A METHOD OF MAKING AN ABRASION RESISTANT COATING ON A SOLID SUBSTRATE AND ARTICLES PRODUCED THEREBY

Abstract: Method for providing an improved abrasion resistant coating on solid substrates such as plastic articles and solid articles prepared thereby having on the surface such abrasion resistant coating. A solid substrate is coated with an organosilanol-type coating liquid comprising organosilanol molecules or a partial condensation product thereof. At least 90 mole percent of said organosilanol molecules are trifunctional silanol molecules of the formula RSi (OH)3, R being a hydrocarbon radical, and at least 50 mole percent of said trisilanols being an alkyl trisilanols of 1-3 carbon atoms or phenyl trisilanol. Preferably, at least 70 mole percent of the trisilanol is methyltrisilanol. After the coating is cured by a conventional means, it is post-treated by a glow discharge to afford an abrasion resistance far superior to those obtained from organosilanol coating liquids without glow discharge post-treatment. There is also disclosed a mirrored solid substrate such as a plastic sheet having an improved abrasion resistance which comprises a layer of a glow discharge treated organosiloxane coating and a mirror layer deposited thereon.

Description: A METHOD OF MAKING AN ABRASION RESISTANT COATING ON A SOLID SUBSTRATE AND ARTICLES PRODUCED THEREBY This a continuation-in-part application of a copending application. Serial Number 409,272, filed August 18, 1982. This invention relates to an improved scratch or abrasion resistant coating for a solid substrate and more particularly to such coatings for transparent plastic substrates. The invention also includes a method for providing an improved abrasion resistant coating which comprises coating the substrate with an organosilanol coating liquid, curing the coating, and then subjecting the coated substrate to a glow discharge by placing it preferably in the positive column region thereof. This invention also relates to a mirrored solid substrate comprising a layer of a glow discharge treated organosiloxane coating and a mirror layer vapor-deposited on said organosiloxane coating layer. Background Art There are a large number of references relating to the preparation of an abrasion-resistant coating on a solid substrate such as a plastic material. In light of the various advantages of plastic materials such as light weight, low material cost and ease of shaping, the development of abrasion-resistant coatings for plastic materials is highly significant from a commercial standpoint. Included among those methods commonly used for such a purpose are a group of methods where a liquid coating composition is applied to a solid substrate and another group of methods where a coating layer is prepared by use of a plasma polymerization of a monomer onto the surface of a solid substrate. Various liquid coating compositions suitable for the first group of methods and various monomers suitable for plasma polymerization have been disclosed in the past. There also exist references relating to the post-treatment of a coated layer which improves or modifies the surface properties thereof. Burzynski et al, U.S. 3,451,838 describes a process of coating plastics with an organosiloxane. It discloses that abrasion resistant organpolysiloxane compounds can be prepared by the hydrolysis and condensation of at least one compound embraced by the general formula T Si Z where each T is independently a hydrocarbon radical such as alkyl, alkenyl and aryl and each Z is independently a hydrolyzable group such as halogen, acyloxy and aryloxy. Krekeler, U.S. 3,713,880 describes a process for coating the surface of transparent thermoplastic resins with a solution of a mixture of alkyl silicate, an organosilane and an antistatic additive and thereafter subjecting the coated material to a heat treatment, said organosilane being a compound of the formula R Si X , R-Si X or a mixture thereof, where R is a hydrocarbon radical and X is a hydrolyzable group, namely, a halogen or a lower alkoxy group. Gagnon, U.S. 3,650,808 describes a process for providing an abrasion resistant coating on a polycarbonate surface which comprises priming the polycarbonate surface with a compound of the formula H NR-Si(OR) where is an alkylene group, and OR is an alkoxy group of 1-4 carbon atoms, and thereafter applying to the surface a coating liquid which is produced by heating methyltrialkoxysilane or a mixture of methyl trialkoxysilane and phenyltrialkoxysilane followed by a partial condensation thereof. Clark, U.S. 3,986,997 discloses a pigment-free aqueous coating composition comprising a dispersion of colloidal silica in a lower aliphatic alcohol-water solution of the partial condensate of a silanol of the formula RSi(OH) in which R is selected from the group consisting of alkyl radicals of 1 to 3 inclusive carbon atoms, the vinyl radical, the 3,3,3-trifluoropropyl radical, the gamma-glycidoxypropyl radical and the gamma-methacryloxypropyl radical, at least 70 weight percent of the silanol being CH Si(OH French, U.S. 3,953,115 describes a process for applying an adherent, optically clear, abrasion resistant coating to plastic ophthalmic substrates which comprises (a) forming a partially hydrolyzed solution of a vinyltri(loweralkoxy)silane in a water-miscible volatile organic solvent, the silane concentration being 25-75% by weight, (b) applying a thin, uniform coating of the partially hydrolyzed solution to a clean surface of the ophthalmic lens; (c) maintaining the coated substrate in a high humidity and preferably elevated temperature environment until the silane is substantially completely hydrolyzed; and (d) dehydrating (curing) the coated substrate under low humidity conditions at an elevated temperature. Frye, U.S. 4,277,287 describes an organosilanol coating liquid comprising a dispersion of colloidal silica in an aliphatic alcohol-water solution of the partial condensate of a silanol of the formula RSi(OH) , wherein R is selected from the group consisting of alkyl having from 1 to 3 carbon atoms and aryl, and a small amount of a polysiloxane polyether copolymer, at least 70 weight percent of the silanol being CH Si(OH) , said composition containing 10 to 50 weight percent solids. Kray, U.S. 4,298,655 describes an organosilanol coating liquid comprising a dispersion of colloidal silica in an aliphatic alcohol-water solution of the partial condensate of a silanol of the formula RSi(OH)_, wherein R is selected from the group consisting of alkyl having from 1 to 3 carbon atoms and aryl, a small amount of a beta- dicarbonyl compound, at least 70 weight percent of the silanol being CH Si(OH) , said composition containing 10 to 50 weight percent solids. Suzuki et al, Japan Patent 1839/1980 describes a method of surface treatment of articles wherein the hydrolysis product of a silicon (where R is hydrogen or methyl, R is an alkylene group of 1-6 3 carbon atoms, and R is a hydrocarbon group of 1-8 carbons or an acyl group of 1-4 carbons) is coated on a substrate and thereafter the coating is post-treated with an electron beam having an extremely high kinetic energy, namely, 0.3-3 mega electron volts in order to enhance the abrasion resistance of the coating. The inventors state that the hardening of the coating is believed to be due to the polymerization of acrylate or methacrylate groups effected by the irradiation of the very high energy electron beam. Berger et al, U.S. 4,225,631, describes a process for making an abrasion resistant coating on a polymeric substrate which comprises applying a coating solution of hydrolyzed vinyl(loweralkoxy)silane in a water miscible volatile organic solvent, curing the coated substrate, and subsequently subjecting the cured substrate to ultraviolet radiation. The Berger method relies on the ultraviolet-induced cross-linking of the vinyl groups to produce a harder coating and a better chemical adhesion between the coating and the substrate. Thus, it is an essential requirement in the Berger method that the main ingredient of the starting coating composition be a trifunctional silane monomer having