PROCESS FOR FABRICATING AN INTRAOCULAR LENS

Abstract: There are provided an improved intraocular lens, meth­ ods of fabricating the same, and methods of implantation of the intraocular lens in a human eye. The intraocular lens implant consists essentially of a hydrogel and is characterized by an index of refraction approximating the refractive index of the natural crystalline lens of the human eye. Fabrication of the intraocular lens may be effected in an open concave mold which is characterized by a sharp, well-defined peripheral mold edge. The intraocular lens can be implanted in the posterior chamber after the cataract operation, by uniquely designed devices and by unique processes.

Description: TNTRAOCULAR LEMSES, METHODS OF FABRICATING THE SAME. AMP METHODS AND APPARATUS FOR IMPLANTATION INTO THE SUMANE EYE BACKGROUND OF T INVENTION 1. Field of the Invention This invention relates to intraocular lenses of hydrogel material adapted for implantation in a human eye. 2. Discussion of the Prior Art The concept of the use of intraocular lenses for the correction of aphasia has a long history. Much of the pioneering work was performed by harold Ridley in London and by Binkhorst in the Netherlands. A comprehensive history of the development and results of the intraocular implant lens is presented by a thesis by Marcel Eugene Nordlohne and reproduced in Document Ophthalmologica, Vol. 38, Issue 1, Dec. 16, 1974. A summary of the history of various artificial lens implants is also found in an article written by D. P. Choyce, published in the Annals of Ophthalmology, October, 1973, pages lil3-1120. In most cases lenses were made from organic high polymers such as, for example, poly (methyl methacrylate). It has also been proposed to implant glass lenses and to utilize lenses made of pure silicate glass. Specific glass compositions have been proposed in the disclosure of U.S. Pat. No. 3,996,627, for example. Although glasses have certain advantages as ocular implants, they are, in most cases, of a density rendering finished lenses relatively high in weight and less than optimum in this respect as implants. An early report.by Schiferli in 1795 described an attempt by Casaamata to introduce a glass lens into the eye after a cataract operation. The lens immediately slipped back toward the fundus of the eye. Many patents are addressed to the problem of 2,834,023; the intraocular lens within the eye so that it can perform its intended function with a minimum of trauma to the eye; see for example 'J.S. Pat. Nows. mounting 3,711,870; 3,673,616; 3,866,249; 3,906,511; AND 3,913,148 Intracameral lenses, i.-e;, prosthesis for the removed natural lens, fabricated of poly(methyl methacrylate) or of many glass-like materials generally are characterized by a refractive index value which is substantially greater than the refractive index value of 1.396 of the natural crystalline lens of a human eye. For example, intraocula lenses of the poly(methyl methacrylate) type possess a refractive index in the area of 1.53. Thus, the geometry and shape of an intraocular implant lens of the poly (methyl methacrylate) type differ from that of a natural lens to enable the artificial lens immersed in the refracting medium (the aqueous humor and vitreous humor) to substantially duplicate the refraction dex characteristic of the natural lens. For example, the artificial lens is shaped with substantially smalle: curvatures of both optical surfaces than is the case with the natural lens. However, such changes in shape of the artificial lens precludes implantation in the exact position of the space occupied by the natural lens. Further disparity is noted in the specific weights of conventional material, e.g., about l.25,used in the fabrication of intraocular lenses compared with the specific weight of the natural lens (about 1.1). Thus an IOL implant of conventional material immersed in the refracting medium of the eye appears several times heavier than the natural lens. This disadvantage has been diminished by the recent practice of designing thin intracameral lenses which, however, further increases the diversity of shape between the artificial lens and the natural lens. Many adaptations have been proposed, and several actually used, to hold a miniaturized but relatively heavy intraocular lens system (body and mounting or securing means) in the desired optical zone. Pat. No. 4,073,015 discloses the mounting and securing of an intraocular lens so as to hold it in place permanently without lasting irritation to the patient. The patentees state that the lens is made of acrylic, hydrogel, or other biologically tolerable lens