POLYSILICON FETS

Abstract: Field effect transistors in which the channel region 17 is made of thin highly doped polysilicon which is preferably also hydrogen passivated.

Description: Background and Summary of the Invention The present invention relates to field effect transistcfrs and to integrated circuits. For numerous applications it would be desirable to be able to fabricate good quality field effect transistors in polycrystalline semiconductor material. Such a capability would lead to breakthroughs in at least two areas. First, silicon on insulator structures could be fabricated on a very wide variety of substrates. At present, silicon on insulator structures can only be used in those cases where a good lattice match between the silicon active device layer and the insulating substrate can be found. Secondly, and perhaps of even more importance, the capability for good quality polysilicon devices permits vertical integration. That is, at present integrated circuits are essentially two-dimensional devices, and active devices cannot be overlaid one on top of another. However, if it were possible to fabricate active devices having polysilicon channels, such active devices could be formed on an insulator layer on top of another active device. This opens the door to a whole new generation of integrated circuit device design. However, the numerous prior attempts in the art to build transistors in polysilicon have encountered three major difficulties. First, the mobility (and hence the bulk conductivity) of polysilicon material is inherently very low. Second, leakage problems have normally been found with polysilicon transistors. Third, the threshold voltages of such transistors have been extremely large. These problems are in some respects complementary. That is, by making the channel of a polysilicon transistor very long, the leakage current can be somewhat reduced. However, in this case, the low mobility of the polysilicon means that the device will have a very large series resistance, so that a huge low-gain device is likely to result if one attempts to design a practical polysilicon transistor using methods of the prior art. Prior art attempts to design a good polysilicon transistor have typically used relatively thick polysilicon (e.g. 3560-75000 Angstroms) at modest doping channel levels of, e.g., 1016 or less per cubic centimeters, operated in the inversion mode. (I.e., the channel is n-type poly for a PMOS transistor having p+ poly sources and drains.) Inversion mode is typically used to reduce leakage current. However, the result of such a device configuration is a very high threshold voltage, typically in the range of eight to ten volts. This is too high for most integrated circuit applications. The present invention avoids these difficulties, by providing a field effect transistor having a channel region which is a thin (preferably 1000 to 1500 Angstroms) highly doped (preferably 1017 to 1018 per cc) polysilicon layer. The channel region is preferably hydrogen annealed, to reduce leakage current. Such a transistor is preferably operated in the accumulation mode. (I.e. the channel is p-type polysilicon for a PMOS device.) The combination of these characteristics results in a transistor which has low leakage current, high source/drain breakdown voltage, low threshold voltage, and low channel series resistance. Thus, it is an object of the present invention to provide a polysilicon-channel transistor having low leakage. It is a further object of the present invention to provide a polysilicon-channel transistor having low series resistance. It is a further object of the present invention to provide a polysilicon-channel transistor having low series resistance and relatively small physical size. It is a further object of the present invention to provide a field effect transistor having a channel region comprised of polycrystalline material, which has low leakage current. It is a further object of the present invention to provide a field effect transistor having a channel composed of polyctystalline material, which has low on-state series resistance. It is a further object of the present invention to provide a polysilicon field effect transistor having a low threshold voltage. According to the present invention there is provided: A field effect transistor comprising: A channel region comprising polycrystalline semiconductor material; Source and drain regions connected to said channel region; and A gate positioned to apply an electric field to said channel region between said source and drain contacts; Wherein said channel has an equilibrium carrier concentration of at least five times 1016 per cubic centimeter. Brief Description of the Drawings The present invention will be described with reference to the a T ompanying drawings, wherein: Figure 1 shows a first conceptual embodiment of the present invention; Figures 2a-2d show the effect of grain boundary passivation on the space charge barriers of the grain boundaries; Figures 3a-3d show successive stages in the fabrication of another embodiment of the present invention. Figures 4-6 show further embodiments of the present invention; Figure 7 shows the effect of hydrogen passivation on the output iv characteristics of a sample device according to the present invention; Figure 8 shows the effect of hydrogen passivation on the drain current versus gate voltage characteristics of a sample device according to the present invention; Figures 9a-9f show the effect of hydrogen passivation on the subthreshold characteristics of a sample device according to the present invention; Figure 10 shows a further sample embodiment of the invention; and Figure ll shows a further embodiment of the invention in a vertically integrated structure. Description of the Preferred Embodiments Figure 3 shows the device structure used to build a first em tdiment of the invention. The starting material was 3-6 ohm-cm, (100), 3" silicon slices 11. A 5000 A LPCVD polysilicon layer 13 was deposited and doped n+ to 30 ohm/sq. using a POCl3 source. A 350 A thermal gate oxide 15 was grown. Then a 1500 A layer 17 of undoped LPCVD polysilicon was deposited by pyrolysis of SiH4 at 6200C. Boron implantation was performed at various doses to adjust the channel doping. Device isolation was accomplished by complete island etch of channel polysilicon layer using a CHF3 based plasma. Source/drain regions 19 were doped by boron implantation. Two splits of slices were made which either did or did not receive grain boundary passivation by a plasma of hydrogen. The plasma was excited in an equal mixture of H2 and N2 by approximately 800 W of RF power at 13.56 MHz. The samples were held in the plasma at 3000C for a duration of 60 minutes. The output characteristics of a first sample device L153/SO4 are shown in Figure 7A. This device has an effective electrical channel width W=127 microns and electrical channel length L = 1.5 microns. No hydrogen passivation treatment was carried out on this device. A well behaved MOSFET action is obtained, which is reproducible across the slice and from slice to slice. The drive current, meansured at VD = VG = 5V, is about 10 microamp. The accumulation hole mobility in the vicinity of VG = -5V, as determined from the linear region transfer curve shown in Figure 8A, is found to be about 1 cm2/V-sec. Figures 7B and 8B show the output characteristics for a second sample device according to the present invention, Ll53/Sl0. The physical parameters for this device are identical to that of L153/S04. The two devices were fabricated with similar processing schedule except that only L153/S10 saw the hydrogen plasma treatment. The drive current for this device is about 200gA, which is a factor of 20 higher than that of the unpatsivated device. The corresponding hole mobility is found to be 7 cm2/V-sec. Polycrystalline silicon is composed of small grains with random orientation separated by grain boundaries. Electrically active traps in the boundary region capture carriers and deplete the surrounding regions, giving rise to a potential barrier. These potential barriers have a significant effect of the conduction behaviour or the MOSFET. The observed increase in driving current after hydrogenation is aprtly relted to the lowering of intergrain potential barrier, a phenomenon well documented in regard to polycrystalline semiconductor materials. Atomic hydrogen penetrates polysilicon during plasma treatment, saturating the dangling bonds at grain boundaries, thereby reducing the trap density. Figure 2 shows the effect of hydrogen passivation on space charges at grain boundaries schematically; Figure 2A shows dangling bonds, Figure 2B shows passivated bonds, Figure 2C shows the potential for Figure 2A, and Figure 2D shows the potential for Figure 2B. Where hydrogen passivation is introduced, as in Figure 2B, the trap densitv qgb at the grain boundary is dramatically reduced, since many of the dangling bonds are now bonded to hydrogen ions, producing electrically neutral cities. This in turn produced a strong reduction in the potential barrier phigb, #gb# which varies as the square of the interface charge density qg: phigb = qgb2/8qEsNA The subthreshold behaviour of these devices resembles the weak inversion characteristics of bulk silicon MOS transistors. However, the mechanism of origin of subthreshold characteristics in these devices is quite distinct from that of inversion mode bulk MOSFETs. At large gate drives the conduction in these devices is predominantly accumulation mode. with small gate bias, the current is largely supported by acceptor doping