PROCESS FOR ANIONIC POLYMERIZATION

Abstract: Control of an anionic polymerization is obtained by monitoring an indicator of molecular weight of the polymer in the polymerizing mixture, measuring the molecular weight of the polymer produced therein and using this information to control the rate at which polymerization initiator is added to the polymerizing mixture in a continuous stirred tank reactor.

Description: The present invention relates to a process and apparatus for the control of anionic polymerization reactions in a continuous stirred tank reactor. The term continuous stirred tank reactor refers to any reactor wherein material is continuously added to and removed from the reactor at about the same rate, the contents of the reactor being maintained in a generally homogeneous condition in both composition and temperature. Thus, a continuous stirred tank reactor may have the configuration of conventional stirred cylindrical or spherical tank, or it may be a loop wherein material is rapidly recirculated within the loop. Polymerization is frequently carried out employing a plug flow reactor wherein the composition at the inlet end is very different from that at the outlet end and a temperature gradient may exist therein. Such is not true with a continuous stirred tank reactor. Often it is desirable to prepare polymers employing anionic initiators in a continuous stirred tank reactor wherein monomer, optionally with a diluent, and anionic initiator are continuously added and the product stream removed for further processing and recovery of the polymer, preferably as pellets. A highly desirable characteristic for commercial polymers is uniformity of both composition and molecular weight. Blending various batches to provide apparent uniformity is costly. Variations in molecular weight between batches of a polymer can result in many fabrication difficulties. Often, particularly with alkenyl aromatic polymers, gels are formed during the polymerization. Such gels are readily recognized on the extrusion of the polymer into strands by the generally lumpy nature of the strands, the lumps or slub-like formations being generally proportional to the gel content. Such gel containing polymer is generally unsuited for extrusion or for injection molding as the final product may show surface irregularities and deviate from the configuration of the mold. In US-A-3,726,849 the control of the typ of polymer product product produced during the solution polymerization of an olefin such as propylene is described. The control is achieved through (i) correcting changes in the average molecular weight by adjusting the rate of monomer feed, (ii) correcting changes of the polymer percentage in the effluent by adjusting the temperature of the monomer feed stream, (iii) correcting changes in the production rate by adjusting the rate of catalyst feed, and (iv) correcting changes in the temperature of the effluent also by adjusting the monomer feed rate. The control of this process proves to be difficult due to the necessity to adjust several different parameters and to compensate for the disturbances caused. Attempts have been made to control anionic polymerization by colorimetric means such as suggested in US-A-3,290,116, 3,468,972 and 3,743,629. In practice, the sensitivity of the colorimeter may vary overtime. Also, impurities in monomer and diluent vary with time as well as the effective amount of the initiator. Therefore, it would be desirable if there were an improved method and apparatus for the control of anionic polymerization which provided a product of generally constant average molecular weight and essentially free of gel. These advantages are achieved by a method for the anionic polymerization of anionically polymerizable alkenyl aromatic monomer with an organometallic anionic initiator in a continuous stirred tank reactor wherein the contents of the reactor are generally homogeneous and the polymerization components are continuously added and the reaction mixture continuously discharged from the reactor at essentially the same rate, and controlling the monomer flow stream to the reactor and measuring the molecular weight of the polymer in the reactor discharge stream, characterized by a conversion of monomer to polymer exceeding 99 weight percent and controlling the initiator feed streams to the reactor by a signal obtained from said measuring of the molecular weight to provide a polymer of essentially constant molecular weight. A particularly desirable embodiment comprises providing a first signal which varies with the molecular weight of polymer in the effluent from the reactor, the first signal altering the rate of polymerization initiator addition to the reactor to maintain a generally constant molecular weight of the polymer, measuring the molecular weight of the polymer thereby obtaining a second signal, employing the second signal to compensate a first signal generating means for drift or error in the first signal generating means to thereby maintain a generally uniform molecular weight of the polymer in the reactor effluent. Also