MULTILAYER PRINTED CIRCUIT BOARD STRUCTURE

Abstract: A composite printed circuit board structure including multiple layers of graphite interleaved with layers of a dielectric material, such as a polyletraflouroethylene (PTFE) and woven glass laminate. Some of the dielectric layers are copper clad, and at least some of the graphite layers are positioned in close proximity to the copper cladding layers, to provide good heat dissipation properties. The PTFE provides a desirably low dielectric constant and the graphite also provides good mechanical strength and a low or negative coefficient of thermal expansion, to permit match­ ing of the coefficient with that of chip carriers used to mount components on the circuit board.

Description: This invention relates generally to printed circuit boards, according to the first part of claim 1, as known e.g. from US-A-4318954, and more particularly, to printed circuit boards on which microelectronic components or chips are mounted. One desirable characteristic of printed circuit boards used for this purpose is that they should be mechanically stable under conditions of varying temperature. This is particularly important in circuit boards used to support microelectronic components housed in chip carriers. Chip carriers are usually fabricated from a ceramic material, such as aluminum oxide, and are produced in the form of a hermetically sealed package for each chip. Bonded leads are brought out from the chip to the edges of the chip carrier, and the carrier is then usually soldered, by its leads, directly to a circuit board. The principal advantage of this structure is a significantly higher circuit density. Also, the use of shorter and more uniform lead lengths results in improved speed and impedance characteristics. Another consideration is that the use of chip carriers substantially reduces the overall cost of a circuit package. Package size reductions as high as a five-to-one ratio can be obtained, compared with an equivalent dual in-line package construction. A major drawback to the use of chip carriers is that the coefficient of thermal expansion of aluminum oxide, the most commonly used chip carrier material, is approximately one-half the coefficient of thermal expansion for glass/epoxy laminates typically used in the manufacture of circuit boards. When the resulting structure is exposed to any significant range of temperatures, the thermal cycling of the structure can crack soldered joints and render the circuit inoperative. One solution to this problem is to use an intermediate member between the chip carrier and the circuit board. The circuit board is sometimes referred to as a mother board, and the intermediate member as a baby board. The intermediate member may also take the form of a hybrid package on which the chip carrier is mounted. Another technique is to use a complaint lead structure between the chip carrier and the circuit board, although this clearly increases the cost of the package and results in inherently long lead lengths. Accordingly, an ideal circuit board should have a coefficient of thermal expansion that closely matches that of chip carriers mounted on the board. If there is a substantial mismatch in coefficients of thermal expansion, the chip carrier may break loose from the board, or the electrical connections may be damaged. Another difficulty that has arisen as larger numbers of components are mounted on circuit boards, is that the heat produced by the components must be dissipated in some manner, whether by conduction through the circuit board or by radiative, convective, or forced-air cooling. Since the principal materials used in circuit boards are insulators, the boards themselves have traditionally played no significant role in dissipating heat from the components that they support. A third factor in the design of circuit boards is that they should ideally be of a material with a relatively low dielectric constant, to enhance the board's ability to propagate signals over relatively long distances. Some materials, such as polytetraflouroethylene (PTFE) have good dielectric properties but an undesirably high coefficient of thermal expansion. Kevlar (trademark of E.I. du Pont de Nemours & Co., Inc.) has a negative coefficient of thermal expansion, and may be used to reduce the average coefficient of thermal expansion in a composite circuit board structure. However, Kevlar is a poor thermal conductor, and therefore does nothing to enhance the thermal conduction properties of the board. US Patent No. 4,318,954 issued to Jensen, proposed the use of a single thick layer of graphite reinforced with a resin, to adjust the coefficient of thermal expansion of a circuit board. The board disclosed in this patent has a surface fabricated from conventional fibre reinforced plastic laminates such as glass fibre reinforced epoxy laminates which is secured to a large bulk of graphite, such that the composite expansion coefficient approaches that of the graphite alone. However, the Jensen patent does not provide any solution to the increasing problem of heat dissipation. It will be appreciated from the foregoing that there is an ever increasing need for a multilayer printed circuit board structure that addresses these problems. Specifically, the ideal circuit board structure should have low dielectric properties, a low or negative thermal coefficient of thermal expansion, in the preferred embodiment, close to or