NAIL ENAMEL CONTAINING SILICONE-COATED PIGMENTS

Abstract: Pigmented nail enamels in which the pigment is coated with an organo-polysiloxane exhibit greatly reduced settling and migration of the pigment.

Description: NAIL ENAMEL CONTAINING SILICONE-COATED PIGMENTS This invention relates to nail enamels. It particularly relates to nail enamels which are substantially free of the settling and the migration of the pigment and other materials suspended in the composition. Conventional nail enamel compositions incorporate in their formulas a montmorillonite clay as a gellant to suspend pigments and pearlescent materials contained therein. To achieve desired properties for these systems, as much as 2.0% or more of the gellant is recommended to effect complete and stable suspension. The use of larger amounts of the gellant in a nail enamel composition adversely affects the application and flow properties of the preparation. When the levels of the gellant are reduced to about 0.5-1.25%, other additives must then be added to maintain desired suspension and performance characteristics. It is also known that nail enamel compositions exhibit pigment migration, i.e., preferential separation, flocculation and flotation as distinguished from settling. While migration does affect the performance of the nail enamel, the streaking effects noticeable from such migration are aesthetically undesirable. U.S. Patent No. 4,166,110 discloses a nail enamel which contains an organically substituted polysiloxane to render the enamel film easily strippable from the nail. The patent does not discuss how to incorporate pigments into such a formulation and does not suggest coating pigments with the polysiloxane. An article by B.V. Ashmead et al., "The Silicone Treatment of Titania", J. Oil Col. Chem. Assoc., Vol. 54 (1971), pp. 403-424, discusses the adsorption of various silicone polymers onto the surface of titanium dioxide and discloses that silicone treated pigments disperse better in conventional paint media than untreated pigments. This disclosure does not suggest how coated pigments would behave in the solvent system employed in nail enamels. Moreover, the emphasis on dispersion, i.e. the length of time one needs to stir the paint in order to disperse. the pigment in the surrounding media, does not support any suggestion as to how quickly the pigment settles and/or migrates once stirring is stopped. Indeed, freedom from settling and migration is of little or no concern to paint manufacturers, because the paint is in a non-transparent can until the user opens the can, stirs the paint, and applies the paint. By contrast, freedom from settling and migration even without stirring are of vital concern to the nail enamel manufacturer, who customarily sells the enamel in a transparent bottle, because the customer must be persuaded to buy the enamel based on how the enamel looks in the bottle. In accordance with the present invention, a pigmented nail enamel is provided which is substantially free from settling and migration of the pigment contained therein, in which the nail enamel contains an inorganic pigment which is coated with a poly(organosiloxane). The improved nail enamel is prepared by coating the pigment with the polysiloxane before mixing the coated pigment with the remaining components of the nail enamel. As indicated, the pigmented nail enamels contain pigment which has been coated with organically substituted polysiloxane. The polysiloxane coating is generally characterized in that it imparts to the pigment the desirable properties mentioned herein when formulated into a nail enamel. While we do not intend to be bound by any particular specific definition for the coating, we use the term "polysiloxane" to include polymeric chains having up to 100 or even to 1,000 repeating (Si-O) units, wherein at least one Si atom of each chain is linked to the pigment surface or the coated pigment surface as hereinafter described through an oxygen atom. The chains can be cross-linked to each other as well. The remaining functional sites of each Si atom in the chain can be occupied by hydrogen, methyl, C2-C30 alkyl or alkenyl, and/or phenyl, and equivalents thereof, resulting in units such as Si(CH3) (C6Hs)Ot, Si(CH3) (H)Ot, or tSi(H)(C6H5)0t, and generally capped with -Si(CH3)3, Satisfactory colors can be obtained in a variety of poly(organosiloxane)-coated pigments from Clarks Colors for whom the sole known distributor is Whittaker, Clark & Daniels, Inc. The product has the trade name "Hydrophobes." Alternatively, one can make the coated pigment by, for instance, reacting the uncoated pigment with (A) a silane of the formula AlSiXlX2X3, wherein A1 is alkyl or alkenyl having up to 30 carbon atoms and X1, X2 and X3 are independently chloro, methoxy or ethoxy; (B) (CH3)3SiO tSi(CH3)20tn Si(CH3)20A2 wherein n is 1 to 100 or up to 1,000, and A2 is C1-C30 alkyl; or (C) (CH3)3Sio4Si(CH3) (H)Otp Si(CH3)3 wherein p is 1 to 100 or up to 1,000. The reaction conditions are chosen so that X1, X2, X3, A2, or (H), as the case may be, hydrolyzes and bonds to the coated pigment surface through oxygen atoms. This mechanism, and appropriate reaction conditions, are familiar matters to the chemist. The pigment which is incorporated within the coating can be any cosmetically acceptable inorganic or organic pigment. Examples of such pigments include: iron oxides, titanated mica, iron oxide coated mica, titanium dioxide (e.g. rutile, anatase), ultramarine, chromium oxide, chromium hydroxide, manganese violet, and their equivalents. Preferred pigments from the above list are iron oxide and titanium dioxide. The poly(organosiloxane) coated pigment can in general comprise up to about 10 wt. % of the nail enamel product. More preferably, the coated pigment comprises up to about 2 wt. %, and