DISPERSING AGENT

Abstract: A dispersing agent of the formula: B-([O-A-CO] n -J) m I wherein A is a divalent aliphatic radical; B is Y (-CO-) m wherein Y is aliphatic or arylaliphatic radical and J is -OM wherein M is H, NH₄ or a metal or J is -Z-R¹, wherein Z is a divalent bridging group and R¹ is an amino group or the salt thereof with an acid or R¹ is a sul­ phonic acid, phosphonic acid, sulphate or phosphate group or the salt thereof with a metal or an amine; or B is the residue of an adduct of a polyisocyanate and an organic compound containing two isocyanate reactive groups having a terminal -CO- group and J is a monovalent aliphatic group; n is an integer from 1 to 19; and m is 1 or 2, provided that at least 30% of the total number of groups represented by A, B and J carry an epoxy group. The dispers­ ing agent is particularly useful for the preparation of pigments dispersions for use in paints, especially thermosetting paints.

Description: Dispersing Agent This specification describes an invention relating to a compound suitable for dispersing a solid in an organic liquid and to a composition containing the compound. A number of very effective dispersing agents for a wide range of solids, including pigments, dyestuffs, oil drilling muds etc., in essentially non-polar organic liquids, especially hydrocarbons and chlorinated hydrocarbons, are known from UK Patent Numbers 1,342,746, 1,393,401, 1,393402, 1,373,660 and 2,001,083. These agents contain mono- or poly-ester residues derived from an aliphatic hydroxy carboxylic acid containing at least 9 carbon atoms with at least 4 carbon atoms separating the carboxyl and hydroxyl groups, a preferred acid being hydroxystearic acid. These agents can, however, have a deleterious effect on the properties of paint films when dispersions containing them are converted into paints. It has now been found that agents of this type are improved, particularly for use in thermosetting paints, if they contain epoxy groups. According to the present invention there is provided a compound of the formula: B -([O - A - CO] - J)m I wherein A is a divalent aliphatic radical ; B is Y (- CO -) m wherein Y is aliphatic or arylaliphatic radical and J is -OM wherein M is H, NS4 or a metal or J is - Z - R, wherein Z is a divalent bridging group and R is an amino group or the salt thereof with an acid or R is a sulphonic acid, phosphonic acid, sulphate or phosphate group or the salt thereof with a metal or an amine; or B is the residue of an adduct of a polyisocyanate and an organic compound containing two isocyanate reactive groups having a terminal - CO - group and J is a monovalent aliphatic group; n is an integer from 1 to 19; ; and m is 1 or 2, provided that at least 30Z of the total number of groups represented by A, B and J carry an epoxy group. Preferably at least 30% of the groups represented by A carry an epoxy group. The divalent aliphatic group represented by A is preferably alkylene or alkenylene preferably containing from 8 to 25 carbon atoms with at least 4 carbon atoms between the oxygen atom and carbonyl group. Where n > 1 the groups represented by A in the polyester chain (0 - A - CG3n may be the same (i.e. it is a homopolyester) or different (i.e. it is a copolyester) and as few as 30% of the groups represented by A in the polyester chain need carry epoxy groups. It is however preferred that at least 50Z and more preferably at least 70% of the groups represented by A carry an epoxy group. The group represented by A may carry up to three epoxy groups but preferably carries a single epoxy group. It is especially preferred that at least 30% of the groups represented by A are 8,-9-epoxy-Il-n-heptyl-unadec-1,11-ylene. It is also especially preferred that n is from 1 to 10. In addition to carrying epoxy groups, the groups represented by A may carry other substituents which do not confer water-solubility on the molecule, such as halogen and alkoxy. The group Y (- CO m represented by B in Formula I may be considered as the residue of an esterifiable carboxylic acid Y-COOR in which the group Y, when m = 2, is preferably alkylene, alkenylene or alkapolyenylene and, when m = 1, is preferably alkyl, alkenyl or alkapolyenyl, arylalkyl or arylalkenyl all of which may conveniently contain up to 50 carbon atoms but more preferably contain from 8 to 25 carbon atoms. The aryl group present in Y is preferably phenyl. The aliphatic groups represented by Y may carry' substituents that do not confer water solubility on the molecule, such as hydroxy, halogen, amino and alkoxy, but are preferably unsubstituted. The group represented by Y may also carry up to three epoxy groups. When B represents a group Y (- CO -) m it is preferred that m is 1 A preferred polyester chain of the formula, [0 - A - CO) n' is derivable from an unsaturated aliphatic hydroxy carboxylic acid containing from 8 to 25 carbon atoms having at least 4 carbon atoms between the hydroxy and carboxyl groups and a carbon-carbon double bond. In the compound of Formula I, containing such a polyester chain, it is preferred that at least 30%, and more preferably 50%, of these carboncarbon double bonds are epoxidised. An example of a suitable unsaturated hydroxy carboxylic acid is ricinoleic acid. In a polyester derived from pure ricinoleic acid the groups represented by A and Y are the same and Y carries a free hydroxy group. However, in their normal commercial forms, hydroxy carboxylic acids often contain small quantities of similar acids which are free from hydroxy groups. These can terminate the polyester chains and form the terminal group, represented by B, when B = Y[- CO -] m in which It is a simple hydrocarbon chain free from hydroxy groups. Examples of suitable acids from which the end group It (- CO -) m is derivable, by reaction with a terminal hydroxy group on the polyester chain, are stearic acid, oleic acid, linoleic acid, linolenic acid, phenylacetic acid, methoxyacetic acid and abietic acid in which any double bonds may be previously or subsequently epoxidised. In the group -OM represented by J in Formula I, M is preferably H or an alkali or alkaline earth metal, especially calcium. In the group - Z - R, represented by J in Formula I above, the bridging group, Z, is preferably of the formula: EMI3.1 or - O - L - wherein Q is H or an alkyl group,preferably containing up to 25 carbon atoms, and L is an alkylene or hydroxyalkylene group containing from 2 to 6 carbon atoms. Examples of the group represented by Q are methyl, ethyl, n-propyl, n-butyl and octadecyl and of the group represented by A are ethylene, trimethylene, tetramethylene, hexamethylene and 2-hydroxytrimethylene. The amino group represented by R may be a primary, secondary or tertiary amino group or a substituted ammonium group and is preferably of the formula: EMI4.1 wherein T1, T2 and T3 are each independently E, alkyl, or cycloalkyl, in which the alkyl group preferably contains up to 25 carbon atoms and the cycloalkyl preferably contains from 4 to 8 carbon atoms and each may be substituted by non-polar groups and V is a coloured or colourless anion. Examples