WATER-DILUTABLE WOOD-PRESERVING LIQUIDS

Abstract: A water-dilutable wood-preserving liquid containing from 10% w/w to 80% w/w of a suitable solvent, from 20% w/w to 80% w/w of a suitable solubilizer and from 0.01% w/w to 10% w/w of an azole of formula or an acid-addition salt thereof.

Description: WATER-DILUTABLE WOOD-PRESERVING LIQUIDS. The present invention is concerned with organic wood-preserving liquids which are dilutable with predominantly aqueous mediums. Since it is desirable to preserve wood from decay caused by microorganisms several compounds having antimicrobial properties have been described as useful wood-preserving agents. As wood is considered, for example, wood products such as timber, lumber, railway sleepers, telephone poles, fences, wood coverings, wicker-work, plywood, particle board, waferboards, clipboard, joinery, bridges or wood products which are generally used in housebuilding. Wood which is preserved from staining and decay is meant to be protected from moulding, rotting, loss of their useful mechanical properties such as breaking strenght, resistance to shock and shearing strenght, or decrease of their optical or other useful properties such as the occurrence of odor, staining, spot formation and dote caused by the following microorganisms: Aspergillus species, Penicillium species, Aureobasidium pullulans, Sclerophoma pityophilla, Verticillium species, Alternaria species, Rhizopus species1 Mucor species, Paecilomyces species, Saccharomyces species, Trichoderma viride, Chaetomium globosum, Stachybotrys atra, Myrothecium verrucaria, Oospora lactis and other staining and wood decay fungi. special emphasis should be led on the good activity against moulds and staining fungi such as Aspergillus niger, Penicillium funiculosum, Trichoderma viride, Alternaria alternata, decay and softrot fungi such as Chaetomium globosum, Trychophyton mentagrophytes, Coriolus versicolor, Coniophora cerebella, Poria monticola, Merulius (Serpula) lacrymans and Lenzites trabea, and yeasts such as Candida albicans and Saccharomyces species. In order to protect wood from decay it is treated with formulations containing one or more wood-preserving agents. Such treatment is applied by several different procedures such as, for example1 by treating the wood in closed pressure- or vacuum systems1 in thermal- or dip systems and the like, or by a wide variety of exterior wood-structure treatments, e.g. by brushing, dipping, spraying or soaking the wood with the formulation containing the wood-preserving agent. Whereas anorganic compounds were used as wood-preserving agents the more recently preferred agents are organic compounds. such as, for example, the azoles described in european Patent No. 38,109. Due to their organic nature these compounds have rather lipophilic properties, resulting in a good solubility in organic mediums and an often inadequate solubility in aqueous mediums. Consequently these organic agents are usually incorporated in organic formulations for applying them to the wood. However, these organic formulations have some less advantageous properties such as, for example, their expense combined with disadvantageous influences on the environment and the safety and health of the applicator. Therefore a number of organic liquids which form emulsions or dispersions with aqueous mediums have recently been developed, such as the organic liquids described in U.S. Patent No. 4.357,163. However these emulsions or dispersions, formed after mixing the organic liquid with the aqueous medium. are known to be too liable to a number of factors, such as, for example1 changes of temperature, pH of the mixture and/or hardness of the water used, the presence of impurities in the wood and the like, resulting in an often inadequate physical stability. Additionally, because a rather invariable concentration of the active agent in the formulation is required to assure a continuous process in closed pressure- or vacuum systems or in thermal- or dip techniques, lack of uniform uptake of the suspension or dispersion by the wood negatively influences the applicability of said suspensions or dispersions in such techniques. Such lack of uniform uptake causes a decreasing or increasing concentration of the active agent in the remaining formulation, which may finally result in a dilution of the formulation respectively a precipitation of the wood-preserving agent. The present invention is concerned with organic wood-preserving liquids which are dilutable with predominantly aqueous mediums, said liquids containing: i) from 10% to 80% of a suitable solvent; ii) from 20% to 80% of a suitable solubilizer: and iii) from 0.01% to 10% of at least one azole having the formula EMI3.1 or an acid addition salt thereof, wherein X is nitrogen or a CH group and R1 is a radical of the formula EMI3.2 wherein CH2 a group -CH2-CH2-, -CH2-CH2-CH2-, -cH(CH3)-CH(CH3)- or -CH2-CH(alkyl)-, wherein said alkyl is a straight or branched 2 C1-C10 alkyl radical; said Ar is a phenyl group which is optionally substituted with 1 to 3 halogens, C -C alkyl radicals, C1-r alkoxy radicals, cyano-. trifluoromethyl- or nitro groups, a thienyl-. halothienyl-, naphthalenyl- or fluorenyl group; and, said R is Cl-Cl0 alkyl, cycloalkyl. cycloalkyllower alkyl. lower alkenyl, aryllower alkyl1 aryloxylower alkyl or a radical of the formula ¯O¯Ro, , wherein said R0 is C1-C10 alkyl, lower alkenyl, lower alkynyl or aryllower alkyl, wherein said aryl radical is phenyl1 naphthalenyl or substituted phenyl, wherein said substituted phenyl has 1 to 3 substituents selected from the group consisting of halo, cyano, nitro, phenyl, lower alkyl and lower alkoxy, provided that when more than one substituent is present only one thereof may be cyano, nitro or phenyl. The said wood-preserving liquids have the advantage that almost instantaneously homogeneous solutions are formed by mixing these liquids with predominantly aqueous mediums. Furthermore, these solutions have an extremely high physical stability, not only at ambient temperature, i.e. at temperatures comprised between 150C and 350C, but also at decreased temperatures. Even after several cycles of crystallization of the aqueous solution below OOC and subsequent storage at ambient temperature the physical stability is not negatively influenced. The homogeneous solutions combine also a good moistening of the wood-surface with a high degree of penetration of the said solutions in the wood, resulting in an unexpectedly high uptake of the solution by the wood, and, consequently, a desired preservation of the treated wood. Additionally, due to a uniform uptake of the aqueous solution the wood-preserving liquids and the resulting aqueous solutions are particularly useful in treatment techniques which require the possibility of a continuous process, such as, for example. impregnation- or dip techniques. Besides the previously cited advantages the subject compositions have also the advantage that the same protection of the treated wood is obtained at lower amounts of active ingredient taken up by the wood when aqueous solutions are used than when solvent-based mixtures are used. In addition the solutions formed with the wood-preserving liquids combine the hereinabove mentioned advantages with those which are characteristic to predominantly aqueous mediums, such as, for example. a relatively high flashpoint, reduced toxicity resulting in advantageous influences on the environment and the health and safety of the applicator, lack of irritation and the like. Particularly interesting liquids in accordance with the present invention are those containing an agent of formula EMI5.1 wherein X has the above-identified meaning and R1' is a radical of the formula EMI5.2 wherein Z' is a group -CH2-CH2-, -CH2-CH2-CH2-, -CH(CH3)-CH2-. -CH(C2H5)-CH2-. -CH(C3H7)-CH2-, -cH(CH3)-CH(CH3)- or -CH(CH3)-CH(C2H5)-; Ar' is unsubstituted phenyl or phenyl substituted with 1 to 3 halogen atoms, preferably chloro atoms, C1-C6 alkyl radicals, C -C alkoxy radicals, cyano or nitro groups: and R' is C1-C6 alkyl or C3-C4 alkenyloxy. More particularly interesting liquids in accordance with the present invention are those containing an agent of formula EMI5.3 wherein X has the above-identified meaning and R1" is a radical of the formula EMI5.4 wherein R" is C1-C4 alkyl, C3-C4 lower alkenyloxy, R3 is hydrogen or C1-C3 alkyl and n is 1 or 2. Preferred liquids in accordance with the present invention are those containing 1-[2-(2,4-dichlorphenyl)-1,3-dioxolan-2-ylmethyl]1H-1,2,4-triazole, generically designated as azaconazole, or a suitable acid addition salt thereof. As it is required that the wood-preserving liquid forms a homogeneous solution with a predominantly aqueous medium the solubilizer must sufficiently solubilize the active agent and the solvent of the liquid in the aqueous medium and may not negatively influence the solubility of the active agent in the solvent. Preferred solubilizers are selected from the group consisting of: i) addition products of 1 to 60 moles of ethylene oxide with 1 mole of a phenol which is further substituted with at least one C1-C15 alkyl group: and ii) addition products of 1 to 60 moles of ethylene oxide with 1 mole of ricinus oil. The most preferred solubilizers are selected from the group consisting of: i) addition products of 1 to 60 moles of ethylene oxide with 1 mole of nonylphenol or octylphenol; and ii) addition products of 1 to 60 moles of ethylene oxide with 1 mole of ricinus oil. The organic solvent of the liquid must fulfill the requirements of sufficiently solubilizing the active ingredient and, combined with the solubilizer, being homogeneously miscible with a predominantly aqueous medium. Preferred