PHOTOCOPOLYMERIZABLE COMPOSITIONS BASED ON EPOXY AND HYDROXYL-CONTAINING ORGANIC MATERIALS HAVING PRIMARY HYDROXYL CONTENT

Abstract: This invention is directed to photocopolymerizable com­ positions comprising an epoxide containing two or more epoxy groups, a poly (active hydrogen) organic compound having at least some primary hydroxyl content and a photoinitiator. The cured coating compositions exhibit fast cure rates, good water resistance and can have utility as automotive finishes, can finishes, appliance finishes, general metal finishes, printing inks, adhesives and the like.

Description: Brief Summary of the Invention Technical field 'This invention is directed in general to coating compositions and, in particular, to photocopolymerizable compositions comprising an epoxide containing two or more epoxy groups, a poly (active hydrogen) organic compound having at least some primary hydroxyl content and a photoinitiator. Background Art In the field of radiation curable coatings, it is well known that coating compositions containing cycloaliphatic epoxides and hydroxyl-containing materials can be radiation cured by the use of onium salts such as FC-508 available from the 3M Company and UVE-1014 available from General Electric Company. The onium salts form shelf-stable formulations with cycloaliphatic epoxides and hydroxyl-containing materials in an environment free of ultraviolet light irradiation. When such onium salts are irradiated with ultraviolet light, a cat ironic catalyst composition is formed that cures the formulation into a coating film. Many hydroxyl-containing materials are described in the art as being useful ingredients in radiation curable coatings. The particular hydroxyl-containing material selected as an ingredient in a radiation curable, epoxy-containing coating formulation can affect the cure rate of the coating formulation and also the properties of the cured film coating. Copending U. S. Patent Application Serial No. 369,835, filed April 19, 1982, discloses photocopolymerizable compositions comprising a cycloaliphatic epoxide, an alkylene oxide derived polyol having an average molecular weight of from about 2000 to about 4500, and a photoinitiator. These compositions are particularly suited for coating paper, wood, metal and plastic substrates. U. S. Patent 4,256,828 describes photocopolymerizable compositions which contain epoxides, organic material with hydroxyl functionality and a photosensitive aromatic sulfonium or iodonium salt of a halogen-containing complex ion. The organic material with hydroxyl functionality is described in the patent beginning at column 4, line 54 and extending through column 6, line 63. It is stated that the organic material contains two or more primary or secondary aliphatic hydroxyl groups (see column 5, lines 4-7). U. S. Patent 4,231,951 also describes photocopolymerizable compositions which contain cycloaliphatic epoxides, organic materials having hydroxyl functionality and a triarylsulfonium complex salt photoinitiator. The organic material with hydroxyl functionality is described in the patent beginning at column 3, line 67 and extending through column 5, line 47. It is stated that the organic material contains two or more primary or secondary aliphatic hydroxyl groups (see column 4, lines 18-21). U. S. Patent 4,173,476 describes photocopolymerizable compositions which contain epoxides, organic materials with hydroxyl functionality and a triarylsulfonium complex salt photoinitiator. The organic material with hydroxyl functionality is described in the patent beginning at column 3, line 62 and extending through column 5, line 42. It is stated that the organic material contains two or more primary or secondary aliphatic hydroxyl groups (see column 4, lines 13-16). U. S. Patent 4,218,531 describes the use of certain organic materials having non-aromatic carbon-carbon unsaturation in connection with photocopolymerizable compositions containing aromatic sulfonium complex salt photoinitiators in order to minimize or eliminate the odor of organosulfur reaction by-products. The photocopolymerizable compositions also contain epoxides and hydroxy-containing organic materials. The hydroxyl-containing organic materials are described in the patent beginning at column 3, line 16 and extending through column 5, line 25. It is stated that the organic material contains two or more primary or secondary aliphatic hydroxyl groups (see column 3, lines 36-39). It has been found as a result of the present invention that photocopolymerizable coating compositions based on epoxy and hydroxyl-containing organic materials, in which the hydroxyl-containing organic materials are poly (active hydrogen) organic compounds having at least some primary hydroxyl content, e.g., propylene oxide polyols capped with ethylene oxide, exhibit significantly higher cure rates in comparison with photocopolymerizable compositions containing hydroxyl-containing materials having no primary hydroxyl content, e.g., propylene oxide polyols not capped with ethylene oxide. The cured coating films of this invention also exhibit good water resistance with no thermal post cure and other highly desirable film properties as described more fully hereinbelow. Disclosure of the Invention The present invention is directed to photocopolymerizable compositions comprising an epoxide containing two or more epoxy groups, a poly (active hydrogen) organic compound having at least some primary hydroxyl content derived from an initiator, e.g. glycerol, and an alkylene oxide having the formula: EMI4.1 and end capped at least to a degree with an alkylene oxide having the formula: EMI4.2 or with a caprolactone having the formula EMI4.3 wherein R1 is individually hydrogen, alkyl, alkoxy, aryl, cycloalkyl, alkaryl or aralkyl having up to 12 carbon atoms, R2 is hydrogen or alkyl having from 1 to about 12 carbon atoms, R3 is alkyl having from 1 to about 12 carbon atoms, x is a D-13,815 value of from 0 to about 5 and y is a value of from o to about 6, and a photoinitiator. The invention is also directed to blend formulations comprising an epoxide containing two or more epoxy groups and a poly (active hydrogen) organic compound having at least some primary hydroxyl content as described above. The above compositions can optionally contain a reactive diluent such as a substituted cycloaliphatic monoepoxide, i.e., 4-vinyl cyclohexene monoepoxide, a surfactant, fillers, additives and an organic solvent where necessary. The photocopolymerizable coating compositions of the present invention based on epoxy and hydroxyl-containing organic materials, in which the hydroxyl-containing organic materials are poly (active hydrogen) organic compounds having at least some primary hydroxyl content as described above, e.g., propylene oxide polyols capped with ethylene oxide, exhibit significantly higher cure rates than photocopolymerizable compositions containing hydroxyl-containing materials having no primary hydroxyl content, e.g., propylene oxide polyols not capped with ethylene oxide. The cured coating films of this invention also exhibit good water resistance with no thermal post cure and other highly desirable film properties as described more fully hereinbelow. The cured coating films are particularly suited for coating paper, wood, metal and plastic substrates, in particular, automotive finishes, can finishes, appliance finishes, business machine finishes, coil coating, house siding, general metal finishing and the like. The invention is further directed to a process for preparing a cured film coating comprising: (1) mixing until homogeneous a photocopolymerizable composition comprising an epoxide containing two or more epoxy groups, a poly (active hydrogen) organic compound having at least some primary hydroxyl content derived from an initiator, e.g. glycerol, and an alkylene oxide having the formula: EMI6.1 and end capped at least to a degree with an alkylene oxide having the formula: : EMI6.2 or with a caprolactone having the formula EMI6.3 wherein R1 is individually hydrogen, alkyl, alkoxy, aryl, cycloalkyl, alkaryl or aralkyl having up to 12 carbon atoms, R2 is hydrogen or alkyl having from I to about 12 carbon atoms, R3 is alkyl having from 1 to about 12 carbon atoms, x is a value of from 0 to about 5 and y is a value of from o to about 6, and a photoinitiator; (2) applying the homogeneous photocopolymerizable composition as a film coating on a suitable surface or substrate; and (3) exposing the film coating to actinic irradiation at a wavelength within the ultraviolet and visible spectral regions or electron beam irradiation for a period of time sufficient to cure the film coating. The cured film coating prepared by the above described