VOLATILE CERIUM COMPLEXES AND PRODUCTION THEREOF

Abstract: A complex characterised in that it is a β-diketonate com­ plex of Ce⁴⁺ with 6,6,7,7,8,8,8-heptafluoro-2,2-dimethyl-­ 3,5-octane-dione (hfod), which corresponds to the following formula: Ce(fod)₄ is disclosed. A complex characterised in that it is a β-diketonate com­ plex of Ce³⁺ and M with 6,6,7,7,8,8,8-heptafluoro-2,2-di­ methyl-3,5-octane-dione (hfod) which corresponds to the following formula M[Ce(fod)₄] wherein M represents Na, Li, K, Cs and Rb is also disclosed. The volatile and thermally stable complex of cerium, Ce(fod)₄, and the alkali metal-cerium β-diketonate interme­ diates useful in its preparation are sources of mixed metals, such as Na[Ce(fod)₄]. The present invention provides advantages over the prior art.

Description: Volatile Cerium Complexes and Production Thereof" This invention relates to volatile cerium complexes and to the production thereof; more particularly it relates to organometallic compounds specifically to ss-diketonate complexes of cerium, which exhibits unusually high volatility and stability. Volatile metal complexes are of interest for a variety of applications, including use as fuel additives, metal vapour sources for vapour phase reactions and gas transport reagents. A useful discussion of ss-diketonate complexes and the usesthereof is provided by R.E. Sievers, et al., Science, 201, [4352], pages 217-223, (July 1978), wherein numerous references to the preparation and use of these complexes are cited. ss-diketonates of the rare earth or lanthanide series of elements of the Periodic Table correspond to the general formula: Ln(AA')3 wherein Ln represents the metal element and AA' represents the diketonate ligand which forms the complex. Discussions of the synthesis and properties of the rare earth ss-diketonate complexes usually do not treat the cerium complexes. This is due to the complexity arising because cerium has two stable oxidation states. The trivalent paramagnetic complexes of Ce with -diketones, such as acetylacetone [Ce(acac)3j, trifluoroacetylacetone [Ce ( tfa) 3] and hexafluoroacetylacetone [Ce(fa)3] are frequently mentioned, but only a few tetravalent (Ce IV) compounds have been reported. These include Ce(acac)4, Ce(tfa)4 and complexes of cerium with 2,2,6,6-tetramethyl-3,5-heptane-dione (thd) and the aromatic diketone (C6H5CO)2CH, the first two being made by the oxidative decomposition of trivalent complexes incorporating the same ligands in an inert solvent in flowing air or oxygen. In the case of Ce(tfa)4, yields are poor even in the presence of excess quantities of the free -diketone (Htfa). Cerium complexes have also been formed with some of the 8-carbon ss-diketones, indluding 6,6,7,7,8,8,8heptafluoro-2,2-dimethyl-3,5-octane-dione [Ce(fod)3] and 2,2,7-trimethyl-3,5-octane-dione [Ce(tod)4]. However, none of these cerium complexes have exhibited sufficient stability and volatility to be truly useful as a cerium metal vapour source for vapour phase reactions. designed to produce cerium-containing products. It is therefore an object of the present invention to provide a cerium complex and a precursor useful in the production of that complex, which result in a stable compound exhibiting sufficient volatility for use as a vapour source of cerium. The present invention relates to a Ce ss-diketonate complex of improved stability and volatility, as well as a group of volatile Ce3+ ss-diketonate complexes useful as intermediates in the production of the pure CE 4+ complex and as volatile sources for mixtures of cerium and alkali metals. The complexes according to the present invention are complexes of cerium with the fluorinated -diketone 6,6,7,7,8,8,8-heptafluoro-2,2-dimethyl-3,5-octane-dione (Hfod), a -diketone corresponding to the following formula: EMI2.1 Cerium 5-diketonate complexes of this -diketone are produced by the deprotonation of the diketone at the C4 position to produce (fod) anions or ligands. Four of these ligands then combine with a cerium ion to form a complex wherein the metal is in 8-fold coordination with the oxygen atoms in the ligands. The formula of the Ce complex with this -diketone is Ce(fod)4. The formula of th-e Ce 3+ complexes, which may be characterised as alkali metal ss-diketonate