ONE-PART MOISTURE CURED AMINOSILOXANES TO SET AND CONDITION HAIR

Abstract: A composition consisting essentially of (A) a polymer having at least one nitrogen-hydrogen bond; and (B) a rea­ dily hydrolyzable, anhydrous additive selected from the group consisting of titanates, zirconates, vanadates, germa­ nates, and mixtures thereof is disclosed. The uniqueness of this invention is that the polymer is crosslinked upon expo­ sure to moisture, such as water vapor but is reverted to noncrosslinked polymer after exposure to liquid water. The composition is particularly useful in a process for concur­ rently setting and conditioning hair.

Description: ONE-PART MOISTURE CURED AMINONOSILOXANES TO SET AND CONDITION HAIR This invention relates to a composition, stable in the absence of moisture, consisting essentially of (A) a polymer having at least one nitrogen-hydrogen bond; and (B) a readily hydrolyzable, anhydrous additive selected from the group consisting of titanates, zirconates, vanadates, germanates and mixtures thereof. The uniqueness of this invention is that the polymer crosslinks upon exposure to moisture such as water vapor and reverts to a noncrosslinked polymer after exposure to liquid water. Furthermore, the components can be s-tored together, in the absence of moisture, with no gelation. Polymers crosslinked upon exposure to moisture and reverting to a polymer after exposure to water can find use in hair care applications and rzversible rubber or elastomer applications. In hair care applications, the composition is applied to hair to set and condition. Upon washing, the composition reverts to a polymer and acts, again, as a hair conditioner. A composition described in the article entitled "New Types of Hair Setting Sprays having Semi-Permanent Properties" authored by Fulvio Sardo in Volume 87, American Cosmetics and Per-umery, pages 43-46 (December, 1972) , discloses the use of al.sylXitanates in c'bination with sllanol endblocked dimethylpolysiloxanes as a hair set.' This composition has limited use as a conditioner, and there is no mention of the co.mposition's capability of reversion to its polymer. Canadian Patent Number 1,112,181 discloses a hair set composition consisting essentially of aminoalkylalkoxysilanes and a titanate ester. This composition also has limited use as a hair conditioner with no mention of reversion capabilities. United States Patent Number 3,832,203 discloses a composition for treating leather comprising an organic solvent solution of (A) a titanate or zirconate, a copolymer of trimethylsiloxane and SiO2 units, a polysiloxane, , and (B) an aminoalkyl substituted silane oi siloxane. There is no mention of this composition being reversible and parts (A) and (B) cannot be stored together. United States Patent Number 4,388,437 discloses an organopolysiloxane composition, used for treating fibers, consisting essentially of an organopolmztsiloxane containing amine functionality, a surfactant, a tritanate, zirconate or germanate, an organic acid, and water The surfactant is needed to emulsify the siloxane. The acid is essential to adjust the pH to a desired range to control the rate of adsorption of the emulsion on the fiber. There is no mention of this composi.ion's reversion capabilities. An object of this invention is to provide a composition stable in the absence of moisture,crosslink- able upon exposure to moisture, and revertable to a polymer after exposure to water. A practical applicatior for this phenomenon provides a process for concuwrenclfr setting and conditioning hair comprising (I) imposing a desired configuration on the hair; (II) coating the hair with a composition comprising (.R) an organosiloxane polymer having an organic substituent containing a nitrogen-hydrogen bond; (B) a readily hydrolyzable, anhydrous compound selected from the group consisting of organic titanates, organic zirconates, organic vanadates, organic germanates, and mixtures thereof; and (C) an anhydrous organic solvent for (A) and (B); and (III) exposing the coated hair to air. So far as is known at this time, any polymer containing at least one nitrogen-hydrogen bond can be employed for the purposes of this invention. Examples of suitable polymers include polyamides, polyesters, polyethers, polyurethanes, polyalkylenes such as polypropylene, polyethylene and polystyrene, and siloxanes. If the polymer is present in solid form, such as polystyrene, the polymer will have to be dissolved in a compatibie solvent, such as toluene or xylene, so the additive can be mixed. Specific examples of suitable polymers include EMI3.1 EMI4.1 which are examples of polyamides, polyesters, polyethers, polyurethanes, and