ARYLENE SULFIDE TERPOLYMERS AND PROCESSES FOR MAKING THEM

Abstract: A process for the production of an arylene sulfide terpolymer is provided comprising reacting at least one alkali metal sulfide, at least one p-dihalo unsubstituted benzene, at least one polyhalo aromatic compound having more than two halogen substituents per molecule, at least one p-dihalo, alkyl substituted benzene, and at least one N-alkyl lactam. Another process is provided comprising first reacting an at least one alkali metal sulfide in hydrated form or in an aqueous mixture with at least one N-alkyl lactam to form a reaction product, thereafter heating the reaction product to form a dehydrated composition, then reacting the dehy­ drated composition with a mixture consisting essentially of at least one p-dihalo unsubstituted benzene, at least one polyhalo aromatic compound having more than 2 halogen atoms per molecule, at least one p-dihalo alkyl substituted benzene, and at least one member selected from the group consisting of (a) water in an amount of about 0.2 mole to about 2.5 moles per molecule of alkali metal sulfide under polymerization conditions for a time sufficient to produce the desired terpolymer. Arylene sulfide terpolymers are pro­ vided as products of the above processes.

Description: ARYIENE SULFIDE TERPOLYMERS AND PROCESSES FOR MAKING THEM This invention relates to arylene sulfide terpolymers and processes for making them. The production of arylene sulfide polymers is well known in the art as disclosed in U.S. Patent 3,354,129 to Edmonds et al. In addition, arylene sulfide copolymers are also known, as disclosed in U.S. Patent 4,038,261. I have now discovered that arylene sulfide terpolymers can be made as well. These terpolymers have applications in the formation of articles of manufacture such as films, sheets, fibers, coatings, and molded articles. Substantially amorphous, essentially non-crystalline arylene sulfide terpolymers are particularly desirable as they are melt stable and can be processed at lower temperatures than crystalline poly(arylene sulfide). Such terpolymers can be prepared directly to the range of melt flow desired for injection molding or can be air cured to attain the desired melt flow. Unexpectedly, I have discovered arylene sulfide terpolymers that are especially non-crystalline (amorphous) and heat stable as they lack both a melting point, Tm, and a crystallization temperature, Tc, value as determined by the conventional method of Differential Thermal Analysis (DTA). Hence, the terpolymers of this invention are particularly useful in applications such as molding injections. These terpolymers can be filled with glass fibers, pigments, clay, talc, and other substances used in molding injections. It is an object of this invention to pr.ekvidv. novAl, aryleno sulfide terpolymers. It is a further object of this invention to provide processes for making these terpolymers. Other objects, aspects, and the several advantages of the present invention will become apparent from this specification and the claims. In one embodiment of the present invention, I have discovered a process for making novel arylene sulfide terpolymers by reacting at least one alkali metal sulfide, at least one p-dihalo unsubstituted benzene, at least one polyhalo aromatic compound having more than two halogen substituents per molecule, at least one p-dibalo, alkyl substituted benzene, and at least one N-alkyl lactam, under polymerization conditions of temperature and time sufficient to produce the desired terpolymer. In a second embodiment of the present invention, I have discovered still another process for making novel arylene sulfide terpolymers by first reacting at least one alkali metal sulfide in hydrated form or in an aqueous mixture with at least one N-alkyl lactam to form a reaction product, thereafter heating the reaction product to form a dehydrated composition, then reacting the dehydrated composition with a mixture consisting essentially of at least one p-dihalo unsubstituted benzene, at least one polyhalo aromatic compound having more than two halogen substituents per molecule, at least one p-halo alkyl substituted benzene, and at least one member selected from the group consisting of (a) water in an amount of about 0.2 mole to about 2.5 moles per molecule of alkali metal sulfide, and (b) at least one alkali metal carboxylate and water, including water of hydration, in an amount of 0.0 mole to aobut 2.5 moles per mole of alkali metal sulfide under polymerization conditions for a time sufficient to produce a desired terpolymer In