CATALYTIC CARBONYLATION OF ALCOHOLS

Abstract: A process for converting alcohols into oxygen-­ containing products having at least one more carbon atom than the starting alcohols such as carboxylic acids, alcohols or aldehydes, or the secondary products thereof, comprises reacting an alcohol having from one to twenty carbon atoms with hydrogen and carbon monoxide in the presence of a heterogeneous sulphided catalyst comprising nickel, or nickel in admixture with a co-catalyst selected from the elements of Group VB, Group VIB and the Actinide series of the Periodic Table. The sulphided catalyst is generally present on a support such as alumina or silica-alumina. The heterogeneous sulphided catalyst can be more easily sepa­ rated from the reaction products than the previously used homogeneous catalysts.

Description: Catalytic carbonylation of alcohols This invention relates to a process for the catalytic carbonylation of alcohols and is concerned with a process for converting alcohols into oxygen-containing products having at least one more carbon atom than the starting alcohol. By virtue of the process of the present invention, it is possible to obtain carboxylic acids, alcohols, or aldehydes, or the secondary products thereof (which may be formed in situ by a subsequent reaction) by reaction of an alcohol with hydrogen and carbon monoxide in the presence of a heterogeneous sulphide catalyst. U.S. Patent No. 2,623,906 discloses that at pressures above 1,000 atmospheres and in the presence of a cobalt catalyst, primary, secondary or tertiary alcohols react with synthesis gas (a mixture of hydrogen and carbon monoxide) to form glycol ethers and monohydric alcohols containing at least one more carbon atom per molecule than the original alcohol reactant. U.S. Patent No. 3,285,948 discloses that an improved yield of ethanol from methanol can be obtained by conducting the synthesis gas homologation reaction in the presence of a cobalt catalyst which is promoted with iodine and a metal halide selected from ruthenium halide and osmium halide. U.S. Patent No. 4,111,837 discloses a process for producing ethanol which comprises reacting methanol with carbon monoxide and hydrogen in the presence of a catalyst consisting essentially of a methanol-soluble cobalt carbonyl and methanol-insoluble rhenium metal. U.S. Patent No. 4,304,946 discloses a process for producing ethanol from methanol, carbon monoxide and hydrogen which comprises conducting the reaction in the presence of a cobalt sulphide or a mixture of a cobalt sulphide and at least one of a nitrogen-containing compound and a phosphorus compound. According to the present invention there is provided a process for converting an alcohol into at least one oxygen-containing product, such as a carboxylic acid, alcohol, aldehyde or a secondary product thereof, having at least one more carbon atom then the alcohol, which comprises reacting an alcohol having from one to twenty carbon atoms with hydrogen and carbon monoxide at 0 a temperature in the range from 150 to 350 C and a pressure in the range from 500 to 5,000 psig in the presence of a heterogeneous sulphided catalyst comprising nickel, or nickel in admixture. with a co-catalyst selected from the elements of Group VB, Group VIB and the Actinide series of the Periodic Table, to obtain the desired reaction product having at least one more carbon atom than the starting alcohol. Among other factors, the present invention is based on the discovery that alcohols can be converted to useful oxygenated products having at least one more carbon atom than the starting alcohol in improved yield and selectivity by utilizing a heterogeneous sulphided nickel catalyst system. An advantage of the process of the present invention lies in the fact that the heterogeneous catalyst employed is easier to separate from the reaction products than the homogeneous catalysts of the prior art. In addition,. it has been found that the process of the present invention does not require the use of any soluble catalyst promoters. This is particularly advantageous, since the absence of a halide promoter in the system obviates the need for expensive corrosion resistant equipment. Oxygen-containing carbon compounds which can be obtained with high selectivity in the process of the invention include carboxylic acids, alcohols, aldehydes or the secondary products which may be formed therefrom under the reaction conditions in a subsequent reaction, for example, esterification, condensation or dehydration. Illustrative of a typical batch procedure, in the process of the invention the alcohol is charged to a high pressure reactor, and then there is introduced a heterogeneous sulphided