HIGH CHARGE DENSITY, CATIONIC METHACRYLAMIDE BASED MONOMERS AND THEIR POLYMERS

Abstract: A new material comprising an acrylamide or methacryla­ mide monomer characterised by the following structural formula: wherein R₁ and R₂ are hydrogen or methyl; R₃, R₄, R₅, R₆ and R₇ are lower alkyls; n is an integer ranging from 1 to 6 and X and Y are the same or different anions.

Description: HIGH CHARGE DENSITY, CATIONIC METHACRYLAMIDE BASED MONOMERS AND THEIR POLYMERS This invention relates to novel acrylamide or methacrylamide monomers and polymers. More particularly, the present invention relates to bis-quaternary ammonium acrylamide or methacrylamide monomers and polymers. Quaternary ammonium monomers of the acrylamide or methacrylamide type are set out in United States Patents Nos. 3,666,810, 4,180,643 and 4,212,820. United States Patent No. 3,962,332 discloses a di-olefin###lly unsaturated compound which contains two quaternary ammonium moieties. The polymers and co-polymers of the bis-quaternary compounds are characterised by high charge density, and find application as flocculants, paper sizes and electroconductive aids. United States Patents Nos. 3,689,468, 3,766,156 and 4,009,201 disclose acrylic acid ester monomers and polymers containing a bisquaternary ammonium halide group for use in a variety of environments, including anti-static agents and flocculants. These compounds, however, contain a hydrolitically unstable ester linkage which \renders the polymers formed from those cationic monomers unsuitable for use in aqueous systems. The present invention surprisingly provides new stable novel cationic monomers which have unique usefulness in areas of application for which the known most closely related materials are unsuitable. Accordingly, the present invention provides a new class of cationic acrylamides and methacrylamides which are useful for a wide variety of purposes normally requiring ionic charged monomers of this general type. The invention provides acrylamide and methacrylamide monomers characterised by the following formula: EMI2.1 wherein R1 and R2 are hydrogen or methyl, R3, R4, R5 R6 and R7 are alkyls of 1 to 4 carbon atoms, n is an integer ranging from 1 to 6 and X and Y are the same or different anions. A preferred monomer of the above defined class of unsaturated bis-quaternary organic compounds can, for example, be synthesised by reacting a 1-chloro-2-hydroxypropyl trimethylammonium halide (e.g., chloride, bromide, fluoride or iodide) with dimethylaminopropylacrylamide or with dimethylaminopropylmethacrylamide. The synthesis can be conducted conveniently by dissolving the reactants in water or other inert polar solvent such as alcohol (for example methanol, ethanol, isoorop-- anol), butanol, benzene, toluene, xylene, acetonitrile, dimethylformamide, te trahydro furan, acetone or dioxane. Mixtures of water and one of the organic solvents mentioned, whether miscible with the water or not, may be used. Preferably the reaction mixture is heated to a temperature in the range from 400C up to the refluxing temperature of the reaction mixture. The time of reaction varies between several minutes and several hours depending mainly on the reaction temperature. The reactants are usually employed in approximately equimolar proportions. It is advantageous to maintain the pH of the system at about 7 so as to prevent hydrolysis of amido groups in the compounds. It is a particular advantage of the compounds of the present invention that they do not contain easily hydrolysable ester groups. By the method of synthesis described above, there are produced compounds of structural formula I in which the anions are of the halide type. These anions can be replaced with other anions by conventional techniques such as by contacting the quaternary halides with an appropriate ion exchange resin. Examples of various anions for X and Y include hydroxide, nitrate, sulfate, sodium acid sulfate, chromate, phosphate, methyl sulfate, acetate, formate, oxalate, sulfamate and acrylate. The unsaturated bis-quaternary monomer compounds of the present invention are readily polymerisable, and the aqueous solutions resulting from the above-described synthesis can be employed directly for this purpose. Any knows polymerisation initiator of the free radical type may be selected for use, such as t-butyl