FEED COMPOSITION EXHIBITING IMPROVED PELLETING CHARACTERISTICS, LIGNOSULFONATE BASED PELLETING AID AND A PROCESS FOR ITS PREPARATION

Abstract: Feed composition exhibiting improved pelleting charac­ teristics and including a lignosulfonate based pelleting aid, which aid contains dried, substantially water soluble, through oxidative crosslinking and/or aldehyde coupling modified sulfonated lignins containing material, especially thus modified calcium, magnesium, sodium and/or ammo­ nium based sulfite spent liquor, and which aid exhibits a viscosity of not more than 10 000 Cp measured in a 25% by weight aqueous solution at 23°C. The invention also relates to a new pelleting aid which contains dried, substantially water soluble, sulfonated lignins containing material which has been modified by oxidative crosslinking, for example using hydrogen peroxide, in the presence of a salt or a complex salt of a metal ion which capable of existing in several different valency states, for example a cyanoferrate (II) or -(III) salt, as an activator, and which exhibits a viscosity of not more than 10 000 cP measured as above. The invention further relates to the process for preparing the pelleting aid according to the invention.

Description: Feed composition exhibiting improved pelleting characteristics, lignosulfonate based pelleting aid and a process for its preparation This invention relates to new feed compositions ex exhibiting improved pelleting characteristics, to a ligno sulfate based pelleting aid for the pelleting of animal feed ratipns, as well as to a process for the preparation of such an aid. In recent years extensive research has been devoted to developing processes and equipment by means of which various kinds of finely divided feed ingredients, solids and liquids may be combined to nutritionally beneficial and mechanically durable pellets and other artificially cubed feed preparations of maximal palatability and easy handling characteristics. It is known that the pelletibility characteristics vary considerably for different feedstuffs and feed compositions. Despite advances in pelleting technique, only few feed rations lend themselves to pelleting without the inclusion of a pelleting aid. Pelleting aids either improve the mechanical durability of the pellet andJor facilitate the output of the pelleting machinery. At this time animal feedstuffs pelleting is a well established large scale industrial process comprising the following steps: - milling, in which the feedstuffs are ground to the desired fineness, - mixing, in which the various feed components and the pelleting aid of choice are well intermingled, - conditioning, in which the temperature and/or the moisture of the feed mix is raised to a predeter mined level, normally using steam, - pelleting, in which the feed mix is combined by forcing the mix through the openings of a pel leting die, and sizing the extrudate into pellets of the desired length, - cooling, in which the temperature of the pellets is reduced in an air current, whereby simultane ously the pellets undergo a drying process, - crumbling, in which the pellets, if desired, are crushed to smaller sized particles. As a rule, cubed rations represent a compromise between nutritional, cost and pelletibility considerations. The nature and amount of pelleting aid employed is generally a crucial factor for producing optimal pellet quality for mixes of least cost. Numerous different kinds of pelleting aids have been proposed, cf. for example US patent specification 3,035,920 and FI patent specifications 40,509, f'-b35 and 56,925. None of these have proved satisfactori- and their drawbacks are well recognized. Clay and lignosui- fonate based pelleting aids and mixtures thereof cover more than 90% of the market today for reasons of their low price and ready availability. Their principal shortcoming is, however, that they require an inclusion rate in the feedstuff of 1.5 to 4% by weight and more, based on the dry weight of the rations, to achieve the desired pelleting effect. Steam quality and availability as well as the choice of the die employed with regard to thickness, hole design and diameter, material composition and state of wear, often prove limiting in that even high amounts of conventional pelleting aids do not afford a durable pellet. When producing