OXAZOLE DERIVATIVES, PROCESS FOR PRODUCTION THEREOF AND USE THEREOF AS PHOTOCONDUCTIVE MATERIAL

Abstract: An oxazole derivative of the formula: wherein R is an alkyl group having 1 to 3 carbon atoms is stable for ultraviolet light without decomposition when exposed thereto and can be used as a photoconductive mater­ ial, for example, in electrophotographic plate.

Description: OXAZOLE DERIVATIVES, PROCESS FOR PRODUCTION THEREOF AND USE THEREOF AS PHOTOCONDUCTIVE MATERIAL This invention relates to oxazole derivatives, a process for production thereof and use thereof as photoconductive materials. As oxazole derivatives, there have heretofore been known 2- (4-dipropylaminophenyl) -4- (4-dimethylaminophenyl) - 5-(2-chlorophenyl)-1,3-oxazole [compound (IV)], 2-(4diethylaminophenyl)-4-(4-dimethylaminophenyl)-5-(2-chlorophenyl)-1,3-oxazole [compound (V)], 2-(4-dimethylaminophenyl)-4-(4-dimethylaminophenyl)-5-(2-chlorophenyl)-1,3oxazole [compound (VI)] and the like, and they are utilized as electrophotographic photosensitive materials for copying machines and laser beam printers (Japanese Patent Appln. Kokai (Laid-Open) No. 123544/81). However, these oxazole derivatives are disadvantageous in that since they are easily decomposed in solution by ultraviolet light to mainly give 2 - (4-dipropylaminophenyl) - 6 -dimethylaminophenanthro- [9,10-d]oxazole as a decomposition product, they require care in handling and are apt to lose their characteristics during production of an electrophotographic plate. This invention aims at solving these problems and providing an oxazole derivative which is stable to ultraviolet light and useful as an electrophotographic photosensitive material or electrochromism display materials, a process for producing the same and a process for using the same. This invention provides an oxazole derivative represented by the formula: EMI2.1 wherein R is an alkyl group having 1 to 3 carbon atoms. This invention further provides a process for producing an oxazole derivative of the formula (I) by reacting a compound represented by the formula: EMI2.2 with a compound represented by the formula: EMI2.3 wherein R is an alkyl group having 1 to 3 carbon atoms. This invention still further provides a process for using the oxazole derivative of the formula (I) as a photoconductive material. In the attached drawings, Fig. 1 is an NMR spectrum of the oxazole derivative obtained in Example 1, Fig. 2 is an IR spectrum thereof, Fig. 3 is an NMR spectrum of the oxazole derivative obtained in Example 2, Fig. 4 is an IR spectrum thereof, Fig. 5 is an NMR spectrum of the oxazole derivative obtained in Example 3, Fig. 6 is an IR spectrum thereof, Fig. 7 is an NMR spectrum of the oxazole derivative obtained in the Comparative Example, Fig. 8 is an IR spectrum thereof, and Fig. 9 is the changes with the lapse of time in the rates of decomposition of respective acetonitrile solutions of the compounds (VIII), (IX), (X) and (V), by irradiation from a high pressure mercury arc lamp. The oxazole derivative represented by EMI3.1 wherein R is preferably a methyl group, an ethyl group or a propyl group, is a novel compound, and has a F atom in place of the C1 atom in each of the well-known compounds (IV), (V) and (VI); therefore it is so stable to ultraviolet light that it is not or difficult to be decomposed by irradiation with ultraviolet light. The oxazole derivative of the formula (I) can be produced by reacting a compound represented by the formula: EMI4.1 with a compound represented by the formula: EMI4.2 wherein R is preferably a methyl group, an ethyl group or a propyl group. The compound rperesented by the formula (II) can be produced, for example, by adding, to a 50% aqueous ethanol solution, 4-dimethylaminobenzaldehyde, 2-f luoro- benzaldehyde and KCN in proportions of 1 mole, 1 mole and 0.1 to 1.5 molest respectively, and refluxing the resulting mixture for 1.5 to 4 hours. The compound represented by the formula (III) can be synthesized, for