METHOD OF MANUFACTURING A SEMICONDUCTOR DEVICE HAVING SMALL DIMENSIONS

Abstract: In a method for manufacturing a semiconductor device having small dimensions, a semiconductor substrate (10) is provided with a gate oxide layer (13), a heavily doped polysilicone electrode (14') and an oxide-nitride mask (15', 16'). After a light doping to form doped regions (21, 22) the substrate is subjected to thermal oxidation at a temperature in the range 700-750 degrees to form a relatively thick oxide layer (23) on the polysilicon gate (14') and a relatively oxide layer (26) on the adjacent substrate region. The oxide-nitride mask (15', 16') is then removed and the substrate subjected to further doping, the sidewall oxide layer (23) protecting the underlying substrate from further doping. The sidewall oxide layers (23) serve to prevent electrical shorts between individual tungsten layers (30, 31) provided on the polysilicon gate (14') and adjacent substrate. Sidewall oxide layers (24, 25) are also formed over polysilicon interconnect conductors (14'', 14''') and similarly prevent shorts between tungsten layers (32, 33) provided thereover.

Description: Method of manufacturing a semiconductor device having small dimensions Technical Field This invention relates to a method of manufacturing a semiconductor device including a substrate having a first metal conductor overlying a polysilicon conductor, and a second metal conductor located adjacent said first metal conductor. Background Art In recent years there has been a continuing trend toward the development of semiconductor devices having extremely small dimensions of the order of 1 micron or less to increase the packing density of devices on an integrated circuit chip. Particularly in the area of MOS memories, gate dimensions and associated interconnect dimensions continue to be scaled down to increase not only the circuit density on the chip, but also to improve the circuit perform¬ ance (by increased operational speeds, etc.). One problem encountered in manufacturing small geometry MOS devices relates to electrical shorts between interconnecting conductors such as the electrical conductors contacting the self-aligned gate, source and drain. To elaborate on this point, in the fabrication of silicon gate MOS devices after forming the polysilicon gate structure and the source- drain regions in correspondence with the gate struc¬ ture, a metal such as tungsten is selectively deposit¬ ed over the polysilicon gate and the source-drain regions of the silicon substrate to provide low re- sistance conductor lines. However, the metal deposit¬ ed in this manner tends to create an electrical short with the metal deposited over the adjacent source- drain regions. A similar shorting problem exists between adjacent closely-spaced polysilicon intercon- nect lines. OMPI WIPO .fr A method of the kind specified is known from U.S. Patent Specification No. 4,330,931, which dis¬ closes a process for forming a self-aligned silicon gate n-MOSFET having n- source-drain extensions. In this process after forming the polysilicon gate having a nitride overhang mask, arsenic ions are implanted to form the n+ source and drain. During this implant step, lightly doped source-drain extensions are also formed due to blocking of some ions by the nitride overhangs. The structure is then subjected to a high temperature (920 degrees C) oxidation step to grow a 1000 Angstroms thick oxide- over the sides of the polysilicon gate and to thicken an oxide layer on the substrate above the source-drain regions. The oxide over the n + source-drain regions is then damaged by argon ion bombardment. During this oxide damaging step, the oxide over the n~ source-drain regions and the sidewalls of the gate is protected by the nitride mask. The damaged oxide and the nitride mask are then removed and a tungsten layer is selectively deposited over the exposed n + source-drain regions and the gate. The known process requires an oxide damaging step which is not only an extra process step, but also requires very careful control lest the source-drain areas may " also be damaged. Both of these requirements are particularly disadvantageous from a high volume manufacturing standpoint. Another disadvantage is that this process requires forming a nitride overhang mask atop the polysilicon by undercutting the polysilicon. This is a critical process step and is very difficult to control. Further, any variation in undercutting the polysilicon may cause possible damage to the sidewall oxide during argon ion bombardment. Yet another disadvantage of the known process is that this process appears to be limited to forming a polysilicon gate sidewall oxide having a thickness of only 1000 Angstroms. Consequently, upon selective deposition of tungsten over the polysilicon gate and the source-drain areas, adjacent tungsten strips may short each other out due to tungsten