RARE EARTH DOPED YTTRIA-GADOLINIA CERAMIC SCINTILLATORS AND METHODS FOR MAKING

Abstract: Rare-earth-doped, polycrystalline yttria-gadolinia cera­ mic scintillators with high density, optical clarity, uniformity, cubic structure and which are useful in the detection of x-rays, include one or more of the oxides of rare earth elements Eu, Nd, Yb, Dy, Tb, and Pr as activators. The ceramic scintillator may also include CaO and SrO as afterglow reducers. Sintering, sintering combined with gas hot isostatic pressing, and hot pressing methods for prepar­ ing the ceramic scintillators are also described.

Description: RARE EARTH DOPED YTTRIA-GADOLINIA CERAMIC SCINTILLATORS AND METHODS FOR MAKING The present invention relates to rare-earth doped ceramic scintillators for computerized tomography (CT) and other x-ray, gamma radiation, and nuclear radiation detecting applications. More specifically, the invention relates to rare-earth-doped, polycrystalline, yttria/gadolinia (Y203/Gd203) ceramic scintillators. Computerized tomography scanners are medical diagnostic instruments in which the subject is exposed to a relatively planar beam or beams of x-ray radiation, the intensity of which varies in direct relationship to the energy absorption along a plurality of subject body paths. By measuring the x-ray intensity (i.e., the x-ray absorption) along these paths from a plurality of different angles or views, an x-ray absorption coefficient can be computed for various areas in any plane of the body through which the radiation passes. These areas typically comprise approximately a square portion of about 1 mm x 1 mm. The absorption coefficients are used to produce a display of, for example, the bodily organs intersected by the x-ray beam. An integral and important part of the scanner is the x-ray detector which receives the x-ray radiation which has been modulated by passage through the particular body under study. Generally, the x-ray detector contains a scin tillator material which, when excited by the impinging x-ray radiation, emits optical wavelength radiation. In typical medical or industrial CT applications, the optical output from the scintillator material is made to impinge upon photoelectrically responsive materials in order to produce electrical output signals, the amplitude of which is directly related to the intensity of the impinging x-ray radiation. The electrical signals are digitized for processing by digital computer means which generates the absorption coefficients in a form suitable for display on a cathode ray tube screen or other permanent media. Due to the specific and demanding computerized tomography requirements, not all scintillator materials which emit optical radiation upon excitation by x-ray or gamma ray radiation are suitable for CT applications. Useful scintillators must be efficient converters of x-ray radiation into optical radiation in those regions of the electromagnetic spectrum (visible and near visible) which are most efficiently detected by photosensors such as photomultipliers or photodiodes. It is also desirable that the scintillator transmit the optical radiation efficiently, avoiding optical trapping, such that optical radiation originating deep in the scintillator body escapes for detection by externally situated photodetectors. This is particularly important in medical diagnostic applications where it is desirable that x-ray dosage be as small as possible to minimize patient exposure, while maintaining adequate quantum detection efficiency and a high signal-to-noise ratio. Among other desirable scintillator material properties are short afterglow or persistence, low hysteresis, high x-ray stopping power, and spectral linearity. Afterglow is the tendency of the scintillator to continue emitting optical radiation for a time after termination of x-ray excitation, resulting in blurring, with time, of the information-bearing signal. Short afterglow is also highly desirable in applications requiring rapid sequential scanning such as, for example, in imaging moving bodily organs. Hysteresis is the scintillator material property whereby the optical output varies for identical x-ray excitation based on the radiation history of the scintillator. This is undesirable due to the requirement in CT for repeated precise measurements of optical output from each scintillator cell and where the optical output must be substantially identical for identical x-ray radiation exposure impinging on the scintillator body. Typical detecting accuracies are on the order of one part in one thousand for a number of successive measurements taken at relatively high rate. High x-ray stopping power is desirable for efficient x-ray detection. Spectral linearity is another important scintillator material property because x-rays impinging thereon have different frequencies. Scintillator response must be substantially uniform at all x-ray frequencies. Among scintillator phosphors considered for CT use are monocrystalline materials such as cesium iodide (CsI), bismuth germanate (Bi4Ge3012), cadmium tungstate (CdWO4), and sodium iodide (NaI). Many of the aforementioned materials typically suffer from one or more deficiencies such as excessive afterglow, low light output, cleavage, low mechanical strength, hysteresis, and high cost. Many monocrystalline scintillators are also subject to hygroscopic attack. Known polycrystalline scintillators are efficient and economical. However, due to their polycrystalline nature, such materials are not efficient light propagators and are subject to considerable optical trapping. Internal light paths are extremely long and tortuous, resulting in unacceptable attenuation of optical output. Fabrication of monocrystalline scintillators from multicomponent powder constituents is typically not economical and is frequently impractical. The multicomponent powder composition must be heated to a temperature above its melting point, and ingots of dimensions larger than those of each detector channel are grown from the melt. Considering the size of the bars required and the temperatures involved, the process is difficult in and of itself. In addition, some materials exhibit phase changes while cooling which would cause the crystals to crack when cooled after the growing process. Furthermore, single crystals tend to be susceptible to the propogation of lattice defects along the crystal planes. U.S. Patent 4,242,221 describes methods for fabricating polycristalline phosphors into ceramic-like scintillator bodies for use in CT. The present invention provides improved ceramic scintillator bodies for use in CT. The present invention provides improved ceramic scintillators composed of yttria-gadolinia and including a variety of rare earth activators for enhancing luminescent efficiency. The terms "transparency" and "translucency", as used herein, describe various degrees of optical clarity in the scintillator material. Typically, the inventive scintillator materials exhibit an optical attenuation coefficient of less than 100 cm , as measured by standard spectral transmittance tests (i.e., "narrow" angle transmission) on a polished scintillator material plate, at the luminescent wavelength of the respective ion. The most desirable scintillator materials have lower attenuation coefficients and hence higher optical clarity (transparency). Rare-earth-doped, polycrystalline, yttria-gadolinia ceramic scintillators having high optical clarity, density, uniformity, cubic structure, and which are useful in CT include between about 5 mole percent and approximately 50 mole percent gadolinia (Gd203), and between about 0.02 and 12 mole percent of at least one rare-earth activator oxide selected from the group consisting of Emu203, Nd203, Yb203, Dy203, Tb203, and Pr203, the remainder being yttria (Y203). The invention also relates to methods for preparing an yttria-gadolinia ceramic scintillator body. One method includes the step of preparing a multicomponent powder containing between about 5 and 50 mole percent God 203 and between about 0.02 and 12 mole percent of at least one rare-earth activator oxide selected from the group consisting of Emu203, Nd203, Yb203, Dry203 Tub203, and Per203, the remainder of the powed being Y203. The multi-component powder is cold pressed to form powder compacts which are sintered to form the yttria-gadolinia polycrystalline ceramic scintillator body. A second method includes the step of preparing a multicomponent powder including Y203, Gd203, and at least one rare hearth activator oxide selected from the group consisting of Eu203, Nd203, Yb 203, Dy203, Tb203, and Pr203. The multi-component powder is pressed to form powder compacts which are sintered to the closed porosity stage. The sintered compacts are then gas hot isostatically pressed at elected temperature to form the polycrystalline ceramic scintillator. Yet another method includes the step of preparing a multicomponent powder containing about 5 and 50 mole percent Gd203, and at least one rare-earth activator oxide selected from the groupe consisting of Eu203, Nd 0 Tb Yb,O,DYZ03 Tb2Q3, and 2 3' yb203, Dy203, L Pr203, the remainder of the multicomponent powder being Y203. The multicomponent powder is pressed under vacuum at a first temperature and pressure. The temperature and pressure are then increased and maintained so as to form the polycristalline ceramic scintillator body. The scintillator may also include strontia (SrO) or calcia (CaO) in quantities of between 0.1 mole percent to 2 nole percent for reducing lurrinescent afterglow. It is an object of the invention to provide polycristalline, yttria-gadolinia ceramic scintillators having high x-ray stopping power and high radiant efficiency. It is another object of the invention to provide rare-earth-doped, polycrystalline yttria-gadolinia ceramic scintillators having high optical clarity, high density, high uniformity, cubic structure and which are particularly useful in CT and other x-ray detecting applications. It is still another object of the invention to provide polycrystalline, yttria-gadolinia ceramic scintillators exhibiting low luminescent afterglow-and low hysteresits. It is yet another object of the invention to provide a sintering process for preparing rare-earth-doped, transparent-to-translucent polycrystalline yttria-gadolinia ceramic scintillators having cubic crystalline structure, high x-ray stopping power, high density, high unifornity, high radiant efficiency and which are useful in radiation detectors such as those used in CT and digital radiography. It is a further object of the invention to provide a sintering and gas hot isostatic pressing process for preparing rare-earth-doped, transparent-to-translucent polycrystalline yttria-gadolinia ceramic scintillators having cubic crystalline structure, high x-ray stopping power, high density, high uniformity, high radiant efficiency and which are useful in radiation detectors such as those used in CT and digital radiography. It is another object of the invention to provide a sintering process for preparing polycrystalline yttria-gadolinia ceramic scintillators exhibiting low luninescence afterglow. It is a further object of the invention to provide a vacuum hot pressing process for preparing rare-earth-doped, transparent-to-translucent polycrystalline yttria-gado linia ceramic scintillators having cubic crystalline structure, high x-ray stopping power, high density, high uniformity, high radiant efficiency and which are useful in radiation detectors such as those used in CT and digital radiography. It is another object of the invention to provide a vacuum hot pressing process for preparing polycrystalline yttria-gadolinia ceramic scintillators exhibiting low luminescence afterglow. The invention itself, however, both as to its organization and method of operation, together with further objects and advantages thereof, may best be understood by reference to the following description taken in conjunction with the accompanying drawings. Fig.l is a graph depicting the effect of increased thoria -(ThO2) content on the light output of a yttria-gadolinia ceramic scintillator containing 3 mole percent Eu203. Fig. 2 is a graphical illustration of the dependence of the relative light output on Emu 203 activator concentration in an inventive scintillator material containing 25 mole percent Gd203. Fig. 3a illustrates graphically the dependence of scintillator efficiency on yttria-gadolinia compositional ratio of an inventive ceramic scintillator containing 3 mole percent Eu203. Fig. 3b is a graph illustrating 73 keV x-ray stopping power versus yttria-gadolinia compositional ratio of an inventive ceramic scintillator. Fig.4 is a graphical illustration of the effect of increased Yob 203 concentrations on scintillator material afterglow. Fig.5 depicts graphically the relative light output of an inventive scintillator material with increased Yob 203 content. Fig.6 is a graphical illustration of the effect of increased SrO concentration on scintillator material afterglow. U.S. Patent 3,640,887, describes the manufacture of transparent polycrystalline ceramic bodies. The bodies includes the oxides of thorium, zirconium and hafnium and mixtures thereof with oxides of rare earth elements 58 through 71 of the Periodic Table. The bodies may optionally include yttria. The average ionic radius of the rare earth oxide, with or without yttria, must not exceed about 0.093 nm, and the difference in ionic sizes of the constituent oxides should not exceed about O.022nm. The-polycrystalline ceramics are used in high temperature applications and/or in applications