process is also part of this invention. In copending U.S. Patent Application Serial No. (D-13813), filed on an even date herewith, there is described photocopolymerizable compositions comprising an epoxide containing two or more epoxy groups, a poly(active hydrogen) organic compound, a photoinitiator, and, as a reactive diluent, a substituted cycloaliphatic monoepoxide. The photocopolymerizable compositions have desirably low viscosity and can be applied in a conventional manner such as roll coating, spray and the like and, after being cured to dry coating films, can have utility as automotive finishes, appliance finishes, general metal finishes and the like. Copending U.S. Patent Application Serial No. (D-13812), filed on an even date herewith, describes photocopolymerizable compositions comprising a poly(active hydrogen) organic compound, a photoinitiator and, as a reactive diluent, a substituted cycloaliphatic monoepoxide. The photocopolymerizable compositions have low viscosity and can be applied to suitable substrates by conventional methods and, after curing, provide excellent pressure sensitive and heat-activated adhesive coatings. In copending U.S. Patent Application Serial No. (D-13816), filed on an even date herewith, there is described photocopolymerizable compositions comprising an epoxide containing two or more epoxy groups, a polymer/poly (active hydrogen) organic compound and a photoinitiator. The cured coating compositions exhibit a clear appearance, good water resistance and can have utility as automotive finishes, appliance finishes, general metal finishing and the like. In copending U.S. Patent Application Serial No. (D-13799), filed on an even date herewith, there is described photocopolymerizable compositions comprising an epoxide containing two or more epoxy groups, a photoinitiator and, as a reactive diluent, a substituted cycloaliphatic monoepoxide. The photocopolymerizable compositions have desirably low viscosity and can be applied to a suitable substrate in a conventional manner such as roll coating, spray and the like. The cured coatings are suitable for use in a variety of applications in the fields of protective coatings and graphic arts. Copending U.S. Patent Application Serial No. (D-13814), filed on an even date herewith, describes photocopolymerizable compositions comprising a photoinitiator selected from diazonium salts, onium salts and mixtures thereof and, as a reactive diluent, a cycloaliphatic epoxide. The photocopolymerizable compositions have desirably low viscosity and can be applied to suitable substrates by conventional methods. Copending U.S. Patent Application Serial No. (D-13835), filed on an even date herewith, describes photocopolymerizable compositions comprising an epoxide containing two or more epoxy groups, a poly (active hydrogen) organic compound and a hydroxyl substituted cycloaliphatic monoepoxide. The photopolymerizable compositions can be cured into coatings which have improved water resistance. Detailed Description The epoxides which may be used herein contain two or more epoxy groups having the formula: EMI9.1 and have a viscosity of about 200, or higher, centipoise at 250C. The epoxy groups can be terminal epoxy groups or internal epoxy groups. The epoxides are primarily cycloaliphatic epoxides. These cycloaliphatic epoxide resins may be blended with minor amounts of glycidyl type epoxides, aliphatic epoxides, epoxy resol novolac resins, epoxy phenol novolac resins, polynuclear phenol-glycidyl ether-derived resins, aromatic and hetercyclic glycidyl amine resins, hydantoin epoxy resins, and the like, and mixtures thereof. These epoxides are well known in the art and many are commercially available. Suitable cycloaliphatic epoxide resins for purposes of this invention are those having an average of two or more epoxy groups per molecule. Illustrative of suitable cycloaliphatic epoxides are the following: FORMULA 1 Diepoxides of cycloaliphatic esters of dicarboxylic acids having the formula: EMI10.1 wherein R1 through R18, which can be the same or different, are hydrogen or alkyl radicals generally containing one to nine carbon atoms inclusive, and preferably containing one to three carbon atoms, inclusive, as for example methyl, ethyl, n-propyl, n-butyl, n-hexyl, 2-ethylhexyl, n-octyl, n-nonyl and the -like; R is a valence bond or a divalent hydrocarbon radical generally containing one to twenty carbon atoms, inclusive, and preferably, containing four to six carbon atoms, inclusive, as for example, alkylene radicals, such as trimethylene, tetramethylene, pentamethylene, hexamethylene, 2-ethylhexamethylene, octamethylene, nonamethylene, hexadecamethylene, and the like; cycloaliphatic radicals, such as 1±4-cyclohexane, 1,3-cyclohexane, 1,2-cyclohexane, and the like. Particularly desirable epoxides, falling within the scope of Formula I, are those wherein R1 through R18 are hydrogen and R is alkylene containing four to six carbon atoms. Among specific diepoxides of cycloaliphatic esters of dicarboxylic acids are the following: bis(3,4-epoxycyclohexylmethyl)oxalate, bis(3,4-epoxycyclohexylmethyl)adipate, bis(3,4-epoxy-6-methylcyclohexylmethyl) adipate, bis(3,4-epoxycyclohexylmethyl)pimelate, and the like. Other suitable compounds are described in, for example, U.S. Patent No. 2,750,395. FORMULA II A 3, 4-epoxycyclohexylmethyl-3, 4-epoxycyclo- hexane carboxylate having the formula: EMI11.1 wherein R1 through R18 which can be the same or different are as defined for R1 through R18 in Formula I. Particularly desirable compounds are those wherein R1 through R18 are hydrogen. Among specific compounds falling within the scope of Formula II are the following: 3,4-epoxycyclohexylmethyl-3,4-epoxycyclohexane carboxylate; 3,4-epoxy-1-methylcyclohexylmethyl-3,4-epoxy-1- methylcyclohexane carboxylate; 6-methyl-3,4-epoxy cyclohexylmethyl-6-methyl-3, 4-epoxycyclohexane carboxylate; 3,4-epoxy-3-methylcyclohexylmethyl3,4-epoxy-3-methylcyclohexane carboxylate; 3,4 epoxy-5-methylcyclohexylmethyl-3, 4-epoxy-S-methyl- cyclohexane carboxylate. Other suitable compounds are described in, for example, U.S. Patent No. 2,890,194. FORMULA III Diepoxides having the formula: EMI12.1 wherein the R single and double primes, which can be the same or different, are monovalent substituents such as hydrogen, halogen, i.e. chlorine, bromine, iodine or fluorine, or monovalent hydrocarbon radicals, or radicals as further defined in U.S. Patent No. 3,318,822. Particularly, desirable compounds are those wherein all the R's are hydrogen. Other suitable cycloaliphatic epoxides are the following: EMI12.2 and the like. The preferred cycloaliphatic epoxides are the following: 3,4-Epoxycyclohexylmethyl-3,4-Epoxy cyclohexane carboxylate EMI13.1 Bis(3,4-Epoxycyclohexylmethyl)adipate EMI13.2 2-(3,4-Epoxycyclohexyl-5,5-spiro-3,4- epoxy)cyclohexane-me.ta-dioxane EMI13.3 or mixtures thereof. Epoxides with six membered ring structures may also be used, such as diglycidyl esters of phthalic acid, partially hydrogenated phthalic acid or fully hydrogenated phthalic acid, the diglycidyl esters of hexahydrophthalic acids being preferred. A representaive diglycidyl ester of phthalic acid is the following: EMI13.4 The glycidyl-type epoxides are preferably diglycidyl ethers of bisphenol A which are derived from bisphenol A and epichlorohydrin and have the following formula: EMI14.1 The cresol-novolac epoxy resins are multifunctional, solid polymers characterized by low ionic and hydrolyzable chlorine impurities, high chemical resistance, and thermal performance. The epoxy phenol novolac resins are generally of the following formula: EMI14.2 The polynuclear phenol-glycidyl etherderived resins are generally of the formula: EMI15.1 Among the aromatic and heterocyclic glycidyl amine resins which may be included herein are the following: tetraglycidylmethylenedianiline derived resins of the following formula: EMI15.2 Triglycidyl-p-aminophenol derived resins, triazine based resins and hydantoin epoxy resins of the formula: : EMI15.3 R' = CH3 It is of course understood by those skilled in the art that when a photoinitator is used, only minor amounts of basic organic nitrogen-containing epoxide compounds may be used so as not to interfere with the photocopolymerization reaction The concentration of the epoxides in the photocopolymerizable and blend compositions of this invention can range from about 1 to about 95 weight percent, preferably from 25 to 90 weight percent, and most preferably from 50 to 80 weight percent of the total weight of the coating composition depending upon the desired properties in the cured compositions. The ratio of the equivalent weight of epoxide to the total hydroxyl equivalent weight of the poly (active