PROCESS OF PREPARING FERRITE WITH A PREDETERMINED FERROUS CONTENT

Abstract: Process of calcining and ball milling Manganese Zinc MnZn, ferrite material for achieving a ferrite having a ferrous iron content appropriate for optimum magnetic properties. The process includes a controlled atmosphere, time, and temperature for the calcining process step, and a controlled ball milling step overtime where the interaction of the stainless steel balls and milled slurry contributes to final ferrous iron content. These two process steps are balanced yielding a MnZn ferrite of a predetermined particle size with a controlled ferrous iron content which is a function of both the calcining and ball milling steps.

Description: Process of preparing ferrite with a predetermined ferrous content This invention relates to development of proper ferrous iron concentration in Manganese Zinc, MnZn, ferrite prior to the densification step by methodsi such as hot pressing or sintering, and more particularly, provides steps of calcining and milling which are balanced to provide proper final ferrous iron content in a ferrite composition. Prior art patents related to the production of MnZn ferrite have not approached the development of proper ferrous iron content during the calcining and milling steps. The prior art has failed to recognize that ferrous iron content can be controlled during the calcining operation and during the length of the milling operation. While the prior art teaches calcining, the prior art does not appear to recognize that the calcining ought to be done in an inert atmosphere such as nitrogen, as recognized in this disclosure The present invention is for a process of calcining and ball milling MnZn ferrite material having compositions in the ranges of about 52-55 mole percent Fe203, about 26-32 mole percent MnO, and about 15-20 mole percent ZnO for achieving a ferrite having a ferrous iron content of about 1,5 percent, thereby providing optimum magnetic properties. This ferrous iron content is achieved by controlling the atmosphere, the time and the temperature of the calcining process, as well as controlling the ball milling step which further'contributes to the ferrous iron content by interaction of the stainless steel balls and the ferrite slurry being milled. These two steps are balanced so that both calcining and ball milling contribute to the final ferrous iron content where the ball milling is the primary contributor to the final particle size. One significant aspect and feature of the invention as claimed is that the process used in the present invention is a key step in the production of ferrite, and particularly MnZn ferrite for magnetic transducer heads. An optimum MnZn ferrite product can be achieved by proper control of the chemistry of the material prior to the final densification step. Another significant aspect and feature of the present invention is an optimum ferrite product for subsequent processing and an optimum ferrite product having qualities which are subsequently maintained through processing steps. Figure 1 illustrates apparatus for precalcine and post calcine wet ball milling and, Figure 2 illustrates apparatus for calcining. Production of MnZn ferrite is done under consideration of the ferrous iron content in the final ferrite material in order to assure the desired magnetic properties. The ferrous iron content is dependent on the MnZn ferrite composition being utilized. The ferrous iron is developed through proper control of atmosphere, time, temperature, and mechanical working following heat treatment, and is accomplished in the following steps of the process. Starting with powders of iron oxide, Fe203, zinc oxide, ZnO, and manganese carbonate, Mac03, the powders are weighed out in proper proportions to achieve the desired ferrite composition, with adjustments being made for volatile losses and iron pick up during milling operations. The ingredients are wet or dry milled together to obtain intimate mixing of these powders. The composition can be either wet ball or dry ball milled with stainless steel balls in a stainless steel container. These milled ingrediants are dryed, pulverized into a fine powder and then placed into a furnace at a temperature in the range of 900 to 1100 OC for one to ten hours under a flowing inert gas. This step eliminates volatiles and the carbonate, allows the oxides to automatically rearrange and form the ferritet spinel structure, and allows for the reduction of the desired amount of iron. This reduction is expressed as 3Fe203 = 2Fe304 + 1/2 Figure 1 illustrates apparatus 10 for precalcine ball milling or post calcine ball milling including a stainless steel ball mill 12 and stainless steel balls 14a-14n therein. The mill 12 is essentially a closed cylinder 16 with a locking cover 18. The mill 12 is supported on a plurality of opposing rotatively driven rollers 20 and 22 which transfer like motion to the mill 12 as illustrated by the arrows. The closed mill 12 includes the powdered ferrite material 24 in a water solution 26 providing a milled slurry. Figure 2 illustrates calcining apparatus 30 including a closed environmental oven 32. An electric heater 34 connected to a power supply 36 controlled by a programmed controller 38. A heat sensor 40 also connects to the programmed controller 38. A gas inlet 42 connects to a source of inert gas such as nitrogen 44 through a gas control valve 46 which connects to the programmed controller 38. The ferrite material 48 to be calcined is placed into a suitable crucible container 50. The programmed controller 38 is programmed to achieve the desired temperature and atmosphere over time within the oven 32. The calcined ferrite is then cooled while being continuously swept with a flowing inert gas such as nitrogen to prevent any reoxidation of the ferrous iron. The cool down temperature of the calcine mixture should be at least 150 OC or less over a period of time prior to exposure to any different type of atmosphere. A second milling then pulverizes the ferrite material to a final particle size in a stainless steel ball media sufficient to achieve a predetermined particle size and ferrous content. Prior to the second milling step, there can be a pulverizing step of the ferrite material to a size of about 0,1 the diameter of the milling media. The wet ball milling occurs over a period of one to four hours. 'he second and final milling step can be a wet ball milling of the pulverized ferrite material for achieving the desired end particle size and terrous content. Again, stainless steel balls in a stainless steel container .-e utilized. Iron debris from the first milling step acts as a catylist in the calcining step, further supplementing this mixture and affecting the control of the ferrous iron content during the calcine operation. This provides that the properties of the ferrite material are optimized for hot pressing or sintering. Example Using MnZn ferrite having a composition of 53 mole percent of Fe203; 32 Mole percent of MnO and 15 Mole percent ZnO, the Fe2O3, MnC03, and ZnO are wet ball milled in a 11,35 liter (2,5 gallon) stainless steel ball mill with stainless steel media in water for two hours. This mixture is dried at 125 OC and pulverized to obtain a fine powder. Under a flowing nitrogen atmosphere, the ferrite is calcined at 1070 OC for five hours. Following the calcine operation, the ferrite material is pulverized and ball milled in a 6,81 liter (1,5 gallon) stainless steel mill and stainless steel media in water for two hours. This provides a ferrite having ferrous iron content of about 1,7 percent. This is a representative example of the principles and teachings of the disclosure of the present invention.

