LIGHT-SENSITIVE SILVER HALIDE COLOR PHOTOGRAPHIC MATERIAL

Abstract: Disclosed is a light-sensitive silver halide color photo­ graphic material having at least one light-sensitive silver halide emulsion layer on a support, characterized in that said light-sensitive silver halide emulsion layer contains a cyan coupler represented by the formula (I) shown below, and said light-sensitive silver halide emulsion layer and/or a layer contiguous to said light-sensitive silver halide emulsion layer contains a colored cyan coupler represented by the formula [II] Formula [I]: wherein X, R₁, and R₂ are as defined in the specification; Formula [II]: wherein (Coup-) c , L, Q₁, Q₂ M, j, and G are as defined in the specification.

Description: This invention relates to a light-sensitive silver halide color photographic material which is in particular highly sensitive and has excellent properties such as graininess, gradation, color reproduction, processing adaptability and others. More particularly, it pertains to a light-sensitive silver halide color photographic material in which the image to be formed in the cyan image forming layer is very high in sensitivity and at the same time excellent in its color reproduction and processing adaptability. It is generally strongly demanded to provide a light-sensitive silver halide color photographic material having high sensitivity as well as excellent image quality. However, it is very difficult to increase dramatically the sensitivity of a light-sensitive silver halide color photographic material. In particular, partly because the cyan image forming layer in a multi-layer light-sensitive silver halide color photographic material is generally positioned on the support side, high sensitization of said light-sensitive layer and improvements in graininess, gradation, color reproduction and other desirable image qualities in said layer are particularly difficult and no satisfactory technique has been developed in this respect. This may be due to the loss during development by delayed diffusion of an aromatic primary amine developing agent in sensitive layers contiguous to the support of the multi-layer light-sensitive color photographic material or optical loss during exposure by a non-sensitive layer positioned at the upper part of the material. Moreover, as a problem inherent in the cyan image forming layer, the colored image formed by the color development processing is subject to poor color return (i.e. a phenomenon that a cyan dye altered to a substantially colorless compound cannot completely be returned to the original dye). These problems make it very difficult to obtain a satisfactory cyan image forming layer. As a further inherent problem in the cyan image forming layer, a naphthol type or a phenol type cyan coupler, when forming a cyan color image through the coupling reaction with an oxidation product such as that of an aromatic primary amine developing agent, does not form an ideal spectroscopic absorption spectrum, but generally has a broad side-absorption centred around green light. Such a side-absorption is not desirable in color reproduction of a light-sensitive material. To remove such a distortion in color reproduction, the so called masking method is generally used, in which a colored color image forming coupler (namely a colored coupler) is used, as described in detail in J. Photo. Soc. Am. 13,94 (1947), J. Opt. Soc. Am. 40,166 (1950) or J. Am. Soc. 72, 1533 (1950). However, in the masking method of the prior art, no masking effective over all spectroscopic absorption spectra has yet been obtained. For example, most of the colored couplers of the prior art, as disclosed in U. S. Patent 2,521,908 are too shallow in colors at the peak absorption thereof, and accordingly it is impossible to achieve a uniform masking effect over all the ranges of the spectroscopic absorption spectrum. Also, some colored couplers, in combinations with couplers for formation of colorless cyan images, are too different in respective reaction rates or relative reactivities from each other to obtain an uniform masking from a low light exposure region to a high light exposure region. Further, among the colored couplers of the type which can release diffusible dyes, there exist some which are excellent in color phase, but, when combined with a cyan coupler, many of them form minute droplets as in a mixed dispersion, as the result of the action caused by their hydrophilic groups. Accordingly, an object of this invention is to provide a light-sensitive halide color photographic material having excellent color reproduction and gradation and reduced poor color return and which is high in sensitivity of the cyan image forming layer. The present invention provides a light-sensitive silver halide color photographic material having on a support at least one light-sensitive silver halide emulsion layer containing a cyan coupler and said light-sensitive silver halide emulsion layer and/or a layer contiguous to said light-sensitive silver halide emulsion layer containing a colored cyan coupler characterised in that the cyan coupler is of formula (I); wherein X represents hydrogen or a group or atom eliminable on coupling with an oxidation product of an aromatic primary amine color development agent; R₁ represents a substituted or unsubstituted naphthyl group or a substituted or unsubstituted heterocyclic group provided that a carbon atom thereof is bonded to the adjacent nitrogen atom of the ureido group, or a phenyl group having at least one substituent which is a trifluoromethyl, nitro, cyano, -COR, -COOR, -SO₂R, -SO₂OR, (where R represents an aliphatic group or an aromatic group, and R′ represents a hydrogen atom, an aliphatic group or an aromatic group) with the proviso that, when said substituent is cyano or SO₂R in the p-position relative to the ureido group, the four remaining positions are not all unsubstituted; and R₂ represents an aliphatic group or an aromatic group necessary for imparting diffusion resistance to