Sodium carboxymethylcellulose

Abstract: Sodium carboxymethylcellulose is specified in that the average degree of substitution ( DS ) of carboxymethyl groups per anhydroglucose unit is in the range of 0.4 to 1.6; the number-average degree of polymerization is in the range of 100 to 1,500; and the mobility distribution (ΔU) as measured by electrophoresis is represented by the following formula: ΔU × 10⁵ < (-3.0 log DS ÷ 3.20) × 10⁵ cm²/sec. V

Description: This invention relates to a process for preparing a sodium carboxymethylcellulose having an average degree of substitution ( DS ) of carboxymethyl groups per anhydroglucose unit in the range of 0.4 to 1.08; a number-average degree of polymerization in the range of 100 to 1500; and a mobility distribution (ΔU) as measured by electrophoresis represented by the following formula ΔU x 10⁵ < (-3,0 log DS + 3,20) cm²/sec.V consisting of the following sequence of steps : reacting sodium hydroxide with powdered cellulose in the presence of a mixture of isopropyl alcohol and water to obtain alkali cellulose, adding isopropyl monochloroacetate as an etherifying agent and optionally isopropyl acetate to neutralize an excess of sodium hydroxide, agitating the mixture to effect etherification, and isolating the reaction product. As is well known, sodium carboxymethylcellulose (hereinafter abbreviated as CMC) has long been manufactured in the industry and has been applied in a variety of uses, such as paste or thickening agent. CMC is used in most cases in the form of an aqueous solution and, therefore, problems due to its form, for example, susceptibility to enzymatic decomposition and a marked loss of solution viscosity by a salt, for example, sodium chloride arise. In addition, there have been problems such as strong thixotropy and marked changes in its solution viscosity with the lapse of time, so that improvements in its respective uses have long been expected. The present inventors have found that it is necessary to confine the carboxymethyl group distribution within a specified range in order to solve the above problems, especially behavior in an aqueous solution, more particularly, solution behavior such as viscosity loss due to the presence of a salt and marked thixotropy. In this invention, the carboxymethyl group distribution is expressed by a mobility distribution for the sake of its actual measurement, as will be described hereinbelow. It is suggested by Terashima et al. in Polymer Journal, Vol. 8, pp. 449 to 455 (1976) that the charge density distribution of a polyelectrolyte, for example, the substitution degree distribution of CMC, can be measured electrophoretically. Brief description of the drawings Fig. 1 is a diagram obtained by plotting the relationship between a migration time and a mobility, Fig. 2 is a diagram schematically showing the state of an electrophoretic boundary in terms of a rate of changes in refractive index, Fig. 3 is a diagram obtained by plotting the relationship between the mobility distribution of a variety of CMC's and average degrees of substitution of carboxymethyl groups, and Fig. 4 is a diagram obtained by plotting the relationship between the average degree of substitution and the median mobility. In this invention, the substitution degree is grasped in terms of a mobility distribution as measured by electrophoresis, and this mobility distribution is defined as one measured according to the following method. The measurement of the DS distribution by electrophoresis is made at 25°±0.1°C by using a Tsukasa-Tiselius electrophoresis apparatus and a Schlieren optical system, under the following conditions: Sample concentration: 0.2 g/100 ml Solvent: 0.1 N aqueous NaCl solution Electric current: 0.002 A When the electrophoresis is carried out under these conditions, electrophoretic mobility U can be determined experimentally by the following equation: wherein K: specific conductivity of solvent 1.067×10⁻² /cm A: cross-sectional area of cell 0.351 cm² i: migration current 0.002 A H: migration distance (cm) t: migration time (second). The state of a boundary realized by carrying out electrophoresis is shown schematically in Fig. 2 in terms of a rate of change (Δn) in refractive index (DS=0.73, after 7 hours) and maximum mobility A, minimum mobility B and median mobility C are obtained corresponding to the respective migration times. In this invention, migration in an ascending boundary is measured for convenience' sake, and the mobilities i.e., the values of points A, B and C are plotted against an abscissa which represents a reciprocal of the time to obtain lines (DS=0.73, 1% viscosity 210 cP) of