salts, is M[Ce(fod)4] wherein M represents an alkali metal selected from Li, Na, K, Rb and Cs. These salts may be used to produce pure Ce(fod)4 by-a process of oxidation or they may be used as sources for Ce-M mixtures in vapour deposition reactions to form metal or oxide products. Ce(fod)4 offers significant advantages over prior art ss-diketonate complexes of cerium with respect to both thermal stability and volatility. It has a vapour pressure at least two orders of magnitude higher than that of the 3-complex with the same ligand, Ce(fod)3. Also, it is stable against decomposition at temperatures sufficiently high to permit vapours of the compound to be efficiently generated at substantial partial pressures. Thus, the compound is believed to be superior to previous cerium compounds when used, for example, as a vapour source of cerium in a chemical vapour deposition reaction. The present invention may be further understood by reference to the accompanying drawings wherein: Fig. 1 illustrates a proton nuclear magnetic resonance spectrum for the ss-diketonate complex Ce(fod)4; Fig. 2 illustrates a thermogravimetric analysis curve demonstrating the volatility of Cd(fod)4; and Fig. 3 illustrates a comparision between the vapour pressures of Ce(fod)4 and Na[Ce(fod)4] with selected known ss-diketonate complexes. The preparation of pure cerium (ford) complexes in accordance with the present invention involves the deprotonation of the -diketone in the presence of cerium (III) nitrate. The following Example describes a suitable method for preparing such a complex. Example 1 A 68.2 g sample of the -diketone 6,6,7,7,8,8,8heptafluoro-2,2-dimethyl-3,5-octane-dione (hfod) is added to 115 ml of 2M aqueous NH4OH resulting in a white precipitate which is separated and dissolved in a mixture of 200 ml of water and 200 ml of methanol The resulting solution is placed in an addition funnel and is added dropwise to a nitric acid solution of cerium nitrate, the latter solution being made by adding 25.0 g CetN0)3.6H20 6H20 to 60 ml of 1.4 M HN03. After addition of the water-methanol solution, 2M NH4OH is added to the reaction mixture to achieve and maintain a pH of 6. The resulting mixture separates into a red oil phase and an aqueous phase. The phases are stirred under oxygen at room temperature to obtain complete oxidation of Ce3+ to Ce This may be accomplished within about 24 hours. Thereafter, hexanes (200 mlY are added and the hexane layer containing the product is separated from the aqueous phase, filtered and evaporated to dryness in a rotary evaporator. The red solid is redissolved in 300 ml of hexanes and 600 ml of ethanol is added. Crystals of red Ce(fod)4 form after cooling of the solution. Proton nuclear magnetic resonance and magnetic susceptibility measurement of the product indicates that the yield is substantially entirely Ce(fod)4, with no evidence of Ce(fod)-4. Fig. 1 of the accompanying drawings illustrates a proton nuclear magnetic resonance spectrum of this product in a CC14 solvent against a tetramethylsilane standard at 60 MHz, from which the absence of trivalent cerium compounds of (fod) may be inferred. In an alternative preparation procedure, Ce(fod)4 is produced by the oxidation of the intermediate Na[Ce(fod)4]. This intermediate results when the deprotonation of the 5-diketone is carried out using NaOH. An illustrative procedure is set out in the following Example. Example 2 A methanolic solution of cerium nitrate is prepared by adding 110 g of Ce(N03)3. 6H20 to 250 ml of methanol. A methanolic solution of Hfod is then prepared by adding 300 g of the ss-diketone to 250 mltof methanol in an addition funnel. This latter solution is then added to the cerium nitrate solution with continuous stirring. After this addition has been completed, 4M NaOH is added to the mixture dropwise with pH monitoring until a pH of from 7 td 8 is attained. 