PROCESS FOR THE PREPARATION OF AN AROMATIC HYDROCARBON MIXTURE

Abstract: C₂-C₄ paraffins or hydrocarbon mixtures comprising more than 50 %w of C₂-C₄ paraffins are converted into an aromatic hydrocarbon mixture over a catalyst comprising gallium on a carrier and a crystalline metal silicate having a SiO₂/(Y₂O₃ + Ga₂O₃) molar ratio of 10-500 (Y = Al, Fe, Co and/or Cr) and a Ga₂O₃/Y₂O₃ molar ratio lower than 1, and having an X-ray powder diffraction pattern after one hour's calcination in air in which pattern the strongest lines are shown at interplanar spacings d(Å) of 11.2 ± 0.2; 10.0, ± 0.2; 3.84 ± 0.07; 3.72 ± 0.06. The catalyst has been subjected at least once to a two-step treatment comprising a coke-­ deposition and a coke-burn off with an oxygen-containing gas at 350-700°C. The quantity of gallium amounts to 1-10 %w, calculated on the quantity of crystalline metal silicate. The gallium-containing carrier is preferably an amorphous carrier or the crystalline metal silicate.

Description: PROCESS FOR THE PREPARATION OF AN AROMATIC HYDROCARBON MIXTURE The present invention relates to a process for the preparation of an aromatic hydrocarbon mixture, in which one or more paraffins with two, three or four carbon atams per molecule or aliphatic hydrocarbon mixtures consisting more than 50 %w of said paraffins are contacted with a catalyst comprising gallium sup ported on a carrier and a crystalline metal silicate which metal silicate a) has been prepared by crystallization starting from an aqueous mixture which, in addition to the components needed for the synthesis of the silicate, comprises one or more compounds of a trivalent metal Y chosen fram the group formed by alumin ium, iron, cobalt and chromium and, if desired, one or more gallium compounds in such quantities that in the formula which represents the camposition of the silicate expressed in rroles of the oxides, the Sio2/ (Y203 + Ga203) solar ratio is 10-500 and the Ga203/Y203 molar ratio is lower than 1, and b) after one hour's calcination in air at 500 C has an X-ray powder diffraction pattern in which the strongest lines are the four lines mentioned in Table A, TABLE A d( ) 11.1 + 0.2 10.0 i 0.2 3.84 + 0.07 3.72 + 0.06 in which catalyst the quantity of gallium supported on a carrier amounts to 1-10 %w, calculated on the quantity of crystalline metal silicate present in the catalyst and which catalyst has been subjected at least once to a two-step treatment comprising a step in which the catalyst is contacted at a temperature of 350-700 C with a hydrocarbon or a mixture of hydrocarbons until in less than 5 hours 0.1-5 %w of coke has been deposited on the catalyst, followed by a second step in which the coke-loaded catalyst is contacted at a temperature of 350-700 C with an oxygen-containing gas until more than 50 %w of the coke present on the catalyst has been removed. By subjecting the catalysts at least once to the above two-step treatment, their performance in the conversion of said paraffins into aromatics is much improved. The treatment results in a substantial increase of the C5+ selectivity. In addition it leads to enhancement of the activity and H2 selectivity of the catalysts. The H2 selectivity increase represents an advantage since in view of the growing demand for hydrogen for a variety of purposes it is important that in the conversion as much as possible of the hydrogen becomes available as molecular hydrogen and not in the form of hydrogen-rich by-proiucts, such as methane. The liquid hydrocarbon mixtures cbtained in the process according to the invention boil substantially in the gasoline range and have a very high octane number. They are therefore excellently suitable for use as motor gasoline or as mixing components for motor gasolines. A carrier for the gallium that may suitably be used is the crystalline silicate of the special structure described above which silicate is present in the catalysts and onto which silicate the gallium has been deposited, for instance by impregnation or ion exchange. In the catalysts the gallium occurring may be partly or wholly deposited on a conventional carrier, such as silica, the gallium-loaded carrier being present in the catalyst in admixture with a crystalline silicate of the special structure. The quantity of crystalline metal silicate, calculated on the sum of the quantity of crystalline metal silicate