ISLAND RECORD FILMS; FABRICATION

Abstract: A novel optical data storage medium is contemplated, one apt for data-modulated writing with a laser beam (and reading with a non-erasing reading laser beam) of predeter­ mined wavelength -- the embodiments thereof being char­ acterized by an island-film information structure on multiple layers whose optical characteristics and thickness are chosen to accommodate a prescribed writing and reading energy and wavelength, whereby to provide an anti-reflection condition for unrecorded portions of the information film and a relatively higher reflectivity for recorded portions; the island configuration being adapted to be so affected by the contemplated write beam as to "agglomerate" and better transmit the read beam.

Description: "ISLAND RECORD FILMS; FABRICATION" The present invention relates to novel thin film structures and more particularly to such films of metal rendered in semicontinuous, "island" form. INTRODUCTION, BACKGROUND This is a Continuation-in-part of my copending application USSN 381694 for "Insular Record Films for Digital Data Storage", filed May 1982, which, by this reference, will be understood as incorporated herein to the extent consistent herewith. Workers in the art of making,and using very thin metal films for recording (e.g., order of afew AO to a few hundred AO) are typically interested.#in making those as continuous as possible, with little or no void area. By contrast, this invention concerns itself with intentionally rendering thin films to be semi-continuous, in "island" (insular) form. It has been found, and is here explained, that such "insular" films may be laid down (e.g., vacuum deposited) so as to exhibit a fairly uniform pattern of islands and void-intervals, with fairly uniform island size and thickness -- doing so with techniques that are (rather precisely) controllable and repeatable, and are relatively straight-forward and inexpensive (e.g., using a known type of vacuum deposition). According to a related feature, it has been found that such "insular" films exhibit some advantageous, unexpected properties and characteristics. For instance, when a metal like gold is so deposited (as "islands"), the insular film appears to exhibit (some) properties which are quite a bit different from those of the bulk metal (e.g., melting at a much lower temperature), and -- as spelled out in great detail in my cited USSN 381694 -insular films can be quite advantageously adapted for an optical (laser) record. Thus, most of the following description of the fabrication and use of exemplary "insular" films is cast in terms of optical disk records, apt for digital laser recording, though workers will contemplate other, quite different applications. Thus, it is an object hereof to provide the foregoing, and other related, features and advantages. A more particular object is to do so, teaching the deposition of gold and like films in "island" (or like discontinuous) form. Another object is to teach such films exhibiting good heat-response, as well as extended service life. A further object is to teach a preferred way of preparing such films. BRIEF DESCRIPTION OF THE DRAWINGS These and other features and advantages of the present invention will be appreciated by workers as they become better understood by reference to the following detailed description of some presently preferred embodiments, these being considered in conjunction with accompanying drawings, wherein like reference symbols denote like elements: : (FIGS. 1-13 are the same as in my cited USSN 381694, the description of which has been incorporated herein by reference, except to the extent inconsistent herewith, this description not being reproduced here in full, in the interests of brevity.) FIG. 1 provides a greatly-enlarged cross-sectional view of an idealized portion of a prior art recording medium; FIG. 2 provides --a similar view of novel recording medium exhibiting a construction in accordance with principles reflecting the present invention; FIG. 3 is a similar view of a related disk record; FIGS. 4 and 6 are idealized plan views of exemplary recorded "bits"; FIG. 5 is a sectional view of another such record; FIG. 7 is a plot of reflectance vs. wavelength for two different exemplary records; ; FIG. 8 is a crude idealized plan view, greatly enlarged, of a different "insular" (actually "peninsular") film; FIG. 9 is a mechanical schematic of a "heat shutter" application of an insular film; FIGS. 10, 11, 12, and 13 are TE micrographs of various "insular" films; and FIGS. 14-21 are TE micrographs of yet other examples of "insular" films. DETAILED DESCRIPTION As mentioned, this description should be understood as explained in terms of (though not limited to) the fabrication of optical recording films ("OR" records) adapted to be "written-upon" by a (prescribed type of) laser radiation and read-back in like fashion (i.e., as per description in cited USSN 381694). Such-"OR records" will be understood as rendered on an "anti-reflective" base, (cf., preferably as part of a "trilayer" as discussed in USSN 381694 and references therein). How such a "trilayer" has heretofore been employed in media using "ablative" absorber films, or other such known "deformational" information structures, will next be discussed. "Disruptive/Deformational" information-structures (using "trilayer"): According to one known approach (see article by A. E. Bell and F. W. Spong, IEEE J. Quantum Electron., QEl4, 487 1978), trilayer optical data storage media utilize a rigid substrate upon which is deposited, in order; an opaque metallic reflector layer, a dielectric spacer, and a thin absorber (or information layer, typically comprised of a low-melting-point metal). The thickness of the dielectric spacer is chosen such that the information layer is at the peak of the standing wave of the optical electric field upon exposure to a focused beam of laser radiation. As the incident radiation is absorbed in a write-site of the information layer, the temperature of this site rises until a physical "disruption" or deformation of the information layer occurs. This disruption, or "deformation" at the write-site, exposes the underlying reflector, resulting in a large and irreversible increase of reflectance, and so creating a written "bit". With conventional trilayer media, such deformation-disruption of the information layer during a laser write-event may be understood as following one of three mechanisms, as follows: (1) The information layer may undergo local ablation with material being ejected from the bit site; or (2) The absorber may undergo local melting, with disruption of the molten metal due to surface tension effects, resulting in a rim of solidified material about the circumference of the bit site; or (3) The material of the spacer layer may be chosen such that heat conducted to this layer from the information layer causes local decomposition and gas evolution in the spacer. The expanding gas causes a slight deformation of the information layer, and the bit site takes the form of a hemispheric bubble. These three "bit-forming" processes may be understood, respectively, as "ablation", "rim formation", and "bubble formation" -- all being disruptive and/or deformational. That is, those bit-formation mechanisms involve some significant "deformation" and/or "disruption", i.e., either a volume change of significant proportions, or mass transport of debris over distances that are large with respect to the radius of the bit site. As a consequence, all these mechanisms reviewed as inherently incompatible with the usual presence of massive conventional in-contact overcoat. This has given rise to some complex overcoat configurations designed to accommodate these gross physical movements involved in such bit formation; e.g., "air gaps" and