Pre-expanded particle of polyolefin and process for preparing the same

Abstract: A pre-expanded particle suitable for foaming in a mold comprising polyolefin which has a characteristic property that an inclination of slope line obtained on a graph when logarithmic values of melt tension of the polyolefin are plotted as ordinate and reciprocals of absolute temperature at which the melt tension is measured are plotted as ab­ scissa is less than 1,500 is provided. A foamed article produced from the pre-expanded particles has an excellent appearance, a flat surface and good mechanical strength, and is useful for wrapping material, insulating material, a container or a fender of cars. A process for preparing the above-mentioned pre-­ expanded particles is also disclosed.

Description: The present invention relates to a pre-expanded particle of ethylene polymer suitable for foaming within a mold which is able to close but unable to seal by heating with a heating medium such as steam and a process for preparing the same. Hitherto, there have been proposed various pre-expanded particles of polyolefin for foaming within a mold. However, in case of molding in industrial scale using a large size, multi-cavity mold, these pre-expanded particles, especially non-crosslinked pre-expanded particles have a number of drawbacks that the particles are not well fused together, that a surface of a molded article is not flat and that appearance of a molded article is not good, and thus, an adequate molded article, as a matter of fact, cannot be obtained. With respect to a process for preparing pre-expanded particles of polyolefin for foaming within a mold, a process including a step of heating the polyolefin particles containing a volatile foaming agent with, for example, steam is generally carried out. However, when the polyolefin particles are polyethylene particles, it is necessary to employ crosslinked polyethylene resin because if polyethylene is not crosslinked, a melt viscosity of the polyethylene resin is remarkably falling down at a temperature about a melting point thereof and it is very difficult to obtain pre-expanded particles which are less shrinked and have a high pre-expansion ratio. For preparing the crosslinked polyethylene resin, high-pressure process, low density polyethylene is widely used as a starting material because the high-pressure process, low density polyethylene can be easily and well crosslinked. A pre-expanded particle obtained from the high-pressure process, low density polyethylene is superior in pliability and bufferability or cushioning property. However, the pre-expanded particle is inferior in heat-resistance and is lacking solidity. Therefore, there can be used only the pre-expanded particle which has a relatively low pre-expansion ratio. Further, from the viewpoint of an industrial production, it is required to produce foamed articles constantly in a high yield which have an excellent appearance, a high expansion ratio and good mechanical properties by foaming process employing pre-expanded particles of polyolefin. The present inventors have studied in order to eliminate the above-mentioned drawbacks which are distinguished when the pre-expanded particles, especially pre-expanded particles of non-crosslinked polymer are employed for foaming within a mold, and we have reached the following knowledge; that is, in case of industrially producing a large size of foamed article, the characteristic properties such as appearance and mechanical strength of the obtained foamed article have a great relation to the characteristic properties such as viscoelasticity of polyolefin when melted, which is a fundamental component of pre-expanded particles of polyolefin used for foaming within a mold, and especially polyolefin having a small change of melt tension due to temperature variation is necessary particularly for producing a large size of foamed article of excellent appearance and good mechanical strength. Consequently, by minimizing the change of melt tension due to temperature variation, even if there is partially generated a difference in temperature among the locations of the pre-expanded particles filled in a mold when the mold charged with the pre-expanded particles is heated, a molded article which is uniform on the whole having excellent properties can be obtained. That means polyolefin employed as fundamental component in a preparation of the pre-expanded particles must have the same characteristic properties as described above. The difference in temperature among the locations of the pre-expanded particles in a mold which generates during heating, as a matter of course, becomes large when a large size of