POLYURETHANE COATING COMPOSITIONS

Abstract: A two-part coating kit, particularly for spraylining pipes, comprises two compositions to be mixed together and cured in situ. The first composition comprises: i) a water-soluble or dispersible alkaline reacting mate­ rial which reacts with carbon dioxide, ii) an emulsifying agent or precursor thereof and iii) at least one polyol having primary hydroxyl groups which is resistant to hydrolysis under alkaline conditions; and the second composition comprises: i) an isocyanate-terminated polyurethane prepolymer derived from the reaction of one or more open chain polyols and a liquid polyisocyanate, said prepolymer being dis­ solved in an aprotic organic solvent; ii) additional liquid polyisocyanate and optionally iii) a particulate mineral filler which is substantially free from moisture.

Description: "POLYURETHANE COATItlr, COMPOSITIONS" This invention relates to materials for use in coating tubes and pipes and more especially to the coating of pipes such as sewerage mains the surfaces of which have become damaged by pro]onged use. The system is essentially based upon the formation in contact with the internal surface of the pipe or main of a cured polyurethane coating employing an aqueous emulsion of previously emulsified polyols and an isocyanate terminated polyurethane prepolymer which are only brought into contact in a mixing device and then sprayed on to the already cleaned surface of the pipe to be. treated, Additional ingredients are incorporated into one or both of the components being sprayed when it is desired to control the thickness and/or uniformity of the resulting coating and also for controlling the physical properties of the applied coating. It is also desirable to apply a coating which cures to a major extent in a short time without substantial frothing and accordingly the system incorporates a suitable alkaline reacting material. Accordingly the present invention provides a two-part coating kit comprising first and second compositions to be mixed together and cured in situ, wherein the first composition comprises: i) a water-soluble o,r,,dispersible alkaline reacting material which reacts with carbon dioxide; ii) an emulsifying agent or precursor thereof and iii) at least one polyol having primary hydroxyl groups which is resistant to hydrolysis under alkaline conditions; and wherein the second composition comprises: i) an isocyanate-terminated polyurethane prepolymerderived from the reaction of one or more' open chain polyols and a liquid polyisocyanate, said prepolymer being dissolved in an aprotic organic solvent; ii) additional liquid polyisocyanate and optionally iii) a particulate mineral filler which is substantially free from moisture. To prepare the final coating composition, the first composition is mixed with water to form an emulsion which is mixed, immediately prior to spraying with the second composition to form the final polyurethane coating. The mixing proportions should be such that the isocyanate terminated prepolymer and liquid polyisocyanate of the second composition are present in an amount which is at least sufficient to react with the polyols present in the first composition, leaving an excess of isocyanate groups which can react with the water present to form amino groups which in turn can take part in cross-linking reactions with further isocyanate groups. It is preferred that the first composition also contains an inert reinforcing inorganic particulate material; this may act as a thixotropic agent when the first and second compositions have been admixed and the resulting mixture is being applied to the surface of the pipe being treated. In one embodiment of the invention the first pack is admixed with water and the emulsion prepared at the work site before admixture with the second pack. This obviates the necessity of taking water to the site when it is already available there. The water-soluble or dispersible alkaline material is preferably quick lime but it can also be strontium or barium oxide. When one of these materials is used and the emulsifying agent is casein the true emulsifying agent, which is then a salt of casein, is also formed at the work site before admixture of the first and second compositions occurs. In this case the casein is a precursor of the actual emulsifying agent. Sodium silicate solutions can also be used as the alkaline material with suitable emulsifying agents and so also can sodium and potassium hydroxides but owing to the hazards involved these are not preferred. The proportion of the alkaline material is preferably 30 to 50 wt % of the first composition before water is added. As already indicated the emulsifying agent, in the form of its precursor, is preferably casein. However other emulsifying agents can also be used in the first composition and there is no limitation as to the type,i.e. the emulsifying agent can be cationic, anionic or non-ionic in nature. Casein is however a preferred material on account of its ready availability and relatively low cost. The emulsifier is preferably used in an amount of 2-4 wt % of the first composition. The first composition preferably includes, in addition to the polyol (iii) mentioned above, a saturated water-soluble polyol having primary hydroxyl groups. Propylene glycol is preferred but other polyols have proved equally successful in practice including glycerine, ethylene glycol, butane diol, erythritol, dextrose