TAILORING ACID STRENGTH OF ZSM-11

Abstract: The present invention relates to a method for preparing an iron-containing synthetic crystalline siliceous molecular sieve material having tailored acid strength and having the structure of ZMS-11, to the tailored synthetic material resulting from said method and to use of said tailored synthetic material as a catalyst component for catalytic conversion of organic com­ pounds.

Description: TAILORING ACID STRENGTH OF ZSM-ll This invention relates to a method for tailoring the acid strength of a synthetic crystalline siliceous molecular sieve material having the structure of ZSM-ll, to the tailored synthetic material resulting from said method and to the use of said tailored synthetic material as a catalyst component for catalytic conversion of organic compounds. Zeolitic materials, both natural and synthetic, have been demonstrated in the past to have catalytic properties for various types of hydrocarbon conversion. Certain zeolitic materials are ordered, porous crystalline aluminosilicates having a definite crystalline structure as determined by X-ray diffraction, within which there are a large number of smaller cavities which may be interconnected by a number of still smaller channels or pores. These cavities and pores are uniform in size within a specific zeolitic material. Since the dimensions of these pores are such as to accept for adsorption molecules of certain dimensions while rejecting those of larger dimensions, these materials have come to be known as "molecular sieves" and are utilized in a variety of ways to take advantage of these properties. Such molecular sieves, both natural and synthetic, include a wide variety of positive ion-containing crystalline aluminosilicates. These aluminosilicates can be described as rigid three-dimensional frameworks of SiD4 and A104 in which the tetrahedra are cross-linked by the sharing of oxygen atoms whereby the ratio of the total aluminum and silicon atoms to oxygen atoms is 1:2. The electrovalence of the tetrahedra containing aluminum is balanced by the inclusion in the crystal of a cation, for example an alkali metal or an alkaline earth metal cation. This can be expressed wherein the ratio of aluminum to the number of various cations, such as Ca/2, Sr/2, Na, K or Li, is equal to unity. One type of cation may be exchanged either entirely or partially with another type of cation utilizing ion exchange techniques in a conventional manner. By means of such cation exchange, it has been possible to vary the properties of a given aluminosilicate by suitable selection of the cation. The spaces between the tetrahedra are occupied by molecules of water prior to dehydration. Prior art techniques have resulted in the formation of a great variety of synthetic aluminosilicate zeolites. The zeolites have come to be designated by letter or other convenient symbols, as illustrated by zeolite A (U. S. Patent 2,882,243), zeolite X (U. S. Patent 2,882,244), zeolite Y (U. S. Patent 3,130,007), zeolite ZK-5 (U. S. Patent 3,247,195), zeolite ZK-4 (U. S. Patent 3,314,752), zeolite ZSM-5 (U. S. Patent 3,702,886), zeolite ZSM-ll (U. S. Patent 3,709,979), zeolite ZSM-12 (U. S. Patent 3,832,449), zeolite ZSM-20 (U. S. Patent 3,972,983), zeolite ZSM-35 (U. S. Patent 4,016,245), zeolite ZSM-38 (U. S. Patent 4,046,859), and zeolite ZSM-23 (U. S. Patent 4,076,842) merely to name a few. Crystalline iron-containing silicate having the structure of zeolite ZSM-5 is claimed in U.S. Patent 4,208,305. U.S. Patent 4,238,318 claims use of the iron-containing silicate of U.S. Patent 4,208,305 as catalyst component for preparing aromatic hydrocarbons from feedstock comprising acyclic organic compounds such as methanol. Crystalline iron-containing silicates are used in U.S. Patent 4,244,807 for reforming and in U.S. Patent 4,329,233 for purifying water. The present invention provides a means for tailoring the acid strength of a synthetic crystalline siliceous molecular sieve material having the structure of zeolite ZSM-ll. In particular, the present invention involves synthesizing said zeolite in a particular fashion to include both aluminum and iron in its anionic framework, i.e. preparation of ferroaluminosilicate of ZSM-ll structure containing tetrahedrally coordinated aluminum and iron, within certain compositional limits. The present invention is also directed to the tailored zeolite so synthesized, as well as to its use in catalytic conversion of organic, e.g. hydrocarbon, compounds. In its zeolite synthesis method aspect, the present invention comprises preparing a mixture containing a source of organic cat ions, a source of silicon, a deliberately-added source of aluminum, a source of iron, a source of alkali metal or alkaline earth metal ions and water, with such a mixture having a particular composition in terms of mole ratios of oxides and ions; maintaining the mixture until crystalline siliceous molecular sieve material is formed at a temperature of from 1000C to 1600C for a time of from 48 hours to 100 days; and recovering from the mixture a particular type of crystalline siliceous molecular sieve material. The components of the reaction mixture used to form the molecular sieve material are present in the following ratios: OH /SiO2 0.05 - 0.20 H20/OH 50-400 Si02/A1203 60-5000 SiO2/Fe203 30-500 R'/R'+M 0.02 - 1.0 wherein R' represents organic cations and M represents alkali metal or alkaline earth metal ions. The crystalline molecular sieve material recovered from the mixture is characterized by an X-ray