ULTRAVIOLET ABSORBING POLYMERS COMPRISING 2-HYDROXY-5-ACRYLYLOXALKYLPHENYL-2H-BENZOTRIAZOLES

Abstract: Ultraviolet light absorbing polymer compositions com­ prising copolymers of 2-Hydroxy-5-acrylyloxyphenyl -2H-­ benzotriazoles with one or more other monomers copolymerizable therewith, particularly acrylic monomers are useful in the manufacture of occular devices, particularly intraoccular lenses and contact lenses. The benzotriazole monomers are prepared from the corresponding intermedi­ ate phenyl alcohols 2′-Hydroxy -5′- acrylyloxyphenyl -2H-­ benzotriazoles.

Description: ULTRAVIOLET ABSORBING POLYMERS COMPRISING 2-HYDROXY-5 ACRYLYLOXYALKYLPHENYL-2H-BENZOTRIAZOLES BACKGROUND OF THE INVENTION This invention relates to ultraviolet light absorbing polymer compositions, and more particularly, to polymer compositions comprising copolymers of 2-Hydroxy-5- acrylyloxyalkylphenyl-21i-benzotriazoles with one or more other monomers copolymerizable therewith, particularly acrylic monomers. This invention further relates to ocular devices, particulary intraoccular lenses and contact lenses, prepared from such ultraviolet light absorbing polymers. The absorption of radiation in the ultraviolet range by polymeric materials is a major cause of the light-induced degradation therein. It is standard practice to add a low molecular weight UV "stabilizer to light-sensitive polymers to absorb the light in the destructive range o; to quench the energy generated as a result of the excitation of the light-absorbing functional groups in the polymer. Although low molecular weight W absorbers or quenchers of various types are effective in inhibiting or retarding the destruction of the polymers to which they are added, their extractibility in various media and/or their volatility during the processing or fabrication of the polymers at elevated temperatures, provide a limitation on their utility. This problem has been remedied to a considerable extent by the synthesis of copolymerizable monomers containing structural moieties capable of functioning as W absorbers or quenchers. The copolymerization of such monomers results in the formation of copolymers with increased stability, i.e. resistance to degradation upon exposure to UV light with decreased extractibility and volatility. The addition of such copolymers to a suitable matrix polymer imparts these properties to the latter. Examples of monomeric ultraviolet absorbers copolymerizable with acrylic monomers as disclosed in U.S. 4,304,895 for use in the preparation of W absorbing hard contact lenses are EMI2.1 2-hydroxit-4-methacryloxy benzophenone and mixtures thereof. Similarly, the copolymerization of an allyl-2-hydroxybenzophenone with an acrylate ester such as methyl methacrylate is described in U.S. 4,310,650, and, the copolynerization of ethylenically unsaturated derivatives of 2,4-dihydroxybenzophenone with other vinyl type comonomers is broadly disclosed in U.S. 3,162,676. W absorbing lenses are particularly desirable for use by persons who have had their natural lenses surgically removed due to cataracts or some damage or natural deterioration of the lens. The visual correction of aphakia resulting from such lens removal requires the use of high plus corrective lens which may be in the form of spectacles, contact lens or intraocular lens. A portion of incident light entering the eye is normally absorbed by various parts of the eye so that only the unabsorbed or transmitted portion strikes the retina. The incident light is, of course, comprised of the entire spectrum of wavelengths including the ultraviolet, visible and infrared. The cornea preferentially absorbs that portion of the light with wavelengths up to about 300 nm. The crystalline lens preferentially absorbs the wavelengths from about 300 up to about 400 nm. There is also a characteristic absorption of the visible portion of the spectrum by other parts of the eye. The overall result of the various absorptions in the hun an eye is to permit the unabsorbed light to be transmitted to the retina, this light being defined by wavelength and intensity at each wavelength. It is apparent that in the aphakic eye, where there is no crystalline lens, light from 300 to 400 nm will be transmitted to the retina and that absorption in the visible range of the spectrum will also be changed to the extent that such visible