INSULATION SYSTEM

Abstract: A method and apparatus for directing a stream of bulk fibers while simultaneously spraying an inorganic tempera­ ture resistant tacky binder material into the stream of fibers. A layer of high temperature insulating fibers may thus be formed. The binder may be a phosphate tackifying agent mixture or a colloidal suspension of materials with the tackify­ ing agent. The tackifying agent is preferably montmorillonite clay.

Description: INSULATION SYSTEM Background of the Invention Field of the Invention The invention relates to a method for applying a layer of fibers coated with a tacky inorganic binder onto B surface. More particularly, the invention is a method for spraying a layer of refractory fibers coated with a high temperature inorganic binder including a montmorillonite clay. By way of further characterization, but not by way of limitation thereto, the invention is a method and apparatus for spraying refractory fibers coated with a novel binder including a montmorillonite clay onto a surface and curing the coated fibers. Descrintion of the Prior Art In the past, high temperature resistant fibrous material has been applied to heated surfaces, such as heat treating furnaces and kilns, by attaching butts or strips containing such fibers to the heated surface. This method requires mechanical anchoring or fastening means to attach the strips to the heated surface. Such mechanical attachment is expensive in that it requires large amounts of labor and fastening materials to attach the strips. In addition, because this method is time consuming, it requires the furnace or kiln to be out of service for extended periods of time. Finally, Saps between adjoining strips may occur either dozing the attachment process or later due to thermal shrinkage which allows heat leakage between the layers of fiber. Improvements to this method of attaching refractory fiber linings to the wall of kilns and furnaces have been made such as is described in U. S. Patent No. 4,381,634. This method involving the mechanical attachment of rdules, overcomes many of the problems associated with layered linings especially the opening of gaps betkeen the edges sE layers due to beat shrinkage at elevated temperatures. However, liko the above method, the use of modules requires mechanical attachment to the metal shells of furnaces which again require considerable cost in labor. The use of modules has also been found to be of value in relining old dense refractor; linings such as refractory brick. In this case the folded or pleated modules are glued to the old monolithic or strick lining by use of a refractory mortar or glue which is generally of the hydraulic setting nature. This method of relining of kilns is labor intensive requiring the application of mortar to the brick work and then quickly applying the folded modules thereon. This method requires that time be given for the setting of the hydraulic mortar before the newly lined kiln can be fired. All the above methods have one feature in common which is that they present an unbonded refractory fiber lining to the interior of the kiln. As time goes by these fibers devitrify (crystallize) and In so doing lose some of their mechanical strength making them more susceptible to mechanical abrasion and destruction due to high velocity gases from the heating mechanisms of the kilns. High temperature resistant binder powders have been mixed with water and sprayed with refractory fibers. Such methods typically employ calcium alumina cements which are very alkaline and will settle when in suspension. It is also dlfffcult to achieve homogenous mixing of fiber and binder with such a system. A hydraulic bond must be achieved prior to drying of tne cemen; otherwise bonding of the fibers will not occur. In addition, careful drying of the sprayed mixture must be undertaken in order to prevent violent spilling. Other methods for spraying insulation have been employed in the past utilizing organic binders. For example, 'U.S. patent 2,929,436 issued on arch 22, 1960 discloses a method and apparatus for spraying a mixture of fibers and resin -material. As indicative of prior methods of application, this patent discloses mixing fiber and resin in a nozzle and spraying the mixture onto a surface. However, while suited for its intended purpose, such method and apparatus, if used in the spraying of refractory fiber with a tacky inorganic binder, would cause clogging of the nczl. In addtIon, incomplete coating of the refractory fibers could cause a weakened layer of fibers which in turn could cause failure of the Insulating layer at high temperatures. Because of the temperatures to which refractory fibers are subjected, often 2.00off or more, south failures could be dangerous to workers In such industries as the steel industry and could cause extensive damage to furnaces and kilns. Thus, the Intimate admixture of refractory fiber and the tacky inorganic binder to form a monolithic layer is important to the safe and efficient operation of such furnaces and kilns. Prior art binders for bonding refractory fibers have included a variety of compounds including colloidal silica and phosphoric acid (actually P205 which may be derived from H3PO4 under appropriate temperature conditions). While these binder systems are useful in certain applications, they are not