hydrogen) organic compound having at least some primary hydroxyl content can range from about 120:1 to about 1:1, preferably from 110:1 to about 5:1, and most preferably from about 100:1 to about 10:1 depending upon the properties desired in the cured compositions. The preferred epoxides for use in the coating compositions of this invention are described in copending U.S. Patent Application Serial No. (D-13799), filed on an even date herewith. The poly (active hydrogen) organic compound having at least some primary hydroxyl content that is blended with the epoxide containing two or more epoxy groups to produce the coating compositions of this invention includes any compatible organic compound containing two or more active hydrogen atoms per molecule and containing at least some primary hydroxyl content. The preferred poly (active hydrogen) organic compounds having at least some primary hydroxyl content can be derived from an initiator, e.g., glycerol, and an alkylene oxide having the formula: EMI17.1 and end capped at least to a degree with an alkylene oxide having the formula: EMI17.2 or with a caprolactone having the formula EMI17.3 wherein RÚ is individually hydrogen, alkyl, alkoxy, aryl, cycloalkyl, alkaryl or aralkyl having up to 12 carbon atoms, Rê is hydrogen or alkyl having from 1 to about 12 carbon atoms', R3 is alkyl having from 1 to about 12 carbon atoms, x is a value of from 0 to about 5 and y is a value of from 0 to about 6. The poly (active hydrogen) organic compounds are well known to those skilled in the art and include, for example, propylene oxide polyols having at least some primary hydroxyl content and the like. Substantially any of the organic polyols having at least some primary hydroxyl content previously used in the art to make coating compositions can be used and are preferred as the poly (active hydrogen) organic compounds in this invention. Illustrative of the organic polyols having at least some primary hydroxyl content useful in producing coating compositions in accordance with this invention are the ethylene oxide capped or caprolactone capped polyhydroxyalkanes, polyoxyalkylene polyols, and the like. Among the organic polyols having primary hydroxyl content which can be employed are those selected from one or more of the following classes of compositions, alone or in admixture, known to those skilled in the art: (a) Alkylene oxide adducts of polyhydroxyalkanes having at least some primary hydroxyl content; (b) Alkylene oxide adducts of non-reducing sugars and sugar derivatives having at least some primary hydroxyl content; (c) Alkylene oxide adducts of phosphorus and polyphosphorus acids having at least some primary hydroxyl content; (d) Alkylene oxide adducts of polyphenols having at least some primary hydroxyl content; and (e) The polyols from natural oils such as castor oil, and the like having at least some primary hydroxyl content. Illustrative alkylene oxide adducts of polyhydroxyalkages (initiator) include, among others, the alkylene oxide adducts of ethylene glycol, propylene glycol, 1,3-dihydroxypropane, 1, 3-dihydroxybutane, 1, 4-dihydroxybutane, 1,4-, 1,5-, and 1,6-dihydroxyhexane, 1,2-, 1,3-, 1,4-, 1,6-, and 1,8-dihydroxyoctane, 1,10-dihydroxydecane, glycerol, 1,2, 4-trihydroxybutane, 1,2, 6-trihydroxybexane, l,l,l-trimethylolethane, 1,1,1-trimethylolpropane, pentaerythritol, polycaprolaet'One, xylitol, arabitol, sorbitol, mannitol, and the like. A preferred class of alkylene oxide adducts of polyhydroxyalkanes are the propylene oxide, butylene oxide, or mixtures thereof, adducts of trihydroxyalkanes. The alkylene oxide adducts of the polyhydroxyalkanes can be capped by conventional methods with ethylene oxide or caprolactone to provide primary hydroxyl content. A further class of organic polyols which can be employed are the alkylene oxide adducts of the non-reducing sugars (initiator), wherein the alkylene oxides have from 2 to 4 carbon atoms. Among the non-reducing sugars and sugar derivatives contemplated are sucrose, alkyl glycosides such as methyl glucoside, ethyl glucoside, and the like, glycol glycosides such as ethylene glycol glucoside, propylene glycol glucoside, glycerol glucoside, 1,2,6-hexanetriol glucoside, and the like, as well as the alkylene oxide adducts of the alkyl glycosides as set forth in U. S. 3,073,788. The alkylene oxide adducts of the non-reducing sugars and sugar derivatives can be capped by conventional methods with ethylene oxide or caprolactone to provide primary hydroxyl content. The alkylene oxide deducts of phosphorus and polyphosphorus acids (initiators) are another useful class of organic polyols. Ethylene oxide, 1,2-epoxypropane, the epoxybutanes, 3-chloro1,2-epoxypropane and the like are preferred alkylene oxides. Phosphoric acid, phosphorus acid, the polyphosphoric acids such as tripolyphosphoric acid, the polymetaphosphoric acids, and the like are desirable for use in this connection. The alkylene oxide adducts of the phosphorus and polyphosphorus acids can be capped by conventional methods with ethylene oxide or caprolactone to provide primary hydroxyl content. A still further useful class of organic polyols is the polyphenols (initiator), and preferably the alkylene oxide adducts thereof wherein the alkylene oxides have from 2 to 4 carbon atoms. Among the polyphenols which are contemplated are, for example, bisphenol A, bisphenol F, condensation products of phenol and formaldehyde, the novolac resins, condensation products of various phenolic compounds and acrolein; the simplest member of this class being the 1,1,3-trisfhydroxphenyl) propanes, condensation products of various phenolic compounds and glyoxal, glutaraldehyde, and other dialdehydes, the simplest members of this class being the 1,1, 2,2-tetrakis (hydroxyphenol) ethanes and the like. The alkylene oxide adducts of polyphenols can be capped by conventional methods with ethylene oxide or caprolactone to provide primary hydroxyl content. The alkylene oxide adducts of various initiators described above can include poly (oxypropylene-oxyethylene) polyols; however, desirably the oxyethylene content should comprise less than 60 percent of the total, preferably less than 50 percent of the total and most preferably less than 30 percent of the total weight of the polyol. The ethylene oxide can be incorporated in any fashion along the polymer chain. Stated another way, the ethylene oxide can be incorporated either in internal blocks, as terminal blocks, or may be randomly distributed along the polymer chain provided the poly (oxypropylene-oxyethylene) polyols have at least some primary hydroxyl content. As is well known in the art, the polyols that are most preferred herein contain varying small amounts of unsaturation. Unsaturation in itself does not affect in any adverse way the formation of the coating compositions in accordance with the present invention. The organic polyols described hereinabove can have hydroxyl numbers which vary over a wide range. In general, the hydroxyl numbers of the above described polyols employed in this invention can range from about 15, and lower, to about 900, and higher. The hydroxyl number is defined as the number of milligrams of potassium hydroxide required for the complete neutralization of the fully phthalated derivative prepared from 1 gram of polyol. The hydroxyl number can also be defined by the equation: OH = 56.1 x 1000 x f m.w. where OB = hydroxyl number of the polyol; f = functionality, that is, average number of hydroxyl groups per molecule of polyol; and m.w. - molecular weight of the polyol. The organic polyols described hereinabove can be prepared by conventional methods and are commercially available from a number of manufacturers. Preferred commercial polyols having at least some primary hydroxyl content include among others a propylene oxide polyol capped with ethylene oxide available from Union Carbide Corporation as E-480, a propylene oxide polyol capped with ethylene oxide commercially available from Union Carbide Corporation as NIAX Polyol 11-34, a propylene oxide polyol capped with ethylene oxide commercially available from Union Carbide Corporation as E-474, and a propylene oxide polyol capped with ethylene oxide commercially available from Union Carbide Corporation as NIAX Polyol 11-27. A most preferred ethylene oxide capped polyoxyalkylene derived polyol suitable for use in this invention has a molecular weight of from about 200 or lower about 10,000 or higher and has the following formula: EMI22.1 wherein R4 is alkyl having from 3 to about 12 carbon atoms, preferably 3 carbon atoms, a has a value of from 0 to about 150, b has a value of from 0 to about 40, d has a value of from I to about 150 and e has a value of from 1 to