NOVEL PIGMENT GRINDING VEHICLE

Abstract: A novel quaternary ammonium group-containing mate­ rial which is obtained from reacting a monoepoxide with an amine containing at least one organic group containing an acyclic moiety of from about 8 to 30 carbon atoms is disclosed. The quaternary ammonium group-containing materials are useful as pigment grinding vehicles and in the formulation of pigment paste, particularly pigment paste with high pigment loadings. When formulated in cationic electrodepositable compositions, the pigment grinding ve­ hicles provide for cured electrodeposited coatings of ex­ cellent corrosion resistance, particularly over untreated and oily steel.

Description: Background of the invention Field of the invention The present invention relates to a composition of matter useful as a pigment grinding vehicle and to pigment pastes formulated with such pigment grinding vehicles. Brief description of the prior art In the formation of paints and especially electrodepositable paints, an important factor is the introduction of pigments into the paint. Pigments are typically ground with a grinding vehicle to form a pigment paste. The resultant paste is then combined with the film forming resin and optional ingredients to form the paint, giving the paint the proper color, or opacity, and application or film properties. US-A 3 468 816 relates to the purification of an impure quaternary ammonium salt by reaction with an epoxide. The impure quaternary salt which comprises unreacted amine and amine salt is obtained by reacting an amine with an epoxide-containing compound. A great number of various amines and various epoxide-containing compounds is described as reactants, but the specific amines used for the preparation of the quaternary ammonium group compound of this invention are not disclosed. The quaternary ammonium salts described herein are mainly useful as antistatic agents. US-A 3 223 718 refers to fatty acid-hydroxyethyl-quaternary ammonium compounds and to their use as textile softeners. The quaternary ammonium compounds are prepared by the reaction of a salt of a fatty acid and a tertiary fatty amine with ethylene oxide. US-A 3 936 405 shows quaternary onium, in particular ammonium, salt group containing epoxy resins, which are useful as grinding media. Such resins comprising ammonium groups are obtained by the reaction of an epoxy compound, having preferably an epoxy equivalence greater than 1.0 and a primary, secondary or tertiary amine. As amine reactants various, preferably lower alkyl and lower alkylhyoroxyalkyl amines are suggested. Such quaternary ammonium salt group containing epoxy resins are usually used as pigment vehicle in a pigment binder ratio of about 4:1 (see Example XI). A problem with many pastes used for electrodeposition is the relatively low ratio of pigment to grinding vehicle which can be used. In cationic electrodepositable paints, pigment to grinding vehicle weight ratios are typically 5 to 1 or less. Pastes with higher ratios are not stable. Also, many pigment grinding vehicles do not contribute to and many actually detract from some of the desirable properties of the resultant coating, particularly the property of corrosion resistance. In accordance with the foregoing, the present invention encompasses a quaternary ammonium group-containing material which is obtained from reacting (1) a monoepoxide, and (2) an amine under conditions sufficient to form the quaternary ammonium group, which is characterized in that (1) the monoepoxide is a glycidyl ether or ester containing an acyclic group of from 4 to 24 carbon atoms and (2) the amine is an amine containing at least one lower alkyl group of from 1 to 4 carbon atoms and at least one organic group, which is an acyclic moiety of from 8 to 30 carbon atoms. The instant composition of matter has been found to be useful as a pigment grinding vehicle. Accordingly, the present invention encompasses a pigment paste comprising the instant composition of matter as a pigment grinding vehicle, and a pigment or pigments dispersed therewith. While these pastes can be useful in inks and many types of coatings, they are particularly useful in cationic electrodeposition compositions. The monoepoxides useful herein are glycidyl ethers or esters of acids or alcohols containing an acyclic group of from 4 to 24 carbon atoms. Typical examples of acids and alcohols include the saturated straight chain and branched chain series of fatty alcohols and