light would have been absorbed by the. crystalline lens. Accordingly, the entire spectrum of the light striking the retina in the aphakic eye is different from that in the normal eye. Intraocular lenses and hard contact lenses are presently produced from polymethylmethacrylate polymers which exhibit a combination of properties desirable for such products, particularly optical clarity, the capability of being cut and polished or molded to specific optical powers, and chemical inertness. W absorbing lenses of PMMA are required to maintain these properties while achieving at least 85% absorption of light at 400 nm based on a polymer film thickness of 1 mm. In addition, the absorption must cut off sharply above 400 ma to avoid yellowing of the lens. While the hydroxy benzophenones copolymerizable with acrylate monomers are effective W absorbers and form chemically stable copolymers, relatively large amounts, i.e. 3 to 10% by weight, must be incorporated in the polymer to obtain 858 UV absorption at 400 rira and 1 mm thickness, and the compounds exhibit very broad absorption bands which eXtend into the visible range. Thus, polymers containing sufficient amounts of the benzophenone to provide effective W absorption often have a significantly yellow cast. It is accordingly an object of the present invention to provide a copolymer composition with improved W absorption characteristics. It is a further object to provide a new W absorbing composition which is copolymerizable with vinyl monomers. A yet further object is to provide a new composition of matter which when copolymerized with acrylic-type monomers is effective to absorb at least 85% of incident W light at 400 nm and 1 mm thickness. It is a further object torArovide a new colaposition of matter which effectively absorbs W light in the range of 300 to 400 nm but cuts off sharply above 400 nm. These and other objects of the present invention will be apparent from the ensuing description and claims. Summary of the Invention There is provided as a new composition of matter 2-Hydroxy -5-acrylyloxyalkylphenyl-2H-benzotriazoles of the structure EMI5.1 wherein X is H or halogen, each R1 is selected from the group consisting of H, CH3, t-alkyl of 4 to 6 carbons and EMI5.2 wherein R2 is C2-C10 alkylene which may be straight chain or branched, and R3 is H or CH39 provided that one R1 is H, C}i31 or t-alkyl and the other R1. l is EMI5.3 The above defined benzotriazoles are copolymerizable with vinyl monolners such as methyl methacrylate to yield optically clear polymers useful in the preparation of intraocular and contact lenses. From 0.05 to about 20% by weight of the benzotriazole compound may be incorporated in the copolymer, the minimum effective amount for 85% absorption at 400 nm and 1 mm film thic?,cness depending upon the particular structure of the benzotriazole compound. High molecular weight homopolymers of the benzotriazole monomers may also be prepared and incorporated into a variety of organic materials to impart W absorption properties thereto. The above defined benzotriazole monomers are prepared from 2'-hydroxy-5'-(hydroxyalkyl)phenyl-2H-benzotriazoles of the structure EMI6.1 wherein X is H, halogen or -0CH3; R1 is selected from the group consisting of H, CH31 and n-, sec- and tert-alkyl of 4 to 6 carbons; and R2 is a Cn alkylene which may be straight chain or branched wherein n is from 2 to 10. Detailed Description The benzotriazole monomers of the present invention are those compositions defined by the structure EMI6.2 wherein X is H or halogen, each R1 is selected from the group consisting of H, CH3, t-alkyl of 4 to 6 carbons and EMI6.3 wherein R2 is C2-C10 alkylene which may be straight chain or branched, and R3 is H or C3, provided that one R1 is H, CH3, or t-alkyl and the other R1 is EMI7.1 Particularly preferred compounds are those where X is H or chlorine, R1 is H or t-butyl, R2 is ethylene or propylene and R3 is methyl. Specific preferred compounds encompassed by the above formula inclu EMI7.2 2-(2'-Hydroxy-5'-methacrylyloxyethylphen benzotriazole EMI7.3 2-(2'-Hydroxy-5'-methacrylyloxyethylphenyl)-5-chloro-2Hbenzotriazole EMI7.4 2-(2'-Hydroxy-5'-methacrylyloxypropylphenyl)-2H benzotriazole EMI8.1 2-(2'-Hydroxy-5'-metllacrylyloxypropylphenyl)-5-chloro-2H- benzotriazole EMI8.2 2-(2'-Hydroxy-5'-methacrylyloxypropyl-3'-tertbutylphenyl)-5-chloro-2H-benzotriazole