CATALYST AND METHOD FOR TREATING EXHAUST GASES

Abstract: A catalytic composite which comprises a zirconia-­ alumina support material and an oxidation catalytic metal component selected from the group consisting of platinum, palladium, and iridium, wherein the zirconia is present in an amount such that the zirconia to oxidation metal component molar ratio is greater than 20:1 and the zirconia to alumina weight ratio is greater than 1:2 is disclosed. Also disclosed is a method for effecting the oxidation of noxious exhaust gases comprising carbon monoxide and hydrocarbons with the subject catalytic composite de­ scribed. Further, there is disclosed a process for effecting the simultaneous conversion of carbon monoxide, hydrocar­ bons and nitrogen oxides contained in hot gases from an internal combustion engine operating upon fuel containing at least .01 gm/liter which process comprises contacting the hot gases with a catalytic composite comprising zirconia-­ alumina and an oxidation catalytic metal component selected from the group consisting of platinum, palladium, iridium, and rhodium, wherein the zirconia is present in an amount such that the zirconia to oxidation catalyst metal component molar ratio is greater than 20:1 and the zirconia to alumina weight ratio is greater than 1:2.

Description: C#TALYST AND MTHOD FOR TREATING EXHAUST GASES BACKGROUND OF THE INVENTION (1) Field of the Invention The present invention relates to a catalytic composite and method for treating a combustible waste gas stream prior to discharging such stream into the atmosphere. The catalytic composite of the present invention possesses enhanced stability and activity as well as resistance to lead poisoning when effecting the conversion of auto exhaust gases or other leadcontaining combustible waste gas stream of a noxious nature. DESCRIPTION OF THE BACKGROUND INFORMATION Gaseous waste products resulting from the burning or combustion of hydrocarbonaceous fuels, such as gasoline and fuel oils, comprise carbon monoxide, hydrocarbons and nitrogen oxides as products of combustion or incomplete combustion, and pose a serious health problem with respect to pollution of the atmosphere. While exhaust gases from other carbonaceous fuel--burning sources, such as stationary engines, industrial furnaces, etc., contribute substantially to air pollution, the exhaust gases from automotive engines are a principal source of pollution. In recent years, with the evergrowing number of automobiles powered by internal combustion engines, the discharge of waste products therefrom has been of increasing concern, particularly in urban areas where the problem is more acute, and the control thereof has become exceedingly important. Of the various methods which have been proposed for converting the carbon monoxide, hydrocarbon and nitrogenoxide pollutants to innocuous products, the incorporation of a catalytic converter in the exhaust system holds the most promise of meeting the increasingly rigid standards established by the responsible governmental agencies. In order to achieve the conversion of the carbon monoxide and hydrocarbon pollutants, it has become the practice to employ a catalyst in conjunction with a fuel-air ratio control means which functions in response to a feedback signal from an oxygen sensor in the engine exhaust bases. The fuel-sir ratio control means is typically programmed to provide fuel and air to the engine in a ratio conducive to a near stoichiometric balance of oxidants and reductants in the hot exhaust gases at engine cruising conditions, and to a stoichiometric excess of reductants at engine idling and acceleration conditions. The result is that the composition of the gas with which the catalyst is contacted fluctuates almost constantly, such that conditions to which the catalyst is exposed are alternatively net reducing and net oxidizing. A catalyst for the oxidation of carbon monoxide and hydrocarbons must be capable of operating in such a dynamic environment. Further, it is desirous to add compounds such as tetraethyl lead or tetramethyl lead to internal combustion engine fuel in order to allay knocking, i.e., the out of sequence detonation of the compressed charge. Unfortunately the catalysts employed in the catalytic converter are poisoned by the lead compounds. Catalytic composites which-are resistant to lead poisoning have heretofore been proposed for the catalytic conversion of exhaust gases from an internal combustion engine. For instance U.S. Patent 3,304,150 to W. A. Stover et al. discloses a catalytic system possessing improved life and stability in the presence of volatile lead compounds contained in exhaust gases. The subject catalytic system includes ferric