without relative disadvantages. For example, prior art phosphoric acid binders do not adhere well to refractory fibers. Binders Including colloidsl silica are subject to irreversible precipitation of the silica if the binder has been subjected to freezing temperatures. A very serious disadvantage with prior art binder systems is binder migration. That is, as the binders are used, the binder migrates to the surface of the material producing a material with a very soft interior. This causes serious Integrity problems with the resulting material. The materiai Is thus not suitable for use in applications requIring a monolithic structure. In addition, prior binder systems employing colloidal suspensions such as colloidal silica or alumina must be cured very carefully. That is, because or binder migration, the colloidal sol must be allowed to gel prior to curing. Failure to do so results in migration of the binder particles from the interior to the surface of the insulation layer. In addition, prior art binders must be sprayed onto a cool surface thus necessitating relatively long cooling periods before a furnace can be insulated. Another dIsadvantage of prior art binders has been that they are not nearly as temperature resistant as the refractory fibers themselves. Thus, high temperature applications of the fiber-binder mix are limited by the properties of the binder rather than the fiber. For example, an insulation product made from refractory fibers which are themselves temperature resistant up to 260off may only be applied In temperature environments up to 2O000F If the binder used in that product is only effective up to 2000eF. Any reaction of the binder and fiber which tends to rlux the fiber composition causes increased fiber shrinkage. Thus, the use temperature of the fiber - binder system is limited to a temperature less than the use temperature of the fibers alone. other practical problems encountered with tSe use of print binder systems is that they are expensive, there may be safety and environmental problems in their applications, they may lack good suspension properties, and finally, as with prior phosphoric acid binders, the binders do not possess the tackiness or adhesIveness properties which are desirable in many applications. In applications where it is desirable to spray the refractory fiber onto a surface such as a furnace wall, it is essential that the binder be sufficiently tacky to cause the fibers to adhere to one another and to the surface. Summary of the InventIon The invention is a method for applying a layer of Fiber to a surface while simultaneously coating the fiber with a tacky inorganic binder. The layer of binder coated fiber is cured such that the layer becomes monolithic. The fibers are coated with the binder as they are directed from the spray gun and the coated fibers are caused to stick to each other and to the surface toward which they have been directed. Once the fibers have been bonded to the surface, they may be compressed by means such as tamping in order to alter the density of the layer. The layer is cured such that all of the moisture is driven out of the layer. Preferably, the layer is subjected to a temperature of at least 3500F for a few hours in order to cure the binder and fiber. However, the layer can be rnmediately exposed to temperatures as high as IOOC' wIthout damage. The present invention combines an inorganic binder matrix with temperature resistant clays. The tacky nature of the binder renders it suitable for a wide variety of applications. The resulting binder of the present invention is temperature resistant to at least 3000n e which allows is use with high temperature refractory fibers. As used herein, refractory fibers are defined as inorganic amorphous or crystalline fibers which are not adverrelv affected by temperatures in excess of i500 F. An example of such fibers is alumina-silica fibers. However, as is knows in the art, fibers including zirconia, chromium, calcium, magnesium and the like may be utilized. The binder disclosed herein could also be employed with metal oxides to provide an Insulating layer of such material. Yn addition, the binder system of the present invention greatly reduces or eliminates binder migration which occurs in prior art binders. The binder includes a tackifying agent in combination with a phosphate binder matrix such as alumInum phosphate. The preferred tackifying agents are temperature resistant clays such as monttnorillonlte clays. The most preferred clay is western bentonite clay. A fluxing agent may also be added to the binder in small quantities to increase the strength of the binder to fiber bonds at elevated temperatures. Chromium oxide may also be added to the binder to improve the stability of the binder to flyer bonds at elevated temperatures. In addition, ch.smium oxide adds color to the binder which may be advantageous in the coating process. In addition to phosphate compounds, colloidal suspensions such as colloidal silica colloidal alumina, and colloidal zirconia may be combIned with the tackifying agents disclosed herein to produce a suitable binder. When the disclosed tsckifying agents are combined with these cclloidal suspensions the severe binder migration problems associated with colloidal binders such as colloidal silica are overcome. The addition of the tackifying agent in parts good suspension characteristics to the binder. AdditIonally, the preferred binder of the present Invention may be sprayed directly onto hot surfaces thus elImInating long delays In insulating furnaces requirIng complete cool down. Finally, the novel binder claimed herein reduces shrinkage of the coated fibers thus improving their refractory characteristics. Because shrinkage is minimized, failure or the Insulation layer due to cracks in the layer is reduced.