of the groups represented by T1 to T3 are methyl, ethyl, n-propyl, n-butyl, octadecyl, 2-hydroxyethyl and cyclohexyl. The anion, V , can be from any inorganic or coloured or colourless organic acid, such as HCl, H2S04, CH3COOH, C2H5COOH, HCOOH, CH3S03H, C6H5S03E, C6H5COOH or an organic dye containing a -SO3H or -COOH group, especially an azo, anthraquinone or phthalocyanine dye containing a -SO3H or -COOH group, such as are described in the Third Edition of the Colour Index (1971). Alternatively the amine group, X, may be a polyalkylene imine as disclosed in UK 2,001,083 or such a polyalkylene imine carrying polyester side chains. The compound of Formula I above in which J comprises a polyalkylene imine is similar to the polyester-polyalkylene- imine dispersing agent described and claimed in UK 2,001,083 except that one or more, and preferably all, of the polyester side chains contain epoxy groups. A preferred polyalkylene imine is a polyethylene imine having a molecular weight in the range from 500 to 100,000. Where IL represents a sulphonic acid, phosphonic acid, sulphate or phosphate group or the salt thereof with a metal or an amine the cation may be a hydrogen ion, a metal ion, an ammonium ion or a substituted ammonium ion and examples of suitable cations are H , Na+, K+, Cm , No4 , N(CE3) and NH(CH3)4+. Where B is the residue of an adduct of a polyisocyanate and an organic compound containing two isocyanate reactive groups, the compound of Formula I above has the same general structure as the dispersing agent disclosed in UK 1,393,401 and UK 1,393,402 except that at least one of the carbon chains caries an epoxy group. The dispersing agent disclosed in these patents is the adduct of one or more compounds from each of the following classes: (a) an organic compound containing two or more isocyanate groups, (b) an organic compound containing two or more groups which are reactive with isocyanate groups, and (c) a compound of the formula: : z - x - E-(T - D) n-i II wherein Z is OH or NHIL and R is a monovalent hydrocarbon group; X X is an optionally substituted divalent hydrocarbon group; T is a divalent hydrocarbon radical n is a positive integer Q is an optionally substituted monovalent hydrocarbon group; E is - CO - 0 - or - CO - NR' - wherein R' is a hydrogen atom or a monovalent hydrocarbon group; and D is - CO - 0 provided that only one of E and D is connected to T via the carbonyl atom of a carbonyl group present in D and E and at least one of the groups represented by X, T and Q contains a carbon chain having at least 5 carbon atoms. In this form of the compound of Formula I the group [0 - A - CO] n in Formula I corresponds to the group (T - D)ni in component (c), the aliphatic group J in Formula I corresponds to the group Q in component (c), and at least one of the hydrocarbon radicals represented by X, Q and T in component (c) carries an epoxy group. The aliphatic group J is preferably C5 25-alkyl, optionally carrying up to three epoxy groups and is derivable from an aliphatic alcohol having up to three carboncarbon double bonds. The compound of Formula I can be prepared by the processes described in UK Patent Nos. 1,342,746, 1,373,660, 1,393,401, 1,393,402 and 2,001,083, provided that at least one of the reactants contains at least one carbon-carbon double bond, followed by epoxidation of the carbon-carbon double bond or bonds. According to a further feature of the present invention there is provided a process for the preparation of a compound according to Formula I which comprises reacting an epoxidising agent with a compound of the formula: B - (tO - A - CO] - J) III wherein B, A and J are as previously defined provided that they are free from epoxy groups and at least 30% of the total number of these groups contain a carbon-carbon double bond. Such a process is particularly suitable for the preparation of compounds of Formula I which are made by esterification or amidification because of the sensitivity of epoxy groups to free amino and hydroxy groups. Where the compound contains a quaternary ammonium group, quaternisation may precede or follow the epoxidation. If the compound of Formula I contains groups, other than epoxidisable double bonds, which are unstable to epoxidising agents it is preferable to perform the epoxidation at an earlier stage and according to another feature of the present invention there is provided a process for the preparation of a compound according to Formula I which comprises reacting a compound of the formula B (- W) m with a compound of the formula: Eo - A - CO - (O - A - )n-1¯ IV wherein W is a group reactive with hydroxy groups, and A, B, m and n have the same meanings as in Formula I and J is a monovalent aliphatic group. This process is particularly suitable for the preparation of compounds according to Formula I in which B is the residue of an adduct of a polyisocyanate and an organic compound containing two isocyanate reactive groups. The epoxidising agent may be any epoxidising agent in general use. It is conventional to use a peroxy acid and especially an organic peroxy acid as epoxidising agent. The organic peroxy acid may be in the aliphatic or aromatic series and may carry polar substituents. Suitable peroxy acids include performic acid, peracetic acid, perbenzoic acid, m-chloroperbenzoic acid, perpropionic acid, trifluoroperacetic acid, monoperoxyphthalic acid and p-nitroperbenzoic acid. The peroxy acid may be used directly or generated in situ. It may be generated in situ by reaction of the corresponding carboxylic acid with a suitable oxidising agent, such as hydrogen peroxide. It is often desirable to promote the in situ formation of the peroxy acid by the addition of an acid catalyst, such as sulphuric acid. Otherwise the acid catalysis may be provided by an immobilised acid catalyst, such as an ion-exchange resin containing sulphonic acid groups. Epoxidation may be performed in the absence or the presence of a solvent. Suitable solvents include chloroform, dichloromethane, benzene, toluene, xylene, 1,2-dichloroethane and l,1,1-trichloroethane. Other epoxidising agents which may be suitable are peroxyimidic acids, generated in situ from an alkyl nitrile and hydrogen peroxide, ethoxyperformic acid, generated in situ from ethoxychloroformate and hydrogen peroxide and hydrogen peroxide itself in the presence of tungstic or molybdic acid at a pH between 4 and 6. The epoxidation may be performed using an electrochemical oxidation method. Processes for the preparation of the compound of Formula III are analogous to those given in the aforementioned patents, using either an unsaturated hydroxycarboxylic acid in place of the saturated hydroxycarboxylic acid disclosed in said patents for the preparation of the mono- or poly-ester residue followed by epoxidisation, or an epoxidised hydroxycarboxylic acid. The disclosures of UK Patent Specification Nos 1,342,746, 1373660, 1,393,401, 1,393,402 and 2,001,083 are'incorporated into the present specification by reference. The compound according to Formula I is suitable for the dispersion of a solid in an organic