PRODUCTION OF MACRO BALLOON STRUCTURES

Abstract: A method of making light weight flame resistant struc­ tures from bonded polyimide macroballoons. An aromatic tetracarboxylic acid dianhydride is reacted with a lactam to produce an N-substituted imide, which is then esterfied with a reactive solvent. At least one diamine is added. The resulting liquid is dried and the dry residue is reduced to an uniform powder having particles with diameters generally in the 0.5 to 10mm. range. The powder expands when heated to a temperature in the range of about 90 to 150°C for a suitable period. Closed cell "macroballoons" having average dia­ meters between about 0.4 and 15mm. result. The macrobal­ loons are bonded together with a very small amount of a suitable resin.

Description: Production of macro balloon structures BACKGROUND OF THE INVENTION This invention relates in general to polyimide foams and, more specifically, to closed cell polyimide foams having improved flame resistance. A number of polyimide compositions having excellent flame resistance and utility as coatings and adhesives are described and claimed in United States Patents 4,161,477, 4,183,138 and 4,183,139, granted to John Gagliani, one of the inventors of the invention claimed in this application. The coating and adhesive compositions described in the above-mentioned prior patents are made by first preparing a suitable bisimide by reacting an aromatic tetracarboxylic acid dianhydride with a cyclic amide or oxime. The ratio of oxime to dianhydride is preferably in the 2.3:1 to 2.7:1 range and the imidization reaction is preferably conducted at a temperature of 170-2000C for 20-60 minutes. The polyimide forming material is then prepared by dissolving the bisimide in an inert solvent; then adding thereto a suitable diamine, producing a viscous fluid containing an intimate, unpolymerized mixture of Nsubstituted cyclic bisimide dicarboxylic acid and diamine which is capable of being converted to a high molecular weight polymer by the application of heat. The solution is coated onto a surface and polymerized by heating to a temperature in the 177-3160C. range for 30 minutes to 5 hours. The following is exemplary of the exchange reaction which occurs: EMI2.1 where n is a positive integer. The resulting coating is tough, highly adherent to various surfaces, with very few pinholes or bubbles. It has excellent peel strength and is resistant to high temperatures, peeling and abrasion. The prior coating material, however, was not suitable for use in applications requiring a cellular or foam material, since conventional agitation foaming and addition of known blowing agents add to process costs and complexity and are not entirely effective at the relatively high polymerization temperature required. Our co-pending European Pat-ent Ap?lication Serial No 8o 9 8 discloses and claims methods of making modified polyimide/polyimide-amide open cell foams and the product thereof. In that method, the reaction of an oxime with an aromatic dianhydride in a mole ratio of from about 0.05:1 to 1.5:1 produces an N-substituted aliphatic mdnoimide which is then esterified with a suitable reactive solvent. A suitable diamine is added and the liquid is dried to a film or powder. The dry material spontaneously expands into a consolidated open cell foam when heated to a temperature in the range of about 230 to 3200C. At the lower end of this temperature range, a primarily polyimideamide foam results, while toward the high end of the range the foam is primarily a polyimide. Flexibility, flame resistance and other physical characteristics vary with the proportions of the two polymers in the final product. While this open cell foam is excellent for many applications, and can have physical properties tailored for specific purposes, it is not optimum for certain uses. The open cell foam tends to shrink when exposed to flame or high heat. It may absorb water or other liquids and is permeable to liquids and gases. Also, the relatively high foaming temperatures require more complex and expensive heating equipment and the process is wasteful of energy. Thus, there is a continuing need for a closed cell foam having a combination of flame and heat resistance, resistance to flame-induced shrinking, flexibility and resistance to penetration by liquids and gases. Also, there is a need for reductions in process complexity and energy consumption. SUMMARY OF THE INVENTION The above problems, and others, are overcome by a process having some similarities to those of the abovementioned patents and application, which, however, produces a flexible, high temperature and flame shrinkage resistant structure of bonded polyimide macroballoons. While the reactions which occur are complex and not. fully understood, it appears that under the polymerization reaction conditions described below, the polymer produced