equal to the coefficient of thermal expansion of Al₂O₃ , and good thermal conduction properties to enhance heat conduction from devices mounted on the board. The present invention satisfies all of these needs. SUMMARY OF THE INVENTION The present invention resides in a multilayer printed circuit board having a desired coefficient of thermal expansion said circuit board comprising: a plurality of layers of a dielectric material, at least some of the surfaces of said layers being coated with patterned conductive metal as dictated by the nature of the components supported on the circuit board; and a layer of graphite interleaved between said layers of dielectric material, and wherein said graphite is bonded to adjacent layers by a layer of insulating adhesive whereby the layer of adhesive serves the additional purpose of electrically separating conductive metal from the graphite characterised in that there are a plurality of layers of graphite at least some of which are positioned in close proximity to conductive layers, to provide good thermal conduction for the dissipation of heat generated in the components mounted on the board; and in that said graphite layers are selected to provide a desired composite coefficient of thermal expansion and are positioned across the thickness of the board in a symmetrical manner, to minimize bowing of the board in conditions of varying temperature. The graphite layers in the structure of the invention take the form of woven sheets of fabric that have been impregnated with a bonding material, such as an epoxy resin. An alternative preferred construction when high modulus carbon fiber material is used takes the form of alternative layers of unidirectional fibers, the fibers in each layer being more or less parallel to one another and the alternate layer fiber directions being arranged to provide stiffness and strength along the major axes of the structure of the invention. Each graphite sheet is separated from adjacent conductive or dielectric layers by a thin layer of insulating adhesive material. The adhesive serves both to bond the two layers together and to electrically insulate the conductive layers from the graphite. Holes may be formed through the graphite, either for plated-through connectors between conductive layers, or to accommodate mounting screws used to secure the board structure to a housing. At each of the predetermined hole positions, the graphite sheets are pre-drilled and the holes are filled with a bonding adhesive material, such as the epoxy resin used to form the sheets. When via holes or mounting screw holes are subsequently drilled through the composite board, a drill of smaller diameter is used. In this way, each hole through a graphite layer has an annular sheath of insulating material around it, and no inadvertent connection is made between conductive layers. However, the insulating material around the mounting screws is thin enough to provide only a small resistance to the flow of heat. Preferably, the conductive metal used in the structure is copper and the dielectric material is a polytetraflouroethylene (PTFE) material. It will be appreciated from the foregoing that the present invention represents a significant advance in the field of multiple-layer printed circuit boards. In particular, the invention provides a circuit board in which the coefficient of thermal expansion may be substantially reduced, and matched to that of an adjacent chip carrier. Moreover, the board of the invention has good thermal conductively properties, excellent mechanical strength, and does not sacrifice dielectric performance. Other aspects and advantages of the invention will become apparent from the following more detailed description, taken in conjunction with the accompanying drawings. BRIEF DESCRIPTION OF THE DRAWINGS FIGURE 1 is a simplified perspective view showing four chip carriers mounted on a circuit board; FIG. 2 is a fragmentary cross-sectional view of a multilayer circuit board made in accordance with the invention; and FIG. 3 is a fragmentary view showing how via holes and mounting screw holes are formed in the board of the invention. DESCRIPTION OF THE PREFERRED EMBODIMENT As shown in the drawings for purposes of illustration, the present invention is principally concerned with multilayer printed circuit boards. There are three desirable properties of circuit boards, especially those used to support electronic components on ceramic chip carriers. First, the board should have a relatively low dielectric constant, to facilitate transmission of signals over relatively long distances. Second, the coefficient of thermal expansion of the board should be controllable to some degree, to match the coefficient of adjacent materials, such as chip carriers. Finally, the board should ideally be a sufficiently good thermal conductor to assist in the dissipation of heat generated in mounted components. Unfortunately, these three desired characteristics cannot be found in a single material. FIG. 1 shows a multilayer circuit board, indicated by reference numeral 10, used to support four chip carriers 12. The chip carriers 12 have leads brought out to their edges and extending around beneath the carriers. The leads are then attached to the circuit board 10 by a reflow soldering process in which the leads are secured to respective pads 14 on the top of the circuit board 10. Any mismatch between the coefficients of thermal expansion of