PERFORATING SCREEN AND METHOD OF MAKING IT

Abstract: A laminated, cylindrical, metal screen or molding ele­ ment for vacuum perforation of plastic film or sheets, comprising two or more relatively thin cylindrical metal screens, each having a predetermined inside and outside diameter and each having a plurality of openings or holes therein of a predetermined size and geometrical shape, and said relatively thin screens stacked and bonded together, diametrically one inside the other thereby providing a screen of a desired thickness and a desired hole geometry wherein the holes in the screen have substantially straight walls perpendicular to the surface of the screen. A method of producing a relatively thick cylindrical metal screen for vacuum perforation of plastic film or sheets wherein the holes or openings in the screen have substan­ tially straight walls perpendicular to the surface of the screen, comprising stacking and bonding together two or more matched relatively thin metal screens diametrically one inside the other.

Description: The present invention is in the general field of perforated plastic film and especially relates to vacuum perforating of plastic film. The invention particularly relates to metal screens or molding elements used in the vacuum perforation of plastic film and to a method of fabricating such screens. Perforated plastic film has many useful applications. It is used in gardening and farming to prevent the growth of grass and weeds while permitting moisture to be transmitted through the film to the soil beneath. Perforated film is also used for making disposable diapers, for example, see U.S. 3,814,101. One of the earlier methods for vacuum perforation of plastic film is disclosed in U.S. 3,054,148. The patentee describes a stationary drum having a molding element or screen mounted around the outer surface of the drum and adapted to freely rotate thereon. A vacuum chamber is employed beneath the screen to create a pressure differential between the respective surfaces of the thermoplastic sheet to be perforated to cause the plasticized sheet to flow into openings provided in the screen and thereby cause a series of openings, holes or perforations to be formed in the plastic sheet or film. A variety of methods and apparatuses including particular types of perforating screens or rotatable molding elements have been developed over the years for particular perforation operations. Examples of these are U.S. 4,155,693, U.S. 4,252,516, U.S. 3,709,647, U.S. 4,151,240, U.S. 4,319,868 and U.S. 4,388,056. In U.S. 4,155,693, the screen is comprised of a series of perforated metal strips preferably welded together to form a cylinder. U.S. 4,252,516 provides a screen having a series of hexagonal depressions with elliptical holes centered therein. U.S. 3,709,647 provides for a rotating vacuum-forming roll having a circulating cooling medium therein. U.S. 4,342,314 discloses a method for forming a planar forming surface or a cylindrical forming surface, each of such surfaces being used to emboss or perforate film. The method, and thus the resultant forming surface, is obtained by first bonding together a plurality of laminae so that the pattern cut in each of the lamina is in alignment with the pattern in all other of the laminae. The various laminae, after bonding, are joined together at two of their opposite ends by means of a seam. U.S. 4,151,240 provides a means for cooling the film after it has been perforated and debossed. U.S. 4,319,868 sets forth an apparatus for making a thermoplastic film having raised bosses with perforated tips. A particularly constructed embossing roll for effecting the desired film pattern is disclosed. U.S. 4,388,056 discloses an apparatus for continuously forming an airlaid fibrous web having oppositely phased, cylindrically undulating side edges and a predetermined basis weight distribution. An air-laying drum has a honeycomb type annular-shape frame including circumferentially extending ribs and transverse plates. A stationary adjustable air flow modulating means is disposed adjacent the radially inwardly disposed boundary of an arcuate portion of a circumferentially segmented annular-shape plenum, circumferentially spanning a plurality of plenum segments for adjusting a pressure drop across particular areas of the surface of the air-laying drum. Vacuum perforation of thin plastic films involves the extrusion of molten polymeric materials such as polyethylene and other plastic polymers though a slot die. The hot melt web of film or plastic sheet exiting the die impinges on a rotating cylindrical screen which is mounted on a stationary vacuum drum or roll. The vacuum roll has an axial slot and a set of seals extending longitudinally the length of its outside surface, beneath the area where the web of plastic impinges on the screen or