METHOD OF PREPARING HIGH SILICA ZEOLITES WITH CONTROL OF ZEOLITE MORPHOLOGY

Abstract: Process for crystallizing high silica zeolites, by control of the pH so as to obtain zeolitic compositions of a varying morphology depending on the final pH of the reaction medium.

Description: METHOD OF PREPARING HIGH SILICA ZEOLITES WITH CONTROL OF ZEOLITE MORPHOLOGY This invention is concerned with the crystallization of high silica zeolites and, more particularly, is concerned with the preparation of high silica zeolites having a silica-to-alumina ratio of greater than 70, up to and approaching infinity, by control of the reaction medium pH so as to obtain zeolitic compositions of a varying morphology depending on the final pH of the reaction medium. High silica zeolites are extremely well known in the art and have been the subject of much attention in both the patent and technical literature. It has now been discovered that the morphology of the crystals produced from a forming solution varies depending upon the final pH of the reaction medium. As is well known in the art of the synthesis of zeolites, it is extremely difficult to control the pH of the zeolite forming solution and, in fact, it is extremely difficult even to measure the pH during crystallization since crystallization is usually carried out in closed vessels under autogeneous pressure such that exact measurements are not practical. It is known in the art that there is a certain pH range over which ZSM-5 type zeolites can be prepared and, in this connection, U.S. 4,061,724 discloses at column 3 a pH range of 10-14. However, this patent does not teach that the morphology of the resulting crystals is dependent on the pH of the reaction medium. It is also known that the pH is difficult to control and that it varies during the course of crystallization. This invention relates to an improved process for carrying out the crystallization of zeolites, and especially high silica ZSM-5 type zeolites, using the same reactants as have previously been described in various patents and technical articles; but carrying out the crystallization in the presence of a buffer such that the pH of the reaction mixture is maintained within the range of 9.5 to 12. In this manner, the morphology of the zeolite products produced can be controlled depending upon whether a low, intermediate, or high final reaction mixture pH is utilized. It has long been recognized in the synthesis of various crystalline aluminosilicates of the low silica type that complexing agents such as phosphates, arsenates, tartrates, citrates, ethylenediaminetetraacetate, etc. also can act as a buffer. The use of these materials has been primarily directed to those situations where it was desired to increase the silica-to-alumina ratio of the zeolite by complexing the alumina. Thus, procedures of this type are disclosed in U.S. Patent 3,886,801; U.S. Patent 4,204,869; as well as in an article entitled "Influence of Phosphate and Other Complexing Agents on the Crystallization of Zeolites," appearing in Molecular Sieves, Soc. of Chem. Industry, London, pp. 85, et. seq. (1967). All of the above three publications have for a common goal the use of a material which complexes the aluminum such that a zeolitic product is obtained which has a higher silica-to-alumina ratio than that which would normally be obtained from the same reaction medium in the absence of such complexing agents. As indicated earlier, certain of the complexing agents are also buffers, but they are used in amounts such that their primary objective is to complex all or a portion of the aluminum, thereby raising the silica-to-alumina ratio of the resulting zeolite. In the above referred to article, as well as in U.S. Patent 3,386,801, low silica zeolites are dealt with such that the complexing agent added does not complex all the aluminum due to equilibrium considerations. On the other hand, U.S. Patent 4,088,605, which is directed towards high silica-to-alumina ratio zeolites, discloses that the function of the complexing agent is indeed to complex substantially all the available aluminum which, of course, also raises the