and sucrose. Thus materials having botM primary and secondary hydroxyl groups can be used. The polyols having primary hydroxyl groups which are resistant to hydrolysis under alkaline conditions are preferably polycaprolactones but may also be other materials such as liquid polyethylene glycols and polyoxypropylene glycols. These materials should react with the polyisocyanate before the latter reacts with the water, since premature reaction of the polyisocyanate with water tends to plasticise the final product. Less resistant to hydrolysis under alkaline conditions are the polyester polyols derived from such acids as adipic and linoleic acids which may nevertheless be used. Mixtures of such materials may be used e.g. a mixture of polycaprolactones which consists of a diol and a triol. The total content of polyols in the first composition is preferably 20 to 40 wt %. The first inert reinforcing inorganic particulate material which may be, and preferably is, a constituent of the first composition, is present essentially as a reinforcing filler but may also impart other properties to the final product. Calcined china clay may be used and has the advantage that when dispersed in water, it produces a creamy thixotropic material. Thus when the mixture of the first and second composition containing calcined china clay is uniformly applied to the interior of a pipe undergoing treatment the thixotropic effect exerted ensures'Uthat the product remains in position and so gives a uniform final coating. A mixture of such reinforcing agents may be used. The filler is preferably used in amount of 10 to 25 wt % of the first composition, before water is added. An additional ingredient which may be present in the first composition is a liquid epoxy resin. The liquid epoxy resin has also been found to behave as a reactive diluent. Suitable liquid epoxy resins may be obtained by the reaction of Bisphenol A with epichlorohydrin and may have an epoxide equivalent of 175-189. The epoxy resin may suitably be included in an amount up to 20 wt % of the first composition, before water is added. Another additional ingredient which may be included in the first composition, suitably in an amount up to 2 wt %, is hydroxypropyl cellulose. This helps to provide the required thixotropy and to prevent separation during pumping. A preservative for the emulsifier may also be included in the first composition, preferably in an amount not exceeding 1 wt 8. The isocyanate-terminated polyurethane prepolymer is derived by the reaction between a saturated open chain polyol and a liquid polyisocyanate. The polyisocyanate is preferably one which is sufficiently reactive to use without a catalyst and which also has a low vapour pressure at ambient temperatures. A convenient choice is diphenylmethane -4,4' - diisocyanate. The saturated open chain polyol preferably contains monocyclic aryl groups in the molecule and preferably contains secondary hydroxyl groups. It may conveniently be the reaction product of one molecule of diphenylolpropane with two molecules of 1,2 -dihydroxypropane. Other aromatic polyols may also be used, as may high molecular weight (e.g. > 1000)polyether diols. The liquid polyisocyanate should be present in excess so as to ensure a product containing terminal isocyanate groups. The reaction is carried out in a solvent for a polyurethane precursor which is free from reactive hydrogen atoms. Ester ethers of alkylene glycols such as ethylene glycol monoethyl ether acetate are eminently suitable for this purpose, as are aromatic aprotic solvents such as xylene. To the solution of the polyurethane precursor there is added a polyisocyanate which is intended to react with the polyols in the first composition and is therefore added in a sufficient proportion to achieve this result when the two compositions are metered prior to mixing. Alternatively the same result may be achieved by adding enough diisocyanate to the polyol to ensure that a sufficient amount remains unreacted: the diisocyanate is best added in portions. The additional polyisocyanate reduces the viscosity of the second composition. The second composition is preferably made from 45 to 65 wt % of polyisocyanate, 12 to 25 wt % total of polyols, 3 to 6 wt % of filler and 15 to 35 wt % of solvent. As mentioned above, the second composition includes a particulate mineral filler which is at least substantially free-from moisture. The filler is preferably an organo-modified fumed silica the surface of which has been rendered hydrophobic. Other particulate materials may be used so long as they are substantially free from moisture or have been pretreated so as to render them substantially free from moisture. This is necessary on account of the presence in the pack of unreacted polyisocyanate which,as already pointed out, is intended to react with the polyol components of the first pack after mixing has taken place. When the universal filler is an organo modified fumed silica it behaves as a thixotropic thickening agent in the final composition and also exerts a reinforcing effect. Finally, the second composition may include a small amount ( preferably not more than 0.1 wt %) of a catalyst to promote the reaction of excess isocyanate groups with water. It will be appreciated that three of the above discussed ingredients can impart thixotropic properties to the final mixture which is sprayed on to the cleaned surface of the pipe or tube