molding element. A high vacuum from inside the screen is directed through the slot in the vacuum roll. The vacuum present within the slot forms or molds the plastic film or sheet to the screen and perforates it through the holes of the screen. At the same time, an airflow is produced which cools the film. The most important component of the vacuum processing equipment is the cylindrical screen. This molding element defines aesthetic and mechanical properties of the film as well as the geometric pattern of the perforated film. In a preferred screen fabrication technique, the desired screen pattern is nickel plated on a specially prepared cylindrical mandrel. A seamless cylindrical nickel screen of any predetermined or desired pattern can be produced. Other metals, such as copper may also be used. Some film products require the use of relatively thick screens, e.g. from 0.020 to 0.100 inches (0.0508 - 0.254 cm) thick, and also require that the walls of the patterned holes are straight and perpendicular to the screen surface. Present screen fabrication techniques as heretofore described are not capable of producing a screen meeting these requirements. The patterned holes on screens produced by nickel plating a prepared cylindrical mandrel, even with the application of specialized plating and post etching techniques, take the shape of inverted, truncated, concaved cones. The thicker the screen, the more exaggerated the effect becomes. This invention provides a laminated, seamless, cylindrical metal screen or molding element for vacuum perforation of plastic film or sheets, comprising two or more thin, seamless, cylindrical metal screens, each of the thin screens having a plurality of openings or holes therein, the thin screens being stacked and bonded together diametrically one inside the other to provide the laminated cylindrical metal screen, the holes of each of the thin screens being substantially aligned with the holes of the other screen or screens and each of the holes in the thin screens having a radial centreline aligned with the radial centreline of the or each aligned hole of the other thin screen or screens. In another aspect, the invention includes a method of making a thick cylindrical metal screen or molding element for vacuum perforation of plastic film or sheets, comprising stacking and bonding together two or more matched thin, seamless, cylindrical metal screens, each of the thin screens having a plurality of openings or holes therein and the thin screens being stacked and bonded together diametrically one inside the other to provide the thick cylindrical metal screen, the holes of each of the thin screens being substantially aligned with the holes of the other screen or screens and each of the holes in the thin screens having a radial centreline aligned with the radial centreline of the or each aligned hole of the other thin screen or screens. In a further aspect, the invention provides a method of fabricating a laminated, cylindrical metal screen or molding element for vacuum perforation of plastic film or sheets, comprising the steps of: a. preparing two or more matched thin, seamless, cylindrical metal screens, each of a predetermined size and having a plurality of holes therethrough, b. overplating each of said matched thin screens with a thin plate of a bonding material whereby after plating, the inside diameter of the largest screen fits, within a specified tolerance, the outside diameter of the next largest screen; c. preparing two seamless, cylindrical metal sleeves, each of a predetermined size with one being larger than the other; d. chrome plating the inside surface of the larger diameter sleeve and the outside surface of the smaller diameter sleeve whereby after plating the inside diameter of the larger sleeve fits, within a specified tolerance, the outside diameter of the largest diameter plated matched screen and the outside diameter of the smaller sleeve fits within a specified tolerance the inside diameter of the smallest diameter plated matched screen; e. coating the entire inside surfaces of each of the matched screens with a flux; f. mounting the larger sleeve in a cradle and so restraining it as to retain its cylindrical shape; g. malforming the largest diameter plated screen, sliding it inside the larger sleeve and then reforming it to its cylindrical shape; h. malforming the next largest diameter plated screen, sliding it inside the largest diameter matched screen, aligning the two screens and fastening them together, and then reforming the next largest diameter matched screen to its cylindrical shape such that the holes of each of the thin screens are substantially aligned with the holes of the other screen or screens and each of the holes in the thin screens has a radial centreline aligned with the radial centreline of the or each aligned