PROCESS FOR THE CONTINUOUS MANUFACTURE OF A LUBRICATING GREASE

Abstract: A process for the continuous manufacture of a lubricat­ ing grease comprising blending feed materials and lubricat­ ing oil and pumping the resulting blend through at least one motionless mixer which is heated to such a temperature that soap formation takes place and a resultant grease is formed.

Description: PROCESS FOR THE CONTINUOUS MANUFACTURE OF A LUBRICATING GREASE This invention relates to a process for the continuous manufacture of a lubricating grease and in particular of a base grease which serves as a basis for the manufacture of a wide variety of lubricating grease formulations containing one or more additives. By first making a base grease a great flexibility is obtained in making a great variety of grease formulations using the same grease manufacturing basic unit. From European patent application 0072184 a process for the continuous manufacture of a lubricating grease, which process shows a great flexibility, is already known. According to this process a rotating screw process unit is used. It has now been found that such processes, which enable the manufacture of a great variety of greases, such as the greases described in said European patent application, can be carried out in a simpler way without the use of moving parts, namely by using motionless mixers, which are readily commercially available. Therefore the present invention relates to a process for the continuous manufacture of a lubricating grease comprising blending feed materials and lubricating oil and pumping the resulting blend thrcugh at least one motionless mixer which is heated to such a temperature that soap formation takes place and a resultant grease is formed. Suitable feed materials are the usual thickening or gelling agents which in the case of soaps are often made in situ in at least part of the lubricating oil from saponifiable material, saponification agents and optionally complexing agents. Suitable saponifiable materials are long chain fatty esters, especially glycerides, in particular where the fatty group contains a hydroxy radical, sudi as ricinoleyl (castor oil) or hydrogenated ricinoleyl (hydrogenated castor oil). Another method of soap formation is to neutralize fatty acids or hydroxy fatty acids in mineral oil with alkali metal or alkaline earth metal hydroxides (or mixtures of both) or hydrates thereof in particular lithium hydroxide monohydrate (LiOH.H2O). Alternatively hydrognated fatty acids or hydrogenated hydroxy fatty acids are commonly used in the neutralization. Suitable saponification agents are alkali metal or alkaline earth metal hydroxides (or mixtures of both), in particular lithium hydroxide, or hydrates thereof. Therefore, the feed materials preferably comprise a) hydrogenated castor oil (HCO) and lithium hydroxide or lithium hydroxide monohydrate; b) HCO and lithium hydroxide (or monohydrate) or calcium hydroxide; c) Hydrogenated castor oil fatty acid (HCOFA) and lithium d) HCOFA and lithium hydroxide (or monohydrate) or calcium hydroxide. Suitable complexing agents are short chain fatty acids, such as acetic acid, dicarboxylic acids, such as azelaic acid, hydroxy aromatic acids such as salicylic acid, boric acid, aluminium compounds, etc. If such catplening agents are used the proportion of saponification agents is usually increased with about the stoichiometric quantity of the complexing agent. Other suitable thickening agents are clays, including coated clays, silica gels, polymers, polyureas, carbon black, dyes, etc. Suitable lubricating oils are mineral oils, including hydro, genated mineral oils, synthetic oils, such as ester oils, polyolefin oils, silicon oils, ate esters, polyphenyl ethers, etc. Suitable mineral lubricating oils include HVI, paraffinic MVI, naphthnnic MVI and LVI oils. To the base greases may be added additional lubricating oil and additives, such as antioxidants, anti-rust, anti-wear and extreme pressure agents, pour point depressants, metal deactivators etc. Suitable laboratory-type motionless or static mixers have the form of a cylinder or tube having a length of 65.5 to 66.5 cm and a dieeeter of 3.3 to 3.6 cm. They are provided with an insulated heating jacket, using e.g. electric tape having a heating capacity of e.g. 400 watt per mixer, or a heating medium as the heating source. The inside of the cylinder is provided with e.g. vanes, corrugated plates, perforated plates, intermeshing and intersecting bars and similar fixed mechanical obstacles causing mixing and heat exchange. A suitable motionless mixer containing perforated plates is described in e.g. British patent specification 2086249, but other types may be used as well. Suitable mixers are: the Sulzer motionless mixer SMX type which is 655 mm long x 36 mm internal diameter and the Sulzer motionless heat exchanger SMXL type which is 665 mm long x 32.8 mm internal diameter. For commercial production the sizes of the mixers require scaling up. According to the present process the base grease-making ingredients are preferably blended at rocm temperature in a container from which they are pumped through at least one motion less mixer, preferably several motionless mixers, preferably longitudinally connected. They may also be, or additionally be, connected in a parallel manner. The average velocity of the mixture in the mixers may be 3 kg to 50 kg/h, preferably 7 to 30 kg/h, the flaw preferably being laminar The pressure at the entrance of the first mixer may be between 1 and 30 bar, preferably between 1 and 15 bar. The mixers are heated to a suitable high temperature, e.g. at least 120 OC, preferably between 120 and 250 DC, preferably up to a inaxinum temperature between 180 and 230 OC, so that a grease structure is formed on cooling. Preferably the temperature of each of the heated mixers is higher than that of the preceding mixer and so on. Thermocouples may be placed between the mixers for tempera- ture control. If desired part of the finished grease may be recycled. Also the pump at the entrance of the first mixer may be provided with a recycling circuit. The subsequent removal of water can be accomplished by simply dumping the resulting grease in an cpen vessel, whereafter any further lubricating oil and any desired additives can be added. Due to condensation some water may be present in the open vessel. If required complete debydration may be accomplished using conventional flash vacuum equipment. Preferably the base grease together with additional lubri- cating oil and additives is pumped through a heat exchanger tube for mixing and cooling to obtain the desired consistency. Homogenisation of the grease, if necessary, is carried out using e.g. z Manton Gaulin homogeniser at 300 psig (20.7 MPa), a mill or a rolling device etc. The inenticn is illustrated by the following Examples. EXAMPLE 1 1.3 kg feed containing: 12 %w hydrogenated castor oil 1.7 %w LiOH.H2O 86.3 %w mineral lubricating oil (HVI, viscosity 10.7-11.8 cSt at 100 OC, VI = 96 (min), and 3 %w (= 39 g) water is mixed at room terrerature for at least 10 minutes in a container and then pumped at a flow rate of 8.3 kg/h once through a series of 4 Sulzer motionaless mixers (each unit containing 2 mixing elements) which are beforehand adjusted to temperatures of 130, 170, 190 and 230 C, respectively, by 4 200 watt electric heaters per mixer. The e finished grease is obtained at the cutlet and cooled in a jacketed SULZER MONOTUBE HEAT EXCHANGER which consists of 2 units each 1540 mm long x 32.8 mm internal diameter. Each unit contains 1 5MXL type heat exchanger. The unworked/worked penetration at 25 OC was 262/273 dmm CASIM D217-82) (1 dmm corresponds with 0.1 mm) and the dropping point was 197 OC. (Worked penetration is the penetration at 25 OC after 60 double strokes in a standard grease worker). The first two Sulzer mixers were of the type SMX DN32, having a length of 655 mm and an internal diameter of 36 nrn and the last two were of the type SMXL DN32 (heat exchanger type for boosting the heat transfer during warming up of the viscous mixture), having a length of 665 mm and an internal diameter of 32.8 mm. Subsequently the water present in the grease was flashed off. Examples 2-6 are carried out in the arrangement of Example 1, but the flow rate is changed, resulting in different outlet temperatures, penetrations and dropping points (see Table A). TABLE A Example Outlet temperature flow rate Penetration (ASTM D217-82) Dropping point, of base grease, C kg/h unmilled milled C unworked/worked unworked/worked dmm dmm 1 218 8.3 277/287 262/273 * 197 2 204 7.4 216/313 302/319 83 3 203 8.2 246/338 319/330 194 4 205 8.9 285/334 323/330 194 5 213 9.2 359/327 289/291 * 202 6 225 8.8 334/357 332/332 198 * The worked penetration of both these greases conform to a National Lubricating Grease Institute (NLGI) 2 number i.e. 265-295. The other greases 2, 3, 4 & 6 are NLGI 1 number i.e. 310-340 (Softer greases than 2 grade) This table indicates that a better yield is obtained at outlet temperatures of around 213-218 C, see especially Example 1.

