PROCESS FOR PREPARING POLYOLEFINS

Abstract: A process for preparing a polyolefin by polymerizing at least one olefin in the presence of a catalyst comprising a solid catalyst component and an organometallic compound, said solid catalyst component being a product obtained by intercontacting the following components (i)-(iv): (i) a silicon oxide and/or an aluminium oxide, (ii) a reaction product obtained by the reaction of a magnesium halide and a compound represented by the general formula Me(OR) n X z-n wherein Me is an element of Groups I-IV in the Periodic Table, z is the valence of the element Me, n is 0 < n ≦ z, X is a halogen atom and R is a hydrocarbon radical having 1 to 20 carbon atoms, (iii) a halogenated silicon compound, and (iv) a titanium compound and/or a vanadium compound.

Description: PROCESS FOR PREPARING POLYOLEFINS BACKGROUND OF THE INVENTION The present invention relates to a new process for preparing polyolefins. More particularly, it is concerned with a process for preparing polyolefins not only capable of remarkably increasing the polymer yield per solid and that per transition metal, thereby dispensing with the step of removing catalyst remaining in the resultant polymer, at the same time enhancing the bulk density of the resultant polymer and diminishing the proportion of fine particles thereof, but also having good particle properties such as, for example, a large average particle diameter. In this technical field, many methods have heretofore been known which employ a catalyst comprising an inorganic magnesium solid as carrier such as magnesium halide, magnesium oxide or magnesium hydroxide and a transition metal compound supported thereon such as a titanium compound or a vanadium compound. In these known methods, however, the resultant polymers generally have a low bulk density, a relatively small average particle diameter and a wide particle size distribution and hence a large proportion of fine particles. Therefore, improvement has strongly been demanded from the standpoint of productivity and polymer handling. Moreover, in molding these polymers there arise problems such as dusting and loweriny of the molding efficiency, and therefore the foregoing increase of bulk density and decrease of the proportion of fine particles have been strongly demanded. Besides, further improvements are considered necessary in order to apply those polymers to processing machines directly in a powdered state without going through a pelletizing step. Demand for such a direct processing method has recently been increasing. The present inventors have previously proposed a novel catalyst component free of the above-mentioned drawbacks in U.S. Patent No.4,396,534. This catalyst can afford a polymer having a high bulk density and a large average particle diameter, but it has been considered necessary to make further improvements in order to apply the resultant powdered polymer to a processing machine directly without going through a pelletizing step. SUMMARY OF THE INVENTION It is the object of the present invention to provide a polymer free of the above-mentioned drawbacks and having a high bulk density, a large average particle diameter, a narrow particle size distribution, an extremely reduced proportion of fine particles and a good fluidity. The present invention resides in a process for homopolymerizing oleo in or copolymerizing olefines in the presence of a catalyst comprising a solid catalyst component and an organometallic compound, said solid catalyst component being a product obtained by intercon- tacting the following components (i) to (iv): : (i) a silicon oxide and/or an aluminum oxide, (ii) a reaction product obtained by the reaction of a magnesium halide and a compound represented by the general formula Me (OR) nX n wherein Me is an element of Groups i-IV in the Periodic Table, z is the valence of the element Me, n is Ocn n X is a halogen atom and each R is a hydrocarbon radical having 1 to 20 carbon atoms, (iii) a halogenated silicon compound, and (iv) a titanium compound and/or a vanadium compound. By using the process of the present invention there can be obtained in high activity a polyolefin having a large average particle diameter, a narrow particle size distribution, a reduced proportion of fine particles and a good fluidity. Besides, the bulk density of the polyolefin is high. This high bulk density, coupled with good fluidity, is very advantageous to the polymerizing operation. Further, tiie polyolefin even in a powdered statc, not to mention pellets, can be subjected to molding, and there are few molding troubles. Thus, it is possible to prepare polyolefins in an extremely advantageous manner. The use of the catalyst of the present invention is further advantageous in that the molecular weight