spiking. In an article by H. Sunami et al. in Japanese Journal of Applied Physics, Vol. 18 (1979) , Supplement 18-1, pages 255-260, there is disclosed a method of manufacturing an MOS transistor wherein a substrate provided with a doped polysilicon gate is subjected to wet thermal oxidation at 700 degrees C to form a relatively thick silicon dioxide layer over the entire surface of the polysilicon gate and a relatively thin silicon dioxide layer over the adjacent substrate region. The thin oxide is then removed utilizing a diffusion-defined uniform etching process and the source and drain regions doped by implantation or thermal " diffusion. Contact metallization to the source and drain regions is then performed utilizing aluminum, a refractory metal, or polysilicon. Howev¬ er, this known process does not relate to the forma- tion of metal covered polysilicon conductors. An article by E. Takeda et al. in IEEE Transactions on Electron Devices, Vol. ED-29, No. 4, pages 611-618, April 1982, discloses a device struc¬ ture for minimizing hot-carrier generation and associ- ated problems in submicrometer MOS devices. According to Fig. 10(c), self-aligned n~ regions are introduced between the channel and n + regions. The n + regions are implanted after selective oxide watering of the polysilicon gate electrode, to fabricate offset re- gions. However, this known process also does not relate to the formation of metal covered polysilicon conductors. Disclosure of the Invention It is an object of the present invention to provide a method of the kind specified whereby the shorting problem between adjacent metal conductors alleviated in a simple and controllable manner. According to one aspect of the present invention, there is provided a method of the kind specified, characterized by the steps of: forming said polysilicon conductor having a masking member there- over from a doped polysilicon layer; thermally oxidiz¬ ing the substrate at a temperature in the range 700- 750 degrees C to form a relatively thick oxide layer on a side surface of said polysilicon conductor and a relatively thin oxide layer on an adjacent region of said substrate, removing the masking member from said polysilicon conductor; subjecting the substrate to doping by a dopant; and forming said first and second metal conductors over the exposed surfaces of said polysilicon conductor and said adjacent region. A method according to this aspect of the invention has the further advantage of being suitable for utilization in a process for forming lightly doped drain-source (LDD) devices in a controllable and reproducible manner. According to another aspect of the invention, there is provided a method of the kind specified, characterized by the steps of forming said second metal conductor to overlie a further polysilicon conductor; providing masking members over said polysilicon conductors; thermally oxidizing the substrate at a temperature in the range 700-750 de¬ grees C to form relatively thick oxide layers on side surfaces of said polysilicon conductors; removing said masking members; and depositing said metal conductors over the exposed upper surfaces of said polysilicon conductors. Brief Description of the Drawings Two embodiments of the present invention will now be described by way of example with reference to the accompanying drawings, in which: OMPI Figs. 1-6 are cross-sectional representations of stages in a process for forming an n-MOSFET with polysilicon gate electrode and interconnecting conduc¬ tors of a single high conductivity and single impurity type; and Figs. 7-9 are cross-sectional representations of stages in manufacturing an n-MOSFET using an alter¬ native process according to the present invention. Best Mode for Carrying Out the Invention The process of forming a sidewall oxide (or oxide trench) structure for silicon gates and interconnections in accordance with the present inven¬ tion will now be described with reference to forming a LDD FET, more specifically, a LDD n-MOSFET. It should be noted that many of the techniques for implementing the various individual steps of the fabrication method are well-known in the art and may be implemented in a number of different ways which are readily apparent to those of ordinary skill in the art. Referring now to Fig. 1, the starting material is a slice of p-type monocrystalline semicon¬ ductor grade silicon. The starting material can be either (111) or (100) orientation and has a bulk resistivity typically of about 8-20 ohm-cm. In the figures, the substrate 10 represents only a very small undivided part of the slice, perhaps less than 15 microns wide for each part. After appropriate clean¬ ing of the slice, the semi-recessed oxide (commonly referred to as field isolation oxide) regions 11-11 are formed in a conventional manner. The oxide re¬ gions 11-11, which are typically about 5,000-15,000 Angstroms (0.5-1.5 