600 ml of water and 500 ml of hexanes are then added to the reaction mixture and a separation of layers occurs with concentration of the ss-diketonate product in the hexane layer. The hexane layer is separated and rotary-evaporated to dryness. The product is a crystalline mixture of Na[Ce(fod)4] and Ce(fod)4, with the proportion of the latter compound depending upon the extent of oxidation which has been permitted to occur after adding NaOH. Separation of the Ce(fod)4 from the Na[Ce(fod)4] may be effected by dissolving the product in hexane and separating the Na[Ce(fod)4] from the solution by adding ethanol, in which the solubility of the sodium complex is relatively high. Oxidation of Na[Ce(fod)4] to Ce(fod)4 To convert the sodium complex to Ce(fod)4, a 255 g sample of Na[Ce(fod)4} is dissolved in 500 ml of hexanes and 500 ml of distilled water. This mature is then refluxed at low temperature for about 60 hours, while bubbling pure 02 gas through the liquid. At the conclusion of this oxidation treatment, the solution is deep red in colour, with a tan solid present on the sides of the reaction container. The solution is separated, filtered and rotary-evaporated to dryness, the product consisting predominantly d5Ce(fod)4 with some residual Na[Ce(fod)4] which is separated from the pure cerium product by partitioning in an ethanol/hexane mixture. The tan solid recovered from the oxidation step is identified by x-ray diffraction as CeO2. The ss-diketonate products produced in accordance with Example 2 above are examined by differential scanning calorimetry to determine melting points. The results are given in Table 1 below. Table l DSC Endothermic Peaks Compound Major Minor Ce(fod)4 970C 840C, 1560C Na[Ce(fod)4] 1200C 650C The infrared spectra of the two complexes are similar over the region from 4,000 to 400 cm , but exhibit important differences in the C=O region, due to the difference in the oxidation state of cerium. The C = O (C = C) stretch frequencies are expected to shift to lower regions as the oxidation state of the metal increases. For Na[Ce(fod)4], these stretching frequencies are evidenced by a strong peak at 1630 cm'l with a weak shoulder at 1645 -1 For Ce(fod)4, strong peaks are observed at 1595 cm and 1610 cm The preparation of other M[Ce(fod)4] alkali metal salts would follow that described in Example 2 above, but replacing NaOH with a base, such as LiOH or KOH, in the deprotonation step. In this way salts, such as Li[Ce(fod)4] and K[Ce(fod)4], may be prepared which could be converted to Ce(fod)4 or used directly as sources of metal mixtures. The very low melting point of Ce(fod)4, e.g. about 970C, is a particular advantage where the compound is to be used to supply cerium-containing vapours for a vapour phase reaction. Both Ce(tod)4 and Ce(tfa)3 exhibit significantiy higher melting points, e.g. 1340C and 1760C, respectively. The high volatility and stability of the Ce(fod)4 complex when compared with other trivalent and tetravalent cerium -diketonates, are particularly important. Fig. 2 of the accompanying drawings illustrates a thermogravimetric analysis curve for Ce(fod)4 which suggests rapid and complete volatilization of the compound with no evidence of decomposition at temperatures below 2750C. The temperature of 50% volatilization of the sample (T1/2), a useful relative measure of volatility, is about 2500C and no unusual weight fluctuations evidencing thermal decomposition during the course of vaporization are evident. This volatilization behaviour is substantially better than that exhibited by any of Ce(tod)4, Ce(hfa)3 or Ce(tfa)3. Ce(tod)4 exhibits no evidence of decomposition, but has a T1/2 temperature of about 3200C, while both Ce(tfa)3 and Ce(hfa)3 exhibit evidence of significant thermal decomposition at these volatilization temperatures during TGA analysis. The high vapour pressure of the tetravalent cerium (fod) complex also favours its use as a source of cerium vapours for vapour phase reactions. Fig. 3 of the accompanying drawings plots vapour pressure as a function of temperature for the cerium 2-diketonate complexes Ce(fod)4, Na[Ce(fod)4], Ce(fod)3, Ce(tfa)3, and Ce(tod)4. The data for the complex Ce(fod)3 was taken from the literature. It is evident from a study of accompanying Fig. 3 that the complex Ce(fod)4 exhibits significantly higher vapour pressure than any of the Ce(tod)4, Ce(tfa)3, and Ce(fod)3 complexes, particularly at temperatures above 1000C where these complexes would be used as vapour sources for cerium metal. Accompanying Fig. 3 also demonstrates the very significant vapour pressure of the Na[Ce(fod)4] complex. Although analogous alkali metal salts of other