requiring light transmission. Exemplary applications include high temperature microscopes, lamp envelopes, laser applications, and furnace windows. The aforedescribed patent teaches that each polycrystalline ceramic body includes between about 2 to 15 mole percent of thoria (ThO2), zirconia (ZrO2), hafnia (HfO2), or some combination thereof to act as a densifying agent during sintering. The inventors herein have found, however, that the inclusion of Tho2, ZrO2, or HfO2 in the scintillator materials of the present invention in the quantities specified in the afore-mentioned patent results in a material having greatly reduced light output when excited by high energy radiation such as x-rays, making such materials unsuitable for CT applications. Fig. 1. illustrates relative light output (vertical axis) of a polycrystalline ceramic composed of about 58.7 mole percent Y2O3r 38 mole percent gadolinia, 3 mole percent Eu203, and 0.3 mole per cent Yb203, with increasing ThO mole percent (shown cent Yb203, 2 on the horizontal axis). As the quantity of Th02 is increased, the quantity of Y 203 is correspondingly decreased. The average ionic radius of the ceramic constituents and the difference between ionic radii are as specified in the patent. It is evident from Fig.l, that the light output for a material containing 2 mole percent ThO2 (the minimum amount specified in U.S.3,640,887) is only 5 percent of the light output for the same mateiral without thoria. In fact, the additionn of as little as 0.5 mole percent ThO2, well below the lower limit specified in the patent, reduces the light output to a value of about 18 percent of that measured for the material without thoria. Ceramic scintillator materials useful in CT should have a light output no lower than about 35 percent of the light output of the material without ThO2. Substantial light output decreases have also been observed for additives such as cerium oxide (CeO2), titanium oxide (Ti02) , zirconium oxide (or02), tantalum oxide (Ta205). For example, the relative light output of a ceramic body containing 55.5 mole percent Yb203, 38 mole percent Gd203, 1 mole percent EU203, 0.5 mole percent Yb203, and 2 mole percent ZrO was found to be 2 4 percent of the light output of the same material but without Zr02. These tetravalent (4 ) and pentavalent (5+) additive species have an inhibiting effect on light output. It is important to note that light output refers to scintillation resulting from x-ray excitation. This is a significant distinction since some ceramic bodies fluoresce under ultraviolet excitation, but do not scintillate upon x-ray excitation, for example. In accordance with the present invention, translucent-to-transparent rare-earth ceramic scintillator bodies are produced without the addition of the aforedescribed scintillation inhibiting densifying additives. The light output of the inventive ceramic scintillators upon x-ray excitation is suffisient to render them useful in CT. The inventive scintillators are made up of rare earth yttria-gadolinia hosts and trivalent rare earth acti vator oxides. The scintillator bodies are fabricated by one of several methods, such as sintering, sintering with gas hot isostatic pressing (GHOP), and hot pressing (all more fully described hereinafter). The finished scintillator bodies having optimum over-all properties are comprised of a cubic solid solution of the chemical constituents as verified by x-ray diffraction techniques. The oxides of trivalent rare earth elements such as europium, neodymium, ytterbium, dysprosium, terbium, and praseodymium (Eu203, Nod203, Yb203, Dry203, Tb203' and Pr203, respectively) are added to the basic yttria-gadolinia system as activators to enhance scintillator efficiency. Yttria-gadolinia scintillators, containing Eu203, exhibit excellent scintillating efficiency. Generally, rare earth activator concentration may range between 0.02 and 12 mole percent. Optimum concentration of Emu203, is between 1 and 6 mole percent. This is illustrated in Fig.2 which shows that the highest relative light output, indicated on the vertical axis, is observed for Emu 203 concentrations of between about 1 and 6 mole percent, as indicated on the horizontal axis. The curve depicted in Fig. 2 was obtained by varying Emu 203 content of a scintillator material containing 25 mole percent Gd203, the remainder being Y203. An exemplary yttria-gadolinia scintilator material using neodymium oxide (Nd203) activator is made up of 30 mole percent Gd203, 0.25 mole percent Nd203, the remainder being Y203. Nd203 is preferably added in quantities of between 0.05 and 1.5 mole percent. Most preferably, however, Nod 203 is added in concentrations of between 0.1 and 0.5 mole percent. Preferred terbium oxide (Tb203) activator concentration is between 0.05 and 3.0 mole percent, while the preferred concentration of dysprosium oxide (Dy203) activator is between 0.03 and 1.0 mole percent. Exemplary compositions of yttria-gadolinia scintillator materials employing Th203 and Dy203 rare earth activators comprise 0.15 mole percent Th203, and 0.2 mole percent Dy203, respectively, each including 40 mole percend God203, the remainder being Y203. The preferred range for Y 203 activator is between about 0.10 and 2.0 mole percent. The preferred mole percentage for the Pr 203 activator is between 0.02 and 0.05. It is to be noted that activator efficacy is independent of the compositional ratios of Y 203 and God203. Eu203 is the preferred activator followed, in order of preference, by Nd203 and Dy203. Fig. 3a illustrated the dependence of scintillator efficiency, as measured by relative light output, on the relative mole percent content of a yttria and gadolinia in a scintillator material containing 3 mole percent Emu2 0 The relative mole percentages of Gd203 and Y203 are shown on the horizontal axis, while the relative light output is shown on the vertical axis. The dashed line at 50 mole percent God 203. Scintillator materials containing between 50 and 65 mole percent Gd203 exhibit modest relative light output, but are increasingly subject to grain boundary cracking and reduced relative light output due to progressive transition from cubic to monoclinic crystalline phase. The cubic crystalline phase is characterized by a high degree of scintillator material structural symmetry. Materials having such structure are particularly desirable for CT applications. Scintillator materials having increasing amounts of monoclinic phase are characterized by lower relative light outputs and poor optical clarity due to grain boundary cracking and nonuniform crystalline structure. Materials having such noncubic structure exhibit appreciable light scattering and reabsorption due to a longer effective relative light path length, thereby decreasing the amount of light available