AN ELECTRICALLY PROGRAMMABLE MEMORY DEVICE AND A METHOD FOR MAKING THE SAME

Abstract: In the present invention, asperity in the floating gate of an EPROM or EEPROM device is reduced. An improved process for fabricating ultrahigh coupling interpoly isolation dielectrics comprising a structure of oxide-nitride-oxide is disclosed. The first oxide is grown on undoped LPCVD polycrystalline silicon (polysilicon) to reduce the grain boundary-oxidation enhancement effect at the interface of floating gate polysilicon and interpoly oxide, This results in much higher breakdown capability of interpoly dielectrics. As a consequence, the shrinkage of the interpoly electrical thickness to an extent far beyond current limitation becomes possible. Implanted dopants through interpoly oxide into the floating gate polysilicon also eliminate the oxidation en­ hanced diffusion from conventional POCl₃ doped polysilicon into tunnel oxide. The phosphorus induced trap in the tunnel oxide region are reduced. The EEPROM threshold window can remain open beyond 10⁶ cycles.

Description: Description An Electrically Programmable Memory Device And A Method For Making The Same Background Of The Invention The present invention relates to an electrically programmable device and a method for making the same. The electrically programmable memory device can be of the type that is commonly called Electrically Programmable Read-Only Memory (EPROM) or Electrically Erasable Programmable Read-Only Memory (EEPROM). More particularly, the present invention relates to the manufacture of ultra high coupling interpoly dielectrics suitable for programming EEPROM and EPROM devices at faster speeds and lower voltages than heretofore achieved. A higher interpoly dielectric breakdown capability and higher interpoly capacitance is required for VLSI technology due to the preferred smaller die size in high circuit density package. The invention involves the development of thinner and stronger interpoly dielectrics. EPROM or EEPROM and methods for making the same are well known in the art. In general, an EPROM or an EEPROM is characterized by a "floating gate" and a electrical connection termed "control gate", both of which are fabricated out of polycrystalline silicon doped with an appropriate doping material to render the polycrystalline conductive. A typical doping material is phosphorus. The floating gate and the control gate are separated by a layer of insulating material, typically silicon dioxide (SiO2). The principle upon which the EPROM or EEPROM device operates is that charges are stored on the "floating gate" in a capacitive manner. Thus, the dielectric of the layer of silicon dioxide between the floating gate and the control gate is important. In the prior art (see for example, U.S. Patent No. 4,203,158 and W.S. Johnson et al. ISCCC Digest of Technical Papers, pp. 152-153 (Feb., 1980)), the floating gate is formed by reacting SiR4 in a low pressure chemical vapor deposition chamber and then doped with POCl3. A layer of silicon dioxide is then deposited or thermally grown on the doped polycrystalline layer of silicon. The layer of silicon dioxide is typically approximately 750 angstroms. Generally, a high oxidation temperature (greater than 1050 C) and heavier phosphorus doping are required to achieve better interpoly quality on breakdown capability. However, oxidation at high temperature on heavily-doped polysilicon involves several drawbacks, such as: (1) outgassing during interpoly oxidation which causes autodoping on wafer. (2) oxidation enhanced diffusion of phosphorus from the floating gate to the tunnel oxide, which, forms a trapping center in the oxide. The phosphorus induced trap collapses the threshold window of EEPROM cell at 10# cycles. (See: R.B. Marcus et al., J. Electrochem. Soc., p. 1282, June, 1982; K. Saraswat et al., Computer-Aided Design of Integrated Circuit Fabrication Process for VLSI Device, p. 244-290, July, 1981.) Finally, the second layer of doped polycrystalline silicon is then formed on top of the insulating layer of Six2. Because the insulating layer of silicon dioxide