about 40. It is appreciated that the propylene oxide adduct is end capped at least to a degree with ethylene oxide. As is well known in the art, the organic polyols preferred herein can contain varying amounts of end capping either with an alkylene oxide having the formula described above, e.g., ethylene oxide, or with a caprolactone having the formula described above, e.g., epsilon-caprolactone. The organic polyols employed in the coating compositions of this invention contain at least some primary hydroxyl content. While epsilon-caprolactone is the preferred lactone, other lactones such as delta-valerolactone, zeta-enantholactone and the like including substituted derivatives thereof that yield primary hydroxyl groups when ring opened with an active hydrogen can also be employed in the coating compositions of this invention. The concentration of the poly (active hydrogen) organic compound having at least some primary hydroxyl content in the photocopolymerizable and blend compositions of this. invention can range from about 1 to about 60 weight percent, preferably from 5 to 40 weight percent, and most preferably from 10 to 30 weight percent of the total weight of the coating composition depending upon the properties desired in the cured compositions. The ratio of the equivalent weight of epoxide to the total hydroxyl equivalent weight of organic polyol can range from about 120:1 to about 1:1, preferably from 110:1 to about 5:1, and most preferably from about 100:1 to about 10:1 depending upon the equivalent weight of the polyol and the properties desired in the cured compositions. The poly (active hydrogen) organic compounds having at least some primary hydroxyl content utilized in the coating compositions of this invention can be mixtures or blends of at least two different poly (active hydrogen) organic compounds having at least some primary hydroxyl content or mixtures or ,blends of a poly (active hydrogen) organic compound having at least some primary hydroxyl content with at least one other poly(active hydrogen) organic compound which does not necessarily have primary hydroxyl content. Suitable poly(active hydrogen) organic compounds which can be mixed or blended with the poly (active hydrogen) organic compound having at least some primary hydroxyl content include polyester and polyether polyols having at least some primary hydroxyl content as described above, polyether polyols as described above but having no primary hydroxyl content, polyester polyols, polycaprolactone polyols, acrylic and vinyl polyols, polymer/polyols and the like. It is appreciated that the suitable polytactive hydrogen) organic compounds which can be blended or mixed with the poly(active hydrogen) organic compound having at least some primary hydroxyl content should be present in minor amounts in the blend or mixture compositions so as to not negate the benefits described hereinabove of the poly (active hydrogen) organic compound having at least some primary hydroxyl content employed in the coating compositions of this invention. Other mixtures or blends may similarly be used if desired. The suitable blended or mixed poly(active hydrogen) organic compounds should be present in amounts less than 50 weight percent, preferably less than 25 weight percent, of the total poly (active hydrogen) organic compound concentration in the coating compositions. The preferred classes of suitable poly(active hydrogen) organic compounds which can be blended or mixed with the poly(active hydrogen) organic compound having at least some primary hydroxyl content and employed in minor amounts in the coating compositions of this invention are the polycoprolactone polyols such as TONE-0200 and TONE-0305 commercially available from Union Carbide Corporation, the dihydroxy functional polytetramethylene oxide polyols such as Polymeg 650, 1000 and 2000 commercially available from Quaker Oats Company, the polymer/polyols such as NIAX Polymer Polyol 31-23 and 34-28 commercially available from Union Carbide Corpo.ration, and of course the ethylene oxide and propylene oxide adducts including ethylene glycol, diethylene glycol, the poly (oxyethylene) glycols, the poly (oxypropylene) glycols,.triols and higher functionality polyols such as LHT-67, LHT-112 and LG-56 commercially available from Union Carbide Corporation. These polyols also include poly(oxypropylene-oxyethylene) polyols; however, desirably, the oxyethylene content should comprise less than 80 percent of the total and preferably less than 60 percent. The ethylene oxide when used can be incorporated as internal blocks along the polymer chain. As is well known in the art, the polyols that are preferred herein contain varying small amounts of unsaturation. Unsaturation in itself does not affect in any adverse way the formation of the coating compositions in accordance with the present invention. Other preferred representative examples of suitable poly(active hydrogen) organic compounds which can be blended or mixed with the poly(active hydrogen) organic compound having at least some primary hydroxyl content and employed in minor amounts in the coating compositions of this invention include copolymers of hydroxypropyl and hydroxyethyl acrylates and methacrylates with other free radical-polymerizable monomers such as acrylate esters, vinyl halides, vinyl acetate, or styrene; copolymers containing pendent hydroxy groups formed by hydrolysis or partial hydrolysis of vinyl acetate copolymers, polyvinylacetal resins containing pendant hydroxyl groups; modified cellulose polymers such as hydroxyethylated and hydroxypropylated cellulose; hydroxy terminated polyesters and hydroxy terminated polyalkadienes. The polyester polyols are the reaction products of polyfunctional organic carboxylic acids and polyhydric alcohols and include, for example, poly(hexamethylene adipate), polytethylene adipate), poly(butylene adipate) and the like. Many of these organic polyols can be prepared by conventional methods and are commercially available from a number of manufacturers such as polyvinylacetal resins commercially available from Monsanto Chemical Company as Butvar B-72A, B-73, B-76, B-90 and B-98 and as Formvar 7/70, 12/85, 7/95S, 7/95E, 15/95S and 15/95E; and aliphatic polyester diol commercially available from Rohm and Haas as Paraplex U-148; saturated polyester polyols commercially available form Mobay Chemical Company as Multron R-2, R-12A, R-16, Rubs, R-38, R-68 and R-74; a hydroxypropylated cellulose having an equivalent weight of approximately 100 commercially available from Hercules, Inc. as Klucel E, and a cellulose acetate butyrate ester having a hydroxyl equivalent weight of approximately 400 commercially available from Eastman Kodak as Alcohol Soluble Butyrate. The photo initiator suitable for use in the coating compositions of this invention may be any one of the well known photoinitiators such as described in, for example, U.S. Patents 4,231,951; 4,256,828; 4,138,255 and 4,058,401 which patents are incorporated herein by reference. Preferred photoinitiators include triarylsulfonium complex salts as described in U.S. Patent 4,231,951, aromatic sulfonium or iodonium salts of halogen-containing complex ions as described in U.S. Patent 4,256,828; aromatic onium salts of Group VIa elements as described in U.S. Patents 4,058,401 and 4,138,255; aromatic onium salts of Group Va elements as described in U.S. Patent 4,069,055. Such salts are commercially available as FC-508 and FC-509 (available from Minnesota Mining and Manufacturing company), and as UVE-1014 (available from General Electric Company). Other preferred photo initiators for use in the coating compositions of this invention are described more fully in copending U.S. Patent Application Serial No. (D-13814), filed on an even date herewith. The photoinitiators are used in conventional amounts such as from about 0.1 to 30 parts by weight per 100 parts by weight of the combination of- epoxide and the poly(active hydrogen) organic compound having at least some primary hydroxyl content. The photocopolymerizable coating compositions of this invention may optionally include a substituted cycloaliphatic monoepoxide as a reactive diluent therein. The use of a substituted cycloaliphatic monoepoxide as a reactive diluent in photocopolymerizable compositions based on epoxy and hydroxyl containing organic materials is more fully described in copending U.S. Patent Application Serial No. (D-13,813), filed on an even date herewith. The substituted cycloaliphatic monoepoxide can be substituted with alkyl of 1 to 9 carbon atoms, halogen, oxygen, ether, ester or vinyl radicals. Preferably, the substituted cycloaliphatic monoepoxide is vinyl substituted cycloaliphatic monoepoxide and