ELECTRICALLY CONDUCTIVE PLASTIC ELECTRODE HAVING A POROUS SURFACE

Abstract: An electrically conductive plastics electrode comprises an electrically conductive plastic electrode body, on whose surface is fixed a porous sheet of an electrically conducting material, directly or by means of an adhesive layer. The plastic electrode is especially intended for a bromine side electrode of a bromine-zinc secondary cell and is capable of improving and stably maintaining the efficiency of the electro-chemical reaction of bromine in such a cell.

Description: ELECTRICALLY CONDUCTIVE PLASTIC ELECTRODE HAVING A POROUS SURFACE Electrically Conductive Plastic Electrode having a porous surface This invention relates to an electrically conductive carbon plastic electrode having a porous surface used in a bromine side electrode of bromine-zinc secondary cell stack battery to the surface of which a layer of electrically conductive porous material is formed for improving and maintaining an. energy efficiency of the electrochemical reaction of bromine in the cell. The electrode in an electric cell stack battery is required in order to provide a site of the electro-chemical reaction and stably prosecute the reaction in the cell. The electrode so far used to this purpose for the bromine-zinc secondary cell stack battery may be classified into a metallic electrode made of metallic materia#, carbon electrode made of carbon itself and an electrically conductive plastic electrode made from a plastic material mixed and blended with an electrically conducting material, such as carbon powder for imparting electrical conductivity to the resulting electrode. The metallic material for the metallic electrode is limited to noble metals such as platinum in view of the corrosive action of molecular bromine that is produced in charging the cell. The noble metals are usually rather low in electric resistance and excellent in Coulomb efficiency while also providing an acceptable voltage efficiency during a discharge period and a prolonged useful discharge time. However, the noble metals are expensive and thus are not practically used as electrode material. Carbon electrodes are less costly than the noble metals and hence used widely from dry cell electrodes to electrodes for plant-size electro-chemical reactions. However, these carbon electrodes are generally poor in operational reliability because they are extremely low in mechanical strength and tend to crack under the effect of mechanical impacts. Moreover, carbon electrodes are generally porous and thus are not usable in a series stack of cells bipolar battery system in which the electrode itself is designed to play the role of a partition plate. As to an electrically conductive plastic electrodes of bromine side electrode one must accept the consequence of lower voltage and Coulomb efficiencies in view of higher electric resistance and lower reactivity with bromine active material, although they are fairly sufficient in mechanical strength. One of the present inventors has devised a bromine side electrode material which is higher in energy efficiency and free from the above inconvenience of the prior-art electrically conductive plastic electrode japanese Patent Laid Open No. 56-119463). However, the electrode material proposed in this elder application in use of bromide side electrode is not completely sufficient to overcome the drawback as to long endurance life time operational energy efficiency and costs. In short, there is not known so far in the art an electrode material that shows a proven quality when used in a bromine side electrode of bromine-zinc secondary cell stack battery. As a result of our repeated researches into bromine side electrode material that is durable and inexpensive and provides an improved energy efficiency, the present inventors have found that the voltage efficiency and the Coulomb efficiency of the bromine side electrically conductive plastic electrode may be improved by providing a porous sheet of the electrically conductive material on the electrode surface, and also found that especially good results may be attained by#using a specific pore size and porosity for the electrically conductive sheet material. The present invention is based on this finding. Thus the present invention resides in providing a layer cf porous electrically conductive material to the surface of the electrically conductive plastic electrode with or without the intermediary of the bromine-corrosionresistant adhesive layer, the porous sheet consisting of carbon fibers and having a pore size in the range of 3nm to 700nm and a porosity higher than 2.0%. Figs. 1 through 3 are graphic charts showing the effects of an electrically conductive plastic electrode having a pOrous surface of the present invention. Polyolefin resins are preferred to use as base polymer of the electrode in that the material is not degraded on long contact period with molecular or ionized bromine. Typical of the polyolefin resins are polyethylene resins, polypropyrene resins, chlorinated polyethylene resins and chlorinated polypropyrene resins, these being used singly or in combination as mixture. Any other resin constituents that may be used in the electrically conductive plastic electrode composition may be added to the aforementioned polyolefin resins for realizing desired electrode properties insofar as these additional components do not detract from the properties usually required of the electrode material: An electrically conductive plastic electrode may be usually prepared by heat press forming of a compound contained the electrically conductive materials and a base polymer of polyolefin resins selected from the aforsmentioned resins. When polyethylene resin is used as base polymer by way of an example, 50 weight parts of carbon black are mixed with 100 weight parts of high density polyethylene (with density, higher than 0.94 g/cm3) to an electrode compound which is then formed in a press heated to approximately 180 to 200 0C to form the ultimate electrically conductive plastic electrode. The electrically conductive material provided as a sheet to the electrically conductive electrode surface in accordance with the present invention is a felted, knitted or woven fabric of electrically conductive carbon fibers having numerous small pores. The carbon fibers are usually made from a polyacrylic fiber or pitch fiber. Carbon fibers per se are in the form of fibers, however, in view of formability, they are preferably in the form of a sheet when formed as layer on the electrically conductive electrode surface. The carbon fiber sheet employed in the present invention has a pore size in the range