diffraction pattern substantially as shown in Table 1 set forth hereinafter, and by a composition on an anhydrous basis and in terms of moles of oxides per mole of silica expressed by the formula: (1 + 0.3)(a + b)R2/nO: a Fe203: b A1203: SiO2 wherein R is at least one cation having the valence n and 0.002 < (a+b) < 0.1 a > 0.0016, and b > 0.0004. Such molecular sieve material also exhibits, when in the ammonium form, a temperature-programmed ammonia desorption peak of from greater than 3100 C to less than 3800C and a temperature-programmed ammonia desorption peak half-height width of from greater than 1400C to less than 1550C. In other aspects, the present invention relates to the particular crystalline molecular sieve material per se recovered from the reaction mixture, to catalyst compositions containing such molecular sieve material and to the catalytic use of such molecular sieve material for the conversion of organic compounds. The catalyst compositions herein, for example, can contain from 1 percent to 90 percent by weight of the crystalline molecular sieve material and from 10 percent to 99 percent by weight of an inorganic oxide matrix material. The acid strength-tailored crystalline ferroaluminosilicate of this invention is a unique composition of matter which exhibits a valuable combination of catalytic and hydrophilic properties which distinguishes it from known aluminosilicates of ZSM-ll structure and iron-containing silicates of any known structure. The ferroaluminosilicate material of the present invention will exhibit unique and useful catalytic, sorptive and shape selective properties along with a silica/alumina mole ratio of as high as about 2500. Preferably such metals have silica/alumina mole ratios less than 900, more preferably less than 500. It is known that catalytic activity and hydrophilic properties of aluminosilicates decrease with increased silica/alumina mole ratios. It is also known that certain aluminosilicates, e.g. Mordenite, Beta and ZSM-35, become more difficult to synthesize as the mole ratio of silica/alumina in the crystallization mixture is increased. It is noted that boron-containing silicates (M. Taramasso et al, Proceedings of the Fifth International Conference on Zeolites, Heyden & Son Ltd., 1980, pp. 40-48) having the structure of zeolite ZSM-ll can be prepared, but, like the corresponding aluminosilicate, the hydrophilic properties thereof may be decreased by increasing the silica/boria mole ratio. The ferroaluminosilicate molecular sieve material prepared by the method of this invention, however, overcomes the potential problems associated with high silica/alumina mole ratio aluminosilicates and with borosilicates in that the present material exhibits a unique tailored acid strength and hydrophilic properties distinguishing it from known aluminosilicates and borosilicates of ZSM-ll structure. Zeolite ZSM-ll is more particularly described in U.S. Patent 3,709,979. The original alkali metal or alkaline earth metal cations of the as synthesized acid strength-tailored ferroaluminosilicate can be replaced in accordance with techniques well known in the art, at least in part, by ion exchange with other cations. Preferred replacing cations include metal ions, hydrogen ions, hydrogen precursor, e.g. ammonium ions and mixtures thereof. Preferred metal cations include rare earth metal and metals of Groups IA, IIA, IIIA, IVA, IB, IIB, IIIB, IVB and VIII of the Periodic Table of the Elements (Sargent-Welch Scientific Company, 1979). Typical ion exchange technique would be to contact the synthetic ferroaluminosilicate with a salt of the desired replacing cation or cations. Examples of such salts include the halides, e.g. chlorides, nitrates and sulfates. The acid-strength tailored zeolite of the present invention can be beneficially thermally treated, either before or after ion exchange. This thermal treatment is performed by heating the zeolite in an atmosphere such as air, nitrogen, hydrogen, steam, etc, at a temperature of from about 3700C to about 11000C for from about 1 minute to about 20 hours. While subatmospheric or superatmospheric pressures may be used for this thermal treatment, atmospheric pressure is desired for reasons of convenience. It may be desirable in certain instances to conduct this thermal treatment at from about 3700C to about 7500C, but the structure of the acid-strength tailored zeolite hereof should be stable up to about 11000C. Zeolite ZSM-l1 exhibits a definite X-ray diffraction which distinguishes it from other zeolites. The X-ray diffraction pattern of the ferroaluminosilicate of the present invention having the structure of zeolite ZSM-l1 has the following characteristic values: Table 1 Interplanar d-Spacing (A) Relative Intensity, I/Io 11.2 + .2 m 10.1 + .2 w 6.05 + .2 w 5.61 + .1 w 4.62 + .1 w 4.39 + .08 w 3.86 + .07 vs 3.73 + .07 s 3.45 + .07 w 3.07 + .05 w 3.00 + .05 w 2.01 + .02 w These X-ray diffraction data were collected with the Philips APD-3600 X-ray system, using copper K-alpha radiation. The positions of the peaks, expressed in degrees 2 theta, where theta is the Bragg angle, were determined by step-scanning at 0.02 degrees of 2 theta intervals and a counting time of 2 seconds for each step. The interplanar spacings, d, measured in Angstrom units (A), and the relative intensities of the lines, I/Io, where Io is one-hundredth of the intensity of the strongest line, including subtraction of the background, were derived with the use of the software "APD Peak Algorithm". The relative intensities