EMI8.3 2-[3'-(1",1"-dimethyl-3"-methacrylyloxypropyl)-2'-hydroxy5'-methylphenyl]-5-chloro-2H-benzotriazole A particularly preferred benzotriazole W absorbing monomer of the present invention is compound V above. This compound is copolymerizable with methyl methacrylate and other vinyl type monomers and imparts excellent W absorbing properties to the copolymer even at concentrations of 1.08 or less. The preparation of this compound, its copolymerization with methyl methacrylate, and the UV transmission characteristics of the resulting polymer, are described in the following examples. EXAMPLE 1 Preparation of Intermediate 3-(3',5'-Di-tert-butyl-4'-hydroxyphenyl)-l-propanol A solution of methyl 3-(31,5'-di-tert-butyl-4'-hydroxy- phenyl) propionate (117 g, 0.4 mol) in 200 ml of anhydrous ether was. added dropwise to a mixture of lithium aluminun hydride (17 g, 0.45 mol) and anhydrous ether (800 ml) under an inert atmosphere with ice-water cooling. After the addition was completed, the reaction mixture was heated at reflux temperature for one hour, then cooled to room temperature. To the cooled mixture was added dropwise 80 ml of 3% sodium hydroxide aqueous solution with vigorous stirring and with ice-water cooling. After the addition was completed, the mixture was stirred at room temperature for 30 minutes. A white precipitate was separated by filtration and washed with ether. The filtrate and washings were combined and evaporated. The residue was vacuum distilled to give 101 g (95%) of the product. EXAMPLE 2 Preparation of Intermediate 3-(3'-tert-Butyl-4'-hydroxypheIyl)-f-pr 3-(3',5'-Di-tert-butyl-4'-hydroxyphenyl)-1-propanol (100 g, 0.38 mol) was dissolved in 500 ml of trifluoracetic acid. The solution was stirred at 40'C for six hours, then poured into an ice-water mixture. The mixture was extracted with methylene chloride. The methylene chloride layer was washed with aqueous sodium carbonate and evaporated. A solution of sodium hydroxide (25 g) in 400 ml of methanol was added to the residue. The mixture was stirred at room temperature for 30 minutes, neutralized with 1N hydrochloric acid and extracted with methylene chloride. The methylene chloride layer was washed with aqueous sodium carbonate and water, dried with anhydrous potassium carbonate, and evaporated. The residue was vacuum distilled to give SI g (64%) of the product. EXAMPLE 3 Preparation of Intermediate 2-tert-Butyl-4-hydroxypropyl-6-(4'-chloro-2'-nitro phenylazo) phenol 4-Chloro-2-nitroaniline (72 g, 0.42 mol) was diazotized in the usual manner such as described in the literature (H. E. Fierz-David and L. Blangley, "Fundamental Processes of Dye Chemistry" p. 247 (Interscience, New York 1949)). The diazonium salt solution was added dropwise to a stirred mixture of 3-(3'-tert-butyl-4'-hydroxyphenyl)-1- propanol (88.5 g, 0.42 mol), concentrated hydrochloric acid (108 g), water (920 ml) and sodium lauryl sulfate (10 g) at 40"C. The mixture was stirred at 400C for sixteen hours, then allowed to stand. After the azo dye settled, the supernatant liquid was decanted. The azo dye was washed with warm water1 and the washings decanted. The azo dye was used for the next reaction without further purification. EXAMPLE 4 Preparation of Intenaediate 2-(2'-Hydroxy-5'-hydroxypropyl-3'-tert-butylphenyl)-5 chioro- 2H-benzotriazole The azo dye of Example 3 was dissolved in 1.7 1 of ethanol. A solution of 151 g of glucose in 1.7 1 of 2N sodium hydroxide was added to the azo dye solution. The mixture was stirred at room telaperature and, after 24 hours of stirring, 131 g of zinc dust was added to the reaction mixture. The mixture was stirred for another two hours at room temperature. The zinc was separated by filtration and washed with ethanol, methylene chloride and ethanol. The filtrate and washings were combined and acidified with concentrated hydrochloric acid. The aqueous layer was extracted with methylene chloride. The combined organic layer was washed with 1N hydrochloric acid and water, dried with potassium carbonate and evaporated. The residue was vacuum distilled to give 107 g (61%) of the benzotriazole. The distillate was further purified-by column chromatography and recrystallization. A pure sample showed a m.p. of 110-1110C and X max peaks at 311 and 350 ma (#311=1.44 x 104, c35o=1o58 x 104 1 mol-1 cm-1). EXAMPLE 5 