oxide which ingredient lends the lead resistance to the catalyst. The catalytic system also contains suitable active oxidation components such as cobalt, copper, manganese and palladium. The oxidation component and ferric oxide are impregnated upon a base or support such as alumina, silica-alumina, silica magnesia, zirconia, zirconia alumina, zirconia magnesia, and magnesia. The preferred base is a gaTrina-type alumina. U.S. Patent 3,378,334 to H. 5. Bloch likewise discloses a catalyst suitable for use for the oxidation of exhaust gases containing vaporized or entrained lead or lead compounds resulting from the combustion of leaded gasolines. In particular, the subject catalyst comprises a high surface or refractory inorganic oxide base or support such as alumina, alumina silica, alumina zirconia, etc., upon which is deposited by precipitation or impregnation techniques, one or more catalytically active metals or metal oxides, in particular, metals of the platinum group family. The preferred refractory oxide contains a major proportion of alumina. An oxide such as silica, titania, zirconia, hafnia or a mixture of two or more of such oxides may be incorporated with the alumina in an amount within the range of about 0.1 to about 30 wt. X. Improved results as to lead poisoning resistance of the catalyst is attributed to maintaining a low average bulk density (ABC) of less than about 0.4 gm/cc of catalyst and more particularly, an ABO within the range of about 0.15 to about 0.35 gm/cc. Supposedly such a structure is characterized by a high percentage of macropores which can adsorb substantial quantities of lead without obstructing active catalytic sites. In any event the carrier material preferably comprises a major portion of alumina, and, for instance, from 0.5 to about 30 wt. X silica based on the carrier material or a major proportion of alumina plus about 0.1 to about 10 wt. X zirconia based on the carrier material. It is preferred that the zirconia be incorporated in an amount ranging from 0.5 to 5 wt. X. U.S. Patent 3,409,390 to J. Hoekstra discloses a catalytic composite having a longer life and enhanced stability as well as resistance to lead absorption and lead poisoning when effecting the conversion of auto exhaust gases or other leadcontaining combustible waste gases. Specifically patentee maintains that an alkaline earth component particularly, barium, calcium, and strontium when incorporated into the catalytic composite is critically important in improving the stability or life of the catalyst as well as decreased lead pickup when the catalyst is subjected to exhaust gas fumes from engines using leaded fuels. The catalytic composite disclosed in the present reference also contains a catalytically active metal component or components composited with a refractory oxide material possessing an ABO of less than 4 gm/cc. The catalytically active metal components composited with theJrefractory inorganic oxide may be one or more of the following; vanadium, chromium, molybdenum, tungsten, members of the iron group and platinum group of the periodic table, copper, silver and gold. Suitable inorganic oxides include silica, boria, thoria, titania, zirconia, hafnia and mixtures of two or more. The preferred inorganic oxide is alumina or if employed in conjunction with another inorganic oxide, such other inorganic oxide is present in an amount within the range of 0.5 two about 25t by weight. U.K. Patent application 2 070 958 further discloses an exhaust gas catalyst resistant to lead compound poisoning. Specifically the catalyst comprises one or more platinum group metals and a base metal component deposited upon a substrate coated with refractory metal oxide. The preferred refractory metal oxide is alumina. U.S. Patent 4,233,189 to Gandhi et al. related to the use of zirconia as a washcoat material to minimize an interaction between rhodium and the washcoat to maintain a higher rhodium dispersion on a catalyst substrate. Rhodium is the active metal employed in the reduction of oxides of nitrogen contained in exhaust gases. Rhodium apparently does not dissolve as readily nto a zirconia washcoat as compared to an alumina washcoat. Patentee points out that despite the fact that zirconia possesses a relatively low surface area, the need for a high surface area washcoat was not as critical anymore since the contaminant levels of lead and phosphorus in gasoline have decreased from 0.03 algal Pb to 0.003 g/gal Pb. Higher surface area washcoats, such as alumina provided a sink for the distribution of the lead contaminants, thereby decreasing the probability of poisoning active metal components of exhaust gas catalysts. Finally, U.S. Patent 4,316,822 to Fujitani et