LAMINATES INCORPORATING A POLYACRYLIC-ACID COMPLEX PRIMER, PACKAGING OR CONTAINERS MADE THEREFROM, AND MANUFACTURE OF SAID LAMINATES

Abstract: A laminate web, for conversion into a container for i.e. reactive or corrosive products, is produced from aluminium foil and an extrusion coating of an ethylene/acrylic acid-type copolymer. A polyacrylic acid chromium complex primer is applied to the foil before the copolymer, to enhance the bond at the interface. The laminate web will usually be formed into a tube with the copolymer disposed on the product facing side, and can advantageously be used to package fluoride toothpastes. The foil/primer/copolymer is a subcombination of the packaging web: to the face of the foil opposite the primer and copolymer, other structural layers such as polyethylene and paper are bonded.

Description: "LAMINATE WEBS INCORPORATING A POLYACRYLIC ACID COMPLEX PRIMER, PACKAGING, E.G. COifnjAINERS MADE THEREFROM, AND METHOD. OF MAWUFACTURE OF SAID WEBS" The present invention relates to laminate webs incorporating a polyacrylic acid complex primer, their applications for packaging or containers, and method of manufacture of the webs. The invention comprehends containers or packages made from the said webs when filled with a degenerative product such as a dentifrice which may include a fluoride anti-caries agent. Tubes and other containers made of laminated webs, that are fabricated from a metal foil and layers of synthetic resinous materials, are widely used for the packaging of a variety of products, such as toothpaste. American Can Company, of Greenwich, Connecticut, markets such tubular containers under its LAMINATE trademark. By properly designing and constructing the laminate, oxygen and moisture barrier properties necessary for the containment of many commodities are obtained, as are the heat sealability and dead fold characteristics that are desirable in a tube-like package. Typically, the product side of the laminate web will comprise an olefinic polymer, such as low density polyethylene, ethylene-acrylic acid copolymer (EAA) or Surlyn ionomer, bonded to the inner surface of the metal layer, which is normally aluminium foil. SURLYN is a Registered Trade Mark. Although containers so constructed are entirely satisfactory under most circumstances, the ingredients of certain products have a tendency to degrade or otherwise attack the materials of construction, causing failure of the container. Certain dentifrice products are notoriously difficult to package in such a laminate web structure, particularly those that contain stannous or sodium fluoride as an anticaries agent. Due to the acid environment and/or the essential flavoring oils and detergents that are present, there is a strong tendency for ingredients of the toothpaste to permeate the inner plastic layer, and to migrate to the metal interface, thereby promoting delamination in the web structure and causing deterioration of the contained product. Of course, the longer the period ofstorage the more pronounced will be the tendency for degeneration to occur in the laminate web, and particularly so if the package is stored at a relatively elevated temperature. Various measures have been taken in the past, not only to enhance the initial level of adhesion achieved between the plastic film and the foil, but also to improve resistance to delamination over extended storage periods, i.e. to extend shelf life. These efforts include flame treatment of the foil, the utilization of interlayers of various adhesive materials, and chemical priming of the metal to increase the strength of the bond at the interface. A notable example of the latter approach entails the utilization of a polyacrylic acid chromium complex product as a foil primer to promote adhesion to polyethylene. Laminate structures so produced have been used for the packaging of alcohol-saturated swabs. While the utilization of such a primer is seen to significantly enhance bond strength, still it is not entirely satisfactory on long-term storage. The use of polyethylene as the product-facing layer may be undesirable in some'instances, due to the tendency of that material to show environmental stress cracking in the presence of certain products, such as toothpaste. Accordingly, it is a primary object of the present invention to provide a laminate web, suitable for making containers and packages, and comprised of aluminiun foil and a layer of a copolymer of ethylene with an acrylic acid or acrylic acid ester monomer, which web is adapted for use to contain degenerative products for extended periods of time. According to the present invention, there is provided a laminate web suitable for use in producing containers for degenerative products, which includes metal e.g. aluminium foil, a film of a copolymer of ethylene having in its molecule pendant carboylic acid or ester groups, and at least a monomolecular layer of a polyacrylic acid transition metal complex primer between the foil and the film. Also according to the present invention, there is provided a method for the production of a laminate web suitable for use in producing containers for degenerative products, the steps including: depositing upon at least one surface of a metal e.g. aluminium foil substrate