other "non-contact" design approaches. From the standpoint of simplicity, durability, and cost of fabrication, the use of an "in-contact" over coat is attractive and advantageous. For the concept of an "in-contact" overcoat to be feasible in practice, however, the bit formation mechanism must proceed without (the need for) "deformation" or disruption", i.e., with out gross motion or mass transport over distances that are a significant fraction of the bit radius. Novel "island" information-structures (not "disruptive/deformational): The development of trilayer optical data storage media compatible with an in-contact overcoat is here treated. Such media will be seen to use a conventional metallic reflector and dielectric spacer configuration, but the information layer will constitute a thin, discon tinuous (gold) "island-film", representing a significant -departure from known approaches. The use of an island film as the information layer gives rise to a unique recording - (bit-forming) mechanism -- "agglomeration" -- that appears capable of being relatively unaffected by the presence of a massive, in-contact overcoat, especially one having a rough "fissured" contact-face. The following describes how island films are made and used, and includes details of this "agglomeration" mechanism in trilayer media incorporating island-gold as the information layer. A phenomenological model is presented to explain observed behavior, describing "agglomeration" and how it functions in the presence of an incontact overcoat. EXAMPLES The following Examples are given by way of teach ing some exemplary concepts, uses, and advantages of such island-film absorbers and associated writing (by "agglomeration") therewith, according to the invention -- to some extent duplicating, as well as supplementing, details of USSN 381694. Advantages and features of the island films will be better appreciated by comparing them with "deformational" absorbers known in the art and described in USSN 381694, such as the "Te Example" (Tellurium). --Example I; absorber of gold material; FIG. 2: The operations, material, methods and structure of the "Te Example" (FIG. 1) described in USSN 381694 are followed here, except as otherwise specified, in a novel record 10 (FIG. 2)#havinQa "gold-absorber" film 15 replacing the tellurium absorber film (5 in FIG. 1). Record 10 will be understood as comprising a support 12 on which an "anti-reflective" base 1-AR is laid (like AR in FIG. 1), preferably comprising a dielectric spacer 14 on an opaque metallic reflective layer 13, with absorber film 15 placed atop spacer 14. Here, and according to a salient feature hereof, absorber 15 comprises a very thin (minimum mass) film of "gold material" laid down in an "island layer" configuration and intended to function as an absorber film (cf., the Te film in the "Te Example"; e.g., apt for somewhat similar recording methods and with similar means). Here, very close attention is paid, during deposition, to controlling absorber thickness so that mass is minimized, island-uniformity maximized -- e.g., monitoring to yield a prescribed minimal "Dark Mirror" reflectance X (e.g., here, 10% is suitable#) as further described below. It is vital of course that film 15 be laid down to be semicontinuous (discontinuous), being formed in a highly-uniform "island" configuration (e.g., roughly exemplified in FIG. 11, a 100,000 x TEM, or Transmission Electromicrograph, and as further described below.) The underlying spacer layer 14, reflector layer 13 and substrate 12 are (at least functionally) otherwise the same as in "Te Example", and thus will be understood as functioning as a "trilayer" (with absorber 15) as understood in the art (e.g., see cited references in USSN 381694) "Gold-island" absorber film 15 may (preferably) be formed by vapor-depositing gold onto the surface of dielectric spacer 4 until (monitoring the well-known "trilayer" effect) surface-reflectivity of 15 first drops to preselected value Rm (10% reflectance, here), taking care to render the required "insular" (islands) configuration. Reflectance Rm may, conveniently, be set at any desired value consistent with adequate "writing" and readout. Here, an Rm of about 10% is arbitrarily selected (minimum for proper focusing, etc, of this laser). Then, somewhat surprising to discover, "writing" on this island film with a prescribed laser beam (as in'Te Example" of USSN 381694) can shift reflectance enough to give good read-out in the described manner. That is, a "written spot" may be seen to exhibit 22-55% reflectance, yielding desired S/N (in the 25-40 dB range -- in some cases a 30--50% increase is satisfactory) Workers will appreciate how other "minimum reflectance" values may be chosen for the "virgin" (unwritten) absorber film. --Preparation details re absorber layer 15; (FIG. 2): Absorber layer 15 thus comprises an extremely 25 thin, highly uniform, minimum-mass, "island-deposit" of gold which is vapor-deposited (thermally evaporated or sputtered) onto spacer layer 14 (i.e., on a relatively flat; e.g., 0.5 X record-surface thereof). Somewhat unexpectedly, one finds that if gold is so deposited on such a "trilayer" only until a prescribed "minimum reflectance" Rm (e.g., 10%), the "islands" are formed such that, when subjected to the described laser write-beam (6338 AO, 10 mW for 40 n. sec., etc.), reflectance -- quite desirably, yet wholly unexpectedly! -- changes significantly: quite enough for adequate read-out. (e.g., "pure" gold may be so deposited in large vacuum chamber at 10-6 -7 in large vacuum chamber at 10 6 10 Torr., from a molybdenum boat which is resistance-heated -- deposition rate being about 5-10 A /sec.) All substrates are cleaned according to present good practice for optical thin films. A light silica "strike" (alternatively Mg.Fl., or the like) may be likewise vapor-deposited on spacer 14 as a "nucleation-strike" before the gold island film 15 is deposited. The "strike" should, in optimized instances, induce minimum-mass, minimum-size islands uniformly across the spacer. It is important that this deposition (by thermal evaporation) cease once the reflectance of film 15 first attains the predetermined "minimum-mass/minimum reflectance level" (Rm) yielding the desired "islands" -- otherwise the contemplated "islands" and associated results may not be produced. As workers know, such deposition may be programmed empirically, or by continually monitoring the surfacereflectance of a "witness-chip" while absorber film 15 is deposited until satisfactory "islands" begin to appear (and see somewhat related deposition approach of Zech in his cited article, in USSN 381694, or refer to other known methods, such as monitoring deposited mass or electrical properties during deposition). --Results of EX. I: The results (laser recording on this "island" configuration) are most surprising, especially in light of expected properties and as compared with conventional media like the known Te absorber films (e.g., prepared as above-described in the "Te Example" of USSN 381694). That is, record 10 will be understood as recorded-upon, read-out and evaluated, with its sensitivity, etc., measured, as in the cited "Te Example" of USSN 381694 (e.g., using an He-Ne laser system of the type mentioned). ThQ so-written bit sites will exhibit the mentioned "agglomeration" (where absorber islands at a write-site have been made to form spheres, and these spheres coalesce when heated by the write-energy) -- this across a write-site diameter comparable to the diameter of the write-beam (e.g., 1/4-3/4 thereof). This "agglomeration" is seen to be accompanied by an associated increase in reflectance and read-out signal. FIG. 6 is an artistic rendering showing such a very crude form of an "agglomerate-hole" (written bit) based on photomicrographs