METHOD AND ARRANGEMENT FOR UNDERWATER ARC WELDING

Abstract: A method and an arrangement for such underwater arc welding in which the welding electrode (32) is placed onto the zone (22) to be welded in lying position, the said electrode being covered with a shield structure (33) and ignited so that, when the burning goes on, it produces the desired weld at the zone (22) to be welded. According to the invention, a mantel (23) is used as the shield structure, which mantle comprises an inner burning layer (33) made of a readily burning, preferably resilient material, by means of which the electrode (32) is covered, and an outer protective layer (23), preferably made of a flexible material, by means of which the burning layer (33) is covered, and fastening means (34), by which the mantel (23) is fixed firmly and tightly in position. The fire gases produced during the burning of the electrode (32) and of the burning layer (33) prevent penetration of water to the electrode (32).

Description: Method and arrangement for underwater arc welding The present invention relates to a method in accordance with claim 1 , which method is applicable to 5 -underwater arc welding. The method is suitable only for the so-called Elin welding, wherein the electrode is not burned in the normal way as perpendicular to the object to be welded, but -the electrode is placed lying on the parent 10 material and is melted in this position like a fuse without participation of the welding operator in the process. The invention also relates to an arrangement to be used for carrying out the method. 15 In prior art, a so-called "fire-cracker" ethod is known, in which one or several thick-coated electrodes placed in a groove are covered with a copper rail which accommodates one or several furrows for the electrodes. Into the space produced, gas is 20 passed, usually air, whereby the water in the space is displaced. For igniting the light arc, either a thin wire fuse or a metal foil is used, upon whose destruc- tion the arc of light starts burning between the elec¬ trodes and the parent material. * The maximum length of 25.• the electrodes when welding on the ground is about 1 metre. It has, however, been noticed that in water it is possible to use twice as long electrodes. It is, however, a drawback of this method that an external pressure-gas source, is required in order to eliminate 30 the water. This is inconvenient, especially when the welding is performed in deep waters. Moreover, it is - difficult to make and to install the copper rail on several welding objects which are not straight or even, such as pipe joints. 5 From the U.S. Patent No. 4,069,408, a method is known according to which the area to be welded is covered by means of a box-shaped structure that contains various pastes and powders and whose top portion is provided with a groove along which the vertically positioned welding electrode can be shifted. It is a drawback of this method that, as the welding area is out of sight, the welding must be performed "blindfold" The object of the present invention is to eliminate the drawbacks present in the prior art technology and to provide a more practical method and arrangement of a novel type for underwater arc welding. Another' objective of use of the invention is to provide a dry space within the area of the arc - and to prevent access of water onto the slag and weld melt about to be cooled. The • invention is based on the idea that by fitting both the electrode and the material covering the electrode tightly onto the object to be welded, which said material generates a gas while the arc is burning, the water, can be displaced automatically. In the method in accordance with the present invention, the object to be welded is first covered, over the entire distance to be welded, with a water- repellent semi-solid material, which is in ,the following called sealing material. It must be spread over an area as wide as possible and with a thickness of at least 1 cm. Hereupon the welding electrode is pressed into the sealing material so that ft is parallel to the parent material to be welded and to the intended weld seam. After the welding electrode has been covered completely in the ' water-repellent sealing material, a resilient heat insulation board of solid material is pressed onto the material so tightly that it presses the electrode against the parent material. The heat insulation board is almost equally long as the electrode to be welded and wide enough so that the sealing mate- rial remains covered by the insulation board wi-th-the exception of any excessive sealing material extruded from the sides of the insulation material. The initial. end of the electrode as well as its final end are allowed to remain visible for the purpose of ignition so that the electrode holder can be attached to the electrode. Hereupon the electrode can be ignited by instantaneously short-circuiting its initial end, e.g., by means of a carbon rod. When the arc is ignited, a tunnel is produced in the heat ' insulation when the electrode burns. Since the fire gases produced escape along ' this tunnel, water cannot follow the arc while the arc proceeds inside the heat insulation and the sealing material. The gas pressure produced by the fire gases in the tunnel is sufficient to keep the water out as long as the electrode is burning. Shortly before the electrode 'has -burnt out, the initial end of the tunnel is covered with a large piece of sealing mate¬ rial in order that the water could not flow into the tunnel after burning out of the electrode and cool- the weld seam produced. Nor must the final end of the electrode be burnt so far that the tunnel is burnt through at that end. This tunnel may also burn through at the top unless the heat insulation is thick enough. The heat insulation board may be removed after about 15 seconds-from the end of the welding. Since the weld seam now produced was all the time