WATER-BASED MAGNETIC COATING COMPOSITION

Abstract: Improved aqueous magnetic coating composition employing a polyacrylic latex polymer as a dispersant. As preferred embodiments, the composition further comprises a polymeric binder having both hard and soft components, as well as the inclusion of flow agents, antifoaming agents, wetting agents and lubricants.

Description: WATER-BASED MAGNETIC COATING COMPOSITION BACKGROUND OF THE INVENTION This invention concerns itself with aqueous magnetic coating formulations. It is ' desirable at times to use aqueous formula¬ tions in place of organic formulations for the latter use expensive and toxic flammable solvents, which must be captured upon drying of the magnetic formulation to prevent air pollution. Furthermore, there have been a number of recent developments in improving magnetic aqueous formulations, which make them attrac¬ tive as substitutes for organic-based coatings generally. Notwithstanding the inherent advantages of employing aqueous magnetic coating formulations, such coatings have not, to date, replaced organic formulations commercially. One reason for the lack of success is that prior art magnetic coating layers employ emulsifiers or dispersants, which do not form an adequate bond between the magnetic pigments incorporated in the - Z - coatings and the water-based binders. As a result, the coatings become brittle as the emulsifiers exude to the coating surface. A further disadvantage of the emulsifiers of the prior art, such as TAMOL 731 which is a sodium salt of a carboxylate sold by Rohm & Haas and TRITON X-100 which is an alkyl aryl polyether alcohol also offered from Rohm & Hass, is their tendency to not only diffuse to the surface of the magnetic coating over time, but also cause the aqueous formulation to foam during prepara¬ tion. The antifoa ing agents employed by the prior art do not completely remedy the problem, particularly in the preparation of high viscosity magnetic coating compositions. Yet another problem in prior art aqueous-based magnetic coating compositions is the tendency of the magnetic particles and other pigments, such as carbon, to flocculate. The use of improved dispersion agents can not only avoid the flocculation problem, but also stabilize the magnetic powder and other pigments incorporated in the composition. It is thus an object of the present invention to provide an improved aqueous magnetic coating composition without the drawbacks of prior art compositions. It is yet another object of the present invention to employ improved dispersing agents in aqueous magnetic coating composi¬ tions to avoid those disadvantages outlined above. These and other objects of this invention will be more fully appreciated when considering the following disclosure. OMPI SUMMARY OF THE INVENTION The present invention deals with an aqueous coating compo¬ sition for forming a magnetic recording layer, the improvement comprising the use of a polyacrylic latex polymer as a dis- 5 persant. As a preferred embodiment, the polyacrylic latex polymer can comprise a copolymer of styrene and a member selected from the group consisting of butyl acrylate and ethyl acrylate. In such a composition, the styrene is preferably present in an amount between approximately 10-20% by weight, and the remaining 10 acrylate is present in an amount between approximately 80-90% by weight. The styrene-acrylate copolymer preferably has a molecular weight between approximately 20,000-40,000. The aqueous coating composition, also as a preferred embodi- 15 .ment, can further comprise a water-insoluble polymeric binder having both a hard and soft component. The hard component preferably comprises a member selected from the group consisting of copolymers and terpolymers of acrylonitrile, ethylacrylate, butylacrylate, methylmethacrylate and mixtures thereof. More 20 specifically,- the hard component can comprise a copolymer of approximately 10-20% by weight of acrylonitrile and approximately 80-90% by weight of a member selected from the group consisting of ethylacrylate and butylacrylate. Similarly, the hard compo- * nent can comprise a terpolymer of approximately 10-20% by w ' eight .25 of acrylonitrile, approximately 10-25% by weight ethylacrylate, approximately 60-80% by weight butylacrylate and approximately 10-20% by weight methylmethacrylate. OMH - h - The soft component making up the aqueous coating composi¬ tion, as a preferred embodiment, can comprise a polymer emulsion of a polyurethane having a glass transition temperature of between approximately -10 β C to -40"C. The aqueous coating composition can also employ flow agents, antifoa ing agents, wetting agents and lubricants. DETAILED DESCRIPTION OF THE INVENTION The aqueous phase of the coating composition can be prepared in a manner taught in copending application Serial No. 345,082, filed on February 2, 1982. In fact, the present invention can include lubricants in the coating composition as are taught in the referenced co-pending application. More specifically, the aqueous coating composition can comprise lubricants selected from the group consisting of aliphatic and aromatic stearates, silicon oils, perfluoro alkyl polyethers and fluorinated fluids having one of the following structures: wherein n, m » 40-90 and F-JCF(CF 3 )CF 2 θ] n ,C 2 F 5 wherein n* » 12-45 and mixtures thereof. The magnetic powders which can be employed in the aqueous coating composition can be selected from the group consisting of γ-Fe 2 0 3 , Fe 3 0 4 , as well as other oxides which are doped or surface treated with metal ions, such as cobalt, nickel or chromium. Generally, these magnetic oxides can be characterized as being needle-shaped and having coercivities from 300-800 Oe. The polymer binders discussed above can be characterized as being latexes of relatively high molecular weight. As previously stated, they preferably comprise polyblends of hard and soft components which provide the toughness which is necessary in magnetic coating compositions. Further, the polyblends of latexes form interpenetrating elastomeric networks in the presence of magnetic pigments. As a generality, the aqueous magnetic coating composition should comprise the following classes of materials, in the approximate parts by weight as indicated: Composition Parts By Weight Magnetic Oxide (or Metal) Powder 70 - 80 Dispersing Agents 1 - 3 Antifoaming Agents 0.05 - 0.1 Flow Agents 0.5 - 2 Aqueous Emulsion (25-50% Solids) 30 - 20 Lubricants 1 - 2 The dispersants, flow agents, antifoaming agents and wetting agents can be added to water followed by the addition of the pigments, which are added slowly while subjecting the composition to high shear mixing. The pH of the composition is maintained from approximately 8 to 10 during the processing steps. The magnetic powders are dispersed by milling and the polyblends of latexes are added to the mix. Lubricants and rheology modifiers are later added as a final mixing step. f OMPI EXAMPLE 1 Approximately 0.31% (wt.) sodium polyphosphate, as well as approximately 1.05% Acrysol WS-24, which is an acrylic emulsion available from Rohm & Haas Co., were added, as dispersing agents, to approximately 46.69% distilled water and dissolved therein. The pH of the solution was controlled between app'roxi- mately 8-10 by the addition of sodium hydroxide, although ammonium hydroxide could have been used equally as well. To this solution was then added approximately 0.47% of a wetting agent, namely, Surfynol 104, an acetylenic glycol available from Air Products Co., and the solution mixed vigor¬ ously under high shear. Also under high shear was then added the magnetic oxide, in this case, approximately 31.55% of the mixed oxide Fe 2 0 3 /Fe 3 0 4 - Flow agents can also be included to improve the characteristics of the coating. A suitable flow agent for practicing this invention is Acrysol RM4 which is an alkyline-soluble emulsion of ethyl alkylate and acrylic acid sold by Rohm & Haas Co. Mixing was continued under high shear employing, for example, a "bead" mill utilizing glass, ceramic or steel milling media. After a good dispersion was obtained, which was verified by visual inspection, the latexes were added. In this example, approximately 6.37% of Rhoplex 1024, an acrylic emulsion avail¬ able from Rohm & Haas Co., was used as the "hard" segment and approximately 12.25% of QW 4147, a polyurethane emulsion avail¬ able from Quinn as the "soft" segment. High shear mixing was continued and the lubricants were then added. Pre-emulsified lubricants were employed, such as those disclosed in co-pending application Serial No. 345,082. In this example, approximately 0.80% butoxyethyl stearate, available from Armak, and approxi¬ mately 0.18% of an emulsion of a silicon oil available from Dow Corning, were used as lubricants. It was observed that the butoxyethyl stearate acts as an internal lubricant as it is compatible with the latexes used herein. The second lubricant, namely, the silicon oil emulsion was incompatible and thus rises to the surface of the water- based coating in time forming a thin layer of lubricant thereon. EXAMPLE 2 The following ingredients were incorporated into a solution in the manufacture of a water-based coating composition, the mixing procedure being substantially the same as that taught in Example 1. Ingredients Weight % DI Water 46 .09 Fe 2 0 3- /Fe 3°4 Oxide 31 . . 