present in the catalyst and the quantity of other material used as carrier for the gallium which may be present in the catalyst, is preferably at least 20 Ew. In the process according to the invention the starting material comprises paraffins having two, three or four carbon atans per molecule or an aliphatic hydrocarbon mixture which consists more than 50 tw of said paraffins. The paraffins with two, three or four carbon atoms per molecule which should constitute more than 50 %w of the feed are ethane, propane, n-butane and isobutane. If the starting material is an aliphatic hydrocarbon mixture which, in addition to the paraffins mentioned, contains other aliphatic hydrocacons as well, this mixture may contain, inter alia, methane, ethene, propene, butene, isobutene, butadiene and paraffins and olefins with five or more carbon atans per molecule. In the process according to the invention the starting material preferred is a feed which consists more than 75 %w, and in particular substantially completely, of one or more paraffins having three or four carbon atoms per molecule. A feedstock which is very suitable for use in the process z ss is a mixture of paraffins with three and four carbon atoms per molecule obtained as a by-product in the production of mineral oil. The process according to the invention is preferably carried out at a temperature of 350-700 C and in particular of 450-650 OC, a pressure of 1-20 bar and in particular of 1-10 bar and a space velocity of 0.1-10 kg.kg .hours and in particular of 0.5-5 kg.kg .hour . In the process according to the invention the feed is contacted with a catalyst containing a crystalline metal silicate which is defined, among other things, by the X-ray powder diffraction pattern which the silicate shows after one hour' s calcination in air at 500 OC. In this pattern the strongest lines should be the four lines mentioned in Table A. The complete X-ray powder diffraction pattern of a typical example of the present crystalline metal silicates after one hour's calcination in air at 500 C is given in Table B. TARTF. B d(A) Bel. int. d(A) Rel. int. 11.1 100 3.84 (D) 57 10.0 (D) 70 3.72 (D) 31 8.93 1 3.63 16 7.99 1 3.47 < 1 7.42 2 3.43 5 6.68 7 3.34 2 6.35 11 3.30 5 5.97 17 3.25 1 5.70 7 3.05 8 5.56 10 2.98 11 5.35 2 2.96 3 4.98 (D) 6 2.86 2 4.60 4 2.73 2 4.35 5 2.60 2 4.25 7 2.48 3 4.07 2 2.40 2 4.00 4 (D) = doublet The catalysts used in the process according to the invention are catalysts comprising the prescribed percentage of gallium supported on a carrier and in addition a crystalline metal silicate of the special structure which has a SiO2/(Y2O3 + Ga2O3) molar ratio of 10-500. A carrier for the gallium that may suitably be used is the crystalline metal silicate. The gallium is preferably deposited on the crystalline metal silicate by impregnation or ion exchange starting fran an aqueous solution of a gallium compound, such as gallium nitrate. Very suitable catalysts for carrying out the present conversion may be prepared by depositing the gallium on a conventional carrier, such as silica and mixing the gallium-loaded carrier with the crystalline metal silicate. Mixtures of gallium supported on silica as the carrier and gallium supported on the crystalline metal silicate as the carrier are also suitable for use as catalyst in the present conversion. In the process according to the invention preference is given to catalysts in which the carrier for the gallium is exclusively the crystalline metal silicate and in which the gallium has been deposited on the crystalline metal silicate by impregnation or ion exchange, as well as to catalysts in which the carrier for the gallium is exclusively an amorphous material, which gallium-loaded carrier is present in the catalyst in admixture with the crys- talline metal silicate. The crystalline metal silicate which is present in the catalysts as the carrier for the gallium and/or as a mixing ponent for a gallium-loaded carrier has a SiO2/(Y203 + Ga203) molar ratio of 10-500. It is pointed out that in determining the SiO2/(Y203 + Ga203) molar ratio only the quantity of gallium should be taken into account which may have been incorporated in the silicate during the synthesis of the silicate by crystalline zation from an aqueous solution containing one or more gallium carcounds. Neither gallium which has been deposited on the ready crystalline