STABLE LATEXES HAVING PHOSPHORUS-CONTAINING SURFACE GROUPS

Abstract: A modified latex composition useful in the coating of substrates with inorganic fillers. A latex particle having -PO(O)2 groups intimately bound to the particle's surface formed by the emulsion polymerization of a latex with a phosphorus-containing compound. Also a method of preparing a composite sheet and a paper coating latex with the modified latex is provided.

Description: STABLE LATEXES HAVING PHOSPHORUS- CONTAINING SURFACE GROUPS The present invention relates to a modified latex having phosphorus-containing surface groups. This modified latex is useful as a coating for substrates and as a binder in aqueous systems containing inorganic fillers commonly employed in paper coatings, carpet backings, wailboards and other substrates. In general mineral coatings or fillers are applied to paper to cover the individual fibers of the paper and fill interstices between fibers, thus rendering the surfaces of the paper more level and uniform in texture. Mineral coatings or fillers are also employed in aqueous dispersions of fiber to form a composite sheet. This process is described in U.S. Patent No. 4,225,383. In order to suitably bind the mineral coatings or fillers to the substrate, latexes are employed. Latexes bind the filler such that it will not be removed by the pull of printing ink. Besides printability, the latexes also help to influence many other qualities of the paper such as appearance and strength. The ability of the latex to function as a binder is very important to the final quality of the finished substrate, such as dry and wet pick in paper coatings. Generally in the art of paper coating, the latex component is admixed with a filler in an aqueous suspension and mechanically applied to the substrate to be coated. Alternatively, in the art of composite sheet formation, a latex is added to an aqueous disper¬ sion of fiber and inorganic filler which is destabilized to form a fibrous agglomerate which is deposited onto a screen or other porous means to form a sheet therefrom. For various reasons, it is desirable to maximize the retention level of inorganic fillers on the substrate to be coated. One way to accomplish this is to use a latex which interacts well with the filler. Improved interaction increases filler retention which has the benefits of reducing the level of flocculant required to destabilize the filler from solution and of reducing the stickiness of the filler and latex to equipment which occurs when high flocculant levels are used. This, in turn, reduces the maintenance needed in the manufacture of composite sheets. The latter benefit is also realized with respect to cleaning up residual filler left behind in the aqueous solution by the latex after deposition. Another advantage to increasing filler retention and thereby filler content is, of course, economical, as higher filler content usually translates to less expensive final products. It is well known in the art, however, that while a particular amount of filler can enhance the properties of a coated product or composite sheet, higher amounts can cause loss of strength due to decreased structural integrity. It, therefore, would be desirable to develop a method to increase filler retention without reducing physical properties or ideally to increase the strength of substrates with higher filler levels. Accordingly, it would be desirable to develop a latex which had improved interaction with inorganic fillers to enable better retention of the fillers. The present invention provides a modified latex composition having a phorphorus-containing surface group, the latex composition comprising at least one ethylenically unsaturated monomer which is emulsion polymerized to form a latex polymer and a phosphorus- -containing compound comprising a -PO(0) 2 group which is intimately bound to the surface of the latex, said phosphorus-containing compound being a phosphonate and/or phosphate compound. The present invention further provides a method for preparing a composite sheet comprising the steps of adding from 2 to 30 percent of the modified latex composition to an aqueous dispersion comprising an inorganic filler and a water-dispersible fiber, colloidally destabilizing the resulting mixture to form a fibrous agglomerate in aqueous suspension, distributing and draining the aqueous suspension on a porous support to form a wet web, and drying the web to form a sheet. Even further, the present invention provides a method of paper coating