CATALYST COMPOSITIONS

Abstract: Catalyst compositions comprising a crystalline aluminium silicate having a pore diameter larger than 0.7 nm and at least an equal quantity by weight of a crystalline metal silicate having after one hour's calcination in air at 500°C an X-ray powder diffraction pattern in which the strongest lines are the four lines mentioned in Table A and having in the formula which represents the composition of the silicate expressed in moles of the oxides and in which, in addition to SiO₂, one or more oxides of an alkali metal (M) and one or more oxides of a trivalent metal X (Al, Fe, Ga, Rh, Cr and Sc) are present, the M₂O/X₂O₃ molar ratio higher than 0.9 and the SiO₂/X₂O₃ molar ratio higher than 10. The catalyst compositions are advantageously used in the production of gasoline by cracking hydrocarbon mixtures boiling above the gasoline range and allow a higher yield of cracked gasoline or a lower coke make.

Description: CATALYST CCMPCSITICNS The invention relates to catalyst compositions suitable for producing gasoline fran a hydrocarbon mixture boiling above the gasoline range. For the production of gasoline from hydrocarbon mixtures boiling above the gasoline range ample use is made of catalytic cracking. Said gasoline production by catalytic cracking is carried out by contacting the hydrocarbon mixture to be cracked at an elevated temperature with a cracking catalyst. Generally, catalytic cracking on a commercial scale is conducted in a continuous process by using an arranged apparatus of a vertically disposed cracking reactor and a catalyst regenerator. Hot regenerated catalyst caning fran the regenerator is suspended in the oil to be cracked and the mixture is passed through the cracking reactor in an upward direction. The catalyst deactivated by the deposition of coke is separated fram the cracked product and stripped, after which it is transferred to the regenerator, where the coke deposit on the catalyst is burnt off. The cracked product is divided into a light fraction having a high C3 and C4 olefin content, a gasoline fraction, and several heavier fractions such as a light cycle oil, a middle cycle oil, a heavy cycle oil and a slurry oil. In order to raise the gasoline production, one or rrore of the heavier product fractions may be recirculated to the cracking reactor and the C3 and C4 olefins present in the light fraction may be alkylated with isctutane to form alkylation gasoline. In catalytic cracking on a carmercial scale an important consideration is for the amount of heat released in the regenerator to correspond substantially with the amount of heat required in the cracking reactor, thus allowing the process to be operated without the necessity to install additional heating or cooling devices. As catalysts for catalytic cracking crystalline aluminium silicates having relatively wide pores, i.e. pore diameters larger than 0.7 nm (7 A) have been found to be very suited. When the value of a catalytic cracking process for the production of gasoline is to be assessed, it is not only the ascent of cracking gasoline obtained in the process that is to be taken into account, but also the amount of gasoline that can be prepared by alkylation of the C3 and C4 olefins present in the light product fraction. An attractive base on which to compare catalytic cracking processes for the production of gasoline with one another is the total amount of gasoline (cracking gasoline + alkylation gasoline) which can be obtained by the various processes. When investigating the use of crystalline aluminium silicates having pore diameters larger than 0.7 nm (7 A) as catalysts for the preparation of gasoline by catalytic cracking, it was found that considerably better results can be obtained by using a catalyst composition which in addition to the aforementioned crystalline aluminium silicate with wide pores contains a crystalline aluminium silicate with narrow pores and which has a special structure. Comparison of the results obtained in a cracking process carried out by using a crystalline aluminium silicate with wide pores as catalyst and those obtained in a cracking process carried out by using the afore-mentioned catalyst composition shows that the use of said catalyst composition results in a cracking gasoline of a higher quality. It is true that this gain in quality is achieved at the expense of the cracking gasoline production, which is lower when the catalyst composition is used, but this lover yield of cracking gasoline is amply compensated for by the fact that the use of the catalyst composition leads to a light product fraction which has a considerably higher C3 and C4 oleo in content. In summary it may be stated that when the catalyst composition is used the total amount of gasoline is laeeer than when a catalyst is used which contains a crystalline aluminium silicate having a pore diameter larger than 0.7 nm (7 A), but in which no narrow pore crystalline metal silicate of a special structure is present. It is assumed that the improved quality of the cracking gasoline which occurs when the catalyst composition is used may be ascribed to the fact that the narrow pore crystalline metal silicate of a special structure serves as an active cracking catalyst for further cracking n-paraffins with a low octane number boiling in the gasoline range (which have primarily been formed fran the feed by cracking) to form C3 and C4 olefins. In the process the production of cracking gasoline will naturally fall while the octane