MULTIFUNCTIONAL ADDITIVES

Abstract: Synthesized- and mineral-based industrial lubricants are stabilized with a triazole adduct of amine phosphates thereby providing excellent oxidation stability, antiwear and rust preventative performance for said industrial lu­ bricants.

Description: This invention relates to reaction products; more particularly, this invention relates to reaction products which are multifunctional lubricant additives; to compositions and to uses thereof. In particular, this invention is directed to circulating/gear oils having antioxidant, antiwear and rust inhibiting properties. DE-OS 25 30 562 discloses a corrosion preventive for metal surfaces, consisting of a solution of benzotriazole, methylbenzotriazole and/or tetrahydrobenzotriazole in an amine salt of a carboxylic acid, an amine salt of a phosphoric acid, a phosphoric acid trialkyl ester, an aminealkylbenzenesulphonate or mixtures thereof as solvent. It has now been found that certain reaction products of triazole compounds and amine phosphates impart excellent oxidation stability, antiwear and rust preventive performance to lubricant compositions to which they are added. They are particularly effective with respect to both synthesized and mineral based industrial lubricants. In accordance with the present invention, there is provided a reaction product of a triazole with an amine phosphate obtained by reacting the triazole and the amine phosphate in a mole ratio from 1:3 to 3:1 at a temperature from 80°C to 125°C, with 98°C to 100°C being preferred. The triazole compound used to form the reaction product of the present invention preferably has the following formula: wherein: R represents a hydrogen atom or a lower alkyl group, such as C₁ to about C₆. R preferably represents a methyl group. However, other triazoles would also be expected to be useful in providing similar reaction products. The aromatic amine phosphate which may be utilized in preparing the reaction product of the present invention preferably has the following formula: wherein: x + y = 3; and AR represents a hydrocarbyl group, preferably an aromatic group such as aryl and alkaryl. In general, the reactants are contacted for 1 to 8 hours with from 2 to 4 hours being preferred. The reaction is usually carried out at ambient pressures, however, higher pressures may be used if desired. As those of skill in the art are aware, the particular reaction parameters utilized depend upon the temperature and pressure selected and the specific reactants employed. Thus, at higher temperatures and pressures the reaction time may be shorter than the time at lower temperatures and pressures for a given pair of reactants. The reaction may proceed with or without the presence of a catalyst. However, a catalyst of an acidic nature, such as acetic acid, propionic acid, toluenesulfonic acid, phosphoric or polyphosphoric and methanesulfonic acids may be effectively employed. Basic catalysts may also be used. Typical examples include sodium or potassium alkoxides and sodium or potassium metal or hydroxides. This invention also provides a lubricant composition comprising a major amount of an oil of lubricating viscosity or a grease prepared therefrom and a minor amount of a reaction product as herein defined. Of particular significance in the present invention is the ability of the reaction product to improve resistance to oxidation and provide improved anticorrosion characteristics to oleaginous materials such as lubricating media which may comprise liquid oils in the form of either a mineral or a synthetic oil of lubricating viscosity or in the form of a grease in which the aforementioned oils may be employed as a vehicle. In general, mineral oil of both paraffinic, naphthenic amd mixtures thereof when employed as a lubricant or grease vehicle may be of any suitable lubricating viscosity range. For example, about 45 SSU at 37.8°C to about 6000 SSU at 37.8°C and preferably from 50 about 250 SSU at 93.4°C. These oils may have viscosity indexes ranging to about 100 or higher. Viscosity indexes from 70 to 95 are preferred. The average molecular weights of these oils may range from 250 to 800. Accordingly, this invention also includes the use of a reaction product as herein defined as an oxidation stabiliser in a lubricant composition, an antiwear additive in a lubricant composition or a rust preventative in a lubricant composition. Where the lubricant is to be employed in the form of a grease, the lubricating oil is generally employed in an amount sufficient to balance the total grease composition, after accounting for the desired quantity of the thickening agent, and other additive components to be included in the grease formulation. A wide variety of materials may be employed as thickening or gelling agents. These may include any of the conventional metal salts or soaps, which are dispersed in the lubricating vehicle in grease-forming quantities in such degree as to impart to the resulting grease composition the desired consistency. Other thickening agents that may be employed in the grease formulation may comprise the non-soap thickeners, such as surface modified clays and silicas, aryl ureas, calcium complexes and similar materials. In general, grease thickeners are employed which do not melt and dissolve when used at the required temperature within a particular environment; however, in all other respects, any material which is normally employed for thickening or gelling hydrocarbon fluids for forming grease can be used in preparing the improved greases in accordance with the present invention. In instances where synthetic oils, or synthetic oils employed as the vehicle for the grease, are desired in preference to mineral oils, or in combination therewith, various compounds of this type may be successfully utilized. Typical synthetic vehicles include polyisobutylene, polybutenes, hydrogenated polydecenes, polypropylene glycol, polyethylene glycol, trimethylol propane esters, neopentyl and pentaerythritol esters, di(2-ethylhexyl) sebacate, di(2-ethylhexyl) adipate, dibutyl phthalate, fluorocarbons, silicate esters, silanes, esters of phosphorus-containing acids, liquid ureas, ferrocene derivatives, hydrogenated mineral oils, chain-type polyphenyls, siloxanes and silicones (polysiloxanes), alkyl-substituted diphenyl ethers typified by a butyl-substituted bis (p-phenoxy phenyl) ether, phenoxy phenylethers. It is to be understood, however, that the compositions contemplated herein can also contain other materials. For example, corrosion inhibitors, extreme pressure agents, viscosity index improvers, co-antioxidants, antiwear agents can be used. These materials do not detract from the value of the compositions of this invention, rather