is on the order of 750 angstroms, the typical write or erase voltage, i.e., the voltage which is needed to place charges on or to remove charges off the floating gate has been high, i.e., in excess of 20 volts, which places the shrinkage limits for gate oxide thickness, junction depth and die size. Silicon nitride (Si3N4) has also been used as an insulating layer of dual dielectric (thermal oxide#ith silicon nitride on it) between the floating gate and the control gate connection. Silicon nitride has the property that it is more dense than silicon dioxide and, therefore, affords higher capacitive coupling between the floating gate and the control gate. A typical dual dielectric between the floating gate and the control gate is composed of 500 angstroms oxide and 400 angstroms nitride. However, even with the use of silicon nitride as the insulating layer, the write and erase voltage is still relatively high, in excess of 20 volts. This is due to the problem of asperity or roughness in the surface of the floating gate. Asperity in the floating gate causes points of electrical field enhancement. Thus, a large amount of insulating material must be interposed between the floating gate and the'control gate. This, however, in turn, requires that a large voltage be used. Summary Of The Invention In the present invention, an electrically programmable memory device is disclosed in which the floating gate is first formed by depositing a layer of polycrystalline silicon. Subsequently, a layer of silicon dioxide of approximately 200 angstroms is thermally formed over the polycrystalline silicon. The layer of polycrystalline silicon is then doped by ion implantation technique in which ions are implanted through the insulating layer of silicon dioxide into the layer of polycrystallihe silicon to dope it to form the floating gate. A LPCVD silicon nitride (approximately 200 angstroms) is then deposited on the layer of silicon dioxide. Finally, a pyrogenic oxidation (H2/O2) is performed to reduce the nitride pinhole and nitride/oxide interface state. Brief Description Of The Drawings Fig. 1 is an enlarged cross-sectional view of an EPROM device of the prior art and of the present invention. Fig. 2 is an enlarged cross-sectional view of an EEPROM device of the prior art and of the present invention. Fig. 3 is a cross-sectional view, greatly enlarged, of a section of the floating gate of the EPROM or EEPROM device of the prior art and a section of the floating gate of EPROM or EEPROM device of the present invention superimposed thereon. Fig. 4 is an enlarged cross-sectional view of another EPROM device of the present invention. Fig. 5 is an enlarged cross-sectional view of another EEPROM device of the present invention. Fig. 6 is a graph showing current-voltage characteristics of a device of the prior art and of the present invention. Detailed Description Of The Drawings Referring to Fig. 1, there is shown an EPROM 10 of the prior art. The EPROM 10 comprises a substrate 12, which is typically a single crystalline silicon of the P type having a source 14 and a drain 16 fabricated therein. A first layer 18 of insulating material, typically SiO2, is grown on the silicon substrate 12. The first layer 18 of SiO is thermally grown at 2 approximately 1,000 degree centigrade, using HCl and 02. On the first layer 18 of SiO2 is deposited the first layer 20 of polycrystalline silicon. The first layer 20 of polycrystalline 20 is deposited by low pressure chemical vapor deposition techniques. In a reaction chamber, SiH4 is introduced and is reacted at approximately between 620-670 degrees centigrade, depositing the layer 20 of polycrystalline silicon. The first layer 20 of polycrystalline silicon is then doped by phosphorus, rendering it conductive to form the floating gate. Phosphorus is introduced into the reaction chamber in the form of POCl3 at 950 degrees centigrade. A second layer 22 of insulating material, i.e., SiO2, is thermally grown on the floating gate 20. The second layer 22 of SiO2 is typically on the order of 750 to 1000 angstroms. A second layer 24 of polycrystalline is