catalyst system comprising nickel or nickel plus an element of Group VB, Group VIB or the Actinide series. The reactor is pressurized with a mixture containing carbon monoxide and hydrogen and heated for a suitable length of time to give the desired conversion. Liquid and gaseous products and reactants can be easily separated from the catalyst by filtration, distillation or other methods. Unreacted starting materials can be recycled. The products can be isolated by means Qf one of a number of known methods, including distillation. In some cases it may be advantageous to further process the products. For example, methyl acetate can be easily hydrolyzed to acetic acid. The process of the present invention can also be run in a continuous fashion. This is particularly advantageous as the catalyst is not soluble in the reaction medium. A number of reactor configurations arF suitable including fixed or fluid beds, slurry beds or stirred tank reactors. As with a batch reaction, unreacted starting materials can be easily recycled and, if desired, the products can be further processed. The alcohols suitable for use in the present invention may be primary, secondary, tertiary or benzylic alcohols having from one to twenty carbon atoms. Diols and polyols may also be used. A preferred alcohol is methanol. If desired, the reactant alcohol may be diluted with an alcohol-miscible solvent such as dioxan, tetrahydrofuran, or N-methylpyrrolidinone. When methanol is used as the starting alcohol, reaction products typically formed include acetic acid, ethanol, acetaldehyde or methyl acetate. The heterogeneous sulphided catalyst system employed in the present process comprises nickel sulphide alone or a composite of sulphides of a nickel component and a Group VB, Group VIB or Actinide component. Cocatalysts suitable for admixture with the nickel component include tantalum, chromium, vanadium, thorium and tungsten. A particularly preferred catalyst system comprises nickel and molybdenum. The catalyst system may optionally contain phosphorus or silicon. In carrying out the reaction, it is usually desirable, although not essential, to place the catalyst on a support. Generally, the support should be a solid, inert material which is relatively insoluble in the solvent employed. Suitable supports include various treated or untreated organic and inorganic supports. Included among these are synthetic and naturally occurring polymers, alumina, silica, titania, silicaalumina, zeolites, glass and carbon. Particularly preferred supports are alumina and silica-alumina. The metals may be added to the support using a method known in the art, such as by impregnation or coprecipitation. The method of loading the catalyst on the support will depend on the nature and composition of the support. Generally, the most convenient method of depositing the metals on the support is by adding a solution of metal salts to the support and subsequently converting them to an insoluble form. An especially suitable catalyst precursor may be prepared by impregnating alumina with an aqueous or organic solution of the metal salts, either together or sequentially, followed by drying and calcining to give the metal oxides. The catalyst may be converted to its active sulphide form by any of a number of conventional procedures. Treatment with hydrogen sulphide or other sulphurcontaining compound such as carbon sulphide, dimethyl disulphide or sulphur, in the presence of hydrogen or synthesis gas is effective. This treatment can be either prior to or concurrent with the alcohol carbonylation reaction. In the process of the present invention alcohols are reacted with carbon monoxide and hydrogen (synthesis gas). Synthesis gas produced by the reaction of carbonaceous material with water is suitable. Mixtures of, for example, carbon dioxide and hydrogen, or carbon monoxide and water, may also be employed. Whether introduced originally, or produced in situ under processing conditions, carbon monoxide and hydrogen are required for the reaction. The relative molar quantities of carbon monoxide and hydrogen present during the reaction can vary in the range from 10:1 to 1: 10, and preferably in the range from 3:1 to 1:3. An inert diluent gas such as nitrogen or helium may be included if desired. The carbonylation reaction requires a relatively high pressure for optimum selectivity and yield of product. The pressure should be maintained in the range from 500 to 5,000 psig, and preferably in the range from 800 to 2000 psig. The reaction is conduced at a temperature in the range from 150 to 3500C, and preferably in the range from 190 to 2900C. The time that the reactants are in contact with the catalyst