ENERGY POLYMERIZABLE COMPOSITIONS CONTAINING ORGANOMETALLIC INITIATORS

Abstract: An energy polymerizable composition and process therefore, comprising a cationically polymerizable material and a catalytically effective amount of an ionic salt of an organometallic complex cation as polymerization initiator, said ionic salt of an organometallic complex cation being capable of adding an intermediate strength nucleophile or upon photolysis capable of liberating at least one coordina­ tion site, said metal in said organometallic complex cation being selected from elements of Periodic Groups IVB, VB, VIB, VIIB, and VIIIB are disclosed. Certain of the organometal­ lic metallic polymerization initiators are novel cationic salts.

Description: Technical Field The present invention relates to a process for the polymerization of cationically-sensitive cyclic ether materials employing as polymerisation initiator a certain class of ionic organometallic compounds. In another aspect, it relates to polymerizable compositions containing cationically-sensitive cyclic ether materials and organometallic complex compounds. In a further aspect, it relates to certain organometallic polymerisation initiators. Background Art The prior art describes various processes for the initiation of cationic polymerisation, particularly the polymerization of epoxy materials. It is known to cure epoxy materials by use of curing additives such as poly-basic anhydrides, organic peroxides, and quinone. It is further known that a metallocene, such as ferrocene, can be used as a curing accelerator for epoxy materials and is described in U.S. Patent No. 3,705,129. U.S. Patent Nos. 3,709,861 and 3,714,006 describe the use of cyclopentadienylmanganese tricarbonyl for the acceleration of the light-catalyzed reaction between polyepoxides and acid anhydrides or polymercaptans. U.S. Patent No. 3,867,354 discloses the use of bis- and tris-salicylic acid complexes of chromium(III) to catalyze the reaction between epoxides and carboxylic acids, and U.S. Patent No. 4,237,242 relates to the use of transition metal complexes (chromium, manganese, iron, etc.) of acetylacetonate type ligands to accelerate the thermally initiated reaction of carboxylic acid group-containing polymers with polyepoxides. Each of the above-mentioned patents teaches the acceleration of the reaction between polyepoxides and polyfunctional curing additives, but they do not teach the polymerization of epoxide group-containing compositions not containing a curing additive. The polymerization of cationically-polymerizable materials, specifically epoxide group-containing materials, in the absence of curing additives is, however, well known. Among such processes are those in which the polymerization catalyst (also called sensitizer or initiator) is (1) a radiation-sensitive onium salt of a Lewis acid (e.g. diazonium salts as are described in U.S. Patent No. 3,794,576 and U.S. Patent No. 4,080,274; halonium salts as are disclosed in U.S. Patent No. 4,026,705; and the onium salts of Group VIA elements, particularly the sulfonium salts, as are disclosed in U.S. Patent No. 4,058,400); (2) a dicarbonyl chelate compound of a Group IIIA-VA element as is disclosed in U.S. Patent No. 4,086,091; (3) a silver salt which is used for the polymerization of tetrahydrofuran as is described by Woodhouse, et al., J. Am. Chem. Soc. 100 , 996 (1978); and (4) titanocene dichloride which is used for the polymerization of epichlorohydrin and 2-chloroethylvinyl ether as is described by Kaerijama et al., J. Polym. Sci., Chem. Ed. 10 , 2833 (1972) and Ibid , 14 , 1547 (1976). Compositions containing the above-mentioned catalysts are unsatisfactory because without the addition of optical sensitizers they are limited to ultraviolet radiation for polymerization. Furthermore, the dicarbonyl chelates are moisture sensitive and the titanocene dichloride requires a co-catalyst. In addition, EP-A-0 094 914, an earlier patent document but published after the priority date of the subject patent and accordingly only available for the purposes of absolute verbal anticipation under Article 54(3) EPC, discloses certain organometallic ionic salts wherein the cationic portion contains a single transition metal atom and certain specific ligands for curing epoxides. Also EP-A-0 094 915, published on the same day as the '914 document mentioned above, discloses organometallic ionic salts for curing cationically polymerizable materials wherein the cationic portion of the salt contains certain specific transition metal atoms and specified ligands. Disclosure of the Invention The present invention provides a process for the polymerization of cationically-sensitive materials comprising a cyclic ether utilizing as catalyst a cationic compound which is a salt of an organometallic complex cation. By selection of the metal and ligands in the organometallic complex and the counterion used, the relative thermal stability and wavelength of sensitivity (from 200 to 600 nm) can be adapted for various applications. In accordance with the present invention there is provided an energy polymerizable composition comprising a cyclic ether, optionally 0.01 to 10 parts by weight per part of organometallic salt of a spectral sensitizer, and a catalytically effective amount of an ionic salt of an organometallic complex cation capable of adding a nucleophile intermediate in strength between hydride and chloride or upon photolysis capable of liberating at least one coordination site, wherein said ionic salt has the formula: [(L 1a ) (L 2a ) (L 3a )M a ]g[(L 1b ) (L 2b ) (L 3b )M b ] h [(L 1c ) (L 2c ) (L 3c )M c ]j[(L 1d ) (L 2d ) (L 3d )M d ] k (L⁴ ) (L⁵ ) (L⁶ ) +e X f I wherein M a , M b , M c , and M d each represents a metal selected from the elements of Periodic Groups IVB, VB, VIB, VIIB, and VIII; with the proviso that Formula I can represent a mononuclear, binuclear, trinuclear, or tetranuclear complex compound comprising M a , M a M b , M a M b M c , or M a M b M c M d respectively with their attendant ligands, L; L 1a , L 1b , L 1c , and L 1d each represents none, 1, 2, or 3 ligands contributing π-electrons that can be the same or different ligands selected from substituted and unsubstituted acyclic and cyclic unsaturated compounds and groups and substituted and unsubstituted carbo-cyclic aromatic and heterocyclic aromatic compounds, each capable of contributing two to twelve π-electrons to the valence shell of M a , M b , M c , and M d respectively; L 2a , L 2b , L 2c and L 2d each represents none or 1 to 6 ligands contributing an even number of σ-electrons that can be the same or different selected from mono-, di-, and tri-dentate ligands, each contributing 2, 4, or 6 σ-electrons to the valence shell of M a , M b , M c , and M d respectively; L 3a , L 3b , L 3c , and L 3d each represents none, 1 or 2 ligands contributing one σ-electron each to the valence shell of M a , M b , M c , and M d respectively; L⁴ represents none or 1 to 6 bridging ligands containing π-electrons that can be the same or different ligand selected from substituted or unsubstituted acyclic and cyclic unsaturated compounds and groups and substituted and unsubstituted carbocyclic aromatic and heterocyclic aromatic compounds, each capable of acting as a bridging ligand contributing 2 to 24 π-electrons to the valence shells of two or more metal atoms M a , M b , M c , or M d simultaneously; L⁵ represents none or 1 to 12 bridging ligands contributing an even number of σ-electrons that can be the same or different selected from mono, di, and tri-dentate ligands, each donating 2, 4, or 6 σ-electrons