silica-to-alumina ratio of the final crystalline product. References such as U.S. Patent 3,949,059 teach the use of buffers in the crystallization of a low silica zeolite. The novel process of this invention is not concerned with the use of complexing agents which may additionally be buffers in amounts such that they complex with aluminum and raise the silica-to-alumina ratio of the zeolitic product nor is the novel process herein concerned with low silica zeolites. In other words, in the novel process of this invention, a buffer is used in an amount such that the silica-to-alumina ratio of the product is substantially unaffected, i.e., it would have the same high silica-to-alumina ratio whether or not a buffer were used. The novel process of this invention is based on the discovery that the pH of the reaction mixture is of paramount importance in establishing the morphology of the high silica crystalline zeolite products, preferably of the ZSM-5 type. It has been discovered that twinned short prismatic ZSM-5 crystals frequently with near spherulitic morphology can be obtained when final pH values of the reaction mixture are above 12 and up to 12.5. On the other hand, if the final pH is in the range of 10-10.5, rod-type ZSM-5 can be crystallized. An intermediate type morphology was found in the pH range of 11-12. Thus, depending on what type of morphology is desired with regard to the ZSM-5 type zeolites, the final pH should be controlled within the general ranges above set forth. As has heretofore been stated, it is well known in the art that the pH of a reaction mixture in zeolite synthesis cannot be carefully controlled and that pH does vary over fairly wide ranges during the steps of gel preparation, aging, and during the course of crystallization. The novel process of this invention minimizes the variation in pH by using a buffer which would effectively control the pH to any desired value within the ranges above set forth, thereby greatly facilitating the crystallization of a zeolite of a particular morphology. A particularly preferred embodiment of this invention resides in controlling the final pH within the range of 10-10.5 in order to obtain ZSM-5 having rod-type morphology. The buffer utilized is not narrowly critical, and any buffer capable of stabilizing the pH in this range at 200to in a pressure vessel can facilitate crystallization of the desired morphology. Typical buffers would include phosphates, tartrates, citrates, oxalates, ethylenediaminetetraacetate, acetate and carbonate. The amount of buffer which is used is determined by many factors, including the particular nature of the buffer itself, as well as the final pH which is desired. In general, though, it can be stated that the buffer has to be used in sufficient amounts such that it does act as a buffer in order to stabilize the pH. In general, it can be stated that the amount of buffer used is such that there is present in the reaction medium 0.1 to about 0.35 equivalents of buffer per mol of silica. Greater amounts of buffer can be used, but the increased salt concentration reduces the rate of crystallization. As has heretofore been stated, the novel process of this invention resides in controlling the pH during crystallization of a high silica zeolite. The method used to control the pH is by the use of a buffer. As has also been indicated, it is difficult to measure the pH during crystallization so that a very effective correlation has been made by measuring the final pH, i.e., the pH after crystallization. It is precisely this final pH which has been correlated with the morphology of the high silica zeolites which are produced. The novel process of this invention is concerned with the synthesis of high silica-containing zeolites, and this expression is intended to define a crystalline structure which has a silica-to-alumina ratio greater than 70 and, more preferably, greater than 500, up to and including those highly siliceous materials where the silica-to-alumina ratio is infinity or as reasonably close to infinity as practically possible. This latter group of highly siliceous materials is exemplified by U.S. Patents 