- Prior art binders, especially colloidal silica binders without the tacifying gent disclosed herein reoulred gelling of the colloidal silica. Othe.wiee, serious binder migration to the surface of the Insulation layer would occur. Brier Description of the Drawings Fig. 1 is an illustration of the binder coated fiber being applied to a furnace; Fiz. 2 is an enlarged perspective view of a novel spray gun for carrying out the method of the present invention; Fig. 3 is a vertical cross-sectional view taken along line 3-3 of Fig. 2; Fig. 4 is an elevational view of the novel spray gun; Fig. 5 is a front perspective vie of an alternate embodiment of the spray gun providing a circular fiber path; and Fig. 6 is a side sectional view of a preferred spray gun for carrying out the method of the invention. Description of the Prey erred Embodiment Referring to Fig. 1, an operator lii dressed in suitable protective clothing 12 including an enclosed breathing apparatus 13, is shown holding a spraying apparatus generally designated as 14 from which a stream 15 of binder coated refractory fiber is being directed onto furnace wall 16. As used herein, refractory fibers are defined as inorganic, amrphous, or crystalline fibers which are not adversely affected by temperatures in excess of l5OOF. Examples of such fibers are alumina-sllica-zirconia fibers, alumina silica fibers and other refractory fibers as are known in the art. Preferably the fiber is blown by air pressure from a suitable compressing apparatus (not ±hwn). Furnace wall 16 is a bare metal wall of furnace 11. Similarly, ceiling 17 is a bare metal wall of furnace 11 onto which stream 15 mas be directed. A previously fired or new refractory brick wall 18 of. furnace 11 may also be coated with the layer of binder coated fiber. Similarly, a wall 19 which has been previously covered with refractory fiber modules as is known to one skilled in the art may also be coated utilizing the method of the present invention. A second operator, generally designated 21, also in protective clothing and breathing apparatus, is shown with a co..press-tng apparatus 22 which may be used fr tamping the layer of binder coated fiber so as to alter the density of the layer deposited by the method of the present invention. Referring to Fig 2, spray gun 14 is shown in more detail. or specifically, the refractory fIber stream 24 is directed through candult 23 so as to emerge from an annular path defined by a deflector body 25 an a manifold 26. Def'ector body 25 is preferably cone shaped and is supported in Q manifold 26 by one or mire vanes 27 as illustrated in Fig. 3. Deflector body 25 deflects the flow of bulk fibers so as to assume an annular path in an oval or circular configuration dependIng upon the shape of deflector 25 and manifold 26. Thus a thin ribbon flow of fibers exits in an annular path to be coated on both sides as explained below. The binder solution is fed through a binder feed line 27 and binder valve 28 into an external nozzle manifold 26 which feeds a plurality of spaced nozzles 31 surrounding the outside 37 of the annular fiber stream 24. Nozzles 31 are directed inwardly so as to spray the liquid binder solution onto the outer fibers 37 as they emanate from spray gun 14. Likewise, a ring of internal nozzles 32 are provided on deflector 25 so as to spray binder into the inner surface 30 of fiber stream 24. Binder is fed under pressure to nozzles 31 through binder feed line 28, valve 29 and manifold 26. Binder is fed under pressure to nozzles 32 through line 28, valve 2 and deflector 25. The fibers are uniformly wetted by the binder from two sides as they are being blown f.om the gun 14. Thus, the fibers are uniformly coated with liquId binder solution before reaching the surface to be coated. Referring to Fig. 4, a side elevationai view of spray gun 14 is shown as connected to flexible tubing 33. Flexible tubing 33 allows the fIber to be fed therethrough to conduit 23 in the spray gun 14 from a remote location thereby allowIng the operator freedom to move about the area to be sprayed. Similarlyq binder is fed to gun 14 through flexible line 28. Referring to Fig. 5, a perspective view of an alternate embodiment of the spray gun is shown in which the deflector 25 and manifold 26 are circular such that annular path 24 of fibers being blown from the spray gun 14 is circular. Referring to Fig. 6, a side sectional view of 2 preferred embodiment of a novel spray Sun is shown. In this spray gun, no deflector Is used to alter the path of fiber stream 24. Rather a nozzle 36 connected to, and supported by, a feed line 35 located in the approxImate center of the path of fiber stream 24. Thus while nozzles 31 spray binder into the outer portions 37 of fiber stream 24, nozzle 36 ensures that the fibers in the center of fiber stream 24 are coated with binder. Nozzle 36 sprays binder in a