NOVEL CHROME-COMPLEXED COMPOUNDS AND PHOTOGRAPHIC SYSTEM

Abstract: Chrome-complexed black dyes which include either a 1-naphthol-2′-naphthol-1′, 2-azo dye moiety or a 2-naphthol-­ 2′-naphthol-1,1′ azo dye moiety, a para-substituted phenyl­ azopyrazolone dye moiety and a cation. Diffusion transfer photographic color products and processes in which these are utilized neutral tone black image dye-providing materials which include a dye chro­ mophore as described above and a diffusion control moiety such as a hydroquinonyl group or a precursor thereof. The image dye-providing materials may be diffusible or nondiffu­ sible as a function of the diffusion control moiety.

Description: NOVEL CHROME-CO##LEXED COMPOUNDS AND PHOTOGRAPHIC SYSTEM BACKGROUND OF THE INVENTION This application relates to novel compounds which are useful as dyes and as intermediates in the preparation of image dye-providing materials which are useful in photography. Further, the application relates to photography and, more particularly, tQ photographic products and processes which utilize the aforesaid image dye-providing materials. Black image dye-providing materials can be used in diffusion transfer photography to form black and white images. The use of such materials to form the image can provide a number of advantages over processes where the image is formed by silver including image stability and the tone of the image. SUMMARY OF THE INVENTION It is an object of the invention to provide novel compounds. It is another object to provide compounds which are useful as dyes. It is a further object to provide black dyes. It is still another object to provide compounds which are useful as intermediates in the preparation of image dye-providing materials. Another object is to provide compounds which are useful in photographic applications. Yet another object is to provide image dye-providing materials which are useful in photography. A further object is to provide image dye-providing materials which include a diffusion control moiety which are useful in diffusion transfer photographic applications. It is another object to provide dye developers which are useful in diffusion transfer photographic applications. Still another object is to provide image dye-providing materials which are useful in dye release diffusion transfer processes. Yet another object is to provide novel photographic products and processes. A further object is to provide novel diffusion transfer photographic products and processes. BRIEF SUMMARY OF THE INVENTION These and other objects and advantages are accomplished in accordance with the invention by providing chrome-complexed black dyes which include a l-naphthol-21-naphthol-l',2-azo dye moiety or a 2-naphthol-2'-naphthol-l,l'-azo dye moiety, a para-substituted azopyrazolone dye moiety and a cation. These compounds are represented by the formula EMI3.1 where A is EMI3.2 R is hydrogen, -NO2, -SO3H or -S02NR1R2; R1 and R2 may be the same or different and each may be hydrogen, alkyl, preferably having from 1 to 6 carbon atoms, aryl such as phenyl or substituted alkyl, or substituted aryl, and X is a cation. It should be noted that the naphthyl moieties may be substituted in any of the available positions with substituents which may be, for example, electron withdrawing groups such as cyano, acetyl, nitro, sulfonic acid, sulfones, sulfonamido, etc. or electron donating groups such as alkyl, methoxy, amino, etc. The p-substituted phenyl and pyrazolone moiot ls may also be substituted in any of the available positions in like manner. In a preferred embodiment compounds within Formula A according to the inventions are represented by the formulas EMI4.1 wherein R3 and R4 may be the same or different and each is hydrogen, alkyl, preferably having from 1 to 6 carbon atoms, aryl such as phenyl, or alkyl or aryl substituted with any of the substituents disclosed above. The compounds are useful as dyes and as intermediates in the preparation of image dye-providing materials which are useful in photography, as will be described in detail herein. In addition the dye compounds of the invention are useful in photographic applications, for example, as filter dyes or as anti-reflection coatings or layers. The image dye-providing materials of the invention provide image dyes which have the chromophoric system represented by the formula EMI5.1 wherein A is as defined above, i.e., a naphthyl residue attached to the nitrogen and oxygen atoms either as l-azo-2-hydroxy or l-hydroxy-2-azo; X is a cation; and R' may be hydrogen, -NO2, -SO3H or -SO2NR"R"', and R" and R"' may be the same or different and each may be hydrogen, alkyl, preferably having from 1 to 6 carbon atoms, aryl such as phenyl or alkyl or aryl substituted with a photographically useful group such as, for example, a diffusion control moiety as will be discussed in detail further below. It should be noted that the naphthyl moieties may be substituted on one or both of the fused rings with any photographically acceptable substituents including, for example, electron withdrawing groups such as cyano, acetyl, nitro, sulfone, sulfonamido, sulfonic acid, etc. and electron donating groups such as alkyl, methoxy, amino, etc. The pyrazolone moiety may also be substituted in any of the available positions with any photographically acceptable substituents. Appropriate substituents may also be attached to the available positions on the phenyl ring. In a preferred embodiment the image dye-providing materials of the invention provide image dyes within Formula D having the chromophoric system represented by the formula EMI6.1 FORMULA E wherein R5 and #6 may be the same or different and each may be hydrogen, alkyl, preferably havinq from 1 to 6 carbon atoms, aryl such as phenyl or alkyl or aryl substituted with any photographically acceptable substituents such as those described above. It has been found that images formed with the preferred image dye-providing materials of the invention exhibit very good light stability and the ability to fade evenly across the visible spectrum. The image dye-providing materials of the invention include a diffusion transfer control moiety such as a hydroquinonyl group or a precursor thereof and may be diffusible or nondiffusible as a function of the diffu sion control moiety. In the photographic diffusion transfer processes of the invention the desired image is obtained by pro cessing an exposed photosensitive silver halide material with a processing composition distributed between two sheet-like elements, one of said elements including said photosensitive material. The processing composition is so applied and confined within and between the two sheet-like elements as not to contact or wet outer surfaces of the superposed elements, thus providing a film unit or film packet whose outer surfaces are dry. The processing composition may be viscous or nonviscous and preferably is distributed from a single use container; such pressure rupturable processing composition containers are commonly referred to as "pods". The final image may be monochrome or multicolor and is formed in an image receiving layer included in one of said sheet-like elements. As is well known in diffusion transfer photography the image dye-providing materials which may be utilized in such processing generally may be characterized as either (1) initially soluble or diffusible in the processing composition but which are selectively rendered nondiffusible imagewise as a function of