hole of the other thin screen or screens; i. successively installing any remaining screens in a manner similar to that of step h such that the holes of each of the thin screens are substantially aligned with the holes of the other screen or screens and each of the holes in the thin screens has a radial centreline aligned with the radial centreline of the or each aligned hole of the other thin screen or screens; j. after all of the matched screens have been installed, installing the smaller cylindrical sleeve in a manner similar to that of the plated screens thereby completing the assembly; k. after assembly is completed, heating it in an oven at a temperature sufficient to effect the bonding of each plated screen to the adjacent plated screen or screens; l. cooling the assembly, and then removing it from the oven; and, m. axially cutting the larger diameter sleeve and removing it from the assembly, thereby providing the desired laminated cylindrical metal screen. Any remaining flux may be removed with an appropriate agent and the inside sleeve is removed thereby leaving a finished laminated screen product of desired specifications. Figure 1 is a schematic view illustration of an apparatus and method for vacuum perforation of thermoplastic film; Figure 2 is a side elevational view of a sleeve mounted in a cradle with a screen partially inserted therein; Figure 3 is an end view of the assembly of Figure 2 with the wall thickness of the screen and sleeve enlarged to show detail; Figure 4 is an end view similar to that of Figure 3, but illustrates a complete assembly of screens and sleeves; Figure 5 is a perspective view of a laminated screen of the invention; Figure 6 is an enlarged view of a segment of the screen of Figure 5; Figure 7 is a sectional view of the screen segment of Figure 6 taken along line 7-7; Figure 8 is a sectional view of a screen segment similar to that of Figure 7 illustrating an alternate hole radial cross-section; Figure 9 is a sectional view of a screen segment similar to that of Figure 7 illustrating another alternate hole radial cross-section; and Figure 10 is a sectional view of a screen segment similar to that of Figure 7 illustrating still another alternate hole radial cross-section. Referring now to Figure 1 of the drawings, vacuum process equipment and method for perforating plastic film or sheet therewith are schematically illustrated. A plastic polymer such as polyethylene is heated to a melt and extruded from an extruder E through a die D where a film web 10 is formed. The web 10 is directed onto a rotating cylindrical screen 11 having a desired pattern of holes which is turning clockwise as indicated by arrow A around a stationary vacuum roll or drum 12. A vacuum chamber 13 within the roll 12, longitudinal air slot 14 and seals 15 are employed to create a pressure differential between the respective surfaces of the thermoplastic sheet or web 10 to cause the plasticized sheet to flow into the holes in the screen in the direction indicated by the arrow B and therefore perforate the web 30. The perforated film web 10' travels onto a guide roll 16 and continues onto a wind-up roll It. Additional guide rolls or tensioning rolls can be employed as desired as well as various film treating equipment. Seamless cylindrical nickel screens produced by plating are made by two principal methods. In one method, a mandrel is ground to a dimension corresponding to the desired dimension of the finished screen. The desired screen hole pattern is engraved on the mandrel either by spiral engraving or malett indexing techniques. A plating resist medium is applied to the surface of the mandrel, filling the pattern produced by the engraving. A finish grinding operation is employed to remove the plating resist medium from the land areas between the engraved pattern, so that only the land area will be subject to plating. Subsequent nickel plating of the mandrel forms the screen. The mandrel is cooled and the finished screen is removed therefrom. The other method of producing a seamless cylindrical nickel screen is similar to the foregoing method, except that instead of engraving the pattern on the mandrel, a special photographic negative of the pattern is created and wrapped around the mandrel. Exposing of the negative transfers the pattern to the mandrel in the form of a plating resist, leaving only the land areas of the screen available for plating. The mandrel is then plated, forming the screen which is then removed from the mandrel to obtain the finished product. Either of these screen manufacturing methods are satisfactory to produce thin screens for lamination; however, the latter method is preferred. Using a photographic negative permits relative ease in transferring a pattern from one diameter screen to an identical one on another diameter screen by reduction of