Process for producing wholly aromatic polyesters

Abstract: Wholly aromatic polyesters having improved mechanic­ al properties are produced by polycondensing a raw material or raw material mixture capable of forming an aromatic polyester and not more than 20 mole%, based on the total amount of the entire raw materials, of 2-hydroxy-­ naphthalene-6-carboxylic acid or its derivative.

Description: This invention relates to an improvement in a process for producing aromatic polyesters. Wholly aromatic polyesters have been known, and, for example, homo- and copolymers of p-hydroxy-benzoic acid have already been manufactured and marketed. These polymers have the defect that they have a low molecular weight, and because of their relatively high melting points or their lower decomposition temperatures than their melting points, they are difficult to process or fabricate. Furthermore, these polymers cannot be formed into practical fibers by a melt-extrusion method. For example, fibers obtained by melt-extrusion at very high temperatures generally have an empty internal structure and a low tensile strength. To overcome these defects, various new wholly aromatic polyesters have been proposed heretofore. They include, for example, polyesters derived from aromatic dicarboxylic acids and aromatic diols, and polyesters derived from aromatic dicarboxylic acids, aromatic hydroxycarboxylic acids and aromatic diols. These wholly aromatic polyesters have not proved to be entirely satisfactory, and have the disadvantage that they have a low molecular weight and tend to undergo decomposition rather than melting, and because of non-uniformity in the polymerization reactions, polymers having fixed properties are difficult to obtain. From EP-A-0 049 617 there was known a polyester of 6-hydroxy-2-naphthoic acid, p-hydroxy benzoic acid terephthalic acid and resorcinol for melt-processing to form shaped articles having increased impact strength. It is an object of this invention to provide a process for preparing wholly aromatic polyesters which at high temperatures have a high dimensional stability and do not tend to decompose in the molten state. That problem is solved according to the invention by a process for producing a melt-processable wholly aromatic polyester which consists essentially of the recurring moieties I, II, III and IV wherein I is 4-hydroxybenzoyl being present in an amount of 30 to 65 mole %; II is dihydroxyaryl derived from hydroquinone, 4,4'-biphenol, naphthalene-2,6-diol and mixtures of the foregoing, being present in an amount of 10 to 30 mole %, III is dicarboxyaryl derived from terephthalic acid, being present in an amount of 10 to 30 mole %, and IV is 2-hydroxy-6-naphthoyl being present in an amount of 2 to 15 mole %, by heating the I, II, III and IV moieties-forming derivatives at a temperature of from 150 to 400°C, optionally in the presence of a heat medium and optionally by using a vacuum. In the process according to the invention, the viscosity of the system decreases and the reaction proceeds smoothly, and as a result, the arrangement of the repeating units of the polymer becomes steady and the resulting polyester has improved properties. The raw material or raw material mixture capable of forming an aromatic polyester in this invention may be any one of the following materials (a), (b) and (c). (a) An aromatic hydroxycarboxylic acid other than 2-hydroxynaphthalene-6-carboxylic acid, or its derivative. (b) a mixture of an aromatic dicarboxylic acid or its derivative and an aromatic diol or its derivative. (c) A mixture of an aromatic dicarboxylic acid or its derivative, an aromatic diol or its derivative, and an aromatic hydroxycarboxylic acid other than 2-hydroxynaphthalene-6-carboxylic acid or its derivative. The amount of 2-hydroxynaphthalene-6-carboxylic acid or its derivative used differs for the above materials (a), (b) and (c). For the materials (a) and (b), it is not more than 10 mole%, preferably 2 to 10 mole%, especially preferably 5 to 10 mole%, based on the total amount of the starting materials (including 2-hydroxynaphthalene-6-carboxylic acid or its derivative). In the case of the material (c), the amount is 2 to 15 mole%, based on the total amount of the starting materials (including 2-hydroxynaphthalene-6-carboxylic acid or its derivative). Amounts