development; or (2) initially insoluble or nondiffusible in the processing composition but which selectively provide a diffusible product imagewise as a function of development. The image dye-providing materials of the invention may be complete dyes or dye intermediates, e.g., couplers. The requisite differential in mobility or solubility may be obtained, for example, by a chemical reaction such as a redox reaction, a coupling reaction or a cleavage reaction. The image dye-providing materials which are capable of providing image dyes including the chromophoric system of Formula D include a diffusion control substituent, Y, which substituent includes a diffusion control moiety, Z. One such group of image dye-providing materials according to the invention is represented by the formula EMI8.1 where R7 and R8 may be the same or different and each may be hydrogen, alkyl, preferably having from 1 to 6 carbon atoms, aryl such as phenyl, alkyl or aryl substituted with any photographically acceptable substituents such as those described above, or (Y) n, each Y is a substituent including at least one diffusion control moiety and each n is O or 1 provided that at least one n is 1. Compounds within Formula F according to the invention are represented by the formulas EMI9.1 It will be noted that Formula G illustrates a naphthyl residue, as designated by A in Formulas D F, which is attached to the nitrogen and oxygen atoms in the 2-azo-l-hydroxy positions and Formula H illustrates a naphthyl residue attached to the nitrogen and oxygen atoms in the l-azo-2-hydroxy positions. In such image dye-providing materials the diffusion control substituent, Y, may be represented by -E-Dev where Dev is a hydroquinonyl group or a precursor thereof and E is a covalent bond or a divalent linking group such as, for example, alkylene. Image dye-providing materials within Formulas F, G and H, as a function of the particular diffusion control moiety, Z, which is present, are suitable for use in diffusion transfer processes employing either initially diffusible or initially nondiffusible image dye-providing materials. Typical suitable diffusion control moieties include, for example, hydroquinonyl.' groups, coupling groups, sulfonamido phenol groups which cleave or ring close following oxidation to release a diffusible dye or dye intermediate, thiazolidine groups whose cleavage is silver catalyzed, and others such as those disclosed in Dye Diffusion Systems in Color Photography, Van de Sande, Angew. Chem. Int. Ed. Engl. 22 (1983), pp 191-209. The diffusion control moiety, Z, may be attached by a covalent bond or a divalent organic radical, for example, an alkylene radical to complete the diffusion control substituent Y. Further where the image dye-providing material is initially diffusible a suitable ballast group, for example, a long chain alkyl group, may be attached to the diffusion control moiety. BRIEF DESCRIPTION OF THE DRAWING For a better understandinq of the invention as well as other objects and further features thereof, reference is made to the following detailed descrip tior: of various preferred embodiments thereof taken in conjunction with the accompanying drawinq wherein: Fig. 1 shows the reflection absorption spectrum of one of the preferred image dye-providing materials of the invention; and Fig. 2 graphically illustrates light stability data obtained for a transparency formed in Example XVI. DESCRIPTION OF THE PREFERRED EMBODIMENTS Specific dyes according to the invention are represented by the formulas EMI11.1 EMI12.1 EMI13.1 EMI14.1 EMI14.2 EMI14.3 The dyes of the invention may be prepared according to techniques which are well known to those skilled in the art as will be apparent from the specific preparative examples which are provided below herein. Accordingly, extensive discussion relating to the preparation of the compounds of the invention is not required. Generally, it is preferred to attach the chromium atom to the para-substituted phenyl-azopyrazolone dye moiety first and subsequently attach the l-naphthol-20-naphthol-l' 2-azo or the 2-naphthol-2'naphthol-l,l'-azo dye moiety. The dye compounds of the invention are typically soluble in various solvents such as, for example, water and various organic solvents such as acetone, methanol, methyl cellosolve, etc. When used as dyes the compounds may be applied to any object such as fabrics and the like by dissolving the dye in a suitable solvent and applying the solution to the object by any of many well known techniques. When used as intermediates in the preparation of image dye-providing materials, the dye compounds can be prepared with the appropriate substituent(s) in the desired position such as, for example, a sulfonic acid or a carboxylic acid group. These groups can then be converted to sulfonyl or carbonyl chloride groups and subsequently reacted with amine hydroquinonyl compounds to attach the silver halide developing hydroquinonyl groups to the dye and provide a dye developer Preferred dye developers according to the invention are represented by the formulas EMI16.1 EMI16.2 EMI17.1 EMI18.1 EMI18.2 EMI19.1 EMI19.2 The imaqe dye-providinq materials can be prepared according to techniques which are well known to those skilled in the art as will be apparent from the specific preparative examples which are provided below herein. Accordinsly, extensive discussion relating to the preparation of the compounds of the invention is not necessary. Generally, it is preferred to attach the chromium atom to the para-substituted phenyl azo pyrazolone dye moiety first dnd subsequently attach the i-naphthcol-2'- naphthol -1', 2-azo dye mo@ety o@ the 2-naphthol-2'- naphthol-l, i'-azo dye mo@ety The black image dye-providing materials of the in Invention typically absorb almost evenly across the visible spectrum as is illustrated by Fig. 1 which is the reflection absorption spectrum of a photographic image made with a film unit includinq Compound I. The image dye-providing materials of the invention may be used generally in association with any silver halide emulsion. As mentioned previously, the image dye-providing materials may be characterized as either (1) initially soluble or diffusible in the processing composition but which are selectively rendered nondiffusible imagewise as a function of development, or (2) initially insoluble or nondiffusible in the processing composition but which selectively provide a diffusible product imagewise as a function of development. The image dye-providing materials may be complete dyes or dye intermediates, e.g., color couplers. The requisite differential in mobility or solubility may be obtained, for example, by a chemical reaction such as a redox reaction, coupling reaction or a cleavage reaction. In a particularly preferred embodiment of the invention, the image dye-providing materials are dye developers which are initially diffusible materials. The dye developers contain, in the same molecule, both the chromophoric system of a dye and a silver halide developing function as is described in U.S. Patent 2,983,606. Other image dye-providing materials of the invention are: initially diffusible coupling dyes such as are useful in the diffusion transfer process described in U.S. Patent 3,087,817 and which are rendered nondiffusible by coupling with the oxidation product of a color developer; initially nondiffusible dyes which release a diffusible dye following oxidation, sometimes referred to as:"redox dye release dyes, such as described