is preferably selected from one or more of the following: (1) 4-vinyl cyclohexene monoepoxide having the formula: EMI28.1 (2) norbornene monoepoxide having the formula: EMI28.2 (3) limonene monoepoxide having the formula: EMI28.3 The substituted cycloaliphatic monoepoxide acts as a reactive diluent that cures into the final coating product, has a marked effect in lowering viscosity, is not volatilized during the radiation cure operation and does not retard the curing rate. The substituted cycloaliphatic monoepoxide can be used in the coating compositions in amounts of from about 0.1 to about 95, preferably from about 1 to about 60, and most preferably, from about 3 to about 30 weight percent. The coating compositions may preferably include additives in conventional quantities such as oils, particularly silicone oil, surfactants such as silicone alkylene oxide copolymers, e.g., L-5410 commercially available from Union Carbide corporation, silicone oil containing aliphatic expoxide groups, fluorocarbon surfactants such as FC-171 commercially available from the 3M Company and FC-430 also commercially available from the 3M Company; low molecular weight alcohols such as RJ-100 commercially available from Monsanto Chemical Company; cellosolves, such as butyl CELLOSOLVE commercially available from Union Carbide Corporation; carbitols such as butyl CARBITOL; diethyleneglycol; low molecular weight hydroxyl-containing vinyl polymers such as UCAR .Solution Vinyl VYES commercially available from Union Carbide Corporation; glycidyl ether monomers of the formula-: EMI29.1 wherein R11 is alkyl or aryl and n is an integer of 1 to 6. Examples are glycidyl ethers of polyhydric phenols obtained by reacting a polyhydric phenol with an excess of chlorohydrin such as epichlorohydrin. Further examples of this type are described in, for example, U.S. Patent 3,018,262; alpha oleo in expoxides; epoxy novolaks, and the like. If desired, one may also include in the coating compositions various conventional non-basic fillers (e.g., silica, talc, glass beads or bubbles, clays, powdered metal such as aluminum, zinc oxide, etc.) up to about 50% by volume or more, viscosity modifiers, rubbers, tackifying agents, pigments, and so forth. The particular additives or fillers selected are of no consequence to the basic invention. In preparing the coating compositions, the ingredients are mixed by conventional procedures used in the production of inks, paints and coating compositions. These procedures are so well known to those skilled in the art that they d6 not require further discussion here. However, it should be noted that when the photoinitiator is incorporated into the coating composition, it is necessary that the curable coating formulation be mixed or blended under "safe light" such as a yellow light source to obviate or minimize photopolymerization. The coating compositions can also contain an organic solvent as an optional component. Any of the conventional solvents used in the coatings industry can be used at a concentration preferably below 30 weight percent of the total weight of the coating composition. Suitable solvents are acetone, methylene chloride and any solvent that does not react appreciably with the epoxide containing two or more epoxy groups and the photoinitiator. While larger amounts of solvent could conceivably be used, the use of larger amounts would negate the benefits of radiation curable coatings which are considered to be essentially 100% solids coatin systems. The solvents are generally added in the small amounts indicated to improve flowability during application of the coating composition to the substrate The curable coating composvtions of this invention are applied to a suitable surface or substrate by conventional means suc 1 as roll coating or spray. Curing or photopolymeri.;ltion of the coating compositions occurs on exposure of the compositions to any source of radiation emitting actinic radiation at a wavelength within the ultraviolet and visible spectral regions. Suitable sources of radiation include mercury, xenon, carbon arc and tungsten filament lamps, sunlight, etc. Exposures may be from less than about 1 second to 10 minutes or more depending upon the amounts of particular polymerizable materials and photoinitiator being utilized and depending upon the radiation source and distance from the source and the thickness of the coating to be cured. The compositions may also be polymerized by exposure to electron beam irradiation. Generally speaking the dosage necessary is from less than 1 megarad to 100 megarad or more. Generally speaking the rate of polymerization increases with increasing amounts of photoinitiator at a given light exposure or irradiation. The rate of polymerization also increases with increasing light intensity or electron dosage. The curing or photopolymerization of the coating composition is a triggered reaction. Once the degradation of the photoinitiator to a cationic catalyst has began by exposure to a radiation source, the curing or photopolymerization reaction proceeds and will continue after the radiation source is removed. The use of thermal energy during or after exposure to a radiation source, i.e., post cure thermally, will generally accelerate the curing reaction, and even a moderate increase in temperature may greatly accelerate cure rate. The photocopolymerizable compositions of this invention can be useful as automotive finishes, can finishes, appliance finishes, business machine finishes, coil coating, house siding finishes, general metal finishes and the like. The compositions can also be used as adhesives, printing inks, casting and molding compounds, potting and encapsulating compounds, caulking and sealing compounds, impregnating and coating compounds and the like. The photocopolymerizable compositions are particularly suitable in a variety of applications in the fields of protective coatings and graphic arts due to their superior water resistance, impact resistance, abrasion-resistance and adhesion to rigid, resilient and flexible substrates such as metal, plastic, rubber, glass, paper, wood, and ceramics. The coating compositions were evaluated according to the following procedures: Solvent Resistance (double acetone rubs): a measure of the resistance of the cured film to attack by acetone in which a film coating surface was rubbed with an acetone soaked cheesecloth back and forth with hand pressure A rub back and forth with hand pressure over the film coating surface with the acetone soaked cheesecloth was designated as one Double acetone rub". The effect that a certain number of double acetone rubs had on the film coating surface was reported by a number in parenthesis following the number of double acetone rubs. The rating system for evaluating acetone resistance for a given.number of double acetone rubs was as follows: Number in Parenthesis After Number of Rubs (1) No change in coating appearance (2) Scratched surface (3) Dulled, marred, some coating removed (4) Breaks in coating appearance (5) About one-half of the coating removed. Pencil Hardness: pencil leads of increasing hardness values were forced against the film coating surface in a precisely defined manner as described in ASTM-D-3363-74 until one pencil lead marred the surface of the film coating. The surface hardness was considered as the hardest pencil grade which just failed to mar the film coating surface. The pencil leads in order of softest to hardest were reported as follows: 6B, 5B, 4B, 3B, 2B, B, HB, F, H, 2H, 3H, 4H, 5H, 6H, 7H, 8H, and 9H. Crosshatch Adhesion; a lattice pattern with ten cuts in each direction was made in the coating film to the substrate and pressure-sensitive adhesive tape was applied over the lattice pattern and then removed. The adhesion was evaluated by comparison with descriptions and illustrations as more fully detailed in ASTM D3359-78. Forward Impact Resistance (Gardner Impact): a measure of the ability of a cured film coating to resist rupture from a falling weight. A Gardner Impact Tester Model IG-1120 using an eight pound dart was used to test film coatings cast and cured on steel panels. The dart was raised to a given height in inches and dropped onto the coated side of the coated steel panel. The inches times pounds, designated inch-pounds, absorbed by the film without rupturing was recorded as the films forward impact resistance. Reverse Impact Resistance (Gardner Impact): a measure of the ability of a cured film coating to resist rupture from a falling weight. A Gardner Impact Tester Model IG-1120 using an eight pound dart was used to test film coatings cast and cured on steel panels. The dart was raised to a given height in inches and dropped onto the uncoated side