liquid and- according to a further feature of the present invention there is provided a dispersible composition of a solid and a compound according to Formula I. It is preferred that the amount of the compound of Formula I, hereinafter referred to as the dispersing agent, present in the composition is from 1% and 50Z, and more preferably from 2X to 30Z, by weight, based on the amount of solid. The composition is suitable for the preparation of a dispersion of the solid in an organic liquid and according to a further feature of the present invention there is provided a dispersion of a solid in an organic liquid containing a compound according to Formula I. The dispersion preferably contains from 5Z to 90%, by weight, of the solid, based on the total weight of the dispersion, the precise quantity depending on the nature of the solid and the relative densities of. the solid and the organic liquid. For example, dispersions of organic solids preferably contain from 15Z to 60X by weight of solid whereas dispersions of inorganic solids preferably contain from 40% to 90Z of the solid, based on the total weight of the dispersion. The organic liquid in which the solid is dispersed may be any inert organic liquid in which-the dispersing agent is at least partially soluble at ambient temperatures and which is stable under the subsequent conditions of usage of the dispersion. If desired mixtures of organic liquids may be used. Preferred organic liquids are aromatic hydrocarbons and aliphatic and aromatic halogenated hydrocarbons such as benzene, toluene, xylene, chlorobenzene, carbon tetrachloride and perchloroethylene. Other organic liquids which can be used are esters, such as propyl acetate, aliphatic alcohols such as n-butanol and ketones such as methylbutylketone and particularly mixtures of these with aromatic hydrocarbons, such as 4:1 xylene:n-butanol, which is widely used in the preparation of thermosetting paints. In general the organic liquid or mixture of liquid selected will depend on the end-use for the dispersion. The dispersed solid is preferably an inorganic or organic pigment from any of the recognised classes of pigments described, for example, in the Third Edition of the Colours Index (1971) and subsequent revisions and supplements, under the chapter headed '9igments". Other preferred solids are fillers and extenders such as talc, kaolin, barytes and chalk. Examples of inorganic pigments are titanium dioxide, zinc oxide, Prussian blue, cadmium sulphide, iron oxides, carbon black, vermillion and ultramarine. Further examples of inorganic pigments are the chrome pigments including chromates, molybdates and mixed chromates/sulphates of lead, zinc, barium and calcium and the various mixtures and modifications thereof which are commercially available as greenish-yellow to red pigments under the names primrose, lemon, middle, orange, scarlet and red chromes. Examples of organic pigments are those from the azo, disazo, condensed disazo, thioindigo, indanthrone, isoindanthrone, anthraquinone, anthranthrone, isodibenzanthrone, triphendioxazine, phthalocyanine, especially copper phthalocyanine and its nuclear halogenated derivatives, and quinacridone series, and lakes of acid, basic and mordant dyes. Preferred organic pigments are copper phthalocyanines, monoazos, disazos, indanthrones and quinacridones The dispersion may also contain other ingredients such as are normally added to improve the-properties and performance of dispersions. Examples of such other ingredients are fluidising agents, antisedimenting agents, preservatives against microbial growth and resins. The present dispersions are compatible with the fluidising agents disclosed in UK Patent Specifications Nos 1,508,576 and 2,108,143 the contents of which are incorporated herein by reference. The fluidising agent described in UK 1,508,576 is a substituted ammonium salt of a coloured acid wherein there are from 19 to 60 carbon atoms in at least 3 chains attached to the N atom of the substituted ammonium ion. The fluidising agent described in UK 2,108,143 is a waterinsoluble disazo compound comprising a central divalent group free from acidic and other ionic substituents linked, througfr azo groups, to two monovalent end groups, one end group being-free from ac-idic and other ionic substituents and the other carrying a single substituted ammoniumacid salt group. The present dispersions incorporating such fluidising agents form a further feature of the present invention. The dispersions of the invention can be obtained by any of the conventional methods for preparing dispersions. Thus the solid, the organic liquid and the dispersing agent may be mixed together in any order and, where necessary, the mixture subjected to a mechanical treatment to reduce the particle size of the solid, for example by ball, gravel or bead milling until a stable dispersion is formed. The treatment is preferably continued until the mean diameter of the pigment particles is below 10 microns and more preferably below 5 microns. The composition of the solid and the compound of Formula I can be isolated by removal of the solvent, for exemple, by evaporation. If the dispersing agent is used in the form of a salt it is not essential to take the preformed salt as this can be prepared in situ during the preparation of the dispersion by mixing together the solid, the organic liquid, the appropriate dispersing agent, in its free acid or base form, and either a base or acid, and subjecting the mixture to a mechanical grinding operation. It is not essential that the dispersing agent is converted completely into the salt form because in many cases the free acid or base form of the agent is equally effective in dispersing the solid. An alternative process comprises reducing the particle size of the solid alone, or in admixture with the organic liquid or the dispersing agent alone followed by the addition of the other ingredients when the desired reduction in particle size has been achieved. Yet another process comprises adding an aqueous emulsion of a solution of the dispersing agent in an organic liquid to an aqueous slurry of the solid, following-which the organic liquid and water are removed, by filtration and the solid mixture is dried to provide a dry composition of the solid and the dispersing agent. A dry composition of a solid and a compound of Formula I forms a further feature of the present invention. The dry composition can be subsequently incorporated into an organic liquid to give a dispersion. inhere the solid is a pigment, such a dry composition can be formed by mixing the dispersing agent, preferably in an aqueous emulsion, with the solid during a late stage in the preparation of the pigment so that the dispersing agent forms an intimate mixture with the pigment. The dispersing agent is particularly suitable for the dispersion of pigments destined for use in paints, especially thermosetting paints, because the agent is compatible with the resins used in such paints and does not adversely affect the properties of the paint film, such as hardness, gloss, transparency etc. In this