foamed article is molded. It is an object of the present invention to provide a pre-expanded particle suitable for foaming within a mold to produce a molded article having a higher expansion ratio, and to provide a pre-expanded particle prepared from non-crosslinked polymer without reducing a pliability and a cushioning property which are the characteristic properties of the conventional pre-expanded particles employing high-pressure process low density crosslinked polyethylene; particularly worthwhile when applied in molding a large size foamed article. It is an another object of the present invention to provide a process for preparing such particles. In accordance with the present invention, there is provided a pre-expanded particle of non-crosslinked linear low density ethylene polymer which is a copolymer of ethylene and α-olefin of C₄ to C₂₀, said copolymer having a melt index of 0.1 to 50g/10 min, a density of 0.910 to 0.940g/cm³ and a melting point of 110 to 123°C. In accordance with the present invention, there is also provided a process for preparing pre-expanded particles of non-crosslinked linear low density ethylene polymer which is a copolymer of ethylene and a α-olefin of C₄ to C₂₀, said copolymer having a melt index of 0.1 to 50g/10 min, a density of 0.910 to 0.940g/cm³ and a melting point of 110 to 123°C, which comprises: dispersing the ethylene copolymer particles and a volatile foaming agent into water in the presence of a dispersing agent in an autolave, heating the resulting dispersion with stirring up to a temperature in a following range: (a melting point of the copolymer -25)°C to (a melting point of the copolymer +10)°C, thereby the copolymer particles are impregnated with the foaming agent, and then, releasing the dispersion of the particles into an atmosphere having a pressure lower than that in the autoclave. A pre-expanded particle of the present invention has a high pre-expansion ratio and is superior in heat-resistance, mechanical strength, pliability and cushioning property, and can be employed for foaming within a mold to give a good foamed article. In accordance with a preferred embodiment of the invention, the ethylene polymer employed in the present invention has a characteristic property that an inclination of slope line obtained on a graph when logarithmic values of melt tension of the ethylene polymer are plotted as ordinate and reciprocals of absolute temperature at which the melt tension is measured are plotted as abscissa is less than 1,500. Hereinafter, the above-defined inclination is referred to as "an inclination of melt tension", and a meaning of the term of an inclination of melt tension described in Claims are defined as same as above. According to the descriptions in "Kobunshi Kako Kogaku" (Japanese translation of "Polymer Processing", by James M. McKelvey, published by John Wiley & Sons, Inc., New York, London, 1962), translated by Katsuhiko Itoh, published by Maruzen Kabushiki Kaisha, p. 37, Arrhenius stated that a relationship between log µ, wherein µ is a viscosity of the polymer, and reciprocal of absolute temperature is proportional in a range of 37.7°C (100 degree Fahrenheit). An inclination of melt tension is, preferably less than 1,000, more preferably less than 700. When an inclination of melt tension is not less than 1,500, it is difficult to control a pre-expansion ratio and cell size during a preparation of pre-expanded particles. In that case, even if pre-expanded particles of desired expansion ratio and cell size are obtained, the resulting foamed article is inferior in appearance and mechanical strength because in general the pre-expanded particles are not heated uniformly during foaming within a mold and they are partly shrinked or varied in shape due to overheating, or are not sufficiently expanded or fused together due to underheating. A reason why the pre-expanded particles are not uniformly heated during foaming within a mold consists in a fundamental structure of the used foaming apparatus and this drawback cannot be eliminated substantially. A foaming apparatus has a structure in which steam passes through the packed pre-expanded particles in a mold to obtain a foamed article and the steam flow more and more hardly according as the pre-expanded particles are expanded and fused together so as to be molded. The foaming apparatus has also a mechanism that when a pressure within a mold finally reaches to a pre-determined pressure, steam flow is shut. In case of employing a foaming apparatus for producing a larger size of foamed article, the pre-expanded particles packed in a mold are heated more ununiformly. Melt tension of the polyolefin is roughly decided