distribution of the resultant polyolefin can be changed in a wide range as desired by changing catalyst preparation conditions. The catalyst of the present invention is preferably used especially for copolymerizing ethylene and one or more other Oc-olefins, thereby a crystalline ethylene copolymer having a very low density (about 0.87 to 0.92 g/cm3) is easily obtainable. DESCRIPTION OF THE PREFERRED EMBODIMENTS The silicon oxide used in the present invention may be silica or a double oxide of silicon and at least one other metal of Groups I-VIII in the Periodic Table. The aluminum oxide used in the present invention may be alumina or a double oxide of aluminum and at least one other metal of Groups I-VIII in the Periodic Table. Typical examples of such double oxides of silicon or aluminum and at least one other metal of Groups I-VIII in the Periodic Table are various natural or synthetic double oxides such as A1203-MgO, Al2O3.CaO, Al2O3.SiO2, Al2O3.MgO.CaO, Al2O3MgO SiO2, Al2O3CuO, Al2O3Fe2O3, A1203-NiO and SiO2MgO. It is to be understood that the above formulae are not molecular formulae, but represent only compositions and that the structure and component ratio of the double oxides used in the present invention are not specially restricted thereby. It goes without saying that the silicon oxide and/or aluminum oxide used in the present invention may contain a small amount of water adsorbed therein and small amounts of impurities. The magnesium halide used in the present invention is a substantially anhydrous one, examples of which are magnesium fluoride, magnesium chloride, magnesium bromide, magnesium iodide, and mixtures thereof, with magnesium chloride being particularly preferred. These magnesium halides may be treated before use with electron donors such as alcohols, esters, ketones, carboxylic acids, ethers, amines and phosphines. As examples of the compound of the general formula Me (OR) nX n used in the present invention wherein Me is an element of Groups I-IV in the Periodic Table, z is the valence of the element Me, 0 < n 5 X is a halogen and Rs, which may be alike or different, are each a hydrocarbon radical such as an alkyl, aryl or aralkyl group having 1 to 20, preferably 1 to 8, carbon atoms, mention may be made of such compounds as NaOR, Mg(OR)2, Mg(OR)X, Ca(OR)2r Zn (OR)2, B (OR) 3, B(OR)2X, Al (OR) 3, Al (OR) 2X, Al(OR)X2, Si (OR) 4, Si(OR)3X, Si(OR)2X2, Si(OR)X3 and Sn (OR) 4 Concrete and preferred examples of these compounds are Mg(OC2H5)2 r Mg(OC2H5)Cl, B(OC2H5) 3' Al(OCH3) 3, Al(OC2H5)3, Al (On-C3H7) 3' Al (Oi-C3H7) 3' awl (On-C4Hg) 3r Al (Osec-C4Hg) 3, Al(Ot-C4H9) 3' Al (OC6ll5)3, Al (OC8H17) 3 Al (OCH3) 2Cl, Al (OC2H5) 2Cl, Al (Oi-C3H7) 2Cl, Al (Oi-C3H7)Cl2, Si (OC2H5)4, Si(OC2H5)3C1, Si(OC2H5)2Cl2 and Si(OC2H5)Cl3. The method of reacting the magnesium halide with the compound of the general formula Me(OR)nXz-n is not specially limited. Both may be mixed and heat-reacted in an organic solvent such as an inert hydrocarbon, alcohol, ether, ketone or ester at a temperature of 20 to 4000C; preferably 500 to 3000C, for 5 minutes to 10 hours. Alternatively, the two may be reacted by a copulverization treatment. Co-pulverization treatment is particularly preferred. The apparatus to be used for the co-pulverization is not specially limited. Usually, ball mill, vibration mill, rod mill or impact mill is used. Conditions such as pulverization temperature and time can be easily determined by those skilled in the art according to the pulverization method used. Generally, the pulverization temperature is in the range of 0 to 2000C, preferably 200 to 1000C, and the pulverization time is in the range of 0.5 to 50 hours, preferably 1 to 30 hours. Of course, the co-pulverizing operation should be done in an inert gas atmosphere, and moisture should be avoided. The reaction ratio of magnesium halide and the compound of the general formula Me(OR)nXz is 1 : 0.01 10, preferably 1 : 0.1 ¯ 5, in terms of Mg : Me (mole ratio). Preferred examples of the halogenated silicon compound used in the present invention are those represented by the general formula Rn Six n wherein R is hydrogen atom or a hydrocarbon radical such as an alkyl, aryl or aralkyl group having 1 to 20, preferably 1 to 8 carbon atoms, X is a halogen atom and 0 < n c 4, such as SiC14, HSiC13, H2SiC12, H3SiCl, CH3SiC13, (CH3)2SiC12, C2H5SiC13, n-C4H9SiC13, C8H17SiCl3, 3 18 37SiC13, C6Ei5SiC13 and (C6H5)2SiCl2, with SiCl4 being particularly preferred. As examples of the titanium compound and/or vanadium compound used in the present invention, mention may be made of halides, alkoxyhalides, alkoxides and halogenated oxides of titanium and/or vanadium. Suitable examples of the titanium compound are tetravalent titanium compounds. As tetravalent titanium compounds, those