these materials serve to impart their customary properties to the particular compositions into which they are incorporated. Mineral oil heat exchange fluids particularly contemplated in accordance with the present invention have the following characteristics: high thermal stability, high initial boiling point, low viscosity, high heat-carrying ability and low corrosion tendency. In addition, the oxidation and corrosion resistance of functional fluids such as hydraulic fluids and circulating/gear oils can be significantly improved by the adducts of the present invention. The reaction product of the present invention may he employed in any amount which is effective for imparting the desired degree of oxidation improvement, or antiwear improvement or corrosion prevention in accordance with the invention. In many applications the reaction product is effectively employed in amounts from 0.01 to 10% by weight, and preferably from 0.1 to 1.0% of the total weight of the composition. The following example and comparative data will serve to illustrate the reaction product of the present invention, and the marked improvement in antioxidant, antitrust and antiwear properties of oleaginous materials containing said adducts. EXAMPLE Reaction Product of Tolyl Triazole and Aromatic Amine Phosphate A mixture of 100 grams of tolyl triazole and 300 grams of aromatic amine phosphate salt obtained commercially (Ciba-Geigy Irgalube 349) was gradually heated to a temperature of 95°C with stirring. After the mixture had been stirred at that temperature for a period of two hours, the resulting product became quite clear and the reaction was immediately discontinued. The reaction product was cooled to room temperature with continuous stirring. The final product was clear and very viscous at room temperature. The same method was used with mixtures of tolyl triazole or benzotriazole and other amine phosphate salts. These mixtures yielded similar reaction products. When the weight ratio between tolyl triazole and amine phosphate salts was varied, the viscosity of the final reaction product varied under identical methods of preparation. Three different blends or reference oils were used in evaluating the reaction product of the present invention. Their respective compositions are disclosed in Table 1. The oxidation stability, antiwear and rust preventitive properties of synthetic circulating/gear oils were determined and the data set fourth in Table 2. The following blends of synthetic base oil A were then compared: a blend containing (alkyl) dinonyl phenyl phosphonate (Sample A); a blend containing the aromatic amine phosphonates (Sample B) and a blend (Sample C) containing the aromatic amine phosphate - tolyl triazole reaction product in accordance with the invention (Example). Each of the blends contained equal amounts of the designated additive. The base oil contained no additional additives other than as set forth in Table 1. Rotary Bomb Oxidation Test (RBOT) - ASTM D-2272 The test oil, water, and copper catalyst coil, contained in a covered glass container, are placed in a bomb equipped with a pressure gage. The bomb is charged with oxygen to a pressure of 721.9 kPa (90 psi), placed in a constant temperature oil bath set at 150°C, and rotated axially at 100 rpm at an angle of 30 deg from the horizontal. The time for the test oil to react with a given volume of oxygen is measured, completion of the time being indicated by a specific drop in pressure. Rust Test - ASTM D-665 This method involves stirring a mixture of 300 ml. of the oil under test with 30 ml. of distilled or synthetic sea water, as required, at a temperature of 60°C with a cylindrical steel specimen completely immersed therein. It is customary to run the test for 24 hours; however, the test period may, at the discretion of the contracting parties, be for a shorter or longer period. Here the test was run for 24 hours using synthetic sea water at 60°C. Catalytic Oxidation Test The reaction products were blended into the respective base oils. The oils were then subjected to a stream of air at the rate of 5 liters per hour at a temperature of 163°C (325°C). for 40 hours in the presence of metals having pro-oxidant properties: iron, copper, lead and aluminum. The lead sample has weighed before and after the test, since lead is one of the metals more susceptible to corrosion by oxidation. The test measurements are: change in acidity or neutralization number as measured by ASTM D-974, change in kinematic viscosity at 98.9°C (210°F), lead loss in milligrams and sludge. Results of the tests are presented in Table 2 and Table 3. The effectiveness of reaction products in accordance with the invention were also evaluated as antiwear/extreme pressure additives using the Standard Four-Ball Wear Test and the Timken Load Test. Synthetic Reference Oil B was used for this evaluation. One example, sample g, contained a standard additive package only which consisted of sulfurized isobutylene, silicone defoament, and BASF Wyandotte's Pluronic polyols. The second Example, sample h, contained the standard additive package plus Example 1 in accordance with the present invention. The effectiveness of Example 1 as an antiwear and EP additive is demonstrated by the data set forth in Table 4. The Standard Four-Ball Wear Test is disclosed in U.S. Patent No. 3,423,3l6. In general, in this test three steel balls of 52-100 steel are held in a ball cup. A fourth ball positioned on a rotatable vertical axis is brought into contact with the three balls and is rotated against them. The force with which the fourth ball is held against the three stationary balls may be varied according to a desired load. The test lubricant is added to the ball cup and acts as a lubricant for the rotation. At the end of the test, the steel balls are investigated for wear-scar; the extent of scarring represents the effectiveness of the lubricant as an antiwear agent (Table 2). The Timken Load Test-ASTM D2782 may be summarized as follows: It determines the load carrying capacity of lubricating fluids by means of the Timken extreme pressure tester. The tester is operated with a steel test cup rotating against a steel test block. The rotating speed is 800± 5 rpm. Fluid samples are preheated to 37.8± 2.8°C before starting the test. Timken OK load is the maxiimum load value at which the rotating cup will not rupture the lubricant film and cause scoring or seisure between the rorating cup and the stationary block. It is apparent from the data of Tables 2, 3 and 4 that the reaction products of the present invention are markedly effective not only as oxidation stabilizers but also as antiwear and rust preventative additives in both mineral and synthetic oils.

