COATING COMPOSITION OF PARTIALLY OXIDIZED NITROCELLULOSE AND MAGNETIC PIGMENT

Abstract: A coating composition is disclosed which is comprised of partially oxidized nitrocellulose and a pigment. The composition may further contain a synthetic resin binder. The partially oxidized nitrocellulose has a nitrogen content of 8.0 to 12.5% and contains 2.0 to 100 mmol in total of carboxyl groups and/or metal salt thereof per 100 g of nitrocellulose. The use of the partially oxidized nitrocellulose provides better dispersion than conventional nitrocellulose and shor­ tens the dispersion time. Furthermore, the quantity of nitrocellulose needed to obtain a desired dispersion is less than needed with conventional nitrocellulose. The use of partially oxidized nitrocellulose does not impare the adhe­ sion of the coating composition to a substrate.

Description: Coating composition of partially oxidized nitrocellulose and pigment. The present invention relates to a coating composition such as paint and ink. More particularly, it relates to a coating composition superior in dispersion of pigment. Heretofore, because of its superior ability to disperse pigment, nitrocellulose has been commonly used for coating compositions such as paints and inks containing pigment as an essential ingredient. inhere still exists a strong demand for technology that makes it possible to efficiently and quickly produce a coating composition which contains finely dispersed pigment as an essential ingredient. Conventional nitrocellulose is not desirable because it cannot be used in an amount sufficient to achieve the necessary level of pigment dispersion, because it sometimes impairs the adhesion of a coating composition to a substrate to be coated when used in a large quantity. Accordingly, there has been a substantial need for a resin having improved dispersion ability and for a coating composition comprised of such a resin. Such a demand is strong particularly in the area of magnetic recording media such as audio tape and video tape where new technical innovations continually take place. The present inventors carried out a series of studs on the structure of nitrocellulose and the dispersibility of pigment. These studies led to the discovery that partially oxidized nitrocellulose having a nitrogen content of 8.0 to 12.5% and containing 2.0 to 100 mmol of carboxyl groups and/or metal salt thereof per 100 g of nitrocellulose exhibits marked ability to disperse pigment. The essence of this invention resides in a coating composition which comprises partially oxidized nitrocellulose and pigment, said partially oxidized nitrocellulose having a nitrogen content of 8.0 to 12.5%, preferably 9.2 to 12.2%, and containing 2.0 to 100 mmol, preferably 3.0 to 20 mmol of carboxyl groups and/or metal salt thereof per 100 g of nitrocellulose. If the nitrogen content is less than 8.0%, the partially oxidized nitrocellulose is low in solubility in organic solvents such as methyl ethyl keton, methyl isobutyl ketone, ethyl acetate, butyl acetate and toluene which are commonly used for paint and ink, and it does not exhibit its inherent ability to disperse pigment. If the nitrogen content is more than 12.5%, the nitrocellulose not only has low solubility in organic solvents such as ethyl acetate, propyl acetate and methanol but also it increases the danger of fire. In view of the solubility in organic solvents such as acetates and ketones and the safety in handling, the nitrogen content is particularly preferably within the range of from 10.0 to 12.2*. If the content of carboxyl groups and/or metal salt thereof is less than 2.0 mmcl per 100 g of nitrocellulsoe, the ability to disperse pigment is not sufficient. If it is more than 100 mmol per 100 g of nitrocellulose, when dissolved in an organic solvent, viscosity of the resulting solution markedly increases presumably due to crosslinking of the carboxyl groups and/or metal salt thereof between the molecules. Therefore it becomes difficult to disperse a pigment.Concerning the dispersibility of pigment and the viscosity, it is preferably within the range of from 3.0 to 20 mmol per 100 g of nitrocellulose. The carboxyl group content is determined as follows: Accurately weigh about 1.5 g