a vinyl group attached to the silicon atom. The term "trifunctional" as used herein signifies that the central silicon atom has three groups attached thereto which are hydroxy groups or groups hydrolyzable to hydroxy groups such as alkoxy groups or.halogens. People skilled in the art also use terms tetrafunctional, difunctional and monofunctional silane monomer. They have the corresponding meanings. For a more detailed explanation of said terms as well as the chemistry of silicon, particularly the chemistry of siloxanes, the reader is referred to standard treatises such as Rochow, "An Introduction to the Chemistry of Silicon", 2nd Ed., John Wiley, New York (1951) . When all of the three OH groups of an organotrisilanol RSi(OH) undergo condensation with OH groups attached to other silanol molecules, the trifunctional silanol gives rise to a trifunctional structural unit (T unit) of polysiloxane network. Said T unit can be depicted by the formula R I - O - Si - O - I 0 I Similarly, a difunctional silanol of the formula R_Si(OH) gives rise to a difunctional structural unit of polysiloxane network, and the tetrafunctional silanol Si(OH) gives rise to a tetrafunctional structural unit of polysiloxane network. Said difunctional structural unit (D unit) and tetrafunctional structural unit (Q unit) can be depicted respectively by the formulas I R O 1 I - O - Si - O - and - o - Si - O - t I R ? / y ξ&RE OMPI ( corrected) In the above three formulas, each unit includes half of each associated oxygen atom. Needless to say, difunctional silanol gives rise primarily to a linear siloxane chain, whereas trifunctional silanol gives rise to a cross-linked siloxane network. It is well known in the art that organosiloxane hard coatings are prepared generally from organosilanol liquid compositions whose main ingredient is trifunctional organosilanol or a partial condensate thereof, whereas softer materials such as siloxane release agents are prepared generally from organosilanol compositions whose main ingredient is difunctional organosilanol. Quite often, organosilanol molecules are formed by virtue of the in-situ hydrolysis of the corresponding hydrolyzable organosilane molecules, such as alkoxy substituted organosilane molecules. The in-situ formed organosilanol molecules present in the coating liquid usually undergo some degree of condensation before the coating liquid is applied to the substrate. In order to avoid repetition, all three forms shall be deemed equivalent to each other for the purpose of describing this invention. Thus, the term organosilanol as used in the specification and the appended claims shall subsume the precursor and the partial condensation product thereof. Precursors of tetrasilanols are not included within the definition of an organosilanol since they hydrolyze to a completely inorganic molecule. Kaplan et al, U.S. 3,843,399 describes a etalized video disc having an insulating layer thereon, where glow discharge is employed to coat the conductive video disc with a polymeric film to obtain a uniform tough dielectric coating which can be repeatedly contacted with a metal tipped stylus without damage. It is stated that monomers suitable for use in forming thin coatings on video discs by glow discharge polymerization include styrene; substituted styrenes; alkyl-substituted silanes such as triethylsilane, tri ethylsilane; tetraethysilane, vinyltrimethylsilane and the like; alkenes and cycloalkenes; alkene-substituted benzenes such as divinylbenzene and the like; halogena ed compounds such as tetrafluoroethylene, methylene chloride and the like; and polysiloxanes such as dimethylpolysiloxane and the like. Mehalso, U.S. 4,018,945 describes a method of improving the long term durability of a dielectric polymer film deposited on a video disc by glow discharge polymerization of a dielectric polymer precursor such as styrene, wherein the dielectric polymer is post-treated by a glow discharge in the presence of an oxygen containing gas. Mehalso et al, U.S. 3,901,994 describes a metalized disc having a dielectric coating thereon wherein a poly-p-xylylene coating is deposited on the metalized disc by a technique such as vapor deposition and then hardened by exposure to a glow discharge. Kaganowicz et al, U.S. 4,072,985 describes a video disc having a dielectric layer formed from styrene in a nitrogen atmosphere in a glow discharge. It is stated that the dielectric layer has improved age deterioration resistance, wear characteristics and adhesion to a metal conductive layer. This is an example of plasma polymerization. Nowlin et al, U.S. 4,123,308 describes a process for chemically bonding a poly-p-xylylene to a thermosetting resin, wherein a low temperature plasma is employed to chemically modify the surface of the poly-p-xylylene to incorporate oxygen atoms into the backbone of the polymer at its surface. Wydeven et al, U.S. 4,137,365 describes an oxygen plasma post- treatment of plastic surfaces coated with plasma polymerized silane monomer wherein a plastic surface is first coated with a polymerized organosilane by use of a plasma polymerization technique conducted in vapor phase and then the coated material is post-treated with an oxygen plasma. It is stated that such oxygen plasma treatment of the coating improves its abrasion resistance. The Wydeven et al disclosure is directed to a situation where a coating is prepared by plasma polymerization of an organosilane monomer having a sufficient vapor pressure to conduct the polymerization in the vapor phase. As examples of organosilanes suitable for their invention, there are mentioned in the patent vinyltrichlorosilane, tetraethoxysilane, vinyltriethoxysilane, hexamethyldisilane, tetramethylsilane, vinyIdimeth lethoxysilane, vinyltrimethox silane, tetravinylsilane, vinyltriacetoxysilane, and methyltrimethoxysilane. Wydeven et al show that the oxygen-plasma post-treatment incorporates oxygen atoms to the polymer treated. There is no teaching in the patent as to plasma treatment of a coating obtained from a liquid coating composition comprising an organosilanol compound or compounds such as the composition described in the aforementioned Clark, Frye or Kray patent. -^3REA MPI In fact, the inventors teach away from using liquid "dip" coating compositions because of problems in controlling the film thickness which in turn affects the abrasion resistance and optical properties of the coated article. Kubacki, U.S. 4,096,315 describes a process for coating an optical plastic substrate which comprises steps of exposing the substrate to a first plasma that forms hydroxy1 groups on said substrate's surface, exposing the substrate to a plasma polymerization using a silicon containing monomer, and exposing the substrate to another plasma treatment in the presence of a gas selected from noble gases, oxygen, nitrogen or air. As examples of suitable silicon containing monomers to be used in the plasma polymerization step, there are mentioned in the patent vinyltrimethylsilane, vin ltri ethylethox silane, vinyldimethylethoxysilane and hexamethyldisilane. In Chapter 4 of a treatise entitled "Thin Film Process", edited by Vossen and Kern, Academic Press, New York (1978) , Yasuda comments on the chemistry involved in the plasma polymerization of three types of hydrocarbon molecules, namely, triple-bond-containing and aromatic compounds (Group I) , double-bond-containing and cyclic compounds (Group II) , and compounds without the aforementioned structures (Group III) . The author states that under glow discharge polymerization conditions Group I forms polymers by utilizing the opening of triple bonds or aromatic structures with the least evolution of hydrogen gas, that Group II forms polymers via both the opening of double bonds or cyclic structures and hydrogen abstractions, the production of hydrogen gas being considerably higher than Group I compounds, and that Group III compounds polymerize primarily by hydrogen abstraction, hydrogen production being much higher than in those in Group II compounds. Based on this explanation of the plasma polymerization process, it follows that when a