for detection by external photosensors. In considering the usefulness of the scintillator material in CT applications, the x-ray stopping power of the material must also be considered. Fig. 3b illustrates the dependence of 73 keV x-ray stopping length versus yttria-gadolinia compositional ratio for transparent and efficient scintillators. Stopping power is measured in terms of x-ray stopping length, i.e., the distance an x-ray photon penetrates into the scintillator prior to its conversion to optical wavelength photons which are detectable by photosensors. X-ray stopping length is primarily dependent on Gd203 content and, as shown in Fig.3b, increases with increased Gd203 concentration. Generally, it is preferred to use between about 5 mole percent and 50 mole percent Gd 203 Materials containing less than about 5 mole percent God 203 exhibit low x-ray stopping power for most practical detector design, while materials having more than 50 mole percent are increasingly non-cubic and exhibit poor optical clarity. A more preferred range of Gd 203 content is between 20 and 40 mole percent. The most preferred range of Gd203 concentration is between 30 mole percent and 40 mole percent, corresponding to an x-ray stopping length of about 0.45 mm. For a 2 millimeter thick scintillator material having an x-ray stopping length of 0.45 mm, approximately 99 percent of x-ray photons entering the material are converted to ptical wavelength photons. Certain additives are useful in the yttria-gadolinia scintillator system of the present invention to reduce undesirable scintillator material luminescent afterglow, which may lead to undesirable distortion and the presence of artifacts in reconstructed images. The luminescent afterglow phenomenon is classifiable into primary or fundamental afterglow and secondary afterglow. Primary afterglow is of relatively short duration (up to approximately 3 milliseconds), while secondary afterglow may be several times to much more than several times the primary decay time. Funda mental luminescent afterglow of a phosphor is thought to be inextricably associated with the specific activator identity and the activator local environment in the host matrix (in this case yttria-gadolinia). The secondary, and most objectionable type of afterglow, can be associated with more subtle changes in the activator environment or simply with the presence of additional electron-hole "trapping" centers created by native defects and/or low level impurities at other sites in the host crystal. Both types of afterglow may be. reduced by suitable purification or the addition of compensating dopants. The added dopants used to reduce afterglow do so by forming "killer" centers which are believed to compete with the activator centers for electron-hole pairs that otherwise combine radiatively at the activator centers. Luminescent afterglow of rare earth doped yttriagadolinia ceramic scintillators of the present invention can be substantially reduced by several type of additives. The addition of ytterbium oxide (Yb203); itself a luminescent activator in the yttria-gadolinia host if used alone as described heretofore, results in the reduction of undesirable secondary afterglow with only minor sacrifice of luminescent efficiency. If, as depicted in Fig. 4, the mole percentage of Yob 203 is increased from zero to about 2 mole percent, the primary or fundamental afterglow, , of the scintillator material activated with 3 mole percent of Eu,O is reduced from 1.1 to 0.82 milliseconds. An in 23 crease in Yb203 content from 0 to 2 mole percent is accompanied by the loss of nearly 50 percent of scintillator material luminescent efficiency as graphically depicted in Fig. 5 in which relative light output is shown on the vertical axis, while the Yob 203 concentration is shown on the horizontal axis. Curves A, B, C, and D, depicted in Fig.4, illustrate the fraction of secondary luminescent after glow (ver tical axis) remaining at times greater than 10 milliseconds (horizontal axis) following the cessation of x-ray excitation. For a scintillator material having 30 mole percent Gd203' 3 mole percent Eu203, and 67 mole percent Y203, it is evident from Curve A that about three percent of the luminescence present immediately upon x-ray shut-off remains at the end of 10 milliseconds following x-ray shut-off. Curves B, C, and D depict fractional afterglow for similar scintillator materials which additionally contain 0.2, 0.5, and 2 mole percent Yb203 respectively, and correspondingly less Y203. It is apparent that increasing quantities of Yb203 reduce secondary afterglow. For example, at about 10 milliseconds after x-ray turnoff, fractional afterglow for a scintillator material containing 2 mole percent Yb203 (Curve D) is only approximately 0.7 percent (7 x 10 of its value immediately upon termination of x-ray excitation as compared to about 3 percent (3 x 10 2) for a material without Yb203 (Curve A). The addition of 0.3 mole percent Yob 203 to a scintillator composition made up of 66.7 mole percent Y203, 30 mole percent God203, and 3 mole percent Emu 203 results in an extremely useful CT scintillator material having a fast decay time. Preferred concentration of Yob 203 for afterglow reduction is between about 0.15 and 0.7 mole percent. Another additive dopant which is effective in reducing scintillator material luminescent afterglow is strontium oxide (SrO). The addition of SrO results primarily in the reduction of secondary afterglow with relatively little sacrifice of luminescent efficiency. In the yttriagadolinia scintillator system, the quantity of SrO generally found to be useful in reducing afterglow is between 0.1 and 2 mole percent. It is shown in Fig.6 that an increase in the quantity of SrO from 0 to 2 mole percent has 'no appreciable effect on primary afterglow, T , 1.08 milliseconds and 1.10 milliseconds, respectively. However, there is appreciable effect on secondary afterglow as depicted by curves E and F. A scintillator material having 30 mole percent God203 mole 2 percent Eu203, 68 mole percent Y203, but no SrO (curve E) exhibits, at about 150 milliseconds after x-ray turn-off, about 0.8 percent (8 x 10-)3 of the luminescence present immediately after x-ray shut-off. Scintillator materials having the same composition (curve F) but including 2 mole percent SrO (and 2 mole percent less Y 203) exhibit, after the same elapsed time, only about 0.03 percent (3 x 10 4) fractional afterglow as indicated on the vertical axis in Fig.6. The addition of calcium oxide (CaO) to the scintillator material (instead of SrO) has been found to produce an afterglow reducing effect similar to that obtained with SrO. CaO is useful as an afterglow reducer in quantities of between 0.1 and 2 mole percent. The aforedescribed yttria-gadolinia rare-earthdoped