at least a monomolecular layer of a polyacrylic acid transition metal complex primer from an aqueous alcoholic solution, heating the thus-coated substrate to substantially dry the primer; extrusion coating a film of a copolymer of ethylene upon the primed surface, or upon at least one of the primed surfaces, of the foil, the copolymer having pendant carboxcylic acid or ester groups in its molecule; and cooling the laminate to provide the web. The primary obJect of the invention is readily attained by laminating the ethylenic copolymer to aluminium foil, preferably employing as the primer a polyacrylic acid chromium complex primer. In preferred embodiments of the web, the copolymer of the film will be selected from the group consisting of poly(ethylene/acrylic acid), poly(ethylene/methacrylic acid), poly(ethylene/ methylacrylate), poly(ethylene/methyl methacrylate), poly(ethylene/vinyl acetate), and ionomer resins. The primer coating can be significantly thicker than a monomolecular layer. The web will generally comprise at least one additional layer: normally it will include at least one synthetic resinous polymer layer disposed upon the side of the foil opposite to that upon which the primer is applied. To make the web, at least a monomolecular layer of a polyacrylic acid chromium complex primer, formulated as an aqueous alcoholic solution, is deposited upon at least one side of an aluminium foil substrate. The coated substrate is thereafter heated substantially to dry the primer. Following this, a film of a copolymer of ethylene (as described above) is extrusion coated upon the primed surface, preferably using the copolymer melt at a temperature of 5500 to 6000 Fahrenheit (288 to 310 C), and most desirably at a temperature of 5750 to 5900 Fahrenheit (3010 to 316 C). A container for a degenerative product fabricated from the laminate web will have the copolymer film disposed on the product side thereof. The container may be a toothpaste tube filled with a degenerative dentrifice substance containing a fluoride anticaries agent and/or one or more essential oils. The container may thus be in the form of a tube having a headpiece bonded within one end of the tubular structure; the headpiece generally being made of a polyolefin resin, such as high density polyethylene. The invention will now be described in more detail by way of example only. ¯¯ As noted initially, foil/ethylene copolymer laminate webs have previously been used in fabricating containers. The present invention provides means by which the strength of the bond between the foil and a copolymer layer on the product side is greatly enhanced, and is rendered substantially less susceptible to degenerative ingredients that may migrate to the interface. The chrome complexes that are utilized to prime the aluminium foil surface are commercially available from the Mica Corporation, of Stamford, Connecticut, under the trade designation MICA A-291, which is a seven percent aqueous solution of a polyacrylic acid chromium complex; it is acidic in nature and has a viscosity of about ten centipoise (10 mPa s). The MICA A-291 product literature indicates use for bonding polyethylene to aluminium foil, for packaging and industrial applications requiring high bonds and resistance to a variety of hard-to-hold materials, including fluorides and essential oils. It is not believed however, that there has heretofore been any recognition that the use of such a primer will achieve the results attained by the present invention, i.e., the development of extremely durable bonds betweenaluminium foil and extrusion coatings of carboxcylic acid or ester-containing copolymers of ethylene, which bonds endure despite intimate contact with products considered to be of a highly degenerative nature. Although the above-identified chromium complex is believed to be the most effective primer for use herein, other closely-related substances may be substituted if so desired. Thus, the length of the polyacrylic acid chain may vary, as may the proportion of the acrylic acid moiety in the copolymer and the ratio of the metal to the organic portion of the complex. Indeed, it is possible that other transition metals, such as cobalt, copper, nickel, and the like, might be substituted for chromium. As indicated above, the primer will generally be applied as a dilute water/alcohol solution to maximize leveling and wetting of the substrate, and thereby afford optimal levels of adhesion of the polymer layer thereto. To prepare the working liquid, the commercial MICA A-291 product may suitably be mixed with additional water and isopropyl alcohol in a volumetric ratio of 30: 60: 10 (product to water to alcohol). The resulting solution will be used in an amount sufficient to provide, when dried, about 0.03 to 0.08, and preferably about 0.035, pound of complex solids per ream (i.e., 3,000 square feet of surface area), (48.8 g/1000 m2; 130 g/1000 m2 and 57.0 g/lO00 m2). In any event, the primer must be of at least monomolecular thickness, and generally it will be at least somewhat heavier. After drying of the primer, typically by passage of the foil structure through an oven held at a suitable temperature, (i.e., about 2500 to 4000 Fahrenheit or 1210 to 2040C), the web may be presented