METAL PIGMENT OF IMPROVED STORAGE RESISTANCE

Abstract: A composition of matter includes a leafing, metallic pigment and a means for inhibiting reaction of the pigment to form hydrogen gas, the improvement including a liquid fatty acid in an amount effective for at least reducing loss of optical properties which would occur in the absence of such fatty acid. A water-borne coating is provided, containing an effective amount of liquid fatty acid for improved optical properties.

Description: The invention concerns improved storability of inhibited, leafing, metallic pigment compositions. The invention also concerns a water-borne coating having the ability to yield improved optical properties when pigmented. These as well as other objects which will become apparent in the discussion that follows are achieved, according to the present invention, by providing in a composition of matter including a leafing, metallic pigment and a means for inhibiting reaction of the pigment to form hydrogen gas, the improvement comprising a liquid fatty acid in an amount effective for at least reducing loss of optical properties which would occur in the absence of such fatty acid, and by providing a water-borne coating containing an effective amount of liquid fatty acid for improved optical properties. Various treatments have been proposed for inhibiting the reaction of water with metal pigment to form hydrogen gas. When such treatment is applied to leafing, metallic pigment, optical properties of the pigment can be degraded. Thus, the total reflectance of a coating containing the pigment can be less, as a function of the length of time since the inhibiting treatment took place. We have discovered that if the inhibited pigment is provided with a liquid fatty acid additive, optical properties are maintained or recaptured. The liquid fatty acid is added at a level of 1-20% based on the weight of the pigment, with a 10% level being preferred. We have also discovered that liquid fatty acid additions yield improved optical properties even in the case of leafing aluminum pigment which has not been treated for inhibiting the water reaction. By "liquid", we mean that the fatty acid is liquid at room temperature (72°F.,22°C.). An example is isostearic acid, where, by "isostearic acid", we intend the more common meaning as explained, e.g. in U.S. Patent No. 4,236,934 at column 5, line 28. The distinction between leafing and non-leafing pigment is explained, for instance, in "Aluminum Flake Pigment" by Rolf Rolles in Pigment Handbook, Volume I, John Wiley & Sons (New York, 1973) and in the above-referenced 4,236,934. Further information, particularly on products of Aluminum Company of America, is contained in "Alcoa Aluminum Pigments Product Data", Section PAP 902, June, 1982. As used herein, "leafing" means a pigment having a leafing value of at least 50 per ASTM D 480-70 before any treatment for inhibiting the water reaction. The invention is particularly applicable to leafing metal pigment treated with the class of chemicals defined in the concurrently filed patent application U.S. 510,982 of Williams and Claassen for "Water Resistant Aluminum Particles and Coating". A preferred inhibiting agent disclosed in that patent application is Virco-Pet 20 of Mobil Chemical Company. A preferred metal is aluminum. Typically, the pigment composition of the invention will be supplied in paste form by provision of sufficient mineral spirits to place the non-volatile content (essentially the aluminum) in the 60 to 75% range. An attractive alternative for the present invention is the substitution of water for all or part of the mineral spirits. The invention is particularly useful in conjunction with water-borne coatings, such as asphalt emulsion coatings, where the pigment composition, including liquid fatty acid, is effective to maintain or recapture total reflectance. Besides addition in admixture with the pigment, according to other embodiments of the invention, the liquid fatty acid is added to the water-borne coating, either before or after the pigment is mixed into the coating. Asphalt emulsions are formed essentially from asphalt, water, and a wetting agent. Other water-borne coating materials useful for the invention are shown in U.S. Patent No. 3,918,984 and in the Kirk-Othmer Encyclopedia of Chemical Technology , 2nd Ed., V.2, particularly pages 778 to 781 and 797 to 798. Further illustrative of the present invention are the following examples. EXAMPLES I. Effect of Time on Total Reflectance On day Zero, Alcoa® Grade 6230 