PROCESS FOR PREPARING A POLYOLEFIN POLYMERIZATION CATALYST

Abstract: An olefin polymerization catalyst prepared by reacting an admixture of anhydrous magnesium dihalide and hyd­ rous magnesium dihalide with reactants including benzoic acid ester, an alkoxytitanium compound, an organoalumi­ num halide, and a titanium halide.

Description: The present invention relates to a process for preparing a catalyst for the polymerization of olefins and its use for the polymerization of olefins. EP-A- 0 060 443 discloses a number of new high activity polymerization catalysts. One of the catalyst types disclosed was prepared by reacting reactants comprising a magnesium dihalide, a benzoic acid ester, and a titanium compound, such as an alkoxytitanium compound, to produce a first catalyst component, then reacting that component with a second catalyst component comprising a precipitating agent, and then reacting the resulting solid product with a halogenating agent, such as TiCl₄. The catalysts of the examples in that application were prepared using commercially available "anhydrous" magnesium dichloride. EP-A 0 115 833 to be considered under Art. 54(3) EPO discloses that the activity of such catalysts can be improved by insuring that the magnesium dihalides have certain specified amounts of water associated therewith. It has subsequently been noted that the addition of water to a hydrocarbon dispersion of the magnesium dihalide is inefficient for producing catalyst for most commercial scale operations since it leads to the formation of large solid agglomerates. The formation of the large solid agglomerates results in inefficient reaction of the magnesium dihalide in the later steps of the catalyst preparation and thus to lower catalyst activity. The presence of the large agglomerates also tends to cause plugging of the lines in which catalyst is generally transferred in modern commercial scale polymerization processes. In accordance with the present invention, the catalyst is produced by reacting an admixture of anhydrous magnesium dihalide and hydrous magnesium dihalide with reactants comprising a benzoic acid ester and an alkoxytitanium compound to form a first catalyst component, and then reacting said first catalyst component with an organoaluminum halide to form a solid product, then reacting that solid product with a halogenating agent comprising a titanium halide, wherein a magnesium dihalide is used comprising (a) magnesium dihalide containing less than 0.5 moles of water and (b) magnesium dihalide containing more than 0.5 moles of water, each per mole of magnesium dihalide, wherein the weight ratio of magnesium dihalide (a) to magnesium dihalide (b) is such that the molar ratio of water to magnesium dihalide in said admixture is in the range of 0.5/1 to 2/1. The level of water in the magnesium dihalide can be determined using routine analysis techniques. Typically such techniques involve the use of Karl Fischer titration plus other conventional techniques such as X-ray diffraction and elemental analysis for determining whether there are significant amounts of other materials, particularly MgO, associated with the MgCl₂. The presently preferred magnesium dihalide is magnesium dichloride. As magnesium dihalide (b) preferably one is employed which contains more than 2 moles of water per mole of magnesium dihalide. Typical examples of magnesium dihalides (b) include those of the formula MgCl₂·nH₂O, wherein n is 1, 2, 4 or 6. The amounts of magnesium dihalides (a) and (b) in the admixture are used to fix the ratio of water to magnesium dihalide in the admixture. A currently preferred mixture is obtained by admixing "anhydrous" MgCl₂ and MgCl₂·6H₂O. The magnesium dihalides (a) and (b) can be admixed in any suitable manner. One currently preferred technique involves the stirring of the dihalides in a suitable liquid. Preferably the liquid employed would be of a type suitable for use in preparing the catalyst composition. Typical examples include hydrocarbons such as n-pentane, n-heptane, methylcyclohexane, toluene or xylene that are substantially free of water. The amount of liquid employed is not considered to be particularly critical, however, for practical reasons it is preferred to use enough liquid to provide a readily stirrable mixture. A particularly desirable mixing technique involves ball milling the magnesium dihalides (a) and (b). The optimum molar ratio for water to magnesium dihalide in said admixture varies to some degree depending upon the monomer to be polymerized. Typically, a ratio in the range of 0.75/1 to 1.75/1 produces optimum results in polymerization. For propylene optimum results are generally achieved if