Preparation of 2-(2'-Hydroxy-5'-methyacrylyloxypropyl-3' tert-butylphenyl)-5-chloro-2H-benzotriazole Methacrylyl chloride (5.9 ml) and triethylamine (8.5 ml) were added dropwise at -50C to a solution of 2-(2' hydroxy-5' -hydroxypropyl-3' tert-butylphenyl)-5-chloro-2H- benzotriazole (20 g) in 250 ml of methylene chloride. The reaction mixture was stirred at oeC overnight and then washed with 1N hydrochloric acid and water. The methylene chloride solution of the product was dried with sodium sulfate, passed through alumina column and evaporated. The crude yield of the product was 22 g (908). A polymer ization grade sample was obtained by recrystallization from methanol - methylene chloride mixture, m.p. 74.5 76.5"C. Other 2-(2'-hydroxy-5'-methacrylyloxyalkyl-3'-tert-butyl phenyl)-5-chloro-2EI-benzotriazoles are readily prepared using a similar procedure and substituting the appropriate benzotriazole alkanol for the intermediate of Example 1. Such compounds wherein the alkanol is C3 to C8 are described, for example, in U.S. Patent No. 4,260,832. EXAMPLE 6 Polymerization 0.1 g of the benotriazole product of Example 5, 2.0 g of ethyl acrylate, 22.9 g of methyl methacrylate, 89 1 of 1dodecanethiol, 0.12 g of stearic acid and 2O.3 mg of azobisisobutyronitrile were placed in a Pyrex tube. The tube was flushed with argon and then sealed. The mixture was polymerized at 70"C for six hours. The resulting polymer containing 0.4% of the benzotriazole was hot pressed into 1 mm thick film. GPC showed that the W absorbing group was chemically bonded in the polymer xnatrix. The film showed transmittance of 17.2% at 400 nm and 0% at 388 nm. EXAMPLE 7 Polymerization The procedure of Example 6 was followed using 0.2 g of the benzotriazole product of Example 5, 1.9 g of ethyl acrylate, 23.0 g of methyl methacrylate, 89 ill of 1dodecanethiol, 0.12 g of stearic acid and 20.3 mg of azobisisobutyronitrile. A 1 mm thick film prepared of the resulting polymer which contained 0.88 of the benzotriazole shoved transmittance of 3.48 at 400 run and 0% at 395 nm. A UV transmittance curve for the Copolymer of this example is plotted in Figure 1 in comparison with a copolymer of methylmethacrylate containing 10 percent 4-(2'-Acrylyloxyethoxy)-2-hydroxybenzophenone (Copolymer A), a copolymerizable UV absorbing monomer of the prior art. The transmittance curve for a commercial acrylic resin not containing any Fuzz absorber is also included for reference. The following examples describe the preparation of other benzotriazole W absorbing compounds within the scope of the present invention. EXAMPLE 8 2-(2'-Hydroxy-5'- methacrylyloxyethylphenyl)-2H-benzotriazole The synthesis of the above compound involved the preparation and esterification of 2-(2'-hydroxy-5'-hydroxyethylphenyl)-2H-benzotriazole as illustrated by the following reaction scheme. Preparation of 2- (2' -Hydroxy-5'-hydroxyethylphenyl ) -2H-benzotriazole A 2000 ml, three-necked flask was equipped with mechanical stirring, an addition funnel and a thermometer. Concentrated hydrochloric acid (150 ml, 1.8 mole) was placed in the reaction vessel and solid o-nitroaniline (55.2 g, 0.4 mole) was added with stirring. The slurry was cooled in an ice bath and a solution of sodium nitrite (27 g, 0.39 mole) in water added dropwise while maintaining the internal temperature in the range of 0-5"C by external cooling. The solution was filtered to remove a small anount of solid particles. A solution of ±-hydroxyphenethyl alcohol (55.2 g, 0.4 mole), sodium hydroxide (16 g, 0.4 mole), and sodium carbonate (120 g, 1.13 mole) in 600 ml of water was prepared and added dropwise to the reaction vessel with stirring over a period of 30 minutes while maintaining the internal temperature at 15f30C. The intermediate azo compound separated as a dark red oil which partially solidified after two hours. It was collected by filtration in a sintered glass funnel and dissolved in 400 ml of 2N sodium hydroxide solution. Zinc dust (120 g, 1.84 mole) was added to the solution in portions over a period of three hours while at the same time 200 ml of 25% sodium hydroxide solution was added dropwise. After completion of the addition, the suspension slowly changed from red to green in a mildly exothermic reaction. The mixture was heated at 700C for one hour to complete the reaction, cooled to room temperature and filtered to remove zinc salts. The dark, brown filtrate was acidified with concentrated hydrochloric acid solution and the solid product was collected by suction filtration and dried in air. The crude solid was distilled on the Kugelrohr (2200 C, 0.1 mm) giving a yellow oil which solidified in the receiver. Crystallization twice from acetone gave the product as a nearly colorless solid (32.64 g, mp 126 127"C). 