of partially oxidized nitrocellulose into a 100-ml Erlenmeyer flask. Add about 50 ml of a 0.1 N HCl aqueous solution. Shake and let stand for about 2 hours. Filter the contents and wash the partially oxidized nitrocellulose with deionized water thoroughly until the washings become completely neutral. Place the washed partially oxidized nitrocellulose in a beaker together with a small amount of water. Add 50 ml of a 0.05 M aqueous solution of calcium acetate to the beaker. Shake and let stand overnight. Take 20 ml of the supernatant liquid from the beaker, and titrate with a 0.01 N NaCH aqueous solution using phenolphthalein indicator. Perform the blank test for 20 ml of a 0.05 M calcium acetate aqueous solution. The carboxyl group content can be calculated according to the following formula. Carboxyl Group = NaOR titrated(ml)-NaOH titrated in black test(m1.) x Content 20 quantity of water*(g) + 50 Sample weight * Water: placed in a beaker together with the washed partially oxidized nitrocellulose The content of the metal salt of the carboxyl groups is determined as follows: First, measure the carboxyl group content of partially oxidized nitrocellulose in the same manner as described above. Accurately weigh about 1.5 g of the same partially oxidized nitrocellulose into a beaker. Add 50 ml of a 0.05 M aqueous solution of calcium acetate to the beaker. Shake and let stand overnight. Take 20 ml of the supernatant liquid from the beaker, and titrate with a 0.01 N NaOH aqueous solution using phenolphthalein indicator. Perform the blank test for 20 ml of a 0.05 M calcium acetate aqueous solution. The content of metal salt of the carboxyl groups can be calculated according to the following formula. Content of Metal Salt = Carboxyl Group Content of Carboxyl Groups NaOH titrated (ml)-NaHO titrated in blank test (ml)/20 50 x sample The molar ratio of the carboxyl group content to the content of metal salt of carboxyl groups in the partially oxidized nitrocellulose of this invention is 100/0 to 0/100 depending on the surface properties, e.g., pH, of the pigment used. The metal in the metal salt of the carboxyl groups in this invention includes lithium, beryllum, sodium, magnesium, potassium, calcium, manganese, iron, cobalt, nickel, copper and zinc. The partially oxidized nitrccellulose containing carboxyl groups and/or metal salt thereof is usually prepared by oxidizing nitrocellulose, or oxidizing raw material cellulose and nitrifying the oxidized cellulose, and optionally performing a post treatment. The oxidation of nitrocellulose is accomplished by adding, with heating to 20 to 1000C, an oxidizing agent such as nitrogen oxides, hypochlorous acid, chlorous acid, chloric acid, perchloric acid, permanganic acid, dichromic acid, metal salts (e.g., Na, Ke, etc.) of the aforesaid acids, or hydrogen peroxide to an aqueous slurry of nitrocellulose or a solution of nitrocellulose dissolved in an organic solvent such as acetone, methyl ethyl ketone, methyl isobutyl ketone, ethyl acetate and butyl acetate. The ketones are preferably used as the organic solvent. of the oxidizing agents, nitrogen oxides, hydrogen peroxide and hypochlorous acid or its sodium salt are preferably used. The oxidation with nitrogen oxides can be performed either by externally introducing nitrogen oxides into the reaction system or by generating nitrogen oxides in the reaction system e.g., utilizing the reaction as follows: 4HUN03 + Cu-- P Cu(N03)2 + 2S20 + 2NO 2 2 The nitrofication of oxidized celluose is accomplished as follows: Cellulose raw material is made into an aqueous slurry. Examples of cellulose raw material include cotton linter, wood pulp, cotton, hemp and jute, with cotton linter-and wood pulp being preferred. The slurry is heated to 20 to 100 0C together with the oxidizing agent described above to give partially oxidized cellulose. The partially oxidized cellulose thus prepared is then nitrified with a nitric acid or a nitric acid/sulfuric acid mixture. The post treatment is accomplished by adding the thus obtained partially oxidized nitrocellulose in an aqueous solution of hydrochloric acid, metal hydroxides (e.g. NaOH, KOH and Ca(OE)2) or metal salts of acetic acid. The partially oxidized nitrocellulose