undergoing treatment. When a uniformly coated pipe is desired at least one of these ingredients should be present in one of the compositions and it is preferred that one should be present in each composition. Most preferably all three ingredients should be included in the two compositions. The first composition, when water has been added is one in whIch the aqueous phase of the resulting emulsion is the continuous phase. To ensure this result, an excess of water should be present. When the first and second compositions are mixed the second should be added to the first in a proportion which brings about an inversion of the emulsion so that the aqueous soluttion is discontinuously dispersed in a continuous organic phase of polyurethane prepolymer solvent free from reactive hydrogen atoms and polyols. The presence of the ingredient'or ingredients which impart thixotropic properties ensures that when the two compositions have been thoroughly mixed the emulsion having the continuous phase is a thixotropic one. This thixotropic emulsion is then sprayed on to the surface of the cleaned pipe or tube undergoing treatment and, due to its thixotropic properties, coats the area which it contacts and remains there. This ensures the application of a uniform coating. Coating of varying thickness can be applied in this way. The invention will be further illustrated in the following examples. EXAMPLE 1. Two compositions were made up as follows: First Composition (aqueous emulsion): Ingredients Weight % Water 32.70 Hydrated lime 22.92 Casein 1.64 Monopropylene glycol 9.17 Liquid Epoxy resin 9.51 Calcined china clay 12.98 Polycaprolactone Diol m.w 550 -, 5.54 Polycaprolactone Triol m.w 540 5.54 Second Composition: Ingredients Weight % Di-isocyanate 52.05 Secondary alcohol 15.96 Ethylene glycol monoethyl ether acetate 27.76 Modified fumed silica 4.23 The polycaprolactone diol and triol used were materials sold under the trade names Capa 200 and Capa 305 respectively. The liquid epoxy resin used was one sold under the trade name Grilon 16-05. The liquid di-isocyanate used was sold under the trade name Desmodur VL and is reputed to be a commercial grade of diphenylmethane - 4,4' -diisocyanate. The secondary alcohol is sold under the trade name Dianol 33 and is reputed to be a condensation product of diphenylolpropane with 2 molecules of 1,2 -dihydroxypropane. It is readily soluble in ethylene glycol monoethyl ether acetate. The diisocyanate and secondary alcohol were reacted in the proportion of four molecular proportions of dirisocyanate to one molecular proportion of secondary alcohol thus producing an socyanate terminated condensation product and an aditional two molecular proportions of diisocyanate is added to the condensation product. The modified fumed silica employed was one sold under the trade name Aerosil R972 and has a hydrophobic surface. It has both thixotropic and reinforcing properties. It has been found that a modest reduction can be made in the amount of lime used in the above formulation to bring about very slight foaming. This ensures that the possibility of shrinkage in the applied coating is eliminated. There are certain advantages in the use of quick lime which is slaked in situ as quick lime of more constant composition can be obtained and this enables closer control of the applied product to be secured. The alkaline material reacts with carbon dioxide which is liberated by the reaction of water with isocyanate groups thus acting as a carbon dioxide ,scavenger. The isocyanate groups are those present in components of the second compositionsit will be apparent that the alkaline material may be present in a sufficient amount to react with all the carbon dioxide thus liberated or it may be slightly less than this amount so that very slight foaming can occur: this can eliminate the occurrence of shinkage in the applied coating and thus afford better protection to the surface of the coated pipes and mains. EXAMPLE 2 The process of Example 1 was repeated for the following compositions: First Composition (Aqueous Emulsion): Ingredients Weight % Water 49.18 Casein 1.64 Hydrated lime 22.54 Calcined china clay 10.24 Hydroxypropyl Cellulose 0.34 Non-Toxic preservative 0.30 Polycaprolactone triol 15.76 (capa 305) Second Composition: Ingredients Weight t Diisocyanate 59.40 (Desmodur VL) Polyether diol 7.39 Secondary alcohol 10.25 (Dianol 33) Xylene 17.95 Modified fumed silica 4.23 Tertiary Amine Catalyst 0.05 The polyether diol was a polyoxpropylene-based diol having a molecular weight of approximately 2000. The non-toxic preservative was included in the first composition to stabilize the casein. The catalyst in composition 2 was a highly specific tertiary amine catalyst sold by Union Carbide Corporation under the trade mark NIAX Al. Compared with the compositons of Example 1, those of Example 2 were found to have improved reactivity and to give a stronger, more elastic coating with improved structure. The composition as sprayed was also more hydrophobic and was therefore easier to use on wet surfaces. The two compositions may be mixed and sprayed to form a coating, such as a self-supporting or structural lining within a sewer or other pipe to rennovate the latter. The spray coating or lining may be applied to pipes which are too small in diameter to allow human access, for example by the remotely controlled apparatus disclosed in our copending Application No: filed on even date.

