SYNTHESIS OF POLYURETHANE PRODUCTS

Abstract: Wide range of polyurethane products, e.g., cellular, dense elastomer, and integral skin microcellular products, obtained by the reaction of (a) a polyisocyanate compound, (b) a polyol, (c) optionally a chain extender and/or blowing agent with/without other known additives, (d) in the presence of a nonhydroxyl flow modifier characterized by carbon and hydrogen atoms, at least one and, generally, a plurality of oxyalkylene groups, and at least one urethane, <SIGN> group. Several of the polyurethane products exhibit unique properties, e.g., foamed articles with capability to conduct static electricity, soft elastomers characterized by improved coefficient of friction, etc. Several classes of the flow modifiers are novel per se. The polyurethane products can be synthesized via the one shot or prepolymer process. Multipackage systems, in particular, two and three component systems are useful in molding operations, e.g., manufacture of shoe soles.

Description: SYNTHESIS OF POLYURETHANE PRODUCTS BACKGROUND OF THE INVENTION This invention relates to the synthesis of poly¬ urethane products obtained by the reaction of form- ulation(s) comprising polyol, polyisocyanate, and chain extender, in the presence of a flow modifier which is characterized by at least one urethane group, i.e., 0 a -NHCO-. The reactants of choice such, as in a two package system, e.g., the isocyanate materials in one package and the materials forming the second package, e.g., polyol- (polyester polyol or polyether polyol), chain extender, blowing agents (organic and/or H2O) , cell regulation agent, etc., which may comprise this isocyanate-curable second package, can influence the kind of polyurethane product obtained as well as its over-all properties. Thus the polyurethane product can be, for instance, a dense elastomer or an integral skin microcellular elastomer or open cellular product and the like. Plasticizers are widely used in polymer arts such as with polyvinyl chloride, chloroprene resins, acrylics, polyvinyl butyral, nitrile rubber, polyreuthanes, cellu- losic products, and others. The plasticizer should be compatible with and not "sweat out" from the plasticized resin. Desirably the plasticizer should act as a process¬ ing aid during the formation of the resin or ultimate resinous article. The plasticizer should achieve the goals which dictated its use in the first place without detracting from the properties of the unplasticized resin. SUMMARY OF THE INVENTION It has now been found that there can be prepared a wide variety of novel non-hydroxyl flow modifiers which are useful in the manufacture of improved polyurethane articles. It has also been found that there can be pre¬ pared novel blends comprising flow modifiers described hereinafter and polyols which are compatible liquids at room temperature or, if not initially compatible liquids, can be made so by heating and thereafter cooling to room temperature. The non-hydroxyl flow modifier can be employed in NCO/OH polyaddition reactions to prepare a wide variety of polyurethane products such as adhesives, foams and elastomers. In the practice of desirable embodiments of the invention, formulations comprising flow modifier, isocyanate compound, polyol, chain extender, and other urethane-for ing ingredients have been found to be extremely useful and, indeed preferred for the preparation of homogeneous and cellular polyurethane products, especially microcellular products such as, for example, integral skin microcellular polyurethanes. Such products exhibit a broad spectrum of highly desirable and/or improved characteristics. For instance, integral skin microcellular urethane articles, e.g., shoe soles, can be obtained which are characterized by a resilient core of substantially uniform density and an integrally formed, tough, substantially continuous surface skin surrounding said core, the boundary between said skin and said core being characterized by a rather abrupt change in density. The skin is itself flexible, essentially devoid of blemishes, impervious to oil and water, directly accepts paint without first requiring primers to its surface, and exhibits good flex life, high tear strength, and generally superior abrasion resistance. Accordingly, it is an object of this invention to synthesize polyurethane products from formulations containing at least one non-hydroxyl flow modifier which is characterized by at least one urethane group, i.e., O II -NHCO-. Another object of the invention is to provide novel compatible homogeneous liquid mixtures containing polyol and flow modifier which are isocyanate curable to yield improved polyurethane products, especially micro¬ cellular products including integral skin microcellular articles, flexible polyester and polyether urethane foams, and solid elastomers. A further object of the invention pertains to novel flow modifiers per se and to the processes for their preparation. A still further object of the invention relates to single and multipackage systems in which the single package or Component (A), an isocyanate curable system, comprises the polyol and chain extender reactants and at least one flow modifier, whereas the multipackage system includes Component (A) above and Component (B) which contains a polyisocyanate reactant. These and other objects of the invention will become apparent to those skilled in the art from a consideration of this specification. DETAILED DESCRIPTION OF THE INVENTION The non-hydroxyl flow modifiers which are contemplated in the preparation of polyurethane products have a boiling point above about 150°C and are normally- liquid, i.e., liquid at about room temperature, or are relatively low melting solids which form with the poly¬ isocyanate compounds or the polyols compatible liquid mixtures at room temperature or at the temperature of use. The flow modifier consists essentially of (a) carbon and hydrogen atoms preferably in the form of a monovalent and/or polyvalent hydrocarbon groups such as a Cι-Ci8~ acyclic group, a Cs-Cycycloaliphatic group including the mono and poly C].-C4alkyl substituted counterparts thereof and/or a benzenoid ring nucleus, e.g., mono-, fused-, and bridged nuclei, including the partially or fully hydro- genated ring nuclei and the unsubstituted- and mono and poly Cj.-C4alkyl substituted- counterparts thereof; (b) etheric oxygen in the form of oxyalkylene group(s), and optionally, also in the form of alkoxy, cycloalkoxy, and 0 aryloxy; and (c) at least one urethane group -NHC0-, and upwards to five such groups, preferably 2-3 such groups, each of the monovalent bonds of the urethane group being monovalently attached to separate carbon atoms of the flow modifier molecule. The term "oxyalkylene", as used here¬ in, characterizes an oxy atom bonded to an acyclic or alicyclic carbon atom to form, as by way of illustrations, the unit -0CH 2 CH 2 -, -OCH2CH- , and -CH CH-O- CH3 \ / N (CH 2 )d wherein d_ is an integer of from 3 to 6. Illustrative di¬ valent oxyalkylene groups include oxyethylene, oxy- propylene, oxytrimethylene, oxytetramethylene, chloro- methyl-substituted oxyethylene, phenyl-substituted oxy¬ ethylene, dimethyl-substituted oxyethylene, cyclohexylene- oxy cyclopentyleneoxy, and methyl-substituted cyclo- hexyleneoxy; the mixed oxyalkylenes of the above such as oxyethyleneoxypropylene, oxvethyleneoxybutylene, and oxy- propyleneoxybutylene; mixed oxyalkylenes which contain minor amounts of oxymethylene groups and the random and block oxyalkylenes of the foregoing; and the like. The flow modifiers contemplated in the practice of various embodiments of the invention are characterized by at least one oxyalkylene group and upwards to 25, and more, of such groups per urethane group, as shown in Formula I infra. The terminal oxyalkylene group is "capped" by a monovalent hydrocarbon group such as a C l-Cl7acγclic hy d rocarbon group, desirably a Ci-Csalkyl group. In various embodi¬ ments of the invention a suitable upper limit is eight OMPI oxyalkylene groups. Preferred flow modifiers are characterized by oxyethylene or oxypropylene group(s) or mixtures of such groups with/without minor amounts of other oxyalkylene group(s). The average molecular weight of the flow modifiers which are employed in the preparation of the novel poly¬ urethane products can vary over a wide range, e.g., upwards to a few thousand, e.g., approximately 3000. Ir 2 flow modifier, as noted previously, is a normally-liquid material or a relatively low melting solid, and forms a compatible liquid with the polyisocyanate reactant and/or polyol reactant at room temperature or at the temperature of use (in the formation of polyurethane products). Desirable flow modifiers are those which are prepared from readily available and relatively inexpensive starting materials, e.g., 2,4- 2,6-tolylene diisoσyanate , methoxy- ethanol, butoxyethanol, methyl Carbitol, butyl Carbitol, and the like. Thus flow modifiers having molecular weights of at least about 250-500 are particularly useful, though lower molecular weights are contemplated. The flow modifiers are characterized by the absence of groups which are normally reactive with an isocyanato group (-NC0) at typical storage and shipping temperatures such as hydroxyl , carboxyl, thiol , primary amino, secondary amino, and the like. In one embodiment flow modifiers which are suitable in the practice of the invention(s) are shown structurally in Formula I infra. wherein the oxyalkylene group generally contains from 2 to 4 carbon atoms in the oxyalkylene chain; wherein each R individually represents a monovalent acyclic, alicyclic or aromatic group; wherein x is at least one and upwards to 25, and more, but generally 1 to 8; wherein ^ is from 1 to 5, preferably 2 to 3; and wherein R represents a mono¬ valent acyclic, alicyclic or aromatic group when is 1 or a polyvalent acyclic, alicyclic or aromatic group when z_ is 2 to 5, the valence of ^2 being equal to the value of z ^ . The maximum average number of oxyC2*-C3alkylene units in the flow modifier of choice is realistically governed by the restriction that the flow modifier employed in the practice of the invention is a liquid or a relatively low melting solid which at room temperature or at the temperature of use forms a compatible stable liquid with the polyisocyanate and/or polyol reactant(s). Illustrative Jl groups include straight and branched alkyls, aralkyls, cycloalkyls, and the aryls (mono-, fused-, and bridged- aryls, and the partially hydrogenated aryls) such as methyl, ethyl, n-butyl, isobutyl, 2-ethyl- hexyl, lauryl, stearyl, oleyl, phenethyl, phenylpropyl, phenyl, tolyl, xylyl, benzyl, cyclopentyl, methylcyclo- hexyl, cyclohexyl, cyclohexyl ethyl, cycloheptyl, and cyclohexenyl. Illustrative R2 groups include alkyl, cycloalkyl, and the aryls illustrated previously as well as the corresponding higher polyvalent acyclic, alicyclic and aromatic groups, e.g., alkylene, cycloalkylene, arylene, and the like. Examples of R2 groups include methyl, ethyl, n-butyl, phenethyl, 3-methoxyhexyl, xylyl, phenyl, mesityl, tolyl, indenyl, 2-methoxyphenyl, 4-bi- phenylyl, naphthyl, cyclohexyl, cyclopentyl, methylcyclo- hexyl, cycloheptyl, 1,4-butylene, 1,6-hexamethylene, cyclopentylene, cyclohexylene, cyclohexenylene, phenylene, 1,5-naphthylene, l-methoxy-2,4-phenylene, l-chloro-2,4- phenylene, hexahydronaphthylene, 4,4'-dicyclohexylene- methane, l-propoxy-2,4-phenylene, xylylene, and tolylene. It is preferred that the foregoing acyclic groups contain no more than 17 carbon atoms (most preferably, no more than 10 carbon atoms), that the alicyclic groups contain from 5 to 7 carbon atoms in the ring nucleus and up to 2 OMPI carbon atoms in any substituent bonded to the ring nucleus, and that the aromatic groups contain up to 12 carbon atoms and one or two benzenoid nucleus, and that equals 2. A particularly preferred subclass of flow modifiers is shown in Formula IA below: IA wherein each R' individually is Ci-Csal yl, C5-C7cyclo- alkyl, methyl- or ethyl-substituted Cs-C cycloalkyl, or aryl-C ] _-C3alkyl; wherein A represents C^-Cgalkylene, cyclohexylene, Cι-C2 lkyl- or Cχ-C2alkoxy-substituted cyclohexylene, unsubstituted, Cχ-C3alkyl-, or Cχ-C3alkoxy- substituted phenylene (preferably tolylene), or divalent (4,4'- and 4,4*-/4,2*-)diphenylenemethane, or the divalent hydrogenated counterparts of the foregoing; wherein x , is at least one and upwards to 25, and more, preferably 1 to 4; and wherein the oxyC ? C-^alkylene unit is oxyethylene, oxypropylene, and mixed and/or block oxyethyleneoxy- propylene unit(s), and mixtures of the foregoing. The flow modifiers of Formulas I and IA are readily prepared by reacting monohydroxyl-terminated oxyalkylene compounds, e.g., R—{-oxyalkylene,-χ—OH, with organic mono- or polyisocyanate compounds using an amount of the mono- hydroxyl compound sufficient to react with all the NCO groups present in the isocyanate compound. The mono¬ hydroxyl-terminated oxyalkylene compounds can be prepared by reacting a monofunctional initiator which contains an active hydrogen atom with an epoxide compound, the preferred initiator being a monohydric alcohol or a phenol and the preferred epoxide compound being the alkylene oxides such as ethylene oxide, propylene oxide, and mixtures thereof, in the presence of a base catalyst. Prior to reacting the resulting monohydroxyl-terminated polyether product with the isocyanate, it is preferred to remove the basic catalyst. These reactions are well documented in the art. Illustrative mono- and polyisocyanates which can be employed in the OH/NCO reaction to form the flow modifiers of Formulas I and IA include aliphatic, alicyclic and aromatic isocyanates, such as phenyl isocyanate, the alkyl isocyanates such as butyl isocyanate; the polymethylene diisocyanates such as hexamethylene diisocyanate; and the aromatic diisocyanates such as 2,4-/2,6-isomers of tolylene diisocyanate, 4,4 f -diphenylmethane diisocyanate, 4,4 '-dicyclohexylmethane diisocyanate. Others are described, for example, in the text by W. Siefken and Justus Liebigs Annalen der Chemie, 562, pages 75 to 136. In another embodiment flow modifiers which can be employed are depicted in Formula II infra; II wherein R, x , and oxyalkylene have the meanings or values assigned in Formula I supra, wherein Rτ_ is a polyvalent (generally a di-, tri- or tetravalent) acyclic, alicyclic, or aromatic group having the broad and preferred meanings assigned to polyvalent R of Formula I supra, the valence of Rτ_ being equal to plus _, wherein each R^ individually is an acyclic, alicyclic or aromatic group, e.g., straight and branched alkyl, cycloalkyl, aryl, etc., as illustrated in Formula I with respect to the R group, wherein j_ has a value of 1 to 2, preferably one, and wherein c has a value