METHOD FOR CAUSTICIZING GREEN LIQUOR IN AN ALKALINE PULPING PROCESS

Abstract: A method for causticizing green liquor in an alkaline pulping process, advantageously in a sulphate process. The causticizing method comprises a primary causticizing process and a secondary causticizing process. In the primary causticizing process lime is added to the green liquor thereby forming white liquor and lime sludge. In the secondary causticizing process a substantial quantity of raw lime or lime otherwise of quality superior to that employed for the primary causticizing is added to the pre-causticized liquor, possibly after separation of the lime sludge, whereby after separation of lime sludge a white liquor of high causticity is obtained.

Description: Method for causticizing green liquor in an alkaline pulping process The present invention relates to a method for causticizing green liquor in an alkaline pulping process, advanta¬ geously in a sulphate process. In the alkaline pulping process, the sulphate process, part of the chemicals are recovered and to a large extent.- reused with the process economy in view. After cooking of the wood pulp black liquor is obtained, which is treated and becomes green liquor. The green liquor contains largely sodium carbonate, sodium sulphide and sodium sulphate. As the sodium carbonate is not active in the pulping process, it must be converted to active sodium hydroxide before the liquor can be used in the pulping process. The green liquor is accordingly treated with calcium hydroxide in order to convert the sodium carbonate to sodium hydroxide so far as is possible. The sulphate process also includes a lime sludge re- burning stage, in which calcium carbonate (lime sludge) from the causticizing process is burned to calcium oxide and carbon dioxide. The calcium oxide (kiln lime) is then reused in the causticizing process after being hydrated to calcium hydroxide. On the addition of calcium oxide to green 1 ' iquor in a lime slaker the lime reacts with the water pre¬ sent in the green liquor developing heat, so that calcium hydroxide is obtained according to the reaction: CaO + H 2 0 = Ca(0H) 2 + heat The calcium hydroxide and" sodium carbonate are thereafter brought to react with each other in a causticizing vessel, so as to obtain the desired sodium hydroxide and calcium carbonate. The reaction follows the formula given below: Ca(0H) 2 + Na 2 C0 3 = CaC0 3 + 2 NaOH The lime sludge is filtered out, washed and stored to be subsequently burned and returned to the process as calcium oxide. The white liquor obtained is fed to the cooking stage. The conventional causticizing process follows in principle the block diagram which is illustrated in Figure 1. The aforementioned causticization reaction is a chemical equilibrium, for which the equilibrium constant is defined as the square of the hydroxide concentration divided by the carbonate-ion concentration, viz. (Cθ ~) The magnitude of the constant indicates how far the reaction can be taken. The parameters which affect the magnitude of the constant include the composition and temperature of the liquor. It has been established that the equilibrium con¬ stant decreases very rapidly as the total alkali concen¬ tration in the liquor increases. According to the standard method SCAN-N 2:63 the components in the green and white liquors of the sulphate process are 3 expressed in terms of grammes NaOH per dm of liquor. The following definitions apply: Total titratable alkali = NaOH +■ Na 2 S + Na 2 C0 3 Active alkali = NaOH + a 2 S Effective alkali = NaOH + V 2 N 2 S Causticity = ggg + ^^ x 100 % Sulphid ty Na 2 S x 10014 NaOH + Na 2 S In the conversion of green liquor to white liquor by caus¬ ticizing it is desirable from the point of view of process economy to optimize the concentration of the sodium hydrox¬ ide which is active in the pulping process. This means that one should establish process conditions which shift the reaction equilibrium as far as possible to the right so as to achieve a high value for the causticity of the white liquor. With respect to the equilibrium conditions it is possible to achieve the causticity values which are given in Figure 2 (Mixerikompendium II, SPCI:s mixerisymposium 1982 For white liquors in the sulphate process the content of titratable alkali usually varies in the range 140-180 g NaOH/dm 3, which means that it is possible to achieve a value for causticity in the range 84-90 %. For white liquors pro¬ duced by conventional processes typical causticity values vary in the range 77-82 %. There are many reasons why satisfactory values for the caus¬ ticity of white liquor are not achieved, including variation in the quality of the kiln lime which makes exact dosing difficult. The lime should have a high content of available calcium oxide but low contents of residual carbonate and im¬ purities. The