CHEMICALLY SPECIFIC SURFACES FOR INFLUENCING CELL ACTIVITY DURING CULTURE

Abstract: Cell culture activity on the surface of the substrate is in­ fluenced by varying surfaces in contact with the cell mem­ brane. In particular, plasma modification processes are used to provide specific chemical functional groups, ele­ mental ratios and other surface properties. In the method of the invention for influencing the growth of cell culture in a growth media on a substrate, the surface chemistry of the substrate is modified by subjecting the surface of the sub­ strate to a plasma which is produced from a material se­ lected from the group consisting of carbon, hydrogen, oxy­ gen, nitrogen, sulfur, phosphorus, halogens and com­ pounds thereof.

Description: CHEMICALLY SPECIFIC SURFACES FOR INFLUENCING CELL ACTIVITY DURING CULTURE The present invention relates generally to methods and articles for influencing cell growth, particularly tissue culture growth. More particularly, the invention relates to the modification of the surfaces of organic and inorganic substrates so as to provide a chemically modified surface which enhances or inhibits the growth of various cells in culture. It is demonstrated herein that cellular function on polymer surfaces can be selectixsely controlled by varying the surface chemistry in contact with the cell membrane. It is known that one of the factors influencing the growth of both primary cell cultures and established cell line cultures is the interface between the growth media in which the cultures are being grown and the substrate providing the boundary layer for the growth media. It is well known to modify the dispersed phase, i.e., the medium, in which a cell culture is being grown. It is also known to alter the surface interface between the medium and the substrate generally by coating the surface with various chemicals, such as collagen, for example. It is common laboratory practice to apply various chemical coatings to the substrate prior to attempting cell culture growth. Some chemicals which have been used include polylysine, collagen, hyalurcnic acid, chondroitin 4-sulfate, chondroitin 6-sulfate, and various polysaccharides and lectins. The most commonly used chemical materials for modifying the substrate surface for primary cell culture growth are collagen, gelatin, and polylysine. It is also known to use only tissue culture grade plastic for growing established adherent cell cultures. For example, commercially available tissue culture products are marketed under the trademark FALCON from Becton, Dickinson and Company. Although commercial tissue culture products appear to work well for established cell lines, they do not work well for primary cell types or certain cell types requiring collagen coating, for example. In a preferred embodiment of the present invention, the surface chemistry of a substrate is modified by subjecting the substrate to a plasma of a suitable material. It is known to subject substrates to plasmas of various types for accomplishing various purposes. For example, a brochure of International Plasma Corporation, Product Bulletin 24000, suggests that polystyrene tissue culture trays can be made wettable and receptive to living cells through plasma treatment with an oxygen or argon plasma. A brochure of Tegal Corporation, CP1287, indicates tbat plasmas can be used for dry stripping, cleaning and etching of electronic parts, cleaning optical surfaces, preparing surfaces having bonding, wettability and chemical resistance properties and dry cleaning of substrates to improve film deposition and adherence. The doctoral thesis of Lee M. Smith, "Cell Adhesion As Influenced By Substrate Surface Properties", Department of Material Science and Engineering, the University of Utah, 1978, p. 67, suggests that cell adherence is a function of the carbon/oxygen ratio of the surface. None of these references, however, teach or suggest that cell growth can be influenced by chemical modification of the surface of the substrate on which the cell is grown. It would be desirable to provide chemically specific substrate surfaces for the growth of selected cell cultures without the need for coating the substrate with chemical materials suitable for enhancement of the growth of primary cell types for example. Due to the high growth rate generally exhibited by fibroblasts in culture, it is sometimes difficult to grow primary cells in culture because of the more rapid contaminating growth of fibroblasts. It would be desirable to provide specific substrate surfaces which are suitable for growth of cell cultures while inhibiting the growth of