ZIRCONIA-TITANIA-SILICA TERGELS AND THEIR USE AS CATALYST SUPPORTS

Abstract: A method of preparing a high pore volume, high surface area zirconia-titania-silica tergel useful as an olefin polymer­ ization or copolymerization catalyst support comprises the steps of coprecipitating hydrous zirconia, hydrous titania and hydrous silica, aging and washing the resulting hydrotergel, removing water from the washed hydrotergel and optionally calcining the resulting xerotergel. Resins with predetermined properties such as high melt index, broad molecular weight distribution, high weight swell, etc. can be produced from catalysts of the chromium or Ziegler type based on these supports.

Description: ZIRCONIA-TITANIA-SILICA TERGELS AND THEIR USE AS CATALYST SUPPORTS BACKGROUND OF THE INVENTION Field of the Invention This invention relates generally to the field of catalyst supports and, more particularly, this invention relates to zirconia-titania-silica tergels useful as supports for olefin polymerization catalysts. Description of the Prior Art The use of xerogels as catalyst supports is well known. Low pore volume, high surface area ceramictype supports, while suitable for use in hydrocarbon cracking catalysts, are unsuitable for use in olefin polymerization catalysts, as the activities of such catalysts are very low. One form of xerogel which is useful as a polymerization catalyst support is the medium pore volume silica xerogel. Often, the silica xerogel is a twocomponent gel comprising zirconia or titania incorporated (in minor proportion) in silica. One type of silica-zirconia xerogel is produced by depositing zirconia on a silica gel. The deposition of zirconia on a silica gel does not provide a support which, when used in a catalyst, produces polyethylene resins with high melt indexes. Dombro et al U.S. Pat. No. 4,246,137, the disclosure of which is hereby incorporated by reference, describes a method of preparing high pore volume zirconia-silica catalyst supports by coprecipitation, washing and water removal. Tergels may also be used as polymerization catalyst supports. Hogan et al U.S. Pat. No. 2,825,721 describes a variety of tergels and their use as polymerization catalyst supports. It is desirable to produce polyolefin resins which have predetermined properties such as high melt index, broad molecular weight distribution, high weight swell, etc., and attempts have been made to produce such resins using catalysts supported on cogels. For example, Hwang et al U.S. Pat. No. 4,128,500 describes a supported chromium (III) acetylacetonate type catalyst. However, prior catalysts supported on cogels and tergels have not been completely successful in providing control of product polymer characteristics. SUMMARY OF THE INVENTION It is an object of the present invention to overcome one or more of the problems described above. In accordance with the invention, a high pore volume, high surface area zirconia-titania-silica tergel useful as a catalyst support for an olefin polymerization and copolymerization catalyst is provided. The invention contemplates, without limitation, the method of making the tergel, the tergel itself, catalyst supports and catalysts based upon the tergel, and a method of polymerizing using the catalysts. More specifically, the present invention contemplates a reaction wherein hydrous zirconia, hydrous titania, and hydrous silica are coprecipitated in aqueous solution. Alkali metal or ammonium salts of zirconium oxalate and titanium oxalate are used as the source of zirconia and titania, respectively. Coprecipitation with silica is acid promoted, and the source of silica is preferably an alkali metal silicate. Such coprecipitation results in intimate and well-distributed incorporation of zirconia and titania in silica. The hydrotergel so produced is then aged and washed to produce a high pore volume hydrotergel. Water removal from the washed hydrotergel is accomplished by any of a variety of methods, such as those disclosed in Dombro et al U.S. Pat. No. 4,247,137 and Dombro U.S. Pat. No. 4,279,780, the disclosures of which are incorporated herein by reference, or by spray-drying or other suitable techniques. The resulting xerotergel can be used as is or may be calcined prior to use as an olefin polymerization catalyst support. Zirconium oxalate compounds, when