rations of lower feed value, inclusion rates of 1.5 to 4% of pelleting aid are for all practical purposes acceptable. For compositions of higher feed value inclusion rates of 1.5 to 4% are both impractical and costly, because the loss in feed value incurred by the inclusion of the pelleting aid has to be made up by more expensive ingredients of higher feed value. These in turn often make for a more difficult cubing of the ration. Inclusion rates of more than 1.58 clay are problematic also from a nutrional point of view-because clays tend to irreversibly bind micro-nutrients. On the other hand, feeds containing 1.5% or more of lignosulfonates tend to give rise to diarrhea in monogastric animals and also affect disadvantageously the palatability of the feed, even to the extent that the animal rejects the feed. By means of the present invention the afore mentioned drawbacks have been largely overcome. The feed compositions incorporating the lignosulfonate pelleting aid in accordance with the invention can be cubed to pellets of substantially improved cohesiveness, durability and resiliency, and the invention thus allows for a substantial reduction of the amount of pelleting aid to be employed in the ration. This in turn results in an elimination of the harmful side effects incurred by the inclusion of high binder levels. Owing to the improved cohesiveness of the feed composition also the hitherto very critical factors, like steam conditioning and die choice, assume secondary significance, which results in lower cost pelleted feed rations. The invention thus relates to a feed composition exhibiting improved pelleting characteristics and containing a lignosulfonate based pelleting aid, which composition is characterizied in that it as the pelleting aid contains dried, substantially water soluble, sulfonated lignins containing material, which has been modified by oxidative crosslinking, and/or coupling with an aldehyde and which exhibits a viscosity of not more than 10 000 cP, measured in a 25% by weight aqueous solution at 23-C. The invention also relates to a new lignosulfonate based pelleting aid for the cubing of feed rations, which pelleting aid is characterizied in that it contains dried, substantially water soluble, sulfonated lignin containing material, which has been modified by oxidative crosslinking and which exhibits a viscosity of not more than 10 000 cP when measured in a 258 aqueous solution at 23 C. The invention further relates to a new process for preparing the above defined pelleting aid, which comprises oxidative crosslinking of a sulfonated lignins containing material in an aqueous solution, using as a redox activator or catalyst a salt or a complex salt of a metal ion which is capable of existing in En'L e t.an one valency state, and the crosslinking reactions is interrupted short of gelling or insolubilization of the reaction product, and the product obtained is dried. The feed compositions according to the invention contain preferably at least 0.05% by weight, advantageously 0.2 to 0.6% by weight, of the crosslinked pelleting aid. The oxidative crosslinking or oxidative coupling reaction comprises a dehydrogenative polymerization reaction, described i.a. by K. Sarkanen in LIGNINS edited by Sarkanen and Ludwig, Wiley-Interscience, as well as by H.H. Nimz et al. in Applied Polymer Symposium No. 28, 1225-1230 (1976), John Wiley & Sons Inc. The DE-patent specification 2 221 353 discloses, on the other hand, oxidative crosslinking of sulfonated lignins present in spent sulfite liquor for gluing particle boards and like wood products, using as oxidant hydrogen peroxide in the presence of a cyanoferrate (II) or cyanoferrate (III) redox catalyst. Oxidative coupling of sulfonated lignin containing material under such conditions readily leads to the formation of insoluble products, as in the process described in DE-patent specifi cation 2 221 353. Such insoluble products are, however, unsuitable for the purpose of this invention. Hydrogen peroxide treatment in the absence of redox catalysts constitutes a well known procedure for improving specific properties of sulfonated lignins, cf U.S.patent 3,476,740, but such treatment does not bring about the product characteristics desired for the practice of our invention. Acid-catalyzed condensations of lignosulfonates, on the other band, with formaldehyde or other aldehydes are known to lead to crosslinked or water soluble product. Such crosslinked products have been observed to enhance the dispersing and flocculation characteristic- of lignosulfonates, cf. U.S.