of such records. Here an "agglomerate-hole" 15p will be understood as a somewhatcircular written-spot, or physical optical discontinuity in the "virgin" (unwritten) absorber island film 15v. The size of spot 15 may be on the order of laser writebeam diameter (e.g., 40-120% thereof). Within the spot 15pw the same amount of absorber material is present, but the write-beam has "agglomerated" (consolidated) tiny islands into "absorber-globs" gL, most of which are relatively larger (and usually fewer) than the tiny "islands" of virgin film 15v and FIG. 11, (and lying relatively farther apart once so written). In effect, spots 15p will be understood as constituting an "optical discontinuity" at the selected readwavelength ( Aw); whereas the (physically discontinuous) virgin is1and#film 15v appears relatively continuous optically -- and a (partial) reflector. Workers will appreciate how such non-deformational "Åagglomeration holes" 15p can be the - fun6tional equivalent of conventional deformational pits like those known with tellurium (see Te Ex. and references cited in USSN 381694). As detailed below, one finds that such an "insular" absorber film can yield a superior record; one giving considerable archival stability, unexpectedlyhigh sensitivity and high S/N, while requiring surprisingly low write-energy, and low write-temperature evidently -- and also apparently having good tolerance to an overcoat. For instance, where, for an island absorber, a useful overcoat need not degrade operational performance beyond practical usefulness -- as presently happens with Te and other deformational absorbers, perhaps because these evidently require a relatively massive translation/deformation of absorber material -- in contradistinction, workers will be pleasantly surprised to note that the invention can "record" (i.e., "open" a bit-hole to "pass" the Read beam) without need for such extensive translating and/or deforming of the absorber in the bit-site -- instead the invention can operate by merely "agglomerating", and thus redistributing absorber within the bit-site, with relatively little or no material necessarily moved extensively across, or outside the site, or ablation-ejected therebeyond, etc. Details are given below. --Island form of absorber film: FIG. 11 is a microscopic plan view (100,000 x TE micrograph) of the original, virgin (i.e., unrecordedupon) reflecting surface of a gold-island absorber film like that above-described. It will be evident that this surface appears as a physically, semi-continuous, or partly discontinuous, "insular" configuration, exhibiting a fairly regular "island" pattern (on an SiO2 spacersurface). For this EX. I, the unwritten islands will be understood as having diameters on the order of a few hundred AO (e.g., 100-300 AO typical), separated by intervals of comparable dimension (e.g., 50-200 AO apart -- vs. laser beam 5000-10,000 AO wide; cf 6328 A0 wavelength). The virgin film 15 will thus exhibit a certain "% void" range (e.g., a few % to 40% voids). Now, subjecting a portion of this virgin film to a laser recording beam as described acts to so "agglomerate" these "islands", increasing the "percent void" in the site (larger island-spacing) -- thus forming an "agglomerate-hole" as in FIG. 6, this process being, here, loosely characterized as "agglomeration". This "island" configuration was not expected -yet more surprising were the unusual "recording properties" realized such as agglomeration -- effects which were quite different from any other recording films and from what the properties of "bulk gold" would indicate! As mentioned above, forming "ODD absorber" films (or any media structure) to exhibit an "island" configuration is unmentioned in the literature; moreover it seems to be contrary to present "good practice" (e.g., as U.S. 4,222,071 makes clear -- see discussion in USSN 381694). At least some of the first-order factors controlling such island formation are believed to be: absorber material, deposition-rate, adhesion; substrate material and condition (e.g., cleaning, roughness, "strike" film as "nucleation surface") and temperature; presence of vapor-contaminants (vacuum pressure) and like factors as will be appreciated by workers. For example, too-cool a substrate will render a continuous film, too-hot will leave no film at all. In this regard workers may compare FIGS. 12 and 13 with FIG. 11. For FIG. 12, a similar film was prepared (like EX. I) except that a silica spacer was coated with a bismuth oxide layer (a "nucleation" aid known in the art). For the FIG. 13 case, a chromium nucleation layer was used. Compared with FIG. 11, the FIG. 12 seemed to exhibit thinner islands, farther apart, while FIG. 13 is a continuous gold film (no islands). The cited laser apparatus could not "write" at all on the film of FIG. 13 (at cited power level); while the film of FIG. 12 wrote generally as in FIG. 11 (EX. I) except for a bit lower sensitivity. Workers will now appreciate that such an "island" absorber can render certain desired results -- taking into account such factors as read/write conditions (e.g., writeenergy, beam-width, X, etc.). Thus, in EX. I satisfactory "bit holes" about 4000 to 10,000 AO diameter were formed with the specified write-beam, etc. (gave satisfactory S/N, etc.). As further detailed below, "agglomeration" (for prescribed write/read conditions) seems to require not only a satisfactory (virgin) island film, but depends (at least to some extent) on "island temperature" and "mobility" during writing (i.e., on the maximum temperature reached by "melting" islands and their associated mobility during the agglomeration phase) -- these, in turn, depending on virgin-island size and "interfacial energy" of melting islands in contact with the host surface(s). --Desired virgin island pattern: One infers that island-diameters or separation which are too large (or too small) will not be satisfactory. More particularly, it seems that the virgin size and spacing of the islands should be such as to accommodate a desired agglomeration, upon recording, with average island diameter well below anything approaching a continuous film (i.e., sufficient spacing and percent void to thermally isolate individual islands); yet large enough (% void low enough) so that absorber film 15 "appears" like a relatively continuous) "optical reflector" at selected X (R/W lasers). And spacing is presumably large enough so that when a spot is laser-heated (written-upon) it will so "agglomerate" to a significant, detectible extent and form the indicated "agglomerate-hole", causing the film 15 to "optically switch" and exhibit a significant shift in detected reflectance (consistent with required S/N, etc. -- i.e., so the "spot" becomes "relatively transparent" now and appears relatively "open" and transparent to the optical system concerned, somewhat like a conventional "pit"). --Desired "agglomeration" Stated otherwise, the write-beam is assumed, here, to so affect the islands in a bit-site as to cause "agglomeration",--with attendant "sphericizati6n" and increase in average island size and spacing (increased % void area). One infers that the initial (virgin) % void will be sufficient to accommodate a prescribed minimal heatAoss, radially, yet not so large that initial reflectance (Ro) exceeds the desired "near zero" value (required for a "Dark Mirror") -- workers will note that so-opening the absorber in a trilayer gives an effective increase in reflectivity (e.g., as here, from about 10% to about 30%). In general, one may describe this writing operation as so energizing the absorber island film as to, in effect, "significantly redistribute" absorber mass at the bit site -- yet not to the extent exhibited by disruptional/"deformational" (non-insular or continuous) films! Thus where an unwritten island