al. discloses a catalyst for reducing nitrogen oxides, carbon monoxide, and hydrocarbons in exhaust gases which catalyst comprises a porous carrier of ceramic selected from the group consisting of alumina and alumina-magne- sia spinel; and a catalyst ingredient supported thereon consisting essentially of zirconium oxide, cerium oxide and a metal selected from the group consisting of platinum, palladium and mixtures thereof. The zirconia and cerium oxide supported on the carrier are preferably present in amounts of 0.6 9 to 100 9 liter carrier, and 0.8 to 170 9 per liter carrier, respectively. SUMMARY OF THE INVENTION It has now been discovered that when zirconia is present in an oxidation catalyst support material in a specified amount, the zirconia provides an oxidation catalyst with improved resistance to lead poisoning when the catalyst is used to effect the oxidation of the CO and hydrocarbon components in leadcontaining exhaust gases. Accordingly, in one aspect the present invention pertains to a catalytic composite which comprises a zirconia-alumina support material and an oxidation catalytic metal component selected from the group consisting of platinum, palladium, and iridium, wherein the zirconia is present in an amount such that the zirconia to oxidation catalytic metal component molar ratio is greater than 20:1 and the zirconia to alumina weight ratio is greater than 1:2. In another aspect the present invention pertains to a method for effecting The oxidation of noxious exhaust gases comprising carbon monoxide and hydrocarbons with a catalytic composite comprising a zirconiaalumina support material and an oxidation catalytic metal component selected from the group consisting of platinum, palladium, and iridium, wherein the zirconia is present in an amount such that the zirconia to oxidation catalytic metal component molar ratio is greater than 20:1 and the zirconia to alumina weight ratio is greater than 1:2. In yet another aspect the present invention pertains to a process for effecting the simultaneous conversion of carbon monoxide, hydrocarbons and nitrogen oxides contained in hot gases from an internal combustion engine operating upon fuel containing at least .01 gm/liter lead which process comprises contacting the hot gases with a catalytic composite comprising a zirconia-alumina support material and an oxidationcatalytic metal component selected from the group consisting of platinum, palladium, iridium, and rhodium, wherein the zirconia is present in an amount such that the zirconia to oxidation catalyst metal component molar ratio is greater than 20:1 and the zirconia to alumina weight ratio is greater than 1:2. DETAILED DESCRIPTION OF THE INVENTION Catalytic composites comprising platinum and/or palladium as the catalytic components have heretofore been proposed for the catalytic oxidation of exhaust gases from an internal combustion engine. Frequently, the catalytic composite will further comprise a base metal component, such as nickel, where the base metal is defined as a metal selected from the group excluding the platinum group metals and gold. The catalytic components are typically supported on a refractory inorganic oxide support. U.S. Patent 3,304,l50 broadly teaches the use of a support such as alumina, silica-alumina, silica magnesia, zirconia, zirconia alumina, zirconia magnesia, magnesia, but the preferred support is alumina. U.K. Patent application 2 070 958 likewise teaches the preferred use of alumina as a support (see also U.s. Patents 3,378,334 and 3,409,390). While U.S. Patents 3,378,334 and 3,409,390 further teach that other refractory oxides may be incorporated with alumina in connection with lead tolerant oxidation catalyst systems, such other z¯fractory inorganic oxides' presence should be limited to 30 wt. X and 25 wt. X, respectively. In fact, U.S. Patent 3,378,334 specifically points out that if zirconia is incorporated with the alumina it should be limited in the preferred amount to less than 5 wt. X. U.S. Patent 4,323,542 also teaches the addition of other refractory inorganic oxides such as silica, zirconia and magnesia in minor proportions to alumina. In contradistinction to the prior art teachings, when zirconia is present in the catalyst support in amounts such that the zirconia to oxidation catalytic component molar ratio is greater than 20:l and the zirconia to alumina weight ratio is greater than 1:2, the zirconia imparts substantial lead resistance qualities to the oxidation catalyst. Contrary to the teachings of U.S. Patent 4,233,l89 the present invention involves an oxidation catalyst comprising a high zirconia content catalyst support which oxidation catalyst can be readily used with lead--containing