a third embodiment of the present invention, novel arylene sulfide terpolymers produced by the processes of the first and second embodiments of the present invention are provided. P-dihalo unsubstituted benzenes which can be employed in the process of this invention can be represented by the formula EMI2.1 where each X is selected from the group consisting of chlorine, bromine, and iodine. Examples of some p-dihalo unsubstituted benenes which can be employed in the process of this invention include p-dichlorobenzene, p-dibromobenzene, p-diiodobenzene, 1-chloro-4-bromobenzene, 1-chloro4-iodobenzene, 1-bromo-4-iodobenzene, and mixtures thereof Polyhalo aromatic compounds having ¯are than two halogen substituents per molecule which can he employed in the process of this invention can be represented by the formula RÚXn, where each X is selected from the group consisting of chlorine; bromine, and iodine, n is an integer of 3 to 6, and R is a polyvalent aromatic radical of valence n which can have up to about 4 methyl substituents, the total number of carbon atoms in R1 being within the range of 6 to about 16. Examples of some polyhalo aromatic compounds having more than two halogen substituents per molecule which can be employed in the process of this invention include 1,2,3-trichlorobenzene, 1,2,4trichlorobenzene, 1,2,3,5-tetrabromobenzene, hexachlorobenzene, 1,3,5 trichloro-2,4,6-trimethylbenzene; 2,2',4,4'-tetrachlorobiphenyl, 2,2',5,5'-tetraiodobiphenyl, 2,2',6,6'-tetrabromo-3,3',5,5'-tetramethylbiphenyl, 1,2,3,4-tetrachloronaphthalene, 1,2,4-tribromo-6-methylnaphthalene, and mixtures thereof. P-halo alkyl substituted benzenes which can be employed in the process of this invention can be represented by the formula: EMI3.1 where R is a C1 to C12 alkyl group, m is 1, 2, 3, or 4, X is either C1, Br, or I. Examples of p-halo alkyl substituted benzenes which can be employed in the process of this invention include 2,5-dichlorotoluene, 2,4-dichlorotoluene, 2,6-dichlorotoluene, 2,5 dichloro-p-xylene, 2,5dibromotoluene, 2,5-diiodo-p-xylene, 2,5-dichloro-1,3,6-trimethylbenzene, and mixtures thereof. Alkali metal sulfides which can be employed in the process of this invention are sodium sulfide, potassium sulfide, rubidium sulfide cesium sulfide, as well as mixtures thereof. The alkali metal sulfide can be used in the anhydrous form, as a hydrate, or as an aqueous mixture. If desired, the alkali metal sulfide can be produced by reaction of hydrogen sulfide or sodium bisulfide with sodium hydroxide in an aqueous medium. N-Alkyl lactams which can be employed in the process of this invention can be represented by the formula EMI4.1 where each R1 is selected from the group consisting of hydrogen and R, R is an alkyl radical having 1 to about 3 carbon atoms, x is an integer of 1 to 3, and the total number of carbon atoms in the N-alkyl lactam is within the range of about 5 to about 10. Examples of some N-alkyl lactams which can be employed in the process of this invention include N-methyl-2-pyrrolidone, N-ethyl-2pyrrolidone, N-isopropyl-2-pyrrolidone, N,3-dimethyl 2-pyrrolidone, N-Propyl-5-methyl-2-pyrrolidone, N,3,4,5-tetramethyl-2-pyrrolidone, N-isopropyl-4-propyl-2-pyrrolidone, N-methyl-2-piperiodone, N,6-diethyl2-piperidone, N-methyl-5-isopropyl-2-piperidone, N-methyl-3-ethyl-2piperidone, N-methyl-2-oxohexamethylenimine, N-ethyl-2-oxohexamethylenimine, N-methyl-2-oxo-5-ethylhexamethylenimine, N-propyl-2-oxo5-methylhexamethylenimine, N-methyl-2-oxo-3-propylhexamethylenimine, N-methyl-2-oxo-7-isopropylhexamethylenimine, and the like, and mixtures thereof. Alkali metal carboxylates which can be employed in the process of this invention can be represented by the formula R4CO2M, where R4 is a hydrocarbyl radical selected from alkyl, cycloalkyl, and aryl, and combinations thereof such as alkaryl, aralkyl, and the like, and the number of carbon atoms in R4is within the range of 1 to about 20 and M is Li, Na, K, Rb, Cs. If desired, the alkali metal carboxylate can be employed as a hydrate or as a solution or dispersion in water. However, if the total amount of free water and/or water of hydration present, including that associated with the alkali metal sulfide, exceeds the amount specified hereinabove, excess water must be removed, e.g., by distillation, prior to the polymerization step. Examples of some alkali metal carboxylates which can be employed in the process of this invention include sodium acetate, sodium propionate, sodium 2-methylpropionate, sodium benzoate, sodium butyrate, sodium valerate, sodium hexanoate, sodium heptanoate, sodium 