coprecipitated in a hydrogel, provide advantages as catalyst supports for polymerization, as the zirconium preserves the pore structure of the calcined xerogel and results in product resins with relatively high melt indexes (i.e. relatively low molecular weights). The xerotergel of the invention has a high pore volume, generally in the range of about 1.5 to 3.5 cc/g (N2-BET) and a high surface area (e.g. about 200 to about 2 600 m /g). The actual physical properties obtained are determined in part by the method used to remove water from the hydrotergel. The concentration of zirconia (ZrO2) and of titania (TiO2) with respect to silica may be equal or different and are generally in the range of about 0.1 wt% to about 67.5 wt%, but are preferably between about 0.2 and 5 wt% of each metal oxide. Further objects and advantages of the invention will be apparent to those skilled in the art from the following detailed description taken in conjunction with the appended claims. DETAILED DESCRIPTION OF THE INVENTION The present invention contemplates the preparation of high pore volume, high surface area zirconia-titania-silica tergels by acid promoted coprecipitation of zirconia and titania with silica, preferably in minor proportion to silica. As a result, zirconia and titania are well distributed and integrated into the bulk of silica. As detailed below, the use of an alkali metal or ammonium salt of zirconium oxalate (e.g., ammonium tetraoxalatozirconate (IV) pentahydrate) and titanium oxalate (e.g., ammonium bis(oxalato)oxotitanate (IV) monohydrate) as the source of zirconia and titania, respectively, during their acid-promoted coprecipitation with silica from an alkali metal silicate leads to the intimate and well distributed incorporation of zirconia and titania, preferably in minor proportion, into silica. Coupled with special water removal techniques, also detailed below, as well as other suitable water removal methods, the procedure provides novel porous xerotergel catalyst supports having high pore volume and high surface area. Hydrotergel Preparation Preparation of high pore volume zirconiatitania-silica tergels is effected by the coprecipitation of hydrous zirconia, hydrous titania, and hydrous silica. A zirconium compound of the type: M4Zr (C2O4)4.nH2O and a titanium compound of the type: M2TiO(C2O4)2.nH2O where M is an alkali metal or ammonium ion and n equals 0 to 10, are reacted with a silicon compound of the type: A2SiO3 where A is an alkali metal ion, in aqueous solution, preferably at a pH of less than about 9. It is desirable that the zirconium compound, the titanium compound and the alkali metal silicate be together in solution prior to precipitation. The zirconium compound may be added to the aqueous silicate solution before, after or together with the titanium compound. The pH of this solution determines whether premature precipitation takes place. Where ammonium salts of titanium oxalate and zirconium oxalate are used, it has been found that the pH of the solution must be equal to or greater than about 11 so as to avoid premature precipitation. The minimum required pH level may vary to some degree if other titanium or zirconium salts are used, but the minimum pH is readily empirically determinable in any case. The coprecipitation reaction is acid-promoted. Therefore, the reaction may be initiated by addition to the solution of an acidic material (e.g. a mineral acid) to lower the solution's pH, preferably to less than about 9. Preferred acidic materials include sulfuric acid, hydrochloric acid and ammonium sulfate. The resulting coprecipitated hydrotergel (in aqueous suspension) is then aged, preferably at a temperature between about ambient and 1000C, for at least one hour at a maintained pH of less than about 9, preferably at a pH of about 6. The aged hydrotergel is then separated from the bulk of the water and washed to remove soluble alkali metal and ammonium salt by-products. Preferably, the aged hydrotergel is first washed with water, then with aqueous ammonium nitrate and again with water. However, it may be washed with water alone, or with any other aqueous liquid in which the by-products are soluble. The alkali metal and ammonium concentration in the final wash liquid should be less than or equal to about 20 parts per million. After washing, a hydrotergel