conical path as shown in order that the fibers be completely coated. It should be expressly understood that, while one nozzle 36 is disclosed, it is within the full intended scope of the invention that more than one nozzle 36 may be located in fiber stream 24. Thus, the combination of nozzles 31 and 32 serve to uniformly coat the fibers in moving stream of fibers 36. As such, all of the fibers are coated with the tacky inorganic binder. This is especially important where the binder is extremely tacky and thus is difficult to spray into a moving stream of material to any depth. Because the fiber and binder are being used in a high temperature environment it is essential that the fibers be coated uniformly in order that the layer formed by the coated fibers be of sufficient integrity to produce a monolithic layer on a furnace wall. Because of the heat to which the layer is subjected incomplete coating of the fibers would result in premature failure of the lining. In practise, the method is best carried out by adding water to the tacky high temperature inorganic binder concentrate in a large drum located at the site of the surface to be sprayed. Bulk, high temperature resistant fibers such as alumina-silica-zirconia fibers are placed in a hopper and may be shredded if needed to allow blowing thereof through spray gun 14. The liquid binder concentrate is mixed with water in the drum preferably in approximately the ratio of, by volume, 4.5 parts water to 1 part binder concentrate. It should be expressly understood that the dIlution ratio depends upon binder concentration and specific applications. Spraying the diluted binder directly onto the surface to be coated imrpoves the bond of the fiber binder layer to the surface. The diluted binder is constantly stirred in the drum as it is fed to the spray gun in order to ensure a homogeneous mixture of diluted binder. Referring to Fig. 6, the diluted binder solution is fed through binder feed line 28 into the external nozzle manifold 26 which feeds nozzles 31.Binder is supplied to nozzle 36 through line 35. Nozzles 31 and 35 spray binder into fiber stream 24. A ratio of about 1.75 lbs. fiber to about 1 lb. liquid binder is preferred. As with binder dilution, this ratio may be varied according to specific binder dilutions and application. The method of the present invention ensures uniform coating of the fibers while in transit to the surface to be sprayed such that the fibers will adhere to each other as well as to the surface end form layers of wetted fibers which may be built up to the desired thickness. In practice, thicknesses of up to 14 inches of wetted fiber have been achieved. Spray gun 14 may be located between about two to four feet or more from the surface as desired. The sprayed binder solution may converse along the axis of the sprayed fibers, either before reaching the surface or, in some cases, the point of convergence may not occur at all before reaching the surf ace but may be at an imaginary point beyond the surface to be sprayed. The bulk fiber may be blown by a suitable blowing apparatus (not shown), preferably at a rate of up to about 200 cubic feet of air per minute through the fiber feed line 23. While water is the preferred diluent because of its availability and cost, other suitable Inert diluents such as alcohol or ethers may be used. Once the coated fibers have been applied to the surface as in Fig. 1, the layer of binder coated fibers may be tamped as by the second operator 21 in Fig. 1. Operator 21 is shown atilizin a compressing trowel 22 in order to pack the coated fibers to the desired density. Once the fibers have been applied to the surface to the desired density, the binder is cured, by raising the tomperature of the furnace to at least 3500F and preferably to about 4St or more. While this is the preferred step for curing the fibers, any curing method which drives orf the water or other diluent and all moisture from the coated fiber layer may be utilized with the method of the present Invention. As shown in Fig. 1, the method of the present invention may be used to apply binder coated fiber to a variety of surfaces. While the stream of binder coated fiber may be applied Jirectit to the surfaces without support, it may be desirable In some instances to provide additicnal support for the fiber layer. That is, for example, expanded metal lathe could be attached to ceiling 17 of furnace 11 in order to provide additional support for the binder coated fiber layer. Any other supporting structure as is known in the art may also be tiiized. Additionally, it should be noted that the binder coated fiber is preferably applied to a surface which has been properly prepared. That is, in the case of refractory brick or other monolithic dense refractory such as shown on wall i8, such brick should be sand-blasted or otherwise prepared to remove loose or flaky material from the surface to be coated. If the binder coated fiber is to be applied to a metal surface as in li or wall 16 in Fig. 1, a asphaltum or other protective coating may be desired in some cases. Where the method is to be used to apply binder coated fiber to a wall of existing refractory fiber as in wall 19 of Fig. is it is desirable to again remove all loose or flaking surfaces from the surface to be coated. The binder coated fibers may also be applied over an