REMOVAL OF CARBON DIOXIDE FROM OLEFIN CONTAINING STREAMS

Abstract: A process for the removal of CO₂ from a gaseous stream containing at least one C₂ to C₄ olefin is provided comprising contacting said stream with a regenerable calcined alkali metal compound-treated alumina.

Description: This invention relates to a process for the removal of carbon dioxide from a gaseous stream containing at least one C₂ to C₄ olefin. Alumina is a well known adsorbent in many chemical processes such as the polymerization of olefins, e.g. ethylene, for the removal of water and small concentrations of methanol, carbonyl-containing compounds, and peroxides. However, the use of alumina has disadvantages that impair its effectiveness as an adsorbent. For example, alumina does not always work as an adsorbent for the removal of CO₂, a well known catalyst inhibitor, from gaseous olefin containing streams which contain CO₂ at low level concentrations (i.e. down to 1 ppm). Molecular sieves are used as adsorbents for CO₂ but are inefficient when used for the removal of CO₂ from a gaseous stream containing low molecular weight olefins such as ethylene. Caustic scrubbers or bulk caustic scrubbers can function as absorbents for CO₂ from a gaseous stream but have the disadvantages of being hazardous, non-regenerable, and adding water to the stream. Therefore, an object of this invention is to provide a process for the removal of CO₂ from gaseous streams employing a regenerable adsorbent which removes even small amounts of CO₂. Other aspects, and the several advantages of the present invention are apparent from a study of this disclosure and the appended claims. In accordance with the present invention, we have discovered that CO₂ can be efficiently removed from a gaseous stream containing a C₂ to C₄ olefin or mixtures thereof by contacting the stream with a regenerable adsorbent consisting essentially of a calcined alkali metal compound-treated alumina as defined in the claims. The removal of water, achieved by the use of alumina in general as known to one skilled in the art, is also within the scope of the present invention. Preferred embodiments of the invention are defined in the dependent claims. Although it is well known in the art to remove CO₂ from gaseous streams by means of solid caustic or caustic solutions (as indicated earlier in this disclosure) which convert CO₂ to an alkali metal carbonate such as Na₂CO₃, this does not occur in the present invention. Instead, CO₂ is chemisorbed on an alkali metal oxide (e.g. Na₂O) alumina surface and can be readily desorbed by mild heating and sweeping the adsorbent bed with a gas free of CO₂. The present invention ist not to be confused with the use of chemical processes which convert CO₂ to alkali metal carbonates in a non-regenerable process which adds water to the gas stream being processed (i.e. 2NaOH+CO₂→ Na₂CO₃+H₂O). In the process of the present invention, CO₂ is removed by a regenerable alumina which at the same time can be used to remove traces of water from the process gas. The gaseous stream treated in accordance with the present invention will contain a C₂ to C₄ olefin or mixtures thereof. Such olefins include ethylene, propylene, isobutylene, 1-butene and 2-butene. The alumina employed in the present invention can be any alumina known in the art. Gamma and eta alumina are preferred and are typically employed. Preferably the alumina employed will contain less than about 20 percent impurities such as SiO₂, Na₂O, Fe₂O₃, TiO₂ and SO = / 4. Broadly the surface area of the alumina should be at least 50 m²/g or greater and preferably 200 m²/g or greater. The alumina employed contains from 1 to 6 weight percent Group IA alkali metal calculated as the oxide form. The level of alkali metal treatment will vary based on the particular alkali metal employed. Thus, when the alumina is treated with a lithium compound, the preferred level of lithium contacted with the alumina support is about 1 to about 3 weight percent calculated as Li₂O. When sodium is employed as the alkali metal, the range of about 2 to about 4 weight percent Na₂O is preferred. When potassium is employed as the alkali metal, the treatment range of about 3 to about 6 weight percent K₂O is preferred. Typically the calcined alkali metal compound-treated alumina is prepared by contacting the alumina with a Group IA alkali metal compound dissolved in a suitable solvent such as water, alcohols, and esters. Water is preferred. Alkali metal compound-alumina contacting can be carried out in any suitable manner known in the art for solid-liquid contacting. For example, the techniques of incipient wetness or bulk solution can be employed. After sufficient contacting of the alumina and alkali metal compound containing solution, excess solution, if any, is removed by filtration, or decantation. Then the treated alumina is heated to a temperature from about 200°C to about 400°C. Heating is maintained for about 1-24 hours, preferably 5-10 hours under a gas flow of about 100-1000 GHSV (gaseous hourly space velocity). Suitable gases include N₂, air, natural gas stream, argon, and helium. Caution should be used with carbonaceous streams such as a natural gas stream to maintain the calcination temperature below about 300°C to minimize formation of carbon deposits on the catalyst. When an oxygen containing gas is employed during