-patent 3,600,308 4,332,589. A prerequisite for the feed compositions according to the invention exhibiting improved pelleting characteristics is that the modified lignosulfonate based pelleting aid can be dried from its aqueous solution to a fine powder, which is substantially water soluble and slightly hydroscopic, and exhibits an increased viscosity, however, of not more than 10 000 cP as measured at 23 C in a 25% by weight aqueous solution with a Brookfield viscosimeter. As a starting material for the crosslinking or coupling reaction for obtaining the improved pelleting aid is preferably used a calcium, magnesium, sodium or ammonium based sulfite spent liquor, or a mixture thereof, which optionally has been enriched in lignosulfonate solids, e.g. by removing carbohydrates, for example by fermentation or ultrafiltration. While such lignosulfonate starting materials, which have a high ratio of lignosulfonates to other solids, have been found to best respond to the purposes of the invention for the preparation of a substantially water soluble crosslinked product, it should be understood that also ordinary spent sulfite liquors are suitable for obtaining the products beneficial for the pelleting of feed ration. The concentration of the lignosulfonate containing starting material is not critical, but for practical purposes it is advantageous to use an about 45 to 55% solids furnish at the start of the reaction and to gradually add water when the crosslinking reaction proceeds and the viscosity builds up. The viscosity of an untreated furnish at 25% solids level is generally of the order of 5 to 6 cP. The crosslinking reactions are carried out in aque-ous solution. Two different coupling mechanisms have^ been found useful and economically viable. The first one, which is also an object of this invention involves oxidative dehydrogenation using as an oxidant advantageously hydrogen peroxide, or other peroxide compounds or salts thereof, and a redox catalyst comprised of a salt or complex salt of a metal ion, which is capable of undergoing valency change, at acidic, neutral or basic pH values of the system. An especially suitable mode for the preparation of the oxidatively crosslinked pelleting aid according to the invention is such wherein hydrogen peroxide is used as the oxidant under slightly acidic, pH 3 to 6,- condi- tions in the presence of catalytic amounts of a cyanoferrate (II) or cyanoferrate (III) salt, or in the presence of the corresponding complexes of cobolt and nickel. Such procedure is operative at pH values prevailing for commonly available sulfite spent liquor preparations and furthermore leads to no precipitation problems incurred, for instance, by adding sulfuric acid to calcium based liquors for the purpose of reducing the pH. While cyanoferrate (III) salts are considered toxic, they apparently convert to non-toxic cyanoferrate (II) salts towards the end of the reaction when the temperature and pH of the reaction medium is raised. Toxicology tests on rats and mice namely surprisingly show that the LD50-values of an untreated lignosulfonate material and a pelleting aid made with cyanoferrate (III) salts do not differ from each other. The aids according to this process may thus quite safely be used for the feeding of animals (LD50 > 10 g/kg body weight). As metal salt activators also other metal salts may be used, e.g. ferri- and ferrosulfates, provided, however, that the metal ion is such which under the influence of an oxidant is capable of valency change in the system, and that such metal ion forms a complex with sulfonated liqnin to prevent decomposition of hydrogen peroxide. The metal salt can be added directly to the sulfonated lignin containing medium or can be precomplexed with such material. As suitable peroxide compounds may be mentioned, besides hydrogen peroxide, for example Na202 as well as Na2S205 or K2S208 as well as their corresponding acids. When hydrogen peroxide is the oxidant it is suitably employed in an amount of about 1 to 10% by weight (calculated as 100%) based on the dry weight of the lignosulfonate