acids as well as ethylenically unsaturated species and mixtures thereof, including octanoic or 2-ethyl-hexanoic acid at the lower end proceeding to lauric, palmitic, stearic etc., at the upper end of the group. Highly branched tertiary carboxylic acid mixtures such as Shell's Versatic 911 acids are particularly useful herein. Fatty alcohols of equivalent chain length are used for the preparation of the glycidyl ethers. The amines useful herein are preferably tertiary amines and are those which are capable of reacting with and opening the epoxide moiety in the presence of acid and/or water and contain at least one lower alkyl group of from 1 to 4 carbon atoms, preferably methyl, and at least one organic group which is an acyclic moiety of from about 8 to 30, preferably 12 to 18 carbon atoms. Preferably, two of the groups are methyl and the other one is an organic group is an acyclic moiety of from about 8 to 30, preferably 12 to 18 carbon atoms. The term "organicc group" as used herein is intended to encompass saturated and unsaturated groups, as well as substituted and unsubstituted hydrocarbyl groups, provided that the substituent does not adversely affect the reaction of the tertiary amine or the performance of the instant compositions derived therefrom. Examples of substituents would be hydroxy groups and alkoxy groups. Also, the acyclic group can contain moieties in the chain such as ester and ether groups. Examples of the tertiary amines are those represented as: wherein R₁, R₂ and R₃ are alkyl groups of which at least one group contains, each independently, from about 8 to 30 carbon atoms, and at least one group is a lower alkyl containing from 1 to 4 carbon atoms, preferably methyl. Preferably, one of the alkyl group is an acyclic moiety containing from about 8 to 30, and more preferably from about 12 to 18 carbon atoms, and two of the groups are lower alkyl containing from 1 to 4 carbon atoms, preferably methyl. Illustrative examples of the useful tertiary amines are N-octadecyldimethylamine, N-tetradecyldimethylamine, N-dodecyldimethylamine, N-decyldimethylamine, N-nonyldimethylamine, and N-octyldimethylamine. It is expected that heterocyclic amines in accordance with the above description will be useful herein. In reacting the amine with the monoepoxide, usually a stoichiometric amount or an excess of epoxy is used. A stoichiometric excess of amine can be used, but is not preferred. With tertiary amines, the monoepoxide and tertiary amine are reacted by mixing the two together, preferably in the presence of a controlled amount of water. The amount of water employed should be that amount of water which allows for smooth reaction of epoxy groups but not sufficient to cause extremely slow or no reaction. Typically, the water is employed on the basis of about 1.0 to about 16, preferably 2 to 10 moles of water per equivalent of amine nitrogen. Reaction temperature may be varied between the lowest temperature at which reaction reasonably proceeds, for example, room temperature, or in the usual case, slightly above ordinary room temperature, to a maximum temperature of about 120°C. Obviously, for lower molecular weight alkylene oxides such as ethylene and propylene oxide which have high vapor pressures at room temperature, lower reaction temperatures should be used, and, if desired, the reaction could be conducted under pressure to insure complete reaction. With higher molecular weight epoxides such as butyl glycidyl ether, or the glycidyl ester of versatic acid, higher reaction temperatures can be used. The reaction may be conducted in the presence of a solvent, if desired. If a solvent is employed, preferably it is capable of being used in the ultimate composition which is formed. For example, alcohols, ketones and glycol ethers may be used. The reaction of the tertiary amine and the monoepoxide is usually conducted in the presence of acid and/or water to form the quaternary ammonium salt or hydroxide. Preferably, reaction is conducted in the presence of acid. Reaction can be conducted by first neutralizing the tertiary amine with acid to form the tertiary amine salt followed by reaction with the epoxide. Alternately, the epoxide, tertiary amine and acid can be reacted simultaneously or the amine and epoxide can be first reacted followed by acidification of the reaction product. Suitable acids are organic or inorganic acids having a pKa less than 6. Preferably, the acid is water-soluble and it is organic. Examples