AN APPARATUS FOR PULLING A SINGLE CRYSTAL

Abstract: An apparatus for pulling a single crystal by CZ method or LEC method includes heating means, a heater is divided into an upper heater and a lower heater, each heater con­ sisting of a rectangular waveform coil whose width direction is vertical. These heaters are preferably separated in the vi­ cinity of the liquid-solid interface. Using this apparatus, a single crystal with a decreased dislocation density can be obtained.

Description: A APPARATUS FOR PULLING A SINGLE CRYSTPL" BACKGROUND OF THE INVENTION 1. Field of the Invention This invention relates to an apparatus for pulling a single crystal by the Czochralski method (hereinafter referred to as OZ method) or by the Liquid Encapsulated Czochralski method (hereinafter referred to as LEC method). 2. Description of the Prior Art In an apparatus for pulling a single crystal by CZ method or LEC method as shown in Fig. 1, raw material melt 4 (e.g. GaAs) is charged in crucible 3, the surface of which is optionally covered with B203 melt 5 (in the case of LEG method), and seed crystal 6 fitted to pull rod 8 is immersed in the surface of melt 4, wetted and then pulled up to obtain single crystal 7 (e.g. GaAs). 1 is a heater in a furnace, 2 is a susceptor (carbon) and 9 is a crucible support shaft (lower shaft). In this case, one heater has been used so as to hold a predetermined temperature distribution in the furnace according to the prior art, but this fails to obtain a high quality single crystal because of the following reasons: The temperature distribution on the central axis (vertical direction) of single crystal 7 varies with the time when seeding is carried out, when single crystal 7 comes out of B205 5 and when the most part of single crystal 7 is pulled up, and for example, the dislocation density (EPD) is thus increased from the seed end to the tail end to a greater extent. As single crystal 7 is pulled out on 3203 melt 5, single crystal 7 is cooled by the atmospheric gas (inert gas such as N2 gas) and the temperature gradient in the axial direction of single crystal 7 is increased to cause thermal stress and to increase dislocation density. When using one heater, however, it is impossible to controllably heat single crystal 7 and raw material melt 4 independently and to hold constant the temperature distribution in the vicinity of the solid-liquid interface from the start to the end of crystal growth. Accordingly, the single crystal cannot be held in a low dislocation density from the seed end to the tail end thereof by the use of one heater as in the prior art. SUMMARY OF THE INVENTION It is an object of the present invention to provide an apparatus for the growth of single crystals, whereby at least some of the above-described disadvantages of the prior art can be overcome. It is another object of the present invention to provide an apparatus for the Czochralski growth of compound single crystals in which the temperature distribution in the vertical direction can readily be controlled from seeding to pulling-up of a single crystal. It is a further object of the present invention to provide an apparatus for pulling a single crystal with a low dislocation density from the seed end to the tail end of the single crystal. The present invention subsists in an apparatus for pulling a single crystal by CZ method, and is characterized in that a heater provided at the side of a furnace is divided into two upper and lower heaters, each heater consisting of a rectangular waveform coil whose width direction is vertical. BRIEF DESCRIPTION OF THE DRAWINGS The accompanying drawings illustrate the principles and merits of the present invention in more detail. Fig. 1 is a vertical-sectional view of one example of an apparatus for pulling a single crystal according to the prior art. Fig. 2 is a vertical-sectional view of one embodiment of an apparatus for pulling a single crystal according to the present invention. Fig. 3(a) and (b) are perspective views of examples of the upper heater and lower heater as shown in Fig. 2. Fig. 4 is a graph showing the etch pit density distributions on the seed ends and the tail ends of single crystals prepared according to the present invention and the prior art. DETAILED DESCRIPTION OF THE INVENTION The inventors have made various efforts to develop an apparatus for the Czochralski growth of a single crystal with a lowered dislocation density from the seed end to the tail end of the single crystal and consequently have found that such a single crystal can be obtained by the use of a single crystal pulling apparatus provided with two stage heaters divided up and down, whereby the temperature distribution in the vertical direction can readily be controlled. The present invention is based on this finding. Single crystals pulled by the apparatus of the present invention include compounds of Group III-V elements of Periodic Table (e.g. GaAs, InAs, Inp, etc.), compounds of Group II-VI elements (e.g. ZnSe, etc.) or