respect it is superior to the aforementioned known dispersing agents of similar structure which do not contain epoxy groups while retaining the powerful dispersing action of these known agents. Paint systems in which the dispersing agent, and dispersions derived therefrom, are particularly suitable include alkyd/melamineformaldehyde paints, alkyd/urea-formaldehyde paints, thermosetting acrylic/melamine-formaldehyde paints, vinyl-modified alkyd/melamineformaldehyde paints and epoxy paints. Other thermosetting or stowing paints for which the dispersing agents and derived dispersions are suitable are those based upon combinations of oil-free alkyd resins, oil-free polyester resins, vinyl-modified alkyd resins, styrenemodified alkyd resins, rosiniphenolic modified alkyd resins and polymethacrylic ester-modified alkyd resins with crosslinkers or hardeners, such as melamine-formaldehyde, urea-formaldehyde, butylated melamine-formaldehyde, butylated urea-formaldehyde or hexamethoxymethylmelamine. The invention is further illustrated by the following examples in which all parts and percentages are by weight unless otherwise indicated. Intermediate 1 A mixture of 3206g of ricinoleic acid and 6g of tetrabutyl titanate was stirred at 170-5"C under a stream of inert gas. The acid value of the reaction mixture was determined at intervals and after 17 hours , when the acid value was 34mg KOB/g, reaction was stopped by cooling the reaction mixture to room temperature. The product is hereinafter called Intermediate 1. Intermediate 2 A mixture of 1276g of Intermediate 1, 40.5g of dimethylaminopropylamine and 104g of toluene was stirred under reflux at 19O0C using a Dean & Stark head to remove water. After two hours, when no further water was being removed, the toluene was removed by distillation under vacuum. The reaction product, hereinafter called Intermediate 2, had an acid value of 24.4mg KOHlg and an equivalent weight, with respect to basic nitrogen, of 3459. Intermediate 3 To 980g of Intermediate 2, stirring at 40at, there were added 33.8g of dimethylsulphate. An exotherm resulted, raising the temperature to 500C and this was raised to 900 and maintained there for 1 hours by the application of external heat. At the end of this period no free dimethyl sulphate could be detected in the reaction mass by gas-liquid chromatography. The product is hereinafter called Intermediate 3. Intermediate 4 A mixture of 350g of ricinoleic acid, lOOg of oleic acid and 0.2g of tetrabutyl titanate was stirred at 18o-185 C under a stream of inert gas. The acid value of the reaction mixture was determined at intervals and, after 8 hours, when the acid value was 70.3 mg,KOHig, reaction was stopped by cooling the reaction mixture to room temperature. The product is hereinafter called Intermediate 4. Intermediate 5 A mixture of 82.5g of Intermediate 4 and 6.22g of highly branched high moecular weight polyethyleneimine (sold under the trade name POLYNIN WATERFREE by BASF) was stirred at 145-1550C for 1 hours. The reaction was then stopped by cooling the reaction mixture. The product, hereinafter called Intermediate 5, had an acid value of 35 .8mg.K0H/g. Intermediate 6 A mixture of-200g ricinoleic acid 87g of oleyl alcohol and 0.3g tetrabutyl titanate was stirred at 170-1800C under a stream of inert gas. The acid value was determined at intervals and after 23 hours when the acid value was 2 gm.KOR/g, reaction was stopped b7 cooling the reaction mixture to room temperature. The product, hereinafter called Intermediate 6, had a hydroxyl value of 57 mg.KOH/g. Intermediate 7 Solution A was prepared by dissolving 3.8g aminoethane sulphonic acid in a mixture of 2.5g of a 48.6Z aqueous solution of sodium hydroxide and 25g water. Solution B was prepared by mixing 50g Intermediate 1 and 21.7g toluene until the mixture was homogeneous. Solution B was transferred to a flask equipped with a gas inlet tube, and a Dean and Stark water separator. Solution A was added to the flask over 1 minute while the contents were stirred rapidly. Stirring was continued while heating was applied, and initially all the water was removed in the Dean and Stark separator. Toluene was then distilled off until the temperature of the reaction mass rose to 1800C. The reaction mass was then stirred at this temperature for 5 hours under a stream of inert gas, after which reaction was stopped by cooling the reaction mixture to room temperature. The reaction product, hereinafter called Intermediate 7, had an acid value of 5.4 mg.KOH/g, Intermediate 8 To a solution of 50g of Intermediate 6 in 296g chloroform there was added, over a period of one hour, a solution of 40g of m-chloroperbenzoic acid in 592g chloroform. An exotherm resulted raising the temperature to approximately 400C. One hour after addition was complete, a test with dampened starch-iodide paper showed the presence of excess peroxy acid. 2 hours after addition the same test showed the absence of peroxy acid. The reaction mixture was allowed to stand overnight, and any crystallised m-chlorobenzoic acid was filtered off. The chloroform solution was first washed with 200g of 10% aqueous sodium sulphite solution, and then with 400g of 5% sodium bicarbonate solution. Finally the chloroform solution was washed until free from alkali with several 800g portions of water and the chloroform removed,by vacuum distillation, to leave the product, hereinafter called Intermediate 8. Intermediate 6 had an iodine value of 91.3g I2/1OOg while Intermediate 8 had an iodine value of 15.5g 1211O0g indicating that the m-chloroperbenzoic acid had epoxidised 83% of the double bonds present in Intermediate 6. Example 1 To a solution of 50g of Intermediate 1 in 296g of chloroform there was added, over a period of one hour, a solution of 46g of m-chloroperbenzoic acid in 660g of chloroform. An exotherm resulted raising the temperature to 400C. After a further two hours stirring, during which the temperature was allowed to fall to ambient, a further 4g of m-chloroperbenzoic acid was added and stirring continued for 30 minutes. The reaction mixture was then checked for the absence of excess peroxy acid using dampened starch-iodide paper. It was then allowed to stand overnight and any crystallised mochlorobenzoic acid was filtered off. After the addition of 200g of 5X aqueous sodium sulphite solution with agitation, the mixture was allowed to stand and the chloroform layer separated from the aqueous layer. The product was worked up by washing the organic layer with 800g 5% sodium bicarbonate solution and then with several 800g portions of water until free from alakli. The chloroform was then removed by vacuum distillation leaving the product, hereinafter called Dispersing Agent 1. Intermediate 1 had an iodine value of 94g I21100g while Dispersing Agent 1 had an iodine value of 15.8g I2/lOOg indicating that the m-chloroperbenzoic acid had epoxidised 83.2X of the double bonds present in Intermediate 1. Example 2 To a solution of 23g of Intermediate 2 in 148g of chloroform was added, over 30 minutes, a solution of 15g of m-chloroperbenzoic acid in 220g of