A METHOD OF PRODUCING A PLASTIC COATED INK ROLLER FOR A PRINTING PRESS

Abstract: An ink roller (3) for use in a printing press is produced by crimping a heated tubular piasticjacket(1) onto a metal cylin­ der (2). According to the invention the metal cylinder is heated to a temperature of the same order as the temperature of the heated plastic jacket prior to fitting the latter onto the metal cylinder.

Description: The present invention relates to a method of producing plastic coated ink rollers for printing presses. Today rollers for printing presses are usually made from stainless steel, or they are mild steel cylinders coated with vinyl or hard rubber. Since such rollers or cylinders are expensive they are not replaced as often as would be recommendable, which frequently leads to an excessive amount of waste at printing start-up. For several years experiments have been going on with plastic coated steel rollers, because PVC plastic material shows better properties than steel, copper and nylon with respect to the capability of retaining oil-containing ink when water drops are added to the ink in the dampening system of the press during printing. It has also been a requirement that the plastic coated rollers should be capable of withstanding machining in a lathe to pattern their surfaces. However, this requirement has not been fulfilled since one has not succeeded in obtaining a sufficiently stable bonding between the plastic and the steel material of the rollers. Most plastic materials, including PVC, have a thermal coefficient of expansion substantially higher than those of the metals which are adapted to form the metal cylinder of the printing rollers, such as steel. A method likely to be suitable for making plastic coated ink rollers would be to shrink a heated tubular plastic jacket onto the metal cylinder, the plastic material upon cooling contracting sufficiently to cause a friction bonding to the metal cylinder. However, practice has shown that the metal cylinder, owing to its high thermal conductivity, causes the plastic coating material to cool down at such a high rate that in order to be able to altogether manage to get the plastic coating onto the cylinder the difference between the external diameter of the metal cylinder and the internal diameter of the heated tubular plastic jacket has to be of such a size that the crimping forces, and consequently the friction forces, after cooling will not be sufficient to restrain the plastic jacket on the metal cylinder when external stresses are applied to the plastic jacket, such as when machining it in a lathe. Therefore some kind of adhesive or other auxiliary means of mechanical type, such as inventions, protrusions or the like, must be utilized to secure the plastic jacket to the metal. This of course will increase the costs of production, and a reliable bonding is not always obtained. In a different art, it is known from DE-C-1,152,814 to apply a plastic coating to a continuous metal wire or tube. This coating is achieved by means of an extrusion process in which the wire or tube is pre-heated so that large thermal stresses in the hot plastic material are avoided. The object of the invention is to provide a method of the above mentioned type which results in a reliable and durable bonding between plastic and metal. According to the invention there is provided a method for producing a plastic coated ink roller for a printing press, comprising shrinking by cooling a heated, tubular jacket of a plastic material such as PVC onto a metal cylinder, said metal cylinder being heated to a temperature in the order of the temperature of the heated plastic jacket prior to fitting the plastic jacket onto the metal cylinder. This method will permit using a very narrow clearance between plastic jacket and metal cylinder during assembly thereof, resulting in correspondingly large shrinking forces after cooling. Thus, the end product will be an ink printing roller provided with a firmly fixed plastic coating or jacket without any air pockets between plastic coating and metal surface and without any risk of the jacket being displaced during machining in a lathe. In addition the plastic jacket may be replaced in a simple and inexpensive manner when needed. The invention will now be explained in detail with reference to the accompanying drawing in which: Fig. 1 is a perspective view of steel cylinder and plastic jacket during assembly thereof according to the invention, and Fig. 2 and 3 are an elevational view and end view respectively of the ink roller produced by the method according to the invention. Referring to the drawings a tubular plastic jacket 1 of a suitable material, for example PVC is to be shrunk onto a metal roller, for example a tubular or solid steel cylinder 2, to form an ink roller 3 for use in a printing press. The metal cylinder 2 and the tubular plastic jacket 1 is heated in a heating chamber (not shown) to the maximum temperature the plastic material can withstand without being deformed. This causes the internal diameter of the tubular plastic jacket to be slightly larger than the external diameter of the metal cylinder, allowing the plastic jacket to be pushed into the heated metal cylinder as indicated by the arrow in fig. 1 in a simple and controllable manner. Owing to the high specific heat of the metal cylinder cooling can take place at room temperature. In each case the internal diameter of the tubular plastic jacket prior to heating is calculated in relation to the coefficient of expansion of the plastic material and the temperature to which the cylinder and jacket is heated. Thus, when using a high impact strength PVC heating of the plastic jacket to about 140°C and the metal cylinder to about 100°C will give a good result if the ratio between the internal diameter of the plastic jacket and the external diameter of the steel cylinder is from about 0,97 to about 1,00 at room temperature. In Fig. 2 and 3 the plastic jacket 1 has been shrunk onto the steel cylinder 2, resulting in the plastic coated ink roller 3. The nominal diameter and length of ink printing rollers produced according to the invention as described above may vary according to the type of printing machine in question. The surface of the plastic jacket may be smooth (machined to the exact diameter) or patterned (serrated).

Claims: A method for producing a plastic coated ink roller for a printing press, comprising shrinking by cooling a heated tubular jacket of a plastic material such as PVC onto a metal cylinder, said metal cylinder being heated to a temperature in the order of the temperature of the heated plastic jacket prior to fitting the plastic jacket onto the metal cylinder. A method according to claim 1, comprising heating the metal cylinder and plastic jacket to the maximum temperature which the plastic can withstand without being deformed. A method according to claim 1 or 2, wherein the tubular plastic jacket is made of a high impact strength PVC material, and wherein the ratio between the internal diameter of the plastic jacket and the external diameter of the steel cylinder at room temperature is from about 0,97 to 1,00, characterised by heating the plastic jacket to about 140°C and the metal cylinder to at least 100°C.

Inventors: GROEDUM, SVEIN, Grödum, Svein
Applicants: GROEDUM, SVEIN
Application year: 1984
Main classification: B29C63
IPC codes: B41N7, B29C63