comprising the steps of adding from 2 to 30 percent of a modified latex composition to an aqueous dispersion of at least one inorganic filler and coating paper with the latex-containing composition. The modified latex of the subject invention can be employed in the formation of composite sheets or as the latex component in a latex coating composition. Generally, the modified latex is formed by using typical latex formulations and methods known in the art with the exception that a phosphorus-containing compound is emulsion copolymerized with the conventional latex mon¬ omers such that -PO(0) 2 groups become intimately bound to the surface of the latex particles. The conventional monomers suitable for the pra¬ ctice of this invention with regard to the latex component comprise ethylenically unsaturated synthetic monomers known in the art. The ethylenically unsaturated monomers are of the general formula CH 2 =CHR wherein R is H, alkyl, aryl, nitrile ester, acid or halogen. The preferred monomers are styrene, butadiene, butyl acrylate and other acrylic esters, vinylidene chloride, vinyl chloride, vinyl acetate and combinations thereof. Poly(styrene- butadiene) is a preferred latex polymer. The phosphorus-containing compounds employed in the practice of this invention generally comprise those compounds containing a -PO(0) 2 group. Preferred phosphorus-containing compounds are of the general structural formula: 0 ιι R-P-0 ( I ) i _, O where R can be a radical such as alkyl, alkylphenyl, alkylamine, fatty alcohol, fatty acid, glycol, polyglycol. However, the principal constituent is the -PO(0)_ group of the phosphorus-containing compound. Therefore, the range of phosphorus containing compounds which can be employed is large. Those latex compositions which have the -PO(0) 2 group intimately bound to the surface of the latex (i.e. to the latex particle's surface) are deemed to be within the scope of this invention. "Intimately bound" to the surface of the latex means chemically or physically bound, such as by covalent bonding or adsorption, such that the -PO(0) 2 group is not desorbed into aqueous medium on diluting or formulating the latex with other components. Preferably the phosphorus containing group is irrevers¬ ibly bound to the latex surface. Exemplary of the phosphorus-containing compounds are derivatives of phosphoric acid; salts of phosphoric acid esters such as alkylphosphates and alkylphenyl phosphates; phosphorus-containing quaternary ammonium surfactants; phosphorus-containing fluoroalcohol based surfactants; derivatives of polyphosphoric acid such as Na 5 R 5 (P_0 10 ) 2 where R is either 2-ethylhexyl or capryl; polymerizable phosphonic acid and phosphoric acid monomers and/or polymerizable, monomeric derivatives thereof such as PO(OH) 2 CH 2 N(CH 2 CHCH 2 ) 2 ; free radical initiators such as K 4 P 2 0 g (potassium peroxydiphosphate) which can give rise to bound P0(0H) 2 groups on the sur¬ face of the latex particles; and phosphated polyethylene oxide esters. In general, a phosphate ester surfactant compound can be used which is a mono-, di- or tri-ester having the following general structural formulas: O O 11 R(OC 2 H 4 ) n O-P-0(C 2 H 4 0) n R (III) OH O II R(OC 2 H 4 ) n O-P-0(C 2 H 4 0) n R (IV) 0(C 2 H 4 0) n R wherein R is an alkyl, alkylphenol, alkylamine, fatty acid, fatty alcohol, glycol or polyglycol and n is greater than 3. One such phosphate ester family would be a phosphated nonylphenol alkoxylate; in partic¬ ular, a phosphated nonylphenol ethoxylate. A suitable phosphate ester surfactant compound is commercially available through the GAF Corporation under the trade name GAFAC ®. The GAFAC surfactants are complex phosphate esters of nonionic surfactants of the ethylene oxide- adduct type. These anionic products are mixtures of mono- and diesters. They are soluble and compatible in solutions of electrolytes and maintain emulsifying properties over a broad pH range. The modified latex of the subject invention is prepared such that the latex particle has -PO(0) 2 groups copolymerized or bound to its surface. One advantage of the copolymerized groups, besides the obvious enhancement of latex stability, is that they are irreversibly attached to the latex particle surface and as such are not desorbed into the aqueous medium on diluting or formulating the latex with other components. This latterx characteristic is particularly important inasmuch as it is this copolymerized or bound -PO(0) 2 surface group which causes the desired inter- action between the