deposited on the second layer 22 of Six,: The second layer 24 of polycrystalline silicon is doped to form the connection for the control gate of the EPROM 10. Referring to Fig. 2, there is shown an EEPROM 110 of the prior art. The EEPROM 110 of the prior art is identical to the EPROM 10 of the prior art, shown in Fig. 1, except for the tunnel oxide 15 region between the drain 16 and the floating gate 20. The tunnel oxide region is typically approximately 100 angstroms thick. This narrow, thin tunnel oxide region 15 permits electrons to tunnel to or from the drain 16 during the erase or write cycle. The fabrication of the first layer 18 and second layer 22 of SiO2 and the formation of the floating gate 20 and of the control gate 24 is similar to that described for the EPROM 10 of Fig. 1. In the method of the present invention, the first layer 18 of Si02 is thermally grown on the single crystalline substrate 12 in the same manner as that for the EPROM 10 or the EEPROM 110 of the prior art. The floating gate 20, however, is formed by depositing a layer of polycrystalline silicon on the first layer 18 of SiO2. The layer 20 of polycrystalline silicon is deposited by low pressure chemical vapor deposition technique in which SiH4 is introduced and is reacted at approximately between 620-670 centigrade. The second layer 22 of SiO2 is then thermally grown on the first layer 20 of undoped polycrystalline silicon. The second layer 22 of SiO2 is approximately 250 angstroms thick. Phosphorus ions are then implanted in the first layer 20 of polycrystalline silicon through the second layer 22 of SiO2. Typically, the phosphorus ions are accelerated at 70-120 KEV to impinge the second layer 22 of SiO2, to pass therethrough and to be deposited in the first layer 20 of polycrystalline silicon. The first layer 20 of polycrystalline silicon, doped with the phosphorus, becomes the floating gate 20. SiO2 can then be further deposited on top of the second layer 22 of Di 2 to increase the total thickness to approximately 400-500 angstroms. The second layer 24 of polycrystalline silicon is then deposited on the second layer 22 of silicon dioxide in the same manner as the prior art. The second layer 24 of polycrystalline can then be doped to be conductive to form the control gate. Referring to Fig. 3, there is shown a section oi the floating gate 20 of the EPROM 10 or EEPROM 110 of the prior art (shown in solid line) and a section of the floating gate 120 of the EPROM or EEPRO,n5 made by the method of the present invention (shown in dotted lines). This is a greatly enlarged view, as typically the dimension of the floating gate is less than one micron in size. As can be seen in Fig. 3, the floating gate 20 of the prior art shows a number of bumps (designated as A, B, C, etc.). The asperity in the floating gate 20 is attributable to the chemical phosphorus doping of the polycrystalline silicon. These bumps in the floating gate 20 form electrical field enhancement points. To prevent undesired discharge between the floating gate 20 and the control gate, the insulating layer therebetween or the second layer 22 of silicon dioxide must be relatively large (on the order of 750 degrees A angstrom). Since Ct, where E is the dielectric constant of the material, A is the area between the two gates, and T is the thickness therebetween, for a large T, the value of C is reduced. Furthermore, since AQ=C¯V for a reduced value of C, a large value of voltage V must be used to place the charge Q on or to remove it from the floating gate 20. Subsequently, the voltage to write or to erase must be large. In contrast, with the floating gate 120 formed by the method of the present invention, the surface is relatively smooth. The doping material is not chemically introduced and does not deform the surface of the floating gate 120. Because the surface of the floating gate 120 is relatively smooth, the second layer 22 of silicon dioxide can be on the order of 400-500 angstroms. This increases the capacitive coupling. Thus, the operating voltage for the write and erase cycles can be much lower. The charging