site (absorber film only) may exhibit 25% absorption-45% transmission-30% reflection, the "so-written" film site may shift these values to about 10% - 70% - 20%, respectively, for the subject write wavelength (whereas the overall trilayer values would shift from 90% - 0% - 10% to 40-50% - 0% - 60-50%). As this "writing" so increases the percent void (area), one infers that the write beam evidently so energizes the islands at a write-site that their average size increases and their average spacing increases (i.e., they "agglomerate" to a written pattern of fewer islands). --"Island-films" as such: Now, "thin metallic films in island form" have received some attention in the literature as a general proposition (i.e., entirely apart from record media applications -- e.g., see article with this title by Doremus in J. App. Physics: June '66, Vol. 37, &num;7, pp 2775 et sequ. where gold films were described -- also see "Optical Constants of Aggregated Gold Film" by Truong, et al. in J. Optical Society Am., Vol. 66, &num;2, February 1976, pp 124 et sequ. where such films were formed by evaporating onto hot glass substrates at 300 C, and wherein the authors opine "it is reasonable to assume that the particles themselves have the bulk optical constants" of their native material; also see "Structural and Electrical Properties of Discontinuous Gold Films on Glass" by Andersson and Norman in "Vacuum", Vol. 27, &num;4, 1977, Pergamon Press, Great Britain: studying electrical resistance of such films, indicating that this resistance exceeds that of the bu ] k gold). Yet no worker appears to have discovered, or even suggested, that there is any advantage to using any such "island films" in a recording medium, whether of gold or any other metal. Indeed, workers appear to have contemplated only "continuous" absorber films for media (e.g., see cited U.S. 4,222,071 specifying that the absorber should "not be agglomerated" but should be a "continuous film"; or see IBM-TDB of March '71, p. 3001, teaching a continuous "metal layer such as gold plus an amorphous sub-layer" like amorphous silicon - these layers to be heated to form "a mixture of gold, crystalline silicon and amorphous silicon", etc.). It was quite accidental and fortuitous that I happened to so render such a "minimum reflectance" insular deposition onto a "trilayer structure". Otherwise I cannot have expected to provide such ODD records exhibiting satisfactory sensitivity and S/N over a long service life (see below). Now, as mentioned, such "island" absorber films seem rather strikingly and unusually affected by a relatively low-energy "write-pulse" -- so that, without evidently being heated to gold's published melting point, the virgin island masses are nonetheless redistributed (agglomerated). This is not predicted by the literature! On the contrary, many workers have assumed that thin metal films would exhibit the properties of the bulk metal. A few have differed, opining that some properties (none related to recording though) may differ. Thus, a worker just could not be sure how such an "island" absorber film would perform in an "OD disk" context (like that here described). Workers will recognize how surprising it is that such island films can be laser-written so as to generate such "agglomerated holes". One might, rather, expect that absorber film continuity was needed to "spread" the (laser-softened) material at the write-site (e.g., pull-apart the pit site, as the cited Zech article postulates, stating that "surface tension" causes a "transverse cavitation", etc.). Workers will welcome a system whereby bits can be radiation-recorded without the intense heat and macroscopic changes implicit in the well-known gross melting (ablating) of a deformational absorber film (as with a Te absorber in the cited "Te Example", and without need for any such massive translation of absorber material). --Overcoating; effects (EX. I-A): The cited "Te Example" is also run with a thin overcoating of SiO (100 AO, vapor deposited) on the (continuous) Te absorber film. This simulates an overcoat, but does not afford a true, full functional overcoat of the kind workers typically postulate (like several mils of a transparent polymer to permit record handling without scratching, to "defocus" surface dust, grime, etc. to impede vapor entry, e.g. of water, oxygen. But this light SiO coat will# nonetheless affect Te "pit formation", raising required write-energy to about double. (Possibly because it so restricts the Te film at the pit-site as to impede associated displacement of Te material there). Workers have expected that such "deformationaldisruptive recording" (as with pits in Te, bubbles in other metals, etc.) would be resisted by any "overcoat" (e.g., read-out signal destroyed; sensitivity raised -the overcoat impeding, if not prohibiting, absorber translation, deformation and/or expulsion from the bitsite, and barring any "ejecta" of course). Significantly however, when a gold island-film like those here described is similarly over-coated (herewith EX. I-A), little or no such resistance is evident and sensitivity is only slightly degraded -- if at all -- further evidence that a different type of bitforming mechanism is at work. (Although, as detailed below, such an absorber coating (SiO2) is disfavored in favor of a more "fissured" coating like the described "modified fluoro-polymer".) As workers will agree, this reinforces the theory that the instant recording mechanism is quite novel (evidently whatever deformation and/or movement of the island mass accompanies such low-power writing of a "bit", it is better tolerated by an overcoat, i.e., the overcoat presents less resistance to the bit-forming mechanism -this being consistent with the described "agglomeration"). This amplifies the attractiveness of such insular absorbers, since tolerance to overcoating is very, very important. --Absence of "Bulk-Au" properties: As another feature hereof, and based on the foregoing Example I, and others, one would infer that such an "island film" absorber (of gold) is not behaving as would be predicted from its reported "Bulk" (gold) properties (e.g., radial conduction of heat is not likely to be significant). The discovery of such characteristics of "insular films" and associated uses, is significant and is further discussed below. It would appear that these "agglomerate-holes" (reflectivity-switched) are formed at temperatures wellbelow the absorber's melting temperature (of bulk gold), that they involve little or no absorber expulsion and that so-writing on them (and agglomerating them) requires much less write-energy. In general, workers may expect that such insular absorber films can be used to make OD disks as contemplated (e.g., satisfying all or most of the usual requirements of such -- see also USSN 381694). --TE Micrographs (FIGS. 14-21): Here, the transmission electron microscope (TEM) is utilized as a major analytical technique to study the morphology, and elucidate the mechanism, of bit formation in trilayer media with island-gold as the information layer. This is an especially powerful technique when combined with a media performance diagnostic such as a laser read/write system, because it allows the direct correlation of media performance parameters, such as read signal amplitude and signal-to-noise ratio, with actual data bit morphologies as observed in the TEM. For the examples of FIGS. 14-21, trilayer optical recording exemplars for TEM examination are deposited upon carbon pre-coated 200 mesh copper grids. The coatings consist of an aluminum reflector, dielectric spacer layer, and a gold absorber layer. An electron-transparent overcoat is also applied in select cases. Laser writing on such TEM specimens is carried out using a read/write system incorporating a modulated helium-neon