exhaust gases. U.S. Patent 4,233,189 is concerned with a reduction/oxidation catalyst which employs rhodium with a washcoat consisting essentially of zirconia. Patentee points out that the zirconia washcoat can be used because gasoline lead content has been decreased to from 0.03 g/gal to 0.003 algal. The catalyst of the present invention, in its embodiment which may be used with a noxious gas containing low or no lead, may not contain rhodium. Further, contrary to the teachings of the 'l89 citation, the present invention in one aspect involves a process for the oxidation of carbon monoxide and hydrocarbons, and the reduction of oxides of nitrogen contained in an exhaust gas from an internal combustion engine operating upon a fuel containing at least O.Ol g/L lead. In particular the process involves contacting the exhaust gases with a catalytic composite comprising a support of zirconia-alumina and one or more of the catalytic metal comnonents: platinum, palladium, iridium, and rhodium. The zirconia is present in an amount such that the zirconia to catalytic metal component molar ratio is greater than 20 1 and the zirconia to alumina weight ratio is greater than 1:2. The features of the present process of the invention are in direct contradistinction to the teachings of U.S. Patent 4,233,189 which cautions against the use of zirconia washcoat to support rhodium in a lead-containing exhaust gas environment. U.S. Patent 4,316,822 is likewise silent with respect to the lead resistance features afforded by the use of zirconia in the catalyst support in amounts prescribed by the present invention. The exhaust gas employed by patentee in the examples does not contain any lead compounds. Patentee's catalyst essentially contains cerium oxide which is not a required ingredient in the present invention catalyst. Without wishing to be bound by the details of any specific theory regarding the mechanism of the invention an attempt is made below to explain a possible mechanism of the invention. It is speculated that the sulfur in the fuel is converted to 502 in the internal combustion engine exhaust gas which 502 is in turn oxidized to S03 by the oxidation component in the catalytic composite. Subsequently PbSO4 is formed at the oxidation component catalytic site; PbS04 being less deleterious to the oxidation component catalytic function. When aluminum is present in the catalyst support Al2(S04)3 preferentially forms at exhaust gas temperatures thereby inhibiting the formation of the desirable PbS04 species. Zr(S04)2 on the other hand, does not form at exhaust gas temperatures; thus freeing the sulfur to form the innocuous -PbS04 species. Accordingly, the presence of zirconia in the requisite amounts in the catalytic support affords the lead tolerant features to the oxidation catalyst. The lead resistant catalytic composite of the present invention comprises one or more metal(s) selected from the group consisting of platinum, palladium and iridium dispersed on a zirconia-containing support material. The support material comprises zirconia-alumina, wherein the zirconia is present in an amount such that the zirconia to catalytic metal component molar ratio is greater than 20:1. The zirconia to alumina weight ratio must be greater than 1:2. The zirconia-containing support material utilized in accordance with the present invention may contain other refractory inorganic oxides such as silica, magnesia, boric, thoria, titania and hatnia. The preferred additional refractory inorganic oxide is alumina. The alumina may be any of the various hydros aluminum oxides or alumina gels such as boehmite, gibbsite, bayerite, and the like. Activated aluminas, such as have been thermally treated at a temperature in excess of about 400 C, with the elimination of at least a portion of the chemically and/or physically combined water and hydroxyl groups commonly associated therewith, are particularly suitable. The preferred alumina is substantially pure gamma or eta-alumina. The zirconia-containing oxidation catalyst support may also contain a thermal stabilizer such as Y2O3, CaO, MgO and BaO. The zircDnia-containing support may be u5ed advantageously in accordance with this invention in any configuration, shape, or size which exposes a catalytically available amount of the metals disposed thereon to the gas to be treated. The choice of configuration, shape, and size of the support depends on the particular circumstances of use of the method of this invention. Generally, in operations in which the catalytic composite is disposed as a fixed bed in an immobile vessel. the support can be conveniently employed in particulate form, as pills, pellets, granules, rings, spheres, etc. Particulate