FIRE RETARDANT POLYAMIDE COMPOSITION

Abstract: A fire retardant polyamide composition comprising at least 35% by weight of polyamide having a molecular weight of at least 3000, at least 3.5% but preferably not more than 10% by weight of the condensation product of 2 moles perchlorocyclopentadiene and 1 mole of 1,5-cyclooctadiene, at least 2%, preferably at least 4% desirably not more than 10% by weight of melamine, a salt of melamine or an organic derivative of melamine and at least 0.5%, but preferably not more than 5.0% of at least one oxide selected from iron oxide and tin oxide, wherein the weight ratio of chlorinated compound to oxide is between 1:1 and 10:1 preferably between 2:1 and 6:1 and the constituents of the composition total 100%. The composition provides improved burning performance in the UL94 test in that dripping is prevented. The composition also provides acceptable burning perform­ ance at a lower concentration of total additives than when halogenated fire retardant/synergistic oxide combinations are used.

Description: The present invention relates to fire retardant polyamide compositions. The use of melamine or melamine derivatives, such as salts of melamine or melamine substituted at one or more of the -NH₂ groups with an organic radical, as a fire retardant in polyamide compositions is well known. British Patent No. 1 204 835 discloses the use in polyamides of melamine, melam or a melamine derivative selected from compounds of the formula: where R and R¹ represent hydrogen, methyl, ethyl, phenyl, toluyl or halogenophenyl. European Patent No. 1322 discloses polyamide compositions containing the salts of melamine or melamine derivatives wherein the salt is selected from borate, sulphamate or demi-sulphate. USP 4 298 518 discloses the use of melamine cyanurate in polyamides. It has now been found that the fire retardant performance of these additives can be improved by the addition of a very specific combination of fire retardant additives. In particular compositions which exhibit freedom from dripping in burning tests can be produced. According to the invention there is provided a fire retardant polyamide moulding composition free of glass fibres comprising a polyamide having a molecular weight of at least 3000, at least 3.5% but preferably not more than 10%, desirably not more than 7.5% by weight of the condensation product of 2 moles perchlorocyclopentadiene and 1 mole of 1,5-cyclooctadiene, at least 2%, preferably at least 4%, desirably not more than 10% by weight of melamine, a salt of melamine or an organic derivative of melamine and at least 0.5%, but preferably not more than 5.0%, desirably not more than 3.0% of at least one oxide selected from iron oxide and tin oxide, wherein the weight ratio of chlorinated compound to oxide is between 1:1 and 10:1 preferably between 2:1 and 6:1,the percentages of the constituents being based on the total weight of the composition. The composition is particularly suited for use as a moulding composition. The presence of the specified combination of chlorinated compound and oxide has a particularly beneficial effect on dripping of the composition when it is subjected to burning. Compositions according to the invention can show a complete absence of drips when subjected to, for example, the Underwriters Laboratories Standard UL94 fire retardant test procedure. The defined combination of the chlorinated compound and the oxide has a very specific effect on the fire retardant performance which is not achieved with alternative compounds which might be considered as comparable by those skilled in the art. Thus apart from the fact that both constituents are essential to the performance of the composition the use of an alternative halogenated compound or the use of alternative synergistic oxides does not give an equivalent effect. Alternative synergistic oxides may be present provided there is also present at least 0.5% by weight of one of the specified oxides. As well as providing the property of non-dripping the compositions of the invention have the added advantage that this is achieved at lower total concentrations of fire retardant additives and at lower cost than when a halogenated fire retardant/synergistic oxide combination is used to obtain a non-dripping burning performance. The iron oxide may be in the form of Fe₂O₃ or Fe₃O₄, preferably the former or as a ferrite such as zinc or magnesium ferrite. The tin oxide preferably is of the formula SnO₂. The condensation product of chlorocyclopentadiene and cyclooctadiene has the formula: hereinafter referred to by the formula C₁₈H₁₂Cl₁₂. The melamine based constituent may be melamine, melam, a salt of melamine selected from the cyanurate, sulphamate, borate or demi-sulphate, or an organic derivative of melamine of formula: where R and R¹ may be the same or different and hydrogen, lower alkyl, phenyl, tolyl or halophenyl. Mixtures of melamine based constituents can be used. The preferred polyamides for use in the invention are thermoplastic polyamides having a melting point of at least 220°C and containing a major proportion of repeating units derived from hexamethylene adipamide, hexamethylene sebacamide or caprolactam. The most suitable polymers are homopolymers of nylon 66 and nylon 6 and copolymers of these materials containing not more than 50% by weight of units other than nylon 66 or nylon 6. These other units may be, for example, of nylon 6.9 or 6.10. The preferred materials are the homopolymers of nylon 66 and nylon 6 and copolymers of nylon 66 with nylon 6. The polyamides preferably have a number average molecular weight of at least 3000. The fire-retardant characteristics of the composition of the invention are conveniently determined using the Underwriters Laboratories Test standard UL94. Using the Vertical Burning Test of this Standard the compositions of the invention should have a rating of 94 V1 or better when tested on samples having a thickness of 1.6 mm both when conditioned at a relative humidity of 50% for 48 hours or at 70°C for one week. In addition to the polyamide and the specified ingredients the compositions of the invention may contain any of the auxiliary materials which are known for use in polyamide compositions. These include heat and light stabilisers, pigments, lubricants and mould release agents. The compositions of the invention are suitable for moulding general purpose electrical components or other components where fire retardancy is important. The invention is further illustrated by reference to the following examples. COMPARATIVE EXAMPLE A Granules of a 97:3 copolymer of nylon 66 and nylon 6 were dry blended with 10% by weight of melamine cyanurate. The mixture was compounded in a single screw extruder at a temperature of 280°C and the intimately mixed product was extruded as a lace, cooled in a water bath and chopped into granules. The product was dried and injection moulded into samples suitable for evaluation in the UL94 Standard and for measurement of tracking resistance. The compositions gave a rating according to the UL94 standard on the Vertical Burning Test of VO both after conditioning at 50% Relative Humidity for 48 hours and at 70°C for 168 hours However, all the samples tested gave molten drips. These drips did not ignite the cotton wool used in the test and the composition is therefore classified as VO. EXAMPLE 1 The procedure of Comparative Example A was followed except in that the composition also contained the combinations of C₁₈H₁₂Cl₁₂ and Fe₂O₃ listed in Table 1. The balance of the compositions listed in Table 1 consists of a polyamide which is a 97:3 copolymer of nylon 66 and nylon 6. EXAMPLE 2 The procedure of Example 1 was followed except in that there was present a mixture of synergist additives including iron oxide. The results are given in Table 2. COMPARATIVE EXAMPLE B The procedure of Comparative Example A was followed except in that there were additionally present the halogenated compounds listed in Table 3. EXAMPLE 3 The compositions listed in Table 4 were prepared by the compounding procedure of Comparative Example A. The results show that melamine cyanurate can be replaced by melamine or melamine sulphate. COMPARATIVE EXAMPLE C Compositions identical to those of Example 3 were prepared except in that the iron oxide was omitted from the compositions. EXAMPLE 4 The compositions listed in Table 5 were prepared according to the compounding procedure of comparative Example A. The results show that zinc ferrite and tin oxide are effective synergists.