represented by the general formula Ti(OR)nX4 are preferred wherein R is an alkyl, aryl or aralkyl group having to 20 carbon atoms, X is a halogen atom and 0 c n < 4, such as, for example, titanium tetrachloride, titanium tetrabromide, titanium tetraiodide, monomethoxytrichlorotitanium, dimethoxydichlorotitanium, trimethoxymonochlorotitanium, tetramethoxytitanium, monoethoxytrlchlorotitanium, tetraethoxydichlorotitanium, triethoxymonochlorotitanium, tetraethoxytitanium, monoisopropoxytrichlorotitanium, diisopropoxydichlorotitanium, triisopropoxymonochlorotitanium, tetraisopropoxytitanium, monobutoxytrichlorotitanium, dibutoxydichlorotitanium, monopentoxytrichlorotitanium, monophenoxytrichlorotitanium, diphenoxydichlorotitanium, triphenoxymonochlorotitanium and tetraphenoxytitanium. As trivalent titanium compounds are exemplified titanium trihalides obtained by reducing titanium tetrahalides such as titanium tetrachloride and titanium tetrabromide with hydrogen, aluminum, titanium or an organometallic compound of a metal of Groups I-III in the Periodic Table, as well as trivalent titanium compounds obtained by reducing tetravalent alkoxytitanium halides of the general formula Ti(OR)mX4 with an organometallic compound of a metal m of Groups I-III in the Periodic Table in which formula R is an alkyl, aryl or aralkyl group having 1 to 20 carbon atoms, X is a halogen atom and 0 < m < 4. Examples of the vanadium compound are tetravalent vanadium compounds such as vanadium tetrachloride, vanadium tetrabromide, vanadium tetraiodide and tetraethoxyvanadium, pentavalent vanadium compounds such as vanadium oxytrichloride, ethoxydichlorovanadyl, triethoxyvanadyl and tributoxyvanadyl, and trivalent vanadium compounds such as vanadium trichloride and vanadium triethoxide. The titanium compound and the vanadium compound are often used together to make the present invention more effective. In this case, it is preferable that the V/Ti mole ratio be in the range of 2/1 to 0.01/1. In obtaining the solid catalyst component used in the present invention, the components (i), (ii), (iii) and (iv) may be contacted and reacted in any of the following orders. 0 Components (i) and (ii) are contacted, followed by contact with component (iii) and then with component (iv). Q2 Components (i) and (ii) are contacted, followed by contact with component (iv) and then with component (iii). a Components (i) and (ii) are contacted, followed by contact with components (iii) and (iv) simultaneously 0 Components (i) and (iv) are contacted, followed by contact with component (ii) and then with component (iii). The above reaction orders C and (g are particularly preferred. The solid catalyst component obtained according to any of the above reaction orders may be further contacted several times with component (iii) and/or component (iv). The method of intercontacting the components (i) to (iv) is not specially limited. These components may be mixed and heated in an organic solvent such as an inert hydrocarbon, alcohol, ether, ketone or ester at a temperature of 50a to 200 C for 5 minutes to 24 hours, followed by removal of the solvent, or may be co-pulverized at a temperature of 0 to 2000C for 0.5 to 50 hours, or may be treated by a suitable combination of these methods. The amount of component (ii) used in the present invention is 0.01 to 5 g., preferably 0.1 to 2 g., per gram of component (i), and the amount of component (iii) is 0.01 to 75 g., preferably 0.1 to 50 g., per gram of component (i). As to the amount of component (iv), it is preferable to adjust it so that the titanium and/or vanadium content of the resultant solid component is in the range of 0.5 to 20 wit., with the range of 1 to 10 wt.t being especially desirable for obtaining a well-balanced activity per titanium and/or vanadium and that per solid. If oleo in polymerization is performed using a catalyst comprising the combination of the solid component thus obtained and an organometallic compound, there can be obtained a polyolefin having a large average particle diameter and a good fluidity as compared with the case where a solid component prepared according to another method is used. As examples of the organometallic compound used in the present invention, mention may be made of organometallic compounds of metals of Groups I-IV in the Periodic Table which are known as one component of Ziegler type catalysts. Particularly, organoaluminum compounds and organozinc compounds are preferred. Concrete examples are organoaluminum compounds of the general formulae, R3Al, R2AlX, RIslX2, R2AlOR, Ral(OR)X and R3A12X3, wherein the Rs,which may be the same or different, are each an alkyl or aryl group having 1 to 20 carbon atoms and X is a halogen atom, and organozinc compounds of the general formula R2Zn wherein