ceramic scintillator materials may be prepared by sintering, sintering plus gas hot isostatic pressing, and hot pressing ceramic methods. The ceramic scintillator materials are preferably and most economically fabricated by employing a sintering process. A preliminary step in the fabrication of the ceramic scintillators, by any of the aforementioned methods, requires the preparation of a suitable powder containing the desired scintillator material constituents. In accordance with a first method for preparing such a powder, submicrometer-to-micrometer powders of yttria (Y203), gadolinia (Gd203) having purities of, for example, 99.99 percent to 99.9999 percent are mixed with the desired rare earth activators in the form of oxides, oxalates, carbonates, or nitrates and mixtures thereof. The mixing of the selected constituents may be carried out in an agate mortar and pestle or in a ball mill using water, heptane, or an alcohol (such as ethyl alcohol) as liquid vehicles. Dry milling may also be used for both mixing and breakup of powder aggregates. If dry milling is employed, a grinding aid such as 1 to 5 weight percent of stearic acid or oleic acid should be employed to prevent powder packing or sticking inside the ball mill. A transparency promoter SrO may also be added in the form of an oxide, nitrate, carbonate, or oxalate before ball milling. If the various additives are nitrates, carbonates, or oxalates, a calcining step is required to obtain the corresponding oxides prior to fabrication of the ceramic scintillator by any of the methods described hereinafter. A second approach to obtaining the desired scintillator starting powder employs a wet chemical oxalate method. In this method, the selected molar percentages of the nitrates of predetermined ones of Y, Gd, Eu, Nb, Yb, Dy, Tb, Pr, and Sr are dissolved in water and coprecipitated in oxalic acid to from the respective oxalates. The oxalate precipitation process involves the addition of an aqueous nitrate solution of the desired scintillator material constituents to an oxalic acid solution which is, for example, 80 percent saturated at room temperature. The resulting coprecipitated oxalates are washed, neutralized, filtered, and dried in air at about 1000C for approximately eight hours. The oxalates are then calcined in air (thermally decomposed) at approximately 7000C to about 9000C for a time ranging from one to four hours, to form the corresponding oxides. Typically,heating for one hour at 8000C is sufficient. Preferably, if either the hot pressing or the sintering method is used to prepare the scintillator, the oxalates and/or the resulting oxides are milled by one of several methods such as ball, colloid, or fluid energy milling to enhance the optical clarity. Milling of the powder for between one-half hour and ten hours has been found to be sufficient. It should be noted, however, that typically the optical clarity of the scintillator is improved by milling the oxalates and/or oxides regardless of the preparation method. Following the preparation of the selected powder composition by one of the methods described above, in accord with the preparation of scintillator materials by sintering, selected amounts of the powder composition are formed into powder compacts by either die pressing, or die pressing followed by isostatic pressing to further increase green density. A die material which is inert with respect to the scintillator constituents is preferred to avoid undesired reactions and contaminations. Suitable die materials include alumina, silicon carbide, and metals such. as molybdenum, hardened steel, or nickel-based alloys. The powder compacts are formed by die pressing at pressures of between about 2.068 daN/mm2 (3,000 psi) and 10.34 daN/mm2 (15,000 psi). Alternatively, the die pressed powder compacts may be isostatically pressed at between about 6.89 daN/mm2 2 (10,000) and 41.36 daN/mm (60,000 psi) to further in- crease powder compact green density. If any grindings aids or compaction aids (lubricants, such as waxes) have been used, an oxidation treatment to remove all organic additives can be employes prior to sintering. During the sintering phase, the compacts are heated in a high temperature tungsten furnace, for example, in vacuum or a reducing atmosphere such as a wet hydrogen atmosphere (dew point of about 23"C, for example) at a rate of between approximately 1000C per hour to 7000C per hour to the sintering temperature of between 18000C and 21000C. The sintering temperature is then held from 1 hour to about 30 hours to cause extensive densification and optical clarity development. Upon termination of the sintering step, the compacts are cooled from the sintering temperature to room temperature over a period of time ranging from about 2 to 10 hours. Sintered ceramic scintillators may also be prepa red by a heating sequence which includes a hold at a temperature lower than the final sintering temperature. Typically, the powder compact is heated at a rate of between 300 C/hr and 400 C/hr to a holding temperature of between about 16000C and 17000C. The holding period may range from 1 hour to 20 hours, following which the temperature is raised to between about 18000C and 21000C for final sintering for between 1 hour and 10 hours. The increase from the holding temperature to the final sintering temperature is at a rate of between about 250C/hr and 750C/hre. A preferred heating sequence comprises heating the powder compact to a holding temperature of 16600C in five hours, holding this temperature for 10 hours, followed by heating to 19500C in 6 hours, and then sintering at 19500C for 2 hours. A first ceramic scintillator composed of 59.85 mole percent Y203, 40 mole percent Gd203, and 0.15 mole percent Tb203, and a second scintillator made up of 59.8 mole percent Y203, 40 mole percent Gd203, and 0.2 mole percent Dy203 were prepared using the preferred sintering sequence. In each case, oxalate coprecipitation method and calcined at 8000C for one hour to obtain the corresponding oxides. The oxides were initially cold pressed daN/mm2 into powder compacts at 2.41 daN/mm2 (3,500 psi) and then 2 isostatically pressed at 19.99 daN/mm2 (29,000 psi) to further increase green density. This was followed by heating the powder compacts in a wet H2 atmosphere in five hours to 16600C. Following a 10 hour holding period at 16600C the temperature was raised to 19500C and held for two hours. The resulting ceramic scintillators were then furnace-cooled to room temperature. Yttria/gadolinia ceramic scintillators for luminescent applications may also be prepared by a combination of processes involving sintering and gas hot isostatic pressing (GHIP). The starting oxide powder compositions are prepared in accordance with one of the aforedescribed methods. Preferably, the oxalate