laser. Read/write wavelength is 632.8 nm. A lens with .65 numerical aperture is used and the spot size is 0.8 micron. Prior to TEM examination, data bits written on the TEM specimens are located using an optical microscope. This facilitates subsequent location of the written bits in the TEM. TEM examination is carried out using a Zeiss EM-109 electron microscope operated at 10Q kilovolts. Specimen damage due to electron beam heating effects is not a problem during routine examination. With extremely high electron beam current density, however, in-situ morphological changes in the island-gold films can be initiated; these are helpful in understanding the phenomenology of heating effects in these films. --EX. II: A gold island-film is deposited on a dielectric spacer layer (e.g., as in EX. I, but omitting the reflector layer, using carbon-coated copper grid as "substrate" as above noted). --Results (FIG. 14): FIG. 14 shows the so-deposited virgin (unwritten) island film. Here the reflector layer is not present in order to simplify the examination of the morphology of the as-deposited gold. The result is seen in FIG. 14, a bright field micrograph. The gold film evidently consists of irregularly shaped islands with an areal coverage of approximately 60 percent. Many of the islands are long and narrow in shape, while some others- are roughly circular. Average island spacing is on the order of 100 AO (1 x 10-2 cm). The use of an island metal film as the information layer in the trilayer optical'storage medium is attractive¯¯ for two reasons. First, the discontinuous structure of the film tends to minimize radial thermal losses during the write pulse. Second, long range surface tension forces, characteristic of media in which rim formation predominates, are absent. --"Fissured" contact-face: Here, and elsewhere, it will also be understood that the "contact-face" of the (fluoro-polymer) overcoat (and, possibly, the under layer spacer), facing the (gold) islands, is in some sense "fissured", or covered with channels disposed and dimensioned to allow a great deal of mobility to the "melting-islands" so they may readily "agglomerate". "Non-fissured" contact faces (e.g., of SiO2) presumably inhibit such mobility. --EX. III: EX. II is replicated, except that a full trilayer (with reflector on fluoro-polymer spacer) is produced; also light overcoating of fluoro-polymer (face "fissured") is overlaid on the gold-island absorber. Further, a light SiO2 strike is applied on the spacer to better "nucleate" gold isles. Then a "bit" is laser-recorded at a bit-site on this structure (10 mW, 40 ns pulse from He-Ne laser operated at 632.8 nm). --Results (FIG. 15): FIG. 15, a micrograph of the so-written trilayer medium, with overcoat, demonstrates agglomeration. Here, written data bit is visible in the central portion of the micrograph, while outside the written data bit, the original (virgin) island structure, similar to that shown in FIG. 14, is visible. Note that the presence of the aluminum reflector layer adds an additional degree of complexity to the interpretation of this micrograph. This layer is polycrystalline with random crystal orientation. In the TEM, aluminum crystals suitably oriented for Bragg diffraction (i.e., in contrast) will appear as dark areas, while other crystals, not suitably oriented, will be invisible. In the micrographs shown here, aluminum crystals in the reflector layer which are in contrast" appear as dark areas approximately 0.1 to 0.4 microns in diameter. It will be clear from the FIG. 15 micrograph that the laser "write-event" has caused a marked change in the morphology of the island-gold information layer. The original, irregularly shaped islands have been replaced by a distribution of spherical particles whose "number density" is substantially less than that of the initial island configuration. The sphericity of the particles in the written area implies that melting has occurred-, while the reduced number density of particles indicates that agglomeration or coalescence of molten particles has taken place. It is important to note that the change in reflectance of the trilayer medium associated with this melting and agglomeration process is quite substantial. The original trilayer, with reflectance of 10% at 632.8 nm, increases reflectance after writing, to 50% at the same wavelength. The signal to peak rms noise ratio, typical of written data with the bit morphology of FIG. 15, is 30 dB over a 20 mHz bandwidth. Thus, while there are optical losses associated with the bit morphology shown in FIG. 15, they do not seriously degrade the optical performance of the medium. (Note: absence of a thick, full overcoat here is understood to enhance read-out, but only slightly -- e.g., vs. read-out with full overcoat as with FIG. 2, etc. -- and, vs.un-overcoated state output is degraded by about one-half -- with smaller, less massive virgin isles one may expect to improve sensitivity, readout, etc., as explained below.) --EX. III-A (FIG. 16): EX. III is replicated with bits "written" (same laser energy) along a number of "tracks". Results: appear in FIG. 16 (TEM like FIG. 15, but lower magnification, and showing several "tracks" (aligned written-bits) --running "vertically"; being spread about 1.2 microns apart.) Otherwise, this is essentially as in EX. III. --EX. III-B (FIG. 17): EX. III is, again, replicated; except that "writing" is conducted at much reduced laser energy (up to about 1/10-1/20 that of FIGS. 15, 16 -- more analogous to "threshold power"). ---Results: FIG. 17 indicates the "incipient" (or "threshold") agglomeration implicit in such "under-power" writing (e.g., bit formation presaging that of FIGS. 15, 16). That is, here, it appears that the very low power laser pulse has brought about some change in island shape due to melting, with some spherical particles in evidence, but the agglomeration process has not gone to completion. Increased write-power will presumably give agglomeration more like that of FIGS. 15, 16. --Bit-forming via "agglomeration": The foregoing micrographs (FIGS. 14-17) demonstrate a bit formation process which is essentially one of melting and agglomeration of the island-gold film to form a distribution of spherical debris particles. The final size and arrangement of the debris particles should be functions of the maximum temperature which is reached by# the molten islands, and of the mobility of the islands during the agglomeration phase. As the island-gold film is exposed to the write pulse of the laser, the temperature of the islands rises due to the enhanced absorption inherent to the trilayer structure. At some point in time a melting event occurs which is accompanied by a change in shape of the islands. This shape change, exemplified by the micrograph of FIG. 17, is driven by the increase in "interfacial energy" for the now-molten gold at the spacer and overcoat interfaces. A consequence of the shape change is the initiation of a "detuning" of the optical absorption of the trilayer, which is accompanied by a decrease in the rate of temperature rise. The temperature at which the melting event occurs is thought to be in the range of 3000C. to 6000C., well below the bulk melting temperature of gold. ---"High-Threshold" media (Big globs-high noise): Here, assume Sample EX. IV, same as for FIG. 15 except that nucleation-strike is tin. The minimum laser write power necessary to bring the island-gold to the critical temperature required for melting, with the shape change and trilayer detung which accompany it, may be understood as the "threshold" power for a given medium. For media which have a high threshold power, isIand#temperatures are high prior to the initiation of melting and detuning of the trilayer. An example, EX. IV, of bit formation in such a medium is shown in FIG. 