POLYMER SOLUTIONS

Abstract: The stability against degradation of a solvent for organic polymers comprising a hydrated tertiary amine N-oxide is improved by the incorporation of a stabilising additive selected from phosphoric acids, phosphate salts, phosphonic acids, phosphonate salts and complexes of any of the foregoing with occluded metal ions. The stabilising additive also helps to stabilise polymers dissolved in the solvent against degradation, particularly cellulose. A preferred additive is sodium hexametaphosphate. In a process for forming fibres or film from amine oxide solutions of cellulose, the stabilising additive helps to prevent discolouration of the fibres or film by degradation products and excessive reduction in the degree of polymerisation of the cellulose which can cause deterioration in strength of the fibres or film.

Description: Polymer solutions This invention relates to the stabilisation of hydrated tertiary amine N-oxides suitable as solvents for organic polymers and of solutions of organic polymers, particularly cellulose, in such solvents. The polymer solutions may be used as spinning or casting dopes for making shaped polymer articles such as fibres or films, and the invention includes a process for making such articles. Hydrated tertiary amine N-oxides (hereinafter referred to on occasion as 'amine oxides' for convenience) are susceptible to degradation, particularly at elevated temperatures and at certain lower levels of hydration, both of which are conditions which favour the dissolution of organic polymers in the amine oxides. Degradation results in a loss of amine oxide, which is an expensive solvent, and can give rise to discolouration of the sol¬ vent and any polymer dissolved in it. Degradation of the amine oxide solvent may also be accompanied by degradation of an organic polymer dissolved in that solvent. In the case of cellulose, there can be a significant reduction in the degree of polymerisation during dissolution at elevated temperatures and during any subsequent interval before the cellulose is regenerated. According to this invention, a solvent for organic polymers comprises a hydrated tertiary amine N-oxide characterised by the incorporation therein as a stabilis¬ ing additive of one or more compounds selected from phos¬ phoric acids, phosphate salts, phosphonic acids, phosphon- ate salts, and complexes of any of the foregoing with occluded metal ions. The invention includes the stabilised solvent of the invention having an organic polymer dissolved therein. The preferred organic polymer is cellulose. The added salt or acid stabilises the amine oxide and any dissolved organic polymer by substantially reduc- ing the rate of degradation reactions. It is believed that these are mainly oxidation reactions catalysed by occluded metal ions in the system, usually iron, and that the added acid or salt complexes with these ions to effectively remove the catalyst. The level of additive required to give the desired stability depends upon a number of factors including the occluded metal ion concentration, the time taken to form an organic polymer solution in the amine oxide and to regenerate the organic polymer from that solution, and the temperature to which the solution is heated as the organic polymer is being dissolved. Reduced process¬ ing times reduce the extent of degradation, and reduced temperatures and occluded metal ion concentrations reduce the rate of degradation. In general, up to 3.0 per cent by weight of stabilis¬ ing additive is sufficient, with a preferred range being 0.1 to 1.0 per cent by weight. In the case of solutions of cellulose, we have found that with commercial grades of wood pulp and amine oxides, and local mains water, a concentration of stabilising additive of 1 per cent by weight or less can give satisfactory stabilisation under conditions chosen to represent those encountered in dope preparation for a fibre spinning process. Phosphoric and phosphonic acids and their salts have the advantage compared with other potential complex- ing agents for occluded metal ions that they do not in general form coloured complexes, particularly with •iron, so that polymeric fibres or films, regenerated from solu- tion are not stained. Suitable acids and salts include disodium hydrogen phosphate, potassium .dihydrogen phos¬ phate, sodium hexa etaphosphate, hydroxyethylidene diphos- phonic acid, and aminoethyl disphosphonic acid. Sodium hexametaphosphate is the preferred stabilising additive. Hydrated tertiary amine N-oxides which are suitable solvents for cellulose and other organic polymers are described in United States Patent No. 2,179,181 and British Patent No. 1,144,048, which are incorporated herein by reference, and such amine oxides can be used in the present invention. The latter patent describes cyclic tertiary amine N-oxides and these are the preferred solvents used in the present