MELT-SHAPABLE FLUOROPOLYMER COMPOSITIONS

Abstract: Melt-shapeable polymeric compositions comprising a first fluoropolymer of relatively low crystallinity and a second fluoropolymer of relatively high crystallinity, especially a fluoropolymer obtained by irradiating a fluoropolymer which cannot be melt-shaped in the absence of other polymers. The first fluoropolymer is preferably a copolymer of tetrafluoro­ ethylene and an perfluorinated comonomer, e.g. hexafluoro­ propylene or a perfluorinated vinyl ether. The second fluoro­ polymer is preferably tetrafluoroethylene which has been ir­ radiated to a dosage of 2.5 to 40 Mrad. The weight ratio of the first to the second polymer is preferably 0.3:1 to 2.5:1. The compositions are melt-shapeable, and the resulting shaped products have a valuable combination of properties derived from both fluoropolymers. For example, the compo­ sitions are particularly useful for electrical insulation, espe­ cially as low loss foamed insulation in coaxial cables.

Description: This invention relates to polymeric compositions comprising fluoropolymers. Fluoropolymers are well known and are useful in a broad range of applications. Some fluoropolymers can be melt-shaped, including for example polyvinylidene fluoride and copolymers of tetrafluoroethylene and ethylene, hexafluoropropylene, or a perfluorinated vinyl ether. These fluoropolymers have been used extensively for electrical insulation, particularly as melt-extruded jackets around conductors,and exhibit a valuable combination of physical and electrical properties. However, other fluoropolymers, in particular polytetrafluoroethylene (PTFE), which have very high crystallinity, also have such high molecular weights that they cannot be melt-shaped. This makes them difficult and expensive to process, and has severely restricted their use, despite the fact that in some respects they offer important advantages over the melt-shapeable fluoropolymers, in particular one or more of good elongation, high melting point ani lds loss tangent at high frequencis. Attempts have been made to produce similar polymers which retain these advantages but have relatively low molecular weights so that they can be melt-extruded. However, such polymers have such poor mechanical properties that they are of little practical value. For example, PTFE can be irradiated to produce a material which retains the crystallinity of the original polymer but has a relatively low molecular weight, but melt extrusion of this material results in products which are extremely brittle. We have now discovered a way of utilizing many of the excellent properties of highly crystalline fluoropolymers in compositions which can be melt-shaped. In particular, we have found that it is possible to obtain melt-shapeable compositions by mixing two fluoropolymers, the first having a crystallinity of less than 45% and being melt-shapeable in the absence of other polymers (eg. a copolymer of tetrafluoroethylene and hexafluoropropylene or a perfluorinated vinyl ether), and the second fluoropolymer having a crystallinity of at least 50% (eg. irradiated PTFE); and that products obtained by melt-shaping such compositions have a valuable combination of properties derived from both fluoropolymers. Thus, the shaped products have tensile and elongation values which are at least adequate for many purposes, coupled with other valuable properties such as elevated melting point and low loss tangent. In one aspect, the present invention provIdes a composition which can be melt-shaped and which comprises a mixture of a first fluoropolymer which has a crystallinity of less than 45% and which can be melt-shaped in the absence of other polymers, and a second crystalline fluoropolymer which has a crystallinity of at least 50%. In another aspect, the invention provides a shaped article prepared by melt-shaping a composition as defined above. The term "fluoropolymer.' is used herein to denote a polymer which contains at least 10%, preferably at least 25%, by weight of fluorine, or a mixture of two or more such polymers. The ter "perfluoropolymer" is used herein to denote a fluoropolymer in which all the substituents on the polymer backbone are fluorine atoms, or perfluoroalkyl or perfluoroalkoxy groups; the polymer backbone can consist of carbon atoms or can also contain hetero atoms, e.g. oxygen. Melt viscosities given in this specification are measured at 380 C at a shear rate of 100 sec 1. Crystan- linities given in this specification are measured usinc a differential scanning calorimeter (DSC). The first fluoropolymer is preferably a crystalline fluoropolymer, particularly a perfluoropolymer, which can be melt-shaped in the absence of other polymers. Thus the first fluoropolymer wili generally have a melt viscosity at 380 C of less than 106 poise, preferably less than 105 poise, particularly less than 5 x 104 poise. The lower the melt viscosity, the easier the comp-osition is to process, but (in general) the less desirable the properties of the final product. Accordingly, the melt viscosity of the first fluoropolymer is generally at least 10 poise, preferably at least 5 x 103 poise, particularly at least 1x104 poise, especially at least 2x104 poise. The first fluoropolymer is generaly a homopolymer or copolymer of one or more fluorine containing olefiniclly unsatured monomers, or a copolymer of one or more fluorine-containing olefinically unsaturated monomers and one or more