example, by the following reaction path. One mole of aniline is reacted with 0.67 mole of a compound represented by the formula: (RO)3PO (VII) wherein R is preferably a methyl group, an ethyl group or a propyl group, under reflux for 2 hours, and the reaction solution is distilled under reduced pressure to obtain a dialkylaniline (in which the alkyl group is a methyl group, an ethyl group or a propyl group; hereinafter the same applies). Subsequently, 0.3 to 0.4 mole of the dialkylaniline is added dropwise to 1 mole of N,N-dimethylformamide at 190 to 220C, and after completion of the addition, the resulting mixture is heated at 900 to 950C for 2 hours, after which the reaction solution thus obtained is distilled under reduced pressure to obtain a dialkylaminobenzaldehyde. With 1 mole of the dialkylaminobenzaldehyde is reacted 1.0 to 1.3 moles of hydroxylamine hydrochloride at room temperature for 20 minutes, and the reaction solution is allowed to stand in a refrigerator to deposit a dialkylaminobenzaldehyde oxime. Finally, 1 mole of the dialkylaminobenzaldehyde oxime is reacted with 2 to 3 moles of acetic anhydride under heating and reflux for 20 minutes to be dehydrated, whereby the compound represented by the formula (III) can be produced. EMI5.1 In the above, production of the dialkylaminobenzonitrile from the dialkylaminobenzaldehyde can be carried out also by the following reaction path (B). With 1 mole of the dialkylaminobenzaldehyde are mixed 1.15 moles of NH2QH-HCQ, a large excess of HCOONa and about 1,500 ml of formic acid, and the resulting mixture is subjected to reaction under reflux for 1 hour, immediately after which the reaction solution thus obtained is poured into water to deposite a precipitate of the dialkylaminobenzonitrile. It is sufficient that the precipitate is recrystallized from water. EMI6.1 The oxazole derivative represented by the formula (I) can be obtained by mixing well the compound of the formulae (II) and (III) and then adding the resulting mixture to concentrated sulfuric acid with stirring in the dark. The reaction temperature is preferably 200 to 700 C. When the reaction temperature is adjusted to 500 to 700C, the reaction is completed in 0.5 to 2 hours. The reaction product can be purified by recrystallization from methanol. It is preferable to mix the compounds of the formulae (II) and (III) previously before the reaction. When the compound of the formula (II) alone is added to concentrated sulfuric acid, it undergoes dehydration reaction before reacting with the compound represented by the formula (III). The oxazole derivative represented by the formula (I) can effectively be used as a photoconductive material. This photoconductive material can be used as a charge transport material in an electrophotographic plate by taking advantage of its photoconductivity. When an electrophotographic plate is produced by using the oxazole derivative of the formula (I) of this invention as a charge transport material for a material for electrophotography, a monolayer comprising a mixture of the compound represented by the formula (I) and a charge generating material can be formed as a photoconductive layer on an electroconductive layer. It is also possible to form a so-called double layer structure as a photoconductive layer on an electroconductive layer by forming individual layers of a charge generating material and a charge transport material. When the monolayer structure is employed, the proportion of the aforesaid charge transport material to the charge generating material is usually 1 to 50 parts by weight of the former to 1 part by weight of the latter. The thickness of the whole photoconductive layer is usually adjusted to 5 to 100 urn. On the other hand, when the double layer structure is employed, it is usual to adjust the thickness of the charge generating material layer to 0.1 to 5 Wm and the thickness of the charge transport material layer to 5 to 100 Vm. However, it is desirable in either