of acids include formic acid, acetic acid, phosphoric acid or the like. To form the quaternary ammonium base group, the use of a tertiary amine is preferred. However, quaternary ammonium base group-containing resins can be prepared with primary and secondary amines. This can be accomplished by first reacting the primary or secondary amine with a monoepoxide. Reaction is continued until a tertiary amine is formed. Further, reaction with unreacted epoxy which may be from the original monoepoxide or from additionally added epoxy material is continued to form the quaternary ammonium base. Besides quaternizing with additionally added epoxy material, alkylating agents such as dimethylsulfate and methyl iodide can be used, but their use is less preferred, particularly in preparing electrodeposition compositions. The compositions of this invention have been found to be very effective as pigment grinding vehicles. The grinding vehicles are used to prepare pigment pastes containing one or more pigments which are ground with the grinding vehicle. The pigment pastes are prepared by grinding or dispersing the pigment into the grinding vehicle in a manner well known in the art. The pigment paste comprises as essential ingredients the quaternary ammonium pigment grinding vehicle prepared as described above and at least one pigment; however, the paste may, in addition; contain optional ingredients such as plasticizers, wetting agents, surfactants or defoamers. Grinding is usually accomplished by the use of ball mills, sand mills, Cowles dissolvers, continuous attritors and the like until the pigment has been reduced to the desired size, preferably has been wet by and dispersed by the grinding vehicle. After the grinding, the particle size of the pigment is generally in the range of 10 microns or less. Preferably, grinding is conducted in an aqueous dispersion of the vehicle. The amount of water present in the aqueous grind should be sufficient to produce a continuous aqueous phase. The aqueous grind usually contains about 30-70 percent total solids. The use of more water merely reduced the effective capacity of the mill and, while less water can be employed, higher resultant viscosity may create problems in certain instances. One of the advantages of the pigment grinding vehicles of the present invention is their ability to be formulated into paste with high pigment to grinding vehicle weight ratios. Depending upon the pigment to be dispersed, typical weight ratios of at least 10 to 1, preferably higher, that is, 15 to 40: 1, can be attained without the paste settling and separating, for example, when stored for 7 days at 120°F. (49°C.). Pigment paste with lower pigment grinding vehicle weight ratios, that is, as low as 1 to 1, can, of course, be prepared. Pigments which may be employed in the practice of the invention are pigments well known in the art. Generally, titanium dioxide is the sole or chief white pigment; other white pigments an/or extender pigments including antimony oxide, zinc oxide, basic lead carbonate, basic lead sulfate, barium carbonate, China clay, calcium carbonate, aluminum silicate, silica, magnesium carbonate, magnesium silicate, among others, may be used. Colored pigments may also be employed, for example, cadmium yellow, cadmium red, carbon black, phthalocyanine blue, chrome yellow, toluidine red, hydrated iron oxide, among others. The pigment paste can be combined with a film forming resin to form a paint. The film forming resin can be a cationic resin known in the art for electrodeposition. These resins are well known in the art and need not be described in detail. Examples of suitable resins include tertiary amine salt-containing resins such as those described in U.S. Patent No. 4,148,772 assigned to PPG Industries, inc., the assignee of the present invention, and quaternary ammonium salt-containing resins such as those described in U.S. Patent No. 3,839,252 to Bosso et al. The portions of these references which describe suitable electrodepositable resins for cationic electrodeposition are hereby incorporated by reference. Enough of the pigment paste is used so that the final electrodeposition composition (electrodepositable resin plus pigment paste) has the properties required for electrodeposition. In most instances, the final electrodepositable composition has a pigment-to-binder (electrodepositable resin plus pigment dispersant) ratio of between about 0.05 to about 0.6. For electrodeposition, a bath