ELECTRON-BEAM AND X-RAY SENSITIVE POLYMERS AND RESISTS

Abstract: There are disclosed polymers, E-beam sensitive ele­ ments and resists obtained therefrom, that are at least as sensitive as 5 x 10⁻⁷ coulombs per cm² when exposed to a 15 keV electron beam. The polymers are copolymers of either allyl or propargyl methacrylate and of an acrylate or methacrylate bearing an oxygen-containing heterocyclic ring.

Description: ELECTRON -BEAM AND X-SY SENSITIVE POLYMERS AND RESISTS This invention relates to negative-working polymers suitable for exposure to electron beams or X-rays to form a resist image. Electron-beam resists are at the forefront of the manufacture of integrated circuits because they permit the formation of smaller images than do resists which are responsive only to light radiation. It is desirable that such electron-beam resists have a mInimum sensitivity of 5 x coulombs/cm2 when exposed to a 15 keV electron beam, and have a resistance to deformation by the developer solvent and a resistance to subsequent fabrication steps, e.g., etching, ion implantation, etc. A negative-working electron-beam resist is described in U.S. Patent No. 4,289,842. That resist comprises, in certain embodiments, copolymers of allyl methacrylate. Although such a resist has been particularly useful, it has demonstrated on occasion, and for reasons that are not completely understood, a sensitivity to the environment in which it is coated. More specifically, unless steps are taken to reduce such things as the amount of humidity in the environment, this resist tends occasionally to form severe "edge scaling" (i.e., residual amounts ot unexposed polymer, resembling scales, projecting from the edges of the image after development and which are not removable). Although the problem can be overcome by controlling the environment, it would be advantageous to develop a negative-working resist of comparable quality that is not so sensitive to environmental conditions. This problem is solved with a novel negative-working polymer that is at least as sensitive as 5 x 10 7 coulombs per cm2 when ex- posed to a 15 keV electron-beam, said polymer comprising recurring A and B units having the structural formulae EMI2.1 respectively wherein R1 is -CHsCH2 or -CwCH, R2 is methyl or hydrogen, Z is a heterocyclic ring having from 3 to 6 ring atoms selected from carbon and oxygen, m = 0, 1, 2, or 3, n = 1 or 2, and r is 0 or 1, said A unit being 50 to 95 mole percent of said polymer and said B unit being 5 to 50 mole percent of said polymer. When coated in a layer on supports, the polymers of the invention are useful as electron-beam resists. The polymers of the invention are also useful as resists for exposure to other forms of high energy radiation, such as x-ray radiation. Certain polymers of the invention demonstrate both outstanding E-beam sensitivity and resistance to edge scaling under a variety of environmental conditions. As used herein, "edge scaling" refers to scales formed on resist images. For example, under certain high humidity conditions, resist poly (allyl methacrylate-co-hydroxyethyl methacrylate), having a Mw of 42,000, following exposure to a line pattern spaced 5 to 10 pm apart and development with the solvent 2-ethoxyethyl acetate/isopropyl alcohol (1:1 by volume), will show under a microscope, resist portions that look like scales projecting away from the edges of lines. The scale portions are unexposed portions of the resist polymer which not only were not developed (removed) by the solvent, but also are resistant to removal by conventional descmming procedures. Such scales are distinguishable from minor scum sometimes encountered, which is readily removable by an oxygen plasma. Tne scales are, of course, objectionable because they act as a protective resist over areas of the substrate that should not be protected from subsequent etching. The resist