IMMOBILIZED ENZYME COMPOSITES

Abstract: An immobilized enzyme composite comprising a suit­ able carrier such as controlled pore glass or paper coupled to an enzyme by derivatizing the carrier with an organotitanate. Such a composite is particularly suited for enzymatic reac­ tions for which a non-aqueous, hydrophobic environment is preferable.

Description: The present invention relates to a novel immobilized enzyme composite. The formation of an organo-metallic compound involving titanium in an immobilized enzyme composite is disclosed in U.S. Patent No. 3,841,969, issued to Emery et al. A polysaccharide carrier is reacted with a titanium salt, such as TiCl₄ or Ti₂(SO₄)₃, to form an organo-metallic derivative of the polysaccharide. Suitable carrier materials are sawdust, wood chips, paper, and cotton wool. An enzyme is attached to the organo-metallic derivatized polysaccharide by reacting the two in the presence of a buffer. Suitable enzymes include amylglucosidase, glucose oxidase, invertase, trypsin, alpha amylase, glucose isomerase, pronase, catalase, lactate dehydrogenase, and urease. In a recent article "Lipase-Catalyzed Interesterification or Oils and Fats", A. R. MacRae, JAOCS, vol. 60 . no. 2, February 1983, p. 291-294, the use of an immobilized composite in a non-aqueous environment is disclosed. The MacRae composite was a lipase absorbed onto alumina particles. In order to be active the composite had to be hydrated in a 10% aqueous solution prior to use. The present invention relates to a novel immobilized enzyme composite product and process that uses an alkoxy organotitanate to bind an enzyme to an insoluble carrier. The present invention provides an immobilized enzyme composite characterised in that it comprises: a) an insoluble carrier; b) an enzyme; and c) an alkoxy organotitanate coupling compound which couples the enzyme to the carrier and forms a hydrophobic environment. The present invention also provides a method of preparing such a composite characterised in that it comprises coating the said insoluble carrier with the said alkoxy organotitanate compound and then loading the enzyme onto the coated carrier. For the purpose of this disclosure, preferred organotitanates include compounds of the following general formula: (R₁O)Ti(OXR₂Y)₃ R₁ represents the aliphatic part of a monoalkoxy group, e.g. isopropyl. R₂ signifies either an aliphatic or an aromatic radical, e.g. isoheptadecyl, phenyl, and ethylene. X symbolizes a binding group which connects titanium to R₂, e.g. carboxyl, phenyl, sulfonyl and pyrophosphate linkage. Y stands for a second functional group, e.g. methacrylic, acrylic, amino, mercapto, hydroxyl, and hydrogen groups. Either R₂ or Y can be absent, but not both. Bulletin No. KR-0278-7 Revision No. 2 from Kenrich Petrochemicals, Inc. of Bayonne, New Jersey, USA describes many of these compounds. Suitable carriers are insoluble materials to which the organotitanate can be bound. Examples are siliceous materials, controlled pore glasses and ceramics, and polysaccharides, i.e., filter paper and wood chips. These are conventional materials having available oxide and hydroxyl groups and are used as carriers in other immobilized enzyme composites. Finally, the last component of the composite, the enzyme, can also be chosen from a list of known materials. Hydrolytic, redox, and transferase enzymes are all suitable for the present composite. Specific enzymes include lipase, protease, glucose isomerase, and amylase. The composite is assembled in a simple, two-step method. First, the carrier is derivitized with the organotitanate. In order to do this, one solubilizes the organotitanate. Then the carrier is immersed in the organotitanate solution for a time suitable to obtain the desired quantity of attachment. Preferable exposure times are 15 minutes to an hour. The second step is to load the enzyme onto the derivitized carrier. Typically, the enzyme is put into a buffer solution and the carrier immersed therein. However, the enzyme solution could just as easily be poured onto the carrier. The present composites are particularly suited for reactions which require a hydrophobic reaction site, e.g. transesterifying oil and fats and esterification of fatty acids and alcohols. The organotitanate provides hydrophobic environment for the attached enzyme, thereby promoting the formation of hydrophobic esters such as lipid carboxylic esters. Synthetic jojoba oil substitutes such as erucyl erucate and behenyl analogs can be made easily with the present composite. In a preferred embodiment, the carrier was a controlled pore glass (CPG). One gram of CPG (SiO₂, 30/45 mesh, 400Å average pore size) was mixed with 3 ml of dry isopropanol and 0.005 g of isopropyl, triisostearoyl titanate (ITT) (KR-TTS brand from Kenrich Petrochemical, Inc.). The mixture was vortexed, then allowed to stand for 30 minutes. The solvent was evaporated, and the 0.5% ITT-coated CPG composite precursor was