MELT BLEND OF NON-THERMOTROPIC AND THERMOTROPIC WHOLLY AROMATIC POLYESTERS

Abstract: A polymer blend which is capable of exhibiting a melt phase containing isotropic and anisotropic regions and the ability to form shaped articles having satisfactory mechanic­ al properties is provided. The polymer blend comprises approximately 20 to approximately 75 percent by weight, based upon the total weight of the blend, of a melt processable wholly aromatic polyester which is not capable of forming an anisotropic melt phase apart from the blend and approximately 25 to approximately 80 percent by weight, based upon the total weight of the blend, of a melt processable wholly aromatic polyester which is capable of forming an anisotropic melt phase apart from the blend and which is substantially present in the melt blend in the form of elongated domains of an aspect ratio of at least about 3 and a volume of at least about 1µ³.

Description: MELT BLEND OF NON-THERMOTROPIC AND THERMOTROPIC WHOLLY AROMATIC POLYESTERS BACKGROUND OF THE INVENTION The present invention relates to a melt blend of melt process able thermotropic and non-thermotropic wholly aromatic polyesters. The characteristics and properties of such a blend differ significantly from those expected in light of observations of the prpperties of ordinary mixtures and of many polymeric blends. With some known exceptions, mixtures of polymeric materials are generally immiscible. That is, they consist of domains of chemically distinct phases. In general, one component forms a continuous phase, while the other component forms roughly spherical domains (aspect ratio less than 3) as inclusions. Under some circumstances, bi-continuous structures are also obtainable. Mixing two arbitrarily chosen polymers usually results in inferior materials having no utility, since in the absence of adhesion between phases, the dispersed phase merely weakens the continuous phase. Many useful blends are known, however, whose morphology and phase interaction are favorable. Some polymeric materials, such as polyalkylene terephthalate and most wholly aromatic polyesters, exhibit an ordered structure in at least some regions of the polymer. This order can exist in one, two, or three dimensions. U.K. Published Patent Application 2,008,598 and U.S. Patent No. 4,228,218 disclose a polymer composition comprising 20 percent or less, based upon the total weight of polymeric material, of a first rigid polymeric material with the balance being a second polymeric material composed substantially of flexible molecular chains. The first polymeric material is dispersed in the second polymeric material in a microscopic region of 1 m. or less. Foreign counterparts of this application include Japan 54065747, French 2407956, and West German 2847782. Blends of various thermotropic wholly aromatic polyesters are known as disclosed in commonly-assigned U.S. Patent No. 4,267,289. Blends of thermotropic wholly aromatic polyesters with polyarylene sulfide are known as disclosed in U.S. Patent No. 4,267,397. It is an object of the present invention to provide a blend of thermotropic and non-thermotropic wholly aromatic polyesters which exhibits satisfactory mechanical properties, such as tensile strength, tensile modulus, flexural strength, flexural modulus, impact strength, and heat deflection temperature. It is also an object of the present invention to provide a blend of thermotropic and non-thermotropic wholly aromatic polyesters which exhibits greater ease of processing due to the viscosity-reducing effect of the thermotropic component. It is also an object of the present invention to provide a blend of thermotropic and non-thermotropic wholly aromatic polyesters which, by virtue of the inclusion of a relatively less expensive component, is less expensive than the relatively more expensive component alone and which exhibits no significant reduction in mechanical properties. These and other objects as well as the scope, nature, and utilization of the present invention will be apparent from the following description and appended claims. SUMMARY OF THE INVENTION In accordance with the present invention, there is thus provided a polymer melt blend which is capable of exhibiting a melt phase containing isotropic and anisotropic regions and possesses the ability to form shaped articles having satisfactory mechanical properties. The melt blend comprises: : (a) approximately 20 to approximately 75 percent by weight, based upon the total weight of components (a) and (b), of a melt prpcessable wholly aromatic polyester which is