reactive properties of kiln lime vary dependin on the varying operating conditions during the lime-sludge reburning. Also variations in the composition of the green liquor influence the result of the causticizing. The present invention has as its purpose the elimination of the drawbacks of prior-known causticizing processes and the provision of a simple and efficient causticizing method yielding a more active white liquor than obtained by con¬ ventional causticizing processes; It has been possible to achieve this in a very satisfactory manner according to the present invention with a method for causticizing green liquor in an alkaline pulping pro- cess by means of adding lime to the green liquor to form white liquor and lime sludge, which is possibly first separated from the white liquor, then reburned to lime and finally returned to the causticizing process, which method is characterized in that to the white liquor or mixture of white liquor and lime sludge obtained from this causticizing process is added in a secondary causticizing process a sub¬ stantial quantity of raw lime or lime otherwise of quality superior to that which is employed for causticizing with subsequent separation and treatment of the lime sludge, by which method white liquor with high caustisity is obtained. The causticizing method of the invention differs, from the conventional method in that causticizing is performed in one or several consecutive stages, in which both kiln lime and fresh raw lime are employed with a view to forcing the causticizing reaction to a high level resulting in a more active white liquor with a higher concentration of sodium hydroxide. In contrast to conventional processes large quantities of raw lime are employed to produce the desired liquor and as a consequence a quantity of the lime sludge formed has to be removed from the process system which has the effect of diminishing the consumption of energy in the reburning of lime sludge. The various stages comprised in the process can themselves be divided into one or more substages. In the first stage of causticizing kiln lime is.added. This is slaked and reacts with the sodium carbonate in the green liquor giving rise to a lime suspension. The pre-causticized white liquor obtained is thereafter treated with fresh raw lime. Thus causticizing continues in this subsequent stage in which fresh raw lime is added to the liquor, slaked and reacts with the remaining unconverted sodium carbonate. The lime sludge formed is separated from the white liquor and the - white liquor, now with increased sodium hydroxide content and causticity, is led to the pulping process. If the lime sludge from the primary causticizing and the lime sludge from the secondary causticizing are separated separately, then the latter lime sludge, in which some un- reacted calcium hydroxide may remain, can be returned to the primary causticizing stage in order to obtain optimal utilization of the lime which thereby replaces part of the kiln lime. The principle of the causticizing method of the invention follows the -block diagram illustrated in Figure 3a and 3b. In Figure 3a the process of the invention is divided into two stages so that the lime sludge which is formed during the primary causticizing is separated from the pre-causti¬ cized white liquor before the latter is treated in the secondary causticizing stage. Hereby the raw lime added can be utilized optimally since after the secondary causti¬ cizing stage it can be separated from the white liquor and returned to the primary causticizing stage. In Figure 3b the primary and secondary causticizing are carried out in a single stage without the lime sludge which is formed during the primary causticizing being separated prior to the secondary causticizing. As a consequence the lime sludge can be separated in only one stage. The method of the invention provides material advantages in comparison with prior-known processes. Advantages which have a direct effect on the process economy include the following: - Considerable energy savings in respect of the liquor evaporation and the circulation of chemicals as a whole as a result of the increased causticity of the white liquor. - Reduced circulation of lime through the lime reburning kiln, resulting in a reduction in in the energy required in the"lime reburning stage " per ton of pulp. - Reduced energy consumption. in the cooking process because of the higher temperature of the white liquor which is a re¬ sult of the heat of reaction given off in the hydration of t lime. - Operating costs can be lowered and reliability increased since there is a reduction in the over-dosage of kiln lime, which also results in an increase in the efficiency of the conventional part of the sulphate process. - Return of the lime sludge from the secondary causticizing stag ' e to the primary causticizing stage