Stable, free-flowing particulate adjuncts for use in detergent compositions

Abstract: A stable, free-flowing, particulate adjunct suitable for use in particulate detergent compositions consists essential­ ly of a liquid, viscous liquid, oily or waxy adjunct absorbed into a granular zeolite material of a particle size distribution of between 50 to 500 µm and having a bulk density of about 450 to 600 g/l. Suitable adjuncts are nonionic surfactants, silicones, waxes and hydrocarbons, fabric softening com­ pounds and perfumes. Use of said particulate free-flowing adjuncts in particu­ late detergent compositions is also disclosed.

Description: This invention relates to the use of stable, free-flowing particulate adjuncts in detergent compositions. Many components which provide special properties to detergent compositions are liquid, viscous liquid, oily or waxy materials under normal temperature conditions. As such can be named, for example, nonionic surfactants; silicones. waxes and hydrocarbons; fabric softening compounds such as the fatty primary, secondary or tertiary amines and cationic quaternary ammonium compounds; liquid enzyme slurries and perfumes. It is often difficult to incorporate such components satisfactorily into a particulate detergent composition. Such components, when incorporated, normally tend to give processing problems, tend to result in sticky powders with a tendency to caking during storage, and are liable to decompose or bleed from the powder. For many years nonionic surfactants which are waxy or viscous liquids at room temperature have been used in small amounts in so-called mixed active detergent formulations, primarily to reduce the amount of foam generated during the washing cycle. Recently, nonionic surfactants have been used in increasing amounts to provide for an improved fatty soil removal and an increase in the bulk density of the powder. It is however known that if a substantial amount of nonionic surfactant, e.g. above 5% by weight, is incorporated into the detergent slurry before spray-drying, a significant air-pollution problem, known as "blue smoke", is encountered. Silicone oils usable as foam depressant, when incorporated into the detergent slurry before spray-drying tend to decompose; the same happens to fatty amines, e.g. long-chain tertiary amines for fabric softening-in-the-wash, enzymes and perfumes. In the manufacture of particulate detergent compositions comprising such components these components are therefore preferably not incorporated in the detergent slurry before spray-drying, but are added to the spray-dried detergent base powder by spraying them in liquid or liquefied form by melting or in solvent-dissolution directly onto the spray-dried detergent base granules. A disadvantage of this method is that it cannot be used to incorporate adequate quantities of the component, especially nonionic surfactants and fatty amines, as required for the desired effect, without getting into problems with respect to free-flowingness, stickiness, caking and bleeding of the particulate detergent compositions. Another disadvantage is that it does not provide adequate protection against decomposition or interaction of certain components. Another known method is spraying the component in liquid or liquefied form by melting or in solvent-dissolution onto a carrier material, which is then mixed with the detergent base formulation. For this purpose various carrier materials have been proposed in the art, but the type of carrier material proposed is normally dependent upon the type of liquid component to be carried. Many of these carrier materials are unsuitable or have limited absorption capacity for certain liquid components. Specific carrier materials for nonionic surfactants are for example described in US Patent 3 769 222, including microsized silicon dioxide, sodium perborate monohydrate and clays, such as bentonite and zeolite. It has now been found that a type of zeolite material having particle size distribution of between 50 and 500 µm and a bulk density of 450-600 g/l can be used as an excellent general purpose carier material for almost any liquid, waxy or oily adjunct to form a stable, free-flowing particulate adjunct which can be suitably mixed with any particulate detergent composition without caking and stability problems. The present invention accordingly provides the use of a granular, spray-dried zeolite carrier material which comprises from 65 to 85 wt% of zeolite A and from 15 to 35 wt% of sodium sulphate and water, and has a particle size distribution of between 50 and 500 µm and a bulk density of 450 - 600 g/litre for absorbing a liquid, viscous-liquid, oily or waxy component which is incorporated in the granular zeolite carrier material by spraying thereon in liquid or liquefied form, so as to form a stable, free-flowing particulate adjunct for mixing with particulate detergent compositions, the adjunct consisting essentially of the liquid, viscous-liquid, oily or waxy component absorbed on the zeolite carrier material. The term "Zeolite" use herein refers to a crystalline aluminosilicate material generally having the formula: (Cat 2/n O) x .Al 2 O 3 .(SiO 2 ) y .z H 2 O, wherein Cat. is a cation having valency n that is exchangeable with Calcium (e.g. Na + or K + ); x is a number from 0.7-1.5; y is a number from 1.3-4; and z is such that the bound water content is from 10% to 28% by weight. A preferred Zeolite for use in preparing the granular carrier material is the commercially available product known as Zeolite A, which is typically: Na 2 O.Al 2 O 3 .2SiO 2 ∼4.5H 2 O and which can also be described by the unit cell content: Na 12 [(AlO 2 ) 12 .(SiO 2 ) 12 ].27H 2 O. The granular carrier material used in the invention, which is obtained by preparing an aqueous slurry of Zeolite A and sodium sulphate which is then subjected to a spray-drying process, comprises from 65 to 85% by weight of Zeolite A sodium sulphate and from 15 to 35% by weight of sodium sulphate and water. It has a high absorption capacity, much higher than any finely divided zeolite type normally used as partial or complete substitute of phosphates in detergent compositions, such that it can readily absorb up to about 100% of its weight of almost any type of liquid, waxy or oily components, such as nonionic surfactants, silicones, waxes and hydrocarbons, long-chain fatty amines, to a sufficient extent, without the risk of the liquid component bleeding. The granular zeolite material used in the present invention will preferably comprise from 65 to 85% by weight of Zeolite A, from 5 to 15% by weight of sodium sulphate and from 10 to 20% by weight of water. Preferably the granular zeolite material will have an average particle size of about 150-200 µm. The particles containing such liquid component remain rigid and free-flowing, feel dry and yet show good disintegration properties on contact with water, liberating both the liquid component and the zeolite serving as a builder. Although the invention will have general applicability to transform liquid components into particulate material, it is particularly suitable for obtaining free-flowing particulate nonionic adjuncts, fabric softening adjuncts and foam-controlling adjuncts. By using the invention it is also possible to prepare high bulk density high nonionic detergent compositions, wherein all the nonionic surfactants do not form part of the detergent slurry composition before spray-drying. The invention has an additional advantage in that, in view of the zeolite applied, less phosphate builder can be used and so limitations that have been placed gradually on the use of polyphosphate builder salts, such as sodium triphosphate, due to alleged detrimental ecological effects thereof, can be effected. Examples 1-7 The following free-flowing particulate adjuncts were prepared by spraying the liquid or liquefied components on to granular zeolite material (Zeolite HAB A40 compound ex Degussa) in a pan-granulator: (1) 65% Zeolite HAB A40 compound 31% primary fatty amine (Noram® SH ex CECA) 3.5% Synperonic® A7 nonionic surfactant ex ICI 0.5% fine silica. (2) 70% Zeolite HAB A40 compound 30% Alcalase® enzyme slurry (1850 GU/mg) (3) 70% Zeolite HAB A40 compound 25% Alcalase® enzyme slurry 5% glycerol/borax/sulphite mixture (4) 80% Zeolite HAB A40 compound 20% silicone oil DB 100 ex Dow Corning (5) 65% Zeolite HAB A40 compound 28% liquid enzyme slurry 1.25% sodium pentaborate 5.75% water. (6) 65% Zeolite HAB A40 compound 35% Synperonic® A7 nonionic surfactant (7) 65% Zeolite HAB A40 compound 35% perfume oil For comparison, granules were prepared by spraying molten Synperonic® A7 (C 13 -C 15 alcohol-7 ethylene oxide) nonionic on to molecular sieve Zeolite A (3-4 µm). The granules obtained therefrom and containing only 25% of nonionic were rather sticky and tended to agglomerate. It was only after weathering by blowing with dry air that a very fine particulate material was obtained. In contrast with the particulate material of Example (6) of the invention containing 35% of the same nonionic compound which is free-flowing, feels hard and non-fatty, the material in which finely divided Zeolite A is used as carrier is fragile and feels soft and fatty. Example 8 A high bulk density nonionic-based heavy duty detergent formulation was prepared by dry-mixing the following components: The powder remained stable and free-flowing with no sign of nonionic bleeding on the pack during storage. Example 9 Adjunct granules were prepared by spraying molten primary amine onto Zeolite HAB A40 compound to obtain a free-flowing granulated softening adjunct material containing 70% HAB A40 compound + 30% primary fatty amine. These granules were incorporated in a conventional particules detergent composition in an amount of about 10% by weight. The composition remained stable and free-flowing during storage and gave satisfactory cleaning and softening washed therewith.

