BIOELECTRODE

Abstract: An improved biomedical electrode is disclosed which is especially useful for delivering current to the body. The electrode comprises a non-metallic electrically-conductive film which is a barrier to the migration of metallic ions located between a thin, conformable, electrically-conductive metal layer and the skin. An extensible backing overlying the metal layer and means for conducting the metal layer to an electromedical device are also essential features of the invention. The electrode is preferably disposable and further comprises an electrically-conductive pressure-sensitive adhesive as an interfacing material between the non-metallic film and the skin.

Description: BIOELECTRODE This invention relates to biomedical electrodes, and in particular, to biomedical electrodes used to deliver current to the body as in, for example, transcutaneous electrical nerve stimulation (TENS), functional electrical stimulation (F.E.S.) and iontophoretic drug delivery. Two primary concerns which must be addressed in the design of bioelectrodes for delivering current to the body are patient comfort and safety. To maximize comfort and safety, stimulating bioelectrodes, e.g., TENS electrodes, are generally constructed of flexible materials such as conductive mesh (U.S. Patent No. 4,243,051), metal foil (U.S. Patent No. 4,125,110), or silicone rubber (published United Kingdom application No. 2,045,088) which conform to the contours of the body over which they are adhered. If good contact is maintained between the electrode and the skin, and if the electrode delivers uniform current densities over its entire surface, the potential for development of "hot spots", and their attendant discomfort and possible burning, is minimized. While the prior art has been moderately successful in providing biomedical electrodes which exhibit good conformability to skin, the aforementioned types of electrodes all suffer from certain disadvantages. Biomedical electrodes such as those described in published United Kingdom application No. 2,045,088, made of conductive silicone rubber, are rather bulky and heavy, comparatively speaking, and less supple than electrodes formed from thinner materials such as conductive mesh or foil. They also tend to be more expensive and more power consuming than the other types of electrodes. While their disadvantages are not of great significance in the case of relatively small TENS electrodes used to treat chronic pain such as lower back pain, they are magnified in the case of larger electrodes such as those used in the management of post-operative pain. In this application, one electrode, often as long as ten inches, is placed on each side of the incision, and therefore thin, supple electrodes are particularly desirable. Electrodes formed of a conductive mesh such as the aluminum-coated fabric described in U.S. Patent No. 4,243,051 or a metal foil can be made thin, light-weight and supple, particularly when a relatively thin layer of a conductive adhesive is used as the interfacing material between the electrode and the skin to reduce impedence and adhere the electrode to the skin. However, a major problem has been discovered recently in connection with metal electrodes used to deliver current to the body. This problem involves the migration of metal ions from the electrode to the skin under the influence of direct current produced by many stimulator units now in use. Stimulators used in TENS therapy are designed to provide a carefully patterned stream of electrical impulses with no D.C. component. It has been discovered, however, that certain stimulators currently in use may produce a significant D.C. component which is capable of electrolyzing metal in the electrode. In electrodes with an aqueous pathway between the electrode and the skin, such as that provided by a typical electrolyte gel or a conductive adhesive dependent on moisture or humidity, deplating of the electrode occurs. A vapor-coated silver layer, for example, can be deplated by one of these stimulators in a few hours. Since the electrodes are often designed to remain on the body for several days, the silver is deposited in the skin, and the effective contact area for current conduction is localized under the point of termination of the lead wire producing a "hot spot" which can result in extreme discomfort and even "burning." The bioelectrode of the present invention effectively prevents the aforementioned problem of deplating and migration of metallic ions while maintaining all of the desirable features of metal electrodes such as thinness, light-weight, suppleness, low cost, etc. Brief Summary of the Invention According to the present invention there is provided a biomedical electrode comprising: (1) a flexible, electrically-conductive nonmetallic film which is a barrier to the migration of metallic ions and has a top surface and a bottom surface; (2) a layer of electricallyconductive metal overlying and in electrical contact with a substantial portion of the top surface of the electricallyconductive film; (3) an extensible electrically insulating backing overlying and adhered to a substantial portion of the metal layer on the side opposite to that contacting the electrically-conductive film; and (4) means for electrically connecting the metal film to an electromedical device. Preferably, the bioelectrode of the invention is disposable and further comprises a conformable, electrically-conductive interfacing material on the bottom surface of the electrically-conductive film. In the preferred