COMPATIBLE POLYOL BLENDS

Abstract: This invention pertains to compositions containing a relatively high molecular weight polyol having primary hydroxyl groups and a relatively low molecular weight polyol, which are usually incompatible in that they separate into two distinct phases upon storage. These compositions are compatibilized by the admixture therewith of urea or a substituted urea.

Description: The present invention pertains to compatible blends containing a relatively high molecular weight polyol having primary hydroxyl groups and a relatively low molecular weight polyol. Polyurethane articles, commonly formed by the RIM (Reaction Injection Molding) process, are polymer products resulting from the reaction of liquid polyol mixtures and liquid polyisocyanates. These rapid polymerization processes commonly employ a blend of low equivalent weight glycols such as ethylene glycol or 1,4 butanediol and primary hydroxyl terminated high molecular weight polyether polyols. Such blends of ethylene glycol and a 5000 mol. wt. primary capped polyether polyol are incompatible fluids that tend to separate into layers on standing. Recognition of this effect dictates that these blends should be constantly agitated to avoid a misformulation by the separation of components or in some cases, additively, a tendency for catalyst migration occurs in these blends that also contain a heavy metal catalyst such as organotin compound. Further, in certain instances, agitation of these fluid blends during storage or shipment or transfer is not practical or may be difficult. US-A 3 929 730 teaches the use of 1,4 butanediol as a "chain extender" that is blended with high molecular weight polyols (about 2000 m.w. or greater) to prepare polyurethane compositions. However, 1,4 butane diol is insoluble in polyol at the concentration usually employed (see lines 60-70, col. 1 and part C of Claim 1). A sufficient amount of phenylenediethanolamine is used to render the mixture soluble in the polyol. US-A 3 993 576 teaches a composition resistant to phase separations (in the mixture of high mol. wt. polyols and low mol. wt. polyols) by the addition of a "solubilizer", a derivative of butylene glycol or propylene glycol. US-A 4 008185 teaches the use of urea as a catalytic modifier for preparing rapid-setting polyurethanes by reacting a polyol free from nitrogen groups or a mixture of such polyols having from 2 to about 8 hydroxyl groups per molecule and an OH equivalent weight from about 30 to about 500 and an aromatic polyisocyanate. However, urea failed to catalyze the reaction of polyols having an equivalent weight of 500 or higher with aromatic isocyanates. The solubilizing agent in US-A 3 929 730 is a substituted ethanolamine and the solubilizing agent in US-A 3 993 576 is a polyol derivative of butylene or propylene glycol. We disclose solubilizing agents within the group of urea and/or substituted ureas that contain no hydroxyl groups or other active hydrogen groups capable of reacting with isocyanates under conventional RIM reaction conditions. Such compounds as diethanol urea dissolved in ethylene glycol failed to compatibilize blends of ethylene glycol and high molecular weight primary hydroxyl terminated polyols compared to the use of urea. We find that the hydrogen atoms bonded to the nitrogen atoms in urea or substituted ureas exhibit no significant reactivity with isocyanates under RIM reaction conditions. The substituted ureas, further, must also be free of reactive groups capable of reacting with hydroxyls or amines. We have discovered that the addition of a minor amount of urea and/or substituted urea's to the incompatible polyol blends renders these mixtures into a compatible or single phase liquid. These blends of low equivalent weight glycol and high equivalent weight primary capped polyol that have been compatibilized by the addition of minor amounts of urea and/or substituted ureas and may also contain an organotin compound as a catalyst show no significant loss in reactivity after standing. We have further discovered that such urea and/or substituted urea compatibilized blends of low equivalent weight polyols such as ethylene glycol and/or 1,4 butane diol and high molecular weight primary capped polyols (equivalent weight of 1000 or greater) where the high mol. wt. polyol is the major constituent of the hydroxyl components is RIM reactive in the absence of any organo metal (for example, Sn carboxylate) or amine catalyst. In other words, the compatibilized polyol blends mentioned above are catalyzed to react with polyisocyanates by the presence of urea and selected substituted ureas as the sole catalyst. The present invention pertains to a compatible single phase fluid comprising (1) at least one polyetherpolyol having an average hydroxyl functionality of from 2 to 4, preferably from 2 to 3, and an average molecular weight of at least 1000, preferably from 2000 to 8000, and with at least 30 percent, preferably from 50 to 100 percent of the hydroxyl groups being primary hydroxyl groups; and (2) at least one polyol having an average hydroxyl functionality of from 2 to 6, preferably from 2 to 4 and a molecular weight of less than 1000, preferably from 60 to 600, in an amount that the mixture in the absence of the compatibility enhancer (3) is incompatible; (3) and as compatibility enhancer at least one material which is either a liquid or a solid forming a crystal clear liquid blend with (1) and (2) and having a melting point not greater than 200°C which material is represented by the formula wherein each R is independently hydrogen or a hydrocarbyl group having a sufficient number of carbon atoms such that the molecular weight of such group is not greater than 400, preferably less than 200; said material being in an amount sufficient to maintain the composition in a single liquid phase for at least 5 days at 25°C but not causing gellation. The term incompatible as employed herein means that the composition upon storage at a temperature of 25°C for 5 days forms at least two distinct layers. The term compatible means that the mixture remains a single phase at a temperature of 25°C for greater than 5 days. A preferred component (1) has an average hydroxyl functionality of 3 and contains at least 10 weight percent terminal oxyethylene groups. In particular component (1) is a glycerine initiated polyoxypropylene triol containing at least 14 weight percent terminal oxyethylene groups, preferably with ethylene glycol as Component (2); a compatible mixture of these components (1) and (2) can also contain up to 6,25 weight percent of a primary amine-containing material. Suitable materials (1) which can be employed herein include those materials which are prepared by reacting a vicinal epoxy-containing compound with an initiator material having from 2 to 8, preferably from 2 to 4, hydroxyl groups per molecule, which reaction product has been subsequently modified so as to contain at least 30 percent, preferably from 50 to 100 percent primary hydroxyl groups. Particularly suitable initiator materials include, for example, water, ethylene glycol, propylene glycol, glycerine, trimethylolpropane, pentaerythritol, sorbitol, sucrose, or mixtures thereof. Suitable components (1) particularly include the reaction product of a vicinal epoxy-containing compound with the aforementioned initiator materials which reaction product has been subsequently modified so as to contain at least 30 percent primary hydroxyl groups, such as by reacting the resultant reaction product with ethylene oxide to the extent that the product contains at least 10, preferably at least 14 weight percent oxyethylene groups. Suitable such vicinal epoxy-containing compounds include, for example, propylene oxide, 1,2-butylene oxide, 2,3-butylene oxide, styrene oxide, epichlorohydrin, epibromohydrin, epiiodohydrin, methylepichlorohydrin, or mixtures thereof. Suitable materials which can be employed herein as relatively low molecular weight polyols include, for example, ethylene glycol, diethylene glycol, propylene glycol, 1,4-butanediol, 1,5-pentanediol, or 1,6-hexanediol. Suitable compatibility enhancers (compatibilizing agents) which can be employed herein include, for example, urea, dimethyl urea, phenyl urea, diallyl urea, tetramethyl urea, or mixtures thereof. The following examples are illustrative of the present invention but are not to be construed as to limiting the invention in any manner. The following components were employed in the examples. RHMW Polyol A was a polyol prepared by reacting glycerine with propylene oxide and subsequently end-capping with 18 weight percent ethylene oxide and having 77 percent primary hydroxyl groups and an average hydroxyl equivalent weight of 1650. RHMW Polyol B was a mixture of 93 weight percent RHMW Polyol A and 7 weight percent of an aminated polyoxypropylene glycol having an average molecular weight of 400. The aminated polyol is commercially available from Texaco Chemical as Jeffamine® D-400. RHMW Polyol C was a polyol prepared by reacting glycerine with propylene oxide and subsequently end-capping with 14 weight percent ethylene oxide and having 70 percent primary hydroxyl groups and an average hydroxyl equivalent weight of 1640. RLMW Polyol A was ethylene glycol. RHMW Polyol D was a blend of 60 weight percent of a capped polyether diol based on poly(propylene oxide) diol of 4000 molecular weight and capped with 18 wt. percent ethylene oxide and 40 