vinyl-group-containing silane monomer such as vinyltrimethoxysilane, vinyltriethoxysilane or vinyIdimethylethyox silane is plasma polymerized, a substantial amount of carbon-carbon polymer backbone will be formed rather than siloxane type bonds. Hurst, U.S. 3,632,386 describes an oxidative treatment, e.g., electric discharge (corona) or flame treatment of a silicone polymer release surface prepared from a silicone polymer release agent such as solvent-soluble liquid or solid curable silicone rubber polymers, whereby the release properties of the silicone polymer surface is reduced. It is (corrected) stated in the patent that usually, the silicone polymer release agents are believed to have the formula: R being a onovalent hydrocarbon radical, thus indicating that the silicon-containing polymer is substantially linear without any appreciable extent of cross-linking. The Hurst patent * is not directed to abrasion resistant coatings and nothing is mentioned in the patent about the abrasion resistance of the coated surface. The aforementioned prior art references can be broadly classified into (1) those relating to organosiloxane-type coatings prepared from an organosilanol-type coating liquid by applying the liquid to a substrate and curing the coat by drying and/or heating, (2) those relating to the plasma polymerization of organosilane monomers, (3) those relating to the plasma polymerization of non-silicon containing organic monomers such as xylene or styrene, (4) those relating to the plasma treatment of certain types of coated substances, namely, plasma polymerized organosilanes, plasma polymerized hydrocarbons such as xylene and styrene, and linear silicone rubber type polymers and (5) post- treatment of carbon-carbon double bonds remaining in the coated material either with UV light or with an electron beam having a kinetic energy of mega volts range. None of the aforementioned references are directed to a glow discharge post-treatment of organosiloxane coating obtained by applying an organosilanol coating liquid to a solid substrate in order to improve its abrasion resistance. The term "post" as used herein shall mean subsequent to the curing of the coated material by a conventional means such as drying and/or heating. The present inventors have discovered that when an organosiloxane type coating prepared from a common organosilanol coating liquid comprising trifunctional organosilanol molecules of the formula RSi(OH) , R being a hydrocarbon radical, or a partial condensation product thereof is post-treated by a glow discharge by placing the coated substrate preferrably in the positive column region of the glow _ OMPI r ec e discharge, the abrasion resistance of the coating layer is enhanced to a surprisingly large value, quite often approaching that of a common glass. This great enhancement of the abrasion resistance beyond those of organosilanol coatings prepared from such organosiloxane coating liquids by conventional curing methods such as drying and/or heating but without glow discharge post-treatment is truly unexpected. The organosilanol coating liquid composition used in this invention comprises as a main ingredient organosilanol molecules, at least 90 mole percent of the organosilanol molecules being trifunctional organosilanol molecules of the formula RSi(OH) or a partial condensation product thereof, where R is a hydrocarbon radical, and at least 50 mole percent of said trifunctional organosilanols being an alkyltrisilanol having one to three carbon atoms, preferably one, or a phenyltrisilanol. More preferably at least.70 mole percent of the trisilanol should be methyltrisilanol. Thus, there may be present a minor amount of other organosilanol molecules such as difunctional organosilanol molecules or a partial condensation product thereof. The coating liquid composition used in this invention may contain other ingredients. A typical example of such other ingredients is colloidal silica or tetrasilanol or its precursor. See for instance the afore-mentioned Clark, Frye and Kray patents. Usually the colloidal silica is dispersed in a lower aliphatic alcohol-water solution of the partial condensate of organosilanol molecules. Suitable examples of such lower aliphatic alcohol includes methanol, ethanol, isopropanol and t-butanol. Isopropanol is particularly preferred. Needless to say, mixtures of such alcohols can be used. Optionally, minor amounts of other water-miscible polar solvents such as acetone may be present in the coating liquid. The term "organosilanol coating liquid" as used in connection with the instant invention shall mean the coating composition as defined above dispersed or dissolved in a suitable medium. Examples of such coating liquids are disclosed in various references, for instance, Clark U.S. 3,986,997, Frye U.S. 4,227,287 and Kray U.S. 4,298,655. The disclosures of these three references are hereby incorporated by (corrected) reference. The term "organosiloxane coating" as used in connection with the instant invention shall mean an abrasion resistant coating prepared from said organosilanol coating liquid. In the past it has been very difficult, if not impossible, to obtain plastic articles having abrasion resistance anywhere near the abrasion resistance of common glass. As a point of reference in discussing and evaluating the advantages of this invention the following typical abrasion resistance values as measured by a rubbing pad abrader instrument in terms of the number of cycles of tin abrasive motion exerted on the surface of the test piece necessary to bring about an increase of 3% absolute in the haze value of the test piece which is expressed as a percent of scattered light in the light transmitted through the test piece. Three per cent haze is the level at which haze in a lens becomes noticeable and objectionable to consumers. Details of the testing method used to evaluate the abrasion resistance of materials are described later in the specification. Table I ABRASION RESISTANCE OF COMMON MATERIALS Material Cycles for 3% Increase Haze Polycarbonate 7 - 11 Acrylic resin 14 - 19 Allyl diglycol carbonate resin 125 - 150 (CR-39 resin) Glass 3000 - 6000 It has also been discovered in this invention that the glow discharge need not be conducted in a special atmosphere and that any gas or vapor may be used as a glow discharge medium. This has significant commercial advantages when the inventive treatment is applied to the commercial treatment of, for instance, a large number of organosiloxane coated acrylic lenses where a large amount of water vapor is released from the lenses at low pressure and it can be used as a glow discharge medium without any substantial addition of a special gas such as oxygen. OMPI correc e The elimination of the need for the addition of an extraneous gas not only saves the material cost but also reduces the manufacturing cost, because such addition of a gas to the glow discharge chamber leads to an increased load for the vacuum pump system for the chamber. The abrasion resistance of coated plastic articles obtained according to this invention is much larger than the abrasion resistance of coated plastic articles obtained by the conventional method involving the application of an organosilanol type coating liquid (but without a glow discharge post- treatment) , the abrasion resistance obtained by a method involving plasma polymerization of an organosilane plus plasma post-treatment thereof, or the abrasion resistance obtained by plasma polymerization of a hydrocarbon molecule plus a plasma post-treatment thereof. Additionally, it has been discovered that the abrasion or scratch resistance of mirrored coatings may be substantially improved by the use of this invention. In the past when a mirrored coating was applied to a plastic substrate, the abrasion resistance of the resultant product was generally lower than the abrasion resistance of the substrate. It has been found that this deterioration of the abrasion resistance is not encountered if the substrate is coated with an organosiloxane coating and treated with a glow discharge prior to the application of a mirror