EPOXIDATION OF ETHYLENE

Abstract: A process for the selective epoxidation of ethylene to ethylene oxide comprises reacting ethylene with a hydroper­ oxide, for example tert-butyl hydroperoxide, in the presence of a complex formed from a Group VB or Group VIB metal and a bidentate, nitrogenous chelate ligand of general formula HO-Ar-CH=NR The reaction may be carried out optionally in the presence of an epoxide such as ethylene oxide or cyclohexene oxide.

Description: EPOXIDATION OF ETHYLENE The present invention relates to a process of epoxidising ethylene using hydroperoxides as the epoxidising agents. Epoxidation of unsaturated compounds, especially olefins, gives rise to epoxides which are the basic monomers for industries based on epoxide polymers and copolymers eg epoxy resins, surfactants, adhesives and elastomeric compositions. Ethylene oxide, propylene oxide and cyclohexene oxide are but a few specific examples of such epoxide monomers. In liquid phase epoxidation processes, the choice of catalyst nist depend upon the following factors: (a) its inertness towards the liquid reaction medium, (b) the speed of reaction, the rate of the selectivity to the desired epoxide product, (c) the cost of the catalyst, (d) the ease of its recovery from the reaction mixture, and (e) its stability in the presence of the hydroperoxide epoxidising agent s. Ideally it would be desirable to convert all the hydroperoxide used into the epoxide in the shortest possible time with maximum selectivity to the olefin oxide. For simple olefins the order of reactivity is related to the number of alkyl substituents coordinated to the carbon-carbon double bond. Ethylene has no such substitutents and is a particularly difficult olefin to epoxidise. Of the several catalysts that have been proposed for the epoxidation of olefins, compounds of the metals in Group V and VI of the Periodic Table have been most effective. Specifically, compounds of molybdenum, vanadium and tungsten have been found to be most suitable. Catalyst compositions containing molybdenum whether in the form of inorganic compounds or as organo-metallic complexes have given the best results. Of these, complexes of molybdenum oxide with organic nitrogen containing bases have been the most successful. British Patent Specification No 1365589 describes the use of complexes of this type in such a reaction. In general, however, these catalysts show poor conversion and selectivity to the epoxide when the oleo in used is ethylene. The object of the present invention, therefore, is to provide complexes for use as catalysts for the epoxidation of ethylene which enable improved conversion and selectivity to ethylene oxide to be achieved. Accordingly, the present invention comprises a process for the epoxidation of ethylene in the liquid phase using a hydroperoxide as an epoxidising agent and, as catalyst, an effective amount of a chelate complex of a Group VB or VIB metal and a bidentate nitrogenous ligand characterised in that the bidentate nitrogenous ligand has the general formula: : HO-Ar-CB = NR wherein Ar is an arylene radical with the OH group and the -CH = NR group in an ortho relationship, R is selected from the groups consisting of OH, -Ar-X and -R1-N=CH-Ar-OH in which -Ar has the same significance as before, X is an -OH or a -COOH group and R1 is either an arylene group or a -(CH2)n-group in which n is an integer selected from 0, 1, 2, 3 and 4. Examples of nitrogenous bidentate ligands include HO-Ar-CH = N-OH (Salicylaldoxime), HO-Ar-CH = NArOH (N-salicylidene-2-aminophenol, hereafter referred to as SAP), HO-Ar-CH = N-Ar-COOH (N-salicylidene-2-aminobenzoic acid, hereafter referred to as SAN), HO-Ar-CH = N-Ar-N = CH-Ar-OH (phenylene bis(salicylimine), hereafter referred to as SALOPH), HO-Ar-CH = N-(CH2)2-N = CH-Ar-OH (ethylene bis(salicylimine), hereafter referred to as SALEN). In each of these compounds the substituents on the