of 1 to 2. O PI A preferred subclass of flow modifiers within the scope of Formula II are shown structurally in Formula IIA below: IIA o o II It RJ oxyC2-C 3 alkyleneτ-χ OCHN-A-NHCOR' wherein R_]_, A, x and oxyC 6 -C* 3 alkylene have the meanings or values assigned in Formula IA supra. The flow modifiers of Formulas II and IIA can be prepared by reacting monohydroxyl-terminated oxyalkylene compounds, e.g., R (oxyalkylene) x OH, with an organic polyisocyanate having 2 to 4 ' -NCO groups, preferably 2 to 3 -NCO groups, such as those illustrated previously, at a 1:1 molar ratio of polyisocyanate to monohydroxyl compound, to form O II R .oxyalkylene• " -* OCNH—R. £NCO) y which in turn is reacted with an excess of a monohydric alcohol or a phenol, or an admixture of same with R (oxyalkylene) x OH, to form the products of Formula II supra. Excess monohydric or phenolic compound can be removed via distillation or other means known to the art. Accordingly, various aspects of the invention are to provide novel formulations and novel processes to prepare highly useful and improved polyurethane products. Such formulations comprise polyol, chain extenders, organic polyisocyanates, and at least one flow modifier. The invention contemplates the "one shot" process and the stepwise or prepolymer processes, including the total prepolymer process and the "quasi-prepolymer" process, wherein only a portion of the polyol is reacted stepwise with the polyisocyanate. The quasi-prepolymer process is the most suitable and preferred in the production of improved microcellular products contemplated by the invention. The one-shot process is the preferred process in the manufacture of flexible polyester and polyether polyurethane foams. For the preparation of solid elastomers, the prepolymer process is normally preferred. In this case it is highly preferable to combine the chain extender with the flow modifier as a separate stream. Improved cellular polyurethane products, especially micro¬ cellular products including integral skin microcellular articles and flexible foams, can be obtained by using blowing agents as well as other known polyurethane-forming or polyurethane-aiding ingredients, as desired. Among the polyisocyanates suitable in the preparation of such useful polyurethane products include the acyclic, alicyclic and aromatic polyisocyanates, mixtures of these polyisocyanates and their carbodiimide ' derivatives, and in particular polyester and polyether prepolymers of these polyisocyanates. Mixtures of these prepolymers with di¬ isocyanates per se and with their carbodiimides are also contemplated. Illustrative of the diisocyanates include 1,4-tetramethylene diisocyanate, 1,6-hexamethylene diiso¬ cyanate, isophorone diisocyanate the urea derivative of this isocyanate [OCN(CN2)δNHCO H(CH2)6 N CO] , cis and trans isomers of methylene bis-(cyclohexyl isocyanate), 4,4'- benzidine diisocyanate, 3,3'-dimethyl-4,4'-benzidine di¬ isocyanate, p-phenylene diisocyanate, 2,4/2,6-isomers of tolylene di-isocyanate, 1,5-naphthylene diisocyanate, 4,4'-diphenylmethane diisocyanate, 4,4'-diphenylmethane diisocyanate containing up to 25%, or more, of the 2,4'- and 2,2'-iso er, a mixture of 4,4'-diphenylmethane di¬ isocyanate and the carbodiimide thereof such as Isonate 143-L (available from The Upjohn Company; U.S. 3,492,330), and mixtures of the above. The methods for the preparation of the above-described polyisocyanates and a more comprehensive listing of polyisocyanates is presented by . Siefken, in Justus Liebigs Annalen der Chemie, Volume 562, Pages 75-136. Isocyanato-terminated prepolymers suitable in the practice of the invention are prepared by reacting a poly¬ ester polyol or polyether polyol described hereinafter with a polyisocyanate compound, e.g., acyclic, alicyclic and aromatic polyisocyanates. Especially suitable poly¬ isocyanates for this purpose include mixtures of 2,4- and 2,6-tolylene diisocyanates, and polyisocyanate compounds characterized by methylene groups (-CH2-), each valence of which is separately bonded to a carbon atom of a benzenoid nucleus such as a diphenylraethane diisocyanate (MDI), for example, 4,4'-diphenylmethane diisocyanate, 2,4'-diphenyl- methane diisocyanate, mixtures of 4,4'-MDI and 2,4'-MDI, a mixture of 4,4'-MDI and the carbodiimide thereof such as Isonate 143-L, mixtures of 4,4'-MDI and minor amount of the 2,4'- and 2,2'-MDI isomers, and the like. The iso¬ cyanate compound and polyol are reacted in a ratio of NCO groups to OH group of at least about 2.5:1, but a more suitable range of NCO equivalents per OH equivalent is from about 2.7 to about 24 (NCO) to one (OH). A NCO/OH ratio in the range of from about 3.7:1 to about 12:1 is preferred with a most preferred ratio being from about 7 to about 12 NCO equivalents per one OH equivalent. Polyols useful in the preparation of a wide variety of polyurethane products have molecular weights in the range of from about 1800 to about 10,000 and preferably in the range from 2000 to 5000. Polyethers containing at least 2 and preferably 2 to 3 hydroxyl groups are suitable for use in the invention, are known, and are obtained, for example, by the polymerization of epoxides, such as ethylene oxide, propylene oxide, butylene oxide, tetra- hydrofuran, styrene oxide or epichlorohyd in alone, for example in the presence of BF3, or by the chemical addition of these epoxides, optionally in admixture with or in succession to starter components having reactive hydrogen atoms. Such starter compounds include water, alcohols, or amines, such as ethylene glycol, 1,3- or 1,2- propylene glycol, trimethylolpropane, 4,4'-dihydroxy- diphenylpropane, aniline, ammonia, ethanolamine and ethylenediamine. In many cases, it is preferred to use polyethers of the kind which contain predominant amounts of primary hydroxyl (-OH) groups (up to 90% by weight, based on all the hydroxy groups present in the poly¬ ether) . Polyethers modified by vinyl polymers of the type obtained by the polymerization of styrene and/or acrylo¬ nitrile in the presence of polyethers (U.S. Pat. Nos. 3,383,351; 3,304,273; 3,523,093; 3,110,695; German Pat. No. 1,152,536) are also suitable, as are polybutadienes containing hydroxyl groups. Polyesters, polythioethers, polyacetals, poly¬ carbonates, and polyesteramides containing hydroxyl groups of the type commonly used for the production of homo¬ geneous and cellular polyurethanes, may also be used in appropriate proportions. Examples of suitable polyesters containing hydroxyl groups are reaction products of poly- hydric (preferably dihydric and, optionally, trihydric) alcohols with polybasic (preferably dibasic carboxylic acids). Instead of free polycarboxylic acids, the corresponding polycarboxylic acid anhydrides or corresponding polycarboxylic acid esters of lower alcohols or mixtures thereof may also be used for the production of the polyesters. The polycarboxylic acids may be aliphatic, cycloaliphatic, aromatic and/or heterocyclic, and may optionally be substituted, for example, by halogen atoms, and/or may be unsaturated. These polycarboxylic OMPI acids include succinic acid, adipic acid, suberic acid, azelaic acid, sebacic acid, phthalic acid, isophthalic acid, trimellitic acid, phthalic acid anhydride, tetra- hydrophthalic acid anhydride, hexahydrophthalic acid anhy¬ dride, tetrachlorophthalic acid anhydride, endomethylene tetrahydrophthalic acid anhydride, glutaric acid anhy¬ dride, maleic acid, maleic acid anhydride, fumaric acid, dimeric and trimeric fatty acids such as oleic acid, optionally in admixture with monomeric fatty acids, tere- phthalic acid dimethyl ester and terephthalic acid-bis- glycol ester. Suitable polyhydric alcohols include ethylene glycol, 1,2- and 1,3-propylene glycol, 1,4- and 2,3-butylene glycol, 1,6-hexanediol, 1,8-octanediol, neo- pentyl glycol, cyclohexanedimethanol (1,4-bis-hydroxy- methylcyclohexane) , 2-methyl-l,3-propanediol, glycerol, trimethylolpropane, 1,2,6-hexanetriol, 1,2,4-butanetriol, trimethylolethane, pentaerythritol, quinitol, mannitol and sorbitol, methyl glycoside, diethylene gl_col, triethylene glycol, tetraethylene glycol, polyethylene glycols, di- propylene glycol, polypropylene glycols, dibutylene glycol and polybutylene glycols. The polyesters may contain terminal carboxyl groups. Polyesters of lactones such as 6 -caprolactone or hydroxycarboxylic acids such as _. - hydroxycaproic acid, may also be used. Particular examples of polythioethers are the condensation products of thiodiglycol with itself and/or with other glycols, dicarboxylic acids, formaldehyde, aminocarboxylic acids or amino alcohols. Depending upon the co-components, these products are polythio mixed ethers, polythioether esters or polythioether ester amides. Suitable polyacetals include those compounds which can be obtained from glycols, such as diethylene glycol, triethylene glycol, 4,4'-dioxethoxydiphenyldimethyl- methane, hexanediol and formaldehyde. Other suitable polyacetals may be obtained by polymerizing cyclic acetals. Suitable polycarbonates containing hydroxyl groups are those known per se. They are obtained for example, by reacting diols such as 1,4-propanediol, 1,4-butanediol and/or 1,6-hexanediol, diethylene glycol, triethylene glycol, tetraethylene glycol; with diaryl carbonates such as diphenyl carbonate or phosgene. Examples of the polyester amides and polyamides are the predominantly linear condensates obtained from poly- hydric saturated and unsaturated amino alcohols, diamines, polyamines, and mixtures thereof. Examples of these compounds are known and are described in High Polymers, Vol. XVI, "Polyurethanes, Chemistry and Technology:, by Saunders-Frisch, Inter- science Publishers, New York-London, Vol. I (1962), pages 32-42 and pages 44-54, and Vol. II (1964), pages 5-6 and pages 198-199 and in Kunststoff-Handbuch, Vol. Ill, Vieweg-Hochtlen, Carl-Hanser-Verlag, Munich (1966) on pages 45-71. The flow modifiers may also be admixed with a wide variety of polyols illustrated herein with/without other ingredients normally used in the formation of polyurethane products to form novel compatible liquid blends at room temperature or at the temperature of use. Accordingly, desirable aspects of the invention are directed to such novel blends in which there can be included the flow modifier in the "polyol resin" side, e.g., polyol, chain extender, with/without blowing agent, and other typical urethane ingredients. Flow modifiers of the present invention which perform well in the manufacture of poly¬ urethane articles, especially in the manufacture of micro¬ cellular parts such as normal polyurethane shoe soles or integral skin shoe soles having a lower density micro¬ cellular core, flexible polyether and polyester poly¬ urethane foams possessing the ability to conduct stati electricity, and solid polyurethane elastomers character¬ ized by relatively low hardness and high coefficient of friction, have generally been observed to form soluble, compatible homogeneous liquid mixtures with the polyol or with polyol/chain extender blends. Such chain extenders are illustrated by glycols, amino alcohols, diamines and water, as well as mixtures of these extenders. In general, the flow modifiers can decrease the viscosity of the polyol reactant mixture, a highly desirable aspect for low temperature processing on polyurethane machinery. Their inclusion with the urethane-forming ingredients also improves the flow of materials, slows down the gel-formation of the polymer, thus bringing about capability to obtain exacting molded products, e.g., shoe soles, vehicle tires, integral-skin parts for automotive applications such as arm rests, instrument panels, and the like, from mold cavities of intricate pattern and design. When the flow modifier is included with the polyether or polyester polyol, or polyol-extender blend, to form compatible homogeneous liquid mixtures, the concentration of the flow modifiers can be in the range of from about 5 parts to as high as 50 parts and higher of flow modifier per 100 parts of polyol. The amount of flow modifier utilized is generally dictated, among other considerations, by its upper limit of compatibility with the resulting polyurethane product. Such compatibility depends upon many variables such as composition of the polyol backbone, the nature of the polyisocyanate and chain extender, and of course upon the chemical composition of the flow modifier contemplated in the present invention. By way of illustrations, for the manufacture of microcellular polyurethane products including integral skin microcellular elastomers for use such as shoe soles, suitable proportions of flow modifier generally range from about 5 to 35 parts, desirably from OMPI [ λ , WIPO .