PROCESS FOR RECOVERY OF HETEROGENEOUS WASTE PLASTIC MATERIALS, AND APPARATUS USABLE IN CARRYING OUT THE SAME

Abstract: Following an initial operation possibly required for separation from other types of refuse, waste plastics ma­ terials are triturated or crushed and cold-mixed. The triturated and mixed wastes undergo a first heating stage at a first temperature, with a view to obtaining a mass in an initial state of plastification. This mass subsequently under­ goes a second heating stage at a second temperature, generally different from said first temperature, until there is obtained thereform a homogeneously melted mass. The apparatus comprises a generally tubular housing (21) carrying at one end thereof a triturating device (2) within which the wastes are reduced to fragments and cold-mixed. The triturating device (2) comprises a toothed rotor (9) fitted onto a rotary element (16) rotatably mounted within the hous­ ing (21) and provided with thrust surfaces for the material with a helicoidal development (24, 25, 26, 28). The hub (10) of the triturator (2) is provided with apertures (15) which permit the triturating material to penetrate radially into this hub (10), so as to be brought into contact with the thrust surfaces of the rotary element (16) which functions as a mixing member. On at least one longitudinal portion (19) of the rotary element (16), the thrust surfaces for the material are defined by angular screw-threaded sectors (25, 26) arranged according to at least two oppositely directed helicoidal trajectories.

Description: Process for the recovery of heterogeneous waste plastics materials, and apparatus usable in carrying out the same The present invention concerns the recovery of waste plastics material and relates, in particular, to a process for the recovery of waste plastics materials that are classifiable on the basis of their composition, as heterogeneous wastes. Such heterogeneous wastes are normally contained in solid urban and industrial refuse. The re-use of waste plastics materials, in permitting recovery of basic raw materials which would otherwise be destroyed, is to be considered as generally remunerative by virtue of the high value of the recoverable materials. Moreover, it solves, in a particularly advantageous manner, the problem of disposing of waste materials which would otherwise be likely to contribute considerably to the pollution of the environment. Well known and currently used processes for the recovery of waste plastics materials provide for the extrusion, blow-moulding and injection-moulding of the waste material. Such processes are, however, in general applicable only to homogeneous wastes that is to say, wastes consisting of a single component only or else to wastes which, whilst not being entirely homogeneous, contain, in addition to a predominant component, negligible percentages of different components. The application of such processes to heterogeneous wastes, that is to say, waste plastics materials derived from a diversity of basic substances, has not up to now permitted the achievement of satisfactory results due to the occurrence of phenomena of incompatibility, of poor adherence or repulsion between the various components treated. Such phenomena cause the recovered products to have very inferior mechanical properties, such as to render impossible any further utilisation thereof. The object of the present invention is to provide a process that permits the recovery or recycling of heterogeneous plastics waste and refuse materials, that is to say, plastics materials derived from basic substances or types or groups or families which differ from one another. According to the present invention, such an object is achieved by a process for the recovery of heterogeneous waste plastics materials, characterised in that it comprises the operations of: - triturating the plastics waste materials; - cold-mixing the triturated waste materials; - subjecting the triturated and mixed waste materials to a first stage of heating in a first temperature range, with a view to obtaining from the said triturated and mixed wastes a mass in an initial state of plastification; - subjecting the said mass in an initial state of plastification to a second heating stage in a second temperature range, generally different from the said first temperature range, until there is obtained from the initially plastified mass a homogeneous melted mass of recovered plastics material. Whilst having observed the fully repeatable nature of the process, the Applicant is not, for the moment, in a position to furnish precise indications regarding the chemico-physical mechanisms underlying the invention. Without any wish for conclusive adoption of any specific theory, it may be observed that the process according to the invention differs from the processes currently used for the recovery of (homogeneous) wastes of plastics materials, in that there is not generally envisaged any addition, to the wastes undergoing treatment, of chemical additives and of substances to ensure compatibility in mixing. In particular, the Applicant has been able to observe that especially advantageous results can be achieved when the first and second heating stages are carried out without any substantial interruption between them, and when the said heating stages are carried out with a virtual absence of rapid transitions of pressure and temperature, and with the application to the waste materials and to the plastified and melted masses obtained therefrom of ranges of mechanical stress that are substantially uniform. It has in fact been observed that the product subjected to the recovery process is susceptible to sudden pressure or temperature changes. Such changes are at the root of phenomena of creep which seriously prejudice the properties of the recovered product. It is moreover important to prevent the homogeneously melted mass from being subjected to significant mechanical forces or to significant pressure or temperature gradients. It is furthermore noted that, in the present description and in the subsequent claims, the term "wastes" is understood as referring generally to heterogeneous mixtures of plastics materials howsoever produced in an industrial or a consumer context. The present invention relates, furthermore, to apparatus for the mixing of plastics materials comprising a tubular housing into one end of which the material to be mixed is fed, and a rotary element rotatably mounted within the said housing, and provided with thrust surfaces with a helicoidal development for acting on the material. The apparatus according to the invention, which has been developed with specific reference to the process for recovering waste plastics materials as described previously, but which can, however, be usefully applied for the mixing of different types of plastics materials such as, for example, components for paints, etc., is characterised in that the said rotary element is provided, on at least one of its longitudinal portions, with thrust surfaces for the material which are discontinuous and arranged according to at least two oppositely directed helicoidal trajectories. In other words, in at least one longitudinal section of the rotating element of the apparatus according to the invention, the thrust surfaces for the material are not constituted by one or more continuous helicoidal screw threads (as in the case of similar apparatus according to the prior art), but by angular sections of threads (blades) distributed in at least two groups each of which comprises angular threaded sections orientated according to a common pitch, that is to say, in such a way as to exert a unidirectional thrust on the material undergoing treatment, through the effect of the rotation of the rotor. The two groups of angular threaded sections therefore exert upon the material opposing thrusts which promote the thorough mixing and homogenizing of the said material. Preferably the housing of the apparatus has associated appendages extending into the housing itself and capable of cooperating with the thrust surfaces of the rotor so as to effect a mixing action on the material to be treated. In carrying out the waste plastics material processing previously described the apparatus according to the invention avoids subjecting the waste material to significant mechanical stresses, which could give rise to creep phenomena such as to render the recovered product effectively unusable. The invention will now be described, purely by way of non-iimiting example, with reference to the appended drawings, wherein: - Figure 1 is a partially cut away, longitudinal axial sectional view of apparatus for use in carrying out the process according to the invention; - Figure 2 is a schematic illustration, in an ideal flat plane development, of the arrangement of some of the elements illustrated in Figure 1, and - Figure 3 is a sectional view along the line III-III in Figure 1. The description makes specific reference to the application of the invention for the recovery of waste plastics materials contained in solid urban refuse and in solid industrial refuse. Solid urban refuse normally includes, in admixture with metal, glass, paper and organic composts derived from traditional household garbage, various types of plastics materials derived from packaging, such as bags, film, small baskets, trays and similar packaging products. Industrial plastics refuse is constituted by remnants or off-cuts resulting from the working processes or moulding, extrusion, rolling and blow-moulding carried out in industry, particularly in the packaging industries, the car-manufacturing industries and the electro-mechanical industries. The plastics materials which are present, in