FLAME RETARDED RESIN COMPOSITION

Abstract: A flame retarded resin composition comprising an inflammable resin and at least one tetrabromodihydroxy­ diphenylmethane selected from the group consisting of the compounds having the formulae:

Description: FLAME RETARDED RESIN COMPOSITION BACKGROUND OF THE INVENTION FIELD OF THE INVENTION This invention relates to a flame retarded resin composition. More particularly, this invention relates to a flame retarded resin composition comprising an inflammable resin and a flame retarder. DESCRIPTION OF PRIOR ARTS Most of resins employed in practice are inflammable. For converting these inflammable resins to flame retarded resins, a flame retarder such as a phosphate ester, a halogen-containing phosphate ester, or a halogen compound is generally added to the inflammable resin. Out of these known flame retarders, the phosphate ester retarder and halogen-containing phosphate ester retarder are mainly employed. However, most of both retarders are liquid, and their uses are accordingly limited to arts for retarding inflammability of urethane resin, vinyl chloride resin, and the like. As for the halogen compound, chlorine compounds were generally employed. However, except for a chlorinated polyethylene and polychlorocyclopentadecane (trade name: Decloran, available from Hooker Chemical Corp.), most of the halogen compound flame retarders have been recently replaced with bromine compound flame retarders. The reason for the replacement is thought as follows: First, the bromine compound provides flame retarding effect several times as much as the chlorine compound when compared at the same dosage level. Second, the bromine compound is less corrosive to metal surfaces of electric machinery and apparatus than the chlorine compound is. Third, the preparation of chlorine compound flame retarders possibly causes environmental pollutions. The bromine compound flame retarders include a variety of types, such as an aliphatic compound type, an alicyclic compound type, and an aromatic compound type. These types of bromine compound flame retarders are properly employed depending upon nature of the resin to be flame-retarded and requirement level of flame retarding. Nevertheless, the aliphatic bromine compound flame retarders generally are poor in both heat resistance and weather resistance, and therefore are recently replaced with more stable alicyclic bromine compound flame retarders. Moreover, more stable aromatic bromine compound flame retarders are usually employed for resins requiring high stability. However, contrary to assumption, previously known aromatic bomine compound flame retaders such as tetrabromobisphenol A (referred to herein as TBA) often show poorer flame retarding effect than the aliphatic and alicyclic bromine compound flame retarders do. It is presumed that such poor flame retarding effect of the aromatic bromine compound flame retarder is caused by the fact that said retarder is easily agglomerated andununiformly dispersed within a resin. SUMMARY OF THE INVENTION Accordingly, a primary object of the present invention is to provide a flame retarded resin composition comprising an inflammable resin and a flame retarder. Another object of the invention is to provide an aromatic bromine compound flame retarder showing high dispersibility within an inflammable resin and thus imparting high flame retarding property to the inflammable resin. The present invention provides a flame retarded resin composition comprising an inflammable resin and at least one tetrabromodihydroxydiphenylmethane selected from the group consisting of (A) compound I having the formula: EMI3.1 (B) compound II having the formula: EMI3.2 