APPARATUS FOR THE PURIFICATION OF SILICEOUS SAND BY MEANS OF ATTRITION

Abstract: An apparatus and method for purifying sand particularly suitable for the manufacture of glass, using opposite jets of slurry containing the impure sand, made to collide with one another at high speed to cause collision of the suspended particles and removal of the impurities adhering to them due to reciprocal attrition, inside a vessel in which the slurry is circulated and from which a flow is extracted containing the purified sand and the impurities, which are sent to a silting operation.

Description: Apparatus and method for the purification of siliceous sand by means of attrition Italsil S.p.A. The present invention relates a method and an apparatus for the purification of sand particularly suitable for manufacture of glass. In manufacturing glass, silica (SO2) is the most important material from the quantitative point of view, since it is ordinarily present in a percentage of approximately 98%. In nature, silica is contaminated with impurities of various kinds, which must be removed to obtain glass of the desired quality. In particular, sand for the manufacture of glass is classified on the basis of its iron oxide content (foe203) Normally, the sand has an iron content greater than 1%, while the manufacture of glass in general requires levels no higher than 0.20%. Thus a series of processes must be adopted to lower the iron content to acceptable values for the various qualities of glass to be produced. In general, a treatment for the purification of sand consists of the following phases: 1) washing to remove the clay fraction and the fraction unusable granulometrically; 2) attrition to facilitate removal of the surface impurities and/or the breaking of granules attached to one another, thanks to the rubbing action of the granules of sand with one another; 3) siltingto eliminate the impurities separated in the attrition phase; 4) flotation to further separate the useful material from the impurities; 5) magnetic separation in place of or in addition to the flotation. Phases of leaching and/or drying may also be added, depending on the requirements. The aim of the present invention is to provide a method and apparatus which allow reduction of the phases necessary for the purification treatment, realizing a degree of impurity -removal similar to that achieved with a longer and more complex treatment. In particular the method and apparatus which are the object of the present invention relate to the 2nd phase described above, and described with the term attrition. In the prior art the attrition phase comprises placing the sand mass in aqueous suspension (from here on, called the "slurry") in closed cells in which suitable rotors are used to create opposing fluid currents, in order to generate reciprocal abrasion between the particles and so allow the mechanical removal of the impurities covering the grains of sand. In this phase, the aggregates of sand particles held tqgether by a cementing element may also be broken up; said cementing element also is an impurity which must be removed. These attrition cells and their operation are known in themselves in the state of the art, and are readily available commercially. A known type of attrition apparatus comprises cells in which rotors rotate to produce a vortex motion of the slurry to cause the reciprocal collision of the particles themselves. Normal apparati provide a certain number of these cells in series. In attrition cells known up to now, the total energy with which the mass to be purified is stirred is not used in an optimal manner, since very high flow rates are not possible since they produce cavitation phenomena on the rotors; moreover, the direction of the flows i not easily controlled. Also, there is an intrinsic damping of the motion due to the viscosity of the slurry, and the rotors must be replaced frequently due to their wear and tear. The method for achieving attrition according to the present invention substantially comprises directing one against the other two or more jets of slurry at a suitable velocity so as to cause collision of the particles themselves, thus eliminating the use of rotors, replacing the latter with suitable flow nozzles and improving considerably the knocking off of the impurities. The apparatus according to the present invention substantially comprises: a vessel equipped on the top with an opening for the introduction of the slurry containing the impure sand, and a recycling outlet on the bottom for removal of the slurry still containing impure sand and returning it to the cycle, where said vessel also has an overflow opening for outlet of the slurry containing purified sand and impurities already separated from one another; an attrition cell equipped on the top with inlets consisting of two or more opposite nozzles for introduction of the impure slurry, said cell connecting on the bottom with said vessel; a pump whose intake is connected to the outlet of the vessel and whose discharge is connected to the nozzles of the attrition cell; and a chamber adjacent to said overflow of the vessel equipped with an outlet for removal of the slurry containing the purified sand and the impurities, so that the impure sand introduced through the nozzles has the impurities knocked off by effect of the attrition action arising from the reciprocal collision of the entering flows of slurry from said nozzles. An apparatus which is a practical realization of the present invention is described below in an exemplicative and non-limiting fashion, with reference to the attached drawings in which: figure 1 represents a scheme for the operation of the apparatus according to the invention; figure 2 shows a top view of the apparatus; figure 3 shows a side view of the pump of the same apparatus; and figure 4 shows a front view of the apparatus in figure 2. With reference to figure 1, a vessel 1 is filled with the slurry fed through a feeding tube 2. The slurry is drawn through an outlet 3 on the bottom of the vessel and pushed by a pump 4, which gives the flow the necessary energy of motion, into an attrition cell 5 through a pair of nozzles 6,6. From the nozzles 6,6, the.flows of slurry are pushed contemporaneously in opposite directions, so causing collision of the:;sand particles. The flow rate is suitably determined so as to prevent breaking of the sand granules, while at the same time allowing mechanical removal of the impurities which cover the granules themselves, as well as eventual breakage of the sand aggregates. A flow rate of approximately 10-50 m/second has been found to be suitable. After this treatment, the slurry falls back into vessel 1, the maximum level of which is held constant thanks to overflow 7. The particles of greater specific gravity, and hence less purified, tend to fall to the bottom of the vessel 1 and be pushed again by pump 4 toward the attritionnozzles 6,6', while the lighter, and so cleaner; particles tend to go out the overflow opening 7 together with the separated impurities. From overflow 7, this purified slurry passes into a chamber 8 and from here is removed through an outltet 9. Sand and impurities come out of outlet 9 to be sent to a subseguent phase of silting or classification. In figures 2, 3 and 4, where elements analogous to those in figure 1 have the same reference numbers, a practical realization of the apparatus according to the invention is illustrated. The vessel 1 is supported by columns 10, and has a truncated pyramidal bottom to which is connected a tube 11 which connects the outlet 3 from the bottom of the vessel 1 withl.the pump 4. The pump is powered by a motor 12. The deliveryyof pump 4 sends the slurry through a rising tube 13 toward a distributor 14 which distributes the slurry to a certain number of opposite nozzles (only one pair in the: realization shown) through distribution tubes 15, 15', which terminate in opposite nozzles 6,6' which spray into the attritioncell 5. Said cell 5 extends on the inside of vessel 1 open on the bottom, and the level of the slurry in vessel 1 is maintained by an overflow outlet 7. The overflowing liquid falls into a chamber 8 and is removed from outlet 9. To prevent a flow short circuit between the impure slurry entering through opening 2 and the "purified" slurry coming out the overflow 7, bulkheads 16 may be provided (see figure 2) to prevent mixing of these slurry flows. It has been found that the method and apparatus according to the invention offer a considerable number of advantages with respect to traditional attrition systems. In fact thanks to the better utilization of the motion energy applied to the slurry flow, and also to the possibility of controlling the direction of the flows which collide with one another, impurities are knocked off to a degree ranging from 20% to 50% higher than that achieved in a traditional attritioncell; furthermore, a considerable energy savings of from 20% to 40% is achieved with--respect to traditional abrasion systems. Moreover, the apparatus according to the invention does not require the use of rotors of a particular shape and structure, since the pump is a normal pump for the movement of sandy fluids. Although the invention has been described in considerable detail, it may be realized with numerous modifications of the present invention all falling within the scope of the following claims.