the ratio is in the range of 1/1 to 2/1, more preferably 1/1 to 1.75/1, for ethylene 0.75/1 to 1.25/1. The alkoxytitanium compounds are those titanium compounds in which the titanium is bonded to at least one oxygen atom and the oxygen atom is bonded to at least one alkyl radical. The preferred alkoxytitanium compounds are those of the formula Ti(OR)₄ wherein each R is individually selected from an alkyl group containing 1 to 20 carbon atoms and each R can be the same or different. The most preferred are those in which each alkyl group contains 1 to 10 carbon atoms. The molar ratio of the alkoxytitanium compound to the metal halide compound can be selected over a relatively broad range. Generally, the molar ratio of alkoxytitanium to magnesium dihalide is in the range of 10/1 to 1/10, more preferably 2/1 to 1/2. The term benzoic acid ester is used generically to include substituted as well as unsubstituted benzoic acid esters. Typical examples include ethyl benzoate, ethyl p-methoxybenzoate, ethyl toluate, ethyl p-butoxybenzoate, and butyl benzoate. The preferred benzoic acid esters are those having 8 to 12 carbon atoms per molecule. In an especially preferred embodiment, a phenol is employed in conjunction with the benzoic acid ester in making the first catalyst component. The term "phenol" is used herein to refer to substituted as well as unsubstituted phenols. Typical examples include phenol; o-methyl phenol, m-methyl phenol, p-methyl phenol, 4-phenyl phenol, o-fluorophenol, m-fluorophenol, p-fluorophenol, p-sec-butyl phenol, p-ethyl phenol, p-isopropyl phenol, p-tertbutyl phenol, p-methoxy phenol, p-cyanophenol, and p-nitrophenol. The currently preferred combination of ester and phenol is 4-phenyl phenol and ethyl benzoate. The total number of moles of 4-phenyl phenol and ethyl benzoate employed can affect the activity and selectivity of the resulting catalyst. Typically, the ratio of the sum of the moles of those two electron donors to the moles of the titanium alkoxide are in the range of 5/1 to 1/5, more preferably 3/1 to 2/1. Most preferably, ½ mole of ethyl benzoate is employed per mole of titanium alkoxide. The formation of the first catalyst component is conducted by reacting the resulting hydrated magnesium dihalide with the titanium compound and a benzoic acid ester, and optionally and preferably with a phenol. The reaction is conducted in a suitable hydrocarbon solvent or diluent substantially free of free water. Examples include n-pentane, n-heptane, methylcyclohexane, toluene and xylenes. The amount of solvent or diluent can be selected over a broad range. Usually the amount of solvent or diluent would be within the range of 20 to 100 mℓ per gram of metal dihalide. Generally, it is preferred to combine the magnesium dihalide and the titanium compound at a temperature in the range of 0 to 50°C, more preferably 10 to 30°C. The reaction between the reactants of the first catalyst component is carried out at a temperature in the range of 15 to 150°C. Typically, the reaction is carried out by refluxing the mixture. While it is not absolutely critical, it is currently preferred to mix the magnesium dihalide and the titanium compound and optionally the phenol at a temperature in the range of 20 to 40°C, then to heat the mixture to 90-100°C for a few minutes, and then to add the ester at that temperature and maintain the mixture at a temperature of 90-100°C to complete the reaction. Generally, the time required for heating the reactants to make the first catalyst component is within the range of 5 minutes to 10 hours, although in most instances a time within the range of 15 minutes to 3 hours is sufficient. The reaction of the organoaluminum halide with the first catalyst component can be carried out by merely adding the organoaluminum halide to a solution of the first component. It is, however, currently preferred to add a hydrocarbon solution of the halide to the first component solution. The temperature employed for reacting the second catalyst component, i.e., the organoaluminum halide, and the first catalyst component can be selected over a broad range. Generally, the temperature employed is within a range of 0 to 50°C or higher, while temperatures within the range of 20 to 30°C were most often employed. Since heat is evolved when the first catalyst component and the second catalyst component are mixed, the mixing rate is adjusted as required and additional cooling is employed in order to maintain a relatively constant mixing temperature. It is noted with respect to mixing the first and second components that the order of addition is not important and either component can be added to the other. However, it