STORABLE DENTAL PORCELAIN PASTE

Abstract: A storable paste-like material for use in preparing porcelain dental prostheses comprises porcelain powder, water, and a small amount of a finely divided ceramic material that overcomes the dilatance of the mixture of porcelain powder and water.

Description: STORABLE DENTAL PORCELAI!J PASTE The invention relates to dental porcelain in a 'storable, paste form. Background of the Invention Dental porcelain that is employed in the production of prostheses such as crowns and bridges, is typically marketed in the form of a fine powder. Then the powder is to be used, it is then mixed with a liquid, usually water containing a small amount of a wetting agent, and is then applied to a metallic coping as a thin film. The practice of mixing the powder with liquid just before use necessarily entails a certain amount of waste, because more material will ordinarily be mixed than will be used. It would be desirable to be able to premix the porcelain powder with the liquid dispersant, however, th'e ¯c'o'nven- tional porcelain powders that are now employed in the nanufacture of dental prostheses exhibit the property of dilatancy, when mixed with water. This means that the water/porcelain powder mixture tends to harden upon standing, and actually tends to become stiffer under the influence of nixing or shearing forces. Thus, dilatancy is, in one sense, the'opposite of the property known as n thixotropyt The present invention is based upon the discovery that a finely divided ceramic material can be added to the dental porcelain powder in a snall proportion, and that such. finely divided ceramic will overcome the tendency of water/porcelain powder mixtures to become dilatant. As an added bonus, the resulting mixture of water, porcelain powder, and finely divided ceramic exhibits a more plastic-like feel, is less gritty, and has- slightly better working properties than the conventional porcelain powder/water nixtures. Brief Sunnarv of the Invention The invention provides a storable paste-like material for use in preparing porcelain dental prostheses, which conprises porcelain powder, water, and finely divided ceramic. The finely divided ceramic has a particle size and is present in such proportion that it overcomes the dilatancy of the mixture of porcelain powder and water. The Prior Art The connercial supplier of "VsEGUIln materials; which are colloidal magnesium aluminum silicates or magnesium silicates, recomnends that they be used as suspending agents in ceramics, as plasticizing agents for nonplastic formulations such as high alumina or zirconia bodies, and as nonnigrating binders in extruded bodies. Detailed Description of the Invention The dental porcelain powders that are employed in the invention are azell-known materials. They are generally forned from nixtures of oxides of silicon, aluninum, titanium, alkali metals, alkaline earth metals, and boron. The mixture of oxides is selected to possess certain properties, such as to match the coefficient of thermal expansion of the netal copings on which the porcelain will be coated, as well as the appropriate mixture of opacity and translucency so that the porcelain will resemble as closely as possible the natural tooth. All of these factors are well-known in the art, and do not constitute part of this invention. The porcelain powders are usually finely divided, having average particle sizes in the range of from 20 to about 40 c r and more usually about 30 + 5 The finely divided ceramic additive that is employed in the invention is used for the purpose of neutralizing or overconing the tendency of porcelain powders to form a dilatant paste when mixed with water or other liquid. Preferred naterials for use in the invention are colloidal magnesium aluminum silicate and magnesium silicate. Other ceramics can also be used in the invention, provided that they have firing properties that are compatible with those of the dental porcelain enploye;. The necessary qualities of the ceramic powder are the following: First, it should nelt or dissolve in the porcelain at a temperature no higher than the porcelain's maturing temperature; Second, it should not significantly alter the thermal expansion, corrosion resistance, and shade (color) properties -of the porcelain; and Third,- it must be very finely divided, i.e'., colloidal, as discussed below. The powdered ceramic is employed in finely divided form, that is, it has an average particle size such that it will inpart thixotropic properties to a mixture of porcelain powder, water, and the finely divided ceramic, when the ceramic is used in small proportions. Typically, the particle size of the ceramic is generally less than 0.3 F and preferably it has an average particle size 9f less than 0.1 e wo. - The powdered ceramic is employed in smalL proportions, typically from 1/4 to 1 weight per cent based upon weight of the porcelain powder. The third component of the storable paste-like material of the invention is water. Water is usually employed in a proportion of from , 24 to 28 weight per cent, based upon -weight of the dental porcelain powder. The, preferred way of preparing the paste-like material'of the invention is to first mix the water with the finely divided ceramic, and to then add the porcelain powder. However, if desired, the ceramic can also be first mixed with the porcelain powder, followed by addition of the water. The mixture of porcelain powder, water, and finely divided ceramic provided by the invention is a paste-like material having the approximate consistency and handling characteristics of modeling clay. This material can be prenixed by the nanufacturer, and can be stored in tubes or syringes for ease of use by the dentist or dental technician who will be employing the material in the production of dental prostheses. Example 1 and Control Example 1 Samples of paste are made from the following formulations: The porcelain powder used in all the experiments haS the following composition: Component Weight Per Cent SiO2 66.7 Al203 14.3 MgO 0.1 CaO 1.4 Na2O 6.0 K20 10.0 Li2O 1.1 S O .0.3 Zro 2 0.1 The porcelain powder has the following particle size analysis: : Particle Diameter, P nL. Cumulative %, Smaller 5 7 10 21 20 48 50 92 As a, Control Example, the above-described porcelain powder is mixed with distilled water containing 1/2 weight per cent of 35 per cent aqueous phosphoric acid (a's a pH adjustor) and ; 1 weight per cent wetting agent, in proportions of .74 weight per cent powder to 26 weight per cent water. The resulting paste 'cannot conveniently be dispensed through a syringe opening or from a flexible tube, because the paste tends to harden when pressure is applied to it. When one attempts to squeeze it out of a flexible tube, there is a tendency for the water and powder to separate so that only water is squeezed out of the tube. If the foregoing experiment is repeated except that 1 weight per cent of colloidal (particle size less than about 0.3 m ) ) magnesium silicate is added to the water (percentage based on weight of water--based on weight of porcelain powder, the percentage would be 1/3) before it is mixed with the porcelain powder, then the resulting paste is smooth, has the consistency of modelling clay, and can be stored in and squeezed out of a flexible tube or a syringe having a 1/8- to 1/4-inch opening. The paste also feels less gritty than the Control, and is easier to smooth on the metallic coping used for a dental restoration. After firing, the porcelain containing the colloidal ceramic has the same appearance as the fired Control porcelain when used as a thin film or layer on a dental restoration. The magnesium silicate employed is a commercially available material sold as "VEEGUM T". It has the following typical analysis (expressed as oxides): 'SiO2 53.74 Mg 23.82 A1203 0.97 Fe2 3 0.15 CaO 4.54 fla 2O 1.74 0.1 Li2O 0.93 Ignition Loss 11.81