aryl nuclei are preferably in the ortho-position. These bases may be complexed either as such or in combination with other conventional ligands such as acetylacetonates. The Group VB and VIB metals referred to herein are suitably used as their oxides. The metals are suitably selected from molybdenum, vanadium and tungsten, and the preferred metal is molybdenum. The chelate complexes are used in the liquid phase with hydroperoxides in the conventional epoxidation reactions. Any of the conventional hydroperoxides may be used. It is preferable to use tert-butyl hydroperoxide. Examples of solvents that may be used as the reaction medium for the liquid phase epoxidation are hydrocarbons such as benzene, cyclohexane and cyclohexene; halogenated hydrocarbons such as dichlorobenzene; and alcohols such as tertiary butanol. It is preferable however to use a solvent which is stable towards oxidation under the reaction conditions. Thus, the ethylene, the chelate complex and the hydroperoxide may be dissolved in an oxidant-stable organic solvent and placed in a reactor equipped with a stirrer and thermometer. The molar ratio of the chelate complex to the hydroperoxide is suitably between 0.005 and 0.1, preferably between 0.02 and 0.05, most preferably 0.01. An excess of the solvent may be used in relation to the hydroperoxide. For instance, between 1.2 and 50 volumes of the solvent may be used per volume of the hydroperoxide. The epoxidation reaction occurs in the presence of an excess of ethylene in relation to the hydroperoxide so as to increase the utilisation of the latter. The ethylene to hydroperoxide molar ratio is suitably between 0.5 and 100, preferably between 2 and 20. The reaction mixture is suitably heated to a temperature of above 50"C, preferably between 50 and 1500C for the duration of the reaction to achieve high conversion of the hydroperoxide. The reaction may be carried out at atmospheric pressure or, as in the case where one of the reactants is a gas, at elevated pressure up to 100 bar. The sequence in which the reactants are added is not significant. However, it is preferable to mix the chelate complex and the hydroperoxide first before adding either component to the ethylene. A further surprising feature of the present invention is the improved ability of the catalyst to epoxidise the relatively inert olefin ethylene in the presence of an agent such as cyclohexene oxide. Thus if the mixture of the chelate complex and the hydroperoxide is added to a mixture of ethylene with cyclohexene oxide, the conversion and selectivity to ethylene oxide is further improved. The product epoxide, ie ethylene oxide may be used as an autocatalytic agent instead of cyclohexene oxide. The amount of epoxide added to the reaction mixture will depend upon the olefin being epoxidised. In general it is suitably between I and 10 moles per mole of the catalyst. The reaction may be carried out either batchwise or continuously. The present invention is further illustrated with reference to the following Examples. Major differences in both activity and selectivity have been observed in the catalytic activity of molybdenum catalysts depending on the actual nitrogenous chelating ligand coordinated. Examples 1-3 [(a) without added epoxide, (b) with added epoxide] illustrate catalysts which are selective to ethylene oxide particularly when an epoxide is added with the catalyst. Less selective are the catalysts of Examples 4 and 5 [(a) without added epoxide, (b) with added epoxide]. However, as Examples 6 and 7 show those complexes which use nitrogenous bases outside those described herein are much less selective towards ethylene oxide. In the Examples, some of the ligands are abbreviated as follows: N-Salicylidene-2-aminophenol as SAP N-Salicylidene-2-aminobenzoic acid as SAN" Phenylene bis(salicylimine) as SALOPH Ethylene bis(salicylimine) as SALEN 4-phenyliminopentanone-2 as PIP 