from 3 to 700nm and a porosity higher than approximately 2.0%. The electricaly conductive porous sheet may also be prepared from a carbon fiber paper or porous metallic sheet having the small pores and the porosity defined above. The porosity is defined by the following formula. EMI5.1 As a result of our researches, it has been found that a linear relation exists between this porosity and the mean discharge electric potential. By the way of testing, several sheets of the#electrical- ly conductive material in the form of cloths having different value of porosity were affixed by heat pressing to respective samples of the electrically conductive carbon plastic electrodes. These porous surface electrodes were immersed in an electrolyte containing 0.4 to 1.0 mole of Br2 per liter corresponding to the values occuring before thebefore expiration of discharge and tbe r'r.an electric potential of electrode V20 at the bromine side in the course of the constant discharge current of 20 mA/cm2 was measured by using Ag - AgCl as reference electrode. The results are tabulated as follows. porosity 0.0 3.2 7.2 13.7 P (%) mean electric 0.723 0.739 0.788 0.796 potential F V20 Fig. 1 shows a straight line adapted by the least square method from a curve obtained from the above Table. The relation between the two variables P and V20 is given by an formula V20 = 5.7 x 10-3 P + 0.73 (corelative coefficient r = 0.928) small size particles of titanium hydroxide and metallic titanium were mixed in a suitable ratio, and the resulting mixture was formed under pressure. The resulting green product was sintered in an inert argon atmosphere furnace to three electrically conductive porous metal sheets having different values of porosity (23, 38 and 53 %), these sheets being then affixed under heat pressing to separate test pieces of the electrically conductive carbon plastic electrode. The resulting porous surface test samples were placed in an electrolyte containing 4 moles of Br2 per liter and the valuers of zean electric potential V at the anode bromine side clectrode)was rlcasuredsunder stable discharge current of 20 mA/cmê by using Hg - HgCL - KCL as reference electrode. The results are tabulated as follows. Porosity (%) 23 38 53 mean electric potential 0.515 0.621 0.717 (v) When plotted on a chart, these values are related to one another by a highly linear function. On the other hand, electrically conductive sheets in the form of knitted fabric and cloths were treated for affording a porosity of approximately 14% and the resulting sheets were affixed by heat pressing to the electrically conductive plastic electrode test pieces to the electrically conductive plastic electrode having a porous surface samples A. Similarly, electrically conductive sheets which have not undergone the treatment were affixed by heat pressing to other electrially conductive plastic test pieces to the electrically conductive plastic electrode having a nonporous surface samples B. The electrically conductive plastic electrode samples C were not treated in this manner. The discharge electric potential character istics of the respective samples A, B, C were measured at room temperature with use of an electrolyte of 3 moles of 2 + B 2 2 + r2 per liter and at the current density of 40 mA/cm . The results are shown in Figs. 2 and 3 for knitted fabric and cloths respectively. These test results are indicative of the excellent properties of the inventive electrode A. In a further test, a bromine-zinc secondary cell with 2 current density of 40 mA/Cm , charging state of 80%, and an electrode-to-electrode distance equal to 2mm, was used as a test cell in which a conventional electrically conductive plastic electrode C was used as cathode (zinc side electrode) and the inventive electrode A provided with a porous electrically conductive layer with porosity of 14 %, the electrode B with affixed non-porous electrically conductive sheet and the conventional electrically conductive plastic electrode C were alternately used as anodes (bromine side electrodes), and the energy efficiency was measured for the respective anodes. It was found that the efficiency was 72 % for electrode A, 64 % for electrode B and 56 % for electrode C. From the foregoing it is apparent that the arrangement of the present invention enables the electric resistance of electrode to be reduced and the reaction area to be increased through the use of the electrically conductive porous sheets with variable porosity levels whereby the energy efficiency of the cell may be improved. In addition, electrically conductive plastic electrodes having a porous surface may be manufactured according to different usage requirements and by a process substantially similar to that of the conventional process. The electrode surface may become homogeneous due to pressure heat bonding of the electrically conductive porous sheet on the electrically conductive electrode thus reducing fluctuations in electrode characteristics. An adhesive layer may optionally be provided when providing the electrically conductive porous sheet to the surface of the electrically conductive plastic electrode. The adhesive need have at least some affinity with both the plastic electrode material and the electrically conductive sheet. In general, one may use dispersion of small particles of silver or electrically conductive carbon in a liquid thermoplastic resin such as polyolefin resin. The electrically conductive plastic electrode having a porous surface obtained in the manner described in the foregoing may be used not only in a bromine-zinc secondary cell for improving and maintaining the energy efficiency of the electro-chemical reaction but as an electrode for a a bipolar type cell stack secondary battery.

Claims: ClAlJ < S: 1. An electrically conductive plastic electrode for a bromine-zinc secondary cell comprising an electrode body of electrically conductive plastics material, characterized in that a porous sheet of electrically conducting material having numerous minute pores is fixed to the surface of said electrode body. 2. An electrode according to Claim 1 characterized in that the porous sheet is fixed to the surface of the electrode body by means of a bromine-durable adhesive layer. 3. An electrode according to Claim 1 or 2 characterized in that the porous sheet has a pore size of from 3 to 700 nm and a porosity higher than 2.0%. 4. An electrode according to any of Claims 1 to 3 characterized in that the porous sheet is a fabric of carbon fibers.

Inventors: FUJII, TOSHINOBU, HIROTA, AKIHIKO
Applicants: KABUSHIKI KAISHA MEIDENSHA
Application year: 1983
Main classification: H01M4
IPC codes: H01M4, H01M10, H01M12