their mixed crystals, elementary semiconductors such as Si and Ge, and other single crystals of oxides, nitrides, carbides and the like. In particular, the apparatus of the present invention can be applied with larger merits to the LEC method in which control of the temperature gradient is difficult because of pulling a single crystal at a high pressure, e.g. 2 to 60 atm using B203 melt. The present invention will now be illustrated as to one preferred embodiment referring to the accompanying drawings. Fig. 2 is a vertically sectional view of one example of the apparatus of the present invention, in which the same numerals show the same parts as those of Fig. 1. The difference between Fig. 1 and Fig. 2 is that the heating means provided at the side of a furnace is divided at a part of the side of crucible 3 into a two-stage heater, comprising an upper heater 11 and a lower heater 12. Upper heater 11 is used mainly for the purpose of controlling the temperature in the vicinity of the solid-liquid interface and that of pulled single crystal 7, while lower heater 12 is used mainly for the purpose of controlling the temperature of raw material melt 4. Upper heater 11 has such a structure as shown in Fig. 3(a), while lower heater 12 has a structure as shown in Fig. 3(b). Upper heater 11 consists of a rectangular waveform coil 13 wound in a cylindrical form along the outside of crucible 3, the width direction (direction of longer side 14) of the coil being vertical, i.e. in the axial direction of crucible 3. End parts 15 and 15 of coil 13 extend downwards along the outside of lower heater 12, form fixed legs of coil 13 and connect with respective terminals, On the other hand, lower heater 12 consists of rectangular waveform coil 16 wound in a funnel form along the outside of the side and bottom of crucible 3, the width direction (direction of longer side 17) of the coil being vertical, i.e. in the axial direction of crucible 3. End parts 18 and 18 form fixed legs of coil 16 and connect with respective terminals. The above-described coils may be made of graphite, carbon or glassy carbon. When upper and lower heaters 11 and 12 are constructed of such rectangular waveform coils 13 and 16, the temperature of raw material melt 4 and single crystal 7 may readily be stabilized. The heating coils may be of plate or strip form with a large surface area. The temperature distribution can readily be changed by changing the dimensions of the heating coils. Upper and lower heaters 11 and 12 may be controlled individually or in combination, whereby the temperature in the vertical direction can readily be controlled to give a predetermined temperature distribution from seeding of a single crystal to the finish of pulling the same. One preferred embodiment of pulling a single crystal by means of the apparatus of the present invention will be given below: Firstly, the power ratio (calorific power) of heaters 11 and 12 is changed to seek conditions capable of giving a small temperature gradient (e.g. 5 to 100 OC/cm) in the central portion of B203 melt 5 in the vertical direction. Under these conditions, seeding is started and when single crystal 7 comes out of B203 melt 5 and is exposed to a high pressure gas, single crystal 7 is warmed by upper heater 11 with observing the growth of the diameter of single crystal 7 and pulling of the single crystal is continued with keeping the temperature gradient in the vertical direction near the solid-liquid interface is maintained at, for example, 5 to 100 OC/cn. When the power of upper heater 11 is increased and single crystal 7 becomes smaller, the power of lower heater 12 is somewhat decreased and pulling is continued to maintain the diameter of single crystal 7. The power ratio as described above depends on the heater structure, but, for example, it is in the range of an upper to lower ratio of 1 to 2 to obtain a temperature gradient of 5 to 60 OC/cm, Since a heater for heating the inside of a furnace is divided in two stages which can be controlled individually or in combination as described above, control of the temperature distribution during growth of a single crystal can readily be carried out to hold constant the diameter of the single crystal grown. The apparatus for pulling a single crystal according to the present invention, as illustrated above, has the following advantages: Since a heater provided for heating the inside of a furnace is constructed of two stage heaters divided up and down, which can be controlled independently, it is possible to control the temperature gradient freely in the vertical direction in the vicinity of the solidliquid interface and to keep small and constant the temperature gradient from the start to the end of pulling the single crystal. In addition, since the each heater consists of a rectangular waveform coil whose width direction is vertical, control of the temperature of a raw material melt and a single crystal is readily feasible due to the larger heating area of the