DUCTILE LOW TEMPERATURE BRAZING ALLOY

Abstract: Titanium-silver alloys containing specified amounts of silver and titanium and controlled amounts of copper, alumi­ num and mixtures thereof are suitable for brazing ceramics, other non-metallic and metallic materials. These alloys also may contain controlled amounts of tin, palladium, indium and mixtures thereof.

Description: DUCTILE LOW TEMPERATURE BRAZING ALLOY FIELD OF INVENTION This invention relates to brazing alloys. More particularly it relates to low temperature brazing alloys containing titanium. BACKGROUND An alloy foil sold under the trademark of Ticusil by the Wesgo Division of GTE Products Corporation, Belmont, California contains 4.5% by weight of titanium, 68.8% by weight of silver and 26.7% by weight of copper. This composite alloy, while having the ability to wet'various ceramic materials and has a relatively low brazing temperature, is not ductile and can not be rolled to a foil in a satisfactory manner and upon brazing contains a brittle dispersed phase. Other titanium containing alloys containing higher amounts titanium are known to wet ceramics. These can be made into a ductile foil form by rapid solidification techniques, however, upon brazing will form a joint¯con- taining a brittle dispersed phase. SUMMARY OF THE INVENTION Reactive metal-silver alloys containing specified amounts of silver and a reactive metal and controlled amounts of copper or aluminum or mixtures thereof also have liquidus temperatures in the range of from about 7500C to about 9500C are ductile and after brazing are relatively free of hard dispersed phases. These alloys also may contain as optional ingredients controlled amounts of tin, palladium, indium and mixtures thereof. DETAILS OF PREFERRED EMBODIMENTS For a better understanding of the present invention, together with other and further objects, advantages and capabilities thereof, reference is made to the following disclosure and appended claims in connection with the above description of some of the aspects of the invention. Within the context of this application the term "reactive metal" means titanium, vanadium, zirconium and mixtures thereof. The amount of the reactive metal in a reactive-silver alloy containing copper or aluminum or mixtures thereof can not appreciably exceed 4% by weight and achieve a ductile material which upon brazing is free of dispersed phases. Table I below shows the effect upon hardness and ductility of various Ti-Ag-Cu alloys. TABLE I Knopp % Titanium % Ag % Cu Hardness (by weight) (by weight) (by weight) 50q Ductility 0 72 28 140 ductile .5 71.6 27.9 140 ductile 1.0 71.3 27.7 145 ductile 3.0 69.8 27.2 140 ductile 4.0 69.1 26.9 130 ductile 4.5 68.8 26.7 201(M) cracks 664(D) 2 phases 5.0 68.4 26.6 190(M) cracks 530(D) 2 phases M = Matrix D = Dispersed Phase As can be seen from the data in Table I about 4% by weight of titanium is the upper weight limit on the amount of titanium that can be present in the Ti-Ag-Cu alloy system and achieve ductility. Similar results upon ductility are achieved when the Ag-Cu ratio changes from the 72% Ag - 28% Cu eutectic. Additionally similar ductility results are achieved in the Ti-Ag-Al system. When vanadium or zirconim or mixtures thereof is the reactive metal the material is not as ductile as when titanium is the reactive metal. The presence of brittle dispersed phases relates to the level of the reactive metal and is independent of the particular reactive metal used. When the reactive metal content is above about 2% by weight when vanadium, zirconium or mixtures thereof are used, rapid solidification manufacture techniques or intermediate annealing is required to produce a ductile foil. Titanium is the preferred reactive metal. In many brazing applications it is desired to utilize relatively low brazing temperatures, that is the liquidus of the alloy should be in the 6000C to 9500C range thus the lower brazing temperatures can be utilized. If desired, in addition to the titanium-silver-copper or aluminum or mixtures of Cu and Al, additional metals of tin, palladium, indium or mixtures thereof can be included as optional ingredients. While the liquidus temperature is in the ranges specified, the flow temperature, that is the temperature at which the alloys of this invention flow and wet the materials to be brazed is important in utilizing the materials using conventional brazing techniques. If the materials to be brazed can withstand about 9000C, it is preferred to utilize brazing temperatures in excess of 9000C even if the particular brazing alloy has a lower liquidus temperature. The flow temperatures for the products of this invention generally range from about 9000C to about 10500C. The amount of reactive metal in the alloys is from about 0.25% by weight to about 4% by weight with from about 1.0% by weight to about 2% by weight being preferred. That amount of silver is from about 20% by weight to about 98.75% by weight. It is preferred that the silver content be between about 60% by weight and about 75% by weight. When copper and aluminum are present in the alloy, the weight percent of these elements can vary from about 1% by weight to about 70% by weight, however, the relative amounts of silver and copper, aluminum or mixture thereof, along with the option- al ingredients of tin, palladium and indium are adjusted to achieve a liquidus temperature within the range of from about 6000C to about 9500C. In the Ti-Ag-Cu system without other metals present it is preferred that the eutectic having a weight ratio of Ag:Cu of about 72:28 be employed. The preferred copper weight range therefore varies from about 20% by weight to about 40% by weight. The preferred aluminum content is from about 4% by weight to about 10% weight. The optional second metal additions include tin, palladium, indium and mixtures thereof. These metal additions can vary from about 1% by weight to about 30% by weight of the alloy When tin is utilized it is preferrably added the weight range of from about 3% by weight to about 15% weight. When palladium is utilized, the preferred amount of palladium is from about 5% by weight to about 25% by weight. When indium is utilized, the preferred amount in from about 2% to about 15% by weight. To more fully illustrate the subject invention the following detailed examples are presented. All parts, percentages and proportions are by weight unless otherwise indicated. Example I Four alloys containing about 1%, 2%, 3% and 4% titanium are prepared using skull melting equipment and a base alloy of the 72% silver-28% copper eutectic. These four alloys are rolled down to a workable, ductile, 5 mil thick foil. A portion of each of the foils is placed between two pieces of 97% alumina ceramic which are 3 /4" wide by 1 1/2" long by 0.025" thick. These four samples are brazed at about 9200C at 10¯5mum Hg for about 5 minutes. Suitable brazed joints are achieved with all four alloys. Example 2 An alloy containing about 2% titanium, about 59% silver, about 29% copper and about 10% tin is prepared and rolled to a foil having a thickness of about 10 mils. The foil is workable and ductile and is used to braze alumina, as in Example 1, except that a brazing temperature of about 9000C is used. A suitable brazed joint is exhibited. Example 3 An alloy containing about 2% titanium, about 67% silver, about 26% copper and about 5% palladium is prepared and rolled to a foil having a thickness of about 4 mils. The foil is cut into a 1/4 inch wide ribbon and a piece of this ribbon is placed between a piece of metallic alloy containing about 53.8% iron, 29% nickel, 17% cobalt and 0.2% manganese known as Kovar and a piece of 97% alumina. The dimension of the Kovar are about 1/2" wide by about 3/4" by .010" thick. The dimensions of the alumina are about 1/2" wide by about 3/4" long by about .030" thick. The Kovar, brazing foil and alumina assembly is heated to about 10200C under about 10'5mum Hg pressure for about 10 minutes. The brazed joint is sound. Example 4 An alloy containing about 3% titanium, about 4.5% aluminum and about 92.5% silver is prepared by convention powder metallurgy techniques. A foil having a thickness of about 4 mils is prepared using an intermediate vacuum anneal. When placed between two pieces of 97% alumina and brazed at about 10500C at 10-5 mm Hg for about 10 minutes, a suitable brazed joint is formed. Example 5 Following the procedure given in Example 4, an alloy containing about 0.5% titanium, about 10% indium, about 24.5% copper and about 65% silver is prepared in the form of a foil. The foil having a thickness of about 6 mils is suitable for brazing copper to alumina using a brazing temperature of about 8500C at 10-5 mm Hg pressure and a time of about 10 minutes. Example 6 Silicon nitride solde under the tradename of SNW-1000 by the Wesgo Division of GTE Products Corporation, Belmont, California is satisfactorily brazed to mild steel at a brazing temperature of about 9200C at 10-5mm Hg. pres- sure using a brazing foil of about 3 mils thickness and having composition of about 2% titanium, about 27.4% copper and about 70.6% silver. Example 7 The following alloys are prepared as in Example 1. 72% Ag - 28% Cu 99.0% 98.0% 97.0% 96.0% Ti 0.5% 1.0% 1.5% 2.0% Zr 0.5% 1.0% 1.5% 2.0% The rolled foil is placed between two alumina substrates and brazed. The use of Ti Zr 1:1 ratio shows reduced flow temperature compared to Ti alloy and flows at 8800C. While there has been shown and described what are at present considered the preferred embodiments of the invention, it will be obvious to those skilled in the art that various changes and modifications may be made therein with out departing from the scope of the invention as defined by the appended claims.