coprecipitation method is used. By way of example and not limitation, one useful yttria-gadolinia scintillator composition comprised 66.8 mole percent Y203, 30 mole percent God23, 3 mole percent Eu203, and 0,3 mole percent Yob2 0 In 3. contrast to the previously described sintering process, which preferably requires milling of the oxalate and/or oxide powders to produce transparent ceramics, the process of sintering combined with GHIP permits the fabrication of transparent ceramics from unmilled powders. In the fabrication of yttria-gadolinia ceramic scintillators by the combined processes of sintering and gas hot isostatic pressing, following the preparation of a powder having the desired composition, powder compacts are formed by cold pressing at pressures of between 2.068 daN/mm2 (3,000 psi) and 6.89 daN/mm (10.000 psi), followed by isostatic pressing at pressures of between 10.34 2 daN/mm2 (15,000 psi) and 41.36 (60,000 psi). The pressed compacts are then presintered to 93 to 98 percent of their theoretical density at temperatures of about 15000C to 17000C for between 1 and 10 hours. The presintered compacts are then gas hot isostatically pressed with argon gas at pressures of 0.689 daN/mm (1,000 psi) to 20.68 daN/mm2 (30.000 psi) at temperatures between 15000C and 18000C for 1 to 2 hours. In accordance with an example of the preparation of a ceramic scintillator employing the sintering and GHIP technique, a powder compact was formed by cold pressing approximately 20 grams of powder in a rectangular die at a pressure of approximately 2.75 daN/mm2 (4,000 psi) . The sample was then isostacally pressed at 20.68 daN/mm2 (30,000 psi) to increase green density to 49 percent of its theoretical value. The cold pressing of the sample was followed by sintering in a wet hydrogen atmosphere (dew point 230C) for two hours at 16600C so that closed porosity is developed. The density of the sintered sample, as measured by the water immersion method, at this stage in the fabrication process was determined to be between 93 and 98 percent of its theoretical value. in order to obtain additional densification and optical transparency, the sample was gas hot isostatically pressed in a carbon resistance furnace at 17500C for one hour at an argon pressure of 17.23 2 daN/mm (25.000 psi). During gas hot isostatic pressing, the temperature was increased to the final value of 17500C in a step-wise manner. The ample was initially heated in one hour to 14000C and the temperature raised thence to 17500C, the resulting ceramic scintillator had a black appearence due to reduction in the reducing furnace atmosphere. The sample was rendered transparent to visible light by suitable oxidation treatment such as heating in air at a temperature of 12000C for thirty-two hours. Comparison of the physical dimensions of the sample before and after the GHIP treatment indicates that the sample shrunk during the GHIP step, indicating further densification. The finished ceramic exhibited a density of greater than 99.9 percent of theoretical value. Transparent yttria-gadolinia ceramic scintillators may also be prepared by vacuum hot pressing a scintillatorl. material powder prepared, preferably, by the afore described wet oxalate coprecipitation process. In accordance with this method, a selected quantity of the calcined oxalate powder (preferably milled) is pressed in a graphite die with molybdenum foil used as spacers between the upper and lower graphite plungers. Alternatively-, a boron nitride coated graphite die may be used. A pressure of 0.689 daN/mm2 2 (1000 psi) to 0.827 daN/mm2 (1200 psi) is applied at a temperature of between about 6000C and 7000C under a vacuum of less than 200 micrometers and maintained for about one hour. Thereafter, the pressure is increased to approximately between 2.76 daN/mm2 (4000 psi) and 6.89 dÅaN/mm2 (10,000 psi). The pressure is released after a hold at the elevated temperature of between one-half to four hours and the sample furnace cooled to room temperature. Ceramic scintillator samples prepared in accordance with the hot-pressing method may be discolored due to surface reaction with the molybdenum spacer. Additional discoloration may be due to oxygen deficiency in the furnace atmosphere during hot pressing. The ceramics, however, can be made optically clear by oxidation in air or an oxygencontaining atmosphere at a temperature of about 8000C to 12000C for between one and twenty hours. Any residual discoloration may be removed by conventional grinding and polishing techniques. In a specific example of the preparation of a scintillator material by the vaccum hot-pressing method, 10 grams of a scintillator oxide material were obtained from the aforedescribed oxalate coprecipitation process by calcination of the oxalates at 8000C for one hour in air. The oxides were initially hot pressed in a boron nitride coated graphite die at 7000C for one hour under a vacuum of about 20 micrometers and at a pressure of 0.827 daN/mm2 (1200 psi). The temperature and pressure were then increased to 14000C and 4.13 daN/mm2 (6,000 psi), respectively, under a vacuum of approximately 100 micrometers. These conditions were maintained for two hours, following which the pressure was released and the resulting scintillator material furnace cooled. The scintillator material was gray to gray-black in color due to the reducing atmosphere created in the hot press. Light grinding of the scintillator surface and heating at 9500C for four hours removed carbon sticking to the scintillator material. The remainder of the dark coloration was removed by additional oxidation at 11500C for two hours in air. The resulting scintillator material was "light tan" in color, translucent to transparent in optical quality, and exhibited good relative light output upon excitation by x-rays. From the foregoing, it will be appreciated that rare earth-doped, polycrystalline yttria-gadolinia scintillators having high density, optical clarity, uniformuity, cubic structure and which are useful in computerized tomography and other x-ray detecting applications have been disclosed. The scintillators also exhibit high x-ray stopping power and high radiant efficiency. Due to inclusion of specific additives, scintillator luminescent afterglow and hysteresis are minimized. From the foregoing, it will also be appreciated that the invention provides methods for sintering, for sintering and gas hot isostatic pressing and for vacuum hot pressing, transparent-to-translucent, rare-earth-doped polycrystalline yttria-gadolinia ceramic scintillators having cubic crystalline structure, high x-ray stopping power, high radiant efficiency, high density, high uniformity, as well as low luminescence afterglow and which are useful radiation detectors such as those used in CT and digital radiography.