is primarily a polyimide with a portion of polyimide-amide. For the purposes of this application the resin, for simplicity, will be identified as a polyimide. The basic steps in producing our polyimide macroballoons are reacting an oxime with an aromatic tetracarboxylic acid dianhydride in a mole ratio of about 0.05:1 to 1.5:1 to produce an N-substituted imide; esterifying the imide with a reactive solvent; adding thereto a suitable diamine; drying the liquid to a nontacky, handleable material; reducing the dry material to a powder having average particle diameters of from about 0.5 to 10 mm.; and heating the unrestrained powder to a temperature of about 90 to 1500C. for a suitable period to produce a plurality of discrete macroballoons by spontaneous foaming and polymerization. Preferably, a step of further drying the material at a moderate temperature and a partial vacuum is performed just before or after the powder size reduction step to remove any remaining excess solvent. DETAILED DESCRIPTION OF TBE INVENTION Either a consolidated, uniform closed cell shaped foam product or a number of macroballoons or beads may be produced, depending on whether full foaming is restrained or unrestrained. Macroballoons can be produced in diameters ranging from about 0.4 to 15 mm. by unrestrained foaming, e.g., on a flat open surface or through feeding the powder into a flowing hot air stream or centered heated metal tube. For best natroballoons, the powder size should be toward the smaller end of the preferred 0.5 to 10 mm. general size range. Tie macroballoons have utility per se, such as for packing material or fillers in other casting resins. As detailed below, a novel foam-like structure may be prepared by wetting the macroballoons with a small quantity, generally less than 10 wt.% based on macroballoon weight, of a suitable liquid bonding agent, shaping the mass as desired, and curing the bonding agent at any suitable temperature, preferably up to about 1500C. The foam-like structures may be formed by any suitable method, such as by filling a mold and curing the bonding agent, by continuously curing a layer of the wetted macroballoons to form panels or sheets, etc. Since very little of the bonding agent is used, amounting to less than about 10 wt. % of the final product, the structures substantially retain the high flame resistance of the polyimide macroballoons. The final structure will vary from rigid to fairly flexible depending upon the bonding agent selected. Any suitable aromatic dianhydride may be used in the preparation of the desired imides. Typical aromatic dianhydrides include those described and referenced in the patents listed above. Due to their ready availability at reasonable prices and the excellent foams which result, pyromellitic dianhydride and 3,3', 4,4 benzophenone tetracarboxylic acid dianhydride (BTDA) are preferred. Any suitable oxime may be reacted with the selected dianhydride to produce the desired imide. Preferably, the oxime has the general formula: EMI5.1 where "x" is a positive integer from 1 to 5. Of these, best results are apparently obtained with caprolactam. While any suitable reaction conditions may be used, we have obtained the best results where the dianhydride is added to the oxime and the mixture is heated to about 1502000C. until imidization is complete, about 5-90 minutes. Optimum results have been obtained at about 170-180 C. for about 30 minutes. In order to produce a superior foaming material, we have found that it is essential that the mole ratio of oxime to dianhydride be in the range of about 0.05:1 to 1.5:1. Above this range, the material forms a coating without foaming, while below this range excessively rigid material is produced. Within this range optimum results occur with a mole ratio of oxime to dianhydride of about 0.5 to 1.0. The imides produced by the above reaction have the general formula: EMI6.1 wherein "x" is an integer from 1 to 5 and "A2" is selected from the group consisting of: EMI6.2 anci mixtures tnereor. The imide thus produced is then esterified by dissolving it in a suitable reactive solvent at a suitable tewperature. Any suitable reactive solvent which acts as an esterifing agent may be used. Typical of these are aliphatic alcohols having up to 7 carbon atoms and aromatic alcohols, which may have halogen or amino substitutions, ana mixtures thereof. We have found that best results are obtained with alcohols having boiling points between about 75 and 1OGOC. Lower boiling alcohols are too reactive and higher boiling alcohols require excessively high processing conditions to dry the resin. Optimum results are obtained with isopropyl alcohol, although good results are also obtained with ethyl alcohol and, especially, secondary alcohols having low reactivity and boiling points in the abovementioned range. The esterification reaction takes place as