isolated from water, •' its properties correspond to the properties of welds produced in a dry chamber. More specifically, the method in accordance with the present invention is , , characterized by what is stated in the carac erizing part of claim 1. On the other hand, the arrangement in accord¬ ance with the invention is characterized by what is stated in the characterizing part of claim 7. By means of the invention, remarkable advan¬ tages are achieved. Thus, the method according to the invention eliminates the water from the area of arc during the welding and thereby reduces the high rate of cooling of the weld, which has constituted a drawback in conventional methods of submerged welding. As an additional advantage, as compared with the dry-chamber methods, may be considered that the fire gases produced from the electrode, from the heat insulation and from the sealing material are very hot, which is advantageous in view of the requirement of lowering the rate of cooling of the weld melt. The invention will be examined below in more detail with the aid of the exemplifying embodiments in accordance-with the attached drawings. Figure 1 is an axonometric view of a test sheet to be welded, provided with a V -groove. Figure 2 is an axonometric view of an enclo¬ sure made of foam rubber and open at the bottom. Figure 3L is an axonometric view of a board of insulation material provided with a projecting ridge. Figure 4 is an axonometric sectional view of one welding arrangement in accordance with the invention. Figure 5 is an axonometric view of a second welding arrangement in accordance with the invention. Figure 6 shows a welding electrode to be used in the arrangement shown in Fig. 5. Figure 7 is an axonometric view of a third welding arrangement in accordance with the invention. Figure 8 is a sectional view on an enlarged scale of the welding arrangement shown in Fig. 7. Figure 9 is a sectional view of a weld pro¬ duced by means of the arrangement shown in Fig. 8. Figure 10 is a schematical view of a fourth welding- arrangement *in accordance with the invention. Example 1 The sheet 1 to be welded was of carbon-manga¬ nese steel Fe 52 D of Messrs. Rautaruukki Oy, whose carbon equivalent was 0.40. In the middle of the sheet 1, in the longitudinal direction, a V groove 2 ( =70°, Fig. 1) had been cut. For fill welding of this groove 2, a shield in accordance with the invention was prepared. The outermost part of the shield consists of an enclo¬ sure 3 made of foam rubber and open at the bottom, as • _ shown in Fig. 2. The empty space 4 of 220x75x40.mm remaining inside the enclosure 3 is filled with a resi¬ lient styrofoam sheet 10, which had been provided with a projection 11 fitting into the V groove of the sheet (Fig. 3) . One end wall 7 of the rubber enclosure 3 was, at the bottom edge, provided with a notch-like opening 5 for the removal of the fire gases. In order that the hot gas flows should not gradually burn the opening 5 larger, both ends of the opening 5 were rein¬ forced by means of metal plates 6, whereby it is also possible to adjust the size of the notch 5 by shifting the said plates 6. ■ The end wall 8 at the final end of the rubber enclosure 3 was also protected by a metal plate 9 in order that the light arc and the welding gases should not burn a hole through the end wall 8 at the final end. When the welding was started, the welding rod or electrode 12 was first placed onto the bottom of the V groove 2. Hereupon, a protective board '10 as described above, preferably made of styrofoam, was placed onto the electrode 12. The V-shaped projection 11 of the board 10 was fitted into the V groove 2 of the sheet 1 to be welded. The function of this pro¬ jection 11 was to press the welding electrode 12 tightly to the bottom of of the V groove 2 and to displace any water placed around the electrode 12 as completely as possible. The protective board 10 placed onto the electrode 12 was then pressed tightly against the sheet 1 to be welded. Since the styrofoam board was made of a resilient material, the electrode 12 was pressed slightly into the insulation material, which favoured the elimination of the water around the electrode 12. The compression (arrow h , Fig. 4) was in this case produced by means of a screw press, not shown, and a pressure plate 14. Hereupon the grounding wire was attached to the sheet 1 and the electrode holder to the core wire 1 of the rod 12 coming through the rear end wall 8 of the shield enclosure 3. The initial end of the rod 12 seen in the opening 5 at the other end wall 7 was short-circuited by means of a carbon rod, whereby the welding electrode 12 started burning. The fire gases from the insulation 10, 13 burning around the welding electrode 12 and from the welding electrode 12 itself escaped at a high pressure through the small gas exhaust opening 5,thereby prevent¬ ing the water outside the shield enclosure 3 from following the arc into the enclosure 3. The electrode 12 burnt out slightly before the rear end wall 8 and was then extinguished by itself. After the rod 12 had been extinguished, the gas pressure in the enclosure 3 was reduced rapidly, whereby water started flowing into the enclosure 3 through the gas exhaust opening 5 at ' the initial end. Even though it would be in itself easy to block the gas exhaust opening 5, e.g., by means of modelling wax, this is not necessary in practice, for the temperature of the weld produced has already by now been lowered well below 500°C even at the final end of the weld. Thus, -the effect of the water cooling the weld " no longer has a substantial effect on the diffusion of T the hydrogen in the weld, nor can hardening effects be produced any more. Since there was no water in the proximity while the arc was .burning, the hydrogen con¬ tent in the fire gases did not become high either (the dissociation of water to oxygen and hydrogen within the area of the arc was previously one of the major causes of the high hydrogen concentrations in underwater welds) . On completion of the welding, the screw press was detached and the shield enclosure 3 was removed. It was noticed that the styrofoam board 10 inside the enclosure had burnt almost completely, but the enclosure 3 of foam rubber itself had not suffered damage. The slag that had been produced during welding was easy to remove, and the weld produced was very uniform and well-shaped, which was obviously a result of the steady position of the electrode 12 and of uniform burning ,5 ' which proceeded automatically. After the styrofoam remainders had been removed from the rubber enclosure 3 and a new styrofoam board been installed in.