is preferable to add the second component to the first. After completing the mixing, the resulting slurry is stirred or agitated for a sufficient time, generally within a range of 15 minutes to 5 hours to insure that mixing of the components is complete. Thereafter, stirring is discontinued and the solid product recovered, e.g. by filtration or decantation. The product is then washed with a suitable material such as a hydrocarbon, e.g., n-pentane, n-heptane, cyclohexane, benzene or xylenes, to remove any soluble material which may be present. The product is then dried and stored under dry nitrogen. The molar ratio of the transition metal compound of the first catalyst component to the second catalyst component can be selected over a relatively broad range. Generally, the molar ratio of the transition metal of the first catalyst component to the second catalyst component is within a range of from 10:1 to 1:10 and more generally within a range of 2:1 to 1:3 since a molar ratio within the latter range usually produces a catalyst which can be employed as an especially active olefin polymerization catalyst. Generally, the reaction between solid product resulting from the reaction of the first and second components with the halide ion exchanging source can be carried out neat or in a liquid medium in which the halide ion exchanging source is soluble. The product from step (2) is generally in a liquid diluent when contacted with the halide ion exchanging source. Any suitable diluent can be employed. Examples include normally liquid hydrocarbons such as n-pentane, n-heptane, cyclohexane, benzene, and xylene. The temperature employed in step (3) can be selected over a relatively broad range, generally in the range of -25 to +250°C, preferably 0 to 200°C, with temperatures of 100°C being most preferred. The treating time can also be selected over a broad range and generally is within the range of 10 minutes to 10 hours. While the weight ratio of the halide ion exchanging source to the product of step (2) can be selected over a relatively broad range, the weight ratio of the halide ion exchanging source to the product of step (2) is generally within a range of 10:1 to 1:10 and more generally from 7:1 to 1:4. Following the treatment of the product of step (2) with the halide ion exchanging source the surplus halide ion exchanging source is removed by washing the solid catalyst with a dry (essential absence of water) liquid such as a hydrocarbon of the type previously disclosed, n-hexane, or xylene, for example. The resulting catalyst, after drying, is stored under dry nitrogen. The currently preferred titanium halide for use as the halide ion exchanging source is TiCl₄. In an especially preferred embodiment, the TiCl₄ is employed in conjunction with a halide of silicon such as HSiCl₃ and/or SiCl₄. The catalyst of the present invention can be used in the polymerization of olefins. Olefins which can be homopolymerized or copolymerized with the invention catalysts include aliphatic mono-1-olefins. While the invention would appear to be suitable for use with any aliphatic mono-1-olefin, those olefins having 2 to 18 carbon atoms are most often used. The mono-1-olefins can be polymerized according to the present invention employing either a particle form process, a gas phase process, or a solution form process. Aliphatic mono-1-olefins can be copolymerized with other 1-olefins and/or with other smaller amounts of other ethylenically unsaturated monomers, such as 1,3-butadiene, isoprene, 1,3-pentadiene, styrene, alpha-methylstyrene, and similar ethylenically unsaturated monomers which do not impair the catalyst. The catalysts of this invention can also be utilized to prepare homopolymers and copolymers of conjugated diolefins. Generally the conjugated diolefins contain 4 to 8 carbon atoms per molecule. Examples of suitable conjugated diolefins include 1,3-butadiene, isoprene, 2-methyl-1,3-butadiene, 1,3-pentadiene, and 1,3-octadiene. Suitable comonomers, besides the conjugated diolefins listed above include mono-1-olefins previously described and vinylaromatic compounds generally. Some suitable vinylaromatic compounds are those having from 8 to 14 carbon atoms per moelcule, and include, for example, styrene and various alkylstyrenes, such as 4-ethylstyrene and such as 1-vinylnaphthalene. The weight percent of the conjugated diolefin in the copolymerization mixture can be selected over a relatively broad range. Generally the weight percent of the conjugated diolefin is from 10 to 95 weight percent and the other comonomers are from 90 to 5 weight percent. However, the weight percent of the conjugated diolefin is preferably from 50 to 90 weight