at the time of preparing the polyolefin. The polyolefin having a low melt tension can be prepared by a number of processes such as that polymerization reaction is carried out with a specified polymerization catalyst, that a plurality of polymer resin having a different melt tension are mixed together, that polymerization reaction is carried out multi-stepwise to prepare a polymer resin consisting of components having a different melt tension and the obtained polymer resin is admixed and the like. According to the present invention, a copolymer of ethylene and α-olefin of C₄ to C₂₀ having 0.1 to 50 g/10 min of melt index measured according to JIS K 6760, 0.910 to 0.940 g/cm³ of a density and 110 to 123°C of a melting point is employed. When the melt index is less than 0.1 g/10 min, it is difficult to prepare the pre-expanded particles because a flowability of the polymer is not good during a preparation of the pre-expanded particles. On the other hand, when the melt index is more than 50 g/10 min, a flowability of the polymer is very high, and the obtained pre-expanded particles have low pre-expansion ratio and tend to shrink. When the density is less than 0.910 g/cm³, the polymer resin is so soft that the obtained pre-expanded particles are apt to shrink. On the other hand, when the density is more than 0.940 g/cm³, the polymer behaves like a high density polyethylene and a foaming procedure is difficult because of a reason described below. When the melting point is less than 110°C, the pre-expanded particles have insufficient heat-resistance. On the other hand, when the melting point is more than 123°C, the polymer behaves like a high density polyethylene and a foaming is difficult. Above-mentioned α-olefin having 4 to 20 carbon atoms includes, for instance, 1-butene, 1-pentene, 1-hexene, 3,3-dimethyl-1-butene, 4-methyl-1-pentene, 4,4-dimethyl-1-pentene, 1-octene, 1-decene, 1-dodecene, 1-tetradecene, 1-octadecene and the like. The α-olefin is employed alone or in admixture thereof. A content of a comonomer is varied according to a kind of the used α-olefin and is generally about 3 to about 12% by weight in the obtained copolymer so as to give a density of the copolymer in the range limited as above. Above-mentioned melting point is a peak temperature of the endothermic curve obtained by raising a temperature of a polymer sample at a rate of 20°C/min up to 200°C to melt, cooling it at a rate of 20°C/min down to room temperature to crystallize and then, re-heating it at a rate of 10°C/min with a differential scanning calorimeter (DSC). A process for preparing the above-mentioned pre-expanded particles is a second aspect of the present invention. In a pre-expanding process in which a mixture of water and polymer resin particles impregnated with a volatile foaming agent is released from a condition of high temperature and high pressure to an atmosphere of low pressure, a temperature of the polymer resin particles must be maintained in a small temperature range. Therefore, a polymer having a small temperature range in which the polymer has a suitable viscoelasticity for pre-expansion, for instance, a high density polyethylene can be employed in contrast with a conventional process for pre-expanding the particles with steam. However, in a foaming process in which a mold is charged with pre-expanded particles and heated, when usually employed ethylene polymer such as a high-pressure process, low density polyethylene or a high density polyethylene is used, foaming procedure is difficult because the heating range to be applied during foaming is very small. The particles are not fused together in case that a heating temperature is low and the particles are shrunk in case that the heating temperature is high. It was found that a copolymer of ethylene and α-olefin of C₄ to C₂₀ having 0.1 to 50 g/10 min of melt index, 0.910 to 0.940 g/cm³ of a density and 110 to 123°C of a melting point have a wide range of heating temperature to be applied during foaming, and that foaming procedure is easy to be carried out. Though the reason has not yet been confirmed, it is supposed to be the reason that a temperature range in which the pre-expanded particles are crystallized is wide as observed, for example, with DSC and that a temperature range in which the pre-expanded particles are expanded to a maximum extent in a mold is close to a temperature range in which the pre-expanded particles are fused together. Contrary to that a conventional process has a drawback that the pre-expanded particles are stuck to each other, particularly when a mixture of the polyolefin particles and water is released into an atmosphere of low pressure through at least