not capable of forming an anisotropic melt phase apart from the blend; (b) approximately 25 to approximately 80 percent by weight, based upon the total weight of components (a) and (b), of a melt processable wholly aromatic polyester which is capable of forming an anisotropic melt phase apart from the blend and which is substantially present in the melt blend in the form of elongated domains of an aspect ratio of at least about 3 and a volume of at least about 1g3. In accordance with the present invention, there are also provided shaped articles comprised of the above-identified blend. BRIEF DESCRIPTION OF THE DRAWINGS Figure 1 is a scanning electron micrograph of a fracture surface of a molded specimen comprised of the blend of the present invention at a magnification of 3500. Figures 2 and 3 are scanning electron micrographs of fracture surfaces of molded specimens comprised of the blend of the present invention at a magnification of 5000. Figure 4 is a scanning electron micrograph of a fracture surface of a molded specimen comprised of the blend of the present invention at a magnification of 1500. Figure 5 is a scanning electron micrograph of a fracture surface of a molded specimen comprised of the blend of the present invention at a magnification of 2000. DETAILED DESCRIPTION OF THE INVENTION The present invention provides a melt blend of melt processable, thermotropic (as defined) and non-thermotropic wholly aromatic polyesters. It has been surprisingly and unexpectedly found that the blends of the present invention exhibit unique self-reinforcing characteristics due to the inherent domain-forming properties of the thermotropic wholly aromatic polyesters employed. Such self-reinforcing characteristics enable the use of reinforcing fibers to be avoided during formation of the blend. The first component of the melt blend of the present invention is a non-thermotropic wholly aromatic polyester. Such non-thermotropic wholly aromatic polyesters are not capable of forming an an isotropic melt phase apart. The non-thermotropic wholly aromatic polyesters are considered to be "wholly" aromatic in the sense that each moiety present in the polymer contributes at least one aromatic ring to the polymer backbone. Such moieties may be derived from aromatic diols, aromatic diacids and aromatic hydroxy acids. Exemplary non-thermotropic wholly aromatic polyesters which can be employed in the present invention include but are not limited to copolymers of bisphenol A and isophthalic or terephthalic acid or mixtures thereof. Such copolymers are well-known in the art as evidenced by the disclosure of U.S. Patent Nos. 3,684,766 and 3,728,4herein incorporated by reference. The bisphenol A will generally be present in such copolymers in an amount of about 50 mole percent, with the isophthalic or terephthalic acid component being present in an amount of about 50 mole percent. When mixtures of the isophthalic and terephthalic acid component are employed, they will generally individually be present in an amount ranging from 25 to 75 mole percent, respectively, of the combined isophthalic and terephthalic acid component. The second component of the melt blend is a thermotropic wholly aromatic polyester. Such polyesters are well-known to those skilled in the art. Thermotropic liquid crystal polymers are polymers which are liquid crystalline (i.e., an isotropic) in the melt phase. These polymers have been described by various terms, including "liquid crystalline", "liquid crystal," "mesomorphic" and "anisotropic". Briefly, the polymers of this class are thought to involve a parallel ordering of the molecular chains. The state wherein the molecules are so ordered is often referred to either as the liquid crystal state or the nematic phase of the liquid crystalline material. These polymers are prepared from monomers which are generally long, flat and fairly rigid along the long axis of the molecule and commonly have chain-extending linkages that are either coaxial or parallel. Such polymers readily form liquid crystals (i.e., exhibit anisotropic properties) in the melt phase. Such properties may be confirmed by conventional polarized light techniques whereby crossed polarizers are utilized. More specifically, the an isotropic melt phase may be confirmed by the use of a Leitz polarizing microscope at a magnification of 40X with the sample on a Leitz hot stage and under nitrogen atmosphere. The polymer is optically anisotropic; i.e., it transmits light when examined between crossed polarizers. Polarized light is transmitted when the sample is