of the coated steel panel. The inches times pounds, designated inch-pounds, absorbed by the film without rupturing was recorded as the films reverse impact resistance. Moisture Resistance: the cured film coating was immersed in water for a specified period of time and at a specified temperature. After removal from the water, the hydrolytic resistance of the cured film coating was determined by the pencil hardness test and the crosshatch adhesion test described hereinabove. Results obtained were compared with the results of identical tests performed on cured film coatings not immersed in water to determine moisture resistance. The following examples are illustrative of the present invention and are not intended as a limitation upon the scope thereof. As used in the examples appearing hereinafter, the following designations, terms and abbreviations have the indicated meanings: cps centipoise in./lbs. inch/pounds OC Centigrade degree OF Fahrenheit degree Hr. hour percent by weight unless otherwise specified Numbered Examples examples which illustrate this invention Lettered Examples comparative examples which do not illustrate this invention Epoxy/OH Eq. Wt. Ratio The ratio of the equivalent weight of expoxide to the total hydroxyl equivalent weight of polyol. Epoxide I 3,4-Epoxycyclohexylmethyl -3,4- epoxycyclohexane carboxylate commercially available from Union Carbide Corporation as ERL-4221. Polyol I A propylene oxide polyol not capped with ethylene oxide having an average equivalent weight of 1385, an average hydroxyl number of 40.5 and commercially available from Union Carbide Corporation as LHT-42. Polyol II A propylene oxide polyol capped with ethylene oxide having an average equivalent weight of 1439, and average hydroxyl number of 39 and available from Union Carbide Corporation as E-480. Polyol III A propylene oxide polyol capped with ethylene oxide having an average equivalent weight of 1603, an average hydroxyl number of 35 and commercially available from Union Carbide Corporation as Niax Polyol 11-34. Polyol IV A propylene oxide polyol not capped with ethylene oxide having an average equivalent weight 1996, an average hydroxyl number of 28.1 and commercially available from Union Carbide Corporation as LHT-28, Polyol V A propylene oxide polyol capped with ethylene oxide having an average equivalent weight of 2004, an average hydroxyl number of 28 and commercially available from Union Carbide Corporation as E-474. Polyol VI A propylene oxide polyol capped with ethylene oxide having an average equivalent weight of 2078, an average hydroxyl number of 27 and commercially available from Union Carbide Corporation as NIAX Polyol 11-27. Reactive Diluent I 4-Vinyl cyclohexene monoepoxide Photoinitiator I A solution of a triarylsulfonium hexafluorophosphate having a specific gravity of 1.33 at 230C, a Brookfield viscosity of 4G,000-60,000 centipoise (+4 spindle at 6 rpm, 230C) and commercially available from the 3M Company as FC-508. Photoinitiator II A solution of a triarylsulfonium hexafluoro antimony salt having a specific gravity of 1.39, a Brookfield viscosity of 74 centipoise at 250C and commercially available from General Electric Company as UVE-1014. Surfactant I A silicone composition having the following structure EMI37.1 and commercially available from Union Carbide Corporation as L-5410. Examples 1 through 4 and Comparative Examples A through D Into brown glass bottles under a yellow light source was added Epoxide I, Polyol I, Polyol II, Polyol IV, Polyol V, Photoinitiator I and Surfactant I in the amounts specified for each example and comparative example in Table I below. The contents in the bottles were thoroughly blended until homogeneous by simple stirring at ambient temperature. The mole percent of monol, diol, and triol and the percent of ethylene oxide capping for Polyol I, Polyol II, Polyol IV and Polyol V are also given in Table I. TABLE I Example A B 1 2 Ingredients, grams Epoxide I 73.95 71.43 73.9 70.7 Polyol I 0 24.07 0 0 Polyol II 0 0 0 24.8 Polyol IV 21.55 0 0 0 Polyol V O 0 21.6 0 Photoinitiator 1 4.0 4.0 4.0 4.0 Surfactant I 0.5 0.5 0.5 0.5 Polyol Properties Polyol Identification IV I V II Mole percent Monol 40. 34 27.1 18.15 12.8 Diol 24. 23 20.5 13.48 7.5 Triol 35.43 52.3 68.40 79.6 % Ethylene Oxide 0 0 15 17 Capping The blended formulations were then applied to Bonderite 37 treated steel panels using a Number 20 wire-wound rod and cured with one pass under a 100 watt per inch, medium pressure, mercury lamp ultraviolet light source at 30 feet per minute. One Bonderite 37R treated steel panel coated with the specified blended formulation was prepared for each example and comparative example. The cured coating on the Bonderite 37R treated steel panels of Examples 3 and 4 was prepared from the blended formulation of Examples 1 and 2 respectively. The cured coating on the Bonderite 37R treated steel panels of Comparative Examples C and D was prepared from the blended formulation of Comparative Examples A and B respectively. The thickness of the coatings vared from about 0.8 mils to about 0.9 mils. The cured coatings were tack free when warm immediately after ultraviolet light irradiation. The cured coatings designated in Table II below were not post cured thermally but were allowed to stand 24 hours at ambient temperature before testing for the properties designated in Table II. The results of the testing are given in Table II. TABLE II Example C D 3 4 Properties Double Acetone Rubs 30(4) 20(4) 100(3) 85(4) Pencil Hardness 4B 2B F H % Crosshatch Adhesion 100 100 100 100 Gardner Impact, in/lbs. Forward 15 2320 2320 > 320 Reverse C5 < 5 ?320 > 320 300 Moisture Resistance 24 Hr. Water Immersion at Room Temperature Pencil Hardness * 4 5B B F % Crosshatch Adhesion * 0 100 20 3 Hr. Water Immersion at 1300F Pencil Hardness * < SB B 2B % Crosshatch Adhesion * 0 100 15 *Cured coating quality too poor to test, Table II shows that cured coatings employing propylene oxide polyols capped with ethylene oxide, e.g., Polyol II and Polyol V, have significantly higher cure speeds (rate of cure) and improved properties over cured coatings employing propylene oxide polyols not capped with ethylene oxide as disclosed in copending U.S. Patent Application Serial No. 369,835, filed April 19, 1982, e.g., Polyol I and Polyol IV. The solvent resistance (double acetone rubs) is indicative of the enhanced cure rate in that the larger the number of rubs, the higher the degree of polymerization (cure) attained by the coating system. Another advantage of the cured coating compositions of this invention over the cured coatings of the above copending application is the achievement of water resistance without employing a thermal post cure after ultraviolet irradiation of the coating, e.g., see Example 3 and Comparative Example C. The hardness of the cured coatings of Examples 3 an 4 is also markedly higher than the hardness of the cured coatings of Comparative Examples C and D. It is believed that the primary hydroxyl end groups of the ethylene oxide capped propylene oxide polyols are responsible for the enhanced reaction rate observed in coating systems employing said polyols as compared with coating systems employing conventional propylene oxide polyols having secondary hydroxyl groups. Examples 5 through 76 Into brown glass bottles under a yellow light source was added Epoxide I, Polyol III, Polyol V, Polyol VI, Reactive Diluent I, Photoinitiator I and Surfactant I in the amounts specified for each example in Table III below. The contents in the bottles were thoroughly blended until homogeneous by simple stirring at ambient temperature. The viscosity of the resulting blends prepared in each example was then determined with a Brookfield viscometer at 310C for Examples 5 through 10 and Examples 23 and 24, at 23.90 for Examples 11 through 16 and Examples 25 and 26, and at 28.90C for Examples 17 through 22 and Examples 27 and 28. The viscosity results are given in Table III. TABLE III Example 5 6 7 8 9 Ingredients, grams Epoxide I 79.7 73.6 69.6 63.8 73.6 Polyol III 0 0 0 0 0 Polyol V 0 0 0 0 0 Polyol VI 15.8 21.9 25.9 31.6 21.9 Reactant Diluent I 0 0 0 0 0 Photoinitiator I 4.0 4.0 4.0 4.0 0 Photoinitiator II 0 0 0 0 4.0 Surfactant I 0.5 0.5 0.5 0.5 0.5 Properties Epoxy/OH Eq. Wt. Ratio 75 50 40 30 50 Viscosity, centipoise 590 662 704 762 600 TABLE III (Cont.) Example 10 11 12 13 14 Ingredients, grams Epoxide I 63.8 77.6 74.1 69.0 60.6 Polyol III 0 17.9 21.4 26.5 34.9 Polyol V 0 0 0 o 0 Polyol VI 31.6 0 0 0 0 Reactive Diluent I 0 0 0 0 0 TABLE III (Cont.) Example 10 11 12 13 14 Photoinitiator I 0 4.0 4.0 4.0 4.0 Photoinitiator II 4.0 0 0 0 0 Surfactant I 0.5 0.5 0.5 0.5 0.5 Properties Epoxy/OH Eq. Wt. Ratio 30 50 40 30 20 