are given in terms of the symbols vs = very strong, s = strong, m = medium and w = weak. It should be understood that this X-ray diffraction pattern is characteristic of all the species of zeolite compositions synthesized by the present invention. Ion exchange of the alkali metal cations with other ions results in a zeolite which reveals substantially the same X-ray diffraction pattern with some minor shifts in interplanar spacing and variation in relative intensity. Other minor variations can occur, depending on the silica to alumina plus iron oxide ratio and the iron to iron plus aluminum ratio of the particular sample, as well as its degree of thermal treatment. Aluminosilicate zeolite ZSMll prepared by the method of U.S. Patent 3,709,979 having a SiO2/A1203 molar ratio of 75, ammonium ion exchanged as above indicated and calcined 3 hours at 5380C exhibits an Alpha Value, hereafter defined, demonstrative of acid catalytic activity, of about 220. Based on the SiO2/A1203 ratio range exemplified for aluminosilicate zeolite ZSM-ll in U.S. Patent 3,709,979, one would expect Alpha Values of from about 170 to greater than about 620. The ferroaluminosilicate zeolite of ZSM-ll structure of the present invention will exhibit an Alpha Value, after said ion exchange and calcination, of less than about 200, usually from about 5 to about 150. Since certain chemical conversion processes are most effectively conducted over catalysts having known limited acid catalytic activity, the ferroaluminosilicate of the present invention will have enhanced utility therein. For example, vapor phase isomerization of xylenes is most effectively conducted over catalyst having an Alpha Value of from 150 to 190; whereas alkylation of benzene with ethylene over catalyst having an Alpha Value of from 40 to 80 is most effective. Also, for conversion of methanol to gasoline, a catalyst having an Alpha Value of from 60 to 100 is most useful. Therefore, a normally synthesized zeolite ZSMll with the structural composition defined in U.S. Patent 3,709,979 is, as known, useful for vapor phase xylene isomerization, whereas an acid strength-tailored ZSM-ll, synthesized hereby, will be more useful for alkylation of benzene and conversion of methanol to gasoline. It is important not to confuse acid activity with acid strength of a particular zeolite. The present invention relates to tailoring the acid strength of a synthetic crystalline molecular sieve material having the structure of zeolite ZSM-1l. Acid activity measured by Alpha Vaue can be altered downward by (1) steaming a higher Alpha zeolite, by (2) crystallization of the zeolite with a higher SiO2/A1203 mole ratio or by (3) crystallization of the zeolite as a metalloaluminosilicate, the metal other than aluminum taking the place of aluminum in the zeolite structure. Method (3) may provide a product zeolite having the same number of acid sites as the product zeolite of method (1), but their acid strength is lower. Alpha Value correlates with the number of acid sites only when the acid strength of those sites is constant. Conversely, Alpha Value should correlate with the acid strength only when the number of acid sites is constant. It is believed that the product acid-strength tailored zeolite hereof will provide a more selective catalyst than those made by steaming a higher Alpha Value zeolite. It is noted that the difference in zeolite acid site density is equivalent to the concentration of an aqueous acid solution, e.g. a solution of H2S04, which can be titrated. The difference in acid strength is equivalent to difference in pK values of aqueous acids, e.g. "strong" acids such as H2504, HN03 and HC1, "medium strong" acids such as H3P04, and "weak" acids such as H3B03, H2C03 and H4SiO4, which can be measured by the pH at which these acids are neutralized (titration curve), or, conversely, by the temperature at which the acid releases a volatile base, e.g. NH3, indicating the strength with which the acid holds the base, e.g. as NH4 Zeolite ZSM-ll exhibits an important characteristic of its crystal structure of constrained access to, and egress from, the intracrystalline free space by virtue of having a pore dimension greater than about 5 Angstroms and pore windows of about a size such as would be provided by 10-membered rings of oxygen atoms. It is to be understood, of course, that these rings are those formed by the regular disposition of the tetrahedra making up the anionic framework of the crystalline zeolite, the oxygen atoms themselves being bonded to the silicon or aluminum or iron atoms at the centers of the tetrahedra for the ferroaluminosilicate of the present invention. The crystalline ferroaluminosilicate produced hereby exhibiting this characteristic freely sorbs normal hexane, and has a Constraint Index of about 8 to 10. In general, the ferroaluminosilicate of the present invention can be prepared from a reaction mixture containing a source of cations, such as, for example,1brganic nitrogen-containing cations, an alkali or alkaline earth metal ion source, a source of silicon, such as, for example, a silicate, a deliberately added source of aluminum, such as, for example, an aluminate, water and a source of iron, such as, for example, an iron salt. The reaction mixture will have a composition, in terms of mole ratios of oxides, within the following ranges: Broad Preferred OH /SiO2 0.05-0.20 2 0.05-0.20 H20/OH 50-400 80-300 Si02/A1203 60-5000 100-3000 SiO2/Fe203 30-500 50-300 R'/R'+M 0.02-1.0 0.05-0.5 wherein R' represents organic cations and M