CHLOROTRIFLUOROETHYLENE TELOMERIZATION PROCESS

Abstract: An improved process for preparing telomers of chloro­ trifluoroethylene comprises the solution telomerization reac­ tion of chlorotrifluoroethylene with carbon tetrachloride in the presence of a catalytic amount of ferric chloride (FeCl₃) and a reductant selected from the group consisting of iron, nickel, cobalt, vanadium, molybdenum, chromium, their alloys and mixtures thereof. Preferably, the solvent for the system comprises acetonitrile, and the telomerization is carried out under elevated pressure conditions and at a temperature in the range of from about 90°C to about 150°C. The crude telomer prepared by this process can be fluorin­ ated to produce a stabilized oil or grease.

Description: CHLOROTRI FLUOROETHYLENE TELOMERIZATION PROCESS BACKGROUND OF THE INVENTION The present invention relates to an improved process for preparing telomers of chlorotrifluoroethylene, hereinafter designated as "CTFE". CTFE telomers are saturated low molecular weight polymers, typically of general formula CC13(CF2CC1F)nCl, where n, the molecular number (the number of repeating units in the telomer chain) is in the range of 1 to 20. Fluorination of the telomer results in replacement of one or more chlorine atoms in the terminal group(s) with fluorine and gives products which are inherently non-flammable, thermally stable, and are particularly suitable for use as hydraulic fluids and high temperature lubricants. Such fluorination can be achieved using a variety of fluorinating agents. For example, British Patents 712,184 and 761,053 disclose the fluorination of CTFE oils using both chlorine trifluoride and cobalt trifluoride. The use of hydrofluoric acid as a fluorinating agent for CTFE oils is also disclosed in U. S. Patent 2,636,908, while U. S. Patent 2,886,607 illustrates the use of antimony trifluoride and antimony pentachloride as fluorinating agents. Various methods of preparing CTFE telomers are known in the prior art and have been practiced commercially for many years. An article by William T. Miller. Jr. et al in industrial and Enaineerina Chemistry3 pages 333-337 (1947), entitled "Low Polymers of Chlorotrlfluoroethylene", describes a process for producing low molecular weight polymers of CTFE by carrying out the polymer ing tn a solution of chloroform using benzoyl peroxide as a poly merization promoter. Other solvents disclosed in the reference as being useful for this purpose include carbon tetrachloride and tetrachloroethylene. The solution is heated in a pressure vessel for 1 3/4 hours at 100 C, and the unreacted CTFE monomer and chloroform are removed by distillation, leaving a "crude telomer of general formula CHC12(CF2CClF)nCl, which can be further heated and distilled to yield products ranging from a light oll to a semisolid wax or grease. U. S. Patent 2,793,201, issued May 21, 1957, discloses improved promoters for polymerizing CTFE monomers to produce low molecular weight polymers. Specific promoters disclosed in the reference include various peroxides such as bls-(trichleroacetyl) peroxide and bis-(perchloroacrylyl) peroxide. The use of such promoters produces a more stable polymer by eliminating the amount of reactive hydrogen present in the polymer. Another process which has been developed for producing low molecular weight CTFE polymers is described in U. S. Patent 2,788,375, issued April 9, 1957. This process comprises reacting CTFE with a saturated organic bromo compound, such as bromotrichloromethane, in the presence of actinic light in a de-oxygenated system to obtain saturated bromopolychlorofluoro compounds containing one or more CTFE units per molecule. These saturated bromopolychlorofluoro compounds can then be converted to corresponding polychlorofluoro compounds by treatment with chlorine, and subsequently fluorinated using, for example, cobalt trifluoride or chlorine trifluoride, in combination with antimony catalysts, to yield more highly fluorinated products. A more recent development in this field is described in a series of articles by Y. Pietrasanta et al entitled "Telomerization by Redox Catalysis" appearing in the European Polymer Journal, Vol. 12 (1976). This technology involves the reaction of a chlorinated telogen, -such as carbon tetrachloride, with CTFE in the presence of benzoin and a suitable redox catalyst, such as ferric chloride hexahydrate (FeC13.6H20). The telomerization reaction is suitably carried out in acetonitrile which is a common solvent for the reactants and catalysts. The telomerization reaction can be illustrated as follows: EMI3.1 <tb> <SEP> FeCl3 <tb> <SEP> 3 <SEP> , <SEP> CC1 <SEP> ,(CF3CFC1 <SEP> (1) <tb> CC14 <SEP> + <SEP> nCF2=CFCl <SEP> Benzoin <tb> <SEP> Benzoin <tb> The redox method has the advantage of directly preparing a high yield of low molecular weight product without the necessity of cracking or fractionating a higher molecular weight polymer. It is known that benzoin acts as a reducing agent for Fe+3 ions in solution and that, in the absence of benzoin, product yield falls to less than 5%. See European Polymer Journal, supra. However, there are certain disadvantages associated with the use of benzoin in the redox telomerization process which could effectively render uneconomical any commercial scale process based on this technology. For example, benzoin must be removed from the crude telomer prior to fluorination or the fluorinated product will contain unsaturation as determined by the KMnO4 test and, as a result, will not meet product specifications. Removal of the benzoin from the crude