existing layer of previously sprayed binder coated fibers or fibrous formed shapes. That is, should a portion of the previous layer be knocked off due to mechanical or other contact with the surface, a new layer of binder coated fibers may be applied over the damaged area. In many situations it is desirable to spray a coating of binder onto the fiber-binder layer after the layer has been applied to the surface. It can readily be seen that this method of applying refractory fiber linings overcomes many of the shortcomings prevIously described. This method, for instance, does not requIre the applIcatIon of a mortar to old brick work or refractory linings in order to apply fibers in modular form as in prior art methods. The binder supplies the adhering mechanism as the new layer is being applied which results in reduced labor costs. Nor does the present method require any particular waiting period for the mortar to form hydraulic bonds and then slowly dry out prior to tir a. It can also be seen that the present method eliminates one of the basic shortcomings in prior attachment methods which required the exposed refractory fiber layer to be coated with a bonding material after the layers or modules were installed to impart abrasion resistance. The present method ensures that all fibers throughout vhe layer are well bonded to one another forming an inherently superior monolithic lining. The surface of the lining applied with the present method is far less affected by mechanical or gas velocity abrasion. To support this statement the following experiment was conducted: a layer approximately 2 inches thick of 26000 refractory fiber anville CER.XCHROM.E) was sprayed according to the present method onto an 13" x 9" free standing refractory brick wall. This wall was placed directly in front of an sir natural gas burner port of a furnace so that the surface of the sprayed lining was at 900F to the flame at a distance of 24" from the burner. Upon repeated firing to temperatures of 2200"F, 2400eF, and 26000F, there was no damage to the sprayed layer from this extreme condition of temperature and gas stream velocity. A novel method has been disclosed for applying refractory or other fiber which has been coated with a binder to a surface. Because the method ensures bonding together of the high temperature resistant fixers and their adherence to a surface, thick layers of heat insulating fibers may be applied very quickly. Because the application of the insulation is done in a very small fraction of the time normally required by present methods, the cost of the installation as well as the down time of the furnace or other device to be Insulated are substantially reduced. Finally, the method disclosed herein allows immediate heating of the fiber layer thereby allowing the furnace or other device to be put into service alm.ot immediately after spraying. Tn fact, with the use of ramota controlled devices such as robots or an air on water cooled lance, the binder fiber layer could be applied to a furnace which is at operating temperature. This would be useful to repaIr furnaces while still in operation. In accordance with the present invention, an excellent binder system has been discovered which preferably comprises chromium aluminum phosphate and a suitable tackifying agent. The chromium aluminum phosphate compound preferred in the present invention may be characterized by the rcllowing generalized formula: Al2O3.3P2O5.xCr@O@ wherein x ranges from about 0.1 to 10. The term "tackifying agent", as used with respect to the present invention, is meant to define those substances which impart tackiness or adhesive properties to the binder system of the present invention. Generaily, such tackifying agents will be inorganic in nature. igh temperature resistant clays, especially montmorilionite clays (preferably the western bentonite variety) have been found to be useful in the present invention Sodium and calcium based clays such as southern bentonlte may also be used as a thckifging agent. Whatever tackifying agent is used should, of course, be compatible with the overall binder system and its intended use with regard to both chemical and physical properties. It is especially Important that the tackifier, in the quantity used, not produce fluxing of the binder-fiber system at elevated temperatures. While the inventive binder system may be made according to any suitable method shown to those skilled in the art, the superior binder system of the present invention is preferably made according to the generalized process described herein below. A mixture of phosphoric acid solution, an appropriate fluxing agent such as boric acid, and bentonite clay are stirred together and then heated to a temperature typically '00 F) sufficient for the ingredients to react with one another. Although varying concentrations of phosphoric acid may be used, in the present invention a 75% or higher phosphoric acid solution is preferred. As used herein, the term appropriate fluxing agent Is meant to include those substances which will Impart added strength to the inventive binder system by improving glassy bonding at elevated temperatures. While boric acid is a preferred fluxing agent, other inorganic metal salts such as sodium carbonate, magnesium chloride, magnesium nitrate, calcium carbonate, cobalt oxide, and others may