Adsorbent and process for preparing the same

Abstract: Adsorbent for removing a harmful substance to be re­ moved from body fluid such as blood or plasma composed of a porous hard gel on which a ligand having an affinity for the harmful substance is immobilized. The adsorbent is suitable for selective removal of harmful substances such as VLDL, LDL, harmful proteins, viruses and harmful cells, in extracorpo­ real circulation treatment.

Description: The present invention relates to a novel adsorbent and a process for preparing the same, more particularly, to an adsorbent for removing harmful substances to be removed from body fluid such as blood or plasma in extracorporeal circulation treatment. There has been required a means for selectively removing harmful substances which appears in body fluid and closely relate to a cause or a progress of a disease. For example, it is known that plasma lipoprotein, especially very low density lipoprotein (hereinafter referred to as "VLDL") and/or low density lipoprotein (hereinafter referred to as "LDL") contain a large amount of cholesterol and cause arteriosclerosis. In hyperlipemia such as familial hyperlipemia or familial hypercholesterolemia, VLDL and/or LDL show several times higher values than those in normal condition, and often cause arteriosclerosis such as coronary arteriosclerosis. Although various types of treatments such as regimen and medications have been adopted, they have limitations in effect and a fear of unfavorable side effects. Particularly in familial hypercholesterolemia, a plasma exchange therapy which is composed of plasma removal and compensatory supplement of exogeneous human plasma protein solutions is probably the only treatment method being effective nowadays. The plasma exchange therapy, however, has various defects such as (1) a need for using expensive fresh plasma or plasma fractions, (2) a fear of infection by hepatitis viruses and the like and (3) loss of all plasma components containing not only harmful components but also useful ones, i.e. in case of lipoprotein, not only VLDL and/or LDL but also high density lipoprotein (hereinafter referred to as "HDL") are lost. For the purpose of solving the above defects, a selective removal of harmful components by a membrane and the like has been adopted. These methods, however, are insufficient in selectivity and cause a large loss of useful components from body fluid. There has been also tried a selective removal of harmful components by means of adsorption. For example, a synthetic adsorbent such as active carbon or Amberlite XAD (a registered trademark, commercially available from Rohm & Haas Co.) has been utilized for liver disease. Such an adsorbent however, has many defects such as poor selectivity and disability for removing high molecular compounds. Furthermore, for the purpose of increasing selectivity, there has been adopted an adsorbent based on the principle of affinity chromatography composed of a carrier on which a material having an affinity for a substance to be specifically removed (such material is hereinafter referred to as "ligand") is immobilized. In that case, however, it is difficult to obtain a sufficient flow rate for an extracorporeal treatment because a carrier is a soft gel such as agarose. Accordingly, a particular modification in column shape is required in order to obtain a large flow rate and the risk of an occasional clogging still remains. Therefore, a stable extracorporeal circulation cannot be achieved by the above method. GB―A―2 075 362 discloses an adsorbent for the adsorption of blood proteins, the adsorbent being based on a porous material. The porous materials comprise porous glass, porous silica, porous alumina and porous ceramics, which may be coated with a hydrophilic polymer. GB―A―2 092 470 discloses a method for reducing pyrogen from pyrogen-containing solutions by means of an adsorbent comprising a water-insoluble carrier having a nitrogen-containing heterocyclic compound bonded to it. An adsorbent of the present invention may be used for selectively removing not only the above-mentioned VLDL and/or LDL but also other harmful substances to be removed from body fluid. It is an object of the present invention to provide an adsorbent for selectively removing harmful substances such as VLDL, LDL, virus and harmful cells from body fluid such as blood or plasma in extracorporeal circulation treatment of immune disease, metabolic disease, inflammatory disease such as hepatitis or nephritis, virus infection, and the