gives some increase in the causticizing power of the combined lime mixture. - Easier separation of white liquor and at the same time a reduction in the proportion of calcium carbonate carried with the white liquor, - Saving in chemical consumption since there is a reduction in refresher chemicals because of the lower sodium losses. - The content of undesirable chemicals which accumulate in the lime circulation is reduced. Increased pulp production capacity where the capacity of the lime reburning kiln or the capacity of the chemical circulation limits the pulp production of the plant. The invention is described in greater detail in the followin The causticizing process is carried out unlike conventional processes in one or more stages in such a fashion that the relation between the kiln lime and raw lime added is materially different. The description relates primarily to a process divided into two stages and which thus comprises a primary causticizing stage and a secondary causticizing stage. It is not, however, necessary for the invention that causticizing is performed in two stages, the essential feature being that the quantities of kiln lime and raw lime are appreciably different from the practice in conventional ' processes. OMPI The first causticizing stage, primary causticizing, is per¬ formed in conventional apparatus, usually in a series of causticizing reactors, in which the green liquor and kiln lime are allowed to react. The inflowing green liquor has a temperature of approx. 90-100°C and contains titratable alkali in a concentration of approx. 140 g NaOH/dm 3. The kiln lime usually has a causticizing power of 70-80 % and is fed into the green liquor whereon the lime is hydrated. In contrast to conventional processes it is not necessary in the primary causticizing stage to add a surplus of kiln lime for the causticizing reaction, but on the contrary it is advantageous to add only such an amount of lime as to achieve a causticity of approx. 70-76 % in the white liquor produced. The causticizing can be performed according to conventional methods at atmospheric pressure or at a some¬ what elevated pressure. In order to avoid an excessively long reaction time the causticizing reactors should be equipped with powerful stirrers, so that the reaction can proceed rapidly. A reaction time of approx. 4 h is required for causticizing, but in principle it can be stopped once a suitable degree of reaction has been attained. In addition to kiln lime also lime sludge, which has been separated from the white liquor in the secondary causticizing stage and which can contain unspent lime, can be added to the green liquor in the primar causticizing stage with a view to optimal utilization of the raw lime introduced into the process. When primary causticizing has been performed the second causticizing stage can be begun directly or alternatively the lime sludge can first be separated out from the pre- causticized white liquor. In the latter case the suspension is pumped to a conventional separator apparatus which usuall comprises a thickener and a filter. In comparison with con- ventional processes sludge separation. is easier, since the sludge is more homogeneous and contains a lower concentratio of unspent calcium hydroxide as a consequence of the lime dosing principle. After separation of the lime sludge the white liquor obtained is pumped to the secondary causticizin stage. The sludge is washed and the wash water containing alkali can be returned to the process according to conven¬ tional technology. The second causticizing stage, secondary causticizing, can be carried out in the same type of apparatus as the primary causticizing, i.e. a series of causticizing reactors which are equipped with stirrers. In this stage too causticizing can be carried out at atmospheric pressure or elevated pressure. In this stage, unlike the primary causticizing stage, fresh raw lime is employed for causticizing. The raw lime is added to the white liquor from the primary causticizing either directly, in which case hydration takes place in the causticizing reactor, or indirectly so that the lime is first hydrated in a lime slaker and the sus¬ pension then fed into the causticizing reactor. The pre-causticized white liquor entering the process can have a causticity of 70-76 %, which is the most advantageous for the process from the viewpoint of economy, but the causticizing method can also be carried out with pre- causticized white liquors having other values of causticity. Following the primary causticizing the white liquor will contain unreacted sodium carbonate equivalent to approx. 