follows: EMI7.1 wherein "x" is an integer from 2 to 4, "A2" is as listed for the imide above and "R" is an aliphatic or aromatic radical which may have halogen or amino substitutions. This esterification may take place under any suitable conditions. Typically, a mole ratio of imide to esterifying agent of from about 1:8 to 1:15 is preferred to assure rapid esterification at reflux temperature. This solution is heated to reflux (about 70-900C.) until clear, which takes about 60-90 minutes. Once the esterification is complete, the selected diamine or diamines are added to the solution. Preferably, an approximately stoichiometric quantity of diamine is used. Any suitable diamine may be used. Typical diamines include meta-phenylene diamine, para-phenylene di amine; 4,4'-diaminodiphenyl ether, 4,4'-diaminodiphenyl sulfone, 3,3'-diaminodiphenyl sulfone, 4,4'-diaminodiphenyl sulfide, 4,4'-diaminodiphenyl methane, 3,3' diaminodiphenyl methane and mixtures thereof. Of these, best results are obtained with 4,4'-diaminodiphenyl methane which is, therefore, preferred. If desired, aliphatic diamines may be used in combination with these aromatic diamines. Typical aliphatic diamines include 1,3 diaminopropane, 1,4 diamino butane, 1,6-diaminohexane, 1,8-diaminooctane, 1,12 diaminododecane and mixtures thereof. Additives to improve various characteristics of the final foam may be added as desired. Any appropriate additives may be used, such as fillers, surfactants and fire retardants to improve product characteristics. physical characteristics of panels fabricated from adhesively bonded polyimide macroballoons may be varied by adding suitable quantities of various fillers. For example, adding from about 1 to 50 weight percent (based on the final panel weight) glass microballoons to the panels will decrease water absorption and increase the oxygen index. Best results are obtained with about 25 weight percent glass microballoons. Adding suitable quantities of fibers such as glass, graphite, Kevlar polyamids, etc., will improve the load carrying capacity as well as the sheer strength. Microwave absorption of the polyiz.ides can be modified and improved by the addition cf from about 1 to 50 weight percent (based on the weight of the final composite) prior to the drying step of any suitable microwave absorbing material such as graphite powder, ferrites, metal-ceramic corpouncs such as ferro titanate or mixtures thereof. The opt bum combination of overall physical properties combined zits i:aximum microwave absorption material, based on the final composite structure weight. Surfactants (surface active agents) are particularly desirable where macroballoons are produced, since they tend to produce higher cell wall thicknesses and walls of greater resiliency. Typical surfactants include Dow Corning Corp. 190 or 193, FC430 from Minnesota Mining & Manufacturing Co., and L550 from Union Carbide Corp. While any suitable concentration may be used, from about 0.01 to 2% (by weight, based on the weight of the solution prior to drying is preferred. Of these surfactants, best results have been obtained with DC 193. Fire retardants can be added to lower smoke emission, reduce flame spread and extend the burnthrough resistance of the products. Typical fire retardants, which may be typically used in amounts of about 2 to 50 wt. %, based on the weight of the final foam or macroballoons, include Firebrake ZB, aluminum trihydrate, antimony oxide and mixtures thereof. The solution is then dried by any suitable method. Simply heating the solution in an oven to a temperature of about 65-950C. until dry is satisfactory. Other conventional methods, such as spray drying, rotary drying, thin film evaporation, etc. may be used as desired. The resulting free-flowing powder or flakes are non-tacky and may be stored indefinitely at room temperature. We have found that in order to produce uniform high quality macroballoons, it is essential that the foaming powder be in the 0.5 to 10 mm. average particle diameter range. Best results are obtained with particle diameters in the 1.0 to 5.0 mm. range. If the drying process did not produce particles in the desired range, the powder should be ground or pulverized to produce the desired particle size. Typically, the powder may be reduced in size by mechanical grinding. The resulting free flowing powder is suitable for the production of closed cell foam or macroballoons. However, for best results with greatest uniformity, it is often preferred that the powder be further dried (either before or after reduction to the final particle size) at a moderate temperature in a moderate vacuum. Best results are obtained if the powder is dried for about 30 to 120 minutes at about 50 to 800C. at a pressure of about 25 to 29 inches of mercury. The final step in converting the powder into a foam or macroballoons is accomplished by