form is especially desirable for large volumes of catalytic composite, and for use in circumstances in which periodic replacement of the catalytic composite may be desired. In circumstances in which less mass is desirable or in which movement or agi- tation of particles of refractory inorganic oxide may result in attrition, dusting, and resulting loss of disposed metals or undue increase in pressure drop across the particles, a monolithic structure is preferred. In automobile exhaust gas applications and in other applications where dimensional or structural stability is particularly desired, a monolithic zirconia-containing structure is preferred. In preparing a monolithic structure of zirconia, it is usually most convenient to employ the zirconia disposed ás a thin film on an inert carrier material which provides the structural support for the refractory inorganic oxide. The inert carrier material can be any refractory material. It is preferred that the carrier material be unreactive with the refractory inorganic oxide and with the gas to which it is exposed. Ceramic m2te- rials are a preferred class of carrier material. Examples of suitable ceramic materials include: sillimanite, petalite, cordierite, mullfte, zircon, zircon mullite, spDdumene, alumina-titan2te, etc. The carrier material can best be utilized in any rigid, unitary configuration which provides a plurality of pores or channels therethrough extending in-the direction of gas flow. It is preferred that the carrier material be in a honeycomb configuration. The carrier material can be used advantageously in either unitary form, or as an arrangement of multiple modules. The carrier material can be oriented such that gas flow is generally in the same direction as the cells or channels of the carrier material, or the gas can flow through the carrier n2- terial in a transverse or radial manner. For a more detailed discus sion of monolithic structures, refer to U.S. Patent No. 3,785,9S8 and U.S. Patent No. 3,767,453. The carrier material may also be made of any metal (including alloys) such as those disclosed in U.K. Patent application 2 0l3 517 which can be fabricated into the desired form (e.g. honeycomb), are oxidation resistant and are otherwise tap- able of withstanding high temperatures. The surface area of the carrier material is not critical to the method of this invention. It is preferred that the micropore volume of the carrier material be relatively low, and it is especially preferred that the carrier material have a macropore distribution such that at least about 90t of the pore volume Is in pores having a diameter of greater than about 20000 A. The surface area of the monolithic structure, as opposed to the carrier material of which the structure is made, should be maximized consistent with pressure drop limitations in the particular embodiment of the method of this-invention selected. It is preferred that the surface area of the monolithic structure be from about 50 to about 1000 square meters per liter of structure, as measured by N2 adsorption, where the volume of the structure Is measured by its exterior dimensions. The geometric surface area of the rncnclithic structure, in tern. of cell density, should be maximized consistent with pressure drop limitations, and is preferably in the range of from about 200 to about BOO cells per square inch of crosssectional area of the structure. The zirconiacontaining catalyst support material can be deposited on the carrier material by any conventional or convenient means such as by dipping the carrier in a zirconia-containing slurry. It is preferred that the zirconia deposit be in the form of a film of from about O.OD03 to about O.Ol inches thick. It is also preferred that the zirconia be present on the carrier material in amounts in the range of from about 800 gms per cubic foot of carrier to about 9000 gms per cubic foot of carrier, where the volume is measured by the exterior dimensions of the carrier material. The catalytic composite of this invention further comprises the catalytic components, platinum, palladium, and/or iridium, and may contain rhodium when the catalyst is used for an exhaust gas derived from fuel containing at least O.Ol g/L of lead. The catalytic components can be incorporated in the catalytic composite in any suitable manner in or on the refractory inorganic oxide, such as by coprecipitation, cogellation, ion##xchange, or impregnation by soaking, dipping, immersion, or otherwise. The preferred method of preparing the catalyst involves the utilization of a soluble, decomposable compound of the particular catalytic component to impregnate the refractory inorganic oxide in a relatively uniform manner. For example, the