CATALYTIC PREPARATION OF DIMETHYL ETHER

Abstract: In the preparation of dimethyl ether by the catalytic dehydration of methanol, reaction rate is enhanced and catalyst coking and byproduct formation are significantly reduced when an aluminosilicate containing a high level of alumina is used as the catalyst.

Description: CATALYTIC PREPARATION OF DIMETI1YL ETHER This invention relates to an improved method for the preparation of dimethyl ether by the catalytic dehydration of methanol. It is more particularly directed to such a method in which the catalyst used is an aluminosilicate containing a high proportion of alumina. Dimethyl ether is a commodity in the chemical industry, widely used as a starting material in the preparation of other chemicals, e.g., dimethyl sulfate, and more recently, as a propellant in aerosol containers. One of the commonly used methods for preparing dimethyl ether is the catalytic dehydration of methanol, using a phosphoric acid-alumina catalyst. While that process is generally satisfactory, the catalyst has a tendency to coke, which makes it necessary to replace it more frequently than is desirable. By "coke" is meant the phenomenon by which the surface of the catalyst becomes coated with carbon, thus blocking its pores and reducing its effectiveness. It has now been found that this coking can be minimized if, instead of the phosphoric acid-alumina catalyst, one uses an aluminosilicate catalyst containing 1-20 wt % silica and 80-99 wt V,Ó alumina. Surprisingly, use of such a catalyst according to the invention not only reduces the amount of coking but also significantly increases the rate of the dehydration reaction over that obtained with the phosphoric acid-alumina catalyst, and greatly reduces the number and amounts of byproducts formed, notably hydrogen, carbon monoxide, methane, ethane, propane, ethylene, propylene and various ethers having high boiling points. The catalytic dehydration of methanol to form dimethyl ether is well known and is described in detail in U.S. Patent 2,014,408. The reaction proceeds according to the general equation: - EMI2.1 The product of the reaction is principally a mixture of dimethyl ether, unreacted methanol and water. The reaction is ordinarily conducted continuously in a column reactor in the vapor phase, generally at a maximum reactor bed temperature of 200-500 C, preferably 275-4200C, and normally at a pressure ranging from ambient to 3447 kPa (gauge), preferably 1034-1723 kPa (gauge). The catalyst is in practice packed into the reactor in the customary way, and the vaporized and pre-heated (200-3000C) methanol passed through it, preferably downwardly. Residence time of the methanol in the reactor is determined according to well-known chemical engineering principles, as are the methods of recovering the dimethyl ether from the reactor effluent and the methods of refining it. The catalysts used according to the invention are aluminosilicates containing 1-20% by weight of silica and 80-99% by weight of alumina, preferably 1-10% of silica and 90-99% of alumina, even more preferably about 6% of silica and about 94% of alumina. A catalyst especially suited for use according to the invention is an aluminosilicate containing about 6% silica and about 94%alumina, sold by Harshaw Chemical Company of Beachwood, Ohio, as A1-1602. The catalysts can he made by the well-known method of coprecipitating appropriate amounts of sodium silicate and sodium aluminate from aqueous solution by bringing the solution to a pH of about 8 with hydrochloric acid, at a temperature of 50-700C. The resulting gel, a mixture of hydroxides, is recovered, then normally washed free of chlorides, dried to a free-flowing powder, pelleted and then calcined at 450-6500C to give a material which con be used directly as the catalyst. The catalyst is customarily used in the form of cylindrical pellets. Pellet size is selected according to recognized chemical engineering principles, and is usually in the range 2-130 mm in all dimensions. The pore volume, pore size and total surface area of the pellets are likewise a matter of choice, and will generally be in the ranges of 0.2-0.8 cc/g, greater than 25 angstrom units, and 100-250 m2/g, respectively. EXAMPLE - Best Mode In the following description, all parts are by weight. Six hundred parts of Harshaw A1-1602 in the form of 6.5 mm cylindrical pellets were packed into an adiabatic column reactor having a length/diameter ratio of 5. Methanol, preheated to 27OOC, was then continuously fed into the top of the reactor. The vapors were passed downwardly through the catalyst bed at a rate of 9000 parts per hour. Pressure in the reactor was 1034 kPa (gauge! and the reactor bed temperature reached a maximum of 390 C. The vapors leaving the reactor were condensed to give a product having the average composition: Dimethyl ether 57 /° Methanol 20etc Water 23%

Claims: CLAIMS 1. A process for the preparation of dimethyl ether which process comprises the catalytic dehydration of methanol using-as the catalyst an aluminosilicate which contains-, by weight, 1-20% of silica and 80-99% alumina. 2. A process as claimed in claim 1 in which the catalyst contains 1-10 by weight of silica and 90-99% by weight of alumina. 3. A process as claimed in claim 1 or claim 2 in which the catalyst contains about 6% by weight of silica and about 94% by weight of alumina. 4. A process as claillle( in any one of claims 1 to 3 wherein the methanol is contacted with the catalyst at a temperature of from 2750C to 4200C. 5. A process as claimed in any preceding claim wherein the methanol is contacted with the catalyst at a pressure of from 150 psig (1034 kPa gauge) to 250 psig (1723 kPa gauge).

Inventors: BRAKE, LOREN DALE
Applicants: E.I. DU PONT DE NEMOURS AND COMPANY
Application year: 1983
Main classification: C07C43
IPC codes: C07C41, C07B61, C07C67, B01J21, C07C43