solvents are 2-butoxyethanol and butyl 2-hydroxyacetic acid ester. In the formulations of the present invention the azoles of formula (I) can also be used in combination with other compounds having a useful activity such as, biocidal compounds, e.g. antimicrobial agents, insecticides and the like. As antimicrobial agents, which may be used in combination with the azoles of formula (I) there may be considered products of the following classes: Phenol derivatives such as 3,5-dichlorophenol, 2,5-dichlorophenol, 3,5-dibromophenol, 2, 5-dibromophenol, 2,5-(resp. 3,5)-dichloro-4bromophenol, 3,4, 5-trichlorophenol, chlorinated hydrodiphenylethers such as, for example, 2-hydroxy-3,2'4'-trichlorodiphenylether, phenylphenol, 4-chloro-2-phenylphenol, 4-chloro-2-benzylphenol, dichlorophene, hexachlorophene: aldehydes such as formaldehyde, glutaraldehyde, salicylaldehyde; alcohols such as phenoxyethanol; antimicrobially active carboxylic acids and their derivatives: organometallic compounds such as tributyltin compounds; iodine compounds such as iodophores, iodonium compounds; mono-, di- and polyamines such as dodecylamine or l1l0-di(n-heptyl)-l1lO-diamino- decane: quaternary ammonium compounds such as benzyl-dimethyldodecylammonium chloride, dimethyldodecylammonium chloride, benzyl-di(2hydroxyethyl)dodecylammonium chloride: sulfonium- and phosphonium compounds; mercapto compounds as well as their alkali, earth alkaline and heavy metal salts such as 2-mercaptopyridine-N-oxide and its sodium and zinc salt, 3-mercaptopyridazin-2-oxide, 2-mercaptoquinoxaline-l-oxide, 2-mercaptoquinoxaline-di-N-oxide, as well as the symmetrical disulfides of said mercapto compounds: ureas such as tribromo- or trichlorocarbanilide, dichloro-trifluoromethyldiphenylurea; tribromosalicylanilide: 2-bromo-2-nitro-1,3-dihydroxypropane; dichlorobenzoxazolon: chlorohexidine; isothia- and benzisothiazolone derivatives. As insecticidal agents which may be used in combination with the azoles of formula (I) the following classes of products may be considered: insecticides having a natural origin, e.g., nicotine, rotenone, pyrethrum and the like; chloridinated hydrocarbons, e.g., lindane, chlordane, endosulfan and the like; organic phosphor compounds, e.g., diazinon, parathion, dichloorvos, dimethoate and the like; carbamates, e.g., carbaryl, aldicarb, methiocarb, propoxur and the like; biological insecticides, e.g., products originating from Bacillus thuringiensis: synthetic pyrethroids, e.g., permethrin, allethrin, cypermethrin, halothrin and the like. Furthermore, the formulations of the subject invention may also contain additives which may improve their applicability, the chemical and/or physical stability and the like properties of the said formulations. Examples of such additives are naturally occuring and synthetic resins, e.g. wood resin, alkyd resin, polyurethane resin and the like, drying oils, e.g. linseed oils, oiticica oil, fish oil, standoil and the like, siccatives, e.g. naphthenoates and the like, stabilization products, e.g. W absorbers. anti-oxydants and the like, pigments, waxes with high softening points and the like. EXPERIMENTAL PART. The following examples are intended to illustrate and not to limit the scope of the present invention. Unless otherwise stated all parts therein are by weight. In the following examples Cemulson NP 8 is a Trade Mark of a mixture of addition products of nonylphenols with ethylene oxide, wherein an average of 8 mole of ethylene oxide has been reacted with 1 mole of nonylphenol and Soprophor BO is a Trade Mark of a mixture of addition products of ricinus oil with ethylene oxide. Octylphenol 8.5 is a mixture of addition products of octylphenols with ethylene oxide, wherein an average of 8.5 moles of ethylene oxide has been reacted with 1 mole of octylphenol. A. PreParation of organic concentrates: example I formulation 1: 3.3% w/w of azaconazole 1.8% w/w of lindane 50% w/w of 2-butoxyethanol; and Cemulsol NP 8 ad 100%. preparation: 3.3 Parts of azaconazole and 1.8 parts of lindane were added portionwise to 50 parts of 2-butoxyethanol at 500C. After complete solubilization the mixture was cooled to 250C and 44.9 parts of Cemulsol NP 89 were added. ExamPle II Following the preparation-procedure described in Example I the following formulations were prepared: formulation 2: 5% w/w of azaconazole 50% w/w of 2-butoxyethanol; and Cemulsol NP 8 ad 1008. formulation 3: 1.8% w/w of azaconazole 3% w/w of lindane 56% w/w of Soprophor B0; and butyl 2-hydroxyacetic acid ester ad 100 ml. formulation 4: 5.0% w/w of azaconazole 10% w/w of permethrin 20% w/w of butyl 2-hydroxyacetic acid ester; and 63.8% w/w of Soprophor B: formulation 5: 5.08 w/w of azaconazole 10% w/w of carbosulfan 20% w/w of butyl 2-hydroxyacetic acid ester and 63.8% w/w of Cemulsol Np 80. formulation 6: 5.0% w/w of azaconazole 