METHOD FOR MANUFACTURING PRINTED MOLDINGS

Abstract: The present method for manufacturing a molded article containing printed information ahdered thereto is characterized by transferring said information from a release sheet to said article during the molding operation using an ink that is at least partially cured prior to being placed in the mold. The ink and article are bonded together during the molding process.

Description: METHOD FOR MANUFACTURING PRINTED MOLDINGS The present invention relates to a method for manufacturing printed molded articles. More particularly, this invention relates to a method during which printed information is bonded to an article as it is being molded. Methods for manufacturing printed molded articles during which characters, figures, symbols, pictures, or other information are printed during molding of a plastic article have been disclosed, for example, in Japanese Laid-Open Patent Application 57-59738 [ 82-59738 ] . Because molding and printing are executed simultaneously, these methods for manufacturing printed molded articles are characterized by a high rate of productivity; however,-the durability of adhesion and the legibility of the information printed on the molding surface of the article are inadequate. Japanese Laid-Open Patent Application 57-59738 [ 82-59738 ] discloses a method during which molding material is poured into a mold and cured after a film printed with a conventional ink has been placed in the mold. The drawback of this method is that the durability of adhesion of the transferred ink is not always good. When an uncured ink is printed on the film before the molding material is poured in and subsequently cured in order to solve this problem, the printed information fades or dims and becomes unclear. The goal of the present invention is to solve the foregoing problems by providing a method for manufacturing printed molded articles wherein the ink printed on the surface of the article has both a high durability of adhesion and high legibility. To achieve the foregoing goal, the method for manufacturing printed molded articles of the present invention is ckaracta -zed by transferring printed information from a release sheet to a molded article during the molding operation using an ink that is at least partially cured prior to being placed in the mold. During the molding operation the ink becomes bonded to the molded article. Figures 1, 2, 3, and 4 depict the stages of a continuous process for preparing printed, molded articles in accordance with the present method. The mold and final article are shown in cross section. Figure 5 is a top view of a printed release sheet bearing a mirror image of the information to be transferred during the present molding method. Figure 6 is a top view of the final molded article, in this case a key top, bearing the information transferred from the release sheet of Figure 5. This invention provides a method for manufacturing a molded article having information imprinted thereon, said method comprising the following sequence of steps: forming a mirror image of said information on a release sheet using a heat curable- or room temperature curable ink, at least partially curing said ink, placing said release sheet with the ink-bearing side up on the bottom of a metal mold cavity, filling the mold cavity with a pumpable curable material, concurrently curing said material and bonding it to said ink to form a printed molded article, removing said printed molded article from the mold and separating said release sheet from said article. As used herein, the term Rat least partially cured" refers to either a semi-cured state or a completely cured state. From the viewpoint of improving the durability of adhesion of the ink to the cured material, the ink is preferably only partially cured prior to placing the release sheet in the mold. The curable ink can be either of a room temperature-curable or heat-curable type. From the viewpoint of increased productivity, a heat-curable type is preferred. Polymers used in heat-curable inks include silicone elastomers, silicone resins, epoxy resins and amino resins. Preferred silicone inks cure by an addition reaction, a condensation reaction, or in the presence of organoperoxides. The curable material from which the molded article is formed can be either a room temperature-curable or heat-curable composition. Heat curable compositions are preferred. Examples of room temperature-curable materials are elastomers such as silicones, polysulfides and polyurethanes. Heat-curable materials include elastomers such as silicone rubber, natural rubber, butyl rubber, SBR, chloroprene, EPDM, acrylic rubber, polybutadiene rubber, polyurethane rubber and fluorinated rubbers. Heat curable materials also include resins such as silicone resins, epoxy resins, amino resins, phenolic resins, unsaturated polyester resins and polyurethane resins. Organoperoxide-curable or addition reaction-curable silicone materials are preferred. The release sheet must be capable of transferring the