optically anisotropic even in the static state. As was the case with the first component, the thermotropic wholly aromatic polyesters employed in the present invention are considered to be "wholly" aromatic in the sense that each moiety present in the polymer contributes at least one aromatic ring to the polymer backbone and which enables the polymer to exhibit anisotropic properties in the melt phase. Such moieties may be derived from aromatic diols, aromatic diacids and aromatic hydroxy acids. Moieties which may be present in such thermotropic liquid crystal polymers suitable for use in the present invention include but are not limited to the following: EMI6.1 For the purposes of the present inventioltatic rings which are included in the polymer backbones of the polymer components may include substitution of at least some of the hydrogen atoms present upon an aromatic ring. Such substituents include alkyl groups of up to four carbon atoms; alkoxy groups having up. to four carbon atoms; halogens; and additional aromatic rings, such as phenyl and substituted phenyl. Preferred halogens include fluorine, chlorine and bromine. Thermotropic liquid crystalline polymers which are suitable for use in the present invention must be capable of forming the requisite domains when present in the blend such that the polymer is substantially present in the blend in the form of domains as defined (e.g., at least 50 percent of the polymer by volume). The presence of the domains may be verified by scanning electron micrographs of fracture surfaces of molded or extruded articles comprised of the blend or of residue left after removal of the non-thermotropic material by a suitable solvent. Thermotropic wholly aromatic polyesters are well-known to those skilled in the art. Recent publications disclosing such polyesters include (a) Belgian Pat. Nos. 828,935 and 828,936, (b) Dutch Pat. No. 7505551, (c) West German Pat. Nos. 2,520,819, 2,520,820, and 2,722,120, (d) Japanese Pat. Nos. 43-223, 2132-116, 3017-692, and 3021-293, (e) U.S. Pat. Nos. 3,991,013; 3,991,014; 4,057,597; 4,066,620; 4,075,262; 4,118,372; 4,146,702; 4,153,779; 4,156,070; 4,159,365; 4,169,933; 4,181,792; 4,188,476; 4,201,856; 4,226,970; 4,232,143; 4,232,144; 4,238,600; 4,245,082; and 4,247,514; and (f) U.K. Application No. 2,002,404. Thermotropic wholly aromatic polyesters are also disclosed in commonly-assiond U.Sw Patent Nos. 4,067,852; 4,083,829; 4,130,545; 4,161,470; 4,184,996; 4,219,461; 4,224,433; ,238,598; 4,238,599; 4,256,624; 4,279,803; 4,299,756; 4,330,557 and 4,337,191. The disclosures of all of the above-identified commonly-assigned U.S. patents and applications are herein incorporated by reference in their entirety. The wholly aromatic polyesters disclosed therein typically are capable of forming an anisotropic melt phase at a temperature below approximately 4000C., and preferably below approximately 35DoC. The thermotropic wholly aromatic polyesters which are suitable for use in the present invention may be formed by a variety of ester-forming techniques whereby organic monomer compounds possessing functional groups which, upon condensation, form the requisite recurring moieties are reacted. For instance, the functional groups of the organic monomer compounds may be carboxylic acid groups, hydroxyl groups, ester groups, acyloxy groups, acid halides, etc. The organic monomer compounds may be reacted in the absence of a heat exchange fluid via a melt acidolysis procedure. They, accordingly, may be heated initially to form a melt solution of the reactants with the reaction continu ing as said polymer particles are suspended therein. A vacuum may be applied to facilitate removal of volatiles formed during the final stage of the condensation (e.g., acetic acid or water). Commonly-assigned U.S. Patent No. 4,083,829, entitled "Melt Prccessable Thermotropic Wholly Aromatic Polyester," describes a slurry polymerization process which may be employed to form the wholly aromatic polyesters which are preferred for use in the present invention. According to such a process, the solid product is suspended in a heat exchange medium. The disclosure of this patent has previously been incorporated herein b refr- ence in its entirety. When employing either the melt acidolysis procedure or the slurry procedure of U.S. Patent No. 4,083,829, the organic monomer reactants from which the wholly aromatic polyesters are derived may be initially provided in a modified form whereby the usual hydroxy groups of such monomers are esterified (i.e., they are provided as lower acyl esters). The