and, (C) compound III having the formula: EMI3.3 DESCRIPTION OF PREFERRED EMBODIMENTS In the present invention, the flame retarder, namely, the compound I, compound II, and compound III, all of which are classified into the tetrabromodihydroxydiphenylmethane, are employable alone or in com bination. The flame retarder of the invention may further comprise small amounts of a trimer having the formula: EMI4.1 and a tetramer having the formula: EMI4.2 The tetrabromodihydroxydiphenylmethane employed as the flame retarder in the invention can be prepared by condensating phenol with formalin and brominating the so obtained condensate consisting mainly of dihydroxydiphenylmethane in the hydroxyl group-free positions, namely, ortho- and para-positions. The te trabromodihydroxydiphenylmethane obtained as above generally comprises all of the compound I, compound II and compound III, in which compound I amounts to 4 - 24 mol %, preferably 10 - 20 mol %; compound II amounts to 35 - 55 mol %, preferably 40 - 50 mol %; and compound III amounts to 22 - 42 mol %, preferably 25 35 mol %. In the tetrabromodihyroxydiphenylmethane mixture obtainable as above generally contains the aforementioned trimer and tetramer. Accordingly, the tetrabromodihydroxydiphenylmethane of the invention may comprise 80 - 99 mol %, preferably 85 - 95 mol %, of the compounds I, II, and III (I + II + III), and 1 - 20 mol %, preferably 5 - 15 mol %, of the trimer and tetramer (trimer + tetramer). In the resin composition of the present invention, there is no specific limitation on the inflammable resin. Examples of the inflammable resin employable in the invention include polystyrene, AS resin, ABS resin, nylon 11, nylon 12, polypropylene, polyethylene, polymethyl methacrylate, polyurethane, polyvinyl chloride, phenol resin, epoxy resin and unsaturated polyester. The flame retarded resin composition of the present invention preferably comprises 60 - 95 % (more preferably 70 - 92 %) by weight of an inflammable resin and 5 40 % (more preferably 8 - 30 %) by weight of tetrabromodihydroxydiphenylmethane. The flame retarder of the present invention, that is, tetrabromodihydroxydiphenylmethane is, very uniformly dispersed in an inflammable resin. Accordingly, the resin composition containing tetrabromodihydroxydiphenylmethane is prominently improved in resistance to flame as compared with the resin compositions containing the conventional aromatic bromine compound flame retarders such as TBA and the like (which are poor in dispersibility in inflammable resins, thus resulting in imparting poor resistance to flame to the resins), when employed at the same dosage level. Moreover, since tetrabromodihydroxydiphenylmethane shows high dispersibility in inflammable resins, the same can be incorporated uniformly into a resin in a relatively great amount so as to enable the inflammable resin to show highly improved resistance to flame. In the flame retarded resin composition of the invention, tetrabromodihydroxydiphenylmethane can be comprised together with one or more other flame retarders and/or one or more flame-retarding assistants such as antimony trioxide. If necessary, other addi tives such as glass fibers, inorganic fillers, etc. can be incorporated as well. The present invention is further described by the following examples. Tetrabromodihydroxydiphenylmethane referred to as Retarder F or Ret-F in the following examples was prepared as follows: One mol. of phenol and 0.03 mol. of 37% formalin were condensed at 1000C for 1 hour in the presence of 0.7 g. of oxalic acid. After the reaction was complete, excess phenol was removed by evaporation to obtain a condensate. In a 3-1. flask equipped with a stirrer, a