like. A further object of the present invention is to provide a process for preparing the adsorbent. These and other objects of the present invention will become apparent from the description hereinafter. In accordance with the present invention, there is provided an adsorbent for removing low and/or very low density lipoproteins from body fluid in continuous extracorporeal circulation treatment comprising a porous cellulose hard gel on which a polyanion compound is immobilized by a covalent linkage; said porous cellulose hard gel having uniformly pores at any part of the gel, having an exclusion limit of from 10 6 to 10 9 daltons, and having a cellulose content of from 2 to 60 %. Fig. 1 is a graph showing relation between flow rate and pressure-drop obtained in Reference Example a, and Fig. 2 is a chart of polyacrylamide disc gel electrophoresis obtained in Example 13. It is suitable that carriers used in the present invention have the following properties: (1) relatively high mechanical strength, (2) low pressure-drop and no column clogging in case of passing body fluid through a column packed with a carrier, (3) a large number of micro pores into which a substance to be removed permeates substantially, and (4) less change caused by a sterilizing procedure such as steam sterilization by autoclaving. Therefore, the most suitable carrier used in the present invention is a water-insoluble porous cellulose gel. The porous cellulose gel used in the present invention is a hard gel and is less swelled with a solvent and less deformed by pressure than a soft gel such as dextran, agarose or acrylamide. The term "hard gel" and "soft gel" in the present invention is explained as follows: A hard gel is distinguished from a soft gel by the following method described in Reference Example a That is, when a relation between flow rate and pressure-drop is determined by passing water through a column uniformly packed with gel, a hard gel shows a linear relationship while a soft gel shows a non-linear relationship. In case of a soft gel, a gel is deformed and consolidated over a certain pressure so that a flow rate does not increase further. In the present invention, a gel having the above linear relationship at least by 0.3 kg/cm 2 is referred to as "hard gel". A pore size of the porous cellulose gel is selected depending on molecular weight, shape, or size of a substance to be removed, and the most suitable pore size may be selected in each case. For measuring the pore size, there are various kinds of methods such as mercury porosimetry and observation by an electron microscope as a direct measuring method. With respect to water-containing particles, however, the above methods sometimes cannot be applied. In such a case, an exclusion limit may be adopted as a measure of pore size. The term "exclusion limit" in the present invention means the minimum molecular weight of a molecular which cannot permeate into a pore in a gel permeation chromatography (cf. Hiroyuki Hatano and Toshihiko Hanai: Zikken Kosoku Ekitai Chromatography (Experimental High-Pressure Liquid Chromatography), published by Kabushiki Kaisha Kagaku Dojin). Phenomenally, a molecule having a molecular weight of more than exclusion limit is eluted near the void volume. Therefore, an exclusion limit can be determined by studying the relations between molecular weights and elution volumes using substances of various molecular weights in a gel permeation chromatography. An exclusion limit varies with a kind of substances to be excluded. In the present invention, an exclusion limit of the porous cellulose gel is measured by using globular proteins and/or viruses, and the exclusion limit is 10 6 to 1×10 9 . When the exclusion limit is more than 1×10 9 , the adsorbing amount of a substance to be removed decreases with a decrease of amount of immobilized ligand, and further a mechanical strength of gel is reduced. Particularly, in case of removing VLDL and/or LDL being giant molecules having a molecular weight of more than 1×10 6 , a porous cellulose gel having an exclusion limit of less than 1×10 6 is not practically available. On the other hand, a porous cellulose gel having an exclusion limit of from 1×10 6 to several million which is near a molecular weight of VLDL or LDL per se may be practically available to a certain extent. A preferable exclusion limit for removal of VLDL and/or LDL is 1×10 6 to 1×10 8 . With respect to a porous structure of the porous cellulose gel used in the present invention has uniformly pores at any