polyalkylenes, respectively. A siloxane polymer is preferred however. Further preference is given to the siloxane polymer having the units containing the nitrogen-hydrogen bonds selected from the group consisting of EMI4.2 and mixtures thereof wherein R is selected from the group consisting of monovalent hydrocarbon radicals, substituted monovalent hydrocarbon radicals, hydrogen, and a radical having the general formula -OX, wherein X is selected from the group consisting of hydrogen, monovalent hydrocarbon radicals, and substituted monostalent hydrocarbon radicals; R' is selected from the group consisting of hydrogen, monovalent hydrocarbon radicals, and substituted monovalent hydrocarbon radicals; wherein at least one R" per siloxy unit is hydrogen; and m and n have values of 1 to 4. It should be understood that the divalent radicals represented as CmH 2m and CnH2n can be either linear or branched hydrocarbon radicals. Specific examples of suitable divalent hydrocarbon radicals represented by CmH2m and Cn H 2n in the above formulae include -(CH2) 2' (CH2)3- -(CH2)-, -CH2CHCH3CH2- and EMI5.1 Specific examples of suitable monovalent hydrocarbon and substituted monovalent hydrocarbon radicals for R, R', and X are alkyl radicals such as the methyl, ethyl, propyl, butyl, amyl, cyclohexyl, decyl, dodecyl, and octadecyl radicals; alkenyl radicals such as the vinyl and allyl radicals; aryl radicals such as the phenyl and bi phenol radicals; alkaryl and araikyl radicals such as the tolyl and benzyl radicals; and the corresponding substituted hydrocarbon radicals such as the chloropropyl, 3,3, 3-trifluoropropyl, dichlorophenyl, cyanobutyl, and nitrophenyl radicals. A siloane polymer having the nitrogen-hydrogen bond units in the siloxy unit having the general formula EMI5.2 wherein R is a monovalent hydrocarbon radical, R' is hydrogen, m has a value of 3 or 4 and n has a value of 2 is preferred. R being an alkyl radical is further preferred with methyl being optimal. The composition of the other units in the siloxane polymer is not critical for the purpose of this invention . The other units of the siloxane polymer-can be selected from the group consisting of RSiO312, R2SiO, and R3SiOF units wherein R is as defined above. A siloxane polymer composed primarily of R2SiO units is preferred. Furthermore the endblocking and the structure of the polymer is not critical for the purpose of this invention as long as the siloxane polymer contains at least on nitrogen-hydrogen bond. Also, the siloxane polymer containing at least one nitrogen-hydrogen bond can be blended with other functional siloxanes or non-functional siloxanes, such as dimethylsiloxane or dimethylcyclosiloxane. However, a greater amount of amine or amide present leads to greater crosslinking. A siloxane polymer having the general formula EMI6.1 wherein R is as defined above, R is selected from the group consisting of monovalent hydrocarbon radicals, substituted monovalent hydrocarbon radicals and a radical having the general formula -OX wherein X is selected from the group consisting of hydrogen, monovalent hydrocarbon radicals, and substituted monovalent hydrocarbon radIcals, aeo has a value of 1 to 2000 with a hazing a value of 0 to 1999, and b having a value of 1 to 2000, is pr0rerred. Specific eanples or suitable monovalent hydrocarbon radicals and substituted monovalent hydrocarbon radicals for R" are as defined above for R, R' r ana and X. but, further pre=renc is given to R being a mvono-alent hydrocarbon radical, with R being an alkyl radical being further preferred, and methyl being optimal. The value of a+b having a value of 50 to 400 with a having a value of 49 to 399 and b having a value of 1 to 30 is also further preferred. A siloxane polymer selected from the group consisting of EMI7.1 is further preferred. So far as is known at this time, any readily hydrolyzable, anhydrous additive selected from the group consisting of titanates, zirconates, vanadates, germanates and mi:cturçes thereof can be employed for the purpose of this invention. Specific examples of suitable organic zirconates include octyleneglycolzirconate, tetra-2-ethylhexylzirconate, ttraisopropylzirconat, tertiarybutyltrimethylzirconate and mixtures thereof. Specific examples of suitable organic titanatcs include tetraethyltitanate, tetradecyltitanate, tetra-2-ethyl hexrltitanate, tetradodecyltitanate , tetraisopropyl- titanate, tetrabutyltitanate and mixtures thereof. Specific examples of suitable organic germanates include tetraethylgermanate, tetraisopropylgermanate, and tetradecylgermanate. Specific examples of suitable organic vanadates include vanadium