PROCESS FOR PREPARING AN IRON OXIDE

Abstract: A process is disclosed for the production of micaceous iron oxide wherein an iron chloride is oxidised at an elevated temperature in the presence of a salt of an alkali metal or alkaline earth metal, preferably sodium chloride. A reaction may be effected in a packed tower reactor comprising a refractory tube 7 containing an inert packing material e.g. aluminosilicate ceramic balls. The reaction charge including packing material, metallic iron and the salt is introduced via hopper 13. A tube 7 is externally heated by electrical resistance elements 10 and chlorine and an oxidising gas are introduced at inlet 8 and the off-gas removed at outlet 9. The micaceous iron reaction product is obtained from a melt film formed on the inert packing material, the film having a minimum thickness of 150 µm. Micaceous iron oxide is used as a pigment for the formulation of metal protective paints.

Description: This invention relates to a process for the preparation of an iron oxide. More particularly, this invention relates to a process for the production of micaceous iron oxide. Micaceous iron oxide is known as a naturally occurring ore which is a steel grey lamellar powder, also known as flake haematite. The flaky structure of the iron oxide is its distinguishing feature since chemically it is substantially ferric oxide (α-Fe₂O₃). The individual particles of micaceous iron oxide resemble thin plates and a major proportion has a size range of 5-150 µm. Micaceous iron oxide is used as a pigment for the formulation of metal protective paints. This use is based primarily on the lamellar nature of the oxide pigment. The plate-like or leafy structure of the micaceous iron oxide provides a physical barrier to the penetration of moisture and thereby reduces the chance of corrosion of the underlying metal substrate. Furthermore, the flakes of this grey pigment reflect solar radiation to a high degree, and a paint film containing this oxide maintains its reflectant ability for many years by shielding the binder from the ultra-violet radiation in sunlight. Micaceous iron oxide has been mined successfully in Spain, England and Austria. However, the deposits in Spain and England have now been exhausted, and the dominant world source is now in Austria, although the quality of the Austrian material is less satisfactory than were the English or were the Spanish oxides. Micaceous iron oxide has in recent years been subject to a considerable price escalation. Thus the paint industry has been faced with a reduction in quality and an increase in prices, coupled with some uncertainty of supply. Various methods have been described in the literature for the manufacture of synthetic micaceous iron oxide. For example, US Patent No. 3,987,156 describes a process for the production of micaceous iron oxide by subjecting an aqueous paste, obtained by mixing an aqueous ferric sulphate solution with an aqueous sodium hydroxide solution, to a hydrothermal treatment whereby micaceous iron oxide is formed in the shape of hexagonal lamellar crystals in conjunction with sodium sulphate. Similar types of processes involving reactions in aqueous media have also been described in Japanese Patent Publications 75 35097, 74 44878 and 74 90599. However, none of the above-mentioned processes has led to a commercially viable process, since they all require either a complicated series of reaction steps or the use of very specific operation conditions, generally in aqueous media. Other methods described in the literature relate to processes in which micaceous iron oxide is formed by the oxidation of an iron chloride feedstock. For example, US Patent No. 3,864,463 described the production of α-Fe₂O₃ in platelet form having a particle diameter of 2- 100 µm by reaction of ferric chloride in the vapour phase with an oxygen-containing gas at a temperature of 400-750°C wherein the reaction is performed in a static bed of generally spheroidal particles and in the presence of a specified amount of an alkali metal halide. Japanese Patent Application No. 1966-1535 describes the formation of a flaky oxide of iron, by introducing oxygen or an oxygen-containing gas into a liquid melt comprising a mixture of an iron (III) chloride with a metal chloride chosen from the Groups:- K, Na, Li, Sr and Ca chlorides. The oxidation reaction is carried out in the temperature range 500-950°C. Such methods comprising the oxidation of iron chlorides possess certain advantages in terms of the simplicity and speed of the chemical reactions involved. High conversions and rapid rates of reaction can be obtained at the relatively high temperatures