leafing aluminum pigment was treated with 10% Virco-Pet 20 material as in Example 3 of the above-referenced application of Williams and Claassen, supplemented with the inclusion of 6% Atlas G3300 surfactant to provide a test batch of paste. This batch was stored at room temperature (about 72°F., 22°C.). On different numbers of days subsequent to day zero, samples of the batch were mixed into Koppers 460 asphalt emulsion (contains water) and the resulting mixture applied as coating on panels, dried, and tested for total reflectance. Over time, total reflectance decreases, as shown in Table I. The reflectance measurements were made using a Diano TR-1 total reflectometer. This instrument utilizes an integrating sphere principle to sum the light reflected in all directions. II. Recapture of Initial Total Reflectance A batch of Alcoa Grade 6230 leafing aluminum pigment (75% NV) was prepared as in Example 3 of the above-referenced application of Williams and Claassen on day zero and then stored at room temperature. About 325 days later, separate 42.6-gram samples were removed and mixed as follows: a. Control mixture 42.6 grams pigment 3.3 grams mineral spirits 1.9 grams G3300 surfactant b. Isostearic mixture 42.6 grams pigment 3.2 grams Emery® 871 isostearic acid .1 gram mineral spirits 1.9 grams G3300 surfactant One day later, the control mixture and the isostearic mixture were thoroughly mixed, each with 202 grams of Koppers 460 asphalt emulsion. The thus-pigmented emulsions were applied as coating on panels, dried, and tested for total reflectance. The control gave a total reflectance of 30%, thus showing the same degradation as in I. above as compared with the total reflectance shown in Table IIB of the above-referenced application of Williams and Claassen for Example 3. In contrast, the isostearic mixture measured 42.5% in total reflectance, showing the ability of isostearic acid addition to restore total reflectance. III. Effect of Various Amounts of Stearic and Isostearic Using the same starting batch as in II, above, various amounts of stearic acid and isostearic acid, together with mineral spirits and surfactant, were mixed with 100-gram samples of the batch. The mix ingredients and other characteristics are given in Table II for the stearic acid examples and in Table III for isostearic acid. Alcoa Grade 6230 leafing aluminum pigment already has stearic acid on it to impart its leafing characteristic. The amounts of stearic acid in Table II are in addition to the basic leafing-effective coating of stearic acid. This extra stearic acid was for the purpose of determining whether extra stearic acid might be able to recapture total reflectance in the manner demonstrated for isostearic acid in II. above. The isostearic examples are for the purpose of determining the effect of isostearic concentration and additionally provide experience with different mineral spirits levels. Following storage overnight, sufficient quantities of these mixtures to provide 31.2 grams aluminum were mixed with 202 grams of Koppers 460 asphalt emulsion, then coated on panels, dried, and tested for total reflectance. The total reflectance measurement results are presented in Tables II and III. If there is any effect from extra stearic acid, it would seem to be a negative one. In contrast, the recapture of lost total reflectance by isostearic acid addition is evident, with recapture improving with increasing isostearic addition. In terms of the effectiveness of the isostearic addition in causing recapture, it is better where no supplemental mineral spirits are added. IV. Accelerated Testing A quantity of Alcoa Grade 6230 leafing aluminum pigment of 65% NV (non-volatiles) was divided into four samples. One served as a control and the others were mixed with Virco-Pet 20 material (VP), isostearic acid (Iso), and butyl alcohol in proportions as shown in Table IV under "Description", always based on aluminum weight. The resulting aluminum pigment compositions were put in cans and the cans put in an oven at 110°F. After various periods of time from one week to four weeks, the compositions were removed and allowed to cool to room temperature. The individual compositions were then incorporated into Koppers 460 asphalt emulsion (at 2 pounds aluminum/gallon for a 65% NV) using Atlas G3300 surfactant at 6% based on weight of aluminum. The pigmented asphalt emulsions were applied as coatings on panels, dried, and tested for total reflectance. Total reflectance measurements are presented in Table IV. As apparent from the data in