Claims: CLAIMS 1. A polycristalline ceramic scintillator consisting essentially of between 5 mole percent and 50 mole percent Gd203, and between 0.02 and 12 mole percent of at least one rare-earth activator oxide selected from the group consisting of Eu203, Nd203, Yb203, Dy203, Tub203, and Pr203, the remainder being Y203. 2. A polycristalline ceramic scintillator comprising between 5 and 50 mole percent of Gd203, between 0.02 and 12 mole percent of at least one rare-earth activator selected from the group consistingt of Eu203, Nd203, Yb2 0 Dy203, Tb203, and Pr203, and between 0.1 à 2 mole percent each of at least one afterglow reducer selected from the group consisting of CaO and SrO, the remainder being Y203. 3. A polycristalline ceramic scintillator consisting essentially of between 5 and 50 mole percent Gd203, 0,5 to 12 mole percent Eu203, and 0.1 and 2 mole percent Yb203, the remainder being Y203. 4. The polycristalline ceramic scintillator of any of claims 1-3 wherein said rare-earth activator oxide consists essentially of between 1 and 6 mole percent of Emu203. s * 5. The polycristalline ceramic scintillator of any of claims 1-3 wherein said rare-earth activator oxide consists essentially of between 20 and 40 mole percent of God2 03. 6.The polycristalline ceramic scintillator of claims 1 or 2 wherein said rare-earth activator oxide consists essentially of between 0.05 and 1.5 mole percent of Nod2 0 7.The polycristalline ceramic scintillator of claim 6 wherein said rare-earth activator oxide consists essentially of between 0.1 and 0.5 mole percent of Nd203. 8.The polycristalline ceramic scintillator of claim 1 or 2 wherein said rare-earth activator oxide consists essentially of between 0.5 and 3 mole percent of Tub2 0 9.The polycristalline ceramic scintillator of claim 1 or 2 wherein said rare-earth activator oxide consists essentially of between 0.1 and 2 mole percent of Yb203. 1O.The polycristalline ceramic scintillator of claim 9 wherein said rare-earth activator oxide consists essentially of between 0.15 and 0.7 mole percent of Yob2 0 11.The polycristalline ceramic scintillator of claim 1 or 2 wherein said rare-earth activator oxide consists essentially of between 0.03 and 1 mole percent of Do203. 12.The polycristalline ceramic scintillator of claim 1 or 2 wherein said rare-earth activator oxide consists essentially of between 0.02 and 0.05 mole percent of Pr203' 13. A method for preparing a polycrystalline ceramic scintillator body comprising the steps of: preparing a multicomponent powder including between 5 and 50 mole percent Gd203, and between 0.02 and 12 mole percent of at least one rare earth activator oxide selected from the group consisting of Eu203, Nd203, Yb203, Dy203, Tb203, and Pr203, the remainder of said multicomponent powder being Y203 cold pressing said multicomponent powder to form a powder compact; and sintering said powder compact to form said polycrystalline ceramic scintillator body. 14. A method for preparing a polycrystalline ceramic scintillator body comprising the steps of: preparing a multicomponent powder including between 5 and 50 mole percent Gd203, and between 0.02 and 12 mole percent of at least one rare earth activator oxide selected from the group consisting of Eu2 0 3' Nd203, Yb203, Dy203, Tb203, and per203, the remainder of said multicomponent powder being Y203 pressing said multicomponent powder to form a powder compact; sintering said powder compact to closed porosity stage ; and pressing the sintered powder compact by the gas hot isostatic process to form said polycrystalline ceramic scintillator body. 15. A method for preparing a polycrystalline ceramic scintillator body comprising the steps of: preparing a multicomponent powder including between 5 and 50 mole percent Gd203, and between 0.02 and 12 mole percent of at least one rare earth activator oxide selected from the group consisting of Eu203, Nod203, Yob203, Dy203, Tb2 3' and Per2 0 3' the remainder of said multicomponent powder being Y203 pressing said multicomponent powder under vacuum at a first temperature and pressure for a first peredetermined period of time; and increasing said first temperature and pressure to a second temperature and pressure and maintaining said second temperature and pressue for a second period of time to form said polycrystalline ceramic scintillator body. 16. The method of any of claims 13-15 wherein said multicomponent powder comprises between 20 and 40 mole percent God203 17. The method of any of claims 13-15 wherein said multi component powder comprises between 1 and 6 mole percent Eu203. 18. The method of any of claims 13-15 wherein said multicomponent powder comprises between 0.1 and 2 mole percent Yb203. 19. The method of any of claims 13-15 wherein said multicomponent powder comprises between 20 and 40 mole percent Gd203, between 1 and 6 mole percent Eu203, between 0.1 and 2 mole percent Yb203, the remainder being Y203. 20. The method of any of claims 13-15 wherein said multicomponent powder comprises between 0.05 and 1.5 mole percent Nd203 21. The method of any of claims 13-15 wherein said multicomponent powder comprises between 0.05 and 3 mole percent Tub 0 23 22. The method of any of claims 13-15 wherein said multicomponent powder comprises between 0.03 and 1 mole percent Dry203 23. The method of any of claims 13-15 wherein said multicomponent powder comprises between 0.02 and 0.05 mole percent Pr 203 24 The method of any of claims 13-15 wherein said multicomponent powder comprises between 0.1 and 2 mole percent SrO or CaO 25. The method of any of claims 13-15 wherein said step of preparing said multicomponent powder comprises mixing high purity, micrometer-to-submicrometer powders of Gd203, Y203, and at least one of said rare earth activator oxides. 