microns) thick, define the device active region and provide dielectric isolation between devices formed on the semiconductor slice. One such device active region is shown in Fig. 1 and designated by numeral 12. Active region 12 is then subjected to - b - suitable ion implantation to adjust the threshold voltage of the LDDFET to be formed thereon to the desired value. Next, a clean and high-quality silicon dioxide layer 13 is formed over the entire structure by conventional techniques such as oxidation of the substrate 10 in an HCl/02 environment at a temperature of about 900-1000 degrees C. Oxide layer 13 serves as the gate insulator for the LDDFET and is typically about 100-500 Angstroms (0.01-0.05 microns) thick. Thereafter, a polycrystalline silicon layer 14 of thickness 2,000-5,000 Angstroms (0.2-0.5 mi¬ crons) is formed over the entire structure by low pressure chemical vapor deposition (LPCVD) . The term polycrystalline is used to include amorphous or near- amorphous as well as truly polycrystalline structure. The polysilicon layer 14 is then heavily doped by a conventional doping technique. One example of polysilicon 14 doping step is phosphorus oxychloride (POCI3) deposition and thermal diffusion such that the phosphorus concentration in the polysilicon layer 14 is about Iθ20_ιo21 atoms per cm3. Another example of polysilicon 14 doping is by ion implantation of arse¬ nic ions into the polysilicon layer. As a result of this high dopant concentration profile, the sheet resistivity of polysilicon layer 14 will be in the range of 10-14 ohms per square. Doping the polysilicon layer 14 to a high concentration level is essential not only for providing a high conductivity to the polysilicon gates and interconnects that will be formed from layer 14 but also to enable forming a thick oxide sidewall structure abutting the polysilicon gates and interconnects as will be fully discussed heTeinbelow. The next step of the present process is forming a masking layer over the polysilicon 14. One approach to forming this masking layer is conversion OMPI of the upper surface of polysilicon layer 14 by ther¬ mal oxidation into a layer of silicon dioxide 15 or deposition of oxide layer 15 onto the upper surface of the polysilicon layer 14 to a thickness of about 150 Angstroms (0.015 microns). A layer of silicon nitride 16 is then formed over the silicon dioxide layer 15 using conventional processing techniques such as CVD using a silicon containing gas and ammonia reactants. The layer of nitride 16 is typically about 1,000-1800 Angstroms (0.1-0.18 microns) thick. The silicon dioxide layer 15 not only serves as a pad between the polysilicon layer 14 and the nitride 16 and prevents damage to the underlying polysilicon 14 by minimizing the stresses created on the polysilicon 14 by the • silicon nitride-polysilicon interface but also aids in the eventual removal of the nitride layer 16. The nitride 16 serves as an oxidation mask during subse¬ quent oxidation steps of the present process. Another approach to forming the mask over the polysilicon 14 omits the pad oxide 15 and forms the nitride layer 16 directly over the polysilicon layer 14 by injecting nitrogen atoms into an upper surface layer of polysilicon 14 and thereby converting this surface layer into silicon nitride. In this tech- nique, a nitrogen dose of about 5 X 10^5 atoms per square cm may be utilized for converting a 300-800 Angstroms (0.03-0.08 microns) thick upper layer of polysilicon 14 into silicon nitride 16. Referring to Figs. 1 and 2, conventional photolithographic and etching techniques are then used to pattern the nitride layer 16, oxide layer 15 and polysilicon layer 14 into the desired combination of gate structures and interconnecting conductor struc- • tures. This includes forming a photoresist layer 17 of typical thickness in the range 6,000-10,000 Ang¬ stroms (0.6-1 micron) over the entire surface of the nitride 16 and then exposing the photoresist to ultra- violet or similar radiation through a mask which defines the desired pattern of gates and interconnect¬ ing conductors. The photoresist is then removed by using a suitable solvent exposing the areas where the nitride is to be etched away. The nitride layer 16 is then etched using the overlying photoresist as a mask by conventional etching techniques such as plasma etch. The oxide 15 and polysilicon 14 are then etched using the overlying photoresist-nitride dual layer and photoresist-nitride-oxide triple layer, respectively, as a mask. A gate structure 18 corresponding to the device active area 12 and two interconnecting conduc¬ tor structures on the top of the isolation oxide 11 and designated by numerals 19 and 20 formed in this manner are shown in Fig. 2. In structures 18, 19 and 20, the various parts designated by single, double and triple primed numerals represent the portions of the layers designated by the unpri ed