represents alkali metal or alkaline earth metal ions. Reaction conditions consist of heating the foregoing reaction mixture to a temperature of from about 1000C to about 1600C for a period of time of from about 48 hours to about 100 days. A more preferred temperature range is from about 1200C to about 1400C with the amount of time at a temperature in such range being from about 100 hours to about 50 days. The digestion of the gel particles is carried out until crystals of the desired ferroaluminosilicate form. The crystalline product is recovered by separating same from the reaction medium, as by cooling the whole to room temperature, filtering and washing at conditions including a pH above 7. The above reaction mixture composition can be prepared utilizing materials which supply the appropriate oxides. Such compositions may include sodium silicate, silica hydrosol, silica gel, silicic acid, sodium hydroxide, a deliberately-added source of aluminum, a source of iron and an appropriate organic compound. The source of aluminum will generally be a deliberately-added aluminum-containing compound. Deliberately-added sources of aluminum are those which, in general, comprise significantly more aluminum than other essential reaction mixture components such as silica-containing compounds or alkali metal-containing compounds which may also contain aluminum as an impurity. The source of iron may be an iron salt such as, for example, ferric sulfate. The organic compounds act as directing agents and contain an element of Group VA, such as nitrogen or phosphorus. A quaternary compound such as tetrabutylammonium chloride or hydroxide, as well as one or more alkylenediamines having from 7 to 12 carbon atoms (See U.S. Patent 4,108,881) may be used to direct synthesis under appropriate conditions of the ferroaluminosilicate having the structure of ZSM-1l. Another way to direct synthesis of the present ferroaluminosilicate molecular sieve having the crystal structure of ZSM-ll is to provide seed crystals of ZSM-ll in the reaction mixture initially. This may be facilitated by providing at least about 0.01 percent, preferably at least about 0.1 percent and still more preferably at least about 1 percent seed crystals of the desired ferroaluminosilicate (based on total reaction mixture weight). While the present invention is not limited by any particular theory of operation, it should be noted that, depending on the ratio of Si/Al in the crystal framework, the influence of Si-O on the Al-O bond length may be larger or smaller. A shortening of the Al-O bond, as happens as the SiO2/A1203 ratio increases, results in a stronger acid, but the number of acid sites (H+-ion concentration) decreases. In a framework aluminosilicate, such as a zeolite ZSM-ll synthesized as in U.S. Patent 3,709,979, the acid strength of the proton associated with an A104- tetrahedron correlates with the Al-O bond length. The longer the bond, the weaker is the acid; the shorter the bond, the stronger is the acid. Since there is a certain narrow range of Al-O bond lengths within a structure, there is a corresponding range of acid strengths. Information on the relative acid strengths can be obtained by following the desorption of ammonia from an ammonium zeolite upon heating with a constant heating rate, e.g. 100C/minute. The desorbed ammonia is continually purged from the thermogravimetric unit with helium and absorbed from a gas stream in boric acid/NH4Cl, where it is continuously titrated with sulfamic acid using an automated titrator (G.T. Kerr and A.W. Chester, Thermochim. Acta., 1971, 3, 113). The rate at which the titrant is added is recorded as a function of the sample temperature. The temperature at which the rate of ammonia evolution reaches a maximum, the temperature-programmed ammonia desorption (TPAD) peak temperature, is a measure of the acid strength of the zeolite acid, since a weaker acid would release NH3 at a lower temperature, a stronger acid at a higher temperature. Whereas an aluminosilicate ZSM-ll of SiO2/A1203 molar ratio of 75 shows the TPAD peak at 3800C, a zeolite of ZSM-11 structure having a SiO2/(A1203+Fe203) molar ratio of 68 and a Fe/(Fe+Al) atomic ratio of 0.92 gives a TPAD peak at 3150C. The widths of the TPAD peaks at half-height for various zeolite samples were measured (see Example 8, hereinafter) and found to be 1400C for the aluminosilicate ZSMll, 1480C for the sample with Fe/(Al+Fe) = 0.92 and also 1480C for the sample containing Fe and Al in the ratio of about 1:1, ie. Fe/(Al+Fe) = 0.48. If the peaks obtained for the Fe-free sample (Example 7) and the material of Example 5, where Fe/(Fe+Al)=0.92, are added by conducting the TPAD test on a physical mixture of equal amounts of Example 5 and Example 7 product, a half-height width of 1750C is obtained. It is concluded from these results that the bond lengths of Fe-O and Awl4) are modified by their mutual influence in the crystal structure resulting in essentially one common acid strength intermediate of the pure Al- and pure Fe-silicates. The Alpha activity of the product of Example 2, hereinafter, is lower than would be expected from the Al content. This is also true for the product of Example 5, hereinafter. This unexpected result indicates that the acid strength of the aluminum sites themselves decreased by the presence of the iron in the zeolite structure. Therefore, the TPAD peak with temperature and half-height width and the Alpha activity indicate that mixed ferroaluminosilicates have acid strength intermediate to ferrosilicate and