- ' position, the following bead could be welded in the same way as the first.one. As the V groove 2 was being filled, the 10 effective gas exhaust opening 5 was also reduced. This is why the gas exhaust opening 5 was increased by means of the metal plates when the surface beads were being welded. The X-ray picture taken later of the welded 5 sheet 1 showed no porosity, no slag inclusions, and no joint flaws. The other tests taken from the sheet 1, such as the hardness, bending, and falling weight tests, gave values corresponding to those obtained from a reference sheet welded on the ground. 0 Example 2 The butt welding of the pipe 21 took place in a way corresponding to Example 1. The rubber shield 23 was now made so long that it extended around the pipe 1 ' 5 - (Fig. 5) , and the styrofoam sheet 33 was shaped so that it could be pressed tightly around 1 the pipe 1. The outer diameter of the pipe was 150 mm, so that a normal 450 mm long flexible welding,electrode 32 extended around the whole ' pipe 1 (Fig. 6) . ' In order that it 0 should be possible to attach the electrode holder 16 to the final end of the electrode and that it should be possible to short-circuit the initial end of the electrode ;32, a space of about 10 mm had to be left between the initial and final end of the rubber 5 shield 23. In order to facilitate the fastening of the electrode holder 18, the bare core wire portion 35 at the final end of the welding electrode 32 was bent perpendicularly upwards from the face of the pipe 1 (Fig. 6) . The rubber shield 23 and the styrofoam layer 33 inside it were pressed around the pipe 1 by means of .tensioning bands 34 (Fig. 5) of the type used, e.g., in the packaging industry. An ordinary hose clip with screw tensioning is also well suitable for the purpose. Since the welding was now performed in all positions, i.e. "downhand", vertical and "uphand" positions, the current in the electrode 32 was reduced for the vertical and "uphand" positions by about 15 to 20 % as compared with the "downhand" position. In the other respects, the welding took place in accordance with the above Example 1. Example 3 ' Figures 7 to 9 show an alternative welding method as applied to the butt welding of pipes 21. According to the method, pasty material has been fitted into the weld groove 22, e.g.,a material defined in the Finnish Patent Application No. 802244. Onto this material, a welding electrode 32 has been fitted which comprises, a coating 43 made of an elastic material and having a cross-sectional, form following the cross section of the groove 22, as well as a core 42 inside the coating 43, the said core consisting of several wires. Being flexible, such a structure 42, 43 is highly purposeful. Onto the welding electrode 32, a styrofoam layer 3,3 has been applied, and onto this a paste layer 36, which has been spread laterally beyond the outer edges of the groove 22. The paste layer 36 is coated with a resilient coating net 37, which keeps the welding arrangement tightly pressed against the groove 22 by means of magnets 39 or of any other, presses or tapes. After the welding electrode 32 has been ignited in accordance with Examples 1 and 2, the insulation la er 33 forms a hollow cavit 40 durin the ro ress - of burning (Fig. 9) , along which cavity the hot weld gases can flow between the slag layer 44 and the paste layer 36 and further out through the initial end of the weld 41. This hot gas flow prevents rapid cooling of the weld 41 , whereby the hydrogen can escape from the weld 41. By means of this gas flow, ; the tempera¬ ture of the weld 41 can be kept for some time above the so-called Curie point (>725°C) . In the solution shown in Fig. 10, after the pressing of the enclosure against the welding base, the water pressure can no longer affect the pressure pre¬ vailing within the arc zone, because there is a tight rubber border in between within the edge area of the enclosure. ' The- thin elastic plastic film 49 is also pressed against the edges of the enclosure 48 so tightly that the electrode 47 remains dry and isolated from water. The elastic film 49 does not prevent automatic ignition of the electrode 47 and does not affect the burning of the arc or the quality of the weld. The elastic ball 51 hanging lower down yields a slight difference Δp in pressure through the hose 52, in order that, during the installation, the film should not be pressed by the effect of the water pressure and be broken against small holes possibly present in the enclosure 48. r After installation in position, when the valve 45 placed above the water surface in the hose 46 (con¬ nected to the gas exhaust opening earlier) is opened, the normal atmospheric pressure is produced within the arc zone of the enclosure 48, whereby the outer water pressure presses the enclosure tightly against the base, such th-±. a separate pressing by a screw press, magnet, band, etc. is no longer required. The insulation in the enclosure may be made so that it, in stead of air, contains a gas that is at the same time a shield gas for welding. In such a case. the same requirements do no longer have to be imposed on the structure of the coating of the electrode 47 as are necessary when welding is performed in the air.