material to be crosslinked, or an equivalent amount of other peroxide compounds, although these amounts are not critical. A suitable amount of activator is about 0.1 to 1.5% by weight, advantageously less than 1.0% by weight based on the dry solids of the lignin containing furnish. The oxidative crosslinking reaction is exothermic. To prevent decomposition of heat and metallic ion sensitive hydrogen peroxide, it is therefore best to keep the reaction mixture close to room temperature by cooling, and to limit the metallic ion content to a maximum of one percent of reaction solids if a metal salt activator is used rather than a strong complex of the latter. The second useful coupling mechanism for obtaining pelleting aids usable in the feed compositions according to the invention, is based on crosslinking with an aldehyde in aqueous solution. As an aldehyde preferably a lower aliphatic aldehyde, such as formaldehyde or a substance forming the same, such as paraformaldehyde, or acetaldehyde is used. Also other types of aldehydes known for this purpose may be employed, such as furfural aldehyde and/or acrolein. For reason of availablity and cost, preferably formaldehyde is used. The aldehyde crosslinking reaction is carried out at an acidic pH-value, i.e. at a value below 7, and preferably at a value below pH 3. It is immaterial in this case whether the reaction is carried out so that the lignosulfonate in a first step is reacted with the aldehyde at basic pH-values, advantageously at a pH-value of about 10 to 12, and in a second step is subjected to condensation at an acidic pH-value, or whether the reaction is conducted in one single step at an acidic pHvalue. The reaction is advantageously conducted, as stated above, employing a rather concentrated, suitably a 45 to 55 percent lignsulfonate solution, as well as at a raised temperature, such as at 40 to 180'C, for practical reasons advantageously about 90'C. The exact concentration of aldehyde in the solution is not critical and a suitable amount is about 1 to 4% by weight (calculated as 100%) based onlignosulfonate dry solids. Essential in both these modifying processes is that the crosslinking reactions are interrupted before the product forms a gel or turns insoluble. In the preliminary gelling stage the products are still water soluble, but when the gels age they turn insoluble and unsuitable for the purposes of the invention. The crosslinking reaction may be stopped in several different ways. Limiting the amount of coupling agent employed is the most effective means of preventing gel formation. However, crosslinking may also be stopped for any desired degree, for instance, by raising the pH of the system in case of aldehyde coupling or raising the temperature, in the case of oxidative coupling. Diluting the reaction mixtures with starting furnshes or even with water are also acceptable means for bringing the reactions to a halt, as is the addition of sodium bisulfite which reacts with hydrogen peroxide and aldehydes. The crosslinking reactions give rise to a viscosity increase which in turn affords a simple means for monitoring the coupling progress and for determining the point for interrupting the reaction, as well. as for defining the products. In general it can be said that pelleting aids exhibiting a viscosity in the range of 75 to 500 cP, as measured in a 25% by weight aqueous solution at 23 C, are suitable for the purpose of the invention, giving good cohesion at inclusion levels of about 0.2 to 0.68 by weight of the ration. Pelleting aids exhibiting a viscosity of about 5000 to 10 000 cP are of limited applicability and require high temperature and moisture levels to become active, i.e. strong conditioning of the feed mix. Pelleting aids of low viscosity, about 5 to 50 cP, on the other hand, require inclusion rates of about 0.8 to 1.5% by weight for good cohesion of most feed compositions. No difference in cohesiveness has been observed for products of similar viscosity but crosslinked in different manner. The viscosity of the crosslinked, sulfonated lignins containing material may, when desired or when necessary, be adjusted downwards to any desired value by adding to the crosslinked product untreated lignosulfonate containing material in suitable amounts, provided, however, that the viscosity of the final