olefines. The first fluoropolymer has a melting point of at least 150it, often at least 250'C, e.g. up to 350"C, the melting point being defined as the temperature above which no crystallinity exists in the polymer (or when a mixture of crystalline polymers is used, in the major crystalline component in the mixture). Particularly preferred first fluoropolymers are copolymers of tetrafluoroethylene with one or more perfluorinated monomers, e.g. hexafluoropropylene or a perfluorinated vinyl ether; such copolymers are preferably perfluoropolymers but can contain small proportions of units derived from monomers which are only partially substituted by fluorine or which are free from fluorine. Commercially available fluoropolymers of this type include those sold by E.I. du Pont de Nemours under the trade names FEP-l00, FEP-l60 and PFA. Other polymers which can be used as the first fluoropolymer include copolymers of ethylene and tetrafluoroethylene and optionally one or more other comonomers (known as ETFE polymers), e.g. a copolymer comprising 35 to 60 mole percent of ethylene, 35 to 60 mole percent of tetrafluoroethylene and up to 10 mole percent of one or more other comonomers; copolymers of ethylene and chlorotrifluoroethylene; polyvinylidene fluoride; and copolymers of vinylidene fluoride with one or both of hexafluoropropylene and tetrafluoroethylene, or with hexafluoroisobutylene. The first fluoropolymer has a crystallinity of less that 45%, preferably less than 30%, especially less than 20%. On the other hand, its crystallinity is preferably at least 5%, particularly at least 10B. The second fluoropolymer is a crystalline fluoropolymer, preferably a perfluoropolymer, which has a crystallinity which is at least 50%, preferably at least 60%, especially at least 65%. The melt viscosity (at 380'C) of the second fluoropolymer is generally less than 106 poise, preferably less than 105 poise, especially less than 2x104 poise. In many cases its melt viscosity (at 3800C) is at least 10, particularly at least 100, especially at least 1000. The invention is of particular value when the second fluoropolymer has been obtained by irradiating (eg. with an electron beam) a fluoropolymer which, prior to irradiation, had a melt viscosity at least 3 times, preferably at least 10 times, particularly at least 100 times, that of the first fluoropolymer (the difference can 5 be verv much larger, e.g. by a factor of the order of 10 or more). The second fluoropolymer can be (prior to irradiation) a melt-shapeable polymer, but the invention is particularly useful when the second polymer is one which, prior to irradiation, could not be melt-processed under practical conditions, because the invention make it possible to utilize at least some of the valuable properties of such polymers while yet retaining the enormous advantages of melt-processing. Preferred second fluoropolymers are polymers of tetrafluoroethylene, in particular polytetrafluoroethylene (PTFE), for example that commercially available under the trade name Teflon from E.I. du Pont de Nemours. Surprisingly, the presence of the irradiated polymer does not have a substantial adverse effect on the processing characteristics of the first polymer, and can indeed substantially improve those characteristics. Thus the novel compositions have a melt viscosity which is preferably less than 2 times, particularly less than 1 time, especially less than 0.5 time, the melt viscosity of the first fluoropolymer. The irradiation will generally be carried out in the substantial absence of any radiation cross-linking agent, so that the predominant effect of the radiation is to degrade the fluoropolymer to a lower molecular weight, more brittle material. The radiation dose is preferably 2.5 to 40 Mrad, particularly 5 to 30 Mrad. The second fluoropolymer can be in the form of granules or any other form when it is irradIated. The relative amounts of the first and second fluoropolymers can vary widely, depending primarily on the desired final product. Thus the ratio by weight of the first to the second fluoropolymer can be from 0.05:1 to 20:1. For many end uses, the preferred rating is 0.3:1 to 2.5:1, particularly 0.3:1 to 1:1, e.g. 0.4:1 to Q.6:1. The polymers can be blended in any convenient way, for example by physical blending of the polymers in the form of granules. The compositions can contain, in addition to the first and second fluoropolymers, other ingredients which do not obviate the advantages provided by the fluoropolymers. Thus the compositions can contain non-polymeric ingredients, for example antioxidants, processing aids, acid acceptors, fire retardants and fillers (reinforcing or non-reinforcinge, and/or relatively small quantities of other polymers. When the composition is to be foamed, it can also contain a foaming agent and/or nuclearing agent. The composition can be melt-shaped in any convenient way, including molding and melt-extrusion, which is generally preferred, especially when the composition is used to provide insulation on an elongate electrical conductor. The composition can provide the sole insulation over an electrical component, or it can provide one of two or more insulatng jackets. The composition can be foamed as part of the shaping oration, and this is particularly desirable when it is important that the insulation should have low loss at high frequencies, for example the insulation in a coaxial cable transmitting high frequency