heating the powder to the selected foaming temperature for a suitable period. The reaction which takes place is quite complex, since it is a combined condensation and exchange reaction. The reactions which are believed to take place are detailed in our copending U.S. patent application Serial No, 390,778, filed June 2, 1982. Heating the powder to a temperature of about 90 to 1500C. for about 10 to 60 minutes causes the powder to expand approximately 50 times in volume, producing a uniform, resilient closed cell foam or macroballoons which appears to be a mixture of polyimlde and polyimide-amide polymers. When foamed in a closed mold, using about 2 to 3 volume percent (based on mold volu,te) powder, a well consolidated foam product results. When foamed without volume restraint, individual macroballoons and/or agglomerations of macroballoons result. The foam or volume of macroballoons produced is tough, resilient and will not shrink appreciably or emit significant smoke or toxic by-products when exposed to open flame. Any suitable liquid bonding agent may be used to bond macroballoons prepared as described above into structures. Typical bonding agents are synthetic resins, including the polyimide liquid of this application, polyimide coating resins as described in our depending european Patent Application filed on the saire date as the present applicatirxn epoxies, polyesters, polyimides, polyvinyls, synthetic rubbers, fluorinated and chlorinated hydrocarbon resins, phenolics, urea and melamine resins and mixtures and copolymers thereof. While any suitable temperature may be used, in order to avoid any chance of degradation of the macroballoons, resins curing at temperatures not exceeding about 1500C. are preferred. Somewhat higher curing temperature resins may be used with care. Only sufficient resin to fully wet the macroballoons need be used. Generally, this results in a final structure in which less than 10 percent by weight is resin. This is preferred to maintain the flame and high temperature resistance of the polyimide macroballoons and to keep the structure as light in weight as possible. Of course, the interstices between macroballoons could be entirely filled with resin, if desired. Any suitable wetting agent may be used to increase the wettability of the macroballoons by the bonding agent. The macroballoons may be pre-treated with etchants, solvents, abrasives, etc., as desired to improve adhesion to the bonding agent thereto. Details of the invention will be further understood upon reference to the following examples, which describe preferred embodiments of the methods and compositions of this invention. All parts and percentages are by weight, unless otherwise indicated. Example I About 515.5 g. (1.6 M) of 3,3',4,4'-benzophenone-- tetracarboxylic acid dianhydride (BTDA) and about 45.2 g. (o.4 M) caprolactam are placed in a three liter flask and heated to about 1750C. After about 30 minutes at this temperature the mixture is cooled to about 700C. and about 965 g. of isopropanol is added. This mixture is heated to reflux temperature (about 900C.). Reflux is continued until the mixture appears clear, about 7G minutes. The mixture is cooled to just below about 700C. and about 317.12 g. (1.6 M) 4,4'-diaminodiphenyl methane is added. This mixture is refluxed (at about 900C. for about 15 minutes, then is cooled to room temperature and coated onto aluminum foil. The coating is dried overnight at about 820C. The brittle product is crushed and placed in a vacuum oven at about 820C. for about 30 minutes at a pressure of about 27 in. Hg. The powder is then further crushed to an average (and fairly uniform) particle size of about 3mm. A mold, preheated to about 1100C. is opened, about 2.5 volume percent of the powder is placed therein and the mold is closed. After about 30 minutes at this temperature, the mold is opened and a consolidated, closed cell foam product is removed. The product is found to be resistant to flame and to not shrink appreciably when exposed to direct flame. Example II The procedure of Example I is repeated four additional times, varying only the particle size of the powder heated in the mold. Where Example I used an average particle diameter of about 3 mm., these additional experiments use average particle diameters of about: II(a) 0.1 mm., II(b) 0.5 mm., II(c) 10 mm., and II(d) 15 mm. The foam produced in II(a) is a mixture of open and closed cell foam having poor physical properties. Examples II(b) and II(c) produce good closed cell foams, while II(d) produces foam with large, irregular closed cells giving a non-unifdrm foam with lower uniformity and resiliency. Thus, foaming powder particle sizes in the 0.5 to 10 mm. range are preferred for good closed cell foam, with best results around the 3mm. size of Example I. Example III The experiment of Example I is repeated except that the vacuum