Claims: WHAT IS CLAIMED IS: 1. Method for underwater arc welding, according to which method - a welding electrode (12, 32) is placed at the zone (2, 22) to be welded in lying position the electrode (12, 32) is covered with -a shield structure (3 to 11, 23, 33 to 39), the electrode (12, 32) is ignited so that it, while the burning goes on, produces the desired weld (41) at the zone (2, 22) to be welded, and - a pressurized gas is allowed to act between the electrode (12, 32) and the shield structure (3 to 11', 23, 33 to 39) so that the surrounding water cannot penetrate to the electrode (12, 32) while the electrode is burning, c h a r a c t e r i z e d in that - a mantle (3, 23) is used as shield structure and comprises an inner burning layer made of a readily burning, preferably resilient material (10, 33), with which the electrode (12, 32) is covered, and an outer protective layer (3, 23, .36) , prefer¬ ably made of a flexible material, with which the burning layer (10, 33) is covered, and fastening •' means (14, 37 to 39) , by means of which the mantle (3, 23) is fixed firmly and tightly in position so that the fire gases produced when the electrode (12, 32) and the burning layer (10, 33) burn prevent access of water to the electrode (12, 32) . 2. Method as claimed in claim 1, c h a r ¬ a c t e r i z e d in that a burning layer (10, 33) is used that has been shaped so as to correspond to the cross section of the zone to be welded, e.g. groove (2, 22) , in such a way that it presses the electrode (12, 32) firmly to its position, while at the same time at least partly filling the space between the electrode (12, 3 and the zone (2, 22) to be welded. 3. Method as claimed in claim 1 , c h a r ¬ a c t e r i z e d in that foam plastic or polystyrene is used as the burning layer (10, 33). 4. Method as claimed in claim 1 , c h a r - -5 a c t e r i z e d in that rubber or foam rubber is used as the protective layer (3) . 5. Method as claimed in claim 1 c h a r ¬ a c t e r i z e d in that a so-called shield paste, e.g. a shield paste in accordance with the Finnish Patent 10 Application No. ' 802244, is used, as the protective layer (36) , which is covered with a resilient cover net (37). keeping the welding arrangement pressed against the groove (22) by means of fastening means, e.g. magnets (39) . 15 6. Method as claimed in claim 1 or 5, c h a r a c t e r i z e d in that a shield * paste layer (15, 35) is fitted between the electrode (12, 32) and the zone (2, 22) to be welded. 7. An arrangement for carrying 20 the method as claimed in claim 1 for underwater arc welding, said arrangement comprising a welding electrode (12, 32) to be applied to the zone (2, 22) to be welded, the side portion of said electrode lying against said zone, and " 25 - a shield structure (3 to 11, 23, -33 to 39), which covers the electrode (12, 32 from the top and from around the zone (2, 22) to be welded, c h a r a c t e.r i z e d in that the shield structure comprises 30 - an inner burning layer (10, 33) made of a readily burning, preferably resilient material, which covers the electrode (12, 32) against the zone [2, 22) to be welded, an outer protective layer (3, 23, 36), preferably 35 made of a flexible material, which covers the burning layer (10,33) from the top and around the zone (2, 22) to be welded, and - fastening means (14, 37 to 39) for fastening the shield structure (3 to 11, 23, 33) above and around the zone (2, 22) to be welded. 8. Arrangement as claimed in claim 7, - c h a r a c t e r i z e d in that the protective layer comprises a box-like structure (3) which is open at the portion to be placed against the zone (2, 22) to be welded and made, e.g., of rubber and at least cine of whose walls (7) is provided with an opening (5) for' removing the fire gases, and the burning layer consists of a board structure (10) the dimensions of which at least approximately correspond to the interior space (4) of the box-like structure (3) and which is made, e.g.,.of foam plastic and provided with ' a projection (11) of a cross section corresponding to the cross section of the zone, e.g., groove (2, 22), to be welded. 9. Arrangement as claimed in claim 7, c h a r a c t e r i z e d in that the burning layer and the protective layer consist of one and the same layer, which is made of a protective paste covered with a resilient cover net (37) , which keeps the welding arrangement compressed against the groove, (22) by means of fastening means, e.g. magnets (39).

Inventors: ASONEN OSMO, ASONEN, OSMO
Applicants: ASONEN OSMO, ASONEN, OSMO
Application year: 1983
Main classification: B23K9
IPC codes: B23K9