latex and fillers with multi-valent ions to occur. The emulsion polymerization of the phosphate modified latex of the subject invention can be performed using techniques generally recognized in the art. Free radical polymerization initiators can be employed, such as persulfates and peroxydiphosphates. The latter initiator is particularly useful because it provides a means to obtain the copolymerized or bound -PO(0) 2 surface groups pertinent to this invention. Chain transfer agents such as carbon tetrachloride and t-dodecyl mercaptan, and seed, latexes such as a styrene/- acrylic acid can also be employed. The introduction of a seed latex has been found desirable to control par¬ ticle size and surface ar^. for the incorporation of the desired amount of phosphorus-containing compound. In general, the emulsion polymerization may be effected by introducing a mixture of the latex monomer(s) and the phosphorus-containing compound in appropriate proportions into an aqueous solution contain¬ ing the seed, initiator and chain transfer agent. In particular, the phosphorus-containing compound comprises from 2 to 15 parts per hundred parts latex polymer prepared (phr) in the total mixture, more preferably, from .3 to 8 phr. It is possible, and in some situations desirable, to use two of the types of phosphorus-con- taining compounds, one being a polymerizable compound such as a comonomer which becomes covalently bonded in the latex polymer and the other being a compound which becomes physically bound in the latex polymer such as phosphate ester surfactant compound. In particular, it has been found desirable for paper coating compositions according to the present invention which comprise phosphate ester surfactant compounds physically bound in the latex to also contain an amount of a polymerizable monomer, • polymerized into the latex polymer which monomer provides a surface -PO(0) 2 group. Such combination provides better, more uniform coatings in some coating processes. An ,β - ethylenically unsaturated carboxylic acid also can be used in place of the polymerizable phosphorus-containing monomer when preparing coating compositions employing the phosphate ester surfactant compounds. Preferably, when the phosphorus-containing compound is a comonomer polymerized into the latex polymer and is used in combination with a phosphate ester sur¬ factant compound, the latex polymer will contain from 0.5 to- 5.0 percent by total weight polymer of the phosphorus- -containing comonomer, more preferably from 1.0 to 3.0 per¬ cent by weight. When an , β ethylenically unsaturated carboxylic acid comonomer is polymerized into the latex polymer, similar amounts should be used. The following examples are given to more clearly illustrate the preparation of the phosphate modified latex of this invention to those skilled-in the art and are not for purposes of limitation. Parts are by total weight polymer. Example I A phosphate modified latex was prepared from the following constituents: Parts Water 118.00 Carbon tetrachloride 4.00 Sodium hydroxide (10%) 0.15 Sodium persulfate 1.00 " Seed latex (styrene/acrylic acid) 1,56 Styrene 60.00 Butadiene 40.00 Phosphated alkylphenol ethoxylate 3.00 After the constituents had been charged to a polymerization vessel, the resulting aqueous composition was heated to 90°C for 45 minutes with mixing and polymerized for 4 hours. A stable phosphated latex containing 43.93 percent solids was obtained thereby. Example II A phosphate modified latex was prepared with the addition of a phosphonate derivative comonomer with the following constituents: Parts Water 118.00 Carbon tetrachloride 4.00 Sodium hydroxide (10%) 0.15 Sodium persulfate 1.00 Seed latex (styrene/acrylic acid) 0.66 Styrene 56.72 Butadiene 40.00 Phosphated alkylphenol ethoxylate 2.00 • Phosphonate comonomer PO OH) 2 CH 2 N(CH 2 CHCH 2 ) 2 3.28- The constituents were charged to a poly¬ merization vessel and heated to 90°C for 45 minutes with mixing and polymerized for 4 hours. A stable latex containing 45.95 percent solids was obtained thereby. Example III A phosphorus-modified latex containing a phosphate ester surfactant compound was prepared with the addition of an acrylic acid comonomer with the following constitutents: Parts Water 118.00 Carbon tetrachloride 4.00 Sodium hydroxide (10%) 0.15 Sodium persulfate 1.00 Seed latex (styrene/acrylic acid) 0.66 Styrene 58.75 Butadiene 40.00 Phosphated alkylphenol ethoxylate 2.00 Acrylic acid 1.25 After the constituents had been charged to a polymerization vessel,- the