exceeding these limits are economically undesirable since 2-hydroxynaphthalene-6-carboxylic acid or its derivative is relatively expensive. In addition, they rather result in a reduction in the effect of carrying out the reaction smoothly. Such excessive amounts should therefore be avoided. Needless to say, in any of the above cases, the amounts of the individual starting materials should be selected such that the total amount of the alcohol component becomes equivalent to the total amount of the acid component. An example of the aromatic hydrocarboxylic acid other than 2-hydroxynaphthalene-6-carboxylic acid is p-hydroxybenzoic acid. An examples of the aromatic dicarboxylic acid and its derivatives is terephthalic acid. Examples of the aromatic diol and its derivatives are 4,4'-biphenol, hydroquinone, and naphthalene-2,6-diol. The polycondensation reaction of the starting materials is carried out by using a known ester interchange catalyst in an amount of about 0.001 to 1% by weight, preferably about 0.01 to about 0.2% by weight, based on the total weight of the starting materials. The ester interchange catalyst includes, for example, dialkyltin oxides, diaryltin oxides, titanium dioxide, titanium alkoxides, alkoxytitanium silicates, alkali metal or alkaline earth metal carboxylates, gaseous acid catalysts, Lewis acids such as BF 3 , and hydrogen halides such as hydrogen chloride. The reaction can be carried out by various known methods for obtaining random copolymers, block copolymers or highly ordered copolymers. A bulk polymerization technique and a suspension polymerization technique using a suitable heat medium can both be used. The reaction temperature is 150 to 400°C, preferably 200 to 400°C, especially preferably 250 to 350°C. Vacuum may be used to facilitate removal of volatile components formed in the final stage of the condensation, such as acetic acid, water, alcohols, and phenol. The wholly aromatic polyester obtained by the method of this invention has an intrinsic viscosity, measured at 60°C for its solution in pentafluorophenol in a concentration of 0.01% by weight, of usually at least about 0.4, preferably at least about 1.0, for example 1.0 to 7.5, and a weight average molecular weight of about 2.000 to 200,000, preferably about 10,000 to about 50,000. The molecular weight of this wholly aromatic polyester can be increased by subjecting it to a solid-state polymerization operation. For example, when the wholly aromatic polyester in the form of granules, fibers or a film is heated at a temperature below its melting point in an atmosphere of an inert gas such as nitrogen for several minutes to several days, if desired under reduced pressure, its molecular weight increases. Since the wholly aromatic polyester obtained by the process of this invention can form a thermotropic molten phase, it can be easily formed into various molded articles such as fibers, films and other three-dimensional molded articles. Fibers are particularly advantageously used as tire cords, and also find applications as conveyor belts, hoses, cables and resin reinforcing materials. Films can be used as packaging tapes, cable wrappings, magnetic tapes, and electrically insulating films. Other three-dimensional molded articles include, for example, machine parts, parts of electronic ovens, heating vessels. The following non-limitative examples specifically illustrate the present invention. The property values given in these examples were measured in accordance with ASTM D256, D638 and D790. Unless otherwise specified, all the viscosity values of the polymers in these examples were measured at 60°C for a solution of the polymer in pentafluorophenol in a concentration of 0.1% by weight. Example 1 27.0 g (0.15 mole) of p-acetoxybenzoic acid, 40.5 g (0.15 mole) of 4,4'-biphenol diacetate, 29.1 g (0.15 mole) of dimethyl terephthalate and 11.5 g (0.05 mole) of 2-acetoxynaphthalene-6-carboxylic acid were stirred in a stream of nitrogen at 250°C for 2.5 hours and then at 280° for 1 hour, and acetic acid and methanol were distilled off. The degree of vacuum was gradually raised at 3102C over the course of about 10 minutes. The reaction mixture was maintained at 13.33 Pa for 30 minutes to terminate the reaction. After cooling, the polymer was finely pulverized and dried at 150°C