triisopropo:'ide oxide and vanadium tri-n-pro?oxide oxide. Titanates are preferred, however. Organic titanates selected from the group consisting of alkyl titanates and titanium chelates are further preferred. Alkyl titanates have the general formula Ti(OD)4 wherein D is a monovalent hydrocarbon radical or a substituted monovalent hydrocarbon radical. Titanium chelates have the general formulae EMI8.1 wherein G is a monovalent hydrocarbon or substituted monovalent hydrocarbon radical, X' is selected from the group consisting of hydrogen, -OCH,CH3, -OH, monovalent hydrocarbon radicals, and substituted monovalent hydrocarbon radicals, Z and Y are divalent hydrocarbon or substituted divalent hydrocarbon radicals, and A and E are trivalent or substituted trivalent hydrocarbon radicals. Specific examples of suitable monovalent hydro carhon or substituted monovalent hydrocarbon radicals for D, X-1, and G are alkyl radicals such as the methyl, ethyl, propyl, butyl, amyl, cyclohexyl, decyl, dodecyl, and octadecyl radicals; alkenyl radicals such as the vinyl and allyl radicals; aryl radicals such as the phenyl and biphenyl radicals; alkaryl and aralkyl radicals such as the tolyl and benzyl radicals; and the corresponding substituted hydrocarbon radicals such as the chloropropyl, 3,3,3-rifluoropropyl, dichiorophenyl, cyanobutyl, and nitrophenyl radicals. The hydrocarbon and substituted hydrocarbon radicals for Y and Z are divalent radicals. Though the above examples of suitable hydrocarbon and substituted hydrocarbon radicals for D, X' and G are in monovalent form, similar divalent radicals are suitable for Y and Z. Specific examples of suitable divalent hydrocarbon radicals include -(CH2)3-, t (CH2)4-' -(CH2)6-, and -CH2CHCH3CH2-. The hydrocarbon and substituted hydrocarbon radicals for A and E are trivalent radicals. Though the above examples of suitable hydrocarbon and substituted hydrocarbon radicals for D, X', and G are in monovalent form, similar trivalent radicals are suitable for A and E. Specific examples of suitable trivalent hydrocarbon radicals include EMI9.1 Specific examples of suitable titanate having the general formula Ti(OD)4 include tetraisopropyltitanate, tetra-n-butyltitanate, and tetrakis(2-ethszl- heyl)titanate. Specific examples of suitable titanates having the general formula EMI9.2 include titanium acetylacetonate and titanium ethyl acetylacetonate. Titanates having the general formula Ti(OD)4 wherein D is an alkyl radical are preferred. Further preference is given to the titanate having the general formula Ti(OD)4 wherein D is selected from the group con sisting of isopropyl, 2-ethylhexyl, and n-butyl radicals. If desired the composition may also contain an anhydrous organic solvent. Examples of suitable solvents include aliphatic hydrocarbon and aliphatic halogenated hydrocarbon solvents such as hexane, heptane, and l,l,l-trichloroethane; and aromatic hydrocarbon solvents such as toluene and xylene. The solvent, l,l,l-tri- chloroethane, is preferred. Cpmpositions containing 0.97 to 90 percent by weight of the siloxane, 0.03 to 15 percent by weight of the metallic additive, and 1 to 99 percent by weight of a solvent are preferred. Compositions containing from 3 to 20 percent by weight of the siloxane, 0.1 to 3 percent by weight of the metallic additive and 77 to 96.9 percent by weight of a solvent are further preferred. If desired, the composition may also contain 0.01 to 50 percent by weight of an alkoxy silane having at least two alkoxy groups per silicon for added durability. Specific examples of suitable alkoxy silanes include methyl trimethoxysilane and a silane having the general formula NH2CH2CH2NHad2CH 2CH2Si(OCH3)3. In addition to the essential ingredients, the composition of this invention may include minor quantities of optional materials which are added for specific purposes. Such other ingredients include, but are not limited to,- medicaments such as anti-dandruff compounds, solvents, perfumes, sequestering agents, conditioning agents such as quaternary ammonium compounds, thickening agents, fillers, opacifiers, anti-static agents, and -antimicrobial preservatives, of which silicone is one. The methods of preparation of the components of the present invention are well known to those skilled in the art and detailed elsewhere in the literature. fleece, no time or space need be devoted here to a repetition of such information. As far as is known at this time, the order or method of mixing the components employed is not critical for the purpose of this invention. Suitable uses for this composition are in the field of hair care and anywhere there is need for a reversible rubber