Claims: CLAIMS 1. A process for the continuous manufacture of a lubricating grease comprising blending feed materials and lubricating oil and purping the resulting blend through at least one motionless mixer which is heated to such a temperature that soap formation takes place and a resultant grease is formed. 2. A process according to claim 1, wherein the blending of feed materials and lubricating oil is carried out at roan temperature. 3. A process according to claim 1 or 2, wherein the feed materials comprise a) hydrogenated castor oil (HCO) and lithium hydroxide or lithium hydroxide chrdrate; b) HCO and lithium hydroxide (or manchydrate) or calcium hydroxide; c) }ydrogenated castor oil fatty acid (HCOFA) and lithium hydroxide or lithium hddrcxide zrnohydrate; and/or d) HCOFA and lithium hydroxide (or monohydrate) or calcium hydroxide. 4. A process according to any one of claims 1-3, wherein a series of heated motionless mixers is used, each mixer haring a higher temperature than the preceding one. 5. A process according to any one of claims 1-4, wherein the motionless mixers have vanes. 6. A process according to any one of claims 1-5, wherein the mixers are heated to a temperature beteeen 120 and 250 OC. 7. A process according to any one of claims 1-6, wherein the resulting grease is cooled in a heat exchanger tube. 8. A process according to any one of claims 1-7, wherein to the resulting grease additional lubricating oil and additives are added. 9. A process according to claim 1, substantially as hereinbefore described. 10. A lubricating grease whenever prepared, according to a process as claimed in any one of claims 1-9.

Inventors: COLECLOUGH, NORMAN, MACPHAIL, ALEXANDER COLQUHOUN BARR, ROBERTS, KENNETH EDWARD
Applicants: SHELL INTERNATIONALE RESEARCH MAATSCHAPPIJ B.V.
Application year: 1984
Main classification: C10M117
IPC codes: C10N50, C10M117, C10M177, C10N70