lower acyl groups preferably have from about two to about four carbon atoms. Preferably, the acetate esters of organic monomer reactants are provided. Representative catalysts which optionally may be employed in either the melt acidolysis procedure or in the slurry procedure of U.S. Patent No. 4,083,829 include dialkyl tin oxide (e.g., dibutyl tin oxide), diaryl tin oxide, titanium dioxide, antimony trioxide, alkoxy titanium silicates, titanium alkoxides, alkali and alkaline earth metal salts of carboxylic acids (e.g., zinc acetate), the gaseous acid catalysts such as Lewis acids (e.g., BF3), hydrogen halides (e.g., HC1), etc. The quantity of catalyst utilized typically is about 0.001 to 1 percent by weight based upon the total monomer weight, and most commonly about 0.01 to 0.2 percent by weight. The thermotropic wholly aromatic polyesters suitable for use in the present invention tend to be substantially insoluble in common solvents and accordingly are not susceptible to solution.processing. As discussed previously, they can be readily processed by common melt processing techniques. Most suitable wholly aromatic polymers are soluble in pentafluorophenol to a limited degree. The thermotropic wholly aromatic polyesters which are rrcscrrcd for l in the recent invention commonly exhibit a weight average molecular weight of about 2,000 to 200,000, and preferably about 10,000 to 50,000, and most preferably about 20,000 to 25,000. Such molecular weight may be determined by gel permeation chromatography as well as by other standard techniques not involving the solutioning of the polymer, e.g., by end group determination via infrared spectroscopy on compression molded films. Alternatively, light scattering techniques in a penta--- fluorophenol solution may be employed to determine the molecular weight. The wholly aromatic polyesters additionally commonly exhibit an inherent viscosity (i.e., I.V.) of at least approximately 2.0 dl./g., e.g., approximately 2.0 to 10.0 dl./g., when dissolved in a concentration of 0.1 percent by weight in pentafluorophenol at 600C. Especially preferred thermotropic wholly aromatic polyesters are those which are disclosed in above-noted U.S. Patent Nos. 4,161,470 and 4,330,457. The wholly aromatic polyester which is disclosed in U.S. Patent No. 4,161,470 is a melt processable wholly aromatic polyester capable of forming an anisotropic melt phase at a temperature below approximately 350 C. The polyester consists essentially of the recurring moieties I and II wherein: EMI10.1 The polyester comprises approximately 10 to 90 mole percent of moiety I, and approximately 10 to 90 mole percent of moiety II. In one embodiment, moiety II is present in a concentration of approximately 65 to 85 mole percent, and preferably in a concentration of approximately 70 to 80 mole percent e.g., approximately 75 mole percent. In another embodiment, moiety II is present in a lesser proportion of approximately 15 to 35 mole percent, and preferably in a concentration of approximately 20 to 30 mole percent. In addition, at least some of the hydrogen atoms present upon the rings optionally may be replaced by substitution selected from the group consisting of an alkyl group of 1 to 4 carbon atoms, an alkoxy group of 1 to 4 carbon atoms, halogen, phenyl, substituted phenyl, and mixtures thereof. The polyester disclosed in U.S. Patent No. 4,330,457 is a melt processable wholly aromatic polyester-amide which is capable of forming an anisotropic melt phase at a temperature below approximately 400"C. The polyester-amide consists essentially of the recurring moieties I, II, III and optionally IV wherein: EMI11.1 II is EMI11.2 where A is a divalent radical comprising at least one aromatic ring or a divalent trans-1,4cyclohexylene radical; III is +Y-Ar-Z+, where Ar is a divalent radical comprising at least one aromatic ring, Y is O, NH, or NR, and Z is NH or NR, where R is an alkyl group of 1 to 6 carbon atoms or an aryl group; and IV is +O-Ar'-O+, where Ar' is a divalent radical com prising at least one aromatic ring; wherein at least some of the hydrogen atoms present upon the rings optionally may be replaced by substitution selected from the group consisting bf an alkyl group of 1 to 4 carbon atoms, an alkoxy group of 1 to 4 carbon atoms, halogen, phenyl, substituted phenyl and mixtures thereof, and wherein said polyester-amide comprises approximately 10 to 90 mole percent of moiety I, approximately 5 to 45 mole percent of moiety II, approximately 5 to 45 mole percent of moiety III, and approximately 0 to 40 mole percent of moiety