A PROCESS FOR PREPARING LIQUID- OR SHOCK-ABSORBING MATERIAL STARTING FROM WASTE SLUDGE FROM THE PAPER OR BOARD INDUSTRY

Abstract: A process for preparing a liquid- or shock-absorbing ma­ terial, comprising the step of dewatering the waste water from a process in which fibres consisting completely or mainly of cellulose are wet-processed, to obtain a semi-dry mass, which mass is then reduced, after which the resulting material is subjected to a drying process, said waste water, based on dry matter, containing 20-50% by weight of fibres and 80-50% by weight of an inorganic pigment and being mixed with a sur­ factant, the reduction being carried out by conveying the semi-dry mass having a water content within the range of from 40 to 70% by weight by means of a screw, thus granulating the material.

Description: Title: A process for preparing liquid- or shock-absorbing material starting from waste sludge from the paper or board industry. The invention relates to a process for preparing a liquidor shock-absorbing material, comprising the step of dewatering the waste water from a process in which fibres consisting completely or mainly of cellulose are wet-processed, to form a semi-dry mass, which mass is then reduced, after which the resulting material is subjected to a drying process. Such a process is known from Dutch patent application 8002562, starting from waste sludge containing, based on the dry matter, 60-80 % by weight of fibres and 40-20 % by weight of filler and 0-10 % by weight of admixture. In this process the waste sludge is first dewatered to form a semi-dry mass and then cylindrical pellets are produced by means of a pelleting apparatus. Since in the paper and board industry waste sludge is often liberated which has a considerably lower fibre content, the known process requires adjustment of the composition of the sludge by adding additional fibrous material. This makes the process so expensive that from an economic point of view the production of the liquid- and shock-absorbing material is not attractive anymore, because this material will find a sale only if it is offered at a very low price. The prior art pelleting process has the drawback that firstly, the rate of absorption and the absorptive capacity of the material and the bulk density are reduced during the pelleting process owing to the composition of the raw material and the pressing pressure, and that secondly, whether the pelleting process proceeds well highly depends on fluctuations in the composition of the waste sludge, which, among other things, can make it necessary to subject the sludge to a pre-drying process. Moreover, it has turned out that when the liquid-absorbing material is presented for use in animal cages and animal toilets, the pellet form obtained by extrusion is too much different from the products holding a fixed position on the market so that this material is in poor demand. Finally, the pelleting process requires a relatively expensive pelleting mill, which again makes the process more expensive. The object of the invention is to provide a process for preparing a liquid- and shock-absorbing material, starting from the waste sludge from the paper and board industry, which material can be prepared without additionally adding fibres from the waste sludge and has a very high absorptive capacity and rate of absorption, and which material can be inexpensively brought into such a form as to obtain a proper adjustment to products holding a fixed position on the market. For this purpose, the invention provides a process of the above type, in which the waste water, based on dry matter, contains 20-50 % by weight of fibres and 80-50 % by weight of an inorganic pigment, the waste water is mixed with a surfactant and the reduction is carried out by conveying the semi-dry mass having a water content ranging from 40 to 70 % by weight by means of a screw, thus granulating the material. Preferably, the end product is granulated by means of a screw conveyor transmitting the semi-dry mass, after it has been dewatered, to the drying apparatus in which the moisture content is reduced to the desired final value. The use of a screw conveyor is not only more advantageous than the use of a pelleting mill, but, as a granular form is obtained, it also provides a better adjustment to the already established liquid-absorbing materials The waste sludge obtained in the waste water purification of, e.g., paper mills and used in the process according to the invention contains fibres and inorganic pigments in the weight ratio ranging from 1:1 to 0.25:1, which corresponds to 20-50 % by weight of fibres and 80-50 % by weight of inorganic pigment, based on the dry matter. If required, the sludge may further contain 0-10 % by weight of admixture. According to the invention a surface active compound is added to the waste sludge and is intensively mixed with waste sludge to control the rate of absorption and the absorptive capacity. The resulting slurry is dewatered to obtain a final moisture content varying from 1 to 10 % by weight, preferably from 2 to 5 % by weight. In order to economically obtain this moisture content, the slurry is first dewatered, e.g., by means of a known per se band filter, to obtain a moisture content of 70-40 % by weight, preferably 65-55 % by weight. The semi-dry mass ts ;si#plied#to a adrying apparatus via a screw mechanism. The product is granulated during the transport through the screw mechanism. These granules may be further reduced, if required, by means of a sieve, which permits the control of the final bulk density. Whether or not sieves are used depends on the drying method and the composition of the raw material. The granulated product is dried in the drying apparatus by means of hot air having a temperature of 80-300 C, preferably 130-200 C. For an economic drying process it is advantageous to utilize for the hot air the waste heat from a boiler or a thermal power station. After drying, the product may be sifted again so as to control the bulk density. The bulk density may vary between 250-500 kg/m3, but is preferably 350-450 kg/m3. The granules prepared by the process according to the invention prove to have excellent water and oil absorbing properties. The granules may absorb 80 % or more of their own weight of respectively oil and water. When these granules are used for animal cages and animal toilets, not only the high rate of absorption and absorptive capacity are advantageous, but also the granular form of the material properly adjusts to the already available similar products.

Claims: CLAIMS 1. A process for preparing a liquid- or shock-absorbing material, comprising the step of dewatering the waste water from a process in which fibres consisting completely or mainly of cellulosearewet-processed, to obtain a semi-dry mass, which mass is then reduced, after which the resulting material is subjected to a drying process, characterized in that the waste water, based on dry matter, contains 20-50 % by weight of fibres and 80-50 % by weight of an inorganic pigment, that the waste water is mixed with a surfactant, and that the reduction is carried out by conveying the semi-dry mass having a water content within the range of from 40 to 70 % by weight by means of a screw, thus granulating the material. 2. A process according to claim 1, characterized in that the waste water, based on the dry matter content, contains 0-10 % by weight of an admixture. 3. A process according to claim 1 or 2, characterized in that the semi-dry mass has a moisture content of 55-65 % by weight when being conveyed by the screw. t. A process according to at least one of the preceding claims, characterized in that the granules are sifted before drying. 5. - A process according to at least one of the preceding claims, characterized in that the granules are dried by means of hot air having a temperature of 80-3000 C. 6. A process according to claim 5, characterized in that the hot air has a temperature of 130-2000 C and the waste heat is from a boiler or a thermal power station. 7. A process according to at least one of the preceding claims, characterized in that the granules formed are dried to obtain a water content of 2-5 % by weight. 8. A process according to at least one of the preceding claims, characterized in that the variables of the individual process steps are so adjusted to each other that the resulting granules have a bulk density of 350-450 kg/m3.

Inventors: ANDRE DE LA PORTE, WICHER, BROENS, HUBERTUS W., DE WILDE, ETIENNE F., André de la Porte, Wicher
Applicants: KNP PAPIER B.V.
Application year: 1984
Main classification: C02F11
IPC codes: C02F11, C09K3, A01K1, D21C11