different amounts, both in urban refuse and in industrial refuse are typically the following: high-density polyethylene (HDPE), low-density polyethylene (LDPE), polypropylene (PP), polyvinyl chloride (PVC), polystyrene (PS), acrylonitrile-butadiene-styrene/ (ABS), polymethylmethacrylate (AM), polyester (PT), polyamide-(nylon) 6 (PA6), polyamide (nylon) 11 (PAll) and acetal resin (POM). Also frequently found in industrial wastes are polyurethane elastomer, polypropylene loaded with talc or various fibres, and polyamide (nylon) 66 loaded with glass fibres. Even though the composition by weight of the wastes vary significantly from zone to zone, depending upon vary significantly from zone to zone, depending upon the particular commercial and industrial activities pursued in each, the distribution by weight of the plastics waste components is substantially as follows: - polyethylene-polypropylene 60% - polystyrene 20% - polyvinyl chloride 15%, and - other components 5%. Whether in urban refuse or in industrial wastes polyolefins, polystyrene resins and vinyl resins, therefore, constitute the majority or prevalent component. Industrial refuse is distinguished essentially through the specific presence therein, as a minority or additional component, of polyamide resins, acetal resins and polyesters. The recovery process proper is normally preceded by a preliminary operation for the separation of the plastics wastes from the other materials with which such wastes may have become mixed, for example, metal, glass, paper, organic composts and other garbage. The separation may be carried out by any known method: mechanical sorting with screening, separation using a magnetic system, compressed air jets, washing, centrifuging, drying, or flotation, or again separation on the basis of density. These are prior art techniques currently used at collection centres for urban cleaning services and for the disposal of industrial waste materials. The recovery process is commenced with an initial stage of triturating (crushing), which reduces the waste materials to fragments having dimensions typically ranging from 2 to 4 mm. In the specific case in which the waste materials may comprise a significant quantity of thin rolled sections, it is advisable to proceed by compacting the rolled sections and then cutting them up. Following or during the trituration stage, the wastes are subjected to a cold-mixing operation, designed to ensure a strictly uniform distribution of the fragments of the various waste materials contained within the mass of the triturated materials. The triturated and mixed wastes are subsequently subjected to a heating operation, with a view to obtaining, from the mixture of the triturated wastes, a homogeneous fluid mass. For the heating of the waste, there are envisaged two successive stages carried out at generally different temperatures. The first heating stage is carried out at a temperature typically within the range of 1200C to about 1500C. The objective in this first heating stage is to obtain, from the triturated and mixed wastes, a mass that is found to be in an initial state of plastification. Preferably the material that is heated is also subjected to continuous mixing in such a way as to bring about the thorough and uniform dispersion of the various components of the waste material within the plastified mass. The experiments conducted by the Applicant indicate that the temperatures to be considered as preferred during the first heating stage are those within the range from about 1200C to about 1400C for waste materials substantially consisting of polyolefine resins, polystyrene resins and vinyl resins, and temperatures within the range from about 1300C to about 1500C, for waste plastics materials in which,as well as a prevalent component consisting of one of the aforesaid resins there may be present an additional component specifically composed of polyamide resins, acetal resins and polyesters. In terms of an actual process the lower range of temperatures is to be considered as preferred for the treatment of waste plastics materials derived from urban refuse. The higher range of temperatures has, on the other hand, proved to be better suited for the treatment of wastes of plastics materials derived from industrial refuse. The duration of this first heating stage does not, in itself, constitute a critical parameter, and it is, therefore, adaptable according to the quantity of material treated, the size of the processing plant used and the operating characteristics of the latter. Any pointless prolongation of the heating stage is generally to be avoided once the plastification of the processed mass has been achieved. The plastified mass is subsequently subjected to a second heating stage at a temperature typically within the range of about 2200C to about 2600C. This second heating stage is effected