containing about 5-25 percent by weight solids, that is, pigment plus resinous vehicle, is usually employed. This aqueous composition is then placed in contact with an electrically conductive anode and an electrically conductive cathode in an electric circuit. While in contact with the bath containing the coating composition, an adherent film of the coating composition is deposited on the cathode. The conditions under which the electrodeposition is carried out are, in general, similar to those used in electrodeposition of other types of coatings. The applied voltage may be varied greatly and can be, for example, as low as one volt or as high as several thousand volts, although typically between 50 volts and 500 volts are usually employed. The current density is usually between about 0.25 ampere and 15 amperes per square foot and tends to decrease during electrodeposition. The method of the invention is applicable to the coating of any conductive substrate and especially metal, such as steel, aluminum, copper and the like. After deposition, the coating is cured at elevated temperatures by any convenient method, such as in baking ovens or with banks of infrared heat lamps. Curing temperatures of at least 100°C, and usually 125°C to 185°C for at least 10 minutes and usually for about 10 to 30 minutes are employed. One of the advantages of the pigment grinding vehicles of the present invention is the excellent corrosion resistance they impart to cationic electrodeposited coatings, over untreated steel or oily steel substrates when the coatings are cured at relatively low temperatures, i.e., 175°C and below, typically 160-175°C. Illustrating the invention are the following examples, which are not to be construed as limiting the invention to their details. All parts and percentages in the examples, as well as throughout this specification, are by weight unless otherwise specifed. Example I This example illustrates the instant composition of matter and the method of preparing same. The composition of matter was prepared by heating the ARMEEN DM12D, butyl glycidyl ether and 2-butoxyethanol in a properly equipped reaction vessel to a temperature of 45°C., followed by adding a solution of the lactic acid and the deionized water. There was a resulting exotherm, with the reaction temperature being maintained over the range of 82-95°C., for a period of 1-½ hours. The resultant reaction product was cooled and stored. Example II This example illustrates the instant composition of matter and its use as a pigment grinding vehicle, the methods of preparing and using same. The ARMEEN DM18D, CARDURA E and 2-butoxyethanol were heated to a temperature of 50°C., followed by adding the acetic acid and the deionized water. There was a resulting exotherm, with the reaction temperature being maintained over the range of 82-95°C., over a period of 1-½ hours. The resultant reaction product was cooled and stored. A pigment paste using the above-described reaction product as a grinding vehicle was prepared as follows: The grinding vehicle was blended with the above pigments and the deionized water to form a slurry which was ground in a Jiffy mill for 2 hours to a Hegman 7⁺ grind. The pigment-to-binder ratio was 15:1. A cationic paint comprising a blend of the above pigment paste and an electrodepositable resinous film-forming composition was prepared as follows. The electrodepositable resinous film-forming composition was prepared with the following: The EPON 829, PCP-0200 and xylene were charged to a reaction vessel and heated with a nitrogen sparge to 210°C. The reaction was held at reflux for about 1/2 hour to remove water. The reaction mixture was cooled to 150°C. and the bisphenol A and 1.6 parts of the benzyldimethylamine (catalyst) added. The reaction mixture was heated to 150-190°C. and held at this temperature for about 1-1/2 hours and then cooled to 130°C. The remaining portion of the benzyldimethylamino catalyst was added and the reaction mixture held at 130°C. for 2-1/2 hours until a reduced Gardner-Holdt viscosity (50 percent resin solids solution in 2-ethoxyethanol) of P was obtained. The polyurethane crosslinker, the diketimine derivative and the N-methylethanolamine were then added and the temperature of the reaction mixture brought to 110°C. and held at this temperature for 1 hour. The 2-hexoxyethanol was added and the reaction mixture was dispersed in water by adding the reaction mixture to a mixture of the acetic acid, deionized