will be dependent, among other factors, on the temperature, pressure, alcohol reactant, catalyst, reactor configuration and the desired level of conversion. The solid catalyst can be easily separated from the generally liquid and gaseous reaction products and unreacted starting materials by, for example, filtration, centrifugation, settling out or distillation. The catalyst can be reused in a subsequent reaction. Unreacted starting materials can be separated from reaction products and are suitable for recycle in the process. The products of the reaction, which can be isolated by one of a number of well-known methods, such as distillation, are generally useful as solvents or chemical intermediates. In some cases it may be advantageous to further process the reaction products by well-known means to form other useful products. For example, methyl acetate can be hydrolyzed to acetic acid, and ethanol and phenethyl alcohol can be dehydrated to ethylene and styrene, respectively. The following Examples are provided to illustrate the invention. Examples 1 to 3 and 14 illustrate the preparation of non-suiphided catalysts suitable for use in the invention, whilst the remainder illustrate the process of the invention. Example 1 A catalyst was prepared from nickel nitrate hexahydrate (8.Ig) and commercial phosphomolybdic acid (l5.lg) by dissolving in water (50 ml), evaporating to dryness on a hot-plate, and further heating first at 2000C for 2 hours and finally at 325 0C for 2 hours to yield l3.4g of a dark brown solid. This catalyst was used in Example 4. Example 2 A catalyst was prepared by impregnating 50g of alumina with a water solution (32 ml) of nickel nitrate hexahydrate (8.6g) and silicotungstic acid hydrate (10.3g). The catalyst was dried under vacuum at 1200C and then calcined in air at 4750C for 4 hours. This catalyst was used in Example 8-g. Example 3 A catalyst was prepared by impregnating 50g of a commercial vanadium oxide on alumina catalyst (Girdler V-0301) with a water solution (32 ml) of nickel nitrate 0 hexahydrate (7.8g). The catalyst was dried at 120 C and 0 then calcined at 475 C for 4 hours. This catalyst was used in Example 8-e. Example 4 A 300 ml stainless steel autoclave was charged with 75 ml of methanol and 5.0g of an unsupported catalyst comprising nickel, molybdenum and phosphorus oxides (as described in Example 1) that had been treated with 10% hydrogen sulphide in hydrogen at 325 0C followed 0 by hydrogen at 400 C. The reactor was sealed and press- urized to 1000 psi with a mixture of one part hydrogen and two parts carbon monoxide, and then heated to 235 C. After 6.0 hours the reactor was cooled and the pressure released. Analysis of the liquid products by gas chromatography indicated methyl acetate (121 mmol) and ethanol (12.8 mmol) as major products as well as minor amounts of n-propanol and acetic acid. Example 5 A 300 ml stainless steel autoclave was charged with 10.00go of a catalyst comprising nickel, molybdenum and phosphorus (approximately 3, 14 and less than 1 wt. %, respectively) oxides on alumina, 2.50g of sulphur and 50 ml of methanol. The reactor was sealed, flushed with nitrogen, and pressurized to 900 psi with a mixture of two parts hydrogen and one part carbon monoxide. The reactor was heated to 2500C and the pressure adjusted to 2500 psi. After 4 hours, the reactor was cooled with ice and the pressure released. Analysis of the liquid product by gas chromatography, after addition of 1,4dioxan as internal standard, indicated methyl acetate (27.3 mmol) and ethanol (12.4 mmol) as products as well as methyl ether and methyl sulphide. Example 6 A 300 ml stainless steel autoclave was purged with nitrogen and charged with 100 ml of methanol, 1,4-dioxan (as internal standard), and 5.0g of a catalyst comprising nickel, molybdenum and phosphorus (approximately 6, 15 and 2 wt %, respectively) oxides on silica-alumina that had been previously treated with 10% hydrogen sulphide in 0 hydrogen at 325 C. The autoclave was sealed and press- urized with 350 psi of a mixture of two parts hydrogen and one part carbon monoxide, then heated to 240 0c to give a final pressure of 1200 psi. After 2 hours, analysis of a small sample indicated methyl acetate (7.8 mmol) and ethanol (0.25 mmol) as major products. This example was repeated except that the initial pressure was 1000 psi and the final pressure was 2300 psi. In this case, the products after two hours of reaction were methyl acetate (34.0 mmol) and ethanol (7.8 mmol). Example 7 Four 18 ml stainless steel reactors were each charged with 5 ml of methanol and O.50g of a catalyst comprising nickel, molybdenum and phosphorus (approximately 3, 13 and 2 