part of the gel (hereinafter referred to as "uniform structure"). It is preferred that a porosity of the gel is not less than 20%. A shape of the carrier is selected depending on a kind of a substance to be removed. The carrier may be selected from suitable shapes such as particle, fiber, sheet and hollow fiber. In case of using a carrier in the shape of particle, although a particle having a smaller size generally shows an excellent adsorbing capacity, the pressure-drop increases with an extremely small size. Therefore, a particle having a size of 1 µm to 5000 µm is preferred. Furthermore, it is preferred that a carrier has functional groups to be utilized for the immobilization of ligand or groups to be easily activated. Examples of the group are, for instance, amino, carboxyl, hydroxyl, thiol, acid anhydride, succinylimide, chlorine, aldehyde, amido, epoxy group, and the like. The porous cellulose gel of the present invention satisfies the above all four points required for the carrier. In addition, the porous cellulose gel has various excellent advantages such as hydrophilicity due to being composed of cellulose, a large number of hydroxyl group to be utilized for immobilization, less nonspecific adsorption, and sufficient adsorbing capacity not inferior to that of sort gel due to its relatively high strength even with a large porosity. Therefore, the porous cellulose gel on which a ligand is immobilized provides a nearly ideal adsorbent. As the porous cellulose gel used in the present invention, although cellulose per se is preferred, a cellulose derivative such as an esterified cellulose or an etherified cellulose, or a mixture of cellulose and the cellulose derivatives may be employed. Examples of the cellulose derivative are, for instance, acetyl cellulose, methyl cellulose, ethyl cellulose, carboxymethyl cellulose, and the like. It is preferred that the cellulose gel is in the spherical shape. The cellulose gel is prepared, for example, by dissolving or swelling cellulose and/or a cellulose derivative with a solvent, dispersing the resulting mixture into another solvent being not admixed with the used solvent to make beads, and then regenerating the beads. The cellulose and/or cellulose derivatives may be cross-linked or not. A porosity of a porous cellulose gel may be a measure of cellulose content. The cellulose content is expressed by the following formula: Cellulose content (%)= W Vt-Vo ×100 wherein W is dry gel weight (g), Vt is a volume of column packed with gel (ml) and Vo is a void volume (ml). The cellulose content of the porous cellulose gel used in the present invention is 2% to 60%. In case of less than 2%, the mechanical strength of gel is reduced, and in case of more than 60%, the pore volume is reduced. Representative examples of the polyanion used in the present invention are as follows: Representative examples of the ligand using antigen-antibody reaction and the like are, for instance, a complement component such as C 1q , an anti-immune complex antibody, and the like for removal of immune complexes; an anti-nuclear antibody appeared in blood in general lupus erythematosus, and the like for removal of autoantibodies in autoimmune diseases; a nucleic acid base, a nucleoside, a nucleotide, a polynucleotide, DNA, RNA, and the like for removal of anti-DNA antibodies; an acetylcholine receptor fraction for removal of anti-acetylcholine receptor antibodies in myasthenia gravis; antibodies to various harmful components in blood such as an antibody to an antigen on a surface of virus for removal of hepatitis virus and an anti-DNA antibody for removal of DNA appeared in blood in general lupus erythemotosus; an anti-B cell antibody or anti-suppressor T cell antibody for removal of lymphocytes in lymphocyte disorder, and the like. Furthermore, antigens to various autoantibodies may be used for removal of autoantibodies. Examples of the polyanion compounds are, for instance, sulfated pclysaccharides such as heparin, dextran sulfate, chondroitin sulfate, chondroitin polysulfate, heparan sulfate, keratan sulfate, heparin sulfate, xylan sulfate, caronin sulfate, cellulose sulfate, chitin sulfate, chitosan sulfate, pectin sulfate, inulin sulfate, arginine sulfate, glycogen sulfate, polylactose sulfate, carrageenan sulfate, starch sulfate, polyglucose sulfate, laminarin sulfate, galactan sulfate, levan sulfate and mepesulfate, phosphorus wolframic acid, polysulfated anethole, polyvinyl alcohol sulfate, polyphosphoric acid, and/or the salts thereof and the like. Preferable