be enplcyed. After heating to approximately 100 F the above reaction mixture is combined with a hydrated alumina. The preferred alumina is a hydrated alumina such as that currently marketed by ALLOT under the trademark C-31. The mixture is the heated to a temperature Jf approximately 180 F at which time chromic oxide (Cr20) ) t is added. The preferred chromi oxide has a specific gravity of 5.1 and is added in a percent, by weight, of 1.96 . of ; the total mixture weight. At this point the reaction becomes eohermic, the temperature rises to approximately F, the volume of the mIxture approximately doubles, and the reaction is complete. The solution is allowed to cool and an nert carrier such as water is added to adjust the specific gravity of the binder to .iO at room temperature. The above ingredients are used in the present invention at the following general, preferred, and most preferred weight percentage levels based upon the total weight of the binder. TABLE Most Ingredient General Preferred Preferred Phosphoric Acid Solution 50-90 75-35 78.8 Fluxing Agent S-) 2-4 2.37 Tackifying Agent 1-3 1-5 2.87 Hydrated Alumina 5-30 10-20 14.2 Chromium Compound 0.5-5 1-2 1.26 While chromic oxide Cr2O3 has been disclosed, other suitable chromium compounds Include solutions of chromic acid (H2CrO4), and chromium salt solutions such as magnesium chromate, which can be converted under appropriate temperature editions to chromia (Cr203 I, may be added. Similarly, while alumina has been disclosed as the preferred metal oxide to be reacted with the phosphoric acid solution, magnesium oxide or other suitable metal oxides may be reacted with the phosphoric acid sclution without departing from the scope of the invention. An alternate binder formulation includes colloidal silica combined with a tackifying agent. Preferably NALCO 1115 Colloidal Silica of the 4 milllimicron size Sol containing 15% solIds is used. Approximately forty pounds (40 1bs) of this colloidal silica was mixed with 1.25 pounds of western bentonite to form a tacky binder. The addition of a montmorillonite clay such as western bentonite to the binder tratrix has been found to produce a tacky binder which adheres tc virtually any surface. While Western Bentonite is preferred, any of the clays selected from the Kontmoriilonite types of clay mInerals have been found to be suitable tacklfying agents. The binder of the present invention may be advantageously employed with refractory fibers In a sprxy-on prccess. That is, refractory fibers may be directed from a spray gun while at the same time being coated with the binder of the present invention. Such applIcation of refractory fiber and binder has been found to raise the operating temperature of the refractory fibers above their normal rated temperature. For application of refractory fiber to a surface such as a furnace wall, the binder is diluted, preferably with water, in a 4.5 to 1 water to binder ratio by volume. This ratio may range from 2 to 1 to 15 to 1 by volume. The diluted binder is preferably stirred in the dilution container to ensure a homogeneous mixture during the spraying process. The diluted binder may be sprayed with the fiber onto a surface In a rntio which depends upon binder diluton. For the preferred chromium aluminum phosphate binder disclosed above, a ratio of 1.75 Ibs. of fiber to 1.0 Ib. binder is preferred. Examples of dIfferent binder formulations and concentrations are listed below: Binder &num;1 was a mixture ot NALCO AG 1115 colloidal silica marketec by NALCO Chemical Corp. of 4 millimlcron size particles containing 15% solids. Forty pounds of this solution was mixed with 1.25 Lobs. of western benionlte. The resulting binder was sprayed in a 30X binder 70% alumina-sillca-zlrconia fiber ratio by weight and cured at 1000 F. A A 12 lb/ft composite material resulted having good intagrity. Binder &num;2 was a mixture of the chromium aluminum phosphate binder matrix with bentonite clay and boric acid in the most preferred formulation previously disclosed. This binder concentrate was dilated 4 to 1 by volume with water and sprayed with aluminasilica-zirconia fiber in a ratio of 14% binder to 86% fiber sy weight. This composite was then cured at 1O000F and produced a 12 ab/ft3 material. binder &num;3 was a mixture of 1/2 lb. colloidal alumina, 2 1bs. of -325 mesh Al2O3 particles and 1 1/4 lbs. bentonite in 40 ibis. of water. This binder concentrate was sprayed with alumina-silica-zirconia fibers in a ratio of 40% binder to 60" fiber. The resulting material was cured at 10000F and produced a material which did not adhere well to the brick substrate and did not produce material or sufficient integrity to allow density to be accurately measured. Binder &num;4 was a mixture of 11 1bes. of Kaolin Clay, 3/4 lbs. western bentonite and 20 lbs.or- water. This binder mixture was too viscous to be sprayed. Binder &num;5 was a mixture of the chromium aluminum phosphate binder matrix with bentonite clay and boric acid in the most preferred formulation previously disclosed. This binder concentrate was diluted 10 to l by volume with water and sprayed in equal amounts by weight with alumina-silica-zirconia fiber. The resulting material was cured at 1000 F and produced a material of 15 1b/ft3 density. Binder &num;6 was a mixture of the chromium al aluminum phosphate binder matrix