pelleting aid is below 10 000 cP when measured in a 25% aqueous solution at 23 C. The crosslinked, sulfonated lignins containing material may advantageously be combined also with ordinary inert carriers, such as clay, talcum, calcium carbonate or gypsum without its good pelleting characteristics suffering. The inclusion of untreated lignosulfonate and/or inert carrier then takes advantageously place before drying the crosslinked product, but can take place also after drying. The pH of the obtained products may, if desired, be adjusted by adding an acid or a base. The pH of the products used for the pelleting of feed compositions is preferably within the range of 2.5 to 11.0, as measured in a 5% aqueous solution. The expression "crosslinked, sulfonated lignins containing material" in this specification and claims means any material containing sulfonated lignins and having been partly or totally subjected to either a oxidative crosslinking reaction using an oxident in the presence of a redox catalyst or acid catalysed crosslinking with an aldehyde for the production of substantially water soluble products exhibiting an increased viscosity. Crosslinking leads to the loss of hydroxylic functions and to steric shielding of groups participating in the formation of hydrogen bridges. - Our finding that the cohesiveness of a feedstuffs composition can be substantially improved by adding thereto a crosslinked, sulfonated lignins containing, substantially water soluble material is thus surprising also in view of the fact that the ability to form hydrogen bridges has been considered an essential feature of pelleting aids. By way of explanation, we therefore venture the following comment. Before pelleting the steam supplied during the conditioning process reacts with the pelleting aid and tends to more or less liquify the same because of its hygroscopic nature. If the viscosity of the steamed and thus liquified lignosulfonate is too high it will not spread and give rise to thick and discontinuous glue lines. If, on the other hand, the viscosity of the liquified lignosulfonate is too low the material will penetrate into the feed and give rise to starved joints. Our crosslinked lignosulfonates therefore also offer the compounder the opportunity to match his pelleting aid requirement to his conditioning system. The following non-limiting Examples illustrate the invention; the viscosity has been measured with a Brookfield viscosimeter in an 25% aqueous solution at 23 C, and the pH has been measured in a 5% aqueous solution. Example I To 150 tons of concentrated (53*) for alcohol fermented calcium based spruce sulfite spent liquor of pH 4.5, was added 800 kg of ferrosulfate, Fe2SO4 7H2O, and 17 000 kg of hydrogen peroxide (40%) at 25-C. The batch was divided into three equal lots to yield three different pelleting aids as follows: Pelleting aid EA One third of the above batch was allowed to stand for 36 hrs under periodic cooling to keep the temperature below 35 C, After this time the reaction mixture was on the point of gelling and it was watered down with 20 tons of water. The pH had dropped to 2.8 during the reaction and it was readjusted to 4.5 using a 50% sodium hydroxide solution and the temperature was raised to 90-C in preparation for spraydrying. After spraydrying in a Niro-type spraydrier, a finely divided, only slightly hygroscopic powder was obtained, which was completely soluble in water and which exhibited a viscosity of 8700 cP. Pelletinq aid IB¯ A second one-third of the above prepared batch was allowed to stand for 36 hrs as for example IA, after which was added 50 tons of the original untreated spent liquor, which had been diluted to a solids content of 40%. The subsequent treatment corresponded to that described in the Example IA. The spraydried product exhibited a viscosity of 75 cP. In substantially similar manner it is possible to adjust the viscosity of the end product to a value between that of the untreated spent liquor and the oxidatively crosslinked material by simply mixing together suitable amounts of spent liquor and reaction product. Pelletinq aid IC¯ To one third of the above mentioned batch was added 10 tons of water and the batch was left standing for 20 hrs with occasional cooling. Adjusting the pH to 4.5, raising the temperature to 90'C and spraydrying afforded a product exhibiting a viscosity of 580 cP. Example II Into a for alcohol fermented sulfite spent liquor according to Example I was added sufficient 50% sulfuric acid and solid sodium sulfate to adjust the pH to 3.5 and to precipitate virtually all calcium as calcium sulfate. To 48 tons of the filtered solution, having a solids content of 44% by weight owing to the diluting effect of the washing waters from the filter cake, was added 25 kg of potassium ferricyanide, K3Fe(CN)6, and 2000 kg of hydrogen peroxide (40%). The mixture was left standing for 10 hrs at 25 C with occasional cooling. 