to the valence shells or two or more metal atoms M a , M b , M c , or M d simultaneously; L⁶ represents none or 1 to 12 bridging ligands contributing 1, 2, 3, or 4 σ-electrons to the valance shells of two or more metal atoms M a , M b , M c , or M d simultaneously; with the proviso that the total electronic charge contributed to M a , M b , M c , and M d by the ligands L 1a , L 2a , L 3a , L 1b , L 2b , L 3b , L 1c , L 2c , L 3c , L 1d , L 2d , L 3d , L⁴, L⁵, and L⁶ plus the sum of ionic charge on M a , M b , M c , and M d results in a residual net positive charge of e to the complex; e is an integer having a value of 1, 2, or 3, the residual electrical charge of the complex cation; X is a halogen containing complex anion of a metal or metalloid; f is an integer of 1 to 3, the number of complex anions required to neutralize the charge e on the complex cation, and g, h, j, and k independently are 0 or 1, with at least one of them being equal to 1; those compositions being excluded wherein either: a) said ionic salt is mononuclear, L 1a is an arene group or a dienylium group and each L 2a ligand is carbonyl, or b) said ionic salt is mononuclear or binuclear with identical transition metal atoms and each ligand thereof is a π-arene or the anion of a π-arene and the composition is free of spectral sensitizer. In another embodiment there is provided an energy polymerizable composition comprising a cyclic ether and a catalytically effective amount of an ionic salt of an organometallic complex cation capable of adding a nucleophile intermediate in strength between hydride and chloride or upon photolysis capable of liberating at least one coordination site, wherein said ionic salt has the formula: [(L⁷) (L⁸)M m ] +e X f II wherein M m represents a metal selected from elements of the Periodic Groups IVB, VB, VIB, VIIB, and VIII; L⁷ represents none, one, or two π-electron contributing ligands that can be the same or different ligand selected from substituted and unsubstituted acyclic and alicyclic unsaturated compounds and groups and substituted and unsubstituted carbocyclic and heterocyclic aromatic compounds, each capable of contributing two to twelve π-electrons to the valence shell of M m ; L⁸ represents none or 1 to 6 ligands that can be the same or different ligand selected from mono-, di-, and tri-dentate ligands, each contributing 2, 4, or 6 σ-electrons to the valence shell of M m ; with the proviso that the total electronic charge contributed to M m by L⁷ and L⁸ plus the ionic charge on M m results in a residual net positive charge of e to the complex; e is an integer having a value of 1, 2, or 3, the residual electrical charge of the complex cation; X is a halogen containing complex anion of a metal or metalloid; and f is an integer of 1 to 3, the number of complex anions required to neutralize the charge of e on the complex cation, those compositions being excluded wherein either: a) L⁷ is an arene group or a dienylium group and each L⁸ ligand is carbonyl, or b) each ligand of said ionic salt is a π-arene or the anion of a π-arene and the composition is free of spectral sensitizer. There is also provided a process for the polymerization of the particular permitted compositions mentioned above comprising the steps of: a) admixing the cyclic ether with a catalytically-effective amount of the permitted ionic salt of an organometallic complex cation, and b) curing the resulting admixture with at least one of a thermal and actinic radiation source. As used in this application. "catalytically effective amount" means a quantity sufficient to effect polymerization of the cationically-polymerizable material at least to a degree to increase the viscosity of the composition. Detailed Description of the Invention The ionic salts of the organometallic complex cations useful in the compositions and processes of the invention are compounds having the formula I or in a preferred embodiment formula II mentioned earlier. Salts of organometallic cations have Formulas I and II, are radiation sensitive in addition to being thermally sensitive. All ligands L 1a to L⁸ are well known in the art of transition metal organometallic compounds. Ligands L 1a , L 1b , L 1c , and L 1d in Formula I, and L⁷ in Formula II, are provided by any monomeric or polymeric compound having an accessible unsaturated group, i.e., an ethylenic, group; acetylenic, -C≡C- group; or aromatic group which have accessible π-electrons regardless of the total molecular weight of the compound. By "accessible", it is meant that the compound (or precursor compound from which the accessible compound is prepared) bearing the unsaturated group is soluble in a reaction medium, such as an alcohol, e.g., methanol; a ketone, e.g., methyl ethyl ketone; an ester, e.g., amyl acetate; a halocarbon, e.g., trichloroethylene; an alkane, e.g., decalin; an aromatic hydrocarbon, e.g., anisole; an ether, e.g., tetrahydrofuran; etc, or that the compound is divisible into very fine particles of high surface area so that the unsaturated group (including aromatic group) is sufficiently close to a metal atom to form a π-bond joining the unsaturated group to the metal atom. By polymeric compound, it is meant, as explained below, that the ligand can be a group on a polymeric chain. Illustrative of ligands L 1a , L 1b , L 1c , L 1d , and L⁷ are the linear and cyclic olefinic and acetylenic compounds having less than 100 carbon atoms, preferably having less than 60 carbon atoms, and up to 10 hetero atoms selected from nitrogen, sulfur, oxygen, phosphorus, arsenic, selenium, boron, antimony, tellurium, silicon, germanium, and tin, such as, for example, ethylene, acetylene, propylene, methylacetylene, 1-butene, 2-butene, diacetylene, butadiene, 1,2-dimethylacetylene, cyclobutene, pentene, cyclopentene, hexene, cyclohexene, 1,3-cyclohexadiene, cyclopentadiene, 1,4-cyclohexadiene, cycloheptene, 1-octene, 4-octene, 3,4-dimethyl-3-hexene, and 1-decene; η³-allyl, η³-pentenyl, norbornadiene, η⁵-cyclohexadienyl, η⁶-cycloheptatriene η⁸-cyclooctatetracene, and substituted and unsubstituted carbocyclic and heterocyclic aromatic ligands having up to 25 rings and up to 100 carbon atoms and up to 10 hetero atoms selected from nitrogen, sulfur, oxygen, phosphorus, arsenic, selenium, boron, antimony, tellurium, silicon, germanium, and tin, such as, for example, η⁵-cyclopentadienyl, η⁶-benzene, η⁶-mesitylene, η⁶-hexamethylbenzene, η⁶-fluorene, η⁶-naphthalene, η⁶-anthracene, η⁶-chrysene, η⁶-pyrene, η⁷-cycloheptatrienyl, η⁶-triphenylmethane, η¹²-paracyclophane, η¹²-1,4-diphenylbutane, η⁵-pyrrole, η⁵-thiophene, η⁵-furan, η⁶-pyridine, η⁶-γ-(picoline, η⁶-quinaldine, η⁶-benzopyran, η⁶-thiochrome, η⁶-benzoxazine, η⁶-indole, η⁶-acridine, η⁶-carbazole, η⁶-triphenylene, η⁶-silabenzene, η⁶-arsabenzene, η⁶-stibabenzene, η⁶-2,4,6-triphenylphosphabenzene, η⁵-selenophene, η⁶-dibenzostannepine, η⁵-tellurophene, η⁶-phenothiarsine, η⁶-selenanthrene, η⁶-phenoxaphosphine, η⁶-phenarsazine, η⁶-phenatellurazine, and n⁶-1-phenylborabenzene. Other suitable aromatic compounds can be found by consulting any of many chemical handbooks. As mentioned before, the ligand can be a unit of a polymer, for example the phenyl group in polystyrene, poly(styrene-cobutadiene), poly(styrene-comethyl methacrylate), poly(α-methylstyrene), polyvinylcarbazole, and polymethylphenylsiloxane; the cyclopentadiene group in poly(vinylcyclopentadiene), poly(η⁴-cyclopentadiene); the pyridine group in poly(vinylpyridine), etc. Polymers having a weight average molecular weight up to 1,000,000 or more can be used. It is preferable that 5 to 50 percent of the unsaturated