BIOCOMPATIBLE, ANTITHROMBOGENIC MATERIALS SUITABLE FOR RECONSTRUCTIVE SURGERY

Abstract: Biocompatible, highly antithrombogenic material for reconstructive surgery, which is based on poly(L-lactic acid) and/or poly(dL-lactic acid) and segmented polyester urethanes or polyether urethanes.

Description: Title: Biocompatible, antithrombogenic materials suitable for reconstruc¬ tive surgery. The invention relates to a new biocompatible, highly anti¬ thrombogenic material, of adjustable porosity, compliance and biodegradability, based on polylactic acid and segmented polyurethanes, for reconstructive surgery, which can 'be built up in layers with different compositions and characteristics and can be modelled in various shapes by including reinforcement material. The versatility of the material according to the present invention gives it a unique adaptability to the biological tissue in which it is incorporated, so that the synthetic material is built up into a new functional entity in reconstructive surgery. Most synthetic materials used for reconstruction do not have the same mechanical properties as the "specific biological tissue and so do not match its specific function. It is known that the specific function of .tissue is the trigger of the constant rebuilding. of tissue in the growth during life. The variability of the elastic properties of the material according to the present invention renders it possible to match the mechanical properties of most of the biological tissue that has to be replaced in the body. As its porosity can be varied, the ingrowth and overgrowth of tissue for complete incorporation can be regulated to provide optimum conditions for a specific replacement. Its adjustable biodegradability makes it possible, if desired, to have the synthetic material completely replaced by biological tissue. Because of the possibility to produce -the material in layers of different compositions, it is also possible to have the characteris¬ tics of each layer match the function of the biological tissue needed to rebuild that layer. Because the material can be modelled by the shapes of mandrels by a dipping technique, every form can be produced to match the shape of an organ to be replaced, such as a tubular neo-artery for example. But also a more complex organ such as a trachea can be produced from OMPI this synthetic material, including a reinforcement material in the layers to maintain its shape during the alternating " positive and negative pressures occurring in the trachea and to prevent collapsing. The constructive reinforcement material can be made of a different material, for example porous hydroxy apatite, which could induce bone formation. Due to the biodegradability and high flexibility of the polylactide-polyurethane porous membranes, these materials can also be used to cover satisfactorily large experimental full-thickness skin wounds. Such membranes can effectively protect these wounds from infection and fluid loss for a long time. Thus these combinations give a wide range of new possibilities in reconstructive surgery, all based on the same principle that perfect matching of the mechanical properties of biological tissue and synthetic materials creates one functional unity between biological tissue and the synthetic material which allows complete incorporation and rebuilding to a new organ. This new composition has been tested in animal experiments, primarily with rabbits, as vascular and tracheal prostheses and artificial skin. In these experiments true biocompatibility and a high degree of a tithrombogenicity of the material was demonstrated. The experiments with the trachel prosthesis revealed that quick tissue ingrowth front the peritracheal tissue is induced if relatively large pores (100 y) were used on the outside. However, overgrowth of tissue on the lu inal side needed only a thin connective tissue layer to which epithelium became firmly attached and differentiated. This was achieved with relatively small pores on the inside (10 - 20 •_ ) . Between the layers of various pore sizes a reinforcement of a spiral bead may be embedded. This possibility of variation by means of different layers can also be used for the composition of an artificial skin where such functions as controlled evaporation, ingrowth of tissue, seeding of epithelial cells and resistance to outside micro-organism require layers with different characteristics. More specifically the invention relates to the