rare earth metal diketonates have shown some volatility, the very high volatility of this complex is surprising, suggesting that it could be used as a source of Ce/Nacontaining vapours for vapour deposition applications where such a combination is required. It is expected that the other alkali metal salts of this complex would also have this utility. A particularly preferred method for making Ce(fod)4 is based on the fact that this complex may be formed immediately and quantitatively by reacting the deprotonated diketonetfod with a soluble cerium (IV) compound, such as cerium (IV) salt. Convenient sources of dissolved cerium (IV) salts are soluble inorganic cerate complexes. For example, cerium (IV) nitrate may be obtained from the (NH4)2Ce(N03)6 complex ammonium hexanitrato cerate. The reaction of the dissolved salt with the deprotonated diketone immediately produces the desired Ce(fod)4 complex and the product is essentially free of cerium (III) complexes, such as Ce(fod)4 Particular cerium (IV) salts which may be used to produce the Ce(fod)4 complex in accordance with the present invention include the nitrate, sulphate and 4+ perchlorate salts of Ce . These are not handled directly, but are instead produced by dissolving complex cerate salts or acids in aqueous acidic solutions, e.g. solutions of HNO3 or other mineral acid. Among the cerate complexes which could be used as cerium (IV) sources are (NH4)2Ce(N03)6, (NH4)4Ce(S04)4. 2H20, H4Ce(S04)4 and H2Ce(ClO4)6. However, cerium (IV) nitrate solutions produced from the (NH4)2Ce(N03)6 starting material are presently preferred because they are anhydrous salts and are available in substantially higher purity (being essentially free of iron or other rare earth elements) than the other cerium (IV) starting materials. As illustrated by the following Example, this method avoids the oxidation step necessary to convert the cerium (III) complex and thus provides a more rapid and convenient synthesis. Example 3 A 15.4 gram sample of ceric ammonium nitrate (ammonium hexanitrato cerate), (NH4)2Ce(N03)6 is dissolved in 25 ml of 1.4 M nitric acid with vigorous stirring to form a ceric nitrate solution. A primary standard certified grade of the cerate, commercially available from the G.F. Smith Chemical Co., Colombus, Ohio, U.S.A. is used. In a separate flask, 34.2 grams of 6,6,7,7,8,8,8 heptafluors2,2-dimethyl-3,5-octane-dione (Hfod) is mixed with 75 ml of 2M NH4OH to give a white precipitate of NH4fod. This white precipitate is dissolved in about 200 ml of methanol to form a ligand solution. The thus-prepared ligand solution is slowly added to the ceric nitrate solution with stirring and a red complex of the desired Ce(fod)4 product is immediately formed. After stirring for 2 hours at room temperature the product is separated from the reaction mixture by filtration and dried in a vacuum. The yield is quanti tative. Additional purification by recrystallization from hexane-ethanol or sublimation is possible, if desired. The identity of the product is confirmed by 1H nuclear magnetic resonance spectroscopy to be the desired Ce(fod)4.

Claims: Claims: 1. A complex characterised in that it is a ss-diketonate complex of Ce4+ with 6,6,7,7,8,8,8- heptafluoro-2,2-dimethyl-3,5-octane-dione (hfod), which corresponds to the following formula: Ce(fod)4. 2. A complex characterised in that it is a (3-diketonate complex of Ce3+ and M+ with 6,6,7,7,8,8,8 heptafluoro-2,2-dimethyl-3,5-octane-dione (hod) which corresponds to the following formula: M[Ce(fod)4] wherein M represents Na, Li, K, Cs and Rb. 3. A complex as claimed in claim 2 wherein M represents Na. 4. A process for the preparation of tetrakis (6,6,7 ,7,8 , 8, 8-heptafluoro-2, 2-dimethyl-3,5-octane- dione) cerium (IV), [Ce(fod)4], as claimed in claim 1 characterised in that it comprises reacting deprotonated 6,6,7,7,8,8,8-heptafluoro-2,2-dimethyl-3,5- octane-dione with a soluble cerium (IV) salt. 5. A process as claimed in claim 4 wherein the cerium (IV) salt cerium (IV) nitrate. 6. A process as claimed in claim 5 wherein the cerium (IV) nitrate is produced by dissolving (NH4)2Ce(N03)6 in an acidic medium.

Inventors: THOMPSON, DAVID ALLEN
Applicants: CORNING GLASS WORKS
Application year: 1983
Main classification: C07C49
IPC codes: C07C45, C07C49