FLAME RETARDANT POLYOLEFIN COMPOSITIONS, ARTICLES, AND PROCESS OF MANUFACTURE

Abstract: Flame retardant admixtures comprising an olefinic polymer, a polyphenylene ether resin, an organic phos­ phate and a brominated compound or polymer, as well as electrical articles such as wires or cables in which cross­ linked forms of the composition are present as insulation material, are described.

Description: FLAME RETARDANT POLYOLEFIN COMPOSITIONS, ARTICLES, -AND PROCESS OF MANUFACTURE BACKGROUND OF THE INVENTION The polyphenylene ether resin and methods for their preparation are know, and moreover, described in the patent literature, including U.S. Patent Nos. 3,306,874 and 3,306,875 (Hay) and U.S. Patents Nos. 3,257,357 and 2,257,358 (Stamatoff). The polyphenylene ether resins are also known to be combinable with other polymers to form compositions which are extrudable and moldable into products characterized by outstanding properties. Cizek, in U.S. Patent No. 3,383,435 described blends of polyphenylene ether resin and polystyrene. Lee, Jr. in U.S. Patent Nos. 4,166,055 and 4,239,673 discloses blends of polyphenylene ether, polyolefin and styrene-butadiene block copolymers. As has also been disclosed previously in the patent literature, blends containing polyphenylene ether resin and styrene polymers, which are normally flammable, can be treated to impart flame retardancy by including additives for that purpose. Thus, for instance, polyphenylene etherpolystyrene compositions containing halogenated aromatic flame retardant compounds are described in U.S. Patent No. 4,203,931 (Lee, Jr); and the combined use of an aromatic phosphate compound and a halogenated aromatic compound to improve the flame resistance of polyphenylene ether-polystyrene blends is proposed in U.S. Patent No. 4,355,126 (Haaf, et al.). SUMMARY OF THE INVENTION This invention comprises, in one aspect, a flame retardant composition which is an admixture of (a) an olefinic polymer and (b) a flame retardant combination of (i) a polyphenylene ether resin, (ii) an organic phosphate, and (iii) a stable brominated material. Another aspect of the invention comprises articles formed in whole or in part from the composition, including electrically conductive articles, for example, wires and cables, in which the composition is employed as an insulation material. Still another facet of the invention comprises a process for forming the above mentioned electrically conductive articles. The compositions described are normally thermoplastic and can be shaped by conventional thermal means such as extrusion or molding. The compositions are also radiation curable provided a crosslinkable polyolefin, for example, polyethylene, is used; curing can be accomplished by exposure to high energy electrons of a sufficient strength to cause crosslinking. In other embodiments, a heat activatable cross-linking agent can be included to make the composition heat curable, and curing can be accomplished by exposure of the composition to elevated temperatures. DESCRIPTION OF THE INVENTION The invention in its various aspects is advantageously practiced with use of certain preferred materials, which are described below. The polyolefins which are suitable for use in the pratice of this invention as component (a) are preferably selected from among homopolymers based on olefines containing from 2 to 10 carbon atoms, that is, a C2 to C10 olefin, and especially preferably, a C2 to C5 olefin, for example, polyethylene, polypropylene, polybutane. Methods of preparation for these polymeric materials are know. A useful reference is the ENCYCLOPEDIA OF POLYMER SCIENCE AND TECHNOLOGY, John Wiley and Sons, Inc. (1965-1969). The pertinent sections are set forth in volume 6, pages 275-286 and 332-338 (polyethylene); volume 11, pages 597-606 (polypropylene); volume 2, pages 759-761 (polybutylene); and volume 9, pages 440-449 (polymers derived from higher olefins, such as 3-methyl-l-butene; 1-pentene; 4-methyl-l-pentene; and 