without any substantial discontinuity with regard to the preceding stage, thus preventing the plastified mass from being subjected to significant temperature gradients. For the second heating stage, the plastified mass may be maintained within the apparatus in whichthe first heating stage has been carried out, the operating temperature of the apparatus being gradually increased and the action of mixing the plastics material being continued throughout. As in the first heating stage, it has been shown to be preferable to choose different temperature ranges for wastes substantially consisting of polyolefine, polystyrene and vinyl resins, and for wastes containing as an additional component polyamide, acetal and polyester resins. For the first materials, what has, in fact, been found to be particularly advantageous is a choice of processing temperature within the range of about 2200C to about 240 C; for the others, the best results have, however, been obtained with processing temperatures within the range of about 2400C to about 2600C. The objective in the second heating stage is to transform the plastified mass, obtained as from the first heating stage, into a melted mass of recovered plastics material which is largely homogeneous. Also the duration of the second heating stage is not, in itself, a critical parameter; this duration may, therefore, be adjusted according to the specific requirements for effecting the process. During both the heating stages, in order to avoid the formation of combustion gases, it is necessary to prevent the treated material from being permitted, in the molten state, to incorporate or even simply to come into contact with air. During the heating stages any rapid temperature or pressure transitions are equally to be avoided. In the final stage of the process, the homogeneous melted mass of recovered plastics material may be subjected to various treatment operations such as, for example: - casting into mould elements, such as shaping or moulding containers which permit, as the final direct result of the recovery process, the production of finished articles consisting of recovered plastics material; - extrusion with a view to obtaining semifinished products such as bars or slabs; and - the formation of granules usable for the completion of moulding or extrusion operations. In the same way as in the preceding heating stages, it is, in any case, necessary to prevent the recovered plastics material from being subjected to marked thermal or mechanical stresses. In particular during casting into mould elements, the molten mass is subjected to a compacting action, applying a light mechanical compression to the poured mass, for example, by means of a piston. When the natural cooling of the cast mass proves imcompatible with the requirements for a rapid recovery process, the material poured into the mould elements should be subjected to a controlled cooling. The casting operation and the ensuing cooling of the cast mass should be controlled in such a way as to permit the relaxation of the cast mass, that is to say, the gradual reduction of the tensions within the mass undergoing casting, the dimensions of which are maintained substantially constant. As is known, said reduction substantially results from the presence of viscous deformations with in the mass itself. The products obtained generally have mechanical and technical characteristics that are variable according to the composition of the waste material subjected to the recovery process. In every case, the products obtained through the process according to the invention have been shown to be entirely devoid of macroscopic defects (such as, for example, surface discontinuities) and have always exhibited good mechanical properties. In Figure 1, there is generally indicated by reference numeral 1 apparatus for use advantageously for carrying out the process for recovering waste plastics materials previously described. For simplicity of illustration the apparatus 1 may ideally be subdivided into three component units, that is to say: - a crushing and cold-mixing unit 2, - a hot-mixing and at least partial homogenisation unit 3, and - a final homogenisation unit 4. The apparatus 1 is provided with fixing elements, illustrated in the form of brackets 5, which permit the mounting thereof upon a base-frame or bed-plate, not shown in the drawings. Upon this base-frame or bed-plate is mounted a motor such as an electric motor which drives, by means of a gear train generally indicated 6, a main shaft 7 rotatable about a horizontal axis. A sleeve element 8 is mounted rotatably on the shaft7, adjacent one end thereof, and drives a rotor 9 constituted by a tubular hub 10 from which project a plurality of radial teeth or fingers 11 positioned in an array (four in the example illustrated). The sleeve 8 is also rotatably driven by the gears 6 