layer to the coated surface. Disclosure of the Invention There is described an improved abrasion resistant coating sometimes called a "hard-coat" and a method of providing such an improved abrasion resistant coating on various solid substrates. Substrates such as plastics, metals and wood, can be treated according to this invention. This invention is particularly useful for plastic substrates. Plastic materials that can be treated by the method of this invention include allyl diglycol carbonate resins (CR-39 resins), polycarbonates, acrylic resins, polystyrene, polyamides, polyesters and polyvinylchloride. The method of this invention comprises first coating the article with an organosilanol coating liquid, curing the coating by a conventional means such as drying and/or heating, and further treating it with a glow discharge in order to enhance its abrasion resistance. Said organosilanol coating liquid comprises as a main ingredient organosilanol molecules, at least 90 mole percent of the organosilanol molecules being (corrected) trifunctional silanols of the formula RSi(OH) where R is a hydrocarbon radical, and at least 50 mole percent of said trifunctional organosilanols being an alkyltrisilanol having 1 to 3 carbon atom, preferably one or a phenyltrisilanol. The method of this invention is particularly useful for preparing improved abrasion resistant spectacle lenses. Any common gas or vapor such as air, nitrogen, oxygen, water, carbon dioxide or mixtures thereof may be used as a medium for the glow discharge treatment. The glow discharge is conducted with a voltage preferably in the range of 1 - 5 kilovolts at a pressure preferably in the range of 5 - 50 microns for a period preferably in the range of 5 - 60 minutes. There is also disclosed a mirrored solid substrate having an improved abrasion resistance which has a glow discharge treated organo¬ siloxane coating layer and a mirror layer on the outer surface. It is prepared by vapor deposition of a light reflective material such as metal or metal oxide over an organosiloxane coating layer which has been prepared from an organosilanol coating liquid and which has been post-treated by a glow discharge. DETAILS OF THE INVENTION The method of this invention for producing an improved abrasion resistant coating comprises coating a solid substrate with an organosilanol coating liquid, curing the liquid by conventional means such as drying and/or heating, and exposing the coated substrate to a glow discharge post-treatment. The method of this invention is particularly suitable for commercial-scale production of hard coated articles, because among other things, the initial coating of the article with a coating liquid is generally more amenable to commercial-scale production than the vapor phase plasma polymerization method. Furthermore, the abrasion resistance of the coated articles obtained by this invention is much higher than the abrasion resistance obtained by the prior art method of Wydeven, or Mehalso involving a plasma polymerization of an organosilane or a hydrocarbon monomer and an oxygen plasma post-treatment of the coated layer. It is also much higher than the abrasion resistance obtained by the prior art method involving the application to a solid substrate of an organosilanol-type coating liquid but not a glow discharge post-treatment of the coated layer. Any standard method of applying the liquid coating composition may be used in the practice of this invention. Examples of such methods are flow coating, dip coating, spray coating, spin coating, etc. A common method of applying such liquid coating compositions to substrates is to immerse the articles in the liquid composition and thereafter withdraw them from the bath at a predetermined rate. It is usually advantageous to thoroughly clean the substrate surface prior to the application of the coating liquid in order to obtain better coatings. Conventional cleaning liquids such as aqueous detergent solutions and volatile fluorocarbons may be used for this purpose. After withdrawal from the bath, the articles are carefully dried in a dust-free atmosphere and thereafter thermally or U.V. cured. Thermal curing is usually conducted at an elevated temperature such as in the range of 50° - 200°C. depending upon the heat distortion temperature of the substrate. This coating method is commonly called "dip-coating" and it is very suitable for a large scale production of hard-coated plastic articles. The dip-coating method is generally more suitable than plasma polymerization for large scale production of plastic hard coat articles for various reasons including process costs and equipment costs. The typical thickness of a coating layer ^obtained by dip-coating method is about 1 - 3 microns. Plastic substrates suitable for the method of this invention include aliphatic and aromatic polycarbonates such as allyl diglycol carbonate and pol (bisphenol-A carbonate) , acrylic resins such as poly(methylmethacrylate) , polystyrene, polyamide, polyesters and cellulose esters such as cellulose acetate butyrate (CAB) . For sunglass applications polycarbonate and acrylic resins are particularly suitable. The general technique of glow discharge is well-known in the art. In this invention the gaseous medium used for the glow discharge is not limited to any specific molecule such as oxygen. It has been found in this invention that the residual gas remaining in the glow discharge chamber after pumping the system can conveniently be used as such without introduction of any specific gas such as oxygen to the system. As mentioned earlier, this is a svibstantial commercial advantage because it eliminates the need to supply any extraneous gas to the system and hence reduces the pump load and consequently reduces the apparatus costs. Introduction of a constant flow of oxygen gas into the vacuum system can create a fire or explosion hazard in the pumping system, particularly in a commercial scale operation. Thus, it is an advantage of this invention that extraneous supply of oxygen gas is not needed in this invention. It has also been found that glow discharge treatments under oxygen, nitrogen, air, carbon dioxide, and water generally give substantially the same enhancement of the abrasion resistance of the organosiloxane coating. The vapor pressure of the gas in the glow discharge chamber can be 5 - 150 microns, preferably in the range of 5 - 50 microns and more preferably in the range of 5 - 30 microns. The discharge may be conducted in either DC or AC mode, but it is more convenient to use the DC mode of operation. In the DC operation the typical voltage is 1 - 5 kilovolts. The plastic articles to be treated should preferrably be placed within the positive luminous region. The time period required for the glow discharge varies depending on various factors such as the spacing between the adjacent articles and the pressure of the gas within the chamber. In a typical operation, the treatment time is 5 - 60 minutes. The operating conditions required to achieve the ef ects of this invention can vary depending upon the design of the equipment. Factors entering into these equipment variables include electrode geometry, the gas pressure within the chamber, the discharge pathlength, the value of the applied voltage, which is in turn dependent upon the electrical " constants of the power supply, and the number of articles or the amount of surface area requiring treatment. A comprehensive discussion of electrical discharges in gases at low pressure such as is used in the practice of this invention may be found in the texts "Vacuum Deposition of Thin Films", L. Holland, F. Inst. P., (John Wiley & Sons Inc. , New York - 1958) . The term "glow discharge" is intended to mean an electric discharge in a vacuum at a pressure of about 5 to 150 microns created by an effective voltage. The term "glow discharge treatment" or "treated in a glow discharge" is intended to mean treating an article in a glow discharge preferably in the positive column region thereof for an effective time. In a laboratory vacuum chamber used in this work it was found that optimum abrasion