wt. percent of a polyether triol of approximately 5000 molecular weight (based on propylene oxide) with 18 wt. percent ethylene oxide capping. Example 1 A series of formulations were prepared by blending various quantities of urea into ethylene glycol and then adding various quantities of these bends into a relatively high molecular weight polyol. The ethylene glycol urea compositions containing less than 35 weight percent urea were blended at room temperature. Those containing greater than 35 weight percent urea required elevated temperatures to effect total dissolution of the urea into the ethylene glycol. The mixtures of ethylene glycol/urea solutions and relatively high molecular weight polyol were then blended at room temperature to evaluate whether a given ratio (parts by weight) of these components would yield an incompatible blend, or a compatible liquid blend, or a gelled mixture. Generally, the result was evident within a few minutes of mixing at room temperature. However some ratios of these components appeared to yield a border line result and storage of these sample at room temperature for 5 days showed a separation of liquid layers for the incompatible compositions or finally showed a gelled product for those compositions that were slow to gel. For any given ratio of ethylene glycol to the relatively high molecular weight polyol, the incompatible fluid blend indicates that an insufficient amount of urea was employed whereas the gelled product indicates that an excess of urea was employed at that particular ethylene glycol to relatively high molecular weight polyol ratio. Further, the gelled compositions of ethylene glycol and relatively high molecular weight polyols were only observed when urea was employed as the compatibilizing agent; substituted ureas as compatibilizing agents were not found to yield gelled products at any concentration employed. Example 2 To a stirred polyol holding tank was added 100 lb(45.36 kg) of Polyol B.Next, a pre-dissolved blend of 3 lb (1.36 kg) urea in 18 lb (8.16 kg) ethylene glycol was added to the same tank and stirred in. This concentration of urea was the minimum required for compatibilizing this polyol blend. Finally, 0.2 wt. percent organotin catalyst (Fomrez® UL-28, commercially available from Witco Chemical Co.) and 0.1 wt. percent Dabco® 33 LV (triethylene diamine, 33 percent in dipropylene glycol, commercially available from Air Products and Chemicals, Inc.) were blended into the same tank. The above mentioned polyol holding tank was an integral part of an Admiral 400-2HP (impingement mixing) RIM processing machine feeding a sheet forming mold clamped in a press. The isocyanate holding tank of this RIM processing machine contained a liquid MDI prepolymer isocyanate (Upjohn Code 114) having an isocyanate equivalent weight of 160. The feed pumps on this RIM processing machine were set to deliver a mass ratio of 1.04 lb polyol per lb of isocyanate (note: the dissolved urea was calculated to exhibit no active hydrogens). The sheet forming mold, designed to form polymer sheets having the dimensions of 12.25 inches (311.15 mm) by 14.75 inches (374.65mm) by 0.125 inches (3.175) thick was preheated to 170°F (76.7°C). This sheet mold fed by the impingement mixed polyol and polyisocyanate streams of the RIM processing machine for a reactive fluid blend flow time of 1.5 seconds was opened in about 60 seconds after liquid reactant injection to yeild a urethane polymer sheet having essentially the dimensions of the mold cavity. Demolded sheets from this RIM processing machine were then subjected toa post-cure by exposure to a 265°F(129.4°C) oven for a total residence time of 30 minutes to complete the cure of these polymer sheets. The properties determined on these sheets are reported in Table II. Example 3 To test the storage stability of the following polyol blend, 12 lb (5.4 kg) of urea was pre-dissolved in 54 lb (24.5 kg) of ethylene glycol and this mixture was then blended with 300 lb (136 kg) of RHMW Polyol B in a 55 gallon (2081) drum. This drum was left standing for 3 weeks at room temperature (27°C). At the end of this period, the drum contents were examined for component separation or signs of incompatibility. The polyol blend was found to be a clear single phase fluid with no sign of incompatibility. The polyol holding tank of the Admiral 400-2HP processing machine was filled with 122 lb (55.3 kg) of polyol blend from the stored 55 gallon (0.208 m³) drum. Next, 0.1 wt. percent UL-28 and 0.1 wt. percent DABCO® 33LV (based on polyol tank contents) were charged and blended in the polyol holding tank. The isocyanate holding tank on this machine was charged with a liquid MDI isocyanate (Upjohn Isonate® 143L) and the feed pumps of