the Rs, which may be the same or different, are each an alkyl group having 1 to 20 carbon atoms, such as triethylaluminum, triisopropylaluminum, triisobutylaluminum, tri-sec-butylaluminum, tri-tert-butylaluminum, trihexylaluminum, trioctylaluminum, diethylaluminum chloride, diisopropylaluminum chloride, diethylaluminum ethoxide, ethylaluminum sesquichloride, diethylzinc, and mixtures thereof. The amount of the organometallic compound used is not specially limited, but usually it is in the range of 0.1 to l,000 moles per mole of the titanium compound and/or vanadium compound. The organometallic compound component used in the present invention may be in the form of a mixture or addition compound with an organic acid ester. In the case of using a mixture of the organometallic compound with an organic acid ester, the organic acid ester is used in an amount of usually 0.1 to 1 moles, preferably 0.2 to 0.5 moles, per mole fo the organometallic compound. In the case of using an addition compound of the organometallic compound with an organic acid ester, it is preferable that the organometallic compound : organic acid ester mole ratio be in the range of 2 : 1 to 1 : 2. The organic acid ester used is an ester of a saturated or unsaturated mono- or dibasic organic carboxylic acid having 1 to 24 carbon atoms with an alcohol having 1 to 30 carbon atoms. Examples are methyl formate, ethyl acetate, amyl acetate, phenyl acetate, octyl acetate, methyl methacrylate, ethyl stearate, methyl benzoate, ethyl benzoate, n-propyl benzoate, isopropyl benzoate, butyl benzoate, hexyl benzoate, cyclopentyl benzoate, cyclohexyl benzoate, phenyl benzoate, benzoic acid-4-tolyl, methyl salicylate, ethyl salicylate, methyl phydroxybenzoate, ethyl p-hydroxybenzoate, phenyl alicylate, cyclohexyl p-hydroxybenzoate, benzyl salicylate, ethyl a-resorcinate, methyl anisate, ethyl anisate, phenyl anisate, benzyl anisate, methyl p-ethoxybenzoate, methyl p-toluylate, ethyl p-toluylate, phenyl p-toluylate, ethyl o-toluylate, ethyl mtoluylate, methyl p-aminobenzoate, ethyl p-aminobenzoate, vinyl benzoate, allyl benzoate, benzyl benzoate, methyl naphthoate, and ethyl naphthoate. Among the organic acid esters exemplified above, alkyl esters, especially methyl and ethyl esters, of benzoic acid, o- or p-toluic acid or anisic acid are particularly preferred. The oleo in polymerization using the catalyst of the present invention may be conducted as a slurry polymerization, solution polymerization or vapor phase polymerization. The catalyst of the invention is particularly suitable for vapor piiase polymerization. The polymerization reaction is performed in the same way as in the conventional oleo in polymerization reaction using a Ziegler type catalyst. More specifically, the reaction is conducted in a substantially oxygen- and water-free condition in the presence or absence of an inert hydrocarbon. Oleo in polymerizing conditions involve temperatures in the range of 200 to 120 C, preferably 400 to 1000C, and pressures in the range from atmospheric pressure to 70 kg/cm2, preferably 2 to 60 kg/cm2. Adjustment of the molecular weight can be made to some extent by changing polymerization conditions such as the polymerization temperature and the catalyst mole ratio, but the addition of hydrogen into the polymerization system is more effective for this purpose. Of course, using the catalyst of the present invention, two or more multi-stage polymerization reactions involving different hydrogen concentrations and different polymerization temperatures can be performed without any trouble. The process of the present invention is applicable to the polymerization of all olefins that are polymerizable with a Ziegler type catalyst, with t- olefines having 2 to 12 carbon atoms being particularly preferred. For example, it is suitable for the homopolymerization of a-olefins such as ethylene, propylene, butene-1, hexene-1 and 4-methylpentene-1, as well as copolymerization of ethylene and propylene, ethylene and butene-1, ethylene and hexene-1, and propylene and butene-1. Copolymerization with dienes for the modification of polyolefins is also preferred. Examples of diene compounds which may be used in such copolymerization are butadiene, 1,4-hexadiene, ethylidene norbornene and dicyclopentadiene. The following examples are given to further illustrate the present invention, but it is to be understood that the invention is not limited thereto. Example 1 (a) Preparation of Solid Catalyst Component 10 g. of a commercially available anhydrous magnesium chloride and 4.2 g. of aluminum triethoxide were placed in a stainless steel pot having an internal volume of 4q0,ml. and containing 25 stainless steel balls each about 12.7mm (1/2 inch) in diameter, and ball-milled at room temperature for 16 hours