employed. According to another example, US Patent No. 3,864,463 describes a process for the oxidation or iron chloride in the vapour phase. A particular problem of vapour-phase oxidation is that there is a severe tendency for iron oxide scale to accumulate on the reactor walls and on associated equipment, thereby causing problems in the efficient operation and maintenance of the reactor. Furthermore the process described in US Patent 3,864,463 comprises a vapour-phase oxidation reaction which is effected in the presence of a bed of inert particles. This gives rise to difficulties in the removal of the product iron oxide from the reactor and in the sticking of the bed material. The problems associated with vapour-phase oxidation can be largely circumvented by employing the oxidation of a melt, such as described, for example, in Japanese Patent Application No. 1966-1535, in which oxygen-containing gas is passed into a melt consisting of a mixture of ferrous or ferric chloride with a suitable added alkali- or alkaline-earth metal salt. The major function of the added salt, for example potassium chloride, is to suppress the volatility of ferric chloride by the formation of complex species such as KFeCl₄. The latter remains in the melt and enables oxidation to be effected without substantial loss of iron chlorides due to the vaporisation of FeCl₃. Oxidation of a melt containing iron chlorides as described in Japanese Patent Application No. 1966-1535 incurs other types of operational problems, however, which are caused by the reduction in mobility of such molten systems which occurs when the concentration of suspended iron oxide (formed as the product of the oxidation reaction) becomes relatively high. We have observed that when a suitable melt of iron chloride and one or more salts of the composition proposed is heated to a temperature in the range 600-750°C and oxidised by the passage of oxygen through the melt, the oxide product formed as a suspension in the melt acts to increase the consistency of the melt. This increase is such that when about half the iron chloride content of the melt has been converted to iron oxide and chlorine the partially-oxidised melt has the consistency of a thick mud which may block the oxygen inlet tube and prevent further progress of the oxidation reaction in this form. Furthermore, the relatively rapid rise in liquidus temperature of the iron chloride-added salt system as the iron chloride is consumed by oxidation effectively imposes an upper limit of 40-50 percent by weight of the conversion of iron chloride to iron oxide. It is therefore apparent that notwithstanding the apparent simplicity of the underlying chemistry involved in the oxidation of iron chlorides in the vapour-phase or in a molten phase to produce micaceous iron oxide, there are serious operational problems associated with each of these methods of carrying out the reaction. Thus, the present invention is based on the finding that micaceous iron oxide can be obtained by subjecting an iron chloride to oxidation with oxygen or an oxygen-containing gas at an elevated temperature in the presence of at least one salt of an alkali metal or alkaline earth metal. The reaction is effected in a packed-tower reactor in the presence of an inert packing material, wherein the weight ratio of salt:inert material to iron content (expressed as metallic iron) is from 0.25:4:1 to 10:20:1 such that the product formed from a film on the inert packing material has a minimum film thickness of 150 µm. The oxidation of the iron chloride occurs according to the chemical equations:- 3 FeCl₂ + 3 NaCl + 3/4 O₂ → 1/2Fe₂O₃ + 3NaCl + 2FeCl₃ (1) 2FeCl₃ + 3NaCl + 3/2 O₂ → Fe₂O₃ + 3NaCl + 3Cl₂ (2) These equations illustrate the use of sodium chloride as the added alkali- or alkaline-earth metal salt. Equation (2) refers to the oxidation of ferric chloride; Equations (1) and (2) together represent the oxidation of ferrous chloride, which first undergoes oxidation to give ferric chloride and micaceous iron oxide, followed by oxidation of the ferric chloride to give micaceous iron oxide and elemental chlorine. According to this embodiment, the iron chloride starting material may be, for example an iron chloride obtained as a by-product from the carbo-chlorination or sulpho-chlorination of minerals such as titaniferous and aluminous minerals e.g. ilmenite and bauxite, of which iron is a secondary component or from spent acid produced as a by-product of the pickling of ferrous metals with hydrochloric acid. When a titaniferous material such as ilmenite is chlorinated in order to extract its TiO₂ content as TiCl₄ by known chlorination