IV. The blend of the present invention comprises approxilately 20 to approximately 75 percent by weight of the nonthermotropic wholly aromatic polyester component and approximately 25 to approximately 80 percent by weight of the thermotropic wholly aromatic polyester component. Preferably, the blend comprises approximately 30 to approximately 50 percent by weight of the thermotropic wholly aromatic polyester component. The above weight percentages are based upon the total weight of the two polymeric components in the blend, exclusive of additionally added components such as fillers, etc. The blend comprised of the previously-identified wholly aromatic polyester components may also include in minor proportion various non-wholly aromatic polyester polymers. Such additional polymers will not be present in an amount greater than about 50 percent by weight, based on the weight of the polymeric components, and preferably will be present in an amount less than about 25 percent by weight. In preparing the blend of the present invention, the individual components are commonly provided in the form of chips or pellets. Each of the components is weighed separately, and then the components are physically mixed together in any appropriate apparatus, e.g., a ball mill. The physical mixture is then dried at approximately 100 C. overnight or for a period of time of approximately 24 hours. The mixture is conveniently dried in a vacuum oven or in a circulating air oven, although any suitable apparatus may be used. The purpose of the drying step is to remove water from the physical mixture so as to prevent degradation of the polymers during the blending operation. After the mixture of solid polymer particles has been dried, the polymer melt blend can then be prepared. A convenient method of forming the polymer melt blend is melt extrusion. The extrusion apparatus thoroughly mixes the polymers in the melt and then extrudes the blend in the form of a strand which, upon solidificaton, can be broken up into chips or pellets. As previously discussed, it is known in the art that melt blends of two polymers tend to undergo phase separation, with a concomitant reduction in properties, due to the incompatibility of the polymers. However, unexpected and surprising results are achieved with the blend of the present invention. It has been observed that mechanical properties of the blend are significantly and usefully improved over that of the non-thermotropic wholly aromatic polyester matrix alone. Such physical advantages have been found to exist as a result of the formation of domains of the liquid crystalline polymer component which provide reinforcement for the blend. Such domain rn highly erongted in dimension and may, for example, be sheet-like or fiber-like in form. The domains have aspect ratios (i.e., the ratio of the length of the domain to the greatest thickness thereof) in excess of at least about 3:1 and generally ranging from about 10:1 to 100:1 or greater. For example, the aspect ratio of a sheet-like domain is the ratio of the length of the sheet to the thickness of the sheet. The length of typical domains can range from about 5u to 100v or- or infinitely long domains, with the volume thereof being at least about 1 3. The domains are oriented in the melt processing direction (i.e., the machine direction) of the blend and provide substantial reinforcement in the machine direction. Such domains offer advantages as a reinforcing material due to the fact that they can be significantly longer in dimension than would be reinforcing fibers which would conventionally separately be admixed with the blend prior to processing. The length of reinforcing fibers added to such blends is limited by the need to retain satisfactory melt processing characteristics and by breaking of the added fibers during the blending. Such considerations render the inclusion of lengthy reinforcing fibers objectionable. By way of contrast, the liquid crystalline polymers employed in the blends of the claimed invention do not suffer from such disadvantages in that they can be processed according to conventional melt processing techniques while inherently forming the self-reinforcing domains in the blend during melt processing. The disposition of the domains is not spacially regular, but the domains are often found to have their long axes oriert esnially parallel. Such parallel orientation enhances the reinforcing characteristics of the domains. The blend of the present invention is capable of undergoing melt processing at a temperature within the range of approximately 