PROCESS FOR THE PRODUCTION OF CARBOXYLIC ACID ESTERS AND/OR CARBOXYLIC ACID

Abstract: Carboxylic acid esters are produced by reacting an unsaturated hydrocarbon, for example an olefin or an alkyne, with carbon monoxide and an alcohol in the presence of a protonic acid and as catalyst (a) at least one of the metals palladium, rhodium, ruthenium, iridium and cobalt, and (b) copper. In a modification of the invention carboxylic acids are produced by omitting the alcohol reactant and replacing it with water in an amount up to 8 mole equivalents based on the unsaturated hydrocarbon and a solvent other than an alcohol, for example tetrahydrofuran.

Description: PROCESS FOR THE PRODUCTION OF CARBOXYLIC ACID ESTERS AND/OR CARBOXYLIC ACIDS The present invention relates in general to a process for the production of carboxylic acid esters and/or carboxylic acids and in particular to a process for the production of carboxylic acid esters and/or carboxylic acids by the catalysed reaction of an unsaturated hydrocarbon, carbon monoxide and either water or an alcohol, optionally in the presence of oxygen. Processes for the production of esters by reacting an oleo in with carbon monoxide and an alcohol in the presence of a catalyst and in the presence or absence of oxygen are known. Representative of the published art are US Patent No 4303589, Belgian Patent No 877770, Japanese Patent Publication No 53040709 and US Patent No 3780074. US Patent No 4303589 (Monsanto) describes a process for the production of carboxylate esters by (a) reacting internal olefines with carbon monoxide and an alcohol at 170 to 2000C and 1200-1800 psig in the presence of a cobalt catalyst and a pyridine promoter, (b) diluting the reaction mixture with a large amount of hydrocarbon to cause phase separation, (c) separating the ester from the other phase, which contains more than 90% of the cobalt catalyst and (d) recycling the catalyst to step (a). Belgian Patent No 877770 describes the production of polycarboxylic esters by reacting an olefin containing at least two conjugated double bonds with carbon monoxide and an alcohol in the presence of a base and a palladium/copper catalyst. Japanese Patent Publication No 5 3040 709 describes the production of dicarboxylic acid diesters by reacting an olefin, carbon monoxide, oxygen and an alcohol in the presence of a catalyst containing (a) a palladium group metal or a compound thereof, (b) a copper salt and (c) a tertiary amine. Finally, USP 3,780,074 describes the production of alkadienoic acid esters by reacting a 4-12 carbon acyclic conjugated aliphatic diolefin with a 1 to 20 carbon monohydroxy alcohol and carbon monoxide in the presence of zero valent palladium and a phosphine activator at 80 to 1600C in the absence of oxygen. Methods are also known for the hydroesterification of acetylene to produce isomeric esters. For example, G.P. Chiusli et al report in Chem. Ind., 977, (1968) the reaction of acetylene with carbon monoxide in the presence of 4Z oxygen and thiourea and a palladium (II) chloride catalyst. A disadvantage of this process is that the selectivity to isomeric esters (cis and trans-diesters) is considerably reduced by the accompanying formation of polymeric materials and isomeric Eouconate esters. We have now found that carboxylic acid esters and/or carboxylic acids can be produced by reacting an unsaturated hydrocarbon with carbon monoxide and either water or an alcohol in the presence of a protonic acid and as catalyst (a) at least one of the metals palladium, rhodium, ruthenium, iridium and cobalt, and (b) copper, both in the presence and the absence of oxygen. In contrast with the majority of prior art processes which utilise a base as an essential reactant, the process of the present invention utilises an acid. The process of the invention in contrast with prior art processes can be operated under relatively mild conditions and exhibits a high regiospecificity to desirable products. Accordingly, the present invention in one aspect provides a process for the production of a carboxylic acid ester which process comprises reacting an unsaturated hydrocarbon with carbon monoxide and an alcohol in the presence of a protonic acid and as catalyst (a) at least one of the metals palladium, rhodium, ruthenium, iridium and cobalt, and (b) copper. The unsaturated hydrocarbon may suitably be an olefin. The olefin may suitably be an acyclic olefin containing from 2 to 30 carbon atoms per molecule or a cyclic olefin containing from 3 to 30 carbon atoms per molecule. The olefin may have either 1, 2 or 3 olefinic carbon-carbon double bonds per molecule, which double bonds may be internal or terminal and may be conjugated or non-conjugated in olefines containing a plurality of carbon-carbon double bonds. Suitable olefines may be represented by the general formula RCH - Cim1 wherein R and R1 are independently either hydrogen, alkyl, alkenyl, alkadienyl, cycloalkyl, aryl, alkaryl, cycloalkenyl or cycloalkadienyl groups, or R and R1 taken together form a cyclic system. Examples of suitable mono-olefins include propylene, 1-butene, 2-butene, l-pentene, 2-pentene, 1-hexene, 2-hexene, 3-hexene, 1-octene, l-decene, cyclododecene, 2-methyl-1-undecene, styrene, 4-methylstyrene, 4-isopropylsytrene, and the like. Examples of suitable diolef ins include 1,3-butadiene, 1,3-pentadiene, 1,5-hexadiene, 4-vinyl cyclohexene, 1,7-octadiene, 1,9-decadiene and the like. Alternatively the diolef in may be allene or an allene homologue, for example dimethyl allene. Examples of suitable triolefins include 1,5,9-cyclododecatriene, cycloheptatriene and the like. Mixtures of olefine may also be employed. Terminal mono-olefins react to give branched chain esters. Internal mono-olefins, for example 2-decene and 4-methyl-2-pentene react exclusively at the 2-position, the c -isomer being more reactive than the trans-isomer. Alternatively, the unsaturated hydrocarbon may be an alkyne. The alkyne may be either a terminal or an internal alkyne. Suitable terminal alkynes include acetylene, l-pentyne, 1-hexyne, l-octyne, benzylacetylene, cyclohexylacetylene and 3-methyl-1-pentyne. Suitable internal alkynes include 2-heptyne, 2-nonyne, 4-methyl-2-pentyne and 2,9-dimethyl-5-decyne. Typically, using acetylene as the unsaturated hydrocarbon the product principally comprises dimethyl maleate together with a minor proportion of dimethyl fumarate. Generally, terminal alkynes give the cis-diester as the principal product and the trans-diester as a by-product. Internal alkynes on the other hand generally give monoesters, not diesters, and furthermore the monoesters tend to be of cis stereochemistry. The carbon monoxide may be provided by any suitable source. The carbon monoxide pressure may suitably be the autogenous pressure at the reaction temperature employed. Alternatively, elevated pressures, suitably in the range from 2 to 250 psig above the autogenous pressure at the reaction temperature may be employed. As regards the alcohol reactant, monohydric and polyhydric alcohols may be employed. Suitable alcohols may be represented by the formula R2CHOH wherein R is independently hydrogen, alkyl, aryl or hydroxyalkyl, or the two groups R together form a ring. Suitably the alcohol is an alkanol. Examples of suitable alcohols include methanol, ethanol, propanols, butanols, pentanols, hexanols, for example 2-ethylhexanol, benzyl alcohol and 1,4-butanediol. The amount of alcohol employed may suitably be at least the stoichiometric amount required to react with the unsaturated hydrocarbon. It is preferred, however, to employ a substantial excess of alcohol over the stoichiometric amount, the alcohol then performing the dual role of reactant and diluent for the reaction. The protonic acid may be either a mineral acid, preferably hydrochloric acid or sulphuric acid, or an organic acid which may suitably be a carboxylic acid. With regard to the catalyst, one or more of the metals palladium, rhodium, ruthenium, iridium and cobalt is employed as component (a). The metals) may be in the form of the elemental metal(s), such as a finely divided powder, or in the form of a compound of the metal(s). Suitable compounds of the metal(s) include the chlorides, iodides, acetates and nitrates, preferably the chlorides. Preferably the metal is palladium, suitably in the form of palladium (11) chloride. Copper, which constitutes component (b) of the catalyst may suitably be added