one orifice having a diameter of 1.2 to 3 times a diameter of a sphere calculated from the volume of the polyolefin particle, that problem is completely solved, i.e. all of the obtained pre-expanded particles are separated piece by piece. The words "a diameter of a sphere calculated from the volume of the polyolefin particle" as used herein means a diameter of a sphere having the same volume as a volume of the polyolefin particle and hereinafter, it is referred to as "a sphere diameter". When a diameter of the orifice is too small, the particles can not pass through the orifice. On the other hand, when a diameter of the orifice is too large, several particles are released simultaneously into an atmosphere of low pressure and thus, the particles are caused to be agglomerated and stuck to each other at a time that they pass through the orifice or that they expand thereafter, and blocking is occurred. A shape of the orifice is generally a circle or an ellipse, but an orifice of a polygon can be employed, as occasion demands. An orifice size is determined from a diameter of the used polyolefin particle. Because a particle having a sphere diameter of about 0.5 to about 6 mm is generally used for a usual foaming within a mold, the orifice has an area of about 0.3 to about 250 mm². Consequently, a releasing speed is controlled by changing a number of the orifice. The orifice can be provided, for instance, by inserting a pressure-resistant orifice plate having at least one orifice behind a releasing valve with a flange. With respect to the third problem, i.e. a defect that pre-expansion ratio of the pre-expanded particles are not uniform, particularly when a temperature and a pressure in a vehicle such as an autoclave, preferably and a partial pressure of the foaming agent in a gas phase in the vehicle are kept constant at a time of releasing the aqueous dispersion of the olefin polymer particles into an atmosphere of low pressure, that defect is clearly eliminated. The temperature varies preferably within 5 degree centigrade during releasing the dispersion. The temperature can be easily controlled, for instance, by using a usually employed autoclave having a jacket. The pressure in an autoclave falls down according as a mixture of particles and water is released because the upper space in an autoclave becomes large, thereby the pre-expansion ratio of the released particles was decreased. Thus, a pressure in an autoclave is preferably kept constant during releasing the aqueous dispersion of the particles. When the releasing procedure is long continued, introducing nitrogen gas or air under pressure into an autoclave is not so effective to keep the pressure in an autoclave constant and thus, pre-expansion ratio of the pre-expanded particles are largely decreased. This is because a content of a foaming agent is lowered owing to a volatilization of the foaming agent from the particles in proportion to a partial pressure of the foaming agent in a gas phase in the autoclave falls down. Thus, more preferably a partial pressure of the foaming agent in a gas phase in the autoclave, as well as a total pressure in the autoclave, is kept constant during releasing operation. This is carried out, for example, by decreasing a volume of the upper space in the vehicle according as the space increases to keep a volume of the upper space constant, or by introducing a volatile foaming agent as well as nitrogen gas or air into the vehicle from outside according as the upper space increases. However, above-mentioned methods are effective only when the upper space in the vehicle is not saturated with a vapour of the foaming agent and a partial pressure of the foaming agent in the gas phase is decreased during releasing the dispersion. Consequently, when the upper space is saturated with the vapour of the foaming agent, for instance, when excess foaming agent is present as liquid in the vehicle, the introduction of the foaming agent is not necessary. The latter method is prefer to the former method, because the former method requires more complicated process. The latter method can be carried out, for instance, by introducing the liquid volatile foaming agent continuously or intermittently via a controlling valve with adjusting the introduced amount to keep a total pressure in the vehicle constant. Thus, the pre-expanded particles, pre-expansion ratio of which is nearly close to each other, can be obtained even when the releasing operation is long continued. The words "to keep a pressure constant'' described in the specification and Claims means to control and maintain a pressure in a pressure range in which the pre-expanded particles having pre-expansion