PROCESS FOR THE QUICK AND CONTROLLED SETTING OF A HYDRAULIC BINDER CONTAINING BOTH PORTLAND CEMENT AND ALUMINA CEMENT, HYDRAULIC BINDER, AS WELL AS A PROCESS FOR THE MANUFACTURE OF BUILDING ELEMENTS

Abstract: The present invention relates to a process for the quick and controlled setting of a hydraulic binder containing both Portland cement and alumina cement. Furthermore the invention relates to a hydraulic binder, optionally in a mixture with an aggregate and/of reinforcing material, for use herein, as well as to a process for the manufacture of building elements using such a hydraulic binder. According to the invention a composition comprising Portland cement and alumina cement in a weight proportion of from 3:1 and 10:1 and an additional amount of a calcium compound of from 0.5 to 5%, by weight, based on the dry weight of Portland cement plus alumina cement, is prepared, water is added to this composition and the slurry obtained is allowed to set. Generally also an aggregate, such as sand, will be added to said binder composition. Preferably fly ash is added too. The use of an acid, in particular citric acid is advan­ tageous.

Description: Process for the quick and controlled setting of a hydraulic binder containing both Portland cement and alumina cement, hydraulic binder, mixture of a hydraulic binder and an aggregate, as well as a process for the manufacture of building elements. The present invention relates to a process for the quick and controlled setting of a hydraulic binder containing both Portland cement and alumina cement. Furthermore the invention relates to a hydraulic binder, optionally in a mix ture with an aggregate and/or reinforcing material, for use herein, as well as to a process for the manufacture of building elements using such a hydraulic binder. Some applications of mixtures of Portland and alumina cement and particularly the problems involved therewith, have been revealed by T.D. Robson in a lecture before the "Road Building Materials Group of the Society" on February 16, 1950. Mixtures of Portland cement and alumina cement provide the advantage of a setting which is quicker than those of the individual cements. Moreover the problems frequently inherent to the quick-set special cements with respect to storage and preservation can be avoided, since the individual cements being per se well storable may be stored separately before being mixed and even the mixtures may be stored for longer time provided that water is strictly excluded. However, it has appeared in practice that the potential applications of such cement mixtures are limited because of the uncontrollability of the processing time, the strength development and the final strength, whereas the final strength is usually lower than those of the individual cements and becomes even lower at later temperature load. Furthermore the setting time being connected with the processing time is strongly dependent on the proportion of both cements in the mixture, for which reason small fluctuations in composition between subsequent cement supplies may cause a retarded or accelerated setting and disturbances. Therefore the use of mixtures of Portland cement and alumina cement is only recommended for a limited number of applications. In the manufacture of building elements, in particular in the continuous manufacture there is, however, a need for binders which bind quicker than each of Portland cement and alumina cement in order to obtain as fast as possible a manageable strength after processing to a mortar, so that the moulded building elements can be removed from the productionline of the continuous manufacture installation for purposes of a final curing. A quicker set results in a shorter residence time of the element in the continuous manufacture installation and so in a higher productivity. Until now spedial cements mixes have been used to this end, wherein the initial strength is determined by formation of sulfo-aluminate. The formation of sulfo-aluminate, however, entails the disadvantage of later changes of length and strength. The invention aims to avoid the disadvantages and problems mentioned above and to provide a binder composition for a mortar which should fulfil the following requirements. A processing time of at least 15 min. should be available for the mortar, whereas after processing the mortar should have already within 6 min. some strength and within 20 min. a manageable strength of about 2 N/mm2 flexural tensile. Furthermore the development of the final strength should proceed without disturbance. Finally the quick setting of the binder composition should be controllable, it means different supplies of the starting materials should not give different results. Accordingly the invention provides a process for the quick and controlled setting of a hydraulic binder containing both Portland cement and alumina cement, characterized in that a composition comprising Portland cement and alumina cement in a weight proportion of from 3:1 and 10:1 and an additional arount of a calcium compound of from 0.5 to 5t, by weight, based on the dry weight of Portland cement plus alumina cement, is prepared, water is added to this composition and the slurry obtained is allowed to set. Generally also an aggregate, such as sand, will be added to said binder composition. The quick-setting mortar prepared by the process of the invention obtains a manageable strength within the short time as a result of an acceleration of the aluminates by the addition of the calcium compound, in particular calcium hydroxide or hydrated lime. Herein the binding strength is optimalized by the indicated amount of the calcium compound. After processing and moulding the mortar it is preferred to have the setting to occur at increased temperatures. Hereby it is rendered possible that the silicates are only hydrated, after the aluminates have been converted into stable end products. If the heat treatment is omittedt may be true that frequently initially higher strengths occur, but then in most cases later a loss of strength follows, which cannot any more be compensated by follow up reaction. Therefore porosity and decrease of the strength are avoided by the heat treatment. Furthermore it is preferred to add fly ash to the binder composition. On the one hand the hydrated lime which is later formed from silicates by hydration, largely is rendered harmless thereby, whereas on the other hand the fly ash contributes to the strength. The reaction with the fly ash results in a reduced porosity, whereby pollution, atmospheric attack and bleeding of lime and iron from the final product are restricted. Furthermore the attack of glass fibers included in