contemplated is an apparatus for the preparation of anionically polymerized alkenyl aromatic polymers comprising in cooperative combination a monomer supply means, a monomer flow control means associated with a discharge of the monomer supply means, an anionic polymerization initiator supply means, an initiator flow control means in association with a discharge of the initiator supply means, a continuously stirred tank reactor having an inlet and an outlet, the inlet of the continuous stirred tank reactor being in operative communication with the monomer flow control means and the initiator flow control means and adapted to receive material therefrom; a discharge conduit connected to the discharge of the continuously stirred tank reactor, the discharge conduit being in operative communication, a means to provide a first signal which varies as molecular weight of polymer in effluent from the continuously stirred tank reactor varies, the first signal adjusting the initiator flow control to thereby provide molecular weight control of a polymer being prepared, means to measure the molecular weight of a polymer and provide a second signal indicative of the molecular weight of the polymer, means to receive the second signal and adjust the means to provide a first signal to thereby provide a polymer of a generally uniform molecular weight. By the term alkenyl aromatic monomer is meant an anionically polymerizable monomer composition containing at least 50 weight percent of monomer having the formula: wherein R is hydrogen or methyl, Ar is an aromatic ring structure having 1 to 3 aromatic rings with or without alkyl substitution wherein any alkyl group contains 1 to 6 carbon atoms, any remaining monomer being monomeric material anionically copolymerizable with the alkenyl aromatic monomer. Typical alkenyl aromatic monomers which may be used alone or in admixture include: styrene, α-methylstyrene, vinyltoluene (all isomers, paravinyltoluene being preferred), ethylstyrene, propylstyrene, tertiarybutylstyrene, octylstyrene, vinylnaphthalene, vinylbiphenyl, vinylanthracene and mixtures thereof. Anionic polymerization is well known in the art. Representative systems are set forth in US-A-3,030,346; 3,954,894; 4,196,153; 4,200,713 and 4,205,016. Generally, it is desirable to conduct the polymerization in the presence of an inert solvent for the polymeric material being formed. Typical solvents include benzene, toluene, ethylbenzene, and ethyltoluene alone or in admixture with minor amounts of alkyl compounds, such as cyclohexane. In the practice of the present invention, it is desirable to maintain uniformity of temperature and composition in the reaction mixture within the polymerization vessel. It is desirable that the temperature of the reaction mixture be maintained at ±3°C throughout the reaction mixture and preferably with ± 1.5°C. To obtain the desired temperature and composition uniformity in a recirculating coil reaction such as described in Schweitzer, et al., US-A-3,035,033, the volume of material circulating within the coil should be at least 15 times and preferably 25 times the volume of material being added to and discharged from the coil. In the case of a stirred tank reactor, the temperature and composition of the reaction mixture should be uniform at all locations within the reactor except for the region immediately adjacent to the point of monomer feed. For the case of a 1.0 m diameter tank, 2.0 m in height having an axially disposed agitator being fed monomer radially inwardly through a side of the tank at the bottom the temperature and composition of the reaction mixture should be generally constant at all locations within the reactor more than 0.1 m from the point of feed. In general, the greater the mixing, the more uniform the product obtained, and the lower chance of gel formation. In polymerization done in accordance with the present invention, conversion of monomer to polymer exceeds 99 weight percent, and due to the nature of a continuous stirred tank reactor and the rapidity of the polymerization, the solids level is generally constant. For each 1 percent solids variation in the reaction mixture for polystyrene of about 300,000 molecular weight, the molecular weight will vary about 4,000 providing a great latitude for the means to generate the first signal. The means for generating the first signal may be any of a variety of sensors which generate a signal indicative of molecular weight of the polymer. Generally, in anionic polymerization, the polymerizing mixture provides a colored anion. For example, in the polymerization of styrene employing an organolithium initiator, a strong red coloration is induced which is more or less proportionate to the number of end groups present and therefore is indicative of the molecular weight of the polymer. A viscometer is also useful, or an analysis of the number of end groups. The means to generate the second signal desirably is a device which actually measures the molecular weight of the product in the reaction mixture and provides essentially a standard against which