washed and dried. An immobilized enzyme composite was made by adding ten microliters of Rhizopus arrhizus lipase (1875 units in sodium phosphate buffer, pH 6.0) to 100 mg of. 0.5% ITT-CPG. The following Examples illustrate the invention:- Transesterification Example 1 Lipids were transesterified using composites made by the above method. A lipid solution having varying amounts of olive oil and C¹⁴-Stearic acid in 5 ml of n-hexane were poured onto the composite. The lipid mixture was incubated on the composite at 25°C for 66 and 72 hours. The incorporation of C¹⁴-Stearic acid into the olive oil triglycerides was analyzed by silica gel-thin layer chromotography. A solvent having petroleum ether, ethyl ether, and acetic acid in an 80-to-20-to-1 ratio separated the triglycerides which were visualized by iodine vapor. After the iodine evaporated, the triglyceride zone was placed in a 10 ml Scintilene™ (Fisher Co.) cocktail and counted. The incorporation was as follows: The incorporation of stearic acids as measured by the radioassay was later found to be lower than the actual incorporation due to adsorption of material on the thin layer. Example 2 A second experiment carried out in a column of immobilized lipase gave a yield of at least 64%. Fifty microliters of Rhizopus arrhizus lipase (209,000 units) were diluted to 200µl with 0.1M sodium phosphate buffer (pH 6.0) and added to 2.0g of 1% ITT-CPG. The immobilized enzyme was packed in a column (1cm x 10cm). A water saturated, n-hexane solution (50ml) of 1.5g each of olive oil and stearic acid was cycled through the column by a GE Minigear positive pump at 5.0ml/min. The entire product was drained from the apparatus every 2 days and replaced with new substances in new solvent. The process was repeated for 14 days. The products of each run were analyzed by HPLC. The formation of 1,3-distearyl-2-oleylglycerol was observed as a peak at Rt = 6.06 (The HPLC column was a Radiopak C-18. A 36:64 acetone/acetonitrile solvent was eluted at 5 ml/min and detected by refractive index detector). The total integration of new triacylglycerols indicated an incorporation of at least 64%. The specificity of transesterification on the 1 and 3 positions was verified by hydrolysis of the transesterified products with porcine pancreas lipase (known to have 1,3 specificity). The radioactivity on the free fatty acids from the 1 and 3 positions as compared to the radioactivity on the 2-monoacylglycerol was greater than 99%. The column was subject to recycling 14 times over one month with no apparent decrease in transesterification rate. Paper Carrier Another embodiment of the present composite used a paper carrier. The advantages were several. Paper was easily configured, relatively inexpensive, and easy to process both as a composite and as waste. The paper composite was made and used like the glass ones. For example, a circle of 7 cm, ashless filter paper (Whatman 41) was dipped in a 1% ITT, n-hexane solution for 30 minutes and air-dried. Then a composite was made by spotting a 4.0 cm² section of the coated paper with a lipase solution (same as above). The composite was mixed with 1.0m mole each of erucyl alcohol and erucic acid and 4.0 ml of n-hexane and incubated at ambient temperature for 48 hours. The yield of erucyl erucate ester was 40% in 4.5 hours and about 80-90% after 48 hours. Having described the invention with particular reference to preferred form, it will be obvious to those skilled in the art to which the invention pertain, that, after understanding the invention, various changes and modifications may be made without departing from the spirit and scope of the invention as defined by the appended claims.

Claims: An immobilized enzyme composite characterised in that it comprises: a) an insoluble carrier; b) an enzyme; and c) an alkoxy organotitanate coupling compound which couples the enzyme to the carrier and forms a hydrophobic environment. A composite as claimed in claim 1 characterised in that the alkoxy organotitanate is isopropyl, triisosteraroyl titanate. A composite as claimed in claim 1 or claim 2 characterised in that the carrier is selected from ceramics, glasses and polysaccharides. A composite as claimed in claim 3 characterised in that the carrier is selected from controlled pore glasses, controlled pore ceramics, and cellulosic material. A composite as claimed in any of claims 1 to 4 characterised in that the enzyme is selected from hydrolytic, redox and transferase enzymes. A composite as claimed in claim 5 characterised in that the enzyme is lipase. A method of preparing an immobilized enzyme composite as claimed in any or claim 1 to 6, characterised in that it comprises coating the said insoluble carrier with the said alkoxy organotitanate compound and then loading the enzyme onto the coated carrier.

Inventors: SIU-LEUNG, LEE
Applicants: CIBA CORNING DIAGNOSTICS CORP.
Application year: 1984
Main classification: C12N11
IPC codes: C12N11