metal silicate after the synthesis, for instance by impregnation or ion exchange, nor gallium which is present in the catalyst supported on a carrier plays a role in the determination of the SiO2/(Y203 + Ga203) molar ratio of the crystalline metal silicate. In the process according to the invention preference is given to the use of a catalyst comprising a crystalline metal silicate with a SiO2/(Y203 + Ga2O3) molar ratio of 25-250. As regards the number of times that the two-step treatment should be carried out in order to obtain a catalyst with opttium performance in the present conversion, it may be remarked, that in general, the performance of the present catalysts can be brought to an optium level by subjecting thK3n at most three times to the two-step treatment. Further investigation has shown that, a preceding calcination at a temperature between 600 and 1000 OC, is detrimental to the catalyst performance in the case of the present catalysts. In the first step of the two-step treatment basically any hydrocarbon or mixture of hydrocabons may be used, provided that at a temperature of 350-700 C and in a period of less than 5 hours a coke deposition an the catalyst of 0.1-5 %w can thereby be realized. For this purpose the hydrocarbon or the mixture of hydrocarbons used as the feed in the process according to the invention is very suitable. The oxygen-containing gas used in the second step of the two-step treatment for the rnal of more than 50 %w of the coke present on the catalyst may very suitably be air. Preferably more than 75 %w of the coke present on the catalyst and in particular substantially all the coke present on the catalyst is removed in the second step of the two-step treatment. The preparation of the crystalline metal silicates used in the process according to the invention may very suitably be carried out starting from an aqueous mixture containing the following canpaunds: one or xore compounds of an alkali metal (M), one or more organic nitrogen compounds (RN) which contain an organic cation or from which an organic cation is formed during the preparation of the silicate, one or more silicon compounds, one or more compounds of a trivalent metal Y and, if desired one or more gallium ccmpownds. The e preparation is carried out by maintaining the mixture at an elevated temperature until the silicate has formed and subsequent ly separating the silicate crystals fran the mother liquor and washing, drying and calcining the crystals. In the aqueous mixture from which the silicates are prepared the various carpounds should be present in the following molar ratios expressed - with the exception of the organic nitrogen compounds - in moles of the oxides: M20 : SiO2 = 0.01-0.35, RN : Sio2 = 0.02-1.0, sio2 : (Y203 + O3) = 10-750, Ga203: Y203 < 1, and H20 : SiO2 = 5-65. In the preparation of the silicates the base mixture may very suitably be a mixture containing a quaternary ammonium compound as the organic nitrogen compound, a sodium carpound as the alkali metal compound and amorphous silica as the silicon compound. In the process according to the invention preference is given to the use of crystalline metal silicates which have been prepared by crystallization fran an aqueous mixture which contains no gallium compounds and which contains at least one or more aluminium carpounds as the compounds of a trivalent metal Y. The silicates prepared as described hereinbefore contain alkali metal ions. By using suitable exchange methods these may be replaced by other cations, such as hydrogen ions or ammonium ions. The crystalline metal silicates used in the process according to the invention preferably have an alkali metal content of less than 0.05 %w. In the process according to the invention the composi- tions comprising gallium supported on a carrier as well as a crystalline metal silicate of a special structure may be used per se or combined with a binder material, such as kaolin or bentonite. The invention is now elucidated with the aid of the following example. Example Three crystalline aluminium silicates (silicates 1-3) were prepared by heating mixtures of NaOH, amorphous silica, (C3H7)4NOH and NaAlO2 in water, in an autoclave under autogenous pressure, at 150 C for 24 hours. After cooling of the reaction mixtures the silicates formed were filtered off, washed with water until the pH of the wash water was