A METHOD FOR PRODUCING A TINTED PAINT

Abstract: A shaped solid concentrate of pigment in a nonparticulate carrier material of minimum softening point 35°C is prepared and is used to tint a base paint comprising a liquid continuous phase. The carrier is dispersible in the liquid continuous phase which may be aqueous or non-aqueous. Each shaped concentrate preferably contains a fixed quantity of pigment to enable preselection of a number of concentrates appropriate to a desired tint.

Description: PREPARATION OF SHAPED, SOLID,PIGMENT CONCENTRATES, THEIR USE IN TINTING PAINTS AND SUITABLE APPARATUS. This invention relates to a concentrate of pigment in a solid carrier material, to the manufacture of such a concentrate, to the use of the concentrate in the tinting of paints, and to an apparatus for tinting paints which employs the concentrate. Paints are commercially available in a wide range of colours, the introduction of the colour having taken place on a large scale by the incorporation of suitable pigment at one or more stages during manufacture of the paint. For various reasons, for example in order to minimise the total stock of paint which need be held by a supplier or to enable the sale of a very wide range of colours, it is frequently desired to produce a relatively small volume of paint having a specified colour or to modify an existing colour at, or near to, the point of sale of the paint. This is commonly effected by adding to a suitable base paint a measured amount of a concentrate of one or more pigments predispersed in a medium which is compatible with, and promotes the ready dispersion of pigment in, the base paint. This type of concentrate is sometimes termed a tinter. One type of known concentrate for use in colouring paints, comprises pigment, dispersing agent and a liquid carrier, such as water and/or glycol. One or more such concentrates, depending upon the colour of paint which is desired, are volummetrically dispensed into a known volume of a base paint. Another type of known concentrate is in the form of a powder, or the powder may be compressed into a desired shape, which comprises a mixture of pigment and a dispersing agent. In the case of water-based paints, the dispersing agent may contain ionisable groups such as carboxyl groups which in their salt form promote the dispersion of pigment in water. Disadvantages of these prior concentrates are, for example, that the dispersing agent may not be compatible with a film-forming or other component of the final paint and/or may adversely affect the properties of the final paint coating; the concentrate may be unstable to prolonged storage; and the concentrate may not in use promote the full tinting potential of the pigment. With the liquid concentrates there is a practical upper limit to the concentration of pigment due to its effect of increasing the viscosity of the concentrate; and since the pigment may settle out it is necessary to provide appropriate agitation. With the powder concentrates, due to their low bulk density, the volume concentration of pigment is correspondingly reduced. A disadvantage of the compressed forms of powder is that their preparation usually involves a costly multi-stage process. Both the liquid and powder types of pigment concentrate require to be accurately measured before addition to a base paint to achieve a desired tint. The liquid concentrates may be measured in a volumetric pump and both liquid and powder concentrates may be measured by gravimetric weighing. These measurements require the use of expensive measuring equipment in paint dispensing machines employed at or near to the point of sale, for example in a retail shop, and the extent of use may not justify this expense. Pre-measurement of the concentrate into portions of known tinting effect, for example by pre-measurement of liquid or powder into suitable containers, will avoid the need for measurement at the point of sale and enables appropriate tinting by the addition of tinter to a base paint from a known number of containers. However, these containers must be emptied and this can be difficult to automate. When the powders are compressed, whilst the bulk density can be increased, the rate of dispersion is slower. We have now found that certain shaped, solid pigment concentrates for use in the colouration of paints overcome the disadvantages of the prior concentrates mentioned above. The new concentrates may be prepared usually by a process which does not involve the use of a solvent or other material which is liquid at ambient temperatures. Thus the invention provides a process of preparing a shaped, solid concentrate of pigment in a non-particulate carrier material for use in tinting paints having a liquid continuous phase, which consists in dispersing the pigment in the liquid carrier material, the carrier material having a minimum softening point (as herein defined) of 350C and being itself dispersible in the liquid continuous phase of the paint to be tinted; and subsequently allowing the pigmented liquefied carrier material to solidify in a desired shape. By the softening point of-the carrier material we mean the softening point of the material as defined in American National Standard ASTM E28-67 (Reapproved 1977). The softening pointof a material is defined therein as the temperature (OOC) at which a specified form of disc of the material held within a horizontal ring is forced downward by a distance of 2.54 cm (1 inch) under the weight of a specified steel ball as the material is heated in a water-glycerol bath at a rate prescribed in ASTM E28-67. The invention also provides a shaped, solid concentrate for use in tinting paints comprising pigment dispersed in a non-particulate carrier material of minimum softening point 350C. The invention further provides a method of tinting a base paint comprising a liquid continuous phase, which consists in treating the base paint with a shaped, solid concentrate comprising pigment and a non-particulate carrier material, the material having a minimum softening point of 350C and being dispersible in the liquid continuous phase of the paint to be tinted, and thereafter agitating the liquid continuous phase to ensure complete dispersion of the concentrate. By a base paint we mean a paint which is to be coloured by a tinting process. The base paint may be uncoloured, for example it may be white, or it may be slightly or substantially coloured. Preferably each individual solid, shaped concentrate which is added to a base paint comprises a unit, or other fixed, quantity of pigment, or a mixture of pigments, which is capable of imparting a known tint, or a component of a tint, to the base paint. The deepness of the tint thus increases with an increase in the number of similar shaped concentrates added to the base paint; or there may be different sizes or shapes of concentrate which contain different but fixed quantities of the same pigment or mixture of pigments. In order to produce a wide range of tints it is obviously necessary to employ a range of shaped concentrates which each comprise a different pigment or mixture of pigments. Thus a desired tint may be obtained, for example, by adding to a base paint one number of shaped concentrates comprising one pigment and another number of shaped concentrates comprising another pigment. It is one advantage of the solid shaped concentrates of this invention that they may be individually selected and/or counted as appropriate before addition to the base paint. According to another aspect of this invention, we provide a method of producing a tinted paint which comprises counting out a predetermined number of shaped, solid concentrates each comprising a unit,or other fixed, quantity of pigment or pigment mixture appropriate to the tint required, adding the concentrates to a base paint and thereafter agitating the continuous phase of the base paint to ensure complete dispersion of the concentrate. Clearly a wide range of tinted paints may be produced from a base paint, for example at the point of sale as selected by a customer from a display of colours, there being a predetermined combination and number of shaped, solid, pigment concentrates appropriate to each colour displayed. Preferably the above method of tinting paints is at least partly automated and the invention further provides an apparatus for tinting a base paint comprising solid means for storing shaped,/pigment concentrates, means for selecting and counting the number of shaped concentrates appropriate to the tint required,means for passing the concentrates to a vessel containing a base paint to be tinted, and means for ensuring complete dispersion of the concentrate in the base paint. Preferably the carrier material which is employed in the preparation of the concentrate has a maximum softening point of 1100C but higher softening points are possible. More preferably the softening point is in the range 60-1000C. When treating a base paint to be tinted with the pigment concentrate, in order to accelerate the dispersion of the pigment and associated carrier material, it may be necessary to liquefy the concentrate before or after addition to the composition by heating to a temperature greater than the minimum softening point of the carrier material. Preferably there is chosen a carrier material which at ambient temperatures will provide a shaped pigment concentrate which is unchanging in shape, i. e. it does not flow and has some rigidity. For example, if the concentrate is to be in the shape of a disc it is desirable to choose a carrier material which when stored does not permit such a shape to become deformed wether due to an increase in temperature or to an operative step in a machine from which it may be dispensed. Apart from the requirement of the carrier material that it has a minimum softening point appropriate to the conditions in which the concentrate will be used, a primary requirement in the carrier material is that it is readily dispersible in the liquid phase of the paint to be tinted. For convenience, paints are often classified as comprising either an aqueous or a non-aqueous liquid as the liquid phase. The present invention is particularly concerned with paints having an aqueous liquid continuous phase but is equally applicable to paints based on a non-aqueous continuous liquid phase. When the paint has an aqueous liquid phase it is understood that the total paint composition comprises at least 30% by weight of water. Other liquids which may be present in a composition together with water include lower alcohols and glycol ethers. A typical non-aqueous continuous phase comprises aliphatic