in U.S. Patents 3,725,062 and 4,076,529; initially nondiffusible image dye-providing materials which release a diffusible dye following oxidation and intrarnolecular ring closure as are described in U.S. Patent 3,443,940 or undergo silver assisted cleavage to release a diffusible dye in accordance with the disclosure of U.S. Patent 3,719,489; and initially nondiffusible image dyeproviding materials which release a diffusible dye following coupling with an oxidized color developer as described in U.S. Patent 3,227,550. The diffusion transfer film units of the invention include those wherein the image receiving element is designed to be separated from the photosensitive element after processing and integral positive-negative diffusion transfer film units which are retained intact after processing. In a preferred embodiment the diffusion transfer film units of the invention utilize initially diffusible dye developers as the image dyeproviding materials. As described in U.S. Patent 2,983,606, a photosensitive element containing a dye developer and a silver halide emulsion is photoexposed and a processing composition applied thereto, for example, by immersion, coating, spraying, flowing, etc., in the dark. The exposed photosensitive element is superposed prior to, during, or after the processing composition is applied, on a sheet-like support element which may be utilized as an image-receiving element. In a pre ferred embodiment, the processing composition is applied to zoo the exposed photosensitive element in a substantially uniform layer as the photosensitive element is brought into superposed relationship with the image-receiving layer. The processing composition, positioned intermediate the photosensitive element and the image-receivlr,a layer, permeates the emulsion to initiate developnent of the latent image contained therein. The dye developer is immobilized or precipitated in exposed areas as a consequence of the development of the latent image. This immobilization is apparently, at least in part, due to a change in the solubility characteristics of the dye developer upon oxidation and especially as regards its solubility in alkaline solutions. It may also be due in part to a tanning effect on the emulsion by oxi dized developing agent, and in part to a localized exhaustion of alkali as a result of develonment. In unexposed and partially exposed areas of the emulsion, the dye developer is unreacted and diffusible and thus provides an imagewise distribution of unoxidized dye developer, diffusible in the processing composition, as a a function of the point-to-point degree of exposure of the silver halide emulsion. At least part of this imagewise distribution of unoxidized dye developer is transferred, by imbibition, to a superposed imagereceiving layer or element, said transfer substantially excluding oxidized dye developer. The image-receiving layer receives a depthwise diffusion, from the developed emulsion, of unoxidized dye developer without appreciably disturbing the imagewise distribution thereof to provide a reversed or positive color image of the developed image. The image-receiving element may contain agents adapted to mordant or otherwise fix the diffused, unoxidized dye developer. In a preferred embodiment of said U.S. Patent No. 2,983,606 and in certain commercial applications thereof, the desired positive image is revealed by separating the image-receiving layer from the photosensitive element at the end of the suitable irnbi & ition period. Alternatively, as also disclosed in said U.S. Patent No. 2,9R3,oC6, the image-receiving layer need not be separated from its superposed contact with the photosensitive element, subsequent to transfer image formation, if the support for the image-receiving layer, as well as any other layers intermediate said support and image-receiving layer, is transparent and a processing composition containing a substance, e.g., a white pigment, effective to mask the developed silver halide emulsion or emulsions is applied between the imagereceiving layer and said silver halide emulsion or emulsions. Dye developers, as noted in said U.S. Patent No. 2,983,606, are compounds which contain, in the same molecule, both thechromophoricsystem of a dye and also a silver halide developing function. By "a silver halide developing function" is meant a grouping adapted to develop exposed silver halide. A preferred silver halide development function is a hydroquinonyl group. In general, the development function includes a benzonoid developing function, that is, an aromatic developing group which forms quinonoid or quinone substances when oxidized. Particularly useful products for providing dye developer images are disclosed in U.S. Patent No. 3,415,644. This patent discloses photographic products wherein a photosensitive element and an image-receiving element are maintained in fixed relationship prior to exposure, and this relationship is maintained as a laminate after processing and imaqe formation. In these products, the final image is viewed through a transparent (support) element against a light-reflecting, i.e., white background. Photoexposure is made through said transparent element and application of the processing composition provides a layer of light-reflecting material to provide a white background. The light-reflecting material (referred to in said patent as an "opacifying agent") is preferably titanium dioxide, and it also performs an opacifying function, i.e., it is effective to mask the developed silver halide emulsions so that the transfer image may be viewed without interference therefrom, and it also acts to protect the photo exposed silver halide emulsions from postexposure fogging by light passing through said transparent layer if the photoexposed film unit is removed from the camera before image-formation is completed. U.S. Patent No. 3,647,437 is concerned with im provements in products and processes disclosed in said U.S. Patent No. 3,415,644, and discloses the provision of light-absorbing materials to permit such processes to be performed, outside of the camera in which photoexposure is effected, under much more intense ambient light conditions. A light-absorbing material or reagent, preferably a pH-sensitive phthalein dye, is provided so positioned and/or constituted as not to interfere with photoexposure but so positioned between the photoexposed silver halide emulsions and the transparent support during processing after photoexposure as to absorb light which otherwise might fog the photoexposed emulsions. Furthermore, the light-absorbing material is so positioned and/ or constituted after processing as not to interfere with viewing the desired image shortly after said image has been formed. In the preferred embodiments, the light-absorbing material, also sometimes referred to as an optical filter agent, is initially contained in the processing composition together with a light-reflecting material, e.g.. titanium dioxide. The concentration of the light-absorbing dye is selected to provide the light transmission opacity required to perform the particular process under the selected light conditions. In a particularly useful embodiment, the lightabsorbing dye is highly colored at the pH of the processing com;)osition. e.g., 13-14, but is substantially nonabsorbing of isible light at a lower pH, e.g., less than 10-12. This pH reduction may be effected by an acid-reacting reagent appropriately positioned in the film unit, e.g., in a layer between