resistance was attained when a coated article such as an acrylic lens was .exposed to a glow discharge conducted at a voltage of 1.5 kv, a current of about 40 milliamperes, at a pressure of 5-20 " y&EJi OMPI microns and for a time of about 5 minutes. This work was done using a planetary substrate holder located approximately nine inches from the cathode. In the laboratory chamber, it was found that the pressure could be varied considerably between 5 and 150 microns with improved results being obtained over the range. However, it is believed that for ease of operation, the operating pressure should be no higher than about 50 microns. In a larger unit, an operating pressure of 10 microns was found to produce best results when the plastic substrate was exposed to a water vapor glow discharge, with the operating voltage at 1.5 kv and the current at 400 - 500 milliamperes. Abrasion resistance of a plastic article is an important property in various applications such, as sunglass lenses and glazing. Abrasion resistance of a surface may be evaluated in many ways.' In the area of sunglass lenses a common practice is to place on a convex surface of a sunglass lens an object having a concave surface which matches the convex surface of the lens. An abrasive powder is placed between the two surfaces and the concave surface is made to reciprocate around a vertical axis under a prescribed weight load. This simulates wiping a lens with a cloth containing dust or dirt particles which is the main cause of scratches in sunglass or ophthalmic lenses. Generally as the number of cycles increases, the extent of haze formation on the surface also increases. ' A common procedure is to express results of the test in terms of percent increase in haze after a certain number of cycles. In the sunglass and ophthalmic industry the above abrasion resistance test is conducted using devices known as a rubbing pad abrader and a hazemeter. A detailed description of the test (hereinafter called the "Rubber Pad Abrader Test") used in this application is as follows: Abrader Description The rubbing pad abrader consists of 1/20 H.P. AC motor, coupled to a Zeromax variable speed transmission which is joined by means of an adjustable eccentric joint, steel rod and two ball joints to a moveable steel table in a sliding fit holder. The steel table is attached to the stroking arm through a ball joint and the other end of the stroking arm is fitted with a ball joint and pin. The pin carries the loading weight (100 grams) on one end and the abrading pad holder on the other end. The pad holder with the abrading pad in place (pads received are self- 'ψys. OMPI adhesive after backing is peeled off) has the same curvature as the sample being tested. The sliding steel table is used to dampen vibrations in the drive mechanism and prevents them from being transmitted to the stroking arm. Procedures for Hazemeter and Photometric Unit The hazemeter is described in ASTM D1003-52 and its operation is described below. The hazemeter is turned on and allowed to warm up for a minimum of 30 minutes to allow the instrument to stabilize. The zero point of the Gardner Digital Photometric Unit (Mod. PG5500) is determined by adjustment of the zero point control with no sample in place and the lid shut. When digital display indicates 0.00, the correction for stray light has taken place and the instrument is zeroed to air. The test specimen must be washed with a mixture of deionized water and a detergent (Liqui-nox) then dried using clean air or dry nitrogen. With the sample to be abraded in place the calibrate control unit is adjusted until the digital display indicates 100.00. This step corrects for the transmission of the sample. The sample is removed and the zero point (0.00) rechecked. If the zero point must be readjusted, then the steps of the proceeding two paragraphs have to be repeated until the zero point no longer needs adjustment. Once the zero point and 100% transmission have been equalized the sample is ready for the initial haze reading. This is the digital readout. Procedures for Abrading Samples The felt pad with the adhesive back is attached to the correct holder which matches the curve of the sample to be abraded. A pre-measured amount of grit (Grit #600, Silicon Carbide, Norton Company, Worcester, Mass.) is placed on the felt pad and spread over the surface of the pad evenly. The holder is then lightly tapped on the side until the abrasive grit settles into the felt pad. The pad and holder is then positioned on the ball socket of the abrader arm and carefully lowered onto the sample to be abraded. The abrader counter is then set to a predetermined amount of cycles depending on the material to be tested. The abrader is turned on and the sample abraded the desired number of cycles. Once the sample has been abraded for the predetermined amount of cycles, the sample is removed from the abrader and washed and dried. - yz J The sample is then placed in the hazemeter and a new haze reading to establish the increase in haze over the initial haze reading taken. This is done bringing the digital readout of the haze meter to 100.0 reading with the sphere in a cocked position, then back to the straight through position for the haze reading. A typical set of readings would be as follows: Initial 2nd % Haze Material Haze Cycles Reading Increase CR-39 Resin 0.2% 150 3.4% Haze 3.2% (15% PMMA) It has been discovered in this invention that the glow discharge treatment of an organosiloxane coating layer prepared from an organosilanol coating liquid affords a surprising increase in abrasion resistance. Thus, for instance, plastic articles having thereon a glow discharge treated organosiloxane coating have an abrasion resistance which is much greater than the typical abrasion resistance obtained by the dip coating of the plastic articles with the organosilanol coating liquid but without the post-treatment. The degree of improvement of the abrasion resistance is so large that the resultant abrasion resistance approaches that of common glass. Furthermore, the abrasion resistance of plastic articles obtained by this invention is much greater than those obtained by a process comprising a plasma polymerization of an organosilane or hydrocarbon monomer onto the surface of a plastic article and an oxygen post-treatment of the coating layer. It has also been discovered in this invention that mirrored plastic articles having a superior abrasion resistance can be obtained if the mirroring process is conducted subsequent to the coating of the plastic articles with an organosilanol coating liquid, the curing of the coating by a conventional means and the plasma post-treatment thereof. The resultant abrasion resistance is substantially higher than that obtained by subjecting an uncaoted plastic article to a glow discharge treatment and a mirroring process. BUREA t _ OM?I y // \n? The method for providing a mirror layer on solid articles such as plastics is well known in the art. The term "mirror" is well understood by people skilled in the art, particularly by people skilled in the art of sunglasses and plastic industry. It simply means a thin layer of light-reflective material coated over a substrate such as plastic sheet. Typical examples of such light-reflecting material include, but are not limited to various metals and metal oxides. Suitable examples of such metals include chromium, nickel, titanium and aluminum, chromium and nickel being particularly preferred. Needless to say, one can also use various alloys, a particularly preferred example being Cr-Ni alloy. A suitable example of metal oxide is chromium oxide. Such light-reflective materials have high refractive indicies compared to those of common substrates such as plastics. The mirror layer, of course, need not be totally reflective; in fact, it is only partially reflective in the case of sunglasses. The mirroring process is conducted inside a high vacuum chamber. The mirror material is vaporized, for instance, by electron beam bombardment or resistance heating. The articles to be mirrored are placed at suitable locations within the vacuum