Claims: EMI7.1 1. A storable paste-like material for use in preparing porcelain dental prostheses, which comprises porcelain powder, water, and finely divided ceramic, said finely divided ceramic having a particle size and being present in such proportion'4that it overcomes the dilatance of the mixture of porcelain powder and water. 2. The storable paste-like material of claim 1 wherein said finely divided ceramic is a magnesium silicate. EMI7.2 3. The storable paste-like material of claim wherein the finely divided ceramic is employed in an anount of from : 1/4 to I weight per cent, based on weight of porcelain powder. EMI7.3 4. The storable paste-like material ofAclaim 3 wherein the water is present in amounts df from 24 to 28 weight per cent, based on weight of porcelain powder. 5. A method of preparing a storable paste-like material for use in preparing porcelain dental prostheses, comprising mixing together porcelain powder, water and finely divided ceramic, said finely divided ceramic having-alparticle size and being present in such proportion that it will overcome the dilatance of the mixture of porcelain powder and water. 6. The method of claim 5, wherein the water is first mixed with the finely divided ceramic and the procelain powder is then added.

Inventors: JONES, ROBIN MACKAY FORBES, PANZERA, CARLINO
Applicants: JOHNSON & JOHNSON DENTAL PRODUCTS COMPANY
Application year: 1984
Main classification: A61K6
IPC codes: A61K6