the said cyan coupler or a cyan dye formed therefrom; and the colored cyan coupler is of formula (II): wherein (Coup-) c represents a cyan coupler residue which is attached at its coupling position to L; L represents a divalent linking group; Q₁ and Q₂ each represent a photographically inactive mono-valent group; M represents a cation or hydrogen; j is 0 or 1; and G represents an acyl group or an alkyl sulfonyl group having 1 to 8 carbon atoms or an arylsulfonyl group having 6 to 8 carbon atoms. Preferably the material is such that the light-sensitive silver halide emulsion layer and/or a layer contiguous to said light-sensitive silver halide emulsion layer also contains at least one colored magenta coupler of the formula (III): (Coup-) M - N = N - W wherein (Coup-) M represents a magenta coupler residue (with the proviso that the azo group is bonded to the active site of the magenta coupler); and W represents a residue of an unsaturated cyclic compound. These materials were found to provide a light-sensitive silver halide color photographic material high in sensitivity or the cyan image forming layer, with good color return in processing steps and excellent in color reproduction and gradation. Preferable cyan couplers according to the formula (I) are represented typically by the following formula (Ia) or (Ib): In the above formula (Ia), Y₁ represents triflouromethyl, nitro, cyano or a group represented by -COR, -COOR, -SO₂R, -SO₂OR, R represents an aliphatic group (preferably an alkyl group (e.g. having 1 to 10 carbon atoms (e.g. methyl, butyl, cyclohexyl, benzyl)) or an aromatic group (preferably a phenyl group (e.g. phenyl or tolyl)), and R′ represents a hydrogen atom or a group represented by R. Y₂ represents an aliphatic group (preferably an alkyl group having 1 to 10 carbon atoms (e.g. methyl, t-butyl, ethoxyethyl, cyanomethyl)), an aromatic group (preferably a phenyl group, a naphthyl group (e.g. phenyl, tolyl)), a halogen atom (e.g. fluorine, chlorine, bromine), an amino group (e.g. ethylamino, diethylamino), a hydroxy or a substituent represented by Y₁. These rings may have any desired substituents theron, including, for example, alkyl groups having 1 to 10 carbon atoms (e.g. ethyl, i-propyl, i-butyl, t-butyl, t-octyl)-, aryl groups (e.g. phenyl, naphthyl), halogen atoms (e.g. fluorine, chlorine, bromine), cyano, nitro, sulfonamide groups (e.g. methanesulfonamide, butanesulfonamide, p-toluenesulfonamide), sulfamoyl groups (e.g. methylsulfamoyl, phenylsulfamoyl), sulfonyl groups (e.g. methanesulfonyl, p-toluenesulfonyl), fluorosulfonyl groups, carbamoyl groups (e.g. dimethylcarbamoyl, phenylcarbamoyl), oxycarbonyl groups (e.g. ethoxycarbonyl, phenoxycarbonyl), acyl groups (e.g. acetyl, benzoyl), heterocyclic groups (e.g pyridyl group, pyrazolyl group), alkoxy groups, aryloxy groups, and acyloxy groups. R₂ and X are as defined above. m is an integer of 1 to 3, and n is an integer of 0 to 3, with the proviso that m + n should be 5 or less, and, when a cyan or -SO₂R group is bonded at the p-position of the ureido group, m + n should be from 2 to 5. Z represents a group of non-metallic atoms which, together with the carbon atoms to which they are attached, form a heterocyclic group or naphthyl group, and as a heterocyclic group, a five-membered or six-membered heterocyclic group containing 1 to 4 hetero atoms which are nitrogen atoms, oxygen atoms or sulfur atoms. For example, there may be included a furyl, thienyl, pyridyl, quinonyl, oxazolyl, tetrazolyl, benzothiazolyl or tetrahydrofuranyl group. R₂ represents an aliphatic group or an aromatic group necessary for imparting diffusion resistance to a cyan coupler represented by the above formula (I) or a cyan dye to be formed from said cyan coupler, preferably an alkyl group having 4 to 30 carbon atoms, an aryl group or a heterocyclic group. For example, there may be included a straight or branched alkyl group (e.g. t-butyl, n-octyl, t-octyl, n-dodecyl), an alkenyl group, a cycloalkyl group, a five-membered or six-membered heterocyclic group or a group represented by the formula (Ic): In the above formula, J represents an oxygen atom or a sulphur atom, k represents 0 or an integer of 1 to 4; I represents 0 or 1; when k is 2 or more, two or more existing R₄'s may be the same or different; R₃ represents a straight or branched alkyl having 1 to 20 carbon atoms; and R₄ represents a monovalent atom or group, including, for example, a hydrogen atom, a halogen atom (preferably chloro, bromo), an alkyl group {preferably a straight or branched alkyl group having 1 to 20 carbon atoms (e.g. methyl, tert-butyl, tert-pentyl, tert-octyl, dodecyl, pentadecyl, benzyl, phenethyl)}, an aryl group (e.g. phenyl), a heterocyclic group (preferably a nitrogen containing heterocyclic group), an alkoxy group {preferably a straight or branched alkyloxy group (e.g. methoxy, ethoxy, tert-butyloxy, octyloxy, decyloxy, dodecyloxy)}, an aryloxy group (e.g. phenoxy), a hydroxy group, an acyloxy group {preferably an alkylcarbonyloxy group, an arylcarbonyloxy group (e.g. acetoxy, benzoyloxy)}, a carboxy group, an alkyoxycarbonyl group (preferably a straight or branched alkyloxycarbonyl group having 1 to 20 carbon atoms), an aryloxycarbonyl group (preferably phenoxycarbonyl), an alkylthio group (preferably having 1 to 20 carbon atoms), an acyl group (preferably a straight or branched alkycarbonyl group having 1 to 20 carbon atoms), an acylamino group (preferably a straight or branched alkylcarboamide, benzenecarboamide having 1 to 20 carbon atoms), a sulfonamide group (preferably a straight or branched alkylsulfonamide group having 1 to 20 carbon atoms, benzenesulfonamide group), a carbamoyl group (preferably a straight or branched alkylaminocarbonyl group having 1 to 20 carbon atoms, phenylaminocarbonyl group), or a sulfamoyl group (preferably an alkylaminosulfonyl group having 1 to 20 carbon atoms, phenylaminosulfonyl group). X represents a hydrogen atom or a group or atom eliminable on coupling with an oxidation