ink to the molded article. Preferred examples of such release sheets are plastic films, plastic-laminated papers, and plastic-laminated metal foils. Preferred plastic films are formed from polytetrafluoroethylene, polyesters, polypropylene, polyethylene, vinylidene chloride; or vinyl chloride copolymers. Preferred plastic-laminated papers are paper laminated with polyethylene, polypropylene or polyesters. Preferred plastic-laminated metal foils include polyethylene-laminated aluminum foil, polypropylene-laminated aluminum foil, and polyester-laminated aluminum foil. The metal mold is divided at least into upper and lower sections. Mold cavities are present in the lower section. Because the release sheet printed with the curable ink is placed on the bottom of the mold cavities, the metal mold is preferably constructed so as to facilitate placement of the release sheet. As will be discussed below, such a metal mold is preferably divided to give a lower section which contains mold cavities. The lower section can, in turn, be separated at the bottom of the mold cavities. By dividing the metal mold to provide access to the bottom of the mold cavities, the release sheet can be readily put in place and the entire molding operation can be easily automated. The curable ink can be printed onto the release sheet by any known method. Screen printing is particularly preferred. Before placing the release sheet at the bottom of the mold cavities, the curable ink printed on the release sheet must be at least partially cured. Preferably the ink is only partially cured at this stage. Curing of the ink is completed while it is in contact with the curable material in the mold cavity, and the curable material and curable ink become a single body. The cured ink is readily released from the release sheet and smoothly transferred to the molded articles. Because the ink is at least partially cured before being placed in the mold, the printed information is not altered when the pumpable curable material is placed in the mold cavities. Thus, a legible, strong printing is obtained without blurring. The preferred embodiments of the present method are described in the following practical examples with reference to the accompanying drawings. Figures 1 to 4 depict the steps in a continuous method for manufacturing printed moldings in accordance with the present invention. In the figures, metal mold 1 is divIded into three sections: la represents a single upper metal mold section while sections Ib and lc constitute the lower portion of the mold. Vertically oriented mold cavities 2 are present in lower metal mold section lb, which constitutes the central section of the mold. Release sheet 3, on which information has been printed using curable ink 4, is inserted between mold sections lb and lc. The side of the release sheet bearing curable ink 4 is positioned so as to face upwards when the release sheet is held between mold sections lb and lc. The curable ink 4 is applied to the release sheet'3 using a screen printer 5. A screen 5a containing the characters to be printed is present between the screen printer 5 and the release sheet 3. The liquid curable ink 4 is printed through this screen. A heater 6 partially cures the printed liquid curable ink 4. In the case of a calculator keyboard, a release sheet is imprinted with the mirror-image characters shown in Figure 5. The printed curable ink 4 is only partially cured prior to insertion of the release sheet between separated lower metal mold sections ib and lc of metal mold 1. During insertion of the sheet, the partially cured ink 4 is positioned so as to face the bottom openings of the mold cavities 2. Next, as shown in Figure 2, while the forward advance of release sheet 3 is stopped, lower mold sections Ib and lc are tightly closed to secure the release sheet. Liquid curable material 8 is then dispensed from supply pipes 7 into mold cavities 2. Differently colored curable materials may be provided to the several mold cavities. After the licuid curable material 8 has been dispensed into mold cavities 2, the upper metal mold section la is closed tightly against lower metal mold section Ib as shown in Figure 3, in order to assemble the whole metal mold into a single piece and perform the heat curing process. During the curing process, curable material 8 and curable ink 4 are simultaneously cured and adhered to one another to yield a unitary, printed molded article M, shown in Figure 4. Upon completion of the curing process, metal mold I is again separated as shown in Figure 4 and molded article M is removed from mold cavities 2. The release sheet is easily peeled from the cured ink that is now adhered to the molded article. Figure 6 shows molded article M, a printed key top, following removal from the metal mold. The cured ink 4 cannot be readily peeled from the article and the printed characters are distinct and unblurred. Besides the printed calculator key top shown in Figure 6, the present invention can also be applied to the simultaneous molding and printing