8 tons of water was added, whereafter the mix was divided into two equal lots, which were treated in the following manner to yield two different grade pelleting aids. Pelleting aid IIA Half of the above mentioned batch was left standing for still 2 hrs, whereafter the temperature was raised to 75 C and the pH adjusted to 8.8 using 50% sodium hydroxide solution. Thereafter the temperature was raised to 90'C, Spraydrying afforded a sodium based product exhibiting a pH of 8.5 and a viscosity of 40 cP. Pelletnq aid IIB Into the second half of the above mentioned batch was added still 1500 kg of hydrogen peroxide solution (40%) and after 3 hrs thereinto was puored 10 tons of water. The product appeared gel-like after 8 hrs, but redissolved readily when the temperature was raised to 75 C and sufficient sodium hydroxide solution was added to pH 8.8. The pH of the spraydried product was 8.5 and the viscosity 9500 cP. Example III Into 25 tons of for ethanol and protein fermented (PEKILO) calcium based spruce sulfite spent liquor, having a solids content of 46%, was added sufficient 50% sulfuric acid to adjust the pH to 3.2. The precipitated calcium sulfate was removed by filtering, whereafter to the filtrate was added 10 kg of potassium ferricyanide and 1000 kg of hydrogen peroxide solution (40%), whereby the mixture thickened within 2 hrs. The reaction mixture, having a solids content of 41% at this stage, was further watered down with 7 tons of water. Raising the temperature to 75 C and adding sufficient sodium hydroxide solution to pH 10.5 and spraydrying afforded a product exhibiting a pH of 10.4 and a viscosity of 240 cP. Example IV To 35 tons of magnesium based sulfite spent liquor exhibiting a pH of 3.3 and solids content of 53%, was added 150 kg of potassium ferrocyanide, K4Fe(CN)6 3H2O, and 4000 kg of hydrogen peroxide solution (408). The solution was continuously cooled to keep the temperature below 35 C, and it started to turn thick after 14 hours. It was diluted with 12 tons of water and its temperature and pH were adjusted to 75 C and 9.0, respectively. The spraydried product exhibited a pH of 8.2 and a viscosity of 25 cP. Example V This example illustrates the use of a water insoluble inert material as a carrier for an oxidatively crosslinked, water soluble, sulfonated lignins containing pelleting aid. To 50 tons of concentrated (53%) for alcohol fermented calcium based spruce sulfite spent liquor was added at 25 C sufficient 50% sodium hydroxide solution to raise the pH to 7.5. While continuously cooling 80 kg of potassium ferrocyanide was added and then 2000 kg of hydrogen peroxide solution (40%) and 30 tons of water. After a reaction time of 4 hrs, the viscosity of the solution was 35 cP. Then the temperature of the solution was raised to 85 C and 20 tons of finely divided talcum was added while continuously heating and stirring vigorously. Spraydrying afforded a finely divided, freely flowing powder having an ash content of about 55%. Example VI To 70 tons concentrated (50%) for alcohol fermented calcium based spruce sulfite spent liquor were added 2000 kg of 37% formaldehyde solution and sufficient sulfuric acid to give a pH of 2.5. The mixture was kept at about 90'C for 36 hrs after which the pH was raised to 5 using 50% caustic soda. Spray-drying yielded a product exhibiting a viscosity of 56 cP. Example VII To 30 tons of concentrated (47%) for ethanol and protein fermented (PEKILO) calcium based spruce sellfite spent liquor was added 1000 kg 37% formaldehyde sXlllFion and sufficient sulfuric acid to give a pH of 2.0@ The mixture was kept at 90'C for 27 hrs after which times it no longer contained free formaldehyde and gelled when taken to room temperature. To the hot