examples of the above polyanion compounds are, for instance, heparin, dextran sulfate, chondroitin polysulfate, and/or the salts thereof, and particularly preferable examples are a dextran sulfate and/or the salt thereof. Examples of the salt of the above polyanion compound are, for instance, a water-soluble salt such as sodium salt or potassium salt, and the like. Dextran sulfate and/or the salt thereof are explained in more detail hereinbelow. Dextran sulfate and/or the salt thereof are sulfuric acid ester of dextran being a polysaccharide produced by Leuconostoc mesenteroides, etc., and/or the salt thereof. It has been known that dextran sulfate and/or the salt thereof form a precipitate with lipoproteins in the presence of a divalent cation, and dextran sulfate and/or the salt thereof having a molecular weight of about 5×10 5 (intrinsic viscosity of about 0.20 dl/g) are generally employed for this precipitation. However, as shown in the following Example 10 of Run Nos. (1) and (2), a porous cellulose gel on which the above-mentioned dextran sulfate and/or the salt thereof are immobilized is sometimes poor in affinity to VLDL and/or LDL. As a result of extensive studies to solve the above problems, it has now been found that dextran sulfate having an intrinsic viscosity of not more than 0.12 dl/g, preferably not more than 0.08 dl/g, and a sulfur content of not less than 15% by weight has high affinity and selectivity to VLDL and/or LDL. Furthermore, the adsorbent of the present invention employing such dextran sulfate and/or the salt thereof as a ligand has high affinity and selectivity even in the absence of a divalent cation. Although a toxicity of dextran sulfate and/or the salt thereof is low, the toxicity increases with increasing of molecular weight. From this point of view, the use of dextran sulfate and/or the salt thereof having an intrinsic viscosity of not more than 0.12 dl/g, preferably not more than 0.08 dl/g can prevent a danger in case that the immobilized dextran sulfate and/or the salt thereof should be released from a carrier. In addition, dextran sulfate and/or the salt thereof are less changed by a sterilizing procedure such as steam sterilization by autoclaving, because they are linked mainly by α(1→6)-glycosidic linkage. Although there are various methods for measuring a molecular weight of dextran sulfate and/or the salt thereof, a method by measuring viscosity is general. Dextran sulfate and/or the salt thereof, however, show different viscosities depending on various conditions such as ion strength, pH value, and sulfur content (content of sulfonic acid group). The term "intrinsic viscosity" used in the present invention means a viscosity of sodium salt of dextran sulfate measured in a neutral 1 M NaCl aqueous solution, at 25°C. The dextran sulfate and/or the salt thereof used in the present invention may be in the form of straight-chain or branched-chain. For coupling a ligand with a carrier, various methods such as physical adsorption methods, ionic coupling methods and covalent coupling methods may be employed. In order to use the adsorbent of the present invention in extracorporeal circulation treatment, it is important that the ligand is not released. Therefore, a covalent coupling method having a strong bond between ligand and carrier is used. If necessary, a spacer may be introduced between ligand and carrier. It is preferred that a gel is activated by a reagent such as a cyanogen halide, epichlorohydrin, a polyoxirane compound such as bisepoxide or triazine halide, and then reacted with a ligand to give the desired absorbent. In that case, it is preferred that a gel having a group to be activated such as hydroxyl group is employed as a carrier. In the above reagents, epichlorohydrin or a polyoxirane compound such as bisepoxide is more preferred, because a ligand is strongly immobilized on a carrier activated by using such a reagent and a release of a ligand is reduced. Epichlorohydrin and a polyoxirane compound, however, show lower reactivity, particularly lower to dextran sulfate and/or the salt thereof, because dextran sulfate and/or the salt thereof have hydroxyl group alone as a functional group. Therefore, it is not easy to obtain a sufficient amount of immobilized ligand. As a result of extensive studies, it has now been found that the following coupling method is preferred in case of using dextran sulfate and/or the salt thereof as a ligand. That is, a porous polymer cellulose gel is reacted with epichlorohydrin and/or a