or aromatic groups present in the polymer be complexed with metallic cations. Each of the ligands L 1a , L 1b , L 1c , L 1d , and L⁷ can be substituted by groups that do not interfere with the complexing of the ligand with the metal atom or which do not reduce the solubility of the ligand to the extent that complexing with the metal atom does not take place. Examples of substituting groups, all of which preferably have less than 30 carbon atoms and up to 10 hetero atoms selected from nitrogen, sulfur, oxygen, phosphorus, arsenic, selenium, antimony, tellurium, silicon, germanium tin, and boron, include hydrocarbyl groups such as methyl, ethyl, butyl, dodecyl, tetracosanyl, phenyl, benzyl, allyl, benzylidene, ethenyl, and ethynyl; hydrocarbyloxy groups such as methoxy, butoxy, and phenoxy; hydrocarbylmercapto groups such as methylmercapto (thiomethoxy), phenylmercapto (thiophenoxy); hydrocarbyloxycarbonyl such as methoxycarbonyl and phenoxycarbonyl; hydrocarbylcarbonyl such as formyl, acetyl, and benzoyl; hydrocarbylcarbonyloxy such as acetoxy, benzoxy, and cyclohexanecarbonyloxy; hydrocarbylcarbonamido, e.g., acetamido, benzamido; azo; boryl; halo, e.g., chloro, iodo, bromo, and fluoro, hydroxy; cyano; nitro; nitroso, oxo; dimethylamino; diphenylphosphino, diphenylarsino; diphenylstibine; trimethylgermane; tributyltin; methylseleno; ethyltelluro; and trimethylsiloxy; condensed rings such as benzo, cyclopenta; naphtho, indeno; and the like. Ligands L 2a , L 2b , L 2c , anti L 2d in Formula I, and L⁸ in Formula II are provided by monodentate and polydentate compounds preferably containing up to about 30 carbon atoms and up to 10 hetero atoms selected from nitrogen, sulfur, oxygen, phosphorus, arsenic, selenium, antimony, and tellurium, in addition to the metal atom, following loss of zero, one, or two hydrogens, the polydentate compounds preferably forming with the metal, M a , M b , M c , M d , and M m , a 4-, 5-, or 6-membered saturated or unsaturated ring. Examples of suitable monodentate compounds or groups are carbon monoxide, carbon sulfide, carbon selenide, carbon telluride, alcohols such as ethanol, butanol, and phenol; nitrosonium (i.e., NO⁺); compounds of Group VA elements such as ammonia, phosphine, trimethylamine, trimethylphosphine, triphenylamine, triphenylphosphine, triphenylarsine, triphenylstibine, tributylphosphite, isonitriles such as phenylisonitrile, butylisonitrile; carbene groups such as ethoxymethylcarbene, dithiomethoxycarbene; alkylidenes such as methylidene, ethylidene; suitable polydentate compounds or groups include 1,2-bis(diphenylphosphino)ethane, 1,2-bis(diphenylarsino)ethane, bis(diphenylphosphino)-methane, ethylenediamine, propylenediamine, diethylenetriamine, 1,3-diisocyanatopropane, and hydridotripyrazolylborate; the hydroxycarboxylic acids such as glycollic acid, lactic acid, salicylic acid; polyhydric phenols such as catechol and 2,2'-dihydroxybiphenyl; hydroxyamines such as ethanolamine, propanolamine, and 2-aminophenol; dithiocarbamates such as diethyldithiocarbamate, dibenzyldithiocarbamate; xanthates such as ethyl xanthate, phenyl xanthate; the dithiolenes such as bis(perfluoromethyl)-1,2-dithiolene; aminocarboxylic acids such as alanine, glycine and o-aminobenzoic acid; dicarboxylic diamides such as oxalamide, biuret; diketones such as 2,4-pentanedione; hydroxyketones such as 2-hydroxyacetophenone; α-hydroxyoximes such as salicyladoxime; ketoximes such as benzil oxime; and glyoximes such as dimethylglyoxime. Other suitable groups are the inorganic groups such as, for example, CN⁻, SCN⁻, F⁻, OH⁻, Cl⁻, Br⁻, I⁻, and H⁻ and the organic groups such as, for example, acetoxy, formyloxy, benzoyloxy, etc. As mentioned before, the ligand can be a unit of a polymer, for example the amino group in poly(ethyleneamine); the phosphino group in poly(4-vinylphenyldiphenylphosphine); the carboxylic acid group in poly(acrylic acid); and the isonitrile group in poly(4-vinylphenylisonitrile). Suitable radicals L 3a , L 3b , L 3c , and L 3d in Formula I include any group having in its structure an atom with an unshared electron. Suitable groups can contain any number of carbon atoms and hetero atoms but preferably contain less than 30 carbon atoms and up to 10 hetero atoms selected from nitrogen, sulfur, oxygen, phosphorus, arsenic, selenium, antimony, tellurium, silicon, germanium, tin, and boron. Examples of such groups are hydrocarbyl groups such as methyl, ethyl, propyl, hexyl, dodecyl, phenyl, tolyl, etc.; unsaturated hydrocarbyl groups such as vinyl, allyl, butenyl, cyclohexenyl; the hydrocarbyl derivatives of a Group IVA element such as trimethylgermanium, triphenyltin, and trimethylsilyl, etc.; and organic groups such as formyl, acetyl, propionyl, acryloyl, octadecoyl, benzoyl, toluenesulfonyl, oxalyl, malonyl, o-phthaloyl. Ligand L⁴ in Formula I is provided by any monomeric or polymeric compound having an accessible unsaturated group, such as an acetylenic, -C≡C- group or an aromatic group which have accessible π-electrons regardless of the total molecular weight of the compound. Illustrative of ligand L⁴ are the linear and cyclic diene and acetylenic compounds preferably having less than 60 carbon atoms and up to 10 hetero atoms selected from nitrogen, sulfur, oxygen, phosphorus, arsenic, selenium, boron, antimony, tellurium, silicon, germanium, and tin, such as for example, acetylene, methylacetylene, diacetylene, butadiene, 1,2-dimethylacetylene, 1,3-cyclohexadiene, cyclopentadiene, and 1,4-cyclohexadiene; η³-allyl, η³-pentenyl, norbornadiene, η⁵-cyclohexadienyl, η⁶-cycloheptatriene, η⁸-cyclooctatetracene, and substituted and unsubstituted carbocyclic and heterocyclic aromatic ligands having up to 25 rings and up to 100 carbon atoms and up to 10 hetero atoms selected from nitrogen, sulfur, oxygen, phosphorus, arsenic, selenium, boron, antimony, tellurium, silicon, germanium, and tin, such as, for example, η⁵-cyclopentadienyl, η⁶-benzene, η⁶-mesitylene, η⁶-hexamethylbenzene, η⁶-fluorene η⁶-naphthalene, η⁶-anthracene, η⁶-chrysene, η⁶-pyrene, η⁷-cycloheptatrienyl, η⁶-triphenylmethane, η⁵-pyrrole, η⁵-thiophene, η⁵-furan, η⁶-pyridine, η⁶- -picoline, η⁶-quinaldine, η⁶-benzopyran, η⁶-thiochrome, η⁶-benzoxazine, η⁶-indole, η⁶-acridine, η⁶-carbazole, η⁶-(1,2,3,4,4a,12a)-η⁶-(7,a,9,10,10a,10b)chrysene, η⁶-triphenylene, η⁶,η 6' -paracyclophane, η⁶,η 6' -1,4-diphenylbutane, η⁶-silabenzene, η⁶-arsabenzene, η⁶-stibabenzene, η⁶-2,4,6-triphenylphosphabenzene, η⁵-selenophene, η⁶-dibenzostannepine, η⁵-tellurophene, η⁶-phenothiarsine, η⁶-selenanthrene, η⁶-phenoxaphosphine, η⁶-phenarsazine, η⁶-phenatellurazine, and η⁶-1-phenylborabenzene. Other suitable aromatic compounds can be found by consulting any of many chemical handbooks. Each of the ligands L⁴ can be substituted by groups that do not interfere with the complexing of the ligand with the metal atom or which do not reduce the solubility of the ligand to the extent that complexing with the metal atom does not take place. Examples of substituting groups, all of which preferably have less than 30 carbon atoms and up to 10 hetero atoms selected from nitrogen, sulfur, oxygen, phosphorus, arsenic, selenium, antimony, tellurium, silicon, germanium, tin, and boron, include hydrocarbyl groups such as methyl, ethyl, butyl, dodecyl, tetracosanyl, phenyl, benzyl, allyl, benzylidene, ethenyl, and ethynyl; hydrocarbyloxy groups such as methoxy, butoxy, and phenoxy; hydrocarbylmercapto groups such as methylmercapto (thiomethoxy), phenylmercapto (thiophenoxy); hydrocarbyloxycarbonyl such as methoxycarbonyl and phenoxycarbonyl; hydrocarbylcarbonyl such as