3,941,871; 4,061,724; 4,073,865; 4,104,294; wherein the materials are prepared from reaction solutions which involve no deliberate addition of aluminum. However, trace quantities of aluminum are usually present due to the impurity of the reactants. It is also to be understood that the expression "high silica-containing zeolite'1 also specifically includes those materials which have other metals besides silica and/or alumina associated therewith, such as boron, iron, chromium, etc. Particularly preferred high silica zeolites which can be prepared in accordance with the present invention are those of the ZSM-5 type. ZSM-5 type zeolites are those having a Constraint Index within the approximate range of 1 to 12. ZSM-5 type zeolites are exemplified by ZSM-5, ZSM-ll, ZSM-12, ZSM-35, ZSM-38, and ZSM-48 and other similar materials. U.S. Patent 3,702,886 describes and claims ZSM-5. ZSM-ll is more particularly described in U.S. Patent 3,709,979. ZSM-12 is more particularly described in U.S. Patent 3,832,449. ZSM-35 is more particularly described in U.S. Patent 4,016,245. ZSM-38 is more particularly described in U.S. Patent 4,046,859. ZSM-48 is more particularly described in U.S. Patent 4,375,573. As is set forth in the above-identified U.S. patents, the zeolites of this invention are prepared from a forming solution containing water, a source of quaternary ammonium cations, an alkali metal, silica, with or without added alumina and with or without the presence of additional metals. As is known in the art, the forming solution is held at elevated temperatures and pressures until the crystals are formed and thereafter the zeolite crystals are removed. The novel process of this invention resides in using the exact forming solutions which have previously been taught for the preparation of zeolites such as ZSM-5 and adding therewith a buffering agent so as to have a final pH within the range of 9.5-12.5 depending on the particular crystal morphology which is desired. The following examples will illustrate the novel process of this invention using various buffering agents. In all cases, colloidal silica sol identified as Ludox LS containing 30 weight percent silica was used for crystallizations. The molar ratio of silica to tetrapropylammonium bromide (TPABr) was held nearly constant at 19.8 to 19.9 and that of sodium hydroxide to TPABr was held constant at 3.05. Percent crystallinity is based on X-ray comparison with a highly crystalline reference sample. Generally, the reaction mixtures were prepared by dissolving tetrapropylammonium bromide, alkali hydroxide and a particular salt, water, and adding (Ludox) silica sol to this solution. All crystallizations were carried out in non-stirred pressure vessels equipped with Teflon liners and heated by immersion in a constant temperature silicone oil bath. Brief Description of the Figures Figures la and lb are scanning electron-micrographs of the product of Examples 3 and 4, respectively. Figures 2a, 2b7 and 2c are scanning electron-micrographs of the product of Examples 6, 7, and 8, respectively. Figure 3 is a scanning electron-micrograph of the product of Example 10. Figures 4a, 4b, and 4c are scanning electron-micrographs of the product of Examples 12, 13, and 14, respectively. Figure 5 is a scanning electron-micrograph of the product of Example 15. Figure 6 is a scanning electron-micrograph of the product of Example 16. Figure 7 is a scanning electron-micrograph of the prdduct of Example 17. Figures 8a and 8b are scanning electron-micrographs of the products of Examples 19 and 20, respectively. Figures 9a, 9b, and 9c are scanning electron-micrographs of the products of Examples 22, 23, and 24, respectively. Figure 10 is a scanning electron-micrograph of the product of Example 25. Figure 11 is a scanning electron-micrograph of the product of Example 27a. Figure 12 is a scanning electron-micrograph of the product of Example 27b. Figure 13 is a scanning electron-micrograph of the product of Example 27c. EXAMPLES 1-4 Crystallization of High Silica ZSM-5 in the Presence of Phosphate As has been indicated previously, phosphate has been known to complex aluminum