the output of the means to generate the first signal can be compared. A variety of devices may be employed as means to generate the second signal such as a viscometer, light scattering and the like. However, the preferred embodiment is to employ a gel permeation chromatograph which alternately measures the molecular weight of the polymer in the reaction mixture and a standard polymer of known molecular weight to provide maximum reliability. Figure 1 schematically represents one embodiment of the invention. Figures 2 and 3 schematically represent a sampling procedure of the arrangement of Figure 1. In Figure 1 there is schematically depicted an apparatus suitable for the practice of the method of the present invention, the apparatus is generally designated by the reference numeral 10. The apparatus 10 comprises in cooperative combination a supply tank 11 having an inlet conduit 12, an inlet conduit 13 and an outlet conduit 14 in which there is disposed a pump 15. The conduit 14 is in communication with a water inlet conduit 17. Both conduits 14 and 17 discharge into a conduit 18 having a heat exchanger 19 disposed therein. The conduit 18 discharges into a cracking column 21. The discharge from the cracking column 21 is to a conduit 23 having heat exchanger 24 therein, a decanter 25, a conduit 26 for the discharge of water and an organic material receiving tank 27. Organic material from tank 27 is forwarded to a distillation column 29 through conduit 28. The distillation column 29 has overhead discharge lines 31 and 32. Discharge conduit 31 has a heat exchanger 33 disposed therein. Conduit 31 connects to and discharges into conduit 32. Distillation column 29 has a discharge conduit 35 and recirculation conduit 36 having heat exchanger 37 disposed therein. Conduit 35 discharges to a second distillation column 38 having overhead discharge conduits 39 and 41, as well as bottoms circulation system similar to column 29. Conduit 39 has a condenser 42 disposed therein. Conduit 41 has disposed therein liquid storage tanks 43 and 44. Tanks 43 and 44 are connected in series. Conduit 41 terminates at a continuous stirred tank reactor 46. The reactor 46 has an inlet 47 and a discharge 48. The reactor 46 has the configuration of a closed loop having a pump 46a therein to provide agitation or circulation of liquid within the reactor 46. An anionic polymerization initiator supply tank 51 is in communication with conduit 41 by means of conduit 52. Conduit 52 has disposed therein a flow control means or variable speed pump 53. The discharge opening 48 of the continuously stirred tank reactor 46 is in operative combination with conduit 55. Within conduit 55 is disposed a means 56 to provide a signal which varies with the molecular weight of polymer contained in material flowing through line 55. Also, disposed within the line 55 is a means 57 which provides a first signal which varies as the molecular weight of the material flowing in line 55 varies; for example, a color detector. A control means 58 is in operative combination with means 56, 57 and pump 53. Conduit 55 remote from discharge 48 discharges to a terminating stirred reactor 61. Also connected to terminating stirred reactor 61 is an inlet conduit 62 and a discharge conduit 63 having disposed therein a pressure control valve 64. Conduit 63 discharges to a devolatilizing apparatus 65. The devolatilizing apparatus 65 has a bottoms discharge conduit 66 and an overhead discharge conduit 67. Within line 67 is a quality indicating means 68, such as infrared spectrometer. In Figure 2, there is schematically depicted a sampling arrangement for the determination of molecular weight of a polymer from a polymerizer 46a discharging to a line 55a. As depicted in Figure 2, a conduit 71 is in selective communication with line 55a. The conduit 71 discharges to a mixing chamber 72 which beneficially is of small volume and has disposed therein an agitator 73. Advantageously, the agitator 73 is magnetically activated. The chamber 72 has associated therewith a nitrogen or other inert gas supply conduit 74 and a vent conduit 75. The conduits 74 and 75 each have a valve disposed therein. The mixing chamber 72 discharges into the conduit 77 to a gel permeation chromatograph. The conduit 77 has a valve disposed therein. A standardizing polymer supply means 78 has associated therewith a valved conduit 79 which is connected to a gel permeation chromatograph 81. The line 77 from chamber 72 also communicates with a gel permeation chromatograph. As depicted in Figure 2, a suitable solvent such as tetrahydrofuran at a pressure of 515 kPa (60 psig) is pumped through the gel permeation chromatograph. Material from the polymerizer 46a passes through line 55a and through a four-way valve 82. In Figure 3, the four-way valve 82 has been repositioned so that a portion of the material flowing through line 55a passes through conduit 71 to the mixing chamber 72 and is passed through the gel permeation chromatograph 81. Although the apparatus and method of the present invention can be employed to provide a wide variety of polymers