material and is formed with laterally extending planar flanges or haptical portions. A woven or knitted fibrous material, such as Dacron, is attached to the ouLe*- perimeter of the haptical portions and provide sites into which tissue of the iris can 13row so as to for a permanent anchor for the lens; see column 1, line 66 to column 2, line 7 of U.S. 4,073,015. The intraocular lens structure and lens mounting system (lens body, integral haptical portion, loops, etc.) is inserted into the location previously occupied by the crystalline lens by expanding the pupillary opening of the iris to admit the said sysvem; column 3, lines 56-66 of U.S. 4,073,015. It is apparent from the specification and drawings that the lens body of the patentees' intraocular lens system is significantly smaller than the natural lens of the patient's eye. SUMMARY OF THE INVENTION The present invention alleviates anchor substantially eliminates many of the problems associated with the implantation of an intraocular lens (IOL) into the general location previously occupied by tile natural crystalline lens. The IOL can be inserted into the empty spaceafter surgical extraction of the cloudy or opacified natural lens by relatively simple means. The IOL body substantially fills or occupies the chamber of the extracted natural lens thereby oftentimes substantially decreasing or even eliminating in some instances the need for lens fastening and positioning means. The IOL hydrogel material possesses or approximates many of the characteristics of a natural crystalline lens including, among other significant properties, an index of refraction value aproximatiny 1.4. The IOL can be fabricated, for example, by techniques using inexpensive open molds of predetermined diensions, The involved process proceeds smoothly and is economically attractive. Also, technically, the IOL can be shaped by means of mechanical cutting, e.g., turning, grinding and/or polishing, the generally anhydrous form of the water-swellable, waterinsoluble, highly hydrophilic material (known in the art as a xerogel which is hydratable to the hydrogel). Accordingl, it is an objecr of the invention to provide improved intraocular implant lenses of hydrogel materials which are stable, biologically inert, biocompatible with living tissue, and possessing suitable refractive indices. It is another object of the invention to provide improved processes and apparatus for fabricating intraocular lenses via simple, inexpensive mcd casting techniques. It is a further object of the invention to provide unique means for introducing hydrogel intraocular lenses into the desired chamber of a human eye. A still further object of the invetion is to provide an improved intraocular lens body having, if necessary, unique circumferential thread-like means within and proximate to the surface of the IOL body per se which serve to anchor or secure the lot body in a fixed position in a human eye. A further object of the invention is to provide a human eye with a hydrogel intraocular implant lens of hydrogel material generally located in the space formerly occupied by the removed natural lens. These and other objects will become readily apparel from a consideration of this disclosure. BRIEF DESCRIPTION OF THE DRAWINGS Figure 1 is a cross-sectional side view of concave mold 10 with curves 11, 12, 13 and 14 representing side sections through the surface of convex menisci formed by overdosing mold cavity 4 with liquid comprising polymerizable reactants. Figure 2 is a cross-sectional side view of the intraocular hydrogel lens as separated from mold 10. Curves and 2 of this view of the IOL are in agreement with the curves defined by mold cavity side section 7 and convex meniscus side section 11 (Figure 1). DETAILED DESCRIPTION nF THE INVENTION This invention pertains to a novel stable intraocular lens body of hydrogel material useful as implants for the natural crystalline lens of a human eye removed by surgical means or otherwise. The intraocular hydrogel lens body has a shape substantially defined by two rotationally symme'rical and coaxial optically finished surfaces, at least one surface being convex, e.g., doubleconvex (preferred), plano-convex, and slightly concavoconvex, provide the required focal length is obtained. In a preferred form both surfaces, e.g., double-convex, of the lens body have a continuous transition, i.e., without sharp edges or sharp line of demarcation. The intraocular lens consists essentially of a water-swellable, waterinsoluble, stable hydrogel which contains at least about 60% by weight, preferably at least about 65-70% by weight of water or physiologic saline (about 0.9% by weight saline solution) based on the total weight of the hydrogel. The iiydrogel, in osmotic equilibrium with physiologic saline, possesses an index of refraction of about 1.4, desirably from about 1.37 to about 1.45, preferably from about 1.38 to about 1.42, and preferably still from about 1.39 to about 1.41. The upper limit of water content in the hydrogel is controlled by its ability to be generally shape-retaining with sufficient mechanical strength to function as an art ficial lens body replacement for the opacified natural lens. In general, an upper water content limit of 90-95tO by weight is suitable; B5-902 by weight is desirable in various embodiments. Hydrogels made via polymerization processes are preferred, and in this respect, the concentration and starting materia±(s) of choice, e.g., mononer(s), will significantly influence the water-swellability characteristic of the resulting polymer(s). The hydrogel material, in the shape of the intraocular replant lens, is further characterized by the following properties: transparency, good optics (giving it capability to function as an lOL), biologically inert, biocompatibility with living tissue, stability in normal physiologic medium, good mechanical properties such as softness, elasticity and modulus. The hydrogel material can be derived from synthetic or natural stable materials, or modification of both types, e.g., the various types of modified collagens and other natural products, polymer ization roducts from ethylenically unsaturated polymerizable monomers, products from the condensation reaction of polyisocyanates and polyols (natural and synthetic), and the like. In a preferred form the hydrogel is a synthetically derived material. The general shape of the novel intracameral hydrogel lens approximates the general shape of the natural crystalline lens in the capsula lentils. Referring to Figure 2, the artificial lens (preferred) is characterized by a front surface 1 whose general shape resembles a flat ellipsoid having a central radius of curvature in the range of from about 7.5 to about 15 mm; a back surface 2 which is a spherical surface or a rotationally symmetrical surface of the second order, the central radius of curvature hoeing in the range of from about 5 to 8 mm; two toroidal surfaces 3 delineated by front surface 1 and back surface 2 and having the shape of a common torus; and a central lens thickness (between front surface 1 and back surface 2) of from about 2.5 to about 5mm. In one aspect of the invention suitable intraocular lenses can be fabricated from starting materials which are employed in the manufacture of so-called soft hydrophilic contact lens of high water conteat and other articles of similar hydrogel materials. Desirably the hydrogel is characterized by a relatively slightly to moderately crosslinked polymeric network and such products are well described in the literature. The operative conditions necessary to effect the appropr1°te reaction, especially the polymerization reaction, are of course well known in the art; see by way of illustrations U.S. Pat. Nos. 4,032,599; 4,067,839; 4,036,814; 4,095,877; 4,275,183 4,361,689; 4,388,436; and 4,408,023. To the extent appropriate, the foregoing patents are hereby incorporated by reference into this disclosure as if set out in full text. One of ordinary skill in the art can select the monomer or mixture of monomers of choice, including the appropriate crosslinking means, catalyst(s), solvent, and the like. Illustrative reactants include- hydrophilic monomers such as 2-hydroxyethyl methacrylate, glycidyl methacrylate, N-vinylpyrrolidone, methacrylamide, acrylamide, N-methylacrylamide, methacrylonitrile,diethylene glycol monomethacrylate, alkali metal salts of itaconic acid, of methacrylic acid, and the like. The hydrophilicity of the polymeric product can oftentimes be enhanced by using, for example, methacrylic acid as one of the monomers. -Crosslinking means include, for example, di- or polyfunctional species such ad divinylbenzens, ethylene glycol diacrylate or dimethacryate, propylene glycol diacrylate or dimethacrylate, and the polyacrylate or polymethacrylate esters of the following polyols: triethanolamine, glycerol, diethylene glycol, triethylene glycol, tetraethylene glycol, trimethylolpropane, and the like. Other crosslinking monomers can be illustrated by N,Nmethylene-bis-acrylamide or methacrylamide and sulfonated divinylbenzene. Polymerization can also be effected using, for example, radiation (U.V., X-Pcy, microwave, or other well-known forms of radiation) with/without the presence of well-known initiator(s) and/cr catalyst(s) such