2-methyloctanoate, sodium dodecanoate, lithium acetate, lithium propionate, lithium hexanoate, rubidium acetate, rubidium butyrate, rubidium heptanoate, cesium acetate, cesium propionate, cesium octanoate and mixtures thereof. The preferred alkali metal carboxylate is sodium acetate. Although the mole ratio of the combination of p-dihalo unsubstituted and substituted benzene to alkali metal sulfide can vary somewhat, generally, it will be within the range of about 0.98:1 to about 1.03:1, preferably within the range of about 0.99:1 to about 1.02:1. The mole ratio of polyhalo aromatic compound having more than two halogen substituents per molecule to alkali metal sulfide can vary considerably, depending in part on the halogen content of said polyhalo aromatic compound and on the water and sodium carboxylate content of the polymerization system, but generally will be within the range of about 0.0002:1 to about 0.014:1, preferably, within the range of about 0.001:1 to about 0.g12:1. The mole ratio of alkali metal carboxylate, when used, to alkali metal sulfide can vary over a wide range, but generally will be within the range of about 0.05: :1 to about 1.5:1, preferably within the range of about 0.1:1 to about 0.8:1. The mole ratio of N-alkyl lactam to alkali metal sulfide can vary considerably, but generally will be within the range of about 2:1 to about 10:1, preferably within the range of about 3:1 to about 6:1. Although the reaction temperature at which the polymerization is conducted can vary over a wide range, generally it will be within the range of about 1800C to about 2850C, preferably within the range of about 1900C to about 2750C. The reaction time can vary greatly, depending in part on the reaction temperature, but generally will be within the range of about 1 hour to about 60 hours, preferably within the range of about 2 hours to about 10 hours. In a presently preferred procedure, the polymerization is conducted within a first temperature in the range of about 1800C to about 2450C, preferably at about 1900C to about 2450C, and then within a second temperature range of about 2450C to about 2850C, preferably about 2450C to about 2750C, the total reaction time for the polymerization in these two temperature ranges being within the range of about 1 hour to about 60 hours, preferably about 2 hours to about 10 hours, about 15 percent to about 70 percent of which time is within the first temperature range, the temperature during at least 50 percent of the reaction time in the first temperature range being at least 200C below the final temperature in the second temperature range. Here, too, the reaction times are dependent, in part, on the reaction temperatures. In either or both of the temperature ranges, the temperature can be increased continuously or maintained predominantly at selected levels within relatively restricted temperature limits. The pressure at which the polymerization reaction is conducted should be sufficient to maintain the p-dihalo unsubstituted benzene, the p-dihalo-alkyl substituted benzene, the polyhalo aromatic compound having more than two halogen substituents per molecule, the N-alkyl lactam, and the water substantially in the liquid phase. The process of this invention can be carried out by mixing the p-dihalo unsubstituted benzene, the p-dihalo-alkyl substituted benzene, the polyhalo aromatic compound having more than two halogen substituents per molecule, the alkali metal sulfide, the N-alkyl lactam, the water, including water of hydration, if used, and the alkali metal carboxylate, if used, in any order. If more than the desired amount of water, in the form of free water and/or water of hydration is present in the mixture or any component of the mixture, any water in excess of the desired amount can be removed, e.g., by distillation. Such excess water can be removed from the component with which water is initially associated, e.g., the alkali metal sulfide or the sodium carboxylate, or from a mixture of two or more of the essential ingredients. For example, water can be removed from a mixture of N-alkyl lactam and hydrated alkali metal sulfide, optionally containing free water and/or alkali metal carboxylate which itself can be employed in anhydrous or hydrated form or as a solution. If the amount of water removed is greater than desired, water can then be added as required to provide the quantity of water desired. When the above dehydration step is employed, it is preferable to add the p-dihalo unsubstituted benzene, the p-dihalo-alkyl substituted benzene, and the polyhalo aromatic compound