wt. %, respectively) oxides on alumina. Reactors 1-3 each contained a source of sulphur as indicated in the following Table 1. The reactors were sealed and pressurized to 850 psi with a mixture of 2 parts hydrogen and I part carbon monoxide. The reactors were heated at 2400C with gentle shaking for 4.0 hours. After cooling and venting, the contents of the reactors were analyzed by gas chromatography. The results are indicated in Table- 1. In addition to the indicated products, methyl ether and methyl sulphide were also produced. TABLE 1 Charges Products Methyl Sulphur Compound Amount Acetate Ethanol 1. Methyl disulphide 0.7 mmol 0.2 mmol trace 2. Carbon disulphide 1.2 1.2 0.3 mmol 3. Sulphur 1.6 0.4 0.1 4. None 0 trace 0 Example 8 A series of 18 ml stainless steel reactors were each charged with methanol (5 ml), 1,4-dioxan (0.10 ml), sulphur (0.13g) and catalyst (0.50g) as indicated in the following Table 2. The reactors were sealed and pressurized with 900 psi of a mixture of two parts hydrogen and one part carbon monoxide. The reactors were heated at 2400C with gentle shaking for 4.0 hours. After cooling and venting, the contents were analyzed by gas chromatography using 1,4-dioxan as internal standard. In addition to the products indicated, methyl ether and methyl sulphide were also formed. TABLE 2 Products Methyl Catalyst1 Methyl Acetate Ethanol a. Ni(8), W(19), Ti(8) on silica-alumina 3.6 mmol 0.3 mmol b. Ni(3), Mo(12), P(0.3) on silica 2.1 0.3 c. Ni(3), Mo(12) on alumina 0.4 0.2 d. Uni(3), Ta(12) on alumina 1.7 0.1 e. Ni(3), V(10) on alumina 0.6 0.03 f. Ni(3), Th(12) on alumina 0.2 0 g. Ni(3), W(12), Si(0.2) on alumina 1.0 0.1 h. Ni(6), Mo(15), P(2) on silica-alumina 4.4 0.9 1 Approximate weight percent of metal in parenthesis, present in oxide form Example 9 An 18 ml stainless steel reactor was charged with 5 ml ethanol, 0.125g sulphur, and 0.50g of a catalyst comprising nickel, molybdenum, and phosphorous (approximately 6, 15, and 2 wt. %) oxides on silica-alumina. The reactor was sealed and pressurized to 900 psi with a mixture. of 2 parts hydrogen and 1 part carbon monoxide, then heated with gentle shaking for 4.0 hours at 240 C. After cooling and releasing the pressure, analysis indicated ethyl propionate (1.2 mmol) and n-propanol (0.6 mmol) as- the major carbonylation products along with an undetermined amount of ethyl ether. Example 10 An 18 ml stainless steel reactor was charged with 5 ml of 1,3-propanediol, 0.125g of sulphur, and 0.5g of a catalyst comprising nickel, molybdenum, and phosphorous (approximately 6, 15, and 2 wt. %) oxides on silicaalumina. The reactor was sealed, pressurized with 900 psi of a mixture of two parts hydrogen and one part carbon monoxide, then heated with gentle shaking to 2400C for 4.0 hours. After cooling and releasing the pressure, gas chromatographic analysis indicated the presence of gamma-butyrolactone. Example 11 Two 18 ml stainless steel reactors were each charged with 1 ml of methanol, 0.125 g sulphur, and 0.50 g of a catalyst comprising nickel, molybdenum, - and phosphorous (approximately 6, 15, and 2 wt 8) oxides on silica-alumina. Additionally one reactor was charged with 4 ml N-methylpyrrolidinone and the other with 4 ml of tetra-hydrofuran. The reactors were sealed and pressurized to 900 psi with a mixture of 2 parts hydrogen and 1 part carbon monoxide. The reactors were heated with gentle shaking for 4.0 hours at 2400C. Analysis of the products indicated 0.6 mmol methyl acetate and minor amounts of acetaldehyde and ethanol in the first, and 1.86 mmol of methyl acetate in the second as well as methyl ether and methyl sulphide in both. Example 12 A stainless steel reactor tube was packed with 5.0g of catalyst comprising nickel, molybdenum, and phosphorous (approximately 3t 13, and 2 wt. %) oxides on alumina. The catalyst was treated with 10% hydrogen sulphide in hydrogen at 3250C for 1 hour, then purged with nitrogen The catalyst bed was maintained at 280 0c as synthesis gas (comprising two parts hydrogen and one part carbon monoxide) and methanol were passed over the catalyst. The reactor pressure was maintained between 1720 and 1760 psi, the GHSV at 4000 hr. -l and LHSV at 2 hr. 1. Analysis of the products collected over a 20.5 hour period indicated methyl acetate (79.2 mmol) and ethanol (102.2 mmol) as major carbonylation products as well as a lesser amount of acetic acid. Methyl ether was also formed. Example 13 A 300 ml stainless steel autoclave was charged with 75 ml methanol and 5.0 g of a 10-12% nickel on gamma alumina catalyst (Girdler T-310) that had been treated with 10% hydrogen sulphide in hydrogen at 325or. The reactor was sealed, pressurized with a mixture of one part hydrogen