and its complexing and buffering properties cause crystallization of zeolites with higher silica-to-alumina ratios than obtained from a similar phosphate-free reaction medium. The reaction mixture of Example 1 was prepared using 4.2 mols of (NH4)2HPO4 per mol of tetrapropylammonium bromide (TPABr) in an at attempt to complex alumina impurities and buffer the sodium hydroxide added. The amount of buffer added was equivalent to 0.42 equivalents of HYPO 4 per equivalent of silica. The amount of (NH4)2HP04 was lowered in Examples 2 and 3 to amounts ranging from 0.21 to 0.14 equivalents per mol of silica, respectively. Finally, ammonia was added in Example 4 to obtain an equimolar concentration of (NH4)2HP04 and NH3. The equivalent amount of Hm=4 per mole of silica was 0.14. The reaction mixtures that crystallized completely had the highest pH, the products having practically identical sorption capacities as will be shown in Table 1. EXAMPLES 5-14 Crystallization of Thigh Silica ZSM-5 in the Presence of Tartrate, Citrate and Oxalate The reaction mixtures containing 2.1 mols of ammonium salts of tartaric, citric, and oxalic acid per mol of TPABr crystallized incompletely or not at all (Examples 5, 9 and 11). This amount is equivalent to 0.21 equivalents of tartrate and oxalate (Examples 5 and 11) and 0.32 equivalents of citrate (Example 9) per mol of silica. Common to all three is very low pH of the final solution. When the amount of tartaric acid was reduced, the crystallinity of the products improved. Simultaneously, the crystals became less elongated (see Figure 2). When only half the amount of ammonium citrate was used (Example 10), citrate to TPABr equals 1.05, equivalents of citrate to moles of silica equals 0.16 which is similar to the reaction mixture of Example 6, and again, a good ZSM-5 was obtained. However, in the citrate mixture, both the citric acid and ammonia were decreased, thereby the pH for Figure 2b was higher than that for Figure 3. When the amount of ammonium oxalate was reduced (Examples 12-13), the resulting products were similar to those obtained with tartrate, i.e., see Table 2 and Figure 4. Sodium oxalate, instead of ammonium oxalate, was used in Example 14 resulting in a higher pH and more crystallization of quartz. Results are shown in Table 2. EXAMPLES 15-17 Crystallization of High Silica ZSM-5 in the Presence of Gluconate, Salicylate and EDTA Reaction mixtures were prepared containing 2.1 moles of gluconate or salicylate per mol of TPABr which is equivalent to .105 equivalents of buffer per mol of silica, and these had pH values above 11 attributable to the weaker acids. The gluconate (Example 15) decomposed during crystallization, and the carbon formed was burned off by calcination at 550eC before analytical tests were carried out. The crystals obtained with gluconate are highly twinned (see Figure 5). Less twinning is observed in the product of Example 16 obtained in the presence of salicylic acid (see Figure 6). Crystals similar to those obtained when phosphate was present in the reaction mixtures, i.e., see Figure 1, crystallized in the presence of ethylenediaminetetraacetate (EDTA) (Figures 7a and b). Multiple twinning resulting in rudimentary spherulites can also be seen in Figure 7b. The material has a high crystallinity which is also evident from the high n-hexane and low cyclohexane sorption capacities. See Table 3. EXAMPLES 18-25 Crystallization in the Presence of Acetate and Carbonate Ammonium acetate was used in Examples 18-21. With 4.2 moles of acetate/mole of TPABr which is equivalent to .21 equivalents of buffer per mol of silica, the crystallization was still incomplete after 495 hours. With less ammonium acetate, 3.2 moles/mol of TPABr (0.16 equivalents per mol of SiO2), somewhat more rapid crystallization was observed, although it was still incomplete after lss hours (see Example 19). The scanning electron micrograph shows the same rod-shaped crystals as observed previously from low pH reaction mixtures, e.g., with tartrate (see Example 6, Figure 2a) and oxalate (Example 12, Figure 4a). At 2.1 moles of ammonium acetate/mole of TPABr (.105 equivalents