drying step is omitted. The final foam is a mixture of open-cell and closed-cell foams due to the excess of solvent present in the powder. Example IV The procedures of Example I are repeated, except that the second drying step using a partial vacuum is performed after the final particle size reduction, rather than before. The foam produced is substantially identical to that produced in Example I. Example V The procedures of Example I are repeated, except that in place of isopropanol, the following solvents are used: 111(a) ethanol (Boiling Point 78.50C.), III(b) aminoethyl alcohol (B.P. 172.20C.), III(c) 2-fluro ethanol (B.P. 103.35 C.) , III(d) methyl alcohol (B.P. 420C.), III(e) benzene (B.P. 800C.O, and III(f) acetone (B.P. 56.5 C.) . Excellent results are obtained with the alcohols having boiling points in the 75 to 110 C, range (Examples 111(a) and III(c)). The higher boiling alcohol of Example III(b) produces poor results due to difficulty in adequately drying the powder. The lower boiling alcohol of Example III(d) is too reactive and produces poor foam. The inert solvents of Examples III(e) and II 1(f) do not act as esterifying agents and fail to produce a foam. Example VI Five samples are prepared as described in Example I up to the heating to foam step. The five powder samples are placed in preheated circulating air ovens at the following temperatures for the following time periods: VIa) about 125 C, for about 40 min., VI(b) about 2100C. for about 30 min., VI(c) about 2500C. for about 50 min., VI(d) about 2800C. for about 20 minutes and VI(e) about 380 C. for about 20 min. The samples of Examples VI(b), VI(c) and VI(d) all produce foam having excellent physical properties. The foam of Example VI (a) is not fully expanded and cured. The sample of Example VI(e) shows a mixture of open-cell and closed-cell foams due to the high temperature of foaming. Example VII The procedures of Example I are repeated four additional times, varying only the quantity of caprolactam used. Where Example I used about 45.2 g. (0.4M) of caprolactam te Sive a molar ratio of caprolactam to BDTA (515.5 g.r 1.6M) of about 0.25:1, these four additional experiments use caE,roXactaF. quantities of about: VII(a) 180.8 g. (1.6 1:1 ratio), VII(b) 220.8 g. (2.OM, 1.25:1 ratio), VII(c) 271 g. (2.4M, 1.5:1 ratio), and VII(d) 361.6 g. (3.2my 2:1 ratio). The foam produced in experiments VII(a) and VII(b) have excellent foam rise characteristics, while that produced in VI;S(c) has low foam rise and the sample of VII(d) does not foam. This demonstrates that ratios of oxime to dianhydride in the 0.05:1 to 1.5:1 range are necessary for the production of good quality foam. Example VIII The experiment of Example I is repeated, except that the following diamines are used in place of the 4,4' diamino-diphenyl methane: VIII(a) m-phenylene diamine (0.375 M), VIII(b) 4,4'-diaminodiphenyl sulfone (0.375M), VIII(c) 4,4'-diaminodiphenyl oxide (0.1875M), and 4,4' diaminodiphenyl sulfide (0.1875M). In each case the resulting foam has a uniform cellular structure and has -excellent heat and flame resistance. The flexibility and resiliency varies somewhat among the sub-examples. Example IX The procedure of Example I is repeated with the only change being the substitution of the following oximes for the 0.4 M caprolactam specified in Example I: IX(a) 2 pyrrolidone (0.4M), IX(b) 2-piperidone (0.4M), IX(c) caprolactam (0.2M) and 2-piperidone (0.2M). The product in each case is an excellent flame resistant foam, with slight changes in physical properties with the different oximes. Example X The experiment of Example I is repeated with four additional samples with the addition of the following agents to the liquid just prior to the first drying step: X(a) about 0.5 wt. % (based on solids) L 550 (available from Union Carbide), X(b) about 1.0 wt. % Corning 193 (available from Dow Corning Corp.), X(c) about 43 g. of very finely divided aluminum hydroxide and X(d) about 60 g. of about 0.25 inch graphite fibers. The samples having the surfactants (Examples X(a) and X(b)) are found to have increased resiliency, while the filler of Example X(c) produces somewhat brittle foams and the reinforcing fibers of Example X(d) results in greater foam strength. Example XI The steps of Example I are repeated except for the drying steps. The liquid is sprayed into a chamber preheated to about 750C. using a high speed atomizer. By carefully adjusting the atomizer, particles in the desired size range are produced. Larger particles are ground to the desired size range where necessary. Samples of the spray dried powder are foamed as described in Example I with and without the second moderate vacuum, drying step. While both samples produce good foam, the second drying is found to result in foam having slightly better physical properties. Example XII Powder samples prepared by the