chloroform. An exotherm raised the temperature to 350C and after a further period of 2 hours, during which the temperature fell to ambient, a further 2g of at-chloroperbenzoic acid was added. After a further 30 minutes of agitation and standing overnight the reaction mixture was tested for presence of peracid (a trace was found) using dampened starch-iodide paper. The product was worked up and isolated as in Example 1. It is hereinafter called Dispersing Agent 2. Example 3 To a solution of 62.5g of Intermediate 3 in 296g of chloroform there was added, over 1 hour, a solution of SOg of moperbenzoic acid in 740g of chloroform. An exotherm raised the temperature to 350C and the mixture was agitated for a further 2 hours and allowed to stand overnight. A test with dampened starch-iodide paper showed the presence of some excess peracid. The product was worked up and isolated as in.Example 1. It is hereinafter called Dispersing Agent 3. Intermediate 3 had an iodine value of 90.5g I2/lOOg and Dispersing Agent 3 had an iodine value of 7g 12/1008. This indicates that the m-chlorobenzoic acid had epoxidised 92Z of the double bonds present in Intermediate 3. Example 4 To a solution of 50g of Intermediate 4 in 296g chloroform was added over 1 hour a solution of 43g m-chloroperbenzoic acid in 600g chloroform. An exotherm raised the temperature to approximately 400 C. After agitation for a further hour, a test with dampened starch-iodide paper showed the absence of peroxy acid. The reaction mixture was allowed to stand overnight. The product was then worked up as in Example 1. It is hereinafter called Dispersing Agent 4. Intermediate 4 had an iodine value of 98.6g 12/1O0g while Dispersing Agent 4 had an iodine value of 21.9g I2/1OOg indicating that the m-chloroperbenzoic acid had epoxidised 78% of the double bonds present in Intermediate 4. Example 5 To a solution of 30g of Intermediate 5 in 222g chloroform was added over 30 minutes a solution of 25g m-chloroperbenzoic acid in 370g chloroform. An exotherm raised the temperature to approximately 350C, and the colour of the reaction mixture lightened during the addition from a dark brown to a pale yellow. After agitation for a further twenty minutes, a test with dampened starch-iodide paper showed a trace of peroxy acid. The reaction mixture was allowed to stand overnight. The product was then worked up as in Example 1. It is hereinafter called Dispersing Agent 5. Intermediate 5 had an iodine value of 96.5g 12/lOOg while Dispersing Agent 5 had an iodine value of 49.9g I2/lOOg indicating that the m-chloroperben20ic acrid had epoxidised 48% of the double bonds present in Intermediate 5. Example 6 To a solution of 16g of Intermediate 7 in 104g chloroform was added over 30 minutes a solution of 13g m-chloroperbenzoic acid in 192g chloroform. The temperature was kept below 35µC during the addition. After allowing the reaction mixture to stand for 16 hours, a test with dampened starch-iodide paper showed no peroxy acid was present. The product was then worked up as in Example 1. It is hereinafter called Dispersing Agent 6. Intermediate 7 had an iodine value of 91g I21100g while Dispersing Agent 6 had an iodine value of 8.27g I2/100g indicating that the m-chloroperbenzoic acid had epoxidised 91% of the double bonds present in Intermediate 7. Example 7 A mixture of 12.1Ng tolylene diisocyanate, O.0019g benzoyl chloride and 15.8g acetone was stirred and 6.2g 1,6-hexanediol was added. This mixture was stirred and heated under reflux for one hour, 25.7g of Intermediate 8 was added, and the reaction mixture stirred and heated under reflux for a further two hours. 0.04g Diazabicyclooctane was then added, and after stirring and heating the reaction mixture under reflux for a further hour it was allowed to stand overnight at room temperature. At this stage the isocyanate group content of the mixture was found to be 0.45%. 0.46g Diethylamine was then added, and there was a slight exotherm. The product was then alkaline to brilliant yellow paper. Acetone was removed by distillation, and, simultaneously, xylene was added in a dropwise manner. The distillation was continued until the temperature of the vapour reached 1200C. The product hereinafter called Dispersing Agent 7 was thereby obtained as a 45.4Z solution in xylene. Example 8 To a solution of 26.6g of Intereediate 1 in 148g chloroform was added over 30 minutes a solution of 10g m-chloroperbenzoic acid in 148g chloroform. A slight exotherm raised the temperature by a few degrees centigrade. After agitation for a further two hours, a test with dampened starch-iodide papet showed the absence of peroxy acid. The product was then worked up as in Example 1. It is hereinafter called Dispersing Agent 8. Intermediate 1 had an iodine value of 94g I2/100g while Dispersing Agent 8 had an iodine value of 57g I2/100g indicating that the m-chloroperbenzoic acid had epoxidised 40% of the double bonds present in Intermediate 1. Example 9 To a solution of 280g of Intermediate 1 and 47g of formic acid in 1000g of dichloromethane stirred at 20-250C there was added, over a period of 6 hours, 170g-of a 35% by weight solution of hydrogen peroxide. The reaction mixture was stirred at 20-250C during a further 18 hours and then checked for the presence of excess peroxy acid using dampened starch-iodide paper. The excess peroxy acid was destroyed by the addition of 40% aqueous sodium hydrogen sulphite solution. To the mixture was added 400g of a 1X solution of cetrimide. The mixture was allowed to stand for 1 hour and the dichloromethane layer was separated from the aqueous layer. The organic layer was washed to freedom.from acid with several 400g portions of water. The dichloromethane was removed by vacuum distillation leaving the product, hereinafter called Dispersing Agent 9. Dispersing Agent 9 had an iodine value of 37.5g I2/100g indicating that the performic acid formed in situ had epoxidised 60% of the double bonds present in Intermediate 1. Example 10 In place of the 170g of 35% solution of hydrogen peroxide used in Example 9 there were used 119g of a 50% solution of hydrogen peroxide. The product, Dispersing Agent 10, had an iodine value of 27.9g I2/lOOg indicating that the performic acid formed in situ had epoxidised 70% of the double bonds present in Intermediate 1. Example 11 To a solution of 280g of Intermediate 1 in 1000g of dichloromethane stirred at 20-250C was added 4g of anhydrous sodium acetate followed, over a period of 5 hours, by 240g of 38% peracetic acid. The reaction mixture was stirred at 20-25QC during a further 18 hours. The excess of peroxy acid was destroyed by the addition of 40% aqueous sodium hydrogen sulphite solution, when a test sample showed no coloration by spotting on to dampened starch-iodide paper. To the mixture was added 800g of a 1% solution of cetrimide. The mixture was allowed to stand for 1 hour and the dichloromethane layer was separated from the aqueous layer. The organic layer was washed to freedom fro acid with several 800g portions of water. The dichloromethane was removed by vacuum distillation leaving the product, hereinafter