formyl, acetyl, and benzoyl; hydrocarbylcarbonyloxy such as acetoxy, benzoxy, and cyclohexanecarbonyloxy; hydrocarbylcarbonamido, e.g., acetamido, benzamido; azo; boryl; halo, e.g., chloro, iodo, bromo, and fluoro, hydroxy; cyano; nitro; nitroso, oxo; dimethylamino; diphenylphosphino, diphenylarsino; diphenylstibine; trimethylgermane; tributyltin; methylseleno; ethyltelluro; and trimethylsiloxy; condensed rings such as benzo, cyclopenta; naphtho, indeno; and the like. Ligand L⁵ is provided by monodentate and polydentate compounds preferably containing up to about 30 carbon atoms and up to 10 hetero atoms selected from nitrogen, sulfur, oxygen, phosphorus, arsenic, selenium, antimony, and tellurium. Examples of suitable monodentate compounds or groups are carbon monoxide, carbon sulfide, carbon selenide, carbon telluride, alcohols such as ethanol, butanol, and phenol; nitrosonium (i.e., NO⁺); compounds of Group VA elements such as triphenylamine, triphenylphosphine, triphenylarsine, triphenylstibine, isonitriles such as phenylisonitrile; suitable polydentate compounds or groups include 1,2-bis(diphenylphosphino)ethane, 1,2-bis-(diphenylarsino)ethane, bis(diphenylphosphino)methane, ethylenediamine, propylenediamine, diethylenetriamine, 1,3-diisocyanatopropane, and hydridotripyrazolyborate; the hydroxycarboxylic acids such as glycollic acid, lactic acid, salicylic acid; polyhydric phenols such as catechol and 2,2'-dihydroxybiphenyl; hydroxyamines such as ethanolamine, propanolamine, and 2-aminophenol; dithiocarbamates such as diethyldithiocarbamate, dibenzyldithiocarbamate; xanthates such as ethyl xanthate, phenyl xanthate; the dithiolenes such as bis(perfluoromethyl)-1,2-dithiolene, aminocarboxylic acids such as alanine, glycine and o-aminobenzoic acid; dicarboxylic diamides such as oxalamide, biuret; diketones such as 2,4-pentanedione; hydroxyketones such as 2-hydroxyacetophenone; α-hydroxyoximes such as salicyladoxime; ketoximes such as benzil oxime; and glyoximes such as dimethylglyoxime. Other suitable groups are the inorganic groups such as, for example, CN⁻, SCN⁻, F⁻, OH⁻, Cl⁻. Br⁻, I⁻, and H⁻ and the organic groups such as, for example, acetoxy, formyloxy, benzoyloxy, etc. Suitable radical L⁶ in Formula I includes any group having in its structure an atom with two or more unpaired electrons. Suitable groups can contain any number of carbon atoms and hetero atoms but preferably contain less than 30 carbon atoms and up to 10 hetero atoms selected from nitrogen, sulfur, oxygen, phosphorus, arsenic, selenium, antimony, tellurium, silicon, germanium, tin, and boron. Examples of such groups are hydrocarbyl groups such as methenyl, ethenyl, propenyl, hexenyl, dodecenyl, methinyl, and carbide. Suitable anions, X, in Formulas I and II, of use as the counterion in the ionic salts of the organometallic complex cation in the preferred radiation-sensitive compositions of the invention are those in which X has the formula DQ r , wherein D is a metal from Groups IB to VIII or a metal or metalloid from Groups IIIA to VA of the Periodic Chart of Elements, Q is a halogen atom, and r is an integer having a value of 1 to 6. Preferably, the metals are copper, zinc, titanium, vanadium, chromium, manganese, iron, cobalt, or nickel and the metalloids preferably are boron, aluminum, antimony, tin, arsenic, and phosphorus. Preferably, the halogen, Q, of Formula II, is chlorine or fluorine. Illustrative of suitable anions are BF₄⁻, PF₆⁻, AsF₆⁻, SbF₆⁻, FeCl₄⁻, SnCl₅⁻, SbF₅ = , AlF₆ = , GaCl₄⁻, InF₄⁻, TiF₆ = , ZrF₆⁻, etc. Preferably, the anions are BF₄⁻, PF₆ - , SbF₆⁻, SbF₅OH⁻, AsF₆⁻, and SbCl₆⁻. Most preferably, the anions are AsF₆⁻, SbF₆⁻, and SbF₅OH⁻. Some of the organometallic complex salts having these three anions are novel and all of these salts provide compositions of the invention that are relatively more active toward polymerization on exposure to energy than are salts having other anions. There are restrictions on the total sum of electrons donated by the ligands, L 1a , L 2a , L 3a , L 1b , L 2b , L 3b , L 1c , L 2c , L 3c , L 1d , L 2d , L 3d , L⁴, L⁵ and L⁶ of Formula I, L⁷ and L⁸ of Formula II, and the valence electrons possessed by the metal, M a , M b , M c , M d , M m , and M p . For most complex compounds not involving intramolecular metal-metal bonding, this sum is governed by the "eighteen electron rule" [see J. Chem. Ed. 46 , 811 (1969)] . This rule is sometimes called the "nine orbital rule", "the effective number rule", or the "rare gas rule". This rule states that the most stable organometallic compounds tend to be those compounds in which the sum of the electrons donated by the ligands and the metal is eighteen. Those skilled in the art, however, know that there are exceptions to this rule and that organometallic complex compounds having a sum of 16, 17, 19, and 20 electrons are also known. Therefore, ionic salts of organometallic complex cations not including intramolecular metal-metal bonding are described by Formulas I, and II in which complexed metal M a , M b , M c , M d , M m and M p have a total sum of 16, 17, 18, 19, or 20 electrons in the valence shell and a residual net positive charge of 1, 2 or 3 are included within the scope of the invention. For complex compounds described in Formula I in which intramolecular metal-metal bonding exists serious departure from the "eighteen electron rule" can occur. It has been proposed [ J. Amer. Chem. Soc. 100 , 5305 (1978)] the departure from the "eighteen electron rule" in these transition metal complexes is due to the metal-metal interactions destabilizing the metal p orbitals to an extent to cause them to be unavailable for ligand bonding. Hence, rather than count electrons around each metal separately in a metal cluster, cluster valence electrons (CVE) are counted. A dinuclear complex, M a M b , is seen to have 34 CVEs, a trinuclear complex, M a M b M c , 48 CVEs, and a tetranuclear complex, M a M b M c M d , having tetrahedron, butterfly, and square planar geometry is seen to have 60, 62, or 64 CVEs, respectively. Those skilled in the art, however, know that there are exceptions to this electron counting method and that organometallic complex cluster compounds having a sum of 42, 44, 46, 50 CVEs for a trinuclear complex and 58 CVEs for a tetranuclear complex are also known. Therefore, ionic salts of di, tri, or tetranuclear organometallic complex cations are described by Formula I in which the complexed metal cluster, M a M b , M a M b M c , or M a M b M c M d has a total sum of 34; 42, 44, 46, 48, 50; or 58, 60, 62, 64 CVEs in the valence shell, respectively, and a residual net positive charge of 1, 2, or 3 are included within the scope of this invention. Suitable organometallic complex ionic salts described by Formulas I and II, of use in the compositions of the invention are those salts that upon application of sufficient energy, either thermal or electromagnetic radiation having a wavelength from about 200 to 600 nm, will generate an active species capable of initiating cationic polymerization. The level of cationic activity will, of course, depend on the choice of metal, ligands, and counterions in the salt. Suitable ionic salts that are activated by heat to initiate cationic polymerization are those that will add a nucleophile intermediate in strength between hydride and chloride such as substituted or unsubstituted trialkyl- add triarylphosphines (preferably triphenylphosphine), trialkyl- add triarylphosphites, pyridines, and anilines. Examples of such compounds are described in Tetrahedron 34 , 3047 (1978) and "Carbonium Ions" 5 , Chapter 37, 