24-30 % of the original sodium carbonate in the green liquor The raw lime input to the secondary causticizing should pre¬ ferably be of good quality with a high value of causticizing power. Raw lime with a causticizing power of 85-95 % is suitable for the secondary causticizing process. Depending on the value of the causticizing power of the raw lime and on the causticity of the incoming pre-causticized white liquor, a lime dosage.can be calculated so that a whit liquor of high causticity can be obtained. When the pre- causticized white liquor, which usually has a temperature of approx. 85-90°C, is mixed with the raw lime there is a tem¬ perature rise of approx. 2-6°C for the suspension as a con¬ sequence of the heat of reaction which is given off in the hydration of the lime. The secondary causticizing can be carried out in one or more stages in a reactor system. The reaction generally requires approx. 2-5 h before equilibrium is attained. In the secon¬ dary causticizing a value for the causticity of the white liquor is obtained which is in the range 85-90% in the im¬ mediate neightbourhood of the equilibrium curve for the caus¬ ticizing reaction. The suspension obtained is thereafter fed into a conventional separator apparatus for separation of the lime sludge. If the lime sludge from the primary causticizing has been separated the sludge content of the suspension is very low, so that a thickening of the suspension is advisable before e.g. filteri is carried out. Depending on the use which is intended for the lime sludge the sludge can be washed to various degrees of purity with water. If the lime sludge, which depending on the degree of reaction may contain some proportion of unspent lime, is to be returned to the primary causticizing then the alkali con¬ tent is not a decisive factor so that the sludge can be washed sparingly or not at all. The white liquor after being freed from solid particles can be pumped as cooking liquor to the cooking process. By means of the method of the invention the white liquor, since it contains a higher concentration of sodium hydroxide, will be more active in the cooking than the white liquor employed in current sulphate processes. Since raw lime is added to the process in very considerable amounts part of the lime sludge which is formed should be separated out from the process before the reburning of lime sludge to kiln lime. This removal of lime sludge also has the effect of removing impurity components which are a souce of trouble in various stages of the sulphate process, particular¬ ly in the liquor evaporation stage. In order to further illustrate the invention some examples of causticizing are described in the following. Example 1 3 A glass retort with a volume of 0.5 dm was immersed in a 3 temperate glycerine bath and 0.4 dm of green liquor was added to the flask and heated to 90°C. The green liquor con¬ tained 153 g Na 2 C0 3 /dm 3 . To the green liquor was added 26.8 g of kiln lime and the suspension was stirred with a magnetic stirrer. The primary causticizing was stopped after a reaction time of 4 h and the lime suspension was then filtered using a Bϋchner funnel coupled to a suction pump. The white liquor obtained was analyzed and found to have a causticity of 70.2 % and a sulphidity of 31.2 %. The content of titratable alkali was 3 160.4 g NaOH/dm . 44.2. of lime sludge was obtained. Of the pre-causticized white liquor obtained 350 ml of sol¬ ution was transferred to the empty glass retort and heated to 83°C. To the solution was added 9.2 g fresh raw lime, which had a causticizing power of 89 %• After the addition of the lime the temperature of the suspension rose in a few minutes to 91°C as a consequence of the heat of reaction of the hydration of the lime. The secondary causticizing pro¬ ceeded under stirring for 6 -hours and samples for analysis were taken regularly from the suspension. The causticity of the white liquor was determined as a function of the reaction time and the following results were obtained: 0.5 h, 80.7 % ', 1.0 h, 82.2 %; 2.0 h, 83.6 %; 3.0 h, 84.6 %; 6.0 h, 85.9 %. After the causticizing was carried out the suspension was filtered. The content of unspent calcium oxide in the lime sludge was found to be 1.7 %-by analysis. The content of 3 titratable alkali was measured as 168.9 g NaOH/dm at the end of the experiment. 7.5 g of lime sludge was obtained. Example 2 In an experiment similar to that of Example 1 primary and secondary causticizing were carried out with the following parameters changed. In primary causticizing 30.7 g of kiln lime was added to the green liquor, as a result of which the causticity of the liquor increased to 80.5 % and its sulphidity was 28.2 %. The content of titratable alkali in the white liquor obtained was 164.0 g NaOH/dm3. The primary causticizing yielded 51.1 g lime sludge. The secondary causticizing was carried out with 322 ml of solution, to which 5.5 g raw lime was added. The temperature then rose from 83 C to 86 C in the suspension. The causticity of the white liquor obtained after 6 hours was 86.0 %, its . sulphidity 24.7 % and content of titratable alkali 158 g 3 NaOH/dm . The secondary causticizing yielded 9.2 g lime sludge, which contained 7.8 % unspent calcium oxide. Example 3 3 3 To a glass vessel with a volume of 5 dm was added 4.0 dm 3 of green liquor containing 153 g a p CO^/dm . The solution CΛΪPI was heated to 90°C, after which 268 g of kiln lime was added. The temperature of the suspension rapidly rose to 100°C. The primary causticizing was carried out for 4 hours, after which the suspension was filtered. The white liquor obtained had a causticity of 69.0 %, sulphidity 31.0 % and a content of tit¬ ratable alkali of 156.4 g NaOH/dm 3 . 