fibroblasts. Accordingly, it is a principal object of the present invention to provide chemically specific surfaces for influencing the growth of various cell cultures at the interface between the growth media and the substrate. It is another object of the present invention to provide a substrate with a chemically modified surface which influences growth of cell cultures on the surface. It is a further object of the present invention to provide a substrate with a chemically modified surface which does not require coating with chemical compounds prior to cell culture growth on the substrate surface. It is a still further object of the present invention to provide a method and an article for influencing the growth of cell cultures. These and other objects of the present invention will become more apparent from the accompanying drawings wherein: Fig. 1 is a schematic diagram of an apparatus which can be employed in the practice of the invention. Fig. 2 is a perspective view of a sample holder illustrated in the apparatus of Fig. 1. Figs. 3 through 10 are x-ray photoelectron spectroscopy, ESCA, scans of various substrates, some of which have been treated in accordance with the invention. Fig. 11 is a plot of the growth characteristics of primary neuronal cells as a function of surface chemistry and time. Fig. 12 is a plot of the growth characteristics of primary fibroblasts as a function of surface chemistry and time. In general, it has been discovered that cell culture activity on the surface of a substrate can be controlled by varying the surface chemistry of a substrate surface in contact with the cell membrane. The surface chemistry of a polymeric surface can be varied by using selected homopolymers, copolymerization, surface grafting and chemical modification, and by plasma treatment of the surface. In particular, plasma modification processes may be used to provide specific chemical functional groups, elemental ratios and other surface properties. In accordance with the invention, polymeric surfaces were prepared by plasma modification techniques which yielded a range of surface chemistries and properties. The modified polymeric surfaces were subJected to cell culture tests which indicate that cellular response is highly dependent on surface chemistry. A plasma of a suitable material may be used to modify the surface layer of organic and inorganic substrates, including polymeric materials1 glass and metals, regardless of thickness and which is independent of substrate composition, so as to provide specific chemical functional groups on the surface of the substrate. In the case of glass and metals, it is desirable to include a carbon source, such as methane, for example, to provide a thin organic layer on the inorganic substrate. Such plasma process is suitable for providing a surface for any cellular growth application whether the desired goal is to enhance or retard cell growth. The surface of the substrate is irreversibly modified by grafting specific chemical functional groups onto the surface with a plasma of a suitable material or with selected components of a plasma of a suitable material. Suitable materials include, but are not limited to oxygen, carbon, hydrogen, nitrogen, halogen, sulfur, phosphorus, mixtures thereof and compounds thereof. The surfaces which are modified in accordance with the present invention have specific chemical functional groups grafted onto the substrate surface and provide suitable surface chemistry for tissue culture growth or suppression of growth. In another embodiment of the present invention there is provided a process for modifying the surface of a substrate, specifically the modification of organic polymeric materials by treatment with specific chemical species comprising: Providing z substrate within a reaction zone. Providing a plasma of a suitable material in the reaction zone which includes neutral material, positive ions of the material, negative ions of the material, electrons and photons. Preventing at least one of the components of the plasma from contacting the surface of the substrate in the reaction zone. Contacting the surface of the substrate with the remainder of the components of the plasma in the reaction zone, and Forming specific functional groups of the material on the surface of the substrate. This embodiment of the present invention is based on. the discovery that utilization of selected reactive species of a plasma in contact with a substrate can be employed to provide specific chemical functional groups on the surface of the substrate which act to influence cell culture growth. Referring now to the