1976, Wiley-Interscience, New York. These reviews contain references to the experimental procedures used to determine if a particular compound will add such a nucleophile. Suitable ionic salts that are activated by electromagnetic radiation to initiate cationic polymerization are those that upon photolysis liberate at least one coordination site on the metal. The ability to liberate at least one coordination site upon photolysis can be verified by doing a ligand exchange experiment. In such an experiment, the compound [(L 1a )(L 2a )(L 3a )M a ] g [(L 1b )(L 2b )(L 3b )M b ] h [L 1c )(L 2c )(L 3c )M c ] j [(L 1d )(L 2d )(L 3d )M d ] k (L⁴)(L⁵)(L⁶) +e X f I is photolyzed in the presence of a potential entering ligand L (L can be of the L¹ or L² types). That L has indeed added or exchanged with at least one ligand L¹ to L⁶ of Formula I can be determined by any number of analytical techniques. It is particularly convenient for this determination to use some spectroscopic technique to monitor the reaction before, during, and after photolysis. If L or at least one of the L 2a , L 2b , L 2c , L 2d , or L⁵ ligands is carbon monoxide, then infrared spectroscopy is a well suited technique to monitor the reaction. Otherwise UV/visible or NMR spectroscopy can be employed. The spectrum before photolysis can be compared with that taken after completion of the reaction to determine if the suspected ligand substituted product is present. A more rigorous method would involve isolation of the photoproduct after completion of the reaction and use of an analytical technique such as elemental analysis to verify that L has indeed entered the coordination sphere of the metal. The proper conditions under which the ligand exchange experiment should be carried out, i.e. organometallic ionic salt concentration, identity of the entering ligand, entering ligand concentration, choice of solvent, irradiation wavelength, irradiation time, light source, light source intensity, reaction vessel, presence or absence of oxygen, analysis technique, etc. must be adjusted by the experimentalist for the particular system under study. Examples of the conditions which have been used to study ligand exchange reactions are contained in "Organometallic Photochemistry", 1979, Academic Press, New York, and references therein, and in Inorg. Chem. , 19 , 3007 (1980). Examples of suitable salts of organometallic complex cations useful in the composition of the invention include the following (proposed structures of typical compounds are shown at the end of the list): (η⁵-cyclopentadienyl)dicarbonylthiocarbonyliron(1+) tetrafluoroborate (η⁵-cyclopentadienyl)carbonylbis(triphenylstibine)iron(1+) hexafluorophosphate (η⁵-cyclopentadienyl)dicarbonyltriphenylstibineiron(1+) hexafluoroantimonate (η⁵-methylcyclopentadienyl)dicarbonylnitrosylmanganese(1+) hexafluoroantimonate (b) (η⁵-methylcyclopentadienyl)(η³-allyl)dicarbonylmanganese(1+) tetrafluoroborate (c) (η⁵-cyclohexadienyl)(ethylidene)carbonyltriphenylphosphineiron(1+) tetrafluoroborate (η⁵-cyclopentadienyl)(ethoxymethylcarbene)carbonyltriphenylphosphineiron(1+) tetrafluoroborate (η⁵-cyclopentadienyl) (dithiomethoxycarbene)-dicarbonyliron(1+) hexafluorophosphate (η⁵-cyclopentadienyl)dicarbonylmethylisonitrileiron(1+) hexafluoroarsenate bis(η⁵-cyclopentadienyl)(η²-ethylene)(σ-methyl)tungsten(1+) hexafluorophosphate (η⁵-cyclopentadienyl)(η²-1-pentene)dicarbonyliron(1+) tetrafluoroborate bis(η⁵-cyclopentadienyl)cobalt(1+) hexafluorophosphate tetracarbonyltriphenylphosphinecobalt(1+) hexafluorophosphate tricarbonylbis(triphenylphosphine)iridium(1+) hexafluorophosphate (η³-allyl)pentacarbonylchromium(1+) tetrafluoroborate pentacarbonylnitrosylmolybdenum(1+) hexafluorophosphate (η³-allyl)tetracarbonyliron(1+) hexafluoroantimonate hexacarbonylrhenium(1+) hexafluoroantimonate dicarbonyl[bis(diphenylphosphino)ethane]bis(η⁵-cyclopentadienyl)diiron(1+) hexafluorophosphate tetra[(η⁵-cyclopentadienyl)carbonyliron](1+) hexafluorophosphate tris[(η⁶-benzene)cobalt]dicarbonyl(1+) hexafluorophosphate tris(η⁵-cyclopentadienyl)dinickel(1+) hexafluorophosphate [(η⁶-1,2,29,18c,18b,18a)(η⁶-7,8,8a,18i,18h,7a)(η⁶-13,14,14a,18o,18n,12a)(η⁶-18t,18u,18v,18w,18x,18y)-tripyreno(2,1,10,9,8,7-defghij:2',1',10',9',8',7'-nopqrst: 2'',1'',10'',9'',8'',7''-xyza,b,c,d(trinaphthalene]tetra(η⁵-cyclopentadienyl)tetrairon(4+) hexafluoroantimonte [(η⁶-4,5,5a,28c,28b,3a)(η⁶-8a,8b,20d,22a,22b,24c)-1H,14H-dipyrano(3,4,5, gh: 3',4',5'-g'h')anthra(2'',1'',9'': 4,5,6;6'',5'',10'':4',5',6')diisoquino(2,1-a:2',1'-a¹)diperimidine]bis(n⁵-cyclopentadienyl)diiron(2+) hexafluoroantimonate [(η⁶-1,2,3,3a,13b,13a)benzo(10,11)chryseno(2,3-d)(1,3)dioxole](η⁵-methylcyclopentadienyl)iron(1+) hexafluorophosphate [(η⁶-1,2,3,3a,16c,16b)(η⁶-9,10,11,11a,13c,8b)cycloocta(1,2,3,4-def:5,6,7,8-d'e'f')diphenanthrene]bis(n⁵-acetylcyclopentadienyl)diiron(2+) tetrafluoroborate bis(η⁵-acetylcyclopentadienyl)iron(1+) tetrafluoroborate [(η⁶-1,2,3,4,4a,42a)(η⁶-16,17,18,19,19a,15a)(η⁶-30,31,32, 32a,32b,29a)naphth(8',1',2':6,5,10)anthra(2,3-i)naphth(2''',3''':6'',7'')indolo(2'',3'':5'6')naphth(2'3':4,5)indolo(2,3-g)naphtho(2,3-i')benzo(1,2-a:4,5-a')dicarbazole]tris(n⁵-cyclopentadienyl)triion(3+) hexafluoroantimonate (η³-1-methyl-allyl)tricarbonyliron(+1) hexafluorophosphate [(η⁵-cyclopentadienyl)nickelnonacarbonyltricobalt](+1) hexafluorophosphate Di-(µ-carbonyltricarbonyl)(dicarbonyliron)(hexacarbonyl- hydrodiruthenium)-µ-hydro-osmium(2Fe-Ru)(Fe-Os)(20s-Ru)(Ru-Ru)(+1) hexafluorophosphate (j) Tetra-µ-hydrotetrakis[(1,2,3,4,5-η)-1,2,3,4,5-pentamethyl-2,4-cyclopentadienyl-1-yl]-tetra- tetrahedro -rhodium(+2) bis(hexafluorophosphate) (k) Bis(µ-diphenylphoshido-µ-carbonyl-π-methylcyclopentadienylcarbonyliron)rhodium(2Rh-Fe)(+1) hexafluorophosphats (1) Di-µ-carbonylpentacarbonyl-µ-carbonyldi-π-cyclopentadienyldirhodio)diiron(Fe-Fe)(4Fe-Rh)(Rh-Rh)(+1) hexafluoroarsenate (m) Di-µ3-carbonyltricarbonylbis(π-cyclopentadienylnickelio)iron(2Fe-Ni)(Ni-Ni)(+1) hexafluoroantimonate (n) (b) (c) (j) C₁₃H₂FeO₁₃OsRu₂PF₆ (k) C₄₀H₆₄Rh₄P₂F₁₂ (1) C₄₀H₃₄Fe₂O₄P₂RhPF₆ (m) C₁₈H₁₀Fe₂O₈Rh₂AsF₆ (n) C₁₅H₁₀FeNi₂O₅SbF₆ Cyclic ether materials that can be cured or polymerized by the compounds of this invention, using the latter in a catalytically effective amount, are those known to undergo cationic polymerization and include 1,2-, 1,3-, and 1,4-cyclic ethers (also designated as 1,2-, 1,3-, and 1,4-epoxides). The cyclic ethers which can be polymerized in accordance with this invention include those described in Ring-Opening Polymerizations", Vol. 2, by Frisch and Reegan, Marcel Dekker, Inc. (1969). Suitable 1,2-cyclic ethers are the monomeric and polymeric types of epoxides. They can be aliphatic, cycloaliphatic, aromatic, or heterocyclic and will typically have an epoxy equivalency of from 1 to 6, preferably 1 to 3. Particularly useful are the aliphatic, cycloaliphatic, and glycidyl ether type 1,2-epoxides such as propylene oxide, epichlorohydrin, styrene oxide, vinylcyclohexene oxide, vinylcyclohexene dioxide, glycidol, butadiene oxide, glycidyl methacrylate, diglycidyl ether of bisphenol A, 3,4-epoxycyclohexylmethyl-3,4-epoxycyclohexanecarboxylate, 3,4-epoxy-6-methylcyclohexylmethyl-3,4-epoxy-6-methylcyclohexanecarboxylate, bis(3,4-epoxy-6-methylcyclohexylmethyl)adipate, dicyclopentadiene dioxide, epoxidized polybutadiene, 1,4-butanediol diglycidyl ether, polyglycidyl ether of phenolformaldehyde resole or novolak resin, resorcinol diglycidyl ether, and epoxy silicones, e.g., dimethylsiloxanes having cycloaliphatic epoxide or glycidyl ether groups. A wide variety of commercial epoxy resins are available and listed in "Handbook of Epoxy