called Dispersing Agent 11. Dispersing agent 11 had an iodine value of 29.8g I2JlOOg indicating that the peracetic acid had epoxidised 68Z of the double bonds present in Intermediate 1. Fluidising Agent 1 This is the product described as Agent B in UK 1508576. Fluidising Agent 2 This is the product described in Example 1 of UK2108143. Fluidising Agent 3 This is the product described in Example 1 of UK2108143. Comparative Dispersing Agent A This is poly(12-hydroxystearic acid) having an acid value of 35mg KOH/g. Comparative Dispersing Agent B A fixture of 320g of Comparative Dispersing Agent A, 10.2g of dimethylaminopropylamine and 65g of toluene was stirred under reflux using a Dean & Stark head to remove water of reaction. The temperature was then raised to 1650C and held there for 6 hours. Finally the toluene was removed by vacuum distillation. Comparative Dispersing Agent C To 200g of Comparative Dispersing Agent B, stirring at 40 C, was added 7.lg of dimethyl sulphate. An exotherm raised the temperature to 500C and this was raised to 900C by the application of external heating. At the end of 1 hour at 900C no free dimethyl sulphate was detected in the product by gas-liquid chromatography. Comparative Dispersing Agent D This is polyricinoleic acid having an acid value of 34mg.KOR/g, and it is also referred to in this patent application as Intermediate 1. Comparative Dispersing Agent E A mixture of 335g 12-hydroxystearic acid, lOOg stearic acid and 1.0g tetrabutyl titanate was stirred at 170-18O0C under a stream of inert gas. The acid value was determined at intervals and after 12 hours, when the acid value was 73 mg.KOH/g, reaction was stopped by cooling the reaction mixture to room temperature. The product is hereinafter called Comparative Dispersing Agent E. Examples 12 to 39 Twenty-eight dispersions, having the formulations described in Table 1 were prepared by ball-milling the ingredients for 16 hours. All the resulting dispersions were fluid, deflocculated and with the pigment particles having a mean diameter below 5 microns. In Table 1 the Pigments are identified by their shade and Colour Index (CI) number. The Dispersing Agents and Fluidising Agents are identified by DA and FA respectively followed by the number identified hereinbefore in the description of these agents. Table 1 Example Pigment Dispersing Agent Fluidising Agent Org Liq & Amount & Amount & Amount & Amount 12 White 6 DA 1 - Xylene - 7.0g 0.35g 2.65g 13 Red 104 DA 2 - Xylene 6.0g 0.6g 14 Red 101 DA 2 - Xylene 6.0g 0.6g 3.4g 15 Green 7 DA 3 FA 1 Xylene 3.0g 0.6g 0.3g 6.1g 16 Black 7 DA 3 FA 1 Xylene 3.0g 0.6g 0.3g 6.1g 17 Yellow 1 DA 3 FA 2 Xylene 3.0g 0.6g 0.3g 6.1g 18 Red 4 DA 3 FA 3 Xylene 3.0g 0.6g 0.3g6.1g 19 Yellow 34 DA 5 - Xylene 7.5g 0.37g 2.13g 20 Blue 15:2 DA 5 FA 1 Xylene 3.0g O.6g 0.3g 6.1g 21 Blue 15: :3 DA 7 FA 1 Xylene 3.0g 0.6g 0.3g 6.1g Example Pigment Dispersing Agent Organic Liquid & Amount & Amount & Amount 22 White 6 DA 7 Xylene 7.0g 0.35g 2.65g 23 Green 7 DA 7 Xylene 3.0g 0.6g 6.4g 24 Yellow 1:1 DA 7 Xylene 2.5g 0.5g 7.0g 25 Violet 19 DA 7 Xylene 2.5g 0.5g 7.0g 26 Red 168 DA 7 Xylene 2.5g 0.5g 7.0g 27 Red 122 DA 5 Xylene 2.5g 0.5g 7.0g 28 Yellow 173 DA 5 Xylene 2.5g 0.5g 7.0g 29 Yellow 34 DA 4 Xylene 6.Og 0.6g 3.4g Yellow 34 DA 6 Toluene 7.0g 0.35g 2.65g 31 Yellow 34 DA 6 2-ethoxyethyl acetate 7.0g 0.35g 2.65 32 Yellow 34 DA 6 methyl-isobutyl ketone 7.0g 0.35g 2.65g 33 Yellow 34 DA 6 butyl acetate 7.0g 0.35g ' 2.65 34 Yellow 34 DA 6 n-butanol 7.0g 0.35g 2.65g 35 Yellow 34 DA 6 perchloroethylene 5.0g 0.25g 36 White 6 DA 6 Xylene 7.5g O.23g 2.27g Example Pigment Dispersing Agent Organic Liquid & Amount & Amount S Amount 37 Yellow 34 DA 8 Xylene 7.0g 0.35g 2.65g 38 Yellow 34 DA 9 Xylene 7.5g 0.38g 2.12g 39 Yellow 34 DA 11 Xylene 7.5g 0.38g 2.12g Compatibility Testing In order to evaluate the compatibility of dispersing agents with various paint resin systems, the following experiments were performed. An Alkyd/Melamine formaldehyde paint resin system A stock solution containing 100g PLASTOKYD C30-AX, 50g BEETLE BE 615 and 50g xylene was prepared. (PLASTOKYD is a registered trade mark of Cray Valley Products Ltd., and PLASTOKYD C30-AX is an alkyd resin comprising 42Z phthalic.anhydride, 40% fatty acid, 18% glycerol and 30Z xylene. BEETLE is a registered trade mark of British Industrial Plastics and BEETLE BE 615 is an n-butylated melamine formaldehyde resin supplied as a 60Z solution in n-butanol). This stock solution was divided into 4g samples which were diluted with a further 2g xylene. Dispersing agent was then added to, and dissolved in, these samples. Table 2 indicates the dispersing agents added. In each case they were added at levels of OZ, 1%, 2%, 5% and 10% calculated as weight on total resin solids weight. A portion of each sample was then poured on to a glass slide, dimension 7.5cm by 2.5cm. The quantity used was sufficient to give a film approximately 75 microns thick, on drying. The slides were air-dried for 30 minutes, then stoved for 30 minutes at 1200C. Complete compatibility is shown by a clear, transparent slide. Incompatibility is manifested in a cloudy, milky appearance to the slide. The slides were assessed on a O to 5 scale where 0 indicates complete transparency, and 5 indicates extreme milkiness. The results are reported in Table.2. Table 2 Dispersing Agent Z Dispersing Agent in film OZ 1% 2% 5% 10Z Comparative Disp.Agent A O 0 1 1-2 3 B O O 1 2 3 C O 1 1-2 3 4 D O 0 0 0-¸ Dispersing Agent 1 0 0 0 0-1 0-1 2 0 0 0 0 0 3 0 0 0 0 0 4 0 0 0 0 0 5 0 0 0 0 0 6 0 0 0 0 7 0 0 0 0 0 8 -Q O 0 O 9 O O O O O A Thermosetting Acrylic Paint System A stock solution containing 187.5g SYNOCRIL 826S, 125g BEETLE BE 615 and 62.5g xylene was prepared (SYNOCRIL is a registered trade mark of Cray Valley Products Ltd., and SYNOCRIL 826S is a hydroxyl acrylic resin supplied as a 60% solution in xylene/n-butanol). Glass slides of this resin system containing various dispersing agents at various levels were prepared in exactly the same way as in the previous experiment. The slides were assessed on the same 0 to 5, scale, and the results are reported in Table 3. Table 3 Dispersing Agent Z Dispersing Agent in film OZ 1Z 22 5Z 10% Comparative Disp.Agent A O 1 1 - 3 4 B O 0 1 3 5 C O 0 1 1-2 3-4 D O 0 0 F 1-2 E O 0 0 0 h Dispersing Agent 1 0 0 0 0 0 2 0 0 ¸ ¸ 1-2 3 0 0 0 0 ¸ 4 0 0 0 0 0 5 0 0 0 0 0 6 0 0 0 O O-¸ 7 -Q 0 0 0 0 8 0 0 0 h 1 9 0 0 0 0 ¸ An Epoxy Paint Resin System A stock solution containing 107.lg ARALDITE PZ 820, 35.7g ARALDITE HZ 820, 34.3g xylene, 5.7g n-butanol and 17.2g methyl isobutyl ketone was prepared. (ARALDITF is a registered trade mark of CIBA-GEIGY Plastics and Additives Co., ARALDITE PZ 820 is an epoxy resin supplied as a 70Z solution in a blend of aromatic, hydroxylic and ketonic solvents, and ARAIDITE HZ 820 is a polyaminoamide curing agent also supplied as a 70Z solution in a blend of aromatic, hydroxylic and ketonic solvents). Glass slides of this resin system containing various dispersing agents at various levels were prepared in exactly the same way as the previous two experiments. The