Λ>J about 10 to 30 parts, per 100 parts of polyol. In the manufacture of foams having the capability to conduct static electricity, flow modifier levels of from about 20 to 50 parts per 100 parts of polyol are generally suit¬ able. In the manufacture of soft elastomers (micro¬ cellular and/or solid), e.g., approximately 50 to 60 Shore A hardness, exhibiting improved coefficient of friction, the use of about 5 to 20 parts of flow modifier per 100 parts of polyol is generally desirable. One or more than one flow modifier can be employed in the practice of the inventions. Chain extenders which are especially useful in the invention are the glycols, amino alcohols, diamines and water. Typical glycols are illustrated by the alkanediols of the formula HO (-CH2 τιOH, wherein n is 2 to 10 or more, e.g., ethylene glycol, 1,3-propanediol, 1,4-butane- diol, 1,5-pentanediol, 1,6-hexanediol, 1,10-decanediol, and the like. Other glycols that are suitable include diethylene glycol-, thiodiglycol, triethylene glycol, tetraethylene glycol, p-xylylenediol, quinitol, neo- pentylene glycol, dihydroxyethylhydroquinone, and mixtures thereof, and the like. It is also possible to use glycols characterized by hetero atoms such as nitrogen and/or sulfur; double bonds; and bromine or other halogen atoms. These include N-methyldiethanolamine, N-t-butyldiethanol- amine, di-beta-hydroxyethylaniline, triethanolamine, tri- isopropanolamine, di-beta-hydroxyethyl sulfide, 2-butene- 1,4-diol, 2,3-dibromo-l,4-butanediol, di-beta-hydroxy- ethylurea, and di-beta-hydroxyethyl urethane. Suitable triol chain extenders further include glycerol, trimethylolpropane, 1,2,6-hexanetriol, and the like. Short chain glycol extenders such as ethylene glycol, 1,4-butanediol, 1,6-hexanediol, di-beta-hydroxy¬ ethylaniline and mixtures thereof are preferred. Suitable amino alcohol and polyamine chain extenders include ethanolamine, p-hydroxyethylaniline, ethylenedi- amine, 1,6-hexanediamine, 4,4'-diphenylmethane diamine, methylene-bis-(o-chloroaniline) , 3,3'-dichloro-4,4'- benzidine, perethylated 2,4- and 2,6-tolylenediamines, 1,4-cyclohexylenediamine, m-xylylenediamine, piperazine, hydrazine, N,N'-dimethylhydrazine, diethylenetriamine, and the like. For the manufacture of foams, water and poly¬ carboxylic acids, and the like may be used as chain extenders. For flexible polyurethane foams, water is highly preferred. Cellular products, in particular, microcellular products including integral skin microcellular poly- urethanes can be prepared by using well-known blowing agents. The choice of the blowing agent(s) is signifi¬ cantly influenced by the polyol reactant employed and the type of cellular polyurethane product desired. Thus, the use of water as the blowing agent in a formulation containing a polyether polyol and prepolymer (from poly¬ ether polyol and MDI) in the presence of the flow modifier will yield an open cell foamed product whereas the use of an organic blowing agent with/without a small amount of water in a formulation comprising polyester polyol, glycol chain extender, and prepolymer (derived from polyester polyol and MDI) in the presence of the flow modifier, in a closed mold system, results in an improved integral skin microcellular polyurethane product. Illustrative blowing agents include water, the halogenated hydrocarbons, in particular fluorocarbons such as trichlorofluoromethane, 1,1-difluoro-l-chloro-2-fluoro-2-dichloro-ethane, difluorodichloromethane, and mixtures of the same and the like halogenated hydrocarbons. It is also feasible to use mixtures of low boiling hydrocarbons, ethers, and ketones with halogenated hydrocarbons. Additional blowing agents are well known in the art. Flexible polyurethane foams exhibiting the capability to conduct static electricity can be prepared by employing flow modifiers described in the present invention that contain a high amount of oxyethylene units. Suitable flow modifiers contain at least about 50%, by weight, of oxy¬ ethylene units in the polyether chain, preferably about 75%, by weight of oxyethylene units, and highly preferably about 85%, by weight, or more of such oxyethylene units, in the polyether chain of said flow modifier. Such poly¬ urethane foams can, for example, be prepared from suitable branched polyether polyols, water as the blowing agent and chain extender, and the commercially known 80:20isomeric mixture of 2,4- and 2,6-tolylene diisocyanate. Typical flow modifier concentrations in the polyurethane foam can vary from about 15-40 weight %, based on the weight of the polyurethane foam, preferably from about 20-30% by weight. Antistatic modifiers of this type can also be used in microcellular elastomers for shoe soles and the like. Such products have excellent utility as carpet underlayments for computer rooms, or for footwear applications where static electricity presents a hazard or other problem. The flow modifers of the present invention are eminently suitable for the manufacture of polyurethane elastomers of relatively low hardness, for example, from 50-65 Shore A. These hardness ranges can be attained at flow modifier levels of from about 5-15 % by weight, based upon the combined ingredients employed in the preparation of said polyurethane elastomers. These products have the capability to approach the friction properties of natural and synthetic rubbers, and lend themselves to use as skid- resistant footwear products having outstanding toughness, durability, and wear resistance, while exhibiting out¬ standing flexibility at low temperatures. .OMPI Catalysts which are employed for the purpose of accelerating the well-known NCO/active hydrogen chemical reactions include tertiary amines, metallic catlaysts and combinations thereof. Typical amine catalysts include tertiary amines, such as triethylamine, tributylamine, N- methylmorpholine, N -ethylmorpholine, N-cocomorpholine, N,N,N' ,N'-tetramethylethylenediamine, 1,4-diazabicyclo- [2.2.2]octane, N-methy1-N*-dimethylaminoethylpiperazine, N,N-dimethylbenzylamine, bis-(N,N-diethylaminoethyl)- adipate, N,N-diethylbenzylamine, pentamethyldiethylenetri- amine, N,N-dimethylcyclohexylamine, N,N,N'-N'-tetra- methyl-l,3-butanediamine, N,N-dimethyl-beta-phenylethyl- amine, 1,2-dimethylimidazole and 2-methylimidazole. Other suitable catalysts are known Mannich bases of secondary amines such as dimethylamine, and aldehydes, preferably formaldehyde; or ketones such as acetone, methyl ethyl ketone, and cyclohexanone; or the phenols such as phenol, nonylphenol and bisphenol. Tertiary amines containing isocyanate-reactive hydrogen atoms may also be used as catalysts and include triethanolamine, triisopropanolamine, N-methyldiethanol- amine, N-ethyldiethanolamine, N,N-dimethylethanolamine, also their reaction products with alkylene oxides such as propylene oxide and/or ethylene oxide. Other suitable catalysts are sila-amines with carbon- silicon bonds of the type described, for example, in U.S. Pat. No. 3,620,984. Specific examples include 2,2,4-tri- methyl-2-silamorpholine and 1,3-diethylaminomethyltetra- methyldisiloxane. It is also possible to use as catalysts nitrogen- containing bases, such as tetraalkylammonium hydroxides; alkali metal hydroxides such as sodium phenolate; or alkali metal alcoholates such as sodium methylate. Hexa- hydrotriazines may also be used as catalysts. Organotin compounds and organomercury compounds may also be used as catalysts. Preferred organotin compounds include tin (II) salts of carboxylic acids, such as tin (II) acetate, tin (II) octoate, tin (II) ethylhexoate and tin (II) laurate, and tin (IV) compounds such as di- butyltin oxide, dibutyltin dichloride, dibutyltin di- acetate, dibutyl dilaurate, dibutyltin maleate or dioctyl- tin diacetate. It is of course possible to use any of the above-mentioned catalysts in the form of mixtures. Organic mercury catalysts are described in U.S. Pat. No. 3,642,044. Further representatives of catalysts suitable for use in accordance with the invention and information on the way in which these catalysts work, may be found in Kunststoff-Handbuch, Vol. VII, by Vieweg and Hochtlen, Carl-Hanser-Verlag, Munich 1966, for example, on pages 96 to 102. The catalyst can be employed in catalytically significant quantities, for example, from about 0.01 to about 1 percent by weight, based on the curable formulation. Further ingredients which may be used depending, of course, on the formulation to be employed and the product desired, include surface active additives such as emulsi- fiers and foam stabilizers. Examples of suitable emulsi- fiers include the sodium salts of castor oil sulphonates or salts of fatty acids with amines, such as diethylamine oleate or diethanolamine stearate-. ' " Alkali metal or ammonium salts of sulphonic acids, for example, of do- decylbenzenesulphonic acid or dinaphthylmethanedisulphonic acid, or of fatty acids, such as ricinoleic acid or of polymeric fatty acids, may also be used as surface-active additives. OMPI Suitable foam stabilizers include polyether silox- anes, especially those which are water-soluble. These compounds are generally synthesized in such a way that a copolymer of ethylene oxide and propylene oxide is attached to a polydimethylsiloxane radical. Foam stabilizers of this type are described, for example, in U.S. Pat. Nos. 2,834,748; 2,917,480; and 2,629,308. Further ingredients which are very useful especially in the preparation of microcellular elastomers including the integral skin type are cell regulating agents such as polydimethylsiloxanes having viscosities of from about 2 to about 100 centistokes at 25°C, preferably from about 2 to about 50 centistokes at 25°C; polyphenylmethyl- siloxanes like the products described in U.S. Pat. No. 4,042,537; mineral oils; polyether polyols comprising copolymers and block copolymers of ethylene and propylene oxides; and the like. Such polyether polyols can be linear or brSrhched copolymers and block copolymers having molecular weights of, for example, from 1000 or lower to 6000 or higher. The preferred polyether polyols are linear copolymers and block copolymers having molecular weights of from about 2000 to about 3500. They can be utilized in proportions from 1 to as high as 20 parts per 100 parts of the polyol, preferably polyester polyols such as described above. These polyether polyols can also be advantageously used with the silicone fluids described below in various proportions in an effective amount to control the cell size as described herein. Highly preferred cell regulating agents are the poly¬ dimethylsiloxanes having viscosities of from about 2 to about 20 centistokes at 25°C. Examples of these products include DC 200 fluids (available from Dow Corning Corporation), having viscosities of from about 5 to about 100 centistokes at 25°C, and also Dow Corning Fluid DCF- 1-1630, having a viscosity of about 3.5 centistokes at OMPI 25°C. (the viscosity being an indicator of the molecular weight of these silicon fluids). DC 200 fluid 5 cs has a molecular weight of 680, 10 cs oil corresponds to 1000, 20 cs to 1600, 50 cs to 3200, and 100 cs to 5000 molecular weight. When utilizing the present invention's) for making shoe soles, either of two commonly employed sole making processes are satisfactory. In one process, the left and right foot soles are cast as plaques, removed from the cast, and then attached to the shoe uppers by a suitable adhesive. In the other process, the shoe uppers, i.e., left and right foot, are presented as one mold surface and the resin is cast in the mold cavity defined by the shoe uppers and the mold walls. In either case, the molds are closed wall molds so as to obtain the mold defined sole shape. This sole shape may not necessarily be smooth (although it is typically so), but may have build in mold ridges such as for resiliency, cushioning, etc. In either process, the typical adhesives (also called "cements") for attaching (also called "cementing") the soles to the uppers are well known. In the second process, i.e., the direct attachment, the adhesive may be the cast polyurethane minus the blowing agent which is cured with the cast foam as it cures, or it may be a different polyurethane adhesive. In making the shoe soles, typically the curable formulation is in a prepackaged form with the isocyanate and prepolymer thereof as one package and the polyol, chain extender, and other additives as another. Among the additives, the presently disclosed flow modifiers are included. A further package may contain the catalyst and the cell control agents such as in a three package system. Thus, for selling to shoe manufacturers, the mixing of the material is done on the premises shortly prior to _, OMPI casting, but the packages are purchased typically in a separate form in proportion suitable for practice of the invention, i.e., for making the shoe soles as well as for obtaining the final product. Consequently, an aspect of the invention includes the "kit" form or "package" form combinations of the components. Hence, package (A) or Component (A) containing polyol and flow modifier as a compatible homogeneous liquid, by itself is believed to be novel as is its combination with/without additional ingredients such as glycol chain extender, blowing agent, cell regulating agent, catalyst, etc. Moreover, the "multi-package" or "kit" form is considered to be novel in that one package (A) comprises polyol and flow modifier with/without additional ingredients mentioned above and a second package (B) contains the polyisocyanate, especially as a quasi-prepolymer obtained by reacting all the iso¬ cyanate component with a predetermined partial quantity of the polyol component in amounts sufficient to result in quasi-prepolymers having NCO/OH ratios of the order stated previously. Several advantages result by using the flow modifiers contemplated herein in polyether polyol systems. Generally, the polyether polyurethane products exhibit improved low temperature characteristics, e.g., resistance to cut tear at extremely low temperatures (-30°C). The elongation characteristic is increased, a property which is particularly useful when the polyurethane product is considered for sealant and adhesive applications. A higher coefficient of friction characteristic is obtained in the flow modified systems. This property is highly de¬ sirable in, for example, tire tread applications. The inclusion of the flow modifier in " the isocyanate curable "resin package", e.g., polyol, glycol chain extender with/without other ingredients, enhances its solubility and compatibility and serves to act in a manner similar to a "coupling agent" in effecting a more uniform polyaddition reaction between the OH groups of the resin package with the NCO group of the isocyanate package. The flow-modified polyester polyurethane products, in general, exhibit many of the foregoing advantages. Though improvement in the low temperature property is noticed, this improvement is seen at a relatively higher tempera¬ ture, e.g., -20°C. The flow modifiers are, in general, excellent viscosity reducers for polyester polyol O II systems. Additionally, the -NHCO- group(s) of the flow modifier is believed to further enhance the solubility and compatibility of polyester polyol systems. This particular property, i.e., viscosity .reducer, is not of particular importance in polyether polyol formulations since commercial polyether polyols are generally low viscosity products. In the practice of highly desirable embodiments of the invention, the flow-modified polyester polyol systems are particularly useful in the manufacture of high per¬ formance microcellular polyurethane elastomer products, in particular shoe soles. The characteristics and properties of preferred polyester products of the invention are detailed in U.S. Patent No. 4,287,307, issued September 1, 1981, and for sake of completeness are summarized herein- below. The microcellular polyester elastomers have cell diameters in the range of from 0.3 to 0.01 mm, or less, with a minimum density of 160 kg/m^ (10 lbs/ft.3). A broad density range is from 160 to 900 kg/m^, correspond¬ ing to a specific gravity of from 0.06 to 0.09 gm/cm3; a preferred range is from 350 to 700 kg/m.3, corresponding to a specific gravity from 0.35 to 0.7 gm/cm^ . The foam por¬ tion of the microcellular polyester polyurethane elastomer comprises a blown cell structure that has a minimum number of about 30-40 cells/cm to 1,000 cells/cm, or more. A preferred range is from 50 cells/cm to 1,000 cells/cm. The surface skin of integral skin microcellular poly¬ ester polyurethane products obtained by the practice of the present invention generally has a thickness of 0.5 to 4 mm, or more, preferably from 1-3 mm. The flex life, as measured by the Ross flex test (ASTM D-1052), or the de Mattia flex test (ASTM D-430), has been found to be extremely good, in comparison with microcellular