platinum and/or palladium component may be added to the zirconia by commingling the latter with an aqueous solution of chloroplatinic and/or chloropalladic acid. The chloroplatinic acid and chloropalladic acid can be in common aqueous solution, or in separate aqueous solutions. In the latter case, in instances in which both a platinum and a palladium component are desired, the commingling of the zlr Dnie with the solutions can be performed sequentially in any order. Other water-soluble compounds or complexes tray be employed in impregnation solutions and include ammonium chloroplatinate, bromoplatinic acid, platinum trichloride, platinum tetrachloride hydrate, platinum dichlorocarbonyl dichioride, dinitrodiaminoplatinum, sodium tetranitroplatinate, palladium chloride, palladium nitrate, palladium dioxide, diamminepalladium hydroxide, and tetramminepalladium chloride. The utilization of a platinum or palladium chloride compound, such as chloroplatinic or chloropalladic acid or iridium trichioride hydrate, is ordinarily preferred. Hydrogen chloride, nitric acid, or the like acid can be added to the solution in order to further facilitate the uniform distribution of the metallic components throughout the zirconiacontaining support material. In addition, it is generally preferred to dispose the catalytic components on the zirconiacontain- ing support material after it has been calcined in order to minimize the risk of washing away the valuable metal compounds; however, in some cases it may be advantageous to dispose the catalytic components on the refractory inorganic oxide when it is in a gel led state. Likewise, when a rhodium component is incorporated with the catalytic composite in connection with the process purifying leaded fuel exhasut gas, the rhodium component may be added to the zirconiacontaining support by commingling the latter with an aqueous solution of rhodium trichloride. Other water soluble compounds or complexes of rhodium may be employed, such as hexamminerhodium chloride, rhodium carbonylchlorides rhodium trichloride hydrate rhodium nitrate, sodium hexachlororhodate, and sodium hexanitrorhodate. Further, when an iridium component is incorporated into the composite, the iridium component may be added to the zirconia-contain- ing support by commingling the latter with an aqueous or anhydrous alcoholic solution of iridium salts such as H2lrCl6, H3lrCl6, Hlrcl2(OH)2, (NH4)3lrCl6, (NH4)2lrCl5(H2O). r(NH3)4Cl2]Cl, Cl3. When the catalytic components are deposited upon a monolith as described above, the component loading is such that it ranges from 10 gift3 monolith to 100 g/ft3 monolith. When the catalytic components are supported in another manner, such as upon pellets, the components are incorporated in amounts ranging from 0.1 to 4 wt. X of the zirconiacontaining support. The catalytic composite of this invention is suitable for use in a converter or a reactor of throughflow, cross-flow, or radial-flow design installed in the exhaust line of an internal combustion engine. The converter or reactor may be employed in series with a subsequent oxidation converter or reactor with combustion air being injected ahead of the oxidation converter to insure conversion of the residual carbon monoxide and hydrocarbons remaining in the exhaust gases. The following examples are comparative examples illustrating the improvement in carbon monoxide and hydrocarbon oxidation to be derived through practice of the present invention. The examples are not intended as an undue limitation on the generally broad scope of the invention as set out in the appended claims. EXAMPLE I In this example the performance of various high zirconiumcontent catalytic composites prepared in accordance with the present invention was compared with the performance of conventional alumina supported catalysts in connection with the use of leaded fuel. The catalytic composites were tested for oxidation activity in an engine dynamometer test. The oxidation activity test consists of a measure of the sustained performance (the % conversion of oxidizable compounds in the exhaust gas) at two different operating regimes. These operating regimes simulate an acceleration condition and a cruise condition for an internal combustion engine. Table I below sets out the test condition for the dynamometer test described below. TABLE I Test Conditions Acceleration Cruise % CO 2.G 0.2 % O2 4.8 5.3 A/F Ratio 17/l 19/l Inlet Temperature, F 700 700 Fuel Concentrations/liter .15 grams Pb 1 milligrams P 200 ppm SulfurTetrahydrothiophene Prior to carrying of the above-described oxidation test the catalytic composites were aged for 300 hours in an aging cycle designed to simulate vehicle aging of oxidation