telomer requires the use of an absorption column, such as a column of activated alumina, which not only removes benzoin but retains a significant amount of telomer which must be reclaimed using, for example, solvent extraction. Thus, use of an activated alumina column is a costly and time-consuming procedure It is thus a principal object of the present invention to provide an effective process for preparing CTFE telomers on a commercial scale without the inherent inefficiencies of prior art processes. It is a further object of this invention to provide a process for preparing CTFE telomers which can be directly fluorinated after removal of solvent and unreacted materials to yield a variety of stabilized products. SUMMARY OF THE INVENTION In accordance with the present invention, there is provided an improved process for preparing telomers of chloro trifluoroethylene comprising reacting chlorotrifluoroethylene with carbon tetrachloride in the presence of a catalystic amount of Fecal3 and a reductant selected from the group con sitting of iron, nickel, cobalt, vanadium, molybdenum, chromium, their alloys and mixtures thereof. The reaction is conducted in a common solvent for the reactants and catalysts and preferably comprises acetonitrile. The telomerization reaction is preferably conducted at a pressure in the range of from about 150 p.s.i. to about 300 p.s.i. and a temperature in the range of from about 900C. to about 1500C. The crude telomer prepared by this process can be fluorinated directly after removal of solvent and unreacted materials using conventional fluorination techniques. The product is a stabilized telomer which has fluorine-substituted end groups and acceptable levels of product unsaturation. DESCRIPTION OF THE PREFERRED EMBODIMENTS The telomerization process of the present invention provides for the reaction of chlorotrifluoroethylene with carbon tetrachloride in a common solvent, such as acetonitrile, in the presence of a catalytic amount of FeC13 and a reductant, and can be illustrated as follows: EMI5.1 wherein M is a metal or alloy selected from the group consisting of iron, nickel, cobalt, vanadium, molybdenum, chromium, their alloys and mixtures thereof. The molecular weight distribution of the telomer is dependent on several factors, including the relative concentration of the Foe 3 ions in the solution, the rate of reduction of Fe+3 ions to Fe+2 ions, and the relative concentration of the reactants in the solution. By carefully controlling these conditions during the telomerization reaction, it is possible to produce a telomer having a relatively precise molecular weight distribution in the desired range, i.e. corresponding to a molecular number of from about 1 to about 20. Although the concentration of reactants in accordance with the present invention can vary depending on the reaction conditions and degree of telomerization desired, it has been found that particularly useful products can be obtained by maintaining a ratio of CTFE/CC14 in the range of from about 1.5 to about 0.5 during the telomerization reaction. Similarly, it is also desirable, although not essential, to maintain the concentration of Fecal3, in the range of from about 0.05% to about 5% by weight of CTFE. During the telomerization reaction, an inordinant amount of Foe 2 ions to the Fe+3 form occurs as a result of side reactions other than (2). Accordingly, it has been found necessary to introduce a reductant into the reaction mixture to reduce the Fe+3 ions at a moderate rate. The use of benzoin as a reducing agent, although effective, has the disadvantage of requiring an additional unit operation, i. e. adsorption using, for instance, a column of activated alumina, for removal of the benzoin prior to fluorination. The present invention obviates the us of benzoin by utilizing, as a reductant, a metal selected from the group consisting of iron, nickel, cobalt, vanadium, molybdenum and chromium. Physical admixtures and alloys of these metals, such as Hastelloy C (Hastelloy is a registered trademark of the Union Carbide Corporation), are also within the scope of this invention. The metal reductant may be physically present in the reaction mixture in a variety of forms, such as a powder, particles of various sizes, wires, plates, or as a cladding material on the internal surface of the reactor vessel. The preferred form is a finely divided powder which is uniformly dispersed in the reaction vessel by means of a mechanical agitation, such as in a stirred reactor. The reductant is preferably present in the reaction mixture in the range of from about 0.05% to about 5% by weight of CTFE. The telomerization reaction is preferably conducted in a stirred reactor under elevated temperature and pressure conditions, with temperatures generally ranging from about 900C to about 1500C, and pressures generally in the range of from about 50 p.s.i. to about 400 p.s.i. The crude CTFE telomer which is prepared according to the procedure described above, can then be stripped of solvent and unreacted monomer and fluorinated directly with a suitable fluorinating agent to produce stabilized telomers. Fluorinating agents which can be employed for this purpose include cobalt trifluoride and chlorine trifluoride, among others. The following examples are intended to further illustrate the various embodiments and advantages of the present invention without limiting it thereby. These examples illustrate the preparation of crude CTFE telomers using various metal reductants according to the present invention. EXAMPLE 1 A one-liter glass-lined stainless