A METHOD OF PROVIDING A PROTECTED LAYER

Abstract: A method of providing on a substrate a protected binder layer characterised in coating an assembly containing on a transparent flexible plastics material film support a binder layer containing particles of less than 10 µm in size and an adhesive layer and adhering said assembly to a substrate. The assemblies coated in the substrate are highly translucent.

Description: A method of providing a protected layer. This invention relates to a method of providing on a substrate a protected layer containing particles. Particulate, preferably pigmented transparent flexible plastics material has found several uses for example as window coverings to reduce glare. However, it is difficult to achieve a wide variety of coloured transparent plastics material because of difficulties associated with dyeing or pigmenting plastics materials especially polyester, dyed polyesters often having very poor light fastness. In general, coated transparent flexible plastics materials wherein the pigment is present in a binder layer coated on the plastics material have not been prepared on a large scale because of their poor scratch resistance, their low humidity resistance and their susceptibility to bacterial and fungal attack. However, binder layers could be advantageous in that a great variety of particulate material can be dispersed therein and the binder then coated on the support. Moreover, unless there is a good refractive index match between the binder and the dispersed phase in the binder, highly light scattering coatings are obtained. This results in the coated material having reduced transparency. However, in applications where a high translucence of the coated material is required it would be necessary to achieve a very small particle size for the pigment in the dis 5lO -2 persed phase, in the order of 5 10 pm so that the light scattering effect does not take place in the visible region of the spectrum. A method has now been found which comprises providing on a substrate a protected binder layer containing particles, in which method the above mentioned disadvantages are minimised. According to the present invention there is provided a method of providing on a substrate a protected binder layer characterised by coating onto a transparent flexible plastics material film support in this order a binder layer containing particles of less than 10 01m in size and an adhesive layer and adhering said assembly to a substrate. Preferably, the transparent flexible plastics material film support is a support used for photographic film materials. Such supports are for example cellulose acetate, cellulose acetate-butyrate and biaxially oriented polyester, polystyrene and polycarbonate. The binder layer may be a solvent coated layer or, preferably, an aqueous coated layer. Most preferably, the binder is gelatin or a mixture of gelatin and an aqueous latex which is obtained, for example, from copolymerisation of an unsaturated carboxylic acid or carboxylic acid ester and an ethylenically unsaturated compound. Examples of suitable mixtures are gelatin and a latex of a copolymer of butyl acrylate/styrene and also gelatin with a latex of a copolymer of hydroxypropyl acrylateAnethylmethacrylate/butyl acrylate. An example of a binder which is at least partially solvent coatable is polyvinyl alcohol coated from an aqueous alcohol mixture. Any adhesive may be coated on the binder layer as long as this coating does not affect the underlying binder layer and as long as activation of the adhesive does not affect the binder layer. Preferably, the adhesive layer is applied from a solvent sytem. Preferred adhesives are pressure-sensitive adhesives and heatsensitive (or hot melt)adhesives. The preferred adhesives are pressure-sensitive adhesives. The preferred pressure-sensitive adhesives are acrylates. Examples of suitable adhesives are listed in "Adhesives Handbook", J. Shields, Butterworths, London 1970. Others are well known to those versed in the art. Examples of particulate material or particles which may be dispersed in