of ammonium acetate per mole of Six20), a well crystallized product was obtained in 65 hours (Example 20). The ratio of width/length of these crystals is considerably increased, and some 900 twinning is observed (see Figure 8b). When the amount of NaOH was reduced (see Example 21), a material similar to that of Example 19 (Figure 8a) was obtained. Ammonium carbonate was used in the remaining examples of Table 4 (Examples 22-25). At 3.2 moles of ammonium carbonate per mole of TPABr (0.16 equivalents of HCO3 per mole of silica), rod-shaped crystals were obtained simultaneously with more stubby and 900 twinned crystals (see Figure 9a). Surface etching, caused by redissolution and beginning recrystallization indicates that the crystallization was completed considerably sooner than after 122 hours when the reaction was terminated. Considerably shorter crystals formed at carbonate/TPABr of 2.1 (Figure 9b) and at 1.05 (Figure 9c)(.105 and .055 equivalents of bicarbonate per mole of silica). Although the latter product (Example 24) had good sorptive properties, beginning redissolution and deposition of quartz crystals caused by the long time at 200 C, is evident in Figure 9c. Very large, highly twinned crystals, about 40 x 70 Angstrom units (10 10m) in size, were obtained when the ratio of NaOH/TPABr was lowered to 2 (see Example 25, Table 4, and Figure 10). The final pH of this reaction mixture was about the same as the initial pH. Results are shown in Table 4. TABLE 1 Example 1 2 3 4 Mol/mol of TPABr (NH4)2HP 4 4.2 2.1 1.4 1.4 NH4OH -- -- -- 1.4 HO 275 275 275 275 Initial pH 9.5 9.9 10.5 10.7 Crystallization Time, Hrs. 128 128 65 65 Temp., oC 200 200 200 200 Final pH 9.4 9.5 10.1 N.A. X-Ray Identification Amor. ZSM-5 ZSM-5 ZSM-5 Cryst. X 80 95 85 Sorption, g/100g Cyclohexane, (2666 Pa) 1.3 0.6 0.6 n,C6H14, (2666 Pa) 7.7 10.7 10.7 H20, (1600 Pa) 1.2 1.4 1.5 Composition of Product Si02, wt. % 89.3 86.6 87.1 A1203, ppm 450 440 480 Na, wt. % 0.02 0.08 0.08 N, wt. % 0.73 0.89 0.82 P, wt. % 0.003 0.01 0.01 Ash, wt. % 91.1 88.8 88.9 SiO2/A1203 (molar) 3374 3346 3085 SEM Fig. la lb TABLE 2 Example 5 6 7 8 9 10 11 12 13 14 Moles/Mole of TPABr Tertaric Acid 2.1 1.58 1.05 0.7 -- -- -- -- -- - Citric Acid -- -- -- -- 2.1 1.05 -- -- -- - (NH4)2C2O4 -- -- -- -- -- -- 2.1 1.59 1.05 - Na2C2O4 -- -- -- -- -- -- -- -- -- 0.7 NH4OH 4.2 4.2 4.2 4.2 6.4 3.2 -- -- -- - H2O 286 286 286 286 267 260 310 310 310 310 Initial pH 9.8 10.4 11.7 12.6 9.2 10.35 9.6 10.0 11.35 13.1 Crystallization Time, Hrs. 168 166 67 91 72* 92 211 165 66 71 Temp., C 200 200 200 200 200 200 200 200 200 200 Final pH 8.7 10.13 10.67 11.06 9.38 10.16 N.A. 9.83 10.76 11.74 X-Ray Identification Amor. ZSM-5 ZSM-5 ZSM-5+ ZSM-5+ ZSM-5 Amor. ZSM-5 ZSM-5 ZSM-5+ some Amor. +ZSM-5 some Quartz Quartz Cryst. % 115 135 145 55 110 35 95 135 100 Sorption, g/100g Cyclohexane, (2666 Pa) 1.4 0.5 1.6 2.4 0.6 1.5 0.4 2.6 n-C6H14, (2666 Pa) 9.5 10.5 10.8 4.7 10.6 8.9 10.9 11.2 H2O, (1600 Pa) 0.7 2.9 5.1 1.9 1.3 0.7 2.8 6.4 Composition of Product SiO2, wt. % 86.5 84.4 86.1 86.7 87.0 83.5 85.9 Al2O3, ppm 430 450 470 460 460 430 500 Na, wt. % 0.03 0.35 0.59 0.06 0.02 0.33 0.84 N, wt. % 0.82 0.87 0.78 0.92 0.79 0.85 0.76 Ash, wt. % 89.1 88.1 88.7 89.1 89.9 87.9 86.9 SiO2/Al2O3 (molar) 3420 3188 3114 3204 3215 3301 2921 SEM Fig. 2a 2b 2c 3 4a 4b 4c * Followed by an additional heating at 180 C for 139 hours. TABLE 3 Example 15 16 17 Moles/Mole of TPABr Gluconic Acid 2.1 Salicylic Acid -- 2.1 - EDTA 0.7 NH40H 2.1 2.1 1.4 HO 280 257 279 Initial pH 11.6 11.4 10.3 Crystallization Time, Hrs. 67 48 67 Temp., C 200 200 200 Final pH 11.64 11.42 10 X-Ray Identification ZSM-5 ZSM-5 ZSM-5 Cryst. % 75 100 105 Sorption, g/100g Cyclohexane, (2666 Pa) 0.5 0.4 0.3 n-C6H14, (2666 Pa) 11.4 11.1 11.0 H2O, (1600 Pa) 2.0 2.4 1.6 Composition of Product SiO2, wt. % 96.7 86.8 86.8 Al2O3, ppm 490 760 580 Na, wt. % 0.24 0.34 0.10 N, wt. % -- 0.81 . 