case to determine them finally with caution so as not to impair the photosensitivity, i.e., the electrification characteristics. When the thickness of the photoconductive layer is too large, the flexibility of the layer itself tends to be lowered, and therefore care must be taken. The aforesaid charge generating material includes Si, Se, AS2S3, Sb2S3, Sb2Se3, CdS, CdSe, CdTe, ZnO, phthalocyanine pigments, azo pigments, anthraquinone pigments, indigoid pigments, quinacridone pigments, perylene pigments, polycyclic quinone pigments, methine squalate pigments, dyes, etc. Already-known binding agents may be used in the photoconductive layer. The binding agent is selected from linear saturated polyester resins, polycarbonate resins, acrylic resins, butyral resins, polyketone resins, polyurethane resins, poly-N-vinylcarbazole, poly (p-vinylphenyl) anthracene and the like. The amount of the binding agent used is suitably 1 to 50 parts by weight per 1 part by weight of the charge generating material in the case of a photoconductor having a monolayer structure. In the case of a photoconductor having a double layer structure, the binding agent should be added to at least the layer comprising a charge transport material, and in this case, the amount of the binding agent is suitably 1 to 50 parts by weight per 1 part by weight of the charge transport material. In the electroconductive layer, aluminum, brass, copper, gold or the like is used. This invention is explained below in detail referring to examples. Synthesis Example 1 [Production of 4-dimethylamino-2' -fluorobenzoin] In 150 ml of a 50% aqueous ethanol solution were dissolved 14.9 g of dimethylaminobenzaldehyde, 12.4 g of 2-fluorobenzaldehyde and 8.0 g of potassium cyanide, and the resulting solution was heated and refluxed for 2 hours and 30 minutes. After the heating and refluxing, the solution was allowed to cool, and the light-yellow crystals deposited were filtered and then dried at 800C. The crystals were recrystallized from 500 ml of methanol to obtain 4-dimethylamino-2'-fluorobenzoin (yield 45%) having a melting point of 168C - 1700C. Synthesis Example 2 [Production of 4-dipropylaminobenzonitrile] After 62 g of aniline and 100 g of n-propyl phosphate were heated and refluxed for 2 hours, the resulting solution was allowed to cool, and when its temperature was lowered to 550 to 600C, an aqueous sodium hydroxide solution (56.3 g/225 ml) was added, and the resulting solution was heated and refluxed for 1 hour. Immediately after completion of the heating and reflux, the reaction solution was transferred into a l-liter beaker and allowed to stand. The reaction solution separated into two layers, and the upper layer was yellow, while the lower layer became a white solid. The white solid was extracted with three 100-ml portions of ether, and the upper layer and the combined extract were dried over anhydrous sodium sulfate. After the ether was distilled off, the same volume of acetic anhydride was added, and the resulting solution was allowed to stand overnight. An aqueous hydrochloric acid solution (45 ml/67.5 ml) was added to this reaction solution and the resulting mixture was allowed to cool, and thereafter a 25% aqueous sodium hydroxide solution was added, upon which the mixture separated into an oil layer and an aqueous layer. The aqueous layer was extracted with three 100-ml portions of ether, and the combined extract was dried together with the oil layer over anhydrous sodium sulfate. After the ether was distilled off, the residue was distilled under reduced pressure (b.p. 1300 - 1400C/18 mmHg) to obtain dipropylaniline (yield 69%). Next, 44.5 g of phosphorus oxychloride was added dropwise to 54 g of N,N-dimethylformamide over a period of 30 minutes while the N,N-dimethylformamide was maintained at 200C or lower. Thereto was added dropwise 35 g of the dipropylaniline obtained in the above over a period of 1 hour. After completion of the addition, the resulting mixture was stirred