catalysts in a high lead content environment. The aging cycle consists of idle, cruise, and high cruise modes of operation. Table II below elucidates the conditions employed in the aging sequence. TABLE II AGING CYCLE Inlet Temperature ( F) 850 @ 25 1400 # 25 1100 4 100 Inlet CO (%) 0.1 - 0.2 0.1 - 0.3 0.1 - 0.2 Inlet 2 (%) 2 4 0.5 1.5 4 0.5 2.0 4 0.5 Aging Fuel: Indolene Containing 570 mg Pb/gal., 4 ing P/gal., 250 wt. ppm S To illustrate the favorable lead tolerant features of the high zirconia content catalyst of the present invention over the conventional alumina-containing catalyst the following samples were prepared. The conventional alumina supported catalyst was prepared by impregnating 300 g of gamma-alumina with 3.74 9 of chloroplatinic acid solution (28.9 wt. % Pt) in excess water (1600 ml). The platinumimpregnated gamma-alumina was subsequently dried at about 1000C in a rotary evaporator. After the drying steps the platinum-impregnated gamma-alumina was calcined for l hour at 10000F in a direct fired furnace. The calcination step was followed by a reduction step at SOODC in a H2 atmosphere for 2 hours. The 300 9 of platinum-impregnated alumina was slurried with 500 9 of H20 and 19 9 of concentrated HN03 and ball-milled for 2 hours. A 2.66 inch in diameter, 3 inch long 300 channel per square inch cordierite monolith was dipped into the above-destribed slurry followed by a blowout of the excess slurry. The monolith was subsequently calcined for 1 hour at lOOOoF. The above dipping and calcining steps were repeated until the catalytic composite contained 10 g platinum per cubic foot which was equivalent to a total washcoat loading of 2782 g/ft3. This conventional aluminawashcoat catalyst was designated catalyst "A". A catalytic composite comprising a support material contain- ing 50 wt. % zirconia, 50 wt. % alumina was prepared as elucidated by the following steps. A platinum impregnated alumina slurry was prepared as described in the preparation method for catalyst "A" above. A platinnum impregnated zirconia slurry was prepared in the same manner as the platinum impregnated zirconia described above. 150 9 of platinum impregnated zirconia was slurried with 150 9 of H20 and 4 9 of concentrated HNO3. The slurry was ball-milled for 2 hours. 150 9 of platinum impregnated alumina was slurried with 250 9 of H20 and 10 9 of concentrated @@@ The zirconia slurry was mixed whith the alumina slurry and bs,l--, 1-1/2 hours. Thereafter the dipping and calcination steps were carried out and repeated as described above in the preparation method for catalyst "A" until the catalytic composite contained 10 9 platinum per cubic foot. The zirconia to platinum molar ratio in the present catalyst was 439. This 50/50 zirconia-alumina catalyst is designated as catalyst "B". Catalyst "C" was prepared exactly as catalyst "A" except that the platinum loading was 3.02 9 (28.89 wt. g chioroplatinic acid) per 150 9 alumina. The washcoat loading was carried out such that it was about 0.6 times that of catalyst "A", about 1900 gIft3. 300 9 of gammaalumina were slurried with 500 9 of water, 19 9 of concentrated HN03. Thus slurry was ball-milled for 2 hours. The above washcoat monolith was dipped into the slurry with the excess slurry blown out. The dipped monolith was thereafter calcined for 1 hour at 1000 F. The dipping and calcining steps were repeated until the total alumina loading was the same as that of catalyst "A's", about 2800 gIft3. This alumina coating was termed an overcoat. Catalyst "C" also contained 10 9 platinum per cubic foot. Catalyst "D" containing a zirconia overcoat was prepared by the following procedure. The same procedure as that employed in the preparation of catalyst "C" wherein an alumina washcoat loading of about 0.6 times that of the pure alumina washcoat loading of catalyst "A" was carried out. 300 g of zirconia was mixed with 200 g of water plus 8 g of concentrated HNO3. This slurry was ball-milled for 6 hours. The above-described monolith was then dipped into the slurry with excess slurry subsequently blown out. The dipped monolith was thereafter calcoined for 1 hour at 1000 F. The dipping and calcination steps were repeated until the total alumina plus zirconia and platinum loadings were the same as that of catalyst "C". The hydrocarbon and carbon monoxide oxidation conversions were measured after the abDve-described 300 hour aging cycle. The conversions were measured at acceleration and cruise conditions. "HCA" denotes conversion of hydrocarbons at acceleration conditions. "COA" and "COC" denote conversion of CO at acceleration and cruise conditions respectively. Table III below sets out the results obtained. The tabulated data clearly shows that