the binder layer are organic pigments for example phthalocyanines, chinacridines, isoindolinones, dioxazines and anthraquinones, inorganic pigments such as oxides of e.g. titanium, zinc, iron, lead, manganese, chromium, cobalt, zinc, antimony and aluminium, sulfides of e.g. mercury, cadmium, antimony and tin, U.V. and I.R. absorbers such as derivatives of triazine, benzotriazole, hydrazone and metal, preferably manganese complexes of ethylene-l,2-dithiolates, nitrosophenols or azo compounds, or derivatives of polymethindyes, finely divided metals such as aluminium, silver, gold or brass, preferably as light-reflecting particles, and photochromic glass beads such as glass beads containing silver halides, preferably silver chloride, further copper and cadmium halides as well as certain organic compounds, such as spiropyran derivatives. Useful coating thicknesses of the binder layer are from 1 to 2000m. Useful coating thicknesses of the adhesive layer are from 0.2 to 100pom. When the assembly of the present invention is adhered to a substrate, i.e. to a glass, plastic, metal or wooden surface for example, the outward facing surface of the assembly is the uncoated side of the plastics material film support which exhibits good scratch resistance. Further bacteria and fungi are inhibited from attacking the binder layer by lack of access to the binder layer. Surprisingly, it has been found, that the inventively used assemblies exhibit an increased transparency which is shown in the accompanying Examples. Example 1: 1 g of an isoindolinone pigment(CI Pigment Yellow 109) having a mean particle dye of 0.69A1In and a polydispersity of 7, as measured on the Coulter Nanosizer, is dispersed in a mixture of 10 ml water and 0.1 ml of a wetting agent, (adduct obtained from octylphenol and 10 mols of ethylene oxide) using 10 g glass beads in a mixer mill for 1 hour. The formulation is further mixed, after washing it free from the glass beads, with water (80 ml), deionised blend gelatin (5 g), and the wetting agent mentioned ( 5 ml of 5% solution). The whole is melted out at 40 C for 1 hour. Formaldehyde (5 ml of 1Z aqueous solution) is added and the mixture immediately coated onto subbed polyester film support to give a coating (I) of 2.5 mg/dmê of said pigment and 12.5 mg/dm of gelatin. When the coating has dried and hardened, a portion of it is further coated on the gelatin side, with a solution of a polyvinyl acetate adhesive in five parts of ethyl acetate. The coating is dried, then applied with pressure to a piece of clear glass so that good adhesion is obtained, giving an assembly (11). The light absorption of the two coatings is measured in a U.V./Visible spectrophotometer. Results are shown thus: Table 1 EMI5.1 <tb> wavelength <SEP> of <SEP> light <SEP> (nm) <SEP> optical <SEP> density <tb> <SEP> (I) <SEP> (11) <tb> <SEP> 700 <SEP> 0.33 <SEP> 0.23 <tb> <SEP> 600 <SEP> 1 <SEP> 0.45 <SEP> 0.35 <tb> <SEP> 500 <SEP> 0.85 <SEP> 0.75 <tb> <SEP> 400 <SEP> 1.40 <SEP> 1.28 <tb> Visual examination further shows that coating (I) is highly scattering, whilst assembly (II) is highly translucent. Optical microscopical examination of assembly (II) shows that the yellow pigment is still present in the gelatin, and none has dissolved in the adhesive layer. Example 2: An assembly is prepared as shown in Example 1, but using 1 g of a dioxazine pigment (Cl Pigment Violet 37) instead of the yellow pigment. The violet pigment has a mean particle size of 0.46pm and a polydispersity of 8. Two assemblies (I) and (II) are prepared as before, and their absorption in a U.V./;risible spectrophotometer is as shown: Table 2 EMI5.2 <tb> wavelength <SEP> of <SEP> light <SEP> (nm) <SEP> optical <SEP> density <tb> <SEP> (I) <SEP> (11) <tb> <SEP> 700 <SEP> 0.80 <SEP> 0.56 <tb> <SEP> 600 <SEP> 1.18 <SEP> 1.02 <tb> <SEP> 500 <SEP> 1.00 <SEP> 0.90 <tb> <SEP> 400 <SEP> 0.55 <SEP> 0.32 <tb> Visual examination of assembly (11) shows that it is highly translucent, whilst assembly (I) is highly scattering. Example 3: A coating (I) of the dioxazine pigment used in Example 2 IS prepared