PROCESS FOR PRODUCING PITCH FOR USING AS RAW MATERIAL FOR CARBON FIBERS

Abstract: A process for producing a pitch which is used as a raw material for producing carbon fibers is disclosed. The process comprises subjecting a petroleum heavy residual oil to hydrogenation treatment in the presence of catalysts, removing a low boiling point fraction of the oil reduced pressure distillation, subjecting the resulting reduced press­ ure distillation residual oil to solvent extraction treatment, and carrying out thermal modification of the resulting extraction component. By utilizing the process for producing the pitch it is possible to use a wide variety of different types of oils in order to produce carbon fibers. The carbon fibers produced from the pitch produced according to the disclosed process have desirable characteristics.

Description: PROCESS FOR PRODUCING PITCH FOR USING AS RAW MATERIAL FOR CARBON FIBERS The present invention relates to a process for producing a pitch (which is an improved raw material for producing carbon fibers having a high modulus of elasticity), using a petroleum heavy residual oil. In pitches which are used as a raw material for producing carbon fibers having excellent strength and excellent modulus of elasticity, optical anisotropy is observed by a polarizing microscope. It has been believed that such pitches contain a mesophase. Further, these pitches used as a raw material for carbon fibers need not possess only optical anisotropy but must also be capable of being stably spun. -Accordingly, in order to produce carbon fibers having excellent strength and excellent modulus of elasticity, it is not always possible to use any material as the raw material for making pitches. Materials having specified properties are required. However, in many published patents, for example, U.S. Patents 3,976,729 and 4,026,788, the raw material is not specifically described or disclosed in the patent specifications and it appears as if pitches used as a raw material for carbon fibers can be produced by carrying out thermal modification of a wide variety of raw materials. However, when the detailed descriptions and examples in such patents are examined in detail, it becomes apparent that desired pitches can only be produced by using the specified raw materials described in the examples of such patents. For example, U.S. Patent 4,115,527 discloses that substances such as chrysne or tarry materials by-produced during the high temperature cracking of petroleum crude oil are suitable for producing the pitch, i.e., a carbon precursor, but conventional petroleum asphalts and coal tar pitches are not suitable. U.S. Patent 3,974,264 discloses that an aromatic base carbonaceous pitch having a carbon content of about 92 to 96% by weight and a hydrogen content of about 4 to 8t by weight is generally suitable for preparation of a mesophase pitch. It has been described that elements excepting carbon and hydrogen, such as oxygen, sulfur and nitrogen, should not be present in an amount of more than about 4% by weight, because they are not suitable. Further, it has been described that the precursor pitch used in Example 1 of the same patent publication has properties comprising a density of 1.23 g/cc, a softening point of 1200C, a quinoline insoluble content of 0.83% by weight, a carbon content of 93.0%, a hydrogen content cf 5.6%, a sulfur content of 1.1 ó an an ash content of 0.044%. Even if the density of 1.23 g/cc in these properties is maintained, petroleum fractions having such a high density are hardly known in conventional petroleum fractions. U.S. Patents 3,976,729, 4,026,788 and 4,005,183 also describe examples wherein the pitch is produced using a specified raw material. The properties of heavy petroleum oils actually depend essentially upon the properties of crude oils from which they were produced and the process for producing the heavy oil. However, it is rare for heavy oils to have the suitable properties described in the above examples, and such oils are often not available. Accordingly, in order to produce carbon fibers having excellent strength and excellent modulus of elasticity industrially in a stabilized state using petroleum heavy oils, it is necessary to develop a process for producing a pitch wherein the properties of the finally resulting pitch are stabilized even if the properties of the raw materials used for making the pitch vary. The present invention relates to a process for producing an improved pitch which is used for producing carbon fibers having a high modulus of elasticity. The pitch is produced industrially in a stabilized state using not only a specified raw material but also an easily available petroleum heavy residual oil. The pitch used for producing carbin fibers having a high modulus of elasticity is produced by a process which comprises subjecting a petroleum heavy residual oil to hydrogenation treatment in the presence of a catalyst, removing a low boiling point fraction by reduced pressure distillation, subjecting the resulting reduced pressure distillation residual oil to solvent extraction treatment with using an organic solvent, and carrying out thermal modification of the resulting