26. The method of any of claims 13-15 wherein said step of preparing said multicomponent powder comprises the steps of: coprecipitating by the wet chemical oxalate process the oxalates of Y, Gd, and at least one of said rare earth activator oxides; and calcining said oxalates so as to obtain the corresponding oxides. 27. The method of any of claims 13-15 wherein said step of calcining comprises the step of heating said oxalates in air at a temperature of between 7000C and 9000C for between 1 hour and 4 hours. 28. The method of claim 26 wherein said step of calcining is preceded by the step of milling said oxalates. 29. The method of any of claims 26 or 28 further comprising the step of milling said oxides obtained in said calcining step. 30. The method of any of claims 13, 25 or 26 wherein said step of cold pressing comprises the step of die pressing said multicomponent powder at a pressure of between 2.068 daN/mm2 (3.000 psi) and 10.34 daN/mm2 (15,000 psi). 31.The method of claim 30 wherein said step of cold pressing further comprises the step of isostatically pressing the die pressed multicomponent powder at a pressure of between 6.89 daN/mm2 (10,000 psi) and 41.36 daN/mm2 (60,000 psi) to further increase the green density and uniformity of said powder compact. 32. The method of claim 31 wherein said step of sintering comprises the steps of: heating said powder compact at a rate of between 1000C per hour and 7000C per hour to a sintering temperature of between 18000C and 21000C; and holding said sintering temperature for between 1 and 30 hours. 33. The method of claim 31 wherein said step of sintering comprises the steps of: heating said powder compact at a rate of between 300 C/hr and 400 C/hr to a holding temperature of between 16000C and 17000C; maintaining said holding temperature for between 1 and 20 hours and then increasing the temperature at a rate of between 250C/hr and 750C/hr to a final sintering temperature of between 18000C and 21000C; and maintaining the final sintering temperature for between 1 and 10 hours. 34. The method of claim 31 wherein said step of heating comprises heating said powder compact in vacuum or in a reducing atmosphere. 35. The method of claim 31 further comprising the step of cooling the resulting polycrystalline ceramic scintillator body to room temperature over a period of between 2 and 10 hours. 36. The method of any of claims 14, 25 or 26 wherein said step of pressing to form said powder compact comprises the steps of: cold pressing said multi-component powder at a pressure of between 2.068 daN/mm2 (3,000 psi) and 6.89 daN/mm2 (10,000 psi) to form a preliminary powder compact; and then isostatically pressing said preliminary powder 2 compact at a pressure of between 10.34 daN/mm2 (15,000 2 psi) and 41.36 daN/mm (60,000 psi) to increase the green density thereof. 37. The method of claim 36 wherein said step of sintering comprises heating said powder compact at a temperature of between 15000C and 17000C for between 1 and 10 hours. 38. The method of claim 37 wherein said step of pressing the sintered powder compact by the gas hot isostatic process comprises the step of heating at a temperature of between 15000C and 18000C for between 1 and 2 hours at an argon gas pressure of between 0.689 daN/mm2 (1,000 psi) and 20.68 daN/mm2 (30,000 psi). 39. The method of claim 38 wherein said step of pressing the sintered powder compact by the gas hot isostatic process more specifically comprises the steps of: heating said powder compact for one hour to raise the temperature thereof to 14000C, continue heating said powder compact for an additional one jour to raise the tem perature thereof to 17500C; and then maintaining the temperature of said powder compact to room temperature, sais steps of heating and maintaining the temperature being performed at an argon gas pressure of 17.23 daN/mm2 (25,000 psi) 40. The method of any of claims 15, 25 or 26 wherein said step of pressing comprises the step of pressing said multicomponent powder at a pressure of between 0.689 daN/mm2 (1,000 psi) and 0.827daNmm2 (1,200 psi) at a temperature of between 6000C and 7000C under a vacuum of up to 200 micrometers for 1 hours. 41. The method of claim 40 wherein said step of increasing said first temperature and pressure comprises increasing the temperature to between 13000C and 1600"C, 2 increasing the pressure to between 2.75 daN/mm2 (4,000 psi) and 6.89 daN/mm2 (10,000 psi), and maintaining said increased temperature and pressure for between one-half hour to 4 hours. 42. The method of claim 41 further comprising the step of o idizing the resulting hot pressed ceramic, said step of oxidizing including heating said ceramic in an oxygen-containing atmosphere for between 1 and 20 hours at a temperature of between 8000C and 1200"C so as to remove any discoloration.

Inventors: CUSANO, DOMINIC ANTHONY, DIBIANCA, FRANK ANTHONY, GRESKOVICH, CHARLES DAVID
Applicants: GENERAL ELECTRIC COMPANY
Application year: 1983
Main classification: G01T1
IPC codes: G01T1, A61B6, C04B35, C09K11