in the channel polysilicon layer. It is the gate modulation of this portion of device current that gives rise to the observed turn off property. On lowering the gate voltage, the channel polysilicon layer eventually becomes completely depleted. The current flow is now space charge limited over the potential barrier at the source end resulting in an exponential drain current dependence on gate bias. The plasma hydrogen passivation reduces the generation/recombination centers in the channel poly, significantly improving the leakage current. The improvement in subthreshold slope, dramatically apparent in Figures 9A-9F, seems to be realted to the reduction in electrically active surface states residing at the gate oxide-channel poly interface. Figures 9A-9C are for passivated devices and Figures 9D-9F are for unpassivated devices. The spread in electrical parameters across the slices remains largely unaltered before and after passivation. For a majority of the tested devices the drive current is within +15% and the leakage current is within +50% of the mean values. It must be mentioned that contact photolithography was used to pattern the source drain separation and may be mainly responsible for the observed spread in drive current. The hydrogen annealing is preferably performed by exposing the polysilicon to a hydrogen plasma, e.g. in a standard parallel-plate plasma reactor. For example, an anneal in a plasma discharge at a partial pressure of molecular hydrogen of 1000 microns for 60 minutes for a four inch wafer at a temperature in the neightborhood of 3000C is sufficient. However, this process step is not at all end point sensitive. The hydrogen is introduced very rapidly, and simply serves to saturate the danling bonds at the grain boundaries. An excess of hydrogen is innocuous. Thus, the transistors of the present invention are preferably made using hydrogen-annealed polysilicon, although the hydrogen annealing step is not strictly necessary. However, it should be ntoed that the hydrogen anneal preferably used is an atomic hydrogen anneal and not a molecular hydrogen anneal. That is, the plasma dissociates the H2 feed gas into species such as H+ ions and monotomic hydrogen free radicals, which are more easily linked with the dangling bonds at the grain boundary sites. The hydrogen will also pass easily through a reaonably thin oxide cap (e.g. 7000 Angstroms). However, a thick nitride cap will retard the in-diffusion of the hydrogen significantly. It should also be noted that prolonged high temperature processing steps subsequent to the hydrogen anneal should be avoided. If prolonged high temperature steps are subsequently used, the danger is that the atomic hydrogen which is passivated in the grain boundaries will recombine an out diffuse as molecular hydrogen. This means that the benefits of passivation at grain boundaries will gradually be lost, and the space charge barriers will gradually increase, degrading mobility and leakage. However, this is a gradual degradation rather than a catastrophic one, and a moderate amount of high-temperature steps can be tolerated. For example, an hour at 450 C, under the hydrogen and the only conditions noted above, can be tolerated easily. Longer high-temperature steps can also be tolerated, although it is prefer able to minimize the subsequent high-temperature time where this can conventiently be done. For example, it is preferred to use a low-temperature multilevel oxide planarization step, rather than the conventional high-temperature PSF reflow. The presently preferred embodiment of this is to use OCD spin-on silicate solutions, which are then baked at low temperature to evaporate the organic solvent. However, a variety of other low-temperature MLO planarization methods can be used, including MLO reflow by transient heating (e.g. by laser annealing,, or use of other low-temperature MLO materials, such as BPSG, lead-doped silica glasses, or organics such as polyimid or PIQ. It should also be ntoed that, in the presently preferred embodiment, the contact centering times and temperatures are slightly reduced. That is, LOM doped with 1% silicon is preferably centerd in hydrogen for ten minutes at 4000. It should be noted that the effects of hydrogen escape during subsequent high-temperature processing steps can be somewhat mitigated by performing the initial hydrogen passivation annel for longer time and/or a higher partial pressure of hydrogen. it should also be ntoed that hydrogen is not the only passivating species which can be used, although it is presently preferred. Fluorine can also be used, and it is believed that other halogen elements are also useful. Alternatively, hydrogen ions could be implanted for grain boundary passivation, but ths is certainly not a preferred embodiment. It should also