percent and the other comonomers are from 50 to 10 weight percent. The inventive catalysts are particularly well suited for producing stereoregular polypropylene, many offering potential for high rates as well as low soluble polymer formation. Polymerization may be conducted in a liquid phase, in the presence or absence of an inert hydrocarbon diluent, or in a gas phase. In the polymerization of propylene, particularly satisfactory results have been attained operating in the presence of an aliphatic or aromatic hydrocarbon diluent, liquid under the polymerization conditions, such as propylene, toluene or gasoline. While it may not be necessary in all instances to employ a cocatalyst with the catalyst of the present invention, the use of cocatalysts is recommended for best results. The organometallic cocatalysts suitable for use in accordance with the invention can be selected from among the hydrides and organometallic compounds of metals of Groups IA, II and IIIA of the Periodic Table. Of the organometallic cocatalysts, organoaluminum compounds such as those described above as suitable for use as the second component of the catalyst, are preferred with the most preferred organoaluminum cocatalysts being compounds of the formula R₃Al which include, for example, trimethylaluminum, triethylaluminum, triisopropylaluminum, tridecylaluminum, trieicosylaluminum, tricyclohexylaluminum, triphenylaluminum, 2-methylpentyldiethylaluminum, and triisoprenylaluminum. Triethylaluminum is preferred since this compound produced excellent results in the runs hereafter described. The molar ratio of the organometallic compound of the cocatalyst to the transition metal compound of the first catalyst component is not particularly critical and can be selected over a relatively broad range. Generally, the molar ratio of the organometallic compound of the cocatalyst to the transition metal compound of the first catalyst component is within a range of 1:1 to 1500:1. For catalyst systems wherein the cocatalyst comprises at least one organoaluminum compound typically there is employed 0.25 to 15 milligrams of the titanium-containing component per mmole of organoaluminum cocatalyst. The catalyst is preferably used with a multicomponent cocatalyst system comprising triethylaluminum (TEA), an aromatic ester such as ethyl anisate (EA), ethyl benzoate (EB) or methyl-p-toluate (MPT), and diethylaluminum chloride. Best selectivity (stereospecificity) is obtained when the TEA:ester mole ratio is about 2:1. The DEAC, when used, helps in increasing activity. Generally, a TEA:ester:DEAC mole ratio of about 2:1:0.5-3 and preferably about 2:1:2 is employed in bench scale testing for batch polymerization. For a continuous, larger scale process, it becomes possible, for example, when using TEA and MPT to use TEA:MPT mole ratios of 3:1 to 5:1 and dispense with the DEAC entirely. A decreased DEAC level is desirable when employing a flash process to recover polymer since the amount of chloride remaining in the polymer is dependent to some extent on the DEAC level. The polymerization process according to the present invention employing the catalysts and cocatalysts as above described can be performed either batchwise or continuously. In a batch process, for example, a stirred autoclave is prepared by first purging with nitrogen and then with a suitable compound, such as isobutane for example. When the catalyst and cocatalyst are employed, either can be charged to the reactor first or they can be charged simultaneously through an entry port under an isobutane purge. After closing the entry port, hydrogen, if used, is added, and then a diluent such as isobutane is added to the reactor. The reactor is heated to the desired reaction temperature, which for polymerizing ethylene, for example, is, for best results, generally within a range of 50 to 120°C and the monomer is then admitted and maintained at a partial pressure within a range of 0.5 MPa to 5.0 MPa (70-725 psig) for best results. At the end of the designated reaction period, the polymerization reaction is terminated and the unreacted olefin and isobutane are vented. The reactor is opened and the polymer, such as polyethylene, is collected as a free-flowing white solid and is dried to obtain the product. In a continuous process, for example, a suitable reactor such as a loop reactor is continuously charged with suitable quantities of solvent or diluent, catalyst, cocatalyst, polymerizable compounds and hydrogen, if any, and in any desirable order. The reactor product is continuously withdrawn and the polymer recovered as appropriate, generally by flashing the diluent (solvent) and unreacted monomers and drying