THIXOTROPIC POLYURETHANE RESIN COMPOSITION

Abstract: A polyurethane resin composition which comprises (1) a polyurethane prepolymer in the form of liquid or solution, (2) colloidal silica and (3) a siloxane compound having a poly­ oxyethylene chain in the molecule maintains an excellent thixotropy even after solvents and additives are added and kneaded as the case may be.

Description: Thixotropic polyurethane resin compositions The present invention relates to novel thixotropic polyurethane resin compositions. In recent years, polyurethanes, because of their excellent rubbery elasticity, weatherability, abrasion resistance, etc., have widely been used in a great variety of fields as elastomers, coatings, sealants, flooring materials, water-proofing materials, walling materials, synthetic or artificial leather and adhesives. When polyurethanes are used in these application fields, they are utilized as self-levelling type resin or thixotropic resin aceording to their intended application fields. In particular, sealing compounds and walling materials, water proofing materials, etc. which are to be worked on vertical or slanting surfaces are used as thixotropic resins to prevent them from slumping and running. As the method of producing such thixotropic polyurethane resin compositions, several proposals have already been made. For example, Japanese Patent Publication No. 41110/70 proposes the thixotropic polyurethane resin compositions which are obtained by combination of a polyurethane prepolymer with collidal silica and a polyoxyethylene glycol derivative; Japanese Patent Publication No. 7632/72 discloses the production of the thixotropic polyurethane resin compositions by combining a polyurethane prepolymer with a large amount of inorganic fillers and a polyoxyalkylene compound; and Japanese Patent Publication No. 11656/76 describes the preparation of the thixotropic polyurethane resin compositions by combining a polyurethane prepolymer with a block copolymer from ethylene oxide and propylene oxide and finely powdered silica, etc. Nevertheless thixotropic polyurethane resin compositions proposed so far lose their thixotropy and never restore it, when they are admixed with other components, for example, organometallic catalyst such as lead octylate and dibutyltin dilaureate and calcium carbonate and kneaded with a conventionally employed mixer such as high-speed disper, planetary mixer and butterfly mixer. Accordingly, when thixotropic urethane polymers or their compounded products such as one-package type sealants are produced on an industrial scale according to such methods, there have been encountered difficulties in supplying invariably stable products due to fluctuations in the product quality. In view of the above situations, the present inventors conducted intensive research in order to impart by far improved thixotropy to fluid polyurethane compositions, and as a result, found that the polyurethane resin compositions which comprise a polyurethane prepolymer in the form of liquid or solution being admixed as the essential components with colloidal silica and a siloxane compound having a polyoxyethylene chanin in the molecule exhibit outstandingly excellent thixotropy. Surprisingly, the thixotropy of the polyurethane resin compositions of the present invention is not affected adversely even by addition of a solvent in a variety of kinds, plasticizers, inorganic fillers, pigments, ultraviolet absorbers, antioxidants and amine or organic metal based catalysts as conventionally used in the urethane industry and the thixotropy is in no way lost, even after such solvents and additives are added and kneaded as the case may be. In addition, it has turned out that the thixotropy to be achieved according to the present invention is not lost even after the kneading in three roll kneader, planetary mixer, disper, butterfly mixer, etc. which are normally utilized for kneading, and thus can