Fig. 1. Extrapolation to infinite time gives mobilities U A ', U B ', and U C '. U A '―U B ' is defined as a mobility distribution (ΔU). Fig. 4 is obtained by plotting U C ' against an average DS as measured by a conventional chemical measurement. As apparent from this figure, the ΔU represents the width of a DS distribution (ΔDS), that is, the difference between the maximum DS and minimum DS of a CMC sample. On the other hand, the solution behavior of an aqueous CMC solution is grasped phenomenally by salt water resistance and thixotropy, but there is an anhydroglucose unit which has no carboxymethyl groups because of a heterogeneity of the reaction or for lack of an absolute amount, that is, a difficultly soluble portion and a soluble portion having carboxymethyl groups in the CMC molecule. The more uniform the DS distribution of CMC is, the larger is the content of the soluble portion of CMC. When a salt such as sodium chloride is added to an aqueous solution of CMC, the repulsive force of the soluble portion decrease to a less extent than otherwise. At the same time, the cohesion of the difficulty soluble portion increases with shear stress decreased. In other words, thixotropy decreases as the external force disappears. This way the stability of the solution, which is established by a balance between the repulsive force among the soluble portions and the cohesive force of the difficultly soluble portion, depends on the DS distribution, while a CMC having a higher average DS or having a larger amount of the soluble portion exhibits a higher stability when it is in solution. Accordingly, a CMC haying an average DS of above 2.0 has a stable solution state irrespective of its production process, because it has a soluble portion constituted by substituting at least one carboxymethyl group into each of almost all anhydroglucose units, whereas a CMC having an average DS of below about 0.5 has an essentially unstable solution state, because half of the anhydroglucose units have no substituents, however uniformly it may be substituted by carboxymethyl groups. Especially, when the DS is below about 0.3, the CMC becomes water-insoluble. However, a CMC having a higher uniformity has a more stable solution state even in these cases. For this reason, an object of this invention is to improve the solution state of a CMC having an averate DS of 0.4 to 1.08. The present inventors have measured the solution state stability typified by ΔU, i.e., ΔDS and a resistance to salinity and enzyme of commercially available CMC's and those produced by a variety of production processes, including that of the prior application of the applicant of this invention. The results are shown in Table 2. These results are illustrated by a diagram of Fig. 3 showing the relationship between log (DS) and ΔU, wherein closed and open circles are distinguished from each other according to the following criterion. In the criterion, among CMC's having an average DS of above 0.7, those having a salt water resistance of below 0.9 are represented by closed circles, while those having a salt water resistance of 0.9 or above are represented by open circles. When it is supposed that, from the values of salt water resistance of CMC's having nearly the same average DS, the value of salt resistance between them is directly proportional to ΔU, the line formed by tying points which show a value of salt water resistance of 0.9 is represented as above by the following equation: ΔU×10⁵={-3.0 log (DS) +3.20} When this line is extrapolated to a point of an average DS of below 0.7, the line forms a boundary between CMC's having good (in a relative sense) salt water resistance and those having poor (in a relative sense) salt water resistance and, also in relative values showing a comparison of the enzyme resistance at the same average DS, the line constitutes a boundary beyond which the enzyme resistance is nearly doubled. It has been found that the above-mentioned line constitutes also a boundary between known and unknown CMC's, that is, those prepared according to the processes described in Japanese Patent Application Nos. 50277/1981 and 142731/1981, which are prior applications of the applicant of this invention. The novel CMC of this invention has a more uniform substituent distribution than the conventional or commercially available products such as those prepared by using ordinary monochloroacetic acid as an etherifying agent, so that it is featured by having, for example, markedly excellent salt water resistance, which is a property of great practical importance in applications of CMC, such as oil drilling mud. It is well known