resulting aqueous composition was heated to 95°C for 45 minutes with mixing and polymerized for 4 hours. A stable phosphated latex composition was obtained thereby. The phosphate modified latexes as prepared above can be readily employed in paper coating and composite sheet formation. In particular, the phosphate modified latexes are useful in binding inorganic fillers as are commonly employed in paper manufacturing. In particular, the subject latexes have found utility as binders for divalent and trivalent metal ions which are present in inorganic fillers. The inorganic fillers are present in aqueous dispersions in amounts of from 40 to 85 percent by weight. Inorganic fillers with multivalent ions are preferred. The inorganic fillers can be chosen from those well known in the paper coating art. Especially applicable are those fillers such as clay, calcium carbonate, talc, mica, magnesium hydroxide or oxide,, zinc oxide, gypsum, doli e, zincite, wallastonite, satin white, barytes, titanium dioxide and aluminum trioxide. The application of a filler and the phosphate modified latex as a binder in paper manufacture has been found to provide excellent, uniform film coverage, i.e., an even distribution of pigment and latex on the fibers, significantly lower flocculant demand, and higher wet and dry sheet strength. Alternatively, the phosphate modified latex may be utilized as a coating on nonporous substrates such as cans and the like to prevent corrosion. With respect to paper manufacturing, the phosphate modified latex is particularly adaptable for use as the latex component in a composite sheet method of manufacture. This product and process is described in U.S. Patent No. 4,225,383, In such a process, a water- -dispersible fiber; a film-forming water insoluble, organic polymer latex of this invention in an amount of from 2 to 30 percent by weight, more perferably from 3 to 15 percent; and a finely divided, substantially water-insoluble non-fibrous, inorganic filler are used to form a sheet therefrom. U.S.Patent 4,225,383 additionally requires in the preferred process a flocculating agent. However, due to the inherent flocculating characteristic of the phosphate modified latex, a much reduced load of flocculating agent is required when the latex of the subject inven- tion is employed. This characteristic is due to the bound -PO(0) 2 groups which allow the modified latex particle to be destabilized much easier than a con¬ ventional latex particle in the presence of fillers 5 with multi-valent ions than conventional latex particles. Further, when the present latex is employed, much higher filler levels are obtained in the composite sheet due to the interaction between the -PO(0) 2 group and the filler. More specifically, when an inorganic filler 10 containing divalent or trivalent metal ions is employed, the -PO(0) 2 groups have been found to interact with them. This interaction has been demonstrated by measur¬ ing the sedimentation volume of an inorganic filler in water. For example, 20 g of CaCO- were added to a 15. graduated cylinder and diluted to 100 ml with water. After equilibrating for 2 hours, the amount of sediment that accumulated in the bottom of the cylinder was approximately 17.5 ml. In another graduated cylinder 20 g of CaC0 3 were diluted to 100 ml with water and 1 g 20 of a -PO(0) 2 group-containing latex was added. Again, after equilibrating for 2 hours, the sediment volume was measured. This time the sediment volume was approx¬ imately 42 ml. This increased volume can be attributed to an interaction between the CaC0 3 and- the phosphate 5 modified latex. Composite sheets were prepared using a control latex comprising 70 parts of a latex of 54 weight percent styrene/45 weight percent butadiene/1 weight percent fum- aric acid and 30 parts of a latex of 75.5 weight percent 0 styrene/19.5 weight percent butadiene/4 weight percent hydroxylethyl acrylate/1 weight percent, fumaric acid and using the modified latex of the present invention. The percent retention of filler was calculated for both latexes Various fibers were also employed to determine the effect of the -PO(0) 2 group-modified latex with respect to retention of the filler. All tests were conducted on a basic formula of 45 percent fiber, 50 percent filler (CaC0 3 ), and 5 percent latex. The modified latex for¬ mulation employed was from Example II disclosed herein- above. The results obtained are tabulated in Table I. TABLE I Percent Filler Retention Control Phosphate Fiber Latex 1 Modified Latex 2 Bleached Kraft 50% Softwood/50% Hardwroooodd 82* 93 Bleached Kraft Hardwood 88* 95 Bleached Kraft Softwood 84* 94 Bleached Sulfite Softwooidd 91* 94 Unbleached Kraft Softwooidd 88* 96 *Not Examples of the present invention. x Latex blend containing 70 parts (54 styrene/45 butadiene/1 fumaric -acid) and 30 parts (75.5 styrene/19.5 butadiene/4 hydroxylethyl acrylate/1 fumaric acid) . 