chamber in order to obtain vacuum deposition of the mirroring material efficiently and uniformly. The following.general glow discharge treatment procedure was used in the Examples of this application. Deviations from this procedure are noted in the specific Examples. Four vacuum chambers were used to treat the dip coated substrates of the Examples. The first vacuum chamber was a laboratory unit equipped with a diffusion pump and a mechanical vacuum pump connected in series. Coated substrates were placed in a holder located about four to ten inches from the cathode. The vacuum chamber was evacuated to a pressure in the range of 5 to 150 microns and 1 to 5 kv. was applied to the electrode to induce a glow discharge. In this laboratory unit, treatment times of two to about thirty minutes were employed and it was determined that five minutes of treatment produced a satisfactory product having an abrasion resistance of approximately 1000 cycles which is approaching glass. In that experiment, the voltage was approximately 1.5 kv. and the current was about 45 milliamperes. The optimum distance of the substrate from the cathode was determined to be about 4.5 inches, said location being within in the positive glow region of the plasma. In a second unit, experiments were conducted on a larger scale to determine the operating parameters of the process. This unit had a capacity to accommodate 6,000 lens blanks mounted on trays which were in turn mounted on a carrier. Nine rod-shaped cathodes were spaced in parallel to each other between the lens blanks and the carrier upon which they were mounted. The carrier acted as an anode and the horizontal surface upon which the trays holding the lens blanks rested was covered by a mesh screen. The interior wall of the vacuum chamber and all other parts existing therein were made of stainless steel. This unit was equipped with a Roots blower connected in series to a Stokes mechanical pump. In this unit, the lens surfaces were placed perpendicular to the longitudinal axis of the cathode. The large scale unit was evacuated using the mechanical pump to remove the bulk of the vapor from the vacuum chamber to a low vacuum. After a pressure of approximately 20 torr was reached, the Roots blower was actuated and the two units operated in series until a pressure of about 20 microns was attained. The glow discharge was then initiated and the substrates were exposed to the glow discharge for 0.25 to one hour. The third unit was a small bell-jar type vacuum chamber and the fourth unit was a cylindrical vacuum chamber having a diameter of about three feet. The following examples are presented solely for the purpose of illustrating the invention. They should not be construed as limiting the scope of this invention. In the following examples unless specifically indicated otherwise, the plasma medium for the glow discharge treatment was the residual gas or gases (primarily a mixture of air and water vapor) remaining in the chamber after it was evacuated to the operating pressure. EXAMPLE I A number of commercially available plastic lenses were procured and tested for abrasion resistance, using the rubbing pad abrader and hazemeter test. The increase in haze percentage (not percentage or relative increase of haze value) was measured on the abraded samples generally after 150 cycles of abrasive motion. The results were as follows (The term "lens" is used throughout the specification in a loose sense. It may or may not have a vision corrective effect. So-called sunglass lenses usually do not have a vision corrective effect.): Increase in Haze Lens Material Coating Percentage Allyl diglycol carbonate None 2.8 - 3.0 resin (CR-39) Allyl diglycol carbonate American 2.3 resin (CR-39) Optical Permalite* Allyl diglycol carbonate 3M Armalite ! - RLX 1.0 (2.6 resin (CR-39) after 300 cycles) Acrylic resin None 3.0 (after 15 cycles) Acrylic resin Mitsubishi UAR 2.3 - 3.6. Acrylic resin G.E. SHC-1200* 3.2 Acrylic resin Dow ARC* 3.2 - 3.6 Acrylic resin DuPont SAR 3.2 - 3.6 Acrylic resin «* >«A« 11 - 13 Polycarbonate None 3.0 Polycarbonate Dow ARC* 2.8 - 3.0 Polycarbonate G.E. - SHC- 1200* 2.6 Polycarbonate R.C.A. 16 - 26 * organosiloxane coating These results show that allyl diglycol carbonate resin (a widely used sunglass and ophthalmic lens material) has substantially better abrasion resistance than does acrylic resin. The various coatings available on acrylic resin generally elevate the abrasion resistance of the substrate approximately to that of allyl diglycol carbonate resin but none come anywhere close to glass. EXAMPLE II Polycarbonate, acrylic and CR-39 lenses were coated with an organosilanol coating liquid sold by General Electric Company under the designation SHC-1200. The lenses were dip-coated with the organosilanol coating liquid, air cured and then thermally cured at 185°F. The thermally cured lenses were then placed in a laboratory vacuum chamber and treated with a glow discharge under the following conditions: Temperature ambient Pressure 30 microns Time 5 minutes Voltage 1.5 kilovolts Current 35 milliamperes The glow discharge had a purplish color indicating that the glow discharge medium comprised water and air remaining in the chamber after it was evacuated to the operating pressure. The lenses having the glow discharge treated organosiloxane coatings were then tested for abrasion resistance and the percent increase in haze measured. The results were as follows: Lens Material Percent Increase with SHC-1200 in Haze Cycle Allyl diglycol carbonate 0.7 150 resin (CR-39) Acrylic Resin 0.3 150 Acrylic Resin 2.9 - 3.3 1150 Comparison of the above results with those of Example I shows a marked increase of the abrasion resistance of the organosiloxane coated lens afforded by the glow discharge post-treatment of organosiloxane coatings according to the method of this invention. Comparison of the above results, particularly the third item in the table with aforementioned Table I shows that the present invention affords coatings having an abrasion resistance approaching that of common glass. EXAMPLE III Acrylic lenses having an organosiloxane coating were subjected to a glow discharge treatment in the laboratory vacuum chamber using different gases as the major constituent of the discharge medium. All runs were made at 20 micron pressure and for five minutes. The results are expressed in terms of the increase of haze percentage after 125 cycles of abrasive motion. RUN % Haze Increas=e Gas A 0.2 Nitrogen purge B 0.1 tt C 0.2 If D 0.0 Air purge 0.2 n F 0.3 If G 0.3 π H 0.3 M I 0.2 Water vapor J 0.3 n The above results indicate that nitrogen, air and water vapor give.comparable improvements when they are used as a medium for the glow discharge treatment. EXAMPLE IV Part (A) Organosiloxane coatings. Plastic substrates having various organosiloxane coatings were obtained from different sources and given a glow discharge treatment under the conditions described in Example II. The effectiveness of the glow discharge treatment for increasing the abrasion resistance of the organosiloxane coatings is summarized below in terms of the percentage increase in haze after 125 cycles of surface abrasion using the rubbing pad abrader test. % Haze Increase After Run Substrate Coating Control Treatment Acrylic G.E. 2.7% 0.2% SHC 1200 B Acrylic Dow ARC 3.3% 0.7% Acrylic American 2.9% 0.1% Optical Permalite (tintable) (EXAMPLE IV continued) D Acrylic Toray 4.0% 0.9% (non-tintable) E Polycarbonate Owens- 6.7% 0.4% Illinois O.I. 650 F Polycarbonate G.E. 3.7% 0.7% SHC-1200 Part (B) Organic coatings. Light-polarizing sheets (polarized sheets) having different organic type abrasion resistant coatings were subjected to a glow discharge treatment and- the abrasion resistance tested in the same manner as Part (A) . The polarized sheets obtained from two sources had a central polyvinylalcohol layer and, on both sides thereof, a cellulose acetate butyrate layer. The results are summarized below. % Haze Increase After Run Substrate Coating Control Treatment G Polarized Sheet Melamine- 3.0%* 2.9% (Source 1) Formaldehyde H Polarized Sheet Ethylene 3.2% 5.9% (Source 2) Glycol Dimethacrylate I Polarized Sheet Poly- . 