catalysts "D" and "B" afford superior conversions after "lead aging" over the conventional alumina washcoat catalyst in virtually all modes of operations. Surprisingly, catalyst "D" which contains only a zirconia overcoat also affords superior results. Apparently merely the presence of zirconia and not necessarily the manner in which it is disposed upon the cordierite monolith promotes the lead-tolerant effects. TABLE III 50%:50% 100 Al Z-03 ;:Alz03 Al2O3 ZrO2 Wasncoat Washcoat Overcoat Overcoat Catalyst A B C D HC A 63 70 53 68 CO A 97 98 90 97 HC C 64 70 67 70 CO C 90 92 90 93 EXAMPLE II The present example serves to show the performance of the high zirconia-content catalytic composites of the present invention when the carrier employed is metallic. The composites were prepared in substantially the same manner as described in Example I. The metallic monolith possessed 403 squares per square inch with a 2.75 inch diameter and a 3 inch length. Each composite washcoat was preimpregnated with platinum at a loading of 10 g/ft3 Catalyst "E" contained a conventional gamma-alumina washcoat at a loading level of 2920 g/ft3 . A.l g/in3 Alseal 500R precoat (Alseal-500R is a high temperature, corrosion and oxidation resistant coating material that contains aluminum powder in an ora.ano-inorganic ceramic binder) was applied to the metallic monolity prior to applicataion of the washcoat in order to facilitate adhesion. Catalyst "F" contained a precoat of Awl seal 500 R (0.1 g/in3) and gamma-alumina (0.17 g/in ). The washcoat contained 90% stabilized zirconia and 10% alumina at a loading of 3197 g/ft3. The following Table IV contains the results of the engine dynamometer oxidation tests of the catalysts. The zirconia-containing washcoat demonstrated superior conversion performance to the alumina washcoat when deposited upon a metallic carrier. TABLE IV 90Q! 10% Zr 2 Al2 3 100 -Alumina Catalyst F HC A 70 55 CO A 96 83 HC C 70 47 CO C 91 74

Claims: WE CLAT.!.. AS OL:R INVENTION: 1. Method for effecting oxidation of noxious exhaust gases comprising a carbon monoxide and hydrocarbons which comprises contacting said gases at oxidation conditions with a catalytic composite comprising a support material which is zirconia-alumina and a catalytic component dispersed on said support material, said catalytic component consistinq essentially of a metal component wherein the metal is selected from the group consisting of platinum, palladium, iridium, and mixtures thereof, wherein the zirconia is present in the support material an an amount such that the zirconia to catalytic component molar ratio is greater than 20:1 and the zirconia is present in amounts such that the zirconia to alumina weight ratio is greater than 1:2. 2. The method of Claim 1 wherein the support material is deposited as a film on a relatively low surface area honeycomb-type ceramic or metallic carrier. 3. A lead resistant exhaust gas oxidation catalytic composite comprising a support material which is zirconia-alumina and a catalytic component dispersed on said support material, said catalytic component consisting essentially of a metal component wherein the metal is selected from the group consisting of platinum, palladium, iridium, and mixtures thereof and wherein the zirconia is present in the support material in an amount such that the zirconia to catalytic component molar ratio is greater than 20:1 and the zirconia is present in amounts such that the zirconia to alumina weight ratio is greater than 1:2. 4. The composite of Claim 1 wherein the support material is deposited as a film on a relatively low surface area honeycomb-type ceramic or metallic carrier. 5. Method for the oxidation of carbon monoxide, the oxidation of hydrocarbons, and the reduction of oxides of nitrogen contained in exhaust gases from an internal combustion engine operating upon fuel containing at least 0.03 g/L lead which process comprises contacting the hot exhaust gases with a catalytic composite comprising a support material which is zirconia-alumina and a catalytic component dispersed on said support material selected from the group consisting of platinum, palladium, iridium, rhodium, and mixtures thereof and wherein the zirconia is present in the support material in an amount such that the zirconia to catalytic component molar ratio is greater than 20:1 and the zirconia is present in amounts such that the zirconia to alumina weight ratio is greater than 1:2. 6. The method of Claim 5 wherein the support material is deposited as a film on a relatively low surface area honeycomb-type ceramic or metallic carrier.

Inventors: ONAL, ISIK
Applicants: UOP INC.
Application year: 1984
Main classification: B01D53
IPC codes: B01D53, B01J23