and copolymers. Figure 1 depicts an arrangement which is particularly suited for the preparation of polystyrene from ethylbenzene. Ethylbenzene is provided to conduit 12 and is stored in tank 11, passed through line 14 and pump 15 to conduit 18 where it is admixed with water and heated in heat exchanger 19 to provide a mixture of ethylbenzene and steam which in turn is passed through the cracking column 21. The effluent from the cracker is passed through line 23 and heat exchanger 24 where the effluent is cooled. The effluent from the cracker column after cooling is passed to the decanting vessel 25 and water is discharged from the conduit 26. Crude styrene passes from the decanting vessel to crude styrene tank 27. From the tank 27 crude styrene is conveyed through conduit, 28 to distillation column 29. Distillation column 29 serves to remove low boiling contaminants such as benzene, toluene and residual water. The bottom fraction from first distillation column 29 passes through line 35 with some recirculation and heating through line 36 and heat exchanger 37. Conduit 35 discharges fraction consisting primarily of ethylbenzene and styrene into distillation column 38. The high boiling fraction consisting primarily of tars and cymene is discharged from the bottom of distillation column 38. The overhead fraction from the second distillation column is passed to conduit 41 and through tanks 43 and 44 to the reactor 46. The overhead fraction is a mixture of about equal parts of ethylbenzene and styrene. After being admixed with an anionic polymerization initiator from conduit 52 and pump 53, effluent from the continuously stirred tank reactor 46 is discharged through conduit 55 and the detectors 56 and 57. Conduit 55 discharges into another continuous stirred tank reactor 61 wherein the polymer is admixed with ethanol to deactivate the polymer. The effluent from reactor 61 is passed through conduit 63 and pressure control valve 64 into the devolatilizer 66 wherein ethylbenzene is removed and molten polystyrene is removed from the devolatilizer 65 through conduit 66. The molecular weight detector 56 provides a signal to a computer 58, the signal being indicative of the weight average molecular weight of the polymer. The color detector 57 also provides a signal to computer 58 and the computer in turn adjusts the set point of the color detector 57 to obtain a generally constant molecular weight polymer. The computer 58 also provides a signal to the pump 53, to thereby provide a desired quantity of the anionic initiator to maintain the desired weight average molecular weight. In practical applications usually continuous monitoring of the molecular weight is not necessary. From a practical standpoint, the molecular weight should be monitored at least every 8 hours and the set point of the color detector adjusted accordingly. Preferably, the molecular weight determination and set point adjustment is made every two hours. The molecular weight arrangement 56a as depicted in Figures 2 and 3 permits the intermittent sampling of the product stream, dilution of the fixed quantity of the stream, the dilution occurring in the chamber 72, and the materials is passed through a gel permeation chromatograph such as 81. To assure close control of the molecular weight of the product and accuracy of the results from the gel permeation chromatograph, a standard is employed. That is, a solution of polymer of known molecular weight and distribution is passed through the gel permeation chromatograph for calibration purposes. Gel permeation chromatography is the preferred method of determining molecular weight; however, other techniques may be utilized, such as melt flow, solution viscosity, light scattering, and vapor phase osmometry. In the practice of the present invention, it is desirable that the residence time of material in the reactor be 1 to 3 hours. If the residence time is less than 1 hour, molecular weight control becomes difficult and if the residence time is greater than 3 hours, the process becomes less economical. It is highly desirable that the polymerization temperature be maintained between 80 and 140°C. If the temperature is below 80°C, the quantity of initiator employed becomes excessive and if the temperature is greater than 140°C, the conversion of monomer to polymer decreases. The weight percentage of polymer to solvent in the reactor should be between 30 and 80 weight percent. If the solids content of the reactor is below 30 weight percent, excessive solvent must be removed to recover the polymer and when the solids content of the reactor is above 80 weight percent, the viscosity of the reaction mixture is higher than can be handled by most practical processing equipment. The solvent generally desired is an alkyl aromatic material. Most commercially used is ethylbenzene. However, xylene and toluene may be employed. A principal advantage of the process of the present invention is that polymers with a very low degree of yellowness can be prepared employing low levels of lithium initiator. To achieve the desired result, the oxygen