number thereof will rise. The crystalline metal silicates with narrow pores and of a special structure are characterized in that after one hour's calcination in air at 500 OC they have the following properties: a) an X-ray powder diffraction pattern in which the strongest lines are the four lines mentioned in Table A TABLE A d( ) 11.1 + 0.2 10.0 + 0.2 3.84 + 0.07 3.72 + 0.06, and b) in the formula which represents the composition of the silicate expressed in moles of the oxides and which, in addition to SiO2, includes one or more oxides of a trivalent metal X, chosen from aluminium, iron, gallium, rhodium, chromium and scandium, the SiO2/X203 molar ratio is higher than 10. The crystalline metal silicates of a special structure may be prepared starting frcm an aqueous mixture comprising the following compounds: one or more silicon compounds, one or more compounds containing a monovalent organic cation (R) or from which such a cation is formed during the preparation of the silicate, one or more compounds in which a trivalent metal X occurs and, if desired, one or more compounds of an alkali metal (M). The preparation is carried out by maintaining the mixture at an elevated temperature until the silicate has formed, followed by washing, drying and calcination of the silicate crystals. The various ccmpounds fran which the silicates are prepared should be present in the aqueous mixture in the following ratios, expressed in moles of the oxides: M2O : SiO2 < 0.35 R2O : SiO2 = 0.01 - 0.5, SiO2 : X2o3 > 10 and H2O : SiO2 5 5-100. If in the preparation of the crystalline metal silicates of a special structure the starting material is an aqueous mixture in which one or more alkali metal compounds are present, the crystalline silicates obtained will contain alkali metal. Depending on the concentration of alkali metal compounds in the aqueous mixture the crystalline silicates obtained may contain more than 1 Fw alkali metal. Since the presence of alkali metal in the crystalline silicates of a special structure has a very unfavourable influence on their cracking activity, only crystalline metal silicates of a special structure whose M20/X203 molar ratio is lower than 0.1 are eligible for use in the aforementioned catalyst compositions. Reduction of the alkali metal content of the crystalline silicates of a special structure prepared in the presence of an alkali metal compound may very suitably be effected by treating such silicates once or several times with a solution of an ammonium carpound Alkali metal ions are then exchanged for NH4+ ions and the silicate converted to the NH4+ form. The NH4 form of the silicate thus obtained is converted to the H form by calcination. Although the use of the process described hereinbefore, wherein the cracking step is carried out using a catalyst composition containing a crystalline metal silicate of special structure which is substantially in the H+ form allows a higher production of gasoline, it is still a drawback of the process that it requires an additional process step: for the higher gasoline yield is obtained only when, following the cracking process, an additional portion of gasoline is produced by alkylation of the C3 and C4 olefins formed. However, practical application urgently needs a cracking process which in itself leads to higher gasoline production without a second process step being required. Continued research into this subject has now revealed that very attractive results can be achieved in the production of gasoline by the catalytic cracking of hydrocarbon mixtures boiling above the gasoline range, when in the afore-mentioned catalyst compositions the crystalline metal silicate of a special structure is substantially in the M+ form instead of substantially in the H+ form. In the present description a crystalline metal silicate of a special structure which is substantially in the M form should be taken to be a silicate for which in the formula which represents the composition expressed in moles of the oxides the M2o/X2o3 molar ratio is higher than 0.9. It has been found that when a catalyst composition is used which, in addition to a crystalline aluminium silicate having a pore diameter larger than 0.7 nm (7 A) (for the sake of brevity hereinafter referred to as component I), contains a crystalline metal silicate of a special structure (for the sake of brevity hereinafter referred to as component II), which component II is substantially in the M+ form, a higher production of cracking gasoline and less deposition of coke on the catalyst composition is obtained than when a catalyst composition is used which contains a component I but no component II. The advantages of the use of catalyst compositions according to the invention, viz. higher yields of cracking gasoline and less coke deposit on the catalyst composition in one process step, are interchangeable. By a suitable choice of the conditions under which to carry out the catalytic cracking process, it is possible to realize considerably less coke deposit on the catalyst composition at a substantially unchanged gasoline production, or a considerably higher gasoline production at a substantially unchanged degree of coke deposit. The e aspect of less coke deposit an the catalyst composition is of special interest when heavier feeds are to be processed in the catalytic cracker. It is common knowledge that, in general, the use of heavier feeds leads to more coke deposit on the catalyst. Mbre coke on the catalyst means more heat in the regenerator, which