Claims: Use of a granular, spray-dried zeolite carrier material which comprises from 65 to 85 wt% of zeolite A and from 15 to 35 wt% of sodium sulphate and water, and has a particle size distribution of between 50 and 500 µm and a bulk density of 450 - 600 g/litre for absorbing a liquid, viscous-liquid, oily or waxy component which is incorporated in the granular zeolite carrier material by spraying thereon in liquid or liquefied form, so as to form a stable, free-flowing particulate adjunct for mixing with particulate detergent compositions, the adjunct consisting essentially of the liquid, viscous-liquid, oily or waxy cdmponent absorbed on the zeolite carrier material. Use as claimed in claim 1, characterised in that the granular zeolite carrier material comprises from 65 to 85 wt% of zeolite A, from 5 to 15 wt% of sodium sulphate, and from 10 to 20 wt% of water. Use as claimed in claim 1 or claim 2, characterised in that the liquid, viscous-liquid, oily or waxy component is a nonionic surfactant, a silicone, wax or hydrocarbon, a fabric softening compound, an enzyme or a perfume. Use as claimed in any one of claims 1 to 3, characterised in that the granular zeolite carrier material has an average particle size within the range of from 150 to 200 µm.

Inventors: HO TAN TAI DR, HO, TAN TAI, DR.
Applicants: UNILEVER NV, UNILEVER PLC, UNILEVER N.V.
Application year: 1984
Main classification: C11D3
IPC codes: C11D17, C11D3