the transparent support and the image-receiving layer. The dye developers may be incorporated in the silver halide emulsion or, preferably, in a separate layer behind the silver halide emulsion. Such dye developer layer may be applied by use of a coating solution containing the dye developer, in a concentration calculated to give the desired coverage of dye developer per unit area, in a film-forming natural or synthetic polymer such as, for example, gelatin, polyvinyl alcohol and the like, adapted to be permeated by the processing composition. Other diffusion transfer products and processes according to the invention are the types described in U.S. Patents 3,573,043 and 3,594,165. For convenience the entire disclosure of each of the five patents referred to immediately above is hereby incorporated by reference herein. As described previously, the image dye-providing materials of the invention are not restricted to dye developers but rather may include many other types of initially diffusible and initially nondiffusible image dye-providing materials. Thus, for example, an initially diffusible coupling dye which is useful in -the diffusion transfer process described in U.S. Patent 3,087,817 may be provided by attaching to the chromophoric system one or more coupling moieties such as a phenol or a naphthol having a free position para to the hydroxyl group. An example of such an image dye-providing material according to the invention is EMI26.1 This dye is initially diffusible but is rendered nondiffusible by coupling with the oxidation product of a color developer, e.g., a p-phenylenediamine or a p-aminophenol, to form a less diffusible product. If the coupling position is substituted by a substituent which renders the dye initially nondiffusible by virtue of a ballast group and which substituent is displaceable upon coupling, such a dye may be employed to provide a diffusible dye where coupling occurs employing the principles described in U.S. Patent 3,227,550. An initially ncjndiffusible "redox dye releaser" image dye-providing material useful in the diffusion transfer process described in U.S. Patent 4,076,529 may be provided by attaching one or more sulfonamidophenol or sulfonamidonapttiol groups to the chromophoric system. An example of such a material according to the invention is represented by the formula EMI27.1 Other sulfonamidophenol and sulfonamidonaphthol groups known in the art, for example, such as those described in U.S. Patent 4,053,312 and 4,055,428, which cleave in alkaline solution at the sulfonamido groups following oxidation may be used in place of the p-sulfonamiodphenol group illustrated above Another class of initially nondiffusible image dye-providing materials (described in U.S. Patent 3,443,940) release a diffusible dye following oxidation and intramolecular ring closure. An image dye-providing material of this type according to the invention is represented by the formula EMI28.1 Other image dye-providing materials which cleave in alkali following oxidatior may be provided by a compound within Formula n or K wllereln Y is -O- or -Sand the hydroquinonyl group contains a ballast group, e.g., C15H31 in accordance with the disclosure of U.S. Patent 3,725,062. An example of such a compound is represented by the formula EMI29.1 It should be noted that although the ballast group shorn in the compounds illustrated above is a ionq chain alkyl group1 other ballast groups known in the art may also be used. In the use of a nondiffusible image dye-providing material which releases c. diffusible image dye-providing material followlrlg oxidation in an alkaline environment, the requisite oxidation may be effected by the oxidation product of a mobile developing agent used to develop the photoexposed silver halide emulsion. A particularly effective developing agent for this purpose is l-phenyl 4,4-8imethyl-3-pyrazolidone; other suitable developing agents are known in the art. Development is advantageously effected in the presence of an onium compound, particularly a quaternary ammonium compound, in accordance with the disclosure of U.S. Patent 3,173,786. Quaternary ammonium compounds which form an active methylene compound in alkali are especially useful. Development may be effected in the presence of a colorless auxiliary or accelerating developing agent such as, for example, a 3-pyrazolidone or a hydroquinone such as 4-methylphenylhydroquinone, which may be initially arranged in a layer of the photosensitive element or in the processing composition. In another preferred embodiment of the invention the diffusion control moiety is a thiazolidine group whose cleavage is silver catalyzed. As described in U.S. Patent 3,719,489, image dye-providing materials of this type are photographically inert in the photographic processing composition but are capable of undergoing cleavage in the presence of an imagewise distribution of silver ions and/or soluble silver complex containing silver ions made available as a function of development to liberate a reaqent in an imagewise distribution corresponding to that of said silver ions and/or said complex. An example of such a compound according to the invention is represented by the formula EMI31.1 The invention will now be described further in detail with respect to specific preferred embodiments by way of examples, it being understood that these are intended to be illustrative only and the invention is not limited to the materials, conditions, process parameters, etc., recited herein. All parts and percentages are by weight unless otherwise specified. EXAMPLE I Exactly 50g (0.25mol.) of 3-hydroxy-2-naphthalene carboxylic acid methyl ester and 18.1g (24.4 ml, 0.25 mol.) of n-butylamine were combined in a 250 ml round bottom flask, heated until a melt formed and then until a gentle reflux started. The reaction mixture was refluxed for about 2 hours after which an additional 15 ml of the n-butylamine was added and the mixture refluxed for an additional hour. The reaction mixture was cooled to room temperature and allowed to stand overnight. The resulting solid was recrystallized from 200 ml of toluene, dried in air overnight and then under vacuum at 400C to give 649 of light yellow crystals. The crystals were stirred in 800 ml of water overnight, acidified to pH 1 with concentrated hydrochloric acid, stirred an additional hour and the product collected by filtration. The product was washed well with water until the washings were neutral and dried in air to give 45.8g (76% yield) of a light yellow solid, m.p. 123 -124 C, represented by the formula EMI32.1 C15H1702N requires 74.05% C, 7.04% H, 13.15% 0 and 5.769N. Elemental analysis found 74.25to, 7.18%H, 13.23@0 and 5.7BEN. To a solution of 1.229 (0.005 mol.) of the previous product in 20 ml of pyridine at 50C, there was added, with stirring l.55q (0.005 mol.) of a diazonium salt represente:: by the formula EMI33.1 and stirring was then continued at room temperature, under nitrogen, for 2 hours. To this mixture there was slowly added 2.5 ml of 50% NaOH and stirring was continued. Coupling took place as evidenced by the. formation of a deep blue color. The solution was stirred for 30 minutes and then slowly poured into 300 ml of stirred water. The mixture was acidified to about pH 6 with concentrated hydrochloric acid and the resulting purple precipitate was collected, washed well with water and dried in air overnight. The crude product was chromatographed on a 2" x 12" silica column, eluted with