destroys the heat balance in the cracking unit, so that additional cooling means have to be provided for. The use of a catalyst composition which shows less tendency towards the formation of coke deposit offers an excellent solution to this prablem. The higher yield of cracking gasoline when using the catalyst composition according to the invention has been found to be accanpanied also with higher yields of C3 and C4 olefins. Naturally the latter aspect is jirportant when C3 and C4 olefins obtained as a by-product in the cracking process are to be converted into gasoline by a further alkylation step. As regards the proportions between components I and II in the catalyst compositions according to the invention, in order to achieve the effects mentioned hereinbefore the quantities by weight of canpanent II should be at least equal to that of catonent I. These catalyst compositions are novel. The present invention therefore relates to catalyst positions ccmprising a component I and at least an equal quantity by weight of a canponent II, catpent I being a crystalline aluminium silicate having a pore diameter larger than 0.7 nm (7 ) and component II being a crystalline metal silicate which after one hour's calcination in air at 500 C has the following prppeties: : a) an X-ray powder diffraction pattern in which the strongest lines are the four lines mentioned in Table A, and b) in the formula which represents the composition of the silicate expressed in moles of the oxides and in which, in addition to SiO2, one or nore oxides of an alkali metal (M) and one or more oxides of a trivalent metal X chosen from aluminium, iron, gallium, rhodium, chromium and scandium are present, the M20/X203 molar ratio is higher than 0.9 and the SiO2/X203 molar ratio is higher than 10. The present invention further relates to the use of catalyst compositions according to the invention in the production of gasoline by cracking hydrocarbon mixtures boiling above the gasoline range. The catalyst compositions of the invention comprise car ponents I and II. It is preferred that these components are present in the catalyst compositions in combination with a porous matrix, such as silica, alumina, magnesia, zirconia or mixtures thereof. Especially preferred are catalyst compositions 10-50 %w of which consists of components I and II and the remainder of a porous matrix. Either of components I and II may be combined with a porous matrix individually. Components I and II may also be combined with a porous matrix together. The ratio in which components I and II are present in the catalyst compositions in accordance with the invention may vary within wide limits, provided that the quantity by weight of component II is at least equal to that of component I. Preference is given to catalyst compositions containing at most 25 and in particular at most 15 parts by weight (pbw) of ccmpanent II per part by weight of cxnx=lent I. As components I the usual crystalline aluminium silicates having a pore diameter larger than 7 known as cracking catalysts are eligible. Examples of such silicates are natural and synthetic faujasites both of the X and of the Y-type and zeolite L. Preference is given to catalyst compositions containing as component I a synthetic zeolite Y and in particular a synthetic zeolite Y in which ions of rare earth metals are present. Catalyst component II is a crystalline metal silicate of a special structure containing one or more trivalent metals X in such quantities that the SiO2/X203 molar ratio is higher than 10. Preference is given to components II in which the SiO2/X203 molar ratio is higher than 50. Preference is further given to conFcrents II in which the SiO2/X203 molar ratio is lower than 2000 and in particular lower than 1500. As regards the metals X present in components II, preference is given to components II in which aluminium and/or iron are present as metals X. The crystalline metal silicates which are present in the catalyst composition as component II are defined, inter alia by the X-ray powder diffraction pattern, which they show after one hour's calcination in air at 500 OC. In this pattern the strongest lines should be the four lines mentioned in Table A. The complete X-ray powder diffraction pattern of a typical example of such a silicate after one hour's calcination in air at 500 OC is given in Table B. TABLE TB B d( ) Rel. int. d( ) Rel. int. 11.1 100 3.84 (D) 57 10.0 (D) 70 3.72 (D) 31 8.93 1 3.63 16 7.99 1 3.47 < 1 7.42 2 3.43 5 6.68 7 3.34 2 6.35 11 3.30 5 5.97 17 3.25 1 5.70 7 3.05 8 5.56 10 2.98 5.35 2 2.96 3 4.98 (D) ' 6 2.86 2 4.60 4 2.73 2 4.35 5 2.60 2 4.25 7 2.48 3 4.07 2 2.40 2 4.00 4 (D) = doublet The crystalline metal silicates present in catalyst compositions according to the invention as components II have a M2o/x2o3 molar ratio higher than 0.9. The introduction of alkali metal ions in order to obtain such crystalline silicates may be performed in various ways. In the synthesis of the silicate the starting material may be an aqueous mixture containing one or more compounds of an alkali metal. In that case the alkali metal ions present in the aqueous mixture will find their way at least partly into the silicate. The silicate may also be subjected, after calcination, to one or more treatments with a solution of an alkali metal compound in which the exchangeable cations present in the silicate are replaced by alkali metal ions. For use as components II in catalyst compositions according to the invention preference is