poly¬ urethane elastomers which result from formulations employing water as the blowing agent (such products having no clearly defined integral-skin surface). The tear strength of these integral-skin microcellular polyester polyurethane elstomer products, when measured according to ASTM D-625, as well as the abrasion resistance, when measured according to the Taber abrasion (ASTM D-3389), are also appreciably bettern in comparison with products prepared by blowing with carbon dioxide (water-isocyanate rection) . Further advantages and properties of the micro¬ cellular polyester polyurethane elastomer products obtained by the practice of preferred aspects of the invention are disclosed in said U.S. Patent No. 4,287,307. Several advantages result by utilizing the flow modifiers contemplated herein in polyether and polyester systems used in the manufacture of flexible polyurethane foams. As described hereinabove, the use of flow modifiers containing a high oxyethylene content can result in polyurethane foams that are capable of dissipating static electricity efficiently from carpets when used in underlayments, or from foamed footwear worn by personnel in computer rooms. OMPI The flow modifiers of the present invention also have the capability to render flexible polyurethane foams hydrophilic. Normal (conventional) low density poly¬ urethane foams are normally prepared from hydrophobic polyethers or polyesters and aromatic isocyanates. The flow modifiers of the present invention have the unique capability of imparting to the polyurethane foam the characteristic to pick up substantial quantities of water without leaching the modifier out of the polyurethane foam. This is believed to be partially due to the fact that reactive urethane hydrogen atoms in the flow modifier have the capability to react with a portion of the iso¬ cyanate groups of the' foam ingredients, rendering the foam surface highly hydrophilic. These foams, both of the polyester and polyether type, are particularly interesting as household sponges, sponges for car washing, hydrophilic plant growing medium sponges, and the like. If desired, the polyurethane foam can be made by incorporating, in addition to the flow modifier, soaps, detergents, shampoos, fertilizers, plant growth hormones, enzymes, and the like. In the manufacture of solid polyurethane elastomers via the prepolymer process (a route that is oftentimes preferred) the flow modifiers of the present invention can be employed to act as convenient solvents for the glycol and/or a ine chain extender. Polyurethane elastomers are often prepared at prepolymer:extender ratios of 100:10 or less. Such dissimilar ratios are difficult to meter. Moreover, the extender is often quite insoluble in the prepolymer. The flow modifier of the present invention oftentimes will greatly facilitate the preparation of a stable extender system that is more readily dispersed (a system oftentimes much lower melting than the pure extender), and yielding additional processing advantages such as the ability to obtain much longer pot-lives due to the lower operating temperature that can be employed. Hence, the application of compatible flow modifier-chain extender combination packages represents a further important aspect of the invention. In addition to the apparent novel flow modifiers embraced by Formula I supra, desirably where the variable x is greater than 1 such as 2 or 3 and upwards to 8 and even 25, or more, many flow modifiers which are particularly preferred from a commercial viewpoint are shown in structural Formula III below: III O 0 II II R , -- oxyC2-C3alkylene)- x -OCNH-A- HCO- C2-C3alkylen oxy•)- x -R , wherein each R^_ individually is alkyl, desirably C^-Cg- alkyl; a C5-C7cycloalkyl desirably methyl- or ethyl- substituted Cs-C cycloalkyl, or aralkyl, desirably phenyl- Cχ-C3alkyl; wherein _A represents alkylene, desirably C\- Cgalkylene; a Cs-C -cycloalkylene, desirably cyclo¬ hexylene, C -C2alkyl- or Cχ-C2alkoxy-substituted cyclo¬ hexylene; Cχ-C4cyclohexylenealkylene such as isopropylcy- clohexylenemethylene; unsubstituted, Cχ-C3alkyl-, or Cχ~ C3alkoxy substituted phenylene (preferably tolylene), or divalent (4,4'- and 4,4*-/4,2'-)diphenylenemethane, or the divalent hydrogenated counterparts of the foregoing; wherein _x is at least one and upwards to 25, and more, preferably 1 or 2 and upwards to 8, more preferably 1 to 4 or 2 to 4; and wherein the oxyC2-C al ylene unit is oxy¬ ethylene (preferred), oxypropylene, and mixed and/or block oxyethyleneoxypropylene unit(s), and mixtures of the fore¬ going. When the oxyC2-C3alkylene unit represents oxy¬ ethyleneoxypropylene, the mol ratio of the oxypropylene moiety to the oxyethylene moiety is in the range of from abubt 75:25 to about 25:90. OMPI A further subclass of flow modifiers which is useful in the practice of the invention(s) include the following: IV O 0 II II R" {-oxyC2-C3alkylene)-jj OCNH A NHCOR' wherein R_, A, >c, and oxyC-^-C-^alkylene have the meaning assigned in Formula III above. Novel flow modifiers which are especially preferred include the urethane products resulting from the reaction of 2,4- and or 2,6-toluene diisocyanate and monoether of mono- and of polyC2-C3alkylene glycol of the formula V O II R'—(■oxyC2-C3al ylene-)- x -—OCNH 2,4- and/or 2,6-tolylene 2 wherein R__ is alkyl or aryl, preferably methyl, ethyl, propyl, isopropyl, butyl, isobutyl, sec-butyl, pentyl, hexyl and phenyl; wherein x. is at least one, preferably 1 or 2 and upwards to 8; and wherein oxyC-p-C^alkylene represents oxyethylene (preferred) and oxypropylene and when x is 2 or more oxyC2-C3alkylene can also be oxyethyleneoxypropylene, desirably where the mol ratio of the oxypropylene moiety to the oxyethylene moiety is in the range of from about 75:25 to about 25:90. Additional novel flow modifiers which are preferred include the urethane reaction products resulting from the reaction of R*—£o yC2-C3alkylene - x —OH, the R^, x , and oxy- C-?-C^alkylene unit having the significance assigned in Formula IV supra, and a diphenylmethane diisocyanate (MDI) such as 4,4'-diphenylmethane diisocyanate, 2,4'-diphenyl- methane diisocyanate, mixtures of 4,4'-MDI and carbodi- imides thereof, e.g., Isonate 143-L, mixtures of 4,4'-MDI and minor amount of the 2,4'- and 2,2'-MDI isomers, and the like. The isocyanate compound and polyol are reacted in amounts to give a ratio of NCO groups to OH groups of one. Other preferred flow modifiers are shown in Formula VI below: ■ foxyC2-C3alkyle eτ- 5 j—OCNH- wherein Y_ represents 4,4'-and/or 2,4'-diphenylenemethane or C4-Csalkylene; and wherein R_, x_, and the oxyC 6 -C- * },alkylene unit have the meanings assigned in Formula V above. DESCRIPTION OF TEST METHODS The following test methods have been used to determine physical properties. The description found in the appropriate ASTM manual applies except as noted below: Tear Strength: Determined in accordance with ASTM D-624. Die C. Tensile Strength: Determined in Accordance with ASTM D-412. Method A. Flex Testing: Determined in accordance with ASTM D-1052, except as noted below: Ageing was under ambient conditions for at least one week prior to testing. Preparations of sample differs from ASTM D-1052 in that a "TEXON" insole material was cemented to the specimen to increase the stress on the hole made with the piercing tool. The "TEXON" material is (available from Texon, Inc., South Hadley, MA.) 0.070 inches in thickness and must be cemented to the entire 1 x 6 inch surface of the specimen. The "TEXON" is cemented to the uppermost molded surface of the plaque. Cementing should be done with a heat activated urethane adhesive applied to both the "TEXON" and the specimen in accordance with the manufacturers' recommendations. Results are reported in cycles at 500% cut growth as well as % cut growth at selected number of cycles. Hardness: Determined in accordance with ASTM D-2240, Durometer Shore A. Viscosity: Determined with a Brookfield viscometer (Brookfield Engineering Laboratories, Inc.) in accordance with ASTM D-2849. f ">MPI _ 'IPO _ Hand Foams : Hand foams are prepared by weighing all the ingred¬ ients of the polyol component (i.e., the polyester polyol, the flow modifier, any extenders, surfactants and catalysts, and the blowing agents as required into a poly¬ ethylene lined paper cup. This component is then mixed well. The required amount of isocyanate is then weighed into the polyol component and mixed at high speed for 8 to 10 seconds. The mixture is then cast into a clean cup or a mold as required. In the tables herein, the following terms of art which are being used are defined below: Cream Time: The time interval between the final mix¬ ing and the point at which the mixture turns creamy or cloudy and starts to expand. Rise Time: The time interval between the liquid mixture poured into the container (mold) and the completion of expansion of the foaming mass. Tack Free The time interval between pouring the Time: liquid mixture and the time that the sur¬ face of the foam can be touched with a finger without sticking. Snap Time: When the reacted polymer can no longer be separated when pinched between two fingers and pulled. Free Blowing The density in lbs./ft.3 of a foam that Density: is allowed to rise in an open cup and is determined by cutting the cap of the foam flush with top of the cup and using the following equation: weight of foam and cup - weight of cup x 62.43 =lbs/ft^ cc of cup '-"fc TREX, OMPI .<& . wipo _ Molded The molded density is expressed in Density: terms of grams per cubic centimeter (gm/cc), and is measured on the molded item by means of volume displacement with a liquid. Inasmuch as a number of components employed in the practice of the invention have been identified by their trade names, for the sake of convenience, these are tabulated herein and their chemical structure or specifi¬ cations further amplified so that any of these components can be readily obtainable or made by those of ordinary skill in the art. The components are marked with a double asterisk (**) in the Examples. TRADE NAME DESIGNATION TABLE Trade Identification of Component(s) and Designation source of same ISONATE 240 The Upjohn Company. Isocyanate A prepolymer comprising the reaction product of about 40 parts by weight of (a) a difunctional copolyester polyol of adipic acid, ethylene glycol and 1,4- butanediol having a molecular weight of about 2000, and (b) about 60 parts by weight of carbodiimide modified 4,4'-di¬ phenylmethane diisocyanate; said pre-polymer having an isocyanate content of about 18.8% by.weight, an isocyanate equivalent of about 223, and a viscosity at 30°C. of about 1000 centipoises. The product crystallizes at approximately 15°C. MONDUR E-501 Mobay Chemical Corporation, Isocyanate Polyurethane Division. A carbodiimide modified diphenylmethane diisocyanate terminated polyester pre¬ polymer having an isocyanate content of about 18.9% by weight, an isocyanate equivalent of about 222.5, and a vis¬ cosity at 30°C. of about 830 centi- poises. MONDUR MR Mobay Chemical Corporation, Isocyanate Polyurethane Division. A crude polymethylene polyphenyl polyiso¬ cyanate having an isocyanate content of about 31.5% and an isocyanate equivalent of about 133.4. ISONATE 125M The Upjohn Company. Isocyanate A high-purity grade of diphenylmethane diisocyanate containing approximately 98% 4,4'-diphenylmethane diisocyanate and 2% 2,4'-diphenylmethane diisocyanate. The average isocyanate equivalent is 125. ISONATE PF Mobay Chemical Corporation, Isocyanate Polyurethane Division. A clear yellow liquid isocyanato- terminated polyether prepolymer made by reacting about 85 weight percent 4,4'- diphenylmethane diisocyanate and about 15 weight percent dipropylene glycol and tripropylene glycol. It has an iso¬ cyanate content of about 22.6% by weight and an isocyanate equivalent of about 186. POLYESTER A A diethylene glycol-glycerol adipate polyol having a degree of branching of about 2.35, a hydroxyl number of 42.7, an acid number of 0.4, and an equivalent weight of about 1300. POLYESTER B An ethylene glycol-1,4 butanediol glycerol adipate polyol having a functionality of about 2.3, a hydroxyl number of 40.7, a carboxyl number of 0.2, and an equivalent weight of about 1370. DABCO 33LV Air Products & Chemicals, Inc. Catalyst A liquid blend catalyst consisting of 1/3 l,4-diazobicyclo[2.2.2]octane and 2/3 dipropylene glycol. L-5340 Union Carbide Corporation. Surfactant A non-hydrolyzable polyoxyethylenepolydi- methylsiloxane surfactant: Viscosity 25°C, Centistokes 130, Flash Point °F, Closed Cup 160; Apparent Specific Gravity 25°/25°C 1.05. SILICONE A A dimethylpolysiloxane silicone fluid having a viscosity of 3.5 centistokes at 25°C. SYNCAT M 601 Plas-Tech Systems, Inc. Catalyst A dialkyltin catalyst in a plasticizer. FREON 113 E. I. duPont deNemours Company. Blowing Agent Trichlorotrifluoroethane having a boiling point of 47.6°C. FREON 11B E.I. duPont deNemours Company. Blowing Agent A stabilized version of trichloromonofluoromethane having a boiling point of 23.8°C. BUTYL Union Carbide Corporation. CARBITOL Diethylene glycol monobutyl ether with a molecular weight of 162. METHYL Union Carbide Corporation. CARBITOL Diethylene glycol monomethyl ether with a molecular weight of 120. HEXYL Union Carbide Corporation. CARBITOL Diethylene glycol monohexyl ether with a molecular weight of 190. METHYL Union Carbide Corporation. CARBITOL Diethylene glycol monomethyl ether with a molecular weight of 120. PROPASOL Union Carbide Corporation. SOLVENT B Butoxypropanol with a molecular weight of 132. PROPASOL Union Carbide Corporation. SOLVENT P Propoxypropanol with a molecular weight of 116. PHENYL Union Carbide Corporation. CELLOSOLVE Ethylene glycol monophenyl ether with a molecular weight of 138. PHENYL Union Carbide Corporation. CARBITOL Diethylene glycol monophenyl ether with a molecular weight of 182. UCON Union Carbide Corporation. LUBRICANT A monobutyl ether of a polyoxyalkylene 50HB660 glycol with an average molecular weight of about 2000 UCON Union Carbide Corporation. LUBRICANT A monobutyl ether of polypropylene LB285 glycol with an average molecular weight of 979. TP-90B Thiokol Chemical Company. Plasticizer C4H OC2H4OC2H4OCH2OC2H4OC2H4OC4H9 CARBOWAX 750 UNION CARBIDE CORPORATION Methoxypolyethyleneoxyglycol found by analysis to have a hydroxyl number of about 76.8 or an equivalent weight of about 730. • -fϋREΛ " OMPI ^ °ιϋ SILICONE UNION CARBIDE CORPORATION SURFACTANT A non-hydrolyzable polyoxyalkylene L-548 polydimethylsiloxane liquid having an apparent specific gravity of 25/ 25°C of 1.03 and a viscosity 25°C (centistokes) of 1250. NIAX POLYOL UNION CARBIDE CORPORATION 12-56 High primary hydroxyl-containing polyoxyethyleneoxypropylene diol of 2000 molecular weight, having an ethyleneoxy content of about 50% by weight. NIAX POLYOL UNION CARBIDE CORPORATION 11-27 High primary hydroxyl-containing polyoxyethyleneoxypropylene triol/ diol mixture containing about 15% by weight of ethyleneoxy-capped end- blocks, having a hydroxyl number of about 27, and a hydroxyl equivalent weight of about 2000. L-5309 UNION CARBIDE CORPORATION SURFACTANT A non-hydrolyzable polyoxyalkylene- polydimethylsiloxane surfactant, known as an especially useful compound for the manufacture of high-resiliency flexible polyether foams. The following Examples are illustrative of the invention but are not to be construed as to limiting the scope thereof in any manner. In the specification, the following should be noted: Room temperature refers to a temperature of 20°C-23°C unless a different temperature is indicated. Percent refers to percent by weight unless indicated otherwise. Parts refers to parts by weight unless indicated otherwise. 