Claims: Claims 1. Apparatus for the purification of silica sands by means of an attrition operation characterized by comprising: a vessel equipped on the top with an opening for the introduction of the slurry containing impure sand and on the bottom with a first outlet for removing the recycle slurry containing impure sand, with an overflow outlet on one wall; an attrition cell equipped on the top with openings for impure slurry and communicating on the bottom with said vessel; one or more opposite nozzles placed in correspondence with said openings of the attrition cell; a pump whose intake is connected to said first outlet of the vessel and whose delivery is connected to said nozzles of the attrition cell; and a chamber adjacent to said overflow from the vessel, equipped with a second outlet for the slurry containing purified sand and impurities, so that the impure sand introduced with the slurry into the cell through said opposite nozzles undergoes a breaking off of the impurities by effect of anattritionaction due to the reciprocal collision of the slurry flows entering through said nozzles. 2. Apparatus according to claim 1, in which a slurry distributor is placed between said nozzles and the pump delivery. 3. Apparatus according to claim 1, in which the area of the vessel near said overflow is separated from the rest of the vessel by two vertical bulkheads. 4. Apparatus according to claim 1, in which said vessel has a truncated pyramid shaped bottom converging toward said first outlet. 5. Method for the purification of siliceous sand by means of attrition, comprising the steps of: forming two currents of slurry containing impure sand with opposite flow direction and a high flow rate; directing said currents one against the other so as to cause collision; and collecting the slurry containing the purified sand and the impurities.

Inventors: FOLIGNO, ADALBERTO, IPPATI, FILIBERTO, MARTI, MARIO
Applicants: ITALSIL S.P.A.
Application year: 1984
Main classification: B02C19
IPC codes: B03B7, B02C19