figures, other features and advantages of the present invention will be described. As shown in Fig. 1 there is provided a first gas reservoir 11, a second gas reservoir 13 with conduit means 15 to deliver either or both a first gas and a second gas to a vacuum chamber 1?. Flow meters 19 and 21 are provided for measuring gas flow rate and a vacuum gauge 23 is provided to monitor the pressure within the vacuum chamber 17. Valves 25, 27 and 29 are provided to regulate the flow rate of the gas in the first gas reservoir 11, the second gas reservoir 15 and the gas entering the vacuum chamber 17. Prior to use, the vacuum chamber 17 is evacuated by opening valve 31 to vacuum pump 33. Suitable electrodes 35 and 37 are connected to a suitable voltage source 39. The reactor system also includes a trap 41, vent conduit 43 and its valve 45. As best seen in Fig. 2, a substrate 47 to be treated in accordance with the invention is placed in a sample holder 55 ana disposed within the vacuum chamber 17. The sample holder includes a grid assenbly of three grids, designated grid I, grid 2 and grid 3. A collector 49 which can be electrically biased is disposed on the other side of the sample from the grid system. The sample is held in place between grid 3 and the collector by means of a suitable holder 51. In operation, any or none of the three grids or the collector can be biased with positive or negative charge to repel selective components of a plasma generated between the electrodes 35 and 37. The substrate in the sample holder is then subjected to reaction with those components of the plasma which are not repelled. The present invention can be employed to alter the surfaces of solid polymeric materials, including natural and synthetic addition and condensation polymers. Such polymeric materials include polyolefins, such as polyethylene, polypropylene, polyisobutylene and ethylene-alpha-olefin copolymers, acrylic polymers and copolymers, such as polyacrylate, polyethylethacrylate, polyethylacrylate; vinyl halide polymers and copolymers, such as polyvinyl chloride; polyvinyl ethers, such as polyvinyl methyl ether; polyvinylidene halides, such as polyvinylidene fluoride and polyvinylidene chloride; polyacrylonitrile, polyvinyl ketones; polyvinyl amindes; polyvinyl aromatics, such as polystyrene, polyvinyl esters such as polyvinyl acetate; copolyers of vinyl monomers with each other and olefines, such as ethyelen-methyl methacrylate copolymers, acrylonitrile-styrene copolyers, ABS resins, and ethylenevinyl acetate copolyers; natural and synthetic rubbers, including butadiene-styrene copolymers, polyisoprene, synthetic polyisoprene, polybutadiene, butadiene-acrylonitrile copolymers, polychloroprene rubbers, polyisobutylene rubber, ethylene-propylene rubber, ethylene-propylene-diene rubbers, isobutylene-isoprene copolymers and polyurethane rubbers; polyamides, such as Nylon 66 and polycaprolactam; polyesters such as poly hellene terephthalate, alkyd resins; phenol-formaldehyde resins; urea-formaldehyde resins, malamine-formaldehyde resins; polycarbonates; polyoxymethylenes; polyimides; polyethers; epoxy resins, poly-urethanes; wool; cotton; silk; rayon; rayon-triacetate; cellulose; cellulose acetate, cellulose butyrate; cellulose acetatebutyrate; cellophane; cellulose nitrate; cellulose propionate; cellulose ethers; and carboxymethyl cellulose. Inorganic materials, the surfaces of which can be modified in accordance with the invention, include non-metals, such as graphite; metals, such as iron, aluminum, tin, copper and nickel; metal and other elemental oxides; such as magnesium oxide, silica, alumina and titania; minerals, such as clay, pyrite and asbestos; salts, such as sodium chloride and calcium carbonate; and such synthetic compositions such as glass and refactories. The substrates whether organic or inorganic, can be any shape, such as continuous or particulate, porous or impervious, and large or small. The invention can be employed for altering the surfaces of crystals, powders, plates, strips, films, sheets, wire, fibers, fabrics, filaments, tubing, and cast, extruded or compressed articles, and the like. Plasmas of the elements of carbon, hydrogen, oxygen, nitrogen, sulfur, phosphorus, the halogens, mixtures thereof and compounds thereof are useful to modify the surface of substrates in accordance with the present invention. Four types of plasmas can be generated; these are thermal plasmas, discharge plasmas, beam plasmas (such as ion beams and electron beams) and hybrid plasmas such as corona discharges. Suitable plasmas for use in the method of the present invention are discharge