GLASS FOR CATHODE RAY TUBE FACEPLATE

Abstract: Glass compositions suitable for cathode ray tube facep­ lates which are essentially free from As₂O₃, MgO, fluorine, and PbO, consist essentially, in weight percent, of

Description: GLASS FOR CATHODE RAY TUBE FACEPLATE This invention relates to a glass for a cathode ray tube faceplate. The faceplate for a cathode ray tube of the type used in television picture tubes is prepared from a transparent glass demonstrating a high degree of Xradiation absorption and excellent resistance to discoloration caused by the bombardment of high velocity electrons thereupon and exposure to Xradiation. The glass must also exhibit a number of physical properties mandated by the process for manufacturing cathode ray tubes. For example: The faceplate glass must display a coefficient of thermal expansion approximating that of glasses customarily utilized in cathode ray tube manufacture (a99 X 10 / C over the temperature range of 250-3000C), in order to assure good compatibility with such glasses and the metal components that are sealed therein. To minimize distortion of the glass components during manufacture of the tube, the glass will most preferably manifest an annealing point not lower than about 500 C and a strain point not lower than about 4550C. On the other hand, for ease in melting and forming, the glass will evidence a liquidus temperature lower than 9000C and, preferably; no higher than about 8800C, and will exhibit a viscosity at the liquidus of at least 100,000 poises. Further, in order to insure proper operation of the tube, the glass must exhibit an electrical resistivity, expressed in terms of Log p, greater than 9 at 250 C and greater than 7 at 3500C. Where electric melting of the glass is contemplated, easily reducible metal oxides, particularly PbO and As2O3, will preferably be essentially absent from the composition. It has been conjectured in the glass art that the inclusion of readily reducible metal oxides in a faceplate composition renders the glass susceptible to discoloration resulting from electron browning. Also, volatilization of arsenic creates an air pollution problem. MgO will desirably be essentially absent from the compositions. Although the mechanism therefor is not fully understood, the presence of MgO appears to render the glass more susceptible to devitrification. Finally, whereas fluorine has frequently been employed as a flux to assist the melting process because its presence does not substantially affect the electrical resistivity of the glass, its volatilization from the glass batch during melting creates a severe air pollution problem. Furthermore, the inclusion of fluorine exacerbates corrosion of the molds used in forming the faceplates'., Consequently, means have been sought to elim6áte the fluorine from the batch while compensating fr%fti'ts beneficial fluxing and softening effects on the glass without sacrifice of electrical properties. Objective of the Invention Therefore, the principal objective of the instant invention is to provide glass compositions essentially free from As2O3, MgO, fluorine, and PbO, which exhibit coefficients of thermal expansion between 97-100 X 10 7/tC (250-3000C), annealing points not lower than about 5000C, strain points not lower than about 4550C, liquidus temperatures lower than 9000C, electrical resistivities (Logp) greater than 9 and greater than 7 at 2500C and 3500C, respectively, and liquidus viscosities of at least 100,000 poises, which are suitable for use as faceplates for cathode ray tubes, and which are designed for melting in electrically-powered melting units (but which can also be melted in conventional fossil fuel fired melting units). Summary of the Invention That objective can be achieved through glass compositions essentially free from As203, MgO, PbO, and F consisting essentially, expressed in terms of weight percent on the oxide basis, of SiO2 60-63 Li2O 0.25-0.75 Al2O3 1.5-3 CaO 1.5-2.5 BaO 5-9 ZrO2 1.5-3 SrO 8-10 TiO2 0.25-0.75 Na2O 7.25-9;5 CeO2 o.15-0.5 K 20 6-8 Colorants conventionally utilized in television picture tube faceplate glasses, e.g., Co3O4, Cr203, and NiO, may also be included, if desired, in customary amounts. Such levels normally range up to about 20 ppm (parts/million) Cho304, up to about 20 ppm Cur203, and up to 250 ppm NiO. Although relatively readily reducible, Sb203 may be tolerated in amounts up to 0.58 to perform as a fining agent. Hence, where a fining agent is deemed necessary, Sb2O3 may be employed instead of As 203 since it is not as easily reduced as As203. Even where electric melting of the glass is not contemplated such that reduction thereof is not as serious a problem, its absence is preferred and no more than about 0.25% can be tolerated. The above ranges of components must be rigorously observed to insure the production of glasses suitable for use as cathode ray tube faceplates and exhibiting the desired physical properties. Thus, TiO2 and CeO2 provide protection against discoloration resulting from exposure to X-radiation. BaO, SrO, and ZrO2 act to absorb X-radiation. And the levels of those components and the ranges of the other glass constituents must be carefully balanced to yield glasses exhibiting the required viscosity characteristics for melting and forming, along with the desired thermal expansion and liquidus value. To illustrate, an increase in the Na2O or K2O content lowers the viscosity of the glass at its liquidus. Li2O has a powerful effect in softening the glass, while increasing the electrical resistivity of the glass, and permits the elimination of fluorine as a fluxing agent in the glass. Nevertheless, because of this strong fluxing action, the Li2 0 content must be carefully controlled. A1203 imparts good chemical durability thereto but has the unwanted side effect of ardening the glass. CaO tends to soften the glass and increase its electrical resistivity, but has the undesirable effect of increasing the liquidus temperature. Higher levels of SrO, BaO, and ZrO2 reduce the liquidus viscosity of the glass. In summary, then, the several components of the inventive glasses will be manipulated within the delineated straitly-defined regimes in order to insure the demanded viscosity characteristics, liquidus values, and physical properties. U.S. Patents 3,464,932; 3,805,107; 3,925,089; 3,987,330; 4,015,966; 4,065,697; 4,089,693; 4,331,770; 4,337,410; and Japanese application No. 53-113813 (1978) are considered to be representative of the state of the art; none of these teach or suggest this invention. Description of the Preferred Embodiments Table I recites a number of glass compositions, expressed in terms of parts by weight on the oxide basis,-illustrating the parameters of the invention. Inasmuch as the sum of the individual components closely approximates 100, for all practical purposes the tabulated values may be deemed to represent weight percent. The actual batch ingredients may comprise any materials, either the oxides or other compounds, which when melted together, will be converted into the desired oxides in the proper proportions. Because it is not known with which cation(s) the fluorine is combined, it is merely reported in terms of fluoride ion, in accordance with conventional glass analysis practice. The batch constituents were compounded, tumble mixed together to aid in obtaining a homogeneous melt, and then charged into platinum crucibles. Lids were placed upon the crucibles and the crucibles were introduced into a furnace operating at 15500 C. After melting for six hours, the molten batches were poured into steel molds to form glass slabs having dimensions of 6" x 6" x 0.5", (15.24 x 15.24 x 1.27 cm), and those slabs transferred immediately to an annealer operating at 5000 C. Samples were thereafter cut from the slabs to be used for the determination of various physical properties. Table I 1 2 3 4 SiO2 61.4 61.08 62.5 62.6 Al2O3 2.0 2.00 2.0 BaO 5.7 5.7 5.7 3.7 SrO 9.7 9.7 9.7 9.7 Na2O 8.1 10.25 8.6 8.6 K20 7.1 5.5 6.6 8.0 Li2O - 0.1 CaO 1.8 1.8 1.8 1.8 MgO - 0.02* - ZrO2 2.5 2.50 2.5 3.5 TiO2 0.4 0.50 0.4 0.4 CeO2 0.2 0.3 0.2 0.2 Sb2O3 - 0.35 - - F 0.7 - - - CO3O4 - 0.0005 - - NiO - 0.0004 - As2O3 - 0.2 - - 5 6 7 8 SiO2 62.7 61.56 60.58 61.33 A12 3 2.0 2.0 2.00 1.99 BaO 1.7 5.49 7.90 5.69 SrO 9.7 9.63 9.20 9.7 Na2O 8.6 8.07 7.55 8.26 K2O 9.4 7.01 7.1 7.09 Li 0 - 0.52 0.5 0.5 2 CaO 1.8 1.8 1.8 1.8 MgO - - 0.02* 0.02* ZrO2 4.5 2.49 2.00 2.5 TiO2 0.4 0.5 0.50 0.5 CeO2 0.2 0.34 0.30 0.3 Sb2O3 - 0.38 0.35 0.35 F- - - Co3O4 - - 0.0005 0.0005 NiO - - 0.0004 0.0004 2 3 0.21 0.2 * Impurity in batch material; not intentionally added. Table II sets forth measurements of various physical properties conducted on samples of Examples 1-8. Thus, values of the softening point (Soft.), the annealing point (Ann.), and the strain point (Str.), all in OC, the coefficient of thermal expansion between 25 -300 C (Exp.) in terms of X 10-7/ C, the internal liquidus temperature in C (Liq.) determined employing a platinum boat in a temperature gradient furnace, the electrical resistivity, expressed in terms of Logp, measured at 2500C and 3500C and the viscosity of the glass (Vis.) at the liquidus temperature in terms of poises, as derived from a standard curve generated by the glass, are included. Table II 1 2 3 4 Soft. 708 698 720 722 Ann. 520 518 525 533 Str. 480 476 499 491 Exp. 94.6 100.4 95.4 97.1 Liq. 858 795 883 903 Logp 250 - 8.461 - Logp 350 - 6.675 - Vis. 5 6 7 - 8 Soft. 731 691 694 689 Ann. 539 507 508 502 Str. 495 473 467 460 Exp. 96.0 98.5 98.3 98.0 Liq. 963 878 812 877 Logp 250 - - 9.70 9.14 Logp 350 - - 7.73 7.23 Vis. - 12 x 104 - 12 x 10 As 203-free Example 8 represents the most preferred embodiment of the invention. Examples 1-5 clearly illustrate that minor variations in composition outside of the specified ranges yield glasses exhibiting properties and behavior outside of those desired.