18, which is a TEM micrograph of a trilayer with an island-gold information layer, written with a 10 mW, 40 ns laser pulse. Here, as a consequence of the high temperature attained prior to melting, island mobility has been enhanced and the agglomeration process prolonged. This has resulted in the distribution of extremely large spherical particles visible in the written bit. In this example, there is also a marked tendency for the spherical particles to migrate toward the edge of the written area. This effect is a consequence of the radial thermal gradient imposed by the Gaussian write pulse. The particles thus tend to move down the thermal gradient to the cooler regions at the edge of the bit. From the standpoint of media performance, the bit morphology shown in FIG. 18 is undesirable, as the non-uniform distribution of extremely large debris particles ("Big Globs") reduces peak-to-peak signal-to-noise ratio. (Note: The FIG. 18 sample, or EX. IV, may be understood as essentially the same as that of FIG. 15, except that a tin strike is substituted for the SiO2 strike -- thus, in light of the indicated Massive agglomeration" of FIG. 18, with fewer, larger globs, non-uniformly distributed (by same write-energy), one might characterize a Sn-strike, or nucleating film, as "high threshold-high noise" where the SiO2 strike could be characterized as "low threshold-low noise" for such gold absorbers -- see further below.) Also, where such Massive agglomeration (mobility) is presumably inhibited by the subject "contact-faces" (e.g., channels in fluoro-polymer overcoat evidently don't "freely pass" these), one will assume that other, more-widely-fissured contact faces will inhibit it less (cf. improvement feature). --"Low-Threshold" media (Tiny globs-low noise): Here, assume EX. V (FIG. 19), same as for FIG. 15 except spacer is another modified fluoro-polymer and has no nucleation film thereon. In cases where the threshold is very low, island temperatures at the onset of melting and trilayer detuning are low, and the island agglomeration process is curtailed (poor agglomeration, more globs, very small). An example (EX. V) of bit formation in a medium which exhibits this behavior is shown in FIG. 19. In this island-gold trilayer medium, written with a 10 mw, 40 ns laser pulse, the areal density of debris particles in the data bit is only slightly lower than the areal density of gold islands in the unwritten regions. Thus, while the islands have melted and reverted to tiny spheres, effectively detuning the trilayer, the low temperatures involved have inhibited the island agglomeration process. The resulting data bit is, in fact, rather difficult to see (center of FIG. 19) with the eye. This uniform distribution of very small spherical particles, however, results in a high signal-tonoise ratio, typically exceeding 30 dB. A characteristic of media with low thresholds is increased bit diameter for a given write power, as compared to media with high thresholds. Due to their lower temperature for melting and optical detuning of the trilayer, low threshold media more effectively utilize the outer, lower power regions of the incident Gaussian beam. Thus, EX. V (FIG. 19) may be characterized as "Low Threshold" (low noise), yet still lacking in full complete agglomeration. Of course, more complete agglomeration will yield increased reflectance shift (AR) and thus usually be desired. --Effect of an In-Contact Overcoat: As mentioned earlier, trilayer bit formation mechanisms which involve gross motion, as in rim formation or bubble formation, are inherently incompatibl,e with the presence of a massive, in-contact overcoat. Even in cases where the mechanical properties of the overcoat material are tailored to minimize constraining effects upon the bit formation mechanism, the degradation in performance after overcoating is substantial. In contrast, the bit formation mechanism described above, for island-gold media, does not involve mass transport over long distances. It involves localized rearrangements of the gold islands which do not necessitate large displacements of adjacent surfaces. As the gold islands cover only approximately 60 percent of the available area, ample space exists to accommodate this rearrangement. Of course, there must be limits to the extent to which the agglomeration process can proceed without being affected by a massive overcoat. The bit morphology shown in FIG. 18, for example, involves the formation and motion of very large particles, and cannot proceed unimpeded in the presence of the usual in-contact overcoat. --EX. VI (medium-writing unaffected by overcoat): EX. II is replicated, except that the SiO2 "strike" on the spacer (nucleating strike) is replaced by another, "low-threshold" material, but one fostering better, more complete agglomeration -- and inducing smaller, reducedmass virgin islands; and processed accordingly. Writing is conducted as in EX. II, etc. ---Results (FIGS. 20, 21): In this sample, optimal (virgin) island deposition is achieved as well as optimal bit-formation (agglomeration, with "low threshold"). More particularly, island deposition evidently (see TEM FIG. 20, showing an as-written "bit" -- magnified 2 x in FIG. 21) yields the smallest islands (least mass, smallest diameter) on the average, of all Examples herein. This evidently due (in part, at least) to the superior nucleation-film used. And, as FIG. 20 indicates, this sample yields superior agglomeration and other writing effects (bitformation; e.g., vs. samples of FIG. 15, or FIG. 19, etc., when similarly written-upon). Surprisingly, bit formation (agglomeration) in this sample medium manifests no degradation in the presence of a massive, in-contact overcoat (as shown in FIG. 20) -something astonishing to workers in this art! In this sample, the diameter of the as-deposited (virgin) gold islands is extremely small, averaging approximately 80 AO. The data bit (FIG. 20, center), written with a 10 mW, 40 ns laser pulse, exhibits a highly uniform distribution of spherical debris particles. Incipient melting and agglomeration effects, visible at the edge of the written bit, delineate a "threshold region". FIGURE 21: FIG. 21, a micrograph of another like written data bit in the same medium (and same write-energy, etc.) shows this "threshold region" at higher magnification. Also, here, the associated "contact surfaces" evidently accommodate, or induce, "small-glob" incipient agglomeration (more, smaller globs), typical of a "moderate to low threshold" surface (cf. same fissured fluoro-polymer overcoat as before). --Some conclusions: TABLE A-l Thus, in light of the subject teachings, a worker can, in designing and fabricating an optical disk record for given read-write radiation (energies) -- presumably using an "information layer" (absorber) with anti-reflective background and suitable "fissured-face" overcoat, as above -- optimize sensitivity and bit-formation (etc.) via teachings herein, such as the following: -1. Apply the absorber layer as a very thin, miminum-mass, minimum-size island configuration (e.g., "nucleating-strike" can help too -- one can monitor for "first reflectance minimum" while depositing); -2. if he desires, use a relatively "high-meltingpoint" absorber material (e.g., gold for extended service life); -3. preferably optimize sensitivity by making virgin-isles very small (minimum mass, size) and uniform in size, being uniformly spaced and distributed -- and also he can arrange "contact surface" characteristics (interfacial energy vs. molten isle; with relatively "low threshold" surfaces) to induce the smallest, most uniform (size, distribution) written-globs, and full-agglomeration (at relatively moderate temperature, yet with high moltenisle "mobility" -- interfacial energy being only high enough to assure good spherical