extraction component. There are a large number of different petroleum heavy residual oils and the properties of them vary over a fairly wide range depending upon the different crude oils from which they are produced or the process for producing them from crude oils. The hydrogenation treatment by which the above-described difference is reduced is carried out in the presence of a catalyst at a temperature of 370 to 4500C, preferably 380 to 4100C, a pressure 2 of 70 to 210 Kgf/cm , preferably 100 to 170 Kgf/cm2, a liquid space velocity of 0.4 to 2.0 He 1, preferably 0.4 to 1.0 Her , and a ratio of hydrogen/oil of 700 to 1,700 Nm3/KQ, preferably 800 to 1,500 Nm3/Ki. By such a process components contained in the petroleum heavy residual oil, such as sulfur, nitrogen, oxygen and slight amounts of metals, etc., are removed. Further, at the same time, the amount of aromatic components having a comparatively high molecular weight such as asphaltenes is reduced by the hydrogenation treatment. Petroleum heavy residual oils to be subjected to such hydrogenation treatment have a boiling point of' 300"C or more and are prepared with a conventional distillation apparatus used in the petroleum industry. The conditions of the hydrogenation treatment are suitably controlled within the above-described ranges according to properties of the petroleum heavy residual oil. The petroleum heavy residual oil is first subjected to hydrogen treatment and then processed by a reduced pressure distillation apparatus to remove a low boiling point fraction. The low boiling point fraction to be removed in this case means a fraction having a boiling point of about 450"C or less an-d, preferably, 500"C or less when distilling by means of a reduced pressure distillation apparatus conventionally used in the petroleum industry. The resulting reduced pressure distillation residual oil is then subjected to solvent extraction treatment using an organic solvent, and the component extracted with the solvent is taken out. This solvent extraction treatment is carried out in order to reduce the amount of the asphaltene in the reduced pressure distillation residual oil, by which the asphaltene is nearly completely removed in addition to the effect of removing the asphaltene by the abovedescribed hydrogenation treatment. The asphaltene is one component in case of analyzing by solvent fractionation. More specifically, it is the component which is insoluble in n-heptane and soluble in benzene when carrying out solvent fractionation. The solvent extraction treatment is carried out using saturated hydrocarbon compounds as a solvent which have 3 to 7 carbon atoms. These compounds may be one or more of propane, butane, pentane, hexane and heptane. When the treatment is carried out the ratio of solvent to oil is 3:1 to 15:1, the temperature is 50 to 2'300C 2 and the pressure is 5 to 50 Kgf/cm . Thereby, the extraction component is removed. The condition of solvent extraction treatment is suitably controlled with consideration to the properties of the reduced pressure distillation residual oil and properties of the extraction component. As described above, since sulfur, nitrogen, oxygen, metals and asphaltene, etc., are removed from the petroleum heavy residual oil by carrying out hydrogenation treatment, reduced pressure distillation and solvent treatment, the difference in the properties is finally eliminated resulting in a product having uniform properties, even if the initial properties of the petroleum heavy residual oil are fairly different from others. The sulfur content, vanadium content, nickel content, and asphaltene content in the extraction component which are removed from the petroleum heavy residual oil are 2.5 wt% or less, 15 ppm or less, 7 ppm or less, and 0.05 wt% or less, respectively. Further, the properties of the oils become suitable for the following thermal modification. The above-described extraction component is then subjected to thermal modification under a condition comprising a temperature of 390 to 4300C to obtain a pitch used as a raw material for carbon fibers. It is necessary that the time for thermal modification is controlled within a range such that infusible materials which obstruct spinning are not formed when carrying out melt spinning of the above-described pitch used as a raw material for carbon fibers. As described above, properties of the petroleum heavy residual oils may be fairly different from each other. Therefore, it is generally difficult to directly produce a pitch used as a raw material for carbon fibers having a high strength and a high modulus of elasticity from every petroleum heavy residual oil. However, some oils may be used for directly producing the pitch used as a raw material for carbon fibers having a high strength and a high modulus of elasticity. The present invention is characterized by the fact that the pitch used as a raw material for the carbon fibers having a high modulus of elasticity can be produced industrially and stably using various kinds of petroleum heavy residual oils including the petroleum heavy residual oils hich cannot be used for producing the pitch by the conventional process, by carrying out a series of