for 1 hour while passing air. The resulting polymer (about 72 g) had an intrinsic viscosity of 5.9. The polymer was melt-extruded into continuous filaments (about 20 denier/filament) and quenched in the outer atmosphere (20°C, relative humidity 65%). The resulting filaments had the following mechanical properties. Tenacity: 19.1 g/denier Tensile modulus: 590 g/denier Elongation: 1.8% When these filaments were heat-treated at 250°C for 90 hours, they showed the following mechanical properties. Tenacity: 26.0 g/denier Tensile modulus: 630 g/denier Elongation: 2.4% These filaments showed low shrinkage at high temperatures, dimensional stability at temperatures between about 150 and 200°C, and excellent resistance to hydrolysis Example 2 27.0 g (0.15 mole) of p-acetoxybenzoic acid, 36.6 g (0.15 mole) of 2,6-bisacetoxy-naphthalene, 29.1 g (0.15 mole) of dimethyl terephthalate and 11.5 g (0.05 mole) of 2-acetoxynaphthalene-6-carboxylic acid were stirred in a stream of nitrogen at 250°C for 1 hour and then at 280°C for 1 hour, and acetic acid and methanol were distilled off. Then, the degree of vacuum was gradually raised at 320°C over the course of about 10 minutes. The reaction mixture was maintained at 66.66 Pa for 1 hour to terminate the reaction. After cooling, the polymer was finely pulverized, and dried at 150°C for 1 hour while passing air. The resulting polymer (about 70 g) had an intrinsic viscosity of 6.9. The polymer was dried overnight under vacuum at 80°C, and injection-molded at 310°C. The molded article had the following properties. Tensile break: 2.254 bar Elongation: 5.2% Tensile modulus: 1.078×10 5 bar Flexural break: 1.568 bar Flexural modulus: 0.784×10 5 bar Notched Izod impact: 61.5 kg-cm/cm Example 3 34.2 g (0.19 mole) of p-acetoxybenzoic acid, 29.1 g (0.15 mole) of hydroquinone diacetate, 29.1 g (0.15 mole) of dimethyl terephthalate and 2.3 g (0.01 mole) of 2-acetoxynaphthalene-6-carboxylic acid were reacted in the same way as in Example 1. The resulting polymer (about 60 g) had an intrinsic viscosity of 4.7. The polymer was melt-extruded into continuous filaments (about 20 denier/filament), and quenched in the outer atmosphere (20°C relative humidity 65%). The resulting filaments had the following mechanical properties. Tenacity: 12.6 g/denier Tensile modulus: 486 g/denier Elongation: 3.2% when these filaments were heat-treated at 250°C for 90 hours, they showed the following mechanical properties. Tenacity: 17.6 g/denier Tensile modulus: 498 g/denier Elongation: 3.4% These filaments had low shrinkage at high temperature, dimensional stability at temperatures between about 150 and about 200°C, and excellent resistance to hydrolysis Comparative Example 1 135.0 g (0.50 mole) of 4,4'-biphenyl diacetate and 97.0 g (0.50 mole) of dimethyl terephthalate were stirred in a stream of nitrogen at 250°C for 4 hours and then at 280°C for 1 hour, and acetic acid and methanol were distilled off. Then, the degree of vacuum was gradually raised at 340°C over the course of about 40 minutes. The reaction mixture was maintained at 13.33-26.66 Pa for 1 hour to terminate the reaction. After cooling, the polymer was finely pulverized, and dried at 150°C for 1 hour while passing air. The resulting polymer (about 157 g) had an intrinsic viscosity of 1.2. The polymer was melt-extruded into filaments (about 20 denier/filament), and quenched in the outer atmosphere (20°C, relative humidity 65%). The resulting filaments had the following mechanical properties. Tenacity: 3.6 g/denier Tensile modulus: 340 g/denier Elongation: 2.0% When these filaments were heat-treated at 250°C for 90 hours, they showed the following mechanical properties. Tenacity: 5.2 g/denier Tensile modulus: 350 g/denier Elongation: 2.8% Comparative Example 2 36.0 g (0.20 mole) of p-acetoxybenzoic acid, 40.5 g (0.15 mole) of 4,4'-biphenol diacetate and 29.1 g (0.15 mole) of dimethyl terephthalate were stirred in a stream of nitrogen at 250°C for 2.5 hours and then at 280°C for 1 hour, and acetic acid and methanol were distilled off. Then, the degree of vacuum was gradually raised at 320°C over the course of about 20 minutes. The reaction mixture was maintained at 13.33-26.66 Pa for 1 hour to terminate the reaction. After cooling, the polymer was finely pulverized, and dried at 150°C for 1 hour while