cake remains which contains about 90% water. Water Removal Water is removed from the washed hydrotergel cake to produce the high pore volume xerotergel of the invention. Water removal can be accomplished by any of a variety of methods. For example, water may be removed by azeotropic distillation with a compound capable of forming an azeotrope with water, such as ethyl acetate. In a second method, water is extracted from the hydrotergel with a water-miscible solvent or mixture of solvents, such as a low molecular weight ketone or a mixture of a ketone and a low molecular weight alcohol. A third method entails extracting the hydrotergel with a water-miscible solvent or mixture of solvents to remove about 90-958 of the water and then treating the partially dehydrated tergel with a ketal of the formula, RC(OR)2R, in which R is the same or different and is an alkyl group of 1-5 carbon atoms, plus a trace of acid, whereby residual water is completely and irreversibly removed by a chemical reaction. In a fourth method water is removed by contacting the hydrotergel directly with sufficient ketal in the presence of a trace of acid as catalyst. Finally, water can be removed from the washed hydrotergel by spray-drying, or by any other suitable method. The xerotergel is thus freed of absorbed organic compounds. It can then be used as is or may be calcined, preferably at temperatures in the range of 400-18500F, prior to use as an olefin polymerization catalyst support, or for any other desired purpose. For example, the tergel may be used to immobilize enzymes for use in chemical and food production processes. Catalyst Supports Ziegler and chromium type olefin polymerization catalysts are among those which may be supported on the tergels of the invention. Selection of components depends on what resin properties are desired. Generally, catalysts are made by depositing a catalytically active material, such as a transition metal or chromium compound, on the tergel support, as by means well known in the art, for example. As an example, a chromium (III) or chromium (VI) compound may be used as the active polymerization ingredient. The chromium compound may be dry blended with or impregnated as a solution onto the xerotergel in a non-aqueous solvent, followed by removal of the solvent. Activation takes place by heating in a fluid bed with dry gases such as air, nitrogen followed by air, nitrogen then air followed by carbon monoxide, etc. Activation temperatures up to 17500F are preferred. Chromium (III) acetylacetonate is a preferred chromium source since water is not reintroduced when it is dry blended with the xerotergel prior to thermal activation to produce the catalyst. The following Examples will serve to illustrate the practice of the invention, but unnecessary limitations should not be inferred therefrom. EXAMPLES Tergel Preparation Example A (Invention) A solution of 7.6g ammonium tetraoxalatozirconate (IV) pentahydrate in 200 cc of deionized water (pH 4.3) was added with agitation to a solution of 400g sodium silicate (6.75 wt% Na2O, 25.3 wt% SiO2; wt. ratio SiO2/Na2O=3.75) in 800 cc of deionized water (pH 11.3) over a period of ten minutes. Ammonia was liberated. To this solution, initially at pH of 11.2, was added a solution of 7g ammonium bis(oxalato)oxotitanate (IV) monohydrate in 200 cc deionized water over a period of twenty minutes. The final pH was 11.1. Coprecipitation occurred when a solution of 12 wt% sulfuric acid was added until a final pH of 6 was reached. The coprecipitated hydrotergel was aged for six hours at about 90"C while the pH was maintained at 6 with additional 12 wt.E sulfuric acid. Following aging, the hydrotergel was collected by filtration and washed first with deionized water, then with a 1 aqueous solution of ammonium nitrate, and finally with deionized water until the sodium ion concentration was about 20 ppm in the final wash. Bulk water was removed by suction filtration to give a hydrotergel cake containing about 90 wt.% water. A portion of the hydrotergel cake was dehydrated by azeotropic distillation with ethyl acetate to give a xerotergel containing 1.1 wt.