invention, particularly N-methyl morpholine N-oxide which combines effectiveness as a solvent with thermal stability. According to the invention there is provided a pro¬ cess for making a shaped article of an organic polymer comprising dissolving the organic polymer in a solvent comprising a hydrated tertiary amine N-oxide to form a solution of the polymer, shaping the polymer solution and coagulating the shaped solution to form the desired shaped polymer article, characterised by incorporating in the solvent prior to the shaping step a stabilising additive which comprises one or more of the compounds comprising phosphoric acids, phosphate salts, phosphonic acids, phosphonate salts, and complexes of any of the foregoing with occluded metal ions. Preferably, the poly¬ mer solution is shaped into the form of fibres or film. For fibre spinning it is usually desirable to obtain as high a polymer concentration in the spinning dope as is compatible with suitable spinning viscosities. By this criterion, tertiary amine N-oxides are most effec¬ tive as solvents for organic polymers when they a,re in their normal hydrated state. The optimum water content of the solvent varies according to the particular amine oxide used, and the particular polymer which it is desired to dissolve. For cellulose a suitable general range is 1 to 30 per cent by weight of water, with a range of about 5 to 20 per cent water being preferred for N- methyl morpholine N-oxide. Polymers for which amine oxides are suitable solvents are set out in the aforementioned British Patent No. 1,144,048, and in addition to cellulose include synthetic polymers such as polyamides and cellulose acetate and natural polymers such as hair, feathers and casein. In the case of cellulose, a preferred source is wood pulp, with the dissolving grades provided for the viscose process being suitable. The polymer material has to be mixed with the amine oxide solvent to obtain dissolution, and it is advan¬ tageous for that solvent to have a water content in excess of that required to give the specified water con¬ tent of the polymer solution. This excess water promotes even polymer/solvent distribution and, in the case of wood pulp, promotes swelling of the cellulose fibres as an aid to dissolution. Even distribution is important because high local concentrations of polymer can give rise to undesirable gel formation. Once a uniform dissolving process is under way, then the water content of the solvent may be reduced to the level specified as optimum. For example in a continuous barrel mixer operated under vacuum to reduce the temperature require¬ ment for a desired dissolution rate, the temperature along the barrel may be profiled so that the excess water has evaporated off by the time solution is completed close to the barrel outlet. A suitable initial water content of the solvent for even mixing with wood pulp is in the range 15 to 50 per cent by weight. For cellulose, a polymer concentration of at least OM 5 per cent by weight of the solution is preferred for a fibre spinning dope, with 5 to 35 per cent by weight being a reasonable working range. Reference has been made to the use of the hydrated amine oxide solvent in combination with excess water to promote even mixing. It is also possible to add other diluents to the solvent, and these may themselves be solvents for a particular polymer or at least act as a co-solvent with the hydrated amine oxide. For example dimethyl acetamide is a suitable co-solvent for cellulose with an amine oxide. The invention is illustrated by the following Examples in which percentages are given by weight on the basis specified. In the Examples, the effect of the stabilising addi¬ tive is shown in comparison .with a control having no additive, and in the case of Examples 1 to 4 in comparison with an alternative additive. The effect is determined according to three parameters measured at the end of the test: the percentage of amine oxide remaining; the degree of polymerisation (D.P.) of the cellulose; and the colour of the solution. The three tests were carried out as follows:- Amine Oxide Yield (%) An aliquot of the solution, containing about 0.5 gm amine oxide, was acidified with hydrochloric acid and then reduced with an excess of titanous chloride solution. The excess titanous chloride used was deter¬ mined by a back titration with ferric ammonium sulphate solution using sodium thiocyanate as an indicator (brick red colour). A blank titration made the excess titanous chloride a known quantity, and the weight of amine * oxide in the sample, and hence the percentage yield, was calcu- O P lated from the formula:- ( — ~V . V t of amine oxide = IQ OO— x x A where B = Blank titre T = Titre of sample F = Molarity of ferric ammonium sulphate A = Molecular weight of amine oxide Cellulose D.P. Water was added to the solution to precipitate cellu¬ lose as a lump. This was sliced into thin