the resulting polymer. For optimum productivity of polymer of low solubility in the continuous polymerization of propylene preferably the cocatalyst comprising the trialkylaluminum-electron donor is contacted with the titanium-containing catalyst prior to being exposed to liquid propylene. The olefin polymers made with the catalysts of this invention are useful in preparing articles by conventional polyolefin processing techniques such as injection molding, rotational molding or extrusion of film. A further understanding of the present invention and its advantages will be provided by the following examples. EXAMPLE I - CATALYST PREPARATIONS General procedure : In each preparation, the catalyst components were charged to separate 1 quart (0.95 ℓ) glass beverage bottles containing a magnetic stirring bar in a dry box containing an argon atmosphere. Each bottle was capped, removed from the dry box and heated with stirring as detailed later. The bottle and contents were cooled to about room temperature (23°C), diluted with dry xylene, and treated dropwise with a 25 weight percent solution of ethylaluminum sesquichloride (EASC) in n-heptane to yield a precipitate. The bottle was returned to the dry box where the solids were isolated by centrifugation, washed by slurrying them and re-centrifugation. This was repeated several times until the supernatant liquid was colorless or nearly so, e.g. 3-4 times. The solids were then dried by standing overnight in the dry box. A portion of each solid was then slurried with the halide ion exchange agent employed in a beverage bottle in the dry box, the bottle was capped, removed from the box and heated with stirring at 100°C for the designated time. The bottle and contents were cooled to about 23°C and returned to the dry box. The resulting solids were recovered by vacuum filtration, washed with n-hexane and dried by standing overnight in the dry box. Specific examples : Comparison catalyst A: The bottle was charged with 19.05 g of unground MgCl₂·6H₂O which corresponds to a calculated anhydrous MgCl₂ of 8.95 g (0.094 mole), 35.8 mℓ (0.105 mole) of titanium tetra-n-butoxide (Ti(OBu)₄), 17.9 g (0.105 mole) of 4-phenylphenol and 15.0 g (0.1 mole) of ethyl benzoate. The mixture was heated for 1 hour at 100°C, cooled to about 23°C and treated dropwise with 25 mℓ (0.089 mole) of the EASC solution. The resulting precipitate was isolated, washed and dried to yield 15.0 g of a yellow-orange solid. 5.0 g of the yellow-orange solid was slurried in a mixture consisting of 50 mℓ (0.45 mole) of titanium tetrachloride, 10 mℓ (0.09 mole) of silicon tetrachloride and 40 mℓ (0.4 mole) of trichlorosilane. On a weight (mole) basis, TiCl₄ constituted 56 weight percent (48 mole %), HSiCl₃ constituted 35 weight % (43 mole %) and SiCl₄ constituted 10 weight % (9.6 mole%). The mixture was heated for 1 hour at 100°C and the solids isolated, washed and dried as described before yielding 4.9. g of a brown solid. Comparison catalyst B-1,2 was prepared in duplicate preparations. Each bottle was charged with 150 mℓ of xylene and 19.8 g of MgCl₂ containing 0.5 weight percent water as found by analysis. The composition corresponds to MgCl₂·0.03H₂O. On a dry basis, the MgCl₂ used amounted to about 19.7 g (0.21 mole). After stirring overnight at 23°C, each bottle was additionally charged with 25 g (0.15 mole) of 4-phenylphenol and 0.105 mole of Ti(OBu)₄. The reaction mixture was at 100°C for 15 minutes, 7.5 mℓ (0.1 mole) of ethyl benzoate (EB) was added and the mixture was heated an additional 45 minutes at 100°C. After cooling, each reaction mixture was treated dropwise with 125 mL (0.39 mole) of the EASC solution. The resulting precipitate was isolated, washed and dried to yield a yellow solid which weighed 34.7 g in preparation B-1 and 38.2 g in duplicate preparation 8-2. 20.0 g of each solid was slurried with sufficient mixture formed from 360 mℓ (3.28 moles) of TiCl₄, 270 mℓ (2.68 moles) of HSiCl₃ and 90 mℓ (1.19 mole) of SiCl₄ to provide a readily stirrable mixture (about 100 mℓ) and the mixture heated for 1 hour at 100°C. On a weight basis (mole) basis, TiCl₄ constituted 56 weight percent (46 mole %), HSiCl₃ constituted 32 weight % (37 mole %) and SiCl₄ constituted 12 weight % (17 mole %). The solids were isolated, washed and dried to yield a light purple solid weighing 17.1 g for preparation B-1 and 17.4 g for duplicate preparation B-2. Invention Catalyst C: The catalyst was prepared exactly as described for comparison catalysts B-1, B-2 with the exception that 22.6 g of MgCl₂ admixture was charged to the bottle. The admixture was prepared in a one quart (0.9 ℓ) Extra Heavy Duty Waring Blendor at about 2300 RPM for 