agglomeration at moderate energies, yet little higher lest threshold TO be raised unduly and "Massive-glob" agglomeration induced); -3a. substrate characteristics can help optimize this -- e.g., a fluoro-polymer with light nucleating strike of SiO2, MgF2 or the like, to form minimum-mass virgin islands; whereas, surfaces of Cr, Bi, Al, or their oxides, are "non-helpful"; -3b. "fissured-face" overcoat (e.g., fluoropolymer) also helps, as above-explained. --Contact-surface factors (molten islands vs. surface of underlying and/or overlying layer): For adequate island migration (mobility) and "agglomeration", one supposes that the "interface region" between the (top of the) -spacer layer and (underside of the) overcoat -- i.e., where the island-gold information layer resides -- exhibits passages (channels, gaps, etc.) through which molten islands can migrate. How readily this occurs along these passages will be determined by island size and temperature, and by the relative "interfacial energy" (i.e., energy of molten gold in contact with the surrounding host surfaces). Thus, a "non-fissured" overcoat like the well-known SiO2 is undesirable (though SiO2 is desirable as a nucleating "strike" film on the substrate-spacer), whereas a fluoro-polymer is quite apt (cf. "fissured face" discussed). When the gold islands are large (e.g., see FIG. 18) with respect to such passageways (that must accommodate their agglomerating-travel), such migration will presumably be impeded. When the temperature (of melting) is low and trilayer detuning is relatively minimal, migration distances (prior to cooling and solidification) will be short. The magnitude of this "interfacial energy" (of melting gold in contact with surrounding surfaces) is important in two respects. First, it is the increase in interfacial energy, upon melting, which causes the gold islands to assume their spherical shape (they tend to minimize surface area per unit volume). Any increase in surface energy, therefore, represents a barrier to melting and will effectively raise the "threshold temperature" at which trilayer-detuning commencts. Second, the driving force for agglomeration is the decrease in surface energy per unit volume represented by a distribution of "fewer large particles", rather than more small particles. The bit-formation exemplified in FIGS. 20 and 21 represents a more optimal balance of the above considerations. Thus, min-mass (-size) virgin isles (extremely small initial island size) assures the free-est and least-impeded migration; moreover, it can impart an extremely high initial surface area per unit volume, and thereby increase the driving force for agglomeration. Thus, the EX. VI situation will usually be most preferred. A phenomenological Model for the Agglomeration Mechanism: The bit-formation (agglomeration) mechanism here proposed for trilayer media incorporating island-gold as the information layer is believed to consist of two stages: melting, then agglomeration; that is: 1st. Melting of gold islands, accompanied by a shape change (more spherical) and simultaneouç opticaldetuning (here AR) of the trilayer; and 2nd. Subsequent movement and coalescence (agglomeration) of the molten islands to form a distribution of larger globs (spherical debris-particles) in which the optical losses are small. The effective temperature at which melting and trilayer-detuning occur is determined by "interfacial energy differences" between the solid and liquid states (of gold) in contact with the host (spacer, overcoat) surfaces. This effective melting temperature is thought to be well below the bulk melting temperature of gold. The shape change associated with island melting is a consequence of an increase in interfacial energy with the change from solid to molten gold in contact with the host surfaces. Upon melting, the gold islands, irregular in shape as-deposited, revert to tiny spheres, thereby minimizing contact area at the (presumed) high energy interfaces. Workers will understand that optimal agglomeration appears to require that contact-surfaces (substrate, overcoat in contact with the molten islands) during "writing" not only be "fissured", but also exhibit a characteristic "interfacial energy" Eif with the molten isles. Energy Eif may be understood as consonant with a "wetting" or physical affinity (of molten isle to contact-surface#. In cases where the increase in interfacial energy with the change from solid to liquid gold in contact with the surrounding material is large-, an energy barrier to melting exists which causes the effective melting temperature to be high. This situation corresponds to a medium with a high threshold power for writing (and low island-mobility) In cases where the increase in interfacial energy is small, the effective melting temperature is low. This situation corresponds to a medium with a low threshold power for writing. The driving force for agglomeration of the molten gold islands is the decrease in surface energy per unit volume represented by the change from a configuration of many tiny particles to a configuration of few large particles. The mobility of molten islands during the agglomeration phase is a function of their temperature and their size. Small islands utilize available passages at the spacer/overcoat interface more efficiently than large islands,- and are thus more mobile. High temperatures imply a longer migration- lifetime, thus prolonging the time available for agglomeration prior to solidification (cooling, which the de-tuning encourages, of course). ---Some-further conclusions: Thus, for instance, a general teaching hereof is that, in fashioning OD disks with an absorber film in "trilayer c-onfiquration"-- (as described), one can achieve surprisingly good sensitivity by laying-down the absorber material in island form. Beyond that, one is taught that noble metals like gold, palladium, etc. (or their alloys) may be so deposited as the absorber -- e.g., to enhance archival life while securing good sensitivity. --Variations: Workers will appreciate that such "island" films may comprise other metals, or their alloys, in certain cases (e.g., other binary alloys of Au or Pd, ternary alloys, etc., or other metals such as Pt, Cu, Ag, Rh). In the usual instance, the absorber film will be advantageously combined in an "anti-reflection" (or like optical) background array. Such island films may, in certain instances, be otherwise deposited, e.g., by other vapor-deposition techniques (vapor-deposition is very practical where, as in EX. I, etc., it may also be used to deposit other related layers such as the reflector, spacer, etc.). Vapor co-deposition will usually be preferred for "alloys". Other methods may be feasible for depositing the absorber, such as sputtering. In any event, it will usually be preferred to monitor the film during deposition to closely control the deposited island configuration. Also, other recording applications for such absorber films will occur to workers, such as for electron beam or infra-red recording. --Conclusion: It will be understood that the preferred embodiments described herein are only exemplary, and that the invention is capable of many modifications and variations in construction, arrangement and use without departing from the spirit of the invention. Further modifications of the invention are also possible. For example, the means and methods disclosed herein are also applicable to other ultra-thin films adapted to be optically-switched with suitably energized (irradiated or analogously heated). The above examples of possible variations of the present invention are merely illustrative. Accordingly, -t-he present invention is to be considered as including all possible modifications and variations coming within the scope of the invention as defined by the appended claims.

