from 170 g to 1500 g. 16. A process according to any of claims 13 to 1S, wherein the water-thinnable curable binder has a content of inoorpated monofunctional phenol in the range of from 10 to 25 %w. 17. An aqueous thermosetting coating composition comprising (D) a binder prepred according to any of claims 13 to 16 and (B) a cross-linking compound in a solids ratio in the range of from 95:5 to 60:40, compound B having been combined with binder (d) before or after neutralization thereof.

Inventors: BEKOOIJ, JURRIANUS, KOOYMANS, PETRUS GERARDUS, RAUDENBUSCH, WERNER THEODOR, STACHOWIAK, STEPHEN ANTHONY
Applicants: SHELL INTERNATIONALE RESEARCH MAATSCHAPPIJ B.V.
Application year: 1984
Main classification: C08G59
IPC codes: C09D5, C09D163, C08G59