even more preferably it comprises about 1 wt. % to about 2 wt. t. Nail enamels which contain the coated pigments set forth above exhibit greatly reduced settling and migration compared to enamels which are identical except for lacking the silicone coating on the pigment. In addition to the coated pigment, the nail enamel contains an otherwise conventional base, including nitrocellulose, solvent, and suspending agent. The base can also include a resin and a plasticizer. The resin should be one which adds to the durability, adhesion, and gloss of the enamel. Examples of preferred resins include toluene sulfonamide formaldehyde resin, and polyesters. The plasticizer should be effective to aid the enamel coating's flexibility. Examples of preferred plasticizers include dibutyl phthalate and dioctyl phthalate. The solvent should dissolve the other components of the base, allowing the enamel to flow onto the nail, and should be able to evaporate from the nail. Examples of preferred solvents include toluene, isopropanol, butyl acetate, ethyl acetate, and mixtures thereof. The suspending agent should help suspend the pigments in the base. Examples of preferred suspending agents include montmorillonite clays. A more complete listing of conventional bases which are useful with this invention can be found in standard sources well-known to the chemist, such as Cosmetics, Science and Technology, Balsam and Sagarin (eds.), 2nd Edition (1972), Vol. 2, Chapter 29 (Wiley Interscience, New York, N.Y.). The coated pigment can be dispersed into the other nail enamel components readily by conventional mixing techniques employed in nail enamel manufacture, for example, chipping, roller milling, etc. The superior effect of the present invention is seen in the following comparative examples. These examples are illustrative only and should not be construed as limiting. The numerical evaluation ratings have the following meanings: 5. Excellent - no visible signs of pigment migra tion or settling. 4. Good - Very slight settling observed, no signs of pigment migration. 3. Average - Some settling and very slight pigment migration. 2. Poor - Settling and migration readily apparent (not saleable). 1. Unacceptable - Very bad settling and migration (not saleable). In the following tables where pigment is indicated as "treated" it had been coated with poly(methyl-hydrogen)siloxane obtained from Clark Colors with the product number 9454 for the coated iron oxide, and product number 9428 for the coated titanium dioxide. The amounts of treated pigment were chosen to provide equal amounts of pigment per se in all four samples. All amounts are in percent by weight. EXAMPLE 1 Four samples of a nail enamel ("Ripe Plum") were prepared by mixing uniformly the ingredients indicated in Table 1. The products were compared for settling and migration after holding for two months without agitation, at room temperature or at 1200F. Table 1 Sample No.: 1 2 3 4 r Nitrocellulose 15.00 15.00 15.00 15.00 Dibutylphthalate 4.50 4.50 4.50 4.50 Toluene sulfonamide 6.00 6.00 6.00 6.00 formaldehyde resin Butyl acetate 30.00 30.00 30.00 30.00 Ethyl acetate 8.00 8.00 8.00 8.00 Toluene 26.00 26.00 26.00 26.00 Isopropanol 7.35 7.35 7.59 7.59 Bentone 27 1.00 1.00 1.00 1.00 (montmorillorite) Titanium dioxide (treated) 1.00 1.00 - Iron oxide (treated) 0.48 - 0.48 Titanium dioxide (untreated) - - 0.76 0.76 Iron oxide (untreated) - 0.48 - 0.48 Untreated organic pigments 0.67 0.67 0.67 0.67 (mixture of D & Red 7 and ferric ammonium ferrocyanide) Observation after 2 mos. - at room temp. 5 4 4 4 - at 1200F 5 3 3 3 EXAMPLE 2 Four samples of a nail enamel ("Carmel") were prepared by mixing uniformly the ingredients indicated in Table 2. The products were compared for settling and migration after holding for two months without agitation, at room temperature or at 1200 C. Table 2 Sanple No.: 1 2 3 4 r Nitrocellulose 15.00 15.00 15.00 15.00 Dibutylphthalate 4.50 4.50 4.50 4.50 Toluene sulfonamide 6.00 6.00 6.00 6.00 formaldehyde resin Butyl acetate 30.00 30.00 30.00 30.00 Ethyl acetate 8.00 8.00 8.00 8.00 Toluene 26.00 26.00 26.00 26.00 Isopropanol 8.327 8.327 9.517 9.517 Bentone 27 1.00 1.00 1.00 1.00 (montmorillorite) Titanium dioxide (treated) 0.79 0.79 Iron oxide (treated) 0.35 - 0.35 Titanium dioxide (untreated) - - 0.60 0.60 Iron oxide (untreated) - 0.35 - 0.35 Untreated organic pigments 0.033 0.033 0.033 0.033 (mixture of D & Yellow 5, D & Red 6, and ferric ammonium ferrocyanide) Observation after 2 ines. - at room temp. 5 4 4 4 at 1200 F 5 3 3 3 The observations in Tables 1 and 2 indicate that nail enamels in which all inorganic pigments were coated with the organopolysiloxane were superior to enamels in which some, or all, inorganic pigments were not so coated.

Claims: WHAT IS CLAIMED IS: 1. In a nail enamel which contains inorganic pigment, the improvement wherein said inorganic pigment has a coating consisting of a poly(organosiloxane) wherein said improved enamel is substantially free from settling and migration of the pigment contained therein. 2. In the manufacture of a nail enamel which contains inorganic pigment, the improvement comprising using as inorganic pigment which has a coating consisting of a poly(organosiloxane) wherein said enamel is thereby rendered substantially free from settling and migration of said inorganic pigment. 3. An improved nail enamel made by the process of Claim 2. 4. The nail enamel of Claim 1 wherein said coated pigment comprises up to about 1C wt. % of the nail enamel. 5. The nail enamel of Claim 1 wherein said coated pigment comprises up to about 2 wt. % of the nail enamel.

Inventors: CASTROGIOVANNI, ANTHONY, ISMAILER, ANATOLY A., SOCCI, ROBERT L.
Applicants: REVLON, INC.
Application year: 1984
Main classification: A61K7
IPC codes: C08L83, A61Q1, A61Q3, A61K8