plasmas, beam plasma-s and hybrid plasmas. Suitable plasmas can be generated by use of DC sources or AC sources having a frequency through the microwave range at power levels from about 1.OW to about 10 kW. Although not limited to high frequency sources, such as radiofrequency (r.f.) sources, plasmas of this type are particularly useful for the method and articles of the present invention in that selected plasma species concentrations can be controlled by source frequency, power, and system pressure. It is also true that r.f. plasmas are suitable for uniformly modifying the surface of more complex article shapes, such as tubing and other enclosures, for which DC and low frequency generated plasmas are not satisfactory. In general, the r.f. plasmas suitable for use in the present invention are generated at a frequency of from about 1.0 to about 300 MHz at a power to initiate breakdown, such as from about 5 to about 1000 watts at pressures ranging from 0.001 to iO Torr. The articles are usually subjected to the r.f. plasma for a period of from about 0.1 sec to about 120 minutes, although longer and shorter periods can be used. The plasma treatment can be followed by a quench cycle designed to provide an atmosphere suitable for reacting with residual active polymer species at or near the surface with pressures ranging from 1 Torr to 760 Torr for time periods of 1 second to 4 hours. The r.f. plasma can be generated between two flat plates, as shown in Figure 1, or can be generated with a helical coil, as shown in United States Patent No. 4,188,426. In the following examples, a substrate of polystyrene is subjected to various plasma species. The substrate is then examined by x-ray photoelectron spectroscopy (ESCA) to determine the nature of the chemical functional groups on the surface of the polystyrene substrate. After being subjected to the plasma of the following examples, the substrates are measured as to the Zeta Potential and Wilhelmy Plate Contact Angle. These values are listed in Table 1. These measurements of surface charge and surface tension characteristics illustrate the wide range of surface chemistries achieved. The culture growth plating efficiency is determined by inoculating petri dishes with a dilute cell suspension containing approximately 30 Human Diploid (MRC5) cells per milliliter in growth medium. The cell cultures were grown until the colonies ranged in size from 100 to 300 cells. The mean number of colonies for each test group of dishes was measured. The plating efficiency is defined as the ratio of the number of colonies per dish to the number of cells inoculated and is expressed as a percentage. The relative plating efficiency is determined by the ratio of the plating efficiency of the sample to that of the same sample grown on a petri dish identified by the Trademark FALCON obtained from Becton Dickinson and Company. It is clear from Table 1 that the cellular response of fibroblasts is highly dependent on the surface chemistry produced by the plasma modification processes. The following examples show that fibroblast growth can be controlled by varying the surface chemistry in contact with the cell membrane. The effect of specific surface chemistries on the growth of MRC5 fibroblasts as measured by relative plating efficiency was demonstrated with surfaces covering a range of carbon, oxygen, nitrogen and sulfur bonds. Example 1 N2/H2/Air A plasma chamber containing petri dishes was evacuated to 60 over a 20-minute period. The chamber was filled with hydrogen at 140M and nitrogen at 70 for five minutes. A 10 MHz 40 watt r.f. plasma was operated for five minutes. The system was left under vacuum for two minutes and then opened to atmosphere. The surface properties and plating efficiency are given in Table 1. ESCA analysis of the surface is illustrated in Figure 3. TABLE 1 Plasma Relative Plating recursor/Quench Zeta Potential Wilhelay Plate Efficiency Gas zeta (nV) ea (equil) MRCS Fibroblasts Falcon -11.8 6+3 100 02/NH3 - 4.0 5+2 85.1 CO2ENH3/NS3 - 4.1 9+1 64.8 N83/NS3 +11.5 65+1 32.7 NH3/Air + 8.2 60+2 35.8 NH3/c02 . +31.3 64+3 31.3 N2/H2/Air -11.0 10+5 89 SO2/Air -19.4 72+3 43 SO2/SO2 -14.8 77+1 0 C02/Air 50.6 Untreated PS - 9.7 101+1 6 Glass 0 48+3 Example 2 CO2/Air The petri dishes were placed in the plasma chamber and evacuated to 75 over a 10-minute period and then filled with CO2 to 180 pressure for two minutes. An r.f. plasma was produced for five minutes with a frequency of 11 MHz at 40 watts power. After treatment, the system was immediately opened to the atmosphere. The plating efficiency is listed in Table 1. Example 3 O2/NH3 The