this machine were set to deliver a mass ratio of 1.23 pbw (parts by weight) polyol blend per pbw of liquid isocyanate. Using the same sheet forming mold described in the previous example and having the mold temperature set at 170°F (76.7°C), the impingement mixed blend of polyols and polyisocyanates was flowed into the mold for a "shot time" of 1.6 seconds. Solid urethane polymer sheets were removed from the mold in 60 seconds after injection of the reactive fluid mix. The demolded polymer sheets from this run were subjected to a post-cure treatment identical to that described in the previous example. The physical properties determined on these post-cured polymer sheets are shown in Table III. Example 4 Urea was pre-dissolved in ethylene glycol in the ratio of 4 pbw urea per 18 pbw ethylene glycol then 22 pbw of this mixture was blended with 100 pbw of RHMW Polyol B in the RIM processing machine polyol tank. No tin or amine catalyst was added to the polyol blend. The isocyanate holding tank on this RIM machine was charged with Isonate® 143L. Next, the feed pumps on the RIM machine were set to feed a mass ratio of 1.17 pbw of polyol per pbw of isocyanate (equivalent to approximately 1.03 NCO equivalents/OH equivalents). When the sheet forming mold reached a temperature of 173°F (78.3°C), the impingement mixed reactive fluid blend was injected into the mold and 60 seconds later, a solid urethane polymer sheet was removed from the mold. During the demolding of this polyurethane product, the sheet stiffness seemed to be only slightly less than the tin and amine catalyzed product of the previous run. The apparent slight reduction in demold stiffness of the urea catalyzed product exhibited no detrimental property loss as shown in Table IV (after post curing the sheets in the manner identical with the previous examples). Further, comparative properties of the polymer sheets not subjected to the post cure process are also shown in Table IV. At the end of the run, a polyol blend retain sample was removed from the polyol holding tank. This sample was a crystal clear liquid blend that showed no evidence of separation of components over the next month of observations. Example 5 Using the same ratio of urea dissolved in the ethylene glycol preblend (4 pbw urea in 18 pbw ethylene glycol) as in Example 4, 29.34 lb (13.31 kg) of this blend was added to and blended with 100 lb (45.36 kg) of RHMW Polyol C. The resultant compatible mixture (without urea an incompatible mixture is obtained) was charged to the polyol holding tank of the RIM processing machine. Again, as in the previous run, no tin or amine or other catalyst was added to either reactive stream of this run. The isocyanate holding tank of the RIM machine was charged with a liquid MDI (Isonate® 143L) having an isocyanate equivalent weight of 144. Next the feed pumps on the machine were set to deliver a mass ratio 0.963 pbw of polyol blend per pbw of isocyanate (equivalent to an NCO equivalent/OH equivalent of 1.03). With the sheet forming mold set at a temperature of 170°F (76.7°C), a 1.75 second shot time of impingement mixed reactive blend of polyol and polyisocyanate was required to fill the mold. Then 60 seconds later the mold was opened to yield a RIM formed polyurethane polymer sheet exhibiting a noticeable increase in sheet stiffness at demold. The properties of the post cured polymer sheets formed in this run are shown in Table V. Example 6 The following components were blended in a vessel at 60°C Next, 25 pbw of this ethylene glycol, amine, urea blend was added to 100 pbw of RHMW Polyol D to form a non-separating compatible polyol blend (without urea an incompatible mixture is obtained) which in turn was added to the RIM machine polyol holding tank. The isocyanate holding tank contained a liquid MDI isocyanate having an isocyanate equivalent weight of 144. No other catalytic agent was added to either reactive component. Then the feed pumps on the machine were adjusted to deliver a mass ratio of 1.50 pbw of polyol blend per pbw of isocyanate. When the sheet foaming mold reached about 170°F (76.7°C), the impingement mixed reactants were fed to the mold at a shot time of 1.95 seconds to fill the mold. These sheets that were removed from the mold in 60 seconds after mold filling exhibited hair cracks on a folded over corner immediately after removing the sheet from the mold. Those polymer sheets that were removed from the mold in 120 seconds after mold filling showed a virtual elimination of the hair cracks on a folded over corner of the demolded sheet. Polymer sheets that were demolded in 120 seconds were further post cured in a 265°F 1129°C) oven for 30 minutes and then subjected to the property determinations indicated in