processings comprising hydrogenation i reduced pressure distillation + solvent extraction + thermal modification. The pitch thus produced by the invention is utilized to produce the carbon fiber. The carbon fiber can be produced by the conventional processes, for example, the process as described in U.S. Patent 3,767,741 which comprises spinning the pitch as a raw material, infusiblizing and carbonizing. In the following, the present invention is illustrated in greater detail by examples. However, the invention is not limited to these examples. EXAMPLE 1 After a heavy residual oil having a boiling point of 350"C or more prepared by distillation of Middle East crude oil (A) was subjected to hydrogenation treatment under a condition comprising a temperature of 390"C, 2 a pressure of 160 Kgf/cm , a liquid space velocity of 0.5 Hr 1 and a ratio of hydrogen/oil of 1,000 Nm3/K±, a fraction having a boiling point of 500"C or less was removed by reduced pressure distillation. The resulting reduced pressure residual oil was subjected to solvent extraction treatment with heptane as a solvent under a condition comprising a ratio of solvent to oil of 10:1, 2 a temperature of 1800C and a pressure of 40 Kgf/cm . The resulting extraction component was subjected to thermal modification at a temperature of 410"C for 10 hours to obtain.a pitch used as a raw material for carbon fibers. Properties of the heavy residual oil from Middle East crude oil (A) used as a raw material, those of the solvent extraction component and those of the pitch used as a raw material for carbon fibers are shown in Table 1. Further, carbon fibers which were obtained by melt spinning of the above-described pitch used as a raw material for carbon fibers at 360"C, infusiblizing at 2600C in the air and carbonizing at 1,0000C had a tensile strength of 11 tons/cm2 and a modulus of elasticity of 1,000 tons/cm2. When the fibers prepared by carbonizing at 1,000"C were additionally graphitized at 1,800 C, they had a tensile strength of 15 tons/cm2 and a modulus of 2 elasticity of 2,100 tons/cm EXAMPLE 2 After a heavy residual oil having a boiling point of more than 350"C prepared by distillation of Middle East crude oil (B) was subjected to hydrogenation treatment under a condition comprising a temperature of 2 390"C, a pressure of 160 Kgf/cm , a liquid space velocity of 0.5 Her 1 and a ratio of hydrogen/oil of 1,000 Nm3/KL, a fraction having a boiling point of 500"C or less was removed by reduced pressure distillation. The resulting reduced pressure residual oil was subjected to solvent extraction treatment with heptane as a solvent under a condition comprising a ratio of solvent to oil of 10:1, 2 a temperature of 1800C and a pressure of 40 Kgf/cm2. The resulting extraction component was subjected to thermal modification at a temperature of 400"C for 15 hours to obtain a pitch used as a raw material for carbon fibers. Properties of the heavy residual oil from Middle East crude oil (B) used as a raw material, those of the solvent extraction component and those of the pitch used as a raw material for carbon fibers are shown in Table 1. Further, carbon fibers which were obtained by melt spinning of the above-described pitch used as a raw material for carbon fibers at 370"C, infusiblizing at 260"C in the air and carbonizing at 1,000 C had a tensile strength of 10 tons/cm2 and a modulus of 2 elasticity of 1,000 tons/cm2. COMPARATIVE EXAMPLE 1 A heavy residual oil having a boiling point of 350"C or more prepared by distillation of Middle East crude oil (A) was subjected to reduced pressure distillation to remove a fraction having a boiling point of 500 C or less. The resulting reduced pressure distillation residual oil was subjected to thermal modification at a temperature of 410"C for 10 hours. Properties of the heavy residual oil from Middle East crude oil (A) used as a raw material and those of the pitch in this case are shown in Table 1. When fibers were produced by melt spinning of the above-described pitch at 350"C, infusiblizing at 260"C in the air and graphitizing at 1,000 C, they had 2 a tensile strength of 5.5 tons/cm2 and a modulus of 2 elasticity of 350 tons/cm2* TABLE 1 Comparative Example 1 Example 2 Example 1 Properties of raw material Specific gravity &commat; 15/4 C 0.955 0.960 0.955 Kinetic viscosity cSt &commat; ;50 C 230 550 230 Residual carbon content wt% 8.5 11 8.5 S wt% 3.0 4.3 3.0 N ppm 1,950 2,200 1,950 V ppm 29 60 29 Ni ppm 8 15 8 Asphaltene content wt 2.0 3.2 2.0 Properties of component after solvent extraction treatment by process of the present invention Specific gravity &commat; 15/4"0 0.940 0.951 Kinetic viscosity cSt &commat;100 C 26.1 30.5 Residual carbon content wt% 6.1 7.6 S wt% 1.2 2.2 N ppm 300 310 V ppm 5 10 Ni ppm 3 5 Asphaitene content wt% 0.03 0.04 Properties of pitch Specific gravity &commat; ; 25/25"0 1.30 1.32 1.32 Softening point CC 330 320 335 Quinoline insoluble content 19.8 18.5 23.1 wt% While the invention has been described in detail and with reference to specific embodiments thereof, it will be apparent to one skilled in the art that various changes and modifications can be made therein without departing from the spirit and scope thereof.