1-hexene). These teachings are incorporated herein by reference. The polyphenylene ether resin, component (b) (i) of the flame retardant combination, is preferably a hom copolymer having units of the formula EMI3.1 wherein Q, Q', Q" and Q"', are independently selected from the group consisting of hydrogen, halogen, hydrocarbon radicals, halohydrocarbon radicals, hydrocarbonoxy radicals, and halohydrocarbonoxy radicals; and n represents the total number of monomer units and is an integer at least about 20, and preferably at least 50. In general, the polyphenylene ether resins are self-condensation products of monohydric monocyclic phenols produced by reacting the phenols with oxygen in the presence of complex metal catalysts, with molecular weight being controlled by reaction time, longer times providing a higher average number of repeating units. Particular procedures are known to those skilled in the art and are described in the patent literature, including U.S. Patent Nos. 3,306,874 and 3,306,875 (to Allan Hay), and U.S. Patent Nos. 3,257,357 and 3,257,358 (to Gelu Stamatoff). Illustrative polymers which can be produced by such procedures and which are within the above general formula are poly(2,6-dilauryl-l,4-phenylene)ether;poly- (2,6-diphenyl-1,4-phenylene)ether; poly(2,6-dimethoxyl,4phenylene)ether; poly(2,6-diethoxy-1,4-phenylene)- ether; poly(2-methoxy-6-ethoxy-1,4-phenylene)ether; poly- (2-ethyl6-stearyloxy-1,4-phenylene)ether; poly( 2, 6-di-chloro-l ,4- phenylene)ether; poly(2-methyl-6-phenyl-1,4-phenylene)ether; poly(2,6-dibenzyl-l,4-phenylene)ether; poly- (2-ethoxy-1,4phenylene)ether; poly(2-chloro-1,4-phenylene)ether; poly (2,6-dibromo-1,4-phenylene)ether; and the like Also included are polyphenylene ether copolymers, such as copolymers of 2,6-dimethylphenol with other phenols, for example, with 2,3,6-trimethylphenol or 2-methyl-S-butyl- phenol, etc. For purposes of the present invention, an especially preferred family of polyphenylene ethers include those having an alkyl substitution in the two positions ortho to the oxygen ether atom, i.e., those of the above formula wherein Q and Q' are alkyl, most preferably having from 1 to 4 carbon atoms. Illustrative members of this class are: poly(2,6-dimethyl-l,4-phenylene)ether; poly(2,6-diethyl-1,4-phenylene)ether; poly(2-methyl-6-ethyl-1,4-phenylene)ether; poly(2-methyl-6-propyl-1,4-phenylene)ether; poly(2,6-dipropyl-l,4-phenylene)ether; poly( 2-ethyl-6-propyl-l , 4-phenylene)ether; and the like The most preferred polyphenylene ether resin for purposes of the present invention is poly(2,6-dimethyl-l,4phenylene)ether. The organic phosphate, component (b) (ii) of the flame retardant combination, is preferably an aromatic phosphate compound of the formula EMI5.1 where R is the same or different and is alkyl, cycloalkyl, aryl, alkyl substituted aryl, halogen substituted aryl, aryl substituted alkyl, halogen, or a combination of any of the foregoing, provided at least on R is aryl. Examples include phenyl bisdodecyl phosphate, phenylbisneopentyl phosphate, phenyl-bis(3,5,5'-tri-methylhexyl phosphate), ethyldiphenyl phosphate,2-ethyl-hexyldi (p-tolyl) phosphate, bis-(2-thylhexyl)p-tolylphosphate, tritolyl phosphate, bis-(2-ethylhexyl)phenyl phosphate, tri (nonylphenyl)phosphate,di(dodecyl)p-tolyl phosphate, tricresyl phosphate, triphenyl phosphate, dibutylphenyl phosphate, 2-chloroethyldiphenyl phosphate, p-tolyl bis (2,5,5'-trimethylhexyl)phosphate, 2-ethylhexyldiphenyl phosphate, and the like. The preferred phosphates are those in which each R is aryl. Especially preferred is triphenyl phosphate, which may be either unsubstituted or substituted, for example, isopropylated triphenyl phosphate. Alternatively, the organic phosphate can be a di or polyfunctional compound or polymer having the formula EMI5.2 EMI6.1 including mixtures thereof, in which R1, R3 and R5 are, independently, hydrocarbon; R2, R4, R6 and R7 are, independently, hydrocarbon or hydrocarbonoxy; X1, X2 and X3 are halogen; m and r are 