56% w/w Soprophor B; butyl 2-hydroxyacetic acid ad 100ml. formulation 7: 5.7% w/w of azaconazole 48.0% w/w of butyl 2-hydroxyacetic acid ester; 44.3% w/w of Soprophor B0; and 2% w/w of colophonium resin. formulation 8: 5.7% w/w of azaconazole 48.0% w/w of butyl 2-hydroxyacetic acid ester; 44.3% w/w of Soprophor B0; and 2% w/w of petroleum resin. formulation 9: 5.78 w/w of azaconazole 48.0% w/w of butyl 2-hydroxyacetic acid ester; 44.3% w/w of Soprophor B0; and 2% w/w of alkyd resin 50W. formulation 10: 5.7% w/w of azaconazole 45.0% w/w of butyl 2-hydroxyacetic acid ester; 44.3% w/w of Soprophor B#; and 5.0% w/w of alkyd resin 50W. formulation 11: 5.7% w/w of azaconazole 40.0% w/w of butyl 2-hydroxyacetic acid ester: 44.3% w/w of Soprophor B0; and 10.0% w/w of alkyd resin 50W. formulation 12: 5.0% w/w of azaconazole 1.2% w/w of acetic acid: 40.0% w/w of butyl 2-hydroxyacetic acid ester; 44.3% w/w of Soprophor B0: and 8.8% w/w of alkyd resin SOW. formulation 13: 5% w/w of etaconazole (1-tt2-(2,4-dichloro- phenyl)-4-ethyl-1,3-dioxolan-2-yl]methyl]-1H 1,2,4-triazole) 50% w/w of butoxyethanol: and 45% w/w of Cemulsol NP 80. formulation 14: 10% w/w of etaconazole 20% w/w of octylphenyl 8.5: 2% w/w of acetic acid: 10% w/w of Polysolvan 0.; and 58% w/w of Cemulsol NP 8#. formulation 15: 5% w/w of etaconazole 56% w/w of Soprophor B0;and 39% w/w of Polysolvan 0#. formulation 16: 5.0% w/w of propiconazole (1-tt2-(2,4-dichloro- phenyl)-4-propyl-1,3-dioxolan-2-yl]methyl]-1H 1,2,4-triazole) 40.7% w/w of butyl 2-hydroxyacetic acid ester: 44.38 w/w of Soprophor 8 : and 109 w/w of alkyd resin SOW. B. Physical stabilitY of the formulations: Example III 100 Parts of formulation 1 was stored during 24 hours at 200C and, subsequently, during 24 hours at -7.50C. The said storage-cycle was repeated during 14 days. Although some of the formulations crystallized during the storage period at -7.50C the mixture always completely homogenized during storage at 200C without the precipitation of any crystals. ExamPle IV Following the procedure described in Example III the formulations 2 - 16 were also stored during 14 days at 200C and at -7.50C. The mixtures completely homogenized during the storage-period at 200C without the precipitation of any crystals. ExamPle V Aqueous solutions prepared by diluting the formulations 1-16 with distilled water to a final concentration of 100 - 10.000ppm of the active ingredient were stored during 24 hours at 200C and, subsequently, during 24 hours at -7.50C. The storage-cycle was repeated during 14 days. Although most of the aqueous solutions crystallized or became heterogeneous during the storage period at -7.50C the solutions homogenized or were easy homogenizable during the storage period at 200C. C. Uptake bY the wood. ExamPle VI Wood Beech wood blocks of 2 cm x 2 cm x 2 cm were stored until needed in desiccators containing saturated solutions of sodium bichromate, assuring a relative humidity of 52% at room temperature Active ingredient formulations The organic solvent type preservative contained 10 g of azaconazole per litre of a solution consisting of white spirit, plastifying co-solvents and resins. The waterborne type preservatives were prepared as described hereinabove. Radiolabelled active ingredient Azaconazole, specifically 14C-labelled at the 2-ethyl carbon, EMI12.1 showed a specific activity of 2.22 Ci/mg. Stock solutions containing 2.5 mg 14C-azaconazole per 25 ml distilled water or 1.25 mg 14C-azaconazole per 20 ml white spirit were prepared. Treatment solutions Since an equal treatment solution strength of 3 g azaconazole per litre was choosen to compare the respective preservative types, the active ingredient formulations were diluted with the appropriate solvents. At the same time radiolabelled active ingredient was spiked in order to facilitate analytical procedures. The composition of the treatment solutions containing azaconazole is given in table 1. Blank treatment solutions were prepared from the blank formulations using identical dilution ratios. Table 1 : The composition of the treatment solutions, containing azaconazole as active ingredient, used for dip treatment and impregnation treatment of beech wood blocks. Initial active ingredient concentration of 3000 ppm. Room temperature. stock stock White liquid solution solution H2O Spirit Xylene A B ad ad ad formulation 2 15 g 12.5 ml - 250 ml - formulation 6 15 g 12.5 ml - 250 ml - Oil based - I 75 ml - 25 ml - 250 ml Oil based - II 75 ml - 25 ml - - 250 ml Oil based - III 75 ml - 25 ml - - 250 ml Stock solution A : 100 g 14C-azaconazole/ml distilled water Stock solution B : 50 g 14C-azaconazole/ml white spirit formulation of the oil based - I and oil based - II liquids 10 g azaconazole 50 g colophonium resin 50 g dibutyl phthalate 100 ml Polysolvan 0. white spirit ad 1000 ml. formulation of the oil based - III liquid 