containing carboxyl groups can be obtained using nitrogen oxides or the acids described above as the oxidizing agent. In order to completely or partially convert the carboxy groups into a metal salt form, the partially oxidized nitrocellulose may be subjected to the post treatment with metal hydroxides or metal salts of acetic acid. When metal salts of the aforesaid acids (e.g., sodium hypochlorite) are used as the oxidizing agent. the partially oxidized nitrocellulose containing metal salt of carboxyl groups can be obtained, the metal salt of which may be completely or partially converted to carboxy groups by the post treatment with hydrochloric acid. Examples of pigments used in this invention include extender pigments such as baryta, precipitated barium sulfate, chalk, precipitated calcium carbonate, whiting, clay, polishing powder, talc, diatomaceous earth, silica white, alumina white, gypsum, satin white, gloss white, bentonite, calcium silicate, precipitated magnesium carbonate, aluminum silicate, and calcium molybdate; white inorganic pigments such as rutile titanium dioxide, anatase titanium dioxide, zinc sulfide, white lead, lithopone, zinc white, basic. lead sulfate, zirconium oxide, antimony white, tin oxide, and lead silicate; black inorganic pigments such as. carbon black, soot, graphite, iron black, silica black, and chrome black; gray inorganic pigments such as zinc dust, lead suboxide, and silicon carbide; red inorganic pigments such as red oxide, red lead, vermillion, cadmium red, molybdenum red, cuprous oxide, and antimony red; brown inorganic pigments such as amber, iron oxide powder, Siena, and copper brown; yellow inorganic pigments such as lead chromate, zinc chromate, cadmium yellow, lead cyanamide, synthetic yellow ocher, titanium yellow, antimony yellow, barium yellow, mineral yellow, stone yellow; green inorganic pigments such as chrome green, chrome oxide green, guinet's green, zinc green, cobalt green, emerald green, cobalt-chrome green, manganese green, and Egypt green; blue inorganic pigments such as Prussian blue, ultramarine blue, cobalt blue, cerulean blue, manganese blue, molybdenum blue, copper sulfide, amd Egypt blue; purple inorganic pigments such as manganese purple cobalt purple, mars purple, and chromium chloride; metal powder pigments such as aluminum powder, copper powder, and brass powder; magnetic oxide pigments such as t-Fe203, Fe304, cobalt-absorbed or -containing product thereof, and Cr02 ; magnetic metal pigments such as Fe, Fe-Co, and Fe-Co-Ni; yellow organic pigments such as Eansa Yellow, Benzidine Yellow, and Parmanent Yellow HR; red organic pigments such as Toluidine Red, Lake Red, Watchung Red, and Chinacridone Red; blue organic pigments such as Cu-Phthalocyanine Blue and Three Blue RS; and green organic pigments such as Cu-Phthalocyanine Green and Green Gold; and mixtures thereof. Of these, magnetic oxide pigments, magnetic metal pigments, carbon black, titanium oxides and phthalocyanines are preferably used in the present invention. The magnetic oxide pigments and magnetic metal pigments must be capable of performing magnetic recording. These pigments are comprised of anisotropic acicular particles having an axis ratio (long axi/short axis) of 5/1 to 15/1, the long axis being 0.1 to 2-micron long. The partially oxidized nitrocellulose containing carboxyl groups and/or metal salt thereof exhibits satisfactory dispersion of pigments, but it may be incorporated with a synthetic resin binder for improved durability and fastness. The weight ratio of the partially oxidized nitrocellulose to the synthetic resin binder is generally from 0.1 to 4/1 depending on use of the coating composition. The synthetic resin binder preferably has a molecular weight of 2,000 to 100,000. Examples of useful synthetic resin binders includes alkyd resin, oil-modified alkyd resin, fatty acid-modified alkyd resin, phenol-modified alkyd resin, rosin-modified alkyd resin, vinyl-modified alkyd resin, rosin-modified maleic resin, maleic resin, rosin-modified phenolic resin, nitrocellulose, ethyl cellulose, cellulose acetate butyrate; butylated melamine resin, butylated urea resin, epoxy resin, polyurethane resin; polyvinyl chloride resin; vinyl chloride/vinyl