given to crystalline metal silicates which have been prepared starting from an aqueous mixture containing one or more ccmpounds of an alkali metal, and which after calcination have been treated once or several times with a solution of an alkali metal compound. For use as components II in catalyst compositions according to the invention preference is given to crystalline metal silicates which are substantially completely in the alkali metal form, i.e. that the exchangeable cations present in the silicate have been replaced substantially by alkali metal ions. For the preparation of such silicates an after-treatment of the silicate with a solution of an alkali metal compound is necessary, since during calcination the organic cations introduced when the silicate was synthesised are converted into hydrogen ions. During the after-treatment with a solution of an alkali metal around these hydrogen ions, among the rest, are replaced by alkali metal ions. Preference is given to catalyst oomponents II in which the alkali metal ions are sodium ions. The present invention also relates to the use of the catalyst compositions according to the invention for the productian of gasoline by cracking hydrocarbon mixtures boiling above the gasoline range. Examples of suitable feeds which can be used for the production of gasoline by catalytic cracking are atmospheric gas oils, vacuum gas oils, deasphalted distillation residues and mixtures thereof. The feed used by preference is a gas oil. Suitable conditions for the catalytic cracking are a temperature of 250-650 OC and preferably of 450-600 OC, a pressure of 1-10 bar and preferably of 1-7.5 bar, a space velocity of 1-250 and preferably of 5-150 kg feed per kg catalyst composition per hour and a catalyst composition/feed weight ratio of 1-25 and preferably of 1.5-20. The invention is now illustrated by the following Example. Example Two crystalline aluminium silicates (silicates 1 and 2) were prepared by heating mixtures of sodium hydroxide, tetra prcpylammonium hydroxide, sodium aluminate and amorphous silica in water in an autoclave under autogenous pressure for 24 hours at 150 OC. After cooling of the reaction mixtures the silicates formed were filtered off, washed with water until the pH of the wash water was about 8 and dried at 120 OC. After one hour's calcination in air at 500 OC silicates 1 and 2 had the following properties: a) an X-ray powder diffraction pattern substantially corresponding with that mentioned in Table B, b) a SiO2/A1203 molar ratio of 130 for silicate 1 and 1000 for silicate 2. Starting from silicates 1 and 2, silicates 1* and 2* were prepared, by calcining silicates 1 and 2 respectively, at 500 "C, boiling with a 1.0 molar sodium nitrate solution, washing with water, boiling again with a 1.0 molar sodium nitrate solution and washing, drying at 120 OC and calcination at 500 OC. The Na2O/A1203 molar ratio of silicates 1* and 2* was 1. Starting fran a catalyst composition A two catalyst compositions (B and C) were prepared by mixing catalyst composition A with silicate 1* and silicate 2*, respectively. Catalyst compositions A-C had the following compositions: Catalyst composition A: a mixture of a faujasite and a silicaalumina matrix in a 1:13 weight ratio. Catalyst composition B: a mixture of catalyst composition A and silicate 1* in a 1:1 weight ratio. Catalyst composition C: a mixture of catalyst composition A and silicate 2* in a 1:1 weight ratio. Catalyst compositions A-C were used in five experiments (Experiments 1-5) for the production of gasoline by cracking a vacuum distillate obtained in the vacuum distillation of an atmospheric distillation residue from a crude mineral oil. In the experiments the feed was contacted at a temperature of 524 OC and at atmospheric pressure separately with each one of the catalyst compositions A-C. The other conditions under which the experiments were carried out and the results of the experiments are given in Tables C-E. The yields given are yields calculated on feed. TABLE C Experiment No. 1 2 Catalyst composition A B Space velocity, kg.kg l.h 1 15.9 7.9 Catalyst composition/feed weight ratio 3.8 7.6 Yield of C5-221 OC gasoline, %w 43.5 50.2 Quantity of coke formed, %w 3.8 3.8 Yield of C3 and C4 olefins, %w 8.1 9.8 TABLE D Experiment No. 3 4 Catalyst composition A C Space velocity, kg.ks'l.h1 33.3 13.1 Catalyst composition/feed weight ratio 1.8 4.6 Yield of C5-221 C gasoline, %w 34.4 40.7 Quantity of coke formed, Fw 2.1 2.1 Yield of C3 and C4 olefins, %w 4.2 5.5 TABLE E Experiment No. 5 4 Catalyst composition A C Space velocity, kg.kg l.h 1 18.0 13.1 Catalyst ccmposition/feed weight ratio 3.3 4.6 Yield of C5-221 OC gasoline, %w 40.7 40.7 Quantity of coke formed, %w 3.5 2.1 Of the experiments listed in Tables C-E only Experiments 2 and 4 are experiments according to the invention. The other experiments are comparative and fall outside the scope of the invention. Comparison of the results of Experiments 1 and 2 given in Table C as well as of the results of Experiments 3 and 4 given in Table D shows that at equal quantities of coke formed on the catalyst the use of a catalyst composition according to the invention leads to a considerably higher yield both of cracking gasoline and of C3 and C4 olefins. Cararison of the results of Experiments 4 and 5 given in Table E shows that at equal yields of cracking gasoline the use of a catalyst composition according to the invention results in a considerably lower quantity of coke formed on the catalyst.