numerals (Fig. 1) from which they were formed. For example, 17' ' repre- sents the portion of the photoresist mask layer 17 corresponding to the interconnect structure 19; 14' ' ' represents the polysilicon interconnect formed from the polysilicon layer 14 corresponding to the inter¬ connect structure 20. After patterning the device gate and interconnect structures in the manner indicated above, referring to Fig. 2, the photoresist masks 17', 17' ' and 17 ι r * for the various structures is removed. Next, the oxide layer 12 not masked by the overlying gate structure 14'-15'-16' is removed by dipping the slice in a dilute hydrofluoric acid etchant solution. In other words, as shown in Fig. 3, the oxide layer 13 is removed over the source and drain areas of the transistor and defined into gate oxide 13'. As shown in Fig. 3, the structure is then subjected to a light doping step using n-type ions to form the lightly doped n-source and drain regions and 22, respectively. This doping step may, typical¬ ly, be accomplished by using arsenic ions of energy 70 keV and dose (1-10) X 101 ions per square cm. The lightly doped source and drain regions 21 and 22, respectively, are shallow and typically of junction depth less than 0.1 microns. The next step of the fabrication process is low temperature steam oxidation of the entire struc¬ ture. The temperature selected for this oxidation step is in the range of 700-750 degrees C and the time of oxidation is about 1-4 hours. Referring to Fig. 4, during this low temperature oxidation step, the un¬ masked side surfaces of doped polysilicon gate 14' and interconnecting conductors 14' ' and 14* ' ' and the exposed regions of the silicon substrate 10 will be oxidized. As a result of this oxidation step, sidewall oxide regions 23-23, 24-24 and 25-25 will be formed corresponding to the polysilicon gate 14', interconnecting lines- 14' ' and 14' 11 , respectively. since the growth rate of silicon dioxide from the heavily doped polysilicon is significantly greater than that of the undoped or lightly doped silicon, the thickness of the oxide formed on the side surfaces of the polysilicon gate 14' and interconnecting conduc- tors 14' ' " and 14''' will be much greater than that of the oxide layer 26 formed over the source and drain regions of the silicon substrate. The thickness ratio of the oxide grown on the side surfaces of the polysilicon to the oxide grown over the source and drain regions of the substrate is a function of such parameters as the crystal orientation of the silicon substrate (in general, the growth rate for (111) surface is about 10-20% higher than that for (100) surface) , the relative dopant concentrations i ' n the polysilicon and silicon substrate (for example, the thickness of the oxide grown on polysilicon doped to a concentration level of lθ20_ιo21 atoms/cm 3 is six to O PΪ eight times the thickness of the oxide grown on un¬ doped (Ϊ00) silicon surface) , oxidation temperature (as the oxidation temperature becomes lower the dif¬ ference in oxidation rate between doped polysilicon and undoped silicon increases) and pressure at which the oxidation is carried out (oxidation rate becomes greater with increasing ambient pressure) . In a specific example of the present polysilicon sidewall oxidation technique, using a (100) silicon substrate 10 having a polysilicon gate 14' of dopant (phos¬ phorus) concentration of lθ20-ιo21 atoms/cm 3 and n~ regions 21 and 22 of dopant (arsenic) concentration of 1016-1018 atoms/cm 3 , the thicknesses of the polysilicon sidewall oxide 23-23 and the oxide layer 26 formed over the substrate when the structure was subjected to an oxidation step at ambient pressure and temperature of about 750 degrees C for a period of three hours were 2,700 Angstroms (0.27 microns) and 440 Angstroms (0.044 microns), respectively. In other words, the thickness of the polysilicon sidewall oxide 23-23 was approximately six times the thickness of the oxide layer 26. Referring to Fig. 4, following the low temperature oxidation step to form the oxide sidewalls extending from the unmasked side surfaces of the polysilicon gate 14' and interconnects 14' ' and 14''*, the nitride-oxide dual mask 16'-15', 16 , r -15*' and 16' » , -i5 , , « corresponding to the polysilicon gate 14', interconnects 14' ' and 14 1 ' 1 , respectively, and the oxide layer 26 over the source and drain regions of the substrate are etched off by conventional tech¬ niques such as plasma etch or concentrated phosphoric acid etch at a temperature of 150 degrees C for remov¬ al of the nitride and dilute hydrofluoric acid etch for removal of the oxide. During the just-mentioned oxide etch step a small portion of the polysilicon sidewall oxide is also removed, but since the sidewall W1PO oxide thickness is quite large to begin with, this will not have any deleterious effect on the final intended structure. Next, referring