or elastomer. In the field of hair care, preference is given to applying the composition to preset and dried hair. The composition can be applied to the hair in any suitable form such as in thickened form by hand, in viscous form, by aerosol, or by pump spray. The composition after curing on the hair acts to hold any set in the hair even when exposed to atmospheric humidity, but when the hair is contacted directly with water such as by washing, the set is removed from the hair. Washing hair with a shampoo rather than just water is even more effective in removing the set from the hair. However, sufficient composition remains on the hair to act as a conditioner for the wet hair. Furthermore, if the hair is reset and dried, the composition again acts to hold the set in the hair although to a somewhat lesser extent than after the initial application of the composition. Although not intending to be bound by this theory, applicant believes that the cured composition when contacted directly with water such as by washing, reverts to the noncrosslinked, uncured polysiloxane which acts as the conditioner for the wet hair. When the hair is again dried hover, applicant believes that the composition that remains on the hair again cures to sufficient extent to improve the set holding properties of the hair. The term "hair" as used in the present invention includes treated and untreated human hair, animal hair, and any L of tiber that needs gloss, ease of combin, set hold, feel of fullness, protection from the elements such as sun, and reduced fly-away. Treated hair includes hair that is chemically changed and/or damaged by permanents and dyes. Setting hair means to curl, wave, control, or straighten hair. Now in order that those skilled in the art may better understand how the present invention can be practiced, the following examples are given by way o-f illustration and not by way of limitation. All parts and percents referred to herein are by weight unless otherwise specified. Example 1 The following formulations were prepared by weighing the components into a 4 oz. bottle, capping, and shaking: Formulation A EMI12.1 0.5 grams tetraisopropyltitanate Formulation B EMI12.2 7.5 grams tetraisopropyltitanate Formulation C EMI12.3 7.5 grams tetrakis ( 2-ethylhexyl)titanate (2-ethylhexyl) titanate Formulation D EMI12.4 7.5 grams tetraisopropyltitanate Formulation E 90 percent by weight EMI13.1 10 percent by weight tetraisopropyltitanate Formulation F 90 percent by weight EMI13.2 10 percent by weight tetra-n-butyltitanate Formulation G 90 percent by weight EMI13.3 10 percent by weight tetrakis(2-ethylhexyl)titanate Formulation H 90 percent by weight EMI13.4 10 percent by weight titanium acetylacetonate Formulation I 90 percent by weight EMI13.5 10 percent by weight titanium ethyl acetylacetonate Formulation J EMI14.1 0.5 grams tetraisopropyltitanate Formulation K EMI14.2 0.5 grams tetraoctylene glycol titanium chelate Formulation L EMI14.3 0.75 grams triethanolamine titanium chelate Formulation H 90 percent by weight EMI14.4 10 percent by weight tetraoctylene glycol titanium chelate Formulation ' 90 percent by weight EMI14.5 10 percent by weight triethanolamine titanium chelate After mixing, the fluids were clear and colorless and there were no apparent increases in viscosity. The caps were removed and a portion o the fluid poured into aluminum cups exposed to atmcspheric air. The results are as follows: Formulation Surface Skin Time, 230C Tack Free Time, 230C A 3 secs 12 secs B immediate immediate C 10 secs 2 min D 2 secs 10 secs E 1 sec 1 sec F 1 sec 20 sec G 5 min 21 min H 12 secs 4.5 min I 45 secs 4 min J* none ---- K* none L* none ---- M* none ---- * none *Included for purposes of comparison After 24 hours of exposure, formulations A, B, C, D, E, F, G, H, and I were cured to a thickness of about 1/16 inch while the materials kept in the capped bottles were still unchanged. Formulation J indicates the importance of the DI-H bond. The composition was exposed to air for 24 hours and showed no surface skin. Formulations, K, L, M, and N indicate the importance of the titanate being readily hydrolyzable. The tetraoctylene glycol titanium chelate and the triethanolamine titanium chelate used in the fornulations are not readily hydrolyzable. These formulations were also eposed to air for 24 hours and showed no evidence of forming a surface skin. The absence of surface skin in these formulations after 24 hours of exposure to the atmosphere is a simple test that can be employed to distinguish organic titanates, zirconates, germanates, and vanadates that are not readily hydrolyzable. Formulation D was shelf-aged for 16 days and then the above process was repeated giving similar results.