which are designed (according to criteria in themselves widely known) in such a way as to permit the rotation of the shaft 7 and of the sleeve 8 at different speeds, selected from respective ranges of variation according to the requirements applicable thereto, and in opposite directions. The gears 6 are housed within a robust metal casing 12, a part of which, indicated 13, has a generally channel section profile, open upwards, which extends so as to enclose the rotor 9. The casing part 13 therefore defines with respect of the rotor 9 a mixing chamber into which there can be dropped the heterogeneous waste plastics materials which it is intended to subject to a recovery process. The internal surface of the crushing chamber defined by the casing part 13 is provided with tooth-shaped or beak shaped projections 14 (Figure 3) which extend in a radial direction towards the rotor 9 in interpenetrating relation to the teeth 11 of said rotor. The rotational trajectories described by the teeth 11 during the rotation of the rotor 9 hence pass through the spaces formed between the projections 14, thus performing a shredding and triturating action on the material that is introduced into the chamber in which the rotor 9 turns. The material thus shredded and triturated also undergoes a thorough cold-mixing process through the effect of the driving action of the teeth 11 of the rotor. At intermediate angular positions between the positions in which the teeth 11 extend apertures 15 are provided in the side of the hub 10 of the rotor 9 to permit the triturated material to penetrate within the said hub 10. A rotary element generally indicated 16 extends through the cavity of the hub 10. In very broad terms, this element may be likened to a screw (scroll) of a standard screw extruder of which the core, indicated 17, constitutes a prolongation of the shaft 7 rotatably driven by the gears 6. An end portion of the element 16, indicated 18, is extended, as previously indicated, within the hub 10 of the rotor 9. The intermediate portion and the other end portion of the element 16, indicated respectively by numerals 19 and 20, are, on the other hand, extended within a tubular housing (pipe) 21 which projects from the casing 12 in a direction axially aligned with the shaft 7 and the core 17 of the element 16. The wall of the housing 21 is made of material which is a good heat conductor, such as a metal, and it is encircled by a plurality of armoured electrical resistance heating elements 22 or similar heating elements (such as flow ducts for a diathermic oil), which permit the internal cavity of the housing 21 to be brought to predetermined temperature levels, which may be different in the various longitudinal portions of the said housing 21. The electrical resistance heating elements 22 are enclosed within a further tubular casing of thermally insulating material 23 designed to contain the external dispersion of heat from the apparatus. The first portion 18 of the element 16 has a configuration that is entirely comparable with that of standard screw or scroll extruders. In this portion, the core 17 is effectively encircled by a continuous helicoidal screw thread 24. This screw thread constitutes a thrust surface which, through the effect of the rotation of the core 17 driven by the shaft 7, imparts to the triturated and cold-mixed material which penetrates within the hub 10 through the apertures 15 an ordered motion of progression towards the intermediate portion 19. During the progression towards this# latter portion, the material arriving from the chamber in which the rotor 9 turns undergoes a further final mixing process. The intermediate portion of the rotary element 16 differs substantially from the preceding portion 18 in that from the core 17 there extends a plurality of helicoidally developed blades 25, 26, which conform essentially to angular sectors of helicoidal screw threads. In the intermediate section 19, the rotary element 16 is thus provided with thrust surfaces for the material which follow overall a helicoidal path like the screw thread 24: in contrast to the latter the blades 25, 26 have a discontinuous development, being angularly spaced apart. Moreover, the blades 25, 26 are arranged in two groups or families according to the orientation of the pitch thereof. In particular, as illustrated in Figure 2 (which represents the ideal development in a flat plane cut along a cylindrical surface surrounding the core 17 of the rotary element 16), the blades 25 constitute angular sections of one or more screw threads which wind around the core 17 in a direction reflecting that of the screw thread 24, whilst the blades 26 constitute angular sections of at least one other screw thread which winds around the core 17 in an opposite direction. During the rotation of the element 16, the blades 25 therefore exert upon the