aluminosilicate, and the acid strength is modified by the mutual effect of the Al-O and Fe-O bonds on their length. This observation allows the conclusion that the acid sites of the presently synthesized acid strenth-tailored zeolite do not behave like hydrogen sites on aluminosilicate (stronger) or like hydrogen sites on ferrosilicates (weaker), but a new type of acid site is unexpectedly formed. The ferroaluminosilicate crystals prepared by the instant invention can be shaped into a wide variety of particle sizes. Generally speaking, the particles can be in the form of a powder, a granule, or a molded product, such as an extrudate having particle size sufficient to pass through a 2 mesh (Tyler) screen and be retained on a 400 mesh (Tyler) screen. In cases where the catalyst is molded, such as by extrusion, the crystals can be extruded before drying or partially dried and then extruded. It may be desired to incorporate the new ferroaluminosilicate crystal with another material, i.e. a matrix material, resistant to the temperatures and other conditions employed in various organic conversion processes. In this manner, catalyst compositions can be prepared. Such matrix materials include active and inactive material and synthetic or naturally occurring zeolites as well as inorganic materials such as clays, silica and/or metal oxides, e.g. alumina. The latter may be either naturally occurring or in the form of gelatinous precipitates or gels including mixtures of silica and metal oxides. Use of a material in conjunction with the new ferroaluminosilicate crystal, i.e. combined therewith, which is active, tends to alter the conversion and/or selectivity of the overall catalyst in certain organic conversion processes. Inactive materials suitably serve as diluents to control the amount of conversion in a given process so that products can be obtained economically and orderly without employing other means for controlling the rate of reaction. These materials may be incorporated into naturally occurring clays, e.g. bentonite and kaolin, to improve the crush strength of the catalyst under commercial operating conditions. Said materials, i.e. clays, oxides, etc., function as binders for the catalyst. It may be desirable to provide a catalyst having good crush strength because in commercial use it is desirable to prevent the catalyst from breaking down into powder-like materials. These clay binders have been employed normally only for the purpose of improving the crush strength of the overall catalyst. Naturally occurring clays which can be composited with the new crystal include the montmorillonite and kaolin family, which families include the subbentonites, and the kaolins commonly known as Dixie, McNamee, Georgia and Florida clays or others in which the main mineral constituent is halloysite, kaolinite, dickite, nacrite, or anauxite. Such clays can be used in the raw state as originally mined or initially subjected to calcination, acid treatment or chemical modification. Binders useful for compositing with the present crystal also include inorganic oxides, notably alumina. In addition to the foregoing materials, the crystalline ferroaluminosilicate can be composited with a porous matrix material such as silica-alumina, silica-magnesia, silica-zirconia, silica-thoria, silica-beryllia, silica-titania as well as ternary compositions such as silica-alumina-thoria, silica-alumina-zirconia silica-alumina-magnesia and silica-magnesia-zirconia. The relative proportions of finely divided crystalline molecular sieve material and inorganic oxide matrix vary widely, with the crystal content ranging from about 1 to about 90 percent by weight and more usually, particularly when the composite is prepared in the form of beads, in the range of about 2 to about 80 weight percent of the composite. Employing a catalytically active form of the novel ferroaluminosilicate material of this invention as a catalyst component, said catalyst possibly containing additional hydrogenation components, reforming stocks can be reformed employing a temperature of from about 3700C to about 5400C, a pressure of from about 100 psig (791 kPa) to about 1000 psig (6996 kPa), preferably from about 200 psig (1480 kPa) to about 700 psig (4928 kPa), a liquid hourly space velocity of from about about 0.1 to about 10, preferably from about 0.5 to about 4, and a hydrogen to hydrocarbon mole ratio of from about 1 to about 20, preferably from about 4 to about 12. A catalyst comprising the present ferroaluminosilicate molecular sieve can also be used for hydroisomerization of normal paraffins, when provided with a hydrogenation component, e.g. platinum. Such hydroisomerization is carried out at a temperature of from about 900C to about 3750C, preferably from about 1450C to about 2900C, with a liquid hourly space velocity of from about 0.01 to about 2, preferably from about 0.25 to about 0.50, and with a hydrogen to hydrocarbon mole ratio of from about 1:1 to about 5:1. Additionally, such a catalyst can be used for olefin or aromatic isomerization, employing a temperature of from about 2000C to about 4800C. Such a catalyst can also be used for reducing the pour point of gas oils. This reaction is carried out at a liquid hourly space velocity of from about 10 to about 30 and at a temperature of from about 4250C to about 5950C. Other reactions which can be accomplished employing a catalyst comprising the ferroaluminosilicate of this invention containing a metal, e.g. platinum, include hydrogenationdehydrogenation reactions and