passing air. The resulting polymer (about 71 g) had an intrinsic viscosity of 3.2. The polymer was melt-extruded into filaments (about 20 denier/filament), and quenched in the outer atmosphere (20°C, relative humidity 65%). The resulting filaments had the following mechanical properties. Tenacity: 5.3 g/denier Tensile modulus: 320 g/denier Elongation: 1.9% When these filaments were heat-treated at 250°C for 90 hours, they showed the following mechanical properties. Tenacity: 7.5 g/denier Tensile modulus: 370 g/denier Elongation: 2.9% Example 4 117.0 g (0.65 mole) of p-acetoxybenzoic acid, 34.5 g (0.15 mole) of 2-acetoxynaphthalene-6-carboxylic acid, 24.6 g (0.10 mole) of 4,4'-biphenol diacetate and 16.6 g (0.10 mole) of terephthalic acid were stirred in a stream of nitrogen at 250°C for 1 hour and then at 280°C for 1 hour, and acetic acid was distilled off. Then, the degree of vacuum was gradually raised at 320°C over the course of about 10 minutes. The reaction mixture was maintained at 66.66 Pa for 1 hour to terminate the reaction. After cooling, the polymer was finely pulverized, and dried at 150°C for 1 hour while passing air. The resulting polymer (about 132 g) had an intrinsic viscosity of 7.3. The polymer was dried overnight in vacuum at 80°C, and injection-molded at 300°C. The molded article had the following properties. Tensile break: 2.058 bar Elongation: 3.2% Tensile modulus: 1.47×10 5 bar Flexural break: 1.568 bar Flexural modulus: 0.882 bar Notched Izod impact: 43.5 kg-cm/cm Example 5 81.0 (0.45 mole) of p-acetoxybenzoic acid, 34.5 g (0.15 mole) of 2-acetoxynaphthalene-6-carboxylic acid, 38.8 g (0.20 mole) of hydroquinone diacetate and 33.2 g (0.20 mole) of terephthalic acid were stirred in a stream of nitrogen at 250°C for 1 hour and then at 280°C for 1 hour, and acetic acid was distilled off. Then, the degree of vacuum was raised gradually at 320°C for about 30 minutes. The reaction mixture was maintained at 26.66 Pa for 2 hours to terminate the reaction. After cooling, the polymer was finely pulverized, and dried at 150°C for 1 hour. The resulting polymer (about 127 g) had an intrinsic viscosity of 6.5. The polymer was dried overnight in vacuum at 80°C, and then injection-molded at 310°C. The molded article had the following properties. Tensile break: 2.254 bar Elongation: 2.5% Tensile modulus: 1.96×10 5 bar Flexural break: 1.470 bar Flexural modulus: 0.882 bar Notched Izod impact: 28.0 kg-cm/cm

Claims: Claims for the following Contracting States : BE, CH, LI A process for producing a melt-processable wholly aromatic polyester which consists essentially of the recurring moieties I, II, III and IV wherein I is 4-hydroxybenzoyl being present in an amount of 30 to 65 mole %; II is dihydroxyaryl derived from hydroquinone, 4,4'-biphenol, naphthalene-2,6-diol and mixtures of the foregoing, being present in an amount of 10 to 30 mole %, III is dicarboxyaryl derived from terephthalic acid, being present in an amount of 10 to 30 mole %, and IV is 2-hydroxy-6-naphthoyl being present in an amount of 2 to 15 mole %, by heating the I, II, III and IV moieties-forming derivatives at a temperature of from 150 to 400°C, optionally in the presence of a heat medium and optionally by using a vacuum. Claims for the following Contracting States : DE, FR, GB, IT, NL A process for producing a melt-processable wholly aromatic polyester which consists essentially of the recurring moieties I, II, III and IV wherein I is 4-hydroxybenzoyl being present in an amount of 30 to 65 mole %; II is dihydroxyaryl derived from hydroqinone, 4,4'-biphenol, naphthalene-2,6-diol and mixtures of the foregoing, being present in an amount of 10 to 30 mole %, III is dicarboxyaryl derived from terephthalic acid being present in an amount of 10 to 30 mole %, and IV is 2-hydroxy-6-naphthoyl being present in an amount of 2 to 15 mole %, excluding 3 to 15 mole %, by heating the I, II, III and IV moieties-forming derivatives at a temperature of from 150 to 400°C, optionally in the presence of a heat medium and optionally by using a vacuum.

Inventors: NAKAMURA YASUNORI, SAKOTA KAZUYUKI, UENO RYUZO, NAKAMURA, YASUNORI, SAKOTA, KAZUYUKI, UENO, RYUZO
Applicants: UENO SEIYAKU OYO KENKYUJO KK, KABUSHIKI KAISHA UENO SEIYAKU OYO KENKYUJO
Application year: 1983
Main classification: C08G63
IPC codes: C08G63