having more than two halogen substituents per molecule after the dehydration step has begun. The arylene sulfide terpolymer produced by the processes of this invention can be separated from the reaction mixture by conventional procedures, e.g., by filtration of the polymer, followed by washing with water, or by dilution of the reaction mixture with water, followed by filtration and water washing of the polymer. Alternatively, N-alkyl lactam can be recovered by distillation from the reaction mixture prior to washing with water. When this latter procedure is employed, and the N-alkyl lactam is distilled at elevated temperatures, e.g., above 2000C, it is preferable that carbon dioxide be added during the polymerization reaction or upon completion of the polymerization reaction, but prior to distillation of the N-alkyl lactam, to inhibit decomposition of the arylene sulfide terpolymer during distillation of the N-alkyl lactam. In a preferred embodiment of the present invention amorphous, essentially non-crystalline arylene sulfide terpolymers are produced. They are prepared in the same manner as described above, except that from about 12 to about 30, preferably from about 15 to about 20 mole percent, of the p-halo alkyl substituted benzene must specifically be employed. The following examples illustrate the present invention. EXAMPES Example I In this example the preparation of the terpolymers of this invention is described. Polymerization reactions were carried out in a 1 liter, electrically heated, stirred autoclave manufactured by Autoclave Engineers, Inc. 125.16 grams (0.98 moles) of sodium sulfide flakes, 24.61 grams (10.30 moles) of anhydrous sodium acetate, 1.2 grams (0.03 moles) of sodium hydroxide and 228 cc of N-methyl-2-pyrrolidone (NMP) were charged to the reactor, and heated, with stirring, under atmospheric pressure until the air in the reactor is replaced by steam. The system was closed, heated under autogenous pressure to about 2350C, cooled to about 1620C, and dehydrated by distillation under atmospheric pressure at a temperature of up to about 2160C. Then 0.9925 moles of either p-dichlorobenzene (DCB) (for a control resin) or 0.9925 moles of a mixture of DCB and either a dichlortoluene (DCT) or a dichloroxylene (DCX) (for inventive resins), 0.905 grams (0.005 moles) of 1,2,4-trichlorobenzene (TCB), 4.5 grams (0.25 moles) of water, and 92 cc of NMP were added to the reactor. The reactor content was heated under autogenous pressure for 2 hours at 2350C and for 3 hours at 2650C. The cooled polymer was removed from the reactor, slurried and washed with hot water, collected on a suction filter, rinsed with acetone, and dried in a vacuum oven at about 100 C. Example II Pertinent properties of four arylene sulfide terpolymers are listed in Table I. Data in Table I show that in terpolymers containing at least 15 mole-% of either 2,5-dichlortoluene or 2,5-dichloroxylene no crystallization temperature (Tc) and melting temperature (Tm) were detected. These results indicate that said terpolymers were essentially non-crystalline. By contrast, terpolymers containing up to 20 mole-% of either 2,4- or 2,6-dichlorotoluene as comonomers remained crystalline. Table I Mole % of Mole % of Mole % of Transition Temperatures a) ( C) Inherent b) Run Comonomer I Comonomer II Comonomer III Tg Tc Tm Viscosity 1 99.5% DCB - 0.5% TCB 85 125 285 0.29 2 94.5% DCB 5.0% 2,5-DCT 0.5% TCB 90 164 256 0.50 3 89.5% DCB 10.0% 2,5-DCT 0.5% TCB 87 165 240 4 84.5% DCB 15.0% 2,5-DCT 0.5% TCB 86 None None 0.25 5 84.0% DCB 15.0% 2,5-DCT 1.0% TCB 88 None None 0.57 6 83.4% DCB 16.1% 2,5-DCT 0.5% TCB 85 None None 0.25 7 79.5% DCB 20.0% 2,5-DCT 0.5% TCB 85 None None 0.20 8 94.5% DCB 5.0% 2,5-DCX 0.5% TCB 87 151 260 0.32 9 89.5% DCB 10.0% 2,5-DCX 0.5% TCB 90 182 245 0.29 10 84.5% DCB 15.0% 2,5-DCX 0.5% TCB 94 None None 0.31 11 84.0% DCB 15.0% 2,5-DCX 1.0% TCB 92 None None 0.37 12 89.5% DCB 10.0% 2,4-DCT 0.5% TCB 61 119 255 0.06 13 84.5% DCB 15.0% 2,4-TCB 0.5% TCB 64 131 233 0.07 14 79.5% DCB 20.0% 2,4-DCT 0.5% TCB 69 155 215 0.06 15 89.5% DCB 10.0% 2,6-DCT 0.5% TCB 74 139 248 0.12 16 84.5% DCB 15.0% 2,6-DCT 0.5% TCB 76 170 230 0.09 17 79.5% DCB 20.0% 2,6-DCT 0.5% TCB 67 160 220 0.08 Footnotes: a) determined with a Du Pont Model 900 Differential Thermal Analyzer; Tg = glass transition temperature; Tc = crystallization temperature; Tm = melting temperature b) determined at 204 C on solutions containing 0.4 grams of terpolymer per 100 ml of 1-chloronaphthalene The following part of the description are preferred embodiments 1 to 64 presented in the format of claims.