polyoxirane compound to introduce epoxy groups into the gel, and then dextran sulfate and/or the salt thereof is reacted with the resulting epoxy-activated gel in a concentration of not less than 3% based on the weight of the whole reaction system excluding the dry weight of the gel, more preferably not less than 10%. This method gives a good immobilizing efficiency. The amount of immobilized ligand varies depending on properties of the ligand used such as shape and activity. For sufficient removal of VLDL and/or LDL by using a polyanion compound, for instance, it is preferred that the polyanion compound is immobilized in an amount of not less than 0.02 mg/ml of an apparent column volume occupied by an adsorbent (hereinafter referred to as "bed volume"), economically 100 mg or less. The preferable range is 0.5 to 20 mg/ml of bed volume. Particularly, for removal of VLDL and/or LDL by using dextran sulfate and/or the salt thereof as a ligand, it is preferred that the amount of immobilized ligand is not less than 0.2 mg/ml of bed volume. After the coupling reaction, the unreacted polyanion compound may be recovered for reuse by purification, etc. It is preferred that the remaining unreacted active groups are blocked by ethanolamine, and the like. In accordance with the present invention, an adsorbent composed of porous-cellulose gel having an exclusion limit of 10 6 to 10 8 and a particle size of 30 to 200 µm on which sodium salt of dextran sulfate having an intrinsic viscosity of not more than 0.12 dl/g and a sulfur content of not less than 15% by weight is immobilized, is particularly suitable for removal of VLDL and/or LDL in extracorporeal circulation treatment of hypercholesterolemia. The adsorbent of the present invention may be employed for the extracorporeal circulation treatment performed by incorporating a column into extracorporeal circulation circuit and passing body fluid such as blood of plasma through the column, the column being packed with the adsorbent of the present invention. The adsorbent of the present invention can be subjected to steam sterilization by autoclaving so long as the ligand is not largely degenerated, and this sterilization procedure does not affect on micro pore structure, particle shape and gel volume of the adsorbent. The present invention is more specifically described and explained by means of the following Reference Examples and Examples. Reference Example a Biogel A5m (a commercially available agarose gel made by Biorad Co., particle size: 0.3 to 0.149 mm openings (U.S.S.) 50 to 100 mesh) as a soft gel and Cellulofine GC-700 (a commercially available porous cellulose gel made by Chisso Corporation, particle size: 45 to 105 µm) were uniformly packed, respectively, in a glass column (inner diameter: 9 mm, height: 150 mm) having filters (pore size: 15 µm) at both top and bottom of the column. Water was passed through the thus obtained column, and a relation between flow rate and pressure-drop was determined. The results are shown in Fig. 1. As shown in Fig. 1, flow rate increased approximately in proportion to increase of pressure-drop in the porous polymer cellulose gel. On the other hand, the agarose gel was consolidated. As a result, increasing pressure did not make flow rate increase. Reference Example 1 Cellulofine GC 700 (a commercially available porous cellulose gel made by Chisso Corporation, exclusion limit: 4×10 5 , particle size: 45 to 105 µm) having a uniform structure was employed as a carrier. The gel was filtered with suction, and 4 g of 20% NaOH and 12 g of heptane were added to 10 g of the suction-filtered gel. One drop of Tween 20 (nonionic surfactant) was further added to the reaction mixture which was stirred for dispersing the gel. After stirring at 40°C for 2 hours, 5 g of epichlorohydrin was added to the reaction mixture which was further stirred at 40°C for 2 hours. After the reaction mixture was allowed to stand, the resulting supernatant was discarded, and the gel was washed with water to introduce epoxy groups into the gel. To the resulting epoxy-activated gel was added 15 ml of concentrated aqueous ammonia, and the reaction mixture was stirred at 40°C for 1.5 hours, filtered with suction and washed with water to introduce amino groups into the gel. Three ml portions of the thus obtained activated gel containing amino groups was added to 10 ml of aqueous solution (pH 4.5) containing 200 mg of heparin. To the resulting reaction mixture was added 200 mg of 1-ethyl-3-(dimethylaminopropyl)-carbodiimide while