Claims: Claims: 1. Process of preparing ferrite with a predetermined ferrous content comprising the steps of: milling a ferrite composition in a stainless steel mill (12) with stainless steel media (14A-14N), drying the milled mixture and pulverizing to reach a powder, calcining the powder for a first predetermined time interval under a flowing inert atmosphere and pulverizing and ball milling in a stainless steel mill (12) with stainless steel media (14A-14N) for a second predetermined time interval providing an optimum ferrous iron content in the ferrite composition. 2. The process of claim 1, wherein said ferrite composition comprises a mixture of Fe2O37 MnC03, and ZnO. 3. The process of any preceding claim, wherein said inert atmosphere is nitrogen. 4. The process of any preceding claim, wherein said temperature is in a range of 900 to 1100 oC. 5. The process of any preceding claim, wherein said first predetermined time interval is one to ten hours. 6. The process of any preceding claim, wherein said second predetermined time interval is one to four hours. 7. The process of any preceding claim, comprising the steps of cooling said calcine mixture in an inert flowing atmosphere. 8. The process of claim 7, wherein said mixture is cooled to a temperature of 150 0C or less. 9. Process for preparing MnZn ferrite with a predetermined ferrous content prior two hot pressing or sintering comprising the steps of: calcining a mixture of Fe2O3, MnC03, and ZnO in a flowing nitrogen atmosphere at a temperature of 900 to 1100 0C for one to ten hours, cooling said calcine mixture to 150 OC or less in an atmosphere of flowing nitrogen, pulverizing said calcine ferrite mixture to a final particle size not exceeding 0,1 diameter of milling media and wet ball milling said pulverized ferrite mixture using ball media for a-one to four hour period thereby achieving predetermined particle size with predetermined ferrous content.

Inventors: SCHEIDECKER, RALPH WILLIAM, SUCHOMEL, ROBERT RICHARD
Applicants: INTERNATIONAL BUSINESS MACHINES CORPORATION
Application year: 1984
Main classification: C04B35
IPC codes: C01G49, H01F1, C04B35