shavings, washed with water to remove residual amine oxide, and then conditioned to 12 per cent water content. The cellulose was dissolved in cuprammonium hydrox¬ ide solution at a concentration of 0.50 per cent, and the viscosity of this solution was measured at 20°C using a Shirley Capillary Rheometer. The related D.P. for that measured viscosity was then taken from a standard graph plotting D.P. against viscosity for such cellulose solutions. The D.P. of the cellulose fibres used for the test was determined beforehand using the same method. Colour The coloured material in the solution was extracted into a known quantity of water, and then the optical density of this extract was measured using a Spekker Colourimeter with a blue filter and a 4.0 cm path length. The optical density (OD) measured was -then converted into the appropriate value for a volumetric dilution of the amine oxide by a factor of 100, and expressed as OD/100. Examples 1 to 4 Woop pulp (Saiccor double red band of D.P. 570), amine oxide (N-methyl morpholine N-oxide supplied by Texaco Inc.), water and any stabilising additive, were mixed to form a wet pulp mixture containing 0.7 per cent stabilising additive (Example 1), 11 per cent cellulose, 55 per cent amine oxide and 33.3 per cent water. For other additive levels (Examples 2, 3 and 4), the concen¬ trations varied in proportion. This mixture was heated under vacuum (14 cm Hg absolute) up to a temperature of 100°C in a glass vessel and held at that temperature for 4 hours. By the end of that period, the cellulose had gone into solution and water had evaporated off to give a final proportion of 15 per cent cellulose, 75 per cent amine oxide, 9 per cent water and 1 per cent stabilising additive (Example 1). Again, there was pro- portionate variation for Examples 2, 3 and 4, and for the control and comparative tests. The solutions obtained were examined for cellulose D.P., amine oxide yield and colour as described. In these Examples the stabilising additive used was disodium hydrogen phosphate in the concentrations specified, with comparative tests being carried out on a potential stabilising additive outside the scope of the invention, namely oxalic acid, again in the range of concentrations specified. The results are shown in the following Table A. Table A The results show that the disodium hydrogen phosphate is effective at all four concentrations against loss of amine oxide and substantially reduces loss of cellulose D.P. This is in contrast with the oxalic acid which, whilst preserving cellulose D.P. rather better, apparently accelerates amine oxide loss and generates substantial discolouration. Examples 7 to 13 The procedure of Examples 1 to 4 was repeated for the concentrations of phosphoric acid, sodium hexmetaphos- phate (S.H.M.P.) and hydroxy ethylidene disphosphonic acid (H.E.D.P.) specified in the following Table B:- OMPI Table B Stabi Using Additive o Yield of Cellulose Colour % in final solution Amine Oxide D.P. (OD/100) Control 0.0 99.0 290 0.015 Ex. 1 Na 2 H P0 4 1.0 99.9 453 0.010 Ex. 7 H 3 P0 4 1.0 100.0 460 0.008 Ex. 8 S.H.M.P. 1.0 100.0 457 0.005 Ex. 9 II 0.5 99.6 470 0.008 Ex. 10 II 0.3 99.4 425 0.010 Ex. 11 II 0.1 99.2 340 0.013 Ex. 12 H.E.D.P. 0.3 100.0 459 0.005 Ex. 13 II 0.1 99.6 438 0.009 Exampies 14 to 24 Solutions of cellulose in amine oxide and water were formed using the same proportions of those materials as specified in Examples 1 to 4 with varying levels of stabilising additives. However, in this case the mixing and solution process was carried out in a stainless steel pfleiderer mixer to more nearly simulate production con¬ ditions. The pfleiderer mixer was jacketed, and mixing was carried out at a jacket temperature of 80°C for 30 minutes and then at 100°C for a further two hours until solutions had formed. The mixer was under a vacuum of 7 cm Hg (absolute) throughout. These solutions were then analysed for cellulose D.P. as in previous Examples, and the results are shown in the following Table C. Amine oxide yield was not measured because of the diffi¬ culty of removing all of the sample solution from the pfleiderer mixer. OMPI Table C Solutions of cellulose in amine oxide and water were formed as described in Examples 14 to 24. At the 1 per cent stabilising additive level, the other concen¬ trations were cellulose 15 per cent, amine oxide 75 per cent, and water 9 per cent, with proportional variation for different additive levels. These solutions were analysed as in previous Examples, and were then transferred to separate glass vessels in which they were heated to various temperatures under a vacuum of 14 cm Hg (abs.) for 4 hours. A repeat analysis was then carried out on the solutions, and the results of the various heat treatments are shown in the following Table D. The amine oxide loss is expressed as a per cent loss per hour, and the cellulose loss is expressed in the same way, as well as on the bas'is of fall in D.P.. The colour rise in terms of OD/100 over the 4 hours is also shown. OMPI Table D Stabilising Additive Temp, 7β Amine Oxide % Cellulose D. P. Fall Colour Rise o final solution °C. Loss per Hour Loss per ( OD/100 ) Hour Control 0.0 100 0.34 0.63 300 -» 140 0.008 — > 0.087 0.0 110 0.85 1.05 300 -> 100 0.008 —v 0.16 0.0 120 1.47 2.56 0.008 -» very dark Ex. 25 H 3 P0 4 1.0 100 0.53 1 .68 388 - 198 0.00 — > 0.13 Ex. 26 " 1.0 110 1.59 2.13 388 - 177 0.00 — > 0.18 Ex. 27 S.H.M.P. 1.0 100 no 0.44 482 -> 449 measurable loss Ex. 28 " 1.0 110 0.04 0.59 482 - 338 0.00 ~> 0.05 Ex. 29 " 1.0 120 0.21 0.68 0.00 -> 0. 