2-(2'-Hydroxy-5'-hydroxyethylphenyl)-2EI-benzOtriazole (150 g, 0.59 mol), methacrylic acid (55 ml, 0.65 mol), hydroquinone (2.4 g), p-toluenesulfonic acid monohydrate (3 g) and toluene (2 1) were placed in a 3 liter flask equipped with a Dean and Stark receiver. After 1.5 hours of refluxing the mixture, another 2.7 g of p-toluenesolfonic acid monohydrate was added and the refluxing was continued for another 15.5 hours. Approximately 10 ml of water was collected (theoretical: 10.6 g) and the yield of the desired compound was 93.7% as judged by a gas chromatography. Another 1 g of p-toluenesolfonic acid monohydrate was added and the reflusing was continued for another 3 hours. A yield of 95.6% was shown by a gas chromatography. After cooling the reaction mixture, it was washed with aqueous sodium hydrogen carbonate solution, water, 5% hydrochloric acid and water. The organic layer was dried with anhydrons magnesium sulfate and chromatographed through an alumina (Fisher, 80-200 mesh) column. After evaporation of the solvent, the residue was recrystallized from distilled methanol twice. Yield: 141.8 g (748); Purity: > 99.9% (G.C.). The IR and NMR data were consistent with the structure. EXAMPLE 9 2-(2'-Hydroxy-5'-methacrylyloxyproPylphenyl)-2H- benzotriazole The above compound was synthesized using a procedure analogous to that of Example 8, with 2-(21-Hydroxy-5'- hydroxypropylphenyl)-2El-benzotriazole as the starting reactant. Comparable yields of purified monomer were obtained without difficulty. The benzotriazole phenyl alcohols which are particularly useful as intermediates in the preparation of the preferred 2'-hydroxy-5'-acrylyloxyalkylphenyl-2Hbenzotriazoles as follows: a. 2-(2' -Hydroxy-5 '-hydroxyethylphenyl)-2H-benzotriazole EMI16.1 as an intermediate in the preparation of 2-(2' Hydroxy-5'-methacrylyloxyethylphenyl)-2H-benzotriazole (I); b. 2-(2'-Hydroxy-5'-hydroxyethylpyhenyl)-5-chloro-2Hbenzotriazole EMI16.2 as an intermediate in the preparation of 2-(2' Hydroxy-5'-methacrylyloxyethylphenyl)-5-chl benzotriazole (II); c. z-92'-Hydroxy-5'-hydroxypropylphenyl)-2H benzotrlazosc EMI16.3 as an intermediate in the preparation of 2-(2' Hydroxy-5'-methacrylyloxypropylphenyl)-2Hbenzotriazole (III); d. 2-(2'-Hydroxy-5'-hydroxypropylphenyl)-5-chloro-2Hbenzotriazole EMI17.1 as an intermediate in the preparation of 2-(2' Hydroxy-5' -methacrylyloxypropylphenyl)-5-chloro-2H- benzotriazole (IV); and e. 2-(2'-Hydroxyfl hydroxypropyl-3'-tert-butylphenyl)-5- chloro-2H-benzotriazole EMI17.2 as an intermediate in the preparation of 2-(2'-Hydroxy-5'- methacrylyloxypropyl-3'-tert-butyiphenyl)-5-chloro-2H- benzotriazole (V) The monoiaers of Example 8 and Example 9 were readily copolymerized with methylmethacrylate and ethylacrylate and hot pressed into films as described above. While both monomers were effective W absorbers, significantly higher concentrations were required to achieve 85% absorption at 400 nm on 1 mm thick films as compared to the preferred monomer of Example 5. Comparative data is as follows: Wt. % in Copolymer in 1 mm Film to UV Absorber Achieve 85% Absorption at 400 nm Example 5 < 1.0 Example 8 14-16 Example 9 10 Monomer A(1) 8 (1) Monomer A = 4-(2'-Acrylyloxyethoxy)-2 hydroxybenzophenone Extinction coefficients of the benzotriazole monomers of Examples 5, 8, and 9 and of Monomer A were measured in methylene chloride solution. The extinction coefficient E is a measure of the molar absorptivity of a compound according to the following equation: A cb wherein A = absorbance; c = concentration of the solute (mol/liter); and b = path length of radiation within the sample (cm). Absorbance is determined according to conventional procedures using a UV-Visible Spectrophotometer as described, for exax.le, in R. M. Silverstein and G. C. Bassler, "Spectrometric Identification of Organic Compounds", 2nd Edition, John Wiley & Sons, Inc., New York, 1967. Since E is proportional to absorbance, a compound