desulfurization reactions, olefin polymerization (oligomerization) and other organic compound conversions, such as the conversion of alcohols (e.g. methanol) or ethers (e.g. dimethylether) to hydrocarbons, and the alkylation of aromatics (e.g. benzene) in the presence of an alkylating agent (e.g. ethylene). In order to more fully illustrate the nature of the invention and the manner of practicing same, the following examples are presented. In the examples, whenever adsorption data are set forth for comparison of sorptive capacities for water, cyclohexane and n-hexane, they were determined as follows: A weighed sample of the calcined adsorbant was contacted with the desired pure adsorbate vapor in an adsorption chamber, evacuated to 1 mm and contacted with 12 mm Hg of water vapor or 20 mm Hg of n-hexane, or cyclohexane vapor, pressures less than the vapor-liquid equilibrium pressure of the respective adsorbate at room temperature. The pressure was kept constant (within about + 0.5 mm) by addition of adsorbate vapor controlled by a manostat during the adsorption period, which did not exceed about 8 hours. As adsorbate was adsorbed by the new ferroaluminosilicate material, the decrease in pressure caused the manostat to open a valve which admitted more adsorbate vapor to the chamber to restore the above control pressures. Sorption was complete when the pressure change was not sufficient to activate the manostat. The increase in weight was calculated as the adsorption capacity of the sample in 9/100 g of calcined adsorbant. When Alpha Value is examined, it is noted that the Alpha Value is an approximate indication of the catalytic cracking activity of the catalyst compared to a standard catalyst and it gives the relative rate constant (rate of normal hexane conversion per volume of catalyst per unit time). It is based on the activity of the highly active silica-alumina cracking catalyst taken as an Alpha of 1 (Rate Constant = 0.016 sec In the case of zeolite HZSM-5, only 174 ppm of tetrahedrally coordinated A1203 are required to provide an Alpha Value of 1. The Alpha Test is described in U.S. Patent 3,354,078 and in The Journal of Catalysis, Vol. IV, pp. 522-529 (August 1965). The zeolite tested in this Alpha Test must be in the hydrogen or hydronium form. This may be accomplished by calcination and contact of the zeolite with an ammonium salt or acid solution followed by calcination, or by calcination of the zeolite if it contains a hydrogen precursor by way of its synthesis. EXAMPLE 1 Two grams of aluminum sulfate, Awl2(504)3 14H20, and 1.9 grams of ferric sulfate, Fe2(S04)3 9H20, were dissolved in 50 grams of water. Concentrated sulfuric acid, 11.5 grams, was added, and the solution was cooled to ambient temperature. After adding a solution of 11.4 grams of tetrabutylammonium bromide in 17.2 grams of water, a mixture of 115.5 grams of sodium waterglass (8.9% Na2O, 28.7% SiO2) and 67.2 grams of water was added rapidly, with vigorous stirring. The reaction mixture was heated at 1200C for 37 days in a static, Teflon-lined autoclave. The product gave the X-ray diffraction pattern (Table 2, hereafter) and had 105% crystallinity compared to a reference sample containing no iron and prepared by the method of U.S. Patent 3,709,979. The chemical composition of the product ferroaluminosilicate, in weight %, was: SiO2 78.9 Al203 0.93 Fe203 1.43 Na20 1.62 N 0.54 Ash 82.9 SiO2/(A1203+Fe203), molar 73 Fe203/(A1203+Fe203), molar 0.50 The sorption capacities, in g/100 g of calcined product zeolite, were as follows: : Cyclohexane, 20 Torr 7.7 n-Hexane, 20 Torr 11.8 Water, 12 Torr 9.4 Table 2 Degrees Interplanar Relative Two Theta d-Spacing (A) Intensity, I/Io 5.65 15.64 6 7.87 11.24 20 8.72 10.15 14 11.76 7.52 2 13.10 6.76 2 14.63 6.05 4 15.78 5.62 4 17.13 5.18 2 17.58 5.05 3 19.11 4.64 4 20.22 4.39 9 23.00 3.87 100 23.79 3.74 49 25.03 3.56 7 25.42 3.50 8 25.85 3.45 13 26.94 3.31 10 28.25 3.16 9 29.05 3.07 9 29.75 3.00 15 31.10 2.875 3 31.80 2.814 2 34.16 2.625 4 35.92 2.500 6 37.17 2.419 4 38.13 2.360 2 38.80 2.321 1 40.26 2.240 1 41.38 2.182 1 42.72 2.117 1 43.38 2.086 2 44.96 2.016 17 45.99 1.974 4 47.15 1.927 3 48.36 1.882 5 49.89 1.828 3 51.23 1.783 2 53.04 1.727 1 54.79 1.676 7 58.89 1.568 1 Example 2 Ten grams of the zeolite product of Example 1 was calcined in a tube furnace in a nitrogen stream to <RTI ID=17.1> 200 C. Ammonia was added to the gas stream, and the temperature was gradually raised to 600 C, where it was held for 2 hours. After cooling the calcined material to room temperature in the N2/NH3 stream, it was exchanged three -times with 450 ml of a 0.1 N NH4Cl/1 N NH4OH solution for 2 hours each at ambient temperature with stirring. The exchanged solid was filtered, washed with 0.1 N NH40H and dried at room temperature. The chemical composition of the exchanged product was, in wt. %: SiO2 (by diff) 89.9 A1203 1.2 Fe203 1.71 Na 0.03 N 0.60 Ash 92.9 SiO2/(A1203+Fe203), molar 67 Fe203/(Al203+Fe203), molar 0.48 N/(Al+Fe), atomic 0.954 Na/(Al+Fe), atomic 0.029 (N+Na)/(Al+Fe), atomic 0.983 A sample of this material was sized 14-25 mesh, calcined for three hours at 5380C in air and tested in the Alpha Test for n-hexane cracking. The Alpha Value was found to be 50. When an aluminosilicate zeolite ZSM-l1 prepared by the method of U.S. Patent 3,709,979 (SiO2/A1203 mole ratio = 75) and exchanged by the method of this Example 2 (see Example 7) was tested in the Alpha Test, it proved to have an Alpha Value of 222. The zeolite ZSM-ll having an Alpha Value of 222 would have too much acid