10 g azaconazole 50 g dibutyl phthalate 100 ml Polysolvan 0. white spirit ad 1000 ml. Methods A. DiP treatment The humidity conditioned wood blocks were placed individually in pre-weighed and labelled 50-ml glass beakers, and their weight was recorded. Five blocks were dried at 1200C during 24 hours to assess the 52% relative humidity moisture content. Three cubes were provided for each preservative type-time combination; for each preservativetime combination one cube for blank treatment was included. The blocks were removed from their beakers, while 15-ml portions of the selected treatment solution were added to each beaker. The initial weight of the treatment solution was recorded. The blocks were dipped in the solutions and retained completely immersed by imposing the tip of a Pasteur pipette, fixed into a rack-mounted clamp. Beakers containing organic solvent type preservative were covered with Parafilm to reduce evaporation losses. After the selected contact time intervals, i.e. after 1 hour, 4 hours or 24 hours, the blocks were removed from the solution and fixed in the clamps to leak out. After 15-30 minutes this step was considered to be complete. The final weight of the treatment solution was assessed. After air-drying for 2 hours the treated blocks were placed in pre-weighed and labelled beakers and transferred to the 52% RH desiccator for storage. The desiccator was vented periodically to remove volatilized solvents. SamPle analvsis Treatments solutions The radioactivity level of the treatment solutions, before and after the dipping treatment, was assayed by liquid scintillation counting (LSC). Solution aliquots of 1 ml were perfectly miscible with 10 ml Insta-Gel II (Packard) scintillator cocktail. A Packard Tri-Carb 4530 microprocessor controlled liquid scintillation spectrometer automatically performing quench and luminescence corrections and converting cpm (counts per minute) into dpm (disintregations per minute) was utilized. Wood blocks Five consecutive 2-mm zones were marked on the surface of the blocks in a direction parallel to the wood fibers. The blocks were clamped in a bench-vice and each 2-mm zone was removed by rasping. The shavings were collected on a plastic sheet fixed on the bench-vice. Quadruplicate 50-mg aliquots per 2-mm section were weighed into combusto-cones (Packard) and combusted in a Packard 306B Sample Oxidizer. The produced 14CO2 was trapped in Carbo-Sorb-II (Packard) (7 ml) and radiocounted in Permafluor V (Packard) (12 ml), with the equipment described above. Calculations The amount of active ingredient, transferred from the treatment solution to the wood was calculated, starting from the radioactivity mass balance Wi . v . dpmi = Wf . v . dpmf + dpmt (1) where Wi equals the initial treatment solution weight (g), Wf the treatment solution weight (g) after dipping, dpmi and dpmf the radioactivity levels (dpm/ml) at these procedure steps, v the treatment solution specific volume (ml/g) and dpmt the total amount of radioactivity transferred from the solution during the dipping. Using the relation between the radioactivity levels of the initial treatment solution, dpmi (dpm/ml) and its active ingredient concentration, Ci (g/ml), the total active ingredient transfer was obtained from X = dpmt Ci .1 dpmi (2) On, expressing the load of active ingredient per unit weight of dry wood equivalent, Wb (g), and combining equations (1) and (2) X/Wb = (Wi . dpmi - Wf . dpmf) . v . Ci . 1 . 1 (in pg/g) (3) dpmi Wb Table 2 : Amount of azaconazole (x + 1 S.D.), expressed in mq Per crram oven-drv wood equivalent, transferred to beech blocks during dipping for various time intervals in three different active ingredient formulations. These amounts were calculated from the massa balance of azaconazole in the treating solutions before and after the dipping. Number of replicates = 3. Initial concentration of the treatment solution : 3 g a.i./litre. Room temperature. EMI16.1 <tb> <SEP> t <SEP> = <SEP> 1 <SEP> hour <SEP> t <SEP> = <SEP> 4 <SEP> hours <SEP> t <SEP> r <SEP> 24 <SEP> hours <tb> Waterborne <tb> formulation <SEP> 2 <SEP> 0.608 <SEP> (+ <SEP> 0.008) <SEP> 1.019 <SEP> (+ <SEP> 0.039) <SEP> 1.858 <SEP> (+ <SEP> 0.297) <tb> formulation <SEP> 6 <SEP> 0.924 <SEP> (+ <SEP> 0.162) <SEP> 0.952 <SEP> (+ <SEP> 0.119) <SEP> 1.810 <SEP> (+ <SEP> 0.376) <tb> Organic <SEP> solvent <tb> Oil <SEP> based <SEP> I <SEP> 0.530 <SEP> (+ <SEP> 0.085) <SEP> 0.835 <SEP> (+ <SEP> 0.012) <SEP> 1.643 <SEP> (+ <SEP> 0.018) <tb> oil <SEP> based <SEP> II <SEP> 0.212 <SEP> (+ <SEP> 0.042) <SEP> 0.279 <SEP> (+ <SEP> 0.069) <SEP> 0.510 <SEP> (+ <SEP> 0.076) <tb> Table 3 : Amount of azaconazole a.i. formulation (x + 1 S.D.), expressed in ml per aram oven-dry wood ecuivalent, transferred to beech blocks during dipping for various time intervals in three different active ingredient formulations. Number