MANUFACTURE OF ASSEMBLAGES OF FASTENERS

Abstract: Assemblages of fasteners (10) are manufactured by molding connected individual fasteners (20) and simultaneously stretching the connected fasteners while subjecting them to controlled heating using an insulated probe (34). The cross bars (20c) of the fasteners are thus protected from adverse heating effects.

Description: MANUFACTUREOFASSEMBLAGESOFFASTENERS BACKGROUND OF THE INVENTION This invention relates to assemblages of fasten¬ ers and their manufacture, and more particularly but not exclusively, to assemblages of fasteners which are dispensable by machine for the tagging and attachment of articles. Many different types of fasteners have been used for the tagging and attachment of articles. One con¬ struction is described in United States Serial No. 153,154, now abandoned. These fasteners wereproduced by molding an assemblage of individual fasteners, each with a thin filament interconnecting a cross bar with a head, and joined together by necks to a common runner bar. These fasteners can be dispensed using a gun as described in United States Patent Specification No. 3,103,666. After the development of the fastener described in Specification No. 153,154, it was discovered that these fasteners could be significantly and unexpect- edly improved by being stretched as described in Patent Specification No. 3,444,597, which also de¬ scribes the stretching of the individual fasteners of an assemblage simultaneously. Various methods for producing stretched fasteners are described in Patent Specification Nos. 3,380,122, 3,444,597, and 3,457,598. As described in those specifications, the assemblages of fasteners are molded with slight tapers in a por¬ tion of their filaments in order to ensure that the stretching will extend substantially to the junctions of the filaments with the cross bars. While the manufacturing methods described in these specifica¬ tions provide suitable fasteners, they require an appreciable time interval, e.g. cycle time, between molding and the completion of stretching. In addi¬ tion, while these methods are eminently suitable for easily stretchable crystalline materials, such as nylon, they are less suitable for relatively rigid crystalline materials such as polypropylene. aAnother difficulty encountered with materials such as polypropylene is that the cross bars tend to be pulled forward at their junctions with fila- ments. This distortion of the cross bar can make the fasteners inoperative and produce jamming in dispensing devices. SUMMARY OF THE INVENTION According to the present invention, an assemblage of fasteners is manufactured by. (a) molding the assemblage as a set of connected individual fasteners, that individu¬ ally include an end member joined by a filament, and (b) stretching the individual fasteners simultaneously while subjecting them to controlled heating using a probe at a prescribed position along the length of at least one filament. The end members of the fastener desirably are protected from adverse heating effects, and the controlled heating is directed to the fila- ments simultaneously. Undesired heating effects at the cross bar of individual fasteners are prevented by selective shielding or masking. It is also desirable to cool at least one of the stretching elements and to have the jaw opening for the associated element of a lesser magnitude than the minimum diameter of the filaments being stretched. Details of certain preferred features are as follows: The assemblage may be fed into a stretching machine with jaws that grip the fasteners at oppo¬ site ends. The jaws are then separated to take up slack in the filaments which are simultaneously subjected to a controlled heating effect with the associated cross bars being shielded or masked. The jaws are then separated for stretching, followed by relaxation to permit removal of the stretched assemblage from the stretching machine. The probe is heated and in contact with at least one of the filaments. It is desirable for the probe to be in¬ sulated as well. The mask or shield is advantageously a part of a stretching jaw, but it may be a separate member. The fasteners can be produced in a mold with separable parts, with the filaments being subject¬ ed to controlled heating as the mold parts are separated. The controlled heating is desirably achieved using an infra-red radiator, in conjunction with a heated probe. The heating effect is principally directed to the junctions of the filaments with their end members. Each of the filaments desirably has a taper over a portion of its length in order to ensure that the stretching extends to the junctions with the cross bars. However, the filaments may be of other configuration, including a generally cylindri¬ cal configuration. The " fasteners are preferably of a crystalline material whose molecules are reoriented by stretch¬ ing and are desirably selected from nylon, poly¬ ethylene, polypropylene and polyester and acetal resins. DESCRIPTION OF THE DRAWINGS The invention may be carried into practice in various ways but a number of examples will now be described with reference to the accompanying drawings, in which: Figure 1A is a perspective view of an assem¬ blage of fasteners; Figure IB is an enlargement of a portion of an individual fastener from the assemblage of Figure 1A; Figure 2A is a plan view of stretching appara¬ tus used to manufacture the assemblage shown in Figures 1A and IB; Figure 2B is a plan view of an alternative stretching apparatus; Figure 3 is a perspective view of heating members used in the machines shown in Figures 2A and 2B; Figures 4A and 4B are views illustrating an alternative method of manufacture; Figure 5 is a