Claims: CLAIMS: 1. A process for producing a pitch for using as a raw material for producing carbon fibers, comprising the steps of: subjecting a petroleum heavy residual oil to hydrogenation treatment in the presence of a catalyst, removing a low boiling point fraction of the oil by reduced pressure distillation, subjecting the resulting reduced pressure distillation residual oil to solvent extraction treatment using an organic solvent, and carrying out thermal modification of the resulting extraction component. 2. A process for producing a pitch for using as a raw material for producing carbon fibers as claimed in Claim 1, wherein a petroleum heavy residual oil comprising a fraction having a boiling point of 300"C or more is used as the petroleum heavy residual oil. 3. A process for producing a pitch for using as a raw material for producing carbon fibers as claimed in Claim 1, herein the hydrogenation treatment is carried out under a condition comprising a temperature 2 of 370 to 450 C, a pressure of 70 to 210 Kgf/cm2, a liquid space velocity of 0.4 to 2.0 Hr 1, and a ratio of hydrogen/oil of 700 to 1,700 Nn3/K±. 4. A process for producing a pitch for using as a raw material for producing carbon fibers as claimed in Claim 1, wherein a fraction having a boiling point of about 450"C or less is removed by reduced pressure distillation. 5. A process for producing a pitch for using as a raw material for producing carbon fibers as claimed in Claim 1, wherein saturated hydrocarbon compounds having 3 to 7 carbon atoms are used as an organic solvent. 6. A process for producing a pitch for using as a raw material for producing carbon fibers as claimed in Claim 1, wherein the solvent extraction treatment is carried out under a condition comprising a ratio of the solvent to oil of 3:1 to 15:1, a temperature of 50 to 230"C and a pressure of 5 to 50 Kgf/cm2. 7. A process for producing a pitch for using as a raw material for producing carbon fibers as claimed in Claim 1, wherein the solvent extraction component is subjected to thermal modification under a condition comprising a temperature of 390 to 4300C. 8. A process for producing a pitch for using as a raw material for producing carbon fibers, comprising the steps of: subjecting a petroleum heavy residual oil comprising a fraction having a boiling point of 300"C or more to hydrogenation treatment in the presence of a catalyst under a condition comprising a temperature of 370 to 450 C, a pressure of 70 to 210 Kgf/cm2, a liquid -l space velocity of 0.4 to 2.0 Hr 1 and a ratio of hydrogen/oil of 700 to 1,700 Nm3/K, removing a fraction having a boiling point of 5000C or less by reduced pressure distillation, subjecting the resulting reduced pressure distillation residual oil to solvent extraction treatment using a saturated hydrocarbon compound having 3 to 7 carbon atoms as a solvent under a condition comprising a ratio of solvent to oil of 3:1 to 15:1, a temperature of 50 to 230"C and a pressure of 5 to 50 Kgf/cm2, and carrying out thermal modification of the resulting extraction component under a condition comprising a temperature of 390 to 43000. 9. A process for producing a pitch for using as a raw material for producing carbon fibers as claimed in Claim 1, wherein the sulfur content, vanadium content, nickel content and asphaltene content in the extraction component are 2.5 wt or less, 15 ppm or less, 7 ppm or less, and 0.05 wtt or less, respectivel-y.

Inventors: HIGASHI, MASAHIRO, IIJIMA, HIROSHI, INOUE, AKIYOSHI, MORIYA, KUNIHIKO, MUROGA, GORO, NAKAMURA, YOSHIKAZU, TATE, KAZUHITO, YANAGIDA, KAZUHIRO
Applicants: MITSUBISHI OIL COMPANY, LIMITED
Application year: 1983
Main classification: C10C3
IPC codes: D01F9, C10C3