with heating at 900 to 950C for 2 hours. Thereafter, the reaction solution thus obtained was added to ice water, and the resulting mixture was neutralized with a saturated aqueous sodium acetate solution. The mixture was then extracted with five 100-ml portions of ether and the combined extract was dried over anhydrous sodium sulfate. After the ether was distilled off, the residue was distiller under reduced pressure (b.p. 155" - 1630C/3 mmHg) to obtain dipropylaminobenzaldehyde (yield 46%). In 23 ml of 95% ethanol was dissolved 11.6 g of the dipropylaminobenzaldehyde, and an aqueous hydroxylamine hydrochloride solution (4.7 g/5.7 ml) was added thereto, after which the resulting solution was stirred for 20 minutes. An aqueous sodium hydroxide solution (3.4 g/4.5 ml) was added to the reaction solution, and the resulting mixture was allowed to stand at room temperature for 2 hours and 30 minutes. Thereto was added 29 g of ice and the air in the reaction system was replaced with CO2 gas, after which the reaction system was allowed to stand overnight in a refrigerator. The white crystals deposited was filtered by means of suction washed with water, and then dried. To the compound thus obtained was added 12.4 g of acetic anhydride, and the resulting mixture was heated and refluxed for 20 minutes. Thereafter, 35 ml of cold water was added to the reaction solution thus obtained, and the resulting solution was neutralized with an aqueous sodium hydroxide solution. The solution neutralized was extracted with three 40-ml portions of ether, and the combined extract was dried over anhydrous sodium sulfate. After the ether was distilled off, the residue was distilled under reduced pressure (b.p. 1800C/4 mm Hg) to obtain 4-dipropylaminobenzonitrile (yield 79%). When allowed to stand, this compound crystallized into yellow crystals having a melting point of 390 - 410C. Synthesis Example 3 [Production of 4-dimethylaminobenzonitrile] There were heated and refluxed for 1 hour 29.8 g of dimethylaminobenzaldehyde synthesized according to the procedure in Synthesis Example 2, 15.9 g of hydroxylamine hydrochloride, 25 g of sodium formate and 333 ml of formic acid. When the reaction solution was added dropwise to 800 ml of water with stirring, light-green crystals were deposited. The crystals were filtered, thereafter dried, and then recrystallized from acetone to obtain 4-dimethylaminobenzonitrile (yield 50%) having a melting point of 67" - 690C. Synthesis Example 4 [Production of 4-diethylaminobenzonitrile] There were heated and refluxed for 1 hour 25 g of diethylaminobenzaldehyde synthesized according to the procedure in Synthesis Example 2, 10.5 g of hydroxylamine hydrochloride, 16.5 g of sodium formate and 220 ml of formic acid. When the reaction solution was added dropwise to 400 ml of water with stirring, white crystals were deposited. The crystals were filtered, thereafter dried, and then recrystallized from water-acetone to obtain 4diethylaminobenzonitrile (yield 50%) having a melting point of 660 - 670C. Example 1 In the dark, 35 g of concentrated sulfuric acid was maintained at 600C and a mixture of 2.4 g of 4-dimethylamino-2'-fluorobenzoin obtained in Synthesis Example 1 and 2.1 g of the 4-dipropylaminobenzonitrile obtained in Synthesis Example 2 was added, after which the resulting mixture was stirred for 1 hour. When the reaction solution thus obtained was added to 900 ml of water, yellowish-green cyrstals were deposited. After the crystals were filtered, the filtrate was made basic with a 3N aqueous sodium hydroxide solution, upon which light-yellow crystals were deposited. The crystals were filtered by means of suction and air-dried. The crystals were then recrystallized from methanol to obtain 1.73 g (yield 43%) of a light-yellow solid. The light-yellow solid was identified as 2-(4dipropylaminophenyl)-4-(4-dimethylaminophenyl)-5-(2fluorophenyl)-1,3-oxazole (the compound VIII) from the following analysis results (1) Melting point: 1340 - 1350C (2) Elementary analysis values: C29H32N30F C H N Calculated (%) 76.15 7.00 9.19 Found (%) 76.07 7.11 9.15 (3) NMR values (the NMR spectrum is shown in Fig. 1): : CDCQ3 T values EMI13.1 <tb> 2.07 <SEP> (doublet <SEP> 2H) <tb> 2.38 <SEP> - <SEP> 2.82 <SEP> (multiplet <SEP> 6H) <SEP> W <SEP> <SEP> aromatic <SEP> ring <tb> 3.37 <SEP> (doublet <SEP> 2H) <tb> 3.40 <SEP> (doublet <SEP> 2H) <tb> 6.72 (triplet 4H the methylene proton of a propyl group) 7.11 (singlet 6H the proton of a methyl group) 8.46 (sextet 4H the central methylene proton of a propyl group) 9.08 (triplet 6H the terminal methyl proton of a propyl group) (4) IR spectrum (KBr method) is shown in Fig. 2. Example 2 In the dark, 35 g of concentrated sulfuric acid was maintained at 600C and a mixture of 2.4 g of the 4dimethylamino-2'-fluorobenzoin obtained in Synthesis Example 1 and 1.5 g of the 4-dimethylaminobenzonitrile obtained in Synthesis Example 3 was added, after which the resulting mixture was stirred for 30 minutes. When the reaction solution thus obtained was added to 900 ml of water, yellowish-green crystals were deposited. After the crystals were filtered, the filtrate was made basic with a 3N aqueous sodium hydroxide solution, upon which light-yellow crystals were deposited. The crystals were filtered. by means of suction and air-dried. The crystals were then recrystallized from methanol to obtain 1.56 g (yield 44%) of a light-yellow solid. The light-yellow solid was identified as 2-(4-dimethylaminophenyl)-4-(4-dimethyl aminophenyl) -5- (2-fluorophenyl) -1, 3-oxazole (the compound IXt from the following analysis results. (1) Melting point: 1720 - 1730C (2) Elementary analysis values: C25H24N3OF C H N Calculated (%) 74.79 6.03 10.47 Found (%) 74.53 6.04 10.47 (3) NMR values (the NMR spectrum is shown in Fig. 3): CDCQ3 z values EMI15.1 <tb> 2.06 <SEP> (doublet <SEP> 2H) <tb> 2.40 <SEP> - <SEP> 2.90 <SEP> (multiplet <SEP> 6H) <tb> <SEP> aromatic <SEP> ring <tb> 3.36 <SEP> (doublet <SEP> 2H) <tb> 3.45 <SEP> (doublet <SEP> 2H) <tb> 7.11 (singlet 12H the proton of a methyl group) (4) IR spectrum (KBr method) is shown in Fig. 4. Example 3 In the dark, 32 g of concentrated sulfuric acid was maintained at 60"C and a mixture of 2.2 g of the 4-dimethylamino-2'-fluorobenzoin obtained in Synthesis Example 1 and 1.64 g of the 4-diethylaminobenzonitrile obtained in Synthesis Example 4 was added, after which the resulting mixture was stirred for 1 hour. When the reaction solution thus obtained was added to 800 ml of water, yellowish-green precipitate was deposited. After the precipitate was filtered, the filtrate was made basic with a 3N aqueous sodium hydroxide solution, upon which lightyellow crystals were deposited. The crystals were filtered by means of suction and air-dried. The crystals were then recrystallized from methanol to obtain 1.39 g (yield 40%) of a light-yellow solid. The light-yellow solid was identified as 2- (4-diethylaminophenyl) - 4- (4-dimethylamino- phenyl)-5- (2-fluorophenyl)-1,3-oxazole (the compound X) from the following analysis results. (1) Melting point: 102C - 1050C (2) Elementary analysis values: C27H28N3OF C H N Calculated (%) 75.35 6.51 9.77 Found (%) 75.25 6.53 9.72 (3) NMR values (the NMR spectrum is shown in Fig. 5): CDCQ3 T values EMI16.1 <tb> 2.09 <SEP> (doublet <SEP> 2H) <tb> 2.40 <SEP> - <SEP> 2.S5 <SEP> (multiplet <SEP> 6H) <tb> <SEP> aromatic <SEP> ring <tb> 3.38 <SEP> (doublet <SEP> 2H) <tb> 3.45 <SEP> (doublet <SEP> 2H) <tb> 6.69 (quartet 4H the methylene proton of an ethyl group) 7.15 (singlet 6H the proton of a methyl group) 8.89 (triplet 6H the terminal methyl proton of an ethyl group) (4) IR spectrum (KBr method) is shown in Fig. 6. Comparative Example 1 In the dark, 25 g of concentrated sulfuric acid was maintained at 600C and a mixture of 1.2 g of 4dimethylamino-2'-chlorobenzoin and 1.0 g of 4-diethyl aminobenzonitrile was added, after which the resulting mixture was stirred for 1 hour and 30 minutes. When the reaction