Claims: What is claimed is: 1. An improved heat-sensitive/radiation-sensitive structure, adapted to respond to a prescribed minimum level of heat/radiation-energy, this structure comprising: an "island film" layer comprised of a prescribed absorber material deposited on a substrate in semi continuous "island" form and adapted to be "agglomerated" by said energy modifying said layer to exhibit fewer islands, spaced further apart, doing so without reliance upon ablation, rim-formation, or bubble-formation. 2. The combination of claim 1 arranged as an optical medium for use in an optical data storage system capable of providing a data-modulated focused write-beam of recording radiation on said medium, while providing relative movement therebetween, said beam being datamodulated to present pulses of prescribed write-energy representing data bits, said medium comprising a layer of absorber material deposited in minimum-mass, discontinuous island form on a nucleating-surface of an anti reflective substrate, whereby to be "agglomerated" upon application of said beam pulses at prescribed bit sites thereon whereby. to detectably alter an optical characteristic there during said movement so as to facilitate read-out by prescribed associated optical detect means, the island-layers so formed presenting well-segmented, more-spherical "island-globs" of absorber material having an average width considerably smaller than the width of said beam, doing so without reliance upon gross deformation or translation of absorber mass over a significant portion of a bit-site. 3. The invention in accordance with claim 2, wherein said radiation is from a laser source; wherein said medium comprises a plurality of layers including a reflective layer, a radiation-transparent dielectric spacer layer overlying said reflective layer, and an absorber layer, or layers, in island form overlying said spacer layer, the thicknesses and optical characteristics of said layers and the optically detectable changes of said absorber layer being chosen, in conjunction with the energy-level and wavelength of the associated reading laser such that, during relative movement between the focused reading laser beam and said medium, the reading laser reflects a read-beam from said medium which will vary in accordance with the data so recorded, the intensity of said read beam additionally being chosen so as to not significantly degrade the subsequent readability of the of the so-altered optical characteristic. 4. The invention in accordance with claim 3 wherein a so-altered characteristic is optical reflectance. 5. The invention in accordance with claim 4 wherein the absorber layer is deposited on a lowthreshold/nucleation substrate surface adapted to minimize deposited-island mass and size. 6. The invention in accordance with claim 5 wherein the absorber layer is coated over with a fissuredface protective layer adapted to accommodate, not inhibit, maximal agglomeration. 7. The invention in accordance with claim 6 wherein the absorber island layer is deposited by evaporation from a melt in a vacuum. 8. The invention in accordance with claim 7 wherein the overall thickness of said absorber island layers is the order of a few dozen Angstroms or less. 9. The invention in accordance with claim 8, wherein said spacer layer is selected and arranged to exhibit very low thermal conductivity and is coated with a good nucleating low-threshold strike-film for the said absorber. 10. The invention in accordance with claim 2, wherein the medium is fabricated by providing an antireflection base on which the island layers are deposited, whereby a prescribed minimal reflectance is exhibited by unrecorded portions of the medium. 11. The invention as recited in claim 10, wherein said island layers are deposited only until yielding a prescribed initial minimal reflectance value. 12. The invention as recited in claim 1, wherein the island layers are so vapor deposited while monitoring reflectance thereof. 13. The invention as recited in claim 1, wherein said island layers are deposited on a "low-threshold" nucleation-film adapted to induce minimum-mass/minimumsize island deposition. 14. The invention as recited in claim 13, wherein the original average size, mass and spacing of the islands so rendered is selected and adapted to optimize a lowenergy "agglomeration" whereby to significantly shift reflectance at each so-energized site. 15. The invention as recited in claim 2, wherein the island layers are so formed as to yield such changes upon recording, yet without necessarily involving any significant ablation or expulsion of absorber material from a recorded bit-site. 16. The invention as recited in claim 1, wherein the island layer is covered with a protective defocusing overcoat and is deposited upon a clear thermally-insulative dielectric serving as part of an anti-reflective base; this overcoat exhibiting a "fissured-face" confronting said island layer. 17. An optical medium for use in an optical data storage system capable of providing a data-modulated focused write-beam of recording radiation on said medium; said medium comprising a layer of absorber material deposited in discontinuous island form so as to be in-effect melted and "agglomerated" upon application of said radiation at any "bit site" thereon whereby to detectably alter an optical characteristic there so as to facilitate read-out by prescribed associated optical detect means, the island layer being so formed as to present minimum-mass "islands" of absorber material apt for this agglomeration. 18. The invention as recited in claim 17, wherein the so-agglomerated islands exhibit increased sphericity, size, mass, and optical reflectance. 19. The invention of claim 18 wherein said islands are formed so as to so function even when covered by a defocusing protective overcoat. 20. The invention of claim 19 where the islands are deposited on a dielectric surface having low thermal conductivity and good low-mass nucleating characteristics for the absorber. 21. The invention of claim 20 wherein a plurality of such island layers are so deposited, the first being selected and adapted to enhance low-mass nucleation, being a low-threshold material. 22. The invention of claim 21 wherein the nucleation layer is comprised of an oxide of silicon. 23. An optical recording medium adapted for recording with prescribed radiation and comprising: a substrate having a low-mass nucleation-film and at least one island-layer thereon, said layers being adapted when exposed to the recording radiation to "agglomerate" exhibiting relatively fewer, further-separated, more spherical island masses at a so-recorded bit site.

Inventors: SHEVLIN, CRAIG M.
Applicants: UNISYS CORPORATION
Application year: 1984
Main classification: G11B7
IPC codes: B41M5, G11B7