SYNTHETIC PHOSPHOLIPID COMPOUNDS, THEIR PREPARATION AND USE

Abstract: Synthetic phospholipid compounds which are phospha­ tidylethanolamine polycarboxyl polyalkylene glycols are prepared by the reaction of a phosphatidylethanolamine, a polycarboxylic acid compound, such as succinic or glutaryl anhydride, and a polyalkylene glycol, such as polyethylene glycol.

Description: SYNTHETIC PHOSPHOLIPID COMPOUNDS, THEIR PREPARATION AND USE Phospholipids such as lecithin, are amphiphatic compounds in that they contain both hydrophobic and hydrophilic groups or regions within the same molecule. The balance between these hydrophobic and hydrophilic regions determines the physical properties of the compounds in an aqueous environment. The uses of natural phospholipids as additives are numerous in the food industry (for example, as emulsifiers), in cosmetics, for industrial uses and for the pharmaceutical industry, especially in the preparation of drug-delivery systems. U.S. Patents 4,086,257; 4,097,502; 4,145,410; and 4,159,988 disclose various modifications of the polar-head-group region of natural phospholipids which lead to unique and unexpected physical properties. Further, various derivatives of lecithin are known, such as, for example, oxyalkylated lecithin compounds (see U.S.Patents 3,085,100 and 2,310,679) and phosphatidylalkanolamine derivatives (see, for example, U.S. Patents 2,801,255; 3,542,820; 3,577,466; and 4,254,115). It is desirable to provide novel, synthetic phospholipids, particularly having enhanced solubility and surfactant properties in an aqueous environment, especially for the formulation of water-insoluble materials, such as drugs or cosmetic ingredients, within an aqueous environment. European Patent Application 0072111 (published 16 February 1983) describes novel, synthetic phospholipid compounds, such as phosphatidylalkanolamine carboxyl polyalkylene glycol compounds, including phosphatidylethanolamine carboxyl polyethylene glycol compounds. These compounds are prepared by the covalent reaction of a carboxylic analog of the polyalkylene glycol with the phosphatidylalkanolamine, to provide biodegradable, phospholipid compounds which contain an amide linkage. This invention relates to synthetic phospholipid compounds, to their preparation and to the use of such compounds, particularly in solubilizing, in an aqueous environment, water-insoluble compounds. The invention describes a new, improved series of phosphelipid- compounds in which the polar-head-group region is modified by the covalent attachment through two or more carboxylic groups of polyalkylene glycols. The novel, synthetic phospholipid compounds of the invention are phosphatidylalkanolamine polycarboxyl polyalkylene glycol compounds, such as phosphatidylethanolamine di- or tri-carboxyl polyethylene and polypropylene glycol compounds. The phospholipids of the invention are analogs of the phospholipid compounds of European Patent Application 0072111. This invention also provides a different and improved method of coupling a polyalkylene glycol to a phospholipid. The phospholipid compounds of the invention have enhanced surfactant properties, are soluble in acetone and are biodegradable. The synthetic phospholipid compounds of the invention are represented by the following structural formula: EMI2.1 wherein a) R1 and R2 each represent hydrogen or a saturated or unsaturated, straight or branch-chain acyl group, such as an organic acyl radical having 2 to 24 carbon atoms; for example, C2 to C20 fatty-acid radicals, such as oleic, stearic, linoleic, linolenic, palmitic, myristic or arachidonic acid radicals, or may be derived from natural products, such as plants like soybean or egg; b) R3 represents an alkylene radical, such as a C2 to C4 group like ethylene, propylene or butylene; that is, tetramethylene; c) R4 represents a polymethylene radical, typically a C2 to C10 polymethylene divalent radical, and particularly an ethylene radical;-- that is a dimethylene radical, as in natural lecithin, or a propylene radical; that is a trimethylene radical; d) R5 represents an organic linking radical; for example, a hydrocarbon radical, of from 1 to 24 carbon atoms, but typically of 2, 3 or 4 carbon atoms, which radical may be saturated or unsaturated, may be substituted, for example, with hydroxyl, amino or carboxyl groups, or be an unsubstituted radical, such as a polymethylene (-CH2-) radical like an ethylene, propylene or butylene radical; e) R6 