hydroperoxide, ammonium persulfate, alkali metal persulfates, the tetra sodium salt of ethylene diamine tetraacetic acid (EDTA), and 2,2'-Azobis(2amidinopropane) hydrochloride and mixtures thereof. The initiator is usually effective in quantities between 0.01% and 5% by weight, based on the weight of the unsaturated bisquaternary monomer. A redox initiator system can be provided by including a reducing agent such as sodium hydrosulfite in the initiator system. These new unsaturated bis-quaternary compounds can be co-polymerised with any other polymerisable olefirrically unsaturated monomer, preferably in aqueous solution and emulsion polymerisation systems with redox initiation. Highly preferred co-polymers of the present invention, which exhibit outstanding properties for application as flocculants and electroconductive aids, are those comprising acrylamide co-polymerised with an unsaturated bis-quaternary compound of structural Formula (I). Any other water-soluble monomer can be co-polymerised with the monomer of Formula (I). Preferred water-soluble monomers include acrylic and methacrylic acid, hydroxyethyl acrylate or methacrylate, hydroxypropyl acrylate or methacrylate, N-methylol acrylamide, N-monoalkyl and -dialkyl acrylamides and methacrylamides. An alternative method for producing co-polymers containing the monomer of Formula (I) is by reacting a polymerisable monomer such as the preferred acrylamide with dimethylaminopropylacrylamide or with dimethylaminopropyl methacrylamide. The co-polymer so produced may then be quaternised by reaction with 1-chloro-2-hydroxypropyl trimethylammonium halide. The co-polymers can generally contain from 0.1% to 95% of a co-monomer. However, the preferred range for most applications is limited to 5% to 70% of a co-monomer, where water-solubility and high charge densities are controlling factors and require the presence of a high population of quaternary groups in the co-polymers. The polymers and co-polymers of the present invention are viscous to solid resinous materials of water-soluble character. They are generally also partially soluble or dispersible in polar organic solvents, for example methanol, acetonitrile or tetrahydrofuran. The molecular weight of the polymers and co-polymers is generally in the range from 20,000 to 2,000,000, preferably at least 500,000. It is an important feature of the present invention that the monomers having structur#Formula (I) do not contain ester linkages, and therefore homo-polymers and co-polymers thereof exhibit outstanding resistance to hydrolysis and chemical degradation. The polymers and co-polymers are therefore versatile in a wide range of applications under extreme conditions of temperature and chemical environment. A polymeric composition of the present invention can be incorporated into paper pulp to render it eledroconducti-ve for the production of paper stock for electrostatic image reproduction systems. For example 0.1% to 10% by weight of the polymer, based on dry fibre weight, can be added to the wood pulp. Pigments and other additives known and used in the paper art can be included. The polymeric compositions of the present invention are suitable for application for paper sizing and as wet strength agents. Co-polymers containing from 0.1% to 20% by weight of bis-quaternary compounds of structural Formula (I) are useful for forming films and coatings having resistance to development of electrostatic charges. The water-soluble polymeric compositions are generally useful as flocculants, particularly the polymeric compositions containing at least 60% by weight of the bis-quaternary compounds of structural Formula (I). The addition of 0.01% to 10% by weight of polymer, based on the weight of suspended solids (e.g., sewage sludge or paper pulp effluent) serves to flocculate the suspended matter and facilitate filtration procedures. The following Examples are further illustrative of the present invention. The reactants and other specific ingredients are presented as being typical, and various modifications within the scope of the invention can be devised in view of the foregoing disclosure. EXAMPLE I To 255 g (1.5 moles) of dimethylaminopropyl methacrylamide (DMSPMA of Texaco Chemical Co.) is added 578.6 g (1.5 moles) of 50.2% aqueous 1-chloro-2-hydroxypropyl trimethylammonium chloride (Quat 188 of Dow