directly to a copolymer extrusion station. Then, its temperature will generally be about 1000 to 1500 Fahrenheit (380 to 660C). The techniques utilized for extrusion coating of the ethylene copolymer upon the aluminium foil are well known to those skilled in the art, and need not be discussed in detail. It should, however, be appreciated that the temperature of the melt is critical to the attainment of optimal bonding, bearing in mind that the copolymer must not only be strongly adhered to the foil, but that its capacity for self-bonding (i.e., for heat sealing) and for bonding to other portions of the ultimate container must also be preserved. Speclfically, and as has been pointed out above, the laminate webs according to the invention will find their widest utility in the production of tubular containers, for which applications the web must be capable of side seaming and secure attachment to a molded headpiece. High melt temperatures favor bonding to the foil; on the other hand, they also promote oxidation, which inhibits the formation of good bonds with other polymeric surfaces (e.g., the headpiece). Consequently (and depending to an extent upon the air gap distance beyond the extruder die lips), as an example ethylene acrylic acid (EAA) will generally be extruded, in the practice of the present method, at a temperature of 5500 to 6000 Fahrenheit (2880 to 316 C). An optimum balance of bonding-properties will usually be realized with a melt temperature of about 575 to 5900 Fahrenheit (3020 to 3100C). While EAA or ionomer will usually constitute the layer of the laminate web ultimately destined to face the product, other copolymers of ethylene having pendant carboxylic acid or ester groups can also be used, such as copolymers with acrylic or methacrylic acids, methylacrylate, methylmethacrylate, and vinyl acetate. The technique normally used to produce the foil/copolymer composite will be extrusion coating in view of its recognized economic and practical benefits. However, other techniques may be found to be feasible under certain circumstances, and may be employed if so desired. Generally, the thickness of the product-facing polymer will range from about 1.0 to 4.0 mils (0.02 to 0.10 mm), and more commonly 1.5 to 3.0 mils (0.04 to 0.08 mm) to provide an optimal functional and economic balance. Insofar as the foil component is concerned, as a practical matter thin-gauge (i.e., about 0.285 to 3.0 mils or 0.007 to 0.08 mm) aluminium will normally be utilized, although for certain applications foils of other metals might be substituted. The laminate web will generally contain additional polymer layers for various purposes, and a paper layer will usually be included to enable facile printing or decoration of the article. A typical laminate arrangement will comprise (from the outside in) : polyethylene, paper, polyethylene, EAA, foil, primer, and lastly the EAA-layer destined to face the product. Save for the foil, primer, EAA subcombination, the basic structure is conventional. The manner in which the laminate web is converted into a container tube (e.g., head bonding, side seaming, and end sealing to form and close the tube) may be entirely conventional and known to those skilled in the art. Accordingly, a detailed description is unnecessary. It might be mentioned, however, that in forming the side seam it is common practice to overlap the edges of the web. Since this will expose both sides of the laminate to the product, advantage can be seen in priming both surfaces of the foil, in accordance herewith. Exemplary of the efficacy of the present invention are the following specific examples: EXAMPLE ONE Webs are produced utilizing a laminate subassembly comprised of layers of polymers and paper bonded to one face of 0.7 mil (0.018 mm) thick aluminium foil, the overall gauge of the subassembly being about 10.2 mils (0.26 mm). The exposed side of the foil is primed by applying, from a rotogravure cylinder, somewhat in excess of a monomolecular layer of a polyacrylic acid chromium complex, using a 30: 60: 10 solution of MICA A-29l: water: isopropyl alcohol, which is subsequently forced air dried in an oven, at about 2500 Fahrenheit (121 C). A first laminate is produced by extrusion coating the primed foil surface with 43.5 pounds per ream (70.8 kg/m2) of low density polyethylene, the extrudate being at a temperature of about 6000 Fahrenheit (3160C). This laminate is designated "A". A second laminate, designated "Rnl is prepared by extrusion coating the subassembly with the same thickness of an EAA copolymer containing 3.5 percent of the acrylic acid monomer, the temperature of the melt also being about 6000 Fahrenheit (3160C). A third laminate designated nCn is prepared in the same manner utilizing, in place of the 3.5 percent resin, an EAA copolymer containing 8.0 percent of the acrylic acid moiety. The foregoing laminates are converted to small pillows measuring 1 x 5-5/8 inches (2.54 x 14.3 cm), which are filled with a commercial dentifrice product (i.e., Proctor & Gamble CREST toothpaste), and are thereafter sealed. Several pillows produced from each of the three laminates are held at a controlled temperature for periods of-from two weeks to six months, after which the condition of the web is