to Fig. 5, an n-type ion implantation step is carried out to form the heavily doped n+ source and drain regions 27 and 28, respec¬ tively. Preferably, arsenic is used as the dopant during this implantation step since it has relatively heavy mass and produces a shallow junction. Typical arsenic ion dose and energy for forming n+ source and drain regions 27 and 28, respectively, are 5 X 1015- 1016 ions per square cm and 80 keV, respectively. During this implantation step, the oxide sidewalls 23- 23 extending from the polysilicon gate 14* will mask the underlying lightly doped n~ source and drain regions 21A and 22A, respectively. In other words, the heavily doped n + source and drain regions 27 and 28 will be spaced away from the channel region by a distance equal to the polysilicon sidewall 23 thick- ness. Electrical connection of the heavily doped source and drain regions 27 and 28 to the channel regions of the substrate is made via the lightly doped source and drain regions 21A and 22A, respectively. In this manner, a self-aligned gate LDD n-MOSFET structure is conveniently formed. The next step in the present fabrication process is a thermal anneal step in nitrogen or argon gas at a temperature of about 1000 degrees C for a period of 1-2.5 hours to drive-in the arsenic ions introduced into the heavily doped source and drain regions 27 and 28, respectively. At the completion of this anneal step, typical junction depth of the n + regions 27 and 28 will be in the range of 0.1-0.5 microns. The junction depths of the n- regions 21A and 22A will be significantly less than the junction depth of the n+ regions 27 and 28. Next, referring to Fig. 6, a metal such as tungsten is selectively deposited, for example, by chemical vapor deposition using gaseous tungsten hexafluoride (WFg) as donor over all the exposed areas of the silicon substrate 10 and the polysilicon mem¬ bers 14', 14' ' and 14 , , , to a thickness of about 1000- 2000 Angstroms. It can be appreciated that during this selective deposition step, no tungsten will be formed over the oxide regions. The tungsten conduct- ing members formed in this manner and making electri¬ cal contact with the source 21A-27, drain 22A-28, polysilicon gate 14' and interconnects 14" ' and.14 1 ' 1 are shown in Fig. 6 and designated by numerals 29, 30, 31, 32 and 33, respectively. Other metals that are suitable for substitution in place of tungsten are refractory metal suicides such as tungsten silicide. An alternative method of forming a LDD n-MOSFET in accordance with the present invention is illustrated in Figs. 1-2 and 7-9. The steps of this alternative method are as follows: Referring to Fig. 2, after removing the photoresist mask members 17', 17' ' and 17' ' * corre¬ sponding to the polysilicon gate and interconnects 14*, 14' ' and 14' 11 , respectively, the structure is subjected to a low temperature (700-750 degrees C) oxidation step for a period of 1-4 hours forming the polysilicon sidewalls 34-34, 35-35 and 36-36 corre¬ sponding to the gate and interconnects 14', 14' ' and 14' 1 ', respectively (see Fig. 7). During this low temperature oxidation step the thickness of the oxide layer 13 outside the gate area will increase by about one-sixth of the polysilicon sidewall oxide (e.g. sidewall 34-34) thickness. This oxide layer outside the gate area is designated by numeral 37. Thereafter, referring to Fig. 8, openings 38 and 39 are made in a central portion of the oxide layer 37 to expose a portion of the source and drain OMH regions of the underlying substrate. Next, the ni¬ tride-oxide members 16 « -15', 16' '-15'' and Iβ'"-^ 111 over the polysilicon gate 14' and interconnects 14' ' and 14' ' • are removed. Referring to Fig. 8, then an n-type ion implantation step is accomplished using, typically, arsenic ions of energy 20 to 80 keV and dose of 1020- 1021 atoms per square centimeter to form a graded dopant profile for source and drain regions designated by numeral pairs 40-41 and 42-43, respectively, each consisting of a shallow n+ region (40, 42) surrounded by a much less shallow n~ region (41, 43) and self- aligned with the gate. The n + regions 40 and 42 are formed due to direct implantation of n-type ions into the substrate through the openings 38 and 39 in the oxide layer 37. The n" regions 41 and 42 are formed by the n-type ions which penetrate the oxide barrier layer 37. The n~ regions are less shallow than the n + regions since a part of the energy of the implanted ions is absorbed by the oxide layer 37, thereby de¬ creasing the ions' penetration depth. The graded dopant profile source 40-41 and drain 42-43 formed in this manner is spaced from the gate 14' by the thick¬ ness of the oxide sidewall 34-34 since the sidewall 34 prevents any ions from reaching the substrate there¬ under during the source-drain ion implantation step. Referring to Fig. 9, after forming the source and drain