mix was added 20 tons hot concentrated (558) calcium based birch sulfite spent liquor and the pH was raised to 4.5 using 50% caustic soda solution. The spray-dried product exhibited a viscosity of 240 cP. In order to demonstrate the improved cohesiveness of the feed compositions according to the invention, three different kinds of feed mixes were prepared employing inclusion rates of 0.1 to 1% by weight of the above prepared pelleting aids and, for purpose of comparison, also 38 by weight of a commercial calcium lignosulfonate feed binder. The feed mixes were pelleted under identical conditions. The pellets were compared in terms of hardness and resiliency by means of a Kahl hardness tester and by rotating the pellets for 3 minutes in a tumbler and recording the fines released from the pellets. The measurements were repeated three times and the samples were removed from the cooler, the first one in the beginning, the second one about half-way and the third at the end. Before measuring each sample was left standing for 30 minutes. In order to simplify the tests, the pelleting aids were added to the feed mixes as obtained in the above Examples. Naturally they may also be added together with a vitamin-tracer element-premix or with other feed ingredients or mixed with clays, die lubricants etc. Example A Pelleted dairy ration In a mixer 900 kg of ground barley, 600 kg of arevnd oats, 240 kg of dried distillers solubles, 500 kg of soybean meal, 490 kg of ground wheat, 75 kg of skiw,. ,'; powder, 75 kg of dicalcium phosphate, 25 kg of salt, 35 kg of ground lime stone, 10 kg of magnesium oxide and 10 kg of a vitamin-tracer element-premix were finely intermingled with the pelleting aid. The mixes then received 9% by weight of molasses and were fed to a Buhler Miag Dpab-type pelleting machine, where the temperature was raised to 67 C and the total moisture to 16.9% using steam. The mixture was then fed at the rate of 15 tons/hr through a die having an opening diameter of 8.5 mm. Thereafter the fines were removed by screening and the pellets were cooled and dried. In substantially similar manner the two following rations were prepared. Example B Pelleted broiler ration Pelleted broiler rations were prepared by mixing the pelleting aids into a mix of 44% by weight of ground barley, 25% by weight of ground wheat, 16% by weight of soybean meal, 4.5% by weight of herring meal, 3.28 by weight of fat, 3.08 by weight of ground oats, 2.08 by weight of feed yeast, 1.7% by weight of dicalcium phosphate, 0.5% by weight of calcium carbonate, 0.25% by weight of sodium bicarbonate and 0.7% by weight of a vitamin-tracer element-premix. The mix was fed to the conditioning chamber and steamed to 72 C, which raised the moisture level to 15.4%. The moist mash was then forced through a die having an opening diameter of 3.2 mm, at the rate of 3 tons/hr, whereafter the pellets were screened and cooled - Example C Pelleted ration for furred animals Pelleted rations for furred animals were prepared by mixing the pelleting aids with a mix of 30% by weight of pre-cooked wheat flour, 10% by weight of finely ground soyabean meal, 8% by weight of rapeseed oil, 48% by weight of herring meal and 2% by weight of a vitamintracer element-premix. To the mixes were added an additional 6% by weight of molasses and steamed to 70'C, which raised the total moisture content to 16.2%. The mixes were then fed to a Buhler DFPC-type pelleting machine and forced through a die having an opening diameter of 4.5 mm. Thereafter the feeds were screened and cooled in an analogous manner as described above. For the pelleted feed rations A to C produced employing the pelleting aids according to the above Examples I to VII, the hardness values and fines reported in the following Table were measured using the above mentioned test procedure. From the Table it is evident that compared to an ordinary calcium based lignosulfonate feed binder, good results are obtained with considerably smaller inclusion rates of the pelleting aids according to the invention. FEED COMPOSITION EMI18.1 A <SEP> B <SEP> C <tb> PELLETING <SEP> INCLUSION <SEP> HARDNESS <SEP> FINES <SEP> HARDNESS <SEP> FINES <SEP> HARDNESS <SEP> FINES <tb> AID <SEP> RATE <SEP> % <SEP> KG <SEP> % <SEP> KG <SEP> % <SEP> KG <SEP> % <tb> IA <SEP> 0.4 <SEP> 4.4 <SEP> 6.1 <SEP> - <SEP> 