Chemical Co.). The resulting solution is heated at 700C for 4 hours. The resulting bis-quaternary monomer has a solids content of 74.6% and apH of 8.1 The calculated monomer content Is 65.4% EXAMPLE II To 255 g (1.5 moles) DMAPMA is added 555 g (1;5 moles) 51.5% active Quat 188. The solution is heated at 800C for 4 hours with a nitrogen sparge during the last 20 minutes. To this is added 0.1 g tetra sodium salt of EDTA and 0.4 g 2,2'-Azobis (2-amidinopropane) hydrochloride (V-50 catalyst of Crescent Chemical Co.) in 10 ml H2O. Heating is continued at 80 0C under N2 sparge for 4 hours. A total of 400 g of H20 is added during this time to reduce the viscosity. A second 0.2 g of 2,2'-Azobis (2-amidinopropane) hydrochloride in 5 ml H20 is added and heating is continued for 2 hours more at 800C under N2. Another 100 g H20 is added during this period. On cooling a viscous, amber polymer solution results with a pH of 7.2. The % NV is 47 2% with a calculated polymer content of 40.8% EXAMPLE Ill The following is charged to a 2 litre 3-neck flask: 70 g H20 100 g 50% Aqueous Acrylamide 229 g Bis-quaternary monomer of Example I 0.1 g Na4EDTA The solution is sparged with N2 for 20 minutes while heating to 8oat. 2,2'-Azobis (2-amidinopropane) hydrochloride, 0.2 g in 1 ml H20, is added and heating is continued at 800C for 2 hours under N2 A total of 500 g H20 is added. A second 0.1 g of 2,2'Azobis (2-amidinopropane) hydrochloride Is added and heating is continued at 800C for 2 hours more under N2. A total of 100 g H20 is added during the second heating period. On cooling a viscous, amber co-polymer solution with apH of 6.9 results. The % NV is 22.7% with a calculated polymer content of 20%. EXAMPLE IV To demonstrate the superior flocculation activity of polymers containing the monomers of the present invention, a homo-polymer of this invention is compared to a homo-polymer of the prior art. The homo-polymer of the prior art is based on the following monomer (United States Patent No. 3,766,156): EMI6.1 which contains a hydrolitically unstable ester linkage. Both homo-polymers are evaluated on an Erie iron ore slime for their.clarification efficiency. A 100 ml cylinder is filled with the iron ore slime and the polymer dosage is added. After inverting 5 times, it is allowed to stand 5 minutes. An aliquot is then taken and the turbidity is measured in ppm using a Hach Model 2100A Turbidimeter. Erie Slimes, Turbidity in pom Amide Based Ester Based Dosage ppm Bis-quat Homopolymer Bis-quat ¯¯¯¯¯¯¯¯¯ Example IT Homopolymer 2 370 1840 4 340 495 6 240 176 It can be seen that the amide based bis-quat homo-polymers of this invention give superior clarity at lower dosage levels. EXAMPLE V The amide based bis-quat homo-polymer of Example II is compared to a prior art amide based quat homo-polymer based on the monomer: EMI7.1 They'are compared for their ability to inhibit the swelling of 100 mesh bentonite clay particles. To 90 ml of water containing a dosage of polymer is slurried 10 g of 100 mesh bentonite. The slurry is hot rolled at 1500F (65.5cm) overnight then sieved to isolate the bentonite. The bentonite is dried and weighed. For complete inhibition all the bentonite is recovered and its texture is much the same as that originally added. Clay Swell Inhibition Minimum Usage Level for Complete Inhibition Amide based bis-quat homo polymer (Example II) 1% Amide based quat homopolymer of prior art 2% Again the superior properties of polymers of this invention are demonstrated by their lower usage levels.

Claims: CLAIMS. 1. A compound of the formula: EMI9.1 wherein R1 and R2 are hydrogen or methyl, R3, R4, Ras, R6 Åand R7 are the same or different alkyls of 1 to 4 carbon atoms, n is an integer ranging from 1 to 6, and X and Y are the same or different anions. 2. A compound of claim 1 in which X and Y are halogen ions. 3. A homo-polymer of a compound of claim 1. 4. A co-polymer of a compound of claim 1 with at least one other olefinically unsaturated monomer. 5. A co-polymer of claim 4 in which the said other olefinically unsaturated monomer is water-soluble. 6. A co-polymer of claim 5 in which the said watersoluble monomer is acrylamide.

Inventors: DAMMANN, LAURENCE G.
Applicants: CELANESE CORPORATION
Application year: 1983
Main classification: C07C103
IPC codes: C08F20, B01D21, D21C11, C02F1, D21H17, D21H25, C07C233