provide the ideal thixotropic polyurethane resin compositions. Thus, the present invention relates to the thixotropic polyurethane resin compositions which comprise a polyurethane prepolymer in the form of liquid or solution, colloidal silica and a siloxane compound having a polyoxyethylene chain in its molecule. The polyurethane prepolymer which is one of the basic materials in the present composition includes polymers having a relatively low molecular weight, which have an average molecular weight ranging from about 500 to about 10,000, formed by polymerization of polyisocyanates and active hydrogen compounds to be described hereinafter at the equivalent ratio of NCO group to active hydrogen group ranging preferably from 1.02 : 1.0 to 5.0 : 1.0, more preferably from 1.1 : 1.0 to 3.0 : 1.0. These prepolymers take the form of a liquid by nature or a solution formed by dissolution in a solvent. Such solvent includes esters such as ethyl acetate, butyl acetate and amyl acetate, ketones such as acetone, methyl ethyl ketone and methyl isobutyl ketone, aromatic hydrocarbons such as toluene, benzene and xylene, ethers such as tetrahydrofuran and dioxane, substituted acid amides such as N,N'-dimethylformamide and N,N'-dimethylacetamide, or dimethylsulfoxide, and so forth. By "polyisocyanate" which is a constituent of the above-mentioned prepolymer are denoted compounds having not less than two NCO groups in one molecule, and such compounds include, for example, 2,4- and 2,6-tolylene diisocyanates, m- and p-phenylene diisocyanates, l-chlorophenylene-2,4-diisocyanate, m- and p-phenylene diisocyanates, l-chlorophenylene-2,4-diisocyanate, 1,5-naphthalene diisocyanate, 3,3'-bis toluene-4,4'-diisocyanate, methylenebisphenylene-4,4'-diisocyanate, tetramethylene diisocyanate, hexamethylene diisocyanate, WI W' -diisocyanatodimethylbenzene, WIW' -diisocyanatodimethylcyclohexane, lysing diisocyanate, dicyclohexylmethane diisocyanate, tetramethylxylene diisocyanate, and dimers and trimers of these isocyanates, and triisocyanates obtained by addition of 3 moles of diisocyanates to triols such as trimethylolpropane, and so forth. "Active hydrogen compound", which is other constituent, denotes polyols or polyamines having on the average 2 to 5 of active hydrogen groups per molecule and 30 to 3000 to the average molecular weight per active hydrogen group, or mixtures thereof, and as examples of such compounds, there may be mentioned: : (1) Low molecular weight diols or-triols such as ethylene glycol, propylene glycol, 1,4-butanediol, hexamethylene glycol, 1,4-cyclohexanediol, triisopropanolamine, trimethylolpropane and glycerol, (2) Polyalkylene glycols, such as polyoxyethylene glycol, polyoxypropylene glycol, glycols of polyoxyethylenepolyoxypropylene copolymers and polyoxytetramethylene glycol, (3) Polymers from alkylene oxides such as ethylene oxide and propylene oxide with low-molecular-weight triols such as glycerine, trimethylolpropane and 1,2,6-hexanetriol or low-molecular-weight tetraols such as erythritol and pentaerythritol, (4) Polyester polyols from low molecular weight polyols and low molecular weight polycarboxylic acids, whereby suitable polyols include ethylene glycol, propylene glycol, 1,4- and 1,3-butanediols, 1,6-hexanediol, etc., and preferred polycarboxylic acids include adipic acid, succinic acid, maleic acid, phthalic acid, terephthalic acid, etc. (5) Ring-opening polymerization products of cyclic esters such as polycaprolactone and polybutyrolactone, (6) Castor oil inclusive of hydrogenated castor oil such as mono or diricinoleate of mono, di- or triethylene glycol, mono-, di- or triricinoleate of 1,2,6-hexanetriol or trimethylolpropane and mono-, di-, tri- or tetraricinoleate of pentaerythritol or erythritol, and its related polyols as well as various esters and hemiesters of ricinoleic acid with polyhydric alcohols, and (7) Polyamines such as