processes and, in particular, by the so-called "carbochlorination" which is chlorination in the presence of carbon or a carbon-containing reducing agent, e.g. chlorination in the presence of carbon and/or carbon monoxide at temperatures between 800° and 1200°C, significant quantities of iron chloride are usually obtained as a by-product. This iron chloride may be ferrous or ferric, or a combination of both, depending on reaction conditions in the chlorinator. Similarly, when an aluminous material such as bauxite is chlorinated in order to extract its aluminium content as a volatile chloride by known carbo-chlorination or sulpho-chlorination processes, significant quantities of iron chloride are usually obtained as by-product. This iron chloride may be either ferrous or ferric chloride, or a combination of both, depending on reaction conditions in the chlorinator and on the method chosen to separate the by-product iron chloride from the primary product, aluminium chloride but it is more usually in the form of ferric chloride. Other suitable sources of iron chloride are, for example, iron chlorides by-produced in the chlorination of copper sulphide or nickel sulphide ores. Iron chloride by-products from all these mineral chlorination processes contain valuable chlorine in chemically combined form. According to another aspect of this embodiment of the invention, it is desirable, therefore, to recover these chlorine values, in particular for recycling to the chlorinator. This is particularly true when the chlorination of a titaniferous material such as ilmenite forms the first stage of the so-called chloride route to the TiO₂ pigment since the quantity of iron chloride by-produced is then considerable. In the case of the chlorination of an aluminous material such as bauxite the by-production of iron chloride, though generally less than with ilmenite, is still large and represents a serious loss of chlorine values. In both cases the environment problems posed by the by-production of large quantities of iron chlorides, with consequent need for disposal of these materials, are no less serious. A further need is an industrially feasible process for the recovery of chlorine values from substantially anhydrous iron chloride derived from aqueous solution, in particular, from substantially anhydrous ferrous chloride derived from spent pickle acid which accumulates in the final stages of steel manufacture. The predominant use of such spent pickle acid is the manufacture of red iron oxide pigment, West Germany being the major centre of productions. One disadvantage of this use of spent pickle acid is that high processing and capital costs make it economic only on a very large scale so that much spent pickle acid is wasted. Another disadvantage is that ferrous chloride is generally reacted with lime to precipitate ferrous hydroxide, leaving calcium chloride in solution for waste disposal, and, thus, the chlorine values in the ferrous chloride are lost. Another, although less widely used, method of utilising spent pickle acid is to spray-roast the spent pickle liquour to produce a weak hydrochloric acid (about 18% compared with the usual 36% level of concentrated hydrochloric acid). However, this method is energy-intensive and results in a ferric oxide by-product of little pigmentary value. There is therefore a need in the industry for a new method for the treatment of spent pickle acid in which the chlorine values from the contained ferrous chloride are recovered and in which an iron oxide of significant industrial utility, micaceous iron oxide, is produced. According to a preferred aspect of the invention metallic iron is used as feedstock to form an iron chloride as disclosed in European Patent Application No. 84300882.2 of which the present application is a divisional. According to another aspect of this embodiment, the iron chloride starting material may be obtained by direct reaction between iron metal and elemental chlorine. Thus the metallic iron feedstock is oxidised, not directly, but by first forming iron chlorides and then oxidising these. This step is essential to the selective formation of micaceous iron oxide rather than other types of oxide (e.g. red iron oxide, magnetite etc) which form when iron is oxidised directly in air or oxygen under various conditions. A number of processes for carrying out this reaction are known. The iron metal and elemental chlorine may be fed into the reactor used in the process according to the present invention to generate the iron chloride in situ , according to the chemical equation:- 2Fe + 3Cl₂ → 2FeCl₃ (3) Since this reaction occurs in the presence of added alkali- or