slides were assessed on the same 0 to 5 scale, and results are reported in Table 4. Table 4 Dispersing Agent Z Dispersing Agent in film OZ 1Z 2% 5% 10% Comparative Disp.Agent A 0 1-2 1-2 3 3 B O 1 2 3 3-4 C 0 2 2-3 3 3-4 D 0 h h 3-4 3-4 Dispersing Agent 1 0 1 1-2 2 3 2 0 0 0-1 2-3 3 3 0 0 0 0 0 4 0 0 0 0 0 5 0 0 0 1 1-2 6 0 0 0 0 1-2 7 0 0 0 0 0 8 -O 0 1 2-3 3 9 0 0 1 1-2 3-4 The results in Tables 2 to 4 demonstrate the significant advantages for the dispersing agents of the present invention over the closest known dispersing agents in compatibility with a range of conventional paint resins. Examples 40 to 43 and Comparative Examples 1 to 6 To evaluate the effect of the dispersing agents in accordance with the present invention on conventional thermosetting paint systems pigmented with a lead chrome pigment and a phthalocyanine pigment, an oven-drying alkyd-melamine paint system was employed. The alkyd resin used had the following formulation: Phthalic Anhydride 42% Fatty acid 40% Glycerol 18% Xyleng 30% and the acid value of the solid portion was 7mg HOHlg. The resin is available as PLASTOKYD C-30 AX (PLASTOKYD is a registered trade mark). In each of Examples 40 and 41 the pigment was dispersed in solvent in the presence of the dispersing agent. In Example 42 a fluidising agent was also added. In Example 43 the pigment was dispersed in the solvent in the presence of resin and the dispersing agent was added to the let-down solution. The Comparative Examples were of 3 different types: (i) Pigment was dispersed in the solvent in the presence of resin, in accordance with normal procedure in paint technology (Comparative Examples 1, 3 & 4); (ii) Pigment was dispersed in the solvent in the presence of resin and two separate dispersing agents in accordance with UK 1,342,746 were added to the let-down solution (Comparative Examples 5 and 6); (iii) Pigment was dispersed in solvent in the presence of a dispersing agent in accordance with UK 1,373,660 (Comparative Example 2). All the paint formulations were prepared as a concentrated mill-base in a ball mill and in each case the mean particle diameter of the pigment, after milling, was below 5 microns. After milling the mill-base was let-down with further resin, cross-linking agent and solvent to produce a usable paint. The precise formulations of the mill-bases and let-down solutions are given in Tables 5 to 7 below, all quantities being expressed in grams weight. Table 5 Component Comparative Comparative Example Example Example 1 Example 2 40 41 Millbase Pigment Yellow 34 28.0 28.0 28.0 28.0 PLASTOKYD C-30 AX 6.54 - - Dispersing Agent 1 - - 1.4 Dispersing Agent 3 - - - 1.4 Comparative Agent C - 1.4 - Xylene 14.66 9.2 9.2 9.2 n-Butanol 3.66 Let-down Solution PLASTOKYD C-30 AX 50.0 56.54 56.54 56.54 BEETLE RE 615 27.5 27.5 27.5 27.5 Xylene 11.6 15.1 15.1 15.1 n-Butanol - 3.66 3.66 3.66 Table 6 Component Comparative Example Example 3 42 Millbase Pigment Blue 15: :2 6.1 6.1 PLASTOKYD C-30 AX 6.97 Dispersing Agent 3 - 0.98 Fluidising Agent 1 - 0.25 Xylene 13.53 10.41 n-Butanol 3.90 2.60 Let-down Solution PLASTOKYD C-30 AX 54.2 .59.77 BEETLE RE 615 30.5 30,5 Xylene 6.8 11.39 Table 7 Component Comparative Comparative Comparative Example Example 4 Example 5 Example 6 43 Millbase Pigment Yellow 34 28.0 28.0 28.0 28.0 PLASTOKYD C-30 AX 6.54 6.54 6.54 6.54 Xylene 14.66 14.66 14.66 14.66 n-Butanol 3.66 3.66 3.66 3.66 Let-don Solution PLASTOKYD C-30 AX 50.0 50.0 50.0 50.0 BEETLE RE 615 27.5 27.5 27.5 27.5 Comparative Agent A - 2.8 Comparative Agent D - - 2.8 Dispersing Agent 1 - - - 2.8 SOLVESSO 10G 5.3 5.3 5.3 5.3 Xylene 9R1 6.3 6.3 6.3 A test panel was prepared for each of the paints identified in Tables 5 to 7 above and these were assessed for gloss and hardness. For the assessment of gloss, in accordance with ASTM D 523 (Specular gloss measured at an incidence angle of 200), spray panels were prepared on anodised aluminium with an average dry paint film thickness of about 8 microns. For the assessment of hardness, in accordance with British Standard Test BS 3900: Part E 2, draw-down panels were prepared on anodised aluminium with an average dry paint film thickness of about 1.8 microns. The results of the assessments for gloss and hardness are shown in Table 8. Table 8 Hardness Gloss (200) BS 3900: Part E 2 ASTM D 523 Comparative Example 1 900 87 Comparative Example 2 300 76 Example 40 800 88 Example 41 1000 88 Comparative Example 3 1050 Example 42 950 Comparative Example 4 1200 92 Comparative Example 5 400 90 Comparative Example 6 700 92 Example 43 1200 94 It will be observed that the paints of Examples 40 and 41 have similar properties to the paint of Comparative Example 1 (a conventional paint) whereas the paint of Comparative Example 2 (containing a known dispersing agent, Comparative Agent C from UK 1,373,660) is inferior in terms of both hardness and gloss. The paint of Example 42 has similar properties to Comparative Example 3 (a conventional paint). The paint of Example 43 has similar properties to the paint of Comp. Example 4 (a conventional paint) while the paints of Comp. Examples 5 and 6 (which contain known dispersings agent, Comparative Agents A and D from UK 1,342,746) are inferior in terms of hardness. Example 44 and Comparative Examples 7 and 8 To further evaluate the effect of the dispersing agents in accordance with the present invention on conventional thermosetting paint systems pigmented with a lead chrome pigment, d thermosetting acrylic paint system was employed. The acrylic resin employed was SYNOCRIL 826S, and the crosslinking agent employed was BEETLE BE 683, a low viscosity n-butylated melamine formaldehyde resin supplied as a 75% solution in n-butanol. All the paint formulations were prepared as a concentrated millbase in a ball mill, and in each case the mean particle diameter of the pigment, after milling, was below 5 microns. After milling the millbase was let-down with acrylic resin cross-linking agent and solvent to produce a usable paint. The precise formulations of the millbases and let-down solutions are given in Table 9 below, all quantities being expressed in grams weight. Table 9 Component Comparative Comparative Example Example 7 Example 8 44 Xillbase Pigment Yellow 34 28.0 36.92 28.0 Dispersing Agent 1 - - 1.4 Comparative Agent-A 1.84 SYNOCRIL 826S 7.63 Xylene 12.21 12.13 9.2 n-butanol 3.05 - Let-down Solution SYNOCRIL 826S 46.33 68.08 51.63 BEETLE BE 683 29.91 39.44 29.91 Xylene 8.77 23.31 17.72 n-butanol 2.13 2.81 2.13 A test panel was prepared for each of the paints identified in Table 9, and assessed for gloss and hardness, as described for Examples 40 to 43, and Comparative Examples 1 to 6. The results are shown in Table 10. Table 10 Hardness Gloss (200) BS 3900:Part E2 ASTM D 523 Comparative Example 7 1100 92 Comparative Example 8 800 92 Example 44 1100 92 It will be seen that the paint of Example 44 has similar properties to the paint of Comparative Example 7 (a conventional paint) whereas the paint of Comparative Example 8 (containing a known dispersing agent, Comparative Agent A, from UK 1,342,746) is inferior in terms of hardness.