hydrocarbon, for example white spirit. Preferably the carrier material itself is soluble in and more preferably is highly soluble in, the liquid phase of the paint when it is added in the solid state. If the softening point of the carrier material is suitably low, for example less than 1000C, then the dispersibility, including the solubility or miscibility, of the carrier material in the liquid phase may be improved by melting the material just before it is added to the coating composition. In general it is preferred that the carrier material is capable of immediate dispersion, for example dissolution, in the liquid phase in the shape in which it is stored before use without external aid apart from simple agitation. The rate of dissolution is obviously affected by the maximum thickness of any given shape. Nevertheless dispersion may be accelerated, for example, by initial mechanical disintegration; by the presence in the paint and/or the concentrate of specific dispersion aids such as acid or base; or by mechanical agitation. In the preparation of the solid, shaped pigment concentrate of this invention the liquid carrier material in which the pigment has been dispersed may be solidified into a variety of shapes, for example in the shape of a rod, ribbon, fibre,sheet, granule, disc, lozenge, cube or other rectilinear form, or sphere, or other shape containing a known amount of pigment. The shape of the concentrate may be determined by the design of apparatus which is employed to perform the tinting of the paint, for example due to the nature of the space within this apparatus for storing the shaped concentrate before use. The shape may also be determined by the rate of dissolution which can be obtained by the use of a particular shape, or by the ease of manufacture of a particular shape. Particularly preferred shapes in which the concentrate is used are those where there is a high ratio of surface area to volume. The dispersion of the pigment in the liquid carrier material may be carried out in conventional equipment such as is used for example in mixing thermoplastic polymers with pigment, plasticiser and other additives. It should be noted that the dispersion of pigment in this way entails less wastage than in the preparation of liquid concentrates. The dispersion of pigment in carrier material and the production of a required shape of concentrate may be achieved using one or more specific types of apparatus.. The dispersion of pigment may be carried out for example, in a compounding extruder, a series of rollers, or a z-blade mixer. An intermediate form of shaped concentrate may be first produced, for example, as a coil of extrudate. The final shaped concentrate may be produced from the pigment dispersion or from an intermediate shape at a later stage, far example by a cutting or moulding process. As well as being itself dispersible, and preferably highly soluble, in the liquid continuous phase of the paint it is also necessary that the carrier material is capable of dispersing the pigment throughout the paint and of ensuring that its tinting properties are well used. If desired, other materials may be present in the concentrate, for example to improve the dispersion of pigment or to improve the mechanical properties of the concentrate, for example by fibre reinforcement. Carrier materials which are solid at ambient temperatures, which have a minimum softening point of 350C and are suitable for use in the water-dispersible pigment concentrate of this invention include materials which comprise a strongly hydrophilic moiety such as a moiety of a poly(ethylene oxide) e.g. a polyethylene glycol, poly(vinyl alcohol) i.e. hydrolysed poly(vinyl acetate), poly(vinyl pyrrolidone) and poly[(meth) acrylamidel. Particularly suitable carrier materials include polyethylene glycols of molecular weight greater than 1000; simple esters of polyethylene glycols, alkyd resins in which a polyethylene glycol has been included as one component or which have been subsequently reacted with polyethylene glycol; and certain commercially available surfactants which comprise a poly(ethylene glycol) moiety. Carrier materials which are solid at ambient temperatures and are suitable for use with paints which comprise aliphatic hydrocarbon as the liquid continuous phase include copolymers of tertiary butyl styrene with lauryl methacrylate or with 2-ethylhexyl acrylate. The invention is illustrated by the following Examples in which parts and percentages are by weight. EXAMPLE 1 7 parts of a phthalocyanine blue pigment, (commercially available under the Registered Trade Mark "Monastral") were dispersed in 3 parts of an adduct carrier material prepared by reacting 5 parts of polyethylene glycol (of molecular weight 1500) and 1 part of tall oil fatty acid using a Z-blade mixer fitted with a heating/cooling jacket to maintain the temperature in the range 40 - 100 C. The resulting product was cast and allowed to cool to ambient temperature in the shape of solid discs containing a known amount of pigment. The softening point of the adduct carrier material was 400C. The discs were readily soluble in an acrylic emulsion base paint and could be used to tint this paint to any desired depth of shade. Up to 75% by weight of the blue pigment could be dispersed in the adduct to provide a useful concentrate. EXAMPLE 2 7 parts of a yellow oxide pigment (commercially available as "Bayferrox" 390) were dispersed in 3 parts of an adduct prepared by reacting 2.8 parts of polyethylene glycol of molecular weight 1500 with 1 part of an alkyd resin (prepared by reacting pentaerythritol trimellitic anhydride and tall oil fatty acid in the weight proportions I/2.5/10.