the building elements as reinforcement appeared to be provented better. According to another embodiment of the invention the processing time of the mortar is adjusted by the addition of acid. Amounts of acids of from 0.1 to 0.3%, by weight, based on the total dry weight of the hydraulic binder, result in processing times of the mortar, which are desirable for a continuous production-line of building elements. Conveniently the acid is previously dissolved in the water to be added and thus together with the water contacted with the homogeneous dry binder composition. Both inorganic and organic acids may be used, where as polyfunctional carboxylic acids mat be particularly mentioned. As acid preferably citric acid is added. Further according to common practice from 0.1 to 0.5%, by weight, of a flux may be included in the mixture of water and binder composition in order to accelerate the mixing and to avoid an excessive inclusion of air. The mortars preparable by the most preferred process of the invention set quickly and result in a high final strength, for which reason the building elements formed therefrom can be applied in various fields. In case of certain applications, such as for example light fire screening plates, where not so much the strength but rather exclusively the quick setting is important, some of the above indicated preferred measures can be omitted. It appeared that for different supplies of the starting materials a virtually constant behaviour is observed when carrying out the process of the invention, which is very surprising in view of the known variation of the processing time of mixtures of Portland cement and alumina cement in dependence of their origin and composition. In accordance with the above explanation a hydraulic binder to be used according to the invention comprises 75-90%, by weight, preferably 79-84%, by weight, of Portland cement 9-24i, by weight, preferably 14-19%, by weight, of alumina cement and 0.5-5%, by weight, preferably 1.5-2%, by weight, of hydrated lime. Optionally 25-50%, by weight, of fly ash, on base of the dry weight of Portland cement plus alumina cement, may be added hereto. A hydraulic binder according to the invention has in that case as composition 50-70%, by weight, of Portland cement, 7-20%, by weight, of alumina cement, 15-30%, by weight, of fly ash, 0.3-5t, by weight, of hydrated lime. The amount of fly ash may be varied with respect to the amount of Portland cement or alumina cement within a broad range, and so may the absolute percentage of the Portland cement and alumina cement respectively. The mutual proportion between the amounts of Portland cement and alumina cement respective ly in connection with the additional amount of hydrated lime is yet more critical and should be comprised within the earlier indicated ranges. A hydraulic hinder containing fly ash is preferred, which contains 52-62%, by weight, of Portland cement, 12-60%, by weight, of alumina cement, 23-28 by weight, of fly ash and 3-5%, by weight, of hydrated lime. The present invention also relates to mixtures containing besides the said binders an aggregate, such as sand, and/or a reinforcing material, such as glass fibers. The process for the setting of hydraulic binders according to the invention as well as the hydraulic binders according to the invention may be used for the manufacture of building elements, wherein the advantages of the invention are especially manifested, when the manufacture of these building elements is carried out continuously. The continuous manufacture of building elements requires the avoidance of fluctuations in the processing time and the beginning of the early strength in order to prevent disturbances in the production-line. Furthermore the mortar should achieve as fast as possible a manageable strength during the binding. These requirements are fulfilled with the process of the invention. The process for the manufacture of building elements according to the invention will now examplarily be eludicated on the base of the accompanying drawing, wherein the present process is schematically illustrated. In the drawing a sand container 1, a Portland cement container 2, an alumina cement container 3, a fly ash container 4 and a hydrated lime container 5 are represented. Through conducts these containers are connected with a dosing device 6, by which metered amounts of the starting materials are introduced batch-wise in a dry mixture 7. After mixing a batch in the dry mixer 7 the batch is conducted to a storage container 8 and a new batch may be dosed in the dry mixer 7. A second series of containers contains the wet components to be added. Thus a Water container 9, an acid container 10, containing for example a concentrated citric acid solution, and a flux container are through conducts in connection with a dosing device 12, by which metered amounts of these components are introduced in a mixer 13. An aqueous solution prepared in the mixer 13 is thereupon conducted to a storage container 14 which optionally may be provided with a temperature controll device 15 in order to secure a constant temperature of the aqueous solution independent of the ambient temperature. The preparation of the aqueous solution is carried out batch-wise. By means of a dosing device 16 the dry mixture kept in the storage container 8 is introduced in a continuous mixer 18 with a desired rate. Through a dosing device 17 also the storage container 14 containing the solution supply is connected with continuous mixer 18 and thus the suitable amount of water containing the acid and the flux is continuously combined with the dry mixture of hydraulic binders and aggregate under formation of a mortar. Next a glass container 19 contains glass fibers which are fed to a glass cutting device 20 which alfiD functions as dosing device. Through a conduct the cut glass fibers are introduced in an external mixer 21 and mixed therein with the mortar leaving the continuous mixer 18 with constant rate. From the external mixer 21 the mixture of mortar and glass fibers is conducted to a moulding section 22, which may comprise for example closed or open moulds. The formed elements being formed in the moulds are introduced in a setting section 23 and subjected there to a heat treatment. In practice the formed elements are heated to a temperature of 40-600C for 5-20 min. Thus the formed elements obtain a manageable strength and thereupon they may be removed from the moulds and be transported to a curing section 24 for a usual final curing, for example during 24 h at 810cm wet and 14 d at 200C wet. The cured building elements are finally processed to the final product and packed in a section 25.