in a nitrogen atmosphere to obtain a reaction product. A three-necked flask equipped with a stirrer and a reflux condenser was purged with nitrogen, into which were charged 5 g. of the above reaction product and 5 g. of SiO2 (#952, a product of Fuji-Davison) which had been calcined at 600 C. Then, 100 ml. of tetrahydrofuran was added and reaction was allowed to take place at 600C for 2 hours, followed by drying at 1200C under reduced pressure to remove tetrahydrofuran. Then, 3 ml. of silicon tetrachloride was added and reaction was allowed to take place at600C for 2 hours. Thereafter, 1.6 ml. of titanium tetrachloride was added and reaction was allowed to proceed at 1300C for 2 hours to obtain a solid catalyst component containing 40 mg of titanium per gram thereof. (b) Vapor Phase Polymerization A stainless steel autoclave was used as a vapor phase polymerization apparatus, and a loop was formed using a blower, a flow controller and a dry cyclone. The temperature of the autoclave was adjusted by passing warm water through the jacket around the autoclave. Into the autoclave adjusted to 600C were fed the above solid catalyst component and triethylaluminum at rates of 250 mg/hr and 50 mmol/hr, respectively. Also, propylene, ethylene and hydrogen,gases were fed while adjusting the propylene/ethylene ratio (mole ratio) in the vapor phase in the autoclave to 0.65 and the hydrogen pressure to 5% of the total pressure, and polymerization was performed while circulating the intra-system gases by the blower to afford a powdered ethylene copolymer having a bulk density of 0.47, a melt index (MI) of 1.2, a density of 0.8900, an average particle diameter of 990pom, free of particles not larger than 177pm, and having a good fluidity. Catalytic activity was 150,000g.copolymer/g.Ti and thus very high. After a continuous run for 100 hours, the autoclave was opened and its interior was inspected. As a result, the interior was found to be clean with no polymer adhesion to the inner walls and stirrer, and there was no agglomeration of polymer. Comparative Example 1 A solid catalyst component was prepared in the same way as in Example 1-(a) except that the silicon tetrachloride was not used. Using the solid catalyst component just prepared above, copolymerization of ethylene and propylene was performed in the same manner as in Example 1-(b) to afford a powdered ethylene copolymer having a bulk density of 0.40, an MI of 1.0, a density of 0.9003, an average particle diameter of 700pm, containing 1.5 wt.% of particles not larger than 177pm, and having a slight stickiness. Catalytic activity was 110,000g.copolylller/g.'l'i. After a continuous run for 100 hours, the autoclave was opened and its interior was inspected. As a result, there was a slight polymer adhesion to the stirrer, and three partially molten polymer agglomerates each about 7 cm in diameter were found in the autoclave. Example 2 (a) Preparation of Solid Catalyst Component 10 g. of a commercially available anhydrous magnesium chloride and 4.2 g. of aluminum triethoxide were placed in a stainless steel pot having an internal volume of ,400, ml and containing 25 stainless steelballs each about 12.7mm (1/2 inch) in diameter, and ball-milled at room temperature for 16 hours in a nitrogen atmosphere to obtain a reaction product. A three-necked flask equipped with a stirrer and a reflux condenser was purged with nitrogen, into which were charged 5 g. of the above reaction product and 5 g. of SiO2 (&num;952, a product of Fuji-Davison) which had been calcined at 600 C. Then, 100 ml. of tetrahydro- furan was added and reaction was allowed to take place at 600C for 2 hours, followed by drying at 1200C under reduced pressure to removed tetrahydrofuran. Then, 30 ml. of silicon tetrachloride was added and reaction was allowed to take place fpr 2 hours under reflux C)f silicon tetrachloride, followed by drying at room temperature under reduced pressure to remove silicon tetrachloride. Thereafter, 1.6 ml. of titanium tetrachloride was added and reaction was allowed to proceed at 1300C for 2 hours to give a solid catalyst component containing 40 mg. of titanium per gram thereof. (b) Vapor Phase Polymerization A stainless steel autoclave was used as a vapor phase polymerization apparatus, and a loop was formed using a blower, a flow controller and a dry cyclone. The temperature of the autoclave was adjusted by passing warm water through the jacket around the autoclave. Into the autoclave adjusted to 600C were fed the solid catalyst component just prepared above and triethylaluminum at rates of 250 mg/hr and 50 mmol/hr, respectively. Also, propylene, ethylene and hydrogen gases were fed while adjusting the propylene/ethylene ratio (mole ratio) in the vapor phase in the autoclave to 0.60 and the hydrogen