solution thus obtained was added to 500 ml of water, yellowish-green precipitate was deposited. After the precipitate was filtered, the filtrate was made basic with a 3N aqueous sodium hydroxide solution, upon which lightyellow crystals were deposited. The crystals were filtered by means of suction and air-dried.. The crystals were then recrystallized from methanol to obtain 0.72 g (yield 37%) of a light-yellow solid. The light-yellow solid was identified as 2-(4-diethylaminophenyl)-4-(4-dimethyl aminophenyl)-5- (2-chlorophenyl) -1,3-oxazole (the compound V) from the following analysis results. (1) Melting point: 1350 - 1390C (2) Elementary analysis values: C27H28N3OCZ C H N Calculated (%) 7-2.65 6.28 9.42 Found (%) 72.58 6.35 9.50 (3) NMR values (the NMR spectrum is shown in Fig. 7): CDCt3 T values EMI17.1 <tb> 2.05 <SEP> (doublet <SEP> 2H) <tb> 2.45 <SEP> - <SEP> 2.82 <SEP> (multiplet <SEP> 6H) <tb> <SEP> aromatic <SEP> ring <tb> 3.35 <SEP> (doublet <SEP> 2H) <tb> 3.45 <SEP> (doublet <SEP> 2H) <tb> 6.68 (quartet 4H the methylene proton of an ethyl group) 7.15 (singlet 6H the methyl proton of methyl group) 8.88 (triplet 6H the methyl proton of an ethyl group) (4) IR spectrum (KBr method) is shown in Fig. 8. Test Example Photolytic property tests on the compounds (VIII), (IX), (X) and (V) obtained in Examples 1 to 3 and Comparative Example 1, respectively, were carried out in the following manner. After nitrogen gas was bubbled for 1 hour through acetonitrile solutions of each of the compounds (VIII), (IX), (X) and (V) having a concentration of 2 x 10 mol/liter, each of the solutions was irradiated from a 150-W high pressure mercury arc lamp while bubbling therethrough nitrogen gas. Samples were collected at 5-minutes intervals after the beginning of the irradiation and diluted with acetonitrile in a definite dilution ratio, after which the change of the absorption spectrum was investigated by means of a ultraviolet spectrophotometer. In the case of the compound (V) shown in Comparative Example, 5 minutes after the irradiation from the mercury arc lamp, the absorption spectrum changed to an absorption spectrum (Bmax = 370.0 nm, 258.0 nm, 245.0 nm) which was different from the initial absorption spectrum (ajax = 363.0 nm E = 4.8 x 104 liter/mol.cm, 310 nm shoulder). The former absorption spectrum was due to 2-(4-diethylaminophenyl)-6-dimethylaminophenanthro[9,10-d]- oxazole produced by decomposition of the compound (V). The decomposition rate of the compound (V) shown in Comparative Example was calculated from the concentration of the decomposition product produced according to Lambert-Beer's law by measurement of the absorbance at 258.0 nm in the absorption spectrum at each time which absorbance appeared owing to the decomposition. In the case of the compounds (VIII), (IX) and (X), even 60 minutes after the irradiation, the absorption spectra did not change in pattern from the initial spectrum (VIII: Amax = 363.0 nm ± = 4.9 x 104 liter/mol.cm, 310.0 nm shoulder; IX: ajax = 359.0 nm C = 4.5 x 104 liter/mol.cm, 310.0 nm shoulder; X: Bmax = 363.0 nm E = 4.5 x 104 liter/ mol.cm, 310.0 nm shoulder). The decomposition rate of each of these compounds was evaluated from the ratio of the absorbance at 310.0 nm (A310 0) to the absorbance at Amax (AAmax) (A310.0/AXmax) in the absorption spectrum at each time. In Fig. 9 are shown the changes with the lapse of time of the rates of photolysis of the acetonitrile solution of the compounds (VIII), (IX), (X) and (V) by the irradiation from the high pressure mercury arc lamp. In Fig. 9, the curve 1 shows the decomposition rate of the compound (VIII), the curve 2 that of the compound (IX), the curve 3 that of the compound (X), and the curve 4 that of the compound (V). Application Example 1 A 5% by weight solution of 1 part by weight of a type metal-free phthalocyanine (Heliogen Blue 7560, a trade name, manufactured by BASF A.G.) and 6.7 parts by weight of a silicone resin (KR255, a trade name, manufactured