the chip carriers 12 and the board 10 can result in damage to the electrical chip connections. In accordance with the invention, and as shown diagrammatically in FIG. 2, the circuit board 10 includes a plurality of layers of graphite 16 interleaved between layers 18 of a dielectric material that includes polytetraflouroethylene (PTFE). Some of the layers 18 are copper coated, as indicated at 20. The PTFE layers 18 provide the basic dielectric material of the board 10, and the graphite layers 16 provide both thermal conductivity and control of thermal coefficient of expansion. The graphite layers 16 are bonded to adjacent copper layers 20 or PTFE layers 18 with a suitable adhesive layer 22. For the copper-to-graphite bond, the adhesive 22 also functions as an electrical insulator, to avoid having the graphite act as an unwanted electrical connection between portions of the copper layers. The adhesive layers 22 are, however, so thin that they offer little resistance to the flow of heat between the copper and the graphite. The graphite layers 16 are formed from fibrous carbon material, such as "Thornel" P100 or P75S, made by Union Carbide Corporation, Carbon Products Division, Chicago, Illinois 60606. The graphite or carbon yarn is woven into a cloth, which is then impregnated with a bonding material, such as an epoxy resin. In an alternative preferred embodiment which incorporates high modulus carbon fibers, the carbon fibers are arranged in each layer so that they are more or less parallel to one another and are not woven into cloth, such weaving may result in damage to the brittle high modulus fibers. Alternate layers are then arranged so that the combination of fiber directions in the layers provides the required rigidity and strength along the major axes of the circuit board. The resin-impregnated graphite cloth cures to a hard, rigid sheet, with practically planar surfaces. Hole locations, such as indicated at 30 in FIG. 3, are predetermined, and the graphite sheets are pre-drilled with oversized holes 32, which are immediately filled with more resin material. Then the graphite boards 16 are ready to be laminated with the PTFE layers 18, using the adhesive 22. Prior to lamination, the copper layers 20 are appropriately patterned as dictated by the design of circuits mounted on the board. After lamination, holes are made through the entire board 10, but using a smaller diameter drill than the one used to pre-drill the graphite layers 16. Thus, each newly formed hole 34 is surrounded by an annular sheath of insulating material, which serves to electrically separate the graphite layers 16 from the copper layers 20, but is thin enough to permit transmission of heat from the copper. The number and thickness of the graphite layers 16 are selected to provide a desired effect on the composite coefficient of thermal expansion of the board 10. In addition, the graphite layers 16 are disposed in a symmetrical fashion across the thickness of the board 10, to minimize the possibility of bending of the board during temperature changes. The coefficient of thermal expansion of the graphite layers 16 is close to zero after impregnation with epoxy renin. The coefficient of thermal expansion for copper is 16.92x10 -6 m/m/°C(9.4 x 10 -6 in/in/°F) , and the coefficient for copper-clad PTFE sheets is much higher. The goal in selecting the number and thickness of the graphite layers 16 is match the coefficient of thermal expansion to that of the chip carrier material. The most common material, aluminum oxide, has a coefficient of thermal expansion 5.994m/m/°C(3.33 x 10 -6 in/in/°F) . The PTFE layers 18 may be part of a suitable material, such as CU-CLAD 233, manufactured by the Electronics Products Division of the 3M Company, St. Paul, Minnesota 55144. This material is a laminate of PTFE and woven glass. It has a low dielectric constant of 2.33, but a relatively high coefficient of thermal expansion. Appropriate selection and positioning of the graphite layers 16 results in a composite coefficient of thermal expansion that closely matches that of the chip carrier material. One of the principal advantages of the use of graphite in the circuit board structure is that it serves as a good conductor of heat, which normally can flow from the mounted components through the copper layers of the board, through mounting bolts, and thence to a housing or other heat sink. In the structure of the invention, the graphite layers 16 provide a parallel path for the flow of heat, and thereby improve the heat dissipation characteristics of the circuit package. Another advantage of the use of graphite is that it is mechanically extremely strong. The tensile modulus of elasticity for single yarns of the graphite specified above is in the range of 517.5-690x10 3 MPa(75-100 x 10 6 p.s.i) , but this is naturally reduced when the graphite is impregnated with resin. Nevertheless, the use of graphite greatly strengthens the circuit board structure. It will be appreciated from the foregoing that the present invention represents a significant advance in the field of multilayer printed circuit boards. In particular, the use of multiple layers of graphite in a circuit board is used to control the coefficient of thermal expansion and to provide a supplementary thermal path for the dissipation of heat from components mounted on the board. The base material used in the board is PTFE with a desirably low dielectric constant.

