STABILIZER COMPOSITION FOR STABILIZING POLYMERS OR COPOLYMERS OF VINYL CHLORIDE

Abstract: Compositions for stabilizing polymers or copolymers of vinyl chloride comprising a mixture of (a) an organotin com­ pound or an antimony mercaptide, and (b) a synergistic amount of a compound derived from barium and a thiocarbo­ xylic acid of the formula HSC(R₁)(R₂)COOH, where R₁ repre­ sents a H-atom or a methyl group and R₂ represents a H-atom or a substituted or unsubstituted alkyl group having from 1 to 18 carbon atoms, a cycloalkyl group having 3 to 6 carbon atoms or a phenyl group. Thus, the proportion and hence the cost of organotin compounds or antimony mercaptides to be used in the com­ positions disclosed can be considerably reduced.

Description: Stabilizer composition for stabilizing polymers or copolymers of vinyl chloride The e invention relates to a stabilizer composition for stabilizing poly- mers or copolymers of vinyl chloride comprising a mixture of (a) an organotin compound or an antimony mercaptide, and (b) a synergistic amount of a compound derived from barium and a thio carboxylic acid of the formula HSC ( ) COOR, where E represents a H-atom or a methyl group and R2 represents a H-atcm or a substituted or unsubstituted alkyl group having from 1 to 18 carbon atoms, a cycloalkyl group having 3 to 6 carbon atoms or a phenyl group, and to polymers or copolymers of vinyl chloride containing a stabilizing amount of said composition, and to shaped articles that are entirely or partly formed of these stabilized polymers. Stabilizer compositions of the type indicated above are described in United States Patent Specification 4 115 352. Over previous systems they have the advantage that the same results may be obtained while adding a smaller amount of tin or antimony compounds, which may lead to a substan- tially reduced cost. Surprisingly, it has been found that the proportion of organotin and antimony compounds to be used may still be reduced considerably by using a stabilizer composition according to the invention. The invention consists in that in a stabilizer composition of the known type mentioned in the opening paragraph compound (b) is the barium bisthiocarboxylate of said acid. It has been found that a stabilizer composition having even better properties may be obtained if in addition to compound (b) it contains an amount of barium S,O-thiocarboxylate of said acid and which acts in synergism therewith. The ratio between the two barium compounds is so chosen then that the molar ratio of thiocarboxylate to barium is at least 1,3. Optimum results are found to be obtained at a molar ratio of thiocarboxylate to barium in the range of 1,5 to 1,7. Preparation of the synergistic compound (b) according to the invention is done in the manner known from the literature. To that end for instance a thiocarboxylic acid of the above formula is reacted with barium oxide, hydroxide or alkoxide in an appropriate solvent. As the reaction is quantitative, also all kinds of mixtures of barium bisthiocarboxylate and barium S,O-thiocarboxylate may be prepared by varying the molar ratio of barium to the thiocarboxylic acid. It has been found that generally favourable results may be obtained if the organotin compound corresponds to the formula: EMI2.1 where where x is 1 or 2, Z represents --S(SH2)nCOOR * where n = 1 or 2, EMI2.2 or R2-Sn = Z* wherein Z* is EMI2.3 -S-, or where R represents an alkyl, cycloalkyl, aryl or mixed alkyl-aryl group having not more than 18 carbon atoms which may be substituted or not with one or more of the following groups: - OH, - CN, OR*, EMI2.4 or - CORR*, where R* represents an alkyl, cycloalkyl, aryl or mixed alkyl-aryl group having not more than 18 carbon atoms. Especially good results have been obtained with mixtures of organotin compounds of the formula RSnZ3 and R2SnZ2. Examples of suitable organotin compounds of the above