0 or integers from 1 to 4, and n and p are integers from 1 to 30. Examples include the bis diphenyl phosphates of resorcinol, hydroquinone and bisphenol-A, respectively, or their polymeric counterparts. Methods for the preparation of the afore-mentioned di- and polyfunctional aromatic phosphates are described in British Patent No. 2,043,083. Component (b) (iii) of the flame retardant combination is a brominated compound, or oligomer or polymer which is reasonably stable at elevated temperatures, particularly those above 100"C and, moreover, preferably relatively nonvolatile at about 100"C. In the preferred embodiments, component (b) (iii) is a bis phenoxy alkane compound of the formula EMI6.2 where R' is alkylene, straight or branched, having from 1 to 10 carbon atoms, and more preferably from 1 to about 6 carbon atoms; and q and s represent the total number of bromine atoms on each ring and are independently integers from 1 to 5. Examples are 1,2-bis(2,4,6,-tribromophenoxy)ethane; 1,3-bis(2,4,6-tribromophenoxy)propane; 1,4-bis(2,4,6-tribromophenoxy)butane; and 2, 2-bis(4-brornophenoxy)propane Preferred are 1,2-bis(2,4,4-tribromophenoxy)ethane and 1,2 -bis(2,3,4,5,6-pentabromophenoxy)ethane. A methode of preparation is described in U.S. Patent No. 4,016,138 (Anderson). Also useful as component (b) (iii) are brominated flame retardant polymers and oligomers, including those which are described in U.S. Patent No. 3,334,154 (Kim) and U.S. Patent No. 3,833,685 (Wambach). For example, these can be aromatic carbonate copolymers having units of te formula EMI7.1 in which R1 and R2 are hydrogen, (lower) alkyl or phenyl, X1 and X2 are bromo or chloro, and m and r are from 1 to 4, and units of the formula EMI7.2 in which R1 and R2 are as defined above. Especially preferred, however, are oligomeric tetrabromobisphenol-A polycarbonates. The amount of the olefinic polymer, component (a), is subject to wide variation within the composition, ranging from minor to major proportions based on the total weight of the composition. Preferably, however, and espacially when the composition is intended for use as insulation material for electrical wires and cables, this component will be present in an amount of at least 30 parts by weight, per 100 parts of (a) and (b) (i) combined. The flame retardant combination is present in at least the minimum amount necessary to impart a degree of flame retardancy to the composition. The particular amount will vary, depending on the amount of the polyolefin present and possibly other normally flammable ingredients which might also be included in the composition. Each of the three components which make up the flame retardant combination will generally be added in an amount within the following preferred ranges Polyphenylene ether resin, (b) (i) 5 to 70 parts Organic phosphate, (b) (ii) 1 to 30 parts Brominated material, (b) (iii) 1 to 50 parts based on 100 parts by weight of (a) and (b) (i) together. If desired, the composition can be modified to be thermosetting, that is, heat curable, by including one or more compounds effective to cause crosslinking of the polyolefines when the composition is exposed to elevated temperatures, for example, about 300OF. or higher, for a relatively brief period of time. Preferably, the crosslinking agent has a low volatility at the temperatures employed for processing, as well as good stability in the presence of the other ingredients of the composition. Special mention is made of organic peroxides, dicumyl peroxide; 2,5-dimethyl-2,5-di(terbutylperoxy)hexane; a,a-bis(t-butylperoxy)-diisopropyl benzene; ethyl 3,3-bis(t-butylperoxy)butyrate; n-butyl-4,4-bis(4-butylperoxy)valerate; and 2,5-dimethyl-2,5-di(t-butylperoxy)hexane-3. Amounts of from about 1.5 to about 10 parts of the crosslinking agent, for each 100 parts of (a) and (b) (i) combined, are generally sufficient to provide the desired curing. The composition can be further modified, if desired, by including one or more additives often used