by Shin-etsu Chemical Industry Co., Ltd.) in tetrahydrofuran as a solvent was prepared, and then kneaded in a ball mill for 5 hours. The pigment dispersion thus obtained was applied to an aluminum plate tan electric conductor) by means of an applicator and dried at 900C for 40 minutes to form a charge generating material layer of 1 urn in thickness. Next, a 27% by weight solution of 1 part by weight of each of the oxazole derivatives of this invention shown in Table 1, 2.4 parts b weight of a polyester resin (Vyron 200, a trade name, manufactured by Toyobo Co., Ltd.) and 0.6 part by weight of a styrene resin (Piccotex 100 manufactured by ESSO Standard Oil Company) in tetrahydrofuran as-a-solvent was prepared, applied to the above-mentioned charge generating material layer by means of an applicator, and then dried at 900C for 40 minutes to form a charge transport material layer-of 25 urn in thickness, whereby an electrophotographic plate was obtained. The electrophotographic characteristics of the double-layer type electrophotographic plates thus produced were measured by means of an electrostatic recording paper analyzer (SP-428, a trade name, manufactured by Kawaguchi Electric Works Co., Ltd.). In Table 1 are shown the half decay exposure sensitivities measured by using a white lap (a tungsten lamp) after corona electrical charging at negative 5 KV for 10 seconds followed by standing in the dark for 30 minutes. Table EMI21.1 <tb> <SEP> Half <SEP> decay <tb> <SEP> Oxazole <SEP> derivative <SEP> exposure <tb> <SEP> sensitivity <tb> <SEP> No. <SEP> Structural <SEP> formula <SEP> (lux.sec.) <tb> <SEP> (H3C) <SEP> 2N <tb> <SEP> N <tb> VIII <SEP> 0 <SEP> 3.0 <tb> <SEP> F <SEP> N(C3H7)2 <tb> <SEP> (H3C)2N <tb> <SEP> N <tb> IX <SEP> ee <SEP> 2.7 <tb> <SEP> F <SEP> N(CH3)2 <tb> <SEP> (H3C)2N <tb> <SEP> 0 <tb> N <tb> X <SEP> e < <SEP> 3.0 <tb> <SEP> 0 <tb> <SEP> F <SEP> N(C2H5)2 <tb> The oxazole derivative of this invention is so stable to ultraviolet light that it is not decomposed by irradiation therewith. Accordingly, at the time of use and when used for various purposes, said oxazole derivative is easy to handle and does not lose its characteristics. Further, its production is easy and therefore said oxazole derivative can be used as a photoconductive material, an electrochromium display material or the like.

Claims: WHAT IS CLAIMED IS: 1. An oxazole derivative of the formula: EMI23.1 wherein R is an alkyl group having 1 to 3 carbon atoms. 2. An oxazole derivative according to Claim 1, which is 2-(4-dipropylaminophenyl)-4-(4-dimethylaminophenyl)-5 (2-fluorophenyl) -1, 3-oxazole. 3. An oxazole derivative according to Claim 1, which is 2- (4-dimethylaminophenyl) -4- (4-dimethylamino- phenyl)-5-(2-fluorophenyl)-1,3-oxazole. 4. An oxazole derivative according to Claim 1, which is 2- (4-diethylaminophenyl) - 4- (4-dimethylaminophenyl) - 5- (2-fluorophenyl) -1,3-oxazole. 5. A process for producing an oxazole derivative of the formula: EMI23.2 wherein R is an alkyl group having 1 to 3 carbon atoms, which comprises reacting a compound of the formula: EMI24.1 with a compound of the formula: EMI24.2 wherein R is as defined above. 6. A process according to Claim 5, wherein the reaction is carried out by dissolving both the compounds of the formulae (II) and (III) in concentrated sulfuric acid and maintaining in the dark at a temperature of 200 to 700C. 7. A process for using the oxazole derivative of the formula (I) as a photoconductive material. 8. A process according to Claim 7, wherein the photoconductive material is used as a charge transport material in an electrophoto graphic plate. 9. A process according to Claim 7, wherein the photoconductive material is used as a charge transport material in a charge transport material layer in a double-layer type electrophotographic plate.

Inventors: HAYASHIDA, SHIGERU
Applicants: HITACHI CHEMICAL CO., LTD.
Application year: 1984
Main classification: C07D263
IPC codes: C07D263, G03G5, C09K9, H01L51