represents hydrogen or an alkyl, such as methyl, radical; f) X represents hydrogen or an alkyl radical, typically a lower alkyl radical like a C1 to C4 alkyl group, such as a methyl radical; and g) n represents a number of the alkylene oxide groups and may vary from 0 to about 200 or more; for example, from 2 to 100, such as 2 to 20, to provide phospholipids having, for example, a molecular weight of from 150 to 3000 or more; for example, 200 to 2000. One particular group of phospholipids of the invention prepared by the use of succinic or glutaric anhydride, or other dicarboxylic acids, is represented by the structural formula: EMI4.1 wherein m represents a number from 1 to 4. The polycarboxylic acids or derivatives used in the preparation of the phospholipid compounds are preferably aliphatic acids and more particularly aliphatic acid anhydride compounds for ease of reaction; for example, C3 to C6 dicarboxylic acids, particularly which form 4-to-7-member-ring anhydrides, such as succinic acid, glutaric acid, adipic acid and phthalic acid anhydride. Suitable carboxylic acids include, but are not limited to, aliphatic, cycloaliphatic, di- and tri-carboxylic acids, such as succinic acid, glutaric acid, glutamic acid, citric acid, tartaric acid, oxalic acid, adipic acid, malic acid and maleic acid, as well as long-chain dicarboxylic acid, although waxy, solid compounds may result from the use of long-chain acids. Preferably the acid compounds employed are the C3 to C7 dicarboxylic acid anhydrides. These novel phospholipid compounds have a distinctly different chemical composition than the compounds described, for example, in U.S. Patents 2,310,679 and 3,085,100, which are products from the coupling of ethylene oxide or similar compounds to crude soy lecithin. The use of the term "lecithin" describes a number of compounds including lecithin (that is, phosphatidylcholine), a compound that cannot react with ethylene oxide. On the other hand, soy lecithin does contain phosphatidylethanolamine, phosphatidylinositol and a variety of glycolipids. All of these compounds in crude lecithin can react with ethylene oxide or similar compounds containing a reactive cyclooxide group to form various adducts. For example, in phosphatidylinositol and with glycolipids, the reactive groups in these molecules are hydroxyl groups which will form an ether linkage, when reacted with ethylene oxide. Phosphatidylethanolamine, which contains a primary amino group, will react with ethylene oxide to form an alkylamine linkage (see N. Schonfeldt, "Surface Active Ethylene Oxide Adducts", Pergamon Press, 1969). In both cases, these adducts are not biologially degradable, and, therefore, such compounds are undesirable for use in the cosmetic and pharmaceutical industries. The phospholipids of the invention comprise synthetic phospholipids in which the linkage between the synthetic ethylene oxide or propylene oxide polymer and the naturally occurring phospholipid is a biologically degradable linkage; for example, an amide linkage, which makes these novel phospholipid compounds useful for cosmetics and pharmaceutical uses. The preparation of the phospholipid compounds is best accomplished by the addition of a cyclic polyacid, particularly anhydride, such as succinic or glutaric acid anhydride, to the polyalkylene oxide polymer. The coupling of the appropriate carboxylic analog of the polyalkylene oxide polymer to the phosphatidylalkanolamine molecule, such as phosphatidylethanolamine, gives the desired compounds. Alternatively, the cyclic acid anhydride can be coupled to the phosphatidylethanolamine, and then the polyalkylene oxide polymer is coupled to the modified phospholipid. For example, in one method the low-cost acidic polyalkylene glycol compound can be mixed with crude soy lecithin for a coupling reaction with the phosphatidylethanolamine, and the novel phospholipid compounds extracted with acetone. The acidic polymer may be converted to an acid halide compound, to increase the speed of the reaction. The acidic polyalkylene glycol polymer compound can be purified further via distillation, ion-exchange chromatography or absorption chromatography. The acyl analog of the polyethylene oxide polymer is activated by a convenient activating agent, such as oxalyl chloride or 1, 1 carbonyl diimidazole. The activated carboxylic derivative of the parent polyalkylene oxide polymer is then coupled to the phosphatidylethanolamine via an amide linkage, to