embodiment, the interfacing material is a layer of a conductive adhesive which is sufficiently tacky to adhere the entire electrode to the skin. In the preferred embodiment, a protective release liner is adhered to the conductive adhesive to protect the adhesive prior to use. The bioelectrode of the invention is designed to provide uniform current densities over the entire surface in contact with the skin. It is relatively thin, supple, light-weight and not affected by direct current which may be generated by stimulators currently in use. The term "flexible" and "conformable" are used interchangeably herein to refer to the ability to conform to the contours of the body over which the bioelectrode is placed to provide a high surface area of contact between the skin and the electrode. The term "extensible" as used herein in connec tion with the backing portion of the bioelectrode refers to the ability of the backing to stretch when mechanical force is applied to it so as not to exert sheer forces on the metal layer to which it is adhered and thereby cause the metal layer to delaminate from and lose electrical contact with the underlying electrically-conductive film. Description of the Drawings Further understanding of the invention will be facilitated by reference to the following drawings wherein like reference numerals refer to like parts, and FIGURE 1 is a perspective view of the bioelectrode of the invention, somewhat out of proportion, having parts thereof peeled back and other parts broken; FIGURE 2 is a greatly enlarged sectional view of the electrode of Figure 1, showing the attachment of the lead wire to the electrode; and FIGURE 3 is an alternative embodiment of the bioelectrode of the invention. Detailed Description Referring now to FIGURES 1 and 2, biomedical electrode 10 is primarily designed as a post-operative TENS electrode. It is elongated and generally rectangular in shape. Electrode 10 comprises a flexible, non-metallic electrically-conductive film 12. Film 12 conducts current electronically, not ionically, and is, therefore, a barrier to the migration of metallic ions. Film 12 is preferably formed from a thermoplastic resin which has been made electrically conductive by the inclusion of conductive carbon particles such as carbon black. A layer of conductive metal 14 overlies the top surface of film 12 and is in good electrical contact therewith over substantially all of its surface area on the side contacting film 12. Preferably, metal layer 14 is a thin layer of silver vapor deposited onto the top surface of film 12. An extensible, electrically-insulating backing 16 overlies the side of metal layer 14 opposite to that contacting film 12, and is adhered to metal layer 14 by means of adhesive 18. Backing 16 adds to the mechanical integrity of the electrode and protects the fragile metal layer 14 from damage. Backing 16 must be extensible enough to stretch in response to the mechanical forces to which the electrode is exposed during application to the body and subsequent use without stressing the metal layer 14 and causing it to delaminate from and lose contact with film 12. Backing 16 must also be conformable to body contours so as not to detract from the overall suppleness of the electrode. The particularly preferred material for backing 16 is PVC foam tape, e.g., Microform" Surgical Tape sold by the 3M Company, St. Paul, Minnesota U.S.A. This tape is one of the most conformable and extensible tapes available. Also suitable is an adhesive film sold under the trademark tegadermt by the 3M Company for use as a wound dressing. This is polyurethane film coated on one side with a pressure sensitive adhesive. This material is thinner than Microform" Surgical Tape and may be preferred for electrodes such as that illustrated in FIGURE 3 which is slightly thicker than the electrode of FIGURES 1 and 2 to minimize overall thickness. Conformable, electrically conductive interfacing material 20 is coated onto the bottom surface of film 12. Interfacing material 20 can be any gel, paste or conductive adhesive conventionally used in biomedical electrodes to reduce impedence and enhance the electrical connection between the electrode and the skin. For ease in manufacture and handling, so called "dry" conductive adhesives such as those described in U.S. Patent No. 4,066,078; U.S. Patent No. 4,352,359; and International Appliation No. PCT/US80/01543 are preferred. Especially preferred is the class of adhesive described in the aforementioned U.S Patent No. 4,352,359 such as a copolymer of n-butyl acrylate and acrylic acid (75'.25) neutralized with methyl diethanolamine. These adhesives are sufficiently tacky to hold the electrode securely on the skin, and because of their low water content, do not dry out during use. Interfacing material 20 may vary greatly in thickness between about 2 and 70 mils depending on the type of interfacing material and the intended use of the electrode. In the embodiment illustrated in FIGURE 1, designed for use as a disposable post-operative TENS electrode, interfacing material 12 is preferably about 4 mils thick. Interfacing material 20 is protected prior to use by a conventional release liner 22. Electrode 10 is connected to an electromedical device such as a stimulator by way of wire 24, illustrated in FIGURE 2. Wire 24 is encased in insulating sheath 26 and sandwiched between backing 18 and metal layer 14. A length approximately 3/4 inch long of wire 24 is exposed from the end of sheath 26 and in intimate electrical contact with metal layer 14. Metal layer 