Claims: 1. A process for making an arylene sulfide terpolymer comprising reacting at least one alkali metal sulfide, at least one p-dihalo unsubstituted benzene, at least one polyhalo aromatic compound having more than two halogen substituents per molecule, at least one p-halo, alkyl substituted benzene, and at least one N-alkyl lactam under polymerization conditions of temperature and time sufficient to produce the desired terpolymer. 2. A process as in claim 1 for making an arylene sulfide terpolymer comprising reacting at least one alkali metal sulfide, at least one p-dihalo unsubstituted benzene, at least one polyhalo aromatic compound having more than two halogen substituents per molecule, at least one p-dihalo, alkyl substituted benzene, at least one N-alkyl lactam, and at least one selected from the group consisting of (a) water, including water of hydration, in an amount of about .2 moles to about 2.5 moles per molecule of alkali metal sulfide, and (b) at least one alkali metal carboxylate and water, including water of hydration, in an amount of 0.0 mole to about 2.5 moles per mole of alkali metal sulfide under polymerization conditions of temperature and time sufficient to produce the desired terpolymer. 3. A process according to claim 2 wherein the mole ratio of the combination of said p-dihalo unsubstituted benzene and said p-dihalo alkyl substituted benzene is within the range of 0.98:1 to about 1.03:1, the mole ratio of said polyhalo aromatic compound to said alkali metal sulfide is within the range of about 0.0002:1 to about 0.014:1, the mole ratio of said N-alkyl lactam to said alkali metal sulfide is within the range of about 2:1 to about 10:1, the mole ratio of alkali metal carboxylate when used, to said alkali metal sulfide is within the range of from about 0.05:1 to about 1.5:1. 4. A process as in claim 2 wherein said p-dihalo unsubstituted benzene is p-dichlorobenzene, said polyhalo aromatic compound is 1,2,4-trichlorobenzene, said p-dihalo alkyl substituted benzene is either 2,5-dichlorotoluene or 2,5-dichloro-p-xylene, said N-alkyl lactam is N-methyl pyrrolidone and said alkali metal carboxylate is a sodium carboxylate. 5. A process as in claim 4 wherein said p-dihalo alkyl substituted benzene is present in an amount from about 15 mole percent to about 30 mole percent. 6. A process as in claim 5 wherein said p-dihalo alkyl substituted benzene is present in an amount from about 15 mole percent to about 20 mole percent. 7. A process according to claim 1 wherein said polymerization is carried out at a temperature of from about 1800C to about 2850C. 8. A process for making an arylene sulfide terpolymer comprising first reacting an at least one alkali metal sulfide in hydrated form or in an aqueous mixture with at least one N-alkyl lactam to form a reaction product, thereafter heating the reaction product to form a dehydrated composition, then reacting the dehydrated composition with a mixture consisting essentially of at least one p-dihalo unsubstituted benzene, at least one polyhalo aromatic compound having more than 2 halogen atoms per molecule, at least one p-dihalo alkyl substituted benzene, and at least one member selected from the group consisting of (a) water in an amount of about 0.2 mole to about 2.5 moles per molecule of alkali metal sulfide, and (b) at least one alkali metal carboxylate and water, including water of hydration, in an amount of 0.0 mole to about 2.5 moles per mole of alkali metal sulfide under polymerization conditions for a time sufficient to produce the desired terpolymer. 9. A process according to claim 8 wherein the mole ratio of the combination of said p-dihalo unsubstituted benzene and said p-dihalo alkyl substituted benzene is within the range of 0.98:1 to about 1.03:1, the mole ratio of said polyhalo aromatic compound to said alkali metal sulfide is within the range of about 0.0002:1 to about 0.014:1, the mole ratio of said N-alkyl lactam to said alkali metal sulfide is within the range of about 2:1 to about 10:1, the mole ratio of alkali metal carboxylate when used, to said alkali metal sulfide is within the range of from about 0.05:1 to about 1.5:1. 10. A process as in claim 9 wherein said p-dihalo unsubstituted benzene is p-dichlorobenzene, said polyhalo aromatic compound is 1,2,4-trichlorobenzene, said p-dihalo alkyl substituted benzene is either 2,5-dichlorotoluene or 2,5-dichloro-p-xylene, and said N-alkyl lactam is N-methyl pyrrolidone and said alkali metal carboxylate is sodium carboxylate. 11. A process as in claim 10 wherein said p-dihalo alkyl substituted benzene is present in an amount from about 12 mole percent to about 30 mole percent. 12. A process as in claim 11 wherein said p-dihalo alkyl substituted benzene is present in an amount from about 15 mole percent to about 20 mole percent. 