of replicates = 3. Initial concentration of the treatment solution : 3 g a.i./litre. Room temperature. EMI16.2 <tb> <SEP> |t <SEP> = <SEP> 1 <SEP> hour <SEP> t <SEP> = <SEP> 4 <SEP> hours <SEP> t <SEP> = <SEP> 24 <SEP> hours <SEP> <tb> Waterborne <tb> formulation <SEP> 2 <SEP> 0.164 <SEP> (+ <SEP> 0.023) <SEP> 0.280 <SEP> (+ <SEP> 0.023) <SEP> 0.588 <SEP> (+ <SEP> 0.051) <tb> formulation <SEP> 6 <SEP> 0.207 <SEP> (+ <SEP> 0.067) <SEP> 0.278 <SEP> (+ <SEP> 0.040) <SEP> 0.471 <SEP> (t <SEP> 0.063) <tb> organic <SEP> solvent <tb> Oil <SEP> based <SEP> I <SEP> 0.110 <SEP> (+ <SEP> 0.016) <SEP> 0.157 <SEP> (+ <SEP> 0.021) <SEP> 0.229 <SEP> (+ <SEP> 0.003) <tb> Oil <SEP> based <SEP> II <SEP> 0.102 <SEP> (+ <SEP> 0.021) <SEP> 0.130 <SEP> (+ <SEP> 0.024) <SEP> 0.232 <SEP> (+ <SEP> 0.027) <tb> Table 4 : Estimated concentration of azaconazole (x + 1 S.D.), expressed in mq Per ml impregnated solution, in the solution transferred to beech blocks during dipping for various time intervals in three different active ingredient formulations. Number of replicates = 3. Initial concentration of the treatment solution : 3 g a.i./litre. Room temperature. EMI17.1 <tb> <SEP> H <SEP> - <SEP> 1 <SEP> hour <SEP> t <SEP> = <SEP> 4 <SEP> hours <SEP> t <SEP> = <SEP> 24 <SEP> hours <tb> Waterborne <tb> formulation <SEP> 2 <SEP> 3.737 <SEP> (+ <SEP> 0.468) <SEP> 3.755 <SEP> (+ <SEP> 0.223) <SEP> 3.145 <SEP> (+ <SEP> 0.236) <tb> formulation <SEP> 6 <SEP> 4.654 <SEP> (+ <SEP> 0.710) <SEP> 3.463 <SEP> (+ <SEP> 0.077) <SEP> 3.944 <SEP> (+ <SEP> 1.061) <tb> Organic <SEP> solvent <tb> oil <SEP> based <SEP> I <SEP> 4.826 <SEP> (+ <SEP> 0.080) <SEP> 5.389 <SEP> (+ <SEP> 0.688) <SEP> 7.161 <SEP> (+ <SEP> 0.387) <tb> oil <SEP> based <SEP> II <SEP> 2.089 <SEP> (+ <SEP> 0.254) <SEP> 2.118 <SEP> (+ <SEP> 0.171) <SEP> 2.189 <SEP> (+ <SEP> 0.079) <tb> Table 5 : Amount of azaconazole as a.i., detected at different penetration depths, in beech blocks dipped for 1 hour in three different active ingredient formulations. Cumulative concentration over the whole block. Initial concentration of the treatment solution : 3 g a.i./litre. Room temperature. penetration depth whole 0-2 mm 2-4 mm 4-6 mm 6-8 mm 8-10 mm block a) a) a) a) a) b) formulation 2 1.687 0.313 0.307 0.302 0.249 0.608 Oil based I 1.384 0.338 0.197 0.190 0.191 0.572 a) concentration in mg of azaconazole as a.i. per gram wood at 52% relative humidity b) concentration in mg of azaconazole as a.i. per gram oven-dry wood equivalent B. ImPreqnation treatment The dried wood specimens were grouped in 5 sets of 15 pine blocks and 5 sets of 15 beech blocks, one set for each formulation type. A selected group was collected in a beaker, covered with a weight for ballasting, and positioned in a vacuum desiccator. Pressure was reduced to 10 mm Hg by a Leybold-Heraeus S8A vacuum pump. After 15 minutes, 200 ml of the chosen treatment solution was drawn into the desiccator through a tube leading to the beaker. Excessive foaming was avoided. When the blocks were covered, the vacuum was released. The beaker was removed from the desiccator and left for two hours to complete the impregnation. Next, the blocks were lifted from the treatment solution, allowed to drip for 1 minute and weighed (weight after treament: Wt). The blocks were air-dried at room temperature, in a forced ventilation fume-hood for 4 hours. Five blocks were taken at random for analysis, whereas the remaining blocks were stored at 250 C in the dark for fixation: five blocks were stored for 2 weeks, five blocks for 7 weeks. The outlined procedure was followed for each of the 10 wood-formulation type combinations. Active ingredient determination Wood¯sPe¯i¯e¯ The concentration of active ingredient in the wood blocks, immediately after treatment was determined by radioassay. The blocks were clamped in a bench-vice and a symmetrical half was removed by rasping. The raspings were collected on a plastic sheet, and homogenized thoroughly. Quadruplicate 50-mg aliquots were weighed into Combusto-Cones (Packard) and combusted in a Packard 306B Sample Oxidiser. The produced 14C02 was trapped in Carbo-Sorb II (Packard) (7 ml) and radiocounted as described hereinbefore in Permafluor V (Packard) (12 ml). Alternatively, wood raspings were solvent extracted, using dichloromethane for oil based formulations-treated blocks and methanol for water dilutable formulations-treated blocks, in a solvent: solids ratio of 20:1 (v:w). Four consecutive extractions, spread over a 24-h period, were performed. The extracts were combined. adjusted to a known volume and radioassayed as described hereinbefore, using Insta-Gel II (Packard) as scintillation cocktail, added directly to l-ml aliquots of the methanol extracts or to the solvent evaporation residue of 1 ml-aliquots of the dichloromethane extracts. The calculated concentration of azaconazole in the-wood. Lw (g a.i./kg wood). was obtained as follows: Lw = U . CO . 