2400C. to 4000C. Preferably, the blend is capable of undergoing melt processing at a temperature within the range of approximately 275 C. to 3500C. The blend of the present invention demonstrates anisotropy in the melt phase. This is due to the fact that the thermotropic wholly aromatic polyester has been found to retain its anisotropic characteristics in spite of the presence of the other component. Thus, the liquid crystalline polymer components impart excellent processability characteristics to the blend. The blend of 'the present invention is useful as a molding resin, and especially for injection molding. The blend can also be used in the formation of extruded articles and fibers and films. Articles molded from the blend of the present invention exhibit good mechanical properties, such as tensile strength, tensile modulus, flexural strength, flexural modulus, notched Izod impact strength, and heat deflection temperature. Articles may also be molded. from a molding compound which includes, as one component, the blend of the present invention. Such a molding compound incorporates into the blend of the present invention approximately 1 to 50 percent and preferably approximately 10 to 30 percent by weight, based upon the total weight of the molding compound, of a solid filler and/or reinforcing agent. Representative fibers which may serve as reinforcing media include glass fibers, asbestos, graphitic carbon fibers, amorphous carbon fibers, synthetic polymeric fibers, aluminum fibers, aluminum silicate fibers, aluminum oxide fibers, titanium fibbers, magnesium fibers. rock wool fibers, steel fibers, tungsten fibers, cotton, wool, and wood cellulose fibers, etc. Representative filler materials include calcium silicate, silica, clays, talc, mica, polytetrafluoroethylene, graphite, alumina trihydrate, sodium aluminum carbonate, barium ferrite, etc. In order to form an article by injection molding from the present blend, or from a molding compound made from the present blend, the blend or molding compound is brought to the melt temperature of the blend, e.g., approximately 2800C. to 3000C., and is then injected into a mold cavity. The mold cavity is commonly maintained at a temperature less than approximately 1000C., e.g., approximately 900C. to 1000C. The blend in its melt phase is injected into the mold cavity at a pressure of approximately 10,000 p.s.i. The cycle time (i.e., the time between injections) for the present blend commonly is about 10 to 40 seconds. The properties of articles formed from blend compositions of the present invention can be improved by heat treatment to promote transesterification between the components. The articles may be thermally treated in an inert atmosphere (e.g., nitrogen, argon, helium) or alternatively a flowing oxygencontaining atmosphere (e.g., air). It has been observed that the properties of articles formed from the blend of the present invention vary with the processing conditions, such as mold temperature, injection pressure, cycle time, etc. However, it would be obvious to one of ordinary skill in the art to experimentally determine those conditions which maximize the properties of articles formed from the present blend. The following examples are given as specific illustrations of the invention. It should be understood, however, that the invention is not limited to the specific details set forth in the examples. A review of the examplary data will indicate that the mechanical properties of the non-liquid crystalline wholly aromatic polyester are improved when present as the matrix polymer as a result of the presence of the liquid crystallinewholly aromatic polyester domains. EXAMPLE 1 A blend comprised of 70 weight percent of a polymer blend marketed by Union. Carbide under the tradename Ardel AX-1500 comprised of a major amount of a non-thermotropic wholly aromatic polyester prepared from bisphenol A, isophthalic acid and terephthalic acid and a minor amount of nylon and 30 weight percent of a thermotropic liquid crystalline wholly aromatic polyester comprised of 40 mole percent of p-oxybenzoyl moieties and 60 mole percent of 6-oxy-2-naphthoyl moieties was formed by physically admixing pellets comprised of the two components and extrusion blending the same in a single screw extruder with the blend then being repelletized. Pellets of the blend were subsequently injection molded at a temperature of 3000C at a mold temperature of 66 C to form tensile bars and flexural bars. The mechanical properties of the bars were determined according to ASTM D638 with a testing area of 