Viscosity, centipoise 692 714 740 762 826 TABLE III (Cont.) Example 15 16 17 18 19 Ingredients, grams Epoxide I 74.1 60.6 79.9 73.9 69.9 Polyol III 21.4 34.9 0 0 0 Polyol V 0 0 15.6 21.6 25.6 Polyol VI 0 0 0 0 0 Reactive Diluent I 0 0 0 0 0 Photoinitiator I 0 0 4.0 4.0 4.0 Photoinitiator II 4.0 4.0 0 0 0 Surfactant I 0.5 0.5 0.5 0.5 0.5 Properties Epoxy/OH Eq. Wt. Ratio 40 20 75 50 40 Viscosity, centipoise 630 756 554 616 669 TABLE III (Cont.) Example 20 21 22 23 24 Ingredients, grams Epoxide I 64.2 73.9 64.2 71.3 62.3 Polyol III 0 0 0 0 0 Polyol V 31.3 21.6 31.3 0 0 Polyol VI 0 0 0 14.2 23.2 Reactive Diluent I O 0 0 10.0 10.0 TABLE III (Cont.) Example 20 21 22 23 24 Photoinitiator I 4.0 0 0 0 0 Photoinitiator II 0 4.0 4.0 4.0 4.0 Surfactant I 0.5 0.5 0.5 0.5 0.5 Properties Epoxy/OH Eq. Wt. Ratio 30 50 30 86 47 Viscosity, centipoise 732 562 671 194 242 TABLE III (Cont.) Example 25 26 27 28 Ingredients, grams Epoxide I 69.5 61.8 71.5 62.6 Polyol III 16.0 23.7 0 0 Polyol V 0 0 14.0 22.9 Polyol VI 0 0 0 0 Reactive Diluent I 10.0 10.0 10.0 10.0 Photoinitiator. I 0 0 0 0 Photoinitiator II 4.0 4.0 4.0 4.0 Surfactant I 0.5 0.5 0.5 0.5 Properties Epoxy/OH Eq. Wt. Ratio 58 35 86 47 Viscosity, centipoise 218 254 182 226 Table III shows that the viscosity of the blend formulations containing Reactive Diluent I, i.e., Examples 23 through 28, is significantly lower than the viscosity of Examples 5 through 22 which do not contain Reactive Diluent I. The coating compositions of this invention may optionally contain Reactive Diluent I as an ingredient. The 'use of Reactive Diluent I in photocopolymerizable compositions based on epoxy and hydroxyl-containing organic, materials is more fully described in copending U.S. Patent Application Serial No. (D-13,813), filed on an even date herewith. The blended formulations were then applied to Bonderite 37R treated steel panels using a Number 20 wire-wound rod and cured with one pass under a 100 watt per inch, medium pressure, mercury lamp ultraviolet light source at 30 feet per minute. One Bonderite 37R treated steel panel coated with the specified blended formulation was prepared for each example. The cured coating on the Bonderite 37R treated steel panels of Examples 29 and 34 and Examples 65 and 66 was prepared from the blended formulation of Examples 5 through 10 and Examples 23 and 24 respectively. The cured coating on the Bonderite 37R treated steel panels of Examples 35 through 40 and Examples 67 and 68 was prepared from the blended formulation of Examples 5 through 10 and Examples 23 and 24 respectively. The cured coating on the Bonderite 37R treated steel panels of Examples 41 through 46 and Examples 69 and 70 was prepared from the blended formulation of Examples 11 through 16 and Examples 25 and 26 respectively. The cured coating on the Bonderite 37R treated steel panels of Examples 47 through 52 and Examples 71 and 72 was prepared from the blended formulation of Examples 11 through 16 and Examples 25 and 26 respectively. The cured coating on the Bonderite 37R treated steel panels of Examples 53 through 58 and Examples 73 and 74 was prepared from the blended formulations of Examples 17 through 22 and Examples 27 and 28 respectively. The cured coating on the Bonderite 37R treated steel panels of Examples 59 through 64 and Example 75 and 76 was prepared from the blended formulation of Examples 17 through 22 and Examples 27 and 28 respectively. The thickness of the coatings varied from about 0.8 mils to about 0.9 mils. The cured coatings were tack free immediately after ultraviolet light irradiation. Specifically designated cured coatings in Table IV below were not post cured thermally and other specifically designated cured coatings in Table IV were post cured thermally at 1700C for 10 minutes before testing for the properties designated in Table IV. The results of the testing are given in Table IV. TABLE IV Example 29 30 31 32 33 34 Properties Double Acetone Rubs 25 25 18 18 100 50 (4) (4) (4) (4) (1) (4) Pencil Hardness F F F F H H % Crosshatch Adhesion 100 100 100 100 100 100 Thermal Post Cure No No No No No No Gardner Impact, in/lbs. Forward 100 2320 2320 2320 2320 > 320 Reverse 175 2320 2320 ?320 > 320 2320 Moisture Resistance 24 Hr. Water Immersion at Room Temperature Pencil Hardness 2B HB HB 2B < 5B < 5B % Crosshatch Adhesion 100 100 100 60 0 75 3 Hr. Water Immersion at 1300F Pencil Hardness 2n B B 2B < 5B < 5B % Crosshatch Adhesion 95 100 100 95 0 0 TABLE IV (Cont.) Example 35 36 37 38 39 40 Properties Double Acetone Rubs 65 45 90 90 100 100 (4) (4) (4) (4) (1) (1) Pencil Hardness H F F F 2H H % Crosshatch Adhesion 100 100 100 100 100 100 Thermal Post Cure yes yes yes yes yes yes Gardner Impact, in/lbs. Forward > 320 > 320 > 320 )320 2320 > 320 > 320 Reverse 2320 2320 > 320 2320 2320 2320 Moisture Resistance 24 Hr. Water Immersion at Room Temperature Pencil Hardness B HB HB HB HB HB 8 Crosshatch Adhesion 100 100 100 80 100 100 3 Hr. Water Immersion at 1300F Pencil Hardness HB HB HB 2B HB F % Crosshatch Adhesion 100 100 100 100 100 100 TABLE IV (Cont.) Example 41 42 43 44 45 46 Properties Double Acetone Rubs 100 73 43 50 100 100 (1) (4) (4) (4) (1) (1) Pencil Hardness HB HB HB 2B HB 2B % Crosshatch Adhesion 100 100 100 100 100 100 Thermal Post Cure no no no no no no Gardner Impact, in/lbs. Forward 200 > 320 2320 2320 300 ?320 Reverse 75 > 320 2320 2320 275 2320 Moisture Resistance 24 Hr. Water Immersion at Room Temperature Pencil Hardness HB HB HB 3B < 5B < 5B % Crosshatch Adhesion 100 100 100 100 0 0 3 Hr. Water Immersion at 1300F Pencil Hardness 2B 3B 5B 3B 45B 45B - % Crosshatch Adhesion 100 100 100 90 0 0 TABLE IV (Cont.) Example 47 48 49 50 51 52 Properties Double Acetone Rubs 100 100 100 100 100 100 (1) (1) (1) (1) (1) (1) Pencil Hardness F F B 2B F B % Crosshatch Adhesion 100 100 100 100 100 100 Thermal Post Cure yes yes yes yes yes yes Gardner Impact, in/lbs. Forward > 320 7320 > 320 > 320 2320 > 320 Reverse > 320 > 320 2320 > 320 2320 > 320 Moisture Resistance 24 Hr. Water Immersion at Room Temperature Pencil Hardness HB RB B 3B F B % Crosshatch Adhesion 100 100 100 100 -100 100 3 Hr. Water Immersion at 1300F Pencil Hardness F RB RB RB F F % Crosshatch Adhesion 100 100 100 100 100 100 TABLE IV (Cont.) Example 53 54 55 56 57 58 Properties Double Acetone Rubs 100 70 52 47 90 50 (1) (4) (4) (4) (4) (4) Pencil Hardness H F F F H F % Crosshatch Adhesion 100 100 100 100 100 100 Thermal Post Cure no no no no no no Gardner Impact, in/lbs. Forward > 320 > 320 > 320 > 320 275 > 320 Reverse > 320 > 320 > 320 7320 250 > 320 Moisture Resistance 24 Hr. Water Immersion at Room Temperature Pencil Hardness 2B F B B B 4B % Crosshatch Adhesion 80 100 100 100 50 0 3 Hr. Water Immersion at 1300F Pencil Hardness 3B 3B B HB 45B 45B % Crosshatch Adhesion 100 100 100 90 0 0 EXAMPLE IV (Cont.) Example 59 60 61 62 63 64 Properties Double Acetone Rubs 100 100 100 100 100 100 (1) (1) (1) (1) (1) (1) Pencil Hardness F F F HB F HB % Crosshatch Adhesion 100 100 100 100 100 100 Thermal Post Cure yes yes yes yes yes yes Gardner Impact, in/lbs. Forward > 320 > 320 > 320 > 320 > 320 200 > 320 Reverse > 320 2320 2320 2320 150 > 320 Moisture Resistance 24 Hr. Water Immersion at Room Temperature Pencil Hardness 2B F B RB HB HB % Crosshatch Adhesion 100 100 100 100 100 100 3 Rr. Water Immersion at 1300F Pencil Hardness F F 133 HB F F % Crosshatch Adhesion 100 100 100 100 100 100 EXAMPLE IV (Cont.) Example 65 66 67 68 69 70 Properties Double Acetone Rubs 100 70 100 100 100 100 (1) (4) (1) (1) (1) (1) Pencil Hardness H F H H H F % Crosshatch Adhesion 98 100 100 100 100 100 Thermal Post Cure no no yes yes no no Gardner Impact, in/lbs. Forward 75 > 320 150 > 320 125 > 320 Reverse 50 300 125 > 320 100 > 320 Moisture Resistance 24 Hr. Water Immersion at Room Temperature Pencil hardness (SB < 5B HB HB < 5B < 5B % Crosshatch Adhesion 0 0 100 100 0 0 3 Hr. Water Immersion at 1300F Pencil Hardness 4SB < 5B F F SB < 5B % Crosshatch Adhesion 0 0 100 100 0 0 TABLE IV (Cont.) Example . 71 72 73 74 75 76 Properties Double Acetone Rubs 100 100 100 80 100 100 (1) (1) (1) (4) (1) (1) Pencil Hardness F F H F H F % Crosshatch Adhesion 100 100 100 100 100 100 Thermal Post Cure yes yes no no yes yes Gardner Impact, in/lbs. Forward 225 > 320 125 > 320 175 > 320 Reverse 200 > 320 100 )320 125 > 320 Moisture Resistance 24 Hr. Water Immersion at Room Temperature Pencil Hardness F F 4B 4B RB HB % Crosshatch Adhesion 100 100 0 0 100 100 3 Hr. Water Immersion at 1300F Pencil Hardness F F 4B < 5B H HB % Crosshatch Adhesion 100 100 0 0 100 100 Table IV shows the properties of cured coatings which were prepared from blend formulations containing propylene oxide polyols capped with ethylene oxide, i.e., Polyol III, Polyol V and Polyol VI.