6.1 <SEP> 3.6 <SEP> 7.8 <tb> IA <SEP> 1.0 <SEP> - <SEP> - <SEP> - <SEP> - <SEP> 3.9 <SEP> 7.2 <tb> IB <SEP> 0.5 <SEP> 6.8 <SEP> 4.2 <SEP> - <SEP> 5.6 <SEP> 2.9 <SEP> 9.3 <tb> IB <SEP> 1.0 <SEP> 7.0 <SEP> 4.6 <SEP> - <SEP> 6.0 <SEP> 3.4 <SEP> 9.6 <tb> IC <SEP> 0.5 <SEP> 7.0 <SEP> 4.6 <SEP> - <SEP> 6.2 <SEP> 3.6 <SEP> 6.4 <tb> IC <SEP> 1.0 <SEP> 7.7 <SEP> 4.1 <SEP> - <SEP> 5.6 <SEP> 4.3 <SEP> 5.9 <tb> IIA <SEP> 0.5 <SEP> 7.2 <SEP> 4.8 <SEP> - <SEP> 6.3 <SEP> 3.2 <SEP> 9.5 <tb> IIB <SEP> 0.5 <SEP> 4.9 <SEP> 7.3 <SEP> - <SEP> 6.8 <SEP> 3.7 <SEP> 8.3 <tb> III <SEP> 0.2 <SEP> 6.9 <SEP> 4.8 <SEP> - <SEP> 5.8 <SEP> 3.4 <SEP> 6.6 <tb> III <SEP> 0.7 <SEP> 7.7 <SEP> 4.2 <SEP> - <SEP> 5.1 <SEP> 4.2 <SEP> 6.1 <tb> 1.0 <tb> IV <SEP> 0.3 <SEP> 7.4 <SEP> 4.5 <SEP> - <SEP> 6.1 <SEP> 3.3 <SEP> 9.2 <tb> V <SEP> 0.3 <SEP> 6.8 <SEP> 5.2 <SEP> - <SEP> 6.3 <SEP> - <SEP> VI <SEP> 0.5 <SEP> 7.3 <SEP> 4.8 <SEP> - <SEP> 6.8 <SEP> 3.2 <SEP> 8.8 <tb> VII <SEP> 0.2 <SEP> 7.3 <SEP> 4.2 <SEP> - <SEP> 6.0 <SEP> 3.2 <SEP> 6.4 <tb> VII <SEP> 0.7 <SEP> 7.5 <SEP> 4.3 <SEP> - <SEP> 4.9 <SEP> 3.9 <SEP> 5.8 <tb> control, <tb> standard <SEP> grade <SEP> 3.0 <SEP> 6.8 <SEP> 4.8 <SEP> - <SEP> 6.1 <SEP> 3.2 <SEP> 9.6 <tb> calcium <SEP> lignosulfonate <tb>

Claims: Claims: 1. Feed composition containing a lignosulfonate based pelleting aid, c h a r a c t e r i z e d in that it as the pelleting aid contains dried, substantially water soluble, sulfonated lignin containing material, which has been modified by oxidative crosslinking and/or coupling with an aldehyde, and which exhibits a viscosity of not more than 10 000 cP, measured in a 25% by weight aqueous solution at 23 C. 2. Feed composition according to the Claim 1, c h a r a c t e r i z e d in that it contains at least 0.05, preferably 0.2 to 0.68 by weight of the pelleting aid. 3. Feed composition according to the Claim 1 or 2, c h a r a c t e r i z e d in that the viscosity of the pelleting aid is 75 to 500 cP, measured in a 258 by weight aqueous solution at 23 C. 4. Feed composition according to any one of the previous claims, c h a r a c t e r i z e d in that the pH of the pelleting aid is 2.5 to 11 as measured in a 5% by weight aqueous solution. 5. Feed composition according to any one of the pre ceding claims, c h a r a c t e r i z e d in that as the oxtdant for the modification reaction, hydrogen peroxide is used in the presence of a cyanoferrate(II) or -(Ill) salt. 6. Feed composition according to any one of the claims 1 to 4, c h a r a c t e r i z e d in that as the aldehyde for the modification reaction, formaldehyde, or a substance forming the same, is used. 7. Feed composition according to any one of the pre ceedinc claims, c h a r a c t e r i z e d in that as sulfonated lignins containing material a calcium, sodium, magnesium or ammonium based sulfite spent liquor is used. 8. Lignosulfonate based pelleting aid for the pelleting of feed compositions, c h a r a c t e r i z e d in that it contains dried, substantially water soluble, sulfonated lignins containing material, which has been modified by means of oxidative crosslinking, and which exhibits a viscosity of not more than 10 000 cP, measured in a 25% by weight aqueous solution at 23 C. 9. Pelleting aid according to the Claim 8, c h a r a c t e r i z e d in that its viscosity is 75 to 500 cP. 10. Process for the preparation of a pelleting aid according to the Claim 8, c h a r a c t e r i z e d in that a sulfonated lignins containing material is crosslinked with an oxidant in an aqueous solution, using as a redox activator or catalyst a salt or a complex salt of a metal ion capable of existing in more than one valency state, and that the crosslinking reaction is interrupted short of gelling or insolubilization of the reaction product and the product obtained is dried. 11. Process according to the Claim 10, c h a r a c t e r i z e d in that as the oxidant, hydrogen peroxide in the presence of a cyanoferrate(II) or -(III) salt is used. 12. Process according to the Claim 10 or 11, c h a r a c t e r i z e d in that the crosslinking reaction is interrupted by limiting the amount of oxidant used or by destroying the oxidant.

Inventors: ASHORN, THEODORE H.G., KARJALAINEN, MATTI S., NYSTEN, BRYNOLF B.J.
Applicants: G.A. SERLACHIUS CORPORATION
Application year: 1983
Main classification: A23K1
IPC codes: A23K1