coil and the temperature gradient at the solid-liquid interface can be kept small and correctly constant from the start to the end of the crystal growth, thus preventing formation of dislocations due to thermal stress. Therefore, the use of the apparatus according to the present invention results in production of a high quality single crystal with a low dislocation density and a uniformity of dislocation densities from the seed end to the tail end of the single crystal in a high yield. Moreover, it is important that, for example, an LED fabricated on a wafer with a large dislocation density has a short life, a semi-insulating single crystal of GaAs (undoped or Cr-doped) has a strong relationship between the dislocation density and resistance and the yield of a device is greatly affected by the dislocation density. Accordingly, the apparatus of the present invention may advantageously increase the yield of such devices and has important significances in these uses. The following example is given in order to illustrate the present invention without limiting the same. Example GaAs single crystal was pulled using the apparatus of the present invention, as exemplified in Fig. 2. This apparatus had the following dimensions: Length of coil 13 of upper heater 11 = 70 mm Total height of upper heater 11 = 250 mm Height of coil 16 of lower heater 12 = 150 mm Length of vertical part of coil 16 = 100 mm Inner diameter of coil = 190 mm8 Outer diameter of coil = 210 =6 Material of coil = carbon About 5 kg of GaAs polycrystal raw material and 500 g of B203 were charged in a quartz crucible of 150 mm in diameter, melted and pulled in a 001) direction at a pressure of 10 kg/cm2 in a furnace, a pulling rate of 12 mm/hr, a crucible raising rate of 1 mm/hr, a pull rod 8 and crucible support rod 9 revolving rate of 10 rpm and a temperature gradient of about 20 OC/cm, the temperature gradient being in the vertical direction near the solidliquid interface during seeding, thus obtaining a GaAs single crystal of 50 mm in diameter and about 500 mm in length. During the growth of the single crystal, the temperature gradient was held at 20 00/cam. The electric power applied to the both heaters was respectively 10 KW. For comparison, a single crystal was similarly prepared but using a pulling apparatus of the prior art, provided with only one heater. (001) wafers cut from the seed end (F) and the tail end (B) of the single crystal were subjected to etching with molten KOH and to measurement of the etch pit density (EPD), thus obtaining results as shown in Fig. 4, in which solid lines showed EPD when using the two stage heaters of the present invention and dotted lines showed EPD when using the one stage heater of the prior art; Ordinate: EPD (cm 2) and Abscissa: distance (mm) from center of wafer. EPD was measured at points inO0I > direc tion on (001) wafers. The mean EPD was as shown in Table 1: Table 1 Mean EPD (x 104 cm 2) Seed End (F) Tail End (B) Present Invention 0.6 0.9 Prior Art 0.9 5 As is evident from the results of Fig. 4 and Table 1, EPD is lower and is scarcely changed from the seed end to the tail end in the present invention, while EPD is remarkably increased from the seed end to the tail end in the prior art.

Claims: CLAIMS: 1. An apparatus for pulling a single crystal by a Czochralski method, characterized in that a heater provided at the side of a furnace (3) is divided into two upper and lower heaters (11,12) each heater comprising a rectangular waveform coil whose width direction is vertical. 2. Apparatus according to claim 1, wherein the upper heater (11) consists of a rectangular waveform coil (13) wound in a cylindrical form along the outside of a crucible (3), the width direction of the coil being in the axial direction of the crucible and the end parts of the coil extending downward along the outside of the lower heater, and the lower heater consists of a rectangular waveform coil (16) wound in a funnel form along the outside of the side and bottom of the crucible, the width direction of the coil being in the axial direction of the crucible. 3. Apparatus according to claim 1 or claim 2, wherein the upper heater mainly controls the temperature of a solid-liquid interface and the temperature of the pulled single crystal and the lower heater mainly controls the temperature of a raw material melt. 4. A process for pulling a single crystal by CZ method or LEC method, characterized in that the pulling is carried out while keeping the temperature gradient in 5 to 100 OC/cm at least in the vicinity of the solid-liquid interface.

Inventors: HOSHIKAWA, KEIGO, KAWASAKI, AKIHISA OSAKA WORKS OF SUMITOMO ELECTRIC, KISHI, MASAO OSAKA WORKS OF SUMITOMO ELECTRIC, KOTANI, TOSHIHIRO OSAKA WORKS OF SUMITOMO ELECTRIC, MIYAZAWA, SHINTARO, NAKAI, RYUSUKE OSAKA WORKS OF SUMITOMO ELECTRIC
Applicants: NIPPON TELEGRAPH AND TELEPHONE CORPORATION, SUMITOMO ELECTRIC INDUSTRIES LIMITED
Application year: 1984
Main classification: C30B15
IPC codes: C30B27, C30B15, H01L21