methylene chloride and then with a mixture of methanol and methylene chloride. The product fractions were combined and evaporated to dryness to give 2.lg (76% yield) of a purple powder represented by the formula EMI34.1 ViS (m@@@. cell. ) @ max 610 n m, #=1@,000. Thin layer @@romatography on whatman KSF silica @ia@es us@@@ 1 : 99 MeOH : CH2CI2 to elute, showed essen- tially a single purple spot, Rf=0.4 with traces of impu@@@ies. C31H2705N3S requires 67.25t C, 4.92t H, 14.45t 0, 7.59% N' and 5.79% S. S. Elemental analysis found 6,.42tC, S.0l%H, 14.27%0, 7.468N and 6.00%S. EXAMPLE II To a dispersion of nitroaminophenol (20g, 0.13 mol.) in 60 mlof acetic acid there was added a solution of sodium nitrite (lOg, 0.14 mol.) in 10 ml of water over a five minute period The resulting azo oxide yellow dispersion was stirred for 20 minutes. A saturated sodium carbonate solution (100 ml) was added to a solution of l-phenyl-3-methyl-pyrazolin5-one (22g, 0.13 mol.) in 500 ml of acetone and the slurry stirred. The azo oxide yellow dispersion was added in portions to the pyrazolone slurry and the mixture stirred for 20 minutes. The reaction mixture was quenched into one gallon of 10% hydrochloric acid. The resulting solid was collected by filtration, rinsed three times with 100 ml of water and dried under vacuum to give an azopyrazolone dye represented by the formula EMI35.1 The azo dye (159, 0.044 mol.) and chromic chloride hexahydrate (35.39, 0.133 mol.) were combined with 100 ml of methyl cellosolve and the mixture was heated to reflux for 2 1/2 hours. The cooled reaction mixture was added to two liters of cold saline solution. The resulting solid was collected by filtration, pressed and rinsed with water and dried under vacuum to yield 20g (95% yield) of a chromed azopyrazolone dye represented by the formula EMI35.2 EXAMPLE III The azopyrazolone dye shown in Example II (lOg, 0.029 mol.) and potassium acetate (109) were dissolved in 75 ml of methyl cellosolve and warmed on a steam cone under nitrogen To the solution there was ridded dropwise a solution of a chromed azo dye (21.5g1 0.029 mol.) represented by the formula EMI36.1 in 400 ml of methyl cellosolve. The reaction mixture was cooled, quenched into 8 liters of water and flocked from solution by adding a minimal amount of 108 hydrochloric acid. The resulting solid was collected by filtration, rinsed and dried to yield 29 g of dye I, a black solid, Vis (meth. cell.) X max 645 n m, ±21,500; 592 n m, ±=20,700; 500 n m, ±=22,800 C46 H39011N8S2Cr requires 55.91% C, 4-168 H, 10.9t N, 6.07% S and 5.53% Cr. Elemental analysis found 55,478 C. 3.95% H, 11.25% N, 6.44% S and 5.22% Cr. EXAMPLE IV The azo dye of Example I (1.Og, 0.0018 mol.), O.86g (0.0018 mol.) of the chromed azopyrazolone dye of Example II, 20 ml of ethanol and 0.53g of KOAc were combined in a 125 ml round bottom flask and heated to reflux. After 15 minutes all of the azo dye had been consumed but a small amount of the chromed azopyrazolone dye remained (as monitored by TLC). Small amounts of the azo dye were added at 10 minute intervals (about 0.15g total) and refluxing was continued. The reaction mixture was cooled at room temperature and quenched into 350 ml of stirred water. The solution was acidified to pH of about 1 with con centrated hydrochloric acid. The resulting, very fine black precipitate was collected, washed with water and dried in air to give l.4g (818 yield) of a black solid, dye VI, Vis (meth. cell.) X max=390 n m, c=19,000; 500 n m, s=17,200; 595 n m, e=15,400; 647 n m, c=16,400. C47H39010N8Cr ¯ 2H2O requires 56.68% C, 4.35% H, 19.28t 0, 11.25% N, 5.22% Cr and 3.22% S. Elemental analysis found 56.56% C, 4.14tH, 11.118 N, 4,838 Cr and 3.73% S. EXAMPLE V To a mixture of the chromed azopyrazolone dye of Example II (0.9g, 0.0019 mol.), 1.0g (0.0019 mol.) of an AZO dye represented by the formula EMI38.1 arid 0.559 (0.0056 mol.) of KOAc in a 50 ml round bottom flask there was added 25 ml of ethanol with stirring and the resulting solution brought to reflux, under nitrogen, on a steam cone. After 30 minutes a small amount of the chromed azopyrazolone dye was added and refluxing was con tinued for one additional hour. The reaction mixture was allowed to cool to room temperature and stirring was con tinued overnight. The entire mixture was poured into about 300 ml of water and acidified to pH of about 1 with concentrated hydrochloric acid. The resulting fine black precipitate was collected on a Buchner funnel, washed with a small amount of acidic water and air dried to give about l.Bg of a black solid. The crude product was dispersed in about 75 ml of ethyl acetate and stirred for about two hours. The product was collected by filtration, washed well with ethyl acetate and dried in air to give l.6g (898 yield) of dye VII. Vis (meth. cell.) X max = 505 nm, E = 19,300; 595 nm, E = 17,800; 652 nm, E = 18,300. EXAMPLE VI Fast @@d ITR (@.Ug, 0.019 mol.) (Aldrich Chenical Co.) was suspended in a mixture of 60 ml of ethanol, 7 ml of @@@ and 15 ml of water with stirring and there was slowly ddded dropwise a solution of NaNo2 (1.33:j, 0.019 mol.) on 3 mi of Water. Stirring was continued in an ice bath for 10 minutes during which time the dye slowly dissolved to give a brownish yellow solution. Methyl ph@nyl py@a@@lone (3. 3@, 0.019 mol.) was dissolved in d mixture of :)0 ml of pyridin@, 200 ml of methanol and 200 ml of water With Stirring and the Fast Red ITR diazonium solution poured Lnto the pyrazolone solution in a slow steady stream. The reaction solution turned orange and then an orange precipitate formed. The mixture was then stirred for 30 minutes, quenched into stirred ice water and acidified to pHl with 60 m of conc. HC1. 'rhe product was collected by filtration, washed with water and recrystallized from methyl cellosolve to give 7.79 (90% yield) of an azo dye represented by the formula EMI39.1 in the form of orange crystals. The structure of the dye was confirmed by a NMR spectrum. The azo dye compound (3.0g, 0.0068 mol.), chromium chloride hexahydrate (6.67g, 0.025 mol.) and 20 ml of methyl cellosolve were combined and heated to reflux with sitrring for 3 hours. The resulting dark orange solution was cooled to room temperature and slowly poured into 200 ml of well stirred brine. The resulting brown precipitate was collected, washed with cold water and dried in air to give 4.09 (1008 yield) of a brown powder represented by the formula EMI40.1 UV, Vis (meth. cell) X max = 330 nm, C = 8,000; 360 nm, E = 6800; 495 nm, E = 16,800. The chrome complexed dye (lOg, 0.0018 mol.) was dissolved in 20 ml of ethanol and to the solution there was added the azo dye illustrated in Example V 0.94g, 0.0018 mol.) and then KOAc (0.53g) and the mixture brought to reflux with stirring. The reaction mixture quickly turned blackish. After 15 minutes an additional O.lg of the azo dye was added and the solution refluxed for an additional 45 minutes, then cooled to room temperature and allowed to stir overnight. The resulting precipitate was collected by filtration, wahsed with ethanol, dried in air and then under vacuum to give 1.7g (92% yield) of black dye VIII. UV, Vis (meth. cell.) X max - 350 nm, e = 15,800; 490 nm, E = 17,200; 505 nm, C = 17,600; 500 nm, E = 14,500; 600 nm; E = 18,200; 652 nm, C = 19,000. EXAMPLE VII To a stirred mixture of 4-lti tro-2-arr,inophenol (30.8g, 0.2 mol.) in 40 ml of acetic acid at 100C there was added dropwise, over 20 minutes, a solution of sodium nitrate (13.8g, 0.2 mol.) in 30 ml of water. Stirring was continued for an additional 15 minutes. The resulting diazonium solution was then added in portions at 100C to a stirred solution of 1469 (0.2 mol.) of a pyrazolone compound represented by the formula EMI41.1 Ir: hOU ml of pyridine. The resulting solution was stirred for one-hal hour and then quenched into a stirred solution of four gallons of ice water containing 600 ml of concentrated hydrochloric acid. The solid was collected by filtration, rinsed well with water, pressed and dried. Recrystallization from two liters of acetonltrlle yielded 160@ (90@ yield) of a light orange dye, Vis(meth. cell.) A max 410 n m, E = 13,200, 513 n m, @ = 6,200, represented by the formula EMI42.1 C54 H49 N508 requires 72.4Y C, 5.47% H, 7.82% N and 14.38 O. Elemental analysis found 72.