product of a color developing agent. For example, there may be included halogen atoms (e.g. chlorine, bromine, fluorine), aryloxy groups, carbamoyloxy groups, carbamoylmethoxy groups, acyloxy groups, sulfonamide grouys, succinimide groups, of which an oxygen atom or nitrogen atom is bonded directly to the coupling position. More specifically, there may be mentioned those as disclosed in U. S. Patent 3,741,563, Japanese Provisional Patent Publication No. 37425/1972, Japanese Patent Publication No. 36894/1973, Japanese Provisional Patent Publication Nos. 10135/1975, 117422/1975, 130441/1975, 108841/1975, 120334/1975, 18315/1977 and 105226/1978. The cyan coupler used in this invention can readily be synthesized by use of the methods as described in, for example, U.S. Patent 3,758,308 and Japanese Provisional Publication No. 65134/1981. Preferable compounds of the cyan coupler of the formula (I) are exemplified below, but the present invention is not limited thereby. It should be noted that, while couplers C-22 and C-37 are excluded from the claims, their retention here is necessary to give meaning to the paragraph immediately preceeding the examples below. As other preferable compounds there may also be employed those as disclosed in, for example, Japanese Laid-open Patent Application No. 204543/1982, 204544/1982 and 204545/1982 (EP-A-67689) falling within Article 54(3) of the EPC, which discloses a photosensitive material comprising a phenol cyan coupler substituted in the 2 position with a phenyl ureido group, in the 4 position with an eliminable group and in the 5 position with an acylamino group; and Japanese Patent Application Nos. 131312/1981 (EP-A-73146) falling within Article 54(3) of the EPC, which discloses a method of forming a photographic image in the presence of a phenol cyan coupler which is substituted in the 2 position with a substituted phenyl ureido group, in the 4 position with an eliminable group and in the 5 position with an acylamino group; and 131313/1981 and 131314/1981 (EP-A-73145) falling within Article 54(3) of the EPC, which discloses a phenol cyan coupler substituted in the 2 position with a ureido or naphthylureido group and in the 5 position with an acylamino group. Next the colored cyan coupler represented by the formula (II) is to be described below. In the formula (II), (Coup-) c represents a cyan coupler residue such as a phenol or naphthol type cyan coupler residue. L represents a divalent linking group connecting the coupler structure moiety to the due structure moiety and bonded to the active site of the cyan coupler residue. L may be exemplified by, for example an oxygen atom a sulfur atom, -NHSO₂-(CH₂)₃-O-, -NHSO₂-(CH₂)₄-O-, -OSO₂(CH₂)₂O-, -OSO₂(CH₂)₄-O-, -O-CONH-, -OCONHCH₂-, -O-CO, -O-COCH₂-, -O-CO-(CH₂)₁-O- (where 1 represents 0, 1, 2, 3, or 4) (with proviso that in the above divalent groups, the coupler structure moieties are meant to be bonded to the left side thereof, while the dye structure moieties to the right side). G represents an acyl group of an alkylsulfonyl group having 1 to 8 carbon atoms or an arylsulfonyl group having 6 to 8 carbon atoms. Q₁ and Q₂ each represent a photographically inactive monovalent group, as exemplified by hydrogen atom, halogen atoms (e.g. fluorine, chlorine), hydroxy, cyanol, alkyl groups e.g. methyl, t-butyl, octyl, benzyl), alkoxy, alkylthio, amide, alkoxycarbonyl and alkylcarbamoyl groups. M is cation (an alkali metal ion, ammonium ion, etc.) or a hydrogen atom. J is 0 or 1. In the following, typical examples of the colored couplers represented by the formula [II] are enumerated, but this invention is not limited thereto. The above compounds can be synthesized according to, for example, the methods as disclosed in U.S. Patent 3,476,563 or Japanese Provisional Patent Publication No. 10135/1975. The colored magenta coupler represented by the formula (III) is preferably a compound represented by the following formula (IV): wherein Ac represents a phenyl group, a naphthyl group or an acyl group which further may have substituents incorporated therein; R₅ to R₇ each represent the same group as Q₁ in the formula (II); and Ar represents a phenyl group, a naphthyl group or a heterocyclic group. Also, as the compounds represented by the formula [III], the following examples may be mentioned, but of course they are not limitative of this invention. The above compounds can be synthesized according to the methods as disclosed in U.S Patents 2,763,552; 2,983,608; 3,519,429; 3,615,506 and 3,476,564; U.K. Patent No. 1,044,778; Japanese Provisional Patent Publication Nos. 123,625/1974, 131,448/1974, 52,532/1979 and 42,121/1977. The compound of formula [I], namely the colorless cyan coupler is incorporated in a silver halide emulsion layer. The amount to be incorporated may be 0.07 to 0.7 mole per mole of a silver halide, and may be incorporated in a conventional manner, by, for example, dissolving in a high boiling solvent as disclosed in U.S Patent 2,322,027. The compound of formula [II], namely the colored cyan coupler can be generally dissolved in either water or an organic solvent, and may be incorporated into a multi-layer light-sensitive material by use of a suitable solvent. For example, it may be dissolved in water in the presence of a surfactant, an auxiliary solvent such as ethyl acetate, ethyl alcohol, etc. or in the presence of an alkali, or alternatively by dissolving in a high boiling solvent as disclosed in U.S. Patent 2,322,027. The compound of formula [III], that is the colored magenta coupler may be added into a multi-layer light-sensitive material similarly as the compounds [I] and [II] by dissolving in a suitable solvent. The colored coupler represented by the formula [II] or [III] may be incorporated directly into the silver halide emulsion layer containing the compound of the formula [I], namely the cyan image forming layer, or alternatively into a layer contiguous thereto. The total amount of the colored coupler of this invention to be coated