and discharging of the floating gate is accomplished by Fowler-Nordheim tunneling of electron across the tunnel oxide. The tunnel current EMI7.1 where p is the electric field across the tunnel oxide, and p are constants, electrical field EMI7.2 where V is the voltage drop across the tunnel oxide and t is the tunnel oxide thickness. V can be calculated from the capacitive equivalent voltage divider circuit. V If we define the coupling ratio as V applied, during the charging state, the coupling ratio is CDP C total where C total is the sum of interpoly capacitance (Cpp), gate oxide capacitance and tunnel oxide capacitance. Higher interpoly capacitance results in higher coupling ratio, which, results either in the reduction of charging state applied programming voltage or in shorter charging state programming time. Referring to Fig. 4, there is shown a crosssectional view of another EPROM 210 of the present invention. The EPROM 210 comprises a single crystalline silicon substrate 212, having a source 214 and a drain 216. A first layer 218 of SiO2 is on the body 212. A first layer of undoped polycrystalline silicon 220 is on the first layer 218 of silicon dioxide. The first layer 220 is deposited by low pressure chemical vapor deposition technique of SiH4 at 620"C. The layer 220 is approximately between 3000-4500 angstroms thick. A second layer 222 of silicon dioxide is on the first layer 220 of polycrystalline silicon. The second layer 222 is substantially between 200-250 angstroms. The second layer 220 is formed by thermal oxidation of dry 02 at approximately 1000 C. The first layer 220 of polycrystalline silicon is doped with phosphorus that has been ion implanted through the second layer of 222 of silicon dioxide. P31 is implanted at 1-5 x 10 /cm2 at 70-120 KEV. Thereafter, the second layer 222 of silicon dioxide is bathed in sulfuric acid at 150 0C for about 10 minutes. Then, the second layer 222 is dipped in a dilute HF acid for about 5 seconds to remove contamination due to the ion implantation. The HF acid removes approximately 25 angstroms of SiO2. The dilute HF acid comprises ten parts of distill water to one part of HF acid. The second layer 222 is then rinsed in distilled water and dried. A third layer 224 of insulating material is deposited on the second layer 222 of silicon dioxide. The third layer 224 comprises silicon nitride (Si3N4) and is deposited by low pressure chemical vapor deposition technique. NH3 and SiH2Cl2 are reacted at approximately 770 CC. The third layer 224 is approximately 250 angstroms. A pyrogenic oxidation (H2/02) cycle is then performed to reduce the nitride pinhole and nitride/oxide interface state. The pyrogenic oxidation step is accomplished by reacting H2 and O2 at 9000C for about 2 hours. This automatically produces the third layer 226 of SiC2 which is between approximately 30-50 angstroms. Finally, the second layer 228 of polycrystalline silicon is then deposited on the third layer 226 of Six2. The second layer 228 of polycrystalline silicon is then doped to form the control gate. Referring to Fig. 5, there is shown another EEPRO 310 of the present invention. The EEPROM 310 of the present invention is identical to the EPROM 210 shown in Fig. 4, except with the addition of a tunnel oxide region 315. In all other respects, the first, second, and third layers of insulating material (comprising the two layers of SiO2 and one layer of Si 3N4) and the two layers of polycrystalline silicon are identical to the similar structures for the EPROM 210 and are made in the same manner. The first layer of SiC2 is approximately 750 angstroms thick over the thick gate region and is approximately 100 ¯angstroms thick in the tunnel oxide region. With the EPROM 210 or the EEPROM 310, there is greater capacitive coupling betwen the control gate and the floating gate due to the silicon nitride deposited therebetween. Since silicon nitride has a higher dielectric constant, the capacitance is increased. This means that a lower operating voltage, on the order of 12 volts, can be used to write or to erase charges from the floating gate 220.