which has a larger E gives greater UV absorption at lower concentrations. The benzotriazoles of the present invention absorb strongly in the W range of 200-400 nm and to cut off sharply above 400 nm. The hydroxy benzophenone control (Monomer A) absorbs less strongly and exhibits a broader absorption band extending into the visible range. Extinction coefficient curves for the above monomers are plotted in Fig. 2, and the data are summarized in the following table: ULTRAVIOLET EXTINCTION COEFFICIENTS Xmaxl Xmax2 t(l mol-1 cm¯l) ABSORBER rim nm #max1 Imax2 400 nm Example 5 311 348 14,675 16,286 755 Example 8 298 336 13,496 17,181 7 Example 9 299 337 13,555 16,326 22 Monomer A 285 323 15,783 10,175 25 Other 2-(2'-hydroxy-5'-methacrylyloxyalkylphenyl)-2Hbenzotriazoles are readily prepared following the procedure of Example 8 using the appropriate 2-(2'hydroxy-5'-hydroxyalkylphenyl)-2H-benzotriazole as the starting reactant. Alkyl groups containing from 2 to 8 carbon atoms are preferred for these compounds. EXAMPLE 10 The monomer of Example 8 ( > 99.9% pure) was homopolymerized in tolulene at 50 C for 63 hours to obtain essentially 100% conversion to a high molecular weight polymer having an inherent viscosity of 1.87 dl/g measured as O.5% by weight solution in chloroform at 250C, Tg 116 C The homopolymer was useful as an additive for incorporation in polymer films to enhance W absorption properties. EXAMPLE 11 The monomer of Example 8 was copolymerized with methyl methacrylate, and with selected third monomers following the general procedure of Example 6 to obtain various copolymers and terpolymers useful in the manufacture of intraoccular lenses. Preferred polymers were selected on the basis of Tg and melt index values amiable to injection molding, and on the basis of good optical clarity. Terpolymers of MMA with 168 of the monomer of Example 8 and either 68 stearyl methacrylate or 10% ethyl acrylate gave particularly good optical clarity with no significant yellowing effect. The benzotriazole monomer of Example 8 is accordingly a preferred W absorber for applications where yellowing of the base polymer is to be avoided. The terpolymer films had transmittance values of 10-148 at 400 nm and 88-908 at 700 nm. Inherent viscosity of the terpolymer ranged in values from about 0.35 to 0.80, and Tg was in the order of 110-115"C. Comparable copolymers of MMA with 16% of the benzotriazole monomer of Example 9 and terpolymers with 10% ethyl acrylate were prepared and pressed into films. Transmittance values for those films was 4-58 at 400 nm and 85 - 88% at 700 nm, indicating that the monomer of Example 9 is a more effective W absorber than the monomer of Example 8. The benzotriazoles of the present invention may be copolymerized with any of a number of unsaturated monomers to provide polymeric compositions having desirable W absorbing characteristics. Alternatively, homopolymers or copolymers of the benzotriazoles of the present invention may be utilized as additives to a wide variety of organic polymers to provide W absorption properties. Representative of the polymers and copolymers useful in conjunction with the benzotriazole monomers and polymers of the present invention are: a. Polymers which are derived from mono- or diolefins, e.g., polyethylene which can optionally be crosslinked, polypropylene, polyisobutylene, polymethylbutene-l, polymethylpentene-l, polyisoprene, polybutadiene. b. Mixtures of the homopolymers cited under (1), for example mixtures of polypropylene and polyethylene, polypropylene and polybutene-l, polypropylene and polyisobutylene. c. Copolymers of the monomers based on the homopolymers cited under (1), for example ethylene/propylene copolymers, propylene/butene-l copolymers, propylene/ isobutylene copolymers, ethylene/butene-l copolymers as well as terpolymers of ethylene and propylene with a diene, for example hexadiene, dicyclopentadiene or ethylidene norbornene, and copolymers of a-olefins, e.g., ethylene with acrylic or methacrylic acid. d. Polystyrene. e. Copolymers of styrene and of -methyistyrene, for example styrene/butadiene copolymers, styrenes acrylonitrile copolymers, styrene/acrylonitrile/ methacrylate copolymers, styrene/acrylonitrile copolymers modified with acrylic ester polymers to provide impact strength as well as block copolymers, e.g., styrene/butadiene/styrene