ratio of allowable variation are obtained. According to the present invention, various volatile foaming agents having a boiling point of -50 to 120°C can be employed. Examples of such a foaming agent are, for instance, an aliphatic hydrocarbon such as propane, butane, pentane, hexane, heptane, cyclopentane or cyclohexane; a halogenated hydrocarbon such as monochloromethane, dichloromethane, monochloroethane, trichloromonofluoromethane, dichlorodifluoromethane, dichloromonofluoromethane, trichlorotrifluoroethane or dichlorotetrafluoroethane and the like. The foaming agent can be employed alone or in admixture thereof. A used amount of the volatile foaming agent is decided according to a kind thereof, a desired pre-expansion ratio of the obtained pre-expanded particle, a ratio of a volume of the polymer resin and a volume of the upper space in the vehicle. In general, the foaming agent is used in 5 to 50 parts by weight to 100 parts by weight of olefin polymer particles. Dispersing agent is used in a little amount at a time of dispersing the polyolefin particles into water in the process of the present invention to inhibit a flocculation of the particles during heating. Examples of such a dispersing agent is, for example, a water-soluble polymer such as polyvinylalcohol, methylcellulose or N-polyvinylpyrrolidone; powders of a water-insoluble inorganic compound such as calcium phosphate, magnesium pyrophosphate, zinc carbonate, titanium oxide or aluminum oxide and the like. The water-insoluble inorganic compound is preferred to the water-soluble polymer because the latter has a probe of environmental pollution. However, when the inorganic powders are used in much amount, pre-expanded particles are not well fused together at a time of foaming. So, a little amount of an anionic surfactant such as sodium alkylbenzenesulfonate including sodium dodecylbenzenesulfonate or the like, sodium α-olefinsulfonate or sodium alkylsulfonate is preferably used with the inorganic powders to decrease the used amount of the powders. In this case, the powders of a water-insoluble inorganic compound are used in 0.1 to 3 parts by weight and the anionic surfactant is used in 0.001 to 0.5 part by weight to 100 parts by weight of the polyolefin resin. According to the present invention, aqueous dispersion of the polyolefin particles are heated into a temperature in a following range: (a melting point of the polyolefin -25)°C to (a melting point of the polyolefin +10)°C preferably (a melting point of the polyolefin -20)°C to (a melting point of the polyolefin +5)°C. The temperature can be varied within the above-mentioned temperature range according to a kind of used volatile foaming agent and a desired pre-expansion ratio. For example, as to an olefin polymer having a melting point of 120°C, heating temperature can be selected from a range of 95 to 125°C. When a heating temperature is less than the above-mentioned temperature range, an expansion ratio is largely decreased. On the other hand, when a heating temperature is more than the temperature range defined above, the cells in the obtained pre-expanded particles are collapsed. The thus obtained pre-expanded particle of ethylene polymer of the present invention can be employed in a foaming process, for instance, a process that the obtained pre-expanded particles are, just as they are, or after aging or drying for a suitable time, or after giving them additional expansion ability, filled in a mold, and the pre-expanded particles are heated with a heating medium such as steam up to about 105 to about 130°C for about 3 sec to about 2 min to give a molded article. A method for further giving the pre-expanded particles additional expansion ability can be carried out, for instance, by introducing a gas such as nitrogen gas or air under pressure into the cells in the particles to elevate a pressure in the cells, or by pressing the pre-expanded particles with a compressed air to elevate a pressure in the cells. It is also effective to compress a mold charged with the pre-expanded particles made expansible or not before foaming. The pre-expanded particles of ethylene polymer of the present invention can also be prepared by other conventional process. The pre-expanded particles of ethylene polymer of the present invention are not stuck together at all and have uniform expansion ratio, and can be industrially employed for a conventional foaming process with ease because they have a wide range of heating temperature. The pre-expanded particles of the present invention can give a large sized foamed article having a flat surface and a good mechanical strength. A foamed article produced from the pre-expanded