Claims: CLAIMS 1. A process for the quick and controlled setting of a hydraulic binder containing both Portland cement and alumina cement, characterized in that a composition comprising Portland cement and alumina cement in a wet proportion of 3:1 to 10:1 and an additional amount of a calcium compound of from 0.5 to 5%, by weight, based on the dry weight of Port- land cement plus alumina cement, is prepared, water is added to this composition and the slurry obtained is allowed to set. 2. The process according to claim 1, characterized in that an aggregate is added to the binder. 3. The process according to claim 1 or 2, characterized in that the setting takes place at increased temperature. 4. The process according to claim 3, characterized 0 in that the setting occurs at 40-60 C. 5. The process according to claims 1-4, characterized in that further fly ashes included in the cement composition. 6. The process according to claim 5, characterized in that the fly ash is added in an amount of 25-50%, by weight, based on the dry weight of Portland cement plus alumina cement. 7. The process according to claims 1-6, characterized in that an acid is added to the cement composition. 8. The process according to claim 7, characterized in that citric is added as the acid. 9. The process according to claim 7 or 8, characterized in that the acid is added in an amount of 0.1-0.3%, by weight, based on the total dry weight of the hydraulic binder. 10. The process according to claims 7-9, characterized in that the acid is added together with the water. 11. A hydraulic binder, characterized in that it contains 75-90%, by weight, of Portland cement, 9-24%, by weight, of alumina cement and 0.5-5%, by weight, of hydrated lime. 12. The hydraulic binder according to claim 11, characterized in that it contains 79-84%, by weight, of Portland cement, 14-19%, by weight, of alumina cement and 1.2-28 by weight, of hydrated lime. 13. The hydraulic binder, characterized in that it contains 50-70%, by weight, of Portland cement, 7-20%, by weight, of alumina cement, 15-30%, by weight, of fly ash and 0.3-5%, by weight, of hydrated lime. 14. The hydraulic binder according to claim 13, characterized in that it contains 52-62%, by weight, of Portland cement, 12-16%, by weight, of alumina cement, 23-28%, by weight, of fly ash and 3-5%, by weight, of hydrated lime. 15. The hydraulic binder according to one of the claims 11-14, characterized in that 9.1-0.3%, by weight, on base of the dry weight of the hydraulic binder, of an acid, in particular citric acid, has been added thereto. 16. The mixture of a hydraulic binder according to one of the claims 11-15 and an aggregate. 17 The mixture of a hydraulic binder according to one of the claims 11-15 and a reinforcing material. 18. The mixture of a hydraulic binder according to one of the claims 11-15, an aggregate and a reinforcing material. 19. The mixture according to claim 18, characterized in that the reinforcing material consists of glass fibers. 20. A process for the manufacture of building elements, characterized in that water is added to a hydraulic binder according to one of the claims 11-15 or to a mixture according to one of the claims 16-19, the slurry obtained is subjected to moulding, the moulded elements are set at increased temperature and the set elements are cured in a usual manner. 21. Building elements obtained under application of the process according to claim 20.

Inventors: VELDHOEN, JAN HENDRIK
Applicants: INDUSTRIELE MAATSCHAPPIJ VELDHOEN B.V.
Application year: 1984
Main classification: C04B28
IPC codes: C04B28