that CMC is an aqueous solution containing a strong electrolyte such as sodium chloride undergoes a marked loss of viscosity as compared with the case where it is in a pure solution because, since CMC is a polyelectrolyte, its dissociation in such an aqueous solution is depressed, which is a great drawback in applications where it is dissolved in an aqueous solution containing a salt, such as those encountered in oil drilling. However, as shown in the examples hereafter described, the CMC of this invention has such excellent salt water resistance that it scarcely undergoes the viscosity loss but rather somewhat increases in viscosity even when it is dissolved in a 4% aqueous sodium chloride solution as compared with the case when it is dissolved in pure water. Moreover, the CMC of this invention has uniformly introduced substituents, so that it is lower in the content of undissolved matter and semi-dissolved swollen gel and excellent in transparency as compared with those prepared by conventional processes and further plugging of a screen is less when it is used as a textile printing paste. Moreover, this CMC is excellent in enzyme resistance (putrefaction resistance) which is a property of great practical importance in various uses such as ground drilling, oil drilling, slurry explosives, lactic acid beverages, toothpastes, textile printing pastes, water-based pastes and fiber walls. As processes for producing the CMC of the present invention, there were proposed by the inventors of this invention a process for producing a CMC having excellent salt water resistance as described above, comprising using an etherifying agent prepared by esterifying at least 50% of monochloroacetic acid with isopropyl alcohol (Japanese Patent Application No. 50277/1981) and a process for producing an alkali salt of carboxymethylcellulose ether by reacting a cellulosic material with an etherifying agent in an aqueous organic solvent system in the presence of an alkali characterized in that the entire portion of the etherifying agent is added at the initial stage; the etherification reaction is started in the system which is excess in the etherifying agent to such an extent that the alkali is present in a molar ratio, [alkali]/[etherifying agent], of above 0.10 to 0.99, and then the etherification reaction is conducted by adding the alkali in portions so that the molar ratio, [alkali]/[etherifying agent] at the final stage is above 1.00 (Japanese Patent Application No 142731/1981), wherein The CMC's obtained by these processes have a very uniform distribution of carboxymethyl groups so that they have a low value of the mobility distribution (ΔU) as measured by electrophoresis, thus constituting a novel CMC of this invention. Namely, according to these processes, it is possible to obtain CMC's having a uniformity of DS distribution expressed in terms of ΔU which has, as the upper limit, a value represented by the following formula: ΔU×10⁵<(-3.0 log DS +3.20) cm²/sec. V. On the other hand, though its lower limit is not particularly specified, it is generally represented by the following formula: ΔU×10⁵>(-2.0 log DS +2.0) cm²/sec. V. Synthesis examples of CMC samples of this invention and comparative CMC samples are shown below. Herein, parts are parts by weight and % is % by weight. Sample A (this invention, according to the process of Japanese Patent Application No. 50277/1981). A 5-liter double-impeller reactor was charged with 651.2 parts of isopropyl alcohol (purity 100%, hereinafter abbreviated as iPA) and then with 96.0 parts of sodium hydroxide (purity 98%) dissolved in 143.0 parts of deionized water and, after cooling to 20°C, further with 200 parts of powdered cellulose (purity 95%, average polymerization degree 850). The contents were agitated at 20 to 30°C for 60 minutes to obtain alkali cellulose. Then, 87.6 parts of isopropyl monochloroacetate (purity 99%) and 56.3 parts of isopropyl acetate (purity 99%) for use in neutralization of excessive sodium hydroxide were diluted with 95.8 parts of iPA and added. The resulting mixture was agitated at 20 to 30°C for 30 minutes. Then, the temperature was raised to 70°C and the mixture was agitated for 2 hours to effect the etherification reaction, followed by neutralization of an excess of sodium hydroxide by acetic acid. After the reaction, the reaction mixture was withdrawn from the reactor, centrifuged to remove iPA as reaction solvent, then washed twice with 4,000 parts of 75% aqueous methyl alcohol to remove sodium chloride and sodium glycolate as byproducts, and then centrifuged to remove the aqueous methyl alcohol. The purified product