5 minutes by charging the blender with 79.0 g of MgCl₂·0.08H₂O and 35.0 g of MgCl₂·6H₂O to form a calculated composition which can be empirically described as MgCl₂·1.1H₂O. Such a composition contains 82.8 weight percent MgCl₂ and 17.2 weight percent water. Thus, 22.6 g of MgCl₂·1.1H₂O is equivalent to 22.6 x 0.828 which gives 18.7 g equivalent of anhydrous MgCl₂ (0.20 mole). Powder X-ray diffraction spectra of the solids resulting from such a mixing reveal peaks characteristic of peaks present in the ASTM reference cards for MgCl₂, MgCl₂·2H₂O, and MgCl₂·4H₂O. The powder specimens for the XRD analysis were loaded onto aluminum holders and covered with Mylar film to exclude moisture and air. A Philips® XRG 3100 XRD apparatus was employed having a variable divergent slit, a 0.005 mm receiving slit, and a graphite monochromometer using CuKα rays produced by a 40 KV, 25 mA generator. In part 1 of the catalyst preparation, 32.2 g of a burnt-orange colored solid was isolated. In part 2 of the preparation, 20.0 g of the orange solid was contacted with a sufficient quantity of the TiCl₄ - HSiCl₃ - SiCl₄ mixture to form a stirrable mixture as for catalyst B-1, B-2, yielding after recovery 18.2 g of a purple solid. EXAMPLE II - PROPYLENE POLYMERIZATION A sample of each catalyst was tested in propylene polymerization for 1 hour at 70°C by employing a liquid full 1 liter stirred stainless steel reactor in the presence of 2.0 mmoles triethylaluminum (TEA) with 1.1 mmoles ethyl anisate (EA), premixed and 2.0 mmoles diethylaluminum chloride (DEAC) as cocatalyst system and hydrogen. Before each run the reactor was conditioned by filling it about ½ full with n-hexane dried with alumina and then heating it for about 10 minutes at over 100°C, e.g. 135°C while stirring. Heating and stirring were discontinued, the reactor contents were dumped, the reactor flushed with dry nitrogen and then purged with propylene vapor. While continuing the propylene purge, the catalyst system was charged to the reactor through an entry port in the following order: TEA·EA mixture, solid catalyst and DEAC. The 3 component cocatalyst system, in terms of moles, can be expressed approximately as TEA:EA:DEAC as 2:1:2. The port was then sealed and the propylene purge discontinued. The reactor was then filled aobut 2/3 full with liquid propylene 69 kPa and (10 psi) hydrogen added (measured as a 10 psi pressure drop from a pressurized, 325 mℓ container of hydrogen). Heating was started and after reaching a reactor temperature of 70°C the reactor was filled liquid full with propylene and maintained liquid full during the run by means of a propylene reservoir open to the reactor pressured with dry nitrogen, e.g. about 515 psia (3.55 MPa). Each run was terminated by discontinuing heating, cooling the reactor below about 60°C, discontinuing stirring and venting unreacted propylene through a dip tube containing a porous end into a dry, tared container. The reactor was then filled with fresh propylene and contents mixed by stirring for several minutes to wash the polymer. The wash propylene was then discharged to the tared container. The polymer in the reactor was then recovered, dried to remove any excess propylene and weighed to determine the yield. The polymer was slurried in an acetone solution containing a conventional antioxidant system for polypropylene and the solvent removed by heating the mixture for about 3 hours at 60°C in a vacuum oven. Propylene soluble polymer contained in the propylene in the tared vessel was determined by heating the vessel to dryness in a vacuum oven at 60°C. The vessel was weighed and the weight of residue remaining was then determined. Xylene soluble polymer and calculated productivity of the solid catalyst were determined as described in EP-A 0 060 443. The amount of each solid catalyst used and the results obtained are set forth in Table I. The results in run 4 of Table I show that a very active polymerization catalyst can be produced from a physical blend of MgCl₂ and MgCl₂·6H₂O which approximates the empirical formula MgCl₂·1.1H₂O. The catalyst produces about 17.2 kg of propylene insoluble polypropylene per g solid catalyst per hour at 70°C in the presence of 69 kPa (10 psi) hydrogen using conditions more exactly described in the example. Control run 1 results, the catalyst formed with MgCl₂·6H₂O, gave high total solubles (27.2 weight percent) and low productivity of aobut 1.2 kg propylene insoluble polypropylene per g solid catalyst. Control runs 2, 3, the catalyst formed with essentially anhydrous MgCl₂, show about double the productivity of control run 1 but did produce low total solubles ranging from about 5 to 7 weight percent.