alkaline-earth metal salt, the reaction is more realistically represented, using sodium chloride as the added salt, by the chemical equation:- 2Fe + 3Cl₂ + 3NaCl → 2 FeCl₃ + 3NaCl (4) Iron metal may also be used to reduce a ferric chloride feed material, in the presence of a suitable added salt, to form ferrous chloride which is subsequently oxidised to micaceous iron oxide according to the invention. The reduction reaction is represented by the chemical equation:- 2FeCl₃ + 3NaCl + Fe → 3FeCl₂ + 3NaCl (5) Equation (5) again illustrates the use of sodium chloride as the added salt. Another method of carrying out the reaction process of this invention is by external recycle of chlorine. Thus a melt consisting of NaFeCl₄ (or NaFeCl₃) is oxidised to micaceous iron oxide and chlorine according to equation (6) :- 2NaFeCl₄ + 3/2O₂ → Fe₂O₃ + 2NaCl + 3Cl₂ (6) The gaseous chlorine generated by this reaction is fed to a second reactor where it reacts exothermically with iron according to equation (3) above and the ferric chloride produced is then mixed with salt and used as the feed material for the first (oxidation) reactor. Alternatively the chlorine could react with a mixture of iron and salt thus directly forming a liquid NaFeCl₄ (or NaFeCl₃) feed for the first (oxidation) reactor. The first (oxidation) reactor could be a packed tower, salt bath or any other suitable gas/liquid reactor, and the second (chlorination) reactor any type of gas/solid reactor such as a packed tower. The preferred method of carrying out the process according to the present invention is, however, to use a metallic iron feedstock to provide an iron chloride and then oxidise this. The metallic iron may be ferrous scrap, in the form of turnings, borings, swarf, punchings, coupons, or the like. There are no particular limitations regarding the size, shape, or other preferred physical form of the metallic iron. It is not normally found necessary to etch, degrease or otherwise pre-treat the metallic iron before use. The use of metallic iron feedstock is advantageous because it is cheap, readily available, easily handled and does not require prior treatment. This preferred embodiment of the invention has the additional advantage that the process does not result in the co-production of substantial proportions of chlorine gas. The co-production of chlorine gas gives rise to the need for handling, storage and liquefaction of the chlorine and this can impose a severe penalty in terms of the capital cost of equipment needed for chlorine handling. These problems are avoided by this embodiment of the present invention which uses metallic iron feedstock. The added alkali- or alkaline-earth metal salt may be any salt which acts to suppress or reduce the volatility of ferric and/or ferrous chlorides. Examples are the chlorides, bromides, iodides and sulphates of the alkali- and alkaline-earth metals. The preferred salts are alkali metal chlorides, which form complexes with ferric chloride of general formula MFeCl₄ (where M is an alkali-metal cation), and which thereby greatly reduce the volatility of ferric chloride. Of the alkali-metal chlorides, the most preferred salt is sodium chloride, for reasons of its low cost, ready availability, and ease of formation of NaFeCl₄ with ferric chloride. Various forms of sodium chloride may be employed, e.g. granular sodium chloride, rock-salt, and the like. Any suitable oxidising gas may be employed but preferably air or oxygen. The choice of oxidising gas depends on factors such as the reaction rate desired, the temperature of reaction, the reactor heat-load, the ratio of metallic iron to added salt, and the ratio of reactants to inert surface area in the reactor. The preferred reaction temperature is in the range of from 500°C to 1000°C most preferably from 650 to 850°C. The salt:iron ratio falls within the range of 0.25:1 to 10:1. The reaction may be performed batch-wise or continuously. The reaction is effected in a packed tower, the inert packing material being a hard impermeable material. Regular spheres, such as ceramic balls have been found to be particularly suitable. The micaceous iron oxide product is formed from a melt film formed on the ceramic balls wherein the film has a thickness of at least 150 µm. The film thickness must be controlled so as to ensure the formation of a micaceous product having acceptable properties as previously defined. An adequate supply of chlorine or chloride within the reactor must be maintained. In particular when metallic iron is employed as an iron source an amount of chlorine must be supplied which is at least sufficient for the formation of an iron chloride