should preferably be determined so that the optical density at the absorption peak wavelength under the coated state may be 0.05 to 1.0. The colored magenta coupler may be coated in the cyan image forming layer of this invention in an amount so that the optical density at the absorption peak wavelength may be 0.005 to 0.5. The cyan coupler is generally used by being incorporated in a red sensitive silver halide emulsion. However, it is not necessarily required to be contained in the red sensitive silver halide emulsion, but, in combinations with other couplers or spectral sensitizers, it may also be used in combination with a blue sensitive silver halide emulsion or a green sensitive silver halide emulsion. As the silver halide to be used in the silver halide emulsion, there may be included any desired silver halide conventionally used in silver halide emulsion, such as silver bromide, silver chloride, silver iodobromide, silver chlorobromide, silver chloroiodobromide and the like. The silver halide emulsion constituting the silver halide emulsion may be prepared according to all preparation methods, including first the conventional preparation methods, as well as various other methods, such as the method as disclosed in Japanese Patent Publication No. 7772/1971, namely the preparation method of the so called conversion emulsion, comprising forming an emulsion of silver salt grains comprising at least a part of silver salts greater in solubility than silver bromide and then converting at least a part of these grains into silver bromide or silver iodide or the preparation method of the Lipman emulsion comprising minute particulate silver halide or 0.1 µmor less. Further, the silver halide emulsion may be chemically sensitized by using either singly or optimally in combination sulfur sensitizers such as allylthiocarbamide, thiourea, cystine, etc; or active or inactive selenium sensitizers; and reducing sensitizers such as stannous salts, polyamines; noble metal sensitizers such as gold sensitizers, typically potassium aurithiocyanate, potassium chloroaurate, 2-aurosulfobenzthiazolemethyl chloride, etc; or sensitizers of water soluble salts such as of ruthenium, rhodium, iridium, etc., typically ammonium chloropalladate, and so on. It is also possible to incorporate in the silver halide emulsion various known additives for photography such as those disclosed in, for example, Research Disclosure, December, 1978, Item 17643. The silver halide may be subjected to spectral sensitization for imparting light-sensitivity to the necessary light-sensitive wavelength region by selection of a suitable sensitizing dye. As such sensitizing dyes, there may be employed various kinds of dyes, which may be used either as a single kind or as a combination of two or more kinds. As the spectral sensitizing dyes to be employed in this invention there may be included typically cyanine dyes, melocyanine dyes or complex cyanine dyes as disclosed in U. S. Patents 2,269,234; 2,270,378; 2,442,710; 2,454,620; and 2,776,280. The color developer to be used in this invention may preferably contain an aromatic primary amine type color developing agent as principal ingredient. Typical examples of this color developing agent are p-phynylenediamine type compounds, including for example, diethyl-p-phenylenediamine hydrochlorides, monomethyl-p-phenylenediamine hydrochlorides, dimethyl-p-phenylenediamine hydrochlorides, 2-amino -5-(N-ethyl-N-dodecylamino)-toluene, 2-amino-5-(N-ethyl-N-β-methanesulfonamidoethyl)aminotoluene sulfate, 4-(N-ethyl-N-β-methanesulfonamidoethylamino)-aniline, 4-(N-ethyl-N-β-hydroxyethylamino)aniline, 2-amino-5-(N-ethyl-N-β-methoxyethyl)aminotoluene and others. After development, conventional steps of bleaching, fixing or bleach-fixing, washing and drying for removal silver and silver halide are conducted. This invention is illustrated in more detail by referring to the following Examples, by which the embodiments of this invention are not limited at all. Although exemplary compounds C-22 and C-37 are not covered by this invention because they possess an -SO₂R grouping in the para-position relative to the ureido group, the form remaining positions being insubstituted, nevertheless these compounds do illustrate the same behaviour as that of the compounds of formula (I) which are covered. Example 1 The couplers and the colored cyan couplers including the combinations of the couplers and the colored cyan couplers according to this invention as indicated in Table 1 were sampled in amounts as indicated in Table 1, respectively, and added to a mixture of dibutyl phthalate in an amount equal to the total amount of each combination and ethyl acetate in an amount three times said total amount and dissolved therein by heating to 60°C. Each solution was mixed with 200 ml of a 5 % aqueous gelatin solution containing 20 ml of a 5 % aqueous solution of Alkanol B (alkylnaphthalene sulfonate, produced by Du Pont de Nemours & Company), and emulsified in a colloid mill to obtain an emulsified product to prepare each dispersion of a coupler and a colored coupler. Then, each dispersion was added to a red sensitive silver iodobromide emulsion (containing 7 mol % of silver iodide) containing 0.1 mol of silver, followed by addition of 0.1 g of the reaction product of 1,2-bisvinylsulfonylethane with taurin and the resultant mixture was coated on a transparent cellulose triacetate film base and dried to obtain 8 kinds of light-sensitive silver halide color photographic materials [Sample Nos. (1 )-(8)]. In the accompanying drawings, Fig. 1 shows a graph indicating the characteristic curves for red, green and blue light absorptions of Sample No. 1; Fig. 2 shows a graph indicating the chararteristic curves for red, green and blue light absorptions of Sample No. 2; Fig. 3 shows a graph indicating the characteristic curves for red, green and blue light absorptions of Sample No. 7; Fig. 4 shows a graph indicating the characteristic curves for red, green and blue light absorptions