Claims: A process for preparing a catalyst for the polymerization of olefins comprising reacting an admixture of magnesium dihalide with reactants comprising a benzoic acid ester and an alkoxytitanium compound to form a first catalyst component and then reacting said first catalyst component with an organoaluminum halide to form a solid product, and then reacting that solid product with a halogenating agent comprising a titanium halide to obtain said catalyst, characterized in that in said admixture of the first catalyst component a magnesium dihalide is used comprising (a) magnesium dihalide containing less than 0.5 moles of water per mole of magnesium dihalide and (b) magnesium dihalide containing more than 0.5 moles of water per mole of magnesium dihalide, whereas the weight ratio of (a) to (b) is such that the molar ratio of water to magnesium dihalide in said admixture is in the range of 0.5:1 to 2:1. The process of claim 1 characterized in that said magnesium dihalide comprises magnesium dichloride. The process of claim 1 or 2 characterized in that said alkoxytitanium compound comprises a compound of the formula Ti(OR)₄ wherein each R is individually selected from alkyl groups containing 1 to 20 carbon atoms. The process of any of the preceding claims characterized in that said organoaluminum halide comprises ethyl aluminium sesquichloride. The process of any of the preceding claims characterized in that a phenol is also employed in the production of said first catalyst component. The process of claim 5, characterized in that said phenol comprises 4-phenylphenol. The process of any of the preceding claims characterized in that said admixture is produced by stirring magnesium dichloride (a) and magnesium dichloride (b) having about 6 moles of water for each mole of MgCl₂ in a hydrocarbon liquid. The process of claim 7 characterized in that said admixture is prepared by mixing substantially anhydrous MgCl₂ and MgCl₂.6H₂O in a molar ratio of about 5:1. The process of claim 1 characterized in that said admixture comprises MgCl₂, MgCl₂.2H₂O, and MgCl₂.4H₂O. The process of any of the preceding claims characterized in that the molar ratio of water to MgCl₂ in said admixture is in the range of 1:1 to 2:1. The process of claim 10 characterized in that said molar ratio of water to MgCl₂ in said admixture is in the range of 0.75 :1 to 1.75 :1. The process of claim 11 characterized in that said molar ratio of water to MgCl₂ in said admixture is about 1:1. The process of any of the preceding claims characterized in that said ester comprises ethyl benzoate. The process of any of the preceding claims characterized in that said halogenating agent comprises titanium tetrachloride, HSiCl₃, and SiCl₄. The process of claim 14 characterized in that the respective molar ratios of TiCl₄, HSiCl₃, and SiCl₄ are about 4:3.3:1. The process of any of the preceding claims characterized in that said catalyst is prepared from magnesium dichloride, titanium tetra-n-butoxide, 4-phenyl-phenol, ethyl benzoate, ethyl aluminum sesquichloride, and a mixture of TiCl₄, HSiCl₃, und SiCl₄. The process of any of the preceding claims characterized in that said admixture of magnesium dihalide has been obtained by ball milling magnesium dihalides (a) and (b). Use of the catalyst as obtained in any of claims 1 to 17 for the homo- or copolymerization of olefins. Use of claim 18 characterized in that said olefin is propylene. Use of claim 18 or 19 characterized in that said catalyst is used in combination with an organometal cocatalyst.

Inventors: HAWLEY, GIL ROSS, INKROTT, KENNETH EARL, NOWLIN, OSCAR DEE, PIERCE, DALE EUGENE, VAUGHAN, JERRY LEWIS
Applicants: PHILLIPS PETROLEUM COMPANY
Application year: 1984
Main classification: C08F10
IPC codes: C08F4, C08F10