Claims: Claims 1. A method of making an electrically programmable memory device of the type having a plurality of electrical connections and a floating gate for storing charges therein, said method comprising the steps of fabricating a body of single crystalline semiconductive material having at least one said connections; thermally growing a first layer of insulating material on said body of semiconductive material; depositing a first layer of semiconductive material on said first layer of insulating material; thermally growing a second layer of insulating material on said first layer of semiconductive material; implanting a doping material through said second layer of insulating material into said first layer of semiconductive material to form said floating gate; and depositing a second layer of semiconductive material over said second layer of insulating material and forming an electrical connection. 2. The method of Claim 1, wherein said body of single crystalline semiconductive material and said first and second layers of #emiconductive material are of silicon. 3. The method of Claim 2, wherein said first and second layers of silicon are polycrystalline silicon. 4. The method of Claim 2 wherein said first and second layers of insulating material are of silicon dioxide (SiO2). 5. The method of Claim 3, wherein said first layer of polycrystalline silicon is deposited by low pressure chemical vapor deposition. 6. The method of Claim 1, wherein said implanting step is by ion implantation. 7. The method of Claim 5, wherein said doping material is phosphorus. 8. the method of Claim 1 after said implanting step further comprising the steps of removing a portion of said second layer of insulating material; and depositing a third layer of insulating material on said second layer of insulating material; wherein said second layer of conductive material being deposited on said third layer of insulting material. 9. The method of Claim 8, wherein said body of single crystalline semiconductive material and said first and second layers of semiconductive material are of silicon. 10. The method of Claim 9, wherein said first and second layers of silicon are polycrystalline silicon. 11. The method of Claim 9, wherein said first and second layers of insulating material are of silicon dioxide (SiO2). 12. The method of Claim 11, wherein said third layer of insulating material is Si3N4. 13. The method of Claim 11, wherein said first layer of polycrystalline silicon is deposited by low pressure chemical vapor deposition. 14. The method of Claim 8, wherein said implanting step is by ion implantation. 15. The method of Claim 13, wherein said doping material is phosphorus. 16. The method of Claim 15, wherein said removing step comprises exposing said second layer of SiO2 to dilute HF acid. 17. The method of Claim 16 further comprising the step of exposing said third layer of insulating material to pyrogenic (H2/O2) oxidation, forming a fourth layer of insulating material of SiO2. 18. The method of Claim 17, wherein said depositing step for the first layer of polycrystalline silicon forms approximately 3000-4000 angstroms; said depositing step for the second layer of SiO2 forms substantially 250 angstroms; said removing step removes substantially 20 angstroms of SiO2; said depositing step for the third layer of Si N forms substantially 250 angstroms; and said fourth layer is substantially 30-50 angstroms. 19. A method of reducing asperity in the floating gate of an electrically programmable memory device, said floating gate positioned between a first layer of insulating material and a second layer of insulating material and being of a semiconductive material, doped with a dopant, where said improvement comprising depositing said semiconductive material on said first layer; thermally growing said second layer on said 10 semiconductive material; and ion implanting said dopant through said second layer into said semiconductive material forming said floating gate. 20. The method of Claim 19, wherein said first and second layers are of Si02; said semiconductive material is polycrystalline silicon; and said dopant is phosphorus. 21. An electrically programmable memory device comprising a body of single crystalline semiconductive material having a source and a drain; a first layer of insulating material on said body; a floating gate on said first layer; a second layer of insulating material on said floating gate; said floating gate formed by depositing a layer of semiconductive material on said first layer of insulating material; thermally growing said second layer of insulating material on said layer of semiconductive material; and ion implant ing a dopant through said second layer of insulat ing material into said layer of semiconductive material; and a gate over said second layer of insulating material. 22. The device of Claim 21 further comprising a third layer of insulating material on said second layer of insulating material; said gate on said third layer. 23. The device of Claim 21, wherein said body and said floating gate is of silicon. 24. The device of Claim 23, wherein said floating gate is of polycrystalline. 25. The device of Claim 24, wherein each of said first and second layers of insulating material is of Six2, and said dopant is phosphorus. 26. The device of Claim 22, wherein said body and said floating gate is of silicon. 27. The device of Claim 26, wherein said floating gate is of polycrystalline. 28. The device of Claim 27, wherein each of said first and second layers of insulating material is of SiO2, and said dopant is phosphorus. 29. The device of Claim 28, wherein said third layer is of Si3N4. 30. The device of Claim 29, wherein said first layer of SiO2 is approximately 750 angstroms over the thick gate area and approximately 100 angstroms over the thin gate area; said floating gate is substantially 3000-4500 angstroms; said second layer of Si02 is substantially 230 angstrons; and said layer of Si3N4 is substantially 250 angstroms.

Inventors: CHANG, THOMAS T. L., HO, CHUN, MALHOTRA, ARUN KUMAR
Applicants: EXEL MICROELECTRONICS, INC.
Application year: 1984
Main classification: H01L29
IPC codes: H01L21, H01L29