acetate copolymer resin; vinyl chloride/vinyl acetate/vinyl alcohol copolymer resin; vinyl chloride/vinyl acetate/maleic acid copolymer resin; vinyl acetate resin; acrylic resin, styrene resin; coumaroneindene resin; and mixtures thereof Polyurethane resin and vinyl chloride/vinyl acetate/vinyl alcohol copolymer resin are preferably used. It is also preferred to use polyisocyanate prepolymer in combination with these resins. The weight ratio of the pigment to the partially oxidized nitrocellulose or the total of partially oxidized nitrocellulose and synthetic resin binder is 10/1 to 0.2/1,preferably 5/1 to 0.3/1, depending on use of the coating composition and type of the pigment used. The coating composition of this invention may be incorporated with dispersants such as alkylpolyether sulfite, alkylbenzene sulfonate, sorbitan alkylate, and lecithin; antisegregation agents such as silicone, lecithin, and lead naphthenate; W absorbers such as benzophenone and cinnamic ester; drying catalysts such as naphthate, resinate, linoleate, octoate, tallate, and other metal soaps; plasticizers such as phthalate ester, phosphate ester, sebacate ester, adipate ester, and epoxy derivatives; antistatic electricity agents such as carbon black; and lubricants such as metal salts of saturated or unsaturated fatty acids. The e weight ratio of each additive to the pigment is 0.001/1 to 0.1/1 depending on use of the coating composition and type of the pigment used. The coating composition of this invention is prepared in the same manner as for the ordinary coating composition as described in e.g., Shigezo Tochihara, Progress in organic Caotings, vol. 10, pp. 195-204 (1982). For example, the coating composition is prepared by thoroughly mixing the partially oxidized nitrocellulose, a pigment and an organic solvent such as methyl ethyl ketone, methyl isobutyl ketone, ethyl acetate, butyl acetate and toluene in a kneader, ball mill, sand mill, attritor mill, two-roll mill, or three-roll mill. If desired, a synthetic resin binder and plasticizer and other additives are added and dispersed uniformly. In another method, the partially oxidized nitrocellulose, a pigment, and an organic solvent are mixed using the above-mentioned mixer, and then the organic solvent is evaporated to form small solid pieces. Thereafter the solid pieces are dissolved in an organic solvent with a synthetic resin binder azid plasticizer. The invention will be now described in detail with reference to the following examples, in which "parts" means "parts by weight". However, the invention is not limited to these examples. Preparation Example 1 100 part of HIG20 second-nitrocellulose (a product of Asahi Kasei Kogyo Kabsuhiki Kaisha) containing 30% of isopropyl alcohol was dissolved in 300 parts of acetone. The solution was placed in an Erlenmeyer flask equipped with a reflux condenser. 4 parts of a 35% hydrogen peroxide solution was added. The flask was heated for 3 hours on a water bath at 70 C. The e content was poured into a large amount of water to give partially oxidized nitrocellulose. This product was designated as Sample A. The nitrogen content in Sample A was 11.20%, and the content of carboxyl groups was 3.6 mmol per 100 g of nitrocellulose. One part of Sample A was added to 20 parts of a 0.005 M aqueous solution of calcium acetate. After standing at room temperature of 3 hours, the solution was poured into a large amount of water. The precipitate was filtered and washed until the washings became neutral. Thus, there was obtained Sample B. Sample B had the nitrogen content of 11.15% and contained 3.6 mmol of carboxyl groups per 100 g of nitrocellulose and 1.4 mmol of metal salt of carboxyl groups per 100 g of nitrocellulose. One part of Sample A was added to 20 parts of a 0.01 M aqueous solution of ferrous acetate. After standing at room temperature for 1 hour, the solution was poured into a large amount of water. The precipitate was filtered and washed until the washings became neutral. Thus, there was obtained Sample C. Sample C had the nitrogen content of 11.12% and contained 3.6 mmol of carboxyl groups per 100 g of nitrocellulose and 1.8 mmol of metal salt of carboxyl groups per 100 g of nitrocellulose. Preparation Example 2 100 parts of H20 second-nitrocellulose (a product of Asahi Kasei Kogyo K.K.) wet with 30% of water was placed in a beaker containing 500 parts of water. 