regions, a metal such as tungsten is selec-. tively deposited over the polysilicon gate 14' and interconnects 14'' and 14' M and the exposed source and drain regions of the substrate in a manner dis¬ cussed previously in connection with Fig. 6. The metal conducting members formed in this fashion and establishing electrical contact with the source 40-41, drain 42-43, polysilicon gate 14' and interconnects 14 1 ', 14* '' are shown in Fig. 9 under the designation of numerals 44-48, respectively. The processing at this point is substantially complete as far as the novelty of the present inven¬ tion is concerned. The balance of the processing is conventionally performed. By using the above process it is possible to fabricate semiconductor MOS-type devices having polysilicon gates and interconnects having a width in the range of 1-5 microns or less and source-drain regions as small as 1-3 microns on a side. Since the various polysilicon conductors are effectively insu¬ lated by thick oxide sidewall or trench structure, short-circuiting between adjacent conductors is pre¬ vented. The relative closeness of the interconnecting conductors is determined by the photolithographic limitations, using conventional optical lithography in combination with the present process it is possible to space the interconnects as close as 1 micron apart. By using X-ray lithography in conjunction with the present process, the spacing between the interconnects can be reduced to much below 1 micron. Since the short-circuiting between adjacent conductors is pre¬ vented, the present process provides a semiconductor device with improved reliability and yield of produc¬ tion. Also, this process is conducive for fabrication of LDD MOSFETs which are free from the debilitating short channel side effects such as drain punchthrough to which scaled down devices are prone.

Claims: CLAIMS: 1. A method of manufacturing a semiconductor device including a substrate (10) having a first metal conductor (31) overlying a polysilicon conductor (14'), and a second metal conductor (30) located adjacent said first metal conductor (31) , characterized by the steps of: forming said polysilicon conductor (14') having a masking member (15', 16') thereover from a doped polysilicon layer (14) ; thermally oxidizing the substrate (10) at a temperature in the range 700-750 degrees C to form a relatively thick oxide layer (23) on a side surface of said polysilicon conductor (14') and a relatively thin oxide layer (26) on an adjacent region of said substrate (10), removing the masking member (15', 16') from said polysilicon conductor (14'); subjecting the substrate to doping by a dopant; and forming said first and second metal conductors (30, 31) over the exposed surfaces of said polysilicon conductor (14') and said adjacent region. 2. A method according to claim 1, characterized in that the said dopant concentration in said polysilicon conductor (14') is at a relatively high level compared with the dopant concentration in said adjacent region. 3. A method according to claim 1, characterized by the step of removing the relatively thin oxide layer (26) from said adjacent region prior to subjecting the substrate (10) to said doping. 4. A method according to claim 1, characterized in that said masking member includes a layer of silicon nitride (16 1 ). 5. A method according to claim 4, characterized in that said masking member includes a layer of silicon dioxide (15') located between said polysilicon conductor (14') and said layer of silicon nitride (16') . 6. A method according to claim 1, characterized by the step of subjecting the substrate to an initial, relatively light doping after forming said polysilicon conductor (14 r ) and prior to thermal- ly oxidizing the substrate (10) . 7. A method according to claim 1, characterized in that said metal conductors (30, 31) consist essentially of tungsten. 8. A method of manufacturing a semiconductor device including a substrate (10) having a first metal conductor (32) overlying a polysilicon conductor (14'') and a second metal conductor (33) located adjacent said first metal conductor (32) , characterized by the steps of forming said second metal conductor (33) to overlie a further polysilicon conductor (14' 1 '); providing masking members (15'', 16' '; 15* •~ ', 16'* 1 ) over said polysilicon conductors (14 r ι , 14'*'); thermally oxidizing the substrate (10) at a temperature in the range 700-750 degrees C to form relatively thick oxide layers (24, 25) on side surfaces of said polysilicon conductors (14*', 14' 1 '); removing said masking members (15*', 16' '; 15' 1 ', 16'''); and depositing said metal conductors (32, 33) over the exposed upper surfaces of said polysilicon conductors (14", 14'").

Inventors: CHIAO SAMUEL YUE, CHIAO, SAMUEL, YUE
Applicants: NCR CO, NCR CORPORATION
Application year: 1984
Main classification: H01L21
IPC codes: H01L21, H01L29