CONTAINERS HAVING HEAT-SEALED JUNCTURE REGIONS

Abstract: A container having at least one heat-sealed juncture is formed from foam polymer sheet material. The foam polymer sheet material includes an area of crushed and compressed cellular structure directly adjacent the heat­ sealed portion. The width of the crushed and compressed area is at least as great as the thickness of uncompressed foam in the layer.

Description: CONTAINERS HAVING HEAT-SEALED JUNCTURE REGIONS The present invention is related to containers of the type having at least one heat-sealed juncture region, and more particularly, to such containers formed from foam polymer sheet materials. Foamed polystyrene is used for products such as egg cartons, food containers and meat trays, since this material is readily thermoformable. However, many container structures are not suitable for thermal formation. Such structures include envelopes, multi-sided cartons, pouches for items such as french fries and others. These structures require a material which can be folded without cracking or breaking at the fold point, thereby excluding conventional foam polystyrene and poly(p-methylstyrene). Also, these structures require that juncture points of the panels be fastened together by heat sealing. However, foamed polystyrene generally has not been satisfactory for heat sealing, perhaps because of the thickness differential between the actual sealed portion and the remaining foamed structure. U. S. Patent No. 4,201,818 describes a flex ible plastic foam formed by partially crushing a foam sheet between textured rollers. The treatment is said tQ provide a product suitable as a replacement for pap er. UK Patent Application No. 2,096,616A includes a similar disclosure. U. S. Patent No. 3,256,527 describes a process for forming envelopes by heat sealing. Two -layers of foam are heat-sealed through the application of heat and pressure. Heat is also applied for a short distance beyond the area in which pressure is applied. The instant application relates to a container comprising a first layer of a foam polymer sheet material; a second layer of a polymer sheet material which is heat-sealed to the first layer; the first layer having an area of crushed and compressed cellular structure adjacent to at least one of the two major surfaces of the layer located directly adjacent the heat-sealed portion, the area of crushed and compressed cellular structure having a width which is at least as great as the thickness of uncompressed foam in the first layer. To produce such a first layer, there is employed a polymer foam which has been treated in such a way as to crush and compress the cell structure of the foam, thus partially destroying the resilience and surface character of the foam and removing at least some compressed gaseous material trapped within the foamed structure. This also reduces the gauge of the foam and causes some of the previously gas-filled cells to become crushed and compressed. This treatment is accomplished by sandwiching the foamed plastic sheet between surfaces, at least one of which is textured, for instance sereen-like, placed in a press or other suitable compressing means and compressed to reduce the thickness of the sheet while si multaneously crushing a substantial portion of the cells of the foamed sheet at one or both surfaces of the heet. Although the cells of the foam become crushed, they remain unruptured. Some ruptured cells can be found at the surface, but no more than can be found with uncrushed foam. The foam is crushed to be about 60-70% of its original thickness. Preheating the foam has been found to have little effect. The foam cells tend to be flattened in the direction of applied pressure and buckle in an nsn curve. The foamed sheet can be subjected to a second compression between smooth surfaces if a sheet with a smoother surface is desired. This will further densify or further reduce the thickness of the foamed sheet and also restore some of the smooth character to the surface of the sheet. This process is described in the aforementioned U. S. Patent No. 4,201,818. Foamed sheet processed in the manner described above possesses improved folding characteristics. The terms folding" or "foldable" are used in the same sense that cellulosic paper is foldable. Just as paper can be folded upon itself and creased at the fold line, the crushed and compressed foamed polymer has at least similar characteristics. The product formed as a result of this process possesses excellent paper-like surface characteristics. Generally, a paperboard will be stiffer and show greater tensile strength than the crushed foam. The foam can be used in a laminate with cloth and7or another polymer such as high impact polystyrene to provide improved mechanical properties. Compression of the foam does not decrease thermal insulation properties, and the compressed foam is about twice as effective as an insulator than paperboard. The compressed foam also has improved oxygen, moisture and grease resistance as compared to paperboard. It also has been determined that as a result of processing the sheet in this manner, the resulting polymer can be bonded- to itself or to another material with a bonding strength which is considerably stronger than foamed polymer not possessing the crushed and compressed cells obtained as a result of the compression treatment. Examples of useful products include envelopes, place mats, cups, ice cream cartons, pie or sandwich boxes, french fry pouches and serving trays. Fig. 1 shows a sectional side view of a heatsealed envelope prepared from a sheet of foam polymeric material according to the present invention; and Fig. 2 shows a sectional side view similar to that of Fig. 1, except using one layer of unfoamed polymeric material. Referring to Fig. 1, an envelope can be prepared which has two layers 10 and 12 of foamed polymeric sheet material. These layers can be produced by using two separate sheets of material, or by folding a single sheet of material upon itself. The two layers are join ed at the heat-sealed region 14. Directly adjacent to the heat-sealed portion of the envelope is an area of crushed and compressed cellular structure 16 or 17. Crushed areas 15 and 17 have been formed through compression of one major sur face of layers 10 and IS, respectfully. However, it would be equally effective to crush both major surfaces of each layer prior to heat sealing. The compressed and crushed cellular structure of the areas 16 or 17 is adjacent to at least one of the two major layer sur faces. That is, the compressed and crushed cellular structure may be near the top and/or bottom of each respective layer 10 and 12. It also is desirable to have the crushed celular structure in the area of any folding. Crushed areas 16 and 17 each have a width which is at least as great as the thickness of uncrushed portion 18 and 19 of the sheet material. The thickness of the uncrushed portion of the foam layer is meant to refer to the thickness in the vicinity of the crushed and compressed area. Variations in the thickness of the layer 18 or 19 at points removed from the crushed areas 16 and 17 have no bearing upon the performance of the present invention. Also, it should be noted that the width of the crushed areas 16 and 17 can be independent of each other. For example, if layer 10 was thinner than layer 12, its crushed area 16 could be narrower than area 17. Also, it is not essential that the portions 18 and 19 be present at all. That is, both layers 10 and 12 may be composed of completely crushed and compressed foam polymer sheet material. Line 20 is provided in Fig. 1 to show the boundary between the layers 10 and 12. The layers 10 and 12 are not physically joined along line 20 but rather merely abut each other and are easily parted to provide the opening within the envelope. Fig. 2 shows a second embodiment of the present invention which includes layers 22 and 24, which are heat-sealed together at 26. Layer 22 is of a foamed material while layer 24 is of an unfoamed polymer. The choice of unfoamed polymer will depend upon the desired use of the product, but may include unfoamed polyethy lene or unfoamed polystyrene. Like layers 10 and 12 of Fig. 1, layer 22 is provided with crushed and compressed area 28. As with the previous embodiment, crushed area 28 has a width which is equal to the thickness of the uncompressed portion 30 of layer 22. As mentioned pre viously, it is not essential that layer 22 be provided with an uncrushed portion 30. Layer 22 may be formed from a sheet which is completely crushed. As mentioned in relation to crushed areas 16 and 17, area 28 has been formed through compression at one major surface of layer 22. However, it would be equally effective if layer 22 was crushed at both major surfaces prior to heat sealing. The present invention contemplates employing any foamed thermoplastic polymer, the cells of which can be crushed and compressed so that its gauge can be re duced. Preferred are polystyrene and poly(p-methyl styrene) foam. In accordance with U.S. Patent No. 4,201,818, a polystyrene foamed sheet of a density of 0.016 glum2 (10 g/100 in.2) basis weight was pressed between window screens of mesh size 20 at a pressure of about 4619.kPa (670 psi) for about ten minutes. The sheet prior to pressing had an average thickness of about 2.54mn (100 mils). Following compression the sheet had an average thickness of about 0.89cm 735 mils). Strips of- the so pressed and so fractured foam were heat-sealed on a Vertrod Thermal Impulse Heat Sealer. The seals produced were significantly stronger than seals formed in strips of unpressed foam. Strips made of the precursor, unpressed foam which were heatsealed, broke apart quite easily. The weakness is believed to be due to the thickness differential between the interfacial sealed region and the gross thickness of the uncrushed cellular foam structure. This gross cel lunar thickness is considerably reduced by the process of U.S. Patent No. 4,201,818 and the result is that a crushed and compressed cell structure of- this type provides an excellent heat-sealed region. In accordance with the present invention three types of containers were made having the comparatively strong heat seal junctures described herein. One is a mailing envelope prepared by folding a length of crushed and compressed polystyrene sheet upon itself so as to leave a closure flap extending beyond the folded over portion. The sides were heat-sealed and the extension cut to a triangular shape for sealing or fastening by any means, including heat-sealing. Another was a tetra hedron carton with heat-sealed junctures made from the same polystyrene stock. The third was a pouch, such as could be used as a container for french fried potatoes. This was formed by as sheet folded back upon itself and side heat-sealed. In all cases the heat-seals were firm and of greater strength than would be the case if non crushed and noncompressed foam were employed.