80/20 TDI refers to an isomeric mixture of 80 parts of 2,4-tolylene diisocyanate and 20 parts of 2,6-tolylene diisocyanate. MDI refers to a diphenylmethane diisocyanate. 4,4'-MDI refers to 4,4'-diphenylmethane diisocyanate. Isocyanate Index is the quotient obtained by dividing the equivalents of NCO by the sum of the equivalents of active hydrogen group(s), multiplied by 100. By way of illustration, a conventional formulation for the manufacture of integral skin microcellular shoe soles may comprise Isonate 240** (quasi-prepolymer of modified 4,4'-MDI and a copoly- ester diol) as Component A and, as Component B, a mixture comprising polyester polyol, 1,4-butanediol chain extender, water, etc. The isocyanate index, expressed in equation form, is shown below: Isocyanate Index = $ Equivalent NCO x 100 ^Total Equivalent OH wherein "≤. total equivalent OH" represents the sum of the equivalent(s) of polyol, 1,4-butanediol and water. In the practice of the present inventions the isocyanate index is generally a number in the range of from about 90 to about 120 depending on the re¬ sulting polyurethane product, e.g., flexible foam, microcellular elastomer, solid elastomer, and the like. Expressed in a different manner, the ratio of NCO/OH equivalents is generally in the range of from about 0.9:1.2, desirably from about 0.9:1.1, prefer¬ ably from about 0.95:1.05, and for many applications generally about 1:1. As used herein including the appended claims, reference to "compatible homogeneous liquid mixture of polyol(s) and flow modifier(s)" shall mean that such mixture (of polyol(s) and flow modifier(s) and optionally chain extender, with/without other well- known urethane ingredients which may be included in the polyol resin package such as catalyst, blowing agent, cell regular, etc.) is a stable, homogeneous liquid blend at approximately room temperature, e.g., 20°C-23°C, or if otherwise, the mixture can be made into a stable, homogeneous liquid state at 20°C-40°C by heating to a moderately elevated temperature, e.g., 80°C to 100°C for 0.5 to 2 hours, followed by slow cooling to about 20°C-40°C. The term "mixture of polyol(s) and flow modifier(s)" shall mean, unless the text indicates otherwise, a compatible homo¬ geneous liquid mixture referred to above as well as mixtures of polyol(s) and flow modifier(s) that are not compatible at the aforesaid lower temperatures but which, under the reaction conditions employed to form polyurethane products, are liquid and convertible by reaction with organic polyisocyanate compounds to such polyurethane products. Example 1 A series of isocyanate-ether alcohol reaction products were prepared and their compatibility with poly¬ ester polyols useful in the manufacture of microcellular foams was investigated and noted. The resulting blends were tested for viscosity at room temperature (23°C.) and 30°C, and used in a typical shoe product formulation and tested for Ross flex at -18°C. (ASTM D-1052). A. Synthesis of Reaction Product A. In this experiment, Butyl Carbitol** (diethylene glycol monobutyl ether having a molecular weight of 162 and a functionality of 1) was reacted with tolylene di¬ isocyanate (80% 2,4- and 20% 2,6-tolylene diisocyanate) having a molecular weight of 174 and a functionality of 2 at an OH/NCO ratio of 1. Starting at room temperature, a clean dry jar was charged with 32.5 gms of Butyl Carbitol and to this 17.4 gms of tolylene diisocyanate was added. The jar was capped tightly and agitated by gentle shaking to mix the components. No heat was applied for the first 10 minutes. The resulting exotherm of the reaction raised the temperature to 55°C. At this point, additional heating was used. The jar was placed in a hot air oven and maintained for 3 hours at 70°C. to complete the reaction. After allowing the reaction product to cool to room temperature overnight, the following observations were made. The reaction product, hereafter referred to as Reaction Product A, was slightly viscous, clear liquid with a dark yellow color. It was also noted that this product was compatible with Polyester A** (a polyester polyol) at a weight ratio of 80 parts of polyester polyol to 20 parts of the Reaction Product A. The resulting polyester polyol/Reaction Product A mixture had a viscosity of 25,800 centipoises at 23°C. and 13,500 centi- poises at 30°C. B. Synthesis of Reaction Product B. The process used to make Reaction Product A was repeated using 34.3 gms of Hexyl Carbitol** (diethylene glycol monohexyl ether with a molecular weight of 190 and a functionality of 1) and 15.7 gms of 80/20 2,4- 2,6-tolylene diisocyanate. After 10 minutes the temperature of this reaction was 43°C. The reaction mixture was heated at 70°C. for 3 hours as in the preparation of Reaction Product A to complete the reaction. The resulting product, hereafter referred to as Reaction Product B, was a clear, light yellow, slightly viscous liquid at room temperature. It proved to be compatible with Polyester A** at a weight ratio of 80 parts of Polyester A to 20 parts of Reaction Product B. The viscosity of Polyester A/Reaction Product B mixture was 22,600 centipoises at 23°C, and 11,500 centipoises at 30°C. C. Synthesis of Reaction Product C. In this experiment 29.0 gms of Methyl Carbitol** (diethylene glycol monomethyl ether with a molecular weight of 120 and a functionality of 1) were reacted with 21.0 gms of 80/20 2,4- 2,6-tolylene diisocyanate using the process of (A) above. After 10 minutes the exotherm of this reaction had increased the temperature of the mixture to 60°C. The reaction mixture was heated for 3 hours at 70°C. and cooled overnight to room temperature as in (A) above. The product (Reaction Product C) was a transparent dark yellow viscous liquid. A compatible mixture of 20 parts by weight of Reaction Product C and 80 parts by weight of Polyester A** had a viscosity of 30,500 centipoises at 23°C, and 16,700 centipoises at 30°C. D. Synthesis of Reaction Product D. Reaction Product D was prepared using 35.2 gms of butoxy triglycol having a molecular weight of 206 and a functionality of 1 and 14.8 gms of 80/20 2,4- 2,6-tolylene diisocyanate. The temperature of the mixture after the first 10 minutes, without added heat, was 44°C. Following the heating and cooling procedure of A above, the product was observed to be a clear, light yellow, slightly viscous liquid at room temperature. This product (Reaction Product D) was compatible with Polyester A** at a weight ratio of 80 parts Polyester A to 20 parts of Reaction Product D. The resulting polyester polyol Reaction Product D blend had a viscosity of 21,000 centipoises at 23°C, and 13,400 centipoises at 30°C. E. Synthesis of Reaction Product E. Using 30.2 gms of Propasol Solvent B** (butoxypro¬ panol) and 19.9 gms of 80/20 2,4- 2,6-tolylene diiso¬ cyanate (TDI), Reaction Product E was prepared following the same procedure used in (A) above. The temperature observed after 10 minutes, without added heat, was 37°C. The reaction mixture was heated and cooled as described previously. There was obtained a transparent, light yellow, viscous liquid (Reaction Product E) which was compatible with Polyester A** at a weight ratio of 80 parts of Polyester A to 20 parts of Reaction Product E. The viscosity of this blend was 27,400 centipoises at 23°C, and 13,600 centipoises at 30°C. F. Synthesis of Reaction Product F. In this experiment the jar was charged with 28.6 gms of Propasol Solvent P** (propoxypropanol having a molecular weight of 116 and a functionality of 1) and reacted with 2.14 gms of 80/20 2,4- 2,6-tolylene diiso¬ cyanate. The addition reaction was conducted following the process used to make Reaction Product A. After 10 minutes, the exotherm had increased the temperature to 40°C. Heating and cooling were carried out under the same conditions used to make Reaction Product A. This produced a clear, light yellow, viscous liquid at room temperature, i.e., Reaction Product F. A blend of 80 parts Polyester OMPI ^ - - A/20 parts Reaction Product F was compatible, and possessed a viscosity of 28,500 centipoises at 23°C, and 15,600 centipoises at 30°C. G. Synthesis of Reaction Product G. In this experiment Butyl Carbitol** was reacted with Isonate 125M** (high purity 4,4'-diphenylmethane diiso¬ cyanate). In this reaction 405.6 gms of Butyl Carbitol were charged to a 1 liter reaction flask, maintained under a nitrogen atmosphere, fitted with a stirrer, thermometer, reflux condenser, and feed inlet. The internal temperature of the reaction flask was raised as necessary by heating the outside of the flask with a heat mantle controlled by a rheostat. The Butyl Carbitol was pre¬ heated to 94°C. The 4,4'-MDI was added in three incre¬ ments with good agitation. The first addition of 4,4'-MDI of 125.7 gms brought the temperature of the mixture to 139°C. within 5 minutes. This being an exothermic reaction, the reaction product mixture was allowed to cool to 62°C. before the second 4,4'-MDI addition of 127.7 gms was made. After 20 minutes a temperature of 94°C. was recorded and the third addition of 4,4'-MDI (59.2 gms) was made. The total amount of Isonate 125M added was 312.6 gms. With moderate heating a temperature of 92°C. to 118°C. was maintained for 2 hours to complete the reaction. Agitation was maintained throughout the entire procedure. Upon cooling to room temperature the product (Reaction Product G) of this reaction was observed to be a very viscous liquid with large crystals forming. At 35°C, it was a hazy liquid with a viscosity of 12,620 centipoises. At temperatures above 95°C, it was a clear light yellow liquid. Reaction Product G was also examined for compatibility with Polyester A. In view of the hazy, semicrystalline nature of this product at room temperature, an 80/20 Polyester A/Reaction Product G mixture was heated to 95°C, agitated, and then allowed to cool to room temperature. The result was a clear, compat¬ ible mixture with a viscosity of 30,750 centipoises at 23°C, and 13,530 centipoises at 30°C. H. Synthesis of Reaction Product H. Reaction Product H was prepared by reacting Butyl Carbitol** and Mondur MR** (a crude polymethylene poly- phenyl polyisocyanate having an isocyanate content of about 31.5% by weight and an isocyanate equivalent of about 133.4). A 1 liter reaction flask was charged with 405.6 gms of Butyl Carbitol. A total of 333.5 gms of Mondur MR was required for a complete reaction at a stoichiometric NCO/OH ratio of one. The Butyl Carbitol was preheated to 82°C, and with good agitation the poly¬ isocyanate added in three increments. The exotherm from the first addition of 144.1 gms of polyisocyanate raised the temperature to 120°C, within 10 minutes. A second addition of 109.7 gms of polyisocyanate was made when the temperature subsided to 92°C, and after 20 minutes a peak temperature of 109°C was noted. The third increment of 79.7 gms of polyisocyanate was added at 99.5°C. Moderate heating and continued agitation was used to maintain the temperature between 99°C. and 107°C for 2 hours to complete the reaction. The resulting product (Reaction Product H) was a dark brown liquid with a viscosity of 342,800 centipoises at 23°C, and 66,400 centipoises at 35°C. Although the color was very dark it was transparent with no solids evident. In view of the high viscosity of Reaction Product H, an 80/20 Polyester A**/Reaction Product H blend was heated to 95°C. to facilitate mixing then allowed to cool to room temperature and checked for compatibility. There was obtained a compatible mixture with a viscosity of 37,000 centipoises at 23°C and 16,190 centipoises at 30°C. OMPI I. Synthesis of Reaction Product I. To a one liter reaction flask, there were charged 730 gms (1 equivalent) of Carbowax 750** and heated to 50°C. A total of 87 gms (0.5 equivalent) of 80/20 2,4-, 2,6- tolylene diisocyanate was then added and the resulting exothermic reaction proceeded to over 100°C. Heat was applied to maintain the reaction product mixture at about 110°C for 2 hours under an atmosphere of nitrogen. Upon cooling to room temperature there was obtained a white- yellowish waxy product having a melting point range of about 30°C-35°C. This product (Reaction Product I) was blended with Niax Diol 12-56** at a ratio of 75/25 Niax Diol 12-56 to Reaction Product I, heated to 50°C, where¬ upon there was formed a homogeneous mixture. Upon cooling to room temperature, the mixture remained compatible. J. Synthesis of Reaction Product K. Reaction Product K was prepared by reacting the ethylene oxide adduct of nonylphenol, having a hydroxyl value of 51, and a hydroxyl equivalent weight of 1100, corresponding to an addition product of about 20 ethylene- oxy units per phenolic hydroxyl group, with the 80/20 mixture of 2,4- and 2,6-tolylene diisocyanate in an equivalent ratio of NCO/OH equal to one. A one liter reaction flask was charged with 700 gms of the phenol- ethylene oxide reaction product (corresponding to 0.636 equivalent of OH), the waxy material was heated to 50°C, and agitated under a stream of nitrogen. A total of 56.0 gms of the tolylene diisocyanate mixture (corresponding to 0.644 equivalent of NCO) was added under good agitation, and the resulting exotherm reached 95°C. The reaction product mixture was further heated to 105°C. for two hours, still under nitrogen. Upon cooling, there was obtained a slightly off-white waxy product that melted at 30°C-35°C. This product (Reaction Product K) was blended with Niax Diol 12-56** at a ratio of 60/40 Niax Diol 12-56 to Reaction Product K, heated to 60°C, properly mixed and allowed to cool to room temperature. The product blend remained compatible for several weeks before it was employed for further experimentation. Foam Experiments and Shoe Sole Parts Hand foam experiments comprising the manufacture of microcellular polyurethane foams from a diethylene glycol adipate polyester polyol (Polyester A), ethylene glycol extender, and an isocyanate prepolymer (Mondur E-501* or Isonate 240**) were conducted to test the suitability of using the Reaction Products A through H of Example 1 in polyurethane foams. Control foams were also made without flow modifier (blank) or with TP-90B** (di[2-(2-butoxy- ethoxy)ethoxy]methane) . The resulting foams had open cells with good cell structure. These foams were prepared using a hand-mixe process at room temperature. Shoe sole parts were also prepared using the same hand-mix process and casting the foam mixture into an epoxy mold held at a temperature of 30°C.