pressure to 7% of the total pressure, and polymerization was performed while circulating the intra-system gases by the blower, to afford a powdered ethylene copolymer having a bulk density of 0.47, an MI of 1.4, a density of 0.8950, an average particle diameter of 950um, free of particles not larger than 177pom, and having a good fluidity. Catalytic activity was 140,000g.copolymer/g.Ti and thus very high. After a ccontinuous run for 100 hours, the autoclave was opened and its interior was inspected. As a result, the interior was found to be clean with no polymer adhesion to the inner wall and stirrer. Example 3 (a) Preparation of Solid Catalyst Component 10 g. of a commercially available anhydrous magnesium chloride and 4.2 . of aluminum triethoxide were placed in a stainless steel pot having an internal volume of 400 ml. and containing 25 stainless steel balls each about 12.7mm (1/2 inch) in diameter, and ball-milled at room temperature for 16 hours in a nitrogen atmosphere to obtain a reaction product. A three-necked flask equipped with a stirrer and a reflux condenser was purged with nitrogen and then charged with 5 g. of the above reaction product and 5 g. of SiO2 (&num;952, a product of Fuji-Davison) which had been calcined at 6000C. Then, 100 ml. of tetrahydrofuran was added and reaction was allowed to take place at 600C for 2 hours, followed by drying at 1200C under reduced pressure to remove tetrahydrofuran. Then, 0.5 ml. of titanium tetrachloride was added and reaction was allowed to take place at llO"C for 2 hours to give a solid catalyst component containing 40 mg. of titanium per gram thereof. (b) Vapor Phase Polymerization A stainless steel autoclave was used as a vapor phase polymerization apparatus, and a loop was formed using a blower, a flow controller and a dry cyclone. The temperature of the autoclave was adjusted by passing warm water through the jacket around the autoclave. Into the autoclave adjusted to 600C were fed the above solid catalyst component and triethylaluminum at rates of 250 mg/hr and 50 mmol/hr, respectively. Also, propylene, ethylene and hydrogen gases were fed while adjusting the propylene/ethylene ratio (mole ratio) in the vapor phase in the autoclave to 0.50 and the hydrogen pressure to 10% of the total pressure, and polymerization was performed while circulating the intra-system gases by the blower, to afford a powdered ethylene copolymer having a bulk density of 0.49, an MI of 2.0, a density of 0.9100, an average particle diameter of 920pom, free of particles not larger than 177um, and having a good fluidity. Catalytic activity was 120,000g.copolymer/g.Ti and thus very high. After a continuous run for 100 hours, the autoclave was opened and its interior was inspected. As a result, the interior was found to be clean with no polymer adhesion to the inner wall and stirrer. Example 4 A vapor phase polymerization was carried out using the solid catalyst component prepared in Example 3. As the vapor phase polymerization apparatus there was used a stainless steel autoclave, and a loop was formed using a blower, a flow controller and a dry cyclone. The temperature of the autoclave was adjusted by passing warm water through the jacket around the autoclave. Into the autoclave adjusted to 600C were fed the solid catalyst component prepared in Example 3 and triethylaluminum at rates of 250 mg/hr and 50 mmol/hr, respectively. Further, butene-1, ethylene and hydrogen gases were fed while adjusting the butene-1/ethylene ratio (mole ratio) in the vapor phase in the autoclave to 0.55 and the hydrogen pressure to 10% of the total pressure, and polymerization was conducted while circulating the intra-system gases by the blower to afford a powdered ethylene copolymer having a bulk density of 0.48, an MI of 1.4, a density of 0.9000, an average particle diameter of 910pm, free of particles not larger than 177pom, and having a good fluidity. Catalytic activity was 112,000g.copolymer/g.Ti and thus very high. After a continuous run for 100 hours, the autoclave was opened and its interior was inspected. As a result, the interior was found to be clean with no polymer adhesion to the inner wall and stirrer. Example 5 (a) Preparation of Solid Catalyst Component 10 g. of a commercially available anhydrous magnesium chloride and 4.2 g. of aluminum triethoxide were placed in a stainless steel pot having an internal volume qf t00 ml. and containing 25 stainless steel balls each about 12.7mm (1/2 inch) in diameter, and ball-milled at room temperature for 16 hours in a nitrogen atmosphere to obtain a reaction product. A three-necked flask equipped with a stirrer and a reflux condenser was purged with nitrogen and then charged with 2.5 g. of the above reaction product and 7.5 g. of SiO2 (&num;952, a product of