condenser, a thermometer and a dropping funnel were placed 210 g; of the condensate, 850 g. of methanol, and 150 g. of water. The mixture was stirred at room temperature until a solution was produced. Into the flask under cooling was dropped 656 g. (4.1 mol.) of bromine to undergo substitution reaction. The reaction mixture was then kept at 60 C for 2 hours for aging to obtain a product at a slurry state. The product was poured into water and then the mixture was stirred. Subsequently, the product was collected by filtration, washed with water, and dried to obtain 534.1 g. of a product. tetrabromodihydroxydiphenylmethane The so obtained product was analyzed in a high speed liquid chromatography (HLC-802, manufactured by Toyo Soda Mfg. Co., Ltd., Japan) and a gas chromatography (GC-7A, manufactured by Shimadzu Seisakusho Ltd., Japan) to reveal content of the product as follows; EMI7.1 13 mol. % 45 mol.% 32 mol. % 8 mol. % EMI7.2 2 mol. % EXAMPLES (1) Preparation of Test Specimen To polystyrene (impact resistant grade, Estyrene H-60, produced by Nippon Steel Chemical Co., Ltd., Japan), AS resin (Estyrene AS-61NT, Nippon Steel Chemical Co., Ltd.), ABS resin (plating grade, Diapet 3001M, produced by Mitsubishi Rayon Co., Ltd., Japan), and nylon 12 (3014B, produced by Ube Industries, Ltd., Japan) was added Retarder F (Ret-F, prepared as above), TBA (Fireguard FG-2000, produced by Teijin Chemical Co. Ltd., Japan), a combination of Retarder F (Ret-F) and antimony trioxide (Sb203, purity 99 %, produced by Nihon Mining & Concentrating Co., Ltd., Japan), and a combination of TBA and antimony trioxide in the amounts set forth in Tables 1 - 4. These are uniformly blended in a tumbling mixer and kneaded under melted conditions in a double-screw extruder (PCM-30, manufactured by Ikegai Iron Works, Ltd., Japan) to prepare pellets. The pellets were then moulded in an injection machine to obtain test specimens (5 in. x 1/2 in. x 1/16 in.) for Standard UL-94, as well as test specimens (5 in. x 1/4 in. x 1/8 in.) for Flammability Test defined in ASTM D 2863. (2) Procedures of Flammability Tests The flammability tests were carried out in accordance with Standard UL-94 (Underwriters-Laboratories Inc. of USA) and ASTM D 2863 (Flammability of Plastics Using the Ocygen-Index Method. In the Standard UL-94 test, a test specimen catching fire on the cotton even for a few seconds were marked UL-94 V-2 according to the Standard. (3) Procedure for Observation on Dispersibility of Flame Retarder The test specimen for the oxygen index flammability test was freeze-dried and ruptured to show a crosssection, from which TBA or Retarder F was extracted with methanol at room temperature for 30 min. The crosssection of the ruptured specimen was then subjected to microscopic observation on the dispersibility by means of a scanning type electron microscope (H-6010 type, manufactured by Hitachi Ltd., Japan). (4) Results The compositions tested in the examples and their test results are set forth in Tables 1 - 4. As is apparent from the results, the resin compositions containing Retarder F according to the present invention show excellent dispersibility and flame retarding effect. Table 1 (Resin: Polystyrene) Dispersi- Flammabilitty Oxygen bility (1/16 in.) Index UL-94 Reference Resin 100 wt.% - Flammable 18.0 Comparison Example 1 Resin 90 wt.% TBA 10 Uniform V-2 - 21.1 2 Resin 90 wt.% TBA 8 Sub 203 2 Uniform Flammable 21.1 3 Resin 80 wt.% TBA 20 Ununiform Flammable 23.7 4 Resin 80 wt.% TBA 16 Sub2O3 4 Ununiform V-2 26.3 Example 1 Resin 90 wt.% Ret-F 10 Uniform V-2 23.2 2 Resin 90 wt.% Ret-F 8 Sb203 2 Uniform V-2 23.2 3 Resin 80 wt.% Ret-F 20 Uniform V-2 25.9 4 Resin 80 wt.