1.4% 6.3% (Source 1) urethane * (after 35 cycles) The results of Part (A) show that all of the organosiloxane coatings improved in abrasion resistance after the glow discharge treatment, whereas the results of Part (B) show that the abrasion resistance of the organic coatings did not improve after the glow discharge treatment. EXAMPLE V Molded acrylic lenses were vacuum deposited with poly-p-xylylene coatings substantially in accordance with the method of Mehalso et al U.S. Patent 3,901,994. The lenses were coated with two thicknesses; (a) 2 microns (lenses C and D); and (b) 4 microns (lenses C & E) . Samples of each thickness were subjected to the glow discharge treatment set forth in Example II. The abrasion resistance of these samples (increase of haze after 125 cycles of abrasion) is summarized below. Sample A is an acrylic lens coated with the aforementioned organosilanol coating liquid SHC-1200 and air and thermally cured as described in Example II. Sample B is an acrylic lens coated with SHC-1200, air and thermally cured and glow-discharge treated as described in Example II. The discharge medium was the residual gas remaining in the chamber after evacuating it to the operating pressure. % Increase Lens Coating Glow Discharge in Haze A Organosiloxane No 2.8 ε n Yes 0.1 C oly-p-xylylen No 54.2 D N Yes 30.2 E fl No 62.9 F If Yes 12.7 The above results show that the poly-p-xylylene coatings, even after the glow discharge treatment, generally have abrasion resistance lower than that of a conventional organosiloxane coating prepared from an organosilsnol coating liquid but not post-treated with glow discharge. EXAMPLE VI Seven acrylic lenses were coated with vinyltrimethoxysilane using a radio frequency plasma polymerization technique substantially in ccύ uάiiuB with the procedures set forth in Wydeven U.S. Patent 4,137,365. The time and pressure of the plasma polymerization process was varied to produce a range of results. Only three of the samples had a coating thickness comparable to that described by Wydeven. Those three samples were cut in half, a control half was tested for abrasion resistance and the other half was treated in a glow discharge for five minutes in the planetary configuration under a pressure of 20 microns and a voltage of 2 kilovolts, and its abrasion resistance was measured. The results are as follows: % Haze Increase - 125 cycles Run Coating Thickness Control Glow Discharge A 0.7 microns 16.3 7.3 B 0,5 microns 14.4 9.6 C Thin ( 0.25 microns) 10.0 10.0 For comparison, the percent haze increase in an acrylic lens having an organosiloxane coating of 1.5 - 2.0 micron thickness and treated with a glow discharge was 0.1%. An uncoated acrylic lens given the same abrader test showed a percent increase in haze of 13.4%. These results show that although there can be some improvement in the abrasion resistance of plasma polymerized vinyltrimethoxysilane, the result does not approach that of the glow discharge treated organosiloxane coatings. EXAMPLE VII Acrylic lenses were coated with the organosilanol coating liquid used in Run (B) of Example IV, (see Clark U.S. Patent 3,986,997) and the effect of the cure time upon the abrasion resistance was studied. These lenses were annealed, coated and cured for 2 hours, 4 hours, 8 hours, 12 hours and 16 hours. The samples were tested on one date and then retested several days later to confirm the original abrasion resistance results. The results are summarized below: Coating - Dow ARC Cure Time Cycles % Haze Buildup Test No. 1 Test No. 2 2 hours 125 3.0-3.0 2.8-2.9 4 hours 125 2.8-3.0 3.0-3.1 8 hours 125 2.7-2.8 2.9-3.0 2 hours 125 2.7-2.7 2.7-2.9 6 hours 125 3.5-3.5 3.3-3.5 A similar experiment was also conducted using the aforementioned organosilanol coating liquid SHC-1200 sold by General Electric Co. No significant improvement of abrasion resistance was observed after four hours of curing. The above results indicate that in the absence of the glow discharge treatment according to this invention, there is a certain limit to the abrasion resistance obtained by the organosiloxane coatings regardless of the cure time and that the method of this invention affords an abrasion resistance far superior to those obtained by such a conventional method. It is believed that the glow discharge post-treatment step according to this invention accomplishes something more than a mere completion of the conventional curing of the organosiloxane coating liquid. EXAMPLE VIII This example illustrates how one can vary operating conditions for the glow discharge and still obtain the improved abrasion resistance coatings of this invention. Acrylic lenses having an organosiloxane coating were loaded into the large vacuum chamber previously described. Only a small number of lenses were loaded for these experiments, approxi¬ mately two full trays, or 480 lenses. Random samples were taken from each experiment after the glow discharge treatment and tested for abrasion resistance. The operating conditions and results are summarized below: Pressure Time- Voltage Current Average % fc-n Microns Mins. kv. mA Haze Incr. A 5 30 2.4 320 0.03 B 10 30 2.2 350 0.40 C 20 30 1.6 390 0.77 D 40 30 1.0 450 1.3 This data indicates that in this equipment, the optimum working pressure is between 5 and 10 microns. • φjKE OMPI EXAMPLE IX A small bell jar chamber was used to obtain a comparison between the effects of an AC voltage and a DC voitage. The AC voltage source was a transformer rated at 10 kv at 23 mA output. Regulation with this transformer was difficult. The DC voltage was obtained from the power supply of the small vacuum chamber unit previously described. The chamber atmosphere was the residual gas remaining after evacuation of the chamber to the operating pressure and it was predominantly water vapor. Acrylic lenses coated with the General Electric SHC 1200 organosilanol coating liquid were used in this experiment. % Haze Pressure Voltage Duration . Increase Run Microns kv Mode min. 125 cycles A 40-50 10 AC 4 1.2 B 40-50 10 AC 4 1.1 C 40-50 10 AC 4 1.7 D 100 10 AC 5 1.7 E 100 10 AC 5 1.3 F 100 0.7 DC 5 1.3 G 30-78 0.7 DC 5 0.7 H ' 70-100 0.7 DC 5 0.8 I 55-150 0.7 DC 5 0.9 The results show that the process works with either AC or DC but that DC is the preferred embodiment. EXAMPLE X A series of runs were conducted to determine the abrasion resistance of mirrored plastic lenses. Acrylic and polycarbonate lenses were coated with the aforementioned organosilanol coating liquid SHC-1200, air and thermally cured in the manner described in Example II. The cured lenses were glow discharge treated in a cylindrical chamber of about three feet in diameter under 10-15 micron pressure of a gaseous matter (primarily water and air) for three minutes with 2.5 kv of DC voltage. The post-treated lenses were then subjected to an electron beam -fJ E OMPI deposition (mirroring) process conducted in the same vacuum chamber used for the glow discharge treatment. Chromium metal was used as the mirroring material and the electron beam deposition conducted under a -4 -5 vacuum of 10 -10 torr range for approximately a few minutes in order to obtain one of two thicknesses: one called "regular mirror" having a thickness of about 150 Angstrom and the other called "light mirror" having a thickness of about 60 Angstrom. For the sake of comparison, the abrasion resistance of a mirrored glass prepared by an electron beam deposition of chromium over a glass was also evaluated. Also evaluated for the sake of comparison was the abrasion resistance of mirrored lenses obtained by subjecting uncoated acrylic, polycarbonate and allyl diglycol carbonate lenses to the glow discharge treatment and the mirroring process described above. The results are summarized in the table below, where .the term "coated" means dip-coated with the above mentioned coating liquid, air and thermally cured and glow discharge treated in the manner described above. REGULAR MIRROR LIGHT MIRROR % Haze % Haze Cycles Increase Cycles Increase Uncoated acrylic 50 17.6% 50 16% Uncoated polycarbonate 50 