#% C, 5.7% H, 7.958 N and 14 25z 0 To a solution of compound (XXII) (15q, 0.0167 mol.) in one liter of methylene chloride, under argon at ambient temperature, there were added, with stirring, boron trifluoride etherate (2.4g, 0.17 mol.) and 2-bromo1,3,2-benzodioxaborole (34g, 0.17 mol i and stirring was continued for 12 hours. The reaction mixture was quenched into a 2 phase dispersion of water (2 liters) and petroleum ether (500 ml) with rapid stirring. The product separated as a solid and was collected by filtration. Recrystallization from acetonitrile yielded 8.0g (90% yield) of a yellow dye developer represented by the formula EMI43.1 Vis (meth cell.) X max = 410 n m, # = 14,700. C26H25O8N5 requires 54.64% C, 5.11% H and 12.258 N. Elemental analysis found 54.89t C, 5.08 ii and 12.92d N. Compouna XXIII(5g, 0.009 mol.) and chromic chloride hexahydrate (7.5g,0.028 mol.) were combined in 75 ml of methyl cellosolve under nitrogen and heated to reflux for two hours. The cooled solution was quenched into 500 ml of saline solution. The resulting solid was collected by filtration, rinsed with cold 50t brine and then with water and dried under vacuum to yield 5.3g of a brown solid, Vis (meth. cell.) A max 490 n m, E = 14,800, 520 n m, # = 10,400, represented by the formula EMI44.1 EXAMPLE VIII A five liter, three neck round bottom flask eslulpsJed with an overhead stirrer was charged with 80gq (0.26 mol.) of an azo oxide compound represented t the formula EMI45.1 one liter of pyridine and two liters of ethanol followed by l-naphthol-4-sulfonic acid sodium salt (100g, 0.41 mol. 600 ml of water and 600 ml of saturated sodium bicarbonate solution. The slurry was stirred at ambient temperature for 48 hours. Analysis by thin layer chromatography indicated complete reaction. The reaction mixture was quenched into 4 gallons of ice water which included 1 liter of concentrated hydrochloric acid. The resulting solid was collected by filtration, rinsed with water and dried in air to give 100g (78% yield) of an azo dye represented by the formula EMI45.2 Vis (meth. cell.) #max Sln n m, = 11,400. EXAMPLE IX Compound XXIV (2g, 0.029 mol.) and Compound XXV (1.5g, 0.'##29 . ) were combined tr, ##() ml of methyl cellosolve with tributy]amine (l.O9y, 0.0059 mol.) and warmed on a Steam cone for one hour. The reaction mixture was quenched into cold 108 hydrochloric acid and the resulting solid collected, rinsed and dried to give 3g (798 yield) of black dye developer IX, Vis (meth. cel I . ) # max 650 n m, #=22,800; 598 n m, E =21,200; 505 nm, # = 20,200. EXAMPLE X Compound X was prepared in the same manner described in Example IX with the exception that potassium acetate was used as a base instead of tributylamine. Vis (meth. cell.) X max 653 n m, E = 19,200; 600 n m, e = 18,000, 500 n m, # = 17,600. EXAMPLE XI Compound XI was prepared in the same manner described in Example IX with the exception that an azo diethylsulfonamide dye compound was employed in place of the azo sulfonic acid dye. The reaction gave l.85g of black dye developer XI (97% yield), Vis (meth. cell.) 500 n m, C = 23,000; 590 n m, E = 22,000; 641 n m, C = 23,000. C68H78015NgS2 Cr requires 59.2% C, 5.8% H,17.4%0, 9.1% N, 4.6% S and 3.8% Cr. Elemental analysis found 59.1%C, 5.5%H, 17.9%0, 8.8%N, 4.68S and 3.8%Cr. EXAMPLE XII Compound XII was prepared in the manner described in Example XI with the exception that an appropriately substituted propylamine was used instead of diethylamine in the preparation of the dye. EXAMPLE XII Compound XIII was prepared in the manner described in Example XI with the exception that EMI47.1 was used instead of diethylamine to form the dye and the methyl ether groups were converted to hydroxy groups by reaction with 2-bromo-1,3,2-benzodioxaborole prior to forming the complete dye developer, Compound V. Vis (meth. cell.) A max 622 n m, E- = 16,000, 580 n m, e =17,900, 504 n m, e = 18,000. EXAMPLE XIV Exactly 10.19 (0.05 mol.) of 3-hydroxy-2naphthalene carboxylic acid methyl ester and 100 ml of methylamine (40% solution in water) were combined in a flask and refluxed for two hours. The solution was cooled to room temperature and stirred overnight. The reaction solution was quenched into a stirred solution of 1500 ml of ice water and 75 ml of conc. hydrochloric acid. The resulting yellow precipitate was collected by filtration , washed well with water and dried in air. The crude product was recrystallized from 300 ml of toluene to give 8.8g (88% yield) of product, light yellow crystals, represented by the formula EMI48.1 The previous product (1.0s, 0.005 mol.), the .#zr oxide utilized in ExaxpleVIll (1.55g, 0.005 mol.) and 75 ml of acetone were combined in a flask and stirred under nitrogen while being cooled in an ict bath To the mixture there was added with stirring, 5 ml of a 50#. (w/v) solution of Nazis The reaction vessel was rer.-jved from the ice bath and stirrirq under nitrogen was continued as the reaction mixture warmed. The mixture slowly turned greenish, then deep blue and finally deep purple. The solution was stirred for an additional 1 1/2 hours and then quenched into a solution of 300 ml of ice water and 10 ml of conc. hydrochloric acid. The resulting purple precipitate-water mixture was stirred overnight. The precipitate was collected by filtration, washed with water and about one liter of a 7:3 solution of methanol in water and dried in air overnight to give 1.4g (55% yield) of a purple powder represented by the formula EMI48.2 A solution of compound XXIV (1.3g, 0.0019 mol.) in 35 ml of ethanol was formed and to it there were added with stirrinq, ,otassiunl acetate (0.6q, 0.006 mol.) aria then Compound XXVI (l.Og, 0.002 mol.). The mixture was then brought to reflux under n# trogen and quickly turned black. After 5 minutes an additional O.lg of Compound XXVI was added te the reaction mixture which was then refluxed an additional 15 minutes. The reaction mixture was quenched inte j solution of 100 ml of water, 50 ml of salllle Ijid 5 ml of conc hydrochloric acid. The resultinu black precipitate was collected by filtration, washed well WitEI 100 ml of water and dried under vacuum to give l.6g (748 yield; of a black powder, dye developer XIV, Vis (meth. cell. max 648 n m, s = 16,500; 595 n m, # = 15,400; 49b n m, E = 17,000; 390 n m, ± = 17,200. EXAMPLE XV A film unit according to the invention was prepared wherein the negative element comprised a transparent subcoated polyester photographic film base having the following layers coated thereon in succession: 1. a dye developer layer comprising about 70 mg./ 2 ft. (753 mg./m.2) of Compound (IX) and about 50 mgs./ft. (538 mgs./m.