content of the feed stream to the reactor should be held to less than 1 part per million (ppm) by weight based on the weight of the total feed stream. If greater than 1 ppm, it adversely affects the color of the recovered polymer. Similarly, water, if present, should be present in an amount less than 10 ppm, and active hydrogen, organic compounds such as acetylenes and oxygen-containing organic impurities should be maintained at a level of less than 60 ppm as such materials also adversely affect the color of the polymer. The recovered polymer should contain less than 20 ppm of lithium as the presence of lithium also adversely affects the color of the polymer. Desirably, conversion of monomer to polymer greater than 99 weight percent are achieved. The invention is further illustrated by the following examples: Example 1 An apparatus was employed generally in accordance with Figures 1 through 3. The cracker had three sections: a pre-heating section about 1 meter long filled with ceramic Beryl saddles, a 0.5 m cracking section having an hourly space velocity of 2.14 reciprocal hours and filled with a cracking catalyst commercially available under the trade designation of Shell 105 containing ferric oxide. The cracking temperature was 625°C and the pressure was 136 kPa (5 psig). In the third section of the cracker, the temperature was reduced to 300°C. The first two cracker sections were heated by ceramic heaters, each about 2500 watt capacity and the ratio of water to ethylbenzene was 0.9. The condenser equivalent to condenser 24 was water cooled. Between the condenser 24 and the decanter 25 was a gas liquid separator which was a flat vessel about 490 cubic cm capacity. From the gas liquid separator crude styrene was pumped from a tank equivalent to tank 27 into the first distillation column. The first distillation column was 5.0 cm in diameter and packed to provide in excess of 40 height equivalent of theoretical plates and was employed to remove the light fraction from the crude mixture. Benzene, toluene and water were the primary materials removed. The bottom fraction from column 1 was fed to the second distillation. The first distillation column was operated under a pressure of 17.3 kPa and had a bottom temperature of 90°C and a reflux ratio of about 5:1. The second distillation column was 10 cm in diameter, packed and had 40 height equivalent of theoretical plates. The second distillation column was operated under a pressure of 14.6 kPa and a temperature of about 85°C bottom. The reflux ratio was 6:1. The overhead composition removed from the second distillation column was a mixture of styrene and ethylbenzene in about a one to one ratio. Bottoms were principally tars and para-cymene. Both columns had a residence time of about 2 hours. The storage vessels equivalent to tanks 43 and 44 had a residence time of about 24 hours. Both tanks were maintained under an atmosphere of nitrogen having a pressure of 240 kPa (20 psig). Impurities other than styrene and ethylbenzene were maintained at a level below a hundred parts per million by weight. Material from the tank 44 was forwarded to a continuously stirred tank reactor 46 by means of a double-headed 0.63 cm Milton-Roy piston pump. The reactor was a recirculating coil constructed of 2.5 cm inside diameter 316 stainless steel tubing connected in a square configuration. The tubing was jacketed and heated with hot water. The contents of the stainless steel tubing reactor were circulated therein using a Northern gear pump, stock No. 4448, operating at about 200 rpm. The internal volume of the reactor was 1867 cubic centimeters. The gear pump was located adjacent the inlet of the ethylbenzene and initiator and downstream thereof to provide prompt mixing of the initiator and feed mixer with the viscous polymerizing mass recirculating within the reactor. Pressure in the reactor was maintained at 450 kPa (50 psig) by manipulation of a pressure control valve, such as valve 64 of Figure 1. The polymerization initiator employed was normal-butyllithium which was purchased as a 15 percent solution in heptane and prior to use was diluted with toluene to provide a normal-butyllithium concentration of from about half to one percent by weight. The pump employed to forward the normal-butyllithium was a Milton-Roy piston pump driven by a variable speed electric motor controlled by a computer. The computer language employed was 'Hewlett Packard Language' commonly known as 'HLB', the computer program employed was as follows: In the computer program, Statements 2-16 initialize all variables and clear all cards. The real-time clock is set up for use and is started. Statements 19-43 control the display of the 9825 which can be changed by the operator by pressing special function key (SFK) f1 on the computer. Statements 44-126 calculate the Mw of the polymer from the detector readings. This segment is executed when all the readings are collected and is under control of the valve subroutine. Statements 88-91 are those that actually modify the colorimeter-initiator addition rate control loop. Statements 