group include: dibutyltin bis (2,4, 4-trimethylpentyl thioglycolate), di-n-octyltin bis (2,4,4-trimethyl-mercaptopropionate), dimethyltin bis (laurylmercaptide), di-n-butyltin bis(methybraleate) bis(methylmaleate), di-n-butyltindilaurate, di-n-butyltin- maleate, monon-butyltin tris (2,4,4-trimethylpentyl thioglycolate), mono-n-octyltin dithioglycolate and di-n-butyltin bis(ethyleneglycol-thio- glycolate). Another group of organotin compounds that may advantageously be used in the stabilizer compositions of the present invention is formed by organotin compounds that correspond to any one of the following formulae: EMI3.1 wherein R represents an alkyl group, a cycloalkyl group, an aryl group, an aralkyl group or an alkaryl group having not more than 18 carbon atoms, Y represents oxygen or sulphur and X is the rest of a polyol or polyhydric phenol having 2 to 6 hydroxyl group after removal of one or more hydroxyl groups, R being substituted or not with one or more of the followinq groups: - OH, -CN, -OR*, EMI4.1 or -OOOR*, where R* represents an alkyl, cycloalkyl, aryl or mixed alkyl-aryl group having not more than 18 carbon atoms. This last-mentioned group of organotin compounds includes, for example: EMI4.2 EMI5.1 A particularly preferred group of organotin compounds satisfies the formula EMI5.2 where n = 1 or 2 and R1 represents an alkyl group having 1 to 18 carbon atoms, which may be substituted or not with an alkoxy group, having 1 to 18 carbon atoms, a polyoxyalkylene group consisting of oxyalkylene groups having 1-4 carbon atoms and as terminal group alkyl or a hydrogen atom, a cycloalkyl group having 3 to 6 carbon atoms, an alkenyl group having 2 to 4 carbon atoms, or a phenyl group, and where X stands for 1/2 S, -S, -S(CH2)mCDO EMI5.3 or -s (CH2)2OCO R3, where m = 1 or 2 and R2 an unsubstituted or substituted alkyl, cycloalkyl, aryl, alkaryl or aralkyl group and R3 has the meaning of an unsubstituted or substituted alkyl, alkenyl, aryl, alkaryl or aralkyl group, with the proviso that n= 2 when x= 1/2 S. Examples of suitable groups for E are: methyl, ethyl, propyl, n-butyl and octadecyl. As examples of polyoxyalkylene groups consisting of oxyalkylene groups having 1 to 4 carbon atoms and as terminal group an alkyl group or a hydrogen atom may be mentioned ethoxyethyl and n-butoxyethyl-oxy-ethyl. An example of a cycloalkyl group is cyclohexyl. An example of an alkenyl group having 2 to 4 carbon atoms is allyl. The estertin compounds that are particularly suitable for use in a stabilizer composition according to the present invention are derived from tetravalent tin and comprise mercaptides of the following formula: EMI6.1 where R2 represents an unsubstituted or substituted alkyl, cycloalkyl, aryl, alkaryl or aralkyl group. w.xamples of these alkyl groups are: ethyl, propyl, butyl, octyl, nonyl, lauryl and octadecyl; aryl, alkaryl and aralkyl groups such as phenyl, benzyl, naphthyl, xylyl or phenyl ethyl. The group S R2, for instance, may represent a mercaptan or mercapto alcohol group. As mentioned before, the group S R2 may be an aliphatic or an aromatic mercaptan. In the case of an aliphatic mercaptan preference is given to compounds having 8 to 18 carbon atoms, such as decyl mercaptan or dodecyl mercaptan. The lower mercaptans are unsuitable for the preparation of stabilizers because of their strong smell. Examples of suitable aromatic mercaptans include thionaphthol, thiobenzyl alcohol and phenxyethyl mercaptan. Examples of suitable mercapto alcohols include monothioethylene glycol, monothiopropylene glycol, thioglycerol and thiodiethylene glycol. Examples of these estertin mercaptides include bis (2-methoxycarbonylethyl) tin dibenzyl mercaptide and 2-lauroxycarbonyl ethyl tin trioctyl mercaptide. British Patent Specification No. 1 502 073 describes estertin compounds of the formula: EMI6.2 Also sulphur-containing ester tin compounds