maintaining the reaction mixture at pH 4.5, and then the reaction mixture was shaken at 4°C for 24 hours. After completion of the reaction, the resulting reaction mixture was washed successively with 2 M NaCl aqueous solution, 0.5 M NaCl aqueous solution and water to give the desired heparin-Cellulofine A-3. The amount of immobilized heparin was 2.5 mg/ml of bed volume. Reference Example 2 and example 3 The procedures of Reference Example 1 were repeated except that Cellulofine A-2 (exclusion limit: 7×10 5 , particle size: 45 to 105 µm) and Cellulofine A-3 (exclusion limit: 5×10 7 , particle size: 45 to 105 µm) instead of Cellulofine GC 700 were employed, respectively, to give each heparin-gel. Both Cellulofine A-2 and Cellulofine A-3 are commercially available porous cellulose gels having a uniform structure made by Chisso Corporation. The amounts of immobilized heparin were, respectively, 2.2 mg and 1.8 mg/ml of bed volume. Example 4 The procedure of Reference Example 1 were repeated except that Cellulofine A-3 having a particle size of 150 to 200 µm instead of 45 to 105 µm was employed. The amount of immobilized heparin was 1.5 mg/ml of bed volume. Example 5 To 4 ml of Cellulofine A-3 was added water to make the volume up to 10 ml, and then 0.5 mole of NalO 4 was added. After stirring at a room temperature for one hour, the reaction mixture was washed with water by filtration to introduce aldehyde groups into the gel. The thus obtained gel was suspended in 10 ml of phosphate buffer of pH 8 and stirred at a room temperature for 20 hours after addition of 50 mg of ethylenediamine. The gel was filtered off and then suspended in 10 ml of 1% NaBH 4 soluton. After reducing reaction for 15 minutes, the reaction mixture was filtered and washed with water to introduce amino groups into the gel. In 10 ml of 0.25 M NalO 4 solution was dissolved 300 mg of sodium salt of dextran sulfate. After stirring at a room temperature for 4 hours, 200 mg of ethylene glycol was added to the resulting solution and stirred for one hour. The resulting solution was adjusted to pH 8, and then the above gel containing amino groups was suspended in the solution and stirred for 24 hours. After completion of the reaction, the gel was filtered, washed with water, and then suspended in 10 ml of 1% NaBH 4 solution. The resulting suspension was subjected to reducing reaction for 15 minutes and washed with water by filtration to give the desired sodium salt of dextran sulfate-Cellulofine A-3. The amount of immobilized sodium salt of dextran sulfate was 0.5 mg/ml of bed volume. Example 6 Cellulofine A-3 was treated in the same manner as in Reference Example 1 to introduce epoxy groups into the gel. Two ml of the thus obtained epoxy-activated gel was added to 2 ml of aqueous solution containing 0.5 g of sodium salt of dextran sulfate (intrinsic viscosity 0.055 dl/g, average polymerization degree: 40, sulfur content: 19% by weight), and the reaction mixture was adjusted to pH 12. The concentration of sodium salt of dextran sulfate was about 10% by weight. The resulting reaction mixture was filtered and washed successively with 2 M NaCl aqueous solution, 0.5 M NaCl aqueous solution and water to give the desired sodium salt of dextran sulfate-Cellulofine A-3. The remaining unreacted epoxy groups were blocked with monoethanolamine. The amount of immobilized sodium salt of dextran sulfate was 1.5 mg/ml of bed volume. Example 7 To 5 g of suction-filtered Cellulofine A-3 were added 2.5 ml of 1,4-butanediol diglycidyl ether and 7.5 ml of 0.1 M NaOH aqueous solution, and the reaction mixture was stirred at a room temperature for 18 hours to introduce epoxy groups into the gel. The thus obtained epoxy-activated gel was reacted with sodium salt of dextran sulfate to give the desired sodium salt of dextran sulfate-Cellulofine A-3. The amount of immobilized sodium salt of dextran sulfate was 1.8 mg/ml of bed volume. Example 8 The procedures of Example 6 were repeated except that Cellulofine A-6 (a commercially available porous cellulose gel made by Chisso Corporation, exclusion limit: 1×10 8 , particle size: 45 to 105 µm) having a uniform structure instead of Cellulofine A-3 was employed to give the desired sodium salt of dextran sulfate-Cellulofine A-6. The amount of immobilized sodium salt of dextran sulfate was 1.2 mg/ml of bed volume. Reference Example 9a Cellulofine A-2 was treated in the same manner as in Reference Example 1 to introduce epoxy groups into the gel. To 1 ml of the thus obtained epoxy-activated gel was added 