3-phenylimino-1-phenylbutanone-1 as "PUB" Acetylacetonate as acac Thus, MoO2 (SALOPH) in Example l(a) and l(b) for instance, refers to a chelate complex of molybdenum oxide with phenylene bis( salicylimine). Moreover, the complexes Mo02(SAN)(acac) (Examples 2(a) and 5(b)) and MoO2(SAP) (Examples 4(a) and 4(b)) referred to below were prepared by the method described by J. Topich, in Inorg. Chem., 1981, 20, 3704-3707. The other complexes were made by ligand exchange between MoO2(acac)2 and the appropriate nitrogenous ligand in a refluxing solvent such as ethanol, toluene or tetrahydrofuran. The ligands PIP and "PUB" are not examples of the ligands defined herein but are included for purposes of comparison. Example l(a) An autoclave was charged with 20ml of a 2.78 molar solution of tert-butyl hydroperoxide in toluene and 0.lg of MoO2 (SALOPH). It was pressured to 50 bar with ethylene and heated to 90 C for 2 hours with stirring. It was then cooled to OOC and the contents discharged. Analysis by gas chromatography and titration showed that 60% of the tert-butyl hydroperoxide had been converted with 49% selectivity to ethylene oxide based on tert-butyl hydroperoxide. Example l(b) An autoclave was charged with 20ml of a 3.44 molar solution of tert-butyl hydroperoxide in toluene, 0.1g Mo02 (SALOPH), and 0.2ml cyclohexene oxide. It was pressured to 49 bar with ethylene and heated to 90 C for 1 hour. The conversion of tert-butyl hydroperoxide was 22% with 67t selectivity to ethylene oxide based on tert-butyl hydroperoxide. Example 2(a) An autoclave was charged with 20ml of a 2.78 molar solution of tert-butyl hydroperoxide in toluene and 0.05g Mo02(salicylaldoxime)2. It was pressured to 50 bar with ethylene and heated to 90 C for 2 hours. The conversion of tert-butyl hydroperoxide was 77% with 51% selectivity to ethylene oxide based on tert-butyl hydroperoxide. Example 2(b) An autoclave was charged with 20ml of a 2.39 molar solution of tert-butyl hydroperoxide in toluene, O.lg MoO2 (salicylaldoxime)2 and 0.2ml cyclohexene oxide. It was pressured to 49 bar with ethylene and heated to 900C for 2 hours. The conversion of tert-butyl hydroperoxide was 58% with 53% selectivity to ethylene oxide based on tert-butyl hydroperoxide. Example 3(a) An autoclave was charged with 20ml of a 4.30 molar solution of tert-butyl hydroperoxide in toluene and O.05g MoO2 (SALEN). It was pressured to 55 bar with ethylene and heated to 90"C for 2 hours. The conversion of tert-butyl hydroperoxide was 4% with 12% selectivity to ethylene oxide based on tert-butyl hydroperoxide. Example 3(b) An autoclave was charged with 20ml of a 3.44 molar solution of tert-butyl hydroperoxide in toluene, O.lg MoO2 (SALEN) and 0.2ml cyclohexene oxide. It was pressured to 47 bar with ethylene and heated to 900C for 1 hour. The conversion of tert-butyl hydroperoxide was 29% with 55% selectivity to ethylene oxide based on tert-butyl hydroperoxide. Example 4(a) An autoclave was charged with 20ml of a 3.39 molar solution of tert-butyl hydroperoxide in toluene and O.1g Mo02 (SAP). It was pressured to 55 bar with ethylene and heated to 900C for 2 hours. The conversion of tert-butyl hydroperoxide was 20% with 26% selectivity to ethylene oxide based on tert-butyl hydroperoxide. Example 4(b) An autoclave was charged with 20ml of a 3.44 molar solution of tert-butyl hydroperoxide in toluene, O.lg MoO2 (SAP) and 0.2ml cyclohexene oxide. It was pressured to 50 bar and heated to 900C for 2 hours. The conversion of tert-butyl hydroperoxide was 54% with 44% selectivity to ethylene oxide based on tert-butyl hydroperoxide. Example 5(a) An autoclave was charged with 20 ml of a 3.39 molar solution of tert-butyl hydroperoxide in toluene and 0.lg MoO2 (SAN) (acac). It was pressured to 55 bar and heated to 900C for 2 hours. The conversion of tert-butyl hydroperoxide was 62% with 29% selectivity to ethylene oxide based on tert-butyl hydroperoxide. Example 