Claims: CLAIMS 1. Catalyst compositions, characterized in that they comprise a ccrmpcent I and at least an equal quantity by weight of a component II, that carpoent I is a crystalline aluminium silicate having a pore diameter larger than 0.7 nm (7 A) and that component II is a crystalline metal silicate which after one hour's calcination in air at 500 C has the following properties: a) an X-ray powder diffraction pattern in which the strongest lines are the four lines mentioned in Table A TABLE A d( ) 11.1 + 0.2 10.0 + 0.2 3.84 + 0.07 3.72 + 0.06, and b) in the formula which represents the composition of the silicate expressed in moles of the oxides and in which, in addition to Sitar one or more oxides of an alkali metal (M) and one or more oxides of a trivalent metal X chosen fran aluminium, iron, gallium, rhodium, cranium and scandium are present, the M2O/X2O3 molar ratio is higher than 0.9 and the SiO2/X203 molar ratio is higher than 10. 2. Catalyst compositions as claimed in claim 1, characterized in that 10-50 %w thereof consists of components I and II and the remainder of a porous matrix. 3. Catalyst compositions as claimed in claim 1 or 2, characterized in that per part by weight of component I they contain at most 25 pow of component II. 4. Catalyst compositions as claimed in claim 3, characterized in that per part by weight of ccoPnent I they contain at most 15 pbw of component II. 5. Catalyst compositions as claimed in any one of claims 1-4, characterized in that as component I they comprise a synthetic zeolite Y. 6. Catalyst compositions as claimed in claim 5, characterized in that as component I they camprise a synthetic zeolite Y in which ions of rare earth metals are present. 7. Catalyst compositions as claimed in any one of claims 1-6, characterized in that as component II they comprise a silicate in which the SiO2/X203 molar ratio is lower than 2000. 8. Catalyst compositions as claimed in claim 7, characterized in that as component II they comprise silicates in which the SiO2/X203 molar ratio lies between 50 and 1500. 9. Catalyst compositions as claimed in any one of claims 1-8, characterized in that as component II they comprise silicates in which aluminium and/or iron are present as metals X. 10. Catalyst compositions as claimed in any one of claims 1-9, characterized in that as component II they comprise a silicate which has been prepared starting ftan an aqueous mixture containing one or more compounds of an alkali metal and which after calcination has been treated ance or several times with a solution of an alkali metal comçound. 11. Catalyst compositions as claimed in any one of claims 1-10, characterized in that as component II they comprise a silicate which is substantially completely in the alkali metal form. 12. Catalyst compositions as claimed in any one of claims 1-11, characterized in that as component II they comprise a silicate in which the alkali metal ions are sodium ions. 13. Catalyst compositions as claimed in claim 1, substantially as described hereinbefore and in particular with reference to the Example. 14. A process for the production of gasoline characterized in that a hydrocaron mixture boiling above the gasoline range is cracked by using a catalyst composition as claimed in any one of claims 1-13, and that a fraction boiling in the gasoline range is separated from the cracked product. 15. A process as claimed in claim 14, characterized in that a gas oil is used as hydrocarbon mixture boiling above the gasoline range. 16. A process as claimed in claim 14 or 15, characterized in that it is carried out at a temperature of 250-650 OC, a pressure of 1-10 bar, a space velocity of 1-250 kg feed per kg catalyst composition per hour and a catalyst composition/feed weight ratio of 1-25. 17. A process as claimed in claim 16, characterized in that it is carried out at a temperature of 450-600 OC, a pressure of 1-7.5 bar, a space velocity of 5-150 kg.kg l.h 1 and a catalyst composition/feed weight ratio of 1.5-20. 18. A process for the production of gasoline as claimed in claim 14, substantially as described hereinbefore and in particular with reference to the Example. 19. Gasoline whenever prepared by a process according to any one of claims 14-18.

Inventors: HEINERMAN, JACOBUS JOHANNES LEONARDUS
Applicants: SHELL INTERNATIONALE RESEARCH MAATSCHAPPIJ B.V.
Application year: 1984
Main classification: B01J29
IPC codes: B01J29, C10G11