0.69 Ash, wt. % 100* 89.2 88.8 SiO2/A1203, molar 3355 1942 2544 SEM Fig. 5 6 7 * calcined form TABLE 4 Exploratory Crystallizations in the Presence of Anions Constants: SiO2/TPABr = 19.9; Temperature - 200 C Example 18 19 20 21 22 23 24 25 Moles/Mole of TPABr NH4-Acetate 4.2 3.2 2.1 2.2 -- -- -- - (NH4)2CO3 -- -- -- -- 3.2 2.1 1.05 1.1 NaOH 3.1 3.1 3.1 2.0 3.1 3.1 3.1 2.0 H2O 275 275 275 277 275 275 275 277 Initial pH 9.80 10.33 11.60 9.92 9.67 9.86 11.07 9.98 Crystallization Time, Hrs. 4.95 163 65 662 122 64 165 72 Final pH 8.78 9.75 10.61 9.73 10.16 10.35 10.44 9.94 X-Ray Cryst., % (1) 90 95 140 100 110 155 130 85 Sorption, g/100g Cyclohexane, (2666 Pa) 0.7 2.4 0.6 3.1 1.5 0.7 2.3 0.8 n-Hexane, (2666 Pa) 8.4 9.4 10.7 9.7 11.1 10.9 11.4 10.8 Water, (1600 Pa) 0.2 0.8 2.8 0.2 1.9 3.5 4.1 0.1 Composition of Product SiO2, wt. % N.A 89.72(2) 86.3 87.7 84.1 83.4 86.52(2) 84.7 Al2O3, ppm N.A 430 445 460 440 495 430 480 Na, wt. % N.A 0.05 0.37 0.05 0.24 0.48 0.57 0.30 N, wt. % N.A 0.81 0.89 0.87 0.82 1.18 0.75 0.81 Ash, wt. % N.A 89.8 88.6 89.0 87.8 86.5 87.3 88.4 SiO2/Al2O3, molar N.A 3546 3297 3241 3249 2864 3420 3000 SEM, Fig. -- 8a 8b -- 9a 9b 9c 10 (1) All products were ZSM-5, no crystalline impurities were detected by x-ray diffraction (2) By difference The following examples demonstrate that the procedure can be applied to the crystallization of other zeolites as well. The pH at which buffering has to be accomplished, however, will change from zeolite to zeolite. EXAMPLE 26 Preparation of ZSM-11 A reaction mixture was prepared having the composition listed in the following table. Crystallization conditions, sorption, a product analysis are also listed. Mol/Mol ThASr (tetrabutylammonium bromide) (NH4)2HPO4 0.74 NH OH 0.74 NaOH 3.9 Sio2 (as silica sol, 30%) 19.8 H20 275 Initial pH 12.89 Crystallization Time, Hrs. 140 Temperature, C 140 Final pH 11.30 X-Ray Identification ZSM-ll Crystallinity, % (rel. to reference sample) 145 Sorption, g/100g Cyclohexane, (2666 Pa) 2.5 n-Hexane, (2666 Pa) 8.6 Water, (1600 Pa) 2.5 Composition of Product SiO2, wt. % 81.6 Al2, ppm 410 Na, wt. % 1.2 N, wt. % 0.69 P, wt. % 0.01 Ash, wt. % 83.3 SiO2/Al2O3, molar 3383 EXAMPLE 27 Preparation of ZSM-12 A reaction mixture was prepared having the composition listed in the following table. Crystallization conditions, sorption, and product analysis are also listed. Mol/Mol MTEAC1 (methyltriethylammonium chloride) a b c NA2HPO4 0.27 -- - (COOH)2 -- 0.14 - EDTA -- -- 0.06 NaOH 0.42 0.50 0.50 SiO2 (as silica sol, 30%) 1.63 1.63 1.63 H20 106 106 106 Inital pH 12.52 13.00 12.97 Crystallization Time, hrs. 185 162 228 Temperature, oc 160 160 160 Final pH 11.41 11.31 11.41 X-Ray Identification ZSM-12 ZSM-12 ZSM-12 Crystallinity, % 80 110 110 Soprtion, g/lOOq Cyclohexane, (2666 Pa) 7.3 7.8 8.1 n-Hexane, (2666 Pa) 7.8 6.5 6.5 water, (1600 Pa) 4.2 5.0 2.1 Chemical Composition SiO2, wt. % 88.5 89.3 89.0 Al2O3, ppm 580 595 495 NO, wt. % 0.50 0.26 0.24 N, wt. % 0.91 0.84 1.05 Ash, wt. % 90.6 91.2 91.3 SiO2/A1203, Molar 2594 2551 3058 SEM Fig. 11 12 13

Claims: CLAIMS: 1. A process for producing high silica zeolites with control of the morphology of the zeolites so produced, which process comprises A) forming a reaction mixture containing a source of alkali metal oxide, a source of silica, a quaternary ammonium ion, water and a buffer capable of controlling the final pH of the reaction mixture to a value within the range of 9.5 to 12; and B) holding said reaction mixture at elevated temperature and pressure until zeolite crystals are formed. 2. The process of Claim 1 wherein the high silica zeolite is a ZSM-5 type zeolite. 3. The process of Claim 1 or Claim 2 wherein the final pH is controlled within a range of 12-12.5 so as to obtain near spherulitic morphology. 4. The process of Claim 1 or Claim 2 wherein the final pH is controlled within a range of 10-10.5 in order to obtain rod-shaped ZSM-5 type crystals. 5. The process of any of Claims 1 to 4 wherein the buffer is selected from the group consisting of phosphate, tartrate, citrate, oxalate, ethylenediaminetetraacetate, acetate and carbonate. 6. The process of any of Claims 2 to 5 wherein the zeolite is ZSM-5. 7. The process of any of Claims 2 to 5 wherein the zeolite is ZSM-12.

Inventors: KUEHL, GUENTER HINRICH
Applicants: MOBIL OIL CORPORATION
Application year: 1983
Main classification: C01B33
IPC codes: C01B39, B01J29, C01B37