the photographic negative. In preparing a matched set of screens for lamination, several requirements must generally be met. First,each successive screen of the set must fit diametrically inside the next larger diameter screen, with sufficient space allowed for the metal or tin-lead alloy plating of each screen. Secondly, each screen of the set is typically geometrically identical. This means that each screen has the same number of holes, both axially and circumferentially, and that the radial centerlines of each hole of any one screen match identically the radial centerlines of the corresponding holes in all other screens in the set. Finally, the individual hole geometry of all the aligned holes in all the screens must generally be nearly identical. The inside diameter of each individual thin screen to be laminated may be calculated by the following formula: Dn = D + 2tp + (n-1) (2t L + 4tp) wherein Dn = Inside diameter of each individual thin screen n; D = Inside diameter of the finished laminated screen; n = The number of individual thin screens, counting from inside out, n = 1, 2, 3, . . . N; t L = The individual thin screen thickness (assumed constant for each screen of the set); and, tp = The thickness of the metal plating to be applied (assumed constant for each screen of the set). The inside diameter of the outer solid metal sleeve may be calculated by the following formula: Do.s = D N + 2t L + 2tp + 2tc wherein Do.s = Inside diameter of the outer sleeve; D N = Inside diameter of the Nth thin screen; and, tc = The thickness of the chrome plating to be applied. The inside diameter of the inner solid metal sleeve may be calculated by the following formula: DI.s = D - 2ts - 2tc wherein ts = The thickness of the solid metal sleeves (assumed to be same for each sleeve). Using the foregoing procedures and formulas, matched sets of seamless, cylindrical metal (nickel) screens may be produced as follows: 1. Grind a mandrel to a dimension corresponding to the finished sleeve inside diameter of Do.s, produce the outer cylindrical metal sleeve thereon, and plate the sleeve to a thickness of ts. 2. Grind the same mandrel to a dimension corresponding to the finished inside diameter of the Nth screen. Apply a desired screen pattern using the photo-negative resist method including a reference alignment mark at each end of the screen. Plate the mandrel to a thickness of t L , forming the largest, "Nth", screen of the matched set. 3. Grind the same mandrel to a dimension corresponding to the finished inside diameter of the (N-1)th screen. Reduce the photographic negative in the circumferential direction only to equal the circumference of the reground mandrel, and apply the pattern to the mandrel as before. Plate the mandrel to a thickness of t L forming the next largest, (N-1)th, screen of the matched set. The photographic negative reduction and transfer operation may be a computerized operation. 4. Repeat Step 3 for each of the remaining screens of the matched set. 5. Grind the same mandrel to a dimension corresponding to the finished sleeve inside diameter of DI.s., produce the inner cylindrical sleeve thereon, and plate the sleeve to a thickness of ts. Since screens are generally prepared for particular film perforating operations, the use of the same mandrel is preferable. Should a number of laminated screens of the same pattern be produced, a number of mandrels may be used, as appropriate. In the preferred form of the invention, a matched set of thin, seamless, cylindrical, nickel screens are prepared as set forth in detail hereinafter. The length and diameter of the screens is selected on the basis of the type of vacuum perforating equipment and the number of screens to be laminated. The thickness of each screen is determined on the basis of the type of hole wall shape desired. A screen thickness of approximately 0.005 inches (0.0127 cm) is preferred for providing hole walls that are substantially straight and perpendicular to the surface of the screen. Each screen of the matched set is overplated with a thin layer of a bonding material, preferably a tin-lead alloy. An alloy of 63 weight percent tin and 37 percent lead is especially preferred. An alloy layer of about 0.00025 inches (0.000635 centimeters) thick is most preferred. Each screen of the matched set is designed and produced so that after plating, the inside diameter of the largest screen fits, within a specified tolerance, the outside diameter of the next largest screen. In turn, each screen of the set fits similarly inside the next largest screen. Each screen of the set is designed and produced with a common reference or aligning mark at each end thereof. Alignment of the reference marks during assembly produces proper pattern hole alignment. Two seamless cylindrical nickel sleeves of different diameters are also required. The