200 parts of sodium hypochlorite was added,followed by heating with stirring for 1 hour on a water bath at 50 C. The solution was poured into a large amount of water to give partially oxidized nitrocellulose. This product was designated as Sample D. Sample D had the nitrogen content of 11.60% and contained 7.20 mol of carboxyl groups. per 100 g of nitrocellulose and 5.80 mmol of metal salt of cboxyl groups per 100 g of nitrocellulose. One part of Sample D was added to 20 parts of a 0.05 N NCl aqueous solution. After standing at room temperature for 2 hours, the solution was poured into a large amoubt of water. The precipitate was filtered and washed until the washings became neutral. Thus, there was obtained Sample E. Sample E had the nitrogen content of 11.68% and contained 7.20 mmol of carboxyl groups per 100 g of nitrocellulose and 0.50 mmol of metal salt of carboxyl groups per 100 g of nitrocellulose. Preparation Example 3 100 parts of purified linter was placed in a desiccator, and 5.8 parts of liquid nitrogen oxide was added. After standing at room temperature for 48 hours, the content was washed with water and dried to give partially oxidized cellulose. This product was then reacted with a mixed acid of B2S04/HN%/H20 (59/23/18 by weight) for minutes to give partially oxidized nitrocellulose. The e nitrogen content was 10.42%, and the content of carboxyl groups was 4.8 mmol per 100 g of nitrocellulose. This product was designated as Sample F. The above procedure was repeated except that 2.9 parts of liquid nitrogen oxide was added, to thereby give partially oxidized nitrocellulose. The product was designated as Sample G (comparison). The nitrogen content was 10.98%, and the content of carboxyl groups was 1.8 mmol per 100 g of nitrocellulose. Further the above procedure as in the preparation of Sample F was repeated except that pulp was used in place of purified linter and a mixed acd of H2 SO4/HNO3/H2O (25/50/25 by weight) was used, to thereby give partially oxidized nitrocellulose. The product was designated as Sample E (comparison). The nitrogen content was 7.8%, and the content of carboxyl groups was 4.6 mmol per 100 g of nitrocellulose. Example 1 The following components were mixed and dispersed in a ball mill of 6 hours. Parts Partially oxidized nitrocellulose* 5 Acrylic resin** 10 Cadmium yellow 3.8 Chrome orange 4.5 Futile titanium dioxide 1.7 Methyl ethyl ketone 35 Methyl isobutyl ketone 20 * Samples A, B, C, D,E, and F ** nAcrydic A 125-50", Åa product of Dainippon Ink & Chemicals, Inc. The resulting mixture-was applied to a polished plate glass using a bar coater, followed by drying. Dispersion of pigment was evaluated by measuring gloss by the method described later and particle diameter using a grindometer The results are shown in Table 1. Example 2 The following components were mixed and dispersed in a ball mill for 12 hours. Parts Partially oxidized nitrocellulose* 10 Alkyd resin** 10 Dibutyl phthalate 3 Carbon black 4 Ethyl acetate 20 Methyl isobutyl ketone 10 Toluene 25 * Samples A, B, C, D. E, and F ** "Bekkosole 1308", a product of Dainippon Ink & Chemicals, Inc. The resulting mixture was applied onto a polished plate glass uisng a bar coater, followed by drying. Dispersion of. pigment was evaluated by measuring gloss by the method described later and particle diameter using a grindometer. The results are shown in Table 2. Example 3 The following components were mixed and dispersed in a ball mill for 20 hours. Parts Partially oxidized nitrocellulose* 5 Urethane elastomer** 20 r 2 3 40 (lon# #xis 0.5 , short axis 0.06 ) Methyl ethyl ketone 12 Methyl isobutyl ketone 25 Toluene 25. * Samples A, B, C, D, E, and F ** "Esten 5703", a product of Goodrich Company The resulting mixture was applied onto a polished plate glass using a bar coater, billowed by drying. Dispersion of pigment was evaluated by measuring gloss by the method described later and particle diameter using a grindometer. The results are shown in Table 3 Comparative Example 1 Example 1 was repeated, except that the partially oxidized