perspective view of a further assemblage of fasteners; and Figures 6A to 6C are perspective views of alternative assemblages prior to stretching. DETAILED DESCRIPTION Turning now to the drawings, Figure 1A shows an assemblage 10 of individual fasteners 20-1 to 20-n of which each individual fastener, for ex- ample the first fastener 20-1, includes a cross bar 20c which is joined to a head 20h by a fila¬ ment 20f. The fasteners 20-1 to 20-n are col¬ lectively joined to a runner bar 11 by individual necks 20n which extend from the cross bars 20c. Although the filaments 20f_ of the fasteners 20-1 to 20-n appear to be cylindrical over the major portion of their length beginning at the cross bars 2θ£, they typically display a region of slight taper. This is illustrated in the enlarged fragment of an individual fastener 20-1 shown in Figure IB. In the illustrative fastener 20-1 of Figure IB there is a minimum diameter of approxi¬ mately 5.59 mm at position A, located approximately 16.76 mm from the junction 20j_ of the fastener 20-1 with the cross bar 20c_. The diameter of the fila¬ ment 20 ' f gradually increases to 6.10 ram at position B, then to 6.35 mm at position C and further to 6.60 mm at position D. The fastener assembly shown in Figures 1A and IB is stretched in a machine 30 of the construction shown in Figure 2A. The machine 30 includes an outer jaw 31, an inner jaw 32, and a heat mask or shield 33. The outer jaw has an interior region 31r_ for receiving one end of the product to be stretched and the inner jaw 32 has a similar interior region 32r for the other end of the product. In the case of an assemblage of unstretched fasteners, of which only the first member 20-1 is visible in Figure 2B, the head of the fastener 20h is within the interior region 31r of the outer jaw 30 and the runner bar 11 is within the interior region 32r of the inner jaw 32. The outer jaw 31 has a channel 3l£ to accom¬ modate the portion of the filament 20f^_ near the head 20h' . A similar channel 3l£ is included in the inner j w 32. In addition, the inner jaw 32 includes a heated probe 34. The heating effect is provided by an inner heating coil 35 which is energized over a cable 36 as desired. It is particularly desirable to operate the probe 34 shortly before and during the stretching operation. In some cases the probe 34 is heated only during stretching. In other cases heating is applied after stretching has terminated. In still other cases the probe is heated continuously. In the particular embodiment of Figure 2A, the inner jaw 32 is stationary and the outer jaw 31 is separable away from the inner jaw by, for example, an hydraulic mechanism. Only one-half of the machine 30 is illustrated in Figure 2A and a similar half is used for the con¬ current stretching of another set of blanks which is joined to the set within the jaws 31 and 32 by a connector 22 constituted by a gating sprue. After the assemblages of fasteners, as joined by the degatable connector or sprue 22, are fed to the machine 30 with, for example, the illustrated fastener 20-1' positioned between the jaws 31 and 32, the outer jaws, for example the jaw 31, are operated to take up slack in the fastener and move from an initial position 31a to an intermediate position 31b. In the general case stretching could proceed by moving the outer jaw 31 to the position 31f. To accelerate the stretching and to facilitate the stretching of stretch resistant crystallized plastics materials such as polypropylene, a con¬ trolled heat source 40 is used. _ OMPI In the case of Figure 2A, an alternative heat mask or shield 33' is employed by attaching an ex¬ tension to the inner jaw 32. The controlled heat source 40 includes a holder 41 and a quartz infra-red lamp 42 which is described in detail below. The heat from the lamp 42 is initially applied when the outer jaw is in its position 31a. The heat effect continues to be applied as the jaw 31 moves to its final position 31f_ which results in the production of the fastener shown in Figure 1A. After stretching is completed, the jaw 31 is relaxed to permit removal of the stretched fasteners from the machine 30. The heat shield 33, which may be affixed to the jaw 32, pro- tects the cross bar 20"£ from adverse heating effects, and, in particular, limits the extent to which the cross bar may become adversely affected during the stretching operation. The channel 32£ of fhe inner jaw 32 shields the neck 20'n of the fasteners so that the gripping action of the jaw 32 is against the runner bar 11' . The shielding of the neck 20'n prevents it from being inadvertently stretched, while the gripping of the runner bar 11' prevents inadvertent damage to the cross bar 20'£. In the modified apparatus shown in Figure 2B, which is otherwise the same as that shown in Figure 1, the lamp 42 is positioned in an adjustable end mount 43 in order to direct the heating to the desired portion of the filament 20f_. The end mount 43 is adjustable in any standard way to control the direction of the infra-red radia¬ tion from the lamp 42. A perspective view of a portion of the lamp 42 shown in Figure 2A (or of the lamp 42 shown in Figure 2B) is shown in Figure 3. A quartz tube 42 OMPI encloses a resistor coil 42£ which has terminal tabs 42l:-l and 42t_-2. Above the coil 42£ there is an internal reflector 42r which orthogonally directs the infra-red radiation. The lamp 42 may be then known as a Unit Tube Infra-Red Heater available from Hugo N. Cahnman, Associates, Inc., 125-10 Queens Boulevard, Kew Gardens, New York 11415, United States of America. It has an infra¬ red emission range of 2 to 5 microns and provides a temperature between 315 and llOOC. The temperature H of the heat source 