Fuji-Davison) which had been calcined at 6000C. Then, 100 ml. of tetrahydrofuran was added and reaction was allowed to take place at 600C for 2 hours, followed by drying at 1200C under reduced pressure to remove tetrahydrofuran. Then, 3 ml. of silicon tetrachloride was added and reaction was allowed to take place at 600C for 2 hours, thereafter 1.6 ml. of titanium tetrachloride was added and reaction was allowed to proceed at 1400C for 2 hours to give a solid catalyst component containing 40 mg. of titanium per gram thereof. (b) Vapor Phase Polymerization A stainless steel autoclave was used as a vapor phase polymerization apparatus, and a loop was formed using a blower, a flow controller and a dry cyclone. The temperature of the autoclave was adjusted by passing warm water through the jacket around the autoclave. Into the autoclave adjusted to 600C were fed the above solid catalyst component and triethylaluminum at rates of 250 mgZhr and 50 mmol/hr, respectively. Further, butene-1, ethylene and hydrogen gases were fed while adjusting the butene-1/ethylene ratio (mole ratio) in the vapor phase in the autoclave to 0.48 and the hydrogen pressure to 15% of the total pressure, and polymerization was performed while circulating the intra-system gases by the blower, to afford a powdered ethylene copolymer having a bulk density of 0.48, an MI of 1.0, a density of 0.9100, an average particle diameter of 900Fun, free of particles not larger than 177ym, and having a good fluidity. Catalytic activity was 120,000g.copolymer/g.Ti and thus very high. After a continuous run for 100 hours, the autoclave was opened and its interior was inspected. As a result, the interior was found to be clean with no polymer adhesion to the inner wall and stirrer. Example 6 (a) Preparation of Solid Catalyst Component 10 g. of a commercially available anhydrous magnesium chloride and 3.3 g. silicon tetraethoxide were placed in a stainless steel pot having an internal volume o; 400 ml. and containing 25 stainless steel balls each about 12.7mm (1/2 inch) in diameter, and balled-milled at room temperature for 16 hours in a nitrogen atmosphere to obtain a reaction product. A three-necked flask equipped with a stirrer and a reflux condenser was purged with nitrogen and then charged with 5 g. pf the above reaction product and 5 g. of SiO2 (#95,28 a product of Fuji-Davison) which had been calcined at 6000C. Then, 100 ml. of tetrahydrofuran was added and reaction was allowed to take place at 600C for 2 hours, followed by drying at 1200C under reduced pressure to remove tetrahydrofuran. Then, 2.0 ml. of titanium tetrachloride was added and reaction was allowed to take place at 1300C for 2 hours, thereafter 4 ml. of silicon tetrachloride was added and reaction was allowed to proceed at 600C for 2 hours to give a solid catalyst component contain- ing 45 mg. of titanium per gram thereof. (b) Vapor Phase Polymerization A stainless steel autoclave was used as a vapor phase polymerization apparatus, and a loop was formed using a blower, a flow controller and a dry cyclone. The temperature of the autoclave was adjusted by passing warm water through the jacket around the autoclave. Into the autoclave adjusted to 600C were fed the above solid catalyst component and triethylaluminum at rates of 250 mg/hr and 50 mmol/hr, respectively. Further, butene-l, ethylene and hydrogen gases were fed while adjusting the butene-1/ethylene ratio (mole ratio) in the vapor phase in the autoclave to 0.50 and the hydrogen pressure to 10 of the total pressure, and polymerization was conducted while circulating the intra-system gases by the blower to afford a powdered ethylene copolymer having a bulk density of 0.48, an MI of 1.1, a density of 0.9005, an average particle diameter of 940Fun, free of particles not larger than 177mum, and having a good fluidity. Catalytic activity was 132,000g.copolymer/g.Ti and thus very high. After a continuous run for 100 hours, the autoclave was opened and its interior was inspected. As a result, the interior was found to be clean with no polymer adhesion to the inner wall and stirrer, and there was no polymer agglomeration. Example 7 (a) Preparation of Solid Catalyst Component 10 g. of a commercially available anhydrous magnesium chloride and 2.4 g. of magnesium diethoxide were placed in a stainless steel pot having an internal volume of 4,00 ml. and containing 25 stainless steel balls each about 12.7mm (1/2 inch) in diameter, and ball-milled at room temperature for 16 hours in a nitrogen atmosphere to obtain a reaction product. A three-necked flask equipped with a stirrer and a reflux condenser was purged with nitrogen and then charged with 5 g. of the above reaction product and 5 g. of SiO2 (&num;952, a product of Fuji-Davison) which had been calcined at 6000C. Then, 