as a cuprous or a cupric compound or as a mixture thereof. A wide variety of copper compounds may be used in the process of the invention. Examples of suitable copper compounds include copper (I) acetate, copper (11) acetylacetonate, copper (I) bromide, copper (I) chloride, copper (11) chloride, copper (I) iodide, copper (11) nitrate, and the like. As regards the ratios of the catalyst components, the molar ratio of copper component (b) to metal(s) component (a) may suitably be in the range from 1:1 to 200:1, preferably from 2:1 to 50:1. The molar ratio of unsaturated hydrocarbon to the metal(s) component (a) may suitably be in the range from 5:1 to 1000:1, preferably from 10:1 to 250:1. Oxygen may be present or absent. However, it is preferred to operate in the presence of oxygen because by doing so the product yields can be improved. Oxygen may be supplied to the reaction either as essentially pure oxygen or admixed with other gases which are substantially inert under the reaction conditions. Air may conveniently be used as the source of oxygen. The oxygen pressure may suitably be the autogenous pressure at the reaction temperature employed. Alternatively elevated pressures may be employed if desired. A supplemental solvent may be employed if desired. The particular solvent employed may form a single phase with the alcohol reactant. Alternatively a solvent which is capable of forming a second liquid phase may be employed. The particular solvent employed should be inert under the reaction conditions. Suitable solvents which form a single phase with the alcohol reactant include oxygenated hydrocarbons, for example tetrahydrofuran. Suitable solvents capable of forming a second liquid phase include aliphatic hydrocarbons, cycloaliphatic hydrocarbons, aromatic hydrocarbons, alkyl-substituted aromatic hydrocarbons or halogenated aliphatic or aromatic hydrocarbons. Examples of suitable solvents capable of forming a second liquid phase include benzene, toluene, hexane, cyclohexane, chlorobenzene, bromobenzene, a xylene, dichloromethane, chloroform and 1,2-dichloroethane. It will be appreciated by those skilled in the art that the organic solvent should be chosen having regard to the difference in boiling points between the products of the reaction and the solvent so as to facilitate separation of the reaction mixture into its individual components. The amount of supplemental solvent based on the olefin reactant may vary over a wide range, suitably from 20 to 0.2, preferably from 5 to 1, volumes of supplemental solvent per volume of olefin reactant. If, in a modification of the invention, the alcohol reactant is replaced by water, provided that the amount of water is less than 8 mole equivalents based on the unsaturated hydrocarbon reactant and a solvent other than an alcohol is employed, then instead of carboxylic acid ester, there is formed the corresponding carboxylic acid. Preferably the amount of water employed is less than 5, even more preferably about 1 mole equivalent based on the unsaturated hydrocarbon reactant. Any suitable solvent other than an alcohol may be employed. Suitable solvents include ethers and hydrocarbons, for example paraffinic and aromatic hydrocarbons. Preferably the solvent is an ether. Examples of suitable ethers include tetrahydrofuran, dioxan, glines and the crown ethers, of which tetrahydrofuran is preferred. The process may suitably be operated at ambient temperature, though elevated temperatures, for example in the range 20 to 1500C or even higher may be employed. The reaction time may vary over a wide range, suitably fros about 30 minutes to 8 hours, though longer reaction times may be employed if desired. The process may be carried out batchwise or continuously, preferably continuously. The invention will now be described in greater detail by reference to the following Examples. PROCESS so OPERATED IN THE PRESENCE OF OXYGEN Example 1 Palladium (11) chloride (O.lg; 0.56 mmol) was added to methanol (50 ml) through which was bubbled carbon monoxide (1 atmosphere). After 1 minute conc. hydrochloric acid (0.5 ml) was added. When the solution turned yellow (indicating that the palladium chloride had dissolved), copper (11) chloride (0.5g; 3.7 mmol) was added and oxygen (1 atmosphere) was bubbled through the solution in addition to the carbon monoxide. l-Decene (6 mmol) was then added and the reaction mixture was stirred for 4 hours at 25"C. After 2 hours a further 0.5 ml conc. hydrochloric acid was added. The reaction product was then extracted with hexane and the hexane evaporated to give a pure product which was identified as methyl 2-methyl decanoate. The ester was obtained in 100X yield based on olefin reactant. Example 2 Example 1 was repeated except that 1-decene was replaced by 1 ,7-octadiene. Example 3 Example 1 was repeated except that 1-decene was replaced by 1,9-decadiene and the reaction time was reduced to 3 hours. Example 4 Example 1 was repeated except that 1-decene was replaced by cyclododecene. Example 5 Example 1 was repeated except that 1-decene was replaced by propene. Example 6 Example 1 was repeated except that l-decene was replaced by 2-methyl-1-undecene and the product was separated by distillation after extraction with hexane. Example 7 Example 6 was repeated except that 2-methyl-1-undecene was replaced by 4-methylstyrene. The results of Examples 2 to 7 together with those of Example 1 are given in Table 1. Example 8 Example 1 was repeated except that the conc. hydrochloric acid was replaced by conc. sulphuric acid (0.33g). Methyl 2-methyl decanoate was obtained in 92% yield. Example 9 The procedure of Example 1 was repeated except that instead of methanol there was used 1,4-butane diol (0.7g) and tetrahydrofuran (30ml) was used as a supplemental solvent. The amounts of other reactants were as follows: palladium (II) chloride = 0.7mmol copper (II) chloride = 6mmol conc. hydrochloric acid - 0.1X1 1-decene - 1.09g The carbon monoxide/oxygen was bubbled through the mixture for 16 hours. After distillation of the crude product, the pure monoester of formula CH3(CH2)7 vCH3 was obtained in 50X yield. COO(CH2)40H Example 10 Palladium (11) chloride (O.lg; 0.56 mmol) was added to methanol (50 ml) through which was bubbled carbon monoxide (1 atmosphere). After 1 minute conc. hydrochloric acid (0.5 ml) was added. When the solution turned yellow (indicating that the palladium chloride had dissolved), copper (11) chloride (0.5g; 3.7 nol) was added and oxygen (1 atmosphere) was bubbled through the solution in addition to the carbon monoxide. Acetylene (6 mmol) was then bubbled through the solution for 4 hours at 250C. After 2 hours a further 0.5 ml conc. hydrochloric acid was added. The reaction product was then extracted with hexane and the hexane evaporated. Analysis of the product gave dimethyl saleate (86Z yield) and dimethyl fumarate (14Z yield). Example 11 The procedure of Example 1 was repeated except that acetylene was replaced by l-pentyne. Cis- and trans- C3H7C(COOCH3)=CHCOOCH3 were obtained in 72 and 25Z yield respectively. Example 12 The procedure of Example 10 was repeated except that acetylene was replaced by 1-hexyne. Cis- and trans- C4HgC(COOCH3)-CHCOOCH3 were obtained in 76 and 24Z yield respectively. Example 13 The procedure of Example 10 was repeated except that acetylene was replaced by l-octyne. Cis- and trans- C6H13C(COOCH3)-CHCOOCH3 were obtained in 80 and 20Z yield respectively. Example 14 The procedure of Example 10 was repeated except that acetylene was replaced by benzyl acetylene. Cis- and trans PhCH2CH2C(COOCH3)=CHCOOCH3 were obtained in 74 and 26X yield respectively Example 15 The procedure of Example 10 was repeated except that acetylene was replaced by cyclohexylacetylene. Cis- and trans C6HllC(COOCH3)=CHCOOCH3 were obtained in 85 and 15% yield respectively. Example 16 The procedure of Example 10 was repeated except that acetylene was replaced by 3-methyl-1-pentyne. Cis- and trans C2HsCH(CH3)C(COOCH3)CHCOOCH3 were obtained in 84 and 16X yield respectively. Example 17 The procedure of Example 10 was repeated except that acetylene was replaced by 2-heptyne. CE13(CH2)3CH=C(CH3)COOCH3 and an ether were obtained in 90 and 10X yield respectively. Example 18 The procedure of Example 10 was repeated except that acetylene was replaced by 2-nonyne. CH3(CH2)sCH=C(CH3)COOCH3 and an ether were obtained in a ratio of 60 and 40Z yield respectively. Example 19 The