be noted that the present invention is not only applicable to insualted gate field effect transistors, but could also be applied to junction field effect transistors having a polysilicon gate. However, the insulated gate embodiment of the present invention is definitely preferred. In particular, the fast and uneven diffusion of dopants characteristic of polysilicon means that diffusion across the silicon/polysilicon boundary is likely to induce undesirable spreading device characteristics. The following references provide useful background information on the characteristics of polysilicon transistors, and are hereby incorporated by reference: T. Ohzone, T. Hirao, K. Tsuji, S. Horiuchi, S. Takayangi, "2Kx8 Bit Static RAM," IEDM Technical Digest, pp. 360-363, 1978. This article teaches use of an accumulation-mode p-channel polysilicon transistor, wherein the polysilicon channel layer is 5000 Angstroms thick and no hydrogen passivation is used. K. Ochii, K. Hashimoto, H. Yasuda, M. Masuda, T. Kondo, H. Nozawa and S. Kohyama, "An Ultralow Power 8Kx8-Bit full CMOS RAM with a Six-Transistor Cell." IEEE J. Solid State Circ., SC-17, pp. 798-803, 1982. Y. Ochida, T. lizuka, 3. Matsunaga, M. Isobe, S. Konishi, M. Sekine, T. Ohtani, and S. Kohyama, "A Low Power Resistive Load 64 Kbit CMOS RAM," IEEE J. Solid State Circ., SC-17, pp. 804-809, 1982 T. C. May and M. E. Woods, "Alpha-Particle-Induced Soft Errors in Dynamic Memories," IEEE Trans. Electron Devices, ED-26, pp. 2-9, 1979. J. F. Gibbons and K. Lee, "A One-Gate-Wide CMOS Inverter," Electron Device Letters, ELD-1, pp. 117-118, 1980. J.P. Colinge, E. Demoulin and M. Lobet, "Stacked Transistors CMOS (ST-MOS), an NMOS Technology Modified to CMOS," IEEE Trans. Electron Devices, ED-29, pp. 585-589, 1982. T. Iizuka, H. Nozawa, Y Mizutani, H. Koneko and S. Kohyama, "Variable Resistance Polysilicon for High Density CMOS RAM," IEDM Technical Digest, pp. 370-373, 1979. J. Y. W. Seto, "The Electrical Properties of Polycrystalline Silicon Films," J. App. Phy., Vol. 46, pp. 5247-5254, 1975. Thus, the present invention teaches a polysilicon transistor which is different from the polysilicon transist° s heretofore known in three important was: 1. L the channel regions is thin; 2. the channel region is highly doped; 3. the channel region has the same doping type as the polysilicon source and drain regions, i.e. the transistor is operated in accumulation mode; 4. the transistor is passivated in hydrogen. The use of high doping levels in the channel (preferably 5x1016 per cubic centimeter or greater) produces two clearly desirable results: the threshold voltage is decreased. As extensively discussed above, high threshold vltages have been a crucial stumbling block to use of prior art polysilicon channel transistors. Secondly, the drain current is substantially increased. Third, the depletion depth Xd, i.e. the depletion depth corresponding to the built in Fermi potential, is decreased. A crucial teaching of the present invention is that the polysilicon channel layer must be thin enough that it is depleted through, that is t is equal to or less than xd+xb, where b is the backside depletion depth caused by the fixed charge typically found at the polysilicon/silicon dioxide backside interface. (This fixed charge will typically produce a depletion depth of about 1000 Angstroms at a polydoping level of 1017 per cubic centimeter.) The use of a thin channel means that a heavily doped accumulation mode channel can be used while achieving good turn off characteristics. Thus, the present invention is the first to achieve the combination of good threshold voltage, good on-state serious resistance, and good thrun-off characteristics (low leakage). A further advantage of the use of a thin polysilicon layer for channel regions is topographic. that is, a 1500 Angstrom layer of polysilicon, as used for transistors according to the present invention, will produce fewer step coverage problems in subsequent layers than will the thicker polysilicpn layers typically used in the prior art. As illustrated in Figure 1: EMI12.1 Increasing NA produces: 1. decreasing VT 2. increasing ID 3. decreasing Xd To prevent leakage: 1. t 5 Xd use thin channel poly 1000 A < t < 1500 A Thin channel polv produces: 1. large drive current 2. low leakage current 3. small vertical step Figures 4, 5, 6, 10, and 11 show a few of the many device embodiments in which the present invention can be configured and numbered analogous to Figure 3 without regard for exchange of n-type and p-type regions, etc. As is obvious to those skilled in the art, the present invention provides a fundamentally new device structure, which can be embodied tin a tremendous variety of integrated circuits, and which solves a high variety of circuit designer's problems. In addition, the