as the organic peroxides, the alkyl percarbonates, hydrogen peroxides, and inorganic materials such as ammonium, sodium, or potassium persulfate. Polymerization temperatures can vary from about 20 C, and lower, to about 1000C, ;nd higher. Desirably the polymerization of the ethylenically unsaturated compounds is carried out in the presence of a liquid medium and/or plasticizer and/or solvent, e,g,, water, glycerol, miscible organic liquid/ water media, and the like. Mixtures of reactants are generally preferred since hydrogels having "tailor-made" character-stics can be prepared. Mixtllrss of hydrophilic and hydrophobic rectants in appropriate concentrations cai be utilized providing the resulting polymeric product has the capability of meeting the desired water content level illustrated previously. Illustrative hydrophobic monomers include the lower alkyl methacrylates such as methyl methacrylate. The foregoing discussion is well documented in the literature, especially the body of patent literature relating to so-called soft contact lenses. In one aspect the invention is directed to a novel method of preparing the novel intraocular lenses via cast ing liquid mixture comprising lens-forming reactant(s) and other ingredients, e.g., water (preferred) and/or miscible organic liquid/water (preferred) or organic medium such as glycerol (preferred) desirably into an open concave mold. The mold is fabric- ed from any suitable material which forms with the said mixture a wetting angle greater than zero. The concave mold cavity has the shape of a sphere or rotational symmetrical surface of second order and terminates with a horizontal circular sharp edge. The liquid mixture of monomers is dosed into the mold cavity in a predetermined amount which generally exceeds (preferred) the volute of the cavity defined by the circular sharp edge. The liquid mixture does not flov over the circular edge, but forms a convex surface of the type of a flat rotational ellipsoid above the circular edge. In this manner the desired surfaces of the intraocular lens are formed in situ. In this procedure the wetting angle, as indicated above, is greater than zero. In other words, if the surface. is unwettable (e.g., Teflon#) or is not completely wetted, the liquid mixture in excess of the volume of the mold cavity does not spill over, but rather it forms the- convex menisci side sections shown as 11, '2, 13 and 14 in Figure 1. The larger the wetting angle th greater the amount of overdosing that can be tolerated. Of course, a point is reached where surface tension, adhesive forces, and other forces and attractions cannot hold the volume of liquid mixture within the bulging convex surface above the circular mold edge. A most suitable shape of the projecting meniscus of liquid mixture is achieved with dosed volumes (of liquid) which are about 10 to about 80 volume percent greater than the volume of the mold cavity per se (below sharp horizontal edge 5). An arbitrary central radius therefore can be obtained by adjustment of the amourt of liquid overdosed above the volume of the mold cavity. One embodiment of the invention, as indicated previously, includes an IOL which can have a plano and even a slightly concave front surface. In such instances the dosing of mold cavity 4 with liquid mixture may slightly exceed sharp circular mold edge 5, may be level with mold edge 5, or may even be slightly below mold edge 5, depending on the IOL optics required by the patient. The liquid mixture comprising monomer(s) after dosing is subjected to polymerization conditions,0e.g., polymerization temperature in an inert atmosphere or it is exposed to a photochemicaily effective light, if photoinitiators are used. On completion of the polymerization reaction, the molded product may be removed from the mold or the mold and product can be immersed in water where it (IOL product) is readily released from the mold after swelling. The IOL product does not require any additional mechanical treatment because its surface is optically precise and completely smooth. Ic r. eds only removal of extracteble low-molecular weight Impurities by required washings with water or aqueous alcohol and the final equilibration with physiological saline. Thereafter it can be sterilized and stored until used for the intended purpose. The intraocular lens of the invention can also be manufactured from a strongly hydrophilic material in the anhydrous or almost anhydrous statc (xerogel), by mechanical proc-ssing (turning, qrinding and polishing) to the required shape but on a reduced scale, followed by the subsequent swelling in aqueous medium of the anhydrous IOL