procedures of Example I and Example XI are sprayed into a moving hot air stream maintained at about 300 OC. The particles are found to spontaneously expand into macroballoons which flow with the air stream to a collector. Example XIII The experiments of Example XII are repeated, except that about 20 g. of DC 193 surfactant is added to the liquid prior to drying. The macroballoons obtained using the surfactant have slightly thicker walls and greater resiliency. Example XIV Macroballoons produced by the methods of Example XIII are mixed with just enough of the liquid of Example I (at the pre-drying stage) to wet the macroballoons. The mixture is packed into a mold preheated to about 2600C.. After about 30 minutes, the consolidated article is removed from the mold. The macroballoons are solidly bonded together by the cured resin. The liquid appears to have polymerized without significant additional foaming. Example XV A quantity of macroballoons produced in Example XIII are placed in a mold which is slightly overfilled. The mold is closed1 applying about 0.5 to 1.0 psig on the macroballoons. The mold is maintained at about 3700C. for about 15 minutes. A consolidated closed cell structure results with the macroballoons adhering well to each other. Example XVI The experiments of Example I are repeated with four additional samples with the addition of the following agents to the liquid just prior to the initial drying step: XVI(a) about 5 wt. % aluminum trihydrate (based on solids); XVI(b) about 30 wt. % aluminum trihydrate (based on solids); XVI(c) about 10 wt. % antimony trioxide; and XVI(d) about 15 wt. % Firebrake ZB. Processing is continued as described in Example I. Each of these foam samples, plus a sample of foam produced in Example I is exposed to a direct flame. Those samples of XVI which includes a fire retardant are found to produce less smoke, have slower flame spread and to have a greater resistance to burn through than the sample of Example I. Example XVII Samples of foamable powder are prepared as described in Example I. Three mold set-ups are prepared as follows: two sheets of material (as specified below) are temporarily adhered to rigid backing and arranged in a facing arrangement, spaced about 0.25 inch apart with the foamable powder uniformly spread over one sheet. The powder occupies about 5% of the volume between the spaced sheets. In these tests, in XVII(a) uses two sheets of aluminum foil, XVII(b) uses two sheets of cured polycarbonate resin and XVII(c) uses one sheet of pnenolic resin and one sheet of aluminum foil. In each case, the sheets and powder are heated to about 1200C for about 40 minutes, cooled to room temperature, and removed from the rigid backing. In each case a well bonded composite sandwich of foam between the outer sheets results. The test of XVII(a) is repeated with the sheets pressed together to a thickness of about 0.18 inch at a temperature of about 1750C, immediately after foaming. A higher density composite results. Example XVII I Three aluminum honeycomb structures, each having a thickness of about 0.5 inches, overall dimensions of about 12 inches-by 12 inch-es and honeycomb hexagon diameters of about 0.25 inch are provided. One honeycomb, XVIII(a) is partially filled (about 58 by volume) with a foamable powder prepared as described in Example I and two other honeycomb structures are entirely filled as follows: XVIII(b) with macroballoons prepared as described in Example XII and XVIII(c) with the mixture of macroballoons and liquid described in Example XIV. In each case, the honeycomb structure is held between two rigid mold surfaces and heated to about 2500C for about 30 minutes. In each case, a strong structure with the foam/macroballoons bonded to the honeycomb results. The sample at XVIII(c) shows superior bonding. Example XIX A quantity of macroballoons is prepared as described in Example XI II. Weighed samples of the macroballoons are each mixed with just enough of the following catalyzed epoxy resins to thoroughly wet the macroballoons. Resins used are: XIX (a) Aralidite 7065 available from Ciba Geigy, XIX(b) Epon 154, available from the Shell Chemical Co. and XIX(c) Aralidite 8047, a flame retardant epoxy from Ciba-Geigy. The coated samples are placed in open rectangular molds and the resins are allowed to fully cure at room temperature. In each case a rigid lightweight structure results. Reweighing the structures shows that less than 10 wt.% of the structures is resin. Each structure has excellent flame resistance with XIX(c) producing the greatest resistance. Example XX Additional samples of macroballoons prepared as described in Example XIII are mixed with adhesive resin solutions as follows: XX(a) a cellulose acetate butyrate adhesive, available from the Dow Chemical Co. under the Dow 276-V9 trademark, XX(b) a water dispersed polyvinyl acetate emulsion available from the Borden Co. under the trademark Gelva S-55 and XX(c) another polyvinyl acetate emulsion available under the Ucar Lates 130 mark from Union Carbide. The samples are placed in open rectangular molds and are heated to about 1000C. for about 60 minutes. Well bonded structures result with less than 10 wt.