PAINT FORMULATIONS

Abstract: A low solvent paint formulation which is container storable has a spreadable functional medium which is diluted, to adjust the solids level, by a gas content present as a gas phase at atmospheric pressure. The gas phase is stably dispersed in the medium and sheds from the formulation when spread as a surface to leave a solidifable coating free of bubbles.

Description: TITLE: PAINT FORMULATIONS This invention relates to contoiner-storable paint formulations, which term is intended to include industrial finishes and inks which are container-storable for application as surface coverings. For a number of years there has been an effort to reduce the use of organic solvents (such as mineral or white spirit) in paints. It is acknowledged that such use involves cost, odour, fire risk, toxicity problems, pollution problems and possible misuse of irreplaceable natural resources. The toxicity problem becomes very acute for example when point, incorporating hydrocarbon solvents is used for covering large areas, like walls and ceilings, in places of poor ventilation as often occurs in house or office decoration. The pollution problem is also acute in industrially applied finishes. The above problems have been discussed in our Co- pending application published as US Pat. No. 4386171 (GB 2 077 746A) and one solution, using water dilution, is proposed therein. The present invention provides a further solution and provides scope for unpressurised formulations (and thereby avoids aerosol problems) and which either contain or do not contain water, the latter being signifi-t cant where the presence of water could limit the choice of otherwise preferred resins and driers. The present invention provides a container-storable point formulation having a prime content of spreadable functional medium characterised in that it has present as a gas phase at atmospheric pressure in excess of 5% by volume stably dispersed in said medium and which can shed from the formulation when spread on a surface to leave a solidifiable coating substantially free of bubbles. (The figure of 5% is referred to above as many known paints contain a minor, less than 5% gas content that arises normally in the production of the paint.) A combination of gas and water may be used to adjust the "solids" level of the formulation, or to aid the generation of stable gas or air dispersion. The formulatiom may be free of organic solvents or there may be a significantly reduced level of organic solvents (e.g. less than 10% by volume). The medium is preferobly of a thixotropic or non-newtonian nature and, as such, is capable of restraining the inherent forces of buoyancy of the gas acting to cause separation of the gas from the medium during storage. It has been found that most paint-familiar hydrocarbon solvents generally tend to act as defoamers and this provides one reason for their preferred avoidance. Where a necessity for some form of solvent arises it is preferred to use a polar solvent, such as glycol ethers which may be present up to 30% by volume. Where the formulation is to be used as a gloss paint the "conventional" level of about 30 - 70% oleoresinous volume solids can be employed. Yarying-the-gos content allows the adjustment of volume solids to a convenient level and so reduces or eliminates organic solvents. The gas content of the formulation is preferably introduced by a simple operation of mechanical aeration and this is most attractive when using ambient air as the gas content. Introduction by means of in-situ chemical reaction or in-situ heat or pressure release are also possibilities. Where ambient air could introduce undesirable oxygen reaction an inert gas such as nitrogen or carbon dioxide could be used. Alternatively additives, such as anti-skinning agents, could be included to suppress oxidation. To aid drying, where the spread formulation is to be air dried, drying agents such as the so-called "coordination driers" like certain aluminium compounds can be included. Such agents should not be required where the formulation is intended for use as a stoved industrial coating. Dry hydrochloric acid gas can be used to aid drying of an alkyd-based paint. In addition to the cost and other savings that arise from, effectively, substituting solvent with air, a further unexpected cost advantage arises. It has been found that organic solvents can tend to reduce opacity and this has to be made good with expensive opacifiers. The avoidance or reduction of organic solvents can correspondingly effect a saving in opacifiers. The gas inclusion also introduces an unexpected advantage with many decorative formulations in that it allows