and two parts carbon monoxide, and heated 0 to 240 C. The pressure was maintained at 2150 to 2250 psi for 6 hours. After cooling and venting the gases, the liquid contents were examined by gas chromatography using 1,4-dioxan as an internal standard. In addition to methanol and methyl ether, 10.5 mmol methyl acetate, 1.0 mmol ethanol, and a small amount of methyl formate were produced. Example 14 A 3% nickel on alumina catalyst was prepared by impregnating 50.0 g of alumina with 32 ml of a water solution containing 7.65 g of nickel nitrate hexahydrate. The catalyst was dried in- a vacuum oven at approximately 0 0 100 C and then calcined at 475 C for 4 hours. Example 15 An 18 ml stainless steel reactor was charged with 5 ml methanol, 0.125 of sulphur, 0.10 ml 1,4-dioxan, and 0.50 g of a 3% nickel on alumina catalyst (described in Example 14). The reactor was sealed and pressurized to 900 psi of a mixture of two parts hydrogen and one part carbon monoxide. After heating for 4.0 hours at 240 C, gas chromatographic analysis of the products, using 1,4dioxan as an internal standard, indicated the presence of 0.51 mmol methyl acetate as well as methyl ether, methyl sulphide, and unreacted methanol. Example 16 An 18 ml stainless steel reactor was charged with 5 ml methanol, 0.10 ml 1,4-dioxan, 0.125 g sulphur, and 0.50 g of a 10-12% nickel on gamma alumina catalyst (Girdler T-310). The reactor was sealed and pressurized to 900 psi with a mixture of two parts hydrogen and one part carbon monoxide The reactor was heated to and maintained at 2400C for 4+0 hours, then cooled and vented. The liquid portion was analyzed by gas chromatography using 1,4-dioxan as an internal standard. In addition to methyl ether and methyl sulphide, 1.8 mmol of methyl acetate was produced. Example 17 The procedure of Example 16 was followed except that ethanol was substituted for methanol. The major carbonylation product was ethyl propionate (0.1 mmol) with a trace of n-propanol. Example 18 An 18 ml stainless steel reactor was charged with 5 ml methanol, 0.1 ml 1,4-dioxan, 0.13 g sulphur, and 0v25 g of a catalyst comprising 40% nickel on a refractory support (Girdler G87). The reactor was pressurized to 900 psi with a mixture of two parts hydrogen and one 0 part carbon monoxide, sealed, heated to 240or and shaken for 4 hours. After cooling and venting the gases, gas chromatographic analysis indicated the presence of methyl -acetate (2.82 mmol) and ethanol (0.05 mmol) as the major carbonylation products. Example 19 An unsupported nickel sulphide catalyst was prepared in situ by combining nickel carbonate (52 mg), sulphur (24 mg), methanol (5 ml), and 1,4-dioxan (0.10 ml) in an 18 ml stainless steel reactor. The reactor was pressurized to 900 psi with a mixture of 2 parts hydrogen and 1 part carbon monoxide, sealed, and heated with gentle shaking at 2400C for 4 hours. After cooling and venting the gases, the contents were removed to yield a clear liquid and a black solid. Gas chromatographic analysis of the liquid using 1,4-dioxan as an internal standard indicated that methyl acetate (0.67 mmol) and ethanol (0.03 mmol) were the major carbonylation products.

Claims: CLAIMS: 1. A process for converting an alcohol into at least one oxygen-containing product having at least one more carbon atom than the alcohol, which comprises reacting an alcohol having from one to twenty carbon atoms with hydrogen and carbon monoxide at a temperature 0 in the range from 150 to 350 C and a pressure in the range from 500 to 5,000 psig in the presence of a heterogeneous sulphided catalyst comprising nickel, or nickel in admixture with a co-catalyst selected from the elements of Group YB, Group VIB and the Actinide series of the Periodic Table, to obtain the desired reaction product having at least one more carbon atom than the starting alcohol. 2. A process according to Claim 1, wherein the sulphided catalyst comprises nickel and molybdenum. 3. A process according to Claim 1 or 2, wherein the sulphided catalyst further comprises phosphorus er silicon. 4. A process according to Claim 1, wherein the sulphided catalyst comprises nickel sulphide alone. 5. A process according to Claim 1, 2, 3 or 4, wherein the sulphided catalyst is present on a support. 6. A process according to Claim 5, wherein the support is alumina or silica-alumina. 7 A process according to any preceding claim, wherein the alcohol is methanol and the reaction product obtained includes one or more of acetic acid, ethanol, acetaldehyde and methyl acetate.

Inventors: CURRENT, STEVEN P.
Applicants: CHEVRON RESEARCH COMPANY
Application year: 1983
Main classification: C07C51
IPC codes: C07C41, C07D315, C07C45, C07C29, C07C51