and its subsequent oxidation. The weight ratio of inert material (ceramic balls) to iron content (expressed as metallic iron) is 4:1 to 20:1. A further advantage of the process according to the invention is that it consumes very little energy due to the fact that the overall reaction, the oxidation of Fe to Fe₂O₃ is exothermic (830524 joules) (198.5 k cal) per mole of Fe₂O₃). Thus, once initiated the reaction is self-sustaining. The micaceous iron oxide product of the process according to the invention preferably has a major proportion with a maximum particle size in the range of 100 to 200µm, more preferably 100 to 150 µm and a preferred median size range of about 35 to 50µm. Desirably the product is substantially wholly in the form of lamellar platelets,having a thickness of at least 1 µm and more preferably about 5µm. The aspect ratio (length:width) is preferably not more than 3:1 since it has been observed that a higher ratio gives rise to an inferior performance in a paint medium. Preferred operating conditions are described in more detail in the following description with reference to the accompanying drawings wherein: Figure 1 is a longitudinal section through an embodiment of an apparatus suitable for carrying out the process according to the invention wherein the reactants are distributed over an inert packing material; Figure 2 is a schematic diagram of one embodiment of a ball-tower reactor suitable for carrying out the process according to the invention; and Figure 3 is a schematic diagram of another embodiment of a ball-tower reactor suitable for carrying out the process according to the invention. According to a first embodiment of the invention the chlorination of metallic iron, is effected in the presence of a suitable added salt e.g. sodium chloride, to give ferric chloride. The ferric chloride is then oxidised, by using an oxidising gas, to produce micaceous iron oxide and chlorine gas. The reactions involved (using sodium chloride as the salt) are represented by Equations (2) and (4) above. The reaction system is so designed that the chlorine gas formed as a co-product of the oxidation reaction according to Equation (2) reacts elsewhere in the reactor with metallic iron, forming ferric chloride according to Equation (4). The ferric chloride thus formed is then oxidised, according to Equation (2), producing micaceous iron oxide and re-generating chlorine gas, and so on. This reaction sequence is most easily achieved in a packed-tower reactor as shown in Figure 1. This contains the reactants (metallic iron and salt) distributed over an inert packing material. This material should be hard and impermeable such as ceramic balls, pebbles, pea gravel or impermeable refractory pieces. The reactor shown in Figure (1) consists of a vertical refractory tube 7, 200 mm internal diameter x 1500 mm total length, provided with gas inlet and outlet ports 8 and 9. The central portion (1000 mm long) of the tube was heated externally by means of electrical resistance elements 10 mounted in the thermally-insulated steel jacket 11. Sheathed thermocouples 12 were inserted at various levels into blind holes drilled in the tube 7. During continuous runs, solid reactants were added to tube 7 by means of the gas-tight hopper 13. A pneumatically-operated gate-valve 14 at the base of the tube served to discharge the reaction product, in the form of ceramic balls coated with micaceous iron oxide and salt. In operation, the reactor was charged with a mixture of aluminosilicate ceramic balls 12 mm in diameter, metallic iron and sodium chloride. The preferred weight ratio of balls:reactants is within the range 4:1 to 20:1. In addition, a "start-up" layer containing ferric chloride or chlorine gas, metallic iron, sodium chloride and ceramic balls was initially placed in the reactor below the main charge. The function of this "start-up" layer was to react with the oxidising gas admitted to the bottom of the reactor, to form synthetic micaceous iron oxide and chloride according to Equation (2). The micaceous iron oxide and sodium chloride remain as a coating on the ceramic balls, whilst the chlorine passes upwards and reacts with the metallic iron in the reactor charge above the "start-up" layer to form ferric chloride according to Equation (4). The ferric chloride thus formed remains trapped or associated with the sodium chloride and is further oxidised, according to Equation (2), to form further synthetic micaceous iron oxide and chlorine gas. This type of packed-tower reactor provides a particularly elegant and simple means of directly feeding metallic iron, sodium chloride and oxygen or air into a single