block copolymers. f. Graft copolymers of styrene, for example the graft polymer of styrene to polybutadiene, the graft polymer of styrene with acrylonitrile to polybutadiene as well as mixtures thereof with the copolymers cited under (5), commonly referred to as acrylonitrile/butadiene/styrene or ABS plastics. g. Halogen-containing vinyl polymers, for example poly vinyl chloride, polyvinylidene chloride, polyvinyl fluoride, polychloroprene, chlorinated rubbers, vinyl chloride/vinylidene chloride copolymers, vinyl chloride/ vinyl acetate copolymers, vinylidene chloride/vinyl acetate copolymers. h. Polymers which are derived from ,ss-unsaturated acids and derivatives thereof, polyacrylates and polymethacry lates, polyacrylic amides and polyacrylonitrile. The instant compounds are advantageously used in heat-curable - acrylic resin lacquers which are coraposed of a copolymer of acrylic acid and one or more of its derivatives, and a melamine-formaldehyde resin. i. Polymers which are derived from unsaturated alcohols and amines and from the acyl derivatives thereof or acetals, for example polyvinyl alcohol, polyvinyl acetate, polyvinyl stearate, polyvinyl benzoate, polyvinyl maleate, polyvinyl butyral, polyallyl phthalate, polyallyl melamine and copolymers thereof with other vinyl compounds, for example ethylene/vinyl acetate copolymers. j. Honopolymers and copolymers which are derived from epoxides, for example polyethylene oxide or the polymers which are derived from bis-glycidyl ethers. k. Polyacetals, for example polyoxymethylene, as well as polyoxymethylenes which contain ethylene oxide as comonomer. 1. Polyalkylene oxides, for example polyoxyethylene, polypropylene oxide or polybutylene oxide. ra. Polyphenylene oxides. n. Polyurethanes and polyureas, such as in urethane coatings. O. Polycarbonates. p. Polysulfones. q. Polyamides and copolyamides which are derived from diamines and dicarboxylic acids and/or from alinocarboxy- lic acids or the corresponding lactams, for example polyamide 6, polyanide 6/6, polyamide 6/10, polyamide 11, polyamide 12, poly-m-phenylene-isophthalamide. r. Polyesters which are derived from dicarboxylic acids and dialcodols and/or from hydroxycarboxylic acids or the corresponding lactones, for example polyethylene glycol terephthalate, poly-1,4-dimethylolcyclohexane terephthalate. 5. Cross-linked polymers which are derived from aldehydes on the one hand and from phenols, ureas and melamine-on the other, for example phenol/formaldehyde, urea/ formaldehyde and melamine/formaldehyde resins. t. Alkyd resins, for example glycerol/phthalic acid resins and mixtures thereof with melamine/forraaldehyde resins. u. Unsaturated polyesters resins which are derived from copolyesters of saturated and unsaturated dicarboxylic acids with polyhydric alcohols as well as from vinyl compounds as cross-linking agents and also the halogencontaining, flame-resistant modifications thereof. v. Natural polymers, for example cellulose, rubber, as well as the chemically modified homologous derivatives thereof, for example cellulose acetates, cellulose propionates and cellulose butyrates and the cellulose ethers, for example methyl cellulose. Particularly useful compositions are copolymers comprising from 0.1 to 20% by weight of benzotriazoles of the present invention with other ethylenically unsaturated materials such as styrene, methyistyrene, acrylates, methacrylates, acrylamide, acrylonitrile, methacrylonitrile, vinylacetate, vinylidene chloride, vinyl chloride, vinyl fluoride, ethylene, propylene, and mixtures thereof. ze homopolymers and copolymers of the benzotriazoles of the present invention find wide application in formulating UV absorbing plastics and other organic materials wherever such materials are exposed to W radiation from either natural or artificial sources. In addition to the medical use in intraoccular and contact lenses described above, the materials of the present invention are useful in many industrial applications such as in solar energy collectors, polymeric coatings, transparent plastic films, fluorescent light diffusers, packaging r.eterials, vinyl window coverings, automobile paints and interior coverings, epoxys, fiberglass constructions and the like. Many other applications will be readily apparent to those familiar with this art as a result of proceeding specification.