about 8 and dried at 120 OC. After one hour's calcination in air at 500 C silicates 1-3 had the following properties a) an X-ray powder diffraction pattern substantially corresponding with that mentioned in Table B, and b) a SiO2/A1203 molar ratio as mentioned in Table C. SABLE C Silicate No. SiO2/At203 molar ratio 1 100 2 100 3 170 The molar compositions of the aqueous mixtures fran which silicates 1-3 were prepared may be rendered as x NO.y (C3H7)4NOH.z A1203.25 SiO2.450 H2O wherein x, y and z have the values given in Table D. TABLE D Silicate No. x y z 1 0.33 9 0.33 2 1 3 0.2 3 1 9 0.1 From silicates 1-3 were prepared silicates I-III, respectively, by boiling silicates 1-3 with a 1.0 molar NH4NO3 solution, washing with water, boiling again with a 1.0 molar NH4NO3 solution and washing, drying at 120 OC and calcination at 500 OC. Catalysts I-III were prepared fran silicates I-III as follows: Catalyst I This catalyst was prepared by impregnating silicate I with an aqueous solution of gallium nitrate. Catalyst I contained 2 %w gallium. Catalyst II This catalyst was prepared by ion exchange of silicate II using an aqueous solution of gallium nitrate. Catalyst II contained 3.2 %w gallium. Catalyst III This catalyst was prepared by mixing silicate III in a weight ratio of 1:1 with a composition which contained 2 %w gallium on silica and had been obtained by impregnation of silica with an aqueous solution of gallium nitrate. Catalyst III contained 1 %w gallium. Samples of catalysts I-III were subjected once or several times to a two-step treatment comprising a step in which the catalyst was contacted with n-butane for 30 minutes at a temr perature of 600 OC, a pressure of 1.5 bar and a space velocity of 8 g.g l.h 1 and in which a quantity of coke ranging from 0.2 to 0.8 %w was deposited on the catalyst, followed by a second step in which the catalyst was contacted with air for 1 hour at a temperature of 500 C and a pressure of 1.5 bar and in which 95-99 %w of the coke present on the catalyst was removed. From catalysts I-III were thus produced catalysts IA, IB, IIA, IIIA, respectively. In addition a sample of catalyst III was first contacted with air for 1 hour at 700 C and then subjected twice to the two-step treatment described hereinbefore. Thus catalyst IIIB was obtained from catalyst III. Catalysts I-IB, II, IIA and III-IIIB were tested in eight experiments (Experiments 1-8) in the preparation of C5 aromatic hydrocarhon mixtures starting from n-butane. The experiments were carried out in a reactor containing a fixed catalyst bed. All the experiments were carried out at a temperature of 550 OC, a pressure of 1.5 bar and a space velocity of 2 -1hour-1 kg.kg hour . The results of the experiments are listed in Table E. Table E also indicates how many times each of the catalysts has been subjected to the two-step treatment as well as the quantities of coke deposited on each catalyst in the first step of the two-step treatment. Of the experIments mentioned in Table E Experiments 2, 3, 5 and 7 are experiments according to the invention. These experi aunts were carried out using catalysts comprising gallium sub- ported on a carrier as well as a crystalline metal silicate of a special structure, which catalysts had been subjected to at most three two-step treatments according to the invention. These catalysts show high activity and h selectivity as well as acceptable c5 selectivity. Caparison of the results of Experiments 1-3 shows that the catalyst performance is inch enhanced if the catalyst is subjected to the two-step treatment once, z , but that the performance shows no marked further improve- ment when the two-step treatment is repeated three times. Experiments 1, 4, 6 and 8 fall outside the scope of the invention. They have been included in the patent application for comparison. Experirents 1, 4 and 6 were carried out using catalysts comprising gallium supported on a carrier and a crystalline metal silicate of a special structure, but these catalysts had not been subjected to a two-step treatment according to the invention. Experiment 8 was carried out using a catalyst comprising gallium supported on a carrier and a crystalline metal silicate of a special structure, which catalyst had been subjected twice to a two-step treatment according to the invention, but this catalyst had been subjected to calcination at 700 C preceding the repeated two-step treatment. TABLE E Experiment No. 1 2 3 4 5 6 7 8 Catalyst No. I IA IB II IIA III IIIA IIIB Number of times that catalyst was subjected - 1 3 - 3 - 2 2* to two-step treatment Quantity of coke deposited on catalyst - 0.2 0.2-0.8 - 0.8-0.9 - 0.7-0.8 0.7-0.8 in first step of twostep treatment, %w Conversion, %w 51 71 70 97 98 91 92 86 Product selectivity, %w on converted material EMI11.1 3.5 5.8 5.5 4.5 5.3 2.3 4.9 3.5 74.2 58.4 52.4 68.8 54.0 78.0 62.8 69.2 4.7 3.3 3.4 0.9 0.3 2.0 1.3 1.4 3.4 2.2 4.9 0.6 0.5 1.4 0.9 1.0 14.2 30.3 33.8 25.2 39.9 16.4 30.1 24.9 * After preceding treatment with air at 700 C