reactor, and by employing the intermediate formation and oxidation of ferric chloride, forming synthetic micaceous iron oxide directly, without the co-production of chlorine. The micaceous iron oxide is produced, in admixture with sodium chloride, as a coating on the ceramic balls. Removal of the micaceous iron oxide is achieved easily and rapidly by leaching the coated ceramic balls in water. Another advantage of the process according to the present invention is the exothermic nature of the overall reaction sequence. The oxidation of metallic iron to give iron oxide is substantially more exothermic than the oxidation of ferrous or ferric chloride to iron oxide which means that in theory, no heat should need to be supplied to the reactor to maintain the required reaction temperature. The reaction can be operated either continuously or batch-wise, preferably batch-wise. In continuous operation, the ceramic balls are gradually descending down the reactor during the course of the operation, and are continuously or intermittently discharged from the bottom of the reactor. After water-leaching of the discharged balls to remove the micaceous iron oxide, the balls are dried and re-cycled to the top of the reactor, together with a further supply of metallic iron and salt. All the chlorine generated by the oxidation reaction according to Equation (2) remains within the reactor, and forms ferric chloride with the descending metallic iron charge. No chlorine therefore emerges from the reactor as "off-gas". In batch operation, the chlorine evolved as co-product from the oxidation reaction according to Equation (2) gradually moves up the tower, ultimately emerging as an off-gas which is fed into a second reactor to form the "start-up" layer of ferric chloride. Batchwise operation of the process may therefore require more than one reactor to accommodate transfer and re-use of chlorine values as the process proceeds. With reference to Figure (2) an apparatus suitable for carrying out the process according to the invention is schematically illustrated and comprises a refractory reactor tube 7 provided with reaction end-plates 15 and having an inlet 16 for an oxidising gas at one end of the tube 7 and an outlet 17 at the opposite end for an off-gas. The reactor tube 14 is packed with an inert support material 18 preferably ceramic balls and contains a reactant charge 19, the iron source and added salt. The apparatus is shown vertical but a horizontal reactor may also be employed. An apparatus suitable for carrying out the process according to the invention is illustrated in more detail in Figure (3). The reactor consists of a steel shell (55 cm diameter) lined with a castable refractory 10 cm thick 20. A taper (1 in 40) was cast in the refractory liner to aid discharge of the reaction products. Refractory lined hinged lids are fitted to the top and bottom 21 and 22 of the reactor and these are adapted to be bolted onto the reactor to form a gas-tight seal. The reactor is packed with a layer of inert packing material 34, a layer of a mixture of inert packing material, iron and salt 35 and finally with a layer of a mixture of inert packing material and salt. The charge of iron, salt and inert packing material can be loaded manually into the reactor, a gas burner (not shown) firing through a gas inlet 23 in the bottom lid is used to pre-heat the bottom of the charge. Gases, air and chlorine, are drawn through the reactor, leaving via a gas exit port 24 and a caustic soda gas scrubber by a vacuum pump. Progress of the reaction up the column of charge is followed by the increase in temperature recorded by the thermocouples, 25 to 33 and by monitoring the chlorine evolved with the off-gas. Completion of the reaction is indicated by the end of chlorine evolution and by the absence of any further temperature rise in the reaction bed. Example 1 This was a continuous run, for which the reactor and hopper illustrated in Figure 1 were charged with a mixture of ceramic balls 12 mm in diameter, metallic iron in the form of mild steel coupons 10 mm x 10 mm, and sodium chloride granules, in the following proportions:- Ceramic balls 14,400 g Metallic iron 700 g Salt 700 g The "start-up" layer placed below the main charge had the following composition:- Ferric chloride 260 g Metallic iron 60 g Sodium chloride 175 g Ceramic balls 3600 g The reactor and contents were heated under nitrogen to 700°C. Oxygen at 5 litres/minute was then passed into the bottom of the reactor via the gas inlet tube 8, and by periodically operating the gate-valve 14 the reactor contents were discharged from the reactor 7 into a receiver vessel (not shown in Figure 