0.125 x 0.075 inches (tensile properties) and ASTM D790 (flexural properties) and listed below as Sample A. Tensile bars and flexural bars comprised solely of Ardel AX-1500 were also formed, with the mechanical properties thereof being set forth below as Sample B A decrease in injection molding pressure of about 35 percent was observed for the Sample A blend as opposed to the Sample B blend. TABLE I ExamPle 1 Results Tensile Tensile Flexural Flexural Sample Strength (KSI) Modulus (MSI) Strength (KSI) Modulus (MSI) A 14.8 0.620 14.6 0.482 B 10.3 0.220 9.75 0.225 Fracture surfaces of the molded sample A were examined under a scanning electron microscope at a magnification of 3500 (Figure 1). Exemplary domains of the liquid crystalline polymer component depicted therein as (1) and (2) had average diameters of about 1 micron and visible lengths of at least about 10 microns. Specifically, domain (1) had a diameter of about 1 micron while domain (2) had a diameter of about 3 microns. EXAMPLE 2 A blend comprised of 70 weight percent of a nonthermotropic wholly aromatic polyester marketed by Union Carbide under the tradename Ardel D-100 prepared from bisphenol A, isophthalic acid and terephthalic acid and 30 weight percent of a thermotropic liquid crystalline wholly aromatic polyester prepared from 60 mole percent of 6-hydroxy-2-naphthoic acid, 20 mole percent of terephthalic acid and 20 mole percent of pacetoxyacetanilide, was formed by physically admixing pellets comprised of the two components and extrusion blending the same in a single screw extruder with the blend then being repelletized. Pellets of the blend were subsequently injection molded at a temperature of 3500C at a mold temperature of 1000C to form tensile bars and flexural bars: The mechanical properties of the bars were determined as in Example 1 and listed below as Sample A. Tensile bars and flexural bars comprised solely of the non-thermotropic wholly aromatic polyester Ardel D100 were also formed, with the mechanical properties thereof being set forth below as Sample B. A decrease in injection molding pressure of about 35 percent was observed for the Sample A blend as opposed to the Sample B blend. TABLE II Example 2 Results Tensile Tensile Flexural Flexural Sample Strength (KSI) Modulus (MSI) Strength (KSI) Modulus (MSI) A 13.4 0.552 12.8 0.426 B 9.0 0.284 12.5 0.328 Fracture surfaces of a molded Sample A were examined under a scanning electron microscope at a magnification of 5000 (Figure 2). Exemplary domains of the liquid crystalline polymer component depicted as (1)-(5) had average diameters of about 1 micron and visible lengths of at least about 10 microns. Figure 3 similarly depicts a fracture surface of a molded Sample A at a magnification of 5000 having domains of the liquid crystalline polymer component which are elongated, parallel, irregular in width and rather flat. The domain widths range from about 0.2 to 2.5 microns, averaging about 0.5 micron. EXAMPLE 3 A blend comprised of 70 weight percent of a nonthermotropic wholly aromatic polyester marketed by Union Carbide under the tradename Ardel AX-1500 (previously identified) and 30 weight percent of a thermotropic liquid crystalline wholly aromatic polyester prepared from 60 mole percent of 6-hydroxy-2naphthoic acid, 20 mole percent of terephthalic acid'and 2 mole percent of p-acetoxyacetanilide was formed by physically admixing pellets comprised of the polymers and extrusion blending the same in a single screw extruder with the blend then being repelletized. Pellets of the blend were subsequently injection molded at a temperature of 350 CC at a mold temperature of 1000C to form tensile bars. Fracture surfaces of the molded specimens were examined under a scanning electron microscope at a magnification of 1500 (Figure 4) and 2000 (Figure 5). Exemplary domains of the liquid crystalline polymer component depicted as (1) and (2) in Figure 4 had average diameters of about 2 microns and lengths of at least about 10 microns. The domain depicted as (3) in Figure 5 had an average diameter of about 2 microns and a visible length of at least 30 microns. The principles, preferred embodiments and modes of operation of the present invention have been described in the foregoing specification. The invention which is intended to be protected herein, however, is not to be construed as limited to the particular forms disclosed, since these are to be regarded as illustrative rather than restrictive. Variations and changes may be made by those skilled in the art without departing from the =.pirit of the intzention.