16 Ex. 30 " 0.3 110 no 396 → 228 measurable loss Examples 31 to 43 Sample solutions of cellulose in amine oxide and water were made according to the procedure described in Examples 1 to 4, with varying amounts of iron (as FeCl-,) and sodium hexametaphosphate being added to the samples at the start of the mixing/solution process. Control samples with no addition of sodium hexametaphos¬ phate were made at various iron levels. The solutions formed contained approximately 75 per cent amine oxide, 15 per cent cellulose with the remainder being water and iron and sodium hexametaphosphate as appropriate. The solution samples were analysed for cellulose D.P., amine oxide yield and colour as described previously and the results are shown below in Table E. These show that degradation of both amine oxide and cellulose appears to increase with increasing iron content. The original D.P. of the cellulose was 580. •-3 ti¬ er t-* as m - ετ

Claims: CLAIMS 1. A solvent for organic polymers comprising a hydrated tertiary amine N-oxide characterised by incorpor¬ ation therein as a stabilising additive of one or more compounds selected from phosphoric acids, phosphate salts, phosphonic acids, phosphonate salts, and complexes of any of the foregoing with occluded metal ions. 2. A solvent as claimed in claim 1 characterised in that the stabilising additive comprises sodium hexa¬ metaphosphate or a complex of occluded metal ions there- with. 3. A solvent as claimed in claim 1 characterised in that the stabilising additive comprises one or more compounds selected from disodium hydrogen phosphate, potassium dihydrogen phosphate, hydroxyethylidene diphos— phonic acid, aminoethyl diphosphonic acid, and complexes of any of the foregoing with occluded metal ions. 4. A solvent as claimed in claim 1 characterised by incorporating up to 3.0 per cent by weight of the stabilising additive. 5. A solvent as claimed in claim 4 characterised by incorporating 0.1 to 1.0 per cent by weight of the stabilising additive. 6. A solvent as claimed in claim 1 characterised by incorporating an organic polymer dissolved therein. 7. A solvent as claimed in claim 6 characterised in that the organic polymer comprises cellulose. 8. A solvent as claimed in claim 1 characterised in that the hydrated tertiary amine N-oxide is a cyclic compound. 9. A solvent as claimed in claim 8 characterised in that the hydrated tertiary amine N-oxide comprises N-methyl morpholine N-oxide. 10. A process for making a shaped article of an organic polymer comprising dissolving the organic polymer in a solvent comprising a hydrated tertiary amine N-oxide to form a solution of the polymer, shaping the polymer solution and coagulating the shaped solution to form the desired shaped polymer article, characterised by incorporating in the solvent prior to the shaping step a stabilising additive which comprises one or more of the compounds comprising phosphoric acids, phosphate salts, phosphonic acids, phosphonate salts, and complexes of any of the foregoing with occluded metal ions. 11. A process as claimed in claim 10 characterised in that the polymer solution is shaped into the form of fibres or film. 12. A process as claimed in claim 10 characterised in that the organic polymer is cellulose and is present in the polymer solution in a concentration of 5 to 35 per cent by weight. 13. A process as claimed in claim 10 characterised in that the stabilising additive comprises sodium hexa¬ metaphosphate or a complex of occluded metal ions there- with. 14. A process as claimed in claim 10 ' characterised in that the polymer solution has a water content of 1 to 30 per cent by weight. 15. A process as claimed in claim 14 characterised in that the solvent comprises N-methyl morpholine N-oxide and the polymer solution has a water content of 5 to - 16 - 20 per cent by weight. 16. A process as claimed in claim 14 characterised in that the solvent used to dissolve the polymer has a water content in excess of that required to give the 5 specified water content of the polymer solution and that excess water is removed from the polymer solution prior to the shaping step. O P

Inventors: LAITY PETER RAFFAELE, LAITY, PETER, RAFFAELE
Applicants: COURTAULDS PLC
Application year: 1983
Main classification: C08J3
IPC codes: C08J3, C08L1