was dried in a dryer at 80 to 100°C for about 4 hours to obtain 255 parts of the CMC of this invention. Samples B through F Samples B through F were obtained by carrying out the reaction and the purification under the same conditions as for Sample A, except that the kinds and amounts of cellulosic material, sodium hydroxide and etherifying agents were varied as shown in Table 1. Samples B through E are CMC's of this invention, while sample F is a CMC of a comparative example. Sample Q (this invention, according to the process of Japanese Patent Application No. 142731/1981) A 5-liter double-impeller reactor was charged with 1,032 parts of iPA, then with 180.8 parts of sodium hydroxide (purity 98%) dissolved in 158.0 parts of deionized water and, after cooling to 20 to 30°C, further with 200 parts of powdered cellulose (purity 95%). The contents were agitated at 20 to 30°C for 60 minutes to obtain alkali cellulose. Then, the temperature was raised to 60°C over 10 minutes and the mixture was etherified for 60 minutes. Then, 63.5 parts of sodium hydroxide dissolved in 42.3 parts of deionized water was added. The resulting mixture was agitated at 60 to 70°C for 15 minutes and then etherified at 70°C for 90 minutes. Then, some remaining sodium hydroxide was neutralized with acetic acid. After the reaction, the reaction mixture was withdrawn from the reactor, centrifuged to remove iPA as reaction solvent, then washed three times with 4,000 parts of 75% aqueous methyl alcohol to remove sodium chloride, sodium glycolate and sodium acetate as by-products, and centrifuged to remove the aqueous methylalcohol. The purified product was dried in a dryer at 80 to 100°C for about 6 hours to obtain the CMC of this invention. Measurements were made for the average degree of substitution (DS) , number-average degree of polymerization ( P ), mobility distribution (ΔU), salt water resistance and enzyme resistance of a variety of CMC's shown in Table 2, including the above samples A through E and Q of this invention, a comparative sample F and commercially available products G, H, I, J, K, L, M, N and P. The results are shown in Table 2. The measurement and evaluation of (1) degree of substitution (DS) , (2) salt water resistance and (3) enzyme resistance listed in Table 2 were made as follows. (1) Degree of substitution (DS) 1 g of CMC is accurately weighed out, placed in a platinum or porcelain crucible and ashed at 600°C. The sodium oxide formed by the ashing is titrated with N/10 sulfuric acid by using phenol-phthalein as an indicator The DS is determined by substituting the volume of the acid added (A ml) into the following equation. f: factor of N/10 sulfuric acid. (2) Salt water resistance Salt water resistance is evaluated in terms of a viscosity ratio represented by the formula shown below. Viscosity is measured with a BL viscometer with rotor #4, 60 rpm, at 25°C. The higher the viscosity ratio, the more excellent the salt water resistance. (3) Enzyme resistance To a 1% aqueous CMC solution is added 5 mg/g-CMC of cellulase (Cellulase-AP, a product of Amano Pharmaceutical Co., Ltd.), and the solution is hydrolyzed at room temperature for 140 to 145 hours (the hydrolysis being brought to substantial completion in about 140 hours). Then, the glucose formed as the hydrolyzate is measured by the glucose oxidase method. When the amount of glucose formed is smaller, the CMC is evaluated as having a higher enzyme resistance. Here, the values of enzyme resistance shown in Table 2 are represented by the amount of glucose formed as expressed by the number per 1,000 anhydroglucose units (number/1,000 AGU).

Claims: A process for preparing a sodium carboxymethylcellulose having an average degree of substitution ( DS ) of carboxymethyl groups per anhydroglucose unit in the range of 0.4 to 1.08; a number-average degree of polymerization in the range of 100 to 1500; and a mobility distribution (ΔU) as measured by electrophoresis represented by the following formula ΔU x 10⁵ < (-3,0 log DS + 3,20) cm²/sec.V consisting of the following sequence of steps : reacting sodium hydroxide with powdered cellulose in the presence of a mixture of isopropyl alcohol and water to obtain alkali cellulose, adding isopropyl monochloroacetate as an etherifying agent and optionally isopropyl acetate to neutralize an excess of sodium hydroxide, agitating the mixture to effect etherification, and isolating the reaction product.

Inventors: OHMIYA TAKEO, TAGUCHI ATSUSHI, OHMIYA, TAKEO, TAGUCHI, ATSUSHI
Applicants: DAICEL CHEM, DAICEL CHEMICAL INDUSTRIES, LTD.
Application year: 1983
Main classification: C08B11
IPC codes: C08B11