% Ret-F 16 Sub2O3 Uniform V-O 28.9 Table 2 (Resin: AS resin) Dispersi- Flammability Oxygen bility (1/16 in.) Index UL-94 Reference Resin 100 wt.% - Flammable 18.9 Comparison Example 5 Resin 90 wt.% TBA 10 Uniform V-2 22.4 6 Resin 90 wt.% TBA 8 Sb2 3 2 Uniform V-2 21.1 7 Resin 80 wt.% TBA 20 Ununiform V-2 23.7 8 Resin 80 wt.% TBA 16 Sb2O3 4 Ununiform V-2 25.4. Example 5 Resin 90 wt.% Ret--F 10 Uniform V-2 25.0 6 Resin 90 wt.% Ret-F 8 Sub203 2 Uniform V-O 23.2 7 Resin 80 wt.% Ret-F 20 Uniform V-O 26.3 8 Resin 80 wt.% Ret-F 16 Sub2O3 4 Uniform V-O 28.5 Table 3 (Resin: ABS resin) Dispersi- Flammability Oxygen bility (1/16 in.-) Index UL-94 Reference Resin 100 wt.% - Flammable 18.9 Comparison Example 9 Resin 90 wt.% TBA 10 Uniform Flammable 22.4 10 Resin 90 wt.% TBA 8 Sb203 2 Uniform Flammable 22.8 11 Resin 80 wt.% TBA 20 Ununiform V-2 27.2 12 Resin 80 wt.% TBA 16 Sb203 4 Ununiform V-2 26.8 Example 9 Resin 90 wt.% Ret-F 10 Uniform V-2 24.1 10 Resin 90 wt.% Ret-F 8 Sub 203 2 Uniform V-2 24.1 11 Resin 80 wt.% Ret-F 20 Uniform V-2 29.4 12 Resin 80 wt.% Ret-F 16 Sub 203 4 Uniform V-O 32.0 Table 4 (Resin: Nylon 12) Dispersi- Flammability Oxygen bility (1/16 in.) Index UL-94 Reference Resin 100 wt.% - V-2 21.1 Comparison Example 13 Resin 90 wt.% TBA 8 Sub2O3 2 Uniform V-2 26.3 14 Resin 80 wt.% TBA 16 Sub2O3 4 Ununiform V-O 30.3 Example 13 Resin 90 wt.% Ret-F 8 Sb203 2 Uniform V-2 28.1 14 Resin 80 wt.% Ret-F 16 Sb203 4 Uniform V-O 32.0

Claims: CLAIMS: 1. A flame retarded resin composition comprising an inflammable resin and at least one tetrabromodihydroxydiphenylmethane selected from the group consisting of (A) compound I having the formula: EMI14.1 (B) compound II having the formula: EMI14.2 and, (C) compound III having the formula: EMI14.3 2. The flame retarded resin composition as claimed in Claim 1, in which the composition comprises 60 - 95 % by weight of an inflammable resin and 5 - 40 % by weight of tetrabromodihydroxydiphenylmethane. 3. The flame retarded resin composition as claimed in Claim 2, in which the composition comprises 70 - 92 % by weight of an inflammable resin and 5 - 30 % by weight of tetrabromodihydroxydiphenylmethane. 4. The flame retarded resin composition as claimed in Claim 1, in which the compound I, compound II and compound III are all comprised in the composition. 5. The flame retarded resin composition as claimed in Claim 4, in which the molar ratio of the compounds I : II : III is 4 - 24 : 35 - 55 : 22 - 42. 6. The flame retarded resin composition as claimed in Claim 5, in which the molar ratio of the compounds I : II : III is 10 - 20 : 40 - 50 : 25 - 35. 7. The flame retarded resin composition as claimed in Claim 1, in which a trimer having the formula: EMI16.1 and a tetramer having the formula: EMI16.2 are further comprised in the composition. 8. The flame retarded resin composition as claimed in Claim 1, in which at least one flame retarding assistant is further comprised in the composition. 9. The flame retarded resin composition as claimed in Claim 8, in which the flame retarding assistant is antimony trioxide. 10. The flame retarded resin composition as claimed in Claim 1, in which the inflammable resin is selected from the group consisting of polystyrene; AS resin, ABS resin, nylon 11, nylon 12, polypropylene, polyethylene, polymethyl methacrylate, polyurethane, polyvinyl chloride, phenol resin, epoxy resin and unsaturated polyester.

Inventors: FUKUDA, KIMIO C/O HIRAKATA RESIN LABORATORIES, ITO, BUNSAKU C/O HIRAKATA RESIN LABORATORIES
Applicants: UBE INDUSTRIES, LTD.
Application year: 1983
Main classification: C08K5
IPC codes: C08L77, C08L33, C08K5, C07C67, C08L1, C09K21, C08L51, C08L67, C08K3, C08L7, C07C39, C07C27, C08L21, C08L101, C08L23, C08L27