Resins" by Lee and Neville, McGraw Hill Book Company, New York (1967) and in "Epoxy Resin Technology" by P. F. Bruins, John Wiley & Sons, New York (1968). Representative of the 1,3-and 1,4-cyclic ethers which can be polymerized in accordance with this invention are oxetane, 3,3-bis(chloromethyl)oxetane, and tetrahydrofuran. There is a host of commercially available cationically-sensitive monomers which can be used in this invention. In particular, cyclic ethers which are readily available include propylene oxide, oxetane, epichlorohydrin, tetrahydrofuran, styrene oxide, vinylcyclohexene oxide, glycidol, glycidyl methacrylate, octylene oxide, phenyl glycidyl ether, 1,2-butane oxide, diglycidyl ether of bisphenol A (e.g., "Epon 828" and "DER 331"), vinylcyclohexene dioxide (e.g., "ERL-4206"), 3,4-epoxycyclohexylmethyl-3,4-epoxycyclohexanecarboxylate (e.g., "ERL-4221"), 3,4-epoxy-6-methylcyclohexylmethyl 3,4-epoxy-6-methylcyclohexanecarboxylate (e.g., "ERL-4201"), bis(3,4-epoxy-6-methylcyclohexylmethyl)adipate (e.g., "ERL-4289"), aliphatic epoxy modified with polypropylene glycol (e.g., "ERL-4050" and "ERL-4052"), dipentene dioxide (e.g., "ERL-4269"), epoxidized polybutadiene (e.g., "Oxiron 2001"), silicone epoxy (e.g., "Syl-Kem 90"), 1,4-butanediol diglycidyl ether (e.g., "Araldite RD-2"), polyglycidyl ether of phenolformaldehyde novolak (e.g., "DER-431", "Epi-Rez 521" and "DER-438"), resorcinol diglycidyl ether (e.g., "Kopoxite"), polyglycol diepoxide (e.g., "DER 736"), polyacrylate epoxide (e.g., "Epocryl U-14"), urethane modified epoxide (e.g., "QX3599"), polyfunctional flexible epoxides (e.g., "Flexibilizer 151"), and mixtures thereof as well as mixtures thereof with co-curatives, curing agents, or hardeners which also are well known (see Lee and Neville and Bruins, supra). Representative of the co-curatives of hardeners which can be used are acid anhydrides such as nadic methyl anhydride, cyclopentanetetracarboxylic dianhydride, pyromellitic anhydride, cis-1,2-cyclohexanedicarboxylic anhydride, and mixtures thereof. In general, the polymerization with the ionic salt of an organometallic complex can be carried out at room temperature although low temperature (e.g., -10°C) or elevated temperatures (e.g., 30° to 200°C, preferably 50° to 150°C), can be used to either subdue the exotherm of polymerization or to accelerate the polymerization. In the case of latent salt catalysts of this invention, temperatures generally in the range of 50° to 250°C, preferably from 50° to 150°C, can be used. The temperature of polymerization and amount of catalyst will vary and be dependent on the particular epoxy monomer used and the desired application of the polymerized or cured product. The amount of ionic salt of an organometallic complex to be used as a catalyst in this invention should be sufficient to effect polymerization of the cationically-sensitive monomer (i.e., a catalytically effective amount) under the desired use conditions. Such amount generally will be in the range of about 0.01 to 20 weight percent, preferably 0.5 to 5.0 weight percent, and most preferably 1.0 to 2.0 weight percent, based on the weight of cationically-sensitive monomer. Solvents can be used to assist in dissolution of the ionic salt in the cationically-sensitive material and are preferred for use in the polymerizable compositions. Representative solvents include acetone, methyl ethyl ketone, cyclopentanone, methyl cellosolve acetate, methylene chloride, nitromethane, methylformate, acetonitrile, and 1,2-dimethoxyethane (glyme). The curable or polymerizable compositions of this invention comprising the cationically-sensitive monomer(s) and the ionic salt of an organometallic complex as catalyst can be used for applications such as those in which other cationically-sensitive compositions employing Lewis acid catalysts such as BF₃ or BF₃·diethyl ether or the radiation sensitive onium salts are used. Thus, the compositions can be used as adhesives, caulking and sealing compounds, casting and molding compounds, potting and encapsulating compounds, impregnating and coating compounds, etc. depending on the particular cationically-sensitive monomer and ionic organometallic complex used. In addition, the composition may contain adjuvants (e.g., fillers, such as silica, talc, glass bubbles, clay, reinforcing fibers, dyes, pigments, plasticizers, slip agents, antioxidants, surface modifying agents, etc.,) as long as they do not interfere with the polymerization of the cationically-sensitive components of the composition or, where the ionic salt of the organometallic complex is radiation-sensitive, absorb radiation to which the complex is responsive. For those compositions of the invention which are radiation-sensitive, i.e., the compositions containing cationically-sensitive monomers and an ionic salt of an organometallic complex of Formulas I, and II, any source of radiation emitting active radiation in the ultraviolet and visible region of the spectrum (e.g., about 200 to 600nm) can be used. Suitable sources of radiation include mercury vapor discharge lamps, carbon arcs, tungsten lamps, xenon lamps, sunlight, etc. The required amount of exposure to effect polymerization is dependent upon such factors as the identity and concentration of the organometallic ionic complex, the particular cationically-sensitive monomer, the thickness of the exposed material, type of substrate, intensity of the radiation source and amount of heat associated with the radiation. Optionally, it is within the scope of this invention to include spectral sensitizers in the radiation-sensitive composition. Any photosensitizer may be useful if its triplet energy is at least 45 kcal/mole. Examples of such sensitizers are given in Table 2-1 of the reference, Steven L. Murov, Handbook of Photochemistry , Marcel Dekker Inc., NY, 27-35 (1973), and include pyrene, fluoroanthrene, benzil, chrysene, p-terphenyl, acenaphthene, naphthalene, phenanthrene, and biphenyl. When present, the amount of sensitizer used in the practice of the present invention is generally in the range of 0.01 to 10 parts, and preferably 0.1 to 1.0 parts, by weight of sensitizer per part of organometallic salt. The objects and advantages of this invention are further illustrated by the following examples, many of which utilize as cationically-sensitive monomer a stock solution consisting of 1 part by weight of vinylcyclohexene dioxide and 1 part by weight of 3,4-epoxycyclohexylmethyl-3,4-epoxycyclohexanecarboxylate. The particular materials and amounts thereof recited in these examples, which are in parts by weight, as well as other conditions and details should not be construed to unduly limit this invention. EXAMPLES 1-4 Polymerizable solutions were prepared by mixing in four suitable vessels 10 parts of stock solution, 1.0 part of acetonitrile, and 0.1 part in each vessel respectively, of (Example 1) the hexafluoroantimonate, (Example 2) the hexafluoroarsenate, (Example 3) the hexafluorophosphate, and (Example 4) the tetrafluoroborate salt of (η⁶-mesitylene)(η⁵-cyclopentadienyl)iron(1+) (each prepared as described in W. A. Hendrickson, Ph.D. thesis, U. of Florida (1978)). The solutions were coated onto polyvinylidene chloride primed 75 micrometer polyester using a number 22 wire wound coating rod and the coatings allowed to air dry for 30 minutes. The coated samples were then exposed to a 150 watt tungsten spotlight at a distance of 10 cm from the sample surface. The time required to produce a non-tacky surface for each sample is given in Table I. Ex. No. Counterion of (η⁶-mesitylene)(η⁵-cyclopentadienyl)iron(1+) Time to