key teaching of thin channel regions with high doping can be embodied in a wide variety of specific thicknesses and channel doping levels. For example, channel thicknesses of less than 3500 Angstroms, at channel doping levesl of a t least 5e16 (5x1016) per cubic centimeter, are within the scope of a first embodiment of the present invention. Additionally, polysilicon transistors having channel thicknesses of 2000 Angstroms or less at channel doping of at least 1017, are also within the scope of the present invention. In general, the accumulation mode polysilicon device having a mobility of at least five centimeters suare per volt second, and a channel thickness of 2000 Angstroms or less, is also within the scope of the present invention. A further advantage of the use of thin polysilicon transistors according to the present invention, in some applications, is that the spontaneous growth in grain size is limited. That is, for VLSI applications MOSFETS having channel lengths on the order of one or two microns are required. The grain size of as-deposited polysilicon will typically be in the range of 300 to 500 Angstroms, so that the number of grain boundaries cutting across the electrically shortest channel length will be reasonably large, e.g. 20 or more, and the variation in the numbers of grain boundaries cutting the channel regions of a particular device will cause onlv a moderate spread in device characteristics. However, if the grain size of the polysilicon spontaeously increases during processing, which it is likely to do, the average number of grain boundaries which lie across the electrically minimal channel is likely to decrease, which means that a much larger spread in device characteristics is likely to result. That is, if the polysilicon grain size spontaineously increases to near one micron, fdu e to high-temperature steps during device processing, as is likely to happen, some devices will have no grain boundaries cutting the channel, some will have one, and some may have two or more. To the extent that the space charge barriers at grain boundaries can be reduced, this source of device characteristics spread becomes less important, as discussed above regarding the hydrogen passivation step. However, since present art does not entirely eliminate the effects of the grain boundaries, it is desirable to minimize the spread in device characteristics which results from the electrical effects of the grain boundaries. In this respect, the use of a thin polysilicon layer is helpful, since polysilicon thicknesses of 2000 Angstroms or less retard the increase in grain size which would otherwise occur spontanously during processing. Thus, the present invention advantageously provides a polysilicon transistor having low leakage and low series resistance. Of course, transistors fabricated according to the present invention can be used in a wide variety of integrated circuit devices. For example, in addition to the silicon on insulator embodiments primarily discussed above, vertically integrated embodiments such as shown in Figure 11 can also be used. Moreover,silicon dioxide is not the only insulating substrate which can be used underneath a polysilicon transistor according to the present invention. A tremendous variety of other substrates can be used, such as sapphire, spinel silicate glasses, ceramics, etc. Moreover, it should also be noted that the present invention is not specifically limited to a polycrystalline silicon transistor, although that is believed to be its primary application, but is also applicable to transistors formed in other polycrystalline semiconductor materials. The key teachings of the present invention in this respect are that theichannel layers should be relatively thin and the channel doping levels should be relatively high and of the same type as the device on-state channel conductivity type. In embodiments using polysilicon, the channel thickness is preferably less than 3000 Angstroms, and the channel doping preferably greater than 1017 per cc. In applying the present invention to other semiconductors, the channel thickness can be adjusted in proportion to the square root of the permittivity of the semiconductor used. Similarly, the dopant concentration is preferably chosen merely to achieve a carrier concentration of greater than 5E16 in the particular semiconductor used. As will be obvious to those skilled in the art, the present invention teaches a fundamental new device structure which can be used in a wide variety of integrated circuit device designs. Thus, not only can the foregoing description be modified and varied in a very wide number of respects, but an extremely broad range of equivalents is expressly asserted for the present invention, which is not limited except as specified in the following claims.