Claims: CLAIMS: 1. A glass essentially free from As203, MgO, fluorine, and PbO suitable for manufacturing faceplates for cathode ray tubes which exhibits a coefficient of thermal expansion (250-3000C) between 97-100 X 10 7 an annealing point not lower than about 5000C, a strain point not lower than about 4550C, an internal liquidus temperature lower than 9000C, LogP at 2500C greater than 9 and Logs at 3500C greater than 7, and a liquidus viscosity of at least 100,000 poises, said glass consisting essentially, expressed in terms of weight percent on the oxide basis, of C SiO2 60-63 Li2O 0.25-0.75 2 3 1.5-3 CaO 1.5-2.5 BaO 5-9 ZrO2 1.5-3 SrO 8-10 TiO2 0.25-0.75 Na2O 7.25-9.5 CeO2 0.15-0.5 K20 6-8 Sub203 0-0.5 2. A glass according to claim 1 also containing up to 20 ppm Cho304 and/or up to 20 ppm Cr203 and/or up to 250 ppm NiO. 3. A process for the preparation of a glass as claimed in claim 1 or claim 2 characterised in that one melts together oxides or materials convertible thereto on melting in those proportions which will give a glass as claimed in claim 1 or claim 2. 4. A cathode ray faceplate tube characterised in that it consists of a glass as claimed in claim 1 or claim 2 or a glass made as in claim 3.

Inventors: FRIESEN, GLEN DELBERT
Applicants: CORNING GLASS WORKS
Application year: 1984
Main classification: C03C3
IPC codes: H01J29, C03C3