of Sample No. 8; Fig. 5 shows a graph indicating the characteristic curves for red, green and blue light absorptions of Sample No. 12 (the portion indicated by ↔ is the green light absorbed portion which must be masked); Fig. 6 shows a graph indicating the characteristic curves for red, green and blue light absorptions of Sample No. 14 (the portion indicated by ↔ is the green light absorbed portion which must be masked); Fig. 7 shows a graph indicating the characteristic curves for red, green and blue light absorptions of Sample No. 15; The thus prepared respective samples were subjected to wedge exposure according to the conventional method, followed by the following development processings to obtain the results as shown in Table 2. The following processing solutions were used in the processing steps: [Composition of color developing solution] Made up to 1 liter with water, and adjusted to pH 10.0 with potassium hydroxide. [Composition of bleaching solution] Made up to 1 liter with water and adjusted to pH 6.0 with aqueous ammonia [Composition of fixing solution] Made up to 1 liter with water and adjusted to ph 6.5 with acetic acid [Composition of stabilizing solution] Made up to 1 liter with water Development processings were performed under the conditions as mentioned above. In comparison between Samples No. 1, No. 3, No. 5 and No. 7, the coupler (C - II) of No. 3 can give a sensitivity and a maximum density which are both higher than those of the cyan coupler (C - 37), but its maximum absorption wavelength is as short as 667 nm with greater secondary absorption of the color formed dye and therefore not preferred as a cyan coupler for a nega color light-sensitive material. Further, Control samples including Sample No. 3 and No. 4 have the drawback of high fog. In (C - I), (C - II) and (C - 37) used in Samples No. 1, No. 3, No. 5 and No. 7, there is observed the characteristic that all the dyes provided have the long maximum absorption wavelength of 697 nm and the secondary absorption is also small. Among these samples, it will be appreciated that the combination No. 8 has excellent sensitivity, fog and maximum density. Also, for illustration of excellent masking characteristic, Fig 1 shows the characteristic curves of Sample No. 1, and similarly Figs. 2-4 those of Sample No. 2, No. 7 and No. 8, respectively. From Fig. 1 and Fig. 3, it can be seen that in both Samples No. 1 and No. 7, the characteristics curves for green and blue lights are similarly increased through secondary absorption as the increase in density for red light absorption. In Control sample No. 2, due to the difference in reactivity between the cyan coupler and the colored cyan coupler of C - I and CC - 1, no uniform characteristic over the whole region cannot be obtained as shown in Fig. 3. Fig. 4 shows the masking characteristics of Sample No. 8. It can be appreciated that there is obtained a uniform masking characteristic. Example 2 Similarly as described in Example 1, there were prepared mixed dispersions of the cyan couplers and the colored cyan couplers corresponding to Sample No. 6 and No. 8, and they were added to red sensitive silver iodobromide emulsions similarly as in Example 1 to provide coating solutions. Then, these coating solutions were kept under warming at 42°C for one hour, 3 hours, and 8 hours. Subsequently, these coating solutions were admixed with film hardeners similarly as in Example 1 and coated on bases and dried to obtain Samples 9 and 10. As the next step, these samples were subjected to wedge exposure and applied with the processings similarly as described in Examples. The results are given in Table 3. From Table 3, it can clearly be seen that Control sample No. 9 has the drawback in stagnant storability of the coating solution, while Sample No. 10 can be appreciated to be very excellent in stability to a great advantage in manufacturing steps. Example 3 Samples No. 2, No. 4 and No. 8 were processed in entirely the same manner as in Example 1 except that the composition of the bleaching solution was changed as shown below and further the processing time was changed to 4 minutes and 20 seconds. [Composition of bleaching solution] Made up to 1 liter with water and adjusted to pH 5.5 with aqueous ammonia The results obtained are shown in Table 4. As apparently seen from Table 4, it can be appreciated that the Sample No. 8 is very excellent in processing characteristics, weak in oxidizing power and generates no poor color return even in a bleaching processing at a low pH. Example 4 The couplers and the colored couplers including combinations of the couplers and the colored couplers of this invention as indicated in Table 1 were sampled in amounts of 0.02 mol and 0.0015 mol, respectively, and dissolved similarly as in Example 1 to prepare emulsified emulsions, which are then added to silver iodobromide emulsions and coated similarly as described in Example 1 to obtain four kinds of light-sensitive silver halide color photographic materials (Sample Nos. 11 - 14). The respective samples thus obtained were exposed to light and subjected to a series of processings as described in Example 1. As the result, only the Samples No. 13 and No. 14 gave effective masking characteristics, and other samples No. 11 and 12 gave no sufficient masking characteristic. For the purpose of illustration, Fig. 5 shows the spectral absorption at the fog portion of Sample No. 12 by a broken line and the spectral absorption at the color formed portion by a full line. Similarly, Fig. 6 shows the spectral absorptions for the Sample No. 14 within the scope of this illustration. It can be appreciated that the Sample No. 14 within the scope of this invention is effectively masked in the wavelength region of green. Example 5 To the combination of the couplers of the colored couplers corresponding to No. 6 of Example 1 and No. 13 and No. 14 of Example 4, there were added the colored magenta couplers as indicated in Table.6, respectively. The couplers were added each in amount