form the phospholipid analog compounds of this invention. The phosphatidylethanolamine either can be isolated from natural sources, synthesized according to established chemical procedures, or enzymatically synthesized using the corresponding phosphatidylcholine compound in the presence of ethanolamine and phospholipase D. The reaction of the phosphatidylethanolamine and the carboxylic derivative of the polyalkylene oxide polymer is carried out in an inert solvent. The progress of the reaction can be monitored by thin-layer chromatography. Purification of the final product, if necessary, may be carried out using column chromatography. In the phospholipid compounds of this invention, the polar-head group of the phosphatidylethanolamine has been modified to alter its physical properties, by the inclusion of a polyalkylene oxide polymer. In all cases where natural phospholipids can be used, such as in drug-delivery systems, in cosmetics, in food, in industrial uses, in treating atherosclerosis, for intravenous nutrition and other uses, these new synthetic phospholipid compounds can be used alone or in combination with other natural phospholipids, especially phosphatidylcholine. Biologically these synthetic phospholipids will be immunologically inert. For example, polyethylene oxide polymers attached to proteins are nonimmunogenic and well tolerated by the body (see Abuchowski et al, J. Biol. Chem. 252, pp 3578-3581 (1977)). The covalent linkage between a typical polyalkylene example, such as polyethylene oxide polymer and the phosphatidylethanolamine, is biologically degradable, and phosphatidylethanolamine, itself, is a natural compound. As a result, these novel compounds have utility in encapsulating drugs, especially water-insoluble drugs, as drug-delivery systems that either can be administered orally or via injection, such as in the encapsulation process disclosed in corresponding U.S. Serial No. 90,994, filed November 13, 1979, as well as in the method of U.S. Patent 4,016,100. The presence of the hydrophilic alkylene oxide polymer, particularly the polyethylene oxide polymer moiety in the phospholipids, also gives rise to novel and unexpected physical properties in an aqueous environment. As an example, unsaturated phosphatidylethanolamines, especially those isolated from soybeans, do not form any stable type of structure in water. Phosphatidylcholine, if hydrated with an aqueous solution forms large ( > 200 nm or 2000 A) structure termed multilamellar liposomes. On the other hand, gangliosides have a similar hydrophobic region, compared to phosphatidylethanolamine and phosphatidylcholine, but the polar region of the ganglioside molecule is composed of hydrophilic oligosaccharides. The presence of these oligosaccharides allows the ganglioside to organize into a stable micelle upon hydration with water. By covalently attaching a hydrophilic polyalkylene polymer, such as polyethylene or polypropylene oxide polymers, to phosphatidylethanolamine, a phospholipid analog to ganglioside is essentially synthesized. It also should be noted that, while no molecular species of phosphatidylethanolamine will form a stable structure in an aqueous environment, the phospholipid analog compounds described herein do form stable structures upon hydration. As a consequence of this physical behavior, a variety of water-insoluble compounds can be formulated in a stable form in an aqueous environment at physiological pH. Furthermore, the spontaneous structure that these phospholipids form, when hydrated with water from the dry state, is small (less than 20 nm or 200 A; for example, typically average 7.5 to 10 nm or 75 to 100 A), which results in an optically clear solution. The actual organization of these structures, however, will depend, at least in part, on the selected acyl chain composition of the phosphatidylethanolamine and the alkylene oxide polymer. In particular, with phosphatidylethanolamine isolated from soybeans and various polyethylene oxide polymers, micellar structures of less than 20 nm (200 A) diameter are spontaneously and easily formed, upon addition of water to the dried phospholipid analog. These structures are distinct and unique, as compared to liposomes or other lipid vehicles that are composed of phosphatidylcholine. The invention is illustrated by the following examples: Example 1. Soy phosphatidylethanolamine succinyl polyethylene glycol monomethyl ether (molecular weight 252) Succinyl polyethylene glycol monomethylether compounds were prepared in accordance with and under the following general method and conditions. 