particles of the present invention has an excellent appearance and a uniform density in which the pre-expanded particles are well fused together. The foamed article has a good cushioning property as similar to a conventional molded article of high-pressure process, low density crosslinked polyethylene, an excellent heat-resistance and a toughness, and are useful for wrapping material, insulating material, a container or a fender of cars. The present invention is more particularly described and explained by means of the following Examples, in which all parts are parts by weight unless otherwise noted. It is to be understood that the present invention is not limited to the Examples. Example 1 A 1000 l autoclave equipped with a stirrer was charged with 100 parts (225 kg) of particles of a copolymer of ethylene and 4-methyl-1-pentene having a melting point of 120°C, a density of 0.920 g/cm³, MI of 2.1 g/10 min and a sphere diameter of about 2 mm, 0.5 part of basic powdered calcium phosphate and 0.006 part of sodium dodecylbenzenesulfonate as dispersing agent and 300 parts of water. After stirring the mixture, to the dispersion thus obtained was added 30 parts of dichlorodifluoromethane with stirring, and the temperature of the dispersion was raised to 117°C. A pressure in the autoclave at that time was 27 kg/cm² · G. By opening a releasing valve provided at a lower part of the autoclave, the aqueous dispersion of the copolymer particles was released into an atmosphere of normal pressure through a round orifice having 4 mm in a diameter in an orifice plate provided behind the valve to give pre-expanded particles. The releasing operation was carried out for half an hour while a pressure in the autoclave was kept constant at 27 kg/cm² · G by introducing liquefied dichlorodifluoromethane under pressure into the autoclave with controlling the introduced amount through an injection valve. The obtained pre-expanded particles were not stuck to each other and have average pre-expansion ratio of 26.7. Almost all the pre-expansion ratio were in a ragne of 24 to 28. Decrease of the pre-expansion ratio was not observed during the latter half of the releasing operation and the pre-expansion ratio of the obtained pre-expanded particles were all nearly close to each other. After drying the pre-expanded particles at 60°C for 24 hrs, the particles were pressed with compressed air of 60°C and 20 kg/cm² · G for 2 hrs to immerse air into the cells of the pre-expanded particles. A mold of 290 mm × 270 mm × 50 mm was charged with thus treated particles and the mold was heated with steam of 1.5 kg/cm² · G for 15 sec to give a foamed article. The obtained foamed article was an excellent article having a flat surface and a density of 0.024 g/cm³, in which the pre-expanded particles were well fused together. Characteristic properties of the foamed article and a molded article of high-pressure process, low density, crosslinked polyethylene (commercially available from Kanegafuchi Kagaku Kogyo Kabushiki Kaisha under a commercial name of "Eperan") are shown in Table 1. As clearly understood from Table 1, a foamed article having 38 of expansion ratio of the present invention has a solidity and a cushioning property of the same rank as a molded article of crosslinked polyethylene having 27 of expansion ratio. A foamed article of Example 4 A molded article of crosslinked polyethylene Density (g/cm³) 0.024 0.034 Expansion-ratio 38 27 Solidity (kg/cm²) 0.7 0.7 Minimum static cushioning coefficient (C min) 3.4 3.6 Comparative Example 1 In a 4 l autoclave equipped with a stirrer 100 parts (900 g) of high-pressure process, low density polyethylene particles having particle size of about 2 mm (Experimental No. 1) or high density polyethylene particles having particle size of about 2 mm (Experimental No. 2) shown in Table 2, 0.5 part of basic powdered calcium phosphate and 0.006 part of sodium dodecylbenzenesulfonate as a dispersing agent were dispersed into 300 parts of water. After 30 parts of dichlorodifluoromethane was added to the obtained dispersion with stirring, the temperature of the dispersion was raised to the temperature shown in Table 2. While maintaining a pressure in the autoclave at that time by introducing nitrogen gas under pressure into the autoclave, the aqueous dispersion was released into an atmosphere of normal pressure through a round orifice having 4 mm in diameter provided in an orifice plate. The pre-expansion ratio of thus obtained pre-expanded particles of the low density polyethylene and the high density polyethylene were shown in Table 2. The foaming procedure of Example 1 was repeated except that the obtained low density and high density