ethylenediamine, propylenediamine, tetramethylenediamine, p-phenylenediamine, 2,4diaminotoluene, methylenebis-4,4'-diaminobenzene and 4,4'methylene-bis-p-chloroaniline. As the colloidal silica, use can be made of any type of commercially available one, and there may be mentioned, for example, Aerosil-200 Aerosil-300, R-812 RX-200 RY-200 and R972 (all are produced by Nippon Aerosil of Japan). The siloxane compound having a polyoxyethylene chain which is furthermore used in the present invention includes polysiloxanes or alkoxysilanes having not less than one polyoxyethylene chain in the molecule, and those having a molecular weight in the range of about 500 to 30,000 are preferable. The proportion in wihch the oxyethylene chain is contained in such siloxane compound is preferably in the range of 30 to 95 weight %, more preferably in the range of 40 to 90 weight %. The average degree of polymerization for one polyoxyethylene chain in the molecule is desirably within the range of 2 to 150, more desirably within the range of 5 to 60. In the present invention, in addition, advantageous use can be made of siloxane compounds having a block copolymer chain of polyoxyethylene with other polyoxyalkylene. For example, a siloxane compound having a polyoxyethylenepolyoxypropylene block polymer chain in some instances conferes liquidity on the compounds, in contrast with a siloxane compound having merely a polyoxyethylene chain. These siloxane compounds having polyoxyethylene chain can each be synthesized by per se known methods, such as the methods as described in Japanese Patent Publication No. 38264/71, Japanese Patent Publication No. 21754/71, Japanese Patent Publication No. 21754/76 and Japanese Patent Publication No. 8360/78, etc. Typical examples of the polysiloxane compound having polyoxyethylene chain, which is useful in the present invention, include compounds of the formula (I): EMI6.1 wherein m is an integer of 0 to 40; n is an integer of 2 to 50; a is an integer of-2 to 150; b is an integer of 0 to 20; R is hydrogen or lower alkyl and compounds of the formula (11): EMI6.2 wherein x is an integer of 5 to 100; y is an integer of 0 to 20; R1 is hydrogen or lower alkyl; R2 is a lower alkyl group. The proportion in which colloidal silica is incorporated into the composition of the present invention is preferably 0.5 to 50 parts by weight against 100 parts by weight of polyurethane prepolymer, particularly preferably 1.0 to20 parts by weight. The ratio of the siloxane compound having a polyoxyethylene chain to be used in the composition of the present invention is desirably 0.1 to 50 parts by weight against 100 parts by weight of colloidal silica more desirably 1 to 20 parts by weight. There may be added to the composition of the present invention, as the case may be, solvents such as toluene, xylene, ethyl acetate, methyl ethyl ketone and ligroin, inorganic fillers such as calcium carbonate, talc, clay and silica, pigments such as titanium oxide, phthalocyanine blue, iron oxide, chrome yellow, ultramarine blue and carbon, plasticizers used for urethanes such as dioctyl phthalate, dioctyl adipate, tricresyl phosphate and liquid petroleum resin, antioxidants, ultraviolet absorbers and a variety of catalysts for urethanes. Example 1 By reacting 639 parts by weight of polyoxypropylene glycol having a molecular weight of 2000, 213 parts by weight of polyoxypropylene triol having a molecular weight of 3000 with 148 parts by weight of a mixture of 2,4tolylene diisocyanate and 2,6-tolylene diisocyanate (80 : 20) in a stream of nitrogen at 800C for 6 hours, there was obtained a polyurethane prepolymer having an isocyanate group content of 3.56%. The product was referred to as "Urethane Prepolymer (A)". To 100 parts by weight of Polyurethane Prepolymer (A) as obtained above were added 5 parts by weight of colloidal silica (Aerosil 200 , produced by Nippon Aerosil Co., Ltd.) and 0.5 part by weight each of the thixotropy imparting agents