of 0.02 mol, the colored cyan couplers in amount of 0.0016 mol and the colored magenta couplers in amount of 0.0002 mol. By use of the above couplers, colored cyan couplers and the colored magenta couplers, coating samples were prepared similarly as in Example 1 and further processings were carried out similarly as in Example 1. As the result, each sample was found to exhibit excellent masking characteristic. Light absorption characteristics for red, green and blue lights of the Sample No. 15 are shown in Fig. 7. As compared with Fig 4. it can be seen that further ideal masking characteristic is obtained. Example 6 On supports comprising a transparent polyethyleneterephthalate, there were provided respective layers shown below consecutively from the side of the support to prepare multi-layer color nega light-sensitive materials (Sample Nos. 18, 19). First layer: Halation prevention layer An aqueous gelatin solution containing black colloidal silver was coated at 0.3 g of silver/m² to a dried film thickness of 3.0 µm. Second layer: Intermediate layer An aqueous gelatin solution was coated to a dried film thickness of 1.0 µm. Third layer: Low sensitivity red sensitive silver halide emulsion layer. A silver iodobromide emulsion (prepared by mixing a silver iodobromide emulsion with a mean grain size of 0.6 µm containing 4 mol % of silver iodine and a silver iodobromide with a mean grain size of 0.3 µm containing 4 mol % of silver iodide at a ratio of 2 : 1) was chemically sensitized with gold and sulfur sensitizers, and further mixed with, as red sensitizing dyes, anhydrous 9-ethyl-3,3′-di-(3-sulfopropyl)4,5,4′,5′-dibenzothiacarbocanine hydroxide; anhydrous 5,5-di-chloro-9-ethyl-3,3′-di(3-sulfobutyl)thiacarbocyanine hydroxide; and anhydrous 2-[2-{(5-chloro-3-ethyl-2(3H)benzothizolildene)methyl}-1-butenyl-5-chloro-3-(4-sulfobutyl)benzooxazolium, followed by addition of 1.0 g of 4-hydroxy-6-methyl-1,3,3a,7-tetrazaindene and 20.0 ml of 1-phenyl-5-mercaptotetrazole to prepare a low sensitivity red sensitive emulsion. In this emulsion, there were employed 0.15 mol of a cyan coupler, 0.01 mol of colored cyan coupler and further 0.002 mol of a colored magenta coupler in combinations as indicated in Table 7 per mole of silver halide. As a DIR compound, 1.7 g of 2-(1-phenyl-5-tetrazolylhio)-4-octadecylsuccinimide-1-indanone and 0.5 g of dodecyl gallate were added and dissolved under heating in a mixture of 65 g of tricresyl phosphate and 136 ml of ethyl acetate, and the resultant solution added into 550 ml of a 7.5 % aqueous gelatin solution containing 5 g of sodium triisopropylnaphthalene sulfonate, followed by emulsification in a colloid mill. The resultant dispersion was added to the above emulsion to prepare a low sensitivity red sensitive emulsion and coated to a dried film thickness of 40 µm (containing 160 g of gelatin per mole of silver halide). Fourth layer: High sensitivity red sensitive silver halide emulsion layer A silver iodobromide emulsion (mean grain size of 1.2 µm, containing 7 mol % of silver iodide) was chemically sensitized with gold and sulfur sensitizers, and further mixed with, as red sensitive sensitizing dyes, anhydrous 9-ethyl-3,3′-di-(3-sulfopropyl)-4,5,4′,5′-dibenzothiacarbocyanine hydroxide; anhydrous 5,5′-dichloro-9-ethyl-3,3′-di(3-sulfobutyl)thiacarbocyanine hydroxide; and anhydrous 2-[2-{(5-chloro-3-ethyl -2-(3H)-benzothizolildene)methyl}-1-butenyl-5-chloro-3-(4-sulfobutyl)benzooxazolium, followed by addition of 1.0 g of 4-hydroxy-6-methyl-1,3,3a,7-tetrazaindene and 10.0 g of 1-phenyl-5-mercaptotetrazole to prepare a high sensitivity red sensitive emulsion. In this emulsion, there were employed 0.05 mol of a cyan coupler, 0.002 mol of a colored cyan coupler, if added, and 0.0004 mol of a colored magenta coupler, if added, in combinations as indicated in Table 7 per mol of silver halide. Further, 0.05 g of dodecyl gallate were added and dissolved under heating in a mixture of 20 g of dibutyl phthalate and 60 ml of ethyl acetate, and the resultant added into 30 ml of a 7.5 % aqueous gelatin solution containing 1.5 g of sodium triisopropylnaphthalene sulfonate, followed by emulsification in colloid mill. The resultant dispersion was added to the above emulsion to prepare a low sensitivity red sensitive emulsion and coated to a dried film thickness of 2.0 µm (containing 160 g of gelatin per mol of silver halide). Fifth layer: Intermediate layer the same as the second layer Sixth layer: Low sensitivity green sensitive silver halide emulsion layer A silver iodobromide emulsion with a mean grain size of 0.6 µm containing 4 mol % of silver iodide and a silver iodobromide emulsion with a mean grain size of 0.3 µm containing 7 mol % of silver iodide were each chemically sensitized with gold and sulfur sensitizers, and further mixed with, as green sensitive sensitizing dyes, anhydrous 5,5-dichloro-9-ethyl-3,3′-di-(3-sulfobutyl)oxacarbocyanine hydroxide; anhydrous 5,5′-diphenyl)-9-ethyl-3,3-di-(sulfobutyl)oxacarbocyanine hydroxide; and anhydrous 9-ethyl-3 ,3-di-(3-sulfopropyl)-5,6,5′,6′-dibenzooxacarbocyanine hydroxide, followed by addition of 1.0 g of 4-hydroxy-6-methyl-1,3,3a,7-tetrazaindene and 20.0 mg of 1-phenyl-5-mercaptotetrazole. The thus obtained two kinds of silver halide emulsions were mixed at a ratio or 1 : 1 to prepare a low sensitivity green sensitive silver halide emulsion. Further, per mol of silver halide, there were added as a magenta coupler 100 g of 1-(2,4,6-trichlorophenyl)-3-{-3-(4-dodecyloxyphenyl)sulfonamidobenzamido}-pyrazolin-5-one, as a colored magenta coupler 2.5 g of 1-(2,4,6-tri-chlorophenyl)-4-(1-naphthylazo)-3-(2-chloro-5-octa-decenylsuccinimidoanilino)-5-pyrazolone, and further 0.5 g of dodecyl gallate was added and dissolved under heating in a mixture of 120 g of tricresyl phosphate and 240 ml, and the resultant solution added into an aqueous gelatin solution containing sodium triiso-propylnaphthalene sulfonate, followed by emulsification in a colloid mill. The resultant dispersion was