98-100 print the Mw information on the paper tape. Statements 130-134 allows offline input of Mw; that is, the operator can input Mw information from another outside source (e.g., another GPC) and modify the colorimeter-initiator addition rate control loop. Statements 135-171 contain the subroutines "valves" and "longvalves". "Valves" controls the GPC sampling valves when the GPC cycle is less than 30 minutes. This control is accomplished through writing to the relay card and turning specific relays on and off. This in turn, opens and closes Whitey® ball valves by suppling power to ASCO® solenoid valves through the relays. The length of the GPC cycle is defined as how often Mw information is received, that is, how often a sample is prepared and run through the GPC. The frequency of standardization (how many samples follow a standard) can be varied through variable V[15]. In addition, the GPC cycle (V[3]) can be varied in 5 second increments. The other variables involved with this subroutine control the injection time, V[28], and when the computer "looks" at the GPC detector for the elution of the injected sample, V[17] and V[20]. "Longvalves" has all of the above features with some minor changes: (1) it is used for GPC cycle times greater than 30 minutes and (2) it allows only the sample cycle of std, sample, std, sample... Statements 172-190: the subroutine "clock" does two important things. First, it decides upon interrupt, what the real-time clock is signalling must be read from the outputting instruments. Secondly, it reads the input signal, either from the colorimeter or the GPC detector. Subroutine "detector" is used for reading the GPC detector. Statements 228-238 is the colorimeter control subroutine which calculates the continuously changing initiator addition requirements based on the anion concentration in the reactor effluent. It then outputs a new voltage on the D/A card to change the rate of addition. This is done by varying the amount of power supplied to the motor which runs the initiator addition pump. The computer outputs a 0-10V signal to a PARAJUST® motor controller, which in turn then varies the power output to the motor. Special Function Key Tape is a printed copy of the statements which are stored in the special function keys of the computer. These statements allow operator control over the mode of control, variable value, display, etc. These statements are stored on a cassette tape and loaded into the memory of the computer in statement #4 (trk 1,ldk 1). Example 2 A feed stream was purified by pumping a 1 to 1 by weight mixture of styrene and ethylbenzene through a heat exchanger at 55°C and discharging through a spray nozzle into a receiver which had an internal pressure of 2.6 kPa to remove oxygen and most of the water present. From the receiver, the feed materials were passed through a bed of molecular sieve commercially available under the trade designation of Linde 3A, the bed having a length to diameter ratio of 18 at a velocity of 5 parts of the stream per part of sieve by weight per hour. The resultant feed material contained styrene and ethylbenzene in about a 1 to 1 ratio having less than 1 ppm of oxygen, 3 ppm of water, 5 ppm benzaldehyde, 5 ppm styrene oxide, 5 ppm of acetophenone, and about 40 ppm of phenylacetylene. The purified styrene-ethylbenzene feed stream was pumped to a polymerizer employing a double-headed 0.6 cm Milton-Roy pump. The polymerization was a 2-liter generally cylindrical reactor, manufactured by Parr and commercially available, with a hollow auger agitator comprising a cylinder slightly shorter in length than the interior of the auger and slightly smaller in diameter. A land was helically disposed on the outside of the cylinder sized such that the cylinder generated by rotation of the hollow cylinder and land was slightly less than the internal volume of the reactor. Such a reactor is described in U.S. 4,239,863. Hot water under pressure was employed to heat the reactor to 95°C. The purified feed stream and initiator were introduced into the side of the reactor at a rate to give a two-hour residence time. The initiator was normal-butyllithium pumped at a rate to provide about 60 ppm. The pressure within the reactor was maintained at 450 kPa (50 psig) using a pressure control valve at the outlet. The stream from the reactor was fed to a terminator coil of 2.5 cm inside diameter, 316 stainless steel tubing connected in a square configuration and having an internal volume of about 467 cubic centimeters. Material was recirculated within the terminator coil using a Northern gear pump stock No. 4448 operating at about 200 revolutions per minute. A solution of 1 weight percent ethanol in ethylbenzene was fed to the terminator coil at a rate about twice that of the normal-butyllithium fed to the polymerizing vessel. Effluent from the terminator coil was then pressure fed into a devolatilizer equipped with a flat plate heater and a screw extruder such as described in U.S. 3,014,702. The exterior of the heater was maintained at a pressure of 4.67 kPa and the reaction mixture