Claims: A reaction product of a triazole with an amine phosphate obtainable by reacting the triazole and the amine phosphate in a mole ratio from 1:3 to 3:1 at a temperature from 80°C to 125°C. A reaction product according to claim 1 wherein the triazole has the following formula: wherein: R represents a hydrogen atom or a lower alkyl group; and the amine phosphate has the following formula: wherein: x + y = 3 ; and AR represents an aromatic group. A reaction product according to claim 1 or 2 wherein the triazole comprises tolyl triazole. A reaction product according to claim 1 or 2 wherein the triazole comprises benzotriazole. A reaction product according to any preceding claim wherein the amine phosphate comprises an aromatic amine phosphate. A lubricant composition comprising a major amount of an oil of lubricating viscosity or a grease prepared therefrom and a minor amount of a reaction product defined in any preceding claim. A lubricant composition defined in claim 6 wherein the reaction product is present in an amount from 0.001 to 10 percent weight. A lubricant composition defined in claim 7 wherein the reaction product is present in an amount from 0.1 to 1.0 percent by weight. A lubricant composition according to any of claims 6 to 8 wherein the oil of lubricating viscosity is a mineral oil or a fraction thereof, a synthetic oil or a mixture of a mineral and a synthetic oil. A lubricant composition according to claim 9 wherein the lubricating oil is circulating/gear oil. Use of a reaction product defined in any of claims 1 to 5 as an oxidation stabiliser in a lubricant composition. Use of a reaction product defined in any of claims 1 to 5 as an antiwear additive in a lubricant composition. Use of a reaction product defined in any of claims 1 to 5 as a rust preventative in a lubricant composition. CLAIMS FOR AUSTRIA: A method of preparing a reaction product of a triazole and an amine phosphate, comprising reacting the triazole and the amine phosphate in a mole ratio from 1:3 to 3:1 at a temperature from 80°C to 125°C. A method according to claim 1, comprising using a triazole having the following formula: wherein: R is a hydrogenation or lower alkyl and the amine phosphate has the generalized formula wherein: x+y=3 and AR = aromatic. A method according to claim 1 or 2 comprising using tolyl triazole as the triazole. A method according to claim 1 or 2 comprising benzotriazole as the triazole. A method according to any preceding claim comprising using an aromatic amine phosphate as the amine phosphate. A method of preparing a lubricant composition comprising combining a major amount of an oil lubricating viscosity or a grease prepared therefrom with a minor amount of a reaction product prepared according to the method of any preceding claim. A method according to claim 6 wherein the reaction product is present in an amount from 0.001 to 10 percent A method according to claim 7 wherein the reaction product is present in an amount from 0.1 to 1.0 percent by weight. A method according to any of claims 6 to 8 wherein the oil of lubricating viscosity is a mineral oil or a fraction thereof, a synthetic oil or a mixture of a mineral and a synthetic oil. A method according to claim 9 wherein the lubricating oil is circulating/gear oil. Use of a reaction product prepared according to the method defined in any of claim 1 to 5 as an oxidation stabiliser in a lubricant composition. Use of a reaction product prepared according to the method defined in any of claims 1 to 5 as an antiwear additive in a lubricant composition. Use of a reaction product prepared according to the method defined in any of claims 1 to 5 as a rust preventative in a lubricant composition.

Inventors: SHIM, JOOSUP
Applicants: MOBIL OIL CORPORATION
Application year: 1984
Main classification: C10M133
IPC codes: C10M133, C10N30, C10N50, C10M159, C07D249, C10N40