ê of cellulose acetate hydrogen phthalate; 2. a blue sensitive silver iodobromide emulsion layer coated at a coverage of about 200 mgs./ft.2 2 (1614 mgs./m. ) of silver (1.6 microns) and about 96 2 (1033 mgs./m. 2) of gelatin; and mg./ft.ê (1033 mgs./m.ê) of gelatin; and 3 a layer (:om¯rlsing about 7.5 m#s./ft.2 i81 mgs./m.ê) of 4'-methyl (phenyl hydroquinone. about 30 .2 ms.ift. (323 mgs./m.2) of gelatin and about 15 mgs./ ft.2 i162 mgs./m.2) of diethyldodecamide; The image receiving element comprised a transparent subcoated polyethylene terephthalate photographic film base on which there were coated the following layers in succession: : 1. as a tolymeric acid layer approximately 9 parts of a 1/2 butyl ester of polyethylene/maieic anhydride copolymer and 1 part of polyvinyl butyral 2 coated at a coverage of about 2450 mg./ft. (26,372 2 mgs./n. ¯ 2. a timing layer containing about 300 mq./ft.2 (3229 mgs./m. 2) of a 60 - 29 - 6 - 4 - 0.4 pentapolymer of butylacrylate, diacetone acrylamide, methacrylic acid, styrene and acrylic acid and including about 5% polyvinyl alcohol; and 3. a polymeric image receiving layer of (a) 3 parts of a mixture of 2 parts polyvinyl alcohol and 1 part poly-4-vinylpyridine and (b) 1 part of a graft copolymer comprised of 4-vinylpyridine (4VP) and vinyl benzyl trimethyl ammonium chloride (TMO) grafted onto hydroxyethyl cellulose (HEC) at a ratio of HEC/4VP/TMQ of 2.2/2.2/1 coated at a coverage of about 300 mg./ft. (3229 mg./m.ê).mg./ft. The film unit was processed with a processing composition comprised of WEIGHT PERCENT Sodium hydroxide 5.0 Titanium dioxide 50.0 Phenylmercaptotetrazole 0.1 6-methyl uracil 0.5 Carboxymethyl hydroxyethyl cellulose 3.0 Water to make 100% The negative was exposed (2 meter-candle-seconds) on a sensitometer to a test exposure scale using a xenon light source and then processed by passing the negative together with the image receiving element through a pair of rollers set at a gap spacing of 0.0020 inch. The film unit was kept intact in the dark for 10 minutes. A well developed dye image was obtained. The neutral density column of the image was read on a densitometer to obtain the Dmax and Dmin values for red, green and blue light respectively. R G B Dmax 1.27 1.30 1.24 Dmin 0.37 0.38 0.37 The reflection spectrum illustrated in Fig. 1 was obtained from an image made using a film unit identical to that described above with the exception that 2 layer 2 of the negative had about 120 mgs./ft. (1292 mgs./m.2) of silver (1.6 microns) and about 80 mgs./ft.2 2 (861 mgs./m. ) of gelatin. It can be seen that the black image dye material absorbs generally evenly across the visible spectrum. EXAMPLE XVI A film unit according to the invention was prepared wherein the negative element comprised a transparent subcoated polyester photographic film base having the following layers coated thereon in succession: 1. a polymeric iioaqe receiving layer containing 2 2 about 300 mgs./ft. (3229 mgs./m. ) of (a) 3 parts of a mixture of 2 parts polyvinyl alcohol and 1 part poly-4-vinylpyridine and (b) 1 part of a graft copolymer comprised of 4-vinylpyridine (4VP) and vinyl benzyl trimethyl ammonium chloride (TMQ) grafted onto hydroxy- ethyl cellulose (HEC) at a ratio of HEC/4VP/TMQ of 2.2/2.2/1 and about 5 mgs./ft.ê (54 mgs./m.ê) of 1, 2.2/2.2/1 and about 5 mgs./ft. '54 mqs./m. of 1, 4-butanediol diglycidyl ether; 2. a release layer made up of about 30 mgs./ ft.2 (323 mgs./m.2) of hydroxyethyl cellulose and about 30 mgs /ft.2 (323 mgs./m.2) of polyethylene wax; 2 3. a layer comprising about 30 mgs./ft. (323 2 2 mgs./m.ê) of gelatin and about 15 mgs./ft. - (161 mgs./m.ê) of carbon black; ; 4. a pan sensitive silver iodobromide emulsion 2 layer coated at a coverage of about 125 mgs./ft. (1345 mgs./m. 2) of silver (1.6 microns) and about 100 mgs./ft. 2 (1076 mgs./m. 2) of gelatin; and 5. a top coat layer comprising about 30 2 2 mgs./ft. (323 mgs./m. ) of gelatin and about 2.5 mgs./ ft.2 (27 mgs./m.2) of succindialdehyde. A second element was prepared having a transparent subcoated polyester photographic film base on which there was coated a dye layer made up of about 2 2 150 mgs./ft. (1614 mgs./m. ) of Compound IX and about 2 100 mgs./ft. (1076 mgs./m.2) of gelatin. The film unit was processed with a processing composition comprised of WEIGHT PERCENT potassium hydroxide 5. n Phcnylmercaptotetrazoie 0.1 Phenidone 0.4 Zinc nitrate 3.0 Sodium thiosulfate 0.1 Carboxymethyl hydroxyethyl cellulose 3.0 Water to make 100 The negative was exposed to a test exposure scale with white light (2 meter-candle-seconds) and passed, together with the second element, through a pair of rollers at- a gap spacing of about 0.0024 inch. The film unit was kept intact in the dark for 5 minutes and then stripped apart at the release layer. A high resolution positive transparency image was obtained in the image receiving layer. The transmission densities to red, green and blue light were read on a transmission densitometer. The results are shown below. R G B Dmax 0.93 1.01 0.96 Dmin 0.03 0.03 0.05 Another transparency was made In the same parne'. described above ulth the exception that the processing composition included 0.28 of phenylnercaptotetrazole and did not Include any sodium thiosul fate and the film unit was processed without any Light exposue. The Image receiving element was then used to determine the dye stability by exposing t, from the image receiving layer side, to the conditions of a Xenon Arc Weatherometer over a period of 33 days. The transparency was periodically rtmoved from the weatherometer and the optical density to red, green and blue, respectively measured on a densitometer. Fig. 2 graphically illustrates the data obtained as percent dye retained (as a function of optical density) for red, green and blue light. It can be seen that the image dye providing material exhibits excellent light stability. Further it is also evident that the slight fading which did occur is generally similar for the red, green and blue light measurements thus illustrating that the material fades evenly across the visible spectrum. EXAMPLE XVII A film unit according to the invention was prepared wherein the negative element comprised a transparent subcoated polyethylene terephthalate photographic film base having the following layers coated thereon in succession: 1. a dye developer layer comprising about 78 (840 mgs./ft.ê(840 mgs./m.ê) of Compound XIII ft. 2 (538 mgs./m. 2) of cellulose acetate hydrogen phthalate; 2. a blue sensitive silver iodobromide emulsion layer coated at a coverage of about 200 mqs./ ft.2 (2153 mgs./m.ê) of silver (1.6 microns) and about 100 mqs./ft.2 (1076 mgs./m. 2) of qelatin; ; and 3. a layer containing about 30 mgs./ft.ê of gelatin (323 mgs./m.2) of gelatin about 7.5 mgs./ ftê (81 mgs./m.ê ) of 4'-methyl phenyl hydroquinone 2 and about 2.5 mgs./ft.ê (27 mgs./m.ê) of succindialdehyde - The same image receiving element and processing composition described in Example XV were used. The film unit was processed in the same manner described in Example XV. A well developped image was obtained. A Dmax = 1.46 and Dmin = 0.60 were obtained with a reflection densitometer using green light. Although the invention has been described in detail with respect to various preferred embodiments thereof, these are intended to be illustrative only and not limiting but rather those skilled in the art will recognize that modifications and variations may be made which are within the spirit of the invention and the scope of the appended claims.