heated to a temperature of about 240°C to provide a polymer containing 0.8 weight percent volatiles. The molecular weight of the resultant polymer over a 24-hour period was maintained at 210,000 ±5,000. The color of the product was excellent with a yellowness index of 0.007. Example 3 A styrene-ethylbenzene mixture about 1 to 1 by weight was purified as in Example 1 except on a larger scale to give a purified feed stream having by analysis 42 weight precent styrene, 58 weight percent ethylbenzene and less than 1 ppm oxygen, 5 ppm water, 14 ppm acetophenone, 5 ppm benzaldehyde, 5 ppm styrene oxide and about 34 ppm phenylacetylene. A polymerization vessel was used which comprised a 1893 l tank having a condenser mounted vertically above the vessel. The condenser had 14.7 sq m of cooling surface. The vessel and condenser were supported on weighing cells, the output of which was employed to control the volume of the reaction mixture within the polymerization vessel. A vacuum system was employed to provide a reduced pressure within the vessel. Vapor removal was utilized to maintain desired polymerization temperature. A variable speed pump was mounted on the bottom of the vessel to remove polymer solution therefrom, the speed of the pump being varied to maintain a generally constant polymerization vessel weight. The polymerization vessel was fitted with a hydraulically driven agitator rotating at about 100 revolutions per minute. Condensate from the condenser was recycled to the feed stream. The polymerization vessel was operated under the following conditions: a reactor inventory of 680 kg; a feed rate of 386 kg per hour; a residence time of 1.75 hours; the temperature of the reaction mixture 100°C; a reactor pressure of 31.5 kPa; normal-butyllithium 80 ppm based on the total weight of the feed; resulting in a product containing 21 ppm lithium and having a yellowness index of 0.029. For a 24-hour period, the weight average molecular weight as determined by gel permeation chromatography was 195,000 plus or minus 10,000. The reaction was terminated by passing the reaction mixture through a section of 3.8 cm pipe containing fiber optic probes and side stream takeoff port which led to gel permeation chromatograph. The reaction mixture was then passed to a section of 15.2 cm jacketed pipe containing eighteen 15 cm x 20 cm static mixing elements commercially available from Koch Engineering Company. The jacket was heated to a temperature of 120°C and a 5 weight percent solution of ethanol in ethylbenzene was pumped into the reaction mixture prior to its entering the static mixers at 4 opposing points generally displaced about 90° from adjacent points on the pipe at a flow rate of about 2.3 kg per hour. After termination, partial polymer was devolatilized using two devolatilizers in series, the first devolatilizer operating at 160°C and 79.7 kPa and the second devolatilizer at 240°C and 2.65 kPa. Example 4 The procedure of Example 2 was repeated with the following exceptions. The feed mixture to the reactor was 42 parts by weight paramethylstyrene, 2 parts by weight paraethyltoluene and 56 parts by weight ethylbenzene. The rate of feed was one reactor volume in a period of one and one-half hours. The polymerization temperature was 80°C. The weight average molecular weight of the product obtained over a period of 24 hours was 340,000 ±30,000. Extrusion of the resultant polymer through a strand die provided a strand with no visible lumps or gels. The product was suitable for extrusion and injection molding of high quality articles. Comparative example 1 The procedure of Example 2 was repeated with the exception that the agitator was not rotated. Over a period of 24 hours the best control of molecular weight that was obtained was about ±100,000. On extrusion of the product a yellow strand was obtained which contained large lumps or gels. A molded product from such a strand has poor color and surface appearance. Comparative example 2 A 1.2 cm diameter 76 cm long jacketed tubular reactor was equipped with a color measuring device and gel permeation chromatograph as described in Example 1. The inlet end of the reactor was fed with a mixture of styrene and ethylbenzene (1:4 by weight), together with a polymerization initiating amount of normal-butyllithium at a rate sufficient to provide a residence time of 15 minutes. Atmospheric steam was applied to the jacket. Temperature sensing probes disposed within the reaction mixture in the reactor indicated the temperature range was about 20°C. Employing the temperature and a gel permeation chromatography signal to control the reaction resulted in product varying ±100,000 from average over a 24-hour period. The effluent from the reactor contained large visible gels. The product was not useful as a good quality material for extrusion or injection molding. Comparative example 3 A vertical stirred tube reactor was employed having an inside diameter of 16.5 cm and a useful internal length of 1.40 m and a volume of 0.026 cu m. The reactor was jacketed into three about equal zones, each zone having a thermocouple