steel autoclave was dried, purged with N2 and charged with 166 ml. of Cm14, 88 ml. of CH3CN, 193 grams of CTFE, and 1.1 grams of Fecal3. Nickel wire (36 inches long, 0.0628 inches in diameter, and 7.1 square inches surface area) was wound around the stirring shaft of the autoclave dipping in the reaction mixture. The 0 autoclave was heated to a reaction temperature of 115 C and a pressure of 198 p.s.i. After about 1 hour, the pressure of the reaction mixture dropped to 180 p.s.i. 70 grams of CTFE was added to increase the pressure to about 200 p.s.i. After 1 3/4 hours an additional 64 grams of CTFE was added to increase the pressure to about 210 p.s.i. The reaction was stopped after 4 hours, the temperature was allowed to fall to ambient and unreacted CTFE was removed. The contents of the autoclave were emptied and stripped to yield 249 grams of product. The crude reaction product was fluorinated to stabilize the end groups. After filtration, the product was colorless and showed no unsaturation when tested using the KMnD4 oxidation test. The Kin04 test is a standardized technique for determining unsaturation of telomers of this type, and generally comprises adding 0.06 ml. of 1% aqueous KMnO4 to a solution of 1 gram of telomer dissolved in 10 ml. of acetone. If the solution remains pink in color for at least 15 minutes, the telomer contains satisfactory limits of unsaturation. EXAMPLE 2 Following the procedure of Example 1, an autoclave lined with Hastelloy C was dried, purged with N2, and charged with 48 ml. of CC14, 26 ml. of CH3CN, 64.8 grams of CTFE and 0.99 grams of FeCI3. The reaction mixture was heated to a temperature of about 110C and stirred for about 2 hours. During this procedure, the pressure varied from about 60 p.s.i. to about 115 p.s.i. The temperature was then allowed to fall to ambient and unreacted CTFE was removed. The contents of the reactor were emptied and stripped to yield a product weighing 28.5 grams. EXAMPLE 3 Following the procedure of Example 1, an autoclave lined with Teflon was dried, purged with N2, and charged with 247.3 grams of CC14, 65.2 grams of CH3CN, 169.5 grams of CTFE, 2.0 grams of Fell3 and 0.7 grams of iron filings. The reaction mixture was heated to a temperature of about 1100C and stirred for about 2 hours. During this procedure, the pressure varied from about 172 p.s.i. to about 199 p.s.i. The temperature was then allowed to fall to ambient and unreacted CTFE was removed. The contents of the reactor were emptied and stripped to yield 148.0 grams of product. EXAMPLE 4 Following the procedure of Example 1, an autoclave lined with Teflon was dried, purged with N2, and charged with 245 grams of Cm14, 65 grams CH3CN, 189 grams of CTFE, 2.0 grams of FeC13, and 0.65 grams of chromium powder. The reaction mixture was heated to a temperature of about 1100C and stirred for about 2 hours. During this procedure, the pressure varied from about 177 p.s.i. to about 199 p.s.i. The temperature was then allowed to fall to ambient and unreacted CTFE was removed. The contents of the reactor were emptied and stripped to yield 173 grams of product. While various embodiments and exemplifications of this invention have been shown and described in the specification, modifications and variations thereof will be readily appreciated by those skilled in the art. It is to be understood, therefore, that the appended claims are intended to cover all such modifications and variations which are considered to be within the scope and spirit of the present invention.

Claims: CLAIMS 1. A process for preparing telomers of chlorotrifluoroethylene comprising reacting chlorotrifluoroethylene with carbon tetrachloride in the presence of a catalytic amount of FeC1 and at least one 3 reductant selected from iron, cobalt, vanadium, nickel, molybdenum, chromium and their alloys, said reaction being conducted in a common solvent for the reactants and catalysts. 2. A process according to claim 1 wherein the common solvent is acetonitrile. 3. A process according to claim 2 wherein the FeC13 is present in the reaction mixture in an amount of from 0.1* to 10% by weight of chlorotrifluoroethylene. 4. A process according to claim 3 wherein the reductant is present in the reaction mixture in an amount of from 0.1% to 10% by weight of chlorotrifluoroethylene. 5. A process according to any one of the preceding claims wherein the telomerization reaction is conducted at a Dressure of from 150 p.s.i. to 300 p.s.i. (1.03 to 2.07 MPa). 6. A process according to any one of the preceding claims wherein the telomerization reaction is conducted at a temperature of from 900C to 150 0C. 7. A process for preparing a stabilized telomer of chlorotrifluoroethylene, which comDrises the steps of: a) reactinq chlorotrifluoroethylene with carbon tetrachioride in accordance with a process as claimed in any one of claims 1 to 6, b) removing solvent anS unreacted materials from the telomer produced in step a), and c) directly fluorinating the telomer from step b) to stabilize the telomer. 8. A process according to claim 7 wherein the solvent and unreacted materials are removed from the telomer by evaporation. 9. A process according to claim 7 or 8 wherein the telomer is fluorinated with chlorine trifluoride. 10. A process according to claim 7, 8 or 9 wherein the fluorination reaction in step (c) is conducted at a temperature of from 1200C to 2000C.

Inventors: SARAN, MOHAN S.
Applicants: OCCIDENTAL CHEMICAL CORPORATION
Application year: 1983
Main classification: C08F14
IPC codes: C07C67, C07C17, C08F14, C08F4, B01J27, C08F2, C07C19, C08F114, C08F8