Claims: CLAIMS : 1. A container comprising a first layer of a foam polymer sheet material; a second layer of a polymer sheet material which is heat-sealed to the first layer; the first layer having an area of crushed and compressed cellular structure adjacent to at least one of the two major surfaces of the layer located directly adjacent the heat-sealed portion, the area of crushed and compressed cellular structure having a width which is at least as great as the thickness of uncompressed foam in the first layer. 2. The container of Claim 1, wherein the second layer is of a foam polymer sheet material having an area of crushed and compressed cellular structure adjacent to at least one of the two major surfaces of the layer located directly adjacent the heat-sealed portion, the area of crushed and compressed cellular structure having a width which is at least as great as the thickness of uncompressed foam in the second layer. 3. The container as in Claim 1, wherein the second layer is of an unfoamed polymer sheet material. 4. The container of any preceding claim, wherein the crushed and compressed cellular structure is ad jacent to each of the two major surfaces of the first layer. 5. The container of Claim 1 or 2, wherein the crushed and compressed cellular structure is adjacent each of the two major surfaces of each of the first and second layers. 6. The container of any preceding claim, wherein the first and second layers are composed of polystyrene or poly(p-methylstyrene).

Inventors: MIER, MARJORY ANNE
Applicants: MOBIL OIL CORPORATION
Application year: 1983
Main classification: B65D30
IPC codes: B32B1, B32B5, B65D30, B29C53, B29C65, B29C44