nitrocellulose was replaced by H1/4 second-nitrocellulose and E1/8 second-nitrocellulose (both made by Asahi Kasei Kogyo K.K.). The results are shown in Table t. Incidentally, the H1/4 second-nitrocellulose had the nitrogen content of 11.70% and contained 1.0 mmol of carboxyl groups per 100 g of nitrocellulose. The 111/8 second-nitrocellulose had the nitrogen content of 11.70% and contained 1.2 mmol of carboxyl groups per 100 g of nitrocellulose. Comparative Example 2 Example 2 was repeated, except that the partially oxidized nitrocellulose was replaced by 111/2 second-nitrocellulose, 111 secondnitrocellulose (both made by Asahi Kasei Kogyo K.K.). The results are shown in Table 2; Incidentally, the 111/2 second-nitrocellulose had the nitrogen content of 11.76% and contained 1.0 mmol of carboxyl groups per 100 g of nitrocellulose. The Hi second-nitrocellulose had the nitrogen content of 11.78% and contained 0.7 mmol of carboxyl groups per 100 g of nitrocellulose. Comparative Example 3 Example 3 was repeated, except that the partially oxidized nitrocellulose was replaced by H1/4 second-nitrocellulose and Samples G and H. The results are shown in Table 3. T a b l e 1 Content of Partially Content of metal salt oxidized Nitrogen carboxyl of carboxyl Particle NC or NC content groups groups Gloss diameter (%) (mmol) (mmol) ( ) Example 1 A 11.20 3.6 0 72 below 10 " B 11.15 3.6 1.4 78 below 10 " C 11.12 3.6 1.8 79 below 10 " D 11.60 7.2 5.8 84 below 10 " E 11.68 7.2 0.5 78 below 10 " F 10.42 4.8 0 74 below 10 Comparative Example 1 H1/4 11.70 1.0 0 44 30 to 40 " H1/8 11.70 1.2 0 39 30 to 40 * NC stands for nitrocellulose. T a b l e 2 Content of Partially Content of metal salt oxidized Nitrogen carboxyl of carboxyl Particle NC or NC content groups groups Gloss diameter (%) (mmol) (mmol) ( ) Example 2 A 11.20 3.6 0 82 below 10 " B 11.15 3.6 1.4 80 below 10 " C 11.12 3.6 1.8 79 below 10 " D 11.60 7.2 5.8 84 below 10 " E 11.68 7.2 0.5 85 below 10 " F 10.42 4.8 0 80 below 10 Comparative Example 2 H1/2 11.76 1.0 0 54 30 to 40 " H1 11.78 0.7 0 50 30 to 40 T a b l e 3 Content of Partially Content of metal salt oxidized Nitrogen carboxyl of carboxyl Particle NC or NC content groups groups Gloss diameter (%) (mmol) (mmol) ( ) Example 3 A 11.20 3.6 0 74 below 10 " B 11.15 3.6 1.4 76 below 10 " C 11.12 3.6 1.8 77 below 10 " D 11.60 7.2 5.8 82 below 10 " E 11.68 7.2 0.5 78 below 10 " F 10.42 4.8 0 76 below 10 Comparative Example 3 H1/4 11.70 1.0 0 31 30 to 40 " Sample G 10.98 1.8 0 38 30 to 40 " Sample H 7.8 4.6 0 23 30 to 40 Example 4 Example 1 was repeated, except that the partially oxidized nitrocellulose was replaced by Samples C and D and the mixing time was changed to 2 hours and 4 hours. Particle diameter was measured with a grindometer and the gloss of the coating film was measured by the method mentioned later The results are shown in Table 4. Table 4 Partially Mixing time Particle oxidized NC in ball mill Gloss diameter (hours) (p) Sample C 2 45 30 to 40 Sample C 4 67 10 to 20 Sample D 2 50 20 to 30 Sample D 4 71 below 10 Example 5 Example 2 was repeated, except that the partially oxidized nitrocellulose was replaced by Sample E in an amount of 3 parts and 6 parts and the quantity of alkyd resin (Bekkosole 1308, a product of Dainippon Ink & Chemicals ,Inc.) was changed to 17 parts and 14 parts. Particle diameter, gloss, and adhesion were measured. The results are shown in Table 5 together with the results in Comparative Example 2. Table 5 Partially Quantity oxidized Quantity of alkyd Particle NC or NC of NC resin Gloss diameter Adhesion (parts) (parts) Sample E 3 17 58 30 to 40 100/100 Sample E 6 14 72 10 to 20 100/100 H1/2 10 10 54 30 to 40 50/100 E1 10 10 sq 30 to 40 50/100 Measurement of gloss > The gloss of the coating film was measured using a digital variable angle gloss meter at 60o/600. (made by Suga Shikenki Company). The standard black board was assigned a specular gloss value of 91.5. Higher gloss shows better dispersion of pigment. < Measurement of particle diameter with a grindometer > A portion. of the mixed coating composition was poured into the groove (deeper one) of a grindometer. The scraping blade was moved to the target 0 at a uniform. speed. within one second. The