material contained in the housing 21 a direct thrust in the direction which tends to move the material away from the first portion 18 (from left to right in Figure 1). At the same time the blades 26 exert upon the material a direct thrust in a direction that is exactly opposite (from right to left in Figure 1). The overall result obtainable is a thorough and intimate mixing of the material which is present within the tubular housing 21. Since this housing is heated by the electrical heating elements 22, the triturated material arriving from the rotor 9 gradually passes into the molten state. In particular, when applying the recovery process to waste plastics material previously described, the portion of the housing 21 which faces towards the rotor 9 is maintained at temperatures in the order of 1200C to 1500 C. In this portion of the housing 21 there is thus gradually formed a mass in an initial state of plastification. Through the effect of the thrust action exerted by the first portion 18 of the element 16 upon the new material introduced into the housing 21 from the rotor 9, the said plastified mass passes subsequently into the portion of the housing 21 that is at furthest from the rotor 9. In this portion the temperatures are of the order of 2200C to 2600C, leading gradually to the formation of a homogeneously melted mass of recovered plastics material. The heating of the material present within the housing 21 is carried out whilst this material is subjected to a continuous mixing action effected by the blades 25 and 26. This mixing action does not, however, involve the application of significant mechanical stresses or of squashing and stirring forces such as would, however, arise in a mixing machine in which the screw thread 24 were also to be extended within the intermediate portion 19 of the element 16. In order to render the mixing action more thorough, the internal surface of the housing 21 is provided with appendages 27 which project radially into this housing 21 in positions permitting them to penetrate between the blades 25, 26, as schematically illustrated by broken lines in the developed plan view of Figure 2. In the example illustrated, and according to a solution currently preferred, the appendages 27 consist of rods which are cylindrical or have a transverse section of oval or a chamfered dihedral profile, and which are inserted in radial holes provided in the walls of the element 21. The appendages 27 consist in fact of fixed inserts which cooperate with the blades 25 and 26 so as to improve the mixing action upon the plastified and melted product which advances within the housing 21. The use of rods or of similar inserts (screws, etc.), inserted in radial holes provided in the housing 21 is shown to be advantageous since it affords the possibility of varying the number and the distribution of the appendages 27, according to the characteristics of the product undergoing treatment. In order to take into account the characteristics of the various mixtures of materials treated it is also advantageous for the blades 25, 26 to be mounted upon the core 17 in such a way that it proves possible to orientate and remove them, thus also ensuring that it is possible to vary the pitch and the number thereof. A possible practical solution is found, to this end, in the mounting of the blades 25, 26 upon rings which may be splined onto the core 17 in various numbers and at various spacings according to the characteristics of the material treated. The structure of the terminal portion 20 of the element 16 may be likened substantially to the structure of the terminal compression portions of standard screw or Archimedean screw extruders. In this portion there is again a continuous helicoidal screw thread 28 winding around the core 17. The core 17, however, has a tapered profile diverging towards the outlet end of the housing 21. The angle of taper of the core is selected in relation to the rotational speed of the element 16, in such a way as to prevent excessive pressure gradients upon the homogeneously melted mass which is expelled from the housing 21. At the outlet end of the housing 21 there is positioned a homogenization unit 4 consisting essentially of a static mixer (of known type) comprising further mixing elements 29 arranged in cascade. Each element 29 comprises a feed chamber of tetrahedral shape from which there emerge a number of ducts which come together, according to a generally cruciform arrangement in the tetrahedral chamber of the element 29 disposed downstream. These elements perform a fluid stream mixing action. At the outlet of the unit 4 there is disposed an extruder 30 which permits the formation, from the homogeneous melted mass issuing from the unit 4, of semi-finished extrusions or granules ("chip") or products in the form of spaghetti, for feeding to other moulding machines.