1 mole of the polyethylene glycol polymer was heated with 5 moles of finely divided succinic anhydride in a slurry of CC14 under a nitrogen atmosphere. The solution was magnetically stirred and heated overnight at 750C under a nitrogen atmosphere. Temperature control is important, as the reaction mixture darkens above 75 0C. Upon cooling at room temperature, the excess succinic anhydride was removed by filtration. The reaction mixture was then dissolved in a 1:1 methylene chloride/methylene mixture, and sufficient concentrated NH4OH was added, so that an aliquot of the reaction mixture was approximately pH 9, when diluted with water. The succinyl polymer reaction mixture was dissolved in a 95:5:0.8 mixture of methylene chloride/methanol-concentrated NH40H and applied to a silicic acid column equilibrated in the same solvent. The succinyl polymer was diluted with a step gradient of increasing methanol content. The purity of the fraction was monitored by thin-layer chromatography, using a solvent system of 90:10:1 of methylene chloride/methanol-concentrated NH40H. Pure fractions of the succinyl polymer were evaporated to near dryness. Sufficient HC1 was added to the mixture, so that an aliquot, when diluted with water, gave a pH of between 2 and 2.5. The compound was then evaporated to dryness. Methylene chloride was added to the dried material, and any particulate material was filtered off. The filtrate was evaporated to dryness and dried overnight under high vacuum. The above conditions were used to make the succinyl polyethylene glycol monomethylether, using, as the starting material, polyethylene glycol monomethylether with a molecular weight of 252. To 2200 pmoles of the succinyl polymer compound were added 2000 pmoles of 1,1 carbonyl diimidazole in a benzene solution. The solution was heated 0 at 60 C for 10 to 15 minutes, until the bubbling had ceased. This solution was transferred to another flask containing 1000 pmoles of dried soy phosphatidylethanolamine (PE), which was prepared by the enzymatic conversion of soy phosphatidylcholine using ethanol amine and phospholipase D from Savoy cabbage. Sufficient benzene was added to ensure that all of the soy PE had dissolved. Then most of the benzene was removed,-leaving a thick slurry. This slurry was stirred with a magnetic stirrer for approximately 6 hours at 70 0C under a nitrogen atmosphere. The extent of the conversion of PE to the desired product was monitored by thin-layer chromatography. The reaction mixture was taken to dryness and then partitioned into a two-phase Folch System, with .2M HC1 in the upper phase. The lower phase was extracted four more times with this acidic Folch upper phase, and twice with a .3M NH4 acetate upper phase, to remove the imidazole and excess noncoupled succinyl polymer compound. The lower phase was evaporated to dryness. The sample was dissolved in 95:5:0.8 methylene chloride/methanol--concentrated NH40H and applied to a silicic acid column equilibrated in the same solvent. The soy PE-succinyl polyethylene glycol monomethylether (molecular weight 252) was eluted with a step gradient of increasing methanol content, while maintaining approximately 0.8 to 1.0 concentrated NH4OH in the eluting solvent. The elution profile was monitored by thin-layer chromatography, using 80:2:1 methylene chloride/methanol-concentrated NH40H as the solvent. Pure fractions of the product were pooled and reduced to dryness. The pH was tested and adjusted, if needed, to between 5 and 7. The compound was then dissolved in methylene chloride. The yield of the product was 35% based on the starting soy PE content. Example 2. Soy phosphatidylethanolamine succinyl polyethylene glycol monomethylether (molecular weight 120) A succinyl polyethylene glycol monomethylether (molecular weight 120) polymer compound was prepared as described in Example 1. 7500 fmoles of the succinyl polyethylene glycol were dissolved in benzene and 4000 pmoles of 1,1 carbonyl diimidazole were added. The solution was 0 heated at 60 C, until all bubbling had ceased. The solution was added to 1000 pmoles of spy PE that previously had been dried under high vacuum. The reaction conditions were the same as in Example 1. The yield of the pure product, after column chromatography, was 428. Example 3. Soy phosphatidylethanolamine succinyl polyethylene glycol monomethylether (average molecular weight 1900) A succinyl polyethylene glycol monomethylether (average molecular weight 1900) was prepared as described in Example 1. 