5(b) An autoclave was charged with 20ml of a 3.44 molar solution of tert-butyl hydroperoxide in toluene, 0.lg MoO2 (SAN) (acac) and 0.2ml cyclohexene oxide. It was pressured to 48 bar with ethylene and heated to 900C for 1 hour. The conversion of tert-butyl hydroperoxide was 67% with 18% selectivity to ethylene oxide based on tert-butyl hydroperoxide. Experiment A An autoclave was charged with 20 ml of a 3.40 molar solution of tert-butyl hydroperoxide in toluene, O.1g MoO2 (PIP)2 and 0.2 ml cycloyhexene oxide. It was pressured to 50 bar with ethylene and heated to 90"C for 2 hours. The conversion of tert-butyl hydroperoxide was 78% with 6% selectivity to ethylene oxide based on tert-butyl hydroperoxide. Experiment B An autoclave was charged with 20 ml of a 3.49 molar solution of tert-butyl hydroperoxide in toluene and 0.1g Mo02 (PPB) and 0.2 ml cyclohexene oxide. It was pressured to 50 bar ethylene and heated to 90 C for 2 hours. The conversion of tert-butyl hydroperoxide was 45% with 7% selectivity to ethylene oxide based on tert-butyl hydroperoxide. Experiments A and B, which do not constitute part of the invention as described, show that other bidentate nitrogenous ligands, which are not members of the class described herein, produce catalysts which are much less selective.

Claims: Claims 1. A process for the epoxidation of ethylene in the liquid phase using a hydroperoxide as an epoxidising agent and, as catalyst, an effective amount of a chelate complex of a Group VB or VIB metal and a bidentate nitrogenous ligand characterised in that the bidentate nitrogenous ligand has the general formula: HO-Ar-CH = NR wherein Ar is an arylene group with the OH group and the -CH=NR group in an ortho relationship and where R is selected from the groups consisting of OH, -ArOH, -Ar-COOH, and -Rl-N=CH-Ar-OH and R1 is either an arylene group or a -(CH2)n- group where n is an integer from O to 4. 2. A process as claimed in claim 1 characterised in that the reaction is carried out in the presence of an epoxide. 3. A process as claimed in claim 3 characterised in that the epoxide is either ethylene oxide or cyclohexene oxide. 4. A process as claimed in claims 1 or 2 characterised in that the bidentate nitrogenous ligand is salicylaldoxime. 5. A process as claimed in claims 1 or 2 characterised in that the bidentate nitrogenous ligand is & salicylidene-2-aminophenol. 6. A process as claimed in claims 1 or 2 characterised in that the bidentate nitrogenous ligand is phenylene bis(salicylimine). 7. A process as claimed in claims 1 or 2 characterised in that the bidentate nitrogenous ligand is ethylene bis(salicylimine). 8. A process as claimed in claim 1 characterised in that the bidentate nitrogenous ligand is N-salicylidene-2-aminobenzoic acid. 9. A process as claimed in claims 1 or 2 characterised in that the Group VIB metal is molybdenum. 10. A process as claimed in claims 1 or 2 characterised in that the molar ratio of the chelate complex to hydroperoxide is between 0.005 and 0.1. 11. A process as claimed in claim 10 characterised in that the molar ratio of the chelate complex to hydroperoxide is between 0.02 and 0.05. 12. A process as claimed in claims 1 or 2 characterised in that the olefin to hydroperoxide molar ratio is between 0.5 and 100. 13. A process as claimed in claims 1 or 2 characterised in that the reaction temperature is between 50 and 1500C. 14. A process as claimed in claims 1 or 2 characterised in that the olefin used is ethylene and the hydroperoxide is tert-butyl hydroperoxide. 15. A process as claimed in claims 1 or 2 characterised in that the reaction is carried out in an inert oxidant stable solvent. 16. Ethylene oxide characterised in that it is produced by a process claimed in any one of the above claims.

Inventors: KELLY, RAYMOND LESLIE
Applicants: BP CHEMICALS LIMITED
Application year: 1984
Main classification: C07D301
IPC codes: C07B61, B01J31, C07D301