Table IV, the total reflectance of the coating containing only the Virco-Pet 20 treated pigment subjected to 1 week of accelerated aging had been degraded to an unacceptable level. After 4 weeks, the untreated pigment control coating had degraded. Incorporation of isostearic kept total reflectance high compared to tests A and B under the rugged conditions of this test, even after 4 weeks. V. Addition to the Coating A quantity of Alcoa Grade 6232 leafing aluminum pigment of 67.6% NV (non-volatiles), manufactured on day zero and subsequently stored at room temperature, was divided into two samples 59 days from day zero. One served as a control and the other was mixed on day 59 with Virco-Pet 20 material (VP) and isostearic acid (Iso) in proportions as shown in Table V under "Description", always based on aluminum weight. The control and the composition resulting from the mixing were put in cans and the cans put in an oven at 125°F. After aging for three weeks, the control and composition were removed, cooled to room temperature, and then incorporated into Koppers 460 asphalt emulsion (at 22.5 grams of pigment composition equal to 15.6 grams aluminum) per 101 grams of Koppers 460 asphalt emulsion using Atlas G3300 surfactant at 0.9 grams. Example 21142-15A (the control), after shaking in the mixer, was foamy and brown in color. Bubbles were present. The emulsion had broken. It was not spread on a panel for a total reflectance measurement, because to do so would have resulted in a patchy, unsatisfactory coating. Example 21142-15C, in the emulsion, was spread on a panel, dried, and measured for total reflectance. Its total reflectance measurement was 32.8. Two additional tests were made by adding to 100 grams of the broken asphalt emulsion resulting from Example 21142-15A and to 100 grams of the asphalt emulsion prepared from Example 21142-15C, 1.2 grams (10% based on the weight of aluminum in the mixture) of isostearic acid (Century 1105 of Union Camp). Following mixing, it was found that the coating mixture containing Example 21142-15A had re-emulsified; it was spread on a panel, dried, and measured for total reflectance, giving a reading of 37.0. The asphalt emulsion coating mixture containing Example 21142-15C, now having a total of 20% isostearic acid, based on the weight of aluminum, gave a total reflectance measurement of 35.3.

Claims: A composition of matter having improved properties, and said composition including a leafing, metallic pigment, preferably comprising aluminum, and a means for inhibiting reaction of the pigment to form hydrogen gas, characterized by comprising a liquid fatty acid in an amount of 1-20 percent based on the weight of the pigment. A composition of matter as claimed in claim 1, characterized in that the liquid fatty acid comprises isostearic acid. A composition of matter as claimed in claim 1 or 2, characterized by being in the form of paste, a water-borne coating, or in an asphalt emulsion. A composition of matter as claimed in claim 1, wherein the liquid fatty acid is present in an amount of 10% based on the weight of the pigment. A water-borne coating pigmented with a leafing, metallic pigment, preferably comprising an asphalt emulsion, characterized by comprising a liquid fatty acid in an amount of 1-20 percent based on the weight of the pigment. A water-borne coating as claimed in claim 5, wherein the liquid fatty acid is present in an amount of 10% based on the weight of the pigment. A method for obtaining coatings of improved optical properties, said coatings including metallic pigment having a leafing character, characterized by comprising adding to a coating mixture a liquid fatty acid in an amount of 1-20 percent based on the weight of the pigment. A method as claimed in claim 7, characterized by the coating mixture including asphalt emulsion. A method as claimed in claim 7, characterized by the liquid fatty acid being added to the coating mixture prior to the pigment. A method as claimed in claim 7, characterized by the liquid fatty acid being added to the coating mixture in admixture with said pigment. A method as claimed in claim 7, characterized by the liquid fatty acid being added to the coating mixture subsequent to the pigment. A method as claimed in claim 7, wherein the liquid fatty acid is added in an amount of 10% based on the weight of the pigment.

Inventors: BOOZ, ALBERT DAVID, CLAASSEN, PAMELA LOUISE
Applicants: SILBERLINE MANUFACTURING CO. INC.
Application year: 1984
Main classification: C09B17
IPC codes: C09C1, C09D7, C09D195, C09D5