A to I described in Table 1, and kneading was carried out with a vacuum kneader at 600C for 1 hour to yield a composition in the form of paste or grease, respectively. These compositions were subjected to slump test in accordance with JIS A-5758, whereby the results as shown in Table 1 were obtained. Table 1 EMI8.1 Silane <SEP> compound <SEP> having <SEP> a <SEP> polyoxyethylene <SEP> chain <SEP> represented <SEP> by <SEP> the <SEP> formula <SEP> (I) <tb> Slump <tb> Sign <SEP> of <SEP> Average <SEP> Average <SEP> molecular <SEP> Content <SEP> of <tb> m <SEP> n <SEP> a <SEP> b <SEP> R <SEP> (m/m) <tb> molecular <SEP> weight <SEP> of <SEP> a <SEP> polyoxy- <SEP> polyoxyethylene <tb> sample <tb> weight <SEP> ethylene <SEP> chain <SEP> chain <SEP> (%) <tb> A <SEP> 10 <SEP> 5 <SEP> 17 <SEP> 0 <SEP> H <SEP> 5,164 <SEP> 748 <SEP> 72.4 <SEP> 0 <tb> <SEP> B <SEP> 10 <SEP> 5 <SEP> 10 <SEP> 0 <SEP> CH3 <SEP> 3,705 <SEP> 440 <SEP> 59.4 <SEP> 0 <tb> C <SEP> 25 <SEP> 5 <SEP> 10 <SEP> 0 <SEP> H <SEP> 4,735 <SEP> 440 <SEP> 46.5 <SEP> 0 <tb> D <SEP> 0 <SEP> 40 <SEP> 10 <SEP> 0 <SEP> H <SEP> 21,928 <SEP> 440 <SEP> 80.3 <SEP> 0 <tb> E <SEP> 5 <SEP> 3 <SEP> 10 <SEP> 0 <SEP> H <SEP> 2,165 <SEP> 440 <SEP> 61.0 <SEP> 0 <tb> F <SEP> 10 <SEP> 5 <SEP> 34 <SEP> 0 <SEP> H <SEP> 8,904 <SEP> 1,500 <SEP> 84.2 <SEP> 0 <tb> G <SEP> 10 <SEP> 5 <SEP> 57 <SEP> 0 <SEP> H <SEP> 13,964 <SEP> 2,500 <SEP> 89.5 <SEP> 0 <tb> H <SEP> 10 <SEP> 5 <SEP> 34 <SEP> 3 <SEP> H <SEP> 9,774 <SEP> 1,500 <SEP> 76.7 <SEP> 0 <tb> I <SEP> 5 <SEP> 3 <SEP> 17 <SEP> 2 <SEP> H <SEP> 3,437 <SEP> 748 <SEP> 65.3 <SEP> 0 <tb> EMI8.2 Example 2 By reacting 590 parts by weight of polyoxypropylene glycol having a molecular weight of 3000, 295 parts by weight of polyoxypropylene triol having a molecular weight of 4500 with 115 parts by weight of 4,4'-diisocyanatodiphenylmethane in a stream of nitrogen at 800C for 4 hours, there was obtained a prepolymer having an isocyanate group content of 1.38%. The product was referred to as "Urethane Prepolymer (B)". To 100 parts by weight of Prepolymer (B) as obtained in the above were added 60 parts by weight of dioctyl phthalate, 8 parts by weight of colloidal silica (Aerosil 200 produced by Nippon Aerosil Co., Ltd.) and 0.8 part by weight each of the thixotropy imparting agents J to N described in Table 2 and kneading was carried out with a vacuum kneader at 600C for 1 hour to yield a composition in the form of paste or grease, respectively. These compositions were subjected to slump test in accordance with JIS A-5758, whereby the results as shown in Table 2 were obtained. Table 2 EMI10.1 Silane <SEP> compound <SEP> having <SEP> a <SEP> polyoxyethylene <SEP> chain <SEP> represented <SEP> by <SEP> the <SEP> formula <SEP> (II) <tb> Slump <tb> Sign <SEP> of <SEP> Average <SEP> Average <SEP> molecular <SEP> Content <SEP> of <tb> a' <SEP> b' <SEP> RÚ <SEP> Rê <tb> sample <SEP> molecular <SEP> weight <SEP> of <SEP> a <SEP> polyoxy- <SEP> polyoxyethylene <SEP> (m/m) <tb> weight <SEP> ethylene <SEP> chain <SEP> chain <SEP> (%) <tb> J <SEP> 15 <SEP> 0 <SEP> H <SEP> CH3 <SEP> 1,000 <SEP> 860 <SEP> 66.0 <SEP> 0 <tb> K <SEP> 34 <SEP> 0 <SEP> CH3 <SEP> CH3 <SEP> 1,850 <SEP> 1,500 <SEP> 81.1 <SEP> 0 <tb> L <SEP> 15 <SEP> 0 <SEP> H <SEP> C2H5 <SEP> 1,042 <SEP> 660 <SEP> 63.3 <SEP> 0 <tb> M <SEP> 55 <SEP> 5 <SEP> CH3 <SEP> CH3 <SEP> 3,064 <SEP> 2,420 <SEP> 79.0 <SEP> 0 <tb> N <SEP> 15 <SEP> 0 <SEP> CH3 <SEP> C2H5 <SEP> 1,056 <SEP> 660 <SEP> 62.5 <SEP> 0 <tb> EMI10.2 Example 3 To 100 parts by weight of Prepolymer (B) as prepared in Example 2 were added 60 parts by weight of dioctyl adipate, 40 parts by weight of calcium carbonate (Escalon 200 produced by Sankyo Seifun Co. of Japan), 9 parts by weight of titanium oxide (R-820 produced by Ishihara Sangyo Kaisha of Japan), 8 parts by weight of colloidal silica (Aerosil 200 produced by Nippon Aerosil), and 0.8 part by weight each of the thixotropy imparting agents A to N, and