with the bentonite clay and boric acid In the most preferred forumulation previously disclosed. This binder concentrate was diluted IS to I by volume with water and sprayed In a ratio of 45% binder to 55% alumina-siiica-zirconia fiber by weight. The resulting material was cured at room temperature and produced a material of 13 lbs/ft density. Binder 27 was a mixture of the chromium alumInum phosphate binder matrix with bentonite clay and boric acid in the most preferred formulation praviously disclosed. This binder was diluted 15 to 1 by volume with water and sprayed in a ratio of 36% binder to 64% alumina-silica-zirconia fiber by weIght. The resulting material was cured at 1000 F but did not produce a material of sufficient integrity to obtain a density measurement. Binder &num;8 was the colloidal silica binder disclosed as binder 11 without the bentonite clay. The binder was sprayed in a 60X binder to 40% fiber ratio by weigh; with alunina-silica-zirconia fibers. The resulting material was cured at 1000 F but did not produce a material of sufficient Integrity to obtain a density measurement due to binder migration. Binder &num;9 was a mixture of bentonite clay and water in a ratio by weight of 10% bentonite to 90 % water. This binder did not bond with the alumina-silica-zirconia fiber. A comparison of characteristics of the binder formulations is given below: IntegrIty with Binder Fibers after Binder Tacky ¯ Curing ration Binder &num;1 Yes Good Some Binder &num;2 Yes Fair Very little Binder &num;3 Yes Fair Some Binder 24 ve- Unknown Unknown Binder &num;5 Yes Excellent Very lIttle Binder &num;6 Yes Excellent Very little Binder &num;7 Yes Fair Unknown Binder 28 No Poor 'ry heavy Binder &num;Q Yes None Unknown A comparison of shrinkage between the materials of binders &num;1, 2, 3, 5, and 6 was made with each other and with the fiber alone. After being exposed to a temperature of 24000F for four hourt the binder - fiber composites exhibited the following shrinkage characteristics: Shrinkage (%) Binder &num;1 2.6 Binder &num;2 1.5 Binder &num;3 1.6 Binder &num;5 1.6 Binder &num;6 1.4 Fiber alone 2.0 From the above it can be seen that composites formed from t. mst preferred pindar concantrate formulation of binder 82, 5 and 6 exhibited less shrinkage than the fiber alone. While bInder 63 exhibited low shrinkage, the specific binder formulation exhIbited only fair bonding characteristics. A comparison of curing temperatures was made for binder &num;5. That is, the material made under binder formulation &num;5 was cured at 250 F, 2500F and 4500F. Each material was then placed in a 90% humidity chamber for 72 hours with the following results: the material cured at 250F received 31% added moisture and was wet and sot suggesting incomplete curing; the material cured at 350°V received 18% added moisture and was somewhat wet and soft, but was marginally acceptable; and the material cured at 450 F received 13% added moisture and was hard and held its integrity. Thus the curio temperature has a lower limit of about 350 F with a preferred curing tenperature of about 450 F or more. In order to determine the preferred limits of dilution and binder to fiber ratio for the most preferred chromium aluminum phosphate binder, the formulations of binders 22, 5, 5 and 7 were tested. The fiber-binder composite materials were compared with respect to the weight ratio of the original binder concentrate to fiber weight ratios in light of the integrity observed in the resulting material. The ratio of the weight of binder concentrate to fiber was 4.6% for binder &num;2; 14.52 for binder 25; 8.335 for binder 26; and 5.72% for binder &num;7. The materials produced by binders &num;5 and 6 had excellent integrity while the material from binders &num;2 and 7 had fair integrity. This suggests that the preferred binder concentrate to fiber weight ratio should be at least 6%. Thus, the binder dilution and dilutea binder to fiber weight ratio should be adJusted accordingly. While the invention has been disclosed with respect to preferred embodiment thereof, it is not to be so limited as changes and modifications may be made which are within the full intended scope of the Invention as defined by the appended claims. For example, as shown in Figs. 2 and 5, various geometric configurations of the spray gun may be employed so as to direct the path of the fibers to a specific application. In addition, various diluents a be used as the carrier for the binder concentrate. While chromium aluminum phosphate with bentonite clay has been disclosed as the preferred binder, other binders employing a temperature resistant clay such as montmorillonite, or plastic ball clays containing montmorillonite clay in quantities sufficient to ensure a tacky inorganic binder, may be employed. Finally, while the inventive method is disclosed with reference to spraying refractory fibers, any fiber such as fiberglass, mineral wool, or other suitable fibers may be utilized with the disclosed method. Combinations of these or dIfferent refractory fibers could also be employed to produce a stratified furnace lining which is extremely cost effective. In addition, the spraying of a binder with particulate matter such as various metallic oxides could be employed to provIde a particularly heat resistant surface over the sprayed fiber-bInder layer.