with thermoplastic polymers, some of which may serve to beneficially affect the chemical and physical properties. Examples are mineral fillers, including clay; reinforcing agents, for example, glass fibers, flakes or spheres; plasticizers; stabilizers, antioxidants; colorants, processing aids, and so forth. Particular mention is made of polymeric materials having elastomeric or elastomeric-like properties. They may be, for instance, copolymers and terpolymers of styrene, such as styrene-butadiene copolymers, styrene-isoprene copolymers, styrene-butadiene-styrene terpolymers, and styrene-isoprene-styrene terpolymers, as well as hydrogenated derivatives of any of the foregoing. Such materials will be added in amounts ranging from 1 to 50 parts by weight, or more, for each 100 parts of (a) and (b) (i) together, which may help to upgrade the compatibility of components (a) and (b) (i). Optionally, and sometimes desirably, a synergist for component (b) (iii) can be added to enhance the flame retardancy effect. This optional component can be selected from among compounds known to synergistically improve the flame resistance imparting properties of brominated agents, and generally such compounds are based on antimony and/or molybdenum. Especially favored for use in the present invention is antimony oxide, usually in amounts of from about 1 to 10 parts by weight for each 100 parts of (a) and (b) (i), but other antimony compounds and amounts are possible depending on particular requirements, and these will be known to those skilled in the art. The composition may be formed simply by mechanical admixture of the ingredients, or preparation may be accomplished by melt or solution blending, which may result in better homogeneity. The admixture may be thermally processed into the desired shaped product as by extrusion or molding, as explained. One particular application involves the use of the composition as insultation material for partial or complete coverage of the surface of electrically conductive articles, for example, copper, nickel or aluminum wires and cables. A method of use comprises heating the composition above the glass transition temperature to form a melt, applying the melt to the surface of the electrical conductor, and then cooling the melt and allowing it to harden or exposing the composition to high energy radiation, such as high energy electrons, to effect crosslinking. The insulated article can additionnaly comprise an outer protective coating, which can be a thermoplastic or thermosetting polymer, for example, polyvinyl chloride. Exemplary embodiments are shown in the accompanying drawings, which are described below. BRIEF DESCRIPTION OF DRAWINGS Figure 1 illustrates an electrically conductive article in accordance with the invention, in cross-section, comprising copper wire 2, and insulation layer 4, consisting of a flame retardant composition as described above. Figure 2 illustrates a modified embodiment, also in cross-section, comprising copper wire 2, flame retardant insulation layer 4, and outer protective polymeric coating 6. DESCRIPTION OF THE SPECIFIC EMBODIMENTS The compositions of the invention are illustrated in the following examples, which are for illustrative pur poses only and are not intended as a limitation of the scope. All amounts shown are in parts by weight. EXAMPLES 1-2 Compositions were prepared using the ingredients noted below by milling the ingredients on a hot two roll mill set a 300 to 3200F. in the case of composition 1, and 250 to 2600F. in the case of composition 2. In each case, the milled material was sheeted and molded. The properties are shown in Table 1. TABLE 1 INGREDIENTS 1 2 Polyethylene, high density 70 - Polyethylene, low density -- 70 Poly(2,6-dimenthyl-l,4-phenylene)ether resin 30 30 Isopropylated triphenyl phosphate 25 25 Bis(2,4,6-tribromophenoxy)ethane 4 4 Antioxidant 1 1 PROPERTIES Tensile strength, psi 1290 560 Elongation, % 40 25 Vertical Burn Test (1/8 inch thick specimen) ND,ND D,D