Claims: CLAIMS 1. A two-part coating kit comprising first and second compositions to be mixed together and cured in situ to form a polyurethane coating, characterised in that the first composition comprises: i) a water-soluble or dispersible alkaline reacting material which reacts with carbon dioxide; ii) an emulsifying agent or precursor thereof and iii) at least one polyol having primary hydroxyl groups which is resistant to hydrolysis under alkaline conditions; and wherein the second composition comprises: i) an isocyanate-terminated polyurethane prepolymer derived from the reaction of one or more open chain polyols and a liquid polyisocyanate, said prepolymer being dissolved in an aprotic organic solvent; ii) additional liquid polyisocyanate and optionally iii) a particulate mineral filler which is substantially free from moisture. 2. A coating kit according to claim 1 wherein the first composition additionally comprises a saturated water-soluble polyol having primary hydroxyl groups. 3. A coating kit according to claim 1 or claim 2 wherein the first composition additionally comprises a liquid epoxy resin. 4. A coating kit according to any preceding claim wherein the first composition additionally comprises hydroxypropyl cellulose. 5. A coating kit according to any preceding claim wherein the first composition additionally comprises an inert reinforcing inorganic particulate material. 6. A coating kit according to claim 5 wherein said inorganic particulate material is calcined china clay. 7. A coating kit according to any preceding claim wherein said water-soluble material is quick lime. 8. A coating kit according to any preceding claim wherein said emulsifying agent is casein. 9. A coating kit according to any preceding claim wherein said polyol (iii) in the first composition comprises one or more polycaprolactones. 10. A coating kit according to any preceding claim wherein the first composition, before admixture with water, contains 30 to 50 wt % of the alkaline material, 2 to 4 wt % of the emulsifying agent, a total of 20 to 40 wt % of polyols, 0 to 20 wt % of liquid epoxy resin, o to 2 wt % of hydroxypropyl cellulose, 10 to 25 wt % of inorganic particulate filler and 0 to 1 wt % of a non-toxic preservative for the emulsifier. 11. A coating kit according to any preceding claim wherein the polyisocyanate in the second composition is diphenylmethane -4,4' diisocyanate. 12. A coating kit according to any preceding claim wherein at least one said chain polyol from which the polyurethane prepolymer is derived contains one or more monocyclic aryl groups. 13. A coating kit according to any preceding claim wherein one said open chain polyol from which the polyurethane prepolymer is derived is a high molecular weight polyether diol. 14. A coating kit according to any preceding claim wherein the solvent in the second composition is an ester ether of an alkylene glycol. 15. A coating kit according to any one of claims 1 to 13 wherein the solvent in the second composition is an aromatic hydrocarbon. 16. A coating kit according to any preceding claim wherein the particulate mineral filler is an organomodified hydrophobic fumed silica. 17. A coating kit according to any preceding claim wherein the second composition also contains a catalyst for the reaction of the polyurethane prepolymer with water. 18. A coating kit according to any preceding claim wherein the second composition is made from 45 to 65 wt % of polyisocyanate, 12 to 25 wt % of polyol, 3 to 6 wt % of particulate mineral filler, 0 to 0.1 wt % of a catalyst to promote the reaction of the polyurethane with water and 15 to 35 wt % of solvent. 19. A method of coating a surface using a coating kit according to any preceding claim, wherein the first composition is mixed with water, the two compositions are mixed together and the mixture is sprayed onto said surface. 20. A method according to claim 20 wherein the first composition and the water are mixed at a weight ratio from 3:7 to 7:3. 21. A method according to claim 21 wherein the surface to be coated is the inside of a pipe and the coating is applied using a rotary sprayer.

Inventors: HOSGOOD, HENRY DAVID
Applicants: COSTAIN STREETER LINING LIMITED
Application year: 1984
Main classification: C08G18
IPC codes: C08G18