Claims: CLAIMS 1. A photocopolymerizable composition' comprising an epoxide containing two or more epoxy groups, a poly(active hydrogen) organic compound having at least some primary hydroxyl content derived from an initiator and an alkylene oxide having the formula: EMI50.1 and end capped at least to a degree with an alkylene oxide having the formula: EMI50.2 or with a caprolactone having the formula EMI50.3 wherein R1 is individually hydrogen, alkyl, alkoxy, aryl, cycloalkyl, alkaryl or aralkyl having up to 12 carbon atoms, Rê is hydrogen or alkyl having from 1 to about 12 carbon atoms, R3is alkyl having from 1 to about 12 carbon atoms, x is a value of from 0 to about 5 and y is a value of from o to about 6, and a photoinitiator. 2. A photocopolymerizable comI.'osition as defined in claim 1 wherein the epoxide containing two or more epoxy groups is a cycloaliphc.tic epoxide, preferably an epoxide of the formulae EMI51.1 wherein R1 through R18, which can be the same or different, are hydrogen or alkyl radicals generally containing one to nine carbon atoms inclusive; R is a valence bond or a divalent hydrocarbon radical generally containing one to twenty carbon atoms inclusive, or EMI51.2 wherein RÚ through R18, which can be the same or different, are hydrogen or alkyl radicals generally containing one to nine carbon atoms inclusive, or EMI51.3 wherein the R prime and double prime groups are the same or different and are monovalent substituents or monovalent hydrocarbon radicals. 3. A photocopolymerizable composition as defined in claim 2 wherein the cycloaliphatic epoxide is 3,4-epoxycyclohexylmethyl-3, 4-epoxycyclohexane carboxylate, bis(3,4-epoxycyclo-hexylmethyl) adipate, or 2-(3,4-epoxycyclohexyl-5, 5-spiro-3,4epoxy) cyclohexane-meta-dioxane. 4. A photocopolymerizable composition as defined in claim 2 or 3 wherein the cycloaliphatic epoxide is a mixture of at least twocycloaliphatic epoxides, preferably a mixture of bis(3,4-epoxycyclohexylmethyl)adipate and 2-( 3, 4-epoxycyclohexyl- 5 ,5-spiro-3, 4-epoxy) -cyclohexane-meta-dioxane, or a mixture of 3, 4-epoxycyclohexylmethyl-3, 4-epoxy- cyclohexane carboxylate and bis(3,4-epoxy-cyclohexylmethyl)adipate which optionally includes 2-(3,4-ep oxycyclohexyl ) -5, 5-spiro-3, 4-epoxy) cyclohexane-meta- dioxane. 5. A photocopolymerizable composition as defined in any of claims 2 to 4 which contains minor amounts of one or more glycidyl type epoxides, aliphatic epoxides, epoxy cresol novolac resins, epoxy phenol novolac resins, polynuclear phenol-glycidyl ether-derived resins, aromatic and heterocyclic glycidyl amine resins or hydantoin epoxy resins. 6. A photocopolymerizable composition as defined in any of claims 1 to 5 wherein the poly-(active hydrogen) organic compound having at least sane primary hydroxyl content is a polyoxyalkylene polyol having at least some primary hydroxyl content or a propylene oxide polyol capped with ethylene oxide or epsilon caprolactone, the initiator being preferably glycerol. 7. A photocopolymerizable composition as defined in any of claims 1 to 6 wherein the poly (active hydrogen) organic compound having at least some primary hydroxyl content is of the following formula: EMI53.1 wherein R4 is alkyl having from 3 to about 12 carbon atoms, a has a value of from 0 to about 150, b has a value of from 0 to about 40, d has a value of from 1 to about 150 and e has a value of from 1 to about 40. 8. A photocopolymerizable composition as defined in any of claims 1 to 5 wherein the poly (active hydrogen) organic compound having at least some primary hydroxy content is a mixture of at least two poly(active hydrogen) organic compounds having at least some primary hydroxyl content, preferably a mixture of a polyoxyalkylene polyol having at least some primary hydroxyl content and at least one of a poly(active hydrogen) organic compound selected from the group consisting of a polyether polyol having no primary hydroxyl content, a polycaprolactone polyol, a polyester polyol, an acrylic polyol and a vinyl polyol. 9. A photocopolymerizable composition as defined in any of claims 1 to 8 further comprising a substituted cycloaliphatic monoepoxide. 10. A photocopolymerizable composition as defined in claim 9 wherein the substituted cycloaliphatic monoepoxide is selected from the group consisting of 4-vinyl cyclohexene monoepoxide, norbornene monoepoxide and limonene monoepoxide. 11. A photocopolymerizable composition as defined in any of claims 1 to 10 further comprising a surfactant. 12. A photocopolymerizable composition as defined in any of claims to 11 further comprising a low molecular weight alcohol and/or CELLOSOLVE and/or CARBOTOLX and/or-diethyleneglycol and/or a low molecular weight hydroxyl-containing vinyl polymer and/or a glycidyl ether monomer and/or an alpha oleo in epoxide and/or an epoxy novolak. 13. A photocopolymerizable composition as defined in any of claims 1 to 12 wherein the photoinitiator is selected from the group consisting of triarylsulfonium complex salts, aromatic sulfonium or iodonium salts of halogen-containing complex ions, aromatic onium salts of Group Va or VIa elements, and mixtures thereof. 14. A blend composition comprising an epoxide containing two or more epoxy groups and a poly (active hydrogen) organic compound having at least some primary hydroxyl content derived from an initiator and an alkylene oxide having the formula: EMI55.1 and end capped at least to a degree with an alkylene oxide having the formula: EMI55.2 or with a caprolactone having the formula EMI55.3 wherein R1 is individually hydrogen, alkyl, alkoxy, aryl, cycloalkyl, alkaryl or aralkyl having up to 12 carbon atoms, R2 is hydrogen or alkyl having from 1 to about 12 carbon atoms, R3 is alkyl having from 1 to about 12 carbon atoms, x is a value of from 0 to about 5 and y is a value of from o to about 6. 15. A blend composition as defined in claim further comprising a surfactant and/or a low molecular weight alcohol and/or CELLOSOLVEOR and/or CARBITOLX and/or diethyleneglycol and/or a low molecular weight hydroxyl-containing vinyl polymer and/or a glycidyl ether monomer and/or an alpha-olefin epoxide and/or an epoxy novolak. 16. A process for preparing a cured film coating comprising: (1) mixing until homogeneous a photocopolymerizable composition comprising an epoxide containing two or more epoxy groups, a poly(active hydrogen) organic compound having at least some primary hydroxyl content derived from an initiator and an alkylene oxide having the formula: EMI56.1 and end, capped at least to a degree with an alkylene oxide having the formula: : EMI56.2 or with a caprolactone having the formula EMI56.3 wherein R1 is individually hydrogen, alkyl, alkoxy, aryl, cycloalkyl, alkaryl or aralkyl having up to 12 carbon atoms, Rê is hydrogen or alkyl having from 1 to about 12 carbon atoms, R3is alkyl having from I to about 12 carbon atoms, x is a value of from 0 to about 5 and y is a value of from o to about 6, and a photoinitiator; (2) applying the homogeneous photocopolymerizable composition as a film coating on a suitable surface or substrate; and (3) exposing the film coating to actinic irradiation at a wavelength within the ultraviolet and visible spectral regions or electron beam irradiation for a period of time sufficient to cure the film coating. 17. The cured film coating of claim 16.

Inventors: KOLESKE, JOSEPH VICTOR
Applicants: UNION CARBIDE CORPORATION
Application year: 1984
Main classification: C08L63
IPC codes: C08G59, C09D163, C08L63, C09D5