mixed with the above emulsion to prepare a low sensitivity green sensitive emulsion, which was coated to a dried film thickness of 4.0 µm (containing 160 g of gelatin per mole of silver halide). Seventh layer: High sensitivity green sensitive silver halide emulsion layer A silver iodobromide emulsion with a mean grain size of 1.2 µm containing 7 mol % of silver iodide was chemically sensitized with gold and sulfur sensitizers, and further mixed with, as green sensitive sensitizing dyes, anhydrous 5,5-dichloro-9-ethyl-3,3′-di-(3-sulfobutyl)oxacarbocyanine hydroxide; anhydrous 5,5′-diphenyl)-9-ethyl-3,3-di-(sulfobutyl)oxacarboxyanine hydroxide; and anhydrous 9-ethyl-3,3-di-(3-sulfopropyl)-5,6,5′,6′-dibenzooxacarbocyanine hydroxide, followed by addition of 1.0 g of 4-hydroxy -6-methyl-1,3,3a,7-tetrazaindene and 10.0 mg of 1-phenyl-5-mercaptotetrazole to prepare a high sensitivity green sensitive silver halide emulsion. Further, there were added as a magenta coupler 80 g of 1-(2,4,6-trichlorophenyl)-3-{-3-(2,4-tert-amylphenoxy-acetamido)benzamido}-pyrazolin-5-one, as a colored magenta coupler 2.5 g of 1-(2,4,6-trichlorophenyl)-4-(1-naphthylazo)-3-(2-chloro-5-octa-decenylsuccinimido-anilino)-5-pyrazolone, and 1.5 g of 2,5-di-t-octyl-hydroquinone, respectively, and dissolved under heating in a mixture of 120 g of tricresyl phosphate and 240 ml, and the resultant solution added into an aqueous gelatin solution containing sodium triisopropylnaphthalene sulfonate, followed by emulsification in a colloid mill. The resultant dispersion was mixed with the above emulsion to prepare a high sensitivity green sensitive emulsion, which was coated to a dried film thickness of 2.0 µm (containing 160 g of gelatin per mole of silver halide). Eighth layer: Intermediate layer the same as the second layer Ninth layer: Yellow filter layer In an aqueous gelatin solution having yellow colloidal silver dispersed therein, there was added a dispersion containing a solution or 3 g of 2,5-di-t-octylhydroquinone and 1.5 g of di-2-ethylhexylphthalate dissolved in 10 ml of ethyl acetate dispersed in an aqueous gelatin solution containing 0.3 g of sodium triisopropylnaphthalane sulfonate, and the resultant mixture was coated at a proportion of 0.9 g of gelatin/ m² and 0.10 g of 2,5-di-t-octylhydroquinone to a dried film thickness of 1.2 µm Tenth layer: Low sensitivity blue sensitive silver halide emulsion layer A silver iodobromide emulsion with a mean grain size of 0.6 µm containing 6 mol % of silver iodide was chemically sensitized with gold and sulfur sensitizers, and further mixed with, as sensitizing dyes, anhydrous 5,5′-dimethoxy-3,3′-di-(3-sulfopropyl)thiacyanine hydroxide, followed by addition of 1.0 g of 4-hydroxy-6-methyl-1,3,3a-7-tetrazaindene and 20.0 mg of 1-phenyl-5-mercaptotetrazole to prepare a low sensitivity blue sensitive silver halide emulsion. Further, per mole of silver halide, there were added as a yellow coupler 120 g of α-pivaloyl-α-(1-benzyl-2-phenyl-3,5-dioxo-1,2,4-triazolidine-4-yl)-2′-chloro-5′-5′-[α-(dodecyloxycarbonyl)ethoxycarbonyl]acetanilide and 50 g of α-{3-[α-(2,4-di-t-amylphenoxy)butylamide)}-benzoyl-2′-methoxyacetanilide and dissolved under heating in a mixture of 120 g of dibutyl phthalate and 300 ml of ethyl acetate, and the resultant solution added into an aqueous gelatin solution containing sodium triisopropylnaphthalene sulfonate, followed by emulsification in a colloid mill. The resultant dispersion was mixed with the above emulsion to prepare a low sensitivity blue sensitive emulsion, which was coated to a dried film thickness of 4.0 µm (containing 160 g of gelatin per mole of silver halide). Eleventh layer: High sensitivity blue sensitive silver halide emulsion layer A silver iodobromide emulsion with a mean grain size of 1.2 µm containing 7 mol % of silver iodide was chemically sensitized with gold and sulfur sensitizers, and further mixed with, as sensitizing dyes, anhydrous 5,5′-dimethoxy-3,3-di-(3-sulfopropyl)thiacyanine hydroxide, followed by addition of 1.0 g of 4-hydroxy-6-methyl-1,3,3a-7-tetrazaindene and 10.0 mg of 1-phenyl-5-mercaptotetrazole to prepare a high sensitivity blue sensitive silver halide emulsion. Further, per mole of silver halide, there were added as a yellow coupler 80 g of α-pivaloyl-α-(1-benzyl-2-phenyl-3,5-dioxo-1,2,4-triazolidine-4-yl)-2′-chloro-5′-5′-[α-(dodecyloxycarbonyl)ethoxycarbonyl]acetanilide and dissolved under heating in a mixture of 80 g of dibutyl phthalate and 240 ml ethyl acetate, and the resultant solution added into an aqueous gelatin solution containing sodium triisopropylnapthalene sulfonate, followed by emulsification in a colloid mill. The resultant dispersion was mixed with the above emulsion to prepare a high sensitivity green sensitive emulsion, which was coated to a dried film thickness of 2.0 µm (containing 240 g of gelatin per mole of silver halide). Twelfth layer: Intermediate layer A dispersion of a mixture of 2 g of di-2-ethyl-hexylphthalate, 2 g of 2-[3-cyano-3-(n-dodecylaminocarbonyl)allylidene]-1-ethylpyrolildine and 2 ml of ethyl acetate dispersed in an aqueous gelatin solution containing 0.6 g of sodium triisopropylnaphthalene sulfonate was coated at a proportion of 1.0 g of gelatin/m² to a dried film thickness of 1.0 µm. Thirteenth layer: Protective layer An aqueous gelatin solution containing 4 g of gelatin and 0.2 g of 1,2-bisvinylsulfonylethane was coated at a proportion or 1.3 g of gelatin/m² to a dried film thickness of 1.2 µm. These high-sensitive multi-layer color nega light-sensitive materials were subjected to wedge exposure and then applied with the processing steps as described in Example 1 and the processing steps as described in Example 3. As the result, it was found that all of the light-sensitive materials were free from poor color return and had high sensitivity with excellent color reproduction and graduation characteristic. It is believed that the words KONIDAX and ALKANOL B are Registered Trade Marks in one or more of the designated states.