2 Latex of 56.72 styrehe/40 Butadiene/3.28 comonomer con- taining -PO(0) 2 group as described in Example II. Immediately observable from Table I is that the modified latex according to the present invention showed a higher filler retention level than the control latex and also showed a more consistent percentage of filler retention independent of the particular fiber employed. Additional testing was conducted with the modified latexes to determine their self-flocculating characteristic. Usually the preferred process for for- ming a composite sheet employs a flocculant which has an opposite charge to the ionic stabilization of the latex in order to cause the latex to become colloidally destabilized. However, the subject modified latex has been shown to require less flocculant load while exhibiting excellent filler retention. In particular, Table II shows the results obtained where a standard latex composition was compared to three modified latexes according to the present invention with various levels of a ,β-ethylenically unsaturated acid comonomer at increasing flocculant levels. The particular flocculants employed are described in Table II. The common recipe employed for the four aqueous dispersions was 45 percent fiber (50/50 hardwood/softwood), 50 percent clay and 5 percent latex. Flocculant was added to each recipe as indicated in Table II. The latex compositions are as indicated in Table III. Table IV contains the retention percentages of inorganic filler by each latex at varying flocculant levels. TABLE II Flocculant Type and Amount A 2 lb/ton Polymeric PC 1 plus 1/2 lb/ton Betz 1260 2 B 4 lb/ton Polymeric PC 1 plus 1/2 lb/ton Betz 1260 2 C 4 lb/ton Polymeric PC 1 plus 1 lb/ton Betz 1260 2 1 Polymeric PC is a cationic copolymer of acrylamide 2 Betz 1260 is a high molecular weight cationic polyacrylamide. TABLE III Latex W 58.5 styrene/40 butadiene/1.5 itaconic acid X 59 styrene/40 butadiene/1 fumaric acid/2 phosphated alkylphenol ethoxylate Y 59.5 styrene/40 butadiene/0.5 fumaric acid/2 phosphated alkylphenol ethoxylate Z 58.75 styrene/40 butadiene/1.25 acrylic acid/2 phosphate alkylphenol ethoxylate TABLE IV % Retention of Inorganic Filler at Increasing Flocculant Levels (A to C) Latex A B C w * 68.5 78.5 82.5 X 72.0 84.0 88.5 Y 78.0 89.5 93 .0 z 79.0 90.5 95.5 * Not an example of the present invention. The percent retention of filler with respect to flocculant loading shows that the modified latex at all acid comonomer levels (latexes X, Y and Z) exhibited increased filler retention. It is further shown that the subject latexes (X, Y and Z) can be employed at lower flocculant loads (A→-C increasing levels) while still obtaining equivalent to greatly enhanced retention over the standard latex (W) at increased flocculant loading. While the flocculating characteristic of the modified latex is especially beneficial in composite sheet manufacture, this inherent destabilizing tendency is not entirely beneficial in a paper coating latex. A paper coating latex instead is generally known in the art to need a certain degree of stabilization in the pre¬ sence of inorganic fillers in order to effectively employ it in paper coating operations. As is well known, paper coating compositions comprise pigments which are inorganic fillers and an adhesive material which consists of a synthetic latex. This latex composition is applied to the paper by conventional means such as letterpress print roll coater, offset roll coater, size press, air knife and blade coater. After application, the latex- composition is dried by any convenient method such as by a current of air and more usually by heated air. The latex employed must exhibit a degree of stability in order to provide a homogeneous aqueous dispersion while it is maintained on a particular coating apparatus. It has been found that when only the phosphate ester type surfactant compound is used in the manufacture of the subject latex the resulting aqueous dispersion may be too destabilized for convenient use as a paper coating binder. However, when the phosphate ester surfactant comp¬ ound is used in conjunction with a latex containing certain