-35°C. Excellent polyurethane parts were produced with the exception of Reaction Products G and H which produced shoe sole parts exhibiting slight shrinkage at the 90/10 polyester polyol/Reaction Product level. All other shoe sole parts did not shrink at the density tested. Reaction Products G and H were prepared using a 4,4'-diphenylmethane diisocyanate as a reactant. The formulations might have to be optimized with regard to the catalyst and surfactant type to avoid all shrinkage, as had been the case with the other flow modifiers tested (Reaction Products A, B, C, D, E, F). The slight shrinkage of Reaction Products G and H did not detract from their exhibiting excellent flex lives at low temperature. A one by six inch strip was die cut from each of the shoe soles and tested for flex properties in a Ross Flex Tester at -18°C (ASTM D-1052). All samples prepared using the Reaction Products A through H of OMPI ■ ' V.fFO Example 1 and TP-90B** show superior flex properties compared to the control formulation (without flow modifier). The specific results of the overall study are described in Table I infra. TABLE I FORMUIATION 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 Polyester A** 100.0 80.0 80.0 80.0 80.0 80.0 80.0 80.0 90.0 80.0 70.0 60.0 90.0 80.0 70.0 60.0 TP-90 B** - Reaction Product A - - 20.0 - - - - - - - - • - - - Reaction Product B 20.0 Reaction Product C - - 20.0 - - - - - - - - Reaction Product D - 20.0 Reaction Product E - - - - - - 20.0 - - — - - - — Reaction Product F - 20.0 Reaction Product G 10.0 20.0 30.0 40.0 - - - - Reaction Product H - - - - 10.0 20.0 30.0 40.0 Ethylene Glycol 11.0 11.0 11.0 11.0 11.0 11.0 11.0 11.0 11.0 11.0 11.0 11.0 11.0 11.0 11.0 11.0 L 5340** 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 Silicone A** 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 DABOO 33LV** 0,9 0.9 0.9 0.9 0.9 0.9 0.9 0.9 0.9 0.9 0.9 0.9 0.9 0.9 0.9 0.9 N / N.N' .N' -tetra- 0.3 0.3 0.3 0.3 0.3 0.3 0.3 . 0.3 0.3 0.3 0.3 0.3 0.3 0.3 0.3 0.3 ιretfty___utaneediam--ne SΪNCAT M 601** 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 FREON 113** 10.0 10.0 10.0 10.0 10.0 10.0 10.0 10.0 10.0 10.0 10.0 10.0 10.0 10.0 10.0 10.0 MONDUR E-501** 96.8 93.4 93.4 93.4 93.4 93.4 93.4 93.4 ISONATE 240** 95.8 94.1 92.4 90.7 95.8 94.1 92.4 90.7 TABLE I (cont'd.) • ΓΌIWIATION 1 2 3 4 5 6 7 8 9 10 11 12 13 14 15 16 Cup Foam: Cream Time 15 15 15 15 15 15 15 15 18 17 18 18 14 14 12 15 (sec) Rise Time 50 45 43 42 42 43 45 42 45 50 57 46 42 42 38 42 (sec) Tack Free Time 60 70 70 72 70 75 70 70 65 70 82 82 60 65 64 65 Snap Time (sec) 100 105 110 105 100 110 105 105 95 110 140 140 95 108 100 100 Free blow density (lbs/ft. 3 ) 10.8 10.4 10.8 10.8 9.9 11.0 10.9 10,5 10.7 11.1 12.2 11.3 N.T. 11.6 11.0 11.0 Cells per cm >50 >50 >60 >80 ?60 60 >60 60 ρ- 60 60 >60 >60 .►60 80 ?80 • ^80 I Molded Shoe Sole C Deirold Time (min) 5 5 5 5 5 5 5 5 5 . 5 7 10 5 5 7 7 Density (g/cc.) 0.33 0.32 0.35 0.34 0.34 0.35 0.33 0.34 0.49 0.50 0.51 0.51 0.50 0.51 0.51 0.51 Hardness - Shore A 50 46 48 48 48 52 53 50 72 72 68 66 72 72 71 70 (ASTM D 2240-75) Ross Flex at <8 218 >272 > 272 >272 >272 >272 242 145.7 114.8 > 266 >266 >266 >266 136.8 146.2 -18°C (x 10 3 cycles) Cut Growth (%) at 272,000 com-, com. None None 160 75 com¬ cycles plete plete plete at 266,000 com- com- 65 40 30 None com- com¬ cycles plete plete plete plete EXAMPLE 2 Synthesis of Reaction Product J. Reaction Product J is a larger batch of Reaction Product A supra and was prepared for evaluation as follows. A 5 liter reaction flask, fitted with a stirrer, thermometer, feed inlet, and reflux condenser, was maintained under a nitrogen atmosphere. The internal temperature of the reactor was raised as necessary by heating the outside of the flask with a heating mantle controlled by a rheostat. To this flask 2593 gms of Butyl Carbitol** were charged with moderate heat being applied. Starting at 30°C and with continuous stirring, the first of three tolylene diisocyanate (80% 2,4- 20% 2,6-TDI iso- meric mixture) additions, 522.3 gms., was added over a one minute period and the increase in temperature observed. After 18 minutes the temperature of the reaction product mixture was 84°C and the heater was turned off. The temperature peaked at 93°C (33 minutes after the first addition). With the temperature at 92°C, a second tolylene diisocyanate addition of 478.5 gms was made. Some slight discoloration was noted as the temperature increased over 100°C. A peak temperature of 123.5°C was reached 18 minutes after the second addition. When the temperature subsided to 80.5°C the third addition of 392.6 gms of tolylene diisocyanate was made. The total amount of tolylene diisocyanate used was 1393.4 gms. The exo- therm peaked 15 minutes after this addition and a temperature of 94°C was noted. Moderate heat was again applied to maintain the temperature of the reaction product mixture between 94°C and 101°C for 3 hours to complete the reaction. Agitation was maintained through¬ out the experiment. The product of this reaction, here¬ after referred to as Reaction Product J, was a dark yellow transparent liquid with a viscosity of 7,600 centipoises at 23°C. This product was tested for compatibility with OMPI " WflPO Polyester A** polyester polyol and Polyester B** polyester polyol with/without Niax Polyol 12-56**, a high primary hydroxyl-containing polyoxyethyleneoxypropylene diol of 2000 molecular weight, and fluorocarbon blowing agents FREON 11B** and FREON 113**. The results of this study are described in Table II. OMPI TABIE II FORMU KTIONS 1 2 _ 5 6 2 8_ 9 10 11 ___. 13 14 15 Lyester A** 90.0 80.0 70.0 70.0 60.0 50.0 90.0 80.0 70.0 Lyester B** 90.0 80.0 70.0 70.0 60.0 50.0 __ POLYOL 12-56** 10.0 20.0 30.0 10.0 20.0 30.0 FREON 113** 10.0 10.0 10.0 FREON 11B** Reaction Produc :t J 10.0 20.0 30.0 10.0 20.0 30.0 20.0 20.0 20.0 20.0 20.0 20.0 10.0 20.0 30.0 Viscosity (centipoises) x 10 3 at 23°C 20.0 17.0 14.3 26.9 24.4 18.5 14.5 N.T. N.T. 14.5 11.2 6.03 11.4 8.91 7.51 at 35°C 11.4 10.0 9.23 16.7 13.5 9.44 6.50 N.T. N.T. 8.78 5.60 3.61 7.06 . 5.35 4.52 Observations 1 1 1 4 3 2 1 1 1 1 2 2 1 1 1 6 6 6 6 5 5 6 6 6 6 1 = clear 2 = slightly hazy 3 = some haze 4 = very hazy 5 = separation 6 = compatible N.T. = not tested because of separation or poor compatibilit ; Polyether Reaction Products I and K which are based on substantially longer polyethyleneoxy chains than Reaction Product J are readily conpatible in the Niax Polyol 12-56**. Hence, it is suggested to select the appropriate conposition of the flow modifier to effect optimized compatibility in polyether or polyester polyols, as the case may warrant. o TABLE II (cont'd.) FORMULΛTIONS 16 17 18 19 20 21 22 23 24 25 26 27 28 29 Polyester A** 90.0 80.0 70.0 90.0 80.0 70.0 Polyester B** 90.0 80.0 70.0 90.0 80.0 70.0 90.0 80.0 NIAX POLYOL 12-56** 10.0 20.0 30.0 10.0 20.0 FREON 113** 10.0 10.0 10.0 FREON 11B** 8.0 8.0 8.0 80 9.0 8.0 Reaction Product J 10.0 20.0 30.0 10.0 20.0 30.0 10.0 20.0 30.0 Viscosity (centipoises) x 10 3 I U at 23°C 14.9 12.7 10.4 11.6 10.2 8.5015.9 13.9 11.5 16.9 N.T. N.T. 21.2 14.1 at 35°C 8.98 7.22 6.21 6.48 5.82 5.14 8.77 6.78 5.47 9.32 N.T. N.T. 12.6 8.53 Observations 1 1 1 1 1 1 1 1 1 2 4 4 1 1 6 6 6 6 6 6 6 6 6 5 5 6 6 ' EXAMPLE 3 Synthesis of Reaction Product L. Reaction Product L was prepared using Ucon Lubricant 50HB660** and 80/20 2,4- 2,6-tolylene diisocyanate (TDI). To the 5 liter reaction flask described in Example 2 supra and maintained under a nitrogen atmosphere, there were charged 4000 gms of Ucon Lubricant 50HB660. Beginning at room temperature, 174.3 gms of the TDI were added under stirring. Moderate heat was applied and the temperature of the mixture rose to 85°C over a period of two hours. The temperature of the reaction product mixture was maintained between 85°C and 90°C under continuous stirring for five hours. Upon cooling to room temperature there was obtained a yellow transparent liquid (Reaction Product L) with a viscosity of 536 centipoises at 25°C. Reaction Product L was also examined for compatibility with poly¬ ester polyols (Polyester A** and Polyester B**), with/ without polyether polyol (Niax Polyol 12-56**), and the fluorocarbon blowing agents (Freon 11B** and Freon 113**). The results of this study are described in the Table III infra. TABLE III FORMULATION 1 2 3 5 6_ 2 £ __ ____ _ 11 _ 12 Polyester A** 90.0 80.0 70.0 70.0 60.0 50.0 Polyester B** 90.0 80.0 70.0 70.0 60.0 50.0 NIAX POLYOL 12-56** 10.0 20.0 30.0 10.0 20.0 30.0 FREON 113** FREON 11B** Reaction Product I_ 10.0 20.0 30.0 10.0 20.0 30.0 20.0 20.0 20.0 20.0 20.0 20.0 Viscosity (centipoises) x 10 at 23°C N.T. N.T. N.T. 23.7 20.6 12.3 N.T. N.T. N.T. 12.3 8.04 5.20 at 35°C N.T. N.T. N.T. 15.9 12.5 9.35 ' N.T. N.T. N.T. 7.97 5.20 3.20 Observations 4 4 4 1 1 1 4 4 4 1 1 1 5 6 6 6 5 6 6 6 1 = clear 2 = slightly hazy 3 = some haze 4 = very hazy 5 = separation 6 = compatible N.T. = not busted Jjecause of separation or poor compatibility. TABLE III (cont'd.) ORMUIATIONS 13 14 15 16 17 18 19 20 21 22 23 -Li Polyester A** 90.0 80.0 70.0 90.0 80.0 70.0 Polyester B** 90.0 80.0 70.0 90.0 80.0 70.0 NIAX POLYOL 12-56** FREON 113** 10.0 10.0 10.0 10.0 10.0 10.0 FREON 11B** 8.0 8.0 8.0 8.0 8.0 8.0 Reaction Product L 10.0 20.0 30.0 10.0 20.0 30.0 10.0 20.0 30.0 10.0 20.0 30.0 Viscosity (centipoises) x 10 3 o at 23 C N.T. N.T. N.T. 12.7 12.0 N.T. N.T. N.T. N.T. 12.4 10.9 N.T. at 35°C N.T. N.T. N.T. 7.78 7.00 N.T. N.T. N.T. N.T. 7.39 5.97 N.T, Observations 4 4 4 1 4 4 4 4 4 1 4 4 5 6 5 5 6 5 5 1 = clear 2 = slightly hazy 3 = some haze 4 = very hazy 5 = separation 6 = compatible N.T. = not tested because of separation or poor compatibility. EXAMPLE 4 Synthesis of Reaction Product M. Reaction Product M was prepared using Ucon Lubricant LB285** and Isonate 125** (4,4'-MDI). To a 500 ml. reaction flask equipped as described in Example 2 and maintained under a nitrogen atmosphere, there were charged 222.5 gms of Ucon Lubricant LB285 and heated to 70°C. Under continuous stirring 56.8 gms of the 4,4'-MDI were added and the temperature of the resulting reaction mixture rose to 90°C within 10 minutes. The temperature was maintained between about 90°-95°C for four hours. There was obtained a white hazy liquid with a viscosity of 2,530 centipoises at 23°C. EXAMPLE 5 A series of hand foam experiments were conducted using Mondur F-501** and Polyester A** or Polyester B** and Reaction Products J, L and M (Examples 2-4 supra) as well as TP-90B** in a typical microcellular polyurethane foam formulation as described in Example I, and cast in an epoxy shoe sole mold. The polyester polyol/flow modifier varied from 90/10 to 60/40 and very good polyurethane parts were obtained. At the 90/10 and 80/20 polyester polyol/flow modifier ratios, the polyurethane parts tested were excellent and were characterized by smooth, strong skins. The data and results are set forth in Table IV infra. _.MPI_ TΛBI£ IV 7 R FORMULATION 1 2 3 4. 5 6 Polyester A** 90.0 90.0 90.0 90.0 80.0 80.0 80.0 70.0 Polyester B** Reaction Product J 10.0 20.0 30.0 Reaction Product L 10.0 20.0 Reaction Product M 10.0 TP-90B** 10.0 20.0 ϋ hylene Glycol 11.0 11.0 1.0 11.0 11.0 11.0 11.0 11.0 1,4 Butanediol L 5340** 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 Silicone A** 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 l_ΛBQO 33LV** 0.9 0.9 0.9 0.9 0.9 0.9 0.9 0.9 N,N,N',N'-_etra methylbutonediamine 0.3 0.3 0.3 0.3 0.3 0.3 0.3 0.3 SYNCAT M 601** 0.1 0.1 0.1 0.1 0.1 0.1 0.1 0.1 Water FREON 113** 10.0 10.0 10.0 10.0 10.0 10.0 10.0 10.0 FRIDON llB MONDU E-501** 95.3 95.3 95.3 95.3 93.6 93.6 93.6 91.9 Index 1 1 1 1 1 1 1 I TABLE IV (cont'd.) FORMULATION 1 2 3_ 4_ 5 6 7 8_ Cream Time (sec) 18 15 15 17 18 16 19 20 Rise Time (sec) 50 45 45 50 52 47 55 55 Tack Free Tine (sec) 75 75 65 75 75 68 80 105 Snap Time (sec) 120 120 120 130 140 150 160 165 Demold Time (min) 5 5 5 5 5 5 5 5 Density (g./cc.) 0.34 0.34 0.33 0.34 0.33 0.34 0.36 0.34 Hardness (Shore A) 51. 46. 49. 46. 48. 48. 46. 48. (ASTM D2240-75) C Cells per cm. 60 60 60 60 50 • 50 50 50 Observations 1 2 1 1 1 1 1 1 1 * good part - no shrinkage noted 2 = slight shrinkage 3 = cells large - also slight set at end of rise k ^ _.1l TABLE IV (cont'd.) PORMUIΛTION 9 10 11 12 13 14 15 16 17 Polyester A** 60.0 Polyester B** 90.0 90.0 90.0 90.0 80.0 80.0 80.0 80.0 Reaction Product J 40.0 10.0 20.0 Reaction Product K 10.0 20.0 Reaction Product L 10.0 20.0 TP-90B** 10.0 20.0 EUiylene Glycol 11.0 1,4 Butanediol 11.5 11.5 11.5 11.5 11.5 11.5 11.5 11.5 L 5340** 0.1 I U Silicone A** 0.2 I DΛBOO 33LV** 0.9 0.6 0.6 0.6 0.6 0.6 0.6 0.6 0.6 N,N,N',N'-tetra πκ_thy_bur___ιeditUi_Lne 0.3 SYNCAT M 601** 0.1 0.5 0.5 0.5 0.5 0.5 0.5 0.5 0.5 Water 0.2 0.2 0.2 0.2 0.2 0.2 0.2 0.2 FREON 113** 10.0 FREON 11B 6.0 6.0 6.0 6.0 6.0 6.0 6.0 6.0 MONDUR E-501** 90.2 77.8 77.8 77.8 77.8 76.1 76.1 76.1 76.1 TABLE IV (cont'd. ) FORMULATION 9 10 ___. 12 13 14 1 16 12 Cream Time (sec) 20 25 22 25 25 29 28 26 52 Rise Tine (sec) 55 65 65 65 65 70 70 50 70 Tack Free Time (sec) 120. 65 65 65 65 75 80 50 75 Snap Tine (sec) 210 75 75 73 75 75 90 75 90 Dcmold Tine (mi.n) 5 5 5 5 5 5 5 5 5 Density (g./cc.) 0.34 0.45 0.47 0.47 0.45 0.47 0.46 0.47. 0.48 Hardness (Shore A) (ASTM D2240-75) 46 51 52 60 51 '56 46 67 50 Cells per cm. 50 70 80 50 50 65 70 8 45 Observations 1 1 1 1 1 1 1 3 1 1 = good part - no slirinkago noted 2 = slight siαrinkage 3 •* » cells large - also slight set at end of rise EXAMPLE 6 In a manner similar to Example 2 supra in the preparation of Reaction Product J, there were charged 2593 gms of Butyl Carbitol** to the flask and heated to 68°C. The 80/20 TDI was added to the flask in three increments and the exotherm recorded. The total amount of 80/20 TDI added was 1393.1 gms. There was obtained a light amber liquid product with a viscosity of 6120 centipoises at 23°C (hereinafter Reaction Product J-2). Foam formulations were prepared and foamed on a Martin Sweets two-component foam machine (Model MOD.MOD 3A, The Martin Sweets Co., Louisville, KY.). One component comprised Polyester A**, Reaction Product J-2, ethylene glycol extender, surfactants (L 5340** and Silicone A**), catalysts (Dabco 33LV** and Syncat M601**), and water. The second component comprised Mondur E-501**. These experiments demonstrate the use of water blown system. Formulation 1 of Table V was used as a control. The mold temperature was maintained at approximately 35°C. Test plaques at 2 thicknesses were prepared and tested for physical properties except Ross Flex was run on the 0.50 inch thickness only. The test specimens were maintained under ambient conditions for at least one week prior to conducting the tests. At 80 Polyester A/20 Reaction Product J-2 flow modifier, the flex properties of the molded polyurethane specimen were clearly superior to the control while retaining acceptable tensile and tear properties. The data and results are shown in Table V infra. TABLE V FORMUIΛTION 2 3 Polyester A 100. 