water and the cationic dispersant. This dispersion was diluted to 32 percent solids with deionized water and vacuum stopped to remove organic solvent to give a dispersion having a solids content of 36 percent. The above electrodepositable composition and pigment pastes were blended to form a cationic paint having a pigment-to-binder ratio of 0.2, and a solids content of 20 percent The paint had a conductivity of about 1400 µ mhos/cm after ultrafiltration, and pH after adjustment with acetic acid was 6.2. Steel panels were electrodeposited in the paint at 175 volts for 2 minutes at a paint temperature of 25°C. The coated panels were baked at 170 and 182°C for 20 minutes to obtain hard, glossy and smooth coatings having a film thickness of about 0.4 to 0.7 mils. Comparative Example For comparison, steel panels were electrocoatad with a paint which was similar to the paint of Example II with the exception of the pigment grinding vehicles used. The pigment grinding vehicle is the reaction product of EPON 828 and a tertiary amine containing blocked isocyanate groups. The vehicle is described in Example II of U.S. Patent 4,007,154. The pigments of Example II were ground with this vehicle to form the paste. The comparative paint had a pigment-to-binder ratio of 0.2 and a solids content of 20 percent by weight, the same as the paint of Example II. Steel panels were electrodeposited in the paint at 275 volts for 2 minutes at a paint temperature of 25°C. The coated panels were baked at 170 and 182°C. for 20 minutes to obtain hard, glossy, smooth coatings having a film thickness of about 0.4 to 0.5 mils. Panels coated with the cured paint of Example II were compared with panels coated with the cured paint of the comparative example. The paint of Example II was adjusted with 2-butoxyethanol (36 grams per gallon of paint) to equal the solvent content of the paint of the Comparative Example. The comparison was between corrosion resistance properties. The coated panels coated and baked as described above were scribed with an "X" mark and placed in a salt spray chamber at 100°F. (38°C.) at 100 percent by weight relative humidity atmosphere of 5 percent by weight aqueous sodium chloride solution for a period of 14 days. After 14 days, the creepage from the scribe mark was measured and reported as shown in Table I below. The above specific illustrations and other descriptions herein are not intended to limit the scope of the invention. Instead, it is intended that the invention include all variations and modifications falling within the scope of the appended claims.

Claims: 1. A quaternary ammonium group-containing material which is obtained from reacting (1) a monoepoxide, and (2) an amine under conditions sufficient to form the quaternary ammonium group, characterized in that (1) the monoepoxide is a glycidyl ether or ester containing an acyclic group from 4 to 24 carbon atoms and (2) the amine is an amine containing at leasts one lower alkyl group of from 1 to 4 carbon atoms and at least one organic group, which is an acyclic moiety of from 8 to 30 carbon atoms. 2. The quaternary ammonium group-containing material of Claim 1, wherein the fatty glycidyl ester is a glycidyl ester of versatic acid. 3. The quaternary ammonium group-containing material of Claim 1, wherein the amine is of the structure wherein R₁, R₂ and R₃ are alkyl groups of which at least one group is a lower alkyl group of from 1 to 4 carbon atoms and at least one group is an acyclic moiety of from about 8 to 30 carbon atoms and at least one group is methyl. 4. The quaternary ammonium group-containing material of Claim 1, containing at least two alkyl groups of 1 to 4 carbon atoms. 5. The quaternary ammonium group-containing material of Claims 3 or 4 wherein two groups are methyl. 6. The quaternary ammonium group-containing material of Claim 4, wherein the amine is N-octadecyldimethylamine. 7. A pigment grinding vehicle comprising the quaternary ammonium group-containing materials of any of Claims 1 to 6 which is at least partially acid-neutralized. 8. A pigment paste comprising (A) the grinding vehicle as recited in Claim 7, and (B) a pigment dispersed with (A). 9. A pigment paste of Claim 8, wherein the weight ratio of (B) to (A) is at least 10:1.

Inventors: JERABEK, ROBERT DAVID, JOHNSON, MARK WILLIAM, KOREN, JEFFREY
Applicants: PPG INDUSTRIES, INC.
Application year: 1983
Main classification: C07C217
IPC codes: C09C3, C09D11, C07C217, C07C213, C09D5, C09D17, C07C67