ethylenically unsaturated comonomers polymerized therein, as described above, the resulting latex dispersion becomes -sufficiently stabilized to be employed as a paper coating composition. The preferred ethylenically unsaturated comonomers are an ,β-ethylenically unsaturated carboxylic acid or a copolymerizable phosphonic acid derivative. The more preferred or,β-ethylenically unsaturated carboxylic acids being fumaric acid and acrylic acid. Acrylic acid being the most preferred. A further discovery with respect to the latex containing both phosphate ester surfactant compounds and copolymerized monomers having -P0(0) 2 groups is that the increased stabilization provides excellent sheet strength despite the increased filler retention. This phenomena is attributed to an optimized flocculation rate which is sufficient to allow a more uniform arrangement of the latex/inorganic filler units. Thus, the more symmetrical packing would have greater structural integrity than a more random or porous packing which would result from a rapidly flocculating system. The following Table V shows how paper com¬ posites formed from copolymer latexes with bound -PO(0) 2 surface groups exhibit increased retention of the inorganic filler with little loss in internal bonding strengths of the paper specimen. This would not be expected in view of the increased filler levels present. With typical latex compositions, depending on the filler type, there can be an improvement in strength at low filler levels as the filler content increases. However, as the optimum amount of filler is exceeded there is a very extreme reduction in strength. Testing was conducted on a Scott Model B Intra-fiber Bond Tester, manufactured by Scott Testers, Inc.; Providence, Rhode Island. The test procedure followed was in accordance with Technical Association of the Pulp and Paper Industry (TAPPI) routine control method RC-308. This method is designed to determine the average force in milli Joules (mJ) and thousandths of a foot pound required to separate a paper specimen, to determine the internal bonding strength of the paper specimen. For this demonstration, paper composites were prepared using a 45 percent fiber (50 percent hardwood/- 50 percent softwood), 50 percent clay and 5 percent latex formulation. The latex compositions employed were those from Table III. Internal bonding strength was measured at various filler retention levels and plotted graphically to compare the four latex compositions at increasing retention levels. The results are as follows: TABLE V . Internal Bonding Strengths** of Paper Specimens Filler Retention Levels Latex 75% 80^ 85% 90% W* 151.1 (111.5) 176.2 (130.0) X 126.0 ( 93.0 ) 150.4 (111.0 ) 168.7 (124.5 ) 174.1 ( 128.5 Y 111.5 ( 82.3 ) 135.5 ( 100.0 ) 154.5 (114.0 ) 169.4 (125.0 Z 126.0 ( 93 .0 ) 149.1 (110.0 ) 166.7 ( 123.0 ) 176.2 (130.0 * Not an example of the present invention. **Internal bonding strengths measured in milli Joules and thousandths of a foot pound required to separate a paper specimen. The strengths in thousandths of a foot pound are given in parentheses. The maximum filler retention of the standard latex, W, was 80 percent and, therefore, no internal bonding values are reported at the 85 and 90 percent filler retention levels. The subject latexes, X, Y, and Z, obtained significantly better exceeding 90 percent retention levels, exceeding 90 percent. However, for pur¬ poses of comparison, Table V only reports values up to the 90 percent level. It is readily seen that at the 90 percent retention level the subject latexes exhibit greater internal bonding strength than the standard latex, W, at the lower 75 percent retention level and bonding strength substantially equivalent to the standard latex at the 80 percent level. This is surprising and unique. Ordinarily, one would expect lower strength values for increasing levels of filler retention because of the lower binder to filler ratio. At equivalent retention levels the standard latex showed better strength but this occurred at lower levels of retention which did not take advantage of the capabilities for higher filler retention according to the present invention. It is to be noted, however, that the invention's internal bonding strength at lower filler retention levels is not unacceptable and, therefore, the invention can be successfully employed at these levels. The preferred mode of operation, however, would be at the higher retention levels as it is here that the advantages of the subject invention are best realized.