10 mg of IgG, and the reaction mixture was adjusted to pH 9 and subjected to reaction at a room temperature for 24 hours. The gel was filtered off and washed successively with 2M NaCl aqueous solution, 0.5 M NaCl aqueous solution and water. After the remaining unreacted epoxy groups were blocked with monoethanolamine solution, the desired IgG-Cellulofine A-3 was obtained. Reference Example 9b Cellulofine A-7 was treated in the same manner as in Reference Example 1 to introduce epoxy groups into the gel. The thus obtained epoxy-activated gel was reacted with DNA in the same manner as in Reference Example 9a to give the desired DNA-Cellulofine A-7. Test Example 1 Each adsorbent obtained in Examples and Reference examples 1 to 9 was uniformly packed in a column (internal volume: about 3 ml, inner diameter; 9 mm, height; 47 mm) and 18 ml of plasma containing 200 U of heparin was passed through the column at a flow rate of 0.3 ml/minute with varying the plasma origins depending on the kind of the desired substance to be removed. That is, human plasma derived from familial hypercholesterolemia, normal human plasma, normal human plasma containing about 100 µg/ml of a commercially available endotoxin, human plasma derived from rheumatism, human plasma derived from systemic lupus erythematosus and human plasma derived from mayasthenia gravis were used, respectively, for the tests of removing VLDL and/or LDL; IgG, C 1q or haptoglobin; endotoxin; rheumatoid factor; anti-DNA antibody or DNA; and anti-acetylcholine receptor antibody. The pressure-drop in the column was 0.02 bar (15 mmHg) or less throughout the test period and no clogging was observed. In each adsorbent, a substance to be removed in plasma which was passed through the column was determined to obtain a removal efficiency. The results are summarized in Table 1. With respect to the coupling method in Table 1, Epichlorohydrin method, Epichlorohydrin-ammonia method, NalO 4 -Diamine, Bisepoxide method, and CNBr method are conducted, respectively, in the same manners as in Reference Example 1 and in examples 5, and 7. Example 10 [Effects of intrinsic viscosity and sulfur content of dextran sulfate and/or the salt thereof] Cellulofine A-3 was treated in the same manner as in Reference Example 1 to introduce epoxy groups into the gel. The thus obtained epoxy-activated gel was reacted with each sodium salt of dextran sulfate having the intrinsic viscosity and sulfur content shown in the following Table 2 (Run Nos. (1) to (7)) in the same manner as in Example 6. One ml portion of the resulting each adsorbent was packed in a column, and then 6 ml of human plasma containing 300 mg/dl of total cholesterol derived from a familial hypercholesterolemia patient was passed through the column at a flow rate of 0.3 ml/minute. The removal efficiency for LDL was determined from the amount of adsorbed LDL measured by using the total amount of cholesterol as an indication. That is, the amount of cholesterol in the human plasma used was mostly derived from LDL. The results are shown in Table 2. Run No. Intrinsic viscosity (dl/g) Sulfur content (% by weight) Concentration of sodium salt of dextran sulfate in the reaction system (% by weight) Amount of immobilized sodium salt of dextran sulfate (mg/ml of bed volume) Removal efficiency (%) (1) 0.20 17.7 about 10 4.2 18 (2) 0.124 5.7 " 2.5 17 (3) 0.027 17.7 " 2 62 (4) 0.055 19.0 " 1.5 50 (5) 0.083 19.2 " 4.0 44 (6) 0.118 17.7 " 4.3 39 (7) 0.055 19.0 2.5 0.15 32 Example 11 [Effect of amount of epoxy group introduced] CSKA-3 (a commercially available porous cellulose gel made by Chisso Corporation, exclusion limit: 5×10 7 , particle size: 45 to 105 µm) having a uniform structure was treated in the same manner as in Example 1 to introduce epoxy groups into the gel. The amount of epoxy groups introduced was 30 µmoles/ml of bed volume. The gel was reacted with sodium salt of dextran sulfate (intrinsic viscosity: 0.027 dl/g, sulfur content: 17.7% by weight) in the same manner as in Example 6 except that the concentration of sodium salt of dextran sulfate based on the weight of the whole reaction system excluding the dry weight of the gel was charged. The thus obtained adsorbent was subjected to the determination of removal efficiency for LDL in the same manner as in Example 10. The results are summarized in Table 3. Carrier Amount of epoxy group introduced (µmole/ml of bed volume) Amount of immobilized sodium salt of dextran sulfate Concentration of sodium salt of dextran sulfate (% by weight) Removal