1). Complete discharge of the reactor contents was achieved in 5 hours 45 minutes. The coated balls obtained as the crude product from the reactor were divided in a random manner into smaller lots using a sample splitter. One of these smaller lots was leached with water to release the micaceous iron oxide, which was filtered off, washed, and dried. The micaceous iron oxide thus produced was in the form of thin, translucent lamellar particles, of size range 5 to 200 microns. Weighing and chemical analysis carried out on this sample of coated balls gave the following results: Total weight of ceramic balls 1882 g Weight of Fe₂O₃ 25.5 g Weight of FeCl₃ 0.1623 g Weight of FeCl₂ 0.254 g no metallic iron present These results therefore indicated 99 percent conversion of the initial iron content of the reactor to micaceous iron oxide. Example 2 This was a batch run, in which the hopper 13 and gate valve 14 of the reactor shown in Figure 1 were removed and replaced by gas-tight end-plates. Before the run, the reactor was charged with a "start-up" layer of the following composition:- Ceramic balls 6000 g Metallic iron 125 g Ferric chloride 762 g Sodium chloride 393 g Above this was placed a main reactor charge, which had the following composition:- Ceramic balls 24,000 g Metallic iron 3,000 g Sodium chloride 3,000 g The metallic iron used for this run was in the form of scrap iron borings, ranging in particle size from fine powder up to pieces ca. 5 mm across. This material was used without any pre-treatment such as degreasing. The reactor was heated under nitrogen to 740°C. The nitrogen supply was then shut off, and air from a compressed air line was passed at 40 litres/minute into the reactor via the inlet tube 8 at the reactor base for a timed period of 8 hours 30 minutes. The sodium hydroxide gas-scrubber solution was periodically sampled and analysed for absorbed chlorine during the run. This analysis showed that 478 grams of chlorine were evolved during the first 8 hours of the run. No further chlorine was evolved during the final 30 minutes of the run, indicating that the reaction had been taken to completion. The weight of chlorine evolved corresponded to a conversion of 95.7 percent, based on the initial chloride content of the reactor. At the end of the run the air supply was shut off and the reactor and contents allowed to cool, after which the reactor end-plates were taken off and the reactor contents were knocked out using an iron bar. The crude product, in the form of ceramic balls coated with micaceous iron oxide and sodium chloride, was split into fractions corresponding to various levels in the reactor. The weights and the chemical analysis results after water-leaching of three of these fractions, together with the corresponding conversions of the iron content to Fe₂O₃, are given below:- No evidence of unreacted metallic iron was found. The micaceous iron oxide, after leaching, filtration, washing and drying, was in the form of thin lamellar platelets of particle size 10 - 170 µm. Example 3 This was a batch run carried out in the reactor shown in Figure 1, using the same proportions of starting materials and run procedure as for Example 2, except that oxygen was used as the oxidising gas. The reactor and contents were heated up to 710°C under nitrogen, whereupon the nitrogen flow was shut off and oxygen at 10 litres/minute was passed into the reactor via the gas entry tube in the reactor base for 8 hours 20 minutes. The sodium hydroxide gas-scrubbing solution was monitored as described in Example 2, from which it was indicated that 464 g chlorine, corresponding to 93 percent of the initial chloride content of the reactor, had been evolved after 8 hours. At the end of the run, the oxygen supply was discontinued and the reactor and contents were allowed to cool. The reactor contents, consisting of ceramic balls coated with micaceous iron oxide and sodium chloride, were then removed, weighed and samples taken and leached and analysed as before. The results of weighing and chemical analysis of two samples of coated ceramic balls taken from two different heights in the reactor are given below, and indicate the high conversion of metallic iron to micaceous iron oxide:- No evidence of unreacted metallic iron was found. The micaceous iron oxide produced was similar in appearance and particle size to the product formed from the run described in Example 2. Example 4 The procedure was carried out in a horizontal mullite reactor tube, 50 mm internal diameter, 60 mm outside diameter, and 1000 mm long. The constituents for the formation of a ferrous chloride layer were prepared by mixing 270g 1.27 cm