determined. Specifically, five pillows of each sample are held at temperatures of 750 and 1050 Fahrenheit (240 and 410C), and three pillows of each sample are held at a temperature of 1200 Fahrenheit (49 C). They are evaluated at intervals of two, four, eight, twelve, and twenty-six weeks. The results are set forth in Table One, which follows: TABLE ONE Feriod (Weeks): 2 Weeks 4 Weesks 8 Weeks 12 Weeks 26 Weeks Temperature ( F) 75 105 120 75 105 120 75 105 120 75 105 120 75 105 120 LAMINATE A - - G - G-E F G-E F P-F G F - G P-F B - - G-E - G-E G-E G-E G-E F G-E G-E - G-E F-G C - - G-E - G-E G-E G-E G-E G G-E G-E - G-E G-E - As used in the Table, the designations "E", nGn, "F" and "P", mean that the condition of the web is Judged to be excellent, good, fair, or poor, respectively; a dash mark indicates that no test is performed under the indicated conditions. To be considered excellent, the level of adhesion must be such that the polymer layer becomes stretched in endeavoring to separate it from the foil. Good adhesion indicates that separation is achieved and sustained only with difficulty. If the laminate offers a significant amount of resistance to separation it is deemed to be fair, and if it is easily delaminated the level of adhesion is regarded to be poor. From Table One, it is seen that surprisingly high levels of bond strength are achieved utilizing the EAA film on the primed foil (laminates ng" and "C"), as compared to that which is exhibited when the laminated polymer is polyethylene (laminate tAn). More particularly, after storage for four weeks at 1200 Fahrenheit (496C), and 8 or 12 weeks at 1050 Fahrenheit (410C), the EAA-containing laminates both exhibit good-to-excellent adhesion, whereas the polyethylene web has only fair bond strength. While these are the most dramatic differences reflected in Table One, it can be seen that in all instances the EAA laminates are invariably superior to those made with the low density polyethylene. In addition to the foregoing delamination tests, environmental stress cracking of the three laminate webs is evaluated by hand squeezing selected pillows. After six months storage time at 1050 Fahrenheit (410C),the pillows produced from the polyethylene web are found to be highly prone to cracking when manually squeezed. In contrast, the EAA-based laminates, conditioned in the same way, satisfactorily survive such manipulation. EYUUMPLE TWO A commercial household cement product (ire., duPont DUCO cement) is sealed within pouches produced from laminates containing either 3.5 percent EAA or ionomer on aluminium foil, the polymer and foil gauges being 2.0 and 0.332 mil (0.051 and 0.008 mm), respectively, in all cases. Two versions of each laminate are produced; i.e., both with and without pretreatment of the foil with the MICA A-291 primer. The pouches are sealed and stored at a temperature of 1050 Fahrenheit (410C), different ones being opened after one and two months' storage time to assess the levels of adhesion that are maintained between the polymer layer and the foil. After storage for one month, the webs made with the primed aluminium show good adhesion regardless of whether the polymer layer is comprised of EAA or ionomer. The unprimed aluminium, on the other hand, produces webs in which delamination (in the case of EAA) or poor adhesion (in the case of the ionomer) occurs. The results are the same following the two-months storage period. Although the foregoing specific examples demonstrate the outstanding ability of the present laminate webs to withstand the degenerative effects of a fluoride toothpaste and a household cement containing highly active organic solvents, it should be appreciated that the webs can be used advantageously for packaging a wide range of other products deemed to be difficult to contain. For example, the web according to the -invention can successfully survive the degenerative effects of NOXEYA Brushless Shave Cream (Noxell Corporation); Helena Rubenstein Skin Lightener; Dap, Inc. Waterless Hand Cleaner; VAGINEX Cream (Schmid Laboratories); Plymouth Citrus Products Industrial Waterless Hand Cleaner; TURTLE WAX Auto Polish Glaze; ARTRA Skin Tone Cream (Plough Inc.); Union Carbide Corporation car polish; ABSORBINE RUB (W.F. Young, Inc.); Red Glazing Putty (Oatey Co.); LX 845 Auto Glaze (Petrolite Corporation), -and Soupletube (France) Product No. 3. In all instances the degree of resistance to delamination is at a very good level, but the specific results achieved with any particular product will, of course, vary. Moreover, it will be appreciated that the foregoing list of commercial products is intended only to be exemplary, and that the laminate webs made in accordance with the present invention may be utilized with comparable advantage for many other products. Thus, it can be seen that the present invention provides a novel laminate web comprised of aluminium foil and a layer of a copolymer of ethylene with an acrylic acid or acrylic acid ester monomer, which web is adapted for successfully containing degenerative products for extended periods of time. The invention also provides a novel container and package fabricated from such a laminate web, and novel methods for the production of such webs, containers and packages.