1750 }1moles of this compound were dissolved in benzene and 1000 rmoles of 1,1 carbonyl diimidazole were added. The solution was heated to 60 C, until the bubbling had ceased. The solution was added to 483 pmoles of dried soy PE. The reaction conditions were as described in Example 1. The yield of column-purified material was 44%. Example 4. Soy phosphatidylethanolamine succinyl polyethylene glycol monomethylether (average molecular weight 350) A succinyl polyethylene glycol momomethylether (average molecular weight 350) was prepared as described in Example 1. 7000 umoles of succinyl polyethylene glycol monomethylether compound were dissolved in benzene and 4000 pmoles of 1,1 carbonyl diimidazole were added. The solution was heated at 60 C, until the bubbling had ceased. This solution was added to 1050 pmoles of dried soy PE. The reaction conditions to form the product were the same as described in Example 1. The yield of the pure product, after column chromatography, was 70%. Example 5. Soy phosphatidylethanolamine succinyl polyethylene glycol monomethylether (average molecular weight 750) A succinyl polyethylene glycol monomethylether (average molecular weight 750) was prepared as described in Example 1. 7500 pmoles of the compound were dissolved in benzene and 5000 pmoles of 1,1 carbonyl diimidazole were added. The solution was heated at 60 0C, until bubbling had ceased. This solution was then added to 1200 pmoles of dried soy PE. The reaction conditions were then as described in Example 1. The yield of the column-purified product was 52%. Example 6. Soy phosphatidylethanolamine succinyl polyethylene glycol monomethylether (average molecular weight 550) A succinyl polyethylene glycol monomethylether (average molecular weight 550) was prepared as described in Example 1. 3070 pmoles of the compound were dissolved in benzene and 2000 pmoles of 1,1 carbonyl diimidazole were added. The solution was heated at 60 C, until the bubbling ceased. The solution was added to 1127 /umoles of dried soy PE. The reaction conditions were the same as described in Example 1. The yield of the column-purified material was 58%. Example 7. Soy phosphatidylethanolamine succinyl polyethylene glycol monomethylether (molecular weight 252) Another method of producing the compounds of the invention is the coupling of succinic anhydride to soy PE and then reacting the modified PE with the appropriate polyethylene glycol polymer. Succinic anhydride (1000 pmoles) was reacted with 1000 pmoles of soy PE in a methylene chloride slurry under a nitrogen atmosphere at 70 0C overnight. The unreacted succinic anhydride was filtered off. The methylene chloride was evaporated and the succinic acid modified PE was purified by column chromatography. 500 rmoles of the succinic acid modified PE was dissolved in benzene, and 500 pmoles of 1,1 carbonyl diimidazole were added. The solution was heated at 60 C, until the bubbling had ceased. 750 Sumoles of the polyethylene glycol monomethylether (molecular weight 252) were added to the solution, and the mixture was heated for 3 hours under a nitrogen atmosphere at 70 C. The purified product was then recovered as described in Example 1. Example 8. Soy phosphatidylethanolamine succinyl tetraethylene glycol (molecular weight 194) The soy PE succinic acid derivative was prepared as described in Example 7. 650 pmoles of the compound were dissolved in benzene and 650 pmoles of 1,1 carbonyl diimidazole were added. The solution was heated at 600C, until the bubbling had ceased. To the solution were added 650 pmoles of tetraethylene glycol. The reaction was heated at 70 0C under a nitrogen atmosphere for 3 hours. The reaction was recovered as described in Example 1. The yield of the column-purified material was 37%. Example 9. Soy phosphatidylethanolamine glutaryl polyethylene monomethylether (molecular weight 252) One of the disadvantages of using the succinic anhydride as a linking agent is the high melting point of the anhydride that prevents a homogeneous reaction mixture. In using glutaric anhydride, many of these disadvantages can be addressed. In particular, 1 mole of the polyethylene glycol was heated with 2 to 3 moles of the glutaric anhydride in a 0 N2 atmosphere at 75 C in the absence of any solvent. At the end of the reaction as determined by thin-layer chromatography, the reaction mixture was dissolved in methylene chloride/methanol 1:1 (v/v) and recovered as described for the succinyl material as described in Example 1. In this particular example, 7.5 g of polyethylene glycol monomethylether (molecular weight 252) and 5 g of glutaric anhydride were placed in a reaction vessel and heated to 75 0C, with magnetic stirring, for 3 hours under a N2 atmosphere. The glutaryl polyethylene glycol compound was purified by column chromatography. 