other than the estertin mercaptides of the above formula are suitable for use in a stabilizer composition according to the present invention. Examples of such compounds are the estertin mercapto acid esters of the formula: EMI6.3 Sn (S (CH) 030 R ) wherein m = 1 or 2 and R 2 m 3 4-n 3 represents an unsubstituted alkyl, alkenyl, aryl, alkaryl or aralkyl group. The e sulphur-containing group can therefore be derived from mer- captoacetic acid or ss-mercaptopropionic acid and octanols, such as 2-ethylhexanol, decanols, glycerol, glycol monoesters, dihydroabietyl alcohol, phenoxy ethanol or pentaerythritol. Examples of these estertin mercaptides include: bis (2-butoxycarbonylethyl) tin bis (isooctylthioglycolate), bis (2-butoxy-ethyloxyethyloxycarbonylethyl) tin bis (octade cyl-ssemercaptopropionate) and 2-butoxycarbonyl-ethyltin tris (laurylthioglycolate). Other suitable estertin compounds may be represented by the formula: EMI7.1 wherein h has the abovementioned meaning. Particularly, preference is given to estertin mercaptides derived from the esters of mercapto acids obtained by reacting thioglycol with an aliphatic, aromatic or alicyclic, saturated or unsaturated carboxylic acid. As example of such an estertin mercaptide may be mentioned bis (2-n-butoxycarbonylethyl) tin bis(2-mercapto-ethyl- oleate). Another group of sulphur-containing estertin compounds that are suitable for use in a stabilizer composition according to the present invention may be represented by the formula: EMI7.2 wherein RI has the above-mentioned meaning. As examples may be mentioned: bis (2-n-butoxycarbonylethyl) tin sulphide, bis(2-phenoxyzarbonylethyl) tin sulphide, bis ( 2-octadecyloxycarbonyl- ethyl) tin sulphide and bis(2-butoxyethyloxyethyloxycarbonylethyl) tin sulphide. The antimony compounds to be used in the stabilizer compositions: of the present invention correspond to the formula: Sb X3, where X has the meaning of sulphur, SR or SR30mR2, wherein R1 and R2 have the meaning of an alkyl, alkenyl, alkynyl, aryl, cycloalkyl, cycloalkenyl or mixed aryl-alkyl group having not more than 18 carbon atoms, which may optionally still be substituted with a halogen atom or a EMI8.1 or -COOR* group, where R* is an alkyl group, cycloalkyl group, aryl group or mixed alkyl-aryl group having not more than 18 carbon atoms and g has the meaning of an alkylene, arylene or aralkylene group having not more than 18 carbon atoms. As examples of organic antimony compounds suitable for use in a stabilizer composition according to the present invention may be mentioned; antimony tris (isooctylthioglycolate), antimony tris (isooctyl-ss-mer- captopropionate), antimony tris (glycol dimercaptoacetate), dodecyl mercapto-antimony bis (isooctythioglycolate) bis(isooctylthioglycolate). It has been found that generally favourable results are obtained when the weight ratid between the tin or antimony compounds of group (a) and of the barium compound(s) of group (b) is in the range of 0,05 : 1 to 3 : 1, preference being given to a weight ratio between ore: 1 and 0,3 : 1. The stabilizer compositions according to the present invention may be prepared in a simple manner by intermixing the separate ingredients. If desired, additives may previously be incorporated into the stabilizer composition to be mixed later on with the polymer. Alternatively, constituents of the stabilizer mixture and any further additives may be mixed into the polymer mixture separately, for instance during processing. The e stabilizer compositions of the present invention are particularly suitable for improving the thermal stability of any kind of polyvinyl chloride resin irrespective of its method of preparation. In this con nection mention is made of solution polymerization, emulsion polymerization and suspension polymerization. The term polyvinyl chloride as used here not only comprises any kind of hopopolymer of vinyl