sleeves are about the same length of the thin screens. The thickness of the sleeves may be varied, but a thickness of approximately 0.010 inches (0.0254 centimeters) is especially preferred. The inside surface of the larger diameter sleeve, and the outside surface of the smaller diameter sleeve are chrome plated. A plating thickness of about 0.0005 inches 0.00127 centimeters) is most preferred. The sleeves are designed and produced so that after chrome plating, the inside diameter of the larger sleeve fits, within a specified tolerance, the outside diameter of the largest diameter thin screen, after the screen has been plated. Also, after chrome plating, the outside diameter of the smaller sleeve is designed and produced to fit the inside diameter of the smallest diameter thin screen of the matched set of screens, after the screen has been plated. The two sleeves are used as fixtures during the assembly and bonding operations as explained hereinafter. The tin-lead alloy plating applied to each screen provides the bonding medium for lamination. The chrome plating applied to the sleeves acts as a resist to prevent the tin screens being laminated from bonding to the sleeves. After the matched set of thin screens and the two sleeves have been prepared in the manner described, the assembly and bonding operations can be completed. Referring now to Figs. 2-4 of the drawings, the larger cylindrical sleeve 20 is mounted in a cradle 21 and restrained therein so as to retain its cylindrical shape by two stiff outside diameter ring clamps 22 and 23. Any other suitable restraining or clamping means may be used. The largest diameter thin screen 30 of the matched set of screens is malformed or otherwise distorted and slid or positioned inside the larger diameter sleeve 20. The screen 30 is then reformed into its cylindrical shape. The next largest screen 3l is similarly malformed and slid inside the largest screen 30 of the assembly 40. Reference marks 32 on the ends of the two screens are aligned and the screens are pinned or otherwise fastened together. If more than two thin screens are to be laminated or assembled, the remaining thin screens are similarly installed with the next largest thin screen being positioned inside the second thin screen 31 and so on, until each thin screen of the matched set of thin screens has been assembled. Once all the thin screens have been assembled, the smaller sleeve 24 is positioned within the smallest diameter thin screen in the same manner as the various thin screens were installed. Prior to the installation of the smaller sleeve, the entire inside surface of the assembly is thoroughly coated with an appropriate flux, for example, a liquid solder flux having a pure resin base or a soldering paste containing zinc chloride, both manufactured by CG Electronics. Any other suitable flux may be used. Once the assembly 40 is completed, it is transferred to an oven and uniformly heated to a temperature of about 400°F + 10°F (204.4°C + 5.56°C) or 390°F to 410°F (or 198.84°C to 209.96°C). During the bonding cycle, the cylindrical nickel sleeves remain on the assembled screens. The sleeves act to uniformly restrain the screen laminates while permitting growth and shrinkage during heating and cooling cycles as they are preferably of the same material as the thin screens. The assembly is then allowed to cool in the oven to nearly room or ambient temperature. It is then removed from the oven for final operations. After the assembly has been cooled and removed from the oven, the outside sleeve is carefully axially cut and removed. Remaining flux residue is removed from the screen assembly with a suitable agent, for example, by washing with a degreasing liquid followed by a neutralizing wash of a 2 percent solution of muriatic acid. Any other suitable flux removing agent may be used. The inside sleeve is then removed, leaving a finished laminated screen of a desired thickness. Although other bonding mediums may be used, the specific one of 63% tin-37% lead, plated to a thickness of 0.00025 inches (0.000635 centimeters) particularly meets the requirements of the fabricating system. Pure, plated nickel initiates embrittlement at approximately 425°F (218.3°C). Any bonding system selected must therefore cure or flow at a temperature below the embrittlement temperature of the nickel plating. The tin-lead alloy preferred is the eutectic formulation of the two elements. The alloy melts and solidifies at 361°F (182.3°C). The instant bonding system is unique, in that, by plating each individual thin screen prior to assembly, difficult and messy applications of bonding mediums during assembly are avoided. The tin-lead alloy plating thickness of 0.00025 inches (0.000635 centimeters) is the optimum thickness to produce good bonding with minimum excess alloy. Referring now to