Claims: A light-sensitive silver halide color photographic material having on a support at least one light sensitive silver halide emulsion layer containing a cyan coupler and said light-sensitive silver halide emulsion layer and/or a layer contiguous to said light-sensitive silver halide emulsion layer containing a colored cyan coupler characterised in that the cyan coupler is of formula (I): wherein X represents hydrogen or a group or atom eliminable on coupling with an oxidation product of an aromatic primary amine color developing agent; R₁ represents a substituted or unsubstituted naphthyl group or substituted or unsubstituted heterocyclic group provided that a carbon atom thereof is bonded to the adjacent nitrogen atom of the ureido group, or a phenyl group having at least one substituent which is a trifluoromethyl nitro, cyano, -COR, -COOR, -SO₂R, -SO₂OR, (where R represents an aliphatic group or an aromatic group, and R′ represents a hydrogen atom, an aliphatic group or an aromatic group) with the proviso that, when said substituent is cyano or -SO₂R in the p-position relative to the ureido group, the four remaining positions are not all unsubstituted; and R₂ represents an aliphatic group or an aromatic group necessary for imparting diffusion resistance to the said cyan coupler or a cyan dye formed therefrom; and the colored cyan coupler is of formula (II): wherein (Coup-) c represents a cyan coupler residue which is attached at its coupling position to L; L represents a divalent linking group; Q₁ and Q₂ each represent a photographically inactive mono-valent group; M represents a cation or hydrogen; j is 0 or 1; and G represents an acyl group or an alkyl sulfonyl group having 1 to 8 carbon atoms or an arylsulfonyl group having 6 to 8 carbon atoms. A light-sensitive silver halide color photographic material according to Claim 1, wherein the light-sensitive silver halide emulsion layer and/or layer contiguous to said light-sensitive silver halide emulsion layer also contains at least one colored magenta coupler of formula (III): Formula (III): (Coup-) M - N = N-W wherein (Coup-) M represents a magenta coupler residue (with the proviso that the azo group is bonded to the active site of the magenta coupler); and W represents a residue of an unsaturated cyclic compound. A light-sensitive silver halide color photographic material according to Claim 1 or 2, wherein said cyan coupler represented by the formula (I) is a compound of formula (Ia) or (Ib): wherein, Y₁ represents trifluoromethyl, nitro, cyano or a group represented by -COR, -COOR, -SO₂R, -SO₂OR, (wherein R represents an aliphatic group or an aromatic group, and R′ represents a hydrogen atom or a group represented by R); Y₂ represents an aliphatic group, an aromatic group, a halogen atom, an amino group, a hydroxy group or a substituent represented by Y₁; m is an integer of 1 to 3, and n is 0 or an integer of 1 to 3; R₂ and X are as defined in Claim 1, and Z represents a group of non-metallic atoms which together with the carbon atom to which they are attached form a heterocyclic group or naphthyl group, said heterocyclic group being a five-membered or six-membered heterocyclic group containing 1 to 4 hetero atoms which are nitrogen atoms, oxygen atoms or sulfur atoms and which may optionally have substituent(s) thereon. A light-sensitive silver halide color photographic material according to Claim 1, 2 or 3, wherein R is an alkyl group of 1 to 10 carbon atoms or a phenyl group; and Y₂ is a phenyl or naphthyl group. A light-sensitive silver halide color photographic material according to Claim 1, 2 or 3, wherein Y₂ is an alkyl group of 1 to 10 carbon atoms. A light-sensitive silver halide color photographic material according to Claim 3, wherein Z is a furyl, thienyl, pyridyl, quinonyl, oxazolyl, tetrazolyl, benzothiazolyl or tetrahydrofuranyl group. A light-sensitive silver halide color photographic material according to Claim 6, wherein Z has at least one substituent which is an alkyl group of 1 to 10 carbon atoms, aryl group, halogen atom, cyano, nitro, sulfonamide, sulfamoyl, sulfonyl, fluorosulfonyl, carbamoyl, oxycarbonyl, acyl, heterocyclic group, alkoxy, aryloxy or acyloxy group. A light-sensitive silver halide color photographic material according to any of one of Claims 1 to 7, wherein R₂ is an alkyl group of 4 to 30 carbon atoms, an alkenyl group, a cycloalkyl group, a five-membered or six-membered heterocyclic group or a group of formula (Ic): wherein J represents an oxygen or sulfur atom, k represents 0 or an integer of 1 to 4; I represents 0 or 1; R₃ represents a straight or branched alkyl having 1 to 20 carbon atoms; and each R₄ which may be the same or different when k is 2 or more represents a monovalent atom or group. A light-sensitive silver halide color photographic material according to any one of Claims 1 to 8, wherein (Coup-) c in the formula (II) is a phenol or naphthol type cyan coupler residue. A light-sensitive silver halide color photographic material according to any one of Claims 1 to 9, wherein Q₁ and Q₂ are each a hydrogen atom, halogen atom hydroxy, cyanol, alkyl, alkoxy, alkylthio, amide, akloxycarbonyl or alkoxycarbamoyl group. A light-sensitive silver halide color photographic material according to any one of Claims 2 to 10, wherein said colored magenta coupler is a compound of formula (IV): wherein Ac represents a substituted or unsubstituted phenyl, naphthyl or acyl group; R₅ to R₇ each represent the same group as Q₁ in the formula (II); and Ar represents a phenyl, naphthyl or heterocyclic group. A light-sensitive silver halide color photographic material according to any one of Claims 1 to 11, wherein said cyan coupler represented by the formula (I) is incorporated in a silver halide emulsion layer in an amount of from 0.07 to 0.7 mole per mole of a silver halide. A light-sensitive silver halide color photographic material according to any one of Claims 1 to 12, wherein the compound of formula I is incorporated in a silver halide emulsion layer in a mixture comprising the compound of formula I and dibutyl phthalate. A light-sensitive material as claimed in Claim 13 in which the compound of formula I is

Inventors: ITO, KENJI, SHIMBA, SATORU, SUGITA, HIROSHI, TSUDA, YASUO
Applicants: KONICA CORPORATION
Application year: 1983
Main classification: G03C7
IPC codes: G03C7, C09B29