Table VI. Example 7 In a vessel containing 20 pounds (9.07 kg) of 1,4 butanediol was added 5 pounds (2.27 kg) of dimethyl urea crystals and dissolved. Then this blend was added to 100 pounds (45.36 kg) of RHMW Polyol A contained within the stirred polyol holding tank of the RIM machine to form a compatible single phase fluid (without urea an incompatible mixture is obtained). The isocyanate holding tank of this RIM processing machine contained a liquid modified 4,4′-diphenylmethane diisocyanate having an isocyanate equivalent weight of 144. Then the feed pumps on this machine were set to deliver a mass ratio of 1.67 pbw of polyol blend per pbw of liquid isocyanate. In this case the dimethyl urea was calculated to exhibit no active hydrogens. The sheet forming mold was preheated to 180°F (82.2°C) and the shot time for the impingement mixed streams of polyol blend and isocyanate was set at 2.15 seconds duration for filling the sheet mold. Urethane polymer sheets were removed from the mold after a 60 second residence time after the liquid injection process. After a sufficient quantity of polymer sheets were formed, approximately 0.1 wt. percent of an organotin catalyst (UL-28) was added to the polyol tank and stirred in the polyol blend. Next, another series of RIM formed sheets were prepared under the same conditions except that these sheets were formed in the presence of a supplemental catalyst. Both sets of low flexural modulus elastomeric sheets were subjected to a post cure process in an oven set at 265°F (129.5°C) for 30 minutes to complete the cure of these sheets. The properties determined on these sheets are reported in Table VII.

Claims: 1. A compatible single phase fluid comprising (1) at least one polyether polyol having an average hydroxyl functionality of from 2 to 4, an average molecular weight of at least 1000, and at least 30 percent of the hydroxyl groups being primary hydroxyl groups; (2) at least one polyol having an average hydroxyl functionality of from 2 to 6 and a molecular weight of less than 1000, in an amount that the mixture in the absence of the compatibility enhancer (3) is incompatible; (3) and as compatibility enhancer at least one material which is either a liquid or a solid forming a crystal clear liquid blend with (1) and (2) and having a melting point not greater than 200°C which material is represented by the formula wherein each R is independently hydrogen or a hydrocarbyl group having a sufficient number of carbon atoms such that the molecular weight of such group is not greater than 400; in an amount sufficient to maintain the composition in a single liquid phase for at least 5 days at 25°C but not causing gellation. 2. A compatible single phase fluid of Claim 1 wherein Component (1) has an average hydroxyl functionality of from 2 to 3; an average molecular weight of from 2000 to 8000; Component (2) has an average hydroxyl functionality of from 2 to 4 and an average molecular weight of from 60 to 600. 3. A compatible single phase fluid of Claim 2 wherein Component (1) has an average hydroxyl functionality of 3 and contains at least 10 weight percent terminal oxyethylene groups. 4. A compatible single phase fluid of Claim 3 wherein Component (1) is a glycerine initiated polyoxypropylene triol containing at least 14 weight percent terminal oxyethylene groups and Component (2) is ethylene glycol. 5. A compatible single phase fluid of Claim 4 wherein said compatible mixture contains up to 6,25 weight percent of a primary amine-containing material. 6. A compatible single phase fluid of Claim 1 wherein Component (3) is urea or dimethyl urea. 7. A compatible single phase fluid of Claim 2 wherein Component (3) is urea or dimethyl urea. 8. A compatible single phase fluid of Claim 3 wherein Component (3) is urea or dimethyl urea. 9. A compatible single phase fluid of Claim 4 wherein Component (3) is urea or dimethyl urea. 10. A compatible single phase fluid of Claim 5 wherein Component (3) is urea or dimethyl urea. 11. A compatible single phase fluid according to claim 1 comprising (1) 100 parts of weight of a polyol comprising a mixture of (a) 93 weight percent of a polyol prepared by reacting glycerine with propylene oxide and subsequently end-capping with 18 weight percent ethylene oxide and having 77 percent primary hydroxyl groups and an average hydroxyl equivalent weight of 1650 and (b) 7 weight percent of an aminated polyoxypropylene glycol having an average molecular weight of 400; (2) 18 parts of weight of ethylene glycol; and (3) 3 parts by weight of urea.

Inventors: OLSTOWSKI, FRANCISZEK, PEFFLEY, RICHARD D.
Applicants: THE DOW CHEMICAL COMPANY
Application year: 1984
Main classification: C08G18
IPC codes: C08G18, C08K5, C08L75, C08L71