Claims: CLAIMS 1. A compound represented by the formula EMI56.1 where A is EMI56.2 R is hydrogen, -NO2, -S03H or -SO2NR1R2; R1 and R2 are the same or different and each is hydrogen, alkyl, or phenyl; and X is a cation. 2. A compound as defined in Claim 1 which is represented by the formula EMI57.1 wherein R3 and R4 are the same or different and each is hydrogen, alkyl or phenyl. 3. A compound represented by the formula EMI57.2 wherein A is EMI58.1 R' is hydrogen -NO2, -SO 3H or -SO2NR"R"'; R" and R"' are the same or different and each is hydrogen, alkyl, phenyl, or alkyl or phenyl substituted with (Y)n; R7 and R8 are the same or different and each is hydrogen, alkyl, phenyl or (Y)n, Y is a substituent including at least one diffusion control moiety, n is O or 1, provided that at least one n is 1, and X is a cation. 4. A compound as defined in Claim 3 wherein said diffusion control moiety is selected from the group consisting of a hydroguinonyl silver halide developing moiety, a coupling phenol or naphthol moiety having an available coupling position para to the hydroxyl group, a sulfonamidophenol group which will cleave or ring close following oxidation and a thiazolidine group which is capable of silvercatalyzed cleavage. 5. A photosensitive element comprising a support, a silver halide emulsion in a layer carried by said support, and an image dye-providing material in a layer carried by said support on the same side thereof as said silver halide emulsion, said image dye-providing material being capable of providing an image dye containing the chromophoric system represented by the formula EMI59.1 wherein A is EMI59.2 R' is hydrogen, -NO2, -503H or -SO2NR"R"'; R" and R"' are the same or different and each is hydrogen, alkyl, substituted alkyl, aryl or substituted aryl; and X is a cation. 6. A photosensitive element as defined in Claim 5 wherein said image dye providing material is capable of providing an image dye containing the chromophoric system represented by the formula EMI60.1 wherein R5 and R6 are the same or different and each is hydrogen, alkyl, substituted alkyl, aryl or substituted aryl. 7. A photosensitive element as defined in Claim 5 wherein said image dye-providing material is a compound represented by the formula EMI60.2 wherein R7 and #8 are the same or different and each is hydrogen, alkyl, substituted alkyl, aryl, substituted aryl or (Y)n, Y is a substituent including at least one diffusion control moiety, and n is O or ', provided that at least one n is 1. 8. A photosensitive element as defined in Claim 7 wherein said diffusion control moiety is selected from the group consisting of a hydroquinonyl silver halide developing moiety, a coupling phenol or naphthol moiety having an available coupling position para to the hydroxyl group, a sulfonamidophenol group which will cleave or ring close following oxidation and a thiazolidine group which is capable of silvercatalyzed cleavage. 9. A photosensitive element as defined in Claim S wherein R is -NO2. 10. A photosensitive element comprising a support, a silver halide emulsion in a layer carried by said support, and an image dye-providing material in a layer carried by said support on the same side thereof as said silver halide emulsion, said image dye providing material being represented by the formula EMI62.1 where X is a cation. 11. A diffusion transfer film unit comprising (a) a photosensitive element as defined in Claim 5; (b) a second sheet-like element adapted to be superposed on said photosensitive element prior to during or after photoexposure; (c) an image receiving layer positioned in one of said photosensitive or second sheet-like element; and (d) a rupturable container releasably holding an aqueous alkaline processing composition and so positioned as to be adapted to distribute said processing composition between predetermined layers and said elements. 12. A diffusion transfer film unit as defined in Claim 11 wherein said image dye-providing material is capable of providing an image dye containing the chromophoric system represented by the formula EMI63.1 wherein R5 and R6 are the same or different and each is hydrogen, alkyl, substituted alkyl, aryl or substituted aryl. 13. A diffusion transfer film unit as defined in Claim 11, wherein said image dye-providing material is a compound represented by the formula EMI64.1 wherein R7 and R8 can be the same or different and each is hydrogen, alkyl, substituted alkyl, aryl, substituted aryl or (Y)n, Y is a substituent including at least one diffusion control moiety, and n is O or 1, provided that at least one n is 1. 14. A diffusion transfer film unit as defined in Claim 13 wherein said diffusion control moiety is selected from the group consisting of a hydroquinonyl silver halide developing moiety, a coupling phenol or naphthol moiety having an available coupling position para to the hydroxyl group, a sulfonamidophenol group which will cleave or ring close following oxidation and a thiazolidine group which is capable of silver-catalyzed cleavage. 15. A diffision transfer film unit as defined in Claim 11 wherein R is -NO2. 16. A diffusion transfer film unit comprising (a) a photosensitive element comprising a support, a silver halide emulsion in a layer carried by said support and an image dye-providing material in a layer carried by said support on the same side thereof as said silver halide emulsion, said image dye-providing material being represented by the formula EMI65.1 where X is a cation; (b) a second sheet-like element adapted to be superposed on said photosensitive element prior to, during or after photoexposure; (c) an image receiving layer positioned in one of said photosensitive or second sheet-like elements; and (d) a rupturable container releasably holding an aqueous alkaline processing composition and so positioned as to be adapted to distribute said processing composition between predetermined layers of said elements. 17. A diffusion transfer process comprising (a) imagewise exposing a photosensitive element including a silver halide emulsion and an image dye-providing material containing at least one diffusion control moiety which is capable of providing a diffusion image dye containing the chromophoric system represented by the formula EMI66.1 wherein A is EMI66.2 R' is hydrogen -NO2, -SO3H or -SO2NR"R"'; R" and R"' are the same or different and each is hydrogen, alkyl, substituted alkyl, aryl or substituted aryl; and X is a cation; (b) developing said exposed photosensitive element with an aqueous alkaline processing composition; (c) forming an imagewise distribution of said diffusible image dye from said image dye-providing material as a function cf development; and (d) transferring at least a portion of said imagewise distribution of said diffusible image dye to an image receiving layer arranged in superposed relationship with said silver halide emulsion to provide a diffusion transfer dye image. 18. A diffusion transfer process as defined in Claim 17 wherein said image dye-providing material is capable of providing a diffusible image dye containing the chromophoric system represented by the formula EMI67.1 wherein R5 and R6 are the same or different and each is hydrogen, alkyl, substituted alkyl, aryl or substituted aryl. 19. A diffusion transfer process as defined in Claim 17 wherein said image dye-providing material is a compound represented by the formula EMI68.1 wherein R7 and R8 are the same or different and each is hydrogen, alkyl, substituted alkyl, aryl, substituted aryl or (Y)n, Y is a substituent including at least one diffusion control moiety, and n is O or 1, provided that at least one n is 1. 20. A diffusion transfer process as defined in Claim 19 wherein said diffusion control moiety is selected from the group consisting of a hydroquinonyl silver halide developing moiety, a coupling phenol or naphthol moiety having an available coupling position para to the hydroxyl group, a sulfonamidophenol group which will cleave or ring close following oxidation and a thiazolidine group which is capable of silvercatalyzed cleavage. 21. A diffusion transfer process as defined in Claim 17 wherein R is -NO2.

Inventors: KING, PATRICK F., STROUD, STEPHEN G.
Applicants: POLAROID CORPORATION
Application year: 1984
Main classification: C09B45
IPC codes: G03C8, C09B45