Claims: CLAIMS 1. A compound of the formula EMI25.1 wherein X is H or halogen, each R1 is selected from the group consisting of H, CH3, t-alkyl of 4 to 6 carbons and EMI25.2 wherein R2 is C2-C10 alkylene which may be straight chain or branched, and R3 is H or 013, provided that one R1 is H, CH3, or t-alkyl and the other R1 is EMI25.3 and homopolymers and copolymers thereof. 2. A compound according to claim 1, which is 2-(2' -Hydroxy-5' -methacrylyloxyethyl-phenyl)-2H- benzotriazole; 2-(2'-Hydroxy-5'-methacrylyloxyethylphenyl)-5-chloro-2H-benzotrazole; 2-(2'-Hydroxy-5'-methacrylyloxypropylphenyl)-2H-benzotriazole; 2-(2'-Hydroxy-5'-methacrylyloxypropylphenyl)-5-chloro-2H-benzotriazole; 2-(2'-Hydroxy-5'-methacrylyloxypropyl-3'- tert-butylphenyl)-2H-benzotriazole; or 2-(2'-Hydroxy-5'-methacrylyloxypropyl-3'tert-butylphenyl)-5-chloro-2H-benzotriazole; and homopolymers and copolymers thereof. 3. An ultraviolet absorbing composition comprising a copolymer of an ethylenically unsaturated monomer and an effective amount of a compound of Claim 1 or claim 2. 4. The composition of Claim 3e wherein said ethyl enically unsaturated monomer is styrene, methylstyrene, acrylate, methylcrylate, acrylamide, acrylonitrile, methacrylonitrile, vinylacetate, vinylidene chloride, vinyl chloride, ethylene, propylene or a mixture thereof. 5. The composition of claim 3 or claim 4 wherein the ethylenically unsaturated monomer is methyl methacrylate. 6. The composition of any one of claims 3 to 5, comprising 0.05 to 20% by weight of said compound according to claim 1 or claim 2. 7. The composition of claim 6, comprising 0.05 to 5.0% by weight of said compound according to claim 1 or claim 2. 8. A contact lens or intraocular lens comprising an optically clear composition according to any one of claims 3 to 7. 9. A compound of the formula EMI27.1 wherein X is H, halogen or -OCH3; R1 is selected from the group consisting of H, Cue3, and n-, sec- and t-alkyl of 4 to 6 carbons; and R2 is a Cn alkylene which may be straight chain or branched wherein n is from 2 to 10. 10 . The compound of claim 9, which is 2-(2'-Hydroxy-5hydroxyethylphenyl)-2H-benzotriazole; 2-(2'-Hydroxy-5'-hydroxyethylphenyl)-5 chloro-21l-benzotriazolei 2-(2'-Hydroxy-5'-hydroxypropylphenyl)2H-benzotriazole; 2-(2' -Hydroxy-5'-hydroxypropylphenyl)-5- chloro-2H-benzotriazole; 2-(2'-Hydroxy-5'-hydroxypropyl-3'-tert butylphenyl)2H-benzotriazole; or 2-(2'-Hydroxy-5'-hydroxypropyl-3'-tertbutylphenyl)-5-chloro-2H-benzotriazole.

Inventors: BEARD, CHARLES DAVID, DODDI, NAMASSIVAYA, YAMADA, AKIRA
Applicants: IOLAB CORPORATION
Application year: 1984
Main classification: C08F20
IPC codes: C08L101, C08F20, C08F212, C09K3, G02B1, C08F220, C07D249, G02B5, G02C7, C08F120, C08K5