petri dishes were placed in the plasma chamber and evacuated to 7511 over a period of 10 minutes. Oxygen at 18 was bled through the system for two minutes to flush out any residual air. While maintaining 180p oxygen, a 10 watt 11 MHz r.f. plasma was run for five minutes. The chamber was then brought up to 700 Torr with NE3 for a two-hour quench. The surface properties and plating efficiencies are listed in Table 1. Example 4 CO2 & NH3/NH3 The petri-dishes were placed in the plasma chamber and evacuated to 7511 over a period of 10 minutes. NH3 and CO2 were bled into the system to 9011 . An r.f. plasma at 11 MHz and 10 watts was produced for five minutes duration. The chamber was then brought up to 700 Torr with NH3 for a twohour quench. The surface properties and plating efficiencies are listed in Table 1. Example 5 NH3/CO2 The petri dishes were placed in the plasma chamber and evacuated to 75y for 10 minutes and filled with 180 of NH3 for two minutes. A 10 MHz 35 watt r.f. plasma was operated for five minutes. The system was then brought up to 700 Torr with CO2 for a two-hour quench. Then the chamber was pumped down to 1 Torr and opened to atmosphere. Surface properties and plating efficiency are listed in Table 1. The ESCA data is given in Figure 4. Example 6 NH3/NH3 This group was prepared identically to Example 5 except that the 700 Torr quench was carried out with NH3 instead of CO2. Surface properties and plating efficiency are listed in Table 1. The ESCA data is given in Figure 5. Example 7 NH3/Air This group was prepared identically to Example 5 except that the surfaces were immediately exposed to air. Surface properties and cloning efficiency are listed in Table 1. The ESCA data is given in Figure 6. Example 8 S02/Air A plasma chamber containing polystyrene petri dishes was evacuated to 50 for 20 minutes, and'then filled to 200yof SO2 for 10 minutes. A 10MHz 34 watt r.f. plasma was operated for five minutes. The system was left at 200ji for two minutes and then pumped down to 50 for two minutes, followed by opening to atmosphere. Surface properties and efficiency are listed in Table 1. The ESCA data is given in Figure 7. It is clear from this example that fibroblast growth is retarded by sulfur containing groups on the surface. Example 9 SO2/SO2 The petri dishes were placed into the plasma chamber and evacuated to 50y for 20 minutes. S02 was inbled to 200 for 10 minutes. A 10 MHz 45 watt r.f. plasma was operated for five minutes. Then the system was immediately filled with S02 to a 700 Torr pressure for a two-hour quench. The system was pumped to 5011 and then opened to air. As illustrated in Table 1, the plating efficiency was negligible for fibroblasts on this surface. This provides a unique surface in that it slows or blocks fibroblast growth in culture. This is particularly useful in primary cultures where fibroblast growth can interfere with maintaining primary cells in culture. The surface chemistry as measured by ESCA is shown in Figure 8. Example 10 Polylysine and collagen coated petri dishes are used extensively in primary cell cultures. In this example, two plasma modification processes ere used to yield nitrogenous surfaces. This type of surface is described by NH3/C02 and NH3/N H3 as prepared in Examples 5 and 6 respectively. ESCA analysis of the NH3/NH3 surface yielded O/C = 0.12 and N/C = 0.14 and O/C = 0.14 and N/C = 0.19 for group NH3/C02. The ESCA scans of these samples are shown in Figures 9 and 10 respectively. The response of primary neuronal cells in culture to these two plasma treated surfaces with respect to polylysine and collagen/polylysine coated control surfaces demonstrate a uniqueness in growth characteristics. Choline acetyltransferase, CAT, is a specific biochemical marker indicative of preferential neuronal cell support. As illustrated in Figure 11, the two plasma modified nitrogenous surfaces NH3/C 02 and NH3/NH3 support synthesis of primary neurons to a much greater extent than any of the chemically coated surfaces. Example 11 Plating efficiency test results with the MRC5 fibroblast cell line resulted in a significant reduction of growth on the two surfaces 502/Air and 502/502 plasma treated as described in Examples 8 and 9 respectively. The abundance of primary fibroblasts in neuronal cell cultures can be measured by LDH content. Lactate dehydrogenase, LDH, is a non-specific cell marker indicative of cytoplasma volume and, therefore; all cells present in culture including primary fibroblasts. As shown in Figure 12, this surface significantly slows down fibroblast growth compared to the control polylysine coated surf ace.