% zirconia, 1.0 wt.E titania and about 97.9 wt.t silica. The xerotergel had a bulk density of 0.13 g/cc, an N pore volume of 2.49 cc/g and a surface area of 484 m /g. Example B (Invention) A 375g portion of the hydrotergel cake of Example A was dehydrated by mixing with 1200 cc of acetone, allowing the hydrotergel to settle by gravity and decanting the clear upper acetone-water layer. This cycle was repeated four more times with 600 cc of fresh acetone added each time following by removal of about 600 cc of the clear upper acetone-water layer. The acetone-hydrotergel slurry containing about 10 wt.% residual water was collected by suction filtration and then mixed with 220 cc of 2,2-dimethoxypropane plus 1 cc of 10% hydrochloric acid. After thorough mixing all volatiles were removed with mild heat under a N2 atmosphere. Final drying of the xerotergel was at 2000C. The xerotergel had a bulk density of 0.22 g/cc, an pore volume of 2.00 cc/g and a surface area of 431 m ig. Example C (Invention) A 375g portion of the hydrotergel cake of Example A was dehydrated by mixing with sufficient acetone to form 1200 cc of slurry. After efficient agitation the slurry was allowed to settle by gravity. The clear upper acetone-water layer was separated by decantation. This process was repeated four more times. The acetone-hydrotergel slurry containing about 0.6 moles of residual water was treated with 220 cc (1.8 moles) of 2,2-dimethoxypropane plus 1 cc of 10% HC1. All organic compounds were then removed under N2 and mild heat. The remaining xerotergel had a bulk density of 0.24g/cc. Example D (Invention} A solution of 7.5 g ammonium tetraoxalatozirconate (IV) pentahydrate in 200 cc of deionized water (pH 4.3) was added with agitation to a solution of 400g sodium silicate in 800 cc of deionized water (pH 11.6) over a period of twenty minutes. Ammonia was liberated. To this solution, initially at a pH of 11.5, was added a solution of 7.5g potassium bis(oxalato)oxotitanate (IV) dihydrate in 200 cc of deionized water over a period of twenty-five minutes. The final pH was 10.8. Coprecipitation occurred in about one hour when a solution of 12 wt.e sulfuric acid was added to a final pH of 6. The coprecipitated hydrotergel was aged for two hours at about 80"C while the pH was maintained at 6 with additional 128 sulfuric acid. Following aging, the hydrotergel was collected and washed as described in Example A. A portion of the hydrotergel cake was dehydrated by azeotropic distillation with ethyl acetate to give a xerotergel containing 1.4 wt.% zirconia, 1.1 wt.% titania and about 97.5 wt.% silica. The xerotergel had a bulk density of 0.13 g/cc, an uni pore volume of 2.41 cc/g and a surface area of 475 m /g. Example E (Comparative) A cogel containing zirconia with silica was prepared as described in U.S. Pat. No. 4,246,137, Example No. 8. The xerocogel contained 2.7 wt.% ZrO2 and had an N2 pore volume of 2.45 cc/g. Example F (Comparative) This porous support was a commercial high pore volume silica with an N2 pore volume of 2.05 cc/g and a 2 surface area of 285 m ig. Catalyst Preparation and Testing Olefin polymerization catalysts based on the tergels of Examples A to D, the cogel of Example E, and the high pore volume commercial silica of Example F were prepared by dry mixing chromium (III) acetylacetonate with the calcined xerotergels, the cogel (10000F) and the silica. The tergel and cogel supported catalysts were activated in a fluidized bed with dry N2 at 17000F followed by a 30 minute dry air treatment at 13000F. The silica supported catalyst was activated at 16000F in a fluid bed with dry air. The concentration of chromium in the activated catalysts was about 1 wt.%. Polymerization was conducted in a one gallon autoclave with isobutane as diluent, under 550 psi pressure at 2250F and with ethylene fed on demand. The data in the Table below show that the molecular weight distribution of polyethylene resin produced by chromium catalysts supported on the zirconia-titania-silica tergels of Examples A-D is much broader than resin produced from similar catalysts supported on a zirconia-silica cogel or on a high pore volume silica. This is expressed by higher RD values which measure resin dispersity (polymerization Examples Nos. 1-4 versus Examples Nos. 5 and 6). Together with broad molecular weight distribution these resins also have high melt index (MI) and weight swell (Sw) (Examples 2 and 3). Such resins produced by catalysts supported on the tergels of this invention find wide