Claims: CLAIMS 1. A process for the preparation of an aromatic hydrocarbon mixture, characterized in that paraffins with two, three or four carbon atoms per molecule or aliphatic hydrocarbon mixtures consisting more than 50 %w of said paraffins are contacted with a catalyst comprising gallium supported on a carrier and a crystalline metal silicate which a) has been prepared by crystallization starting from an aqueous mixture which, in addition to the ccmponents needed for the synthesis of the silicate, comprises one or more carpounds of a trivalent metal Y chosen from the group formed by alumin- ium, iron, cobalt adn chromium and, if desired, one or more gallium compounds in such quantities that in the formula which represents the ccmposition of the silicate expressed in moles of the oxides, the SiO2/ (Y203 + Ga203) itolar ratio is 10-500 and the Ga203/Y203 molar ratio is lower than 1, and b) after one hours calcination in air at 500 C has an X-ray powder diffraction pattern in which the strongest lines are the four lines mentioned in Table A, TABLE A d( ) 11.1 + 0.2 10.0 i 0.2 3.84 + 0.07 3.72 + 0.06 in which catalyst the quantity of gallium supported on a carrier amounts to 1-10 bw, calculated on the quantity of crystalline metal silicate present in the catalyst, and which catalyst has been subjected at least once to a two-step treatment comprising a step in which the catalyst is con tacted at a temperature of 350-700 C with a hydrocarbon or a mixture of hydrocarbons until in less than 5 hours 0.1-5 %w of coke has been deposited on the catalyst, followed by a second step in which the coke-loaded catalyst is contacted at a tepperature of 350-700 C with an oxygen-containing gas until more than 50 Ew of the coke present on the catalyst has been removed. 2. A process as claimed in claim 1, characterized in that it is applied to a feedstock more than 75 %w of which consists of one or more paraffins having three or four carbon atans per molecule. 3. A process as claimed in claim 1 or 2, characterized in that it is carried out at a temperature of350-700 OC, a pressure of 1-20 bar and a space velocity of 0.1-10 kg.kg l.h 1. 4. A process as claimed in any one of claims 1-3, characterized in that the catalyst is subjected to the two-step treatment at frost three times. 5. A process z ss as claimed in any one of claims 1-4, characterized in that the quantity of crystalline metal silicate, calculated on the sum of the quantity of crystalline metal silicate present in the catalyst and the quantity of other material used as carrier for the gallium which may be present in the catalyst, is at least 20 %w. 6. A process as claimed in any one of clams 1-5, characterized in that the gallium present in the catalyst is supported on the crystalline metal silicate as carrier and that the gallium has been deposited on the crystalline metal silicate by inpregnation or ion exchange. 7. A process as claimed in any one of claims 1-5, characterized in that the gallium present in the catalyst is supported on an amorphous carrier material. 8. A process as claimed in any one of claims 1-7, characterized in that the feedstock is used to achieve the desired level of coke deposition in the first step of the two-step treatment. 9. A process as claimed in any one of claims 1-8, characterized in that air is used as the oxygen-oontaining gas in the second step of the two-step treatment. 10. A process as claimed in any one of claims 1-9, characterized in that in the second step of the two-step treattult more than 75 %w of the coke present on the catalyst is removed.

Inventors: KIEFFER, EDUARD PHILIP
Applicants: SHELL INTERNATIONALE RESEARCH MAATSCHAPPIJ B.V.
Application year: 1983
Main classification: C07C2
IPC codes: C07C2, B01J29