procedure of Example 10 was repeated except that acetylene was replaced by 4-methyl-2-pentyne. (CH3)2CHCH-C(CH3)COOCE3 and an ether were obtained in 75 and 25X yield respectively. Example 20 The procedure of Example 10 was repeated except that acetylene was replaced by 2,9-dimethyl-5-decyne. Cis-(CH3)2CHCH2CH2CH-C(CH2CH2CH[CH3]2)COOCH3 and an ether were obtained in 70 and 30X yield respectively. Example 21 Example 15 was repeated except that methanol was replaced by ethanol. Cis- and trans- C6H11C(COOC2Hg )CHCOOC2H5 were obtained in 86 and 13X yield respectively. Example 22 Example 17 was repeated except that n-propyl alcohol was used in place of methanol. Cis-CH3(CH2)3CH-C(CH3)COOC3H7 was obtained in 76Z yield. In Examples 10 to 22 the Z yields are based on reactant alkyne. Example 23 Carbon monoxide was bubbled through a solution containing tetrahydrofuran (30 ml) and water (1 ml). Palladium (II) chloride (O.140g, 0.78 mmol) was added, followed by concentrated hydrochloric acid (1.0 ml), copper (II) chloride (0.84g, 6.24 mmol), and then oxygen was bubbled through the mixture. 1-Decene (7.8 wool) was added and the reaction mixture was stirred at room temperature for 4 hours. The product was worked-up by adding distilled water (50 ml) and extracting three times with hexane (in total 250 ml). The extract was dried using magnesium sulphate and then concentrated. Further purification was carried out by dissolving the acid in 1M NaOH, extracting with ether, acidifying, and extracting again with ether. 2-Methyldecanoic acid was obtained in 100% yield. Example 24 The procedure of Example 23 was repeated except that 1-decene was replaced by 1-octene and the reaction time was increased to 18 hours. 2-Methyloctanoic acid was obtained in 92X yield. Example 25 The procedure of Example 23 was repeated except that 1-decene was replaced by vinylcyclohexene. C6HllCH(CH3)COOH was obtained in 53Z yield. Example 26 The procedure of Example 25 was repeated except that the reaction time was increased to 18 hours. C6HllCH(CH3)COOH was obtained in 89X yield. Example 27 The procedure of Example 23 was repeated except that 1-decene was replaced by 1,7-octadiene and the reaction time was increased to 18 hours. HOCOCH(CH3)(CH2)4CH(CH3)COOH was obtained in 93% yield. Example 28 The procedure of Example 23 was repeated except that l-decene was replaced by 1,9-decadiene and the reaction time was increased to 18 hours. HOCOCH(CH3)(CH2)6CH(CH3)COOH was obtained in 100% yield. Example 29 The procedure of Example 23 was repeated except that 1-decene was replaced by cis-2-decene. CH3(CH2)7CH(CH3)COOH was obtained in 59% yield. Example 30 The procedure of Example 23 was repeated except that 1-decene was replaced by trans-2-decene. CH3(CH2)7CH(CH3)COOH was obtained in 302 yield. Example 31 The procedure of Example 30 was repeated except that the time was increased to 18 hours. CH3(CH2)7CH(CH3)COOH was obtained in 77Z yield. Example 32 The procedure of Example 23 was repeated except that cyclododecene was used instead of 1-decene. The yield of cyclododecanecarboxylic acid was 64%. Example 33 The procedure of Example 23 was repeated except that cis-4-methyl-2-pentene was used instead of l-decene. The yield of 2,4-dimethylpentanoic acid was 84Z. Example 34 The procedure of Example 23 was repeated except that trans-4-methyl-2-pentene was used instead of l-decene. The yield of 2,4-dimethylpentanoic acid was 64%. Example 35 The procedure of Example 23 was used except that instead of 1-decene there was used 1,7-octadiene (1.15ml; 7.8mmol). The amounts of the other reactants were as follows: Tetrahydrofuran - 30ml Palladium (II) chloride - 0.130g (0.7mmol) Conc. hydrochloric acid = O.lml Copper (II) chloride = 6mmol. Water = 0.14ml (7.8 mmole) Carbon monoxide/oxygen was bubbled through the mixture for 16 hours. An 80X mixture of the monoacids of formula: CH3CH(COOH)(CHZ )4CHCEI2 andCH3CH(COOH)(CH2)3CH-CH2CH3 were obtained. PROCESS OPERATED IN THE ABSENCE OF OXYGEN Example 36 Palladium (11) chloride (O.lg; 0.56 mmol) was added to methanol (50 ml) through which was bubbled carbon monoxide (1 atmosphere). After im conc. hydrochloric acid (1.0 ml) was added. The solution turned yellow. l-Decene (6 mmol) was