13. A process according to claim 8 wherein said polymerization is carried out at a temperature of from about 1800C to about 285 C. 14. A terpolymer made according to the process of claim 1. 15. A terpolymer made according to the process of claim 2. 16. A terpolymer according to claim 15 wherein the mole ratio of the combination of said p-dihalo unsubstituted benzene and said p-dihalo alkyl substituted benzene is within the range of 0.98:1 to about 1.03:1, the mole ratio of said polyhalo aromatic compound to said alkali metal sulfide is within the range of about 0.0002:1 to about 0.014:1, the mole ratio of said N-alkyl lactam to said alkali metal sulfide is within the range of about 2:1 to about 10:1, the mole ratio of alkali metal carboxylate when used, to said alkali metal sulfide is within the range of from about 0.05:1 to about 1.5:1. 17. A terpolymer according to claim 16 wherein said p-dihalo unsubstituted benzene is p-dichlorobenzene, said polyhalo aromatic compound is 1,2,4-trichlorobenzene, said p-dihalo alkyl substituted benzene is either 2,5 dichlorotoluene or 2,5-dichloro-p-xylene, and said N-alkyl lactam is N-methyl pyrrolidone and said alkali metal carboxylate is sodium carboxylate. 18. A terpolymer according to claim 17 wherein said p-dihalo alkyl substituted benzene is present in an amount from about 12 mole percent to about 30 mole percent. 19. A terpolymer according to claim 18 wherein said p-dihalo alkyl substituted benzene is present in an amount from about 15 mole percent to about 20 mole percent. 20. A terpolymer according to claim 19 wherein said polymerization is carried out at a temperature of from about 1800C to about 2850C. 21. A terpolymer made according to the process of claim 8. 22. A terpolymer according to claim 21 wherein the mole ratio of the combination of said p-dihalo unsubstituted benzene and said p-dihalo alkyl substituted benzene is within the range of 0.98:1 to about 1.03:1, the mole ratio of said polyhalo aromatic compound to said alkali metal sulfide is within the range of about 0.0002:1 to about 0.014:1, the mole ratio of said N-alkyl lactam to said alkali metal sulfide is within the range of about 2:1 to about 10:1, the mole ratio of sodium carboxylate when used, to said alkali metal sulfide is within the range of from about 0.05:1 to about 1.5:1. 23. A terpolymer according to claim 22 wherein said p-dihalo unsubstituted benzene is p-dichlorobenzene, said polyhalo aromatic compound is 1,2,4-trichlorobenzene, said p-dihalo alkyl substituted benzene is either 2.5 dichlorotoluene or 2,5-dichloro-p-xylene, and said N-alkyl lactam is N-methyl pyrrolidone. 24. A terpolymer according to claim 23 wherein said p-dihalo alkyl substituted benzene is present in an amount from about 12 mole percent to about 30 mole percent. 25. A terpolymer according to claim 24 wherein said p-dihalo alkyl substituted benzene is present in an amount from about 15 mole percent to about 20 mole percent. 26. A terpolymer according to claim 25 wherein said polymerization is carried out at a temperature of from about 1800C to about 2850C. 27. A process for making arylene sulfide terpolymers comprising reacting at least one alkali metal sulfide, at least one p-dihalo unsubstituted bezene, at least one polyhaloaromatic compound having more than two halogen substituents per molecule, at least one p-dihalo, alkyl substituted benzene, and at least one N-alkyl lactam at a temperature of from about 1800C to about 2850C for a period of time from about 1 to about 60 hours. 28. A process as in claim 27 for making an arylene sulfide terpolymer comprising reacting at least one alkali metal sulfide, at least one p-dihalo unsubstituted benzene, at least one polyhalo aromatic compound having more than two halogen substituents per molecule, at least one p-dihalo, alkyl substituted benzene, at least one N-alkyl lactam, and at least one selected from the group consisting of (a) water, including water of hydration, in an amount of about 0.2 moles to about 2.5 moles per molecule of alkali metal sulfide, and (b) at least one alkali metal carboxylate and water, including water of hydration, in an amount of 0.0 mole to about 2.5 moles per mole of alkali metal sulfide under polymerization conditions of temperature and time sufficient to produce the desired terpolymer. 29. A process according to claim 28 wherein the mole ratio of the combination of said p-dihalo unsubstituted benzene and said p-dihalo alkyl substituted benzene is within the range of 0.98:1 to about 1.03:1, the mole ratio of said polyhalo aromatic compound to said alkali metal sulfide is within the range of about 0.0002:1 to about 0.014:1, the mole ratio of said N-alkyl lactam to said alkali metal sulfide is within the range of about 2:1 to about 10:1, the mole ratio of alkali metal carboxylate when used, to said alkali metal sulfide is within the range of from about 0.05:1 to about 1.5:1. 