application. Catalyst and Resin Evaluation Polymerization Catalyst Catalyst Rda b MIc Example No. Support Productivity d w Example No. (g/g Catalyst) 1 A 2173 8.0 4.6 0.9 2 B 3893 7.7 4.8 2.4 3 C 4079 7.2 4.8 2.0 4 D 1329 6.6 4.4 0.3 5 E 1600 4.0 4.9 3.4 6 F 5200 5.0 5.1 0.8 a) Shida, M. and Cancio, L., "Polymer Engineering and Science", Vol. II, p. 124-128, March, 1971. b) Cancio, L. and Joyner, R., "Modern Plastics", Jan., 1977. c) ASTM D-1238-62T Condition E, g/10 minutes. Milled and stabilized. The foregoing detailed description is given for clearness of understanding only, and no unnecessary limitations should be inferred therefrom, as variations within the scope of the invention will be obvious to those skilled in the art. WE CLAIM: 1. A method of preparing zirconia-titaniasilica tergels comprising the steps of: a) mixing a zirconium compound of the formula M4Zr(C2O4)4 .nH2O and a titanium compound of the formula M2TiO (C2O4)2. nH2O, where M is an alkali metal or ammonium ion and n equals 0 to 10, with a silicon compound of the formula A2S iO3, where A is an alkali metal ion, in an aqueous solution at a pH sufficiently high to avoid precipitation of a tergel; b) adding an acidic material to said solution to lower the pH thereof sufficiently to result in precipitation of a hydrotergel; c) aging said hydrotergel of b); d) washing said aged hydrotergel of c) with an aqueous liquid; and e) removing water from the washed hydrotergel of d) to produce a xerotergel. 2. The method of claim 1 wherein M is an alkali metal ion. 3. The method of claim 1 wherein M is an ammonium ion. 4. The method of claim 3 wherein said solution pH of step a) is at least about 11. 5. The method of claim 4 wherein said acidic material of step b) is added in an amount sufficient to lower said pH to less than about 9.

Claims: 6. The method of claim 1 wherein said acidic material is sulfuric acid, hydrochloric acid or ammonium sulfate. 7. The method of claim 1 wherein said aging is done at a temperature between about ambient to 1000C for at least one hour. 8. The method of claim 1 wherein said water is removed from the washed hydrotergel by azeotropic distillation with a compound capable of forming an azeotrope with water. 9. The method of claim 1 wherein said water is removed from the washed hydrotergel by washing the hydrotergel with a water miscible solvent or mixture of solvents. 10. The method of claim 9 wherein said solvent is a low molecular weight ketone or a mixture of a ketone and a low molecular weight alcohol. 11. The method of claim 1 wherein said water is removed from the washed hydrotergel by extracting the hydrotergel with a water miscible solvent or mixture of solvents to remove about 90-95t of the water and then treating the partially dehydrated tergel with a ketal of the formula RC(OR)2R, in which R is the same or different and is an alkyl group of 1-5 carbon atoms, plus a trace of acid, whereby residue water is completely and irreversibly removed. 12. The method of claim 1 wherein said water is removed from the washed hydrotergel by spray-drying. 13. The method of claim 1 comprising the additional step of calcining said xerotergel of e). 14. The method of claim 13 wherein said calcining is done at a temperature of about 400-18500F. 15. A zirconia-titania-silica tergel prepared by the method of any of claims 1-14. 16. An olefin polymerization or copolymerization catalyst prepared by the method of any of claims 1-12, including the further steps of: f) calcining said xerotergel of e); g) introducing a catalytically active compound onto said calcined xerotergel of f); and, h) activating to produce an active polymerization or copolymerication catalyst. 17. The catalyst of claim 16 wherein said calcining step f) is done at a temperature of about 4000-18500F. 18. The catalyst of claim 16 wherein said active compound of g) is a chromium compound 19. The catalyst of claim 16 wherein said active compound of g) is a transition metal compound. 20 The method of polymerizing or copolymerizing olefins comprising contacting said olefins under polymerizing conditions with the catalyst of any of claims 16-19.

Inventors: DOMBRO, ROBERT ALEXANDER, KIRCH, WILLIAM
Applicants: QUANTUM CHEMICAL CORPORATION (A VIRGINIA CORP.)
Application year: 1984
Main classification: C01B33
IPC codes: C08F4, C01B33, C08F10, B01J21