1 . 1 (1) do WO where U is the treatment solution uptake (in g per test block), Co the a.i. concentration in the treatment solution (in g per litre), do the density of this solution (in kg per litre) and Wo the weight of the test block (in g). Alternatively, the azaconazole load can be expressed on a volume basis (kg a.i./m3 wood): Lv = U . Co . 1 . 1/v (2) d0 where V is the volume of the wood blocks (6 cm). The determined concentration of azaconazole in the wood. immediately after treatment. was obtained by measuring the radioactivity levels. Table 6: The weight of the test bolcks, the uptake of azaconazole formulation during impregnation, and the concentration of active ingredient (a.i.) - expressed in g per kg wood or in kg per m wood - calculated from uptake or determined by radioassay (x # 1 S.D.). Determined azaconazole concentrations are subjected to Duncan's Multiple Range test. Oven-dry Treatement Calculated azaconazole Determined azaconale weight of solution concentration concentration Wood Formulation blocks uptake species Wo U (g) (g/block) g a.i./kg kg a.i./m g a.i./kg kg a.i./m PINE Oil based II 3.00(#0.14) 2.51(#0.18) 2.92(#0.29) 1.46(#0.10) 2.93(#0.23= 1.48(#0.14) Oil based III 3.03(#0.11) 2.54(#0.20) 2.98(#0.27) 1.50(#0.12) 2.97(#0.34) 1.49(#0.17) formulation 6 3.03(#0.12) 4.13(#0.20) 4.10(#0.24) 2.06(#0.10) 4.21(#0.17) 2.13(#0.08) formulation 9 3.04(#0.14) 4.13(#0.25) 4.09(#0.37) 2.06(#0.12) 4.23(#0.53) 2.19(#0.21) formulation 17 3.05(#0.12) 4.19(#0.23) 4.12(#0.26) 2.09(#0.12) 4.31(#0.30) 2.22(#0.13) BEECH Oil based II 3.43(#0.15) 1.84(#0.18) 1.87(#0.20) 1.07(#0.10) 1.84(#0.22) : B 1.04(#0.10) Oil based III 3.54(#0.16) 2.01(#0.21) 2.01(#0.23) 1.19(#0.12) 1.80(#0.25) : B 1.04(#0.12) formulation 6 3.42(#0.09) 3.43(#0.36) 3.01(#0.31) 1.71(#0.18) 3.10(#0.38) : A 1.76(#0.22) formulation 9 3.49(#0.10) 3.45(#0.56) 3.01(#0.52) 1.72(#0.28) 3.05(#0.62) : A 1.77(#0.32) formulation 17 3.49(#0.08) 3.50(#0.30) 3.00(#0.22) 1.75(#0.15) 3.21(#0.30) : A 1.85(#0.20) D. Efficacv ExamPle VII I. EXPERIMENTAL PROCEDURE I.1. Materials a) Test fungus: Coriolus versicolor 863 A or ConioPhora Puteana was grown on malt agar at 250C in Petri dishes, having a diameter of 120 mm. 20-day-old cultures were used in the test. b) Test wood: Wood blocks (5 x 2 x 0.6 cm.) (beech or pine) were used as test material. c) Test solutions: Test solutions were made by dissolving a desired amount of the concerned formulation in distilled water or xylene. I.2. Methods a) Treatment of wood blocks with preservatives Test bocks were oven dried for 18 hours at 100-1100C, cooled in a desiccator and weighed (i.e. initial dry weight). Test blocks were weighed down in a Petri dish bottom and placed in a vacuum desiccator. The pressure was reduced to 40 mbar by a water suction pump, the blocks were impregnated with the preservative solution or the blanco solution through a tube leading to the Petri dish. When the blocks were well covered, vacuum was released, the Petri dish was removed from the desiccator and left for four hours in order to saturate and sterilize the blocks. Control blocks were treated in a similar sterile manner by impregnating the wood blocks with a blanco solution. Blocks were tamponed with sterile filter paper and weighed under sterile conditions (i.e. weight after treatment). The amount of preservative taken up by the blocks was calculated (i.e. preservative in wood). b) Inoculation of blocks After drying for six days in a laminar air flow chamber the blocks were transferred to the inoculum Petri dishes and exposed to the attack of Coriolus versicolor or conloPhora Puteana by placing two blocks, one treated with preservative and one control block, on a stainless steel frame in the Petri dish. Pairs of blocks were chosen in the same weight range. c) Duration of test The test blocks were exposed to fungal attack for 8 weeks at 250C. Petri dishes were put together in a plastic bag to avoid desiccation. d) Examination of test blocks after exPosure to final attack The blocks were freed from adhering mycelium, oven dried for 18 hours at 100-1100C, allowed to cool in a desiccator and weighed (i.e. final dry weight). II. RESULTS Table 7 illustrates the toxic thresholds for the aqueous solutions and the oil based mixtures. Toxic threshold as used herein is the amount of azole per m3 of wood preventing the wood from decay in such an amount that 3 percent weight loss is effected. The percentage of weight loss is found following the formula initial dry weight - final dry weight 100 initial dry weight and the amount of test compound absorbed per m3 of wood is found following the formula Csol (weight after treatment - initial dry weight) . d50l wherein CSO1 and dsol have the meaning of the concentration of the preservative in the test solution, respectively the