electro-magnetic energy. EXAMPLES The invention is illustrated by the following Examples, which are summarized in the Table below. Examples 1-5 are comparative Examples. The various ingredients given in the Table are further identified below. FEP-160 is a high molecular weight copolymer of tetrafluoroethylene and hexafluoropro pylene, available frown du Pont. PFA-350 is a high molecular weight copolymer of tetrafluoroethylene and a perfluoro vinyl ether, also available fro du Pont. PTFE is hIgh molecular weight polytetrafluoro- ethylene available under the trade nase Teflon from du Pont. PTFE !10 MR) is PTFE which has been irradiated to a dose of 10 Mesarads. PE (20 MR) is PTFE which has been irradiated to a dose of 20 Megarads PTFE (3C MR) is PTFE which has been irradiated to a dose of 30 Megarads The tensile strengths and elongations reported in the Table were measured by pulling a cylindrical rod in an Instron Tensile Testing Machine using an elongation rate of 2 inches/minute. The irradiated PTFE's were too brittle for their tensile strengths and elongations to be measured. The crystallinities reported in the Table are calculated from measured heats of fusion, using a value of 22.2 calories/gram for 100% crystalline polymer. The viscosities reported in the Table are measured (as discussed above) at 380 C at a shear rate of 100 sex 1 in a Rheometrics viscometer. The Loss Tangents reported in the Table are measured at a frequency of 10 GHz. The blends were prepared by dry-mixing the components, followed by melt-blending in a counter-rotating twin-screw extruder. Cylindrical rods for tensile testing were meltshaped from the blends (or from the individual polymers) by extrusion through a cylindrical die at 380 C. -11- MPO880 TABLE Viscosity Loss Tangent Tensile Elongation Tm ( C) Crystallinity (poise) (x104) (psi) % C % 1. FEP-160 3.7 x 104 6.5 3000 300 268 11 2. PFA-350 5.0 x 104 11.0 4000 300 310 20 3. PTPE (10 MR) 2.3 x 104 - 0 0 338 65 4. PTFE (20 MR) 3.1 x 10 - 0 0 339 67 5. PTFE (30 MR) 1.4 x 10 - 0 0 333 67 6. 50% PTFE (10 MR) 50% FEP-160 3.6 x 104 6.2 1990 45 330 29 7.50% PTFE (20 MR) 50% FEP-160 2.6 x 104 6.2 2250 125 329 27 8. 50% PTFE (30 MR) 50% FEP-160 2.3 x 104 7.5 2098 225 329 27 9. 66% PTFE (30 MR) 34% FEP-160 8.7 x 10 5.9 1994 92 325 45 10. 40% PTFE (30 MR) 60% PFA-350 2.5 x 104 - 3100 370 322 30

Claims: CLAIMS: 1. A composition which can be melt-shaped and which comprises a mixture of (1) a first fluoropolymer which has a crystallinity of less than 45% and which can be melt-shaped in the absence of other polymers, and 2) a second crystalline fluoropolymer which has a crystallinity of at least 508. 2. A composition according to Claim 1 wherein the first fluoropolymer has a melt viscosity at 380 C of 5x103 to lxi 06 poise. 3. A composition according to Claim 2 wherein the first polymer has a melt viscosity at 380 C of 104 to i05 poise. 4. A. composition according to any of the preceding claims, wherein the second fluoropolymer has a melt viscosIty at 380C of less than 106 poise. 5. A composition according to claim 4, wherein the second fluoropolymer has a melt viscosity at 380 C of 5 less than 10 poise. 6. A composition according any of the preceding claims wherein the ratio by weight of the first fluoropolymer to the second fluoropolymer is within the range from 0.3:1 to 2.5:1. 7. A composition according to claim 6, wherein the said ratio is within the range from 0.3:1 to 0.7:1. 8. A composition according to any of the precedinq claims wherein the first fluoropolymer has a crystallinity of 5% to 30%. 9. A composition according to Claim 8 wherein the first fluoropolymer has a crystallinity of less than 208. 10. A composition according to any of the preceding claims, wherein the second fluoropolymer has a crystallinity of more than 60%. 11. A composition according to claim 10, wherein the second copolymer has a crystallinity of more than 65%. 12. A composition according to any of the preceding claims wherein the second fluoropolymer is a polymer obtained by irradiating a fluoropolymer whose melt viscosity at 380'C, prior to irradiation, was at least three times the melt viscosity at 380 C of the first fluoropolymer. 13. A composition according to any of the precedinq claims wherein the second fluoropoyrter is a polymer obtained by irradiating a fluoropcly:r-er which, prior to irradiation, could not be melt-extruded in the absence of other polymers. 14. A composition according to any of the precedinq claims wherein the second fluoropolymer is polytetrafluoroethylene which has been irradiated to a dosage of 2.5 to 40, preferably 5 to 30 Mrad. 15. A composition according to Claim 14 wherein the first fluoropolymer is a copolymer of tetrafluoroethylene and at least one other perfluorinated comonomer. 16. A composition according to Claim 14 wherein the first fluoropolymer is a copolymer of tetrafluoroethylene and hexafluoropropylene. 17. A composition according to Claim 14 wherein the first fluoropolymer is a copolymer of tetrafluoroethylene and a perfluorinated vinyl ether. 18. A shaped article which is composed of a meltshaped composition according to any of the preceding claims. 19. An article according to Claim 18 in the form of foamed insulation in a coaxial cable.

Inventors: LUNK, HANS EDMUND, REED, DONALD ALLEN
Applicants: RAYCHEM CORPORATION (A DELAWARE CORPORATION)
Application year: 1984
Main classification: C08L27
IPC codes: C08L1, C08L23, H01B3, C08L27, C08L57