aluminosilicate balls 65.3g FeCl₃ 11.3g Fe 35g NaCl This layer occupied 13 cm of length in the middle of the tube and the remainder was packed with clean 1.27 cm aluminosilicate balls. The tube was heated by the electrical furnace to 700°C under a flow of N₂ (600 ml/min). At this temperature O₂ (600 ml/min) was introduced and the chlorine evolved was collected in 5% NaOH solution contained in Dreschel bottles, for subsequent analysis using Kl/thiosulphate and by weight. A Kl "guard" Dreschel bottle was placed in series with and downstream of the NaOH Dreschel bottles. No gas was evolved until 5 mins after introduction of O₂, when chlorine followed by oxygen was evolved. The product was recovered by removal of the coated support balls from the tube, followed by leaching in water, filtering off the iron oxide, and analysis of the leach liquor for Fe²⁺, Fe³⁺ and Cl from which mass balance data was obtained. The experiment was performed in duplicate, with the following results:- Example 5 The procedure was as described in Example 4 using the same apparatus except that O₂ was introduced at a flow rate of 300 ml/min. The following results were obtained. Example 6 The procedure was as described in Example 4 except that the oxidising gas introduced was 600 ml N₂ + 600 ml O₂ per minute. The results were as follows:- Example 7 A reaction was performed using the apparatus described in Figure 3. A reaction charge consisting of 30 cm deep lower layer of 2.53 cms diameter refractory balls (40 kg) to aid gas and heat distribution 34, a 90 cm deep charge layer consisting of a mixture of 1.265 cms diameter refractory balls, (96 kg), iron (12 kg), salt (12 kg) 35 and finally a 10 cm deep layer of a mixture of (1.265 cms) refractory balls (16 kg) and salt (2 kg) 36 was loaded into the reactor. The bottom of the charge was then heated using the gas burner bolted onto the bottom lid until the temperature recorded by thermocouple 25 reached 775°C. Reaction gases were fed into the tower consisting of chlorine (25 1/minute for 60 minutes) and air (12 m³/hour for 3 hours 15 minutes). Thus the temperatures recorded by thermocouple 29 about halfway up the reaction bed rose from 366°C to 803°C in 45 minutes and by thermocouple 32, the top of the charge, from 186°C to 783°C in 120 minutes. Chlorine evolution reached a maximum after 145 minutes. Total chlorine recovery amounted to 3.55 kg representing 80% of the calculated chlorine input (4.4 kg). On completion of the reaction the bottom and top lids 21 and 22 were unbolted and the charge pushed out into a collection bin using a hydraulic jack. The refactory balls coated with salt and micaceous iro oxide were then washed with 200 litres of water which dissolved the salt releasing the micaceous iron oxide product. This micaceous iron oxide was filtered, washed free of soluble chloride and dried. 15.2 kg of micaceous iron oxide was obtained, a yield of 89%. Unreacted iron recovered weighed 913 g (7.6% of feed). Soluble iron chlorides in the wash liquor amounted to 340 g FeCl₂ and 39g FeCl₃.

Claims: A process for the preparation of micaceous iron oxide by oxidising an iron chloride with oxygen or an oxygen-containing gas at an elevated temperature in the presence of at least one salt of an alkali metal or alkaline earth metal, characterised in that the reaction is effected in a packed-tower in the presence of an inert packing material wherein the weight ratio of salt:inert material to iron content (expressed as metallic iron) is from 0.25:4:1 to 10:20:1 such that the micaceous iron oxide product is formed from a melt film on the inert packing material and that the film has a minimum thickness of 150 µm. A process according to claim 1, wherein the reaction is effected at a temperature of 500°C to 1000°C. A process according to claim 2, wherein the reaction is effected at a temperature of 650°C to 850°C. A process according to any of claims 1 to 3, wherein the salt is a chloride, bromide, iodide or sulphate of an alkali metal or alkaline earth metal. A process according to claim 4, wherein the salt is sodium chloride. A process according to any of claims 1 to 5, wherein the iron chloride is obtained as a byproduct from the carbo-chlorination or sulpho-chlorination of which iron is a secondary component. A process according to any of claims 1 to 5, wherein the iron chloride is obtained from spent acid produced as a by-product of the pickling of ferrous metals with hydrochloric acid.

Inventors: LAUNDON, ROY DAVID, TURNER, JOHN HARRY WALLICE, WICKENS, ANTHONY JOHN
Applicants: COOKSON LAMINOX LIMITED
Application year: 1984
Main classification: C01G49
IPC codes: C09C1, C01G49, B01J10