density of the test solution. Since it is irrealistic to define the exact the exact amount of azole/m of wood preventing the wood from decay in such an amount that exactly 3 percent weight loss is effected Table 7 illustrates the range wherein the exact amount is embraced. The said range is limited by a lower amount, i.e. the highest tested amount where more than 3 percent weight loss is effected, and a higher amount, i.e. the lowest tested amount where less than 3 percent weight loss is effected. Table 7: Toxic threshold. diluted Coriola versicolor Coniophora puteana with kg azaconazole/m3 kg azaconazole/m3 formulation 2 water 0.031-0.057 0.537-0.823 formulation 6 water 0.033-0.061 0.547-0.742 oil-based I xylene 0.069-0.143 0.940-1.222

Claims: CLAIMS 1. A water-dilutable wood-preserving liquid containing i) from 10% w/w to 80% w/w of a suitable solvent; ii) from 20% w/w to 80% w/w of a suitable solubilizer; and iii) from 0.018 w/w to 10% w/w of at least one azole having the formula EMI24.1 or an acid addition salt thereof, wherein X is nitrogen or a CH group and R1 is a radical of the formula EMI24.2 wherein Z is a group -CH2-CH2-, -CH2-CH2-CH2- -CH(CH3)-CH(CH3)- or -CH2-CH(alkyl)-, wherein said alkyl is a straight or branched C1-C10 alkyl radical; said Ar is a phenyl group which is optionally substituted with 1 to 3 halogens, C -C aikyl radicals. C1-C6 alkoxy radicals. cyano-, trifluoromethyl- or nitro groups, a thienyl-, halothienyl-, naphthalenyl- or fluorenyl group: and, said R is C1C10 alkyl. cycloalkyl, cycloalkyllower alkyl. lower alkenyl, aryllower alkyl. aryloxylower alkyl or a radical of the formula -O-Ro, wherein said R0 is Cl-C1O alkyl. lower alkenyl, lower alkynyl or aryllower alkyl. wherein said aryl radical is phenyl, naphthalenyl or substituted phenyl, wherein said substi tuted phenyl has 1 to 3 substituents selected from the group consisting of halo, cyano, nitro, phenyl, lower alkyl and lower alkoxy, provided that when more than one substituent is present only one thereof may be cyano, nitro or phenyl. 2. A liquid according to claim 1 wherein the azole is selected from the compounds having the formula: EMI25.1 wherein X is N or CH and R1, is a radical of the formula EMI25.2 wherein Z is a group -CH2-CH2-, -CH2-CH2-CH2-, -CH(CH3)-CH2-, CH(C2H5)-CH2-, CH(C3H7)-CH2-, -CH(CH3)-CH(CH3)- or -CH(CH3)-CH(C2H5)-; Ar' is unsubstituted phenyl or phenyl substituted with 1 to 3 halogen atoms, preferably chloro atoms, C1-C6 alkyl radicals, C1-C6 alkoxy radicals, cyano or nitro groups; and R' is C1-C6 alkyl or C3-C4 alkenyloxy. 3. A liquid according to claim 1 wherein the azole is selected from the compounds having the formula EMI25.3 wherein X is N or CH and R1" is a radical of the formula EMI25.4 wherein R" is C1-C4 alkyl, C3-C4 lower alkenyloxy, R3 is hydrogen or C1-C3 alkyl and n is 1 or 2. 4. A liquid according to claim 1 wherein the azole is 1-[2-(2,4-dichlorophenyl)-1,3-dioxolan-2-ylmethyl]-1H-1,2,4-triazole. 5. A liquid according to any of claims 1 to 4 wherein the solubilizer is selected from the group consisting of: i) addition products of 1 to 60 moles of ethylene oxide with 1 mole of a phenol which is further substituted with at least one C1-C15 alkyl group; and ii) addition products of 1 to 60 moles of ethylene oxide with 1 mole of ricinus oil. 6. A liquid according to any of claims 1 to 4 wherein the solubilizer is selected from the group consisting of: i) addition products of 1 to 60 moles of ethylene oxide with 1 mole of nonylphenol or octylphenol; and ii) addition products of 1 to 60 moles of ethylene oxide with 1 mole of ricinus oil. 7. A liquid according to any of claims 1 to 6 wherein the solvent is 2-butoxyethanol or butyl 2-hydroxyacetic acid ester. 8. A water-dilutable wood-preserving liquid containing: i) from 108 w/w to 80% w/w of 2-butoxyethanol; ii) from 0.018 w/w to 10% w/w of l-(2-(214-dichlorophenyl)- 1,3-dioxolan-2-ylmethyl]-lH-1,2,4-triazole or an acid addition salt thereof; and iii) a mixture of addition products of nonylphenols with ethylene oxide wherein an average of 8 moles of ethylene oxide has been reacted with 1 mole of nonylphenol, ad 100% w/w. 9. A water-dilutable wood-preserving liquid containing: i) from 10% w/w to 80% w/w of butyl 2-hydroxyacetic acid ester; ii) from 0.01% w/w to 108 w/w of 1-(2-(214-dichlorophenyl)- 1,3-dioxolan-2-ylmethyl]-lH-1,2,4-triazole or an acid addition salt thereof; and iii) a mixture of addition products of ricinus oils with ethylene oxide, ad 1008 w/w. 10. An aqueous mixture prepared by diluting a water-dilutable liquid according to any of claims 1 to 9, for use in the preservation of wood.

Inventors: LIGTVOET, THEO FRANS MARIA CORNELIUS, VAN DYCK, PAUL CONSTANT MARTIN, VAN LEEMPUT, LEO JAN JOZEF
Applicants: JANSSEN PHARMACEUTICA N.V.
Application year: 1984
Main classification: B27K3
IPC codes: A01N43, A01N25, B27K3