Fig. 5, a laminated screen 50 of the invention is seen which comprises four thin screens 51, 52, 53 and 54 which have been stacked and bonded together in accordance with the foregoing procedure. As seen in Fig. 6, the screen 50 has a plurality of openings or holes 50a therein. The holes 50a have walls 50b which are substantially straight as best seen in Fig. 7. In the latter figure, it is readily seen that the walls 50b are formed from the individual walls 51b, 52b, 53b and 54b of each of the tin screens 51, 52, 53 and 54, respectively. For purposes of illustration, the truncated holes of the thin screens have been exaggerated. The effect of the multiscreen lamination provides hole walls which are substantially straight. While the invention is particularly directed to a method of producing relatively thick seamless cylindrical metal screens, especially nickel screens, with holes or openings which are essentially straight and perpendicular to the screen surface, the method can also be utilized to provide thick screens with an expanded variety of hole radial cross-sections. It is only essential that the basic hole radial centerlines of each screen laminate be the same. Although for simplification, the invention is illustrated with screens having round holes, other hole configurations or patterns are suitable. Such holes may be oval, rectangular, pentagonal, hexagonal or any other desired geometric shape. Figs. 8-10 illustrate some of the screen arrangements that can be achieved by using thin screens of different hole sizes. It can readily be appreciated that a wide variety of hole shapes and sizes can be obtained for providing a particular hole effect in a thermoplastic film or sheet. It is preferred for the holes to have a diameter of from about 0.015 to about 0.02 inches (0.0381 - 0.0508 cm). It is also preferred for there to about 100 to 20,000 holes per square inch (15.5 to 3100 holes/cm²) of screen surface. Although the invention is particularly suited for perforating thermoplastic sheets or film made from polyolefins, especially polyethylene and polypropylene, it can be used with other types of thermoplastic films as desired.

Claims: A laminated, seamless, cylindrical metal screen or molding element (50) for vacuum perforation of plastic film or sheets, comprising two or more thin, seamless, cylindrical metal screens (51,52,53,54), each of the thin screens having a plurality of openings or holes (50a) therein, the thin screens being stacked and bonded together diametrically one inside the other to provide the laminated cylindrical metal screen (50), the holes of each of the thin screens being substantially aligned with the holes of the other screen or screens and each of the holes in the thin screens having a radial centreline aligned with the radial centreline of the or each aligned hole of the other thin screen or screens. A method of making a thick cylindrical metal screen or molding element (50) for vacuum perforation of plastic film or sheets, comprising stacking and bonding together two or more matched thin, seamless, cylindrical metal screens (51,52,53,54), each of the thin screens having a plurality of openings or holes (50a) therein and the thin screens being stacked and bonded together diametrically one inside the other to provide the thick cylindrical metal screen (50), the holes of each of the thin screens being substantially aligned with the holes of the other screen or screens and each of the holes in the thin screens having a radial centreline aligned with the radial centreline of the or each aligned hole of the other thin screen or screens. A method of fabricating a laminated, cylindrical metal screen or molding element for vacuum perforation of plastic film or sheets, comprising the steps of: a. preparing two or more matched thin, seamless, cylindrical metal screens (30,31), each of a predetermined size and having a plurality of holes therethrough, b. overplating each of said matched thin screens (30,31) with a thin plate of a bonding material whereby after plating, the inside diameter of the largest screen (30) fits, within a specified tolerance, the outside diameter of the next largest screen (31); c. preparing two seamless, cylindrical metal sleeves (20,24), each of a predetermined size with one being larger than the other; d. chrome plating the inside surface of the larger diameter sleeve (20) and the outside surface of the smaller diameter sleeve (24) whereby after plating the inside diameter of the larger sleeve (20) fits, within a specified tolerance, the outside diameter of the largest diameter plated matched screen (30) and the outside diameter of the smaller sleeve (24) fits within a specified tolerance the inside diameter of the smallest diameter plated matched screen (31); e. coating the entire inside surfaces of each of the matched screens (30,31) with a flux; f. mounting the larger sleeve (20) in a cradle (21) and so restraining it as to retain its cylindrical shape; g. malforming the largest diameter plated screen (30), sliding it inside the larger sleeve (20) and then reforming it to its cylindrical shape; h. malforming the next largest diameter plated screen (31), sliding it inside the largest diameter matched screen (30), aligning the two screens and fastening them together, and then reforming the next largest diameter matched screen to its cylindrical shape (31) such that the holes of each of the thin screens are substantially aligned with the holes of the other screen or screens and each of the holes in the thin screens has a radial centreline aligned with the radial centreline of the or each aligned hole of the other thin screen or screens; i. successively installing any remaining screens in a manner similar to that of step h such that the holes of each of the thin screens are substantially aligned with the holes of the other screen or screens and each of the holes in the thin screens has a radial centreline aligned with the radial centreline of the or each aligned hole of the other thin screen or screens; j.. after all of the matched screens have been installed, installing the smaller cylindrical sleeve (24) in a manner similar to that of the plated screens thereby completing the assembly; k. after assembly is completed, heating it in an oven at a temperature sufficient to effect the bonding of each plated screen to the adjacent plated screen or screens; l. cooling the assembly, and then removing it from the oven; and, m. axially cutting the larger diameter sleeve and removing it from the assembly, thereby providing the desired laminated cylindrical metal screen. A method according to claim 3 in which the metal sleeves are nickel sleeves. A method according to claim 3 or claim 4 in which the chrome plating on the metal sleeves is about 0.0005 inches (0.00127 centimeters) thick. A laminated metal screen according to claim 1 or a method according to any one of claims 2 to 5, wherein the holes in each thin metal screen have substantially straight walls substantially perpendicular to the surface of the thin metal screen. A laminated metal screen according to claim 1 or claim 6 or a method according to any one of claims 2 to 6 wherein each of said thin screens has a thickness of about 0.005 inches (0.0127 centimeters). A laminated metal screen according to any one of claims 1, 6 or 7 or a method according to any one of claims 2 to 7 wherein said screen has a total thickness of 0.02 to 0.100 inches (0.0508 to 0.254 centimeters). A laminated metal screen according to any of claims 1 or 6 to 8 or a method according to any one of claims 2 to 8 wherein the metal is nickel or copper. A laminated metal screen according to claim 1 or a method according to claim 2, wherein the thin metal screens are overplated with a bonding metal. A method according to claim 10, wherein the bonding is accomplished by coating the entire inner surface of the thin screens with a flux and heating the stacked screens in an oven to a temperature sufficient to effect the bonding. A laminated metal screen according to claim 10 or a method according to claim 10 or claim 11, wherein the relatively thin screens are as defined in claim 6 and/or claim 7, and/or wherein the laminated metal screen is as defined in claim 8 and/or claim 9. A laminated metal screen according to claim 10 or claim 12 or a method according to any one of claims 2 or 10 to 12 wherein the thin screens are overplated with a tin lead plating as the bonding metal or material. A laminated metal screen according to claim 13 or a method according to claim 13 wherein the tin-lead plating is about 63 weight percent tin and 37 weight percent lead. A laminated metal screen according to any one of claims 10 or 12 to 14 or a method according to any one of claims 2 or 10 to 14 wherein the thin screens are overplated with bonding metal alloy in a thickness of 0.00025 inches (0.000635 centimeters). A laminated, cylindrical metal screen according to any of claims 1, 6 to 10 or 12 to 15 or a method according to any one of claims 2 to 14 wherein the individual geometry of the holes in each of the thin screens is substantially identical. A method of vacuum perforating plastic film or sheets using a screen or molding element according to any one of claims 1 or 6 to 16. A method of vacuum perforating plastic film or sheets comprising effecting a method according to any one of claims 2 to 16 and thereafter using the resulting screen or moulding element for vacuum perforating plastic film or sheets.

Inventors: RALEY, GARLAND EUGENE, SPEAR, DEAN MICHAEL
Applicants: ETHYL CORPORATION
Application year: 1984
Main classification: B23P15
IPC codes: B23P15, B26F3, B23K1, B29K105, B26F1, B29C67, B29L7, B23K101