comprises the copolymers described above. As noted, Z is a heterocyclic ring, and as used herein, "heterocyclic ring" includes both substituted and unsubstituted heterocyclic rings, as well as saturated and unsaturated heterocyclic rings having the ring atoms that conform to the specified requirements. Preferred examples of substituents on such substituted rings include one or two alkyl groups each of from 1 to 3 carbon atoms, that is to say methyl, ethyl, propyl or isopropyl; halo, for example, chloro, fluoro, and the like; cyano; and alkoxy of from 1 to 3 carbon atoms, for example, methoxy, ethoxy, and propoxy. Particularly preferred heterocyclic rings include glycidyl; furyl; pyranyl; and 2 ,2-dimethyldioxalanyl. Particularly preferred examples of useful copolymers for this invention inc lude poly (allyl methacrylate-co-glycidyl methacrylate); poly (allyl methacrylate-co-2, 2-dimethyl-4- dioxalanylmethyl methacrylate); poly(propargyl meth acryiate-co-2,2-dimethyl-4-dioxalanylmethyl methacrylate); poly[allyl methacrylate-co(2H-2-tetrahy- dropyranyloxy)ethyl methacrylate); poly(allyl methacrylate-co-2-furfuryl methacrylate); poly(propargyl methacrylate-co-glycidyl methacrylate); and poly (allyl #ethacrylate-co-2, 2-dimethyl-4-dioxalanyl- methyl acrylate). Other comonomers can be included to form recurring units in the polymer of the invention, provided that they are compatible with the preferred comonomers (i.e., they do not interfere with the crosslinking of the polymer). Preferably, to insure maximum sensitivity and etch resistance, the A and B units together comprise at least 70 mole percent of the polymer. Other comonomers are preferably not included. It has been found that the polymers of the invention have better adhesion with high speed and good plasma etch resistance. The polymers of the invention have electron-beam sensitivities of at least 5 x 10 coulombs/cm2. Such results are achieved for weight average molecular weights (herein "M-w") that are, in most cases, below 100,000. Thus, the polymers of the invention can be used to prepare very sensitive nega- tive-working electron-beam recording resists. Electron-beam sensitivities herein described were determined, as is conventional, by exposing identical coatings to increased dosage values and measuring the amount of resist remaining in the exposed area after development. The sensitivity is that dosage required to crosslink enough of the composition to retain 5U percent of the initial coating thickness. The smaller the dosage, the less energy tat is required, and therefore the more sensitive is the polymer. Tne molecular weights of useful polymers or the invention vary widely. Preferably the polymer has a low enough viscosity in the solvent of choice to permit it to be coated. It has been found that useful viscosities are generally 0.3 inherent viscosity or less, as measured in N,N-dimethylformamide at 250C. However, very low-molecular weights tend to reduce electron-beam sensitivity. Preferably, therefore, the styrene equivalent weight average molecular weight of the polymer, as determined by gel permeation chromatography analysis, is between 10,000 and 70,000. Most preferably, it is between 25,000 and 45,000 for the dioxalanyl copolymers, 30,000 to 50,U00 for the glycidyl and furfuryl copolymers, and 25,000-55,000 for the tetrahydropyranyloxy copolymers. A further advantage of the polymers of the invention is in improved film properties of the coated polymers, such as adhesion to supports that are to be resist--coated. These properties are unexpectedly superior compared to the properties of the homopolymers that result when one of the comonomers is not present. For example, the homopolymer of allyl methacrylate demonstrates unsatisfactory adhesion to chrome-clad glass when exposed to dosages greater than 5 X 10-7 coulomb/cm2. Similarly, the homopolymer of propargyl