30. A process as in claim 29 wherein said p-dihalo unsubstituted benzene is p-dichlorobenzene, said polyhalo aromatic compound is 1,2,4-trichlorobenzene, said p-dihalo alkyl substituted benzene is either 2,5-dichlorotoluene or 2,5-dichloro-p-xylene, said N-alkyl lactam is N-methyl pyrrolidone and said alkali metal carboxylate is a sodium carboxylate. 31. A process as in claim 30 wherein said p-dihalo alkyl substituted benzene is present in an amount from about 12 mole percent to about 30 mole percent. 32. A process as in claim 31 wherein said p-dihalo alkyl substituted benzene is present in an amount from about 15 mole percent to about 20 mole percent. 33. A process for making an arylene sulfide terpolymer comprising making an arylene sulfide terpolymer comprising first reacting an at least one alkali metal sulfide in hydrated form or in an aqueous mixture with at least one N-alkyl lactam to form a reaction product, thereafter heating the reaction product to form a dehydrated composition, then reacting the dehydrated composition with a mixture consisting essentially of at least one p-dihalo unsubstituted benzene, at least one polyhalo aromatic compound having more than 2 halogen atoms per molecule, at least one p-dihalo alkyl substituted benzene, and at least one member selected from the group cosnisting of (a) water in an amount of about 0.2 mole to about 2.5 moles per molecule of alkali metal sulfide, and (b) at least one alkali metal carboxylate and water, including water of hydration, in an amount of 0.0 mole to about 2.5 moles per mole of alkali metal sulfide at a temperature of from about 1800C to about 2850C for a period of time from about 1 to 60 hours. 34. A process according to claim 33 wherein the mole ratio of the combination of said p-dihalo unsubstituted benzene and said p-dihalo alkyl substituted benzene is within the range of 0.98:1 to about 1.03:1, the mole ratio of said polyhalo aromatic compound to said alkali metal sulfide is within the range of about 0.0002:1 to about 0.014:1, the mole ratio of said N-alkyl lactam to said alkali metal sulfide is within the range of about 2:1 to about 10:1, the mole ratio of alkali metal carboxylate when used, to said alkali metal sulfide is within the range of from about 0.05:1 to about 1.5:1. 35. A process as in claim 34 wherein said p-dihalo unsubstituted benzene is p-dichlorobenzene, said polyhalo aromatic compound is 1,2,4-trichiorobenzene, said p-dihalo alkyl substituted benzene is either 2,5-dichlorotoluene or 2,5-dichloro-p-xylene, and said N-alkyl lactam is N-methyl pyrrolidone and said alkali metal carboxylate is sodium carboxylate. 36. A process as in claim 35 wherein said p-dihalo alkyl substituted benzene is present in an amount from about 12 mole percent to about 30 mole percent. 37. A process as in claim 36 wherein said p-dihalo alkyl substituted benzene is present in an amount from about 15 mole percent to about 20 mole percent. 38. A terpolymer according to claim 27. 39. A terpolymer made according to the process of claim 28. 40. A terpolymer according to claim 39 wherein the mole ratio of the combination of said p-dihalo unsubstituted benzene and said p-dihalo alkyl substituted benzene is within the range of 0.98:1 to about 1.03:1, the mole ratio of said polyhalo aromatic compound to said alkali metal sulfide is within the range of about 0.0002:1 to about 0.014:1, the mole ratio of said N-alkyl lactam to said alkali metal sulfide is within the range of about 2:1 to about 10:1, the mole ratio of alkali metal carboxylate when used, to said alkali metal sulfide is within the range of from about 0.05:1 to about 1.5:1. 41. A terpolymer according to claim 40 wherein said p-dihalo unsubstituted benzene is p-dichlorobenzene, said polyhalo aromatic compound is 1,2,4-trichlorobenzene, said p-dihalo alkyl substituted benzene is either 2.5 dichlorotoluene or 2,5-dichloro-p-xylene, and said N-alkyl lactam is N-methyl pyrrolidone and said alkali metal carboxylate is sodium carboxylate. 42. A terpolymer according to claim 41 wherein said p-dihalo alkyl substituted benzene is present in an amount from about 12 mole percent to about 30 mole percent. 43. A terpolymer according to claim 42 wherein said p-dihalo alkyl substituted benzene is present in an amount from about 15 mole percent to about 20 mole percent. 44. A terpolymer made according to the process of claim 33. 45. A terpolymer according to claim 44 wherein the mole ratio of the combination of said p-dihalo unsubstituted benzene and said p-dihalo alkyl substituted benzene is within the range of 0.98:1 to about 1.03:1, the mole ratio of said polyhalo aromatic compound to said alkali metal sulfide is within the range of about 0.0002:1 to about 0.014:1, the mole ratio of said N-alkyl lactam to said alkali metal sulfide is within the range of about 2:1 to about 10:1, the mole ratio of sodium carboxylate when used, to said alkali metal sulfide is within the range of from about 0.05:1 to about 1.5:1. 