Claims: Claims: 1. A laminate web suitable for use in producing containers for degenerative products, which includes metal e.g. aluminium foil, characterised in that the web also includes a film of a copolymer of ethylene having in its molecule pendant carboxcylic acid or ester groups, and at least a monomolecular layer of a polyacrylic acid transition metal complex primer between the foil and the film. 2. The web according to claim 1, characterised in that the copolymer is selected from poly(ethylene/ acrylic acid), poly( ethylene/methacrylic acid), poly(ethylene/methyl acrylate), poly(ethylene/ methyl methacrylate), poly(ethylene/vinyl acetate), and monomer. 3. The web according to claim 1 or claim 2, further characterised by including a film of a synthetic resinous polymer on the side of the foil opposite to the primer. 4. The web according to claim 1, 2 or 3, wherein the primer comprises a polyacrylic acid chromium complex. 5. The web according to claim 1, 2, 3 or 4, characterised in that the primer is present in an amount of 48.8 to 130 g/1000 m2 of web, the copolymer film is 0.02 to 0.10 mm thick and the foil is 0.007 to 0.08 mm thick. 6. A container for a degenerative product fabricated from the laminate web claimed in any of claims 1 to 5, wherein the said copolymer film is on the product-facing side thereof. 7. The container according to claim 6, characterised in that the laminate web is formed into a tubular configuration, and a headpiece is secured to one end of the tubular structure. 8. The container according to claim 7, characterised in that the headpiece is fabricated from high density polyethylene. 9. The container according to claim 7, or claim 8, characterised in that the laminate is formed into a side-seamed tube by heat sealing and the headpiece is heat sealed thereto. 10. A method for the production of a laminate web suitable for use in producing containers for degenerative products, characterised by the steps including: depositing upon at least one surface of a metal e.g. aluminium foil substrate at least a monomolecular layer of a polyacrylic acid transition metal complex primer from an aqueous alcoholic solution, heating the thus-coated substrate to substantially dry the primer; extrusion coating a film of a copolymer of ethylene upon the primed surface, or upon at least one of the primed surfaces, of the foil, the copolymer having pendant carboxcylic acid or ester groups in its molecule; and cooling the laminate to provide the web. 11. The method according to claim 10, characterised in that the copolymer is selected from poly(ethylene/acrylic acid) poly(ethylene/ methacrylic acid) poly(ethylene/methyl acrylate), poly(ethylene/methyl methacrylate). poly(ethylene/ vinyl acetate) and ionomer resin. 12. The method according to claim 11, wherein the copolymer is poly(ethylene/acrylic acid), and the method being further characterised by said copolymer being extruded from an extrusion dye at a melt temperature of 5500 to 6000 Fahrenheit (232 to 3160C). 13. The method according to any of claims 10 to 12, wherein the foil is coated with a polyacrylic acid chromium complex primer. 14. A method according to any of claims 10 to 13, characterised in that the web is formed into a container configuration with said copolymer film disposed on the inside thereof. 15. A method according to claim 14, characterised by forming the web into a tubular structure, and by bonding a headpiece to said web at one end of the resulting tubular structure. 16. The method according to claim 15, wherein the headpiece is fabricated from high density polyethylene. 17. A packaging method comprising the steps of forming the container as claimed in claim 14, 15 or 16 and filling the container with a degenerative product such as a dentifrice substance containing a fluoride anticaries agent.

Inventors: MIDDLETON, SCOTT W.
Applicants: AMERICAN CAN COMPANY
Application year: 1983
Main classification: B32B15
IPC codes: B65D35, B32B15