100 ml. of tetrahydrofuran was added and reaction was allowed to take place at 600C for 2 hours, followed by drying at 1200C under reduced pressure to remove tetrahydrofuran. Then, 0.5 ml. of titanium tetrachloride was added and reaction was allowed to take place at 1100C for 2 hours, thereafter 3 ml. of silicon tetrachloride was added and reaction was allowed to proceed at 600C for 2 hours, followed by further addition of 1.1 ml. of titanium tetrachloride and reaction at 1400C for 2 hours to afford a solid catalyst component containing 40 mg. of titanium per gram thereof. (b) Vapor Phase Polymerization A stainless steel autoclave was used as a vapor phase polymerization apparatus, and a loop was formed using a blower, a flow controller and a dry cyclone. The temperature of the autoclave was adjusted by passing warm water through the jacket around the autoclave. Into the autoclave adjusted to 600C were fed the above solid catalyst component and triethylaluminum at rates of 250 mg/hr and 50 mmol/hr, respectively. Further, propylene, ethylene and hydrogen were fed while adjusting the propylene/ethylene ratio (mole ratio) in the vapor phase in the autoclave to 0.50 and the hydrogen pressure to 10% of the total pressure, and polymerization was conducted while circulating the intra-system gases by the blower to afford a powdered ethylene copolymer having a bulk density of 0.47, an MI of 1.8, a density of 0.9091, an average particle diameter of 900pm, free of particles not larger than 177cm, and having a good fluidity. Catalytic activity was 120,000g.copolymer/g.Ti and thus very high. After a continuous run for 100 hours, the autoclave was opened and its interior was inspected. As a result, the interior was found to be clean with no polymer adhesion to the inner wall and stirrer.

Claims: CLAIMS: 1. A process for preparing a polyolefin by polymerizing at least one oleo in in the presence of a catalyst comprising a solid catalyst component and an organometallic compound, said solid catalyst component being a product obtained by intercontacting the following components (i)-(iv): (i) a silicon oxide and/or an aluminum oxide, (ii) a reaction product obtained by the reaction of a magnesium halide and a compound represented by the general formula Me (OR) nX n wherein Me is an element of Groups I-IV in the Periodic Table, z is the valence of the element Me, 0 < n c z, X is a halogen atom and each R is a hydrocarbon radical having 1 to 20 carbon atoms, (iii) a halogenated silicon compound, and (iv) a titanium compound and/or a vanadium compound. 2. The process of claim 1, wherein the silicon oxide is silica. 3. The process of claim 1 or claim 2 wherein the aluminum oxide is alumina. 4. The process of claim 1, claim 2 or claim 3 wherein the magnesium halide is an anhydrous magnesium chloride. 5. The process of any one of claims 1 to 4 wherein Me is Na, Mg, Ca, Zn, Cd, B, Al, Si, or Sn. 6. The process of any one of claims 1 to 5, wherein each R is an alkyl, aryl or aralkyl group having not more than 8 carbon atoms. 7. The process of any one of claims 1 to 6, wherein the halogenated silicon compound is a compound represented by the general formula RnSiX4-n R SiX wherein R is hydrogen atom or a n 4-n hydrocarbon radical having l to 20 carbon atoms, X is a halogen atom and 0#n < 4. 8. The process of any one of claims 1 to 7, wherein the titanium and/or vanadium compound is or are selected from halides, alkoxyhalides, alkoxides and halogenated oxides of titanium and vanadium. 9. The process of any one of claims 1 to 8, wherein the amount of component (ii) is in the range of 0.01 to 5 g. per gram of component (i), and/or the amount of component (iii) is in the range of 0.01 to 75 g. per gram of component (i), and/or the amount of component (iv) is in the range of 0.5 to 20 weight percent as the titanium and/or vanadium content of the solid catalyst component. 10. The process of any one of claims 1 to 9, wherein the reaction ratio of the magnesium halide to the compound of the general formula Me(OR) X in component (ii) is 1 : 0.012-10 n z-n in terms of Mg : Me mole ratio. 11. The process of any one of claims 1 to 10, wherein the organometallic compound is an organoaluminum compound or an organozinc compound. 12. The process of any one of claims 1 to 11, wherein the olefin is anCsolefin having 2 to 12 carbon atoms. 13. The process of any one of claims 1 to 12, wherein the polymerisation reaction is carried out at a temperature in the range of 200 to 1200C and at a pressure in the range of atmospheric pressure to 70 kg/cm2.

Inventors: KAMIISHI, HIROFUMI, KURODA, NOBUYUKI, MATSUURA, KAZUO, MIYOSHI, MITUJI, OKAMOTO, MITSUO, SHIRAISHI, TAKEICHI
Applicants: NIPPON OIL CO. LTD.
Application year: 1984
Main classification: C08F10
IPC codes: C08F4, C08F10