strength for efficient use in a process such as alkylation of benzene with an olefin (eg. ethylene). The ferroaluminosilicate of the present invention, i.e. the Example 2 product, having an Alpha Value of 50, is an ideal catalyst for such a process in comparison. Conversion is high, selectivity is observed and aging is favorably low for the Example 2 product compared to the ZSM-ll having an Alpha Value of 222. Example 3 Three grams of the ammonium exchanged product of Example 2 was exchanged three times with 135 ml of 0.1 N NaCl at 710C for one hour each. The product was filtered, washed chloride-free and dried at ambient temperature. The chemical composition of this sodium back-exchanged product, in wt%, was: SiO2 (by diff) 95.5 Awl203 1.2 Fe203 1.71 Na20 1.19 N 0.07 Ash 92.0 SiO/(A1203+Fe203), molar 65.2 Fe203/(A1203+Fe203), molar 0.476 N/(Al+Fe), atomic 0.855 Na/(Al+Fe), atomic 0.111 (Na+N)/(Al+Fe), atomic 0.966 The (Na+N)/(Al+Fe) atomic ratios after both the ammonium exchange and the sodium back-exchange being close to 1.0 prove that the iron contributes to the ion-exchange capacity of the zeolite. This offers proof that the Fe of the ferroaluminosilicate of the present invention is located in the zeolite framework. Example 4 A 3.8 gram quantity of ferric sulfate, Fe2(S04)3 9H20, was dissolved in 50 grams of water. Concentrated sulfuric acid, 11.5 grams, was slowly added with stirring. After cooling to ambient temperature, a solution of 22.8 grams of tetrabutylammonium bromide in 17.2 grams of water was added. Finally 115.5 grams of sodium silicate (8.9% Na20, 28.7% SiO2 and about 0.02% A1203), diluted with 67.2 grams of water, was added rapidly, with stirring. The reaction mixture was heated at 1400C in a Teflon-lined pressure vessel for 205 hours. The crystalline material was separated from the mother liquor by filtration, washed with water and dried at ambient temperature. It displayed the X-ray diffraction pattern listed in Table 3, and had 115% crystallinity compared to the reference sample of aluminosilicate ZSM-11. Table 3 Degrees Interplanar Relative Two Theta d-Spacing (A) Intensity, I/Io 5.61 15.77 1 7.83 11.29 21 8.66 10.21 14 11.73 7.54 2 13.03 6.80 2 13.69 6.47 1 14.57 6.08 3 15.72 5.64 3 17.53 5.06 2 19.06 4.66 3 20.17 4.40 8 22.94 3.88 100 23.73 3.75 46 25.37 3.51 5 26.50 3.36 6 27.85 3.20 1 29.01 3.08 8 29.70 3.01 14 31.02 2.884 2 31.87 2.808 1 34.12 2.628 2 34.89 2.572 1 35.49 2.530 3 35.83 2.506 6 37.17 2.417 3 37.29 2.415 3 40.11 2.248 1 41.26 2.188 1 42.63 2.121 1 43.31 2.089 2 44.92 2.018 17 45.88 1.978 3 47.03 1.932 3 48.30 1.884 5 49.21 1.852 1 51.21 1.784 2 53.53 1.712 1 54.68 1.679 7 56.29 1.635 1 56.79 1.621 1 58.72 1.572 1 The chemical composition of the product ferroaluminosilicate of this Example 4, in weight %, was: : Si02 79.1 Al203 0.16 Fe2O3 2.86 Na20 1.11 N 0.77 Ash 84.6 SiO2/(A1203 + Fe203), molar 68 Fe203/ (A1203 + Fe203), molar 0.92 The sorption capacities, in 9/lOO of calcined product zeolite, were as follows: Cyclohexane, 20 Torr 8.9 n-Hexane, 20 Torr 10.7 Water, 12 Torr 6.4 Example 5 A quantity of the zeolite product of Example 4 was calcined, exchanged, filtered and washed as in Example 2. The exchanged product contained 0.01 weight percent Na. A sample of this exchanged material was then calcined and tested in the Alpha Test as in Example 2. It exhibited an Alpha Value of 25. Example 6 For comparison purposes, zeolite ZSM-11 was prepared as taught in U.S. Patent 3,709,979. The product of this example was 110% crystalline ZSM-11 according to X-ray diffraction analysis: The chemical composition of the product of this example, in weight %, was: SiO2 74.8 Awl 203 1.7 Foe 203 0 Na20 1.19 N 0.52 Ash 80.6 SiO2/A1203, molar 75 SiO2/(A1203 + Fe203), molar 75 Fe/(Al + Fe), atomic O The sorption capacities, in g/lOOg of calcined product zeolite, were as follows: Cyclohexane, 20 Torr 8.0 n-Hexane, 20 Torr 11.6 Water, 12 Torr 4.2 Example 7 A quantity of the zeolite product of Example 6 was calcined, exchanged, filtered and washed as in Example 2. The exchanged product contained less than 0.01 weight percent Na. A sample of this exchanged material was then calcined and tested in the Alpha Test as in Example 2. It exhibited an Alpha Value of 222. Example 8 A temperature-programmed ammonia desorption (TPAD) test was conducted on product samples from Examples 2, 5 and 7 with the following results (Table 4) confirming the conclusion that a new type of acid site is unexpectedly formed by the present acid strength-tailoring method. The TPAD test was also conducted on a sample of a physical mixture of Example 7 and Example 5 zeolite product, indicating a half-height width of 1750C. Table 4 Example Product 5 & 2 5 7 mixture TPAD Peak, OC 335 315 380 340 Width at Half-Height, OC 148 148 140 175 Alpha Value Found 50 25 222 Alpha Value Expected 80 35 220 (from the SiO2/A1203 mole ratio) This evidence leads to the unexpected result that, at the conditions noted hereinbefore for TPAD testing, the acid strength-tailored zeolite of the present invention will exhibit a TPAD peak of less than about 3800C, and depending on the Fe/(Fe + Al) atomic ratio of the zeolite, a TPAD peak of from greater than about 3100C to less than about 3800C. Further, at the TPAD test conditions noted hereinbefore, the acid strength-tailored zeolite of the present invention will exhibit a TPAD half-height width of less than about 1550C, and depending on the Fe/(Fe + Al) atomic ratio of the zeolite, a TPAD half-height width of from greater than about 140 C to less than about 1550C.