provision of a material which comprises the following composition in wt. %: poly(L-lactic acid) and/or poly(dL-lactic acid) with a viscosity-average O PI 5 6 molecular weight in the range of 2 x 10 to 5 x 10 , from 5 to 95; and polyester urethane or polyether urethane, from 5 to-95. Polyester urethane of polyether urethane may be based on: polytetramethylene adipate, poly(ethyleneglycol adipate), poly(tetrame- thylene oxide), pol (tetramethylene glycol) or pol (diethyleneglycol adipate, p,p'-diphenylmethane diisocyanate, or toluene diisocyanate, or hexamethylene diisocyanate and 1,4 butanediol or ethylene dia ine. The segmented polyurethane .imparts the desired flexibility, strength and antithrombogenity to the material. The polylactic acid ensures the required modulus and porosity. By varying the proportion of polylactic acid, the proposed compliance and type or porosity can be controlled. As the esther, ether and urethane groups of polyurethane and the carboxylic group of polylactic acid exhibit poor hydrolytic stability, the material easily breaks down to be eliminated from the body after replacement of the graft by the body tissues. In order to increase the rate of material resorption in the body, it is recommended to use a material which contains at least 20 % by weight of polylactic acid and polyesther urethane, based on hexamethylene diisocyanate, polyethyleneglycol adipate and 1,4-butanediol. In order to improve antithrombogenic effect, the polyurethane based on polytetramethylene glycol and p,p'-diphenylmethanemay be used. For the preparation of arteries, arteriovenous shunts or cardiopulmonary bypass, the following compositions of the material, in % by weight, are recommended: a. poly(L-lactic acid) or poly(dL-lactic acid), 20; polyether urethane, 80. b. polylactic acid, 30; polyether urethane, 70. c. polylactic acid, 15; polyether urethane, 85. For the preparation of veins with a diameter in the range of 1,5 to 10 mm, the following composition, in % by weight, is recommended: a. polylactic acid, 80; polyester urethane, 20. b. polylactic acid, 70; polyester urethane, 30. c. polylactic acid, 60; polyester urethane, 40. For the preparation of tracheal prostheses with a diameter in the range of 7 - 25 mm, the following composition, in % by weight, is recommended: a. polylactic acid, 50; polyester or polyeter urethane, 50. b. polylactic acid, 40; polyester of polyeter urethane, 60. For the preparation of artificial skin having a size in the range of 50 to 500 mm by 50 to 500 mm -the following composition, in % by weighty is recommended: polylactic acid, 20 to 50; polyester urethane 50 to 80. The techniques applied for the preparation of tubular grafts and porous membranes may for example be as follows: A. Vascular grafts a) For higher concentrations of polylactic acid in the mixture: Polylactic acid is dissolved in chloroform at room temperature and 5 to 20 % by weight of sodium citrate in chloroform ethanol mixture is added to the solution. Polyurethane is dissolved in tetrahydrofuran so as to give a solution with a concentration in the range of 5 - 15 % by weight. The solutions of polylactic acid and polyurethane are mixed together right before the preparation of the tubes. The tubes are prepared on a stainless steel mandrel coated with polytetrafluoroethylene. For this purpose the mandrels are dipped into the polymer solution and dried at room temperature. Dipping and solvent evaporation procedure is repeated to provide the graft with a required wall thickness. The grafts are extracted with distilled water and ethanol for 5 to 10 hours to remove sodium citrate. Depending on the concentration of sodium citrate in the polymer solution and the proportion of polylactic acid, the size of the pores formed in the grafts is in the range of 5 to 200 ym. In addition the pore size may be adjusted by changing the polymer concentration in the solution from which the grafts are made. From a more concentrated solution grafts with smaller pores are obtained. When layers of polymer 3 REA OMPI ■ are deposited on the mandrel from solutions with different polymer concentrations composite grafts are formed having a gradually increasing pore size, suitable for certain types of implants. b) For higher concentrations of polyurethane in the mixture: Polylactic acid is dissolved in tetrahyd ofuran at 50 to 90°C. Poly¬ urethane is " dissolved separately in tetrahydrofuran. The two solutions are mixed together prior to the