methacrylate tends to lose adhesion when over-exposed. PolyCdioxalanyl methacrylate) also fails to adhere following image development, for the reason that it is insensitive to E-beams at the aforesaid dosage and will not crosslink to provide insoluble portions. Poly(glycidyl methacrylate), though adherent, is unstable when stored. The polymers of the invention can be prepared by conventional synthesis techniques. Dilute reaction conditions are preferred to avoid undesirable crosslinking. Examples 1 to 4 below illustrate the preparation of polymers of the invention. Example 1. Poloallyl methacrylate-co-2,2- dimethyl-4-dioxalanyimethyl methacrylate) EMI6.1 In a 5L 3-neck flask, 2.5# of 1,2dichloroethane (DOE) was heated under a nitrogen atmosphere to a mild reflux. A monomer solution was prepared containing: 100 g allyl methacrylate (0.79 mole) 56.6 g 2,2-dimethyl-4-dioxalanylmethyl methacrylate (0.26 mole) 0.87 g 2,2' -azobis (2-methylpropionitrile) (AIBN) 750 ml DOE. The monomer solution was added slowly to the stirred, refluxing DOE (over a one-hour period). Reflux was maintained for 20 hours after the addition was completed. The reaction mixture was allowed to cool, filtered, and reduced to Cla on tne rotary evaporator. The product was precipitated into lU# of vigorously stirred heptane. The precipitate was collected on a Buchner funnel, washed with fresh heptane, then dried under vacuum with a nitrogen bleed at 2000. for 48 hours. Yield: 102.4 g (65Z). (In tne allyl methacrylate polymer products herein# described, there is present some amount of polymerized cyclized allyl methacrylate monomer that does not conform to the structure noted.) Elemental Analysis NX CZ HZ GPC Mn - 18,469 Theory 0 64.3 8.0 MW s 42,641 Found < 0.3 64.2 8.0 Ratio (Mn/Mw) - 2.31 Example 2. Poly(allyl methacrylate-co-glycidyl methacrylate) EMI7.1 A 12-liter round-bottom reaction vessel equipped with magnetic stirrer, reflux condenser, pressure-equalized dropping funnel, nitrogen inlet and heating mantle was charged with 4.5 liters of DCE. The system was purged with nitrogen and reflux established. To the reaction vessel was added dropwise a solution of 200 g of allyl methacrylate (1.59 moles), 75 g of glycidyl methacrylate (0.53 mole), and 3 g of 2,2'-azobis(2-methylpropionitrile) (AIBN) (1.8 X 10-2 moles) in 1 liter of DCF, over tne period of 1/2 hour. reflux was maintained for 15 hours. One-half of the solvent was removed on a rotary evaporator and the remaining solution was added dropwise to 25 liters of vigorously stirred heptane to precipitate the polymer. The white, solid polymer was collected on a filter funnel, washed twice with 509 ml of fresh heptane, and dried in vacuum with no heat. 210 g yield, 76X. HB 34,459, ME - 14,407, Mw/N - 2.39 by gel permeation chromatography. Example 3. Preparation of PolyEallyl methacrylateco-2-(tetrahydropyran-2-yloxy)ethyl methacrylate)3 # EMI8.1 *(as described in U S. Patent 4,289,842) The starting copolymer was dissolved in 1800 ml of dry pyridine. The solution was stirred under nitrogen and warmed to reflux Dihydropyran (25.5 g, 0.30 mole) was then added and the reflux continued for 6 hour. The reaction mixture was then cooled to room temperature and filtered to remove any insoluble polymer The polymer solution was precipitated into water through an aspirator and washed completely with cold water several times. The polymer was collected and dried at 20 C. under vacuum with a nitrogen bleed for 72 hours. Yield: 94 g. Example 4. Preparation of Poly(propargyl methacrylate-co-glycidyl methacrylate EMI9.1 DCE (2.7 ±) was warmed to gentle reflux with stirring under a nitrogen atmosphere. A mono merlinitiator solution was prepared by dissolving 111.7 g (0.9 mole) of propargyl methacrylate, 42.7 g (0.3 mole) of glycidyl methacrylate and 0.77 X of w1ssN in 700 ml of DCE. reflux was continued while the monomer-initiator