Claims: CLAIMS: 1. A method for synthesizing a synthetic crystalline siliceous molecular sieve material containing both aluminum and iron in its anionic framework, which method comprises preparing a mixture containing a source of organic cations, a source of silicon, a deliberately-added source of aluminum, a source of iron, a source of alkali metal or alkaline earth metal ions and water, said mixture having a composition, in terms of mole ratios of oxides and ions, within the following ranges: : OH /SiO2 0.05 - 0.20 H2 0/OH 50-400 SiO2/A1203 60-5000 SiO2/Fe203 30-500 R'/R'+M 0.02 - 1.0 wherein R' represents organic cations and M represents alkali metal or alkaline earth metal ions; maintaining said mixture until crystalline siliceous molecular sieve material is formed at a temperature of from 1000C to 1600C for a time of from 48 hours to 100 days; and recovering from said mixture crystalline siliceous molecular sieve material which is characterized by an X-ray diffraction pattern substantially as shown in Table 1 of the specification, and by a composition on an anhydrous basis and in terms of moles of oxides per mole of silica expressed by the formula: (1 + 0.3)(a + b)R2/nO: a Fe203: b A1203: : SiO2 wherein R is at least one cation having the valence n and 0.002 < (a+b) < 0.1 a > 0.0016, and b > 0.0004, said molecular sieve material further exhibiting when in the ammonium form, a temperature-programmed ammonia desorption peak of from greater than 3100C to less than 3800C and a temperature-programmed ammonia desorption peak half-height width of from greater than 1400C to less than 1550C. 2. The method of Claim 1 wherein said mixture has a composition, in terms of mole ratios of oxides and ions, within the following ranges: OH /SiO2 0.08 2 0.08 - 0.17 H20/OH 80 - 300 SiO2/A1203 100 - 3000 SiO2/Fe203 50 - 300 R'/R'+M 0.05 - 0.5 and wherein the molar ratio of SiO2 to A1203 in the recovered crystalline molecular sieve material is less than 900. 3. The method of Claim 1 or Claim 2 which comprises the additional step of heating said recovered crystalline material at a temperature of from 3700C to 11000C. 4. The method of any of Claims 1 to 3 which comprises the additional step of replacing original cations of the recovered crystalline material, at least in part, with a cation or a mixture of cations selected from hydrogen and hydrogen precursors, rare earth metals, or metals of Groups IA, IIA, IIIA, IVA, IB, IIB, IIIB, IVB, VIB or VIII of the Periodic Table of the Elements. 5. The method of any of Claims 1 to 4 wherein the source of organic cations is a compound selected from tetrabutylammonium compounds, tetrabutylphosphonium compounds or alkylenediamines having from 7 to 12 carbon atoms. 6. The method of any of Claims 1 to 5 wherein the recovered crystalline molecular sieve material is characterized by an Alpha Value of less than 200 following its conversion to the hydrogen form. 7. A synthetic crystalline siliceous molecular sieve material containing both aluminum and iron in its anionic framework, said crystalline molecular sieve material being characterized by having an X-ray diffraction pattern substantially as shown in Table 1 of the specification, and by having a composition on an anhydrous basis and in terms of moles of oxides per mole of silica expressed by the formula: (1 + O.3)(a + b)R2/nO: a Fe203: b A1203: SiO2 wherein R is at least one cation having the valence n, and 0.002 < (a+b) < 0.1 a > 0.0016, and b > 0.0004; said molecular sieve material further exhibiting, when in the ammonium form, a temperature-programmed ammonia desorption peak of from greater than 3100C to less than 3800C and a temperature-programmed ammonia desorption peak half-height width of from greater than 1400C to less than 1550C. 8. The crystalline molecular sieve material of Claim 7 wherein the molar ratio of SiO2 to A1203 therein is less than 900. 9. The crystalline molecular sieve material of Claim 7 or Claim 8 wherein R is a cation or a mixture of cations selected from hydrogen and hydrogen precursors, rare earth metals, and metals of Groups IA, IIA, IIIA, IVA, IB, IIB, IIIB, IVB, VIB and VIII of the Periodic Table of the Elements. 10. A catalyst composition comprising A) from 1 percent to 90 percent by weight of a crystalline molecular sieve material prepared in accordance with the method of any of Claims 1 to 6; and B) from 10 percent to 99 percent by weight of an inorganic oxide matrix material. 11. Use of crystalline molecular sieve material prepared in accordance with the method of any of Claims 1 to 6 as a catalyst for the conversion of organic compounds.

Inventors: KUEHL, GUENTER HINRICH
Applicants: MOBIL OIL CORPORATION
Application year: 1984
Main classification: C01B33
IPC codes: C01B39, B01J29