graft preparation. The concentration of polymer in the solution is in the range of 5-20 % by weight. Tubes are prepared on stainless steel mandrels coated with polytetrafluoroethylene (PTFE) , the mandrels being dipped into the polymer solution maintained at a temperature of 60 to 85°C and next into an ethanol distilled water mixture to precipitate the polymer. Depending on the concentration of polymer in the solution, a porous structure with different pore size is formed. The structure is composed of thin, elastic polyurethane fibers covered wi-th a thin layer of polylactic acid. As a general rule it is recommended that more concentrated polymer solutions are. used for the preparation of grafts having smaller pore sizes. These highly porous polylactic acid - polyurethane materials composed of randomly distributed holes and elastic fibers exhibit both radial and linear compliance. In all cases the pore-to-matrix ratio by volume can be adjusted from 0 to 90 percent. B. Tracheal Prostheses Solutions of polymers were prepared as described in Aa and Ab. After the deposition of 2 to 3 polymer layers on the mandrel, a reinforcing bead extruded from polyether urethane or polyamide urethane is wound tightly around the polymer-coated mandrel and another coating of polymer is applied. Due to partial dissolution and swelling of the surface of the reinforcing bead, an excellent, homogenous connection between the bead and the inner and outer walls of the prostheses is formed. C. Artificial skin Solutions of polymers are prepared as described in Aa and Ab. A glass cylinder with a rough, sand-blasted surface is dipped into the polymer solution maintained at a temperature of 60 to 85°C, and next into an ethanol distilled water mixture to precipitate the polymer. After washing with water and extraction with ethanol the porous sleeve is removed from the glass mould and cut along its longitudinal axis. On the upper side of the membrane a polyether urethane or Dow Corning Silastic Medical Adhesive Type A is spread. The diameter and the length of the glass mold may be in the range of 50 to 200 mm and 50 to 200 mm, respectively, depending on the size of the piece of artificial skin required for implantation. The proposed material in the form of vascular and tracheal grafts and porous membranes-artificio with various polylactic acid- pσlyurethane compositions and porosities, was tested in vivo for anticlotting properties and tissue ingrowth by implanting into chincilla rabbits and albino rats weighing 2 to 2.5 kg and 100 to 150 g, respectively. Histological analysis showed no clotting, connective tissue ingrowth, blood vessels ingrowth, etc.

Claims: -7- C L A I M S 1. Biocompatible, highly antithrombogenic material for reconstructive surgery, which is based on poly(L-lactic acid) and/or pol (dL-lactic acid) and segmented polyester urethanes or polyether urethanes. 2. Material according to claim 1 , characterized by the following composition in % by weight: poly(L-lactic acid), 5 to 95, or poly(dL-lacti'c acid), 5 to 95, and polyester urethane, 5 to 95, or polyether urethane, 5 to 95. 3. Material according to claims 1-2,,. characterized in that the polyester urethane is based on: poly(tetramethylene adipate), poly(ethyleneglycol adipate), p.p'- diphenylmethane diisocyanate, toluene diisocyanate, hexamethylene diisocyanate, and 1,4-butanediol or ethylene diamine; and the polyether urethane is based on: poly(tetramethylene oxide), poly(tetramethylene glycol), poly- (diethyleneglycol adipate), p,p'-diphenylmethane diisocyanate, toluene diisocyanate, hexamethylene diisocyanate, and 1,4-butanediol, or . ethylene diamine. 4. Biocompatible, highly antithrombogenic, biodegradable grafts based on polylactic acid and segmented polyurethanes, characterized in that compliance is adjusted by the ratio between the polylactic acid and the polyurethane in the mixture. 5. Biocompatible highly antithrombogenic, biodegradable grafts based on polylactic acid and segmented polyurethanes, characterized in that the pore size and the pore-to-matrix ratio by volume is adjusted from 0 to 90 percent. -$JR£ 6 OMPI ^ >fe?NATlO !

Inventors: GOGOLEWSKI SYLVESTER, PENNINGS ALBERT JOHAN, WILDEVUUR CHARLES ROELF HENDRI, GOGOLEWSKI, SYLVESTER, PENNINGS, ALBERT, JOHAN, WILDEVUUR, CHARLES, ROELF, HENDRIK
Applicants: UNIV GRONINGEN, RIJKSUNIVERSITEIT TE GRONINGEN
Application year: 1983
Main classification: A61L17
IPC codes: A61L26, A61L27, A61L33, A61M1, C08L67