of various items such as telephone pushbuttons, packings, O-rings, end caps, anode caps, connectors, spark plug boots, and rubber plugs. As described hereinbefore, the method for manufacturing printed molded articles of the present invention comprises the placing of a release sheet, printed with a curable ink which has been at least semi-cured, on the bottom of the mold cavities. When pumpable curable material is dispensed into the mold, the shape of the partially cured ink is not altered by the weight of the curable material. The ink and curable material are tightly solidified into a unitary article during the preferred simultaneous curing operation. Accordingly, the curable ink is strongly adhered fro the cured article and a legible, unblurred and nonviSming printing is made possible. .,;âlMplE 1 A black condensation reaction-curing silicone ink was printed on a polyester film release sheet. The sheet was heated at 2000C for 5 minutes to partially cure the silicone ink. The release sheet was placed between the two separated lower metal mold sections of a three-section metal mold for molding key tops as shown in Figure 1. A white two-component addition reaction curing silicone elastomer composition (viscosity = 700 Pa.s) was poured into the mold cavities and the entire metal mold was tightly closed. Curing was carried out for 40 seconds at 1500C. The printed and transferred characters on the key top moldings were distinct and legible. The durability of adhesion was considered excellent and no peeling was observed following repeated folding. Example 2 A white addition reaction-curing silicone ink was printed op a polyester film release sheet and the silicone ink was partially cured at 2000C for 5 minutes. The release sheet was then inserted between the two separated lower metal mold sections of a three-section metal mold for molding key tops. A light gray, single-component organoperoxide-curlng silicone elastomer composition (viscosity = 700 Pa.s) was poured into the mold cavities and the whole metal mold was closed tightly. Curing was carried out for 90 seconds at 16()0C. The printed and transferred characters on the key top moldings were distinct and legible. The durability of adhesion was considered excellent and no peeling was observed following repeated foldings. Example 3 A red epoxy resin ink was printed on a polypropylene-laminated paper release sheet. The ink was then partially cured at 1000C for io minutes. This release sheet was inserted between the two separated lower metal mold sections of a three-section metal mold for molding connectors. A black two-component polyurethane composition (viscosity = 5 Pa.s) was poured into the mold cavities and the whole mold was closed tightly. Curing was conducted at 1200C for 3 hours. The printed and transferred characters on the molded connectors were distinct and legible. The durability of adhesion was considered excellent and no peeling occurred under repeated folding and compression.

Claims: CLAIMS: 1. A method for manufacturing a molded article having information imprinted thereon, said method comprising the following sequence of steps: forming a mirror image of said information on a release sheet using a heat curable- or room temperature curable ink at least partially curing said ink placing said release sheet with the ink-bearing side up on the bottom of a metal mold cavity filling the mold cavity with a pumpable curable material; concurrently curing said material and bonding it to said ink to form a printed molded article; removing said printed molded article from the mold; and separating said release sheet from said article. 2. The method of claim 1 where said ink is only partially cured prior to placing said release sheet in said mold cavity and becomes completely cured during curing of said molded article. 3. The method of claim 1 where said ink and said curable material are heat curable. 4. The method of claim l where said ink is a silicone elastomer that is curable by means of an addition reaction, a condensation reaction or a reaction catalyzed by organoperoxides and said curable material is a silicone elastomer that is curable by means of an addition reaction or one catalyzed by organoperoxides. 5. The method of claim l where said ink is printed onto said release sheet by screen printing, the release sheet is placed between two sections of said mold, and the curable material is poured in from the top of the mold cavity. 6. The method of claim 1 where the release sheet is a plastic film, plastic-laminated paper or plastic-laminated metal foil. 7. The method of claim 1 where said mold is separable into an upper mold section, a central section containing said mold cavity and a lower section providing access to the bottom of said mold cavity to facilitate placement of said release sheet.

Inventors: HAMADA, MITSUO, SHIMIZU, KOJI, TAKAMI, MAKOTO
Applicants: TORAY SILICONE COMPANY LIMITED
Application year: 1984
Main classification: B29C39
IPC codes: B41M1, B32B33, B29C39, B29L9, B29C33, B29K101, B29C70, B32B38