added and the reaction mixture was stirred at room temperature. When the reaction mixture turned green, a small amount of copper (11) chloride was added [1:1 ratio overall of palladium (11) chloride to copper (11) chloride]. This operation was repeated as long as the solution turned green. Eventually the solution remained yellow, at which point it was extracted with hexane. The hexane was then evaporated to give methyl 2-methyl decanoate in 100X yield. TABLE 1 EMI13.1 <tb> eXAMPLE <SEP> OLEFIN <SEP> PRODUCT <SEP> YIELD <tb> <SEP> (x) <tb> <SEP> 1 <SEP> 1-decene <SEP> CgH17CH <SEP> COOCH3 <SEP> 100 <tb> <SEP> 3 <tb> <SEP> 2 <SEP> 1, <SEP> 7-octadiene <SEP> CH3OOCCE(CH2)4CHCOOCH3 <SEP> 100 <tb> <SEP> 3 <SEP> 1,9-decadiene <SEP> CH3OOCCH(CH2)6CHCOOCH3 <SEP> 70 <tb> <SEP> h'33 <tb> <SEP> tR3 <SEP> tE3 <tb> <SEP> 4 <SEP> cyclododecene <SEP> methyl <SEP> cyclododecane <SEP> carboxylate <SEP> 85 <tb> <SEP> 5 <SEP> propene <SEP> (CH3)2CHCOOCH3 <SEP> 100* <tb> <SEP> 6 <SEP> 2-methyl-1- <SEP> C9HlgC(CH3 <SEP> )2 <SEP> COOCH3 <SEP> 63 <tb> <SEP> unde <SEP> cene <tb> <SEP> CgB19C(CH3)20CH3 <SEP> 18 <tb> <SEP> Internal <SEP> olefin <SEP> 8 <tb> <SEP> 7 <SEP> 4-methyl- <SEP> 4-CH3C6H4CHCoocH3 <SEP> 90 <tb> <SEP> styrene <tb> <SEP> tH3 <tb> <SEP> 4-CH3C6H4CHoCH3 <SEP> 8 <tb> <SEP> Internal <SEP> olefin <SEP> 2 <tb> * The yield is approximate since the exact weight of propene was not determined. No CH3CH2CH2COOCH3 was isolated. Examples 37 Example 36 was repeated except that 1-decene was replaced by 1-pentene. Example 38 Example 36 was repeated except that 1-decene was replaced by 2-methyl-1-undecene and the product was separated by distillation after extraction with hexane. Example 39 Example 36 was repeated except that 1-decene was replaced by 4-methylstyrene and the product was separated by distillation after extraction with hexane. The results of Examples 36 to 39, together with those for Example 36, are given in Table 2. In Examples 23 to 39 the Z yields are based on reactant olefin. TABLE 2 EMI14.1 <tb> EXAMPLE <SEP> OLEFIN <SEP> YIELD <tb> <SEP> (x) <tb> <SEP> 36 <SEP> 1-decene <SEP> C8H17CHCOOCH3 <SEP> 100 <tb> <SEP> 37 <SEP> l-pentene <SEP> C3H7CHCOOCH3 <SEP> 90 <tb> <SEP> 38 <SEP> 2-methyl-l- <SEP> C9H19C(CH3)2COOCH3 <SEP> 6 <tb> <SEP> undecene <tb> <SEP> CsH19C(CH3)zoCII3 <SEP> 14 <tb> <SEP> 39 <SEP> 4-methylstyrene <SEP> 4-CH3C6HqCBCOOCH3 <SEP> 50 <tb> <SEP> hl <tb> <SEP> 4-CH3C6H4CHOCH3 <SEP> 50 <tb> <SEP> 50 <tb>

Claims: Claims: 1. A process for the production of a carboxylic acid ester which process comprises reacting an unsaturated hydrocarbon with carbon monoxide and an alcohol in the presence of a protonic acid and as catalyst (a) at least one of the metals palladium, rhodium, ruthenium, iridium and cobalt, and (b) copper. 2. A process according to claim 1 wherein the unsaturated hydrocarbon is an olefin. 3. A process according to claim 1 wherein the unsaturated hydrocarbon is an alkyne. 4. A process according to any one of the preceding claims wherein the alcohol has the formula R2CHOH wherein R is independently hydrogen, alkyl, aryl or hydroxyalkyl, or the two groups R together form a ring. 5. A process according to any one of the preceding claims wherein the protonic acid is either hydrochloric acid or sulphuric acid. 6. A process according to any one of the preceding claims wherein component (a) of the catalyst is palladium. 7. A process according to any one of the preceding claims wherein a supplemental solvent is employed. 8. A modification''of the process as claimed in any one of the preceding claims wherein the unsaturated hydrocarbon is reacted with carbon monoxide and water, provided that the amount of water is less than 8 mole equivalents based on the unsaturated hydrocarbon, in the presence of a solvent other than an alcohol and the product produced thereby is a carboxylic acid. 9. A process according to claim 8 wherein the solvent is an ether. 10. A process according to claim 9 wherein the ether is t etrahydrofuran.

Inventors: ALPER, HOWARD, DESPEYROUX, BERTRAND, SMITH, DAVID JOHN HARRY, WOELL, JAMES BERNARD
Applicants: THE BRITISH PETROLEUM COMPANY P.L.C.
Application year: 1983
Main classification: C07C67
IPC codes: B01J23, C07C67, C07C51, C07B61