Seconds to quench, 1st ignition 0,0 12,21 2st ignition 0,2 > 30 D = Drip ND = No Drip EXAMPLES 3-8 Additional components were prepared by hot roll milling the ingredients noted below at a temperature of 350 to 3600F., then sheeting and molding. The results are shown in Table 2. TABLE 2 INGREDIENTS 3 4 5 6 7 8 High density polyethylene 70 60 60 50 70 60 SEBS block copolymer 10 10 20 20 10 10 Poly (2,6-dimethyl-1,4-phenylene ether resin 20 30 20 30 20 30 Isopropylated triphenyl phosphate 25 25 25 25 10 10 Bis (2,4,6-tribromophenoxy) ethane 4 4 4 4 4 4 Antioxidant 1 1 1 1 1 1 PROPERTIES Tensile strength, psi 1345 1370 1280 1200 1390 1400 Elongation, % 55 40 50 55 50 45 Vertical Burn Test (1/8") ND,ND ND,ND ND,ND ND,ND ND,ND ND,ND Seconds to quench, 1st ignition 6,10 0,1 3,5 0,0 8,1 0,1 2nd ignition > 30 2,4 12,16 0,1 14,16 0,0 ND = No Drip SEBS : styrene-ethylene/butylene-styrene EXAMPLES 9-11 The ingredients listed below were hot roll milled at 360 to 370OF., sheeted and molded to provide test samples having the properties shown in Table 3. TABLE 3 INGREDIENTS 9 10 11 High density polyethylene 50 50 34 SEBS block copolymer 20 25 33 Poly(2,6-dimethyl-l,4-phenyleneether)resin 30 25 33 Isopropylated triphenyl phosphate 10 10 10 Bis(2,4,6-tribromophenoxy)ethane 4 4 4 Antioxidant 1 1 1 PROPERTIES Tensile strength, psi 1375 1320 560 Elongation, % 65 65 70 Vertical Burn Test, (1/8") ND,ND ND,ND ND,ND Seconds to quench, 1st ignition 0,0 0,1 0,0 2st ignition 1,0 0,0 0,0 ND = No Drip SEBS = Styrene-ethylene/butylene-styrene EXAMPLES 12-14 The ingredients were hot roll milled at 380 to 390OF. in each case. After milling, the composition of Example 12 was molded for 10 minutes at 450OF., and the compositions of Examples 13 and 14 were molded for the same amount of time but at 460OF. The results are reported in Table 4. TABLE 4 INGREDIENTS 12 13 14 Polypropylene 50 50 50 Poly(2,6-dimethyl-1,4-phenylene ether) resin 40 40 40 Isopropylated triphenyl phosphate 10 10 10 Tetrabromobisphenol-A oligomeric polycarbonate 10 20 20 Styrene-ethylene/butylene-styrene block copolymer 10 10 10 Bis diphenyl phosphate of resorcinol 10 10 10 Antimony oxide 5 -- 5 PROPERTIES Horizontal propagation, in inches, after 30 seconds 3/4" 1/2" 1/2" Horizontal Burn Test, 1/8 inch specimen ND ND ND *Pre-extruded at 500 to 6000F. ND = No Drip EXAMPLES 15-16 The ingredients were hot roll milled at 410 to 4200F., then molded for 10 minutes at 460OF. to give the properties shown below in Table 5. TABLE 5 INGREDIENTS 15 16 Polypropylene 50 50 *Poly(2,6-dimethyl-l,4-phenylene ether) resin 50 50 Tetrabromobisphenol-A oligomeric polycarbonate 40 50 Styrene-ethylene/butylene-styrene block copolymer 20 20 *Bis diphenyl phosphate of resorcinol 10 10 Antimony oxide 5 5 PROPERTIES Horizontal propagation, in inches, after 30 seconds 1/4" ND Horizontal Burn Test, 1/8 inch specimen ND ND Vertical Burn Test, 1/8 inch specimen Drip characteristics ND,ND ND,ND Seconds to quench, 1st ignition 0,0 0,0 2nd ignition 5,5 5,5 *Pre-extruded together at 490-5700F. NP = No Propagation ND = No Drip EXAMPLE 17 The ingredients were hot roll milled at 380 to 390OF., then molded for 10 minutes at 450OF. to give the results shown in Table 6. TABLE 6 INGREDIENTS Polybutene 50 *Poly(2,6-dimethyl-l,4-phenylene ether)resin 40 Styreneethylene/butylene-styrene block copolymer 10 *Isopropylated triphenyl phosphate 10 Tetrabromobisphenol-A oligomeric polycarbonate 10 PROPERTIES Horizontal propagation, in inches after 30 seconds 3/4 Horizontal Burn Test, 1/8 inch specimen ND *Pre-extruded together at 500 to 6000F. All of the above mentioned patents and publications are incorporated herein by reference. Other modifications and variations of the invention are possible and will occur to those skilled in the art in light of the above disclosure. It is to be understood, therefore, that changes may be made in the particular embodiments shown without departing from the spirit of the invention or its scope as defined in the appended claims.