1200 pmoles of 1,1 carbonyl diimidazole were added to 1500 pmoles of the glutaryl polyethylene glycol compound dissolved in benzene. 0 The solution was heated at 60 C, until the bubbling had ceased. This solution was added to 1127 pmoles of dry soy 0 PE, and the reaction mixture was heated for 3 hours at 70 C. The mixture was extracted and purified as described in Example 1. The yield of pure product was 67%. Examples 10-14 illustrate that the phospholipids of the invention are useful in solubilizing water-insoluble drugs, oils and fragrances,- to provide aqueous solutions. Example 10. The anticancer drug, Taxol (an experimental drug of the National Cancer Institute which inhibits the ability of cells to divide) is insoluble in water. 8 pmoles of Taxol (6.5 mg) were dissolved in methylene chloride with 72jumoles of soy phosphatidylethanolamine succinyl polyethylene glycol monomethylether (average molecular weight 550). The solution was taken to dryness and pumped on by a high vacuum. The dried material was hydrated with 1 ml of 10 mM Tris (pH 8.5) and vortexed at room temperature. The resulting solution was optically clear. The solution was then adjusted with concentrated dextrose, to bring the dextrose concentration to 0.3M; thus making the sample suitable for intravenous injection. Example 11. Pentobarbital is a barbiturate that is insoluble in water at physiological pH as the acid form. It is the water-insoluble form that exerts its therapeutic activity. A standard solution sodium pentobarbital is stable only at high pH and was adjusted with dilute HCL to pH 3. The precipitated pentobarbital was removed by filtration. 40 umoles of the pentobarbital were dissolved in methylene chloride with 60 umoles of the soy phosphatidylethanolamine succinyl polyethylene glycol monomethylether (molecular weight 252). The solution was taken to dryness and then pumped on by high vacuum. The dried material was hydrated with 2 ml of 10 mM Tris (pH 8.5), to form an optically clear solution. The solution was adjusted with concentrated dextrose to give a 0.3M solution suitable for intravenous injection. Example 12. The anticancer drug, hexamethylmelamine, is water-insoluble. 2 mg of hexamethylmelamine and 70 umoles of soy phosphatidylethanolamine succinyl polyethylene glycol monomethylether (average molecular weight 550) were dissolved in methylene chloride. The solution was taken to dryness and then pumped on by high vacuum. The solution was hydrated with 1 ml of 10 mM Tris (pH 8.5), to give an optically clear solution. The solution was adjusted with concentrated dextrose to give a final dextrose concentration of 0.3M suitable for intravenous injection. Example 13. Another property of the phospholipids of the invention is their ability to act as exceedingly powerful surfactants for cosmetic ingredients, such as oils and petroleum jelly. As an illustration of such ability, 1.6 g of petroleum jelly and 160 mg of soy phosphatidylethanolamine succinyl polyethylene glycol monomethylether (molecular weight 252) were dissolved in hexane and taken to dryness and pumped on at high vacuum. To the dried material were added 4 ml of 10 mM Tris (pH 8.5). The hydrated solution was then sonicated with a Branson W-375 sonifier at 400C for 2 minutes. The resulting solution was opaque, but had excellent flow characteristics. When applied to the skin, there was an immediate and noticeable cooling sensation, due to the evaporation of water, and a pleasing tactile sensation. Example 14. Another example of the use of the compounds of the invention in the cosmetic field is the solubilization of water-insoluble fragrance oils in an aqueous environment. For example, 0.250 ml of a fragrance oil and 200 pmoles of soy phosphatidylethanolamine glutaryl polyethylene glycol monomethylether (molecular weight 252) were dissolved in 0.5 ml of ethanol. The solution was then diluted with 40 ml of water. The resulting solution was optically clear and retained the fragrance aroma.