% resin. Example XXI The experiment of Example I is repeated, except that the foamable powder is sprinkled lightly over a moving web instead of being placed in a mold. The web is continuously moved through a heated zone where the powder is heated to about 1500C. for about 10 minutes, causing the powder to expand into macroballoons and a few aggregates of several macroballoons. Four samples of the resulting macroballoons are each coated with-resin as follows: XXI(a) a polyamide available from General Mills Chemical under the Versamid C trademark and XXl(b) a polyamide available from the Dow Chemical Co. under the D.E.H-. trademark, XXI(c) a vinyl pyridine latex, Pliobond LVP-4668 available from Goodyear and XXI(d) VPX-500, a vinyl pyridine latex from E.I. duPont de Nemours. The samples are placed in cylindrical molds and any excess resin is allowed to drain away. The molds are heated as follows: XXI (a) 2000F. for about 60 min., XXI(b) 3000F. for about 20 min., XXI(C) 1400F. for about 30 min., and XXI(d) 1500F. for about 20 min. In each case, a well bonded lightweight structure results. Pre- and postweighings show that less than about 10 of the structure weight is resin. Example XXII Samples of macroballoons prepared as described in Example XXI are placed in two molds. The first mold is flooded with a mixture of a urea-formaldehyde resin (diluted to 40% solids by weight) available from American Cyanamid Co. under the Urac trademark and about 3 wt.t (based on resin weight) of-a catalyst, HF6 from National Casein Corp. The second mold is flooded with a thin aqueous mixture of Resimene, a melamine-formaldehyde resin from Monsanto and about 4 wt.% (based on resin weight) of ammonium sulfate catalyst. Each mold is drained of excess solution. The first mold is heated to about 1200C. for about 2 hours and the second mold is heated to about 900C. for about 4 hours. The products are well consolidated lightweight structures, with slightly over about 10 wt.% resin. Example XXIII A quantity of macroballoons prepared as described in Example XIII is divided into four samples. Each sample is mixed with enough catalyzed Epon 154 epoxy resin from Shell Chemical Co. to lightly coat the macroballoons. The samples are then treated as follows: XXIII ( ) the coated macroballoons are spread in an about 0.5 inch thick layer over a thin aluminum foil, then a second foil is placed over the layer, XXIII(b) the coated macroballoons are spread in an about 1 inch thick layer on a mold-release coated surface and a thin glass fiber fabric impregnated with catalyzed Epon 154 resin is placed over the macroballoon layer and a second 1 inch layer of coated macroballoons is laid thereover, XXIII(c) an aluminum box section structural shape having a length of about 2 feet and a lxl inch cross-section is filled with the coated macroballoons and XXIII(d) a titanium honeycomb structure having a thickness of about 2 inches and a cell diameter of about 0.3 inch is filled with the coated macroballoons. Each of these structures is heated to about 900C. until cure is complete. In each case a lightweight structure results with the macroballoons bonded to each other and to the adjacent elements. The panels of Examples XXIII(a) and (b) exhibit greater strength and rigidity than macroballoon structures used alone. The structural members of Examples XXIII(c) and (d) show greater impact resistance and rigidity. Example XXIV The experiment described in Example XIX(a) is repeated, with the following changes: XXIV(a) about 5 wt.% (based on resin weight) of finely chopped graphite fibers is added to the epoxy coating liquid prior to coating the macroballoons, XXIV(b) about 10 wt.t (based on resin weight) of finely chopped glass fibers is added to the epoxy coating liquid just prior to coating the macroballoons. After coating and curing as described in Example XIX(a), the lightweight structures are tested and are found to be slightly stronger and more rigid than the corresponding structures without the fiber additives. Although specific components, proportions and conditions have been specified in the above examples, these may be varied with similar results, where suitable. In addition, other materials may be added to the foamable material, such as fillers, colorants, ultraviolet absorbers or the like. Other applications, modifications and ramifications of the present invention will occur to those skilled in the art upon reading the present disclosure. These are intended to be included within the scope of the invention as defined in the appended claims.