solution was added over a 30-minute period. Reflux continued for 16 hours and then the reaction vessel was allowed to return to 200C. The polymer solution was reduced in volume to about 1.5 X, on a rotary evaporator. The reduced solution was added dropwise to 12 X of vigorously stirred heptane. A granular white precipitate was obtained and isolated by collecting on a filter. The collected polymer was washed twice with heptane and dried at 20 C. under vacuum with a nitrogen bleed. Obtained - 50 g of white polymer (32Z) Mn - 6867, Mw - 9609, Mw/KE - 1.4 (polystyrene equivalent weights) Elemental Analysis %C %H %O Theory 65.4 6.7 28.0 Found 65.3 6.7 2b.7 As a resist, the polymers of the invention are preferably coated onto the support that is to be etched. Preferably the coating composition is free of sensitizers and initiators, to permit white-light handling. The resist is then dried, imagewise exposed, and developed to remove the unexposed portions. Any suitable support is useful. Particularly preferred examples of supports include semiconductors such as silicon wafers, chrome-clad glass, and metals such as aluminum. Conventional solvents are useful for both the coating step and the development step. Preferred examples of solvents useful for either process step include 2-methoxyethyl acetate, 2-ethoxyethyl acetate, 2-ethoxyethanol, 2-butanone, cyclohexanone, cyclopentanone, 4 butyrolactone, and mixtures of these with 2-propanol or ethanol. Conventional coating procedures are useful to apply the polymer to tne support. Preferred are whirler or spin coating, brushing, doctor-blade coating, or hopper coating. Further details of such conventional procedures are described in Product Licensing Index, Vol. 92, Dec. 1971, Publication No. 9232, at p. 109. The drying step is preferably accomplished by baking in an oven, optionally in a vacuum, for example, at 9000. for 30 minutes. Optionally, a conventional post-bake step is included after exposure and development to enhance adhesion of the final resist coating to the areas to be protected, prior to etching. Etching of the underlying support is achieved by using a chemical solvent for the support, or by treatment with a plasma gas, both of which are conventional. Examples 5 to 13 below illustrate the use of polymers of invention as resists. To demonstrate resistance to edge scaling, the polymers of Table I in 2-ethoxyethyl acetate were coated onto SiO2-coated silicon wafers at a thickness of 0.5 micron (each example). The resist polymers were imagewise exposed to an electron beam of 20 keV energy, stored at 100 percent relative humidity for about 12 hours, and developed in 1:1 (by volume) 2-ethoxyethyl acetate/isopropanol for 30 seconds. Thereafter, the samples were spin-spray rinsed with isopropanol. The resistance to edge scaling was determined by microscopic observation-see Table I. Table I Was Edge Scaling Example Polymer Present? Control Poly(allyl meth Yes acrylate-co-hydroxy ethyl methacrylate) (3:1)* 5 Poly(allyI meth- No--free of edge acrylate-co-glycidyl scaling methacrylate) (3:1) 6 Poly(allyl meth acrylate-co-2,2 dimethyl-4-dioxalanyl methyl methacrylate) (3:1) 7 Poly(propargyl meth acrylate-co-2,2 d imethyl-4-dioxalanyl- methyl methacrylate) (3:1) 8 PolyEallyl meth- II acrylate-co-2 (2tt-2-tetrahydro- pyranyloxy)ethyl methacrylatej (3:1) 9 Poly(allyl meth acrylate-co furfuryl meth acrylate) (3:1) * All ratios of this table are expressed in terms of the mole ratios of the comonomers incorporated into the polymer. Examples 5 to 9 were repeated, and these coated wafers were exposed at 15 keV to determine their sensitivity. Sensitivity curves were plotted, and the contrast was determined as the slope of the sensitiv- ity curve at the 50 percent thickness point. A Comparative Example was prepared by the procedure of Example 5, except that the polymer was poly(allyl