Claims: CLAIMS What is claimed is: 1) A field effect transistor comprising: A channel region comprising polycrystalline semiconductor material; source and drain regions connected to said channel region; and a gate positioned to apply an electric field to said channel region between said source and drain regions; Wherein said channel has an equilibrium carrier concentration of at least 1017 per cubic centimeter. 2) A field effect transistor comprising: A channel region comprising polycrystalline semiconductor material; Source and drain regions connected to said channel region; and A gate positioned to apply an electric field to said channel region between said source and drain regions. Wherein said channel has an equilibrium carrier concentration of at least five times 1016 per cubic centimeter; and Wherein said channel is less than 3000 Angstroms thick. 3) A field effect transistor comprising: A channel region comprising po lyc r ys tall i ne semiconductor materrial; Source and drain regions connected to said channel region; and A gate positioned to apply an electric field to said channel region between said source and drain regions; Wherein said channel has an equilibrium carrier concentration of at least five times 1016 Der cubic centimeter. 4) A field effect transistor comprising: a channel region comprising polycrystalline semiconductor material; source and drain regions connected to said channel region; and a gate positioned to apply an electric field to said channel region between said source and drain regions; wherein said channel has an equilibrium carrier concentration of at least 1017 per cubic centimeter, and a thickness less than 2000 Angstroms. 5. A field effect transistor comprising: a channel region comprising polycrystalline semiconductor material; source and drain regions connected to said channel region; and a gate positioned to apply an electric field to said channel region between saidd source and drain regions; wherein said channel has an equilibrium carrier concentration of at least five times 1016 per cubic centimeter, and is of the same conductivity type as said source and drain regions; wherein said channel is sufficiently thin to be depleted at zero applied gate voltage. 6. A field effect transistor comprising: a channel region comprising polycrystalline semiconductor material; source and drain regions connected to said channel region; and a gate positioned to apply an electric field to said channel region between said source and drain regions; wherein said channel has an equilibrium carrier concentration of a t least five times 1016 per cubic centimeter, and has the same conductivity type as said source and drain regions. 7) The transistor of Claim 1 wherein said polycrystalline material comprises polysilicon. 8) The transistor of Claim 2 wherein said polycrystalline material comprises polysilicon. 9) The transistor of Claim 3 wherein said polycrystalline material comprises polysilicon. 10) The transistor of Claim 4 wherein said polycrystalline material comprises polysilicon. 11) The transistor of Claim 5 wherein said polycrystalline material comprises polysilicon. 12) The transistor of Claim 6 wherein said polycrystalline material comprises polysilicon. l3) The transistor of Claim 7 wheein said polysilicon contains a substantial admixture of a passivating species at grain boundaries thereof 14) The transistor of Claim 8 wherein said polysilicon contains a substantial admixture of a passivating species at grain boundaries thereof. 15) The transistor of Claim 9 wherein said polysilicon contains a substantial admixture of a passivating species at grain boundaries thereof. 16) The transistor of Claim 10 wherein said polysilicon contains a substantial admixture of a passivating species at grain boundaries thereof. 17) The transistor of Claim 11 wherein said polysilicon contains a substantial admixture of a passivating species at grain boundaries thereof. 18) The transistor of Claim 12 wherein said polysilicon contains a substantial admixture of a passivating species at grain boundaries thereof. 19) The transistor of Claim 7 wherein said gate also comprises polysilicon, said gate and channel regions being doped with the same conductivity type. 20) The transistor of Claim 8 wherein said gate also comprises polysilicon, said gate and channel regions being doped with the same conductivity type. 21) The transistor of Claim 9 wherein said gate also comprises polysilicon, said gate and channel regions being doped with the same conductivity type. 22) The transistor of Claim 10 wherein said gate also comprises polysilicon, said gate and channel regions being doped with the same conductivity type. 23) The transistor of Claim 11 wherein said gate also comprises polysilicon, said gate and channel regions being doped with the same conductivity type. 24) The transistor of Claim 12 wherein said gate also comprises polysilicon, said gate and channel regions being doped with the same conductivity type.

Inventors: MALHI, SATWINDER, SHAH, RAJIV
Applicants: TEXAS INSTRUMENTS INCORPORATED
Application year: 1984
Main classification: H01L29
IPC codes: H01L27, H01L29