replica to the required size. This method, being somewhat more costly (labor-intensive), is not as desirable as the casting technique described previously. In view of the soft and elastic shape retaining nature of the novel intraocular lens, the lens can be conveniently sterilized and stored, preferably in a tubular container, and thus made ready for use during primary (preferred) or secondary implantation operations. In one form the tubular container (e.g., fabricced of flexible plastic such as polyethylene) has a diameter at one end, thereof which is smaller than the diameter (thickness) of the intraocular lens. The IOL can be forced to the narrower end of a flexible, thir walled container by exerting pressure on the container to cause the IOL to become sufficiently deformed, oblong-wise, so as to be capable of exiting from the narrow pening of the container. Pressure on the container can be conveniently effected by hand pressing the container (e.g., by the ophthalmologist) to the extent necessary to cause the deformation but not the rupture or loss of integrity of the intraocular lens. in amoeba-like fashion the IOL is thus sneezed out from its container and will thereafter readily assume its original size and shape. If the internal wall of a container, conveniently a flexible container such as plastic, e.g., polyethylene or polypropylene, is hydrophilizea . by techniques known in the art, the movement of the IOL therein and its exit therefrom can be made quite facile. The intraocular lens may be fixed within the container in a manner whereby the front and back surfaces of the IO1. are indicated on the container wall. A further aspect of the invention provides a novel method of inserting the novel IOL body into the empty space created, .or example, by the surgical extraction of a turbid lens. If the rear capsula lentis has not been removed it can function as a thin natural membrane or foil which as a rule is clear and which precisely delimits the space for an artificial lens of similar size and shape. The most closel fitting intraocular lens can be generally ascertained according to the shape and volume or weight of the removed natural lens. In this respect the ophthalmologist can choose from a large stock of the novel intracameral lenses and insert the appropriate lens into the space occupied by the removed lens. If the capsula lent is is intact after the removal of the turbid lens and if the ciliary muscles proximal thereto have not degenerated, the novel IOL, being sufficiently soft and elastic and occupying the space formerly occupied by the natural lens, can be at least ,rtially deformed by the muscles (as in the functioning of a normal natural lens) thereby imparting at least partial accommodation to the eye of the patient. The hydrated IOL can be introduced into the posterior chamber of the eye (utilizing a tubular container of the principle discussed previously) as through the pupillary aperture which is smaller than the diameter of the IOL in its normal relaxed state or through any small acceptable surgical opening to the posterior chamber. In view of the capability of the intraocular leti to become temporarily deformable into amoeba-like shapes, the surgical opening for introducing the novel IOL into the empty chamber by the nove techniques illustrated previoucly can be of the order of 1 to 2 mm (and greater if required). In principle, the IOL can be inserted through the pupillary aperture in a partially or essentially dry state (since the lens dimensions are measurably smaller in such state). Such lens assumes its final dimensions after several hours in the eye by swelling to equilibrium in the surrounding viernum. In the event the IOL will not maintain its correct position in the human eye, the IOL can be provided with a thread-like mounting means such as textile fibrous material, e.g., Dacron and/or absorbable surgical material, advantageously in a ring-like arrangement about the IOL circumference. Such means should provide maximum non-interference with the optical zone of the intraocular lens. The novel casting polymerization technique can take place in the presence of, for instance, a preshaped reinforcing (e.g., thread-like or filament-shaped) structure, crimped if desired, to provide stretch and elongation characteristics, contained within the concave mold cavity proximate to the shaped edge of the mold perimeter. In its preferred form the resulting IOL lens product possesses an optical zone essentially free from interfence of the mounting means thus imbedded therein. Such mounting means can be anchored within the eye, e.g., iris, by known surgical procedures. In one