methacrylate-co-4-methyl-2H-2-pyranon-6-ylmethyl methacrylate at a My of 30,700. (See British Patent Pub. 1,446,981.) Tne results appear in Table II. Table II Sensitivity (Coulombs/ Ex. Polymer Mw cm2) Contrast 5 Poly(allyl meth- 34,500 3.4 X 19-7 1.1 acrylate-co-glycidyl methacrylate) 6 Poly(allyl meth- 38,400 3.5 X 10-7 1.2 acrylate-co-2,2 dimethyl-4-dioxalany 1 methyl methacrylate) 7 Poly(propargyl meth- 10,400 2.2 X 10-7 1.0 acrylate-co-2,2 d imethyl-4-dioxalany 1 methyl methacrylate) 8 Polytallyl meth- 42,000 2 X 10-7 0.94 acrylate-co-2 (2H-2-tetrahydro pyranyloxy)ethyl methacrylate J 9 Poly(allyl meth- 62,400 5.0 X 10'1 0.85 acrylate-co-2 furfuryl meth acrylate) Com. acrylate) ----------- N.A. 6.0 X 10-7 1.1 Ex. (not available) The value of 6.0 X 1cur' of the comparative example, by reason of the larger exposure required as indicated by the larger number, is not as sensitive as the values < 5 X 1cur' provided by the polymers of the invention, and was considered unacceptable. Examples 10-12 Examples 5, 6 and 8 were repeated as Examples 10-12, and following development, the samples were etched with a plasma etch of 91.5Z CF4 and 8.5X 02, applied at 100 w, 0.7 Torr pressure. As controls, two separate layers of poly(methyl methacrylate) and a commercial copolymer of glycidylmethacrylate and ethyl acrylate, available under tne trademark "±TI/MEAD COP" from KTI Chemicals, Inc., were similarly coated, exposed, developed and etched. Examples 10-12 demonstrated greater etch resistance than did the two controls. Example 13 Poly(allyl methacrylate-co-2, 2-dimethyl-4- dioxalanylmethyl acrylate), having a mole ratio of 3:1 for the comonomers incorporated into the polymer, was coated onto a chrome-clad glass, exposed to a 15 KeV electron beam, and developed for 1 minute with a 1:1 mixture of 2-ethoxyethyl acetate and ethanol. The sensitivity and contrast were found to be 4.1 X 10-7 coulombs/cm2 and 1.22, respectively.

Claims: CLAIMS: 1. A negative-working polymer that is at least as sensitive as 5 x coulombs per cmê when exposed to a 15 KeV electronbeam, said polymer comprising recurring A and B units having the structural formulae EMI15.1 ,respectively wherein R1 is -CH-CH2 or -CwCH, R2 is methyl or hydrogen, Z is a heterocyclic ring having from 3 to 6 ring atoms selected from carbon and oxygen, m is 0, 1, 2, or 3, n is 1 or 2, and r is 0 or 1, said A unit being 50 to 95 mole percent of said polymer and said B unit being 5 to 50 mole percent of said polymer. 2. A polymer according to Claim 1 wherein said A and B units form a poly(allyl methacrylate-coglycidyl methacrylate). 3. A polymer according to Claim 1 wherein said A and B units form a poly(allyl methacrylate-co2,2-dimethyl-4-dioxalanylmethyl methacrylate). 4. A polymer according to Claim 1 wherein said A and B units form a poly(propargyl meth acrylate-co-2 ,2-dimethyl-4-dioxalanylmethyl methacrylate). 5. A polymer according to Claim 1 wherein said A and B units form a poly [ allyl methacrylate-co (2H-2-tetrahydropyranyloxy)ethyl methacrylate). 6. A polymer according to Claim 1 wherein said A and B units form a poly(allyl metbacrylate-co- 2-furfuryl methacrylate). 7. A polymer according to Claim 1 wherein said A and B units form a poly(propargyl methacrylate-co-glycidyl methacrylate). 8. A polymer according to Claim 1 wherein said A and B units form a poly(allyl methacrylate-co2,2-dimethyl-4-dioxalanylmethyl acrylate). 9. A polymer as in Claim 1 having a weight average molecular weight below 100,000. 10. A polymer as in Claim 1 wherein the A and B units constitute at least 70 percent of sai#d polymer. 11. An E-beam or x-ray sensitive element comprising a support having thereon a layer of a polymer as defined in any of Claims 1 to 8.

Inventors: DALY, ROBERT CURTIS, TAN, ZOILO CHEN-HO
Applicants: EASTMAN KODAK COMPANY
Application year: 1984
Main classification: G03F7
IPC codes: C08F20, C08F220, G03F7