Claims: CLAIMS 1. A process for the recovery of heterogeneous waste plastics material, characterised in that it comprises the operations of: - triturating the said plastics waste material, - cold-mixing the triturated waste materials, - subjecting the triturated and mixed wastes to a first heating stage within a first range of temperatures, to obtain from the said triturated and mixed wastes a mass in an initial state of plastification; - subjecting the said mass in an initial state of plastification to a second heating stage within a second range of temperatures, generally different from the said first range of temperatures, until there is obtained from the initially plastified mass a homogeneous melted mass of recovered plastics material. 2. A process according to Claim 1, characterised in that it further comprises the operations of: - continuous mixing of the wastes during the said first heating stage, and - continuous mixing of the said mass in an initial state of plastification during the said second heating stage. 3. A process according to Claim 1 or Claim 2, characterised in that said first and said second heating stages are carried out with a virtual absence of rapid pressure and temperature transitions and with the application to the wastes and to the plastified and melted masses obtained therefrom of substantially uniform ranges of mechanical stress. 4. A process according to any one of the Claims 1 to 3, characterised in that said first and second heating stages are carried out consecutively without any substantial interruption between them. 5. A process according to any one of the preceding claims, characterised in that said first and second heating stages are carried out in a controlled environment, in the virtual absence of air. 6. A process according to any one of Claims 1 to 5, characterised in that said first heating stage is conducted at a temperature substantially within the range of about 1200C to about 1500C. 7. A process according to Claim 6, applied to waste plastics materials substantially consisting of polyolefine, polystyrene and vinyl resins, characterised in that said first heating stage is conducted at temperatures susbtantially within the range of about 1200C to about 1400C. 8. A process according to Claim 6, applied to waste plastics materials with a prevalent component of polyolefine, polystyrene and vinyl resins and an additional component of polyamide, acetal and polyester resins, characterised in that said first heating stage is conducted at temperatures substantially within the range of about 1300C to about 1500C. 9. A process according to any one of the preceding claims 1 to 8, characterised in that said second heating stage is conducted at temperatures substantially within the range of about 2200C to 2600C. 10. A process according to Claim 8, applied to waste plastics materials susbtantially consisting of polyolefine, polystyrene and vinyl resins, characterised in that said second heating stage is conducted at temperatures substantially within the range of about 2200C to about 2400C. 11. A process according to Claim 8, applied to waste plastics materials with a prevalent component of polyolefine, polystyrene and vinyl resins and an additional component of polyamide, acetalic and polyester resins, characterised in that said second heating stage is conducted at temperatures substantially within the range of about 2400C to about 260 C. 12. A process according to any one of the preceding claims, applied to the recovery of waste plastics materials contained in solid refuse, characterised in that it includes the preliminary operation of separating said wastes from the mass of solid refuse. 13. Apparatus for the mixing of plastics materials, usable in carrying out the process according to any one of the preceding Claims 1 to 12, and comprising a generally tubular housing (21) fed at one end (2) with the material to be mixed and a rotary element (16) rotatably mounted within said housing (21) and provided with thrust surfaces for the material having a helicoidal development (24, 25, 26, 28), characterised in that said rotary element (16) is provided, on at least one of its longitudinal portions (19), with thrust surfaces(25,26)for the material which are discontinuous and arranged according to at least two oppositely directed helicoidal trajectories. 14. Apparatus according to Claim 13, characterised in that said discontinuous thrust surfaces (25, 26) are provided in the middle portion (19) of the rotary element (16). 15. Apparatus according to Claim 13 or Claim 14, characterised in that said thrust surfaces are in the form of blades (25, 26) of a helicoidal development. 16. Apparatus according to any one of Claims 13 to 15, characterised in that with said generally tubular housing (21) there are associated appendages (27) extending into the housing (21) itself and capable of cooperating with the said discontinuous thrust surfaces (26, 26) to effect a mixing action on the material to be treated. 17. Apparatus according to any one of Claims 13 to 16, characterised in that it further includes a device (2) for the preliminary trituration of the material to be treated, in that said device (2) comprises a toothed rotor (9) provided with a tubular hub (10), and in that the wall of said hub (10) is provided with apertures (15) which permit the triturated material to penetrate radially into the hub (10) so as to be brought into contact with the thrust surface (24) of the rotary element (16). 18. Apparatus according to Claim 17, characterised in that said device (2) comprises a casing (13) in which said rotor (9) is rotatably mounted, and in that said casing (13) is provided with projections (14) extending towards the rotor (9) in interpenetrating relation to the teeth (11) of said rotor. 19. Apparatus according to Claim 13 and Claim 16, characterised in that it includes drive means (6) for imparting to the said rotary element (16) and to said rotor (9) rotational movements in opposite directions.

Inventors: FORNASERO, RENATO
Applicants: FORNASERO, RENATO
Application year: 1984
Main classification: B29B17
IPC codes: B29C47, B29B9, B29B17, B29B7