1 4 Rhoplex WL91 (Acrylonitrile Acrylic) 7 , .58 QW4147 (Polyurethane Emulsion) T2. .09 Acrysol WS-24 (Acrylic Emulsion) 1 . .04 Silicon Oil Emulsion 0 , . 1 7 Butoxyethyl Stearate 0. , 79 Sodium Polyphosphate 0. , 31 Surfynol 104 0. , 47 NH.OH (Ammonium Hydroxide) 0. 32 100.00 The formulary of Example 2 differs in substance from that shown in Example 1 through the inclusion of an acrylonitrile acrylic. These materials improve the mechanical properties of the magnetic coating layer by toughening the overall polymeric composition. It was found that formulations prepared according to the present invention have improved mechanical properties and are smooth and quite glossy after drying and after surface treat¬ ment. The signal to noise ratio has been found to be excellent and the output improved principally because of the ability to control the rheological characteristics. By controlling the viscosity of the formulation, one is able to improve the square¬ ness and orientation ratio of jnagnetic tapes made therefrom while exhibiting very low values in the coefficients of friction. - \) E OMPl

Claims: WHAT IS CLAIMED IS: 1. In an aqueous coating composition for forming a magnetic recording layer, the improvement comprising the use of a polyacrylic latex polymer as a dispersant. 2. The aqueous coating composition of claim 1 wherein the polyacrylic latex polymer comprises a terpolymer of styrene and a member selected from the group consisting of butyl acrylate and methylmethacrylate. 3. The aqueous coating composition of claim 2 wherein styrene is present in the polyacrylic latex in an amount between approximately 10-20% by weight and the remaining acrylate is present in the polyacrylic latex in an amount between approxi- mately 80-90% by weight. 4. The aqueous coating composition of claim 2 wherein ' said copolymer is of a molecular weight between approximately 20,000 to 40,000. 5. The aqueous coating composition of claim 1 further comprising a water insoluble polymeric binder having both a hard and a soft component. 6. The aqueous coating composition of claim 5 wherein the hard component comprises a member selected from the group consisting of copolymers and terpolymers of acrylonitrile, ethyl acrylate, butylacrylate, methylmethacrylate and mixtures thereof. 7. The aqueous coating composition of claim 6 wherein the hard component comprises a copolymer of approximately 10-20% by weight of acrylonitrile and approximately 80-90% by weight of a member selected from the group consisting of ethylacrylate and butylacrylate. 8. The aqueous coating composition of claim 6 wherein the hard component comprises a terpolymer of approximately 10-20% by weight of acrylonitrile, approximately 10-25% by weight ethylacrylate, approximately 60-80% by weight butyl- acrylate and approximately 10-20% by weight methylmethacrylate. 9. The aqueous coating composition of claim 5 wherein the soft component comprises a polymer emulsion of a polyurethane having a glass transition temperature of between approximately -10 * C to -40 * C. 10. The aqueous coating composition of claim 5 further comprising a flow agent, antifoaming agent, wetting agent and lubricant. 11. The aqueous coating composition of claim 10 wherein said flow agent is an alkyline-soluble emulsion of ethyl acrylate and acrylic acid. 12. The aqueous coating composition of claim 10 wherein said lubricant comprises a member selected from the group consisting of aliphatic and aromatic stearates, silicone oils, perfluoro alkyl polyethers and fluorinated fluids having one of the following structures: wherein n = 40- 90 « 40' -90 and F-fcF(CF 3 )CF 2 θ] n |C 2 F 5 wherein n' * 14- -45 and mixtures thereof, •

Inventors: IQBAL SIKANDAR, IQBAL, SIKANDAR
Applicants: MEMOREX CORP, MEMOREX CORPORATION
Application year: 1983
Main classification: G11B5
IPC codes: G11B5