Claims: Claim What Is claimed is: 1. A method for applying a layer of fibers to a surface comprising the steps of: directing a stream of said fibers toward said surface; co & ing said directed fibers with a tacky inorganic binder during said step of directing such that said fibers adhere to one another and to said surface; and curing said coated fibers. 2. M9.thod according to Claim 1 wherein said fibers include refractory fibers. 3. Method according to Claim t further including the step of diluting said inorganic binder prior to said step of directing. 4. Method according to Claim l further includIng the step of comprising said binder coated fiber layer to a desired density prior to said step of curing. 5. Method according to Claim i wherein said sap of curing includes exposIng a face of said fiber layer opposite to said surface to a temperature of at least 350 F. 6. Method of Claim 1 wherein said step of coating said fibers occurs as said fibers are directed from a spray gun. 7. Method according to Claim l wherein said binder is sprayed into said fiber stream. 8. Method according tc Claim l wherein said binder includes a suspension of colloidal particles, the oxide of which will not act as a fluxing agent to alumina silica fibers at temperature above 1500 F 9. Method according to Claim 1 wherein said binder includes a phosphate compound and montmorillonite cls. 10. Method according to Claim 1 further Including the step of spraying saId binder onto said surface prior to said step of directing. ll. A method for producing a layer of fibers comprising the steps of: directing said fibers is a strea@ configuration: directIng a tacky inorganic binuer nto said stream configuration so as to coat said fibers with said binder causing said fibers to adhere to one another; and curing said coated fibers. 12. Method according to claim 1 further including the step of, prior to curing said coated fibers: directing a stream of partIculate material such as a metal oxide toward said coated fibers; and coating said particulate material with said binder during said step of directing such that said coated particulate material adheres to one another and to said coated fibers. 13. A refractory binder comprising: a phosphate matrix; and a tackifyin agent in intimate admixture with said phosphate matrix. 14. Binder according to Claim 13 wherein said tacgifying agent is montmorillonite clay. 15. Binder according to Claim 13 wherein said tackifying agent is bentonite clay. 16. Binder according to Claim 13 further including a fluxing agent. 17. Binder according to Claim 13 further including a metal oxide selected from the group consisting of alumina, magnesium or silica. 18. Binder according to Claim 16 wherein said fluxing agent is boric acid. 19. Binder according to Claim 13 further including a chromium compound. 20. Binder according to Claim 19 wherein said chromium compound is chromic oxide. 21. A refractory binder comprising by weight percent: chromium compound 1-2% phosphoric acid 75-85t hydrated alumina 1°-20N. tackifying agent '- 5% 22. A refractory binder according to Claim 21 further including, up to 5 by weight percent of a fluxing agent. 23. A refractory binder according to Claim 21 wherein said tackifying agent includes montmorillonite clay. 24. A refractory binder comprising: a suspension of colloidal particles the oxide of which will not act as a fluxing agent to alumina silica fibers at temperatures above '500 F; and a tackifylng agent in intinate admixture with the said suspension, 25. Binder according to Claim 24 wherein said colloidal suspension particles are selected from a group consisting of alumina, silica, or zirconia. 26. Binder according to Claim 24 whereIn said tackifying agent includes a montmorillonite clay. 27. Method for making a refractory binder comprising the steps of: stirring a phosphate - tacklfying agent mixture; heating said mixture to at least approximately 100 F; adding hydrated alumina to said mixture; and heating said hydrated alumina-phosphate-tackifying agent to at least approximately ;80 F. 28. Method according to Claim 22 further including the step of adding a chromium compound to said mixture. 29. Method according to Claim 27 further including the step of adding 2 fluting agent to said phosphate-tacklfylng mixture. 30. Method according to Claim 27 wherein said tackifying agent includes montmorillonite clay. 31. Method according to Claim 29 wherein said fluxing agent is boric acid. 32. Method for making a refractory binder comprising the step of reacting a colloidal suspension of particles selected from among the group consisting of alumina, silica or zirconia with a tackifying agent. 33. Method according to Claim 32 wherein said tackifying agent is montmorillonlte clay. 34. A refractory material comprii a plurality of refractory bers and a phosphate-tackifyinO agent mixture. 35. Material according to Claim 34 wherein said tackifying agent includes montmorillonite clay. 36. Material accordIng to ClaIm 34 wherein said mixture further includes a chromium compound. 37. Material according to Claim 34 wherein said mixture further includes a fluxing agent. 38. Material according to Claim 37 wherein said fluxing agent is boric acid. 39. Material according to Claim 34 wherein seid mixture further includes alumina. 40. A refractory material comprising: a plurality of refractory fibers; and a binder including: a suspension of colloidal particles the oxide of which will not act as a fluxing agent to said refractory fibers at temperatures above 15000F; and a tackifying agent in intimate admixture with said suspension. 41. Material according to Claim 40 wherein said colloidal suspension particles are selected from a group consisting of alumina, silica, or zirconia. 42. MaterIal according to Claim 40 wherein said tacklfying agent includes montmorillonite clay. 43. In a spray gun for directing a stream of moving material Including a feed line for confining said stream of moving material in a predetermined configuration and at least one outside spray nozzle located on said spray gun for directing a stream of binder onto the outside of said stream of moving material, the improvement comprising: at least one inside spray nozzle located within ai moving stream. 44. A spray gun comprising: a feed line for directing a stream of moving material in a predetermined path; a deflector located within said feed line for configuring said moving stream of material in an annular path; at least one spray nozzle connected to said spray gun outside of said annular path; and at least one spray nozzle located on said spray gun inside of said annular path.

Inventors: SMITH, WILLIAM HAHN
Applicants: MANVILLE CORPORATION
Application year: 1984
Main classification: F24D1
IPC codes: F27D1, C04B35, B05B7, C04B28, C04B30