polyethylene particles were used. As a result, good foamed articles could not be produced as shown in Table 2. High-pressure process, low density polyethylene High density polyethylene Melting point (°C 109 131 Density (g/cm³) 0.922 0.950 MI (g/10 min) 1.5 2.5 Heating temperature (°C) 103 125 Pressure in the autoclave (kg/cm² · G) 22.5 26.2 Pre-expansion ratio 30.0 26.1 Molding property Any foamed article could not be produced, since the packed pre-expanded particles were immediately shrinked when the particles were heated with steam Comparative Example 2 The procedure of Example 1 was repeated except that the aqueous dispersion was released through a releasing valve having 25 mm in inner diameter instead of the orifice. The obtained pre-expanded particles included many agglomerated particles which had 2 to 20 pre-expanded particles stuck to each other. Those pre-expanded particles could not be used for the further molding process. Comparative Example 3 The procedure of Example 1 was repeated except that, at the time of releasing the dispersion, compressed nitrogen gas was introduced instead of liquefied dichlorodifluoromethane. As a result, the pre-expansion ratio of the obtained pre-expanded particles was changed from 26.7 to 15.3 during the releasing procedure, i.e. 30 mins. Example 2 The procedure of Comparative Example 1 was repeated except that the copolymer particles of ethylene and the monomers as shown in Table 3 having a sphere diameter of about 2 mm to produce foamed articles. The obtained foamed articles were not shrinked at all and had an excellent molding property, i.e. the pre-expanded particles were completely fused together. The results are shown in Table 3. Experimental No. 1 2 3 4 Comonomer 4-methyl-1-pentene 4-methyl-1-pentene 1-butene 1-butene Melting point (°C) 122 123 120 122 Density (g/cm³) 0.930 0.935 0.922 0.930 MI (g/10 min) 2.1 2.1 0.6 0.6 Heating temperature (°C) 118 119 117 120 Pressure in the autoclave (kg/cm² · G) 28 30 27 27 Pre-expansion ratio 26.1 20.4 26.7 22.3

Claims: A pre-expanded particle of noncrosslinked linear low density ethylene polymer which is a copolymer of ethylene and α-olefin of C₄ to C₂₀, said copolymer having a melt index of 0.1 to 50g/10 min, a density of 0.910 to 0.940g/cm³ and a melting point of 110 to 123°C. The pre-expanded particle of Claim 1, wherein the non-crosslinked linear low density ethylene polymer has an inclination of the line obtained by plotting the logarithmic values of melt tension as ordinate and reciprocals of the absolute temperature at which the melt tension is measured as abscissa on a graph, of less than 1,500. The pre-expanded particle of Claim 1, wherein the non-crosslinked linear low density ethylene polymer contains 3 to 12% weight of the α-olefin. A process for preparing pre-expanded particles of non-crosslinked linear low density ethylene polymer which is a copolymer of ethylene and a α-olefin of C₄ to C₂₀, said copolymer having a melt index of 0.1 to 50g/10 min, a density of 0.910 to 0.940g/cm³ and a melting point of 110 to 123°C, which comprises: dispersing the ethylene copolymer particles and a volatile foaming agent into water in the presence of a dispersing agent in an autoclave, heating the resulting dispersion with stirring up to a temperature in a following range: (a melting point of the copolymer -25)°C to (a melting point of the copolymer +10)°C, thereby the copolymer particles are impregnated with the foaming agent, and then, releasing the dispersion of the particles into an atmosphere having a pressure lower than that in the autoclave. A process of Claim 4, wherein a temperature and a pressure in the autoclave are kept constant at a time of releasing the dispersion of the copolymer particles into an atmosphere having a pressure lower than that in the autoclave. A process of Claim 4, wherein a temperature and a pressure in the autoclave and a partial pressure of the foaming agent in a gas phase in the autoclave are kept constant at a time of releasing the dispersion of the copolymer particles into an atmosphere having a pressure lower than that in the autoclave. A process of Claim 4, wherein the dispersion of the copolymer particles was released into an atmosphere having a pressure lower than that in the autoclave through at least one orifice having a diameter of 1.2 to 3 times a diameter of a sphere calculated from the volume of the particle.

Inventors: KENICHI SENDA, KYOICHI NAKAMURA, MASAO ANDO, TATEHIKO NISHIDA, KENICHI, SENDA, KYOICHI, NAKAMURA, MASAO, ANDO, TATEHIKO, NISHIDA
Applicants: KANEGAFUCHI CHEMICAL IND, KANEGAFUCHI KAGAKU KOGYO KABUSHIKI KAISHA
Application year: 1984
Main classification: C08L23
IPC codes: C08J9