catalyst preparation, it is desirable to purge the finished catalyst with an inert gas such as N₂, Ar, He, to ensure that oxygen is not introduced into the hydrocarbon feed stream. Although pressure is not critical, it is preferred to maintain the pressure during catalyst calcination near atmospheric or below to aid removal of gaseous species generated during the heating process. Alkali metal compounds suitable for use in the present invention are soluble in the solvents disclosed previously, and are convertible under calcination conditions to the alkali metal oxide form, M₂O. Examples of suitable compounds include the hydroxide, nitrate, and acetate forms of the alkali metals. Hydroxides of lithium, sodium, and potassium are preferred because of their availability and cost. The rate at which the olefin stream is fed to the adsorbent bed is not critical but will vary with reactor size. Broadly, the rate of olefin introduction will be about 1-15 WHSV (weight hourly space velocity), preferably about 5-8 WHSV. For a gaseous feed such as ethylene, the WHSV will vary as a function of the pressure employed. In any event, it should be at a rate sufficient to effect efficient contact between the feed and the treated alumina. This invention is well suited for continuous reaction in which the olefin feed is continuously passed over a bed of calcined alkali metal compound-treated alumina at the desired reaction conditions. Generally, the process of the present invention is carried out at a temperature of from about 0°C to about 100°C. Presently preferred is a temperature in the range of from about 25°C to about 50°C. The pressure under which this invention is practiced will be from about atmospheric to about 1500 psig. Preferably, the pressure will be from about 400 to about 1000 psig (2750 to about 6900 kPa) with ethylene; atmospheric to about 130 psig (900 kPa) with propylene, and atmospheric to about 30 psig (206 kPa) for a butene stream. In light of the effectiveness of the present invention, olefin streams containing as little as 1 ppm of an inhibitor such as CO₂ can be processed. The calcined alkali metal compound-treated alumina may readily be regenerated by heating it in the presence of a gas stream such as N₂, He, Ar, air, or a natural gas stream. As described above, it is desirable to purge the regenerated catalyst bed with an inert gas such as N₂, He, or Ar prior to returning the catalyst to the process when an oxygen containing stream is used for catalyst regeneration. A temperature of from about 150°C to about 700°C, preferably about 200°C to about 400°C is employed until no further CO₂ and water vapor removal from the catalyst is achieved. Typically, regeneration takes about 1 to 24 hours, preferably 5-10 hours. For typical plant scale operation, the inventive catalyst could be deployed in three packed beds such that at any given time one bed would be undergoing regeneration, and the other two beds in series would be contacting the olefin containing feed stream. As the first bed to contact the olefin containing feed stream becomes saturated with CO₂ (as evidenced by CO₂ in the effluent from the first bed), the backup catalyst bed would become the primary bed for contacting the olefin containing feed stream; the freshly regenerated bed would be put on stream as the backup catalyst bed, and the saturated bed would be treated under suitable regeneration conditions. The following examples further illustrate the present invention. Examples Example I Alumina treatment Adsorbents from a variety of supplies were employed: The general procedure employed for treating alumina supports with an alkali metal compound was as follows. All alumina supports employed were crushed and sieved before use, 10-28 mesh (3-10 mesh per cm) particles being collected for use in the laboratory adsorption studies. The desired amount of hydroxide, such as sodium hydroxide, was dissolved in a volume of water just sufficient to wet the alumina thoroughly. The alumina adsorbent to be employed was then added to the alkali metal compound containing solution. The wet alumina support was then dried, such as by heating to above 100°C for about 20 minutes or longer. Dry, alkali metal hydroxide treated adsorbent was typically activated by heating to about 260°C for 5 hours in N₂ with flow maintained at about 40 l/hr. For example, alumina adsorbent treated with enough sodium hydroxide to give 2.0% Na₂O was prepared as follows. NaOH in the amount of 0.21 g was dissolved in 5 ml of water. To this solution, 8.0 g of Alcoa H-151 alumina was added with stirring. The wet alumina was heated in an evaporating dish to remove most of the excess water and then was activated at 260°C for 5 hrs. under a 40 l/hr. nitrogen flow. Example II In a series of tests, 50-60 mg of activated adsorbent was placed on the pan of a Perkin-Elmer TGS-2 thermogravimetric analyzer (TGA), heated to 260°C and held at 260°C while being swept with helium at 1.5 SCFM (42.5 ltr/min standard condition) until a constant weight was reached (indicating loss of moisture had ceased). The sample holder was then cooled to 30°C in the helium stream and the sample weight was recorded. A helium-CO₂ mixture containing 10 mole percent CO₂ was then substituted for the helium stream, and the gain in weight due to CO₂ adsorption was followed until a constant weight was reached, usually