stirring was effected in a vacuum kneader at 600C for 1 hour, respectively. The resultant compositions were subjected to slump test in accordance with JIS A-5758, whereby they all showed the satisfactory result of 0 mm in slump. Reference Example 1 To 100 parts by weight of Prepolymer (B) as prepared in Example 2 were added 60 parts by weight of dioctyl adipate, 40 parts by weight of calcium carbonate (Escalon, produced by Sankyo Seifun Co. of Japan), 9 parts by weight of titanium oxide (R-820QD, produced by Ishihara Sangyo Kaisha of Japan) and 8 parts by weight of colloidal silica (Aerosil-200 R, produced by Nippon Aerosil Co., Ltd.), and kneading was carried out in a vacuum kneader at 600C for 1 hour. Furthermore, 0.8 part by weight of polyoxyethylene glycol (average molecular weight of 1000, produced by Sanyo Chemical Industries Ltd. of Japan) as a thixotropy imparting agent was added toihe mixture, followed by kneading with a vacuum kneader. The samples taken after kneading for different periods of time of 5, 10 and 30 minutes after the addition of polyoxyethylene glycol were each subjected to slump test in accordance with JIS A-5758, whereby the samples being kneaded for 5 and 10 minutes showed the slump of 3 mm and 15 mm, respectively, while the sample kneaded for 30 minutes almost lost thixotropy and fell down. Reference Example 2 To 100 parts by weight of Prepolymer (B) as prepared in Example 2 were added 60 parts by weight of dioxtyl adipate, 40 parts by weight of calcium carbonate (Escalon 200 produced by Sankyo Seifun Co., Ltd. of Japan), 9 parts by weight of titanium oxide (R-820R, produced by Ishihara Sangyo Kaisha of Japan), 8 parts by weight of colloidal silica (Aerosil 200 produced by Nippon Aerosil Co., Ltd.) and 3 parts by weight of polyoxyethylene glycol (average molecular weight of 20,000, produced by Wako Pure Chemicals Industries Ltd. of Japan) as well as 1 part by weight of alkyl-modified polysiloxane (SH-203 , produced by Toray Silicone Co., Ltd. of Japan), and stirring was effected in a vacuum kneader at 60 C for 1 hour. The resultant composition was subjected to slump test in accordnace with JIS A5758, whereby it hardly showed thixotropy and fell down.

Claims: What is claimed is: 1. A thixotropic polyurethane resin composition which comprises (1) a polyurethane prepolymer in the form of liquid or solution, (2) colloidal silica and (3) a siloxane compound having a polyoxyethylene chain in the molecule. 2. A composition claimed in Claim 1, wherein the proportion of the colloidal silica against 100 parts by weight of the polyurethane prepolymer is 0.5 to 50 parts by weight and the proportion of the siloxane compound against 100 parts by weight of colloidal silica is 0.1 to 50 parts by weight. 3. A composition claimed in Claim 1, wherein the proportion of the colloidal silica against 100 parts by weight of the polyurethane prepolymer is 1.0 to 20 parts by weight and the proportion of the siloxane compound against 100 parts by weight of colloidal silica is 1 to 20 parts by weight. 4. A composition claimed in Claim 1, wherein a siloxane compound is one having polyoxyethylene chain in the proportion ranging from 40 to 90 weight percent per molecule. 5. A composition claimed in Claim 1, wherein a siloxane compound is one represented by the formula (I): EMI13.1 wherein m is an integer of 0 to 40; n is an integer of 2 to 50; a is an integer of 2 to 150; b is an integer of 0 to 20; R is hydrogen or lower alkyl. 6. A composition claimed in Claim 1, wherein a siloxane compound is one represented by the formula (II): EMI14.1 wherein x is an integer of 5 to 100; y is an integer of 0 to 20; R1 is hydrogen or lower alkyl; R2 is a lower alkyl group.

Inventors: HIGASHI, SACHIO, KOBAYASHI, ATSUO, NISHINO, KENICHI, YAMAMOTO, SHINICHIRO
Applicants: TAKEDA CHEMICAL INDUSTRIES, LTD.
Application year: 1984
Main classification: C08L75
IPC codes: C08K3, C08G18, C08L83, C08L75, C09D175