Claims: CLAIMS 1. A compound of the formula: B -([O - A - CO0n J) I wherein A is a divalent aliphatic radical ; B is Y (- CO -) m wherein Y is aliphatic or arylaliphatic radical and J is -OH wherein X is H, NH4 or a metal or J is - Z - 1, wherein Z is a divalent bridging group and R1 is is an amino group or the salt thereof with an acid or R1 is a sulphonic acid, phosphonic acid, sulphate or phosphate group or the salt thereof with a metal or an amine; or B is the residue of an adduct of a polyisocyanate and an organic compound containing two isocyanate reactive groups having a terminal - CO - group and J is a monovalent aliphatic group; n is an integer from 1 to 19; ; and m is 1 or 2, provided that at least 30% of the total number of groups represented by A, B and J carry an epoxy group. 2. A compound according to Claim 1 wherein the divalent aliphatic group represented by A is alkylene or alkenylene containing from 8 to 25 carbon atoms with at least 4 carbon atoms between the oxygen atom and carbonyl group and at least 30Z of the groups represented by A carry an epoxy group. 3. Compound according to Claim 2 wherein at least 30% of the groups represented by A are 8,9-epoxy-11-n-heptyl-unadec-1,11-ylene. 4. A compound according to any one of Claims 1 to 3 wherein-at least 50% of the groups represented by A carry an epoxy group. 5. A compound according to any one of Claims 1 to 4 wherein B represents a group Y (- CO -)m in which m is 1 and Y is alkyl, alkenyl or alkapolyenyl containing from 8 to 25 carbon atoms and up to three epoxy groups. 6. A compound according to any one of Claims 1 to 5 wherein the bridging group, Z, is preferably of the formula: EMI33.1 or - O - L - wherein Q is H or an alkyl group containing up to 25 carbon atoms, and L is an alkylene or hydroxyalkylen,e group containing from 2 to 6 carbon atoms. 7. A compound according to anyone of Claims 1 to 6 wherein the amino group represented by R is a primary, secondary or tertiary amino group or a substituted ammonium group of the formula: EMI33.2 wherein T1, T2 and T3 are each independently H, C1 25-alkyl, or C4 8-cycloalkyl and V is a coloured or colourless anion. 8. A compound according to anyone of Claims 1 to 7 wherein the amine group, R, is a polyalkylene imine. 9. A compound according to Claim 8 wherein the amine group, R, is a polyethylene imine, molecular weight in the range 500-100,000. 10. A compound according to Claim 1 which is the adduct of one or more compounds from each of the following classes: (a) an organic compound containing two or more isocyanate groups, (b) an organic compound containing two or more groups. which are reactive with isocyanate groups, and (c) a compound of the formula: : z - X - E-(T - )n-l¯ II wherein Z is OH or NHR and R is a monovalent hydrocarbon group; X is an optionally substituted divalent hydrocarbon group; T is a divalent hydrocarbon radical n is a positive integer Q is an optionally substituted monovalent hydrocarbon group; E is - CO - 0 - or - CO - NR' - wherein R' is a hydrogen atom or a monovalent hydrocarbon group; and D is - CO - 0 provided that only one of E and D is connected to T via the carbonyl atom of a carbonyl group present in D and E, at least one of the groups represented by X, T, Q, contains a carbon chain having at least 5 carbon atoms and at least one of the groups represented by X, Q and T carries an epoxy group. 11. A compound according to Claim 1 wherein at least 30X of the groups represented by A carry an epoxy group. 12. A process for the preparation of a compound according to Claim 1 which comprises reacting an epoxidising agent with a compound of the formula: B - ([0 - A - CO] - J)m . II wherein B, A and J are as previously defined, except that they are free from epoxy groups, and at least 30% of the total number of the groups B, A and J contain a carbon-carbon double bond. 13. A process for the preparation of a compound according to Claim 1 which comprises reacting a compound of the formula B (- W) m with a compound of the formula: HO - A - CO - (O - A - CO)n-1 J III wherein W is a group reactive with hydroxy groups 14. A dispersible composition of a solid and from 1 to 50% by weight, based on the weight of the solid, of a compound according to any one of Claims 1 to 11. 15. A dispersion of from 5% to 85% by weight, based on the total weight of the dispersion, of a solid in an organic liquid containing from 1% to 50% by weight, based on the weight of the solid, of a compound according to any one of Claims 1 to 11. 16. A dispersible composition or dispersion according to Claim 14 or Claim 15 wherein the solid is a pigment. 17.. A dispersion according to Claim 15 or Claim 16 wherein the organic liquid is an aromatic hydrocarbon or an aliphatic or aromatic halogenated hydrocarbon or a mixture of this with and ester, an aliphatic alcohol or a ketone.

Inventors: SCHOFIELD, JOHN DAVID
Applicants: IMPERIAL CHEMICAL INDUSTRIES PLC
Application year: 1984
Main classification: C07D303
IPC codes: C09D7, B01F17, B01J13, C09B67, C07D303, C08G63, C09D17