14 distributes the current evenly throughout its surface area where it is conducted via film 12 and interfacing material 20 to the skin underlying the electrode. The embodiment of FIGURE 3 is an alternative embodiment of the bioelectrode of the invention. The electrode 30, as illustrated is rectangular in shape, but any desired shape may be used. Electrode 30 is smaller in leng#th and width than the embodiment shown in FIGURE 1 and may be used for any type of application where electrical current is delivered to the body such as TENS, F.E.S. or, possibly, iontophoretic drug delivery. Most of the elements of the electrode are similar to those of the electrode of FIGURES 1 and 2, except the layer of interfacing material 20 is thicker (and may be drug containing gel or paste), the backing 16 is thinner, and the means for connection to the stimulator is different. Electrode 30 contains a body-conformable one-piece electrically-conductive connector 32 having a substantially flat lower surface 34 overlying and in electrical contact with a portion of metal layer 14. Backing 16 overlies the top surface 36 of connector 34 and the portion of metal layer 14 not covered by connector 34, and is adhered thereto by a thin layer of adhesive (not shown). Connector 34 has a passageway 38 extending through the central portion thereof with an opening on each lateral face of the electrode. Passageway 38 serves as a female receptacle for plug 40 which is connected to the lead wire 42 of an electromedical stimulator. Connector 34 distributes current to the underlying metal layer 14 and is preferably made of carbonimpregnated silicone rubber (e.g., Silicone Rubber Compound C-968, SWS Silicones Corporation, Adrian, Michigan 49221). Other suitable carbon impregnated polymeric materials include plasticized polyvinyl chloride, epichlorohydric rubber, polyurethane molding compound, polytetrafluoroethylene and a polymer of ethylene-propylene-diene (e.g., EPDM rubber). The interfacing material 20 of electrode 30 is slightly thicker than that shown in the embodiment of FIGURES 1 and 2, e.g., on the order of 10-70 mils (0.0254 0.1778 cm). If used for iontophoretic drug delivery, the drug may be incorporated into the interfacing layer and the interfacing layer tends to be thicker. The essence of the present invention lies in the unique combination of metal layer 14 with film 12 which serves as a barrier against the migration of metal ions from metal layer 14 to the skin. The preferred composition of film 12 is 71 percent ethylene vinyl acetate (Grade UE 632 "Ultrathene" from USI Chemicals) and 29 percent carbon black (X-C 72, Cabot Corporation). The ingredients are mixed, pelletized and extruded using conventional techniques to form a film, having a thickness in the general range of 2 to 4 mils (50 to 100 micrometers). The preferred thickness is about 3 mils (approximately 75 micrometers). Conductivity measurements on this film, using two probes [ 1/2 x 1 inch (1.27 x 2.54 cm) copper plates 1 clamped on opposite sides of the film two inches (approximately 5.1 cm) apart, indicate resistance of less than 0.7 ohm. Although ethylene vinyl acetate is the presently preferred thermoplastic resin for, use in forming film 12, a variety of other resins, such as PVC, polyethylene and polypropylene, can be used to achieve the requisite conformability and conductivity when mixed with electrically conductive carbon. Carbon black is the preferred conductive carbon, and it typically comprises between about 25 and 30 percent of the film. Below a concentration of about 25 percent, conductivity falls off, and minimal advantages are perceived by adding more than 30 percent. Metal layer 14 conducts the current evenly over the entire area of the electrode. Metal layer 14 is preferably vapor deposited on one surface of film 12. Silver is the present metal of choice, and a layer having a o thickness of about 400 A (about 300 mcg/sq.2) is preferred and easily applied using conventional techniques for vapor deposition of metals. Vapor coating is economical and provides better electrical contact with film 12 and better suppleness than is obtainable with metal foil or meshes. In addition to providing a barrier to the migration of metal ions from metal layer 14 to the skin, film 12 has the additional advantage that its electrical conductivity is relatively unaffected by flexing and bending. A woven material, on the other hand, is difficult to coat evenly with metal, and, when flexed, movement of fibers relative to each other interferes with electrical conductivity. To use the biomedical electrode of the present invention as illustrated in FIGURES 1-3, the release liner 22 is removed, and the electrode is placed on the desired surface of the skin. Prior to placing the electrode on the skin, the lower surface of interfacing material 20 or the skin may be wetted with water to optimize adherence and conductivity of the skin adhesive interphase. The electrode is then connected to an electromedical device. Electrodes of the present invention have been found to have a very low impedence, on the order of 30 ohms at 60-80 Hz. To determine direct current stability, electrodes according to the present invention were placed on an agar surface (agar 1.5%, KC1 8.0%, water 90.5%). Direct current (1 microamp) was passed through the electrodes, used as both the anode and cathode, for 24 hours. No physical change was observed in any of the electrodes. No deplating of the metal layer was detected, and the electrodes were able to function normally after the test.