46. A terpolymer according to claim 45 wherein said p-dihalo unsubstituted benzene is p-dichlorobenzene, said polyhalo aromatic compound is 1,2,4-trichlorobenzene, said p-dihalo alkyl substituted benzene is either 2,5-dichlorotoluene or 2,5-dichloro-p-xylene, and said N-alkyl lactam is N-methyl pyrrolidone. 47. A terpolymer according to claim 46 wherein said p-dihalo alkyl substituted benzene is present in an amount from about 12 mole percent to about 30 mole percent. 48. A terpolymer according to claim 47 wherein said p-dihalo alkyl substituted benzene is present in an amount from about 15 mole percent to about 20 mole percent. 49. A terpolymer according to claim 48 wherein said polymerization is carried out at a temperature of from about 1800C to about 2850C. 50. An article of manufacture prepared from the terpolymer of claim 14. 51. An article of manufacture prepared from the terpolymer of claim 15. 52. An article of manufacture prepared from the terpolymer of claim 18. 53. An article of manufacture prepared from the terpolymer of claim 19. 54. An article of manufacture prepared from the terpolymer of claim 21. 55. An article of manufacture prepared from the terpolymer of claim 22. 56. An article of manufacture prepared from the terpolymer of claim 24. 57. An article of manufacture prepared from the terpolymer of claim 25. 58. An article of manufacture prepared from the terpolymer of claim 38. 59. An article of manufacture prepared from the terpolymer of claim 39. 60. An article of manufacture prepared from the terpolymer of claim 42. 61. An article of manufacture prepared from the terpolymer of claim 43. 62. An article of manufacture prepared from the terpolymer of claim 44. 63. An article of manufacture prepared from the terpolymer of claim 47. 64. An article of manufacture prepared from the terpolymer of claim 48. Claims 1. A process for making an arylene sulfide terpolymer com prising reacting at least one alkali metal sulfide, at least one p-dihalo unsubstituted benzene, at least one polyhalo aromatic compound having more than two halogen substituents per molecule, at least one p-halo, alkyl substituted benzene, and at least one N-alkyl lactam under polymerization conditions. 2. The process of claim 1 characterized in that said reac tion is carried out in the presence of (a) water, inclu ding water of hydration, in an amount of 0.2 to 2.5 moles per mole of alkali metal sulfide, or (b) at least one alkali metal carboxylate and water, including water of hydration, in an amount of 0.0 to 2.5 moles per mole of alkali metal sulfide. 3. The process of claim 2 characterized by first reacting said alkali metal sulfide in hydrated form or in an aqueous mixture with said N-alkyl lactam to form a reac tion product, thereafter heating the reaction product to form a dehydrated composition, then reacting the dehydra ted composition with a mixture containing said p-dihalo unsubstituted benzene, said polyhalo aromatic compound having more than 2 halogen atoms per molecule, said p-dihalo alkyl substituted benzene, and said (a) or (b). 4. The process of any of claims 1 to 3 characterized in that the mole ratio of said p-dihalo unsubstituted ben zene to said p-dihalo alkyl substituted benzene is within the range of 0.98:1 to 1.03:1, the mole ratio of said polyhalo aromatic compound to said alkali metal sulfide is within the range of C40002:1 to 0.014:1 and the mole ratio of said N-alkyl lactam to said alkali metal sulfide is within the range of 2:1 to 10:1. 5. The process of any of claims 1 to 4 characterized in that said p-dihalo unsubstituted benzene is p-dichlorobenzene, said polyhalo aromatic compound is 1,2,4-trichlorobenzene, said p-dihalo alkyl substituted benzene is either 2,5-di chlorotoluene or 2,5-dichloro -xylene and said N-alkyl lactam is N-methyl pyrrolidone. 6. The process of any of claims 1 to 5 characterized in that said p-dihalo alkyl substituted benzene is present in an amount from 12 to 30 mole percent. 7. The process of claim 6 characterized in that said p-di halo alkyl substituted benzene is present in an amount from 1.5 to 20 mole percent. 8. The process of any of claims 1 to 7 characterized in that said polymerization is carried out at a temperature of 180 to 2850C; in particular wherein said polymerization is carried out for a period of time from 1 to 60 hours. 9. The process of any of claims 2 to 8 characterized in that the mole ratio of alkali metal carboxylate when used, to said alkali metal sulfide is within the range of 0.05:1 to 1.5:1; in particular wherein said alkali metal carb oxylate is a sodium carboxylate. 10. A terpolymer made according to the process of one of claims 1 to 9. 11. An article of manufacture prepared from the terpolymer of claim 10.

Inventors: CLEARY, JAMES WILLIAM
Applicants: PHILLIPS PETROLEUM COMPANY
Application year: 1983
Main classification: C08G75
IPC codes: C08G75