Claims: -22- WHAT IS CLAIMED IS: 1. A modified latex composition having a phosphorus-containing surface group, the latex composition comprising: (a) at least one ethylenically unsatu¬ rated monomer which is emulsion polymerized to form a latex polymer, and (b) a phosphorus-containing compound comprising a -P0(0) 2 group which is intimately bound to the surface of said latex said phosphorus- -containing compound being a phosphonate and/or a phosphate compound. 2. The composition of Claim 1 wherein said ethylenically unsaturated monomer is of the general formula CH 2 =CHR wherein R is H, alkyl, aryl, nitrile, ester, acid or halogen. 3. The composition of Claim 1 wherein said latex polymer is a copolymer. 4. The composition of Claim 3 wherein said copolymer is poly(styrene-butadiene). 5. The composition of Claim 1 wherein said phosphorus-containing compound is a phosphate ester sur¬ factant. 6. The mixture of Claim 1 wherein said phosphorus-containing compound is a polymerized phosphonic acid or phosphoric acid monomer and/or polymerized der¬ ivative of a phosphonic or phosphoric acid. 7. A method for preparing a composite sheet comprising the steps of: (a) adding from 2 to 30 percent of a modified latex composition according to Claim 1 to an aqueous dispersion comprising a water-dispersible fiber and an inorganic filler; (b) colloidally destabilizing the resulting mixture to form a fibrous agglomerate in aqueous suspension; (c) distributing and draining said aqueous suspension on a porous support to form a wet web; and (d) drying said web to form a sheet. 8. A method of paper coating comprising the steps of: (a) adding from 2 to 30 percent.of a modified latex composition according to Claim 1 to an aqueous dispersion of at least one inorganic filler and monome which is emulsion polymerized to form a latex, ' and a mixture comprising: (1) a surfactant containing a -P0(0) 2 group, and (2) an ethylenically unsaturated comonomer (b) coating paper with the latex-con¬ taining composition. 9. The method of Claim 8 wherein said phos¬ phorus- containing compound is a polymerizable phosphonic acid or phosphoric acid monomer and/or a polymerizable derivative of a phosphonic or phosphoric acid. 10. The method of Claim 8 wherein said modified latex composition comprises phosphate ester surfactant compound and a polymerized phosphonic acid monomer and/or a polymerized derivative of a phosphonic or phosphoric acid. 11. The method of Claim 8 ' wherein said mod¬ ified latex composition comprises phosphate ester sur¬ factant compound and a polymerized α,β-ethylenically unsaturated carboxylic acid monomer.

Inventors: CHEN SUN-LIN, GREENE BETTYE W, CHEN, SUN-LIN, GREENE, BETTYE, W.
Applicants: DOW CHEMICAL CO, THE DOW CHEMICAL COMPANY
Application year: 1984
Main classification: C08K3
IPC codes: C08F2, D21H17, D21H19