projecting into the reaction mixture. The top driven agitator had a shaft diameter of 2.5 cm and 1.3 cm straight arms spaced 6.3 cm apart on the agitator shaft. A plurality of 1.2 cm diameter fixed rods projected radially inwardly into the reactor for a distance of 6.17 cm. The fixed rods interdigitated with the agitator arms on rotation of the agitator. The reactor had a total heat transfer area of 1.04 sq m. The physical arrangement of the reactor was such that the axis of rotation was vertically disposed. The reaction mixture had excellent mixing in planes normal to the axis of the reactor and the agitator shaft while top to bottom mixing was very poor to nonexistent, resulting in what may be considered a plug flow reactor. A pump by means of an external line was connected between the top and bottom of the reactor. The pump was capable of recirculating the contents of the reactor at a rate of 7.5 times per hour. Equal parts by weight of styrene and ethylbenzene purified as in Example 2 and a polymerization initiating amount of a normal-butyllithium solution were pumped into the top of the reactor. The reactants were fed to the reactor at a rate of one-half reactor volume per hour for a residence of 2 hours. The following temperature relationships were observed: In a 24-hour period of operation, the weight average molecular weight could not be maintained closer than plus or minus 50,000. The major amount of polymerization appears to occur in the middle zone of the reactor. On extrusion of the product as a strand, gels or lumps were observed and the polymer was unsatisfactory for extrusion or injection molding.

Claims: A method for the anionic polymerization of anionically polymerizable alkenyl aromatic monomer with an organo-metallic anionic initiator in a continuous stirred tank reactor wherein the contents of the reactor are generally homogeneous and the polymerization components are continuously added and the reaction mixture continuously discharged from the reactor at essentially the same rate, and controlling the monomer flow stream to the reactor and measuring the molecular weight of the polymer in the reactor discharge stream characterized by a conversion of monomer to polymer exceeding 99 weight percent and controlling the initiator feed streams to the reactor by a signal obtained from said measuring of the molecular weight to provide a polymer of essentially constant molecular weight. The method of Claim 1 wherein the polymerizable monomer is styrene. The method of Claim 1 wherein the polymerizable monomer is para-vinyl toluene. The method of claim 2 wherein styrene is diluted with ethylbenzene. The method of Claim 4 wherein the weight ratio of ethylbenzene to styrene is about 1:1. The method of Claim 1 wherein the organometallic polymerization initiating compound is a butyllithium. The method of Claim 1 wherein the reactor is a closed loop. The method of Claim 1 including the step of providing a first signal which varies with the molecular weight of the polymer in the effluent from the reactor, the first signal altering the rate of polymerization initiator addition to the reactor to maintain a generally constant molecular weight of the polymer, measuring the molecular weight of the polymer thereby obtaining a second signal, employing the second signal to compensate the first signal generating means for drift or error in the first signal generating means to thereby maintain a generally uniform molecular weight of the polymer in the reactor effluent. An apparatus (10) for the preparation of anionically polymerized alkenyl aromatic polymers, comprising in cooperative combination a monomer supply means, a monomer flow control means associated with a discharge of the monomer supply means (41), an anionic polymerization initiator supply means (51), an initiator flow control means (53) in association with a discharge of the initiator supply means (52), a continuously stirred tank reactor (46) having an inlet (47) and an outlet (48), the inlet (47) of the continuously stirred tank reactor (46) being in operative communication with the monomer flow control means and the initiator flow control means (53) and adapted to receive material therefrom; a discharge conduit (55) connected to the discharge (48) of the continuously stirred tank reactor, (46) the discharge conduit (55) being in operative communication, a means (57) to provide a first signal which varies as molecular weight of polymer in effluent from the continuously stirred tank reactor (46) varies, the first signal adjusting the initiator flow control to thereby provide molecular control of a polymer being prepared, means (56) to measure the molecular weight of a polymer and provide a second signal indicative of the molecular weight of the polymer, means (58) to receive the second signal and adjust the means (57) to provide a first signal to thereby provide a polymer of a generally uniform molecular weight.

Inventors: PIRC, MICHAEL, PRIDDY, DUANE B.
Applicants: THE DOW CHEMICAL COMPANY
Application year: 1984
Main classification: C08F2
IPC codes: C08F2, B01J19