the use of higher molecular weight alkyd resins. Thus, gas-containing paints can be produced having a brushing character comparable with conventional organicsolvent-thinned paints of, say, 5 poise even though the viscosity is greater than this (e.g. 8 poise at 10,000 sex 1 at 250c). The use of higher molecular weight resins can improve drying times and other properties. The invention could also be applied to containerstored inks, such as litho inks, and adhesives with an encouraging avoidance or reduction of offensive solvents. Formulations according to the invention will now be given. Formulation No. 1 - White Gloss Paint Ti 02..... Bms . . . . . . . . . . . . . . . . . . . .350 gms Vehicle "A" (see below) ........250 gms Vehicle "B" (see below) ........250 gms Calcium as octoate (10%) .........5.0 gms Cobalt as octoate (8%) .........9.4 gms Lead as octoate (36%) ........34.7 gms The formulation was mechanically aerated and hod the following constituents: Volume Solids TiO2and vehicles "A" and "B" above ..........67% Air ...............................................................25% Organic Solvent ...........................................8% -l The viscosity after aeration was 13 poise at 10,000 sec at 25 C. Vehicle "A" is 100% N.V. (non-volatile) soya bean oil - viscosity 7 poise at 200C. Vehicle "B" is 100% N.V. thixotropic modified soya bean oil. Formulation No. 2 - Moisture-curing polyurethane wood primer *DESMODUR E21 100% N.V..........50 parts by weight *DESMODUR KL5-2550 100% N.V..........50 parts by weight Ti02 (dry) ..........70 parts by weight The formulation was mechanically aerated to give a solids content of 60% by volume and a dry air content of 40%. *Moisture-cured polyurethane resins ex Bayer of Germany and Registered Trade Marks. Formulotion No. 3 Titanium Dioxide .........................70 parts by weight *Alkyd Resin (92% N.V.) ...........109 parts by weight Calcium Octoate (10% N.V.) .............l 1 port part by weight Cobalt Octoate (8% N.V.) .............l 1 part part by weight Lead Octoate (36% N.V.) .............2 2 parts parts by weight Water ................................................10 parts by weight White Spirit 2 . . . ...............................2 parts by weight Sodium Sulphosuccinate .................. 1 part part by weight Viscosity at 10,000 sec at 25 C = 9 poise. The above paint was aerated by a mechanical aerator and the resultant product contained 38% air by volume. *Alkyd resin based on soya bean oil (69%) pthalic anhydride and pentaerythritol with 8% solvent, mono ethyl ether of ethylene glycol. Formulation No. 4 Titanium Dioxide .....................57 parts by weight Alkyd Resin (97% N.V.) ..............44 44 parts parts by weight Alkyd Resin II (98% N.V.) ................70 70 patrs parts by weight Aluminium Co-ordination Drier ........23 parts by weight Cobalt Octoate .......................1 1 part part by weight Viscosity of above paint at 10,000 sec-1 and 21 C was 8.0 poise. The above paint was mechanically aerated to give a product which contained approximately 35% air by volume. Alkyd Resin I based on Tall Oil Fatty Acid/ Trimellitic Anhdride/Trimethylol Propane. Alkyd Resin II is a thixotropic modification of Alkyd I. The paint contained 8.5% organic volatile by weight including White (Mineral) Spirit from the alkyd resin and organic volatiles combined with the co-ordination drier.

Claims: CLAIMS 1. A container-storable paint formulation having a prime content of spreadable functional medium characterised in that it has a gas content present as a gas phase at atmospheric pressure in excess of 5% by volume stably dispersed in said medium and which can shed from the formulation when spread onto a surface to leave a solidifiable coating substantially free of bubbles. 2. A formulation as claimed in claim 1 in which the medium is thixotropic. 3. A formulation as claimed in claim 1 or 2 having a hydrocarbon solvent content of less than 10% by volume or no hydrocarbon solvent. 4. A formulation as claimed in claim 3 also having a polar solvent to give a polar solvent content of less than 30% by volume. 5. A formulation as claimed in any preceding claim in which the gas is ambient air. 6. A formulation as claimed in any preceding claim including a gas which reacts with and contributes to the drying of the solidifiable coating. 7. A formulation as claimed in any preceding claim which is suitable for brush application and which has a -l viscosity at 10,000 sec 1 of greater than 8 poise at 250cm

Inventors: FOLEY, MICHAEL JAMES YATES, GRAHAM, THOMAS
Applicants: REED INTERNATIONAL P.L.C.
Application year: 1983
Main classification: C09D7
IPC codes: C09D7