90.0 80.0 Reaction Product J-2 10.0 20.0 Ethylene Glycol 8.15 8.15 8.15 L 5340 0.1 0.1 0.1 Silicone A 0.2 0.2 0.2 nΛBOO 33 LV 0.9 0.9 0.9 N ,N , ' , N ' -tetrame hyl- 0.3 0.3 0.3 butanediamine SYNCΛT M 601 0.1 0.1 0.1 I t Water 0.4 0.4 0.4 MOtlDUR E-501 86.5 84.8 83.1 Index 1.0 1.0 1.0 Cream Tine (sec) 15. 15. 16. Rise Tine (sec) 50. 55. 57. Tack Free Time (sec) 70 75 85 Snap Time (sec) 75 80 100. TABLE V (cont'd.) FORMULATION Demold Time (min.) 3 - 31/2 31/4 4 - 41/2 EXAMPLE 7 In this Example a series of experiments were con¬ ducted using TP-90B**, Butyl Carbitol**, Ucon Lubricant 50HB660**, and Reaction Product J-3 (preparation of which is described hereinafter). In these experiments, the polyether monoalcohol, i.e., Butyl Carbitol and Ucon Lubricant 50HB660, were employed in the polyol resin portion and reacted with the isocyanate component in a "one step" process. Inasmuch as Reaction Product J (Example 2), Reaction Product J-2 (Example 6), and Reaction Product J—3 (Example 7) involved the addition reaction of a weight ratio of 13 parts of Butyl Carbitol to 7 parts of 80/20 TDI, there were employed 13 parts of Butyl Carbitol and 20 parts of Reaction Product J-3 in the following experiments documented in Table VI and VII infra. Similarly, since Reaction Product K (Example 3) involved the addition reaction of a weight ratio of 19.2 parts of Ucon Lubricant 50HB660 and 0.8 part of 80/20 TDI, there were employed 19.2 parts of Ucon Lubricant 50HB660. In a manner similar to Example 5 supra in the preparation of Reaction Product J-2, there were charged 6500 gms of Butyl Carbitol to a 12 liter flask and heated to 68°C. The 80/20 TDI was added to the flask in three increments and the exotherm recorded. The total amount of 80/20 TDI added was 3500 gms. There was obtained a clear, slightly viscous, medium amber liquid product with a viscosity of 7010 centipoises at 21°C and 2537 centipoises at 35°C (hereinafter Reaction Product J-3). Reaction Product J-3, TP-90B, Butyl Carbitol and Ucon 50HB660 were examined for compatibility with Polyester A** with/without ethylene glycol extender. The results are set forth in Table VI infra. Hand foam experiments were conducted using TP-90B, Reaction Product J-3, Butyl Carbitol, and Ucon Lubricant 50HB660 with Polyester A** in typical foam formulations. The foam made with Butyl Carbitol was cheezy and did not develop any strength with cure, while the foam made with unreacted Ucon Lubricant 50HB660 had a good, strong skin. Plaques were prepared by the hand foaming technique and cast into an epoxy mold held at about 30-35°C. It was noted that the Ucon Lubricant 50HB660 and the Reaction Product J-3 plaques exhibited superior flex properties when compared to a blank without flow modifier and with a plaque containing TP-90B. Data and results are shown in Table VII infra. TABLE VI FORMULATION 1 2 4, 5 6 Polyester A 80.0 80.0 80.0 80.0 80.0 80.0 TP-90B** 20.0 20.0 BUTYL CARBITOL** 13.0 13.0 UCON Lubricant 50HB660** 19.2 19.2 Reaction Product J-3 Ethylene Glycol 11.0 11.0 11.0 Viscosity (centipoises) (x 10 3 ) at 23°C. 6.72 3.72 8.40 4.06 22.5 11.0 Observations 1 2 1 1 3 3 1 = clear and compatible 2 - hazy 3 = separated TABLE VII FORMULATION 1 2 3 4_ 5 Polyester A 80.0 TP-90B** 20.0 — Reaction Product J-3 20.0 BUTYL CARBITOL** 13.0 UCON 50HB660** *"* — 19.2 - Ethylene Glycol 11.0 11.0 11.0 11.0 11.0 L-5340** 0.1 0.1 0.1 0.1 0.1 Silicone A** 0.2 0.2 0.2 0.2 0.2 DABCO 33LV** 0.9 0.9 0.9 0.9 0.9 N,N,N' ,N'-tetramethylbutane- diamine 0.3 0.3 0.3 0.3 0.3 SYNCAT M 601** 0.1 0.1 0.1 0.1 0.1 FREON 113** 10.0 10.0 10.0 10.0 10.0 MONDUR E501** 93.6 93.6 111.2 95.7 93.6 Index 1.0 1.0 1.0 1.0 1.0 TABLE VII (cont'd.) • FORMULATION 1 1 3 i 5 Plaque Density (g./cc) 0.52 0.52 0.49 0.50 0.49 Cells per cm. >60 >70 >60 70 • >1Q Hardness (Shore A) (ASTM D2240-75) 71 74 67 72 84 Ross Flex at -18°C (x 10 3 cycles) at 500% cut growth 73 .4 >210 0.2 210 5.4 Observations 1 = good part - no shrinkage noted 2 = cheezy - no strength EXAMPLE 8 A series of foam formulations comprising Reaction Product J-3, Ucon Lubricant 50HB660**, or TP-90B** were prepared and run on a Desma two component foam machine (Desma erke GMbH, 2807, Achim bei Bremen, Germany). Component A of the formulations comprised Polyester A** with/without Reaction Product J-3, Ucon Lubricant 50HB660 or TP-90B plus ethylene glycol extender, surfactants, catalysts, and fluorocarbon blowing agent; Component B consisted of the polyisocyanate (Mondur E-501**). Component A was maintained at 30°C and Component B at 32°C in pressurized tanks under constant agitation to prevent phase separation. The foam mix was cast into aluminum mold cavities 6 inches x 8 inches x 0.5 inch thick which was held at a temperature of 46°C. Test plaques of varied densities were prepared. The data and results are shown in Table VIII infra. TAME VIII FORMULATION 1 2 3 4_ 5 Polyester A** 80.0 90.0 80.0 90.0 80.0 TP-90B** 20.0 Reaction Product J-3 10.0 20.0 LOON Lubricant 5011B660** 10.0 20.0 Ethylene Glycol 11.0 11.0 11.0 11.0 11.0 L5340** 0 .1 0.1 0.1 0.1 0.1 Silicone A** 0. .2 0.2 0.2 0.2 0.2 DABCO 33LV** 0 , .9 0.9 0.9 0.9 0.9 N,N,N',N'-tetra- metn lbutanediamine 0. .3 0.3 0.3 0.3 0.3 SYIJCΛT M 601** 0 , .1 0.1 0.1 0.1 0.1 FREON 113** 10. ,0 10.0 10.0 10.0 10.0 MONDUR E501** 94 , ,2 96.1 94.4 97.2 96.7 Index 1. ,0 1.0 1.0 1.0 1.0 Cream Tine (sec) 8-10 6 6 6 5 Rise Time (sec) 28 25 30 18 18 Tack Free Time (sec) 35 30 35 30 30 Snap Time (sec) 70 60 70 60 70 Demold Time (min) 3 3 3 3 3 TABU- VIII (cont'd.) EXAMPLES 9 - 26 Flow modifiers (Reaction Products A, C, G, H and K) were examined for compatibility with Isonate 240**, Mondur E-501**, and Mondur PF** (isocyanato-terminated prepolymers) . Each flow modifier was tested at three concentrations by weight (90 parts isocyanate/10 parts flow modifier, 80 parts isocyanate/20 parts flow modifier and 70 parts isocyanate/30 parts flow modifier) . Karl Fischer tests (ASTM D-2849) for % H θ show no detectable levels of water. The samples were prepared by weighing into a test tube the following: 90/10 80/20 70/30 Flow Modifier (gms) 1. 5 3. 0 4.5 Isocyanate (gms) 13.5 12.0 10.5 The test tubes were tightly capped and heated to 70°C for 20-30 minutes. The samples were agitated by vigorous shaking while hot and observations with respect to miscibility at this temperature (70°C) were made. The samples were cooled in a constant temperature bath to 25°C for 4-6 hours and the observations at 25°C were then made. Compatible mixtures were then further cooled in a constant temperature bath to 20°C, 15°C, 10°C, 5°C, 0°C, -5°C, and -10 β C, respectively, and allowed to remain at each temperature for a minimum of 24 hours. Observations regarding separation, cloud point (the temperature when haze is first observed), and freezing point (the temperature when crystals are first observed) were made at each temperature interval. A 15 gram sample of Isonate 240, Mondur E-501, Mondur PF was tested as controls. Hazy mixtures at 25°C were subjected to further treatment as indicated in the footnotes of Tables IX, X, and XI. The data are set forth in Tables IX, X, and XI. OMPI • WIPO TABLE IX COMPATIBILITY AND FREEZE POINT DETERMINATION IN ISONATE 240 CONCENTRATION COMPATIBILITY SEPARATION CLOUD FREEZE No . FLOW MODIFIER BY WEIGHT @ 70°C @25°C POINT , °C POINT , °ι C POINT , 9. Reaction 10 YES YES (1) 0°C 0°C Product A (Butyl Carbitol/ 20 YES YES (1) 0°C 0°C TDI) (1) 30 YES YES 5°C 0°C 0°C (1,4) 10. Reaction 10 YES SI. HAZE 20°C > 5°C 0°C Product C (Methyl Carbitol/ 20 YES SI. HAZE(1,4) 20°C. 5°C 0°C TDI) (1,4) 30 YES SI. HAZE 20°C 0°C 0°C 11. Reaction 10 HAZY WHITE (1/4) N.T. (6) Product G (Butyl Carbitol/ 20 HAZY WHITE^ 1 ' ^ N.T. (6 > Isonate 125M) 30 HAZY WHITE^' ) N.T. (6) TABLE IX (cont'd.) COMPATIBILITY AND FREEZE POINT DETERMINATION IN ISONATE 240** CONCENTRATION COMPATIBILITY SEPARATION CLOUD FREEZE Q No. FLOW MODIFIER BY WEIGHT @ 70°C @25°C ' POINT, °C POINT, °C POINT, . C 12- Reaction 10 YES YES M 5°C 5°C Product- H (Butyl Carbitol/ 20 YES YES < 1 - > 5°C 5°C Mondur MR) 30 YES YES ^ 5°C 0°C • 13. Reaction 10 YES YES ) 0°C 0°C it Product L (UCON 50HB660/TDI) 20 YES YES M 0°C -5°C 30 YES YES (1) -10°C -10°C ) 14. ISONATE 240** NONE - - 4 U VC (5 4 o υ „C(5) Control TABLE IX (cont'd.) FOOTNOTES: (1) Test tube heated to 70 C for 20-30 minutes, the contents agitated by vigorous shaking; and then allowed to cool to 25°C and maintained thereat for 4-6 hours. Compatible mixtures were furhter cooled as stated previously. (2) These mixtures were not compatible at 70°C and some reaction with the isocyanate was observed. It appears that catalyst may have been present in the mixture. The flow modifier was analyzed for % 11,0 and showed no detectable levels of water present. (3) Test tube was reheated to 80°C, contents were reagitated and held at 80°C for one hour, and then allowed to cool to 22°C for at least 4-6 hours. (4) Test tube was reheated to 80°C. , contents were reagitated and held at 80°C for 16 hours, and then allowed to cool for at least 16 hours. (5) After 16 hours at 4°C control is a solid mass indicating that crystal formation occurs appreciably above 4°C. (6) Not tested. TABLE X COMPATIBILITY AND FREEZE POINT DETERMTNATIOiM IN MONDUR E-501 CONCENTRATION COMPATIBILITY SEPARATION CLOUD FREEZE No. FLOW MODIFIER BY WEIGHT @ 70°C @25°C POINT, °C POINT ' , °C POINT, C (1) 15. Reaction 10 YES YES 0°C . 0°C Product A (1) ' (Butyl Carbitol/ 20 YES YES 0°C -5°C TDI) (X) 30 YES YES 5°C -5°C 16, Reaction 10 YES YES* 1* " 0°C -5°C Product C (Mathyl Carbitol/ 20 YES YES ^ - 0°C 0°C TDI) ,„ (1) 30 YES YES 0°C -5°C 17, YES (1,2) Reaction 10 YES - 15°C -5°C Product G (Butyl Carbitol/ 20 Slight HAZY (1,2) >25°C -5°C Isonate 125M) Haze 30 Slight HAZY l 1 ' 2 ' - >25°C -5°C Haze TAB E X. (cont'd.) COMPATIBILITY AND FREEZE POINT DE_ * EI ENATIOSl IN MONDUR E-501 OONCI-NTRATiα. COMPATIBILITY SEPARATION C CLLOOUUDD FREEZE No. FLOW MODIFIER BY WEIGHT 0 70°C : @25°C POINT, °C POINT, C o 18. Reaction 1U YES YES^ ) 10 C 5°C Product H (Butyl Carbitol/ 20 ' YES YES (1) 5°C. 0°C Mondur MR) 30 YES YES ( *• -) 5°C 0°C 19. Reaction 10 YES YES (1 .- * - • -5°C Product L (UCON 50HB660/TDI) 20 YES YES * 1 - ) -5°C -10°C 30 YES YES f 1 - 1 -5°C -10°C 20. E-501 None - - 4°C (3) 4θ c (3) Control (1) See footnote (1), Table IX. (2) See footnote (2), Table IX. TABLE XI COMPATIBILITY AND FREEZE POINT DETERMINATION IN MONDUR PF CONCENTRATION COMPATIBILITY SEPARATION CLOUD FREEZE No. FLOW MODIFIER BY WEIGHT @ 70°C @25°C POINT, °C POINT, °C POINT, . C 21, Reaction 10 YES YES 1 N.N. (2) 5°C Product A (Butyl Carbitol/ 20 YES YES* 1 '' - N,N. (2) 0°C TDI) 30 YES YJV£ j (l) 5°C N.N. (2) 0°C I - 0 22. I Reaction 10 YES YES* 1 * N.N. (2) 5°C Product C (Mathyl Carbitol/ 20 YES YES- 1 ' - 5°C 5°C TDI) 30 YES YES- 1' 20°C 20°C 0°C (2) 23. Reaction 10 YES YES* 1 * * - N.N. 5°C Product G (Butyl Carbitol/ 20 YES YES* 1 ' 3) - 20°C 5°C Isonate 125M) TABLE XI (cont'd.) COMPATIBILITY AND FREEZE POIWT DETERMINATION IN MONDUR PF CONCENTRATION COMPATIBILITY SEPARATION CLOUD FREEZE No. FLOW MODIFIER BY WEIGHT @ 70°C @25°C POINT, °C POINT, °C POINT, . C 24 Reaction lϋ YES YES* 1 * 15°C 5°C Product H (Butyl Carbitol/ 20 YES YES* 1 * 5°C * 5°C Mondur MR) o 30 YES 1 ' : 5°C 0 C 25. Reaction 10 YES YES* 1 * N.N. W 10°C • Product L (UCON 50IIB660/TDI) 20 YES YES* 1 * 5°C 5°C 30 YES YES(l) N.N.* 2 * 0°C 26. MONDUR PF** NONE - - N.N.* 2 * 10°C* ) Control TABLE XI (cont'd.) FOOTNOTES: (1) Test tube heated to 70 C for 20-30 minutes, the contents agitated by vigorous shaking, and then allowed to cool to 25°c and maintained thereat for 4-6 hours. Compatible mixtures were further cooled as stated previously. (2) None notices. (3) Test tube was reheated to 80°C, contents were reagitated and held at 80°C for one hour, and then allowed to cool to 22°C for at least 4-6 hours. (4) After 16 hours about half solid mass. EXAMPLE 27 Preparation of Solid Polyurethane Elastomer. To a 500 ml reaction flask there were charged 200 gms of Niax Diol 12-56** and 67 gms of Reaction Product I. The resulting mixture was then degassed in a vacuum of 5-10 mm Hg at 100°C. for 1.5 hours. Thereafter, 10.0 gms of ethylene glycol and 0.3 g of phenylmercuric propionate catalyst (Netasol DPG; 80% dipropylene glycol, 20% active mercury compound) were added, and the resulting mixture was allowed to cool to 30°C, where it was subjected to a vacuum of 20 mm Hg for five minutes. The vacuum was broken, and a total of 98 gms of MONDUR PF** was added at 30°C. with good agitation. The reaction product mixture was degassed quickly and cast into a warm 1/4" aluminum mold cavity having a dimension of 6" x 8". The reaction product gelled in 5-6 minutes. There was obtained a strong, tough polyurethane elastomer exhibiting a Shore A hardness of 55-60, and was found to possess an electrical resistance that was appreciably lower than the product made from the same formulation but not containing Reaction Product I. This property of electrical resistance imparts utility in elastomeric applications requiring antistatic properties. EXAMPLE 28 A flexible polyether/polyurethane foam was prepared from Niax Polyol 11-27**, Reaction Product K, and the 80/20 mixture of 2,4- and 2,6-tolylene diisocyanate. The following foam recipe was employed Niax Polyol 11-27 200 gms Reaction Product I 100 gms Silicone Surfactant L-548** 1.0 gm Diethanolamine 1.0 gm Water 5.6 gms Dabco 33 LV** 0.6 gm Dibutyltin dilaurate : 0.02 gm 80/20 mixture of 2,4- and 2,6-tolylene diisocyanate : 69.0 gms (Isocyanate index — 105) The ingredients were mixed at about 1500 rp by means of a laboratory mixer, poured into a paper mold, allowed to rise and cure at room temperature for about 30 minutes. The resulting foamed product was dry to the touch. After one week, the foam was cut into one inch thick slabs. The foam exhibited good strength characteristics and was found to exhibit a substantially lower electrical resistivity than the foamed product made from the corresponding fomulation without flow modifier. This property highlights the utility of the foamed product as an antistatic carpet underlayment in computer rooms and the like.