within 30 minutes or less. The weight gain was recorded and the weight percent CO₂ loading was calculated. In some cases the adsorbent was regenerated by heating to 260°C in helium and holding at 260°C until weight loss ceased. The adsorbent was then recooled and the CO₂ adsorption experiment repeated. Results of these tests are shown in Table I. The data show that CO₂ adsorption capacity increased sharply when Na₂O content of alumina was increased from sample to sample. The H-151 alumina, which originally contained about 2.7% Na₂O as an impurity, and the K-201 alumina, which originally contained about 0.3% Na₂O, were almost equally effective in CO₂ adsorption when promoted with additional Na₂O. The Li₂O and K₂O promoted aluminas were also effective in adsorbing CO₂. In these experiments, the molecular sieves were quite effective in adsorbing CO₂ from helium, but were inefficient in the presence of ethylene, as shown in Example III. Silica and silica-alumina were less efficient than alumina. Bulk NaOH removed CO₂ but could not be regenerated. Example III A series of tests, designed to closely simulate conditions used in treating ethylene monomer with alumina in a polyethylene plant were conducted as follows. A 2-3 g sample of adsorbent to be tested, previously activated at 260°C, was transferred into a 1/8''x2½'' (3 mmx64 mm) brass pipe closed at each end with a needle valve. Ethylene, containing 11-17 ppm CO₂ (by volume) was passed through the adsorbent maintained at 700 psig (4800 kPa) at a rate of approximately 7 g per hour per g of adsorbent. The effluent ethylene was periodically sampled and analyzed for CO₂ as follows: The sample was injected into a Carle Model 211M chromatograph equipped with a 3/16''x22' (5 mmx560 mm) Carbopack B column (80/100 mesh (34/41 mesh per cm)) operated at 50°C. A 60 ml/min He carrier gas stream carried the sample through the column and into a methanizer unit which converted the CO₂ to methane before being determined by a flame ionization detector. Sensitivity for CO₂ was less than 1 ppm. The ethylene flow and sampling were continued several days as necessary until CO₂ broke through the adsorbent and until the CO₂ concentration in the effluent approached that in the feed. The CO₂ concentration in the effluent was plotted against time, and the time to breakthrough and saturation determined. The total amount of CO₂ adsorbed was calculated and expressed as weight percent CO₂ loading on the adsorbent. Results are shown in Table II. From Table II is can be seen that sodium oxide promoted aluminas were far more effective than molecular sieves, which are frequently recommended by the adsorbent industry for CO₂ removal from gas streams. Li₂O on alumina was also effective. KOH pellets, normally considered preferable to NaOH when used in bulk for CO₂ removal, were ineffective under these conditions (dry). The optimum Na₂O concentration proved to be in the range of 2-4 weight percent of the alumina. Example IV In a large polyethylene plant, alumina beds, used primarily to remove traces of moisture from ethylene at 700 psig (4800 kPa) and a flow ratio of 5-10 kg ethylene per hour per kg of alumina, had to be regenerated about every 4 days to effect CO₂ removal when present at 5-6 ppm. The alumina was then removed and replaced with identical alumina to which had been added 3 weight percent Na₂O, added as a NaOH solution. At the same CO₂ concentration of 5-6 ppm in the ethylene, regeneration was now required only every 2 weeks. This example shows that a calcined alkali metal compound treated alumina is considerably more effective for CO₂ removal than untreated alumina.

Claims: A process for removing low concentrations of CO₂ from a gaseous olefin stream containing at least one C₂ to C₄ olefin characterized by passing said gaseous olefin stream containing CO₂ into contact with a regenerable, calcined adsorbent, said regenerable, calcined adsorbent having been made by (a) contacting alumina with an alkali metal compound in an amount of 1-6 weight percent on the adsorbent, calculated as alkali metal oxide, said alkali metal compound being selected from sodium, potassium and lithium compounds which are convertible to the metal oxide on calcination, (b) drying the resulting alkali metal compound-treated alumina, and (c) thereafter calcining the dried treated alumina at a temperature from 200°C to 400°C. The process of claim 1 characterized in that said olefin stream is ethylene and said alkali metal compound is selected from hydroxides, nitrates and acetates of sodium, potassium and lithium. The process of claim 2 characterized in that said alkali metal compound is selected from lithium hydroxide, sodium hydroxide and potassium hydroxide. The process of any of the preceding claims characterized in that said alkali metal oxide is lithium oxide which is present in an amount form 1 to 3 weight percent. The process of any of claims 1 to 3 characterized in that said alkali metal oxide is sodium oxide which is present in an amount from 2 to 4 weight percent. The process of any of claims 1 to 3 characterized in that said alkali metal oxide is potassium oxide which is present in an amount from 3 to 6 weight percent.

Inventors: HOGAN, JOHN PAUL, NEASE, CHARLES RUNG
Applicants: PHILLIPS PETROLEUM COMPANY
Application year: 1983
Main classification: B01D53
IPC codes: C07C7, B01J20, B01D53