("Bayferrox" is a trade mark). The means of dispersion was a twin-screw extruder fitted with a heating/cooling jacket to maintain the temperature in the range 35-100 C. The product was moulded in the shape of a lozenge and allowed to cool to the ambient temperature. Each lozenge contained a known amount of pigment. The softening point of the adduct carrier material was 400C. Concentrates containing up to 70% by weight of pigment could be prepared. EXAMPLE 3 7 parts of a yellow pigment (commercially available under the Registered Trade Mark "Irgazin") were dispersed in 3 parts of the monomethyl ether of polyethylene glycol of molecular weight 2000 using a Z-blade mixer fitted with a heating/cooling jacket to maintain the temperature in the range 40-100 C. The product was extruded in the shape of a rod and allowed to cool to ambient temperature. Concentrates containing up to 704 by weight of the pigment could be prepared. EXAMPLE 4 6 parts of a phthalocyanine blue pigment (commercially available under the Registered Trade Mark "Monastral") were dispersed in 4 parts of an adduct carrier material prepared by reacting 54.5 parts of tertiary butyl styrene and 45.5 parts of lauryl methacrylate using a Z-blade mixer fitted with a heating/ cooling jacket to maintain the temperature in the range 60-1000C. The resulting product was pressed into discs and allowed to cool to ambient temperature. The discs were readily soluble in an alkyd based paint. The softening point of the copolymer was in the range 60-1 000C. EXAMPLE 5 6 parts of a phthalocyanine blue pigment (commercially available under the Registered Trade Mark "Monastral") were dispersed in 4 parts of an adduct carrier material prepared by reacting 56.5 parts of tertiary butyl styrene and 43.5 parts of 2-ethylhexyl acrylate. The means of dispersion was a Z-blade mixer fitted with a heating/cooling jacket to maintain the temperature in the range 60-1000C and the material was moulded into the shape of a lozenge and allowed to cool in ambient temperature. The softening point of the copolymer was in the range 60-100 C.

Claims: WE CLAIM : 1. A process of preparing a shaped, solid concentrate of pigment in a non-particulate carrier material for use in tinting paints having a liquid continuous phase, which consists in dispersing the pigment in the liquefied carrier material, the carrier material having a minimum softening point (as herein defined) of 350C and being itself dispersible in the liquid continuous phase of the paint to be tinted; and subsequently allowing the pigmented liquefied carrier material to solidify in a desired shape. 2. A process according to claim 1, wherein the carrier material has a maximum softening point of 1100C. 3. A process according to claim 1 or claim 2, wherein the carrier material has a softening point in the range 60-100 C. 4. A process according to any one of claims 1 to 3, wherein the concentrate is in the shape of a rod, ribbon, fibre, sheet, granule, disc, lozenge, cube or sphere. 5. A shaped, solid concentrate for use in tinting paints comprising pigment dispersed in a non-particulate carrier material of minimum softening point 350C. 6. A method of tinting a base paint comprising a liquid continuous phase, which consists in treating the base paint with a shaped, solid concentrate comprising pigment and a non-particulate carrier material, the carrier material having a minimum softening point of 350C and being dispersible in the liquid continuous phase of the paint to be tinted, and thereafter agitating the liquid continuous phase to ensure complete dispersion of the concentrate. 7. A method of tinting a base paint according to claim 6, wherein the paint has an aqueous liquid continuous phase which comprises at least 30% by weight of water based on the total weight of the paint. 8. A method of tinting a base paint according to claim 6, wherein the paint has a non-aqueous liquid continuous phase comprising an aliphatic hydrocarbon. 9. A method of producing a tinted paint which comprises counting out a predetermined number.of shaped, solid concentrates each comprising a unit, or other fixed, quantity of pigment or pigment mixture appropriate to the tint required; adding the concentrates to a base paint; and thereafter agitating the continuous phase of the paint to ensure complete dispersion of the concentrate. 10 An apparatus for tinting a base paint which comprises in combination means for storing shaped, solid pigment concen trates; means for selecting and counting the number of shaped concentrates appropriate to the tint required; means for passing the concentrates to a vessel containing the base paint to be tinted; and means for ensuring complete dispersion of the concentrate in the base paint.

Inventors: GRAYSTONE, JONATHAN ALBERT, SNAITH, STEPHEN PAUL
Applicants: IMPERIAL CHEMICAL INDUSTRIES PLC
Application year: 1984
Main classification: C09D7
IPC codes: C09C3, C09D7, C09D145, C09D133, C09B67, C09D171, C09D17