Claims: CLAIMS 1. A synthetic phospholipid compound having the structural formula: EMI17.1 wherein R1 and R2 each represent hydrogen or an organic acyl radical; R3 represents a C2 or C3 alkylene radical; X represents hydrogen or an alkyl radical; R4 represents a C2 to C10 alkylene radical; R5 represents an organic linking radical; R6 represents hydrogen or a C1 to C4 alkyl radical; and n represents a number of from 0 to 200. 2. A phospholipid compound according to claim 1 wherein R1 and R2 each represent a C2 to C20 fatty-acid radical. 3. A phospholipid compound according to claim 1 wherein R1 and R2 are organic radicals derived from soybeans. 4. A phospholipid compound according to claim 1, 2 or 3 wherein R5 represents a polymethylene radical. 5. A phospholipid compound according to claim 4 wherein R5 represents a C1 to C4 methylene radical. 6. A phospholipid compound according to any one of the preceding claims wherein n represents a number from 2 to 20. 7. A synthetic phospholipid compound according to claim 1 which is a soy phosphatidylethanolamine succinyl or glutaryl polyethylene glycol compound. 8. A synthetic phospholipid compound having the structural formula: EMI18.1 wherein R1 and R2 each represent a C2 to C20 hydrocarbon organic acyl radical;- X represents hydrogen or a methyl radical; m represents a number of from 1 to 4; and n represents a number of from 0 to 200. 9. A method of preparing a phosphatidylalkanolamine polycarboxyl polyalkylene glycol compound, which method comprises reacting a phosphatidylalkanolamine, a polycarboxylic acid or derivative thereof and a polyalkylene glycol. 10. A method according to claim 9 which comprises reacting a dicarboxylic acid anhydride with a poly C2 or C3 alkylene glycol, to form the carboxyl poly C2 or C3 alkylene glycol compound and thereafter reacting the carboxyl poly C2 or C3 alkylene glycol compound with a phosphatidylethanolamine. 11. A method according to claim 9 or 10 wherein the polyalkylene glycol is polyethylene glycol having a molecular weight of from 150 to 3000. 12. A method according to claim 9, 10 or 11 wherein the polycarboxylic acid derivative is a C2 to C7 dicarboxylic acid anhydride. 13. A method according to any one of claims 9 to 12 wherein the phosphatidylalkanolamine is phosphatidylethanolamine. 14. A method according to claim 13 wherein the phosphatidylethanolamine is derived from crude soy lecithin. 15. A method according to any one of claims 9 to 14 which includes recovering the phosphatidylalkanolamine polycarboxyl polyalkylene glycol by extracting with acetone. 16. A method according to claim 9 which comprises reacting a dicarboxylic acid anhydride with a phosphatidylethanolamine, to form the phosphatidylethanolamine carboxylic acid compound and thereafter reacting the phosphatidylethanolamine carboxylic acid compound with a poly C2 or C3 alkylene glycol. 17. A method according to any one of claims 9 to 16 wherein the dicarboxylic acid derivative is succinyl acid anhydride or glutaric acid anhydride. 18. A method of solubilizing, in an aqueous environment, a water-insoluble compound, which method comprises mixing a solubilizing amount of a hydrated phospholipid compound as claimed in any one of claims 1 to 8 with water and a water-insoluble compound. 19. An aqueous composition which comprises water, a micelle-forming amount of a synthetic phospholipid as claimed in any one of claims 1 to 8 and a water-insoluble compound. 20. An aqueous composition according to claim 19, which solution has micelles therein of less than 20 nm (200 Angstroms) in size. 21. An aqueous composition according to claim 19 or 20 which comprises a therapeutic drug, petroleum jelly or a fragrance oil as the water-insoluble compound.

Inventors: SEARS, BARRY D.
Applicants: LIPID SPECIALTIES, INC.
Application year: 1984
Main classification: C07F9
IPC codes: C08G65, C07F9, A61K47, A61K9