42 and time T during which the fasteners are exposed to the heating effect is desirably optimised so that the product of the heating effect and the temperature is below the value which would cause melting of the fasteners. The internal reflector 42r of the heat source 42 can cause about 85 percent of the radiated energy to be directed at the product. In addition a heated probe 34' is mounted at the end of the shield 33'. The probe 33' is ener¬ gized over a cable 36' as in the case of Figure 2A. In the case of Figure 2B, it is desirable for the probe 33' to be in actual physical contact with the filament 20-1. The particular probe 33' of Figure 2B is triangular in cross section and makes a point contact with the filament 20-1. An alternative form of fastener is shown in the jaw 35 in Figure 4A. For the individual fastener 24-1 of Figure 4A the filament 24F is substantially cylindrical throughout the major portion of its length. Because of the heat effect H, stretching takes place as illustrated in Figure 4B. Since the filament is of cylindrical cross section its stretched counterpart is also substantially cylindrical. How¬ ever, there is a slight region of taper t: near the head 24h. The cylindrical filament 24f_, although more difficult to control, does not require as great a mold expense and avoids the possibility of having a region of excessive thickness which could lead to inadvertent fracture during stretch¬ ing. Figure 5 shows an assemblage 50 of fasteners each of which is stretched and has two cylindrical filaments 50-1 and cross bars 5θ£-l and 5θ£-2 at opposite ends and rubber bars 11-1 and 11-2 asso¬ ciated with the respective cross bars. Either of the runner bars 11-1 or 11-2 can be used for feed¬ ing purposes in a gun as described in, for example, United States Patent Specification No. 3,103,666 mentioned above. The other runner bar 11-2 or 11-1 gives stiffness to the assemblage 50 and faci¬ litates their being handled during stretching opera¬ tions where controlled heating is employed. One of the runner bars can be removed by degating at the completion of the stretching operation. It will be apparent that an auxiliary runner bar to facilitate handling in stretcher operations which employ con¬ trolled heating can be used for other kinds of fasteners and devices. Other kinds of blanks which can be subjected to stretching in the manner described are shown in Figures 6A to 6C. In Figure 6A the unstretched fastener 25 has its minimum diameter 25d_ a short distance from the cross bar 25£. In Figure 6B the fastener 26 has a substantially cylindrical filament 26f with a minimum diameter in an intermediate posi¬ tion 26d. In Figure 6C the minimum diameter 27d is at the junction of a decreasing taper 27jt-l (begin¬ ning at the cross bar 27£) and a forward taper 27^-2. When uniform heating is applied to the fila¬ ments 25:£, 26 , and 27f in Figures 6A and 6C stretching begins at the minimum diameter positions 25d, 26d and 27d and progresses in the direction of the succeeding minima. Thus in the case of Figure 6C, since the second taper 27^-2 has a higher shoulder than the first taper 27t:-l, stretching takes, place to the junction 27j_ before there is any significant stretching in the region of the forward taper 27t-2.

Claims: I CLAIM: 1. The method of manufacturing an assemblage of fasteners which comprises the steps of: (a) molding the assemblage as a set of connected individual fasteners, each individual attachment including an end member which is joined by a filament, and (b) stretching at least one of the indi¬ vidual fasteners while a heated probe is in contact with the filament of said one fastener at a pre¬ scribed position along the length of its filament. 2. The method of claim 1 wherein said heated probe is positioned at the junction of said filament and its adjoining end members. 3. The method of claim 1 wherein said filament is subjected to a supplemental heating effect simul¬ taneously with the heat of said probe. 4. The method of claim 1 wherein said probe makes point contact with said filament. 5. The method of claim 2 wherein insulation is applied between said probe and said end member. 6. The method of manufacturing an assemblage of fasteners which comprises the steps of: (a) molding the assemblage as a set of connected individual f steners, each individual attachment including an end member which is joined by a filament, and (b) stretching the individual fasteners simultaneously while subjecting them to controlled heating using a probe at a prescribed position along the lengths of their filaments. 7. A method as claimed in claim 1 or 6 in which the fasteners are connected at one end by a common member and the stretching takes place using jaws which grasp the common member and the other end of the fasteners. 8. The method of claim 1 or 6 wherein the assemblage is fed into a stretching machine with jaws which grip the fasteners at opposite ends and the jaws are separated to take up slack in the fasteners while causing their filaments to become controllably heated, after which the jaws are separated to stretch the filaments simultaneously and are then relaxed to free the assemblage of stretched fasteners and permit their removal. 9. A method as claimed in any of the preceding claims 1 and 2 in which the material of the fasten¬ ers is a crystalline substance whose molecules are reoriented by stretching. 10. The method of claim 1 wherein said fasten¬ ers are molded from polypropylene material which is resistant to cold stretching.

Inventors: PARADIS JOSEPH R, PARADIS, JOSEPH, R.
Applicants: DENNISON MFG CO, DENNISON MANUFACTURING COMPANY
Application year: 1983
Main classification: B29C17
IPC codes: B29C55, G09F3