Claims: CLS9E 1. A process for producing high temperature and flame resistant macroballoon structures which comprises the steps of: reacting an oxime with an aromatic tetracarboxylic acid dianhydride in a mole ratio thereof between about 0.05:1 and 1.5:1 to produce an N-substituted imide; esterfying said N-substituted imide by mixing therewith a reactive solvent; adding thereto at least one diamine; drying the resulting liquid composition; reducing the dried material to an average particle diameter of from about 0.5 to 10 mm.; separating said particles from each other; heating said particles to a temperature in the range of about 90 to 1500C. while substantially preventing interparticle contact, whereby said particles expand producing a plurality of discrete macroballoons; ; coating said macroballoons with a thin layer of a liquid bonding agent; bringing said macroballoons into contact with each other in a desired structural configuration; and curing said bonding agent to a dry state; whereby a lightweight structure of bonded macroballoons results. 2. The process according to claim 1 wherein said liquid bonding agent is a synthetic resin selected from the group consisting of epoxies, polyesters, polyimides, polyvinyls, synthetic rubber, fluorinated hydrocarbons, chlorinated hydrocarbons, phenolics, ureas, melamines and mixtures and copolymers thereof. 3. The process according to claim I wherein the bonding agen-t constitutes up to about 10 wt.% of the dry light weight structure. 4. The process according to claim 1 wherein said structural configuration is obtained by filling a mold with said coated macroballoons and removing the lightweight structure from the mold after curing of the bonding agent. 5. The process according to claim 1 wherein said desired structural configuration is obtained by curing said coated microballoons in contact with a surface so that said bonding agent also serves to bond said macroballoons to said surface. 6. The process according to claim I wherein said particles are heated and expanded into macroballoons by feeding said particles into a moving hot air stream. 7. The process according to claim I wherein said aromatic tetracarboxylic acid dianhydride is selected from the group consisting of 3,3', 4,4'-benzophenone tetracarboxylic acid dianhydride, pyromellitic dianhydride, and mixtures thereof, and wherein said oxime is selected from the group consisting of caprolactam, 2-pyrrolidone, 2piperidone and mixtures thereof. 8. The process according to claim 1 wherein said oxime is caprolactam, said reactive solvent is isopropyl alcohol and said diamine is 4,4'-diaminodiphenyl methane. 9. The process according to claim 1 further including the step of adding a filler to said liquid bonding agent prior to said coating step and wherein said filler is selected from the group consisting of aramid fibers, graphite fibers, glass fibers, carbon fibers, graphite powders, fluorocarbon powders and mixtures thereof. 10. The process according to claim 1 further including the step of adding from about 2 to 30 weight percent, based on the macroballoon weight, of a fire retardant to said liquid composition prior to said drying step; said fire retardant composition being selected from the group consisting of aluminum trihydrate, antimony oxide and mixtures thereof. 11. The process according to claim 1 further including the step of adding prior to said drying step from about 1 to 50 weight percent, based on final composite weight, of glass macroballoons. 12. The process according to claim 11 wherein about 25 weight percent glass macroballoons is added. 13. The process according to claim 1 further including the step of adding prior to said drying step from about 1 to 50 weight percent, based on final composite weight, of a radar absorbing material selected from the group consisting of graphite, ferrites and metal ceramic compounds. 14. The process according to claim 13 wherein said microwave absorbing material is ferro titanate, of which about 10 weight percent is added.

Inventors: GAGLIANI, JOHN, LONG, JOHN V.
Applicants: GAGLIANI, JOHN, LONG, JOHN V.
Application year: 1983
Main classification: C08J9
IPC codes: B29C67, B29C59, C08J9