produce non-tacky surface 1 SbF₆⁻ 30 sec 2 AsF₆⁻ 45 sec 3 PF₆⁻ 120 sec 4 BF₄⁻ greater than 30 min EXAMPLES 5-7 Coatings were prepared as described in Examples 1-4 using as catalyst the hexafluorophosphate salts of, respectively, (Example 5) (η⁶ - naphthalene)(η⁵-cyclopentadienyl)iron(1+), (Example 6) (η⁶-chrysene)(η⁵-cyclopentadienyl)iron(1+), and (Example 7) (η⁶-pyrene)(η⁵-cyclopentadienyl)iron(1+). (These salts were prepared according to the procedure described in J. Organometal. Chem. 101 , 221 (1975)). Samples of each coating (labeled (b)) were exposed to the output of the 150 watt tungsten lamp as described in Examples 1-4 and other samples of the coatings (labeled (c)) were exposed to the output of the 150 watt tungsten lamp that passed through a light filter that removed 99% of the radiation below 440 nm. The time to produce a non-tacky coating for each sample is recorded in Table II. EX. No. Catalyst Time to produce non-tacky surface hexafluorophosphate salt of: (b) no filter (c) 440nm filter 5 (η⁶-naphthalene)(η5-cyclopentadienyl)iron(1+) 30 sec 60 sec 6 (η⁶-chrysene)(η⁵-cyclopentadienyl)iron(1+) 30 sec 60 sec 7 (η⁶-pyrene)(η⁵-cyclopentadienyl)iron(1+) 15 sec 30 sec EXAMPLES 8 and 9 The procedure of Example 5-7 gas repeated using as catalyst the hexafluorophosphate salt and the hexafluoroantimonate salt of (η⁶-fluorene)(η⁵-cyclopentadienyl)iron(1+). The time required to produce a non-tacky surface with the hexafluorophosphate salt was 60 seconds for exposures without the filter and 120 seconds with the filter. With the hexafluoroantimonate salt, exposures to produce a non-tacky surface were 30 and 60 seconds respectively. The (η⁶-fluorene)(η⁵-cyclopentadienyl)iron(1+) salts were prepared as described in Hendrickson, Ph.D. thesis, Univ. of Florida (1978). EXAMPLES 10-15 Coating solutions were prepared by mixing 10 parts of stock solution, 2 parts of acetone and 0.1 part of each of the various organometallic complex salts shown in Table III. Each solution was coated and dried as described in Examples 1-4 and exposed as described in Examples 5-7. The time required to produce a non-tacky surface for each is given in Table III. EXAMPLE 16 A coating solution, prepared by mixing 10 parts of stock solution, 1 part of acetonitrile and 0.1 part of (η⁶-toluene)(η⁵-cyclopentadienyl)iron(1+) hexafluorophosphate, (prepared as described in the previously cited Ph.D. Thesis of W. A. Hendrickson), was coated and dried as described in Examples 1-4. On exposure of the dried coating to a 150 watt tungsten spotlight at 10 cm, a non-tacky surface was obtained in 60 seconds. Only 30 seconds were required to produce a non-tacky surface when the coating was exposed to the output of a 275 watt G.E. sunlamp at 10 cm. EXAMPLES 17 AND 18 Example 16 was repeated using poly(η⁶-styrene)(η⁵-cyclopentadienyl)iron(1+) hexafluorophosphate or poly(η⁶-styrene)tricarbonylmanganese(1+) hexafluoroarsenate in place of (η⁶-toluene)(η⁵-cyclopentadienyl)iron(1+) hexafluorophosphate. Exposure times were 120 seconds and 45 seconds to produce a non-tacky coating using the 150 watt tungsten spotlight and the 275 watt sunlamp respectively. The polystyrene iron complex was prepared as described in the before-mentioned Ph.D. thesis and the polystyrene manganese complex was prepared as described in J.Chem.Soc. ( Chem . Comm.) 688 (1975) using polystyrene having a number average molecular weight of 22,000 in place of mesitylene or toluene, respectively. The iron complex obtained had approximately one (η⁵-cyclopentadienyl)iron(1+) unit per eight styrene units and the manganese complex obtained had approximately one tricarbonylmanganese(1+) unit per three styrene units. EXAMPLES 19-42 Polymerizable solutions were prepared as described in previous examples using the polymerizable compositions and the organometallic salts listed in Table IV. Each solution was coated onto primed polyester film and the coating dried as previously described, and exposed to polymerizing conditions as shown in Table IV. The time required to obtain a tack-free coating for each is given in Table IV. EXAMPLES 43-50 To illustrate the range of concentrations of ionic salts of organometallic complexes effective for catalyzing the polymerization of cationically polymerizable compounds, solutions were prepared as described previously consisting of stock solution, solvent, and 10.0 to 0.01 percent by weight, based on total weight of stock solution, of ionic salt as shown in Table V. Each mixture was coated onto poly(vinylidene chloride) primed polyester sheeting, dried, and exposed to the radiation of a 275 watt G. E. sunlamp at a distance of 10 cm until the coating was non-tacky to the touch. The results are given in Table V.

Claims: An energy polymerizable composition comprising a cyclic ether, optionally 0.01 to 10 parts by weight per part of organometallic salt of a spectral sensitizer, and a catalytically effective amount of an ionic salt of organometallic complex cation capable of adding a nucleophile intermediate in strength between hydride and chloride or upon photolysis capable of liberating at least one coordination site, wherein said ionic salt has the formula: [(L 1a ) (L 2a ) (L 3a )M³]g[(L 1b ) (L 2b ) (L 3b )M b ] h [(L 1c ) (L 2c ) (L 3c )M c ]j[(L 1d ) (L 2d ) (L 3d )M d ] k (L⁴) (L⁵) (L⁶) +e X f I wherein M a , M b , M c , and M d each represents a metal selected from the elements of Periodic Groups IVB, VB, VIB, VIIB, and VIII; with the proviso that Formula I can represent a mononuclear, binuclear, trinuclear, or tetranuclear complex compound comprising M a, M a M b , M a M b M c , or M a M b M c M d respectively with their attendant ligands, L; L 1a , L 1b , L 1c , and L 1d each represents none, 1, 2, or 3 ligands contributing π-electrons that can be the same or different ligands selected from substituted and unsubstituted acyclic and cyclic unsaturated compounds and groups and substituted and unsubstituted carbo-cyclic aromatic and heterocyclic aromatic compounds, each capable of contributing two to twelve π-electrons to the valence shell of M a , M b , M c , and M d respectively; L 2a , L 2b , L 2c and L 2d each represents none or 1 to 6 ligands contributing an even number of σ-electrons that can be the same or different selected from mono-, di-, and tri-dentate ligands, each contributing 2, 4, or 6 σ-electrons to the valence shell of M a , M b , M c , and M d respectively; L 3a , L 3b , L 3c , and L 3d each represents none, 1 or 2 ligands contributing one σ-electron each to the valence shell of M a , M b , M c , and M d respectively; L⁴ represents none or 1 to 6 bridging ligands containing π-electrons that can be the same or different ligand selected from substituted or unsubstituted acyclic and cyclic unsaturated compounds and groups and substituted and unsubstituted carbocyclic aromatic and heterocyclic aromatic compounds, each capable of acting as a bridging ligand contributing 2 to 24 π-electrons to the valence shells of two or more metal atoms M a , M b , M c , or M d simultaneously; L⁵ represents none or 1 to 12 bridging ligands contributing an even number of σ-electrons that can be the same or different selected from mono, di, and tri-dentate ligands, each donating 2, 4, or 6 σ-electrons to the valence shells of two or more metal atoms M a , M b , M c , or M d simultaneously; L⁶ represents none or 1 to 12 bridging ligands contributing 1, 2, 3, or 4 σ-electrons to the valence shells of two or more metal atoms M a , M b , M c , or M d simultaneously; with the proviso that the total electronic charge contributed to M a , M b , M c , and M d by the ligands L 1a , L 2a , L 3a , L 1b , L 2b , L 3b , L 1c , L ²c , L 3c , L 1d , L 2d , L 3d , L⁴, L⁵, and L⁶ plus the sum or ionic charge on M a , M b , M c , and M d results in a residual net positive charge of e to the complex; e is an integer having a value of 1, 2, or 3, the residual electrical charge of the complex cation; X is a halogen containing complex anion of a metal or metalloid; f is an integer of 1 to 3, the number of complex anions required to neutralize the charge e on the complex cation, and g, h, j, and k independently are 0 or 1, with at least one of them being equal to 1; those compositions being excluded wherein either: a) said ionic salt is mononuclear, L 1a is an arene group or a dienylium group and each L 2a ligand is carbonyl, or b) said ionic salt is mononuclear or binuclear with identical transistion metal atoms and each ligand thereof is a π-arene or the anion of a π-arene and the composition is free of sensitizer. An energy polymerizable composition comprising a cyclic ether and a catalytically effective amount of an ionic salt of an organometallic complex cation capable of adding a nucleonphile intermediate in strength between hydride and chloride or upon photolysis capable of liberating at least one coordination site, wherein said ionic salt has the formula: [(L⁷) (L⁸)M m ] +e X f II wherein M m represents a metal selected from elements of the Periodic Groups IVB, VB, VIB, VIIB, and VIII; L⁷ represents none, one, or two π-electron contributing ligands that can be the same or different ligand selected from substituted and unsubstituted acyclic and alicyclic unsaturated compounds and groups and substituted and unsubstituted carbocyclic and heterocyclic aromatic compounds, each capable of contributing two to twelve π-electrons to the valence shell of M m ; L⁸ represents none or 1 to 6 ligands that can be the same or different ligand selected from mono-, di-, and tri-dentate ligands, each contributing 2, 4, or 6 σ-electrons to the valence shell of M m ; with the proviso that the total electronic charge contributed to M m by L⁷ and L⁸ plus the ionic charge on M m results in a residual net positive charge of e to the complex; e is an integer having a value of 1, 2, or 3, the residual electrical charge of the complex cation; X is a halogen containing complex anion of a metal or metalloid; and f is an integer of 1 to 3, the number of complex anions required to neutralize the charge of e on the complex cation, those compositions being excluded wherein either: a) L⁷ is an arene group or a dienylium group and each L⁸ ligand is carbonyl, or b) each ligand of said ionic salt is a π-arene or the anion of a π-arene and the composition is free of spectral sensitizer. A composition according to claim 1 wherein in Formula I, the ligands L 1a , L 1b , L 1c , and L 1d of the ionic salt each contains less than 100 carbon atoms and up to 10 hetero atoms selected from nitrogen, sulfur, oxygen, phosphorus, arsenic, selenium, antimony, tellurium, silicon, germanium, tin, and boron; the ligands L 2a , L 2b , L 2c , and L 2d of the ionic salt are each selected from: a. monodentate ligands having up to 30 carbon atoms and up to 10 hetero atoms selected from nitrogen, sulfur, oxygen, phosphorus, arsenic, selenium, antimony, tellurium, and b. polydentate ligands capable of forming with metal M a , M b , M c , or M d a 4-, 5-, or 6-membered saturated or unsaturated ring containing up to 10 hetero atoms selected from nitrogen, sulfur, oxygen, phosphorus, arsenic, selenium, antimony, tellurium, in addition to the metal atom; the ligands L 3a , L 3b , L 3c , and L 3d of the ionic salt each have up to 30 carbon atoms and up to 10 hetero atoms selected from nitrogen, sulfur, oxygen, phosphorus, arsenic, selenium, antimony, tellurium, silicon, germanium, tin, and boron; the bridging ligand L⁴ of the ionic salt contains less than 100 carbon atoms and up to 10 hetero atoms selected from nitrogen, sulfur, oxygen and nitrogen, sulfur, oxygen, phosphorus, arsenic, selenium, antimony, tellurium, silicon, germanium, tin, and boron; the bridging ligand L⁵ of the ionic salt contains up to 30 carbon atoms and up to 10 hetero atoms selected from nitrogen, sulfur, oxygen, phosphorus, arsenic, selenium, antimony, tellurium, and boron; and the bridging radical L⁶ of the ionic salt has up to 30 carbon atoms and up to 10 hetero atoms selected from nitrogen, sulfur, oxygen, phosphorus, arsenic, selenium, antimony, tellurium, silicon, germanium, tin, and boron. A composition according to claim 2 wherein in Formula II ligand L⁷ of the ionic salt contains less than 100 carbon atoms and up to 10 hetero atoms selected from nitrogen, sulfur, oxygen, phosphorus, arsenic, selenium, antimony, tellurium, silicon, germanium, tin, and boron; ligand L⁸ of the ionic salt is selected from: a. monodentate ligands having up to 30 carbon atoms and up to 2 hetero atoms selected from nitrogen, sulfur, oxygen, phosphorus, arsenic, selenium, antimony, tellurium, silicon, germanium, tin, and boron, and b. polydentate ligands capable of forming with metal M m a 4-, 5-, or 6-membered saturated or unsaturated ring containing up to 10 hetero atoms selected from nitrogen, sulfur, oxygen, phosphorus, arsenic, selenium, antimony, tellurium, silicon, germanium, tin, and boron in addition to the metal atom. A composition according to any of claims 1 to 4 wherein the ligands L 1a , L 1b , L 1c , L 1d , and L⁷ are each independently unsubstituted or substituted by a group selected from hydrocarbyl, hydrocarbyloxy, hydrocarbylmercapto, hydrocarbyloxycarbonyl, hydrocarbylcarbonyl, hydrocarbylcarbonamido, phenyl, azo, boryl, halo, hydroxy, cyano, nitro, nitroso, oxo, dimethylamino, diphenylphosphino, trimethylsiloxy, and condensed rings, said group containing up to 30 carbon atoms and up to 10 hetero atoms selected from nitrogen, sulfur, oxygen, phosphorus, arsenic, selenium, antimony, tellurium, silicon, germanium, tin, and boron. A composition according to any preceding claim wherein said salt is present in an amount in the range of 0.01 to 20 weight percent of said cyclic ether. A composition according to any preceding claim further comprising in the range of 0.01 to 10 parts by weight of a spectral sensitizer per part of organometallic salt. A composition according to any of claims 1 to 7 wherein said L 1a , L 1b , L 1c , L 1d , L 2a , L 2b , L 2c , L 2d , L 3a , L 3b , L 3c , L 3d , L⁴, L⁵, L⁶, L⁷, and L⁸ ligands independently are groups on a polymeric chain. A composition according to any of claims 1 to 7 wherein said L 1a and L⁷ ligands are selected from polystyrene, poly(styrene-co-methyl methacrylate), and polyvinylcarbazole, eta-3-allyl, eta-5-cyclopentadienyl, eta-5-methylcyclopentadienyl, eta-6-benzene, eta-6-mesitylene, eta-6-naphthalene, and eta-6-fluorene. A composition according to any of claims 1 to 7 wherein said L⁴ ligand is selected from eta-3-allyl, eta-5-cyclopentadienyl, eta-5-methylcyclopentadienyl, eta-6-benzene, eta-6-mesitylene, eta-6-naphthalene, and eta-6-fluorene. A process for polymerizing the composition according to any preceding claim, said process comprising: a. admixing said cyclic ether with a catalytically effective amount of said ionic salt of an organometallic complex, and b. curing the resulting admixture with at least one of a thermal and actinic radiation source.

Inventors: HENDRICKSON, WILLIAM A. C/O MINNESOTA, PALAZZOTTO, MICHAEL C. C/O MINNESOTA
Applicants: MINNESOTA MINING AND MANUFACTURING COMPANY
Application year: 1983
Main classification: C08F4
IPC codes: C08G77, C08F2, C08F10, C08G59, C07F13, C07F7, C08G65, C08F4, C08G85, C07F15, C07F17, C08F8