- A portion of its cured rubber, 1/16 inch thick, was also heat aged 3 days at 1000C with no apparent adverse effects. Another portion of this cured rubber was immersed in tap water and became soft after 3 hours. After 3 days of'immersion, the cured rubber reverted to the polymer and a white precipitate. Example 2 A formulation was evaluated for the ability of the present invention to hold a set to hair. The formulation consisted of 10 percent by weight of EMI16.1 1 percent by weight of tetraisopropyltivanate, and 89 percent by weight of l,l,l-trichloroethane. The components were mixed together and the formulation was then placed in an aerosol can with 50 cc of dichlorodifluoromethane propellant. The test consisted of spraying the formulation onto undyed, preset, and dried hair and then exposing the hair to a water mist. An untreated specimen, also undid, preset, and dried, was also exposed to the water mist. The silicone treated hair held its set while thecontrol completely lost its set after 24 hours exposure to atmospheric air. Example 3 The following formulations were prepared b weighing the components into a 1 ounce bottle, capping and shaking. The siloxane employed in the formulations had the general formula of EMI17.1 Nine grams of the siloxane and 1 gram of the additive were employed. Vanadium triisopropoxide oxide, zirconium-npropoxide, and germanium butoxide were the additives employed in Formulations A, B, and C, respectively. After mixing, the formulations were clear with no apparent increase in viscosity. The caps were then removed and a portion poured into aluminum cups exposed to atmospheric moisture. The results are as follows: Surface Skin Time, Tack Free Time, Formulation 23"C 230C A 2 seconds 5 seconds B 15 seconds 85 seconds C 3 seconds 20 seconds After 24 hours of exposure, formulations A, B, and C were cured to a thickness of about 1/16 inch while the material kept in the capped bottles was still in an unchanged, fluid state.

Claims: Claims: I. A composition, stable in the absence of moisture, consisting essentially of (A) a polymer having at least one nitrogen-hydrogen bon-d and (B) a readily hydrolyzable, anhydrous additive selected from the group consisting of titanates, zirconates, vanadates, germanates and mixtures thereof. 2. A composition as defined in Claim 1 wherein (A) the polymer is a siloxane wherein the units containing the nitrogen-hydrogen bond in (A) the siloxane polymer are selected from the group consisting of EMI18.1 and mixtures thereof wherein R is selected from the group consisting of monovalent hydrocarbon radicals, substituted monovalent hydrocarbon radicals, hydrogen, and a radical having the general formula -OX wherein X is selected from the group consisting of hydrogen, monovalent hydrocarbon radicals and substituted monovalent hydrdcarbon radicals; R' is selected from the group consisting of hydrogen, monovalent hydrocarbon radicals, and substituted monovalent hydrocarbon radicals; wherein at least one R' per siloxy unit is hydrogen; and m and n have values of 1 to 4 and (B) the additive is a titanate. 3. A composition as defined in Claim 2 wherein the units containing the nitrogen-hydrogen bond in (A) the siloxane polymer are EMI19.1 wherein R is a monovalent hydrocarbon radical, R' is hydrogen, m has a value of 3 or 4, and n has a value of 2; and (B) the titanate is an alkyl titanate having the general formula Ti(OD) 4 wherein D is an alkyl radical. 4. A composition as defined in Claim 3 wherein (A) the siloxane polymer has the general formula EMI19.2 wherein R is an alkyl radical; R Is selected from the group consisting cf monovalent hydrocarbon radicals, subs.itu-ed monovalent hydrocarbon radicals, and a radical having the general formula -OX wherein X is selected from the group consisting of hydrogen, monovalent hydrocarbon radicals, and substituted monovalent hydrocarbon radicals; and a+b has a value of 1 to 2000 with a having a value of 0 to 1999 and b having a value of 1 to 2000. 5. A composition as defined in Claim 4 wherein (A) the siloxane polymer is selected from the group consisting of EMI20.1 in lB) D is selected from the group consisting of isopropyl, 2-ethylhexyl, and n-butyl radicals. 6. A process for concurrently setting and conditioning hair comprising: (I) imposing a desired configuration on the hair; (II) coating the hair with a composition according to claim 1; and (Ill) exposing the coated hair to air.

Inventors: HOMAN, GARY REX, SWIHART, TERENCE JOHN
Applicants: DOW CORNING CORPORATION
Application year: 1983
Main classification: C08L83
IPC codes: C08K5, A61K8, A61Q5