chloride, and post-chlorinated polyvinyl chloride, but also copolymers whose most important constituent is vinyl chloride and a small amount of other copolymerizable monomers, such as copolymers of vinyl chloride and vinyl acetate, copolymers of vinyl chloride and vinylidene chloride, copolymers of vinyl chloride and acrylonitrile, copolymers of vinyl chloride and maleic or fumaric esters and copolymers of vinyl choride and styrene, and also mixtures containing a high percentage of polyvinyl chloride resin and a low percentage of sane other resin, such as chlorinated polyethylene, copolymers of acrylonitrile, butadiene and styrene. The invention is further described in but not limited by the following examples. The heat stability figures provided by the examples were obtained as follows. First the various constituents of each specific formulation were mixed on a laboratory two-roll mill at a temperature of 1600C for a period of 4 minutes after gelation. The approximately 1,5 ttrn thick sheet leaving the roll mill was cut into samples. Heat stability tests were performed in a Heraeus oven equipped with rotating sample trays. Samples were removed from the oven at 10 minute intervals and visually assessed for colour development. The change of colour was taken as a measure of the decomposition rate of the PVC. The e results of the ex- periments are rated from 1 (colourless) to 10 (black). Example I. The following "rigid" PVC formulation was prepared and tested in the above-described manner: parts bs weight: PVC (prepared by suspension polymerization; K-value 62) 100 lubricant (mixed esters) 1,0 processing aid derived from acrylic acid 1,0 stabilizer 1,2 The e organotin compounds used were: : bis (2-butoxycarbonylethyl) tin bis (2-ethylhexylthioglycolate) = stabilizer A dioctyltin bis (2-ethylhexylthioglycolate) = Oct2 Sn bis (2-n-butoxycarbonylethyl) tinsulphide = (Bu Ac) 2 S bis (2-n-butoxycarbonylethyl) tin bis (monomethylmaleate) = (Bu Ac) 2 Sn (MMM)2 butyltin tris (2-ethylhexylthioglycolate) = Bu Sn (2 EHTG)3 dibutyltinoxide = Bu2 Sn O dibutyltindilaurate = Bu2 Sn (laurate)2 In all the cases where the aboveementioned tin compounds were combined with barium bisthioglycolate (Ba (TG) 2) the weight ratio was 1 part of barium compound to 0,2 parts of tin compound. The colour development results obtained during the heat stability test at 1850C are given in the following table. Table I Comparison of Ba (TG) 2 / Organotin mixtures Stabilizer composition Ba (TG) 2 Organotin EMI11.1 <tb> 1,0 <tb> 0,2 <tb> per 100 parts of PVC Colour DeveloPment after stated Period at 185 C EMI11.2 <SEP> <tb> Stabilizer <SEP> Time <SEP> (min.) <tb> Car <SEP> position <SEP> O <SEP> <SEP> 10 <SEP> 20 <SEP> 30 <SEP> 40 <SEP> 50 <SEP> 60 <SEP> 70 <SEP> 80 <SEP> 90 <SEP> 100 <SEP> 110 <SEP> 120 <SEP> 130 <tb> A <SEP> (1,2) <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 1 <SEP> 10 <tb> A <SEP> (0,2)+ <tb> Ba(TG)2 <SEP> (1,0) <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 1 <SEP> 2 <SEP> 2 <SEP> 3 <SEP> 3 <SEP> 4 <SEP> 5 <SEP> 7 <SEP> 8 <SEP> 10 <tb> Oct2Sn(2EHTG)2 <SEP> (1,2) <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 1 <SEP> 2 <SEP> 2 <SEP> 3 <SEP> 7 <SEP> 10 <tb> Oct2Sn(2EE1TG)2 <SEP> (0,2)+ <tb> Ba(TG)2 <SEP> (1,0) <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 1 <SEP> 1 <SEP> 2 <SEP> 2 <SEP> 3 <SEP> 4 <SEP> 5 <SEP> 7 <SEP> 9 <SEP> 10 <tb> (BuAc)2SnS <SEP> (1,2) <SEP> 1 <SEP> 2 <SEP> 2 <SEP> 2 <SEP> 3 <SEP> 3 <SEP> 3 <SEP> 4 <SEP> 6 <SEP> 10 <tb> (BuAc)2SnS <SEP> (0,2)+ <tb> Ba(TG) <SEP> 2 <SEP> (1,0) <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 1 <SEP> 1 <SEP> 2 <SEP> 3 <SEP> 5 <SEP> 7 <SEP> 9 <SEP> 10 <tb> (BuAc)2Sn(MMM)2 <SEP> (1,2) <SEP> 2 <SEP> 3 <SEP> 4 <SEP> 7 <SEP> 10 <tb> (BuAc)2Sn(MMM)2 <SEP> (0,2) <SEP> + <SEP> <tb> Ba(TG)2 <SEP> (1,0) <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 1 <SEP> 2 <SEP> 2 <SEP> 3 <SEP> 3 <SEP> 4 <SEP> 5 <SEP> 7 <SEP> 8 <SEP> 10 <tb> BuSn(2EErG)3 <SEP> (1,2) <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 10 <tb> BuSn(2EHTG)3 <SEP> (0,2)+ <SEP> <tb> Ba(TG)2 <SEP> (1,0) <SEP> 0 <SEP> 2 <SEP> 2 <SEP> 3 <SEP> 3 <SEP> 4 <SEP> 5 <SEP> 6 <SEP> 7 <SEP> 9 <SEP> 10 <tb> BSrO <SEP> (1,2) <SEP> 3 <SEP> 4 <SEP> 7 <SEP> 8 <SEP> 10 <tb> Bu2SnO <SEP> (0,2)+ <tb> Bu3SnO <tb> Ba <SEP> (TG)2 <SEP> (1,0) <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 2 <SEP> 3 <SEP> 6 <SEP> 7 <SEP> 9 <SEP> 10 <tb> Bu2Sn(laurate)2 <SEP> (1,2) <SEP> 0 <SEP> 4 <SEP> 5 <SEP> 6 <SEP> 7 <SEP> 10 <tb> Bu2Sn(laurate)2 <SEP> (0,2) <SEP> + <tb> Ba(TG)2 <SEP> (1,0) <SEP> 0 <SEP> 1 <SEP> 1 <SEP> 2 <SEP> 2 <SEP> 3 <SEP> 4 <SEP> 5 <SEP> 6 <SEP> 8 <SEP> 9 <SEP> 10 <tb> Ba(TG)2 <SEP> (1,2) <SEP> 2 <SEP> 6 <SEP> 6 <SEP> 6 <SEP> 6 <SEP> 6 <SEP> 7 <SEP> 10 <tb> Example II In this example the results are given of a heat stability test at 1850C on antimony tris (2-ethylhexyl thioglycolate) = Sb (2 EHTG)3 and barium bisthioglycolate = Ba(TG)2. In addition, the results are given of a comparative test on Sb (2EH TG) and barium bis(2-ethylhexyl thioglycolate) = Ba (2EH TG)2 and barium thioglycolate = Ba(TG) The results are given in the table below. Table II Comparison of Sb (2EHT2G)3/Ba (2EHTG)2, Sb(2EHTG)3/BaTG and Sb (2EHTG)3/Ba(TG)2 mixtures. Colour Development after stated period at 1850C EMI12.1 <tb> Stabilizer <SEP> Time <SEP> (min.) <tb> Composition <SEP> 0 <SEP> 10 <SEP> '20 <SEP> 30 <SEP> 40 <SEP> 50 <SEP> 60 <SEP> 70 <SEP> 80 <SEP> 90 <SEP> 100 <SEP> llO <SEP> 120 <SEP> 130 <SEP> <tb> A <SEP> (0,2) <SEP> 0 <SEP> 0 <SEP> 1 <SEP> 2 <SEP> 2 <SEP> 3 <SEP> 3 <SEP> 4 <SEP> 5 <SEP> 7 <SEP> 8 <SEP> 10 <SEP> <tb> Ba(TG)2 <SEP> (1,0) <tb> Sb(2EHTG)3 <SEP> (1,2) <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 1 <SEP> 10 <tb> Sb(2EHTG)3 <SEP> (0,2) <tb> Ba(2EHTG)2 <SEP> (1,0) <SEP> 2 <SEP> 3 <SEP> 3 <SEP> 4 <SEP> 6 <SEP> 8 <SEP> 9 <SEP> 10 <tb> Sb(2EHTG)3 <SEP> (0,2) <tb> BaTG <SEP> (1,0) <SEP> O <SEP> 0 <SEP> O <SEP> <SEP> 1 <SEP> 4 <SEP> 6 <SEP> 6 <SEP> 7 <SEP> 7 <SEP> 8 <SEP> 8 <SEP> 9 <SEP> 10 <tb> Sb(2EHTG)3 <SEP> (0t2) <tb> Ba(TG)2 <SEP> (1,0) <SEP> 0 <SEP> 0 <SEP> 1 <SEP> 1 <SEP> 1 <SEP> 1 <SEP> 2 <SEP> 2 <SEP> 3 <SEP> 3 <SEP> 4 <SEP> 7 <SEP> 9 <SEP> 10 <SEP> <tb> The results in the above table clearly show that PVC containing the combination of Sb(2 EE?rG) 3 with Ba(TG)2 according to the invention is far more stable than that stabilized with the combinations of Sb(2ErG)3, with BaTG or Ba(2EHIG)2 recommended in United States Patent Specification 4 115 352. Example III In this example the results are given for the organotin stabilizer A of Example I in various weight ratios, use being made of some barium salts according to United States Patent Specification 4 115 352 and barium bisthioglycolate according to the invention. It is clear from this table that the effect of the synergistic action between A and Ba (TG) 2 is optimal upon using a fivefold excess of Ba (TG) 2 Table III Comparison of A/Ba(O2C.CH2SH)2, EMI14.1 A/Ba(2EHTG)2 mixtures. Colour development after stated period at 1850C EMI14.2 <tb> Stabilizer <SEP> Time <SEP> (min.) <tb> Composition <SEP> 0 <SEP> 10 <SEP> 20 <SEP> 30 <SEP> 40 <SEP> 50 <SEP> 60 <SEP> 70 <SEP> 80 <SEP> 90 <SEP> 100 <SEP> 110 <SEP> <SEP> 120 <SEP> <tb> A <SEP> (1,2) <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 1 <SEP> 10 <tb> A <SEP> (0,6) <tb> Ba(2EHTG)2 <SEP> (0,6) <SEP> 2 <SEP> 2 <SEP> 2 <SEP> 2 <SEP> 3 <SEP> 3 <SEP> 5 <SEP> 10 <tb> A <SEP> (0,4) <tb> Ba(2EHTG)2 <SEP> (0,8) <SEP> 3 <SEP> 3 <SEP> 3 <SEP> 3 <SEP> 3 <SEP> 5 <SEP> 6 <SEP> 10 <tb> A <SEP> (0,2) <SEP> <tb> Ba(2EHTG)2 <SEP> (1,0) <SEP> 3 <SEP> 3 <SEP> 4 <SEP> 4 <SEP> 5 <SEP> 6 <SEP> 8 <SEP> 9 <SEP> 10 <tb> Ba(2EHTG)2 <SEP> (1,2) <SEP> 5 <SEP> 6 <SEP> 8 <SEP> <RTI ID=14.7> 9 <SEP> 10 <tb> A <SEP> (0,6) <tb> Ba <SEP> TG <SEP> (0,6) <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 