embodiment the mounting means may comprise thread-iike or fine knit-like material which extends outwardly from the lens body (preferably proximal to toroidal surface 3). Such material, textile and/or absorbable suture, engage eye tissue proximal thereto, and with the passage of time an intermingling of tissue growth with the said material takes place. The non-absorabable thread-like material will be permanently engaged with the tissue growth; the absorbable thread-like material is, as expected, absorbed into the tissue body. The anchoring technique of the intraocular lens in the above manner is effective and permanent with minimum trauma to the eye However, as stated previously, it may not be necessary to secure the IOL implant by surgical means. If the IOL is proper chosen in shape and size and is properly inserted into the posterior chamber, especially in those cases where the rear surface of the capsula lent is is no; destroyed, the prognosis of a permanent IOL implant is favorable. EXAMPLES 1-4 A solution is prepared using 10 ml f 2-hydroxyethyl methacrylate, 0.03 ml of ethylene glycol dimethacrylate, 0.16 g of sodium methacrylate, and 10 m). of glycerol. To this solution there is added 0.015 g of ammonium peroxodisulfate in the form of a 25% aqueous solution as a polymerization catalyst. The resulting clear liquid is charged into the concave cavity of four separate polypropylene molds shown in Figure 1, the cavity of which is formed from a central spherical cap of a sphere radius 6 mm and width 9 mm continuously linked to a toroidal surface. The toroidal surface i formed by the rotation of a meridian circle of diameter 1 mm, the center of which is distanced from the axis 3.7 mm. The toroidal surface is terminated by a sharp circular edge of diameter 9.4 mm which delimits the sagittal depth of mold equal to 2.9 mm. The cavity volume of this mold is 134 microliters. The volume of clear polymerizable liquid separately dosed into each of the four molds was 181, 214, 247, and 278 microliters, respectively. The resulting convex menisci surfaces of the dosed molds, for convenience, are shown as 11, 12, 13, and 14 of Figure 1. The molds are maintaiaeu in X horizontal position at all times and are carefully inserted into a tunnel heated to 750C with an inert atmosphere maintained by a moderate stream of nitrogen. Practically complete conversion is achieved after 30 minutes of polymerization. The molds with gel moldings are immersed in distiiiri water at ambient temperarure for 24 hours. The leases are then released from the molds. To obtain perfect washing, the molded lenses are heated for several days to 800C in 50% aqueous isopropyl alcohol (fresh aqueous isopropyl alcohol is used daily). Similar washings are carried out with distilled water for several days and the washed lenses are eventually stored in an aqueous solution containing 0.6% NaCl and 0.43% NaHCO3 in a form ready for surgical application. The intraocular lerses made from the above stated four various doses of liquid mixture have the characteristics set out in Table I below: TABLE I ------ IOL THICKNESS CENTRAL REFRACTION REFRACTIVE DIAMETER (mm) CURVATURE (diopters)(b) INDEX (mm) (mm) (a) ----------------------------------------------------------------------------- 1 4.1 15 13 1.41 9.7 2 4.9 10 15 1.41 9.7 3 5.6 8 16.5 1.41 9.7 4 6.3 7 18 1.41 9.7 (a) Central curvature of front surface. (b) Refraction in immersion of physiologic saline. Figure 1 shows the axial sectional view in which the front surface of the four intraocular lenses corresponds to the curves defined by 11, 12, 13, and 14. If the polymerizable liquia mixture is prepared by diluting the above stated amount of monomers with a volume of glycerol other than 10 ml, there is obtained an intraocular lens having the same shape but of different size. The size differs from the original IOL size by a factor f = (0.4 + 0.04V)-1/3, wherein V is the amount of added glycerol in ml. Thus, by diluting the monomer mixture with only 7 ml of glycercl, dinie,sjons, i.e., diameter, thic'ness, and radii o¯ curvature, will be increased by the factor 1.14. O, the other hand, by diluting with 20 ml of glycerol, the IOL lenses will be contracted by the factor 0.94. Because dilution of the monomer mixture does not substantially arfect the resulting refractive index of gel, the refraction is changed so, that the above given values should be divided by,the pertinent factor f. Other lightly crosslinked hydrophilic polymers, desirably those which have a refractive index between about 1.38 and 1.44 in equilibrium with the physiologic medium, can be used similarly as the aforesaid type of gel.