Claims: HAT IS CLAIMED IS: 1. A polyurethane product prepared by reacting a mixture comprising (a) a polyol having a molecular weight in the range of from about 1800 to about 10,000, (b) an organic polyisocyanate, (c) optionally, a chain extender, and (d) a catalyst for the NCO/active hydrogen reaction, in the presence of (e) from about 5 to about 50 parts by weight, per 100 parts by weight of said polyol, of a non-hydroxyl flow modifier, said flow modifier having the following characteristics: (i) a boiling point above about 150°C, (ii) normally-liquid or low melting solid forming a compatible liquid with said polyol, (iii) an average molecular weight upwards to about 3000, (iv) consisting essentially of carbon and hydrogen atoms in the form of monovalent or polyvalent hydrocarbon groups; and from 1 to 5 urethane ( groups; and from 1 to 25 oxyalkylene groups per urethane group. 2. The polyurethane product of claim 1 wherein said flow modifier is of the group consisting of Formula I infra: O >xyalkylene)-χ—OC I!NH R2 wherein the oxyalkylene unit contains from 2 to 4 carbon atoms in the oxyalkylene chain; wherein each R, individually, represents a monovalent acyclic, alicyclic or aromatic group; wherein x is at least one and upwards to 25; wherein z_ is from 1 to 5; and wherein R_2. represents a monovalent acyclic, alicyclic or aromatic group when z_ is 1 or a polyvalent acyclic, alicyclic or aromatic group when z_ is 2 to 5, the valence of R>_ being equal to the value of z; and Formula II infra: OMPI II O O I! I! - oxyalkylene χ~ OCNH- -Rl- -NHCOR3), wherein R, J and oxyalkylene have the meanings assigned in Formula I supra, wherein R-^ is a polyvalent acyclic, alicyclic, or aromatic group having the polyvalent meanings assigned to R^ of Formula I supra, the valence of Rl being equal to £ plus y_, wherein each R^ individually is an acyclic, alicyclic or aromatic group; wherein y_ has a value of 1 to 2; and wherein £ has a value of 1 to 2. 3. The polyurethane product of claim 2 wherein said product is of the group consisting of cellular products and solid products. 4. The polyurethane product of claim 3 wherein the reaction is effected in the presence of from 5 to 35 parts of said flow modifier and wherein said product is a micro¬ cellular polyurethane. 5. The polyurethane product of claim 4 wherein the reaction is effected in the presence of from 10 to 30 parts of said flow modifier and wherein said product is an integral skin microcellular elastomer. 6. The polyurethane product of claim 5 wherein said organic polyisocyanate is a quasi-prepolymer of a 4,4'- diphenylmethane diisocyanate and wherein said product is in the shape of a shoe sole. 7. The polyurethane product of claim 3 wherein the reaction is effected in the presence of from 20 to 50 parts of said flow modifier and wherein said product is a polyurethane foam. 8. The polyurethane foam of claim 7 characterized by its capability to conduct static electricity. 9. The polyurethane product of claim 3 wherein the reaction is effected in the presence of from 5 to 20 parts of said flow modifier and wherein said product is a soft polyurethane elastomer. 10. The polyurethane elastomer of claim 9 character¬ ized by its improved coefficient of friction. 11. The polyurethane product of claim 2 wherein the oxyalkylene units in Formulas I and II are oxyethylene units. 12. A polyurethane product prepared according to claim 1 wherein said flow modifier has the structural formula: O 0 II II R f —{oxyC2-C3alkylenehr-OCHN-A-NHCO-fC2-C3alkyleneoxy) x —R' wherein each R', individually, is Cχ-Csalkyl or a C5-C7- cycloalkyl; wherein A represents Cχ-Csalkylene, unsub- stituted and Cχ-C3alkyl-substituted phenylene, divalent (4,4'- and 4,4'-/4,2'-)diphenylenemethane, the divalent hydrogenated counterparts of unsubstituted and Cχ-C3alkyl- substituted phenylene or (4,4'- and 4,4'-/4,2'-)- diphenylenemethane; wherein X is at least one and upwards to 25; and wherein the oxyC2~C3alkylene unit is oxy¬ ethylene, oxypropylene, oxyethyleneoxypropylene, or mixtures thereof. 13. The polyurethane product prepared according to claim 12 wherein the mixture includes a blowing agent and from 10 to 30 parts of flow modifier and wherein said product is an integral skin microcellular elastomer. 14. A polyurethane foamed product prepared according to claim 12 wherein the mixture includes a blowing agent and from 20 to 50 parts of flow modifier. OMPI 15. The polyurethane product of claim 12 wherein the mixture includes a blowing agent and from about 5 to 20 parts of flow modifier and wherein said product is a microcellular elastomer. 16. The polyurethane product of claim 12 wherein the oxyC2*-C3alkylene unit in the formula is oxyethylene. 17. The polyurethane product of claim 13 wherein the divalent A variable in the flow modifier formula is tolylene or diphenylenemethane and wherein said product is •a cellular product. 18. The cellular product of claim 17 wherein the oxyC2~C3alkylene unit in the formula is oxyethylene. 19. A polyurethane elastomer product prepared according to claim 1 wherein the reaction is effected in the presence of from 5 to 20 parts of flow modifier having the structural formula: O O II H R'— oxyC2-C3alkyleneJ-j^-OCNH-A-NHCO- C2-C3alkyleneoxy)<r-R* wherein each R', individually, is Cχ-Csalkyl or a C5-C7- cycloalkyl; wherein A represents Cχ-C8alkylene, unsub¬ stituted and Cχ-C3alkyl-substituted phenylene, divalent (4,4'- and 4,4'-/4,2'-)diphenylenemethane, the divalent hydrogenated counterparts of unsubstituted and Cχ-C3alkyl- substituted phenylene or (4,4'- and 4,4'-/4,2'-)- diphenylenemethane; wherein x is at least one and upwards to 25; and wherein the oxyC2"C3alkylene unit is oxyethylene, oxypropylene, oxyethyleneoxypropylene, or mixtures thereof. 20. The polyurethane elastomer product of claim 19 wherein the oxyC2-C3alkylene unit in the flow modifier formula is oxyethylene. 21. As an isocyanate curable composition, for the manufacture of polyurethane products, a compatible homogeneous liquid mixture comprising (a) a polyol as defined in claim 1, and (b) from 5 to about 50 parts per 100 parts of polyol, of a flow modifier as defined in claim 1. 22. The homogeneous liquid mixture of claim 21 which contains a chain extender. 23. The homogeneous liquid mixture of claim 21 wherein said flow modifier is defined in claim 2. 24. The homogeneous liquid mixture of claim 21 wherein said polyol is a polyether polyol. 25. The homogeneous liquid mixture of claim 21 wherein said polyol is a polyester polyol. 26. As an isocyanate curable composition, for the manufacture of polyurethane foamed products characterized by its capability to conduct static electricity, a compat¬ ible homogeneous liquid mixture comprising (a) a polyol as defined in claim 1, and (b) from 20 to about 50 parts, per 100 parts of polyol, of a flow modifier as defined in claim 2. 27. As an isocyanate curable composition, for the manufacture of integral skin microcellular polyurethane products, a compatible homogeneous liquid mixture compris¬ ing (a) a polyol as defined in claim 1, and (b) from 10 to about 30 parts, per 100 parts of polyol, of a flow modifier as defined in claim 2. 28. The homogeneous liquid mixture of claim 27 which contains a chain extender. 29. As an isocyanate curable composition, for the manufacture of soft polyurethane elastomer products, a compatible homogeneous liquid mixture comprising (a) a polyol as defined in claim 1, and (b) from 5 to about 20 parts, per 100 parts of polyol, of a flow modifier as defined in claim 2. 30. As an isocyante curable composition, for the manufacture of polyurethane products, a compatible homogeneous liquid mixture comprising (a) a polyol as defined in claim 1, and (b) from 5 to about 50 parts, per 100 parts of polyol, of a flow modifier defined by the formula of claim 12. 31. The homogeneous liquid mixture of claim 30 which contains a chain extender. 32. The homogeneous liquid mixture of claim 30 wherein the oxyC2~C3alkylene group in the flow modifier formula is oxyethylene. 33. The homogeneous liquid mixture of claim 30 wherein the divalent A variable of the flow modifier formula is tolylene. 34. A multipackage curable system useful in the manufacture of polyurethane products comprising Component A and Component B, (a) wherein said Component A is a mixture of polyol and flow modifier in amounts which provide from about 5 to about 50 parts by weight of flow modifier per 100 parts by weight of polyol, (i) said polyol having a molecular weight of from about 1,800 to about 10,000, and (ii) said flow modifier being defined by claim 2; (b) wherein said Component B is an organic polyisocyanate. 35. The multipackage curable system of claim 34 useful in the preparation of microcellular and solid elastomers wherein (a) said Component A contains from about 5 to 35 parts of flow modifier per 100 parts of polyol, wherein said polyol contains from 2 to 3 hydroxyl groups, wherein said flow modifier is of the group consisting of Formula III infra: III O O I! * II R--foxyC2-C3alkylene)χ—OCNH-A-NHCO-C2-C3alkyleneoxy χ-R- wherein each R_J_, individually, is of the group consisting of alkyl, a C5-C7cycloalkyl, and aralkyl; wherein A represents Cχ-Csalkylene, a cyclohexylene, Cχ-C4cyclo- hexylenelalkylene, a phenylene, a divalent diphenylene- methane, and the divalent hydrogenated counterparts there¬ of; wherein JC is at least one and upwards to 25; and • wherein the oxyC2~C 3 alkylene unit is oxyethylene, oxypropylene, oxyethyleneoxypropylene, ormixtures thereof; and Formula IV infra: IV O O R' {oxyC2-C3alkylene,-χ- OC IINH A NHCIIOR• wherein R _, A, x^ and oxyC 2 ~C^alkylene have the meanings assigned in Formula III above; and wherein said Component A includes a chain extender; and wherein (b) said organic polyisocyanate in Component B is a quasi-prepolymer. 36. The multipackage curable system of claim 35 wherein said polyol has a molecular weight of from about 2000 to 5000, and wherein said quasi-prepolymer is the reaction product of a diphenylmethane diisocyanate and polyol. 37. The multipackage curable system of claim 36 wherein said flow modifier is of the group consisting of Formula V infra: V 0 II R'—(oxyC2~C3alkylene —OCNH 2,4-and/or 2,6-tolylene 2 wherein each R' , individually, is of the group consisting OMPI " of alkyl and phenyl; wherein x is from 2 to 8; and wherein oxyC2-C-*,alkylene is oxyethylene, oxypropylene, or oxy¬ ethyleneoxypropylene; and Formula VI infra: VI O II R* (oxyC2-C3alkylene χ —OCNH- wherein _ represents a 4,4'-and/or 2,4'-diphenylenemethane or C4-C6alkylene; and wherein R_, jc, and the oxyC2~C3- -alkylene unit have the meanings assigned in Formula V above. 38. The multipackage curable system of claim 34 use¬ ful in the manufacture of foamed polyurethane products comprising Component A and Component B, (a) wherein said Component A is a mixture of polyol and flow modifier and additionally, a blowing agent, said flow modifier being present in an amount which provides from about 5 to about 50 parts by weight of flow modifier per 100 parts by weight of polyol, (i) said polyol having a molecular weight of from about 1,800 to about 10,000, and (ii) said flow modifier being defined by claim 2; (b) wherein said Component B is an organic polyisocyanate. 39. The multipackage curable system of claim 38 wherein said flow modifier * of Component A is defined by Formula V of claim 37. 40. The multipackage curable system of claim 39 wherein the oxyC2~C3alkylene units of Formula V are oxyethylene units.

Inventors: HOSTETTLER FRITZ, HOSTETTLER, FRITZ
Applicants: HOSTETTLER FRITZ, PIRRI JAQUELYN P, HOSTETTLER, FRITZ, PIRRI, JAQUELYN, P.
Application year: 1984
Main classification: B28B3
IPC codes: C08K5