1 <SEP> 2 <SEP> 3 <SEP> 5 <SEP> 9 <SEP> 10 <SEP> <tb> A <SEP> (0,4) <tb> Ba <SEP> TG <SEP> (0,8) <SEP> 0 <SEP> 0 <SEP> 1 <SEP> 2 <SEP> 3 <SEP> 5 <SEP> 6 <SEP> 9 <SEP> 10 <tb> A <SEP> (0,2) <tb> Ba <SEP> TG <SEP> (1,0) <SEP> 0 <SEP> 0 <SEP> 1 <SEP> 3 <SEP> 4 <SEP> 5 <SEP> 6 <SEP> 8 <SEP> 10 <tb> Ba <SEP> TG <SEP> (1,2) <SEP> 1 <SEP> 3 <SEP> 5 <SEP> 6 <SEP> 9 <SEP> 10 <tb> A <SEP> (0,6) <SEP> <tb> Ba(TG)2 <SEP> (0,6) <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 1 <SEP> 2 <SEP> 7 <SEP> 8 <SEP> 10 <tb> A <SEP> (0,4) <tb> Ba(TG)2 <SEP> (0,8) <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 1 <SEP> 1 <SEP> 1 <SEP> 2 <SEP> 4 <SEP> 6 <SEP> 810 <tb> A <SEP> (0,2) <tb> Ba(TG)2 <SEP> (1,0) <SEP> 0 <SEP> O <SEP> <RTI ID=14.11> O <SEP> <SEP> 1 <SEP> 2 <SEP> 2 <SEP> 3 <SEP> 3 <SEP> 4 <SEP> 5 <SEP> 7 <SEP> 8 <SEP> 10 <tb> Ba(TG)2 <SEP> (1,2) <SEP> 2 <SEP> 6 <SEP> 6 <SEP> 6 <SEP> 6 <SEP> 6 <SEP> 7 <SEP> 10 <tb> example IV In this example the following PVC formulation was tested: parts by weight PVC (prepared by suspension polymerization; K value 57) 100 cetyl/stearyl alcohol 1,0 polyethylene wax 0,1 processing aid derived from acrylic acid 1,0 stabilizer 1,2 For each stabilizer composition the time was measured (in a Brabender Plasticorder) after which the mixture began to degrade. The results are given in the table below. Table IV Stabilizer Degradation Time (min) A (1,2) 14 Ba(2 EHTG)-2 (1,2) 10 A (0,2) + Ba(2 EHIG)2 (1,0) 12 BY TUG (1,2) 10 A (0,2) + Ba TG (1,0) 16 Ba (TG)2 (1,2) 14 A (0,2) + Ba (TG)2 (1,0) 18 The above table clearly shows that the stabilizer mixture of 0,2 A and 1,0 Ba (TG) 2 degraded slowest. Example V In this example a comparison is made of combinations of an organotin com- pound with various barium salts including barium bisthioglycolate. The amount of barium salt was so chosen that the barium content of each come position was equivalent to that of a córresponding Ba(TG)2-containing composition. The stabilizer compositions were incorporated into the same PVC formulation as given in Eye I. The results are listed in the table below, in which Ba (vers)2 stands for barium versatate (13% Ba) Ba (Nap)2 stands for barium naphthenate (10% Ba) Ba (TG)2 stands for barium bisthioglycolate (43% Ba). Table V Comparison of A/Ba(TG)2 with A/Barium soap mixtures at equivalent Ba concentration. Colour development after stated period at 185 C EMI16.1 <tb> Stabilizer <SEP> Tilne <SEP> (min) <tb> Composition <SEP> 0 <SEP> 10 <SEP> 20 <SEP> 30 <SEP> 40 <SEP> 50 <SEP> 60 <SEP> 70 <SEP> 80 <SEP> 90 <SEP> 100 <SEP> 110 <SEP> 120 <SEP> <tb> A <SEP> (1,2) <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 1 <SEP> 10 <SEP> <tb> A <SEP> (0,2) <tb> Ba(Vers)2 <SEP> (3,3) <SEP> 2 <SEP> 3 <SEP> 4 <SEP> 5 <SEP> 6 <SEP> 8 <SEP> 10 <tb> A <SEP> (0,2) <tb> Ba(Nap)2 <SEP> (4,6) <SEP> 2 <SEP> 2 <SEP> 3 <SEP> 4 <SEP> 5 <SEP> 7 <SEP> 10 <tb> A <SEP> (0,2) <SEP> <tb> Ba(TG)2 <SEP> (1,9) <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 1 <SEP> 2 <SEP> 2 <SEP> 3 <SEP> 3 <SEP> 4 <SEP> 5 <SEP> 7 <SEP> 8 <SEP> 10 <tb> Ba(Vers)2 <SEP> (4,0) <SEP> 2 <SEP> 5 <SEP> 7 <SEP> 9 <SEP> 10 <tb> Ba <SEP> (Nap)2 <SEP> (5,5) <SEP> 2 <SEP> 5 <SEP> 5 <SEP> 7 <SEP> 10 <tb> Ba(TG)2 <SEP> (1,2) <SEP> 2 <SEP> 6 <SEP> 6 <SEP> 6 <SEP> 6 <SEP> 6 <SEP> 7 <SEP> 10 <tb> Exattiple V1: In this example the effect is ascertained of alkaline earth bisthioglycolates other than barium. The table below shows that use of Ba(TG)2 and an organotin compound leads to considerably better results than Sr(TG)2 or Ca (TG) 2 The change in colour was again determined at 1850C. Table VI Comparison of AM(TG) 2 mixtures. Colour Development after stated period at 1850C EMI17.1 <tb> Stabilizer <SEP> Time <SEP> (min) <SEP> <tb> Composition <SEP> 0 <SEP> 10 <SEP> 20 <SEP> 30 <SEP> 40 <SEP> 50 <SEP> 60 <SEP> 70 <SEP> 80 <SEP> 90 <SEP> 100 <SEP> 110 <SEP> <SEP> 120 <tb> A <SEP> (1,2) <SEP> 0 <SEP> 0 <SEP> 0 <SEP> <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 1 <SEP> 10 <tb> A <SEP> (0,2) <SEP> <tb> Ba(TG)2 <SEP> (1,0) <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 1 <SEP> 2 <SEP> 2 <SEP> 3 <SEP> 3 <SEP> 4 <SEP> 5 <SEP> 7 <SEP> 8 <SEP> 10 <tb> A <SEP> (0,2) <tb> Sr(TG)2 <SEP> (1,0) <SEP> 0 <SEP> 0 <SEP> 2 <SEP> 4 <SEP> 4 <SEP> 4 <SEP> 5 <SEP> 6 <SEP> 6 <SEP> 6 <SEP> 7 <SEP> 8 <SEP> 10 <tb> A <SEP> (0,2) <tb> Ca(TG)2 <SEP> (1,0) <SEP> 0 <SEP> 1 <SEP> 3 <SEP> 6 <SEP> 7 <SEP> 7 <SEP> 7 <SEP> 8 <SEP> 8 <SEP> 9 <SEP> 10 <tb> Ba(TG)2 <SEP> (1,2) <SEP> 2 <SEP> 6 <SEP> 6 <SEP> 6 <SEP> 6 <SEP> 6 <SEP> 7 <SEP> 10 <tb> Sr(TG)2 <SEP> (1,2) <SEP> 2 <SEP> 6 <SEP> 6 <SEP> 6 <SEP> 6 <SEP> 7 <SEP> 10 <tb> Ca(TG)2 <SEP> (1,2) <SEP> 4 <SEP> 7 <SEP> 8 <SEP> 8 <SEP> 8 <SEP> 9 <SEP> 10 <tb> Example VII In this example it is shown that the use of the stabilizer compositions according to the invention leads to even better results at a thioglycolate to barium ratio lower than 2. The stabilizer compositions were incorporated into a PVC formulation as indicated in Example I. The colour development at 1850C is given in the table below. Table VII Comparison of A/Ba(TG)n mixtures (n=l-µ 2) Colour Developed after stated period at 1850C EMI18.1 <tb> Stabilizer <SEP> Time <SEP> (min) <SEP> <tb> Composition <SEP> 0 <SEP> 10 <SEP> 20 <SEP> 30 <SEP> 40 <SEP> 50 <SEP> 60 <SEP> 70 <SEP> 80 <SEP> 90 <SEP> 100 <tb> A <SEP> (1,2) <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 1 <SEP> 10 <tb> A <SEP> (0,6) <tb> Ba <SEP> TG <SEP> (0,6) <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 1 <SEP> 2 <SEP> 3 <SEP> 5 <SEP> 9 <SEP> 10 <SEP> <tb> A <SEP> (0,6) <tb> Ba(TG)1 <SEP> 3 <SEP> (0,6) <SEP> 0 <SEP> 0 <SEP> 0 <SEP> O <SEP> <SEP> O <SEP> <SEP> 1 <SEP> 2 <SEP> 7 <SEP> 8 <SEP> 10 <tb> A <SEP> (0,6) <tb> <RTI ID=18.9> Ba(TG)1,6 <SEP> (0,6) <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 1 <SEP> 5 <SEP> 8 <SEP> 10 <tb> A <SEP> (0,6) <SEP> <tb> Ba(TG)2 <SEP> (0,6) <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 1 <SEP> 2 <SEP> 7 <SEP> 8 <SEP> 10 <tb> Example VIII In this example the results are given of a heat stability test at 1850C on a combination of barium bisthiolactate and the organotin stabilizer A of Example I. In addition, the results are given of comparative tests on stabilizer A and barium bisthiolactate, respectively. The stabilizer compositions were incorporated into the same PV: formulation as given in Example I. The results are listed in the table below, in which Ba (Tl) 2 stands for barium bisthiolactate. Table VIII Colour developed after stated period at 1850C time (min) EMI18.2 <tb> Stabilizer <SEP> Time <SEP> (min) <tb> Composition <SEP> 0 <SEP> 10 <SEP> 20 <SEP> 30 <SEP> 40 <SEP> 50 <SEP> 60 <SEP> 70 <SEP> 80 <SEP> 90 <SEP> 100 <SEP> llO <SEP> 120 <SEP> <tb> A <SEP> (1,2) <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 0 <SEP> 1 <SEP> 10 <tb> A <SEP> (0,2) <tb> Ba(Tl)2 <SEP> (1,0) <SEP> 0 <SEP> 0 <SEP> 1 <SEP> 1 <SEP> 1 <SEP> 2 <SEP> 2 <SEP> 3 <SEP> 5 <SEP> 8 <SEP> 10 <tb> Ba(T1)2 <SEP> (1,2) <SEP> 2 <SEP> 3 <SEP> 5 <SEP> 5 <SEP> 6 <SEP> 9 <SEP> 10 <tb>

Claims: PALMS 1. A stabilizer composition for stabilizing polymers or copolymers of vinyl chloride comprising a mixture of (a) an organotin compound or an antimony mercaptide, and (b) a synergistic amount of a compound derived from barium and a thiocarboxylic acid of the formula HSC (R2) OOOH, where RI represents a H-atom or a methyl group and R2 represents a H-atom or a substituted or unsubstituted alkyl group having from 1 to 18 carbon atoms, a cycloalkyl group having 3 to 6 carbon atoms or a phenyl group, characterized in that compound (b) is the barium bisthiocarboxylate of said acid. 2. A stabilizer composition according to claim 1, characterized in that in addition to compound (b) it contains an amount of barium S,O-thio carboxylate derived from said acid and which acts in synergism there with. 3. A.stabilizer composition according to claim 2, characterized in that the molar ratio of thiocarboxylate to barium is at least 1,3. 