Claims: CLAIMS 1. A flame retardant composition, comprising an admixture of (a) an olefinic polymer; and (b) an effective amount of a flame retardant agent comprising, in combination, (i) a polyphenylene ether resin, (ii) an organic phosphate, and (iii) a stable brominated material. 2. A composition according to Claim 1, in which (a) is a polymer of a C2 to C10 olefin. 3. A composition according to Claim 1, in which (a) is a polymer of a C2 to C4 olefin. 4. A composition according to Claim 1, in which (a) is polyethylene. 5. A composition according to Claim 1, in which (a) is polypropylene. 6. A composition according to Claim 1, in which (a) is polybutene. 7. A composition according to Claim 1, in which (b) (i) is a homopolymer or copolymer having units of the formula EMI17.1 wherein Q, Q', Q" and Q"', are independently selected from the groupe consisting of hydrogen, halogen, hydrocarbon radicals, halohydrocarbon radicals, hydroxycarbonoxy radicals, and halohydrocarbonoxy radicals; and n represents the total number of monomer units and is an integer at least about 20. 8. A composition according to Claim 1, in which (b)(i) is poly(2,6-dimethyl-1,4-phenylene ether)resin. 9. A composition according to Claim 1, in which (b) (ii) is a coumpound having the formula EMI18.1 where R is the same or different and is alkyl, cycloalkyl, aryl, alkyl substituted aryl, halogen substituted aryl, aryl substituted alkyl, halogen, or a combination of any of the feregoing, provided at least one R is aryl. 10. A composition according to Claim 1, in which component (b) (ii) is triphenyl phosphate. 11. A composition according to Claim 10, in which the triphenyl phosphate is isopropylated. 12. A composition according to Claim 1, in which (b) (ii) is a di-or polyfunctional compound or polymer having the formula EMI18.2 including mixtures thereof, wherein R1, R3, and R5 are R7 independently, hydrocarbon; R2, R4, R6 and 2 are independently, hydrocarbon or hydrocarbonoxy; x , x and X3 are halogen; m and r are 0 or integers from 1 to 4, and n and p are from 1 to 30. 13. A composition according to Claim 12, in which (b) (ii) is the bis diphenyl phosphate of resorcinol. 14. A composition according to Claim 12, in which (b) (ii) is the diphenyl phosphate of hydroquinone. 15. A composition according to Claim 12, in which (b) (ii) is the bis diphenyl phosphate of bisphenol A. 16. A composition according to Claim 1, in which (b) (iii) is a compound having the formula EMI19.1 where R' is alkylene, straight or branched, having from 1 to 10 carbon atoms; and q and s represent the total number of bromine atoms on each ring and are independently integers from 1 to 5. 17. A composition according to Claim 16, in which (b) (iii) is 1,2-bis(2,4,6-tribromophenoxy)ethane. 18. a composition according to Claim 16, in which (b) (iii) is 1,2 bis(2,3,4,5,6-pentabromophenoxy)ethane. 19. A composition according to Claim 1, in which (b) (iii) is a brominated polymer. 20. A composition according to Claim 19, in which (b) (iii) is a tetrabromobisphenol A oligomeric polycarbonate. 21. A composition according to Claim 1, which also includes an amount of a synergistic agent which enhances the flameretardancy effect of (b) (iii). 22. A composition according to Claim 21, in which the synergistic agent is an antimony compound. 23. A composition according to Claim 22, in which the antimony compound is antimony oxide. 24. A composition according to Claim 1, which includes a polymer having elastomeric properties. 25. A composition according to Claim 24, in which the polymer is a styrene co-or terpolymer. 26. A compostion according to Claim 25, in which the polymer is a styrene-butadiene-styrene terpolymer. 27. A composition according to Claim 25, in which the polymer is a styrene-isoprene-styrene terpolymer. 28. A composition according to Claim 25, in which the polymer is a styrene-ethylene/butylene-styrene terpolymer. 29. A composition according to Claim 1, which contains at least 30 parts by weight of (a) per 100 parts of (a) and (b) (i) combined. 30. A composition according to Claim 1, in which component (a) is crosslinkable, said composition bein curable upon exposure to high energy radiation. 