efficiency (%) mg/ml of bed volume µg/µmole of epoxy group CSKA-3 30 0.15 5 2.5 36 " 30 2.3 76 13 63 Example 12 One ml portion of the adsorbent obtained in Example 10 of Run No. (3) was uniformly packed in a column having an internal volume of 1 ml, and 6 ml of normal human plasma containing LDL and HDL cholesterol in the ratio of approximately 1:1 was passed through the column. LDL in the plasma passed through the column was greatly reduced, while HDL was scarcely reduced. Example 13 One ml portion of the adsorbent obtained in Example 10 of Run No. (3) was uniformly packed in a column having an internal volume of 1 ml, and 6 ml of normal rabbit plasma containing lipoproteins of VLDL, LDL and HDL was passed through the column. The plasma obtained before and after the column treatment were, respectively, examined by polyacrylamide disc gel electrophoresis. The results are shown in Fig. 2. In Fig. 2, curves A and B show, respectively, the results obtained before and after the column treatment. The axis of ordinates indicates the absorbance at 570 nm and the axis of abscissa indicates the migration positions at which bands of VLDL, LDL and HDL were, respectively appeared. As shown in Fig. 2, VLDL and LDL were significantly adsorbed, while HDL was not. Example 14 The adsorbents obtained in Reference Example 1 and 2 and in Examples 3 and 6 to 8 were sterilized in an autoclave at 120°C for 15 minutes. Each resulting sterilized adsorbent was subjected to the determination of removal efficiency for LDL in the same manner as in Test Example 1. As a result, the removal efficiencies were not inferior to those obtained without sterilizing by autoclaving. In addition, pressure-drop was not changed.

Claims: An adsorbent for removing low and/or very low density lipoproteins from body fluid in continuous extracorporeal circulation treatment comprising a porous cellulose hard gel on which a polyanion compound is immobilized by a covalent linkage; said porous cellulose hard gel having uniformly pores at any part of the gel, having an exclusion limit of from 10 6 to 10 9 daltons, and having a cellulose content of from 2 to 60 %. The adsorbent of claim 1, wherein said polyanion compound is a sulfated polysaccharide. The adsorbent of claim 2, wherein said sulfated polysaccharide is a member selected from the group consisting of heparin, dextran sulfate, chondroitin sulfate, and their salts. The adsorbent of claim 1, wherein said exclusion limit is 10 6 to 10 8 daltons. The adsorbent of claim 1, comprising a porous cellulose gel having an exclusion limit of 10 6 to 10 8 daltons on which a polyanion compound having an affinity for a lipoprotein is immobilized. The adsorbent of claim 1, wherein said polyanion compound is immobilized in an amount of 0.02 mg to 100 mg/ml of bed volume. The adsorbent of claim 3, wherein said dextran sulfate, a salt thereof or a mixture of the dextran sulfate and the salt has an intrinsic viscosity of not more than 0.12 dl/g and a sulfur content of not less than 15% by weight. The adsorbent of claim 3, wherein said dextran sulfate, a salt thereof or a mixture of the dextran sulfate and the salt is immobilized in an amount of not less than 0.2 mg/ml of bed volume. The adsorbent of claim 1, wherein a dextran sulfate, a salt thereof or a mixture of the dextran sulfate and the salt is immobilized on a porous cellulose gel by the covalent linkage. A process of preparing an adsorbent for removing low and/or very low density lipoproteins from body fluid in continuous extracorporeal circulation treatment which comprises immobilizing a polyanion compound on a porous cellulose hard gel having a uniform structure, by reacting the porous cellulose hard gel having a uniform structure with epichlorohydrin or a polyoxirane compound to introduce epoxy groups into the gel and reacting the resulting epoxy-activated gel with the polyanion compound. The process of claim 10, wherein said polyanion compound is dextran sulfate, a salt thereof or a mixture of the dextran sulfate and the salt, said dextran sulfate, the salt thereof or the mixture of the dextran sulfate and the salt being reacted with said epoxy-activated gel in a concentration of not less than 3% based on the weight of the whole reaction system excluding the dry weight of the porous hard gel.

Inventors: HAYASHI TSUNEO, TANI NOBUTAKA, HAYASHI, TSUNEO, TANI, NOBUTAKA
Applicants: KANEGAFUCHI CHEMICAL IND, KANEGAFUCHI KAGAKU KOGYO KABUSHIKI KAISHA
Application year: 1983
Main classification: B01J20
IPC codes: A61K35, B01J20, A61M1