Claims: CLAIMS 1. An artificial intraocular lens adapted to be implanted in the posterior chamber of a human eye which consists essentially of an intraocular lens body having a shape z istantially defined by two rotationally symmetrical and coxial optically finished surfaces, at least one surface being convex, said lens body consisting essentially of water-swellable, water-insoluble stable hydrogel arterial which contains at least about 60% by weight of water, said hydrogel material possessing an index of refraction of about 1.4. 2. The illt aocular lens of claim 1 wherein said two optically finished surfaces are convex. 3. The intraocular lens of claim 1 wherein both surfaces are characterized by a continuous transition. 4. The intraocular lens of claim 3 wherein there is embedded mounting means proximal to the toroidal surfaces thereof for anchoring said lens in a fixed position in a human eye. 5. The intraocular lens of claim 3 wherein there is embedded thread-like mounting means for anchoring said lens in a fixed position in a human eye, the optical zone of said lens being essentially free from interference of the embedded mounting means. 6. The intraocular lens of claim 3 wherein said hydrogel material is a polymer of 2-hydroxyethyl methacrylate. 7. The intraocular lens of claim 4 wherein said hydrogel material is a polymer of 2-hydroxyethyl methacrylate. 8. The intraocular lens of claim 6 wherein said hydrogel contains 60-90 by weight water and possesses an index of r±fration in the range of from about 1.38 to about 1.42. 9. A process for fabricatIng an intraocular lens of predetermined dimensions which comprises: a. introducing a liquid mixture comprising intraocular lens-forming reactants into a cavity of a mold which has a concave surface corresponding to the convex shape of one surface of the prestermind intraocular lens product, said cavity perimeter being delimited by a sharp edge; b. said liquid mixture being introduced in an amount at least sufficient to approximately reach the level of the said sharp edge perimeter of said mold; c. reacting the lens-forming reactants for a period of time sufficient to form an intraoculr lens product having at least one convex surface; d. equilibrating said intraocular lens product by repeating washings in an aqueous medium; and e. thereafter storing and maintaining the resulting predetermined intraocular lens hydrogel. characterized by at least one optically finished convex surface,-in osmotic equilibrium with physiologic solution. 10. The process of claim.9 wherein said liquid mixture comprises polymerizable ethylenically unsaturated compound. 11. The process of claim 10 wherein said liquid mixture is introduced into the cavity of the mold in a predetermined amount which exceeds the volume of said mold cavity and thereby forms above the sharp edge perimeter of the mold a convex body of said liquid mixture bounded by the said mold edge perimeter; and wherein the resulting intraocular lens hydrogel is characterized by two optically finished convex surfaces. 12. The process of claim 10 wherein said liquid mixture comprises 2-hydroxyethyl methacrylate. 13. The process of claim 10 wherein a preshaped reinforcing structure is contained within the mold cavity proximal to the sharp edge perimeter thereof, and wherein the resulting intraocular lens hydrogel contains said reinforcing structure proximal tc the optical surfaces but essentially free from interference with the optical zone of the said lens. 14. The process of claim 11 wherein a preshaped reinforcing structure is contained within the mold cavity proximal to the sharp edge perimeter thereof, and wherein the resulting intraocular lens hydrogel contains said reinforcing structure proximal to the optical surfaces but essentially freq from interference with the optical zone of the said lens. 15. An artificial intraocular lens adapted to be implanted In the posterior chamber of a human eye which consists essentially of: a. an intraocular lens body having a shape substantially defined by two rotationally symmetrical and coxial optically finished surfaces, at least one surface being convex, sad lens body consisting essentially of water-swellable, water-insoluble stable hydrogel material; b. said intraocular lens being contained in an aqueous medium and in osmotic equilibrium therewith thereby attaining its final dimensions; and c. said intraocular lens after attaining its final dimensions being characterized by: at least about 60% by weight of the aqueous medium, an index of refraction of about 1.4, good optics, biological inertness, biocompatibility with living tissue, stability in normal physiologic medium, and good mechanical properties including softness and elasticity. 