Claims: WHAT IS CLAIMED IS: 1. A brazing alloy consisting essentially of from about 0.25% to about 4% by weight of a reactive metal, selected from the group consisting of titanium, vanadium, zirconium and mixtures thereof, from about 20% by weight to about 98.75% by weight of silver and from about 1% to about 70% by weight of a metal selected from the group consisting of copper, aluminum and mixtures thereof wherein said alloy has a liquidus temperature of from about 6000C to about 9500C. 2. An alloy according to Claim 1 wherein said reactive metal is titanium. 3. An alloy acording to Claim 2 wherein said metal is copper. 4. An alloy according to Claim 3 wherein said metal is aluminum. 5. An alloy according to Claim 4 wherein said aluminum is present in amounts of from about 4% by weight to about 10% by weight. 6. An alloy according to Claim 3 wherein said copper is present in amounts of from about 20% by weight to about 40% by weight. 7. A brazing alloy consisting essentially of from about 0.25% to about 4% by weight of a reactive metal selected from the group consisting of titanium, vanadium, zirconium and mixtures thereof, from about 20% by weight to about 85% by weight of silver, from about 1% to about 70% of a first metal selected from the group consisting of copper, aluminum and mixtures and from about 3% to about 30% by weight of a second metal selected from tin, palladium, indium and mixtures threof wherein said alloy has a liquidus temperature of from about 6000C to about 9500C. 8. An alloy according to Claim 7 wherein said reactive metal is titanium. 9. An alloy according to Claim 7 wherein said first metal is copper and wherein said second metal is tin and is present in amounts of about 3% by weight to about 154. 10. An alloy according to Claim 7 wherein said first metal is copper and said second metal is palladium and is present in amounts of from about 5% to about 25% by weight. 11. An alloy according to Claim 7 wherein said first metal is copper and said second metal is indium and is present in amounts of from about 2% to about 15% by weight.

Inventors: MIZUHARA, HOWARD
Applicants: GTE PRODUCTS CORPORATION
Application year: 1983
Main classification: B23K35
IPC codes: B23K35