Claims: CLAIMS 1. A biomedical electrode comprising an electrically-conductive metallic layer and means for electrically connecting said metallic layer to an electromedical device characterized in that said electrode further comprises a flexible, electrically-conductive, non-metallic film which is a barrier to the migration of metallic ions having a top surface and a bottom surface; and said electrically-conductive metallic layer overlies and is in electrical contact with a substantial portion of said top surface of said film, and further characterized in that an extensible, electrically insulating backing overlies and is adhered to a substantial portion of said metallic layer on the side opposite to the side contacting said film. 2. The biomedical electrode of claim 1 further characterized by a coating of a conformable, electricallyconductive interfacing material on said bottom surface of said film. 3. The biomedical electrode of claim 2 further characterized in that said interfacing material is an electrically-conductive pressure sensitive adhesive. 4. The biomedical electrode of claim 3 further characterized by a release liner adhered to the exposed surface of said pressure sensitive adhesive. 5. The biomedical electrode of claim I Lurtller characterized in that said film comprises a thermoplastic resin containing an effective amount of electricallyconductive carbon to render said resin electricallyconductive. 6. The biomedical electrode of claim 5 further characterized in that said resin is ethylene vinyl acetate. 7. The biomedical electrode of claim 5 further characterized in that said electrically-conductive carbon is carbon black. 8. The biomedical electrode of claim 7 further characterized in that said carbon black comprises between about 25 and 30 percent of said film. 9. The biomedical electrode of claim further characterized in that said metallic layer comprises silver. 10. The biomedical electrode of claim 9 further characterized in that said silver is vapor-deposited on said top surface of said film. 11. The biomedical electrode of claim 1 further characterized in that said backing comprises a polyvinyl chloride foam tape. 12. The biomedical electrode of claim 1 further characterized in that said backing comprises a thermoplastic polyurethane film having a layer of pressure sensitive adhesive on the side thereof contacting said metallic layer. 13. The biomedical electrode of claim 1 further characterized in that said means for electrically connecting said metal layer to an electromedical device is an electrically conductive wire sandwiched between said metal layer and said backing in electrical contact with said metal layer. 14. The biomedical electrode of claim 1 further characerized in that said means for electrically connecting said metal layer to an electromedical device is a one-piece electrically- conductive connector sandwiched between said metal layer and said backing with at least one end thereof exposed, said connector having a substantially flat lower surface overlying a portion of said metal layer and in electrical contact therewith and a female receptacle in said exposed end for receiving an electrical plug for attachment to said electromedical device. 15. The biomedical electrode of claim 3 further characterized in that said electrically-conductive pressure-sensitive adhesive is a copolymer of n-butyl acrylate and acrylic acid neutralized with methyl diethanolamine. 16. The biomedical electrode of claim 3 further characterized by a drug contained in said interfacing material capable of iontophoretic delivery to the skin.

Inventors: ROBERTS, CHARLES W. MINNESOTA MINING AND MANUFACT.
Applicants: MINNESOTA MINING AND MANUFACTURING COMPANY
Application year: 1983
Main classification: A61N1
IPC codes: A61N1