18.9% 50 15.1% Uncoated allyl diglycol 50 2.1 50 3.8 carbonate Coated acrylic 125 0.2% 125 0.3% Coated polycarbonate 125 0.4% 125 0.0% Glass 125 0.8% 125 1.0% The results of this experiment show that the organosiloxane coatings treated in accordance with this invention produce superior mirrored lenses. Note that uncoated acrylic, polycarbonate, and allyl diglycol carbonate lenses exhibit no such improvement. It is noticed that just as glow discharge treatment of uncoated acrylic, polycarbonate and allyl diglycol carbonate resins does not bring out any substantial improvement of abrasion resistance, no substantial improvement of abrasion resistance is obtained by subjecting these plastic materials to a glow discharge treatment and a mirroring process f E unless the materials are previously coated with organosiloxane coating. EXAMPLE XI Acrylic lenses coated in the manner described in Example II were subjected to a glow discharge treatment under different gaseous atmospheres. The laboratory vacuum chamber was used for these experiments and a free flow of gas through the chamber was maintained during the experiments. All experiments were conducted at a voltage of two kilovolts and except for Run A at a pressure of 20 microns. Run A was conducted at a pressure of 10 microns. After the glow discharge treatment the samples were tested for abrasion resistance by abrading them until a three percent increase in haze was observed. The number of cycles required to produce this percent haze increase and the operating conditions for the experiments are- set forth below: Run Gas Time Min Cycles A Nitrogen 20 1000 B Air 5 1900 C Nitrogen 5 1000-1375 D Carbon Dioxide 5 1500-2500 E Nitrogen 10 1125 F Nitrogen 20 1000-3000 These experiments show that any gas may be used as the plasma medium and that the abrasion resistance of the treated lenses approaches that of common glass. As is apparent from the foregoing description of the invention the process of this invention has been found to improve the abrasion resistance of articles coated with G.E. SHC-1200 liquid to an unequaled high level. It works well for numerous other organosiloxane coatings. It does not appear to work well on organic coatings, plasma polymerized p-xylylene, or plasma polymerized vinyltrimethoxysilane. -^J E OMPI Mirrored lenses having surprisingly high abrasion resistance can be obtained if the substrate has a glow discharge-treated organosiloxane coating. Mirroring of plastic articles not having glow discharge-treated organosiloxane coating does not afford such a high abrasion resistance. The glow discharge post-treatment of this invention appears to involve something other than a mere completion of the conventional curing of organosiloxane coating since extended conventional cures of the organosiloxane coatings do not improve their abrasion resistance. The improvement of abrasion resistance is substantially independent of the gas present in the discharge chamber, and the glow discharge treatment is most effective when the substrate is placed in the positive column of a DC discharge at low pressures. - J E i OMPI

Claims: , (twice corrected/31, October 1983) WHAT IS CLAIMED IS: 1. A method of improving the abrasion resistance of cross-linked organosiloxane coating, said coating having been prepared by applying to a solid substrate an organosilanol coating liquid comprising as a main ingredient organosilanol molecules, at least 90 mole percent of which being trifunctional silanols of the formula RSi(OH)_ where R is a hydrocarbon radical, and at least 50 mole percent of said trifunctional silanols being an alkyltrisilanol of 1-3 carbons or phenyltrisilanol, or a precursor thereof or a partial hydrolysis product thereof and by curing the resultant coating in order to obtain an abrasion resistant, cross-linked organosiloxane coating, which method comprises a glow discharge treatment of said cross-linked organosiloxane coating under a pressure range of from about 5 to about 150 microns. 2. The method as defined in Claim 1 wherein the glow discharge treatment is conducted under a pressure within the range of 5-50 microns. 3. The method as defined in Claim 1 wherein at least 50 mole percent of the trifunctional silanols is methyltrisilanol. 4. The method as defined in Claim 3 wherein at least 70 mole percent of the trifunctional silanols is methyltrisilanol. 5. The method as defined in Claim 1, wherein the solid substrate is a plastic material. 6. The method as defined in Claim 5, wherein the plastic material is selected from the group consisting of acrylic resin, polycarbonate resin, allyl diglycol carbonate resin, polyester resin, polyamide resin, polystyrene resin and cellulose ester resin. * §WE ^ OMPI - 32 - (corrected) 7. A solid substrate coated with an abrasion-resistant cross-linked organosiloxane coating comprising the cross-linked condensation product of organosilanol molecules at least 90 mole percent of which being trifunctional silanols of the formula RSi(OH) where R is a hydrocarbon radical, and at least 50 mole percent of said trifunctional silanols being an alkyltrisilanol of 1-3 carbons or phenyltrisilanol, a precursor thereof or a partial hydrolysis product thereof that has been glow discharge treated at a pressure of 5-150 microns subsequent to condensation and crosslinking. 8. The solid substrate as defined in Claim 7 wherein the glow discharge treatment is conducted under a pressure within the range of 5-50 microns. 9. The solid substrate as defined in Claim 7 wherein at least 50 mole percent of the trifunctional silanols is methyltrisilanol. 10. The solid substrate as defined in Claim 9 wherein at least 70 mole percent of the trifunctional silanols is methyltrisilanol. 11. The solid substrate as defined in Claim 7 wherein the solid substrate is a plastic material. 12. The solid substrate as defined in Claim 11 wherein the plastic material is selected from the group consisting of acrylic resin, polycarbonate resin, allyl diglycol carbonate resin, polyester resin, polyamide resin, polystyrene resin and cellulose ester resin. OMPI - 33 - (corrected) 13. A solid substrate having (a) an abrasion-resistant cross-linked organosiloxane coating comprising the cross-linked condensation product of organosilanol molecules at least 90 mole percent of which being trifunctional silanols of the formula RSi(OH) where R is a hydrocarbon radical, and at least 50 mole percent of said trifunctional silanols being an alkyltrisilanol of 1-3 carbons or phenyltrisilanol, a precursor thereof or a partial hydrolysis product thereof that has been glow discharge treated at a pressure of 5-150 microns subsequent to condensation and crosslinking and (b) a metallic layer deposited by a vapor deposition method on said organosiloxane coating. 14. The solid substrate as defined in Claim 13, wherein the solid substrate is a plastic material. 15. The solid substrate as defined in Claim 14, wherein the plastic material is selected from the group consisting of acrylic resin, polycarbonate resin, allyl diglycol carbonate resin, polyester resin, polyamide resin, polystyrene resin and cellulose ester resin. 16. A solid substrate coated with an abrasion-resistant organosiloxane coating having siloxane cross-linkages, which solid substrate having an abrasion resistance such that the number of cycles of abrasive motion required to increase the haze value of the solid substrate by 3% is at least 500 as determined by the rubbing pad abrader test method under 100 gram load. 17. The solid substrate as defined by Claim 16 wherein the solid substrate is a plastic material. 18. The solid substrate as defined by Claim 17 wherein the plastic material is selected from the group consisting of acrylic resin, polycarbonate resin, allyl diglycol carbonate resin, polyester resin, polyamide resin, polystyrene resin and cellulose ester resin.

Inventors: HADDAD THEODORE A, PHILLIPS RICHARD A, HADDAD, THEODORE, A., PHILLIPS, RICHARD, A.
Applicants: FOSTER GRANT CORP, FOSTER GRANT CORPORATION
Application year: 1983
Main classification: B32B9
IPC codes: B05D3, B05D7, B32B7, B32B9, B32B15, C08J7, C09D183, C23C14, G02B1