Claims: CLAIMS 1. A method for influencing the growth of cell culture in a growth media on a substrate, characterized in that the surface chemistry of the substrate is modified by subjecting the surface of the substrate to a plasma which is produced from carbon, hydrogen, oxygen, nitrogen, sulphur, phosphorus, a halogen, or a compound of any one of these elements. 2. A method in accordance with claim 1 wherein the plasma is a discharge plasma generated at a frequency of from 1 to 300 megahertz at a power of from 5 to 1000 watts at a pressure of from 0.001 to 10 Torr. 3. A method in accordance with claim 1 or 2 wherein the plasma material comprises oxygen or an oxygen compound. 4. A method in accordance with claim 1 or 2 wherein the plasma material comprises nitrogen or a nitrogen compound. 5. A method in accordance with claim 1 or 2 wherein the plasma material comprises sulphur or a sulphur compound. 6. A method in accordance with claim 1 or 2 wherein the plasma material comprises phosphorus or a phosphorus compound. 7. A method in accordance with claim l or 2 wherein the plasma material comprises halogen or a halogen compound. 8. A method in accordance with claim 1 or 2 wherein the plasma material comprises carbon or a carbon compound. 9. A method in accordance with claim 1 or 2 wherein the plasma material comprises hydrogen or a hydrogen compound. 10. An article suitable for influencing the culture growth of at cell in contact therewith comprising a polymeric article whose surface chemistry has been modified by subjecting the surface to a plasma which is produced from a material comprising carbon, hydrogen, nitrogen, sulphur, phosphorus, a halogen, or a compound of any of these elements, or an oxygen compound. 11. An article suitable for influencing the culture growth of a cell in contact therewith comprising an inorganic article whose surface chemistry has been modified by subjecting the surface to a plasma which is produced from a material comprising carbon, hydrogen, oxygen, nitrogen, sulphur, phosphorus, a halogen, or compound of any of these elements. 12. A method for influencing the growth of cell culture in a growth media on a substrate comprising modifying the surface chemistry of the substrate by steps comprising: (a) positioning the substrate within a reaction zone (b) introducing a material into the reaction zone, the material being suitable for providing a plasma (c) subjecting the material to plasma producing conditions, whereby the plasma comprises neutral material, positive ions of the material, negative ions of the material, electrons and photons (d) preventing at least one of the components of the plasma from contacting the surface of the substrate (e) contacting the surface of the substrate with the remainder of the components of the plasma, and (f) forming specific functional groups of the material on the surface of the organic substrate. 13. A method in accordance with claim 12 wherein the plasma is produced under electrical discharge conditions. 14. A method in accordance with claim 12 or 13 wherein the material comprises oxygen, nitrogen, halogen, sulphur, compounds thereof, or mixtures thereof.

Inventors: DUNN, TERRY S., WILLIAMS, JOEL L.
Applicants: BECTON, DICKINSON AND COMPANY
Application year: 1983
Main classification: C12N5
IPC codes: C12M3, C08J7, B01J19, B29C59, C12N5