as in Example 2. It is then pressed together with a coating of a polyvinyl acetate adhesive on a paper silicone treated on the side upon which adhesive has been coated. Removal of the silicone paper results in the total transfer of the adhesive from it to the gel coating. This assembly can then be adhered to glass, e.g., just as assembly (II) of Example 2. Objective and subjective measurements on the degree of scatter in this new assembly are identical to those of (II) above. Further, the adhesive-coated assembly can be adhered to glass, torn off and re-adhered a number of times without damage to the assembly, and without leaving adhesive or gelatin fragments on the glass. Example 4: An assembly is prepared as in Example 1, but fusing 1 g of photocromic glass beads of amean particle size of 5pom instead of the yellow pigment. The glass beads contain silver chloride as the photochromic system. U.V./visible measurements on assemblies (I) and (II) lead to the following optical density values: Table 3 EMI6.1 <tb> wavelength <SEP> of <SEP> light <SEP> (nm) <SEP> optical <SEP> density <tb> <SEP> (I) <SEP> (11) <tb> <SEP> 700 <SEP> 0.16 <SEP> 0.05 <tb> <SEP> 600 <SEP> 0.155 <SEP> 0.055 <tb> <SEP> 500 <SEP> 0.15 <SEP> 0.075 <tb> <SEP> 400 <SEP> 0.165 <SEP> 0.085 <tb> Visual examination of assembly (I) shows it to be dull and scattering, whilst assembly (II) is bright and clear. Example 5: 1 g of polymethylmethacrylate beads, of average particle size 2.3 Fm are dispersed in water, using an alkylnaphthalene sulphonate surfactant. This dispersion is added to a formulation containing gelatin, a styrene/butyl acrylate latex (of a mean particle size of 0.3 m), the ethoxylated octylphenol surfactant of Example 1 and dimethylolurea as gelatin hardener. Coating this mixture onto lOO,um clear subbed polyester gives a somewhat scattering coating (I) containing gelatin 10 mg/dmê, latex 5 mg/dmê, and polymethylmeth 2 acrylate beads 2.5 mg/dm Application of an adhesive-coated silicone paper, as in Example 3, removal of the paper and adhesion to glass, gives a non-scattering assembly (II). Examination of (I) and (II) by U.V./Visible spectroscopy afforded the following confirmatory results: Table 4: EMI7.1 <tb> wavelength <SEP> of <SEP> light <SEP> (nm) <SEP> optical <SEP> density <tb> <SEP> (I) <SEP> (11) <tb> <SEP> 700 <SEP> 0.13 <SEP> 0.01 <tb> <SEP> 600 <SEP> 0.125 <SEP> 0.015 <tb> <SEP> 500 <SEP> 0.125 <SEP> 0.025 <tb> <SEP> 400 <SEP> 0.135 <SEP> 0.045 <tb>

Claims: CLAIMS: 1. A method of providing on a substrate a protected binder layer characterised by coating onto a transparent flexible plastics material film support in this order a binder layer containing particles of less than 10 pm in size and an adhesive layer and adhering said assembly to a substrate. 2. A method according to claim 1, wherein the film support is cellulose acetate, cellulose acetate-butyrate or biaxially oriented polyester, polystyrene or polycarbonate. 3. A method according to claim 1 or 2, wherein the binder is gelatin or a mixture of gelatin and a copolymer latex or is polyvinyl alcohol. 4. A method according to any one of claims 1 to 3, wherein the adhesive layer is applied from a solvent system. 5. A method according to any one of claims 1 to 4, wherein the adhesive is a pressure-sensitive adhesive or a hot-melt adhesive. 6. A method according to claim 5, wherein the pressure-sensitive adhesive is an acrylic adhesive. 7. A method according to any one of claims 1 to 6, wherein the thickness of the binder layer is from 1 to 2000 pm. 8. A method according to any one of claims 1 to 7, wherein the thickness of the adhesive layer is from 0.2 to 100 pm. 9. A method according to any one of claims 1 to 8, wherein the particulate material is a pigment, a U.V. or an I.R. absorber, a finely divided metal or a photochromic glass bead. 10. An assembly used in the method according to any one of claims 1 to 9.

Inventors: BARBER, ROY PATRICK, POSTLE, STEPHEN RODERICK, DR.
Applicants: CIBA-GEIGY AG
Application year: 1983
Main classification: C09J7
IPC codes: C09J7, B32B27, B44C1, B32B23