Claims: 'cLAIMS: 1. A polymer melt blend which is capable of exhibiting an anisotropic melt phase and the ability to form shaped articles having satisfactory mechanical properties comprising: (a) approximately 20 to approximately 75 percent by weight, based upon the total weight of components (a) and (b), of a melt processable wholly aromatic polyester which is not capable of forming an anisotropic melt phase apart from said blend; and (b) approximately 25 to approximately 80 percent by weight, based upon the total weight of components (a) and (b), of a melt processable wholly aromatic polyester which is capable of forming an aniso tropic melt phase apart from said blend and which is substantially present in the blend in the form of elongated domains of an aspect ratio of at least about 3 and a volume of at least about lu31 2. The polymer blend of Claim 1 which is capable of undergoing melt processing at a temperature within the range of approximately 240 C. to 4000C. 3. The polymer blend of Claim 1 which is capable of undergoing melt processing at a temperature within the range of approximately 275"C. to 3500C. 4. The polymer blend of Claim 1 wherein said component (a) is a copolymer of bisphenol A, isophthalic acid and terephthalic acid. 5. The polymer blend of Claim 1 wherein said component (a) is a copolymer of bisphenol A and terephthalic acid. 6. The polymer blend of Claim 1 wherein said component (b) apart from said blend is capable of forming an an isotropic melt phase at a temperature below approximately 400 C. 7. The polymer blend of Claim 1 wherein said component (b) apart from said blend exhibits an inherent viscosity of at least 2.0 dl./g. when dissolved in a concentration of 0.1 percent by weight in pentafluorophenol at 600C. 8. The polymer blend of claim 1 wherein said component (a) is present in an amount ranging from approximately 70 to approximately 50 percent by weight and said component (b) is present in an amount ranging from approximately 30 to 50 percent by weight. 9. A molding compound comprising the polymer blend of claim 1 which incorporates approximately 1 to 50 percent by weight based upon the total weight of said molding compound, of a solid filler and/or reinforcing agent. 10. The molding compound of Claim 9 which incorporates approximeteLy 10 to annroximately 30 percent by weight, based upon the total weight of said molding compound, of a solid filler and/or reinforcing agent. 11. A molded article comprising the polymer blend of claim 1. 12. An extruded article comprising the polymer blend of claim 1. 13. A fiber which has been melt spun from the polymer blend of claim 1. 14. A film which has been melt extruded from the polymer blend of claim 1. 15. The polymer blend of claim 1 wherein said component (b) consists essentially of the recurring moieties I and II wherein: EMI23.1 wherein the polyester comprises approximately 10 to 90 mole percent of moiety I, and approximately 10 to 90 mole percent of moiety II, and wherein at least some of the hydrogen atoms present upon the rings optionally may be replaced by substitution selected from the group consisting of an alkyl group of 1 to 4 carbon atoms, an alkoxy group of 1 to 4 carbon atoms, halogen, phenyl, substituted phenyl, and mixtures thereof. 16. The polymer blend of claim 1 wherein said component (b) consists essentially of recurring moieties I, II, III and, pptionally, IV wherein: EMI24.1 II is EMI24.2 where A is a divalent radical comprising at least one aromatic ring or a divalent trans-1,4 cyclohexylene radical; III is iY-Ar-Zi, where Ar is a divalent radical comprising at least one aromatic ring, Y is O, NH, or NR, and Z is NH or NR, where R is an alkyl group of 1 to 6 carbon atoms or an aryl group; and IV is +O-Ar'-O+, where Ar' is a divalent radical comprising at least one aromatic ring. wherein at least some of the hydrogen atoms present upon the rings optionally may be replaced by substitution selected from the group consisting of an alkyl group of 1 to 4 carbon atoms, an alkoxy group of 1 to 4 carbon atoms, halogen, phenyl, substituted phenyl and mixtures thereof, and wherein said polyester-amide comprises approximately 10 to 90 mole percent of moiety I, approximately 5 to 45 mole percent of moiety II, approximately 5 to 45 mole percent of moiety III, and approximately 0 to 40 mole percent of moiety IV.

Inventors: KISS, GABOR D.
Applicants: CELANESE CORPORATION
Application year: 1984
Main classification: C08L67
IPC codes: C08L67