Claims: A fire retardant polyamide composition free of glass fibres comprising a polyamide having a molecular weight of at least 3000, at least 3.5% by weight of the condensation product of 2 moles perchlorocylopentadiene and 1 mole of 1,5-cyclooctadiene, from 2% to 10% by weight of melamine, a salt of melamine or an organic derivative of melamine and from 0.5% to 5.0% by weight of at least one synergistic metal oxide provided that at least 0.5% by weight is selected from iron oxide and tin oxide, wherein the weight ratio of chlorinated compound to oxide is between 1:1 and 10:1, the percentages of the constituents being based on the total weight of the composition. A fire retardant polyamide composition according to claim 1 containing not more than 3.0% by weight of the oxide. A fire retardant polyamide composition according to either of claims 1 or 2 wherein the concentration of the condensation product is not greater than 10% by weight. A fire retardant polyamide composition according to claim 3 wherein the concentration of condensation product is not greater than 7.5% by weight. A fire retardant polyamide composition according to any one of the preceding claims wherein the melamine compound is selected from melamine, melamine cyanurate or melamine demi-sulphate. A fire retardant polyamide composition according to claim 5 wherein the oxide is an iron oxide in the form of Fe₂O₃, Fe₃O₄, zinc ferrite or magnesium ferrite. Articles moulded from a composition according to any one of claims 1 to 6.

Inventors: GABRIEL, WILLIAMS IAN
Applicants: IMPERIAL CHEMICAL INDUSTRIES PLC
Application year: 1984
Main classification: C08L77
IPC codes: C08K3, C08K5, C08L77, C08K13