31. A composition according to Claim 30, which includes an effective amount of a crosslinking agent for (a), said composition being curable upon heating. 32. A composition according to Claim 31, in which the crosslinking agent is an organic peroxide. 33. An electrically conductive article, comprising a metallic conductor, at least a portion of the surface of which is covered with an electrically insulating layer of a flame retardant composition comprising an admixture of (a) an olefinic polymer, and (b) an effective amount of a flame retardant agent comprising, in combination, (i) a polyphenylene ether resin, (ii) an organic phosphate, and (iii) a stable brominated material. 34. An article according to Claim 33, in which (a) is polyethylene, polypropylene or polybutene. 35. An article according to Claim 33, in which (b) (i) is poly(2,6-dimethyl-l,4-phenylene)ether. 36. An article according to Claim 33, in which (b) (ii) is triphenyl phosphate. 37. An article according to Claim 33,, in which (b) (ii) is the bis diphenyl phosphate of resorcinol. 38. An article according to Claim 33, in which (b) (ii) is the bis diphenyl phosphate of hydroquinone. 39. An article according to Claim 33, in which (b) (ii) is the bis diphenyl phosphate of bisphenol A. 40. An article according to Claim 33, in which (b) (iii) is 1,2-bis(2,4,6-tribromophenoxy)ethane. 41. An article according to Claim 33, in which (b) (ii) is 1 ,2-bis(2,3,4,5,6-pentabromophenoxy)ethane. 42. An article according to Claim 33, in which (b) (iii) is a tetrabromobisphenol A oligomeric polycarbonate. 43. An article according to Claim 33, which includes a synergist for (b) (iii). 44. An article according to Claim 43, in which the synergist is antimony oxide. 45. An article according to Claim 33, which comprises a protective polymeric outer coating for the insulating layer. 46. An article according to Claim 33, in which the flame retardant composition has been cured by exposure to high energy radiation. 47. An article according to Claim 46, in which the composition also includes a crosslinking agent. 48. An article according to Claim 33, in which the flame retardant composition includes a crosslinking agent and has been cured by exposure to heat. 49. A method for preparing an electrically con ducting article comprising an electrical conductor and a layer of a flame retardant insulating material on at least a portion of the conductor surface, comprising providing a composition according to Claim 1, forming a melt thereof, applying it to the conductor surface anf effecting cure. 50. A method according to Claim 49, in which the flame retardant insulating composition comprises polyethylene, polypropylene or polybutene. 51. A methode according to Claim 50, in which the flame retardant insulating composition comprises poly-(2,6-dimethyl-1,4-phenylene ether). 52. A methode according to Claim 50, in which the flame retardant of the insulating composition comprises, in combination, poly(2,6-dimethyl-1,4-phenylene ether), isopropylated triphenyl phosphate and bis (2,4,6-tribromophenoxy)ethane. 53. A methode according to Claim 50, in which the flame retardant of the insulating composition comprised, in combination, poly(2,6-dimethyl-l,4-phenylene ether), bis diphenyl phosphate of resorcinol and tetrabromobisphenol A oligomeric polycarbonate. 54. A methode according to Claim 50, in which the flame retardant of the insulating composition comprises, in combination, poly(2,6-dimethyl-l,4-phenylene ether), isopropylated triphenyl phosphate and tetrabromobisphenol A oligomeric polycarbonate. 55. A methode according to Claim 49, in which curing is effected by exposure to high energy radiation. 56. A methode according to Claim 55, in which the flame retardant composition includes a crosslinking agent. 57. A methode according to Claim 49, in which curing is effected by exposure of the composition to heat in the presence of a crosslinking agent.

Inventors: ABOLINS, VISVALDIS, BETTS, JOSEPH ELWOOD, HOLUB, FRED FRANK, LEE, GIM FUN, JR.
Applicants: GENERAL ELECTRIC COMPANY
Application year: 1984
Main classification: C08L23
IPC codes: H01B3, C08L69, C08L23, C08K5, C08L71