4. A stabilizer composition according to claim 2, characterized in that the molar ratio of thiocarboxylate to barium is in the range of 1,5 to 1,7. 5. A stabilizer composition according to one or more of the preceding claims, characterized in that the organotin compound corresponds to the formula: EMI19.1 Rx-Sn-Z(4 (4-x)' where x is 1 or 2, Z represents --S(CH2) )nCOOR * where n = 1 or 2, EMI20.1 or R2-Sn = Z* wherein Z* is EMI20.2 where R represents an alkyl, cycloalkyl, aryl or mixed alkyl-aryl group having not more than 18 carbon atoms which may be substituted or not with one or more of the following groups: : - OH, - CN, OR*, EMI20.3 or - POOR*, where R* represents an alkyl, cycloalkyl, aryl or mixed alkyl-aryl group having not more than 18 carbon atoms. 6. A stabilizer composition according to one or more of the claims 1-4, characterized in that the organotin compound corresponds to one of the following formulae: EMI20.4 wherein R is an alkyl group, a cycloalkyl group, an aryl group, an aralkyl group or an alkaryl group having not more than 18 carbon atoms, Y represents oxygen or sulphur and X is the rest of a polyol or polyhydric phenol having 2 to 6 hydroxyl groups after removal of one or more hydroxyl groups, the group R being substituted or not with one or more of the following groups: * - OH, - CN, - OR, EMI21.1 or - CCOR*, wherein R* is an alkyl group, cycloalkyl group, aryl group or mixed alkyl-aryl group having not more than 18 carbon atoms. 7. A stabilizer composition according to one or more of the claims 1-4, characterized in that the organotin compound corresponds to the formula: EMI21.2 Sn X4 n where n = 1 or 2 and R1 represents an alkyl group having 1 to 18 carbon atoms that may optionally be substituted with an alkoxygroup having 1 to 18 carbon atoms, a polyoxyalkylene group consisting of oxyalkylene groups having 1-4 carbon atoms and as a terminal group alkyl or a hydrogen atom, a cycloalkyl group having 3 to 6 carbon atoms, an alkenyl group having 2 to 4 carbon atoms, or a phenyl group, and wherein X stands for 1/2 S, -SR2, -S(CH2)m COO R3, EMI21.3 or -S(CH2)m O CO R3, wherein m = 1 or 2 and R2 represents an unsubstituted or substituted alkyl, cycloalkyl, aryl, alkaryl or aralkyl group, and R3 has the meaning of an unsubstituted or sub stituted alkyl, alkenyl, aryl, alkaryl, or aralkyl group, with the proviso that n = 2 when X = 1/2 S. 8. A stabilizer composition according to one or more of the claims 1-4, characterized in that the organo-antimony sulphur compound corre sponds to the formula: Sb X3, where X has the meaning of sulphur, SR1 or SR30X1R2, wherein R1 and h have the meaning of an alkyl, alkenyl, alkynyl, aryl, cycloalkyl, cycloalkenyl or mixed aryl-alkyl group having not more than 18 carbon atoms, which may optionally still be substituted with a halogen atom or a EMI22.1 or -C00R* group, where R* is an alkyl group, cycloalkyl group, aryl group or mixed alkyl-aryl group having not more than 18 carbon atoms and R3 has the meaning of an alkylene, arylene or aralkylene group having not more than 18 carbon atoms. 9. Polymers or copolymers of vinyl chloride containing a stabilizing amount of a stabilizer composition according to one or more of the preceding claims. 10 Polymers or copolymers of vinyl chloride according to claim 9 characterized in that the amount of stabilizer composition is in the range of from 0,05 to 3 parts by weight per 100 parts by weight of polymer. 11. Shaped articles entirely or partly composed of a polymer or copoly mer of vinyl chloride according to claim 9 or 10.

Inventors: BURLEY, JOSEPH WILLIAM
Applicants: AKZO N.V.
Application year: 1983
Main classification: C08L27
IPC codes: C08K5, C08L27, C08L1