3 The secondary causticizing was carried out with 3.75 dm of solution, to which 104.2 g fresh raw lime was added whereon the temperature of the suspension rapidly rose from 85 C to 90°C. The causticizing power of the lime was 89 %. Causti¬ cizing was carried out for 5 hours, after which the suspensio was filtered. The white liquor obtained had a causticity of 86.2 % and sulphidity of 25.0 % . The secondary causticizing yielded 147 g of lime sludge. Example 4 3 A glass retort with a volume of 0.5 dm was immersed in a 3 temperate glycerine bath and 0.4 dm of green liquor was added to the retort and heated to 90°C. The green liquor 3 contained 153 g a C /dm . To the green liquor was added 26.5 g of kiln lime for primary causticizing. After 4 hours reaction under stirring a sample was taken from the suspen¬ sion for analysis, whereon it was found that the liquor had a causticity of 72,3 %, sulphidity 29.3 % and a content- of titratable alkali of 181.6 g NaOH/dm 3 . Without filtering off the lime sludge formed 5.9 g of fresh raw lime was added to the suspension. The causticizing power of the raw lime was 89 %. The temperature of the suspension then rose rapidly from 85°C to 87.5°C as a consequence of the heat of reaction from the slaking of the lime. The secondary casuticizing pro¬ ceeded under stirring for 3 hours and samples of the suspen¬ sion were taken for analysis. The causticity of the white liquor was determined as a function of the reactio n time and the following results were obtained: 0.5 h, 82.9 %; 1.0 h, 83.8 " %; 2.0 h r 84.3 %; 3.0 h, 84.9 %. After the causticizing was performed the suspension was filtered. The amount of sludge obtained was 54.3 g and its content of unspent cal- cium oxide was 0.06 % after washing with 1.0 dm 3 of water. The content of titratable alkali in the white liquor was 169.6 g NaOH/dm 3 .

Claims: Claims 1. A method for causticizing green liquor in an alkaline pulping process by the addition of lime to said green liquor to form white liquor and lime sludge, which latter is possibly first separated from said white liquor and then reburned to lime and finally returned to the causticizing process, characterized in that in a secondary causticizing process a substantial quantity of raw lime or lime other¬ wise of a quality superior to that employed for the primary causticizing is added to the white liquor or mixture of white liquor and lime sludge obtained from the primary causticizing process with subsequent separation and treat¬ ment of the lime sludge, whereby white liquor of high causticity is obtained. 2. A method according to claim 1, characterized in that the primary causticizing is carried out using a stoichio- metric quantity of lime or a deficit of lime in relation to the soda content of the green liquor. 3. A method according to claim 1 or 2, characterized in that the lime sludge which is separated after the secondary causticizing, in the case that said sludge consists of lime sludge formed in both the primary causticizing and secondary causticizing, is partially or entirely reburned to lime and returned to the primary causticizing stage. 4. A method according to claim 1 or 2, characterized in that the lime sludge which is separated after the secondary causticizing, in the case that said sludge consists only of lime sludge formed during the secondary causticizing, is re¬ turned to the primary causticizing stage with or without undergoing washing. 5. A method according to any of the preceding claims, characterized in that the lime sludges of different qualities _ C ΪP obtained from different stages of causticizing or a part of these sludges are mixed together and treated further. 6. A method according to any of the preceding claims, characterized in that lime sludge formed during the primary causticizing and/or secondary causticizing is separated out from the process for the purpose of reducing contaminating salt components which are a source of trouble in the pulping process.

Inventors: DAHLBERG KJELL, JANSSON GOERAN, LEIRITIE MARKKU, SUNDSTROEM CHRISTER, DAHLBERG, KJELL, JANSSON, GOERAN, LEIRITIE, MARKKU, SUNDSTROEM, CHRISTER
Applicants: PARTEK AB, OY PARTEK AB
Application year: 1984
Main classification: D21C11
IPC codes: D21C11