state of distribution of particles was read on the scale. < Measurement of adhesion > A portion. of the mixed coating composition was applied onto a treated polypropylene film using a bar coater in a dry thickness of 10 p. After standing overnight, the film was dried at 600c for 6 hours in a constant temperature bath. After. cooling,adhesive cellophane tape was pressed down over the coating by rubbing five times with a finger, and then jerked away. The ratio of the area of the reamining coating to the area of the original coating was given as a measure of adhesion. It is seen from the above results that the use of partially oxidized nitrocellulose offers better dispersion than conventional nitrocellulose, and also shortens the dispersion time if the same degree of dispersionas conventional nitrocellulose is to be achieved. In addition, the partially oxidized nitrocellulose is much improved in the ability to disperse pigment. as compared with conventional nitrocellulose Therefore, the quantity can be reduced to achieve the same level of dispersion as would be accomplished by conventional nitrocellulose. Thus, according to this invention, it is possible to produce a coating composition which is not impaired in adhesion to the substrate. While the invention has been described in detail and with reference to specific embodiment thereof, it will be apparent to one skilled in the art that various changes and modifications can be made therein without departing from the spirit and scope thereof.

Claims: C L A I M S. 1. A coating composition, comprising: partially oxidized nitrocellulose; and a pigment, wherein said partially oxidized nitrocellulose has a nitrogen content of 8.0 to 12.5% and contains 2.0 to 100 mmol in. total-. of carboxyl groups and/or metal salt thereof per 100 g of nitrocellulose. 2. A coating composition as claimed in claim 1, further comprising a synthetic resin binder. 3. A coating composition as claimed in claim 1 or 2 ,wherein the partially oxidized nitrocellulose is prepared by oxidizing a cellulose selected from the group consisting of cotton linter and wood pulp and then nitrifying the oxidized cellulose. 4. A coating composition as claimed in claim 1 or 2, wherein the partially oxidized nitrocellulose is prepared by oxidizing a nitrocellulose with an oxidizing agent. 5. A coating composition as claimed in claim L or 2,wherein the pigment is selected from the group consisting of carbon black, titanium oxides, and phthalocyanines. 6. A coating composition as claimed in claim 1 or 2, wherein the pigment is a magnetic oxide pigment or a magnetic metal pigment. 7. A coating composition as claimed in claim 1 or 2, wherein the pigment is selected from the group consisting of y-Fe203, Fe304, Coadsorbed or -containing product thereof and CrO2, the pigment having an axis ratio (long axis/short axis) of 5/1 to 15/1 wherein the long axis is within the range of 0.1 to 2 microns long. 8 A coating composition as claimed in claim 1 or 2, wherein the pigment is selected from the group consisting of Fe, Fe-Co, or Fe-Co-Ni, the pigment having an axis ratio of 5/1 to 15/1, wherein the long axis is within the range of 0.1 to 2 microns long. 9. A coating composition as claimed in claim 1, wherein the weight ratio of the pigment to the partially oxidized nitrocellulose is within the range of 10/1 to 0.2/1. 10. A coating composition as claimed in claim 2, wherein the weight ratio of the pigment to the total of partially oxidized nitrocellulose and synthetic resin binder is within the range of 10/1 to 0.2/1. 11. A coating composition as claimed in claim 2, wherein the weight ratio of the partially oxidized nitrocellulose to the synthetic resin binder is within the range of from 0.1/1 to 4/1. 12. A coating composition as claimed in claim 1 lcr 2, wherein the partially oxidized nitrocellulose has a nitrogen content of 10.0 to 12.28 and contains 3,0 to 20 mmol in total of carboxyl groups and/or metal salt thereof per 100 g of nitrocellulose.

Inventors: ISHINO, TEIICHI, KAI, RIKIYA ASAHI KASEI ARAHIRA SHATAKU, NAGATOMO, SUEO, UEDA, IKUO
Applicants: ASAHI KASEI KOGYO KABUSHIKI KAISHA
Application year: 1983
Main classification: C08B5
IPC codes: C08B5, C08L1, G11B5, C08K5, C08K3, C09D101