Claims: A multilayer printed circuit board having a desired coefficient of thermal expansion said circuit board comprising: a plurality of layers of a dielectric material, at least some of the surfaces of said layers being coated with patterned conductive metal as dictated by the nature of the components supported on the circuit board; and a layer of graphite interleaved between said layers of dielectric material and wherein said graphite layer is bonded to adjacent layers by a layer of insulating adhesive whereby the layer of adhesive serves the additional purpose of electrically separating conductive metal from the graphite characterised in that there are a plurality of layers of graphite at least some of which are positioned in close proximity to conductive layers, to provide good thermal conduction for the dissipation of heat generated in the components mounted on the board; and in that said graphite layers are selected to provide a desired composite coefficient of thermal expansion and are positioned across the thickness of the board in a symmetrical manner, to minimize bowing of the board in conditions of varying temperature. A multilayer printed circuit board as set forth in claim 1, wherein: said graphite layers are formed from woven sheets of graphite impregnated with a bonding material. A multilayer printed circuit board as set forth in claim 1, wherein: said graphite layers are formed from unidirectional fibers of graphite impregnated with a bonding material. A printed circuit board as set forth in claim 2 or 3, wherein: said bonding material is a plastic bonding material. A printed circuit board as set forth in claim 4, wherein: said plastic bonding material is an epoxy resin. A multilayer printed circuit board as set forth in any preceding claim, wherein: said conductive metal is copper; and said layers of dielectric material include a polytetraflouroethylene (PTFE) material. A method of fabrication of a multilayer circuit board, comprising the steps of: forming a plurality of solid graphite sheets; etching a plurality of copper-clad sheets of polytetraflouroethylene (PTFE) and woven glass with predetermined circuit patterns; positioning the graphite layers between the etched circuit sheets in a symmetrical manner as to the thickness of the multilayer board, so as to form this multilayer circuit board composite with a selected coefficient of thermal expansion, and laminating the plurality of graphite sheets and the copper-clad sheets together with additional sheets of PTFE and woven glass. A method as set forth in claim 7 wherein said step of forming a plurality of solid graphite sheets comprises impregnating a layer of unidirectional graphite fibers with a resin. A method as set forth in claim 7 wherein said step of forming a plurality of solid graphite sheets comprises impregnating a woven graphite cloth with a resin. A method as set forth in any one of claims 7-9 wherein said laminating step includes: applying an insulating adhesive layer between adjacent layers, whereby the adhesive layer also electrically insulates the graphite and copper cladding materials. A method as set forth in any one of claims 7-10, and further including the steps of: pre-drilling the graphite sheets, prior to said laminating step, at predetermined locations for via holes and mounting screw holes; filling the pre-drilled holes with a resin; drilling the laminated board at the predetermined hole locations, using a smaller diameter drill, to leave an annular sheath of insulating resin around each hole through a graphite sheet.

Inventors: LEIBOWITZ, JOSEPH DAVID
Applicants: TRW INC.
Application year: 1984
Main classification: H05K3
IPC codes: B32B15, H05K1, H05K3