16. The intraocular lens of claim 15 wherein said two optically fished surfaces are convex. 17. The intraocular lens of claim 15 wherein both surfaces are characterized by a continuous transition. 18. The intraocular lens of claim 17 wherein there is embedded mounting means proximal to the toroidal surfaces thereof f,r anchoring said lens in a fixed position in a human eye. 19. The intraocular lens of claim 17 wherein there is embedded thread-like mounting means for anchoring said lens in a fixed position in a human eye, the optical zone of said lens being essentially free from interference of the embedded mounting means. 20. The intraocular lens of claim 17 wherein said hydrogel material is a polymer of 2-hydroxyethyl methacrylate. 21. The intraocular lens of claim 20 wherein said hydrogel contains 60-90% by weight water and possesses an index refraction in the range of from about 1.38 to about 1.42. 22. The artificial intraocular lens of claim 15 in physiologic solution and in osmotic equilibrium therewith and contained in a sterilized, sealed container. 23. The container of claim 22 which is substantially tubular in shape, one closed end thereof being defined by a narrow diameter which is less than the thickness of the intraocular lens. 24. The container of claim 23 whereinthe wall of said tubular shaped container is flexible and capable of being deformed by hand pressure to the extent necessary to cause deformation but not the rupture of the intraocular lens as it is caused to exit from the container. 25. The container of claim 23 wherein the internal wall of said tubular container is hydrophilized. 26. The container of claim 24 wherein the wall of said container is fabricated from plastic material. 27. The container of claim 24 wherein the wall of said container is fabricated from polyethylene. 28 The container of claim 24 wherein the wall of said container is fabricated fro. polypropylene. 29. A method of implanting an artificial intraocular lens in a human eye as a replacent of the removed natural lens which comprises: (a) making an incision in a human eye; and (b) inserting the artificial water-swellable, waterinsoluble intr2vcular lens of claim 15 through the said incision and into the empty space formerly occupied by the natural lens; and (c) orienting said intraocular lens so that the optical zone thereof is correctly positioned for vision by the patient. 30. A method of implanting an artificial intraocular lens in a human eye as a replacement for the removed natural lens which comprises: (a) making a small incision in a human eye; (b) placing the narrow end of the tubular shaped contained of claim 23 in the incision, said narrow end being opcn to permit passage there through of said intraocular lens hydrogel contained therein; (c) applying pressure to said container sufficient to cause deformation but-not rupture of the intraocular lens whereby said lens exits from said container and into the posterior chamber of said eye; and (d) positioning said intraocular lens in said chamber so that the optical zone thereof is oriented for proper vision by the patient. 31. The method of claim 30 wherein said container is a flexible tubular container. 32. The method of claim 31 wherein said container is a flexible plastic tubular container and pressure is applied thereto by hand squeezing 33. The method of claim 31 wherein the internal wall of said container is hydrophilized to facilitate the passage of said intraocular lens trough the narrowed open end thereof. 34. The method of claim 30 wherein the capsula lent is of the eye is substantially intact and forms a membane-like s-pport for the intraocular lens. 35. The method of claim 34 wherein the ciliary muscles of the h man eye are sufficiently viable to impart at least partial accommodation to the eye of the patient. 36. The wethod of claim 30 wherein the intraocular lens positioned within a human eye is defined by claim 17.

Inventors: EICHTERLE, OTTO
Applicants: CESKOSLOVENSKA AKADEMIE VED
Application year: 1984
Main classification: A61F2
IPC codes: B29D11, A61F2